  1. L1{sub 0}-FePt films fabricated by wet-chemical route

    Energy Technology Data Exchange (ETDEWEB)

    Hong, Xiaoliang; Xiao, Wen; Bao, Nina; Li, Weimin; Chichvarina, Olga, E-mail: A0077107@nus.edu.sg; Ding, Jun, E-mail: msedingj@nus.edu.sg

    2015-08-31

    In this work, we have developed a method to fabricate FePt films by a combination of chemical deposition and post-annealing. Pt-doped Fe films were deposited on Pt(100 nm)/Ti(50 nm)/SiO{sub 2}/Si substrate using thermal deposition and the as-deposited films were subsequently annealed from 300 °C to 800 °C under 5% H{sub 2}/95% N{sub 2}. FePt films were achieved through diffusion and rearrangement of Fe and Pt atoms in post-annealing process. From X-ray diffraction results, the face-centered cubic (fcc) FePt phase appeared at 300 °C and the transformation from fcc to L1{sub 0} phase started at 400 °C. The L1{sub 0}-FePt film possessed an out-of-plane anisotropy and a coercivity of 729 kA/m after annealing at 600 °C. A further increase in annealing temperature led to lower value of coercivity, probably because of grain growth. In addition, the thickness of Pt-doped Fe films could be controlled from 150 nm to 700 nm by adjusting the amount of surfactant used. Our superconducting quantum interference device analysis showed that Pt dopant could significantly improve the chemical stability of Fe films in air. - Highlights: • We fabricated FePt film by a combination of chemical deposition and post-annealing. • L1{sub 0} FePt film was formed by Fe/Pt diffusion in annealing of Pt-doped Fe film. • L1{sub 0}-phase FePt with high coercivity and small out-of-plane anisotropy • Relatively small amount of Pt dopant can enhance chemical stability greatly. • We studied structure and magnetic property of as-deposited and annealed FePt film.

  2. On the Relationship of Magnetocrystalline Anisotropy and Stoichiometry in Epitaxial L1{sub 0} CoPt(001) and FePt(001) Thin Films

    Energy Technology Data Exchange (ETDEWEB)

    Barmak, K

    2004-08-10

    Two series of epitaxial CoPt and FePt films, with nominal thicknesses of 42 or 50 nm, were prepared by sputtering onto single crystal MgO(001) substrates in order to investigate the chemical ordering and the resultant magnetic properties as a function of alloy composition. In the first series, the film composition was kept constant, while the substrate temperature was increased from 144 to 704 C. In the second series the substrate temperature was kept constant at 704 C for CoPt and 620 C for FePt, while the alloy stoichiometry was varied in the nominalrange of 40-60 at% Co(Fe). Film compositions and thicknesses were measured via Rutherford backscattering spectrometry. The lattice and long-range order parameter for the L1{sub 0} phase were obtained for both sets of films using x-ray diffraction. The room-temperature magnetocrystalline anisotropy constants were determined for a subset of the films using torque magnetometry. The order parameter was found to increase with increasing temperature, with ordering occurring more readily in FePt when compared with CoPt. A perpendicular anisotropy developed in CoPt for substrate temperatures above 534 C and in FePt above 321 C. The structure and width of the magnetic domains in CoPt and FePt, as seen by magnetic force microscopy, also demonstrated an increase in magnetic anisotropy with increasing temperature. For the films deposited at the highest temperatures (704 C for CoPt and 620 C for FePt), the order parameter reached a maximum near the equiatomic composition, whereas the magnetocrystalline anisotropy increased as the concentration of Co or Fe was increased from below to slightly above the equiatomic composition. It is concluded that non-stoichiometric L1{sub 0} CoPt and FePt, with a slight excess of Co or Fe, are preferable for applications requiring the highest anisotropies.

  3. L1{sub 0} phase transition in FePt thin films via direct interface reaction

    Energy Technology Data Exchange (ETDEWEB)

    Li Xiaohong; Sun Hongyu; Wang Fengqing; Li Wei; Zhang Xiangyi [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, 066004 Qinhuangdao (China); Liu Baoting; Guo Jianxin [College of Physics Science and Technology, Hebei University, 071002 Baoding (China)], E-mail: xyzh66@ysu.edu.cn

    2008-12-07

    Lowering the L1{sub 0} ordering temperature of FePt films is of great significance for their application as an ultrahigh density magnetic recording medium. In this study, the L1{sub 0} ordering process of FePt thin films deposited directly on Si substrates has been significantly accelerated by the interface reaction between the thin film and the Si substrate, and thus the thin films show a low L1{sub 0} ordering temperature of T = 310 deg. C as compared with those deposited on Si/SiO{sub 2} substrates. The accelerated L1{sub 0} ordering transition is predominantly dependent on the rapid growth of the ordered domains during the interface reaction. The film thickness has an important effect on the interface reaction and thus can be used to tune the L1{sub 0} ordering process of the FePt films.

  4. Direct synthesis of L1 type Fe-Pt nanoparticles using microwave-polyol method

    International Nuclear Information System (INIS)

    Minami, Rumiko; Kitamoto, Yoshitaka; Chikata, Tsukasa; Kato, Shunsaku

    2005-01-01

    We report the synthesis of Fe-Pt nanoparticles with microwave irradiation during polyol-reduction reaction. Chemically ordered Fe-Pt nanoparticles with L1 structure are fabricated at 250 deg. C using a microwave-polyol method without any post-synthesis treatments. Moessbauer analyses reveal the nanoparticles have partially ordered L1 structure. The partially ordered Fe-Pt nanoparticles exhibit coercivity of 3.4 kOe, saturation magnetization of 49 emu/g, and anisotropy field of 83 kOe at room temperature

  5. Tunable magnetic properties by interfacial manipulation of L1(0)-FePt perpendicular ultrathin film with island-like structures.

    Science.gov (United States)

    Feng, C; Wang, S G; Yang, M Y; Zhang, E; Zhan, Q; Jiang, Y; Li, B H; Yu, G H

    2012-02-01

    Based on interfacial manipulation of the MgO single crystal substrate and non-magnetic AIN compound, a L1(0)-FePt perpendicular ultrathin film with the structure of MgO/FePt-AIN/Ta was designed, prepared, and investigated. The film is comprised of L1(0)-FePt "magnetic islands," which exhibits a perpendicular magnetic anisotropy (PMA), tunable coercivity (Hc), and interparticle exchange coupling (IEC). The MgO substrate promotes PMA of the film because of interfacial control of the FePt lattice orientation. The AIN compound is doped to increase the difference of surface energy between FePt layer and MgO substrate and to suppress the growth of FePt grains, which takes control of island growth mode of FePt atoms. The AIN compound also acts as isolator of L1(0)-FePt islands to pin the sites of FePt domains, resulting in the tunability of Hc and IEC of the films.

  6. Highly (001) oriented L1{sub 0}-CoPt/TiN multilayer films on glass substrates with perpendicular magnetic anisotropy

    Energy Technology Data Exchange (ETDEWEB)

    An, Hongyu; Sannomiya, Takumi; Muraishi, Shinji; Nakamura, Yoshio; Shi, Ji, E-mail: shi.j.aa@m.titech.ac.jp [Department of Metallurgy and Ceramics Science, Tokyo Institute of Technology, 2-12-1, Ookayama, Meguro-ku, Tokyo 152-8552 (Japan); Xie, Qian; Zhang, Zhengjun [Key Laboratory of Advanced Materials, School of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China); Wang, Jian [National Institute for Materials Science (NIMS), Sengen 1-2-1, Tsukuba, Ibaraki 305-0047 (Japan)

    2015-03-15

    To obtain strong perpendicular magnetic anisotropy (PMA) based on L1{sub 0} structure for magnetic storage devices, costly single crystalline substrates are generally required to achieve (001) texture. Recently, various studies also have focused on depositing different kinds of seed layers on glass or other amorphous substrates to promote (001) preferred orientation of L1{sub 0} CoPt and FePt. TiN is a very promising seed layer material because of its cubic crystalline structure (similar to MgO) and excellent diffusion barring property even at high temperatures. In the present work, highly (001) oriented L1{sub 0}-CoPt/TiN multilayer films have been successfully deposited on glass substrates. After annealing at 700 °C, the film exhibits PMA, and a strong (001) peak is detected from the x-ray diffraction profiles, indicating the ordering transformation of CoPt layers from fcc (A1) to L1{sub 0} structure. It also is found that alternate deposition of cubic TiN and CoPt effectively improves the crystallinity and (001) preferred orientation of CoPt layers. This effect is verified by the substantial enhancement of (001) reflection and PMA with increasing the period number of the multilayer films.

  7. Formation of hard magnetic L1{sub 0}-FePt/FePd monolayers from elemental multilayers

    Energy Technology Data Exchange (ETDEWEB)

    Goo, Nam Hoon

    2007-06-18

    In this thesis, ordered L1{sub 0}-FePt and FePd films of different nominal compositions are prepared from Fe/Pt and Fe/Pd multilayers by annealing. In case of the L1{sub 0}-FePt films the composition of the films is modified by changing the individual elemental layer thicknesses in the multilayer precursors. This simple variation of the composition is the great advantage of the multilayer approach compared to sputtering single alloy layer from an alloy target. The formation mechanism of the fct phase from the multilayers and the microstructural properties are investigated. The characteristics of the hysteresis loop (coercivity {mu}{sub 0}H{sub c}, remanence J{sub r}) and of the intrinsic magnetic properties (anisotropy constant K{sub l}, spontaneous polarization J{sub s}, exchange constant A) of the ordered L1{sub 0}-FePt and FePd films are studied. The effects of the composition of the L1{sub 0}-FePt films on the microstructural and magnetic properties are investigated. The microstructure of these ordered L1{sub 0}-FePt films are then correlated to the magnetic properties with microstructural parameters by investigating the temperature dependence of the coercivity. (orig.)

  8. Optimization of L1{sub 0} FePt/Fe{sub 45}Co{sub 55} thin films for rare earth free permanent magnet applications

    Energy Technology Data Exchange (ETDEWEB)

    Giannopoulos, G., E-mail: g.giannopoulos@inn.demokritos.gr; Psycharis, V.; Niarchos, D. [INN, NCSR Demokritos, Athens 15310 (Greece); Reichel, L. [IFW Dresden, P.O. Box 270116, 01171 Dresden (Germany); TU Dresden, Institute for Materials Science, 01062 Dresden (Germany); Markou, A.; Panagiotopoulos, I. [Department of Materials Science and Engineering, University of Ioannina, Ioannina 45110 (Greece); Damm, C.; Fähler, S. [IFW Dresden, P.O. Box 270116, 01171 Dresden (Germany); Khan, Imran; Hong, Jisang [Department of Physics, Pukyong National University, Busan 608-737 (Korea, Republic of)

    2015-06-14

    The magnetic properties of magnetron sputtered bilayers consisting of Fe{sub 45}Co{sub 55} ultrathin layers on top of L1{sub 0} FePt films epitaxially grown on MgO substrates are studied in view of their possible application as rare earth free permanent magnets. It is found that FePt layers induce a tetragonal distortion to the Fe-Co layers which leads to increased anisotropy. This allows to take advantage of the Fe-Co high magnetic moment with less significant loss of the coercivity compared to a typical hard/soft exchange spring system. A maximum energy product approaching 50 MGOe is obtained for a FePt(7 ML)/FeCo/(5 ML) sample. The results are in accordance with first-principles computational methods, which predict that even higher energy products are possible for micromagnetically optimized microstructures.

  9. Growth, structure and magnetic properties of FePt nanostructures on NaCl(001) and MgO(001)

    International Nuclear Information System (INIS)

    Liscio, F; Maret, M; Doisneau-Cottignies, B; Makarov, D; Albrecht, M; Roussel, H

    2010-01-01

    A comparison of the structural and magnetic properties of FePt nanostructures grown at different temperatures on NaCl(001) and MgO(001) substrates is presented. A strong influence of the deposition temperature on the epitaxial growth as well as on the size distribution of FePt nanostructures grown on NaCl substrates is observed. In spite of a large lattice mismatch between FePt and NaCl, a 'cube-over-cube' growth of nanostructures with a narrow size distribution was achieved at 520 K. Moreover, the growth of FePt nanostructures on NaCl(001) is not preceded by the formation of a wetting layer as observed on MgO(001). The higher degree of L1 0 chemical ordering in FePt nanostructures grown on MgO(001) accompanied by the absence of L1 0 variants with an in-plane tetragonal c-axis indicates that the tensile epitaxial stress induced by the MgO substrate is a key factor in the formation of the L1 0 phase with an out-of-plane c-axis. Superparamagnetic behavior is revealed for the FePt nanostructures grown on NaCl(001) due to their small size and relatively poor chemical order.

  10. Effect of TiON–MgO intermediate layer on microstructure and magnetic properties of L1{sub 0} FePt–C–SiO{sub 2} films

    Energy Technology Data Exchange (ETDEWEB)

    Deng, J.Y. [Department of Materials Science and Engineering, National University of Singapore, Singapore 117576 (Singapore); Dong, K.F. [School of Automation, China University of Geosciences, Wuhan 430074 (China); Peng, Y.G.; Ju, G.P. [Seagate Technology, Fremont, CA 94538 (United States); Hu, J.F. [Data Storage Institute (DSI), Singapore 117608 (Singapore); Chow, G.M.; Chen, J.S. [Department of Materials Science and Engineering, National University of Singapore, Singapore 117576 (Singapore)

    2016-11-01

    The microstructure and magnetic properties of L1{sub 0} FePt–C–SiO{sub 2} films grown on TiON–MgO intermediate layer were studied. TiON–MgO layer was deposited by co-sputtering TiN and MgO–TiO{sub 2} targets at 380 °C. With increasing MgO–TiO{sub 2} doping concentration, the contact angle between FePt grains with intermediate layer gradually increased, and it was close to 90° when the volume percentage of MgO–TiO{sub 2} reached 30%. At this condition, a high out-of-plane coercivity of 19.1 kOe was obtained, while the opening-up of in-plane M-H loop was very narrow. Moreover, it was found that the out-of-plane coercivity can be further improved to 21.6 kOe, by slightly increasing the percentage of MgO–TiO{sub 2} to 35 vol%. - Highlights: • The effect of TiON–MgO intermediate layer was studied. • With increasing the MgO composition, the surface energy of intermediate layer increased, and the FePt/TiON–MgO interfacial energy decreased. The contact angle of FePt grains with intermediate layer increased with the MgO composition, and 90° contact angle could be achieved by optimizing the MgO composition. • Good perpendicular magnetic anisotropy was retained with large out-of-plane coercivity and narrow in-plane opening-up.

  11. Origin of open recoil curves in L1_0-A1 FePt exchange coupled nanocomposite thin film

    International Nuclear Information System (INIS)

    Goyal, Rajan; Kapoor, Akanksha; Lamba, S.; Annapoorni, S.

    2016-01-01

    Mixed phase FePt systems with intergranular coupling may be looked upon as natural exchange spring systems. The coupling strength between the soft and hard phase in these systems can be analyzed using recoil curves. However, the origin of open recoil curves depicting the breakdown of exchange coupling or anisotropy variation in hard phase is still an ambiguity and requires an in-depth analysis. In order to investigate this, an analysis of the recoil curves for L1_0–A1 FePt nanocomposite thin films of varying thickness have been performed. The switching field distribution reveals that the maximum of openness of recoil curve is directly proportional to the amount of uncoupled soft phase present in the system. The coupling between the hard and soft phase is also found to increase with the thickness of the film. Monte Carlo simulations on a model three dimensional array of interacting nanomagnetic grains provide further insight into the effect of inter granular exchange interactions between the soft and hard phases. - Highlights: • L1_0-A1 FePt nanocomposites thin films of different thickness have been fabricated by DC sputtering. • Hysteresis curve measurements exhibit perfect single phase (L1_0) like behavior for thicker films. • SFD reveals that the openness of recoil curves is directly linked with the amount of uncoupled soft (A1) phase. • Monte Carlo simulation predicts that the extent of exchange interaction increases with thickness of the film.

  12. Origin of open recoil curves in L1{sub 0}-A1 FePt exchange coupled nanocomposite thin film

    Energy Technology Data Exchange (ETDEWEB)

    Goyal, Rajan [Department of Physics and Astrophysics, University of Delhi, Delhi 110007 (India); Kapoor, Akanksha [M. Tech Nanoscience and Nanotechnology, University of Delhi, Delhi 110007 (India); Lamba, S. [School of Sciences, Indira Gandhi National Open University, New Delhi 110068 (India); Annapoorni, S., E-mail: annapoornis@yahoo.co.in [Department of Physics and Astrophysics, University of Delhi, Delhi 110007 (India)

    2016-11-15

    Mixed phase FePt systems with intergranular coupling may be looked upon as natural exchange spring systems. The coupling strength between the soft and hard phase in these systems can be analyzed using recoil curves. However, the origin of open recoil curves depicting the breakdown of exchange coupling or anisotropy variation in hard phase is still an ambiguity and requires an in-depth analysis. In order to investigate this, an analysis of the recoil curves for L1{sub 0}–A1 FePt nanocomposite thin films of varying thickness have been performed. The switching field distribution reveals that the maximum of openness of recoil curve is directly proportional to the amount of uncoupled soft phase present in the system. The coupling between the hard and soft phase is also found to increase with the thickness of the film. Monte Carlo simulations on a model three dimensional array of interacting nanomagnetic grains provide further insight into the effect of inter granular exchange interactions between the soft and hard phases. - Highlights: • L1{sub 0}-A1 FePt nanocomposites thin films of different thickness have been fabricated by DC sputtering. • Hysteresis curve measurements exhibit perfect single phase (L1{sub 0}) like behavior for thicker films. • SFD reveals that the openness of recoil curves is directly linked with the amount of uncoupled soft (A1) phase. • Monte Carlo simulation predicts that the extent of exchange interaction increases with thickness of the film.

  13. Thickness dependence of magnetization reversal mechanism in perpendicularly magnetized L1{sub 0} FePt films

    Energy Technology Data Exchange (ETDEWEB)

    Bi, Mei; Wang, Xin, E-mail: xinwang@uestc.edu.cn; Lu, Haipeng; Zhang, Li; Deng, Longjiang; Xie, Jianliang

    2017-04-15

    We have studied the magnetic switching behavior of L1{sub 0}-ordered FePt films with varying thickness. It was found that coercivity is strongly dependent on the film thickness. The obvious variations of the coercivity in the thin films are confirmed by the measurements of structural and magnetic properties. With increasing thickness, the degree of L1{sub 0} chemical ordering increased, while the magnetization reversal process transforms from a pinned two-steps magnetization reversal to a comparatively smooth domain wall motion behavior. Although considering anisotropy, exchange interaction and applied magnetic field, the switching behavior in films is quite complex, the main features of the magnetization reversal mechanism can be understood by performing detailed investigation on the effect of the deposition temperature and the angle of magnetic field. - Highlights: • Series of FePt films with L1{sub 0} phase have been prepared. • We focused on the magnetization reversal mechanism with varying thicknesses. • The angle-dependence of switching process is revealed in the FePt films. • Different switching mechanisms were found by increasing the film thickness.

  14. Orientation and magnetic properties of FePt and CoPt films grown on MgO(1 1 0) single-crystal substrate by electron-beam coevaporation

    Energy Technology Data Exchange (ETDEWEB)

    Yu Minghui [Department of Materials Science and Engineering, University of Maryland, College Park, MD 20742 (United States); Department of Physics, University of Texas at Arlington, Arlington, TX 76019 (United States); Advanced Materials Research Institute, University of New Orleans, New Orleans, LA 70148 (United States)], E-mail: myu1@uno.edu; Ohguchi, H.; Zambano, A.; Takeuchi, I. [Department of Materials Science and Engineering, University of Maryland, College Park, MD 20742 (United States); Liu, J.P. [Department of Physics, University of Texas at Arlington, Arlington, TX 76019 (United States); Josell, D.; Bendersky, L.A. [Metallurgy Division, Materials Science and Engineering Laboratory, National Institute of Standards and Technology, Gaithersburg, MD 20899 (United States)

    2007-09-25

    We have studied the orientation and magnetic properties of FePt and CoPt films deposited by electron-beam co-evaporation on MgO(1 1 0) single-crystal substrates at substrate temperatures from 500 to 700 deg. C. We observed that long-range chemical ordering of the L1{sub 0} structure occurred over the entire range of substrate temperatures in FePt films and at 600 deg. C and up in CoPt films. Growth of FePt and CoPt yielded epitaxial films with cube-on-cube orientation of the pseudo-cubic L1{sub 0} lattice with respect to the cubic MgO. X-ray diffraction patterns and magnetization loops of the FePt and CoPt films revealed the existence of L1{sub 0} domains with the tetragonal c axis inclined at 45 deg. to the film plane, orientations (0 h h) and (h 0 h), as well as L1{sub 0} domains with the tetragonal c axis in the plane of the film, orientation (h h 0). The FePt and CoPt films for which X-ray diffraction indicated tetragonal phase was present all exhibited hard magnetic properties with easy axis along the [0 0 1] substrate direction as well as large in-plane magnetocrystalline anisotropy.

  15. XMCD study of CoPt nanoparticles embedded in MgO and amorphous carbon matrices

    International Nuclear Information System (INIS)

    Tournus, F.; Blanc, N.; Tamion, A.; Ohresser, P.; Perez, A.; Dupuis, V.

    2008-01-01

    We report the synthesis and characterization of CoPt nanoparticles, using X-ray magnetic circular dichroism (XMCD) at the Co L 2,3 edges. Clusters are produced in ultra-high vacuum conditions, following a physical route, and embedded in non-metallic matrices: MgO and amorphous carbon (a-C). In MgO, Co atoms are partially oxidized, which goes with a μ L /μ S enhancement. On the contrary, a-C appears as a very suitable matrix. In particular, annealing of CoPt cluster embedded in a-C is able to promote L 1 0 chemical order, without alteration of the sample. This transformation, which has been directly evidenced by transmission electron microscopy observations, is accompanied by a striking augmentation of μ S , μ L and the μ L /μ S ratio of Co. The presence of Pt leads to an enhanced Co magnetic moment, as compared to Co bulk, even for the chemically disordered alloy. Moreover, the high value of 1.91μ B /at. measured for μ S is unusual for Co and must be a signature of chemical order in CoPt alloy nanoparticles

  16. Growth and structure of L1 sub 0 ordered FePt films on GaAs(001)

    CERN Document Server

    Nefedov, A; Theis-Broehl, K; Zabel, H; Doi, M; Schuster, E; Keune, W

    2002-01-01

    The structural properties of epitaxial L1 sub 0 ordered FePt(001) films, grown by molecular beam epitaxy (alternating deposition of Fe and Pt atomic layers) on buffer-Pt/seed-Fe/GaAs(001) have been studied by in situ reflection high-energy electron diffraction and by ex situ x-ray scattering as a function of the growth conditions. Reflection high-energy electron diffraction intensity oscillations measured during FePt layer growth provide evidence for island growth at T sub s = 200 deg. C and quasi layer-by-layer growth at T sub s = 350 deg. C. From small-angle and wide-angle x-ray scattering it was found that the degree of epitaxy depends critically on morphology of the seed layer and the substrate roughness. X-ray diffraction analysis showed that the long-range order parameter increases from near zero for films grown at 200 deg. C to 0.65 for films grown at 350 deg. C. This confirms the fact that the order parameter is mainly determined by the surface mobility of the atoms which is controlled experimentally ...

  17. Preventing dewetting during rapid-thermal annealing of FePt films with enhanced L1{sub 0} ordering by introducing Ag cap-layers

    Energy Technology Data Exchange (ETDEWEB)

    Hsiao, S.N., E-mail: pmami.hsiao@gmail.com [Department of Materials Science and Engineering, Feng Chia University, Taichung 40724, Taiwan (China); Department of Power Mechanical Engineering, National Tsing Hua University, Hsinchu 30013, Taiwan (China); Wu, S.C. [Department of Materials Science and Engineering, National Chung Hsing University, Taichung 40227, Taiwan (China); Liu, S.H. [Department of Materials Science and Engineering, Feng Chia University, Taichung 40724, Taiwan (China); Tsai, J.L., E-mail: tsaijl@dragon.nchu.edu.tw [Department of Materials Science and Engineering, National Chung Hsing University, Taichung 40227, Taiwan (China); Chen, S.K. [Department of Materials Science and Engineering, Feng Chia University, Taichung 40724, Taiwan (China); Chang, Y.C. [Department of Materials Science and Engineering, National Tsing Hua University, Hsinchu 30013, Taiwan (China); Lee, H.Y. [Scientific Research Division, National Synchrotron Radiation Research Center, Hsinchu 30077, Taiwan (China)

    2015-11-15

    High-order FePt continuous films with a strong (001) texture were fabricated on a glass substrate by introducing Ag layers and rapid thermal annealing (RTA). The dewetting of the (001)-textured FePt was suppressed during RTA with high heating rates (>80 K/s). The Ag cap layers not only increased the in-plane tensile stress, but also improved the (001) anisotropy and L1{sub 0} ordering of the FePt layers. All continuous Ag/FePt bilayer films possessed strong perpendicular anisotropies and high-ordered states irrespective of the Ag layer thickness. - Highlights: • Dewetting of (001) FePt fims were suppressed by introducing Ag cap layers. • Ag layers enhanced in-plane tensile stress, (001) texture and L1{sub 0} ordering. • Irrespective of Ag thickness, the Ag/FePt films exhibited strong (001) texture.

  18. Influence of the phenomena occurring at the interface between L1{sub 0}-ordered-FePt and Fe on the coercivity behavior

    Energy Technology Data Exchange (ETDEWEB)

    Carbucicchio, Massimo, E-mail: massimo.carbucicchio@ino.it [University of Parma, Physics Department (Italy)

    2016-12-15

    L1{sub 0}-ordered FePt/Fe thin bi-layers were grown using a molecular beam epitaxy onto (100)-MgO substrates changing the soft Fe layer thickness. The study of the intermixing phenomena occurring at the hard/soft interfaces was carried out using surface Mössbauer spectroscopy. The magnetic properties of the samples were analyzed with a magneto-optical Kerr effect magnetometer. The surface morphology and the magnetic domains were analyzed with an UHV atomic and magnetic force microscopy in tapping and lift mode respectively.The present work clearly demonstrates that the degree of interface intermixing and reactions is the responsible for the coercivity behavior in exchange-spring magnets.

  19. FePt and CoPt nanoparticles prepared by micellar method. Effects of A1{yields}L1{sub 0} transition on oxidation resistance and magnetic properties

    Energy Technology Data Exchange (ETDEWEB)

    Han, Luyang

    2011-02-15

    In this thesis FePt and CoPt alloy nanoparticles are prepared with reverse micelles. The metallic nanoparticles with diameters of 2-12 nm and interparticle distances of 20-140 nm are obtained on Si substrates. The magnetic properties of FePt and CoPt nanoparticles as well as oxidation behavior of FePt nanoparticles are investigated. X-ray magnetic circular dichroism (XMCD) measurements on 5.8 nm FePt nanoparticles after hydrogen plasma reduction at 300 C reveals that the magnetic moment per Fe atom and magnetic anisotropy energy match chemically disordered FePt in A1 phase. Annealing at 650 C transform portion of FePt particles to chemically ordered L1{sub 0} phase. The presense of nanoparticles in L1{sub 0} phase is identified by high-resolution transmission electronmicroscopy (HRTEM) investigation, where it is also observed that large fraction of the particles contain defects such as twin boundaries and stacking faults. By increasing the annealing temperature or prolonging annealing time, ratio of transformed particles increases. The average magnetic anisotropy energy of the transformed particles is below 30% of the value of bulk FePt in L1{sub 0} phase. Annealing at above 750 C, however, decreases the average magnetic anisotropy in the sample. Similar A1 {yields} L1{sub 0} transition is observed in FePt nanoparticles with different diameters as well as in CoPt nanoparticles. The spin moment of Fe in FePt nanoparticles decreases with smaller particle diameter, while the orbital moment stays almost constant. Magnetic moments at room temperature are significantly reduced compared to those at low temperature, suggesting the Curie temperatures in FePt and CoPt nanoparticles are significantly lower than in the bulk. The annealing also induces Pt segregation towards the surface in FePt nanoparticles, which is identified by the decreased apparent Fe content measured by X-ray photoelectron spectroscopy (XPS) and X-ray absorption spectroscopy (XAS). The segregation of Pt

  20. Evolution of microstructure and residual stress on L1{sub 0} ordering in FePt thin films with different initial stress states

    Energy Technology Data Exchange (ETDEWEB)

    Hsiao, S.N., E-mail: pmami.hsiao@gmail.com [Department of Materials Science and Engineering, Feng Chia University, Taichung 407, Taiwan (China); Yuan, F.T. [iSentek Ltd., Advanced Sensor Laboratory, New Taipei City 221, Taiwan (China); Chen, S.K. [Department of Materials Science and Engineering, Feng Chia University, Taichung 407, Taiwan (China); Sun, A.C. [Department of Chemical Engineering and Materials Science, Yuan Ze University, Jungli 320, Taiwan (China); Su, S.H.; Chiu, K.F. [Department of Materials Science and Engineering, Feng Chia University, Taichung 407, Taiwan (China)

    2016-01-15

    We have characterized the dependence of microstructure, and internal strain/stress on L1{sub 0} ordering in 40 nm thick FePt films with different initial stresses. The microstructural and crystallographic results indicate that defect annihilation and grain growth induced an increase in tensile stress of ~1 GPa before extensive L1{sub 0} ordering. The induced tensile stress can efficiently facilitate the nucleation of L1{sub 0} phase owing to that the volume expansion of L1{sub 0} ordering and atomic rearrangement neutralizes the tensile stress. If the as-deposited FePt film has a highly compressive state, the induced tensile stress will be canceled out and ordering is retarded, which results in a higher ordering temperature. - Highlights: • Microstructure-stress connection in FePt films was studied. • Initial stress alters microstructure and stress evolution during annealing. • Densification induces tensile stress of ~1 GPa before extensive L1{sub 0} ordering. • Induced tensile stress can efficiently facilitate the nucleation of L1{sub 0} phase. • Compressively initial stress results in a higher ordering temperature .

  1. Microstructure and magnetic properties of nanocomposite FePt/MgO and FePt/Ag films

    International Nuclear Information System (INIS)

    Chen, S.C.; Kuo, P.C.; Sun, A.C.; Chou, C.Y.; Fang, Y.H.; Wu, T.H.

    2006-01-01

    An in-plane magnetic anisotropy of FePt film is obtained in the MgO 5 nm/FePt t nm/MgO 5 nm films (where t=5, 10 and 20 nm). Both the in-plane coercivity (H c- parallel ) and the perpendicular magnetic anisotropy of FePt films are increased when introducing an Ag-capped layer instead of MgO-capped layer. An in-plane coercivity is 3154 Oe for the MgO 5 nm/FePt 10 nm/MgO 5 nm film, and it can be increased to 4846 Oe as a 5 nm Ag-capped layer instead of MgO-capped layer. The transmission electron microscopy (TEM)-energy disperse spectrum (EDS) analysis shows that the Ag mainly distributed at the grain boundary of FePt, that leads the increase of the grain boundary energy, which will enhance coercivity and perpendicular magnetic anisotropy of FePt film

  2. In situ x-ray reflectivity and grazing incidence x-ray diffraction study of L 1{sub 0} ordering in {sup 57}Fe/Pt multilayers

    Energy Technology Data Exchange (ETDEWEB)

    Raghavendra Reddy, V; Gupta, Ajay; Gome, Anil [UGC-DAE Consortium for Scientific Research, University Campus, Khandwa Road, Indore-452 017 (India); Leitenberger, Wolfram [Institute of Physics, University of Potsdam, 14469 Potsdam (Germany); Pietsch, U [Physics Department, University of Siegen, D-57068 Siegen (Germany)], E-mail: vrreddy@csr.ernet.in, E-mail: varimalla@yahoo.com

    2009-05-06

    In situ high temperature x-ray reflectivity and grazing incidence x-ray diffraction measurements in the energy dispersive mode are used to study the ordered face-centered tetragonal (fct) L 1{sub 0} phase formation in [Fe(19 A)/Pt(25 A)]{sub x 10} multilayers prepared by ion beam sputtering. With the in situ x-ray measurements it is observed that (i) the multilayer structure first transforms to a disordered FePt and subsequently to an ordered fct L 1{sub 0} phase, (ii) the ordered fct L 1{sub 0} FePt peaks start to appear at 320 deg. C annealing, (iii) the activation energy of the interdiffusion is 0.8 eV and (iv) ordered fct FePt grains have preferential out-of-plane texture. The magneto-optical Kerr effect and conversion electron Moessbauer spectroscopies are used to study the magnetic properties of the as-deposited and 400 deg. C annealed multilayers. The magnetic data for the 400 {sup 0}C annealed sample indicate that the magnetization is at an angle of {approx}50 deg. from the plane of the film.

  3. Development of novel FePt/nanodiamond hybrid nanostructures: L1{sub 0} phase size-growth suppression and magnetic properties

    Energy Technology Data Exchange (ETDEWEB)

    Douvalis, A. P., E-mail: adouval@uoi.gr; Bourlinos, A. B. [University of Ioannina, Physics Department (Greece); Tucek, J.; Čépe, K. [Palacký University Olomouc, Regional Centre of Advanced Technologies and Materials, Department of Physical Chemistry, Faculty of Science (Czech Republic); Bakas, T. [University of Ioannina, Physics Department (Greece); Zboril, R. [Palacký University Olomouc, Regional Centre of Advanced Technologies and Materials, Department of Physical Chemistry, Faculty of Science (Czech Republic)

    2016-05-15

    A new type of hybrid nanomaterial composed of magnetic FePt nanoparticles grown on the surface of nanodiamond nanotemplate assemblies is described for the first time. Post annealing in vacuum of the as-made nanomaterial bearing cubic A1 soft magnetic FePt nanoparticles leads to the development of FePt nanoparticles with tetragonal L1{sub 0} hard, magnetic-phase characteristics, leaving untouched the nanodiamond nanotemplate assemblies. X-ray diffraction, high-resolution transmission electron microscopy including chemical mapping (HRTEM/HAADF), magnetization measurements, and {sup 57}Fe Mössbauer spectroscopy data show that the magnetic FePt nanoparticles, with average sizes of 3 and 8 nm in the as-made and annealed hybrids, respectively, are homogenously distributed within the nanodiamond template in both nanomaterials. As a consequence, their structural, morphological, and magnetic properties differ significantly from the corresponding properties of the nonsupported (free) as-made and annealed FePt nanoparticles with average sizes of 6 and 32 nm, respectively, developed by the same methods. This spatial isolation suppresses the size-growth of the FePt nanoparticles during the post-annealing procedure, triggering superparamagnetic relaxation phenomena, which are exposed as a combination of hard and soft magnetic-phase characteristics.

  4. Magnetic and structural properties of L1{sub 1} type CoPt-C ordered alloy perpendicular films as a function of C content

    Energy Technology Data Exchange (ETDEWEB)

    Shimatsu, T; Kataoka, H; Aoi, H [Research Institute of Electrical Communication, Tohoku University, Sendai, 980-8577 (Japan); Sato, H; Okamoto, S; Kitakami, O, E-mail: shimatsu@riec.tohoku.ac.j [Institute of Multidisciplinary Research for Advanced Materials, Tohoku University, Sendai, 980-8577 (Japan)

    2010-01-01

    Magnetic and structural properties of L1{sub 1} type (Co{sub 0.5}Pt{sub 0.5}){sub 100-X}-C{sub X} ordered alloy perpendicular films, fabricated on 2.5 inch size glass disks by sputter deposition, were examined as a function of C content, X. L1{sub 1} type Co{sub 0.5}Pt{sub 0.5}-C polycrystalline films (10 nm thickness), with <111> axis (the easy axis) perpendicular to the film plane, were successfully fabricated even for a 30 vol% C content. Structural analysis indicated the segregation of C to the grain boundaries. Uniaxial magnetic anisotropy, K{sub u}, of Co{sub 0.5}Pt{sub 0.5} films without C addition was relatively low, about 1.5x10{sup 7} erg/cm{sup 3} under the present deposition conditions. However, the addition of 5 vol.% C to Co-Pt films enhanced the ordering, resulting in an increase in K{sub u} to around 2.5 x10{sup 7} erg/cm{sup 3}. A further increase in C content reduced K{sub u}; however, K{sub u} maintained a relatively large value of about 1.8x10{sup 7} erg/cm{sup 3} even for a 20vol% C content, without degrading the easy axis orientation perpendicular to the film plane. Experimental results demonstrated the potential of the L1{sub 1} type Co{sub 0.5}Pt{sub 0.5}-C films for use in granular media applications, due to their very high K{sub u}, the relatively low fabrication temperature, and good controllability of the grain orientation.

  5. Role of Ta-spacer layer on tuning the tilt angle magnetic anisotropy of L1{sub 1}-CoPt/Ta/NiFe exchange springs

    Energy Technology Data Exchange (ETDEWEB)

    Saravanan, P., E-mail: psdrdo@gmail.com [Defence Metallurgical Research Laboratory, Hyderabad 500058 (India); Talapatra, A.; Mohanty, J. [Department of Physics, Indian Institute of Technology Hyderabad, Hyderabad 502285 (India); Hsu, Jen-Hwa, E-mail: jhhsu@phys.ntu.edu.tw [Department of Physics, National Taiwan University, Taipei 106, Taiwan (China); Kamat, S.V. [Defence Metallurgical Research Laboratory, Hyderabad 500058 (India)

    2017-06-15

    Highlights: • Role of Ta-spacer layer in L1{sub 1}-CoPt(10 nm)/Ta//NiFe(4 nm) trilayers was investigated. • Domain size increased at the expense of magnetic phase contrast with increasing t{sub Ta}. • Tilt angle magnetization increased from 43° to 77° upon increasing t{sub Ta} (0–2.5 nm). • Micromagnetic studies confirmed the existence of tilted magnetic anisotropy. • Ta-spacer is effective in preserving competing anisotropies of CoPt and NiFe-layers. - Abstract: L1{sub 1}-CoPt/Ta/NiFe trilayers are chosen as model films for probing the role of spacer layer on tuning the tilt angle magnetization (θ{sub M}) in such exchange springs. For this purpose, a non-magnetic layer (Ta) with varying thickness (t{sub Ta}) from 0 to 2.5 nm was inserted between 10-nm thick CoPt film exhibiting strong perpendicular magnetic anisotropy (PMA) and 4-nm thick NiFe film having in-plane magnetic anisotropy (IMA). With the insertion of Ta-spacer, the magnetic hysteresis loops become more and more tilted as t{sub Ta} increases. Upon increasing the t{sub Ta} from 0 to 2.5 nm, the estimated SQR{sub ⊥} (=M{sub r⊥}/M{sub s⊥}) from the M–H loops is found to decrease moderately; while the θ{sub M} increases significantly from 43° to 77°. MFM images revealed maze-like domain patterns and the domain size tends to increase at the expense of magnetic phase contrast with increasing t{sub Ta}. Micro-magnetic simulation of tilt in the anisotropy axis with respect to the bare CoPt-layer showed a trend similar to that of those observed with the M–H loops obtained by VSM measurements. The results of present study suggest that the insertion of Ta-spacer is not only beneficial in terms of preserving the competing anisotropies such as PMA and IMA of CoPt and NiFe-layers respectively through weakened exchange coupling; but also, act as an appropriate means for realizing tunable tilted magnetic anisotropy in the L1{sub 1}-CoPt/NiFe exchange springs.

  6. The A1 to L10 transformation in FePt films with ternary alloying additions of Mg, V, Mn, and B

    International Nuclear Information System (INIS)

    Wang, B.; Barmak, K.; Klemmer, T. J.

    2011-01-01

    The impact of ternary additions of Mg, V, Mn, and B on the A1 [face centered cubic (fcc)] to L1 0 phase transformation has been studied. The films were cosputter deposited from elemental targets at room temperature and annealed after deposition. The films had Mg additions in the range ∼0-2.6 at.%, V additions in the range 0.7-12.2 at.%, Mn additions in the range 2.2-16.3 at.%, and B additions in the range 1.2-12.9 at.%. For all four ternary alloy systems, annealing resulted in the formation of no other phases than the L1 0 phase. Ternary additions of C than the binary FePt films with the same Pt content.

  7. High magnetic coercivity of FePt-Ag/MgO granular nanolayers

    Science.gov (United States)

    Roghani, R.; Sebt, S. A.; Khajehnezhad, A.

    2018-06-01

    L10-FePt ferromagnetic nanoparticles have a hight coercivity of Tesla order. Thus, these nanoparticles, with size of 10 to 15 nm and uniform surface distribution, are suitable in magnetic data storage technology with density of more than 1GB. In order to improve structural and magnetic properties of FePt nanoparticles, some elements and combinations have been added to compound. In this research, we show that due to the presence of the Ag, the phase transition temperature of FePt from fcc to L10-fct phase decreases. The presence of Ag as an additive in FePt-Ag nanocomposite, increases the magnetic coercivity. This nanocomposite, with 10% Ag, was deposited by magnetron sputtering on the MgO heat layer. VSM results of 10 nm nanoparticles show that coercivity has increased up to 1.4 T. XRD and FESEM results confirm that the size of the L10-FePt nanoparticles are 10 nm and their surface distribution are uniform. Ag gradually form nano scale clusters with separate lattice and FePt-Ag nanocomposite appears. The result of this process is emptiness of Ag position in FePt-fcc lattice. So, the mobility of Fe and Pt atoms in this lattice increases and it can be possible for them to move in lower temperature. This mechanism explain the effect of Ag on decreasing the transition temperature to fct-L10 phase, and hight coercivity of FePt nanoparticles.

  8. Strength of FePd/MgO and FePt/MgO interfaces from first principles

    Science.gov (United States)

    Černý, M.

    2018-04-01

    Cleavage characteristics such as the cleavage energy and the cleavage stress of FePd/MgO and FePt/MgO interfaces are computed from first principles. Considering several possible cleavage planes, the weakest link in these systems is found as the plane with the lowest cleavage stress. This weakest plane is identified in both systems with the interface plane, where the cohesion is reduced by 30% compared to the MgO bulk. Two distinct models of tensile test are employed to verify the results and convergence of computed values with respect to size of the simulation cell is discussed.

  9. Ab initio investigation of superconductivity in orthorhombic MgPtSi

    Energy Technology Data Exchange (ETDEWEB)

    Tütüncü, H.M., E-mail: tutuncu@sakarya.edu.tr [Sakarya Üniversitesi, Fen-Edebiyat Fakültesi, Fizik Bölümü, 54187, Adapazarı (Turkey); Sakarya Üniversitesi, BIMAYAM Biyomedikal, Manyetik ve Yarıiletken Malzemeler Araştırma Merkezi, 54187, Adapazarı (Turkey); Ertuǧrul Karaca [Sakarya Üniversitesi, Fen-Edebiyat Fakültesi, Fizik Bölümü, 54187, Adapazarı (Turkey); Srivastava, G.P. [School of Physics, University of Exeter, Stocker Road, Exeter EX4 4QL (United Kingdom)

    2016-07-15

    We have performed an ab initio study of electronic, vibrational and superconducting properties of the orthorhombic MgPtSi by employing the density functional theory, a linear-response formalism, and the plane-wave pseudopotential method. Our electronic results suggest that the density of states at the Fermi level is primarily contributed by Pt 5d and Si 3p states with much smaller contribution from Mg electronic states. Phonon anomalies have been found for all three acoustic branches. Due to these phonon anomalies, the acoustic branches make large contributions to the average electron-phonon coupling parameter. From the Eliashberg spectral function, the value of average electron-phonon coupling parameter is found to 0.707. Using this value, the superconducting critical temperature is obtained to be 2.4 K, in excellent accordance with its experimental value of 2.5 K. - Highlights: • The electronic structure of MgPtSi is studied using ab initio pseudopotential method. • Phonons and electron–phonon interaction in MgPtSi are studied using a linear response theory. • The acoustic phonon modes couple more strongly with electrons. • The value of λ is found to be 0.707 which shows that MgPtSi is a conventional honon-mediated superconductor. • The calculated T{sub c} of 2.4 K is in excellent accordance with its experimental value of 2.5 K.

  10. Nano-structure formation of Fe-Pt perpendicular magnetic recording media co-deposited with MgO, Al2O3 and SiO2 additives

    International Nuclear Information System (INIS)

    Safran, G.; Suzuki, T.; Ouchi, K.; Barna, P.B.; Radnoczi, G.

    2006-01-01

    Perpendicular magnetic recording media samples were prepared by sputter deposition on sapphire with a layer sequence of MgO seed-layer/Cr under-layer/FeSi soft magnetic under-layer/MgO intermediate layer/FePt-oxide recording layer. The effects of MgO, Al 2 O 3 and SiO 2 additives on the morphology and orientation of the FePt layer were investigated by transmission electron microscopy. The samples exhibited (001) orientation of the L1 FePt phase with the mutual orientations of sapphire substrate//MgO(100)[001]//Cr(100)[11-bar0]//FeSi(100)[11-bar0]//MgO(100) [001]//FePt(001)[100]. The morphology of the FePt films varied due to the co-deposited oxides: The FePt layers were continuous and segmented by stacking faults aligned at 54 o to the surface. Films with SiO 2 addition, beside the oriented columnar FePt grains, exhibited a fraction of misoriented crystallites due to random repeated nucleation. Al 2 O 3 addition resulted in a layered structure, i.e. an initial continuous epitaxial FePt layer covered by a secondary layer of FePt-Al 2 O 3 composite. Both components (FePt and MgO) of the MgO-added samples were grown epitaxially on the MgO intermediate layer, so that a nano-composite of intercalated (001) FePt and (001) MgO was formed. The revealed microstructures and formation mechanisms may facilitate the improvement of the structural and magnetic properties of the FePt-oxide composite perpendicular magnetic recording media

  11. Tuning anomalous Hall conductivity in L1[sub 0] FePt films by long range chemical ordering

    KAUST Repository

    Chen, M.; Shi, Z.; Xu, W. J.; Zhang, Xixiang; Du, J.; Zhou, S. M.

    2011-01-01

    For L10 FePt films, the anomalous Hall conductivity σ xy=-a σxx-b, where a=a0f(T), b=b 0f(T), and f (T) is the temperature dependence factor of the spontaneous magnetization. With increasing chemical long range ordering S, a0 changes its sign accompanied by a reduction of its magnitude and b0 increases monotonically. The spin-orbit coupling strength is suggested to increase with increasing S. As an approach, the long range chemical ordering can be used to control the anomalous Hall effect in ferromagnetic alloy films. © 2011 American Institute of Physics.

  12. Tuning anomalous Hall conductivity in L1[sub 0] FePt films by long range chemical ordering

    KAUST Repository

    Chen, M.

    2011-02-24

    For L10 FePt films, the anomalous Hall conductivity σ xy=-a σxx-b, where a=a0f(T), b=b 0f(T), and f (T) is the temperature dependence factor of the spontaneous magnetization. With increasing chemical long range ordering S, a0 changes its sign accompanied by a reduction of its magnitude and b0 increases monotonically. The spin-orbit coupling strength is suggested to increase with increasing S. As an approach, the long range chemical ordering can be used to control the anomalous Hall effect in ferromagnetic alloy films. © 2011 American Institute of Physics.

  13. Interplay between out-of-plane anisotropic L1{sub 1}-type CoPt and in-plane anisotropic NiFe layers in CoPt/NiFe exchange springs

    Energy Technology Data Exchange (ETDEWEB)

    Saravanan, P. [Department of Physics, National Taiwan University, Taipei 106, Taiwan (China); Defence Metallurgical Research Laboratory, Hyderabad 500058 (India); Hsu, Jen-Hwa, E-mail: jhhsu@phys.ntu.edu.tw; Tsai, C. L. [Department of Physics, National Taiwan University, Taipei 106, Taiwan (China); Tsai, C. Y.; Lin, Y. H. [Graduate Institute of Materials Science and Engineering, National Taiwan University, Taipei 106, Taiwan (China); Kuo, C. Y.; Wu, J.-C. [Department of Physics, National Chang Hua University of Education, Chang Hua 50000, Taiwan (China); Lee, C.-M. [Graduate School of Materials Science, National Yunlin University of Science and Technology, Douliou 64002, Taiwan (China)

    2014-06-28

    Films of L1{sub 1}-type CoPt/NiFe exchange springs were grown with different NiFe (Permalloy) layer thickness (t{sub NiFe} = 0–10 nm). X-ray diffraction analysis reveals that the characteristic peak position of NiFe(111) is not affected by the CoPt-layer—confirming the absence of any inter-diffusion between the CoPt and NiFe layers. Magnetic studies indicate that the magnetization orientation of NiFe layer can be tuned through varying t{sub NiFe} and the perpendicular magnetic anisotropy of L1{sub 1}-type CoPt/NiFe films cannot sustain for t{sub NiFe} larger than 3.0 nm due to the existence of exchange interaction at the interface of L1{sub 1}-CoPt and NiFe layers. Magnetic force microscopy analysis on the as-grown samples shows the changes in morphology from maze-like domains with good contrast to hazy domains when t{sub NiFe} ≥ 3.0 nm. The three-dimensional micro-magnetic simulation results demonstrate that the magnetization orientation in NiFe layer is not uniform, which continuously increases from the interface to the top of NiFe layer. Furthermore, the tilt angle of the topmost NiFe layers can be changed over a very wide range from a small number to about 75° by varying t{sub NiFe} from 1 to 10 nm. It is worth noting that there is an abrupt change in the magnetization direction at the interface, for all the t{sub NiFe} investigated. The results of present study demonstrate that the tunable tilted exchange springs can be realized with L1{sub 1}-type CoPt/NiFe bilayers for future applications in three-axis magnetic sensors or advanced spintronic devices demanding inclined magnetic anisotropy.

  14. Magnetic properties of soft layer/FePt-MgO exchange coupled composite Perpendicular recording media

    Institute of Scientific and Technical Information of China (English)

    Yin Jin-Hua; Takao Suzuki; Pan Li-Qing

    2008-01-01

    The magnetic properties of exchange coupled composite(ECC)media that are composed of perpendicular magnetic recording media FePt-MgO and two kinds of soft layers have been studied by using an x-ray diffractometer,a polar Kerr magneto-optical system(PMOKE)and a vibrating sample magnetometer(VSM).The results show that ECC media can reduce the coercivities of perpendicular magnetic recording media FePt-MgO.The ECC media with granular-type soft layers have weaker exchange couplings between magnetic grains and the magnetization process,for ECC media of this kind mainly follow the Stoner-Wohlfarth model.

  15. Surface enrichment of Pt in stable Pt-Ir nano-alloy particles on MgAl 2 O 4 spinel in oxidizing atmosphere

    Energy Technology Data Exchange (ETDEWEB)

    Li, Weizhen; Nie, Lei; Chen, Ying; Kovarik, Libor; Liu, Jun; Wang, Yong

    2017-04-01

    With the capability of MgAl2O4 spinel {111} nano-facets in stabilizing small Rh, Ir and Pt particles, bimetallic Ir-Pt catalysts on the same support were investigated, aiming at further lowering the catalyst cost by substituting expensive Pt with cheaper Ir in the bulk. Small Pt-Ir nano-alloy particles (< 2nm) were successfully stabilized on the spinel {111} nano-facets as expected. Interestingly, methanol oxidative dehydrogenation (ODH) rate on the surface Pt atoms increases with oxidizing aging but decreases upon reducing treatment, where Ir is almost inactive under the same reaction conditions. Up to three times enhancement in Pt exposure was achieved when the sample was oxidized at 800 °C in air for 1 week and subsequently reduced by H2 for 2 h, demonstrating successful surface enrichment of Pt on Pt-Ir nano-alloy particles. A dynamic stabilization mechanism involving wetting\

  16. Hyperfine interaction of 13O and 23Mg implanted in Pt

    International Nuclear Information System (INIS)

    Matsuta, K.; Yoshida, K.; Ozawa, A.; Momota, S.; Kobayashi, T.; Tanihata, I.; Alonso, J.R.; Krebs, G.F.; Symons, T.J.M.

    1996-01-01

    The spin relaxation time T 1 for short-lived beta emitters 13 O and 23 Mg implanted in Pt have been measured for the first time; T 1 T( 13 O)=2.90±0.65 Ks and T 1 T( 23 Mg)=1665±140 Ks. The Knight shift for 13 O in Pt was measured at 300 K to be K( 13 O)=+(4.23±0.14).10 -3 . In the case of 13 O, the Knight shift is unusually large and the relaxation time is unusually fast compared with other interstitial impurities in Pt. A KKR band-structure calculation reproduces the present large Knight shift fairly well. (orig.)

  17. Annealing effect on magnetic property and recording performance of [FePt/MgO]n perpendicular magnetic recording media

    International Nuclear Information System (INIS)

    Suzuki, Takao; Zhang, Zhengang; Singh, Amarendra K.; Yin, Jinhua; Perumal, A.; Osawa, Hiroshi

    2005-01-01

    Granular-type FePt perpendicular magnetic recording media with (001)-texture, obtained by annealing FePt/MgO multilayer films, are fabricated onto 2.5-in glass discs. For the sake of spin-stand testing, the coercivity of FePt films is carefully modulated by controlling the annealing conditions. With annealing, exchange coupling between FePt grains is decreased, indicated by the reductions in α value and activation volume. FePt ordering process is dependent on initial FePt/MgO multilayer structures, which governs the optimum annealing condition regarding coercivities and α(=4π(dM/dH)H=Hc). The SNR ratio exhibits a sensitive dependence on initial FePt/MgO multilayer structures as well as annealing conditions

  18. A comparative study of Mg and Pt contacts on semi-insulating GaAs: Electrical and XPS characterization

    Energy Technology Data Exchange (ETDEWEB)

    Dubecký, F., E-mail: elekfdub@savba.sk [Institute of Electrical Engineering, SAS, Dúbravská cesta 9, Bratislava, SK-84104 (Slovakia); Kindl, D.; Hubík, P. [Institute of Physics CAS, v.v.i., Cukrovarnická 10, CZ-16200 Prague (Czech Republic); Mičušík, M. [Polymer Institute, SAS, Dúbravská cesta 9, Bratislava, SK-84541 (Slovakia); Dubecký, M. [Department of Physics, Faculty of Science, University of Ostrava, 30. dubna 22, CZ-70103 Ostrava 1 (Czech Republic); Boháček, P.; Vanko, G. [Institute of Electrical Engineering, SAS, Dúbravská cesta 9, Bratislava, SK-84104 (Slovakia); Gombia, E. [IMEM-CNR, Parco area delle Scienze 37/A, Parma, I-43010 (Italy); Nečas, V. [Faculty of Electrical Engineering and Information Technology, SUT, Ilkovičova 3, Bratislava, SK-81219 (Slovakia); Mudroň, J. [Department of Electronics, Academy of Armed Forces, Demänová 393, Liptovský Mikuláš, SK-03106 (Slovakia)

    2017-02-15

    Highlights: • Explored were diodes with full-area low/high work function metal contacts on semi-insulating GaAs (S). • The Mg-S-Mg diode is promising for radiation detectors for its low high-field current. • The XPS analysis of Mg-S interface shows presence of MgO instead of Mg metal. - Abstract: We present a comparative study of the symmetric metal-SI GaAs-metal (M-S-M) diodes with full-area contacts on both device sides, in order to demonstrate the effect of contact metal work function in a straightforward way. We compare the conventional high work function Pt contact versus the less explored low work function Mg contact. The Pt-S-Pt, Mg-S-Mg and mixed Mg-S-Pt structures are characterized by the current-voltage measurements, and individual Pt-S and Mg-S contacts are investigated by the X-ray photoelectron spectroscopy (XPS). The transport measurements of Mg-S-Pt structure show a significant current decrease at low bias while the Mg-S-Mg structure shows saturation current at high voltages more than an order of magnitude lower with respect to the Pt-S-Pt reference. The phenomena observed in Mg-containing samples are explained by the presence of insulating MgO layer at the M-S interface, instead of the elementary Mg, as confirmed by the XPS analysis. Alternative explanations of the influence of MgO layer on the effective resistance of the structures are presented. The reported findings have potential applications in M-S-M sensors and radiation detectors based on SI GaAs.

  19. Highly selective bimetallic Pt-Cu/Mg(Al)O catalysts for the aqueous-phase reforming of glycerol

    NARCIS (Netherlands)

    Boga, D.A.; Oord, R.; Beale, A.M.; Chung, Y.M.; Bruijnincx, P.C.A.; Weckhuysen, B.M.

    2013-01-01

    Monometallic Pt and bimetallic Pt-Cu catalysts supported on Mg(Al)O mixed oxides, obtained by calcination of the corresponding layered double hydroxides (LDHs), were prepared and tested in the aqueous-phase reforming (APR) of glycerol. The effect of the Mg/Al ratio and calcination temperature of the

  20. Localized-Surface-Plasmon Enhanced the 357 nm Forward Emission from ZnMgO Films Capped by Pt Nanoparticles

    Directory of Open Access Journals (Sweden)

    Song XM

    2009-01-01

    Full Text Available Abstract The Pt nanoparticles (NPs, which posses the wider tunable localized-surface-plasmon (LSP energy varying from deep ultraviolet to visible region depending on their morphology, were prepared by annealing Pt thin films with different initial mass-thicknesses. A sixfold enhancement of the 357 nm forward emission of ZnMgO was observed after capping with Pt NPs, which is due to the resonance coupling between the LSP of Pt NPs and the band-gap emission of ZnMgO. The other factors affecting the ultraviolet emission of ZnMgO, such as emission from Pt itself and light multi-scattering at the interface, were also discussed. These results indicate that Pt NPs can be used to enhance the ultraviolet emission through the LSP coupling for various wide band-gap semiconductors.

  1. Large enhancement of Blocking temperature by control of interfacial structures in Pt/NiFe/IrMn/MgO/Pt multilayers

    Directory of Open Access Journals (Sweden)

    Xi Chen

    2015-09-01

    Full Text Available The Blocking temperature (TB of Pt/NiFe/IrMn/MgO/Pt multilayers was greatly enhanced from far below room temperature (RT to above RT by inserting 1 nm thick Mg layer at IrMn/MgO interface. Furthermore, the exchange bias field (Heb was increased as well by the control of interfacial structures. The evidence for a significant fraction of Mn-O bonding at IrMn/MgO interface without Mg insertion layer was provided by X-ray photoelectron spectroscopy. The bonding between Mn and O can decrease the antiferromagnetism of IrMn film, leading to lower value of TB in Pt/NiFe/IrMn/MgO/Pt multilayers. Ultrathin Mg film inserted at IrMn/MgO interface acting as an oxygen sinking layer can suppress the oxidation reactions between Mn and O and reduce the formation of Mn-O bonding greatly. The oxidation suppression results in the recovery of the antiferromagnetism of IrMn film, which can enhance TB and Heb. Furthermore, the high resolution transmission electron microscopy demonstrates that the Mg insertion layer can efficiently promote a high-quality MgO (200 texture. This study will enhance the understanding of physics in antiferromagnet-based spintronic devices.

  2. Dielectric and magnetic characterizations of capacitor structures with an ionic liquid/MgO barrier and a ferromagnetic Pt electrode

    Directory of Open Access Journals (Sweden)

    D. Hayakawa

    2016-11-01

    Full Text Available The dielectric and magnetic properties of electric double layer (EDL capacitor structures with a perpendicularly magnetized Pt/Co/Pt electrode and an insulating cap layer (MgO are investigated. An electric field is applied through a mixed ionic liquid/MgO barrier to the surface of the top Pt layer, at which the magnetic moment is induced by the ferromagnetic proximity effect. The basic dielectric properties of the EDL capacitor are studied by varying the thickness of the MgO cap layer. The results indicate that the capacitance, i.e., the accumulated charge density at the Pt surface, is reduced with increasing the MgO thickness. From the MgO thickness dependence of the capacitance value, the effective dielectric constant of the ionic liquid is evaluated. Almost no electric field effect on the magnetic moment, the coercivity, or the Curie temperature is confirmed in the top Pt layer with the thickness of 1.3 nm, regardless of the presence or absence of the MgO cap layer, whereas the a clear change in the magnetic moment is observed when the top Pt layer is replaced by a Pd layer of 1.7 nm.

  3. Double-layered perpendicular magnetic recording media of granular-type FePt-MgO films

    International Nuclear Information System (INIS)

    Zhang Zhengang; Singh, Amarendra K.; Yin Jinhua; Perumal, A.; Suzuki, Takao

    2005-01-01

    The recording performance of double-layered granular-type FePt-MgO perpendicular magnetic recording media fabricated onto glass discs by sputtering is investigated. The (0 0 1)-textured FePt granular films are obtained by annealing FePt/MgO multilayers. Three different multilayer structures are compared in their magnetic properties and recording SNR performances. To evaluate thermal stability property of these granular-type FePt disks, the time-dependent magnetic force microscope (MFM) signal from the written bits on one of these disks is recorded in the temperature range 25-200 degree sign C. The signal decay at high observation temperature is interpreted based on the temperature dependence of magnetic anisotropy (K u )

  4. L1{sub 0} stacked binaries as candidates for hard-magnets. FePt, MnAl and MnGa

    Energy Technology Data Exchange (ETDEWEB)

    Matsushita, Yu-ichiro [Max-Planck Institut fuer Microstrukture Physics, Halle (Germany); Department of Applied Physics, The University of Tokyo (Japan); Madjarova, Galia [Max-Planck Institut fuer Microstrukture Physics, Halle (Germany); Department of Physical Chemistry, Faculty of Chemistry and Pharmacy, Sofia University (Bulgaria); Flores-Livas, Jose A. [Department of Physics, Universitaet Basel (Switzerland); Dewhurst, J.K.; Gross, E.K.U. [Max-Planck Institut fuer Microstrukture Physics, Halle (Germany); Felser, C. [Max Planck Institute for Chemical Physics of Solids, Dresden (Germany); Sharma, S. [Max-Planck Institut fuer Microstrukture Physics, Halle (Germany); Department of Physics, Indian Institute of Technology, Roorkee, Uttarkhand (India)

    2017-08-15

    We present a novel approach for designing new hard magnets by forming stacks of existing binary magnets to enhance the magneto crystalline anisotropy. This is followed by an attempt at reducing the amount of expensive metal in these stacks by replacing it with cheaper metal with similar ionic radius. This strategy is explored using examples of FePt, MnAl and MnGa. In this study a few promising materials are suggested as good candidates for hard magnets: stacked binary FePt{sub 2}MnGa{sub 2} in structure where each magnetic layer is separated by two non-magnetic layers, FePtMnGa and FePtMnAl in hexagonally distorted Heusler structures and FePt{sub 0.5}Ti{sub 0.5}MnAl. (copyright 2017 by WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  5. High Coke-Resistance Pt/Mg1-xNixO Catalyst for Dry Reforming of Methane.

    Directory of Open Access Journals (Sweden)

    Faris A J Al-Doghachi

    Full Text Available A highly active and stable nano structured Pt/Mg1-xNixO catalysts was developed by a simple co-precipitation method. The obtained Pt/Mg1-xNixO catalyst exhibited cubic structure nanocatalyst with a size of 50-80 nm and realized CH4 and CO2 conversions as high as 98% at 900°C with excellent stability in the dry reforming of methane. The characterization of catalyst was performed using various kinds of analytical techniques including XRD, BET, XRF, TPR-H2, TGA, TEM, FESEM, FT-IR, and XPS analyses. Characterization of spent catalyst further confirms that Pt/Mg1-xNixO catalyst has high coke-resistance for dry reforming. Thus, the catalyst demonstrated in this study, offers a promising catalyst for resolving the dilemma between dispersion and reducibility of supported metal, as well as activity and stability during high temperature reactions.

  6. Reforming of Ethanol to Produce Hydrogen over PtRuMg/ZrO2 Catalyst

    Directory of Open Access Journals (Sweden)

    Josh Y. Z. Chiou

    2012-01-01

    Full Text Available A modified PtRu/ZrO2 catalyst with Mg is evaluated for the oxidative steam reforming of ethanol (OSRE and the steam reforming of ethanol (SRE. In order to understand the variation in the reaction mechanism on OSRE and SRE, further analysis of both fresh and used catalyst is concentrated on for TEM, TG, Raman, and TPR characterization. The results show that the OSRE reaction requires a higher temperature (∼390°C to achieve 100% ethanol conversion than the SRE reaction (∼2500°C. The distribution of CO is minor for both reactions (< 5% for OSRE, < 1% for SRE. This demonstrates that the water gas shift (WGS reaction is an important side-reaction in the reforming of ethanol to produce H2 and CO2. A comparison of the temperature of WGS (WGS shows it is lower for the SRE reaction (WGS∼250°C for SRE, ~340°C for OSRE.

  7. Theoretical study of the elastic and thermodynamic properties of Pt_{3}Al with the L1_{2} structure under high pressure

    Directory of Open Access Journals (Sweden)

    N. Wei

    2015-12-01

    Full Text Available In this work, the elastic and thermodynamic properties of Pt_{3}Al under high pressure are investigated using density functional theory within the generalized gradient approximation. The results of bulk modulus and elastic constants at zero pressure are in good agreement with the available theoretical and experimental values. Under high pressure, all the elastic constants meet the corresponding mechanical stability criteria, meaning that Pt_{3}Al possesses mechanical stability. In addition, the elastic constants and elastic modulus increase linearly with the applied pressure. According to the Poisson's ratio ν and elastic modulus ratio (B/G, Pt_{3}Al alloy is found to be ductile, and higher pressure can significantly enhance the ductility. Those indicate that the elastic properties of Pt_{3}Al will be improved under high pressure. Through the quasi-harmonic Debye model, we first successfully report the variations of the Debye temperature Θ_{D}, specific heats C_{P}, thermal expansion coefficient α, and Grüneisen parameter γ under pressure range from 0 to 100 GPa and temperature range from 0 to 1000 K.

  8. Thermal dewetting with a chemically heterogeneous nano-template for self-assembled L1(0) FePt nanoparticle arrays.

    Science.gov (United States)

    Wang, Liang-Wei; Cheng, Chung-Fu; Liao, Jung-Wei; Wang, Chiu-Yen; Wang, Ding-Shuo; Huang, Kuo-Feng; Lin, Tzu-Ying; Ho, Rong-Ming; Chen, Lih-Juann; Lai, Chih-Huang

    2016-02-21

    A design for the fabrication of metallic nanoparticles is presented by thermal dewetting with a chemically heterogeneous nano-template. For the template, we fabricate a nanostructured polystyrene-b-polydimethylsiloxane (PS-b-PDMS) film on a Si|SiO2 substrate, followed by a thermal annealing and reactive ion etching (RIE) process. This gives a template composed of an ordered hexagonal array of SiOC hemispheres emerging in the polystyrene matrix. After the deposition of a FePt film on this template, we utilize the rapid thermal annealing (RTA) process, which provides in-plane stress, to achieve thermal dewetting and structural ordering of FePt simultaneously. Since the template is composed of different composition surfaces with periodically varied morphologies, it offers more tuning knobs to manipulate the nanostructures. We show that both the decrease in the area of the PS matrix and the increase in the strain energy relaxation transfer the dewetted pattern from the randomly distributed nanoparticles into a hexagonal periodic array of L10 FePt nanoparticles. Transmission electron microscopy with the in situ heating stage reveals the evolution of the dewetting process, and confirms that the positions of nanoparticles are aligned with those of the SiOC hemispheres. The nanoparticles formed by this template-dewetting show an average diameter and center-to-center distance of 19.30 ± 2.09 nm and 39.85 ± 4.80 nm, respectively. The hexagonal array of FePt nanoparticles reveals a large coercivity of 1.5 T, much larger than the nanoparticles fabricated by top-down approaches. This approach offers an efficient pathway toward self-assembled nanostructures in a wide range of material systems.

  9. Spin-orbit driven phenomena in the isoelectronic L1.sub.0./sub.-Fe(Pd,Pt) alloys from first principles

    Czech Academy of Sciences Publication Activity Database

    Kudrnovský, Josef; Drchal, Václav; Turek, Ilja

    2017-01-01

    Roč. 96, č. 21 (2017), s. 1-7, č. článku 214437. ISSN 2469-9950 R&D Projects: GA ČR GA15-13436S Institutional support: RVO:68378271 ; RVO:68081723 Keywords : anomalous Hall effect * Gilbert damping * partial order * first-principles * Fe(Pd,Pt) alloys Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 3.836, year: 2016

  10. Interplay of Rashba effect and spin Hall effect in perpendicular Pt/Co/MgO magnetic multilayers

    Institute of Scientific and Technical Information of China (English)

    赵云驰; 杨光; 董博闻; 王守国; 王超; 孙阳; 张静言; 于广华

    2016-01-01

    The interplay of the Rashba effect and the spin Hall effect originating from current induced spin–orbit coupling was investigated in the as-deposited and annealed Pt/Co/MgO stacks with perpendicular magnetic anisotropy. The above two effects were analyzed based on Hall measurements under external magnetic fields longitudinal and vertical to dc current, respectively. The coercive field as a function of dc current in vertical mode with only the Rashba effect involved decreases due to thermal annealing. Meanwhile, spin orbit torques calculated from Hall resistance with only the spin Hall effect involved in the longitudinal mode decrease in the annealed sample. The experimental results prove that the bottom Pt/Co interface rather than the Co/MgO top one plays a more critical role in both Rashba effect and spin Hall effect.

  11. Study on the effect of the metal–support (Fe-MgO and Pt-MgO) interaction in alcohol-CVD synthesis of carbon nanotubes

    International Nuclear Information System (INIS)

    Steplewska, Anna; Borowiak-Palen, Ewa

    2011-01-01

    This study presents the effect of the metal–support interaction in two systems: (1) iron particle, and (2) platinum particles, being supported on magnesium oxide (MgO) nanopowder in alcohol-CVD process for carbon nanotubes (CNTs) growth. The employment of the different metals but the same substrate (with equal molar ratio) resulted in the synthesis of single-walled CNTs (SWCNTs) or double-walled CNTs (DWCNTs), using iron and platinum, respectively. Furthermore, along with the prolongation of the process time, the decrease of the mean nanotubes diameter in case of iron-catalyzed materials was detected. Interestingly, the extention of the growth time in the synthesis using Pt/MgO resulted in the synthesis of the thicker mean nanotubes diameter. However, for both applied catalytic systems the reduction of the diameter distribution of the tubes and the increase of relative purity of the samples upon the growth time increase were detected.

  12. Study on the effect of the metal-support (Fe-MgO and Pt-MgO) interaction in alcohol-CVD synthesis of carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Steplewska, Anna, E-mail: asteplewska@zut.edu.pl; Borowiak-Palen, Ewa [West Pomeranian University of Technology, Centre of Knowledge Based Nanomaterials and Technologies, Institute of Chemical and Environment Engineering (Poland)

    2011-05-15

    This study presents the effect of the metal-support interaction in two systems: (1) iron particle, and (2) platinum particles, being supported on magnesium oxide (MgO) nanopowder in alcohol-CVD process for carbon nanotubes (CNTs) growth. The employment of the different metals but the same substrate (with equal molar ratio) resulted in the synthesis of single-walled CNTs (SWCNTs) or double-walled CNTs (DWCNTs), using iron and platinum, respectively. Furthermore, along with the prolongation of the process time, the decrease of the mean nanotubes diameter in case of iron-catalyzed materials was detected. Interestingly, the extention of the growth time in the synthesis using Pt/MgO resulted in the synthesis of the thicker mean nanotubes diameter. However, for both applied catalytic systems the reduction of the diameter distribution of the tubes and the increase of relative purity of the samples upon the growth time increase were detected.

  13. Preparation of c-axis perpendicularly oriented ultra-thin L10-FePt films on MgO and VN underlayers

    Science.gov (United States)

    Futamoto, Masaaki; Shimizu, Tomoki; Ohtake, Mitsuru

    2018-05-01

    Ultra-thin L10-FePt films of 2 nm average thickness are prepared on (001) oriented MgO and VN underlayers epitaxially grown on base substrate of SrTiO3(001) single crystal. Detailed cross-sectional structures are observed by high-resolution transmission electron microscopy. Continuous L10-FePt(001) thin films with very flat surface are prepared on VN(001) underlayer whereas the films prepared on MgO(001) underlayer consist of isolated L10-FePt(001) crystal islands. Presence of misfit dislocation and lattice bending in L10-FePt material is reducing the effective lattice mismatch with respect to the underlayer to be less than 0.5 %. Formation of very flat and continuous FePt layer on VN underlayer is due to the large surface energy of VN material where de-wetting of FePt material at high temperature annealing process is suppressed under a force balance between the surface and interface energies of FePt and VN materials. An employment of underlayer or substrate material with the lattice constant and the surface energy larger than those of L10-FePt is important for the preparation of very thin FePt epitaxial thin continuous film with the c-axis controlled to be perpendicular to the substrate surface.

  14. Surface structure of MgO underlayer with Ti diffusion for (002 oriented L10 FePt-based heat assisted magnetic recording media

    Directory of Open Access Journals (Sweden)

    Sintaro Hinata

    2018-05-01

    Full Text Available Surface morphology of the MgO layer and magnetic properties of FePt-C layer deposited on the MgO were investigated for the FePt-based heat assisted magnetic recording media. Stacking structure of the underlayer for the FePt-C layer was MgO (0-5 nm/Cr80Mn20 (0-30 nm/Cr50Ti50 (0-50 nm/glass sub.. Surface observation result for the MgO film by using an atomic force microscope revealed the existence of nodules with a height of about 2 nm and a network-like convex structure with a height difference of about sub nm (boundary wall, BW on the MgO crystal grain boundary. Density of the nodules largely depends on the surface roughness of the CrTi layer, RaCrTi and it is suppressed from 10 to 2/0.5 μm2 by reducing RaCrTi from 420 to 260 pm. Height of the BW depends on thickness of the MgO layer, tMgO and it can be suppressed by reducing tMgO to less than 4 nm. From the cross-sectional energy dispersive x-ray mapping, it is clarified that the BW is formed by atomic diffusion of Ti atoms from CrTi layer due to the substrate heating process, and a compound consists of Mg, Ti and O atoms. This BW can be used as a template to magnetically isolate the FePt column in the FePt-based granular film, such as FePt-SiO2, if the size of the BW is reduced to less than 10 nm. M-H loop of the FePt-C granular film deposited on the underlayer showed that the nodule and BW induce oxidation of the FePt grains, and reduction of intergranular exchange coupling.

  15. Surface structure of MgO underlayer with Ti diffusion for (002) oriented L10 FePt-based heat assisted magnetic recording media

    Science.gov (United States)

    Hinata, Sintaro; Jo, Shin; Saito, Shin

    2018-05-01

    Surface morphology of the MgO layer and magnetic properties of FePt-C layer deposited on the MgO were investigated for the FePt-based heat assisted magnetic recording media. Stacking structure of the underlayer for the FePt-C layer was MgO (0-5 nm)/Cr80Mn20 (0-30 nm)/Cr50Ti50 (0-50 nm)/glass sub.. Surface observation result for the MgO film by using an atomic force microscope revealed the existence of nodules with a height of about 2 nm and a network-like convex structure with a height difference of about sub nm (boundary wall, BW) on the MgO crystal grain boundary. Density of the nodules largely depends on the surface roughness of the CrTi layer, RaCrTi and it is suppressed from 10 to 2/0.5 μm2 by reducing RaCrTi from 420 to 260 pm. Height of the BW depends on thickness of the MgO layer, tMgO and it can be suppressed by reducing tMgO to less than 4 nm. From the cross-sectional energy dispersive x-ray mapping, it is clarified that the BW is formed by atomic diffusion of Ti atoms from CrTi layer due to the substrate heating process, and a compound consists of Mg, Ti and O atoms. This BW can be used as a template to magnetically isolate the FePt column in the FePt-based granular film, such as FePt-SiO2, if the size of the BW is reduced to less than 10 nm. M-H loop of the FePt-C granular film deposited on the underlayer showed that the nodule and BW induce oxidation of the FePt grains, and reduction of intergranular exchange coupling.

  16. Growth and microstructure of columnar Y-doped SrZrO{sub 3} films deposited on Pt-coated MgO by pulsed laser deposition

    Energy Technology Data Exchange (ETDEWEB)

    Luo, Sijun, E-mail: sluo1@tulane.edu; Riggs, Brian C.; Shipman, Joshua T.; Adireddy, Shiva; Sklare, Samuel C.; Chrisey, Douglas B., E-mail: dchrisey@tulane.edu [Department of Physics and Engineering Physics, Tulane University, New Orleans, Louisiana 70118 (United States); Zhang, Xiaodong; Koplitz, Brent [Department of Chemistry, Tulane University, New Orleans, Louisiana 70118 (United States)

    2015-07-21

    Direct integration of proton conductor films on Pt-coated substrates opens the way to film-based proton transport devices. Columnar SrZr{sub 0.95}Y{sub 0.05}O{sub 3−δ} (SZY) films with dense microstructure were deposited on Pt-coated MgO(100) substrates at 830 °C by pulsed laser deposition. The optimal window of ambient O{sub 2} pressure for good crystallinity of SZY films is from 400 to 600 mTorr. The ambient O{sub 2} compresses the plasma plume of SZY and increases the deposition rate. The 10 nm thick Ti adhesion layer on MgO(100) greatly affects the orientation of the sputtered Pt layers. Pt deposited directly on MgO shows a highly (111)-preferred orientation and leads to preferentially oriented SZY films while the addition of a Ti adhesion layer makes Pt show a less preferential orientation that leads to randomly oriented SZY films. The RMS surface roughness of preferentially oriented SZY films is larger than that of randomly oriented SZY films deposited under the same ambient O{sub 2} pressure. As the O{sub 2} pressure increased, the RMS surface roughness of preferentially oriented SZY films increased, reaching 45.7 nm (2.61% of film thickness) at 600 mTorr. This study revealed the ambient O{sub 2} pressure and orientation dependent surface roughness of SZY films grown on Pt-coated MgO substrates, which provides the potential to control the surface microstructure of SZY films for electrochemical applications in film-based hydrogen devices.

  17. Water-gas shift. An examination of Pt promoted MgO and tetragonal and monoclinic ZrO2 by in situ drifts

    International Nuclear Information System (INIS)

    Chenu, Emilie; Jacobs, Gary; Crawford, Adam C.; Keogh, Robert A.; Patterson, Patricia M.; Sparks, Dennis E.; Davis, Burtron H.

    2005-01-01

    In situ DRIFTS measurements on unpromoted and Pt promoted MgO and ZrO 2 (both tetragonal and monoclinic) indicate that at high H 2 O/CO ratios, where the reaction rate has been reported to be zero order in H 2 O and first order in CO, the mechanism involved in the catalysis of water-gas shift is likely a surface formate mechanism, in agreement with Shido and Iwasawa. Pt was found to catalyze the removal of surface carbonates and to facilitate the generation of active OH groups relative to the unpromoted catalyst. Comparison with Pt/ceria revealed that the OH groups involved in the catalysis of magnesia and zirconia may be those of the bridging variety which occur at defect sites. That is, water dissociated over vacancies to produce bridging OH groups, as observed by infrared spectroscopy. The existence of such an adsorbed species is implied in the zero reaction order for water, where kinetics suggests that the surface should be saturated by an adsorbed water species. The lower extent of vacancy formation for magnesia and zirconia-based materials in comparison with ceria could explain a lower surface population of active bridging OH groups. CO was used as a probe molecule of the reduced centers, as it reacts with bridging OH groups to generate surface formates, a proposed WGS intermediate, and the decomposition of which is proposed to be the rate-limiting step. The trends in formate intensity by CO adsorption and CO conversion in WGS catalytic testing both followed the order: Pt/ceria>Pt/m-zirconia>Pt/t-zirconia>Pt/magnesia. In all cases, a normal kinetic isotope effect was observed in switching from H 2 O to D 2 O, consistent with a link between the rate-limiting step and the decomposition of surface formates, as noted previously by Shido and Iwasawa for Rh/ceria, MgO, and ZnO

  18. Study of interlayer coupling between FePt and FeCoB thin films through MgO spacer layer

    Science.gov (United States)

    Singh, Sadhana; Kumar, Dileep; Gupta, Mukul; Reddy, V. Raghvendra

    2017-05-01

    Interlayer exchange coupling between hard-FePt and soft-FeCoB magnetic layers has been studied with increasing thickness of insulator MgO spacer layer in FePt/MgO/FeCoB sandwiched structure. A series of the samples were prepared in identical condition using ion beam sputtering method and characterized for their magnetic and structural properties using magneto-optical Kerr effect (MOKE) and X-ray reflectivity measurements. The nature of coupling between FePt and FeCoB was found to be ferromagnetic which decreases exponentially with increasing thickness of MgO layer. At very low thickness of MgO layer, both layers were found strongly coupled thus exhibiting coherent magnetization reversal. At higher thickness, both layers were found decoupled and magnetization reversal occurred at different switching fields. Strong coupling at very low thickness is attributed to pin holes in MgO layer which lead to direct coupling whereas on increasing thickness, coupling may arise due to magneto-static interactions.

  19. Technology in L1

    DEFF Research Database (Denmark)

    Elf, Nikolaj Frydensbjerg; Hanghøj, Thorkild; Skaar, Håvard

    2015-01-01

    In recent decades, several Scandinavian research projects have had an explicit focus on how technology intervenes in L1 (or so-called Mother Tongue Education) practices in Swedish, Norwegian and Danish educational contexts, and how this may impact on understanding of the subject. There is currently......-of-school literacy practices. A final finding is the emphasis on teacher uncertainty regarding how and why to integrate technology within existing paradigms of the subject. This calls for further research on how technology may be justified in L1 practice, including various forms of teacher education....... no systematic overview of the documented possibilities and challenges related to the use of technology in L1. At the same time, there is terminological confusion in use of ‘technology’ and related concepts in L1. Finally, there is a general lack of critical reflection on the relation between technological...

  20. ATG16L1

    DEFF Research Database (Denmark)

    Salem, Mohammad; Ammitzboell, Mette; Nys, Kris

    2015-01-01

    Genetic variations in the autophagic pathway influence genetic predispositions to Crohn disease. Autophagy, the major lysosomal pathway for degrading and recycling cytoplasmic material, constitutes an important homeostatic cellular process. Of interest, single-nucleotide polymorphisms in ATG16L1...... (autophagy-related 16-like 1 [S. cerevisiae]), a key component in the autophagic response to invading pathogens, have been associated with an increased risk of developing Crohn disease. The most common and well-studied genetic variant of ATG16L1 (rs2241880; leading to a T300A conversion) exhibits a strong...... association with risk for developing Crohn disease. The rs2241880 variant plays a crucial role in pathogen clearance, resulting in imbalanced cytokine production, and is linked to other biological processes, such as the endoplasmic reticulum stress/unfolded protein response. In this review, we focus...

  1. Integral data test of HENDL1.0/MG and visualBUS with neutronics shielding experiments. Pt.1

    International Nuclear Information System (INIS)

    Gao Chunjing; Deng Tieru; Xu Dezheng; Li Jingjing; Wu Yican

    2004-01-01

    HENDL1.0/MG, a multi-group working library of the Hybrid Evaluated Nuclear Data Library, was home-developed by the FDS Team of ASIPP (Institute of Plasma Physics, Chinese Academy of Sciences) on the basis of several national data libraries. To validate and qualify the process of producing HENDL1.0/MG, simulating calculations of a series of existent spherical shell benchmark experiments (Al, Mo, Co, Ti, Mn, W, Be and V) have been performed with HENDL1.0/MG and the multifunctional neutronics code system named VisualBUS home-developed also by FDS Team. (authors)

  2. The anisotropy field of FePt L10 nanoparticles controlled by very thin Pt layer

    International Nuclear Information System (INIS)

    Okamoto, Satoshi; Kitakami, Osamu; Kikuchi, Nobuaki; Miyazaki, Takamichi; Shimada, Yutaka; Chiang, Te-Hsuan

    2004-01-01

    We have prepared epitaxial FePt L1 0 (001) nanoparticles covered with Pt [d Pt nm]/Ag[(4-d Pt ) nm] overlayers. The particles are oblate spheroids approximately 10 nm in diameter and 2 nm in height. The anisotropy field H k at 0 K, which is evaluated from the temperature dependences of coercivity H c , decreases from 90 to 60 kOe on increasing the Pt thickness from d Pt 0 to 1.5 nm, while the energy barrier at zero field remains unchanged. The significant reduction of H k due to the presence of the adjacent Pt layer can be attributed to an enhanced magnetic moment caused by the ferromagnetic polarization of Pt atoms at the interface. This finding suggests an effective method of controlling the switching field of FePt L1 0 nanoparticles

  3. Dependency of tunneling magnetoresistance ratio on Pt seed-layer thickness for double MgO perpendicular magnetic tunneling junction spin-valves with a top Co2Fe6B2 free layer ex-situ annealed at 400 °C.

    Science.gov (United States)

    Takemura, Yasutaka; Lee, Du-Yeong; Lee, Seung-Eun; Park, Jea-Gun

    2016-12-02

    For the double MgO based perpendicular magnetic tunneling junction (p-MTJ) spin-valves with a top Co 2 Fe 6 B 2 free layer ex situ annealed at 400 °C, the tunneling-magnetoresistance ratio (TMR) strongly depended on the platinum (Pt) seed layer thickness (t Pt ): it peaked (∼134%) at a specific t Pt (3.3 nm). The TMR ratio was initially and slightly increased from 113%-134% by the enhancement of the magnetic moment of the Co 2 Fe 6 B 2 pinned layer when t Pt increased from 2.0-3.3 nm, and then rapidly decreased from 134%-38.6% by the degrading face-centered-cubic crystallinity of the MgO tunneling barrier when t Pt increased from 3.3-14.3 nm.

  4. Effects of deposition temperature and in-situ annealing time on structure and magnetic properties of (001) orientation FePt films

    International Nuclear Information System (INIS)

    Yu, Yongsheng; George, T.A.; Li, Haibo; Sun, Daqian; Ren, Zhenan; Sellmyer, D.J.

    2013-01-01

    FePt films were prepared on (100) oriented single crystal MgO substrates at high temperature ranging from 620 until 800 °C and in-situ annealed for different times ranging from 0 to 60 min to obtain ordered FePt films. The structural analysis indicates that FePt films grow epitaxially on MgO (100) substrates. Both increasing deposition temperature and in-situ annealing time enhance the (001) texture and ordering of FePt films. The magnetic analysis shows that these L1 0 FePt films have perpendicular anisotropy and the easy magnetization c-axis is perpendicular to the film plane. Magnetization reversal is controlled by a rotational mechanism. The hard magnetic properties of the films are improved with increasing deposition temperature or in-situ annealing time. - Highlights: ► The paper reports the texture and magnetic evolution of FePt films deposited on MgO substrates. ► Increasing deposition temperature or annealing time enhanced the texture and ordering. ► The magnetic analysis shows L1 0 FePt films have perpendicular anisotropy.

  5. Extrap L-1 experimental stability

    International Nuclear Information System (INIS)

    Brunsell, P.; Hellblom, G.; Karlsson, P.; Mazur, S.; Nordlund, P.; Scheffel, J.

    1990-01-01

    In the Extrap scheme a Z-pinch is stabilized by imposing a strongly inhomogeneous octupole magnetic field. This field is generated by four conductor rods, each carrying equal currents I v antiparallel to the plasma current I p itself. Theoretically, interchange stability is improved by the magnetic field, as well as long-wavelength kinks due to induced currents in the plasma and in the rods. Short wavelength kinks are, as in the 1-D pinch, stabilized by FLR and viscous-resistive effects. We have performed a set of experiments in the linear Extrap L-1 device (length 40 cm, plasma radius a 2 cm, rod distance 3 cm) in order to determine optimal performance in terms of confined current (5-20 kA) and stability during the discharge length (80 μs; of the order 100 Alfven times). In this paper we summarize our results from two types of experiments; with and without external axial magnetic field. The results are compared with theory in the final paragraph. (author) 5 figs

  6. Effects of Cr underlayer and Pt buffer layer on the interfacial structure and magnetic characteristics of sputtered FePt films

    International Nuclear Information System (INIS)

    Sun, A.-C.; Hsu, J.-H.; Huang, H.L.; Kuo, P.C.

    2006-01-01

    This work develops a new method for growing L1 0 FePt(0 0 1) thin film on a Pt/Cr bilayer using an amorphous glass substrate. Semi-coherent epitaxial growth was initiated from the Cr(0 0 2) underlayer, continued through the Pt(0 0 1) buffer layer, and extended into the L1 0 FePt(0 0 1) magnetic layer. The squareness of the L1 0 FePt film in the presence of both a Cr underlayer and a Pt buffer layer was close to unity as the magnetic field was applied perpendicular to the film plane. The single L1 0 FePt(1 1 1) orientation was observed in the absence of a Cr underlayer. When a Cr underlayer is inserted, the preferred orientation switched from L1 0 FePt(1 1 1) to L1 0 FePt(0 0 1) and the magnetic film exhibited perpendicular magnetic anisotropy. However, in the absence of an Pt intermediate layer, the Cr atoms diffused directly into the FePt magnetic layer and prevented the formation of the L1 0 FePt(0 0 1) preferred orientation. When a Pt buffer layer was introduced between the FePt and Cr underlayer, the L1 0 FePt(0 0 1) peak appeared. The thickness of the Pt buffer layer also substantially affected the magnetic properties and atomic arrangement at the FePt/Pt and Pt/Cr interfaces

  7. PD-L1-specific T cells

    DEFF Research Database (Denmark)

    Ahmad, Shamaila Munir; Borch, Troels Holz; Hansen, Morten

    2016-01-01

    -specific T cells that recognize both PD-L1-expressing immune cells and malignant cells. Thus, PD-L1-specific T cells have the ability to modulate adaptive immune reactions by reacting to regulatory cells. Thus, utilization of PD-L1-derived T cell epitopes may represent an attractive vaccination strategy...... for targeting the tumor microenvironment and for boosting the clinical effects of additional anticancer immunotherapy. This review summarizes present information about PD-L1 as a T cell antigen, depicts the initial findings about the function of PD-L1-specific T cells in the adjustment of immune responses...

  8. Magnetic anisotropy and chemical long-range order in epitaxial ferrimagnetic CrPt sub 3 films

    CERN Document Server

    Maret, M; Köhler, J; Poinsot, R; Ulhaq-Bouillet, C; Tonnerre, J M; Berar, J F; Bucher, E

    2000-01-01

    Thin films of CrPt sub 3 were prepared by molecular beam epitaxy on both Al sub 2 O sub 3 (0 0 0 1) and MgO(0 0 1) substrates, either directly by co-deposition of Cr and Pt at high temperatures or after in situ annealing of superlattices [Cr(2 A)/Pt(7 A)]. In situ RHEED observations and X-ray diffraction measurements have allowed us to check the single-crystal quality of CrPt sub 3 films and to determine the degree of L1 sub 2 -type long-range order (LRO). In films co-deposited between 850 deg. C and 950 deg. C a nearly perfect LRO has been observed. As in bulk alloys, such ordering yields a ferrimagnetic order, while the disordered films are non-magnetic. In contrast with the ferromagnetic L1 sub 2 -type ordered CoPt sub 3 (1 1 1) films, the ferrimagnetic CrPt sub 3 (1 1 1) films exhibit perpendicular magnetic anisotropy with quality factors, K sub u /K sub d , as large as 5 and large coercivities around 450 kA/m. Such anisotropy could be related to the arrangement of Cr atoms, which owing to their large mag...

  9. Monoclonal Antibody L1Mab-13 Detected Human PD-L1 in Lung Cancers.

    Science.gov (United States)

    Yamada, Shinji; Itai, Shunsuke; Nakamura, Takuro; Yanaka, Miyuki; Chang, Yao-Wen; Suzuki, Hiroyoshi; Kaneko, Mika K; Kato, Yukinari

    2018-04-01

    Programmed cell death ligand-1 (PD-L1) is a type I transmembrane glycoprotein expressed on antigen-presenting cells. It is also expressed in several tumor cells such as melanoma and lung cancer cells. A strong correlation has been reported between human PD-L1 (hPD-L1) expression in tumor cells and negative prognosis in cancer patients. Here, a novel anti-hPD-L1 monoclonal antibody (mAb) L 1 Mab-13 (IgG 1 , kappa) was produced using a cell-based immunization and screening (CBIS) method. We investigated hPD-L1 expression in lung cancer using flow cytometry, Western blot, and immunohistochemical analyses. L 1 Mab-13 specifically reacted hPD-L1 of hPD-L1-overexpressed Chinese hamster ovary (CHO)-K1 cells and endogenous hPD-L1 of KMST-6 (human fibroblast) in flow cytometry and Western blot. Furthermore, L 1 Mab-13 reacted with lung cancer cell lines (EBC-1, Lu65, and Lu99) in flow cytometry and stained lung cancer tissues in a membrane-staining pattern in immunohistochemical analysis. These results indicate that a novel anti-hPD-L1 mAb, L 1 Mab-13, is very useful for detecting hPD-L1 of lung cancers in flow cytometry, Western blot, and immunohistochemical analyses.

  10. Ferromagnetic alloy material CoFeC with high thermal tolerance in MgO/CoFeC/Pt structure and comparable intrinsic damping factor with CoFeB

    Science.gov (United States)

    Chen, Shaohai; Zhou, Jing; Lin, Weinan; Yu, Jihang; Guo, Rui; Poh, Francis; Shum, Danny; Chen, Jingsheng

    2018-02-01

    The thermal tolerance and perpendicular magnetic anisotropy (PMA) of ferromagnetic alloy Co40Fe40C20 in the structure MgO/CoFeC/Pt (or Ta) were investigated and compared with the commonly used CoFeB alloy. It is found that the PMA of CoFeC with {{K}i,CoFeC}=2.21 erg c{{m}-2} , which is 59% higher than that of CoFeB, can be obtained after proper post-annealing treatment. Furthermore, CoFeC alloy provides better thermal tolerance to temperature of 400 °C than CoFeB. The studies on ferromagnetic resonance show that the intrinsic damping constant α in of Co40Fe40C20 alloy is 0.0047, which is similar to the reported value of 0.004 for Co40Fe40B20 alloy. The comprehensive comparisons indicate that CoFeC alloy is a promising candidate for the application of the integration of spin torque transfer magnetic random access memory with complementary metal-oxide semiconductor processes.

  11. PODAAC-CYGNS-L1X20

    Data.gov (United States)

    National Aeronautics and Space Administration — This Level 1 (L1) dataset contains the Version 2.0 geo-located Delay Doppler Maps (DDMs) calibrated into Power Received (Watts) and Bistatic Radar Cross Section...

  12. Phobos L1 Operational Tether Experiment (PHLOTE)

    Data.gov (United States)

    National Aeronautics and Space Administration — A sensor package that “floats” just above the surface of Phobos, suspended by a tether from a small spacecraft operating at the Mars/Phobos Lagrange 1 (L1) Point...

  13. Voice and Narrative in L1 Writing

    DEFF Research Database (Denmark)

    Krogh, Ellen; Piekut, Anke

    2015-01-01

    This paper investigates issues of voice and narrative in L1 writing. Three branches of research are initial-ly discussed: research on narratives as resources for identity work, research on writer identity and voice as an essential aspect of identity, and research on Bildung in L1 writing. Subsequ...... training of voice and narratives as a resource for academic writing, and that the Bildung potential of L1 writing may be tied to this issue.......This paper investigates issues of voice and narrative in L1 writing. Three branches of research are initial-ly discussed: research on narratives as resources for identity work, research on writer identity and voice as an essential aspect of identity, and research on Bildung in L1 writing...... in lower secondary L1, she found that her previous writing strategies were not rewarded in upper secondary school. In the second empiri-cal study, two upper-secondary exam papers are investigated, with a focus on their approaches to exam genres and their use of narrative resources to address issues...

  14. Validation of ATLAS L1 Topological Triggers

    CERN Document Server

    Praderio, Marco

    2017-01-01

    The Topological trigger (L1Topo) is a new component of the ATLAS L1 (Level-1) trigger. Its purpose is that of reducing the otherwise too high rate of data collection from the LHC by rejecting those events considered “uninteresting” (meaning that they have already been studied). This event rate reduction is achieved by applying topological requirements to the physical objects present in each event. It is very important to make sure that this trigger does not reject any “interesting” event. Therefore we need to verify its correct functioning. The goal of this summer student project is to study the response of two L1Topo algorithms (concerning ∆R and invariant mass). To do so I will compare the trigger decisions produced by the L1Topo hardware with the ones produced by the “official” L1Topo simulation. This way I will be able to identify events that could be incorrectly rejected. Simultaneously I will produce an emulation of these triggers that will help me understand the cause of disagreements bet...

  15. Quantitative transmission electron microscopy analysis of multi-variant grains in present L10-FePt based heat assisted magnetic recording media

    International Nuclear Information System (INIS)

    Ho, Hoan; Zhu, Jingxi; Kulovits, Andreas; Laughlin, David E.; Zhu, Jian-Gang

    2014-01-01

    We present a study on atomic ordering within individual grains in granular L1 0 -FePt thin films using transmission electron microscopy techniques. The film, used as a medium for heat assisted magnetic recording, consists of a single layer of FePt grains separated by non-magnetic grain boundaries and is grown on an MgO underlayer. Using convergent-beam techniques, diffraction patterns of individual grains are obtained for a large number of crystallites. The study found that although the majority of grains are ordered in the perpendicular direction, more than 15% of them are multi-variant, or of in-plane c-axis orientation, or disordered fcc. It was also found that these multi-variant and in-plane grains have always grown across MgO grain boundaries separating two or more MgO grains of the underlayer. The in-plane ordered portion within a multi-variant L1 0 -FePt grain always lacks atomic coherence with the MgO directly underneath it, whereas, the perpendicularly ordered portion is always coherent with the underlying MgO grain. Since the existence of multi-variant and in-plane ordered grains are severely detrimental to high density data storage capability, the understanding of their formation mechanism obtained here should make a significant impact on the future development of hard disk drive technology

  16. Generalized L1 penalized matrix factorization

    DEFF Research Database (Denmark)

    Rasmussen, Morten Arendt

    2017-01-01

    Traditionally, chemometric models consists of parameters found by solving a least squares criterion. However, these models can suffer from overfitting, as well as being hard to interpret because of the large number of active parameters. This work proposes the use of a generalized L1 norm penalty ...

  17. Dirichlet expression for L(1, χ )

    Indian Academy of Sciences (India)

    We show that this expression with obvious modification is valid for the general primitive Dirichlet character χ. Keywords. Hurwitz zeta function; Dirichlet character; Dirichlet L-series; primitive character. 1. Introduction. In Dirichlet's famous work dealing with class number formula, the value of L(1,χ) is expressed in terms of finite ...

  18. Small Molecule Agonists of Cell Adhesion Molecule L1 Mimic L1 Functions In Vivo.

    Science.gov (United States)

    Kataria, Hardeep; Lutz, David; Chaudhary, Harshita; Schachner, Melitta; Loers, Gabriele

    2016-09-01

    Lack of permissive mechanisms and abundance of inhibitory molecules in the lesioned central nervous system of adult mammals contribute to the failure of functional recovery after injury, leading to severe disabilities in motor functions and pain. Peripheral nerve injury impairs motor, sensory, and autonomic functions, particularly in cases where nerve gaps are large and chronic nerve injury ensues. Previous studies have indicated that the neural cell adhesion molecule L1 constitutes a viable target to promote regeneration after acute injury. We screened libraries of known drugs for small molecule agonists of L1 and evaluated the effect of hit compounds in cell-based assays in vitro and in mice after femoral nerve and spinal cord injuries in vivo. We identified eight small molecule L1 agonists and showed in cell-based assays that they stimulate neuronal survival, neuronal migration, and neurite outgrowth and enhance Schwann cell proliferation and migration and myelination of neurons in an L1-dependent manner. In a femoral nerve injury mouse model, enhanced functional regeneration and remyelination after application of the L1 agonists were observed. In a spinal cord injury mouse model, L1 agonists improved recovery of motor functions, being paralleled by enhanced remyelination, neuronal survival, and monoaminergic innervation, reduced astrogliosis, and activation of microglia. Together, these findings suggest that application of small organic compounds that bind to L1 and stimulate the beneficial homophilic L1 functions may prove to be a valuable addition to treatments of nervous system injuries.

  19. High Pt utilization PEMFC electrode obtained by alternative ion-exchange/electrodeposition.

    Science.gov (United States)

    Chen, Siguo; Wei, Zidong; Li, Hua; Li, Li

    2010-12-14

    High Pt utilization PEMFC electrodes were prepared by an alternative ion-exchange/electrodeposition (AIEE) technique. The results demonstrated that the MEA employing an AIEE electrode with a Pt loading of 0.014 mg Pt cm(-2) exhibits performance approximately 2.2 times larger than that employing a conventional Nafion-bonded Pt/C electrode with a same Pt loading.

  20. L-1 constraint in Liouville gravity

    International Nuclear Information System (INIS)

    Kitazawa, Y.

    1992-01-01

    In this paper, the authors study recursion relations among the amplitudes which involve discrete states in c = 1 Liouville gravity on the sphere. The authors find that the spin J = 1/2 discrete state gives rise to the L -1 type recursion relation. Multiple point correlation functions are determined recursively from fewer point functions by this recursion relation. The authors further point out that the analogs of J = 1/2 state exist in c -1 type recursion relation

  1. Effect of substitutional defects on Kambersky damping in L1{sub 0} magnetic materials

    Energy Technology Data Exchange (ETDEWEB)

    Qu, T. [School of Physics and Astronomy, University of Minnesota, Minneapolis, Minnesota 55455 (United States); Victora, R. H., E-mail: victora@umn.edu [School of Physics and Astronomy, University of Minnesota, Minneapolis, Minnesota 55455 (United States); Department of Electrical and Computer Engineering, University of Minnesota, Minneapolis, Minnesota 55455 (United States)

    2015-02-16

    Kambersky damping, representing the loss of magnetic energy from the electrons to the lattice through the spin orbit interaction, is calculated for L1{sub 0} FePt, FePd, CoPt, and CoPd alloys versus chemical degree of order. When more substitutional defects exist in the alloys, damping is predicted to increase due to the increase of the spin-flip channels allowed by the broken symmetry. It is demonstrated that this corresponds to an enhanced density of states (DOS) at the Fermi level, owing to the rounding of the DOS with loss of long-range order. Both the damping and the DOS of the Co-based alloy are found to be less affected by the disorder. Pd-based alloys are predicted to have lower damping than Pt-based alloys, making them more suitable for high density spintronic applications.

  2. Helical magnetic axis configuration combined with l = 1 and weak l = -1 torsatron fields

    International Nuclear Information System (INIS)

    Kikuchi, Hitoshi; Saito, Katsunori; Gesso, Hirokazu; Shiina, Shoichi

    1989-01-01

    The superposition of a relatively weak l = -1 torsatron field on a main l = 1 torsatron field leads to the improvement of the confinement properties due to the formation of a local magnetic well, which results from the local curvature of the helical magnetic axis with a larger excursion in the major radius direction. This l±1 helical magnetic axis system has a comparatively simple, compact coil structure. Here the vacuum configuration properties of l = ±1 system are described. (author)

  3. Three cases with L1 syndrome and two novel mutations in the L1CAM gene.

    Science.gov (United States)

    Marín, Rosario; Ley-Martos, Miriam; Gutiérrez, Gema; Rodríguez-Sánchez, Felicidad; Arroyo, Diego; Mora-López, Francisco

    2015-11-01

    Mutations in the L1CAM gene have been identified in the following various X-linked neurological disorders: congenital hydrocephalus; mental retardation, aphasia, shuffling gait, and adducted thumbs (MASA) syndrome; spastic paraplegia; and agenesis of the corpus callosum. These conditions are currently considered different phenotypes of a single entity known as L1 syndrome. We present three families with L1 syndrome. Sequencing of the L1CAM gene allowed the identification of the following mutations involved: a known splicing mutation (c.3531-12G>A) and two novel ones: a missense mutation (c.1754A>C; p.Asp585Ala) and a nonsense mutation (c.3478C>T; p.Gln1160Stop). The number of affected males and carrier females identified in a relatively small population suggests that L1 syndrome may be under-diagnosed. L1 syndrome should be considered in the differential diagnosis of intellectual disability or mental retardation in children, especially when other signs such as hydrocephalus or adducted thumbs are present.

  4. Pt skin coated hollow Ag-Pt bimetallic nanoparticles with high catalytic activity for oxygen reduction reaction

    Science.gov (United States)

    Fu, Tao; Huang, Jianxing; Lai, Shaobo; Zhang, Size; Fang, Jun; Zhao, Jinbao

    2017-10-01

    The catalytic activity and stability of electrocatalyst is critical for the commercialization of fuel cells, and recent reports reveal the great potential of the hollow structures with Pt skin coat for developing high-powered electrocatalysts due to their highly efficient utilization of the Pt atoms. Here, we provide a novel strategy to prepare the Pt skin coated hollow Ag-Pt structure (Ag-Pt@Pt) of ∼8 nm size at room temperature. As loaded on the graphene, the Ag-Pt@Pt exhibits a remarkable mass activity of 0.864 A/mgPt (at 0.9 V, vs. reversible hydrogen electrode (RHE)) towards oxygen reduction reaction (ORR), which is 5.30 times of the commercial Pt/C catalyst, and the Ag-Pt@Pt also shows a better stability during the ORR catalytic process. The mechanism of this significant enhancement can be attributed to the higher Pt utilization and the unique Pt on Ag-Pt surface structure, which is confirmed by the density functional theory (DFT) calculations and other characterization methods. In conclusion, this original work offers a low-cost and environment-friendly method to prepare a high active electrocatalyst with cheaper price, and this work also discloses the correlation between surface structures and ORR catalytic activity for the hollow structures with Pt skin coat, which can be instructive for designing novel advanced electrocatalysts for fuel cells.

  5. Contribution of L1 in EFL Teaching

    Directory of Open Access Journals (Sweden)

    Wahjuningsih Usadiati

    2009-01-01

    Full Text Available This study is conducted in a classroom action research to improve the students’ achievement in writing English sentences in Present Perfect Tense in Structure 1 lessons. The subject consisted of 20 Semester II students who took Structure I lessons in English Education Department of Palangka Raya University, Central Kalimantan, Indonesia. The data were taken from the results of pre test and post test after the action was done. The results show that in cycle 1, in which the explanations were fully in English, only 40% of the students got a good achievement; 5-7 out of 20 test items were correct. After cycle 2 was done using L1 interchangeably with English in the explanations, the students’ achievement of writing English sentences in Present Perfect Tense increased to 75%, in which 15-18 out 20 test items were correct.

  6. Iron-platinum multilayer thin film reactions to form L1(0) iron-platinum and exchange spring magnets

    Science.gov (United States)

    Yao, Bo

    (substrate temperature, periodicity) have a strong influence on the structure (effective interdiffusivity, L1 0 phase volume fraction, grain size, and density) and magnetic properties. The correlation of these parameters suggests that the annealed [Fe/Pt]n multilayer films have limited nuclei, and the subsequent growth of L10 phase is very important to the extent of ordered phase formed. A correlation between the grain size of fcc FePt phase, grain size of the L10 FePt phase, the L10 FePt phase fraction, and magnetic properties strongly suggests that the phase transformation of fcc →L10 is highly dependent on the grain size of the parent fcc FePt phase. A selective phase growth model is proposed to explain the phenomena observed. An investigation of the influence of total film thickness on the phase formation of the L10 FePt phase in [Fe/Pt] n multilayer films and a comparison of this to that of FePt co-deposited alloy films is also conducted. A general trend of greater L1 0 phase formation in thicker films was observed in both types of films. It was further found that the thickness dependence of the structure and of the magnetic properties in [Fe/Pt]n multilayer films is much stronger than that in FePt alloy films. This is related to the greater chemical energy contained in [Fe/Pt]n films than FePt alloy films, which is helpful for the L10 FePt phase growth. However, the initial nucleation temperature of [Fe/Pt]n multilayers and co-deposited alloy films was found to be similar. An investigation of L10 FePt-based exchange spring magnets is presented based on our understanding of the L10 formation in [Fe/Pt] n multilayer films. It is known that exchange coupling is an interfacial magnetic interaction and it was experimentally shown that this interaction is limited to within several nanometers of the interface. A higher degree of order of the hard phase is shown to increase the length scale slightly. Two approaches can be used to construct the magnets. For samples with

  7. Rendezvous missions with minimoons from L1

    Science.gov (United States)

    Chyba, M.; Haberkorn, T.; Patterson, G.

    2014-07-01

    We propose to present asteroid capture missions with the so-called minimoons. Minimoons are small asteroids that are temporarily captured objects on orbits in the Earth-Moon system. It has been suggested that, despite their small capture probability, at any time there are one or two meter diameter minimoons, and progressively greater numbers at smaller diameters. The minimoons orbits differ significantly from elliptical orbits which renders a rendezvous mission more challenging, however they offer many advantages for such missions that overcome this fact. First, they are already on geocentric orbits which results in short duration missions with low Delta-v, this translates in cost efficiency and low-risk targets. Second, beside their close proximity to Earth, an advantage is their small size since it provides us with the luxury to retrieve the entire asteroid and not only a sample of material. Accessing the interior structure of a near-Earth satellite in its morphological context is crucial to an in-depth analysis of the structure of the asteroid. Historically, 2006 RH120 is the only minimoon that has been detected but work is ongoing to determine which modifications to current observation facilities is necessary to provide detection algorithm capabilities. In the event that detection is successful, an efficient algorithm to produce a space mission to rendezvous with the detected minimoon is highly desirable to take advantage of this opportunity. This is the main focus of our work. For the design of the mission we propose the following. The spacecraft is first placed in hibernation on a Lissajoux orbit around the liberation point L1 of the Earth-Moon system. We focus on eight-shaped Lissajoux orbits to take advantage of the stability properties of their invariant manifolds for our transfers since the cost to minimize is the spacecraft fuel consumption. Once a minimoon has been detected we must choose a point on its orbit to rendezvous (in position and velocities

  8. Mechanism of coercivity enhancement by Ag addition in FePt-C granular films for heat assisted magnetic recording media

    Energy Technology Data Exchange (ETDEWEB)

    Varaprasad, B. S. D. Ch. S.; Takahashi, Y. K., E-mail: takahashi.yukiko@nims.go.jp; Wang, J.; Hono, K. [National Institute for Materials Science (NIMS), 1-2-1 Sengen, Tsukuba 305-0047 (Japan); Ina, T.; Nakamura, T.; Ueno, W.; Nitta, K.; Uruga, T. [Japan Synchrotron Radiation Research Institute (JASRI/SPring-8), 1-1-1 Kouto, Sayo, Hyogo 679-5198 (Japan)

    2014-06-02

    We investigated the Ag distribution in a FePtAg-C granular film that is under consideration for a heat assisted magnetic recording medium by aberration-corrected scanning transmission electron microscope-energy dispersive X-ray spectroscopy and X-ray absorption fine structure. Ag is rejected from the core of FePt grains during the deposition, forming Ag-enriched shell surrounding L1{sub 0}-ordered FePt grains. Since Ag has no solubility in both Fe and Pt, the rejection of Ag induces atomic diffusions thereby enhancing the kinetics of the L1{sub 0}-order in the FePt grains.

  9. Molecular mechanism of PD-1/PD-L1 blockade via anti-PD-L1 antibodies atezolizumab and durvalumab.

    Science.gov (United States)

    Lee, Hyun Tae; Lee, Ju Yeon; Lim, Heejin; Lee, Sang Hyung; Moon, Yu Jeong; Pyo, Hyo Jeong; Ryu, Seong Eon; Shin, Woori; Heo, Yong-Seok

    2017-07-17

    In 2016 and 2017, monoclonal antibodies targeting PD-L1, including atezolizumab, durvalumab, and avelumab, were approved by the FDA for the treatment of multiple advanced cancers. And many other anti-PD-L1 antibodies are under clinical trials. Recently, the crystal structures of PD-L1 in complex with BMS-936559 and avelumab have been determined, revealing details of the antigen-antibody interactions. However, it is still unknown how atezolizumab and durvalumab specifically recognize PD-L1, although this is important for investigating novel binding sites on PD-L1 targeted by other therapeutic antibodies for the design and improvement of anti-PD-L1 agents. Here, we report the crystal structures of PD-L1 in complex with atezolizumab and durvalumab to elucidate the precise epitopes involved and the structural basis for PD-1/PD-L1 blockade by these antibodies. A comprehensive comparison of PD-L1 interactions with anti-PD-L1 antibodies provides a better understanding of the mechanism of PD-L1 blockade as well as new insights into the rational design of improved anti-PD-L1 therapeutics.

  10. Ordering process of sputtered FePt films

    International Nuclear Information System (INIS)

    Takahashi, Y.K.; Ohnuma, M.; Hono, K.

    2003-01-01

    We have investigated the in situ ordering process of sputtered FePt thin films deposited on heated substrates at 300 deg. C with different thicknesses. The films thinner than 50 nm were composed of nanograins (∼5 nm) of disordered FePt phase. Recrystallization occurred when films were grown thicker than 100 nm, and transformation twins were observed in recrystallized grains, in which ordering to the L1 0 structure was confirmed

  11. Prothrombin time (PT)

    Science.gov (United States)

    PT; Pro-time; Anticoagulant-prothrombin time; Clotting time: protime; INR; International normalized ratio ... PT is measured in seconds. Most of the time, results are given as what is called INR ( ...

  12. Detection of high PD-L1 expression in oral cancers by a novel monoclonal antibody L1Mab-4.

    Science.gov (United States)

    Yamada, Shinji; Itai, Shunsuke; Kaneko, Mika K; Kato, Yukinari

    2018-03-01

    Programmed cell death-ligand 1 (PD-L1), which is a ligand of programmed cell death-1 (PD-1), is a type I transmembrane glycoprotein that is expressed on antigen-presenting cells and several tumor cells, including melanoma and lung cancer cells. There is a strong correlation between human PD-L1 (hPD-L1) expression on tumor cells and negative prognosis in cancer patients. In this study, we produced a novel anti-hPD-L1 monoclonal antibody (mAb), L 1 Mab-4 (IgG 2b , kappa), using cell-based immunization and screening (CBIS) method and investigated hPD-L1 expression in oral cancers. L 1 Mab-4 reacted with oral cancer cell lines (Ca9-22, HO-1-u-1, SAS, HSC-2, HSC-3, and HSC-4) in flow cytometry and stained oral cancers in a membrane-staining pattern. L 1 Mab-4 stained 106/150 (70.7%) of oral squamous cell carcinomas, indicating the very high sensitivity of L 1 Mab-4. These results indicate that L 1 Mab-4 could be useful for investigating the function of hPD-L1 in oral cancers.

  13. Detection of high PD-L1 expression in oral cancers by a novel monoclonal antibody L1Mab-4

    Directory of Open Access Journals (Sweden)

    Shinji Yamada

    2018-03-01

    Full Text Available Programmed cell death-ligand 1 (PD-L1, which is a ligand of programmed cell death-1 (PD-1, is a type I transmembrane glycoprotein that is expressed on antigen-presenting cells and several tumor cells, including melanoma and lung cancer cells. There is a strong correlation between human PD-L1 (hPD-L1 expression on tumor cells and negative prognosis in cancer patients. In this study, we produced a novel anti-hPD-L1 monoclonal antibody (mAb, L1Mab-4 (IgG2b, kappa, using cell-based immunization and screening (CBIS method and investigated hPD-L1 expression in oral cancers. L1Mab-4 reacted with oral cancer cell lines (Ca9-22, HO-1-u-1, SAS, HSC-2, HSC-3, and HSC-4 in flow cytometry and stained oral cancers in a membrane-staining pattern. L1Mab-4 stained 106/150 (70.7% of oral squamous cell carcinomas, indicating the very high sensitivity of L1Mab-4. These results indicate that L1Mab-4 could be useful for investigating the function of hPD-L1 in oral cancers. Keywords: Programmed cell death-ligand 1, Monoclonal antibody, Oral cancer

  14. Ubiquitin C-Terminal Hydrolase L1 in Tumorigenesis

    Directory of Open Access Journals (Sweden)

    Jennifer Hurst-Kennedy

    2012-01-01

    Full Text Available Ubiquitin carboxyl-terminal hydrolase L1 (UCH-L1, aka PGP9.5 is an abundant, neuronal deubiquitinating enzyme that has also been suggested to possess E3 ubiquitin-protein ligase activity and/or stabilize ubiquitin monomers in vivo. Recent evidence implicates dysregulation of UCH-L1 in the pathogenesis and progression of human cancers. Although typically only expressed in neurons, high levels of UCH-L1 have been found in many nonneuronal tumors, including breast, colorectal, and pancreatic carcinomas. UCH-L1 has also been implicated in the regulation of metastasis and cell growth during the progression of nonsmall cell lung carcinoma, colorectal cancer, and lymphoma. Together these studies suggest UCH-L1 has a potent oncogenic role and drives tumor development. Conversely, others have observed promoter methylation-mediated silencing of UCH-L1 in certain tumor subtypes, suggesting a potential tumor suppressor role for UCH-L1. In this paper, we provide an overview of the evidence supporting the involvement of UCH-L1 in tumor development and discuss the potential mechanisms of action of UCH-L1 in oncogenesis.

  15. Intrinsic Properties of Fe-Substituted L1(0) Magnets

    Energy Technology Data Exchange (ETDEWEB)

    Manchanda, P; Kumar, P; Kashyap, A; Lucis, MJ; Shield, JE; Mubarok, A; Goldstein, JI; Constantinides, S; Barmak, K; Lewis, LH; Sellmyer, DJ; Skomski, R

    2013-10-01

    First-principle supercell calculations are used to determine how 3d elemental additions, especially Fe additions, modify the magnetization, exchange and anisotropy of L1(0)-ordered ferromagnets. Calculations are performed using the VASP code and partially involve configurational averaging over site disorder. Three isostructural systems are investigated: Fe-Co-Pt, Mn-Al-Fe, and transition metal-doped Fe-Ni. In all three systems the iron strongly influences the magnetic properties of these compounds, but the specific effect depends on the host. In CoPt(Fe) iron enhances the magnetization, with subtle changes in the magnetic moments that depend on the distribution of the Fe and Co atoms. The addition of Fe to MnAl is detrimental to the magnetization, because it creates antiferromagnetic exchange interactions, but it enhances the magnetic anisotropy. The replacement of 50% of Mn by Fe in MnFeAl2 enhances the anisotropy from 1.77 to 2.5 MJ/m(3). Further, the substitution of light 3d elements such as Ti, V, Cr into L1(0)-ordered FeNi is shown to substantially reduce the magnetization.

  16. Learners’ L1 Use in a Task-based Classroom

    DEFF Research Database (Denmark)

    Bao, Rui; Du, Xiangyun

    2015-01-01

    , but with only a very small amount oc- curring for off-task talk across tasks. L1 use mainly occurred in learners’ efforts to mediate completion of the tasks. The findings highlight the role of L1 in foreign language learning and suggest that L1 use is associated with a number of factors, such as task types......’ extensive L1 use and off-task talk. Informed by sociocultural theory, this study explored the extent to which L1s and their func- tions were used when performing tasks. The subjects were beginner-level lower-secondary school learners of Chinese. The data shows that learners have a high amount of L1 use...

  17. Interface-engineered spin-dependent transport in perpendicular Co/Pt multilayers

    Energy Technology Data Exchange (ETDEWEB)

    Jiang, Shao-Long; Yang, Guang; Teng, Jiao, E-mail: tengjiao@mater.ustb.edu.cn; Guo, Qi-Xun; Li, Lei-Lei; Yu, Guang-Hua, E-mail: ghyu@mater.ustb.edu.cn

    2016-11-30

    Highlights: • The anomalous Hall effect in Co/Pt multilayers is studied. • Thermally stable AHE feature is obtained in [Pt/Co]{sub 3}/Ta/MgO multilayers. • Good thermal stability is due to enhanced side-jump and intrinsic contributions. - Abstract: The improvement of anomalous Hall effect (AHE) has been obtained through the introduction of a Ta metallic layer at the Co/MgO interface in perpendicular [Pt/Co]{sub 3}/MgO multilayers. It is exhibited that the saturation anomalous Hall resistivity is 42% larger than that in Co/Pt multilayers without Ta insertion. More meaningfully, thermally stable AHE feature is gained in perpendicular [Pt/Co]{sub 3}/Ta/MgO multilayers despite Co-Pt interdiffusion. The AHE is enhanced for sample [Pt/Co]{sub 3}/Ta/MgO after annealing, mainly due to the enhancement of the side-jump and intrinsic contributions.

  18. L10 phase transition in FePt thin films via direct interface reaction

    International Nuclear Information System (INIS)

    Li Xiaohong; Sun Hongyu; Wang Fengqing; Li Wei; Zhang Xiangyi; Liu Baoting; Guo Jianxin

    2008-01-01

    Lowering the L1 0 ordering temperature of FePt films is of great significance for their application as an ultrahigh density magnetic recording medium. In this study, the L1 0 ordering process of FePt thin films deposited directly on Si substrates has been significantly accelerated by the interface reaction between the thin film and the Si substrate, and thus the thin films show a low L1 0 ordering temperature of T = 310 deg. C as compared with those deposited on Si/SiO 2 substrates. The accelerated L1 0 ordering transition is predominantly dependent on the rapid growth of the ordered domains during the interface reaction. The film thickness has an important effect on the interface reaction and thus can be used to tune the L1 0 ordering process of the FePt films.

  19. Rapid thermal annealing of FePt and FePt/Cu thin films

    Energy Technology Data Exchange (ETDEWEB)

    Brombacher, Christoph

    2011-01-10

    Chemically ordered FePt is one of the most promising materials to reach the ultimate limitations in storage density of future magnetic recording devices due to its high uniaxial magnetocrystalline anisotropy and a corrosion resistance superior to rare-earth based magnets. In this study, FePt and FePt/Cu bilayers have been sputter deposited at room temperature onto thermally oxidized silicon wafers, glass substrates and self-assembled arrays of spherical SiO{sub 2} particles with diameters down to 10 nm. Millisecond flash lamp annealing, as well as conventional rapid thermal annealing was employed to induce the phase transformation from the chemically disordered A1 phase into the chemically ordered L1{sub 0} phase. The influence of the annealing temperature, annealing time and the film thickness on the ordering transformation and (001) texture evolution of FePt films with near equiatomic composition was studied. Whereas flash lamp annealed FePt films exhibit a polycrystalline morphology with high chemical L1{sub 0} order, rapid thermal annealing can lead to the formation of chemically ordered FePt films with (001) texture on amorphous SiO{sub 2}/Si substrates. The resultant high perpendicular magnetic anisotropy and large coercivities up to 40 kOe are demonstrated. Simultaneously to the ordering transformation, rapid thermal annealing to temperatures exceeding 600 C leads to a break up of the continuous FePt film into separated islands. This dewetting behavior was utilized to create regular arrays of FePt nanostructures on SiO{sub 2} particle templates with periods down to 50 nm. The addition of Cu improves the (001) texture formation and chemical ordering for annealing temperatures T{sub a} {<=}600 C. In addition, the magnetic anisotropy and the coercivity of the ternary FePtCu alloy can be effectively tailored by adjusting the Cu content. The prospects of FePtCu based exchange spring media, as well as the magnetic properties of FePtCu nanostructures fabricated

  20. SiO2-supported Pt particles studied by electron microscopy

    International Nuclear Information System (INIS)

    Wang, D.; Penner, S.; Su, D.S.; Rupprechter, G.; Hayek, K.; Schloegl, R.

    2003-01-01

    Regularly grown Pt particles supported by amorphous SiO 2 were heated in hydrogen at 873 K after an oxidising treatment. The morphological and structural changes were studied by electron microscopy. Platinum silicides Pt 3 Si with L1 2 (Cu 3 Au) structure, monoclinic Pt 3 Si and tetragonal Pt 12 Si 5 were identified after the treatment. The mechanisms of coalescence of the particles and the formation of irregular large particles are suggested. A topotactic structural transformation accompanied with the migration of Si from the substrate to the particles are suggested to take place during Pt 3 Si formation

  1. Microstructural and magnetic properties of L10 FePt-C (0 0 1) textured nanocomposite films grown on different intermediate layers

    International Nuclear Information System (INIS)

    Chen, J S; Chow, G M; Lim, B C; Hu, J F; Ding, Y F; Ju, G

    2008-01-01

    The FePt : C films with different volume fractions of carbon and different thicknesses were epitaxially grown on a CrRu(2 0 0) underlayer with Pt and MgO intermediate layers. The magnetic properties and microstructure of these FePt : C films were investigated. The FePt : C films grown on the Pt intermediate layer consisted of a continuous layer of FePt, with overlying granular FePt grains, while the FePt : C films grown on the MgO intermediate layer consisted of granular FePt : C layers with overlying granular grains. The formation of the overlying granular FePt grains was attributed to carbon diffusion to the surface which resulted in the second nucleation of FePt. The different interface energies and surface energies of FePt on Pt and MgO intermediate layers caused the formation of an initial continuous FePt layer on the Pt intermediate layer and initial granular FePt layers on the MgO intermediate layer. The coupling between the continuous FePt layer or the granular FePt layer and the overlying granular FePt grains resulted in simultaneous magnetization reversal and thus strong exchange coupling in FePt : C films.

  2. Magnetic properties of nanocrystallized Fe-Pt-B melt-spun ribbons

    International Nuclear Information System (INIS)

    Yamamoto, Tokujiro; Omori, Akihiro; Kimura, Hisamichi; Inoue, Akihisa

    2007-01-01

    L1 0 FePt nanoparticles have been prepared by etching grain boundaries of heat-treated melt-spun Fe-19Pt-25B (at.%) alloy ribbons. It is revealed that an L1 0 FePt nanocrystalline phase is directly formed from the Fe-Pt-B amorphous ribbons by long-time heat treatment at low temperatures in the vicinity of 723 K. With increasing heat treatment time, dimensions of the nanocrystallized FePt grains increase, accompanied by a change from soft ferromagnetic to hard ferromagnetic. The ribbon crystallized at 723 K for 1.8 ks consists of only an FePt L1 0 phase and its coercivity is as low as 0.381 kA/m. However, it increases to 372 kA/m with increasing grain size of precipitated L1 0 phase to about 30 nm by heat treatment for 86.4 ks, while the saturation magnetic flux density remains constant at about 0.4 T. Etching boundaries in heat-treated ribbons has been performed to obtain ferromagnetic L1 0 FePt nanoparticles and several particles were observed by means of transmission electron microscopy

  3. Antisite-defect-induced surface segregation in ordered NiPt alloy

    DEFF Research Database (Denmark)

    Pourovskii, L.V.; Ruban, Andrei; Abrikosov, I.A.

    2003-01-01

    alloys corresponds to the (111) truncation of the bulk L1(0) ordered structure. However, the (111) surface of the nickel deficient Ni49Pt51 alloy is strongly enriched by Pt and should exhibit the pattern of the 2x2 structure. Such a drastic change in the segregation behavior is due to the presence...

  4. Attitudes held by Setswana L1-speaking university students toward ...

    African Journals Online (AJOL)

    Respondents believed that their L1 had limitations in wider society; and that it had prestige, albeit a covert one. Generally, they held favourable attitudes toward their L1. Further comprehensive research needs to be done to explore these new variables, as well as to explore their statistical significance in language attitude ...

  5. On the Link Between L1-PCA and ICA.

    Science.gov (United States)

    Martin-Clemente, Ruben; Zarzoso, Vicente

    2017-03-01

    Principal component analysis (PCA) based on L1-norm maximization is an emerging technique that has drawn growing interest in the signal processing and machine learning research communities, especially due to its robustness to outliers. The present work proves that L1-norm PCA can perform independent component analysis (ICA) under the whitening assumption. However, when the source probability distributions fulfil certain conditions, the L1-norm criterion needs to be minimized rather than maximized, which can be accomplished by simple modifications on existing optimal algorithms for L1-PCA. If the sources have symmetric distributions, we show in addition that L1-PCA is linked to kurtosis optimization. A number of numerical experiments illustrate the theoretical results and analyze the comparative performance of different algorithms for ICA via L1-PCA. Although our analysis is asymptotic in the sample size, this equivalence opens interesting new perspectives for performing ICA using optimal algorithms for L1-PCA with guaranteed global convergence while inheriting the increased robustness to outliers of the L1-norm criterion.

  6. Metabolic rate regulates L1 longevity in C. elegans.

    Directory of Open Access Journals (Sweden)

    Inhwan Lee

    Full Text Available Animals have to cope with starvation. The molecular mechanisms by which animals survive long-term starvation, however, are not clearly understood. When they hatch without food, C. elegans arrests development at the first larval stage (L1 and survives more than two weeks. Here we show that the survival span of arrested L1s, which we call L1 longevity, is a starvation response regulated by metabolic rate during starvation. A high rate of metabolism shortens the L1 survival span, whereas a low rate of metabolism lengthens it. The longer worms are starved, the slower they grow once they are fed, suggesting that L1 arrest has metabolic costs. Furthermore, mutants of genes that regulate metabolism show altered L1 longevity. Among them, we found that AMP-dependent protein kinase (AMPK, as a key energy sensor, regulates L1 longevity by regulating this metabolic arrest. Our results suggest that L1 longevity is determined by metabolic rate and that AMPK as a master regulator of metabolism controls this arrest so that the animals survive long-term starvation.

  7. Multivalent human papillomavirus l1 DNA vaccination utilizing electroporation.

    Directory of Open Access Journals (Sweden)

    Kihyuck Kwak

    Full Text Available Naked DNA vaccines can be manufactured simply and are stable at ambient temperature, but require improved delivery technologies to boost immunogenicity. Here we explore in vivo electroporation for multivalent codon-optimized human papillomavirus (HPV L1 and L2 DNA vaccination.Balb/c mice were vaccinated three times at two week intervals with a fusion protein comprising L2 residues ∼11-88 of 8 different HPV types (11-88×8 or its DNA expression vector, DNA constructs expressing L1 only or L1+L2 of a single HPV type, or as a mixture of several high-risk HPV types and administered utilizing electroporation, i.m. injection or gene gun. Serum was collected two weeks and 3 months after the last vaccination. Sera from immunized mice were tested for in-vitro neutralization titer, and protective efficacy upon passive transfer to naive mice and vaginal HPV challenge. Heterotypic interactions between L1 proteins of HPV6, HPV16 and HPV18 in 293TT cells were tested by co-precipitation using type-specific monoclonal antibodies.Electroporation with L2 multimer DNA did not elicit detectable antibody titer, whereas DNA expressing L1 or L1+L2 induced L1-specific, type-restricted neutralizing antibodies, with titers approaching those induced by Gardasil. Co-expression of L2 neither augmented L1-specific responses nor induced L2-specific antibodies. Delivery of HPV L1 DNA via in vivo electroporation produces a stronger antibody response compared to i.m. injection or i.d. ballistic delivery via gene gun. Reduced neutralizing antibody titers were observed for certain types when vaccinating with a mixture of L1 (or L1+L2 vectors of multiple HPV types, likely resulting from heterotypic L1 interactions observed in co-immunoprecipitation studies. High titers were restored by vaccinating with individual constructs at different sites, or partially recovered by co-expression of L2, such that durable protective antibody titers were achieved for each type

  8. Do L1 Reading Achievement and L1 Print Exposure Contribute to the Prediction of L2 Proficiency?

    Science.gov (United States)

    Sparks, Richard L.; Patton, Jon; Ganschow, Leonore; Humbach, Nancy

    2012-01-01

    The study examined whether individual differences in high school first language (L1) reading achievement and print exposure would account for unique variance in second language (L2) written (word decoding, spelling, writing, reading comprehension) and oral (listening/speaking) proficiency after adjusting for the effects of early L1 literacy and…

  9. TV-L1 optical flow for vector valued images

    DEFF Research Database (Denmark)

    Rakêt, Lars Lau; Roholm, Lars; Nielsen, Mads

    2011-01-01

    The variational TV-L1 framework has become one of the most popular and successful approaches for calculating optical flow. One reason for the popularity is the very appealing properties of the two terms in the energy formulation of the problem, the robust L1-norm of the data fidelity term combined...... with the total variation (TV) regular- ization that smoothes the flow, but preserve strong discontinuities such as edges. Specifically the approach of Zach et al. [1] has provided a very clean and efficient algorithm for calculating TV-L1 optical flows between grayscale images. In this paper we propose...

  10. Robotic synthesis of L-[1-11C]tyrosine

    International Nuclear Information System (INIS)

    Luurtsema, Gert; Medema, Jitze; Elsinga, P.H.; Visser, G.M.; Vaalburg, Willem

    1994-01-01

    L-[1- 11 C]tyrosine promises to become an important tracer for determination of the protein synthesis rate (PSR) in tumor tissue and brain. The commercially available Anatech RB-86 robotic system is utilized for the automation of the L-[1- 11 C]tyrosine production via the isocyanide method as reported by Bolster et al. (Eur. J. Nucl. Med. 12, 321-324, 1986). The total synthesis time, including HPLC-purification and enantiomeric separation is 60 min. With a practical yield of 20 mCi L-[1- 11 C]tyrosine at a specific activity > 1000 Ci/mmol. (author)

  11. Simultaneous removal of carbon and nitrogen by mycelial pellets of a heterotrophic nitrifying fungus-Penicillium sp. L1.

    Science.gov (United States)

    Liu, Yuxiang; Hu, Tingting; Zhao, Jing; Lv, Yongkang; Ren, Ruipeng

    2017-02-01

    A novel heterotrophic nitrifying fungus, defined as Penicillium sp. L1, can form mycelial pellets in liquid medium in this study. The effects of inoculation method, C/N ratio, initial pH, and temperature were gradually evaluated to improve the simultaneous removal of total nitrogen (TN) and chemical oxygen demand (COD) in wastewater by Penicillium sp. L1. Results showed that compared with spore inoculation, 48 h pellet inoculum could significantly increase the pellet size (from about 1.5 mm to 3.2 mm) and improve the removal capability, particularly for COD removal (from less than 50-86.20%). The removal efficiencies of TN and COD reached 98.38% (from 136.01 mg/L to 2.20 mg/L) and 92.40% (from 10,720 mg/L to 815 mg/L) under the following conditions: C/N 36, pH 3, 30°C, and inoculation with 48 h pellets. The pellet diameter reached 4.8 mm after 4-day cultivation. In this case, Penicillium sp. L1 removed TN from 415.93 mg/L to 43.39 mg/L, as well as COD from 29,533 mg/L to 8850 mg/L. Overall, the results indicated that the pellet size was closely related to the pollutant-removal ability of Penicillium sp. L1. Furthermore, mycelial pellets (4.8 mm, dead) only adsorbed 38.08% TN (from 125.45 mg/L to 77.78 mg/L), which indicated that adsorption did not play a major role in the nitrogen-removal process. Copyright © 2016 The Society for Biotechnology, Japan. Published by Elsevier B.V. All rights reserved.

  12. Phosphatidylcholine induces apoptosis of 3T3-L1 adipocytes

    Directory of Open Access Journals (Sweden)

    Li Hailan

    2011-12-01

    Full Text Available Abstract Background Phosphatidylcholine (PPC formulation is used for lipolytic injection, even though its mechanism of action is not well understood. Methods The viability of 3T3-L1 pre-adipocytes and differentiated 3T3-L1 cells was measured after treatment of PPC alone, its vehicle sodium deoxycholate (SD, and a PPC formulation. Western blot analysis was performed to examine PPC-induced signaling pathways. Results PPC, SD, and PPC formulation significantly decreased 3T3-L1 cell viability in a concentration-dependent manner. PPC alone was not cytotoxic to CCD-25Sk human fibroblasts at concentrations Conclusions PPC results in apoptosis of 3T3-L1 cells.

  13. 26 CFR 1.7701(l)-1 - Conduit financing arrangements.

    Science.gov (United States)

    2010-04-01

    ... determines that such recharacterization is appropriate to prevent avoidance of any tax imposed by title 26 of...) INCOME TAX (CONTINUED) INCOME TAXES General Actuarial Valuations § 1.7701(l)-1 Conduit financing...

  14. IceBridge Atmospheric Chemistry L1B Data

    Data.gov (United States)

    National Aeronautics and Space Administration — The IceBridge Atmospheric Chemistry L1B Data set (ICHEM1B) contains measurements acquired over Antarctica using the AVOCET differential Non-Dispersive Infrared...

  15. Toward the direct deposition of L10 FePt nanoparticles

    International Nuclear Information System (INIS)

    Qiu Jiaoming; Judy, Jack H.; Weller, Dieter; Wang Jianping

    2005-01-01

    In this paper we report a technique that can directly fabricate L1 0 phase FePt nanoparticles. FePt nanoparticles were generated through gas-phase aggregation using a magnetron-sputtering-based nanocluster source. Following the source chamber, an online halogen-lamp heater was used for the L1 0 phase formation during the particles' flight in vacuum. Transmission electron microscopy and vibrating-sample magnetometer data verified the successful fabrication of the L1 0 phase FePt nanoparticles. The coercivity value at 300 K is 1100 Oe for the nanoparticles with online heating. Neon carrier gas was applied to manipulate FePt nanoparticle size and to enhance particle size uniformity. The size dependence of nanoparticle ordering was investigated

  16. Gold nanoparticles functionalized with a fragment of the neural cell adhesion molecule L1 stimulate L1-mediated functions

    Science.gov (United States)

    Schulz, Florian; Lutz, David; Rusche, Norman; Bastús, Neus G.; Stieben, Martin; Höltig, Michael; Grüner, Florian; Weller, Horst; Schachner, Melitta; Vossmeyer, Tobias; Loers, Gabriele

    2013-10-01

    The neural cell adhesion molecule L1 is involved in nervous system development and promotes regeneration in animal models of acute and chronic injury of the adult nervous system. To translate these conducive functions into therapeutic approaches, a 22-mer peptide that encompasses a minimal and functional L1 sequence of the third fibronectin type III domain of murine L1 was identified and conjugated to gold nanoparticles (AuNPs) to obtain constructs that interact homophilically with the extracellular domain of L1 and trigger the cognate beneficial L1-mediated functions. Covalent conjugation was achieved by reacting mixtures of two cysteine-terminated forms of this L1 peptide and thiolated poly(ethylene) glycol (PEG) ligands (~2.1 kDa) with citrate stabilized AuNPs of two different sizes (~14 and 40 nm in diameter). By varying the ratio of the L1 peptide-PEG mixtures, an optimized layer composition was achieved that resulted in the expected homophilic interaction of the AuNPs. These AuNPs were stable as tested over a time period of 30 days in artificial cerebrospinal fluid and interacted with the extracellular domain of L1 on neurons and Schwann cells, as could be shown by using cells from wild-type and L1-deficient mice. In vitro, the L1-derivatized particles promoted neurite outgrowth and survival of neurons from the central and peripheral nervous system and stimulated Schwann cell process formation and proliferation. These observations raise the hope that, in combination with other therapeutic approaches, L1 peptide-functionalized AuNPs may become a useful tool to ameliorate the deficits resulting from acute and chronic injuries of the mammalian nervous system.The neural cell adhesion molecule L1 is involved in nervous system development and promotes regeneration in animal models of acute and chronic injury of the adult nervous system. To translate these conducive functions into therapeutic approaches, a 22-mer peptide that encompasses a minimal and functional L1

  17. The Pleiotropic Role of L1CAM in Tumor Vasculature

    Directory of Open Access Journals (Sweden)

    Francesca Angiolini

    2017-01-01

    Full Text Available Angiogenesis, the formation of new vessels, is a key step in the development, invasion, and dissemination of solid tumors and, therefore, represents a viable target in the context of antitumor therapy. Indeed, antiangiogenic approaches have given promising results in preclinical models and entered the clinical practice. However, in patients, the results obtained so far with antiangiogenic drugs have not completely fulfilled expectations, especially because their effect has been transient with tumors developing resistance and evasion mechanisms. A better understanding of the mechanisms that underlie tumor vascularization and the functional regulation of cancer vessels is a prerequisite for the development of novel and alternative antiangiogenic treatments. The L1 cell adhesion molecule (L1CAM, a cell surface glycoprotein previously implicated in the development and plasticity of the nervous system, is aberrantly expressed in the vasculature of various cancer types. L1CAM plays multiple pro-angiogenic roles in the endothelial cells of tumor-associated vessels, thus emerging as a potential therapeutic target. In addition, L1CAM prevents the maturation of cancer vasculature and its inhibition promotes vessel normalization, a process that is thought to improve the therapeutic response of tumors to cytotoxic drugs. We here provide an overview on tumor angiogenesis and antiangiogenic therapies and summarize the current knowledge on the biological role of L1CAM in cancer vasculature. Finally, we highlight the clinical implications of targeting L1CAM as a novel antiangiogenic and vessel-normalizing approach.

  18. α-NiPt(Al) and phase equilibria in the Ni-Al-Pt system at 1150 deg C

    International Nuclear Information System (INIS)

    Hayashi, S.; Ford, S.I.; Young, D.J.; Sordelet, D.J.; Besser, M.F.; Gleeson, B.

    2005-01-01

    The α-NiPt(Al) phase and its associated equilibria in the Ni-Al-Pt system at 1150 deg C were investigated by analyzing equilibrated bulk alloys and the interdiffusion zones of diffusion couples. Phase constitutions, tie-lines and microstructures were determined using a combination of techniques, including high-energy synchrotron X-ray diffraction, scanning electron microscopy and electron probe microanalysis. A large Pt solubility limit was found to exist in the β-NiAl, ∼42 at.%, and in γ'-Ni 3 Al, ∼32 at.%. The α-NiPt(Al) phase was found to have wide Pt solubility range of about 33-60 at.% and to skew along an almost constant Pt/Al ratio of 1.5. The α-NiPt(Al) has an ordered face-centered tetragonal L1 0 crystal structure, with the Al and Pt atoms found to be preferentially located in the corners and prismatic faces, respectively. The temperature dependence of the lattice parameters and unit cell volume of the α phase were also determined

  19. CoPt nanoparticles by chemical reduction

    International Nuclear Information System (INIS)

    Wang, H.L.; Zhang, Y.; Huang, Y.; Zeng, Q.; Hadjipanayis, G.C.

    2004-01-01

    CoPt nanoparticles with a size of 1-2 nm were synthesized by chemical reduction using the solvents of water and alcohol. A phase transformation from the originally disordered face centered cubic (FCC) structure to an ordered face centered tetragonal L1 0 structure occurred after annealing, which results in the coercivity up to 9 kOe because of the high anisotropy of the tetragonal phase (K∼2-4x10 7 erg/cm 3 ) (Philos. Mag. 13 (1966) 567; IEEE Trans. Magn. 20 (1984) 1625). HREM images of as-grow Co 48 Pt 52 shows the single-crystalline FCC structure with the shape of columnar and spherical

  20. PtRu nanoparticles dispersed on nitrogen-doped carbon nanohorns as an efficient electrocatalyst for methanol oxidation reaction

    International Nuclear Information System (INIS)

    Zhang, Linwei; Gao, Ang; Liu, Yan; Wang, Yuan; Ma, Jiantai

    2014-01-01

    Highlights: • A novel anode catalyst is synthesized using N-doped carbon nanohorns as support. • PtRu/NCNHs exhibits an excellent activity for MOR relative to PtRu/C catalysts. • The enhancement is due to the electronic interaction between NCNHs and PtRu NPs. - Abstract: A novel anode catalyst (PtRu/NCNHs) assembled with nitrogen-doped carbon nanohorns (NCNHs) and PtRu nanoparticles (1.9 nm) exhibits an obvious enhancement in the tolerance to carbonaceous intermediates and the electocatalytic activity for methanol oxidation reaction (MOR) in comparison to a commercial PtRu/C-JM catalyst and a home-made PtRu/Vulcan catalyst. The MOR mass activity of PtRu/NCNHs (850 mA mg −1 PtRu ) is 2.5 times as high as that of PtRu/C-JM (341 mA mg −1 PtRu ). The MOR specific activity of PtRu/NCNHs is 1.8 times as high as that of PtRu/Vulcan having similar Pt/Ru atomic ratios, specific electrochemical surface areas and particle sizes of PtRu NPs. The electronic interaction between PtRu NPs and NCNHs is responsible for the enhancement in the MOR activity of PtRu/NCNHs

  1. Epitaxial growth of zigzag PtAu alloy surface on Au nano-pentagrams with enhanced Pt utilization and electrocatalytic performance toward ethanol oxidation reaction

    International Nuclear Information System (INIS)

    Du, Cheng; Gao, Xiaohui; Zhuang, Zhihua; Cheng, Chunfeng; Zheng, Fuqin; Li, Xiaokun; Chen, Wei

    2017-01-01

    Highlights: • PtAu nanoalloy surface is heteroepitaxially grown on the pre-synthesized Au nano-pentagrams. • The PtAu/Au nano-pentagrams exhibit excellent electrocatalytic activity for ethanol oxidation. • The charge transfer resistance of PtAu/Au is lower than that of commercial Pt/C. • The durability and anti-poisoning ability of PtAu/Au is much better than those of commercial Pt/C - Abstract: Improving Pt utilization is of fundamental importance for many significant processes in energy conversion, which is strongly dependent on the surface structure of used catalysts. Based on the traditional Pt-on-Au system which has been proved to be an ideal nanostructure for improving the catalytic activity and stability of Pt, and the recent follow-up studies on this system, we introduce here a new strategy for fabricating Pt surface with high-index facets over the Pt-on-Au system. To achieve this goal, we elaborately designed and fabricated a unique zigzag PtAu alloy nanosurface on Au nano-pentagrams (PtAu/Au NPs) through epitaxial growth of Pt along the high-index facets on the pre-synthesized Au nano-pentagrams. Owing to the surface electronic interaction between Au and Pt and the exposed high-index facets from the unique morphology of zigzag PtAu alloy nanosurface, the as-prepared PtAu/Au NPs exhibited excellent electrocatalytic performance toward ethanol oxidation reaction (EOR) in alkaline condition. The specific activity (8.3 mA cm"−"2) and mass activity (4.4 A mg"−"1) obtained from PtAu/Au NPs are about 5.2 and 5.5 times, respectively, higher than those from commercial Pt/C for EOR.

  2. CO tolerance of PdPt/C and PdPtRu/C anodes for PEMFC

    International Nuclear Information System (INIS)

    Garcia, Amanda C.; Paganin, Valdecir A.; Ticianelli, Edson A.

    2008-01-01

    The performance of H 2 /O 2 proton exchange membrane fuel cells (PEMFCs) fed with CO-contaminated hydrogen was investigated for anodes with PdPt/C and PdPtRu/C electrocatalysts. The physicochemical properties of the catalysts were characterized by energy dispersive X-ray (EDX) analyses, X-ray diffraction (XRD) and 'in situ' X-ray absorption near edge structure (XANES). Experiments were conducted in electrochemical half and single cells by cyclic voltammetry (CV) and I-V polarization measurements, while DEMS was employed to verify the formation of CO 2 at the PEMFC anode outlet. A quite high performance was achieved for the PEMFC fed with H 2 + 100 ppm CO with the PdPt/C and PdPtRu/C anodes containing 0.4 mg metal cm -2 , with the cell presenting potential losses below 200 mV at 1 A cm -2 , with respect to the system fed with pure H 2 . For the PdPt/C catalysts no CO 2 formation was seen at the PEMFC anode outlet, indicating that the CO tolerance is improved due to the existence of more free surface sites for H 2 electrooxidation, probably due to a lower Pd-CO interaction compared to pure Pd or Pt. For PdPtRu/C the CO tolerance may also have a contribution from the bifunctional mechanism, as shown by the presence of CO 2 in the PEMFC anode outlet

  3. Effect of Ni doping on the structural and magnetic properties of FePt nanoparticles

    International Nuclear Information System (INIS)

    Yang, H.-W.; Chung, C.-M.; Ding, Jack Y.

    2007-01-01

    A serial of FePtNi nanoparticles were investigated on their crystal structure and magnetic properties. The FePtNi nanoparticles were synthesized simultaneously by the reduction of iron (III) acetylacetonate, platinum (II) acetylacetonate and nickel (II) acetylacetonate with 1,2-hexadecanediol as the reducing agent. The X-ray diffraction patterns indicate that the addition of 8, 12, 17 at% Ni in FePt nanoparticles suppressed the transformation of the particles from disorder face-centered cubic to order face-centered tetragonal L1 0 -phase under annealing treatment. However, further increasing Ni contents to 21 at%, the nanoparticle transformed to L1 2 phase. Doping of Ni into the FePt compound system may decrease coercivity and crystal anisotropy energy. A maximum coercivity of 7 KOe at room temperature was obtained for (Fe 52 Pt 48 ) 92 Ni 8 nanoparticles after annealing at 600 deg. C for 30 min

  4. Pt-catalyzed ozonation of aqueous phenol solution using high-gravity rotating packed bed

    International Nuclear Information System (INIS)

    Chang, Chia-Chi; Chiu, Chun-Yu; Chang, Ching-Yuan; Chang, Chiung-Fen; Chen, Yi-Hung; Ji, Dar-Ren; Tseng, Jyi-Yeong; Yu, Yue-Hwa

    2009-01-01

    In this study, a high-gravity rotating packed bed (HGRPB or HG) was used as a catalytic ozonation (Cat-OZ) reactor to decompose phenol. The operation of HGRPB system was carried out in a semi-batch apparatus which combines two major parts, namely the rotating packed bed (RPB) and photo-reactor (PR). The high rotating speed of RPB can give a high volumetric gas-liquid mass transfer coefficient with one or two orders of magnitude higher than those in the conventional packed beds. The platinum-containing catalyst (Dash 220N, Pt/γ-Al 2 O 3 ) and activated alumina (γ-Al 2 O 3 ) were packed in the RPB respectively to adsorb molecular ozone and the target pollutant of phenol on the surface to catalyze the oxidation of phenol. An ultra violet (UV) lamp (applicable wavelength λ = 200-280 nm) was installed in the PR to enhance the self-decomposition of molecular ozone in water to form high reactive radical species. Different combinations of advanced oxidation processes (AOPs) with the HGRPB for the degradation of phenol were tested. These included high-gravity OZ (HG-OZ), HG catalytic OZ (HG-Cat-OZ), HG photolysis OZ (HG-UV-OZ) and HG-Cat-OZ with UV (HG-Cat-UV-OZ). The decomposition efficiency of total organic compound (η TOC ) of HG-UV-OZ with power of UV (P UV ) of 16 W is 54% at applied dosage of ozone per volume sample m A,in = 1200 mg L -1 (reaction time t = 20 min), while that of HG-OZ without the UV irradiation is 24%. After 80 min oxidation (m A,in = 4800 mg L -1 ), the η TOC of HG-UV-OZ is as high as 94% compared to 82% of HG-OZ process. The values of η TOC for HG-Cat-OZ process with m S = 42 g are 56% and 87% at m A,in = 1200 and 4800 mg L -1 , respectively. By increasing the catalyst mass to 77 g, the η TOC for the HG-Cat-OZ process reaches 71% and 90% at m A,in = 1200 and 4800 mg L -1 , respectively. The introduction of Pt/γ-Al 2 O 3 as well as UV irradiation in the HG-OZ process can enhance the η TOC of phenol significantly, while γ-Al 2 O 3 exhibits

  5. Experiment prediction for Loft Nonnuclear Experiment L1-4

    International Nuclear Information System (INIS)

    White, J.R.; Berta, V.T.; Holmstrom, H.L.O.

    1977-04-01

    A computer analysis, using the WHAM and RELAP4 computer codes, was performed to predict the LOFT system thermal-hydraulic response for Experiment L1-4 of the nonnuclear (isothermal) test series. Experiment L1-4 will simulate a 200 percent double-ended offset shear in the cold leg of a four-loop large pressurized water reactor. A core simulator will be used to provide a reactor vessel pressure drop representative of the LOFT nuclear core. Experiment L1-4 will be initiated with a nominal isothermal primary coolant temperature of 282.2 0 C, a pressurizer pressure of 15.51 MPa, and a primary coolant flow of 270.9 kg/s. In general, the predictions of saturated blowdown for Experiment Ll-4 are consistent with the expected system behavior, and predicted trends agree with results from Semiscale Test S-01-4A, which simulated the Ll-4 experiment conditions

  6. L 1 Generalized Procrustes 2D Shape Alignment

    DEFF Research Database (Denmark)

    Larsen, Rasmus

    2008-01-01

    on the orientation of the coordinate system, i.e. it is not rotationally invariant. However, by simultaneously minimizing the city block distances in a series of rotated coordinate systems we are able to approximate the circular equidistance curves of Euclidean distances with a regular polygonal equidistance curve...... to the precision needed. Using 3 coordinate systems rotated 30 degrees we get a 12 sided regular polygon, with which we achieve deviations from Euclidean distances less than 2 % over all directions. This new formulation allows for minimization in the L1-norm using LP. We demonstrate that the use of the L1-norm...

  7. PT and INR Test

    Science.gov (United States)

    ... Plasma Free Metanephrines Platelet Count Platelet Function Tests Pleural Fluid Analysis PML-RARA Porphyrin Tests Potassium Prealbumin ... and vitamin K (either in a multivitamin or liquid nutrition supplement) may decrease PT. Certain foods, such ...

  8. High-coercivity FePt sputtered films

    International Nuclear Information System (INIS)

    Luong, N.H.; Hiep, V.V.; Hong, D.M.; Chau, N.; Linh, N.D.; Kurisu, M.; Anh, D.T.K.; Nakamoto, G.

    2005-01-01

    Fe 56 Pt 44 thin films have been prepared by RF magnetron sputtering on Si substrates. The substrate temperature was kept at 350 deg C. The X-ray diffraction patterns of as-deposited FePt films exhibited a disordered structure. Annealing of the films at 650-685 deg C for 1 h yielded an ordered L1 0 phase with FCT structure. The high value for coercivity H C of 17 kOe was obtained at room temperature for the 68 nm thick film annealed at 685 deg C. The hard magnetic properties as well as grain structure of the films strongly depend on the annealing conditions

  9. CoPt nanoparticles deposited by electron beam evaporation

    International Nuclear Information System (INIS)

    Castaldi, L.; Giannakopoulos, K.; Travlos, A.; Niarchos, D.; Boukari, S.; Beaurepaire, E.

    2005-01-01

    Co 50 Pt 50 nanoparticles were co-deposited on thermally oxidized Si substrates by electron beam evaporation at 750 deg C. The mean particle sizes are between ∼5 and ∼20 nm and depend on the nominal thickness of the layer. Different processing conditions resulted in different structural and morphological properties of the samples which led to superparamagnetic and ferromagnetic behaviors. The post-annealing treatment of the CoPt nanograins resulted in the crystallization of the L1 0 ordered phase and in the magnetic hardening of nanoparticles with a maximum coercivity of ∼7.4 kOe

  10. Variantes moleculares en el gen L1 del virus del papiloma humano tipo 16, y regiones de la proteína L1 probablemente involucradas en la interacción virus-célula epitelial

    Directory of Open Access Journals (Sweden)

    María Mercedes Bravo

    2004-03-01

    Full Text Available

    pt; font-family: Arial">La infección con virus del papiloma humano de alto riesgo es considerada como el principal factor de riesgo en el desarrollo del cáncer de cuello uterino. Entre los HPV de alto riesgo, el tipo 16 es el más frecuente tanto en mujeres con citología normal, como en mujeres con lesiones premalignas y en cáncer invasivo. Se ha demostrado la existencia de variaciones en la secuencia del genoma de HPV16, estos polimorfismos se han agrupado en cinco ramas filogenéticas denominadas según su distribución geográfica: Europeas (E, Asiaticas-Americanas (AA, Asiáticas (As, Africanas (Af y Norteamericanas (NA; determinadas por sustituciones nucleotídicas en los genes E6, L1 y L2 y la región larga de control.

    pt; font-family: Arial">Varios estudios han sugerido que las variantes no Europeas son más agresivas que las Europeas, esto puede ser el reflejo de una interacción diferente con el huésped y por tanto implicar diferencias en el resultado final de la infección (mayor persistencia o mayor oncogenicidad.

    pt; font-family: Arial">Particularmente se ha demostrado que las variaciones en la secuencia de aminoácidos de la proteína L1, la proteína principal de la cápside viral, pueden modificar las epítopes neutralizantes del virus afectando la efectividad de la respuesta inmune, también estas variaciones pueden afectar la capacidad de ensamble de las cápsides y la afinidad por receptores a nivel epitelial.

    pt; font-family: Arial">El propósito de este estudio fue identificar las variaciones moleculares del gen L1 de HPV16 en aislamientos provenientes de cepillados cervicales de mujeres colombianas con citología normal y con cáncer de cuello uterino, con el fin de analizar si existen variaciones que alteren las regiones

  11. Evidence from adult L1 Afrikaans L2 French

    African Journals Online (AJOL)

    results of this study show that a large number of the L2 learners had indeed acquired ... position in V2-languages (such as German) and in third position in non-V2 ... L1, allows construction types x and y but he will have no problem acquiring .... Modern Foreign Languages at Stellenbosch University at the time of testing.

  12. Discourse Connectives in L1 and L2 Argumentative Writing

    Science.gov (United States)

    Hu, Chunyu; Li, Yuanyuan

    2015-01-01

    Discourse connectives (DCs) are multi-functional devices used to connect discourse segments and fulfill interpersonal levels of discourse. This study investigates the use of selected 80 DCs within 11 categories in the argumentative essays produced by L1 and L2 university students. The analysis is based on the International Corpus Network of Asian…

  13. Biodegradation of alkaline lignin by Bacillus ligniniphilus L1

    Energy Technology Data Exchange (ETDEWEB)

    Zhu, Daochen; Zhang, Peipei; Xie, Changxiao; Zhang, Weimin; Sun, Jianzhong; Qian, Wei-Jun; Yang, Bin

    2017-02-21

    Background: Lignin is the most abundant aromatic biopolymer in the biosphere and it comprises up to 30% of plant biomass. Although lignin is the most recalcitrant component of the plant cell wall, still there are microorganisms able to decompose it or degrade it. Fungi are recognized as the most widely used microbes for lignin degradation. However, bacteria have also been known to be able to utilize lignin as a carbon or energy source. Bacillus ligniniphilus L1 was selected in this study due to its capability to utilize alkaline lignin as a single carbon or energy source and its excellent ability to survive in extreme environments. Results: To investigate the aromatic metabolites of strain L1 decomposing alkaline lignin, GC-MS analyze was performed and fifteen single phenol ring aromatic compounds were identified. The dominant absorption peak included phenylacetic acid, 4-hydroxy-benzoicacid, and vanillic acid with the highest proportion of metabolites resulting in 42%. Comparison proteomic analysis were carried out for further study showed that approximately 1447 kinds of proteins were produced, 141 of which were at least 2-fold up-regulated with alkaline lignin as the single carbon source. The up-regulated proteins contents different categories in the biological functions of protein including lignin degradation, ABC transport system, environmental response factors, protein synthesis and assembly, etc. Conclusions: GC-MS analysis showed that alkaline lignin degradation of strain L1 produced 15 kinds of aromatic compounds. Comparison proteomic data and metabolic analysis showed that to ensure the degradation of lignin and growth of strain L1, multiple aspects of cells metabolism including transporter, environmental response factors, and protein synthesis were enhanced. Based on genome and proteomic analysis, at least four kinds of lignin degradation pathway might be present in strain L1, including a Gentisate pathway, the benzoic acid pathway and the

  14. Facile synthesis of flower like FePt@ZnO core–shell structure and its bifunctional properties

    Energy Technology Data Exchange (ETDEWEB)

    Majeed, Jerina [Chemistry Division, Bhabha Atomic Research Centre, Trombay, Mumbai 400085 (India); Jayakumar, O.D., E-mail: ddjaya@barc.gov.in [Chemistry Division, Bhabha Atomic Research Centre, Trombay, Mumbai 400085 (India); Mandal, B.P. [Chemistry Division, Bhabha Atomic Research Centre, Trombay, Mumbai 400085 (India); Salunke, H.G. [Technical Physics Division, Bhabha Atomic Research Centre, Trombay, Mumbai 400085 (India); Naik, R. [Department of Physics, Wayne State University, Detroit, MI 48202 (United States); Tyagi, A.K., E-mail: aktyagi@barc.gov.in [Chemistry Division, Bhabha Atomic Research Centre, Trombay, Mumbai 400085 (India)

    2014-06-01

    Graphical abstract: Flower shaped FePt and ZnO coated FePt with core–shell nanostructures are synthesized by a facile solvothermal procedure. Shell thickness of ZnO over FePt core was tuned by varying FePt concentration with respect to ZnO. Hybrid structure with lower FePt concentration exhibited bifunctionality such as near room temperature ferromagnetism and photoluminescence. Pristine FePt crystallize in the fct (L1{sub 0}) phase whereas it converts into fcc phase in presence of ZnO. - Highlights: • FePt@ZnO hybrid core–shell particles, with unique flower shape morphology have been prepared by solvothermal method. • Phase transition of fct-FePt to fcc-FePt has been found in presence of ZnO nanoparticles. • Plausible mechanism for growth of flowershaped nanoparticle is in accordance with energy minimization principle. • The core shell structure (FePt@ZnO) exhibits bi-functional properties. - Abstract: Flower shaped FePt and ZnO coated FePt (FePt@ZnO) core–shell nanostructures are synthesized by a facile solvothermal procedure. Two different compositions (molar ratio) of FePt and ZnO (FePt:ZnO = 1:3 and FePt:ZnO = 1:6) core–shells with different thicknesses of ZnO shells were synthesized. Hybrid FePt@ZnO core–shell flower structure with lower FePt concentration (FePt:ZnO = 1:6) exhibited bifunctionality including near room temperature ferromagnetism and photoluminescence at ambient conditions. X-ray diffraction patterns of pristine FePt showed partially ordered face centred tetragonal (fct) L1{sub 0} phase whereas ZnO coated FePt (FePt@ZnO) nanostructures showed hexagonal ZnO and disordered phase of FePt with fcc structure. The phase transition of fct FePt to fcc phase occurring in presence of ZnO is further confirmed by transmission electron microscopy and magnetic measurement studies. The formation of the nanoflowers was possibly due to growth along the [0 1 1] or [0 0 1] direction, keeping the core nearly spherical in accordance with the

  15. Columnar grain growth of FePt(L10) thin films

    International Nuclear Information System (INIS)

    Yang En; Ho Hoan; Laughlin, David E.; Zhu Jiangang

    2012-01-01

    An experimental approach for obtaining perpendicular FePt-SiOx thin films with a large height to diameter ratio FePt(L1 0 ) columnar grains is presented in this work. The microstructure for FePt-SiOx composite thin films as a function of oxide volume fraction, substrate temperature, and film thickness is studied by plan view and cross section TEM. The relations between processing, microstructure, epitaxial texture, and magnetic properties are discussed. By tuning the thickness of the magnetic layer and the volume fraction of oxide in the film at a sputtering temperature of 410 deg. C, a 16 nm thick perpendicular FePt film with ∼8 nm diameter of FePt grains was obtained. The height to diameter ratio of the FePt grains was as large as 2. Ordering at lower temperature can be achieved by introducing a Ag sacrificial layer.

  16. Safety and Activity of Anti–PD-L1 Antibody in Patients with Advanced Cancer

    Science.gov (United States)

    Brahmer, Julie R.; Tykodi, Scott S.; Chow, Laura Q.M.; Hwu, Wen-Jen; Topalian, Suzanne L.; Hwu, Patrick; Drake, Charles G.; Camacho, Luis H.; Kauh, John; Odunsi, Kunle; Pitot, Henry C.; Hamid, Omid; Bhatia, Shailender; Martins, Renato; Eaton, Keith; Chen, Shuming; Salay, Theresa M.; Alaparthy, Suresh; Grosso, Joseph F.; Korman, Alan J.; Parker, Susan M.; Agrawal, Shruti; Goldberg, Stacie M.; Pardoll, Drew M.; Gupta, Ashok; Wigginton, Jon M.

    2013-01-01

    BACKGROUND Programmed death 1 (PD-1) protein, a T-cell coinhibitory receptor, and one of its ligands, PD-L1, play a pivotal role in the ability of tumor cells to evade the host’s immune system. Blockade of interactions between PD-1 and PD-L1 enhances immune function in vitro and mediates antitumor activity in preclinical models. METHODS In this multicenter phase 1 trial, we administered intravenous anti–PD-L1 antibody (at escalating doses ranging from 0.3 to 10 mg per kilogram of body weight) to patients with selected advanced cancers. Anti–PD-L1 antibody was administered every 14 days in 6-week cycles for up to 16 cycles or until the patient had a complete response or confirmed disease progression. RESULTS As of February 24, 2012, a total of 207 patients — 75 with non–small-cell lung cancer, 55 with melanoma, 18 with colorectal cancer, 17 with renal-cell cancer, 17 with ovarian cancer, 14 with pancreatic cancer, 7 with gastric cancer, and 4 with breast cancer — had received anti–PD-L1 antibody. The median duration of therapy was 12 weeks (range, 2 to 111). Grade 3 or 4 toxic effects that investigators considered to be related to treatment occurred in 9% of patients. Among patients with a response that could be evaluated, an objective response (a complete or partial response) was observed in 9 of 52 patients with melanoma, 2 of 17 with renal-cell cancer, 5 of 49 with non–small-cell lung cancer, and 1 of 17 with ovarian cancer. Responses lasted for 1 year or more in 8 of 16 patients with at least 1 year of follow-up. CONCLUSIONS Antibody-mediated blockade of PD-L1 induced durable tumor regression (objective response rate of 6 to 17%) and prolonged stabilization of disease (rates of 12 to 41% at 24 weeks) in patients with advanced cancers, including non–small-cell lung cancer, melanoma, and renal-cell cancer. (Funded by Bristol-Myers Squibb and others; ClinicalTrials.gov number, NCT00729664.) PMID:22658128

  17. Conditions for l =1 Pomeranchuk instability in a Fermi liquid

    Science.gov (United States)

    Wu, Yi-Ming; Klein, Avraham; Chubukov, Andrey V.

    2018-04-01

    We perform a microscopic analysis of how the constraints imposed by conservation laws affect q =0 Pomeranchuk instabilities in a Fermi liquid. The conventional view is that these instabilities are determined by the static interaction between low-energy quasiparticles near the Fermi surface, in the limit of vanishing momentum transfer q . The condition for a Pomeranchuk instability is set by Flc (s )=-1 , where Flc (s ) (a Landau parameter) is a properly normalized partial component of the antisymmetrized static interaction F (k ,k +q ;p ,p -q ) in a charge (c) or spin (s) subchannel with angular momentum l . However, it is known that conservation laws for total spin and charge prevent Pomeranchuk instabilities for l =1 spin- and charge-current order parameters. Our study aims to understand whether this holds only for these special forms of l =1 order parameters or is a more generic result. To this end we perform a diagrammatic analysis of spin and charge susceptibilities for charge and spin density order parameters, as well as perturbative calculations to second order in the Hubbard U . We argue that for l =1 spin-current and charge-current order parameters, certain vertex functions, which are determined by high-energy fermions, vanish at Fl=1 c (s )=-1 , preventing a Pomeranchuk instability from taking place. For an order parameter with a generic l =1 form factor, the vertex function is not expressed in terms of Fl=1 c (s ), and a Pomeranchuk instability may occur when F1c (s )=-1 . We argue that for other values of l , a Pomeranchuk instability may occur at Flc (s )=-1 for an order parameter with any form factor.

  18. Anti-PD-L1 Treatment Induced Central Diabetes Insipidus.

    Science.gov (United States)

    Zhao, Chen; Tella, Sri Harsha; Del Rivero, Jaydira; Kommalapati, Anuhya; Ebenuwa, Ifechukwude; Gulley, James; Strauss, Julius; Brownell, Isaac

    2018-02-01

    Immune checkpoint inhibitors, including anti-programmed cell death protein 1 (PD-1), anti-programmed cell death protein ligand 1 (PD-L1), and anti-cytotoxic T-lymphocyte antigen 4 (anti-CTLA4) monoclonal antibodies, have been widely used in cancer treatment. They are known to cause immune-related adverse events (irAEs), which resemble autoimmune diseases. Anterior pituitary hypophysitis with secondary hypopituitarism is a frequently reported irAE, especially in patients receiving anti-CTLA4 treatment. In contrast, posterior pituitary involvement, such as central diabetes insipidus (DI), is relatively rare and is unreported in patients undergoing PD-1/PD-L1 blockade. We describe a case of a 73-year-old man with Merkel cell carcinoma who received the anti-PD-L1 monoclonal antibody avelumab and achieved partial response. The patient developed nocturia, polydipsia, and polyuria 3 months after starting avelumab. Further laboratory testing revealed central DI. Avelumab was held and he received desmopressin for the management of central DI. Within 6 weeks after discontinuation of avelumab, the patient's symptoms resolved and he was eventually taken off desmopressin. The patient remained off avelumab and there were no signs or symptoms of DI 2 months after the discontinuation of desmopressin. To our knowledge, this is the first report of central DI associated with anti-PD-L1 immunotherapy. The patient's endocrinopathy was successfully managed by holding treatment with the immune checkpoint inhibitor. This case highlights the importance of early screening and appropriate management of hormonal irAEs in subjects undergoing treatment with immune checkpoint inhibitors to minimize morbidity and mortality. Copyright © 2017 Endocrine Society

  19. Selection of regularization parameter for l1-regularized damage detection

    Science.gov (United States)

    Hou, Rongrong; Xia, Yong; Bao, Yuequan; Zhou, Xiaoqing

    2018-06-01

    The l1 regularization technique has been developed for structural health monitoring and damage detection through employing the sparsity condition of structural damage. The regularization parameter, which controls the trade-off between data fidelity and solution size of the regularization problem, exerts a crucial effect on the solution. However, the l1 regularization problem has no closed-form solution, and the regularization parameter is usually selected by experience. This study proposes two strategies of selecting the regularization parameter for the l1-regularized damage detection problem. The first method utilizes the residual and solution norms of the optimization problem and ensures that they are both small. The other method is based on the discrepancy principle, which requires that the variance of the discrepancy between the calculated and measured responses is close to the variance of the measurement noise. The two methods are applied to a cantilever beam and a three-story frame. A range of the regularization parameter, rather than one single value, can be determined. When the regularization parameter in this range is selected, the damage can be accurately identified even for multiple damage scenarios. This range also indicates the sensitivity degree of the damage identification problem to the regularization parameter.

  20. Prospective role of indigenous Exiguobacterium profundum PT2 in arsenic biotransformation and biosorption by planktonic cultures and biofilms.

    Science.gov (United States)

    Saba; Andreasen, R; Li, Y; Rehman, Y; Ahmed, M; Meyer, R L; Sabri, A N

    2018-02-01

    The aim of this study was to analyse arsenic (As) transformation and biosorption by indigenous As-resistant bacteria both in planktonic and biofilm modes of growth. As-resistant bacteria were isolated from industrial waste water and strain PT2, and identified as Exiguobacterium profundum through 16S rRNA gene sequencing was selected for further study. As transformation and biosorption by E. profundumPT2 was determined by HPLC-ICP-MS analysis. Planktonic cultures reduced 3·73 mmol l -1 As 5+ into As 3+ from artificial waste water effluent after 48-h incubation. In case of biosorption, planktonic cultures and biofilms exhibited 25·2 and 29·4 mg g -1 biomass biosorption, respectively. As biosorption kinetics followed Freundlich isotherm and pseudo second-order model. Biofilm formation peaked after 3 days of incubation, and in the presence of As stress, biofilm formation was significantly affected in contrast to control (P biofilms with an increased demand of nutrients was revealed by minimum roughness and maximum surface to biovolume ratio measured through CLSM analysis. Indigenous As-resistant E. profundumPT2 was found capable of As transformation and biosorption both in the form of planktonic cultures and biofilms. Indigenous biofilm forming E. profundum PT2 revealing As biosorption and biotransformation potential is presented an eco-friendly and cost-effective source for As remediation that can be implemented for waste water treatment. © 2017 The Society for Applied Microbiology.

  1. Development and structural characterization of exchange-spring-like nanomagnets in (Fe,Co)-Pt bulk nanocrystalline alloys

    Energy Technology Data Exchange (ETDEWEB)

    Crisan, O.; Crisan, A.D.; Mercioniu, I. [National Institute for Materials Physics, P.O. Box MG-7, 077125 Magurele, Bucharest (Romania); Nicula, R. [Empa, Swiss Federal Laboratories for Materials Science and Technology, Advanced Materials Processing, Feuerwerkerstr. 39, CH-3602 Thun (Switzerland); Vasiliu, F., E-mail: fvasiliu@infim.ro [National Institute for Materials Physics, P.O. Box MG-7, 077125 Magurele, Bucharest (Romania)

    2016-03-01

    FePt-based alloys are currently under scrutiny for their possible use as materials for perpendicular magnetic recording. Another possible application is in the field of permanent magnets without rare-earths, magnets that may operate at higher temperatures than the classic Nd–Fe–B magnets. Within this study, FeCoPt alloys prepared by rapid solidification from the melt are structurally and magnetically characterized. In the as-cast FeCoPt ribbons, a three-phase structure comprising well-ordered CoFePt and CoPt L1{sub 0} phases embedded in a disordered fcc FePt matrix was evidenced by XRD, HREM and SAED. Extended transmission electron microscopy analysis demonstrates the incipient formation of ordered L1{sub 0} phases. X-ray diffraction was used to characterize the phase structure and to obtain the structural parameters of interest for L1{sub 0} ordering. In the as-cast state, the co-existence of hard magnetic CoFePt and CoPt L1{sub 0} tetragonal phases with the soft fcc FePt phase is obtained within a refined microstructure made of alternatively disposed grains (grain sizes from 1 to 7 nm). Following a thermal treatment of 1 h at 670 °C, the soft magnetic fcc matrix phase transforms to tetragonal L1{sub 0} phases (disorder–order transition). The resulting CoPt and CoFePt L1{sub 0} phases have grains of around 5–20 nm in size. In the as-cast state, magnetic measurements show a quite large remanence (0.75 T), close to the value of the parent L1{sub 0} FePt phase. Coercive fields of about 200 kA/m at 5 K were obtained, comparable with those reported for some FePt-based bulk alloys. Upon annealing both remanence and coercivity are increased and values of up to 254 kA/m at 300 K are obtained. The polycrystalline structure of the annealed FeCoPt samples, as well as the formation of multiple c-axis domains in different CoPt and CoFePt regions (which leads to a reduction of the magneto-crystalline anisotropy) may account for the observed coercive fields that are

  2. Microwave-polyol synthesis and electrocatalytic performance of Pt/graphene nanocomposites

    International Nuclear Information System (INIS)

    Liao, Chien-Shiun; Liao, Chien-Tsao; Tso, Ching-Yu; Shy, Hsiou-Jeng

    2011-01-01

    Highlights: · One-pot microwave-polyol synthesis of Pt/graphene electrocatalyst. · Simultaneous formation of Pt nanoparticles and reduction of graphene oxide. · Electrocatalytic activities depend on the morphology of the deposited Pt particles. · Dense dispersion of isolated Pt particles with high electrochemical active surface. · Few particle clusters of Pt have large number of active sites for methanol oxidation. - Abstract: Graphene oxide (GO) prepared by the modified Hummers method is used as a support in the formation of a Pt/GO nanocomposite electrocatalyst by microwave-polyol synthesis. The effects of microwave reaction times on particle size, dispersion, and electrocatalytic performance of Pt nanoparticles are studied using wide-angle X-ray diffractometery, Raman spectroscopy, transmission electron microscopy and three-electrode electrochemical measurements. The results indicate that Pt nanoparticles nucleation and growth occur, and the particles are uniformly deposited on the GO nanosheets within a short time. The maximum electrochemical active surface area 85.71 m 2 g -1 for a Pt/GO reaction time of 5 min, is a result of the deposition of a dense dispersion of small Pt particles. The highest methanol oxidation peak current density, I f , of 0.59 A mg -1 occurs for a Pt/GO reaction time of 10 min and is due to the formation of interconnecting Pt particles clusters. This novel Pt/GO nanocomposite electrocatalyst with high electrocatalytic activities has the potential for use as an anode material in fuel cells.

  3. L1 French learning of L2 Spanish past tenses: L1 transfer versus aspect and interface issues

    Directory of Open Access Journals (Sweden)

    José Amenós Pons

    2017-09-01

    Full Text Available This paper examines the process of acquiring L2s that are closely related to the L1 through data on how adult French speakers learning L2 Spanish in a formal setting develop knowledge and use of past tenses in this L2. We consider the role of transfer and simplification in acquiring mental representations of the L2 grammar, specifically in the area of tense and aspect, and how learners deal with integrating grammatically encoded, lexical and discursive information, including mismatching feature combinations leading to particular inferential effects on interpretation. Data is presented on the Spanish past tenses (simple and compound past, pluperfect, imperfect and progressive forms from two tasks, an oral production filmretell and a multiple-choice interpretation task, completed by learners at A2, B1, B2 and C1 CEFR levels (N = 20-24 per level. L1 influence is progressively attenuated as proficiency increases. Difficulties were not always due to negative L1 transfer, but related also to grammar-discourse interface issues when integrating linguistic and pragmatic information in the interpretation process. This has clear implications for the teaching of closely related languages: instruction should not only focus on crosslinguistic contrasts, but also prioritize uses requiring complex interface integration, which are harder to process.

  4. Nanocrystalline Fe-Pt alloys. Phase transformations, structure and magnetism

    Energy Technology Data Exchange (ETDEWEB)

    Lyubina, J.V.

    2006-12-21

    This work has been devoted to the study of phase transformations involving chemical ordering and magnetic properties evolution in bulk Fe-Pt alloys composed of nanometersized grains. Nanocrystalline Fe{sub 100-x}Pt{sub x} (x=40-60) alloys have been prepared by mechanical ball milling of elemental Fe and Pt powders at liquid nitrogen temperature. The as-milled Fe-Pt alloys consist of {proportional_to} 100 {mu}m sized particles constituted by randomly oriented grains having an average size in the range of 10-40 nm. Depending on the milling time, three major microstructure types have been obtained: samples with a multilayer-type structure of Fe and Pt with a thickness of 20-300 nm and a very thin (several nanometers) A1 layer at their interfaces (2 h milled), an intermediate structure, consisting of finer lamellae of Fe and Pt (below approximately 100 nm) with the A1 layer thickness reaching several tens of nanometers (4 h milled) and alloys containing a homogeneous A1 phase (7 h milled). Subsequent heat treatment at elevated temperatures is required for the formation of the L1{sub 0} FePt phase. The ordering develops via so-called combined solid state reactions. It is accompanied by grain growth and thermally assisted removal of defects introduced by milling and proceeds rapidly at moderate temperatures by nucleation and growth of the ordered phases with a high degree of the long-range order. In a two-particle interaction model elaborated in the present work, the existence of hysteresis in recoil loops has been shown to arise from insufficient coupling between the low- and the high-anisotropy particles. The model reveals the main features of magnetisation reversal processes observed experimentally in exchange-coupled systems. Neutron diffraction has been used for the investigation of the magnetic structure of ordered and partially ordered nanocrystalline Fe-Pt alloys. (orig.)

  5. The L1-shell ionisation of atoms by relativistic particles

    International Nuclear Information System (INIS)

    Moiseiwitsch, B.L.; Norrington, P.H.

    1979-01-01

    An expression for the L 1 -shell ionisation cross sections of atoms by high-energy particles has been derived using the relativistic plane-wave Born approximation. The incident and scattered particles are described by Dirac plane waves while Darwin hydrogenic wavefunctions are used for the atomic electrons. A comparison is made with experimental total cross sections for incident electrons in the energy range 1-2 MeV. The agreement is a considerable improvement on that obtained using the non-relativistic planewave Born approximation. (author)

  6. House dust mite induces expression of intercellular adhesion molecule-1 in EoL-1 human eosinophilic leukemic cells.

    Science.gov (United States)

    Kwon, Byoung Chul; Sohn, Myung Hyun; Kim, Kyung Won; Kim, Eun Soo; Kim, Kyu-Earn; Shin, Myeong Heon

    2007-10-01

    The house dust mite (HDM) is considered to be the most common indoor allergen associated with bronchial asthma. In this study, we investigated whether crude extract of the HDM Dermatophagoides farinae could activate human eosinophilic leukemic cells (EoL-1) to induce upregulation of cell-surface adhesion molecules. When EoL-1 cells were incubated with D. farinae extract, expression of intercellular adhesion molecule-1 (ICAM-1) significantly increased on the cell surfaces compared to cells incubated with medium alone. In contrast, surface expression of CD11b and CD49d in EoL-1 cells was not affected by D. farinae extract. In addition, pretreatment of cells with NF-kappaB inhibitor (MG-132) or JNK inhibitor (SP600125) significantly inhibited ICAM-1 expression promoted by HDM extract. However, neither p38 MAP kinase inhibitor nor MEK inhibitor prevented HDM-induced ICAM-1 expression in EoL-1 cells. These results suggest that crude extract of D. farinae induces ICAM-1 expression in EoL-1 cells through signaling pathways involving both NF-kappaB and JNK.

  7. Pt, Co–Pt and Fe–Pt alloy nanoclusters encapsulated in virus capsids

    International Nuclear Information System (INIS)

    Okuda, M; Eloi, J-C; Jones, S E Ward; Schwarzacher, W; Verwegen, M; Cornelissen, J J L M

    2016-01-01

    Nanostructured Pt-based alloys show great promise, not only for catalysis but also in medical and magnetic applications. To extend the properties of this class of materials, we have developed a means of synthesizing Pt and Pt-based alloy nanoclusters in the capsid of a virus. Pure Pt and Pt-alloy nanoclusters are formed through the chemical reduction of [PtCl 4 ] − by NaBH 4 with/without additional metal ions (Co or Fe). The opening and closing of the ion channels in the virus capsid were controlled by changing the pH and ionic strength of the solution. The size of the nanoclusters is limited to 18 nm by the internal diameter of the capsid. Their magnetic properties suggest potential applications in hyperthermia for the Co–Pt and Fe–Pt magnetic alloy nanoclusters. This study introduces a new way to fabricate size-restricted nanoclusters using virus capsid. (paper)

  8. L1 Adaptive Control for a Vertical Rotor Orientation System

    Directory of Open Access Journals (Sweden)

    Sijia Liu

    2016-08-01

    Full Text Available Bottom-fixed vertical rotating devices are widely used in industrial and civilian fields. The free upside of the rotor will cause vibration and lead to noise and damage during operation. Meanwhile, parameter uncertainties, nonlinearities and external disturbances will further deteriorate the performance of the rotor. Therefore, in this paper, we present a rotor orientation control system based on an active magnetic bearing with L 1 adaptive control to restrain the influence of the nonlinearity and uncertainty and reduce the vibration amplitude of the vertical rotor. The boundedness and stability of the adaptive system are analyzed via a theoretical derivation. The impact of the adaptive gain is discussed through simulation. An experimental rig based on dSPACE is designed to test the validity of the rotor orientation system. The experimental results show that the relative vibration amplitude of the rotor using the L 1 adaptive controller will be reduced to ∼50% of that in the initial state, which is a 10% greater reduction than can be achieved with the nonadaptive controller. The control approach in this paper is of some significance to solve the orientation control problem in a low-speed vertical rotor with uncertainties and nonlinearities.

  9. L1 track finding for a time multiplexed trigger

    Energy Technology Data Exchange (ETDEWEB)

    Cieri, D., E-mail: davide.cieri@bristol.ac.uk [University of Bristol, Bristol (United Kingdom); Rutherford Appleton Laboratory, Didcot (United Kingdom); Brooke, J.; Grimes, M. [University of Bristol, Bristol (United Kingdom); Newbold, D. [University of Bristol, Bristol (United Kingdom); Rutherford Appleton Laboratory, Didcot (United Kingdom); Harder, K.; Shepherd-Themistocleous, C.; Tomalin, I. [Rutherford Appleton Laboratory, Didcot (United Kingdom); Vichoudis, P. [CERN, Geneva (Switzerland); Reid, I. [Brunel University, London (United Kingdom); Iles, G.; Hall, G.; James, T.; Pesaresi, M.; Rose, A.; Tapper, A.; Uchida, K. [Imperial College, London (United Kingdom)

    2016-07-11

    At the HL-LHC, proton bunches will cross each other every 25 ns, producing an average of 140 pp-collisions per bunch crossing. To operate in such an environment, the CMS experiment will need a L1 hardware trigger able to identify interesting events within a latency of 12.5 μs. The future L1 trigger will make use also of data coming from the silicon tracker to control the trigger rate. The architecture that will be used in future to process tracker data is still under discussion. One interesting proposal makes use of the Time Multiplexed Trigger concept, already implemented in the CMS calorimeter trigger for the Phase I trigger upgrade. The proposed track finding algorithm is based on the Hough Transform method. The algorithm has been tested using simulated pp-collision data. Results show a very good tracking efficiency. The algorithm will be demonstrated in hardware in the coming months using the MP7, which is a μTCA board with a powerful FPGA capable of handling data rates approaching 1 Tb/s.

  10. Aspartame downregulates 3T3-L1 differentiation.

    Science.gov (United States)

    Pandurangan, Muthuraman; Park, Jeongeun; Kim, Eunjung

    2014-10-01

    Aspartame is an artificial sweetener used as an alternate for sugar in several foods and beverages. Since aspartame is 200 times sweeter than traditional sugar, it can give the same level of sweetness with less substance, which leads to lower-calorie food intake. There are reports that consumption of aspartame-containing products can help obese people lose weight. However, the potential role of aspartame in obesity is not clear. The present study investigated whether aspartame suppresses 3T3-L1 differentiation, by downregulating phosphorylated peroxisome proliferator-activated receptor γ (p-PPARγ), peroxisome proliferator-activated receptor γ (PPARγ), fatty acid-binding protein 4 (FABP4), CCAAT/enhancer-binding protein α (C/EBPα), and sterol regulatory element-binding protein 1 (SREBP1), which are critical for adipogenesis. The 3T3-L1 adipocytes were cultured and differentiated for 6 d in the absence and presence of 10 μg/ml of aspartame. Aspartame reduced lipid accumulation in differentiated adipocytes as evidenced by Oil Red O staining. qRT-PCR analysis showed that the PPARγ, FABP4, and C/EBPα mRNA expression was significantly reduced in the aspartame-treated adipocytes. Western blot analysis showed that the induction of p-PPARγ, PPARγ, SREBP1, and adipsin was markedly reduced in the aspartame-treated adipocytes. Taken together, these data suggest that aspartame may be a potent substance to alter adipocyte differentiation and control obesity.

  11. L1 Track Finding for a Time Multiplexed Trigger

    CERN Document Server

    AUTHOR|(CDS)2090481; Grimes, M.; Newbold, D.; Harder, K.; Shepherd-Themistocleous, C.; Tomalin, I.; Vichoudis, P.; Reid, I.; Iles, G.; Hall, G.; James, T.; Pesaresi, M.; Rose, A.; Tapper, A.; Uchida, K.

    2016-01-01

    At the HL-LHC, proton bunches will cross each other every 25 ns, producing an average of 140 p p-collisions per bunch crossing. To operate in such an environment, the CMS experiment will need a L1 hardware trigger able to identify interesting events within a latency of 12.5 us. The future L1 trigger will make use also of data coming from the silicon tracker to control the trigger rate. The architecture that will be used in future to process tracker data is still under discussion. One interesting proposal makes use of the Time Multiplexed Trigger concept, already implemented in the CMS calorimeter trigger for the Phase I trigger upgrade. The proposed track finding algorithm is based on the Hough Transform method. The algorithm has been tested using simulated pp-collision data. Results show a very good tracking efficiency. The algorithm will be demonstrated in hardware in the coming months using the MP7, which is a uTCA board with a powerful FPGA capable of handling data rates approaching 1 Tb/s.

  12. Influence of an Fe cap layer on the structural and magnetic properties of Fe49Pt51/Fe bi-layers

    International Nuclear Information System (INIS)

    Chao-Yang, Duan; Bin, Ma; Zong-Zhi, Zhang; Qing-Yuan, Jin; Fu-Lin, Wei

    2009-01-01

    The influences of an Fe cap layer on the structural and magnetic properties of FePt/Fe bi-layers are investigated. Compared with single FePt alloy films, a thin Fe layer can affect the crystalline orientation and improve the chemical ordering of L1 0 FePt films. Moreover, the coercivity increases when a thin Fe layer covers the FePt layer. Beyond a critical thickness, however, the Fe cover layer quickens the magnetization reversal of Fe 49 Pt 51 /Fe bi-layers by their exchange coupling

  13. Growth, structure and magnetic properties of magnetron sputtered FePt thin films

    Energy Technology Data Exchange (ETDEWEB)

    Cantelli, Valentina

    2010-07-01

    The L1{sub 0} FePt phase belongs to the most promising hard ferromagnetic materials for high density recording media. The main challenges for thin FePt films are: (i) to lower the process temperature for the transition from the soft magnetic A1 to the hard magnetic L1{sub 0} phase, (ii) to realize c-axes preferential oriented layers independently from the substrate nature and (iii) to control layer morphology supporting the formation of FePt-L1{sub 0} selforganized isolated nanoislands towards an increase of the signal-to-noise ratio. In this study, dc magnetron sputtered FePt thin films on amorphous substrates were investigated. The work is focused on the correlation between structural and magnetic properties with respect to the influence of deposition parameters like growth mode (cosputtering vs. layer - by - layer) and the variation of the deposition gas (Ar, Xe) or pressure (0.3-3 Pa). In low-pressure Ar discharges, high energetic particle impacts support vacancies formation during layer growth lowering the phase transition temperature to (320{+-}20) C. By reducing the particle kinetic energy in Xe discharges, highly (001) preferential oriented L1{sub 0}-FePt films were obtained on a-SiO{sub 2} after vacuum annealing. L1{sub 0}-FePt nano-island formation was supported by the introduction of an Ag matrix, or by random ballistic aggregation and atomic self shadowing realized by FePt depositions at very high pressure (3 Pa). The high coercivity (1.5 T) of granular, magnetic isotropic FePt layers, deposited in Ar discharges, was measured with SQUID magnetometer hysteresis loops. For non-granular films with (001) preferential orientation the coercivity decreased (0.6 T) together with an enhancement of the out-of- plane anisotropy. Nanoislands show a coercive field close to the values obtained for granular layers but exhibit an in-plane easy axis due to shape anisotropy effects. An extensive study with different synchrotron X-ray scattering techniques, mainly

  14. Structurally simple supported platinum clusters prepared from [Pt15(CO)30]2- on magnesium oxide

    NARCIS (Netherlands)

    Chang, J.R.; Koningsberger, D.C.; Gates, B.C.

    1992-01-01

    A G. Longoni-P. Chini (1976) cluster, [Pt15(CO)30]2-, was prepd. on MgO powder by a surface-mediated synthesis from Na2PtCl6 in the presence of CO. The formation of [Pt15(CO)30]2- and its decarbonylation at 120 Deg under vacuum were characterized by IR and x-ray spectra. The decarbonylated cluster

  15. Solar and Heliospheric Data Requirements: Going Further Than L1

    Science.gov (United States)

    Szabo, A.

    2011-01-01

    Current operational space weather forecasting relies on solar wind observations made by the ACE spacecraft located at the L1 point providing 30-40 minutes warning time. Some use is also made of SOHO and STEREO solar imaging that potentially can give multiple days of warning time. However, our understanding of the propagation and evolution of solar wind transients is still limited resulting in a typical timing uncertainty of approximately 10 hours. In order to improve this critical understanding, a number of NASA missions are being planned. Specifically the Solar Probe Plus and Solar Orbiter missions will investigate the inner Heliospheric evolution of coronal mass ejections and the acceleration and propagation of solar energetic particles. In addition, a number of multi-spacecraft concepts have been studied that have the potential to significantly improve the accuracy of long-term space weather forecasts.

  16. l=1,2 high-beta stellarator

    International Nuclear Information System (INIS)

    Bartsch, R.R.; Cantrell, E.L.; Gribble, R.F.; Klare, K.A.; Kutac, K.J.; Miller, G.; Siemon, R.E.

    1978-01-01

    The final scyllac experiments are described. These experiments utilized a feedback-stabilized, l=1,2 high-beta stellarator configuration and like the previous feedback-stabilization experiments were carried out in a toroidal sector, rather than a complete torus. The energy confinement time, obtained from excluded flux measurements, agrees with a two-dimensional calculation of particle end loss from a straight theta pinch. Because simple end loss was dominant, the energy confinement time was independent of whether equilibrium adjustment or feedback stabilization fields were applied. The dynamical characteristics of the toroidal equilibrium were improved by elimination of the l=0 field used previously, as expected from theory. A modal rather than local feedback control algorithm was used. Although feedback clearly decreased the m=1 motion of the plasma, the experimental test of modal feedback, which is expected from theory to be superior to local feedback, is considered inconclusive because of the limitations imposed by the sector configuration

  17. Preventing dewetting during rapid-thermal annealing of FePt films with enhanced L10 ordering by introducing Ag cap-layers

    International Nuclear Information System (INIS)

    Hsiao, S.N.; Wu, S.C.; Liu, S.H.; Tsai, J.L.; Chen, S.K.; Chang, Y.C.; Lee, H.Y.

    2015-01-01

    High-order FePt continuous films with a strong (001) texture were fabricated on a glass substrate by introducing Ag layers and rapid thermal annealing (RTA). The dewetting of the (001)-textured FePt was suppressed during RTA with high heating rates (>80 K/s). The Ag cap layers not only increased the in-plane tensile stress, but also improved the (001) anisotropy and L1 0 ordering of the FePt layers. All continuous Ag/FePt bilayer films possessed strong perpendicular anisotropies and high-ordered states irrespective of the Ag layer thickness. - Highlights: • Dewetting of (001) FePt fims were suppressed by introducing Ag cap layers. • Ag layers enhanced in-plane tensile stress, (001) texture and L1 0 ordering. • Irrespective of Ag thickness, the Ag/FePt films exhibited strong (001) texture

  18. Magnetic properties and microstructure of low ordering temperature L10 FePt thin films

    International Nuclear Information System (INIS)

    Sun, A.C.; Kuo, P.C.; Chen, S.C.; Chou, C.Y.; Huang, H.L.; Hsu, J.H.

    2004-01-01

    Polycrystalline Fe 52 Pt 48 alloy thin films were prepared by dc magnetron sputtering on preheated natural-oxidized silicon wafer substrates. The film thickness was varied from 10 to 100 nm. The as-deposited film was encapsulated in a quartz tube and postannealed in vacuum at various temperatures for 1 h, then furnace cooled. It is found that the ordering temperature from as-deposited soft magnetic fcc FePt phase to hard magnetic fct L1 0 FePt phase could be reduced to about 350 deg. C by preheating substrate and furnace cooling treatment. The magnetic properties measurements indicated that the in-plane coercivity of the films was increased rapidly as annealing temperature is increased from 300 to 400 deg. C, but it decreased when the annealing temperature is higher than 400 deg. C. X-ray diffraction analysis shown that the as-deposited FePt thin film was a disorder fcc FePt phase. The magnetic measurement indicated that the transformation of disorder fcc FePt to fct L1 0 FePt phase was started at about 350 deg. C, which is consistent with the analysis of x-ray diffraction patterns. From scanning electron microscopy observation and selected area energy disperse spectrum analysis, the distributions of Fe and Pt elements in the films became nonuniform when the annealing temperature was higher than 500 deg. C due to the formation of the Fe 3 Pt phase. After annealing at 400 deg. C, the in plane coercivity of Fe 52 Pt 48 thin film with film thickness of 100 nm is 10 kOe, M s is 580 emu/cm3, and grain size is about 12 nm

  19. Analysis of Ca and Mg in blood of golden hamster using NAA technique

    International Nuclear Information System (INIS)

    Aguiar, Rodrigo O.; Zamboni, Cibele B.; Medeiros, Jose A.G.

    2009-01-01

    Neutron activation analysis (NAA) technique has been used to determine simultaneously Ca and Mg concentrations in whole blood of Golden Hamster. The reference values for Ca (0.17 - 0.29 gL -1 ) and Mg (0.042 - 0.074 gL -1 ) can be used to performed biochemistry investigation using whole blood. (author)

  20. Polymorphisms of vitamin K-related genes (EPHX1 and VKORC1L1) and stable warfarin doses.

    Science.gov (United States)

    Chung, Jee-Eun; Lee, Kyung Eun; Chang, Byung Chul; Gwak, Hye Sun

    2018-01-30

    The aim of this study was to investigate the possible effects of EPHX1 and VKORC1L1 polymorphisms on variability of responses to warfarin. Sixteen single nucleotide polymorphisms (SNPs) in 201 patients with stable warfarin doses were analyzed including genes of VKORC1, CYP2C9, CYP4F2, GGCX, EPHX1 and VKORC1L1. Univariate analysis was conducted for the association of genotypes with stable warfarin doses. Multiple linear regression analysis was used to investigate factors that independently affected the inter-individual variability of warfarin dose requirements. The rs4072879 of VKORC1L1 (A>G) was significantly associated with stable warfarin doses; wild homozygote carriers (AA) required significantly lower stable warfarin doses than those with the variant G allele (5.02±1.56 vs. 5.96±2.01mg; p=0.001). Multivariate analysis showed that EPHX1 rs1877724 and VKORC1L1 rs4072879 accounted for 1.5% and 1.3% of the warfarin dose variability. Adding EPHX1 and VKORC1L1 SNPs to the base model including non-genetic variables (operation age, body weight and the therapy of ACEI or ARB) and genetic variables (VKORC1 rs9934438, CYP2C9 rs1057910, and CYP4F2 rs2108622) gave a number needed to genotype of 34. This study showed that polymorphisms of EPHX1 and VKORC1L1 could be determinants of stable warfarin doses. Copyright © 2017. Published by Elsevier B.V.

  1. Chitinase activity of Pseudomonas stutzeri PT5 in different fermentation condition

    Science.gov (United States)

    Chalidah, N.; Khotimah, I. N.; Hakim, A. R.; Meata, B. A.; Puspita, I. D.; Nugraheni, P. S.; Ustadi; Pudjiraharti, S.

    2018-03-01

    This study aimed to determine the incubation condition of Pseudomonas stutzeri PT5 in producing chitin degrading enzyme in various pH and temperatures; to compare the production of chitin degrading enzyme in chitin medium supplemented with additional nitrogen, carbon and a mixture of nitrogen and carbon sources and to observe the production of chitin degrading enzyme in 250 mL-shake flasks and 2 L-fermentor. The parameters tested during production were chitinase activity (U·mL-1) of culture supernatant and N-acetylglucosamine concentration (μg·mL-1) in the medium. The results showed that Pseudomonas stutzeri PT5 was able to produce the highest chitinase activity at pH 6 and temperature of 37 °C (0.024 U·mL-1). The addition of 0.1 % of ammonium phosphate and 0.1 % of maltose, increased the chitinase activity of Pseudomonas stutzeri PT5 by 3.24 and 8.08 folds, respectively, compared to the control. The addition of 0.1 % ammonium phosphate and 0.1 % maltose mixture to chitin medium resulted in the shorter time of chitinase production compared to the addition of sole nutrition. The production of chitinase using 2 L-fermentor shows that the highest chitinase activity produced by Pseudomonas stutzeri PT5 was reached at 1-day incubation (0.0283 U·mL-1), which was shorter than in 250 mL-shake flasks.

  2. Expression of PD-L1 on canine tumor cells and enhancement of IFN-γ production from tumor-infiltrating cells by PD-L1 blockade.

    Directory of Open Access Journals (Sweden)

    Naoya Maekawa

    Full Text Available Programmed death 1 (PD-1, an immunoinhibitory receptor, and programmed death ligand 1 (PD-L1, its ligand, together induce the "exhausted" status in antigen-specific lymphocytes and are thus involved in the immune evasion of tumor cells. In this study, canine PD-1 and PD-L1 were molecularly characterized, and their potential as therapeutic targets for canine tumors was discussed. The canine PD-1 and PD-L1 genes were conserved among canine breeds. Based on the sequence information obtained, the recombinant canine PD-1 and PD-L1 proteins were constructed; they were confirmed to bind each other. Antibovine PD-L1 monoclonal antibody effectively blocked the binding of recombinant PD-1 with PD-L1-expressing cells in a dose-dependent manner. Canine melanoma, mastocytoma, renal cell carcinoma, and other types of tumors examined expressed PD-L1, whereas some did not. Interestingly, anti-PD-L1 antibody treatment enhanced IFN-γ production from tumor-infiltrating cells. These results showed that the canine PD-1/PD-L1 pathway is also associated with T-cell exhaustion in canine tumors and that its blockade with antibody could be a new therapeutic strategy for canine tumors. Further investigations are needed to confirm the ability of anti-PD-L1 antibody to reactivate canine antitumor immunity in vivo, and its therapeutic potential has to be further discussed.

  3. Mechanism for the decrease in the FIP1L1-PDGFRalpha protein level in EoL-1 cells by histone deacetylase inhibitors.

    Science.gov (United States)

    Ishihara, Kenji; Kaneko, Motoko; Kitamura, Hajime; Takahashi, Aki; Hong, Jang Ja; Seyama, Toshio; Iida, Koji; Wada, Hiroshi; Hirasawa, Noriyasu; Ohuchi, Kazuo

    2008-01-01

    Acetylation and deacetylation of proteins occur in cells in response to various stimuli, and are reversibly catalyzed by histone acetyltransferase and histone deacetylase (HDAC), respectively. EoL-1 cells have an FIP1L1-PDGFRA fusion gene that causes transformation of eosinophilic precursor cells into leukemia cells. The HDAC inhibitors apicidin and n-butyrate suppress the proliferation of EoL-1 cells and induce differentiation into eosinophils by a decrease in the protein level of FIP1L1-PDGFRalpha without affecting the mRNA level for FIP1L1-PDGFRA. In this study, we analyzed the mechanism by which the protein level of FIP1L1-PDGFRalpha is decreased by apicidin and n-butyrate. EoL-1 cells were incubated in the presence of the HDAC inhibitors apicidin, trichostatin A or n-butyrate. The protein levels of FIP1L1-PDGFRalpha and phosphorylated eIF-2alpha were determined by Western blotting. Actinomycin D and cycloheximide were used to block RNA synthesis and protein synthesis, respectively, in the chasing experiment of the amount of FIP1L1-PDGFRalpha protein. When apicidin- and n-butyrate-treated EoL-1 cells were incubated in the presence of actinomycin D, the decrease in the protein level of FIP1L1-PDGFRalpha was significantly enhanced when compared with controls. In contrast, the protein levels were not changed by cycloheximide among these groups. Apicidin and n-butyrate induced the continuous phosphorylation of eIF-2alpha for up to 8 days. The decrease in the level of FIP1L1-PDGFRalpha protein by continuous inhibition of HDAC may be due to the decrease in the translation rate of FIP1L1-PDGFRA. Copyright 2008 S. Karger AG, Basel.

  4. A facile route to synthesis of CoPt magnetic nanoparticles

    International Nuclear Information System (INIS)

    Liu, Yang; Yang, Yanting; Zhang, Yongjun; Wang, Yaxin; Zhang, Xiaolong; Jiang, Yuhong; Wei, Maobin; Liu, Yanqing; Liu, Xiaoyan; Yang, Jinghai

    2013-01-01

    Graphical abstract: CoPt NPs are successfully synthesized by sol–gel method. Different distinct particle sizes with narrow particle size distribution of CoPt nanoparticles are obtained. The maximum coercivity of 254,720.3 A/m is obtained for 800 °C heat-treated sample. Display Omitted Highlights: ► L1 0 -CoPt NPs with FCT structure are successfully synthesized by sol–gel method. ► The maximum value of 254,720.3 A/m is obtained for the samples heated at 800 °C. ► The synthetic route proposed in this study is less toxic and easy-to-handle. -- Abstract: The face-centered tetragonal (FCT) ordered L1 0 CoPt nanoparticles (NPs) are prepared by the sol–gel method. Their structure and magnetic properties are characterized by the X-ray diffraction (XRD), the transmission electron microscope (TEM) and the vibrating sample magnetometer (VSM). The results indicate that the CoPt NPs heated at 400 °C are the disordered face-centered cubic (FCC) structure, whereas the samples annealed at the temperature above 600 °C exhibit an ordered FCT structure. TEM images show the increase of the particle size as the annealing temperature increases. SAED images show the appearance of the L1 0 phase at 800 °C, and the maximum coercivity is 254,720.3 A/m.

  5. Characterization of azo dyes on Pt and Pt/polyaniline/dispersed Pt electrodes

    Energy Technology Data Exchange (ETDEWEB)

    Molina, J.; Fernandez, J.; Rio, A.I. del; Bonastre, J. [Departamento de Ingenieria Textil y Papelera, EPS de Alcoy, Universitat Politecnica de Valencia, Plaza Ferrandiz y Carbonell s/n, 03801 Alcoy (Spain); Cases, F., E-mail: fjcases@txp.upv.es [Departamento de Ingenieria Textil y Papelera, EPS de Alcoy, Universitat Politecnica de Valencia, Plaza Ferrandiz y Carbonell s/n, 03801 Alcoy (Spain)

    2012-06-15

    The electrochemical characterization of two organic dyes (amaranth and procion orange MX-2R) has been performed on Pt electrodes and Pt electrodes coated with polyaniline and dispersed Pt. Electrodes with different Pt loads have been synthesized and characterized obtaining that a load of 300 {mu}g cm{sup -2} was the optimum one. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) was employed to observe the distribution and morphology of the Pt nanoparticles. The electroactivity of the electrodes has also been characterized by means of scanning electrochemical microscopy (SECM). The chemical characterization of Pt dispersed Pani coated Pt electrodes (Pt-Pani-Pt) was performed by means of X-ray photoelectron spectroscopy (XPS). The electrochemical characterization of the dyes has been performed by means of cyclic voltammetry. Voltammograms have shown that the presence of the dyes diminishes characteristic Pt oxidation and reduction peaks. However, redox processes due to the dyes, appeared in the voltammograms. The different species responsible of these redox processes were generated in the vicinity of the electrode and were not adsorbed on the electrode surface since after stirring, the different redox processes disappeared. Characterization with different scan rates showed that redox processes of both dyes were controlled by diffusion.

  6. Soluble semiclassical model for a one-dimensional Δl=1, Δm=0, decay

    International Nuclear Information System (INIS)

    Costa, R.C.T. da; Crestana, S.

    1978-01-01

    The radiation emitted by a plane of excited two-level atoms, Δl=1, Δm=0 transition, is exactly calculated using a semiclassical model in which the electromagnetic field is treated classically (Maxwell's equations) and the coupling between matter and field is described in the electric dipole approximation. The influence of the plane density in the radiation rate is investigated in both limits of weak and strong coupling (defined in the text). It is shown that, in the second case, we can observe infinitely many solutions of the problem, depending on the initial value of the phase difference appearing in the definition of the excited state. Cases of phase choices leading to enhanced or attenuated emission rates are also discussed [pt

  7. Prediction of LOFT L1-4 experiment

    International Nuclear Information System (INIS)

    Soda, Kunihisa; Sasaki, Shinobu; Akimoto, Masayuki; Koizumi, Yasuo; Araya, Fumimasa

    1977-10-01

    LOFT L1-4 experimental results were predicted by LOFT Analysis Group and Code Development Group using RELAP-4J and ALARM-P1 respectively. The input data prepared by the former group were used in both the analyses. Thus any differences in the results should stem from the differences in code performance characteristics of the two codes. (1) The coolant behaviors predicted by RELAP-4J and ALARM-P1 are in good agreement although some differences do exist between these two calculation models. (2) Large difference is seen in coolant flow rate across the pump. The coast down and the flow rate by ALARM-P1 are larger and smaller respectively than by RELAP-4J. (3) An explicit method of the ALARM-P1 leads to unstable calculation at a T shaped junction when one of the two volumes connected by the junction is filled with subcooled water. (4) Coolant flow in the downcomer, heat transfer to and from the steam generator secondary and suppression tank behavior must be modified to better predict the experimental results. (5) Additional instrumentation in reflood assist and ECC injection lines are necessary to better nderstand the coolant behavior. (auth.)

  8. On Recursive Modification in Child L1 French

    Directory of Open Access Journals (Sweden)

    Yves Roberge

    2018-03-01

    Full Text Available This paper investigates nominal recursive modification (RM in the L1 acquisition of French. Although recursion is considered the fundamental property of human languages, recursive self-embedding is found to be difficult for children in a variety of languages and constructions. Despite these challenges, the acquisition of RM proves to be resilient; acquirable even under severely degraded input conditions. From a minimalist perspective on the operations of narrow syntax, recursive embedding is essentially the application of a sequence of Merge operations (Chomsky 1995; Trotzke and Zwart 2014; therefore, given the universality of Merge, we do not expect to find cross-linguistic differences in how difficult recursion is. But if the challenging nature of recursion stems from factors which might differ from language to language, we expect different outcomes cross-linguistically. We compare new data from French to existing English data (Pérez-Leroux et al. 2012 in order to examine to what extent language-specific properties of RM structures determine the acquisition path. While children’s production differs significantly from their adult’s counterparts, we find no differences between French-speaking and English-speaking children. Our findings suggest that the challenging nature of recursion does not stem from the grammar itself and that what shapes the acquisition path is the interaction between universal properties of language and considerations not specific to language, namely computational efficiency.

  9. Status of the ESA L1 mission candidate ATHENA

    Science.gov (United States)

    Rando, N.; Martin, D.; Lumb, D.; Verhoeve, P.; Oosterbroek, T.; Bavdaz, M.; Fransen, S.; Linder, M.; Peyrou-Lauga, R.; Voirin, T.; Braghin, M.; Mangunsong, S.; van Pelt, M.; Wille, E.

    2012-09-01

    ATHENA (Advanced Telescope for High Energy Astrophysics) was an L class mission candidate within the science programme Cosmic Vision 2015-2025 of the European Space Agency, with a planned launch by 2022. ATHENA was conceived as an ESA-led project, open to the possibility of focused contributions from JAXA and NASA. By allowing astrophysical observations between 100 eV and 10 keV, it would represent the new generation X-ray observatory, following the XMM-Newton, Astro-H and Chandra heritage. The main scientific objectives of ATHENA include the study of large scale structures, the evolution of black holes, strong gravity effects, neutron star structure as well as investigations into dark matter. The ATHENA mission concept would be based on focal length of 12m achieved via a rigid metering tube and a twoaperture, x-ray telescope. Two identical x-ray mirrors would illuminate fixed focal plane instruments: a cryogenic imaging spectrometer (XMS) and a wide field imager (WFI). The S/C is designed to be fully compatible with Ariane 5 ECA. The observatory would operate at SE-L2, with a nominal lifetime of 5 yr. This paper provides a summary of the reformulation activities, completed in December 2011. An overview of the spacecraft design and of the payload is provided, including both telescope and instruments. Following the ESA Science Programme Committee decision on the L1 mission in May 2012, ATHENA was not selected to enter Definition Phase.

  10. Reference payload of the ESA L1 mission candidate ATHENA

    Science.gov (United States)

    Martin, Didier; Rando, Nicola; Lumb, David; Verhoeve, Peter; Oosterbroek, Tim; Bavdaz, Marcos

    2012-09-01

    The Advanced Telescope for High ENergy Astrophysics (ATHENA) is one of the three candidates that competed for the first large-class mission (L1) in ESA’s Cosmic Vision 2015-2025 programme, with a launch planned by 2022 and is the result of the IXO reformulation activities. ATHENA is an ESA-led project and is conceived as the next generation X-ray observatory. It is meant to address fundamental questions about accretion around black-holes, reveal the physics underpinning cosmic feedback, trace the large scale structure of baryons in galaxy clusters and the cosmic as well as a large number of astrophysics and fundamental physics phenomena. The observatory consists of two identical mirrors each illuminating a fixed focal plane instrument, providing collectively 1 m2 effective area at 1 keV. The reference payload consists of a medium resolution wide field imager (WFI) and a high resolution X-ray micro-calorimeter spectrometer (XMS). The WFI is based on a monolithic Si DepFET array providing imaging over a 24 × 24 arcmin2 field of view and a good PSF oversampling. The sensor will measure X-rays in the range 0.1-15 keV and provides near Fano limited energy resolution (150eV at 6keV). The XMS is based on a micro-calorimeter array operating at its transition temperature of ~100mK and provides Definition Phase.

  11. Low Pt content Pt-Ru-Ir-Sn quaternary catalysts for anodic methanol oxidation in DMFC

    Energy Technology Data Exchange (ETDEWEB)

    Neburchilov, Vladimir; Wang, Haijiang; Zhang, Jiujun [Institute for Fuel Cell Innovation, National Research Council (Canada)

    2007-07-15

    In this communication we report our research work on low Pt content Pt-Ru-Ir-Sn quaternary catalysts for use in DMFC anodes. The carbon-supported quaternary metal alloy catalyst was synthesized according to the solution reduction method and was deposited onto a carbon fiber paper or a carbon aerogel nanofoam to form the anode for direct methanol fuel cells. The Pt loading of the electrode is 0.1 mg/cm{sup 2}. The testing results from a three-electrode electrochemical cell show that the simultaneous use of higher Ir (25-35 wt.%) and Sn (10 wt.%) content gives satisfactory stability and higher activity for methanol oxidation than the commercially available E-TEK anode (80%[0.5Pt 0.5Ru]/C on carbon cloth). Energy dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), scanning electron microscope (SEM), and Bruner-Emmett-Teller method (BET) measurements were carried out to characterize the composition, structure, morphology, and surface area of the developed catalysts. (author)

  12. Malignant mesothelioma effusions are infiltrated by CD3+ T cells highly expressing PD-L1 and the PD-L1+ tumor cells within these effusions are susceptible to ADCC by the anti-PD-L1 antibody avelumab

    Science.gov (United States)

    Khanna, Swati; Thomas, Anish; Abate-Daga, Daniel; Zhang, Jingli; Morrow, Betsy; Steinberg, Seth M.; Orlandi, Augusto; Ferroni, Patrizia; Schlom, Jeffrey; Guadagni, Fiorella; Hassan, Raffit

    2016-01-01

    INTRODUCTION The functional aspects of programmed death 1 (PD-1) and PD ligand 1 (PD-L1) immune checkpoints in malignant mesothelioma have not been studied. METHODS Tumor samples from 65 patients with mesothelioma were evaluated for PD-L1 expression by immunohistochemistry and its prognostic significance. Malignant effusions from patients with pleural and peritoneal mesothelioma were evaluated for PD-1+ and PD-L1+ infiltrating lymphocytes and their role in inducing tumor cell PD-L1 expression. Antibody dependent cellular cytotoxicity (ADCC) of avelumab, a fully humanized IgG1 anti PD-L1 antibody towards primary mesothelioma cell lines was evaluated in presence of autologous and allogeneic NK cells. RESULTS Of 65 pleural and peritoneal mesothelioma tumors examined, 41 (63%) were PD-L1 positive, which was associated with slightly inferior overall survival compared to patients with PD-L1 negative tumors (median 23.0 vs. 33.3 months; p=0.35). The frequency of PD-L1 expression was similar in pleural and peritoneal mesothelioma patients with 62% and 64% of samples positive, respectively. Of nine mesothelioma effusion samples evaluated, the fraction of cells expressing PD-L1 ranged from 12 to 83%. Of 7 patients with paired malignant effusion and peripheral blood mononuclear cells (PBMC) samples, PD-L1 expression was significantly higher on CD3+ T cells present in malignant effusions as compared with PBMC (p=0.016). In addition, CD14+PD-1+ cells were elevated in malignant effusions compared with PBMC (p=0.031). The lymphocytes present in malignant effusions recognized autologous tumor cells and induced IFN-γ-mediated PD-L1 expression on the tumor cell surface. Of the three primary mesothelioma cell lines tested, two were susceptible to avelumab mediated ADCC in presence of autologous NK cells. CONCLUSION The majority of pleural as well as peritoneal mesothelioma express PD-L1. Malignant effusions in this disease are characterized by presence of tumor cells and CD3+ T

  13. Atomically thin Pt shells on Au nanoparticle cores: facile synthesis and efficient synergetic catalysis

    DEFF Research Database (Denmark)

    Engelbrekt, Christian; Seselj, Nedjeljko; Poreddy, Raju

    2016-01-01

    in electrooxidation of sustainable fuels (i.e. formic acid, methanol and ethanol), and selective hydrogenation of benzene derivatives. Especially high activity was achieved for formic acid oxidation, 549 mA (mgPt)−1 (at 0.6 V vs. SCE), which is 3.5 fold higher than a commercial ... properties were thoroughly characterized by ultraviolet-visible light spectrophotometry, transmission electron microscopy, nanoparticle tracking analysis and electrochemistry. The 8 ± 2 nm Au@PtNPs contained 24 ± 1 mol% Pt and 76 ± 1 mol% Au corresponding to an atomically thin Pt shell. Electrochemical data...

  14. Adaptive L1/2 Shooting Regularization Method for Survival Analysis Using Gene Expression Data

    Directory of Open Access Journals (Sweden)

    Xiao-Ying Liu

    2013-01-01

    Full Text Available A new adaptive L1/2 shooting regularization method for variable selection based on the Cox’s proportional hazards mode being proposed. This adaptive L1/2 shooting algorithm can be easily obtained by the optimization of a reweighed iterative series of L1 penalties and a shooting strategy of L1/2 penalty. Simulation results based on high dimensional artificial data show that the adaptive L1/2 shooting regularization method can be more accurate for variable selection than Lasso and adaptive Lasso methods. The results from real gene expression dataset (DLBCL also indicate that the L1/2 regularization method performs competitively.

  15. Thermal stability, thermal expansion and grain-growth in exchange-coupled Fe-Pt-Ag-B bulk nanocomposite magnets

    International Nuclear Information System (INIS)

    Nicula, R.; Crisan, O.; Crisan, A.D.; Mercioniu, I.; Stir, M.; Vasiliu, F.

    2015-01-01

    Highlights: • Formation of the L10 FePt hard-magnetic phase (>90%) directly in the as-cast state. • Specific alternating hard/soft nanostructure is stable to 600 °C without grain growth. • Anisotropic and non-linear thermal expansion effects. • The FePtAgB alloy behaves like a single magnetic phase (full exchange coupling). - Abstract: Rare-earth free (RE-free) exchange coupling nanocomposite magnets are intensively studied nowadays due to their potential use in applications demanding stable high-temperature operation and corrosion resistance. In this respect, the FePt alloy system is one of the most actively addressed potential permanent magnet solutions. In FePt alloys, promising magnetic features arise from the co-existence of hard magnetic L1 0 FePt and soft magnetic L1 2 Fe 3 Pt phases emerged from the same metastable precursor. The present work deals with an in-situ temperature-resolved synchrotron radiation study of the thermal stability, thermal expansion and microstructure evolution in exchange-coupled FePtAgB alloys. The as-cast microstructural state as well as the optimized magnetic behavior are given as reference and correlated to the observed microstructural evolution with temperature. The melt-spun Fe 48 Pt 28 Ag 6 B 18 alloy ribbons were examined in situ by synchrotron X-ray powder diffraction from ambient temperature up to 600 °C. The FePt-Fe 3 Pt exchange-coupled microstructure achieved by rapid solidification is not significantly altered during the high temperature exposure. The thermal expansion of the FePt L1 0 unit cell has been found to be strongly anisotropic, being essentially an in-plane expansion which may be seen as an anisotropic invar effect. For the FePt L1 0 phase, a significant deviation from linear thermal expansion is observed at the Curie temperature T C = 477 °C. This non-linear behavior above T C is tentatively linked to a diffusion/segregation mechanism of Ag. The promising hard magnetic properties as well as the

  16. Coulomb excitation of the 4+1 states of 194Pt, 196Pt and 198Pt

    International Nuclear Information System (INIS)

    Fewell, M.P.; Gyapong, G.J.; Spear, R.H.

    1987-09-01

    Probabilities for the Coulomb excitation of the 4 1 + states of 194 Pt, 196 Pt, 198 Pt by the backscattering of 4 He, 12 C and 16 O ions are reported. Model-independent values of the matrix elements 1 + ; M(E4), 4 1 + > and 1 + , M(E2), 4 1 + > are extracted. Agreement with previous measurements of these matrix elements is good. Values of β 2 and β 4 are determined for 194 Pt and compared with calculations of these quantities

  17. Ga-Doped Pt-Ni Octahedral Nanoparticles as a Highly Active and Durable Electrocatalyst for Oxygen Reduction Reaction.

    Science.gov (United States)

    Lim, JeongHoon; Shin, Hyeyoung; Kim, MinJoong; Lee, Hoin; Lee, Kug-Seung; Kwon, YongKeun; Song, DongHoon; Oh, SeKwon; Kim, Hyungjun; Cho, EunAe

    2018-04-11

    Bimetallic PtNi nanoparticles have been considered as a promising electrocatalyst for oxygen reduction reaction (ORR) in polymer electrolyte membrane fuel cells (PEMFCs) owing to their high catalytic activity. However, under typical fuel cell operating conditions, Ni atoms easily dissolve into the electrolyte, resulting in degradation of the catalyst and the membrane-electrode assembly (MEA). Here, we report gallium-doped PtNi octahedral nanoparticles on a carbon support (Ga-PtNi/C). The Ga-PtNi/C shows high ORR activity, marking an 11.7-fold improvement in the mass activity (1.24 A mg Pt -1 ) and a 17.3-fold improvement in the specific activity (2.53 mA cm -2 ) compared to the commercial Pt/C (0.106 A mg Pt -1 and 0.146 mA cm -2 ). Density functional theory calculations demonstrate that addition of Ga to octahedral PtNi can cause an increase in the oxygen intermediate binding energy, leading to the enhanced catalytic activity toward ORR. In a voltage-cycling test, the Ga-PtNi/C exhibits superior stability to PtNi/C and the commercial Pt/C, maintaining the initial Ni concentration and octahedral shape of the nanoparticles. Single cell using the Ga-PtNi/C exhibits higher initial performance and durability than those using the PtNi/C and the commercial Pt/C. The majority of the Ga-PtNi nanoparticles well maintain the octahedral shape without agglomeration after the single cell durability test (30,000 cycles). This work demonstrates that the octahedral Ga-PtNi/C can be utilized as a highly active and durable ORR catalyst in practical fuel cell applications.

  18. Reviving the dead: history and reactivation of an extinct l1.

    Science.gov (United States)

    Yang, Lei; Brunsfeld, John; Scott, LuAnn; Wichman, Holly

    2014-06-01

    Although L1 sequences are present in the genomes of all placental mammals and marsupials examined to date, their activity was lost in the megabat family, Pteropodidae, ∼24 million years ago. To examine the characteristics of L1s prior to their extinction, we analyzed the evolutionary history of L1s in the genome of a megabat, Pteropus vampyrus, and found a pattern of periodic L1 expansion and quiescence. In contrast to the well-characterized L1s in human and mouse, megabat genomes have accommodated two or more simultaneously active L1 families throughout their evolutionary history, and major peaks of L1 deposition into the genome always involved multiple families. We compared the consensus sequences of the two major megabat L1 families at the time of their extinction to consensus L1s of a variety of mammalian species. Megabat L1s are comparable to the other mammalian L1s in terms of adenosine content and conserved amino acids in the open reading frames (ORFs). However, the intergenic region (IGR) of the reconstructed element from the more active family is dramatically longer than the IGR of well-characterized human and mouse L1s. We synthesized the reconstructed element from this L1 family and tested the ability of its components to support retrotransposition in a tissue culture assay. Both ORFs are capable of supporting retrotransposition, while the IGR is inhibitory to retrotransposition, especially when combined with either of the reconstructed ORFs. We dissected the inhibitory effect of the IGR by testing truncated and shuffled versions and found that length is a key factor, but not the only one affecting inhibition of retrotransposition. Although the IGR is inhibitory to retrotransposition, this inhibition does not account for the extinction of L1s in megabats. Overall, the evolution of the L1 sequence or the quiescence of L1 is unlikely the reason of L1 extinction.

  19. Reviving the dead: history and reactivation of an extinct l1.

    Directory of Open Access Journals (Sweden)

    Lei Yang

    2014-06-01

    Full Text Available Although L1 sequences are present in the genomes of all placental mammals and marsupials examined to date, their activity was lost in the megabat family, Pteropodidae, ∼24 million years ago. To examine the characteristics of L1s prior to their extinction, we analyzed the evolutionary history of L1s in the genome of a megabat, Pteropus vampyrus, and found a pattern of periodic L1 expansion and quiescence. In contrast to the well-characterized L1s in human and mouse, megabat genomes have accommodated two or more simultaneously active L1 families throughout their evolutionary history, and major peaks of L1 deposition into the genome always involved multiple families. We compared the consensus sequences of the two major megabat L1 families at the time of their extinction to consensus L1s of a variety of mammalian species. Megabat L1s are comparable to the other mammalian L1s in terms of adenosine content and conserved amino acids in the open reading frames (ORFs. However, the intergenic region (IGR of the reconstructed element from the more active family is dramatically longer than the IGR of well-characterized human and mouse L1s. We synthesized the reconstructed element from this L1 family and tested the ability of its components to support retrotransposition in a tissue culture assay. Both ORFs are capable of supporting retrotransposition, while the IGR is inhibitory to retrotransposition, especially when combined with either of the reconstructed ORFs. We dissected the inhibitory effect of the IGR by testing truncated and shuffled versions and found that length is a key factor, but not the only one affecting inhibition of retrotransposition. Although the IGR is inhibitory to retrotransposition, this inhibition does not account for the extinction of L1s in megabats. Overall, the evolution of the L1 sequence or the quiescence of L1 is unlikely the reason of L1 extinction.

  20. Antagonistic Activities of Novel Peptides from Bacillus amyloliquefaciens PT14 against Fusarium solani and Fusarium oxysporum.

    Science.gov (United States)

    Kim, Young Gwon; Kang, Hee Kyoung; Kwon, Kee-Deok; Seo, Chang Ho; Lee, Hyang Burm; Park, Yoonkyung

    2015-12-09

    Bacillus species have recently drawn attention due to their potential use in the biological control of fungal diseases. This paper reports on the antifungal activity of novel peptides isolated from Bacillus amyloliquefaciens PT14. Reverse-phase high-performance liquid chromatography revealed that B. amyloliquefaciens PT14 produces five peptides (PT14-1, -2, -3, -4a, and -4b) that exhibit antifungal activity but are inactive against bacterial strains. In particular, PT14-3 and PT14-4a showed broad-spectrum antifungal activity against Fusarium solani and Fusarium oxysporum. The PT14-4a N-terminal amino acid sequence was identified through Edman degradation, and a BLAST homology analysis showed it not to be identical to any other protein or peptide. PT14-4a displayed strong fungicidal activity with minimal inhibitory concentrations of 3.12 mg/L (F. solani) and 6.25 mg/L (F. oxysporum), inducing severe morphological deformation in the conidia and hyphae. On the other hand, PT14-4a had no detectable hemolytic activity. This suggests PT14-4a has the potential to serve as an antifungal agent in clinical therapeutic and crop-protection applications.

  1. Antibody fragments directed against different portions of the human neural cell adhesion molecule L1 act as inhibitors or activators of L1 function.

    Directory of Open Access Journals (Sweden)

    Yan Wang

    Full Text Available The neural cell adhesion molecule L1 plays important roles in neuronal migration and survival, neuritogenesis and synaptogenesis. L1 has also been found in tumors of different origins, with levels of L1 expression correlating positively with the metastatic potential of tumors. To select antibodies targeting the varied functions of L1, we screened the Tomlinson library of recombinant human antibody fragments to identify antibodies binding to recombinant human L1 protein comprising the entire extracellular domain of human L1. We obtained four L1 binding single-chain variable fragment antibodies (scFvs, named I4, I6, I13, and I27 and showed by enzyme-linked immunosorbent assay (ELISA that scFvs I4 and I6 have high affinity to the immunoglobulin-like (Ig domains 1-4 of L1, while scFvs I13 and I27 bind strongly to the fibronectin type III homologous (Fn domains 1-3 of L1. Application of scFvs I4 and I6 to human SK-N-SH neuroblastoma cells reduced proliferation and transmigration of these cells. Treatment of SK-N-SH cells with scFvs I13 and I27 enhanced cell proliferation and migration, neurite outgrowth, and protected against the toxic effects of H(2O(2 by increasing the ratio of Bcl-2/Bax. In addition, scFvs I4 and I6 inhibited and scFvs I13 and I27 promoted phosphorylation of src and Erk. Our findings indicate that scFvs reacting with the immunoglobulin-like domains 1-4 inhibit L1 functions, whereas scFvs interacting with the fibronectin type III domains 1-3 trigger L1 functions of cultured neuroblastoma cells.

  2. Highly open bowl-like PtAuAg nanocages as robust electrocatalysts towards ethylene glycol oxidation

    Science.gov (United States)

    Xu, Hui; Yan, Bo; Li, Shumin; Wang, Jin; Song, Pingping; Wang, Caiqin; Guo, Jun; Du, Yukou

    2018-04-01

    A novel combined seed mediated and galvanic replacement method has been demonstrated to synthesize a new class of trimetallic PtAuAg nanocatalysts with highly open bowl-like nanocage structure. The newly-generated PtAuAg nanocages catalysts exhibit superior electrocatalytic performances towards ethylene glycol oxidation with the mass activity of 6357.1 mA mg-1, 5.5 times higher than that of commercial Pt/C (1151.1 mA mg-1). This work demonstrates the first example of designing shape-controlled architectures of trimetallic bowl-like PtAuAg nanocages for liquid fuel electrooxidation.

  3. PD-L1 expression by neurons nearby tumors indicates better prognosis in glioblastoma patients

    DEFF Research Database (Denmark)

    Liu, Yawei; Carlsson, Robert; Ambjørn, Malene

    2013-01-01

    Glioblastoma multiforme (GBM) is the most aggressive form of brain tumor. In general, tumor growth requires disruption of the tissue microenvironment, yet how this affects glioma progression is unknown. We studied program death-ligand (PD-L)1 in neurons and gliomas in tumors from GBM patients...... and associated the findings with clinical outcome. Remarkably, we found that upregulation of PD-L1 by neurons in tumor-adjacent brain tissue (TABT) associated positively with GBM patient survival, whereas lack of neuronal PD-L1 expression was associated with high PD-L1 in tumors and unfavorable prognosis...... in GBM patients, better survival in wild-type mice was associated with high neuronal PD-L1 in TABT and downregulation of PD-L1 in tumors, which was defective in Ifnb-/- mice. Our data indicated that neuronal PD-L1 signaling in brain cells was important for GBM patient survival. Reciprocal PD-L1...

  4. A novel PKD2L1 C-terminal domain critical for trimerization and channel function.

    Science.gov (United States)

    Zheng, Wang; Hussein, Shaimaa; Yang, JungWoo; Huang, Jun; Zhang, Fan; Hernandez-Anzaldo, Samuel; Fernandez-Patron, Carlos; Cao, Ying; Zeng, Hongbo; Tang, Jingfeng; Chen, Xing-Zhen

    2015-03-30

    As a transient receptor potential (TRP) superfamily member, polycystic kidney disease 2-like-1 (PKD2L1) is also called TRPP3 and has similar membrane topology as voltage-gated cation channels. PKD2L1 is involved in hedgehog signaling, intestinal development, and sour tasting. PKD2L1 and PKD1L3 form heterotetramers with 3:1 stoichiometry. C-terminal coiled-coil-2 (CC2) domain (G699-W743) of PKD2L1 was reported to be important for its trimerization but independent studies showed that CC2 does not affect PKD2L1 channel function. It thus remains unclear how PKD2L1 proteins oligomerize into a functional channel. By SDS-PAGE, blue native PAGE and mutagenesis we here identified a novel C-terminal domain called C1 (K575-T622) involved in stronger homotrimerization than the non-overlapping CC2, and found that the PKD2L1 N-terminus is critical for dimerization. By electrophysiology and Xenopus oocyte expression, we found that C1, but not CC2, is critical for PKD2L1 channel function. Our co-immunoprecipitation and dynamic light scattering experiments further supported involvement of C1 in trimerization. Further, C1 acted as a blocking peptide that inhibits PKD2L1 trimerization as well as PKD2L1 and PKD2L1/PKD1L3 channel function. Thus, our study identified C1 as the first PKD2L1 domain essential for both PKD2L1 trimerization and channel function, and suggest that PKD2L1 and PKD2L1/PKD1L3 channels share the PKD2L1 trimerization process.

  5. L1 Korean and L1 Mandarin L2 English Learners' Acquisition of the Count/Mass Distinction in English

    Science.gov (United States)

    Choi, Sea Hee; Ionin, Tania; Zhu, Yeqiu

    2018-01-01

    This study investigates the second language (L2) acquisition of the English count/mass distinction by speakers of Korean and Mandarin Chinese, with a focus on the semantics of atomicity. It is hypothesized that L1-Korean and L1-Mandarin L2-English learners are influenced by atomicity in the use of the count/mass morphosyntax in English. This…

  6. Do L2 Writing Courses Affect the Improvement of L1 Writing Skills via Skills Transfer from L2 to L1?

    Science.gov (United States)

    Gonca, Altmisdort

    2016-01-01

    This study investigates the relationship of second language (L2) writing skills proficiency with the first language (L1) writing skills, in light of the language transfer. The study aims to analyze the positive effects of L2 writing proficiency on L1 writing proficiency. Forty native Turkish-speaking university students participated in the study.…

  7. Effect of Hf underlayer on structure and magnetic properties of rapid thermal annealed FePt thin films

    International Nuclear Information System (INIS)

    Shen, C.Y.; Yuan, F.T.; Chang, H.W.; Lin, M.C.; Su, C.C.; Chang, S.T.; Wang, C.R.; Mei, J.K.; Hsiao, S.N.; Chen, C.C.; Shih, C.W.; Chang, W.C.

    2014-01-01

    FePt(20 nm) and FePt(20 nm)/Hf(10 nm) thin films prepared on the glass substrates by sputtering and post annealing are studied. For both samples, the as deposited films are disordered and L1 0 -ordering is triggered by a 400 °C-annealing. At T a ≥600 °C, Hf–Pt intermetallic compound forms with increasing T a , which consumes Pt in FePt layer and results in the formation of Fe 3 Pt phase. The film becomes soft magnetic at T a =800 °C. The optimized condition of FePt/Hf film is in the T a range of 500 to 600 °C where the interdiffusion between Hf and FePt layer is not extensive. The value of H c is 8.9 kOe and M r is 650–670 emu/cm 3 . Unlike FePt films, the Hf-undelayered samples show significantly reduced out-of-plane remanent and coercivity. The values for both are around 50% smaller than that of the FePt films. Additionally, Hf underlayer markedly reduces the FePt grain size and narrows the distribution, which enhances magnetic intergrain coupling. Good in-plane magnetic properties are preferred for the uses like a hard biasing magnet in a spintronic device. - Highlights: • Effect of Hf underlayer on structure and magnetic properties of FePt films are studied. • Hf underlayer reduces size, narrows the distribution of grains and thus enhances intergrain coupling. • Higher T a ≥600 °C makes Hf–Pt intermetallic compound and thus Fe 3 Pt phase form. • Good in-plane magnetic property is proper for uses in hard biasing magnet in spintronic devices

  8. Metacognitive Online Reading Strategy Use: Readers' Perceptions in L1 and L2

    Science.gov (United States)

    Taki, Saeed

    2016-01-01

    This study aimed to explore whether first-language (L1) readers of different language backgrounds would employ similar metacognitive online reading strategies and whether reading online in a second language (L2) could be influenced by L1 reading strategies. To this end, 52 Canadian college students as English L1 readers and 38 Iranian university…

  9. PD-L1 expression in non-small cell lung cancer : Correlations with genetic alterations

    NARCIS (Netherlands)

    Scheel, Andreas H.; Ansen, Sascha; Schultheis, Anne M.; Scheffler, Matthias; Fischer, Rieke N.; Michels, Sebastian; Hellmich, Martin; George, Julie; Zander, Thomas; Brockmann, Michael; Stoelben, Erich; Groen, Harry; Timens, Wim; Perner, Sven; von Bergwelt-Baildon, Michael; Buettner, Reinhard; Wolf, Juergen

    2016-01-01

    Inhibition of the PD-1/PD-L1 pathway may induce anticancer immune responses in non-small cell lung cancer (NSCLC). Two PD-L1 immunohistochemistry (IHC) assays have been approved as companion diagnostic tests for therapeutic anti-PD-1 antibodies. However, many aspects of PD-L1 prevalence and

  10. Mechanism for the differentiation of EoL-1 cells into eosinophils by histone deacetylase inhibitors.

    Science.gov (United States)

    Kaneko, Motoko; Ishihara, Kenji; Takahashi, Aki; Hong, Jangja; Hirasawa, Noriyasu; Zee, Okpyo; Ohuchi, Kazuo

    2007-01-01

    EoL-1 cells have a FIP1L1-PDGFRA fusion gene which causes the transformation of eosinophilic precursor cells into leukemia cells. Recently, we suggested that the induction of differentiation of EoL-1 cells into eosinophils by the HDAC inhibitors apicidin and n-butyrate is due to the continuous inhibition of HDACs. However, neither apicidin nor n-butyrate inhibited the expression of FIP1L1-PDGFRA mRNA, although both these inhibitors suppressed cell proliferation. Therefore, in this study, we analyzed whether the levels of FIP1L1-PDGFRalpha protein and phosphorylated-Stat5 involved in the signaling for the proliferation of EoL-1 cells are attenuated by HDAC inhibitors. EoL-1 cells were incubated in the presence of apicidin, TSA or n-butyrate. FIP1L1-PDGFRalpha and phosphorylated-Stat5 were detected by Western blotting. Treatment of EoL-1 cells with apicidin at 100 nM or n-butyrate at 500 microM decreased the levels of FIP1L1-PDGFRalpha protein and phosphorylated-Stat5, while that with trichostatin A at 30 nM did not. The decrease in the level of FIP1L1-PDGFRalpha protein caused by apicidin and n-butyrate might be one of the mechanisms by which EoL-1 cells are induced to differentiate into eosinophils by these HDAC inhibitors.

  11. The Influence of Schema and Cultural Difference on L1 and L2 Reading

    Science.gov (United States)

    Yang, Shi-sheng

    2010-01-01

    Reading in L1 shares numerous basic elements with reading in L2, and the processes also differ greatly. Intriguing questions involve whether there are two parallel cognitive processes at work, or whether there are processing strategies that accommodate both L1 and L2. This paper examines how reading in L1 is different from and similar to reading…

  12. Sintering prevention and phase transformation of FePt nanoparticles

    International Nuclear Information System (INIS)

    Ding, Y.; Majetich, S.A.; Kim, J.; Barmak, K.; Rollins, H.; Sides, P.

    2004-01-01

    Two approaches attempted to overcome FePt nanoparticle sintering during the transformation to the high coercivity L1 0 phase, which currently limits the use of these nanoparticles in data storage media. High-pressure treatment of dilute nanoparticle solutions failed to prevent sintering due to surfactant decomposition above 360 deg. C. By pre-annealing nanoparticle monolayers to decompose the surfactant, and then coating with an immiscible SiO 2 matrix, sintering was prevented with annealing temperatures up to 700 deg. C

  13. Structural Investigation of Rapidly Quenched FeCoPtB Alloys

    International Nuclear Information System (INIS)

    Grabias, A.; Kopcewicz, M.; Latuch, J.; Oleszak, D.

    2011-01-01

    Two sets of Fe 52-x Co x Pt 28 B 20 (x = 0-26 at.%) and Fe 60-x Co x Pt 25 B 15 (x = 0-40 at.%) alloys were prepared in the form of ribbons by the rapid quenching technique. Structure of the samples was characterized by Moessbauer spectroscopy and X-ray diffraction. In the as-quenched alloys the amorphous phase coexisted with the fcc-(Fe,Co)Pt disordered solid solution. Differential scanning calorimetry measurements performed in the range 50-720 ± C revealed one or two exothermal peaks. The magnetically hard ordered L1 0 (Fe,Co)Pt and magnetically soft (Fe,Co) 2 B nanocrystalline phases were formed due to thermal treatment of the alloys. The influence of Co content on the structure of the as-quenched and heated alloys was studied. (authors)

  14. Preparation and characterization of Pt Sn / C-rare earth and PtRu / C-rare earth using an alcohol reduction process for ethanol electron-oxidation

    International Nuclear Information System (INIS)

    Rodrigues, Rita Maria de Sousa

    2011-01-01

    The electro catalyst PtRu / C-rare earth and PtSn/C-rare earth (20 wt%) were prepared by alcohol reduction method using H 2 PtCl 6 .6H 2 O Ru Cl xH 2 O, SnCl 2 .2H 2 O as a source of metals 85 % Vulcan - 15 % rare earth as a support and, finally, ethylene glycol as reducing agent. The electrocatalysts were characterized physically by X-ray diffraction (XRD), energy dispersive X-ray (EDX), and transmission electron microscopy (TEM). Analyses by EDX showed that the atomic ratios of different electrocatalysts, prepared by alcohol reduction method are similar to the nominal starting compositions indicating that this methodology is promising for the preparation of electrocatalysts. In all the XRD patterns for the prepared electrocatalysts there is a broad peak at about 2θ = 25 o , which is associated with the carbon support and four additional diffraction peaks at approximately 2θ = 40 o , 47 o , 67 o e 82 o , which in turn are associated with the plans (111), (200), (220) e (311), respectively, of face-centered cubic structure (FCC) platinum. The results of X-ray diffraction also showed average crystallite sizes between 2.0 and 4.0 nm for PtSn e 2,0 a 3,0 para PtRu. The studies for the electrochemical oxidation of ethanol in acid medium were carried out using the technique of chronoamperometry in a solution 0,5 mol.L-1 H 2 SO 4 , + 1,0 mol.L-1 de C 2 H 5 OH. The polarization curves obtained in the fuel cell unit, powered directly by ethanol, are in agreement with the results of voltammetry and chronoamperometry noting the beneficial effect of rare earths in the preparation of electrocatalysts and attesting that the electrocatalysts PtSn/C are more effective than PtRu/C for the oxidation of ethanol.

  15. Anomalous Hall effect assisted by interfacial chemical reaction in perpendicular Co/Pt multilayers

    Science.gov (United States)

    Liu, Qian; Jiang, Shaolong; Teng, Jiao

    2018-05-01

    To uncover the underlying mechanism of Mg effect on the improved anomalous Hall effect (AHE) of perpendicular [Pt/Co]3/Mg/HfO2 multilayers, the X-ray photoelectron spectroscopy analysis has been carried out. It is found that Mg interlayer at the Co/HfO2 interface could prevent the Co oxidation to some extent via interfacial chemical reaction. As a result, A large anomalous Hall resistivity (ρAH) is obtained in perpendicular [Pt/Co]3/Mg/HfO2 multilayers, with a maximum ρAH of 3.02 μΩ cm, which is 59% larger than that in Co/Pt multilayers without Mg insertion. This effective modification of the AHE based on interfacial chemical reaction provides a promising pathway for spintronic applications.

  16. Reviving the Dead: History and Reactivation of an Extinct L1

    OpenAIRE

    Yang, Lei; Brunsfeld, John; Scott, LuAnn; Wichman, Holly

    2014-01-01

    Although L1 sequences are present in the genomes of all placental mammals and marsupials examined to date, their activity was lost in the megabat family, Pteropodidae, ∼24 million years ago. To examine the characteristics of L1s prior to their extinction, we analyzed the evolutionary history of L1s in the genome of a megabat, Pteropus vampyrus, and found a pattern of periodic L1 expansion and quiescence. In contrast to the well-characterized L1s in human and mouse, megabat genomes have accomm...

  17. Asymptotic properties of solvable PT-symmetric potentials

    International Nuclear Information System (INIS)

    Levai, G.

    2010-01-01

    states. The examples included the Scarf II potential V(x) = - V 1 /cosh 2 x + iV 2 sinhx/cosh 2 x; (1) the Rosen-Morse II potential V(x) -V 1 /cosh 2 (x) + iV 3 tanh(x) (2) and the Coulomb potential V(x) = iZ/t + l(l + 1)/t 2 . (3) Potentials (1) and (2) are both defined on the real x axis, and their real components have the same form, while potential (3) is defined on a U-shaped trajectory running on both sides of the imaginary x axis encircling the origin. Despite these circumstances, we found that the bound-state properties of potential (1) show more similarity with those of (3) than with those of (2). The former two systems possess strictly negative-energy bound states that are characterized by the q = ±1 quantum number. Reaching a critical value of V 2 - V 1 and l the spontaneous breakdown of PT symmetry occurs and the bound states with opposite q merge pairwise and their energy eigenvalues turn complex for arbitrary value of the n principal quantum number. In contrast, the energy eigenvalues of potential (2) stay real for arbitrary value of V 1 and V 3 and do not carry the q quantum number. The spontaneous breakdown of PT symmetry does not occur in this case, rather with increasing non-hermeticity the energy eigenvalues are gradually shifted to the positive domain. The properties of potential (2) are reminiscent of the purely imaginary ix 3 potential, the classic example of PT-symmetric quantum mechanics. The marked differences described above, which, however, do not show up in the scattering solutions, might be due to the asymptotically dominant and non-vanishing imaginary component in (2).

  18. Uniform Au@Pt core-shell nanodendrites supported on molybdenum disulfide nanosheets for the methanol oxidation reaction

    Science.gov (United States)

    Su, Shao; Zhang, Chi; Yuwen, Lihui; Liu, Xingfen; Wang, Lihua; Fan, Chunhai; Wang, Lianhui

    2015-12-01

    Herein, we presented a facile seeded growth method to prepare high-quality three-dimensional (3D) Au@Pt bimetallic nanodendrite-decorated molybdenum disulfide (MoS2) nanosheets (Au@Pt/MoS2). Transmission electron microscopy (TEM) and high-resolution TEM exhibited that Au@Pt core-shell nanostructures were dispersed onto the surface of MoS2 nanosheets. More importantly, the thickness of the Pt shell of the Au@Pt bimetallic nanodendrites on the surface of the MoS2 nanosheets could be easily tuned via simply changing the synthesis parameters, such as the concentration of H2PtCl6, reaction time and temperature, which greatly influence the catalytic ability of Au@Pt/MoS2 nanohybrids. Both cyclic voltammetry (CV) and chronoamperometry (CA) demonstrated that the as-prepared Au@Pt/MoS2 nanohybrids possessed much higher electrocatalytic activity and stability than Pt/MoS2 or commercial Pt/C catalyst. The peak current mass density of the selected Au@Pt/MoS2 was 6.24 A mg-1, which was 3389 and 20.3 times those of Pt/C (0.00184 A mg-1) and Pt/MoS2 (0.307 A mg-1), respectively. The presented method may be a facile approach for the synthesis of MoS2-supported bimetallic nanocomposites, which is significant for the development of high performance MoS2-based sensors and catalysts.Herein, we presented a facile seeded growth method to prepare high-quality three-dimensional (3D) Au@Pt bimetallic nanodendrite-decorated molybdenum disulfide (MoS2) nanosheets (Au@Pt/MoS2). Transmission electron microscopy (TEM) and high-resolution TEM exhibited that Au@Pt core-shell nanostructures were dispersed onto the surface of MoS2 nanosheets. More importantly, the thickness of the Pt shell of the Au@Pt bimetallic nanodendrites on the surface of the MoS2 nanosheets could be easily tuned via simply changing the synthesis parameters, such as the concentration of H2PtCl6, reaction time and temperature, which greatly influence the catalytic ability of Au@Pt/MoS2 nanohybrids. Both cyclic voltammetry (CV

  19. Synthesis and Electrocatalytic Performance of Multi-Component Nanoporous PtRuCuW Alloy for Direct Methanol Fuel Cells

    Directory of Open Access Journals (Sweden)

    Xiaoting Chen

    2015-06-01

    Full Text Available We have prepared a multi-component nanoporous PtRuCuW (np-PtRuCuW electrocatalyst via a combined chemical dealloying and mechanical alloying process. The X-ray diffraction (XRD, transmission electron microscopy (TEM and electrochemical measurements have been applied to characterize the microstructure and electrocatalytic activities of the np-PtRuCuW. The np-PtRuCuW catalyst has a unique three-dimensional bi-continuous ligament structure and the length scale is 2.0 ± 0.3 nm. The np-PtRuCuW catalyst shows a relatively high level of activity normalized to mass (467.1 mA mgPt−1 and electrochemically active surface area (1.8 mA cm−2 compared to the state-of-the-art commercial PtC and PtRu catalyst at anode. Although the CO stripping peak of np-PtRuCuW 0.47 V (vs. saturated calomel electrode, SCE is more positive than PtRu, there is a 200 mV negative shift compared to PtC (0.67 V vs. SCE. In addition, the half-wave potential and specific activity towards oxygen reduction of np-PtRuCuW are 0.877 V (vs. reversible hydrogen electrode, RHE and 0.26 mA cm−2, indicating a great enhancement towards oxygen reduction than the commercial PtC.

  20. Apolipoprotein L1 confers pH-switchable ion permeability to phospholipid vesicles.

    Science.gov (United States)

    Bruno, Jonathan; Pozzi, Nicola; Oliva, Jonathan; Edwards, John C

    2017-11-03

    Apolipoprotein L1 (ApoL1) is a human serum protein conferring resistance to African trypanosomes, and certain ApoL1 variants increase susceptibility to some progressive kidney diseases. ApoL1 has been hypothesized to function like a pore-forming colicin and has been reported to have permeability effects on both intracellular and plasma membranes. Here, to gain insight into how ApoL1 may function in vivo , we used vesicle-based ion permeability, direct membrane association, and intrinsic fluorescence to study the activities of purified recombinant ApoL1. We found that ApoL1 confers chloride-selective permeability to preformed phospholipid vesicles and that this selectivity is strongly pH-sensitive, with maximal activity at pH 5 and little activity above pH 7. When ApoL1 and lipid were allowed to interact at low pH and were then brought to neutral pH, chloride permeability was suppressed, and potassium permeability was activated. Both chloride and potassium permeability linearly correlated with the mass of ApoL1 in the reaction mixture, and both exhibited lipid selectivity, requiring the presence of negatively charged lipids for activity. Potassium, but not chloride, permease activity required the presence of calcium ions in both the association and activation steps. Direct assessment of ApoL1-lipid associations confirmed that ApoL1 stably associates with phospholipid vesicles, requiring low pH and the presence of negatively charged phospholipids for maximal binding. Intrinsic fluorescence of ApoL1 supported the presence of a significant structural transition when ApoL1 is mixed with lipids at low pH. This pH-switchable ion-selective permeability may explain the different effects of ApoL1 reported in intracellular and plasma membrane environments. © 2017 by The American Society for Biochemistry and Molecular Biology, Inc.

  1. Misfit strain phase diagrams of epitaxial PMN–PT films

    Energy Technology Data Exchange (ETDEWEB)

    Khakpash, N.; Khassaf, H.; Rossetti, G. A. [Department of Materials Science and Engineering and Institute of Materials Science, University of Connecticut, Storrs, Connecticut 06269 (United States); Alpay, S. P., E-mail: p.alpay@ims.uconn.edu [Department of Materials Science and Engineering and Institute of Materials Science, University of Connecticut, Storrs, Connecticut 06269 (United States); Department of Physics, University of Connecticut, Storrs, Connecticut 06269 (United States)

    2015-02-23

    Misfit strain–temperature phase diagrams of three compositions of (001) pseudocubic (1 − x)·Pb (Mg{sub l/3}Nb{sub 2/3})O{sub 3} − x·PbTiO{sub 3} (PMN–PT) thin films are computed using a phenomenological model. Two (x = 0.30, 0.42) are located near the morphotropic phase boundary (MPB) of bulk PMN–PT at room temperature (RT) and one (x = 0.70) is located far from the MPB. The results show that it is possible to stabilize an adaptive monoclinic phase over a wide range of misfit strains. At RT, the stability region of this phase is much larger for PMN–PT compared to barium strontium titanate and lead zirconate titanate films.

  2. The high-pressure phase of CePtAl

    International Nuclear Information System (INIS)

    Heymann, Gunter; Heying, Birgit; Rodewald, Ute C.; Janka, Oliver; Univ. Oldenburg

    2017-01-01

    The intermetallic aluminum compound HP-CePtAl was synthesized by arc melting of the elements with subsequent high-pressure/high-temperature treatment at 1620 K and 10.5 GPa in a multianvil press. The compound crystallizes in the hexagonal MgZn_2-type structure (P6_3/mmc) with lattice parameters of a=552.7(1) and c=898.8(2) pm refined from powder X-ray diffraction data. With the help of single crystal investigations (wR=0.0527, 187 F"2 values, 13 variables), the proposed structure type was confirmed and the mixed Pt/Al site occupations could be refined. Magnetic susceptibility measurements showed a disappearance of the complex magnetic ordering phenomena, which are observed in NP-CePtAl.

  3. The high-pressure phase of CePtAl

    Energy Technology Data Exchange (ETDEWEB)

    Heymann, Gunter [Univ. Innsbruck (Austria). Inst. fuer Allgemeine, Anorganische und Theoretische Chemie; Heying, Birgit; Rodewald, Ute C. [Univ. Muenster (Germany). Inst. fuer Anorganische und Analytische Chemie; Janka, Oliver [Univ. Muenster (Germany). Inst. fuer Anorganische und Analytische Chemie; Univ. Oldenburg (Germany). Inst. fuer Chemie

    2017-03-01

    The intermetallic aluminum compound HP-CePtAl was synthesized by arc melting of the elements with subsequent high-pressure/high-temperature treatment at 1620 K and 10.5 GPa in a multianvil press. The compound crystallizes in the hexagonal MgZn{sub 2}-type structure (P6{sub 3}/mmc) with lattice parameters of a=552.7(1) and c=898.8(2) pm refined from powder X-ray diffraction data. With the help of single crystal investigations (wR=0.0527, 187 F{sup 2} values, 13 variables), the proposed structure type was confirmed and the mixed Pt/Al site occupations could be refined. Magnetic susceptibility measurements showed a disappearance of the complex magnetic ordering phenomena, which are observed in NP-CePtAl.

  4. Optimization of Pt-Ir on carbon fiber paper for the electro-oxidation of ammonia in alkaline media

    International Nuclear Information System (INIS)

    Boggs, Bryan K.; Botte, Gerardine G.

    2010-01-01

    Plating bath concentrations of Pt(IV) and Ir(III) have been optimized as well as the total catalytic loading of bimetallic Pt-Ir alloy for the electro-oxidation of ammonia in alkaline media at standard conditions. This was accomplished using cyclic voltammetry, scanning electron microscopy (SEM), energy dispersive X-ray (EDX), and statistical optimization tools. Concentrations of Pt(IV) and Ir(III) of the plating bath strongly influence electrode surface atomic compositions of the Pt-Ir alloy directly affecting the electro-oxidation behavior of ammonia. Several anode materials were studied using cyclic voltammetry, which demonstrated that Pt-Ir was the most active catalyst for the electro-oxidation of ammonia. Criteria for optimization were minimizing the climatic oxidation overpotential for ammonia and maximizing the exchange current density. Optimized bath composition was found to be 8.844 ± 0.001 g L -1 Pt(IV) and 4.112 ± 0.001 g L -1 Ir(III) based on electrochemical techniques. Physical characterization of the electrodes by SEM indicates that the plating bath concentrations of Pt and Ir influence the growth and deposition behavior of the alloy.

  5. Avelumab, an anti-PD-L1 antibody, in patients with locally advanced or metastatic breast cancer: a phase 1b JAVELIN Solid Tumor study

    OpenAIRE

    Dirix, Luc Y.; Takacs, Istvan; Jerusalem, Guy; Nikolinakos, Petros; Arkenau, Hendrik-Tobias; Forero-Torres, Andres; Boccia, Ralph; Lippman, Marc E.; Somer, Robert; Smakal, Martin; Emens, Leisha A.; Hrinczenko, Borys; Edenfield, William; Gurtler, Jayne; von Heydebreck, Anja

    2017-01-01

    Purpose Agents targeting programmed death receptor 1 (PD-1) or its ligand (PD-L1) have shown antitumor activity in the treatment of metastatic breast cancer (MBC). The aim of this study was to assess the activity of avelumab, a PD-L1 inhibitor, in patients with MBC. Methods In a phase 1 trial (JAVELIN Solid Tumor; NCT01772004), patients with MBC refractory to or progressing after standard-of-care therapy received avelumab intravenously 10 mg/kg every 2 weeks. Tumors were assessed every 6 week...

  6. Laser sputtering. Pt. 1

    International Nuclear Information System (INIS)

    Kelly, R.; Cuomo, J.J.; Leary, P.A.; Rothenburg, J.E.; Braren, B.E.; Aliotta, C.F.

    1985-01-01

    Irradiation, i.e. bombardment, with 193 nm laser pulses having an energy fluence of 2.5 J/cm 2 and a duration of proportional12 ns leads to rapid sputtering with Au, Al 2 O 3 , MgO, MgO.Al 2 O 3 , SiO 2 , glass, and LaB 6 , relatively slow sputtering with MgF 2 and diamond, and mainly thermal-stress cracking with W. Scanning electron microscopy (SEM) suggests that the mechanism for the sputtering of Au in either vacuum or air is one based on the hydrodynamics of molten Au, while an SEM-derived surface temperature estimate confirms that thermal sputtering (which might have been expected) is not possible. SEM with W shows that the near total lack of material removal is due to the thermal-stress cracking not leading to completed exfoliation, together with the surface temperature being too low for either hydrodynamical or thermal processes. Corresponding SEM with Al 2 O 3 shows, in the case of specimens bombarded in vacuum, topography of such a type that all mechanisms except electronic ones can be ruled out. The topography of Al 2 O 3 or other oxides bombarded in air through a mask is somewhat different, showing craters as for vacuum bombardments but ones which have a cone-like pattern on the bottom. (orig.)

  7. Magnetic properties and microstructure study of high coercivity Au/FePt/Au trilayer thin films

    International Nuclear Information System (INIS)

    Chen, S.K.; Yuan, F.T.; Liao, W.M.; Hsu, C.W.; Horng, Lance

    2006-01-01

    High-coercivity Au(60 nm)/FePt(δ nm)/Au(60 nm) trilayer samples were prepared by sputtering at room temperature, followed by post annealing at different temperatures. For the sample with δ=60 nm, L1 ordering transformation occurs at 500 deg. C. Coercivity (H c ) is increased with the annealing temperature in the studied range 400-800 deg. C. The H c value of the trilayer films is also varied with thickness of FePt intermediate layer (δ), from 27 kOe for δ=60 nm to a maximum value of 33.5 kOe for δ=20 nm. X-ray diffraction data indicate that the diffusion of Au atoms into the FePt L1 lattice is negligible even after a high-temperature (800 deg. C) annealing process. Furthermore, ordering parameter is almost unchanged as δ is reduced from 60 to 15 nm. Transmission electron microscope (TEM) photos indicate that small FePt Ll particles are dispersed amid the large-grained Au. We believe that the high coercivity of the trilayer sample is attributed to the small and uniform grain sizes of the highly ordered FePt particles which have perfect phase separation with Au matrix

  8. Improved (0 0 1)-texture of FePt-C for heat-assisted magnetic recording media by insertion of Cr buffer layer

    Energy Technology Data Exchange (ETDEWEB)

    Shiroyama, T.; Wang, J.; Felicia, A.; Takahashi, Y.K.; Hono, K., E-mail: kazuhiro.hono@nims.go.jp

    2017-06-15

    Highlights: • Improvement of (0 0 1)-texture of prototype FePt-C granular films for heat heat assisted magnetic recording media. • Insertion of Cr buffer layer improves the crystallographic textures of the MgO underlayers, thereby reduces in-plane component in the FePt-C recording layer. • The growth in the grain size of the MgO underlayer as well as the (0 0 1)-texture of the MgO underlayer are the key factor in reducing the in-plane component in the FePt-C recording layer. - Abstract: FePt-C granular films deposited on MgO underlayers are the prototype media for heat-assisted magnetic recording. To reduce the in-plane magnetic component in the FePt-C media, we investigated the effect of Cr buffer layers on the crystallographic textures of the MgO underlayers and the resultant magnetic properties of the FePt-C layers. By growing a MgO underlayer on a Cr buffer layer, the (0 0 1) texture of the MgO underlayer is improved, on which the in-plane component of a FePt-C film is substantially reduced. We conclude that the growth in the grain size of the MgO underlayer is the key factor in reducing the in-plane component in the FePt-C recording layer.

  9. Effects of ethanol and NAP on cerebellar expression of the neural cell adhesion molecule L1.

    Directory of Open Access Journals (Sweden)

    Devon M Fitzgerald

    Full Text Available The neural cell adhesion molecule L1 is critical for brain development and plays a role in learning and memory in the adult. Ethanol inhibits L1-mediated cell adhesion and neurite outgrowth in cerebellar granule neurons (CGNs, and these actions might underlie the cerebellar dysmorphology of fetal alcohol spectrum disorders. The peptide NAP potently blocks ethanol inhibition of L1 adhesion and prevents ethanol teratogenesis. We used quantitative RT-PCR and Western blotting of extracts of cerebellar slices, CGNs, and astrocytes from postnatal day 7 (PD7 rats to investigate whether ethanol and NAP act in part by regulating the expression of L1. Treatment of cerebellar slices with 20 mM ethanol, 10(-12 M NAP, or both for 4 hours, 24 hours, and 10 days did not significantly affect L1 mRNA and protein levels. Similar treatment for 4 or 24 hours did not regulate L1 expression in primary cultures of CGNs and astrocytes, the predominant cerebellar cell types. Because ethanol also damages the adult cerebellum, we studied the effects of chronic ethanol exposure in adult rats. One year of binge drinking did not alter L1 gene and protein expression in extracts from whole cerebellum. Thus, ethanol does not alter L1 expression in the developing or adult cerebellum; more likely, ethanol disrupts L1 function by modifying its conformation and signaling. Likewise, NAP antagonizes the actions of ethanol without altering L1 expression.

  10. Mechanisms for the proliferation of eosinophilic leukemia cells by FIP1L1-PDGFRα

    International Nuclear Information System (INIS)

    Ishihara, Kenji; Kitamura, Hajime; Hiraizumi, Kenji; Kaneko, Motoko; Takahashi, Aki; Zee, OkPyo; Seyama, Toshio; Hong, JangJa; Ohuchi, Kazuo; Hirasawa, Noriyasu

    2008-01-01

    The constitutively activated tyrosine kinase Fip1-like 1 (FIP1L1)-platelet-derived growth factor receptor α (PDGFRα) causes eosinophilic leukemia EoL-1 cells to proliferate. Recently, we demonstrated that histone deacetylase inhibitors suppressed this proliferation and induced the differentiation of EoL-1 cells into eosinophils in parallel with a decrease in the level of FIP1L1-PDGFRα. In this study, we analyzed the mechanism by which FIP1L1-PDGFRα induces the proliferation and whether the suppression of cell proliferation triggers the differentiation into eosinophils. The FIP1L1-PDGFRα inhibitor imatinib inhibited the proliferation of EoL-1 cells and decreased the level of the oncoprotein c-Myc as well as the phosphorylation of extracellular signal-regulated kinase and c-Jun N-terminal kinase (JNK). The proliferation of EoL-1 cells and expression of c-Myc were also inhibited by the MEK inhibitor U0126 and JNK inhibitor SP600125. The expression of the eosinophilic differentiation marker CCR3 was not induced by imatinib. These findings suggest that FIP1L1-PDGFRα induces the proliferation of EoL-1 cells through the induction of c-Myc expression via ERK and JNK signaling pathways, but is not involved in the inhibition of differentiation toward mature eosinophils

  11. Pt/C Fuel Cell Catalyst Degradation

    DEFF Research Database (Denmark)

    Zana, Alessandro

    This thesis investigates the degradation behavior of Pt/C catalysts under simulated automotive conditions. By using the “tool box” synthesis method the Pt loading has been changed from low to high Pt loadings, therefore permitting to study the role of Pt on the degradation of high surface area (H...

  12. Metal Phosphate-Supported Pt Catalysts for CO Oxidation

    Directory of Open Access Journals (Sweden)

    Xiaoshuang Qian

    2014-12-01

    Full Text Available Oxides (such as SiO2, TiO2, ZrO2, Al2O3, Fe2O3, CeO2 have often been used to prepare supported Pt catalysts for CO oxidation and other reactions, whereas metal phosphate-supported Pt catalysts for CO oxidation were rarely reported. Metal phosphates are a family of metal salts with high thermal stability and acid-base properties. Hydroxyapatite (Ca10(PO46(OH2, denoted as Ca-P-O here also has rich hydroxyls. Here we report a series of metal phosphate-supported Pt (Pt/M-P-O, M = Mg, Al, Ca, Fe, Co, Zn, La catalysts for CO oxidation. Pt/Ca-P-O shows the highest activity. Relevant characterization was conducted using N2 adsorption-desorption, inductively coupled plasma (ICP atomic emission spectroscopy, X-ray diffraction (XRD, transmission electron microscopy (TEM, CO2 temperature-programmed desorption (CO2-TPD, X-ray photoelectron spectroscopy (XPS, and H2 temperature-programmed reduction (H2-TPR. This work furnishes a new catalyst system for CO oxidation and other possible reactions.

  13. Thermically stimulated exoelectronic emissions and thermoluminescence of MgO

    International Nuclear Information System (INIS)

    Chubaci, J.F.D.

    1987-01-01

    In this work, studies were performed on the following topics: i) thermically stimulated exoelectronic emission (TSEE) in pure MgO single crystals ion implanted, submitted to thermal treatment with fast on slow cooling and water adsorption; ii) ultraviolet light effect on TSEE; iii) thermoluminescent emission; iv) crystallization of FeCoB amorphous alloys. (A.C.A.S.) [pt

  14. Influence of surface morphology on methanol oxidation at a glassy carbon-supported Pt catalyst

    Directory of Open Access Journals (Sweden)

    S. STEVANOVIC

    2008-08-01

    Full Text Available Platinum supported on glassy carbon (GC was used as a model system for studying the influence of the surface morphology of a Pt catalyst on methanol oxidation in alkaline and acidic solutions. Platinum was deposited by the potential step method on GC samples from H2SO4 + H2PtCl6 solution under the same conditions with loadings from 10 to 80 mg cm-2. AFM and STM images of the GC/Pt electrodes showed that the Pt was deposited in the form of 3D agglomerates composed of spherical particles. Longer deposition times resulted in increased growth of Pt forms and a decrease in the specific area of the Pt. The real surface area of Pt increased with loading but the changes were almost negligible at higher loadings. Nevertheless, both the specific and mass activity of platinum supported on glassy carbon for methanol oxidation in acidic and in alkaline solutions exhibit a volcanic dependence with respect to the platinum loading. The increase in the activity can be explained by the increasing the particle size with the loading and thus an increase in the contiguous Pt sites available for adsorption and decomposition of methanol. However, the decrease in the activity of the catalyst with further increase of loading and particle size after reaching the maximum is related to the decrease of active sites available for methanol adsorption and their accessibility as a result of more close proximity and pronounced coalescence of the Pt particles.

  15. Te/Pt nanonetwork modified carbon fiber microelectrodes for methanol oxidation

    International Nuclear Information System (INIS)

    Tsai, Hsiang-Yu; Shih, Zih-Yu; Lin, Zong-Hong; Chang, Huan-Tsung

    2013-01-01

    Te/Pt nanonetwork-decorated carbon fiber microelectrodes (CFMEs) have been fabricated and employed as anodic catalysts in a direct methanol fuel cell (DMFC). Te nanowires were prepared from tellurite ions (TeO 3 2− ) through a seed-mediated growth process and were deposited onto CFMEs to form three-dimensional Te nanonetworks. The Te nanonetworks then acted as a framework and reducing agent to reduce PtCl 6 2− ions to form Te/Pt through a galvanic replacement reaction, leading to the formation of Te/PtCFMEs. By controlling the reaction time, the amount of Pt and morphology of Te/Pt nanonetworks were controlled, leading to various degrees of electrocatalytic activity. The Te/PtCFMEs provide a high electrochemical active surface area (129.2 m 2 g −1 ), good catalytic activity (1.2 A mg −1 ), high current density (20.0 mA cm −2 ), long durability, and tolerance toward the poisoning species for methanol oxidation in 0.5 M sulfuric acid containing 1 M methanol. We have further demonstrated an enhanced current density by separately using 3 and 5 Te/PtCFMEs. Our results show that the low-cost, stable, and effective Te/PtCFMEs have great potential in the fabrication of cost-effective fuel cells. (paper)

  16. Lowering of the L10 ordering temperature of FePt nanoparticles by He+ ion irradiation

    International Nuclear Information System (INIS)

    Wiedwald, U.; Klimmer, A.; Kern, B.; Han, L.; Boyen, H.-G.; Ziemann, P.; Fauth, K.

    2007-01-01

    Arrays of FePt particles (diameter 7 nm) with mean interparticle distances of 60 nm are prepared by a micellar technique on Si substrates. The phase transition of these magnetic particles towards the chemically ordered L1 0 phase is tracked for 350 kV He + ion irradiated samples and compared to a nonirradiated reference. Due to the large separation of the magnetically decoupled particles the array can be safely annealed without any agglomeration as usually observed for more densely packed colloidal FePt nanoparticles. The He + ion exposure yields a significant reduction of the ordering temperature by more than 100 K

  17. Controlled synthesis of Pt/CS/PW12-GNs composite as an anodic electrocatalyst for direct methanol fuel cells

    International Nuclear Information System (INIS)

    Li, Zhongshui; Lei, Fengling; Ye, Lingting; Zhang, Xiaofeng; Lin, Shen

    2015-01-01

    Controlled assembly in aqueous solution was used to synthesize the well-organized Pt/CS/PW 12 -GNs composite. By the aid of linear cationic polysaccharide chitosan, 2-D distribution worm-like Pt nanoparticles with their length and width of 15–20 and 3–4 nm, respectively, were formed on the surface of CS/PW 12 -GNs using HCOOH as a reducing agent at room temperature. The introduction of CS leads to well dispersion of worm-like Pt nanoparticles, the electroactivity of H 3 PW 12 O 40 (PW 12 ) alleviates CO poisoning toward Pt particles, and graphene nanosheets (GNs) ensure excellent electrical conductivity of the composites. The combined action among different components results in significantly enhanced catalytic activity of Pt/CS/PW 12 -GNs toward methanol oxidation and better tolerance of CO. The as-synthesized Pt/CS/PW 12 -GNs exhibit the forward peak current density of 445 mA mg −1 , which is much higher than that (220 mA mg −1 ) for Pt/C-JM (the commercially available Johnson Matthey Hispec4000 catalyst, simplified as Pt/C-JM) and some recently reported Pt/graphene-based nanomaterials. The construction of 2-D distribution worm-like Pt nanoparticles and facile wet chemical synthesis strategy provide a promising way to develop superior performance electrocatalysts for direct methanol fuel cells applications

  18. Controlled synthesis of Pt/CS/PW{sub 12}-GNs composite as an anodic electrocatalyst for direct methanol fuel cells

    Energy Technology Data Exchange (ETDEWEB)

    Li, Zhongshui; Lei, Fengling; Ye, Lingting; Zhang, Xiaofeng; Lin, Shen, E-mail: shenlin@fjnu.edu.cn [Fujian Normal University, College of Chemistry & Chemical Engineering (China)

    2015-04-15

    Controlled assembly in aqueous solution was used to synthesize the well-organized Pt/CS/PW{sub 12}-GNs composite. By the aid of linear cationic polysaccharide chitosan, 2-D distribution worm-like Pt nanoparticles with their length and width of 15–20 and 3–4 nm, respectively, were formed on the surface of CS/PW{sub 12}-GNs using HCOOH as a reducing agent at room temperature. The introduction of CS leads to well dispersion of worm-like Pt nanoparticles, the electroactivity of H{sub 3}PW{sub 12}O{sub 40} (PW{sub 12}) alleviates CO poisoning toward Pt particles, and graphene nanosheets (GNs) ensure excellent electrical conductivity of the composites. The combined action among different components results in significantly enhanced catalytic activity of Pt/CS/PW{sub 12}-GNs toward methanol oxidation and better tolerance of CO. The as-synthesized Pt/CS/PW{sub 12}-GNs exhibit the forward peak current density of 445 mA mg{sup −1}, which is much higher than that (220 mA mg{sup −1}) for Pt/C-JM (the commercially available Johnson Matthey Hispec4000 catalyst, simplified as Pt/C-JM) and some recently reported Pt/graphene-based nanomaterials. The construction of 2-D distribution worm-like Pt nanoparticles and facile wet chemical synthesis strategy provide a promising way to develop superior performance electrocatalysts for direct methanol fuel cells applications.

  19. Subband Adaptive Filtering with l1-Norm Constraint for Sparse System Identification

    Directory of Open Access Journals (Sweden)

    Young-Seok Choi

    2013-01-01

    Full Text Available This paper presents a new approach of the normalized subband adaptive filter (NSAF which directly exploits the sparsity condition of an underlying system for sparse system identification. The proposed NSAF integrates a weighted l1-norm constraint into the cost function of the NSAF algorithm. To get the optimum solution of the weighted l1-norm regularized cost function, a subgradient calculus is employed, resulting in a stochastic gradient based update recursion of the weighted l1-norm regularized NSAF. The choice of distinct weighted l1-norm regularization leads to two versions of the l1-norm regularized NSAF. Numerical results clearly indicate the superior convergence of the l1-norm regularized NSAFs over the classical NSAF especially when identifying a sparse system.

  20. How Does L1 and L2 Exposure Impact L1 Performance in Bilingual Children? Evidence from Polish-English Migrants to the United Kingdom

    Directory of Open Access Journals (Sweden)

    Ewa Haman

    2017-09-01

    Full Text Available Most studies on bilingual language development focus on children’s second language (L2. Here, we investigated first language (L1 development of Polish-English early migrant bilinguals in four domains: vocabulary, grammar, phonological processing, and discourse. We first compared Polish language skills between bilinguals and their Polish non-migrant monolingual peers, and then investigated the influence of the cumulative exposure to L1 and L2 on bilinguals’ performance. We then examined whether high exposure to L1 could possibly minimize the gap between monolinguals and bilinguals. We analyzed data from 233 typically developing children (88 bilingual and 145 monolingual aged 4;0 to 7;5 (years;months on six language measures in Polish: receptive vocabulary, productive vocabulary, receptive grammar, productive grammar (sentence repetition, phonological processing (non-word repetition, and discourse abilities (narration. Information about language exposure was obtained via parental questionnaires. For each language task, we analyzed the data from the subsample of bilinguals who had completed all the tasks in question and from monolinguals matched one-on-one to the bilingual group on age, SES (measured by years of mother’s education, gender, non-verbal IQ, and short-term memory. The bilingual children scored lower than monolinguals in all language domains, except discourse. The group differences were more pronounced on the productive tasks (vocabulary, grammar, and phonological processing and moderate on the receptive tasks (vocabulary and grammar. L1 exposure correlated positively with the vocabulary size and phonological processing. Grammar scores were not related to the levels of L1 exposure, but were predicted by general cognitive abilities. L2 exposure negatively influenced productive grammar in L1, suggesting possible L2 transfer effects on L1 grammatical performance. Children’s narrative skills benefitted from exposure to two languages

  1. Structure, magnetism, and interface properties of epitactical thin Fe and FePt films on GaAs(001) substrates; Struktur, Magnetismus und Grenzflaecheneigenschaften epitaktischer duenner Fe- und FePt-Filme auf GaAs(001)-Substraten

    Energy Technology Data Exchange (ETDEWEB)

    Schuster, Ellen Ursula

    2007-12-17

    The research in this thesis is focused on the study of the Fe spin structure and interface magnetism of thin epitaxial Fe layers or epitaxial FePt alloy films with chemical L1{sub 0} order on GaAs(001) surfaces. The main method of investigation was isotope-specific conversion electron Moessbauer spectroscopy (CEMS) combined with the {sup 57}Fe probe-layer technique in the temperature range of 4.2-300 K. The film structure was studied using electron diffraction (RHEED) and X-ray diffraction (XRD). The chemical order parameter S determined by XRD was found to increase with rising growth temperature, T{sub S}, to a maximum value of 0.71, until long range order is destroyed at T{sub S}>350 C by alloying with the substrate. As an important result a linear correlation between short-range order (revealed by the relative spectral area of the L1{sub 0} phase) and long-range order S was observed. The observed perpendicular Fe spin texture, characterized by the mean tilting angle left angle {theta} right angle of the Fe spins (relative to the film normal direction), was found to correlate with the L1{sub 0} phase content and with S. Furthermore, epitaxial Fe(001) films on GaAs(001)-(4 x 6) and on GaAs(001)-LED surfaces were grown successfully. In the initial stage of Fe film growth non-monotonous behavior of the in-plane lattice parameter was observed by RHEED. The magnetic hyperfine field distributions P(B{sub hf}) at the Fe/GaAs interface extracted from CEMS spectra for T{sub S}=-140 C or room temperature (RT) were found to be very similar. The observed large mean hyperfine fields of left angle B{sub hf} right angle {approx}25-27 T at the interface indicate the presence of high average Fe moments of 1.7-1.8 {mu}{sub B}. Nonmagnetic interface layers either can be excluded (Fe/GaAs) or are very thin (0.5 ML,Fe/GaAs-LED). Owing to its island structure an ultrathin (1.9 ML thick) uncoated Fe(001) film on GaAs(001)-(4 x 6) shows superparamagnetism with a blocking temperature of

  2. Equilibrium, stability and transport in L=1 compact helical axis configuration

    International Nuclear Information System (INIS)

    Kikuchi, Hitoshi; Ueno, Hikaru; Aizawa, Masamitsu; Suzuki, Kiyomitsu; Gesso, Hirokazu; Saito, Katsunori; Kawakami, Ichiro; Shiina, Shoichi

    1990-01-01

    The L=1 torsatron is modified by two methods to improve the plasma stability. First one is the negative pitch modulation of coil winding. Second is the superposition of a relatively weak L=-1 torsatron field. These modification give rise to a local magnetic well keeping a positive magnetic shear. The equilibrium, stability and transport of plasma in these modified L=1 torsatrons are described and discussed. (author)

  3. Paucity of PD-L1 expression in prostate cancer: innate and adaptive immune resistance.

    Science.gov (United States)

    Martin, A M; Nirschl, T R; Nirschl, C J; Francica, B J; Kochel, C M; van Bokhoven, A; Meeker, A K; Lucia, M S; Anders, R A; DeMarzo, A M; Drake, C G

    2015-12-01

    Primary prostate cancers are infiltrated with programmed death-1 (PD-1) expressing CD8+ T-cells. However, in early clinical trials, men with metastatic castrate-resistant prostate cancer did not respond to PD-1 blockade as a monotherapy. One explanation for this unresponsiveness could be that prostate tumors generally do not express programmed death ligand-1 (PD-L1), the primary ligand for PD-1. However, lack of PD-L1 expression in prostate cancer would be surprising, given that phosphatase and tensin homolog (PTEN) loss is relatively common in prostate cancer and several studies have shown that PTEN loss correlates with PD-L1 upregulation--constituting a mechanism of innate immune resistance. This study tested whether prostate cancer cells were capable of expressing PD-L1, and whether the rare PD-L1 expression that occurs in human specimens correlates with PTEN loss. Human prostate cancer cell lines were evaluated for PD-L1 expression and loss of PTEN by flow cytometry and western blotting, respectively. Immunohistochemical (IHC) staining for PTEN was correlated with PD-L1 IHC using a series of resected human prostate cancer samples. In vitro, many prostate cancer cell lines upregulated PD-L1 expression in response to inflammatory cytokines, consistent with adaptive immune resistance. In these cell lines, no association between PTEN loss and PD-L1 expression was apparent. In primary prostate tumors, PD-L1 expression was rare, and was not associated with PTEN loss. These studies show that some prostate cancer cell lines are capable of expressing PD-L1. However, in human prostate cancer, PTEN loss is not associated with PD-L1 expression, arguing against innate immune resistance as a mechanism that mitigates antitumor immune responses in this disease.

  4. Purification and Characterization of Recombinant Vaccinia L1R Protein from Escherichia coli

    Science.gov (United States)

    2016-08-01

    RECOMBINANT VACCINIA L1R PROTEIN FROM ESCHERICHIA COLI 1. INTRODUCTION 1.1 Background Vaccinia virus (VACV) is the active component of the...the preparation of the recombinant VACV L1R protein fragment by denaturing , refolding, and purifying material expressed into inclusion bodies in...PURIFICATION AND CHARACTERIZATION OF RECOMBINANT VACCINIA L1R PROTEIN FROM ESCHERICHIA COLI ECBC-TR-1370

  5. Ultrasensitive colorimetric immunoassay for hCG detection based on dual catalysis of Au@Pt core-shell nanoparticle functionalized by horseradish peroxidase

    Science.gov (United States)

    Wang, Weiguo; Zou, Yake; Yan, Jinwu; Liu, Jing; Chen, Huixiong; Li, Shan; Zhang, Lei

    2018-03-01

    In this paper, an ultrasensitive colorimetric biosensor for human chorionic gonadotrophin (hCG) detection was designed from bottom-up method based on the dual catalysis of the horseradish peroxidase (HRP) and Au@Pt nanoparticles (NPs) relative to H2O2-TEM system. HRP and monoclonal mouse anti-hCG antibody (β-submit, mAb1) were co-immobilized onto the Au@Pt NP surface to improve catalytic efficiency and specificity, which formed a dual functionalized Au@Pt-HRP probe with the mean size of 42.8 nm (D50). The colorimetric immunoassay was developed for the hCG detection, and the Au@Pt-HRP probe featured a higher sensitivity in the concentration range of 0.4-12.8 IU L- 1 with a low limit of detection (LOD) of 0.1 IU L- 1 compared with the LODs of 0.8 IU L- 1 for BA-ELISA and of 2.0 IU L- 1 for Au@Pt, which indicated that the Au@Pt-HRP probe possessed higher catalytic efficiency with 2.8-fold increase over Au@Pt and 33.8-fold increase over HRP. Also, the Au@Pt-HRP probe exhibited good precision and reproducibility, high specificity and acceptable accuracy with CV being less than 15%. The dual functionalized Au@Pt-HRP probe as a type of signal amplified method was firstly applied in the colorimetric immunoassay for the hCG detection.

  6. Combining Amplification Typing of L1 Active Subfamilies (ATLAS) with High-Throughput Sequencing.

    Science.gov (United States)

    Rahbari, Raheleh; Badge, Richard M

    2016-01-01

    With the advent of new generations of high-throughput sequencing technologies, the catalog of human genome variants created by retrotransposon activity is expanding rapidly. However, despite these advances in describing L1 diversity and the fact that L1 must retrotranspose in the germline or prior to germline partitioning to be evolutionarily successful, direct assessment of de novo L1 retrotransposition in the germline or early embryogenesis has not been achieved for endogenous L1 elements. A direct study of de novo L1 retrotransposition into susceptible loci within sperm DNA (Freeman et al., Hum Mutat 32(8):978-988, 2011) suggested that the rate of L1 retrotransposition in the germline is much lower than previously estimated (ATLAS L1 display technique (Badge et al., Am J Hum Genet 72(4):823-838, 2003) to investigate de novo L1 retrotransposition in human genomes. In this chapter, we describe how we combined a high-coverage ATLAS variant with high-throughput sequencing, achieving 11-25× sequence depth per single amplicon, to study L1 retrotransposition in whole genome amplified (WGA) DNAs.

  7. Hepatic NPC1L1 overexpression ameliorates glucose metabolism in diabetic mice via suppression of gluconeogenesis.

    Science.gov (United States)

    Kurano, Makoto; Hara, Masumi; Satoh, Hiroaki; Tsukamoto, Kazuhisa

    2015-05-01

    Inhibition of intestinal NPC1L1 by ezetimibe has been demonstrated to improve glucose metabolism in rodent models; however, the role of hepatic NPC1L1 in glucose metabolism has not been elucidated. In this study, we analyzed the effects of hepatic NPC1L1 on glucose metabolism. We overexpressed NPC1L1 in the livers of lean wild type mice, diet-induced obesity mice and db/db mice with adenoviral gene transfer. We found that in all three mouse models, hepatic NPC1L1 overexpression lowered fasting blood glucose levels as well as blood glucose levels on ad libitum; in db/db mice, hepatic NPC1L1 overexpression improved blood glucose levels to almost the same as those found in lean wild type mice. A pyruvate tolerance test revealed that gluconeogenesis was suppressed by hepatic NPC1L1 overexpression. Further analyses revealed that hepatic NPC1L1 overexpression decreased the expression of FoxO1, resulting in the reduced expression of G6Pase and PEPCK, key enzymes in gluconeogenesis. These results indicate that hepatic NPC1L1 might have distinct properties of suppressing gluconeogenesis via inhibition of FoxO1 pathways. Copyright © 2015 Elsevier Inc. All rights reserved.

  8. Negative Transfer of L1 on English Grammar Learning in SLA

    Institute of Scientific and Technical Information of China (English)

    马秀琳

    2015-01-01

    At present,many scholars pay more attention to the positive transfer of native language on the English learning,while ignoring the negative transfer of L1 on English grammar learning.Therefore native transfer of L1 often appears on English grammar learning.This paper aims to point out that the negative transfer of L1 has a profound and vast influence on the English grammar learning,to find out the countermeasures to reduce the influence of negative transfer of L1 and finally to bring the benefits to the following relative studies.

  9. HPV-16 L1 genes with inactivated negative RNA elements induce potent immune responses

    International Nuclear Information System (INIS)

    Rollman, Erik; Arnheim, Lisen; Collier, Brian; Oeberg, Daniel; Hall, Haakan; Klingstroem, Jonas; Dillner, Joakim; Pastrana, Diana V.; Buck, Chris B.; Hinkula, Jorma; Wahren, Britta; Schwartz, Stefan

    2004-01-01

    Introduction of point mutations in the 5' end of the human papillomavirus type 16 (HPV-16) L1 gene specifically inactivates negative regulatory RNA processing elements. DNA vaccination of C57Bl/6 mice with the mutated L1 gene resulted in improved immunogenicity for both neutralizing antibodies as well as for broad cellular immune responses. Previous reports on the activation of L1 by codon optimization may be explained by inactivation of the regulatory RNA elements. The modified HPV-16 L1 DNA that induced anti-HPV-16 immunity may be seen as a complementary approach to protein subunit immunization against papillomavirus

  10. Effect of Pt coverage in Pt-deposited Pd nanostructure electrodes on electrochemical properties

    Energy Technology Data Exchange (ETDEWEB)

    Park, Ah-Reum; Lee, Young-Woo; Kwak, Da-Hee; Park, Kyung-Won [Soongsil University, Seoul (Korea, Republic of)

    2015-06-15

    We have fabricated Pt-deposited Pd electrodes via a two-gun sputtering deposition system by separately operating Pd and Pt target as a function of sputtering time of Pt target. For Pt-deposited Pd electrodes (Pd/Pt-X), Pd were first deposited on the substrates at 20 W for 5min, followed by depositing Pt on the Pd-only electrodes as a function of sputtering time (X=1, 3, 5, 7, and 10min) at 20W on the Pt target. As the sputtering time of Pt target increased, the portion of Pt on the Pd electrodes increased, representing an increased coverage of Pt on the Pd electrodes. The Pd/Pt-7 electrode having an optimized Pt coverage exhibits an excellent electrocatalytic activity for methanol oxidation reaction.

  11. Templated assembly of Co-Pt nanoparticles via thermal and laser-induced dewetting of bilayer metal films.

    Science.gov (United States)

    Oh, Yong-Jun; Kim, Jung-Hwan; Thompson, Carl V; Ross, Caroline A

    2013-01-07

    Templated dewetting of a Co/Pt metal bilayer film on a topographic substrate was used to assemble arrays of Co-Pt alloy nanoparticles, with highly uniform particle size, shape and notably composition compared to nanoparticles formed on an untemplated substrate. Solid-state and liquid-state dewetting processes, using furnace annealing and laser irradiation respectively, were compared. Liquid state dewetting produced more uniform, conformal nanoparticles but they had a polycrystalline disordered fcc structure and relatively low magnetic coercivity. In contrast, solid state dewetting enabled formation of magnetically hard, ordered L1(0) Co-Pt single-crystal particles with coercivity >12 kOe. Furnace annealing converted the nanoparticles formed by liquid state dewetting into the L1(0) phase.

  12. Nephrogenic diabetes insipidus in a patient with L1 syndrome: a new report of a contiguous gene deletion syndrome including L1CAM and AVPR2.

    Science.gov (United States)

    Knops, Noël B B; Bos, Krista K; Kerstjens, Mieke; van Dael, Karin; Vos, Yvonne J

    2008-07-15

    We report on an infant boy with congenital hydrocephalus due to L1 syndrome and polyuria due to diabetes insipidus. We initially believed his excessive urine loss was from central diabetes insipidus and that the cerebral malformation caused a secondary insufficient pituitary vasopressin release. However, he failed to respond to treatment with a vasopressin analogue, which pointed to nephrogenic diabetes insipidus (NDI). L1 syndrome and X-linked NDI are distinct clinical disorders caused by mutations in the L1CAM and AVPR2 genes, respectively, located in adjacent positions in Xq28. In this boy we found a deletion of 61,577 basepairs encompassing the entire L1CAM and AVPR2 genes and extending into intron 7 of the ARHGAP4 gene. To our knowledge this is the first description of a patient with a deletion of these three genes. He is the second patient to be described with L1 syndrome and NDI. During follow-up he manifested complications from the hydrocephalus and NDI including global developmental delay and growth failure with low IGF-1 and hypothyroidism. 2008 Wiley-Liss, Inc.

  13. The Expression and Biological Significance of PD-L1 on Lung Cancer Cell Lines

    Directory of Open Access Journals (Sweden)

    Cheng CHEN

    2009-08-01

    Full Text Available Background and objective Tumor-associated PD-L1 expression was recently shown to promote T-cell apoptosis and proposed as a potential mechanism of immune evasion by tumors. On the basis of the ability of tumor-associated PD-L1 to mediate activated T-cell death, it is likely that manipulation of the PD-L1 pathway at defined time points during the development of the T-cell antitumor immune response can enhance the efficacy of T-cell-based immunotherapy. Here, the levels of expression of PD-L1 on lung cancer cell lines and its role in interaction of CTL and target cells was investigated. Methods Human PBMC derived DCs were loaded with apoptotic tumor cells and stimulated by CD40 mAb (5C11. Tumor specific CTL was generated in vitro by autologous T cells co-cultured with mature DCs. Expression of PD-L1 on lung cancer cell lines H1299 and A549 were analyzed by FCM. JAM assay was used to detect the cytolytic activity of CTL with or without blocking PD-L1 by PD-L1 mAb respectively. The concentrations of IFN-γ in supernatants from distinct groups were analyzed by ELISA. Results Tumor cells-loaded mature DCs could induce the generation of the tumor specific CTL. Expression of PD-L1 was low on A549 cell, but high on H1299 cell. Blockade of PD-L1 on A549 could not improve cytolytic effect of CTL on target cells and IFN-γ production, but fragmentation of H1299 cells and IFN-γ production were significantly enhanced by the combination of PD-L1 mAb and CTL. Conclusion Expression of PD-L1 on lung cancer cell line can decrease the cytolytic effect of CTL on target cells.

  14. The specificity and flexibility of l1 reverse transcription priming at imperfect T-tracts.

    Directory of Open Access Journals (Sweden)

    Clément Monot

    2013-05-01

    Full Text Available L1 retrotransposons have a prominent role in reshaping mammalian genomes. To replicate, the L1 ribonucleoprotein particle (RNP first uses its endonuclease (EN to nick the genomic DNA. The newly generated DNA end is subsequently used as a primer to initiate reverse transcription within the L1 RNA poly(A tail, a process known as target-primed reverse transcription (TPRT. Prior studies demonstrated that most L1 insertions occur into sequences related to the L1 EN consensus sequence (degenerate 5'-TTTT/A-3' sites and frequently preceded by imperfect T-tracts. However, it is currently unclear whether--and to which degree--the liberated 3'-hydroxyl extremity on the genomic DNA needs to be accessible and complementary to the poly(A tail of the L1 RNA for efficient priming of reverse transcription. Here, we employed a direct assay for the initiation of L1 reverse transcription to define the molecular rules that guide this process. First, efficient priming is detected with as few as 4 matching nucleotides at the primer 3' end. Second, L1 RNP can tolerate terminal mismatches if they are compensated within the 10 last bases of the primer by an increased number of matching nucleotides. All terminal mismatches are not equally detrimental to DNA extension, a C being extended at higher levels than an A or a G. Third, efficient priming in the context of duplex DNA requires a 3' overhang. This suggests the possible existence of additional DNA processing steps, which generate a single-stranded 3' end to allow L1 reverse transcription. Based on these data we propose that the specificity of L1 reverse transcription initiation contributes, together with the specificity of the initial EN cleavage, to the distribution of new L1 insertions within the human genome.

  15. Molecular identification of the ompL1 gene within Leptospira interrogans standard serovars.

    Science.gov (United States)

    Dezhbord, Mehrangiz; Esmaelizad, Majid; Khaki, Pejvak; Fotohi, Fariba; Zarehparvar Moghaddam, Athena

    2014-06-11

    Leptospirosis, caused by infection with pathogenic Leptospira species, is one of the most prevalent zoonotic diseases in the world. Current leptospiral vaccines are mainly multivalent dead whole-cell mixtures made of several local dominant serovars. Therefore, design and construction of an efficient recombinant vaccine for leptospirosis control is very important. OmpL1 is an immunogenic porin protein that could be of special significance in vaccination and serodiagnosis for leptospirosis. Three strains belonging to pathogenic L. interrogans were analyzed. The specific primers for proliferation of the ompL1 gene were designed. The amplified gene was cloned. In order to investigate the ompL1 nucleotide sequence and homological analysis of this gene, ompL1 genes cloned from standard vaccinal Leptospira serovars prevalent in Iran were sequenced and cloned. PCR amplification of the ompL1 gene using the designed primers resulted in a 963 bp ompL1 gene product. The PCR based on the ompL1 gene detected all pathogenic reference serovars of Leptospira spp. tested. Based on alignment and phylogenetic analysis, although the ompL1 nucleotide sequence was slightly different within three vaccinal serovars (100%-85% identity), amino acid alignment of the OmpL1 proteins revealed that there would be inconsiderable difference among them. The ompL1 gene of the three isolates was well conserved, differing only by a total of 6 bp and the proteins by 2 amino acids. The cloned gene could be further used for expression and recombinant OmpL1 as an efficient and conserved antigen, and may be a useful vaccine candidate against leptospirosis in our region.

  16. The specificity and flexibility of l1 reverse transcription priming at imperfect T-tracts.

    Science.gov (United States)

    Monot, Clément; Kuciak, Monika; Viollet, Sébastien; Mir, Ashfaq Ali; Gabus, Caroline; Darlix, Jean-Luc; Cristofari, Gaël

    2013-05-01

    L1 retrotransposons have a prominent role in reshaping mammalian genomes. To replicate, the L1 ribonucleoprotein particle (RNP) first uses its endonuclease (EN) to nick the genomic DNA. The newly generated DNA end is subsequently used as a primer to initiate reverse transcription within the L1 RNA poly(A) tail, a process known as target-primed reverse transcription (TPRT). Prior studies demonstrated that most L1 insertions occur into sequences related to the L1 EN consensus sequence (degenerate 5'-TTTT/A-3' sites) and frequently preceded by imperfect T-tracts. However, it is currently unclear whether--and to which degree--the liberated 3'-hydroxyl extremity on the genomic DNA needs to be accessible and complementary to the poly(A) tail of the L1 RNA for efficient priming of reverse transcription. Here, we employed a direct assay for the initiation of L1 reverse transcription to define the molecular rules that guide this process. First, efficient priming is detected with as few as 4 matching nucleotides at the primer 3' end. Second, L1 RNP can tolerate terminal mismatches if they are compensated within the 10 last bases of the primer by an increased number of matching nucleotides. All terminal mismatches are not equally detrimental to DNA extension, a C being extended at higher levels than an A or a G. Third, efficient priming in the context of duplex DNA requires a 3' overhang. This suggests the possible existence of additional DNA processing steps, which generate a single-stranded 3' end to allow L1 reverse transcription. Based on these data we propose that the specificity of L1 reverse transcription initiation contributes, together with the specificity of the initial EN cleavage, to the distribution of new L1 insertions within the human genome.

  17. Engineering Ru@Pt Core-Shell Catalysts for Enhanced Electrochemical Oxygen Reduction Mass Activity and Stability.

    Science.gov (United States)

    Jackson, Ariel; Strickler, Alaina; Higgins, Drew; Jaramillo, Thomas Francisco

    2018-01-12

    Improving the performance of oxygen reduction reaction (ORR) electrocatalysts is essential for the commercial efficacy of many renewable energy technologies, including low temperature polymer electrolyte fuel cells (PEFCs). Herein, we report highly active and stable carbon-supported Ru@Pt core-shell nanoparticles (Ru@Pt/C) prepared by a wet chemical synthesis technique. Through rotating disc electrode testing, the Ru@Pt/C achieves an ORR Pt mass-based activity of 0.50 A mg Pt -1 at 0.9 V versus the reversible hydrogen electrode (RHE), which exceeds the activity of the state-of-the-art commercial Pt/C catalyst as well as the Department of Energy 2020 PEFC electrocatalyst activity targets for transportation applications. The impact of various synthetic parameters, including Pt to Ru ratios and catalyst pretreatments (i.e., annealing) are thoroughly explored. Pt-based mass activity of all prepared Ru@Pt/C catalysts was found to exceed 0.4 mg Pt -1 across the range of compositions investigated, with the maximum activity catalyst having a Ru:Pt ratio of 1:1. This optimized composition of Ru@Pt/C catalyst demonstrated remarkable stability after 30,000 accelerated durability cycles (0.6 to 1.0 V vs. RHE at 125 mV s -1 ), maintaining 85% of its initial mass activity. Scanning transmission electron microscopy energy dispersive spectroscopy (STEM-EDS) analysis at various stages of electrochemical testing demonstrated that the Pt shell can provide sufficient protection against the dissolution of the otherwise unstable Ru core.

  18. Gram-Scale Synthesis of Highly Active and Durable Octahedral PtNi Nanoparticle Catalysts for Proton Exchange Membrane Fuel Cell

    DEFF Research Database (Denmark)

    Choi, Juhyuk; Jang, Jue-Hyuk; Roh, Chi-Woo

    2018-01-01

    for the commercialization of PEMFCs. In this study, we focus on gram-scale synthesis of octahedral PtNi nanoparticles with Pt overlayers (PtNi@Pt) supported on the carbon, resulting in enhanced catalytic activity and durability. Such PtNi@Pt catalysts show high mass activity (1.24 A mgPt−1) at 0.9 V (vs RHE) for the ORR......Proton exchange membrane fuel cells (PEMFC) are regarded as a promising renewable energy source for a future hydrogen energy society. However, highly active and durable catalysts are required for the PEMFCs because of their intrinsic high overpotential at the cathode and operation under the acidic...... condition for oxygen reduction reaction (ORR). Since the discovery of the exceptionally high surface activity of Pt3Ni(111), the octahedral PtNi nanoparticles have been synthesized and tested. Nonetheless, their milligram-scale synthesis method and poor durability make them unsuitable...

  19. Avelumab, an anti-PD-L1 antibody, in patients with locally advanced or metastatic breast cancer: a phase 1b JAVELIN Solid Tumor study.

    Science.gov (United States)

    Dirix, Luc Y; Takacs, Istvan; Jerusalem, Guy; Nikolinakos, Petros; Arkenau, Hendrik-Tobias; Forero-Torres, Andres; Boccia, Ralph; Lippman, Marc E; Somer, Robert; Smakal, Martin; Emens, Leisha A; Hrinczenko, Borys; Edenfield, William; Gurtler, Jayne; von Heydebreck, Anja; Grote, Hans Juergen; Chin, Kevin; Hamilton, Erika P

    2018-02-01

    Agents targeting programmed death receptor 1 (PD-1) or its ligand (PD-L1) have shown antitumor activity in the treatment of metastatic breast cancer (MBC). The aim of this study was to assess the activity of avelumab, a PD-L1 inhibitor, in patients with MBC. In a phase 1 trial (JAVELIN Solid Tumor; NCT01772004), patients with MBC refractory to or progressing after standard-of-care therapy received avelumab intravenously 10 mg/kg every 2 weeks. Tumors were assessed every 6 weeks by RECIST v1.1. Adverse events (AEs) were graded by NCI-CTCAE v4.0. Membrane PD-L1 expression was assessed by immunohistochemistry (Dako PD-L1 IHC 73-10 pharmDx). A total of 168 patients with MBC, including 58 patients with triple-negative breast cancer (TNBC), were treated with avelumab for 2-50 weeks and followed for 6-15 months. Patients were heavily pretreated with a median of three prior therapies for metastatic or locally advanced disease. Grade ≥ 3 treatment-related AEs occurred in 13.7% of patients, including two treatment-related deaths. The confirmed objective response rate (ORR) was 3.0% overall (one complete response and four partial responses) and 5.2% in patients with TNBC. A trend toward a higher ORR was seen in patients with PD-L1+ versus PD-L1- tumor-associated immune cells in the overall population (16.7% vs. 1.6%) and in the TNBC subgroup (22.2% vs. 2.6%). Avelumab showed an acceptable safety profile and clinical activity in a subset of patients with MBC. PD-L1 expression in tumor-associated immune cells may be associated with a higher probability of clinical response to avelumab in MBC.

  20. Structural and magnetic properties of FePt nanoparticles from the gas phase; Strukturelle und magnetische Eigenschaften von FePt-Nanopartikeln aus der Gasphase

    Energy Technology Data Exchange (ETDEWEB)

    Dmitrieva, O.

    2007-09-21

    In this work, we present the structural and magnetic characterization of FePt nanoparticles. The nanoparticles with mean size of about 6 nm were prepared by sputtering in the gas and subsequent inert gas condensation. The particles are annealed in the furnace during their flight prior to deposition on a substrate. The aim of this work is to prepare magnetically hard FePt nanoparticles in the L1{sub 0}-ordered phase. The structure of the particles was investigated by high-resolution transmission electron microscopy, and the investigations were supported by contrast simulations. The morphology of the particles varies with the sputter-gas pressure and with the annealing temperature. At a pressure of 0.5 mbar, the FePt-nanoparticles are multiply-twinned with an icosahedral structure and exhibit no formation of the L1{sub 0}-ordered phase. At a higher pressure of 1 mbar and an annealing temperature of 1000 C, the particles are partially single-crystalline. About 36 % of the particles are found to be in the L1{sub 0}-ordered state as was estimated by statistical counting supported by simulations. In order to activate the volume diffusion in the particles and to stabilize the formation of the L1{sub 0}-ordered state, the addition of nitrogen was used during the sputtering phase. In this phase, atomic nitrogen is incorporated interstitially into the structure of the primary particles. After annealing nitrogen effuses out of the particles and, thereby, increases the volume diffusion of the Fe and Pt atoms. The incorporation of nitrogen atoms during nucleation and their effusion at an annealing temperature of 1000 C was verified by electron energy loss spectroscopy (EELS) and X-ray absorption spectroscopy (XAS). Structural investigations on particles prepared in the presence of nitrogen shows that most of the particles are single-crystalline and about 70 % of them are L1{sub 0}-ordered. Detailed structural analysis of the nanoparticles was done by the exit wave

  1. A canine chimeric monoclonal antibody targeting PD-L1 and its clinical efficacy in canine oral malignant melanoma or undifferentiated sarcoma.

    Science.gov (United States)

    Maekawa, Naoya; Konnai, Satoru; Takagi, Satoshi; Kagawa, Yumiko; Okagawa, Tomohiro; Nishimori, Asami; Ikebuchi, Ryoyo; Izumi, Yusuke; Deguchi, Tatsuya; Nakajima, Chie; Kato, Yukinari; Yamamoto, Keiichi; Uemura, Hidetoshi; Suzuki, Yasuhiko; Murata, Shiro; Ohashi, Kazuhiko

    2017-08-21

    Immunotherapy targeting immune checkpoint molecules, programmed cell death 1 (PD-1) and PD-ligand 1 (PD-L1), using therapeutic antibodies has been widely used for some human malignancies in the last 5 years. A costimulatory receptor, PD-1, is expressed on T cells and suppresses effector functions when it binds to its ligand, PD-L1. Aberrant PD-L1 expression is reported in various human cancers and is considered an immune escape mechanism. Antibodies blocking the PD-1/PD-L1 axis induce antitumour responses in patients with malignant melanoma and other cancers. In dogs, no such clinical studies have been performed to date because of the lack of therapeutic antibodies that can be used in dogs. In this study, the immunomodulatory effects of c4G12, a canine-chimerised anti-PD-L1 monoclonal antibody, were evaluated in vitro, demonstrating significantly enhanced cytokine production and proliferation of dog peripheral blood mononuclear cells. A pilot clinical study was performed on seven dogs with oral malignant melanoma (OMM) and two with undifferentiated sarcoma. Objective antitumour responses were observed in one dog with OMM (14.3%, 1/7) and one with undifferentiated sarcoma (50.0%, 1/2) when c4G12 was given at 2 or 5 mg/kg, every 2 weeks. c4G12 could be a safe and effective treatment option for canine cancers.

  2. Preparation of Fe-Pt perpendicular double-layered media with high electric resistivity backlayer

    International Nuclear Information System (INIS)

    Uchida, Masaru; Suzuki, Toshio; Ouchi, Kazuhiro

    2001-01-01

    High electric resistivity materials, oxide-added Fe-Si, were investigated as a soft-magnetic backlayer for Fe-Pt perpendicular double-layered media. It was found that there is a possibility of using (Fe-Si)-MgO as a backlayer. To promote a hetero-epitaxial growth of ordered Fe-Pt FCT(0 0 1), the backlayer needed a BCC(2 0 0) crystal orientation, in a situation where surface topology also played an important role

  3. Complete Genome Sequence of Bacillus velezensis L-1, Which Has Antagonistic Activity against Pear Diseases

    OpenAIRE

    Sun, Pingping; Cui, Jianchao; Jia, Xiaohui; Wang, Wenhui

    2017-01-01

    ABSTRACT Bacillus velezensis L-1 is an effective biocontrol agent against pear diseases. Here, we report the complete genome sequence of B. velezensis L-1 in which clusters related to the biosynthesis of secondary metabolites were predicted. This genome provides insights into the possible biocontrol mechanisms and furthers application of this specific bacterium.

  4. Complete Genome Sequence of Bacillus velezensis L-1, Which Has Antagonistic Activity against Pear Diseases.

    Science.gov (United States)

    Sun, Pingping; Cui, Jianchao; Jia, Xiaohui; Wang, Wenhui

    2017-11-30

    Bacillus velezensis L-1 is an effective biocontrol agent against pear diseases. Here, we report the complete genome sequence of B. velezensis L-1 in which clusters related to the biosynthesis of secondary metabolites were predicted. This genome provides insights into the possible biocontrol mechanisms and furthers application of this specific bacterium. Copyright © 2017 Sun et al.

  5. Structural basis of a novel PD-L1 nanobody for immune checkpoint blockade.

    Science.gov (United States)

    Zhang, Fei; Wei, Hudie; Wang, Xiaoxiao; Bai, Yu; Wang, Pilin; Wu, Jiawei; Jiang, Xiaoyong; Wang, Yugang; Cai, Haiyan; Xu, Ting; Zhou, Aiwu

    2017-01-01

    The use of antibodies to target immune checkpoints, particularly PD-1/PD-L1, has made a profound impact in the field of cancer immunotherapy. Here, we identified KN035, an anti-PD-L1 nanobody that can strongly induce T-cell responses and inhibit tumor growth. The crystal structures of KN035 complexed with PD-L1 and free PD-L1, solved here at 1.7 and 2.7 Å resolution, respectively, show that KN035 competes with PD-1 (programmed death protein 1) for the same flat surface on PD-L1, mainly through a single surface loop of 21 amino acids. This loop forms two short helices and develops key hydrophobic and ionic interactions with PD-L1 residues, such as Ile54, Tyr56 and Arg113, which are also involved in PD-1 binding. The detailed mutagenesis study identified the hotspot residues of the PD-L1 surface and provides an explanation for the stronger (~1 000-fold) binding of KN035 to PD-L1 than PD-1 and its lack of binding to PD-L2. Overall, this study reveals how a single immunoglobulin-variable scaffold of KN035 or PD-1 can bind to a flat protein surface through either a single surface loop or beta-sheet strands; and provides a basis for designing new immune checkpoint blockers and generating bi-specific antibodies for combination therapy.

  6. [Regulatory Mechanisms of PD-L1 Expression and Its Role in Immune Evasion].

    Science.gov (United States)

    Kataoka, Keisuke

    2017-11-01

    Immune checkpoint blockade therapy using anti-PD-1 or anti-PD-L1 antibodies can unleash anti-tumor immunity and induce durable remission in a variety ofhuman cancers. However, the regulatory mechanisms of PD-L1 expression mediating immune evasion ofcancer cells have not been fully elucidated, including the genetic alterations causing PD-L1 overexpression. Recently, we have reported a novel genetic mechanism ofimmune evasion associated with structural variations(SVs)disrupting the 3'-untranslated region(UTR)ofthe PD-L1 gene in various malignancies, such as aggressive lymphomas and gastrointestinal cancers. Despite a heterogenous nature ofthese SVs, they are closely associated with a marked upregulation of PD-L1 expression, which augments tumor growth and escape from anti-tumor immunity. Here we present an overview of the regulatory mechanisms of PD-L1 expression in cancer cells, highlighting the genetic mechanisms of PD-L1 constitutive activation, with specific focus on PD-L1 3'-UTR disruption.

  7. Regulation of synaptic structure by ubiquitin C-terminal hydrolase L1.

    Science.gov (United States)

    Cartier, Anna E; Djakovic, Stevan N; Salehi, Afshin; Wilson, Scott M; Masliah, Eliezer; Patrick, Gentry N

    2009-06-17

    Ubiquitin C-terminal hydrolase L1 (UCH-L1) is a deubiquitinating enzyme that is selectively and abundantly expressed in the brain, and its activity is required for normal synaptic function. Here, we show that UCH-L1 functions in maintaining normal synaptic structure in hippocampal neurons. We found that UCH-L1 activity is rapidly upregulated by NMDA receptor activation, which leads to an increase in the levels of free monomeric ubiquitin. Conversely, pharmacological inhibition of UCH-L1 significantly reduces monomeric ubiquitin levels and causes dramatic alterations in synaptic protein distribution and spine morphology. Inhibition of UCH-L1 activity increases spine size while decreasing spine density. Furthermore, there is a concomitant increase in the size of presynaptic and postsynaptic protein clusters. Interestingly, however, ectopic expression of ubiquitin restores normal synaptic structure in UCH-L1-inhibited neurons. These findings point to a significant role of UCH-L1 in synaptic remodeling, most likely by modulating free monomeric ubiquitin levels in an activity-dependent manner.

  8. L1-L2 Transfer in the Narrative Styles of Chinese EFL Learners' Written Personal Narratives

    Science.gov (United States)

    Su, I-Ru; Chou, Yi-Chun

    2016-01-01

    Most of the research on second language (L2) narratives has focused on whether or how L2 learners carry their L1 narrative styles into L2 narration; few studies have explored whether L2 learners' knowledge of the L2 also in turn affects their L1 narrative performance. The present study attempted to probe the issue of cultural transfer in narrative…

  9. L1 Differences and L2 Similarities: Teaching Verb Tenses in English

    Science.gov (United States)

    Collins, Laura

    2007-01-01

    In making decisions regarding the focus for grammar teaching, ESL instructors may take into consideration errors that appear to result from the influence of their students' first language(s) (L1). There is also evidence from language acquisition research suggesting that for some grammatical features, learners of different L1 backgrounds may face…

  10. L1 and L2 Strategy Use in Reading Comprehension of Chinese EFL Readers

    Science.gov (United States)

    Tsai, Yea-Ru; Ernst, Cheryl; Talley, Paul C.

    2010-01-01

    This study revealed the relationship between L1 (Mandarin Chinese) and L2 (English) strategy use in L2 reading comprehension by focusing on the correlation of L1 reading ability, L2 proficiency and employed reading strategies. The participants, 222 undergraduates learning English as a foreign language (EFL), were classified into skilled and…

  11. Modeling of the structure of ribosomal protein L1 from the archaeon Haloarcula marismortui

    Science.gov (United States)

    Nevskaya, N. A.; Kljashtorny, V. G.; Vakhrusheva, A. V.; Garber, M. B.; Nikonov, S. V.

    2017-07-01

    The halophilic archaeon Haloarcula marismortui proliferates in the Dead Sea at extremely high salt concentrations (higher than 3 M). This is the only archaeon, for which the crystal structure of the ribosomal 50S subunit was determined. However, the structure of the functionally important side protuberance containing the abnormally negatively charged protein L1 (HmaL1) was not visualized. Attempts to crystallize HmaL1 in the isolated state or as its complex with RNA using normal salt concentrations (≤500 mM) failed. A theoretical model of HmaL1 was built based on the structural data for homologs of the protein L1 from other organisms, and this model was refined by molecular dynamics methods. Analysis of this model showed that the protein HmaL1 can undergo aggregation due to the presence of a cluster of positive charges unique for proteins L1. This cluster is located at the RNA-protein interface, which interferes with the crystallization of HmaL1 and the binding of the latter to RNA.

  12. L2 Word Recognition: Influence of L1 Orthography on Multi-Syllabic Word Recognition

    Science.gov (United States)

    Hamada, Megumi

    2017-01-01

    L2 reading research suggests that L1 orthographic experience influences L2 word recognition. Nevertheless, the findings on multi-syllabic words in English are still limited despite the fact that a vast majority of words are multi-syllabic. The study investigated whether L1 orthography influences the recognition of multi-syllabic words, focusing on…

  13. X-linked hydrocephalus : A novel missense mutation in the L1CAM gene

    NARCIS (Netherlands)

    Sztriha, L; Vos, YJ; Verlind, E; Johansen, J; Berg, B

    2002-01-01

    X-linked hydrocephalus is associated with mutations in the L1 neuronal cell adhesion molecule gene. L1 protein plays a key role in neurite outgrowth, axonal guidance, and pathfinding during the development of the nervous system. A male is described with X-linked hydrocephalus who had multiple small

  14. Equilibrium and stability of high-beta plasma in a finite l=+-1 toroidal system

    International Nuclear Information System (INIS)

    Shiina, S.; Saito, K.; Todoroki, J.; Hamada, S.; Gesso, H.; Nogi, Y.; Osanai, Y.; Yoshimura, H.

    1983-01-01

    The equilibrium and stability are theoretically and experimentally investigated of high-beta plasma in the Modified Bumpy Torus, which is an asymmetric closed-line system with fairly large l=0 and l=+-1 field components. The finiteness of the l=+-1 component induces significant stabilizing effects due both to self formation of a magnetic well and to the conducting wall. (author)

  15. The Status of the Auxiliary "Do" in L1 and L2 English Negative Clauses

    Science.gov (United States)

    Perales, Susana

    2010-01-01

    This paper addresses the issue of whether negative sentences containing auxiliary "do" in L1 and L2 English share the same underlying syntactic representation. To this end, I compare the negative sentences produced by 77 bilingual (Spanish/Basque) L2 learners of English with the corresponding data available for L1 acquirers reported on in Schutze…

  16. Ternary Weighted Function and Beurling Ternary Banach Algebra l1ω(S

    Directory of Open Access Journals (Sweden)

    Mehdi Dehghanian

    2011-01-01

    Full Text Available Let S be a ternary semigroup. In this paper, we introduce our notation and prove some elementary properties of a ternary weight function ω on S. Also, we make ternary weighted algebra l1ω(S and show that l1ω(S is a ternary Banach algebra.

  17. CDC91L1 (PIG-U) is a newly discovered oncogene in human bladder cancer.

    NARCIS (Netherlands)

    Guo, Z.; Linn, J.F.; Wu, G.; Anzick, S.L.; Eisenberger, C.F.; Halachmi, S.; Cohen, Y.; Fomenkov, A.; Hoque, M.O.; Okami, K.; Steiner, G.; Engles, J.M.; Osada, M.; Moon, C.; Ratovitski, E.; Trent, J.M.; Meltzer, P.S.; Westra, W.H.; Kiemeney, L.A.L.M.; Schoenberg, M.P.; Sidransky, D.; Trink, B.

    2004-01-01

    Genomic amplification at 20q11-13 is a common event in human cancers. We isolated a germline translocation breakpoint at 20q11 from a bladder cancer patient. We identified CDC91L1, the gene encoding CDC91L1 (also called phosphatidylinositol glycan class U (PIG-U), a transamidase complex unit in the

  18. Enhanced spatial resolution in fluorescence molecular tomography using restarted L1-regularized nonlinear conjugate gradient algorithm.

    Science.gov (United States)

    Shi, Junwei; Liu, Fei; Zhang, Guanglei; Luo, Jianwen; Bai, Jing

    2014-04-01

    Owing to the high degree of scattering of light through tissues, the ill-posedness of fluorescence molecular tomography (FMT) inverse problem causes relatively low spatial resolution in the reconstruction results. Unlike L2 regularization, L1 regularization can preserve the details and reduce the noise effectively. Reconstruction is obtained through a restarted L1 regularization-based nonlinear conjugate gradient (re-L1-NCG) algorithm, which has been proven to be able to increase the computational speed with low memory consumption. The algorithm consists of inner and outer iterations. In the inner iteration, L1-NCG is used to obtain the L1-regularized results. In the outer iteration, the restarted strategy is used to increase the convergence speed of L1-NCG. To demonstrate the performance of re-L1-NCG in terms of spatial resolution, simulation and physical phantom studies with fluorescent targets located with different edge-to-edge distances were carried out. The reconstruction results show that the re-L1-NCG algorithm has the ability to resolve targets with an edge-to-edge distance of 0.1 cm at a depth of 1.5 cm, which is a significant improvement for FMT.

  19. Code-Switching: L1-Coded Mediation in a Kindergarten Foreign Language Classroom

    Science.gov (United States)

    Lin, Zheng

    2012-01-01

    This paper is based on a qualitative inquiry that investigated the role of teachers' mediation in three different modes of coding in a kindergarten foreign language classroom in China (i.e. L2-coded intralinguistic mediation, L1-coded cross-lingual mediation, and L2-and-L1-mixed mediation). Through an exploratory examination of the varying effects…

  20. L1 effects on the processing of grammatical gender in L2

    NARCIS (Netherlands)

    Sabourin, L; Foster-Cohen, S.; Nizegorodcew, A.

    2001-01-01

    This paper explores L1 effects on the L2 off-line processing of Dutch (grammatical gender) agreement The L2 participants had either German, English or a Romance language as their L1. Non-gender agreement (finiteness and agreement) was tested to ascertain the level of proficiency of the participants

  1. L1 and L2 Distance Effects in Learning L3 Dutch

    Science.gov (United States)

    Schepens, Job J.; der Slik, Frans; Hout, Roeland

    2016-01-01

    Many people speak more than two languages. How do languages acquired earlier affect the learnability of additional languages? We show that linguistic distances between speakers' first (L1) and second (L2) languages and their third (L3) language play a role. Larger distances from the L1 to the L3 and from the L2 to the L3 correlate with lower…

  2. Heterologous production of human papillomavirus type-16 L1 protein by a lactic acid bacterium

    Directory of Open Access Journals (Sweden)

    Bermúdez-Humarán Luis G

    2009-08-01

    Full Text Available Abstract Background The expression of vaccine antigens in lactic acid bacteria (LAB is a safe and cost-effective alternative to traditional expression systems. In this study, we investigated i the expression of Human papillomavirus type 16 (HPV-16 L1 major capsid protein in the model LAB Lactococcus lactis and ii the ability of the resulting recombinant strain to produce either capsomer-or virus-like particles (VLPs. Results and conclusion HPV-16 L1 gene was cloned into two vectors, pCYT and pSEC, designed for controlled intra- or extracellular heterologous expression in L. lactis, respectively. The capacity of L. lactis harboring either pCYT:L1 or pSEC:L1 plasmid to accumulate L1 in the cytoplasm and supernatant samples was confirmed by Western blot assays. Electron microscopy analysis suggests that, L1 protein produced by recombinant lactococci can self-assemble into structures morphologically similar to VLPs intracellularly. The presence of conformational epitopes on the L. lactis-derived VLPs was confirmed by ELISA using an anti-HPV16 L1 capsid antigen antibody. Our results support the feasibility of using recombinant food-grade LAB, such as L. lactis, for the production of L1-based VLPs and open the possibility for the development of a new safe mucosal vector for HPV-16 prophylactic vaccination.

  3. Exonization of active mouse L1s: a driver of transcriptome evolution?

    Directory of Open Access Journals (Sweden)

    Badge Richard

    2007-10-01

    Full Text Available Abstract Background Long interspersed nuclear elements (LINE-1s, L1s have been recently implicated in the regulation of mammalian transcriptomes. Results Here, we show that members of the three active mouse L1 subfamilies (A, GF and TF contain, in addition to those on their sense strands, conserved functional splice sites on their antisense strands, which trigger multiple exonization events. The latter is particularly intriguing in the light of the strong antisense orientation bias of intronic L1s, implying that the toleration of antisense insertions results in an increased potential for exonization. Conclusion In a genome-wide analysis, we have uncovered evidence suggesting that the mobility of the large number of retrotransposition-competent mouse L1s (~2400 potentially active L1s in NCBIm35 has significant potential to shape the mouse transcriptome by continuously generating insertions into transcriptional units.

  4. Identification of CREB3L1 as a Biomarker Predicting Doxorubicin Treatment Outcome.

    Directory of Open Access Journals (Sweden)

    Bray Denard

    Full Text Available Doxorubicin has been shown to inhibit proliferation of cancer cells through proteolytic activation of CREB3L1 (cAMP response element binding protein 3-like 1, a transcription factor synthesized as a membrane-bound precursor. Upon doxorubicin treatment, CREB3L1 is cleaved so that the N-terminal domain of the protein can reach the nucleus where it activates transcription of genes that inhibit cell proliferation. These results suggest that the level of CREB3L1 in cancer cells may determine their sensitivity to doxorubicin.Mice transplanted with 6 lines of renal cell carcinoma (RCC were injected with doxorubicin to observe the effect of the chemotherapy on tumor growth. Immunohistochemistry and bioinformatics analyses were performed to compare CREB3L1 levels in types of cancer known to respond to doxorubicin versus those resistant to doxorubicin.Higher levels of CREB3L1 protein are correlated with increased doxorubicin sensitivity of xenograft RCC tumors (p = 0.017 by Pearson analysis. From patient tumor biopsies we analyzed, CREB3L1 was expressed in 19% of RCC, which is generally resistant to doxorubicin, but in 70% of diffuse large B-cell lymphoma that is sensitive to doxorubicin. Doxorubicin is used as the standard treatment for cancers that express the highest levels of CREB3L1 such as osteosarcoma and malignant fibrous histiocytoma but is not generally used to treat those that express the lowest levels of CREB3L1 such as RCC.Identification of CREB3L1 as the biomarker for doxorubicin sensitivity may markedly improve the doxorubicin response rate by applying doxorubicin only to patients with cancers expressing CREB3L1.

  5. PD-L1 expression associated with worse survival outcome in malignant pleural mesothelioma.

    Science.gov (United States)

    Nguyen, Bella Hai; Montgomery, Renn; Fadia, Mitali; Wang, Jiali; Ali, Sayed

    2018-02-01

    There is currently a need to identify prognostic biomarkers to assist in a risk adopted approach in treatment of malignant pleural mesothelioma (MPM). Expression of programmed death ligand 1 (PD-L1) has been studied as a prognostic biomarker in a number of tumors given its central role in antitumoral immune response evasion. Four previously published analyses found PD-L1 positivity to be an adverse survival prognostic factor in MPM. This study aims to further investigate the relationship between PD-L1 expression in mesothelioma tissues and survival outcome. Clinical data of MPM patients from a single institution between 2006 and 2016 were reviewed. Patient's archived tissues were stained with PD-L1 (Clone Ventana SP263). PD-L1 positivity was defined as > 1% membranous staining regardless of intensity. Data from fifty eight patients were analyzed. Median age was 73, majority was male (49, 84%) and had ECOG between 0 and 2 (46, 79%). Most common histopathological subtype was epithelioid (42, 72%), 9 (16%) biphasic subtype and 7 (12%) sarcomatoid. Thirty one patients (53%) received best supportive care and twenty seven patients (47%) received chemotherapy or combination treatment. Forty-two patients had positive PD-L1 expression (72.4%). The median survival time for PD-L1 negative group is 15.5 months and 6 months for the positive group. Positive PD-L1 expression is independently correlated with worse prognosis (HR = 2.02; 95% CI, 1.005-4.057; P-value = 0.0484). Our analysis found a higher percentage of MPM patients with positive PD-L1 (> 1%) compared to other studies. Highly positive PD-L1 expression was associated with statistically significantly lower median survival time. © 2017 John Wiley & Sons Australia, Ltd.

  6. Ab-initio study of the coadsorption of Li and H on Pt(001), Pt(110) and Pt(111) surfaces

    Energy Technology Data Exchange (ETDEWEB)

    Saad, Farida [Laboratoire de Physique et Chimie Quantique, Faculte des Sciences, Universite Mouloud Mammeri, 15000 Tizi-Ouzou (Algeria); Zemirli, Mourad, E-mail: zemirlimourad@mail.ummto.dz [Laboratoire de Physique et Chimie Quantique, Faculte des Sciences, Universite Mouloud Mammeri, 15000 Tizi-Ouzou (Algeria); Benakki, Mouloud; Bouarab, Said [Laboratoire de Physique et Chimie Quantique, Faculte des Sciences, Universite Mouloud Mammeri, 15000 Tizi-Ouzou (Algeria)

    2012-02-15

    The coadsorption of Li and H atoms on Pt(001), Pt(110) and Pt(111) surfaces is studied using density functional theory with generalised gradient approximation. In all calculations Li, H and the two topmost layers of the metal were allowed to relax. At coverage of 0.25 mono-layer in a p(2 Multiplication-Sign 2) unit cell, lithium adsorption at the hollow site for the three surfaces is favoured over top and bridge sites. The most favoured adsorption sites for H atom on the Pt(001) and Pt(110) surfaces are the top and bridge sites, while on Pt(111) surface the fcc site appears to be slightly favoured over the hcp site. The coadsorption of Li and atomic hydrogen shows that the interaction between the two adsorbates is stabilising when they are far from each other. The analysis of Li, H and Pt local density of states shows that Li strongly interacts with the Pt surfaces.

  7. A dual-type responsive electrochemical immunosensor for quantitative detection of PCSK9 based on n-C60-PdPt/N-GNRs and Pt-poly (methylene blue) nanocomposites.

    Science.gov (United States)

    Li, Yan; He, Junlin; Chen, Jun; Niu, Yazhen; Zhao, Yilin; Zhang, Yuchan; Yu, Chao

    2018-03-15

    In this study, a dual-type responsive electrochemical immunosensor was developed for the quantitative detection of proprotein convertase subtilisin/kexin type 9 (PCSK9), a potential biomarker of cardiovascular disease in serum. N-doped graphene nanoribbons (N-GNRs) with good conductivity were used as the sensing matrix modifying the glassy carbon electrode. Palladium platinum alloy (PdPt) nanoparticles with high catalytic performance toward the reduction of hydrogen peroxide (H 2 O 2 ) were reduced onto amino-functionalized fullerene (n-C 60 -PdPt) and significantly amplified the electrochemical signal recorded by the amperometric i-t curve. Furthermore, staphylococcus protein A (SPA) with antibody orientation function was introduced to improve the immunoreaction efficiency. Accordingly, a label-free immunosensor was fabricated based on n-C 60 -PdPt/N-GNRs for the quick detection of PCSK9. Meanwhile, to realize ultrasensitive detection of PCSK9, Pt-poly (methylene blue) (Pt-PMB) nanocomposites synthesized by a one-pot method for the first time were used as a novel signal label, which exhibited uniform morphology as well as good conductivity and produced an electrochemical signal recorded by differential pulse voltammetry (DPV). Herein, a novel sandwich-type immunosensor was designed using n-C 60 -PdPt/N-GNRs as the sensing matrix and Pt-PMB as the signal label for sensitive detection of PCSK9. Under optimal conditions, the label-free immunosensor showed a linear range of 10pgmL -1 to 100ngmL -1 with a detection limit of 3.33pgmL -1 (S/N=3), and the sandwich-type immunosensor exhibited a linear range of 100 fg mL -1 to 100ngmL -1 with a detection limit of 0.033pgmL -1 (S/N=3) for PCSK9 detection, indicating its potential application in clinical bioassay analysis. Copyright © 2017 Elsevier B.V. All rights reserved.

  8. Vaccine potential of recombinant cathepsinL1G against Fasciola gigantica in mice.

    Science.gov (United States)

    Changklungmoa, Narin; Phoinok, Natthacha; Yencham, Chonthicha; Sobhon, Prasert; Kueakhai, Pornanan

    2016-08-15

    In this study, we characterized and investigated the vaccine potential of FgCatL1G against Fasciola gigantica infection in mice. Recombinant mature FgCatL1G (rmFgCatL1G) was expressed in Escherichia coli BL21. The vaccination was performed in Imprinting Control Region (ICR) mice (n=10) by subcutaneous injection with 50μg of rmFgCatL1G combined with Freund's adjuvant. Two weeks after the second boost, mice were infected with 15 metacercariae by the oral route. The percents of protection of rmFgCatL1G vaccine were estimated to be 56.5% and 58.3% when compared with non vaccinated-infected and adjuvant-infected controls, respectively. Antibodies in the immune sera of vaccinated mice were shown by immunoblot to react with the native FgCatL1s in the extract of all stages of parasites and rmFgCatL1H, recombinant pro - FgCatL1 (rpFgCatL1). By immunohistochemistry, the immune sera also reacted with FgCatL1s in the caecal epithelial cells of the parasites. The levels of IgG1 and IgG2a in the immune sera, which are indicative of Th2 and Th1 immune responses, were also increased with IgG1 predominating. The levels of serum glutamic oxaloacetic transaminase (SGOT) and serum glutamic pyruvic transaminase (SGPT) in rmFgCatL1G-immunized group showed no significant difference from the control groups, but pathological lesions of livers in rmFgCatL1G-immunized group showed significant decrease when compared to the control groups. This study indicates that rmFgCatL1G has a vaccine potential against F. gigantica in mice, and this potential will be tested in larger livestock animals. Copyright © 2016 Elsevier B.V. All rights reserved.

  9. Small-Molecule Sigma1 Modulator Induces Autophagic Degradation of PD-L1.

    Science.gov (United States)

    Maher, Christina M; Thomas, Jeffrey D; Haas, Derick A; Longen, Charles G; Oyer, Halley M; Tong, Jane Y; Kim, Felix J

    2018-02-01

    Emerging evidence suggests that Sigma1 ( SIGMAR1 , also known as sigma-1 receptor) is a unique ligand-regulated integral membrane scaffolding protein that contributes to cellular protein and lipid homeostasis. Previously, we demonstrated that some small-molecule modulators of Sigma1 alter endoplasmic reticulum (ER)-associated protein homeostasis pathways in cancer cells, including the unfolded protein response and autophagy. Programmed death-ligand 1 (PD-L1) is a type I integral membrane glycoprotein that is cotranslationally inserted into the ER and is processed and transported through the secretory pathway. Once at the surface of cancer cells, PD-L1 acts as a T-cell inhibitory checkpoint molecule and suppresses antitumor immunity. Here, we demonstrate that in Sigma1-expressing triple-negative breast and androgen-independent prostate cancer cells, PD-L1 protein levels were suppressed by RNAi knockdown of Sigma1 and by small-molecule inhibition of Sigma1. Sigma1-mediated action was confirmed by pharmacologic competition between Sigma1-selective inhibitor and activator ligands. When administered alone, the Sigma1 inhibitor decreased cell surface PD-L1 expression and suppressed functional interaction of PD-1 and PD-L1 in a coculture of T cells and cancer cells. Conversely, the Sigma1 activator increased PD-L1 cell surface expression, demonstrating the ability to positively and negatively modulate Sigma1 associated PD-L1 processing. We discovered that the Sigma1 inhibitor induced degradation of PD-L1 via autophagy, by a mechanism distinct from bulk macroautophagy or general ER stress-associated autophagy. Finally, the Sigma1 inhibitor suppressed IFNγ-induced PD-L1. Our data demonstrate that small-molecule Sigma1 modulators can be used to regulate PD-L1 in cancer cells and trigger its degradation by selective autophagy. Implications: Sigma1 modulators sequester and eliminate PD-L1 by autophagy, thus preventing functional PD-L1 expression at the cell surface. This

  10. Multiple oxide content media for columnar grain growth in L10 FePt thin films

    International Nuclear Information System (INIS)

    Ho, Hoan; Yang, En; Laughlin, David E.; Zhu, Jian-Gang

    2013-01-01

    An approach to enhance the height-to-diameter ratio of FePt grains in heat-assisted magnetic recording media is proposed. The FePt-SiO x thin films are deposited with a decrease of the SiO x percentage along the film growth direction. When bi-layer and tri-layer media are sputtered at 410 °C, we observe discontinuities in the FePt grains at interfaces between layers, which lead to poor epitaxial growth. Due to increased atomic diffusion, the bi-layer media sputtered at 450 °C is shown to (1) grow into continuous columnar grains with similar size as single-layer media but much higher aspect ratio, (2) have better L1 0 ordering and larger coercivity.

  11. rno-miR-665 targets BCL2L1 (Bcl-xl) and increases vulnerability to propofol in developing astrocytes.

    Science.gov (United States)

    Sun, Wen-Chong; Pei, Ling

    2016-07-01

    Propofol exerts a cytotoxic influence over immature neurocytes. Our previous study revealed that clinically relevant doses of propofol accelerated apoptosis of primary cultured astrocytes of developing rodent brains via rno-miR-665 regulation. However, the role of rno-miR-665 during the growth spurt of neonatal rodent brains in vivo is still uncertain. Post-natal day 7 (P7) rats received a single injection of propofol 30 mg/kg intraperitoneally (i.p.), and neuroapoptosis of hippocampal astrocytes was analyzed by immunofluorescence and scanning electron microscopy. The differential expression of rno-miR-665, BCL2L1 (Bcl-xl), and cleaved caspase 3 (CC3) was surveyed by qRT-PCR and western blotting. In addition, the utility of A-1155463, a highly potent and BCL2L1-selective antagonist, was aimed to assess the contribution of BCL2L1 for neuroglial survival. Following the intraventricular injection of lentivirus rno-miR-665, neuroprotection was detected by 5-point scale measurement. The single dose of propofol 30 mg/kg triggered dose-dependent apoptosis of developing hippocampal astrocytes. Meanwhile, propofol triggered both rno-miR-665 and CC3, and depressed BCL2L1, which was predicted as one target gene of rno-miR-665. Combination treatment with A-1155463 and propofol induced lower mRNA and protein levels of BCL2L1 and more CC3 activation than propofol treatment alone in vivo. The lentivirus-mediated knockdown of rno-miR-665 elevated BCL2L1 and attenuated CC3 levels, whereas up-regulation of rno-miR-665 suppressed BCL2L1 and induced CC3 expression in vivo. More importantly, rno-miR-665 antagomir infusion improved neurological outcomes of pups receiving propofol during the brain growth spurt. Rno-miR-665, providing a potential target for alternative therapeutics for pediatric anesthesia, is susceptible to propofol by negatively targeting antiapoptotic BCL2L1. Relatively little is known about the association between exposure of astrocytes to brief propofol

  12. Dialogic spaces of knowledge construction in research article Conclusion sections written by English L1, English L2 and Spanish L1 writers

    Directory of Open Access Journals (Sweden)

    Elena Sheldon

    2018-04-01

    Full Text Available While vast research efforts have been directed to the identification of moves and their constituent steps in research articles (RA, less attention has been paid to the social negotiation of knowledge, in particular in the Conclusion section of RAs. In this paper, I examine the Conclusion sections of RAs in English and Spanish, including RA Conclusions written in English by Spanish-background speakers in the field of applied linguistics. This study brings together two complementary frameworks, genre-based knowledge and evaluative stance, drawing on Swales’s (1990, 2004 move analysis framework and on the engagement system in Martin and White’s (2005 Appraisal framework. The results indicate that the English L1 group negotiates a consistent space for readers to approve or disapprove the writers’ propositions. However, the Spanish L1 group aligns with readers, using a limited space through contracting resources, which may be because this group addresses a smaller audience in comparison to the English L1 group which addresses an international readership. On the other hand, the English L2 group tends to move towards English rhetorical international practice, but without fully abandoning their SpL1. These results contribute to gaining a better understanding of how successful scholarly writing in English is achieved, and offers important insights for teaching multilingual researchers.

  13. Consumption of Pt anode in phosphoric acid

    Energy Technology Data Exchange (ETDEWEB)

    Kamiya, N.; Urata, K.; Motohira, N.; Ota, K. [Yokohama National University, Yokohama (Japan)

    1997-12-05

    Consumption of Pt anode was investigated in phosphoric acid of various concentration. In 30-70wt% phosphoric acid, Pt dissolved at the rate of 19{mu}gcm{sup -2}h{sup -1}. On the other hand, in 85 wt% phosphoric acid, the amount increased to 0.91 mgcm{sup -2}h{sup -1} which is ca. 180 and 1800 times as much as in 1M sulfuric acid and 1M alkaline solution, respectively. In the diluted phosphoric acid solution, the Pt surface was covered with Pt oxides during the electrolysis, which would prevent the surface from corrosion. However, in the concentrated phosphoric acid, no such oxide surface was observed. Concentrated phosphoric acid might form stable complex with Pt species, therefore the uncovered bare Pt surface is situated in the serious corrosion condition under the high overvoltage and Pt would dissolve into the solution directly instead of forming the Pt oxides. 11 refs., 9 figs., 1 tab.

  14. Regulation of Synaptic Structure by the Ubiquitin C-terminal Hydrolase UCH-L1

    Science.gov (United States)

    Cartier, Anna E.; Djakovic, Stevan N.; Salehi, Afshin; Wilson, Scott M.; Masliah, Eliezer; Patrick, Gentry N.

    2009-01-01

    UCH-L1 is a de-ubiquitinating enzyme that is selectively and abundantly expressed in the brain, and its activity is required for normal synaptic function. Here, we show that UCH-L1 functions in maintaining normal synaptic structure in hippocampal neurons. We have found that UCH-L1 activity is rapidly up-regulated by NMDA receptor activation which leads to an increase in the levels of free monomeric ubiquitin. Conversely, pharmacological inhibition of UCH-L1 significantly reduces monomeric ubiquitin levels and causes dramatic alterations in synaptic protein distribution and spine morphology. Inhibition of UCH-L1 activity increases spine size while decreasing spine density. Furthermore, there is a concomitant increase in the size of pre and postsynaptic protein clusters. Interestingly, however, ectopic expression of ubiquitin restores normal synaptic structure in UCH-L1 inhibited neurons. These findings point to a significant role of UCH-L1 in synaptic remodeling most likely by modulating free monomeric ubiquitin levels in an activity-dependent manner. PMID:19535597

  15. Novel functions for the endocytic regulatory proteins MICAL-L1 and EHD1 in mitosis.

    Science.gov (United States)

    Reinecke, James B; Katafiasz, Dawn; Naslavsky, Naava; Caplan, Steve

    2015-01-01

    During interphase, recycling endosomes mediate the transport of internalized cargo back to the plasma membrane. However, in mitotic cells, recycling endosomes are essential for the completion of cytokinesis, the last phase of mitosis that promotes the physical separation the two daughter cells. Despite recent advances, our understanding of the molecular determinants that regulate recycling endosome dynamics during cytokinesis remains incomplete. We have previously demonstrated that Molecule Interacting with CasL Like-1 (MICAL-L1) and C-terminal Eps15 Homology Domain protein 1 (EHD1) coordinately regulate receptor transport from tubular recycling endosomes during interphase. However, their potential roles in controlling cytokinesis had not been addressed. In this study, we show that MICAL-L1 and EHD1 regulate mitosis. Depletion of either protein resulted in increased numbers of bi-nucleated cells. We provide evidence that bi-nucleation in MICAL-L1- and EHD1-depleted cells is a consequence of impaired recycling endosome transport during late cytokinesis. However, depletion of MICAL-L1, but not EHD1, resulted in aberrant chromosome alignment and lagging chromosomes, suggesting an EHD1-independent function for MICAL-L1 earlier in mitosis. Moreover, we provide evidence that MICAL-L1 and EHD1 differentially influence microtubule dynamics during early and late mitosis. Collectively, our new data suggest several unanticipated roles for MICAL-L1 and EHD1 during the cell cycle. © 2014 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

  16. L1-norm kernel discriminant analysis via Bayes error bound optimization for robust feature extraction.

    Science.gov (United States)

    Zheng, Wenming; Lin, Zhouchen; Wang, Haixian

    2014-04-01

    A novel discriminant analysis criterion is derived in this paper under the theoretical framework of Bayes optimality. In contrast to the conventional Fisher's discriminant criterion, the major novelty of the proposed one is the use of L1 norm rather than L2 norm, which makes it less sensitive to the outliers. With the L1-norm discriminant criterion, we propose a new linear discriminant analysis (L1-LDA) method for linear feature extraction problem. To solve the L1-LDA optimization problem, we propose an efficient iterative algorithm, in which a novel surrogate convex function is introduced such that the optimization problem in each iteration is to simply solve a convex programming problem and a close-form solution is guaranteed to this problem. Moreover, we also generalize the L1-LDA method to deal with the nonlinear robust feature extraction problems via the use of kernel trick, and hereafter proposed the L1-norm kernel discriminant analysis (L1-KDA) method. Extensive experiments on simulated and real data sets are conducted to evaluate the effectiveness of the proposed method in comparing with the state-of-the-art methods.

  17. Cryo-EM structure of the polycystic kidney disease-like channel PKD2L1.

    Science.gov (United States)

    Su, Qiang; Hu, Feizhuo; Liu, Yuxia; Ge, Xiaofei; Mei, Changlin; Yu, Shengqiang; Shen, Aiwen; Zhou, Qiang; Yan, Chuangye; Lei, Jianlin; Zhang, Yanqing; Liu, Xiaodong; Wang, Tingliang

    2018-03-22

    PKD2L1, also termed TRPP3 from the TRPP subfamily (polycystic TRP channels), is involved in the sour sensation and other pH-dependent processes. PKD2L1 is believed to be a nonselective cation channel that can be regulated by voltage, protons, and calcium. Despite its considerable importance, the molecular mechanisms underlying PKD2L1 regulations are largely unknown. Here, we determine the PKD2L1 atomic structure at 3.38 Å resolution by cryo-electron microscopy, whereby side chains of nearly all residues are assigned. Unlike its ortholog PKD2, the pore helix (PH) and transmembrane segment 6 (S6) of PKD2L1, which are involved in upper and lower-gate opening, adopt an open conformation. Structural comparisons of PKD2L1 with a PKD2-based homologous model indicate that the pore domain dilation is coupled to conformational changes of voltage-sensing domains (VSDs) via a series of π-π interactions, suggesting a potential PKD2L1 gating mechanism.

  18. PD-L1 Deficiency within Islets Reduces Allograft Survival in Mice.

    Directory of Open Access Journals (Sweden)

    Dongxia Ma

    Full Text Available Islet transplantation may potentially cure type 1 diabetes mellitus (T1DM. However, immune rejection, especially that induced by the alloreactive T-cell response, remains a restraining factor for the long-term survival of grafted islets. Programmed death ligand-1 (PD-L1 is a negative costimulatory molecule. PD-L1 deficiency within the donor heart accelerates allograft rejection. Here, we investigate whether PD-L1 deficiency in donor islets reduces allograft survival time.Glucose Stimulation Assays were performed to evaluate whether PD-L1 deficiency has detrimental effects on islet function. Islets isolated from PDL1-deficient mice or wild- type (WT mice (C57BL/6j were implanted beneath the renal capsule of streptozotocin (STZ-induced diabetic BALB/c mice. Blood glucose levels and graft survival time after transplantation were monitored. Moreover, we analyzed the residual islets, infiltrating immune cells and alloreactive cells from the recipients.PD-L1 deficiency within islets does not affect islet function. However, islet PD-L1 deficiency increased allograft rejection and was associated with enhanced inflammatory cell infiltration and recipient T-cell alloreactivity.This is the first report to demonstrate that PD-L1 deficiency accelerated islet allograft rejection and regulated recipient alloimmune responses.

  19. Differentiation of eosinophilic leukemia EoL-1 cells into eosinophils induced by histone deacetylase inhibitors.

    Science.gov (United States)

    Ishihara, Kenji; Takahashi, Aki; Kaneko, Motoko; Sugeno, Hiroki; Hirasawa, Noriyasu; Hong, JangJa; Zee, OkPyo; Ohuchi, Kazuo

    2007-03-06

    EoL-1 cells differentiate into eosinophils in the presence of n-butyrate, but the mechanism has remained to be elucidated. Because n-butyrate can inhibit histone deacetylases, we hypothesized that the inhibition of histone deacetylases induces the differentiation of EoL-1 cells into eosinophils. In this study, using n-butyrate and two other histone deacetylase inhibitors, apicidin and trichostatin A, we have analyzed the relationship between the inhibition of histone deacetylases and the differentiation into eosinophils in EoL-1 cells. It was demonstrated that apicidin and n-butyrate induced a continuous acetylation of histones H4 and H3, inhibited the proliferation of EoL-1 cells without attenuating the level of FIP1L1-PDGFRA mRNA, and induced the expression of markers for mature eosinophils such as integrin beta7, CCR1, and CCR3 on EoL-1 cells, while trichostatin A evoked a transient acetylation of histones and induced no differentiation into eosinophils. These findings suggest that the continuous inhibition of histone deacetylases in EoL-1 cells induces the differentiation into mature eosinophils.

  20. L1 arrest, daf-16/FoxO and nonautonomous control of post-embryonic development.

    Science.gov (United States)

    Kaplan, Rebecca E W; Baugh, L Ryan

    2016-01-01

    Post-embryonic development is governed by nutrient availability. L1 arrest, dauer formation and aging illustrate how starvation, anticipation of starvation and caloric restriction have profound influence on C. elegans development, respectively. Insulin-like signaling through the Forkhead box O transcription factor daf-16/FoxO regulates each of these processes. We recently reported that ins-4, ins-6 and daf-28 promote L1 development from the intestine and chemosensory neurons, similar to their role in dauer development. daf-16 functions cell-nonautonomously in regulation of L1 arrest, dauer development and aging. Discrepancies in daf-16 sites of action have been reported in each context, but the consensus implicates epidermis, intestine and nervous system. We suggest technical limitations of the experimental approach responsible for discrepant results. Steroid hormone signaling through daf-12/NHR is known to function downstream of daf-16 in control of dauer development, but signaling pathways mediating cell-nonautonomous effects of daf-16 in aging and L1 arrest had not been identified. We recently showed that daf-16 promotes L1 arrest by inhibiting daf-12/NHR and dbl-1/TGF-β Sma/Mab signaling, two pathways that promote L1 development in fed larvae. We will review these results on L1 arrest and speculate on why there are so many signals and signaling centers regulating post-embryonic development.

  1. New superconductors. Pt. B

    International Nuclear Information System (INIS)

    Assmann, H.; Endres, G.; Friedrich, B.; Grosse, J.; Guenther, A.; Heine, K.; Helldoerfer, H.; Herkert, W.; Hofer, G.; Jenovelis, A.; Kleinlein, W.; Koerner, F.; Krauth, H.; Kress, B.; Moser, T.; Neumueller, H.W.; Proelss, N.; Schmatjko, K.J.; Schmidt, W.; Seebacher, B.; Stieding, P.; Tenbrink, J.; Uzel, Y.; Wilhelm, M.

    1992-02-01

    Based on the results of the work on thin films, ceramics and measurement techniques performed in part A, the aim of part B 'Conductor development' was to investigate and to evaluate selected fabrication processes suitable for the manufacturing of conductors (tapes, wires) for applicatons in magnet technology and power engineering. Critical current densities j c of about 1 kA/cm 2 (77 K, zero field) were obtained for melt-textured 2212 BiSrCaCuO bulk material and 2212 BiSrCaCuO Ag-wires; but j c strongly decreases in magnetic field B (factor 10 3 at 0.1 T). At 4.2 K, the Ag-wires made by the powder in tube technique (PIT) achieved j c -values of 50 kA/cm 2 and j c (B) is practically not affected by a magnetic field below 320 K (j c =10 kA/cm 2 at 20 T). Therefore, these conductors are intended for applications in high field magnets operated between 4.2 K and 20 K. First test coils (conductor lengths 1.5 m) had somewhat reduced j c =10 kA/cm 2 (4.2 K, zero field) The PIT-technique ws successfully applied with the three layer Bi-compound. j c vlaues up to 35 kA/cm 2 were obtained at 77 K (zero field), which are within the international top values reported so far. Another continuous manufacturing process is the laser melting technique which achieves rapid melting of YBaCuO-layers of 10-20 μm in thickness on (Ag) substrates, jc=1.4-4 kA/cm 2 were obtained without any process optimization using textured precursors made by electrophoretic deposition. As a preliminary step for the proposed high-current demonstration conductor (200 A, 77 K), laser-ablated YBaCuO films were tested on technical substrates (Ni-based alloys) with buffer layers (MgO, ZrO 2 ). The films had good c-axis orientation. Until now it has been not possible to measure j c at 77 K. (orig.). 67 refs., 21 tabs., 131 figs [de

  2. Active form Notch4 promotes the proliferation and differentiation of 3T3-L1 preadipocytes

    Energy Technology Data Exchange (ETDEWEB)

    Lai, Peng-Yeh [Institute of Molecular Biology and Department of Life Science, National Chung Cheng University, Chiayi 621, Taiwan, ROC (China); Tsai, Chong-Bin [Institute of Molecular Biology and Department of Life Science, National Chung Cheng University, Chiayi 621, Taiwan, ROC (China); Department of Ophthalmology, Chiayi Christian Hospital, Chiayi 600, Taiwan, ROC (China); Tseng, Min-Jen, E-mail: biomjt@ccu.edu.tw [Institute of Molecular Biology and Department of Life Science, National Chung Cheng University, Chiayi 621, Taiwan, ROC (China)

    2013-01-18

    Highlights: ► Notch4IC modulates the ERK pathway and cell cycle to promote 3T3-L1 proliferation. ► Notch4IC facilitates 3T3-L1 differentiation by up-regulating proadipogenic genes. ► Notch4IC promotes proliferation during the early stage of 3T3-L1 adipogenesis. ► Notch4IC enhances differentiation during subsequent stages of 3T3-L1 adipogenesis. -- Abstract: Adipose tissue is composed of adipocytes, which differentiate from precursor cells in a process called adipogenesis. Many signal molecules are involved in the transcriptional control of adipogenesis, including the Notch pathway. Previous adipogenic studies of Notch have focused on Notch1 and HES1; however, the role of other Notch receptors in adipogenesis remains unclear. Q-RT-PCR analyses showed that the augmentation of Notch4 expression during the differentiation of 3T3-L1 preadipocytes was comparable to that of Notch1. To elucidate the role of Notch4 in adipogenesis, the human active form Notch4 (N4IC) was transiently transfected into 3T3-L1 cells. The expression of HES1, Hey1, C/EBPδ and PPARγ was up-regulated, and the expression of Pref-1, an adipogenic inhibitor, was down-regulated. To further characterize the effect of N4IC in adipogenesis, stable cells expressing human N4IC were established. The expression of N4IC promoted proliferation and enhanced differentiation of 3T3-L1 cells compared with those of control cells. These data suggest that N4IC promoted proliferation through modulating the ERK pathway and the cell cycle during the early stage of 3T3-L1 adipogenesis and facilitated differentiation through up-regulating adipogenic genes such as C/EBPα, PPARγ, aP2, LPL and HSL during the middle and late stages of 3T3-L1 adipogenesis.

  3. Characterization of new cell line stably expressing CHI3L1 oncogene

    Directory of Open Access Journals (Sweden)

    Chekhonin V. P.

    2011-06-01

    Full Text Available Aim. To characterize the immortalized 293 cell line after stable transfection with human oncogene (CHI3L1. Methods. 293 cells, stably transfected with pcDNA3.1_CHI3L1, and 293 cells, stably transfected with pcDNA3.1 as a negative control, were used throughout all experiments. The clones of CHI3L1-expressing 293 cells and 293 cells, transfected with pcDNA3.1, were analyzed by immunofluorescence and confocal microscopy. Cell proliferation was measured using MTT assay; analyses of ERK1/2 and AKT activation and their cellular localization were performed with anti-phospho-ERK and anti-phospho-AKT antibodies. Specific activation of MAP and PI3 kinases was measured by densitometric analysis of Western-blot signals. Results. The obtained results show quite modest ability of CHI3L1 to stimulate cell growth and reflect rather an improved cellular plating efficiency of the 293 cells stably transfected with pcDNA3.1_CHI3L1 as compared to the 293 cells transfected with an «empty» vector. ERK1/2 and AKT are activated in the 293_CHI3L1 cells. In these cells phosphorylated ERK1/2 were localized in both cell cytoplasm and nuclei while AKT only in cytoplasm. The 293_CHI3L1 cells differed from the 293 cells, transfected with an «empty» vector, in their size and ability to adhere to the culture plates. Conclusions. The overexpression of CHI3L1 is likely to have an important role in tumorigenesis via a mechanism which involves activation of PI3K and ERK1/2 pathways. The tumors which can be induced by orthotopic implantation of the transformed human cells with overexpressed human oncogene CHI3L1 into the rat brain can be used as a target for anticancer drug development.

  4. Localization and role of NPC1L1 in cholesterol absorption in human intestine.

    Science.gov (United States)

    Sané, Alain Théophile; Sinnett, Daniel; Delvin, Edgard; Bendayan, Moise; Marcil, Valérie; Ménard, Daniel; Beaulieu, Jean-François; Levy, Emile

    2006-10-01

    Recent studies have documented the presence of Niemann-Pick C1-Like 1 (NPC1L1) in the small intestine and its capacity to transport cholesterol in mice and rats. The current investigation was undertaken to explore the localization and function of NPC1L1 in human enterocytes. Cell fractionation experiments revealed an NPC1L1 association with apical membrane of the enterocyte in human jejunum. Signal was also detected in lysosomes, endosomes, and mitochondria. Confirmation of cellular NPC1L1 distribution was obtained by immunocytochemistry. Knockdown of NPC1L1 caused a decline in the ability of Caco-2 cells to capture micellar [(14)C]free cholesterol. Furthermore, this NPC1L1 suppression resulted in increased and decreased mRNA levels and activity of HMG-CoA reductase, the rate-limiting step in cholesterol synthesis, and of ACAT, the key enzyme in cholesterol esterification, respectively. An increase was also noted in the transcriptional factor sterol-regulatory element binding protein that modulates cholesterol homeostasis. Efforts were devoted to define the impact of NPC1L1 knockdown on other mediators of cholesterol uptake. RT-PCR evidence is presented to show the significant decrease in the levels of scavenger receptor class B type I (SR-BI) with no changes in ABCA1, ABCG5, and cluster determinant 36 in NPC1L1-deficient Caco-2 cells. Together, our data suggest that NPC1L1 contributes to intestinal cholesterol homeostasis and possibly cooperates with SR-BI to mediate cholesterol absorption in humans.

  5. Prognostic Value of PD-L1 in Breast Cancer: A Meta-Analysis.

    Science.gov (United States)

    Wang, Changjun; Zhu, Hanjiang; Zhou, Yidong; Mao, Feng; Lin, Yan; Pan, Bo; Zhang, Xiaohui; Xu, Qianqian; Huang, Xin; Sun, Qiang

    2017-07-01

    Programmed cell death 1 ligand 1 (PD-L1) is a promising therapeutic target for cancer immunotherapy. However, the correlation between PD-L1 and breast cancer survival remains unclear. Here, we present the first meta-analysis to investigate the prognostic value of PD-L1 in breast cancer. We searched Pubmed, Embase, and Cochrane Central Register of Controlled Trials databases for relevant studies evaluating PD-L1 expression and breast cancer survival. Fixed- and random-effect meta-analyses were conducted based on heterogeneity of included studies. Publication bias was evaluated by funnel plot and Begg's test. Overall, nine relevant studies with 8583 patients were included. PD-L1 overexpression was found in 25.8% of breast cancer patients. PD-L1 (+) associated with several high-risk prognostic indicators, such as ductal cancer (p = 0.037), high tumor grade (p = 0.000), ER negativity (p = 0.000), PR negativity (p = 0.000), HER2 positivity (p = 0.001) and aggressive molecular subtypes (HER2-rich and Basal-like p = 0.000). PD-L1 overexpression had no significant impact on metastasis-free survival (HR 0.924, 95% CI = 0.747-1.141, p = 0.462), disease-free survival (HR 1.122, 95% CI = 0.878-1.434, p = 0.357) and overall specific survival (HR 0.837, 95% CI = 0.640-1.093, p = 0.191), but significantly correlated with shortened overall survival (HR 1.573, 95% CI = 1.010-2.451, p = 0.045). PD-L1 overexpression in breast cancer associates with multiple clinicopathological parameters that indicated poor outcome, and may increase the risk for mortality. Further standardization of PD-L1 assessment assay and well-controlled clinical trials are warranted to clarify its prognostic and therapeutic value. © 2017 Wiley Periodicals, Inc.

  6. Perancangan Promosi Digital PT Campina Di Surabaya

    OpenAIRE

    Wijaya, Fernando; Hartanto, Deddi Duto; Sylvia, Merry

    2013-01-01

    Perancangan ini dilakukan untuk mempromosikan PT. Campina Ice Cream Industry beserta produknya. PT. Campina Ice Cream Industry diangkat sebagai topic perancangan karena banyak competitor-kompetitor yang bermunculan. Dengan melihat berbagai kelebihan dan kekurangan PT. Campina Ice Cream Industry, promosi dirancang agar dapat menggambarkan kelebihan PT. Campina Ice Cream Industry. Sehingga diharapkan dapat mengingatkan kembali ice cream Campina dalam benak konsumen. Untuk media promosi digital...

  7. Sn surface-enriched Pt-Sn bimetallic nanoparticles as a selective and stable catalyst for propane dehydrogenation

    KAUST Repository

    Zhu, Haibo

    2014-12-01

    A new one pot, surfactant-free, synthetic route based on the surface organometallic chemistry (SOMC) concept has been developed for the synthesis of Sn surface-enriched Pt-Sn nanoparticles. Bu3SnH selectively reacts with [Pt]-H formed in situ at the surface of Pt nanoparticles, Pt NPs, obtained by reduction of K2PtCl4 by LiB(C2H5)3H. Chemical analysis, 1H MAS and 13C CP/MAS solid-state NMR as well as two-dimensional double-quantum (DQ) and triple-quantum (TQ) experiments show that organo-tin moieties Sn(n-C4H9) are chemically linked to the surface of Pt NPs to produce, in fine, after removal of most of the n-butyl fragment, bimetallic Pt-Sn nanoparticles. The Sn(n-CH2CH2CH2CH3) groups remaining at the surface are believed to stabilize the as-synthesized Pt-Sn NPs, enabling the bimetallic NPs to be well dispersed in THF. Additionally, the Pt-Sn nanoparticles can be supported on MgAl2O4 during the synthesis of the nanoparticles. Some of the Pt-Sn/MgAl2O4 catalyst thus prepared exhibits high activity in PROX of CO and an extremely high selectivity and stability in propane dehydrogenation to propylene. The enhanced activity in propane dehydrogenation is associated with the high concentration of inactive Sn at the surface of Pt nanoparticles which ”isolates” the active Pt atoms. This conclusion is confirmed by XRD, NMR, TEM, and XPS analysis.

  8. High performance polymer electrolyte fuel cells with ultra-low Pt loading electrodes prepared by dual ion-beam assisted deposition

    International Nuclear Information System (INIS)

    Saha, Madhu Sudan; Gulla, Andrea F.; Allen, Robert J.; Mukerjee, Sanjeev

    2006-01-01

    Ultra-low pure Pt-based electrodes (0.04-0.12 mg Pt /cm 2 ) were prepared by dual ion-beam assisted deposition (dual IBAD) method on the surface of a non-catalyzed gas diffusion layer (GDL) substrate. Film thicknesses ranged between 250 and 750 A, these are compared with a control, a conventional Pt/C (1.0 mg Pt(MEA) /cm 2 , E-TEK). The IBAD electrode constituted a significantly different morphology, where low density Pt deposits (largely amorphous) were formed with varying depths of penetration into the gas diffusion layer, exhibiting a gradual change towards increasing crystalline character (from 250 to 750 A). Mass specific power density of 0.297 g Pt /kW is reported with 250 A IBAD deposit (0.04 mg Pt /cm 2 for a total MEA loading of 0.08 mg Pt /cm 2 ) at 0.65 V. This is contrasted with the commercial MEA with a loading of 1 mg Pt(MEA) /cm 2 where mass specific power density obtained was 1.18 g Pt /kW (at 0.65 V), a value typical of current state of the art commercial electrodes containing Pt/C. The principal shortcoming in this effort is the area specific power density which was in the range of 0.27-0.43 W/cm 2 (for 250-750 A IBAD) at 0.65 V, hence much below the automotive target value of 0.8-0.9 W/cm 2 (at 0.65 V). An attempt to mitigate these losses is reported with the use of patterning. In this context a series of patterns ranging from 45 to 80% Pt coverage were used in conjunction with a hexagonal hole geometry. Up to 30% lowering of mass transport losses were realized

  9. Modelling and L1 Adaptive Control of pH in Bioethanol Enzymatic Process

    DEFF Research Database (Denmark)

    Prunescu, Remus Mihail; Blanke, Mogens; Sin, Gürkan

    2013-01-01

    for pH level regulation: one is a classical PI controller; the other an L1 adaptive output feedback controller. Model-based feed-forward terms are added to the controllers to enhance their performances. A new tuning method of the L1 adaptive controller is also proposed. Further, a new performance...... function is formulated and tailored to this type of processes and is used to monitor the performances of the process in closed loop. The L1 design is found to outperform the PI controller in all tests....

  10. Effect of L1-ORF2 on senescence of GES-1 cells and its molecular mechanisms

    Directory of Open Access Journals (Sweden)

    Ying-nan LI

    2016-06-01

    Full Text Available Objective  To investigate the effect of long interspersed nuclear elements 1 open reading frame 2(L1-ORF2 gene on the senescence of GES-1 cells and its mechanism of molecular regulation. Methods  Cell culture of high glucose was used to construct stable model of senescent GES-1 cells. L1-ORF2 siRNA vector was constructed and then transfected into normal GES1 and senescent ones with liposome transfection reagents for transient expression. Forty eight hours after transfection, cell growth curves were drawn to show the speed of cell proliferation, flow cytometry was used to analyze the cell cycle, β-galactosidase staining to detect cell aging and Western blotting to detect the expressions of L1-ORF2, P53 and P21proteins. Results  Senescent GES-1 cell model and L1-ORF2 siRNA vector were constructed. Compared with negative control group, the L1-ORF2 expression decreased in normal and senescent GES-1 cells transfected with L1-ORF2 siRNA vector. There was a faster proliferation of senescent GES1 cells (P<0.05 and lower ratio of β-galactosidase (56% vs 69%, P<0.05 and G0/G1 phase (34.2% vs 39.3%, P<0.05 in senescent GES-1 cells transfected with L1-ORE2 siRNA vector than those transfected with negative control vector, while there was no obvious difference between normal GES-1 cells transfected with L1-ORF2 siRNA vector and negative control vector (P>0.05. P53 protein was expressed only in senescent GES-1 cell, while P21 protein was expressed in both normal and senescent GES-1 cells, and the latter had a higher expression level (P<0.05. The GES-1 cells transfected with L1-ORF2 siRNA vector showed lower expressions of P53 and P21 proteins than those transfected with negative control vector (P<0.05. Conclusions  L1-ORF2-siRNA vector could down-regulate the expression of L1-ORF2 protein in normal and senescent GES-1 cells and promote the proliferation of senescent GES-1 cells. P21 and P53 proteins participate in the process of L1-ORF2 regulating

  11. Mn doping effect on structure and magnetism of epitaxial (FePt)1-xMnx films

    International Nuclear Information System (INIS)

    Huang, J.C.A.; Chang, Y.C.; Yu, C.C.; Yao, Y.D.; Hu, Y.M.; Fu, C.M.

    2003-01-01

    We study the structure and perpendicular magnetism of molecular beam epitaxy grown (FePt) 1-x Mn x films with doping concentration x=0, 1%, 2%, 3%, 4%, and 5%. The (FePt) 1-x Mn x films were made by multilayers growth of [Fe/Pt/Mn]xN at 100 deg. C and annealed at 600 deg. C. X-ray diffraction scans indicate that relatively better L1 0 ordered structure for low Mn doping (x 3%. The perpendicular magnetic anisotropy effect of the (FePt) 1-x Mn x films tends to decrease with the increase of Mn doping for x>1%. However, the x=1% doped films possess slightly better perpendicular magnetic anisotropy effect than the zero doped film. The perpendicular magnetic anisotropy constant are of about 1.3x10 7 and 1.6x10 7 erg/cm 3 for x=0% and x=1%, respectively

  12. Degradation of fifteen emerging contaminants at microg L(-1) initial concentrations by mild solar photo-Fenton in MWTP effluents.

    Science.gov (United States)

    Klamerth, N; Rizzo, L; Malato, S; Maldonado, Manuel I; Agüera, A; Fernández-Alba, A R

    2010-01-01

    The degradation of 15 emerging contaminants (ECs) at low concentrations in simulated and real effluent of municipal wastewater treatment plant with photo-Fenton at unchanged pH and Fe=5 mg L(-1) in a pilot-scale solar CPC reactor was studied. The degradation of those 15 compounds (Acetaminophen, Antipyrine, Atrazine, Caffeine, Carbamazepine, Diclofenac, Flumequine, Hydroxybiphenyl, Ibuprofen, Isoproturon, Ketorolac, Ofloxacin, Progesterone, Sulfamethoxazole and Triclosan), each with an initial concentration of 100 microg L(-1), was found to depend on the presence of CO(3)(2-) and HCO(3)(-) (hydroxyl radicals scavengers) and on the type of water (simulated water, simulated effluent wastewater and real effluent wastewater), but is relatively independent of pH, the type of acid used for release of hydroxyl radicals scavengers and the initial H(2)O(2) concentration used. Toxicity tests with Vibrio fisheri showed that degradation of the compounds in real effluent wastewater led to toxicity increase. (c) 2009 Elsevier Ltd. All rights reserved.

  13. Mg2BIV: Narrow Bandgap Thermoelectric Semiconductors

    Science.gov (United States)

    Kim, Il-Ho

    2018-05-01

    Thermoelectric materials can convert thermal energy directly into electric energy and vice versa. The electricity generation from waste heat via thermoelectric devices can be considered as a new energy source. For instance, automotive exhaust gas and all industrial processes generate an enormous amount of waste heat that can be converted to electricity by using thermoelectric devices. Magnesium compound Mg2BIV (BIV = Si, Ge or Sn) has a favorable combination of physical and chemical properties and can be a good base for the development of new efficient thermoelectrics. Because they possess similar properties to those of group BIV elemental semiconductors, they have been recognized as good candidates for thermoelectric applications. Mg2Si, Mg2Ge and Mg2Sn with an antifluorite structure are narrow bandgap semiconductors with indirect band gaps of 0.77 eV, 0.74 eV, and 0.35 eV, respectively. Mg2BIV has been recognized as a promising material for thermoelectric energy conversion at temperatures ranging from 500 K to 800 K. Compared to other thermoelectric materials operating in the similar temperature range, such as PbTe and filled skutterudites, the important aspects of Mg2BIV are non-toxic and earth-abundant elements. Based on classical thermoelectric theory, the material factor β ( m* / m e)3/2μκ L -1 can be utilized as the criterion for thermoelectric material selection, where m* is the density-of-states effective mass, me is the mass of an electron, μ is the carrier mobility, and κL is the lattice thermal conductivity. The β for magnesium silicides is 14, which is very high compared to 0.8 for iron silicides, 1.4 for manganese silicides, and 2.6 for silicon-germanium alloys. In this paper, basic phenomena of thermoelectricity and transport parameters for thermoelectric materials were briefly introduced, and thermoelectric properties of Mg2BIV synthesized by using a solid-state reaction were reviewed. In addition, various Mg2BIV compounds were discussed

  14. EX1004L1 Water Column Summary Report and Profile Data Collection

    Data.gov (United States)

    National Oceanic and Atmospheric Administration, Department of Commerce — A complete set of water column profile data and CTD Summary Report (if generated) generated by the Okeanos Explorer during EX1004L1: Exploration Indonesia - Guam to...

  15. IceBridge NSERC L1B Geolocated Meteorologic and Surface Temperature Data

    Data.gov (United States)

    National Aeronautics and Space Administration — The IceBridge National Suborbital Education & Research Center (NSERC) L1B Geolocated Meteorologic and Surface Temperature (IAMET1B) data set is a collection of...

  16. IceBridge NSERC L1B Geolocated Meteorologic and Surface Temperature Data, Version 1

    Data.gov (United States)

    National Aeronautics and Space Administration — The IceBridge National Suborbital Education & Research Center (NSERC) L1B Geolocated Meteorologic and Surface Temperature (IAMET1B) data set is a collection of...

  17. IceBridge LVIS POS/AV L1B Corrected Position and Attitude Data

    Data.gov (United States)

    National Aeronautics and Space Administration — The IceBridge LVIS POS/AV L1B Corrected Position and Attitude Data (IPPLV1B) data set contains georeferencing data from the Applanix 510 and 610 POS AV systems flown...

  18. IceBridge POS/AV L1B Corrected Position and Attitude Data

    Data.gov (United States)

    National Aeronautics and Space Administration — The IceBridge POS/AV L1B Corrected Position and Attitude (IPAPP1B) data set contains georeferencing data from the Applanix 510 POS AV system flown with the Digital...

  19. EX1205L1 Water Column Summary Report and Profile Data Collection

    Data.gov (United States)

    National Oceanic and Atmospheric Administration, Department of Commerce — A complete set of water column profile data and CTD Summary Report (if generated) generated by the Okeanos Explorer during EX1205L1: Exploration, Blake Plateau...

  20. EX1502L1 Water Column Summary Report and Profile Data Collection

    Data.gov (United States)

    National Oceanic and Atmospheric Administration, Department of Commerce — A complete set of water column profile data and CTD Summary Report (if generated) generated by the Okeanos Explorer during EX1502L1: Caribbean Exploration (Mapping)...

  1. EX1504L1 Water Column Summary Report and Profile Data Collection

    Data.gov (United States)

    National Oceanic and Atmospheric Administration, Department of Commerce — A complete set of water column profile data and CTD Summary Report (if generated) generated by the Okeanos Explorer during EX1504L1: CAPSTONE NWHI & Johnston...

  2. SMAP L1B Radiometer Half-Orbit Time-Ordered Brightness Temperatures V003

    Data.gov (United States)

    National Aeronautics and Space Administration — This Level-1B (L1B) product provides calibrated estimates of time-ordered geolocated brightness temperatures measured by the Soil Moisture Active Passive (SMAP)...

  3. EX1503L1 Water Column Summary Report and Profile Data Collection

    Data.gov (United States)

    National Oceanic and Atmospheric Administration, Department of Commerce — A complete set of water column profile data and CTD Summary Report (if generated) generated by the Okeanos Explorer during EX1503L1: Tropical Exploration (Mapping I)...

  4. Okeanos Explorer (EX1402L1): Gulf of Mexico Mapping and Exploration

    Data.gov (United States)

    National Oceanic and Atmospheric Administration, Department of Commerce — During EX1402L1, multibeam,single beam, and subbottom data will be collected 24 hours a day and XBT casts will be conducted at an interval defined by prevailing...

  5. An optimal L1-minimization algorithm for stationary Hamilton-Jacobi equations

    KAUST Repository

    Guermond, Jean-Luc; Popov, Bojan

    2009-01-01

    We describe an algorithm for solving steady one-dimensional convex-like Hamilton-Jacobi equations using a L1-minimization technique on piecewise linear approximations. For a large class of convex Hamiltonians, the algorithm is proven

  6. ASTER Expedited L1A Reconstructed Unprocessed Instrument Data V003

    Data.gov (United States)

    National Aeronautics and Space Administration — The ASTER Expedited L1A Reconstructed Unprocessed Instrument Data is produced with the express purpose of providing the ASTER Science Team members and others, data...

  7. Assay for the pattern recognition molecule collectin liver 1 (CL-L1)

    DEFF Research Database (Denmark)

    Axelgaard, Esben; Jensenius, Jens Christian; Thiel, Steffen

    Collectin liver 1 (also termed collectin 10 and CL-L1) is a C-type lectin that functions as a pattern recognition molecule (PRM) in the innate immune system1. We have produced antibodies against CL-L1 and have developed a sandwich-type time-resolved immuno-fluorometric assay (TRIFMA...... to co-purify with MASPs, possibly rendering it a role in complement. CL-L1 showed binding activity towards mannose-TSK beads in a Ca2+-dependent manner. This binding could be inhibited by mannose and glucose, but not by galactose, indicating that CL-L1 binds via its carbohydrate-recognition domain (CRD)....

  8. MODIS/Aqua Raw Radiances in Counts 5-Min L1A Swath V006

    Data.gov (United States)

    National Aeronautics and Space Administration — The MODIS/Aqua Raw Radiances in Counts 5-Min L1A Swath (MYD01) product contains reformatted and packaged raw instrument data. MODIS instrument data, in packetized...

  9. IceBridge Riegl Laser Altimeter L1B Time-Tagged Laser Ranges

    Data.gov (United States)

    National Aeronautics and Space Administration — The NASA IceBridge Riegl Laser Altimeter L1B Time-Tagged Laser Ranges (ILUTP1B) data set contains laser ranges, returned pulses, and deviation for returned pulses in...

  10. EX1402L1 Water Column Summary Report and Profile Data Collection

    Data.gov (United States)

    National Oceanic and Atmospheric Administration, Department of Commerce — A complete set of water column profile data and CTD Summary Report (if generated) generated by the Okeanos Explorer during EX1402L1: Gulf of Mexico Mapping and...

  11. Hydrography - MO 2014 Class L1 Lake Watersheds WQS TableG (SHP)

    Data.gov (United States)

    NSGIC State | GIS Inventory — This feature class contains watersheds for Class L1 lakes listed in Table G - Lake Classifications and Use Designations of the Water Quality Standards rule published...

  12. IceBridge Scintrex CS-3 Cesium Magnetometer L1B Geolocated Magnetic Anomalies, Version 1

    Data.gov (United States)

    National Aeronautics and Space Administration — The NASA IceBridge Scintrex CS-3 Cesium Magnetometer L1B Geolocated Magnetic Anomalies (IMCS31B) data set contains magnetic field readings taken over Greenland using...

  13. Strategic Alliance Between PT Dirgantara Indonesia and Airbus Millitary (a Case Study of PT Dirgantara Indonesia)

    OpenAIRE

    Indriyanto, Reza Relen; Wandebori, Harimukti; Astuti, Novika Candra

    2013-01-01

    PT Dirgantara Indonesia (PT DI) is one of the aircraft manufacturing companies in Indonesia. The tight of competition in aerospace industry needs to improve its performance to gain niche market. Therefore, Ministry State of Own Enterprises has instructed PT Perusahaan Pengelola Aset (PT PPA) and PT DI to restructure and revitalize company with supported by Airbus Military as a strategic alliance partner, in order to increase the performance of production capacity, aircraft sales, and financia...

  14. Large tunneling anisotropic magneto-Seebeck effect in a CoPt/MgO/Pt tunnel junction

    Czech Academy of Sciences Publication Activity Database

    Amin, V.P.; Zemen, Jan; Železný, Jakub; Jungwirth, Tomáš; Sinova, Jairo

    2014-01-01

    Roč. 90, č. 14 (2014), , "140406-1"-"140406-5" ISSN 1098-0121 R&D Projects: GA MŠk(CZ) LM2011026; GA ČR GB14-37427G EU Projects: European Commission(XE) 268066 - 0MSPIN Institutional support: RVO:68378271 Keywords : spin tronics * spin caloritronics Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 3.736, year: 2014

  15. YKL-40 and genetic status of CHI3L1 in a large group of asthmatics

    DEFF Research Database (Denmark)

    Hansen, Jakob W; Thomsen, Simon F; Porsbjerg, Celeste

    2015-01-01

    BACKGROUND: Studies have shown a relationship between asthma, serum YKL-40, and the single nucleotide polymorphism (SNP) (-131 C/G, rs4950928) in the CHI3L1 gene that codes for YKL-40. However, the findings differ. We studied the relationship between clinical asthma phenotypes, serum YKL-40...... to clarify the relationship between different asthma phenotypes, YKL-40, and CHI3L1....

  16. High-dose Resveratrol Inhibits Insulin Signaling Pathway in 3T3-L1 Adipocytes

    OpenAIRE

    Lee, Haemi; Kim, Jae-woo

    2013-01-01

    Background Insulin resistance is a major factor in the development of metabolic syndrome and is associated with central obesity and glucose intolerance. Resveratrol, a polyphenol found in fruits, has been shown to improve metabolic conditions. Although it has been widely studied how resveratrol affects metabolism, little is known about how resveratrol regulates lipogenesis with insulin signaling in 3T3-L1 adipocytes. Methods: We treated differentiated 3T3-L1 adipocytes with resveratrol to obs...

  17. L1 Use in EFL Classes with English-only Policy: Insights from Triangulated Data

    Directory of Open Access Journals (Sweden)

    Seyyed Hatam Tamimi Sa’d

    2015-06-01

    Full Text Available This study examines the role of the use of the L1 in EFL classes from the perspective of EFL learners. The triangulated data were collected using class observations, focus group semi-structured interviews and the learners’ written reports of their perceptions and attitudes in a purpose-designed questionnaire. The participants consisted of sixty male Iranian EFL learners who constituted three classes. The results indicated a strong tendency among the participants toward L1 and its positive effects on language learning; while only a minority of the learners favoured an English-only policy, the majority supported the judicious, limited and occasional use of the L1, particularly on the part of the teacher. The participants mentioned the advantages as well as the disadvantages of the use/non-use of the L1. While the major advantage and the main purpose of L1 use was said to be the clarification and intelligibility of instructions, grammatical and lexical items, the main advantages of avoiding it were stated as being the improvement of speaking and listening skills, aximizing learners’ exposure to English and their becoming accustomed to it. The study concludes that, overall and in line with the majority of the previous research studies, a judicious, occasional and limited use of the L1 is a better approach to take in EFL classes than to include or exclude it totally. In conclusion, a re-examination of the English-only policy and a reconsideration of the role of the L1 are recommended. Finally, the commonly held assumption that L1 is a hindrance and an impediment to the learners’ language learning is challenged.

  18. Multiplexed Immunofluorescence Reveals Potential PD-1/PD-L1 Pathway Vulnerabilities in Craniopharyngioma.

    Science.gov (United States)

    Coy, Shannon; Rashid, Rumana; Lin, Jia-Ren; Du, Ziming; Donson, Andrew M; Hankinson, Todd C; Foreman, Nicholas K; Manley, Peter E; Kieran, Mark W; Reardon, David A; Sorger, Peter K; Santagata, Sandro

    2018-03-02

    Craniopharyngiomas are neoplasms of the sellar/parasellar region that are classified into adamantinomatous (ACP) and papillary (PCP) subtypes. Surgical resection of craniopharyngiomas is challenging, and recurrence is common, frequently leading to profound morbidity. BRAF V600E mutations render PCP susceptible to BRAF/MEK inhibitors, but effective targeted therapies are needed for ACP. We explored the feasibility of targeting the PD-1/PD-L1 immune checkpoint pathway in ACP and PCP. We mapped and quantified PD-L1 and PD-1 expression in ACP and PCP resections using immunohistochemistry, immunofluorescence, and RNA in situ hybridization. We used tissue-based cyclic immunofluorescence (t-CyCIF) to map the spatial distribution of immune cells and characterize cell cycle and signaling pathways in ACP tumor cells which intrinsically express PD-1. All ACP (15±14% of cells, n=23, average±S.D.) and PCP (35±22% of cells, n=18) resections expressed PD-L1. In ACP, PD-L1 was predominantly expressed by tumor cells comprising the cyst-lining. In PCP, PD-L1 was highly-expressed by tumor cells surrounding the stromal fibrovascular cores. ACP also exhibited tumor cell-intrinsic PD-1 expression in whorled epithelial cells with nuclear-localized beta-catenin. These cells exhibited evidence of elevated mTOR and MAPK signaling. Profiling of immune populations in ACP and PCP showed a modest density of CD8+ T-cells. ACP exhibit PD-L1 expression in the tumor cyst-lining and intrinsic PD-1 expression in cells proposed to comprise an oncogenic stem-like population. In PCP, proliferative tumor cells express PD-L1 in a continuous band at the stromal-epithelial interface. Targeting PD-L1 and/or PD-1 in both subtypes of craniopharyngioma might therefore be an effective therapeutic strategy.

  19. PD-1/PD-L1 Inhibitors for Immuno-oncology: From Antibodies to Small Molecules.

    Science.gov (United States)

    Geng, Qiaohong; Jiao, Peifu; Jin, Peng; Su, Gaoxing; Dong, Jinlong; Yan, Bing

    2018-02-12

    The recent regulatory approvals of immune checkpoint protein inhibitors, such as ipilimumab, pembrolizumab, nivolumab, atezolizumab, durvalumab, and avelumab ushered a new era in cancer therapy. These inhibitors do not attack tumor cells directly but instead mobilize the immune system to re-recognize and eradicate tumors, which endows them with unique advantages including durable clinical responses and substantial clinical benefits. PD-1/PD-L1 inhibitors, a pillar of immune checkpoint protein inhibitors, have demonstrated unprecedented clinical efficacy in more than 20 cancer types. Besides monoclonal antibodies, diverse PD- 1/PD-L1 inhibiting candidates, such as peptides, small molecules have formed a powerful collection of weapons to fight cancer. The goal of this review is to summarize and discuss the current PD-1/PD-L1 inhibitors including candidates under clinical development, their molecular interactions with PD-1 or PD-L1, the disclosed structureactivity relationships of peptides and small molecules as inhibitors. Current PD-1/PD-L1 inhibitors under clinical development are exclusively dominated by antibodies. The molecular interactions of therapeutic antibodies with PD-1 or PD-L1 have been gradually elucidated for the design of novel inhibitors. Various peptides and traditional small molecules have been investigated in preclinical model to discover novel PD-1/PD-L1 inhibitors. Peptides and small molecules may play an important role in immuno-oncology because they may bind to multiple immune checkpoint proteins via rational design, opening opportunity for a new generation of novel PD-1/PD-L1 inhibitors. Copyright© Bentham Science Publishers; For any queries, please email at epub@benthamscience.org.

  20. Chemotherapy treatment is associated with altered PD-L1 expression in lung cancer patients

    DEFF Research Database (Denmark)

    Rojkó, Lívia; Reiniger, Lilla; Téglási, Vanda

    2018-01-01

    Objectives: While the predictive value of programmed cell death ligand-1 (PD-L1) protein expression for immune checkpoint inhibitor therapy of lung cancer has been extensively studied, the impact of standard platinum-based chemotherapy on PD-L1 or programmed cell death-1 (PD-1) expression is unkn...... expression of TC in a subset of patients, therefore, rebiopsy and re-evaluation of PD-L1 expression may be necessary for the indication of immune checkpoint inhibitor therapy.......Objectives: While the predictive value of programmed cell death ligand-1 (PD-L1) protein expression for immune checkpoint inhibitor therapy of lung cancer has been extensively studied, the impact of standard platinum-based chemotherapy on PD-L1 or programmed cell death-1 (PD-1) expression...... is unknown. The aim of this study was to determine the changes in PD-L1 expression of tumor cells (TC) and immune cells (IC), in PD-1 expression of IC, and in the amount of stromal mononuclear cell infiltration after platinum-based chemotherapy in patients with lung cancer. Materials and methods: We...

  1. Improved l1-SPIRiT using 3D walsh transform-based sparsity basis.

    Science.gov (United States)

    Feng, Zhen; Liu, Feng; Jiang, Mingfeng; Crozier, Stuart; Guo, He; Wang, Yuxin

    2014-09-01

    l1-SPIRiT is a fast magnetic resonance imaging (MRI) method which combines parallel imaging (PI) with compressed sensing (CS) by performing a joint l1-norm and l2-norm optimization procedure. The original l1-SPIRiT method uses two-dimensional (2D) Wavelet transform to exploit the intra-coil data redundancies and a joint sparsity model to exploit the inter-coil data redundancies. In this work, we propose to stack all the coil images into a three-dimensional (3D) matrix, and then a novel 3D Walsh transform-based sparsity basis is applied to simultaneously reduce the intra-coil and inter-coil data redundancies. Both the 2D Wavelet transform-based and the proposed 3D Walsh transform-based sparsity bases were investigated in the l1-SPIRiT method. The experimental results show that the proposed 3D Walsh transform-based l1-SPIRiT method outperformed the original l1-SPIRiT in terms of image quality and computational efficiency. Copyright © 2014 Elsevier Inc. All rights reserved.

  2. Structural and biochemical characterization of the cell fate determining nucleotidyltransferase fold protein MAB21L1.

    Science.gov (United States)

    de Oliveira Mann, Carina C; Kiefersauer, Reiner; Witte, Gregor; Hopfner, Karl-Peter

    2016-06-08

    The exceptionally conserved metazoan MAB21 proteins are implicated in cell fate decisions and share considerable sequence homology with the cyclic GMP-AMP synthase. cGAS is the major innate immune sensor for cytosolic DNA and produces the second messenger 2'-5', 3'-5' cyclic GMP-AMP. Little is known about the structure and biochemical function of other proteins of the cGAS-MAB21 subfamily, such as MAB21L1, MAB21L2 and MAB21L3. We have determined the crystal structure of human full-length MAB21L1. Our analysis reveals high structural conservation between MAB21L1 and cGAS but also uncovers important differences. Although monomeric in solution, MAB21L1 forms a highly symmetric double-pentameric oligomer in the crystal, raising the possibility that oligomerization could be a feature of MAB21L1. In the crystal, MAB21L1 is in an inactive conformation requiring a conformational change - similar to cGAS - to develop any nucleotidyltransferase activity. Co-crystallization with NTP identified a putative ligand binding site of MAB21 proteins that corresponds to the DNA binding site of cGAS. Finally, we offer a structure-based explanation for the effects of MAB21L2 mutations in patients with eye malformations. The underlying residues participate in fold-stabilizing interaction networks and mutations destabilize the protein. In summary, we provide a first structural framework for MAB21 proteins.

  3. Systemic Immunization with Papillomavirus L1 Protein Completely Prevents the Development of Viral Mucosal Papillomas

    Science.gov (United States)

    Suzich, Joann A.; Ghim, Shin-Je; Palmer-Hill, Frances J.; White, Wendy I.; Tamura, James K.; Bell, Judith A.; Newsome, Joseph A.; Bennett Jenson, A.; Schlegel, Richard

    1995-12-01

    Infection of mucosal epithelium by papillomaviruses is responsible for the induction of genital and oral warts and plays a critical role in the development of human cervical and oropharyngeal cancer. We have employed a canine model to develop a systemic vaccine that completely protects against experimentally induced oral mucosal papillomas. The major capsid protein, L1, of canine oral papillomavirus (COPV) was expressed in Sf9 insect cells in native conformation. L1 protein, which self-assembled into virus-like particles, was purified on CsCl gradients and injected intradermally into the foot pad of beagles. Vaccinated animals developed circulating antibodies against COPV and became completely resistant to experimental challenge with COPV. Successful immunization was strictly dependent upon native L1 protein conformation and L1 type. Partial protection was achieved with as little as 0.125 ng of L1 protein, and adjuvants appeared useful for prolonging the host immune response. Serum immunoglobulins passively transferred from COPV L1-immunized beagles to naive beagles conferred protection from experimental infection with COPV. Our results indicate the feasibility of developing a human vaccine to prevent mucosal papillomas, which can progress to malignancy.

  4. Homozygous YME1L1 mutation causes mitochondriopathy with optic atrophy and mitochondrial network fragmentation.

    Science.gov (United States)

    Hartmann, Bianca; Wai, Timothy; Hu, Hao; MacVicar, Thomas; Musante, Luciana; Fischer-Zirnsak, Björn; Stenzel, Werner; Gräf, Ralph; van den Heuvel, Lambert; Ropers, Hans-Hilger; Wienker, Thomas F; Hübner, Christoph; Langer, Thomas; Kaindl, Angela M

    2016-08-06

    Mitochondriopathies often present clinically as multisystemic disorders of primarily high-energy consuming organs. Assembly, turnover, and surveillance of mitochondrial proteins are essential for mitochondrial function and a key task of AAA family members of metalloproteases. We identified a homozygous mutation in the nuclear encoded mitochondrial escape 1-like 1 gene YME1L1, member of the AAA protease family, as a cause of a novel mitochondriopathy in a consanguineous pedigree of Saudi Arabian descent. The homozygous missense mutation, located in a highly conserved region in the mitochondrial pre-sequence, inhibits cleavage of YME1L1 by the mitochondrial processing peptidase, which culminates in the rapid degradation of YME1L1 precursor protein. Impaired YME1L1 function causes a proliferation defect and mitochondrial network fragmentation due to abnormal processing of OPA1. Our results identify mutations in YME1L1 as a cause of a mitochondriopathy with optic nerve atrophy highlighting the importance of YME1L1 for mitochondrial functionality in humans.

  5. Homozygous YME1L1 mutation causes mitochondriopathy with optic atrophy and mitochondrial network fragmentation

    Science.gov (United States)

    Hartmann, Bianca; Wai, Timothy; Hu, Hao; MacVicar, Thomas; Musante, Luciana; Fischer-Zirnsak, Björn; Stenzel, Werner; Gräf, Ralph; van den Heuvel, Lambert; Ropers, Hans-Hilger; Wienker, Thomas F; Hübner, Christoph; Langer, Thomas; Kaindl, Angela M

    2016-01-01

    Mitochondriopathies often present clinically as multisystemic disorders of primarily high-energy consuming organs. Assembly, turnover, and surveillance of mitochondrial proteins are essential for mitochondrial function and a key task of AAA family members of metalloproteases. We identified a homozygous mutation in the nuclear encoded mitochondrial escape 1-like 1 gene YME1L1, member of the AAA protease family, as a cause of a novel mitochondriopathy in a consanguineous pedigree of Saudi Arabian descent. The homozygous missense mutation, located in a highly conserved region in the mitochondrial pre-sequence, inhibits cleavage of YME1L1 by the mitochondrial processing peptidase, which culminates in the rapid degradation of YME1L1 precursor protein. Impaired YME1L1 function causes a proliferation defect and mitochondrial network fragmentation due to abnormal processing of OPA1. Our results identify mutations in YME1L1 as a cause of a mitochondriopathy with optic nerve atrophy highlighting the importance of YME1L1 for mitochondrial functionality in humans. DOI: http://dx.doi.org/10.7554/eLife.16078.001 PMID:27495975

  6. Effects of Larval Density on Gene Regulation in Caenorhabditis elegans During Routine L1 Synchronization.

    Science.gov (United States)

    Chan, Io Long; Rando, Oliver J; Conine, Colin C

    2018-05-04

    Bleaching gravid C. elegans followed by a short period of starvation of the L1 larvae is a routine method performed by worm researchers for generating synchronous populations for experiments. During the process of investigating dietary effects on gene regulation in L1 stage worms by single-worm RNA-Seq, we found that the density of resuspended L1 larvae affects expression of many mRNAs. Specifically, a number of genes related to metabolism and signaling are highly expressed in worms arrested at low density, but are repressed at higher arrest densities. We generated a GFP reporter strain based on one of the most density-dependent genes in our dataset - lips-15 - and confirmed that this reporter was expressed specifically in worms arrested at relatively low density. Finally, we show that conditioned media from high density L1 cultures was able to downregulate lips-15 even in L1 animals arrested at low density, and experiments using daf-22 mutant animals demonstrated that this effect is not mediated by the ascaroside family of signaling pheromones. Together, our data implicate a soluble signaling molecule in density sensing by L1 stage C. elegans , and provide guidance for design of experiments focused on early developmental gene regulation. Copyright © 2018 Chan et al.

  7. Asynchronous L1-gain control of uncertain switched positive linear systems with dwell time.

    Science.gov (United States)

    Li, Yang; Zhang, Hongbin

    2018-04-01

    In this paper, dwell time (DT) stability, L 1 -gain performance analysis and asynchronous L 1 -gain controller design problems of uncertain switched positive linear systems (SPLSs) are investigated. Via a time-scheduled multiple linear co-positive Lyapunov function (TSMLCLF) approach, convex sufficient conditions of DT stability and L 1 -gain performance of SPLSs with interval and polytopic uncertainties are presented. Furthermore, by utilizing the feature that the TSMLCLF keeps decreasing even if the controller is running asynchronously with the system, the asynchronous L 1 -gain controller design problem of SPLSs with interval and polytopic uncertainties is investigated. Convex sufficient conditions of the existence of time-varying asynchronous state-feedback controller which can ensure the closed-loop system's positivity, stability and L 1 -gain performance are established, and the controller gain matrices can be calculated instantaneously online. The obtained L 1 -gain in the paper is standard. All the results are presented in terms of linear programming. A practical example is provided to show the effectiveness of the results. Copyright © 2018 ISA. Published by Elsevier Ltd. All rights reserved.

  8. Methanol adsorption on Pt(111)

    International Nuclear Information System (INIS)

    Melo, A.V.; Chottiner, G.S.; Hoffman, R.W.; O'Grady, W.E.

    1984-12-01

    High resolution electron energy loss spectroscopy has been used to study the decomposition of methanol on a Pt(111) surface. Several intermediate states in the decomposition are identified by quenching the sample when reactions occur. At 100 K a set of peaks at 800, 1040, 1350, and 2890 cm -1 indicates the presence of a multilayer molecularly adsorbed methanol. As the sample is warmed to 130 K peaks develop at 1700 and 2780 cm -1 , suggesting the formation of formaldehyde on the surface. With further heating, peaks grow at 1820 and 2560 cm -1 due to the formation of a formyl species during the decomposition of methanol over Pt(111). Further heating leads to the final conversion of the surface species to adsorbed CO and carbonaceous residues

  9. Features of dielectric response in PMN-PT ferroelectric ceramics

    International Nuclear Information System (INIS)

    Guerra, J D S; Araujo, E B; Guarany, C A; Reis, R N; Lima, E C

    2008-01-01

    In this paper, electrical and structural properties were reported for pyrochlore free (1 - x)[Pb(Mg 1/3 Nb 2/3 )O 3 ] - xPbTiO 3 (PMN-PT) (with 35 mol% PbTiO 3 ) ceramics obtained from fine powders. Dielectric studies were focused on the investigation of the complex dielectric permittivity (ε' - iε'') as a function of frequency and temperature. The effects of the dc applied electric field on dielectric response were also investigated. Results revealed a field dependence dielectric anomaly in the dielectric permittivity curves (ε(T)) in the low dc electric field region, which in turn prevails in the whole analysed frequency interval. To the best of our knowledge, these properties for the PMN-PT ceramic system have not been reported before as in this work. The results were analysed within the framework of the current models found in the literature.

  10. Influence of cobalt content on the structure and hard magnetic properties of nanocomposite (Fe,Co)-Pt-B alloys

    Energy Technology Data Exchange (ETDEWEB)

    Grabias, A., E-mail: agnieszka.grabias@itme.edu.pl [Institute of Electronic Materials Technology, Wólczyńska 133, 01-919 Warsaw (Poland); Kopcewicz, M. [Institute of Electronic Materials Technology, Wólczyńska 133, 01-919 Warsaw (Poland); Latuch, J.; Oleszak, D. [Faculty of Materials Science and Engineering, Warsaw University of Technology, Wołoska 141, 02-507 Warsaw (Poland); Pękała, M. [Department of Chemistry, University of Warsaw, Al. Żwirki i Wigury 101, 02-089 Warsaw (Poland); Kowalczyk, M. [Faculty of Materials Science and Engineering, Warsaw University of Technology, Wołoska 141, 02-507 Warsaw (Poland)

    2017-07-15

    Highlights: • Nanocomposite alloys were formed by annealing of the rapidly quenched alloys. • Magnetically hard L1{sub 0} (Fe,Co)Pt and soft (Fe,Co){sub 2}B or (Fe,Co)B were formed. • Mössbauer spectra revealed Co substitution for Fe in L1{sub 0} FePt, FeB and Fe{sub 2}B phases. • Annealed alloys exhibit hard magnetic properties which depend on phase compositions. • Co addition was found to decrease the magnetization and the energy product. - Abstract: The influence of Co content on the structural and hard magnetic properties of two sets of nanocrystalline Fe{sub 52−x}Co{sub x}Pt{sub 28}B{sub 20} (x = 0–26) and Fe{sub 60−y}Co{sub y}Pt{sub 25}B{sub 15} (y = 0–40) alloys was studied. The alloys were prepared as ribbons by the rapid quenching technique. The nanocomposite structure in the alloys was obtained by annealing at 840–880 K for 30 min. Structural characterization of the samples was performed using the Mössbauer spectroscopy and X-ray diffraction. Magnetic properties of the samples were studied by the measurements of the hysteresis loops and of the magnetization at increasing temperatures. An amorphous phase prevailed in the as-quenched Fe{sub 52−x}Co{sub x}Pt{sub 28}B{sub 20} alloys while a disordered solid solution of fcc-(Fe,Co)Pt was a dominating phase in the Fe{sub 60−y}Co{sub y}Pt{sub 25}B{sub 15} ribbons. Differential scanning calorimetry measurements revealed one or two exothermic peaks at temperatures up to 993 K, depending on the composition of the alloys. Thermal treatment of the samples led to the formation of the magnetically hard ordered L1{sub 0} tetragonal (Fe,Co)Pt nanocrystallites and magnetically softer phases of (Fe,Co)B (for Fe{sub 52−x}Co{sub x}Pt{sub 28}B{sub 20}) or (Fe,Co){sub 2}B (for Fe{sub 60−y}Co{sub y}Pt{sub 25}B{sub 15}). Detailed Mössbauer spectroscopy studies revealed that cobalt substituted for iron in both the L1{sub 0} phase and in iron borides. The nanocomposite Fe{sub 60−y}Co{sub y}Pt

  11. Synthesis and Characterization of Pt-Ag Alloy Nanocages with Enhanced Activity and Durability toward Oxygen Reduction.

    Science.gov (United States)

    Yang, Xuan; Roling, Luke T; Vara, Madeline; Elnabawy, Ahmed O; Zhao, Ming; Hood, Zachary D; Bao, Shixiong; Mavrikakis, Manos; Xia, Younan

    2016-10-12

    Engineering the elemental composition of metal nanocrystals offers an effective strategy for the development of catalysts or electrocatalysts with greatly enhanced activity. Herein, we report the synthesis of Pt-Ag alloy nanocages with an outer edge length of 18 nm and a wall thickness of about 3 nm. Such nanocages with a composition of Pt 19 Ag 81 could be readily prepared in one step through the galvanic replacement reaction between Ag nanocubes and a Pt(II) precursor. After 10 000 cycles of potential cycling in the range of 0.60-1.0 V as in an accelerated durability test, the composition of the nanocages changed to Pt 56 Ag 44 , together with a specific activity of 1.23 mA cm -2 toward oxygen reduction, which was 3.3 times that of a state-of-the-art commercial Pt/C catalyst (0.37 mA cm -2 ) prior to durability testing. Density functional theory calculations attributed the increased activity to the stabilization of the transition state for breaking the O-O bond in molecular oxygen. Even after 30 000 cycles of potential cycling, the mass activity of the nanocages only dropped from 0.64 to 0.33 A mg -1 Pt , which was still about two times that of the pristine Pt/C catalyst (0.19 A mg -1 Pt ).

  12. Inhibitory effects of ethyl acetate-soluble fraction from morus alba on lipid accumulation in 3T3-L1 cells.

    Science.gov (United States)

    Park, Hee-Sook; Shim, Soon-Mi; Kim, Gun-Hee

    2013-11-01

    Fruits of mulberry (Morus alba) have been widely used for therapeutic purposes in Asian countries for centuries. Treatment of 3T3-L1 cells with ethanolic extracts of M. alba decreased adipocyte differentiation at 100 microg/mL by 18.6%. Treatment suppressed mRNA levels of PPARgamma and C/EBPalpha expression in 3T3-L1 cells. However, the extract did not change free glycerol release from mature adipocytes. Thus, M. alba inhibited lipid accumulation by regulating transcription factors in 3T3-L1 adipocytes without a lipolytic effect. Among the soluble- fractions, the ethyl acetate-soluble fraction had the highest antiadipogenic effects on 3T3-L1 cells. This fraction decreasing intracellular lipid accumulation by 38.5% in response to treatment with 100 microg/mL. In addition, HPLC analysis of the ethyl acetate-soluble fraction of M. alba contained 167.7 microM of protocatechulic acid in 1 mg/mL of fraction, which inhibited lipid accumulation by 44.8% in response to treatment with 100 microM. From these results, M. alba is a possible candidate for regulating lipid accumulation in obesity.

  13. Electronic structures of PtCu, PtAg, and PtAu molecules: a Dirac four-component relativistic study

    International Nuclear Information System (INIS)

    Abe, Minori; Mori, Sayaka; Nakajima, Takahito; Hirao, Kimihiko

    2005-01-01

    Relativistic four-component calculations at several correlated levels have been performed for diatomic PtCu, PtAg, and PtAu molecules. The ground state spectroscopic constants of PtCu were calculated using the four-component MP2 method, and show good agreement with experiment. We also performed calculations on the experimentally unknown species, PtAg and PtAu, and the mono-cationic systems, PtCu + , PtAg + , and PtAu + . The low-lying excited states of these diatomic molecules were also investigated using the four-component multi-reference CI method

  14. Controlled Synthesis of Pt Nanowires with Ordered Large Mesopores for Methanol Oxidation Reaction

    Science.gov (United States)

    Zhang, Chengwei; Xu, Lianbin; Yan, Yushan; Chen, Jianfeng

    2016-08-01

    Catalysts for methanol oxidation reaction (MOR) are at the heart of key green-energy fuel cell technology. Nanostructured Pt materials are the most popular and effective catalysts for MOR. Controlling the morphology and structure of Pt nanomaterials can provide opportunities to greatly increase their activity and stability. Ordered nanoporous Pt nanowires with controlled large mesopores (15, 30 and 45 nm) are facilely fabricated by chemical reduction deposition from dual templates using porous anodic aluminum oxide (AAO) membranes with silica nanospheres self-assembled in the channels. The prepared mesoporous Pt nanowires are highly active and stable electrocatalysts for MOR. The mesoporous Pt nanowires with 15 nm mesopores exhibit a large electrochemically active surface area (ECSA, 40.5 m2 g-1), a high mass activity (398 mA mg-1) and specific activity (0.98 mA cm-2), and a good If/Ib ratio (1.15), better than the other mesoporous Pt nanowires and the commercial Pt black catalyst.

  15. SFG study of the ethanol in an acidic medium--Pt(110) interface: effects of the alcohol concentration.

    Science.gov (United States)

    Gomes, Janaina F; Busson, Bertrand; Tadjeddine, Abderrahmane

    2006-03-23

    Ethanol in an acidic solution-Pt(110) interface was studied by SFG spectroscopy (between 1820 and 2325 cm(-1)) to explore primarily the effects of the alcohol concentration. Stretching bands of H-Pt (ca. 1970 or 2050 cm(-1)) and CO (ca. 1980 and 2040 cm(-1)) species, produced by the ethanol oxidation, were detected during the adsorption and oxidation of 0-1 mol L(-1) ethanol in a 0.1 mol L(-1) HClO(4) solution on the electrode surface. Hydrogen and CO coadsorb stably on Pt(110) between 0.05 and 0.15 V in ethanol-containing solutions. In this potential range, the blue shift of the hydrogen resonance (ca. 80 cm(-1)) reveals a weakening of the hydrogen bonding between adsorbed hydrogen and water molecules in the double layer. After the hydrogen desorption (0.15 V), the formation of compact CO islands, depending on the ethanol concentration, lifts the Pt(110) surface reconstruction. In ethanol-free solution, the surface remains reconstructed. The lower-frequency CO band is assigned to the CO species adsorbed on (1 x 2) reconstructed Pt(110) domains, having smaller local coverages, while the higher-frequency CO band is attributed to the close-packed CO species adsorbed on (1 x 1) patches. The reaction pathway forming CO(2) is less favored with increasing ethanol concentration.

  16. Effect of sputter pressure on magnetotransport properties of FePt nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Mi, Shu, E-mail: mishu@buaa.edu.cn; Liu, Rui, E-mail: liurui1987@buaa.edu.cn; Li, Yuanyuan, E-mail: buaaliyuan@163.com; Ye, Jun, E-mail: yejun@iphy.ac.cn; Xie, Yong, E-mail: xiey@buaa.edu.cn; Chen, Ziyu, E-mail: chenzy@buaa.edu.cn

    2016-04-01

    FePt films were prepared by magnetron sputtering deposition using Ar as the sputtering gas under different working pressures (0.3–0.7 Pa). The effect of sputtering gas pressure on the microstructure, magnetic, and magnetoresistance properties has been investigated. The results show that the crystallization of FePt films is strongly dependent on the Ar sputter pressure. With the decrease of Ar working pressures, the fct phase forms and the coercivity (Hc) of FePt films rises under the same annealing temperature. As a result, the giant magnetoresistance (GMR) increases by 20% at the room temperature. At 0.7 Pa, the anisotropy magnetoresistance (AMR) can be observed clearly at a low field. However, as the Ar pressure decreases, the increase of GMR leads to a degradation of AMR effect. We believe that the improvement of GMR effect results from the increase of magnetic anisotropy and spin polarization in the process of transformation from the soft magnetic fcc phase to the hard magnetic fct phase. - Highlights: • FePt films were sputtered under different Ar working pressures. • The low Ar pressure promotes the formation of L1{sub 0} phase. • The Hc of FePt films enlarges with the reduction of Ar pressure. • As the Ar pressure decreases, the MR increases by 20%. • The total MR results from the competition of GMR and AMR.

  17. Effect of sputter pressure on magnetotransport properties of FePt nanocomposites

    International Nuclear Information System (INIS)

    Mi, Shu; Liu, Rui; Li, Yuanyuan; Ye, Jun; Xie, Yong; Chen, Ziyu

    2016-01-01

    FePt films were prepared by magnetron sputtering deposition using Ar as the sputtering gas under different working pressures (0.3–0.7 Pa). The effect of sputtering gas pressure on the microstructure, magnetic, and magnetoresistance properties has been investigated. The results show that the crystallization of FePt films is strongly dependent on the Ar sputter pressure. With the decrease of Ar working pressures, the fct phase forms and the coercivity (Hc) of FePt films rises under the same annealing temperature. As a result, the giant magnetoresistance (GMR) increases by 20% at the room temperature. At 0.7 Pa, the anisotropy magnetoresistance (AMR) can be observed clearly at a low field. However, as the Ar pressure decreases, the increase of GMR leads to a degradation of AMR effect. We believe that the improvement of GMR effect results from the increase of magnetic anisotropy and spin polarization in the process of transformation from the soft magnetic fcc phase to the hard magnetic fct phase. - Highlights: • FePt films were sputtered under different Ar working pressures. • The low Ar pressure promotes the formation of L1 0 phase. • The Hc of FePt films enlarges with the reduction of Ar pressure. • As the Ar pressure decreases, the MR increases by 20%. • The total MR results from the competition of GMR and AMR.

  18. Fabrication, morphological, structural and magnetic properties of electrodeposited Fe{sub 3}Pt nanowires and nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Khan, U. [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190 (China); Adeela, N. [Centre for High Energy Physics, University of the Punjab, Lahore 54000 (Pakistan); Li, Wenjing; Irfan, M.; Javed, K.; Riaz, S. [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190 (China); Han, X.F., E-mail: xfhan@iphy.ac.cn [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190 (China)

    2017-02-15

    Highly ordered Fe{sub 3}Pt nanowires (NWs) and nanotubes (NTs) embedded in anodic aluminum oxide (AAO) template have been fabricated by dc electrodeposition method. Response of heat treatment on structural and magnetic properties of the samples has been studied with and without the presence of magnetic field (1 T). X-Ray Diffraction analysis shows chemically ordered L1{sub 2} face centered cubic (FCC) as the dominant phase for Fe{sub 3}Pt NWs and heat treatment improves crystallinity with retained its phase. Whereas, Fe{sub 3}Pt NTs show amorphous behavior with and without magnetic field annealing. Furthermore, magnetic properties of the samples have been investigated by vibrating sample magnetometer (VSM). Magnetic parameters of Fe{sub 3}Pt including magnetic coercivity, saturation magnetization, squareness and shape of MH-loops have been investigated as a result of simple and MF annealing. - Highlights: • Fe{sub 3}Pt NWs and NTs embedded into anodic alumina templates have been synthesized by dc electrodeposition method. • Structural analysis (XRD) confirmed the formation of fcc structure. • Magnetic properties have been measured as a function of simple and magnetic field annealing.

  19. Effect of boron addition on the structure and magnetic properties of CoPt nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Khemjeen, Yutthaya [Materials Science and Nanotechnology Program, Faculty of Science, Khon Kaen University, Khon Kaen 40002 (Thailand); Pinitsoontorn, Supree, E-mail: psupree@kku.ac.th; Chompoosor, Apiwat [Department of Physics, Faculty of Science, Khon Kaen University, Khon Kaen 40002 (Thailand); Integrated Nanotechnology Research Center, Khon Kaen University, Khon Kaen 40002 (Thailand); Nanotec-KKU Center of Excellence on Advanced Nanomaterials for Energy Production and Storage, Khon Kaen University, Khon Kaen 40002 (Thailand)

    2015-05-07

    The effect of B addition on CoPt nanoparticles was investigated. The CoPt-B nanoparticles were synthesized by means of the polyol process. Transmission electron microscopy has shown that the as-synthesized particles have a spherical morphology with average size about 2–3 nm. The X-ray absorption spectroscopy and the X-ray diffraction technique showed the effect of B concentration on phase transformation. The addition of B at up to 60% promoted the formation of the L1{sub 0} phase when the nanoparticles were subjected to annealing at 600 °C. If the B content is higher than 60%, the phase transition is suppressed. The evidence of B addition on the structure of CoPt nanoparticles was further supported by the magnetic measurements. The results show that the coercivity of the annealed CoPt-B nanoparticles was enhanced by the B additions from 20% to 60%, with the maximum coercivity of 12 000 Oe for the CoPt-40%B sample.

  20. Engineering Ru@Pt Core-Shell Catalysts for Enhanced Electrochemical Oxygen Reduction Mass Activity and Stability

    Directory of Open Access Journals (Sweden)

    Ariel Jackson

    2018-01-01

    Full Text Available Improving the performance of oxygen reduction reaction (ORR electrocatalysts is essential for the commercial efficacy of many renewable energy technologies, including low temperature polymer electrolyte fuel cells (PEFCs. Herein, we report highly active and stable carbon-supported Ru@Pt core-shell nanoparticles (Ru@Pt/C prepared by a wet chemical synthesis technique. Through rotating disc electrode testing, the Ru@Pt/C achieves an ORR Pt mass-based activity of 0.50 A mgPt−1 at 0.9 V versus the reversible hydrogen electrode (RHE, which exceeds the activity of the state-of-the-art commercial Pt/C catalyst as well as the Department of Energy 2020 PEFC electrocatalyst activity targets for transportation applications. The impact of various synthetic parameters, including Pt to Ru ratios and catalyst pretreatments (i.e., annealing are thoroughly explored. Pt-based mass activity of all prepared Ru@Pt/C catalysts was found to exceed 0.4 mgPt−1 across the range of compositions investigated, with the maximum activity catalyst having a Ru:Pt ratio of 1:1. This optimized composition of Ru@Pt/C catalyst demonstrated remarkable stability after 30,000 accelerated durability cycles (0.6 to 1.0 V vs. RHE at 125 mV s−1, maintaining 85% of its initial mass activity. Scanning transmission electron microscopy energy dispersive spectroscopy (STEM-EDS analysis at various stages of electrochemical testing demonstrated that the Pt shell can provide sufficient protection against the dissolution of the otherwise unstable Ru core.

  1. Reversibility of Pt-Skin and Pt-Skeleton Nanostructures in Acidic Media.

    Science.gov (United States)

    Durst, Julien; Lopez-Haro, Miguel; Dubau, Laetitia; Chatenet, Marian; Soldo-Olivier, Yvonne; Guétaz, Laure; Bayle-Guillemaud, Pascale; Maillard, Frédéric

    2014-02-06

    Following a well-defined series of acid and heat treatments on a benchmark Pt3Co/C sample, three different nanostructures of interest for the electrocatalysis of the oxygen reduction reaction were tailored. These nanostructures could be sorted into the "Pt-skin" structure, made of one pure Pt overlayer, and the "Pt-skeleton" structure, made of 2-3 Pt overlayers surrounding the Pt-Co alloy core. Using a unique combination of high-resolution aberration-corrected STEM-EELS, XRD, EXAFS, and XANES measurements, we provide atomically resolved pictures of these different nanostructures, including measurement of the Pt-shell thickness forming in acidic media and the resulting changes of the bulk and core chemical composition. It is shown that the Pt-skin is reverted toward the Pt-skeleton upon contact with acid electrolyte. This change in structure causes strong variations of the chemical composition.

  2. PT AND PT/NI "NEEDLE" ELETROCATALYSTS ON CARBON NANOTUBES WITH HIGH ACTIVITY FOR THE ORR

    Energy Technology Data Exchange (ETDEWEB)

    Colon-Mercado, H.

    2011-11-10

    Platinum and platinum/nickel alloy electrocatalysts supported on graphitized (gCNT) or nitrogen doped carbon nanotubes (nCNT) are prepared and characterized. Pt deposition onto carbon nanotubes results in Pt 'needle' formations that are 3.5 nm in diameter and {approx}100 nm in length. Subsequent Ni deposition and heat treatment results in PtNi 'needles' with an increased diameter. All Pt and Pt/Ni materials were tested as electrocatalysts for the oxygen reduction reaction (ORR). The Pt and Pt/Ni catalysts showed excellent performance for the ORR, with the heat treated PtNi/gCNT (1.06 mA/cm{sup 2}) and PtNi/nCNT (0.664 mA/cm{sup 2}) showing the highest activity.

  3. UCH-L1-containing exosomes mediate chemotherapeutic resistance transfer in breast cancer.

    Science.gov (United States)

    Ning, Kuan; Wang, Teng; Sun, Xu; Zhang, Pengfei; Chen, Yun; Jin, Jian; Hua, Dong

    2017-06-01

    Chemotherapy resistance has become a serious challenge in the treatment of breast cancer. Previous studies showed cells can transfer proteins, including those responsible for drug resistance to adjacent cells via exosomes. The switches of drug resistance via exosomes transfer were assessed by CellTiter-Blue Viability assay, flow cytometry, and immunostaining analysis. Relative protein levels of Ubiquitin carboxyl terminal hydrolase-L1 (UCH-L1), P-glycoprotein (P-gp), extracellular-signal regulated protein kinase1/2 (ERK1/2), and phospho-extracellular-signal regulated protein kinase1/2 (p-ERK1/2) were measured by Western blot. Immunohistochemistry was performed on 93 breast cancer samples to assess the associations of UCH-L1 levels with immunofluorescence value of UCH-L1 in circulating exosomes. The Adriamycin-resistant human breast cancer cells (MCF7/ADM) secreted exosomes carrying UCH-L1 and P-gp proteins into the extracellular microenvironment then integrated into Adriamycin-sensitive human breast cancer cells (MCF7/WT) in a time-dependent manner, transferring the chemoresistance phenotype. Notably, in blood samples from patients with breast cancer, the level of exosomes carrying UCH-L1 before chemotherapy was significantly negatively correlated with prognosis. Our study demonstrated that UCH-L1-containing exosomes can transfer chemoresistance to recipient cells and these exosomes may be useful as non-invasive diagnostic biomarkers for detection of chemoresitance in breast cancer patients, achieving more effective and individualized chemotherapy. © 2017 Wiley Periodicals, Inc.

  4. OmpL1 is an extracellular matrix- and plasminogen-interacting protein of Leptospira spp.

    Science.gov (United States)

    Fernandes, Luis G V; Vieira, Monica L; Kirchgatter, Karin; Alves, Ivy J; de Morais, Zenaide M; Vasconcellos, Silvio A; Romero, Eliete C; Nascimento, Ana L T O

    2012-10-01

    Leptospirosis is a zoonosis with multisystem involvement caused by pathogenic strains of the genus Leptospira. OmpL1 is an outer membrane protein of Leptospira spp. that is expressed during infection. In this work, we investigated novel features of this protein. We describe that OmpL1 is a novel leptospiral extracellular matrix (ECM)-binding protein and a plasminogen (PLG) receptor. The recombinant protein was expressed in Escherichia coli BL21(DE3) Star/pLysS as inclusion bodies, refolded, and purified by metal-chelating chromatography. The protein presented a typical β-strand secondary structure, as evaluated by circular dichroism spectroscopy. The recombinant protein reacted with antibodies in serum samples from convalescent leptospirosis patients with a high specificity compared to serum samples from individuals with unrelated diseases. These data strengthen the usefulness of OmpL1 as a diagnostic marker of leptospirosis. The characterization of the immunogenicity of recombinant OmpL1 in inoculated BALB/c mice showed that the protein has the capacity to elicit humoral and cellular immune responses, as denoted by high antibody titers and the proliferation of lymphocytes. We demonstrate that OmpL1 has the ability to mediate attachment to laminin and plasma fibronectin, with K(D) (equilibrium dissociation constant) values of 2,099.93 ± 871.03 nM and 1,239.23 ± 506.85 nM, respectively. OmpL1 is also a PLG receptor, with a K(D) of 368.63 ± 121.23 nM, capable of generating enzymatically active plasmin. This is the first report that shows and characterizes OmpL1 as an ECM-interacting and a PLG-binding protein of Leptospira spp. that may play a role in bacterial pathogenesis when expressed during infection.

  5. L1-norm locally linear representation regularization multi-source adaptation learning.

    Science.gov (United States)

    Tao, Jianwen; Wen, Shiting; Hu, Wenjun

    2015-09-01

    In most supervised domain adaptation learning (DAL) tasks, one has access only to a small number of labeled examples from target domain. Therefore the success of supervised DAL in this "small sample" regime needs the effective utilization of the large amounts of unlabeled data to extract information that is useful for generalization. Toward this end, we here use the geometric intuition of manifold assumption to extend the established frameworks in existing model-based DAL methods for function learning by incorporating additional information about the target geometric structure of the marginal distribution. We would like to ensure that the solution is smooth with respect to both the ambient space and the target marginal distribution. In doing this, we propose a novel L1-norm locally linear representation regularization multi-source adaptation learning framework which exploits the geometry of the probability distribution, which has two techniques. Firstly, an L1-norm locally linear representation method is presented for robust graph construction by replacing the L2-norm reconstruction measure in LLE with L1-norm one, which is termed as L1-LLR for short. Secondly, considering the robust graph regularization, we replace traditional graph Laplacian regularization with our new L1-LLR graph Laplacian regularization and therefore construct new graph-based semi-supervised learning framework with multi-source adaptation constraint, which is coined as L1-MSAL method. Moreover, to deal with the nonlinear learning problem, we also generalize the L1-MSAL method by mapping the input data points from the input space to a high-dimensional reproducing kernel Hilbert space (RKHS) via a nonlinear mapping. Promising experimental results have been obtained on several real-world datasets such as face, visual video and object. Copyright © 2015 Elsevier Ltd. All rights reserved.

  6. New Method to Synthesize Highly Active and Durable Chemically Ordered fct-PtCo Cathode Catalyst for PEMFCs.

    Science.gov (United States)

    Jung, Won Suk; Popov, Branko N

    2017-07-19

    In the bottom-up synthesis strategy performed in this study, the Co-catalyzed pyrolysis of chelate-complex and activated carbon black at high temperatures triggers the graphitization reaction which introduces Co particles in the N-doped graphitic carbon matrix and immobilizes N-modified active sites for the oxygen reduction reaction (ORR) on the carbon surface. In this study, the Co particles encapsulated within the N-doped graphitic carbon shell diffuse up to the Pt surface under the polymer protective layer and forms a chemically ordered face-centered tetragonal (fct) Pt-Co catalyst PtCo/CCCS catalyst as evidenced by structural and compositional studies. The fct-structured PtCo/CCCS at low-Pt loading (0.1 mg Pt cm -2 ) shows 6% higher power density than that of the state-of-the-art commercial Pt/C catalyst. After the MEA durability test of 30 000 potential cycles, the performance loss of the catalyst is negligible. The electrochemical surface area loss is less than 40%, while that of commercial Pt/C is nearly 80%. After the accelerated stress test, the uniform catalyst distribution is retained and the mean particle size increases approximate 1 nm. The results obtained in this study indicated that highly stable compositional and structural properties of chemically ordered PtCo/CCCS catalyst contribute to its exceptional catalyst durability.

  7. Metamorphic reprocessing of a serpentinized carbonate-bearing peridotite after detachment from the mantle wedge: A P-T path constrained from textures and phase diagrams in the system CaO-MgO-Al 2O 3-SiO 2-CO 2-H 2O

    Science.gov (United States)

    Mposkos, E.; Baziotis, I.; Proyer, A.

    2010-08-01

    In the central Rhodope mountains of Greece a carbonate-bearing metaperidotite lens ˜ 200 × 500 m in size crops out as part of the high- to ultrahigh-pressure metamorphic Upper Sidironero Complex ˜ 500 m SE of the Gorgona Village, north of Xanthi town. It is composed primarily of coarse grained (3-20 mm in size) olivine and orthopyroxene, medium grained clinohumite and medium to fine grained tremolite, chlorite, dolomite, magnesite, talc, antigorite and various spinel phases. Whole-rock chemistry, mineral textures and compositions, and phase diagram calculations show that the metaperidotite was subjected to a prograde HP metamorphism, isofacial with the surrounding migmatitic gneisses, metapelites and amphibolites. The prograde character of metamorphism is demonstrated by inclusions of talc, antigorite, chlorite, dolomite, magnesite and Ti-clinohumite in ferrit-chromite, olivine, and orthopyroxene, as well as of olivine in orthopyroxene, and by the typical change in composition of zoned spinel minerals from ferrit-chromite in the core to chromian spinel at the rim. The prograde path is characterized by successive growth of amphibole, Ti-clinohumite, olivine and orthopyroxene, followed by the breakdown of Ti-clinohumite to olivine + Mg-ilmenite and of chlorite to olivine + spinel, probably during exhumation. The construction of a partial petrogenetic P- T grid in the system CaO-MgO-Al 2O 3-SiO 2-CO 2-H 2O (CMASCH) for Ca-poor ultramafic bulk compositions has proven highly useful for the reconstruction of the metamorphic evolution and a P- T path, indicating that the use of univariant reactions in mixed volatile systems is highly warranted. The P- T path is clearly constrained to pressures below 1.5-1.7 GPa by the absence of clinopyroxene. These pressures are slightly lower than those recorded in the closely associated Jurassic eclogites and much lower than those recorded in the diamond-bearing gneisses 5 km to the south in the same tectonic unit. The carbonate

  8. X-band EPR studies of ferroelectric lead titanate (PT), piezoelectric lead magnesium niobate (PMN), and PMN/PT powders at 10 and 85 K

    International Nuclear Information System (INIS)

    Huang, J.; Fitzgerald, J.J.; Chasteen, N.D.

    1998-01-01

    X-band EPR spectra of lead titanate (PT) and lead magnesium niobate (PMN) powders prepared by different synthetic methods and a PMN/PT powder of the composition 0.9 PMN/01 PT were obtained at 85 and 10 K. Several EPR signals due to adventitious Fe 3+ ion impurities, a signal due to the Ti 3+ ion, and a signal due to the Pb 3+ ion are observed for PT, PMN, and PMN/PT powders. The EPR signals observed at g = 2.0 and 6.0 are assigned to Fe 3+ ions in the B-sites of the perovskite lattice structure of lad titanate with axial symmetry. The EPR signals observed at g = 1.99 and 4.25 are assigned to Fe 3+ ions in the B-sites of the perovskite lattice structure of PMN and 0.9 PMN/0.1 PT materials with cubic and rhombic symmetries, respectively. The sharp EPR signal observed at g = 1.94 is assigned to Ti 3= ion for PT and 0.9 PMN/0.1 PT powders. In addition, a broader EPR signal at g = 2.28--2.30 for PMN obtained by the molten salt method is assigned to axial Pb 3+ ion sites in this PMN material. EPR results obtained here for the e 3+ ions in the B-sites of the PMN materials, in particular, suggest that both cubic and rhombic symmetry sites corresponding to a range of Nb(OMg) x (ONb) 6-x site configurations exist in the PMN. These EPR results indicate that PMN likely exists with partial B-site cation (Mg/Nb) ordering in the perovskite lattice structure

  9. Production and characterization of a monoclonal antibody against recombinant cathepsin L1 of Fasciola gigantica.

    Science.gov (United States)

    Anuracpreeda, Panat; Srirakam, Thippawan; Pandonlan, Sudarat; Changklungmoa, Narin; Chotwiwatthanakun, Charoonroj; Tinikul, Yotsawan; Poljaroen, Jaruwan; Meemon, Krai; Sobhon, Prasert

    2014-08-01

    Monoclonal antibodies (MoAbs) against a recombinant cathepsin L1 of Fasciola gigantica (rFgCatL1) were produced in vitro by fusion of BALB/c mice spleen cells immunized with rFgCatL1 and mouse myeloma cells. Reactivity and specificity of these MoAbs were evaluated by indirect ELISA and immunoblotting techniques. Seven MoAb clones were selected from the stable hybridoma clones, namely 1E10, 1F5, 3D11, 4B10, 4D3, 4E3 and 5E7. Clones 1E10, 1F5 and 3D11 were IgM, whereas clones 4B10, 4D3, 4E3 and 5E7 were IgG1. All MoAbs had kappa light chain isotypes. All MoAbs reacted with rCatL1 at molecular weight (MW) 30kDa and with the native CatL1 at MW 27kDa in whole body (WB) extracts of metacercariae (Met), newly excysted juveniles (NEJ), 1, 3, 5-week-old juveniles (Ju), adult WB and adult excretory-secretory (ES) fractions, but not with adult tegumental antigens (TA). All of these MoAbs showed no cross-reactions with antigens of other parasites commonly found in ruminants and human, including Paramphistomum cervi, Eurytrema pancreaticum, Gigantocotyle explanatum, Schistosoma spindale, Schistosoma mansoni, Moniezia benedeni, Avitellina centripunctata, Trichuris sp., Haemonchus placei and Setaria labiato-papillosa. Localization of CatL1 in each developmental stages of F. gigantica by immunoperoxidase technique, using these MoAbs as probes, indicated that CatL1 was present at high concentration in the caecal epithelium and caecal lumen of metacercariae, NEJ, 1, 3, 5-week-old juveniles and adult fluke. This finding indicated that CatL1 is a copiously expressed parasite protein that is released into the ES, thus CatL1 and its MoAb could be a good candidate for immunodiagnosis of fasciolosis in ruminant and human. Copyright © 2014 Elsevier B.V. All rights reserved.

  10. Differential L1 regulation in pluripotent stem cells of humans and apes.

    Science.gov (United States)

    Marchetto, Maria C N; Narvaiza, Iñigo; Denli, Ahmet M; Benner, Christopher; Lazzarini, Thomas A; Nathanson, Jason L; Paquola, Apuã C M; Desai, Keval N; Herai, Roberto H; Weitzman, Matthew D; Yeo, Gene W; Muotri, Alysson R; Gage, Fred H

    2013-11-28

    Identifying cellular and molecular differences between human and non-human primates (NHPs) is essential to the basic understanding of the evolution and diversity of our own species. Until now, preserved tissues have been the main source for most comparative studies between humans, chimpanzees (Pan troglodytes) and bonobos (Pan paniscus). However, these tissue samples do not fairly represent the distinctive traits of live cell behaviour and are not amenable to genetic manipulation. We propose that induced pluripotent stem (iPS) cells could be a unique biological resource to determine relevant phenotypical differences between human and NHPs, and that those differences could have potential adaptation and speciation value. Here we describe the generation and initial characterization of iPS cells from chimpanzees and bonobos as new tools to explore factors that may have contributed to great ape evolution. Comparative gene expression analysis of human and NHP iPS cells revealed differences in the regulation of long interspersed element-1 (L1, also known as LINE-1) transposons. A force of change in mammalian evolution, L1 elements are retrotransposons that have remained active during primate evolution. Decreased levels of L1-restricting factors APOBEC3B (also known as A3B) and PIWIL2 (ref. 7) in NHP iPS cells correlated with increased L1 mobility and endogenous L1 messenger RNA levels. Moreover, results from the manipulation of A3B and PIWIL2 levels in iPS cells supported a causal inverse relationship between levels of these proteins and L1 retrotransposition. Finally, we found increased copy numbers of species-specific L1 elements in the genome of chimpanzees compared to humans, supporting the idea that increased L1 mobility in NHPs is not limited to iPS cells in culture and may have also occurred in the germ line or embryonic cells developmentally upstream to germline specification during primate evolution. We propose that differences in L1 mobility may have

  11. The effect of myostatin on proliferation and lipid accumulation in 3T3-L1 preadipocytes.

    Science.gov (United States)

    Zhu, Hui Juan; Pan, Hui; Zhang, Xu Zhe; Li, Nai Shi; Wang, Lin Jie; Yang, Hong Bo; Gong, Feng Ying

    2015-06-01

    Myostatin is a critical negative regulator of skeletal muscle development, and has been reported to be involved in the progression of obesity and diabetes. In the present study, we explored the effects of myostatin on the proliferation and differentiation of 3T3-L1 preadipocytes by using 3-[4,5-dimethylthiazol-2-yl] 2,5-diphenyl tetrazolium bromide spectrophotometry, intracellular triglyceride (TG) assays, and real-time quantitative RT-PCR methods. The results indicated that recombinant myostatin significantly promoted the proliferation of 3T3-L1 preadipocytes and the expression of proliferation-related genes, including Cyclin B2, Cyclin D1, Cyclin E1, Pcna, and c-Myc, and IGF1 levels in the medium of 3T3-L1 were notably upregulated by 35.2, 30.5, 20.5, 33.4, 51.2, and 179% respectively (all Pmyostatin-treated 3T3-L1 cells. Meanwhile, the intracellular lipid content of myostatin-treated cells was notably reduced as compared with the non-treated cells. Additionally, the mRNA levels of Pparγ, Cebpα, Gpdh, Dgat, Acs1, Atgl, and Hsl were significantly downregulated by 22-76% in fully differentiated myostatin-treated adipocytes. Finally, myostatin regulated the mRNA levels and secretion of adipokines, including Adiponectin, Resistin, Visfatin, and plasminogen activator inhibitor-1 (PAI-1) in 3T3-L1 adipocytes (all Pmyostatin promoted 3T3-L1 proliferation by increasing the expression of cell-proliferation-related genes and by stimulating IGF1 secretion. Myostatin inhibited 3T3-L1 adipocyte differentiation by suppressing Pparγ and Cebpα expression, which consequently deceased lipid accumulation in 3T3-L1 cells by inhibiting the expression of critical lipogenic enzymes and by promoting the expression of lipolytic enzymes. Finally, myostatin modulated the expression and secretion of adipokines in fully differentiated 3T3-L1 adipocytes. © 2015 Society for Endocrinology.

  12. Enhanced activity and interfacial durability study of ultra low Pt based electrocatalysts prepared by ion beam assisted deposition (IBAD) method

    International Nuclear Information System (INIS)

    Ramaswamy, N.; Arruda, T.M.; Wen, W.; Hakim, N.; Saha, M.; Gulla, A.; Mukerjee, S.

    2009-01-01

    Ultra low loading noble metal (0.04-0.12 mg Pt /cm 2 ) based electrodes were obtained by direct metallization of non-catalyzed gas diffusion layers via dual ion beam assisted deposition (IBAD) method. Fuel cell performance results reported earlier indicate significant improvements in terms of mass specific power density of 0.297 g Pt /kW with 250 A thick IBAD deposit (0.04 mg Pt /cm 2 for a total MEA loading of 0.08 mg Pt /cm 2 ) at 0.65 V in contrast to the state of the art power density of 1.18 g Pt /kW using 1 mg Pt(MEA) /cm 2 at 0.65 V. In this article we report the peroxide radical initiated attack of the membrane electrode assembly utilizing IBAD electrodes in comparison to commercially available E-TEK (now BASF Fuel Cell GmbH) electrodes and find the pathway of membrane degradation as well. A novel segmented fuel cell is used for this purpose to relate membrane degradation to peroxide generation at the electrode/electrolyte interface by means of systematic pre and post analyses of the membrane are presented. Also, we present the results of in situ X-ray absorption spectroscopy (XAS) experiments to elucidate the structure/property relationships of these electrodes that lead to superior performance in terms of gravimetric power density obtained during fuel cell operation.

  13. Low Pt content direct methanol fuel cell anode catalyst: nanophase PtRuNiZr

    Science.gov (United States)

    Narayanan, Sekharipuram R. (Inventor); Whitacre, Jay F. (Inventor)

    2010-01-01

    A method for the preparation of a metallic material having catalytic activity that includes synthesizing a material composition comprising a metal content with a lower Pt content than a binary alloy containing Pt but that displays at least a comparable catalytic activity on a per mole Pt basis as the binary alloy containing Pt; and evaluating a representative sample of the material composition to ensure that the material composition displays a property of at least a comparable catalytic activity on a per mole Pt basis as a representative binary alloy containing Pt. Furthermore, metallic compositions are disclosed that possess substantial resistance to corrosive acids.

  14. Results of the Proficiency Test, PT1 and PT2, 2012

    DEFF Research Database (Denmark)

    Vendramin, Niccolò; Nicolajsen, Nicole; Christophersen, Maj-Britt

    A comparative test of diagnostic procedures was provided by the European Union Reference Laboratory (EURL) for Fish Diseases. The test was divided into proficiency test 1 (PT1) and proficiency test 2 (PT2). The number of National Reference Laboratories (NRLs) participating in PT1 and PT2 was 43. ....... The tests were sent from the EURL in the beginning of September 2012. Both PT1 and PT2 are accredited by DANAK under registration number 515 for proficiency testing according to the quality assurance standard DS/EN ISO/IEC 17043....

  15. Robust Non-Local TV-L1 Optical Flow Estimation with Occlusion Detection.

    Science.gov (United States)

    Zhang, Congxuan; Chen, Zhen; Wang, Mingrun; Li, Ming; Jiang, Shaofeng

    2017-06-05

    In this paper, we propose a robust non-local TV-L1 optical flow method with occlusion detection to address the problem of weak robustness of optical flow estimation with motion occlusion. Firstly, a TV-L1 form for flow estimation is defined using a combination of the brightness constancy and gradient constancy assumptions in the data term and by varying the weight under the Charbonnier function in the smoothing term. Secondly, to handle the potential risk of the outlier in the flow field, a general non-local term is added in the TV-L1 optical flow model to engender the typical non-local TV-L1 form. Thirdly, an occlusion detection method based on triangulation is presented to detect the occlusion regions of the sequence. The proposed non-local TV-L1 optical flow model is performed in a linearizing iterative scheme using improved median filtering and a coarse-to-fine computing strategy. The results of the complex experiment indicate that the proposed method can overcome the significant influence of non-rigid motion, motion occlusion, and large displacement motion. Results of experiments comparing the proposed method and existing state-of-the-art methods by respectively using Middlebury and MPI Sintel database test sequences show that the proposed method has higher accuracy and better robustness.

  16. Generation and Nuclear Translocation of Sumoylated Transmembrane Fragment of Cell Adhesion Molecule L1

    Science.gov (United States)

    Lutz, David; Wolters-Eisfeld, Gerrit; Joshi, Gunjan; Djogo, Nevena; Jakovcevski, Igor; Schachner, Melitta; Kleene, Ralf

    2012-01-01

    The functions of the cell adhesion molecule L1 in the developing and adult nervous system are triggered by homophilic and heterophilic interactions that stimulate signal transductions that activate cellular responses. Here, we show that stimulation of signaling by function-triggering L1 antibodies or L1-Fc leads to serine protease-dependent cleavage of full-length L1 at the plasma membrane and generation of a sumoylated transmembrane 70-kDa fragment comprising the intracellular and transmembrane domains and part of the extracellular domain. The 70-kDa transmembrane fragment is transported from the plasma membrane to a late endosomal compartment, released from endosomal membranes into the cytoplasm, and transferred from there into the nucleus by a pathway that depends on importin and chromatin-modifying protein 1. Mutation of the sumoylation site at Lys1172 or of the nuclear localization signal at Lys1147 abolished L1-stimulated generation or nuclear import of the 70-kDa fragment, respectively. Nuclear import of the 70-kDa fragment may activate cellular responses in parallel or in association with phosphorylation-dependent signaling pathways. Alterations in the levels of the 70-kDa fragment during development and in the adult after spinal cord injury or in a mouse model of Alzheimer disease suggest that this fragment is functionally implicated in development, regeneration, neurodegeneration, tumorigenesis, and possibly synaptic plasticity in the mature nervous system. PMID:22431726

  17. RAC1 P29S regulates PD-L1 expression in melanoma

    Science.gov (United States)

    Vu, Ha Linh; Rosenbaum, Sheera; Purwin, Timothy J.; Davies, Michael A.; Aplin, Andrew E.

    2015-01-01

    Summary Whole exome sequencing of cutaneous melanoma has led to the detection of P29 mutations in RAC1 in 5–9% of samples, but the role of RAC1 P29 mutations in melanoma biology remains unclear. Using reverse phase protein array analysis to examine the changes in protein/phospho-protein expression, we identified cyclin B1, PD-L1, Ets-1, and Syk as being selectively upregulated with RAC1 P29S expression and downregulated with RAC1 P29S depletion. Using the melanoma patient samples in TCGA, we found PD-L1 expression to be significantly increased in RAC1 P29S patients compared to RAC1 WT as well as other RAC1 mutants. The finding that PD-L1 is upregulated suggests that oncogenic RAC1 P29S may promote suppression of the antitumor immune response. This is a new insight into the biological function of RAC1 P29S mutations with potential clinical implications as PD-L1 is a candidate biomarker for increased benefit from treatment with anti-PD1 or anti-PD-L1 antibodies. PMID:26176707

  18. Progress of PD-1/PD-L1 Inhibitors in Non-small Cell Lung Cancer

    Directory of Open Access Journals (Sweden)

    Zhansheng JIANG

    2017-02-01

    Full Text Available Pembrolizumab, an inhibitor target programmed death 1 (PD-1, was approved into the first line therapy in advanced non-small cell lung cancer (NSCLC. It was a milestone that immune checkpoints drugs have played an important role in the treatment system of NSCLC. The results of clinical trials revealed the superiority of PD-1/programmed death ligand 1 (PD-L1 inhibitors compared with chemotherapy in first-line, second-line and multidrug resistance phase therapy. Objective response rate (ORR was up to 80% with pembrolizumab plus chemotherapy, and progression-free survival (PFS with single pembrolizumab in first line was nearly 1 year (10.3 months, the hazard ratio for death fell by 40%. Overall survival (OS was more or less 1 year with single drug pembrolizumab, nivolumab and atezolizumab for second line therapy. PD-L1 expression was a predictor of PD-1/PD-L1 inhibitors. The positive rate of PD-L1 (more than 1% in advanced NSCLC was about 60% with little difference between the tissue types. However, there was no gold standard test of PD-L1 expression.

  19. [Mode of action of plantaricin L-1, an antilisteria bacteriocin produced by Lactobacillus plantarum].

    Science.gov (United States)

    Zhou, Wei; Liu, Guo-rong; Li, Ping-lan; Dai, Yun-qing; Zhou, Kang

    2007-04-01

    Plantaricin L-1, an anti-Listeria bacteriocin, was produced by Lactobacillus plantarum and successfully purified by SP-Sepharose FF cation exchange chromatography. The mechanism on energized cells of Listeria monocytogenes was studied with purified plantaricin L-1. After adding plantaricin L-1 to Listeria monocytogenes at 64 AU/mL, leakage of intercellular K+ ions, inorganic phosphate, lactic dehydrogenase, UV-absorbing materials and the intracellular ATP was observed, and the action resulted in the dissipation of the membrane potential (delta psi) and pH gradient (delta psi), two components of the proton motive force (PMF). All the data suggested that the primary site of action of plantaricin L-1 was the cytoplasmic membrane of sensitive cells. By forming the nonselective pores which leak ions and small organic compounds plantaricin L-1 induced the cells death, this action was similar to membrane corruption caused by peptide effect. Penetrability increased due to the enlarged pore and dysfuction of membrane transporters, which ensured efficient killing of target bacteria.

  20. Wind Turbine Pitch Control and Load Mitigation Using an L1 Adaptive Approach

    Directory of Open Access Journals (Sweden)

    Danyong Li

    2014-01-01

    Full Text Available We present an application of L1 adaptive output feedback control design to wind turbine collective pitch control and load mitigation. Our main objective is the design of an L1 output feedback controller without wind speed estimation, ensuring that the generator speed tracks the reference trajectory with robustness to uncertain parameters and time-varying disturbances (mainly the uniform wind disturbance across the wind turbine rotor. The wind turbine model CART (controls advanced research turbine developed by the national renewable energy laboratory (NREL is used to validate the performance of the proposed L1 adaptive controller using the FAST (fatigue, aerodynamics, structures, and turbulence code. A comparative study is also conducted between the proposed controller and the most popular methods in practice: gain scheduling PI (GSPI controls and disturbance accommodating control (DAC methods. The results show better performance of L1 output feedback controller over the other two methods. Moreover, based on the FAST software and LQR analysis in the reference model selection of L1 adaptive controller, tradeoff can be achieved between control performance and loads mitigation.

  1. Embryonic stem cell self-renewal pathways converge on the transcription factor Tfcp2l1

    Science.gov (United States)

    Ye, Shoudong; Li, Ping; Tong, Chang; Ying, Qi-Long

    2013-01-01

    Mouse embryonic stem cell (mESC) self-renewal can be maintained by activation of the leukaemia inhibitory factor (LIF)/signal transducer and activator of transcription 3 (Stat3) signalling pathway or dual inhibition (2i) of glycogen synthase kinase 3 (Gsk3) and mitogen-activated protein kinase kinase (MEK). Several downstream targets of the pathways involved have been identified that when individually overexpressed can partially support self-renewal. However, none of these targets is shared among the involved pathways. Here, we show that the CP2 family transcription factor Tfcp2l1 is a common target in LIF/Stat3- and 2i-mediated self-renewal, and forced expression of Tfcp2l1 can recapitulate the self-renewal-promoting effect of LIF or either of the 2i components. In addition, Tfcp2l1 can reprogram post-implantation epiblast stem cells to naïve pluripotent ESCs. Tfcp2l1 upregulates Nanog expression and promotes self-renewal in a Nanog-dependent manner. We conclude that Tfcp2l1 is at the intersection of LIF- and 2i-mediated self-renewal pathways and plays a critical role in maintaining ESC identity. Our study provides an expanded understanding of the current model of ground-state pluripotency. PMID:23942238

  2. Passive dosing of triclosan in multi-generation tests with copepods - Stable exposure concentrations and effects at the low µg l-1 range

    DEFF Research Database (Denmark)

    Ribbenstedt, Anton; Mustajärvi, Lukas; Breitholtz, Magnus

    2017-01-01

    to test the applicability of passive dosing to maintain stable concentrations of the organochlorine bacteriocide triclosan in the water phase during a 6-week multi-generation population development test with the harpacticoid copepod Nitocra spinipes. Triclosan was loaded into silicone (1000 mg), which...... was used as passive dosing phase in the exposure vials. The distribution ratio for triclosan between silicone and water (Dsilicone-water ) was 10466 ± 1927. A population development test was conducted at three concentration levels of triclosan that were measured to be 3-5 µg L(-1) , 7-11 µg L(-1) and 16...... exerted on juvenile development. Progressively lower development index values in the populations exposed to increasing triclosan concentrations suggest developmental retardation. Our results further stress the need for chronic exposure during ecotoxicity testing in chemical risk assessment as even...

  3. Pt Skin Versus Pt Skeleton Structures of Pt3Sc as Electrocatalysts for Oxygen Reduction

    DEFF Research Database (Denmark)

    Johansson, Tobias Peter; Ulrikkeholm, Elisabeth Therese; Hernandez-Fernandez, Patricia

    2014-01-01

    . The development of new materials for this reaction is essential in order to increase the overall effeciency of the fuel cell. Herein, we study the effect of ultra high vacuum annealing on the structure and activity of polycrystalline Pt3Sc. Upon annealing in ultra high vacuum a Pt overlayer is formed......, relative to Pt(111), consistent with the CO adsorption energies calculated using density functional theory calculations. Exposing the annealed Pt3Sc sample to 200 mbar O2 at room temperature results in similar to 14 % Sc oxide as measured by X-ray photoelectron spectroscopy. Electrochemical testing...

  4. Exchange coupled CoPt/FePtC media for heat assisted magnetic recording

    Science.gov (United States)

    Dutta, Tanmay; Piramanayagam, S. N.; Ru, Tan Hui; Saifullah, M. S. M.; Bhatia, C. S.; Yang, Hyunsoo

    2018-04-01

    L10 FePtC granular media are being studied as potential future magnetic recording media and are set to be used in conjunction with heat assisted magnetic recording (HAMR) to enable recording at write fields within the range of current day recording heads. Media structures based on a FePtC storage layer and a capping layer can alleviate the switching field distribution (SFD) requirements of HAMR and reduce the noise originating from the writing process. However, the current designs suffer from SFD issues due to high temperature writing. To overcome this problem, we study a CoPt/FePtC exchange coupled composite structure, where FePtC serves as the storage layer and CoPt (with higher Curie temperature, Tc) as the capping layer. CoPt remains ferromagnetic at near Tc of FePtC. Consequently, the counter exchange energy from CoPt would reduce the noise resulting from the adjacent grain interactions during the writing process. CoPt/FePtC bilayer samples with different thicknesses of CoPt were investigated. Our studies found that CoPt forms a continuous layer at a thickness of 6 nm and leads to considerable reduction in the saturation field and its distribution.

  5. Cell Volume Regulation and Signaling in 3T3-L1 Pre-adipocytes and Adipocytes

    DEFF Research Database (Denmark)

    Eduardsen, Kathrine; Larsen, Susanne; Novak, Ivana

    2011-01-01

    Caveolae have been implicated in sensing of cell volume perturbations, yet evidence is still limited and findings contradictory. Here, we investigated the possible role of caveolae in cell volume regulation and volume sensitive signaling in an adipocyte system with high (3T3-L1 adipocytes......); intermediate (3T3-L1 pre-adipocytes); and low (cholesterol-depleted 3T3-L1 pre-adipocytes) caveolae levels. Using large-angle light scattering, we show that compared to pre-adipocytes, differentiated adipocytes exhibit several-fold increased rates of volume restoration following osmotic cell swelling (RVD......) and osmotic cell shrinkage (RVI), accompanied by increased swelling-activated taurine efflux. However, caveolin-1 distribution was not detectably altered after osmotic swelling or shrinkage, and caveolae integrity, as studied by cholesterol depletion or expression of dominant negative Cav-1, was not required...

  6. Time Series Imputation via L1 Norm-Based Singular Spectrum Analysis

    Science.gov (United States)

    Kalantari, Mahdi; Yarmohammadi, Masoud; Hassani, Hossein; Silva, Emmanuel Sirimal

    Missing values in time series data is a well-known and important problem which many researchers have studied extensively in various fields. In this paper, a new nonparametric approach for missing value imputation in time series is proposed. The main novelty of this research is applying the L1 norm-based version of Singular Spectrum Analysis (SSA), namely L1-SSA which is robust against outliers. The performance of the new imputation method has been compared with many other established methods. The comparison is done by applying them to various real and simulated time series. The obtained results confirm that the SSA-based methods, especially L1-SSA can provide better imputation in comparison to other methods.

  7. Critical contrastive rhetoric: The influence of L2 letter writing instruction on L1letter writing

    Directory of Open Access Journals (Sweden)

    Mehrnoosh Fakharzadeh

    2014-08-01

    Full Text Available The present study employed critical contrastive rhetoric to investigate the L2 to L1 transfer of organizational pattern and directness level of speech acts in business complaint letters. By examining the L1 complaint letters of 30 tourism university students in two phases of study, pre and post instruction of English complaint letter, the study revealed that the rhetorical organization of Persian letters are in a state of hybridity. The post instruction comparison of letters, however, showed a tendency towards applying English conventions both in organization and directness level of complaint speech act in the L1 complaint letters. The results also revealed that after instruction the expert in the field of tourism viewed some letters as inappropriate in terms of politeness which is reflected through some lexical items.

  8. Asymmetric light transmission based on coupling between photonic crystal waveguides and L1/L3 cavity

    Science.gov (United States)

    Zhang, Jinqiannan; Chai, Hongyu; Yu, Zhongyuan; Cheng, Xiang; Ye, Han; Liu, Yumin

    2017-09-01

    A compact design of all-optical diode with mode conversion function based on a two-dimensional photonic crystal waveguide and an L1 or L3 cavity is theoretically investigated. The proposed photonic crystal structures comprise a triangular arrangement of air holes embedded in a silicon substrate. Asymmetric light propagation is achieved via the spatial mode match/mismatch in the coupling region. The simulations show that at each cavity's resonance frequency, the transmission efficiency of the structure with the L1 and L3 cavities reach 79% and 73%, while the corresponding unidirectionalities are 46 and 37 dB, respectively. The functional frequency can be controlled by simply adjusting the radii of specific air holes in the L1 and L3 cavities. The proposed structure can be used as a frequency filter, a beam splitter and has potential applications in all-optical integrated circuits.

  9. A Prototype of Tropospheric Delay Correction in L1-SAIF Augmentation

    Science.gov (United States)

    Takeichi, Noboru; Sakai, Takeyasu; Fukushima, Sounosuke; Ito, Ken

    L1-SAIF signal is one of the navigation signals of Quasi-Zenith Satellite System, which provides an augmentation function for mobile users in Japan. This paper presents the detail of the tropospheric delay correction in L1-SAIF augmentation. The tropospheric delay correction information is generated at the ground station using the data collected at GEONET (GPS Earth Observation NETwork) stations. The correction message contains the information of the zenith tropospheric delay (ZTD) values at 105 Tropospheric Grid Points (TGP) in the experiment area. From this message a mobile user can acquire the ZTD value at some neighboring TGPs, and estimate the local ZTD value accurately by using a suitable ZTD model function. Only 3 L1-SAIF messages are necessary to provide all of the tropospheric correction information. Several investigations using the actual data observed at many GEONET stations overall Japan have proved that it is possible to achieve the correction accuracy of 13.2mm (rms).

  10. Development of Real-Time Precise Positioning Algorithm Using GPS L1 Carrier Phase Data

    Directory of Open Access Journals (Sweden)

    Jeong-Ho Joh

    2002-12-01

    Full Text Available We have developed Real-time Phase DAta Processor(RPDAP for GPS L1 carrier. And also, we tested the RPDAP's positioning accuracy compared with results of real time kinematic(RTK positioning. While quality of the conventional L1 RTK positioning highly depend on receiving condition, the RPDAP can gives more stable positioning result because of different set of common GPS satellites, which searched by elevation mask angle and signal strength. In this paper, we demonstrated characteristics of the RPDAP compared with the L1 RTK technique. And we discussed several improvement ways to apply the RPDAP to precise real-time positioning using low-cost GPS receiver. With correcting the discussed weak points in near future, the RPDAP will be used in the field of precise real-time application, such as precise car navigation and precise personal location services.

  11. L1 track triggering with associative memory for the CMS HL-LHC tracker

    International Nuclear Information System (INIS)

    Sabes, D.

    2014-01-01

    One of the proposed solutions currently under study in Compact Muon Solenoid (CMS) collaboration [1] to reconstruct tracks at the first level trigger (L1) for the High Luminosity - Large Hadron Collider (HL-LHC) is based on the usage of Associative Memory [2] (AM) chips. The tracker information is first reduced to suppress low p T tracks and sent to boards equipped with AM chips. Each AM compares the tracker information with pre-calculated expectations (pattern matching) in a very short time (order of a μs), therefore providing a solution to the challenging computational problem of pattern recognition in a very busy environment. Associated to fast track fit methods, like the Hough transform, the AM approach should be able to fulfil the very demanding requirements of L1 tracking. The proposed architecture for the AM-based L1 track reconstruction system will be presented, together with the latest results obtained using a complete software emulation of this system

  12. Efficient L1 regularization-based reconstruction for fluorescent molecular tomography using restarted nonlinear conjugate gradient.

    Science.gov (United States)

    Shi, Junwei; Zhang, Bin; Liu, Fei; Luo, Jianwen; Bai, Jing

    2013-09-15

    For the ill-posed fluorescent molecular tomography (FMT) inverse problem, the L1 regularization can protect the high-frequency information like edges while effectively reduce the image noise. However, the state-of-the-art L1 regularization-based algorithms for FMT reconstruction are expensive in memory, especially for large-scale problems. An efficient L1 regularization-based reconstruction algorithm based on nonlinear conjugate gradient with restarted strategy is proposed to increase the computational speed with low memory consumption. The reconstruction results from phantom experiments demonstrate that the proposed algorithm can obtain high spatial resolution and high signal-to-noise ratio, as well as high localization accuracy for fluorescence targets.

  13. On the advantages of spring magnets compared to pure FePt: Strategy for rare-earth free permanent magnets following a bottom-up approach

    Energy Technology Data Exchange (ETDEWEB)

    Pousthomis, M.; Garnero, C. [Université de Toulouse, UMR 5215 INSA, CNRS, UPS, Laboratoire de Physique et Chimie des Nano-Objets, 135 avenue de Rangueil, F-31077 Toulouse Cedex 4 (France); Marcelot, C.G. [Université de Toulouse, UMR 5215 INSA, CNRS, UPS, Laboratoire de Physique et Chimie des Nano-Objets, 135 avenue de Rangueil, F-31077 Toulouse Cedex 4 (France); Centre d’Elaboration de Matériaux et d’Etudes Structurales, CEMES-CNRS, 29 rue Jeanne Marvig, B.P. 94347, 31055 Toulouse (France); Blon, T.; Cayez, S. [Université de Toulouse, UMR 5215 INSA, CNRS, UPS, Laboratoire de Physique et Chimie des Nano-Objets, 135 avenue de Rangueil, F-31077 Toulouse Cedex 4 (France); Cassignol, C.; Du, V.A.; Krispin, M. [Siemens AG, Corporate Technology, Munich (Germany); Arenal, R. [Transpyrenean Advanced Laboratory for Electron Microscopy (TALEM), INSA - INA, CNRS - Universidad de Zaragoza, 30155 Toulouse (France); Laboratorio de Microscopias Avanzadas (LMA), Instituto de Nanociencia de Aragon (INA), U. Zaragoza, C/Mariano Esquillor s/n, 50018 Zaragoza (Spain); Fundacion ARAID, 50018 Zaragoza (Spain); Soulantica, K.; Viau, G. [Université de Toulouse, UMR 5215 INSA, CNRS, UPS, Laboratoire de Physique et Chimie des Nano-Objets, 135 avenue de Rangueil, F-31077 Toulouse Cedex 4 (France); Lacroix, L.-M., E-mail: lmlacroi@insa-toulouse.fr [Université de Toulouse, UMR 5215 INSA, CNRS, UPS, Laboratoire de Physique et Chimie des Nano-Objets, 135 avenue de Rangueil, F-31077 Toulouse Cedex 4 (France); Transpyrenean Advanced Laboratory for Electron Microscopy (TALEM), INSA - INA, CNRS - Universidad de Zaragoza, 30155 Toulouse (France)

    2017-02-15

    Nanostructured magnets benefiting from efficient exchange-coupling between hard and soft grains represent an appealing approach for integrated miniaturized magnetic power sources. Using a bottom-up approach, nanostructured materials were prepared from binary assemblies of bcc FeCo and fcc FePt nanoparticles and compared with pure L1{sub 0}-FePt materials. The use of a bifunctional mercapto benzoic acid yields homogeneous assemblies of the two types of particles while reducing the organic matter amount. The 650 °C thermal annealing, mandatory to allow the L1{sub 0}-FePt phase transition, led to an important interdiffusion and thus decreased drastically the amount of soft phase present in the final composites. The analysis of recoil curves however evidenced the presence of an efficient interphase exchange coupling, which allows obtaining better magnetic performances than pure L1{sub 0} FePt materials, energy product above 100 kJ m{sup −3} being estimated for a Pt content of only 33%. These results clearly evidenced the interest of chemically grown nanoparticles for the preparation of performant spring-magnets, opening promising perspective for integrated subcentimetric magnets with optimized properties.

  14. Kinetic imaging of NPC1L1 and sterol trafficking between plasma membrane and recycling endosomes in hepatoma cells

    DEFF Research Database (Denmark)

    Hartwig Petersen, Nicole; Færgeman, Nils J; Yu, Liqing

    2008-01-01

    fluorescent protein (NPC1L1-EGFP) and cholesterol analogues in hepatoma cells. At steady state about 42% of NPC1L1 resided in the transferrin (Tf) positive, sterol enriched endocytic recycling compartment (ERC), while time-lapse microscopy demonstrated NPC1L1 traffic between plasma membrane and ERC...... the ERC to the plasma membrane. NPC1L1-EGFP facilitated transport of fluorescent sterols from the plasma membrane to the ERC. Insulin induced translocation of vesicles containing NPC1L1 and fluorescent sterol from the ERC to the cell membrane. Upon polarization of hepatoma cells NPC1L1 resided almost...... exclusively in the canalicular membrane, where the protein is highly mobile. Our study demonstrates dynamic trafficking of NPC1L1 between cell surface and intracellular compartments and suggests that this transport is involved in NPC1L1 mediated cellular sterol uptake....

  15. A Small Spacecraft Swarm Deployment and Stationkeeping Strategy for Sun-Earth L1 Halo Orbits

    Science.gov (United States)

    Renea Conn, Tracie; Bookbinder, Jay

    2018-01-01

    Spacecraft orbits about the Sun-Earth librarian point L1 have been of interest since the 1950s. An L1 halo orbit was first achieved with the International Sun-Earth Explorer-3 (ISEE-3) mission, and similar orbits around Sun-Earth L1 were achieved in the Solar and Heliospheric Observatory (SOHO), Advanced Composition Explorer (ACE), Genesis, and Deep Space Climate Observatory (DSCOVR) missions. With recent advancements in CubeSat technology, we envision that it will soon be feasible to deploy CubeSats at L1. As opposed to these prior missions where one large satellite orbited alone, a swarm of CubeSats at L1 would enable novel science data return, providing a topology for intersatellite measurements of heliophysics phenomena both spatially and temporally, at varying spatial scales.The purpose of this iPoster is to present a flight dynamics strategy for a swarm of numerous CubeSats orbiting Sun-Earth L1. The presented method is a coupled, two-part solution. First, we present a deployment strategy for the CubeSats that is optimized to produce prescribed, time-varying intersatellite baselines for the purposes of collecting magnetometer data as well as radiometric measurements from cross-links. Second, we employ a loose control strategy that was successfully applied to SOHO and ACE for minimized stationkeeping propellant expenditure. We emphasize that the presented solution is practical within the current state-of-the-art and heritage CubeSat technology, citing capabilities of CubeSat designs that will launch on the upcoming Exploration Mission 1 (EM-1) to lunar orbits and beyond. Within this iPoster, we present animations of the simulated deployment strategy and resulting spacecraft trajectories. Mission design parameters such as total Δv required for long-term station keeping and minimum/maximum/mean spacecraft separation distances are also presented.

  16. A Crohn's disease variant in Atg16l1 enhances its degradation by caspase 3

    Science.gov (United States)

    Murthy, Aditya; Li, Yun; Peng, Ivan; Reichelt, Mike; Katakam, Anand Kumar; Noubade, Rajkumar; Roose-Girma, Merone; Devoss, Jason; Diehl, Lauri; Graham, Robert R.; van Lookeren Campagne, Menno

    2014-02-01

    Crohn's disease is a debilitating inflammatory bowel disease (IBD) that can involve the entire digestive tract. A single-nucleotide polymorphism (SNP) encoding a missense variant in the autophagy gene ATG16L1 (rs2241880, Thr300Ala) is strongly associated with the incidence of Crohn's disease. Numerous studies have demonstrated the effect of ATG16L1 deletion or deficiency; however, the molecular consequences of the Thr300Ala (T300A) variant remains unknown. Here we show that amino acids 296-299 constitute a caspase cleavage motif in ATG16L1 and that the T300A variant (T316A in mice) significantly increases ATG16L1 sensitization to caspase-3-mediated processing. We observed that death-receptor activation or starvation-induced metabolic stress in human and murine macrophages increased degradation of the T300A or T316A variants of ATG16L1, respectively, resulting in diminished autophagy. Knock-in mice harbouring the T316A variant showed defective clearance of the ileal pathogen Yersinia enterocolitica and an elevated inflammatory cytokine response. In turn, deletion of the caspase-3-encoding gene, Casp3, or elimination of the caspase cleavage site by site-directed mutagenesis rescued starvation-induced autophagy and pathogen clearance, respectively. These findings demonstrate that caspase 3 activation in the presence of a common risk allele leads to accelerated degradation of ATG16L1, placing cellular stress, apoptotic stimuli and impaired autophagy in a unified pathway that predisposes to Crohn's disease.

  17. In situ investigation of ordering phase transformations in FePt magnetic nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Wittig, James E., E-mail: j.wittig@vanderbilt.edu [Interdisciplinary Materials Science, Vanderbilt University, PMB 351683, 2301 Vanderbilt Place, Nashville, TN 37232 (United States); Bentley, James, E-mail: bentleyj48@gmail.com [Materials Science and Technology Division, Oak Ridge National Laboratory, PO Box 2008, Oak Ridge, TN 37831-6376 (United States); Allard, Lawrence F., E-mail: allardlfjr@ornl.gov [Materials Science and Technology Division, Oak Ridge National Laboratory, PO Box 2008, Oak Ridge, TN 37831-6376 (United States)

    2017-05-15

    In situ high-resolution electron microscopy was used to reveal information at the atomic level for the disordered-to-ordered phase transformation of equiatomic FePt nanoparticles that can exhibit outstanding magnetic properties after transforming from disordered face-centered-cubic into the tetragonal L1{sub 0} ordered structure. High-angle annular dark-field imaging in the scanning transmission electron microscope provided sufficient contrast between the Fe and Pt atoms to readily monitor the ordering of the atoms during in situ heating experiments. However, during continuous high-magnification imaging the electron beam influenced the kinetics of the transformation so annealing had to be performed with the electron beam blanked. At 500 °C where the reaction rate was relatively slow, observation of the transformation mechanisms using this sequential imaging protocol revealed that ordering proceeded from (002) surface facets but was incomplete and multiple-domain particles were formed that contained anti-phase domain boundaries and anti-site defects. At 600 and 700 °C, the limitations of sequential imaging were revealed as a consequence of increased transformation kinetics. Annealing for only 5 min at 700 °C produced complete single-domain L1{sub 0} order; such single-domain particles were more spherical in shape with (002) facets. The in situ experiments also provided information concerning nanoparticle sintering, coalescence, and consolidation. Although there was resistance to complete sintering due to the crystallography of L1{sub 0} order, the driving force from the large surface-area-to-volume ratio resulted in considerable nanoparticle coalescence, which would render such FePt nanoparticles unsuitable for use as magnetic recording media. Comparison of the in situ data acquired using the protocol described above with parallel ex situ annealing experiments showed that identical behavior resulted in all cases. - Highlights: • HAADF STEM imaging reveals the

  18. Influence of a magnetic field on microstructure formation in L1{sub 0}-type ferromagnetic intermetallics

    Energy Technology Data Exchange (ETDEWEB)

    Farjami, Sahar; Fukuda, Takashi; Kakeshita, Tomoyuki [Department of Materials Science and Engineering, Graduate School of Engineering, Osaka University, 2-1, Yamadaoka, Suita, Osaka 565-0871 (Japan)], E-mail: farjami@mat.eng.osaka-u.ac.jp

    2009-05-01

    The influence of a magnetic field on microstructure formation through a disorder-order transformation has been investigated in Co-Pt and Fe-Pd alloys. Single crystals of disordered Co-50Pt(at%) and Fe-55Pd(at%) were subjected to an ordering heat-treatment under a magnetic field. When the ordering heat-treatment is performed without applying a magnetic field, three equivalent variants are formed. On the other hand, when the ordering heat-treatment is performed under a magnetic field of 0.5 T (in CoPt) - 4 T (in Fe-55Pd) and higher as applied along the [001] direction of the disordered phase, a single variant with an easy axis along the field direction is obtained. The induced anisotropy energy of the ordered phase under a magnetic field of 1 T was 4.1 kJ|m{sup -3} at 773 K for CoPt and 45.3 kJ|m{sup -3} at 673 K for Fe-55Pd.

  19. The clinical spectrum of mutations in L1, a neuronal cell adhesion molecule

    Energy Technology Data Exchange (ETDEWEB)

    Fransen, E.; Vits, L.; Van Camp, G.; Willems, P.J. [Univ. of Antwerp (Belgium)

    1996-07-12

    Mutations in the gene encoding the neuronal cell adhesion molecule L1 are responsible for several syndromes with clinical overlap, including X-linked hydrocephalus (XLH, HSAS), MASA (mental retardation, aphasia, shuffling gait, adducted thumbs) syndrome, complicated X-linked spastic paraplegia (SP 1), X-linked mental retardation-clasped thumb (MR-CT) syndrome, and some forms of X-linked agenesis of the corpus callosum (ACC). We review 34 L1 mutations in patients with these phenotypes. 22 refs., 3 figs., 4 tabs.

  20. Genetic variants in CHI3L1 influencing YKL-40 levels

    DEFF Research Database (Denmark)

    Kjaergaard, Alisa D; Johansen, Julia S; Nordestgaard, Børge G

    2013-01-01

    Despite its important role in many serious diseases, the genetic background for plasma YKL-40 has still not been systematically catalogued. Therefore, we aimed at identifying genetic variants in CHI3L1 influencing plasma YKL-40 levels in the general population.......Despite its important role in many serious diseases, the genetic background for plasma YKL-40 has still not been systematically catalogued. Therefore, we aimed at identifying genetic variants in CHI3L1 influencing plasma YKL-40 levels in the general population....

  1. L1{sub 0} phase formation in ternary FePdNi alloys

    Energy Technology Data Exchange (ETDEWEB)

    Montes-Arango, A.M. [Department of Mechanical and Industrial Engineering, Northeastern University, Boston, MA 02115 (United States); Bordeaux, N.C. [Department of Chemical Engineering, Northeastern University, Boston, MA 02115 (United States); Liu, J.; Barmak, K. [Department of Applied Physics and Applied Mathematics, Columbia University, New York, NY 10027 (United States); Lewis, L.H., E-mail: lhlewis@neu.edu [Department of Mechanical and Industrial Engineering, Northeastern University, Boston, MA 02115 (United States); Department of Chemical Engineering, Northeastern University, Boston, MA 02115 (United States)

    2015-11-05

    Metallurgical routes to highly metastable phases are required to access new materials with new functionalities. To this end, the stability of the tetragonal chemically ordered L1{sub 0} phase in the ternary Fe–Pd–Ni system is quantified to provide enabling information concerning synthesis of L1{sub 0}-type FeNi, a highly attractive yet highly elusive advanced permanent magnet candidate. Fe{sub 50}Pd{sub 50−x}Ni{sub x} (x = 0–7 at%) samples were arc-melted and annealed at 773 K (500 °C) for 100 h to induce formation of the chemically ordered L1{sub 0} phase. Coupled calorimetry, structural and magnetic investigations allow determination of an isothermal section of the ternary Fe–Pd–Ni phase diagram featuring a single phase L1{sub 0} region near the FePd boundary for x < 6 at%. It is demonstrated that increased Ni content in Fe{sub 50}Pd{sub 50−x}Ni{sub x} alloys systematically decreases the order-disorder transition temperature, resulting in a lower thermodynamic driving force for the ordering phase transformation. The Fe{sub 50}Pd{sub 50−x}Ni{sub x} L1{sub 0} → fcc disordering transformation is determined to occur via a two-step process, with compositionally-dependent enthalpies and transition temperatures. These results highlight the need to investigate ternary alloys with higher Ni content to determine the stability range of the L1{sub 0} phase near the FeNi boundary, thereby facilitating kinetic access to the important L1{sub 0} FeNi ferromagnetic phase. - Highlights: • Chemical ordering in FePdNi enhances intrinsic and extrinsic magnetic properties. • 773 K annealed FePdNi alloys studied show a stable L1{sub 0} phase for Ni ≤ 5.2 at%. • Chemical disordering in FePdNi occurs by a previously unreported two-step process. • Ni additions to FePd dramatically decrease the chemical order-disorder temperature. • The chemical-ordering transformation kinetics are greatly affected by Ni content.

  2. Copolyimide mixed matrix membranes with oriented microporous titanosilicate JDF-L1sheet particles

    OpenAIRE

    Galve, Alejandro; Vispe, Eugenio; Téllez, Carlos; Coronas, Joaquín

    2011-01-01

    JDF-L1 is a microporous titanosilicate exhibiting a layer structure with pore size of about 3 Å. It is consequently an attractive material to separate H2-containing mixtures. This is the reason why JDF-L1, after disaggregation by means of hexadecyltrimethylammonium surfactant, has been combined with a carboxyl group containing copolyimide (6FDA-4MPD/6FDA-DABA 4:1) to produce mixed matrix membranes, which were applied to the separation of H2/CH4 and O2/N2 mixtures. Additionally, due to the she...

  3. Design of L1 -Adaptive Controller for Single Axis Positioning Table

    Directory of Open Access Journals (Sweden)

    Amjad Jalil Humaidi

    2017-11-01

    Full Text Available L1 adaptive controller has proven to provide fast adaptation with guaranteed transients in a large variety of systems. It is commonly used for controlling systems with uncertain time-varying unknown parameters. The effectiveness of L1 adaptive controller for position control of single axis has been examined and compared with Model Reference Adaptive Controller (MRAC. The Linear servo motor is one of the main constituting elements of the x-y table which is mostly used in automation application. It is characterized by time-varying friction and disturbance

  4. Experimental study on L-[1-13C] phenylalanine breath test for quantitative assessment of liver function with animal

    International Nuclear Information System (INIS)

    Yan Weili; Fudan Univ., Shanghai; Lin Xiangtong; Sun Dayu; Jiang Yibin; Sun Xu; Rong Lan; Liang Qi

    2006-01-01

    Objective: Using a small animal breath test model we designed and L-[1- 13 C] phenylalanine breath test ( 13 C-PheBT) of rats, the authors investigated its feasibility and validity and determined effective parameter of the test. Methods: Twenty male Sprague-Dawley (SD) weighting 280-290 g rats randomized into two groups acute hepatitis rats (n=10) and control rats (n=10). Hepatitis was induced by carbon tetrachloride (CCl 4 ) olive oil administration through intragastric gavage. PheBT was assisted by small mechanical ventilator improved and air samples were collected discontinuously, 20 mg/kg body weight L-[1- 13 C] phenylalanine ( 13 C-Phe) was administered intravenously. Twenty-nine breath samples were taken before and different intervals within sixty minutes after administration. 13 Cenrichment was measured by isotope ratio mass spectrometer. Results: All time phase curves of 13 C enrichment in rat breath reached a peak almost at 2 min after the intravenous administration of 13 C-Phe. The PheBT parameters, 13 C excretion rate constant (PheBT-K), of CCl 4 hepatitis rats were significantly lower than that of normal control rats [(2.45 ± 0.25) x 10 -2 min -1 vs (2.98 ± 0.19) x 10 -2 min -1 , t = 5.40, P 13 C fast phase disposition constant did not statistically differ between the two groups (t=0.58, P>0.05). PheBT-K had significant negative cor-relation with serum ALT, AKP, TBA and total bilirum TBIL (the correlation coefficient r is -0.74, -0.73, -0.82 and -0.67 respectively, P 0.05). Conclusions: It was indicated that the small animal breath test model we designed was a virtual tool to use in experimental study on breath test and PheBT-K was a sensitive index. (authors)

  5. Trichosanthes cucumerina extracts enhance glucose uptake and regulate adiponectin and leptin concentrations in 3T3-L1 adipocytes model

    Directory of Open Access Journals (Sweden)

    Sassi, A.,

    2017-10-01

    Full Text Available Trichosanthes cucumerina (Cucurbitaceae commonly known as Snake gourd or Labu Ular is considered the largest genre in the Cucurbitaceae family and is mainly found in the southeast areas of Asia. It has been used in Ayurvedic medicine as a treatment for certain diseases such as Diabetes mellitus, but these acclaims lack scientific-based evidence. In this study, water and ethanol extracts of three parts of Trichosanthes cucumerina namely; whole vegetable, peels, and seeds, were assessed for toxicity through a cell viability assay using 3T3-L1 pre-adipocytes model which revealed a maximum toleration concentration of 0.063 mg/mL. The extracts were further tested on adipocytes’ differentiation and positively showed a stimulation of lipid droplets formation during adipogenesis and significantly (p<0.001 increased glycerol release levels (75.34±3.69 μg/ml during adipolysis. The extracts also significantly (p<0.001 promoted the uptake of glucose into the cells (2636.22±91.33 Bq in an action similar to that of insulin. Similar results were observed during ELISA assay with a significant increase (p<0.001 in adiponectin concentrations (3593.1±225.25 ng/mL and a decrease in leptin concentrations (23870±5066.07 pg/mL. The present study results indicate a beneficial effect of Trichosanthes cucumerina extracts on adipogenesis, adipolysis and glucose uptake, in addition to a regulation of adiponectin and leptin concentrations in 3T3-L1 adipocytes which can be of clinical importance in energy regulation which is a key factor in treating diabetes, obesity, and metabolic syndrome.

  6. The Effects of Giving and Receiving Marginal L1 Glosses on L2 Vocabulary Learning by Upper Secondary Learners

    Science.gov (United States)

    Samian, Hosein Vafadar; Foo, Thomas Chow Voon; Mohebbi, Hassan

    2016-01-01

    This paper reports the findings of a study that investigated the effect of giving and receiving marginal L1 glosses on L2 vocabulary learning. To that end, forty nine Iranian learners of English were assigned to three different experimental conditions including marginal L1 glosses Giver (n = 17), marginal L1 glosses Receiver (n = 17), and no…

  7. L2 Acquisition of Prosodic Properties of Speech Rhythm: Evidence from L1 Mandarin and German Learners of English

    Science.gov (United States)

    Li, Aike; Post, Brechtje

    2014-01-01

    This study examines the development of speech rhythm in second language (L2) learners of typologically different first languages (L1s) at different levels of proficiency. An empirical investigation of durational variation in L2 English productions by L1 Mandarin learners and L1 German learners compared to native control values in English and the…

  8. Effect of atomic composition on the compressive strain and electrocatalytic activity of PtCoFe/sulfonated graphene

    International Nuclear Information System (INIS)

    Lohrasbi, Elaheh; Javanbakht, Mehran; Mozaffari, Sayed Ahmad

    2017-01-01

    Highlights: • SO_3H-graphene supported PtFeCo alloy nanoparticles were prepared. • Co:Fe atomic ratio plays important role in the electrocatalytic performance. • PtCoFe/SG with 7:3 Co:Fe atomic ratio is optimized for PEMFCs. • Power density of 530 mW cm"−"2 with 0.1 mg cm"−"2 Pt loading was obtained at 75 °C. - Abstract: The aim of this work is improvement of the stability and durability of sulfonated graphene supported PtCoFe electrocatalyst (PtCoFe/SG) for application in proton exchange membrane fuel cells (PEMFCs). The durability investigation of PtCoFe/SG is evaluated by a repetitive potential cycling test. The compressive strain in the lattice of PtCoFe/SG towards the electrocatalytic oxygen reduction reaction is studied. The synthesized electrocatalysts are examined physically and electrochemically for their structure, morphology and electrocatalytic performance. It is shown that presence of SO_3− groups on the graphene cause better adsorption of PtCoFe nanoparticles on the support and increase stability of electrocatalysts. Also, it is shown that Co:Fe atomic ratio in the synthesized electrocatalysts plays important role in their electrocatalytic performance. In the optimum Co:Fe atomic ratio, the compressive strain goes through the ideal value of the binding energy; further increase in Co/Fe atomic fraction introduces the excessive compressive strain and the activity of electrocatalyst decreases. The electrocatalyst synthesized in the optimum conditions is utilized as cathode in PEMFC. The power density of the PEMFC in low metal loading (0.1 mg cm"−"2 Pt) reaches to a maximum of 530 mW cm"−"2 at 75 °C. It suggests that PtCoFe/SG with 7:3 Co:Fe atomic ratio promises to improve the power density of PEMFCs.

  9. Remarks on the PT-pseudo-norm in PT-symmetric quantum mechanics

    Energy Technology Data Exchange (ETDEWEB)

    Duc Tai Trinh [Department of Mathematics, Teacher Training College of Dalat, 29 Yersin, Dalat (Viet Nam)]|[Abdus Salam International Centre for Theoretical Physics, Strada Costiera 11, Trieste 34014 (Italy)

    2005-04-22

    This paper presents an underlying analytical relationship between the PT-pseudo-norm associated with the PT-symmetric Hamiltonian H = p{sup 2} + V(q) and the Stokes multiplier of the differential equation corresponding to this Hamiltonian. We show that the sign alternation of the PT-pseudo-norm, which has been observed as a generic feature of the PT-inner product, is essentially controlled by the derivative of a Stokes multiplier with respect to the eigenparameter.

  10. Hydrogenation of Phenol over Pt/CNTs: The Effects of Pt Loading and Reaction Solvents

    OpenAIRE

    Feng Li; Bo Cao; Wenxi Zhu; Hua Song; Keliang Wang; Cuiqin Li

    2017-01-01

    Carbon nanotubes (CNTs)-supported Pt nanoparticles were prepared with selective deposition of Pt nanoparticles inside and outside CNTs (Pt–in/CNTs and Pt–out/CNTs). The effects of Pt loading and reaction solvents on phenol hydrogenation were investigated. The Pt nanoparticles in Pt–in/CNTs versus Pt–out/CNTs are smaller and better dispersed. The catalytic activity and reuse stability toward phenol hydrogenation both improved markedly. The dichloromethane–water mixture as the reaction solvent,...

  11. Electron transport in a Pt-CO-Pt nanocontact: Density functional theory calculations

    DEFF Research Database (Denmark)

    Strange, Mikkel; Thygesen, Kristian Sommer; Jacobsen, Karsten Wedel

    2006-01-01

    We have performed first-principles calculations for the mechanic and electric properties of pure Pt nanocontacts and a Pt contact with a single CO molecule adsorbed. For the pure Pt contacts we see a clear difference between point contacts and short chains in good agreement with experiments. We...

  12. MgB2 and Mg1-xAlxB2 single crystals: high pressure growth and physical properties

    International Nuclear Information System (INIS)

    Karpinski, J.; Kazakov, S.M.; Jun, J.; Zhigadlo, N.D.; Angst, M.; Puzniak, R.; Wisniewski, A.

    2004-01-01

    Single crystals of MgB 2 have been grown with a high pressure cubic anvil technique. They grow via the peritectic decomposition of the MgNB 9 ternary nitride. The crystals are of a size up to 2 x 1 x 0.1 mm 3 with a weight up to 230 μg. Typically they have transition temperatures between 38 and 38.6 K with a width of 0.3-0.5 K. Investigations of the P-T phase diagram prove that the MgB 2 phase is stable at least up to 2190 deg. C at high hydrostatic pressure in the presence of Mg vapor under high pressure. Substitution of aluminum for magnesium in single crystals leads to stepwise decrease of T c . This indicates a possible appearance of superstructures or phases with different T c 's. The upper critical field decreases with Al doping

  13. KSHV LANA and EBV LMP1 induce the expression of UCH-L1 following viral transformation

    Energy Technology Data Exchange (ETDEWEB)

    Bentz, Gretchen L.; Bheda-Malge, Anjali; Wang, Ling [Lineberger Comprehensive Cancer Center, University of North Carolina, Chapel Hill (United States); Shackelford, Julia [Lineberger Comprehensive Cancer Center, University of North Carolina, Chapel Hill (United States); Department of Cell and Developmental Biology, University of North Carolina, Chapel Hill (United States); Damania, Blossom [Lineberger Comprehensive Cancer Center, University of North Carolina, Chapel Hill (United States); Departments of Medicine and of Microbiology and Immunology, University of North Carolina, Chapel Hill, NC (United States); Pagano, Joseph S., E-mail: joseph_pagano@med.unc.edu [Lineberger Comprehensive Cancer Center, University of North Carolina, Chapel Hill (United States); Departments of Medicine and of Microbiology and Immunology, University of North Carolina, Chapel Hill, NC (United States)

    2014-01-05

    Ubiquitin C-terminal Hydrolase L1 (UCH-L1) has oncogenic properties and is highly expressed during malignancies. We recently documented that Epstein-Barr virus (EBV) infection induces uch-l1 expression. Here we show that Kaposi's Sarcoma-associated herpesvirus (KSHV) infection induced UCH-L1 expression, via cooperation of KSHV Latency-Associated Nuclear Antigen (LANA) and RBP-Jκ and activation of the uch-l1 promoter. UCH-L1 expression was also increased in Primary Effusion Lymphoma (PEL) cells co-infected with KSHV and EBV compared with PEL cells infected only with KSHV, suggesting EBV augments the effect of LANA on uch-l1. EBV latent membrane protein 1 (LMP1) is one of the few EBV products expressed in PEL cells. Results showed that LMP1 was sufficient to induce uch-l1 expression, and co-expression of LMP1 and LANA had an additive effect on uch-l1 expression. These results indicate that viral latency products of both human γ-herpesviruses contribute to uch-l1 expression, which may contribute to the progression of lymphoid malignancies. - Highlights: • Infection of endothelial cells with KSHV induced UCH-L1 expression. • KSHV LANA is sufficient for the induction of uch-l1. • Co-infection with KSHV and EBV (observed in some PELs) results in the additive induction of uch-l1. • EBV LMP1 also induced UCH-L1 expression. • LANA- and LMP1-mediated activation of the uch-l1 promoter is in part through RBP-Jκ.

  14. GAS2L1 Is a Centriole-Associated Protein Required for Centrosome Dynamics and Disjunction.

    NARCIS (Netherlands)

    Au, F.K.; Jia, Y.; Jiang, K.; Grigoriev, I.S.; Hau, B.K.; Shen, Y.; Du, S.; Akhmanova, A.S.; Qi, R.Z.

    2017-01-01

    Mitotic spindle formation and chromosome segregation require timely separation of the two duplicated centrosomes, and this process is initiated in late G2 by centrosome disjunction. Here we report that GAS2L1, a microtubule- and actin-binding protein, associates with the proximal end of mature

  15. MASA syndrome is caused by mutations in the neural cell adhesion gene, L1CAM

    Energy Technology Data Exchange (ETDEWEB)

    Schwartz, C.E.; Wang, Y.; Schroer, R.J.; Stevenson, R.E. [Greenwood Genetic Center, SC (United States)

    1994-09-01

    The MASA syndrome is a recessive X-linked disorder characterized by Mental retardation, Adducted thumbs, Shuffling gait and Aphasia. Recently we found that MASA in one family was likely caused by a point mutation in exon 6 of the L1CAM gene. This gene has also been shown to be involved in X-linked hydrocephalus (HSAS). We have screened 60 patients with either sporadic HSAS or MASA as well as two additional families with MASA. For the screening, we initially utilized 3 cDNA probes for the L1CAM gene. In one of the MASA families, K8310, two affected males were found to have an altered BglII band. The band was present in their carrier mother but not in their normal brothers. This band was detected by the entire cDNA probe as well as the cDNA probe for 3{prime} end of the gene. Analysis of the L1CAM sequence indicated the altered BglII site is distal to the exon 28 but proximal to the punative poly A signal site. It is hypothesized that this point mutation alters the stability of the L1CAM mRNA. This is being tested using cell lines established from the two affected males.

  16. Evidence consistent with human L1 retrotransposition in maternal meiosis I

    NARCIS (Netherlands)

    Brouha, Brook; Meischl, Christof; Ostertag, Eric; de Boer, Martin; Zhang, Yue; Neijens, Herman; Roos, Dirk; Kazazian, Haig H.

    2002-01-01

    We have used a unique polymorphic 3' transduction to show that a human L1, or LINE-1 ((l) under bar ong (i) under bar nterspersed (n) under bar ucleotide (e) under bar lement-1), retrotransposition event most likely occurred in the maternal primary oocyte during meiosis I. We characterized a

  17. Fluorescence lifetime imaging of lipids during 3T3-L1 cell differentiation

    Science.gov (United States)

    Song, Young Sik; Won, Young Jae; Lee, Sang-Hak; Kim, Dug Young

    2014-03-01

    Obesity is becoming a big health problem in these days. Since increased body weight is due to increased number and size of the triglyceride-storing adipocytes, many researchers are working on differentiation conditions and processes of adipocytes. Adipocytes also work as regulators of whole-body energy homeostasis by secreting several proteins that regulate processes as diverse as haemostasis, blood pressure, immune function, angiogenesis and energy balance. 3T3-L1 cells are widely used cell line for studying adipogenesis because it can differentiate into an adipocyte-like phenotype under appropriate conditions. In this paper, we propose an effective fluorescence lifetime imaging technique which can easily distinguish lipids in membrane and those in lipid droplets. Nile red dyes are attached to lipids in 3T3-L1 cells. Fluorescence lifetime images were taken for 2 week during differentiation procedure of 3T3-L1 cells into adipocytes. We used 488 nm pulsed laser with 5MHz repetition rate and emission wavelength is 520 nm of Nile Red fluorescent dye. Results clearly show that the lifetime of Nile red in lipid droplets are smaller than those in cell membrane. Our results suggest that fluorescence lifetime imaging can be a very powerful tool to monitor lipid droplet formation in adipocytes from 3T3-L1 cells.

  18. Reading Skills and Strategies: Assessing Primary School Students’ Awareness in L1 and EFL Strategy Use

    Directory of Open Access Journals (Sweden)

    Evdokimos Aivazoglou

    2014-09-01

    Full Text Available The present study was designed and conducted with the purpose to assess primary school students’ awareness in GL1 (Greek as first language and EFL (English as a foreign language strategy use and investigate the relations between the reported reading strategies use in first (L1 and foreign language (FL.  The sample (455 students attending the fifth and sixth grades of primary schools in Northern Greece was first categorized into skilled and less skilled L1 and EFL readers through screening reading comprehension tests, one in L1 and one in FL, before filling in the reading strategy questionnaires. The findings revealed participants’ preference for “problem solving” strategies, while “global strategies” coming next. Girls were proved to be more aware of their reading strategies use with the boys reporting a more frequent use in both languages. Also, skilled readers were found to use reading strategies more effectively, and appeared to be more flexible in transferring strategies from L1 to FL compared to less-skilled readers.

  19. L1 and L2 Spoken Word Processing: Evidence from Divided Attention Paradigm.

    Science.gov (United States)

    Shafiee Nahrkhalaji, Saeedeh; Lotfi, Ahmad Reza; Koosha, Mansour

    2016-10-01

    The present study aims to reveal some facts concerning first language (L 1 ) and second language (L 2 ) spoken-word processing in unbalanced proficient bilinguals using behavioral measures. The intention here is to examine the effects of auditory repetition word priming and semantic priming in first and second languages of these bilinguals. The other goal is to explore the effects of attention manipulation on implicit retrieval of perceptual and conceptual properties of spoken L 1 and L 2 words. In so doing, the participants performed auditory word priming and semantic priming as memory tests in their L 1 and L 2 . In a half of the trials of each experiment, they carried out the memory test while simultaneously performing a secondary task in visual modality. The results revealed that effects of auditory word priming and semantic priming were present when participants processed L 1 and L 2 words in full attention condition. Attention manipulation could reduce priming magnitude in both experiments in L 2 . Moreover, L 2 word retrieval increases the reaction times and reduces accuracy on the simultaneous secondary task to protect its own accuracy and speed.

  20. Simulation Experiment Description Markup Language (SED-ML Level 1 Version 3 (L1V3

    Directory of Open Access Journals (Sweden)

    Bergmann Frank T.

    2018-03-01

    Full Text Available The creation of computational simulation experiments to inform modern biological research poses challenges to reproduce, annotate, archive, and share such experiments. Efforts such as SBML or CellML standardize the formal representation of computational models in various areas of biology. The Simulation Experiment Description Markup Language (SED-ML describes what procedures the models are subjected to, and the details of those procedures. These standards, together with further COMBINE standards, describe models sufficiently well for the reproduction of simulation studies among users and software tools. The Simulation Experiment Description Markup Language (SED-ML is an XML-based format that encodes, for a given simulation experiment, (i which models to use; (ii which modifications to apply to models before simulation; (iii which simulation procedures to run on each model; (iv how to post-process the data; and (v how these results should be plotted and reported. SED-ML Level 1 Version 1 (L1V1 implemented support for the encoding of basic time course simulations. SED-ML L1V2 added support for more complex types of simulations, specifically repeated tasks and chained simulation procedures. SED-ML L1V3 extends L1V2 by means to describe which datasets and subsets thereof to use within a simulation experiment.

  1. Anti-Obesity Effects of Starter Fermented Kimchi on 3T3-L1 Adipocytes

    Science.gov (United States)

    Lee, Kyung-Hee; Song, Jia-Le; Park, Eui-Seong; Ju, Jaehyun; Kim, Hee-Young; Park, Kun-Young

    2015-01-01

    The anti-obesity effects of starter (Leuconostoc mesenteroides+Lactobacillus plantarum) fermented kimchi on 3T3-L1 adipocyte were studied using naturally fermented kimchi (NK), a functional kimchi (FK, NK supplemented with green tea), and FK supplemented with added starters (FKS). Oil red O staining and cellular levels of triglyceride (TG) and glycerol were used to evaluate the in vitro anti-obesity effects of these kimchis in 3T3-L1 cells. The expressions of adipogenesis/lipogenesis-related genes of peroxisome proliferator-active receptor (PPAR)-γ, CCAAT/enhance-binding protein (C/EBP)-α, and fatty acid synthase (FAS) were determined by RT-PCR. Kimchis, especially FKS, markedly decreased TG levels and increased levels of intracellular glycerol and lipid lipolysis. In addition, FKS also reduced the mRNA levels of PPAR-γ, C/EBP-α, and FAS, which are related to adipogenesis/lipogenesis in 3T3-L1 cells. These results suggest the anti-obesity effects of FKS were to due to enhanced lipolysis and reduced adipogenesis/lipogenesis in 3T3-L1 adipocytes. PMID:26770918

  2. Mixed Total Variation and L1 Regularization Method for Optical Tomography Based on Radiative Transfer Equation

    Directory of Open Access Journals (Sweden)

    Jinping Tang

    2017-01-01

    Full Text Available Optical tomography is an emerging and important molecular imaging modality. The aim of optical tomography is to reconstruct optical properties of human tissues. In this paper, we focus on reconstructing the absorption coefficient based on the radiative transfer equation (RTE. It is an ill-posed parameter identification problem. Regularization methods have been broadly applied to reconstruct the optical coefficients, such as the total variation (TV regularization and the L1 regularization. In order to better reconstruct the piecewise constant and sparse coefficient distributions, TV and L1 norms are combined as the regularization. The forward problem is discretized with the discontinuous Galerkin method on the spatial space and the finite element method on the angular space. The minimization problem is solved by a Jacobian-based Levenberg-Marquardt type method which is equipped with a split Bregman algorithms for the L1 regularization. We use the adjoint method to compute the Jacobian matrix which dramatically improves the computation efficiency. By comparing with the other imaging reconstruction methods based on TV and L1 regularizations, the simulation results show the validity and efficiency of the proposed method.

  3. Data of evolutionary structure change: 1E14L-1PCRM [Confc[Archive

    Lifescience Database Archive (English)

    Full Text Available 1E14L-1PCRM 1E14 1PCR L M -ALLSFERKYRVPGGT-----LVGGNLFD----FWVGP-...entryChain> 1PCR M 1PCRM...dbChain>M 1PCRM YGLSFAAPLKE 1PCR M 1PCRM IADRG-----TAAER M 1PCRM TVVDN----WYVWG

  4. Enhancing Foreign Language Learning through Listening Strategies Delivered in L1: An Experimental Study

    Science.gov (United States)

    Bozorgian, Hossein; Pillay, Hitendra

    2013-01-01

    Listening used in language teaching refers to a complex process that allows us to understand spoken language. The current study, conducted in Iran with an experimental design, investigated the effectiveness of teaching listening strategies delivered in L1 (Persian) and its effect on listening comprehension in L2. Five listening strategies:…

  5. Outlier identification procedures for contingency tables using maximum likelihood and $L_1$ estimates

    NARCIS (Netherlands)

    Kuhnt, S.

    2004-01-01

    Observed cell counts in contingency tables are perceived as outliers if they have low probability under an anticipated loglinear Poisson model. New procedures for the identification of such outliers are derived using the classical maximum likelihood estimator and an estimator based on the L1 norm.

  6. Structural basis for small molecule targeting of the programmed death ligand 1 (PD-L1)

    NARCIS (Netherlands)

    Zak, Krzysztof M.; Grudnik, Przemyslaw; Guzik, Katarzyna; Zieba, Bartosz J.; Musielak, Bogdan; Dömling, Alexander; Dubin, Grzegorz; Holak, Tad A.

    2016-01-01

    Targeting the PD-1/PD-L1 immunologic checkpoint with monoclonal antibodies has provided unprecedented results in cancer treatment in the recent years. Development of chemical inhibitors for this pathway lags the antibody development because of insufficient structural information. The first

  7. Quantitative and Qualitative Aspects of L1 (Swedish) and L2 (English) Idiom Comprehension

    Science.gov (United States)

    Karlsson, Monica

    2013-01-01

    In the present investigation, 15 first term university students were faced with 80 context-based idioms in English (L2) and Swedish (L1) respectively, 30 of which were in the source domain of animals, commonly used in both languages, and asked to explain their meaning. The idioms were of varying frequency and transparency. Three main research…

  8. MODIS/Terra Calibrated Radiances 5-Min L1B Swath 1km V006

    Data.gov (United States)

    National Aeronautics and Space Administration — The MODIS/Terra Calibrated Radiances 5-Min L1B Swath 1km (MOD021KM) contains calibrated and geolocated at-aperture radiances for 36 discrete bands located in the 0.4...

  9. A> L1-TV algorithm for robust perspective photometric stereo with spatially-varying lightings

    DEFF Research Database (Denmark)

    Quéau, Yvain; Lauze, Francois Bernard; Durou, Jean-Denis

    2015-01-01

    We tackle the problem of perspective 3D-reconstruction of Lambertian surfaces through photometric stereo, in the presence of outliers to Lambert's law, depth discontinuities, and unknown spatially-varying lightings. To this purpose, we introduce a robust $L^1$-TV variational formulation of the re...

  10. Comparing L1 and L2 Texts and Writers in First-Year Composition

    Science.gov (United States)

    Eckstein, Grant; Ferris, Dana

    2018-01-01

    Scholars have at various points discussed the needs of second language (L2) writers enrolled in "mainstream" composition courses where they are mixed with native (L1) English speakers. Other researchers have investigated the experiences of L2 writers in mainstream classes and the perceptions of their instructors about their abilities and…

  11. The Design of Morphological/Linguistic Data in L1 and L2 ...

    African Journals Online (AJOL)

    user

    learners' MA of an L1 or L2 can be measured (and, as an extension to this, that users' and .... and they could activate these strategies and skills when confronted with new .... cussion of a wide range of morphological phenomena in English.

  12. Brain tumors : L-[1-C-11]tyrosine PET for visualization and quantification of protein synthesis rate

    NARCIS (Netherlands)

    Pruim, J; Willemsen, A T; Molenaar, W M; Waarde, A van; Paans, A M; Heesters, M A; Go, K G; Visser, Gerben; Franssen, E J; Vaalburg, W

    1995-01-01

    PURPOSE: Positron emission tomography (PET) with the amino acid tracer L-[1-C-11]-tyrosine was evaluated in 27 patients with primary and recurrent brain tumors. MATERIALS AND METHODS: Patients underwent either static (n = 14) or dynamic PET (n = 13), with quantification of protein synthesis rate

  13. A Prerequisite to L1 Homophone Effects in L2 Spoken-Word Recognition

    Science.gov (United States)

    Nakai, Satsuki; Lindsay, Shane; Ota, Mitsuhiko

    2015-01-01

    When both members of a phonemic contrast in L2 (second language) are perceptually mapped to a single phoneme in one's L1 (first language), L2 words containing a member of that contrast can spuriously activate L2 words in spoken-word recognition. For example, upon hearing cattle, Dutch speakers of English are reported to experience activation…

  14. Nonlinear parabolic problems with Neumann-type boundary conditions and L^1-data

    Directory of Open Access Journals (Sweden)

    Abderrahmane El Hachimi

    2007-11-01

    $$ \\frac{\\partial u}{\\partial t}-\\triangle_{p}u+\\alpha(u=f \\quad \\text{in } ]0,\\ T[\\times\\Omega, $$ with Neumann-type boundary conditions and initial data in $L^1$. Our approach is based essentially on the time discretization technique by Euler forward scheme.

  15. Morphological Family Size effects in L1 and L2 processing: An electrophysiological study

    NARCIS (Netherlands)

    Mulder, K.; Schreuder, R.; Dijkstra, A.F.J.

    2013-01-01

    The present study examined Morphological Family Size effects in first and second language processing. Items with a high or low Dutch (L1) Family Size were contrasted in four experiments involving Dutch–English bilinguals. In two experiments, reaction times (RTs) were collected in English (L2) and

  16. Conceptualisations of "Grammar Teaching": L1 English Teachers' Beliefs about Teaching Grammar for Writing

    Science.gov (United States)

    Watson, Annabel Mary

    2015-01-01

    This paper reports on an investigation of L1 English teachers' conceptual and evaluative beliefs about teaching grammar, one strand of a larger Economic and Social Research Council (ESRC)-funded investigation into the impact of contextualised grammar teaching [RES-062-23-0775]. Thirty-one teachers in English secondary schools were interviewed…

  17. Hydrocephalus and intestinal aganglionosis : Is L1CAM a modifier gene in Hirschsprung disease?

    NARCIS (Netherlands)

    Parisi, MA; Kapur, RP; Neilson, [No Value; Hofstra, RMW; Holloway, LW; Michaelis, RC; Leppig, KA

    2002-01-01

    Congenital hydrocephalus associated with aqueductal stenosis and/or agenesis of the corpus callosum has been described in newborn males with mutations in L1CAM, a gene that encodes a neural cell adhesion molecule. These males usually have severe mental retardation and may have spastic paraplegia and

  18. Production of recombinant proteins GST L1, E6 and E7 tag HPV 16 ...

    African Journals Online (AJOL)

    In the present work recombinant proteins were produced for used in LUMINEX in order to undergo serological study of Tunisian female population. HPV types 16 L1, E6 and E7 sequences fused to their 3'-end to a sequence encoding the terminal undecapeptide of the SV40 large T-antigen (tag) were isolated from plasmids ...

  19. Axiomatic and operational connections between the l1-norm of coherence and negativity

    Science.gov (United States)

    Zhu, Huangjun; Hayashi, Masahito; Chen, Lin

    2018-02-01

    Quantum coherence plays a central role in various research areas. The l1-norm of coherence is one of the most important coherence measures that are easily computable, but it is not easy to find a simple interpretation. We show that the l1-norm of coherence is uniquely characterized by a few simple axioms, which demonstrates in a precise sense that it is the analog of negativity in entanglement theory and sum negativity in the resource theory of magic-state quantum computation. We also provide an operational interpretation of the l1-norm of coherence as the maximum entanglement, measured by the negativity, produced by incoherent operations acting on the system and an incoherent ancilla. To achieve this goal, we clarify the relation between the l1-norm of coherence and negativity for all bipartite states, which leads to an interesting generalization of maximally correlated states. Surprisingly, all entangled states thus obtained are distillable. Moreover, their entanglement cost and distillable entanglement can be computed explicitly for a qubit-qudit system.

  20. An optimal L1-minimization algorithm for stationary Hamilton-Jacobi equations

    KAUST Repository

    Guermond, Jean-Luc

    2009-01-01

    We describe an algorithm for solving steady one-dimensional convex-like Hamilton-Jacobi equations using a L1-minimization technique on piecewise linear approximations. For a large class of convex Hamiltonians, the algorithm is proven to be convergent and of optimal complexity whenever the viscosity solution is q-semiconcave. Numerical results are presented to illustrate the performance of the method.

  1. Genetic variation in the cholesterol transporter NPC1L1, ischaemic vascular disease, and gallstone disease

    DEFF Research Database (Denmark)

    Lauridsen, Bo Kobberø; Stender, Stefan; Frikke-Schmidt, Ruth

    2015-01-01

    developed IVD or symptomatic gallstone disease, respectively, during follow-up from 1977 to 2013. We genotyped four common NPC1L1 variants, previously associated with reduced LDL cholesterol levels, thus mimicking the effect of ezetimibe, and calculated a weighted genotype score. With increasing genotype...

  2. The Use of Paraphrase in Summary Writing: A Comparison of L1 and L2 Writers

    Science.gov (United States)

    Keck, Casey

    2006-01-01

    Paraphrasing is considered by many to be an important skill for academic writing, and some have argued that the teaching of paraphrasing might help students avoid copying from source texts. Few studies, however, have investigated the ways in which both L1 and L2 academic writers already use paraphrasing as a textual borrowing strategy when…

  3. Requirements for an "ideal" bilingual L1 →L2 translation- oriented ...

    African Journals Online (AJOL)

    The major aim of this article is to outline the requirements for an "ideal" bilingual L1 →L2 dictionary of the general vocabulary specifically designed for the purposes of professional translation. The article challenges three commonly accepted beliefs: (a) a bilingual dictionary equals a translation dictionary; (b) a bilingual ...

  4. Isoproterenol Increases Uncoupling, Glycolysis, and Markers of Beiging in Mature 3T3-L1 Adipocytes.

    Directory of Open Access Journals (Sweden)

    Colette N Miller

    Full Text Available Beta-adrenergic activation stimulates uncoupling protein 1 (UCP1, enhancing metabolic rate. In vitro, most work has studied brown adipocytes, however, few have investigated more established adipocyte lines such as the murine 3T3-L1 line. To assess the effect of beta-adrenergic activation, mature 3T3-L1s were treated for 6 or 48 hours with or without isoproterenol (10 and 100 μM following standard differentiation supplemented with thyroid hormone (T3; 1 nM. The highest dose of isoproterenol increased lipid content following 48 hours of treatment. This concentration enhanced UCP1 mRNA and protein expression. The increase in UCP1 following 48 hours of isoproterenol increased oxygen consumption rate. Further, coupling efficiency of the electron transport chain was disturbed and an enhancement of glycolytic rate was measured alongside this, indicating an attempt to meet the energy demands of the cell. Lastly, markers of beige adipocytes (protein content of CD137 and gene transcript of CITED1 were also found to be upregulated at 48 hours of isoproterenol treatment. This data indicates that mature 3T3-L1 adipocytes are responsive to isoproterenol and induce UCP1 expression and activity. Further, this finding provides a model for further pharmaceutical and nutraceutical investigation of UCP1 in 3T3-L1s.

  5. Statistical characteristics of L1 carrier phase observations from four low-cost GPS receivers

    DEFF Research Database (Denmark)

    Cederholm, Jens Peter

    2010-01-01

    Statistical properties of L1 carrier phase observations from four low-cost GPS receivers are investigated through a case study. The observations are collected on a zero baseline with a frequency of 1 Hz and processed with a double difference model. The carrier phase residuals from an ambiguity...

  6. Impact of L1 Use in L2 English Writing Classes

    African Journals Online (AJOL)

    This experimental study endeavored to assess the impact of L1 use in .... Two sections were selected using simple ... practice. In all the four writing practice activities, the experimental group ..... during the pre-test, but this was not true for.

  7. Task-Modality and L1 Use in EFL Oral Interaction

    Science.gov (United States)

    Azkarai, Agurtzane; del Pilar García Mayo, María

    2015-01-01

    This study examines whether task-modality (speaking vs. speaking+writing) influences first language (L1) use in task-based English as a foreign language (EFL) learner-learner interaction. Research on the topic has shown that different task-modality triggers different learning opportunities with collaborative speaking tasks drawing learners'…

  8. Spanish as a Second Language when L1 Is Quechua: Endangered Languages and the SLA Researcher

    Science.gov (United States)

    Kalt, Susan E.

    2012-01-01

    Spanish is one of the most widely spoken languages in the world. Quechua is the largest indigenous language family to constitute the first language (L1) of second language (L2) Spanish speakers. Despite sheer number of speakers and typologically interesting contrasts, Quechua-Spanish second language acquisition is a nearly untapped research area,…

  9. Electromagnetic decay widths for L=1, Jsup(PC)=1-- T-baryonia: II

    International Nuclear Information System (INIS)

    Ellis, R.G.; McKellar, B.H.J.; Joshi, G.C.

    1981-01-01

    The electromagnetic decay widths of the Jsup(PC)=1 -- , L=1 T-baryonia in the 1-5 GeV region are estimated. The Van Royen-Weisskopf technique is extended to baryonia within the framework of the QCD potential model. The diquark and antidiquark are assumed to have finite extent. Potential dependent coefficients are scaled from known baryon and mesons

  10. Simulation Experiment Description Markup Language (SED-ML) Level 1 Version 3 (L1V3).

    Science.gov (United States)

    Bergmann, Frank T; Cooper, Jonathan; König, Matthias; Moraru, Ion; Nickerson, David; Le Novère, Nicolas; Olivier, Brett G; Sahle, Sven; Smith, Lucian; Waltemath, Dagmar

    2018-03-19

    The creation of computational simulation experiments to inform modern biological research poses challenges to reproduce, annotate, archive, and share such experiments. Efforts such as SBML or CellML standardize the formal representation of computational models in various areas of biology. The Simulation Experiment Description Markup Language (SED-ML) describes what procedures the models are subjected to, and the details of those procedures. These standards, together with further COMBINE standards, describe models sufficiently well for the reproduction of simulation studies among users and software tools. The Simulation Experiment Description Markup Language (SED-ML) is an XML-based format that encodes, for a given simulation experiment, (i) which models to use; (ii) which modifications to apply to models before simulation; (iii) which simulation procedures to run on each model; (iv) how to post-process the data; and (v) how these results should be plotted and reported. SED-ML Level 1 Version 1 (L1V1) implemented support for the encoding of basic time course simulations. SED-ML L1V2 added support for more complex types of simulations, specifically repeated tasks and chained simulation procedures. SED-ML L1V3 extends L1V2 by means to describe which datasets and subsets thereof to use within a simulation experiment.

  11. Cognitive Style and Reading Comprehension in L1 and L2.

    Science.gov (United States)

    Vivaldo-Lima, Javier

    This paper presents the results of a research study carried out with Mexican college students to analyze the relationship between readers' cognitive styles (field dependent/independent) and their performance at different levels of written discourse processing in Spanish (L1) and English (L2). The sample for the study included 452 undergraduate…

  12. Effect of different body postures on the pressures generated during an L-1 maneuver.

    Science.gov (United States)

    Williams, C A; Lind, A R; Wiley, R L; Douglas, J E; Miller, G

    1988-10-01

    Changes in blood pressure, intrathoracic pressure, heart rate and the electromyographic activity of various muscle groups were determined while nine male subjects performed 15-s L-1 straining maneuvers at four spine-to-thigh angles (70, 84, 94, and 105 degrees) and two seatback angles (30 and 60 degrees). There was no significant difference between the changes in these variables due to the different body positions. At the onset of the L-1, arterial pressure immediately increased to 195 +/- 5 mm Hg, but fell progressively during the next 5 s to 160 +/- 5 mm Hg. It remained constant during the next 5 s of the maneuver and then recovered to 180 +/- mm Hg during the last 5 s of the maneuver. Esophageal pressure followed essentially the same pattern of response, but heart rate progressively increased during the entire L-1. No one muscle group was utilized more than another. Inflation of an anti-G suit to 4 PSI had no effect on the variables measured. Generation of high arterial pressures during L-1 maneuvers is transitory and not affected either positively or negatively by altering subject body position.

  13. Asimmetrie L1/L2: una sfida nella didattica di “lingua e traduzione”.

    Directory of Open Access Journals (Sweden)

    Laura Salmon

    2004-12-01

    Full Text Available Asymmetries Between L1 and L2: a Challenge in the Teaching of "Language and Translation" Language teaching is deeply connected to the cognitive and brain sciences. The attribution of meaning of linguistic messages depends on the interaction between the communicant’s brain and the external world. The interaction is based on the cognitive and emotional experience shared by a L-community. Competence in L2 is acquired by the development of an internal data base of contextualised .units of living speech. (Lurija 1976. L2 teaching is particularly successful when the L2 units are inscribed in memory by means of the functionally equivalent L1 units. Selection of the L1/L2 correspondent units is due to the principle of markedness: each unit of L1 has a functional equivalent in one and only one unit of the L2. Because of the interlingual asymmetries (a set of Italian/Russian examples is given, functional equivalence differs from morphosyntactic and lexical equivalence. The competency in ascribing a degree of markedness to each linguistic unit needs the regular implicit acquisition of the L2 intonational and prosodic system; the processes of the metalinguistic conscious reflection are instead a .hindrance. to the procedural acting of a “living speaker”.

  14. Similarities of L1 (Mother Tongue) in Terms of Grammar and Language Structure in Translation

    Science.gov (United States)

    Subramaniam, Vijayaletchumy

    2011-01-01

    Malaysian philosophy, purpose and objective of the education system are rooted and based on policies stated in the National Education Policy 1956 and Education Act 1961. Whereas the Education Ordinance 1952 urged all Chinese and Tamil schools to be given an equal opportunity to learn English and Malay language together with their L1 (mother…

  15. EXPLORING L1 INTERFERENCE IN THE WRITINGS OF KADAZANDUSUN ESL STUDENTS

    Directory of Open Access Journals (Sweden)

    Chelster Sherralyn Jeoffrey Pudin

    2015-07-01

    Full Text Available For many ethnic KadazanDusuns from Sabah, North Borneo, English is a third language after their mother tongue and Malay. The burden of having to contend with an additional language frequently leads to errors, particularly those caused by interference from the first language (L1. This study set out to identify the types and frequency of English language errors and their correlations in the writing of KadazanDusun ESL students at Universiti Malaysia Sabah. A further aim of the study was to establish which of these errors could be attributed to L1 interference. A total of 54 students with lower Malaysian University Entrance Test (MUET band scores were asked to complete a questionnaire and write a short essay on a designated topic. The language errors were categorized and analysed via statistical analysis. Errors considered to be related to L1 interference were then identified after consultation with an experienced KadazanDusun language lecturer. The most common errors were those involving singular /plural nouns and unusual sentence structures. The results show that approximately 25% of the errors were attributable to L1 interference, i.e. mode (normal/involuntary, voice (actor (-ing form /undergoer (-ed form, overuse of article, linker (when linker is used, no article is needed, auxiliary verb and direct translation. The findings of this study give ESL practitioners a better insight into student errors and should lead to improved writing performance in the classroom.

  16. Comparing Hypertext Reading in L1 and L2: The Case of Filipino Adults

    Science.gov (United States)

    Gruspe, Michael Angelo M.; Marinas, Christian Joshua L.; Villasin, Marren Nicole F.; Villanueva, Ariel Josephe Therese R.; Vizconde, Camilla J.

    2015-01-01

    This research probed into the reading experiences of adult readers in their first language (L1) and second language (L2). Qualitative in nature, the investigation focused on twelve (12) adult readers , six (6) males and six (6) females, whose first language is Filipino. Data were gathered through interviews and focus-group discussions. Based on…

  17. L1 influence in the L2 acquisition of isiXhosa verb placement by ...

    African Journals Online (AJOL)

    1. Introduction. In second language (L2) acquisition research conducted within ..... versus Afrikaans-speaking beginner learners of isiXhosa, with regard to verb ..... Language contact within one home is also illustrated by the case of the four L1 ...

  18. Pragmatic assessment of schizophrenic bilinguals' L1 and L2 use ...

    African Journals Online (AJOL)

    This paper reports on a study investigating the pragmatic skills and deficits of schizophrenic bilinguals in their spontaneous first language (L1) and second language (L2) speech. Smit (2009) (see also Smit et al., this volume) argues that the locus of deficits in schizophrenic speech is semantics and suggests that a next step ...

  19. Increase of cells expressing PD-L1 in bovine leukemia virus infection and enhancement of anti-viral immune responses in vitro via PD-L1 blockade

    Directory of Open Access Journals (Sweden)

    Ikebuchi Ryoyo

    2011-09-01

    Full Text Available Abstract The inhibitory receptor programmed death-1 (PD-1 and its ligand, programmed death-ligand 1 (PD-L1 are involved in immune evasion mechanisms for several pathogens causing chronic infections. Blockade of the PD-1/PD-L1 pathway restores anti-virus immune responses, with concomitant reduction in viral load. In a previous report, we showed that, in bovine leukemia virus (BLV infection, the expression of bovine PD-1 is closely associated with disease progression. However, the functions of bovine PD-L1 are still unknown. To investigate the role of PD-L1 in BLV infection, we identified the bovine PD-L1 gene, and examined PD-L1 expression in BLV-infected cattle in comparison with uninfected cattle. The deduced amino acid sequence of bovine PD-L1 shows high homology to the human and mouse PD-L1. The proportion of PD-L1 positive cells, especially among B cells, was upregulated in cattle with the late stage of the disease compared to cattle at the aleukemic infection stage or uninfected cattle. The proportion of PD-L1 positive cells correlated positively with prediction markers for the progression of the disease such as leukocyte number, virus load and virus titer whilst on the contrary, it inversely correlated with the degree of interferon-gamma expression. Blockade of the PD-1/PD-L1 pathway in vitro by PD-L1-specific antibody upregulated the production of interleukin-2 and interferon-gamma, and correspondingly, downregulated the BLV provirus load and the proportion of BLV-gp51 expressing cells. These data suggest that PD-L1 induces immunoinhibition in disease progressed cattle during chronic BLV infection. Therefore, PD-L1 would be a potential target for developing immunotherapies against BLV infection.

  20. Science objectives of the magnetic field experiment onboard Aditya-L1 spacecraft

    Science.gov (United States)

    Yadav, Vipin K.; Srivastava, Nandita; Ghosh, S. S.; Srikar, P. T.; Subhalakshmi, Krishnamoorthy

    2018-01-01

    The Aditya-L1 is first Indian solar mission scheduled to be placed in a halo orbit around the first Lagrangian point (L1) of Sun-Earth system in the year 2018-19. The approved scientific payloads onboard Aditya-L1 spacecraft includes a Fluxgate Digital Magnetometer (FGM) to measure the local magnetic field which is necessary to supplement the outcome of other scientific experiments onboard. The in-situ vector magnetic field data at L1 is essential for better understanding of the data provided by the particle and plasma analysis experiments, onboard Aditya-L1 mission. Also, the dynamics of Coronal Mass Ejections (CMEs) can be better understood with the help of in-situ magnetic field data at the L1 point region. This data will also serve as crucial input for the short lead-time space weather forecasting models. The proposed FGM is a dual range magnetic sensor on a 6 m long boom mounted on the Sun viewing panel deck and configured to deploy along the negative roll direction of the spacecraft. Two sets of sensors (tri-axial each) are proposed to be mounted, one at the tip of boom (6 m from the spacecraft) and other, midway (3 m from the spacecraft). The main science objective of this experiment is to measure the magnitude and nature of the interplanetary magnetic field (IMF) locally and to study the disturbed magnetic conditions and extreme solar events by detecting the CME from Sun as a transient event. The proposed secondary science objectives are to study the impact of interplanetary structures and shock solar wind interaction on geo-space environment and to detect low frequency plasma waves emanating from the solar corona at L1 point. This will provide a better understanding on how the Sun affects interplanetary space. In this paper, we shall give the main scientific objectives of the magnetic field experiment and brief technical details of the FGM onboard Aditya-1 spacecraft.

  1. GLI ERRORI DI ITALIANO L1 ED L2: INTERFERENZA E APPRENDIMENTO

    Directory of Open Access Journals (Sweden)

    Rosaria Solarino

    2011-02-01

    Full Text Available Si può oggi affrontare il tema degli errori di italiano da una prospettiva che possa giovare contemporaneamente a docenti di italiano L1 ed L2? Noi pensiamo di sì: la ricerca glottodidattica sembra aver ormai apprestato un terreno comune alle due situazioni di apprendimento, sgombrando il campo da vecchi pregiudizi e distinzioni che appaiono ormai superate. Attraverso la contrapposizione di concetti quali “lingua parlata/lingua scritta”,  “errori di lingua / errori di linguaggio”, “apprendimento spontaneo/apprendimento guidato”, “italiano L1/italiano L2”, “errori di apprendimento/errori di interferenza, si indicano diversi criteri per la interpretazione degli errori e la loro valutazione in relazione alle cause, alle situazioni comunicative, ai contesti o allo stadio di evoluzione dell’apprendimento della lingua.     Errors in italian L1 and L2: interference and learning   Can errors in Italian be approached in a way that benefits both L1 and L2 Italian teachers? We believe so: glottodidactic research seems to have prepared a common terrain for these two learning situations, clearing the field of old prejudices and obsolete distinctions.  Through the juxtaposition of concepts like “spoken language/written language”, “language errors/speech errors”, “spontaneous learning/guided learning”, “L1 Italian/L2 Italian”, “learning errors/interference errors”, different criteria for interpreting errors and evaluating them in relation to their causes, to communicative situations, to contexts and the developmental state in learning a language are singled out.

  2. Monodispersed porous flowerlike PtAu nanocrystals as effective electrocatalysts for ethanol oxidation

    Science.gov (United States)

    Li, Shumin; Xu, Hui; Xiong, Zhiping; Zhang, Ke; Wang, Caiqin; Yan, Bo; Guo, Jun; Du, Yukou

    2017-11-01

    Designing and tuning the bimetallic nanoparticles with desirable morphology and structure can embody them with greatly enhanced electrocatalytic activity and stability towards liquid fuel oxidation. We herein reported a facile one-pot method for the controlled synthesis of monodispersed binary PtAu nanoflowers with abundant exposed surface area. Owing to its fantastic structure, synergistic and electronic effect, such as-prepared PtAu nanoflowers exhibited outstandingly high electrocatalytic activity with the mass activity of 6482 mA mg-1 towards ethanol oxidation, which is 28.3 times higher than that of commercial Pt/C (227 mA mg-1). More interesting, the present PtAu nanoflower catalysts are more stable for the ethanol oxidation reaction in the alkaline with lower current density decay and retained a much higher current density after successive CVs of 500 cycles than that of commercial Pt/C. This work may open a new way for maximizing the catalytic performance of electrocatalysts towards ethanol oxidation by synthesizing shape-controlled alloy nanoparticles with more surface active sites to enhance the performances of direct fuel cells reaction, chemical conversion, and beyond.

  3. Facile synthesis of hollow dendritic Ag/Pt alloy nanoparticles for enhanced methanol oxidation efficiency.

    Science.gov (United States)

    Sui, Ning; Wang, Ke; Shan, Xinyao; Bai, Qiang; Wang, Lina; Xiao, Hailian; Liu, Manhong; Colvin, Vicki L; Yu, William W

    2017-11-14

    Hollow dendritic Ag/Pt alloy nanoparticles were synthesized by a double template method: Ag nanoparticles as the hard template to obtain hollow spheres by a galvanic replacement reaction between PtCl 6 2- and metallic Ag and surfactant micelles (Brij58) as the soft template to generate porous dendrites. The formation of a Ag/Pt alloy phase was confirmed by XRD and HRTEM. Elemental mapping and line scanning revealed the formation of the hollow architecture. We studied the effects of the Ag/Pt ratio, surfactant and reaction temperature on the morphology. In addition, we explored the formation process of hollow dendritic Ag/Pt nanoparticles by tracking the morphologies of the nanostructures formed at different stages. In order to improve the electrocatalytic property, we controlled the size of the nanoparticles and the thickness of the shell by adjusting the amount of the precursor. We found that these Ag/Pt alloy nanoparticles exhibited high activity (440 mA mg -1 ) and stability as an electrocatalyst for catalyzing methanol oxidation.

  4. Energy scavenging based on a single-crystal PMN-PT nanobelt

    Science.gov (United States)

    Wu, Fan; Cai, Wei; Yeh, Yao-Wen; Xu, Shiyou; Yao, Nan

    2016-03-01

    Self-powered nanodevices scavenging mechanical energy require piezoelectric nanostructures with high piezoelectric coefficients. Here we report the fabrication of a single-crystal (1 - x)Pb(Mg1/3Nb2/3)O3 - xPbTiO3 (PMN-PT) nanobelt with a superior piezoelectric constant (d33 = ~550 pm/V), which is approximately ~150%, 430%, and 2100% of the largest reported values for previous PMN-PT, PZT and ZnO nanostructures, respectively. The high d33 of the single-crystalline PMN-PT nanobelt results from the precise orientation control during its fabrication. As a demonstration of its application in energy scavenging, a piezoelectric nanogenerator (PNG) is built on the single PMN-PT nanobelt, generating a maximum output voltage of ~1.2 V. This value is ~4 times higher than that of a single-CdTe PNG, ~13 times higher than that of a single-ZnSnO3 PNG, and ~26 times higher than that of a single-ZnO PNG. The profoundly increased output voltage of a lateral PNG built on a single PMN-PT nanobelt demonstrates the potential application of PMN-PT nanostructures in energy harvesting, thus enriching the material choices for PNGs.

  5. L1cam is crucial for cell locomotion and terminal translocation of the Soma in radial migration during murine corticogenesis.

    Directory of Open Access Journals (Sweden)

    Madoka Tonosaki

    Full Text Available L1cam (L1 is a cell adhesion molecule associated with a spectrum of human neurological diseases, the most well-known being X-linked hydrocephalus. Although we recently demonstrated that L1 plays an important role in neuronal migration during cortical histogenesis, the mechanisms of delayed migration have still not been clarified. In this study, we found that cell locomotion in the intermediate zone and terminal translocation in the primitive cortical zone (PCZ were affected by L1-knockdown (L1-KD. Time-lapse analyses revealed that L1-KD neurons produced by in utero electroporation of shRNA targeting L1 (L1-shRNAs molecules showed decreased locomotion velocity in the intermediate zone, compared with control neurons. Furthermore, L1-KD neurons showed longer and more undulated leading processes during translocation through the primitive cortical zone. The curvature index, a quantitative index for curvilinearity, as well as the length of the leading process, were increased, whereas the somal movement was decreased in L1-KD neurons during terminal translocation in the PCZ. These results suggest that L1 has a role in radial migration of cortical neurons.

  6. Pt-Ag cubic nanocages with wall thickness less than 2 nm and their enhanced catalytic activity toward oxygen reduction.

    Science.gov (United States)

    Sun, Xiaojun; Yang, Xuan; Zhang, Yun; Ding, Yong; Su, Dong; Qin, Dong

    2017-10-12

    We report a facile synthesis of Pt-Ag nanocages with walls thinner than 2 nm by depositing a few atomic layers of Pt as conformal shells on Ag nanocubes and then selectively removing the Ag template via wet etching. In a typical process, we inject a specific volume of aqueous H 2 PtCl 6 into a mixture of Ag nanocubes, ascorbic acid (H 2 Asc), NaOH, and poly(vinylpyrrolidone) in water under ambient conditions. At an initial pH of 11.9, the Pt(iv) precursor is quickly reduced by an ascorbate monoanion, a strong reducing agent derived from the neutralization of H 2 Asc with NaOH. The newly formed Pt atoms are deposited onto the edges and then corners and side faces of Ag nanocubes, leading to the generation of Ag@Pt core-shell nanocubes with a conformal Pt shell of approximately three atomic layers (or, about 0.6 nm in thickness) when 0.4 mL of 0.2 mM H 2 PtCl 6 is involved. After the selective removal of Ag in the core using an etchant based on a mixture of Fe(NO 3 ) 3 and HNO 3 , we transform the core-shell nanocubes into Pt-Ag alloy nanocages with an ultrathin wall thickness of less than 2 nm. We further demonstrate that the as-obtained nanocages with a composition of Pt 42 Ag 58 exhibit an enhanced catalytic activity toward the oxygen reduction reaction, with a mass activity of 0.30 A mg -1 and a specific activity of 0.93 mA cm -2 , which are 1.6 and 2.5 times, respectively, greater than those of a commercial Pt/C catalyst.

  7. Dual-functional Pt-on-Pd supported on reduced graphene oxide hybrids: peroxidase-mimic activity and an enhanced electrocatalytic oxidation characteristic.

    Science.gov (United States)

    Zhang, Xiahong; Wu, Genghuang; Cai, Zhixiong; Chen, Xi

    2015-03-01

    In this study, a facile hydrothermal method was developed to synthesize Pt-on-Pd supported on reduced graphene oxide (Pt-on-Pd/RGO) hybrids. Because of the synergistic effect between Pt-on-Pd and RGO, the obtained Pt-on-Pd/RGO had superior peroxidase-mimic activities in H2O2 reduction and TMB oxidation. The reaction medium was optimized and a sensing approach for H2O2 was developed with a linear range from 0.98 to 130.7 μM of H2O2. In addition, the characteristic of electrocatalytic oxidation of methanol was investigated. The peak current density value, j(f), for the Pt-on-Pd/RGO hybrid (328 mA mg(Pt)(-1)) was about 1.85 fold higher than that of commercial Pt black (177 mA mg(Pt)(-1)) and, also, more durable electrocatalytic activity could be obtained. For the first time, the dual-functional Pt-on-Pd/RGO with peroxidase-mimic activity and an enhanced electrocatalytic oxidation characteristic was reported. Copyright © 2014 Elsevier B.V. All rights reserved.

  8. Tuning magnetic properties of non-collinear magnetization configuration in Pt/[Pt/Co]{sub 6}/Pt/Co/Pt multilayer structure

    Energy Technology Data Exchange (ETDEWEB)

    Kalaycı, Taner, E-mail: taner.kalayci@marmara.edu.tr [Department of Physics, Marmara University, 34722, Kadıköy, Istanbul (Turkey); Deger, Caner [Department of Physics, Marmara University, 34722, Kadıköy, Istanbul (Turkey); Akbulut, Salih [Department of Physics, Gebze Technical University, 41400, Gebze, Kocaeli (Turkey); Yildiz, Fikret, E-mail: fyildiz@gtu.edu.tr [Department of Physics, Gebze Technical University, 41400, Gebze, Kocaeli (Turkey)

    2017-08-15

    Highlights: • Effects of Pt spacer and reference layers thickness are investigated by MOKE and FMR. • Controlling of non-collinear states in multilayered thin film systems is studied. • Micromagnetic approach is used for modeling of magnetic multilayered structure. • Magnetic parameters are determined by a simulation based on metropolis algorithm. - Abstract: In this study, effects of Pt spacer and Co reference layers thickness in [Co/Pt]{sub 6}/Pt/Co multilayer have been revealed to tailor magnetization directions in non-collinear configuration. Magneto-optic Kerr effect and ferromagnetic resonance techniques were employed to investigate magnetic properties. Bilinear coupling between [Co/Pt]{sub 6} and Co layers and anisotropy constants were determined by a micromagnetic simulation based on metropolis algorithm. 3 nm spacer causes ferromagnetic coupling while the samples have 4 and 5 nm spacer are coupled anti-ferromagneticaly. Also, tuning magnetic anisotropy of [Co/Pt]{sub 6} layer was accomplished by Co reference layer. It is revealed that controlling of non-collinear states in such systems is possible by variation of thickness of spacer and reference layers and [Co/Pt]{sub 6}/t{sub Pt}/t{sub Co} trilayer system can be used in multilayered magnetic systems.

  9. Effect of different seawater Mg

    NARCIS (Netherlands)

    Mewes, A.; Langer, G.; de Nooijer, L.J.; Bijma, J.; Reichart, G.J.

    2014-01-01

    Magnesium, incorporated in foraminiferal calcite (Mg/CaCC), is used intensively to reconstruct past seawater temperatures but, in addition to temperature, the Mg/CaCC of foraminiferal tests also depends on the ratio of Mg and Ca in seawater (Mg/CaSW). The physiological mechanisms responsible for

  10. Detention of HPV L1 Capsid Protein and hTERC Gene in Screening of Cervical Cancer

    Directory of Open Access Journals (Sweden)

    Huang Bin

    2013-06-01

    Full Text Available   Objective(s: To investigate the expression of human papilloma virus (HPV L1 capsid protein, and human telomerase RNA component (hTERC in cervical cancer and the role of detection of both genes in screening of cervical cancer.   Materials and Methods: A total of 309 patients were recruited and cervical exfoliated cells were collected. Immunocytochemistry was employed to detect HPV L1 capsid protein, and fluorescent in situ hybridization (FISH was performed to detect the hTERC. Results: The expression of HPV L1 capsid protein reduced with the increase of the histological grade of cervical cells and was negatively related to the grade of cervical lesions. However, the expression of hTERC increased with the increase of the histological grade and positively associated with the grade of cervical lesions. The proportion of patients with L1(-/hTERC(+ was higher in patients with histological grade of CIN2 or higher than that in those with histological grade of CIN1. The L1(+/hTERC(- and L1(-/hTERC(- were negatively related to the grade of cervical lesions. L1(-/hTERC(+ was positively associated with the grade of cervical lesions. The L1/hTERC ratio increased. The negative predictive value of both HPV L1 and hTERC was higher than that of HPV L1 or hTERC, but there was no marked difference in the screening efficacy of cervical cancer among HPV L1, hTERC and HPV L1+hTERC. Conclusion: HPV L1 capsid protein and hTERC gene may serve as markers for the early diagnosis and prediction of cervical lesions. The increase in L1/hTERC ratio reflects the progression of cervical lesions to a certain extent.

  11. Nuclear structure of 194Pt

    International Nuclear Information System (INIS)

    Cleveland, W.E.; Zganjar, E.F.

    1976-01-01

    The decay of 194 Ir has been thoroughly studied resulting in the construction of a decay scheme consisting of 26 excited states and 69 transitions. Nine new levels and 29 new transitions were added to the previously known scheme. Of these, levels at 1,893.6 and 2,053.0 keV as well as 9 γ-ray transitions are new to the 194 Pt level scheme. Precise γ-ray energy and intensity measurements as well as quantitative coincidence measurements were performed, and the internal conversion spectrum was investigated with a Si(Li) detector. Directional correlation measurements were performed for selected cascades with the major result being the unique assignment of 0 + to the new level at 1,893.6 keV. The structure was interpreted within the framework of the PPQ model as well as the effective-core picture including nuclear triaxiality. (orig.) [de

  12. Nonlinear PT-symmetric plaquettes

    International Nuclear Information System (INIS)

    Li Kai; Kevrekidis, P G; Malomed, Boris A; Günther, Uwe

    2012-01-01

    We introduce four basic two-dimensional (2D) plaquette configurations with onsite cubic nonlinearities, which may be used as building blocks for 2D PT-symmetric lattices. For each configuration, we develop a dynamical model and examine its PTsymmetry. The corresponding nonlinear modes are analyzed starting from the Hamiltonian limit, with zero value of the gain–loss coefficient, γ. Once the relevant waveforms have been identified (chiefly, in an analytical form), their stability is examined by means of linearization in the vicinity of stationary points. This reveals diverse and, occasionally, fairly complex bifurcations. The evolution of unstable modes is explored by means of direct simulations. In particular, stable localized modes are found in these systems, although the majority of identified solutions are unstable. This article is part of a special issue of Journal of Physics A: Mathematical and Theoretical devoted to ‘Quantum physics with non-Hermitian operators’. (paper)

  13. Adsorption studies on Pt(111)

    International Nuclear Information System (INIS)

    Hopster, H.

    1977-06-01

    The adsorption of O 2 , CO, and C 2 H 2 as well as the CO oxidation on Pt(111) were studied by high-resolution electron spectroscopy. Using a platinum monocrystal sample with a contonuous stage density, the adhesion coefficient for O 2 and the reaction probability for CO were determined as a function of stage density and oxygen cover by measuring the oxygen cover and its time behaviour. The study of vibrations of adsorbed CO showed that CO is bound in linear form on two different adsorption sites. The adsorption of acetylene was studied at 140 K and 300 K. The frequencies of the C-H stretching and flexural vibrations as well as the C-C-H bonding angle were determined. (orig./GSC) [de

  14. Structure and magnetic properties of L10-FePt thin films on TiN/RuAl underlayers

    International Nuclear Information System (INIS)

    Yang En; Ratanaphan, Sutatch; Zhu Jiangang; Laughlin, David E.

    2011-01-01

    Highly ordered L1 0 FePt-oxide thin films with small grains were prepared by using a RuAl layer as a grain size defining seed layer along with a TiN barrier layer. Different HAMR (Heat Assisted Magnetic Recording) favorable underlayers were studied to encourage perpendicular texture and preferred microstructure. It was found that the epitaxial and small grain growth from the RuAl/TiN underlayer results in small and uniform grains in the FePt layer with perpendicular texture. By introducing the grain size defining underlayers, the FePt grain size can be reduced from 30 to 6 nm with the same volume fraction (9%) of SiO 2 in the film, excellent perpendicular texture, and very high order parameter at 520 deg. C.

  15. Surface coverage of Pt atoms on PtCo nanoparticles and catalytic kinetics for oxygen reduction

    Energy Technology Data Exchange (ETDEWEB)

    Jiang Rongzhong, E-mail: rongzhong.jiang@us.army.mi [Sensors and Electron Devices Directorate, U.S. Army Research Laboratory, 2800 Powder Mill Road, Adelphi, MD 20783-1197 (United States); Rong, Charles; Chu, Deryn [Sensors and Electron Devices Directorate, U.S. Army Research Laboratory, 2800 Powder Mill Road, Adelphi, MD 20783-1197 (United States)

    2011-02-01

    The surface coverage of Pt atoms on PtCo nanoparticles and its effect on catalytic kinetics for oxygen reduction were investigated. The PtCo nanoparticles with different surface coverage of Pt atoms were synthesized with various methods, including normal chemical method, microemulsion synthesis, and ultrasound-assisted microemulsion. A model of Pt atoms filling into a spherical nanoparticle was proposed to explain the relationship of surface metal atoms and nanoparticle size. The catalytic activity of the PtCo nano-particles is highly dependent on the synthetic methods, even if they have the same chemical composition. The PtCo nano-particles synthesized with ultrasound-assisted microemulsion showed the highest activity, which is attributed to an increase of active surface coverage of Pt atoms on the metal nanoparticles. The rate of oxygen reduction at 0.5 V (vs. SCE) catalyzed by the PtCo synthesized with ultrasound-assisted micro-emulsion was about four times higher than that of the PtCo synthesized with normal chemical method. As demonstrated with rotating-ring disk electrode measurement, the PtCo nano-particles can catalyze oxygen 4-electron reduction to water without intermediate H{sub 2}O{sub 2} detected.

  16. Corrosion inhibition of powder metallurgy Mg by fluoride treatments.

    Science.gov (United States)

    Pereda, M D; Alonso, C; Burgos-Asperilla, L; del Valle, J A; Ruano, O A; Perez, P; Fernández Lorenzo de Mele, M A

    2010-05-01

    Pure Mg has been proposed as a potential degradable biomaterial to avoid both the disadvantages of non-degradable internal fixation implants and the use of alloying elements that may be toxic. However, it shows excessively high corrosion rate and insufficient yield strength. The effects of reinforcing Mg by a powder metallurgy (PM) route and the application of biocompatible corrosion inhibitors (immersion in 0.1 and 1M KF solution treatments, 0.1M FST and 1M FST, respectively) were analyzed in order to improve Mg mechanical and corrosion resistance, respectively. Open circuit potential measurements, polarization techniques (PT), scanning electrochemical microscopy (SECM) and electrochemical impedance spectroscopy (EIS) were performed to evaluate its corrosion behavior. SECM showed that the local current of attacked areas decreased during the F(-) treatments. The corrosion inhibitory action of 0.1M FST and 1M FST in phosphate buffered solution was assessed by PT and EIS. Under the experimental conditions assayed, 0.1M FST revealed better performance. X-ray photoelectron spectroscopy, energy dispersive X-ray and X-ray diffraction analyses of Mg(PM) with 0.1M FST showed the presence of KMgF(3) crystals on the surface while a MgF(2) film was detected for 1M FST. After fluoride inhibition treatments, promising results were observed for Mg(PM) as degradable metallic biomaterial due to its higher yield strength and lower initial corrosion rate than untreated Mg, as well as a progressive loss of the protective characteristics of the F(-)-containing film which ensures the gradual degradation process. Copyright (c) 2009 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  17. Ethanol electrooxidation on Pt-Sn and Pt-Sn-W bulk alloys

    Energy Technology Data Exchange (ETDEWEB)

    Anjos, D.M. dos; Hahn, F.; Leger, J.M.; Kokoh, K.B. [Universite de Poitiers, Poitiers Cedex (France). Centre National de la Recherche Scientifique (CNRS). Equipe Electrocatalyse; Tremiliosi-Filho, G. [Universidade de Sao Paulo (USP), Sao Carlos, SP (Brazil). Inst. de Quimica

    2008-07-01

    Ethanol oxidation has been studied on Pt-Sn and Pt-Sn-W electrodes prepared in an arc-melting furnace. Different electrochemical techniques like cyclic voltammetry and chronoamperometry were used to evaluate the catalytic activity of these materials. The electro-oxidation process was also investigated by in situ infrared reflectance spectroscopy in order to determine adsorbed intermediates and reaction products. Experimental results indicated that Pt-Sn and Pt-Sn-W alloys are able to oxidize ethanol mainly to acetaldehyde and acetic acid. Adsorbed CO was also detected, demonstrating the viability of splitting the C-C bond in the ethanol molecule during the oxidation process. The adsorbed CO was further oxidized to CO{sub 2}.This reaction product was clearly detected by SNIFTIRS. Pt-Sn-W catalyst showed a better electrochemical performance than Pt-Sn that, in it turn, is better than Pt-alone. (author)

  18. Magnetic and structural characterizations on nanoparticles of FePt, FeRh and their composites

    International Nuclear Information System (INIS)

    Ko, Hnin Yu Yu; Suzuki, Takao; Nam, Nguyen T.; Phuoc, Nguyen N.; Cao Jiangwei; Hirotsu, Yoshihiko

    2008-01-01

    The various compositions of FePt and FeRh nanoparticles, and their composite particles have been fabricated by the solution-phase chemical method and their magnetic properties characterized. High-resolution transmission electron microscopic observations indicate that mono-dispersed FeRh and FePt/FeRh nanoparticles are fabricated with the average size of 3-5 nm. However, larger size particles are distributed in the annealed state. From X-ray diffraction results, the as-deposited FeRh nanoparticles reveal a chemically disordered fcc structure which can be transformed into CsCl-type structure through thermal annealing. Similarly, the annealed FePt nanoparticles show the L1 0 -phase fct structure although the fcc structure is apparent in the as-deposited state. It is also found that the first time in the exchange bias effect in the composite of ferromagnetic (FePt) and anti-ferromagnetic (FeRh) nanoparticles; result in a shift of the hysteresis loop after field cooling process

  19. Influence of Support Material of PtSnNiGa/C Electrocatalysts for Ethanol Oxidation

    Directory of Open Access Journals (Sweden)

    Deise M Santos

    2017-07-01

    Full Text Available Ethanol is a promising alternative source for fuel cells due to its low toxicity and high power density. However, the cleavage of the C-C bond, CO poisoning, and low electrocatalyst stability are still considered crucial issues. To overcome this limitation, binary, ternary and quaternary electrocatalysts have been investigated along with new carbon supports. This paper presents a physicochemical and electrochemical investigation of quaternary PtSnNiGa/C electrocatalysts supported on Vulcan XC72 and Printex-L6 carbons and also a carbon produced by natural gas pyrolysis in an Argon plasma torch (Black Plasma. The electrochemical characterization was performed through cyclic voltammetry, chronoamperometry, chronopotentiometry and electrochemical impedance spectroscopy in the presence of ethanol 1.0 mol L-1. Energy dispersive X-ray spectroscopy, X-ray diffraction, Raman spectroscopy and transmission electron microscopy were also carried out for physicochemical characterization. The electrochemical results show that the quaternary electrocatalysts supported on Vulcan XC72 and Printex-L6 carbons display a high current normalized by Pt mass and are more stable than the electrocatalyst supported on Black Plasma. In addition, the quaternary electrocatalysts with reduced Pt loading display better electrocatalytic activity towards the EOR compared to high Pt loading electrocatalysts. DOI: http://dx.doi.org/10.17807/orbital.v9i3.949 

  20. Reducing the ordering temperature of CoPt nanoparticles by B additive

    Energy Technology Data Exchange (ETDEWEB)

    Khemjeen, Yutthaya [Materials Science and Nanotechnology Program, Faculty of Science, Khon Kaen University, Khon Kaen 40002 (Thailand); Pinitsoontorn, Supree, E-mail: psupree@kku.ac.th; Chompoosor, Apiwat [Department of Physics, Faculty of Science, Khon Kaen University, Khon Kaen 40002 (Thailand); Integrated Nanotechnology Research Center, Khon Kaen University, Khon Kaen 40002 (Thailand); Nanotec-KKU Center of Excellence on Advanced Nanomaterials for Energy Production and Storage, Khon Kaen University, Khon Kaen 40002 (Thailand); Maensiri, Santi [School of Physics, Institute of Science, Suranaree University of Technology, Nakhon Ratchasima 30000 (Thailand)

    2014-08-07

    We reported the effect of boron addition on magnetic properties and structure of CoPt nanoparticles prepared by a polyol method. The magnetic property measurement showed that the CoPt-B sample exhibited a much larger coercivity compared to the sample without B additive at the same annealing temperature. Transmission electron microscopy and energy dispersive X-ray spectroscopy revealed that the average particle size was about 2 nm for the as-synthesized sample with the ratio of Co and Pt close to 1:1. After annealing, the particle sizes increased but the composition was maintained. The phase transformation of the nanoparticles versus temperature was investigated using a combination of X-ray diffraction and in-situ X-ray absorption analysis. It was shown that the phase transition temperature at which the nanoparticles change from the disordered A1 phase to the ordered L1{sub 0} phase occurs at temperature of 600 °C. We concluded that boron additives could reduce the ordering temperature of CoPt of about 100 °C.

  1. Kerr microscopy study of exchange-coupled FePt/Fe exchange spring magnets

    Energy Technology Data Exchange (ETDEWEB)

    Hussain, Zaineb; Kumar, Dileep [UGC-DAE Consortium for Scientific Research, University Campus, Khandwa Road, Indore 452001 (India); Reddy, V. Raghavendra, E-mail: varimalla@yahoo.com [UGC-DAE Consortium for Scientific Research, University Campus, Khandwa Road, Indore 452001 (India); Gupta, Ajay [Amity Center for Spintronic Materials, Amity University, Noida 201303 (India)

    2017-05-15

    Magnetization reversal and magnetic microstructure of top soft magnetic layer (Fe) in exchange spring coupled L1{sub 0} FePt/Fe is studied using high resolution Kerr microscopy. With remnant state of the hard magnetic layer (L1{sub 0} FePt) as initial condition, magnetization loops along with magnetic domains are recorded for the top soft magnetic layer (Fe) using Kerr microscopy. Considerable shifting of Fe layer hysteresis loop from center which is similar to exchange bias phenomena is observed. It is also observed that one can tune the magnitude of hysteresis shift by reaching the remanent state from different saturating fields (H{sub SAT}) and also by varying the angle between measuring field and H{sub SAT}. The hysteresis loops and magnetic domains of top soft Fe layer demonstrate unambiguously that soft magnetic layer at remanent state in such exchange coupled system is having unidirectional anisotropy. An analogy is drawn and the observations are explained in terms of established model of exchange bias phenomena framed for field-cooled ferromagnetic - antiferromagnetic bilayer systems. - Highlights: • Kerr microscopy of top soft magnetic Fe layer in exchange spring coupled L1{sub 0} FePt (30 nm)/Fe (22 nm) is reported. • Considerable shifting of Fe layer hysteresis loop from center which is similar to exchange bias phenomena is observed. • Tuneable nature of magnitude of hysteresis shift is shown. • It is unambiguously shown that the top soft Fe magnetic layer at remanent state is having unidirectional anisotropy.

  2. Lunar and Lagrangian Point L1 L2 CubeSat Communication and Navigation Considerations

    Science.gov (United States)

    Schaire, Scott; Wong, Yen F.; Altunc, Serhat; Bussey, George; Shelton, Marta; Folta, Dave; Gramling, Cheryl; Celeste, Peter; Anderson, Mile; Perrotto, Trish; hide

    2017-01-01

    CubeSats have grown in sophistication to the point that relatively low-cost mission solutions could be undertaken for planetary exploration. There are unique considerations for lunar and L1/L2 CubeSat communication and navigation compared with low earth orbit CubeSats. This paper explores those considerations as they relate to the Lunar IceCube Mission. The Lunar IceCube is a CubeSat mission led by Morehead State University with participation from NASA Goddard Space Flight Center, Jet Propulsion Laboratory, the Busek Company and Vermont Tech. It will search for surface water ice and other resources from a high inclination lunar orbit. Lunar IceCube is one of a select group of CubeSats designed to explore beyond low-earth orbit that will fly on NASA’s Space Launch System (SLS) as secondary payloads for Exploration Mission (EM) 1. Lunar IceCube and the EM-1 CubeSats will lay the groundwork for future lunar and L1/L2 CubeSat missions. This paper discusses communication and navigation needs for the Lunar IceCube mission and navigation and radiation tolerance requirements related to lunar and L1/L2 orbits. Potential CubeSat radios and antennas for such missions are investigated and compared. Ground station coverage, link analysis, and ground station solutions are also discussed. This paper will describe modifications in process for the Morehead ground station, as well as further enhancements of the Morehead ground station and NASA Near Earth Network (NEN) that are being considered. The potential NEN enhancements include upgrading current NEN Cortex receiver with Forward Error Correction (FEC) Turbo Code, providing X-band uplink capability, and adding ranging options. The benefits of ground station enhancements for CubeSats flown on NASA Exploration Missions (EM) are presented. This paper also describes how the NEN may support lunar and L1/L2 CubeSats without any enhancements. In addition, NEN is studying other initiatives to better support the CubeSat community

  3. Highly effective and CO-tolerant PtRu electrocatalysts supported on poly(ethyleneimine) functionalized carbon nanotubes for direct methanol fuel cells

    International Nuclear Information System (INIS)

    Cheng, Yi; Jiang, San Ping

    2013-01-01

    A highly efficient and CO tolerant PtRu electrocatalysts supported on amino-rich, cationic poly(ethyleneimine) polyelectrolyte functionalized multi-walled carbon nanotubes (PtRu/PEI-MWCNTs) has been developed. The catalysts were characterized by thermogravimetric analysis, Raman spectroscopy, cyclic voltammograms, CO stripping, chronoamperometry, transmission electron microscopy (TEM) and X-ray diffraction (XRD). The PtRu particles with average size ∼2.5 nm are well dispersed on PEI-MWCNTs. The peak current for the methanol oxidation reaction on 40% PtRu/PEI-MWCNTs is 636mAmg Pt −1 , 5.7 times higher than 112mA mg Pt −1 measured on the 40% PtRu supported on acid treated MWCNTs (PtRu/AO-MWCNTs) under identical conditions. PtRu/PEI-MWCNTs catalysts exhibit a superior electrocatalytic activity and stability for the methanol oxidation reaction due to its high tolerance toward CO poisoning as compared with PtRu/AO-MWCNTs for direct methanol fuel cells

  4. Cell recognition molecule L1 promotes embryonic stem cell differentiation through the regulation of cell surface glycosylation

    Energy Technology Data Exchange (ETDEWEB)

    Li, Ying [Department of Biochemistry and Molecular Biology, Dalian Medical University, Dalian 116044 (China); Department of Clinical Laboratory, Second Affiliated Hospital of Dalian Medical University, Dalian 116023 (China); Huang, Xiaohua [Department of Biochemistry and Molecular Biology, Dalian Medical University, Dalian 116044 (China); Department of Clinical Biochemistry, College of Laboratory Medicine, Dalian Medical University, Dalian 116044 (China); An, Yue [Department of Clinical Laboratory, Second Affiliated Hospital of Dalian Medical University, Dalian 116023 (China); Ren, Feng [Department of Biochemistry and Molecular Biology, Dalian Medical University, Dalian 116044 (China); Yang, Zara Zhuyun; Zhu, Hongmei; Zhou, Lei [The Key Laboratory of Stem Cell and Regenerative Medicine, Institute of Molecular and Clinical Medicine, Kunming Medical University, Kunming 650228 (China); Department of Anatomy and Developmental Biology, Monash University, Clayton 3800 (Australia); He, Xiaowen; Schachner, Melitta [Keck Center for Collaborative Neuroscience and Department of Cell Biology and Neuroscience, Rutgers University, New Brunswick, NJ (United States); Xiao, Zhicheng, E-mail: zhicheng.xiao@monash.edu [The Key Laboratory of Stem Cell and Regenerative Medicine, Institute of Molecular and Clinical Medicine, Kunming Medical University, Kunming 650228 (China); Department of Anatomy and Developmental Biology, Monash University, Clayton 3800 (Australia); Ma, Keli, E-mail: makeli666@aliyun.com [Department of Biochemistry and Molecular Biology, Dalian Medical University, Dalian 116044 (China); Li, Yali, E-mail: yalilipaper@gmail.com [Department of Biochemistry and Molecular Biology, Dalian Medical University, Dalian 116044 (China); Department of Anatomy, National University of Singapore, Singapore 119078 (Singapore)

    2013-10-25

    Highlights: •Down-regulating FUT9 and ST3Gal4 expression blocks L1-induced neuronal differentiation of ESCs. •Up-regulating FUT9 and ST3Gal4 expression in L1-ESCs depends on the activation of PLCγ. •L1 promotes ESCs to differentiate into neuron through regulating cell surface glycosylation. -- Abstract: Cell recognition molecule L1 (CD171) plays an important role in neuronal survival, migration, differentiation, neurite outgrowth, myelination, synaptic plasticity and regeneration after injury. Our previous study has demonstrated that overexpressing L1 enhances cell survival and proliferation of mouse embryonic stem cells (ESCs) through promoting the expression of FUT9 and ST3Gal4, which upregulates cell surface sialylation and fucosylation. In the present study, we examined whether sialylation and fucosylation are involved in ESC differentiation through L1 signaling. RNA interference analysis showed that L1 enhanced differentiation of ESCs into neurons through the upregulation of FUT9 and ST3Gal4. Furthermore, blocking the phospholipase Cγ (PLCγ) signaling pathway with either a specific PLCγ inhibitor or knockdown PLCγ reduced the expression levels of both FUT9 and ST3Gal4 mRNAs and inhibited L1-mediated neuronal differentiation. These results demonstrate that L1 promotes neuronal differentiation from ESCs through the L1-mediated enhancement of FUT9 and ST3Gal4 expression.

  5. Cell recognition molecule L1 promotes embryonic stem cell differentiation through the regulation of cell surface glycosylation

    International Nuclear Information System (INIS)

    Li, Ying; Huang, Xiaohua; An, Yue; Ren, Feng; Yang, Zara Zhuyun; Zhu, Hongmei; Zhou, Lei; He, Xiaowen; Schachner, Melitta; Xiao, Zhicheng; Ma, Keli; Li, Yali

    2013-01-01

    Highlights: •Down-regulating FUT9 and ST3Gal4 expression blocks L1-induced neuronal differentiation of ESCs. •Up-regulating FUT9 and ST3Gal4 expression in L1-ESCs depends on the activation of PLCγ. •L1 promotes ESCs to differentiate into neuron through regulating cell surface glycosylation. -- Abstract: Cell recognition molecule L1 (CD171) plays an important role in neuronal survival, migration, differentiation, neurite outgrowth, myelination, synaptic plasticity and regeneration after injury. Our previous study has demonstrated that overexpressing L1 enhances cell survival and proliferation of mouse embryonic stem cells (ESCs) through promoting the expression of FUT9 and ST3Gal4, which upregulates cell surface sialylation and fucosylation. In the present study, we examined whether sialylation and fucosylation are involved in ESC differentiation through L1 signaling. RNA interference analysis showed that L1 enhanced differentiation of ESCs into neurons through the upregulation of FUT9 and ST3Gal4. Furthermore, blocking the phospholipase Cγ (PLCγ) signaling pathway with either a specific PLCγ inhibitor or knockdown PLCγ reduced the expression levels of both FUT9 and ST3Gal4 mRNAs and inhibited L1-mediated neuronal differentiation. These results demonstrate that L1 promotes neuronal differentiation from ESCs through the L1-mediated enhancement of FUT9 and ST3Gal4 expression

  6. miR-21-3p is a positive regulator of L1CAM in several human carcinomas.

    Science.gov (United States)

    Doberstein, Kai; Bretz, Niko P; Schirmer, Uwe; Fiegl, Heidi; Blaheta, Roman; Breunig, Christian; Müller-Holzner, Elisabeth; Reimer, Dan; Zeimet, Alain G; Altevogt, Peter

    2014-11-28

    Expression of L1 cell adhesion molecule (L1CAM) occurs frequently in human cancers and is associated with poor prognosis in cancers such as ovarian, endometrial, breast, renal cell carcinoma and pancreatic ductal adenocarcinoma. L1CAM promotes cell motility, invasion, chemoresistance and metastasis formation. Elucidating genetic processes involved in the expression of L1CAM in cancers is of considerable importance. Transcription factors such as SLUG, β-catenin/TCF-LEF, PAX8 and VHL have been implicated in the re-activation of L1CAM in various types of cancers. There is increasing evidence that micro-RNAs can also have strong effects on gene expression. Here we have identified miR-21-3p as a positive regulator of L1CAM expression. Over-expression of miR-21-3p (miR-21*) but not the complementary sequence miR-21-5p (miR-21) could strongly augment L1CAM expression in renal, endometrial and ovarian carcinoma derived cell lines by an unknown mechanism involving transcriptional activation of the L1CAM gene. In patient cohorts from renal, endometrial and ovarian cancers we observed a strong positive correlation of L1CAM and miR-21-3p expressions. Although L1CAM alone was a reliable marker for overall and disease free survival, the combination of L1CAM and miR-21-3p expressions strongly enhanced the predictive power. Our findings shed new light on the complex regulation of L1CAM in cancers and advocate the use of L1CAM/miR-21-3p for diagnostic application. Copyright © 2014 Elsevier Ireland Ltd. All rights reserved.

  7. WATERSHED INFARCTION IN HYPEREOSINOPHILIC SYNDROME: A DIAGNOSTIC DILEMMA IN FIP1L1-PDGFR ALPHA-ASSOCIATED MYELOID NEOPLASM.

    Science.gov (United States)

    Marton, Imelda; Pósfai, Éva; Annus, János Kristóf; Borbényi, Zita; Nemes, Attila; Vecsei, László; Vörös, Erika

    2015-05-30

    The FIP1L1-PDGFR alpha-positive, hypereosinophilic syndrome (HES) is a new category of hematological entities. Various clinical symptoms may occur, with no specific characteristics in either the clinical picture or the neuroimaging findings, and this may give rise to a diagnostic dilemma. A report on a long follow-up period (10 years) in a case of HES that presented with neuropsychiatric symptoms appears to be unique. Besides the complexity of the diagnostic process, the successful treatment is discussed. The HES was diagnosed in a male patient at the age of 33 years, with involvement of the central nervous system and the myocardium. After the onset of the clinical signs, the MRI indicated bilateral cerebral and cerebellar cortico-subcortical lesions involving the watershed areas, mainly in the parieto-occipital regions. High-dose intravenous steroid (methylprednisolone 500 mg/day) alleviated the neurological symptoms within a few weeks, and the administration of imatinib (200 mg/day) resulted in an impressive regression of the hypereosinophilia and splenomegaly within 6 weeks. During the follow-up, the patient has continued to receive imatinib. The molecular remission has persisted, no new complaints have developed and the condition of the patient has remained stable. The timely recognition of the HES and identification of the disease subtype which led to the administration of imatinib may be the key to successful treatment. The long stable follow-up period gives rise to a new dilemma in the treatment of the HES in these special cases: for how long should a patient receive a tyrosine kinase inhibitor, and may the treatment be suspended?

  8. Simulations and Prototyping of the LHCb L1 and HLT Triggers

    CERN Document Server

    Shears, T; Kechadi, T; McNulty, R; Smoker, A; Barczyk, A; Dufey, J; Jost, B; Neufeld, N

    2004-01-01

    The Level 1 (L1) and High Level Triggers (HLT) for the LHCb experiment are software triggers which will be implemented on a farm of approximately 1800 computers, connected via a Gigabit LAN with a bandwidth capacity of 7.1 GB/s and containing some 500 Ethernet links. The architecture of the readout network must be optimised to maximise data throughput, control data flow and minimise errors. We report on the development and results of two independent software simulations which allow us to evaluate the performance of various network configurations. We also describe the construction of two hardware testbeds of the LHCb L1 and HLT trigger system, which allow microscopic and macroscopic study of network and switch behaviour.

  9. L1-Penalized N-way PLS for subset of electrodes selection in BCI experiments

    Science.gov (United States)

    Eliseyev, Andrey; Moro, Cecile; Faber, Jean; Wyss, Alexander; Torres, Napoleon; Mestais, Corinne; Benabid, Alim Louis; Aksenova, Tetiana

    2012-08-01

    Recently, the N-way partial least squares (NPLS) approach was reported as an effective tool for neuronal signal decoding and brain-computer interface (BCI) system calibration. This method simultaneously analyzes data in several domains. It combines the projection of a data tensor to a low dimensional space with linear regression. In this paper the L1-Penalized NPLS is proposed for sparse BCI system calibration, allowing uniting the projection technique with an effective selection of subset of features. The L1-Penalized NPLS was applied for the binary self-paced BCI system calibration, providing selection of electrodes subset. Our BCI system is designed for animal research, in particular for research in non-human primates.

  10. Regulated expression of the neural cell adhesion molecule L1 by specific patterns of neural impulses.

    Science.gov (United States)

    Itoh, K; Stevens, B; Schachner, M; Fields, R D

    1995-11-24

    Development of the mammalian nervous system is regulated by neural impulse activity, but the molecular mechanisms are not well understood. If cell recognition molecules [for example, L1 and the neural cell adhesion molecule (NCAM)] were influenced by specific patterns of impulse activity, cell-cell interactions controlling nervous system structure could be regulated by nervous system function at critical stages of development. Low-frequency electrical pulses delivered to mouse sensory neurons in culture (0.1 hertz for 5 days) down-regulated expression of L1 messenger RNA and protein (but not NCAM). Fasciculation of neurites, adhesion of neuroblastoma cells, and the number of Schwann cells on neurites was reduced after 0.1-hertz stimulation, but higher frequencies or stimulation after synaptogenesis were without effect.

  11. Automated Manipulation of Micro-Nano Objects with SPM by Using L1 Adaptive Controller

    Directory of Open Access Journals (Sweden)

    Qinmin Yang

    2012-12-01

    Full Text Available In this paper, a novel control methodology for automatically manipulating micro/nano particles by using a Scanning Probe Microscope (SPM is presented. First of all, a mathematical model of micro/nanomanipulation, including the interactive forces and dynamics between the tip, particle and substrate along with the roughness effect of the substrate, is described. Then, the L1 adaptive control design for the manipulation system of micro/nano objects is presented, which consists of a state predictor with fast adaptation, a piece-wise continuous adaptive law and a low-pass filtered control design. This control framework can handle nonlinear uncertainties and ensures uniformly bounded tracking performance. The tracking performance bound can be systematically improved by reducing the step size of integration. Rigorous mathematical proof is provided. Simulation results demonstrate the effectiveness of the presented L1 adaptive control law on the micro/nanomanipulation model.

  12. A proximity algorithm accelerated by Gauss-Seidel iterations for L1/TV denoising models

    Science.gov (United States)

    Li, Qia; Micchelli, Charles A.; Shen, Lixin; Xu, Yuesheng

    2012-09-01

    Our goal in this paper is to improve the computational performance of the proximity algorithms for the L1/TV denoising model. This leads us to a new characterization of all solutions to the L1/TV model via fixed-point equations expressed in terms of the proximity operators. Based upon this observation we develop an algorithm for solving the model and establish its convergence. Furthermore, we demonstrate that the proposed algorithm can be accelerated through the use of the componentwise Gauss-Seidel iteration so that the CPU time consumed is significantly reduced. Numerical experiments using the proposed algorithm for impulsive noise removal are included, with a comparison to three recently developed algorithms. The numerical results show that while the proposed algorithm enjoys a high quality of the restored images, as the other three known algorithms do, it performs significantly better in terms of computational efficiency measured in the CPU time consumed.

  13. A proximity algorithm accelerated by Gauss–Seidel iterations for L1/TV denoising models

    International Nuclear Information System (INIS)

    Li, Qia; Shen, Lixin; Xu, Yuesheng; Micchelli, Charles A

    2012-01-01

    Our goal in this paper is to improve the computational performance of the proximity algorithms for the L1/TV denoising model. This leads us to a new characterization of all solutions to the L1/TV model via fixed-point equations expressed in terms of the proximity operators. Based upon this observation we develop an algorithm for solving the model and establish its convergence. Furthermore, we demonstrate that the proposed algorithm can be accelerated through the use of the componentwise Gauss–Seidel iteration so that the CPU time consumed is significantly reduced. Numerical experiments using the proposed algorithm for impulsive noise removal are included, with a comparison to three recently developed algorithms. The numerical results show that while the proposed algorithm enjoys a high quality of the restored images, as the other three known algorithms do, it performs significantly better in terms of computational efficiency measured in the CPU time consumed. (paper)

  14. PD-L1 blockade with avelumab: A new paradigm for treating Merkel cell carcinoma.

    Science.gov (United States)

    Barkdull, Savannah; Brownell, Isaac

    2017-12-02

    Merkel cell carcinoma (MCC) is a rare and aggressive neuroendocrine skin cancer. Until recently, no durable treatment options were available for patients with advanced disease. As an immunogenic cancer, MCC was hypothesized to be a candidate for PD-L1/PD-1 targeted therapy. On March 23, 2017 the US Food and Drug Administration granted accelerated approval for avelumab, an anti-PD-L1 monoclonal antibody, for the treatment of metastatic MCC on the basis of the JAVELIN Merkel 200 trial. Here we examine the results and implications of this pivotal study, published in Lancet Oncology by Kaufman et al., as well as current developments in the use of immune-checkpoint therapies for treating patients with MCC.

  15. STRUCTURE TENSOR IMAGE FILTERING USING RIEMANNIAN L1 AND L∞ CENTER-OF-MASS

    Directory of Open Access Journals (Sweden)

    Jesus Angulo

    2014-06-01

    Full Text Available Structure tensor images are obtained by a Gaussian smoothing of the dyadic product of gradient image. These images give at each pixel a n×n symmetric positive definite matrix SPD(n, representing the local orientation and the edge information. Processing such images requires appropriate algorithms working on the Riemannian manifold on the SPD(n matrices. This contribution deals with structure tensor image filtering based on Lp geometric averaging. In particular, L1 center-of-mass (Riemannian median or Fermat-Weber point and L∞ center-of-mass (Riemannian circumcenter can be obtained for structure tensors using recently proposed algorithms. Our contribution in this paper is to study the interest of L1 and L∞ Riemannian estimators for structure tensor image processing. In particular, we compare both for two image analysis tasks: (i structure tensor image denoising; (ii anomaly detection in structure tensor images.

  16. Thermodynamic modeling of the Pt-Zr system

    International Nuclear Information System (INIS)

    Gao Yongliang; Guo Cuiping; Li Changrong; Du Zhenmin

    2010-01-01

    By means of the CALPHAD (CALculation of PHAse Diagram) technique, the Pt-Zr system was critically assessed. The solution phases (liquid, bcc, fcc and hcp) are described with the substitutional model. The intermetallic compounds Pt 4 Zr, Pt 4 Zr 3 , αPtZr and Pt 3 Zr 5 are treated as the formula (Pt,Zr) m (Pt,Zr) n by a two-sublattice model with the elements Pt and Zr on the first and the second sublattices, respectively. A two-sublattice model (Pt,Zr) 0.5 (Pt,Zr) 0.5 is applied to describe the compound βPtZr with CsCl-type structure (B2) in order to cope with the order-disorder transition between bcc solution (A2) and βPtZr (B2). Another two-sublattice model (Pt,Zr) 0.75 (Pt,Zr) 0.25 with Ni 3 Ti-type structure (D0 24 ) is applied to describe the compound Pt 3 Zr in order to cope with the order-disorder transition between hexagonal close-packed (A3) and Pt 3 Zr (D0 24 ). The compound Pt 10 Zr 7 is treated as a stoichiometric compound. A set of self-consistent thermodynamic parameters of the Pt-Zr system was obtained. (orig.)

  17. Experiment data report for LOFT nonnuclear test L1-3

    International Nuclear Information System (INIS)

    Millar, G.M.

    1977-04-01

    Test L1-3 was the third in a series of five nonnuclear isothermal blowdown tests conducted by the Loss of Fluid Test (LOFT) Program. For this test the LOFT Facility was configured to simulate a loss-of-coolant accident in a large pressurized water reactor resulting from a 200 percent double-ended shear break in a cold leg of the primary coolant system. A hydraulic core simulator assembly was installed in place of the nuclear core. The initial conditions in the primary coolant system intact loop were: temperature at 540 0 F, pressure at 2256 psig, and loop flow at 2.34 x 10 6 lbm/hr. During system depressurization, emergency core cooling water was specified to be injected into the lower plenum of the reactor vessel using an accumulator, a low-pressure injection system pump, and a high-pressure injection system pump to provide data on the effects of emergency core cooling on the system thermal-hydraulic response. Injection into the lower plenum was initiated from the high- and low-pressure injection systems. Injection from the accumulator, however, was not initiated because a valve was inadvertently left closed. The experiment, therefore, was not completely successful in that one of the objectives outlined in the experiment operating specification for this test was not accomplished. Test L1-3 was repeated at Test L1-3A to meet the experimental requirements. Despite these difficulties, Test L1-3 did provide very valuable data to verify experiment repeatability

  18. Bi-allelic Mutations in PKD1L1 Are Associated with Laterality Defects in Humans.

    Science.gov (United States)

    Vetrini, Francesco; D'Alessandro, Lisa C A; Akdemir, Zeynep C; Braxton, Alicia; Azamian, Mahshid S; Eldomery, Mohammad K; Miller, Kathryn; Kois, Chelsea; Sack, Virginia; Shur, Natasha; Rijhsinghani, Asha; Chandarana, Jignesh; Ding, Yan; Holtzman, Judy; Jhangiani, Shalini N; Muzny, Donna M; Gibbs, Richard A; Eng, Christine M; Hanchard, Neil A; Harel, Tamar; Rosenfeld, Jill A; Belmont, John W; Lupski, James R; Yang, Yaping

    2016-10-06

    Disruption of the establishment of left-right (L-R) asymmetry leads to situs anomalies ranging from situs inversus totalis (SIT) to situs ambiguus (heterotaxy). The genetic causes of laterality defects in humans are highly heterogeneous. Via whole-exome sequencing (WES), we identified homozygous mutations in PKD1L1 from three affected individuals in two unrelated families. PKD1L1 encodes a polycystin-1-like protein and its loss of function is known to cause laterality defects in mouse and medaka fish models. Family 1 had one fetus and one deceased child with heterotaxy and complex congenital heart malformations. WES identified a homozygous splicing mutation, c.6473+2_6473+3delTG, which disrupts the invariant splice donor site in intron 42, in both affected individuals. In the second family, a homozygous c.5072G>C (p.Cys1691Ser) missense mutation was detected in an individual with SIT and congenital heart disease. The p.Cys1691Ser substitution affects a highly conserved cysteine residue and is predicted by molecular modeling to disrupt a disulfide bridge essential for the proper folding of the G protein-coupled receptor proteolytic site (GPS) motif. Damaging effects associated with substitutions of this conserved cysteine residue in the GPS motif have also been reported in other genes, namely GPR56, BAI3, and PKD1 in human and lat-1 in C. elegans, further supporting the likely pathogenicity of p.Cys1691Ser in PKD1L1. The identification of bi-allelic PKD1L1 mutations recapitulates previous findings regarding phenotypic consequences of loss of function of the orthologous genes in mice and medaka fish and further expands our understanding of genetic contributions to laterality defects in humans. Copyright © 2016 American Society of Human Genetics. Published by Elsevier Inc. All rights reserved.

  19. Enhancing Foreign Language Learning through Listening Strategies Delivered in L1: An Experimental Study

    OpenAIRE

    Hitendra Pillay; Hossein Bozorgian

    2013-01-01

    Listening used in language teaching refers to a complex process that allows us to understand spoken language. The current study, conducted in Iran with an experimental design, investigated the effectiveness of teaching listening strategies delivered in L1 (Persian) and its effect on listening comprehension in L2. Five listening strategies: Guessing, making inferences, identifying topics, repetition, and note-taking were taught over 14 weeks during a semester. Sixty lower intermediate female p...

  20. A Fast and Accurate Algorithm for l1 Minimization Problems in Compressive Sampling (Preprint)

    Science.gov (United States)

    2013-01-22

    However, updating uk+1 via the formulation of Step 2 in Algorithm 1 can be implemented through the use of the component-wise Gauss - Seidel iteration which...may accelerate the rate of convergence of the algorithm and therefore reduce the total CPU-time consumed. The efficiency of component-wise Gauss - Seidel ...Micchelli, L. Shen, and Y. Xu, A proximity algorithm accelerated by Gauss - Seidel iterations for L1/TV denoising models, Inverse Problems, 28 (2012), p

  1. L1 Adaptive Manoeuvring Control of Unmanned High-speed Water Craft

    DEFF Research Database (Denmark)

    Svendsen, Casper H.; Holck, Niels Ole; Galeazzi, Roberto

    2012-01-01

    This work addresses the issue of designing an adaptive robust control system to govern the steering of a high speed unmanned personal watercraft (PWC) maintaining equal performance across the craft’s envelope of operation. The maneuvering dynamics of a high speed PWC is presented and a strong var......-of-freedom surge-sway-yaw-roll model. An L1 adaptive autopilot is then designed, which allows to achieve fast adaption to system parameters’ changes and robustness of the closed loop system....

  2. Intrinsic magnetic properties of L1(0) FeNi obtained from meteorite NWA 6259

    Energy Technology Data Exchange (ETDEWEB)

    Poirier, E; Pinkerton, FE; Kubic, R; Mishra, RK; Bordeaux, N; Mubarok, A; Lewis, LH; Goldstein, JI; Skomski, R; Barmak, K

    2015-05-07

    FeNi having the tetragonal L1(0) crystal structure is a promising new rare-earth-free permanent magnet material. Laboratory synthesis is challenging, however, tetragonal L1(0) FeNi-the mineral "tetrataenite"-has been characterized using specimens found in nickel-iron meteorites. Most notably, the meteorite NWA 6259 recovered from Northwest Africa is 95 vol.% tetrataenite with a composition of 43 at.% Ni. Hysteresis loops were measured as a function of sample orientation on a specimen cut from NWA 6259 in order to rigorously deduce the intrinsic hard magnetic properties of its L1(0) phase. Electron backscatter diffraction showed that NWA 6259 is strongly textured, containing L1(0) grains oriented along any one of the three equivalent cubic directions of the parent fcc structure. The magnetic structure was modeled as a superposition of the three orthonormal uniaxial variants. By simultaneously fitting first-quadrant magnetization data for 13 different orientations of the sample with respect to the applied field direction, the intrinsic magnetic properties were estimated to be saturation magnetization 4 pi M-s = 14.7 kG and anisotropy field H-a = 14.4 kOe. The anisotropy constant K = 0.84 MJ/m(3) is somewhat smaller than the value K = 1.3 MJ/m(3) obtained by earlier researchers from nominally equiatomic FeNi prepared by neutron irradiation accompanied by annealing in a magnetic field, suggesting that higher Ni content (fewer Fe antisite defects) may improve the anisotropy. The fit also indicated that NWA 6259 contains one dominant variant (62% by volume), the remainder of the sample being a second variant, and the third variant being absent altogether. (C) 2015 AIP Publishing LLC.

  3. Strongly nonlinear nonhomogeneous elliptic unilateral problems with L^1 data and no sign conditions

    Directory of Open Access Journals (Sweden)

    Elhoussine Azroul

    2012-05-01

    Full Text Available In this article, we prove the existence of solutions to unilateral problems involving nonlinear operators of the form: $$ Au+H(x,u,abla u=f $$ where $A$ is a Leray Lions operator from $W_0^{1,p(x}(Omega$ into its dual $W^{-1,p'(x}(Omega$ and $H(x,s,xi$ is the nonlinear term satisfying some growth condition but no sign condition. The right hand side $f$ belong to $L^1(Omega$.

  4. Intrinsic magnetic properties of L1{sub 0} FeNi obtained from meteorite NWA 6259

    Energy Technology Data Exchange (ETDEWEB)

    Poirier, Eric [MEDA Engineering and Technical Services, Southfield, Michigan 48075 (United States); Pinkerton, Frederick E., E-mail: frederick.e.pinkerton@gm.com; Kubic, Robert; Mishra, Raja K. [Chemical Sciences and Materials Systems Lab, GM R and D Center, Warren, Michigan 48090 (United States); Bordeaux, Nina; Lewis, Laura H. [Department of Chemical Engineering, Northeastern University, Boston, Massachusetts 02115 (United States); Mubarok, Arif; Goldstein, Joseph I. [Department of Mechanical and Industrial Engineering, University of Massachusetts, Amherst, Massachusetts 01003 (United States); Skomski, Ralph [Department of Physics and Astronomy, University of Nebraska, Lincoln, Nebraska 68588 (United States); Barmak, Katayun [Department of Applied Physics and Applied Mathematics, Columbia University, New York, New York 10027 (United States)

    2015-05-07

    FeNi having the tetragonal L1{sub 0} crystal structure is a promising new rare-earth-free permanent magnet material. Laboratory synthesis is challenging, however, tetragonal L1{sub 0} FeNi—the mineral “tetrataenite”—has been characterized using specimens found in nickel-iron meteorites. Most notably, the meteorite NWA 6259 recovered from Northwest Africa is 95 vol. % tetrataenite with a composition of 43 at. % Ni. Hysteresis loops were measured as a function of sample orientation on a specimen cut from NWA 6259 in order to rigorously deduce the intrinsic hard magnetic properties of its L1{sub 0} phase. Electron backscatter diffraction showed that NWA 6259 is strongly textured, containing L1{sub 0} grains oriented along any one of the three equivalent cubic directions of the parent fcc structure. The magnetic structure was modeled as a superposition of the three orthonormal uniaxial variants. By simultaneously fitting first-quadrant magnetization data for 13 different orientations of the sample with respect to the applied field direction, the intrinsic magnetic properties were estimated to be saturation magnetization 4πM{sub s} = 14.7 kG and anisotropy field H{sub a} = 14.4 kOe. The anisotropy constant K = 0.84 MJ/m{sup 3} is somewhat smaller than the value K = 1.3 MJ/m{sup 3} obtained by earlier researchers from nominally equiatomic FeNi prepared by neutron irradiation accompanied by annealing in a magnetic field, suggesting that higher Ni content (fewer Fe antisite defects) may improve the anisotropy. The fit also indicated that NWA 6259 contains one dominant variant (62% by volume), the remainder of the sample being a second variant, and the third variant being absent altogether.

  5. Characterization and enzyme-conjugation of a specific anti-L1 nanobody.

    Science.gov (United States)

    Minaeian, Sara; Rahbarizadeh, Fatemeh; Zarkesh Esfahani, Sayyed Hamid; Ahmadvand, Davoud

    2012-01-01

    Persistent infection of the human papillomaviruses (HPV) has been shown to result in cervical cancer and intraepithelial neoplasia. Early detection and screening programs are essential strategies against cervical cancer. A nanobody is the smallest antigen-binding fragment known and is derived from a camelid heavy-chain antibody. This tiny protein shows high solubility and stability. It can be produced cost-effectively with high yield production. In this study, we enriched a nanobody library against the L1 protein of HPV. Several colons were selected from this enriched library using monoclonal phage-enzyme linked immunosorbent assay (phage-ELISA) and analyzed for identification of nanobody genes. The expression of nanobody fragments was performed in Rosetta gami2. The C74 nanobody that showed strong binding to the L1 protein of HPV16 was selected, purified, and characterized by Western blotting and ELISA. The selected nanobody was tested for sensitivity, specificity, and affinity. A nanobody conjugated to horseradish peroxidase (HRP) was selected and used for detection of L1 protein of HPV16. This study demonstrates that the C74-HRP, due to its specificity and good binding affinity for a specific viral antigen, is a potential diagnostic tool that can be used as a promising reagent for the new generation of HPV diagnosis approaches.

  6. Heads or tails: L1 insertion-associated 5' homopolymeric sequences

    Directory of Open Access Journals (Sweden)

    Meyer Thomas J

    2010-02-01

    Full Text Available Abstract Background L1s are one of the most successful autonomous mobile elements in primate genomes. These elements comprise as much as 17% of primate genomes with the majority of insertions occurring via target primed reverse transcription (TPRT. Twin priming, a variant of TPRT, can result in unusual DNA sequence architecture. These insertions appear to be inverted, truncated L1s flanked by target site duplications. Results We report on loci with sequence architecture consistent with variants of the twin priming mechanism and introduce dual priming, a mechanism that could generate similar sequence characteristics. These insertions take the form of truncated L1s with hallmarks of classical TPRT insertions but having a poly(T simple repeat at the 5' end of the insertion. We identified loci using computational analyses of the human, chimpanzee, orangutan, rhesus macaque and marmoset genomes. Insertion site characteristics for all putative loci were experimentally verified. Conclusions The 39 loci that passed our computational and experimental screens probably represent inversion-deletion events which resulted in a 5' inverted poly(A tail. Based on our observations of these loci and their local sequence properties, we conclude that they most probably represent twin priming events with unusually short non-inverted portions. We postulate that dual priming could, theoretically, produce the same patterns. The resulting homopolymeric stretches associated with these insertion events may promote genomic instability and create potential target sites for future retrotransposition events.

  7. Ginkgolide C Suppresses Adipogenesis in 3T3-L1 Adipocytes via the AMPK Signaling Pathway

    Directory of Open Access Journals (Sweden)

    Chian-Jiun Liou

    2015-01-01

    Full Text Available Ginkgolide C, isolated from Ginkgo biloba leaves, is a flavone reported to have multiple biological functions, from decreased platelet aggregation to ameliorating Alzheimer disease. The study aim was to evaluate the antiadipogenic effect of ginkgolide C in 3T3-L1 adipocytes. Ginkgolide C was used to treat differentiated 3T3-L1 cells. Cell supernatant was collected to assay glycerol release, and cells were lysed to measure protein and gene expression related to adipogenesis and lipolysis by western blot and real-time PCR, respectively. Ginkgolide C significantly suppressed lipid accumulation in differentiated adipocytes. It also decreased adipogenesis-related transcription factor expression, including peroxisome proliferator-activated receptor and CCAAT/enhancer-binding protein. Furthermore, ginkgolide C enhanced adipose triglyceride lipase and hormone-sensitive lipase production for lipolysis and increased phosphorylation of AMP-activated protein kinase (AMPK, resulting in decreased activity of acetyl-CoA carboxylase for fatty acid synthesis. In coculture with an AMPK inhibitor (compound C, ginkgolide C also improved activation of sirtuin 1 and phosphorylation of AMPK in differentiated 3T3-L1 cells. The results suggest that ginkgolide C is an effective flavone for increasing lipolysis and inhibiting adipogenesis in adipocytes through the activated AMPK pathway.

  8. Endoplasmic reticulum stress suppresses lipin-1 expression in 3T3-L1 adipocytes

    Energy Technology Data Exchange (ETDEWEB)

    Takahashi, Nobuhiko, E-mail: ntkhs@hoku-iryo-u.ac.jp [Department of Internal Medicine, School of Dentistry, Health Sciences University of Hokkaido, 1757, Kanazawa, Ishikari-Toubetsu, Hokkaido 061-0023 (Japan); Division of Gastroenterology and Hematology/Oncology, Department of Medicine, Asahikawa Medical University, 2-1-1-1, Midorigaoka-Higashi, Asahikawa, Hokkaido 078-8510 (Japan); Yoshizaki, Takayuki [Innovation Center, Kagoshima University, 1-21-40, Korimoto, Kagoshima 890-0065 (Japan); Hiranaka, Natsumi; Suzuki, Takeshi [Department of Internal Medicine, School of Dentistry, Health Sciences University of Hokkaido, 1757, Kanazawa, Ishikari-Toubetsu, Hokkaido 061-0023 (Japan); Yui, Tomoo; Akanuma, Masayoshi [Department of Fixed Prosthodontics and Oral Implantology, School of Dentistry, Health Sciences University of Hokkaido, 1757, Kanazawa, Ishikari-Toubetsu, Hokkaido 061-0023 (Japan); Kanazawa, Kaoru [Department of Dental Anesthesiology, School of Dentistry, Health Sciences University of Hokkaido, 1757, Kanazawa, Ishikari-Toubetsu, Hokkaido 061-0023 (Japan); Yoshida, Mika; Naito, Sumiyoshi [Department of Clinical Laboratory, Health Sciences University of Hokkaido, 1757, Kanazawa, Ishikari-Toubetsu, Hokkaido 061-0023 (Japan); Fujiya, Mikihiro; Kohgo, Yutaka [Division of Gastroenterology and Hematology/Oncology, Department of Medicine, Asahikawa Medical University, 2-1-1-1, Midorigaoka-Higashi, Asahikawa, Hokkaido 078-8510 (Japan); Ieko, Masahiro [Department of Internal Medicine, School of Dentistry, Health Sciences University of Hokkaido, 1757, Kanazawa, Ishikari-Toubetsu, Hokkaido 061-0023 (Japan)

    2013-02-01

    Highlights: ► Lipin-1 involves lipid metabolism, adipocyte differentiation, and inflammation. ► Adipose lipin-1 expression is reduced in obesity. ► ER stress suppresses lipin-1 expression in 3T3-L1 adipocytes. ► Activation of PPAR-γ recovers ER stress-induced lipin-1 reduction. -- Abstract: Lipin-1 plays crucial roles in the regulation of lipid metabolism and cell differentiation in adipocytes. In obesity, adipose lipin-1 mRNA expression is decreased and positively correlated with systemic insulin sensitivity. Amelioration of the lipin-1 depletion might be improved dysmetabolism. Although some cytokines such as TNF-α and interleukin-1β reduces adipose lipin-1 expression, the mechanism of decreased adipose lipin-1 expression in obesity remains unclear. Recently, endoplasmic reticulum (ER) stress is implicated in the pathogenesis of obesity. Here we investigated the role of ER stress on the lipin-1 expression in 3T3-L1 adipocytes. We demonstrated that lipin-1 expression was suppressed by the treatment with ER stress inducers (tunicamycin and thapsigargin) at transcriptional level. We also showed that constitutive lipin-1 expression could be maintained by peroxisome proliferator-activated receptor-γ in 3T3-L1 adipocytes. Activation of peroxisome proliferator-activated receptor-γ recovered the ER stress-induced lipin-1 suppression. These results suggested that ER stress might be involved in the pathogenesis of obesity through lipin-1 depletion.

  9. ATLAS L1 Muon Trigger Upgrade with sTGC: Design and Performance

    CERN Document Server

    Gerbaudo, Davide

    2014-01-01

    We describe the upgrade of the ATLAS forward Level 1 (L1) muon trigger planned for the LHC run with luminosity above 2 10 34 cm. This upgrade, which aims at suppressing the fake muon triggers from non-pointing tracks, foresees the installation of a New Small Wheel (NSW) detector in the endcap region. This region of the detector will be instrumented with small-strip Thin Gap Chambers (sTGC) that will allow to keep the L1 muon trigger rate below 25 kHz. This rate suppression is realized with a two-step trigger system: first, an ultra-fast pad trigger defines the regions of interest containing potential high- p T muon candidates; second, an accurate track measurement is performed with precision readouts from the sTGC strips, providing the required 1 mrad angular resolution. The new, sTGC-based, L1 muon trigger is reviewed. A description of the sTGC detector as well as of its readout system is given. The first results from the simulation of this new trigger system are presented. These studies show that the pad-tr...

  10. Stevioside from Stevia rebaudiana Bertoni Increases Insulin Sensitivity in 3T3-L1 Adipocytes

    Directory of Open Access Journals (Sweden)

    Nabilatul Hani Mohd-Radzman

    2013-01-01

    Full Text Available Stevioside from Stevia rebaudiana has been reported to exert antihyperglycemic effects in both rat and human subjects. There have been few studies on these effects in vitro. In this paper, radioactive glucose uptake assay was implemented in order to assess improvements in insulin sensitivity in 3T3-L1 cells by elevation of glucose uptake following treatment with stevioside. Oil Red-O staining and MTT assay were utilized to confirm adipocyte differentiation and cell viability, respectively. Findings from this research showed a significant increase in absorbance values in mature adipocytes following Oil Red-O staining, confirming the differentiation process. Stevioside was noncytotoxic to 3T3-L1 cells as cell viability was reduced by a maximum of 17%, making it impossible to determine its IC50. Stevioside increased glucose uptake activities by 2.1 times (p<0.001 in normal conditions and up to 4.4 times (p<0.001 in insulin-resistant states. At times, this increase was higher than that seen in positive control group treated with rosiglitazone maleate, an antidiabetic agent. Expressions of pY20 and p-IRS1 which were measured via Western blot were improved by stevioside treatment. In conclusion, stevioside has direct effects on 3T3-L1 insulin sensitivity via increase in glucose uptake and enhanced expression of proteins involved in insulin-signalling pathway.

  11. The lipid fraction of human milk initiates adipocyte differentiation in 3T3-L1 cells.

    Science.gov (United States)

    Fujisawa, Yasuko; Yamaguchi, Rie; Nagata, Eiko; Satake, Eiichiro; Sano, Shinichiro; Matsushita, Rie; Kitsuta, Kazunobu; Nakashima, Shinichi; Nakanishi, Toshiki; Nakagawa, Yuichi; Ogata, Tsutomu

    2013-09-01

    The prevalence of childhood obesity has increased worldwide over the past decade. Despite evidence that human milk lowers the risk of childhood obesity, the mechanism is not fully understood. We investigated the direct effect of human milk on differentiation of 3T3-L1 preadipocytes. 3T3-L1 preadipocytes were treated with donated human milk only or the combination of the standard hormone mixture; insulin, dexamethasone (DEX), and 3-isobututyl-1-methylxanthine (IBMX). Furthermore, the induction of preadipocyte differentiation by extracted lipids from human milk was tested in comparison to the cells treated with lipid extracts from infant formula. Adipocyte differentiation, specific genes as well as formation of lipid droplets were examined. We clearly show that lipids present in human milk initiate 3T3-L1 preadipocyte differentiation. In contrast, this effect was not observed in response to lipids present in infant formula. The initiation of preadipocyte differentiation by human milk was enhanced by adding the adipogenic hormone, DEX or insulin. The expression of late adipocyte markers in Day 7 adipocytes that have been induced into differentiation with human milk lipid extracts was comparable to those in control cells initiated by a standard adipogenic hormone cocktail. These results demonstrate that human milk contains bioactive lipids that can initiate preadipocyte differentiation in the absence of the standard adipogenic compounds via a unique pathway. Copyright © 2013 Elsevier Ltd. All rights reserved.

  12. The impact of language co-activation on L1 and L2 speech fluency.

    Science.gov (United States)

    Bergmann, Christopher; Sprenger, Simone A; Schmid, Monika S

    2015-10-01

    Fluent speech depends on the availability of well-established linguistic knowledge and routines for speech planning and articulation. A lack of speech fluency in late second-language (L2) learners may point to a deficiency of these representations, due to incomplete acquisition. Experiments on bilingual language processing have shown, however, that there are strong reasons to believe that multilingual speakers experience co-activation of the languages they speak. We have studied to what degree language co-activation affects fluency in the speech of bilinguals, comparing a monolingual German control group with two bilingual groups: 1) first-language (L1) attriters, who have fully acquired German before emigrating to an L2 English environment, and 2) immersed L2 learners of German (L1: English). We have analysed the temporal fluency and the incidence of disfluency markers (pauses, repetitions and self-corrections) in spontaneous film retellings. Our findings show that learners to speak more slowly than controls and attriters. Also, on each count, the speech of at least one of the bilingual groups contains more disfluency markers than the retellings of the control group. Generally speaking, both bilingual groups-learners and attriters-are equally (dis)fluent and significantly more disfluent than the monolingual speakers. Given that the L1 attriters are unaffected by incomplete acquisition, we interpret these findings as evidence for language competition during speech production. Copyright © 2015. Published by Elsevier B.V.

  13. WEHI-3 cells inhibit adipocyte differentiation in 3T3-L1 cells

    Energy Technology Data Exchange (ETDEWEB)

    Lai, Jing [The First Affiliated Hospital, Jinan University, Guangzhou, Guangdong (China); Liu, Gexiu [Institute of Hematology, School of Medicine, Jinan University, Guangzhou, Guangdong (China); Yan, Guoyao [The First Affiliated Hospital, Jinan University, Guangzhou, Guangdong (China); He, Dongmei [Institute of Hematology, School of Medicine, Jinan University, Guangzhou, Guangdong (China); Zhou, Ying [The First Affiliated Hospital, Jinan University, Guangzhou, Guangdong (China); Chen, Shengting, E-mail: shengtingchen@sina.cn [The First Affiliated Hospital, Jinan University, Guangzhou, Guangdong (China)

    2015-06-26

    By investigating the anti-adipogenic effects of WEHI-3 cells – a murine acute myelomonocytic leukemia cell line – we sought to improve the efficiency of hematopoietic stem cell transplantation (HSCT). Analysis of Oil Red O staining and the expression of adipogenic genes, including PPARγ, C/EBPα, FAS and LPL, indicated that WEHI-3 cells significantly inhibited 3T3-L1 mouse preadipocyte cells from differentiating into adipocytes. In vivo, fat vacuoles in mice injected with WEHI-3 cells were also remarkably reduced in the murine bone marrow pimelosis model. Moreover, the key gene in the Rho signaling pathway, ROCKII, and the key gene in the Wnt signaling pathway, β-catenin, were both upregulated compared with the control group. siRNA-mediated knockdown of ROCKII and β-catenin reversed these WEHI-3-mediated anti-adipogenic effects. Taken together, these data suggest that WEHI-3 cells exert anti-adipogenic effects and that both ROCKII and β-catenin are involved in this process. - Highlights: • WEHI-3, an acute myelomonocytic leukemia cell line, inhibited 3T3-L1 preadipocyte from differentiating into adipocyte. • WEHI-3 cells can arrest 3T3-L1 cells in G0/G1 phase by secreting soluble factors and thus inhibit their proliferation. • WEHI-3 cells reduced bone marrow pimelosis in the murine model. • Both ROCKII and β-catenin were involved in the WEHI-3-mediated anti-adipogenic effects.

  14. English Orthographic Learning in Chinese-L1 Young EFL Beginners.

    Science.gov (United States)

    Cheng, Yu-Lin

    2017-12-01

    English orthographic learning, among Chinese-L1 children who were beginning to learn English as a foreign language, was documented when: (1) only visual memory was at their disposal, (2) visual memory and either some letter-sound knowledge or some semantic information was available, and (3) visual memory, some letter-sound knowledge and some semantic information were all available. When only visual memory was available, orthographic learning (measured via an orthographic choice test) was meagre. Orthographic learning was significant when either semantic information or letter-sound knowledge supplemented visual memory, with letter-sound knowledge generating greater significance. Although the results suggest that letter-sound knowledge plays a more important role than semantic information, letter-sound knowledge alone does not suffice to achieve perfect orthographic learning, as orthographic learning was greatest when letter-sound knowledge and semantic information were both available. The present findings are congruent with a view that the orthography of a foreign language drives its orthographic learning more than L1 orthographic learning experience, thus extending Share's (Cognition 55:151-218, 1995) self-teaching hypothesis to include non-alphabetic L1 children's orthographic learning of an alphabetic foreign language. The little letter-sound knowledge development observed in the experiment-I control group indicates that very little letter-sound knowledge develops in the absence of dedicated letter-sound training. Given the important role of letter-sound knowledge in English orthographic learning, dedicated letter-sound instruction is highly recommended.

  15. Caenorhabditis elegans battling starvation stress: low levels of ethanol prolong lifespan in L1 larvae.

    Directory of Open Access Journals (Sweden)

    Paola V Castro

    Full Text Available The nematode Caenorhabditis elegans arrests development at the first larval stage if food is not present upon hatching. Larvae in this stage provide an excellent model for studying stress responses during development. We found that supplementing starved larvae with ethanol markedly extends their lifespan within this L1 diapause. The effects of ethanol-induced lifespan extension can be observed when the ethanol is added to the medium at any time between 0 and 10 days after hatching. The lowest ethanol concentration that extended lifespan was 1 mM (0.005%; higher concentrations to 68 mM (0.4% did not result in increased survival. In spite of their extended survival, larvae did not progress to the L2 stage. Supplementing starved cultures with n-propanol and n-butanol also extended lifespan, but methanol and isopropanol had no measurable effect. Mass spectrometry analysis of nematode fatty acids and amino acids revealed that L1 larvae can incorporate atoms from ethanol into both types of molecules. Based on these data, we suggest that ethanol supplementation may extend the lifespan of L1 larvae by either serving as a carbon and energy source and/or by inducing a stress response.

  16. L1 Transfer in Post-Verbal Preposition: An Inter-level Comparison

    Directory of Open Access Journals (Sweden)

    Samira Mollaei

    2013-10-01

    Full Text Available The study intended to investigate the well-known issue of L1 transfer in L2acquisition. The primary aim of this research was to compare the extent to which L1 transfer may take place in different developmental stages in L2 learning procedure. Persian learners of English have been observed to misuse a number of the prepositions with some of the verbs. Having scrutinized more than a hundred pieces of students’ writing assignments, the authors came up with a pattern of errors in this area. It was observed that the majority of these errors could be attributed to Persian: the learners’ choice of preposition mirror the corresponding case in their L1, Persian. Moreover, the pattern of mistakes was put to test to check whether these mistakes increase or decrease according to the level of proficiency of the learners. To this end, two groups of students, one in elementary and the other in intermediate level, were tested on their use of proper prepositions with different verbs and the results of these tests were compared to see whether any significant difference exists between the two groups of students. The results showed no significant difference between the students of the two proficiency levels.

  17. A blind deconvolution method based on L1/L2 regularization prior in the gradient space

    Science.gov (United States)

    Cai, Ying; Shi, Yu; Hua, Xia

    2018-02-01

    In the process of image restoration, the result of image restoration is very different from the real image because of the existence of noise, in order to solve the ill posed problem in image restoration, a blind deconvolution method based on L1/L2 regularization prior to gradient domain is proposed. The method presented in this paper first adds a function to the prior knowledge, which is the ratio of the L1 norm to the L2 norm, and takes the function as the penalty term in the high frequency domain of the image. Then, the function is iteratively updated, and the iterative shrinkage threshold algorithm is applied to solve the high frequency image. In this paper, it is considered that the information in the gradient domain is better for the estimation of blur kernel, so the blur kernel is estimated in the gradient domain. This problem can be quickly implemented in the frequency domain by fast Fast Fourier Transform. In addition, in order to improve the effectiveness of the algorithm, we have added a multi-scale iterative optimization method. This paper proposes the blind deconvolution method based on L1/L2 regularization priors in the gradient space can obtain the unique and stable solution in the process of image restoration, which not only keeps the edges and details of the image, but also ensures the accuracy of the results.

  18. Endoplasmic reticulum stress suppresses lipin-1 expression in 3T3-L1 adipocytes

    International Nuclear Information System (INIS)

    Takahashi, Nobuhiko; Yoshizaki, Takayuki; Hiranaka, Natsumi; Suzuki, Takeshi; Yui, Tomoo; Akanuma, Masayoshi; Kanazawa, Kaoru; Yoshida, Mika; Naito, Sumiyoshi; Fujiya, Mikihiro; Kohgo, Yutaka; Ieko, Masahiro

    2013-01-01

    Highlights: ► Lipin-1 involves lipid metabolism, adipocyte differentiation, and inflammation. ► Adipose lipin-1 expression is reduced in obesity. ► ER stress suppresses lipin-1 expression in 3T3-L1 adipocytes. ► Activation of PPAR-γ recovers ER stress-induced lipin-1 reduction. -- Abstract: Lipin-1 plays crucial roles in the regulation of lipid metabolism and cell differentiation in adipocytes. In obesity, adipose lipin-1 mRNA expression is decreased and positively correlated with systemic insulin sensitivity. Amelioration of the lipin-1 depletion might be improved dysmetabolism. Although some cytokines such as TNF-α and interleukin-1β reduces adipose lipin-1 expression, the mechanism of decreased adipose lipin-1 expression in obesity remains unclear. Recently, endoplasmic reticulum (ER) stress is implicated in the pathogenesis of obesity. Here we investigated the role of ER stress on the lipin-1 expression in 3T3-L1 adipocytes. We demonstrated that lipin-1 expression was suppressed by the treatment with ER stress inducers (tunicamycin and thapsigargin) at transcriptional level. We also showed that constitutive lipin-1 expression could be maintained by peroxisome proliferator-activated receptor-γ in 3T3-L1 adipocytes. Activation of peroxisome proliferator-activated receptor-γ recovered the ER stress-induced lipin-1 suppression. These results suggested that ER stress might be involved in the pathogenesis of obesity through lipin-1 depletion

  19. Neural overlap of L1 and L2 semantic representations in speech: A decoding approach.

    Science.gov (United States)

    Van de Putte, Eowyn; De Baene, Wouter; Brass, Marcel; Duyck, Wouter

    2017-11-15

    Although research has now converged towards a consensus that both languages of a bilingual are represented in at least partly shared systems for language comprehension, it remains unclear whether both languages are represented in the same neural populations for production. We investigated the neural overlap between L1 and L2 semantic representations of translation equivalents using a production task in which the participants had to name pictures in L1 and L2. Using a decoding approach, we tested whether brain activity during the production of individual nouns in one language allowed predicting the production of the same concepts in the other language. Because both languages only share the underlying semantic representation (sensory and lexical overlap was maximally avoided), this would offer very strong evidence for neural overlap in semantic representations of bilinguals. Based on the brain activation for the individual concepts in one language in the bilateral occipito-temporal cortex and the inferior and the middle temporal gyrus, we could accurately predict the equivalent individual concepts in the other language. This indicates that these regions share semantic representations across L1 and L2 word production. Copyright © 2017 Elsevier Inc. All rights reserved.

  20. Enhancing Foreign Language Learning through Listening Strategies Delivered in L1: An Experimental Study

    Directory of Open Access Journals (Sweden)

    Hitendra Pillay

    2013-01-01

    Full Text Available Listening used in language teaching refers to a complex process that allows us to understand spoken language. The current study, conducted in Iran with an experimental design, investigated the effectiveness of teaching listening strategies delivered in L1 (Persian and its effect on listening comprehension in L2. Five listening strat