  1. Tailoring the wettability of nanocrystalline TiO 2 films

    Science.gov (United States)

    Liang, Qiyu; Chen, Yan; Fan, Yuzun; Hu, Yong; Wu, Yuedong; Zhao, Ziqiang; Meng, Qingbo

    2012-01-01

    The water contact angle (WCA) of nanocrystalline TiO2 films was adjusted by fluoroalkylsilane (FAS) modification and photocatalytic lithography. FAS modification made the surface hydrophobic with the WCA up to ∼156°, while ultraviolet (UV) irradiation changed surface to hydrophilic with the WCA down to ∼0°. Both the hydrophobicity and hydrophilicity were enhanced by surface roughness. The wettability can be tailored by varying the concentration of FAS solution and soaking time, as well as the UV light intensity and irradiation time. Additionally, with the help of photomasks, hydrophobic-hydrophilic micropatterns can be fabricated and manifested via area-selective deposition of polystyrene particles.

  2. Preparation and characterization of nanocrystalline porous TiO2/WO3 composite thin films

    International Nuclear Information System (INIS)

    Hsu, C.-S.; Lin, C.-K.; Chan, C.-C.; Chang, C.-C.; Tsay, C.-Y.

    2006-01-01

    TiO 2 materials possessing not only photocatalytic but also electrochromic properties have attracted many research and development interests. Though WO 3 exhibits excellent electrochromic properties, the much higher cost and water-sensitivity of WO 3 as compared with the TiO 2 may restrict the practical application of WO 3 materials. In the present study, the feasibility of preparing nanocrystalline porous TiO 2 /WO 3 composite thin films was investigated. Precursors of sols TiO 2 and/or WO 3 and polystyrene microspheres were used to prepare nanocrystalline pure TiO 2 , WO 3 , and composite TiO 2 /WO 3 thin films by spin coating. The spin-coated thin films were amorphous and, after heat treating at a temperature of 500 o C, nanocrystalline TiO 2 , TiO 2 /WO 3 , and WO 3 thin films with or without pores were prepared successfully. The heat-treated thin films were colorless and coloration-bleaching phenomena can be observed during cyclic voltammetry tests. The heat-treated thin films exhibited good reversible electrochromic behavior while the porous TiO 2 /WO 3 composite film exhibited improved electrochromic properties

  3. Mesoscopic CH 3 NH 3 PbI 3 /TiO 2 Heterojunction Solar Cells

    KAUST Repository

    Etgar, Lioz

    2012-10-24

    We report for the first time on a hole conductor-free mesoscopic methylammonium lead iodide (CH 3NH 3PbI 3) perovskite/TiO 2 heterojunction solar cell, produced by deposition of perovskite nanoparticles from a solution of CH 3NH 3I and PbI 2 in γ-butyrolactone on a 400 nm thick film of TiO 2 (anatase) nanosheets exposing (001) facets. A gold film was evaporated on top of the CH 3NH 3PbI 3 as a back contact. Importantly, the CH 3NH 3PbI 3 nanoparticles assume here simultaneously the roles of both light harvester and hole conductor, rendering superfluous the use of an additional hole transporting material. The simple mesoscopic CH 3NH 3PbI 3/TiO 2 heterojunction solar cell shows impressive photovoltaic performance, with short-circuit photocurrent J sc= 16.1 mA/cm 2, open-circuit photovoltage V oc = 0.631 V, and a fill factor FF = 0.57, corresponding to a light to electric power conversion efficiency (PCE) of 5.5% under standard AM 1.5 solar light of 1000 W/m 2 intensity. At a lower light intensity of 100W/m 2, a PCE of 7.3% was measured. The advent of such simple solution-processed mesoscopic heterojunction solar cells paves the way to realize low-cost, high-efficiency solar cells. © 2012 American Chemical Society.

  4. Photocatalytic properties of nanocrystalline TiO2 thin film with Ag additions

    International Nuclear Information System (INIS)

    Chang, C.-C.; Lin, C.-K.; Chan, C.-C.; Hsu, C.-S.; Chen, C.-Y.

    2006-01-01

    In the present study, nanocrystalline TiO 2 /Ag composite thin films were prepared by a sol-gel spin coating technique. While, by introducing polystyrene (PS) microspheres, porous TiO 2 /Ag films were obtained after calcining at a temperature of 500 o C. The as-prepared TiO 2 and TiO 2 /Ag thin films were characterized by X-ray diffractometry, and scanning electron microscopy to reveal the structural and morphological differences. In addition, the photocatalytic properties of these films were investigated by degrading methylene blue under UV irradiation. After 500 o C calcination, the microstructure of PS-TiO 2 film without Ag addition exhibited a sponge-like microstructure while significant sintering effect was noticed with Ag additions and the films exhibited a porous microstructure. Meanwhile, coalescence of nanocrystalline anatase-phase TiO 2 can be observed with respect to the sharpening of XRD diffraction peaks. The photodegradation of porous TiO 2 doped with 1 mol% Ag exhibited the best photocatalytic efficiency where 72% methylene blue can be decomposed after UV exposure for 12 h

  5. A chemical route to room-temperature synthesis of nanocrystalline TiO2 thin films

    International Nuclear Information System (INIS)

    Pathan, Habib M.; Kim, Woo Young; Jung, Kwang-Deog; Joo, Oh-Shim

    2005-01-01

    A lot of methods are developed for the deposition of TiO 2 thin films; however, in each of these methods as-deposited films are amorphous and need further heat treatment at high temperature. In the present article, a chemical bath deposition (CBD) method was used for the preparation of TiO 2 thin films. We investigated nanocrystalline TiO 2 thin films using CBD at room temperature onto glass and ITO coated glass substrate. The films were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and high-resolution transmission electron microscopy (HRTEM) techniques. The chemically synthesized films were nanocrystalline and composed of crystal grains of 2-3 nm

  6. Theoretical Verification of Photoelectrochemical Water Oxidation Using Nanocrystalline TiO2 Electrodes

    Directory of Open Access Journals (Sweden)

    Shozo Yanagida

    2015-05-01

    Full Text Available Mesoscopic anatase nanocrystalline TiO2 (nc-TiO2 electrodes play effective and efficient catalytic roles in photoelectrochemical (PEC H2O oxidation under short circuit energy gap excitation conditions. Interfacial molecular orbital structures of (H2O3 &OH(TiO29H as a stationary model under neutral conditions and the radical-cation model of [(H2O3&OH(TiO29H]+ as a working nc-TiO2 model are simulated employing a cluster model OH(TiO29H (Yamashita/Jono’s model and a H2O cluster model of (H2O3 to examine excellent H2O oxidation on nc-TiO2 electrodes in PEC cells. The stationary model, (H2O3&OH(TiO29H reveals that the model surface provides catalytic H2O binding sites through hydrogen bonding, van der Waals and Coulombic interactions. The working model, [(H2O3&OH(TiO29H]+ discloses to have a very narrow energy gap (0.3 eV between HOMO and LUMO potentials, proving that PEC nc-TiO2 electrodes become conductive at photo-irradiated working conditions. DFT-simulation of stepwise oxidation of a hydroxide ion cluster model of OH−(H2O3, proves that successive two-electron oxidation leads to hydroxyl radical clusters, which should give hydrogen peroxide as a precursor of oxygen molecules. Under working bias conditions of PEC cells, nc-TiO2 electrodes are now verified to become conductive by energy gap photo-excitation and the electrode surface provides powerful oxidizing sites for successive H2O oxidation to oxygen via hydrogen peroxide.

  7. Yttrium-substituted nanocrystalline TiO 2 photoanodes for perovskite based heterojunction solar cells

    KAUST Repository

    Qin, Peng; Domanski, Anna L.; Chandiran, Aravind Kumar; Berger, Rü diger; Butt, Hans-Jü rgen; Dar, M. Ibrahim; Moehl, Thomas; Tetreault, Nicolas; Gao, Peng; Ahmad, Shahzada; Nazeeruddin, Mohammad K.; Grä tzel, Michael

    2014-01-01

    We report the use of Y3+-substituted TiO2 (0.5%Y-TiO2) in solid-state mesoscopic solar cells, consisting of CH3NH3PbI3 as the light harvester and spiro-OMeTAD as the hole transport material. A power conversion efficiency of 11.2% under simulated AM 1.5 full sun illumination was measured. A 15% improvement in the short-circuit current density was obtained compared with pure TiO2, due to the effect of Y3+ on the dimensions of perovskite nanoparticles formed on the semiconductor surface, showing that the surface modification of the semiconductor is an effective way to improve the light harvesters' morphology and electron transfer properties in the solid-state mesoscopic solar cells. © 2013 The Royal Society of Chemistry.

  8. Yttrium-substituted nanocrystalline TiO 2 photoanodes for perovskite based heterojunction solar cells

    KAUST Repository

    Qin, Peng

    2014-01-01

    We report the use of Y3+-substituted TiO2 (0.5%Y-TiO2) in solid-state mesoscopic solar cells, consisting of CH3NH3PbI3 as the light harvester and spiro-OMeTAD as the hole transport material. A power conversion efficiency of 11.2% under simulated AM 1.5 full sun illumination was measured. A 15% improvement in the short-circuit current density was obtained compared with pure TiO2, due to the effect of Y3+ on the dimensions of perovskite nanoparticles formed on the semiconductor surface, showing that the surface modification of the semiconductor is an effective way to improve the light harvesters\\' morphology and electron transfer properties in the solid-state mesoscopic solar cells. © 2013 The Royal Society of Chemistry.

  9. Mechanochemical preparation of nanocrystalline TiO2 powders and their behavior at high temperatures

    International Nuclear Information System (INIS)

    Gajovic, A.; Furic, K.; Tomasic, N.; Popovic, S.; Skoko, Z.; Music, S.

    2005-01-01

    Nanocrystalline TiO 2 powders were prepared by high-energy ball-milling using zirconia vial and balls. The changes of microstructure caused by material processing were studied using Raman spectroscopy, X-ray powder diffraction (XRD), transmission electron microscopy (TEM) and selected area electron diffraction (SAED). The milling of the starting TiO 2 powder (anatase + rutile in traces) induced phase transitions to high-pressure polymorph, TiO 2 II, and rutile. We found that the phase transition to TiO 2 II was initiated at the surface of the small particles, while transition to rutile started in their center. Changes in crystallite size during milling process were obtained by the Scherrer method, while the particle size changes were monitored by TEM. The kinetics of phase changes, a decrease in crystallite/particle size, as well as zirconia contamination depended on the powder-to-ball weight ratio. The starting powder and some selected ball-milled samples were investigated in situ by Raman spectroscopy and XRD at high temperatures (up to 1300 deg. C) to examine their behavior during the sintering process. A difference in the results obtained by these two techniques was explained in frame of basic physical properties characterizing both methods. The morphology of the final sinters was monitored by scanning electron microscopy (SEM)

  10. Aggregate formation of eosin-Y adsorbed on nanocrystalline TiO2 films

    Science.gov (United States)

    Yaguchi, Kaori; Furube, Akihiro; Katoh, Ryuzi

    2012-11-01

    We have studied the adsorption of eosin-Y on nanocrystalline TiO2 films with two different solvents namely acetonitrile (ACN) and ethanol (EtOH). A Langmuir-type adsorption isotherm was observed with ACN. In contrast, a Freundlich-type adsorption isotherm was observed with EtOH, suggesting that EtOH molecules co-adsorbed on TiO2 surface. Absorption spectra of the dye adsorbed films clearly show aggregate formation at high concentrations of dye in the solutions. From the analysis of the spectra, we conclude that head-to-tail type aggregates are observed with ACN, whereas various types of aggregates, including H-type and head-to-tail type aggregates, are observed with EtOH.

  11. Comparative analysis of Dye-Sensitized Solar Cells (DSSC) having different nanocrystalline TiO2 layer structures

    International Nuclear Information System (INIS)

    Forcade, Fresnel; Gonzalez, Bernardo; Vigil, Elena; Jennings, James R.; Duna, Halina; Wang, Hongxia; Peter, Laurence M.

    2009-01-01

    Full text: Dye-sensitized solar cells (DSSC) are very prospective because of their low cost and comparatively not so low efficiency. This represents an advantage together with the innocuous character of the constituent materials. We study different types of DSSC. The procedure for making them has been the same except for the TiO 2 layer structure. This layer must be porous and nanocrystalline in order to increase light absorption by the sensitizer. On the other hand, this condition causes that the electrolyte contacts the transparent conducting oxide (TCO) underneath the TiO 2 originating undesired recombinations. Also the electrical contact of the Tio to the TCO depends on the technology used to deposit the TiO 2 . In order to avoid possible leakage currents caused by recombinations from the TCO to the electrolyte and improve TiO 2 -TCO electrical contact, a thin TiO 2 film is placed in between the porous TiO 2 layer and the TCO. Different structures are obtained using different technologies to obtain the thin TiO 2 film. These structures are analyzed from their volt-amperic characteristic, external quantum efficiency spectra and voltage decay observed when light is suppressed. Results obtained allow making recommendations regarding nanocrystalline TiO 2 structure to be used in DSSC. (author)

  12. Room temperature growth of nanocrystalline anatase TiO2 thin films by dc magnetron sputtering

    International Nuclear Information System (INIS)

    Singh, Preetam; Kaur, Davinder

    2010-01-01

    We report, the structural and optical properties of nanocrystalline anatase TiO 2 thin films grown on glass substrate by dc magnetron sputtering at room temperature. The influence of sputtering power and pressure over crystallinity and surface morphology of the films were investigated. It was observed that increase in sputtering power activates the TiO 2 film growth from relative lower surface free energy to higher surface free energy. XRD pattern revealed the change in preferred orientation from (1 0 1) to (0 0 4) with increase in sputtering power, which is accounted for different surface energy associated with different planes. Microstructure of the films also changes from cauliflower type to columnar type structures with increase in sputtering power. FESEM images of films grown at low pressure and low sputtering power showed typical cauliflower like structure. The optical measurement revealed the systematic variation of the optical constants with deposition parameters. The films are highly transparent with transmission higher than 90% with sharp ultraviolet cut off. The transmittance of these films was found to be influenced by the surface roughness and film thickness. The optical band gap was found to decrease with increase in the sputtering power and pressure. The refractive index of the films was found to vary in the range of 2.50-2.24 with increase in sputtering pressure or sputtering power, resulting in the possibility of producing TiO 2 films for device applications with different refractive index, by changing the deposition parameters.

  13. THERMALLY STABLE NANOCRYSTALLINE TIO2 PHOTOCATALYSTS SYNTHESIZED VIA SOL-GEL METHODS MODIFIED WITH IONIC LIQUID AND SURFACTANT MOLECULES

    Science.gov (United States)

    Recently, sol-gel methods employing ionic liquids (ILs) have shown significant implications for the synthesis of well-defined nanostructured inorganic materials. Herein, we synthesized nanocrystalline TiO2 particles via an alkoxide sol-gel method employing a water-immi...

  14. Sealed two-electrode photoelectrochemical cell based on nanocrystalline TiO2 analyzed as a UV sensor

    International Nuclear Information System (INIS)

    Forcade, Fresnel; Gonzalez, Bernardo; Maqueda, Ma. de la Luz; Curbelo, Larisa; Vigil, Elena; Jennings, James R.; Dunn, Halina; Wang, Hongxia; PeteR, Lauri M.

    2008-01-01

    Potentialities as UV sensor of a sealed two-electrode photoelectrochemical cell (PEC) based on nanocrystalline TiO 2 are analyzed. Ultraviolet component of solar light is responsible for a number of skin disorders and diseases. An inexpensive and simple UV sensor would be convenient to measure the UV intensity been exposed to. Nanocrystalline TiO 2 is a rather inexpensive material, innocuous and very stable which is intensively studied at the present moment because of its possible applications in dye-sensitized solar cells, photocatalysis, electrochromics, etc. The method for obtaining the sensor and its structure are described. Different TiO 2 layer structures for the photoelectrode are studied. Important parameters, such as, spectral response, external quantum efficiency, current vs light intensity and current-voltage curve are presented. Results show prospective for the implementation of this type of sensor. (Full text)

  15. Integration of High-Performance Nanocrystalline TiO2 Photoelectrodes for N719-Sensitized Solar Cells

    Directory of Open Access Journals (Sweden)

    Ke-Jian Jiang

    2013-01-01

    Full Text Available We report on enhanced performance of N719-sensitized TiO2 solar cells (DSCs incorporating size and photoelectron diffusion-controlled TiO2 as sensitizer-matched light-scatter layers on conventional nanocrystalline TiO2 electrodes. The double-layered N719/TiO2 composite electrode with a high dye-loading capacity exhibits the diffused reflectance of more than 50% in the range of λ = 650–800 nm, even when the films are coupled with the titania nanocrystalline underlayer in the device. As a result, the increased near-infrared light-harvesting produces a high light-to-electricity conversion efficiency of over 9% mainly due to the significant increase of Jsc. Such an optical effect of the NIR-light scattering TiO2 electrodes will be beneficial when the sensitizers with low molar extinction coefficients, such as N719, are introduced in the device.

  16. Synthesis of Nanocrystalline SnO2 Modified TiO2:a Material for Carbon Monoxide Gas Sensor

    Directory of Open Access Journals (Sweden)

    A. B. BODADE

    2008-11-01

    Full Text Available Nanocrystalline SnO2 doped TiO2 having average crystallite size of 45-50 nm were synthesized by the sol-gel method and studied for gas sensing behavior to reducing gases like CO, liquefied petroleum gas (LPG, NH3 and H2. The material characterization was done by using X-ray diffraction (XRD, Fourier transform infrared spectroscopy (FT-IR and scanning electron microscope (SEM. The sensitivity measurements were carried out as a function of different operating temperature in SnO2 doped TiO2. The 15 wt.% SnO2 doped TiO2 based CO sensor shows better sensitivity at an operating temperature 240°C Incorporation of 0.5 wt% Pd improved the sensitivity, selectivity, response time and reduced the operating temperature from 240°C to 200°C for CO sensor.

  17. Hysteretic current-voltage characteristics in RF-sputtered nanocrystalline TiO2 thin films

    International Nuclear Information System (INIS)

    Villafuerte, Manuel; Juarez, Gabriel; Heluani, Silvia P. de; Comedi, David

    2007-01-01

    We have measured the current-voltage characteristics at room temperature of a nanocrystalline TiO 2 thin film fabricated by reactive RF-sputtering deposition and sandwiched between ITO (indium-tin-oxide)-buffered glass substrate and an indium top electrode. The I-V characteristics are ohmic for low voltages and become non-linear, hysteretic and asymmetric as the voltage is increased. The system is shown to be well represented by two distinct resistance states in the non-ohmic region. Current transient evolutions were also measured for constant voltage excitations. The resistance is stable in time for voltages in the ohmic regime. In contrast, for voltages in the non-ohmic regime, the resistance has a small variation for a short period of time (order of tens seconds) and then increases with time. For those transients, long characteristic times (on the order of tens of minutes up to hours) were found. The behavior of the system is discussed on the basis of experimental results reported in the literature for similar systems and existing models for electric-field induced resistive switching

  18. The Function of TiO2 with Respect to Sensitizer Stability in Nanocrystalline Dye Solar Cells

    Directory of Open Access Journals (Sweden)

    A. Barkschat

    2008-01-01

    Full Text Available Dyes of characteristically different composition have been tested with respect to long-term stability in operating standardized dye sensitized cells during a time period of up to 3600 hours. Selective solar illumination, the use of graded filters, and imaging of photocurrents revealed that degradation is linked to the density of photocurrent passed. Photoelectrochemical degradation was observed with all sensitizers investigated. Sensitization was less efficient and sensitizers were less photostable with nanostructured ZnO compared to nanostructured TiO2. The best performance was confirmed for cis-RuII(dcbpyH22(NCS2 on TiO2. However, it was 7–10 times less stable under other identical conditions on ZnO. Stability is favored by carboxylate anchoring and metal-centred electron transfer. In presence of TiO2, it is enhanced by formation of a stabilizing charge-transfer complex between oxidized Ru dye and back-bonding interfacial Ti3+ states. This is considered to be the main reason for the ongoing use of expensive Ru complexes in combination with TiO2. The local surface chemistry of the nanocrystalline TiO2 turned out to be a crucial factor for sensitizer stability and requires further investigation.

  19. Comparison Study on the Microstructure of Nanocrystalline TiO2 in Different Ti-Si Binary Oxides

    Institute of Scientific and Technical Information of China (English)

    2007-01-01

    Three different Ti-Si oxide structuares, silica supported titania, silica coated titania and intimately mixed silicatitania, containing 10%-40% SiO2, were made by sol-gel process. The variations of microstructure parameters of nanocrystalline (nc) TiO2-anatase in the three kirds of binary oxides, including in-plane spacing d, cell constants (a0, CQ), cell volume V, cell axial ratio c0/a0 and crystal grain size, were comparatively investigated by high resolution transmission electron microscopy (HRTEM) and X-ray diffraction (XRD). It is found that the microstructure parameters vary remarkably with increasing SiO2 content and annealing temperature. Different structured Ti-Si binary oxides lead to different variation tendencies of microstructure parameters. The more SiO2 the binary oxide contains, the more lattice defects of nc TiO2-anatase appear; diffusion or migration of Si cations could be an important influential factor in the variations of microstructure. The grain size of nc TiO2 in the three kinds of binary oxides not only depends on SiO2 content and annealing temperature but also on the degree of lattice microstrain and distortion of nc TiO2-anatase. Both grain size and phase transformation of nc TiO2-anatase are effectively inhibited with increasing SiOa content.

  20. Electrophoretic deposition of nanocrystalline TiO2 films on Ti substrates for use in flexible dye-sensitized solar cells

    International Nuclear Information System (INIS)

    Tan Weiwei; Yin Xiong; Zhou Xiaowen; Zhang Jingbo; Xiao Xurui; Lin Yuan

    2009-01-01

    Nanocrystalline TiO 2 films were prepared on flexible Ti-metal sheets by electrophoretic deposition followed by chemical treatment with tetra-n-butyl titanate (TBT) and sintering at 450 deg. C. X-ray diffraction (XRD) analysis indicates that TBT treatment led to the formation of additional anatase TiO 2 , which plays an important role in improving the interconnection between TiO 2 particles, as well as the adherence of the film to the substrate, and in modifying the surface properties of the nanocrystalline particles. The effect of TBT treatment on the electron transport in the nanocrystalline films was studied by intensity-modulated photocurrent spectroscopy (IMPS). An increase in the conversion efficiency was obtained for the dye-sensitized solar cells with TBT-treated nanocrystalline TiO 2 films. The cell performance was further optimized by designing nanocrystalline TiO 2 films with a double-layer structure composed of a light-scattering layer and a transparent layer. The light-scattering effect of the double-layer nanocrystalline films was evaluated by diffuse reflectance spectra. Employing the double-layer nanocrystalline films as the photoelectrodes resulted in a significant improvement in the incident photo-to-current conversion efficiency of the corresponding cells due to enhanced solar absorption by light scattering. A high conversion efficiency of 6.33% was measured under illumination with 100 mW cm -2 (AM 1.5) simulated sunlight.

  1. Synthesis of nanocrystalline TiO2 thin films by liquid phase ...

    Indian Academy of Sciences (India)

    WINTEC

    goes degradation efficiently in presence of TiO2 thin films by exposing its aqueous solution to .... Figure 6. Photodegradation of IGOR organic dye by a. bare TiO2 thin film and b. ... Meng L-J and Dos Santos M P 1993 Thin Solid Films 226 22.

  2. Photocatalytic behaviors and structural characterization of nanocrystalline Fe-doped TiO2 synthesized by mechanical alloying

    International Nuclear Information System (INIS)

    Kim, Dong Hyun; Hong, Hyun Seon; Kim, Sun Jae; Song, Jae Sung; Lee, Kyung Sub

    2004-01-01

    Nanocrystalline Fe-doped TiO 2 powders were synthesized by mechanical alloying (MA) with varying Fe contents from 0 up to 4.8 wt.% to shift the absorption threshold into the visible light region. The photocatalytic feasibility of the Fe-doped TiO 2 powder was evaluated by quantifying the visible light absorption capacity using ultraviolet and visible (UV-Vis) spectroscopy and photoluminescence spectroscopy. Effects of Fe additions on the crystal structures and the morphologies of the Fe-doped powders were also investigated as a function of the doping content using transmission electron microscopy-electron diffraction pattern (TEM-EDP), X-ray diffraction (XRD) and energy dispersive X-ray (EDAX) and X-ray photoelectron spectroscopy (XPS). The UV-Vis study showed that the UV absorption for the Fe-doped powder moved to a longer wavelength (red shift) and the photoefficiency was enhanced. Based on the analysis of the photoluminescence spectra, the red shift was believed to be induced by localizing the dopant level near the valence band of TiO 2 . The UV-Vis absorption depended on the Fe concentration. TEM-EDP and XRD investigations showed that the Fe-doped powder had a rutile phase in which the added Fe atoms were dissolved. The rutile phase was composed of spherical particles and chestnut bur shaped particles, resulting in a larger surface area than the spherical P-25 powder

  3. Surface properties of nanocrystalline TiO2 coatings in relation to the in vitro plasma protein adsorption

    International Nuclear Information System (INIS)

    Lorenzetti, M; Kobe, S; Novak, S; Bernardini, G; Santucci, A; Luxbacher, T

    2015-01-01

    This study reports on the selective adsorption of whole plasma proteins on hydrothermally (HT) grown TiO 2 -anatase coatings and its dependence on the three main surface properties: surface charge, wettability and roughness. The influence of the photo-activation of TiO 2 by UV irradiation was also evaluated. Even though the protein adhesion onto Ti-based substrates was only moderate, better adsorption of any protein (at pH = 7.4) occurred for the most negatively charged and hydrophobic substrate (Ti non-treated) and for the most nanorough and hydrophilic surface (HT Ti3), indicating that the mutual action of the surface characteristics is responsible for the attraction and adhesion of the proteins. The HT coatings showed a higher adsorption of certain proteins (albumin ‘passivation’ layer, apolipoproteins, vitamin D-binding protein, ceruloplasmin, α-2-HS-glycoprotein) and higher ratios of albumin to fibrinogen and albumin to immunoglobulin γ-chains. The UV pre-irradiation affected the surface properties and strongly reduced the adsorption of the proteins. These results provide in-depth knowledge about the characterization of nanocrystalline TiO 2 coatings for body implants and provide a basis for future studies on the hemocompatibility and biocompatibility of such surfaces. (paper)

  4. Influence of nanocrystalline structure and surface properties of TiO2 thin films on the viability of L929 cells

    Directory of Open Access Journals (Sweden)

    Osękowska Małgorzata

    2015-09-01

    Full Text Available In this work the physicochemical and biological properties of nanocrystalline TiO2 thin films were investigated. Thin films were prepared by magnetron sputtering method. Their properties were examined by X-ray diffraction, photoelectron spectroscopy, atomic force microscopy, optical transmission method and optical profiler. Moreover, surface wettability and scratch resistance were determined. It was found that as-deposited coatings were nanocrystalline and had TiO2-anatase structure, built from crystallites in size of 24 nm. The surface of the films was homogenous, composed of closely packed grains and hydrophilic. Due to nanocrystalline structure thin films exhibited good scratch resistance. The results were correlated to the biological activity (in vitro of thin films. Morphological changes of mouse fibroblasts (L929 cell line after contact with the surface of TiO2 films were evaluated with the use of a contrast-phase microscope, while their viability was tested by MTT colorimetric assay. The viability of cell line upon contact with the surface of nanocrystalline TiO2 film was comparable to the control sample. L929 cells had homogenous cytoplasm and were forming a confluent monofilm, while lysis and inhibition of cell growth was not observed. Moreover, the viability in contact with surface of examined films was high. This confirms non-cytotoxic effect of TiO2 film surface on mouse fibroblasts.

  5. Structure of electron collection electrode in dye-sensitized nanocrystalline TiO2

    International Nuclear Information System (INIS)

    Yanagida, Masatoshi; Numata, Youhei; Yoshimatsu, Keiichi; Ochiai, Masayuki; Naito, Hiroyoshi; Han, Liyuan

    2013-01-01

    As part of the effort to control electron transport in the TiO 2 films of dye-sensitized solar cells (DSCs), the structure of the electron collection electrode on the films has been investigated. Here, we report the comparison between a sandwich-type dye-sensitized solar cell (SW-DSC), in which the TiO 2 film is sandwiched between a TCO glass front electron collection electrode and a sputtered Ti back charge collection electrode, and a normal DSC (N-DSC), which has no back electrode. In N-DSCs, electrons in TiO 2 that are far from the front electrode have to diffuse for a long distance (ca. 10 μm), and therefore, the photocurrent cannot rapidly respond to light with a modulation frequency >100 Hz. In SW-DSCs, the photocurrent response was enhanced at frequencies between 10 and 500 Hz because electrons in TiO 2 can be extracted by both front and back electrodes, which can be also explained by an electron diffusion model. Calculations based on the electron diffusion model suggested that a high short-circuit photocurrent could be maintained in SW-DSCs even when the electron diffusion length in the TiO 2 film was shortened.

  6. Nanocrystalline Pt-doped TiO2 thin films prepared by spray pyrolysis ...

    Indian Academy of Sciences (India)

    Administrator

    Spray pyrolysis techniques; TiO2 thin films; hydrogen gas response. 1. Introduction ... tion is necessary during the production, storage and use of hydrogen. It is also ..... ient, and 'green': it may be used to large scale industrial application for ...

  7. Nanocrystalline TiO2 by three different synthetic approaches: A ...

    Indian Academy of Sciences (India)

    TECS

    TiO2 produced by the above three methods are analysed. Keywords. ... micelles that acted as the micro-reactor for the hydrolysis and condensation of .... (figure 3) indicated the formation of rutile phase (JCPDS card no. 82-0514) of ...

  8. Synthesis of nanocrystalline TiO 2 thin films by liquid phase ...

    Indian Academy of Sciences (India)

    A transparent, high purity titanium dioxide thin film composed of densely packed nanometer sized grains has been successfully deposited on a glass substrate at 30°C from an aqueous solution of TiO2–HF with the addition of boric acid as a scavenger by liquid phase deposition technique. From X-ray diffraction ...

  9. Shape-dependent Surface Energetics of Nanocrystalline TiO2

    International Nuclear Information System (INIS)

    Park, T.J.; Wong, S.; Levchenko, A.A.; Zhou, H.; Navrotsky, A.

    2010-01-01

    We report the direct determination of surface enthalpies for nanophase TiO 2 anatase with different morphologies derived from drop solution calorimetry in a molten sodium molybdate (3Na 2 Ol·4MoO 3 ) solvent at 702 C. The energetics of surface hydration has been measured using a Calvet microcalorimeter coupled with a gas dosing system. The surface enthalpies of hydrated surfaces for anatase TiO 2 nanoparticles, nanowires and sea-urchin-like assemblies are 0.51 ± 0.05, 1.07 ± 0.28, and 1.29 ± 0.16 J m -2 , respectively, whereas those of anhydrous surfaces are 0.74 ± 0.04, 1.24 ± 0.28, and 1.41 ± 0.16 J m -2 , respectively. The trend in TiO 2 , which shows higher surface enthalpies for more complex nanostructures, is consistent with that reported in ZnO. The shape-dependent surface enthalpy at the nanoscale level is discussed in terms of exposed surface structures. The enthalpies of hydration appear to be similar for all morphologies.

  10. Low-Temperature Preparation of Amorphous-Shell/Nanocrystalline-Core Nanostructured TiO2 Electrodes for Flexible Dye-Sensitized Solar Cells

    Directory of Open Access Journals (Sweden)

    Dongshe Zhang

    2008-01-01

    Full Text Available An amorphous shell/nanocrystalline core nanostructured TiO2 electrode was prepared at low temperature, in which the mixture of TiO2 powder and TiCl4 aqueous solution was used as the paste for coating a film and in this film amorphous TiO2 resulted from direct hydrolysis of TiCl4 at 100∘C sintering was produced to connect the particles forming a thick crack-free uniform nanostructured TiO2 film (12 μm, and on which a photoelectrochemical solar cell-based was fabricated, generating a short-circuit photocurrent density of 13.58 mA/cm2, an open-circuit voltage of 0.647 V, and an overall 4.48% light-to-electricity conversion efficiency under 1 sun illumination.

  11. Red shifts of the Eg(1) Raman mode of nanocrystalline TiO2:Er monoliths grown by sol-gel process

    Science.gov (United States)

    Palomino-Merino, R.; Trejo-Garcia, P.; Portillo-Moreno, O.; Jiménez-Sandoval, S.; Tomás, S. A.; Zelaya-Angel, O.; Lozada-Morales, R.; Castaño, V. M.

    2015-08-01

    Nanocrystalline monoliths of Er doped TiO2 were prepared by the sol-gel technique, by controlling the Er-doping levels into the TiO2 precursor solution. As-prepared and annealed in air samples showed the anatase TiO2 phase. The average diameter of the nanoparticles ranged from 19 to 2.6 nm as the nominal concentration of Er varies from 0% to 7%, as revealed by EDS analysis in an electron microscope. Photo Acoustic Spectroscopy (PAS) allowed calculate the forbidden band gap, evidencing an absorption edge at around 300 nm, attributed to TiO2 and evidence of electronic transitions or Er3+. The Raman spectra, corresponding to the anatase phase, show the main phonon mode Eg(1) band position at 144 cm-1 with a red shift for the annealing samples.

  12. Low temperature self-assembled growth of rutile TiO2/manganese oxide nanocrystalline films

    Science.gov (United States)

    Sun, Zhenya; Zhou, Daokun; Du, Jianhua; Xie, Yuxing

    2017-10-01

    We report formation of rutile TiO2 nanocrystal at low temperature range in the presence of α-MnO2 which self-assembled onto sulfanyl radical activated silicon oxide substrate. SEM, HRTEM, XPS and Raman spectroscopy were used to study the morphology and oxidation state of synthesised crystals. The results showed that when the α-MnO2 was reduced to Mn3O4, it induced the formation of rutile instead of anatase phase in the TiCl4-HCl aqueous system. The finding will promote the understanding of phase transformation mechanism when manganese oxide and titanium oxide co-exist in soil and water environment.

  13. Effective charge collection in dye-sensitized nanocrystalline TiO2

    Science.gov (United States)

    Yanagida, Masatoshi; Numata, Youhei; Yoshimatsu, Keiichi; Satoh, Shin; Han, Liyuan

    2013-03-01

    The effective charge collection in dye-sensitized solar cells (DSCs) is an important factor to improve the efficiency. Here, we report the comparison of three types of structures in DSCs. One type of structure is a sandwich-type DSC (SW-DSC), in which the TiO2 film is sandwiched between a TCO glass front electron-collection electrode and a sputtered Ti back collection electrode. The second is a normal DSC (N-DSC), which has no back electrode. The third is a back-contact-type DSC (BC-DSC), in which a sputtered Ti back electrode is deposited on a TiO2 film on the opposite side of the normal glass as an optical window. The photocurrent response of an SW-DSC is the fastest of the three structures due to using intensity modulated photocurrent spectroscopy, which can be explained by the electron diffusion model. The model shows that the SW-DSC is a favorable structure for effective charge collection in DSCs.

  14. Effective charge collection in dye-sensitized nanocrystalline TiO2

    International Nuclear Information System (INIS)

    Yanagida, Masatoshi; Numata, Youhei; Yoshimatsu, Keiichi; Satoh, Shin; Han, Liyuan

    2013-01-01

    The effective charge collection in dye-sensitized solar cells (DSCs) is an important factor to improve the efficiency. Here, we report the comparison of three types of structures in DSCs. One type of structure is a sandwich-type DSC (SW-DSC), in which the TiO 2 film is sandwiched between a TCO glass front electron-collection electrode and a sputtered Ti back collection electrode. The second is a normal DSC (N-DSC), which has no back electrode. The third is a back-contact-type DSC (BC-DSC), in which a sputtered Ti back electrode is deposited on a TiO 2 film on the opposite side of the normal glass as an optical window. The photocurrent response of an SW-DSC is the fastest of the three structures due to using intensity modulated photocurrent spectroscopy, which can be explained by the electron diffusion model. The model shows that the SW-DSC is a favorable structure for effective charge collection in DSCs. (paper)

  15. Semiconducting polymer-incorporated nanocrystalline TiO2 particles for photovoltaic applications

    International Nuclear Information System (INIS)

    Peng Fuguo; Wu Jihuai; Li Qingbei; Wang Yue; Yue Gentian; Xiao Yaoming; Li Qinghua; Lan Zhang; Fan Leqing; Lin Jianming; Huang Miaoliang

    2011-01-01

    Highlights: → A P3HT-PCBM/TiO 2 trinary hybrid solar cell has been fabricated. → P3HT-PCBM heterojunction replaces the dye and electrolyte in dye-sensitized cell, → Which simplifies preparation procedure and decreases the device cost. → The hybrid cell achieves a light-to-electric conversion efficiency of 2.61%. - Abstract: In this work, we study hybrid solar cells based on blends of the semiconducting polymer poly(3-octylthiophene-2,5-diyl)(P3OT) and [6,6]-phenyl C 61 butyric acid methyl (PCBM) coated titanium dioxide (TiO 2 ) nanocrystal film. The Fourier transform infrared spectra (FTIR), UV-vis absorption spectra and PL quenching researches show that the films had a stronger absorption in visible light range. The influence of the PCBM:P3OT ratio were researched and the optimized ratio of PCBM to P3OT (1:1.5) exhibit a short circuit current of 4.42 mA cm -2 , an open circuit voltage of 0.81 V, a fill factor of 0.73 and a light-to-electric conversion efficiency of 2.61% under a simulated solar light irradiation of 100 mW cm -2 .

  16. Study on defect properties of nanocrystalline TiO2 during phase transition by positron annihilation lifetime

    Science.gov (United States)

    Zheng, F.; Liu, Y.; Liu, Z.; Dai, Y.-Q.; Fang, P.-F.; Wang, S.-J.

    2012-08-01

    The defect properties of nanocrystalline TiO2 were investigated by positron annihilation lifetime spectroscopy (PALS) and X-ray diffraction (XRD) as a function of annealed temperature that ranged from 300 to 850 °C. Below 500 °C, the measured positron lifetimes of τ1 (200-206 ps) and τ2 (378-402 ps) revealed the existence of mono-vacancy and vacancy-clusters at grain surface and in the micro-void of intergranular region. Between 500 and 750 °C, the phase transition from anatase to rutile was probed by the variations of positron lifetime and XRD pattern. With the increasing temperature from 500 to 850 °C, the positron lifetime τ1, τ2 and its intensity I2 sharply decreased from 200 ps, 378 ps, and 60% to 135 ps, 274 ps, and 33%, respectively. The results clearly indicate that the mono-vacancy or vacancy-clusters at grain surface and micro-voids between the grains were annealed out during the phase transition.

  17. Natural Dye-Sensitized Solar Cell Based on Nanocrystalline TiO2

    International Nuclear Information System (INIS)

    Jasim, K.E.

    2012-01-01

    During the last quarter of the twentieth century there have been intensive research activities looking for green sources of energy. The main aim of the green generators or converters of energy is to replace the conventional (fossil) energy sources, hence reducing further accumulation of the green house gasses GHGs. Conventional silicon and III-V semiconductor solar cell based on crystalline bulk, quantum well and quantum dots structure or amorphous and thin film structures provided a feasible solution. However, natural dye sensitized solar cells NDSSC are a promising class of photovoltaic cells with the capability of generating green energy at low production cost since no vacuum systems or expensive equipment are required in their fabrication. Also, natural dyes are abundant, easily extracted and safe materials. In NDSSC, once dye molecules exposed to light they become oxidized and transfer electrons to a nano structured layer of wide bandgap semiconductors such as TiO 2 . The generated electrons are drawn outside the cell through ohmic contact to a load. In this paper we review the structure and operation principles of the dye sensitized solar cell DSSC. We discuss preparation procedures, optical and electrical characterization of the NDSSC using local dyes extracted from Henna (Lawsonia inermis L.), pomegranate, cherries and Bahraini raspberries (Rubus spp.). These natural organic dyes are potential candidates to replace some of the man-made dyes used as sensitizer in many commercialized photoelectrochemical cells. Factors limiting the operation of the DSSC are discussed. NDSSCs are expected to be a favored choice in the building-integrated photovoltaic (BIPV) due to their robustness, therefore, requiring no special shielding from natural events such as tree strikes or hails. (author)

  18. Degradation of organic dyes using spray deposited nanocrystalline stratified WO3/TiO2 photoelectrodes under sunlight illumination

    Science.gov (United States)

    Hunge, Y. M.; Yadav, A. A.; Mahadik, M. A.; Bulakhe, R. N.; Shim, J. J.; Mathe, V. L.; Bhosale, C. H.

    2018-02-01

    The need to utilize TiO2 based metal oxide hetero nanostructures for the degradation of environmental pollutants like Rhodamine B and reactive red 152 from the wastewater using stratified WO3/TiO2 catalyst under sunlight illumination. WO3, TiO2 and stratified WO3/TiO2 catalysts were prepared by a spray pyrolysis method. It was found that the stratified WO3/TiO2 heterostructure has high crystallinity, no mixed phase formation occurs, strong optical absorption in the visible region of the solar spectrum, and large surface area. The photocatalytic activity was tested for degradation of Rhodamine B (Rh B) and reactive red 152 in an aqueous medium. TiO2 layer in stratified WO3/TiO2 catalyst helps to extend its absorption spectrum in the solar light region. Rh B and Reactive red 152is eliminated up to 98 and 94% within the 30 and 40 min respectively at optimum experimental condition by stratified WO3/TiO2. Moreover, stratified WO3/TiO2 photoelectrode has good stability and reusability than individual TiO2 and WO3 thin film in the degradation of Rh B and reactive red 152. The photoelectrocatalytic experimental results indicate that stratified WO3/TiO2 photoelectrode is a promising material for dye removal.

  19. Dye Sensitized Solar Cell with Conventionally Annealed and Post-Hydrothermally Treated Nanocrystalline Semiconductor Oxide TiO2 Derived from Sol-Gel Process

    Directory of Open Access Journals (Sweden)

    Akhmad Yuwono

    2011-05-01

    Full Text Available Dye-sensitized solar cell (DSSC is one of the very promising alternative renewable energy sources to anticipate the declination in the fossil fuel reserves in the next few decades and to make use of the abundance of intensive sunlight energy in tropical countries like Indonesia. In the present study, TiO2 nanoparticles of different nanocrystallinity was synthesized via sol−gel process with various water to inorganic precursor ratio (Rw of 0.85, 2.00 and 3.50 upon sol preparation, followed with subsequent drying, conventional annealing and post-hydrothermal treatments. The resulting nanoparticles were integrated into the DSSC prototype and sensitized with an organic dye made of the extract of red onion. The basic performance of the fabricated DSSC has been examined and correlated to the crystallite size and band gap energy of TiO2 nanoparticles. It was found that post-hydrothermally treated TiO2 nanoparticles derived from sol of 2.00 Rw, with the most enhanced nanocrystalline size of 12.46 nm and the lowest band gap energy of 3.48 eV, showed the highest open circuit voltage (Voc of 69.33 mV.

  20. The influence of metal interlayers on the structural and optical properties of nano-crystalline TiO 2 films

    KAUST Repository

    Yang, Yong

    2012-03-01

    TiO 2-M-TiO 2 (M = W, Co and Ag) multilayer films have been deposited on glass substrates using reactive magnetron sputtering, then annealed in air for 2 h at 500°C. The structure, surface morphology and optical properties of the films have been studied using X-ray diffraction, Raman spectroscopy, atomic force microscopy and UV-vis spectroscopy. The TiO 2-W-TiO 2 and TiO 2-Co-TiO 2 films showed crystalline phases, whereas the TiO 2-Ag-TiO 2 films remained in the amorphous state. The crystallization temperature for the TiO 2-M-TiO 2 films decreased significantly compared with pure TiO 2 film deposited on quartz. Detailed analysis of the Raman spectra suggested that the crystallization of TiO 2-M-TiO 2 films was associated with the large structural deformation imposed by the oxidation of intermediate metal layers. Moreover, the optical band gap of the films narrowed due to the appearance of impurity levels as the metal ions migrated into the TiO 2 matrix. These results indicate that the insertion of intermediate metal layers provides a feasible access to improve the structural and optical properties of anatase TiO 2 films, leading to promising applications in the field of photocatalysis. © 2011 Elsevier B.V. All rights reserved.

  1. Coupling of Nanocrystalline Anatase TiO2 to Porous Nanosized LaFeO3 for Efficient Visible-Light Photocatalytic Degradation of Pollutants

    Directory of Open Access Journals (Sweden)

    Muhammad Humayun

    2016-01-01

    Full Text Available In this work we have successfully fabricated nanocrystalline anatase TiO2/perovskite-type porous nanosized LaFeO3 (T/P-LFO nanocomposites using a simple wet chemical method. It is clearly demonstrated by means of atmosphere-controlled steady-state surface photovoltage spectroscopy (SPS responses, photoluminescence spectra, and fluorescence spectra related to the formed OH− radical amount that the photogenerated charge carriers in the resultant T/P-LFO nanocomposites with a proper mole ratio percentage of TiO2 display much higher separation in comparison to the P-LFO alone. This is highly responsible for the improved visible-light activities of T/P-LFO nanocomposites for photocatalytic degradation of gas-phase acetaldehyde and liquid-phase phenol. This work will provide a feasible route to synthesize visible-light responsive nano-photocatalysts for efficient solar energy utilization.

  2. Nanocrystalline TiO2 Composite Films for the Photodegradation of Formaldehyde and Oxytetracycline under Visible Light Irradiation

    Directory of Open Access Journals (Sweden)

    Min Wei

    2017-06-01

    Full Text Available In order to effectively photodegradate organic pollutants, ZnO composite and Co-B codoped TiO2 films were successfully deposited on glass substrates via a modified sol-gel method and a controllable dip-coating technique. Combining with UV–Vis diffuse reflectance spectroscopy (DRS and photoluminescence spectra (PL analyses, the multi-modification could not only extend the optical response of TiO2 to visible light region but also decrease the recombination rate of electron-hole pairs. XRD results revealed that the multi-modified TiO2 film had an anatase-brookite biphase heterostructure. FE-SEM results indicated that the multi-modified TiO2 film without cracks was composed of smaller round-like nanoparticles compared to pure TiO2. BET surface area results showed that the specific surface area of pure TiO2 and the multi-modified TiO2 sample was 47.8 and 115.8 m2/g, respectively. By degradation of formaldehyde and oxytetracycline, experimental results showed that the multi-modified TiO2 film had excellent photodegradation performance under visible light irradiation.

  3. Surfactant-assisted sol gel preparation of high-surface area mesoporous TiO2 nanocrystalline Li-ion battery anodes

    International Nuclear Information System (INIS)

    Casino, S.; Di Lupo, F.; Francia, C.; Tuel, A.; Bodoardo, S.; Gerbaldi, C.

    2014-01-01

    Highlights: • Mesoporous TiO 2 nanocrystalline lithium battery anodes with tunable morphology. • Simple sol–gel technique using different cationic surfactants is adopted. • Textural/morphological characteristics define the electrochemical behaviour. • TiO 2 anatase using C16TAB exhibits stable performance after 200 cycles. • It shows promising prospects as high-voltage safe Li-ion battery anode. - Abstract: We here investigate the physico-chemical/morphological characteristics and cycling behaviour of several kinds of nanocrystalline TiO 2 Li-ion battery anodes selectively prepared through a simple sol–gel strategy based on a low-cost titanium oxysulfate precursor, by mediation of different cationic surfactants having different features (e.g., chain lengths, counter ion, etc.): i.e., cetyl-trimethylammonium bromide (CTAB), cetyl-trimethylammonium chloride (CTAC), benzalkonium chloride (BC) or octadecyl-trimethyl ammonium bromide (C 18 TAB). X-ray diffraction profiles reveal single phase anatase having good correspondence with the reference pattern when using short chain CTAB, while in the other cases the presence of chloride and/or an increased chain length affect the purity of the samples. FESEM analysis reveal nanosized particles forming cauliflower-like aggregates. TiO 2 materials demonstrate mesoporous characteristics and large specific surface area ranging from 250 to 30 m 2 g −1 . Remarkably stable electrode performance are achieved by appropriately selecting the cationic surfactant and the surfactant/precursor ratio. Detailed analysis is provided on the effect of the reaction conditions upon the formation of mesoporous crystalline titania enlightening new directions for the development of high performing lithium storage electrodes by a simple and low cost sol–gel strategy

  4. Photo catalytic degradation of nitrobenzene using nanocrystalline TiO2 photo catalyst doped with Zn ions

    International Nuclear Information System (INIS)

    Reynoso S, E. A.; Perez S, S.; Reyes C, A. P.; Castro R, C. L.; Felix N, R. M.; Lin H, S. W.; Paraguay D, F.; Alonso N, G.

    2013-01-01

    Photo catalysis is a method widely used in the degradation of organic pollutants of the environment. The development of new materials is very important to improve the photo catalytic properties and to find new applications for TiO 2 as a photo catalyst. In this article we reported the synthesis of a photo catalyst based on TiO 2 doped with Zn 2+ ions highly efficient in the degradation of nitrobenzene. The results of photo catalytic activity experiments showed that the Zn 2+ doped TiO 2 is more active that un-doped TiO 2 catalyst with an efficiency of 99% for the nitrobenzene degradation at 120 min with an apparent rate constant of 35 x 10 -3 min -1 . For the characterization of photo catalyst X-ray diffraction, transmission electron microscopy and Raman spectroscopy were used. (Author)

  5. Influence of surfactant and annealing temperature on optical properties of sol-gel derived nano-crystalline TiO2 thin films.

    Science.gov (United States)

    Vishwas, M; Sharma, Sudhir Kumar; Rao, K Narasimha; Mohan, S; Gowda, K V Arjuna; Chakradhar, R P S

    2010-03-01

    Titanium dioxide thin films have been synthesized by sol-gel spin coating technique on glass and silicon substrates with and without surfactant polyethylene glycol (PEG). XRD and SEM results confirm the presence of nano-crystalline (anatase) phase at an annealing temperature of 300 degrees C. The influence of surfactant and annealing temperature on optical properties of TiO(2) thin films has been studied. Optical constants and film thickness were estimated by Swanepoel's (envelope) method and by ellipsometric measurements in the visible spectral range. The optical transmittance and reflectance were found to decrease with an increase in PEG percentage. Refractive index of the films decreased and film thickness increased with the increase in percentage of surfactant. The refractive index of the un-doped TiO(2) films was estimated at different annealing temperatures and it has increased with the increasing annealing temperature. The optical band gap of pure TiO(2) films was estimated by Tauc's method at different annealing temperature. Copyright 2010 Elsevier B.V. All rights reserved.

  6. Electronic structure of the indium tin oxide/nanocrystalline anatase (TiO2)/ruthenium-dye interfaces in dye-sensitized solar cells

    Science.gov (United States)

    Lyon, J. E.; Rayan, M. K.; Beerbom, M. M.; Schlaf, R.

    2008-10-01

    The electronic structure of two interfaces commonly found in dye-sensitized photovoltaic cells based on nanocrystalline anatase TiO2 ("Grätzel cells") was investigated using photoemission spectroscopy (PES). X-ray photoemission spectroscopy (XPS) and ultraviolet photoemission spectroscopy (UPS) measurements were carried out on the indium tin oxide (ITO)/TiO2 and the TiO2/cis-bis(isothiocyanato)bis(2,2'-bipyridyl-4,4'-dicarboxylato)-ruthenium(II)bis-tetrabutylammonium dye ("N719" or "Ruthenium 535-bisTBA") interfaces. Both contacts were investigated using a multistep deposition procedure where the entire structure was prepared in vacuum using electrospray deposition. In between deposition steps the surface was characterized with XPS and UPS resulting in a series of spectra, allowing the determination of the orbital and band lineup at the interfaces. The results of these efforts confirm previous PES measurements on TiO2/dye contacts prepared under ambient conditions, suggesting that ambient contamination might not have significant influence on the electronic structure at the dye/TiO2 interface. The results also demonstrate that there may be a significant barrier for electron injection at the sputtered ITO/TiO2 interface and that this interface should be viewed as a semiconductor heterojunction rather than as metal-semiconductor (Schottky) contact.

  7. Enhancing the photocatalytic activity of nanocrystalline TiO2 by co-doping with fluorine and yttrium

    International Nuclear Information System (INIS)

    Zhang, Huarong; Miao, Guashuai; Ma, Xingping; Wang, Bei; Zheng, Haiwu

    2014-01-01

    Highlights: • (F, Y)-codoped TiO 2 nanoparticles were prepared by a simple sol–gel method. • The highest photocatalytic activity (15 times of that over the pure TiO 2 ) was exhibited in the codoped TiO 2 with 0.05% Y doping level. • The Y doping induced oxygen vancancies played a duel role on the photocatalyic activity of the codoped TiO 2 . • The photocatalytic reactive oxygen species are critical to the photocatalytic degradation processes. - Abstract: Fluorine and yttrium codoped TiO 2 nanoparticles were prepared using a simple sol–gel method. The products were characterized with various spectroscopic and analytical techniques to determine their structural, morphological, optical absorption and photocatalytic properties. The results reveal that neither F nor Y doping causes obvious absorption edge shift in TiO 2 . Photoluminescence (PL) emission spectra present that the PL signal is enhanced, suggesting a decrease of photo-generated charge carrier separation efficiency, after the F or Y doping. The synergistic action by the F and Y doping leads to the highest photocatalytic activity for the degradation of methylene blue solution in the 0.05% (F, Y)-codoped sample (15 times of that over the pure TiO 2 ). With the increase of Y doping level, the photocatalytic performance in the codoped samples increases firstly and then decreases. The photocatalytic activity variations after the F and Y doping were interpreted by the formation of photocatalytic reactive oxygen species induced by the dopings

  8. Synthesis and visible light photoactivity of anatase Ag, and garlic loaded TiO2 nanocrystalline catalyst

    Science.gov (United States)

    An excellent visible light activated Ag and S doped TiO2 nanocatalyst was prepared by using AgNO3 and garlic (Allium sativum) as Ag+ and sulfur sources, respectively. The catalyst resisted the change from anatase to rutile phase even at calcination at 700 oC. The photocatalytic e...

  9. The influence of metal interlayers on the structural and optical properties of nano-crystalline TiO 2 films

    KAUST Repository

    Yang, Yong; Zhang, Qiang; Zhang, Bei; Mi, Wenbo; Chen, Long; Li, Lin; Zhao, Chao; Diallo, Elhadj; Zhang, Xixiang

    2012-01-01

    TiO 2-M-TiO 2 (M = W, Co and Ag) multilayer films have been deposited on glass substrates using reactive magnetron sputtering, then annealed in air for 2 h at 500°C. The structure, surface morphology and optical properties of the films have been

  10. Synthesis of nanocrystalline TiB2 powder from TiO2, B2O3 and Mg ...

    Indian Academy of Sciences (India)

    gered by using: (i) a furnace or (ii) an electrical element touching the surface ... plicity, low energy consumption and good purity of the products. [12,13]. SHS method .... Similar to the TiO2–Mg system, by increasing the ini- tial temperature, the ...

  11. An investigation of the photosubstitution reaction between N719-dyed nanocrystalline TiO2 particles and 4-tert-butylpyridine

    DEFF Research Database (Denmark)

    Nour-Mohammadi, Farahnaz; Nguyen, Thai Hoang; Boschloo, Gerrit

    2007-01-01

    concentration. Based on this observation, a degradation mechanism was proposed, in which the reaction proceeds through the rate-determining formation of a common intermediate complex, I=[RuII(H2dcbpy)2(NCS)(NCS)]+. An average degradation rate of kdeg=6×10-3s-1 was obtained from the value of Φdeg and the back...... electron-transfer rate, kback of the reaction TiO2+e-|N719+→TiO2|N719, obtained by means of photo-induced absorption (PIA) measurements. The lifetime of the solar cell sensitizer N719 was estimated to be between 34 years, based on kdeg and an average literature value of the regeneration rate, kreg=2×106M-1...... simple model experiments. In these experiments, colloidal solutions of N719-dyed nanocrystalline TiO2 particles in acetonitrile were irradiated with 532-nm laser light in the presence of 0-1mol/l of 4-TBP. Five degradation products were identified using LC-ESI-MS: the 4-tert-butylpyridine substitution...

  12. Nanocrystalline SnO2-TiO2 thin film deposited on base of equilateral prism as an opto-electronic humidity sensor

    Science.gov (United States)

    Yadav, B. C.; Verma, Nidhi; Singh, Satyendra

    2012-09-01

    Present paper reports the synthesis of SnO2-TiO2 nanocomposite, its characterization and performance as opto-electronic humidity sensor. Nanocrystalline SnO2-TiO2 film was deposited on the base of an equilateral prism using a photo resist spinner and the as prepared film was annealed at 200 °C for 2 h. The crystal structure of the prepared film was investigated using X-ray diffraction (XRD). Minimum crystallite size of the material was found 7 nm. Surface morphology of the film was investigated by Scanning electron microscope (SEM LEO-0430, Cambridge). SEM image shows that the film is porous. Differential scanning calorimetry (DSC) of as synthesized material shows two exothermic peaks at about 40 and 110 °C, respectively which are due to the evaporation of chemical impurities and water. Further the prepared film was investigated through the exposure of humidity and relative humidity (%RH) was measured directly in terms of modulation in the intensity of light recorded on a digital power meter. The maximum sensitivity of sensor was found 4.14 μW/%RH, which is quite significant for sensor fabrication purposes.

  13. Fine control of the amount of preferential <001> orientation in DC magnetron sputtered nanocrystalline TiO2 films

    International Nuclear Information System (INIS)

    Stefanov, B; Granqvist, C G; Österlund, L

    2014-01-01

    Different crystal facets of anatase TiO 2 are known to have different chemical reactivity; in particular the {001} facets which truncates the bi-tetrahedral anatase morphology are reported to be more reactive than the usually dominant {101} facets. Anatase TiO 2 thin films were deposited by reactive DC magnetron sputtering in Ar/O 2 atmosphere and were characterized using Rietveld refined grazing incidence X-ray diffraction, atomic force microscopy and UV/Vis spectroscopy. By varying the partial O2 pressure in the deposition chamber, the degree of orientation of the grains in the film could be systematically varied with preferred <001> orientation changing from random upto 39% as determined by March-Dollase method. The orientation of the films is shown to correlate with their reactivity, as measured by photo-degradation of methylene blue in water solutions. The results have implications for fabrication of purposefully chemically reactive thin TiO 2 films prepared by sputtering methods

  14. The use of Red Cabbage’s anthocyanine extract as a photosensitizer on a Dye-Sensitized Nanocrystalline TiO2 Solar Cell

    Directory of Open Access Journals (Sweden)

    Akhiruddin Maddu

    2010-10-01

    Full Text Available A solid-state dye-sensitized nanocrystalline TiO2 solar cell utilizing anthocyanin extract form red cabbage as photosensitizer was fabricated. The solar cell was formed in sandwich structure, which two electrodes sandwiching polymer electrolyte containing a redox couple (I-/I3-. One of the electrodes, namely working electrode, TiO2 layer on TCO (transparent conducting oxide coated glass substrate was sensitized with anthocyanin dye as electron donor in the system. Another electrode was a carbon sheet as a counter electrode. Gel electrolyte based on PEG (polyethylene glycol containing a redox couple (I-/I3- used instead of liquid electrolyte in this photoelectrochemical cell. Two fabricated cells have an active area of 1 cm2 were soaked with anthocyanine dye for 1 hr and 24 hrs, respectively. The cells were tested by irradiation with halogen lamp of 24 Watt with intensity 4 mW/cm2 at a distance 30 cm. The testing results of the cells show an ideal I-V characteristic with output parameters: open circuit voltage (VOC of 500 mV, short circuit current (ISC of 5,6 μA and 7,2 μA for each cells, fill factor (FF of 48% for both cells, energy conversion (η of 0.023 % and 0,055 % for the cells with 1 hr and 24 hrs dye soaked, respectively.

  15. Synthesis and electronic structure of low-density monoliths of nanoporous nanocrystalline anatase TiO2

    Energy Technology Data Exchange (ETDEWEB)

    Kucheyev, S O; Baumann, T F; Wang, Y M; van Buuren, T; Satcher, J H

    2004-08-13

    Monolithic nanocrystalline anatase titania aerogels are synthesized by the epoxide sol-gel method followed by thermal annealing at 550 C. These aerogels are formed by {approx}10-20 nm size anatase nanoparticles which are randomly oriented and interconnected into an open-cell solid network. Aerogel monoliths have an apparent density of {approx}6% and a surface area of {approx} 100 m{sup 2} g{sup -1}. High-resolution transmission electron microscopy and soft x-ray absorption near-edge structure spectroscopy reveal good crystallinity of the anatase nanoparticles forming the aerogel skeleton.

  16. Equilibrium lithium-ion transport between nanocrystalline lithium-inserted anatase TiO2 and the electrolyte.

    Science.gov (United States)

    Ganapathy, Swapna; van Eck, Ernst R H; Kentgens, Arno P M; Mulder, Fokko M; Wagemaker, Marnix

    2011-12-23

    The power density of lithium-ion batteries requires the fast transfer of ions between the electrode and electrolyte. The achievable power density is directly related to the spontaneous equilibrium exchange of charged lithium ions across the electrolyte/electrode interface. Direct and unique characterization of this charge-transfer process is very difficult if not impossible, and consequently little is known about the solid/liquid ion transfer in lithium-ion-battery materials. Herein we report the direct observation by solid-state NMR spectroscopy of continuous lithium-ion exchange between the promising nanosized anatase TiO(2) electrode material and the electrolyte. Our results reveal that the energy barrier to charge transfer across the electrode/electrolyte interface is equal to or greater than the barrier to lithium-ion diffusion through the solid anatase matrix. The composition of the electrolyte and in turn the solid/electrolyte interface (SEI) has a significant effect on the electrolyte/electrode lithium-ion exchange; this suggests potential improvements in the power of batteries by optimizing the electrolyte composition. Copyright © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  17. Enhanced photovoltaic performance of dye-sensitized solar cells based on NaYF4:Yb(3+), Er(3+)-incorporated nanocrystalline TiO2 electrodes.

    Science.gov (United States)

    Zhu, Guang; Wang, Hongyan; Zhang, Quanxin; Zhang, Li

    2015-08-01

    Near infrared to visible up-conversion of light by rare earth ion-doped phosphors (NaYF4:Yb(3+), Er(3+)) that convert multiple photons of lower energy to higher energy photons offer new possibilities for improved performance of photovoltaic devices. Here, up-conversion phosphor NaYF4:Yb(3+), Er(3+) doped nanocrystalline TiO2 films are designed and used as a electrode for dye-sensitized solar cells, and the photovoltaic performance of DSSCs based on composite electrodes are investigated. The results show the cell with NaYF4:Yb(3+), Er(3+) achieves a power conversion efficiency of 7.65% under one sun illumination (AM 1.5G, 100mWcm(-2)), which is an increase of 14% compared to the cell without NaYF4:Yb(3+), Er(3+) (6.71%). The performance improvement is attributed to the dual effects of enhanced light harvesting from extended light absorption range and increased light scattering, and lower electron transfer resistance. Copyright © 2015 Elsevier Inc. All rights reserved.

  18. Low-temperature fabrication of TiO2 nanocrystalline film electrodes for dye-sensitized solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Shan, G.; Lee, K.E.; Charboneau, C.; Demopoulos, G.P.; Gauvin, R. [McGill Univ., Montreal, PQ (Canada). Dept. of Materials Engineering; Savadogo, O. [Ecole Polytechnique de Montreal, PQ (Canada). Dept. de Genie Chimique

    2008-07-01

    Dye-sensitized solar cells (DSSCs) have the potential to render solar energy widely accessible. The deposition of titania nano-crystalline powders on a substrate is an important step in the manufacture of the DSSC. The deposition forms a mesoporous thin film that is followed by thermal treatment and sensitization. Usually titania films are deposited on glass by screen printing and then annealed at temperatures as high as 530 degrees C to provide a good electrical contact between the semiconductor particles and crystallization of the anatase phase. Several research and development efforts have focused on the deposition of titania film on flexible plastic substrates that will simplify the whole manufacturing process in terms of flexibility, weight, application and cost. Lower temperature processing is needed for the preparation of plastic-based titania film electrodes, but this has proven to be counterproductive when it comes to the cell's conversion efficiency. This paper presented a comprehensive evaluation of the different coating and annealing techniques at low temperature as well as important processing factors for improvement. To date, these techniques include pressing, hydrothermal process, electrodeposition, electrophoretic deposition, microwave or UV irradiation, and lift-off technique.

  19. Nano-crystalline thin and nano-particulate thick TiO2 layer: Cost effective sequential deposition and study on dye sensitized solar cell characteristics

    International Nuclear Information System (INIS)

    Das, P.; Sengupta, D.; Kasinadhuni, U.; Mondal, B.; Mukherjee, K.

    2015-01-01

    Highlights: • Thin TiO 2 layer is deposited on conducting substrate using sol–gel based dip coating. • TiO 2 nano-particles are synthesized using hydrothermal route. • Thick TiO 2 particulate layer is deposited on prepared thin layer. • Dye sensitized solar cells are made using thin and thick layer based photo-anode. • Introduction of thin layer in particulate photo-anode improves the cell efficiency. - Abstract: A compact thin TiO 2 passivation layer is introduced between the mesoporous TiO 2 nano-particulate layer and the conducting glass substrate to prepare photo-anode for dye-sensitized solar cell (DSSC). In order to understand the effect of passivation layer, other two DSSCs are also developed separately using TiO 2 nano-particulate and compact thin film based photo-anodes. Nano-particles are prepared using hydrothermal synthesis route and the compact passivation layer is prepared by simply dip coating the precursor sol prepared through wet chemical route. The TiO 2 compact layer and the nano-particles are characterised in terms of their micro-structural features and phase formation behavior. It is found that introduction of a compact TiO 2 layer in between the mesoporous TiO 2 nano-particulate layer and the conducting substrate improves the solar to electric conversion efficiency of the fabricated cell. The dense thin passivation layer is supposed to enhance the photo-excited electron transfer and prevent the recombination of photo-excited electrons

  20. Influence of different TiO2 blocking films on the photovoltaic performance of perovskite solar cells

    Science.gov (United States)

    Zhang, Chenxi; Luo, Yudan; Chen, Xiaohong; Ou-Yang, Wei; Chen, Yiwei; Sun, Zhuo; Huang, Sumei

    2016-12-01

    Organolead trihalide perovskite materials have been successfully used as light absorbers in efficient photovoltaic (PV) cells. Cell structures based on mesoscopic metal oxides and planar heterojunctions have already demonstrated very impressive and brisk advances, holding great potential to grow into a mature PV technology. High power conversion efficiency (PCE) values have been obtained from the mesoscopic configuration in which a few hundred nano-meter thick mesoporous scaffold (e.g. TiO2 or Al2O3) infiltrated by perovskite absorber was sandwiched between the electron and hole transport layers. A uniform and compact hole-blocking layer is necessary for high efficient perovskite-based thin film solar cells. In this study, we investigated the characteristics of TiO2 compact layer using various methods and its effects on the PV performance of perovskite solar cells. TiO2 compact layer was prepared by a sol-gel method based on titanium isopropoxide and HCl, spin-coating of titanium diisopropoxide bis (acetylacetonate), screen-printing of Dyesol's bocking layer titania paste, and a chemical bath deposition (CBD) technique via hydrolysis of TiCl4, respectively. The morphological and micro-structural properties of the formed compact TiO2 layers were characterized by scanning electronic microscopy and X-ray diffraction. The analyses of devices performance characteristics showed that surface morphologies of TiO2 compact films played a critical role in affecting the efficiencies. The nanocrystalline TiO2 film deposited via the CBD route acts as the most efficient hole-blocking layer and achieves the best performance in perovskite solar cells. The CBD-based TiO2 compact and dense layer offers a small series resistance and a large recombination resistance inside the device, and makes it possible to achieve a high power conversion efficiency of 12.80%.

  1. Biomolecule-controlled hydrothermal synthesis of C-N-S-tridoped TiO2 nanocrystalline photocatalysts for NO removal under simulated solar light irradiation.

    Science.gov (United States)

    Wang, Yawen; Huang, Yu; Ho, Wingkei; Zhang, Lizhi; Zou, Zhigang; Lee, Shuncheng

    2009-09-30

    In this study, C-N-S-tridoped titanium dioxide (TiO(2)) nanocrystals were synthesized by using a facile hydrothermal method in the presence of a biomolecule l-cysteine. This biomolecule could not only serve as the common source for the carbon, sulfur and nitrogen tridoping, but also could control the final crystal phases and morphology. The resulting materials were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), nitrogen adsorption and UV-vis diffuse reflectance spectroscopy. XPS analysis revealed that S was incorporated into the lattice of TiO(2) through substituting oxygen atoms, N might coexist in the forms of N-Ti-O and Ti-O-N in tridoped TiO(2) and most C could form a mixed layer of carbonate species deposited on the surface of TiO(2) nanoparticles. The photocatalytic activities of the samples were tested on the removal of NO at typical indoor air level in a flow system under simulated solar light irradiation. The tridoped TiO(2) samples showed much higher removal efficiency than commercial P25 and the undoped counterpart photocatalyst. The enhanced visible light photocatalytic activity of C-N-S-tridoped TiO(2) nanocrystals was explained on the basis of characterizations. The possible formation process of the monodispersed C-N-S-tridoped anatase TiO(2) nanocrystals was also proposed. This study provides a new method to prepare visible light active TiO(2) photocatalyst.

  2. Biomolecule-controlled hydrothermal synthesis of C-N-S-tridoped TiO2 nanocrystalline photocatalysts for NO removal under simulated solar light irradiation

    International Nuclear Information System (INIS)

    Wang Yawen; Huang Yu; Ho Wingkei; Zhang Lizhi; Zou Zhigang; Lee Shuncheng

    2009-01-01

    In this study, C-N-S-tridoped titanium dioxide (TiO 2 ) nanocrystals were synthesized by using a facile hydrothermal method in the presence of a biomolecule L-cysteine. This biomolecule could not only serve as the common source for the carbon, sulfur and nitrogen tridoping, but also could control the final crystal phases and morphology. The resulting materials were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), nitrogen adsorption and UV-vis diffuse reflectance spectroscopy. XPS analysis revealed that S was incorporated into the lattice of TiO 2 through substituting oxygen atoms, N might coexist in the forms of N-Ti-O and Ti-O-N in tridoped TiO 2 and most C could form a mixed layer of carbonate species deposited on the surface of TiO 2 nanoparticles. The photocatalytic activities of the samples were tested on the removal of NO at typical indoor air level in a flow system under simulated solar light irradiation. The tridoped TiO 2 samples showed much higher removal efficiency than commercial P25 and the undoped counterpart photocatalyst. The enhanced visible light photocatalytic activity of C-N-S-tridoped TiO 2 nanocrystals was explained on the basis of characterizations. The possible formation process of the monodispersed C-N-S-tridoped anatase TiO 2 nanocrystals was also proposed. This study provides a new method to prepare visible light active TiO 2 photocatalyst.

  3. Surface modification of porous nanocrystalline TiO2 films for dye-sensitized solar cell application by various gas plasmas

    International Nuclear Information System (INIS)

    Kim, Youngsoo; Yoon, Chang-Ho; Kim, Kang-Jin; Lee, Yeonhee

    2007-01-01

    Titanium dioxide (TiO 2 ) film for dye-sensitized solar cells (DSSCs) has surface defects such as oxygen vacancies created during the annealing process. The authors used a plasma treatment technique to reduce defects on TiO 2 surfaces. They investigated the influence of different gas plasma treatments of TiO 2 film on the photoelectric performance of DSSC. Short-circuit photocurrent density (J sc ), open-circuit photovoltage (V oc ), and the amount of adsorbed dye for DSSCs were measured. As a result, the solar-to-electricity conversion efficiencies of the O 2 - and N 2 -treated cells increased by 15%-20% compared to untreated cells. On the other hand, solar energy conversion efficiency of CF 4 -plasma treated cells decreased drastically. The increased amount of adsorbed dye on the TiO 2 film was measured by time-of-flight secondary ion mass spectrometry. TiO 2 surfaces modified by plasma treatment were characterized using analytical instruments such as x-ray photoelectron spectroscopy and near-edge x-ray absorption fine structure

  4. Influences of the iron ion (Fe3+)-doping on structural and optical properties of nanocrystalline TiO2 thin films prepared by sol-gel spin coating

    International Nuclear Information System (INIS)

    Ben Naceur, J.; Mechiakh, R.; Bousbih, F.; Chtourou, R.

    2011-01-01

    Titanium dioxide (TiO 2 ) thin films doping of various iron ion (Fe 3+ ) concentrations were deposited on silicon (Si) (100) and quartz substrates by sol-gel Spin Coating technique followed by a thermal treatment at 600 deg. C. The structure, surface morphology and optical properties, as a function of the doping, have been studied by X-ray diffractometer (XRD), Raman, ultraviolet-visible (UV-vis) and Spectroscopic Ellipsometry (SE). XRD and Raman analyzes of our thin films show that the crystalline phase of TiO 2 thin films comprised only the anatase TiO 2 , but the crystallinity decreased when the Fe 3+ content increased from 0% to 20%. During the Fe 3+ addition to 20%, the phase of TiO 2 thin film still maintained the amorphous state. The grain size calculated from XRD patterns varies from 29.3 to 22.6 nm. The complex index and the optical band gap (E g ) of the films were determined by the spectroscopic ellipsometry analysis. We have found that the optical band gap decreased with an increasing Fe 3+ content.

  5. Co-sensitization of quantum dot sensitized solar cells composed of TiO2 nanocrystalline photoanode with CdS and PbS nanoparticles and effect of PbS on the performance of solar cell

    Directory of Open Access Journals (Sweden)

    Maziar Marandi

    2017-09-01

    Full Text Available In this research, CdS and PbS quantum dots were applied as the light sensitizers in TiO2 based nanostructured solar cells. The PbS quantum dots could absorb a wide range of the sunlight spectrum on earth due to their low bandgap energy. As a result, the cell sensitization is more effective by application of both CdS and PbS quantum dots sensitizers. The TiO2 nanocrystals were synthesized through a hydrothermal process and deposited on FTO glass substrates as the photoanode scaffold. Then PbS quantum dots were grown on the surface of this nanocrystalline layer by a successive ionic layer adsorption and reaction (SILAR method. The CdS quantum dots were over-grown in the next step through a similar deposition method. Finally this sensitized layer was applied as the photoelectrode of the corresponding quantum dot sensitized solar cells. The results demonstrated that the maximum efficiency was achieved for the cell with a photoanode made of co-sensitization through 2 and 6 cycles of PbS and CdS deposition, respectively. The photovoltaic parameters of this cell were measured as Jsc of 10.81 mA/cm2, Voc of 590 mv and energy conversion efficiency of 2.7+0.2%.

  6. Determination of the light-induced degradation rate of the solar cell sensitizer N719 on TiO2 nanocrystalline particles

    DEFF Research Database (Denmark)

    Nour-Mohammadi, Farahnaz; Doan Nguyen, Sau; Boschloo, Gerrit

    2005-01-01

    The oxidative degradation rate, kdeg of the solar cell dye (Bu4N+)2 [Ru(dcbpyH)2(NCS)2]2–, referred to as N719 or [RuL2(NCS)2], was obtained by applying a simple model system. Colloidal solutions of N719-dyed TiO2 particles in acetonitrile were irradiated with 532-nm monochromatic light, and the ...

  7. Thermal analysis of formation of nano-crystalline BaTiO3 using Ba(NO32 and TiO2

    Directory of Open Access Journals (Sweden)

    Md. Jawed Ansaree

    2015-12-01

    Full Text Available The reaction of Ba(NO32 with TiO2 was studied by thermogravimetric (TG and differential scanning calorimetric (DSC techniques up to 1000 °C and in nitrogen atmosphere. It was found that the formation of BaTiO3 takes place above 600 °C and that precursor mixing time and heating rate have no effect on the reaction temperature. BaTiO3 powder was prepared by calcination of Ba(NO32 and TiO2 precursor mixture at 800 °C for 8 h. X-ray diffraction analysis of the synthesized BaTiO3 confirmed the formation of tetragonal phase with lattice parameters a = 3.9950±0.0003 Å and c = 4.0318±0.0004 Å. Thermal analysis of the synthesized BaTiO3 powder showed weight loss within temperature range 40–1000 °C of only 0.40%. This small amount of weight loss was connected with some impurity phase, and identified as BaCO3 using Fourier transform infrared (FTIR technique.

  8. Passivation of nanocrystalline TiO2 junctions by surface adsorbed phosphinate amphiphiles enhances the photovoltaic performance of dye sensitized solar cells

    KAUST Repository

    Wang, Mingkui

    2009-01-01

    We report a new class of molecular insulators that electronically passivate the surface of nanocrystalline titania films for high performance dye sensitized solar cells (DSC). Using electrical impedance measurements we demonstrate that co-adsorption of dineohexyl bis-(3,3-dimethyl-butyl)-phosphinic acid (DINHOP), along with the amphiphilic ruthenium sensitizer Z907Na increased substantially the power output of the cells mainly due to a retardation of interfacial recombination of photo-generated charge carriers. The use of phosphinates as anchoring groups opens up new avenues for modification of the surface by molecular insulators, sensitizers and other electro-active molecules to realize the desired optoelectronic performance of devices based on oxide junctions. © 2009 The Royal Society of Chemistry.

  9. Electronic-state-driven adsorption of O2 on a nanocrystalline TiO2 under 'dark' and UV-irradiation conditions: Ab initio study

    Science.gov (United States)

    Kevorkyants, R.; Sboev, M. N.; Chizhov, Yu. V.

    2018-04-01

    DFT study on O2 adsorption on a nanocrystalline titania is presented for the first time. The dioxide's nanoparticle is modeled via the nanocluster Ti8O16. According to the calculations, O2 physisorbs on the nanocluster Ti8O16 in S0 and T0 states and chemisorbs on the nanocluster in S1 state. The computed adsorption enthalpies, O2 vibrational frequencies, and O2-g-tensor agree well with available data. In contrast to the axial O2 orientation on a surface of titania with oxygen vacancies, in the chemisorption complex O2 is oriented laterally. We explain this by the sterical hindrance of the Ti3+ centers in the former case.

  10. Electrochemical Behavior of TiO2 Nanoparticle Doped WO3 Thin Films

    Directory of Open Access Journals (Sweden)

    Suvarna R. Bathe

    2014-01-01

    Full Text Available Nanoparticle TiO2 doped WO3 thin films by pulsed spray pyrolysis technique have been studied on fluorine tin doped (FTO and glass substrate. XRD shows amorphous nature for undoped and anatase phase of TiO2 having (101 plane for nanoparticle TiO2 doped WO3 thin film. SEM shows microfibrous reticulated porous network for WO3 with 600 nm fiber diameter and nanocrystalline having size 40 nm for TiO2 nanoparticle doped WO3 thin film. TiO2 nanoparticle doped WO3 thin film shows ~95% reversibility due to may be attributed to nanocrystalline nature of the film, which helpful for charge insertion and deinsertion process. The diffusion coefficient for TiO2 nanoparticle doped WO3 film is less than undoped WO3.

  11. Dye-Sensitized Solar Cells with Anatase TiO2 Nanorods Prepared by Hydrothermal Method

    Directory of Open Access Journals (Sweden)

    Ming-Jer Jeng

    2013-01-01

    Full Text Available The hydrothermal method provides an effective reaction environment for the synthesis of nanocrystalline materials with high purity and well-controlled crystallinity. In this work, we started with various sizes of commercial TiO2 powders and used the hydrothermal method to prepare TiO2 thin films. We found that the synthesized TiO2 nanorods were thin and long when smaller TiO2 particles were used, while larger TiO2 particles produced thicker and shorter nanorods. We also found that TiO2 films prepared by TiO2 nanorods exhibited larger surface roughness than those prepared by the commercial TiO2 particles. It was found that a pure anatase phase of TiO2 nanorods can be obtained from the hydrothermal method. The dye-sensitized solar cells fabricated with TiO2 nanorods exhibited a higher solar efficiency than those fabricated with commercial TiO2 nanoparticles directly. Further, triple-layer structures of TiO2 thin films with different particle sizes were investigated to improve the solar efficiency.

  12. Bilirubin adsorption on nanocrystalline titania films

    International Nuclear Information System (INIS)

    Yang Zhengpeng; Si Shihui; Fung Yingsing

    2007-01-01

    Bilirubin produced from hemoglobin metabolism and normally conjugated with albumin is a kind of lipophilic endotoxin, and can cause various diseases when its concentration is high. Bilirubin adsorption on the nanocrystalline TiO 2 films was investigated using quartz crystal microbalance, UV-vis and IR techniques, and factors affecting its adsorption such as pH, bilirubin concentration, solution ionic strength, temperature and thickness of TiO 2 films were discussed. The amount of adsorption and parameters for the adsorption kinetics were estimated from the frequency measurements of quartz crystal microbalance. A fresh surface of the nanocrystalline TiO 2 films could be photochemically regenerated because holes and hydroxyl radicals were generated by irradiating the nanocrystalline TiO 2 films with UV light, which could oxidize and decompose organic materials, and the nanocrystalline TiO 2 films can be easily regenerated when it is used as adsorbent for the removal of bilirubin

  13. Effects of Homogenization Scheme of TiO2 Screen-Printing Paste for Dye-Sensitized Solar Cells

    Directory of Open Access Journals (Sweden)

    Seigo Ito

    2012-01-01

    Full Text Available TiO2 porous electrodes have been fabricated for photoelectrodes in dye-sensitized solar cells (DSCs using TiO2 screen-printing paste from nanocrystalline TiO2 powder dried from the synthesized sol. We prepared the TiO2 screen-printing paste by two different methods to disperse the nanocrystalline TiO2 powder: a “ball-milling route” and a “mortal-grinding route.” The TiO2 ball-milling (TiO2-BM route gave monodisperse TiO2 nanoparticles, resulting in high photocurrent density (14.2 mA cm−2 and high photoconversion efficiency (8.27%. On the other hand, the TiO2 mortal-grinding (TiO2-MG route gave large aggregate of TiO2 nanoparticles, resulting in low photocurrent density (11.5 mA cm−2 and low photoconversion efficiency (6.43%. To analyze the photovoltaic characteristics, we measured the incident photon-to-current efficiency, light absorption spectroscopy, and electrical impedance spectroscopy of DSCs.

  14. Monte Carlo random walk simulation of electron transport in confined porous TiO2 as a promising candidate for photo-electrode of nano-crystalline solar cells

    Science.gov (United States)

    Javadi, M.; Abdi, Y.

    2015-08-01

    Monte Carlo continuous time random walk simulation is used to study the effects of confinement on electron transport, in porous TiO2. In this work, we have introduced a columnar structure instead of the thick layer of porous TiO2 used as anode in conventional dye solar cells. Our simulation results show that electron diffusion coefficient in the proposed columnar structure is significantly higher than the diffusion coefficient in the conventional structure. It is shown that electron diffusion in the columnar structure depends both on the cross section area of the columns and the porosity of the structure. Also, we demonstrate that such enhanced electron diffusion can be realized in the columnar photo-electrodes with a cross sectional area of ˜1 μm2 and porosity of 55%, by a simple and low cost fabrication process. Our results open up a promising approach to achieve solar cells with higher efficiencies by engineering the photo-electrode structure.

  15. Monte Carlo random walk simulation of electron transport in confined porous TiO2 as a promising candidate for photo-electrode of nano-crystalline solar cells

    International Nuclear Information System (INIS)

    Javadi, M.; Abdi, Y.

    2015-01-01

    Monte Carlo continuous time random walk simulation is used to study the effects of confinement on electron transport, in porous TiO 2 . In this work, we have introduced a columnar structure instead of the thick layer of porous TiO 2 used as anode in conventional dye solar cells. Our simulation results show that electron diffusion coefficient in the proposed columnar structure is significantly higher than the diffusion coefficient in the conventional structure. It is shown that electron diffusion in the columnar structure depends both on the cross section area of the columns and the porosity of the structure. Also, we demonstrate that such enhanced electron diffusion can be realized in the columnar photo-electrodes with a cross sectional area of ∼1 μm 2 and porosity of 55%, by a simple and low cost fabrication process. Our results open up a promising approach to achieve solar cells with higher efficiencies by engineering the photo-electrode structure

  16. Photodecomposition of volatile organic compounds using TiO2 nanoparticles.

    Science.gov (United States)

    Jwo, Ching-Song; Chang, Ho; Kao, Mu-Jnug; Lin, Chi-Hsiang

    2007-06-01

    This study examined the photodecomposition of volatile organic compounds (VOCs) using TiO2 catalyst fabricated by the Submerged Arc Nanoparticle Synthesis System (SANSS). TiO2 catalyst was employed to decompose volatile organic compounds and compare with Degussa-P25 TiO2 in terms of decomposition efficiency. In the electric discharge manufacturing process, a Ti bar, applied as the electrode, was melted and vaporized under high temperature. The vaporized Ti powders were then rapidly quenched under low-temperature and low-pressure conditions in deionized water, thus nucleating and forming nanocrystalline powders uniformly dispersed in the base solvent. The average diameter of the TiO2 nanoparticles was 20 nm. X-ray diffraction analysis confirmed that the nanoparticles in the deionized water were Anatase type TiO2. It was found that gaseous toluene exposed to UV irradiation produced intermediates that were even harder to decompose. After 60-min photocomposition, Degussa-P25 TiO2 reduced the concentration of gaseous toluene to 8.18% while the concentration after decomposition by SANSS TiO2 catalyst dropped to 0.35%. Under UV irradiation at 253.7 +/- 184.9 nm, TiO2 prepared by SANSS can produce strong chemical debonding energy, thus showing great efficiency, superior to that of Degussa-P25 TiO2, in decomposing gaseous toluene and its intermediates.

  17. Photocatalytic properties of porous TiO2/Ag thin films

    International Nuclear Information System (INIS)

    Chang, C.-C.; Chen, J.-Y.; Hsu, T.-L.; Lin, C.-K.; Chan, C.-C.

    2008-01-01

    In this study, nanocrystalline TiO 2 /Ag composite thin films were prepared by a sol-gel spin-coating technique. By introducing polystyrene (PS) spheres into the precursor solution, porous TiO 2 /Ag thin films were prepared after calcination at a temperature of 500 deg. C for 4 h. Three different sizes (50, 200, and 400 nm) of PS spheres were used to prepare porous TiO 2 films. The as-prepared TiO 2 and TiO 2 /Ag thin films were characterized by X-ray diffractometry (XRD) and by scanning electron microscopy to reveal structural and morphological differences. In addition, the photocatalytic properties of these films were investigated by degrading methylene blue under UV irradiation. When PS spheres of different sizes were introduced after calcination, the as-prepared TiO 2 films exhibited different porous structures. XRD results showed that all TiO 2 /Ag films exhibited a major anatase phase. The photodegradation of porous TiO 2 thin films prepared with 200 nm PS spheres and doped with 1 mol% Ag exhibited the best photocatalytic efficiency where ∼ 100% methylene blue was decomposed within 8 h under UV exposure

  18. Chemically deposited TiO2/CdS bilayer system for ...

    Indian Academy of Sciences (India)

    FTO/TiO2/CdS bilayers system showed improved performance of PEC properties over individual ... form distribution of nanocrystalline CdS on TiO2 and this is unfavourable for the ... (TEA), the pH of the solution maintained at 12·0 by drop.

  19. Correlation of Photocatalysis and Photoluminescence Effect in Relation to the Surface Properties of TiO2:Tb Thin Films

    Directory of Open Access Journals (Sweden)

    Damian Wojcieszak

    2013-01-01

    Full Text Available In this paper structural, optical, photoluminescence, and photocatalytic properties of TiO2 and TiO2:(2.6 at. % Tb thin films have been compared. Thin films were prepared by high-energy reactive magnetron sputtering process, which enables obtaining highly nanocrystalline rutile structure of deposited films. Crystallites sizes were 8.7 nm and 6.6 nm for TiO2 and TiO2:Tb, respectively. Surface of prepared thin films was homogenous with small roughness of ca. 7.2 and 2.1 nm in case of TiO2 and TiO2:Tb samples, respectively. Optical properties measurements have shown that the incorporation of Tb into TiO2 matrix has not changed significantly the thin films transparency. It also enables obtaining photoluminescence effect in wide range from 350 to 800 nm, what is unique phenomenon in case of TiO2 with rutile structure. Moreover, it has been found that the incorporation of 2.6 at. % of Tb has increased the photocatalytic activity more than two times as compared to undoped TiO2. Additionally, for the first time in the current state of the art, the relationship between photoluminescence effect, photocatalytic activity, and surface properties of TiO2:Tb thin films has been theoretically explained.

  20. Molecular design of TiO2 for gigantic red shift via sublattice substitution.

    Science.gov (United States)

    Shao, Guosheng; Deng, Quanrong; Wan, Lin; Guo, Meilan; Xia, Xiaohong; Gao, Yun

    2010-11-01

    The effects of 3d transition metal doping in TiO2 phases have been simulated in detail. The results of modelling indicate that Mn has the biggest potential among 3d transition metals, for the reduction of energy gap and the introduction of effective intermediate bands to allow multi-band optical absorption. On the basis of theoretical formulation, we have incorporated considerable amount of Mn in nano-crystalline TiO2 materials. Mn doped samples demonstrate significant red shift in the optical absorption edge, with a secondary absorption edge corresponding to theoretically predicted intermediate bands/states. The gigantic red shift achievable in Mn-doped TiO2 is expected to extend the useful TiO2 functionalities well beyond the UV threshold via the optical absorption of both visible and infrared photon irradiance.

  1. Mesoscopic biology

    Indian Academy of Sciences (India)

    In this paper we present a qualitative outlook of mesoscopic biology where the typical length scale is of the order of nanometers and the energy scales comparable to thermal energy. Novel biomolecular machines, governed by coded information at the level of DNA and proteins, operate at these length scales in biological ...

  2. TiO2-BASED Composite Films for the Photodegradation of Oxytetracycline

    Science.gov (United States)

    Li, Hui; Guan, Ling-Xiao; Feng, Ji-Jun; Li, Fang; Yao, Ming-Ming

    2015-02-01

    The spread of the antibiotic oxytetracycline (OTC) has been thought as a threat to the safety of drinking water. In this paper, the photocatalytic activity of the nanocrystalline Fe/Ca co-doped TiO2-SiO2 composite film for the degradation of OTC was studied. The films were characterized by field emission scanning electron microscopy (FE-SEM) equipped with energy-dispersive spectroscopy (EDS), N2 adsorption/desorption isotherms, photoluminescence (PL) spectra, and UV-Vis diffraction reflectance absorption spectra (DRS). The FE-SEM results indicated that the Fe/Ca co-doped TiO2-SiO2 film was composed of smaller nanoparticles compared to pure TiO2 or TiO2-SiO2 film. The BET surface area results showed that the specific surface area of the pure TiO2, TiO2-SiO2 and Ca2+/Fe3+ co-doped TiO2-SiO2 is 118.3 m2g-1, 294.3 m2g-1 and 393.7 m2g-1, respectively. The DRS and PL spectra revealed that the Fe/Ca co-doped TiO2-SiO2 film had strong visible light adsorption and diminished electrons/holes recombination. Experimental results showed that the Fe/Ca co-doped TiO2-SiO2 film is effective in the degradation of OTC under both UV and visible light irradiation.

  3. Synthesis of photosensitive nanograined TiO2 thin films by SILAR method

    International Nuclear Information System (INIS)

    Patil, U.M.; Gurav, K.V.; Joo, Oh-Shim; Lokhande, C.D.

    2009-01-01

    Nanocrystalline TiO 2 thin films are deposited by simple successive ionic layer adsorption and reaction (SILAR) method on glass and fluorine-doped tin oxide (FTO)-coated glass substrate from aqueous solution. The as-deposited films are heat treated at 673 K for 2 h in air. The change in structural, morphological and optical properties are studied by means of X-ray diffraction (XRD), selected area electron diffraction (SAED), scanning electron microscopy (SEM), Fourier transform infrared (FTIR), transmission electron microscopy (TEM) and UV-vis-NIR spectrophotometer. The results show that the SILAR method allows the formation of anatase, nanocrystalline, and porous TiO 2 thin films. The heat-treated film showed conversion efficiency of 0.047% in photoelectrochemical cell with 1 M NaOH electrolyte.

  4. Promotion of Phenol Photodecomposition over TiO2 Using Au, Pd, and AuPd Nanoparticles

    DEFF Research Database (Denmark)

    Su, Ren; Tiruvalam, Ramchandra; He, Qian

    2012-01-01

    Noble metal nanoparticles (Au, Pd, AuPd alloys) with a narrow size distribution supported on nanocrystalline TiO2 (M/TiO2) have been synthesized via a sol-immobilization route. The effect of metal identity and size on the photocatalytic performance of M/TiO2 has been systematically investigated u...

  5. Synthesis, characterization, and analysis of enhanced photocatalytic activity of Zr-doped TiO2 nanostructured powders under UV light

    Science.gov (United States)

    Sekhar, M. Chandra; Purusottam Reddy, B.; Mallikarjuna, K.; Shanmugam, Gnanendra; Ahn, Chang-Hoi; Park, Si-Hyun

    2018-01-01

    Zr-doped and pure TiO2 nanoparticles (NPs) were synthesized using a simple inexpensive sol-gel method. X-ray powder diffractometry and Fourier transform infrared spectrometry revealed the presence of anatase-phase TiO2 NPs. Scanning electron microscopy and transmission electron microscopy revealed that the average nanocrystalline size of approximately 15 nm. The photocatalytic activities of these materials were evaluated using Rhodamine B (Rh B) as an organic contaminant. The photocatalytic activity of pure and Zr-doped TiO2 NPs (with at% 4, 8, 12 and 16) was measured in terms of the degradation of Rh B under UV light. The antibacterial activities of pure and Zr-doped (with 8 at%) TiO2 NPs were evaluated against Bacillus subtillis, Escherichia coli, and Pseudomonas aeruginosa. A maximum inhibition zone (19 mm) was observed for pure TiO2 NPs, against Bacillus subtillis and Pseudomonas aeruginosa, while Zr-doped TiO2 (8 at%) exhibited a lesser inhibition zone (18 mm) against the same Bacillus subtillis and Pseudomonas aeruginosa (18 mm). However, Zr-doped TiO2 (8 at%) NPs exhibited a greater inhibition zone against Escherichia coli (17 mm), while the activity of pure TiO2 NPs against Escherichia coli (15 mm) was retarded. Thus, pure TiO2 NPs and Zr-doped TiO2 (8 at%) NPs have competent activities and can be used as antibacterial agents against different bacteria.

  6. Correlation between photoconductivity in nanocrystalline titania and short circuit current transients in MEH-PPV/titania solar cells

    International Nuclear Information System (INIS)

    Xie, Z B; Henry, B M; Kirov, K R; Barkhouse, D A R; Burlakov, V M; Smith, H E; Grovenor, C R M; Assender, H E; Briggs, G A D; Kano, M; Tsukahara, Y

    2007-01-01

    We report the first experimental observation of a direct relationship between electron transport in different nanocrystalline TiO 2 thin films and the photovoltaic performance of TiO 2 /MEH-PPV composite solar cells made using these same TiO 2 films. We show that the transient behaviour in the composite solar cells under illumination can be explained by the transient photoconductivity performance of the TiO 2 layer

  7. Preparation and characterization of phase-pure anatase and rutile TiO2 powder by new chemistry route

    International Nuclear Information System (INIS)

    Pereira, E. A.; Montanhera, M.A.; Paula, F.R.; Spada, E.R.

    2014-01-01

    Titanium dioxide (TiO 2 ) is used in a wire range applications such as photocatalysis and sensor device. In this work is shown a new and effective method for the preparation of TiO 2 nanocrystalline in the crystallographic forms, anatase and rutile. The method involves dissolving the TiOSO 4 powder in H 2 O 2 solution and thermal treatment of amorphous precipitate. The technique of X-ray diffraction was used to follow the structure evolution of amorphous precipitate. Pure anatase structure and rutile are obtained at 600 deg C and 1000 deg C with a grain size estimated 24 and 55 nm respectively. TiO 2 nanoparticles is a promising alternative of the low cost whose potential for solar cells deserve a careful evaluation, especially in hybrid solar cells that employs TiO 2 as electron acceptor and as transport channels. (author)

  8. Effect of the dielectric constant of mesoscopic particle on the exciton binding energy

    International Nuclear Information System (INIS)

    Lai Zuyou; Gu Shiwei

    1991-09-01

    For materials with big exciton reduced mass and big dielectric constant, such as TiO 2 , the variation of dielectric constant with the radius of an ultrafine particle (UFP) is important for determining the exciton binding energy. For the first time a phenomenological formula of the dielectric constant of a UFP with its radius in mesoscopic range is put forward in order to explain the optical properties of TiO 2 UFP. (author). 22 refs, 3 figs, 1 tab

  9. Sol–gel synthesis of highly TiO2 aerogel photocatalyst via high temperature supercritical drying

    Directory of Open Access Journals (Sweden)

    Rebah Moussaoui

    2017-09-01

    Full Text Available Nanocrystalline powders of TiO2 xerogel and aerogel were prepared by using acid-modified sol–gel approach. For TiO2 aerogel material (TA, the solvent was high temperature supercritically extracted at 300 °C and 100 bars. However, the TiO2 xerogel material (TX was dried at 200 °C and ambient pressure. The effects of the drying processes on the crystalline structure, phase transformation and grain growth were determined by Raman spectroscopy, SAED and X-ray diffraction (XRD analyses using Rietveld refinement method. The TiO2 aerogel was composed of anatase crystalline structure. The TiO2 xerogel material was composed of anatase, brookite and small amount of amorphous phase with anatase as dominant phase. The TX sample still contains a relatively high concentration of carbon than that of TA, indicating the amorphous character of TiO2 xerogel. These materials were applied as catalyst for the degradation of indigo carmine in aqueous medium. Photo-degradation ability of TA and TX was compared to the TiO2 commercial Degussa P25. The photo-catalytic results showed that the degradation efficiency was in the order TA > P25 > TX. The photo-degradation of indigo carmine followed pseudo first order reaction kinetics.

  10. Visible photoenhanced current-voltage characteristics of Au : TiO2 nanocomposite thin films as photoanodes

    International Nuclear Information System (INIS)

    Naseri, N; Amiri, M; Moshfegh, A Z

    2010-01-01

    In this investigation, the effect of annealing temperature and concentration of gold nanoparticles on the photoelectrochemical properties of sol-gel deposited Au : TiO 2 nanocomposite thin films is studied. Various gold concentrations have been added to the TiO 2 thin films and their properties are compared. All the deposited samples are annealed at different temperatures. The optical density spectra of the films show the formation of gold nanoparticles in the films. The optical bandgap energy of the Au : TiO 2 films decreases with increasing Au concentration. The crystalline structure of the nanocomposite films is studied by x-ray diffractometry indicating the formation of gold nanocrystals in the anatase TiO 2 nanocrystalline thin films. X-ray photoelectron spectroscopy reveals that the presence of gold in the metallic state and the formation of TiO 2 are stoichiometric. The photoelectrochemical properties of the Au : TiO 2 samples are characterized using a compartment cell containing H 2 SO 4 and KOH as cathodic and anodic electrolytes, respectively. It is found that the addition of Au nanoparticles in TiO 2 films enhances the photoresponse of the layer and the addition of gold nanocrystals with an optimum value of 5 mol% resulted in the highest photoelectrochemical activity. Moreover, the photoresponse of the samples is also enhanced with an increase in the annealing temperature.

  11. A novel single-step synthesis of N-doped TiO2 via a sonochemical method

    International Nuclear Information System (INIS)

    Wang, Xi-Kui; Wang, Chen; Guo, Wei-Lin; Wang, Jin-Gang

    2011-01-01

    Graphical abstract: The N-doped anatase TiO 2 nanoparticles were synthesized by sonochemical method. The as-prepared sample is characterized by XRD, TEM, XPS and UV-Vis DRS. The photocatalytic activity of the photocatalyst was evaluated by the photodegradation of an azo dye direct sky blue 5B. Highlights: → A novel singal-step sonochemical synthesis method for the preparation of anatase N-doped TiO 2 nanocrystalline at low temperature has been devoleped. → The as-prepared sample is characterized by XRD, TEM, XPS and UV-Vis DRS. → The photodegradation of azo dye direct sky blue 5 showed that the N-doped TiO 2 catalyst is of high visible-light photocatalytic activity. -- Abstract: A novel single-step synthetic method for the preparation of anatase N-doped TiO 2 nanocrystalline at low temperature has been devoleped. The N-doped anatase TiO 2 nanoparticles were synthesized by sonication of the solution of tetraisopropyl titanium and urea in water and isopropyl alcohol at 80 o C for 150 min. The as-prepared sample was characterized by X-ray diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy and UV-vis absorption spectrum. The product structure depends on the reaction temperature and reaction time. The photocatalytic activity of the as-prepared photocatalyst was evaluated via the photodegradation of an azo dye direct sky blue 5B. The results show that the N-doped TiO 2 nanocrystalline prepared via sonication exhibit an excellent photocatalytic activity under UV light and simulated sunlight.

  12. Preparation of flexible TiO2 photoelectrodes for dye-sensitized solar cells

    Science.gov (United States)

    Li, Wen-Ren; Wang, Hsiu-Hsuan; Lin, Chia-Feng; Su, Chaochin

    2014-09-01

    Dye-sensitized solar cells (DSSCs) based on nanocrystalline TiO2 photoelectrodes on indium tin oxide (ITO) coated polymer substrates have drawn great attention due to its lightweight, flexibility and advantages in commercial applications. However, the thermal instability of polymer substrates limits the process temperature to below 150 °C. In order to assure high and firm interparticle connection between TiO2 nanocrystals (TiO2-NC) and polymer substrates, the post-treatment of flexible TiO2 photoelectrodes (F-TiO2-PE) by mechanical compression was employed. In this work, Degussa P25 TiO2-NC was mixed with tert-butyl alcohol and DI-water to form TiO2 paste. F-TiO2-PE was then prepared by coating the TiO2 paste onto ITO coated polyethylene terephthalate (PET) substrate using doctor blade followed by low temperature sintering at 120 °C for 2 hours. To study the effect of mechanical compression, we applied 50 and 100 kg/cm2 pressure on TiO2/PET to complete the fabrication of F-TiO2-PE. The surface morphology of F-TiO2-PE was characterized using scanning electron microscopy. The resultant F-TiO2-PE sample exhibited a smooth, crack-free structure indicating the great improvement in the interparticle connection of TiO2-NC. Increase of compression pressure could lead to the increase of DSSC photoconversion efficiency. The best photoconversion efficiency of 4.19 % (open circuit voltage (Voc) = 0.79 V, short-circuit photocurrent density (Jsc) = 7.75 mA/cm2, fill factor (FF) = 0.68) was obtained for the F-TiO2-PE device, which showed great enhancement compared with the F-TiO2-PE cell without compression treatment. The effect of compression in DSSC performance was vindicated by the electrochemical impedance spectroscopy measurement.

  13. Rapid fabrication of mesoporous TiO2 thin films by pulsed fibre laser for dye sensitized solar cells

    Science.gov (United States)

    Hadi, Aseel; Alhabradi, Mansour; Chen, Qian; Liu, Hong; Guo, Wei; Curioni, Michele; Cernik, Robert; Liu, Zhu

    2018-01-01

    In this paper we demonstrate for the first time that a fibre laser with a wavelength of 1070 nm and a pulse width of milliseconds can be applied to generate mesoporous nanocrystalline (nc) TiO2 thin films on ITO coated glass in ambient atmosphere, by complete vaporisation of organic binder and inter-connection of TiO2 nanoparticles, without thermally damaging the ITO layer and the glass substrate. The fabrication of the mesoporous TiO2 thin films was achieved by stationary laser beam irradiation of 1 min. The dye sensitized solar cell (DSSC) with the laser-sintered TiO2 photoanode reached higher power conversion efficiency (PCE) of 3.20% for the TiO2 film thickness of 6 μm compared with 2.99% for the furnace-sintered. Electrochemical impedance spectroscopy studies revealed that the laser sintering under the optimised condition effectively decreased charge transfer resistance and increased electron lifetime of the TiO2 thin films. The use of the fibre laser with over 40% wall-plug efficiency offers an economically-feasible, industrial viable solution to the major challenge of rapid fabrication of large scale, mass production of mesoporous metal oxide thin film based solar energy systems, potentially for perovskite and monolithic tandem solar cells, in the future.

  14. Mesoscopic Oxide Double Layer as Electron Specific Contact for Highly Efficient and UV Stable Perovskite Photovoltaics.

    Science.gov (United States)

    Tavakoli, Mohammad Mahdi; Giordano, Fabrizio; Zakeeruddin, Shaik Mohammed; Grätzel, Michael

    2018-04-11

    The solar to electric power conversion efficiency (PCE) of perovskite solar cells (PSCs) has recently reached 22.7%, exceeding that of competing thin film photovoltaics and the market leader polycrystalline silicon. Further augmentation of the PCE toward the Shockley-Queisser limit of 33.5% warrants suppression of radiationless carrier recombination by judicious engineering of the interface between the light harvesting perovskite and the charge carrier extraction layers. Here, we introduce a mesoscopic oxide double layer as electron selective contact consisting of a scaffold of TiO 2 nanoparticles covered by a thin film of SnO 2 , either in amorphous (a-SnO 2 ), crystalline (c-SnO 2 ), or nanocrystalline (quantum dot) form (SnO 2 -NC). We find that the band gap of a-SnO 2 is larger than that of the crystalline (tetragonal) polymorph leading to a corresponding lift in its conduction band edge energy which aligns it perfectly with the conduction band edge of both the triple cation perovskite and the TiO 2 scaffold. This enables very fast electron extraction from the light perovskite, suppressing the notorious hysteresis in the current-voltage ( J-V) curves and retarding nonradiative charge carrier recombination. As a result, we gain a remarkable 170 mV in open circuit photovoltage ( V oc ) by replacing the crystalline SnO 2 by an amorphous phase. Because of the quantum size effect, the band gap of our SnO 2 -NC particles is larger than that of bulk SnO 2 causing their conduction band edge to shift also to a higher energy thereby increasing the V oc . However, for SnO 2 -NC there remains a barrier for electron injection into the TiO 2 scaffold decreasing the fill factor of the device and lowering the PCE. Introducing the a-SnO 2 coated mp-TiO 2 scaffold as electron extraction layer not only increases the V oc and PEC of the solar cells but also render them resistant to UV light which forebodes well for outdoor deployment of these new PSC architectures.

  15. Preparation of Fluorine-Doped TiO2 Photocatalysts with Controlled Crystalline Structure

    Directory of Open Access Journals (Sweden)

    N. Todorova

    2008-01-01

    Full Text Available Nanocrystalline F-doped TiO2 powders were prepared by sol-gel route. The thermal behavior of the powders was recorded by DTA/TG technique. The crystalline phase of the fluorinated TiO2 powders was determined by X-ray diffraction technique. It was demonstrated that F-doping using CF3COOH favors the formation of rutile along with anatase phase even at low temperature. Moreover, the rutile's phase content increases with the increase of the quantity of the fluorine precursor in the starting solution. The surface area of the powders and the pore size distribution were studied by N2 adsorption-desorption using BET and BJH methods. X-ray photoelectron spectroscopy (XPS revealed that the fluorine is presented in the TiO2 powders mainly as metal fluoride in quantities ∼16 at %. The F-doped TiO2 showed a red-shift absorption in UV-vis region which was attributed to the increased content of rutile phase in the powders. The powders exhibited enhanced photocatalytic activity in decomposition of acetone.

  16. Solution-Processed Ultrathin TiO2 Compact Layer Hybridized with Mesoporous TiO2 for High-Performance Perovskite Solar Cells.

    Science.gov (United States)

    Jeong, Inyoung; Park, Yun Hee; Bae, Seunghwan; Park, Minwoo; Jeong, Hansol; Lee, Phillip; Ko, Min Jae

    2017-10-25

    The electron transport layer (ETL) is a key component of perovskite solar cells (PSCs) and must provide efficient electron extraction and collection while minimizing the charge recombination at interfaces in order to ensure high performance. Conventional bilayered TiO 2 ETLs fabricated by depositing compact TiO 2 (c-TiO 2 ) and mesoporous TiO 2 (mp-TiO 2 ) in sequence exhibit resistive losses due to the contact resistance at the c-TiO 2 /mp-TiO 2 interface and the series resistance arising from the intrinsically low conductivity of TiO 2 . Herein, to minimize such resistive losses, we developed a novel ETL consisting of an ultrathin c-TiO 2 layer hybridized with mp-TiO 2 , which is fabricated by performing one-step spin-coating of a mp-TiO 2 solution containing a small amount of titanium diisopropoxide bis(acetylacetonate) (TAA). By using electron microscopies and elemental mapping analysis, we establish that the optimal concentration of TAA produces an ultrathin blocking layer with a thickness of ∼3 nm and ensures that the mp-TiO 2 layer has a suitable porosity for efficient perovskite infiltration. We compare PSCs based on mesoscopic ETLs with and without compact layers to determine the role of the hole-blocking layer in their performances. The hybrid ETLs exhibit enhanced electron extraction and reduced charge recombination, resulting in better photovoltaic performances and reduced hysteresis of PSCs compared to those with conventional bilayered ETLs.

  17. Nano structured TiO2 thin films by polymeric precursor method

    International Nuclear Information System (INIS)

    Stroppa, Daniel Grando; Giraldi, Tania Regina; Leite, Edson Roberto; Varela, Jose Arana; Longo, Elson

    2008-01-01

    This work focuses in optimizing setup for obtaining TiO 2 thin films by polymeric precursor route due to its advantages on stoichiometric and morphological control. Precursor stoichiometry, synthesis pH, solids concentration and rotation speed at deposition were optimized evaluating thin films morphology and thickness. Thermogravimetry and NMR were applied for precursor's characterization and AFM, XRD and ellipsometry for thin films evaluation. Results showed successful attainment of homogeneous nanocrystalline anatase TiO 2 thin films with outstanding control over morphological characteristics, mean grain size of 17 nm, packing densities between 57 and 75%, estimated surface areas of 90 m 2 /g and monolayers thickness within 20 and 128 nm. (author)

  18. NANOSTRUCTURED TiO2 SENSITIZED WITH PORPHYRINS FOR SOLAR WATER-SPLITTING

    Directory of Open Access Journals (Sweden)

    MARCELA-CORINA ROŞU

    2011-03-01

    Full Text Available Nanostructured TiO2 sensitized with porphyrins for Solar water-splitting.The production of hydrogen from water using solar light is very promising for generations of an ecologically pure carrier contributing to a clean, sustainable and renewable energy system. The selection of specific photocatalyst material for hydrogen production in photoelectrochemical cells (PECs is based on some important characteristics of semiconductor, such as photo-corrosion and chemical corrosion stability, photocatalytic potential, high sensitivity for UV-visible light. In the present paper, different nanocrystalline TiO2 photoanodes have been prepared via wet-chemical techniques followed by annealing treatment and sensitized with porphyrins and supramolecular complexes of porphyrins. The so obtained photocatalysts were characterized with UV-VIS absorption spectroscopy and spectrofluorimetry. The purpose of these experiments is to show if the prepared materials possess the necessary photocatalytic characteristics and if they can be used with success in H2 production from water decomposition in PECs.

  19. Preparation of anatase TiO2 nanoparticles using low hydrothermal temperature for dye-sensitized solar cell

    Science.gov (United States)

    Sofyan, N.; Ridhova, A.; Yuwono, A. H.; Udhiarto, A.

    2018-03-01

    One device being developed as an alternative source of renewable energy by utilizing solar energy source is dye-sensitized solar cells (DSSC). This device works using simple photosynthetic-electrochemical principle in the molecular level. In this device, the inorganic oxide semiconductor of titanium dioxide (TiO2) has a great potential for the absorption of the photon energy from the solar energy source, especially in the form of TiO2 nanoparticle structure. This nanoparticle structure is expected to improve the performance of DSSC because the surface area to weight ratio of this nanostructures is very large. In this study, the synthesis of TiO2 nanoparticle from its precursors has been performed along with the fabrication of the DSSC device. Effort to improve the size of nanocrystalline anatase TiO2 was accomplished by low hydrothermal treatment at various temperatures whereas the crystallinity of the anatase phase in the structure was performed by calcination process. Characterization of the materials was performed using X-ray Diffraction (XRD) and scanning electron microscope (SEM), while the DSSC performance was examined through a high precision current versus voltage (I-V) curve analyzer. The results showed that pure anatase TiO2 nanoparticles could be obtained at low hydrothermal of 100, 125, and 150 °C followed by calcination at 450 °C. The best performance of photocurrent-voltage characteristic was given by TiO2 hydrothermally synthesized at 150 °C with power conversion efficiency (PCE) of 4.40 %, whereas the standard TiO2 nanoparticles has PCE only 4.02 %. This result is very promising in terms low temperature and thus low cost of anatase TiO2 semiconductor preparation for DSSC application.

  20. Characterization and Comparison of Photocatalytic Activity Silver Ion doped on TiO2(TiO2/Ag+) and Silver Ion doped on Black TiO2(Black TiO2/Ag+)

    Science.gov (United States)

    Kim, Jin Yi; Sim, Ho Hyung; Song, Sinae; Noh, Yeoung Ah; Lee, Hong Woon; Taik Kim, Hee

    2018-03-01

    Titanium dioxide (TiO2) is one of the representative ceramic materials containing photocatalyst, optic and antibacterial activity. The hydroxyl radical in TiO2 applies to the intensive oxidizing agent, hence TiO2 is suitable to use photocatalytic materials. Black TiO2was prepared through reduction of amorphous TiO2 conducting under H2 which leads to color changes. Its black color is proven that absorbs 100% light across the whole-visible light, drawing enhancement of photocatalytic property. In this study, we aimed to compare the photocatalytic activity of silver ion doped on TiO2(TiO2/Ag+) and silver ion doped on black TiO2(black TiO2/Ag+) under visible light range. TiO2/Ag+ was fabricated following steps. 1) TiO2 was synthesized by a sol-gel method from Titanium tetraisopropoxide (TTIP). 2) Then AgNO3 was added during an aging process step for silver ion doping on the surface of TiO2. Moreover, Black TiO2/Ag+ was obtained same as TiO2/Ag+ except for calcination under H2. The samples were characterized X-ray diffraction (XRD), UV-visible reflectance (UV-vis DRS), and Methylene Blue degradation test. XRD analysis confirmed morphology of TiO2. The band gap of black TiO2/Ag+ was confirmed (2.6 eV) through UV-vis DRS, which was lower than TiO2/Ag+ (2.9 eV). The photocatalytic effect was conducted by methylene blue degradation test. It demonstrated that black TiO2/Ag+ had a photocatalytic effect under UV light also visible light.

  1. Chemical and electrochemical synthesis of nano-sized TiO2 anatase for large-area photon conversion

    International Nuclear Information System (INIS)

    Babasaheb, Raghunath Sankapal; Shrikrishna, Dattatraya Sartale; Lux-Steiner, M.Ch.; Ennaoui, A.

    2006-01-01

    We report on the synthesis of nanocrystalline titanium dioxide thin films and powders by chemical and electrochemical deposition methods. Both methods are simple, inexpensive and suitable for large-scale production. Air-annealing of the films and powders at T = 500 C leads to densely packed nanometer sized anatase TiO 2 particles. The obtained layers are characterized by different methods such as: X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM). Titanium dioxide TiO 2 (anatase) phase with (101) preferred orientation has been obtained for the films deposited on glass; indium doped tin oxide (ITO) and quartz substrates. The powder obtained as the byproduct consists of TiO 2 with anatase-phase as well. (authors)

  2. Preparation and solar-light photocatalytic activity of TiO2 composites: TiO2/kaolin, TiO2/diatomite, and TiO2/zeolite

    Science.gov (United States)

    Li, Y.; Li, S. G.; Wang, J.; Li, Y.; Ma, C. H.; Zhang, L.

    2014-12-01

    Three TiO2 loaded composites, TiO2/kaolin, TiO2/diatomite, and TiO2/zeolite, were prepared in order to improve the solar-light photocatalytic activity of TiO2. The results showed that the photocatalytic activity could obviously be enhanced by loading appropriate amount of inorganic mineral materials. Meanwhile, TiO2 content, heat-treatment temperature and heat-treatment time on the photocatalytic activity were reviewed. Otherwise, the effect of solar light irradiation time and dye concentration on the photocatalytic degradation of Acid Red B was investigated. Furthermore, the degradation mechanism and adsorption process were also discussed.

  3. Spontaneous and Photoinduced Conversion of CO2 on TiO2 Anatase (001)/(101) Surfaces

    Czech Academy of Sciences Publication Activity Database

    Ferus, Martin; Kavan, Ladislav; Zukalová, Markéta; Zukal, Arnošt; Klementová, Mariana; Civiš, Svatopluk

    2014-01-01

    Roč. 118, č. 46 (2014), s. 26845-26850 ISSN 1932-7447 R&D Projects: GA ČR(CZ) GAP108/12/0814; GA MŠk LD14115; GA MŠk(CZ) LD13060 Grant - others:COST(XE) CM1104 Institutional support: RVO:61388955 ; RVO:61388980 ; RVO:68081707 Keywords : TiO2 * FT-IR spectroscopy * nanocrystalline anatase Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 4.772, year: 2014

  4. Influence of nitrogen dopants on N-doped TiO2 electrodes and their applications in dye-sensitized solar cells

    International Nuclear Information System (INIS)

    Guo Wei; Shen Yihua; Boschloo, Gerrit; Hagfeldt, Anders; Ma Tingli

    2011-01-01

    Highlights: → Three different types of nanocrystalline N-doped TiO 2 synthesized by several nitrogen dopants. → N-doped DSCs achieves a high conversion efficiency of 8.32%. → Ammonia acts as good nitrogen dopants. → Enhanced photocurrent of ca. 36% in N-doped DSCs. → Less charge are needed to get a high open-circuit voltage in N-doped films. - Abstract: Three different types of nanocrystalline, N-doped TiO 2 electrodes were synthesized using several nitrogen dopants through wet methods. The obtained nanocrystalline, N-doped TiO 2 electrodes possessed different crystallite sizes, surface areas, and N-doping amounts. Characterizations were performed to reveal the nitrogen-doping processes for the wet methods using ammonia, urea, and triethylamine as the nitrogen dopants. Additionally, a high conversion efficiency of 8.32% was achieved by the dye-sensitized solar cells, based on the N-doped TiO 2 electrodes. For instance, in comparison with the commercial P25 (5.76%) and pure anatase TiO 2 electrodes (7.14%), significant improvements (44% and 17%, respectively) in the efficiencies were obtained. The findings also indicated that the ammonia nitrogen dopant was more efficient than other two nitrogen dopants. The electron transports, electron lifetimes, and charge recombination in the dye-sensitized N-doped TiO 2 solar cells also differed from those in the pure TiO 2 -based dye-sensitized solar cells (DSCs). Specifically, an enhanced photocurrent of ca. 36% in N-doped DSCs resulted from the synergistic effects of the high dye uptake and the efficient electron transport. Moreover, the relationship between charge and voltage revealed that less charge was needed to get a high open-circuit voltage in the N-doping films.

  5. Dielectric response and room temperature ferromagnetism in Cr doped anatase TiO2 nanoparticles

    Science.gov (United States)

    Naseem, Swaleha; Khan, Wasi; Khan, Shakeel; Husain, Shahid; Ahmad, Abid

    2018-02-01

    In the present work, nanocrystalline samples of Ti1-xCrxO2 (x = 0, 0.02, 0.04, 0.06 and 0.08) were synthesized in anatase phase through simple and cost effective acid modified sol gel method. The influence of Cr doping on thermal, microstructural, electrical and magnetic properties was investigated in TiO2 host matrix. The surface morphology has revealed less agglomeration and considerable reduction in particle size in case of Cr doped TiO2 as compared to undoped TiO2 nanoparticles (NPs). Energy dispersive x-ray spectroscopy (EDS), Raman and X-ray photoelectron spectroscopy (XPS) established high purity, appropriate stoichiometry and oxidation states of the compositions. The dielectric properties of the nanoparticles were altered by the doping concentration, applied frequency as well as temperature variation. The variation in dielectric constant (ε‧), dielectric loss (δ) and ac conductivity as a function of frequency and temperature at different doping concentration of Cr were interpreted in the light of Maxwell Wagner theory, space charge polarization mechanism and drift mobility of charge carriers. Both undoped and Cr doped TiO2 samples exhibit room temperature ferromagnetism (RTFM) that remarkably influenced by means of the Cr content. The significant enhancement in the magnetization was observed at 4% Cr doping. However, decrease in magnetization for higher doping signify antiferromagnetic interactions between Cr ions or superexchange mechanism. These results reveal that the oxygen vacancies play a crucial role to initiate the RTFM. Therefore, the present investigation suggests the potential applications of Cr doped TiO2 nanoparticles for spintronics application.

  6. Functionalized TiO2 nanoparticle containing isocyanate groups

    International Nuclear Information System (INIS)

    Ou, Baoli; Li, Duxin; Liu, Qingquan; Zhou, Zhihua; Liao, Bo

    2012-01-01

    Functionalized TiO 2 nanoparticle containing isocyanate groups can extend the TiO 2 nanoparticle chemistry, and may promote their many potential applications such as in polymer composites and coatings. This paper describes a facile method to prepare functionalized TiO 2 nanoparticle with highly reactive isocyanate groups on its surface, via the reaction between toluene-2, 4-diisocyanate (TDI) and hydroxyl on TiO 2 nanoparticle surface. The main effect factors on the reaction of TiO 2 with TDI were studied by determining the reaction extent of hydroxyl groups on TiO 2 surface. Fourier-transformed infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA) confirmed that reactive isocyanate groups were covalently attached to the TiO 2 nanoparticle surface. The dispersion of the TDI-functionalized TiO 2 nanoparticle was studied by transmission electron microscopy (TEM). Owing to the TDI molecules covalently bonded on TiO 2 nanoparticle surface, it was established that the TiO 2 nanoparticle can be uniformly dispersed in toluene, thus indicating that this functionalization method can prevent TiO 2 nanoparticle from agglomerating. -- Highlights: ► TiO 2 nanoparticle was functionalized with toluene-2, 4-diisocyanate. ► Functionalized TiO 2 nanoparticle can be uniformly dispersed in xylene. ► Compatibility of TiO 2 nanoparticle and organic solvent is significantly improved. ► TiO 2 containing isocyanate groups can extend the TiO 2 nanoparticle chemistry.

  7. Instability of Hydrogenated TiO2

    Energy Technology Data Exchange (ETDEWEB)

    Nandasiri, Manjula I.; Shutthanandan, V.; Manandhar, Sandeep; Schwarz, Ashleigh M.; Oxenford, Lucas S.; Kennedy, John V.; Thevuthasan, Suntharampillai; Henderson, Michael A.

    2015-11-06

    Hydrogenated TiO2 (H-TiO2) is toted as a viable visible light photocatalyst. We report a systematic study on the thermal stability of H-implanted TiO2 using X-ray photoelectron spectroscopy (XPS), ultraviolet photoelectron spectroscopy (UPS), Rutherford backscattering spectrometry (RBS) and nuclear reaction analysis (NRA). Protons (40 keV) implanted at a ~2 atom % level within a ~120 nm wide profile of rutile TiO2(110) were situated ~300 nm below the surface. NRA revealed that this H-profile broadened preferentially toward the surface after annealing at 373 K, dissipated out of the crystal into vacuum at 473 K, and was absent within the beam sampling depth (~800 nm) at 523 K. Photoemission showed that the surface was reduced in concert with these changes. Similar anneals had no effect on pristine TiO2(110). The facile bulk diffusivity of H in rutile, as well as its activity toward interfacial reduction, significantly limits the utilization of H-TiO2 as a photocatalyst. This work was supported by the US Department of Energy, Office of Science, Office of Basic Energy Sciences, Division of Chemical Sciences, Geosciences & Biosciences. Pacific Northwest National Laboratory (PNNL) is a multiprogram national laboratory operated for DOE by Battelle. The research was performed using the Environmental Molecular Sciences Laboratory (EMSL), a national scientific user facility sponsored by the Department of Energy's Office of Biological and Environmental Research and located at Pacific Northwest National Laboratory.

  8. An impact of the copper additive on photocatalytic and bactericidal properties of TiO2 thin films

    Directory of Open Access Journals (Sweden)

    Wojcieszak Damian

    2017-07-01

    Full Text Available The biological and photocatalytic activity of TiO2 and TiO2:Cu in relation to their structure, surface topography, wettability and optical properties of the thin films was investigated. Thin-film coatings were prepared by magnetron sputtering method in oxygen plasma with use of metallic targets (Ti and Ti-Cu. The results of structural studies revealed that addition of Cu into titania matrix (during the deposition process resulted in obtaining of an amorphous film, while in case of undoped TiO2, presence of nanocrystalline anatase (with crystallites size of 20 nm was found. Moreover, an addition of cooper had also an effect on surface diversification and decrease of its hydrophilicity. The roughness of TiO2:Cu film was 25 % lower (0.6 nm as-compared to titania (0.8 nm. These modifications of TiO2:Cu had an impact on the decrease of its photocatalytic activity, probably as a result of the active surface area decrease. Antibacterial and antifungal properties of the thin films against bacteria (Enterococcus hirae, Staphylococcus aureus, Bacillus subtilis, Escherichia coli and yeast (Candida albicans were also examined. For the purpose of this work the method dedicated for the evaluation of antimicrobial properties of thin films was developed. It was revealed that Cu-additive has a positive impact on neutralization of microorganisms.

  9. Influence of Nd-Doping on Photocatalytic Properties of TiO2 Nanoparticles and Thin Film Coatings

    Directory of Open Access Journals (Sweden)

    Damian Wojcieszak

    2014-01-01

    Full Text Available Structural, optical, and photocatalytic properties of TiO2 and TiO2:Nd nanopowders and thin films composed of those materials have been compared. Titania nanoparticles with 1, 3, and 6 at. % of Nd-dopant were synthesized by sol-gel method. Additionally, thin films with the same material composition were prepared with the aid of spin-coating method. The analysis of structural investigations revealed that all as-prepared nanopowders were nanocrystalline and had TiO2-anatase structure. The average size of crystallites was ca. 4-5 nm and the correlation between the amount of neodymium and the size of TiO2 crystallites was observed. It was shown that the dopant content influenced the agglomeration of the nanoparticles. The results of photocatalytic decomposition of MO showed that doping with Nd (especially in the amount of 3 at. % increased self-cleaning activity of the prepared titania nanopowder. Similar effect was received in case of the thin films, but the decomposition rate was lower due to their smaller active surface area. However, the as-prepared TiO2:Nd photocatalyst in the form of thin films or nanopowders seems to be a very attractive material for various applications.

  10. TiO2-TiO2 composite resistive humidity sensor: ethanol crosssensitivity

    International Nuclear Information System (INIS)

    Ghalamboran, Milad; Saedi, Yasin

    2016-01-01

    The fabrication method and characterization results of a TiO 2 -TiO 2 composite bead used for humidity sensing along with its negative cross-sensitivity to ethanol vapor are reported. The bead shaped resistive sample sensors are fabricated by the drop-casting of a TiO 2 slurry on two Pt wire segments. The dried bead is pre-fired at 750°C and subsequently impregnated with a Ti-based sol. The sample is ready for characterization after a thermal annealing at 600°C in air. Structurally, the bead is a composite of the micron-sized TiO 2 crystallites embedded in a matrix of nanometric TiO 2 particle aggregates. The performance of the beads as resistive humidity sensors is recorded at room temperature in standard humidity level chambers. Results evince the wide dynamic range of the sensors fabricated in the low relative humidity range. While the sensor conductance is not sensitive to ethanol vapor in dry air, in humid air, sensor's responses are negatively affected by the contaminant. (paper)

  11. Electrochemical synthesis of nanosized TiO2 nanopowder involving choline chloride based ionic liquids

    International Nuclear Information System (INIS)

    Anicai, Liana; Petica, Aurora; Patroi, Delia; Marinescu, Virgil; Prioteasa, Paula; Costovici, Stefania

    2015-01-01

    Highlights: • TiO 2 nanopowder electrochemically prepared using choline chloride based ionic liquids. • The new proposed method allowed high anodic synthesis efficiencies of minimum 92%. • High surface area of the electrochemically synthesized titania nanopowders. • Enhanced photocatalytic activity. - Abstract: The paper presents some experimental results regarding the electrochemical synthesis of TiO 2 nanopowders through anodic dissolution of Ti metal in choline chloride based eutectic mixtures (DES). A detailed characterization of the obtained titania has been performed, using various techniques, including XRD, Raman spectroscopy, XPS, SEM associated with EDX analysis, BET and UV–vis diffuse reflectance spectra. The anodic behavior of Ti electrode in DES has been also investigated. The photoreactivity of the synthesized materials was evaluated for the degradation of Orange II dye under UV (λ = 365 nm) and visible light irradiation. An anodic synthesis efficiency of minimum 92% has been determined. The as-synthesized TiO 2 showed amorphous structure and a calcination post-treatment at temperatures between 400 and 600 °C yielded anatase. The anodically obtained nanocrystalline oxides have crystallite sizes of 8–18 nm, a high surface area and enhanced photocatalytic effect

  12. Water Adsorption on TiO2

    DEFF Research Database (Denmark)

    Hammer, Bjørk; Wendt, Stefan; Besenbacher, Flemming

    2010-01-01

    Scanning Tunneling Microscopy (STM) studies and Density Functional Theory (DFT) investigations of the interaction of water with the rutile TiO2 (110) surface are summarized. From high-resolution STM the following reactions have been revealed: water adsorption and diffusion in the Ti troughs, water...... dissociation in bridging oxygen vacancies, assembly of adsorbed water monomers into rapidly diffusing water dimers, and formation of water dimers by reduction of oxygen molecules. The STM results are rationalized based on DFT calculations, revealing the bonding geometries and reaction pathways of the water...

  13. Mesoscopic pairing without superconductivity

    Science.gov (United States)

    Hofmann, Johannes

    2017-12-01

    We discuss pairing signatures in mesoscopic nanowires with a variable attractive pairing interaction. Depending on the wire length, density, and interaction strength, these systems realize a simultaneous bulk-to-mesoscopic and BCS-BEC crossover, which we describe in terms of the parity parameter that quantifies the odd-even energy difference and generalizes the bulk Cooper pair binding energy to mesoscopic systems. We show that the parity parameter can be extracted from recent measurements of conductance oscillations in SrTiO3 nanowires by Cheng et al. [Nature (London) 521, 196 (2015), 10.1038/nature14398], where it marks the critical magnetic field that separates pair and single-particle currents. Our results place the experiment in the fluctuation-dominated mesoscopic regime on the BCS side of the crossover.

  14. Remediation of Organic and Inorganic Arsenic Contaminated Groundwater using a Nonocrystalline TiO2 Based Adsorbent

    Energy Technology Data Exchange (ETDEWEB)

    Jing, C.; Meng, X; Calvache, E; Jiang, G

    2009-01-01

    A nanocrystalline TiO2-based adsorbent was evaluated for the simultaneous removal of As(V), As(III), monomethylarsonic acid (MMA), and dimethylarsinic acid (DMA) in contaminated groundwater. Batch experimental results show that As adsorption followed pseudo-second order rate kinetics. The competitive adsorption was described with the charge distribution multi-site surface complexation model (CD-MUSIC). The groundwater containing an average of 329 ?g L-1 As(III), 246 ?g L-1 As(V), 151 ?g L-1 MMA, and 202 ?g L-1 DMA was continuously passed through a TiO2 filter at an empty bed contact time of 6 min for 4 months. Approximately 11 000, 14 000, and 9900 bed volumes of water had been treated before the As(III), As(V), and MMA concentration in the effluent increased to 10 ?g L-1. However, very little DMA was removed. The EXAFS results demonstrate the existence of a bidentate binuclear As(V) surface complex on spent adsorbent, indicating the oxidation of adsorbed As(III). A nanocrystalline TiO2-based adsorbent could be used for the simultaneous removal of As(V), As(III), MMA, and DMA in contaminated groundwater.

  15. Mesoscopic CH 3 NH 3 PbI 3 /TiO 2 Heterojunction Solar Cells

    KAUST Repository

    Etgar, Lioz; Gao, Peng; Xue, Zhaosheng; Peng, Qin; Chandiran, Aravind Kumar; Liu, Bin; Nazeeruddin, Md. K.; Grä tzel, Michael

    2012-01-01

    .1 mA/cm 2, open-circuit photovoltage V oc = 0.631 V, and a fill factor FF = 0.57, corresponding to a light to electric power conversion efficiency (PCE) of 5.5% under standard AM 1.5 solar light of 1000 W/m 2 intensity. At a lower light intensity

  16. Fabrication of a TiO2-P25/(TiO2-P25+TiO2 nanotubes junction for dye sensitized solar cells

    Directory of Open Access Journals (Sweden)

    Nguyen Huy Hao

    2016-08-01

    Full Text Available The dye sensitized solar cell (DSSC, which converts solar light into electric energy, is expected to be a promising renewable energy source for today's world. In this work, dye sensitized solar cells, one containing a single layer and one containing a double layer, were fabricated. In the double layer DSSC structure, the under-layer was TiO2-P25 film, and the top layer consisted of a mixture of TiO2-P25 and TiO2 nanotubes. The results indicated that the efficiency of the DSSC with the double layer structure was a significant improvement in comparison to the DSSC consisting of only a single film layer. The addition of TiO2-P25 in the top layer caused an improvement in the adsorption of dye molecules on the film rather than on the TiO2 nanotubes only. The presence of the TiO2 nanotubes together with TiO2-P25 in the top layer revealed the enhancement in harvesting the incident light and an improvement of electron transport through the film.

  17. TiO2 beads and TiO2-chitosan beads for urease immobilization

    International Nuclear Information System (INIS)

    Ispirli Doğaç, Yasemin; Deveci, İlyas; Teke, Mustafa; Mercimek, Bedrettin

    2014-01-01

    The aim of the present study is to synthesize TiO 2 beads for urease immobilization. Two different strategies were used to immobilize the urease on TiO 2 beads. In the first method (A), urease enzyme was immobilized onto TiO 2 beads by adsorption and then crosslinking. In the second method (B), TiO 2 beads were coated with chitosan-urease mixture. To determine optimum conditions of immobilization, different parameters were investigated. The parameters of optimization were initial enzyme concentration (0.5; 1; 1.5; 2 mg/ml), alginate concentration (1; 2; 3%), glutaraldehyde concentration (1; 2; 3% v/v) and chitosan concentration (2; 3; 4 mg/ml). The optimum enzyme concentrations were determined as 1.5 mg/ml for A and 1.0 mg/ml for B. The other optimum conditions were found 2.0% (w/v) for alginate concentration (both A and B); 3.0 mg/ml for chitosan concentration (B) and 2.0% (v/v) for glutaraldehyde concentration (A). The optimum temperature (20-60 °C), optimum pH (3.0-10.0), kinetic parameters, thermal stability (4–70 °C), pH stability (4.0-9.0), operational stability (0-230 min) and reusability (20 times) were investigated for characterization. The optimum temperatures were 30 °C (A), 40 °C (B) and 35 °C (soluble). The temperature profiles of the immobilized ureases were spread over a large area. The optimum pH values for the soluble urease and immobilized urease prepared by using methods (A) and (B) were found to be 7.5, 7.0, 7.0, respectively. The thermal stabilities of immobilized enzyme sets were studied and they maintained 50% activity at 65 °C. However, at this temperature free urease protected only 15% activity. - Highlights: • TiO 2 and TiO 2 -chitosan beads for urease immobilization have been prepared and characterized. • The beads used in this work are good matrices for the immobilization of urease. • The immobilized urease was shown to have good properties and stabilities (pH and thermal stability, operational stability). • The 50% activity was protected after 11 cycles for method A and 16 cycles for method B

  18. Applications of mesoscopic physics

    International Nuclear Information System (INIS)

    Feng, Shechao.

    1993-01-01

    Research activities in the area ''applications of mesoscopic physics to novel correlations and fluctuations of speckle patterns: imaging and tomography with multiply scattered classical waves'' are briefly summarized. The main thrust in fundamental research is in the general areas of mesoscopic effects in disordered semiconductors and metals and the related field of applications of mesoscopic physics to the subject matter of classical wave propagation through disordered scattering media. Specific topics are Fabry-Perot interferometer with disorder: correlations and light localization; electron-phonon inelastic scattering rate and the temperature scaling exponent in integer quantum Hall effect; and transmission and reflection correlations of second harmonic waves in nonlinear random media. Research in applied physics centered on far infrared photon-assisted transport through quantum point contact devices and photon migration distributions in multiple scattering media. 7 refs

  19. Controlled Directional Growth of TiO2 Nanotubes

    DEFF Research Database (Denmark)

    In, Su-il; Hou, Yidong; Abrams, Billie

    2010-01-01

    We demonstrate how the anodization direction and growth rate of vertically aligned, highly ordered TiO2 nanotube (NT) arrays can be controlled and manipulated by the local concentration of O-2 in the electrolyte. This leads to the growth of highly active TiO2 NT arrays directly on nonconducting s...

  20. Silicon protected with atomic layer deposited TiO2

    DEFF Research Database (Denmark)

    Seger, Brian; Tilley, S. David; Pedersen, Thomas

    2013-01-01

    The present work demonstrates that tuning the donor density of protective TiO2 layers on a photocathode has dramatic consequences for electronic conduction through TiO2 with implications for the stabilization of oxidation-sensitive catalysts on the surface. Vacuum annealing at 400 °C for 1 hour o...

  1. Preparation, characterization and photocatalytic activity of TiO2 ...

    Indian Academy of Sciences (India)

    Photocatalyst; TiO2 nanoparticle; polyaniline; conducting polymer; core-shell nanocomposite. 1. Introduction ..... tine TiO2 nanoparticles, HCl-doped PANI and PANI/TiO2 ..... Karim M R, Lim K T, Lee M S, Kim K and Yeum J H 2009 Synth. Met.

  2. New Hybrid Properties of TiO2 Nanoparticles Surface Modified With Catecholate Type Ligands

    Directory of Open Access Journals (Sweden)

    Džunuzović Enis

    2009-01-01

    Full Text Available Abstract Surface modification of nanocrystalline TiO2 particles (45 Å with bidentate benzene derivatives (catechol, pyrogallol, and gallic acid was found to alter optical properties of nanoparticles. The formation of the inner-sphere charge–transfer complexes results in a red shift of the semiconductor absorption compared to unmodified nanocrystallites. The binding structures were investigated by using FTIR spectroscopy. The investigated ligands have the optimal geometry for chelating surface Ti atoms, resulting in ring coordination complexes (catecholate type of binuclear bidentate binding–bridging thus restoring in six-coordinated octahedral geometry of surface Ti atoms. From the Benesi–Hildebrand plot, the stability constants at pH 2 of the order 103 M−1 have been determined.

  3. Optimized nanostructured TiO2 photocatalysts

    Science.gov (United States)

    Topcu, Selda; Jodhani, Gagan; Gouma, Pelagia

    2016-07-01

    Titania is the most widely studied photocatalyst. In it’s mixed-phase configuration (anatase-rutile form) -as manifested in the commercially available P25 Degussa material- titania was previously found to exhibit the best photocatalytic properties reported for the pure system. A great deal of published research by various workers in the field have not fully explained the underlying mechanism for the observed behavior of mixed-phase titania photocatalysts. One of the prevalent hypothesis in the literature that is tested in this work involves the presence of small, active clusters of interwoven anatase and rutile crystallites or “catalytic “hot-spots””. Therefore, non-woven nanofibrous mats of titania were produced and upon calcination the mats consisted of nanostructured fibers with different anatase-rutile ratios. By assessing the photocatalytic and photoelectrochemical properties of these samples the optimized photocatalyst was determined. This consisted of TiO2 nanostructures annealed at 500˚C with an anatase /rutile content of 90/10. Since the performance of this material exceeded that of P25 complete structural characterization was employed to understand the catalytic mechanism involved. It was determined that the dominant factors controlling the photocatalytic behavior of the titania system are the relative particle size of the different phases of titania and the growth of rutile laths on anatase grains which allow for rapid electron transfer between the two phases. This explains how to optimize the response of the pure system.

  4. Oriented epitaxial TiO2 nanowires for water splitting

    Science.gov (United States)

    Hou, Wenting; Cortez, Pablo; Wuhrer, Richard; Macartney, Sam; Bozhilov, Krassimir N.; Liu, Rong; Sheppard, Leigh R.; Kisailus, David

    2017-06-01

    Highly oriented epitaxial rutile titanium dioxide (TiO2) nanowire arrays have been hydrothermally grown on polycrystalline TiO2 templates with their orientation dependent on the underlying TiO2 grain. Both the diameter and areal density of the nanowires were tuned by controlling the precursor concentration, and the template surface energy and roughness. Nanowire tip sharpness was influenced by precursor solubility and diffusivity. A new secondary ion mass spectrometer technique has been developed to install additional nucleation sites in single crystal TiO2 templates and the effect on nanowire growth was probed. Using the acquired TiO2 nanowire synthesis knowhow, an assortment of nanowire arrays were installed upon the surface of undoped TiO2 photo-electrodes and assessed for their photo-electrochemical water splitting performance. The key result obtained was that the presence of short and dispersed nanowire arrays significantly improved the photocurrent when the illumination intensity was increased from 100 to 200 mW cm-2. This is attributed to the alignment of the homoepitaxially grown nanowires to the [001] direction, which provides the fastest charge transport in TiO2 and an improved pathway for photo-holes to find water molecules and undertake oxidation. This result lays a foundation for achieving efficient water splitting under conditions of concentrated solar illumination.

  5. Enhanced visible-light activities for PEC water reduction of CuO nanoplates by coupling with anatase TiO2 and mechanism

    International Nuclear Information System (INIS)

    Li, Zhijun; Qu, Yang; He, Guangwen; Humayun, Muhammad; Chen, Shuangying; Jing, Liqiang

    2015-01-01

    Graphical abstract: - Highlights: • CuO nanoplates were successfully prepared as photocathodes for PEC water reduction. • Visible-light activity for PEC water reduction is improved after coupling with TiO 2 . • Improved PEC performance is attributed to the enhanced visible-excited charge separation. • Enhanced charge separation results from high-energy electron transfer from CuO to TiO 2 . - Abstract: CuO nanoplates were prepared by a feasible hydrothermal method, and then utilized as photocathodes for photoelectrochemical (PEC) water reduction in a neutral medium under visible-light irradiation. It is clearly demonstrated that the visible-light activities of the resulting nanoplates for PEC water reduction could be greatly improved after coupling with a proper amount of nanocrystalline anatase TiO 2 . This is attributed to the enhanced charge separation in the fabricated TiO 2 /CuO nanoplate composites mainly based on the atmosphere-controlled steady-state surface photovoltage spectra. Moreover, it is suggested that the enhanced charge separation resulted from the transfer of visible-light-excited high-energy electrons from CuO to TiO 2 as confirmed from the single-wavelength PEC behavior

  6. Mesoscopic photon heat transistor

    DEFF Research Database (Denmark)

    Ojanen, T.; Jauho, Antti-Pekka

    2008-01-01

    We show that the heat transport between two bodies, mediated by electromagnetic fluctuations, can be controlled with an intermediate quantum circuit-leading to the device concept of a mesoscopic photon heat transistor (MPHT). Our theoretical analysis is based on a novel Meir-Wingreen-Landauer-typ......We show that the heat transport between two bodies, mediated by electromagnetic fluctuations, can be controlled with an intermediate quantum circuit-leading to the device concept of a mesoscopic photon heat transistor (MPHT). Our theoretical analysis is based on a novel Meir......-Wingreen-Landauer-type of conductance formula, which gives the photonic heat current through an arbitrary circuit element coupled to two dissipative reservoirs at finite temperatures. As an illustration we present an exact solution for the case when the intermediate circuit can be described as an electromagnetic resonator. We discuss...

  7. Improved efficiency of dye-sensitized solar cells by doping of strontium aluminate phosphor in TiO2 photoelectrode

    Directory of Open Access Journals (Sweden)

    Hwangbo Seung

    2015-06-01

    Full Text Available SrAl2O4:Eu2+, Dy3+ phosphor was synthesized by chemical solution route to use as a dopant in TiO2 layer employed as a photoelectrode for down conversion of ultraviolet and near-ultraviolet to visible and near-infrared light in a dye-sensitized solar cell. Nano-crystalline structure of the SrAl2O4:Eu2+, Dy3+ powder was confirmed by X-ray diffraction analysis and field emission scanning electron microscopy. Monitored at 520 nm, SrAl2O4:Eu2+, Dy3+ phosphor showed emission peaks at 460 to 610 nm due to 4f6 4f7 transitions of Eu2+ ions. For the study, SrAl2O4:Eu2+, Dy3+ phosphor-doped TiO2 layer was deposited on fluorine-doped tin oxide coated glass by electrostatic spray deposition. The short circuit current, open circuit voltage, fill factor, and conversion efficiency of the cells were measured. Experimental results revealed that the device efficiency for the SrAl2O4:Eu2+, Dy3+ phosphor-doped TiO2 layer increased to 7.20 %, whereas that of the pure-TiO2 photoelectrode was 4.13 %.

  8. Fabrication and Characteristics of Macroporous TiO2 Photocatalyst

    Directory of Open Access Journals (Sweden)

    Guiyun Yi

    2014-01-01

    Full Text Available Macroporous TiO2 photocatalyst was synthesized by a facile nanocasting method using polystyrene (PS spherical particles as the hard template. The synthesized photocatalyst was characterized by transmission electron microscope (TEM, scanning electron microscopy (SEM, thermogravimetry-differential thermogravimetry (TG-DTG, X-ray diffraction (XRD, and N2-sorption. TEM, SEM, and XRD characterizations confirmed that the macroporous TiO2 photocatalyst is composed of anatase phase. The high specific surface area of 87.85 m2/g can be achieved according to the N2-sorption analysis. Rhodamine B (RhB was chosen as probe molecule to evaluate the photocatalytic activity of the TiO2 catalysts. Compared with the TiO2 materials synthesized in the absence of PS spherical template, the macroporous TiO2 photocatalyst sintered at 500°C exhibits much higher activity on the degradation of RhB under the UV irradiation, which can be assigned to the well-structured macroporosity. The macroporous TiO2 material presents great potential in the fields of environmental remediation and energy conversion and storage.

  9. High pressure synthesis of amorphous TiO2 nanotubes

    Directory of Open Access Journals (Sweden)

    Quanjun Li

    2015-09-01

    Full Text Available Amorphous TiO2 nanotubes with diameters of 8-10 nm and length of several nanometers were synthesized by high pressure treatment of anatase TiO2 nanotubes. The structural phase transitions of anatase TiO2 nanotubes were investigated by using in-situ high-pressure synchrotron X-ray diffraction (XRD method. The starting anatase structure is stable up to ∼20GPa, and transforms into a high-density amorphous (HDA form at higher pressure. Pressure-modified high- to low-density transition was observed in the amorphous form upon decompression. The pressure-induced amorphization and polyamorphism are in good agreement with the previous results in ultrafine TiO2 nanoparticles and nanoribbons. The relationship between the LDA form and α-PbO2 phase was revealed by high-resolution transmission electron microscopy (HRTEM study. In addition, the bulk modulus (B0 = 158 GPa of the anatase TiO2 nanotubes is smaller than those of the corresponding bulks and nanoparticles (180-240 GPa. We suggest that the unique open-ended nanotube morphology and nanosize play important roles in the high pressure phase transition of TiO2 nanotubes.

  10. The effect of TiO2 on nucleation and crystallization of a Li2O-Al2O3-SiO2 glass investigated by XANES and STEM.

    Science.gov (United States)

    Kleebusch, Enrico; Patzig, Christian; Krause, Michael; Hu, Yongfeng; Höche, Thomas; Rüssel, Christian

    2018-02-13

    Glass ceramics based on Li 2 O/Al 2 O 3 /SiO 2 are of high economic importance, as they often show very low coefficients of thermal expansion. This enables a number of challenging applications, such as cooktop panels, furnace windows or telescope mirror blanks. Usually, the crystallization of the desired LAS crystal phases within the glasses must be tailored by a careful choice of crystallization schedule and type of nucleation agents to be used. The present work describes the formation of nanocrystalline TiO 2 within an LAS base composition that contains solely TiO 2 as nucleating agent. Using a combination of scanning transmission electron microscopy as well as X-ray absorption spectroscopy, it is found that a mixture of four- and six-fold coordinated Ti 4+ ions exists already within the glass. Heating of the glass to 740 °C immediately changes this ratio towards a high content of six-fold coordinated Ti, which accumulates in liquid-liquid phase-separation droplets. During the course of thermal treatment, these droplets eventually evolve into nanocrystalline TiO 2 precipitations, in which Ti 4+ is six-fold coordinated. Thus, it is shown that the nucleation of nanocrystalline TiO 2 is initiated by a gradual re-arrangement of the Ti ions in the amorphous, glassy matrix, from a four-fold towards a six-fold coordination.

  11. TiO2-ITO and TiO2-ZnO nanocomposites: application on water treatment

    Directory of Open Access Journals (Sweden)

    Bessais B.

    2012-06-01

    Full Text Available One of the most promising ideas to enhance the photocatalytic efficiency of the TiO2 is to couple this photocatalyst with other semiconductors. In this work, we report on the development of photo-catalytic properties of two types of composites based on TiO2 – ITO (Indium Tin Oxide and TiO2 – ZnO deposited on conventional ceramic substrates. The samples were characterized by X-ray diffraction (XRD and transmission Electron Microscopy (TEM. The photo-catalytic test was carried out under UV light in order to reduce/oxidize a typical textile dye (Cibacron Yellow. The experiment was carried out in a bench scale reactor using a solution having a known initial dye concentration. After optimization, we found that both nanocomposites exhibit better photocatalytic activity compared to the standard photocatalyst P25 TiO2.

  12. Electro-spray deposition of a mesoporous TiO2 charge collection layer: toward large scale and continuous production of high efficiency perovskite solar cells.

    Science.gov (United States)

    Kim, Min-cheol; Kim, Byeong Jo; Yoon, Jungjin; Lee, Jin-wook; Suh, Dongchul; Park, Nam-gyu; Choi, Mansoo; Jung, Hyun Suk

    2015-12-28

    The spin-coating method, which is widely used for thin film device fabrication, is incapable of large-area deposition or being performed continuously. In perovskite hybrid solar cells using CH(3)NH(3)PbI(3) (MAPbI(3)), large-area deposition is essential for their potential use in mass production. Prior to replacing all the spin-coating process for fabrication of perovskite solar cells, herein, a mesoporous TiO(2) electron-collection layer is fabricated by using the electro-spray deposition (ESD) system. Moreover, impedance spectroscopy and transient photocurrent and photovoltage measurements reveal that the electro-sprayed mesoscopic TiO(2) film facilitates charge collection from the perovskite. The series resistance of the perovskite solar cell is also reduced owing to the highly porous nature of, and the low density of point defects in, the film. An optimized power conversion efficiency of 15.11% is achieved under an illumination of 1 sun; this efficiency is higher than that (13.67%) of the perovskite solar cell with the conventional spin-coated TiO(2) films. Furthermore, the large-area coating capability of the ESD process is verified through the coating of uniform 10 × 10 cm(2) TiO(2) films. This study clearly shows that ESD constitutes therefore a viable alternative for the fabrication of high-throughput, large-area perovskite solar cells.

  13. Nanocrystalline solids

    International Nuclear Information System (INIS)

    Gleiter, H.

    1991-01-01

    Nanocrystalline solids are polycrystals, the crystal size of which is a few (typically 1 to 10) nanometres so that 50% or more of the solid consists of incoherent interfaces between crystals of different orientations. Solids consisting primarily of internal interfaces represent a separate class of atomic structures because the atomic arrangement formed in the core of an interface is known to be an arrangement of minimum energy in the potential field of the two adjacent crystal lattices with different crystallographic orientations on either side of the boundary core. These boundary conditions result in atomic structures in the interfacial cores which cannot be formed elsewhere (e.g. in glasses or perfect crystals). Nanocrystalline solids are of interest for the following four reasons: (1) Nanocrystalline solids exhibit an atomic structure which differs from that of the two known solid states: the crystalline (with long-range order) and the glassy (with short-range order). (2) The properties of nanocrystalline solids differ (in some cases by several orders of magnitude) from those of glasses and/or crystals with the same chemical composition, which suggests that they may be utilized technologically in the future. (3) Nanocrystalline solids seem to permit the alloying of conventionally immiscible components. (4) If small (1 to 10 nm diameter) solid droplets with a glassy structure are consolidated (instead of small crystals), a new type of glass, called nanoglass, is obtained. Such glasses seem to differ structurally from conventional glasses. (orig.)

  14. ??????????? ??????????????? ????? ??????-???????? ????????????? ?????????? ??????? ?aO?Al2O3?TiO2 ??? ???????? ?????? ?????

    OpenAIRE

    ???????, ????; ??????, ?????????

    2011-01-01

    ? ????? ?????? ?????????? ???????? ?????????????? ??????????? ????????????? ??? ??????-????????? ???????????????? ?????????? ??????? ?aO?Al2O3?TiO2, ?? ???????? ??????? ? ???????????? ??????? ??? ???????? ? ?????? ????????? ?????? ?????. ???????? ?????????? ???????? ??? ??????????? ?????????? ??????? ????????? ???????????? ?????????? ??? ??????????? 12000?, ?? ????????? ?????????????? ????????????? ???????, ????????? ???? ? ?????????? ????? ???????? ??????? ???????????. ????????, ?? ?? ...

  15. Mesoscopic phenomena in solids

    CERN Document Server

    Altshuler, BL; Webb, RA

    1991-01-01

    The physics of disordered systems has enjoyed a resurgence of interest in the last decade. New concepts such as weak localization, interaction effects and Coulomb gap, have been developed for the transport properties of metals and insulators. With the fabrication of smaller and smaller samples and the routine availability of low temperatures, new physics has emerged from the studies of small devices. The new field goes under the name ""mesoscopic physics"" and has rapidly developed, both experimentally and theoretically. This book is designed to review the current status of the field.

  16. Thermal degradation of TiO2 nanotubes on titanium

    Science.gov (United States)

    Shivaram, Anish; Bose, Susmita; Bandyopadhyay, Amit

    2014-10-01

    The objective of this research was to study thermal degradation behavior of TiO2 nanotubes on titanium (Ti). TiO2 nanotubes were grown via anodization method on commercially pure Ti (Cp-Ti) discs using two different electrolytes, 1 vol. % HF in deionized (DI) water and 1 vol. % HF + 0.5 wt. % NH4F + 10 vol. % DI water in ethylene glycol, to obtain nanotubes with two different lengths, 300 nm and 950 nm keeping the nanotube diameter constant at 100 ± 20 nm. As grown TiO2 nanotubes were subjected to heat treatment to understand thermal degradation as a function of both temperature and hold time. The signs of degradation were observed mainly when amorphous nanotubes started to crystallize, however the crystallization temperature varied based on TiO2 nanotubes length and anodizing condition. Overall, 300 nm nanotubes were thermally stable at least up to 400 °C for 12 h, while the 950 nm long nanotubes show signs of degradation from 400 °C for 6 h only. Clearly, length of nanotubes, heat treatment temperature as well as hold times show influence toward degradation kinetics of TiO2 nanotubes on titanium.

  17. Influence of TiCl4 post-treatment condition on TiO2 electrode for enhancement photovoltaic efficiency of dye-sensitized solar cells.

    Science.gov (United States)

    Eom, Tae Sung; Kim, Kyung Hwan; Bark, Chung Wung; Choi, Hyung Wook

    2014-10-01

    Titanium tetrachloride (TiCl4) treatment processed by chemical bath deposition is usually adopted as pre- and post-treatment for nanocrystalline titanium dioxide (TiO2) film deposition in the dye-sensitized solar cells (DSSCs) technology. TiCl4 post-treatment is a widely known method capable of improving the performance of dye-sensitized solar cells. In this work, the effect of TiCl4 post-treatment on the TiO2 electrode is proposed and compared to the untreated film. A TiO2 passivating layer was deposited on FTO glass by RF magnetron sputtering. The TiO2 sol prepared sol-gel method, nanoporous TiO2 upper layer was deposited by screen printing method on the passivating layer. TiCl4 post-treatment was deposited on the substrate by hydrolysis of TiCl4 aqueous solution. Crystalline structure was adjusted by various TiCl4 concentration and dipping time: 20 mM-150 mM and 30 min-120 min. The conversion efficiency was measured by solar simulator (100 mW/cm2). The dye-sensitized solar cell using TiCl4 post-treatment was measured the maximum conversion efficiency of 5.04% due to electron transport effectively. As a result, the DSSCs based on TiCl4 post-treatment showed better photovoltaic performance than cells made purely of TiO2 nanoparticles. The relative DSSCs devices are characterized in terms of short circuit current density, open circuit voltage, fill factor, conversion efficiency.

  18. Xanes and SR-XRF Study of Skin as a Barrier to Ultra-Fine Nanocrystals of TiO2

    International Nuclear Information System (INIS)

    Kwiatek, W.M.; Lekki, J.; Stachura, Z.; Hanson, A.; Ablett, J.

    2007-01-01

    Nanocrystalline TiO 2 is commonly used in cosmetic industry as a photoprotective agent. With recent advances in nanomaterial processing, the size of TiO 2 crystals decreased into the nanometre regime. There is no satisfactory evidence that crystals of such small size are harmless to the human population. An EU project NANODERM has been launched where several techniques have been applied to investigate the possibility of particle penetration through the protective horny layer into vital skin regions. Skin biopsies of the animal and human skin have been collected after exposition to formulations containing TiO 2 nanocrystals. The Ti depth distributions were measured by electron and ion microscopy. The microscopy studies did not detect penetration into vital tissue of healthy skin what does not exclude a possibility that TiO 2 could penetrate pathological skin with lowered barrier efficiency. Due to literature the physical effect of the UV irradiation of the TiO 2 nanoparticle is the shift from 4 th to 3 rd oxidation state of the Ti. Titanium at 3 rd oxidation state interact with environment producing free radicals and Reactive Oxygen Species. In order to quantify the oxidation state shift, XANES experiments were carried out with commercially available TiO 2 nanocrystals (6 - 100 nm size), both in anatase and rutile phase. The samples were irradiated with X-rays with, and without accompanying UV illumination at the NSLS X27A beam line. The corresponding XANES spectra were registered and the absorption edge was compared in UV - illuminated and not illuminated spectra. A shift of about 1 eV in the absorption edge position of the rutile sample exposed to UVA light (365 nm, 20 mW/cm 2 ) has been measured and attributed to the changed electron configuration. However, the direction of the shift detected in measured samples was opposite to the expected. (author)

  19. Synthesis, characterization, and photocatalytic properties of core/shell mesoporous silica nanospheres supporting nanocrystalline titania

    International Nuclear Information System (INIS)

    Cendrowski, K.; Chen, X.; Zielinska, B.; Kalenczuk, R. J.; Rümmeli, M. H.; Büchner, B.; Klingeler, R.; Borowiak-Palen, E.

    2011-01-01

    The facile bulk synthesis of silica nanospheres makes them an attractive support for the transport of chemical compounds such as nanocrystalline titanium dioxide. In this contribution we present a promising route for the synthesis of mesoporous silica nanospheres (m-SiO 2 ) with diameter in range 200 nm, which are ideal supports for nanocrystalline titanium dioxide (TiO 2 ). The detailed microscopic and spectroscopic characterizations of core/shell structure (m-SiO 2 /TiO 2 ) were conducted. Moreover, the photocatalytic potential of the nanostructures was investigated via phenol decomposition and hydrogen generation. A clear enhancement of photoactivity in both reactions as compared to commercial TiO 2 -Degussa P25 catalyst is detected.

  20. Synthesis, characterization, and photocatalytic properties of core/shell mesoporous silica nanospheres supporting nanocrystalline titania

    Science.gov (United States)

    Cendrowski, K.; Chen, X.; Zielinska, B.; Kalenczuk, R. J.; Rümmeli, M. H.; Büchner, B.; Klingeler, R.; Borowiak-Palen, E.

    2011-11-01

    The facile bulk synthesis of silica nanospheres makes them an attractive support for the transport of chemical compounds such as nanocrystalline titanium dioxide. In this contribution we present a promising route for the synthesis of mesoporous silica nanospheres (m-SiO2) with diameter in range 200 nm, which are ideal supports for nanocrystalline titanium dioxide (TiO2). The detailed microscopic and spectroscopic characterizations of core/shell structure (m-SiO2/TiO2) were conducted. Moreover, the photocatalytic potential of the nanostructures was investigated via phenol decomposition and hydrogen generation. A clear enhancement of photoactivity in both reactions as compared to commercial TiO2-Degussa P25 catalyst is detected.

  1. Dynamic theory for the mesoscopic electric circuit

    International Nuclear Information System (INIS)

    Chen Bin; Shen Xiaojuan; Li Youquan; Sun LiLy; Yin Zhujian

    2005-01-01

    The quantum theory for mesoscopic electric circuit with charge discreteness is briefly described. The minibands of quasienergy in LC design mesoscopic electric circuit have been found. In the mesoscopic 'pure' inductance design circuit, just like in the mesoscopic metallic rings, the quantum dynamic characteristics have been obtained explicitly. In the 'pure' capacity design circuit, the Coulomb blockade had also been addressed

  2. Synthesis of titanate, TiO2 (B), and anatase TiO2 nanofibers from natural rutile sand

    International Nuclear Information System (INIS)

    Pavasupree, Sorapong; Suzuki, Yoshikazu; Yoshikawa, Susumu; Kawahata, Ryoji

    2005-01-01

    Titanate nanofibers were synthesized by hydrothermal method (150 deg. C for 72 h) using natural rutile sand as the starting materials. TiO 2 (B) and anatase TiO 2 (high crystallinity) nanofibers with the diameters of 20-100 nm and the lengths of 10-100 μm were obtained by calcined titanate nanofibers for 4 h at 400 and 700 deg. C (in air), respectively. The samples characterized by XRD, SEM, TEM, SAED, HRTEM, and BET surface area. This synthesis method provides a simple route to fabricate one-dimensional nanostructured TiO 2 from low cost material. -- Graphical abstract: Titanate nanofibers (b) were synthesized by hydrothermal method (150 deg. C for 72 h) using natural rutile sand (a) as the starting materials. TiO 2 (B) (c) and anatase TiO 2 (d) nanofibers with the diameters of 20-50 nm and the lengths of 10-100 μm were obtained by calcined titanate nanofibers for 4 h at 400 deg. C and 700 deg. C (in air), respectively

  3. Effect of TiO2 on the Gas Sensing Features of TiO2/PANi Nanocomposites

    Directory of Open Access Journals (Sweden)

    Duong Ngoc Huyen

    2011-02-01

    Full Text Available A nanocomposite of titanium dioxide (TiO2 and polyaniline (PANi was synthesized by in-situ chemical polymerization using aniline (ANi monomer and TiCl4 as precursors. SEM pictures show that the nanocomposite was created in the form of long PANi chains decorated with TiO2 nanoparticles. FTIR, Raman and UV-Vis spectra reveal that the PANi component undergoes an electronic structure modification as a result of the TiO2 and PANi interaction. The electrical resistor of the nanocomposite is highly sensitive to oxygen and NH3 gas, accounting for the physical adsorption of these gases. A nanocomposite with around 55% TiO2 shows an oxygen sensitivity of 600–700%, 20–25 times higher than that of neat PANi. The n-p contacts between TiO2 nanoparticles and PANi matrix give rise to variety of shallow donors and acceptor levels in the PANi band gap which enhance the physical adsorption of gas molecules.

  4. Influence of Ce Doping on the Electrical and Optical Properties of TiO2 and Its Photocatalytic Activity for the Degradation of Remazol Brilliant Blue R

    Directory of Open Access Journals (Sweden)

    Aisha Malik

    2013-01-01

    Full Text Available Nanocrystalline TiO2 particles doped with different concentrations of Cerium (Ce, 1–10% have been synthesized using sol-gel method. The prepared particles were characterized by standard analytical techniques such as X-ray diffraction (XRD, FTIR and Scanning Electron Microscopy (SEM, and Transmission Electron Microscopy (TEM. The XRD analysis shows no change in crystal structure of TiO2 after doping with different concentrations of Ce, which indicates the single-phase polycrystalline material. The SEM analysis shows the partial crystalline nature of undoped, and doped TiO2 and TEM analysis shows the particle sizes were in the range of 9–14 nm in size. The a.c. analysis shows that the dielectric constant ε and dielectric loss tan δ decrease with the increase in frequency. The dielectric property decreases with the increase in dopant concentration. It is also observed that the impedance increases with an increase in dopant concentration. The photocatalytic activity of the synthesized particles (Ce-doped TiO2 with dopant concentration of 9% (Ce showed the highest photocatalytic activity for the degradation of the dye derivative Remazol Brilliant Blue R in an immersion well photochemical reactor with 500 W halogen linear lamp in the presence of atmospheric oxygen.

  5. Study of Dye-Sensitized Solar Cells by Scanning Electron Micrograph Observation and Thickness Optimization of Porous TiO2 Electrodes

    Directory of Open Access Journals (Sweden)

    Seigo Ito

    2009-01-01

    Full Text Available In order to improve the photoenergy conversion efficiency of dye-sensitized solar cells (DSCs, it is important to optimize their porous TiO2 electrodes. This paper examines the surface and cross-sectional views of the electrodes using scanning electron micrography. Two types of samples for cross-sectional viewing were prepared by mechanically breaking the substrate and by using an Ar-ion etching beam. The former displays the surface of the TiO2 particles and the latter shows the cross-section of the TiO2 particles. We found interesting surface and cross-sectional structures in the scattering layer containing the 400 nm diameter particles, which have an angular and horned shape. The influence of TiO2 particle size and the thickness of the nanocrystalline-TiO2 electrode in DSCs using four kinds of sensitizing dyes (D149, K19, N719 and Z907 and two kinds of electrolytes (acetonitrile-based and ionic-liquid electrolytes are discussed in regards to conversion efficiency, which this paper aims to optimize.

  6. Photocatalytic activity of Ti3+ self-doped dark TiO2 ultrafine nanorods, grey SiO2 nanotwin crystalline, and their composite under visible light

    Science.gov (United States)

    Zhang, Renhui; Yang, Yingchang; Leng, Senlin; Wang, Qing

    2018-04-01

    Efficient electron-holes separation is of crucial importance for the improvement of photocatalytic activity for photocatalytic reaction. In this work, dark TiO2 (D-TiO2) nanorods, grey SiO2 (G-SiO2) and D-TiO2/G-SiO2 composite with surface defects are synthesized. We report that the efficiency of photo-generated electrons and holes separation is well enhanced by introducing G-SiO2 into D-TiO2 lattice. Using first-principles method, we find that surface defects (O or Si vacancy) can be conducive to improving the optical absorption under visible-light region. Combination of the experimental results, for D-TiO2/G-SiO2 composite, the surface defects of TiO2 nanocrystallines can significantly improve the photocatalytic efficiency.

  7. Study on the use of TiO2 passivation layer to reduce recombination losses in dye sensitized solar cells

    International Nuclear Information System (INIS)

    Eskander bin Samsudin, Adel; Mohamed, Norani Muti; Nayan, Nafarizal; Ali, Riyaz Ahmad Mohamed; Shariffuddin, Sharifah Amira Amir; Omar, Salwa

    2012-01-01

    A lot of research on various aspects of dye solar cells (DSC) has been carried out in order to improve efficiency. This paper analyzes the utilization of TiO 2 passivation layers of different thicknesses by improving the electron transport properties. Four different thicknesses of passivation layers namely 10, 20, 50 and 100 nm were deposited onto the working electrode using r.f sputtering. The electrodes were assembled into TiO 2 based DSC with active area of 1 cm 2 . The solar performance was investigated using 100 mW/cm 2 of AM 1.5 simulated sunlight from solar simulator. The kinetics of the solar cells was investigated using Electrochemical Impedance Spectroscopy (EIS) measurement and the spectral response was measured using Incident Photon to Electron Conversion (IPCE) measurement system. The highest efficiency was found for DSC with 20 nm passivation layer. DSCs with the passivation layer have open circuit voltage, V OC increased by 57 mV, their current density, J SC increased by 0.774 mA cm −2 compared to the one without the passivation layer. The quantum efficiency of the 20 nm passivation layer is the highest, peaking at the wavelength of 534 nm, resulting in the highest performance. All DSCs with the passivation layer recorded higher ratio of R BR /R T where R T is the diffusion resistance of the TiO 2 particles in the mesoscopic layer and R BR is the recombination resistance of the electron to the electrolyte. This implies that the recombination of the electrolyte I − 3 /3I − couple at the substrate/electrolyte interface has been effectively reduced resulting in an enhanced efficiency.

  8. Universal mesoscopic conductance fluctuations

    International Nuclear Information System (INIS)

    Evangelou, S.N.

    1992-01-01

    The theory of conductance fluctuations in disordered metallic systems with size large compared to the mean free path of the electron but small compared to localization length is considered. It is demonstrates that fluctuations have an universal character and are due to repulsion between levels and spectral rigidity. The basic fluctuation measures for the energy spectrum in the mesoscopic regime of disordered systems are consistent with the Gaussian random matrix ensemble predictions. Although our disordered electron random matrix ensemble does not belong to the Gaussian ensemble the two ensembles turn out to be essentially similar. The level repulsion and the spectral rigidity found in nuclear spectra should also be observed in the metallic regime of Anderson localization. 7 refs. (orig.)

  9. Photocatalytic Degradation of Methylene Blue under UV Light Irradiation on Prepared Carbonaceous TiO2

    Directory of Open Access Journals (Sweden)

    Zatil Amali Che Ramli

    2014-01-01

    Full Text Available This study involves the investigation of altering the photocatalytic activity of TiO2 using composite materials. Three different forms of modified TiO2, namely, TiO2/activated carbon (AC, TiO2/carbon (C, and TiO2/PANi, were compared. The TiO2/carbon composite was obtained by pyrolysis of TiO2/PANi prepared by in situ polymerization method, while the TiO2/activated carbon (TiO2/AC was obtained after treating TiO2/carbon with 1.0 M KOH solution, followed by calcination at a temperature of 450°C. X-ray powder diffraction (XRD, transmission electron microscopy (TEM, Fourier transform infrared (FTIR, thermogravimetric analysis (TG-DTA, Brunauer-Emmet-Teller (BET, and UV-Vis spectroscopy were used to characterize and evaluate the prepared samples. The specific surface area was determined to be in the following order: TiO2/AC > TiO2/C > TiO2/PANi > TiO2 (179 > 134 > 54 > 9 m2 g−1. The evaluation of photocatalytic performance for the degradation of methylene blue under UV light irradiation was also of the same order, with 98 > 84.7 > 69% conversion rate, which is likely to be attributed to the porosity and synergistic effect in the prepared samples.

  10. Quantum Transport in Mesoscopic Systems

    Indian Academy of Sciences (India)

    voltage bias, the tunneling of the electron from the lead to the dot and vice versa will happen very rarely. Then two successive ..... A typical mesoscopic quantum dot system (a small drop- .... dynamical behavior of the distribution function of the.

  11. Sulphur doped nanoparticles of TiO2

    Czech Academy of Sciences Publication Activity Database

    Szatmáry, Lórant; Bakardjieva, Snejana; Šubrt, Jan; Bezdička, Petr; Jirkovský, Jaromír; Bastl, Zdeněk; Brezová, V.; Korenko, M.

    2011-01-01

    Roč. 161, č. 1 (2011), s. 23-28 ISSN 0920-5861 R&D Projects: GA MŠk 1M0577 Institutional research plan: CEZ:AV0Z40400503; CEZ:AV0Z40320502 Keywords : photocatalyst * S-doped TiO2 * Thiourea Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 3.407, year: 2011

  12. Impedance spectroscopy studies of surface engineered TiO2 ...

    Indian Academy of Sciences (India)

    Administrator

    Impedance; nanoTiO2; self-assembled monolayers; electrical resistivity; permittivity. 1. Introduction ... search studies showed that nanostructured TiO2 ceramics possess ..... tion handbook (ed) J Cazes (New York: Marcel Dekker). 3rd ed, p ...

  13. Supercritical Flow Synthesis of TiO2

    DEFF Research Database (Denmark)

    Hellstern, Henrik Christian; Becker, Jacob; Hald, Peter

    2014-01-01

    A new, up-scaled supercritical flow synthesis apparatus has been constructed in Aarhus. A module based system allows for a range of parameter studies with improved parameter control. The dual-reactor setup enables both single phase and core-shell nanoparticle synthesis. TiO2 is a well-known mater...

  14. Fluoropolymer - TiO2 coatings and their superhydrophilicity

    DEFF Research Database (Denmark)

    Søgaard, Erik Gydesen; Simonsen, Morten Enggrob; Jepsen, Henrik

    In this work the superhydrophilicity of coatings on fluoropolymer were investigated. The different coatings were prepared by help of P25 Degussa TiO2 powder, titaniumisopropoxide, Lumiflon® and two different curing agents (BL 3175 and Cymel 303). The investigations were performed by help of a sta...

  15. High-pressure polymorphs of anatase TiO2

    DEFF Research Database (Denmark)

    Arlt, T.; Bermejo, M.; Blanco, M. A.

    2000-01-01

    The equation of state of anatase TiO2 has been determined experimentally-using polycrystalline as well as single-crystal material-and compared with theoretical calculations using the ab initio perturbed ion model. The results are highly consistent, the zero-pressure bulk modulus being 179(2) GPa ...

  16. Protein Corona Prevents TiO2 Phototoxicity.

    Directory of Open Access Journals (Sweden)

    Maja Garvas

    Full Text Available TiO2 nanoparticles have generally low toxicity in the in vitro systems although some toxicity is expected to originate in the TiO2-associated photo-generated radical production, which can however be modulated by the radical trapping ability of the serum proteins. To explore the role of serum proteins in the phototoxicity of the TiO2 nanoparticles we measure viability of the exposed cells depending on the nanoparticle and serum protein concentrations.Fluorescence and spin trapping EPR spectroscopy reveal that the ratio between the nanoparticle and protein concentrations determines the amount of the nanoparticles' surface which is not covered by the serum proteins and is proportional to the amount of photo-induced radicals. Phototoxicity thus becomes substantial only at the protein concentration being too low to completely coat the nanotubes' surface.These results imply that TiO2 nanoparticles should be applied with ligands such as proteins when phototoxic effects are not desired - for example in cosmetics industry. On the other hand, the nanoparticles should be used in serum free medium or any other ligand free medium, when phototoxic effects are desired - as for efficient photodynamic cancer therapy.

  17. Shape-dependent Surface Energetics of Nanocrystalline TiO2

    Energy Technology Data Exchange (ETDEWEB)

    Park, T.J.; Wong, S.; Levchenko, A.A.; Zhou, H.; Navrotsky, A.

    2010-10-21

    We report the direct determination of surface enthalpies for nanophase TiO{sub 2} anatase with different morphologies derived from drop solution calorimetry in a molten sodium molybdate (3Na{sub 2}Ol{center_dot}4MoO{sub 3}) solvent at 702 C. The energetics of surface hydration has been measured using a Calvet microcalorimeter coupled with a gas dosing system. The surface enthalpies of hydrated surfaces for anatase TiO{sub 2} nanoparticles, nanowires and sea-urchin-like assemblies are 0.51 {+-} 0.05, 1.07 {+-} 0.28, and 1.29 {+-} 0.16 J m{sup -2}, respectively, whereas those of anhydrous surfaces are 0.74 {+-} 0.04, 1.24 {+-} 0.28, and 1.41 {+-} 0.16 J m{sup -2}, respectively. The trend in TiO{sub 2}, which shows higher surface enthalpies for more complex nanostructures, is consistent with that reported in ZnO. The shape-dependent surface enthalpy at the nanoscale level is discussed in terms of exposed surface structures. The enthalpies of hydration appear to be similar for all morphologies.

  18. Photoinduced properties of nanocrystalline TiO2 sol–gel derived ...

    Indian Academy of Sciences (India)

    Administrator

    photocatalysis, sterilizing, solar energy cells, gas sensors, self-cleaning effect etc ... The production of nanostructure films is nowadays an established method and .... and hydrogen bonds interactions between H2O and –OH will be increased.

  19. Nanocrystalline TiO2 for Solar Cells and Lithium Batteries

    Czech Academy of Sciences Publication Activity Database

    Kavan, Ladislav

    2006-01-01

    Roč. 51, - (2006), s. 20-29. ISBN 3-908158-08-7. ISSN 1661-819X Grant - others:EC project Molycell(XE) SES6-CT-2003-502783; High Power Lithium(XE) EC-COST D35.0002 Institutional research plan: CEZ:AV0Z40400503 Keywords : titanium dioxide * solar cells * Li- ion batteries Subject RIV: CG - Electrochemistry

  20. Synthesis of nanocrystalline TiO2 by tartarate gel method

    Indian Academy of Sciences (India)

    Unknown

    mixture of tartaric acid and TiOCl2 solution forms a gel on heating on a water bath which decomposes at higher temperatures, > 423 K. During calcination process, a black fluffy mass (foam-like) is formed which occupies large volumes of the furnace. As the temperature increases, the black mass turns to white in colour with ...

  1. TiO2--a prototypical memristive material.

    Science.gov (United States)

    Szot, K; Rogala, M; Speier, W; Klusek, Z; Besmehn, A; Waser, R

    2011-06-24

    Redox-based memristive switching has been observed in many binary transition metal oxides and related compounds. Since, on the one hand, many recent reports utilize TiO(2) for their studies of the memristive phenomenon and, on the other hand, there is a long history of the electronic structure and the crystallographic structure of TiO(2) under the impact of reduction and oxidation processes, we selected this material as a prototypical material to provide deeper insight into the mechanisms behind memristive switching. In part I, we briefly outline the results of the historical and recent studies of electroforming and resistive switching of TiO(2)-based cells. We describe the (tiny) stoichiometrical range for TiO(2 - x) as a homogeneous compound, the aggregation of point defects (oxygen vacancies) into extended defects, and the formation of the various Magnéli phases. Furthermore, we discuss the driving forces for these solid-state reactions from the thermodynamical point of view. In part II, we provide new experimental details about the hierarchical transformation of TiO(2) single crystals into Magnéli phases, and vice versa, under the influence of chemical, electrical and thermal gradients, on the basis of the macroscopic and nanoscopic measurements. Those include thermogravimetry, high-temperature x-ray diffraction (XRD), high-temperature conductivity measurements, as well as low-energy electron diffraction (LEED), x-ray photoelectron spectroscopy (XPS), and LC-AFM (atomic force microscope equipped with a conducting tip) studies. Conclusions are drawn concerning the relevant parameters that need to be controlled in order to tailor the memristive properties.

  2. Fate of pristine TiO2 nanoparticles and aged paint-containing TiO2 nanoparticles in lettuce crop after foliar exposure.

    Science.gov (United States)

    Larue, Camille; Castillo-Michel, Hiram; Sobanska, Sophie; Trcera, Nicolas; Sorieul, Stéphanie; Cécillon, Lauric; Ouerdane, Laurent; Legros, Samuel; Sarret, Géraldine

    2014-05-30

    Engineered TiO2 nanoparticles (TiO2-NPs) are present in a large variety of consumer products, and are produced in largest amount. The building industry is a major sector using TiO2-NPs, especially in paints. The fate of NPs after their release in the environment is still largely unknown, and their possible transfer in plants and subsequent impacts have not been studied in detail. The foliar transfer pathway is even less understood than the root pathway. In this study, lettuces were exposed to pristine TiO2-NPs and aged paint leachate containing TiO2-NPs and microparticles (TiO2-MPs). Internalization and in situ speciation of Ti were investigated by a combination of microscopic and spectroscopic techniques. Not only TiO2-NPs pristine and from aged paints, but also TiO2-MPs were internalized in lettuce leaves, and observed in all types of tissues. No change in speciation was noticed, but an organic coating of TiO2-NPs is likely. Phytotoxicity markers were tested for plants exposed to pristine TiO2-NPs. No acute phytotoxicity was observed; variations were only observed in glutathione and phytochelatin levels but remained low as compared to typical values. These results obtained on the foliar uptake mechanisms of nano- and microparticles are important in the perspective of risk assessment of atmospheric contaminations. Copyright © 2014 Elsevier B.V. All rights reserved.

  3. Favorable recycling photocatalyst TiO2/CFA: Effects of loading percent of TiO2 on the structural property and photocatalytic activity

    International Nuclear Information System (INIS)

    Shi Jianwen; Chen Shaohua; Ye Zhilong; Wang Shumei; Wu Peng

    2010-01-01

    A series of photocatalysts TiO 2 /CFA were prepared using coal fly ash (CFA), waste discharged from coal-fired power plant, as substrate, and then these photocatalysts were characterized by scanning electron microscope, X-ray diffraction analysis, nitrogen adsorption test and ultraviolet-visible absorption analysis. The effects of loading percent of TiO 2 on the photocatalytic activity and re-use property of TiO 2 /CFA were evaluated by the photocatalytic decoloration and mineralization of methyl orange solution. The results show that the pore volume and the specific surface area of the TiO 2 /CFA both increased with the increase in the loading percent of TiO 2 , which improved the photocatalytic activity of TiO 2 /CFA. However, when the loading percent of TiO 2 was too high (up to 54.51%), superfluous TiO 2 was easy to break away from CFA in the course of water treatment, which was disadvantaged to the recycling property of TiO 2 /CFA. In this study, the optimal loading percent of TiO 2 was 49.97%, and the efficiencies of photocatalytic decoloration and mineralization could be maintained above 99% and 90%, respectively, when the photocatalyst was used repeatedly, without any decline, even at the sixth cycle.

  4. Investigation of various properties of HfO2-TiO2 thin film composites deposited by multi-magnetron sputtering system

    Science.gov (United States)

    Mazur, M.; Poniedziałek, A.; Kaczmarek, D.; Wojcieszak, D.; Domaradzki, J.; Gibson, D.

    2017-11-01

    In this work the properties of hafnium dioxide (HfO2), titanium dioxide (TiO2) and mixed HfO2-TiO2 thin films with various amount of titanium addition, deposited by magnetron sputtering were described. Structural, surface, optical and mechanical properties of deposited coatings were analyzed. Based on X-ray diffraction and Raman scattering measuremets it was observed that there was a significant influence of titanium concentration in mixed TiO2-HfO2 thin films on their microstructure. Increase of Ti content in prepared mixed oxides coatings caused, e.g. a decrease of average crystallite size and amorphisation of the coatings. As-deposited hafnia and titania thin films exhibited nanocrystalline structure of monoclinic phase and mixed anatase-rutile phase for HfO2 and TiO2 thin films, respectively. Atomic force microscopy investigations showed that the surface of deposited thin films was densely packed, crack-free and composed of visible grains. Surface roughness and the value of water contact angle decreased with the increase of Ti content in mixed oxides. Results of optical studies showed that all deposited thin films were well transparent in a visible light range. The effect of the change of material composition on the cut-off wavelength, refractive index and packing density was also investigated. Performed measurements of mechanical properties revealed that hardness and Young's elastic modulus of thin films were dependent on material composition. Hardness of thin films increased with an increase of Ti content in thin films, from 4.90 GPa to 13.7 GPa for HfO2 and TiO2, respectively. The results of the scratch resistance showed that thin films with proper material composition can be used as protective coatings in optical devices.

  5. Obtention and characterization of TiO2/TiN multilayers coatings

    International Nuclear Information System (INIS)

    Goncalves, Andre

    2010-01-01

    Nano science has emerged in recent years as one of the most important areas for future technological developments, especially in the area of electronic devices. Nanotechnology has an interdisciplinary character which includes knowledge from physics, chemistry, engineering, and biology. This technology is being used in the manufacture of microprocessors, pumps for dose of medicine, and coating materials, among others. The MOCVD technique has been used recently to obtain nanocrystalline coatings, and provide films of better quality than those obtained by conventional CVD or physical methods. Furthermore, the MOCVD technique presents itself as a competitive alternative because it is relatively inexpensive and easy to deploy compared to physical deposition methods. In this work multilayer coatings of TiO 2 /TiN were produced. During the experiment, the opening and closing of the valves of gases admission, requires from the operator manual ability to trigger the valve and controlling the deposition time, which creates the possibility of errors, leading directly into the thickness of each layer. Thus, the need of reducing the influence of the operator, and the possibility of using time intervals of less than a minute in the growths, created the opportunity to develop a computer program to manage the whole system. The software was developed using the 'State machine' concept for the process control and Hardware in the loop simulation. (author)

  6. Superhydrophilicity of TiO2 nano thin films

    International Nuclear Information System (INIS)

    Mohammadizadeh, M.R.; Ashkarran, A.A.

    2007-01-01

    Full text: Among the several oxide semiconductors, titanium dioxide has a more helpful role in our environmental purification due to its photocatalytic activity, photo-induced superhydrophilicity, and as a result of them non-toxicity, self cleaning, and antifogging effects. After the discovery of superhydrophilicity of titanium dioxide in 1997, several researches have been performed due to its nature and useful applications. The superhydrophilicity property of the surface allows water to spread completely across the surface rather than remains as droplets, thus making the surface antifog and easy-to-clean. The distinction of photo-induced catalytic and hydrophilicity properties of TiO 2 thin films has been accepted although, the origin of hydrophilicity property has not been recognized completely yet. TiO 2 thin films on soda lime glass were prepared by the sol-gel method and spin coating process. The calcination temperature was changed from 100 to 550 C. XRD patterns show increasing the content of polycrystalline anatase phase with increasing the calcination temperature. The AFM results indicate granular morphology of the films, which particle size changes from 22 to 166 nm by increasing the calcination temperature. The RBS, EDX and Raman spectroscopy of the films show the ratio of Ti:O∼0.5, and diffusion of sodium ions from substrate into the layer, by increasing the calcination temperature. The UV/Vis. spectroscopy of the films indicates a red shift by increasing the calcination temperature. The contact angle meter experiment shows that superhydrophilicity of the films depends on the formation of anatase crystal structure and diffused sodium content from substrate to the layer. The best hydrophilicity property was observed at 450 C calcination temperature, where the film is converted to a superhydrophilic surface after 10 minutes under 2mW/cm 2 UV irradiation. TiO 2 thin film on Si(111), Si(100), and quartz substrates needs less time to be converted to superhydrophilic surface rather than glass and polycrystalline Si substrates. Our results are consistent with the idea that UV-induced wetting of TiO 2 surface is caused by the removal of hydrophobic layers of hydrocarbons by TiO 2 -mediated photo-oxidation, which leads to the attractive interaction of water with clean TiO 2 surface. (authors)

  7. Synthesis and photocatalytic activity of Ce-doped TiO2 and TiO2 nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Arruda, L.B.; Pereira, E.A.; Paula, F.R.; Lisboa Filho, P.N. [Universidade Estadual Paulista Julio de Mesquita Filho (UNESP), SP (Brazil)

    2016-07-01

    Full text: One-dimensional nanostructures have been intensively studied, from the point of view of their synthesis and mechanisms of formation, as well as their applications in photonics, solar energy conversion, environmental and photocatalysis, since their properties due high surface area, electrical conductivity and light dispersion effects. Titanium dioxide (TiO2) nanoparticles have been demonstrated to be an effective multifunctional material especially when the particle size is less than 50 nm exhibit photoinduced activities that originate from the semiconductor band gap. TiO2 is semiconductor more used in photocatalysis, for this reason various properties have been thoroughly investigated in order to show that the photocatalytic activity and TiO2 reaction mechanism are influenced by structure, defects and impurities, surface morphology. and interfaces in addition to the concentration of dopants, such as rare-earth elements. Cerium ions, for example, vary between Ce4+ and Ce3 + oxidation state making the cerium oxide appear as CeO2 and Ce2O3 under oxidation and reduction conditions. These different electronic structures of Ce3+ (4f15d0) and Ce4+ (4f05d0) provide different catalytic and optical properties at the TiO2. In this work, samples of Ce-doped TiO2 and TiO2 were synthesized by alkali route, and its photocatalytic activity analyzed in order to create a relationship between the response obtained and the structure and morphology of each sample. Alkali route consists in submitting TiO2 (anatase) powder directly in medium of the NaOH (10M) and maintained at 120°C/20 hours by a glycerin bath with subsequent washed with water and HCl (0.1M) until reaching the desired pH. The synthesized samples were then studied by X-ray diffraction (XRD), transmission electron microscopy (TEM), and X-ray photoelectron spectroscopy (XPS). The photocatalytic decomposition of rhodamine B (Rh.B) it was performed under UV irradiation and visible light in air. For the obtained samples with pH 7, XRD measurements showed the coexistence of TiO2 and sodium titanate phase. By decreasing the pH during acid washing the sodium content was eliminated leaving only the main phase. This behavior was observed for samples containing Cerium concentrations up to 0.2%. The obtained nanotubes presented multiple walls, having dimensions of 5 nm of diameter and about 200 nm of length. Energy dispersive X-ray spectroscopy analyzes revealed that nanotubes are mainly composed of titanium and oxygen, with small amounts of sodium when pH is 7 and sodium no was observed for the sample obtained at pH 4. It shows that synthesis conditions are very important in order to obtain single-phase structures. In addition, TiO2 nanotubes showed good photocatalytic activity with degradation around 100 minutes.(author)

  8. Synthesis and photocatalytic activity of Ce-doped TiO2 and TiO2 nanotubes

    International Nuclear Information System (INIS)

    Arruda, L.B.; Pereira, E.A.; Paula, F.R.; Lisboa Filho, P.N.

    2016-01-01

    Full text: One-dimensional nanostructures have been intensively studied, from the point of view of their synthesis and mechanisms of formation, as well as their applications in photonics, solar energy conversion, environmental and photocatalysis, since their properties due high surface area, electrical conductivity and light dispersion effects. Titanium dioxide (TiO2) nanoparticles have been demonstrated to be an effective multifunctional material especially when the particle size is less than 50 nm exhibit photoinduced activities that originate from the semiconductor band gap. TiO2 is semiconductor more used in photocatalysis, for this reason various properties have been thoroughly investigated in order to show that the photocatalytic activity and TiO2 reaction mechanism are influenced by structure, defects and impurities, surface morphology. and interfaces in addition to the concentration of dopants, such as rare-earth elements. Cerium ions, for example, vary between Ce4+ and Ce3 + oxidation state making the cerium oxide appear as CeO2 and Ce2O3 under oxidation and reduction conditions. These different electronic structures of Ce3+ (4f15d0) and Ce4+ (4f05d0) provide different catalytic and optical properties at the TiO2. In this work, samples of Ce-doped TiO2 and TiO2 were synthesized by alkali route, and its photocatalytic activity analyzed in order to create a relationship between the response obtained and the structure and morphology of each sample. Alkali route consists in submitting TiO2 (anatase) powder directly in medium of the NaOH (10M) and maintained at 120°C/20 hours by a glycerin bath with subsequent washed with water and HCl (0.1M) until reaching the desired pH. The synthesized samples were then studied by X-ray diffraction (XRD), transmission electron microscopy (TEM), and X-ray photoelectron spectroscopy (XPS). The photocatalytic decomposition of rhodamine B (Rh.B) it was performed under UV irradiation and visible light in air. For the obtained samples with pH 7, XRD measurements showed the coexistence of TiO2 and sodium titanate phase. By decreasing the pH during acid washing the sodium content was eliminated leaving only the main phase. This behavior was observed for samples containing Cerium concentrations up to 0.2%. The obtained nanotubes presented multiple walls, having dimensions of 5 nm of diameter and about 200 nm of length. Energy dispersive X-ray spectroscopy analyzes revealed that nanotubes are mainly composed of titanium and oxygen, with small amounts of sodium when pH is 7 and sodium no was observed for the sample obtained at pH 4. It shows that synthesis conditions are very important in order to obtain single-phase structures. In addition, TiO2 nanotubes showed good photocatalytic activity with degradation around 100 minutes.(author)

  9. Photocorrosion Mechanism of TiO2-Coated Photoanodes

    Directory of Open Access Journals (Sweden)

    Arjen Didden

    2015-01-01

    Full Text Available Atomic layer deposition was used to coat CdS photoanodes with 7 nm thick TiO2 films to protect them from photocorrosion during photoelectrochemical water splitting. Photoelectrochemical measurements indicate that the TiO2 coating does not provide full protection against photocorrosion. The degradation of the film initiates from small pinholes and shows oscillatory behavior that can be explained by an Avrami-type model for photocorrosion that is halfway between 2D and 3D etching. XPS analysis of corroded films indicates that a thin layer of CdS remains present on the surface of the corroded photoanode that is more resilient towards photocorrosion.

  10. Application of TIO2 as A sorbent for radioactive waste

    International Nuclear Information System (INIS)

    Zamroni, H.; Las, T.; Kamarz, H.

    1997-01-01

    The sorption properties of the neodymium has been studied by using TiO 2 sorbent. The experiment was carried out by batch methods to investigate the kinetic sorption, effect of pH and effect of NaNO 3 concentration in the solution. Neodymium uses for a model of trivalent actinide treated by TiO 2 which was known as materials having high thermal and radiation stabilities as well as potentially used for immobilization of waste with cement or vitrification. the results show that the optimum of kinetic sorption was obtained after one day experiment to reach the equilibrium in sorption on pH 4, and the increasing of NaNO 3 concentrations will increase the sorption of neodymium in solution (author)

  11. TiO2 and SiC nanostructured films, organized CNT structures

    Indian Academy of Sciences (India)

    sized nanostructured TiO2 films through hydrolysis of titanium tetra-isopropoxide. (TTIP) [9 ... structured TiO2 as a photocatalyst is as follows [15]:. TiO2(ns) ... The deposited films were easily detached from the silica tube and subjected to. SEM.

  12. Enhanced Bonding of Silver Nanoparticles on Oxidized TiO2(110)

    DEFF Research Database (Denmark)

    Hansen, Jonas Ørbæk; Salazar, Estephania Lira; Galliker, Patrick

    2010-01-01

    The nucleation and growth of silver nanoclusters on TiO2(110) surfaces with on-top O adatoms (oxidized TiO2), surface O vacancies and H adatoms (reduced TiO2) have been studied. From the interplay of scanning tunneling microscopy/photoelectron spectroscopy experiments and density functional theor...

  13. Photocatalytic Water Treatment on TiO2 Thin Layers.

    Czech Academy of Sciences Publication Activity Database

    Šolcová, Olga; Spáčilová, L.; Maléterová, Ywetta; Morozová, Magdalena; Ezechiáš, Martin; Křesinová, Zdena

    2016-01-01

    Roč. 57, č. 25 (2016), s. 11631-11638 ISSN 1944-3994. [International Conference on Protection and Restoration of the Environment /12./. Skiathos Island, 29.06.2014-03.07.2014] R&D Projects: GA TA ČR TA01020804 Institutional support: RVO:67985858 ; RVO:61388971 Keywords : water purification * endocrine disruptor * photocatalytic * TiO2 layers Subject RIV: CI - Industrial Chemistry, Chemical Engineering; EE - Microbiology, Virology (MBU-M) Impact factor: 1.631, year: 2016

  14. TiO(2)-graphene nanocomposite as high performace photocatalysts

    Czech Academy of Sciences Publication Activity Database

    Štengl, Václav; Popelková, Daniela; Vláčil, P.

    2011-01-01

    Roč. 115, č. 51 (2011), s. 25209-25218 ISSN 1932-7447 R&D Projects: GA MPO(CZ) FI-IM3/061; GA MPO FI-IM5/239 Institutional research plan: CEZ:AV0Z40320502 Keywords : titanium-dioxide * visible-light * doped TiO2 * degradation * graphene * oxide Subject RIV: CA - Inorganic Chemistry Impact factor: 4.805, year: 2011

  15. Defects improved photocatalytic ability of TiO2

    International Nuclear Information System (INIS)

    Li, Lei; Tian, Hong-Wei; Meng, Fan-Ling; Hu, Xiao-Ying; Zheng, Wei-Tao; Sun, Chang Q.

    2014-01-01

    Highlights: • Defect improves the photocatalytic ability by band gap narrowing and carrier life prolonging. • Atomic undercoordination shortens the local bonds, entraps, and polarizes electrons. • Polarization lowers the local workfunction and lengthens carrier life. • Entrapment and polarization narrows the band gap tuning the wavelength of absorption. - Abstract: Defect generation forms an important means modulating the photocatalytic ability of TiO 2 with mechanisms that remain yet unclear. Here we show that a spectral distillation clarifies the impact of defect on modulating the band gap, electroaffinity, and work function of the substance. Firstly, by analyzing XPS measurements, we calibrated the 2p 3/2 level of 451.47 eV for an isolated Ti atom and its shifts by 2.14 and 6.94 eV, respectively, upon Ti and TiO 2 bulk formation. Spectral difference between the defected and the un-defected TiO 2 skin revealed then that the 2p 3/2 level shifts further from 6.94 to 9.67 eV due to the defect-induced quantum entrapment. This entrapment is associated with an elevation of the upper edges of both the 2p 3/2 and the conduction band by polarization. The shortening and strengthening of bonds between undercoordinated atoms densify and entrap the core electrons, which in turn polarize the dangling bond electrons of defect atoms. The entrapment and polarization mediate thus the band gap, the electroaffinity, the work function, and the photocatalytic ability of TiO 2

  16. Versatile preparation method for mesoporous TiO2 electrodes ...

    Indian Academy of Sciences (India)

    Unknown

    cyanate into CuI layer further enhanced the efficiency up to 2⋅75% under the irradiance .... an extremely easy way to dope films with virtually any .... to see the effect of ionic liquid on CuI, 1-ethyl-3-methyl- ... This analysis showed that TiO2 electrodes were polycrys- .... thin insulating layer of Al2O3 by using dip-coating meth-.

  17. Drug loading of nanoporous TiO2 films

    International Nuclear Information System (INIS)

    Ayon, Arturo A; Cantu, Michael; Chava, Kalpana; Agrawal, C Mauli; Feldman, Marc D; Johnson, Dave; Patel, Devang; Marton, Denes; Shi, Emily

    2006-01-01

    The loading of therapeutic amounts of drug on a nanoporous TiO 2 surface is described. This novel drug-loading scheme on a biocompatible surface, when employed on medical implants, will benefit patients who require the deployment of drug-eluting implants. Anticoagulants, analgesics and antibiotics can be considered on the associated implants for drug delivery during the time of maximal pain or risk for patients undergoing orthopedic procedures. Therefore, this scheme will maximize the chances of patient recovery. (communication)

  18. Lattice defects in rutile, TiO2

    International Nuclear Information System (INIS)

    Nakagawa, M.; Itoh, H.; Nakanishi, S.; Kondo, K.; Okada, M.; Atobe, K.

    1991-01-01

    Rutile, TiO 2 , having a relatively high melting point exhibits strong optical absorption after neutron irradiation (8 x 10 16 n f /cm 2 ) at 15K. The band peak is located near 0.96 μ, having a FWHM of 0.87 eV (at liquid nitrogen temperature). After inverse recovery at 120K, lattice defects due probably to F centers are annealed out at about 220K. (author)

  19. Microporous TiO2-WO3/TiO2 films with visible-light photocatalytic activity synthesized by micro arc oxidation and DC magnetron sputtering

    International Nuclear Information System (INIS)

    Wu, Kee-Rong; Hung, Chung-Hsuang; Yeh, Chung-Wei; Wu, Jiing-Kae

    2012-01-01

    Highlights: ► A simple MAO is used to prepare porous WO 3 /TiO 2 layer on Ti sheet as a visible-light enabled catalyst. ► The photocatalytic activity of the WO 3 /TiO 2 is enhanced by sputtering over an N,C-TiO 2 layer. ► This is ascribed to the synergetic effect of hybrid sample prepared by two-step method. - Abstract: This study reports the preparation of microporous TiO 2 -WO 3 /TiO 2 films with a high surface area using a two-step approach. A porous WO 3 /TiO 2 template was synthesized by oxidizing a titanium sheet using a micro arc oxidation (MAO) process. This sheet was subsequently overlaid with a visible light (Vis)-enabled TiO 2 (N,C-TiO 2 ) film, which was deposited by codoping nitrogen (N) and carbon (C) ions into a TiO 2 lattice using direct current magnetron sputtering. The resulting microporous TiO 2 -WO 3 /TiO 2 film with a 0.38-μm-thick N,C-TiO 2 top-layer exhibited high photocatalytic activity in methylene blue (MB) degradation among samples under ultraviolet (UV) and Vis irradiation. This is attributable to the synergetic effect of two-step preparation method, which provides a highly porous microstructure and the well-crystallized N,C-TiO 2 top-layer. This is because a higher surface area with high crystallinity favors the adsorption of more MB molecules and more photocatalytic active areas. Thus, the microporous TiO 2 -WO 3 /TiO 2 film has promising applications in the photocatalytic degradation of dye solution under UV and Vis irradiation. These results imply that the microporous WO 3 /TiO 2 can be used as a template of hybrid electrode because it enables rapid fabrication.

  20. Sensing and electrical properties of TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Usman, M.

    2011-01-01

    The purpose of this work was to synthesize TiO 2 nanoparticles using Coprecipitation method. 2 different samples were synthesized, one with a modifier and other without using a modifier. After synthesis, newly formed nanoparticles were characterized b different techniques to find various properties of these nanoparticles. Scanning electron Microscopy (SEM) was used to study structure and morphology of Cu nanoparticles and for compositional analysis Energy dispersive spectroscopy (EDS) was used. X-Ray Diffraction (XRD) Studies were also carried out to find phase an average particle Size. To find the band gap of our nanoparticles, UV-Visible Spectroscopy was also done. Non-Modified nanoparticles were as small as 12nm reported by SEM images which were synthesized using a modifier were as small as 10nm. Modified TiO 2 nanoparticles were used in humidity sensing devices and it properties as a humidity sensor were examined by doing Impedance spectroscopy, D measurements and Dielectric measurements. Our TiO 2 humidity sensor showed sensitivity for humidity at low and mid-range frequencies while its response time was 4 seconds when we changed RH% to 90 from 40% and measured the impedance. (author)

  1. Incorporation of chromium into TiO2 nanopowders

    International Nuclear Information System (INIS)

    Kollbek, Kamila; Sikora, Marcin; Kapusta, Czesław; Szlachetko, Jakub; Radecka, Marta; Lyson-Sypien, Barbara; Zakrzewska, Katarzyna

    2015-01-01

    Highlights: • Nanopowders of TiO 2 :Cr with different amount of Cr dopant were obtained by flame spray synthesis, FSS. • Increase in the optical absorption and a shift of the absorption edge were observed upon Cr doping. • HERFD-XANES measurements indicated that the average valence state of titanium ions was preserved. • Increasing magnetic susceptibility of a paramagnetic character was observed upon Cr doping. - Abstract: The paper reports on the results of a study of optical, electronic and magnetic properties of TiO 2 nanopowders doped with Cr ions. Diffused reflectance spectra reveal an increase in the optical absorption and a shift of the absorption edge towards lower energies upon Cr doping. Direct information on the Ti electronic state and the symmetry of its nearest environment is obtained from XANES Ti K-edge spectra. Magnetic behaviour is probed by means of the temperature dependence of DC magnetic susceptibility. Increasing magnetic susceptibility of a paramagnetic character is observed upon increasing chromium doping. The Curie constant of TiO 2 :10 at.% Cr sample (0.12 emu K/mol Oe) is lower than that expected for Cr 3+ (0.1875 emu K/mol Oe) possibly due to the appearance of Cr 4+ or the presence of the orbital contribution to the magnetic moment

  2. Mesoscopic quantum cryptography

    Energy Technology Data Exchange (ETDEWEB)

    Molotkov, S. N., E-mail: sergei.molotkov@gmail.com [Russian Academy of Sciences, Institute of Solid State Physics (Russian Federation)

    2017-03-15

    Since a strictly single-photon source is not yet available, in quantum cryptography systems, one uses, as information quantum states, coherent radiation of a laser with an average number of photons of μ ≈ 0.1–0.5 in a pulse, attenuated to the quasi-single-photon level. The linear independence of a set of coherent quasi-single-photon information states leads to the possibility of unambiguous measurements that, in the presence of losses in the line, restrict the transmission range of secret keys. Starting from a certain value of critical loss (the length of the line), the eavesdropper knows the entire key, does not make errors, and is not detected—the distribution of secret keys becomes impossible. This problem is solved by introducing an additional reference state with an average number of photons of μ{sub cl} ≈ 10{sup 3}–10{sup 6}, depending on the length of the communication line. It is shown that the use of a reference state does not allow the eavesdropper to carry out measurements with conclusive outcome while remaining undetected. A reference state guarantees detecting an eavesdropper in a channel with high losses. In this case, information states may contain a mesoscopic average number of photons in the range of μ{sub q} ≈ 0.5–10{sup 2}. The protocol proposed is easy to implement technically, admits flexible adjustment of parameters to the length of the communication line, and is simple and transparent for proving the secrecy of keys.

  3. Sol-gel synthesis of TiO2 nanoparticles and photocatalytic degradation of methyl orange in aqueous TiO2 suspensions

    International Nuclear Information System (INIS)

    Yang Huaming; Zhang Ke; Shi Rongrong; Li Xianwei; Dong Xiaodan; Yu Yongmei

    2006-01-01

    Anatase TiO 2 nanoparticles of about 16 nm in crystal size have been successfully synthesized via a sol-gel method. Thermal treatment of the precursor at 500-600 deg. C results in the formation of different TiO 2 phase compositions. The samples were characterized by means of X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM). Effects of the pH value of the solution, H 2 O 2 addition, TiO 2 phase composition and recycled TiO 2 on the photocatalytic degradation of methyl orange (MeO) in TiO 2 suspensions under ultraviolet (UV) illumination were primarily investigated. The results indicate that a low pH value, proper amount of H 2 O 2 and pure anatase TiO 2 will facilitate the photocatalytic oxidation of the MeO solution. The photodegradation degree decreases with increasing the pH value of the solution and varies with different amounts of H 2 O 2 . Pure anatase TiO 2 shows better photocatalytic activity for MeO decolorization than biphase TiO 2 . The photocatalytic mechanism of the as-synthesized TiO 2 nanoparticles was discussed

  4. OXIDACIÓN DE p -NITROFENOL USANDO TiO 2 -ADENOSINA MONOFOSFATO I OXIDATION OF p -NITROPHENOL USING TiO 2 -ADENOSIN MONOPHOSPHATE

    Directory of Open Access Journals (Sweden)

    Carlos F. Rivas

    2018-04-01

    Full Text Available The surface of TiO2 was modified with the nucleotides adenosine 3’-monophosphate (AMP’3 and Adenosine 5’-monophosphate (AMP’5. The adsorption of nucleotides was adjusted to Langmuir ́s adsorption model, determining that the optimal condition for TiO 2 modification was at neutral pH. UV-Visible Diffuse Reflectance and IR Attenuated Total Reflectance spectra show that the chemisorption of nucleotides take placed on TiO 2 anatase. The new catalysts (TiO 2 -nucleotide improved the photodegradation of p -nitrophenol in a wide range of pH as compared with the titanium dioxide precursor. Most photoactivity was generated by using the new photocatalytic in the degradation of p -nitrophenol at pH = 6, obtaining high values for the pseudo first order kinetic constant (0.0254 min -1 and 0.0244 min -1 for TiO 2 -AMP’3 and TiO 2 -AMP’5, respectively. For all pH, the trend obtained for the photodegradation was: TiO 2 -AMP ́3 @ TiO 2 -AMP’5 > TiO 2 . Langmuir-Hinshelwood kinetics shows that the contribution of the surface reac tion rate governs the oxidation of the contaminant.

  5. Photocatalytic effects for the TiO2-coated phosphor materials

    International Nuclear Information System (INIS)

    Yoon, Jin-Ho; Jung, Sang-Chul; Kim, Jung-Sik

    2011-01-01

    Research highlights: → The photocatalytic behavior of the coupling of TiO 2 with phosphorescent materials. → The photobleaching of an MB aqueous solution under visible light irradiation. → The ALD TiO 2 -coated phosphor composite showed much higher photocatalytic reactivity. → The light emitted from the phosphors contributed to the photo-generation. - Abstract: This study investigated the photocatalytic behavior of the coupling of TiO 2 with phosphorescent materials. A TiO 2 thin film was deposited on CaAl 2 O 4 :Eu 2+ ,Nd 3+ phosphor particles by using atomic layer deposition (ALD), and its photocatalytic reaction was investigated by the photobleaching of an aqueous solution of methylene-blue (MB) under visible light irradiation. To clarify the mechanism of the TiO 2 -phosphorescent materials, two different samples of TiO 2 -coated phosphor and TiO 2 -Al 2 O 3 -coated phosphor particles were prepared. The photocatalytic mechanisms of the ALD TiO 2 -coated phosphor powders were different from those of the pure TiO 2 and TiO 2 -Al 2 O 3 -coated phosphor. The absorbance in a solution of the ALD TiO 2 -coated phosphor decreased much faster than that of pure TiO 2 under visible irradiation. In addition, the ALD TiO 2 -coated phosphor showed moderately higher photocatalytic degradation of MB solution than the TiO 2 -Al 2 O 3 -coated phosphor did. The TiO 2 -coated phosphorescent materials were characterized by transmission electron microscopy (TEM), Auger electron spectroscopy (AES) and X-ray photon spectroscopy (XPS).

  6. Mesoscopic models of biological membranes

    DEFF Research Database (Denmark)

    Venturoli, M.; Sperotto, Maria Maddalena; Kranenburg, M.

    2006-01-01

    Phospholipids are the main components of biological membranes and dissolved in water these molecules self-assemble into closed structures, of which bilayers are the most relevant from a biological point of view. Lipid bilayers are often used, both in experimental and by theoretical investigations...... to coarse grain a biological membrane. The conclusion of this comparison is that there can be many valid different strategies, but that the results obtained by the various mesoscopic models are surprisingly consistent. A second objective of this review is to illustrate how mesoscopic models can be used...

  7. Synthesis of nanostructured TiO2 (anatase) and TiO2(B) in ionic liquids

    Czech Academy of Sciences Publication Activity Database

    Mansfeldová, Věra; Lásková, Barbora; Krýsová, Hana; Zukalová, Markéta; Kavan, Ladislav

    2014-01-01

    Roč. 230, JUL 2014 (2014), s. 85-90 ISSN 0920-5861 R&D Projects: GA ČR GA13-07724S; GA MŠk 7E09117 Grant - others:European Commission(XE) NMP-229036 Institutional support: RVO:61388955 Keywords : TiO2(B) * ionic liquid * electrochemistry Subject RIV: CG - Electrochemistry Impact factor: 3.893, year: 2014

  8. Synergistic effects between TiO2 and carbon nanotubes (CNTs) in a TiO2/CNTs system under visible light irradiation.

    Science.gov (United States)

    Wu, Chung-Hsin; Kuo, Chao-Yin; Chen, Shih-Ting

    2013-01-01

    This study synthesized a TiO2/carbon nanotubes (CNTs) composite via the sol-gel method. The surface characteristics of the TiO2/CNTs composite were determined by X-ray diffraction, transmission electron microscopy, specific surface area analyser, ultraviolent (UV)-vis spectroscopy, X-ray photoelectron spectroscopy and Raman spectrometer. The photocatalytic activity ofthe TiO2/CNTs composite was evaluated by decolourizing C.I. Reactive Red 2 (RR2) under visible light irradiation. Furthermore, the effects of calcination temperature, pH, RR2 concentration, and the TiO2/CNTs composite dosage on RR2 decolourization were determined simultaneously. The optimal calcination temperature to generate TiO2 and the TiO2/CNTs composite was 673 K, as the percentage of anatase crystallization at this temperature was highest. The specific surface area of the TiO2/CNTs composite and TiO2 were 45 and 42 m2/g, respectively. The band gap of TiO2 and the TiO2/CNTs composite was 2.97 and 2.71 eV by UV-vis measurements, respectively. Experimental data indicate that the Ti-O-C bond formed in the TiO2/CNTs composite. The RR2 decolourization rates can be approximated by pseudo-first-order kinetics; moreover, only the TiO2/CNTs composite had photocatalytic activity under visible light irradiation. At pH 7, the RR2 decolourization rate constant of 0.5, 1 and 2 g/L TiO2/CNTs addition was 0.005, 0.0015, and 0.0047 min(-1), respectively. Decolourization rate increased as pH and the RR2 concentration decreased. The CNTs functioned as electron acceptors, promoting separation of photoinduced electron-hole pairs to retard their recombination; thus, photocatalytic activity of the TiO2/CNTs composite exceeded that of TiO2.

  9. High pressure structural phase transitions of TiO2 nanomaterials

    International Nuclear Information System (INIS)

    Li Quan-Jun; Liu Bing-Bing

    2016-01-01

    Recently, the high pressure study on the TiO 2 nanomaterials has attracted considerable attention due to the typical crystal structure and the fascinating properties of TiO 2 with nanoscale sizes. In this paper, we briefly review the recent progress in the high pressure phase transitions of TiO 2 nanomaterials. We discuss the size effects and morphology effects on the high pressure phase transitions of TiO 2 nanomaterials with different particle sizes, morphologies, and microstructures. Several typical pressure-induced structural phase transitions in TiO 2 nanomaterials are presented, including size-dependent phase transition selectivity in nanoparticles, morphology-tuned phase transition in nanowires, nanosheets, and nanoporous materials, and pressure-induced amorphization (PIA) and polyamorphism in ultrafine nanoparticles and TiO 2 -B nanoribbons. Various TiO 2 nanostructural materials with high pressure structures are prepared successfully by high pressure treatment of the corresponding crystal nanomaterials, such as amorphous TiO 2 nanoribbons, α -PbO 2 -type TiO 2 nanowires, nanosheets, and nanoporous materials. These studies suggest that the high pressure phase transitions of TiO 2 nanomaterials depend on the nanosize, morphology, interface energy, and microstructure. The diversity of high pressure behaviors of TiO 2 nanomaterials provides a new insight into the properties of nanomaterials, and paves a way for preparing new nanomaterials with novel high pressure structures and properties for various applications. (topical review)

  10. Synthesis of Si, N co-Doped Nano-Sized TiO2 with High Thermal Stability and Photocatalytic Activity by Mechanochemical Method

    Directory of Open Access Journals (Sweden)

    Peisan Wang

    2018-05-01

    Full Text Available Τhe photocatalytic activity in the range of visible light wavelengths and the thermal stability of the structure were significantly enhanced in Si, N co-doped nano-sized TiO2, and synthesized through high-energy mechanical milling of TiO2 and SiO2 powders, which was followed by calcination at 600 °C in an ammonia atmosphere. High-energy mechanical milling had a pronounced effect on the mixing and the reaction between the starting powders and greatly favored the transformation of the resultant powder mixture into an amorphous phase that contained a large number of evenly-dispersed nanocrystalline TiO2 particles as anatase seeds. The experimental results suggest that the elements were homogeneously dispersed at an atomic level in this amorphous phase. After calcination, most of the amorphous phase was crystallized, which resulted in a unique nano-sized crystalline-core/disordered-shell morphology. This novel experimental process is simple, template-free, and provides features of high reproducibility in large-scale industrial production.

  11. Design and construction of hierarchical TiO2 nanorod arrays by combining layer-by-layer and hydrothermal crystallization techniques for electrochromic application

    Science.gov (United States)

    Chen, Yongbo; Li, Xiaomin; Bi, Zhijie; He, Xiaoli; Li, Guanjie; Xu, Xiaoke; Gao, Xiangdong

    2018-05-01

    The hierarchical TiO2 (H-TiO2) nanorod arrays (NRAs) composed of single-crystalline nanorods and nanocrystals were finely designed and successfully constructed for electrochromic (EC) application. By combining layer-by-layer (LBL) method and hydrothermal crystallization technique, the superfine nanocrystals (5-7 nm), which can provide abundant active sites and facilitate ion insertion/extraction during EC reactions, were uniformly and conformally assembled on the surface of single-crystalline TiO2 (SC-TiO2) NRAs. The as-formed H-TiO2 NRAs integrate the advantages of one-dimensional NRAs with fast kinetics and superfine nanocrystals with high ion capacity, showing highly enhanced EC performance. Large optical contrast (40.3%), shorter coloring/bleaching time (22/4 s), high coloration efficiency (11.2 cm2 C-1), and excellent cycling stability can be achieved in H-TiO2 NRAs, superior to the pristine SC-TiO2 NRAs and nanocrystalline TiO2 films. This work provides a feasible and well-designed strategy to explore high-performance materials for EC application.

  12. Preparation and optical properties of mesoporous TiO2 thin films by a two-step sol-gel technique

    International Nuclear Information System (INIS)

    Kartini, I.; Lu, G.Q.; Meredith, P.; Zhao, X.S.

    2002-01-01

    This paper concerns the preparation of mesoporous titania nanopowders and thin films for use in next generation photoelectrochemical solar cells. We have recently developed a novel method for preparing mesoporous TiO 2 powders using a Two-Step Sol-gel method (TSS). These materials have crystalline domains characteristic of anatase. The first step of the process involves the hydrolysis of titanium isopropoxide in a basic aqueous solution mediated by neutral surfactant. The solid product resulting from Step-1 is then treated in acidified ethanol solution containing a titanium precursor to yield anatase TiO 2 . The resultant powder exhibits a high surface area and large pore volume with uniform mesopores. Slurries made from the resultant powder of Steps 1 and 2 have been used to produce thin titania films on glass slides. The optical and structural properties of these films have been compared to the films made of a commercial titania (Degussa P25, BASF). We will discuss these properties with respect to the possible use of such mesoporous titania films as the wide band gap semiconductor in dye-sensitized nanocrystalline TiO 2 solar cells

  13. Low temperature fabrication of perovskite solar cells with TiO2 nanoparticle layers

    International Nuclear Information System (INIS)

    Kanayama, Masato; Oku, Takeo; Suzuki, Atsushi; Yamada, Masahiro; Sakamoto, Hiroki; Minami, Satoshi; Kohno, Kazufumi

    2016-01-01

    TiO 2 /CH 3 NH 3 PbI 3 -based photovoltaic devices were fabricated by a spin-coating method using a mixture solution. TiO 2 require high-temperature processing to achieve suitably high carrier mobility. TiO 2 electron transport layers and TiO 2 scaffold layers for the perovskite were fabricated from TiO 2 nanoparticles with different grain sizes. The photovoltaic properties and microstructures of solar cells were characterized. Nanoparticle sizes of these TiO 2 were 23 nm and 3 nm and the performance of solar cells was improved by combination of two TiO 2 nanoparticles

  14. Photocatalytic decouloration of malachite green dye by application of TiO2 nanotubes

    International Nuclear Information System (INIS)

    Prado, Alexandre G.S.; Costa, Leonardo L.

    2009-01-01

    The nanotubes of titania were synthesized in a hydrothermal system and characterized by scanning electronic microscopy (SEM), FT-IR, FT-Raman, and surface charge density by surface area analyzer. These nanomaterials were applied to photocatalyse malachite green dye degradation. Photodegradation capacity of TiO 2 nanotubes was compared to TiO 2 anatase photoactivity. Malachite dye was completely degraded in 75 and 105 min of reaction photocatalysed by TiO 2 nanotubes and TiO 2 anatase, respectively. Catalysts displayed high photodegradation activity at pH 4. TiO 2 nanotubes were easily recycled whereas the reuse of TiO 2 anatase was not effective. Nanotubes maintained 80% of their activity after 10 catalytic cycles and TiO 2 anatase presented only 8% of its activity after 10 cycles.

  15. First-principles atomistic Wulff constructions for an equilibrium rutile TiO2 shape modeling

    Science.gov (United States)

    Jiang, Fengzhou; Yang, Lei; Zhou, Dali; He, Gang; Zhou, Jiabei; Wang, Fanhou; Chen, Zhi-Gang

    2018-04-01

    Identifying the exposed surfaces of rutile TiO2 crystal is crucial for its industry application and surface engineering. In this study, the shape of the rutile TiO2 was constructed by applying equilibrium thermodynamics of TiO2 crystals via first-principles density functional theory (DFT) and Wulff principles. From the DFT calculations, the surface energies of six low-index stoichiometric facets of TiO2 are determined after the calibrations of crystal structure. And then, combined surface energy calculations and Wulff principles, a geometric model of equilibrium rutile TiO2 is built up, which is coherent with the typical morphology of fully-developed equilibrium TiO2 crystal. This study provides fundamental theoretical guidance for the surface analysis and surface modification of the rutile TiO2-based materials from experimental research to industry manufacturing.

  16. Composition of Surface Adsorbed Layer of TiO2 Stored in Ambient Air

    Directory of Open Access Journals (Sweden)

    Zakharenko V.S.

    2017-11-01

    Full Text Available The processes of dark, UV, and visible light promoted desorption of surface species were investigated for three different TiO2 samples: TiO2 prepared by dispersion of the titania single crystal, TiO2 prepared by combustion of a pyrotechnic mixture in air, and commercial TiO2 P25. The composition of the adsorbed layer was identified in the dark and under UV and visible light irradiation. The composition of desorption products showed the dependence of the adsorption layer state on the TiO2 nature. Methane photodesorption was detected only for the commercial TiO2 P25. Possible reasons for methane emission include the capturing of complete molecules during the TiO2 production process and photocatalytic hydrogenation of CO2 under UV-light.

  17. Immobilization of TiO2 nanoparticles on Fe-filled carbon nanocapsules for photocatalytic applications

    International Nuclear Information System (INIS)

    Huang, H.-C.; Huang, G.-L.; Chen, H.-L.; Lee, Y.-D.

    2006-01-01

    Using a simple sol-gel method, a novel magnetic photocatalyst was produced by immobilization of TiO 2 nano-crystal on Fe-filled carbon nanocapsules (Fe-CNC). High resolution TEM images indicated that the immobilization of TiO 2 on Fe-CNC was driven primarily by heterogeneous coagulation, whereas surface nucleation and growth was the dominant mechanism for immobilizing TiO 2 on acid-functionalized hollow CNC. The TiO 2 immobilized on Fe-CNC exhibited the anatase phase as revealed by the X-ray diffraction (XRD) patterns. In comparison with free TiO 2 and TiO 2 -coated CNC, TiO 2 -coated Fe-CNC displayed good performance in the removal of NO gas under UV exposure. Due to the advantages of easy recycling and good photocatalytic efficiency, the novel magnetic photocatalyst developed here has potential use in photocatalytic applications for pollution prevention

  18. Study of TiO2 nanotubes as an implant application

    International Nuclear Information System (INIS)

    Hazan, Roshasnorlyza; Sreekantan, Srimala; Mydin, Rabiatul Basria S. M. N.; Mat, Ishak; Abdullah, Yusof

    2016-01-01

    Vertically aligned TiO 2 nanotubes have become the primary candidates for implant materials that can provide direct control of cell behaviors. In this work, 65 nm inner diameters of TiO 2 nanotubes were successfully prepared by anodization method. The interaction of bone marrow stromal cells (BMSC) in term of cell adhesion and cell morphology on bare titanium and TiO 2 nanotubes is reported. Field emission scanning electron microscopy (FESEM) analysis proved interaction of BMSC on TiO 2 nanotubes structure was better than flat titanium (Ti) surface. Also, significant cell adhesion on TiO 2 nanotubes surface during in vitro study revealed that BMSC prone to attach on TiO 2 nanotubes. From the result, it can be conclude that TiO 2 nanotubes are biocompatible to biological environment and become a new generation for advanced implant materials

  19. Lead iodide perovskite sensitized all-solid-state submicron thin film mesoscopic solar cell with efficiency exceeding 9%.

    KAUST Repository

    Kim, Hui-Seon; Lee, Chang-Ryul; Im, Jeong-Hyeok; Lee, Ki-Beom; Moehl, Thomas; Marchioro, Arianna; Moon, Soo-Jin; Humphry-Baker, Robin; Yum, Jun-Ho; Moser, Jacques E; Grä tzel, Michael; Park, Nam-Gyu

    2012-01-01

    We report on solid-state mesoscopic heterojunction solar cells employing nanoparticles (NPs) of methyl ammonium lead iodide (CH(3)NH(3))PbI(3) as light harvesters. The perovskite NPs were produced by reaction of methylammonium iodide with PbI(2) and deposited onto a submicron-thick mesoscopic TiO(2) film, whose pores were infiltrated with the hole-conductor spiro-MeOTAD. Illumination with standard AM-1.5 sunlight generated large photocurrents (J(SC)) exceeding 17 mA/cm(2), an open circuit photovoltage (V(OC)) of 0.888 V and a fill factor (FF) of 0.62 yielding a power conversion efficiency (PCE) of 9.7%, the highest reported to date for such cells. Femto second laser studies combined with photo-induced absorption measurements showed charge separation to proceed via hole injection from the excited (CH(3)NH(3))PbI(3) NPs into the spiro-MeOTAD followed by electron transfer to the mesoscopic TiO(2) film. The use of a solid hole conductor dramatically improved the device stability compared to (CH(3)NH(3))PbI(3) -sensitized liquid junction cells.

  20. Lead iodide perovskite sensitized all-solid-state submicron thin film mesoscopic solar cell with efficiency exceeding 9%.

    KAUST Repository

    Kim, Hui-Seon

    2012-08-21

    We report on solid-state mesoscopic heterojunction solar cells employing nanoparticles (NPs) of methyl ammonium lead iodide (CH(3)NH(3))PbI(3) as light harvesters. The perovskite NPs were produced by reaction of methylammonium iodide with PbI(2) and deposited onto a submicron-thick mesoscopic TiO(2) film, whose pores were infiltrated with the hole-conductor spiro-MeOTAD. Illumination with standard AM-1.5 sunlight generated large photocurrents (J(SC)) exceeding 17 mA/cm(2), an open circuit photovoltage (V(OC)) of 0.888 V and a fill factor (FF) of 0.62 yielding a power conversion efficiency (PCE) of 9.7%, the highest reported to date for such cells. Femto second laser studies combined with photo-induced absorption measurements showed charge separation to proceed via hole injection from the excited (CH(3)NH(3))PbI(3) NPs into the spiro-MeOTAD followed by electron transfer to the mesoscopic TiO(2) film. The use of a solid hole conductor dramatically improved the device stability compared to (CH(3)NH(3))PbI(3) -sensitized liquid junction cells.

  1. Lead Iodide Perovskite Sensitized All-Solid-State Submicron Thin Film Mesoscopic Solar Cell with Efficiency Exceeding 9%

    Science.gov (United States)

    Kim, Hui-Seon; Lee, Chang-Ryul; Im, Jeong-Hyeok; Lee, Ki-Beom; Moehl, Thomas; Marchioro, Arianna; Moon, Soo-Jin; Humphry-Baker, Robin; Yum, Jun-Ho; Moser, Jacques E.; Grätzel, Michael; Park, Nam-Gyu

    2012-01-01

    We report on solid-state mesoscopic heterojunction solar cells employing nanoparticles (NPs) of methyl ammonium lead iodide (CH3NH3)PbI3 as light harvesters. The perovskite NPs were produced by reaction of methylammonium iodide with PbI2 and deposited onto a submicron-thick mesoscopic TiO2 film, whose pores were infiltrated with the hole-conductor spiro-MeOTAD. Illumination with standard AM-1.5 sunlight generated large photocurrents (JSC) exceeding 17 mA/cm2, an open circuit photovoltage (VOC) of 0.888 V and a fill factor (FF) of 0.62 yielding a power conversion efficiency (PCE) of 9.7%, the highest reported to date for such cells. Femto second laser studies combined with photo-induced absorption measurements showed charge separation to proceed via hole injection from the excited (CH3NH3)PbI3 NPs into the spiro-MeOTAD followed by electron transfer to the mesoscopic TiO2 film. The use of a solid hole conductor dramatically improved the device stability compared to (CH3NH3)PbI3 -sensitized liquid junction cells. PMID:22912919

  2. Optical Properties and Surface Morphology of Nano-composite PMMA: TiO2 Thin Films

    International Nuclear Information System (INIS)

    Lyly Nyl Ismail; Ahmad Fairoz Aziz; Habibah Zulkefle

    2011-01-01

    There are two nano-composite PMMA: TiO 2 solutions were prepared in this research. First solution is nano-composite PMMA commercially available TiO 2 nanopowder and the second solution is nano-composite PMMA with self-prepared TiO 2 powder. The self-prepared TiO 2 powder is obtained by preparing the TiO 2 sol-gel. Solvo thermal method were used to dry the TiO 2 sol-gel and obtained TiO 2 crystal. Ball millers were used to grind the TiO 2 crystal in order to obtained nano sized powder. Triton-X was used as surfactant to stabilizer the composite between PMMA: TiO 2 . Besides comparing the nano-composite solution, we also studied the effect of the thin films thickness on the optical properties and surface morphology of the thin films. The thin films were deposited by sol-gel spin coating method on glass substrates. The optical properties and surface characterization were measured with UV-VIS spectrometer equipment and atomic force microscopy (AFM). The result showed that nano-composite PMMA with self prepared TiO 2 give high optical transparency than nano-composite PMMA with commercially available TiO 2 nano powder. The results also indicate as the thickness is increased the optical transparency are decreased. Both AFM images showed that the agglomerations of TiO 2 particles are occurred on the thin films and the surface roughness is increased when the thickness is increased. High agglomeration particles exist in the AFM images for nano-composite PMMA: TiO 2 with TiO 2 nano powder compare to the other nano-composite solution. (author)

  3. Distinct toxic interactions of TiO2 nanoparticles with four coexisting organochlorine contaminants on algae.

    Science.gov (United States)

    Zhang, Shuai; Deng, Rui; Lin, Daohui; Wu, Fengchang

    Engineered nanoparticles are increasingly discharged into the environment. After discharge, these nanoparticles can interact with co-existing organic contaminants, resulting in a phenomena referred to as 'joint toxicity'. This study evaluated joint toxicities of TiO 2 nanoparticles (TiO 2 NPs) with four different (atrazine, hexachlorobenzene, pentachlorobenzene, and 3,3',4,4'-tetrachlorobiphenyl) organochlorine contaminants (OCs) toward algae (Chlorella pyrenoidosa). The potential mechanisms underlying the joint toxicity were discussed, including TiO 2 NPs-OC interactions, effects of TiO 2 NPs and OCs on biophysicochemical properties of algae and effects of TiO 2 NPs and OCs on each other's bioaccumulation in algae. The results indicate that coexposure led to a synergistic effect on the joint toxicity for TiO 2 NPs-atrazine, antagonistic effect for TiO 2 NPs-hexachlorobenzene and TiO 2 NPs-3,3',4,4'-tetrachlorobiphenyl, and an additive effect for TiO 2 NPs-pentachlorobenzene. There was nearly no adsorption of OCs by TiO 2 NPs, and the physicochemical properties of TiO 2 NPs were largely unaltered by the presence of OCs. However, both OCs and NPs affected the biophysicochemical properties of algal cells and thereby influenced the cell surface binding and/or internalization. TiO 2 NPs significantly increased the bioaccumulation of each OC. However, with the exception of atrazine, the bioaccumulation of TiO 2 NPs decreased when used with each OC. The distinct joint toxicity outcomes were a result of the balance between the increased toxicities of OCs (increased bioaccumulations) and the altered toxicity of TiO 2 NPs (bioaccumulation can either increase or decrease). These results can significantly improve our understanding of the potential environmental risks associated with NPs.

  4. Statewide mesoscopic simulation for Wyoming.

    Science.gov (United States)

    2013-10-01

    This study developed a mesoscopic simulator which is capable of representing both city-level and statewide roadway : networks. The key feature of such models are the integration of (i) a traffic flow model which is efficient enough to : scale to larg...

  5. Spin tunnelling in mesoscopic systems

    Indian Academy of Sciences (India)

    We study spin tunnelling in molecular magnets as an instance of a mesoscopic phenomenon, with special emphasis on the molecule Fe8. We show that the tunnel splitting between various pairs of Zeeman levels in this molecule oscillates as a function of applied magnetic field, vanishing completely at special points in the ...

  6. Hybrid matrices of TiO2 and TiO2–Ag nanofibers with silicone for high water flux photocatalytic degradation of dairy effluent

    DEFF Research Database (Denmark)

    Kanjwal, Muzafar Ahmad; Alm, Martin; Thomsen, Peter

    2016-01-01

    TiO2 and TiO2–Ag nanofibers were produced by electrospinning technique and surface coated on silicone elastomer (diameter: 10.0 mm; thickness: 2.0 mm) by dipcoating method. These coated hybrid nanoporous matrices were characterized by various morphological and physicochemical techniques (like SEM...

  7. TiO2/Cu2O composite based on TiO2 NTPC photoanode for photoelectrochemical (PEC) water splitting under visible light

    KAUST Repository

    Shi, Le

    2015-01-01

    in practice of water splitting with pure TiO2 material, one of the most popular semiconductor material used for photoelectrochemical water splitting, is still challenging. One dimensional TiO2 nanotubes is highly desired with its less recombination

  8. Charge transfer between biogenic jarosite derived Fe3+and TiO2 enhances visible light photocatalytic activity of TiO2.

    Science.gov (United States)

    Chowdhury, Mahabubur; Shoko, Sipiwe; Cummings, Fransciuos; Fester, Veruscha; Ojumu, Tunde Victor

    2017-04-01

    In this work, we have shown that mining waste derived Fe 3+ can be used to enhance the photocatalytic activity of TiO 2 . This will allow us to harness a waste product from the mines, and utilize it to enhance TiO 2 photocatalytic waste water treatment efficiency. An organic linker mediated route was utilized to create a composite of TiO 2 and biogenic jarosite. Evidence of FeOTi bonding in the TiO 2 /jarosite composite was apparent from the FTIR, EFTEM, EELS and ELNEFS analysis. The as prepared material showed enhanced photocatalytic activity compared to pristine TiO 2 , biogenic jarosite and mechanically mixed sample of jarosite and TiO 2 under both simulated and natural solar irradiation. The prepared material can reduce the electrical energy consumption by 4 times compared to pristine P25 for degradation of organic pollutant in water. The material also showed good recyclability. Results obtained from sedimentation experiments showed that the larger sized jarosite material provided the surface to TiO 2 nanoparticles, which increases the settling rate of the materials. This allowed simple and efficient recovery of the catalyst from the reaction system after completion of photocatalysis. Enhanced photocatalytic activity of the composite material was due to effective charge transfer between TiO 2 and jarosite derived Fe 3+ as was shown from the EELS and ELNEFS. Generation of OH was supported by photoluminesence (PL) experiments. Copyright © 2016. Published by Elsevier B.V.

  9. Structural properties of TiO2 nanomaterials

    Science.gov (United States)

    Kusior, Anna; Banas, Joanna; Trenczek-Zajac, Anita; Zubrzycka, Paulina; Micek-Ilnicka, Anna; Radecka, Marta

    2018-04-01

    The surface of solids is characterized by active, energy-rich sites that determine physicochemical interaction with gaseous and liquid media and possible applications in photocatalysis. The behavior of materials in such processes is related to their form and amount of various species, especially water and forms of oxygen adsorbed on the surface. The preparation of materials with controlled morphology, which includes modifications of the size, geometry, and composition, is currently an important way of optimizing properties, as many of them depend on not only the size and phase composition, but also on shape. Hydroxylated centers on the surface, which can be treated as trapping sites, are particularly significant. Water adsorbed on the surface bridging hydroxyl groups can distinctly modulate the properties of the surface of titania. The saturation of the surface with hydroxyl groups may improve the photocatalytic properties. TiO2 nanomaterials were obtained via different methods. SEM and TEM analysis were performed to study the morphology. The analysis of XRD and Raman data revealed a phase composition of obtained materials. To examine the surface properties, FTIR absorption spectra of TiO2 nanomaterials were recorded. The photocatalytic activity of titanium dioxide nanoparticles was investigated through the decomposition of methylene blue. It was demonstrated that each surface modification affects the amount of adsorbed hydroxyl groups. The different contributions of the two species to the ν(H2O) FTIR bands for different nanostructures result from the preparation conditions. It was noted that pre-adsorbed water (the surface-bridging hydroxyl) might significantly modulate the surface properties of the material. The increase in hydroxyl group density on the titanium dioxide surface enhances the effectiveness of the photocatalytic processes. It was demonstrated that flower-like titania obtained via hydrothermal synthesis exhibits the weakest catalytic activity, in contrast to the typical spherical TiO2.

  10. Nanocrystalline ceramic materials

    Science.gov (United States)

    Siegel, Richard W.; Nieman, G. William; Weertman, Julia R.

    1994-01-01

    A method for preparing a treated nanocrystalline metallic material. The method of preparation includes providing a starting nanocrystalline metallic material with a grain size less than about 35 nm, compacting the starting nanocrystalline metallic material in an inert atmosphere and annealing the compacted metallic material at a temperature less than about one-half the melting point of the metallic material.

  11. Structure and properties of nanophase TiO2

    International Nuclear Information System (INIS)

    Siegel, R.W.; Hahn, H.; Ramasamy, S.; Zongquan, Li; Ting, Lu; Gronsky, R.

    1987-07-01

    Ultrafine-grained, nanophase samples of TiO 2 (rutile) were synthesized by the gas-condensation method and subsequent in-situ compaction, and then studied by transmission electron microscopy, Vickers hardness measurements, and positron annihilation spectroscopy as a function of sintering temperature. The nanophase compacts densified rapidly above 500 0 C, with only a small increase in grain size. The hardness values obtained by this method are comparable to or greater than coarser-grained compacts, but at temperatures 400 to 600 0 C lower than conventional sintering temperatures and without the need for sintering aids. 11 refs., 3 figs

  12. On Multiple Zagreb Indices of TiO2 Nanotubes.

    Science.gov (United States)

    Malik, Mehar Ali; Imran, Muhammad

    2015-01-01

    The First and Second Zagreb indices were first introduced by I. Gutman and N. Trinajstic in 1972. It is reported that these indices are useful in the study of anti-inflammatory activities of certain chemical instances, and in elsewhere. Recently, the first and second multiple Zagreb indices of a graph were introduced by Ghorbani and Azimi in 2012. In this paper, we calculate the Zagreb indices and the multiplicative versions of the Zagreb indices of an infinite class of Titania nanotubes TiO(2)[m,n].

  13. Carrier recombination dynamics in anatase TiO 2 nanoparticles

    Science.gov (United States)

    Cavigli, Lucia; Bogani, Franco; Vinattieri, Anna; Cortese, Lorenzo; Colocci, Marcello; Faso, Valentina; Baldi, Giovanni

    2010-11-01

    We present an experimental study of the radiative recombination dynamics in size-controlled TiO 2 nanoparticles in the range 20-130 nm. Time-integrated photoluminescence spectra clearly show a dominance of self-trapped exciton (STE) emission, with main features not dependent on the nanoparticle size and on its environment. From picosecond time-resolved experiments as a function of the excitation density and the nanoparticle size we address the STE recombination dynamics as the result of two main processes related to the direct STE formation and to the indirect STE formation mediated by non-radiative surface states.

  14. Al-bound hole polarons in TiO2

    International Nuclear Information System (INIS)

    Stashans, Arvids; Bermeo, Sthefano

    2009-01-01

    Changes in the structural and electronic properties of TiO 2 (anatase and rutile) due to the Al-doping are studied using a quantum-chemical approach based on the Hartree-Fock theory. The formation of hole polarons trapped at oxygen sites near the Al impurity has been discovered and their spatial configuration are discussed. The occurrence of well-localized one-center hole polarons in rutile may influence its photocatalytic activity. Optical absorption energy for this hole center is obtained, 0.4 eV, using the ΔSCF approach.

  15. Highly uniform bipolar resistive switching characteristics in TiO2/BaTiO3/TiO2 multilayer

    International Nuclear Information System (INIS)

    Ma, W. J.; Zhang, X. Y.; Wang, Ying; Zheng, Yue; Lin, S. P.; Luo, J. M.; Wang, B.; Li, Z. X.

    2013-01-01

    Nanoscale multilayer structure TiO 2 /BaTiO 3 /TiO 2 has been fabricated on Pt/Ti/SiO 2 /Si substrate by chemical solution deposition method. Highly uniform bipolar resistive switching (BRS) characteristics have been observed in Pt/TiO 2 /BaTiO 3 /TiO 2 /Pt cells. Analysis of the current-voltage relationship demonstrates that the space-charge-limited current conduction controlled by the localized oxygen vacancies should be important to the resistive switching behavior. X-ray photoelectron spectroscopy results indicated that oxygen vacancies in TiO 2 play a crucial role in the resistive switching phenomenon and the introduced TiO 2 /BaTiO 3 interfaces result in the high uniformity of bipolar resistive switching characteristics

  16. Synthesis of Fe2O3/TiO2 nanorod-nanotube arrays by filling TiO2 nanotubes with Fe

    International Nuclear Information System (INIS)

    Mohapatra, Susanta K; Banerjee, Subarna; Misra, Mano

    2008-01-01

    Synthesis of hematite (α-Fe 2 O 3 ) nanostructures on a titania (TiO 2 ) nanotubular template is carried out using a pulsed electrodeposition technique. The TiO 2 nanotubes are prepared by the sonoelectrochemical anodization method and are filled with iron (Fe) by pulsed electrodeposition. The Fe/TiO 2 composite is then annealed in an O 2 atmosphere to convert it to Fe 2 O 3 /TiO 2 nanorod-nanotube arrays. The length of the Fe 2 O 3 inside the TiO 2 nanotubes can be tuned from 50 to 550 nm by changing the deposition time. The composite material is characterized by scanning electron microscopy, transmission electron microscopy and diffuse reflectance ultraviolet-visible studies to confirm the formation of one-dimensional Fe 2 O 3 /TiO 2 nanorod-nanotube arrays. The present approach can be used for designing variable one-dimensional metal oxide heterostructures

  17. Photocatalytic activities of heterostructured TiO2-graphene porous microspheres prepared by ultrasonic spray pyrolysis

    International Nuclear Information System (INIS)

    Yang, Jikai; Zhang, Xintong; Li, Bing; Liu, Hong; Sun, Panpan; Wang, Changhua; Wang, Lingling; Liu, Yichun

    2014-01-01

    Highlights: • USP method is used to prepare TiO 2 -graphene porous microspheres. • XPS shows GO sheets in the composites has been reduced to graphene. • TiO 2 -graphene microspheres display a red-shifted absorption edge. • PL spectra indicate graphene can accept the photoexcited electrons from TiO 2 . • TiO 2 -graphene shows higher photocatalytic activity than TiO 2 under solar light. -- Abstract: TiO 2 -graphene porous microspheres were prepared by ultrasonic spray pyrolysis (USP) of aqueous suspension of graphene oxide containing TiO 2 nanoparticles (Degussa P25). The composite microspheres were characterized with SEM, XPS, photoluminescence, Raman and UV–Vis absorption spectra. TiO 2 -graphene porous microspheres displayed higher photocatalytic activity for the degradation of methylene blue solution than pristine TiO 2 microspheres under the irradiation of Xe lamp, and the highest activity was obtained at a weight percentage of graphene around 1%. The effect of graphene on photocatalytic activity of porous microsphere was discussed in terms of the enhanced charge separation by TiO 2 -graphene heterojunction, increased absorption of the visible light, as well as the possible hindrance of mass transportation in microspheres

  18. Photocatalytic Decolorization Study of Methyl Orange by TiO2–Chitosan Nanocomposites

    Directory of Open Access Journals (Sweden)

    Imelda Fajriati

    2014-10-01

    Full Text Available The photocatalytic decolorization of methyl orange (MO by TiO2-chitosan nanocomposite has been studied. This study was started by synthesizing TiO2-chitosan nanocomposites using sol-gel method with various concentrations of Titanium(IV isopropoxide (TTIP as the TiO2 precursor. The structure, surface morphology, thermal and optical property of TiO2-chitosan nanocomposite were characterized by X-ray diffraction (XRD, fourier transform infra red (FTIR spectroscopy, scanning electron microscopy (SEM, thermogravimetric analysis (TGA, and diffuse reflectance ultra violet (DRUV spectroscopy. The photocatalytic activity of TiO2-chitosan nanocomposite was evaluated by photocatalytic decolorization of methyl orange as a model pollutant. The results indicate that the particle size of TiO2 increases with increasing ofthe concentration of TTIP, in which TiO2 with smallest particle size exhibit the highest photocatalytic activity. The highest photocatalytic decolorization was obtained at 5 h of contact time, initial concentration of MO at 20 ppm and at solution pH of 4. Using these conditions, over 90% of MO was able to be decolorized using 0.02 g of TiO2-chitosan nanocomposite under UV light irradiation. The TiO2-chitosan nanocomposite could be reused, which meant that the TiO2-chitosan nanocomposites can be developed as an effective and economical photocatalyst to decolorize or treat dye in wastewater.

  19. The Influence of NiO Addition in TiO2 Structure and Its Photoactivity

    Science.gov (United States)

    Wahyuningsih, S.; Ramelan, A. H.; Purwanti, P. D.; Munawaroh, H.; Ichsan, S.; Kristiawan, Y. R.

    2018-03-01

    The synthesis of TiO2 together with the TiO2-NiO composite using various annealing temperatures has been studied. The synthesis of TiO2 was performed by sol gel method using Titanium Tetra Isopropoxide (TTIP) precursor, whereas the synthesis of TiO2-NiO composite was done by wet impregnation method using NiNO3.6H2O precursor. This study aims to determine the influence of NiO addition in its structure and photoactivity. The diffraction of synthesized TiO2 at 400 °C temperature shows anatase TiO2 peak at 2θ = 25.35 °. The addition of NiO dopant to the synthesis of TiO2 process is carried out by annealing at 300 °C, 400 °C, 500 °C, 600 °C, and 700 °C, respectively. The TiO2-NiO composite has been prepared and shows the diffraction peak of NiO at 2θ=43° about 33.08 to 36.68%. The optimum result of Rhodamine B photodegradation with TiO2 was 43.15%, while the optimum result of Rhodamine B degradation with TiO2-NiO composite was 92.85%.

  20. A thick hierarchical rutile TiO2 nanomaterial with multilayered structure

    International Nuclear Information System (INIS)

    Zhu, Shengli; Xie, Guoqiang; Yang, Xianjin; Cui, Zhenduo

    2013-01-01

    Highlights: ► We synthesized a new rutile TiO 2 nanomaterial with a hierarchical nanostructure. ► The nano architecture structure consist of nanorods and nanoflower arrays. ► The rutile TiO 2 nanomaterial is thick in size (several 10 μm). ► The TiO 2 nanomaterials present a multilayer structure. - Abstract: In the present paper, we synthesized a new type of rutile TiO 2 nanomaterial with a hierarchical nanostructure using a novel method, which combined dealloying process with chemical synthesis. The structure characters were examined using X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The rutile TiO 2 nanomaterial is thick in size (several 10 μm). The hierarchical structure of the rutile TiO 2 nanomaterial consists of large quantities nanorods and nanoflower arrays. The nanoflowers consist of serveral nanopetals with diameter of 100–200 nm. The cross section of TiO 2 nanomaterials presents a multilayer structure with the layer thickness of about 3–5 μm. The rutile TiO 2 nanomaterial has high specific surface area. The formation mechanism of the rutile TiO 2 nanomaterial was discussed according to the experimental results. The rutile TiO 2 nanomaterial has potential applications in catalysis, photocatalysis and solar cells

  1. Preparation of rutile TiO(2) coating by thermal chemical vapor deposition for anticoking applications.

    Science.gov (United States)

    Tang, Shiyun; Wang, Jianli; Zhu, Quan; Chen, Yaoqiang; Li, Xiangyuan

    2014-10-08

    To inhibit the metal catalytic coking and improve the oxidation resistance of TiN coating, rutile TiO2 coating has been directly designed as an efficient anticoking coating for n-hexane pyrolysis. TiO2 coatings were prepared on the inner surface of SS304 tubes by a thermal CVD method under varied temperatures from 650 to 900 °C. The rutile TiO2 coating was obtained by annealing the as-deposited TiO2 coating, which is an alternative route for the deposition of rutile TiO2 coating. The morphology, elemental and phase composition of TiO2 coatings were characterized by SEM, EDX and XRD, respectively. The results show that deposition temperature of TiO2 coatings has a strong effect on the morphology and thickness of as-deposited TiO2 coatings. Fe, Cr and Ni at.% of the substrate gradually changes to 0 when the temperature is increased to 800 °C. The thickness of TiO2 coating is more than 6 μm and uniform by metalloscopy, and the films have a nonstoichiometric composition of Ti3O8 when the deposition temperature is above 800 °C. The anticoking tests show that the TiO2 coating at a deposition temperature of 800 °C is sufficiently thick to cover the cracks and gaps on the surface of blank substrate and cut off the catalytic coke growth effect of the metal substrate. The anticoking ratio of TiO2 coating corresponding to each 5 cm segments is above 65% and the average anticoking ratio of TiO2 coating is up to 76%. Thus, the TiO2 coating can provide a very good protective layer to prevent the substrate from severe coking efficiently.

  2. Exchange of TiO2 nanoparticles between streams and streambeds.

    Science.gov (United States)

    Boncagni, Natalia Ticiana; Otaegui, Justo Manuel; Warner, Evelyn; Curran, Trisha; Ren, Jianhong; de Cortalezzi, Maria Marta Fidalgo

    2009-10-15

    The expanding use of manufactured nanoparticles has increased the potential for their release into the natural environment. Particularly, TiO2 nanoparticles pose significant exposure risk to humans and other living species due to their extensive use in a wide range of fields. To better understand the environmental and health risks associated with the release of TiO2 nanoparticles, knowledge on their fate and transport is needed. This study evaluates the transport of two different TiO2 nanoparticles: one commercially available (P25 TiO2 and the other synthesized at a lab scale (synthesized TiO2). Laboratory flume, column, and batch experiments were conducted to investigate the processes dominating the transport of TiO2 nanoparticles between streams and streambeds and to characterize the properties of these nanoparticles under different physicochemical conditions. Results show that the synthesized TiO2 was more stable compared to the P25 TiO2, which underwent significant aggregation under the same experimental conditions. As a result, P25 TiO2 deposited at a faster rate than the synthesized TiO2 in the streambed. Both types of TiO2 nanoparticles deposited in the streambed were easily released when the stream velocity was increased. The aggregation and deposition of P25 TiO2 were highly dependent on pH. A process-based colloid exchange model was applied to interpret the observed transport behavior of the TiO2 nanoparticles.

  3. Microwave-assisted self-doping of TiO2 photonic crystals for efficient photoelectrochemical water splitting

    KAUST Repository

    Zhang, Zhonghai; Yang, Xiulin; Hedhili, Mohamed N.; Ahmed, Elaf S.; Shi, Le; Wang, Peng

    2014-01-01

    In this article, we report that the combination of microwave heating and ethylene glycol, a mild reducing agent, can induce Ti3+ self-doping in TiO2. A hierarchical TiO2 nanotube array with the top layer serving as TiO2 photonic crystals (TiO2 NTPCs

  4. Photoluminescence studies on Eu doped TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Ningthoujam, R.S.; Sudarsan, V.; Vatsa, R.K.; Kadam, R.M.; Jagannath; Gupta, A.

    2009-01-01

    Eu 3+ doped TiO 2 nanoparticles were prepared by urea hydrolysis in ethylene glycol medium at low temperature of 150 deg. C. X-ray diffraction study showed that anatase phase of tetragonal structure was formed below 500 deg. C; and above this temperature, additional peaks due to rutile phase were also observed. From luminescence study, it was found that as prepared nanoparticles showed the enhanced luminescence intensity due to energy transfer from host to europium ions. However, photoluminescence from these nanoparticles was found to disappear when the samples were heated above 900 deg. C. We established the origin of the reduction in the luminescence intensity from Eu 3+ when doped in TiO 2 and heated at 900 deg. C. Based on detailed studies at different heat-treatment temperatures using techniques such as X-ray diffraction, X-ray photoelectron spectroscopy, electron paramagnetic resonance, Raman spectroscopy, and Moessbauer spectroscopy, it has been established that formation of Eu 2 Ti 2 O 7 phase, wherein Eu 3+ ions occupy high symmetric environment (D 3d ) and also reduced distance between Eu 3+ and Eu 3+ ions is responsible for the decrease/loss in the luminescence intensity.

  5. Unconventional cells of TiO2 doped with erbium

    International Nuclear Information System (INIS)

    Ribeiro, P.C.; Campos, R.D.; Oliveira, A.S.; Wellen, R.; Diniz, V.C.S.; Costa, A.C.F.M. da

    2016-01-01

    The technology used in TiO_2 solar cells is in constant improvement, new configurations have been developed, aiming practicality and leading to efficiency increase of photovoltaic devices. This paper proposes a new technology for the production of solar cells in order to investigate a better utilization of solar spectrum of TiO2 doped with erbium (Er"3"+), proven by energetic conversion. The Ti_0_,_9Er_0_,_1O2 system was obtained by Pechini method. Nanoparticles have a crystallite size 65.30 nm and surface area 118.48 m"2/g. These characteristics are essential for the formation of the film to be deposited on the conductive glass substrate constituting the cell's photoelectrode. The other side of the cell is the platinum counter electrode. The cell will have the faces sealed by a thermoplastic and, finally the electrolyte will be inserted, then they will be electrically evaluated through energy efficiency and confronted with the literature data base. (author)

  6. Fabrication and characterization of TiO2-epoxy nanocomposite

    International Nuclear Information System (INIS)

    Chatterjee, Amit; Islam, Muhammad S.

    2008-01-01

    A systematic study has been conducted to investigate the matrix properties by introducing nanosize TiO 2 (5-40 nm, 0.5-2% by weight) fillers into an epoxy resin. Ultrasonic mixing process, via sonic cavitations, was employed to disperse the particles into the resin system. The thermal, mechanical, morphology and the viscoelastic properties of the nanocomposite and the neat resin were measured with TGA, DMA, TEM and Instron. The nano-particles are dispersed evenly throughout the entire volume of the resin. The nanofiller infusion improves the thermal, mechanical and viscoelastic properties of the epoxy resin. The nanocomposite shows increase in storage modulus, glass transition temperature, tensile modulus, flexural modulus and short beam shear strength from neat epoxy resin. The mechanical performance and thermal stability of the epoxy nanocomposites are depending on with the dispersion state of the TiO 2 in the epoxy matrix and are correlated with loading (0.0015-0.006% by volume). In addition, the nanocomposite shows enhanced flexural strength. Several reasons to explain these effects in terms of reinforcing mechanisms were discussed

  7. Electrical conductivity characteristic of TiO2 nanowires from hydrothermal method

    International Nuclear Information System (INIS)

    Othman, Mohd Azlishah; Amat, Noor Faridah; Ahmad, Badrul Hisham; Rajan, Jose

    2014-01-01

    One dimensional nanostructures of titanium dioxide (TiO 2 ) were synthesized via hydrothermal method by mixing TiO 2 as precursor in aqueous solution of NaOH as solvent. Then, heat and washing treatment was applied. Thus obtained wires had diameter ∼15 nm. TiO 2 nanowires will be used as a network in solar cell such dye-sensitized solar cell in order to improve the performance of electron movement in the device. To improve the performance of electron movement, the characteristics of TiO 2 nanowires have been analyses using field emission scanning electron microscopy (FESEM) analysis, x-ray diffractometer (XRD) analysis and brunauer emmett teller (BET) analysis. Finally, electrical conductivity of TiO 2 nanowires was determined by measuring the resistance of the TiO 2 nanowires paste on microscope glass.

  8. Optimization of photoelectrochemical water splitting performance on hierarchical TiO 2 nanotube arrays

    KAUST Repository

    Zhang, Z.; Wang, Peng

    2012-01-01

    In this paper, we show that by varying the voltages during two-step anodization the morphology of the hierarchical top-layer/bottom-tube TiO 2 (TiO 2 NTs) can be finely tuned between nanoring/nanotube, nanopore/nanotube, and nanohole-nanocave/nanotube morphologies. This allows us to optimize the photoelectrochemical (PEC) water splitting performance on the hierarchical TiO 2 NTs. The optimized photocurrent density and photoconversion efficiency in this study, occurring on the nanopore/nanotube TiO 2 NTs, were 1.59 mA cm -2 at 1.23 V vs. RHE and 0.84% respectively, which are the highest values ever reported on pristine TiO 2 materials under illumination of AM 1.5G. Our findings contribute to further improvement of the energy conversion efficiency of TiO 2-based devices.

  9. Reflectance spectroscopy from TiO2 particles embedded in polyurethane

    DEFF Research Database (Denmark)

    Gudla, Visweswara Chakravarthy; Canulescu, Stela; Johansen, Villads Egede

    2013-01-01

    This paper presents the results of a physical simulation carried out using TiO2-Polyurethane composite coating on bright aluminium surface to understand the light scattering effect for designing white surfaces. Polyurethane matrix is selected due to the matching refractive index (1.7) with Al2O3...... layer on anodized aluminium surfaces. Three different TiO2 particle distributions were dispersed in polyurethane and spin coated onto high gloss and caustic etched aluminium substrates. Reflectance spectra of TiO2-polyurethane films of various concentrations were analysed using an integrating sphere....... The results show that the TiO2-polyurethane coatings have a high diffuse reflectance as a result of multiple scattering from TiO2 particles. Diffuse reflectance spectra of TiO2 containing films vary weakly with particle concentration and reach a steady state value at a concentration of 0.75 wt.%. Using...

  10. Photodegradation of Reactive Golden Yellow R Dye Catalyzed by Effective Titania (TiO2)

    International Nuclear Information System (INIS)

    Bedurus, E.A.; Marinah Mohd Ariffin; Mohd Hasmizam Razali

    2015-01-01

    In the present research, Microwave Assisted Synthesis (MAS) method was applied to synthesize titania (TiO 2 ) at 150 degree Celsius in a range of 2-6 hours heating time. Each prepared TiO 2 were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and nitrogen gas (N 2 ) sorption analysis (Brunaeur-Emmett-Teller (BET) and Barrett-Joyner-Halenda (BJH) calculation) techniques. The TiO 2 prepared by MAS 150 degree Celsius (4 hours) has emerged with the highest photo catalytic activity. Within 4 hours, the TiO 2 managed to catalyze the degradation of Reactive Golden Yellow R dye up to 98.51 %. This is because of the TiO 2 possessed high crystallinity of anatase phase, small crystallite size and high pore volume compared to other prepared TiO 2 . (author)

  11. Optimization of photoelectrochemical water splitting performance on hierarchical TiO 2 nanotube arrays

    KAUST Repository

    Zhang, Z.

    2012-02-10

    In this paper, we show that by varying the voltages during two-step anodization the morphology of the hierarchical top-layer/bottom-tube TiO 2 (TiO 2 NTs) can be finely tuned between nanoring/nanotube, nanopore/nanotube, and nanohole-nanocave/nanotube morphologies. This allows us to optimize the photoelectrochemical (PEC) water splitting performance on the hierarchical TiO 2 NTs. The optimized photocurrent density and photoconversion efficiency in this study, occurring on the nanopore/nanotube TiO 2 NTs, were 1.59 mA cm -2 at 1.23 V vs. RHE and 0.84% respectively, which are the highest values ever reported on pristine TiO 2 materials under illumination of AM 1.5G. Our findings contribute to further improvement of the energy conversion efficiency of TiO 2-based devices.

  12. Engineering of highly ordered TiO2 nanopore arrays by anodization

    Science.gov (United States)

    Wang, Huijie; Huang, Zhennan; Zhang, Li; Ding, Jie; Ma, Zhaoxia; Liu, Yong; Kou, Shengzhong; Yang, Hangsheng

    2016-07-01

    Finite element analysis was used to simulate the current density distributions in the TiO2 barrier layer formed at the initial stage of Ti anodization. The morphology modification of the barrier layer was found to induce current density distribution change. By starting the anodization with proper TiO2 barrier layer morphology, the current density distribution can be adjusted to favor the formation of either nanotube arrays or nanopore arrays of anodic TiO2. We also found that the addition of sodium acetate into the electrolyte suppressed both the field-assisted chemical dissolution of TiO2 and the TiF62- hydrolysis induced TiO2 deposition during anodization, and thus further favored the nanopore formation. Accordingly, highly ordered anodic TiO2 nanopore arrays, similar to anodic aluminum oxide nanopore arrays, were successfully prepared.

  13. XRD analysis of undoped and Fe doped TiO2 nanoparticles by Williamson Hall method

    International Nuclear Information System (INIS)

    Bharti, Bandna; Barman, P. B.; Kumar, Rajesh

    2015-01-01

    Undoped and Fe doped titanium dioxide (TiO 2 ) nanoparticles were synthesized by sol-gel method at room temperature. The synthesized samples were annealed at 500°C. For structural analysis, the prepared samples were characterized by X-ray diffraction (XRD). The crystallite size of TiO 2 and Fe doped TiO 2 nanoparticles were calculated by Scherer’s formula, and was found to be 15 nm and 11 nm, respectively. Reduction in crystallite size of TiO 2 with Fe doping was observed. The anatase phase of Fe-doped TiO 2 nanoparticles was also confirmed by X-ray diffraction. By using Williamson-Hall method, lattice strain and crystallite size were also calculated. Williamson–Hall plot indicates the presence of compressive strain for TiO 2 and tensile strain for Fe-TiO 2 nanoparticles annealed at 500°C

  14. Effect of surface ethoxy groups on photoactivity of TiO2 nanocrystals

    International Nuclear Information System (INIS)

    Tian Lihong; Deng Kejian; Ye Liqun; Zan Lin

    2011-01-01

    TiO 2 nanocrystals modified by ethoxy groups were prepared by a facile nonhydrolytic solvothermal method and characterized by XRD, TEM, TG-DTA and XPS, which showed an enhanced visible-light photocatalytic activity on the degradation of Rhodamine B compared with TiO 2 modified by benzyloxy groups and the 'naked' TiO 2 . The adsorption and degradation pathway of Rhodamine B on TiO 2 modified by ethoxy groups were also investigated. The zeta-potential (ζ) results showed that the TiO 2 modified by ethoxy groups had high negative surface charge, which incited the positive -N(Et) 2 group of RhB absorbing on the TiO 2 surface and preferably led the N-dealkylation pathway under visible light irradiation.

  15. An innovative approach to synthesize highly-ordered TiO2 nanotubes.

    Science.gov (United States)

    Isimjan, Tayirjan T; Yang, D Q; Rohani, Sohrab; Ray, Ajay K

    2011-02-01

    An innovative route to prepare highly-ordered and dimensionally controlled TiO2 nanotubes has been proposed using a mild sonication method. The nanotube arrays were prepared by the anodization of titanium in an electrolyte containing 3% NH4F and 5% H2O in glycerol. It is demonstrated that the TiO2 nanostructures has two layers: the top layer is TiO2 nanowire and underneath is well-ordered TiO2 nanotubes. The top layer can easily fall off and form nanowires bundles by implementing a mild sonication after a short annealing time. We found that the dimensions of the TiO2 nanotubes were only dependent on the anodizing condition. The proposed technique may be extended to fabricate reproducible well-ordered TiO2 nanotubes with large area on other metals.

  16. Graphene-enhanced Raman imaging of TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Naumenko, Denys; Snitka, Valentinas; Snopok, Boris; Arpiainen, Sanna; Lipsanen, Harri

    2012-01-01

    The interaction of anatase titanium dioxide (TiO 2 ) nanoparticles with chemical vapour deposited graphene sheets transferred on glass substrates is investigated by using atomic force microscopy, Raman spectroscopy and imaging. Significant electronic interactions between the nanoparticles of TiO 2 and graphene were found. The changes in the graphene Raman peak positions and intensity ratios indicate that charge transfer between graphene and TiO 2 nanoparticles occurred, increasing the Raman signal of the TiO 2 nanoparticles up to five times. The normalized Raman intensity of TiO 2 nanoparticles per their volume increased with the disorder of the graphene structure. The complementary reason for the observed enhancement is that due to the higher density of states in the defect sites of graphene, a higher electron transfer occurs from the graphene to the anatase TiO 2 nanoparticles. (paper)

  17. Enhanced photoelectrochemical and photocatalytic activity of WO3-surface modified TiO2 thin film

    Science.gov (United States)

    Qamar, Mohammad; Drmosh, Qasem; Ahmed, Muhammad I.; Qamaruddin, Muhammad; Yamani, Zain H.

    2015-02-01

    Development of nanostructured photocatalysts for harnessing solar energy in energy-efficient and environmentally benign way remains an important area of research. Pure and WO3-surface modified thin films of TiO2 were prepared by magnetron sputtering on indium tin oxide glass, and photoelectrochemical and photocatalytic activities of these films were studied. TiO2 particles were <50 nm, while deposited WO3 particles were <20 nm in size. An enhancement in the photocurrent was observed when the TiO2 surface was modified WO3 nanoparticles. Effect of potential, WO3 amount, and radiations of different wavelengths on the photoelectrochemical activity of TiO2 electrodes was investigated. Photocatalytic activity of TiO2 and WO3-modified TiO2 for the decolorization of methyl orange was tested.

  18. Ammonia Sensing Behaviors of TiO2-PANI/PA6 Composite Nanofibers

    Directory of Open Access Journals (Sweden)

    Fenglin Huang

    2012-12-01

    Full Text Available Titanium dioxide-polyaniline/polyamide 6 (TiO2-PANI/PA6 composite nanofibers were prepared by in situ polymerization of aniline in the presence of PA6 nanofibers and a sputtering-deposition process with a high purity titanium sputtering target. TiO2-PANI/PA6 composite nanofibers and PANI/PA6 composite nanofibers were fabricated for ammonia gas sensing. The ammonia sensing behaviors of the sensors were examined at room temperature. All the results indicated that the ammonia sensing property of TiO2-PANI/PA6 composite nanofibers was superior to that of PANI/PA6 composite nanofibers. TiO2-PANI/PA6 composite nanofibers had good selectivity to ammonia. It was also found that the content of TiO2 had a great influence on both the morphology and the sensing property of TiO2-PANI/PA6 composite nanofibers.

  19. Eco-friendly synthesis of TiO2, Au and Pt doped TiO2 nanoparticles for dye sensitized solar cell applications and evaluation of toxicity

    Science.gov (United States)

    Gopinath, K.; Kumaraguru, S.; Bhakyaraj, K.; Thirumal, S.; Arumugam, A.

    2016-04-01

    Driven by the demand of pure TiO2, Au and Pt doped TiO2 NPs were successfully synthesized using Terminalia arjuna bark extract. The eco-friendly synthesized NPs were characterized by UV-Vis-DRS, ATR-FT-IR, PL, XRD, Raman, SEM with EDX and TEM analysis. The synthesized NPs were investigation for dye sensitized solar cell applications. UV-Vis-Diffused Reflectance Spectra clearly showed that the expected TiO2 inter band absorption below 306 nm, incorporation of gold shows surface plasma resonant (SPR) near 555 nm and platinum incorporated TiO2 NPs shows absorbance at 460 nm. The energy conversion efficiency for Au doped TiO2 NPs when compared to pure and Pt doped TiO2 NPs. In addition to that, Au noble metal present TiO2 matrix and an improve open-circuit voltage (Voc) of DSSC. Synthesized NPs was evaluated into antibacterial and antifungal activities by disk diffusion method. It is observed that NPs have not shown any activities in all tested bacterial and fungal strains. In this eco-friendly synthesis method to provide non toxic and environmental friendly nanomaterials can be used for solar energy device application.

  20. TiO2 nanofiber solid-state dye sensitized solar cells with thin TiO2 hole blocking layer prepared by atomic layer deposition

    International Nuclear Information System (INIS)

    Li, Jinwei; Chen, Xi; Xu, Weihe; Nam, Chang-Yong; Shi, Yong

    2013-01-01

    We incorporated a thin but structurally dense TiO 2 layer prepared by atomic layer deposition (ALD) as an efficient hole blocking layer in the TiO 2 nanofiber based solid-state dye sensitized solar cell (ss-DSSC). The nanofiber ss-DSSCs having ALD TiO 2 layers displayed increased open circuit voltage, short circuit current density, and power conversion efficiency compared to control devices with blocking layers prepared by spin-coating liquid TiO 2 precursor. We attribute the improved photovoltaic device performance to the structural integrity of ALD-coated TiO 2 layer and consequently enhanced hole blocking effect that results in reduced dark leakage current and increased charge carrier lifetime. - Highlights: • TiO 2 blocking locking layer prepared by atomic layer deposition (ALD) method. • ALD-coated TiO 2 layer enhanced hole blocking effect. • ALD blocking layer improved the voltage, current and efficiency. • ALD blocking layer reduced dark leakage current and increased electron lifetime

  1. Mesoscopic model for binary fluids

    Science.gov (United States)

    Echeverria, C.; Tucci, K.; Alvarez-Llamoza, O.; Orozco-Guillén, E. E.; Morales, M.; Cosenza, M. G.

    2017-10-01

    We propose a model for studying binary fluids based on the mesoscopic molecular simulation technique known as multiparticle collision, where the space and state variables are continuous, and time is discrete. We include a repulsion rule to simulate segregation processes that does not require calculation of the interaction forces between particles, so binary fluids can be described on a mesoscopic scale. The model is conceptually simple and computationally efficient; it maintains Galilean invariance and conserves the mass and energy in the system at the micro- and macro-scale, whereas momentum is conserved globally. For a wide range of temperatures and densities, the model yields results in good agreement with the known properties of binary fluids, such as the density profile, interface width, phase separation, and phase growth. We also apply the model to the study of binary fluids in crowded environments with consistent results.

  2. Engineering the TiO2 -graphene interface to enhance photocatalytic H2 production.

    Science.gov (United States)

    Liu, Lichen; Liu, Zhe; Liu, Annai; Gu, Xianrui; Ge, Chengyan; Gao, Fei; Dong, Lin

    2014-02-01

    In this work, TiO2 -graphene nanocomposites are synthesized with tunable TiO2 crystal facets ({100}, {101}, and {001} facets) through an anion-assisted method. These three TiO2 -graphene nanocomposites have similar particle sizes and surface areas; the only difference between them is the crystal facet exposed in TiO2 nanocrystals. UV/Vis spectra show that band structures of TiO2 nanocrystals and TiO2 -graphene nanocomposites are dependent on the crystal facets. Time-resolved photoluminescence spectra suggest that the charge-transfer rate between {100} facets and graphene is approximately 1.4 times of that between {001} facets and graphene. Photoelectrochemical measurements also confirm that the charge-separation efficiency between TiO2 and graphene is greatly dependent on the crystal facets. X-ray photoelectron spectroscopy reveals that Ti-C bonds are formed between {100} facets and graphene, while {101} facets and {001} facets are connected with graphene mainly through Ti-O-C bonds. With Ti-C bonds between TiO2 and graphene, TiO2 -100-G shows the fastest charge-transfer rate, leading to higher activity in photocatalytic H2 production from methanol solution. TiO2 -101-G with more reductive electrons and medium interfacial charge-transfer rate also shows good H2 evolution rate. As a result of its disadvantageous electronic structure and interfacial connections, TiO2 -001-G shows the lowest H2 evolution rate. These results suggest that engineering the structures of the TiO2 -graphene interface can be an effective strategy to achieve excellent photocatalytic performances. Copyright © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  3. Characterization of manufactured TiO2 nanoparticles

    Science.gov (United States)

    Motzkus, C.; Macé, T.; Vaslin-Reimann, S.; Ausset, P.; Maillé, M.

    2013-04-01

    Technological advances in nanomaterials have allowed the development of new applications in industry, increasing the probability of finding airborne manufactured and engineered nano-objects in the workplace, as well as in ambient air. Scientific studies on health and environmental risks have indicated that airborne nano-objects in ambient air have potential adverse effects on the health of exposed workers and the general population. For regulatory purposes, ambient measurements of particulate matter are based on the determination of mass concentrations for PM10 and PM2.5, as regulated in the European Directive 2008/50/EC. However, this legislation is not suitable for airborne manufactured and engineered nano-objects. Parameters characterising ultrafine particles, such as particle number concentration and size distribution, are under consideration for future health-based legislation, to monitor workplaces and to control industrial processes. Currently, there are no existing regulations covering manufactured airborne nano-objects. There is therefore a clear, unaddressed need to focus on the toxicology and exposure assessment of nano-objects such as titanium dioxide (TiO2), which are manufactured and engineered in large quantities in industry. To perform reliable toxicology studies it is necessary to determine the relevant characteristics of nano-objects, such as morphology, surface area, agglomeration, chemical composition, particle size and concentration, by applying traceable methods. Manufacturing of nanomaterials, and their use in industrial applications, also require traceable characterisation of the nanomaterials, particularly for quality control of the process. The present study arises from the OECD WPMN sponsorship programme, supported by the French Agency for Environmental and Occupational Health Safety (ANSES), in order to develop analytical methods for the characterization of TiO2 nanoparticles in size and count size distribution, based on different techniques to characterize five different manufactured TiO2 nanoparticles. In this study, different measurement techniques have been implemented: Transmission Electron Microscopy (TEM), Scanning Mobility Particle Sizer (SMPS) and Aerodynamic Particle Sizer (APS). The TEM results lead to a relatively good agreement between data from the manufacturer and our characterizations of primary particle size. With regard to the dustiness, the results show a strong presence of agglomerates / aggregates of primary particles and a significant presence of emitted airborne nanoparticles with a diameter below 100 nm (composed of isolated primary particles and small aggregates / agglomerates formed from a few primary particles): the number proportion of these particles varies from 0 to 44 % in the measurement range 14-360 nm depending on the types of powders and corrections of measurements.

  4. Characterization of manufactured TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Motzkus, C; Macé, T; Vaslin-Reimann, S; Ausset, P; Maillé, M

    2013-01-01

    Technological advances in nanomaterials have allowed the development of new applications in industry, increasing the probability of finding airborne manufactured and engineered nano-objects in the workplace, as well as in ambient air. Scientific studies on health and environmental risks have indicated that airborne nano-objects in ambient air have potential adverse effects on the health of exposed workers and the general population. For regulatory purposes, ambient measurements of particulate matter are based on the determination of mass concentrations for PM10 and PM2.5, as regulated in the European Directive 2008/50/EC. However, this legislation is not suitable for airborne manufactured and engineered nano-objects. Parameters characterising ultrafine particles, such as particle number concentration and size distribution, are under consideration for future health-based legislation, to monitor workplaces and to control industrial processes. Currently, there are no existing regulations covering manufactured airborne nano-objects. There is therefore a clear, unaddressed need to focus on the toxicology and exposure assessment of nano-objects such as titanium dioxide (TiO 2 ), which are manufactured and engineered in large quantities in industry. To perform reliable toxicology studies it is necessary to determine the relevant characteristics of nano-objects, such as morphology, surface area, agglomeration, chemical composition, particle size and concentration, by applying traceable methods. Manufacturing of nanomaterials, and their use in industrial applications, also require traceable characterisation of the nanomaterials, particularly for quality control of the process. The present study arises from the OECD WPMN sponsorship programme, supported by the French Agency for Environmental and Occupational Health Safety (ANSES), in order to develop analytical methods for the characterization of TiO 2 nanoparticles in size and count size distribution, based on different techniques to characterize five different manufactured TiO 2 nanoparticles. In this study, different measurement techniques have been implemented: Transmission Electron Microscopy (TEM), Scanning Mobility Particle Sizer (SMPS) and Aerodynamic Particle Sizer (APS). The TEM results lead to a relatively good agreement between data from the manufacturer and our characterizations of primary particle size. With regard to the dustiness, the results show a strong presence of agglomerates / aggregates of primary particles and a significant presence of emitted airborne nanoparticles with a diameter below 100 nm (composed of isolated primary particles and small aggregates / agglomerates formed from a few primary particles): the number proportion of these particles varies from 0 to 44 % in the measurement range 14-360 nm depending on the types of powders and corrections of measurements.

  5. Positron annihilation lifetime characterization of oxygen ion irradiated rutile TiO2

    Science.gov (United States)

    Luitel, Homnath; Sarkar, A.; Chakrabarti, Mahuya; Chattopadhyay, S.; Asokan, K.; Sanyal, D.

    2016-07-01

    Ferromagnetic ordering at room temperature has been induced in rutile phase of TiO2 polycrystalline sample by O ion irradiation. 96 MeV O ion induced defects in rutile TiO2 sample has been characterized by positron annihilation spectroscopic techniques. Positron annihilation results indicate the formation of cation vacancy (VTi, Ti vacancy) in these irradiated TiO2 samples. Ab initio density functional theoretical calculations indicate that in TiO2 magnetic moment can be induced either by creating Ti or O vacancies.

  6. The effects of nanostructures on the mechanical and tribological properties of TiO2 nanotubes

    Science.gov (United States)

    Yoon, Yeoungchin; Park, Jeongwon

    2018-04-01

    TiO2 nanotubes were prepared by anodization on Ti substrates with a diameter variation of 30-100 nm, and the structure of the nanotubes were studied using x-ray diffraction and Raman spectroscopy, which confirmed the structure changes from the anatase phase to the rutile phase of TiO2 at a diameter below 50 nm. The tribological behaviors of TiO2 nanotubes were investigated with different diameters. The effectiveness of the rutile phase and the diameter size enhanced the frictional performance of TiO2 nanotubes.

  7. Annealing of TiO2 Films Deposited on Si by Irradiating Nitrogen Ion Beams

    International Nuclear Information System (INIS)

    Yokota, Katsuhiro; Yano, Yoshinori; Miyashita, Fumiyoshi

    2006-01-01

    Thin TiO2 films were deposited on Si at a temperature of 600 deg. C by an ion beam assisted deposition (IBAD) method. The TiO2 films were annealed for 30 min in Ar at temperatures below 700 deg. C. The as-deposited TiO2 films had high permittivities such 200 εo and consisted of crystallites that were not preferentially oriented to the c-axis but had an expanded c-axis. On the annealed TiO2 films, permittivities became lower with increasing annealing temperature, and crystallites were oriented preferentially to the (110) plane

  8. Synthesis of Nd3+doped TiO2 nanoparticles and Its Optical Behaviour

    Directory of Open Access Journals (Sweden)

    Ezhil Arasi S.

    2017-04-01

    Full Text Available Pure and Rare earth ion doped TiO2 nanoparticles were synthesized by Sol-gel method. The synthesized TiO2 nanoparticles were characterized by X-ray diffraction, Raman spectroscopy, UV–Vis spectroscopy and photoluminescence emission spectra. From the UV-visible measurement, the absorption edge of Nd3+-TiO2 was shifted to a higher wavelength side with decreasing band gap. Photoluminescence emission studies reveal the energy transfer mechanism of Nd3+ doped TiO2 nanoparticles explain.

  9. Defective TiO2 with oxygen vacancies: synthesis, properties and photocatalytic applications

    Science.gov (United States)

    Pan, Xiaoyang; Yang, Min-Quan; Fu, Xianzhi; Zhang, Nan; Xu, Yi-Jun

    2013-04-01

    Titanium dioxide (TiO2), as an important semiconductor metal oxide, has been widely investigated in the field of photocatalysis. The properties of TiO2, including its light absorption, charge transport and surface adsorption, are closely related to its defect disorder, which in turn plays a significant role in the photocatalytic performance of TiO2. Among all the defects identified in TiO2, oxygen vacancy is one of the most important and is supposed to be the prevalent defect in many metal oxides, which has been widely investigated both by theoretical calculations and experimental characterizations. Here, we give a short review on the existing strategies for the synthesis of defective TiO2 with oxygen vacancies, and the defect related properties of TiO2 including structural, electronic, optical, dissociative adsorption and reductive properties, which are intimately related to the photocatalytic performance of TiO2. In particular, photocatalytic applications with regard to defective TiO2 are outlined. In addition, we offer some perspectives on the challenge and new direction for future research in this field. We hope that this tutorial minireview would provide some useful contribution to the future design and fabrication of defective semiconductor-based nanomaterials for diverse photocatalytic applications.Titanium dioxide (TiO2), as an important semiconductor metal oxide, has been widely investigated in the field of photocatalysis. The properties of TiO2, including its light absorption, charge transport and surface adsorption, are closely related to its defect disorder, which in turn plays a significant role in the photocatalytic performance of TiO2. Among all the defects identified in TiO2, oxygen vacancy is one of the most important and is supposed to be the prevalent defect in many metal oxides, which has been widely investigated both by theoretical calculations and experimental characterizations. Here, we give a short review on the existing strategies for the synthesis of defective TiO2 with oxygen vacancies, and the defect related properties of TiO2 including structural, electronic, optical, dissociative adsorption and reductive properties, which are intimately related to the photocatalytic performance of TiO2. In particular, photocatalytic applications with regard to defective TiO2 are outlined. In addition, we offer some perspectives on the challenge and new direction for future research in this field. We hope that this tutorial minireview would provide some useful contribution to the future design and fabrication of defective semiconductor-based nanomaterials for diverse photocatalytic applications. Electronic supplementary information (ESI) available. See DOI: 10.1039/c3nr00476g

  10. Enhancing lipid productivity of Chlorella vulgaris using oxidative stress by TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Kang, Nam Kyu; Lee, Bongsoo; Choi, Gang-Guk; Moon, Myounghoon; Park, Min S.; Yang, Ji-Won; Lim, JitKang

    2014-01-01

    Ability to increase the lipid production in microalgae is one of the heavily sought-after ideas to improve the economic feasibility of microalgae-derived transportation fuels for commercial applications. We used the oxidative stress by TiO 2 nanoparticles, a well-known photocatalyst, to induce lipid production in microalgae. Chlorella vulgaris UTEX 265 was cultivated under various concentrations of TiO 2 ranging from 0.1 to 5 g/L under UV-A illumination. Maximum specific growth rate was affected in responding to TiO 2 concentrations. In the presence of UV-A, chlorophyll concentration was decreased at the highest concentration of TiO 2 (5 g/L TiO 2 ) by oxidative stress. The fatty acid methyl ester (FAME) composition analysis suggested that oxidative stress causes the accumulation and decomposition of lipids. The highest FAME productivity was 18.2 g/L/d under low concentrations of TiO 2 (0.1 g/L) and a short induction time (two days). The controlled condition of TiO 2 /UV-A inducing oxidative stress (0.1 g/L TiO 2 and two days induction) could be used to increase the lipid productivity of C. vulgaris UTEX 265. Our results show the possibility of modulating the lipid induction process through oxidative stress with TiO 2 /UV-A

  11. Flow-Regulated Growth of Titanium Dioxide (TiO2 ) Nanotubes in Microfluidics.

    Science.gov (United States)

    Fan, Rong; Chen, Xinye; Wang, Zihao; Custer, David; Wan, Jiandi

    2017-08-01

    Electrochemical anodization of titanium (Ti) in a static, bulk condition is used widely to fabricate self-organized TiO 2 nanotube arrays. Such bulk approaches, however, require extended anodization times to obtain long TiO 2 nanotubes and produce only vertically aligned nanotubes. To date, it remains challenging to develop effective strategies to grow long TiO 2 nanotubes in a short period of time, and to control the nanotube orientation. Here, it is shown that the anodic growth of TiO 2 nanotubes is significantly enhanced (≈16-20 times faster) under flow conditions in microfluidics. Flow not only controls the diameter, length, and crystal orientations of TiO 2 nanotubes, but also regulates the spatial distribution of nanotubes inside microfluidic devices. Strikingly, when a Ti thin film is deposited on silicon substrates and anodized in microfluidics, both vertically and horizontally aligned (relative to the bottom substrate) TiO 2 nanotubes can be produced. The results demonstrate previously unidentified roles of flow in the regulation of growth of TiO 2 nanotubes, and provide powerful approaches to effectively grow long, oriented TiO 2 nanotubes, and construct hierarchical TiO 2 nanotube arrays on silicon-based materials. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  12. One-component solution system to prepare nanometric anatase TiO2

    International Nuclear Information System (INIS)

    Trung, Tran; Ha, Chang-Sik

    2004-01-01

    A novel one-pot synthesis route was proposed to prepare nanometric anatase TiO 2 using trichloroethylene as reaction medium, which may have great advantage over multicomponent solution systems when TiO 2 is used as a reinforcing filler for polymers dissolved in trichloroethylene. The anatase TiO 2 nanoparticles were characterized using X-ray diffraction (XRD), scanning electron microscopy and small-angle X-ray scattering (SAXS). It was found that the diameters of TiO 2 nanoparticles are in the range from 5 to 13 nm

  13. Enhanced bonding between TiO2-Graphene oxide

    DEFF Research Database (Denmark)

    Naknikham, Usuma; Buffa, Vittorio; Yue, Yuanzheng

    analysis. Besides, the study of Ti-O-C and Ti-C interface bonding was carried out using XPS. The band-gap energy was determined using a UV-VIS spectrophotometer equipped with an integrating sphere. Thus, it was possible for us to determine the reactivity of the new photocatalysts under the visible light...... as photocatalysts, which can efficiently react with organic species under solar light and can enhance the adsorption of water pollutants [3]. Many studies have shown that TiO2-GO heterostructures can quickly mineralize organic dyes in solution under UV-light. However, it is not clear if these materials can provide...... the same performances under sunlight and with complex real water systems. Hence, this research aims to study the photocatalystic property on GO-TiO2 composites with aqueous solutions of selected emerging pollutants under visible light. The samples were synthesized via the in-situ sol-gel nucleation...

  14. Fabrication, characterization and photocatalytic properties of Ag nanoparticles modified TiO2 NTs

    International Nuclear Information System (INIS)

    Wang Qingyao; Yang Xiuchun; Liu Dan; Zhao Jianfu

    2012-01-01

    Graphical abstract: The TiO 2 NTs were first treated with bi-functional mercaptoacetic acid linkers (HOOC–R–S). The –OH group on the surface of TiO 2 NT provides a strong affinity with the carboxylate group in the linker molecules. The thiol functional group in the linker molecules facilitates the binding with Ag from AgNO 3 solution. After Ag + ions were reduced by NaBH 4 , Ag nanoparticles formed by nucleation and growth. Highlights: ► Ag nanoparticles with an average diameter of 9.2 nm were filled in the TiO 2 nanotubes by a successive ionic layer adsorption and reaction (SILAR) technique. ► Bi-functional mercaptoacetic acid linkers were used to bind TiO 2 nanotubes with Ag nanoparticles. ► Ag nanoparticles modification of TiO 2 NTs largely enhanced the photocatalytic degradation of methyl orange under ultraviolet light irradiation. - Abstract: Ordered anatase TiO 2 nanotubes (TiO 2 NTs) on Ti substrate were synthesized by electrochemical anodization and subsequently vapor-thermal treatment. Ag nanoparticles were decorated on TiO 2 NTs by successive ionic layer adsorption and reaction (SILAR) technique. Raman spectroscopy, X-ray absorption near edge spectroscopy (XANES), X-ray diffraction (XRD), UV–vis diffuse reflectance spectroscopy, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used for the characterization of surface morphology, phase composition, and microstructure of the original TiO 2 NTs, the vapor-thermally treated TiO 2 NTs and the Ag nanoparticles decorated TiO 2 NTs. The results indicate that vapor-thermal treatment favors to the transformation of amorphous TiO 2 into anatase phase. Increasing the SILAR cycle times favors to increase the loaded amounts of Ag nanoparticles in TiO 2 NTs. Ag nanoparticles are uniformly distributed in the TiO 2 NTs, and the SILAR process does not damage the ordered tubular structure. A possible formation mechanism of Ag/TiO 2 NTs has also been proposed. The photocatalytic results showed that the Ag nanoparticle modified TiO 2 NTs largely enhanced the photocatalytic degradation of methyl orange under ultraviolet light irradiation.

  15. The Effects of Anchor Groups on (1) TiO2-Catalyzed Photooxidation and (2) Linker-Assisted Assembly on TiO2

    Science.gov (United States)

    Anderson, Ian Mark

    Quantum dot-sensitized solar cells (QDSSCs) are a popular target for research due to their potential for highly efficient, easily tuned absorption. Typically, light is absorbed by quantum dots attached to a semiconductor substrate, such as TiO2, via bifunctional linker molecules. This research aims to create a patterned monolayer of linker molecules on a TiO2 film, which would in turn allow the attachment of a patterned layer of quantum dots. One method for the creation of a patterned monolayer is the functionalization of a TiO2 film with a linker molecule, followed by illumination with a laser at 355 nm. This initiates a TiO 2-catalyzed oxidation reaction, causing loss of surface coverage. A second linker molecule can then be adsorbed onto the TiO2 surface in the illuminated area. Towards that end, the behaviors of carboxylic and phosphonic acids adsorbed on TiO2 have been studied. TiO2 films were functionalized by immersion in solutions a single adsorbate and surface coverage was determined by IR spectroscopy. It is shown that phosphonic acids attain higher surface coverage than carboxylic acids, and will displace them from TiO2 when in a polar solvent. Alkyl chain lengths, which can influence stabilities of monolayers, are shown not to have an effect on this relationship. Equilibrium binding data for the adsorption of n-hexadecanoic acid to TiO2 from a THF solution are presented. It is shown that solvent polarity can affect monolayer stability; carboxylates and phosphonates undergo more desorption into polar solvents than nonpolar. Through illumination, it was possible to remove nearly all adsorbed linkers from TiO2. However, the illuminated areas were found not to be receptive to attachment by a second adsorbate. A possible reason for this behavior is presented. I also report on the synthesis and characterization of a straight-chain, thiol-terminated phosphonic acid. Initial experiments involving monolayer formation and quantum dot attachment are presented. Finally, it was found that quantum dots attach in high amounts to linker-functionalized TiO2 when suspended in pyridine. This increased surface attachment was present even when the linker molecule used lacked a functional group which would bind to the CdSe surface.

  16. The synthesis of aqueous-dispersible anatase TiO2 nanoplatelets

    International Nuclear Information System (INIS)

    Shan Guobin; Demopoulos, George P

    2010-01-01

    Aqueous well-dispersed and phase-pure anatase TiO 2 truncated octahedron nanoplatelets (NPLs) were prepared via controlled hydrolysis of titanium tetrachloride (TiCl 4 ) in ethylene glycol at 240 deg. C. Two shapes, square and hexagon, were observed by microscopy, exactly corresponding to the truncated octahedron NPLs. Ethylene glycol was found to produce water in situ that reacts with TiCl 4 to produce TiO 2 and HCl-the latter promoting TiO 2 colloid peptization. TiO 2 truncated octahedron NPLs are formed under the stabilizing action of ethylene glycol thermolysis derivatives, such as aldehydes. Crystal growth of the TiO 2 NPLs was affected by the reaction temperature that determines the water production rate and HCl-assisted peptization. TGA and FT-IR results showed ∼1.2% ethylene glycol thermolysis derivatives are attached to the surface of the TiO 2 NPLs, which prevents their agglomeration, hence making them easily dispersible in aqueous media. HR-TEM and SAED results showed that the TiO 2 NPLs are well crystallized and that the SAED patterns of the single TiO 2 NPL changes with its size and shape. XRD patterns showed that the TiO 2 NPLs are phase-pure anatase and the percentage of the {101} plane in the TiO 2 NPLs to be only 18%-a structural feature that renders the TiO 2 NPLs with enhanced UV absorption and reactivity properties.

  17. The Influence of Cr3+ on TiO2 Crystal Growth and Photoactivity Properties

    Science.gov (United States)

    Wahyuningsih, S.; Hidayatika, W. N.; Sari, P. L.; Sari, P. P.; Hidayat, R.; Munawaroh, H.; Ramelan, A. H.

    2018-03-01

    The photocatalyst technology is an integrated combination of photochemical processes and catalysis in order to carry out a chemical transformation reaction. One of the semiconductor materials that have good photocatalytic activity is TiO2 anatase. This study aim to determine the effect of the Cr3+ addition on the growth of TiO2 rutile crystal and the increasing of TiO2 photoactivity. Diffractogram X-Ray of the samples showed that the synthesized TiO2 at 400 °C has been produced 100% TiO2 anatase. Synthesis of TiO2 doped Cr3+ composite was using wet impregnation method. The TiO2 doped Cr3+ composites have beed grown by annealed at a temperature of 300, 400, 500, 600 and 700 °C, respectively Annealing process have capabled to gain to the TiO2 doped Cr3+ nanocomposite. The result product annealed at 500 °C only appear anatase phase due to the Cr3+ addition influence that was able to suppress the growth of rutile. Identification of TiO2 doped Cr3+ composite using Fourier Transform Infra-Red (FT-IR) showed O-Cr vibration at 2283.72 cm-1. The TiO2 doped Cr3+ photoactivity was studied to degrade Rhodamin B. The best result on photodegradation of Rhodamin B was performed by using TiO2 doped Cr3+ composite which was annealed at 700 °C i.e. 74.71%.

  18. Rapid detection of TiO2 (E171) in table sugar using Raman spectroscopy.

    Science.gov (United States)

    Tan, Chen; Zhao, Bin; Zhang, Zhiyun; He, Lili

    2017-02-01

    The potential toxic effects of titanium dioxide (TiO 2 ) to humans remain debatable despite its broad application as a food additive. Thus, confirmation of the existence of TiO 2 particles in food matrices and subsequently quantifying them are becoming increasingly critical. This study developed a facile, rapid (E171) from food products (e.g., table sugar) by Raman spectroscopy. To detect TiO 2 particles from sugar solution, sequential centrifugation and washing procedures were effectively applied to separate and recover 97% of TiO 2 particles from the sugar solution. The peak intensity of TiO 2 sensitively responded to the concentration of TiO 2 with a limit of detection (LOD) of 0.073 mg kg -1 . In the case of sugar granules, a mapping technique was applied to directly estimate the level of TiO 2 , which can be potentially used for rapid online monitoring. The plot of averaged intensity to TiO 2 concentration in the sugar granules exhibited a good linear relationship in the wide range of 5-2000 mg kg -1 , with an LOD of 8.46 mg kg -1 . Additionally, we applied Raman spectroscopy to prove the presence of TiO 2 in sugar-coated doughnuts. This study begins to fill in the analytical gaps that exist regarding the rapid detection and quantification of TiO 2 in food, which facilitate the risk assessment of TiO 2 through food exposure.

  19. Enhanced photoelectrocatalytic performance for degradation of diclofenac and mechanism with TiO2 nano-particles decorated TiO2 nano-tubes arrays photoelectrode

    International Nuclear Information System (INIS)

    Cheng, Xiuwen; Liu, Huiling; Chen, Qinghua; Li, Junjing; Wang, Pu

    2013-01-01

    In this study, TiO 2 nano-particles decorated TiO 2 nano-tubes arrays (TiO 2 NPs/TiO 2 NTAs) photoelectrodes have been successfully prepared through anodization, combined with ultrasonic strategy, followed by annealing post-treatment. The morphology and structure of the as-prepared TiO 2 NPs/TiO 2 NTAs photoelectrodes were characterized by scanning electrons microscopy (SEM), N 2 adsorption/desorption isotherms, X-ray diffraction (XRD) and UV–visible light diffuse reflection spectroscopy (DRS). In addition, the generation of hydroxyl radicals (·OH) was detected by a photoluminescence (PL) spectra using terephthalic acid (TA) as a probe molecule. Furthermore, the photoelectrochemical (PECH) properties of TiO 2 NPs/TiO 2 NTAs photoanode were investigated through transient open circuit potential (OCP), photocurrent response (PCR) and electrochemical impedance spectroscopy (EIS). It was found that TiO 2 NPs/TiO 2 NTAs photoelectrode exhibited a distinct decrease of OCP of −0.219 mV cm −2 and PCR of 0.049 mA cm −2 , while a significantly enhanced photoelectrocatalytic (PEC) efficiency of 63.6% (0.4 V vs. SCE) for the degradation of diclofenac. Moreover, the enhanced PEC mechanism of TiO 2 NPs/TiO 2 NTAs photoanode was proposed. The high PEC performance could be attributed to the decoration of TiO 2 NPs, which could improve the mobility and separation efficiency of photoinduced charge carriers under external potential

  20. Photocatalytic degradation of paracetamol on TiO2 nanoparticles and TiO2/cellulosic fiber under UV and sunlight irradiation

    Directory of Open Access Journals (Sweden)

    Nabil Jallouli

    2017-05-01

    Full Text Available In the present study, photocatalytic degradation of acetaminophen ((N-(4-hydroxyphe-nylacetamide, an analgesic drug has been investigated in a batch reactor using TiO2 P25 as a photocatalyst in slurry and under UV light. Using TiO2 P25 nanoparticles, much faster photodegradation of paracetamol and effective mineralization occurred, more than 90% of 2.65 × 10−4 M paracetamol was degraded under UV irradiation. Changes in pH values affected the adsorption and the photodegradation of paracetamol. pH 9.0 is found to be the optimum for the photodegradation of paracetamol. HPLC detected hydroquinone, benzoquinone, p-nitrophenol, and 1,2,4-trihydroxybenzene during the TiO2-assisted photodegradation of paracetamol among which some pathway products are disclosed for the first time. The results showed that TiO2 suspension/UV system is more efficient than the TiO2/cellulosic fiber mode combined to solar light for the photocatalytic degradation of paracetamol. Nerveless the immobilization of TiO2 showed many advantages over slurry system because it can enhance adsorption properties while allowing easy separation of the photocatalyst from the treated solution with improved reusable performance.

  1. SiO2@TiO2 Coating: Synthesis, Physical Characterization and Photocatalytic Evaluation

    Directory of Open Access Journals (Sweden)

    A. Rosales

    2018-03-01

    Full Text Available Use of silicon dioxide (SiO2 and titanium dioxide (TiO2 have been widely investigated individually in coatings technology, but their combined properties promote compatibility for different innovative applications. For example, the photocatalytic properties of TiO2 coatings, when exposed to UV light, have interesting environmental applications, such as air purification, self-cleaning and antibacterial properties. However, as reported in different pilot projects, serious durability problems, associated with the adhesion between the substrate and TiO2, have been evidenced. Thus, the aim of this work is to synthesize SiO2 together with TiO2 to increase the durability of the photocatalytic coating without affecting its photocatalytic potential. Therefore, synthesis using sonochemistry, synthesis without sonochemistry, physical characterization, photocatalytic evaluation, and durability of the SiO2, SiO2@TiO2 and TiO2 coatings are presented. Results indicate that using SiO2 improved the durability of the TiO2 coating without affecting its photocatalytic properties. Thus, this novel SiO2@TiO2 coating shows potential for developing long-lasting, self-cleaning and air-purifying construction materials.

  2. Synthesis of TiO2-doped SiO2 composite films and its applications

    Indian Academy of Sciences (India)

    Wintec

    structure of the titanium oxide species in the TiO2-doped SiO2 composite films and the photocatalytic reactiv- ity in order to ... gaku D-max γA diffractometer with graphite mono- chromized ... FT–IR absorption spectra of TiO2-doped SiO2 com-.

  3. TiO2-Based Advanced Oxidation Nanotechnologies For Water Purification And Reuse

    Science.gov (United States)

    TiO2 photocatalysis, one of the UV-based advanced oxidation technologies (AOTs) and nanotechnologies (AONs), has attracted great attention for the development of efficient water treatment and purification systems due to the effectiveness of TiO2 to generate ...

  4. Oxidation and photo-oxidation of water on TiO2 surface

    DEFF Research Database (Denmark)

    Valdes, A.; Qu, Z.W.; Kroes, G.J.

    2008-01-01

    The oxidation and photo-oxidation of water on the rutile TiO2(110) surface is investigated using density functional theory (DFT) calculations. We investigate the relative stability of different surface terminations of TiO2 interacting with H2O and analyze the overpotential needed for the electrol...

  5. Hazards of TiO2 and amorphous SiO2 nanoparticles

    NARCIS (Netherlands)

    Reijnders, L.; Kahn, H.A.; Arif, I.A.

    2012-01-01

    TiO2 and amorphous SiO2 nanoparticles have been described as ‘safe’, ‘non-toxic’ and ‘environment friendly’ in scientific literature. However, though toxicity data are far from complete, there is evidence that these nanoparticles are hazardous. TiO2 nanoparticles have been found hazardous to humans

  6. Spectral Sensitization of TiO2 Substrates by Monolayers of Porphyrin Heterodimers

    NARCIS (Netherlands)

    Koehorst, R.B.M.; Boschloo, G.K.; Savenije, T.J.; Goossens, A.; Schaafsma, T.J.

    2000-01-01

    Photoelectrochemical cells have been constructed by depositing monolayers of oriented covalently linked zinc/free base porphyrin heterodimers onto ~30 nm nonporous layers of TiO2 on ITO, deposited by metal-organic chemical vapor deposition (MO-CVD), and onto ~100 nm porous, nanostructured TiO2

  7. Construction of hydrophobic wood surfaces by room temperature deposition of rutile (TiO2) nanostructures

    Science.gov (United States)

    Rongbo Zheng; Mandla A. Tshabalala; Qingyu Li; Hongyan Wang

    2015-01-01

    A convenient room temperature approach was developed for growing rutile TiO2 hierarchical structures on the wood surface by direct hydrolysis and crystallization of TiCl3 in saturated NaCl aqueous solution.The morphology and the crystal structure of TiO2 coated on the wood surface were characterized...

  8. TiO2 Based Photocatalyst: From Synthesis and Characterization to Optimization and Design

    DEFF Research Database (Denmark)

    Su, Ren

    2012-01-01

    TiO2 based photocatalyst has attracted gerat attentions from both fundamental and an applied aspects in water/air purifications and energy production. In this thesis, series of well-defined TiO2 photocatalyst with various parameters (i.e., polymorph composition, shape, impurity concentration, sur...

  9. Characterization of low temperature deposited atomic layer deposition TiO2 for MEMS applications

    NARCIS (Netherlands)

    Huang, Y.; Pandraud, G.; Sarro, P.M.

    2012-01-01

    TiO2 is an interesting and promising material for micro-/nanoelectromechanical systems (MEMS/NEMS). For high performance and reliable MEMS/NEMS, optimization of the optical characteristics, mechanical stress, and especially surface smoothness of TiO2 is required. To overcome the roughness issue of

  10. The Effects of Leaching Process to the TiO2 Synthesis from Bangka Ilmenite

    Science.gov (United States)

    Wahyuningsih, S.; Ramelan, A. H.; Pramono, E.; Argawan, P.; Djatisulistya, A.; Firdiyono, F.; Sulistiyono, E.; Sari, P. P.

    2018-03-01

    Ilmenite mineral is a naturally occurring iron titanate (FeTiO3) and is abundant in nature. The separation of components into TiO2 and Fe2O3 must be expand. The purpose of this research is to synthesis TiO2 nanoparticles from the filtrate of Bangka ilmenite leaching process. Leaching of ilmenite was done with H2SO4 and HCl at various concentrations. The formation of TiO2 crystal determined by hydrolysis conditions and condensation reaction. TiO2 synthesized from the filtrate of sulfuric acid leaching that produced from TiO2 anatase phase when hydrolyzed in an aquaregia solvent and low concentrations of HCl (0.1M). Hydrolysis conditions at higher concentrations of HCl (1M) was produced TiO2 anatase-rutile phase. The synthesis of TiO2 from the filtrate of hydrochloric acid leaching was produced anatase phase. While the condition under the alcoholic solvent (2-propanol: H2O (v/v) = 9: 1) anatase phase crystallites grow in the temperature range up to 550 °C, above this temperature, TiO2 transform into rutile phase.

  11. Hydrothermal synthesis of TiO2 Nanotubes: Microwave heating versus conventional heating

    CSIR Research Space (South Africa)

    Sikhwivhilu, LM

    2010-01-01

    Full Text Available The influence of the method of synthesis in the properties of the tubular structures derived from TiO2 was investigated using XRD, SEM and BET analysis. The use of microwave irradiation resulted in the formation of TiO2 tubes comprising anatase...

  12. TiO2 Photocatalysis Damages Lipids and Proteins in Escherichia coli

    NARCIS (Netherlands)

    Carre, Gaelle; Hamon, Erwann; Ennahar, Said; Estner, Maxime; Lett, Marie-Claire; Horvatovich, Peter; Gies, Jean-Pierre; Keller, Valerie; Keller, Nicolas; Andre, Philippe

    This study investigates the mechanisms of UV-A (315 to 400 nm) photocatalysis with titanium dioxide (TiO2) applied to the degradation of Escherichia coli and their effects on two key cellular components: lipids and proteins. The impact of TiO2 photocatalysis on E. coli survival was monitored by

  13. New TiO2/DSAT Immobilization System for Photodegradation of Anionic and Cationic Dyes

    Directory of Open Access Journals (Sweden)

    Wan Izhan Nawawi Wan Ismail

    2015-01-01

    Full Text Available A new immobilized TiO2 technique was prepared by coating TiO2 solution onto double-sided adhesive tape (DSAT as a thin layer binder without adding any organic additives. Glass plate was used as support material to immobilized TiO2/DSAT. Two different charges of dyes were applied, namely, anionic reactive red 4 (RR4 and cationic methylene blue (MB dyes. Photocatalytic degradation of RR4 and MB dyes was observed under immobilized TiO2/DSAT with the degradation rate slightly lower and higher, respectively, compared with TiO2 in suspension mode. It was observed that DSAT is able to provide a very strong intact between glass and TiO2 layers thus making the reusability of immobilized TiO2/DSAT be up to 30 cycles. In fact, a better photodegradation activity was observed by number of cycles due to increasing formation of pores on TiO2 surface observed by SEM analysis.

  14. Synthesis, structure and photocatalytic activity of nano TiO2 and ...

    Indian Academy of Sciences (India)

    salicylic acid over combustion-synthesized nano TiO2 under UV and solar exposure has been carried out. Under identical conditions of UV exposure, the initial degra- dation rate of phenol with combustion-synthesized TiO2 is two times higher than the initial degradation rate of phenol with Degussa P25, the commercial ...

  15. Microstructure and antibacterial property of in situ TiO(2) nanotube layers/titanium biocomposites.

    Science.gov (United States)

    Cui, C X; Gao, X; Qi, Y M; Liu, S J; Sun, J B

    2012-04-01

    The TiO(2) nanotube layer was in situ synthesized on the surface of pure titanium by the electrochemical anodic oxidation. The diameter of nano- TiO(2) nanotubes was about 70~100 nm. The surface morphology and phase compositions of TiO(2) nanotube layers were observed and analyzed using the scanning electron microscope (SEM). The important processing parameters, including anodizing voltage, reaction time, concentration of electrolyte, were optimized in more detail. The photocatalytic activity of the nano- TiO(2) nanotube layers prepared with optimal conditions was evaluated via the photodegradation of methylthionine in aqueous solution. The antibacterial property of TiO(2) nanotube layers prepared with optimal conditions was evaluated by inoculating Streptococcus mutans on the TiO(2) nanotube layers in vitro. The results showed that TiO(2) nanotube layers/Ti biocomposites had very good antibacterial activity to resist Streptococcus mutans. As a dental implant biomaterial, in situ TiO(2) nanotube layer/Ti biocomposite has better and wider application prospects. Copyright © 2012 Elsevier Ltd. All rights reserved.

  16. Growth and characterization of hydroxyapatite nanorice on TiO2 nanofibers

    KAUST Repository

    Chetibi, Loubna; Hamana, Djamel; Achour, Slimane

    2014-01-01

    with anatase TiO2 nanofibers. These nanofibers were prepared by in situ oxidation of Ti foils in a concentrated solution of H 2O2 and NaOH, followed by proton exchange and calcinations. Afterward, TiO2 nanofibers on Ti substrate were coated with HA

  17. Electrospinning processed nanofibrous TiO2 membranes for photovoltaic applications

    Science.gov (United States)

    Onozuka, Katsuhiro; Ding, Bin; Tsuge, Yosuke; Naka, Takayuki; Yamazaki, Michiyo; Sugi, Shinichiro; Ohno, Shingo; Yoshikawa, Masato; Shiratori, Seimei

    2006-02-01

    We have recently fabricated dye-sensitized solar cells (DSSCs) comprising nanofibrous TiO2 membranes as electrode materials. A thin TiO2 film was pre-deposited on fluorine doped tin oxide (FTO) coated conducting glass substrate by immersion in TiF4 aqueous solution to reduce the electron back-transfer from FTO to the electrolyte. The composite polyvinyl acetate (PVac)/titania nanofibrous membranes can be deposited on the pre-deposited thin TiO2 film coated FTO by electrospinning of a mixture of PVac and titanium isopropoxide in N,N-dimethylformamide (DMF). The nanofibrous TiO2 membranes were obtained by calcining the electrospun composite nanofibres of PVac/titania as the precursor. Spectral sensitization of the nanofibrous TiO2 membranes was carried out with a ruthenium (II) complex, cis-dithiocyanate-N,N'-bis(2,2'-bipyridyl-4,4'-dicarboxylic acid) ruthenium (II) dihydrate. The results indicated that the photocurrent and conversion efficiency of electrodes can be increased with the addition of the pre-deposited TiO2 film and the adhesion treatment using DMF. Additionally, the dye loading, photocurrent, and efficiency of the electrodes were gradually increased by increasing the average thickness of the nanofibrous TiO2 membranes. The efficiency of the fibrous TiO2 photoelectrode with the average membrane thickness of 3.9 µm has a maximum value of 4.14%.

  18. Nanoscale surface potential imaging of the photocatalytic TiO2 films on aluminum

    DEFF Research Database (Denmark)

    Daviðsdóttir, Svava; Dirscherl, Kai; Canulescu, Stela

    2013-01-01

    in the surface potential of TiO2 coatings upon UV-illumination are closely correlated to the band gap and thickness of the coatings. The inhomogeneity surface potential distribution of a 100 nm TiO2 film indicates a heterogeneous coating. Transition to a homogeneous surface potential distribution was observed...

  19. TiO2@C Core-Shell Nanoparticles Formed by Polymeric Nano-Encapsulation

    Directory of Open Access Journals (Sweden)

    Mitra eVasei

    2014-07-01

    Full Text Available TiO2 semiconducting nanoparticles are known to be photocatalysts of moderate activity due to their high band-gap and high rate of electron-hole recombination. The formation of a shell of carbon around the core of TiO2, i.e. the formation of TiO2@C nanoparticles, is believed to partly alleviate these problems. It is usually achieved by a hydrothermal treatment in a presence of a sugar derivative. We present here a novel method for the formation of highly uniform C shell around TiO2 nanoparticles. For this purpose, TiO2 nanoparticles were dispersed in water using an oligomeric dispersant prepared by Reversible Addition-Fragmentation chain Transfer (RAFT polymerization. Then the nanoparticles were engaged into an emulsion polymerization of acrylonitrile, resulting in the formation of a shell of polyacrylonitrile (PAN around each TiO2 nanoparticles. Upon pyrolisis, the PAN was transformed into carbon, resulting in the formation of TiO2@C nanoparticles. The structure of the resulting particles was elucidated by X-Ray diffraction, FTIR, UV-VIS and Raman spectroscopy as well as TEM microscopy. Preliminary results about the use of the TiO2@C particles as photocatalysts for the splitting of water are presented. They indicate that the presence of the C shell is responsible for a significant enhancement of the photocurrent.

  20. Hot corrosion performance of LVOF sprayed Al2O3–40% TiO2 ...

    Indian Academy of Sciences (India)

    ficients of thermal expansions of the two. ... size 40 mesh just prior to deposition of the coating. Al2O3–. 40% TiO2 ... the laboratory Kanthal wire tube furnace, which was cali- ... formation of TiO2, Al2O3 and Al2Ti7O15 phases in the coat- ing.

  1. Intrinsic Photocatalytic Assessment of Reactively Sputtered TiO2 Films

    NARCIS (Netherlands)

    Rafieian Boroujeni, Damon; Driessen, Rick Theodorus; Driessen, Rick T.; Ogieglo, Wojciech; Lammertink, Rob G.H.

    2015-01-01

    Thin TiO2 films were prepared by DC magnetron reactive sputtering at different oxygen partial pressures. Depending on the oxygen partial pressure during sputtering, a transition from metallic Ti to TiO2 was identified by spectroscopic ellipsometry. The crystalline nature of the film developed during

  2. Electrochemical characteristics of porous TiO2 encapsulated silicon anode

    International Nuclear Information System (INIS)

    Jeon, Bup Ju; Lee, Joong Kee

    2011-01-01

    Graphical abstract: Cycling performances of the TiO 2 coated silicon anode at different catalyst pH values. Display Omitted Highlights: → TiO 2 coated silicon was used as the anode material for lithium batteries. → TiO 2 layer acted as a buffer layer for reducing the volume expansion. → Pore size distribution of TiO 2 coated silicon influenced discharge capacity. → Higher capacity retention was exhibited at pH 10.7. - Abstract: TiO 2 coated silicon, which was prepared by the modified sol-gel method, was employed as the anode material for lithium secondary batteries and the relationship between the diffusivity and electrochemical characteristics was investigated. The results showed that the physical properties of the samples, such as their diffusivity and pore size distribution, enhanced the cycling efficiency of the TiO 2 coated silicon, probably due to the reduction of the side reactions, which may be closely related to the pore size distribution of the TiO 2 coating layer. The pore size of the coating layer plays an important role in retarding the lithium ion diffusion. In the experimental range studied herein, higher capacity retention was exhibited for the TiO 2 coated silicon prepared at pH 10.7.

  3. Fullerene C70 decorated TiO2 nanowires for visible-light-responsive photocatalyst

    International Nuclear Information System (INIS)

    Cho, Er-Chieh; Ciou, Jing-Hao; Zheng, Jia-Huei; Pan, Job; Hsiao, Yu-Sheng; Lee, Kuen-Chan; Huang, Jen-Hsien

    2015-01-01

    Graphical abstract: - Highlights: • TiO 2 nanowire decorated with C 60 and C 70 derivatives has been synthesized. • The fullerenes impede the charge recombination due to its high electron affinity. • The fullerenes expand the utilization of solar light from UV to visible light. • The modified-TiO 2 has great biocompatibility. - Abstract: In this study, we have synthesized C 60 and C 70 -modified TiO 2 nanowire (NW) through interfacial chemical bonding. The results indicate that the fullerenes (C 60 and C 70 derivatives) can act as sinks for photogenerated electrons in TiO 2 , while the fullerene/TiO 2 is illuminated under ultraviolet (UV) light. Therefore, in comparison to the pure TiO 2 NWs, the modified TiO 2 NWs display a higher photocatalytic activity under UV irradiation. Moreover, the fullerenes also can function as a sensitizer to TiO 2 which expand the utilization of solar light from UV to visible light. The results reveal that the C 70 /TiO 2 NWs show a significant photocatalytic activity for degradation of methylene blue (MB) in visible light region. To better understand the mechanism responsible for the effect of fullerenes on the photocatalytic properties of TiO 2 , the electron only devices and photoelectrochemical cells based on fullerenes/TiO 2 are also fabricated and evaluated.

  4. Complex impedance study on nano-CeO2 coating TiO2

    International Nuclear Information System (INIS)

    Zhang Mei; Wang Honglian; Wang Xidong; Li Wenchao

    2006-01-01

    Titanium dioxide (TiO 2 ) nanoparticles and cerium dioxide (CeO 2 ) nanoparticles coated titanium dioxide (TiO 2 ) nanoparticles (CeO 2 -TiO 2 nanoparticles) have been successfully synthesized by sol-gel method. The complex impedance of the materials was investigated. The grain resistance, boundary resistance and activation energy of the nanoparticles were calculated according to Arrhenius equation. According to calculating results, the active capacity of pure TiO 2 nanoparticles has been improved because of nano-CeO 2 coating. An optimal CeO 2 content of 4.9 mol% was achieved. The high resolution electron microscopy images of CeO 2 -TiO 2 nanoparticles showed that TiO 2 nanoparticles, as a core, were covered by CeO 2 nanoparticles. The average size of CeO 2 coating TiO 2 nanoparticles was about 70 nm. Scanning electron microscopy observation indicted that CeO 2 nanoparticle coating improved the separation, insulation, and stability the CeO 2 -TiO 2 nanoparticles, which was benefit to the activity of materials

  5. MoSe2 modified TiO2 nanotube arrays with superior photoelectrochemical performance

    Science.gov (United States)

    Zhang, Yaping; Zhu, Haifeng; Yu, Lianqing; He, Jiandong; Huang, Chengxing

    2018-04-01

    TiO2 nanotube arrays (TNTs) are first prepared by anodization Ti foils in ethylene glycol electrolyte. Then, MoSe2 deposites electrochemically on TNTs. The as-synthesized MoSe2/TiO2 composite has a much higher photocurrent density of 1.07 mA cm‑2 at 0 V than pure TNTs of 0.38 mA cm‑2, which suggests that the MoSe2/TiO2 composite film has optimum photoelectrocatalysis properties. The electron transport resistances of the MoSe2/TiO2 decreases to half of pure TiO2, at 295.6 ohm/cm2. Both photocurrent-time and Mott-Schottky plots indicate MoSe2 a p-type semiconductor characteristics. MoSe2/TiO2 composite can achieve a maximum 5 orders of magnitude enhancement in carrier density (4.650 × 1027 cm‑3) than that of pure TiO2 arrays. It can be attributed to p-n heterojunction formed between MoSe2 and TiO2, and the composite can be potentially applied in photoelectrochemical, photocatalysis fields.

  6. Azo dyes decomposition on new nitrogen-modified anatase TiO2 with high adsorptivity

    International Nuclear Information System (INIS)

    Janus, M.; Choina, J.; Morawski, A.W.

    2009-01-01

    New vis active photocatalyst was obtained by the modification of commercial anatase TiO 2 (Police, Poland) in pressure reactor in an ammonia water atmosphere at 100 o C for 4 h. The photocatalytic activity of new material was tested during three azo dyes decomposition: monoazo (Reactive Read), diazo (Reactive Black) and poliazodye (Direct Green). Obtained photocatalyst had new bands at 1430-1440 cm -1 attributed to the bending vibrations of NH 4 + and at 1535 cm -1 associated with NH 2 groups or NO 2 and NO. UV-vis/DR spectra of photocatalyst had also insignificant decrease in visible region. Fluorescence technique was used for studying the amount of hydroxyl radicals produced on TiO 2 surface during visible light irradiation. The hydroxyl radicals produced react with coumarin present in the solution to form 7-hydroxycoumarin which has fluorescent capacity. Photocatalytic activity of modified TiO 2 was compared with commercial titanium dioxide P25 (Degussa, Germany). The photocatalytic activity of TiO 2 /N was higher than that of unmodified material and P25 under visible light irradiation. The ability for dye adsorption (Reactive Red) on photocatalyst surface was also tested. Unmodified TiO 2 and P25 has isotherm of adsorption by Freundlich model, and nitrogen-modified TiO 2 by Langmuir model. The presence of nitrogen at the surface of TiO 2 significantly increased adsorption capacity of TiO 2 as well as OH· radicals formation under visible radiation.

  7. Y-doping TiO2 nanorod arrays for efficient perovskite solar cells

    Science.gov (United States)

    Deng, Xinlian; Wang, Yanqing; Cui, Zhendong; Li, Long; Shi, Chengwu

    2018-05-01

    To improve the electron transportation in TiO2 nanorod arrays and charge separation in the interface of TiO2/perovskite, Y-doping TiO2 nanorod arrays with the length of 200 nm, diameter of 11 nm and areal density of 1050 μm-2 were successfully prepared by the hydrothermal method and the influence of Y/Ti molar ratios of 0%, 3%, 5% in the hydrothermal grown solutions on the growth of TiO2 nanorod arrays was investigated. The results revealed that the appropriate Y/Ti molar ratios can increase the areal density of the corresponding TiO2 nanorod arrays and improve the charge separation in the interface of the TiO2/perovskite. The Y-doping TiO2 nanorod array perovskite solar cells with the Y/Ti molar ratio of 3% exhibited a photoelectric conversion efficiency (PCE) of 18.11% along with an open-circuit voltage (Voc) of 1.06 V, short-circuit photocurrent density (Jsc) of 22.50 mA cm-2 and fill factor (FF) of 76.16%, while the un-doping TiO2 nanorod array perovskite solar cells gave a PCE of 16.42% along with Voc of 1.04 V, Jsc of 21.66 mA cm-2 and FF of 72.97%.

  8. Microstructure, cold workability and strain hardening behavior of trimodaled AA 6061-TiO2 nanocomposite prepared by mechanical alloying

    International Nuclear Information System (INIS)

    Sivasankaran, S.; Sivaprasad, K.; Narayanasamy, R.

    2011-01-01

    Highlights: → Trimodaled composites consisting of UFG and CG matrix phases and ceramic phase were produced successfully. → Cold deformation behavior was investigated. → The 15% CG trimodaled composite yielded a high compressive strength of 935 MPa. → The 30% CG composite exhibited higher ductility while maintaining strength and toughness. - Abstract: In the present work, the improvement of compressive ductility while maintaining high strength and toughness for nanocrystalline materials by cold upsetting (incremental loads) of bulk trimodaled composite was studied. Mechanically alloyed nanocrystalline (NC) AA 6061 alloy powders reinforced with nano TiO 2 were blended with 0, 5, 10, 15, 20, 25, and 30 wt.% coarse grain (CG) elemental powders related to AA 6061 alloy composition to produce trimodal microstructure. The synthesized composite preforms were characterized by optical microscope, scanning electron microscope, transmission electron microscope and X-ray diffraction. The room temperature compressive deformation behavior was evaluated under triaxial stress state condition. With increasing percentage of CG phase in the nanocomposite, the gradual improvement in compressive ductility was observed at the cost of a small amount of strength but it favored the ease of deformation. The 15% CG trimodal composite exhibited an extremely high compressive strength of 935 MPa due to non-coalescence of individual CG particles and effective load transfer occurred in multi scale microstructures. But the 30% CG trimodal composite showed an incremental compressive ductility of around 16% while sacrificing a small amount of strength (845 MPa) and this composite displayed improved toughness (area under true effective stress and true effective strain curve) of over 600% than nanocomposite (0% CG). Also, the percentage cold workability of 30% CG composite was six times higher than that of 0% CG composite. Hence, the 30% CG trimodal composite was observed to be the good one as

  9. Improvement of light harvesting and device performance of dye-sensitized solar cells using rod-like nanocrystal TiO2 overlay coating on TiO2 nanoparticle working electrode

    International Nuclear Information System (INIS)

    Liu, Xueyang; Fang, Jian; Gao, Mei; Wang, Hongxia; Yang, Weidong; Lin, Tong

    2015-01-01

    Novel TiO 2 single crystalline nanorods were synthesized by electrospinning and hydrothermal treatment. The role of the TiO 2 nanorods on TiO 2 nanoparticle electrode in improvement of light harvesting and photovoltaic properties of dye-sensitized solar cells (DSSCs) was examined. Although the TiO 2 nanorods had lower dye loading than TiO 2 nanoparticle, they showed higher light utilization behaviour. Electron transfer in TiO 2 nanorods received less resistance than that in TiO 2 nanoparticle aggregation. By just applying a thin layer of TiO 2 nanorods on TiO 2 nanoparticle working electrode, the DSSC device light harvesting ability and energy conversion efficiency were improved significantly. The thickness of the nanorod layer in the working electrode played an important role in determining the photovoltaic property of DSSCs. An energy conversion efficiency as high as 6.6% was found on a DSSC device with the working electrode consisting of a 12 μm think TiO 2 nanoparticle layer covered with 3 μm thick TiO 2 nanorods. The results obtained from this study may benefit further design of highly efficient DSSCs. - Highlights: • Single crystalline TiO 2 nanorods were prepared for DSSC application. • TiO 2 nanorods show effective light scattering performance. • TiO 2 nanorods have higher electron transfer efficiency than TiO 2 nanoparticles. • TiO 2 nanorods on TiO 2 nanoparticle electrode improve DSSC efficiency

  10. Spin tunnelling in mesoscopic systems

    Science.gov (United States)

    Garg, Anupam

    2001-02-01

    We study spin tunnelling in molecular magnets as an instance of a mesoscopic phenomenon, with special emphasis on the molecule Fe8. We show that the tunnel splitting between various pairs of Zeeman levels in this molecule oscillates as a function of applied magnetic field, vanishing completely at special points in the space of magnetic fields, known as diabolical points. This phenomena is explained in terms of two approaches, one based on spin-coherent-state path integrals, and the other on a generalization of the phase integral (or WKB) method to difference equations. Explicit formulas for the diabolical points are obtained for a model Hamiltonian.

  11. TiO2-Containing Carbon Derived from a Metal-Organic Framework Composite: A Highly Active Catalyst for Oxidative Desulfurization.

    Science.gov (United States)

    Bhadra, Biswa Nath; Song, Ji Yoon; Khan, Nazmul Abedin; Jhung, Sung Hwa

    2017-09-13

    A new metal-organic framework (MOF) composite consisting of Ti- and Zn-based MOFs (ZIF-8(x)@H 2 N-MIL-125; in brief, ZIF(x)@MOF) was designed and synthesized. The pristine MOF [H 2 N-MIL-125 (MOF)]- and an MOF-composite [ZIF(30)@MOF]-derived mesoporous carbons consisting of TiO 2 nanoparticles were prepared by pyrolysis (named MDC-P and MDC-C, respectively). MDC-C showed a higher surface area, larger pore sizes, and larger mesopore volumes than MDC-P. In addition, the TiO 2 nanoparticles on MDC-C have more uniform shapes and sizes and are smaller than those of MDC-P. The obtained MDC-C and MDC-P [together with MOF, ZIF(30)@MOF, pure/nanocrystalline TiO 2 , and activated carbon] were applied in the oxidative desulfurization reaction of dibenzothiophene in a model fuel. The MDC-C, even with a lower TiO 2 content than that of MDC-P, showed an outstanding catalytic performance, especially with a very low catalyst dose (i.e., a very high quantity of dibenzothiophene was converted per unit weight of the catalyst), fast kinetics (∼3 times faster than that for MDC-P), and a low activation energy (lower than that for any reported catalyst) for the oxidation of dibenzothiophene. The large mesopores of MDC-C and the well-dispersed/small TiO 2 might be the dominant factors for the superior catalytic conversions. The oxidative desulfurization of other sulfur-containing organic compounds with various electron densities was also studied with MDC-C to understand the mechanism of catalysis. Moreover, the MDC-C catalyst can be reused many times in the oxidative desulfurization reaction after a simple washing with acetone. Finally, composing MOFs and subsequent pyrolysis is suggested as an effective way to prepare a catalyst with well-dispersed active sites, large pores, and high mesoporosity.

  12. First-Principles Modeling of Polaron Formation in TiO2 Polymorphs.

    Science.gov (United States)

    Elmaslmane, A R; Watkins, M B; McKenna, K P

    2018-06-21

    We present a computationally efficient and predictive methodology for modeling the formation and properties of electron and hole polarons in solids. Through a nonempirical and self-consistent optimization of the fraction of Hartree-Fock exchange (α) in a hybrid functional, we ensure the generalized Koopmans' condition is satisfied and self-interaction error is minimized. The approach is applied to model polaron formation in known stable and metastable phases of TiO 2 including anatase, rutile, brookite, TiO 2 (H), TiO 2 (R), and TiO 2 (B). Electron polarons are predicted to form in rutile, TiO 2 (H), and TiO 2 (R) (with trapping energies ranging from -0.02 eV to -0.35 eV). In rutile the electron localizes on a single Ti ion, whereas in TiO 2 (H) and TiO 2 (R) the electron is distributed across two neighboring Ti sites. Hole polarons are predicted to form in anatase, brookite, TiO 2 (H), TiO 2 (R), and TiO 2 (B) (with trapping energies ranging from -0.16 eV to -0.52 eV). In anatase, brookite, and TiO 2 (B) holes localize on a single O ion, whereas in TiO 2 (H) and TiO 2 (R) holes can also be distributed across two O sites. We find that the optimized α has a degree of transferability across the phases, with α = 0.115 describing all phases well. We also note the approach yields accurate band gaps, with anatase, rutile, and brookite within six percent of experimental values. We conclude our study with a comparison of the alignment of polaron charge transition levels across the different phases. Since the approach we describe is only two to three times more expensive than a standard density functional theory calculation, it is ideally suited to model charge trapping at complex defects (such as surfaces and interfaces) in a range of materials relevant for technological applications but previously inaccessible to predictive modeling.

  13. Positively charged TiO2 particles in non-polar system for electrophoretic display

    International Nuclear Information System (INIS)

    Chang, Young Seon

    2005-02-01

    Electrophoretic display uses a technique called electrophoresis to represent images and letters electronically with electronic ink. Although it has good characteristics such as wide viewing angle, high contrast ratio and extremely low power consumption, there are still several issues to be resolved to improve its performances. Higher mobility and stability of the ink particles are the most important issues among them. In this study, TiO 2 particles coated with acrylamide were found to be effective ink particles that satisfy higher mobility and stability. The TiO 2 particles coated with 5∼40% acrylamide were prepared by dispersion polymerization using monomers of methyl methacrylate (MMA) and acrylamide. The TiO 2 particles coated with acrylamide were dispersed in isopar-G with sorbitan esters such as span 20, span 80 and span 85. The size of the TiO 2 particles were changed from 200±150 nm to 350∼500 nm by the coating process. The morphology of coated particles was observed using a transmission electron microscope (TEM) and thermogravimetric analysis (TGA). From the TGA results, the weight fraction of TiO 2 and polymer in coated particle were calculated. From the zeta potential measurement, it was shown that as acrylamide concentration was increased from 5% to 30%, zeta potential of the coated TiO 2 particles was increased from 50mV to about 230mV. The zeta potential of the coated TiO 2 particles with 40% acrylamide was decreased to 50mV. As a stabilizer, span 85 was the most effective surfactant to improve stability of the TiO 2 particles coated with acrylamide among used surfactants in this study. Span 85 showed best stability in the storage test with TiO 2 particles coated with 10% acrylamide. The mobility of TiO 2 particles coated with acrylamide with span 85 in dye solution (Oil Blue-N dissolved in isopar-G) were measured by ITO cell test. The mobility of TiO 2 particles coated with 10∼30% acrylamide was over 600μm 2 /Vs while the mobility of TiO 2 particles coated with 40% acrylamide was about 400μm 2 /Vs. Span 85 was effective to improve the mobility of TiO 2 particles coated with acrylamide. As the concentration of span 85 was increased from 0 to 1.75 vol %, mobility of the TiO 2 particles coated with 20% acrylamide was increased from 250μm 2 /Vs to about 720μ 2 /Vs

  14. Structural, optical and ferromagnetic properties of Cr doped TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Choudhury, Biswajit; Choudhury, Amarjyoti

    2013-01-01

    Graphical abstract: Doping of Cr 3+ distorts the lattice of TiO 2 , generate oxygen vacancies and create d-band states in the mid band gap of TiO 2 . Incorporation of Cr 3+ also imparts magnetism in non-magnetic TiO 2 by undergoing coupling with the neighboring oxygen vacancies. -- Highlights: • Incorporation of Cr 3+ increases the concentration of oxygen vacancies in TiO 2 nanoparticles. • Doped TiO 2 nanoparticles contain absorption peaks corresponding to d–d transition of Cr 3+ into TiO 2 . • Pure and doped TiO 2 nanoparticles contain emission peaks related to oxygen vacancies. • Pure TiO 2 shows diamagnetism while Cr doped TiO 2 shows ferromagnetism. • The ferromagnetism is due to the interaction of Cr 3+ ions via oxygen vacancies. -- Abstract: Cr doped TiO 2 nanoparticles are prepared with three different concentrations of chromium, 1.5%, 3.0% and 4.5 mol% respectively. Doping decreases the crystallinity and increases the width of the X-ray diffraction peak. The Raman active E g peak of TiO 2 nanoparticles become asymmetric and shifted to higher energy on doping of 4.5% chromium. Electron paramagnetic resonance spectra reveal the presence of Cr 3+ in the host TiO 2 matrix. The absorption spectra of Cr doped TiO 2 nanoparticles contain absorption peaks corresponding to d–d transition of Cr 3+ in octahedral coordination. Most of the visible emission peaks are due to the electrons trapped in the oxygen vacancy centers. Undoped TiO 2 nanoparticles show diamagnetism at room temperature while all chromium doped samples show ferromagnetism. The magnetization of the doped samples increases at 1.5% and 3.0% and decreases at 4.5%. The ferromagnetism arises owing to the interaction of the neighboring Cr 3+ ions via oxygen vacancies. The decrease of magnetization at the highest doping is possibly due to the antiferromagnetic interactions of Cr 3+ pairs or due to Cr 3+ -O 2− -Cr 3+ superexchange interaction in the lattice

  15. Synergistic effects for the TiO2/RuO2/Pt photodissociation of water

    Energy Technology Data Exchange (ETDEWEB)

    Blondel, G; Harriman, A; Williams, D

    1983-07-01

    Compressed discs of naked TiO2 or TiO2 coated with a thin film of a noble metal (e.g. Pt) do not photodissociate water upon illumination with UV light, but small amounts of H2 are generated if the TiO2 has been reduced in a stream of H2 at 600 C. Discs prepared from mixtures of TiO2/RuO2 facilitate the UV photodissociation of water into H2 and O2 although the yields are very low. When a thin (about 9 nm) film of Pt is applied to the TiO2/RuO2 discs, the yields of H2 and O2 observed upon irradiation with UV light are improved drastically. 25 references.

  16. Synthesis and Photocatalytic Activity of Anatase TiO2 Nanoparticles-coated Carbon Nanotubes

    Directory of Open Access Journals (Sweden)

    Xie Yi

    2009-01-01

    Full Text Available Abstract A simple and straightforward approach to prepare TiO2-coated carbon nanotubes (CNTs is presented. Anatase TiO2 nanoparticles (NPs with the average size ~8 nm were coated on CNTs from peroxo titanic acid (PTA precursor even at low temperature of 100 °C. We demonstrate the effects of CNTs/TiO2 molar ratio on the adsorption capability and photocatalytic efficiency under UV–visible irradiation. The samples showed not only good optical absorption in visible range, but also great adsorption capacity for methyl orange (MO dye molecules. These properties facilitated the great enhancement of photocatalytic activity of TiO2 NPs-coated CNTs photocatalysts. The TiO2 NPs-coated CNTs exhibited 2.45 times higher photocatalytic activity for MO degradation than that of pure TiO2.

  17. Properties of phases in HfO2-TiO2 system

    International Nuclear Information System (INIS)

    Red'ko, V.P.; Terekhovskij, P.B.; Majster, I.M.; Shevchenko, A.V.; Lopato, L.M.; Dvernyakova, A.A.

    1990-01-01

    A study was made on axial and linear coefficients of thermal expansion (CTE) of HfO 2 -TiO 2 system samples in concentration range of 25-50 mol% TiO 2 . Samples, containing 35 and 37 mol% TiO 2 , are characterized by the lowest values of linear CTE. Dispersion of the basic substances doesn't affect CTE value. Correlation with axial and linear CTE of samples in ZrO 2 -TiO 2 system was conducted. Presence of anisotropy of change of lattice parameters was supported for samples, containing 37.5 and 40 mol% TiO 2 . Polymorphous transformations for hafnium titanate were not revealed

  18. Enhanced photoelectrochemical properties of TiO2 nanorod arrays decorated with CdS nanoparticles

    International Nuclear Information System (INIS)

    Xie, Zheng; Wang, Weipeng; Liu, Can; Li, Zhengcao; Liu, Xiangxuan; Zhang, Zhengjun

    2014-01-01

    TiO 2 nanorod arrays (TiO 2 NRAs) sensitized with CdS nanoparticles were fabricated via successive ion layer adsorption and reaction (SILAR), and TiO 2 NRAs were obtained by oxidizing Ti NRAs obtained through oblique angle deposition. The TiO 2 NRAs decorated with CdS nanoparticles exhibited excellent photoelectrochemical and photocatalytic properties under visible light, and the one decorated with 20 SILAR cycles CdS nanoparticles shows the best performance. This can be attributed to the enhanced separation of electrons and holes by forming heterojunctions of CdS nanoparticles and TiO 2 NRAs. This provides a promising way to fabricate the material for solar energy conversion and wastewater degradation. (paper)

  19. Preparation and performance of photocatalytic TiO2 immobilized on palladium-doped carbon fibers

    International Nuclear Information System (INIS)

    Zhu Yaofeng; Fu Yaqin; Ni Qingqing

    2011-01-01

    Pd-modified carbon fibers (CFs) are obtained by a facile oxidation-reduction method and then dip-coated in a sol-gel of titanium dioxide (TiO 2 ) to form supported TiO 2 /Pd-CF photocatalysts. The morphology of the Pd-modified CFs and the amount Pd deposited are characterized by field emission scanning electron microscopy and atomic absorption spectrometry, respectively. X-ray diffraction is used to investigate the crystal structures of the TiO 2 photocatalyst. Acid orange II is used as a model contaminant to evaluate the photocatalytic properties of the photocatalyst under UV irradiation. TiO 2 /Pd-CF exhibits higher catalytic activity than TiO 2 /CF towards the degradation of acid orange II. Optimum photocatalytic performance and support properties are achieved when the Pd particle loading is about 10.8 mg/g.

  20. Effects of highly ordered TiO2 nanotube substrates on the nucleation of Cu electrodeposits.

    Science.gov (United States)

    Ryu, Won Hee; Park, Chan Jin; Kwon, Hyuk Sang

    2010-05-01

    We investigated the effects of TiO2 nanotube substrates on the nucleation density of Cu during electrodeposition in a solution of CuSO4 and H2SO4 at 50 degrees C compared with those of pure Ti and micro-porous TiO2 substrates. During electrodeposition, the density of Cu nuclei on the TiO2 nanotube substrate increased and the average size of Cu nuclei decreased with increasing anodizing voltage and time for the synthesis of the substrate. In addition, the nucleation density of Cu electrodeposits on the highly ordered TiO2 nanotube substrate was much higher than that on pure Ti and micro-porous TiO2 substrates.

  1. Preparation of anatase TiO2 thin films by vacuum arc plasma evaporation

    International Nuclear Information System (INIS)

    Miyata, Toshihiro; Tsukada, Satoshi; Minami, Tadatsugu

    2006-01-01

    Anatase titanium dioxide (TiO 2 ) thin films with high photocatalytic activity have been prepared with deposition rates as high as 16 nm/min by a newly developed vacuum arc plasma evaporation (VAPE) method using sintered TiO 2 pellets as the source material. Highly transparent TiO 2 thin films prepared at substrate temperatures from room temperature to 400 deg. C exhibited photocatalytic activity, regardless whether oxygen (O 2 ) gas was introduced during the VAPE deposition. The highest photocatalytic activity and photo-induced hydrophilicity were obtained in anatase TiO 2 thin films prepared at 300 deg. C, which correlated to the best crystallinity of the films, as evidenced from X-ray diffraction. In addition, a transparent and conductive anatase TiO 2 thin film with a resistivity of 2.6 x 10 -1 Ω cm was prepared at a substrate temperature of 400 deg. C without the introduction of O 2 gas

  2. Three-dimensional observation of TiO2 nanostructures by electron tomography

    KAUST Repository

    Suh, Young Joon

    2013-03-01

    Three-dimensional nanostructures of TiO2 related materials including nanotubes, electron acceptor materials in hybrid polymer solar cells, and working electrodes of dye sensitized solar cells (DSSCs) were visualized by electron tomography as well as TEM micrographs. The regions on the wall of TiO2 nanotubes where the streptavidins were attached were elucidated by electron tomogram analysis. The coverage of TiO2 nanotubes by streptavidin was also investigated. The TiO2 nanostructures in hybrid polymer solar cells made by sol-gel and atomic layer deposition (ALD) methods and the morphologies of pores between TiO2 particles in DSSCs were also observed by reconstructed three-dimensional images made by electron tomography. © 2012 Elsevier Ltd.

  3. Antimicrobial and Barrier Properties of Bovine Gelatin Films Reinforced by Nano TiO2

    Directory of Open Access Journals (Sweden)

    R. Nassiri

    2013-11-01

    Full Text Available The effects of nano titanium dioxide incorporation were investigated on the water vaporpermeability, oxygen permeability, and antimicrobial properties of bovine gelatin films. The nano TiO2 (TiO2-N was homogenized by sonication and incorporated into bovine gelatin solutions at different concentrations(e.g. 1, 2, 3, and 5% w/w of dried gelatin. The permeability of the films to water vapor and oxygen wassignificantly decreased by incorporating of low concentration TiO2-N to gelatin solutions. TiO2-N gelatin filmsshowed an excellent antimicrobial activity against Staphylococcus aureus and Escherichia coli. Theseproperties suggest that TiO2-N has the potential as filler in gelatin-based films for using as an active packagingmaterials in pharmaceutical and food packaging industries.

  4. Optimized monolayer grafting of 3-aminopropyltriethoxysilane onto amorphous, anatase and rutile TiO 2

    Science.gov (United States)

    Song, Yan-Yan; Hildebrand, Helga; Schmuki, Patrik

    2010-02-01

    Experimental conditions were studied for optimized attachment of 3-aminopropyltriethoxysilane (APTES) onto amorphous, anatase and rutile titanium dioxide (TiO 2) surfaces. The attachment process and extent was characterized using X-ray photoelectron spectroscopy (XPS). In particular, the effect of attachment time, silane concentration, reaction temperature and the TiO 2 crystalline structure on the growth kinetics of the silane layers was studied. The measurements reveal that typically monolayers are more dense on amorphous than on crystalline TiO 2. The results show that critical experimental conditions exist where APTES attachment to the TiO 2 surface changes from a monolayer to a multilayer growth mode. The obtained results and parameters to produce optimized APTES layers are of a high practical relevance as APTES attachment often constitutes the initial step for organic modification of TiO 2 surface with biorelevant molecules such as proteins, enzymes or growth factors.

  5. One-Dimensional TiO2 Nanostructures as Photoanodes for Dye-Sensitized Solar Cells

    Directory of Open Access Journals (Sweden)

    Jie Qu

    2013-01-01

    Full Text Available Titanium dioxide (TiO2 is star materials due to its remarkable optical and electronic properties, resulting in various applications, especially in the fields of dye-sensitized solar cells (DSSCs. Photoanode is the most important part of the DSSCs, which help to adsorb dye molecules and transport the injected electrons. The size, structure, and morphology of TiO2 photoanode have been found to show significant influence on the photovoltaic performance of DSSCs. In this paper, we briefly summarize the synthesis and properties of one-dimensional (1D TiO2 nanomaterials (bare 1D TiO2 nanomaterial and 1D hierarchical TiO2 and their photovoltaic performance in DSSCs.

  6. Excess electrons in reduced rutile and anatase TiO2

    Science.gov (United States)

    Yin, Wen-Jin; Wen, Bo; Zhou, Chuanyao; Selloni, Annabella; Liu, Li-Min

    2018-05-01

    As a prototypical photocatalyst, TiO2 is a material of scientific and technological interest. In photocatalysis and other applications, TiO2 is often reduced, behaving as an n-type semiconductor with unique physico-chemical properties. In this review, we summarize recent advances in the understanding of the fundamental properties and applications of excess electrons in reduced, undoped TiO2. We discuss the characteristics of excess electrons in the bulk and at the surface of rutile and anatase TiO2 focusing on their localization, spatial distribution, energy levels, and dynamical properties. We examine specific features of the electronic states for photoexcited TiO2, for intrinsic oxygen vacancy and Ti interstitial defects, and for surface hydroxyls. We discuss similarities and differences in the behaviors of excess electrons in the rutile and anatase phases. Finally, we consider the effect of excess electrons on the reactivity, focusing on the interaction between excess electrons and adsorbates.

  7. ADSORCIÓN DE ALDEHÍDOS INSATURADOS SOBRE TiO2

    Directory of Open Access Journals (Sweden)

    Natalia Ortega

    2012-01-01

    Full Text Available En el presente trabajo se estudió la adsorción de aldehídos insaturados sobre la superficie del TiO2. Para evaluar su eficiencia como catalizador, se realizaron experimentos de fotocatálisis heterogénea de p-nitrofenol (PNF y una muestra proveniente de efluentes industriales. Se empleó un simulador solar y cuatro sistemas de TiO2: el TiO2-sólo (sin modificar y los sistemas TiO2-dienal constituidos por la adsorción química de 2,4 hexadienal, 2,4 heptadienal y el trans-cinamaldehído sobre la superficie del TiO2. La adsorción de los aldehídos insaturados sobre el TiO2 se cuantificó empleando los modelos de adsorción de Langmuir y Freundlich. Se evaluó la influencia del pH en los sistemas TiO2-dienal y su efecto en la degradación fotocatalítica del PNF. En condiciones básicas, la constante de velocidad del PNF es mayor al emplear los sistemas TiO2-dienal en comparación con el TiO2-sólo, mientras que en condiciones ácidas se encontró la tendencia opuesta. El sistema TiO2-cina resultó ser el fotocatalizador de mayor eficiencia.

  8. Synthesis and photocatalytic activity of graphene based doped TiO2 nanocomposites

    International Nuclear Information System (INIS)

    Gu, Yongji; Xing, Mingyang; Zhang, Jinlong

    2014-01-01

    Graphical abstract: - Highlights: • Graphene based doped TiO 2 nanocomposites were prepared. • The intimate contact between doped TiO 2 and graphene is achieved simultaneously. • These nanocomposites showed higher photocatalytic activity than TiO 2 and doped TiO 2 . • Photocatalytic mechanism was explained thoroughly. - Abstract: The nanocomposites of reduced graphene oxide based nitrogen doped TiO 2 (N–TiO 2 –RGO) and reduced graphene oxide based nitrogen and vanadium co-doped TiO 2 (N, V–TiO 2 –RGO) were prepared via a facile hydrothermal reaction of graphene oxide and TiO 2 in a water solvent. In this hydrothermal treatment, the reduction of graphene oxide and the intimate contact between nitrogen doped TiO 2 (N–TiO 2 ) or nitrogen and vanadium co-doped TiO 2 (N,V–TiO 2 ) and the RGO sheet is achieved simultaneously. Both N–TiO 2 –RGO and N,V–TiO 2 –RGO nanocomposites exhibit much higher visible light photocatalytic activity than N–TiO 2 and N,V–TiO 2 , and the order of visible light photocatalytic activity is N,V–TiO 2 –RGO > N–TiO 2 –RGO > N,V–TiO 2 > N–TiO 2 > TiO 2 . According to the characterization, the enhanced photocatalytic activity of the nanocomposites is attributed to reasons, such as enhancement of adsorption of pollutants, light absorption intensity, minimizing the recombination of photoinduced electrons and holes and more excited states of these nanocomposites under visible light irradiation. Overall, this work provides a more marked contrast of graphene based semiconductor nanocomposites and a more comprehensive explanation of the mechanism

  9. Recovery TiO2 by leaching process of carbothermic reduced Kalimantan ilmenite

    Science.gov (United States)

    Wahyuningsih, S.; Sari, P. P.; Ramelan, A. H.

    2018-05-01

    Ilmenite naturally occurred in iron titanate (FeTiO3) minerals. The separation of natural ilmenite into TiO2 and Fe2O3 need to be explored to gain the high purity separation product. A new combination method named of carbothermic reduction, acidic-leaching and complexation by EDTA were proposed for separation TiO2 from Ilmenite. Roasting of ilmenite was carried out at 950 °C for 1 h by the addition of activated carbon with mass ratio of ilmenite : activated carbon =4:3. The carbothermic reduction was carried out to yield a high separation of initial content of ilmenite that will be easily to dissolve within hydrochloric acid solution in leaching process. The composition of ilmenite observed by X-Ray Fluoresences (XRF) changed after the carbothermic reduction process and the dominant content is TiO2 (57.56%). X-Ray Diffraction (XRD) of roasted ilmenite composed of decomposed product of ilmenite i.e. hematite (Fe2O3), TiO2 anatase, TiO2 rutile, and inorganic salt. The leaching of the roasted ilmenite has been done by sulphuric acid solution (6 M) to gain the titanyl sulphate solution. Separation of iron impurities of TiO2 gel from titanyl sulphate (TiOSO4) solution was conducted by complexation method using EDTA as a complexation agent. The characteristic of TiO2 obtained using XRD showed that TiO2 is anatase type and the percentage of TiO2 using XRF showed that TiO2 content of 86,03%.

  10. Characterization and improved solar light activity of vanadium doped TiO2/diatomite hybrid catalysts

    International Nuclear Information System (INIS)

    Wang, Bin; Zhang, Guangxin; Leng, Xue; Sun, Zhiming; Zheng, Shuilin

    2015-01-01

    Highlights: • V-doped TiO 2 /diatomite composite photocatalyst was synthesized. • The physiochemical property and solar light photoactivity were characterized. • The presence and influence of V ions in TiO 2 matrix was systematically analyzed. • The photocatalysis for Rhodamine B were studied under solar light illumination. - Abstract: V-doped TiO 2 /diatomite composite photocatalysts with different vanadium concentrations were synthesized by a modified sol–gel method. The diatomite was responsible for the well dispersion of TiO 2 nanoparticles on the matrix and consequently inhibited the agglomeration. V-TiO 2 /diatomite hybrids showed red shift in TiO 2 absorption edge with enhanced absorption intensity. Most importantly, the dopant energy levels were formed in the TiO 2 bandgap due to V 4+ ions substituted to Ti 4+ sites. The 0.5% V-TiO 2 /diatomite photocatalyst displayed narrower bandgap (2.95 eV) compared to undoped sample (3.13 eV) and other doped samples (3.05 eV) with higher doping concentration. The photocatalytic activities of V doped TiO 2 /diatomite samples for the degradation of Rhodamine B under stimulated solar light illumination were significantly improved compared with the undoped sample. In our case, V 4+ ions incorporated in TiO 2 lattice were responsible for increased visible-light absorption and electron transfer to oxygen molecules adsorbed on the surface of TiO 2 to produce superoxide radicals ·O 2 – , while V 5+ species presented on the surface of TiO 2 particles in the form of V 2 O 5 contributed to e – –h + separation. In addition, due to the combination of diatomite as support, this hybrid photocatalyst could be separated from solution quickly by natural settlement and exhibited good reusability

  11. Efficient photodecomposition of herbicide imazapyr over mesoporous Ga2O3-TiO2 nanocomposites.

    Science.gov (United States)

    Ismail, Adel A; Abdelfattah, Ibrahim; Faisal, M; Helal, Ahmed

    2018-01-15

    The unabated release of herbicide imazapyr into the soil and groundwater led to crop destruction and several pollution-related concerns. In this contribution, heterogeneous photocatalytic technique was employed utilizing mesoporous Ga 2 O 3 -TiO 2 nanocomposites for degrading imazapyr herbicide as a model pollutant molecule. Mesoporous Ga 2 O 3 -TiO 2 nanocomposites with varied Ga 2 O 3 contents (0-5wt%) were synthesized through sol-gel process. XRD and Raman spectra exhibited extremely crystalline anatase TiO 2 phase at low Ga 2 O 3 content which gradually reduced with the increase of Ga 2 O 3 content. TEM images display uniform TiO 2 particles (10±2nm) with mesoporous structure. The mesoporous TiO 2 exhibits large surface areas of 167m 2 g -1 , diminished to 108m 2 g -1 upon 5% Ga 2 O 3 incorporation, with tunable mesopore diameter in the range of 3-9nm. The photocatalytic efficiency of synthesized Ga 2 O 3 -TiO 2 nanocomposites was assessed by degrading imazapyr herbicide and comparing with commercial photocatalyst UV-100 and mesoporous Ga 2 O 3 under UV illumination. 0.1% Ga 2 O 3 -TiO 2 nanocomposite is considered the optimum photocatalyst, which degrades 98% of imazapyr herbicide within 180min. Also, the photodegradation rate of imazapyr using 0.1% Ga 2 O 3 -TiO 2 nanocomposite is nearly 10 and 3-fold higher than that of mesoporous Ga 2 O 3 and UV-100, respectively. The high photonic efficiency and long-term stability of the mesoporous Ga 2 O 3 -TiO 2 nanocomposites are ascribed to its stronger oxidative capability in comparison with either mesoporous TiO 2 , Ga 2 O 3 or commercial UV-100. Copyright © 2017 Elsevier B.V. All rights reserved.

  12. TiO2/Cu2O composite based on TiO2 NTPC photoanode for photoelectrochemical (PEC) water splitting under visible light

    KAUST Repository

    Shi, Le

    2015-05-01

    Water splitting through photoelectrochemical reaction is widely regarded as a major method to generate H2 , a promising source of renewable energy to deal with the energy crisis faced up to human being. Efficient exploitation of visible light in practice of water splitting with pure TiO2 material, one of the most popular semiconductor material used for photoelectrochemical water splitting, is still challenging. One dimensional TiO2 nanotubes is highly desired with its less recombination with the short distance for charge carrier diffusion and light-scattering properties. This work is based on TiO2 NTPC electrode by the optimized two-step anodization method from our group. A highly crystalized p-type Cu2O layer was deposited by optimized pulse potentiostatic electrochemical deposition onto TiO2 nanotubes to enhance the visible light absorption of a pure p-type TiO2 substrate and to build a p-n junction at the interface to improve the PEC performance. However, because of the real photocurrent of Cu2O is far away from its theoretical limit and also poor stability in the aqueous environment, a design of rGO medium layer was added between TiO2 nanotube and Cu2O layer to enhance the photogenerated electrons and holes separation, extend charge carrier diffusion length (in comparison with those of conventional pure TiO2 or Cu2O materials) which could significantly increase photocurrent to 0.65 mA/cm2 under visible light illumination (>420 nm) and also largely improve the stability of Cu2O layer, finally lead to an enhancement of water splitting performance.

  13. Structural and optical properties of AgCl-sensitized TiO2 (TiO2 @AgCl prepared by a reflux technique under alkaline condition

    Directory of Open Access Journals (Sweden)

    V. A. Mu’izayanti

    Full Text Available Abstract The AgCl-sensitized TiO2 (TiO2@AgCl has been prepared from the precursor of TiO2-rutile type which on its surface adsorb chloride anion (Cl- and various amounts of silver using AgNO3 as starting material: AgNO3/(AgNO3+TiO2 mass ratio of 0.00, 1.14, 3.25, 6.38 and 10.32%. Reflux under alkaline condition was the employed technique. All samples were characterized by X-ray diffraction (XRD and diffuse reflectance UV-vis spectroscopy. The sample without the addition of AgNO3 was analyzed by scanning electron microscope and surface area analyzer. The morphology of the sample showed a distribution of microspheres of approximately 0.5 to 1.0 µm and the specific surface area was 68 m2/g. XRD patterns indicated that the sample without the addition of AgNO3 contained two types of TiO2: rutile (major and anatase (minor, whereas the samples with the addition of AgNO3 consisted of one phase of AgCl and two types of TiO2: rutile and anatase. The bandgaps of the samples were in the range of 2.97 to 3.24 eV, which were very close to the bandgap of intrinsic TiO2 powder. The presence of 0.8, 2.6 and 4.4 wt% of AgCl in each sample resulted in an additional bandgap in visible light region of 1.90, 1.94 and 2.26 eV, respectively, whereas the presence of 9.4 wt% of AgCl in the sample resulted in two bandgaps in visible light region of 1.98 and 1.88 eV.

  14. Interface actions between TiO2 and porous diatomite on the structure and photocatalytic activity of TiO2-diatomite

    International Nuclear Information System (INIS)

    Xia, Yue; Li, Fangfei; Jiang, Yinshan; Xia, Maosheng; Xue, Bing; Li, Yanjuan

    2014-01-01

    TiO 2 -diatomite photocatalysts were prepared by sol–gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption–desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO 2 , the anatase-to-rutile phase transition temperature of TiO 2 loaded on diatomite carrier is significantly increased to nearly 900 °C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange (MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H 3 PO 4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si–O–Ti bond, increase the binding strength between TiO 2 and diatomite, restrain crystal growth of loaded TiO 2 , and thus form thermal-stable mesoporous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO 2 -diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO 2 -diatomite pretreated by phosphoric acid.

  15. Interface actions between TiO2 and porous diatomite on the structure and photocatalytic activity of TiO2-diatomite

    Science.gov (United States)

    Xia, Yue; Li, Fangfei; Jiang, Yinshan; Xia, Maosheng; Xue, Bing; Li, Yanjuan

    2014-06-01

    TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 °C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange (MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable mesoporous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid.

  16. XAS study of TiO2-based nanomaterials

    Science.gov (United States)

    Schneider, K.; Zajac, D.; Sikora, M.; Kapusta, Cz.; Michalow-Mauke, K.; Graule, Th.; Rekas, M.

    2015-07-01

    X-Ray Absorption Spectroscopy studies of the W (0-1 at% W) and Mo-doped TiO2 (0-1 at% Mo) nanoparticle specimens at the K edges of titanium and molybdenum as well as at the L2 L3 edges of tungsten are presented. The materials were prepared with Flame Spray Synthesis process by oxidation of metal-organic precursors. The Ti:K edge spectra in the XANES range show pre-edge and post-edge features characteristic for anatase. A decrease of the amplitude of the EXAFS function with doping is observed and attributed to a softening of the crystal lattice. The Mo EXAFS functions show a considerable decrease of the second-neighbour-shell peak with increasing Mo content, which is attributed to an increased number of cation vacancies. For tungsten a less pronounced effect is observed. The Mo and W XANES spectra do not show noticeable changes with doping level, which indicates their unchanged oxidation states.

  17. Optical spectroscopy of rare earth ion-doped TiO2 nanophosphors.

    Science.gov (United States)

    Chen, Xueyuan; Luo, Wenqin

    2010-03-01

    Trivalent rare-earth (RE3+) ion-doped TiO2 nanophosphors belong to one kind of novel optical materials and have attracted increasing attention. The luminescence properties of different RE3+ ions in various TiO2 nanomaterials have been reviewed. Much attention is paid to our recent progresses on the luminescence properties of RE3+ (RE = Eu, Er, Sm, Nd) ions in anatase TiO2 nanoparticles prepared by a sol-gel-solvothermal method. Using Eu3+ as a sensitive optical probe, three significantly different luminescence centers of Eu3+ in TiO2 nanoparticles were detected by means of site-selective spectroscopy at 10 K. Based on the crystal-field (CF) splitting of Eu3+ at each site, C2v and D2 symmetries were proposed for Eu3+ incorporated at two lattice sites. A structural model for the formation of multiple sites was proposed based on the optical behaviors of Eu3+ at different sites. Similar multi-site luminescence was observed in Sm(3+)- or Nd(3+)-doped TiO2 nanoparticles. In Eu(3+)-doped TiO2 nanoparticles, only weak energy transfer from the TiO2 host to the Eu3+ ions was observed at 10 K due to the mismatch of energy between the TiO2 band-gap and the Eu3+ excited states. On the contrary, efficient host-sensitized luminescences were realized in Sm(3+)- or Nd(3+)-doped anatase TiO2 nanoparticles due to the match of energy between TiO2 band-gap and the Sm3+ and Nd3+ excited states. The excitation spectra of both Sm(3+)- and Nd(3+)-doped samples exhibit a dominant broad peak centered at approximately 340 nm, which is associated with the band-gap of TiO2, indicating that sensitized emission is much more efficient than direct excitation of the Sm3+ and Nd3+ ions. Single lattice site emission of Er3+ in TiO2 nanocrystals can be achieved by modifying the experimental conditions. Upon excitation by a Ti: sapphire laser at 978 nm, intense green upconverted luminescence was observed. The characteristic emission of Er3+ ions was obtained both in the ultraviolet-visible (UV-vis) and near-infrared regions through the high-resolution experiments at 10 K. The CF experienced by Er3+ in TiO2 nanocrystal was systematically studied by means of the energy level fitting.

  18. Temperature effects during Ostwald ripening on structural and bandgap properties of TiO2 nanoparticles prepared by sonochemical synthesis

    International Nuclear Information System (INIS)

    Gonzalez-Reyes, L.; Hernandez-Perez, I.; Diaz-Barriga Arceo, L.; Dorantes-Rosales, H.; Arce-Estrada, E.; Suarez-Parra, R.; Cruz-Rivera, J.J.

    2010-01-01

    Anatase TiO 2 nanocrystalline (6 nm) with BET specific surface area of 300 m 2 /g and direct bandgap of 3.31 eV were prepared sonochemically and then it was subjected to thermal treatment from 400 to 900 deg. C for 2 h, in order to produce variable anatase-rutile ratio. Three stages were considered in the samples thermally treated: (i) anatase grains coarsening as a result of heat treatment temperature increasing the structural homogeneity and crystallinity and both phenomena produce a reduction in the specific surface area, (ii) coexistence of two phases (anatase and rutile) separated by a transition region, called an interface, and (iii) process where the rutile grains evolve into a new equilibrium shape without the presence of anatase phase, minimizing the total surface and the grain boundary energies, by mass transport diffusion. In this last stage the rutile phase has the sole function of growth and densification. The structure evolution, morphology and microstructure characteristics were obtained by X-ray diffraction (XRD) and transmission electron microscopy (TEM). All the stages of phase transformation are subject to thermal effects that stem from the redistribution of energy in the system. The UV-vis absorption spectra show that direct and indirect transitions can take place in the same sample simultaneously. This is attributed to the combined effect of samples with variable anatase-rutile ratio and particle size effect.

  19. Photocatalytic removal of NO and HCHO over nanocrystalline Zn2SnO4 microcubes for indoor air purification

    International Nuclear Information System (INIS)

    Ai Zhihui; Lee Shuncheng; Huang Yu; Ho Wingkei; Zhang Lizhi

    2010-01-01

    Nanocrystalline Zn 2 SnO 4 microcubes were hydrothermally synthesized and systematically characterized by XRD, SEM, TEM, XPS, N 2 adsorption-desorption, and UV-vis DRS analysis. The resulting Zn 2 SnO 4 microcubes with the edge size ranging from 0.8 to 1.2 μm were composed of numerous nanoparticles with size of 10-20 nm, and their optical band gap energy was estimated to be 3.25 eV from the UV-vis diffuse reflectance spectra. On degradation of nitrogen monoxide (NO) and formaldehyde (HCHO) at typical concentrations for indoor air quality, these nanocrystalline Zn 2 SnO 4 microcubes exhibited superior photocatalytic activity to the hydrothermally synthesized ZnO, SnO 2 , and Degussa TiO 2 P25, as well as C doped TiO 2 under UV-vis light irradiation. This enhanced photocatalytic activity of the nanocrystalline Zn 2 SnO 4 microcubes was attributed to their bigger surface areas, smaller particle size, special porous structures, and special electronic configuration. The nanocrystalline Zn 2 SnO 4 microcubes were chemically stable as there was no obvious deactivation during the multiple photocatalytic reactions. This work presents a promising approach for scaling-up industrial production of Zn 2 SnO 4 nanostructures and suggests that the synthesized nanocrystalline Zn 2 SnO 4 microcubes are promising photocatalysts for indoor air purification.

  20. In situ controlled synthesis of various TiO2 nanostructured materials via a facile hydrothermal route

    International Nuclear Information System (INIS)

    Wang Hai; Liu Yong; Zhong Minyi; Xu Hongmei; Huang Hong; Shen Hui

    2011-01-01

    Various TiO 2 nanomaterials, such as nanosheets, nanoflowers, and nanowires were directly self assembled on titanium substrate on a large scale under hydrothermal conditions. The morphology of the formed TiO 2 nanomaterials could be easily tuned by varying the experimental parameters of temperature, reaction time, and the NaOH concentration. A possible formation mechanism was suggested on the basis of the shape evolution of TiO 2 nanostructures by SEM images in combination with XRD patterns of as-grown samples. The optical properties of TiO 2 nanosheets, nanoflowers, and nanowires were characterized by reflectance spectroscopy. The studies revealed that the absorption capability of visible light is obviously different for TiO 2 with different morphologies. Moreover, TiO 2 nanosheets exhibited better light trapping than TiO 2 nanoflowers and TiO 2 nanowires due to their unique nanostructure.

  1. Influence of Nitrogen Doping on Device Operation for TiO2-Based Solid-State Dye-Sensitized Solar Cells: Photo-Physics from Materials to Devices

    Directory of Open Access Journals (Sweden)

    Jin Wang

    2016-02-01

    Full Text Available Solid-state dye-sensitized solar cells (ssDSSC constitute a major approach to photovoltaic energy conversion with efficiencies over 8% reported thanks to the rational design of efficient porous metal oxide electrodes, organic chromophores, and hole transporters. Among the various strategies used to push the performance ahead, doping of the nanocrystalline titanium dioxide (TiO2 electrode is regularly proposed to extend the photo-activity of the materials into the visible range. However, although various beneficial effects for device performance have been observed in the literature, they remain strongly dependent on the method used for the production of the metal oxide, and the influence of nitrogen atoms on charge kinetics remains unclear. To shed light on this open question, we synthesized a set of N-doped TiO2 nanopowders with various nitrogen contents, and exploited them for the fabrication of ssDSSC. Particularly, we carefully analyzed the localization of the dopants using X-ray photo-electron spectroscopy (XPS and monitored their influence on the photo-induced charge kinetics probed both at the material and device levels. We demonstrate a strong correlation between the kinetics of photo-induced charge carriers probed both at the level of the nanopowders and at the level of working solar cells, illustrating a direct transposition of the photo-physic properties from materials to devices.

  2. Laser induced photocurrent and photovoltage transient measurements of dye-sensitized solar cells based on TiO_2 nanosheets and TiO_2 nanoparticles

    International Nuclear Information System (INIS)

    Ghaithan, Hamid M.; Qaid, Saif M.H.; Hezam, Mahmoud; Labis, Joselito P.; Alduraibi, Mohammad; Bedja, Idriss M.; Aldwayyan, Abdullah S.

    2016-01-01

    Dye-sensitized solar cells (DSSCs) based on TiO_2 nanoparticles and TiO_2 nanosheets with exposed {001} facets are investigated using laser-induced photovoltage and photocurrent transient decay (LIPVCD) measurements. We adopted a simplified version of LIPVCD technique, in which a single illumination light source and a laboratory oscilloscope could be conveniently used for the measurements. Although the {001} surface of TiO_2 nanosheets allowed a noticeably slower recombination with the electrolyte, this was counterpoised by a slower electron transport probably due to its planar morphology, resulting in a shorter diffusion length in TiO_2 nanosheets. The nanosheet morphology also resulted in less surface area and therefore reduced short circuit current density in the fabricated devices. Our work highlights the fact that the morphological parameters of TiO_2 nanosheets finally resulting after electrode film deposition is of no less importance than the reported efficient dye adsorption and slow electron recombination at the surface of individual nanosheets.

  3. Disruption of Autolysis in Bacillus subtilis using TiO2 Nanoparticles.

    Science.gov (United States)

    McGivney, Eric; Han, Linchen; Avellan, Astrid; VanBriesen, Jeanne; Gregory, Kelvin B

    2017-03-17

    In contrast to many nanotoxicity studies where nanoparticles (NPs) are observed to be toxic or reduce viable cells in a population of bacteria, we observed that increasing concentration of TiO 2 NPs increased the cell survival of Bacillus subtilis in autolysis-inducing buffer by 0.5 to 5 orders of magnitude over an 8 hour exposure. Molecular investigations revealed that TiO 2 NPs prevent or delay cell autolysis, an important survival and growth-regulating process in bacterial populations. Overall, the results suggest two potential mechanisms for the disruption of autolysis by TiO 2 NPs in a concentration dependent manner: (i) directly, through TiO 2 NP deposition on the cell wall, delaying the collapse of the protonmotive-force and preventing the onset of autolysis; and (ii) indirectly, through adsorption of autolysins on TiO 2 NP, limiting the activity of released autolysins and preventing further lytic activity. Enhanced darkfield microscopy coupled to hyperspectral analysis was used to map TiO 2 deposition on B. subtilis cell walls and released enzymes, supporting both mechanisms of autolysis interference. The disruption of autolysis in B. subtilis cultures by TiO 2 NPs suggests the mechanisms and kinetics of cell death may be influenced by nano-scale metal oxide materials, which are abundant in natural systems.

  4. Thiourea-Modified TiO2 Nanorods with Enhanced Photocatalytic Activity

    Directory of Open Access Journals (Sweden)

    Xiaofeng Wu

    2016-02-01

    Full Text Available Semiconductor TiO2 photocatalysis has attracted much attention due to its potential application in solving the problems of environmental pollution. In this paper, thiourea (CH4N2S modified anatase TiO2 nanorods were fabricated by calcination of the mixture of TiO2 nanorods and thiourea at 600 °C for 2 h. It was found that only N element was doped into the lattice of TiO2 nanorods. With increasing the weight ratio of thiourea to TiO2 (R from 0 to 8, the light-harvesting ability of the photocatalyst steady increases. Both the crystallization and photocatalytic activity of TiO2 nanorods increase first and then decrease with increase in R value, and R2 sample showed the highest crystallization and photocatalytic activity in degradation of Brilliant Red X3B (X3B and Rhodamine B (RhB dyes under visible light irradiation (λ > 420 nm. The increased visible-light photocatalytic activity of the prepared N-doped TiO2 nanorods is due to the synergistic effects of the enhanced crystallization, improved light-harvesting ability and reduced recombination rate of photo-generated electron-hole pairs. Note that the enhanced visible photocatalytic activity of N-doped nanorods is not based on the scarification of their UV photocatalytic activity.

  5. Adsorption and photodegradation of methylene blue on TiO_2-halloysite adsorbents

    International Nuclear Information System (INIS)

    Du, Yuanyuan; Zheng, Pengwu

    2014-01-01

    TiO_2-halloysite (TiO_2-HNT) composites were fabricated by depositing anatase TiO_2 on the halloysite (HNT) surfaces with calcination treatment at 100, 200, 300 and 500 .deg. C. The obtained composites were characterized by transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FTIR) and X-Ray diffraction (XRD). HNT was attached with TiO_2 particles or clusters in sizes of 10-30 nm. With the increasing of calcination temperature, the crystalline of anatase became more perfect, but the structure of HNT could be destroyed at 500 .deg. C. The adsorption and photodegradation of methylene blue (MB) by TiO_2-HNTs were investigated. The kinetic adsorption fit the pseudo second-order, and the isotherm data followed the Langmuir model. The maximum adsorption capacities of MB were in the range of 38.57 to 54.29 mg/g. TiO_2-HNTs exhibited an efficient photocatalytic activity in the decomposition of MB. For TiO_2-HNT calcined at 300 .deg. C, 81.6% MB were degraded after 4 h treatment of UV irradiation

  6. High-performance thermoelectric materials based on ternary TiO2/CNT/PANI composites.

    Science.gov (United States)

    Erden, Fuat; Li, Hui; Wang, Xizu; Wang, FuKe; He, Chaobin

    2018-04-04

    In the present work, we report the fabrication of high-performance thermoelectric materials using TiO2/CNT/PANI ternary composites. We showed that a conductivity of ∼2730 S cm-1 can be achieved for the binary CNT (70%)/PANI (30%) composite, which is the highest recorded value for the reported CNT/PANI composites. We further demonstrated that the Seebeck coefficient of CNT/PANI composites could be enhanced by incorporating TiO2 nanoparticles into the binary CNT/PANI composites, which could be attributed to lower carrier density and the energy scattering of low-energy carriers at the interfaces of TiO2/a-CNT and TiO2/PANI. The resulting TiO2/a-CNT/PANI ternary system exhibits a higher Seebeck coefficient and enhanced thermoelectric power. Further optimization of the thermoelectric power was achieved by water treatment and by tuning the processing temperature. A high thermoelectric power factor of 114.5 μW mK-2 was obtained for the ternary composite of 30% TiO2/70% (a-CNT (70%)/PANI (30%)), which is the highest reported value among the reported PANI based ternary composites. The improvement of thermoelectric performance by incorporation of TiO2 suggests a promising approach to enhance power factor of organic thermoelectric materials by judicial tuning of the carrier concentration and electrical conductivity.

  7. Toxicity of nanotitanium dioxide (TiO2-NP) on human monocytes and their mitochondria.

    Science.gov (United States)

    Ghanbary, Fatemeh; Seydi, Enaytollah; Naserzadeh, Parvaneh; Salimi, Ahmad

    2018-03-01

    The effect of nanotitanium dioxide (TiO 2 -NP) in human monocytes is still unknown. Therefore, an understanding of probable cytotoxicity of TiO 2 -NP on human monocytes and underlining the mechanisms involved is of significant interest. The aim of this study was to assess the cytotoxicity of TiO 2 -NP on human monocytes. Using biochemical and flow cytometry assessments, we demonstrated that addition of TiO 2 -NP at 10 μg/ml concentration to monocytes induced cytotoxicity following 12 h. The TiO 2 -NP-induced cytotoxicity on monocytes was associated with intracellular reactive oxygen species (ROS) generation, mitochondrial membrane potential (MMP) collapse, lysosomal membrane injury, lipid peroxidation, and depletion of glutathione. According to our results, TiO 2 -NP triggers oxidative stress and organelles damages in monocytes which are important cells in defense against foreign agents. Finally, our findings suggest that use of antioxidants and mitochondrial/lysosomal protective agents could be of benefit for the people in the exposure with TiO 2 -NP.

  8. Single-Nanoparticle Photoelectrochemistry at a Nanoparticulate TiO2 -Filmed Ultramicroelectrode.

    Science.gov (United States)

    Peng, Yue-Yi; Ma, Hui; Ma, Wei; Long, Yi-Tao; Tian, He

    2018-03-26

    An ultrasensitive photoelectrochemical method for achieving real-time detection of single nanoparticle collision events is presented. Using a micrometer-thick nanoparticulate TiO 2 -filmed Au ultra-microelectrode (TiO 2 @Au UME), a sub-millisecond photocurrent transient was observed for an individual N719-tagged TiO 2 (N719@TiO 2 ) nanoparticle and is due to the instantaneous collision process. Owing to a trap-limited electron diffusion process as the rate-limiting step, a random three-dimensional diffusion model was developed to simulate electron transport dynamics in TiO 2 film. The combination of theoretical simulation and high-resolution photocurrent measurement allow electron-transfer information of a single N719@TiO 2 nanoparticle to be quantified at single-molecule accuracy and the electron diffusivity and the electron-collection efficiency of TiO 2 @Au UME to be estimated. This method provides a test for studies of photoinduced electron transfer at the single-nanoparticle level. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  9. SAXS Studies of TiO2 Nanoparticles in Polymer Electrolytes and in Nanostructured Films

    Directory of Open Access Journals (Sweden)

    Sigrid Bernstorff

    2010-11-01

    Full Text Available Polymer electrolytes as nanostructured materials are very attractive components for batteries and opto-electronic devices. (PEO8ZnCl2 polymer electrolytes were prepared from PEO and ZnCl2. The nanocomposites (PEO8ZnCl2/TiO2 themselves contained TiO2 nanograins. In this work, the influence of the TiO2 nanograins on the morphology and ionic conductivity of the nanocomposite was systematically studied by transmission small-angle X-ray scattering (SAXS simultaneously recorded with wide-angle X-ray diffraction (WAXD and differential scanning calorimetry (DSC at the synchrotron ELETTRA. Films containing nanosized grains of titanium dioxide (TiO2 are widely used in the research of optical and photovoltaic devices. The TiO2 films, prepared by chemical vapor deposition and e-beam epitaxy, were annealed in hydrogen atmospheres in the temperature range between 20 °C and 900 °C in order to study anatase-rutile phase transition at 740 °C. Also, grazing-incidence small angle X-ray scattering (GISAXS spectra for each TiO2 film were measured in reflection geometry at different grazing incident angles. Environmentally friendly galvanic cells, as well as solar cells of the second generation, are to be constructed with TiO2 film as working electrode, and nanocomposite polymer as electrolyte.

  10. Simplified TiO2 force fields for studies of its interaction with biomolecules

    Science.gov (United States)

    Luan, Binquan; Huynh, Tien; Zhou, Ruhong

    2015-06-01

    Engineered TiO2 nanoparticles have been routinely applied in nanotechnology, as well as in cosmetics and food industries. Despite active experimental studies intended to clarify TiO2's biological effects, including potential toxicity, the relation between experimentally inferred nanotoxicity and industry standards for safely applying nanoparticles remains somewhat ambiguous with justified concerns. Supplemental to experiments, molecular dynamics simulations have proven to be efficacious in investigating the molecular mechanism of a biological process occurring at nanoscale. In this article, to facilitate the nanotoxicity and nanomedicine research related to this important metal oxide, we provide a simplified force field, based on the original Matsui-Akaogi force field but compatible to the Lennard-Jones potentials normally used in modeling biomolecules, for simulating TiO2 nanoparticles interacting with biomolecules. The force field parameters were tested in simulating the bulk structure of TiO2, TiO2 nanoparticle-water interaction, as well as the adsorption of proteins on the TiO2 nanoparticle. We demonstrate that these simulation results are consistent with experimental data/observations. We expect that simulations will help to better understand the interaction between TiO2 and molecules.

  11. Titanium Dioxide (TiO2) Dye-Sensitized Solar Cells

    Science.gov (United States)

    Alseadi, Anwar Abdulaziz

    With the increasing global energy consumption and diminishing fossil fuels, various renewable and sustainable energies have been harvested in past decades and related devices have been fabricated. Dye-sensitized solar cells (DSSCs) are the most efficient third-generation solar cells to harvest solar energy into electricity directly. Titanium dioxide (TiO2) based DSSCs were invented in 1988 and have attracted more and more attention since then because of low-cost and high efficiency. TiO2 nanoparticles are one kind of popular anode materials of DSSC because of stability, abundance, environment safety, non-toxicity, and excellent photovoltaic properties. In the project, TiO2 nanoparticles with different crystallographic sizes were produced by ball-milling. Physical properties of the produced TiO 2 nanoparticles were characterized by X-ray powder diffraction, UV-visible spectroscopy, and Raman scattering. TiO2-based DSSCs were fabricated and their photovoltaic performances were tested. The effects of TiO2 layer thickness, crystallographic size, and microsphere fillings were investigated. The project enriched our understanding of TiO2-based DSSCs.

  12. Enhanced Photocatalytic Properties of Ag-Loaded N-Doped Tio2 Nanotube Arrays

    Directory of Open Access Journals (Sweden)

    Gao Dawei

    2018-03-01

    Full Text Available Highly ordered TiO2 nanotube (TiO2 NT arrays were prepared by anodic oxidizing method on the surface of the Ti substrate. Nitrogen-doped TiO2 nanotube (N-TiO2 NT arrays were carried out by ammonia solution immersion, and Ag nanoparticles loaded N-doped TiO2 nanotube (Ag/N-TiO2 NT arrays were obtained by successive ionic layer adsorption and reaction (SILAR technique. The samples were characterized by the X-ray diffraction (XRD, X-ray photoelectron spectroscopy (XPS, field emission scanning electron microscopy (FESEM, high-resolution transmission electron microscopy (HRTEM, photoluminescence (PL emission spectra, ultraviolet–visible (UV–vis diffuse reflectance spectroscopy (DRS. The result indicated that the diameter and wall thickness of the TiO2 NT are 100–120 and 20–30 nm, respectively. Moreover, the morphology and structure of the highly ordered TiO2 NTs were not affected by N-doping. Furthermore, Ag nanoparticles were evenly deposited on the surface of TiO2 NTs in the form of elemental silver. Finally, the photocatalytic activity of Ag/N-TiO2 NTs was evaluated by degradation of methyl orange (MO under visible-light irradiation. The Ag/N-TiO2 NTs exhibited enhanced photocatalytic properties, which could reach 95% after 90-min irradiation.

  13. Decolorization of dyeing wastewater in continuous photoreactors using tio2 coated glass tube media

    Directory of Open Access Journals (Sweden)

    Jutaporn Chanathaworn

    2014-02-01

    Full Text Available The present study deals with a decolorization development of malachite green (MG dyeing wastewater using TiO2 thin films coated glass tube media in photoreactor. The TiO2 photocatalyst was synthesized by three methods: TTIP sol-gel, TiO2 powder-modified sol, and TiO2 powder suspension coating on raschig ring glass tube media and was investigated crystallinity phase by SEM, XRD, and AFM. Degradation kinetics of the dyeing wastewater by photocatalytic was carried out under UV light irradiation. The Langmuir first-order model provided the best fit to the experimental data. The catalyst prepared by powder suspension technique and coated on glass tube had given the highest of decolorization kinetics and efficiency. Continuous photoreactor packed with the TiO2 coating media was designed and proven to be the high effectiveness for MG dyeing degradation and stable throughout the recyclability test. The light intensity, dye solution flow rate, and TiO2 loading were the most important parameters that response to decolorization efficiency. The optimum condition of photo decolorization of MG dye solution can be obtained from RSM model. Effectiveness of the synthesized TiO2 thin films using suspension technique and the continuous photoreactor design were obtained with a great potential to be proven for wastewater treatment at industrial scale.

  14. Light-induced antifungal activity of TiO2 nanoparticles/ZnO nanowires

    International Nuclear Information System (INIS)

    Haghighi, N.; Abdi, Y.; Haghighi, F.

    2011-01-01

    Antifungal activity of TiO 2 /ZnO nanostructures under visible light irradiation was investigated. A simple chemical method was used to synthesize ZnO nanowires. Zinc acetate dihydrate, Polyvinyl Pyrrolidone and deionized water were used as precursor, capping and solvent, respectively. TiO 2 nanoparticles were deposited on ZnO nanowires using an atmospheric pressure chemical vapor deposition system. X-ray diffraction pattern of TiO 2 /ZnO nano-composite has represented the diffraction peaks relating to the crystal planes of the TiO 2 (anatase and rutile) and ZnO. TiO 2 /ZnO nanostructure antifungal effect on Candida albicans biofilms was studied and compared with the activity of TiO 2 nanoparticles and ZnO nanowires. The high efficiency photocatalytic activity of TiO 2 nanoparticles leads to increased antifungal activity of ZnO nanowires. Scanning electron microscope was utilized to study the morphology of the as prepared nanostructures and the degradation of the yeast.

  15. Enhanced properties of nanostructured TiO2-graphene composites by rapid sintering

    Science.gov (United States)

    Shon, In-Jin; Yoon, Jin-Kook; Hong, Kyung-Tae

    2018-01-01

    Despite of many attractive properties of TiO2, the drawback of TiO2 ceramic is low fracture toughness for widely industrial application. The method to improve the fracture toughness and hardness has been reported by addition of reinforcing phase to fabricate a nanostructured composite. In this regard, graphene has been evaluated as an ideal second phase in ceramics. Nearly full density of nanostructured TiO2-graphene composite was achieved within one min using pulsed current activated sintering. The effect of graphene on microstructure, fracture toughness and hardness of TiO2-graphene composite was evaluated using Vickers hardness tester and field emission scanning electron microscopy. The grain size of TiO2 in the TiO2-x vol% (x = 0, 1, 3, and 5) graphene composite was greatly reduced with increase in addition of graphene. Both hardness and fracture toughness of TiO2-graphene composites simultaneously increased in the addition of graphene.

  16. ALMA observations of TiO2 around VY Canis Majoris

    Science.gov (United States)

    De Beck, E.; Vlemmings, W.; Muller, S.; Black, J. H.; O'Gorman, E.; Richards, A. M. S.; Baudry, A.; Maercker, M.; Decin, L.; Humphreys, E. M.

    2015-08-01

    Context. Titanium dioxide, TiO2, is a refractory species that could play a crucial role in the dust-condensation sequence around oxygen-rich evolved stars. To date, gas phase TiO2 has been detected only in the complex environment of the red supergiant VY CMa. Aims: We aim to constrain the distribution and excitation of TiO2 around VY CMa in order to clarify its role in dust formation. Methods: We analyse spectra and channel maps for TiO2 extracted from ALMA science verification data. Results: We detect 15 transitions of TiO2, and spatially resolve the emission for the first time. The maps demonstrate a highly clumpy, anisotropic outflow in which the TiO2 emission likely traces gas exposed to the stellar radiation field. An accelerating bipolar-like structure is found, oriented roughly east-west, of which the blue component runs into and breaks up around a solid continuum component. A distinct tail to the south-west is seen for some transitions, consistent with features seen in the optical and near-infrared. Conclusions: We find that a significant fraction of TiO2 remains in the gas phase outside the dust-formation zone and suggest that this species might play only a minor role in the dust-condensation process around extreme oxygen-rich evolved stars like VY CMa. Appendix A is available in electronic form at http://www.aanda.org

  17. Photocatalytic degradation of Rhodamine B dye using Fe doped TiO2 nanocomposites

    Science.gov (United States)

    Barkhade, Tejal; Banerjee, Indrani

    2018-05-01

    The unique properties of titanium dioxide (TiO2) such as high photo catalytic activity, high chemical stability and low toxicity have made it a suitable photocatalyst in recent decades. The effect of modification of TiO2 with doping of iron on its characteristics and photo catalytic efficiency was studied. The change in band gap energy of TiO2 nanoparticles after doping with Fe has been studied. Significant enhancement in photo catalytic property of TiO2 after Fe doping under light exposure conditions has been investigated. Acute exposure to non-biodegradable Rhodamine B resulted in many health problems like burning of eyes, skin irritation, nasal burning, and chest pain etc. Therefore, degradation of this dye is needed to save environment and animals. Considering the similar radius of Fe3+ and Ti4+ ions (respectively 0.64 Å and 0.68 Å), titanium position in the lattice of TiO2 can be replaced by iron cations easily. The undoped and Fe doped TiO2 nano composites were synthesized by sol-gel method, in which 1.0M% of Fe was doped with TiO2 and then the samples were characterized by using FE-SEM, UV-Visible diffuse spectroscopy, Raman Spectroscopy, and FTIR. Photo catalytic degradation of Rhodamine B dye experiment was carried out in visible light range. After 90 min time duration pink colour of dye turned colourless, indicating significant degradation rate with time.

  18. Photocatalytic oxidative desulfurization of dibenzothiophene catalyzed by amorphous TiO2 in ionic liquid

    International Nuclear Information System (INIS)

    Zhu, Wenshuai; Xu, Yehai; Li, Huaming; Dai, Bilian; Xu, Hui; Wang, Chao; Chao, Yanhong; Liu, Hui

    2014-01-01

    Three types of TiO 2 were synthesized by a hydrolysis and calcination method. The catalysts were characterized by X-ray powder diffraction (XRD), diffuse reflectance spectrum (DRS), Raman spectra, and X-ray photoelectron spectroscopy (XPS). The XRD and Raman spectra indicated that amorphous TiO 2 was successfully obtained at 100 .deg. C. The results indicated that amorphous TiO 2 achieved the highest efficiency of desulfurization. The photocatalytic oxidation of dibenzothiophene (DBT), benzothiophene (BT), 4,6-dimethyldibenzothiophene (4,6-DMDBT) and dodecanethiol (RSH) in model oil was studied at room temperature (30 .deg. C) with three catalysts. The system contained amorphous TiO 2 , H 2 O 2 , and [Bmim]BF 4 ionic liquid, ultraviolet (UV), which played vitally important roles in the photocatalytic oxidative desulfurization. Especially, the molar ratio of H 2 O 2 and sulfur (O/S) was only 2 : 1, which corresponded to the stoichiometric reaction. The sulfur removal of DBT-containing model oil with amorphous TiO 2 could reach 96.6%, which was apparently superior to a system with anatase TiO 2 (23.6%) or with anatase - rutile TiO 2 (18.2%). The system could be recycled seven times without a signicant decrease in photocatalytic activity

  19. NOx photocatalytic degradation on gypsum plates modified by TiO2-N,C photocatalysts

    Directory of Open Access Journals (Sweden)

    Janus Magdalena

    2015-09-01

    Full Text Available In presented studies the photocatalytic decomposition of NOx on gypsum plates modified by TiO2-N,Cphotocatalysts were presented. The gypsum plates were obtained by addition of 10 or 20 wt.% of different types of titanium dioxide, such as: pure TiO2 and carbon and nitrogen co-modified TiO2 (TiO2-N,C to gypsum. TiO2-N,C photocatalysts were obtained by heating up the starting TiO2 (Grupa Azoty Zakłady Chemiczne Police S.A in the atmosphere of ammonia and carbon at the temperature: 100, 300 i 600ºC. Photocatalyst were characterized by FTIR/DRS, UVVis/DR, BET and XRD methods. Moreover the compressive strength tests of modified gypsum were also done. Photocatalytic activity of gypsum plates was done during NOx decomposition. The highest photocatalytic activity has gypsum with 20 wt.% addition of TiO2-N,C obtained at 300ºC.

  20. Facile synthesis of porous TiO_2 photocatalysts using waste sludge as the template

    International Nuclear Information System (INIS)

    Wang, Xiaopeng; Huang, Shouqiang; Zhu, Nanwen; Lou, Ziyang; Yuan, Haiping

    2015-01-01

    Graphical abstract: Waste sludge is introduced to synthesize the waste sludge templated TiO_2 photocatalyst with porous structure, which possesses better photocatalytic activity compared to pure TiO_2. - Highlights: • Waste sludge is introduced to synthesize the TiO_2 photocatalyst. • Waste sludge templated TiO_2 sample possesses porous structure. • Waste sludge templated TiO_2 sample exhibits high photocatalytic activity. - Abstract: A resource utilization method of waste sludge is present by the synthesis of waste sludge templated TiO_2 photocatalysts. The organic materials in waste sludge are used as the pore-forming agents, and the transition metals included in the remaining waste sludge through calcination (WSC) can serve as the dopants for the WSC-TiO_2 (WSCT) photocatalyst. The visible and UV–visible light driven photocatalytic activities of WSCT are much better compared to those of pure TiO_2 and WSC, and it is originated from the higher light absorption property and the efficient electron–hole pair separation provided by waste sludge.

  1. Probing Photocatalytic Characteristics of Sb-Doped TiO2 under Visible Light Irradiation

    Directory of Open Access Journals (Sweden)

    Lingjing Luo

    2014-01-01

    Full Text Available Sb-doped TiO2 nanoparticle with varied dopant concentrations was synthesized using titanium tetrachloride (TiCl4 and antimony chloride (SbCl3 as the precursors. The properties of Sb-doped TiO2 nanoparticles were characterized by X-ray diffraction (XRD, scanning electron microscope (SEM, fluorescence spectrophotometer, and Uv-vis spectrophotometer. The absorption edge of TiO2 nanoparticles could be extended to visible region after doping with antimony, in contrast to the UV absorption of pure TiO2. The results showed that the photocatalytic activity of Sb-doped TiO2 nanoparticles was much more active than pure TiO2. The 0.1% Sb-doped TiO2 nanoparticles demonstrated the best photocatalytic activity which was better than that of the Degussa P25 under visible light irradiation using terephthalic acid as fluorescent probe. The effects of Sb dopant on the photocatalytic activity and the involved mechanism were extensively investigated in this work as well.

  2. W-doped TiO2 photoanode for high performance perovskite solar cell

    International Nuclear Information System (INIS)

    Liu, Jinwang; Zhang, Jing; Yue, Guoqiang; Lu, Xingwei; Hu, Ziyang; Zhu, Yuejin

    2016-01-01

    Titanium dioxide (TiO 2 ) with dispersed W-doping shows its capability for efficient electron collection from perovskite to TiO 2 in perovskite solar cell. The conduction band (CB) of TiO 2 moves downward (positive shift) with increasing the tungsten (W) content, which enlarges the energy gap between the CB of TiO 2 and the perovskite. Thus, the efficiency of electron injection from perovskite to TiO 2 is increased. Due to the increased electron injection, W-doped TiO 2 (≤0.2% W content) enhances the short-circuit photocurrent (J sc ) of perovskite solar cell and improves the performance of perovskite solar cell. Perovskite solar cell with 0.1% W-doped photoanode obtains the highest power conversion efficiency (η = 10.6%), which shows enhancement by 13% in J sc and by 17% in η, as compared with the undoped TiO 2 perovskite solar cell.

  3. TiO2 nanoparticle biosynthesis and its physiological effect on mung bean (Vigna radiata L.

    Directory of Open Access Journals (Sweden)

    Ramesh Raliya

    2015-03-01

    Full Text Available TiO2 nanoparticle (NPs biosynthesis is a low cost, ecofriendly approach developed using the fungi Aspergillus flavus TFR 7. To determine whether TiO2 NPs is suitable for nutrient, we conducted a two part study; biosynthesis of TiO2 NP and evaluates their influence on mung bean. The characterized TiO2 NPs were foliar sprayed at 10 mgL−1 concentration on the leaves of 14 days old mung bean plants. A significant improvement was observed in shoot length (17.02%, root length (49.6%, root area (43%, root nodule (67.5%, chlorophyll content (46.4% and total soluble leaf protein (94% as a result of TiO2 NPs application. In the rhizosphere microbial population increased by 21.4–48.1% and activity of acid phosphatase (67.3%, alkaline phosphatase (72%, phytase (64% and dehydrogenase (108.7% enzyme was observed over control in six weeks old plants owing to application of TiO2 NPs. A possible mechanism has also been hypothesized for TiO2 NPs biosynthesis.

  4. Enhanced photocatalytic activity of wool-ball-like TiO2 microspheres on carbon fabric and FTO substrates

    Science.gov (United States)

    Zhang, Yu; Gu, Jian; Zhang, Mengqi

    2018-06-01

    The wool-ball-like TiO2 microspheres on carbon fabric (TiO2-CF) and FTO substrates (TiO2-FTO) have been synthesized by a facile hydrothermal method in alkali environment, using commercial TiO2 (P25) as precursors. The XRD results indicate that the as-prepared TiO2 have good crystallinity. And the SEM images show that the wool-ball-like TiO2 microspheres with a diameter of 2-3 μm are composed of TiO2 nanowires, which have a diameter of 50 nm. The photocatalytic behavior of the wool-ball-like TiO2 microspheres, TiO2-CF and TiO2-FTO under ultraviolet light was investigated by a pseudo first-order kinetic model, using methyl orange (MO) as pollutant. The wool-ball-like TiO2 microspheres obtained a degradation rate constant (Kap) of 6.91×10-3 min-1 . The Kap values of TiO2-FTO and TiO2-CF reach 13.97×10-3 min-1 and 11.80×10-3 min-1, which are 2.0 and 1.7 times higher than that of pristine wool-ball-like TiO2 microspheres due to the "sum effect" between TiO2 and substrates. This study offers a facile hydrothermal method to prepare wool-ball-like TiO2 microspheres on CF and FTO substrates, which will improve the recyclability of phtocatalysts and can be extended to other fields.

  5. Photocatalytic and microwave absorbing properties of polypyrrole/Fe-doped TiO2 composite by in situ polymerization method

    International Nuclear Information System (INIS)

    Li Qiaoling; Zhang Cunrui; Li Jianqiang

    2011-01-01

    Research highlights: → Polypyrrole/Fe-doped TiO 2 composite is prepared by in situ polymerization of pyrrole on the Fe-doped TiO 2 template. → The Fe-doped TiO 2 microbelts are prepared by sol-gel method using the absorbent cotton template for the first time. → Then the Fe-doped TiO 2 microbelts are used as template for the preparation of polypyrrole/Fe-doped TiO 2 composites. → The structure, morphology and properties of the composites are characterized with scanning electron microscope (SEM), IR, Net-work Analyzer. → A possible formation mechanism of Fe-doped TiO 2 microbelts and polypyrrole/Fe-doped TiO 2 composites has been proposed. → The effect of the mol ratio of pyrrole/Fe-doped TiO 2 on the photocatalysis properties and microwave loss properties of the composites is investigated. - Abstract: The Fe-doped TiO 2 microbelts were prepared by sol-gel method using the absorbent cotton template for the first time. Then the Fe-doped TiO 2 microbelts were used as templates for the preparation of polypyrrole/Fe-doped TiO 2 composites. Polypyrrole/Fe-doped TiO 2 composites were prepared by in situ polymerization of pyrrole on the Fe-doped TiO 2 template. The structure, morphology and properties of the composites were characterized with scanning electron microscope (SEM), FTIR, Net-work Analyzer. The possible formation mechanisms of Fe-doped TiO 2 microbelts and polypyrrole/Fe-doped TiO 2 composites have been proposed. The effect of the molar ratio of pyrrole/Fe-doped TiO 2 on the photocatalytic properties and microwave loss properties of the composites was investigated.

  6. Coulomb drag in the mesoscopic regime

    DEFF Research Database (Denmark)

    Mortensen, N. Asger; Flensberg, Karsten; Jauho, Antti-Pekka

    2002-01-01

    We present a theory for Coulomb drug between two mesoscopic systems which expresses the drag in terms of scattering matrices and wave functions. The formalism can be applied to both ballistic and disordered systems and the consequences can be studied either by numerical simulations or analytic...... means such as perturbation theory or random matrix theory. The physics of Coulomb drag in the mesoscopic regime is very different from Coulomb drag between extended electron systems. In the mesoscopic regime we in general find fluctuations of the drag comparable to the mean value. Examples are vanishing...

  7. Coulomb drag in the mesoscopic regime

    DEFF Research Database (Denmark)

    Mortensen, N.A.; Flensberg, Karsten; Jauho, Antti-Pekka

    2002-01-01

    We present a theory for Coulomb drag between two mesoscopic systems which expresses the drag in terms of scattering matrices and wave functions. The formalism can be applied to both ballistic and disordered systems and the consequences can be studied either by numerical simulations or analytic...... means such as perturbation theory or random matrix theory. The physics of Coulomb drag in the mesoscopic regime is very different from Coulomb drag between extended electron systems. In the mesoscopic regime we in general find fluctuations of the drag comparable to the mean value. Examples are vanishing...

  8. Effect of TiO_2 Loading on Pt-Ru Catalysts During Alcohol Electrooxidation

    International Nuclear Information System (INIS)

    Hasa, Bjorn; Kalamaras, Evangelos; Papaioannou, Evangelos I.; Vakros, John; Sygellou, Labrini; Katsaounis, Alexandros

    2015-01-01

    Highlights: • TiO_2 can be used to modify Pt-Ru based electrodes for alcohol oxidation. • TiO_2 modified electrodes with lower amount of metals had higher active surface area than pure Pt-Ru electrodes. • TiO_2 modified electrodes showed comparable performance with pure Pt-Ru electrode both in a single cell and in a PEM fuel cell under alcohol fuelling. - Abstract: In this study, Pt-Ru based electrodes modified by TiO_2 were prepared by means of thermal decomposition of chloride and isopropoxide precursors on Ti substrates, characterised by X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM), X-ray Photoelectron Spectroscopy (XPS), electrochemical techniques and CO stripping and used as anodes for alcohol oxidation. The minimization of the metal loading without electrocatalytic activity losses was also explored. TiO_2 was chosen due to its chemical stability, low cost and excellent properties as substrate for metal dispersion. It was found that TiO_2 loading up to 50% results in a 3-fold increase of the Electrochemically Active Surface (EAS). This conclusion has been confirmed by CO stripping experiments. All samples have been evaluated during the electrochemical oxidation of methanol, ethanol and glycerol. In all cases, the Pt_2_5-Ru_2_5-(TiO_2)_5_0 electrode had better electrocatalytic activity than the pure Pt_5_0-Ru_5_0 anode. The best modified electrode, (Pt_2_5-Ru_2_5-(TiO_2)_5_0), was also evaluated as anode in a PEM fuel cell under methanol fuelling conditions. The observed higher performance of the TiO_2 modified electrodes was attributed to the enhanced Pt-Ru dispersion as well as the formation of smaller Pt and Ru particles.

  9. Adsorption and Recovery of Polyphenolic Flavonoids Using TiO_2-Functionalized Mesoporous Silica Nanoparticles

    International Nuclear Information System (INIS)

    Khan, M. Arif; Wallace, William T.; Islam, Syed Z.; Nagpure, Suraj; Strzalka, Joseph

    2017-01-01

    Exploiting specific interactions with titania (TiO_2) has been proposed for the separation and recovery of a broad range of biomolecules and natural products, including therapeutic polyphenolic flavonoids which are susceptible to degradation, such as quercetin. Functionalizing mesoporous silica with TiO_2 has many potential advantages over bulk and mesoporous TiO_2 as an adsorbent for natural products, including robust synthetic approaches leading to high surface area, stable separation platforms. Here, TiO_2 surface functionalized mesoporous silica nanoparticles (MSNPs) are synthesized and characterized as a function of TiO_2 content (up to 636 mg TiO2/g). The adsorption isotherms of two polyphenolic flavonoids, quercetin and rutin, were determined (0.05-10 mg/ml in ethanol), and a 100-fold increase in the adsorption capacity was observed relative to functionalized nonporous particles with similar TiO_2 surface coverage. An optimum extent of functionalization (approximately 440 mg TiO_2/g particles) is interpreted from characterization techniques including grazing incidence x-ray scattering (GIXS), high resolution transmission electron microscopy (HRTEM) and nitrogen adsorption, which examined the interplay between the extent of TiO_2 functionalization and the accessibility of the porous structures. The recovery of flavonoids is demonstrated using ligand displacement in ethanolic citric acid solution (20% w/v), in which greater than 90% recovery can be achieved in a multistep extraction process. The radical scavenging activity (RSA) of the recovered and particle-bound quercetin as measured by 2,2-diphenyl-1-picrylhydrazyl (DPPH) radical scavenging assay demonstrates greater than 80% retention of antioxidant activity by both particle-bound and recovered quercetin. In conclusion, these mesoporous titanosilicate materials can serve as a synthetic platform to isolate, recover, and potentially deliver degradation-sensitive natural products to biological systems.

  10. Preparation, Characterization and Analysis of Fouling Mechanisms of TiO2- Embedded PVDF Membranes

    Directory of Open Access Journals (Sweden)

    Yoones Jafarzadeh

    2017-01-01

    Full Text Available Titanium dioxide (TiO2-embedded polyvinylidene fluoride (PVDF mixed matrix membranes were prepared through a nonsolvent induced phase separation (NIPS method. The structure of the membranes was characterized by FESEM, EDX, water drop contact angle measurement, pure water flux and mean pore radius analysis. The results showed that the prepared membranes had asymmetric structures with macro-voids and the presence of TiO2 nanoparticles increased the size of macro-voids. Moreover, pure water flux increased from 41 kg/m2h to 162 kg/m2h the content of TiO2 nanoparticles increased from 1 wt% to 5 wt% as embedded membrane. The contact angle dropped from 100° for 1 wt% TiO2- embedded membrane to 69° for 5 wt% TiO2-embedded membrane, showing that the hydrophilicity of membranes increased by addition of inorganic TiO2 nanoparticles. The fouling behavior oftheprepared mixed matrix membranes was studied in filtration process of 1% humic acid solution. The results showed that fouling resistance of the membranes increased with higher content of TiO2 nanoparticles. The results of classic fouling modeling of membranes showed that for 2 and 5 wt% TiO2-embedded membranes the best fit of the data occurred with the intermediate blockage model whereas cake formation model was the dominant mechanism for other membranes. Moreover, the analysis of fouling mechanisms by combined models showed that cake filtration-intermediate blockage model was in good agreement with the experimental data for all membranes. Finally, the results showed that the rejection of membranes increased with the addition of TiO2 nanoparticles, and then decreased.

  11. Synthesis and photocatalytic activity of mesoporous – (001) facets TiO_2 single crystals

    International Nuclear Information System (INIS)

    Dong, Yeshuo; Fei, Xuening; Zhou, Yongzhu

    2017-01-01

    Highlights: • The (001) facets of TiO_2 single crystals with mesoporous structure. • The (010) and (100) facets of TiO_2 single crystals were covered by the flower – shaped TiO_2 crystals. • This special structure could promote charge separation and provide more active sites, which will lead to a substantial increase in photocatalytic activity. - Abstract: In this work, the mesoporous – (001) facets TiO_2 single crystals have been successfully synthesized through a two-step solvothermal route without any template. Their structure and morphology were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), ultraviolet-visible (UV–vis) diffuse reflectance spectroscopy and energy dispersive X-ray spectrometer (EDX). Based on the different characteristics and atomic arrangements on each facet of anatase TiO_2 single crystals, we synthesized these mesoporous – (001) facets TiO_2 single crystals by controlling the interaction characteristics of hydrofluoric acid (HF) and isopropanol (i-PrOH) on the crystal facets. It can been seen that the (001) facets of these as-synthesized TiO_2 single crystals have a clear mesoporous structure through the SEM images and BET methods. Moreover, the other four facets were covered by the flower – shaped TiO_2 crystals with the generation of the mesoporous – (001) facets. This special and interesting morphology could promote charge separation and provide more active sites, which will lead to a substantial increase in photocatalytic activity. Moreover, it is more intuitive to reflect that the different crystal facets possess the different properties due to their atomic arrangement. Besides, according to the different synthetic routes, we proposed and discussed a plausible synthesis mechanism of these mesoporous – (001) facets TiO_2 single crystals.

  12. Preparation and Characterization of Nano-Sized TiO2@Chitosan for Bone Tissue Engineering

    Directory of Open Access Journals (Sweden)

    Lei JIANG

    2016-12-01

    Full Text Available Background: With the development of genetic engineering, it is urgent to find a vector with high transfection efficiency and good biocompatibility for genes. We considered combining nano-TiO2 with chitosan (CTS in order to tap their respective advantages to make a better new nanoparticle as gene vector.Methods: TiO2@CTS was prepared using microemulsion method. The physicochemical property of TiO2@CTS was measured by transmission electron microscopy (TEM and zeta potential. The safety and influence on MC3T3-E1 cells were detected by methyl thiazolyl tetrazolium (MTT, blood compatibility assay and flow cytometry.Results: TiO2@CTS was well prepared and it was safe to cells under concentration tests. TiO2@CTS particles had a fuzzy boundary with a particle size remaining in 20-30 nm. Besides, the results also showed that TiO2@CTS did better in cellular uptake than TiO2 at 2 h and 24 h, and had good biocompatibility. MTT assay proved that the MC3T3 cells remained good growth when treated with different concentrations of TiO2@CTS (2.5, 5, 10, 20, 40 and 80 μg/mL. Moreover, transfection assay in vitro and electrophoretic mobility shift assay illustrated the high transfection efficiency of TiO2@CTS.Conclusion: TiO2@CTS is a good choice to gene transfection, with good biocompatibility, and it also provides a new thought for the application of nanotechnology in the field of aveolar bone graft material.

  13. Liquid phase deposition of WO3/TiO2 heterojunction films with high photoelectrocatalytic activity under visible light irradiation

    International Nuclear Information System (INIS)

    Zhang, Man; Yang, Changzhu; Pu, Wenhong; Tan, Yuanbin; Yang, Kun; Zhang, Jingdong

    2014-01-01

    Highlights: • Liquid phase deposition is developed for preparing WO 3 /TiO 2 heterojunction films. • TiO 2 film provides an excellent platform for WO 3 deposition. • WO 3 expands the absorption band edge of TiO 2 film to visible light region. • WO 3 /TiO 2 heterojunction film shows high photoelectrocatalytic activity. - ABSTRACT: The heterojunction films of WO 3 /TiO 2 were prepared by liquid phase deposition (LPD) method via two-step processes. The scanning electron microscopy, X-ray diffraction and X-ray photoelectron spectroscopic analysis indicated that flower-like WO 3 film was successfully deposited on TiO 2 film with the LPD processes. The TiO 2 film provided an excellent platform for WO 3 deposition while WO 3 obviously expanded the absorption of TiO 2 film to visible light. As the result, the heterojunction film of WO 3 /TiO 2 exhibited higher photocurrent response to visible light illumination than pure TiO 2 or WO 3 film. The photoelectrocatalytic (PEC) activity of WO 3 /TiO 2 film was evaluated by degrading Rhodamin B (RhB) and 4-chlorophenol (4-CP) under visible light irradiation. The results showed that the LPD WO 3 /TiO 2 film possessed high PEC activity for efficient removal of various refractory organic pollutants

  14. Application of nitrogen-doped TiO2 nano-tubes in dye-sensitized solar cells

    DEFF Research Database (Denmark)

    Tran, Vy Anh; Thinh Troung, Trieu; Pham Phan, Thu Anh

    2017-01-01

    Our research aimed to improve the overall energy conversion efficiency of DSCs by applying nitrogen-doped TiO2 nano-tubes (N-TNT) for the preparation of DSCs photo-anodes. The none-doped TiO2 nano-tubes (TNTs) were synthesized by alkaline hydrothermal treatment of Degussa P25 TiO2 particles in 10...

  15. Development and Application of TiO2 Nanoparticles Coupled with Silver Halide

    Directory of Open Access Journals (Sweden)

    Xiaojia Wan

    2014-01-01

    Full Text Available Titanium dioxide (TiO2 is proposed to be effective photocatalyst for wastewater treatment, air purification, and self-cleaning ability, because of its strong oxidation and superhydrophilicity. In order to conquer the limits of TiO2, a variety of methods have been used. This paper presents a critical review of novel research and achievements in the modification of TiO2 nanoparticles with silver halide (AgX, X=Cl, Br, I, which aims at enhancing the visible light absorption and photosensitivity. Herein we study the synthesis, physical and chemical properties, and the mechanism of this composite photocatalyst.

  16. TiO2-Anatase Nanowire Dispersed Composite Electrode for Dye-Sensitized Solar Cells

    International Nuclear Information System (INIS)

    Asagoe, K; Suzuki, Y; Ngamsinlapasathian, S; Yoshikawa, S

    2007-01-01

    TiO 2 anatase nanowires have been prepared by a hydrothermal process followed by post-heat treatment in air. TiO 2 nanoparticle/TiO 2 nanowire composite electrodes were prepared for dye-sensitized solar cells (DSC) in order to improve light-to-electricity conversion efficiency. The TiO 2 NP/TiO 2 NW composite cells showed higher DSC performance than ordinary nanoparticle cells and fully nanowire cells: efficiency (η = 6.53 % for DSC with 10% nanowire, whereas 5.59% for 0% nanowire, and 2.42% for 100% nanowire

  17. Fabrication and electrical characteristics for MIS diode by utilizing TiO2 ceramics

    International Nuclear Information System (INIS)

    Bae, S.H.

    1981-01-01

    Metal insulator semiconductor diodes were made by utilizing TiO 2 ceramics. Tunnel field emission is here proposed as a model for rectification in TiO 2 diode. Measurements of junction depth show very satisfactory agreement with value obtained from the Richardson plot, thus serving as additional supporting evidence of field emission in TiO 2 ceramic. The measured junction area exceeds by a factor of 10 6 the value expected by assuming field emission. The Richardson plot shows a deviation from the emission theory at low voltage, which is probably due to leakage currents which are present in MIS rutile diode. (author)

  18. Effective Removal of Congo Red by Triarrhena Biochar Loading with TiO2 Nanoparticles

    Directory of Open Access Journals (Sweden)

    Peng Yu

    2018-01-01

    Full Text Available A composite of pyrolytic Triarrhena biochar loading with TiO2 nanoparticles has been synthesized by the sol-gel method. The composite shows a well-developed hollow mesoporous and macropore structure as characterized by XRD, BET, and SEM. When used as an absorbent to remove Congo red from aqueous solution, it was found that as-prepared composite performed better absorption capacity than single biochar or TiO2. The results suggest that biochar loading with TiO2 could be promisingly implemented as an environmentally friendly and inexpensive adsorbent for Congo red removal from wastewater.

  19. Fabrication and characterization of mesoporous TiO2/polypyrrole-based nanocomposite for electrorheological fluid

    International Nuclear Information System (INIS)

    Wei Chuan; Zhu Yihua; Jin Yi; Yang Xiaoling; Li Chunzhong

    2008-01-01

    Mesoporous TiO 2 /polypyrrole (PPy)-based nanocomposite for electrorheological fluid was synthesized through one-pot method. By exploiting the combination conductivity of PPy and high dielectric constant of TiO 2 , the ER fluid exhibited an enhanced effect. The shear stress was 3.3 times as high as that of mesoporous TiO 2 . Powder X-ray diffraction (XRD), TEM and Fourier transform infrared (FT-IR) spectroscopy were employed to characterize the as-made samples. Using a modified rotational viscometer, the electrorheological effect was measured. Dielectric spectra were also given to explain the mechanism

  20. Photocatalytic Degradation of Methylene Blue Using TiO2 Impregnated Diatomite

    OpenAIRE

    Zuo, Ranfang; Du, Gaoxiang; Zhang, Weiwei; Liu, Lianhua; Liu, Yanming; Mei, Lefu; Li, Zhaohui

    2014-01-01

    Nano-TiO2 showed a good catalytic activity, but it is easy to agglomerate, resulting in the reduction or even complete loss of photocatalytic activity. The dispersion of TiO2 particles on porous materials was a potential solution to this problem. Diatomite has high specific surface and absorbability because of its particular shell structure. Thus, TiO2/diatomite composite, prepared by loading TiO2 on the surface of diatomite, was a good photocatalyst, through absorbing organic compounds with ...

  1. Carbon and TiO_2 synergistic effect on methylene blue adsorption

    International Nuclear Information System (INIS)

    Simonetti, Evelyn Alves Nunes; Simone Cividanes, Luciana de; Campos, Tiago Moreira Bastos; Rossi Canuto de Menezes, Beatriz; Brito, Felipe Sales; Thim, Gilmar Patrocínio

    2016-01-01

    Due to its high efficiency, low cost and a simple operation, the adsorption process is an important and widely used technique for industrial wastewater treatment. Recent studies on the removal of artificial dyes by adsorption include a large number of adsorbents, such as: activated carbon, silicates, carbon nanotube, graphene, fibers, titanates and doped titanates. The carbon insertion in the TiO_2 structure promotes a synergistic effect on the adsorbent composite, improving the adsorption and the charge-transfer efficiency rates. However, there are few studies regarding the adsorption capacity of TiO_2/Carbon composites with the carbon concentration. This study evaluates the effect of carbon (resorcinol/formaldehyde) insertion on TiO_2 structure through the adsorption process. Adsorbents were prepared by varying the carbon weight percentages using the sol-gel method. The physicochemical properties of the catalysts prepared, such as crystallinity, particle size, surface morphology, specific surface area and pore volume were investigated. The kinetic study, adsorption isotherm, pH effect and thermodynamic study were examined in batch experiments using methylene blue as organic molecule. In addition, the effect of carbon phase on the adsorption capacity of TiO_2-carbon composite was deeply investigated. SEM micrographs showed that TiO_2 phase grows along the carbon phase and FT-IR results showed the presence of Ti−O−C chemical bonding. The experiments indicate that the carbon phase acted as a nucleation agent for the growth of TiO_2 during the sol-gel step, with a TiO_2 structure suitable for blue methylene adsorption, resulting in a material with large surface area and slit-like or wedge-shaped pores. Further experiments will show the best carbon concentration for methylene blue adsorption using a TiO_2 based material. - Highlights: • This article deals with the adsorption of methylene blue onto TiO_2-Carbon composite. • The sol-gel synthesis was efficient to insert TiO_2 particles on carbon structure. • The TiO_2 nanoparticles presented mesopore area around the carbon structure. • The wedge shapes pores which were the main responsible for methylene blue removal. • A new TiO_2-Carbon materials can be used for removal of large pollutants molecules.

  2. Nonequilibrium mesoscopic transport: a genealogy

    International Nuclear Information System (INIS)

    Das, Mukunda P; Green, Frederick

    2012-01-01

    Models of nonequilibrium quantum transport underpin all modern electronic devices, from the largest scales to the smallest. Past simplifications such as coarse graining and bulk self-averaging served well to understand electronic materials. Such particular notions become inapplicable at mesoscopic dimensions, edging towards the truly quantum regime. Nevertheless a unifying thread continues to run through transport physics, animating the design of small-scale electronic technology: microscopic conservation and nonequilibrium dissipation. These fundamentals are inherent in quantum transport and gain even greater and more explicit experimental meaning in the passage to atomic-sized devices. We review their genesis, their theoretical context, and their governing role in the electronic response of meso- and nanoscopic systems. (topical review)

  3. FTIR study of formic acid interaction with TiO2 and TiO2 doped with Pd and Cu in photocatalytic processes

    International Nuclear Information System (INIS)

    Arana, J.; Garriga i Cabo, C.; Dona-Rodriguez, J.M.; Gonzalez-Diaz, O.; Herrera-Melian, J.A.; Perez-Pena, J.

    2004-01-01

    In this study the different processes occurring on the TiO 2 and Pd and Cu doped TiO 2 surfaces during the photocatalytic formic acid degradation in the presence or absence of S 2 O 8 2- or H 2 O 2 have been investigated. FTIR studies have shown the relevance of the H-bounded hydroxyl groups. It has been observed that formate molecules interact simultaneously with the dopants and surfacial Ti atoms yielding an intermediate species which plays an important role in the phototacatalytic degradation mechanism. Also, it has been determined that Pd or Cu oxides may act as receptors or transmitters of the TiO 2 photogenerated electrons and thus modify the degradation mechanism. Different redox reactions have been proposed according to the obtained results

  4. Thermally Stable Nanocrystalline Steel

    Science.gov (United States)

    Hulme-Smith, Christopher Neil; Ooi, Shgh Woei; Bhadeshia, Harshad K. D. H.

    2017-10-01

    Two novel nanocrystalline steels were designed to withstand elevated temperatures without catastrophic microstructural changes. In the most successful alloy, a large quantity of nickel was added to stabilize austenite and allow a reduction in the carbon content. A 50 kg cast of the novel alloy was produced and used to verify the formation of nanocrystalline bainite. Synchrotron X-ray diffractometry using in situ heating showed that austenite was able to survive more than 1 hour at 773 K (500 °C) and subsequent cooling to ambient temperature. This is the first reported nanocrystalline steel with high-temperature capability.

  5. Photocatalytic degradation of paracetamol on TiO2 nanoparticles and TiO2/cellulosic fiber under UV and sunlight irradiation

    OpenAIRE

    Jallouli, Nabil; Elghniji, Kais; Trabelsi, Hassen; Ksibi, Mohamed

    2014-01-01

    In the present study, photocatalytic degradation of acetaminophen ((N-(4-hydroxyphe-nyl)acetamide)), an analgesic drug has been investigated in a batch reactor using TiO2 P25 as a photocatalyst in slurry and under UV light. Using TiO2 P25 nanoparticles, much faster photodegradation of paracetamol and effective mineralization occurred, more than 90% of 2.65 × 10−4 M paracetamol was degraded under UV irradiation. Changes in pH values affected the adsorption and the photodegradation of paracetam...

  6. Mesoscopic effects in the quantum Hall regime

    Indian Academy of Sciences (India)

    . When band mixing between multiple Landau levels is present, mesoscopic effects cause a crossover from a sequence of quantum Hall transitions for weak disorder to classical behavior for strong disorder. This behavior may be of relevance ...

  7. Quantum fluctuations in mesoscopic and macroscopic systems

    International Nuclear Information System (INIS)

    Cerdeira, H.A.; Guinea Lopez, F.; Weiss, U.

    1991-01-01

    The conference presentations have been grouped in three chapters; Quantum Transport (4 papers), Dissipation in Discrete Systems (7 papers) and Mesoscopic Junction, Rings and Arrays (6 papers). A separate abstract was prepared for each paper. Refs and figs

  8. Copper doping enhanced the oxidative stress-mediated cytotoxicity of TiO2 nanoparticles in A549 cells.

    Science.gov (United States)

    Ahmad, J; Siddiqui, M A; Akhtar, M J; Alhadlaq, H A; Alshamsan, A; Khan, S T; Wahab, R; Al-Khedhairy, A A; Al-Salim, A; Musarrat, J; Saquib, Q; Fareed, M; Ahamed, M

    2018-05-01

    Physicochemical properties of titanium dioxide nanoparticles (TiO 2 NPs) can be tuned by doping with metals or nonmetals. Copper (Cu) doping improved the photocatalytic behavior of TiO 2 NPs that can be applied in various fields such as environmental remediation and nanomedicine. However, interaction of Cu-doped TiO 2 NPs with human cells is scarce. This study was designed to explore the role of Cu doping in cytotoxic response of TiO 2 NPs in human lung epithelial (A549) cells. Characterization data demonstrated the presence of both TiO 2 and Cu in Cu-doped TiO 2 NPs with high-quality lattice fringes without any distortion. The size of Cu-doped TiO 2 NPs (24 nm) was lower than pure TiO 2 NPs (30 nm). Biological results showed that both pure and Cu-doped TiO 2 NPs induced cytotoxicity and oxidative stress in a dose-dependent manner. Low mitochondrial membrane potential and higher caspase-3 enzyme (apoptotic markers) activity were also observed in A549 cells exposed to pure and Cu-doped TiO 2 NPs. We further observed that cytotoxicity caused by Cu-doped TiO 2 NPs was higher than pure TiO 2 NPs. Moreover, antioxidant N-acetyl cysteine effectively prevented the reactive oxygen species generation, glutathione depletion, and cell viability reduction caused by Cu-doped TiO 2 NPs. This is the first report showing that Cu-doped TiO 2 NPs induced cytotoxicity and oxidative stress in A549 cells. This study warranted further research to explore the role of Cu doping in toxicity mechanisms of TiO 2 NPs.

  9. Photon side-bands in mesoscopics

    DEFF Research Database (Denmark)

    Jauho, Antti-Pekka

    1998-01-01

    This paper reviews several applications of photonic side bands, used by Buttiker and Landauer (Phys. Rev. Lett. 49, 1739 (1982)) in their theory of traversal time in tunneling, in transport and optics of mesoscopic systems. Topics include generalizations of the transmission theory of transport...... to time-dependent situations, optics and transport of mesoscopic systems in THz electromagnetic fields, and phase-measurements of photon-assisted tunneling through a quantum dot. (C) 1998 Academic Press Limited....

  10. Anti-fish bacterial pathogen effect of visible light responsive Fe3O4@TiO2 nanoparticles immobilized on glass using TiO2 sol–gel

    International Nuclear Information System (INIS)

    Yeh, N.; Lee, Y.C.; Chang, C.Y.; Cheng, T.C.

    2013-01-01

    This paper demonstrates a fish pathogen reduction procedure that uses TiO 2 sol–gel coating Fe 3 O 4 @TiO 2 powder on glass substrate. Such procedure can effectively relieve two constraints that haunt TiO 2 sterilization applications: 1) the need for UV for overcoming the wide band gap of pure TiO 2 and 2) the difficulty of its recovering from water for reuse. In the process, visible light responsive Fe 3 O 4 /TiO 2 nanoparticles are synthesized and immobilized on glass using TiO 2 sol–gel as the binder for fish bacterial pathogen disinfection test. After 3 h of visible light irradiation, the immobilized Fe 3 O 4 @TiO 2 's inhibition efficiencies for fish bacterial pathogen are, respectively, 50% for Edwardsiella tarda (BCRC 10670) and 23% for Aeromonas hydrophila (BCRC 13018)

  11. ELECTROPHORETIC DEPOSITION OF TIO2-MULTI-WALLED CARBON NANOTUBE COMPOSITE COATINGS: MORPHOLOGICAL STUDY

    Directory of Open Access Journals (Sweden)

    M. S. MAHMOUDI JOZEE

    2016-09-01

    Full Text Available A homogenous TiO2 / multi-walled carbon nanotubes(MWCNTs composite film were prepared by electrophoretic co-deposition from organic suspension on a stainless steel substrate.  In this study, MWCNTs was incorporated to the coating because of their long structure and their capability to be functionalized by different inorganic groups on the surface. FTIR spectroscopy showed the existence of carboxylic groups on the modified carbon nanotubes surface. The effect of applied electrical fields, deposition time and concentration of nanoparticulates on coatings morphology were investigated by scanning electron microscopy. It was found that combination of MWCNTs within TiO2 matrix eliminating micro cracks presented on TiO2 coating. Also, by increasing the deposition voltages, micro cracks were increased. SEM observation of the coatings revealed that TiO2/multi-walled carbon nanotubes coatings produced from optimized electric field was uniform and had good adhesive to the substrate.

  12. Effect of chemisorbed surface species on the photocatalytic activity of TiO2 nanoparticulate films

    International Nuclear Information System (INIS)

    Cao Yaan; Yang Wensheng; Chen Yongmei; Du Hui; Yue, Polock

    2004-01-01

    TiO 2 sols prepared in acidic and basic medium were deposited into films by a spin coating method. Photodegradation experiments showed that photocatalytic activity of the films prepared from acidic sol was much higher than that from basic sol. It is identified that there are more chemisorbed species of CO 2 on the surface of the TiO 2 films from the basic sol than on the surface of the TiO 2 films from the acidic sol. The chemisorbed species of CO 2 reduce the concentration of active species such as hydroxyl group and bridging oxygen on surface of the TiO 2 film and contribute to the formation of surface electron traps in the band gap which are detrimental to charge separation, thus lowering the photocatalytic activity

  13. The properties of transparent TiO2 films for Schottky photodetector

    Directory of Open Access Journals (Sweden)

    Sung-Ho Park

    2017-08-01

    Full Text Available In this data, the properties of transparent TiO2 film for Schottky photodetector are presented for the research article, entitled as “High-performing transparent photodetectors based on Schottky contacts” (Patel et al., 2017 [1]. The transparent photoelectric device was demonstrated by using various Schottky metals, such as Cu, Mo and Ni. This article mainly shows the optical transmittance of the Ni-transparent Schottky photodetector, analyzed by the energy dispersive spectroscopy and interfacial TEM images for transparency to observe the interface between NiO and TiO2 film. The observation and analyses clearly show that no pinhole formation in the TiO2 film by Ni diffusion. The rapid thermal process is an effective way to form the quality TiO2 film formation without degradation, such as pinholes (Qiu et al., 2015 [2]. This thermal process may apply to form functional metal oxide layers for solar cells and photodetectors.

  14. Biomimetic Approach to Solar Cells Based on TiO2 Nanotubes

    National Research Council Canada - National Science Library

    Allen, Jan L; Lee, Ivan C; Wolfenstine, Jeff

    2008-01-01

    The goal of this research was to explore the use of nanotube titanium dioxide (TiO2) as an electrode material in dye-sensitized solar cells in order to further the development of solar cell technology...

  15. Synthesis of nanocomposite coating based on TiO2/ZnAl layer double hydroxides

    International Nuclear Information System (INIS)

    Jovanov, V.; Rudic, O.; Ranogajec, J.; Fidanchevska, E.

    2017-01-01

    The aim of this investigation was the synthesis of nanocomposite coatings based on Zn-Al layered double hydroxides (Zn-Al LDH) and TiO2. The Zn-Al LDH material, which acted as the catalyst support of the active TiO2 component (in the content of 3 and 10 wt. %), was synthesized by a low super saturation co-precipitation method. The interaction between the Zn-Al LDH and the active TiO2 component was accomplished by using vacuum evaporation prior to the mechanical activation and only by mechanical activation. The final suspension based on Zn-Al LDH and 10wt. % TiO2, impregnated only by mechanical activation, showed the optimal characteristics from the aspect of particle size distribution and XRD analysis. These properties had a positive effect on the functional properties of the coatings (photocatalytic activity and self-cleaning efficiency) after the water rinsing procedure. [es

  16. Polymer Photovoltaic Cell Using TiO2/G-PEDOT Nanocomplex Film as Electrode

    Directory of Open Access Journals (Sweden)

    F. X. Xie

    2008-01-01

    Full Text Available Using TiO2/G-PEDOT (PEDOT/PSS doped with glycerol nanocomplex film as a substitute for metal electrode in organic photovoltaic cell is described. Indium tin oxide (ITO worked as cathode and TiO2/G-PEDOT nanocomplex works as anode. The thickness of TiO2 layer in nanocomplex greatly affects the act of this nonmetallic electrode of the device. To enhance its performance, this inverted organic photovoltaic cell uses another TiO2 layer as electron selective layer contacted to ITO coated glass substrates. All films made by solution processing techniques are coated on the transparent substrate (glass with a conducting film ITO. The efficiency of this solar cell is compared with the conventional device using Al as electrode.

  17. Influence of TiO2 Nanoparticles on Growth, Chemical Constituents and Toxicity of Fennel Plant

    International Nuclear Information System (INIS)

    Khater, M.S.; Osman, Y.A.H.

    2015-01-01

    The present work is carried out to evaluate the effect of TiO 2 nanoparticles treatments on fennel (Feoniculum Vulgare Mill) plants. The plants were sprayed with different concentrations of TiO 2 nanoparticles 2, 4 and 6 ppm. In most cases, the tallest plants, the highest number of branches , the highest fruit yield per plant and the highest values of Pigments, Carbohydrates, Sugars nitrogen , phosphorus , potassium were obtained from the treatment of 6 ppm TiO 2 nanoparticles of fennel . Results showed that sprayed fennel plant with concentrations of TiO 2 nanoparticles 0, 2, 4 and 6 ppm is safe and enhanced chlorophyll synthesis and consequently enhanced photosynthesis

  18. ADSORCIÓN DE ALDEHÍDOS INSATURADOS SOBRE TiO2

    OpenAIRE

    Natalia Ortega; Oswaldo Núñez

    2012-01-01

    En el presente trabajo se estudió la adsorción de aldehídos insaturados sobre la superficie del TiO2. Para evaluar su eficiencia como catalizador, se realizaron experimentos de fotocatálisis heterogénea de p-nitrofenol (PNF) y una muestra proveniente de efluentes industriales. Se empleó un simulador solar y cuatro sistemas de TiO2: el TiO2-sólo (sin modificar) y los sistemas TiO2-dienal constituidos por la adsorción química de 2,4 hexadienal, 2,4 heptadienal y el trans-cinamaldehído sobre la ...

  19. Control of Electron Transfer from Lead-Salt Nanocrystals to TiO 2

    KAUST Repository

    Hyun, Byung-Ryool; Bartnik, A. C.; Sun, Liangfeng; Hanrath, Tobias; Wise, F. W.

    2011-01-01

    The roles of solvent reorganization energy and electronic coupling strength on the transfer of photoexcited electrons from PbS nanocrystals to TiO 2 nanoparticles are investigated. We find that the electron transfer depends only weakly

  20. GW quasiparticle bandgaps of anatase TiO2 starting from DFT + U.

    Science.gov (United States)

    Patrick, Christopher E; Giustino, Feliciano

    2012-05-23

    We investigate the quasiparticle band structure of anatase TiO(2), a wide gap semiconductor widely employed in photovoltaics and photocatalysis. We obtain GW quasiparticle energies starting from density-functional theory (DFT) calculations including Hubbard U corrections. Using a simple iterative procedure we determine the value of the Hubbard parameter yielding a vanishing quasiparticle correction to the fundamental bandgap of anatase TiO(2). The bandgap (3.3 eV) calculated using this optimal Hubbard parameter is smaller than the value obtained by applying many-body perturbation theory to standard DFT eigenstates and eigenvalues (3.7 eV). We extend our analysis to the rutile polymorph of TiO(2) and reach similar conclusions. Our work highlights the role of the starting non-interacting Hamiltonian in the calculation of GW quasiparticle energies in TiO(2) and suggests an optimal Hubbard parameter for future calculations.

  1. Recent Progress in TiO2-Mediated Solar Photocatalysis for Industrial Wastewater Treatment

    Directory of Open Access Journals (Sweden)

    Tong Zhang

    2014-01-01

    Full Text Available The current paper reviews the application of TiO2-mediated solar photocatalysis for industrial wastewater treatment, starting with a brief introduction on the background of industrial wastewater and the development of wastewater treatment processes, especially advanced oxidation processes (AOPs. We, then, discuss the application of solar TiO2 photocatalysis in treating different kinds of industrial wastewater, such as paper mill wastewater, textile wastewater, and olive mill wastewater. In the end, we compare solar TiO2 photocatalysis with other AOPs in terms of effectiveness, energy, and chemical consumption. Personal perspectives are also given, which may provide new insights to the future development of TiO2 photocatalysis for industrial wastewater.

  2. Synthesis of highly ordered TiO2 nanotube in malonic acid solution by anodization.

    Science.gov (United States)

    Ryu, Won Hee; Park, Chan Jin; Kwon, Hyuk Sang

    2008-10-01

    We synthesized TiO2 nanotube array by anodizing in a solution of malonic acid (HOOCCH2COOH) and NH4F, and analyzed the morphology of the nanotube using scanning electron microscopy (SEM). The morphology of TiO2 nanotube was largely affected by anodizing time, anodizing voltage, and malonic acid concentration. With increasing the anodizing voltage from 5 V to 20 V, the diameter of TiO2 nanotube was increased from about 20 nm to 110 nm and its length from about 10 nm to 700 nm. In addition, the length of TiO2 nanotube was increased with increasing anodizing time up to 6 h at 20 V. We obtained the longest and the most highly ordered nanotube structure when anodizing Ti in a solution of 0.5 wt% NH4F and 1 M malonic acid at 20 V for 6 h.

  3. Three-dimensional observation of TiO2 nanostructures by electron tomography

    KAUST Repository

    Suh, Young Joon; Lu, Ning; Park, Seong Yong; Lee, Tae Hun; Lee, Sang Hoon; Cha, Dong Kyu; Lee, Min Gun; Huang, Jie; Kim, Sung Soo; Sohn, Byeong Hyeok; Kim, Geung Ho; Ko, Min Jae; Kim, Jiyoung; Kim, Moon J.

    2013-01-01

    Three-dimensional nanostructures of TiO2 related materials including nanotubes, electron acceptor materials in hybrid polymer solar cells, and working electrodes of dye sensitized solar cells (DSSCs) were visualized by electron tomography as well

  4. Novel bamboo structured TiO2 nanotubes for energy storage/production applications

    Science.gov (United States)

    Samuel, J. J.; Beh, K. P.; Cheong, Y. L.; Yusuf, W. A. A.; Yam, F. K.

    2018-04-01

    Nanostructured TiO2 received much attention owing to its high surface-to-volume ratio, which can be advantageous in energy storage and production applications. However, the increase in energy consumption at present and possibly the foreseeable future has demanded energy storage and production devices of even higher performance. A direct approach would be manipulating the physical aspects of TiO2 nanostructures, particularly, nanotubes. In this work, dual voltage anodization system has been implemented to fabricate bamboo shaped TiO2 nanotubes, which offers even greater surface area. This unique nanostructure would be used in Dye Sensitized Solar Cell (DSSC) fabrication and its performance will be evaluated and compared along other forms of TiO2 nanotubes. The results showed that bamboo shaped nanotubes indeed are superior morphologically, with an increase of efficiency of 107% at 1.130% efficiency when compared to smooth walled nanotubes at 0.546% efficiency.

  5. Investigation on the Photoelectrocatalytic Activity of Well-Aligned TiO2 Nanotube Arrays

    Directory of Open Access Journals (Sweden)

    Xiaomeng Wu

    2012-01-01

    Full Text Available Well-aligned TiO2 nanotube arrays were fabricated by anodizing Ti foil in viscous F− containing organic electrolytes, and the crystal structure and morphology of the TiO2 nanotube array were characterized and analyzed by XRD, SEM, and TEM, respectively. The photocatalytic activity of the TiO2 nanotube arrays was evaluated in the photocatalytic (PC and photoelectrocatalytic (PEC degradation of methylene blue (MB dye in different supporting solutions. The excellent performance of ca. 97% for color removal was reached after 90 min in the PEC process compared to that of PC process which indicates that a certain external potential bias favors the promotion of the electrode reaction rate on TiO2 nanotube array when it is under illumination. In addition, it is found that PEC process conducted in supporting solutions with low pH and containing Cl− is also beneficial to accelerate the degradation rate of MB.

  6. Room temperature alcohol sensing by oxygen vacancy controlled TiO2 nanotube array

    International Nuclear Information System (INIS)

    Hazra, A.; Dutta, K.; Bhowmik, B.; Bhattacharyya, P.; Chattopadhyay, P. P.

    2014-01-01

    Oxygen vacancy (OV) controlled TiO 2 nanotubes, having diameters of 50–70 nm and lengths of 200–250 nm, were synthesized by electrochemical anodization in the mixed electrolyte comprising NH 4 F and ethylene glycol with selective H 2 O content. The structural evolution of TiO 2 nanoforms has been studied by field emission scanning electron microscopy. Variation in the formation of OVs with the variation of the structure of TiO 2 nanoforms has been evaluated by photoluminescence and X-ray photoelectron spectroscopy. The sensor characteristics were correlated to the variation of the amount of induced OVs in the nanotubes. The efficient room temperature sensing achieved by the control of OVs of TiO 2 nanotube array has paved the way for developing fast responding alcohol sensor with corresponding response magnitude of 60.2%, 45.3%, and 36.5% towards methanol, ethanol, and 2-propanol, respectively.

  7. Studies on Nano-Engineered TiO2 Photo Catalyst for Effective Degradation of Dye

    Science.gov (United States)

    Sowmya, S. R.; Madhu, G. M.; Hashir, Mohammed

    2018-02-01

    All Heterogeneous photo catalysis employing efficient photo-catalyst is the advanced dye degradation technology for the purification of textile effluent. The present work focuses on Congo red dye degradation employing synthesized Ag doped TiO2 nanoparticles as photocatalyst which is characterized using SEM, XRD and FTIR. Studies are conducted to study the effect of various parameters such as initial dye concentration, catalyst loading and pH of solution. Ag Doped TiO2 photocatalyst improve the efficacy of TiO2 by reducing high band gap and electron hole recombination of TiO2. The reaction kinetics is analyzed and the process is found to follow pseudo first order kinetics.

  8. Amine functionalized TiO2-carbon nanotube composite: synthesis, characterization and application to glucose biosensing

    Science.gov (United States)

    Tasviri, Mahboubeh; Rafiee-Pour, Hossain-Ali; Ghourchian, Hedayatollah; Gholami, Mohammad Reza

    2011-12-01

    The synthesis of amine functionalized TiO2-coated multiwalled carbon nanotubes (NH2-TiO2-CNTs) using sol-gel method was investigated. The synthesized nanocomposite was characterized with XRD, FTIR spectroscopy, BET test and SEM imaging. The results demonstrated a unique nanostructure with no destruction of the CNTs' shape. In addition, the presence of amine groups on the composite surface was confirmed by FTIR. This nanocomposite was used for one-step immobilization of glucose oxidase (GOx) to sense glucose. The result of cyclic voltammetry showed a pair of well-defined and quasi-reversible peaks for direct electron transfer of GOx in the absence of glucose. Also, the result of electrochemical impedance spectroscopy indicated that GOx was successfully immobilized on the surface of NH2-TiO2-CNTs. Furthermore, good amperometric response showed that immobilized GOx on the NH2-TiO2-CNTs exhibits exceptional bioelectrocatalytic activity toward glucose oxidation.

  9. Variable range hopping in TiO2 insulating layers for oxide electronic devices

    Directory of Open Access Journals (Sweden)

    Y. L. Zhao

    2012-03-01

    Full Text Available TiO2 thin films are of importance in oxide electronics, e.g., Pt/TiO2/Pt for memristors and Co-TiO2/TiO2/Co-TiO2 for spin tunneling devices. When such structures are deposited at a variety of oxygen pressures, how does TiO2 behave as an insulator? We report the discovery of an anomalous resistivity minimum in a TiO2 film at low pressure (not strongly dependent on deposition temperature. Hall measurements rule out band transport and in most of the pressure range the transport is variable range hopping (VRH though below 20 K it was difficult to differentiate between Mott and Efros-Shklovskii's (ES mechanism. Magnetoresistance (MR of the sample with lowest resistivity was positive at low temperature (for VRH but negative above 10 K indicating quantum interference effects.

  10. 1 composite mixture of TiO2 nanoparticles and nanotubes in dye

    Indian Academy of Sciences (India)

    Administrator

    Abstract. TiO2-based nanotubes (NTs), nanoparticles (NPs) and composite structural film (50% NP + 50% ... of faster electron injection ratio compared with other .... exist in this system. .... the open circuit voltage, Im the maximum current and.

  11. Production of TiO_2 particles by sol-gel ultrasound assisted for photocatalytic applications

    International Nuclear Information System (INIS)

    Martinez Rojas, Vanessa; Solis Veliz, Jose; Gomez Leon, Monica; Matejova, Lenka; Lopez, Alcides; Cruz, Gerardo J.

    2015-01-01

    Synthesis of TiO_2 particles was made by sol-gel technique assisted of ultrasonic radiation from an alcoholic solution of titanium isopropoxide. Then was subjected to a heat treatment in air at 350 °C for 1 h. X-ray diffraction and transmission electron microscopy confirmed that the size of the crystalline domains is between 10 and 37 nm. Infrared spectroscopy study confirms the presence of -OH groups on the surface of TiO_2. Modification of the morphology and surface area, due to the influence of exposure time to the ultrasonic radiation, is evidenced by studies of SEM and BET respectively. Properties of TiO_2 obtained were studied by monitoring the degradation of solutions of methyl orange in the presence of UV-A radiation. It was observed that larger the ultrasonic radiation exposure during the TiO_2 synthesis larger the constant velocity for the photocatalytic reaction for the methyl orange. (author)

  12. High-temperature interaction in the ZrSiO4-TiO2 system

    International Nuclear Information System (INIS)

    Matveeva, F.A.; Melekhova, T.F.; Samsonova, T.I.

    1976-01-01

    The solid phase interaction in the ZrSiO 4 - TiO 2 system in the region of lower concentrations of TiO 2 (between 0-30%) when heating in the range 1400-1600 0 C is investigated. The different mechanism of the interaction of zircon and titanium dioxide with a content of titanium dioxide of 10% and higher is shown. In compounds with a TiO 2 content to 10%, a solid solution of titanium dioxide and zircon arises, with a limiting value of TiO 2 dissolving in zircon of 1% at 1400 0 C and 2% at 1500-1600 0 C. The partial decomposition of zircon giving crystobalite and the solid solution of separated zirconium dioxide with rutile occurs when the content of titanium dioxide is higher than 10%

  13. TiO2 Nanoparticles as a Soft X-ray Molecular Probe

    Energy Technology Data Exchange (ETDEWEB)

    Larabell, Carolyn; Ashcroft, Jared M.; Gu, Weiwei; Zhang, Tierui; Hughes, Steven M.; Hartman, Keith B.; Hofmann, Cristina; Kanaras, Antonios G.; Kilcoyne, David A.; Le Gros, Mark; Yin, Yadong; Alivisatos, A. Paul; Larabell, Carolyn A.

    2007-06-30

    With the emergence of soft x-ray techniques for imaging cells, there is a pressing need to develop protein localization probes that can be unambiguously identified within the region of x-ray spectrum used for imaging. TiO2 nanocrystal colloids, which have a strong absorption cross-section within the "water-window" region of x-rays, areideally suited as soft x-ray microscopy probes. To demonstrate their efficacy, TiO2-streptavidin nanoconjugates were prepared and subsequently labeled microtubules polymerized from biotinylated tubulin. The microtubules were imaged using scanning transmission x-ray microscopy (STXM), and the TiO2 nanoparticle tags were specifically identified using x-ray absorption near edge spectroscopy (XANES). These experiments demonstrate that TiO2 nanoparticles are potential probes for protein localization analyses using soft x-ray microscopy.

  14. Non-equilibrium nitrogen DC-arc plasma treatment of TiO2 nanopowder.

    Science.gov (United States)

    Suzuki, Yoshikazu; Gonzalez-Aguilar, José; Traisnel, Noel; Berger, Marie-Hélène; Repoux, Monique; Fulcheri, Laurent

    2009-01-01

    Non-equilibrium nitrogen DC-arc plasma treatment of a commercial TiO2 anatase nanopowder was examined to obtain nitrogen-doped TiO2. By using a non-thermal discharge at low current (150 mA) and high voltage (1200 V) using pure N2 gas, light yellowish-gray TiO2 powder was successfully obtained within a short period of 5-10 min. XPS and TEM-EELS studies confirmed the existence of doped nitrogen. Due to the relatively mild conditions (plasma power of 180 W), metastable anatase structure and fine crystallite size of TiO2 (ca. 10 nm) were maintained after the plasma treatment. The in-flight powder treatment system used in this study is promising for various type of powder treatment.

  15. Spectroscopic ellipsometry characterization of amorphous and crystalline TiO2 thin films grown by atomic layer deposition at different temperatures

    Science.gov (United States)

    Saha, D.; Ajimsha, R. S.; Rajiv, K.; Mukherjee, C.; Gupta, M.; Misra, P.; Kukreja, L. M.

    2014-10-01

    TiO2 thin films of widely different structural and morphological characteristics were grown on Si (1 0 0) substrates using Atomic Layer Deposition (ALD) by varying the substrate temperature (Ts) in a wide range (50 °C ≤ Ts ≤ 400 °C). Spectroscopic ellipsometry (SE) measurements were carried out to investigate the effect of growth temperature on the optical properties of the films. Measured SE data were analyzed by considering double layer optical model for the sample together with the single oscillator Tauc-Lorentz dispersion relation. Surface roughness was taken into consideration due to the columnar growths of grains in crystalline films. The refractive index was found to be increased from amorphous (Ts ≤ 150 °C) to the nanocrystalline films (2500 < Ts ≤ 400 °C). The pronounced surface roughening for the large-grained anatase film obtained at the amorphous to crystalline phase transformation temperature of 200 °C, impeded SE measurement. The dispersions of refractive indices below the interband absorption edge were found to be strongly correlated with the single oscillator Wemple-DiDomenico (WD) model. The increase in dispersion energy parameter in WD model from disordered amorphous to the more ordered nanocrystalline films was found to be associated with the increase in the film density and coordination number.

  16. One-step preparation and photocatalytic performance of vanadium doped TiO2 coatings

    International Nuclear Information System (INIS)

    Vasilić, R.; Stojadinović, S.; Radić, N.; Stefanov, P.; Dohčević-Mitrović, Z.; Grbić, B.

    2015-01-01

    In this paper, we have investigated one-step preparation of vanadium doped TiO 2 coatings formed by plasma electrolytic oxidation (PEO) of titanium in electrolyte containing 10 g/L Na 3 PO 4 ·12H 2 O + 0.5 g/L NH 4 VO 3 . The morphology, phase structure, and elemental composition of the formed coatings were characterized by atomic force microscopy (AFM), x-ray diffraction (XRD), and x-ray photoelectron spectroscopy (XPS) techniques. Ultraviolet–visible diffuse reflectance spectroscopy (UV–Vis DRS) was employed to evaluate the band gap energy of obtained coatings. Vanadium doped TiO 2 coatings are partly crystallized and mainly composed of anatase phase TiO 2 , with up to about 2 wt% of vanadium present in the surface layer of the oxide. The valence band photoelectron spectra and UV–Vis DRS showed that vanadium doped TiO 2 coatings exhibit notable red shift with respect to the pure TiO 2 coatings. The photocatalytic activity was evaluated by monitoring the degradation of methyl orange under simulated sunlight conditions. Photocatalytic activity of vanadium doped TiO 2 coatings increases with PEO time. Prolonged PEO times result in higher roughness of obtained coatings, thus increasing surface area available for methyl orange degradation. Vanadium doped TiO 2 coatings obtained after 180 s of PEO time exhibit the best photocatalytic activity and about 67% of methyl orange is degraded after 12 h of irradiation under simulated sunlight. - Highlights: • One-step preparation of V-doped TiO 2 coatings in 10 g/L Na 3 PO 4 ·12H 2 O + 0.5 g/L NH 4 VO 3 . • Properties of obtained coatings strongly depend on microdischarge characteristics. • Band gap of V-doped TiO 2 coatings is shifted towards red side of the spectrum. • V-doped TiO 2 coatings have better photocatalytic activity than pure TiO 2 . • After 12 h of simulated sunlight irradiation, 67% of methyl orange was decomposed

  17. Karakteristik Pasta TiO2 Suhu Rendah untuk Aplikasi Dye Sensitized Solar Cell (DSSC

    Directory of Open Access Journals (Sweden)

    Mariya Al Qibtiya

    2016-06-01

    Full Text Available Pada tulisan ini, diuraikan karakteristik pasta TiO2 suhu rendah untuk aplikasi sel surya berbasis dye-sensitized yang dipreparasi dengan penambahan serbuk TiO2 reflektor. Penambahan TiO2 reflektor sebagai light scattering layer pada pasta dilakukan untuk melihat pengaruhnya terhadap karakteristik listrik sel surya yang dihasilkan. Preparasi pasta dilakukan menggunakan bahan komersial yaitu pasta T-Nanooxide D-L (Solaronix dan serbuk pasta WER2-O (Dyesiol sebagai bahan reflector. Bahan tersebut dianalisis struktur kristalnya. Hasil karakterisasi X-Ray Diffraction (XRD menunjukan bahwa bahan TiO2 serbuk yang digunakan adalah nanokristal dengan struktur kristal anatase. Pasta ini dideposisi di atas permukaan plastik dan kaca konduktif (ITO-PET dan FTO dengan metode doctor blade printing. Proses sintering lapisan TiO2 dilakukan pada suhu rendah yaitu 120 ˚C selama 4 jam. Morfologi permukaan lapisan TiO2 dianalisa menggunakan Scanning Electron Microscopy (SEM. Lapisan TiO2 yang terbentuk diaplikasikan pada DSSC sebagai fotoelektroda. Pewarnaan dengan larutan N-719 (Ruthenium Complex, lapisan elektroda kerja platina dan larutan elektrolit iodine. Karakteristik kurva I-V dengan ukuran sel daerah aktif 1 cm2 diukur menggunakan Sun Simulator AM1,5 dengan sumber cahaya Xenon dan intensitas 50 mW/cm2. Hasil pengukuran menunjukkan penambahan serbuk TiO2 reflektor dapat meningkatkan unjuk kerja sel surya fleksibel yang dihasilkan. Efisiensi terbaik DSSC yang dihasilkan adalah 0,166% untuk substrat plastik dan 0,167% untuk substrat kaca.

  18. TiO2-Based Nanomaterials for Gas Sensing-Influence of Anatase and Rutile Contributions.

    Science.gov (United States)

    Zakrzewska, K; Radecka, M

    2017-12-01

    The paper deals with application of three nanomaterial systems: undoped TiO 2 , chromium-doped TiO 2 :Cr and TiO 2 -SnO 2 synthesized by flame spray synthesis (FSS) technique for hydrogen sensing. The emphasis is put on the role of anatase and rutile polymorphic forms of TiO 2 in enhancing sensitivity towards reducing gases. Anatase-to-rutile transformation is achieved by annealing of undoped TiO 2 in air at 700 °C, specific Cr doping and modification with SnO 2 . Undoped TiO 2 and TiO 2 -SnO 2 exhibit n-type behaviour and while TiO 2 : 5 at.% Cr is a p-type semiconductor. X-ray diffraction (XRD) has been applied to determine anatase-to-rutile weight ratio as well as anatase and rutile crystal size. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) have been used to characterize the structure and morphological parameters. Optical reflectometry enabled to find and compare the band gaps E g of anatase and rutile predominated compositions. Electrical properties, i.e. the electrical conductivity and values of constant phase element (CPE), have been established on the basis of impedance spectroscopy. Dynamic responses of the electrical resistance as a function of hydrogen concentration revealed that predominance of rutile in anatase/rutile mixture is beneficial for gas sensing. Partial transformation to rutile in all three material systems under study resulted in an increased sensitivity towards hydrogen. It is proposed that this effect can be explained in a similar way as in photocatalysis, i.e. by specific band alignment and electron transfer from rutile to anatase to facilitate oxygen preadsorption on the surface of anatase grains.

  19. Genotoxic and cytotoxic activity of green synthesized TiO2 nanoparticles

    Science.gov (United States)

    Koca, Fatih Doğan; Duman, Fatih

    2018-03-01

    Nowadays, nanomaterials that are smaller than 100 nm in size are very attractive owing to their enhanced physicochemical properties. Although they have been used widely for industrial applications, their toxicity still remains a problem. This article is a new record of the synthesis of titanium dioxide nanoparticles (TiO2 NPs) by a Mentha aquatica leaf extract and determination of its toxicity to rat marrow mesenchymal stem cells. In this study, we aimed to determine the genotoxic and cytotoxic effects of biologically synthetized TiO2 NPs. The characteristic peak of the nanomaterial was observed at 354 nm. The mean size of the nanomaterial was measured to be 69 nm from SEM images. According to zeta analysis, the surface charge of the nanomaterial was - 37.6 mV. The crystalline structure of the nanomaterial was determined using XRD analysis. It was concluded that the obtained nanomaterial was TiO2 The results of the FT-IR analysis showed that the functional groups that were found in the plant extract could play an important role in the formation and stabilization of TiO2 NPs. The effective size of the TiO2 NPs was found to be 304 nm using DLS analysis. The TGA analysis results showed that the total mass loss was 4% at 900 °C. According to DNA cleavage analysis results, TiO2 NPs cause damage to the plasmid pBR322 DNA in a concentration-dependant matter. It has been noted that TiO2 NPs lead to decreased cell viability during increased time and concentration of applications on rat marrow mesenchymal stem cells. It has also been determined that bulk TiO2 causes a greater reduction in the stem cell viability compared to the biosynthesized NPs. The obtained results could be useful for further application and toxicity studies.

  20. CdS-sensitized TiO2 nanocorals: hydrothermal synthesis, characterization, application.

    Science.gov (United States)

    Mali, S S; Desai, S K; Dalavi, D S; Betty, C A; Bhosale, P N; Patil, P S

    2011-10-01

    Cadmium sulfide (CdS) nanoparticle-sensitized titanium oxide nanocorals (TNC) were synthesized using a two-step deposition process. The TiO(2) nanocorals were grown on the conducting glass substrates (FTO) using A hydrothermal process and CdS nanoparticles were loaded on TNC using successive ionic layer adsorption and reaction (SILAR) method. The TiO(2), CdS and TiO(2)-CdS samples were characterized by optical absorption, X-ray diffraction (XRD), FT-Raman, FT-IR, scanning electron microscopy (SEM) and contact angle. Further, their photoelectrochemical (PEC) performance was tested in NaOH, Na(2)S-NaOH-S and Na(2)S electrolytes, respectively. When CdS nanoparticles are coated on TNCs, the optical absorption is found to be enhanced and band edge is red-shifted towards visible region. The TiO(2)-CdS sample exhibits improved photoelectrochemical (PEC) performance with maximum short circuit current of (J(sc)) 1.04 mA cm(-2). After applying these TiO(2)-CdS electrodes in photovoltaic cells, the photocurrent was found to be enhanced by 2.7 and 32.5 times, as compared with those of bare CdS and TiO(2) nanocorals films electrodes respectively. Also, the power conversion efficiency of TiO(2)-CdS electrodes is 0.72%, which is enhanced by about 16 and 29 times for TiO(2), CdS samples. This journal is © The Royal Society of Chemistry and Owner Societies 2011

  1. Deep-level transient spectroscopy of TiO2/CuInS2 heterojunctions

    NARCIS (Netherlands)

    Nanu, M.; Boulch, F.; Schoonman, J.; Goossens, A.

    2005-01-01

    Deep-level transient spectroscopy (DLTS) has been used to measure the concentration and energy position of deep electronic states in CuInS2. Flat TiO2?CuInS2 heterojunctions as well as TiO2-CuInS2 nanocomposites have been investigated. Subband-gap electronic states in CuInS2 films are mostly due to

  2. Catalytic Study on TiO2 Photo catalyst Synthesised Via Microemulsion Method on Atrazine

    International Nuclear Information System (INIS)

    Ruslimie, C.A.; Hasmizam Razali; Khairul, W.M.

    2011-01-01

    Titanium dioxide photo catalyst was synthesised by microemulsions method under controlled hydrolysis of titanium butoxide, Ti(O(CH 2 ) 3 )CH 3 . The synthesised TiO 2 photo catalyst was compared with Sigma-commercial TiO 2 by carrying out the investigation on its properties using scanning electron microscopy (SEM), x-ray diffraction (XRD) analysis and thermal gravimetric analysis (TGA). The photo catalytic activities for both photo catalysts were studied for atrazine photodegradation. (author)

  3. Physicochemical Study of Photocatalytic Activity of TiO2 Supported Palygorskite Clay Mineral

    Directory of Open Access Journals (Sweden)

    Lahcen Bouna

    2013-01-01

    Full Text Available This study deals with the influence of physicochemical parameters, namely, the photocatalyst loading, dye concentration, and pH of polluted solutions, on the degradation efficiency of Orange G (OG solutions containing TiO2 nanoparticles supported on palygorskite clay mineral (TiO2-Pal. The TiO2 photocatalyst attached to natural palygorskite fibers was elaborated by colloidal sol-gel route. It exhibits the anatase structure that is the most photoactive crystallographic form. The highest performances of supported photocatalyst on OG degradation were found using an optimum amount of TiO2-Pal around 0.8 g·L−1, which corresponds properly to ca. 0.4 g·L−1 of TiO2. This amount is interestingly lower than the 2.5 g·L−1 generally reported when using pure unsupported TiO2 powder. The photodegradation rate increases by decreasing OG initial concentration, and it was found significantly higher when the OG solution is either acidic (pH<4 or basic (pH≈11. For OG concentrations in the range 5×10-6– 5×10-4 M, the kinetic law of the OG degradation in presence of TiO2-Pal is similar to that reported for unsupported TiO2 nanopowder. It follows a Langmuir-Hinshelwood model with a first-order reaction and an apparent rate constant of about 2.9×10-2 min−1.

  4. TiO2 nanoparticles in seawater: Aggregation and interactions with the green alga Dunaliella tertiolecta.

    Science.gov (United States)

    Morelli, Elisabetta; Gabellieri, Edi; Bonomini, Alessandra; Tognotti, Danika; Grassi, Giacomo; Corsi, Ilaria

    2018-02-01

    Titanium dioxide nanoparticles (TiO 2 NPs) have been widely employed in industrial applications, thus rising concern about their impact in the aquatic environment. In this study we investigated the chemical behaviour of TiO 2 NPs in the culture medium and its effect on the green alga Dunaliella tertiolecta, in terms of growth inhibition, oxidative stress, ROS (Reactive Oxygen Species) accumulation and chlorophyll content. In addition, the influence of exopolymeric substances (EPS) excreted by the microalgae on the stability of NPs has been evaluated. The physicochemical characterization showed a high propensity of TiO 2 NPs to form micrometric-sized aggregates within 30min, large enough to partially settle to the bottom of the test vessel. Indeed, an increasing amount of TiO 2 particles settled out with time, but the presence of EPS seemed to mitigate this behaviour in the first 6h of exposure where the main effects in D. tertiolecta were observed. TiO 2 NPs did not inhibit the 72-h growth rate of D. tertiolecta, nor affected the cellular chlorophyll concentration in the range 0.01-10mgL -1 . The time-course of ROS production showed an initial transient increase of ROS in TiO 2 NP-exposed algae compared to the control, concomitant with an enhancement of catalase activity. Interestingly, intracellular ROS was a small fraction of total ROS, the highest amount being extracellular. The occurrence of cell-mediated chemical transformations of TiO 2 NPs in the external medium, related to the presence of EPS, has been evaluated. Our results showed that carbohydrates were the major component of EPS, whereas proteins of medium molecular weight (20-80kDa) were preferentially bound to TiO 2 NPs, likely influencing their biological fate. Copyright © 2017 Elsevier Inc. All rights reserved.

  5. Characterization and improved solar light activity of vanadium doped TiO2/diatomite hybrid catalysts.

    Science.gov (United States)

    Wang, Bin; Zhang, Guangxin; Leng, Xue; Sun, Zhiming; Zheng, Shuilin

    2015-03-21

    V-doped TiO2/diatomite composite photocatalysts with different vanadium concentrations were synthesized by a modified sol-gel method. The diatomite was responsible for the well dispersion of TiO2 nanoparticles on the matrix and consequently inhibited the agglomeration. V-TiO2/diatomite hybrids showed red shift in TiO2 absorption edge with enhanced absorption intensity. Most importantly, the dopant energy levels were formed in the TiO2 bandgap due to V(4+) ions substituted to Ti(4+) sites. The 0.5% V-TiO2/diatomite photocatalyst displayed narrower bandgap (2.95 eV) compared to undoped sample (3.13 eV) and other doped samples (3.05 eV) with higher doping concentration. The photocatalytic activities of V doped TiO2/diatomite samples for the degradation of Rhodamine B under stimulated solar light illumination were significantly improved compared with the undoped sample. In our case, V(4+) ions incorporated in TiO2 lattice were responsible for increased visible-light absorption and electron transfer to oxygen molecules adsorbed on the surface of TiO2 to produce superoxide radicals ˙O2(-), while V(5+) species presented on the surface of TiO2 particles in the form of V2O5 contributed to e(-)-h(+) separation. In addition, due to the combination of diatomite as support, this hybrid photocatalyst could be separated from solution quickly by natural settlement and exhibited good reusability. Copyright © 2014 Elsevier B.V. All rights reserved.

  6. Microglial cells (BV-2) internalize titanium dioxide (TiO2) nanoparticles: toxicity and cellular responses.

    Science.gov (United States)

    Rihane, Naima; Nury, Thomas; M'rad, Imen; El Mir, Lassaad; Sakly, Mohsen; Amara, Salem; Lizard, Gérard

    2016-05-01

    Because of their whitening and photocatalytic effects, titanium dioxide nanoparticles (TiO2-NPs) are widely used in daily life. These NPs can be found in paints, plastics, papers, sunscreens, foods, medicines (pills), toothpastes, and cosmetics. However, the biological effect of TiO2-NPs on the human body, especially on the central nervous system, is still unclear. Many studies have demonstrated that the brain is one of the target organs in acute or chronic TiO2-NPs toxicity. The present study aimed to investigate the effect of TiO2-NPs at different concentrations (0.1 to 200 μg/mL) on murine microglial cells (BV-2) to assess their activity on cell growth and viability, as well as their neurotoxicity. Different parameters were measured: cell viability, cell proliferation and DNA content (SubG1 peak), mitochondrial depolarization, overproduction of reactive oxygen species (especially superoxide anions), and ultrastructural changes. Results showed that TiO2-NPs induced some cytotoxic effects with a slight inhibition of cell growth. Thus, at high concentrations, TiO2-NPs were not only able to inhibit cell adhesion but also enhanced cytoplasmic membrane permeability to propidium iodide associated with a loss of mitochondrial transmembrane potential and an overproduction of superoxide anions. No induction of apoptosis based on the presence of a SubG1 peak was detected. The microscopic observations also indicated that small groups of nanosized particles and micron-sized aggregates were engulfed by the BV-2 cells and sequestered as intracytoplasmic aggregates after 24-h exposure to TiO2-NPs. Altogether, our data show that the accumulation TiO2-NPs in microglial BV-2 cells favors mitochondrial dysfunctions and oxidative stress.

  7. Sub-Picosecond Injection of Electrons from Excited {Ru (2,2'-bipy-4,4'-dicarboxy)2(SCN)2} into TiO2 Using Transient Mid-Infrared Spectroscopy

    International Nuclear Information System (INIS)

    Nozik, A.J.; Ghosh, H.N.; Asbury, J.B.; Sprague, J.R.; Ellingson, R.J.; Ferrere, S.; Lian, T.

    1999-01-01

    We have used femtosecond pump-probe spectroscopy to time resolve the injection of electrons into nanocrystalline TiO2 film electrodes under ambient conditions following photoexcitation of the adsorbed dye, [Ru(4,4'-dicarboxy-2,2'-bipyridine)2(NCS)2] (N3). Pumping at one of the metal-to-ligand charge transfer adsorption peaks and probing the absorption of electrons injected into the TiO2 conduction band at 1.52 m and in the range of 4.1 to 7.0 m, we have directly observed the arrival of the injected electrons. Our measurements indicate an instrument-limited 50-fs upper limit on the electron injection time under ambient conditions in air. We have compared the infrared transient absorption for non-injecting (blank) systems consisting of N3 in ethanol and N3 adsorbed to films of nanocrystalline Al2O3 and ZrO2, and found no indication of electron injection at probe wavelengths in the mid-IR (4.1 to 7.0 m). At 1.52 m interferences exist in the observed transient adsorption signal for the blanks

  8. Wet-Chemical Preparation of TiO2-Based Composites with Different Morphologies and Photocatalytic Properties

    Directory of Open Access Journals (Sweden)

    Liqin Xiang

    2017-10-01

    Full Text Available TiO2-based composites have been paid significant attention in the photocatalysis field. The size, crystallinity and nanomorphology of TiO2 materials have an important effect on the photocatalytic efficiency. The synthesis and photocatalytic activity of TiO2-based materials have been widely investigated in past decades. Based on our group’s research works on TiO2 materials, this review introduces several methods for the fabrication of TiO2, rare-earth-doped TiO2 and noble-metal-decorated TiO2 particles with different morphologies. We focused on the preparation and the formation mechanism of TiO2-based materials with unique structures including spheres, hollow spheres, porous spheres, hollow porous spheres and urchin-like spheres. The photocatalytical activity of urchin-like TiO2, noble metal nanoparticle-decorated 3D (three-dimensional urchin-like TiO2 and bimetallic core/shell nanoparticle-decorated urchin-like hierarchical TiO2 are briefly discussed.

  9. Effect of dissolved ozone or ferric ions on photodegradation of thiacloprid in presence of different TiO2 catalysts

    International Nuclear Information System (INIS)

    Cernigoj, Urh; Stangar, Urska Lavrencic; Jirkovsky, Jaromir

    2010-01-01

    Combining TiO 2 photocatalysis with inorganic oxidants (such as O 3 and H 2 O 2 ) or transition metal ions (Fe 3+ , Cu 2+ and Ag + ) often leads to a synergic effect. Electron transfer between TiO 2 and the oxidant is usually involved. Accordingly, the degree of synergy could be influenced by TiO 2 surface area. With this in mind, the disappearance of thiacloprid, a neonicotinoid insecticide, was studied applying various photochemical AOPs and different TiO 2 photocatalysts. In photocatalytic ozonation experiments, synergic effect of three different TiO 2 photocatalysts was quantified. Higher surface area resulted in a more pronounced synergic effect but an increasing amount of TiO 2 did not influence the degree of the synergy. This supports the theory that the synergy is a consequence of adsorption of ozone on the TiO 2 surface. No synergy was observed in photocatalytic degradation of thiacloprid in the presence of dissolved iron(III) species performed under varied experimental conditions (concentration, age of iron(III) solution, different TiO 2 films, usage of TiO 2 slurries). This goes against the literature for different organic compounds (i.e., monuron). It indicates different roles of iron(III) in the photodegradation of different organic molecules. Moreover, TiO 2 surface area did not affect photodegradation efficiency in iron(III)-based experiments which could confirm absence of electron transfer between TiO 2 photocatalyst and iron(III).

  10. The Photocatalytic Activity and Compact Layer Characteristics of TiO2 Films Prepared Using Radio Frequency Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    H. C. Chang

    2014-01-01

    Full Text Available TiO2 compact layers are used in dye-sensitized solar cells (DSSCs to prevent charge recombination between the electrolyte and the transparent conductive substrate (indium tin oxide, ITO; fluorine-doped tin oxide, FTO. Thin TiO2 compact layers are deposited onto ITO/glass by means of radio frequency (rf magnetron sputtering, using deposition parameters that ensure greater photocatalytic activity and increased DSSC conversion efficiency. The photoinduced decomposition of methylene blue (MB and the photoinduced hydrophilicity of the TiO2 thin films are also investigated. The photocatalytic performance characteristics for the deposition of TiO2 films are improved by using the Grey-Taguchi method. The average transmittance in the visible region exceeds 85% for all samples. The XRD patterns of the TiO2 films, for sol-gel with spin coating of porous TiO2/TiO2 compact/ITO/glass, show a good crystalline structure. In contrast, without the TiO2 compact layer (only porous TiO2, the peak intensity of the anatase (101 plane in the XRD patterns for the TiO2 film has a lower value, which demonstrates inferior crystalline quality. With a TiO2 compact layer to prevent charge recombination, a higher short-circuit current density is obtained. The DSSC with the FTO/glass and Pt counter electrode demonstrates the energy conversion efficiency increased.

  11. Photocatalytic Study of New Immobilized TiO2 Technique Towards Degradation of Reactive Red 4 Dye

    Directory of Open Access Journals (Sweden)

    Ain S. K.

    2016-01-01

    Full Text Available The study on TiO2 for wastewater remediation has gained interest among researchers. However, the application of this photocatalyst is limited due to non-recyclability of conventional TiO2. Thus, immobilization technique has been developed to solve this issue. Hence, a comparison study between two types of immobilized photocatalysts namely titanium dioxide (TiO2 and TiO2 mixed with polyvinyl alcohol (PVA has been conducted in this work to observe the significant effect of PVA polymer in photocatalysis reaction of reactive red 4 (RR4 dye. Double sided adhesive tape (DSAT was used as thin layer binder in this immobilization system. The result shows that the photocatalytic performance of TiO2-PVA/DSAT was higher than that of TiO2/DSAT under both normal UV and visible light irradiations due to the conjugated unsaturated polymer from PVA serve as electron donor for TiO2 thus increase the photocatalysis process. Besides, TiO2-PVA/DSAT was also found to possess much better adhesion strength to the support material compared to TiO2/DSAT. Based on the findings, this TiO2 immobilization system is expected to be beneficial in the industrial wastewater treatment. Thus, further study to improve the photocatalytic activity of this immobilized TiO2 will be in our future work.

  12. TiO2 thin-films on polymer substrates and their photocatalytic activity

    International Nuclear Information System (INIS)

    Yang, Jae-Hun; Han, Yang-Su; Choy, Jin-Ho

    2006-01-01

    We have developed dip-coating process for TiO 2 -thin film on polymer substrates (acrylonitrile-butadiene-styrene polymer: ABS, polystyrene: PS). At first, a monodispersed and transparent TiO 2 nano-sol solution was prepared by the controlled hydrolysis of titanium iso-propoxide in the presence of acetylacetone and nitric acid catalyst at 80 deg. C. Powder X-ray diffraction patterns of the dried particles are indicative of crystalline TiO 2 with anatase-type structure. According to the XRD and transmission electron microscopy (TEM) studies, the mean particle size was estimated to be ca. 5 nm. The transparent thin films on ABS and PS substrates were fabricated by dip-coating process by changing the processing variables, such as the number of dip-coating and TiO 2 concentration in nano-sol solution. Scanning electron microscopic (SEM) analysis for the thin film samples reveals that the acetylacetone-modified TiO 2 nano-sol particles are effective for enhancing the interfacial adherence between films and polymeric substrates compared to the unmodified one. Photocatalytic degradation of methylene blue (MB) on the TiO 2 thin-films has also been systematically investigated

  13. Photoetching of Immobilized TiO2-ENR50-PVC Composite for Improved Photocatalytic Activity

    Directory of Open Access Journals (Sweden)

    M. A. Nawi

    2012-01-01

    Full Text Available Commercially acquired TiO2 photocatalyst (99% anatase powder was mixed with epoxidized natural rubber-50 (ENR50/polyvinyl chloride (PVC blend by ultrasonication and immobilized onto glass plates as TiO2-ENR50-PVC composite via a dip-coating method. Photoetching of the immobilized TiO2-ENR50-PVC composite was investigated under the irradiation of a 45 W compact fluorescent lamp and characterized by chemical oxygen demand (COD analysis, scanning electron microscopy-energy dispersive X-ray (SEM-EDX spectrometry, thermogravimetry analysis (TGA, and fourier transform infrared (FTIR spectroscopy. The BET surface area of the photoetched TiO2 composite was observed to be larger than the original TiO2 powder due to the systematic removal of ENR50 while PVC was retained within the composite. It also exhibited better photocatalytic efficiency than the TiO2 powder in a slurry mode and was highly reproducible and reusable. More than 98% of MB removal was consistently achieved for 10 repeated runs of the photo-etched photocatalyst system. About 93% of the 20 mg L−1 MB was mineralized over a period of 480 min. The presence of SO42−, NO3−, and Cl− anions was detected in the mineralized solution where the solution pH was reduced from 7 to 4.

  14. The Effects of Doping Copper and Mesoporous Structure on Photocatalytic Properties of TiO2

    Directory of Open Access Journals (Sweden)

    Yang Wang

    2014-01-01

    Full Text Available This paper describes a system for the synthesis of Cu-doped mesoporous TiO2 nanoparticles by a hydrothermal method at relatively low temperatures. The technique used is to dope the as-prepared mesoporous TiO2 system with copper. In this method, the copper species with the form of Cu1+, which was attributed to the reduction effect of dehydroxylation and evidenced by X-ray photoelectron spectroscopy (XPS and X-ray diffraction (XRD, was well dispersed in the optimal concentration 1 wt.% Cu-doped mesoporous TiO2. In this as-prepared mesoporous TiO2 system, original particles with a size of approximately 20 nm are aggregated together to shapes of approximately 1100 nm, which resulted in the porous aggregate structure. More importantly, the enhancement of the photocatalytic activity was discussed as effects due to the formation of stable Cu(I and the mesoporous structure in the Cu-doped mesoporous TiO2. Among them, Cu-doped mesoporous TiO2 shows the highest degradation rate of methyl orange (MO. In addition, the effects of initial solution pH on degradation of MO had also been investigated. As a result, the optimum values of initial solution pH were found to be 3.

  15. Effect of Graphite Doped TiO_2 Nanoparticles on Smoke Degradation

    International Nuclear Information System (INIS)

    Roshasnorlyza Hazan; Mohamad Shahrizal Md Zain; Natrah Syafiqah Rosli

    2016-01-01

    Secondhand smoke affects in the same way as regular smoker. The best solution is to purify the air efficiently and effectively. In this study, we were successfully doped TiO_2 nanoparticle with graphite to accelerate the degradation of cigarette smoke. The graphite doped and undoped TiO_2 nanoparticles were prepared from synthetic rutile using alkaline fusion method and their photo catalytic activity were investigated under visible light irradiation. The photo catalytic activity of the TiO_2 nanoparticles was analyzed in terms of their particle size analysis, crystallization and optical band gap. TiO_2 nanoparticle act as photo catalyzer by utilization of light energy to excite electron-hole pairs in smoke degradation processes. With the aided from graphite in TiO_2 nanoparticles, the smoke degradation was accelerate up to 44.4 %. In this case, graphite helps to reduce optical band gap of TiO_2 nanoparticle, thus increasing excitation of electron from valence band to conduction band. (author)

  16. Enhanced oxidation of naphthalene using plasma activation of TiO2/diatomite catalyst.

    Science.gov (United States)

    Wu, Zuliang; Zhu, Zhoubin; Hao, Xiaodong; Zhou, Weili; Han, Jingyi; Tang, Xiujuan; Yao, Shuiliang; Zhang, Xuming

    2018-04-05

    Non-thermal plasma technology has great potential in reducing polycyclic aromatic hydrocarbons (PAHs) emission. But in plasma-alone process, various undesired by-products are produced, which causes secondary pollutions. Here, a dielectric barrier discharge (DBD) reactor has been developed for the oxidation of naphthalene over a TiO 2 /diatomite catalyst at low temperature. In comparison to plasma-alone process, the combination of plasma and TiO 2 /diatomite catalyst significantly enhanced naphthalene conversion (up to 40%) and CO x selectivity (up to 92%), and substantially reduced the formation of aerosol (up to 90%) and secondary volatile organic compounds (up to near 100%). The mechanistic study suggested that the presence of the TiO 2 /diatomite catalyst intensified the electron energy in the DBD. Meantime, the energized electrons generated in the discharge activated TiO 2 , while the presence of ozone enhanced the activity of the TiO 2 /diatomite catalyst. This plasma-catalyst interaction led to the synergetic effect resulting from the combination of plasma and TiO 2 /diatomite catalyst, consequently enhanced the oxidation of naphthalene. Importantly, we have demonstrated the effectiveness of plasma to activate the photocatalyst for the deep oxidation of PAH without external heating, which is potentially valuable in the development of cost-effective gas cleaning process for the removal of PAHs in vehicle applications during cold start conditions. Copyright © 2017 Elsevier B.V. All rights reserved.

  17. Enhancement of tributyltin degradation under natural light by N-doped TiO2 photocatalyst

    International Nuclear Information System (INIS)

    Bangkedphol, S.; Keenan, H.E.; Davidson, C.M.; Sakultantimetha, A.; Sirisaksoontorn, W.; Songsasen, A.

    2010-01-01

    Photo-degradation of tributyltin (TBT) has been enhanced by TiO 2 nanoparticles doped with nitrogen (N-doped TiO 2 ). The N-doped catalyst was prepared by a sol-gel reaction of titanium (IV) tetraisopropoxide with 25% ammonia solution and calcined at various temperatures from 300 to 600 deg. C. X-ray diffraction results showed that N-doped TiO 2 remained amorphous at 300 deg. C. At 400 deg. C the anatase phase occurred then transformed to the rutile phase at 600 deg. C. The crystallite size calculated from Scherrer's equation was in the range of 16-51 nm which depended on the calcination temperature. N-doped TiO 2 calcined at 400 deg. C which contained 0.054% nitrogen, demonstrated the highest photocatalytic degradation of TBT at 28% in 3 h under natural light when compared with undoped TiO 2 and commercial photocatalyst, P25-TiO 2 which gave 14.8 and 18% conversion, respectively.

  18. Surface Plasmon Enhanced Photocatalysis of Au/Pt-decorated TiO2 Nanopillar Arrays

    Science.gov (United States)

    Shuang, Shuang; Lv, Ruitao; Xie, Zheng; Zhang, Zhengjun

    2016-05-01

    The low quantum yields and lack of visible light utilization hinder the practical application of TiO2 in high-performance photocatalysis. Herein, we present a design of TiO2 nanopillar arrays (NPAs) decorated with both Au and Pt nanoparticles (NPs) directly synthesized through successive ion layer adsorption and reaction (SILAR) at room temperature. Au/Pt NPs with sizes of ~4 nm are well-dispersed on the TiO2 NPAs as evidenced by electron microscopic analyses. The present design of Au/Pt co-decoration on the TiO2 NPAs shows much higher visible and ultraviolet (UV) light absorption response, which leads to remarkably enhanced photocatalytic activities on both the dye degradation and photoelectrochemical (PEC) performance. Its photocatalytic reaction efficiency is 21 and 13 times higher than that of pure TiO2 sample under UV-vis and visible light, respectively. This great enhancement can be attributed to the synergy of electron-sink function of Pt and surface plasmon resonance (SPR) of Au NPs, which significantly improves charge separation of photoexcited TiO2. Our studies demonstrate that through rational design of composite nanostructures one can harvest visible light through the SPR effect to enhance the photocatalytic activities initiated by UV-light, and thus realize more effectively utilization of the whole solar spectrum for energy conversion.

  19. Charge transfer in photorechargeable composite films of TiO2 and polyaniline

    Science.gov (United States)

    Nomiyama, Teruaki; Sasabe, Kenichi; Sakamoto, Kenta; Horie, Yuji

    2015-07-01

    A photorechargeable battery (PRB) is a photovoltaic device having an energy storage function in a single cell. The photoactive electrode of PRB is a bilayer film consisting of bare porous TiO2 and a TiO2-polyaniline (PANi) mixture that work as a photovoltaic current generator and an electrochemical energy storage by ion dedoping, respectively. To study the charge transfer between TiO2 and PANi, the photorechargeable quantum efficiency QE ([electron count on discharge]/[incident photon count on photocharge]) was measured by varying the thickness LS of the TiO2-PANi mixture. The quantum efficiency QEuv for UV photons had a maximum of ˜7% at LS ˜ 7 µm. The time constant τTP for the charge transfer was about 10-1 s, which was longer ten times or more than the lifetime of excited electrons within TiO2. These facts reveal that the main rate-limiting factor in the photocharging process is the charge transfer between TiO2 and PANi.

  20. Photocatalytic Degradation of Methylene Blue Using TiO2 Impregnated Diatomite

    Directory of Open Access Journals (Sweden)

    Ranfang Zuo

    2014-01-01

    Full Text Available Nano-TiO2 showed a good catalytic activity, but it is easy to agglomerate, resulting in the reduction or even complete loss of photocatalytic activity. The dispersion of TiO2 particles on porous materials was a potential solution to this problem. Diatomite has high specific surface and absorbability because of its particular shell structure. Thus, TiO2/diatomite composite, prepared by loading TiO2 on the surface of diatomite, was a good photocatalyst, through absorbing organic compounds with diatomite and degrading them with TiO2. Scanning electron microscopy (SEM, energy dispersive spectrum (EDS, X-ray diffraction (XRD, chemical analysis, and Fourier transform infrared spectrometry (FTIR indicated that TiO2 was impregnated well on the surface of diatomite. Furthermore, TiO2/diatomite was more active than nano-TiO2 for the degradation of methylene blue (MB in solution. MB at concentrations of 15 and 35 ppm can be completely degraded in 20 and 40 min, respectively.

  1. Photocatalytic decolorization of basic dye by TiO2 nanoparticle in photoreactor

    Directory of Open Access Journals (Sweden)

    Jutaporn Chanathaworn1

    2012-04-01

    Full Text Available Photocatalytic decolorization of rhodamine B (RB and malachite green (MG basic dyes in aqueous solution wasevaluated using TiO2 powder as a semiconductor photocatalyst under UV black light irradiation. A 0.5 L batch photoreactorcontaining dyeing solution was installed in a stainless steel chamber with air cooling under irradiation. The TiO2 powder wascharacterized by XRD observation and it was shown that the nanoparticles could be identified as 73 nm anatase crystals. Theeffects of operational parameters such as light intensity (0-114 W/m2, initial dye concentration (10-30 mg/L, and TiO2 powderloading (0.5-1.5 g/L on the decolorization of dye samples were examined. The photocatalytic decolorization rate depended onthe pollutant’s structure, such that the MG dye could be removed faster than the RB dye. Decolorization efficiency (% of thephotocatalytic system increased with increasing TiO2 loading and light intensity; however, it decreased with increasing initialdye concentration. A loading of 1.5 g TiO2/L, initial dye concentration of 20 mg/L, and light intensity of 114 W/m2 were foundto yield the highest removal efficiency of dye solution based on time requirement. The kinetics are of first order and dependon the TiO2 powder loading and dye structure. The research had a perfect application foreground.

  2. Phosphorus doped TiO2 as oxygen sensor with low operating temperature and sensing mechanism

    International Nuclear Information System (INIS)

    Han, Zhizhong; Wang, Jiejie; Liao, Lan; Pan, Haibo; Shen, Shuifa; Chen, Jianzhong

    2013-01-01

    Nano-scale TiO 2 powders doped with phosphorus were prepared by sol–gel method. The characterization of the materials was performed by XRD, BET, FT-IR spectroscopy, Zeta potential measurement and XPS analysis. The results indicate that the phosphorus suppresses the crystal growth and phase transformation and, at the same time, increases the surface area and enhances the sensitivity and selectivity for the P-doped TiO 2 oxygen sensors. In this system, the operating temperature is low, only 116 °C, and the response time is short. The spectra of FT-IR and XPS show that the phosphorus dopant presents as the pentavalent-oxidation state in TiO 2 , further phosphorus can connect with Ti 4+ through the bond of Ti-O-P. The positive shifts of XPS peaks indicate that electron depleted layer of P-doped TiO 2 is narrowed compared with that of pure TiO 2 , and the results of Zeta potential illuminate that the density of surface charge carrier is intensified. The adsorptive active site and Lewis acid characteristics of the surface are reinforced by phosphorus doping, where phosphorus ions act as a new active site. Thus, the sensitivity of P-doped TiO 2 is improved, and the 5 mol% P-doped sample has the optimal oxygen sensing properties.

  3. Improved hydrogen storage properties of MgH2 catalyzed with TiO2

    Science.gov (United States)

    Jangir, Mukesh; Meena, Priyanka; Jain, I. P.

    2018-05-01

    In order to improve the hydrogenation properties of the MgH2, various concentration of rutile Titanium Oxide (TiO2) (X wt%= 5, 10, 15 wt %) is added to MgH2 by ball milling and the catalytic effect of TiO2 on hydriding/dehydriding properties of MgH2 has been investigated. Result shows that the TiO2 significantly reduced onset temperature of desorption. Onset temperature as low as 190 °C were observed for the MgH2-15 wt% TiO2 sample which is 60 °C and 160 °C lower than the as-milled and as-received MgH2. Fromm the Kissinger plot the activation energy of 15 wt% TiO2 added sample is calculated to be -75.48 KJ/mol. These results indicate that the hydrogenation properties of MgH2-TiO2 have been improved compared to the as-milled and as-received MgH2. Furthermore, XRD and XPS were performed to characterize the structural evolution upon milling and dehydrogenation.

  4. Antimicrobial Activity of TiO2 Nanoparticle-Coated Film for Potential Food Packaging Applications

    Directory of Open Access Journals (Sweden)

    Siti Hajar Othman

    2014-01-01

    Full Text Available Recent uses of titanium dioxide (TiO2 have involved various applications which include the food industry. This study aims to develop TiO2 nanoparticle-coated film for potential food packaging applications due to the photocatalytic antimicrobial property of TiO2. The TiO2 nanoparticles with varying concentrations (0–0.11 g/ 100 mL organic solvent were coated on food packaging film, particularly low density polyethylene (LDPE film. The antimicrobial activity of the films was investigated by their capability to inactivate Escherichia coli (E. coli in an actual food packaging application test under various conditions, including types of light (fluorescent and ultraviolet (UV and the length of time the film was exposed to light (one–three days. The antimicrobial activity of the TiO2 nanoparticle-coated films exposed under both types of lighting was found to increase with an increase in the TiO2 nanoparticle concentration and the light exposure time. It was also found that the antimicrobial activity of the films exposed under UV light was higher than that under fluorescent light. The developed film has the potential to be used as a food packaging film that can extend the shelf life, maintain the quality, and assure the safety of food.

  5. Novel preparation and photocatalytic activity of one-dimensional TiO2 hollow structures

    International Nuclear Information System (INIS)

    Yu Huogen; Yu Jiaguo; Cheng Bei; Liu Shengwei

    2007-01-01

    Usually, templated methods include two important steps: the coating of nanocrystals on the surface of the templates and the removal of the templates. In this study, one-dimensional TiO 2 hollow structures, based on the template-directed deposition and then in situ template-sacrificial reaction (or dissolution), were prepared by a one-step template method using vanadium oxide nanobelts as the templates and TiF 4 as the precursor at 60 deg. C. The coating of TiO 2 nanoparticles on the surface of the templates was accompanied with the dissolution of vanadium oxide nanobelts by HF produced during the hydrolysis of TiF 4 in the reaction solution. It was found that the prepared one-dimensional TiO 2 hollow structures with a mesoporous wall were composed of TiO 2 nanoparticles with a diameter of 10-55 nm, resulting in a large specific surface area (77.2 m 2 g -1 ) and high pore volume (0.13 cm 3 g -1 ), and the wall thickness of the TiO 2 hollow structures could be easily controlled by adjusting the precursor concentration of TiF 4 . The photocatalytic activity experiment indicated that the prepared one-dimensional TiO 2 hollow structures, which could be readily separated from a slurry system after photocatalytic reaction, exhibited obvious photocatalytic activity for the photocatalytic degradation of methyl orange aqueous solution

  6. Adsorption performance of titanium dioxide (TiO2) coated air filters for volatile organic compounds.

    Science.gov (United States)

    Zhong, Lexuan; Lee, Chang-Seo; Haghighat, Fariborz

    2012-12-01

    The photocatalytic oxidation (PCO) technology as an alternative method for air purification has been studied for decades and a variety of PCO models indicate that the adsorption of reactants on the catalyst surface is one of the major physical and chemical processes occurring at a heterogeneous photocatalytic reaction. However, limited study explored the adsorption effect of a photocatalyst. This study carried out a systematic evaluation of adsorption performance of titanium dioxide (TiO(2)) coated fiberglass fibers (FGFs), TiO(2) coated carbon cloth fibers (CCFs), and original CCFs air filters at various relative humidity conditions for nine volatile organic compounds. TiO(2)/FGFs, TiO(2)/CCFs, and CCFs were characterized by SEM for morphology and N(2) adsorption isotherm for BET surface area and pore structure. A bench-scale adsorption test setup was constructed and adsorption tests were performed at various relative humidity conditions and four different injected concentrations for each compound. The isothermal adsorption curves at low concentration levels were obtained and they were well described by Langmuir isotherm model. It was noticed that there were significant differences between the adsorption behaviors and photocatalytic activities of TiO(2)/FGFs and TiO(2)/CCFs. It was concluded that adsorption performance is closely related to the characteristics of substrates and therefore, the development of a substrate with high adsorption ability is a promising trend for improving the performance of the UV-PCO technology. Copyright © 2012 Elsevier B.V. All rights reserved.

  7. Microwave synthesized nanostructured TiO2-activated carbon composite electrodes for supercapacitor

    International Nuclear Information System (INIS)

    Selvakumar, M.; Bhat, D. Krishna

    2012-01-01

    Highlights: ► Nanostructure TiO 2 has been prepared by a microwave assisted synthesis method. ► Microwave irradiation was varied with time duration on the formation of nanoparticles. ► TiO 2 -activate carbon show very good specific capacitance for supercapacitor. ► Electrochemical properties were studied on electroanalytical techniques. - Abstract: Electrochemical properties of a supercapacitor based on nanocomposite electrodes of activated carbon with TiO 2 nano particles synthesized by a microwave method have been determined. The TiO 2 /activated carbon nanocomposite electrode with a composition of 1:3 showed a specific capacitance 92 Fg −1 . The specific capacitance of the electrode decreased with increase in titanium dioxide content. The p/p symmetrical supercapacitor fabricated with TiO 2 /activated carbon composite electrodes showed a specific capacitance of 122 Fg −1 . The electrochemical behavior of the neat TiO 2 nanoparticles has also been studied for comparison purpose. The galvanostatic charge–discharge test of the fabricated supercapacitor showed that the device has good coulombic efficiency and cycle life. The specific capacitance of the supercapacitor was stable up to 5000 cycles at current densities of 2, 4, 6 and 7 mA cm −2 .

  8. Preparation of Nanoporous TiO2 Electrodes for Dye-Sensitized Solar Cells

    Directory of Open Access Journals (Sweden)

    Hsiue-Hsyan Wang

    2011-01-01

    Full Text Available Nano-porous TiO2 thin films have been widely used as the working electrodes in dye-sensitized solar cells (DSSCs. In this work, the phase-pure anatase TiO2 (a-TiO2 and rutile TiO2 (r-TiO2 have been prepared using hydrothermal processes. The investigation of photo-to-electron conversion efficiency of DSSCs fabricated from mixed-TiO2 with a-TiO2 and r-TiO2 ratio of 80 : 20 (A8R2 was performed and compared to that from commercial TiO2 (DP-25. The results showed higher efficiency of DSSC for A8R2 cells with same dependence of cell efficiency on the film thickness for both A8R2 and DP-25 cells. The best efficiency obtained in this work is 5.2% from A8R2 cell with TiO2 film thickness of 12.0 μm. The correlation between the TiO2 films thickness and photoelectron chemical properties of DSSCs fabricated from A8R2 and DP-25 was compared and discussed.

  9. Biocompatibility and Surface Properties of TiO2 Thin Films Deposited by DC Magnetron Sputtering

    Science.gov (United States)

    López-Huerta, Francisco; Cervantes, Blanca; González, Octavio; Hernández-Torres, Julián; García-González, Leandro; Vega, Rosario; Herrera-May, Agustín L.; Soto, Enrique

    2014-01-01

    We present the study of the biocompatibility and surface properties of titanium dioxide (TiO2) thin films deposited by direct current magnetron sputtering. These films are deposited on a quartz substrate at room temperature and annealed with different temperatures (100, 300, 500, 800 and 1100 °C). The biocompatibility of the TiO2 thin films is analyzed using primary cultures of dorsal root ganglion (DRG) of Wistar rats, whose neurons are incubated on the TiO2 thin films and on a control substrate during 18 to 24 h. These neurons are activated by electrical stimuli and its ionic currents and action potential activity recorded. Through X-ray diffraction (XRD), the surface of TiO2 thin films showed a good quality, homogeneity and roughness. The XRD results showed the anatase to rutile phase transition in TiO2 thin films at temperatures between 500 and 1100 °C. This phase had a grain size from 15 to 38 nm, which allowed a suitable structural and crystal phase stability of the TiO2 thin films for low and high temperature. The biocompatibility experiments of these films indicated that they were appropriated for culture of living neurons which displayed normal electrical behavior. PMID:28788667

  10. Ultra-fine structural characterization and bioactivity evaluation of TiO2 nanotube layers.

    Science.gov (United States)

    Jang, JaeMyung; Kwon, TaeYub; Kim, KyoHan

    2008-10-01

    For an application as biomedical materials of high performance with a good biocompatibility, the TiO2 nanotube-type oxide film on Ti substrate has been fabricated by electrochemical method, and the effects of surface characteristics of TiO2 naotube layer have been investigated. The surface morphology of TiO2 nanotube layer depends on factors such as anodizing time, current density, and electrolyte temperature. Moreover, the cell and pore size gradually were increased with the passage of anodizing time. X-ray diffraction (XRD) results indicated that the TiO2 nanotube layer formed in acidic electrolytes was mainly composed of anatase structure containing rutile. From the analysis of chemical states of TiO2 nanotube layer using X-ray photoelectron spectroscopy (XPS), Ti2p, P2p and O1s were observed in the nanotubes layer, which were penetrated from the electrolyte into the oxide layer during anodic process. The incorporated phosphate species were found mostly in the forms of HPO4-, PO4-, and PO3-. From the result of biological evaluation in simulated body fluid (SBF) the TiO2 nanotube layer was effective for bioactive property.

  11. Photoelectrolysis of water using heterostructural composite of TiO2 nanotubes and nanoparticles

    International Nuclear Information System (INIS)

    Das, Prajna P; Mohapatra, Susanta K; Misra, Mano

    2008-01-01

    Efficient photoelectrolysis of water to generate hydrogen (H 2 ) can be carried out by designing photocatalysts with good absorption as well as charge transport properties. One dimensional (1D), self-organized titania (TiO 2 ) nanotubes are known to have excellent charge transport properties and TiO 2 nanoparticles (NPs) are good for better photon absorption. This paper describes the synthesis of a composite photocatalyst combining the above two properties of TiO 2 nanocomposites with different morphologies. TiO 2 NPs (5-9 nm nanocrystals form 500-700 nm clusters) have been synthesized from TiCl 4 precursor on TiO 2 nanotubular arrays (∼80 nm diameter and ∼550 nm length) synthesized by the sonoelectrochemical anodization method. This TiO 2 nanotube-nanoparticle composite photoanode has enabled obtaining of enhanced photocurrent density (2.2 mA cm -2 ) as compared with NTs (0.9 mA cm -2 ) and NPs (0.65 mA cm -2 ) alone.

  12. Nanocomposites of TiO2/cyanoethylated cellulose with ultra high dielectric constants

    International Nuclear Information System (INIS)

    Madusanka, Nadeesh; Shivareddy, Sai G; Hiralal, Pritesh; Choi, Youngjin; Amaratunga, Gehan A J; Eddleston, Mark D; Oliver, Rachel A

    2016-01-01

    A novel dielectric nanocomposite containing a high permittivity polymer, cyanoethylated cellulose (CRS) and TiO 2 nanoparticles was successfully prepared with different weight percentages (10%, 20% and 30%) of TiO 2 . The intermolecular interactions and morphology within the polymer nanocomposites were analysed. TiO 2 /CRS nanofilms on SiO 2 /Si wafers were used to form metal–insulator–metal type capacitors. Capacitances and loss factors in the frequency range of 1 kHz–1 MHz were measured. At 1 kHz CRS-TiO 2 nanocomposites exhibited ultra high dielectric constants of 118, 176 and 207 for nanocomposites with 10%, 20% and 30% weight of TiO 2 respectively, significantly higher than reported values of pure CRS (21), TiO 2 (41) and other dielectric polymer-TiO 2 nanocomposite films. Furthermore, all three CRS-TiO 2 nanocomposites show a loss factor <0.3 at 1 kHz and low leakage current densities (10 −6 –10 −7 A cm −2 ). Leakage was studied using conductive atomic force microscopy and it was observed that the leakage is associated with TiO 2 nanoparticles embedded in the CRS polymer matrix. A new class of ultra high dielectric constant hybrids using nanoscale inorganic dielectrics dispersed in a high permittivity polymer suitable for energy management applications is reported. (paper)

  13. Construction of anatase/rutile TiO2 hollow boxes for highly efficient photocatalytic performance

    Science.gov (United States)

    Jia, Changchao; Zhang, Xiao; Yang, Ping

    2018-02-01

    Hollow TiO2 hierarchical boxes with suitable anatase and rutile ratios were designed for photocatalysis. The unique hierarchical structure was fabricated via a Topotactic synthetic method. CaTiO3 cubes were acted as the sacrificial templates to create TiO2 hollow hierarchical boxes with well-defined phase distribution. The phase composition of the hollow TiO2 hierarchical boxes is similar to that of TiO2 P25 nanoparticles (∼80% anatase, and 20% rutile). Compared with nanaoparticles, TiO2 hollow boxes with hierarchical structures exhibited an excellent performance in the photocatalytic degradation of methylene blue organic pollutant. Quantificationally, the degradation rate of the hollow boxes is higher than that of TiO2 P25 nanoparticles by a factor of 2.7. This is ascribed that hollow structure provide an opportunity for using incident light more efficiently. The surface hierarchical and well-organized porous structures are beneficial to supply more active sites and enough transport channels for reactant molecules. The boxes consist of single crystal anatase and rutile combined well with each other, which gives photon-generated carriers transfer efficiently.

  14. Sputtered PdO Decorated TiO2 Sensing Layer for a Hydrogen Gas Sensor

    Directory of Open Access Journals (Sweden)

    Jeong Hoon Lee

    2018-01-01

    Full Text Available We report a sputtered PdO decorated TiO2 sensing layer by radiofrequency (RF sputtering methods and demonstrated gas sensing performance for H2 gas. We prepared sputtered anatase TiO2 sensing films with 200 nm thickness and deposited a Pd layer on top of the TiO2 films with a thickness ranging from 3 nm to 13 nm. Using an in situ TiO2/Pd multilayer annealing process at 550°C for 1 hour, we observed that Pd turns into PdO by Auger electron spectroscopy (AES depth profile and confirmed decorated PdO on TiO2 sensing layer from scanning electron microscope (SEM and atomic-force microscope (AFM. We also observed a positive sensing signal for 3, 4.5, and 6.5 nm PdO decorated TiO2 sensor while we observed negative output signal for a 13.5 nm PdO decorated one. Using a microheater platform, we acquired fast response time as ~11 sec and sensitivity as 6 μV/ppm for 3 nm PdO under 33 mW power.

  15. Love Wave Ultraviolet Photodetector Fabricated on a TiO2/ST-Cut Quartz Structure

    Directory of Open Access Journals (Sweden)

    Walter Water

    2014-01-01

    Full Text Available A TiO2 thin film deposited on a 90° rotated 42°45′ ST-cut quartz substrate was applied to fabricate a Love wave ultraviolet photodetector. TiO2 thin films were grown by radio frequency magnetron sputtering. The crystalline structure and surface morphology of TiO2 thin films were examined using X-ray diffraction, scanning electron microscope, and atomic force microscope. The effect of TiO2 thin film thickness on the phase velocity, electromechanical coupling coefficient, temperature coefficient of frequency, and sensitivity of ultraviolet of devices was investigated. TiO2 thin film increases the electromechanical coupling coefficient but decreases the temperature coefficient of frequency for Love wave propagation on the 90° rotated 42°45′ ST-cut quartz. For Love wave ultraviolet photodetector application, the maximum insertion loss shift and phase shift are 2.81 dB and 3.55 degree at the 1.35-μm-thick TiO2 film.

  16. Eu"2"+ doped TiO_2 nano structures synthesized by HYSYCVD for thermoluminescence dosimetry

    International Nuclear Information System (INIS)

    Perez A, J. A.; Leal C, A. L.; Melendrez A, R.; Barboza F, M.

    2016-10-01

    Titania (TiO_2) has attracted interest owing his potential applications as dosimetry material given his excellent optical, electrical and thermal properties and the ability to shape his structure make TiO_2 suitable for research and dosimetry applications. In this work, a systematic study to know the magnitude of processing parameters influence on thermoluminescent properties of undoped (TiO_2) and doped (TiO_2:Eu"2"+) nano materials obtained by hybrid precursor systems chemical vapor deposition (HYSYCVD) technique is presented. Synthesis of one dimension nano structures of TiO_2:Eu"2"+ was carried out using K_2TiF_6 and EuCl_2 as dopant at 0.5, 1, 2.5 and 5 wt %. The nano structures samples were irradiated with β-ray in a doses range of 0.083-3000 Gy. All thermoluminescence (Tl) glow curves showed 3 broad Tl peaks around 373, 473 and 573 K, and a dosimetric linear behavior from 0.083 to 300 Gy. The Tl has a good reproducibility, with deviations of around 5%, making these TiO_2:Eu"2"+ nano materials suitable for dosimetric applications. (Author)

  17. Exposure to TiO2 nanoparticles increases Staphylococcusaureusinfection of HeLa cells

    Science.gov (United States)

    Xu, Yan; Wei, Ming-Tzo; Walker, Stephen. G.; Wang, Hong Zhan; Gondon, Chris; Brink, Peter; Guterman, Shoshana; Zawacki, Emma; Applebaum, Eliana; Rafailovich, Miriam; Ou-Yang, H. Daniel; Mironava, Tatsiana

    TiO2 is one of the most common nanoparticles in industry from food additives to energy generation. Even though TiO2 is also used as an anti-bacterial agent in combination with UV, we found that, in the absence of UV, exposure of HeLa cells to TiO2 nanoparticles largely increased their risk of bacterial invasion. HeLa cells cultured with low dosage rutile and anatase TiO2 nanoparticles (0.1 mg/ml) for 24 hrs prior to exposure to bacteria had 350% and 250% respectively more bacteria infected per cell. The increase was attributed to increased LDH leakage, and changes in the mechanical response of the cell membrane. On the other hand, macrophages exposed to TiO2 particles ingested 40% fewer bacteria, further increasing the risk of infection. In combination, these two factors raise serious concerns regarding the impact of exposure to TiO2 nanoparticles on the ability of organisms to resist bacterial infection.

  18. TiO2 (NanoParticles Extracted from Sugar-Coated Confectionery

    Directory of Open Access Journals (Sweden)

    Martina Lorenzetti

    2017-01-01

    Full Text Available As the debate about TiO2 food additive safety is still open, the present study focuses on the extraction and characterisation of TiO2 (nanoparticles added as a whitening agent to confectionary products, that is, chewing gum pellets. The aim was to (1 determine the colloidal properties of suspensions mutually containing TiO2 and all other chewing gum ingredients in biologically relevant media (preingestion conditions; (2 characterise the TiO2 (nanoparticles extracted from the chewing gum coating (after ingestion; and (3 verify their potential photocatalysis. The particle size distribution, in agreement with the zeta potential results, indicated that a small but significant portion of the particle population retained mean dimensions close to the nanosize range, even in conditions of moderate stability, and in presence of all other ingredients. The dispersibility was enhanced by proteins (i.e., albumin, which acted as surfactants and reduced particle size. The particle extraction methods involved conventional techniques and no harmful chemicals. The presence of TiO2 particles embedded in the sugar-based coating was confirmed, including 17–30% fraction in the nanorange (<100 nm. The decomposition of organics under UV irradiation proved the photocatalytic activity of the extracted (nanoparticles. Surprisingly, photocatalysis occurred even in presence of an amorphous SiO2 layer surrounding the TiO2 particles.

  19. Phenol degradation by TiO2 photocatalysts combined with different pulsed discharge systems.

    Science.gov (United States)

    Zhang, Yi; Lu, Jiani; Wang, Xiaoping; Xin, Qing; Cong, Yanqing; Wang, Qi; Li, Chunjuan

    2013-11-01

    Films of TiO2 nanotubes distributed over the inner surface of a discharge reactor cylinder (CTD) or adhered to a stainless steel electrode surface (PTD) in a discharge reactor were compared with a single-discharge (SD) system to investigate their efficiencies in phenol degradation. Morphology studies indicated that the TiO2 film was destroyed in the PTD system, but that there was no change in the CTD system after discharge. X-ray diffraction results revealed that the anatase phase of the original sample was preserved in the CTD system, but that an anatase-to-rutile phase transformation occurred in the PTD system after discharge. The highest efficiencies of phenol degradation and total organic carbon (TOC) mineralization were observed in the CTD system, and there was no decrease in phenol degradation efficiency upon reuse of a TiO2 film, indicating high catalysis activity and stability of the TiO2 photocatalysts in the combined treatment. TiO2 photocatalysts favored the formation of hydrogen peroxide and disfavored the formation of ozone. A greater degree of oxidation of intermediates and higher energy efficiency in phenol oxidation were observed with the TiO2-plasma systems, especially in the CTD system, compared to those with the SD system. Copyright © 2013 Elsevier Inc. All rights reserved.

  20. Influence of surface treatment on preparing nanosized TiO2 supported on carbon nanotubes

    International Nuclear Information System (INIS)

    Wang Shuo; Ji Lijun; Wu Bin; Gong Qianming; Zhu Yuefeng; Liang Ji

    2008-01-01

    In this paper, nanosize titanium dioxide (TiO 2 ) deposited on pristine and acid treated carbon nanotubes (CNTs) were prepared by a modified sol-gel method. The nanoscale materials were extensively characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD), Fourier transform infrared spectrometer (FTIR) and Raman spectra. The results indicated that about 6.8 nm TiO 2 nanoparticles were successfully deposited on acid-treated CNTs surface homogeneously and densely, which was smaller than TiO 2 coated on pristine CNTs. The surface state of CNTs was a critical factor in obtaining a homogeneous distribution of nanoscale TiO 2 particles. Acid oxidization could etch the surface of CNTs and introduce functional groups, which were beneficial to controllable homogeneous deposition. The TiO 2 coated on acid-treated CNTs was used as photocatalyst for Reactive Brilliant Red X-3B dye degradation under UV irradiation, which showed higher efficiency than that of TiO 2 coated on pristine CNTs and commercial photocatalyst P25.

  1. Production and Characterization of (004) Oriented Single Anatase TiO2 Films

    Science.gov (United States)

    Atay, Ferhunde; Akyuz, Idris; Cergel, Muge Soyleyici; Erdogan, Banu

    2018-02-01

    Highly (004) oriented anatase TiO2 films have been successfully obtained by an inexpensive ultrasonic spray pyrolysis technique at low substrate temperatures and without additional annealing. X-ray diffraction analysis, ultraviolet-visible spectroscopy and field emission scanning electron microscopy were used to analyze the structural, optical and surface properties of the films. By using the less reported TiCl4 solution, the optical band gap values falling into the visible region (between 2.70 eV and 2.92 eV) have been obtained for all films. Spectroscopic ellipsometry technique has been used to determine the dispersive refractive index and extinction coefficient of TiO2 films. Possible electrical conduction mechanisms in TiO2 films have been examined using temperature dependent conductivity measurements in the temperature range of 78-300 K. At room temperature, electrical resistivity values of TiO2 films change between 1.68 × 104 Ω cm and 5.88 × 104 Ω cm. Considering the analyzed parameters with respect to substrate temperature, this work refers to the properties of anatase TiO2 films that are strongly correlated to the growth direction, namely (004). As a result, (004) oriented anatase TiO2 films with appropriate optical band gap values are promising materials for technological applications, especially for photocatalysts.

  2. Multi-Layered TiO2 Films towards Enhancement of Escherichia coli Inactivation

    Directory of Open Access Journals (Sweden)

    Sorachon Yoriya

    2016-09-01

    Full Text Available Crystalline TiO2 has shown its great photocatalytic properties in bacterial inactivation. This work presents a design fabrication of low-cost, layered TiO2 films assembled reactors and a study of their performance for a better understanding to elucidate the photocatalytic effect on inactivation of E. coli in water. The ability to reduce the number of bacteria in water samples for the layered TiO2 composing reactors has been investigated as a function of time, while varying the parameters of light sources, initial concentration of bacteria, and ratios of TiO2 film area and volume of water. Herein, the layered TiO2 films have been fabricated on the glass plates by thermal spray coating prior to screen printing, allowing a good adhesion of the films. Surface topology and crystallographic phase of TiO2 for the screen-printed active layer have been characterized, resulting in the ratio of anatase:rutile being 80:20. Under exposure to sunlight and a given condition employed in this study, the optimized film area:water volume of 1:2.62 has shown a significant ability to reduce the E. coli cells in water samples. The ratio of surface area of photocatalytic active base to volume of water medium is believed to play a predominant role facilitating the cells inactivation. The kinetic rate of inactivation and its behavior are also described in terms of adsorption of reaction species at different contact times.

  3. Origin of visible-light sensitivity in N-doped TiO2 films

    International Nuclear Information System (INIS)

    Nakano, Yoshitaka; Morikawa, Takeshi; Ohwaki, Takeshi; Taga, Yasunori

    2007-01-01

    We report on visible-light sensitivity in N-doped TiO 2 (TiO 2 :N) films that were deposited on n + -GaN/Al 2 O 3 substrates by reactive magnetron sputtering and subsequently crystallized by annealing at 550 deg. C in flowing N 2 gas. The N-doping concentration was ∼8.8%, as determined by X-ray photoelectron spectroscopy measurements. From transmission electron microscopic observations and optical absorption measurements, yellow-colored TiO 2 :N samples showed an enhanced granular structure and strong absorption in the visible-light region. Photoelectron spectroscopy in air measurements showed a noticeable decrease in ionization energy of TiO 2 by the N doping. Deep-level optical spectroscopy measurements revealed two characteristic deep levels located at ∼1.18 and ∼2.48 eV below the conduction band. The 1.18 eV level is probably attributable to the O vacancy state and can be active as an efficient generation-recombination center. The pronounced 2.48 eV band is newly introduced by the N doping and contributes to band-gap narrowing of TiO 2 by mixing with the O 2p valence band. Therefore, this localized intraband is probably one origin of visible-light sensitivity in TiO 2 :N

  4. Hydrothermal synthesis spherical TiO2 and its photo-degradation property on salicylic acid

    International Nuclear Information System (INIS)

    Guo Wenlu; Liu Xiaolin; Huo Pengwei; Gao Xun; Wu Di; Lu Ziyang; Yan Yongsheng

    2012-01-01

    Anatase TiO 2 spheres have been prepared using hydrothermal synthesis. The prepared spheres were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM) and UV-vis diffuse reflectance spectra (UV-vis DRS). The TiO 2 consisted of well-defined spheres with size of 3-5 μm. The photocatalytic activity of spherical TiO 2 was determined by degradation of salicylic acid under visible light irradiation. It was revealed that the degradation rate of the spherical TiO 2 which was processed at 150 °C for 48 h could reach 81.758%. And the kinetics of photocatalytic degradation obeyed first-order kinetic, which the rate constant value was 0.01716 S -1 of the salicylic acid onto TiO 2 (temperature: 150, time: 48 h). The kinetics of adsorption followed the pseudo-second-order model and the rate constant was 1.2695 g mg -1 of the salicylic acid onto TiO 2 (temperature: 150, time: 48 h).

  5. Experimental measurement and modelling of reactive species generation in TiO2 nanoparticle photocatalysis.

    Science.gov (United States)

    Turolla, Andrea; Piazzoli, Andrea; Budarz, Jeffrey Farner; Wiesner, Mark R; Antonelli, Manuela

    2015-07-01

    The generation of reactive species in titanium dioxide (TiO 2 ) nanoparticle photocatalysis was assessed in a laboratory scale setup, in which P25 Aeroxide TiO 2 suspensions were photoactivated by means of UV-A radiation. Photogenerated holes and hydroxyl radicals were monitored over time by observing their selective reaction with probe compounds, iodide and terephthalic acid, respectively. TiO 2 aggregate size and structure were characterized over the reaction time. Reactive species quenching was then described by a model, accounting for radiative phenomena, TiO 2 nanoparticle aggregation and kinetic reactions. The interaction between iodide and photogenerated holes was influenced by iodide adsorption on TiO 2 surface, described by a Langmuir-Hinshelwood mechanism, whose parameters were studied as a function of TiO 2 concentration and irradiation time. Iodide oxidation was effectively simulated by modelling the reaction volume as a completely stirred two-dimensional domain, in which irradiation phenomena were described by a two-flux model and the steady state for reactive species was assumed. The kinetic parameters for iodide adsorption and oxidation were estimated and successfully validated in a different experimental setup. The same model was adapted to describe the oxidation of terephthalic acid by hydroxyl radicals. The kinetic parameters for terephthalic acid oxidation were estimated and validated, while the issues in investigating the interaction mechanisms among the involved species have been discussed. The sensitivity of operating parameters on model response was assessed and the most relevant parameters were highlighted.

  6. Formation of textured microstructure by mist deposition of TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Qin, Gang; Watanabe, Akira

    2013-01-01

    Unique and various textured TiO 2 films have been easily fabricated by mist deposition method on silicon and glass substrates with mild preparation conditions. Two kinds of TiO 2 nanoparticle with different shape, size, and crystal form were used as starting material, which resulted in a simple preparation process under low temperature and ordinary pressure. It was easy to control the thickness, morphology, and roughness of textured TiO 2 film by adjusting the mist deposition conditions such as deposition time, temperature, and the shape and size of nanoparticles. The optical properties of textured TiO 2 films before and after spin coating of Ag nanoparticles were investigated. The angular dependence of the reflectance was obviously reduced by textured TiO 2 surface and such effect was enhanced by Ag nanoparticles coating. A broad plasmon band of Ag grains was observed in the absorption spectrum of the textured Ag nanoparticle-coated TiO 2 film

  7. Optical properties of TiO2 nanotube arrays fabricated by the electrochemical anodization method

    International Nuclear Information System (INIS)

    Ly, Ngoc Tai; Nguyen, Van Chien; Dao, Thi Hoa; Hoang To, Le Hong; Pham, Duy Long; Do, Hung Manh; Vu, Dinh Lam; Le, Van Hong

    2014-01-01

    Perpendicularly self-aligned TiO 2 nanotube samples of size of 3 × 5 cm 2 were fabricated by the electrochemical anodization method using a solution containing NH 4 F. Influences of the technological conditions such as NH 4 F concentration and anodization voltage were studied. It was found that NH 4 F concentration in the solution and anodization voltage significantly affect the diameter and length of a TiO 2 nanotube. The diameter and the length of a TiO 2 nanotube were observed and estimated by using scanning electron microscopy. It has shown that the largest diameter and the longest length of about 80 nm and 20 μm, respectively, were obtained for the sample anodized in a solution containing 0.4% of NH 4 F, under a voltage of 48 V. Photoluminescence spectra excited by laser lights having wavelengths of 325 and 442 nm (having energies higher and lower than the band gap energy of TiO 2 ) was recorded at room temperature for the TiO 2 nanotube arrays. An abnormal luminescence result was observed. It is experimental evidence that the manufactured TiO 2 nanotube array is an expected material for hydrogen splitting from water by photochemical effect under sunlight as well as for the nano solar cells. (paper)

  8. TiO2-based photocatalytic disinfection of microbes in aqueous media: A review.

    Science.gov (United States)

    Laxma Reddy, P Venkata; Kavitha, Beluri; Kumar Reddy, Police Anil; Kim, Ki-Hyun

    2017-04-01

    The TiO 2 based photocatalyst has great potential for the disinfection/inactivation of harmful pathogens (such as E.coli in aqueous media) along with its well-known usefulness on various chemical pollutants. The disinfection property of TiO 2 is primarily attributed to surface generation of reactive oxygen species (ROS) as well as free metal ions formation. Furthermore, its disinfection capacity and overall performance can be significantly improved through modifications of the TiO 2 material. In this review, we provide a brief survey on the effect of various TiO 2 materials in the disinfection of a wide range of environmentally harmful microbial pathogens (e.g., bacteria, fungi, algae, and viruses) in aqueous media. The influencing factors (such as reactor design, water chemistry, and TiO 2 modifications) of such processes are discussed along with the mechanisms of such disinfection. It is believed that the combined application of disinfection and decontamination will greatly enhance the utilization of TiO 2 photocatalyst as a potential alternative to conventional methods of water purification. Copyright © 2017 Elsevier Inc. All rights reserved.

  9. Coaxial nanofibers containing TiO2 in the shell for water treatment applications

    Science.gov (United States)

    Kizildag, N.; Geltmeyer, J.; Ucar, N.; De Buysser, K.; De Clerck, K.

    2017-10-01

    In recent years, the basic electrospinning setup has undergone many modifications carried out to enhance the quality and improve the functionality of the resulting nanofibers. Being one of these modifications, coaxial electrospinning has attracted great attention. It enables to use different materials in nanofiber production and produce multi-layered and functional nanofibers in one step. In this study, TiO2 has been added to the shell layer of coaxial nanofibers to develop functional nanofibers which may be used in water treatment applications. The coaxial nanofibers containing TiO2 in the shell layer are compared to uniaxial nanofibers containing TiO2 in bulk fiber structure, regarding their morphology and photocatalytic activity. Uniform uniaxial and coaxial nanofibers with TiO2 were obtained. The average nanofiber diameter of coaxial nanofibers were higher. Coaxial nanofibers, which contained lower amount of TiO2, displayed similar performance to uniaxial nanofibers with TiO2 in terms of photocatalytic degradation ability against isoproturon.

  10. Chalcogenide Sensitized Carbon Based TiO2 Nanomaterial For Solar Driven Applications

    Science.gov (United States)

    Pathak, Pawan

    The demand for renewable energy is growing because fossils fuels are depleting at a rapid pace. Solar energy an abundant green energy resource. Utilizing this resource in a smart manner can resolve energy-crisis related issues. Sun light can be efficiently harvested using semiconductor based materials by utilizing photo-generated charges for numerous beneficial applications. The main goal of this thesis is to synthesize different nanostructures of TiO2, develop a novel method of coupling and synthesizing chalcogenide nanocrystals with TiO2 and to study the charge transportation effects of the various carbon allotropes in the chalcogenide nanocrystal sensitized TiO2 nanostructure. We have fabricated different nanostructures of TiO2 as solar energy harvesting materials. Effects of the different phases of TiO2 have also been studied. The anatase phase of TiO2 is more photoactive than the rutile phase of TiO2, and the higher dimension of the TiO2 can increase the surface area of the material which can produce higher photocurrent. Since TiO2 only absorbs in the UV range; to increase the absorbance TiO2 should be coupled to visible light absorbing materials. This dissertation presents a simple approach to synthesize and couple chalcogenide nanocrystals with TiO2 nanostructure to form a heterostructured composite. An atmospheric pressure based, single precursor, one-pot approach has been developed and tested to assemble chalcogenide nanocrystal on the TiO2 surface. Surface characterization using microscopy, X-ray diffraction, and elemental analysis indicates the formation of nanocrystals along the nanotube walls and inter-tubular spacing. Optical measurements indicate that the chalcogenide nanocrystals absorb in the visible region and demonstrate an increase in photocurrent in comparison to bare TiO2 nanostructure. The CdS synthesized TiO2 nanostructure produced the highest photocurrent as measured in the three electrode system. We have also assembled the PbS nanocrystal sensitized photoanode using the one pot method. Finally, the charge transportation effect of carbon allotropes has been studied. For this we assembled TiO2 conductive carbon chalcogenide nanocomposite system. Surface and elemental characterization using electron microscopy, EDX (energy dispersive x-ray) and x-ray diffraction pattern, provide the insights into the assembly of the nanostructure. Optical absorbance, Photo chronometry, Linear sweep voltammetry, and electrochemical impedance analysis have been used to provide opto-electronic performance of the material. We have studied the loading effect of various carbon allotropes, [fullerene (C 60), reduced graphene oxide (RGO), carbon nanotubes (CNTs), and graphene quantum dots (GQDs)], loading effect of chalcogenide, and effect of nitrogen doping on the carbon allotropes to optimize the performance of the heterostructure. This dissertation is expected to impact the materials synthesis strategies and assemble the nanostructures used in composite electrode driven applications in the area of photo electrochemistry, PV, solar-fuels, and other associated topics of energy storage and sensing.

  11. Enhanced electrochromic properties of TiO2 nanoporous film prepared based on an assistance of polyethylene glycol

    Science.gov (United States)

    Xu, Shunjian; Luo, Xiaorui; Xiao, Zonghu; Luo, Yongping; Zhong, Wei; Ou, Hui; Li, Yinshuai

    2017-01-01

    Polyethylene glycol (PEG) was employed as pore-forming agent to prepare TiO2 nanoporous film based on spin-coating a TiO2 nanoparticle mixed paste on fluorine doped tin oxide (FTO) glass. The electrochromic and optical properties of the obtained TiO2 film were investigated by cyclic voltammetry (CV), chronoamperometry (CA) and UV-Vis spectrophotometer. The results show that the PEG in the mixed paste endows the TiO2 film with well-developed porous structure and improves the uniformity of the TiO2 film, which are helpful for the rapid intercalation and extraction of lithium ions within the TiO2 film and the strengthening of the diffuse reflection of visible light in the TiO2 film. As a result, the TiO2 film derived from the mixed paste with PEG displays higher electrochemical activity and more excellent electrochromic performances compared with the TiO2 film derived from the mixed paste without PEG. The switching times of coloration/bleaching are respectively 10.16/5.65 and 12.77/6.13 s for the TiO2 films with PEG and without PEG. The maximum value of the optical contrast of the TiO2 film with PEG is 21.2% while that of the optical contrast of the TiO2 film without PEG is 14.9%. Furthermore, the TiO2 film with PEG has better stability of the colored state than the TiO2 film without PEG.

  12. Pilot-plant evaluation of TiO2 and TiO2-based hybrid photocatalysts for solar treatment of polluted water.

    Science.gov (United States)

    Andronic, Luminita; Isac, Luminita; Miralles-Cuevas, Sara; Visa, Maria; Oller, Isabel; Duta, Anca; Malato, Sixto

    2016-12-15

    Materials with photocatalytic and adsorption properties for advanced wastewater treatment targeting reuse were studied. Making use of TiO 2 as a well-known photocatalyst, Cu 2 S as a Vis-active semiconductor, and fly ash as a good adsorbent, dispersed mixtures/composites were prepared to remove pollutants from wastewater. X-ray diffraction, scanning electron microscopy, energy-dispersive X-Ray spectroscopy, atomic force microscopy, band gap energy, point of zero charge (pH pzc ) and BET porosity were used to characterize the substrates. Phenol, imidacloprid and dichloroacetic acid were used as pollutants for photocatalytic activity of the new photocatalysts. Experiments using the new dispersed powders were carried out at laboratory scale in two solar simulators and under natural solar irradiation at the Plataforma Solar de Almería, in a Compound Parabolic Collector (CPC) for a comparative analysis of pollutants removal and mineralization efficiencies, and to identify features that could facilitate photocatalyst separation and reuse. The results show that radiation intensity significantly affects the phenol degradation rate. The composite mixture of TiO 2 and fly ash is 2-3 times less active than sol-gel TiO 2 . Photodegradation kinetic data on the highly active TiO 2 are compared for pollutants elimination. Photodegradation of dichloroacetic acid was fast and complete after 90min in the CPC, while after 150min imidacloprid and phenol removal was 90% and 56% respectively. Copyright © 2016 Elsevier B.V. All rights reserved.

  13. The Influence of TiO2 Nanoparticles on LaFeO3/TiO2 Nanocomposites for Reduction of Aqueous Organic Dyes

    International Nuclear Information System (INIS)

    Afifah, N.; Saleh, R.

    2016-01-01

    A series of Lanthanum ferrite (LaFeO3) nanoparticles over titanium dioxide (TiO2) were synthesized using sol-gel method at room temperature by varying the loading of LaFeO3 on TiO2. The magnetic properties of samples were measured using vibrating sample magnetometer and photosonocatalytic activity towards the degradation of methylene blue under light (UV or visible) and ultrasound irradiation was also evaluated. The morphology and structure of the samples were characterized by field emission scanning electron microscope, energy dispersive analysis and X-ray diffraction. Furthermore the optical properties were also characterized by UV-visible diffuse reflectance. The experimental results showed that the prepared perovskites had sphere-like shape and strong visible light absorption. LaFeO3 demonstrated ferromagnetic properties and the magnetization decreased with the incorporation of TiO2 in the samples. However, the incorporation of TiO2 increased the photosonocatalytic activity and extended the photoresponding to UV light. (paper)

  14. Pilot-plant evaluation of TiO_2 and TiO_2-based hybrid photocatalysts for solar treatment of polluted water

    International Nuclear Information System (INIS)

    Andronic, Luminita; Isac, Luminita; Miralles-Cuevas, Sara; Visa, Maria; Oller, Isabel; Duta, Anca; Malato, Sixto

    2016-01-01

    Materials with photocatalytic and adsorption properties for advanced wastewater treatment targeting reuse were studied. Making use of TiO_2 as a well-known photocatalyst, Cu_2S as a Vis-active semiconductor, and fly ash as a good adsorbent, dispersed mixtures/composites were prepared to remove pollutants from wastewater. X-ray diffraction, scanning electron microscopy, energy-dispersive X-Ray spectroscopy, atomic force microscopy, band gap energy, point of zero charge (pH_p_z_c) and BET porosity were used to characterize the substrates. Phenol, imidacloprid and dichloroacetic acid were used as pollutants for photocatalytic activity of the new photocatalysts. Experiments using the new dispersed powders were carried out at laboratory scale in two solar simulators and under natural solar irradiation at the Plataforma Solar de Almería, in a Compound Parabolic Collector (CPC) for a comparative analysis of pollutants removal and mineralization efficiencies, and to identify features that could facilitate photocatalyst separation and reuse. The results show that radiation intensity significantly affects the phenol degradation rate. The composite mixture of TiO_2 and fly ash is 2-3 times less active than sol-gel TiO_2. Photodegradation kinetic data on the highly active TiO_2 are compared for pollutants elimination. Photodegradation of dichloroacetic acid was fast and complete after 90 min in the CPC, while after 150 min imidacloprid and phenol removal was 90% and 56% respectively.

  15. 1D TiO2 Nanostructures Prepared from Seeds Presenting Tailored TiO2 Crystalline Phases and Their Photocatalytic Activity for Escherichia coli in Water

    Directory of Open Access Journals (Sweden)

    Julieta Cabrera

    2018-01-01

    Full Text Available TiO2 nanotubes were synthesized by alkaline hydrothermal treatment of TiO2 nanoparticles with a controlled proportion of anatase and rutile. Tailoring of TiO2 phases was achieved by adjusting the pH and type of acid used in the hydrolysis of titanium isopropoxide (first step in the sol-gel synthesis. The anatase proportion in the precursor nanoparticles was in the 3–100% range. Tube-like nanostructures were obtained with an anatase percentage of 18 or higher while flake-like shapes were obtained when rutile was dominant in the seed. After annealing at 400°C for 2 h, a fraction of nanotubes was conserved in all the samples but, depending on the anatase/rutile ratio in the starting material, spherical and rod-shaped structures were also observed. The photocatalytic activity of 1D nanostructures was evaluated by measuring the deactivation of E. coli in stirred water in the dark and under UV-A/B irradiation. Results show that in addition to the bactericidal activity of TiO2 under UV-A illumination, under dark conditions, the decrease in bacteria viability is ascribed to mechanical stress due to stirring.

  16. Efectos de fotodegradación propiciados por recubrimientos de TiO2 y TiO2-SiO2 obtenidos por Sol-Gel

    Directory of Open Access Journals (Sweden)

    Rodriguez Paez, J. E.

    2008-10-01

    Full Text Available Photodegradation effect is widely used for water purification this contributes to preservation and protection of environment. Titanium oxide, (TiO2, is a compound that shows up this phenomenon. TiO2 is a semiconductor which may degradate pollutants through of a oxidation process. It permit the treatment of the residual water. It this work we has conformed coatings of TiO2 y TiO2-SiO2, utilized Sol-Gel method and investigated the degradation of the blue Methylene. For this, we introduced these coatings in the blue methylene solution which was illuminated with radiation of λ=365nm to activate its photocatilist properties. The structures of the coatings were characterized using Atomic Force Microscopy (AFM and X-ray Photoelectron Spectroscopy (XPS.El efecto de fotodegradación es ampliamente utilizado para la purificación del agua, acción que contribuye a la conservación y protección del medio ambiente; el óxido de titanio (TiO2 es uno de los semiconductores que pueden degradar contaminantes mediante procesos de oxidación, lo que lo hace apto para el tratamiento de aguas residuales. En este trabajo se conformaron recubrimientos de TiO2 y TiO2-SiO2, por el método Sol-Gel, y se estudio la degradación que experimentaba una solución de azul de metileno al introducirle estos recubrimientos e iluminarlos con una radiación de λ=365nm para activar su propiedad fotocatalítica. Los recubrimientos fueron caracterizados microestructuralmente utilizando Microscopía de Fuerza Atómica (MFA y Espectroscopía de Fotoelectrones de rayos X (XPS. Los resultados obtenidos de los ensayos de fotodegradación indican que los recubrimientos con una cantidad pequeña de silicio presentan un mayor efecto de fotodegradación indicando que el silicio puede generar puntos de anclaje que facilitan las reacciones de fotocatálisis. Por otro lado, la formación de centros activos, constituidos principalmente por carbono, también contribuyeron al desarrollo de estas reacciones.

  17. Nanoparticulate anatase TiO2 (TiO2 NPs) upregulates the expression of silkworm (Bombyx mori) neuropeptide receptor and promotes silkworm feeding, growth, and silking.

    Science.gov (United States)

    Ni, Min; Zhang, Hua; Li, Fan Chi; Wang, Bin Bin; Xu, Kai Zun; Shen, Wei De; Li, Bing

    2015-06-01

    Bombyx mori orphan G protein-coupled receptor, BNGR-A4, is the specific receptor of B. mori neuropeptide F (BmNPFR, neuropeptide F designated NPF). BmNPFR binds specifically and efficiently to B. mori neuropeptides BmNPF1a and BmNPF1b, which activates the ERK1/2 signaling pathway to regulate B. mori food intake and growth. Titanium dioxide nanoparticles (TiO2 NPs) can promote B. mori growth. However, whether the mechanisms of TiO2 NPs' effects are correlated with BmNPFR remains unknown. In this study, the effects of TiO2 NPs (5mg/L) feeding and BmNPFR-dsRNA injection on B. mori food intake and growth were investigated; after TiO2 NPs treatments, B. mori food intake, body weight, and cocoon shell weight were 5.82%, 4.64%, and 9.30% higher, respectively, than those of controls. The food intake, body weight, and cocoon shell weight of the BmNPFR-dsRNA injection group were reduced by 8.05%, 6.28%, and 6.98%, respectively, compared to the control. After TiO2 NPs treatment for 72h, the transcriptional levels of BmNPFR, BmNPF1a, and BmNPF1b in the midgut were 1.58, 1.43, and 1.34-folds, respectively, of those of the control, but 1.99, 2.26, and 2.19-folds, respectively, of the BmNPFR-dsRNA injection group; the phosphorylation level of MAPK was 24.03% higher than the control, while the phosphorylation level of BmNPFR-dsRNA injection group was 71.00% of control. The results indicated that TiO2 NPs affect B. mori feeding and growth through increasing the expression of BmNPFR. This study helps clarify the roles of BmNPF/BmNPFR system in TiO2 NPs' effects on B. mori feeding, growth, and development. Copyright © 2015 Elsevier Inc. All rights reserved.

  18. Photoactivity of brookite-rutile TiO(2) nanocrystalline mixtures obtained by heat treatment of hydrothermally prepared brookite

    Czech Academy of Sciences Publication Activity Database

    Štengl, Václav; Králová, Daniela

    2011-01-01

    Roč. 129, č. 3 (2011), s. 794-801 ISSN 0254-0584 R&D Projects: GA ČR GA203/08/0334 Institutional research plan: CEZ:AV0Z40320502; CEZ:AV0Z40500505 Keywords : oxides * heat treatment * titania * photocatalysis Subject RIV: CA - Inorganic Chemistry Impact factor: 2.234, year: 2011

  19. Preparation of pure TiO2 sorption material

    International Nuclear Information System (INIS)

    Špendlíková, Irena; Raindl, Jakub; Němec, Mojmír

    2013-01-01

    Among the natural or anthropogenic radionuclides of very low concentrations nowadays measured in environmental samples, the radionuclide of 236 U has been recently included. In these ultra-trace analyses, the purity of sorption materials is very important and the traditional preparation procedures have to be optimized to minimize possible contamination. In the case of the determination of natural concentration of 236 U ( 236 U/ 238 U ∼ 10 -10 - 10 -14 ), the sample treatment procedure has to be modified in order to eliminate possible contamination from anthropogenic 236 U that may result even in more than ten thousand times higher 236 U/ 238 U ratios. Many inorganic and organic materials have been proposed for the extraction of uranium. However, only several of them are suitable for the uranium sorption from the solutions of low uranium concentration, but relatively high salt content, such as fresh water, sea water etc. At the same time they have to meet other limiting parameters such as fast kinetics, chemical stability, and low costs. Among the inorganic sorption materials, titanium dioxide has been studied for years with promising results. Titanium dioxides can be prepared via the hydrolysis of titanium compounds, either inorganic salts or organic derivatives, but their properties strongly depend on the preparation conditions. In classical procedures, titanium dioxides are prepared from commercial inorganic salts, such as sulphates or chlorides, or even from industrial intermediates of the titanium white production. Typically, the resulting titanium dioxides are contaminated with uranium already from the origin. Assuming that most organic compounds do not contain uranium and that it is possible to find 'uranium free' water, titanium dioxide free of uranium contamination could be prepared by the hydrolysis of organic titanium derivatives. The aim of this study was to find a suitable way of pure titanium dioxide preparation and to optimize the preparation procedure with respect to the sorption properties of the resulting material towards uranium. Therefore, an organic compound, tetrabutylorthotitanate, was used for the preparation of a series of titanium dioxide samples. The conditions of the preparation procedure slightly varied (e.g. different washing solutions - ethanol, acetone or both) but the important steps like sample drying remain unchanged. One of the aspects which should be considered in the preparation of TiO 2 -based absorbers is the fact that the sorption properties of titanium dioxide strongly depend on the crystal structure and their capacities increase in order: rutile 2 : 1 N 2 at the temperature of 77 K. Sorption capacities for uranium were deduced from their sorption isotherms determined with fixed uranium concentration (20 mmol.L -1 ) and variable values of V/m (10 - 1400 mL.g -1 ). Based on this characterization, the most promising material has been chosen. In the future study, this material will be prepared in larger quantity using 'uranium free' water and used for the uranium concentration from environmental samples and for the consecutive determination of 236 u/ 238 U ratios using Accelerator Mass Spectrometry which will outline the contamination with anthropogenic 236 U and/or its natural abundance. (author)

  20. The design, fabrication, and photocatalytic utility of nanostructured semiconductors: focus on TiO2-based nanostructures

    Directory of Open Access Journals (Sweden)

    Arghya Narayan Banerjee

    2011-02-01

    Full Text Available Arghya Narayan BanerjeeSchool of Mechanical Engineering, Yeungnam University, Gyeongsan, South KoreaAbstract: Recent advances in basic fabrication techniques of TiO2-based nanomaterials such as nanoparticles, nanowires, nanoplatelets, and both physical- and solution-based techniques have been adopted by various research groups around the world. Our research focus has been mainly on various deposition parameters used for fabricating nanostructured materials, including TiO2-organic/inorganic nanocomposite materials. Technically, TiO2 shows relatively high reactivity under ultraviolet light, the energy of which exceeds the band gap of TiO2. The development of photocatalysts exhibiting high reactivity under visible light allows the main part of the solar spectrum to be used. Visible light-activated TiO2 could be prepared by doping or sensitizing. As far as doping of TiO2 is concerned, in obtaining tailored material with improved properties, metal and nonmetal doping has been performed in the context of improved photoactivity. Nonmetal doping seems to be more promising than metal doping. TiO2 represents an effective photocatalyst for water and air purification and for self-cleaning surfaces. Additionally, it can be used as an antibacterial agent because of its strong oxidation activity and superhydrophilicity. Therefore, applications of TiO2 in terms of photocatalytic activities are discussed here. The basic mechanisms of the photoactivities of TiO2 and nanostructures are considered alongside band structure engineering and surface modification in nanostructured TiO2 in the context of doping. The article reviews the basic structural, optical, and electrical properties of TiO2, followed by detailed fabrication techniques of 0-, 1-, and quasi-2-dimensional TiO2 nanomaterials. Applications and future directions of nanostructured TiO2 are considered in the context of various photoinduced phenomena such as hydrogen production, electricity generation via dye-sensitized solar cells, photokilling and self-cleaning effect, photo-oxidation of organic pollutant, wastewater management, and organic synthesis.Keywords: TiO2 nanostructure, fabrication techniques, doping in TiO2, TiO2-assisted photoactivity, solar hydrogen, TiO2-based dye-sensitized solar cells, TiO2 self-cleaning, organic synthesis

  1. Optimization of the Photoanode of CdS Quantum Dot-Sensitized Solar Cells Using Light-Scattering TiO2 Hollow Spheres

    Science.gov (United States)

    Marandi, Maziar; Rahmani, Elham; Ahangarani Farahani, Farzaneh

    2017-12-01

    about 55% compared with a similar QDSC with ZnS-free bilayer photoanode. The final improvement was carried out by applying methanol-based Cd precursor solution in the SILAR deposition process. The best photoanodes from the previous stages were selected and used in this sensitizing process. Besides, nanocrystalline TiO2 sublayers with different thicknesses were applied for further optimization. The results revealed that maximum power conversion efficiency of 3.7% was achieved as a result of such improvement, for a QDSC with optimized double-layer photoanode including TiO2 HSs and NCs and ZnS blocking layer.

  2. Recovery of hexavalent chromium from water using photoactive TiO2-montmorillonite under sunlight

    Directory of Open Access Journals (Sweden)

    Ridha Djellabi

    2016-04-01

    Full Text Available Hexavalent chromium was removed from water under sunlight using a synthesized TiO2-montmorillonite (TiO2-M employing tartaric acid as a hole scavenger. Cr(VI species was then reduced to Cr(III species by electrons arising from TiO2 particles. After that, the produced Cr(III species  was transferred to montmorillonite  due to electrostatic attractions leading to  set free TiO2 particles for a further Cr(VI species reduction. Furthermore, produced Cr(III, after Cr(VI reduction, does not  penetrate into the solution. The results indicate that no dark adsorption of Cr(VI species on TiO2-M is present, however, the reduction of Cr(VI species under sunlight increased strongly as a function of tartaric acid concentration up to 60 ppm, for which the extent of reduction is maximum within 3 h. On the other hand, the reduction extent of Cr(VI species is maximum with an initial concentration of Cr(VI species lower than 30 ppm by the use of 0.2 g/L of TiO2-M. Nevertheless, the increase of the Cr(VI initial concentration led to increase the amount of Cr(VI species reduced (capacity of reduction until a Cr(VI concentration of 75 and 100 ppm, for which  it remained constant at around 221 mg/g. For comparison, the increase of Cr(VI species concentration in the case of the commercial TiO2 P25 under the same conditions exhibited its deactivation when the reduced amount decreased from 198.1 to 157.6 mg/g as the concentration increased from 75 to 100 ppm.

  3. Protein profiling as early detection biomarkers for TiO2 nanoparticle toxicity in Daphnia magna.

    Science.gov (United States)

    Sá-Pereira, Paula; Diniz, Mário S; Moita, Liliana; Pinheiro, Teresa; Mendonça, Elsa; Paixão, Susana M; Picado, Ana

    2018-05-01

    The mode of action for nanoparticle (NP) toxicity in aquatic organisms is not yet fully understood. In this work, a strategy other than toxicity testing was applied to Daphnia magna exposed to TiO 2 -NPs: the use of nuclear microscopy and the assessment of protein profile. D. magna is a keystone species broadly used as a model system in ecotoxicology. Titanium (Ti) was found in the D. magna digestive tract, mainly in the gut. The penetration of Ti into the epithelial region was greater at higher exposure levels and also observed in eggs in the brood pouch. The protein profile of individuals exposed to different concentrations showed that 2.8 and 5.6 mg/L TiO 2 -NP concentrations induced an over-expression of the majority of proteins, in particular proteins with molecular weight of ∼120, 85 and 15 kDa, while 11.2 mg/L TiO 2 -NP had an inhibitory effect on protein expression. The Matrix-assisted laser desorption ionization with tandem time of flight mass spectrometry (MALDI-TOF/TOF MS) analysis of these proteins consistently identified them as vitellogenin (Vtg)-like proteins, associated with enzymes involved in redox balance. These results indicate that Vtg-like proteins are up-regulated in D. magna exposed to TiO 2 -NPs. Vitellogenesis is associated with the reproduction system, suggesting that TiO 2 -NP exposure can impair reproduction by affecting this process. The precise mode of action of TiO 2 -NPs is still unclear and the results from this study are a first attempt to identify specific proteins as potential markers of TiO 2 -NP toxicity in D. magna, providing useful information for future research.

  4. Mesoporous TiO2 Micro-Nanometer Composite Structure: Synthesis, Optoelectric Properties, and Photocatalytic Selectivity

    Directory of Open Access Journals (Sweden)

    Kun Liu

    2012-01-01

    Full Text Available Mesoporous anatase TiO2 micro-nanometer composite structure was synthesized by solvothermal method at 180°C, followed by calcination at 400°C for 2 h. The as-prepared TiO2 was characterized by X-ray diffraction (XRD, scanning electron microscope (SEM, transmission electron microscope (TEM, and Fourier transform infrared spectrum (FT-IR. The specific surface area and pore size distribution were obtained from N2 adsorption-desorption isotherm, and the optoelectric property of the mesoporous TiO2 was studied by UV-Vis absorption spectrum and surface photovoltage spectra (SPS. The photocatalytic activity was evaluated by photodegradation of sole rhodamine B (RhB and sole phenol aqueous solutions under simulated sunlight irradiation and compared with that of Degussa P-25 (P25 under the same conditions. The photodegradation preference of this mesoporous TiO2 was also investigated for an RhB-phenol mixed solution. The results show that the TiO2 composite structure consists of microspheres (∼0.5–2 μm in diameter and irregular aggregates (several hundred nanometers with rough surfaces and the average primary particle size is 10.2 nm. The photodegradation activities of this mesoporous TiO2 on both RhB and phenol solutions are higher than those of P25. Moreover, this as-prepared TiO2 exhibits photodegradation preference on RhB in the RhB-phenol mixture solution.

  5. Chromate enhanced visible light driven TiO2 photocatalytic mechanism on Acid Orange 7 photodegradation

    International Nuclear Information System (INIS)

    Wang, Yeoung-Sheng; Shen, Jyun-Hong; Horng, Jao-Jia

    2014-01-01

    Highlights: • Photocatalysis of Cr(VI) and TiO 2 were studied by ESR analysis on DMPO-OH signals. • Mechanism of Cr(VI)-enhanced by visible light was different from that by UV. • O 2 adsorbed on TiO 2 surfaces could react with Cr(VI) to lower photoenergy needed. • Even by UV, no TiO 2 photocatalysis was observed without O 2 solution. • Visible light and Cr(VI) redox reaction could activate TiO 2 and would yield ·OH. - Abstract: When hexavalent chromium (Cr(VI)) is added to a TiO 2 photocatalytic reaction, the decolorization and mineralization efficiencies of azo dyes Acid Orange 7 (AO7) are enhanced even though the mechanism is unclear. This study used 5,5-dimethyl-L-pyrroline-N-oxide (DMPO) as the scavenger and the analysis of Electron Spin Resonance (ESR) to investigate this enhancement effect by observing the hydroxyl radical (·OH) generation of the Cr(VI)/TiO 2 system under UV and visible light (Vis) irradiation. With Cr(VI), the decolorization efficiencies were approximately 95% and 62% under UV and Vis, and those efficiencies were 25% less in the absence of Cr(VI). The phenomena of the DMPO-OH signals during the ESR analysis under Vis 405 and 550 nm irradiation were obviously the enhancement effects of Cr(VI) in aerobic conditions. In anoxic conditions, the catalytic effects of Cr(VI) could not be achieved due to the lack of a redox reaction between Cr(VI) and the adsorbed oxygen at the oxygen vacancy sites on the TiO 2 surfaces . The results suggest that by introducing the agents of redox reactions such as chromate ions, we could lower the photoenergy of TiO 2 needed and allow Vis irradiation to activate photocatalysis

  6. Quantum Dot Sensitized Solar Cells Based on TiO2/AgInS2

    Science.gov (United States)

    Pawar, Sachin A.; Jeong, Jae Pil; Patil, Dipali S.; More, Vivek M.; Lee, Rochelle S.; Shin, Jae Cheol; Choi, Won Jun

    2018-05-01

    Quantum dot heterojunctions with type-II band alignment can efficiently separate photogenerated electron-hole pairs and, hence, are useful for solar cell studies. In this study, a quantum dot sensitized solar cell (QDSSC) made of TiO2/AgInS2 is achieved to boost the photoconversion efficiency for the TiO2-based system by varying the AgInS2 layer's thickness. The TiO2 nanorods array film is prepared by using a simple hydrothermal technique. The formation of a AgInS2 QD-sensitized TiO2-nanorod photoelectrode is carried out by successive ionic layer adsorption and reaction (SILAR) technique. The effect of the QD layer on the performance of the solar cell is studied by varying the SILAR cycles of the QD coating. The synthesized electrode materials are characterized by using X-ray diffraction, X-ray photoelectron spectroscopy, field emission scanning electron microscopy, high resolution transmission electron microscopy and solar cell performances. The results indicate that the nanocrystals have effectively covered the outer surfaces of the TiO2 nanorods. The interfacial structure of quantum dots (QDs)/TiO2 is also investigated, and the growth interface is verified. A careful comparison between TiO2/AgInS2 sensitized cells reveals that the trasfer of electrons and hole proceeds efficiently, the recombination is suppressed for the optimum thickness of the QD layer and light from the entire visible spectrum is utilised. Under AM 1.5G illumination, a high photocurrent of 1.36 mAcm-2 with an improved power conversion efficiency of 0.48% is obtained. The solar cell properties of our photoanodes suggest that the TiO2 nanorod array films co-sensitized by AgInS2 nanoclusters have potential applications in solar cells.

  7. Evaluate humidity sensing properties of novel TiO2–WO3 composite material

    International Nuclear Information System (INIS)

    Lin, Wang-De; Lai, De-Sheng; Chen, Min-Hung; Wu, Ren-Jang; Chen, Fu-Chou

    2013-01-01

    Graphical abstract: TiO 2 –WO 3 (1:1) showed better humidity sensing properties than others within the range of 12–90% relative humidity (RH), the response and recovery time were about 20 s and 160 s, respectively. Compared to the previous studies, the prepared sensor exhibits higher sensitivity (S = 451) and the low hysteresis value was around 0.13% at 32% RH. - Highlights: • Novel TiO 2 –WO 3 composite material was prepared for humidity sensor. • The sensor exhibits higher sensitivity (S = 451). • Low hysteresis value was around 0.13% at 32% RH. - Abstract: A novel TiO 2 –WO 3 composite material was prepared using a different proportion of TiO 2 and WO 3 to that investigated in previous studies. The obtained mesoporous material was characterized using X-ray diffraction, Fourier transform infrared spectrometry, transmission electron microscopy, energy dispersive X-ray spectroscopy, and N 2 adsorption-desorption techniques. The humidity-sensing properties were measured using an inductance, capacitance and resistance analyzer. The results demonstrated that the TiO 2 –WO 3 sample with a ratio of 1:1 showed better humidity sensing properties. Compared to previous studies, the prepared sensor exhibited higher sensitivity (S = 451) and the lower hysteresis value was around 0.13% at 32% RH. Complex impedance analysis indicated that the enhanced humidity sensitivity was probably due to spherical Brunauer–Emmett–Teller surface area and the hetero-junction between TiO 2 –WO 3 thin films, while the impedance varied about three orders of magnitude. Our results demonstrated the potential application of TiO 2 –WO 3 composite for fabricating high performance humidity sensors

  8. Enhanced photocatalytic degradation of dyes under sunlight using biocompatible TiO2 nanoparticles

    Science.gov (United States)

    Bharati, B.; Sonkar, A. K.; Singh, N.; Dash, D.; Rath, Chandana

    2017-08-01

    As TiO2 is one of the most popular photocatalysts, we have studied here the photocatalytic degradation of the most common dyestuffs like rhodamine B (RhB), congo red (CR) and methylene blue (MB), which mainly come from the textile and photographic industries using nanoparticles of TiO2. Nanoparticles of TiO2 synthesized through a simple and cost effective sol-gel technique crystallizes in the anatase phase, showing a band gap less than that of bulk value. Particles consisting of coherently scattered domains of size 33 nm are found to be agglomerated and polycrystalline in nature. While the degradation rates of MB, CR and RhB after irradiating with a renewable source of energy, i.e. sunlight, show 100% degradation, TiO2 irradiated with UV light of 4.8 eV shows a much slower degradation rate. To use the waste water after photocatalysis, we examine further the biocompatibile nature of the TiO2 nanoparticles by platelet interaction activity, hemolysis effect and MTT assay. It is worth mentioning here that TiO2 nanoparticles are found to be highly hemocompatible, show no platelet aggregation, and the level of intracellular ROS in human platelets does not show significant change in ROS level. We conclude that TiO2 nanoparticles constitute an excellent photocatalyst and biocompatible material, and that after photocatalytic degradation of dye effluents obtained from textile industries, purified water can be used in agriculture and domestic sectors.

  9. Nuclear microscopy as a tool in TiO2 nanoparticles bioaccumulation studies in aquatic species

    Science.gov (United States)

    Pinheiro, Teresa; Moita, Liliana; Silva, Luís; Mendonça, Elsa; Picado, Ana

    2013-07-01

    Engineered Titanium nanoparticles are used for a wide range of applications from coatings, sunscreen cosmetic additives to solar cells or water treatment agents. Inevitably environmental exposure can be expected and data on the ecotoxicological evaluation of nanoparticles are still scarce. The potential effects of nanoparticles of titanium dioxide (TiO2) on two model organisms, the water flea, Daphnia magna and the duckweed Lemna minor, were examined in semichronic toxicity tests. Daphnia and Lemna were exposed to TiO2 nanoparticles (average particle size value of 28 ± 11 nm (n = 42); concentration range, 1.4-25 mg/L) by dietary route and growth in medium containing the nanoparticles of TiO2, respectively. Both morphology and microdistribution of Ti in the individuals were examined by nuclear microscopy techniques. A significant amount of TiO2 was found accumulated in Daphnia exposed to nanoparticles. Nuclear microscopy imaging revealed that Ti was localized only in the digestive tract of the Daphnia, which displayed difficulty in eliminating the nanoparticles from their body. Daphnia showed higher mortality when exposed to higher concentrations of TiO2 (>10 mg/L). The exposure to TiO2 nanoparticles above 25 mg/L caused morphological alterations in Lemna. The roots became stiff and fronds colorless. The Ti mapping of cross-sections of roots and fronds showed that Ti was mainly deposited in the epidermis of the fronds and roots, with minor internalization. In summary, exposure of aquatic organisms to TiO2 nanoparticles may alter the physiology of these organisms at individual and population levels, posing risks to aquatic ecosystems.

  10. Nuclear microscopy as a tool in TiO2 nanoparticles bioaccumulation studies in aquatic species

    International Nuclear Information System (INIS)

    Pinheiro, Teresa; Moita, Liliana; Silva, Luís; Mendonça, Elsa; Picado, Ana

    2013-01-01

    Engineered Titanium nanoparticles are used for a wide range of applications from coatings, sunscreen cosmetic additives to solar cells or water treatment agents. Inevitably environmental exposure can be expected and data on the ecotoxicological evaluation of nanoparticles are still scarce. The potential effects of nanoparticles of titanium dioxide (TiO 2 ) on two model organisms, the water flea, Daphnia magna and the duckweed Lemna minor, were examined in semichronic toxicity tests. Daphnia and Lemna were exposed to TiO 2 nanoparticles (average particle size value of 28 ± 11 nm (n = 42); concentration range, 1.4–25 mg/L) by dietary route and growth in medium containing the nanoparticles of TiO 2 , respectively. Both morphology and microdistribution of Ti in the individuals were examined by nuclear microscopy techniques. A significant amount of TiO 2 was found accumulated in Daphnia exposed to nanoparticles. Nuclear microscopy imaging revealed that Ti was localized only in the digestive tract of the Daphnia, which displayed difficulty in eliminating the nanoparticles from their body. Daphnia showed higher mortality when exposed to higher concentrations of TiO 2 (>10 mg/L). The exposure to TiO 2 nanoparticles above 25 mg/L caused morphological alterations in Lemna. The roots became stiff and fronds colorless. The Ti mapping of cross-sections of roots and fronds showed that Ti was mainly deposited in the epidermis of the fronds and roots, with minor internalization. In summary, exposure of aquatic organisms to TiO 2 nanoparticles may alter the physiology of these organisms at individual and population levels, posing risks to aquatic ecosystems

  11. Highly efficient indoor air purification using adsorption-enhanced-photocatalysis-based microporous TiO2 at short residence time.

    Science.gov (United States)

    Lv, Jinze; Zhu, Lizhong

    2013-01-01

    A short residence time is a key design parameter for the removal of organic pollutants in catalyst-based indoor air purification systems. In this study, we synthesized a series of TiO2 with different micropore volumes and studied their removal efficiency of indoor carbonyl pollutants at a short residence time. Our results indicated that the superior adsorption capability of TiO2 with micropores improved its performance in the photocatalytic degradation of cyclohexanone, while the photocatalytic removal of the pollutant successfully kept porous TiO2 from becoming saturated. When treated with 1 mg m(-3) cyclohexanone at a relatively humidity of 18%, the adsorption amount on microporous TiO2 was 5.4-7.9 times higher than that on P25. Removal efficiency via photocatalysis followed'the same order as the adsorption amount: TiO2-5 > TiO2-20 > TiO2-60 > TiO2-180 > P25. The advantage of microporous TiO2 over P25 became more pronounced when the residence time declined from 0.072 to 0.036 s. Moreover, as the concentration of cyclohexanone deceased from 1000 ppb to 500 ppb, removal efficiency by microporous TiO2 increased more rapidly than P25.

  12. Synthesis and characterization of TiO2/CdS core–shell nanorod arrays and their photoelectrochemical property

    International Nuclear Information System (INIS)

    Cao Chunlan; Hu Chenguo; Shen Weidong; Wang, Shuxia; Tian Yongshu; Wang Xue

    2012-01-01

    Highlights: ► TiO 2 /CdS core–shell nanorod arrays were fabricated by spin-SILAR method. ► The enhanced photocurrent was found in the TiO 2 /CdS core–shell nanorod arrays. ► The CdS coated on TiO 2 increases the e-h separation and enlarges light absorption range. - Abstract: TiO 2 /CdS core–shell nanorod arrays have been fabricated via a two-step method. Vertically aligned TiO 2 nanorod arrays (NRs) were synthesized by a facile hydrothermal method, and followed by depositing CdS nanoparticles on TiO 2 NRs by spin-coating successive ion layer adsorption and reaction (spin-SILAR) method. The surface morphology, structure, optical and photoelectrochemical behaviors of the core–shell NRs films are considered. The UV–vis absorption spectrum results suggested that the absorption peak of the TiO 2 /CdS core–shell NRs shifts from the ultraviolet region to the visible region in comparison to that of the pure TiO 2 NRs. The obviously enhanced photoelectrochemical (PEC) performances of the heterojunction NRs were found under illumination of the simulated sunlight in comparison with that of the TiO 2 NRs. The enhanced PEC performance and formation mechanism of TiO 2 /CdS core–shell NRs were discussed in detail.

  13. STRUKTUR MORFOLOGI, KOMPOSISI KIMIA DAN RESISTANSI LAPISAN TIO2-CU SEBAGAI LAPISAN AKTIF PADA SEL SURYA FOTOELEKTROKIMIA

    Directory of Open Access Journals (Sweden)

    Rita Prasetyowati

    2013-11-01

    Full Text Available Peningkatan efisiensi sel surya titania terus dikembangkan. Salah satunya adalah memodifikasi titania yang berfungsi sebagai lapisan aktif. Lapisan titania dapat disisipi dengan logam Cu. Penyisipan logam Cu pada TiO2 dilakukan melalui pembuatan nanokomposit TiO2-Cu dengan metode sol-gel. Lapisan TiO2-Cu yang terbentuk dikarakterisasi dengan SEM (Scanning Electron Microscopy untuk mengetahui struktur morfologi permukaan, EDX (Energy dispersive X-ray spectroscopy untuk mengetahui komposisi bahan. Sedangkan resistansi lapisan diukur menggunakan Jembatan Wheatstone. Berdasarkan hasil SEM dapat ditunjukkan bahwa struktur morfologi permukaan lapisan TiO2-Cu tidak berbeda secara signifikan dengan lapisan TiO2, yaitu cukup homogen dan memiliki ukuran butir (grain yang hampir sama. Tetapi dari hasil EDX diperoleh bahwa lapisan TiO2-Cu yaitu lapisan TiO2 yang disisipi logam tembaga mengandung  unsur Ti sebanyak 59,8%, unsur O sebanyak 40,02% dan unsur Cu sebanyak 0,19%. Sedangkan lapisan TiO2 saja mengandung unsur Ti sebanyak 54,25% dan unsur O sebanyak 45,75%. Penyisipan logam tembaga pada lapisan titania dapat menurunkan resistansi listrik lapisan. Nilai resistansi lapisan TiO2 adalah 7,714 kilo ohm. Sedangkan nilai resistansi lapisan TiO2-Cu adalah 6,624 kilo ohm.

  14. Photocatalytic Oxidation of Acetone Over High Thermally Stable TiO2 Nanosheets With Exposed (001) Facets.

    Science.gov (United States)

    Shi, Ting; Duan, Youyu; Lv, Kangle; Hu, Zhao; Li, Qin; Li, Mei; Li, Xiaofang

    2018-01-01

    Anatase TiO 2 (A-TiO 2 ) usually exhibits superior photocatalytic activity than rutile TiO 2 (R-TiO 2 ). However, the phase transformation from A-TiO 2 to R-TiO 2 will inevitably happens when the calcination temperature is up to 600°C, which hampers the practical applications of TiO 2 photocatalysis in hyperthermal situations. In this paper, high energy faceted TiO 2 nanosheets (TiO 2 -NSs) with super thermal stability was prepared by calcination of TiOF 2 cubes. With increase in the calcination temperature from 300 to 600°C, TiOF 2 transforms into TiO 2 hollow nanoboxes (TiO 2 -HNBs) assembly from TiO 2 -NSs via Ostwald Rippening process. Almost all of the TiO 2 -HNBs are disassembled into discrete TiO 2 -NSs when calcination temperature is higher than 700°C. Phase transformation from A-TiO 2 to R-TiO 2 begins at 1000°C. Only when the calcination temperature is higher than 1200°C can all the TiO 2 -NSs transforms into R-TiO 2 . The 500°C-calcined sample (T500) exhibits the highest photoreactivity toward acetone oxidation possibly because of the production of high energy TiO 2 -NSs with exposed high energy (001) facets and the surface adsorbed fluorine. Surface oxygen vacancy, due to the heat-induced removal of surface adsorbed fluoride ions, is responsible for the high thermal stability of TiO 2 -NSs which are prepared by calcination of TiOF 2 cubes.

  15. The design, fabrication, and photocatalytic utility of nanostructured semiconductors: focus on TiO2-based nanostructures

    Science.gov (United States)

    Banerjee, Arghya Narayan

    2011-01-01

    Recent advances in basic fabrication techniques of TiO2-based nanomaterials such as nanoparticles, nanowires, nanoplatelets, and both physical- and solution-based techniques have been adopted by various research groups around the world. Our research focus has been mainly on various deposition parameters used for fabricating nanostructured materials, including TiO2-organic/inorganic nanocomposite materials. Technically, TiO2 shows relatively high reactivity under ultraviolet light, the energy of which exceeds the band gap of TiO2. The development of photocatalysts exhibiting high reactivity under visible light allows the main part of the solar spectrum to be used. Visible light-activated TiO2 could be prepared by doping or sensitizing. As far as doping of TiO2 is concerned, in obtaining tailored material with improved properties, metal and nonmetal doping has been performed in the context of improved photoactivity. Nonmetal doping seems to be more promising than metal doping. TiO2 represents an effective photocatalyst for water and air purification and for self-cleaning surfaces. Additionally, it can be used as an antibacterial agent because of its strong oxidation activity and superhydrophilicity. Therefore, applications of TiO2 in terms of photocatalytic activities are discussed here. The basic mechanisms of the photoactivities of TiO2 and nanostructures are considered alongside band structure engineering and surface modification in nanostructured TiO2 in the context of doping. The article reviews the basic structural, optical, and electrical properties of TiO2, followed by detailed fabrication techniques of 0-, 1-, and quasi-2-dimensional TiO2 nanomaterials. Applications and future directions of nanostructured TiO2 are considered in the context of various photoinduced phenomena such as hydrogen production, electricity generation via dye-sensitized solar cells, photokilling and self-cleaning effect, photo-oxidation of organic pollutant, wastewater management, and organic synthesis. PMID:24198485

  16. Interaction of TiO2 nanoparticles with the marine microalga Nitzschia closterium: Growth inhibition, oxidative stress and internalization

    International Nuclear Information System (INIS)

    Xia, Bin; Chen, Bijuan; Sun, Xuemei; Qu, Keming; Ma, Feifei; Du, Meirong

    2015-01-01

    The toxicity of TiO 2 engineered nanoparticles (NPs) to the marine microalga Nitzschia closterium was investigated by examining growth inhibition, oxidative stress and uptake. The results indicated that the toxicity of TiO 2 particles to algal cells significantly increased with decreasing nominal particle size, which was evidenced by the 96 EC 50 values of 88.78, 118.80 and 179.05 mg/L for 21 nm, 60 nm and 400 nm TiO 2 particles, respectively. The growth rate was significantly inhibited when the alga was exposed to 5 mg/L TiO 2 NPs (21 nm). Measurements of antioxidant enzyme activities showed that superoxide dismutase (SOD), catalase (CAT) and peroxidase (POD) activities were first induced and subsequently inhibited following exposure to 5 mg/L TiO 2 NPs. The depletion of antioxidant enzymes with a concomitant increase in malondialdehyde (MDA) levels and reactive oxygen species (ROS) posed a hazard to membrane integrity. A combination of flow cytometry analysis, transmission electron microscopy and Ti content measurement indicated that TiO 2 NPs were internalized in N. closterium cells. The level of extracellular ROS, which was induced by TiO 2 NPs under visible light, was negligible when compared with the intracellular ROS level (accounting for less than 6.0% of the total ROS level). These findings suggest that elevated TiO 2 nanotoxicity in marine environments is related to increased ROS levels caused by internalization of TiO 2 NPs. - Highlights: • Inhibition of marine microalgae by TiO 2 NPs and bulk particles was evaluated. • Aggregation of TiO 2 NPs and bulk particles was observed in marine algal test medium. • TiO 2 NPs induced damage to algal cell membranes as detected by flow cytometry. • Increased TiO 2 nanotoxicity to algal cells was caused by internalization of NPs

  17. Correlation between photoelectrochemical behaviour and photoelectrocatalytic activity and scaling-up of P25-TiO2 electrodes

    International Nuclear Information System (INIS)

    Pablos, Cristina; Marugán, Javier; Grieken, Rafael van; Adán, Cristina; Riquelme, Ainhoa; Palma, Jesús

    2014-01-01

    The use of TiO 2 electrodes may solve the two main drawbacks of photocatalytic processes: i) the necessity of recovering the catalyst and ii) the low quantum yield in the use of the radiation. This work focuses on the correlation between the photoelectrochemical properties of TiO 2 electrodes and their activity for the photoelectrocatalytic oxidation of methanol. Particulate TiO 2 electrodes prepared by deposition of P25-TiO 2 nanoparticles on titanium (TiO 2 /Ti) or conductive glass support (TiO 2 /ITO) seem to be effective for charge carrier transference on TiO 2 surface favouring the formation of ·OH radicals and consequently, the oxidation of molecules. In contrast, thermal TiO 2 electrodes prepared by annealing of titanium (Ti) present better properties for charge carrier separation as a consequence of the application of a potential bias. Despite reducing charge carrier recombination by applying an electric potential bias, the activity of thermal electrodes remains lower than that of P25-particulate electrodes. TiO 2 structure of P25-particulate electrodes does not completely allow developing a potential gradient. However, their adequate TiO 2 layer characteristics for charge carrier transfer lead to a reduction in charge carrier recombination making up for the lack of charge carrier separation when applying an electric potential bias. TiO 2 /Ti showed the highest values of activity. Therefore, the combination of the suitable TiO 2 surface properties for charge carrier transfer with an adequate conductive support seems to increase the properties of the electrode for allowing charge carrier separation. The scaling-up calculations for a TiO 2 /ITO electrode do lead to good estimations of the activity and photocurrent of larger electrodes since this photoanode made from ITO as conductive support does not seem to be significantly affected by the applied potential bias

  18. Structural and electrical properties of TiO2/ZnO core–shell nanoparticles synthesized by hydrothermal method

    International Nuclear Information System (INIS)

    Vlazan, P.; Ursu, D.H.; Irina-Moisescu, C.; Miron, I.; Sfirloaga, P.; Rusu, E.

    2015-01-01

    TiO 2 /ZnO core–shell nanoparticles were successfully synthesized by hydrothermal method in two stages: first stage is the hydrothermal synthesis of ZnO nanoparticles and second stage the obtained ZnO nanoparticles are encapsulated in TiO 2 . The obtained ZnO, TiO 2 and TiO 2 /ZnO core–shell nanoparticles were investigated by means of X-ray diffraction, transmission electron microscopy, Brunauer, Emmett, Teller and resistance measurements. X-ray diffraction analysis revealed the presence of both, TiO 2 and ZnO phases in TiO 2 /ZnO core–shell nanoparticles. According to transmission electron microscopy images, ZnO nanoparticles have hexagonal shapes, TiO 2 nanoparticles have a spherical shape, and TiO 2 /ZnO core–shell nanoparticles present agglomerates and the shape of particles is not well defined. The activation energy of TiO 2 /ZnO core–shell nanoparticles was about 101 meV. - Graphical abstract: Display Omitted - Highlights: • TiO 2 /ZnO core–shell nanoparticles were synthesized by hydrothermal method. • TiO 2 /ZnO core–shell nanoparticles were investigated by means of XRD, TEM and BET. • Electrical properties of TiO 2 /ZnO core–shell nanoparticles were investigated. • The activation energy of TiO 2 /ZnO core–shell nanoparticles was about E a = 101 meV

  19. Vortex properties of mesoscopic superconducting samples

    Energy Technology Data Exchange (ETDEWEB)

    Cabral, Leonardo R.E. [Laboratorio de Supercondutividade e Materiais Avancados, Departamento de Fisica, Universidade Federal de Pernambuco, Recife 50670-901 (Brazil); Barba-Ortega, J. [Grupo de Fi' sica de Nuevos Materiales, Departamento de Fisica, Universidad Nacional de Colombia, Bogota (Colombia); Souza Silva, C.C. de [Laboratorio de Supercondutividade e Materiais Avancados, Departamento de Fisica, Universidade Federal de Pernambuco, Recife 50670-901 (Brazil); Albino Aguiar, J., E-mail: albino@df.ufpe.b [Laboratorio de Supercondutividade e Materiais Avancados, Departamento de Fisica, Universidade Federal de Pernambuco, Recife 50670-901 (Brazil)

    2010-10-01

    In this work we investigated theoretically the vortex properties of mesoscopic samples of different geometries, submitted to an external magnetic field. We use both London and Ginzburg-Landau theories and also solve the non-linear Time Dependent Ginzburg-Landau equations to obtain vortex configurations, equilibrium states and the spatial distribution of the superconducting electron density in a mesoscopic superconducting triangle and long prisms with square cross-section. For a mesoscopic triangle with the magnetic field applied perpendicularly to sample plane the vortex configurations were obtained by using Langevin dynamics simulations. In most of the configurations the vortices sit close to the corners, presenting twofold or three-fold symmetry. A study of different meta-stable configurations with same number of vortices is also presented. Next, by taking into account de Gennes boundary conditions via the extrapolation length, b, we study the properties of a mesoscopic superconducting square surrounded by different metallic materials and in the presence of an external magnetic field applied perpendicularly to the square surface. It is determined the b-limit for the occurrence of a single vortex in a mesoscopic square of area d{sup 2}, for 4{xi}(0){<=}d{<=}10{xi}(0).

  20. PHOTODEGRADATION OF ALIZARIN S DYE USING TiO2-ZEOLITE AND UV RADIATION

    Directory of Open Access Journals (Sweden)

    Karna Wijaya

    2010-06-01

    Full Text Available An investigation of Alizarin S photodegradation using TiO2-zeolite and UV radiation was performed. TiO2-zeolite was prepared by dispersing oligocations of titanium into suspension of zeolite. The suspension was stirred and then filtered to separate the solid phase from the filtrate. the solid phase was calcined by microwave oven at 800 Watt for 5 minutes to convert the oligocations into its oxide forms. The calcined product and unmodified zeolite were characterized using x-ray diffractometry, FT-IR spectrophotometry, X-ray fluorescence and gas sorption analysis methods to determine their physicochemical properties. Photocatalytic activity of TiO2-zeolite was tested on Alizarin S solution using following method: 50 mg of zeolite was dispersed into 25 mL of 10-4 M Alizarin S. The dispersion was irradiated using 365 nm UV light at room temperature on various irradiation times, i.e. 10, 20, 30, 40 and 60 minutes. At certain irradiation time, the dispersion was filtered and the filtrate was then analyzed its concentration using UV-Vis spectrophotometry method. Characterization results exhibited that the formation of TiO2 on internal as well as external surfaces of zeolite could not be detected  with x-ray diffractometry and FT-IR spectrophotometry, however determination of titanium using x-ray fluorescence analysis on the calcined product showed that the concentration of titanium was much higher than zeolite (0.22% on zeolite and 12.08% on TiO2-zeolite. Gas sorption analysis result indicated that the the calcination  resulted in the increase of specific surface area (16,31 m2/g on zeolite and 100.96 m2/g on TiO2-zeolite as well as total pore volume of calcined product (13.34 mL/Å/g on zeolite and 57.54 mL/Å/g on TiO2-zeolite. The result of photocatalytic activitiy study showed that ca 99 % of Alizarin S was degraded by TiO2-zeolite after UV irradiation for 60 min.   Keywords: TiO2-zeolite, photocatalytic, Alizarin S.

  1. Amorphous and crystalline TiO2 nanotube arrays for enhanced Li-ion intercalation properties.

    Science.gov (United States)

    Guan, Dongsheng; Cai, Chuan; Wang, Ying

    2011-04-01

    We have employed a simple process of anodizing Ti foils to prepare TiO2 nanotube arrays which show enhanced electrochemical properties for applications as Li-ion battery electrode materials. The lengths and pore diameters of TiO2 nanotubes can be finely tuned by varying voltage, electrolyte composition, or anodization time. The as-prepared nanotubes are amorphous and can be converted into anatase nanotubes with heat treatment at 480 degrees C. Rutile crystallites emerge in the anatase nanotube when the annealing temperature is increased to 580 degrees C, resulting in TiO2 nanotubes of mixed phases. The morphological features of nanotubes remain unchanged after annealing. Li-ion insertion performance has been studied for amorphous and crystalline TiO2 nanotube arrays. Amorphous nanotubes with a length of 3.0 microm and an outer diameter of 125 nm deliver a capacity of 91.2 microA h cm(-2) at a current density of 400 microA cm(-2), while those with a length of 25 microm and an outer diameter of 158 nm display a capacity of 533 microA h cm-2. When the 3-microm long nanotubes become crystalline, they deliver lower capacities: the anatase nanotubes and nanotubes of mixed phases show capacities of 53.8 microA h cm-2 and 63.1 microA h cm(-2), respectively at the same current density. The amorphous nanotubes show excellent capacity retention ability over 50 cycles. The cycled nanotubes show little change in morphology compared to the nanotubes before electrochemical cycling. All the TiO2 nanotubes demonstrate higher capacities than amorphous TiO2 compact layer reported in literature. The amorphous TiO2 nanotubes with a length of 1.9 microm exhibit a capacity five times higher than that of TiO2 compact layer even when the nanotube array is cycled at a current density 80 times higher than that for the compact layer. These results suggest that anodic TiO2 nanotube arrays are promising electrode materials for rechargeable Li-ion batteries.

  2. Evaluation of the content of TiO2 nanoparticles in the coatings of chewing gums.

    Science.gov (United States)

    Dudefoi, William; Terrisse, Hélène; Popa, Aurelian Florin; Gautron, Eric; Humbert, Bernard; Ropers, Marie-Hélène

    2018-02-01

    Titanium dioxide is a metal oxide used as a white pigment in many food categories, including confectionery. Due to differences in the mass fraction of nanoparticles contained in TiO 2 , the estimated intakes of TiO 2 nanoparticles differ by a factor of 10 in the literature. To resolve this problem, a better estimation of the mass of nanoparticles present in food products is needed. In this study, we focused our efforts on chewing gum, which is one of the food products contributing most to the intake of TiO 2 . The coatings of four kinds of chewing gum, where the presence of TiO 2 was confirmed by Raman spectroscopy, were extracted in aqueous phases. The extracts were analysed by transmission electron microscopy (TEM), X-ray diffraction, Fourier Transform Raman spectroscopy, and inductively coupled plasma atomic emission spectroscopy (ICP-AES) to establish their chemical composition, crystallinity and size distribution. The coatings of the four chewing gums differ chemically from each other, and more specifically the amount of TiO 2 varies from one coating to another. TiO 2 particles constitute the entire coating of some chewing gums, whereas for others, TiO 2 particles are embedded in an organic matrix and/or mixed with minerals like calcium carbonate, talc, or magnesium silicate. We found 1.1 ± 0.3 to 17.3 ± 0.9 mg TiO 2 particles per piece of chewing gum, with a mean diameter of 135 ± 42 nm. TiO 2 nanoparticles account for 19 ± 4% of all particles, which represents a mass fraction of 4.2 ± 0.1% on average. The intake of nanoparticles is thus highly dependent on the kind of chewing gum, with an estimated range extending from 0.04 ± 0.01 to 0.81 ± 0.04 mg of nano-TiO 2 per piece of chewing gum. These data should serve to refine the exposure scenario.

  3. Single-walled carbon nanotube-facilitated dispersion of particulate TiO2 on ZrO2 ceramic membrane filters.

    Science.gov (United States)

    Yao, Yuan; Li, Gonghu; Gray, Kimberly A; Lueptow, Richard M

    2008-07-15

    We report that SWCNTs substantially improve the uniformity and coverage of TiO2 coatings on porous ZrO2 ceramic membrane filters. The ZrO2 filters were dip coated with 100 nm anatase TiO2, TiO2/SWCNT composites, a TiO2+SWCNT mixture, and a TiO2/MWCNT composite at pH 3, 5, and 8. Whereas the TiO2+SWCNT mixture and the TiO2/MWCNT composite promote better coverage and less clumping than TiO2 alone, the TiO2/SWCNT composite forms a complete uniform coating without cracking at pH 5 ( approximately 100% coverage). A combination of chemical and electrostatic effects between TiO2 and SWCNTs forming the composite as well as between the composite and the ZrO2 surface explains these observations.

  4. Photocatalytic activity of TiO2/Nb2O5/PANI and TiO2/Nb2O5/RGO as new nanocomposites for degradation of organic pollutants.

    Science.gov (United States)

    Zarrin, Saviz; Heshmatpour, Felora

    2018-06-05

    In this study, highly active titanium dioxide modified by niobium oxide (Nb 2 O 5 ), polymer (PANI) and reduced graphene oxide (RGO) were successfully prepared. The morphology, structure, surface area and light absorption properties of the present nanocomposites for removal of methylene blue (MB) and methyl orange (MO) were investigated and compared with those of TiO 2 /Nb 2 O 5 and TiO 2 nanoparticles. The characterization techniques such as XRD, FT-IR, UV-vis, SEM, EDX, BET and TEM were employed in order to identify the nanocomposites. Also, photocatalytic properties of TiO 2 /Nb 2 O 5 /PANI and TiO 2 /Nb 2 O 5 /RGO nanocomposites under visible light irradiation were studied. In this way, the obtained results were compared to each other and also compared to TiO 2 /Nb 2 O 5 and TiO 2 nanoparticles. In this context, the chemical oxygen demand (COD) removal follows the photodegradation in observed performance. The results indicate that reduced TiO 2 /Nb 2 O 5 nanocomposite is effectively modified by graphene oxide to give TiO 2 /Nb 2 O 5 /RGO composite. The TiO 2 /Nb 2 O 5 /RGO exhibits significantly higher photocatalytic activity in degradation of organic dyes under visible light rather than that of TiO 2 /Nb 2 O 5 /PANI, TiO 2 /Nb 2 O 5 and pure TiO 2 . Copyright © 2018 Elsevier B.V. All rights reserved.

  5. Synthesis and Photocatalytic Activity of Mo-Doped TiO2 Nanoparticles

    Directory of Open Access Journals (Sweden)

    Ji-guo Huang

    2015-01-01

    Full Text Available The undoped and Mo-doped TiO2 nanoparticles were synthesized by sol-gel method. The as-prepared samples were characterized by X-ray diffraction (XRD, diffuse reflectance UV-visible absorption spectra (UV-vis DRS, X-ray photoelectron spectra (XPS, and transmission electron microscopy (TEM. The photocatalytic activity was evaluated by photocatalytic degradation of methylene blue under irradiation of a 500 W xenon lamp and natural solar light outdoor. Effects of calcination temperatures and Mo doping amounts on crystal phase, crystallite size, lattice distortion, and optical properties were investigated. The results showed that most of Mo6+ took the place of Ti4+ in the crystal lattice of TiO2, which inhibited the growth of crystallite size, suppressed the transformation from anatase to rutile, and led to lattice distortion of TiO2. Mo doping narrowed the band gap (from 3.05 eV of TiO2 to 2.73 eV of TiMo0.02O and efficiently increased the optical absorption in visible region. Mo doping was shown to be an efficient method for degradation of methylene blue under visible light, especially under solar light. When the calcination temperature was 550°C and the Mo doping amount was 2.0%, the Mo-doped TiO2 sample exhibited the highest photocatalytic activity.

  6. Decolorization of Methylene Blue with TiO2 Sol via UV Irradiation Photocatalytic Degradation

    Directory of Open Access Journals (Sweden)

    Jun Yao

    2010-01-01

    Full Text Available TiO2 sol was prepared for the degradation of methylene blue (MB solution under ultraviolet (UV irradiation. The absorption spectra of MB indicated that the maximum wavelength, 663 nm, almost kept the same. The performance of 92.3% for color removal was reached after 160 min. The particle size of TiO2 sol was about 22.5 nm. X-ray diffraction showed that TiO2 consisted of a single anatase phase. The small size and anatase phase probably resulted in high photocatalytic activity of TiO2 sol. The degradation ratio decreased as the initial concentration of MB increased. The photodegradation efficiency decreased in the order of pH 2>pH 9>pH 7. Regarding catalyst load, the degradation increased with the mass of catalyst up to an amount of 1.5 g⋅L−1 then decreased as the mass continued to increase. The addition of H2O2 to TiO2 sol resulted in an increase on the degradation ratio.

  7. Highly stable colloidal TiO2 nanocrystals with strong violet-blue emission

    International Nuclear Information System (INIS)

    Ghamsari, Morteza Sasani; Gaeeni, Mohammad Reza; Han, Wooje; Park, Hyung-Ho

    2016-01-01

    Improved sol–gel method has been applied to prepare highly stable colloidal TiO 2 nanocrystals. The synthesized titania nanocrystals exhibit strong emission in the violet-blue wavelength region. Very long evolution time was obtained by preventing the sol to gel conversion with reflux process. FTIR, XRD, UV–vis absorption, photoluminescence and high resolution transmission electron microscope (HRTEM) were used to study the optical properties, crystalline phase, morphology, shape and size of prepared TiO 2 colloidal nanocrystals. HRTEM showed that the diameter of TiO 2 colloidal nanocrystals is about 5 nm. Although the PL spectra show similar spectral features upon excitation wavelengths at 280, 300 and 350 nm, but their emission intensities are significantly different from each other. Photoluminescence quantum yield for TiO 2 colloidal nanocrystals is estimated to be 49% with 280 nm excitation wavelength which is in agreement and better than reported before. Obtained results confirm that the prepared colloidal TiO 2 sample has enough potential for optoelectronics applications.

  8. Fabrication of TiO2 Nanotanks Embedded in a Nanoporous Alumina Template

    Directory of Open Access Journals (Sweden)

    C. Massard

    2015-01-01

    Full Text Available The feasibility of surface nanopatterning with TiO2 nanotanks embedded in a nanoporous alumina template was investigated. Self-assembled anodized aluminium oxide (AAO template, in conjunction with sol gel process, was used to fabricate this nanocomposite object. Through hydrolysis and condensation of the titanium alkoxide, an inorganic TiO2 gel was moulded within the nanopore cavities of the alumina template. The nanocomposite object underwent two thermal treatments to stabilize and crystallize the TiO2. The morphology of the nanocomposite object was characterized by Field Emission Scanning Electron Microscopy (FESEM. The TiO2 nanotanks obtained have cylindrical shapes and are approximately 69 nm in diameter with a tank-to-tank distance of 26 nm. X-ray diffraction analyses performed by Transmission Electron Microscopy (TEM with selected area electron diffraction (SAED were used to investigate the TiO2 structure. The optical properties were studied using UV-Vis spectroscopy.

  9. Sol-Gel TiO2 thin films sensitized with the mulberry pigment cyanidin

    Directory of Open Access Journals (Sweden)

    Emerson Henrique de Faria

    2007-12-01

    Full Text Available TiO2 films have various applications, among them solar cells and photodegradation of pollutants. In this study, we investigated TiO2 films functionalized with the organic dye cyanidin extracted from black mulberry (Morus nigra. The TiO2 was functionalized by the sol-gel method and the film was deposited on glass substrates by dip-coating. Our aim was to investigate the interaction between the semiconductor and the dye, as well as the influence of the velocity and number of deposits on the characteristics of the film. Using ultraviolet-visible spectroscopy, we observed a shift from the maximum absorption band at 545 nm for the dye’s ethanol solution to 595 nm for the film, indicating interaction of the cyanidin with the TiO2. The absorption spectra in the infrared region of the functionalized TiO2 particles showed bands characteristic of the oxide and indicated their interaction with the dye. Using profilometry and m-line techniques, we found that the films presented thicknesses in the order of 100 nm. A SEM analysis confirmed the high density of the films.

  10. Enhanced Photocatalytic Activity of TiO2 Nanoparticles Supported on Electrically Polarized Hydroxyapatite.

    Science.gov (United States)

    Zhang, Xuefei; Yates, Matthew Z

    2018-05-23

    Fast recombination of photogenerated charge carriers in titanium dioxide (TiO 2 ) remains a challenging issue, limiting the photocatalytic activity. This study demonstrates increased photocatalytic performance of TiO 2 nanoparticles supported on electrically polarized hydroxyapatite (HA) films. Dense and thermally stable yttrium and fluorine co-doped HA films with giant internal polarization were synthesized as photocatalyst supports. TiO 2 nanoparticles deposited on the support were then used to catalyze the photochemical reduction of aqueous silver ions to produce silver nanoparticles. It was found that significantly more silver nanoparticles were produced on polarized HA supports than on depolarized HA supports. In addition, the photodegradation of methyl orange with TiO 2 nanoparticles on polarized HA supports was found to be much faster than with TiO 2 nanoparticles on depolarized HA supports. It is proposed that separation of photogenerated electrons and holes in TiO nanoparticles is promoted by the internal polarization of the HA support, and consequently, the recombination of charge carriers is mitigated. The results imply that materials with large internal polarization can be used in strategies for enhancing quantum efficiency of photocatalysts.

  11. Solvothermal preparation of micro/nanostructured TiO_2 with enhanced lithium storage capability

    International Nuclear Information System (INIS)

    Li, Jie; Wang, Chao; Zheng, Ping; Zhang, Lei; Chen, Gongxuan; Tang, Chengchun; Wu, Tian

    2017-01-01

    Facile and controllable preparation of TiO_2 is of prime importance to elaborately tailor and then fully exploit its intriguing functionalities in energy storage, catalysis and environmental remediation. Herein, a solvothermal method combined with post annealing is conducted, in which the hydrolysis of tetrabutyl titanate is controlled by the in-situ generated water during solvothermal treatment. By controlling synthetic conditions (i.e. reactant ratio, solvothermal temperature and reaction time), we manage to tailor the morphologies of TiO_2. Specially, three typical structures (nanoparticle, nanoneedle and nanorod) are studied to reveal the growth mechanism and the effects of the synthesis conditions. Nanoneedle-structured TiO_2 shows higher specific capacity and enhanced cycle stability as anode material for lithium ion batteries. - Highlights: • Controllable preparation of nano-TiO_2 is achieved by a solvothermal method. • TiO_2 morphology is tailored by tuning reactant ratio, temperature and duration. • Needle structured TiO_2 shows enhanced lithium storage capability.

  12. Efficient silver modification of TiO2 nanotubes with enhanced photocatalytic activity

    Science.gov (United States)

    Huang, Jing; Ding, Lei; Xi, Yaoning; Shi, Liang; Su, Ge; Gao, Rongjie; Wang, Wei; Dong, Bohua; Cao, Lixin

    2018-06-01

    In this paper, Ag(CH3NH2)2+, Ag(NH3)2+ and Ag+ with different radii have been used as silver sources to find out the distribution of Ag ions on the H-TNT surface, which is critical to the final performance. The influence of this distribution on visible photocatalytic activity is further studied. The results indicate that, when Ag+ used as silver source with low concentration, these small sized silver ions mainly distribute on interlayer spacing of H-TNT. After heat-treatment and photo-reduction, the generated silver nanoparticles uniformly embed in the anatase TiO2 nanotube walls, and bring large interfacial area between Ag particles and TiO2 nanotubes. The separation effect of photogenerated electron-hole pair in TiO2 is enhanced by Ag particles, and achieves the best at 0.15 g/L, much higher than P25, TiO2/0, Ag-N@TiO2 and Ag-C-N@TiO2. This paper provides new ideas for the modification of TiO2 nanotubes.

  13. Application of a TiO2 nanocomposite in earplugs, a case study of noise reduction.

    Science.gov (United States)

    Ibrahimi Ghavamabadi, Leila; Fouladi Dehaghi, Behzad; Hesampour, Morteza; Ahmadi Angali, Kambiz

    2018-03-13

    Use of hearing protection devices (HPDs) has become necessary when other control measures cannot reduce noise to a safe and standard level. In most countries, more effective hearing protection devices are in demand. The aim of this study was to examine the effects of titanium dioxide (TiO 2 ) nanoparticles on noise reduction efficiency in a polyvinyl chloride (PVC) earplug. An S-60 type PVC polymer as main matrix and TiO 2 with 30 nm size were used. PVC/TiO 2 nanocomposite was mixed at a temperature of 160 °C and 40 rounds per minute (rpm) and the samples were prepared with 0, 0.2 and 0.5 wt% of TiO 2 nanoparticle concentrations. Earplug samples with PVC/TiO 2 (0.2, 0.5 wt%) nanoparticles, when compared with raw earplugs, showed almost equal noise attenuation at low frequencies (500- 125 Hz). However, at high frequencies (2-8 kHz), the power of noise reduction of earplugs containing TiO 2 nanoparticles was significantly increased. The results of the present study showed that samples containing nanoparticles of TiO 2 had more noticeable noise reduction abilities at higher frequencies in comparison with samples without the nanoparticles.

  14. Self-assembled supramolecular system PDINH on TiO2 surface enhances hydrogen production.

    Science.gov (United States)

    Li, Xin; Lv, Xingshuai; Zhang, Qianqian; Huang, Baibiao; Wang, Peng; Qin, Xiaoyan; Zhang, Xiaoyang; Dai, Ying

    2018-09-01

    Constructing organic-inorganic hybrids is one of the hopeful strategies to improve photocatalyst performance. In this study, perylene-3,4,9,10-tetracarboxylic diimide (PDINH) and commercial TiO 2 P25 are chosen as raw materials to construct a PDINH/TiO 2 organic-inorganic hybrid, which has higher photocatalytic H 2 production activity and photocurrent intensity than pure PDINH and TiO 2 , respectively. The apparent quantum efficiency for H 2 production over 0.5%PDINH/TiO 2 reaches as high as 70.69% using irradiation at 365 nm. Moreover, XRD, DRS, HRTEM, FT-IR, and XPS are used to characterize the crystal structure, optical absorption, morphology, molecular structure, and chemical bonds, as well as the elemental and chemical states of PDINH/TiO 2 organic-inorganic hybrid. The interfaces between PDINH and TiO 2 , which largely determine photocatalytic performance, is also analyzed systematically. Furthermore, charge density difference (Δρ) is used to analyze the electron-ion interactions of PDINH and TiO 2 , and reveals that substantial charge transfer occurs from PDINH to TiO 2 . Copyright © 2018. Published by Elsevier Inc.

  15. Significantly enhanced visible light response in single TiO2 nanowire by nitrogen ion implantation

    Science.gov (United States)

    Wu, Pengcheng; Song, Xianyin; Si, Shuyao; Ke, Zunjian; Cheng, Li; Li, Wenqing; Xiao, Xiangheng; Jiang, Changzhong

    2018-05-01

    The metal-oxide semiconductor TiO2 shows enormous potential in the field of photoelectric detection; however, UV-light absorption only restricts its widespread application. It is considered that nitrogen doping can improve the visible light absorption of TiO2, but the effect of traditional chemical doping is far from being used for visible light detection. Herein, we dramatically broadened the absorption spectrum of the TiO2 nanowire (NW) by nitrogen ion implantation and apply the N-doped single TiO2 NW to visible light detection for the first time. Moreover, this novel strategy effectively modifies the surface states and thus regulates the height of Schottky barriers at the metal/semiconductor interface, which is crucial to realizing high responsivity and a fast response rate. Under the illumination of a laser with a wavelength of 457 nm, our fabricated photodetector exhibits favorable responsivity (8 A W-1) and a short response time (0.5 s). These results indicate that ion implantation is a promising method in exploring the visible light detection of TiO2.

  16. Tailoring luminescence properties of TiO2 nanoparticles by Mn doping

    International Nuclear Information System (INIS)

    Choudhury, B.; Choudhury, A.

    2013-01-01

    TiO 2 nanoparticles are doped with three different concentrations of Mn, 2%, 4% and 6% respectively. Absorption edge of TiO 2 is shifted from UV to visible region on amplification of Mn content. Room temperature photoluminescence spectra, excited at 320 nm, exhibit band edge and visible emission peaks associated with self trapped excitons, oxygen defects, etc. Doping of Mn increases the width and decreases the intensity of the UV emission peak. Potential fluctuations of impurities increase the width and auger type non-radiative recombination decreases the intensity of the UV emission peak. The intensity ratio of the UV to defect emission band decreases on doping, indicating degradation of structural quality. Excitation of pure and doped nanoparticles at 390 nm results in Mn 2+ emission peaks at 525 nm and 585 nm respectively. Photoluminescence excitation spectra also indicate the presence of Mn 2+ in the crystalline environment of TiO 2 . The oxygen defects and Mn related impurities act as efficient trap centers and increases the lifetime of the charge carriers. -- Highlights: ► Doping of Mn increases the d-spacing of TiO 2 nanoparticles. ► Characteristic d–d electronic transition of Mn 2+ is observed in the absorption spectra. ► Doping of Mn quenches the UV and visible emission peaks of TiO 2 . ► Photoexcitation at 390 nm generates emission peaks of Mn 2+

  17. Soft-Template Synthesis of Mesoporous Anatase TiO2 Nanospheres and Its Enhanced Photoactivity

    Directory of Open Access Journals (Sweden)

    Xiaojia Li

    2017-11-01

    Full Text Available Highly crystalline mesoporous anatase TiO2 nanospheres with high surface area (higher than P25 and anatase TiO2 are prepared by a soft-template method. Despite the high specific surface area, these samples have three times lower equilibrium adsorption (<2% than Degussa P25. The rate constant of the mesoporous anatase TiO2 (0.024 min−1 reported here is 364% higher than that of P25 (0.0066 min−1, for the same catalytic loading. The results of oxidation-extraction photometry using several reactive oxygen species (ROS scavengers indicated that mesoporous anatase TiO2 generates more ROS than P25 under UV-light irradiation. This significant improvement in the photocatalytic performance of mesoporous spherical TiO2 arises from the following synergistic effects in the reported sample: (i high surface area; (ii improved crystallinity; (iii narrow pore wall thicknesses (ensuring the rapid migration of photogenerated carriers to the surface of the material; and (iv greater ROS generation under UV-light.

  18. First-principles study of Mn-S codoped anatase TiO2

    Science.gov (United States)

    Li, Senlin; Huang, Jinliang; Ning, Xiangmei; Chen, Yongcha; Shi, Qingkui

    2018-04-01

    In this work, the CASTEP program in Materials Studio 2017 software package was applied to calculate the electronic structures and optical properties of pure anatase TiO2, S-doped, Mn-doped and Mn-S co-doped anatase TiO2 by GGA + U methods based on the density function theory (DFT). The results indicate that the lattice is distorted and the lattice constant is reduce due to doping. The doping also introduces impurity energy levels into the forbidden band. After substitution of Mn for Ti atom, band gap narrowing of anatase TiO2 is caused by the impurity energy levels appearance in the near Fermi surface, which are contributed by Mn-3d orbital, Ti-3d orbital and O-2p orbital hybridization. After substitution of S for O atom, band gap narrowing is creited with the shallow accepter level under the conduction hand of S-3p orbital. The Mn-S co-doped anatase TiO2 could be a potential candidate for a photocatalyst because of tis enhanced absorption ability of visible light. The results can well explain the immanent cause of a band gap narrowing as well as a red shift in the spectrum for doped anatase TiO2.

  19. Density functional theory studies of TiO2 for photocatalysis and Li storage applications

    Science.gov (United States)

    Kim, Yong-Hoon; Lee, Ji Il; Lee, Dong Ki; Lee, Gyu Heon; Kang, Jeung Ku

    We present two theory-experiment collaboration studies of anatase TiO2 for energy applications. First, we discuss a hydrogen-nitrogen co-doped TiO2 (HN-TiO2) as a photocatalyst, and show that the interstitially introduced HN contributes to the increase of solar-to-fuel conversion efficiency. We find that the variation of valence band maximum (VBM) of NH-TiO2 extends the photoactive spectrum to the visible light, and argue that created mid-gap states produce efficient electron and hole conduction channels. Next, we consider experimentally fabricated hierarchical TiO2 nanocrystals integrated with binder-free porous graphene (PG) network foam for a Li storage application. It was found that the TiO2-PG facilitated rapid ionic transfer during the Li-ion insertion/extraction process. We clarify the mechanisms by showing that Li ion migration into the TiO2-PG interface stabilize the binder-free oxide-graphene interface. Atomistic mechanism of Li ion insertion and migration is discussed by comparing cases between an isolated Li ion, when the crowding effect is included, and when the surface Li ions are present. We found that the supply of additional surface Li ions significantly reduce the Li insertion barrier, driving a spontaneous domino-like concerted Li insertion at the oxide surface region.

  20. Nitrogen and europium doped TiO2 anodized films with applications in photocatalysis

    International Nuclear Information System (INIS)

    Chi, Choong-Soo; Choi, Jinwook; Jeong, Yongsoo; Lee, Oh Yeon; Oh, Han-Jun

    2011-01-01

    Micro-arc oxidation method is a useful process for mesoporous titanium dioxide films. In order to improve the photocatalytic activity of the TiO 2 film, N-Eu co-doped titania catalyst was synthesized by micro-arc oxidation in the H 2 SO 4 /Eu(NO 3 ) 3 mixture solution. The specific surface area and the roughness of the anodic titania film fabricated in the H 2 SO 4 /Eu(NO 3 ) 3 electrolyte, were increased compared to that of the anodic TiO 2 film prepared in H 2 SO 4 solution. The absorbance response of N-Eu titania film shows a higher adsorption onset toward visible light region, and the incorporated N and Eu ions during anodization as a dopant in the anodic TiO 2 film significantly enhanced the photocatalytic activity for dye degradation. After dye decomposition test for 3 h, dye removal rates for the anodic TiO 2 film were 60.7% and 90.1% for the N-Eu doped titania film. The improvement of the photocatalytic activity was ascribed to the synergistic effects of the surface enlargement and the new electronic state of the TiO 2 band gap by N and Eu co-doping.