  1. Dynamic recrystallization behavior of a medium carbon vanadium microalloyed steel

    International Nuclear Information System (INIS)

    Wei, Hai-lian; Liu, Guo-quan; Xiao, Xiang; Zhang, Ming-he

    2013-01-01

    The dynamic recrystallization behavior of a medium carbon vanadium microalloyed steel was systematically investigated at the temperatures from 900 °C to 1100 °C and strain rates from 0.01 s −1 to 10 s −1 on a Gleeble-1500 thermo-simulation machine. The flow stress constitutive equation of hot deformation for this steel was developed with the activation energy Q being about 273 kJ/mol, which is in reasonable agreement with those reported before. Activation energy analysis showed that vanadium addition in microalloyed steels seemed not to affect the activation energy much. The effect of Zener–Hollomon parameter on the characteristic points of flow curves was studied using the power law relation, and the dependence of critical strain (stress) on peak strain (stress) obeyed a linear equation. Dynamic recrystallization is the most important softening mechanism for the experimental steel during hot compression. The dynamic recrystallization kinetics model of this steel was established based on flow stress and a frequently-used dynamic recrystallization kinetics equation. Dynamic recrystallization microstructure under different deformation conditions was also observed and the dependence of steady-state grain size on the Zener–Hollomon parameter was plotted

  2. Intragranular ferrite morphologies in medium carbon vanadium-microalloyed steel

    Directory of Open Access Journals (Sweden)

    Fadel A.

    2013-01-01

    Full Text Available The aim of this work was to determine TTT diagram of medium carbon V-N micro-alloyed steel with emphasis on the development of intragranular ferrite morphologies. The isothermal treatment was carried out at 350, 400, 450, 500, 550 and 600°C. These treatments were interrupted at different times in order to analyze the evolution of the microstructure. Metallographic evaluation was done using optical and scanning electron microscopy (SEM. The results show that at high temperatures (≥ 500°C polygonal intragranulary nucleated ferrite idiomorphs, combined with grain boundary ferrite and pearlite were produced and followed by an incomplete transformation phenomenon. At intermediate temperatures (450, 500°C an interloced acicular ferrite (AF microstructure is produced, and at low temperatures (400, 350°C the sheave of parallel acicular ferrite plates, similar to bainitic sheaves but intragranularly nucleated were observed. In addition to sheaf type acicular ferrite, the grain boundary nucleated bainitic sheaves are observed. [Projekat Ministartsva nauke Republike Srbije, br. OI174004

  3. Plastic behavior of medium carbon vanadium microalloyed steel at temperatures near g « a transformation

    Directory of Open Access Journals (Sweden)

    Lourenço N.J.

    2001-01-01

    Full Text Available Dilatometric techniques were used to build the continuous cooling transformation (CCT diagram for a medium carbon microalloyed steel; the microstructure and hardness were determined at different cooling rates. The mechanical behavior of the steel in the austenite field and at temperatures approaching austenite to ferrite transformation was measured by means of hot torsion tests under isothermal and continuous cooling conditions. The no recrystallization temperatures, Tnr, and start of phase transformation, Ar3, were determined under continuous cooling condition using mean flow stress vs. inverse of absolute temperature diagrams. Interruption of static recrystallization within the interpass time in the austenite field indicated that the start of vanadium carbonitride precipitation occurred under 860 °C. Austenite transformation was found to start at around 710 °C, a temperature similar to that measured by dilatometry, suggesting that interphase precipitation delays the transformation of deformed austenite. Pearlite was observed at temperatures ranging from 650 °C to 600 °C, with the flow curves taking on a particular shape, i.e., stress rose sharply as strain was increased, reaching peak stress at low deformation, around 0.2, followed by an extensive softening region after peak stress.

  4. Study on the behavior of medium carbon vanadium microalloyed steel by hot compression test

    Energy Technology Data Exchange (ETDEWEB)

    Meysami, Majid [School of Metallurgy and Materials Engineering, University College of Engineering, University of Tehran, P.O. Box 11155-4653, Tehran (Iran, Islamic Republic of); Mousavi, Seyed Ali Asghar Akbari, E-mail: akbarimusavi@ut.ac.ir [School of Metallurgy and Materials Engineering, University College of Engineering, University of Tehran, P.O. Box 11155-4653, Tehran (Iran, Islamic Republic of)

    2011-03-25

    Research highlights: {yields} At low Z parameter, the multi peak dynamic recrystallization behavior was observed. {yields} At high Z, the stress-strain curves were exhibited with a single peak stress. {yields} The hyperbolic sine law was found to provide the best fit for calculation of Q. {yields} The average value of n was obtained as 4.687. {yields} The peak stress and of the studied material was obtained. - Abstract: This article investigates the hot working behavior of medium carbon vanadium microalloyed steel by hot compression tests over the temperature range of 850-1100 deg. C and strain rate range of 0.001-0.5 s{sup -1} to strain of 0.8. In this study, the general constitutive equations were used to determine the hot working constants. The peak stress ({sigma}{sub P}) and strain ({epsilon}{sub P}) for initiation of dynamic recrystallization (DRX) at different temperatures and strain rates were calculated. The power law, exponential and hyperbolic sinusoidal types of Zener-Hollomon equations were used to determine the hot deformation activation energy (Q). The results suggested that the highest correlation coefficient was achieved for the hyperbolic sine law for the studied material. The magnitude of hot deformation activation energy (Q) was obtained as 319.910 kJ/mol. The classical single peak DRX was observed in most of temperatures and strain rates. However, for temperature of 1100 deg. C and strain rates of 0.001 s{sup -1}, 0.01 s{sup -1}, and also for temperature of 950 deg. C and strain rate of 0.001 s{sup -1} the multiple peak dynamic recrystallization (MDRX) was observed, which showed that the 'recrystallization' was an observed strain rate behavior.

  5. Study on the behavior of medium carbon vanadium microalloyed steel by hot compression test

    International Nuclear Information System (INIS)

    Meysami, Majid; Mousavi, Seyed Ali Asghar Akbari

    2011-01-01

    Research highlights: → At low Z parameter, the multi peak dynamic recrystallization behavior was observed. → At high Z, the stress-strain curves were exhibited with a single peak stress. → The hyperbolic sine law was found to provide the best fit for calculation of Q. → The average value of n was obtained as 4.687. → The peak stress and of the studied material was obtained. - Abstract: This article investigates the hot working behavior of medium carbon vanadium microalloyed steel by hot compression tests over the temperature range of 850-1100 deg. C and strain rate range of 0.001-0.5 s -1 to strain of 0.8. In this study, the general constitutive equations were used to determine the hot working constants. The peak stress (σ P ) and strain (ε P ) for initiation of dynamic recrystallization (DRX) at different temperatures and strain rates were calculated. The power law, exponential and hyperbolic sinusoidal types of Zener-Hollomon equations were used to determine the hot deformation activation energy (Q). The results suggested that the highest correlation coefficient was achieved for the hyperbolic sine law for the studied material. The magnitude of hot deformation activation energy (Q) was obtained as 319.910 kJ/mol. The classical single peak DRX was observed in most of temperatures and strain rates. However, for temperature of 1100 deg. C and strain rates of 0.001 s -1 , 0.01 s -1 , and also for temperature of 950 deg. C and strain rate of 0.001 s -1 the multiple peak dynamic recrystallization (MDRX) was observed, which showed that the 'recrystallization' was an observed strain rate behavior.

  6. Simulation of the hot flow behaviour of a medium carbon microalloyed steel. Part 2. Dynamic recrystallization: onset and kinetics

    International Nuclear Information System (INIS)

    Cabrera, J.M.; Al Omar, A.; Prado, J.M.

    1997-01-01

    According to the part 1 of this work, in this second part the dynamic recrystallization of a commercial medium carbon microalloyed steel is characterized from the point of view of its onset and kinetics. For this purpose uniaxial hot compression tests were carried out over a range of five orders of magnitude in strain rate and 300 degree centigree of temperature. Experimental results are compared with those reported in the literature and the possible effect of dynamic precipitation is also analyzed. It is verified that the kinetics of dynamics recrystallization can balefully be described by the classical Avrami equation. (Author) 42 refs

  7. Influence of microstructure on the low and high cycle fatigue behaviour of a medium carbon microalloyed steel

    International Nuclear Information System (INIS)

    Srivastava, V.; Padmanabhan, K.A.

    2001-01-01

    This paper reports the room temperature monotonic and cyclic stress-strain (CSS) response, the low and high cycle fatigue behaviour of a medium carbon microalloyed (MA) steel in different microstructural conditions obtained by isothermal transformation at 973, 773 and 573 K following austenitizing at 1123 K. The isothermal transformations resulted in coarse pearlite (CP), fine pearlite (FP), and acicular ferrite/bainite (AF/B) microstructures, respectively. In low cycle fatigue, the CP and FP microstructures exhibited cyclic softening at low total strain amplitudes ( cys ) of the material and was approximately equal to 0.7σ cys . (orig.)

  8. Modeling of kinetics of isothermal idiomorphic ferrite formation in a medium carbon vanadium-titanium microalloyed steel

    International Nuclear Information System (INIS)

    Capdevila, C.; Caballer, E. G.; Garcia de Andres, C.

    2002-01-01

    A theoretical model is presented in this work to calculate the evolution of isothermal austenite-to-idiomorphic ferrite transformation in a medium carbon vanadium-titanium microalloyed steel. This model has been developed on the basis of the study of the nucleation and growth kinetics of idiomorphic ferrite, considering the influence of the nature, size and distribution of the inclusions, which are responsible of the intragranular nucleation of idiomorphic ferrite. Moreover, the influence of the austenite grain size on the isothermal decomposition of austenite in idiomorphic ferrite has been thoroughly analysed. An excellent agreement (85% in R''2) has been obtained between experimental and predicted values of volume fraction of idiomorphic ferrite. (Author) 32 refs

  9. Simulation of the hot flow behaviour of a medium carbon microalloyed steel. Part 1. Theoretical approach

    International Nuclear Information System (INIS)

    Cabrera, J.M.; Prado, J.M.

    1997-01-01

    The constitutive equations to model the hot flow behaviour of metallic materials in general, and of microalloyed steels in particular (see part 2 of this work) are established in this work. Special emphasis is done on the dynamic softening mechanisms, i.e., dynamic recovery and recrystallization phenomena. The equations developed are physic-based, not empirical, and the modelling allows an easy implementation in an analysis by numerical methods. The resulting equations are even able to predict the final grain size. (Author) 39 refs

  10. Simulation of the hot flow behaviour of a medium carbon microalloyed steel

    International Nuclear Information System (INIS)

    Cabrera, J.M.; Al Omar, A.; Prado, J.M.

    1997-01-01

    According to the part 1 of this work the constitutive equations of the hot flow behaviour of a commercial microalloyed steel have been obtained. For this purpose, the uniaxial hot compression tests described in the part 2 were employed. Tests were carried out over a range of 5 orders of magnitude in strain rate and 300 degree centigree of temperature. Experimental results are compared with the theoretical model introduced in the first part of this study. It is concluded that deviations between experimental and theoretical curves are lower than 10%. It is shown that the classical hyperbolic sine constitutive equation described accurately the experimental behaviour provided that stresses are normalized by the Young's modulus and strain rates by the self-diffusion coefficient. An internal stress must also be introduced in the latter equation when the initial grain size is fine enough. (Author) 24 refs

  11. Computational Design of a Novel Medium-Carbon, Low-Alloy Steel Microalloyed with Niobium

    Science.gov (United States)

    Javaheri, Vahid; Nyyssönen, Tuomo; Grande, Bjørnar; Porter, David

    2018-04-01

    The design of a new steel with specific properties is always challenging owing to the complex interactions of many variables. In this work, this challenge is dealt with by combining metallurgical principles with computational thermodynamics and kinetics to design a novel steel composition suitable for thermomechanical processing and induction heat treatment to achieve a hardness level in excess of 600 HV with the potential for good fracture toughness. CALPHAD-based packages for the thermodynamics and kinetics of phase transformations and diffusion, namely Thermo-Calc® and JMatPro®, have been combined with an interdendritic segregation tool (IDS) to optimize the contents of chromium, molybdenum and niobium in a proposed medium-carbon low-manganese steel composition. Important factors taken into account in the modeling and optimization were hardenability and as-quenched hardness, grain refinement and alloying cost. For further investigations and verification, the designed composition, i.e., in wt.% 0.40C, 0.20Si, 0.25Mn, 0.90Cr, 0.50Mo, was cast with two nominal levels of Nb: 0 and 0.012 wt.%. The results showed that an addition of Nb decreases the austenite grain size during casting and after slab reheating prior to hot rolling. Validation experiments showed that the predicted properties, i.e., hardness, hardenability and level of segregation, for the designed composition were realistic. It is also demonstrated that the applied procedure could be useful in reducing the number of experiments required for developing compositions for other new steels.

  12. Application of processing maps in the optimization of the parameters of a hot working process. Part 2. Processing maps of a microalloyed medium carbon steel

    International Nuclear Information System (INIS)

    Al Omar, A.; Cabrera, J.M.; Prado, J.M.

    1997-01-01

    Part 1 of this work presents a revision of the general characteristics of the so called dynamic materials model on which processing maps are developed. In this part following the methodology described in part 1, processing maps of a microalloyed medium carbon steel are developed over a temperature range varying from 900 to 1.150 degree centigree at different true strain rates ranging from 10''-4 to 10s''-1. The analysis of these maps revealed a domain of dynamic recrystallization centred at about 1.1.50 degree centigree and strain rate 10 s''-1 and a domain of dynamic recovery centred at 900 degree centigree and 0,1 s''-1. (Author) 20 refs

  13. Carbon Equivalence and Weldability of Microalloyed Steels

    Science.gov (United States)

    1989-10-25

    being considered for Navy applications. Wilson et al [181 in their review of copper-adde. steels have shown that in the CCT diagram for modified versions...almost linearly with austenite grain size (Fig. 4.2) [211. Therefore, the net effect of the addition of micro-alloying elements is to shift the CCT ... diagram to shorter times and thereby decrease the amount of martensite in the HAZ. Recently, computation of austenite grain growth in the HAZ’s of micro

  14. Medium carbon vanadium micro alloyed steels for drop forging

    International Nuclear Information System (INIS)

    Jeszensky, Gabor; Plaut, Ronald Lesley

    1992-01-01

    Growing competitiveness of alternative manufacturing routes requires cost minimization in the production of drop forged components. The authors analyse the potential of medium carbon, vanadium microalloyed steels for drop forging. Laboratory and industrial experiments have been carried out emphasizing deformation and temperature cycles, strain rates and dwell times showing a typical processing path, associated mechanical properties and corresponding microstructures. The steels the required levels of mechanical properties on cooling after forging, eliminating subsequent heat treatment. The machinability of V-microalloyed steels is also improved when compared with plain medium carbon steels. (author)

  15. High carbon microalloyed martensitic steel with ultrahigh strength-ductility

    Energy Technology Data Exchange (ETDEWEB)

    Qin, Shengwei; Liu, Yu; Hao, Qingguo [School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Wang, Ying [School of Mechanical Engineering, Shanghai Dianji University, Shanghai 200245 (China); Chen, Nailu, E-mail: nlchen@sjtu.edu.cn [School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Zuo, Xunwei; Rong, Yonghua [School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China)

    2016-04-29

    Based on the idea of rising the mechanical stability of retained austenite by the addition of Si in Fe-Mn based steels, an Fe-0.63C-1.52Mn-1.49Si-0.62Cr-0.036Nb was designed, then its hot rolled plate was successively tread by normalization process as pretreatment of novel quenching-partitioning-tempering (Q-P-T) process. Product of tensile and elongation (PSE) of 53.94 GPa% were obtained for this high carbon Q-P-T martensitic steel, and the PSE (40.18 GPa%) obtained by the conversion of tensile sample size using Oliver formula still is more excellent PSE than those of other microalloyed advanced high strength steels reported. The microstructural characterization reveals origin of ultrahigh PSE resulting from both the increase of considerable and dispersed carbon enriched retained austenite with relative high mechanical stability in volume fraction and the decrease of brittle twin-type martensite with the sensitivity of notch.

  16. Study of the thermo-mechanical behavior of medium carbon microalloyed steel during hot forming process using an artificial neural network; Estudio del comportamiento termo-mecanico de un acero microaleado de medio carbono durante un proceso de conformado en caliente usando una red neuronal artificial

    Energy Technology Data Exchange (ETDEWEB)

    Alcelay, I.; Pena, E.; Al Omar, A.

    2016-10-01

    The thermo-mechanical behavior of medium carbon microalloyed steel has been analyzed by an Artificial Neural Network (ANN). The flow curves for training the ANN have been obtained from the hot compression tests, carried out over a temperature range varying from 900 to 1150 degree centigrade and at different true strain rates ranging from 10{sup -}4 to 10 s{sup -}1. It has been found that the ANN model developed in this study is capable to predict accurately and efficiently the flow behavior of the studied steel and there is a good agreement between the experimental results and the ANN results. To analyze the formability of the studied steel, processing maps have been constructed on the basis of the Dynamic Materials Model (DMM), using the ANN values of the flow stress. The study of maps reveals the different domains of the flow behavior of the studied steel and shows the great similarity between the experimental results and the theoretical results, so the use of the ANN can constitute an interesting alternative for design and study of hot forming processes. (Author)

  17. Precipitation Strengthening by Induction Treatment in High Strength Low Carbon Microalloyed Hot-Rolled Plates

    Science.gov (United States)

    Larzabal, G.; Isasti, N.; Rodriguez-Ibabe, J. M.; Uranga, P.

    2018-03-01

    The use of microalloyed steels in the production of thick plates is expanding due to the possibility of achieving attractive combinations of strength and toughness. As market requirements for high strength plates are increasing and new applications require reduced weight and innovative designs, novel approaches to attaining cost-effective grades are being developed. The mechanism of precipitation strengthening has been widely used in thin strip products, since the optimization of the coiling strategy offers interesting combinations in terms of final properties and microalloying additions. Precipitation strengthening in thick plates, however, is less widespread due to the limitation of interphase precipitation during continuous cooling after hot rolling. With the main objective of exploring the limits of this strengthening mechanism, laboratory thermomechanical simulations that reproduced plate hot rolling mill conditions were performed using low carbon steels microalloyed with Nb, NbMo, and TiMo additions. After continuous cooling to room temperature, a set of heat treatments using fast heating rates were applied simulating the conditions of induction heat treatments. An important increase of both yield and tensile strengths was measured after induction treatment without any important impairment in toughness properties. A significant precipitation hardening is observed in Mo-containing grades under specific heat treatment parameters.

  18. Hot ductility behavior of a low carbon advanced high strength steel (AHSS) microalloyed with boron

    OpenAIRE

    Mejía, Ignacio; Bedolla Jacuinde, Arnoldo; Maldonado, Cuauhtémoc; Cabrera Marrero, José M.

    2011-01-01

    The current study analyses the influence of boron addition on the hot ductility of a low carbon advanced high strength NiCrVCu steel. For this purpose hot tensile tests were carried out at different temperatures (650, 750, 800, 900 and 1000 ◦C) at a constant true strain rate of 0.001 s−1. Experimental results showed a substantial improvement in hot ductility for the low carbon advanced high strength steel when microalloyed with boron compared with that without boron addition. Nevertheless,...

  19. Nb(C,N) precipitation kinetics in the bainite region of a low-carbon Nb-microalloyed steel

    International Nuclear Information System (INIS)

    Park, J.S.; Lee, Y.K.

    2007-01-01

    Nb(C,N) precipitation in the bainite region (580-660 deg. C) of a low-carbon Nb-microalloyed steel was investigated by electrical resistivity and transmission electron microscopy. Nb(C,N) particles started precipitating after 100-200 s at isothermal temperatures after bainite transformation and cementite formation, and precipitation finished in 1000-2000 s. The precipitation-time-temperature diagram of Nb(C,N) in the bainite region of a low-carbon microalloyed steel was a type of C-curve, with a nose temperature of about 615 deg. C

  20. The kinetics of dynamic recrystallization of a low carbon vanadium-nitride microalloyed steel

    International Nuclear Information System (INIS)

    Zhao, Baochun; Zhao, Tan; Li, Guiyan; Lu, Qiang

    2014-01-01

    Single-pass compression tests were performed on a Gleeble-3800 thermo-mechanical simulator to study the dynamic recrystallization behavior of a low carbon vanadium-nitride microalloyed steel at the temperature in the range from 900 °C to 1050 °C and strain rate in the range from 0.1 s −1 to 10 s −1 . Based on the flow curves from the tests, the effects of temperature and strain rate on the dynamic recrystallization behavior were analyzed. With the assistance of the process parameters, constitutive equations were used to obtain the activation energy and hot working equation. The strain hardening rate versus stress curves were used to determine the critical stress (strain) or the peak stress (strain). The dependence of the characteristic values on Zener–Hollomon was found. The dynamic recrystallization kinetics model of the tested steel was constructed and the validity was confirmed based on the experimental results

  1. Hot ductility behavior of a low carbon advanced high strength steel (AHSS) microalloyed with boron

    International Nuclear Information System (INIS)

    Mejia, I.; Bedolla-Jacuinde, A.; Maldonado, C.; Cabrera, J.M.

    2011-01-01

    Research highlights: → Effect of boron on the hot ductility behavior of a low carbon NiCrVCu AHSS. → Boron addition of 117 ppm improves hot ductility over 100% in terms of RA. → Hot ductility improvement is associated with segregation/precipitation of boron. → Typical hot ductility recovery at lower temperatures does not appear in this steel. → Hot ductility loss is associated with precipitates/inclusions coupled with voids. - Abstract: The current study analyses the influence of boron addition on the hot ductility of a low carbon advanced high strength NiCrVCu steel. For this purpose hot tensile tests were carried out at different temperatures (650, 750, 800, 900 and 1000 deg. C) at a constant true strain rate of 0.001 s -1 . Experimental results showed a substantial improvement in hot ductility for the low carbon advanced high strength steel when microalloyed with boron compared with that without boron addition. Nevertheless, both steels showed poor ductility when tested at the lowest temperatures (650, 750 and 800 deg. C), and such behavior is associated to the precipitation of vanadium carbides/nitrides and inclusions, particularly MnS and CuS particles. The fracture mode of the low carbon advanced high strength steel microalloyed with boron seems to be more ductile than the steel without boron addition. Furthermore, the fracture surfaces of specimens tested at temperatures showing the highest ductility (900 and 1000 deg. C) indicate that the fracture mode is a result of ductile failure, while in the region of poor ductility the fracture mode is of the ductile-brittle type failure. It was shown that precipitates and/or inclusions coupled with voids play a meaningful role on the crack nucleation mechanism which in turn causes a hot ductility loss. Likewise, dynamic recrystallization (DRX) which always results in restoration of ductility only occurs in the range from 900 to 1000 deg. C. Results are discussed in terms of boron segregation towards

  2. Hot ductility behavior of a low carbon advanced high strength steel (AHSS) microalloyed with boron

    Energy Technology Data Exchange (ETDEWEB)

    Mejia, I., E-mail: imejia@umich.mx [Instituto de Investigaciones Metalurgicas, Universidad Michoacana de San Nicolas de Hidalgo, Edificio ' U' , Ciudad Universitaria, 58066 Morelia, Michoacan (Mexico); Bedolla-Jacuinde, A.; Maldonado, C. [Instituto de Investigaciones Metalurgicas, Universidad Michoacana de San Nicolas de Hidalgo, Edificio ' U' , Ciudad Universitaria, 58066 Morelia, Michoacan (Mexico); Cabrera, J.M. [Departament de Ciencia dels Materials i Enginyeria Metal.lurgica, ETSEIB - Universitat Politecnica de Catalunya, Av. Diagonal 647, 08028 Barcelona (Spain); Fundacio CTM Centre Tecnologic, Av. de las Bases de Manresa 1, 08240 Manresa (Spain)

    2011-05-25

    Research highlights: {yields} Effect of boron on the hot ductility behavior of a low carbon NiCrVCu AHSS. {yields} Boron addition of 117 ppm improves hot ductility over 100% in terms of RA. {yields} Hot ductility improvement is associated with segregation/precipitation of boron. {yields} Typical hot ductility recovery at lower temperatures does not appear in this steel. {yields} Hot ductility loss is associated with precipitates/inclusions coupled with voids. - Abstract: The current study analyses the influence of boron addition on the hot ductility of a low carbon advanced high strength NiCrVCu steel. For this purpose hot tensile tests were carried out at different temperatures (650, 750, 800, 900 and 1000 deg. C) at a constant true strain rate of 0.001 s{sup -1}. Experimental results showed a substantial improvement in hot ductility for the low carbon advanced high strength steel when microalloyed with boron compared with that without boron addition. Nevertheless, both steels showed poor ductility when tested at the lowest temperatures (650, 750 and 800 deg. C), and such behavior is associated to the precipitation of vanadium carbides/nitrides and inclusions, particularly MnS and CuS particles. The fracture mode of the low carbon advanced high strength steel microalloyed with boron seems to be more ductile than the steel without boron addition. Furthermore, the fracture surfaces of specimens tested at temperatures showing the highest ductility (900 and 1000 deg. C) indicate that the fracture mode is a result of ductile failure, while in the region of poor ductility the fracture mode is of the ductile-brittle type failure. It was shown that precipitates and/or inclusions coupled with voids play a meaningful role on the crack nucleation mechanism which in turn causes a hot ductility loss. Likewise, dynamic recrystallization (DRX) which always results in restoration of ductility only occurs in the range from 900 to 1000 deg. C. Results are discussed in terms of

  3. Contributions of Rare Earth Element (La,Ce) Addition to the Impact Toughness of Low Carbon Cast Niobium Microalloyed Steels

    Science.gov (United States)

    Torkamani, Hadi; Raygan, Shahram; Garcia Mateo, Carlos; Rassizadehghani, Jafar; Palizdar, Yahya; San-Martin, David

    2018-03-01

    In this research Rare Earth elements (RE), La and Ce (200 ppm), were added to a low carbon cast microalloyed steel to disclose their influence on the microstructure and impact toughness. It is suggested that RE are able to change the interaction between the inclusions and matrix during the solidification process (comprising peritectic transformation), which could affect the microstructural features and consequently the impact property; compared to the base steel a clear evolution was observed in nature and morphology of the inclusions present in the RE-added steel i.e. (1) they changed from MnS-based to (RE,Al)(S,O) and RE(S)-based; (2) they obtained an aspect ratio closer to 1 with a lower area fraction as well as a smaller average size. Besides, the microstructural examination of the matrix phases showed that a bimodal type of ferrite grain size distribution exists in both base and RE-added steels, while the mean ferrite grain size was reduced from 12 to 7 μm and the bimodality was redressed in the RE-added steel. It was found that pearlite nodule size decreases from 9 to 6 μm in the RE-added steel; however, microalloying with RE caused only a slight decrease in pearlite volume fraction. After detailed fractography analyses, it was found that, compared to the based steel, the significant enhancement of the impact toughness in RE-added steel (from 63 to 100 J) can be mainly attributed to the differences observed in the nature of the inclusions, the ferrite grain size distribution, and the pearlite nodule size. The presence of carbides (cementite) at ferrite grain boundaries and probable change in distribution of Nb-nanoprecipitation (promoted by RE addition) can be considered as other reasons affecting the impact toughness of steels under investigation.

  4. Improved ductility of Ni3Si by microalloying with boron or carbon

    International Nuclear Information System (INIS)

    Taub, A.I.; Briant, C.L.

    1989-01-01

    The effects of boron and carbon additions on the tendency for intergranular fracture in trinickel silicide intermetallics are reported. Melt spinning of Ni 77 Si 23 alloyed with 0.1 at. pct boron results in full bend ductility and complete transgranular fracture compared with brittle intergranular fracture for the unmodified compound. Alloying with 0.1 at. pct carbon also produced full bend ductility but a mixed mode failure (30 pct transgranular). For both carbon and boron additions, reducing the Ni concentration of the base compound results in a greater percentage of intergranular fracture. For Ni 77 Si 23 , the solubility limit is between 0.1 and 0.2 t. pct boron. For compounds with silicon concentrations of 23.5 and 24.0 at. pct, the solubility limit is less than 0.1 at. pct boron. Boron additions above the solubility limit result in Ni 3 B precipitates which degrade the bend ductility and increase the percentage of intergranular fracture. Alloying with carbon above the solubility limit ( 77 Si 23 , increasing the carbon concentration from 0.1 to 1.0 at. pct resulted in no change in the ductility. Auger examination of the grain boundary composition showed strong segregation of both boron and carbon. Enrichment in silicon concentration was also observed

  5. Nano-sized precipitation and properties of a low carbon niobium micro-alloyed bainitic steel

    Energy Technology Data Exchange (ETDEWEB)

    Xie, Z.J. [School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China); Department of Materials Science and Engineering, McMaster University, Hamilton L8S 4L8 (Canada); Ma, X.P. [Department of Materials Science and Engineering, McMaster University, Hamilton L8S 4L8 (Canada); Shang, C.J., E-mail: cjshang@ustb.edu.cn [School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China); Wang, X.M. [School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China); Subramanian, S.V. [Department of Materials Science and Engineering, McMaster University, Hamilton L8S 4L8 (Canada)

    2015-08-12

    The present work focuses on microstructure evolution and precipitation strengthening during tempering at region of 550–680 °C to elucidate the structure–property relationship in the steel. The effect of tempering on the development of a 700 MPa grade high strength hot rolled cost-effective bainitic steel was studied for infrastructure applications. Granular bainite with dispersed martenisit–austenite (M–A) constituents in the bainitic ferrite matrix was obtained after hot rolling and air cooling to room temperature. The decomposition of M–A constituents to cementite carbides and the precipitation of nano-sized NbC carbides in bainitic matrix on tempering were characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Nano-sized precipitates of NbC precipitated during tempering were in average diameter of ~4.1–6.1 nm. There were ~86–173 MPa increases in yield strength after tempering at region of 550–680 °C. It is noticeable that those nano-sized NbC precipitates provide an effective way to significantly increase the strength of the low carbon bainitic steel. High yield strength of 716 MPa with high ductility (uniform elongation of 9.3% and total elongation of 22.4%), low yield to tensile ratio of 0.9 and good low temperature toughness of 47 J (half thickness) at –40 °C was obtained after tempering at 680 °C for 30 min.

  6. Structure–property relationship in a 960 MPa grade ultrahigh strength low carbon niobium–vanadium microalloyed steel: The significance of high frequency induction tempering

    International Nuclear Information System (INIS)

    Xie, Z.J.; Fang, Y.P.; Han, G.; Guo, H.; Misra, R.D.K.; Shang, C.J.

    2014-01-01

    The present study describes the microstructure and precipitation behavior in an ultra-high strength low carbon niobium–vanadium microalloyed steel that was processed by quenching and high frequency induction tempering. Ultrahigh yield strength of ∼1000 MPa with high elongation of ∼15% and high low temperature toughness of 55 J (half thickness) at −40 °C was obtained after quenching from austenitization at 900 °C for 30 min, and tempering at 600 °C for 15 min by induction reheating with a reheating rate of ∼50 °C/s. While the yield strength increase on tempering was similar for both induction reheating and conventional reheating (electrical resistance reheating), there was ∼100% increase in low temperature toughness in induction reheated steel compared to the conventional reheating process. The underlying reason for the increase in toughness was attributed to the transformation of cementite film observed in conventional reheating and tempering to nanoscale cementite in induction reheating and tempering. The precipitation of nanoscale carbides is believed to significantly contribute to ultra-high strength, good ductility, and high toughness in the high frequency induction reheating and tempering process

  7. Distribution of Stress in Deformation Zone of Niobium Microalloyed Steel

    Science.gov (United States)

    Jandrlić, Ivan; Rešković, Stoja; Brlić, Tin

    2018-07-01

    Microalloyed steels today represent a significant part of total world production and processing of steel. Although widely used, there are scarce data on the stress distribution in the deformation zone of these steels. Research was carried out on two steel grades, both low-carbon structural steels with the same basic chemical composition, with one of them additionally microalloyed with niobium. Differences in the stress distribution in the deformation zone between two tested steels were continuously observed and measured using the methods of digital image correlation and thermography. It has been found out that niobium microalloyed steel has significantly more complex material flow and stress distribution in the deformation zone when compared to the plain low carbon steel.

  8. Distribution of Stress in Deformation Zone of Niobium Microalloyed Steel

    Science.gov (United States)

    Jandrlić, Ivan; Rešković, Stoja; Brlić, Tin

    2018-03-01

    Microalloyed steels today represent a significant part of total world production and processing of steel. Although widely used, there are scarce data on the stress distribution in the deformation zone of these steels. Research was carried out on two steel grades, both low-carbon structural steels with the same basic chemical composition, with one of them additionally microalloyed with niobium. Differences in the stress distribution in the deformation zone between two tested steels were continuously observed and measured using the methods of digital image correlation and thermography. It has been found out that niobium microalloyed steel has significantly more complex material flow and stress distribution in the deformation zone when compared to the plain low carbon steel.

  9. Microstructure and mechanical properties of a Ti-microalloyed low-carbon stainless steel treated by quenching-partitioning-tempering process

    Energy Technology Data Exchange (ETDEWEB)

    Xie, S.T., E-mail: xst-2007@163.com [State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819 (China); Liu, Z.Y. [State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819 (China); Wang, Z. [Research Institute, Baoshan Iron & Steel Co. Ltd., Shanghai 201900 (China); Wang, G.D. [State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819 (China)

    2016-06-15

    Quenching-partitioning-tempering (Q-P-T) process was used to treat a Ti-microalloyed low-carbon stainless steel after cold rolling. In addition to martensite, ferrite and retained austenite, TiN, coarse TiC, fine TiC, (Fe,Cr){sub 3}C and ultra-fine TiC precipitates were formed after the Q-P-T treatment. Based on field emission-scanning electron microscope (FESEM) and transmission electron microscope (TEM) observations, thermodynamic, crystallographic and statistical analyses were used to reveal the precipitation behaviors of these particles. The effects of partitioning-tempering (P-T) temperature and time on the microstructure and mechanical properties of Q-P-T treated specimens were specially studied. The coarsening and spheroidization of (Fe,Cr){sub 3}C particles during P-T stage were obviously retarded by large Cr addition. The retained austenite was obtained significantly with appropriate P-T parameters. The precipitation of ultra-fine TiC particles in the martensite during the P-T stage at 500 °C induced a secondary hardening. - Highlights: • Some fine TiC with 30–70 nm precipitated in austenite during partial austenization. • A part of fine TiC had K-S OR with martensite after Q-P-T treatment. • A part of fine TiC had a OR specially deviating from K-S OR with martensite. • Coarsening and spheroidization of (Fe,Cr){sub 3}C were retarded during P-T stage. • Ultra-fine TiC with < 10 nm precipitated in martensite during P-T stage at 500 °C.

  10. Mixed structures in continuously cooled low-carbon automotive steels

    International Nuclear Information System (INIS)

    Khalid, F.A.; Edmonds, D.V.

    1993-01-01

    Mixed microstructures have been studied in low- carbon microalloyed steels suitable for automotive applications, after continuous cooling from the hot-rolled condition. Microstructural features such as polygonal ferrite, bainitic and acicular ferrite and microphase constituent are identified using transmission electron microscopy. The influence of these mixed structures on the tensile strength, impact toughness and fracture behaviour is examined. It is found that improvements in impact toughness as compared with microalloyed medium- carbon ferrite/pearlite steels can be achieved from these predominantly acicular structures developed by controlling alloy composition and continuous cooling of these lower carbon steels. (orig.)

  11. Deformation behavior of two continuously cooled vanadium microalloyed steels at liquid nitrogen temperature

    Directory of Open Access Journals (Sweden)

    Glišić Dragomir M.

    2013-01-01

    Full Text Available The aim of this work was to establish deformation behaviour of two vanadium microalloyed medium carbon steels with different contents of carbon and titanium by tensile testing at 77 K. Samples were reheated at 1250°C/30 min and continuously cooled at still air. Beside acicular ferrite as dominant morphology in both microstructures, the steel with lower content of carbon and negligible amount of titanium contains considerable fraction of grain boundary ferrite and pearlite. It was found that Ti-free steel exhibits higher strain hardening rate and significantly lower elongation at 77 K than the fully acicular ferrite steel. The difference in tensile behavior at 77 K of the two steels has been associated with the influence of the pearlite, together with higher dislocation density of acicular ferrite. [Projekat Ministarstva nauke Republike Srbije, br. OI174004

  12. Effect of microalloying elements on microstructure and properties of quenched and tempered constructional steel

    Science.gov (United States)

    Ma, Qingshen; Huang, Leqing; Di, Guobiao; Wang, Yanfeng; Yang, Yongda; Ma, Changwen

    2017-09-01

    The effects of microalloying elements Nb, V and Ti on microstructure and properties of quenched and tempered steel were studied. Results showed that the addition of microalloying elements led to the formation of bainite and increased strength, while the austenization and ferrite transformation temperature was barely affected, i.e. 10°C. Microalloying elements shortened the incubation time for bainite transformation by refinement of austenite grain, and decreased the hardenability by forming carbides and therefore reducing the carbon content of super-cooled austenite. Either of them promoted the bainite transformation. The better tempering stability was ascribed to the as hot-rolled bainite microstructure and secondary carbide precipitation during tempering.

  13. Medium temperature carbon dioxide gas turbine reactor

    International Nuclear Information System (INIS)

    Kato, Yasuyoshi; Nitawaki, Takeshi; Muto, Yasushi

    2004-01-01

    A carbon dioxide (CO 2 ) gas turbine reactor with a partial pre-cooling cycle attains comparable cycle efficiencies of 45.8% at medium temperature of 650 deg. C and pressure of 7 MPa with a typical helium (He) gas turbine reactor of GT-MHR (47.7%) at high temperature of 850 deg. C. This higher efficiency is ascribed to: reduced compression work around the critical point of CO 2 ; and consideration of variation in CO 2 specific heat at constant pressure, C p , with pressure and temperature into cycle configuration. Lowering temperature to 650 deg. C provides flexibility in choosing materials and eases maintenance through the lower diffusion leak rate of fission products from coated particle fuel by about two orders of magnitude. At medium temperature of 650 deg. C, less expensive corrosion resistant materials such as type 316 stainless steel are applicable and their performance in CO 2 have been proven during extensive operation in AGRs. In the previous study, the CO 2 cycle gas turbomachinery weight was estimated to be about one-fifth compared with He cycles. The proposed medium temperature CO 2 gas turbine reactor is expected to be an alternative solution to current high-temperature He gas turbine reactors

  14. High toughness in the intercritically reheated coarse-grained (ICRCG) heat-affected zone (HAZ) of low carbon microalloyed steel

    Energy Technology Data Exchange (ETDEWEB)

    Hu, Jun, E-mail: hujunral@163.com [The State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819 (China); Du, Lin-Xiu [The State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819 (China); Wang, Jian-Jun [Institute of Materials Research, School of Material and Metallurgy, Northeastern University, Shenyang 110819 (China); Xie, Hui; Gao, Cai-Ru [The State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819 (China); Misra, R.D.K. [Laboratory for Excellence in Advanced Steel Research, Center for Structural and Functional Materials, University of Louisiana at Lafayette, Lafayette, LA 70504-4130 (United States)

    2014-01-10

    Motivated by the small lattice mismatch between ferrite and vanadium nitride (VN), we describe here the welding thermal cycle simulation that provides high toughness in the ICRCG HAZ of low carbon V–N steel. This unique behavior is attributed to the formation of ultra-fine grained ferrite along prior austenite grain boundaries generated by the first pass welding thermal cycle with high misorientation boundaries, where V(C, N) precipitates provide potential nucleation sites for ferrite, leading to extraordinary refinement of martensite/austenite (M/A) constituent. Nitrogen stimulates the precipitation behavior of V(C, N). The nucleation of high density of V(C, N) precipitates consumes carbon-content in the austenite, leading to decrease in the carbon-content in the M/A constituent, with consequent decrease in hardness. The increase in toughness is explained in terms of Griffith's crack propagation theory.

  15. High toughness in the intercritically reheated coarse-grained (ICRCG) heat-affected zone (HAZ) of low carbon microalloyed steel

    International Nuclear Information System (INIS)

    Hu, Jun; Du, Lin-Xiu; Wang, Jian-Jun; Xie, Hui; Gao, Cai-Ru; Misra, R.D.K.

    2014-01-01

    Motivated by the small lattice mismatch between ferrite and vanadium nitride (VN), we describe here the welding thermal cycle simulation that provides high toughness in the ICRCG HAZ of low carbon V–N steel. This unique behavior is attributed to the formation of ultra-fine grained ferrite along prior austenite grain boundaries generated by the first pass welding thermal cycle with high misorientation boundaries, where V(C, N) precipitates provide potential nucleation sites for ferrite, leading to extraordinary refinement of martensite/austenite (M/A) constituent. Nitrogen stimulates the precipitation behavior of V(C, N). The nucleation of high density of V(C, N) precipitates consumes carbon-content in the austenite, leading to decrease in the carbon-content in the M/A constituent, with consequent decrease in hardness. The increase in toughness is explained in terms of Griffith's crack propagation theory

  16. Hot flow behavior of boron microalloyed steels

    International Nuclear Information System (INIS)

    Lopez-Chipres, E.; Mejia, I.; Maldonado, C.; Bedolla-Jacuinde, A.; El-Wahabi, M.; Cabrera, J.M.

    2008-01-01

    This research work studies the effect of boron contents on the hot flow behavior of boron microalloyed steels. For this purpose, uniaxial hot-compression tests were carried out in a low carbon steel microalloyed with four different amounts of boron over a wide range of temperatures (950, 1000, 1050 and 1100 deg. C) and constant true strain rates (10 -3 , 10 -2 and 10 -1 s -1 ). Experimental results revealed that both peak stress and peak strain tend to decrease as boron content increases, which indicates that boron additions have a solid solution softening effect. Likewise, the flow curves show a delaying effect on the kinetics of dynamic recrystallization (DRX) when increasing boron content. Deformed microstructures show a finer austenitic grain size in the steel with higher boron content (grain refinement effect). Results are discussed in terms of boron segregation towards austenitic grain boundaries during plastic deformation, which increases the movement of dislocations, enhances the grain boundary cohesion and modificates the grain boundary structure

  17. Plane strain forging of a niobium micro-alloyed steel

    International Nuclear Information System (INIS)

    Balancin, O.; Ferran L, G.; Rio de Janeiro Univ.

    1984-01-01

    Various termomechanical treatments were carried out on a niobium micro-alloyed steel and a low carbon steel as reference material, using an apparatus for hot phane strain forging. Control of processing variables and the presence of niobium strongly modify the austenite microstructure, which upon decomposition produces various phases such as polygonal and acicular ferrite and martensite, alone or together in variable proportions. Corresponding to this diversity of structures there is a wide variation in mechanical properties at room temperature: the initial yield point varies from 310 to 650 MPa and the reduction of area in uniaxial tension from 82 to 57% for the niobium steel. These results show that hot forging a niobium micro-alloyed steel may be a suitable manufacturing process for satisfying a wide range of specifications in a final product with low equivalent carbon. (Author) [pt

  18. HYDROGEN INDUCED CRACKING IN MICROALLOYED STEELS

    Directory of Open Access Journals (Sweden)

    Duberney Hincapie-Ladino

    2015-03-01

    Full Text Available The need for microalloyed steels resistant to harsh environments in oil and gas fields, such as pre-salt which contain considerable amounts of hydrogen sulfide (H2 S and carbon dioxide (CO2 , requires that all sectors involved in petroleum industry know the factors that influence the processes of corrosion and failures by hydrogen in pipelines and components fabricated with microalloyed steels. This text was prepared from a collection of selected publications and research done at the Electrochemical Processes Laboratory of Metallurgical and Materials Engineering Department, Polytechnic School, São Paulo University. This document does not intend to be a complete or exhaustive review of the literature, but rather to address the main scientific and technological factors associated with failures by hydrogen in the presence of wet hydrogen sulfide (H2 S, particularly, when related to the Hydrogen Induced Cracking (HIC phenomenon. This complex phenomenon that involves several successive stages, HIC phenomena were discussed in terms of environmental and metallurgical variables. The HIC starts with the process of corrosion of steel, therefore must be considered the corrosive media (H2 S presence effect. Moreover, it is necessary to know the interactions of compounds present in the electrolyte with the metal surface, and how they affect the hydrogen adsorption and absorption into steel. The following stages are hydrogen diffusion, trapping and metal cracking, directly related to the chemical composition and the microstructure, factors that depend strongly on the manufacture of steel. The purpose of this paper is to provide the scientific information about the failures caused by hydrogen and challenge for the Oil and Gas Pipeline Industry.

  19. Chemistry of neptunium and of other actinides in carbonate medium

    International Nuclear Information System (INIS)

    Riglet, C.

    1990-01-01

    This work is a contribution to the establishment of a thermodynamic data base in order to forecast the behaviour of Np and other actinides in natural waters that might come into contact with a nuclear waste repository. Redox potentials and complexation constants in acidic and carbonate media are measured in aqueous solutions, in the presence of an inert salt (sodium perchlorate) of variable concentrations. The activity coefficients are calculated, from the variation of thermodynamic measurements with the ionic strength, with the Specific Interaction Theory (S.I.T.). The electrochemical data, obtained by polarography and voltamperometry, are interpreted, for irreversible systems, with numerical and graphical methods based on the Koutecky-Weber's and S.I.T. equations. The equilibrium constants in carbonate medium are measured by absorption spectrophotometry and a graphical method is proposed to determine the stoichiometries of polynuclear species. In this work are proposed numerical data relative to: - the redox potentials of the systems: M(VI/V) and M(IV/III) in acidic medium where M = U, Np, Pu; U(VI/V) in carbonate medium; Np(VI/V) in bicarbonate medium of ionic strength 3 M. - the formation constants of the hexakis (carbonato) tris [dioxoneptunate (VI)] complex in 3 M medium - the formation constants of the mono, di and tri (carbonato) dioxoneptunate (V) complexes - the influence of the ionic strength on some of the studied chemical equilibria by using, when necessary, literature results. All specific interaction coefficients (activity coefficients) of these species are also measured or calculated [fr

  20. Vanadium Effect on a Medium Carbon Forging Steel

    Directory of Open Access Journals (Sweden)

    Carlos Garcia-Mateo

    2016-05-01

    Full Text Available In the present work the influence of vanadium on the hardenability and the bainitic transformation of a medium carbon steel is analyzed. While V in solid solution enhances the former, it hardly affects bainitic transformation. The results also reveal an unexpected result, an increase of the prior austenite grain size as the V content increases.

  1. Medium carbon vanadium steels for closed die forging

    International Nuclear Information System (INIS)

    Jeszensky, Gabor; Plaut, Ronald Lesley

    1993-01-01

    This work analyses the medium carbon micro alloyed vanadium potential for closed die forged production. The steels reach the mechanical resistance requests during cooling after forging, eliminating the subsequent thermal treatment. Those steels also present good fatigue resistance and machinability. The industrial scale experiments are also reported

  2. Heterogeneously Catalysed Chemical Reactions in Carbon Dioxide Medium

    DEFF Research Database (Denmark)

    Musko, Nikolai E.

    In this PhD-study the different areas of chemical engineering, heterogeneous catalysis, supercritical fluids, and phase equilibrium thermodynamics have been brought together for selected reactions. To exploit the beneficial properties of supercritical fluids in heterogeneous catalysis, experimental...... studies of catalytic chemical reactions in dense and supercritical carbon dioxide have been complemented by the theoretical calculations of phase equilibria using advanced thermodynamic models. In the recent years, the use of compressed carbon dioxide as innovative, non-toxic and non-flammable, cheap......, and widely available reaction medium for many practical and industrial applications has drastically increased. Particularly attractive are heterogeneously catalysed chemical reactions. The beneficial use of CO2 is attributed to its unique properties at dense and supercritical states (at temperatures...

  3. Hot ductility of medium carbon steel with vanadium

    International Nuclear Information System (INIS)

    Lee, Chang-Hoon; Park, Jun-Young; Chung, JunHo; Park, Dae-Bum; Jang, Jin-Young; Huh, Sungyul; Ju Kim, Sung; Kang, Jun-Yun; Moon, Joonoh; Lee, Tae-Ho

    2016-01-01

    Hot ductility of medium carbon steel containing 0.52 wt% of carbon and 0.11 wt% of vanadium was investigated using a hot tensile test performed up to fracture. The hot ductility was evaluated by measuring the reduction of area of the fractured specimens, which were strained at a variety of test temperatures in a range of 600–1100 °C at a strain rate of 2×10"−"3/s. The hot ductility was excellent in a temperature range of 950–1100 °C, followed by a decrease of the hot ductility below 950 °C. The hot ductility continued to drop as the temperature was lowered to 600 °C. The loss of hot ductility in a temperature range of 800–950 °C, which is above the Ae_3 temperature, was due to V(C,N) precipitation at austenite grain boundaries. The further decline of hot ductility between 700 °C and 750 °C resulted from the transformation of ferrite films decorating austenite grain boundaries. The hot ductility continued to decrease at 650 °C or less, owing to ferrite films and the pearlite matrix, which is harder than ferrite. The pearlite was transformed from austenite due to relatively high carbon content.

  4. Allowable carbon emissions for medium-to-high mitigation scenarios

    Energy Technology Data Exchange (ETDEWEB)

    Tachiiri, Kaoru; Hargreaves, Julia C.; Annan, James D.; Kawamiya, Michio [Research Inst. for Global Change, Japan Agency for Marine-Earth Science and Technology, Yokohama, (Japan)], e-mail: tachiiri@jamstec.go.jp; Huntingford, Chris [Centre for Ecology and Hydrology, Wallingford (United Kingdom)

    2013-11-15

    Using an ensemble of simulations with an intermediate complexity climate model and in a probabilistic framework, we estimate future ranges of carbon dioxide (CO{sub 2}) emissions in order to follow three medium-high mitigation concentration pathways: RCP2.6, RCP4.5 and SCP4.5 to 2.6. Uncertainty is first estimated by allowing modelled equilibrium climate sensitivity, aerosol forcing and intrinsic physical and biogeochemical processes to vary within widely accepted ranges. Results are then constrained by comparison against contemporary measurements. For both constrained and unconstrained projections, our calculated allowable emissions are close to the standard (harmonised) emission scenarios associated with these pathways. For RCP4.5, which is the most moderate scenario considered in terms of required emission abatement, then after year 2100 very low net emissions are needed to maintain prescribed year 2100 CO{sub 2} concentrations. As expected, RCP2.6 and SCP4.5 to 2.6 require more strict emission reductions. The implication of this is that direct sequestration of carbon dioxide is likely to be required for RCP4.5 or higher mitigation scenarios, to offset any minimum emissions for society to function (the 'emissions floor'). Despite large uncertainties in the physical and biogeochemical processes, constraints from model-observational comparisons support a high degree of confidence in predicting the allowable emissions consistent with a particular concentration pathway. In contrast the uncertainty in the resulting temperature range remains large. For many parameter sets, and especially for RCP2.6, the land will turn into a carbon source within the twenty first century, but the ocean will remain as a carbon sink. For land carbon storage and our modelling framework, major reductions are seen in northern high latitudes and the Amazon basin even after atmospheric CO{sub 2} is stabilised, while for ocean carbon uptake, the tropical ocean regions will be a

  5. Study of the Metallurgical Aspects of Steel Micro-Alloying by Titan

    Directory of Open Access Journals (Sweden)

    Kijac, J.

    2006-01-01

    Full Text Available The metal properties upgrading applying it’s alloying with the simultaneous limitation of the impurities represents a prospective possibility of the metallurgical production further development. The interaction of the alloying substance active element with oxygen in metal and adjacent multiphase environment occurs under the actual conditions. Present paper is oriented particularly to the thermodynamic aspects of deoxygenation by titan in process of production of micro alloyed low carbon steel in two plants (oxygen converter 1-OC1 and 2-OC2 with the different effect of micro-alloy exploitation. Analysis of the effect of the metallurgical factors on the titan smelting loss in micro-alloyed steel production points at the need to master the metal preparation for the alloying and especially has got the decisive effect upon the oxidizing ability and rate of the slag phase availability. When comparing the micro-alloying matter yield among the individual production units, disclosed have been better results obtained in plant OC 2. Confirmed has been the effect of the slag amount (average amount of 7,3 t at OC 1 and 5,83 t at OC 2 and its quality during the steel tapping as one among the most significant factors affecting the alloying process and which also represent its oxidizing potential.

  6. Mechanical properties of as-cast microalloyed steels produced via investment casting

    International Nuclear Information System (INIS)

    Najafi, H.; Rassizadehghani, J.; Norouzi, S.

    2011-01-01

    Tensile and room temperature Charpy V-notch impact tests were used to evaluate the variations in the as-cast mechanical properties of a low-carbon steel produced via shell mould investment casting and containing combinations of vanadium, niobium and titanium. Tensile results indicate that the yield strength and ultimate tensile strength (UTS) have increased up to respectively 615 MPa and 770 MPa due to the fine-scale microalloy precipitates in the microalloyed samples. Room temperature impact test results show that while addition of vanadium individually has not changed the impact energy, Nb has decreased it considerably. However, examination of fracture surfaces reveals that all microalloyed samples have failed by transgranular cleavage. Based on the transmission electron microscope (TEM) studies, it seems that carbonitrides being greater than 50 nm in size and formed along prior austenite grain boundaries before γ transformation are responsible for the observed reduction in impact energies and brittle fracture. In comparison to sand mould casting, the yield and UTS obtained from investment casting are superior. Furthermore, although the impact energies of Nb-containing alloys are approximately the same as those obtained from sand moulds, the impact energy of the alloy containing only vanadium has improved considerably.

  7. Study on Spheroidization and Related Heat Treatments of Medium Carbon Alloy Steels

    Directory of Open Access Journals (Sweden)

    Harisha S. R.

    2018-01-01

    Full Text Available The importance of medium carbon steels as engineering materials is reflected by the fact that out of the vast majority of engineering grade ferrous alloys available and used in the market today, a large proportion of them are from the family of medium carbon steels. Typically medium carbon steels have a carbon range of 0.25 to 0.65% by weight, and a manganese content ranging from 0.060 to 1.65% by weight. Medium carbon steels are more resistive to cutting, welding and forming as compared to low carbon steels. From the last two decades a number of research scholars reported the use of verity of heat treatments to tailor the properties of medium carbon steels. Spheroidizing is the novel industrial heat treatment employed to improve formability and machinability of medium/high carbon low alloy steels. This exclusive study covers procedure, the effects and possible outcomes of various heat treatments on medium carbon steels. In the present work, other related heat treatments like annealing and special treatments for property alterations which serve as pretreatments for spheroidizing are also reviewed. Medium carbon steels with property alterations by various heat treatment processes are finding increased responsiveness in transportation, aerospace, space, underwater along with other variegated fields. Improved tribological and mechanical properties consisting of impact resistance, stiffness, abrasion and strength are the main reasons for the increased attention of these steels in various industries. In the present scenario for the consolidation of important aspects of various heat treatments and effects on mechanical properties of medium carbons steel, a review of different research papers has been attempted. This review may be used as a guide to provide practical data for heat treatment industry, especially as a tool to enhance workability and tool life.

  8. Benefits of carbon markets to small and medium enterprises (SMEs ...

    African Journals Online (AJOL)

    Harvested wooden handicrafts products have the ability to lock carbon for long time and mitigate climate change. These products are currently eligible for availing benefits from voluntary carbon markets. The market size and opportunities for carbon credits are likely to increase substantially for these products during the ...

  9. Engineering of rolled constructional microalloyed steel products

    International Nuclear Information System (INIS)

    Adamczyk, J.

    2003-01-01

    Flexibility of the microalloyed steels on manufacturing of products with high mechanical and technological properties at not exaggerated production costs, it caused of their application for different constructions and machines in many branches of economy. It is a reason of the big interest of this steel group and the improvement of metallurgical and technological processing. In the work the examples of applications of C-Mn microalloyed steels with V and N microadditions for production of long shape products of R p0.2 > 650 MPa and KCU2 > 57 Jcm -2 are presented. They are manufactured in the controlled rolling process. Moreover this work presents liquid metal treatment in ladlemann process and influence of ingots solidification conditions, controlled rolling of weldable plates with Nb, Ti, V and B microadditions which after quenching and tempering have R p0.2 > 870 MPa, KV -50 o C > 27 J and plastic strain ratio equals 1.2. This work also presents the energy saving rolling technology with controlled recrystallization (method of thermomechanical treatment) of improved Weldox 960 steel plates with Mb, Ti, V and B microadditions which have after high-temperature tempering R p0.2 > 100 MPa, KV -50 o C >90 J and plastic strain ratio is less than 1.2. The introduction of microalloyed constructional steels and the appropriate technology in the domestic industry will contribute to high-processed products with properties competitive to products manufactured in high-industrialized countries. Thanks to that it will be possible to increase the technical level as well as to reduce production costs and import. (author)

  10. Hot ductility behavior of boron microalloyed steels

    International Nuclear Information System (INIS)

    Lopez-Chipres, E.; Mejia, I.; Maldonado, C.; Bedolla-Jacuinde, A.; Cabrera, J.M.

    2007-01-01

    The current study analyses the influence of boron contents (between 29 and 105 ppm) on the hot ductility of boron microalloyed steels. For this purpose, hot tensile tests were carried out at different temperatures (700, 800, 900 and 1000 deg. C) at a constant true strain rate of 0.001 s -1 . In general, results revealed an improvement of the hot ductility of steels at increasing boron content. At 700, 900 and 1000 deg. C the ductility is higher than at 800 deg. C, where boron microalloyed steels exhibit a region of ductility loss (trough region). Likewise, dynamic recrystallization only occurred at 900 and 1000 deg. C. The fracture surfaces of the tested steels at temperatures giving the high temperature ductility regime show that the fracture mode is a result of ductile failure, whereas it is ductile-brittle failure in the trough region. Results are discussed in terms of dynamic recrystallization and boron segregation towards austenite grain boundaries, which may retard the formation of pro-eutectoid ferrite and increase grain boundary cohesion

  11. Benefits of carbon markets to small and medium enterprises (SMEs ...

    African Journals Online (AJOL)

    Administrator

    furniture can store carbon for more than 100 years. (Haripriya Gundimeda .... centre of wholesale and retail trade, particularly in grain, timber and textiles. The description of ... local wood carving cottage industry and other demands. There are ...

  12. On the carbon enrichment of the interstellar medium

    International Nuclear Information System (INIS)

    Sarmiento, A.; Peimbert, M.

    1985-01-01

    The contribution of novae, IMS, and massive stars to the 12 C and 13 C enrichment of the interstellar medium is evaluated. The following results are obtained: a) novae are not important contributors to the 12 C abundance but contribute significantly to 13 C, b) limits to the ratio of the mixing length to the pressure scale height,α, and to the mass loss rate parameter, eta, are derived for IMS, c) IMS are the main contributors to the 12 C and 13 C enrichment of the interstellar medium, d) it is easier to explain the solar vicinity 12 C/ 13 C ratio than the solar system ratio, e) to explain the 12 C/ 13 C ratio in the ISM the mass ejected per nova outburst has to be approx. 1 x 10 -5 M sub(sun). (author)

  13. Are carbon nanostructures an efficient hydrogen storage medium?

    NARCIS (Netherlands)

    Hirscher, M.; Becher, M.; Haluska, M.; Zeppelin, von F.; Chen, X.; Dettlaff-Weglikowska, U.; Roth, S.

    2003-01-01

    Literature data on the storage capacities of hydrogen in carbon nanostructures show a scatter over several orders of magnitude which cannot be solely explained by the limited quantity or purity of these novel nanoscale materials. With this in mind, this article revisits important experiments.

  14. Characterization and observation of water-based nanofluids quench medium with carbon particle content variation

    Science.gov (United States)

    Yahya, S. S.; Harjanto, S.; Putra, W. N.; Ramahdita, G.; Kresnodrianto, Mahiswara, E. P.

    2018-05-01

    Recently, nanofluids have been widely used in heat treatment industries as quench medium with better quenching performance. The thermal conductivity of nanofluids is higher compared to conventional quench medium such as polymer, water, brine, and petroleum-based oil. This characteristic can be achieved by mixing high thermal conductivity particles in nanometer scale with a fluid as base. In this research, carbon powder and distilled water were used as nanoparticles and base respectively. The carbon source used in this research was laboratory grade carbon powder, and activated carbon as a cheaper alternative source. By adjusting the percentage of dispersed carbon particles, thermal conductivity of nanofluids could be controlled as needed. To obtain nanoscale carbon particles, planetary ball mill was used to grind laboratory-grade carbon and active carbon powder to further decrease its particle size. This milling method will provide nanoparticles with lower production cost. Milling speed and duration were set at 500 rpm and 15 hours. Scanning electron microscope (SEM) and Energy Dispersive X-Ray (EDX) were carried out respectively to determine the particle size, material identification, particle morphology. The carbon nanoparticle content in nanofluids quench mediums for this research were varied at 0.1, 0.3, and 0.5 % vol. Furthermore, these mediums were used to quench AISI 1045 carbon steel samples which had been annealed at 1000 °C. Hardness testing and metallography observation were then conducted to check the effect of different quench medium in steel samples. Preliminary characterizations showed that the carbon particle dimension after milling was hundreds of nanometers, or still in sub-micron range. Therefore, the milling process parameters are need to be optimized further. EDX observation in laboratory-grade carbon powder showed that the powder was pure carbon as expected for, but in activated carbon has some impurities. The nanofluid itself, however, was

  15. Suitability of activated carbon fabric as sorption medium for ammonia

    International Nuclear Information System (INIS)

    Pallavee, V.K.; Soundararajan, S.; Patkulkar, D.S.; Ganesh, G.; Tripathi, R.M.

    2016-01-01

    Ammonia is used extensively in many industries and laboratories. It is also used in nuclear industries for production of heavy water and for preparation of uranium production process for preparation of ADU (Ammonium Diuranate). Being harmful to health, it's hazard need to be managed in a systematic and controlled manner with adequate personal protection. Granular activated carbon (GAC) is mostly used as standard absorbent in respirators against several gases and vapours but due to its bulkiness and higher pressure drop attempt was made to replace it with activated carbon fabric (ACF) which is thinner, light weight and have larger surface area. The aim of this study was to investigate the potential of ACF in realistic respirator cartridges in filtering pollutant gases like ammonia by determining its filtration efficiency

  16. Fatigue Life Estimation of Medium-Carbon Steel with Different Surface Roughness

    Directory of Open Access Journals (Sweden)

    Changyou Li

    2017-03-01

    Full Text Available Medium-carbon steel is commonly used for the rail, wire ropes, tire cord, cold heading, forging steels, cold finished steel bars, machinable steel and so on. Its fatigue behavior analysis and fatigue life estimation play an important role in the machinery industry. In this paper, the estimation of fatigue life of medium-carbon steel with different surface roughness using established S-N and P-S-N curves is presented. To estimate the fatigue life, the effect of the average surface roughness on the fatigue life of medium-carbon steel has been investigated using 75 fatigue tests in three groups with average surface roughness (Ra: 0.4 μm, 0.8 μm, and 1.6 μm, respectively. S-N curves and P-S-N curves have been established based on the fatigue tests. The fatigue life of medium-carbon steel is then estimated based on Tanaka-Mura crack initiation life model, the crack propagation life model using Paris law, and material constants of the S-N curves. Six more fatigue tests have been conducted to validate the presented fatigue life estimation formulation. The experimental results have shown that the presented model could estimate well the mean fatigue life of medium-carbon steel with different surface roughness.

  17. Studies on sorption of plutonium on inorganic exchangers from sodium carbonate medium

    Energy Technology Data Exchange (ETDEWEB)

    Pius, I C; Charyulu, M M; Sivaramakrishnan, C K [Fuel Chemistry Division, Bhabha Atomic Research Centre, Mumbai (India); Venkataramani, B [Chemistry Division, Bhabha Atomic Research Centre, Mumbai (India)

    1994-06-01

    Sorption of Pu(IV) from sodium carbonate medium has been investigated by using different inorganic exchangers alumina, silica gel and hydrous titanium oxide. Distribution ratios of Pu(IV) for its sorption on these exchangers from sodium carbonate medium were found to be sufficiently high indicating the suitability of these exchangers for the removal of Pu(IV). The presence of uranium and dibutyl phosphate do not have any effect on distribution ratio. The 10% Pu(IV) breakthrough capacities for above exchangers have been determined with 5 ml bed at a flow rate of 30 ml/hour. (author). 4 refs., 2 tabs.

  18. Behavior of the extraction of metallic ions in carbonate medium, using N-benzoylphenylhydroxylamine (BPHA) - benzene

    International Nuclear Information System (INIS)

    Cipriani, M.

    1978-01-01

    The possibility of separating quantitatively trace impurities like Cu, Fe, In and Pb, present in uranium base materials of nuclear grade, is demonstrated. A solvent extraction is employed which makes use of -benzoylphenylhydroxylamine(BPHA)-benzene solution and separation is effected in a medium containing 252 moles per liter of sodium-uranyl tricarbonate at pH of 9,0. Carbonate ions under such conditions inhibit uranium extraction by masking uranyl ion-BPHA reaction. The uranyl ions show a demasking action, releasing, thereby, Pb(II) ions which are being extracted from carbonate medium. The Atomic Absorption Spectrophometry technique is used to obtain the experimental data [pt

  19. Dissolving of Nb and Ti carbonitride precipitates in microalloyed steels

    Institute of Scientific and Technical Information of China (English)

    Wenjin Nie; Shanwu Yang; Shaoqiang Yuan; Xinlai He

    2003-01-01

    The dissolving behaviour of Nb and Ti carbonitride precipitates in microalloyed steels during isothermal holding at 1300℃ was investigated by Transmission electron microscopy (TEM) and energy dispersion x-ray spectrum (EDX). It was found that all precipitates in Nb-Ti microalloyed steel are (Nb, Ti)(C,N). With holding time increasing, the atomic ratio of Nb/Ti in precipitates decrease gradually. These precipitates still existe even after holding for 48 h at 1300℃ while Nb(C,N) precipitates dissolve away in Nb microalloyed steel only after 4 h at the same temperature. These results show that formation and thermostability of precipitates are considerably influenced by interaction between Nb and Ti.

  20. Corrosion behavior of carbon steel in wet Na-bentonite medium

    International Nuclear Information System (INIS)

    Yeon, Jae-Won; Ha, Young-Kyoung; Choi, In-Kyu; Chun, Kwan-Sik

    1996-01-01

    Corrosion behaviors of carbon steel in wet Na-bentonite medium were studied. Corrosion rate of carbon steel in wet bentonite was measured to be 20 μm/yr at 25 deg C using the AC impedance technique. This value is agreed with that obtained by weight loss at 40 deg C for 1 year. The effect of bicarbonate ion on the corrosion of carbon steel in wet bentonite was also evaluated. The carbon steels in wet bentonite having 0.001, 0.01, and 0.1 M concentration of bicarbonate ion gave corrosion rates of 20, 8, and 0.2 μm/yr, respectively. Corrosion potentials of specimens were also measured and compared with the AC impedance results. Both results indicated that bicarbonate ion could effectively reduce the corrosion rate of carbon steels in bentonite due to the formation of protective layer on the carbon steel. (author)

  1. Addition of Carbon to the Culture Medium Improves the Detection Efficiency of Aflatoxin Synthetic Fungi

    Directory of Open Access Journals (Sweden)

    Tadahiro Suzuki

    2016-11-01

    Full Text Available Aflatoxin (AF is a harmful secondary metabolite that is synthesized by the Aspergillus species. Although AF detection techniques have been developed, techniques for detection of AF synthetic fungi are still required. Techniques such as plate culture methods are continually being modified for this purpose. However, plate culture methods require refinement because they suffer from several issues. In this study, activated charcoal powder (carbon was added to a culture medium containing cyclodextrin (CD to enhance the contrast of fluorescence and improve the detection efficiency for AF synthetic fungi. Two culture media, potato dextrose agar and yeast extract sucrose agar, were investigated using both plate and liquid cultures. The final concentrations of CD and carbon in the media were 3 mg/mL and 0.3 mg/mL, respectively. Addition of carbon improved the visibility of fluorescence by attenuating approximately 30% of light scattering. Several fungi that could not be detected with only CD in the medium were detected with carbon addition. The carbon also facilitated fungal growth in the potato dextrose liquid medium. The results suggest that addition of carbon to media can enhance the observation of AF-derived fluorescence.

  2. Bainite Formation in Medium-Carbon Low-Silicon Spring Steels Accounting for Chemical Segregation

    NARCIS (Netherlands)

    Goulas, C.; Mecozzi, M.G.; Sietsma, J.

    2016-01-01

    In this paper, the effect of chemical inhomogeneity on the isothermal bainite formation is investigated in medium-carbon low-silicon spring steel by dilatometry and microscopy. The analysis of the microstructure at different times during transformation shows that chemical segregation of

  3. Phase Transformation Study in Nb-Mo Microalloyed Steels Using Dilatometry and EBSD Quantification

    Science.gov (United States)

    Isasti, Nerea; Jorge-Badiola, Denis; Taheri, Mitra L.; Uranga, Pello

    2013-08-01

    A complete microstructural characterization and phase transformation analysis has been performed for several Nb and Nb-Mo microalloyed low-carbon steels using electron backscattered diffraction (EBSD) and dilatometry tests. Compression thermomechanical schedules were designed resulting in the undeformed and deformed austenite structures before final transformation. The effects of microalloying additions and accumulated deformation were analyzed after CCT diagram development and microstructural quantification. The resulting microstructures ranged from polygonal ferrite and pearlite at slow cooling ranges, to a combination of quasipolygonal ferrite and granular ferrite for intermediate cooling rates, and finally, to bainitic ferrite with martensite for fast cooling rates. The addition of Mo promotes a shift in the CCT diagrams to lower transformation start temperatures. When the amount of Nb is increased, CCT diagrams show little variations for transformations from the undeformed austenite and higher initial transformation temperatures in the transformations from the deformed austenite. This different behavior is due to the effect of niobium on strain accumulation in austenite and its subsequent acceleration of transformation kinetics. This article shows the complex interactions between chemical composition, deformation, and the phases formed, as well as their effect on microstructural unit sizes and homogeneity.

  4. Toward the detection of pure carbon clusters in the Interstellar Medium (ISM)

    Science.gov (United States)

    Heath, J. R.; Van Orden, A.; Hwang, H. J.; Kuo, E. W.; Tanaka, K.; Saykally, R. J.

    1995-01-01

    Determination of the form and distribution of carbon in the universe is critical to understanding the origin of life on Earth and elsewhere. Two potentially large reservoirs of carbon in the interstellar medium (ISM) remain unexplored. These are polycyclic aromatic hydrocarbons (PAH) and pure carbon clusters. Little information exists on the structures, properties, and transition frequencies of pure carbon clusters. The work described is designed to provide a specific inventory of laboratory frequencies and physical properties of this carbon clusters so that efforts can be made to detect them in cold interstellar sources by far-infrared astronomy. Data is given from infrared laser spectroscopy determination of the structure of C3, C4, C5, C6, C7, and C9.

  5. Comparative study of different types of granular activated carbon in removing medium level radon from water

    International Nuclear Information System (INIS)

    Alabdula'aly, A.I.; Maghrawy, H.B.

    2011-01-01

    Granular activated carbon (GAC) has proven its effectiveness in removing radon from water supplies. Laboratory and pilot plant studies were carried out using three different types of activated carbons (F-300, F-400, and HD-4000) to remove radon from water supply. From the experimental kinetic study, the data indicated that at least 6 h are needed to attain equilibrium between radon activity adsorbed onto carbon and its concentration in the aqueous phase. Also, it showed that HD-4000 has higher capacity for removing radon than the other two investigated carbons F-300 and F-400. The adsorption isotherms were satisfactorily explained by Freundlich equation. In the pilot plant study, the performance of the three activated carbons in removing radon at medium concentration (∼111 Bq dm -3 ) was evaluated over 60 days of continuous water flow. Four empty-bed contact times (EBCTs) corresponding to four bed depths were continuously monitored and the corresponding steady state adsorption-decay constant values were calculated and the efficiency of each carbon was used to provide a facet for comparison. The γ-radiation exposure rate distribution throughout each GAC bed was measured and compared. This study, despite paucity of literature in this field, is useful for designing a GAC adsorption system for the removal of medium level radon concentration from water supplies. (author)

  6. Transformation kinetics of microalloyed steels after hot controlled ...

    African Journals Online (AJOL)

    Transformation kinetics of austenite into ferrite after controlled hot rolling has been investigated in three microalloyed steels (Nb, Nb-Ti and C-Mn-V) using hot interrupted compression tests on the Gleeble 1500 within the testing temperature range of 875°C-1100°C. Holding times were varied between 0.5 and 30s, strain ...

  7. Dependence of the cytotoxicity of multi-walled carbon nanotubes on the culture medium

    International Nuclear Information System (INIS)

    Zhu Ying; Ran Tiecheng; Li Yuguo; Guo Jinxue; Li Wenxin

    2006-01-01

    This study examined the influence of multi-walled carbon nanotubes (MWNTs) on the growth of the unicellular protozoan Tetrahymena pyriformis. Contrary to the findings from most other investigations, our experiment indicated that MWNTs stimulated growth of the cells cultured in proteose peptone yeast extract medium (PPY). Atomic force microscopy images and thermogravimetric analysis showed the spontaneous formation of peptone-MWNT conjugates in the medium by noncovalent binding. Uptake of large amounts of the conjugates by Tetrahymena pyriformis was responsible for growth stimulation, evidenced by images with fluorescently labelled peptone. After the PPY medium was replaced by a filtrated pond water medium (FPW), however, inhibition of the growth of cells exposed to MWNTs occurred. Measurements of the level of malondialdehyde and superoxide dismutase activity demonstrated further that MWNTs might be either toxic or nontoxic, depending on the medium used to cultivate Tetrahymena pyriformis. The biological effects of the interaction of MWNTs with some composites in culture media would be helpful for understanding the mechanisms of the toxicity of carbon nanotubes to living systems

  8. Powder metallurgical nanostructured medium carbon bainitic steel: Kinetics, structure, and in situ thermal stability studies

    Energy Technology Data Exchange (ETDEWEB)

    Lonardelli, I., E-mail: il244@cam.ac.uk [University of Cambridge, Materials Science and Metallurgy, Pembroke Street, Cambridge CB2 3QZ (United Kingdom); University of Trento, Materials Engineering and Industrial Technologies, via Mesiano 77, 38123 Trento (Italy); Bortolotti, M. [Fondazione Bruno Kessler, via Sommarive 18, 38123 Trento (Italy); Beek, W. van [Swiss-Norwegian Beamlines, ESRF, BP 220, 38043 Grenoble Cedex (France); Girardini, L.; Zadra, M. [K4-Sint, via Dante 300, 38057 Pergine Valsugana (Italy); Bhadeshia, H.K.D.H. [University of Cambridge, Materials Science and Metallurgy, Pembroke Street, Cambridge CB2 3QZ (United Kingdom)

    2012-10-15

    It has been possible to produce incredibly fine plates of bainitic ferrite separated by a percolating network of retained austenite in a medium carbon steel produced by mechanical alloying followed by spark plasma sintering and isothermal heat treatment. This is because the sintering process limits the growth of the austenite grains to such an extent that the martensite-start temperature is suppressed in spite of the medium carbon concentration. Furthermore, the fine austenite grain size accelerates the bainite transformation, which can therefore be suppressed to low temperatures to obtain a nanostructure. Microscopy and in situ synchrotron X-ray diffraction were used to investigate the morphology and the thermal stability of the retained austenite during continuous heating. These latter experiments revealed a gradient of carbon concentration in the retained austenite and a reduced thermal stability in high carbon film-austenite. It was also possible to correlate the evolution of defect density and carbon depletion in both retained austenite and bainitic ferrite during tempering.

  9. Hydrogen degradation of 21-6-9 and medium carbon steel by disc pressure test

    International Nuclear Information System (INIS)

    Zhou, D.H.; Zhou, W.X.; Xu, Z.L.

    1986-01-01

    This paper reports the method of disc pressure test and the results for 21-6-9 stainless steel and medium carbon steel in hydrogen gas with different pressures and time of storage. The results show the hydrogen induced degradation of these two kinds of steel. An attempt was made to establish an index which uses variation of area of deformed disc to determine the degradation of ductility in a hydrogen environment. (orig.)

  10. Carbide characterization in a Nb-microalloyed advanced ultrahigh strength steel after quenching-partitioning-tempering process

    International Nuclear Information System (INIS)

    Wang, X.D.; Xu, W.Z.; Guo, Z.H.; Wang, L.; Rong, Y.H.

    2010-01-01

    Based on the observations of scanning electron microscopy and transmission electron microscopy, four kinds of carbides were identified in a Nb-microalloyed steel after quenching-partitioning-tempering treatment. In addition to transitional epsilon carbide that usually forms in silicon-free carbon steel, other three types of niobium carbides (NbC) formed at various treatment stages respectively. They are incoherent NbC inclusion that nucleated at solidification mainly, fine NbC that nucleated in lath martensite at tempering stage and regular polygonal NbC that nucleated in austenite before quenching. Their formation mechanisms on steel were discussed briefly based on thermodynamics.

  11. Chemistry of the aqueous medium - Determining factor of corrosion in carbon steel components of secondary circuit

    International Nuclear Information System (INIS)

    Radulescu, M.; Pirvan, I.; Dinu, A.; Velciu, L.

    2003-01-01

    The interplay of chemistry of aqueous medium and corrosion processes followed by deposition and/or release of corrosion products determines both formation and growth of superficial films as well as the kinetics of ion release from materials into the aqueous medium. Material corrosion in the secondary circuit of a NPP can be minimized by choosing the materials of the components and by a rigorous inspection of the chemistry of aqueous agent. The chemical inspection helps in minimizing: - the corrosion of the components immersed in feedwater and vapor and of Steam Generator components; - 'dirtying' of the systems particularly of the surfaces implied in heat transfer; - the amount of insoluble chemical species resulting in corrosion process and carried along the circuit; - the corrosion of secondary circuit components during revisions or outages. An important role among the chemical parameters of the fluids circulated in NPP tubing appears to be the pH. In CANDU reactors it must be kept within the range of 8.7 to 9.4 by treating the medium with volatile amines (morpholine and cyclohexylamine). A plot is presented giving the corrosion rate of carbon steels as a function of the pH of the medium. Besides, the oxygen concentration dissolved in the aqueous medium must be maintained under 5 μg per water kg. Other factors determining the corrosion rates are also discussed. The paper gives the results of the experiments done with various materials, solutions and analysis methods

  12. Longitudinal waves in carbon nanotubes in the presence of transverse magnetic field and elastic medium

    Science.gov (United States)

    Liu, Hu; Liu, Hua; Yang, Jialing

    2017-09-01

    In the present paper, the coupling effect of transverse magnetic field and elastic medium on the longitudinal wave propagation along a carbon nanotube (CNT) is studied. Based on the nonlocal elasticity theory and Hamilton's principle, a unified nonlocal rod theory which takes into account the effects of small size scale, lateral inertia and radial deformation is proposed. The existing rod theories including the classic rod theory, the Rayleigh-Love theory and Rayleigh-Bishop theory for macro solids can be treated as the special cases of the present model. A two-parameter foundation model (Pasternak-type model) is used to represent the elastic medium. The influence of transverse magnetic field, Pasternak-type elastic medium and small size scale on the longitudinal wave propagation behavior of the CNT is investigated in detail. It is shown that the influences of lateral inertia and radial deformation cannot be neglected in analyzing the longitudinal wave propagation characteristics of the CNT. The results also show that the elastic medium and the transverse magnetic field will also affect the longitudinal wave dispersion behavior of the CNT significantly. The results obtained in this paper are helpful for understanding the mechanical behaviors of nanostructures embedded in an elastic medium.

  13. MICROALLOYED STEELS FOR THE AUTOMOTIVE INDUSTRY

    Directory of Open Access Journals (Sweden)

    Debanshu Bhattacharya

    2014-12-01

    is the so-called “3rd Generation” AHSS. These steels are designed to fill the region between the dual-phase/TRIP and the Twin Induced Plasticity (TWIP steels with very high ductility at strength levels comparable to the conventional AHSS. Enhanced Q&P steels may be one method to achieve this target. Other ideas include TRIP assisted dual phase steels, high manganese steels and carbide-free bainitic (CFB steels. Finally the post hardened steels (PHS are an important component of the strategy of future vehicles. In this paper, some of the above families of advanced formable and high strength steels with micro-alloying additions, utilized in the automotive industry will be discussed.

  14. Advanced metallic structural materials and a new role for microalloyed steels

    International Nuclear Information System (INIS)

    Korchynsky, M.

    2004-01-01

    The recent worldwide surge of steel consumption, mainly of low-strength carbon grades, has created raw-materials shortages and price increases. These supply-demand strains could be relaxed by satisfying engineering needs with less steel. However, materials used for such a substitution must combine high weight reducing potential with low cost. Microalloyed (MA) steels are cost-effective substitutes, since their high strength is the result of grain refinement and precipitation hardening. These two strengthening mechanisms are developed by the interaction of micro-additives: niobium or vanadium with the deformation occurring during hot rolling followed by cooling. The physical metallurgy of these phenomena is discussed in the paper. The optimum alloy design of MA steels combines superior properties with lowest processing cost. In many applications, the versatility and adaptability of vanadium steels provides an economic advantage. The monetary value of weight production is sufficient to increase the profitability of steel makers and to lower the material cost to steel users. This 'win-win' situation is financed by the elimination of efforts spent in producing inefficient steel, yielding an increase in wealth formation. The gain acceptance of substitution by the consumer, a long-term strategic plan is needed to be implemented by the beneficiaries - both steel producers and steel users. The successful substitution is of importance to the national economy, resources and energy conservation, and the environment. Since microalloyed steels, used as a replacement for carbon steels, offer low cost weight savings, they deserve to be classified as advanced structural materials. (author)

  15. The Effects of Finish Rolling Temperature and Niobium Microalloying on the Microstructure and Properties of a Direct Quenched High-Strength Steel

    Directory of Open Access Journals (Sweden)

    Kaijalainen A.

    2017-06-01

    Full Text Available This paper comprehends the effects of finish rolling temperature (FRT and Nb-microalloying on the microstructural evolution and resultant properties of a low carbon direct quenched steel in the yield strength category of ≥900 MPa. Results indicate that a decrease in FRT close to Ar3 temperature significantly influenced the microstructure following phase transformation, especially at the subsurface (~50-400 μm of the rolled strip. On decreasing the FRT, the subsurface microstructure revealed a fine mixture of ferrite and bainite obviously as a result of strain-induced transformation, whereas the structure at the centreline remained essentially martensitic. Further, Nb-microalloying promoted the formation of ferrite and bainite even at higher FRTs, thus influencing the mechanical properties. The microstructures of the hot-rolled strips were further corroborated with the aid of CCT diagrams.

  16. Development of Microalloyed Steels for The Oil and Gas Industry

    Science.gov (United States)

    Henein, H.; Ivey, D. G.; Luo, J.; Wiskel, J. B.

    Microalloying, in combination with thermomechanical controlled processing (TMCP), is a cost effective method of producing steels for a wide range of applications where improved mechanical properties, namel y strength, formability and toughness coupled with weldability, are required. This paper reviews the efforts undertaken at the University of Alberta aimed at improving the above mentioned mechanical properties in microalloyed steels used in the transmission of oil and gas (i.e., pipelines). Topics that will be reviewed include the characterization of precipitates, the effect of processing conditions on precipitate evolution, and the effect of pipe forming and subsequent low temperature heat treatment on tensile behaviour and the use of Genetic Algorithm optimization of the laminar cooling system to produce a uniform through thickness microstructure.

  17. Microalloying with Cd of Antifriction Sn-Sb-Cu Alloys

    Directory of Open Access Journals (Sweden)

    Cinca Ionel Lupinca

    2012-09-01

    Full Text Available In the case of bimetallic sliding linings with superior technological characteristics, the use of an antifriction ally is imposed an alloy of the type Sn-Sb-Cu, which possesses a high adherence to the steel stand and a high durability in exploitation. For this reason we use the microalloying of the antifriction alloy with cadmium. The microalloying with Cd of antifriction alloys Sn-Sb-Cu determines an increase of the adhesion property of the antifriction alloy on the steel stand. The steel stand is previously subjected to a process of degreasing with ZnCl2 and washing so that is can later be subjected to a thermal-chemical treatment of tinning.

  18. Electrochemical Reduction of Oxygen on Anthraquinone/Carbon Nanotubes Nanohybrid Modified Glassy Carbon Electrode in Neutral Medium

    Directory of Open Access Journals (Sweden)

    Zheng Gong

    2013-01-01

    Full Text Available The electrochemical behaviors of monohydroxy-anthraquinone/multiwall carbon nanotubes (MHAQ/MWCNTs nanohybrid modified glassy carbon (MHAQ/MWCNTs/GC electrodes in neutral medium were investigated; also reported was their application in the electrocatalysis of oxygen reduction reaction (ORR. The resulting MHAQ/MWCNTs nanohybrid was characterized by scanning electron microscope (SEM and transmission electron microscope (TEM. It was found that the ORR at the MHAQ/MWCNTs/GC electrode occurs irreversibly at a potential about 214 mV less negative than at a bare GC electrode in pH 7.0 buffer solution. Cyclic voltammetric and rotating disk electrode (RDE techniques indicated that the MHAQ/MWCNTs nanohybrid has high electrocatalytic activity for the two-electron reduction of oxygen in the studied potential range. The kinetic parameters of ORR at the MHAQ/MWCNTs nanohybrid modified GC electrode were also determined by RDE and EIS techniques.

  19. Fatigue behaviour of friction welded medium carbon steel and austenitic stainless steel dissimilar joints

    International Nuclear Information System (INIS)

    Paventhan, R.; Lakshminarayanan, P.R.; Balasubramanian, V.

    2011-01-01

    Research highlights: → Fusion welding of dissimilar metals is a problem due to difference in properties. → Solid state welding process such as friction welding is a solution for the above problem. → Fatigue life of friction welded carbon steel and stainless steel joints are evaluated. → Effect of notch on the fatigue life of friction welded dissimilar joints is reported. → Formation of intermetallic is responsible for reduction in fatigue life of dissimilar joints. -- Abstract: This paper reports the fatigue behaviour of friction welded medium carbon steel-austenitic stainless steel (MCS-ASS) dissimilar joints. Commercial grade medium carbon steel rods of 12 mm diameter and AISI 304 grade austenitic stainless steel rods of 12 mm diameter were used to fabricate the joints. A constant speed, continuous drive friction welding machine was used to fabricate the joints. Fatigue life of the joints was evaluated conducting the experiments using rotary bending fatigue testing machine (R = -1). Applied stress vs. number of cycles to failure (S-N) curve was plotted for unnotched and notched specimens. Basquin constants, fatigue strength, fatigue notch factor and notch sensitivity factor were evaluated for the dissimilar joints. Fatigue strength of the joints is correlated with microstructure, microhardness and tensile properties of the joints.

  20. Extension of equilibrium formation criteria to metastable microalloys

    International Nuclear Information System (INIS)

    Kaufmann, E.N.; Vianden, R.; Chelikowsky, J.R.; Phillips, J.C.

    1977-01-01

    Metastable microalloys of 25 metallic elements with beryllium have been prepared by ion implantation. The injected atoms have been found to occupy one of three sites available in the solvent lattice. A modified Laudau-Ginsburg expansion using bulk alloy variables proposed by Miedema is completely successful in predicting the observed metastable-site preferences and indicates a broader applicability of these variables than was heretofore anticipated

  1. Carbon dioxide as working fluid for medium and high-temperature concentrated solar thermal systems

    Directory of Open Access Journals (Sweden)

    Van Duong

    2014-03-01

    Full Text Available This paper explores the benefits and drawbacks of using carbon dioxide in solar thermal systems at medium and high operating temperatures. For medium temperatures, application of CO2 in non-imaging-optics based compound parabolic concentrators (CPC combined with evacuated-tube collectors is studied. These collectors have been shown to obtain efficiencies higher than 40% operating at around 200℃ without the need of tracking. Validated numerical models of external compound parabolic concentrators (XCPCs are used to simulate their performance using CO2 as working fluid. For higher temperatures, a mathematical model is implemented to analyze the operating performance of a parabolic trough solar collector (PTC using CO2 at temperatures between 100℃ and 600℃.

  2. Microstructure and Mechanical Properties of Austempered Medium-Carbon Spring Steel

    Science.gov (United States)

    Kim, Seong Hoon; Kim, Kwan-Ho; Bae, Chul-Min; Lee, Jae Sang; Suh, Dong-Woo

    2018-03-01

    Changes in microstructure and mechanical properties of medium-carbon spring steel during austempering were investigated. After austempering for 1 h at 290 °C or 330 °C, the bainite transformation stabilized austenite, and microstructure consisting of bainitic ferrite and austenite could be obtained after final cooling; the retained austenite fraction was smaller in the alloy austempered at 290 °C because carbon redistribution between bainitic ferrite and austenite slowed as the temperature decreased, and thereby gave persistent driving force for the bainite transformation. The products of tensile strength and reduction of area in the austempered alloy were much larger in the austempered steel than in quenched and tempered alloy, mainly because of significant increase in reduction of area in austempered alloy.

  3. Multiphase Microstructure in a Metastability-Assisted Medium Carbon Alloy Steel

    Science.gov (United States)

    Liu, Cheng; Cui, Xixi; Yang, Chen

    2018-05-01

    A medium carbon alloy steel is processed by austenizing at 900 °C for 30 min, then rapid quenching into a patented quenching liquid and holding at 170 °C for 5 min, finally isothermally holding at 250 °C for different times. The morphology and mechanical properties are performed by using optical microscopy and scanning electron microscopy. A multiphase microstructure characterized by a mixture of lenticular prior martensite (PM), fine needle bainitic ferrite and filmy retained austenite (RA) is obtained. It is found that the PM formed firstly upon quenching can accelerate the subsequent bainitic transformation and promote refinement of multiphase colonies. The results show that an optimum mechanical property of a 4000.9 MPa bending strength and a 2030 MPa tensile strength is achieved at 250 °C for 120 min, which is attributed to the multiphase microstructural characteristics and a high product of the volume fraction of RA and the carbon content of austenite.

  4. Characteristics of polyaniline electrosynthesized in propylene carbonate medium in the presence of di- and trichloroacetic acids

    Directory of Open Access Journals (Sweden)

    Venancio Everaldo C.

    2001-01-01

    Full Text Available In the present work the characterization of polyaniline electrosynthesized in propylene carbonate medium in the presence of di- and trichloroacetic acids was performed using different techniques. The electrochemical response by cyclic voltammetry showed redox processes due to the formation of polaron and bipolaron and polymer degradation. The characterization by infrared and UV-visible spectroscopies indicated that the polymers are in the emeraldine salt form with perchlorate anions incorporated. The films produced with both acids in propylene carbonate media presented a compact morphology as observed by scanning electron microscopy. By testing the polyaniline film produced in selected conditions in a lithium battery environment it was found that it presents a high coulombic efficiency, promising for battery applications.

  5. Computing the carbonate chemistry of the coral calcifying medium and its response to ocean acidification.

    Science.gov (United States)

    Raybaud, Virginie; Tambutté, Sylvie; Ferrier-Pagès, Christine; Reynaud, Stéphanie; Venn, Alexander A; Tambutté, Éric; Nival, Paul; Allemand, Denis

    2017-07-07

    Critical to determining vulnerability or resilience of reef corals to Ocean Acidification (OA) is a clearer understanding of the extent to which corals can control carbonate chemistry in their Extracellular Calcifying Medium (ECM) where the CaCO 3 skeleton is produced. Here, we employ a mathematical framework to calculate ECM aragonite saturation state (Ω arag.(ECM) ) and carbonate system ion concentration using measurements of calcification rate, seawater characteristics (temperature, salinity and pH) and ECM pH (pH (ECM) ). Our calculations of ECM carbonate chemistry at current-day seawater pH, indicate that Ω arag.(ECM) ranges from ∼10 to 38 (mean 20.41), i.e. about 5 to 6-fold higher than seawater. Accordingly, Dissolved Inorganic Carbon (DIC) and Total Alkalinity (TA) were calculated to be around 3 times higher in the ECM than in seawater. We also assessed the effects of acidification on ECM chemical properties of the coral Stylophora pistillata. At reduced seawater pH our calculations indicate that Ω arag.(ECM) remains almost constant. DIC (ECM) and TA (ECM) gradually increase as seawater pH declines, reaching values about 5 to 6-fold higher than in seawater, respectively for DIC and TA. We propose that these ECM characteristics buffer the effect of acidification and explain why certain corals continue to produce CaCO 3 even when seawater chemistry is less favourable. Copyright © 2017 Elsevier Ltd. All rights reserved.

  6. Influence of Heat Treatments on the Corrosion Resistance of Medium -Carbon Steel using Sulfuric Spring Water

    Directory of Open Access Journals (Sweden)

    Ikhlas Basheer

    2015-02-01

    Full Text Available The corrosion is one of the important problems that may be occur to the parts of machinery and equipment after manufactured and when used as a result of exposure to corrosive media. Plain-carbon steel is considered as one of the most common minerals used in industrial applications. Some of heat treatments can have direct effect on the corrosion rate of steel by building up galvanic corrosion cells between its microscopic phases. Therefore, to adopt one of kinds of the plain-carbon steel and the most commonly used in industry to be study subject, that is medium carbon steel and took samples of this steel has been treated thermally in three methods which the normalising, annealing, and hardening .The corrosive media used in the research is Sulfuric Spring, it contains many chemical compounds to show its influence on the corrosion of steel. The weight loss method is used to determine corrosion rate and to compare between the results obtained, show that the greatest corrosion resistance of the annealed steel and the corrosion resistance of the hardened steel is the lowest while the corrosion  resistance of the normalised steel is in-between them.         Calcium carbonate was formed on the metal surface which acts as an isolating layer which decrease corrosion rate with time

  7. Fluid phase equilibria during propylene carbonate synthesis from propylene oxide in carbon dioxide medium

    DEFF Research Database (Denmark)

    Gharnati, Loubna; Musko, Nikolai; Jensen, Anker Degn

    2013-01-01

    -cyclic guanidinium bromide on SBA-15 (HEPCGBr/SBA-15) as catalyst in the absence of any co-catalyst. It was found that the yield was strongly dependent on the amount of CO2 added to the system and that the phase behavior strongly changes along the reaction pathway. The Cubic-Plus-Association (CPA) equation of state...... was used to predict the phase behavior during the reaction and the number and composition of coexisting phases in the multicomponent reaction system were determined. In accordance with the experimental data, the maximum conversion was achieved in the transition region between the two- and the one-phase...... region where a CO2-expanded reactant/product phase (larger volume due to the dissolution of carbon dioxide in the liquid phase) is present. Optimal conditions for performing the reaction have been derived which requires consideration not only of the phase behavior of the starting phase but also...

  8. Evaluating Strengthening and Impact Toughness Mechanisms for Ferritic and Bainitic Microstructures in Nb, Nb-Mo and Ti-Mo Microalloyed Steels

    Directory of Open Access Journals (Sweden)

    Gorka Larzabal

    2017-02-01

    Full Text Available Low carbon microalloyed steels show interesting commercial possibilities by combining different “micro”-alloying elements when high strength and low temperature toughness properties are required. Depending on the elements chosen for the chemistry design, the mechanisms controlling the strengths and toughness may differ. In this paper, a detailed characterization of the microstructural features of three different microalloyed steels, Nb, Nb-Mo and Ti-Mo, is described using mainly the electron backscattered diffraction technique (EBSD as well as transmission electron microscopy (TEM. The contribution of different strengthening mechanisms to yield strength and impact toughness is evaluated, and its relative weight is computed for different coiling temperatures. Grain refinement is shown to be the most effective mechanism for controlling both mechanical properties. As yield strength increases, the relative contribution of precipitation strengthening increases, and this factor is especially important in the Ti-Mo microalloyed steel where different combinations of interphase and random precipitation are detected depending on the coiling temperature. In addition to average grain size values, microstructural heterogeneity is considered in order to propose a new equation for predicting ductile–brittle transition temperature (DBTT. This equation considers the wide range of microstructures analyzed as well as the increase in the transition temperature related to precipitation strengthening.

  9. Ukrainian brown-coal tars recovered at low-temperature carbonization with solid heating medium

    Energy Technology Data Exchange (ETDEWEB)

    Kuznetsov, V I; Govorova, R P; Fadeicheva, A G; Kigel, T B; Chernykh, M K

    1955-01-01

    Three samples of tar were recovered in the laboratory from brown coals carbonized at 375/sup 0/ to 456/sup 0/ +- 25/sup 0/ in a retort with inner heating by solid circulating medium, namely, semicoke (ratio: 4 or 3:1) first heated to 700/sup 0/. One comparative (parallel) experiment was carried out in a retort with inner heating by inert gases entering the retort at 580/sup 0/ to 600/sup 0/ and leaving it at 115/sup 0/ to 120/sup 0/. The tars that were recovered from the retort with the solid heating medium contained a high percentage of coal dust and moisture, which were separated from the tars in supercentrifuges (15,000 rpm). Four samples of cleaned tars were fractionated in a Cu flask with a 2-ball fractional column. The tars from the retort with the solid-heating medium are characterized by increased yield of the petroleum-ether fraction (16.3 or 19.3%) and decreased yield of the paraffin fraction (15.1 to 21.2%) in comparison with those of tar from the retort with gas heating (5.9% of the petroleum ether fraction and 36.5% of paraffin fraction). The yield of paraffin from the paraffin fraction also decreased from 90.6% to 62.6-74.3%. This result shows that in the first case the carbonized products were cracked to a higher degree than those from the retort with gas heating. In raw phenols recovered from fractions of investigated tars, the yield of the phenol-cresol fraction (182/sup 0/ to 204/sup 0/) decreased from 25.9% to 13.0-18.9%.

  10. Passivation of Cu-Zn alloy on low carbon steel electrodeposited from a pyrophosphate medium

    Science.gov (United States)

    Yavuz, Abdulcabbar; Yakup Hacıibrahimoğlu, M.; Bedir, Metin

    2018-01-01

    The motivation of this study is to understand whether zinc-based alloy also has a passivation behaviour similar to zinc itself. Cu-Zn alloys were electrodeposited potentiostatically from a pyrophosphate medium on a carbon steel electrode and their corrosion behaviours were studied. Pt and carbon steel electrodes were used in order to examine the corrosion/passivation behaviour of bare Cu, bare Zn and Cu-Zn alloy coatings. The passivation behaviour of all brass-modified electrodes having Zn content between 10% and 100% was investigated. The growth potential affects the morphology and structure of crystals. The brass coatings are more porous than their pure components. The crystalline structure of Cu-Zn alloys can be obtained by changing the deposition potential. The zinc content in brass increases when the deposition voltage applied decreases. However, the growth potential and the ratio of zinc in brass do not affect the passivation behaviour of the resulting alloys. The coatings obtained by applying different growth potentials were immersed in tap water for 24 h to compare their corrosion behaviours with carbon steel having pitting formation.

  11. The Influence of Vanadium on Ferrite and Bainite Formation in a Medium Carbon Steel

    Science.gov (United States)

    Sourmail, T.; Garcia-Mateo, C.; Caballero, F. G.; Cazottes, S.; Epicier, T.; Danoix, F.; Milbourn, D.

    2017-09-01

    The influence of vanadium additions on transformation kinetics has been investigated in a medium carbon forging steel. Using dilatometry to track transformation during continuous cooling or isothermal transformation, the impact of vanadium on both ferrite-pearlite and bainite has been quantified. Transmission electron microscopy and atom probe tomography have been used to establish whether vanadium was present in solid solution, or as clusters and precipitates. The results show that vanadium in solid solution has a pronounced retarding influence on ferrite-pearlite formation and that, unlike in the case of niobium, this effect can be exploited even during relatively slow cooling. The influence on bainite transformation was found to depend on temperature; an explanation in terms of the effect of vanadium on heterogeneous nucleation is tentatively proposed.

  12. Chip formation in turning S45C medium carbon steel in cryogenic conditions

    Directory of Open Access Journals (Sweden)

    Jaharah A. Ghani

    2017-09-01

    Full Text Available This paper presents the tribology issue regarding the chip formation in machining medium carbon steel (S45C using a coated and uncoated carbide tools. The machining parameters under investigation were cutting speed, feed rate, and depth of cut under dry and cryogenic cutting condition using coated and uncoated carbide tools. The chip shape was largely depended on the combination of machining parameters, especially at high depth of cut and feed rate; the favorable chip was produced. Larger value of shear angle results in smaller shear plane area that provides benefits of lower cutting force needed to shear off the chips and lower cutting temperature being generated during the machining process.

  13. Effect of Nitridation Time on the Surface Hardness of Medium Carbon Steels (AISI 1045)

    International Nuclear Information System (INIS)

    Setyo Atmojo; Tjipto Sujitno; Sukidi

    2003-01-01

    It has been investigated the effect of nitridation time on the surface hardness of medium carbon steels (AISI 1045). Parameters determining to the results were flow rate of the nitrogen gas, temperature and time. In this experiments, sample having diameter of 15 mm, thick 2 mm placed in tube of glass with diameter 35 mm heated 550 o C, flow rate and temperature were kept constants, 100 cc/minutes and 550 o C respectively, while the time were varied from 5, 10, 20 and 30 hours. It was found, that for the nitridation time of 5, 10, 20, and 30 hours, the surface hardness increased from 145 VHN to, 23.7, 296.8, 382.4 and 426.1 VHN, respectively. (author)

  14. Selection of inactivation medium for fungal spores in clinical wastes by supercritical carbon dioxide.

    Science.gov (United States)

    Noman, Efaq; Norulaini Nik Ab Rahman, Nik; Al-Gheethi, Adel; Nagao, Hideyuki; Talip, Balkis A; Ab Kadir, Omar

    2018-05-21

    The present study aimed to select the best medium for inactivation of Aspergillus fumigatus, Aspergillus spp. in section Nigri, A. niger, A. terreus var. terreus, A. tubingensis, Penicillium waksmanii, P. simplicissimum, and Aspergillus sp. strain no. 145 spores in clinical wastes by using supercritical carbon dioxide (SC-CO 2 ). There were three types of solutions used including normal saline, seawater, distilled water, and physiological saline with 1% of methanol; each solution was tested at 5, 10, and 20 mL of the water contents. The experiments were conducted at the optimum operating parameters of supercritical carbon dioxide (30 MPa, 75 °C, 90 min). The results showed that the inactivation rate was more effective in distilled water with the presence of 1% methanol (6 log reductions). Meanwhile, the seawater decreases inactivation rate more than normal saline (4.5 vs. 5.1 log reduction). On the other hand, the experiments performed with different volumes of distilled water (5, 10, and 20 mL) indicated that A. niger spores were completely inactivated with 10 mL of distilled water. The inactivation rate of fungal spores decreased from 6 to 4.5 log as the amount of distilled water increased from 10 to 20 mL. The analysis for the spore morphology of A. fumigatus and Aspergillus spp. in section Nigri using scanning electron microscopy (SEM) has revealed the role of temperature and pressure in the SC-CO 2 in the destruction of the cell walls of the spores. It can be concluded that the distilled water represent the best medium for inactivation of fungal spores in the clinical solid wastes by SC-CO 2 .

  15. Effect of Quenching Media on Mechanical Properties of Medium Carbon Steel 1030

    Directory of Open Access Journals (Sweden)

    Khansaa Dawood Salman

    2018-01-01

    Full Text Available This investigation aims to study the effect of quenching media (water, oil, Poly Vinyl Chloride PVC on mechanical properties of 1030 steel. The applications of this steel include machinery parts where strength and hardness are requisites. The steel is heated to about 950  and soaked for 1hr in electrical furnace and then quenched in different quenching medium such as water, oil and poly vinyl chloride. After heat treatment by quenching, the specimens are tempered at 250  for 1hr and then cooling in air. The mechanical properties of the specimens are determined by using universal tensile testing machine for tensile test, Vickers hardness apparatus for hardness testing, measuring the grain size of the phases and examine the microstructure of the specimens before and after heat-treatment. The results of this work showed that improving the mechanical properties of medium carbon 1030 steel, which is quenching by water gives the preferred results as the following: Quenching by water leads to increase σy, σu.t.s, K and hardness, but at the same time quenching by water leads to decrease E and n. Also the quenching by water and followed by tempering leads to improve the microstructure and decreasing (refining of the grain size of ferrite and pearlite phases of the steel used in this work.

  16. Optimization of carbon and nitrogen medium components for biomass production using non-Saccharomyces wine yeasts.

    Science.gov (United States)

    Schnierda, T; Bauer, F F; Divol, B; van Rensburg, E; Görgens, J F

    2014-05-01

    The impact of different nitrogen and carbon sources on biomass production of the non-Saccharomyces wine yeast species Lachancea thermotolerans, Metschnikowia pulcherrima and Issatchenkia orientalis was assessed. Using a molasses-based medium, yeast extract and corn steep liquor as well as ammonium sulphate and di-ammonium phosphate (DAP) as nitrogen sources were compared in shake-flask cultures. A medium with 20 g l⁻¹ sugar (diluted molasses) and 500 mg l⁻¹ total yeast assimilable nitrogen, from yeast extract, gave the highest biomass concentrations and yields. Invertase pretreatment was required for cultures of M. pulcherrima and I. orientalis, and respective biomass yields of 0.7 and 0.8 g g⁻¹ were achieved in aerobic bioreactor cultures. The absence of ethanol production suggested Crabtree-negative behaviour by these yeasts, whereas Crabtree-positive behaviour by L. thermotolerans resulted in ethanol and biomass concentrations of 5.5 and 11.1 g l⁻¹, respectively. Recent studies demonstrate that non-Saccharomyces yeasts confer positive attributes to the final composition of wine. However, optimal process conditions for their biomass production have not been described, thereby limiting commercial application. In this study, industrial media and methods of yeast cultivation were investigated to develop protocols for biomass production of non-Saccharomyces yeast starter cultures for the wine industry. © 2014 The Society for Applied Microbiology.

  17. The effect of double steps heat treatment on the microstructure of nanostructure bainitic medium carbon steels

    Science.gov (United States)

    Foughani, Milad; Kolahi, Alireza; Palizdar, Yahya

    2018-01-01

    Nowadays, Nano structure bainitic steel have attracted attention mostly because of its special mechanical properties such as high tensile strength, hardness, appropriate toughness and low manufacturing cost. The main concern for the mass production of this type of steels is prolong austempering process which increases the production costs as well as time. In this research, in order to accelerate the bainitic transformation and decrease the production time, a medium carbon steel has been prepared and two steps austempering process was employed to prevent the bainite laths thickening. The Samples were austenetized at 1000°C for 15 min and were kept in the salt bath between 1 - 12 hours at 290°C in one step and between 1 - 12 hours at the temperature range of 250°C - 300°C in two steps bainite transformation. The obtained micro structures were studied by the optical and scanning electron microscopy (FESEM) and the mechanical properties were investigated by using tensile and hardness tests. The results show that the two steps austempering process and lower carbon concentration lead to lower austempering time as well as the formation of more stable retained austenite and nanostructured bainite lath which results in higher mechanical properties.

  18. Voltammetric studies on the electrochemical determination of methylmercury in chloride medium at carbon microelectrodes

    Energy Technology Data Exchange (ETDEWEB)

    Ribeiro, F. [Centro de Electroquimica e Cinetica da Universidade de Lisboa, Departamento de Quimica e Bioquimica, Faculdade de Ciencias, Universidade de Lisboa, Campo Grande, Ed. C8, 1749-016 Lisbon (Portugal); Neto, M.M.M. [Centro de Electroquimica e Cinetica da Universidade de Lisboa, Departamento de Quimica e Bioquimica, Faculdade de Ciencias, Universidade de Lisboa, Campo Grande, Ed. C8, 1749-016 Lisbon (Portugal) and Departamento de Quimica Agricola e Ambiental, Instituto Superior de Agronomia, Tapada da Ajuda, 1349-017 Lisbon (Portugal)]. E-mail: mm.neto@netcabo.pt; Rocha, M.M. [Centro de Electroquimica e Cinetica da Universidade de Lisboa, Departamento de Quimica e Bioquimica, Faculdade de Ciencias, Universidade de Lisboa, Campo Grande, Ed. C8, 1749-016 Lisbon (Portugal); Fonseca, I.T.E. [Centro de Electroquimica e Cinetica da Universidade de Lisboa, Departamento de Quimica e Bioquimica, Faculdade de Ciencias, Universidade de Lisboa, Campo Grande, Ed. C8, 1749-016 Lisbon (Portugal)

    2006-10-10

    Electroanalytical techniques have been used to determine methylmercury at low levels in environmental matrices. The electrochemical behaviour of methylmercury at carbon microelectrodes in a hydrochloric acid medium using cyclic, square wave and fast-scan linear-sweep voltammetric techniques has been investigated. The analytical utility of the methylmercury reoxidation peak has been explored, but the recorded peak currents were found to be poorly reproducible. This is ascribed to two factors: the adsorption of insoluble chloromercury compounds on the electrode surface, which appears to be an important contribution to hinder the voltammetric signal of methylmercury; and the competition between the reoxidation of the methylmercury radical and its dimerization reaction, which limits the reproducibility of the methylmercury peak. These problems were successfully overcome by adopting the appropriate experimental conditions. Fast-scan rates were employed and an efficient electrochemical regeneration procedure of the electrode surface was achieved, under potentiostatic conditions in a mercury-free solution containing potassium thiocyanate-a strong complexing agent. The influence of chloride ion concentration was analysed. Interference by metals, such as lead and cadmium, was considered. Calibration plots were obtained in the micromolar and submicromolar concentration ranges, allowing the electrochemical determination of methylmercury in trace amounts. An estuarine water sample was analysed using the new method with a glassy carbon microelectrode.

  19. The carbon consumption pattern of the spoilage yeast Brettanomyces bruxellensis in synthetic wine-like medium.

    Science.gov (United States)

    Smith, Brendan D; Divol, Benoit

    2018-08-01

    The wine matrix contains limited carbon compounds to sustain microbial life. Brettanomyces bruxellensis is one of very few yeast species that has adapted to this environment. Indeed, the presence of growth-inhibiting compounds and conditions do not prevent its proliferation. Literature regarding the nutritional requirements of this yeast is surprisingly poor, given the observation that B. bruxellensis produces biomass with apparently less nutrients than other yeasts. In this study, various carbon sources were screened in a synthetic wine medium, under anaerobic and semi-aerobic growth conditions, in order to determine which compounds B. bruxellensis assimilates. Slight differences were observed between strains but overall, B. bruxellensis produced biomass from limited nutrients consumed in a specific order regardless of the oxygen conditions. Upon initial consumption of the simple sugars, B. bruxellensis was able to remain viable, by concurrently utilising ethanol (only in the presence of oxygen) and malic acid. Although initially beneficial, oxygen was found detrimental in the long term. Formation of volatile phenols occurred during the consumption of the sugars but not as a mechanism to help correct the redox imbalance. The study confirms that B. bruxellensis is able to survive using limited amount of nutrients, making this yeast a challenge for winemakers. Copyright © 2017 Elsevier Ltd. All rights reserved.

  20. Voltammetric studies on the electrochemical determination of methylmercury in chloride medium at carbon microelectrodes

    International Nuclear Information System (INIS)

    Ribeiro, F.; Neto, M.M.M.; Rocha, M.M.; Fonseca, I.T.E.

    2006-01-01

    Electroanalytical techniques have been used to determine methylmercury at low levels in environmental matrices. The electrochemical behaviour of methylmercury at carbon microelectrodes in a hydrochloric acid medium using cyclic, square wave and fast-scan linear-sweep voltammetric techniques has been investigated. The analytical utility of the methylmercury reoxidation peak has been explored, but the recorded peak currents were found to be poorly reproducible. This is ascribed to two factors: the adsorption of insoluble chloromercury compounds on the electrode surface, which appears to be an important contribution to hinder the voltammetric signal of methylmercury; and the competition between the reoxidation of the methylmercury radical and its dimerization reaction, which limits the reproducibility of the methylmercury peak. These problems were successfully overcome by adopting the appropriate experimental conditions. Fast-scan rates were employed and an efficient electrochemical regeneration procedure of the electrode surface was achieved, under potentiostatic conditions in a mercury-free solution containing potassium thiocyanate-a strong complexing agent. The influence of chloride ion concentration was analysed. Interference by metals, such as lead and cadmium, was considered. Calibration plots were obtained in the micromolar and submicromolar concentration ranges, allowing the electrochemical determination of methylmercury in trace amounts. An estuarine water sample was analysed using the new method with a glassy carbon microelectrode

  1. Project of Carbon Capture in Small and Medium Farms in the Brunca Region, Costa Rica

    Directory of Open Access Journals (Sweden)

    Gilmar Navarrete

    2013-12-01

    Full Text Available The Clean Development Mechanism (CDM of the Kyoto Protocol, allows the non Annex 1 countries to receive projects that contribute to reducing greenhouse gas emissions and sustainable development in developing countries. The CDM, since its inception, has issued credits equivalent to 1.434.737.562 tons of CO2, distributed across 7.450 projects around the world, from 15 different sectors. Sectors 14 that allow forestry projects (such as reforestation and afforestation have registered 53 projects to date; 19 of which are in Latin America. Nevertheless, the contribution of this sector currently represents less than 1% of CDM Certificates of Emissions Reduction (CERs issued. In September 2013, through their National Forestry Financing Fund (FONAFIFO, Costa Rica registered their first CDM project with the United Nations Framework Convention on Climate Change (UNFCCC, after having complied with all the project cycle processes. The project, known as "Carbon Sequestration in Small and Medium Farms, Brunca Region, Costa Rica" was a project executed by FONAFIFO under their Environmental Services Payment Program. This project was developed in Pérez Zeledón, San José, Costa Rica in partnership with the Cooperative Corporation CoopeAgri RL. The total goal of the project is to reduce the greenhouse gas emission by 176,050 ton of CO2-e, in a period of 20 years and commercialize the CERs in the regulated carbon market.

  2. Medium-scale carbon nanotube thin-film integrated circuits on flexible plastic substrates.

    Science.gov (United States)

    Cao, Qing; Kim, Hoon-sik; Pimparkar, Ninad; Kulkarni, Jaydeep P; Wang, Congjun; Shim, Moonsub; Roy, Kaushik; Alam, Muhammad A; Rogers, John A

    2008-07-24

    The ability to form integrated circuits on flexible sheets of plastic enables attributes (for example conformal and flexible formats and lightweight and shock resistant construction) in electronic devices that are difficult or impossible to achieve with technologies that use semiconductor wafers or glass plates as substrates. Organic small-molecule and polymer-based materials represent the most widely explored types of semiconductors for such flexible circuitry. Although these materials and those that use films or nanostructures of inorganics have promise for certain applications, existing demonstrations of them in circuits on plastic indicate modest performance characteristics that might restrict the application possibilities. Here we report implementations of a comparatively high-performance carbon-based semiconductor consisting of sub-monolayer, random networks of single-walled carbon nanotubes to yield small- to medium-scale integrated digital circuits, composed of up to nearly 100 transistors on plastic substrates. Transistors in these integrated circuits have excellent properties: mobilities as high as 80 cm(2) V(-1) s(-1), subthreshold slopes as low as 140 m V dec(-1), operating voltages less than 5 V together with deterministic control over the threshold voltages, on/off ratios as high as 10(5), switching speeds in the kilohertz range even for coarse (approximately 100-microm) device geometries, and good mechanical flexibility-all with levels of uniformity and reproducibility that enable high-yield fabrication of integrated circuits. Theoretical calculations, in contexts ranging from heterogeneous percolative transport through the networks to compact models for the transistors to circuit level simulations, provide quantitative and predictive understanding of these systems. Taken together, these results suggest that sub-monolayer films of single-walled carbon nanotubes are attractive materials for flexible integrated circuits, with many potential areas of

  3. Effect of titanium as a microalloying addition in the apparent activation energy of medium carbon steels. Influencia del titanio como microaleante en la energia de activacion aparente de los aceros con contenidos medios de carbono

    Energy Technology Data Exchange (ETDEWEB)

    Penalba, F.; Carsi, M. (INASMET, San Sebastian (Spain))

    1994-01-01

    Static recrystallization kinetics of five micro alloyed steels containing from 0.003% to 0.039 wt% Ti have been studied using torsion tests. A different behaviour has been appreciated when the titanium level is near 0.02 wt.%. The activation energy is 45% higher than that of steel without titanium. The results obtained using metallographic observation and softening methods has been compared, obtaining a good concordance in both cases. The energies of the recrystallization process have been studied and finally have been checked by alternative methods in the power law zone. The evolution of the recrystallization at various temperatures has been checked also, and the steel with the optimum titanium content has maintained a different behaviour. (Author) 16 refs.

  4. The Development of Lightweight Commercial Vehicle Wheels Using Microalloying Steel

    Science.gov (United States)

    Lu, Hongzhou; Zhang, Lilong; Wang, Jiegong; Xuan, Zhaozhi; Liu, Xiandong; Guo, Aimin; Wang, Wenjun; Lu, Guimin

    Lightweight wheels can reduce weight about 100kg for commercial vehicles, and it can save energy and reduce emission, what's more, it can enhance the profits for logistics companies. The development of lightweight commercial vehicle wheels is achieved by the development of new steel for rim, the process optimization of flash butt welding, and structure optimization by finite element methods. Niobium micro-alloying technology can improve hole expansion rate, weldability and fatigue performance of wheel steel, and based on Niobium micro-alloying technology, a special wheel steel has been studied whose microstructure are Ferrite and Bainite, with high formability and high fatigue performance, and stable mechanical properties. The content of Nb in this new steel is 0.025% and the hole expansion rate is ≥ 100%. At the same time, welding parameters including electric upsetting time, upset allowance, upsetting pressure and flash allowance are optimized, and by CAE analysis, an optimized structure has been attained. As a results, the weight of 22.5in×8.25in wheel is up to 31.5kg, which is most lightweight comparing the same size wheels. And its functions including bending fatigue performance and radial fatigue performance meet the application requirements of truck makers and logistics companies.

  5. The analysis of bainitic ferrite microstructure in microalloyed plate steels through quantitative characterization of intervariant boundaries

    Energy Technology Data Exchange (ETDEWEB)

    Kang, Singon, E-mail: sikang@mines.edu [Advanced Steel Processing and Products Research Center, Colorado School of Mines, Golden, CO 80401 (United States); Speer, John G.; Regier, Ryan W. [Advanced Steel Processing and Products Research Center, Colorado School of Mines, Golden, CO 80401 (United States); Nako, Hidenori [Advanced Steel Processing and Products Research Center, Colorado School of Mines, Golden, CO 80401 (United States); Materials Research Laboratory, Kobe Steel Ltd., Kobe, Hyogo 651-2271 (Japan); Kennett, Shane C. [Advanced Steel Processing and Products Research Center, Colorado School of Mines, Golden, CO 80401 (United States); Exponent Failure Analysis Associates, Menlo Park, CA 94025 (United States); Findley, Kip O. [Advanced Steel Processing and Products Research Center, Colorado School of Mines, Golden, CO 80401 (United States)

    2016-07-04

    Electron backscatter diffraction (EBSD) measurements were performed to investigate the bainitic ferrite microstructure in low-carbon, microalloyed steels with varying C and Mn contents. Fully austenitized samples were isothermally heat treated at temperatures ranging from 450 to 550 °C to form bainitic ferrite. The bainitic ferrite microstructures and boundary characteristics obtained from the EBSD measurements were analyzed based on an inferred Kurdjumov-Sachs (K-S) orientation relationship. The heat treated samples exhibit a microstructure composed of laths and the lath aspect ratio tends to increase at lower isothermal heat treatment temperatures. High fractions of boundary misorientation angles below 5° are observed, which are due to lath boundaries in the microstructure. Additionally, misorientations of approximately 7°, 53° and 60° are observed, which are related to the sub-block, packet, and block boundaries, respectively. With decreasing isothermal heat treatment temperature, there is an increase of block boundaries; these boundaries are intervariant boundaries between different blocks within a packet, most of which have the misorientation angle of 60°. The specimens with a higher carbon level contained increased length of block boundaries, whereas the addition of Mn moderated the dependence of block boundary length on the heat treatment temperature within the experimental temperature range. Meanwhile, the length of intervariant boundaries of both packet and sub-block character did not vary much with heat treatment temperature and alloy composition.

  6. Quantitative Analysis on Carbide Precipitation in V-Ti Microalloyed TRIP Steel Containing Aluminum

    Directory of Open Access Journals (Sweden)

    Fu Shiyu

    2016-01-01

    Full Text Available Introducing fine precipitates is an important way to enhance the properties of transformation-induced plasticity (TRIP steels. In present work, two V-Ti microalloyed TRIP steels containing aluminum with different content were compared. The average size, size distribution and numbers of vanadium-titanium carbides in samples cold rolled, quenched after being held at 800°C and quenched after intercritical annealing at 800°C and being held at bainitic isothermal transformation temperature of 400°C were investigated by using the technique of carbon extraction replica, twin jet chemical polishing thinning and transmission electron microscopy. The carbides were identified to be (Ti,VC precipitates in steel A and VC in steel B respectively, precipitated mainly from ferrites grains. The average equivalent radius was 3~6nm. Comparison of the experimental results in A and B steel revealed low carbon diffusion rate caused by aluminum inhibited the coarsening of vanadium-titanium carbides. The experimental results also showed that VC carbides dissolution occurred during the intercritical annealing at 800°C.

  7. Effects of niobium addition on the structure and properties of medium and high carbon steels. v. 1,2

    International Nuclear Information System (INIS)

    Mei, P.R.

    1983-01-01

    An evaluation about the use of niobium in medium and high carbon steels, with ferritic-pearlitic structure, through the understanding of niobium actuaction mechanism in the structure, and consequently in the mechanical properties of those steels is done. (E.G.) [pt

  8. Carbon supported Pd-Sn and Pd-Ru-Sn nanocatalysts for ethanol electro-oxidation in alkaline medium

    CSIR Research Space (South Africa)

    Modibedi, RM

    2011-04-01

    Full Text Available Carbon supported Pd-Sn and Pd-Ru-Sn nanocatalysts were prepared by the chemical reduction method, using sodium borohydride and ethylene glycol mixture as the reducing agent. The catalytic activity towards ethanol electro-oxidation in alkaline medium...

  9. Medium carbon vanadium steels for closed die forging; Acos de medio carbono microligados ao vanadio para forjaria em matriz fechada

    Energy Technology Data Exchange (ETDEWEB)

    Jeszensky, Gabor; Plaut, Ronald Lesley

    1994-12-31

    This work analyses the medium carbon micro alloyed vanadium potential for closed die forged production. The steels reach the mechanical resistance requests during cooling after forging, eliminating the subsequent thermal treatment. Those steels also present good fatigue resistance and machinability. The industrial scale experiments are also reported 16 refs., 21 figs.

  10. Preliminary work of mangrove ecosystem carbon stock mapping in small island using remote sensing: above and below ground carbon stock mapping on medium resolution satellite image

    Science.gov (United States)

    Wicaksono, Pramaditya; Danoedoro, Projo; Hartono, Hartono; Nehren, Udo; Ribbe, Lars

    2011-11-01

    Mangrove forest is an important ecosystem located in coastal area that provides various important ecological and economical services. One of the services provided by mangrove forest is the ability to act as carbon sink by sequestering CO2 from atmosphere through photosynthesis and carbon burial on the sediment. The carbon buried on mangrove sediment may persist for millennia before return to the atmosphere, and thus act as an effective long-term carbon sink. Therefore, it is important to understand the distribution of carbon stored within mangrove forest in a spatial and temporal context. In this paper, an effort to map carbon stocks in mangrove forest is presented using remote sensing technology to overcome the handicap encountered by field survey. In mangrove carbon stock mapping, the use of medium spatial resolution Landsat 7 ETM+ is emphasized. Landsat 7 ETM+ images are relatively cheap, widely available and have large area coverage, and thus provide a cost and time effective way of mapping mangrove carbon stocks. Using field data, two image processing techniques namely Vegetation Index and Linear Spectral Unmixing (LSU) were evaluated to find the best method to explain the variation in mangrove carbon stocks using remote sensing data. In addition, we also tried to estimate mangrove carbon sequestration rate via multitemporal analysis. Finally, the technique which produces significantly better result was used to produce a map of mangrove forest carbon stocks, which is spatially extensive and temporally repetitive.

  11. Carbon-supported cubic CoSe2 catalysts for oxygen reduction reaction in alkaline medium

    International Nuclear Information System (INIS)

    Feng Yongjun; Alonso-Vante, Nicolas

    2012-01-01

    Highlights: ► Cubic CoSe 2 a non-precious metal electrocatalyst for oxygen reduction in KOH. ► The catalyst shows four-electron transfer pathway in overall reaction. ► Catalyst has higher methanol tolerance than commercial Pt/C catalyst. - Abstract: A Carbon-supported CoSe 2 nanocatalyst has been developed as an alternative non-precious metal electrocatalyst for oxygen reduction reaction (ORR) in alkaline medium. The catalyst was prepared via a surfactant-free route and its electrocatalytic activity for the ORR has been investigated in detail in 0.1 M KOH electrolyte at 25 °C using rotating disk electrode (RDE) and rotating ring-disk electrode (RRDE) techniques. The prepared catalyst showed promising catalytic activity towards ORR in a four-electron transfer pathway and higher tolerance to methanol compared to commercial Pt/C catalyst in 0.1 M KOH. To some extent, the increase of CoSe 2 loading on the electrode favors a faster reduction of H 2 O 2 intermediate to H 2 O.

  12. Low cycle fatigue behavior in a medium-carbon carbide-free bainitic steel

    Energy Technology Data Exchange (ETDEWEB)

    Kang, J. [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); Zhang, F.C., E-mail: zfc@ysu.edu.cn [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); Long, X.Y. [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); Lv, B. [College of Environmental and Chemical Engineering, Yanshan University, Qinhuangdao 066004 (China)

    2016-06-01

    In the paper, different morphologies of bainite were obtained through isothermal quenching at 320 °C and 395 °C in a medium-carbon carbide-free bainitic steel. The cyclic deformation mechanism was explored by using low cycle fatigue testing. The volume fraction of retained austenite was measured by X-ray diffraction and the space partitioning of the solute atoms was constructed by three-dimensional atom probe. Results showed that the fatigue life at 320 °C was always higher than that at 395 °C under low and high total strain amplitude. The cyclic softening at the early fatigue stage increased the plastic strain of the sample which was responsible for the reduction of the fatigue life at 395 °C. Strain-induced retained austenite to martensite contributed to initial cyclic hardening, but almost having no effect on the subsequent cyclic stable/softening behaviors. The finer bainitic ferrite sheaves obtained at 320 °C changed the small fatigue crack propagation direction and delayed the crack propagation rate, which was beneficial for the fatigue properties. In addition, the substitutional atoms did not redistribute between the retained austenite and bainitic ferrite before and after cyclic deformation.

  13. Influence of Austempering Heat Treatment on Microstructure and Mechanical Properties of Medium Carbon High Silicon Steel

    Science.gov (United States)

    Palaksha, P. A.; Ravishankar, K. S.

    2017-08-01

    In the present investigation, the influence of austempering heat treatment on the microstructure and mechanical properties of medium carbon high silicon steel was evaluated. The test specimens were machined from the as-received steel and were first austenitised at 900 °C for 45 minutes, followed by austempering heat treatment in salt bath at various temperatures 300 °C, 350 °C and 400 °C for a fixed duration of two hours, after that those specimens were air-cooled to room temperature. The characterization studies were carried out using optical microscope, scanning electron microscope (SEM) and x-ray diffractometer (XRD) and then correlated to the hardness and tensile properties. Results indicate that, the specimens austempered at lower temperature i.e. at 300 °C, which offered high hardness, tensile strength and lower ductility (1857 MPa and 13.3 %) due to the presence of acicular bainite i.e. lower bainite and also some martensite in the microstructure. At 350 °C, reduction in the tensile strength and hardness was observed, but comparatively higher ductility, which was favored by the presence of bainite laths i.e. upper bainitic structure along with higher retained austenite content. Finally at 400 °C, reduction in both ductility and tensile strength was observed, which is due to the precipitation of carbides between the banite laths, however good strain hardening response was observed at austempering temperatures of 350 °C and 400 °C.

  14. Measurement of labile copper in wine by medium exchange stripping potentiometry utilising screen printed carbon electrodes.

    Science.gov (United States)

    Clark, Andrew C; Kontoudakis, Nikolaos; Barril, Celia; Schmidtke, Leigh M; Scollary, Geoffrey R

    2016-07-01

    The presence of copper in wine is known to impact the reductive, oxidative and colloidal stability of wine, and techniques enabling measurement of different forms of copper in wine are of particular interest in understanding these spoilage processes. Electrochemical stripping techniques developed to date require significant pretreatment of wine, potentially disturbing the copper binding equilibria. A thin mercury film on a screen printed carbon electrode was utilised in a flow system for the direct analysis of labile copper in red and white wine by constant current stripping potentiometry with medium exchange. Under the optimised conditions, including an enrichment time of 500s and constant current of 1.0μA, the response range was linear from 0.015 to 0.200mg/L. The analysis of 52 red and white wines showed that this technique generally provided lower labile copper concentrations than reported for batch measurement by related techniques. Studies in a model system and in finished wines showed that the copper sulfide was not measured as labile copper, and that loss of hydrogen sulfide via volatilisation induced an increase in labile copper within the model wine system. Copyright © 2016 Elsevier B.V. All rights reserved.

  15. Highly Uniform Carbon Nanotube Field-Effect Transistors and Medium Scale Integrated Circuits.

    Science.gov (United States)

    Chen, Bingyan; Zhang, Panpan; Ding, Li; Han, Jie; Qiu, Song; Li, Qingwen; Zhang, Zhiyong; Peng, Lian-Mao

    2016-08-10

    Top-gated p-type field-effect transistors (FETs) have been fabricated in batch based on carbon nanotube (CNT) network thin films prepared from CNT solution and present high yield and highly uniform performance with small threshold voltage distribution with standard deviation of 34 mV. According to the property of FETs, various logical and arithmetical gates, shifters, and d-latch circuits were designed and demonstrated with rail-to-rail output. In particular, a 4-bit adder consisting of 140 p-type CNT FETs was demonstrated with higher packing density and lower supply voltage than other published integrated circuits based on CNT films, which indicates that CNT based integrated circuits can reach to medium scale. In addition, a 2-bit multiplier has been realized for the first time. Benefitted from the high uniformity and suitable threshold voltage of CNT FETs, all of the fabricated circuits based on CNT FETs can be driven by a single voltage as small as 2 V.

  16. Wear Behavior of Medium Carbon Steel with Biomimetic Surface Under Starved Lubricated Conditions

    Science.gov (United States)

    Zhang, Zhihui; Shao, Feixian; Liang, Yunhong; Lin, Pengyu; Tong, Xin; Ren, Luquan

    2017-07-01

    Friction and wear under starved lubrication condition are both key life-related factors for mechanical performance of many structural parts. In this paper, different surface morphologies on medium carbon steel were fabricated using laser, inspired by the surface coupling effect of biological system. The friction and sliding wear behaviors of biomimetic specimens (characterized by convex and concave units on the specimen surface) were studied under starved lubrication condition. The stress distribution on different sliding surfaces under sliding friction was studied using finite element method. The results showed that the tribological performance of studied surfaces under starved lubrication condition depended not only on the surface morphology but also on the structure of biomimetic units below surface (subsurface structure). The friction coefficient of biomimetic surface was effectively reduced by the concave unit depth, while the refined microstructure with higher hardness led to the much better wear resistance. In addition to lubricant reserving and wear debris trapping effect derived from the surface concave morphology, it was believed that the well-formed subsurface structure of biomimetic units could carry much heavy loads against tribopair, which enhanced the function of surface topography and resulted in complementary lubrication in the wear contact area. The uniform stress distribution on the entire biomimetic surface also played an important role in stabilizing the friction coefficient and reducing the wear cracks.

  17. Effect of tempering on the microstructure and mechanical properties of a medium carbon bainitic steel

    Energy Technology Data Exchange (ETDEWEB)

    Kang, J. [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); Zhang, F.C., E-mail: zfc@ysu.edu.cn [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); National Engineering Research Center for Equipment and Technology of Cold Strip Rolling, Yanshan University, Qinhuangdao 066004 (China); Yang, X.W. [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); Lv, B. [College of Environmental and Chemical Engineering, Yanshan University, Qinhuangdao 066004 (China); Wu, K.M. [International Research Institute for Steel Technology, Wuhan University of Science and Technology, Wuhan 430081 (China); Materials Science and Metallurgy, University of Cambridge, Cambridge CB2 3QZ (United Kingdom)

    2017-02-16

    The effect of tempering on the microstructure and mechanical properties of a medium carbon bainitic steel has been investigated through optical microscopy, electron back-scattered diffraction, transmission electron microscopy and X-ray diffraction analyses. A nano-level microstructure containing plate-like bainitic ferrite and film-like retained austenite is obtained by isothermal transformation at Ms+10 °C followed by tempering within 240–450 °C. Results show that the sample tempered at 340 °C occupies the optimal balance of strength and toughness by maintaining a certain level of plasticity; samples tempered at 320 °C and 360 °C with low and high yield ratio come second. The microstructure of the steel is not sensitive to tempering temperatures before 360 °C. When the temperature is increased to 450 °C, the significantly coarsened bainitic ferrite plate and the occurrence of a small quantity of carbide precipitation account for its low toughness. The amount of retained austenite increases with the tempering temperature before 400 °C, followed by decreasing with further increase in the temperature. This behavior is related to the competition between retained austenite further transforming into bainite and decomposing into carbide during tempering.

  18. Stages of destruction and elastic compression of granular nanoporous carbon medium at high pressures

    International Nuclear Information System (INIS)

    Neklyudov, I.M.; Ledenyov, O.P.; Bobrova, N.B.; Chupikov, A.A.

    2015-01-01

    The granular nanoporous carbon medium, made of the cylindrical coal granules of the adsorbent of CKT-3, at an influence by the high pressures from 1 MPa to 3 GPa has been researched. The eight consecutive stages of the material's specific volume change, which is characterized by a certain dependence of the volume change on the pressure change, have been registered. It is shown that there is a linear dependence on the double log-log plot of the material's specific volume change on the pressure for an every stage of considered process. The two stages are clearly distinguished: a stage of material's mechanical destruction, and a stage of elastic compression of material without the disintegration of structure at a nano-scale. The hysteresis dependence of the material's specific volume change on the pressure change at the pressure decrease is observed. The small disperse coal dust particles jettisoning between the high pressure cell and the base plate was observed, resulting in the elastic stress reduction in relation to the small disperse coal dust particles volume. The obtained research data can be used to improve the designs of air filters for the radioactive chemical elements absorption at the NPP with the aims to protect the environment

  19. Effects of microalloying on hot-rolled and cold-rolled Q&P steels

    Science.gov (United States)

    Azevedo de Araujo, Ana Luiza

    Third generation advanced high strength steels (AHSS) have been a major focus in steel development over the last decade. The premise of these types of steel is based on the potential to obtain excellent combinations of strength and ductility with low-alloy compositions by forming mixed microstructures containing retained austenite (RA). The development of heat treatments able to achieve the desired structures and properties, such as quenching and partitioning (Q&P) steels, is driven by new requirements to increase vehicle fuel economy by reducing overall weight while maintaining safety and crashworthiness. Microalloying additions of niobium (Nb) and vanadium (V) in sheet products are known to provide strengthening via grain refinement and precipitation hardening and may influence RA volume fraction and transformation behavior. Additions of microalloying elements in Q&P steels have not been extensively studied to date, however. The objective of the present study was to begin to understand the potential roles of Nb and V in hot-rolled and cold-rolled Q&P steel. For that, a common Q&P steel composition was selected as a Base alloy with 0.2C-1.5Si-2.0Mn (wt. %). Two alloys with an addition of Nb (0.02 and 0.04 wt. %) and one with an addition of V (0.06 wt. %) to the Base alloy were investigated. Both hot-rolled and cold-rolled/annealed Q&P simulations were conducted. In the hot-rolled Q&P study, thermomechanical processing was simulated via hot torsion testing in a GleebleRTM 3500, and four coiling temperatures (CT) were chosen. Microstructural evaluation (including RA measurements via electron backscattered diffraction - EBSD) and hardness measurements were performed for all alloys and coiling conditions. The analysis showed that Nb additions led to overall refinement of the prior microstructure. Maximum RA fractions were measured at the 375 °C CT, and microalloying was associated with increased RA in this condition when compared to the Base alloy. A change in

  20. [Effects of straw returning combined with medium and microelements application on soil organic carbon sequestration in cropland.

    Science.gov (United States)

    Jiang, Zhen Hui; Shi, Jiang Lan; Jia, Zhou; Ding, Ting Ting; Tian, Xiao Hong

    2016-04-22

    A 52-day incubation experiment was conducted to investigate the effects of maize straw decomposition with combined medium element (S) and microelements (Fe and Zn) application on arable soil organic carbon sequestration. During the straw decomposition, the soil microbial biomass carbon (MBC) content and CO 2 -C mineralization rate increased with the addition of S, Fe and Zn, respectively. Also, the cumulative CO 2 -C efflux after 52-day laboratory incubation significantly increased in the treatments with S, or Fe, or Zn addition, while there was no significant reduction of soil organic carbon content in the treatments. In addition, Fe or Zn application increased the inert C pools and their proportion, and apparent balance of soil organic carbon, indicating a promoting effect of Fe or Zn addition on soil organic carbon sequestration. In contrast, S addition decreased the proportion of inert C pools and apparent balance of soil organic carbon, indicating an adverse effect of S addition on soil organic carbon sequestration. The results suggested that when nitrogen and phosphorus fertilizers were applied, inclusion of S, or Fe, or Zn in straw incorporation could promote soil organic carbon mineralization process, while organic carbon sequestration was favored by Fe or Zn addition, but not by S addition.

  1. Influence of viscosity of the medium on the disposition of carbon nanotubes anisotropic structures formation induced by electric field

    International Nuclear Information System (INIS)

    Yakovenko, O.S.; Matsuj, L.Yu.; Zhuravkov, O.V.; Vovchenko, L.D.

    2014-01-01

    To obtain carbon nanotubes (CNT)-polymer composites with anisotropic physical properties an electric field application can be used. This investigation considers factors of CNT anisotropic distribution formation induced by electric field and consideration is supported with experimental results where some factors were varied. In the article an influence of magnitude and type of electric field and time of processing by electric field on CNT anisotropic structures formation in polymer mediums of different viscosities (oil, epoxy resins) is investigated. The aim of this work was to examine the CNT structuration process induced by electric field in viscous mediums and to find out the most optimal conditions of preparation of polymer/carbon composite materials (CM) with specified distribution of carbon filler induced by electric field. Scoping on polymer/carbon CM structuration was conducted by optical microscopy method. It was found that the main factors during CNT network formation are the type and viscosity of polymer binder and applied electric field parameters. It was observed that for high viscous polymer CNT network formation is unfeasible even at high applied electric field strength. But also for low viscous medium at relatively low electric field strength the CNT network formation is complicated too. And it was seen from optical observation that a type of the polymer variation causes different response of network form under the same experimental conditions. These distinctions are considered in the article

  2. The odd-carbon medium-chain fatty triglyceride triheptanoin does not reduce hepatic steatosis.

    Science.gov (United States)

    Comhair, Tine M; Garcia Caraballo, Sonia C; Dejong, Cornelis H C; Lamers, Wouter H; Koehler, S Eleonore

    2017-02-01

    Non-alcoholic fatty-liver disease (NAFLD) is the hepatic manifestation of the metabolic syndrome. Previously, we showed that a high-protein diet minimized diet-induced development of fatty liver and even reversed pre-existing steatosis. A high-protein diet leads to amino-acid catabolism, which in turn causes anaplerosis of the tricarboxylic-acid (TCA) cycle. Therefore, we hypothesized that anaplerosis of the TCA cycle could be responsible for the high-protein diet-induced improvement of NAFLD by channeling amino acids into the TCA cycle. Next we considered that an efficient anaplerotic agent, the odd-carbon medium-chain triglyceride triheptanoin (TH), might have similar beneficial effects. C57BL/6J mice were fed low-fat (8en%) or high-fat (42en%) oleate-containing diets with or without 15en% TH for 3 weeks. TH treatment enhanced the hepatic capacity for fatty-acid oxidation by a selective increase in hepatic Ppara, Acox, and Cd36 expression, and a decline in plasma acetyl-carnitines. It also induced pyruvate cycling through an increased hepatic PCK1 protein concentration and it increased thermogenesis reflected by an increased Ucp2 mRNA content. TH, however, did not reduce hepatic lipid content. The comparison of the present effects of dietary triheptanoin with a previous study by our group on protein supplementation shows that the beneficial effects of the high-protein diet are not mimicked by TH. This argues against anaplerosis as the sole explanatory mechanism for the anti-steatotic effect of a high-protein diet. Copyright © 2015 Elsevier Ltd and European Society for Clinical Nutrition and Metabolism. All rights reserved.

  3. A Simple and Accurate Network for Hydrogen and Carbon Chemistry in the Interstellar Medium

    Science.gov (United States)

    Gong, Munan; Ostriker, Eve C.; Wolfire, Mark G.

    2017-07-01

    Chemistry plays an important role in the interstellar medium (ISM), regulating the heating and cooling of the gas and determining abundances of molecular species that trace gas properties in observations. Although solving the time-dependent equations is necessary for accurate abundances and temperature in the dynamic ISM, a full chemical network is too computationally expensive to incorporate into numerical simulations. In this paper, we propose a new simplified chemical network for hydrogen and carbon chemistry in the atomic and molecular ISM. We compare results from our chemical network in detail with results from a full photodissociation region (PDR) code, and also with the Nelson & Langer (NL99) network previously adopted in the simulation literature. We show that our chemical network gives similar results to the PDR code in the equilibrium abundances of all species over a wide range of densities, temperature, and metallicities, whereas the NL99 network shows significant disagreement. Applying our network to 1D models, we find that the CO-dominated regime delimits the coldest gas and that the corresponding temperature tracks the cosmic-ray ionization rate in molecular clouds. We provide a simple fit for the locus of CO-dominated regions as a function of gas density and column. We also compare with observations of diffuse and translucent clouds. We find that the CO, {{CH}}x, and {{OH}}x abundances are consistent with equilibrium predictions for densities n=100{--}1000 {{cm}}-3, but the predicted equilibrium C abundance is higher than that seen in observations, signaling the potential importance of non-equilibrium/dynamical effects.

  4. Three dimensional vibration and bending analysis of carbon nanotubes embedded in elastic medium based on theory of elasticity

    Directory of Open Access Journals (Sweden)

    M. Shaban

    Full Text Available This paper studies free vibration and bending behavior of singlewalled carbon nanotubes (SWCNTs embedded on elastic medium based on three-dimensional theory of elasticity. To accounting the size effect of carbon nanotubes, non-local theory is adopted to shell model. The nonlocal parameter is incorporated into all constitutive equations in three dimensions. The surrounding medium is modeled as two-parameter elastic foundation. By using Fourier series expansion in axial and circumferential direction, the set of coupled governing equations are reduced to the ordinary differential equations in thickness direction. Then, the state-space method as an efficient and accurate method is used to solve the resulting equations analytically. Comprehensive parametric studies are carried out to show the influences of the nonlocal parameter, radial and shear elastic stiffness, thickness-to-radius ratio and radiusto-length ratio.

  5. Effect of Calcium Nitrate and Sodium Nitrite on the Rebar Corrosion of Medium Carbon Steel in Seawater and Cassava Fluid

    OpenAIRE

    Adamu, M; Umoru, LE; Ige, OO

    2014-01-01

    Inhibitors are regularly used as one of the principal prevention and control techniques in reinforcement corrosion. Hence this study investigates the effect of calcium nitrate and sodium nitrite inhibitors on the rebar corrosion of medium carbon steel in seawater and cassava fluid with a view to determining inhibitive potentials of the different inhibitors in the two media. Gravimetric and voltametric techniques were employed in this study and a total of forty-five corrosion coupons of differ...

  6. The Influence of Vanadium Microalloying on the Production of Thin Slab Casting and Direct Rolled Steel Strip

    Science.gov (United States)

    Li, Yu; Milbourn, David

    Vanadium microalloying is highly effective in high strength strip steels produced by thin slab casting and direct rolled process. Because of the high solubility of V(C,N) in austenite, vanadium is likely to remain in solution during casting, equalisation and rolling. Vanadium microalloyed steels have better hot ductility and are less prone to transverse cracking than niobium containing steels. Despite a coarse as-cast austenite grain size before rolling, significant grain refinement can be achieved in vanadium microalloyed steels by repeated recrystallization during rolling, resulting in a fine uniform ferrite microstructure in final strip. Almost all vanadium present in microalloyed steels is available to precipitate in ferrite as very fine particles, contributing to precipitation strengthening. Vanadium microalloyed steels show less sensitivity to rolling process variables and exhibit excellent combination of strength and toughness.

  7. Activated carbon from peach stones using phosphoric acid activation at medium temperatures.

    Science.gov (United States)

    Kim, Dong-Su

    2004-01-01

    In the present study, the activation features of phosphoric acid have been investigated using waste peach stones as the raw material in the production of granular activated carbon. Thermogravimetry/differential thermal analysis was conducted to characterize the thermal behavior of peach stone and titration method was used to evaluate the adsorption capacity of the produced activated carbon. It was observed that the iodine value of the activated carbon increased with activation temperature. However, temperatures higher than 500 degrees C caused a thermal destruction, which resulted in the decrease of the adsorption capacity. Activation longer than 1.5 h at 500 degrees C resulted in thermal degradation of the porous structure of the activated carbon. The adsorption capacity was enhanced with increasing of amounts of phosphoric acid, however, excessive phosphoric acid caused a decrease in the iodine value. In addition, it was found that the carbon yields generally decreased with activation temperature and activation time. Scanning electron microscopy analysis was conducted to observe the changes in the poros structure of the activated carbon produced in different temperatures. Activation of carbon by phosphoric acid was found to be superior to that by CaCl2 and gas activation. The activated carbon produced from peach stone was applied as an adsorbent in the treatment of synthesized wastewater containing cadmium ion and its adsorption capacity was found to be as good as that of the commercial one.

  8. Iron (II) tetrakis(diaquaplatinum) octacarboxyphthalocyanine supported on multi-walled carbon nanotubes as effective electrocatalyst for oxygen reduction reaction in alkaline medium

    CSIR Research Space (South Africa)

    Mamuru, SA

    2010-11-01

    Full Text Available Oxygen reduction reaction (ORR) in alkaline medium at iron (II) tetrakis (diaquaplatinum) octacarboxyphthalocyanine (PtFeOCPc) catalyst supported on multi-walled carbon nanotubes (MWCNTs) has been described. The ORR followed the direct 4-electron...

  9. Mexico and emerging carbon markets : investment opportunities for small and medium-size companies and the global climate agenda

    International Nuclear Information System (INIS)

    Vaughan, S.; Carpentier, C.L.; Patterson, Z.; Kelly, K.; De Alba, E.; Hoyt, E.A.; Breceda, M.; Ouimet, B.

    2001-11-01

    This report provides information to the financial services sector on major environmental issues in North America in an effort to identify potential financial opportunities in Mexico regarding the climate change agenda and those coming from possible carbon offset projects. As a non-Annex 1 country, Mexico is not obliged to meet domestic GHG emission reduction targets, but given the strong economic links between Mexico, Canada and the United States it is suggested that investment transfer links to climate change should follow existing international investment and trade patterns. This report examined three sectors in Mexico, including electric power generation, steel production and land-use change and forestry, in an effort to evaluate their potential for carbon reduction. The report identifies carbon-related opportunities involving small and medium-size enterprises (SMEs) in particular because large companies are already better positioned to examine opportunities associated with the international climate agenda. SMEs, however, face many challenges in taking advantage of climate-related projects and associated investment opportunities, including higher entry and transaction costs, difficulty in accessing capital markets, and difficulty in estimating individual baselines and inventories. The report showed that the main carbon-related opportunity in Mexico's electricity sector are closely related to the planned expansion of natural gas use. This study also suggests that the climate agenda can contribute to changing Mexican forests from their current state of being a net source of greenhouse gas emissions, to becoming a significant carbon sink. tabs., figs

  10. Supercritical carbon dioxide as an innovative reaction medium for selective oxidation

    Energy Technology Data Exchange (ETDEWEB)

    Loeker, F.; Leitner, W. [Max-Planck-Institut fuer Kohlenforschung, Muelheim an der Ruhr (Germany)

    1998-12-31

    Although the catalytic efficiency of all catalytic oxidation processes studied in scCO{sub 2} up to now is far from being satisfactory, the principle possibility to carry out such reactions in this medium is clearly evident. Future research in our group will be directed towards the development of homogeneous and heterogeneous catalysts that are adopted to the special requirements of both the oxidation process and the supercritical reaction medium. Preliminary results from these studies regarding the epoxidation of olefins with molecular oxygen as oxidant will be presented on the conference poster. (orig.)

  11. Morphology, crystallography, and crack paths of tempered lath martensite in a medium-carbon low-alloy steel

    International Nuclear Information System (INIS)

    Wang, Chengduo; Qiu, Hai; Kimura, Yuuji; Inoue, Tadanobu

    2016-01-01

    The tempered lath martensite and its crack propagation have significant influence on the ductility and toughness of the warm tempformed medium-carbon steel. The martensitic microstructures of these medium-carbon steels are transformed from twinned austenite and the orientation relationship of lath martensite (α′) with prior austenite (γ) is distinctive. In the present paper we investigate the microstructure and fracture mode of a quenched and tempered 0.4%C-2%Si-1%Cr-1%Mo steel using electron backscatter diffraction technique. The results showed that the orientation relationship between γ and α′ is Greninger-Troiano (G-T) relationship. A single γ grain was divided into 4 packets and each packet was subdivided into 3 blocks. The misorientation angles between adjacent blocks were ~54.3° or ~60.0° in a packet. Most γ grains were twins sharing a {111} γ plane. There were 7 packets in a twinned γ grain and the twin boundaries were in a special packet. Besides the common packet, there were three packets in each twin. Being different from the cleavage fracture along the {001} planes in conventional martensitic steels, both cleavage and intergranular cracks were present in our medium-carbon steel. The former was in the larger blocks and it propagated along the {001}, {011}, and {112} planes. The latter propagated along the block, packet, or prior austenite boundaries. The intergranular cracks were generally in the fine block region. These results suggested that the block size is the key factor in controlling the brittle fracture mode of lath martensitic steel.

  12. Thermodynamic and kinetic characteristics of the austenite-to-ferrite transformation under high magnetic field in medium carbon steel

    International Nuclear Information System (INIS)

    Zhang Yudong; He Changshu; Zhao Xiang; Zuo Liang; Esling, Claude

    2005-01-01

    The thermodynamic and kinetic characteristics of austenite-to-ferrite phase transformation in medium carbon steel in the high magnetic fields were investigated. Results showed that the magnetic field could obviously change the γ/α+γ phase equilibrium-by increasing the amount of ferrite obtained during cooling-and greatly accelerate the transformation. Thus the microstructure obtained under fast cooling with high magnetic field was still ferritic and pearlitic, while that obtained without the magnetic field under the same cooling conditions was bainitic. Exploration in this area contributes both to enriching the new theory on electromagnetic processing of materials (EPM) and in establishing new techniques for materials processing

  13. Structure of a Wear-Resistant Medium-Carbon Steel After Hot Deformation in Hammer Dies and Heat Treatment

    Science.gov (United States)

    Knyazyuk, T. V.; Petrov, S. N.; Ryabov, V. V.; Khlusova, E. I.

    2018-01-01

    The structure of model specimens and articles fabricated from medium-carbon high-strength steels is studied for developing modes of forming of working members of tilling machines with cutting edges thinned without the expensive operation of electromachining. The effect of the temperature of heating of billets on the grain size of austenite is determined. The kinetics of recrystallization is studied in the temperature, rate and strain ranges typical for hot forming. A quantitative crystallographic analysis of the microstructure is performed by the EBSD technique. The degrees of distortion of the crystal lattices of structural components and the mean sizes of martensite blocks are determined.

  14. Three-dimensional ultrashort optical Airy beams in an inhomogeneous medium with carbon nanotubes

    Science.gov (United States)

    Zhukov, Alexander V.; Bouffanais, Roland; Belonenko, Mikhail B.; Dvuzhilov, Ilya S.

    2017-03-01

    In this Letter, we consider the problem of the dynamics of propagation of three-dimensional optical pulses (a.k.a. light bullets) with an Airy profile through a heterogeneous environment of carbon nanotubes. We show numerically that such beams exhibit sustained and stable propagation. Moreover, we demonstrate that by varying the density modulation period of the carbon nanotubes one can indirectly control the pulse velocity, which is a particularly valuable feature for the design and manufacturing of novel pulse delay devices.

  15. Carbon footprint analysis as a tool for energy and environmental management in small and medium-sized enterprises

    Science.gov (United States)

    Giama, E.; Papadopoulos, A. M.

    2018-01-01

    The reduction of carbon emissions has become a top priority in the decision-making process for governments and companies, the strict European legislation framework being a major driving force behind this effort. On the other hand, many companies face difficulties in estimating their footprint and in linking the results derived from environmental evaluation processes with an integrated energy management strategy, which will eventually lead to energy-efficient and cost-effective solutions. The paper highlights the need of companies to establish integrated environmental management practices, with tools such as carbon footprint analysis to monitor the energy performance of production processes. Concepts and methods are analysed, and selected indicators are presented by means of benchmarking, monitoring and reporting the results in order to be used effectively from the companies. The study is based on data from more than 90 Greek small and medium enterprises, followed by a comprehensive discussion of cost-effective and realistic energy-saving measures.

  16. Effect of austenite deformation temperature on Nb clustering and precipitation in microalloyed steel

    International Nuclear Information System (INIS)

    Pereloma, E.V.; Kostryzhev, A.G.; AlShahrani, A.; Zhu, C.; Cairney, J.M.; Killmore, C.R.; Ringer, S.P.

    2014-01-01

    The effect of thermomechanical processing conditions on Nb clustering and precipitation in both austenite and ferrite in a Nb–Ti microalloyed steel was studied using electron microscopy and atom probe tomography. A decrease in the deformation temperature increased the Nb-rich precipitation in austenite and decreased the extent of precipitation in ferrite. Microstructural mechanisms that explain this variation are discussed

  17. Mass return to the interstellar medium from highly-evolved carbon stars

    International Nuclear Information System (INIS)

    Latter, W.B.; Thronson, H.A. Jr.; Hacking, P.; Bally, J.; Black, J.; Bell Telephone Labs. Inc., Holmdel, NJ)

    1986-01-01

    Data produced by the Infrared Astronomy Satellite (IRAS) was surveyed at the mid- and far-infrared wavelengths. Visually-identified carbon stars in the 12/25/60 micron color-color diagram were plotted, along with the location of a number of mass-losing stars that lie near the location of the carbon stars, but are not carbon rich. The final sample consisted of 619 objects, which were estimated to be contaminated by 7 % noncarbon-rich objects. The mass return rate was estimated for all evolved circumstellar envelopes. The IRAS Point Source Catalog (PSC) was also searched for the entire class of stars with excess emission. Mass-loss rates, lifetimes, and birthrates for evolved stars were also estimated

  18. Performance Evaluation Of Africa Elemi Melon And Africa Locust Bean Oil As Potential Quenchants For Medium Carbon Steel

    Directory of Open Access Journals (Sweden)

    C. S. Ibeh

    2017-06-01

    Full Text Available A qualitative and comparative study was carried out on some locally sourced oils melon oil Africa elemi oil and Africa locust bean oil to evaluate suitability as substitute quenching media to mineral-based oil. The cooling ability of the oils was investigated using AISI 1034 medium carbon steel. The effect of heat transfer coefficient on quench severity mechanical properties of the quenched specimens were investigated in the course of the study. Results showed that the peak rate of heat extraction of melon oil Africa locust bean and Africa elemi oil were higher than that of mineral oil. Higher heat transfer coefficient of 1463 1023 Wm2k were obtained for melon oil and Africa locust bean Africa elemi and SAE 40 oil have heat transfer coefficient of 982 and 469 Wm2k respectively. The selected oils can be used as quenchants for medium carbon steel since the oils exhibits better cooling properties and mechanical properties than mineral-based oil.

  19. Culture medium type affects endocytosis of multi-walled carbon nanotubes in BEAS-2B cells and subsequent biological response.

    Science.gov (United States)

    Haniu, Hisao; Saito, Naoto; Matsuda, Yoshikazu; Tsukahara, Tamotsu; Maruyama, Kayo; Usui, Yuki; Aoki, Kaoru; Takanashi, Seiji; Kobayashi, Shinsuke; Nomura, Hiroki; Okamoto, Masanori; Shimizu, Masayuki; Kato, Hiroyuki

    2013-09-01

    We examined the cytotoxicity of multi-walled carbon nanotubes (MWCNTs) and the resulting cytokine secretion in BEAS-2B cells or normal human bronchial epithelial cells (HBEpCs) in two types of culture media (Ham's F12 containing 10% FBS [Ham's F12] and serum-free growth medium [SFGM]). Cellular uptake of MWCNT was observed by fluorescent microscopy and analyzed using flow cytometry. Moreover, we evaluated whether MWCNT uptake was suppressed by 2 types of endocytosis inhibitors. We found that BEAS-2B cells cultured in Ham's F12 and HBEpCs cultured in SFGM showed similar biological responses, but BEAS-2B cells cultured in SFGM did not internalize MWCNTs, and the 50% inhibitory concentration value, i.e., the cytotoxicity, was increased by more than 10-fold. MWCNT uptake was suppressed by a clathrin-mediated endocytosis inhibitor and a caveolae-mediated endocytosis inhibitor in BEAS-2B cells cultured in Ham's F12 and HBEpCs cultured in SFGM. In conclusion, we suggest that BEAS-2B cells cultured in a medium containing serum should be used for the safety evaluation of nanomaterials as a model of normal human bronchial epithelial cells. However, the culture medium composition may affect the proteins that are expressed on the cytoplasmic membrane, which may influence the biological response to MWCNTs. Copyright © 2013 The Authors. Published by Elsevier Ltd.. All rights reserved.

  20. Heterogeneously Catalysed Aldol Reactions in Supercritical Carbon Dioxide as Innovative and Non-Flammable Reaction Medium

    DEFF Research Database (Denmark)

    Musko, Nikolai; Grunwaldt, Jan-Dierk

    2011-01-01

    Aldol reactions of several aldehydes have been investigated over acidic and basic catalysts in supercritical carbon dioxide at 180 bar and 100 °C. Both acidic (Amberlyst-15, tungstosilicic acid (TSA) on SiO2 and MCM-41) and basic (hydrotalcite) materials showed interesting performance in this pre...

  1. Combined Effect of Heating Rate and Microalloying Elements on Recrystallization During Annealing of Dual-Phase Steels

    Science.gov (United States)

    Bellavoine, Marion; Dumont, Myriam; Drillet, Josée; Hébert, Véronique; Maugis, Philippe

    2018-05-01

    Adjusting ferrite recrystallization kinetics during annealing is a way to control the final microstructure and thus the mechanical properties of advanced cold-rolled high-strength steels. Two strategies are commonly used for this purpose: adjusting heating rates and/or adding microalloying elements. The present work investigates the effect of heating rate and microalloying elements Ti, Nb, and Mo on recrystallization kinetics during annealing in various cold-rolled Dual-Phase steel grades. The use of combined experimental and modeling approaches allows a deeper understanding of the separate influence of heating rate and the addition of microalloying elements. The comparative effect of Ti, Nb, and Mo as solute elements and as precipitates on ferrite recrystallization is also clarified. It is shown that solute drag has the largest delaying effect on recrystallization in the present case and that the order of solute drag effectiveness of microalloying elements is Nb > Mo > Ti.

  2. Cognition and Synaptic-Plasticity Related Changes in Aged Rats Supplemented with 8- and 10-Carbon Medium Chain Triglycerides.

    Directory of Open Access Journals (Sweden)

    Dongmei Wang

    Full Text Available Brain glucose hypometabolism is a common feature of Alzheimer's disease (AD. Previous studies have shown that cognition is improved by providing AD patients with an alternate energy source: ketones derived from either ketogenic diet or supplementation with medium chain triglycerides (MCT. Recently, data on the neuroprotective capacity of MCT-derived medium chain fatty acids (MCFA suggest 8-carbon and 10-carbon MCFA may have cognition-enhancing properties which are not related to ketone production. We investigated the effect of 8 week treatment with MCT8, MCT10 or sunflower oil supplementation (5% by weight of chow diet in 21 month old Wistar rats. Both MCT diets increased ketones plasma similarly compared to control diet, but MCT diets did not increase ketones in the brain. Treatment with MCT10, but not MCT8, significantly improved novel object recognition memory compared to control diet, while social recognition increased in both MCT groups. MCT8 and MCT10 diets decreased weight compared to control diet, where MCFA plasma levels were higher in MCT10 groups than in MCT8 groups. Both MCT diets increased IRS-1 (612 phosphorylation and decreased S6K phosphorylation (240/244 but only MCT10 increased Akt phosphorylation (473. MCT8 supplementation increased synaptophysin, but not PSD-95, in contrast MCT10 had no effect on either synaptic marker. Expression of Ube3a, which controls synaptic stability, was increased by both MCT diets. Cortex transcription via qPCR showed that immediate early genes related to synaptic plasticity (arc, plk3, junb, egr2, nr4a1 were downregulated by both MCT diets while MCT8 additionally down-regulated fosb and egr1 but upregulated grin1 and gba2. These results demonstrate that treatment of 8- and 10-carbon length MCTs in aged rats have slight differential effects on synaptic stability, protein synthesis and behavior that may be independent of brain ketone levels.

  3. Porous carbon with small mesoporesas an ultra-high capacity adsorption medium

    Science.gov (United States)

    Gao, Biaofeng; Zhou, Haitao; Chen, De; Yang, Jianhong

    2017-10-01

    Resins (732-type), abundant and inexpensive resources were used to prepare porous carbon with small mesopores (CSM) by carbonization and post-chemical-activation with potassium hydroxide (KOH). The N2 adsorption measurements revealed that CSM had high surface areas (1776.5 m2 g-1), large pore volumes (1.10 cm3 g-1), and nearly optimal narrow small mesopore sizes ranging from 2 to 7 nm. CSM was used as adsorbent to investigate the adsorption behavior for Rhodamine B (RhB). Due to the optimal pore size distributions (PSD), intensive-stacking interaction, S-doped, and electrostatic attraction, the CSM exhibited an ultra-high-capacity of 1590 mg g-1 for RhB in aqueous solutions.

  4. Three-dimensional ultrashort optical Airy beams in an inhomogeneous medium with carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Zhukov, Alexander V., E-mail: alex.zhukov@outlook.sg [Singapore University of Technology & Design, 8 Somapah Road, 487372 Singapore (Singapore); Bouffanais, Roland [Singapore University of Technology & Design, 8 Somapah Road, 487372 Singapore (Singapore); Belonenko, Mikhail B. [Laboratory of Nanotechnology, Volgograd Institute of Business, 400048 Volgograd (Russian Federation); Volgograd State University, 400062 Volgograd (Russian Federation); Dvuzhilov, Ilya S. [Volgograd State University, 400062 Volgograd (Russian Federation)

    2017-03-11

    In this Letter, we consider the problem of the dynamics of propagation of three-dimensional optical pulses (a.k.a. light bullets) with an Airy profile through a heterogeneous environment of carbon nanotubes. We show numerically that such beams exhibit sustained and stable propagation. Moreover, we demonstrate that by varying the density modulation period of the carbon nanotubes one can indirectly control the pulse velocity, which is a particularly valuable feature for the design and manufacturing of novel pulse delay devices. - Highlights: • Propagation of Airy pulses in CNTs with modulated density. • Light bullets propagate stably. • Influence of Airy parameter is revealed. • Modulation period results in an increase of the pulse velocity.

  5. Medium scale carbon nanotube thin film integrated circuits on flexible plastic substrates

    Science.gov (United States)

    Rogers, John A; Cao, Qing; Alam, Muhammad; Pimparkar, Ninad

    2015-02-03

    The present invention provides device components geometries and fabrication strategies for enhancing the electronic performance of electronic devices based on thin films of randomly oriented or partially aligned semiconducting nanotubes. In certain aspects, devices and methods of the present invention incorporate a patterned layer of randomly oriented or partially aligned carbon nanotubes, such as one or more interconnected SWNT networks, providing a semiconductor channel exhibiting improved electronic properties relative to conventional nanotubes-based electronic systems.

  6. Effect of carbonate in slightly alkaline medium on the corrosion of maraging steel

    International Nuclear Information System (INIS)

    Bellanger, G.

    1994-01-01

    This study was carried out to ascertain the behavior of maraging steel identified as AMS. 65-12 and used in the tanks of the French plant for the reprocessing of radioactive water. This water has a pH of 9 and contains carbonate ions. The rest or corrosion potentials can be in the transpassive or active region due to radiolytic species. Therefore, the behavior of maraging steel was studied in these two regions. In the neighborhood of the active-passive transition potentials, maraging steel is corroded by means of intermediates. The corrosion potential does not change with carbonate at a constant pH. With carbonate and a low scan rate, the breakdown transpassive potentials are displaced towards more positive potentials and the passive potential region is broader, while at a high scan rate these potentials are displaced towards more negative values. After the beginning of the reverse scan, the current is again positive. These suggest that the corrosion kinetics are not the same. The diffusion coefficient of species inside the oxide layer was determined. ((orig.))

  7. High electrocatalytic performance of nitrogen-doped carbon nanofiber-supported nickel oxide nanocomposite for methanol oxidation in alkaline medium

    Energy Technology Data Exchange (ETDEWEB)

    Al-Enizi, Abdullah M. [Department of Chemistry, King Saud University, PO Box: 2455, Riyadh 11451 (Saudi Arabia); Elzatahry, Ahmed A., E-mail: aelzatahry@ksu.edu.sa [Materials Science and Technology Program, College of Arts and Science, Qatar University, Doha 2713 (Qatar); Advanced Technology and New Materials Research Institute, City of Scientific Research and Technology Applications, New Borg El-Arab City, Alexandria 21934 (Egypt); Abdullah, Aboubakr M., E-mail: bakr@qu.edu.qa [Center for Advanced Materials, Qatar University, Doha 2713 (Qatar); Vinu, Ajayan [Future Industries Institute, University of South Australia, Building X-X2-09, Mawson Lakes Campus, Mawson Lakes 5095 SA (Australia); Iwai, Hideo [Materials Analysis Station, National Institute for Materials Science, 1-2-1 Sengen, Tsukuba, Ibaraki, 305-0047 (Japan); Al-Deyab, Salem S. [Petrochemical Research Chair, Department of Chemistry, King Saud University, PO Box: 2455, Riyadh 11451 (Saudi Arabia)

    2017-04-15

    Highlights: • A mixture of Polyvinylpyrrolidone (PVP), graphene and emeraldine base polyaniline (PANi) was electrospun and used as starting materials to prepare a nitrogen-doped carbon nanofiber (N-CNF). • Nickel oxide was loaded on the N-CNF to form a nanocomposite which was calcined later at different temperatures. • The effect of calcination temperature on the electrocatalytic behavior of the nanocomposite was studied which shows that the nanocomposite calcined at 500 °C was proved to be very high compared to the other calcination temperatures. • The stability of catalyst was excellent and its resistance to the adsorption of the intermediates generated from the methanol oxidation was very high. - Abstract: Nitrogen-Doped Carbon Nanofiber (N-CNF)–supported NiO composite was prepared by electrospinning a sol-gel mixture of graphene and polyaniline (PANi) with aqueous solutions of Polyvinylpyrrolidone (PVP) followed by a high-temperature annealing process. The electrospun was stabilized for 2 h at 280 °C, carbonized for 5 h at 1200 °C then loaded by 10% NiO. The electrocatalytic activities of the produced nanocomposite have been studied using cyclic voltammetry, and chronoamperometry. Also, N-CNF was characterized by X-ray diffraction (XRD), thermogravimetric analysis (TGA), surface area (BET), X-ray photoelectron spectroscopy (XPS), transmission electron microscope (TEM), and scanning-electron microscopy (SEM). The obtained N-doped carbon nanofiber was found to have a nitrogen content of 2.6 atomic% with a diameter range of (140–160) nm, and a surface area (393.3 m{sup 2} g{sup −1}). In addition, it showed a high electrocatalytic behavior towards methanol oxidation reaction in alkaline medium and high stability and resistivity to the adsorption of intermediates.

  8. Oxygen reduction reaction on carbon-supported CoSe2 nanoparticles in an acidic medium

    International Nuclear Information System (INIS)

    Feng Yongjun; He Ting; Alonso-Vante, Nicolas

    2009-01-01

    We investigated the effect of CoSe 2 /C nanoparticle loading rate on oxygen reduction reaction (ORR) activity and H 2 O 2 production using the rotating disk electrode and the rotating ring-disk electrode techniques. We prepared carbon-supported CoSe 2 nanoparticles with different nominal loading rates and evaluated these samples by means of powder X-ray diffraction. All the catalysts had an OCP value of 0.81 V vs. RHE. H 2 O 2 production during the ORR process decreased with an increase in catalytic layer thickness. This decrease was related to the CoSe 2 loading on the disk electrode. H 2 O 2 production also decreased with increasing catalytic site density, a phenomenon related to the CoSe 2 loading rate on the carbon substrate. The cathodic current density significantly increased with increasing catalytic layer thickness, but decreased with increasing catalytic site density. In the case of 20 wt% CoSe 2 /C nanoparticles at 22 μg cm -2 , we determined that the transfer process involves about 3.5 electrons.

  9. Enhancement of electrocatalytic properties of carbonized polyaniline nanoparticles upon a hydrothermal treatment in alkaline medium

    International Nuclear Information System (INIS)

    Gavrilov, Nemanja; Vujkovic, Milica; Pasti, Igor A.; Ciric-Marjanovic, Gordana; Mentus, Slavko V.

    2011-01-01

    Highlights: → Carbonized polyaniline nanoparticles were treated hydrothermally in 1 M KOH. → Hydrothermal treatment improved the electrocatalytic activity towards ORR. → Significant effect of catalyst loading was evidenced too. → At the loading 0.5 mg cm -2 the 4e - reaction path was achieved. - Abstract: The electrocatalytic activity of carbonized polyaniline nanostructures (Carb-nanoPANI) towards oxygen reduction reaction (ORR), estimated in 0.1 mol dm -3 KOH solution, was significantly improved upon a hydrothermal treatment in 1 mol dm -3 KOH solution. Namely, the onset of ORR was shifted by ∼70 mV to more positive potentials, and the number of electrons consumed per O 2 molecule was enhanced in comparison to the original material. The number of electrons involved in ORR depended on loading, and with a loading of 0.5 mg cm -2 , for the potentials lower than -0.5 V vs SCE, the number of electrons approached 4. For this material, high stability of electrochemical behavior and resistance to the poisoning by ethanol was evidenced by potentiodynamic cycling.

  10. Enhancement of electrocatalytic properties of carbonized polyaniline nanoparticles upon a hydrothermal treatment in alkaline medium

    Energy Technology Data Exchange (ETDEWEB)

    Gavrilov, Nemanja; Vujkovic, Milica; Pasti, Igor A.; Ciric-Marjanovic, Gordana [University of Belgrade, Faculty of Physical Chemistry, Studentski trg 12-16, 11158 Belgrade (Serbia); Mentus, Slavko V., E-mail: slavko@ffh.bg.ac.rs [University of Belgrade, Faculty of Physical Chemistry, Studentski trg 12-16, 11158 Belgrade (Serbia); Serbian Academy of Sciences and Arts, Knez Mihajlova 35, 11158 Belgrade (Serbia)

    2011-10-30

    Highlights: > Carbonized polyaniline nanoparticles were treated hydrothermally in 1 M KOH. > Hydrothermal treatment improved the electrocatalytic activity towards ORR. > Significant effect of catalyst loading was evidenced too. > At the loading 0.5 mg cm{sup -2} the 4e{sup -} reaction path was achieved. - Abstract: The electrocatalytic activity of carbonized polyaniline nanostructures (Carb-nanoPANI) towards oxygen reduction reaction (ORR), estimated in 0.1 mol dm{sup -3} KOH solution, was significantly improved upon a hydrothermal treatment in 1 mol dm{sup -3} KOH solution. Namely, the onset of ORR was shifted by {approx}70 mV to more positive potentials, and the number of electrons consumed per O{sub 2} molecule was enhanced in comparison to the original material. The number of electrons involved in ORR depended on loading, and with a loading of 0.5 mg cm{sup -2}, for the potentials lower than -0.5 V vs SCE, the number of electrons approached 4. For this material, high stability of electrochemical behavior and resistance to the poisoning by ethanol was evidenced by potentiodynamic cycling.

  11. Effect of Longitudinal Magnetic Field on Vibration Characteristics of Single-Walled Carbon Nanotubes in a Viscoelastic Medium

    Science.gov (United States)

    Zhang, D. P.; Lei, Y.; Shen, Z. B.

    2017-12-01

    The effect of longitudinal magnetic field on vibration response of a sing-walled carbon nanotube (SWCNT) embedded in viscoelastic medium is investigated. Based on nonlocal Euler-Bernoulli beam theory, Maxwell's relations, and Kelvin viscoelastic foundation model, the governing equations of motion for vibration analysis are established. The complex natural frequencies and corresponding mode shapes in closed form for the embedded SWCNT with arbitrary boundary conditions are obtained using transfer function method (TFM). The new analytical expressions for the complex natural frequencies are also derived for certain typical boundary conditions and Kelvin-Voigt model. Numerical results from the model are presented to show the effects of nonlocal parameter, viscoelastic parameter, boundary conditions, aspect ratio, and strength of the magnetic field on vibration characteristics for the embedded SWCNT in longitudinal magnetic field. The results demonstrate the efficiency of the proposed methods for vibration analysis of embedded SWCNTs under magnetic field.

  12. The effect of coiling temperature on the microstructure and mechanical properties of a niobium–titanium microalloyed steel processed via thin slab casting

    International Nuclear Information System (INIS)

    Challa, V.S.A.; Zhou, W.H.; Misra, R.D.K.; O'Malley, R.; Jansto, S.G.

    2014-01-01

    We describe here the influence of coiling temperature on the microstructure and mechanical properties, especially toughness, in a low carbon niobium microalloyed steel processed via thin slab casting. The objective is to elucidate the impact of coiling temperature on the nature and distribution of microstructural constituents (including different phases, precipitates, and dislocations) that contribute to variation in the strength–toughness relationship of these steels. In general, the microstructure primarily consisted of fine lath-type bainite and polygonal ferrite, and NbC, TiC and (Nb, Ti)C precipitates of size ∼2–10 nm in the matrix and at dislocations. However, the dominance of bainite and distribution of precipitates was a function of coiling temperature. The lower coiling temperature provided superior strength–toughness combination and is attributed to predominantly bainitic microstructure and uniform precipitation of NbC, TiC, and (Nb, Ti)C during the coiling process, consistent with continuous cooling transformation diagrams

  13. The effect of coiling temperature on the microstructure and mechanical properties of a niobium–titanium microalloyed steel processed via thin slab casting

    Energy Technology Data Exchange (ETDEWEB)

    Challa, V.S.A.; Zhou, W.H. [Laboratory for Excellence in Advanced Steel Research, Center for Structural and Functional Materials, Institute for Material Research and Innovation, University of Louisiana at Lafayette, P.O. Box 44130, Lafayette, LA 70503 (United States); Misra, R.D.K., E-mail: dmisra@louisiana.edu [Laboratory for Excellence in Advanced Steel Research, Center for Structural and Functional Materials, Institute for Material Research and Innovation, University of Louisiana at Lafayette, P.O. Box 44130, Lafayette, LA 70503 (United States); O' Malley, R. [Nucor Decatur Sheet Mill, 4301 Iverson Blvd., Trinity, AL 35673 (United States); Jansto, S.G. [CBMM North America, 1000 Old Pond Road, Bridgeville, PA 15017 (United States)

    2014-02-10

    We describe here the influence of coiling temperature on the microstructure and mechanical properties, especially toughness, in a low carbon niobium microalloyed steel processed via thin slab casting. The objective is to elucidate the impact of coiling temperature on the nature and distribution of microstructural constituents (including different phases, precipitates, and dislocations) that contribute to variation in the strength–toughness relationship of these steels. In general, the microstructure primarily consisted of fine lath-type bainite and polygonal ferrite, and NbC, TiC and (Nb, Ti)C precipitates of size ∼2–10 nm in the matrix and at dislocations. However, the dominance of bainite and distribution of precipitates was a function of coiling temperature. The lower coiling temperature provided superior strength–toughness combination and is attributed to predominantly bainitic microstructure and uniform precipitation of NbC, TiC, and (Nb, Ti)C during the coiling process, consistent with continuous cooling transformation diagrams.

  14. High Electrocatalytic Performance of CuCoNi@CNTs Modified Glassy Carbon Electrode towards Methanol Oxidation in Alkaline Medium

    Directory of Open Access Journals (Sweden)

    Amina A. Hamza

    2017-01-01

    Full Text Available A novel non-precious multiwalled carbon nanotubes (CNTs—supported metal oxide electrocatalyst was developed for methanol electrooxidation in alkaline medium. The catalyst was fabricated by simultaneous electrodeposition of copper-cobalt-nickel ternary nanostructures (CuCoNi on a glassy carbon electrode (GCE modified with CNTs. The proposed electrode was characterized using X-ray diffraction (XRD, energy dispersive X-ray (EDX, and scanning electron microscopy (SEM. The electrochemical behavior and the electrocatalytic performance of the suggested electrode towards the oxidation of methanol were evaluated by cyclic voltammetry (CV, linear sweep voltammetry (LSV, and chronoamperometry (CA in alkaline medium. Several parameters were investigated, e.g., deposition time, potential scan rate, etc. Compared to Cu, Co, or Ni mono electrocatalysts, the electrode based on ternary-metals exhibited superior electrocatalytic activity and stability towards methanol electrooxidation. For instance, CuCoNi@CNTs/GCE has shown at least 2.5 times electrocatalytic activity and stability compared to the mono eletrocatalysts. Moreover, the present study found that the optimized loading level is 1500 s of simultaneous electrodeposition. At this loading level, it was found that the relation between the Ip/ν1/2 function and scan rate gives the characteristic features of a catalytic process. The enhanced activity and stability of CuCoNi@CNTs/GCE was attributed to (i a synergism between three metal oxides coexisting in the same structure; (ii the presence of CNTs as a support for the metal oxides, that offers high surface area for the deposited tertiary alloy and suppresses the aggregation and sintering of the metals oxide with time; as well as (iii the increase of the conductivity of the deposited semiconducting metal oxides.

  15. Impact toughness and microstructure relationship in niobium- and vanadium-microalloyed steels processed with varied cooling rates to similar yield strength

    Energy Technology Data Exchange (ETDEWEB)

    Shanmugam, S. [Center for Structural and Functional Materials and Department of Chemical Engineering, University of Louisiana at Lafayette, LA 70504-4130 (United States); Misra, R.D.K. [Center for Structural and Functional Materials and Department of Chemical Engineering, University of Louisiana at Lafayette, LA 70504-4130 (United States)]. E-mail: dmisra@louisiana.edu; Mannering, T. [Nucor-Yamato Steel, P.O. Box 1228, 5929 East State Highway 18, Blytheville, AR 72316 (United States); Panda, D. [Nucor-Yamato Steel, P.O. Box 1228, 5929 East State Highway 18, Blytheville, AR 72316 (United States); Jansto, S.G. [Reference Metals, 1000 Old Pond Road, Bridgeville, PA 15017 (United States)

    2006-11-15

    We describe here the relationship between microstructure and impact toughness behavior as a function of cooling rate for industrially processed Nb- and V-microalloyed steels of almost similar yield strength ({approx}60 ksi). Both Nb- and V-microalloyed steels exhibited increase in toughness with increase in cooling rates during processing. However, Nb-microalloyed steels were characterized by relatively higher toughness than the V-microalloyed steels under identical processing conditions. The microstructure of Nb- and V-microalloyed steels processed at conventional cooling rate, primarily consisted of polygonal ferrite-pearlite microconstituents, while Nb-microalloyed steels besides polygonal ferrite and pearlite contained significant fraction of degenerated pearlite. The microstructure of Nb- and V-microalloyed steels processed at relatively higher cooling rate contained degenerated pearlite and lath-type (acicular) ferrite in addition to the primary ferrite-pearlite constituents. The fraction of degenerated pearlite was higher in Nb-microalloyed steels than in the V-microalloyed steels. In both Nb- and V-microalloyed steels the precipitation characteristics were similar with precipitation occurring at grain boundaries, dislocations, and in the ferrite matrix. Fine-scale ({approx}5-10 nm) precipitation was observed in the ferrite matrix of both the steels. The selected area diffraction (SAD) pattern analysis revealed that these fine precipitates were MC type of niobium and vanadium carbides in the respective steels and followed Baker-Nutting orientation relationship with the ferrite matrix. The microstructural studies suggest that the increase in toughness of Nb-microalloyed steels is attributed to higher fraction of degenerated pearlite in the steel.

  16. Impact toughness and microstructure relationship in niobium- and vanadium-microalloyed steels processed with varied cooling rates to similar yield strength

    International Nuclear Information System (INIS)

    Shanmugam, S.; Misra, R.D.K.; Mannering, T.; Panda, D.; Jansto, S.G.

    2006-01-01

    We describe here the relationship between microstructure and impact toughness behavior as a function of cooling rate for industrially processed Nb- and V-microalloyed steels of almost similar yield strength (∼60 ksi). Both Nb- and V-microalloyed steels exhibited increase in toughness with increase in cooling rates during processing. However, Nb-microalloyed steels were characterized by relatively higher toughness than the V-microalloyed steels under identical processing conditions. The microstructure of Nb- and V-microalloyed steels processed at conventional cooling rate, primarily consisted of polygonal ferrite-pearlite microconstituents, while Nb-microalloyed steels besides polygonal ferrite and pearlite contained significant fraction of degenerated pearlite. The microstructure of Nb- and V-microalloyed steels processed at relatively higher cooling rate contained degenerated pearlite and lath-type (acicular) ferrite in addition to the primary ferrite-pearlite constituents. The fraction of degenerated pearlite was higher in Nb-microalloyed steels than in the V-microalloyed steels. In both Nb- and V-microalloyed steels the precipitation characteristics were similar with precipitation occurring at grain boundaries, dislocations, and in the ferrite matrix. Fine-scale (∼5-10 nm) precipitation was observed in the ferrite matrix of both the steels. The selected area diffraction (SAD) pattern analysis revealed that these fine precipitates were MC type of niobium and vanadium carbides in the respective steels and followed Baker-Nutting orientation relationship with the ferrite matrix. The microstructural studies suggest that the increase in toughness of Nb-microalloyed steels is attributed to higher fraction of degenerated pearlite in the steel

  17. Nucleation and growth characteristics of graphite spheroids in bainite during graphitization annealing of a medium carbon steel

    International Nuclear Information System (INIS)

    Gao, J.X.; Wei, B.Q.; Li, D.D.; He, K.

    2016-01-01

    The evolution of microstructure in bainite during graphitization annealing at 680 °C of Jominy-quenched bars of an Al-Si bearing medium carbon (0.4C wt%) steel has been studied and compared with that in martensite by using light, scanning and transmission electron microscopy. The results show that the graphitization process in bainite is different from that in martensite in many aspects such as the initial carbon state, the behavior of cementite, the nucleation-growth feature and kinetics of formation of graphite spheroids during graphitization annealing, and the shape, size and distribution of these graphite spheroids. The fact that the graphitization in bainite can produce more homogeneous graphite spheroids with more spherical shape and finer size in a shorter annealing time without the help of preexisting coring particles implies that bainite should be a better starting structure than martensite for making graphitic steel. - Highlights: • This article presents a microstructural characterization of formation of graphite spheroids in bainite. • Nucleation and growth characteristics of graphite spheroids formed in bainite and martensite are compared. • Bainite should be a better starting structure for making graphitic steel as results show.

  18. Medium-chain-length poly-3-hydroxyalkanoates-carbon nanotubes composite anode enhances the performance of microbial fuel cell.

    Science.gov (United States)

    Hindatu, Y; Annuar, M S M; Subramaniam, R; Gumel, A M

    2017-06-01

    Insufficient power generation from a microbial fuel cell (MFC) hampers its progress towards utility-scale development. Electrode modification with biopolymeric materials could potentially address this issue. In this study, medium-chain-length poly-3-hydroxyalkanoates (PHA)/carbon nanotubes (C) composite (CPHA) was successfully applied to modify the surface of carbon cloth (CC) anode in MFC. Characterization of the functional groups on the anodic surface and its morphology was carried out. The CC-CPHA composite anode recorded maximum power density of 254 mW/m 2 , which was 15-53% higher than the MFC operated with CC-C (214 mW/m 2 ) and pristine CC (119 mW/m 2 ) as the anode in a double-chambered MFC operated with Escherichia coli as the biocatalyst. Electrochemical impedance spectroscopy and cyclic voltammetry showed that power enhancement was attributed to better electron transfer capability by the bacteria for the MFC setup with CC-CPHA anode.

  19. Carbon-13 kinetic isotope effects in the decarbonylation of lactic acid of natural isotopic composition in phosphoric acid medium

    International Nuclear Information System (INIS)

    Zielinski, M.; Czarnota, G.; Papiernik-Zielinska, H.; Kasprzyk, G.; Gumolka, L.; Staedter, W.

    1993-01-01

    The 13 C kinetic isotope effect fractionation in the decarbonylation of lactic acid (LA) of natural isotopic composition by concentrated phosphoric acids (PA) and by 85% H 3 PO 4 has been studied in the temperature interval of 60-150 deg C. The values of the 13 C (1) isotope effects in the decarbonylation of lactic acid in 100% H 3 PO 4 , in pyrophosphoric acid and in more concentrated phosphoric acids are intermediate between the values calculated assuming that the C (1)- OH bond is broken in the rate-controlling step of dehydration and those calculated for rupture of the carbon-carbon bond in the transition state. In the temperature interval of 90-130 deg C the experimental 13 C fractionation factors determined in concentrated PA approach quite closely the 13 C fractionation corresponding to C (2)- C (1) bond scission. The 13 C (1) kinetic isotope effects in the decarbonylation of LA in 85% orthophosphoric acid in the temperature range of 110-150 deg C coincide with the 13 C isotope effects calculated assuming that the frequency corresponding to the C (1) -OH vibration is lost in the transition state of decarbonylation. A change of the mechanism of decarbonylation of LA in going from concentrated PA medium to 85% H 3 PO 4 has been suggested. A possible secondary 18 O and a primary 18 O kinetic isotope effect in decarbonylation of lactic acid in phosphoric acids media have been discussed, too. (author) 21 refs.; 3 tabs

  20. Ag supported on carbon fiber cloth as the catalyst for hydrazine oxidation in alkaline medium

    International Nuclear Information System (INIS)

    Liu, Ran; Ye, Ke; Gao, Yinyi; Zhang, Wenping; Wang, Guiling; Cao, Dianxue

    2015-01-01

    Highlights: • CFC supported microspherical Ag is obtained by square-wave potential method. • Ag/CFC electrode has high catalytic activity toward hydrazine oxidation. • Hydrazine oxidation on the electrode proceeds by a near 4-electron pathway. - Abstract: Silver particles with microspheric structure are directly electrodeposited on carbon fiber cloth (CFC) substrate by square-wave potential electrodeposition method. The electrocatalytic behaviors of the Ag/CFC electrode toward hydrazine oxidation in alkaline solution are examined by cyclic voltammetry and chronoamperometry. An onset oxidation potential of -0.5 V and a peak current density of 30 mA cm −2 are achieved in the solution containing 1.0 mol L −1 KOH and 20.0 mmol L −1 hydrazine. The microspheric structure of the Ag/CFC electrode provides large electroactive surface area, hence, abundant active sites are vacant for hydrazine oxidation. The calculated apparent activation energies at different potentials show that hydrazine electro-oxidation at higher potential has faster kinetics than that at lower potential. In addition, the transfer electron number of hydrazine oxidation reaction on the Ag/CFC electrode is close to four, suggesting hydrazine is almost completely electrooxidized on the electrode and the full use of hydrazine fuel is basically achieved.

  1. Effects of Rare Earth on Behavior of Precipitation and Properties in Microalloyed Steels

    Institute of Scientific and Technical Information of China (English)

    林勤; 陈邦文; 唐历; 李联生; 朱兴元; 王怀斌

    2003-01-01

    The influence of rare earths on the behavior of precipitation of 14MnNb,X60 and 10MnV steels was studied by STEM, XRD, ICP and thermal simulation method. The main carbonitride precipitates are Nb(C, N),(Nb, Ti)(C, N)and V(C, N). In austenite RE delays the beginning of precipitation, and decreases the rate of precipitation. In ferrite RE promotes precipitation and increases the amount of equilibrium carbonitride precipitation. RE can make precipitates fine, globular and dispersed in the microalloyed steels. With the increase of the amount of RE in steel, the amount of precipitation increases. The promotion effect is weakened with excessive RE. RE has only little influence on the strength of microalloyed steel, but it can improve impact toughness effectively.

  2. Improved ductility and oxidation resistance of cast Ti–6Al–4V alloys by microalloying

    International Nuclear Information System (INIS)

    Luan, J.H.; Jiao, Z.B.; Chen, G.; Liu, C.T.

    2014-01-01

    Highlights: • Modified Ti64 alloys with improved ductility and oxidation resistance are developed. • B improves the ductility by refining grain size and enhancing boundary cohesion. • Y enhances the oxidation resistance by possibly slowing down the oxidation kinetics. - Abstract: The effects of B and Y on the mechanical properties and oxidation behavior of cast Ti–6Al–4V alloys were systematically investigated, and the new alloys with improved ductility and oxidation resistance are developed by the microalloying approach. The results indicate that boron is beneficial for improving the ductility by not only grain-size refinement but also grain-boundary enhancement, while yttrium is effective in increasing the oxidation resistance through possibly slowing down the oxidation kinetics. The improved properties, together with their high strength, make the microalloyed cast Ti–6Al–4V alloys competitive for practical engineering applications

  3. The Microstructure and Properties of Super Martensitic Stainless Steel Microalloyed with Tungsten and Copper

    Science.gov (United States)

    Ye, Dong; Li, Jun; Liu, Yu-Rong; Yong, Qi-Long; Su, Jie; Cao, Jian-Chun; Tao, Jing-Mei; Zhao, Kun-Yu

    2011-06-01

    The microstructure and properties of super martensitic stainless steel (SMSS) microalloyed with tungsten and copper were studied by means of optical microscopy, dilatometer, X-ray diffraction, and tensile tests. The results showed that the microstructure of SMSS, after quenching and tempering, was a typical biphase structure with tempered martensite and reversed austenite dispersedly distributed in the martensite matrix. W and Cu were added into the SMSS to reduce the transformation temperature (Ms) and improve the strength and hardness of the matrix by grain refining and solid solution strengthening. Thermocalc calculations confirmed that M23C6 compound and Laves phase were precipitated during tempering in the investigated steel. Compared with the traditional SMSS, the steel microalloyed with W and Cu performed better mechanical properties.

  4. Extraction and isotopic analysis of medium molecular weight hydrocarbons from Murchison using supercritical carbon dioxide

    Science.gov (United States)

    Gilmour, Iain; Pillinger, Colin

    1993-03-01

    The large variety of organic compounds present in carbonaceous chondrites poses particular problems in their analysis not the least of which is terrestrial contamination. Conventional analytical approaches employ simple chromatographic techniques to fractionate the extractable compounds into broad classes of similar chemical structure. However, the use of organic solvents and their subsequent removal by evaporation results in the depletion or loss of semi-volatile compounds as well as requiring considerable preparative work to assure solvent purity. Supercritical fluids have been shown to provide a powerful alternative to conventional liquid organic solvents used for analytical extractions. A sample of Murchison from the Field Museum was analyzed. Two interior fragments were used; the first (2.85 g) was crushed in an agate pestel and mortar to a grain size of ca. 50-100 micron, the second (1.80 g) was broken into chips 3-8 mm in size. Each sample was loaded into a stainless steel bomb and placed in the extraction chamber of an Isco supercritical fluid extractor maintained at 35 C. High purity (99.9995 percent) carbon dioxide was used and was pressurized using an Isco syringe pump. The samples were extracted dynamically by flowing CO2 under pressure through the bomb and venting via a 50 micron fused filica capillary into 5 mls of hexane used as a collection solvent. The hexane was maintained at a temperature of 0.5 C. A series of extractions were done on each sample using CO2 of increasing density. The principal components extracted in each fraction are summarized.

  5. Simulation Kinetics of Austenitic Phase Transformation in Ti+Nb Stabilized IF and Microalloyed Steels

    Science.gov (United States)

    Ghosh, Sumit; Dasharath, S. M.; Mula, Suhrit

    2018-05-01

    In the present study, the influence of cooling rates (low to ultrafast) on diffusion controlled and displacive transformation of Ti-Nb IF and microalloyed steels has been thoroughly investigated. Mechanisms of nucleation and formation of non-equiaxed ferrite morphologies (i.e., acicular ferrite and bainitic ferrite) have been analyzed in details. The continuous cooling transformation behavior has been studied in a thermomechanical simulator (Gleeble 3800) using the cooling rates of 1-150 °C/s. On the basis of the dilatometric analysis of each cooling rate, continuous cooling transformation (CCT) diagrams have been constructed for both the steels to correlate the microstructural features at each cooling rate in different critical zones. In the case of the IF steel, massive ferrite grains along with granular bainite structures have been developed at cooling rates > 120 °C/s. On the other hand, a mixture of lath bainitic and lath martensite structures has been formed at a cooling rate of 80 °C/s in the microalloyed steel. A strong dependence of the cooling rates and C content on the microstructures and mechanical properties has been established. The steel samples that were fast cooled to a mixture of bainite ferrite and martensite showed a significant improvement of impact toughness and hardness (157 J, for IF steel and 174 J for microalloyed steel) as compared to that of the as-received specimens (133 J for IF steel and 116 J for microalloyed steel). Thus, it can be concluded that the hardness and impact toughness properties are correlated well with the microstructural constituents as indicated by the CCT diagram. Transformation mechanisms and kinetics of austenitic transformation to different phase morphologies at various cooling rates have been discussed in details to correlate microstructural evolution and mechanical properties.

  6. Development of microstructure of niobium-microalloyed steels after deformation in two-phase region

    International Nuclear Information System (INIS)

    Majta, J.; Bator, A.

    1999-01-01

    The inhomogeneity of microstructure development of hot deformed niobium-microalloyed steels in the austenite and two phase region is effectively described using an integrated computer modeling process. In particular, the effect of varying the finish deformation temperature, strain and strain rate on the inhomogeneity of austenite and ferrite structures are studied. Presented here investigations take into account kinetics of recrystallization, phase transformation, and the resulting mechanical properties. (author)

  7. Mechanical behavior of a controlled rolled highstrenght low alloy steeel plate, microalloyed with Nb e V

    International Nuclear Information System (INIS)

    Maria, C.R.; Bruno, J.C.; Gomes, D.T.; Chawla, K.K.

    1986-01-01

    The tension and fatique behaviour of a controlled rolled high-strength low-alloy steel plate, microalloyed with Nb and V, was studied. It was verified that the material showed an anisotropic tensile behaviour. In spite of this anisotropy, it was verified that the fatique crack propagation rates (da/Dn) in the L, T and S directions showed similar results with respect to the two levels of mean applied stress. (Author) [pt

  8. Effect of variable load on crack initiation microalloyed steel S 690-QL

    Directory of Open Access Journals (Sweden)

    M. Burzić

    2015-01-01

    Full Text Available The accumulation of damage in the form of initiation and growth of micro-cracks is the first stage of destruction that ends when the merger microcracks form macro cracks. Cracks formed in the cycle number N =104 - 105 are the result of low cycle fatigue. From the need to evaluate low cycle fatigue life was carried out to investigate the low cycle fatigue microalloyed high-strength steel S690QL in the heat-treated.

  9. Removal of chromium (VI) from water by micro-alloyed aluminium ...

    African Journals Online (AJOL)

    This paper deals with Cr(VI) ion removal from water, by micro-alloyed aluminium composite (MAlC), under flow conditions. In a water environment the MAlC acts as a strong reducing agent. Dissolving it in water is accompanied by the generation of Al(III) ions and reduction of water to H2, with OH- ions. The final product is ...

  10. Welding of Nb micro-alloyed steel by the submerged arc process using Brazilian consumables

    International Nuclear Information System (INIS)

    Scotti, A.; Quites, A.M.

    1982-01-01

    A set of procedures was established for welding of Nb micro-alloyed steel by the submerged arc process, using national consumables, in order to simultaneously achieve a more economic welding and better mechanical properties. From all the wire-flux combinations the better were the correspondent to AWS F84ED1, F74EM12K and F84EH14, the last being the best. (Author) [pt

  11. Microstructure-property relationship in microalloyed high-strength steel welds

    International Nuclear Information System (INIS)

    Zhang, Lei

    2017-01-01

    High-strength steels are favoured materials in the industry for production of safe and sustainable structures. The main technology used for joining the components of such steel is fusion welding. Steel alloy design concepts combined with advanced processing technologies have been extensively investigated during the development of High-Strength Low-Alloy (HSLA) steels. However, very few studies have addressed the issue of how various alloy designs, even with limited microalloy addition, can influence the properties of high-strength steel welds. In high-strength steel welding practices, the challenges regarding microstructure evolution and the resulting mechanical properties variation, are of great interest. The main focus is the debate regarding the role of microalloy elements on phase transformation and weld performance. Limited Heat Affected Zone (HAZ) softening and limited austenite grain coarsening are significant design essentials, but the primary goal is to ensure excellent toughness and tensile properties in the steel weld. To achieve this purpose, microalloy elements such as Ti, Nb, or V were intentionally added to modern high-strength steels. The focus of this work was to understand the mechanical properties of HSLA steels resulting from differences in alloy design after joining by modern welding processes. To begin, three microalloyed S690QL steels (Nb, Ti, and Ti+V addition) were investigated. Optical microscopy confirmed that similar mixtures of tempered bainite and martensite predominated the parent microstructure in the three steels, different types of coarse microalloy precipitates were also visible. These precipitates were analysed by using a thermodynamic-based software and then identified by Transmission Electron Microscopy (TEM). Results of mechanical testing revealed that all three steels performed above the standard toughness and tensile strength values, but with varied yielding phenomena. During the welding operation, each of the three steels

  12. Effect of cooling rate on the microstructure and mechanical properties of Nb-microalloyed steels

    International Nuclear Information System (INIS)

    Shanmugam, S.; Ramisetti, N.K.; Misra, R.D.K.; Mannering, T.; Panda, D.; Jansto, S.

    2007-01-01

    We describe here the effect of cooling rate on the microstructure and mechanical properties of Nb-microalloyed steels that were processed as structural beams at three different cooling rates. Nb-microalloyed steels exhibited increase in yield strength with increase in cooling rate during processing. However, the increase in the yield strength was not accompanied by loss in toughness. The microstructure at conventional cooling rate, primarily consisted of polygonal ferrite-pearlite microconstituents, while at intermediate cooling rate besides polygonal ferrite and pearlite contained significant fraction of degenerated pearlite and lath-type ferrite. At higher cooling rate, predominantly, lath-type (acicular) or bainitic ferrite was obtained. The precipitation characteristics were similar at the three cooling rates investigated with precipitation occurring at grain boundaries, on dislocations, and in the ferrite matrix. The fine scale (∼8-12 nm) precipitates in the ferrite matrix were MC type of niobium carbides. The microstructural studies suggest that the increase in toughness of Nb-microalloyed steels with increase in cooling rate is related to the change in the microstructure from predominantly ferrite-pearlite to predominantly bainitic ferrite

  13. Effect of cooling rate on the microstructure and mechanical properties of Nb-microalloyed steels

    Energy Technology Data Exchange (ETDEWEB)

    Shanmugam, S. [Center for Structural and Functional Materials, University of Louisiana at Lafayette, Lafayette, LA 70504-4130 (United States); Ramisetti, N.K. [Department of Chemical Engineering, University of Louisiana at Lafayette, Lafayette, LA 70504-4130 (United States); Misra, R.D.K. [Center for Structural and Functional Materials, University of Louisiana at Lafayette, Lafayette, LA 70504-4130 (United States); Department of Chemical Engineering, University of Louisiana at Lafayette, Lafayette, LA 70504-4130 (United States)], E-mail: dmisra@louisiana.edu; Mannering, T. [Nucor-Yamato Steel, P.O. Box 1228, 5929 East State Highway 18, Blytheville, AR 72316 (United States); Panda, D. [Nucor-Yamato Steel, P.O. Box 1228, 5929 East State Highway 18, Blytheville, AR 72316 (United States); Jansto, S. [Reference Metals, 1000 Old Pond Road, Bridgeville, PA 15017 (United States)

    2007-07-15

    We describe here the effect of cooling rate on the microstructure and mechanical properties of Nb-microalloyed steels that were processed as structural beams at three different cooling rates. Nb-microalloyed steels exhibited increase in yield strength with increase in cooling rate during processing. However, the increase in the yield strength was not accompanied by loss in toughness. The microstructure at conventional cooling rate, primarily consisted of polygonal ferrite-pearlite microconstituents, while at intermediate cooling rate besides polygonal ferrite and pearlite contained significant fraction of degenerated pearlite and lath-type ferrite. At higher cooling rate, predominantly, lath-type (acicular) or bainitic ferrite was obtained. The precipitation characteristics were similar at the three cooling rates investigated with precipitation occurring at grain boundaries, on dislocations, and in the ferrite matrix. The fine scale ({approx}8-12 nm) precipitates in the ferrite matrix were MC type of niobium carbides. The microstructural studies suggest that the increase in toughness of Nb-microalloyed steels with increase in cooling rate is related to the change in the microstructure from predominantly ferrite-pearlite to predominantly bainitic ferrite.

  14. Electrophysical properties of microalloyed alumo-silicate ceramics as active dielectric

    Directory of Open Access Journals (Sweden)

    Purenović Jelena

    2013-01-01

    Full Text Available In this paper, electrophysical properties of porous alumo-silicate ceramics, modified by alloying with magnesium and microalloying with aluminum, were investigated. Complex multiphase system, as active microalloyed ceramics, has specific behavior under influence of external electrical field, which involves changes of dielectric losses and impedance, depending on frequency and temperature. Dielectric properties were measured in the frequency range 20 Hz - 1 MHz. Values for permittivity (εr ranged between 140 - 430. Order of magnitude for electrical resistivity was about 106 Ωm, for impedance 104 - 108 Ω, and loss tangent had values about and greater than 0.05. Current flow through active dielectric takes place through dielectric barrier and throughout conduction bands of thin aluminum and magnesium metal films. Permittivity has nonlinear distribution and complex functional dependences because of significant nonhomogeneity of active microalloyed ceramics. Lower values of electrical resistivity are the result of complex electron and ion transfer of charge through solid phase and pores, with decreased potential barriers height, due to the influence of additives, ingredients and defects. [Projekat Ministarstva nauke Republike Srbije, br. III 45012 i br. ON 172057

  15. Microstructure-property relationship in microalloyed high-strength steel welds

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Lei

    2017-04-01

    High-strength steels are favoured materials in the industry for production of safe and sustainable structures. The main technology used for joining the components of such steel is fusion welding. Steel alloy design concepts combined with advanced processing technologies have been extensively investigated during the development of High-Strength Low-Alloy (HSLA) steels. However, very few studies have addressed the issue of how various alloy designs, even with limited microalloy addition, can influence the properties of high-strength steel welds. In high-strength steel welding practices, the challenges regarding microstructure evolution and the resulting mechanical properties variation, are of great interest. The main focus is the debate regarding the role of microalloy elements on phase transformation and weld performance. Limited Heat Affected Zone (HAZ) softening and limited austenite grain coarsening are significant design essentials, but the primary goal is to ensure excellent toughness and tensile properties in the steel weld. To achieve this purpose, microalloy elements such as Ti, Nb, or V were intentionally added to modern high-strength steels. The focus of this work was to understand the mechanical properties of HSLA steels resulting from differences in alloy design after joining by modern welding processes. To begin, three microalloyed S690QL steels (Nb, Ti, and Ti+V addition) were investigated. Optical microscopy confirmed that similar mixtures of tempered bainite and martensite predominated the parent microstructure in the three steels, different types of coarse microalloy precipitates were also visible. These precipitates were analysed by using a thermodynamic-based software and then identified by Transmission Electron Microscopy (TEM). Results of mechanical testing revealed that all three steels performed above the standard toughness and tensile strength values, but with varied yielding phenomena. During the welding operation, each of the three steels

  16. Precipitation model in microalloyed steels both isothermal and continuous cooling conditions

    International Nuclear Information System (INIS)

    Medina, S. F.; Quispe, A.; Gomez, M.

    2015-01-01

    Niobium and vanadium precipitates (nitrides and carbides) can inhibit the static recrystallization of austenite but this does not happen for Ti, which form nitrides at high temperatures. RPTT diagrams show the interaction between recrystallization and precipitation allowing study the strain induced precipitation kinetics and precipitate coarsening. Based on Dutta and Sellars expression for the start of strain-induced precipitation in microalloyed steels, a new model has been constructed which takes into account the influence of variables such as microalloying element percentages, strain, temperature, strain rate and grain size. Recrystallization- Precipitation-Time-Temperature (RPTT) diagrams have been plotted thanks to a new experimental study carried out by means of hot torsion tests on approximately twenty microalloyed steels with different Nb, V and Ti contents. Mathematical analysis of the results recommends the modification of some parameters such as the supersaturation ratio (ks) and constant B, which is no longer a constant but a function of ks. The expressions are now more consistent and predict the Precipitation-Time-Temperature (PTT) curves with remarkable accuracy. The model for strain-induced precipitation kinetics is completed by means of Avramis equation. Finally, the model constructed in isothermal testing conditions, it has been converted to continuous cooling conditions in order to apply it in hot rolling. (Author)

  17. Impact of carbon monoxide partial pressures on methanogenesis and medium chain fatty acids production during ethanol fermentation.

    Science.gov (United States)

    Esquivel-Elizondo, Sofia; Miceli, Joseph; Torres, Cesar I; Krajmalnik-Brown, Rosa

    2018-02-01

    Medium-chain fatty acids (MCFA) are important biofuel precursors. Carbon monoxide (CO) is a sustainable electron and carbon donor for fatty acid elongation, since it is metabolized to MCFA precursors, it is toxic to most methanogens, and it is a waste product generated in the gasification of waste biomass. The main objective of this work was to determine if the inhibition of methanogenesis through the continuous addition of CO would lead to increased acetate or MCFA production during fermentation of ethanol. The effects of CO partial pressures (P CO ; 0.08-0.3 atm) on methanogenesis, fatty acids production, and the associated microbial communities were studied in batch cultures fed with CO and ethanol. Methanogenesis was partially inhibited at P CO  ≥ 0.11 atm. This inhibition led to increased acetate production during the first phase of fermentation (0-19 days). However, a second addition of ethanol (day 19) triggered MCFA production only at P CO  ≥ 0.11 atm, which probably occurred through the elongation of acetate with CO-derived ethanol and H 2 :CO 2 . Accordingly, during the second phase of fermentation (days 20-36), the distribution of electrons to acetate decreased at higher P CO , while electrons channeled to MCFA increased. Most probably, Acetobacterium, Clostridium, Pleomorphomonas, Oscillospira, and Blautia metabolized CO to H 2 :CO 2 , ethanol and/or fatty acids, while Peptostreptococcaceae, Lachnospiraceae, and other Clostridiales utilized these metabolites, along with the provided ethanol, for MCFA production. These results are important for biotechnological systems where fatty acids production are preferred over methanogenesis, such as in chain elongation systems and microbial fuel cells. © 2017 Wiley Periodicals, Inc.

  18. Use of activated carbon as a support medium for H2S biofiltration and effect of bacterial immobilization on available pore surface.

    Science.gov (United States)

    Ng, Y L; Yan, R; Chen, X G; Geng, A L; Gould, W D; Liang, D T; Koe, L C C

    2004-12-01

    The use of support media for the immobilization of microorganisms is widely known to provide a surface for microbial growth and a shelter that protects the microorganisms from inhibitory compounds. In this study, activated carbon is used as a support medium for the immobilization of microorganisms enriched from municipal sewage activated sludge to remove gas-phase hydrogen sulfide (H2S), a major odorous component of waste gas from sewage treatment plants. A series of designed experiments is used to examine the effect on bacteria-immobilized activated carbon (termed "biocarbon") due to physical adsorption, chemical reaction, and microbial degradation in the overall removal of H2S. H2S breakthrough tests are conducted with various samples, including microbe-immobilized carbon and Teflon discs, salts-medium-washed carbon, and ultra-pure water-washed carbon. The results show a higher removal capacity for the microbe-immobilized activated carbon compared with the activated carbon control in a batch biofilter column. The increase in removal capacity is attributed to the role played by the immobilized microorganisms in metabolizing adsorbed sulfur and sulfur compounds on the biocarbon, hence releasing the adsorption sites for further H2S uptake. The advantage for activated carbon serving as the support medium is to adsorb a high initial concentration of substrate and progressively release this for microbial degradation, hence acting as a buffer for the microorganisms. Results obtained from surface area and pore size distribution analyses of the biocarbon show a correlation between the available surface area and pore volume with the extent of microbial immobilization and H2S uptake. The depletion of surface area and pore volume is seen as one of the factors which cause the onset of column breakthrough. Microbial growth retardation is due to the accumulation of metabolic products (i.e., sulfuric acid); and a lack of water and nutrient salts in the batch biofilter are other

  19. Hydrothermal Carbonization of Municipal Woody and Herbaceous Prunings: Hydrochar Valorisation as Soil Amendment and Growth Medium for Horticulture

    Directory of Open Access Journals (Sweden)

    Monica Puccini

    2018-03-01

    Full Text Available In this study, we investigate the suitability of hydrochar, produced at industrial scale by hydrothermal carbonization of municipal woody and herbaceous prunings, to be used as soil amendment and peat substitute in organic growth medium for horticulture. Fresh hydrochar and the products of two different hydrochar post-treatments (i.e., washing and aging were compared in terms of potential phytotoxicity throughout physicochemical characterization and germination tests, performed with a sensitive species (Lactuca sativa. The results showed that the fresh hydrochar obtained from municipal green wastes complies with the Italian regulated parameters for the use as soil amendment. Moreover, hydrochar exhibits biological activity and a high content in organic C, Ca, and other micronutrients (Mg, Zn, Cu, Na, Cl. On the other hand, post-treatments are needed before application of hydrochar as peat substitute in potting mix, since appreciable phytotoxic effects on lettuce seed germination and radicle length of plantlets were observed (e.g., germination percentage of 56% and 54%, with 5 and 10 wt % of hydrochar in the blend, respectively. The inhibition of germination could be mainly attributed to the presence of polyphenols (tannins and volatile fatty acids, which were most effectively removed through the aging post-treatment.

  20. Precipitation behavior of the lower bainitic carbide in a medium-carbon steel containing Si, Mn and Mo

    International Nuclear Information System (INIS)

    Liu, J.; Luo, C.P.

    2006-01-01

    The fine microstructure, crystallographic features and ε-carbides precipitation behavior of lower bainite produced by isothermal transformation in a medium-carbon steel containing Si, Mn and Mo were investigated using transmission electronic microscopy. It was found that the microstructure produced by isothermal reaction at 320 deg. C was composed of a large amount of plate-like lower bainite with retained austenite embedded between the plates, and ε-carbides precipitated within them. Midrib and subunits were readily visible in the lower bainite plate. The bainite plate kept a G-T orientation relationship (OR) with the austenite. Selected area electron diffraction patterns of 'three phases in four variants' and analysis indicated that two variants of ε-carbides precipitated in a single bainitic ferrite plate. The two (or three) variants of ε-carbides can simultaneously keep a Jack OR with its 'bainite matrix', while keeping no fixed OR with the austenite. The crystallographic features of ε-carbides precipitated within the bainite were the same as those observed in tempered martensite. The results indicated that the bainitic transformation bore an analogy to the martensitic one in carbide precipitation

  1. High-Performance Complementary Transistors and Medium-Scale Integrated Circuits Based on Carbon Nanotube Thin Films.

    Science.gov (United States)

    Yang, Yingjun; Ding, Li; Han, Jie; Zhang, Zhiyong; Peng, Lian-Mao

    2017-04-25

    Solution-derived carbon nanotube (CNT) network films with high semiconducting purity are suitable materials for the wafer-scale fabrication of field-effect transistors (FETs) and integrated circuits (ICs). However, it is challenging to realize high-performance complementary metal-oxide semiconductor (CMOS) FETs with high yield and stability on such CNT network films, and this difficulty hinders the development of CNT-film-based ICs. In this work, we developed a doping-free process for the fabrication of CMOS FETs based on solution-processed CNT network films, in which the polarity of the FETs was controlled using Sc or Pd as the source/drain contacts to selectively inject carriers into the channels. The fabricated top-gated CMOS FETs showed high symmetry between the characteristics of n- and p-type devices and exhibited high-performance uniformity and excellent scalability down to a gate length of 1 μm. Many common types of CMOS ICs, including typical logic gates, sequential circuits, and arithmetic units, were constructed based on CNT films, and the fabricated ICs exhibited rail-to-rail outputs because of the high noise margin of CMOS circuits. In particular, 4-bit full adders consisting of 132 CMOS FETs were realized with 100% yield, thereby demonstrating that this CMOS technology shows the potential to advance the development of medium-scale CNT-network-film-based ICs.

  2. Joining of CBN abrasive grains to medium carbon steel with Ag-Cu/Ti powder mixture as active brazing alloy

    International Nuclear Information System (INIS)

    Ding, W.F.; Xu, J.H.; Shen, M.; Su, H.H.; Fu, Y.C.; Xiao, B.

    2006-01-01

    In order to develop new generation brazed CBN grinding wheels, the joining experiments of CBN abrasive grains and medium carbon steel using the powder mixture of Ag-Cu alloy and pure Ti as active brazing alloy are carried out at elevated temperature under high vacuum condition. The relevant characteristics of the special powder mixture, the microstructure of the interfacial region, which are both the key factors for determining the joining behavior among the CBN grains, the filler layer and the steel substrate, are investigated extensively by means of differential thermal analysis (DTA), scanning electron microscope (SEM) and energy dispersion spectrometer (EDS), as well X-ray diffraction (XRD) analysis. The results show that, similar to Ag-Cu-Ti filler alloy, Ag-Cu/Ti powder mixture exhibits good soakage capability to CBN grains during brazing. Moreover, Ti in the powder mixture concentrates preferentially on the surface of the grains to form a layer of needlelike Ti-N and Ti-B compounds by chemical metallurgic interaction between Ti, N and B at high temperature. Additionally, based on the experimental results, the brazing and joining mechanism is deeply discussed in a view of thermodynamic criterion and phase diagram of Ti-B-N ternary system

  3. Grain boundary characteristics and texture formation in a medium carbon steel during its austenitic decomposition in a high magnetic field

    International Nuclear Information System (INIS)

    Zhang, Y.D.; Esling, C.; Lecomte, J.S.; He, C.S.; Zhao, X.; Zuo, L.

    2005-01-01

    A 12-T magnetic field has been applied to a medium plain carbon steel during the diffusional decomposition of austenite and the effect of a high magnetic field on the distribution of misorientation angles, grain boundary characteristics and texture formation in the ferrite produced has been investigated. The results show that a high magnetic field can cause a considerable decrease in the frequency of low-angle misorientations and an increase in the occurrence of low Σ coincidence boundaries, in particular the Σ3 of ferrite. This may be attributed to the elevation in the transformation temperature caused by the magnetic field and, therefore, the reduction of the transformation stress. The wider temperature range for grain growth offers longer time to the less mobile Σ boundaries to enlarge their areas. Moreover, the magnetic field can enhance the transverse field-direction fiber ( parallel TFD). It can be assumed that the effects of the field were caused by the dipolar interaction between the magnetic moments of Fe atoms

  4. The intra- and extracellular proteome of Aspergillus niger growing on defined medium with xylose or maltose as carbon substrate

    Directory of Open Access Journals (Sweden)

    Wissing Josef

    2010-04-01

    Full Text Available Abstract Background The filamentous fungus Aspergillus niger is well-known as a producer of primary metabolites and extracellular proteins. For example, glucoamylase is the most efficiently secreted protein of Aspergillus niger, thus the homologous glucoamylase (glaA promoter as well as the glaA signal sequence are widely used for heterologous protein production. Xylose is known to strongly repress glaA expression while maltose is a potent inducer of glaA promoter controlled genes. For a more profound understanding of A. niger physiology, a comprehensive analysis of the intra- and extracellular proteome of Aspergillus niger AB1.13 growing on defined medium with xylose or maltose as carbon substrate was carried out using 2-D gel electrophoresis/Maldi-ToF and nano-HPLC MS/MS. Results The intracellular proteome of A. niger growing either on xylose or maltose in well-aerated controlled bioreactor cultures revealed striking similarities. In both cultures the most abundant intracellular protein was the TCA cycle enzyme malate-dehydrogenase. Moreover, the glycolytic enzymes fructose-bis-phosphate aldolase and glyceraldehyde-3-phosphate-dehydrogenase and the flavohemoglobin FhbA were identified as major proteins in both cultures. On the other hand, enzymes involved in the removal of reactive oxygen species, such as superoxide dismutase and peroxiredoxin, were present at elevated levels in the culture growing on maltose but only in minor amounts in the xylose culture. The composition of the extracellular proteome differed considerably depending on the carbon substrate. In the secretome of the xylose-grown culture, a variety of plant cell wall degrading enzymes were identified, mostly under the control of the xylanolytic transcriptional activator XlnR, with xylanase B and ferulic acid esterase as the most abundant ones. The secretome of the maltose-grown culture did not contain xylanolytic enzymes, instead high levels of catalases were found and

  5. The intra- and extracellular proteome of Aspergillus niger growing on defined medium with xylose or maltose as carbon substrate.

    Science.gov (United States)

    Lu, Xin; Sun, Jibin; Nimtz, Manfred; Wissing, Josef; Zeng, An-Ping; Rinas, Ursula

    2010-04-20

    The filamentous fungus Aspergillus niger is well-known as a producer of primary metabolites and extracellular proteins. For example, glucoamylase is the most efficiently secreted protein of Aspergillus niger, thus the homologous glucoamylase (glaA) promoter as well as the glaA signal sequence are widely used for heterologous protein production. Xylose is known to strongly repress glaA expression while maltose is a potent inducer of glaA promoter controlled genes. For a more profound understanding of A. niger physiology, a comprehensive analysis of the intra- and extracellular proteome of Aspergillus niger AB1.13 growing on defined medium with xylose or maltose as carbon substrate was carried out using 2-D gel electrophoresis/Maldi-ToF and nano-HPLC MS/MS. The intracellular proteome of A. niger growing either on xylose or maltose in well-aerated controlled bioreactor cultures revealed striking similarities. In both cultures the most abundant intracellular protein was the TCA cycle enzyme malate-dehydrogenase. Moreover, the glycolytic enzymes fructose-bis-phosphate aldolase and glyceraldehyde-3-phosphate-dehydrogenase and the flavohemoglobin FhbA were identified as major proteins in both cultures. On the other hand, enzymes involved in the removal of reactive oxygen species, such as superoxide dismutase and peroxiredoxin, were present at elevated levels in the culture growing on maltose but only in minor amounts in the xylose culture. The composition of the extracellular proteome differed considerably depending on the carbon substrate. In the secretome of the xylose-grown culture, a variety of plant cell wall degrading enzymes were identified, mostly under the control of the xylanolytic transcriptional activator XlnR, with xylanase B and ferulic acid esterase as the most abundant ones. The secretome of the maltose-grown culture did not contain xylanolytic enzymes, instead high levels of catalases were found and glucoamylase (multiple spots) was identified as the most

  6. Thermodynamic Calculation of Carbide Precipitate in Niobium Microalloyed Steels

    Institute of Scientific and Technical Information of China (English)

    XU Yun-bo; YU Yong-mei; LIU Xiang-hua; WANG Guo-dong

    2006-01-01

    On the basis of regular solution sublattice model, thermodynamic equilibrium of austenite/carbide in Fe-Nb-C ternary system was investigated. The equilibrium volume fraction, chemical driving force of carbide precipitates and molar fraction of niobium and carbon in solution at different temperatures were evaluated respectively. The volume fraction of precipitates increases, molar fraction of niobium dissolved in austenite decreases and molar fraction of carbon increases with decreasing the niobium content. The driving force increases with the decrease of temperature, and then comes to be stable at relatively low temperatures. The predicted ratio of carbon in precipitates is in good agreement with the measured one.

  7. EXPERIMENTAL ANALYSIS AND ISHIKAWA DIAGRAM FOR BURN ON EFFECT ON MANGANESE SILICON ALLOY MEDIUM CARBON STEEL SHAFT

    Directory of Open Access Journals (Sweden)

    AsmamawTegegne

    2013-12-01

    Full Text Available Burn on/metal penetration is one of the surface defects of metal castings in general and steel castings in particular. A research on the effect of burn on the six ton medium carbon steel shaft for making a roller of cold rolled steel sheet produced at one of the metals industry was carried out. The shaft was cast using sand casting by pouring through riser/feeding head step by step (with time interval of pouring. As it was required to use foam casting method for better surface finish and dimensional accuracy of the cast, the pattern was prepared from polystyrene and embedded by silica sand. Physical observations, photographic analysis, visual inspection, measurement of depth of penetration and fish bone diagram were used as method of results analysis. The shaft produced has strongly affected by sand sintering (burn on/metal penetration. Many reasons may be the case for these defects, however analysis results showed that the use of poorly designed gating system led to turbulence flow, uncontrollable high temperature fused the silica sand and liquid polystyrene penetrated the poorly reclaimed and rammed sand mold as a result of which eroded sand has penetrated the liquid metal deeply and reacted with it, consequently after solidification and finishing the required 240mm diameter of the shaft has reduced un evenly to 133mm minimum and 229mm maximum mm that end in the rejection of the shaft from the product since it is below the required standard for the designed application. In addition, it was not possible to remove the adhered sand by grinding. Thus burn on is included in mechanical type burn on.

  8. Synthesis of inorganic materials in a supercritical carbon dioxide medium. Application to ceramic cross-flow filtration membranes preparation

    International Nuclear Information System (INIS)

    Papet, Sebastien

    2000-01-01

    Membrane separations, using cross-flow mineral ceramic membranes, allows fractionation of aqueous solutions due to the molecular sieve effect and electrostatic charges. To obtain a high selectivity, preparation of new selective ceramic membranes is necessary. We propose in this document two different routes to prepare such cross-flow tubular mineral membranes. In the first exposed method, a ceramic material is used, titanium dioxide, synthesized in supercritical carbon dioxide by the hydrolysis of an organometallic precursor of the oxide. The influence of operating parameters is similar to what is observed during a liquid-phase synthesis (sol-gel process), and leads us to control the size and texture of the prepared particles. This material is then used to prepare mineral membrane with a compressed layer process. The particles are mixed with organic components to form a liquid suspension. A layer is then deposited on the internal surface of a tubular porous support by slip-casting. The layer is then dried and compressed on the support before sintering. The obtained membranes arc in the ultrafiltration range. A second process has been developed in this work. It consists on the hydrolysis, in a supercritical CO 2 medium, of a precursor of titanium dioxide infiltrated into the support. The obtained material is then both deposited on the support but also infiltrated into the porosity. This new method leads to obtain ultrafiltration membranes that retain molecules which molecular weight is round 4000 g.mol -1 . Furthermore, we studied mass transfer mechanisms in cross-flow filtration of aqueous solutions. An electrostatic model, based on generalized Nernst-Planck equation that takes into account electrostatic interactions between solutes and the ceramic material, lead us to obtain a good correlation between experimental results and the numerical simulation. (author) [fr

  9. Medium carbon steel deep drawing: A study on the evolution of mechanical properties, texture and simulations, from cold rolling to the end product

    Energy Technology Data Exchange (ETDEWEB)

    Plaut, Ronald L. [University of Sao Paulo, Sao Paulo (Brazil)], E-mail: rlplaut@usp.br; Padilha, Angelo F. [University of Sao Paulo, Sao Paulo (Brazil); Lima, N.B. [IPEN-CNEN/SP, Sao Paulo (Brazil); Herrera, Clara [Max-Planck-Institut fuer Eisenforschung (Germany); Filho, Antenor Ferreira [Industrial Director, Brasmetal Waelzholz S/A, Diadema (Brazil); Yoshimura, Leandro H. [CCS Consulting, Sao Paulo (Brazil)

    2009-01-15

    Medium carbon steels are mostly used for simple applications; nevertheless new applications have been developed for which good sheet formability is required. This class of steels has an inherent low formability. A medium carbon hot rolled SAE 1050 steel has been selected for this study. It has been cold rolled with reductions in the 7-80% range. Samples have been used to assess the cold work hardening curve. For samples with a 50 and 80% thickness reduction, an annealing heat treatment has been performed to obtain recrystallization. The material has been characterized in the 'as received', cold rolled and annealed conditions, using several methods: optical microscopy, X-ray diffraction (texture), Vickers hardness and tensile testing. The 50% cold rolled and recrystallized material has been further studied in terms of sheet metal formability and texture evolution during the actual stamping of a steel toecap that has been used to validate the finite element simulations.

  10. Modeling of the hot flow behavior of advanced ultra-high strength steels (A-UHSS) microalloyed with boron

    Energy Technology Data Exchange (ETDEWEB)

    Mejía, I., E-mail: imejia@umich.mx [Instituto de Investigaciones Metalúrgicas, Universidad Michoacana de San Nicolás de Hidalgo, Edificio “U”, Ciudad Universitaria, 58066 Morelia, Michoacán (Mexico); Altamirano, G.; Bedolla-Jacuinde, A. [Instituto de Investigaciones Metalúrgicas, Universidad Michoacana de San Nicolás de Hidalgo, Edificio “U”, Ciudad Universitaria, 58066 Morelia, Michoacán (Mexico); Cabrera, J.M. [Departament de Ciència dels Materials i Enginyeria Metallúrgica, ETSEIB – Universitat Politècnica de Catalunya, Av. Diagonal 647, 08028 Barcelona (Spain); Fundació CTM Centre Tecnològic, Av. de las Bases de Manresa, 1, 08240 Manresa (Spain)

    2014-07-29

    In this research work, modeling of the hot flow behavior was carried out in a low carbon advanced ultra-high strength steels (A-UHSS) microalloyed with different amounts of boron (14, 33, 82, 126 and 214 ppm). For this purpose, experimental stress–strain data of uniaxial hot-compression tests over a wide range of temperatures (1223, 1273, 1323 and 1373 K (950, 1000, 1050 and 1100 °C)) and strain rates (10{sup −3}, 10{sup −2} and 10{sup −1} s{sup −1}) were used. The stress–strain relationships as a function of temperature and strain rate were successfully described on the basis of the approach proposed by Estrin, Mecking, and Bergström, together with the classical Avrami equation and the conventional hyperbolic sine function. The analysis of the modeling parameters of the hot flow curves shows that boron additions to A-UHSS play a major role in softening mechanisms rather than on hardening. The peak stress (σ{sub p}) and steady-state stress (σ{sub ss}) values show a decreasing trend with increasing boron content, which indicates that boron additions promote a solid solution softening effect additional to that produced by DRX. The time for 50% recrystallization (t{sub 50%}) tends to increase with boron additions, revealing that boron additions cause a delay of the DRX kinetics during hot deformation. Similarly, the presence of boron in the steel decreases the apparent activation energy for recrystallization (Q{sub t}), indicating that boron additions accelerate the onset of DRX. The constitutive equations developed in this way provided an excellent description of the experimental hot flow curves.

  11. Modeling of the hot flow behavior of advanced ultra-high strength steels (A-UHSS) microalloyed with boron

    International Nuclear Information System (INIS)

    Mejía, I.; Altamirano, G.; Bedolla-Jacuinde, A.; Cabrera, J.M.

    2014-01-01

    In this research work, modeling of the hot flow behavior was carried out in a low carbon advanced ultra-high strength steels (A-UHSS) microalloyed with different amounts of boron (14, 33, 82, 126 and 214 ppm). For this purpose, experimental stress–strain data of uniaxial hot-compression tests over a wide range of temperatures (1223, 1273, 1323 and 1373 K (950, 1000, 1050 and 1100 °C)) and strain rates (10 −3 , 10 −2 and 10 −1 s −1 ) were used. The stress–strain relationships as a function of temperature and strain rate were successfully described on the basis of the approach proposed by Estrin, Mecking, and Bergström, together with the classical Avrami equation and the conventional hyperbolic sine function. The analysis of the modeling parameters of the hot flow curves shows that boron additions to A-UHSS play a major role in softening mechanisms rather than on hardening. The peak stress (σ p ) and steady-state stress (σ ss ) values show a decreasing trend with increasing boron content, which indicates that boron additions promote a solid solution softening effect additional to that produced by DRX. The time for 50% recrystallization (t 50% ) tends to increase with boron additions, revealing that boron additions cause a delay of the DRX kinetics during hot deformation. Similarly, the presence of boron in the steel decreases the apparent activation energy for recrystallization (Q t ), indicating that boron additions accelerate the onset of DRX. The constitutive equations developed in this way provided an excellent description of the experimental hot flow curves

  12. Variations of microstructure and properties of 690 MPa grade low carbon bainitic steel after tempering

    Energy Technology Data Exchange (ETDEWEB)

    Feng, Rui [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan Shandong 250061 (China); School of Materials Science and Engineering, Shandong University, Jinan Shandong 250061 (China); Li, Shengli, E-mail: lishengli@sdu.edu.cn [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan Shandong 250061 (China); School of Materials Science and Engineering, Shandong University, Jinan Shandong 250061 (China); Li, Zhenshun; Tian, Lei [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan Shandong 250061 (China); School of Materials Science and Engineering, Shandong University, Jinan Shandong 250061 (China)

    2012-12-15

    The variations of microstructure, mechanical properties and electrical resistivity of 690 MPa grade low carbon bainitic steel tempered at different temperatures were investigated with Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM) and double-arm Bridge. The results show that the appearance of granular bainite, decomposition of retained austenite, variations of dislocation density and solid solution of microalloying elements are the main reasons for variations of mechanical properties and electrical resistivity. Electrical resistivity reflects the solution content of microalloying elements and variations of dislocation density, which can be used as a fast and effective way to analyze the microstructure of materials.

  13. On the determining role of microstructure of niobium-microalloyed steels with differences in impact toughness

    International Nuclear Information System (INIS)

    Anumolu, R.; Kumar, B. Ravi; Misra, R.D.K.; Mannering, T.; Panda, D.; Jansto, S.G.

    2008-01-01

    The relationship between microstructure and impact toughness was investigated for niobium-microalloyed steels with similar yield strength. The nominal steel composition was similar and any variation in processing history was unintentional. The general microstructure of the investigated steel was similar and consisted of 85% polygonal ferrite and 15% pearlite. Despite these similarities, they exhibited variation in toughness and were classified as high- and low-toughness steels. Detailed microstructural investigation including stereological analysis and electron microscopy implied that toughness is strongly influenced by mean intercept length of polygonal ferrite and pearlite colony, and their distribution, interlamellar spacing, and degenerated pearlite

  14. On the determining role of microstructure of niobium-microalloyed steels with differences in impact toughness

    Energy Technology Data Exchange (ETDEWEB)

    Anumolu, R. [Center for Structural and Functional Materials, University of Louisiana at Lafayette, LA 70504-4130 (United States); Department of Chemical Engineering, University of Louisiana at Lafayette, Lafayette, LA 70504-4130 (United States); Kumar, B. Ravi [Center for Structural and Functional Materials, University of Louisiana at Lafayette, LA 70504-4130 (United States); Misra, R.D.K. [Center for Structural and Functional Materials, University of Louisiana at Lafayette, LA 70504-4130 (United States); Department of Chemical Engineering, University of Louisiana at Lafayette, Lafayette, LA 70504-4130 (United States)], E-mail: dmisra@louisiana.edu; Mannering, T.; Panda, D. [Nucor-Yamato Steel, P.O. Box 1228, 5929 East State Highway 18, Blytheville, AR 72316 (United States); Jansto, S.G. [Reference Metals, 1000 Old Pond Road, Bridgeville, PA 15017 (United States)

    2008-09-15

    The relationship between microstructure and impact toughness was investigated for niobium-microalloyed steels with similar yield strength. The nominal steel composition was similar and any variation in processing history was unintentional. The general microstructure of the investigated steel was similar and consisted of 85% polygonal ferrite and 15% pearlite. Despite these similarities, they exhibited variation in toughness and were classified as high- and low-toughness steels. Detailed microstructural investigation including stereological analysis and electron microscopy implied that toughness is strongly influenced by mean intercept length of polygonal ferrite and pearlite colony, and their distribution, interlamellar spacing, and degenerated pearlite.

  15. Mathematical Modelling of Carbonitride Precipitation during Hot Working in Nb Microalloyed Steels

    Institute of Scientific and Technical Information of China (English)

    2006-01-01

    Based on thermodynamics and kinetics, precipitation behavior of microalloyed steels was analyzed. Deformation greatly promotes isothermal carbonitride precipitation and makes C-curve shift leftwards. The position and shape of C-curve also depend on the content of Nb and N. C-curve shifts leftwards a little when N content increases and the nose temperature is raised with increasing Nb content. Deformation shortened precipitation start time during continuous cooling, raised precipitation start temperature, accelerated precipitation kinetics of carbonitrides. With decreasing the finishing temperature and coiling temperature, the precipitates volume fraction increases and strength increment is raised during hot rolling. The simulated results are in agreementwith experiment results.

  16. Strengthening from Nb-rich clusters in a Nb-microalloyed steel

    International Nuclear Information System (INIS)

    Xie, Kelvin Y.; Zheng, Tianxiao; Cairney, Julie M.; Kaul, Harold; Williams, James G.; Barbaro, Frank J.; Killmore, Chris R.; Ringer, Simon P.

    2012-01-01

    We demonstrate that a Nb-microalloyed ultra-thin cast strip steel can be strengthened substantially without compromising ductility by performing a simple heat treatment at 700 °C for 4 min. The strengthening was attributed to a fine dispersion of Nb-rich solute atom clusters. These clusters had an average size of ∼60 atoms at peak hardness and resembled Guinier–Preston zones in Al–Cu alloys. The application of the Ashby–Orowan equation indicates that these clusters are potent strengthening agents when compared to conventional Nb(C,N) precipitation strengthening.

  17. Atomic force microscopy applied to the quantification of nano-precipitates in thermo-mechanically treated microalloyed steels

    Energy Technology Data Exchange (ETDEWEB)

    Renteria-Borja, Luciano [Instituto Tecnologico de Morelia, Av. Tecnologico No. 1500, Lomas de Santiaguito, 58120 Morelia (Mexico); Hurtado-Delgado, Eduardo, E-mail: hurtado@itmorelia.edu.mx [Instituto Tecnologico de Morelia, Av. Tecnologico No. 1500, Lomas de Santiaguito, 58120 Morelia (Mexico); Garnica-Gonzalez, Pedro [Instituto Tecnologico de Morelia, Av. Tecnologico No. 1500, Lomas de Santiaguito, 58120 Morelia (Mexico); Dominguez-Lopez, Ivan; Garcia-Garcia, Adrian Luis [Centro de Investigacion en Ciencia Aplicada y Tecnologia Avanzada-IPN Unidad Queretaro, Cerro Blanco No. 141, Colinas del Cimatario, 76090 Queretaro (Mexico)

    2012-07-15

    Quantification of nanometer-size precipitates in microalloyed steels has been traditionally performed using transmission electron microscopy (TEM), in spite of its complicated sample preparation procedures, prone to preparation errors and sample perturbation. In contrast to TEM procedures, atomic force microscopy (AFM) is performed on the as-prepared specimen, with sample preparation requirements similar to those for optical microscopy (OM), rendering three-dimensional representations of the sample surface with vertical resolution of a fraction of a nanometer. In AFM, contrast mechanisms are directly related to surface properties such as topography, adhesion, and stiffness, among others. Chemical etching was performed using 0.5% nital, at time intervals between 4 and 20 s, in 4 s steps, until reaching the desired surface finish. For the present application, an average surface-roughness peak-height below 200 nm was sought. Quantification results of nanometric precipitates were obtained from the statistical analysis of AFM images of the microstructure developed by microalloyed Nb and V-Mo steels. Topography and phase contrast AFM images were used for quantification. The results obtained using AFM are consistent with similar TEM reports. - Highlights: Black-Right-Pointing-Pointer We quantified nanometric precipitates in Nb and V-Mo microalloyed steels using AFM. Black-Right-Pointing-Pointer Microstructures of the thermo-mechanically treated microalloyed steels were used. Black-Right-Pointing-Pointer Topography and phase contrast AFM images were used for quantification. Black-Right-Pointing-Pointer AFM results are comparable with traditionally obtained TEM measurements.

  18. Tempering of martensitic steel for fasteners : Effects of micro-alloying on microstructure and mechanical property evolution

    NARCIS (Netherlands)

    Öhlund, C.E.I.C.

    2015-01-01

    The research presented in this thesis aims to deepen our understanding of the effect of micro-alloying on the microstructure and mechanical property evolution during tempering of martensitic steel for fasteners. The ongoing trend of engine down-sizing has led to the need for stronger and more

  19. Influence of Cu alloying on hot ductility of C-Mn-Al and Ti-Nb microalloyed steels

    Directory of Open Access Journals (Sweden)

    Comineli, O.

    2005-12-01

    Full Text Available A beneficial effect of the copper on the hot ductility was observed in Ti-Nb microalloyed steels over the temperature range 800-1,000 °C at the cooling rate of 0.4 °C/s, but no influence at the cooling rate of 4 °C/s. Precipitates containing Nb and Ti were present whose size was coarser in the Cu-bearing grade as cooled at 0.4 °C/s. Cu-bearing precipitates were not found. In the C-Mn-Al steel, no influence of the copper on the hot ductility was recorded, but CuS particles were detected. Two mechanisms are proposed to explain the positive influence of the copper in the microalloyed steel. The first is that the copper atoms in the solid solution affect the activity of the carbon and the nitrogen analogically to the previously observed effect of the silicon, enhancing the precipitation at high temperatures, and another mechanism that the copper atoms can prolong the lifetime of vacancies generated by straining assisting the formation of TiNb-vacancy complexes and thereby coarsening the precipitates.

    Se ha observado un efecto beneficioso del cobre sobre la ductilidad en caliente del acero microaleado al Ti-Nb, en el rango de temperaturas 800-1.000 °C. La influencia fue observada a velocidades de enfriamiento bajas, 0,4 °C/s, mientras que a 4 °C/s no se aprecia. En el acero C-Mn-Al, la influencia de cobre no fue detectada. En el acero microaleado se detectó la presencia de precipidados que contienen niobio y titanio, la dimensión de los cuales es mayor cuando se enfría a 0,4 °C/s. En este acero no se detectó la presencia de precipitados con contenidos de cobre, en contraste con el acero C-Mn-Al, donde sí se observaron partículas de CuS. Se proponen dos mecanismos para explicar la influencia positiva del cobre en aceros microaleados. El primero es el aumento de la actividad de carbono y nitrógeno en austenita debido a presencia de átomos de cobre en solución sólida, con el mismo efecto que el silicio, el cual aumenta la

  20. Use of activated carbon as a support medium for H{sub 2}S biofiltration and effect of bacterial immobilization on available pore surface

    Energy Technology Data Exchange (ETDEWEB)

    Ng, Y.L.; Yan, R.; Chen, X.G.; Geng, A.L.; Liang, D.T.; Koe, L.C.C. [Institute of Environmental Science and Engineering, Nanyang Technological Univ., Singapore (Singapore); Gould, W.D. [Environmental Lab., CANMET, Natural Resources Canada, Ottawa, ON (Canada)

    2004-12-01

    The use of support media for the immobilization of micro-organisms widely known to provide a surface for microbial growth and a shelter that protects the microorganisms from inhibitory compounds. In this study, activated carbon is used as a support medium for the immobilization of microorganisms enriched from municipal sewage activated sludge to remove gas-phase hydrogen sulfide (H{sub 2}S), a major odorous component of waste gas from sewage treatment plants. A series of designed experiments is used to examine the effect on bacteria-immobilized activated carbon (termed ''biocarbon'') due to physical adsorption, chemical reaction and microbial degradation in the overall removal of H{sub 2}S. H{sub 2}S breakthrough tests are conducted with various samples, including micro-immobilized carbon and Teflon discs, salts-medium-washed carbon, and ultra-pure water-washed carbon. The results show a higher removal capacity for the microbe-immobilized activated carbon compared with the activated carbon control in a batch biofilter column. The increase in removal capacity is attributed to the role played by the immobilized micro-organisms in metabolizing adsorbed sulfur and sulfur compounds on the biocarbon, hence releasing the adsorption sites for further H{sub 2}S uptake. The advantage for activated carbon serving as the support medium is to adsorb a high initial concentration of substrate and progressively release this for microbial degradation, hence acting as a buffer for the microorganisms. Results obtained from surface area and pore size distribution analyses of the biocarbon show a correlation between the available surface area and pore volume with the extent of microbial immobilization and H{sub 2}S uptake. The depletion of surface area and pore volume is seen as one of the factors which cause the onset of column breakthrough. Microbial growth retardation is due to the accumulation of metabolic products (i.e., sulfuric acid); and a lack of water and

  1. Culture medium pH influence on Gluconacetobacter physiology: Cellulose production rate and yield enhancement in presence of multiple carbon sources.

    Science.gov (United States)

    Yassine, Fatima; Bassil, Nathalie; Flouty, Roula; Chokr, Ali; Samrani, Antoine El; Boiteux, Gisèle; Tahchi, Mario El

    2016-08-01

    Gluconacetobacter genera are valued for bacterial cellulose (BC) and acetic acid production. BC is produced at optimal yields in classical microbiological media that are expensive for a large scale of production. In addition, BC usage for industrial purposes is limited due to low conversion rate into cellulose and to long incubation duration. In this paper, Gluconacetobacter isolated from apple vinegar was kinetically studied to evaluate cellulose production in presence of different carbon sources. Acetic and citric acid effect on Gluconacetobacter metabolism is clarified. It was shown that Gluconacetobacter uses glucose as a primary carbon source for cells growth and products formation. Acetic acid employment as a co-carbon source in Hestrin Schramm medium showed an increase of 17% in BC yield with a moderate decrease in the crystallite size of the resulting polymer. Copyright © 2016 Elsevier Ltd. All rights reserved.

  2. A methodology for replacement of conventional steel by microalloyed steel in bus tubular structures

    International Nuclear Information System (INIS)

    Cruz, Magnus G.H.; Viecelli, Alexandre

    2008-01-01

    The aim of this article is to show the use of a methodology that allows, in a trustful way and without the need to build up a complete physical model, the replacement of conventional steel by structural microalloyed steel (HSLA) in tubular structure, concerning passengers transport in vehicles with capacity of more than 20 people. The validation of the methodology is based on the ECE R66-00 regulation and on the Brazilian CONTRAN 811/96 resolution, which regulate minimal conditions of safety for this kind of vehicle. The methodology has four sequential and dependent stages, where the main focus is related to the experimental tests through the models that are simplified initially for later calibration using finite element method. Modular structures made of two different materials were tested and analyzed to confirm the present methodology, first the structure made of steel that is used by the bus industry in Brazil was tested and then it was compared with the new microalloyed steel. Experimental values are compared with calculated ones, foreseeing parametric optimisation and keeping the security levels according to legislation

  3. A methodology for replacement of conventional steel by microalloyed steel in bus tubular structures

    Energy Technology Data Exchange (ETDEWEB)

    Cruz, Magnus G.H. [Marcopolo S.A., Unidade Ana Rech, Av. Rio Branco, 4889, Ana Rach, 95060-650 Caxias do Sul (Brazil)], E-mail: magnus@verbonet.com.br; Viecelli, Alexandre [Mechanical Engineering Department, Universidade de Caxias do Sul, Rua Francisco Getulio Vargas, 1130, 95070-560 Caxias do Sul, RS (Brazil)], E-mail: avieceli@ucs.br

    2008-07-01

    The aim of this article is to show the use of a methodology that allows, in a trustful way and without the need to build up a complete physical model, the replacement of conventional steel by structural microalloyed steel (HSLA) in tubular structure, concerning passengers transport in vehicles with capacity of more than 20 people. The validation of the methodology is based on the ECE R66-00 regulation and on the Brazilian CONTRAN 811/96 resolution, which regulate minimal conditions of safety for this kind of vehicle. The methodology has four sequential and dependent stages, where the main focus is related to the experimental tests through the models that are simplified initially for later calibration using finite element method. Modular structures made of two different materials were tested and analyzed to confirm the present methodology, first the structure made of steel that is used by the bus industry in Brazil was tested and then it was compared with the new microalloyed steel. Experimental values are compared with calculated ones, foreseeing parametric optimisation and keeping the security levels according to legislation.

  4. Design Optimization of Microalloyed Steels Using Thermodynamics Principles and Neural-Network-Based Modeling

    Science.gov (United States)

    Mohanty, Itishree; Chintha, Appa Rao; Kundu, Saurabh

    2018-06-01

    The optimization of process parameters and composition is essential to achieve the desired properties with minimal additions of alloying elements in microalloyed steels. In some cases, it may be possible to substitute such steels for those which are more richly alloyed. However, process control involves a larger number of parameters, making the relationship between structure and properties difficult to assess. In this work, neural network models have been developed to estimate the mechanical properties of steels containing Nb + V or Nb + Ti. The outcomes have been validated by thermodynamic calculations and plant data. It has been shown that subtle thermodynamic trends can be captured by the neural network model. Some experimental rolling data have also been used to support the model, which in addition has been applied to calculate the costs of optimizing microalloyed steel. The generated pareto fronts identify many combinations of strength and elongation, making it possible to select composition and process parameters for a range of applications. The ANN model and the optimization model are being used for prediction of properties in a running plant and for development of new alloys, respectively.

  5. Bystander effect in human hepatoma HepG2 cells caused by medium transfers at different times after high-LET carbon ion irradiation

    International Nuclear Information System (INIS)

    Wu Qingfeng; Li Qiang; Jin Xiaodong; Liu Xinguo; Dai Zhongying

    2011-01-01

    Although radiation-induced bystander effects have been well documented in a variety of biological systems, whether irradiated cells have the ability to generate bystander signaling persistently is still unclear and the clinical relevance of bystander effects in radiotherapy remains to be elucidated. This study examines tumor cellular bystander response to autologous medium from cell culture irradiated with high-linear energy transfer (LET) heavy ions at a therapeutically relevant dose in terms of clonogenic cell survival. In vitro experiments were performed using human hepatoma HepG2 cell line exposed to 100 keV/μm carbon ions at a dose of 2 Gy. Two different periods (2 and 12 h) after irradiation, irradiated cell conditioned medium (ICCM) and replenished fresh medium were harvested and then transferred to unirradiated bystander cells. Cellular bystander responses were measured with the different medium transfer protocols. Significant higher survival fractions of unirradiated cells receiving the media from the irradiated cultures at the different times post-irradiation than those of the control were observed. Even replenishing fresh medium for unirradiated cells which had been exposed to the ICCM for 12 h could not prevent the bystander cells from the increased survival fraction. These results suggest that the irradiated cells could release unidentified signal factor(s), which induced the increase in survival fraction for the unirradiated bystander cells, into the media sustainedly and the carbon ions triggered a cascade of signaling events in the irradiated cells rather than secreting the soluble signal factor(s) just at a short period after irradiation. Based on the observations in this study, the importance of bystander effect in clinical radiotherapy was discussed and incorporating the bystander effect into the current radiobiological models, which are applicable to heavy ion radiotherapy, is needed urgently.

  6. Pathways to a low-carbon iron and steel industry in the medium-term : the case of Germany

    NARCIS (Netherlands)

    Arens, Marlene; Worrell, Ernst; Eichhammer, Wolfgang; Hasanbeigi, Ali; Zhang, Qi

    2017-01-01

    The iron and steel industry is a major industrial emitter of carbon dioxide globally and in Germany. If European and German climate targets were set as equal proportional reduction targets (referred to here as “flat” targets) among sectors, the German steel industry would have to reduce its carbon

  7. High Strength-High Ductility Combination Ultrafine-Grained Dual-Phase Steels Through Introduction of High Degree of Strain at Room Temperature Followed by Ultrarapid Heating During Continuous Annealing of a Nb-Microalloyed Steel

    Science.gov (United States)

    Deng, Yonggang; Di, Hongshuang; Hu, Meiyuan; Zhang, Jiecen; Misra, R. D. K.

    2017-07-01

    Ultrafine-grained dual-phase (UFG-DP) steel consisting of ferrite (1.2 μm) and martensite (1 μm) was uniquely processed via combination of hot rolling, cold rolling and continuous annealing of a low-carbon Nb-microalloyed steel. Room temperature tensile properties were evaluated and fracture mechanisms studied and compared to the coarse-grained (CG) counterpart. In contrast to the CG-DP steel, UFG-DP had 12.7% higher ultimate tensile strength and 10.7% greater uniform elongation. This is partly attributed to the increase in the initial strain-hardening rate, decrease in nanohardness ratio of martensite and ferrite. Moreover, a decreasing number of ferrite grains with {001} orientation increased the cleavage fracture stress and increased the crack initiation threshold stress with consequent improvement in ductility UFG-DP steel.

  8. Feasibility studies of a carbon/oxygen logging tool for evaluating the CO2 content of the medium in nuclear device containment

    International Nuclear Information System (INIS)

    West, H.I. Jr.; Glasgow, J.E.

    1983-12-01

    The feasibility of using oil-well bore-hole logging techniques for assaying the carbonate content of a potential shot site has been investigated. The procedure makes use of the detection of the 4439-keV γ ray of carbon and the 6130-keV γ ray of oxygen produced by the inelastic scattering of 14-MeV neutrons in the bore-hole medium. For the needs of the containment program, a sensitivity of detection of CO 2 to less than or equal to 0.02 weight fraction must be achieved. Laboratory measurements indicate that only with considerable development effort could a tool be made that would come close to achieving this goal

  9. Hot deformation behavior of austenite in HSLA-100 microalloyed steel

    International Nuclear Information System (INIS)

    Momeni, A.; Arabi, H.; Rezaei, A.; Badri, H.; Abbasi, S.M.

    2011-01-01

    Research highlights: → The flow stress is well fitted by the exponential constitutive equation. → The average value of apparent activation energy for hot deformation is 377 kJ mol -1 . → A yield point phenomenon is observed on flow curves at high temperatures. → The Avrami exponent is determined around unity for dynamic recrystallization. - Abstract: Dynamic recrystallization of austenite in the Cu-bearing HSLA-100 steel was investigated by hot compression testing at a temperature range of 850-1150 deg. C and a strain rate of 0.001-1 s -1 . The obtained flow curves at temperatures higher than 950 deg. C were typical of DRX while at lower temperatures the flow curves were associated with work hardening without any indication of DRX. At high temperatures, flow stress exhibited a linear relation with temperature while at temperatures below 950 deg. C the behavior changed to non-linear. Hence, the temperature of 950 deg. C was introduced as the T nr of the alloy. All the flow curves showed a yield point elongation like phenomenon which was attributed to the interaction of solute atoms, notably carbon, and moving dislocations. The maximum elongation associated with the yield point phenomenon was observed at about 950 deg. C. Since the maximum yield point elongation was observed about the calculated T nr , it was concluded that carbon atoms were responsible for it. It was also concluded that the temperature at which the yield point elongation reaches the maximum value increases as strain rate rises. The stress and strain of the characteristic points of DRX flow curves were successfully correlated to the Zener-Hollomon parameter, Z, by power-law equations. The constitutive exponential equation was found more precise than the hyperbolic sine equation for modeling the dependence of flow stress on Z. The apparent activation energy for DRX was determined as 377 kJ mol -1 . The kinetics of DRX was modeled by an Avrami-type equation and the Avrami's exponent was

  10. Ferrite morphology and residual phases in continuously cooled low carbon steels

    International Nuclear Information System (INIS)

    Dunne, D.P.

    1999-01-01

    Although much research has been conducted on the isothermal transformation products of medium to high carbon hardenable steels, relatively little has been reported for transformation of low carbon structural steels under continuous cooling conditions. The trend towards reduced carbon levels (less than about 0.1 wt% C) has been driven by demands for formability and weldability, challenging steel designers to maintain strength by microalloying and/or thermomechanical controlled processing. Although control of the ferritic products formed in low carbon steels after hot rolling, normalising and welding is essential in order to ensure adequate strength and toughness, understanding of the microstructures formed on continuous cooling is still limited. In addition, transformation mechanisms remain controversial because of polarisation of researchers into groups championing diffusional and displacive theories for the transformation of austenite over a wide range of cooling rates. The present review compares and draws together the main ferrite classification schemes, and discusses some critical issues on kinetics and mechanisms, in an attempt to rationalise the effects of cooling rate, prior austenite structure and composition on the resulting ferrite structure and its mechanical properties. It is concluded that with increasing cooling rate the ferritic product becomes finer, more plate-like, more dislocated, more carbon supersaturated, more likely to be formed by a displacive mechanism, harder and stronger. Other conclusions are that: (i) 'bainitic ferrite', which is a pervasive form of ferrite in continuously cooled low carbon steels, is different from the conventional upper and lower bainites observed in higher carbon steels, insofar as the co-product 'phase' is typically martensite-austenite islands rather than cementite; and (ii) low carbon bainite rather than martensite is the dominant product at typical fast cooling rates (<500K/s) associated with commercial

  11. Effect of young’s modulus on springback for low, medium and high carbon steels during cold drawing of seamless tubes

    Science.gov (United States)

    Karanjule, D. B.; Bhamare, S. S.; Rao, T. H.

    2018-04-01

    Cold drawing is widely used deformation process for seamless tube manufacturing. Springback is one of the major problem faced in tube drawing. Springback is due to the elastic energy stored in the tubes during forming process. It is found that this springback depends upon Young’s modulus of the material. This paper reports mechanical testing of three grades of steels viz. low carbon steel, medium carbon steel and high carbon steel to measure their Young’s modulus and corresponding springback. The results shows that there is 10-20 % variation in the Young’s modulus and inverse proportion between the springback and Young’s modulus. More the percentage of carbon, more the strength, less the value of Young’s modulus and more will springback. The study further leads to identify optimum die semi angle of 15 degree, land width of 10 mm and drawing speed of 8, 6 and 4 m/min for least springback in all the three grades respectively and die semi angle as a most dominant factor causing springback.

  12. Effects of thermo-mechanical treatment and microalloying with Cr, Nb and Ti on phase transformation in C-Mn steel strips produced by compact strip production process

    International Nuclear Information System (INIS)

    Zhu, Y.Z.; Liang, D.M.; Li, J.C.; Xu, J.P.; Xue, Z.L.

    2011-01-01

    Highlights: → The order of solid solution of carbides influences phase transformation of C-Mn steel in cooling. → Evidences of early stage of solid solution of carbides were provides in the paper. → Transitional state evidences such as carbon enriched regions were observed in this study. - Abstract: The C-Mn steel strips microalloyed with Cr, Nb, Ti was produced by compact strip production process and then heat-treated under different conditions. Optical microscopy, scanning electron microscopy, energy dispersive spectroscopy and transmission electron microscopy were used to investigate phase transformations in the steel after different treatments. It was revealed that the phase transformations upon quenching were greatly affected by the austenization temperature and time. When the steel was annealed at 950 deg. C, carbides of Cr, Mn and Fe were dissolved dramatically, while carbides of Nb and Ti are relatively stable at this temperature. When the temperature increases to 1100 deg. C, the carbides of Nb were dissolved rapidly, while the carbides of Ti still show somewhat stable (partial dissolution). Annealing time influences both the amount and the shapes of carbides in the steel, which leads to different phase transformations in the following air cooling processes. Grain growth in the steel in annealing process strongly depends on the dissolution of carbides on grain boundaries. Additionally, a subsequent rolling after annealing treatment at 950 deg. C lead to obvious precipitation of carbides of Ti and Nb in the steel.

  13. Effect of microalloying on precipitate evolution in ferritic welds and implications for toughness

    International Nuclear Information System (INIS)

    Narayanan, Badri K.; Kovarik, L.; Sarosi, Peter M.; Quintana, Marie A.; Mills, M.J.

    2010-01-01

    Ferritic weld metal deposited with a self-shielded arc-welding process has intentional additions of aluminum, magnesium, titanium and zirconium. This results in a complex precipitation process that has been characterized with a combination of electron microscopy techniques. This work indicates that the formation of a spinel oxide is critical for the nucleation of nitrides of zirconium and titanium and prevents the agglomeration of aluminum rich oxides and the formation of large aluminum nitrides. High-resolution transmission electron microscopy has been used to characterize the core/shell structure of the precipitates with microalloying additions. Thermodynamic modeling of the precipitate formation during solidification is consistent with the microstructural observations. The evolution of precipitate formation is critical to limit large inclusions and improve weld metal toughness.

  14. Solidification of cast iron - A study on the effect of microalloy elements on cast iron

    DEFF Research Database (Denmark)

    Moumeni, Elham

    The present thesis deals with the heat transfer and solidification of ductile and microalloyed grey cast iron. Heterogeneous nucleation of nodular graphite at inclusions in ductile iron during eutectic solidification has been investigated. A series of ductile iron samples with two different...... of the austenite, in the last region to solidify. The superfine graphite which forms in this type of irons is short (10-20µm) and stubby. The microstructure of this kind of graphite flakes in titanium alloyed cast iron is studied using electron microscopy techniques. The methods to prepare samples of cast iron...... for comprehensive transmission electron microscopy of graphite and the surrounding iron matrix have been developed and explained. Dual beam microscopes are used for sample preparation. A TEM study has been carried out on graphite flakes in grey cast iron using selected area electron diffraction (SAED). Based...

  15. Semisolid forming of 44MnSiV6 microalloyed steel

    Science.gov (United States)

    Plata, Gorka; Lozares, Jokin; Hurtado, Iñaki; Azpilgain, Zigor; Idoyaga, Zuriñe

    2018-05-01

    Globalisation is forcing many sectors to be more cost-effective due to the low manpower cost of developing countries. This, in combination with European trends of green production and reduction of emissions, enhances the necessity of advanced technologies to remain at the forefront of the market. It is precisely in this field where the Semisolid forming (SSF) exhibits a great potential. In Mondragon Unibertsitatea, it has been demonstrated the capability of producing sound components of 42CrMo4 and S48C steels by saving material, energy and attaining as hot forged properties. To make the process even more cost-effective, it has also been proved the capacity of SSF 44MnSiV6 microalloyed steel that enables the striking of the post processing heat treatment.

  16. Effect of niobium clustering and precipitation on strength of an NbTi-microalloyed ferritic steel

    International Nuclear Information System (INIS)

    Kostryzhev, A.G.; Al Shahrani, A.; Zhu, C.; Cairney, J.M.; Ringer, S.P.; Killmore, C.R.; Pereloma, E.V.

    2014-01-01

    The microstructure–property relationship of an NbTi-microalloyed ferritic steel was studied as a function of thermo-mechanical schedule using a Gleeble 3500 simulator, optical and scanning electron microscope, and atom probe tomography. Contributions to the yield stress from grain size, solid solution, work hardening, particle and cluster strengthening were calculated using the established equations and the measured microstructural parameters. With a decrease in the austenite deformation temperature the yield stress decreased, following a decrease in the number density of >20 nm Nb-rich particles and ≈5 nm Nb-C clusters, although the grain refinement contribution increased. To achieve the maximum cluster/precipitation strengthening in ferrite, the austenite deformation should be carried out in the recrystallisation temperature region where there is a limited tendency for strain-induced precipitation. Based on the analysis of cluster strengthening increment, it could be suggested that the mechanism of dislocation–cluster interaction is closer to shearing than looping

  17. Effect of niobium clustering and precipitation on strength of an NbTi-microalloyed ferritic steel

    Energy Technology Data Exchange (ETDEWEB)

    Kostryzhev, A.G., E-mail: kostryzhev@yahoo.com [School of Mechanical, Materials and Mechatronic Engineering, University of Wollongong, NSW 2500 (Australia); Al Shahrani, A. [School of Mechanical, Materials and Mechatronic Engineering, University of Wollongong, NSW 2500 (Australia); Zhu, C.; Cairney, J.M.; Ringer, S.P. [Australian Centre for Microscopy and Microanalysis, The University of Sydney, NSW 2006 (Australia); School of Aerospace, Mechanical and Mechatronic Engineering, The University of Sydney, NSW 2006 (Australia); Killmore, C.R. [BlueScope Steel Limited, Five Islands Road, Port Kembla, NSW 2505 (Australia); Pereloma, E.V. [School of Mechanical, Materials and Mechatronic Engineering, University of Wollongong, NSW 2500 (Australia); UOW Electron Microscopy Centre, University of Wollongong, NSW 2519 (Australia)

    2014-06-01

    The microstructure–property relationship of an NbTi-microalloyed ferritic steel was studied as a function of thermo-mechanical schedule using a Gleeble 3500 simulator, optical and scanning electron microscope, and atom probe tomography. Contributions to the yield stress from grain size, solid solution, work hardening, particle and cluster strengthening were calculated using the established equations and the measured microstructural parameters. With a decrease in the austenite deformation temperature the yield stress decreased, following a decrease in the number density of >20 nm Nb-rich particles and ≈5 nm Nb-C clusters, although the grain refinement contribution increased. To achieve the maximum cluster/precipitation strengthening in ferrite, the austenite deformation should be carried out in the recrystallisation temperature region where there is a limited tendency for strain-induced precipitation. Based on the analysis of cluster strengthening increment, it could be suggested that the mechanism of dislocation–cluster interaction is closer to shearing than looping.

  18. Study of the structural damage in a niobium-microalloyed steel sheet

    International Nuclear Information System (INIS)

    Fernandes, J.; Riba, J.; Verdeja, J.I.

    1986-01-01

    A quantitative experimental study of the damage developed as a consequence of straining has been performed on a microalloyed (niobium) steel sheet by means of a SEM. Equivalent strains range between 0 and 0.68 and strain paths between 0 and 1 and have been obtained in a bulge test. Damage associated to Al 2 O 3 and SMn inclusions is already present in the ''as received'' sheet and grows with strain. Damage associated to CFe 3 second phase particles appears later in the forming of the sheet. For stages previous to necking SMn stringers have dramatically developed more than 50% of total damage. The nucleation equivalent strain is between 0,3 and 0,4. (author)

  19. State parameter-based modelling of microstructure evolution in micro-alloyed steel during hot forming

    International Nuclear Information System (INIS)

    Buken, H; Kozeschnik, E

    2016-01-01

    In steel production, thermo-mechanical treatment at elevated temperatures is an inevitable step for controlling the microstructure and, thus, the mechanical-technological properties of the final product. One of the main goals in modelling microstructure evolution is the prediction of progress and interaction of hardening and softening mechanism at temperatures, where reheating, hot rolling, finish rolling and coiling are typically carried out. The main mechanisms that need to be accounted for are precipitation, grain growth, solute drag, recovery, recrystallization and phase transformation, which are to be described as functions of temperature, external loading and chemical composition of the material. In the present work, we present a new approach for dealing with these problems and apply it to the thermal and mechanical loading of microalloyed steel. Within this model, we quantitatively predict, for instance, the phenomenon of recrystallization stop in the presence of precipitation. The computational treatment is verified against experimental data from literature, where good agreement is achieved. (paper)

  20. Microstructure and microtexture evolutions of deformed oxide layers on a hot-rolled microalloyed steel

    International Nuclear Information System (INIS)

    Yu, Xianglong; Jiang, Zhengyi; Zhao, Jingwei; Wei, Dongbin; Zhou, Cunlong; Huang, Qingxue

    2015-01-01

    Highlights: • Microtexture development of deformed oxide layers is investigated. • Magnetite shares the {0 0 1} fibre texture with wustite. • Hematite develops the {0 0 0 1} basal fibre parallel to the oxide growth. • Stress relief and ion vacancy diffusion mechanism for magnetite seam. - Abstract: Electron backscatter diffraction (EBSD) analysis has been presented to investigate the microstructure and microtexture evolutions of deformed oxide scale formed on a microalloyed steel during hot rolling and accelerated cooling. Magnetite and wustite in oxide layers share a strong {0 0 1} and a weak {1 1 0} fibres texture parallel to the oxide growth. Trigonal hematite develops the {0 0 0 1} basal fibre parallel to the crystallographic plane {1 1 1} in magnetite. Taylor factor estimates have been conducted to elucidate the microtexture evolution. The fine-grained magnetite seam adjacent to the substrate is governed by stress relief and ions vacancy diffusion mechanism

  1. Influence of austenite grain size on recrystallisation-precipitation interaction in a V-microalloyed steel

    International Nuclear Information System (INIS)

    Quispe, A.; Medina, S.F.; Gomez, M.; Chaves, J.I.

    2007-01-01

    By means of torsion tests using small specimens, the influence of austenite grain size on strain induced precipitation kinetics has been determined in a vanadium microalloyed steel. Determination of recrystallisation-precipitation-time-temperature (RPTT) diagrams for two austenite grain sizes allows values of the aforementioned magnitudes to be determined. An ample discussion is made of the quantitative influence found and its relation with nucleation and growth mechanisms of precipitates. The results are compared with the quantitative influence exerted by the other variables, reaching the conclusion that the austenite grain size has a notable influence on strain induced precipitation kinetics which should not be underestimated. Finally, the influence of austenite grain size is included in a strain induced precipitation model constructed by the authors of this work and which also takes into account the other aforementioned variables

  2. Improving precipitation hardening behavior of Mg−Zn based alloys with Ce−Ca microalloying additions

    Energy Technology Data Exchange (ETDEWEB)

    Langelier, B., E-mail: langelb@mcmaster.ca [Mechanical & Mechatronics Engineering, The University of Waterloo, N2L 3G1 (Canada); Canadian Centre for Electron Microscopy, McMaster University, L8S 4L8 (Canada); Korinek, A. [Canadian Centre for Electron Microscopy, McMaster University, L8S 4L8 (Canada); Donnadieu, P. [Univ. Grenoble Alpes, SIMAP, F-38000 Grenoble (France); CNRS, SIMAP, F-38000 Grenoble (France); Esmaeili, S. [Mechanical & Mechatronics Engineering, The University of Waterloo, N2L 3G1 (Canada)

    2016-10-15

    The precipitation hardening behavior of newly developed Mg−Zn−Ca−Ce alloys, with modified texture and improved ductility, is studied to delineate the microstructural characteristics that lead to effective hardening upon ageing treatments. Advanced electron microscopy and atom probe techniques are used to analyze the structural characteristics in relevance to the hardening potential. It has been found that the formation of a new basal precipitate phase, which evolves from a single atomic layer GP zone, and is finely distributed in both under-aged and peak-aged microstructures, has a significant impact in the improvement of the hardening response compared with the base Mg−Zn alloys. It has also been found that the β′{sub 1} rod precipitates, commonly formed during ageing treatments of Mg−Zn alloys, have their size and distribution significantly refined in the Ca−Ce containing alloys. The role of alloy chemistry in the formation of the fine basal plate GP zones and the refinement in β′{sub 1} precipitation and their relationships to the hardening behavior are discussed. It is proposed that Ca microalloying governs the formation of the GP zones and the enhancement of hardening, particularly in the under-aged conditions, but that this is aided by a beneficial effect from Ce. - Highlights: • Ce−Ca microalloying additions improve hardening in Mg−Zn, over Ce or Ca alone. • Improved hardening is due to refined β′{sub 1} rods, and fine basal plate precipitates. • Atom probe tomography identifies Ca in both β′{sub 1} and the fine basal plates. • The fine basal plates originate as ordered monolayer GP zones with 1:1 Zn:Ca (at.%). • With ageing GP zones become more Zn-rich and transform to the fine basal plates.

  3. Hot tensile behaviour in silicon-killed boron microalloyed steels

    Science.gov (United States)

    Chown, Lesley H.; Cornish, Lesley A.

    2017-10-01

    Low carbon steel for drawing and cold heading applications should have low strength, high ductility and low strain ageing rates. To achieve this, nitrogen must be removed from solid solution, which can be done by low additions of boron. A wire producer had been experiencing occasional problems with severe cracking on silicon-killed, boron steel billets during continuous casting, but the solution was not obvious. Samples from four billets, each from different casts, were removed for analysis and testing. The tested steel compositions were within the specification limits, with boron to nitrogen ratios of 0.40-1.19. Hot ductility testing was performed on a Gleeble 1500 using parameters approximating the capabilities of this particular billet caster. The steel specimens were subjected to in situ melting, then cooled at a rate of 2 C.s-1 to temperatures in the range 750-1250°C, where they were then pulled to failure at a strain rate of 8x10-4 s-1. In this work, it was found that both the boron to nitrogen ratio and the manganese to sulphur ratio influenced the hot ductility and hence the crack susceptibility. Excellent hot ductility was found for B:N ratios above 1.0, which confirmed that the B:N ratio should be above a stoichiometric value of 0.8 to remove all nitrogen from solid solution. TEM analysis showed that coarse BN precipitates nucleated on other precipitates, such as (Fe,Mn)S, which have relatively low melting points, and are detrimental to hot ductility. Low Mn:S ratios of 10 - 12 were shown to promote precipitation of FeS, so a Mn:S > 14 was recommended. A narrower billet surface temperature range for straightening was recommended to prevent transverse surface cracking. Additionally, analysis of industrial casting data showed that the scrap percentage due to transverse cracking increased significantly for Mn:S < 14. An exponential decay relationship between the manganese to sulphur ratio and the average scrap percentage due to transverse cracking was

  4. Vibration and instability of a viscous-fluid-conveying single-walled carbon nanotube embedded in a visco-elastic medium

    International Nuclear Information System (INIS)

    Soltani, P; Farshidianfar, A; Taherian, M M

    2010-01-01

    In this study, for the first time, the transverse vibrational model of a viscous-fluid-conveying single-walled carbon nanotube (SWCNT) embedded in biological soft tissue is developed. Nonlocal Euler-Bernoulli beam theory has been used to investigate fluid-induced vibration of the SWCNT while visco-elastic behaviour of the surrounding tissue is simulated by the Kelvin-Voigt model. The results indicate that the resonant frequencies and the critical flow velocity at which structural instability of nanotubes emerges are significantly dependent on the properties of the medium around the nanotube, the boundary conditions, the viscosity of the fluid and the nonlocal parameter. Detailed results are demonstrated for the dependence of damping and elastic properties of the medium on the resonant frequencies and the critical flow velocity. Three standard boundary conditions, namely clamped-clamped, clamped-pinned and pinned-pinned, are applied to study the effect of the supported end conditions. Furthermore, it is found that the visco-elastic foundation causes an obvious reduction in the critical velocity in comparison with the elastic foundation, in particular for a compliant medium, pinned-pinned boundary condition, high viscosity of the fluid and small values of the nonlocal coefficient.

  5. Solvent--solvent extraction of rhodium-103m from ruthenium-103 employing a sulfate-carbon tetrachloride medium

    International Nuclear Information System (INIS)

    Epperson, C.E.; Landolt, R.R.; Kessler, W.V.

    1976-01-01

    /sup 103m/Rh in equilibrium with parent 103 Ru was separated in yields of 94 percent of those theoretically possible. 103 Ru chloride was first converted to the tetroxide which was then extracted from an aqueous solution of the equilibrium mixture with carbon tetrachloride

  6. Tempering of martensitic steel for fasteners: Effects of micro-alloying on microstructure and mechanical property evolution

    OpenAIRE

    Öhlund, C.E.I.C.

    2015-01-01

    The research presented in this thesis aims to deepen our understanding of the effect of micro-alloying on the microstructure and mechanical property evolution during tempering of martensitic steel for fasteners. The ongoing trend of engine down-sizing has led to the need for stronger and more temperature resistant fasteners than currently available according to international standards. A new martensitic fastener steel called KNDS4 has been developed, that combines higher strength with improve...

  7. New 1H-pyrrole-2,5-dione derivatives as efficient organic inhibitors of carbon steel corrosion in hydrochloric acid medium: Electrochemical, XPS and DFT studies

    International Nuclear Information System (INIS)

    Zarrouk, A.; Hammouti, B.; Lakhlifi, T.; Traisnel, M.; Vezin, H.; Bentiss, F.

    2015-01-01

    Highlights: • 1H-pyrrole derivatives act as good corrosion inhibitors for carbon steel in 1 M HCl. • Adsorption of the inhibitors on carbon steel surface obeys Langmuir’s isotherm. • XPS showed that the inhibitors are chemisorbed on the metal surface. • Quantum chemical parameters were correlated with experimental results. - Abstract: New 1H-pyrrole-2,5-dione derivatives, namely 1-phenyl-1H-pyrrole-2,5-dione (PPD) and 1-(4-methylphenyl)-1H-pyrrole-2,5-dione (MPPD) were synthesised and their inhibitive action against the corrosion of carbon steel in 1 M HCl solution were investigated at 308 K by weight loss, potentiodynamic polarization curves, and electrochemical impedance spectroscopy (EIS) methods. The results showed that the investigated 1H-pyrrole-2,5-dione derivatives are good corrosion inhibitors for carbon steel in 1 M HCl medium, their inhibition efficiency increased with inhibitor concentration, and MPPD is slightly more effective than PPD. Potentiostatic polarization study showed that PPD and MPPD are mixed-type inhibitors in 1 M HCl. Impedance experimental data revealed a frequency distribution of the capacitance, simulated as constant phase element. The results obtained from electrochemical and weight loss studies were in reasonable agreement. The adsorption of MPPD and PPD on steel surface obeyed Langmuir’s adsorption isotherm. Thermodynamic data and XPS analysis clearly indicated that the adsorption mechanism of 1H-pyrrole-2,5-dione derivatives on carbon steel surface in 1 M HCl solution is mainly controlled by a chemisorption process. Quantum chemical calculations using the Density Functional Theory (DFT) were performed on 1H-pyrrole-2,5-dione derivatives to determine the relationship between molecular structures and their inhibition efficiencies

  8. Monte Carlo Calculations of Dose to Medium and Dose to Water for Carbon Ion Beams in Various Media

    DEFF Research Database (Denmark)

    Herrmann, Rochus; Petersen, Jørgen B.B.; Jäkel, Oliver

    treatment plans. Here, we quantisize the effect of dose to water vs. dose to medium for a series of typical target materials found in medical physics. 2     Material and Methods The Monte Carlo code FLUKA [Battistioni et al. 2007] is used to simulate the particle fluence spectrum in a series of target...... for water. This represents the case that our “detector” is an infinitesimal small non-perturbing entity made of water, where charged particle equilibrium can be assumed following the Bragg-Gray cavity theory. Dw and Dm are calculated for typical materials such as bone, brain, lung and soft-tissues using...

  9. Comparative Effect of Mo and Cr on Microstructure and Mechanical Properties in NbV-Microalloyed Bainitic Steels

    Directory of Open Access Journals (Sweden)

    Andrii Kostryzhev

    2018-02-01

    Full Text Available Steel product markets require the rolled stock with further increasing mechanical properties and simultaneously decreasing price. The steel cost can be reduced via decreasing the microalloying elements contents, although this decrease may undermine the mechanical properties. Multi-element microalloying with minor additions is the route to optimise steel composition and keep the properties high. However, this requires deep understanding of mutual effects of elements on each other’s performance with respect to the development of microstructure and mechanical properties. This knowledge is insufficient at the moment. In the present work we investigate the microstructure and mechanical properties of bainitic steels microalloyed with Cr, Mo, Nb and V. Comparison of 0.2 wt. % Mo and Cr additions has shown a more pronounced effect of Mo on precipitation than on phase balance. Superior strength of the MoNbV-steel originated from the strong solid solution strengthening effect. Superior ductility of the CrNbV-steel corresponded to the more pronounced precipitation in this steel. Nature of these mechanisms is discussed.

  10. The potential significance of microalloying with niobium in governing very high cycle fatigue behavior of bainite/martensite multiphase steels

    International Nuclear Information System (INIS)

    Zhao, P.; Cheng, C.; Gao, G.; Hui, W.; Misra, R.D.K.; Bai, B.; Weng, Y.

    2016-01-01

    We elucidate here the effect of microalloying with niobium (Nb) on very high cycle fatigue (VHCF) behavior in high-strength C–Mn–Si–Cr bainite/martensite (B/M) multiphase steels studied through ultrasonic fatigue testing. The tensile strength (R_m) and fatigue limit strength after 10"9 cycles (σ_w_9) and in the non-failure condition of the steel microalloyed with Nb were 1640 MPa and 900 MPa, respectively. Thus, the value of σ_w_9/R_m exceeded in comparison to conventional steels and was approximate 0.55. Three types of failure modes were observed in Nb-bearing steels depending on the surface condition, inclusion, and the matrix microstructure, i.e., surface defect-induced failure mode (S-mode), inclusion-induced failure mode (I-mode), and non-inclusion induced failure mode (N-mode). Only two failure modes were observed in Nb-free steels, the S-mode and the N-mode. The study clearly suggests that Nb had a distinct effect on the VHCF properties of B/M steels. The VHCF limit of Nb-bearing steel was enhanced by 200 MPa because of refinement of the microstructure and pinning of dislocations by randomly distributed nanometer-sized Nb(C, N) precipitates. It is underscored that microalloying with Nb is a potential approach to enhance VHCF properties in advanced high-strength steels.

  11. Performance of carbon nanofiber supported Pd-Ni catalysts for electro-oxidation of ethanol in alkaline medium

    Science.gov (United States)

    Maiyalagan, T.; Scott, Keith

    Carbon nanofibers (CNF) supported Pd-Ni nanoparticles have been prepared by chemical reduction with NaBH 4 as a reducing agent. The Pd-Ni/CNF catalysts were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electrochemical voltammetry analysis. TEM showed that the Pd-Ni particles were quite uniformly distributed on the surface of the carbon nanofiber with an average particle size of 4.0 nm. The electro-catalytic activity of the Pd-Ni/CNF for oxidation of ethanol was examined by cyclic voltammetry (CV). The onset potential was 200 mV lower and the peak current density four times higher for ethanol oxidation for Pd-Ni/CNF compared to that for Pd/C. The effect of an increase in temperature from 20 to 60 °C had a great effect on increasing the ethanol oxidation activity.

  12. Performance of carbon nanofiber supported Pd-Ni catalysts for electro-oxidation of ethanol in alkaline medium

    Energy Technology Data Exchange (ETDEWEB)

    Maiyalagan, T.; Scott, Keith [School of Chemical Engineering and Advanced Materials, University of Newcastle upon Tyne, Newcastle upon Tyne NE1 7RU (United Kingdom)

    2010-08-15

    Carbon nanofibers (CNF) supported Pd-Ni nanoparticles have been prepared by chemical reduction with NaBH{sub 4} as a reducing agent. The Pd-Ni/CNF catalysts were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electrochemical voltammetry analysis. TEM showed that the Pd-Ni particles were quite uniformly distributed on the surface of the carbon nanofiber with an average particle size of 4.0 nm. The electro-catalytic activity of the Pd-Ni/CNF for oxidation of ethanol was examined by cyclic voltammetry (CV). The onset potential was 200 mV lower and the peak current density four times higher for ethanol oxidation for Pd-Ni/CNF compared to that for Pd/C. The effect of an increase in temperature from 20 to 60 C had a great effect on increasing the ethanol oxidation activity. (author)

  13. High content of pyridinic- and pyrrolic-nitrogen-modified carbon nanotubes derived from blood biomass for the electrocatalysis of oxygen reduction reaction in alkaline medium

    International Nuclear Information System (INIS)

    Zheng, Jie; Guo, Chaozhong; Chen, Chunyan; Fan, Mingzhi; Gong, Jianping; Zhang, Yanfang; Zhao, Tianxin; Sun, Yuelin; Xu, Xiaofan; Li, Mengmeng; Wang, Ran; Luo, Zhongli; Chen, Changguo

    2015-01-01

    Graphical abstract: Display Omitted -- Highlights: •An ORR electrocatalyst was fabricated from blood biomass and carbon nanotube. •The N-CNT catalyst exhibits good ORR activity, methanol resistance and stability. •The pyrolysis process produces high contents of pyridinic and pyrrolic N species. •The pyridinic-N group may play more important role in the active sites for ORR. -- Abstract: Here we present a facile synthetic route to design nitrogen-doped nanostructured carbon-based electrocatalyst for oxygen reduction reaction (ORR) by the copyrolysis of blood biomass from pig and carbon nanotubes (CNTs) at high temperatures. The nitrogen-doped CNTs obtained at 800 °C not only results in excellent ORR activity with four-electron transfer selectivity in alkaline medium, but also exhibits superior methanol-tolerant property and long-term stability. It is confirmed that high-temperature pyrolysis processes can facilitate to produce higher contents of pyridinic- and pyrrolic-N binding groups in electrocatalysts, contributing to the enhancement of ORR performance in terms of onset potential, half-wave potential, and limited current density. We also propose that the planar-N configuration may be the active site that is responsible for the improved ORR electrocatalytic performance. The straight-forward and cheap synthesis of the active and stable electrocatalyst makes it a promising candidate for electrochemical power sources such as fuel cells or metal-air batteries

  14. Effect of starting microstructure upon the nucleation sites and distribution of graphite particles during a graphitising anneal of an experimental medium-carbon machining steel

    Energy Technology Data Exchange (ETDEWEB)

    Inam, A., E-mail: aqil.ceet@pu.edu.pk; Brydson, R., E-mail: mtlrmdb@leeds.ac.uk; Edmonds, D.V., E-mail: d.v.edmonds@leeds.ac.uk

    2015-08-15

    The potential for using graphite particles as an internal lubricant during machining is considered. Graphite particles were found to form during graphitisation of experimental medium-carbon steel alloyed with Si and Al. The graphite nucleation sites were strongly influenced by the starting microstructure, whether ferrite–pearlite, bainite or martensite, as revealed by light and electron microscopy. Favourable nucleation sites in the ferrite–pearlite starting microstructure were, not unexpectedly, found to be located within pearlite colonies, no doubt due to the presence of abundant cementite as a source of carbon. In consequence, the final distribution of graphite nodules in ferrite–pearlite microstructures was less uniform than for the bainite microstructure studied. In the case of martensite, this study found a predominance of nucleation at grain boundaries, again leading to less uniform graphite dispersions. - Highlights: • Metallography of formation of graphite particles in experimental carbon steel. • Potential for using graphite in steel as an internal lubricant during machining. • Microstructure features expected to influence improved machinability studied. • Influence of pre-anneal starting microstructure on graphite nucleation sites. • Influence of pre-anneal starting microstructure on graphite distribution. • Potential benefit is new free-cutting steel compositions without e.g. Pb alloying.

  15. Effect of the hypo and hyperstoichiometry of niobium about the solidification of steel with medium carbon content

    International Nuclear Information System (INIS)

    Kestenbach, H.-J.; Rodrigues, J.A.; Makray, E.T.

    1984-01-01

    The solidification sequency and the microstructure from carbon steel with 0.4%C and several content of Nb were investigated. Additions between 1 and 5% in Nb weight to obtain compositions hypo and hyperstoichiometric in relation to the niobium carbide formation were used. The metallographic observations were interpreted based in several solidifications reactions that could be occur in the iron rich region of the ternary diagram Fe-Nb-C. (E.G.) [pt

  16. Durability of carbon-supported manganese oxide nanoparticles for the oxygen reduction reaction (ORR) in alkaline medium

    Czech Academy of Sciences Publication Activity Database

    Roche, I.; Chainet, E.; Chatenet, M.; Vondrák, Jiří

    2008-01-01

    Roč. 38, č. 9 (2008), s. 1195-1201 ISSN 0021-891X R&D Projects: GA AV ČR KJB4813302; GA ČR GA104/02/0731 Grant - others:CNRS(FR) 18105 Institutional research plan: CEZ:AV0Z40320502 Keywords : oxygen reduction reaction * rotating ring-disc electrode * carbon-supported manganese oxide Subject RIV: CA - Inorganic Chemistry Impact factor: 1.540, year: 2008

  17. Influence of carbon dioxide, temperature, medium kind and light intensity on the growth of algae Chlamydomonas reinhardtii and Scenedesmus obliquus

    Directory of Open Access Journals (Sweden)

    Olejnik Przemysław Piotr

    2016-01-01

    Full Text Available Microalgae attracts the attention of scientists because of the possibility of using in the energy industry as one of the substrates for the production of renewable energy. So far, the greatest emphasis was put on attempts to obtain strains, and technologies of their culturing, in order to efficiently acquire fat from cells and its further conversion to biodiesel using transesterification reaction. Increasingly, algae are considered also as an efficient biomass producer, which can be used as a substrate for methane production in biogas plants. In this study the influence of different physical and chemical conditions, on the growth of two algae species: Chlamydomonasreinhardtii and Scenedesmus obliquus was investigated. Based on the literature and the data obtained for the algae growth on the standard medium and the digestate remaining after fermentation, one may suggest further investigations on the use of other liquid waste from agriculture and industry for algae breeding, including chemical. analysis and supplementation of these mediums so as to provide the best conditions for their growth.

  18. Effects of carbon content and chromium segregation on creep rupture properties of low carbon and medium nitrogen type 316 stainless steel

    International Nuclear Information System (INIS)

    Nakazawa, Takanori; Fujita, Nobuhiro; Kimura, Hidetaka; Komatsu, Hajime; Kotoh, Hiroyuki; Kaguchi, Hitoshi.

    1997-01-01

    The creep rupture properties of type 316 stainless steels containing 0.005-0.022%C and 0.07%N have been investigated at 550degC and 600degC from the aspect of the grain boundary carbide precipitation which was changed with carbon content and chromium segregation. A small amount of carbide precipitated on grain boundaries during creep, because the solubility limit of the carbide is less than 0.005%. The creep rupture ductility of this steel increased with the reduction of carbon content from 0.010% to 0.005% while it decreased with increasing carbon content from 0.010% to 0.020%. Since the amount of grain boundary carbide decreased with reducing carbon content, the increase in ductility was due to the suppression of grain boundary embrittlement caused by the carbide. The creep rupture ductility of this steel was also improved by reducing chromium segregation. This behavior was attributed to the change in carbide morphology from concentrated type to dispersed one, which reduced the grain boundary embrittlement. (author)

  19. Effect of microalloying elements (Nb, V and Ti) on the hot flow behavior of high-Mn austenitic twinning induced plasticity (TWIP) steel

    International Nuclear Information System (INIS)

    Reyes-Calderón, F.; Mejía, I.; Boulaajaj, A.; Cabrera, J.M.

    2013-01-01

    This research work studies the effect of microalloying elements such as Nb, V and Ti on the hot flow behavior of high-Mn austenitic TWIP steel. For this purpose, isothermal uniaxial hot compression tests were carried out at three temperatures (900, 1000 and 1100 °C) and four constant strain rates (10 −1 , 10 −2 , 10 −3 and 10 −4 s −1 ). Experimental results revealed that hot flow curves of microalloyed TWIP steels show single peak curves for all test conditions. Results are discussed in terms of the peak stress (σ p ) and peak strain (ε p ) and its dependence on the strain rate (ε) and temperature. The addition of microalloying elements such as Nb, V and Ti in TWIP steels generates a slight increase in the σ p value, and Ti microalloyed TWIP steel exhibits the highest σ p value. Hot deformed microstructures were analyzed by the Electron Back-Scattering Diffraction Technique (EBSD). The most important results of the austenitic recrystallized grain refinement were obtained for V and Ti microalloyed TWIP steels.

  20. Enhanced Butanol Production by Clostridium acetobutylicum NCIMB 13357 Grown on Date Fruit as Carbon Source in P2 Medium

    Directory of Open Access Journals (Sweden)

    Emran I. Khamaiseh

    2014-01-01

    Full Text Available The production of biobutanol was studied by the cultivation of Clostridium acetobutylicum NCIMB 13557 in P2 medium including date fruit as the sole substrate. The effect of P2 medium and the effect of different concentrations of date fruit ranging from 10 to 100 g/L on biobutanol production were investigated. Anaerobic batch culture was carried out at 35°C incubation temperature and pH 7.0 ± 0.2 for 72 h. Experimental results showed that the lowest yield of biobutanol and acetone-butanol-ethanol (ABE was 0.32 and 0.35 gram per gram of carbohydrate consumed (g/g, respectively, when an initial date fruit concentration of 10 g/L was utilized. At this fruit date concentration a biobutanol production value of 1.56 g/L was obtained. On the other hand, the maximum yield of biobutanol (0.48 g/g and ABE (0.63 g/g was produced at 50 g/L date fruit concentration with a biobutanol production value as high as 11 g/L. However, when a higher initial date fruit concentration was used, biobutanol and ABE production decreased to reach the yield of 0.22 g/g and 0.35 g/g, respectively, where 100 g/L date fruit was used. Similar results also revealed that 10.03 g/L biobutanol was produced using 100 g/L date fruit.

  1. Novel dispersed magnetite core-shell nanogel polymers as corrosion inhibitors for carbon steel in acidic medium

    International Nuclear Information System (INIS)

    Atta, Ayman M.; El-Azabawy, Olfat E.; Ismail, H.S.; Hegazy, M.A.

    2011-01-01

    Graphical abstract: Display Omitted Research highlights: → Through a one-step thermal reaction, magnetite nanoparticles were synthesized, and self-assembled mixed films of modified cross-linked ionic polymer magnetite nanoparticles were prepared on iron surface. → The size distribution and shape of magnetite nanoparticles were examined using transmission electron microscopy (TEM). → The corrosion inhibition efficiency of carbon steel in 1 M HCl by the synthesized Fe 3 O 4 nanogel polymers has been studied using potentiodynamic polarization and EIS. → Scanning electron microscopy (SEM) measurements were applied to study the morphology of the carbon steel surface. - Abstract: Novel core-shell preparing poly(2-acrylamido-2-methylpropane sulfonic acid) (PAMPS) and copolymers with acrylic acid (AA) or acrylamide (AM) magnetic nanogels with controllable particle size produced via free aqueous polymerization at room temperature have been developed for the first time. The crosslinking polymerization was carried out in the presence of N,N'-methylenebisacrylamide (MBA) as a crosslinker, N,N,N',N'-tetramethylethylenediamine (TEMED) and potassium peroxydisulfate (KPS) as redox initiator system. The structure and morphology of the magnetic nanogels were characterized by Fourier transform infrared spectroscopy (FTIR), transmission and scanning electron microscopy (TEM and SEM). The effectiveness of the synthesized compounds as corrosion inhibitors for carbon steel in 1 M HCl was investigated by various electrochemical techniques such as potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). The results showed enhancement in inhibition efficiencies with increasing the inhibitor concentrations and temperatures. The results showed the nanogel particles act as mixed inhibitors. Adsorption of nanogel particles was found to fit the Langmuir isotherm and was chemisorption.

  2. Studies on the kinetics of UO2 dissolution in carbonate-bicarbonate medium using sodium hypochlorite as oxidant

    International Nuclear Information System (INIS)

    Sharma, J.N.; Bhattacharya, K.; Swami, R.G.; Tangri, S.K.; Mukherjee, T.K.

    1996-01-01

    The dissolution of UO 2 in carbonate-bicarbonate solutions containing sodium hypochlorite as an oxidant has been investigated. The effect of temperature, sodium hypochlorite concentration and stirring speed was examined. In the temperature range of 303 to 318 K, the leaching reaction displayed linear kinetics. Apparent activation energy obtained from the differential approach was found to be 57 kJ mol -1 . This relatively high activation energy value indicates a chemically controlled behavior of UO 2 dissolution. The order of reaction with respect to sodium hypochlorite concentration was found to be unity. (author). 18 refs., 6 figs

  3. Bainitic transformation during the two-step quenching and partitioning process in a medium carbon steel containing silicon

    Energy Technology Data Exchange (ETDEWEB)

    Li, H.Y.; Lu, X.W. [School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Wu, X.C.; Min, Y.A. [School of Materials Science and Engineering, Shanghai University, Shanghai 200240 (China); Jin, X.J., E-mail: jin@sjtu.edu.cn [School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China)

    2010-09-15

    Research highlights: In this paper, SEM and TEM were used to characterize microstructure of Q and P steels with different partitioning time at 300 deg. C. The interesting phenomena were discovered and discussed: 1.Lower bainite (bainitic ferrite plus {epsilon}-carbide) rather than carbide-free bainite was observed during partitioning process. 2.The mechanical properties of Q and P steels can be tailored and adjusted through balance volume fraction of retained austenite and lower bainite during partitioning process. 3.The final amount of austenite was influenced by the transformation kinetics of lower bainite during partitioning process. According to the analysis, it can be concluded that associated with carbon partitioning from martensite to austenite, lower bainite transformation inevitably occurred. More importantly, lower bainite transformation seriously affected the mechanical properties of Q and P steels and final amount of austenite. - Abstract: A study of 40SiMnNiCr steel subjected to a two-step quenching and partitioning process (Q and P) is presented. The result suggests that strength variation of Q and P steels during the two-step Q and P process was a cumulative effect of increase of retained austenite fraction, decrease of carbon supersaturation of virgin martensite, and particularly much of lower bainite formation. A trade-off between high strength and good ductility of two-step Q and P steels can be tailored and adjusted by controlling lower bainite fraction. The final amount of austenite was influenced by the transformation kinetics of lower bainite during the partitioning process.

  4. Bainitic transformation during the two-step quenching and partitioning process in a medium carbon steel containing silicon

    International Nuclear Information System (INIS)

    Li, H.Y.; Lu, X.W.; Wu, X.C.; Min, Y.A.; Jin, X.J.

    2010-01-01

    Research highlights: In this paper, SEM and TEM were used to characterize microstructure of Q and P steels with different partitioning time at 300 deg. C. The interesting phenomena were discovered and discussed: 1.Lower bainite (bainitic ferrite plus ε-carbide) rather than carbide-free bainite was observed during partitioning process. 2.The mechanical properties of Q and P steels can be tailored and adjusted through balance volume fraction of retained austenite and lower bainite during partitioning process. 3.The final amount of austenite was influenced by the transformation kinetics of lower bainite during partitioning process. According to the analysis, it can be concluded that associated with carbon partitioning from martensite to austenite, lower bainite transformation inevitably occurred. More importantly, lower bainite transformation seriously affected the mechanical properties of Q and P steels and final amount of austenite. - Abstract: A study of 40SiMnNiCr steel subjected to a two-step quenching and partitioning process (Q and P) is presented. The result suggests that strength variation of Q and P steels during the two-step Q and P process was a cumulative effect of increase of retained austenite fraction, decrease of carbon supersaturation of virgin martensite, and particularly much of lower bainite formation. A trade-off between high strength and good ductility of two-step Q and P steels can be tailored and adjusted by controlling lower bainite fraction. The final amount of austenite was influenced by the transformation kinetics of lower bainite during the partitioning process.

  5. A study of electrochemically-induced corrosion of low carbon steel in a medium modelling acid rain

    International Nuclear Information System (INIS)

    Vertes, C.; Lakatos-Varsanyi, M.; Vertes, A.; Meisel, W.; Guetlich, P.

    1994-01-01

    Complementary electrochemical, spectrophotometric and electron microsopic investigations were made in addition to the conversion electron Moessbauer spectroscopic (CEMS) measurements to learn more about the mechanism of corrosion of low carbon steel samples in aqueous sulfate and sulfite containing sulfate solutions (pH 3.5, 6.5 and 8.5). Passivation of iron in pure sulfate solution was studied in detail in earlier papers. In the present work, we used a solution containing both sulfate and sulfite anions to obtain more information about the effect of acid rain on low carbon steel samples. The compositions and thicknesses of the passive films formed due to the electrochemical treatments were determined from the CEM spectra. γ-FeOOH was found in each case on the surface of the samples; nevertheless, at pH 3.5 the sextet belonging to Fe 3 C appears in the CEM spectra, and also FeSO 4 . H 2 O was detected in low concentration after the shortest polarization time (90 min). The results of the applied methods proved that the sulfite ions induce pitting corrosion at pH 3.5 and 6.5, while the measurements referred to suppressed pitting at pH 8.5. (orig.)

  6. Precipitation Behaviour of Carbonitrides in Ti-Nb-C-N Microalloyed Steels and an Engineering Application with Homogenously Precipitated Nano-particles

    Directory of Open Access Journals (Sweden)

    Yanlin WANG

    2015-11-01

    Full Text Available A thermodynamic model enabling calculation of equilibrium carbonitride composition and relative amounts as a function of steel composition and temperature has been developed previously based on the chemical equilibrium method. In the present work, actual carbonitride precipitation behaviour has been verified in the Ti-Nb-C-N microalloyed steels. The Ti microalloyed steel after refining with 0.012 % Nb exhibited highly improved tensile strength without sacrificing ductility. According to further detailed SEM and TEM analysis, the improved mechanical properties of Ti/Nb microalloyed steel could be attributed to the larger solubility of Nb and Ti, inducing fine dispersion of the carbonitrides with particle size of 2 – 10 nm in the ferrite matrix.DOI: http://dx.doi.org/10.5755/j01.ms.21.4.9622

  7. Influence of the Crc regulator on the hierarchical use of carbon sources from a complete medium in Pseudomonas.

    Science.gov (United States)

    La Rosa, Ruggero; Behrends, Volker; Williams, Huw D; Bundy, Jacob G; Rojo, Fernando

    2016-03-01

    The Crc protein, together with the Hfq protein, participates in catabolite repression in pseudomonads, helping to coordinate metabolism. Little is known about how Crc affects the hierarchy of metabolite assimilation from complex mixtures. Using proton Nuclear Magnetic Resonance (NMR) spectroscopy, we carried out comprehensive metabolite profiling of culture supernatants (metabolic footprinting) over the course of growth of both Pseudomonas putida and P. aeruginosa, and compared the wild-type strains with deletion mutants for crc. A complex metabolite consumption hierarchy was observed, which was broadly similar between the two species, although with some important differences, for example in sugar utilization. The order of metabolite utilization changed upon inactivation of the crc gene, but even in the Crc-null strains some compounds were completely consumed before late metabolites were taken up. This suggests the presence of additional regulatory elements that determine the time and order of consumption of compounds. Unexpectedly, the loss of Crc led both species to excrete acetate and pyruvate as a result of unbalanced growth during exponential phase, compounds that were later consumed in stationary phase. This loss of carbon during growth helps to explain the contribution of the Crc/Hfq regulatory system to evolutionary fitness of pseudomonads. © 2015 Society for Applied Microbiology and John Wiley & Sons Ltd.

  8. Protection of Petroleum Pipeline Carbon Steel Alloys with New Modified Core-Shell Magnetite Nanogel against Corrosion in Acidic Medium

    Directory of Open Access Journals (Sweden)

    Gamal A. El Mahdy

    2013-01-01

    Full Text Available New method was used to prepare magnetite nanoparticle based on reduction of Fe(III ions with potassium iodide to produce Fe3O4 nanoparticle. The prepared magnetite was stabilized with cross-linked polymer based on 2-acrylamido-2-methylpropane sulfonic acid (AMPS to prepare novel core-shell nanogel. In this respect, Fe3O4/poly(2-acrylamido-2-methylpropane sulfonic acid (PAMPS magnetic nanogels with controllable particle size produced via free aqueous polymerization at 65°C have been developed for the first time. The polymer was crosslinked in the presence of N,N-methylenebisacrylamide (MBA as a crosslinker and potassium peroxydisulfate (KPS as redox initiator system. The structure and morphology of the magnetic nanogel were characterized by Fourier transform infrared spectroscopy (FTIR and transmission and scanning electron microscopy (TEM and SEM. The effectiveness of the synthesized compounds as corrosion inhibitors for carbon steel in 1 M HCl was investigated by various electrochemical techniques such as potentiodynamic polarization and electrochemical impedance spectroscopy (EIS. The results showed enhancement in inhibition efficiencies with increasing the inhibitor concentrations. The results showed that the nanogel particles act as mixed inhibitors. EIS data revealed that Rct increases with increasing inhibitor concentration.

  9. Fabrication of TiO2/Carbon Photocatalyst using Submerged DC Arc Discharged in Ethanol/Acetic Acid Medium

    Science.gov (United States)

    Saraswati, T. E.; Nandika, A. O.; Andhika, I. F.; Patiha; Purnawan, C.; Wahyuningsih, S.; Rahardjo, S. B.

    2017-05-01

    This study aimed to fabricate a modified photocatalyst of TiO2/C to enhance its performance. The fabrication was achieved using the submerged direct current (DC) arc-discharge method employing two graphite electrodes, one of which was filled with a mixture of carbon powder, TiO2, and binder, in ethanol with acetic acid added in various concentrations. The arc-discharge method was conducted by flowing a current of 10-20 A (~20 V). X-ray diffraction (XRD) patterns showed significant placements of the main peak characteristics of TiO2, C graphite, and titanium carbide. The surface analysis using Fourier transform infrared spectroscopy (FTIR) revealed that fabricated TiO2/C nanoparticles had stretching vibrations of Ti-O, C-H, C═O, C-O, O-H and C═C in the regions of 450-550 cm-1, 2900-2880 cm-1, 1690-1760 cm-1, 1050-1300 cm-1, 3400-3700 cm-1 and ~1600 cm-1, respectively. In addition, the study investigated the photocatalysts of unmodified and modified TiO2/C for photodegradation of methylene blue (MB) dye solution under mercury lamp irradiation. The effectiveness of the degradation was defined by the decrease in 60-minute absorbance under a UV-Vis spectrophotometer. Modified TiO2/C proved to be significantly more efficient in reducing dye concentrations, reaching ~70%. It indicated that the oxygen-containing functional groups have been successfully attached to the surface of the nanoparticles and played a role in enhancing photocatalytic activity.

  10. Nanograined Ti–Nb microalloy steel achieved by Accumulative Roll Bonding (ARB) process

    International Nuclear Information System (INIS)

    Tohidi, A.A.; Ketabchi, M.; Hasannia, A.

    2013-01-01

    Over the last decade, nanocrystalline and ultra-fine grained (UFG) materials with grain size less than 1 μm have aroused considerable interest due to their superior mechanical properties compared to conventionally grained materials. In this work Ti–Nb microalloy steel was processed by the severe plastic deformation (SPD) technique called Accumulative Roll Bonding (ARB) in order to produce an ultra-fine grained microstructure and improve the mechanical properties. After initial preparation to achieve good sheet bonding, 8 cycles of ARB at 550 °C were successfully performed. Observation of optical microstructure, scanning electron microscopy (SEM) micrographs, and X-Ray Diffraction (XRD) peak broadening analysis were used for the characterization of grain structure of the ARB processed sample. The mechanical attributes after rolling and cooling were examined. It was calculated that metal's yield and tensile strength increased by 334% and 215% respectively, while the ductility dropped from as-received value of 34% to 2.9%. Microhardness of the material was studied at room temperature. There was a continuous enhancement of hardness by increasing the pass number of the ARB process. At the 8th pass, the hardness values increased by 230%. The rolling process was stopped at 8th cycle when cracking of the edge became pronounced

  11. Analysis of Flow Behavior of an Nb-Ti Microalloyed Steel During Hot Deformation

    Science.gov (United States)

    Mohebbi, Mohammad Sadegh; Parsa, Mohammad Habibi; Rezayat, Mohammad; Orovčík, L'ubomír

    2018-03-01

    The hot flow behavior of an Nb-Ti microalloyed steel is investigated through hot compression test at various strain rates and temperatures. By the combination of dynamic recovery (DRV) and dynamic recrystallization (DRX) models, a phenomenological constitutive model is developed to derive the flow stress. The predefined activation energy of Q = 270 kJ/mol and the exponent of n = 5 are successfully set to derive critical stress at the onset of DRX and saturation stress of DRV as functions of the Zener-Hollomon parameter by the classical hyperbolic sine equation. The remaining parameters of the constitutive model are determined by fitting them to the experiments. Through substitution of a normalized strain in the DRV model and considering the interconnections between dependent parameters, a new model is developed. It is shown that, despite its fewer parameters, this model is in good agreement with the experiments. Accurate analyses of flow data along with microstructural analyses indicate that the dissolution of NbC precipitates and its consequent solid solution strengthening and retardation of DRX are responsible for the distinguished behaviors in the two temperature ranges between T employed for the present steel in the whole tested temperature ranges.

  12. Austenite grain growth and microstructure control in simulated heat affected zones of microalloyed HSLA steel

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Lei [Department of Machine Tools and Factory Management, Technical University of Berlin, Pascalstraße 8 – 9, 10587, Berlin (Germany); Federal Institute for Materials Research and Testing, Unter den Eichen 87, 12205, Berlin (Germany); Kannengiesser, Thomas [Federal Institute for Materials Research and Testing, Unter den Eichen 87, 12205, Berlin (Germany); Institute of Materials and Joining Technology, Otto von Guericke University Magdeburg, Universitetsplatz 2, 39106, Magdeburg (Germany)

    2014-09-08

    The roles of microalloying niobium, titanium and vanadium for controlling austenite grain growth, microstructure evolution and hardness were investigated at different simulated heat affected zones (HAZ) for high strength low alloy (HSLA) S690QL steel. High resolution FEG-SEM has been used to characterize fine bainitic ferrite, martensite and nanosized second phases at simulated coarse and fine grain HAZs. It was found that for Ti bearing steel (Ti/N ratio is 2) austenite grain had the slowest growth rate due to the presence of most stable TiN. The fine cuboidal particles promoted intragranular acicular ferrite (IGF) formation. Nb bearing steel exhibited relatively weaker grain growth retardation compared with titanium bearing steels and a mixed microstructure of bainite and martensite was present for all simulated HAZs. IGF existed at coarse grain HAZ of Ti+V bearing steel but it was totally replaced by bainite at fine grain HAZs. Hardness result was closely related to the morphology of bainitic ferrite, intragranular ferrite and second phases within ferrite. The microstructure and hardness results of different simulated HAZs were in good agreement with welded experimental results.

  13. EFFECTS OF MO ADDITION ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF CAST MICROALLOYED STEEL

    Directory of Open Access Journals (Sweden)

    H. Torkamani

    2017-09-01

    Full Text Available In industry, the cost of production is an important factor and it is preferred to use conventional and low cost procedures for producing the parts. Heat treatment cycles and alloying additions are the key factors affecting the microstructure and mechanical properties of the cast steels. In this study an attempt was made to evaluate the influence of minor Mo addition on the microstructure and mechanical properties of conventionally heat treated cast micro-alloyed steels. The results of Jominy and dilatometry tests and also microstructural examinations revealed that Mo could effectively increase the hardenability of the investigated steel and change the microstructure features of the air-cooled samples. Acicular microstructure was the consequence of increasing the hardenability in Mo-added steel. Besides, it was found that Mo could greatly affect the isothermal bainitic transformation and higher fraction of martensite after cooling (from isothermal temperature was due to the Mo addition. The results of impact test indicated that the microstructure obtained in air-cooled Mo-added steel led to better impact toughness (28J in comparison with the base steel (23J. Moreover, Mo-added steel possessed higher hardness (291HV, yield (524MPa and tensile (1108MPa strengths compared to the base one.

  14. Development of Microstructure and Crystallographic Texture in a Double-Sided Friction Stir Welded Microalloyed Steel

    Science.gov (United States)

    Rahimi, S.; Wynne, B. P.; Baker, T. N.

    2017-01-01

    The evolution of microstructure and crystallographic texture has been investigated in double-sided friction stir welded microalloyed steel, using electron backscatter diffraction (EBSD). The microstructure analyses show that the center of stirred zone reached a temperature between Ac1 and Ac3 during FSW, resulting in a dual-phase austenitic/ ferritic microstructure. The temperatures in the thermo-mechanically affected zone and the overlapped area between the first and second weld pass did not exceed the Ac1. The shear generated by the rotation probe occurs in austenitic/ferritic phase field where the austenite portion of the microstructure is transformed to a bainitic ferrite, on cooling. Analysis of crystallographic textures with regard to shear flow lines generated by the probe tool shows the dominance of simple shear components across the whole weld. The austenite texture at Ac1 - Ac3 is dominated by the B { {1bar{1}2} }D2 { {11bar{2}} }< 111rangle simple shear texture components. The formation of ultrafine equiaxed ferrite with submicron grain size has been observed in the overlapped area between the first and second weld pass. This is due to continuous dynamic strain-induced recrystallization as a result of simultaneous severe shear deformation and drastic undercooling.

  15. Optimization of Micro-Alloying Elements for Mechanical Properties in Normalized Cast Steel Using Taguchi Technique

    Directory of Open Access Journals (Sweden)

    Chokkalingam B.

    2017-06-01

    Full Text Available In this study, Taguchi method is used to find out the effect of micro alloying elements like vanadium, niobium and titanium on the hardness and tensile strength of the normalized cast steel. Based on this method, plan of experiments were made by using orthogonal arrays to acquire the data on hardness and tensile strength. The signal to noise ratio and analysis of variance (ANOVA are used to investigate the effect of these micro alloying elements on these two mechanical properties of the micro alloyed normalized cast steel. The results indicated that in the micro alloyed normalized cast steel both these properties increases when compared to non-micro-alloyed normalized cast steel. The effect of niobium addition was found to be significantly higher to obtain higher hardness and tensile strength when compared to other micro alloying elements. The maximum hardness of 200HV and the maximum tensile strength of 780 N/mm2 were obtained in 0.05%Nb addition micro alloyed normalized cast steel. Micro-alloyed with niobium normalized cast steel have the finest and uniform microstructure and fine pearlite colonies distributed uniformly in the ferrite. The optimum condition to obtain higher hardness and tensile strength were determined. The results were verified with experiments.

  16. Precipitation characteristic of high strength steels microalloyed with titanium produced by compact strip production

    Institute of Scientific and Technical Information of China (English)

    Jian Zhou; Yonglin Kang; Xinping Mao

    2008-01-01

    Transmission electron microscopy (TEM) and physics-chemical phase analysis were employed to investigate the precipitates in high strength steels microalloyed with Ti produced by compact strip production (CSP). It was seen that precipitates in Ti mieroalloyed steels mainly included TiN, Ti4C2S2, and TiC. The size of TiN particles varied from 50 to 500 nm, and they could precipitate during or before soaking. The Ti4C2S>2 with the size of 40-100 nm might precipitate before rolling, and the TiC particles with the size of 5-50 nm precipitated heterogeneously. High Ti content would lead to the presence of bigger TiC particles that precipitated in austenite, and by contrast, TiC particles that precipitated in ferrite and the transformation of austenite to ferrite was smaller. They were less than 30 nm and mainly responsible for precipitate strengthening. It should be noted that the TiC particles in higher Ti content were generally smaller than those in the steel with a lower Ti content.

  17. Effects of Niobium Microalloying on Microstructure and Properties of Hot-Dip Galvanized Sheet

    Energy Technology Data Exchange (ETDEWEB)

    Mohrbacher, Hardy [NiobelCon bvba, Brussels (Belgium)

    2010-04-15

    Niobium microalloying is effective in hot-rolled and cold-rolled steels by providing a fine-grained microstructure resulting in increased strength. To optimize the strengthening effect, alloy design and hot-rolling conditions have to be adapted. As a key issue the dissolution and precipitation characteristics of Nb are discussed in particular with regard to the run-out table conditions. It is then considered how the hot-rolled microstructure and the solute state of Nb interact with the hot-dip galvanizing cycle. The adjusted conditions allow controlling the morphology and distribution of phases in the cold-rolled annealed material. Additional precipitation hardening can be achieved as well. The derived options can be readily applied to produce conventional HSLA and IF high strength steels as well as to modem multiphase steels. It will be explained how important application properties such as strength, elongation, bendability, weldability and delayed cracking resistance can be influenced in a controlled and favorable way. Examples of practical relevance and experience are given.

  18. The effect of manganese content on mechanical properties of high titanium microalloyed steels

    Energy Technology Data Exchange (ETDEWEB)

    Li, Xiaolin, E-mail: lixiaolinwork@163.com [Shougang Research Institute of Technology, Beijing 100041 (China); Li, Fei; Cui, Yang; Xiao, Baoliang [Shougang Research Institute of Technology, Beijing 100041 (China); Wang, Xuemin [School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China)

    2016-11-20

    In this work, in order to achieve an optimum combination of high strength, ductility and toughness of high Ti microalloyed steel, extensive research efforts were exerted to study the effect of soaking temperature, manganese and sulfur content on properties of titanium steels. Precipitation hardening of Ti-bearing steels has been found to vary with different soaking temperature. Higher strength was achieved in these steels at higher soaking temperature due to dissolution of more TiC, Ti{sub 4}S{sub 2}C{sub 2} and little TiN, which lead to re-precipitation of fine carbides with greater volume fraction. The results of transmission electron microscope (TEM)analysis indicates that there were more and finer TiC precipitates coherent or semi-coherent with the ferrite matrix in the high manganese content steel than in low manganese content steel. The marked improvement in strength is also associated with low sulfur content. TiC particles smaller than 20 nm in 8Ti-8Mn steel help enhance strength to higher than 302 MPa compared with 8Mn steel.

  19. Microalloying in case hardening steels - a challenge for the lean production of gears

    Energy Technology Data Exchange (ETDEWEB)

    Trute, S.; Bleck, W. [RWTH Aachen (Germany). Dept. of Ferrous Metallurgy; Hippenstiel, F. [Edelstahlwerke Buderus AG, Wetzlar (Germany); Klinkenberg, C. [Niobium Products Company GmbH, Duesseldorf (Germany)

    2005-07-01

    Case hardening steels cover a dominant fraction of engineering steel production. Particularly with recent developments in automotive power train elements, where good hardenability, high tensile strength, high fatigue strength and high impact resistance are required. With a share of up to 40% the material and the heat treatment process take a main part of the overall manufacturing costs. Production costs can be reduced by shortening the overall process time from the melting to the finishing. New developments in carburising technology with an increased carburising temperature offer the possibility of time and cost reduction. Simultaneously a precise grain size control during austenitising is required. A homogenous former austenite grain size distribution results in a more uniform performance of the mechanical properties. This paper summarizes the results of recent research regarding the demands on steels for a high temperature carburising process. The possibility to prevent undesired grain growth by increasing the grain coarsening temperature using microalloying elements as well as the impact on the production process is discussed. (orig.)

  20. Hot ductility of a microalloyed steel in the intermediate temperature range

    International Nuclear Information System (INIS)

    Darsouni, A.; Bouzabata, B.; Montheillet, F.

    1995-01-01

    In this study hot ductility has been determined from tensile tests for two states of a microalloyed steel: after casting and after rolling processes. Hot deformations were carried out at speeds varying from 10 -4 s -1 to 10 -2 s -1 and temperatures from 750 C to 1100 C. Two heat treatments were chosen before hot deformation. A ferrite precipitation is observed at austenitic grain boundaries in the intercritical temperature range, causing intergranular embrittlement. Ductility trough is deeper in the as-cast samples due to the growth of large grain size. Also, precipitation makes the hot ductility curve wider and deeper around 900 C. The results show a decrease in hot ductility. Minimum values of hot ductility are determined for (ITC) treatment at 900 C and for (DTC) treatment at 800 C. For this second treatment another decrease in hot ductility was observed at 900 C. We can explain hot ductility losses by the presence of precipitates in the austenitic region and the presence of the two-phase structure in the intercritical region. (orig.)

  1. Microstructure and properties of TP2 copper tube with La microalloying by horizontal continuous casting

    Directory of Open Access Journals (Sweden)

    Jin-hu Wu

    2018-01-01

    Full Text Available The TP2 copper tube was prepared with La microalloying by horizontal continuous casting (HCC. The absorptivity of La and its effects on microstructure, tensile and corrosion properties of HCC TP2 copper tube were studied by means of the inductively coupled plasma optical emission spectrometer (ICP-OES, optical microscope (OM, scanning electron microscope (SEM and potentiodynamic polarization measurements. The results show that the absorptivity of La in the HCC TP2 copper tube is about 15% under antivacuum conditions due to the good chemical activities of La. The impurity elements in copper tube such as O, S, Pb and Si can be significantly reduced, and the average columnar dendrite spacing of the copper tube can also be reduced from 2.21 mm to 0.93 mm by adding La. The ultimate tensile strength and the elongation with and without La addition are almost unchanged. However, the annual corrosion rate of the HCC TP2 copper tube is reduced from 10.18 mm•a-1 to 9.37 mm•a-1 by the purification effect of trace La.

  2. Toward interplay between substructure evolution, dislocation configuration, and yield strength in a microalloyed steel

    International Nuclear Information System (INIS)

    Venkatsurya, P.K.C.; Misra, R.D.K.; Mulholland, M.D.; Manohar, M.; Hartmann, J.E.

    2014-01-01

    We focus our attention here on the directional dependence of yield strength in high strength microalloyed steel using transmission electron microscopy and x-ray diffraction. The primary objective is to study the interplay between substructural evolution, notably cell size, dense dislocation walls (DDWs), dislocation tangle zones (DTZs), lamellar boundaries, crystallographic texture, and yield strength. The study elucidates for the first time the strong impact of thermo-mechanical deformation-induced dislocation and lamellar structures, which are likely to modify the slip pattern, leading to directional dependence of yield strength. Majority of the dislocations tend to pile along the {110} slip planes as dense dislocation walls. At low strains, grains are first divided into cell blocks that are nearly dislocation-free. At higher strains and with progress in thermo-mechanical processing dislocation tangled zones and lamellar boundaries develop. It is hypothesized that the differences in dislocation configurations, dislocations cells and cell blocks, and lamellar boundaries synergistically contribute to directional dependence of the yield strength in the high strength ferrous alloy. The presumption is envisaged on the basis of observations that the microstructural constituents were similar in the entire plane of the hot rolled strip and the crystallographic texture was weak

  3. An Investigation of Aging Behaviour in Microalloyed Steel (X70) UOE Pipe

    Science.gov (United States)

    Wiskel, J. B.; Ma, J.; Ivey, D. G.; Henein, H.

    Aging of microalloyed steel pipe can occur at relatively low temperatures associated with the pipe coating process and/or during long term storage or use. The aging phenomenon is primarily attributed to C diffusion to dislocations and subsequent pinning of these dislocations. Important factors in the aging process include time, temperature, chemical composition and plastic deformation (arising from the pipe forming process). The work presented in this paper uses a Box-Behnken experimental design to determine the effect of time, temperature, location in the UOE pipe (90° or 180° to the weld), position through the pipe wall thickness (ID, CL or OD) and the steel's C/Nb ratio (0.60, 1.25 and 1.80) on the change in yield strength of three (uncoated) X70 UOE pipes. Quantitative microstructure analysis is undertaken to determine the grain size and microconstituent fractions of the as-received pipe material. Quadratic equations and response surface(s) correlating the significant aging variables with changes in the longitudinal yield stress of the pipe are developed. Both through thickness position and the C/Nb ratio, followed by aging temperature, had the largest effect on the change in longitudinal yield strength.

  4. Modification of Non-Metallic Inclusions by Rare-Earth Elements in Microalloyed Steels

    Directory of Open Access Journals (Sweden)

    M. Opiela

    2012-04-01

    Full Text Available The modification of the chemical composition of non-metallic inclusions by rare-earth elements in the new-developed microalloyed steels was discussed in the paper. The investigated steels are assigned to production of forged elements by thermo- mechanical treatment. The steels were melted in a vaccum induction furnace and modification of non-metallic inclusions was carried out by the michmetal in the amount of 2.0 g per 1 kg of steel. It was found that using material charge of high purity and a realization of metallurgical process in vacuous conditions result in a low concentration of sulfur (0.004%, phosphorus (from 0.006 to 0.008% and oxygen (6 ppm. The high metallurgical purity is confirmed by a small fraction of non-metallic inclusions averaging 0.075%. A large majority of non-metallic inclusions are fine, globular oxide-sulfide or sulfide particles with a mean size 17m2. The chemical composition and morphology of non-metallic inclusions was modified by Ce, La and Nd, what results a small deformability of non- metallic inclusions during hot-working.

  5. Carbon/ternary alloy/carbon optical stack on mylar as an optical data storage medium to potentially replace magnetic tape.

    Science.gov (United States)

    Wang, Hao; Lunt, Barry M; Gates, Richard J; Asplund, Matthew C; Shutthanandan, V; Davis, Robert C; Linford, Matthew R

    2013-09-11

    A novel write-once-read-many (WORM) optical stack on Mylar tape is proposed as a replacement for magnetic tape for archival data storage. This optical tape contains a cosputtered bismuth-tellurium-selenium (BTS) alloy as the write layer sandwiched between thin, protective films of reactively sputtered carbon. The composition and thickness of the BTS layer were confirmed by Rutherford Backscattering (RBS) and atomic force microscopy (AFM), respectively. The C/BTS/C stack on Mylar was written to/marked by 532 nm laser pulses. Under the same conditions, control Mylar films without the optical stack were unaffected. Marks, which showed craters/movement of the write material, were characterized by optical microscopy and AFM. The threshold laser powers for making marks on C/BTS/C stacks with different thicknesses were explored. Higher quality marks were made with a 60× objective compared to a 40× objective in our marking apparatus. The laser writing process was simulated with COMSOL.

  6. Carbon/Ternary Alloy/Carbon Optical Stack on Mylar as an Optical Data Storage Medium to Potentially Replace Magnetic Tape

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Hao; Lunt, Barry M.; Gates, Richard J.; Asplund, Matthew C.; Shutthanandan, V.; Davis, Robert C.; Linford, Matthew R.

    2013-09-11

    A novel write-once-read-many (WORM) optical stack on Mylar tape is proposed as a replacement for magnetic tape for archival data storage. This optical tape contains a cosputtered bismuth–tellurium–selenium (BTS) alloy as the write layer sandwiched between thin, protective films of reactively sputtered carbon. The composition and thickness of the BTS layer were confirmed by Rutherford Backscattering (RBS) and atomic force microscopy (AFM), respectively. The C/BTS/C stack on Mylar was written to/marked by 532 nm laser pulses. Under the same conditions, control Mylar films without the optical stack were unaffected. Marks, which showed craters/movement of the write material, were characterized by optical microscopy and AFM. The threshold laser powers for making marks on C/BTS/C stacks with different thicknesses were explored. Higher quality marks were made with a 60× objective compared to a 40× objective in our marking apparatus. Finally, the laser writing process was simulated with COMSOL.

  7. Monitoring the aeration efficiency and carbon footprint of a medium-sized WWTP: experimental results on oxidation tank and aerobic digester.

    Science.gov (United States)

    Caivano, Marianna; Bellandi, Giacomo; Mancini, Ignazio M; Masi, Salvatore; Brienza, Rosanna; Panariello, Simona; Gori, Riccardo; Caniani, Donatella

    2017-03-01

    The efficiency of aeration systems should be monitored to guarantee suitable biological processes. Among the available tools for evaluating the aeration efficiency, the off-gas method is one of the most useful. Increasing interest towards reducing greenhouse gas (GHG) emissions from biological processes has resulted in researchers using this method to quantify N 2 O and CO 2 concentrations in the off-gas. Experimental measurements of direct GHG emissions from aerobic digesters (AeDs) are not available in literature yet. In this study, the floating hood technique was used for the first time to monitor AeDs. The floating hood technique was used to evaluate oxygen transfer rates in an activated sludge (AS) tank of a medium-sized municipal wastewater treatment plant located in Italy. Very low values of oxygen transfer efficiency were found, confirming that small-to-medium-sized plants are often scarcely monitored and wrongly managed. Average CO 2 and N 2 O emissions from the AS tank were 0.14 kg CO2 /kg bCOD and 0.007 kg CO2,eq /kg bCOD , respectively. For an AeD, 3 × 10 -10  kg CO2 /kg bCOD direct CO 2 emissions were measured, while CO 2,eq emissions from N 2 O were 4 × 10 -9  kg CO2,eq /kg bCOD . The results for the AS tank and the AeD were used to estimate the net carbon and energy footprint of the entire plant.

  8. The effects of microalloying with silicon and germanium on microstructure and hardness of a commercial aluminum alloy

    Directory of Open Access Journals (Sweden)

    VESNA MAKSIMOVIC

    2003-11-01

    Full Text Available The effect of small additions of Si and Ge on the microstructure and hardness was investigated during aging of a commercial 2219 aluminum alloy. It was found that for the same level of microalloying in alloy 2219SG (containing Si and Ge, a maximum hardness was achieved 3 times faster than in alloy 2219S (without Ge. The accelerated precipitation kinetics is a consequence of the presence of fine Si–Ge particles, serving as heterogeneous precipitation sites for q” strengthening particles.

  9. A phase quantification method based on EBSD data for a continuously cooled microalloyed steel

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, H.; Wynne, B.P.; Palmiere, E.J., E-mail: e.j.palmiere@sheffield.ac.uk

    2017-01-15

    Mechanical properties of steels depend on the phase constitutions of the final microstructures which can be related to the processing parameters. Therefore, accurate quantification of different phases is necessary to investigate the relationships between processing parameters, final microstructures and mechanical properties. Point counting on micrographs observed by optical or scanning electron microscopy is widely used as a phase quantification method, and different phases are discriminated according to their morphological characteristics. However, it is difficult to differentiate some of the phase constituents with similar morphology. Differently, for EBSD based phase quantification methods, besides morphological characteristics, other parameters derived from the orientation information can also be used for discrimination. In this research, a phase quantification method based on EBSD data in the unit of grains was proposed to identify and quantify the complex phase constitutions of a microalloyed steel subjected to accelerated coolings. Characteristics of polygonal ferrite/quasi-polygonal ferrite, acicular ferrite and bainitic ferrite on grain averaged misorientation angles, aspect ratios, high angle grain boundary fractions and grain sizes were analysed and used to develop the identification criteria for each phase. Comparing the results obtained by this EBSD based method and point counting, it was found that this EBSD based method can provide accurate and reliable phase quantification results for microstructures with relatively slow cooling rates. - Highlights: •A phase quantification method based on EBSD data in the unit of grains was proposed. •The critical grain area above which GAM angles are valid parameters was obtained. •Grain size and grain boundary misorientation were used to identify acicular ferrite. •High cooling rates deteriorate the accuracy of this EBSD based method.

  10. Effects of tungsten on continuous cooling transformation characteristics of microalloyed steels

    International Nuclear Information System (INIS)

    Zhao, Jingwei; Jiang, Zhengyi; Kim, Ji Soo; Lee, Chong Soo

    2013-01-01

    Highlights: ► W has a positive effect on refining the austenite grains and precipitates. ► W shifts the ranges of transformation products to the right side of CCT diagram. ► W addition induces increased austenitisation starting and finishing temperatures. ► The critical cooling rate for phase transformation is decreased after W addition. - Abstract: Continuous cooling transformation (CCT) characteristics of microalloyed steels with different tungsten (W) contents (0, 0.1 and 1 wt.%) were investigated to obtain the necessary information for heat treatment of these steels. The effects of W addition on the sizes of prior austenite grains and precipitates were analysed. CCT diagrams were obtained by varying the cooling rates from 0.1 to 120 °C/s. Transformation characteristics were determined by using dilatometer test, microscopic observation and hardness measurement. The results showed that W had a positive effect on the refinement of prior austenite grains and precipitates. The CCT diagrams exhibited that the ranges of transformation products were shifted to the right side of the diagram when the W content increased. CCT diagram for steel with 0.1% W was similar in shape to that without W. The addition of 1% W induced two separated transformation ranges in the cooling rate range of 0.1 to 1 °C/s in the diagram. Both the austenitisation starting and finishing temperatures were raised as W was added. W addition induced decreased critical cooling rates for phase transformations and obtaining complete ferrite + pearlite microstructures. The martensite transformation temperature was decreased after W addition. The addition of W caused increased hardness, and the hardness obeyed an exponential type relationship with cooling rate

  11. Formation and Thermal Stability of Large Precipitates and Oxides in Titanium and Niobium Microalloyed Steel

    Institute of Scientific and Technical Information of China (English)

    ZHUO Xiao-jun; WOO Dae-hee; WANG Xin-hua; LEE Hae-geon

    2008-01-01

    As-cast CC slabs of microalloyed steels are prone to surface and sub-surface cracking. Precipitation phenomena in-itiated during solidification reduce ductility at high temperature. The unidirectional solidification unit is employed to sim-ulate the solidification process during continuous casting. Precipitation behavior and thermal stability are systemati-cally investigated. Samples of adding titanium and niobium to steels have been examined using field emission scanning electron microscope (FE-SEM), electron probe X-ray microanalyzer (EPMA), and transmission electron microscope (TEM). It has been found that the addition of titanium and niobium to high-strength low-alloyed (HSLA) steel resuited in undesirable large precipitation in the steels, i. e. , precipitation of large precipitates with various morphologies. The composition of the large precipitates has been determined. The effect of cooling rate on (Ti, Nb)(C, N) precipitate formation is investigated. With increasing the cooling rate, titanium-rich (Ti,Nb)(C, N) precipitates are transformed to niobium-rich (Ti,Nb)(C,N) precipitates. The thermal stability of these large precipitates and oxides have been assessed by carrying out various heat treatments such as holding and quenching from temperature at 800 and 1 200 ℃. It has been found that titanium-rich (Ti,Nb)(C,N) precipitate is stable at about 1 200 ℃ and niobi-um-rich (Ti,Nb)(C,N) precipitate is stable at about 800 ℃. After reheating at 1 200 ℃ for 1 h, (Ca, Mn)S and TiN are precipitated from Ca-Al oxide. However, during reheating at 800 ℃ for 1 h, Ca-Al-Ti oxide in specimens was stable. The thermodynamic calculation of simulating the thermal process is employed. The calculation results are in good agreement with the experimental results.

  12. Carbide precipitation kinetics in austenite of a Nb-Ti-V microalloyed steel

    International Nuclear Information System (INIS)

    Jung, Jae-Gil; Park, June-Soo; Kim, Jiyoung; Lee, Young-Kook

    2011-01-01

    Highlights: → Carbide precipitation kinetic was fastest at 950 deg. C and accelerated by strain. → Nucleation sites for (Nb,Ti)C above 950 deg. C were mainly undissolved (Ti,Nb)(C,N). → Strain enabled (Nb,Ti)C to nucleate on all sides of (Ti,Nb)(C,N) above 950 deg. C. → Strain changed nucleation sites from (Ti,Nb)(C,N) to dislocations below 900 deg. C. → Strain also accelerated the change in particle composition to equilibrium one. - Abstract: The isothermal precipitation kinetics of carbides in both strain-free and strained austenite (γ) of a microalloyed steel were quantitatively investigated through the electrical resistivity and transmission electron microscopy. The (Nb,Ti)C carbides at the interfaces of the undissolved (Ti,Nb)(C,N) carbonitrides were observed at all temperatures in strain-free γ. However, for strain-induced precipitation, above 950 deg. C, the precipitation of (Nb,Ti)C carbides near the undissolved (Ti,Nb)(C,N) carbonitrides was predominant due to the recrystallization of strained γ. Meanwhile, the fine (Nb,Ti,V)C carbides were homogeneously precipitated in non-recrystallized γ at 850 deg. C and 900 deg. C, as well as near the undissolved (Ti,Nb)(C,N) particles. The electrical resistivity method was successfully used to quantitatively measure the isothermal precipitation kinetics of carbides in both strain-free and strained γ. The precipitation-time-temperature diagrams of the carbide in strain-free and strained γ, with nose temperatures of 950 deg. C, were generated and the precipitation kinetics were greatly accelerated by the applied strain.

  13. Hot Ductility Behavior of Boron Containing Microalloyed Steels with Varying Manganese Contents

    Science.gov (United States)

    Brune, Tobias; Senk, Dieter; Walpot, Raphael; Steenken, Bernhard

    2015-02-01

    The hot ductility is measured for six different steel grades with different microalloying elements and with varying manganese contents using the hot tensile test machine with melting/solidification unit at the Department of Ferrous Metallurgy RWTH Aachen University. To identify the influence of manganese on hot ductility, tests are performed with varying the manganese content from 0.7 to 18.2 wt pct, a high manganese steel. Additionally, the effect of different cooling and strain rates is analyzed by changing the particular rate for selected samples in the minima. To investigate and detect the cause of cracking during testing, the fracture surfaces in the ductility minima are considered with scanning electron microscope-energy dispersive X-ray spectroscopy. Thermodynamic modeling is conducted on basis of the commercial software ThermoCalc©. A sharp decrease of the hot ductility is recognizable at 1398 K (1125 °C), at only 0.7 wt pct manganese because of the low manganese to sulfur ratio. The grades with a Mn content up to 1.9 wt pct show a good ductility with minimal ductility loss. In comparison, the steel grade with 18.2 wt pct has a poor hot ductility. Because of the formation of complex precipitates, where several alloying elements are involved, the influence of boron on hot ductility is not fully clarified. By increasing the cooling rate, the reduction of area values are shifted to smaller values. For high test temperatures, these measured values are decreased for lower strain rates. Thereby, an early drop of the ductility is noticeable for the high temperatures around 1373 K (1100 °C).

  14. Corrosion behavior of carbon steel exposed for long time to an inoculation medium of sulfate-reducing bacteria; Ryusan`en kangenkin ga seisokusuru baichi ni chokikan shinshinshita tansoko no fushoku kyodo

    Energy Technology Data Exchange (ETDEWEB)

    Baba, F.; Suzuki, T. [Ajinomoto Co. Inc., Kawasaki (Japan). Technology and Engineering Lab.; Seo, M. [Hokkaido Univ., Sapporo (Japan). Graduate School of Engineering

    1996-10-15

    In this paper, carbon steel was exposed more than six weeks to an inoculation medium of the sulfate-reducing bacteria in which the Fe{sup 2+} concentration was adjusted to a fixed value, the corrosion behavior of carbon steel was investigated by measuring the weight change and surface analysis using EPMA. As a result, the conclusions were obtained as follows: in the case of the medium with high Fe{sup 2+} concentration, the corrosion rate reached a maximum. In this case, the corrosion rate was suppressed to be low during the exposure for up to three weeks, and was increased above four weeks. The corrosion rate became 0.06 mm year{sup -1} by extrapolating the weight loss during the exposure up to six weeks. This value was higher than the average corrosion rate of carbon steel in a neutral solution with deaeration. It was shown from the analysis results using the EPMA that the FeS scale area covered on the surface of carbon steel would act as a cathode, and the other area would act as an anode. The formation of a scale effectively acting as a cathode depended on the exposure time and the formation of FeS in the medium. 15 refs., 10 figs., 1 tab.

  15. Products, practices and processes: exploring the innovation potential for low-carbon housing refurbishment among small and medium-sized enterprises (SMEs) in the UK construction industry

    International Nuclear Information System (INIS)

    Killip, Gavin

    2013-01-01

    Scenario-based studies agree that the technical potential for CO 2 emissions reduction from the housing stock is large. This paper explores how a market might be developed for the refurbishment activities assumed in these scenarios, taking the existing market for repair, maintenance and improvement (RMI) as its starting point. Interviews with 16 small and medium-sized enterprises (SMEs) in the construction industry reveal the interdependence of products, practices and processes in housing renovation activities. Conservative practice as well as innovation can be understood as the outcome of multi-lateral influences on firms from other firms, clients, the material buildings and products in their working lives, and from regulations and regulators. Contractors' openness to innovation is contingent on an informal approach to risk assessment, taking account of cost, time efficiency, client demands, and installer confidence in the reliability of the resulting work. The implications of the research are discussed in relation to the need for new practices and processes on refurbishment projects, raising questions for future research on key questions of quality assurance, performance over time, the application of standards, and vocational training. -- Highlights: •Repair, maintenance and improvement works are triggers for low-carbon refurbishment. •Millions of property owners and small firms make for fragmented decision-making. •Actor-Network Theory is used to frame decision-making processes for refurbishment. •Small builders can be innovative if clients allow time and money for experimentation. •Energy policy for existing homes needs to engage with the construction sector

  16. Effect of volume ratio of liquid to solid on the interfacial microstructure and mechanical properties of high chromium cast iron and medium carbon steel bimetal

    International Nuclear Information System (INIS)

    Xiong Bowen; Cai Changchun; Lu Baiping

    2011-01-01

    Highlights: → Volume ratio of liquid to solid affects significantly the interfacial microstructure. → Elemental diffusion activity is increased by increasing volume ratio. → Mechanical property is improved by increasing volume ratio. - Abstract: The high chromium cast iron and medium carbon steel bimetal was fabricated by liquid-solid casting technology. The effect of volume ratios of liquid to solid (6:1, 10:1 and 12:1) on the interfacial microstructure and mechanical properties of bimetal was investigated. The interfacial microstructure was analyzed using scanning electron microscope (SEM) and transmission electron microscope (TEM). The shear strength and microhardness in as-cast condition were studied at room temperature. The results show that the volume ratios of liquid to solid affect significantly the interfacial microstructure. When liquid-solid volume ratio was 6:1, the unbonded region was detected in interface region because the imported heat energy cannot support effectively the diffusion of element, whereas, when liquid-solid volume ratios reach 10:1 and 12:1, a sound interfacial microstructure was achieved by the diffusion of C, Cr, Mo, Cu and Mn, and metallurgical bonding without unbonded region, void and hole, etc. was detected. With the increase of liquid-solid volume ratio, the elemental diffusion activity improves, resulting in the increase of width of interface transition region. At the same distance from interface, with the increase of liquid-solid volume ratio, the microhardness is degraded in HCCI, but increased in MCS. The shear strength is also improved with the increase of liquid-solid volume ratio.

  17. Metabolism of sulfate-reducing bacteria and corrosion behavior of carbon steel in the continuous culturing medium; Renzoku baiyo baichichu ni okeru ryusan`en kangen no taisha to tansoko no fushoku kyodo

    Energy Technology Data Exchange (ETDEWEB)

    Baba, F.; Suzuki, T. [Ajinomoto Co. Inc., Tokyo (Japan); Seo, M. [Hokkaido University, Sapporo (Japan)

    1997-08-25

    Investigations were made on metabolism of sulfate-reducing bacteria and corrosion behavior of carbon steel in the continuous culturing medium. Sulfate-reducing bacteria were cultured for 50 days by supplying the culturing medium prepared to a prescribed chemical composition (containing Fe {sup 2+} at 0.01 mol/kg) at a rate of 10 cm {sup 3}/h, and drawing them out at the same rate. Test carbon steel pieces were immersed into this culturing medium. As a result, the following matters were clarified: the number of bacteria is maintained at more than 10 {sup 10}/cm{sup 3} after several days since inauguration of the immersion, with the bacteria stably producing H2S and FeS until the culturing is finished; comma-shaped bacteria which move actively and rod-shaped bacteria which do not move very actively exist in the culturing medium; a black film has been produced on surface of the test pieces throughout the culturing period, and satin-like corrosion was found underneath the surface; and weight increase of this film and weight decrease of the lower layer progress as the time lapses (the weight decrease of the lower layer has reached 40 mg/cm{sup 2} in 50 days). 28 refs., 8 figs., 1 tab.

  18. The effect of alloying on the resistance of carbon steel for oilfield applications to CO2 corrosion

    OpenAIRE

    Edmonds, David V.; Cochrane, Robert C.

    2005-01-01

    A systematic study has been conducted to investigate the influence of a wide range of alloying elements and different processing conditions on the resistance of low-carbon steels to CO2 corrosion. Strong carbide-forming microalloying elements such as Ti, Nb and V, along with Cr additions, and different levels of Mn, Si, Cu, Mo and Ni, have been explored, along with treatments simulating different processing conditions, for example, controlled rolling, and quenching and tempering. Corrosion te...

  19. Thermal conductivity of partially graphitized biocarbon obtained by carbonization of medium-density fiberboard in the presence of a Ni-based catalyst

    Science.gov (United States)

    Orlova, T. S.; Parfen'eva, L. S.; Smirnov, B. I.; Gutierrez-Pardo, A.; Ramirez-Rico, J.

    2016-01-01

    The thermal conductivity k and resistivity ρ of biocarbon matrices, prepared by carbonizing medium-density fiberboard at T carb = 850 and 1500°C in the presence of a Ni-based catalyst (samples MDF-C( Ni)) and without a catalyst (samples MDF-C), have been measured for the first time in the temperature range of 5-300 K. X-ray diffraction analysis has revealed that the bulk graphite phase arises only at T carb = 1500°C. It has been shown that the temperature dependences of the thermal conductivity of samples MDFC- 850 and MDF-C-850(Ni) in the range of 80-300 K are to each other and follow the law of k( T) ˜ T 1.65, but the use of the Ni-catalyst leads to an increase in the thermal conductivity by a factor of approximately 1.5, due to the formation of a greater fraction of the nanocrystalline phase in the presence of the Ni-catalyst at T carb = 850°C. In biocarbon MDF-C-1500 prepared without a catalyst, the dependence is k( T) ˜ T 1.65, and it is controlled by the nanocrystalline phase. In MDF-C-1500(Ni), the bulk graphite phase formed increases the thermal conductivity by a factor of 1.5-2 compared to the thermal conductivity of MDF-C-1500 in the entire temperature range of 5-300 K; k( T = 300 K) reaches the values of ˜10 W m-1 K-1, characteristic of biocarbon obtained without a catalyst only at high temperatures of T carb = 2400°C. It has been shown that MDF-C-1500(Ni) in the temperature range of 40‒300 K is characterized by the dependence, k( T) ˜ T 1.3, which can be described in terms of the model of partially graphitized biocarbon as a composite of an amorphous matrix with spherical inclusions of the graphite phase.

  20. Surface Modification of Micro-Alloyed High-Strength Low-Alloy Steel by Controlled TIG Arcing Process

    Science.gov (United States)

    Ghosh, P. K.; Kumar, Ravindra

    2015-02-01

    Surface modification of micro-alloyed HSLA steel plate has been carried out by autogenous conventional and pulse current tungsten inert gas arcing (TIGA) processes at different welding parameters while the energy input was kept constant. At a given energy input the influence of pulse parameters on the characteristics of surface modification has been studied in case of employing single and multi-run procedure. The role of pulse parameters has been studied by considering their summarized influence defined by a factor Φ. The variation in Φ and pulse frequency has been found to significantly affect the thermal behavior of fusion and accordingly the width and penetration of the modified region along with its microstructure, hardness and wear characteristics. It is found that pulsed TIGA is relatively more advantageous over the conventional TIGA process, as it leads to higher hardness, improved wear resistance, and a better control over surface characteristics.

  1. Structural Origin of the Enhanced Glass-Forming Ability Induced by Microalloying Y in the ZrCuAl Alloy

    Directory of Open Access Journals (Sweden)

    Gu-Qing Guo

    2016-03-01

    Full Text Available In this work, the structural origin of the enhanced glass-forming ability induced by microalloying Y in a ZrCuAl multicomponent system is studied by performing synchrotron radiation experiments combined with simulations. It is revealed that the addition of Y leads to the optimization of local structures, including: (1 more Zr-centered and Y-centered icosahedral-like clusters occur in the microstructure; (2 the atomic packing efficiency inside clusters and the regularity of clusters are both enhanced. These structural optimizations help to stabilize the amorphous structure in the ZrCuAlY system, and lead to a high glass-forming ability (GFA. The present work provides an understanding of GFAs in multicomponent alloys and will shed light on the development of more metallic glasses with high GFAs.

  2. Additional grain refinement in recrystallization controlled rolling of Ti-microalloyed steels processed by near-net-shape casting technology

    International Nuclear Information System (INIS)

    Arribas, M.; Lopez, B.; Rodriguez-Ibabe, J.M.

    2008-01-01

    This paper analyzes the recrystallization kinetics in Ti-microalloyed steels processed using 'beam blank' casting technology. The faster solidification rates associated with this technology brings a finer precipitation of TiN particles which are very effective in controlling austenite grain growth during hot working. Furthermore, these small precipitates have been shown to delay static and dynamic recrystallization. The finer the precipitates the higher the delay in recrystallization. Nevertheless, beyond particle size and distribution, the level of delay is very dependent on microstructure (above all austenite grain size) and deformation conditions (strain and temperature). This paper studies the effects of this recrystallization delay on the microstructure evolution during hot rolling. Special attention was paid to the study of the occurrence of partial recrystallization during the final stages of rolling, which could lead to the presence of mixed microstructures before transformation. The possibility of achieving an additional austenite grain size refinement prior to transformation was evaluated

  3. Effect of Ag micro-alloying on the microstructure and properties of Cu-14Fe in situ composite

    International Nuclear Information System (INIS)

    Liu, K.M.; Lu, D.P.; Zhou, H.T.; Atrens, A.; Zou, J.; Yang, Y.L.; Zeng, S.M.

    2010-01-01

    This paper studied Ag micro-alloying in the deformation-processed Cu-14Fe in situ composite, by a comparison of Cu-14Fe and Cu-14Fe-0.06Ag. Each alloy was prepared by casting and processed into an in situ composite by hot and cold working. The microstructures were documented using light microscopy and scanning electron microscopy (SEM). The mechanical properties were measured with a tensile-testing machine. The electrical conductivity was measured with a micro-ohmmeter. For both alloys, the as-cast microstructure consisted of a Cu matrix and Fe dendrites; after hot and cold working the microstructure consisted of a Cu matrix containing Fe fibres elongated in the working direction. The as-cast Ag-containing alloy contained finer Fe dendrites. The Ag-containing in situ composite had thinner Fe fibres, higher tensile strength, higher ductility, and higher conductivity. The cold worked Cu-14Fe-0.06Ag in situ composite with cumulative cold deformation strain η = 7.8 (where η = ln(A 0 /A) and A 0 and A are the original and final cross-section areas, respectively), achieved a tensile strength of 930 MPa and a conductivity of 56%IACS (International Annealed Copper Standard; 17.241 nΩ m is defined as 100%IACS). The Ag micro-alloyed in situ composite had a combination of properties comparable to that of a much more expensive alloy containing much more Ag. After 1 h heat treatment at 300 deg. C, the tensile strength was increased to 950 MPa and the conductivity was increased to 56.4%IACS.

  4. The impact of carbon sequestration on the production cost of electricity and hydrogen from coal and natural-gas technologies in Europe in the medium term

    International Nuclear Information System (INIS)

    Tzimas, Evangelos; Peteves, Stathis D.

    2005-01-01

    Carbon sequestration is a distinct technological option with a potential for controlling carbon emissions; it complements other measures, such as improvements in energy efficiency and utilization of renewable energy sources. The deployment of carbon sequestration technologies in electricity generation and hydrogen production will increase the production costs of these energy carriers. Our economic assessment has shown that the introduction of carbon sequestration technologies in Europe in 2020, will result in an increase in the production cost of electricity by coal and natural gas technologies of 30-55% depending on the electricity-generation technology used; gas turbines will remain the most competitive option for generating electricity; and integrated gasification combined cycle technology will become competitive. When carbon sequestration is coupled with natural-gas steam reforming or coal gasification for hydrogen production, the production cost of hydrogen will increase by 14-16%. Furthermore, natural-gas steam reforming with carbon sequestration is far more economically competitive than coal gasification

  5. The effect of clustering on the mobility of dislocations during aging in Nb-microalloyed strip cast steels: In situ heating TEM observations

    International Nuclear Information System (INIS)

    Shrestha, Sachin L.; Xie, Kelvin Y.; Ringer, Simon P.; Carpenter, Kristin R.; Smith, David R.; Killmore, Chris R.; Cairney, Julie M.

    2013-01-01

    Cluster-strengthened Nb-microalloyed strip cast steels are of interest as clustering during aging leads to an enhancement in strength without compromising ductility, resulting in desirable mechanical properties. However, the precise strengthening mechanism is not well understood. Using in situ heating transmission electron microscopy, clustering was found to impede the movement of dislocations during aging. The attractive combination of ductility and strength was attributed to the effects of recovery and the restricted movement of dislocations through clustering

  6. Niobium Solar Mobile Project — High Strength Niobium Microalloyed Steel as a Solution to Improve Electric Super Scooter and Motorcycle Performance

    Science.gov (United States)

    Richards, Terry; Kauppi, Erik; Flanagan, Lauren; Ribeio, Eduardo A. A. G.; Nogueira, Marcos A. Stuart; McCourtney, Ian

    This paper presents the advantages of replacing mild steel with high strength niobium microalloyed steel in the structure of Electric Super Scooters, Electric Cargo Motorcycles and Solar Charging Stations. The Mini-Fleet-in-a-Box concept was developed by Current Motor to guarantee mobility, efficiency and solar generated electricity. With the adoption of niobium microalloyed high strength steel for more than 90% of the Super Scooter and Motorcycle structures, it was possible to redesign the frame, resulting in a 31% weight reduction and a very modern and functional body. Together with a new powertrain, these changes were responsible for increasing Motorcycle autonomy by more than 15%, depending on average speed. The new frame design reduced the number of high strain points in the frame, increasing the safety of the project. The Solar Charging Station was built using the container concept and designed with high strength niobium microalloyed steel, which resulted in a weight reduction of 25%. CBMM's facility in Araxá, Brazil was selected in the second half of 2013 as the demonstration site to test the efficiency of the Super Scooter and Solar Charging Station. Each Super Scooter has run more than 2,000 km maintenance-free with an autonomy of more than 100 km per charge.

  7. Length-scale dependent microalloying effects on precipitation behaviors and mechanical properties of Al–Cu alloys with minor Sc addition

    International Nuclear Information System (INIS)

    Jiang, L.; Li, J.K.; Liu, G.; Wang, R.H.; Chen, B.A.; Zhang, J.Y.; Sun, J.; Yang, M.X.; Yang, G.; Yang, J.; Cao, X.Z.

    2015-01-01

    Heat-treatable Al alloys containing Al–2.5 wt% Cu (Al–Cu) and Al–2.5 wt% Cu–0.3 wt% Sc (Al–Cu–Sc) with different grain length scales, i.e., average grain size >10 μm ( defined coarse grained, CG), 1–2 μm (fine grained, FG), and <1 μm (ultrafine grained, UFG), were prepared by equal-channel angular pressing (ECAP). The length scale and Sc microalloying effects and their interplay on the precipitation behavior and mechanical properties of the Al–Cu alloys were systematically investigated. In the Al–Cu alloys, intergranular θ-Al 2 Cu precipitation gradually dominated by sacrificing the intragranular θ′-Al 2 Cu precipitation with reducing the length scale. Especially in the UFG regime, only intergranular θ-Al 2 Cu particles were precipitated and intragranular θ′-Al 2 Cu precipitation was completely disappeared. This led to a remarkable reduction in yield strength and ductility due to insufficient dislocation storage capacity. The minor Sc addition resulted in a microalloying effect in the Al–Cu alloy, which, however, is strongly dependent on the length scale. The smaller is the grain size, the more active is the microalloying effect that promotes the intragranular precipitation while reduces the intergranular precipitation. Correspondingly, compared with their Sc-free counterparts, the yield strength of post-aged CG, FG, and UFG Al–Cu alloys with Sc addition increased by ~36 MPa, ~56 MPa, and ~150 MPa, simultaneously in tensile elongation by ~20%, ~30%, and 280%, respectively. The grain size-induced evolutions in vacancy concentration/distribution and number density of vacancy-solute/solute–solute clusters and their influences on precipitation nucleation and kinetics have been comprehensively considered to rationalize the length scale-dependent Sc microalloying mechanisms using positron annihilation lifetime spectrum and three dimension atom probe. The increase in ductility was analyzed in the light of Sc microalloying effect and the

  8. Length-scale dependent microalloying effects on precipitation behaviors and mechanical properties of Al–Cu alloys with minor Sc addition

    Energy Technology Data Exchange (ETDEWEB)

    Jiang, L.; Li, J.K. [State Key Laboratory for Mechanical Behavior of Materials, Xi' an Jiaotong University, Xi' an 710049 (China); Liu, G., E-mail: lgsammer@mail.xjtu.edu.cn [State Key Laboratory for Mechanical Behavior of Materials, Xi' an Jiaotong University, Xi' an 710049 (China); Wang, R.H. [School of Materials Science and Engineering, Xi' an University of Technology, Xi' an 710048 (China); Chen, B.A.; Zhang, J.Y. [State Key Laboratory for Mechanical Behavior of Materials, Xi' an Jiaotong University, Xi' an 710049 (China); Sun, J., E-mail: junsun@mail.xjtu.edu.cn [State Key Laboratory for Mechanical Behavior of Materials, Xi' an Jiaotong University, Xi' an 710049 (China); Yang, M.X.; Yang, G. [Central Iron and Steel Research Institute, Beijing 100081 (China); Yang, J.; Cao, X.Z. [Key Laboratory of Nuclear Radiation and Nuclear Energy Technology, Institute of High Energy Physics, Chinese Academy of Sciences, Beijing 100049 (China)

    2015-06-18

    Heat-treatable Al alloys containing Al–2.5 wt% Cu (Al–Cu) and Al–2.5 wt% Cu–0.3 wt% Sc (Al–Cu–Sc) with different grain length scales, i.e., average grain size >10 μm ( defined coarse grained, CG), 1–2 μm (fine grained, FG), and <1 μm (ultrafine grained, UFG), were prepared by equal-channel angular pressing (ECAP). The length scale and Sc microalloying effects and their interplay on the precipitation behavior and mechanical properties of the Al–Cu alloys were systematically investigated. In the Al–Cu alloys, intergranular θ-Al{sub 2}Cu precipitation gradually dominated by sacrificing the intragranular θ′-Al{sub 2}Cu precipitation with reducing the length scale. Especially in the UFG regime, only intergranular θ-Al{sub 2}Cu particles were precipitated and intragranular θ′-Al{sub 2}Cu precipitation was completely disappeared. This led to a remarkable reduction in yield strength and ductility due to insufficient dislocation storage capacity. The minor Sc addition resulted in a microalloying effect in the Al–Cu alloy, which, however, is strongly dependent on the length scale. The smaller is the grain size, the more active is the microalloying effect that promotes the intragranular precipitation while reduces the intergranular precipitation. Correspondingly, compared with their Sc-free counterparts, the yield strength of post-aged CG, FG, and UFG Al–Cu alloys with Sc addition increased by ~36 MPa, ~56 MPa, and ~150 MPa, simultaneously in tensile elongation by ~20%, ~30%, and 280%, respectively. The grain size-induced evolutions in vacancy concentration/distribution and number density of vacancy-solute/solute–solute clusters and their influences on precipitation nucleation and kinetics have been comprehensively considered to rationalize the length scale-dependent Sc microalloying mechanisms using positron annihilation lifetime spectrum and three dimension atom probe. The increase in ductility was analyzed in the light of Sc microalloying

  9. Carbon-13 isotope fractionation in the decarboxylation of phenylpropiolic (PPA) below and above its melting point and in the decarboxylation of PPA in phenylacetylene medium

    International Nuclear Information System (INIS)

    Zielinski, M.; Zielinska, A.; Papiernik-Zielinska, H.

    2000-01-01

    C-13 isotope fractionation in the decarboxylation of pure phenylpropiolic acid (PPA) below and above its melting point and the decarboxylation of PPA in phenylacetylene solutions has been investigated in sealed under vacuum reaction vessels. The reactive PPA undergoing decarboxylation polymerizes with the liquid product, phenylacetylene in reaction cage producing a condensation compound, which does not decarboxylate measurably in the 120-190 o C. Especially low final carbon dioxide yields (about 11%) have been obtained in the decarboxylation of PPA in phenylacetylene solution at 132 o C and below this temperature. The carbon dioxide is depleted in carbon-13. The ratio of the carbon isotope ratios of carboxylic carbon of PPA before decarboxylation, R( 13 C/ 12 C so ), and of the first portions of carbon dioxide obtained at partial decarboxylation R( 13 C/ 12 C) pf , located in the range 1.007-1.010, indicates that the pure kinetic fractionation of 13 C in the elementary decarboxylation step is negligible and the C-13 fractionation in the condensed phase dimer/monomer equilibria contributes mainly to the resultant experimental carbon isotope fractionation. A preliminary discussion of the experimental isotope findings is presented. (author)

  10. Production of medium-chain fatty acids and higher alcohols by a synthetic co-culture grown on carbon monoxide or syngas

    NARCIS (Netherlands)

    Diender, M.; Stams, A.J.M.; Machado de Sousa, D.Z.

    2016-01-01

    Background
    Synthesis gas, a mixture of CO, H2, and CO2, is a promising renewable feedstock for bio-based production of organic chemicals. Production of medium-chain fatty acids can be performed via chain elongation, utilizing acetate and ethanol as main substrates. Acetate and ethanol are main

  11. The use of coal mining wastes as soilles growing medium; Utilizacion de los Esteriles del Carbon como Sustratos en Cultivos sin Suelo

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    1998-12-31

    This project was aimed at evaluating the technical appropriateness of coal mining wastes as: (I) substrate in soilless culture (hydroponics) being used as the only medium or in a mixture with other materials; (II) basic component for container gardening of decorative plants in order to determine the standard mixture with other materials and the most appropriate plant. A greenhouse was built for conducting the tests, vegetables and decorative plants were planted and an exhaustive control of the plantations was carried out. The results obtained proved that coal mining wastes can be used as soilless growing medium for vegetables and for container gardening. At present, the company HORPLASMA with three greenhouses (11,300 m``2) is dedicated to the growing of vegetables with coal mining wastes as substrate and the pot-culture of more than 30,000 decorative plants using as substrate a mixture of 60% coal mining wastes and 40% turf. (Author)

  12. Antimony (Sb) sorption studies on zircaloy, carbon steel (CS) and magnetite coated CS (MCS) surfaces in aqueous medium at pH 10.2 and 280℃

    International Nuclear Information System (INIS)

    Keny, S.J.; Kumbhar, A.G.; Achary, S.N.; Basu, Saibal

    2014-01-01

    Antimony sorption studies on zircaloy, CS and magnetite coated carbon steel (MCS) at primary heat transport temperature (290℃) of pressurised heavy water reactor (PHWR) are of direct relevance in investigating Sb activity problem faced in Indian PHWRs. Sb impregnated PHT pump carbon bearing releases Sb to reactor core. This Sb activates, and redeposit on out-of-core surfaces and results in exposure and apparent high decontamination factors. This Sb is not amenable to normal decantation. The form and state of deposited Sb is not yet fully known. This works attempts for this

  13. Processing-structure-mechanical property relationship in Ti-Nb microalloyed steel: Continuous cooling versus interrupted cooling

    Energy Technology Data Exchange (ETDEWEB)

    Natarajan, V.V. [Laboratory for Excellence in Advanced Steel Research, Materials Science and Engineering Program, Department of Metallurgical, Materials and Biomedical Engineering, University of Texas at El Paso, 500 W. University Avenue, El Paso, TX 79968 (United States); Liu, S. [Laboratory for Excellence in Advanced Steel Research, Materials Science and Engineering Program, Department of Metallurgical, Materials and Biomedical Engineering, University of Texas at El Paso, 500 W. University Avenue, El Paso, TX 79968 (United States); School of Materials Science and Engineering, University of Science and Technology, Beijing (China); Challa, V.S.A. [Laboratory for Excellence in Advanced Steel Research, Materials Science and Engineering Program, Department of Metallurgical, Materials and Biomedical Engineering, University of Texas at El Paso, 500 W. University Avenue, El Paso, TX 79968 (United States); Misra, R.D.K., E-mail: dmisra2@utep.edu [Laboratory for Excellence in Advanced Steel Research, Materials Science and Engineering Program, Department of Metallurgical, Materials and Biomedical Engineering, University of Texas at El Paso, 500 W. University Avenue, El Paso, TX 79968 (United States); Sidorenko, D.M.; Mulholland, M.D.; Manohar, M.; Hartmann, J.E. [ArcelorMittal Global R& D Center, 3001 East Columbus Drive, East Chicago, IN 46312 (United States)

    2016-08-01

    The process parameters associated with thermo-mechanical controlled processing (TMCP) of steels play an important role in influencing the ultimate mechanical properties. The study of TMCP parameters have not received the required attention. In this regard, we elucidate here the impact of finish cooling temperature on interrupted cooling and compare with continuous cooling on microstructural evolution and precipitation behavior and associated mechanical properties in Ti-Nb microalloyed steels. The microstructural evolution was studied via transmission electron microscopy and electron back scattered diffraction (EBSD). The microstructure of continuously cooled and interrupted cooled steels with different finish exit temperatures consisted of polygonal ferrite, bainite and martensite/austenite constituent. However, the fraction of different microstructural constituents was different in each of the experimental steels. Similarly, there were differences in the distribution and average size of (Nb, Ti)C precipitates. The aforementioned differences in the microstructure and precipitation introduced differences in tensile properties. Furthermore, electron back scattered diffraction studies indicated distinct variation in average grain area and high angle boundaries between continuously cooled and interrupted cooled steels.

  14. Use of carbon dioxide as a reaction medium in the thermo-chemical process for the enhanced generation of syngas and tuning adsorption ability of biochar

    International Nuclear Information System (INIS)

    Cho, Dong-Wan; Kwon, Eilhann E.; Song, Hocheol

    2016-01-01

    Highlights: • Utilizing CO_2 as a reaction medium in thermo-chemical conversion of aquatic biomass. • Enhanced generation of syngas in the presence of CO_2. • Considerable reduction of pyrolytic oil in CO_2-assisted pyrolysis. • Generation of biochar with high surface area and more porous structure by CO_2. - Abstract: This study mechanistically investigated the influences of CO_2 on syngas (H_2 and CO) production during thermo-chemical conversion of red seaweed, and further explored the possible utility of the produced biochar as a medium for adsorption of inorganic/organic contaminants in aqueous phase. In order to elucidate the key roles of CO_2 in the thermo-chemical process, the composition analysis of syngas and the qualitative analysis of pyrolytic oil were conducted and compared with those in pyrolysis in N_2 condition. Pyrolysis of red seaweed in the presence of CO_2 led to the enhanced generation of syngas at the entire experimental temperatures. For example, the ratio of CO to H_2 in the presence of CO_2 at 620 °C was enhanced by ∼400%, as compared to the case in N_2. This enhanced generation of syngas resulted in significant pyrolytic oil reduction by ∼70% at 620 °C via the unknown reactions between VOCs and CO_2. In addition, biochar generated in the CO_2 environment exhibited comparatively higher surface area (61 m"2 g"−"1) and more porous structure. The morphological modification induced by CO_2 provided the favorable condition for removal of methylene blue from the aqueous phase. Thus, this study experimentally demonstrated that exploiting CO_2 as a reaction medium would provide an attractive option for the enhanced generation of syngas and the tuned adsorption capability of biochar.

  15. Effect of Q&P heat treatment on fine microstructure and mechanical properties of a low-alloy medium-carbon steel

    Science.gov (United States)

    Jafari, Rahim; Kheirandish, Shahram; Mirdamadi, Shamsoddin

    2018-01-01

    The current research investigates the effect of ultrafine microstructure resulted from Quench and Partitioning (Q&P) process on obtaining ultra-high strengths in a low-alloy steel with 4wt.% carbon. The purpose of Q&P heat treatment is to enrich the austenite with carbon by partitioning of carbon from supersaturated martensite to austenite, in order to stabilize it to the room temperature. The microstructure, consequently, is consists of martensite, retained austenite and in some conditions bainite. Two-step Q&P heat treatment with quench and partitioning temperatures equal to 120°C and 300°C respectively were applied to the samples at different times. Mechanical behavior was studied by tensile test. The microstructure of the samples was observed using SEM, and TEM and to quantify the amount of retained austenite X-ray diffraction was used. The retained austenite grain size was estimated to be about 0.5 µm and the highest amount of retained austenite obtained was 10 vol%. All samples showed a yield strength and a tensile strength of above 900MPa and 1500MP respectively. The yield strength increased with increase in partitioning time, whereas tensile strength showed an inverse behavior. The elongation in samples varied from 5% to 9% which seemed to not have a direct connection with the amount of retained austenite, but instead it was related to the ferritic structures formed during partitioning such as coalesced martensite, bainite and tempered martensite.

  16. Understanding the corrosion inhibition of carbon steel and copper in sulphuric acid medium by amino acids using electrochemical techniques allied to molecular modelling methods

    International Nuclear Information System (INIS)

    Mendonça, Glaydson L.F.; Costa, Stefane N.; Freire, Valder N.; Casciano, Paulo N.S.; Correia, Adriana N.; Lima-Neto, Pedro de

    2017-01-01

    Highlights: • Corrosion inhibition of carbon steel and of copper by the amino acids was studied. • Inhibition efficiencies were experimentally achieved by electrochemical impedance. • DFT and Monte Carlo methods allowed correlating molecular properties with inhibition efficiency. • The corrosion inhibition followed the electron donation the electron-back donations process. - Abstract: Six amino acids were evaluated as corrosion inhibitors for carbon steel and copper in 0.5 mol L"−"1 H_2SO_4 solution by potentiodynamic polarization and electrochemical impedance techniques allied to Density Functional Theory (DFT) and Monte Carlo computations The corrosion inhibitor rankings were: Arg > Gln > Asn > Met > Cys > Ser, for copper, and Met > Cys > Ser > Arg > Gln > Asn, for carbon steel. The DFT approach failed to explain the corrosion inhibition rating based on the HOMO and LUMO energies of the isolated amino acid molecules, while the simpler classical Monte Carlo approach, performed considering the interaction energies between the corrosion inhibitor and the metallic substrate, was successful.

  17. Effects of Cu and Ni additions on the heat affected zone (HAZ) microstructure and mechanical properties of a C-Mn niobium microalloyed steel

    International Nuclear Information System (INIS)

    Ale, Ricardo Miranda; Rebello, Joao Marques A.; Charlier, Jacques

    1996-01-01

    The influence of small additions of Cu and Ni on the heat affected zone microstructure and mechanical properties, particularly toughness, of C-Mn microalloyed steel has been evaluated. Cu and Ni additions improved the toughness of both coarse grained region and coarse grained region reheated intercritically due to the formation of lower bainite and avoiding Nb precipitation hardening, respectively. With Cu and Ni additions the embrittlement of the coarse grained region reheated intercritically, due to MA constituent, is counterbalanced by the formation of fine ferrite recrystallized grains near the prior austenite grain boundaries and the stabilisation of austenite between ferrite laths. (author)

  18. A Study on the Corrosion Behavior of Carbon Steel Exposed to a H2S-Containing NH4Cl Medium

    Science.gov (United States)

    Wang, Hai-bo; Li, Yun; Cheng, Guang-xu; Wu, Wei; Zhang, Yao-heng

    2018-04-01

    NH4Cl corrosion failure often occurs in the overhead systems of hydrotreaters, and this failure is always accompanied by the appearance of H2S. A combination of electrochemical and surface spectroscopic (SEM/EDS, AFM, XRD) techniques was used to investigate the effect of different factors, including the surface roughness, temperature, dissolved oxygen, pH and H2S concentration, on the corrosion behavior of carbon steel in an NH4Cl environment with the presence of H2S. The effect of H2S concentrations (at the ppm level) on the corrosion behavior of carbon steel was systematically revealed. The experimental results clearly indicated that the corrosion rate reached a minimum value at 10 ppm H2S. The steel surface was covered by a uniform corrosion product film in a 10 ppm H2S environment, and the corrosion product film was tight and protective. The ammonia from NH4Cl helped maintaining the protectiveness of the corrosion films in this environment. Dissolved oxygen mainly accelerated the cathodic reaction. The cathodic limiting current density increased with increasing temperature, and the anodic branch polarization curves were similar at different temperatures. The anodic current density decreased as the pH decreased, and the cathodic current density increased as the pH decreased. The absolute surface roughness (R a) of carbon steel increased from 132.856 nm at 72 h to 153.973 nm at 144 h, and the rougher surface resulted in a higher corrosion rate. The critical innovation in this research was that multiple influential factors were revealed in the NH4Cl environment with the presence of H2S.

  19. A Study on the Corrosion Behavior of Carbon Steel Exposed to a H2S-Containing NH4Cl Medium

    Science.gov (United States)

    Wang, Hai-bo; Li, Yun; Cheng, Guang-xu; Wu, Wei; Zhang, Yao-heng

    2018-05-01

    NH4Cl corrosion failure often occurs in the overhead systems of hydrotreaters, and this failure is always accompanied by the appearance of H2S. A combination of electrochemical and surface spectroscopic (SEM/EDS, AFM, XRD) techniques was used to investigate the effect of different factors, including the surface roughness, temperature, dissolved oxygen, pH and H2S concentration, on the corrosion behavior of carbon steel in an NH4Cl environment with the presence of H2S. The effect of H2S concentrations (at the ppm level) on the corrosion behavior of carbon steel was systematically revealed. The experimental results clearly indicated that the corrosion rate reached a minimum value at 10 ppm H2S. The steel surface was covered by a uniform corrosion product film in a 10 ppm H2S environment, and the corrosion product film was tight and protective. The ammonia from NH4Cl helped maintaining the protectiveness of the corrosion films in this environment. Dissolved oxygen mainly accelerated the cathodic reaction. The cathodic limiting current density increased with increasing temperature, and the anodic branch polarization curves were similar at different temperatures. The anodic current density decreased as the pH decreased, and the cathodic current density increased as the pH decreased. The absolute surface roughness ( R a) of carbon steel increased from 132.856 nm at 72 h to 153.973 nm at 144 h, and the rougher surface resulted in a higher corrosion rate. The critical innovation in this research was that multiple influential factors were revealed in the NH4Cl environment with the presence of H2S.

  20. Refining cocoon to prepare (N, S, and Fe) ternary-doped porous carbon aerogel as efficient catalyst for the oxygen reduction reaction in alkaline medium

    Science.gov (United States)

    Li, Changqing; Sun, Fengzhan; Lin, Yuqing

    2018-04-01

    Various advanced sulfur doped Fe-N-C non-noble metal catalysts of oxygen reduction reaction (ORR) have been recently designed and reported with excellent catalytic activity. Herein, we refined cocoon with several steps to form silk fibroin solution, treated with iron salt to prepare an easy available, heteroatom (N, S, and Fe) ternary-doped, porous carbon aerogel (HDCA). Heteroatom existed in organic compounds in silk fibroin endow active site for ORR of the resultant carbon frameworks. Moreover, the amino acids presented in silk fibroin acted as ligands, functioning with Fe ions to form FeNx coordination compounds, which also served as active sites towards ORR. The synthesized HDCA electrocatalysts, especially HDCA-800 (obtained at 800 °C) displayed excellent catalytic activity with onsets, half-wave potential of 0.94 V, 0.79 V and higher limited current density of 3.80 mA cm-2 through a near four-electron reduction pathway with an average electron transferred number of 3.86, making them promising alternatives for state-of-the-art ORR electrocatalysts in fuel cell field. The porous structure with synergistic effect of N and S heteroatom doping has been proposed to play a key role in facilitating the desired ORR reaction.

  1. In situ synthesis of TiB2-TiC particulates locally reinforced medium carbon steel-matrix composites via the SHS reaction of Ni-Ti-B4C system during casting

    International Nuclear Information System (INIS)

    Wang, H.Y.; Huang, L.; Jiang, Q.C.

    2005-01-01

    The fabrication of medium carbon steel-matrix composites locally reinforced with in situ TiB 2 -TiC particulates using self-propagating high-temperature synthesis (SHS) reaction of Ni-Ti-B 4 C system during casting was investigated. X-ray diffraction (XRD) results reveal that the exotherm of 1042 deg. C initiated by heat release of the solid state reaction in the differential thermal analysis (DTA) curve is an incomplete reaction in Ni-Ti-B 4 C system. As-cast microstructures of the in situ processed composites reveal a relatively uniform distribution of TiB 2 -TiC particulates in the locally reinforced regions. Furthermore, the particulate size and micro-porosity in the locally reinforced regions are significantly decreased with the increasing of the Ni content in the preforms. For a Ni content of 30 and 40 wt.%, near fully dense composites locally reinforced with in situ TiB 2 and TiC particulates can be fabricated. Although most of fine TiB 2 and TiC particulates which form by the reaction-precipitation mechanism during SHS reaction are present in the locally reinforced region, some large particulates which form by the nucleation-growth mechanism during solidification are entrapped inside the Fe-rich region located in the reinforcing region or inside the matrix region nearby the interface between matrix and reinforcing region. The hardness of the reinforcing region in the composite is significantly higher than that of the unreinforced medium carbon steel. Furthermore, the hardness values of the composites synthesized from 30 to 40 wt.% Ni-Ti-B 4 C systems are higher than those of the composites synthesized from 10 to 20 wt.% Ni-Ti-B 4 C systems

  2. Surface chemistry of pyrite during the pre-processing for the flotation in alkaline sodium carbonate medium during uranium ore processing

    International Nuclear Information System (INIS)

    Neudert, A.; Sommer, H.; Schubert, H.

    1991-01-01

    It is often necessary during processing of uranium ore to flotate pyrite at sodium carbonate alkaline pH value caused by the subsequent hydrometallurgical process stages. It was found out by ESCA analyses that the pyrite surface changes chemically prior to the addition of flotation agents. FeS 2 becomes FeO within a few hours in the case of storage in process water; limonite and/or geothite result from pyrite. The copper ions of the activator CuSO 4 are exclusively monovalent on the pyrite surface. The resulting heavy metal xanthogenate is Cu(I) xanthogenate. Conclusions are derived for the flotation practice for the intensification of the reagent regime. (orig./HP) [de

  3. Pd Nanoparticles-Supported Carbon Nanotube-Encapsulated NiO/MgO Composite as an Enhanced Electrocatalyst for Ethanol Electrooxidation in Alkaline Medium

    DEFF Research Database (Denmark)

    Mahendiran, Chinnathambi; Rajesh, Dhanushkotti; Maiyalagan, Thandavarayan

    2017-01-01

    /(NiO/MgO-CNT) catalysts exhibit superior electrochemical performance compare to the commercial Pd/C catalysts. The current densities of the main anodic peak of electrooxidation of ethanol increases sharply for the Pd/(NiO/MgO-CNT) (98.20 mA/cm2), which are ∼2.1 times as large as that of Pd/C (47 mA/cm2). The excellent......In this work, an easy method is developed to prepare well-dispersed palladium nanoparticles into the carbon nanotube (CNT) encapsulated NiO/MgO nanocomposite by the chemical reduction method. CNT encapsulated NiO/MgO nanocomposite were prepared by autogenous pressure at elevated temperature (RAPET...

  4. Simulation techniques of medium or small sized coal mining; Sistema de simulacion de labores de minas subterraneas de carbon de tamano mediano o pequeno

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    1998-12-01

    Usually an underground mining company designs new production systems in order to reach higher productivity levels, but there is always some uncertainty about reaching the planned figures. This research project, so called Project SimCAR, applies to medium or small sized coal mining companies and tries to become a powerful tool in helping technical staff to answer questions about how future systems will behave. The project`s paradigm is to use computer simulation techniques in order to diminish the implicit uncertainty associated to coal mining activities. As a result, this implies to obtain the best possible scenarios for real economic investments in mine planning. The final programs we have built help technical staff to: 1. Study existing systems in depth. The precision of the resulting model exclusively depends on the correctness of input data and a perfect understanding of the system`s logic processes. 2. Perform several changes on the input system variables over the simulated models in order to allow the technical staff to know the system will react under several conditions. 3. Introduce new strategies on the model construction in order to get a complete optimization under productive and economic viewpoints. (Author)

  5. The determining impact of coiling temperature on the microstructure and mechanical properties of a titanium-niobium ultrahigh strength microalloyed steel: Competing effects of precipitation and bainite

    Energy Technology Data Exchange (ETDEWEB)

    Natarajan, V.V.; Challa, V.S.A. [Laboratory for Excellence in Advanced Steel Research, Materials Science and Engineering Program, Department of Metallurgical, Materials and Biomedical Engineering, 500 W. University Avenue, University of Texas at El Paso, El Paso, TX 79968 (United States); Misra, R.D.K., E-mail: dmisra2@utep.edu [Laboratory for Excellence in Advanced Steel Research, Materials Science and Engineering Program, Department of Metallurgical, Materials and Biomedical Engineering, 500 W. University Avenue, University of Texas at El Paso, El Paso, TX 79968 (United States); Sidorenko, D.M.; Mulholland, M.D.; Manohar, M.; Hartmann, J.E. [ArcelorMittal Global R& D Center, 3001 East Columbus Drive, East Chicago, IN 46312 (United States)

    2016-05-17

    We elucidate here the influence of coiling temperature on the microstructure and mechanical properties, in an ultrahigh strength titanium-niobium microalloyed steel. The objective was to underscore the impact of coiling temperature on the nature and distribution of microstructural constituents (including different phases, precipitates, and dislocation structure) that significantly contributed to differences in the yield and tensile strength of these steels. Depending on the coiling temperature, the microstructure consisted of either a combination of fine lath-type bainite and polygonal ferrite or polygonal ferrite together with the precipitation of microalloyed carbides of size ~2–10 nm in the matrix and at dislocations. The microstructure of steel coiled at lower temperature predominantly consisted of bainitic ferrite with lower yield strength compared to the steel coiled at higher temperature, and the yield to tensile strength ratio was 0.76. The steel coiled at higher temperature consisted of polygonal ferrite and extensive precipitation of carbides and was characterized by higher yield strength and with yield strength/tensile strength ratio of 0.936. The difference in the tensile strength was insignificant for the two coiling temperatures. The observed microstructure was consistent with the continuous cooling transformation diagram.

  6. Precipitation behavior during thin slab thermomechanical processing and isothermal aging of copper-bearing niobium-microalloyed high strength structural steels: The effect on mechanical properties

    Energy Technology Data Exchange (ETDEWEB)

    Misra, R.D.K., E-mail: dmisra@louisiana.edu [Center for Structural and Functional Materials, University of Louisiana at Lafayette, P.O. Box 44130, Lafayette, LA 70503 (United States); Jia, Z. [Center for Structural and Functional Materials, University of Louisiana at Lafayette, P.O. Box 44130, Lafayette, LA 70503 (United States); O' Malley, R. [Nucor Steel Decatur, LLC Sheet Mill, 4301, Iverson Blvd., Trinity, AL 35673 (United States); Jansto, S.J. [CBMM-Reference Metals Company, 1000 Old Pond Road, Bridgeville, PA 15017 (United States)

    2011-11-15

    Highlights: {yields} Copper does not significantly influence toughness. {yields} Copper precipitation during aging occurs at dislocations. {yields} Precipitation of copper and carbides is mutually exclusive. - Abstract: We describe here the precipitation behavior of copper and fine-scale carbides during thermo-mechanical processing and isothermal aging of copper-bearing niobium-microalloyed high strength steels. During thermo-mechanical processing, precipitation of {epsilon}-copper occurs in polygonal ferrite and at the austenite-ferrite interface. In contrast, during isothermal aging, nucleation of {epsilon}-copper precipitation occurs at dislocations. In the three different chemistries investigated, the increase in strength associated with copper during aging results only in a small decrease in impact toughness, implying that copper precipitates do not seriously impair toughness, and can be considered as a viable strengthening element in microalloyed steels. Precipitation of fine-scale niobium carbides occurs extensively at dislocations and within ferrite matrix together with vanadium carbides. In the presence of titanium, titanium carbides act as a nucleus for niobium carbide formation. Irrespective of the nature of carbides, copper precipitates and carbides are mutually exclusive.

  7. Precipitation behavior during thin slab thermomechanical processing and isothermal aging of copper-bearing niobium-microalloyed high strength structural steels: The effect on mechanical properties

    International Nuclear Information System (INIS)

    Misra, R.D.K.; Jia, Z.; O'Malley, R.; Jansto, S.J.

    2011-01-01

    Highlights: → Copper does not significantly influence toughness. → Copper precipitation during aging occurs at dislocations. → Precipitation of copper and carbides is mutually exclusive. - Abstract: We describe here the precipitation behavior of copper and fine-scale carbides during thermo-mechanical processing and isothermal aging of copper-bearing niobium-microalloyed high strength steels. During thermo-mechanical processing, precipitation of ε-copper occurs in polygonal ferrite and at the austenite-ferrite interface. In contrast, during isothermal aging, nucleation of ε-copper precipitation occurs at dislocations. In the three different chemistries investigated, the increase in strength associated with copper during aging results only in a small decrease in impact toughness, implying that copper precipitates do not seriously impair toughness, and can be considered as a viable strengthening element in microalloyed steels. Precipitation of fine-scale niobium carbides occurs extensively at dislocations and within ferrite matrix together with vanadium carbides. In the presence of titanium, titanium carbides act as a nucleus for niobium carbide formation. Irrespective of the nature of carbides, copper precipitates and carbides are mutually exclusive.

  8. Carbonization

    Energy Technology Data Exchange (ETDEWEB)

    Hennebutte, H G; Goutal, E

    1921-07-04

    Materials such as coal, peat, or schist are subjected to a rising temperature in successive stages in apparatus in which the distillation products are withdrawn at each stage. For example in a three-stage process, the acid products of the first or low-temperature stage are fixed in a suitable reagent, the basic products from a second or higher-temperature stage are absorbed in an acid reagent, hydrocarbons being retained by solvents, while the third are subjected to a pyrogenation process carried out in a closed vessel. Wherein the material is subjected in stages to a rising temperature, the gasified products being withdrawn at each stage, and are prevented as far as possible from mixing with the carbonized products.

  9. Thermo-mechanical vibration analysis of a single-walled carbon nanotube embedded in an elastic medium based on higher-order shear deformation beam theory

    International Nuclear Information System (INIS)

    Ebrahimi, Farzad; Salari, Erfan

    2015-01-01

    In this study, the thermal effect on the free vibration characteristics of embedded Single-walled carbon nanotubes (SWCNTs) based on the size-dependent Reddy higher order shear deformation beam theory subjected to in-plane thermal loading is investigated by presenting a Navier-type solution and employing a semi-analytical Differential transform method (DTM) for the first time. In addition, the exact nonlocal Reddy beam theory solution presented here should be useful to engineers designing nanoelectromechanical devices. The small scale effect is considered based on nonlocal elasticity theory of Eringen. The nonlocal equations of motion are derived through Hamilton's principle, and they are solved by applying DTM. Numerical results reveal that the proposed modeling and semi-analytical approach can provide more accurate frequency results of the SWCNTs compared to analytical results and some cases in the literature. The detailed mathematical derivations are presented, and numerical investigations are performed, whereas emphasis is placed on investigating the effect of several parameters such as small-scale effects, boundary conditions, mode number, thickness ratio, temperature change, and Winkler spring modulus on the natural frequencies of the SWCNTs in detail. The vibration behavior of SWCNTs is significantly influenced by these effects. Results indicate that the inclusion of size effect results in a decrease in nanobeam stiffness and leads to a decrease in natural frequency. Numerical results are presented to serve as benchmarks for future analyses of SWCNTs.

  10. Pd-NiO decorated multiwalled carbon nanotubes supported on reduced graphene oxide as an efficient electrocatalyst for ethanol oxidation in alkaline medium

    Science.gov (United States)

    Rajesh, Dhanushkotti; Indra Neel, Pulidindi; Pandurangan, Arumugam; Mahendiran, Chinnathambi

    2018-06-01

    The synthesis of Pd-NiO nanoparticles decorated multiwalled carbon nanotubes (MWCNTs) on reduced graphene oxide (rGO) for ethanol electrooxidation is reported. NiO nanoparticles (NPs) were deposited on functionalized MWCNTs by wet impregnation method. Pd nanoparticles were formed on NiO-MWCNTs by the addition of PdCl2 and its reduction using NaBH4. The Pd-NiO/MWCNTs nanocomposite then deposited on rGO support using ultrasound irradiation which led to the formation of the Pd-NiO/MWCNTs/rGO electrocatalyst. The prepared electrocatalysts were characterized by XRD, SEM, HR-TEM and XPS analysis. Electrochemical measurements demonstrate that as synthesized Pd-NiO/MWCNTs/rGO electrocatalyst exhibit higher catalytic activity (90.89 mA/cm2) than either Pd/MWCNTs/rGO (43.05 mA/cm2) or Pd/C (28.0 mA/cm2) commercial catalyst. Chronoamperometry study of Pd-NiO/MWCNTs/rGO electrocatalyst showed long-term electrochemical stability. The enhanced catalytic activity of Pd-NiO/MWCNTs/rGO electrocatalyst for electrooxidation of ethanol can be attributed to the synergistic effect between Pd & NiO active sites.

  11. Change of sulfide inclusions in steel microalloying with rare earth and alkaline-earth elements

    International Nuclear Information System (INIS)

    Averin, V.V.; Polonskaya, S.M.; Chistyakov, V.F.

    1977-01-01

    The conditions for the formation of sulfides in molten and solid iron were determined by considering the thermodynamics of the interaction of sulfur and of oxygen with various components. It was shown in casting of low-carbon steel under a blanket of slag-forming briquettes, calcium of the silicocalcium partly passes to iron and to the sulfide phase. The sulfide inclusions with calcium in rolling become lens-shaped and acquire a greater strength, proportional to the content of calcium, thus ensuring a lesser anisotropy of steel. The change in the shape and the composition of sulfide inclusions effects the fracture of the metal which changes in type from separation along lamellar inclusions to a plastic fracture, i.e., enhances resilience. It is thus noted that rare-earth and alkali-earth elements, in particular, cerium and calcium are promising agents for desulfurating molten iron

  12. MODELING OF STRAIN-INDUCED PRECIPITATION KINETICS IN Nb MICROALLOYED STEELS

    Institute of Scientific and Technical Information of China (English)

    X.G. Zhou; Z.Y. Liu; D. Wu; Z.Li; C.M. Li

    2006-01-01

    On the basis of the thermodynamic calculation of precipitation and considering the effect of strain on the precipitation behavior and chemical composition (Si and Mn), the kinetics of precipitation from austenite has been investigated for different temperatures and strains. Nucleation theory and the solubility product of niobium, carbon, and nitrogen in austenite have been used to derive equations for the start time of precipitation as a function of temperature and composition. The value of n in Avrami equation was determined using the available experimental data from the published reports, which indicated that n is a constant independent of temperature and the end time of precipitation is a function of n and the start time of precipitation. The values of the start time and end time of precipitation predicted by the new model are compared with the experimental values and a good agreement was obtained between both.

  13. A Low Cost Ferritic Stainless Steel Microalloyed by Higher Nb for Automotive Exhaust System

    Science.gov (United States)

    Chen, Erhu; Wang, Xuelin; Shang, Chengjia

    Automotive engine exhaust gas after combustion of fuel, and the gas will be liquefied in the rear of automotive exhaust system. A lot of corrosive anions existing in the condensate make corrosion of the exhaust system materials. Therefore, once pitting perforation, automotive exhaust system will fail directly. In 1980s, automotive exhaust manifold was made of Si-Mo ductile iron, mufflers and the tail pipe were made of carbon steel or aluminized steel. But with higher emission standards carried out, the improvement of engine performance and the higher exhaust temperature as well as the needs of the automotive light-weighting, we need the higher corrosion resistance of the material for automotive exhaust systems to meet the requirements.

  14. Detection and spatial characterization of carbon steel pitting corrosion in anaerobic sulpho-genic medium; Detection et caracterisation spatiale de la corrosion localisee des aciers au carbone en milieu anaerobie sulfurogene

    Energy Technology Data Exchange (ETDEWEB)

    Festy, D.; Forest, B. [Institut francais de Recherche pour l' Exploitation de la Mer - IFREMER, Centre de Brest, Service Materiaux et Structures, 29 - Plouzane (France); Keddam, M.; Monfort Moros, N.; Tribollet, B. [UPR 15 du CNRS Lab. de Physique des Liquides et Electrochimie, 75 - Paris (France); Marchal, R.; Monfort Moros, N. [Institut Francais du Petrole (IFP), Div. Chimie et Physico-Chimie Appliquee, Dept. Microbiologie, 92 - Rueil-Malmaison (France)

    2002-07-01

    The bio-film developing on carbon steel surfaces in anaerobic condition may induce localised corrosion. To be able to better understand this type of bio-corrosion, this piper presents a new electrochemical technique, which has been developed in collaboration between IFREMER and the Laboratory for liquid physic and electrochemistry. Focussed on local aspect of this phenomenon, the described technique enables surface torrent density mapping to be performed and anodic or cathodic zones to be identified. A double micro-electrode probe is placed closed to the steel simple surface and potential difference between them is measured. This value is directly connected to ohmic drop within electrolyte and consequently, to local torrent. By scanning the substrate surface, local torrent repartition is visualized and one tan detect and characterise Localised corrosion attacks. After presenting the technique and the calibration procedure, a bio-corrosion phenomenon induced by stripping a bio-film at a carbon steel simple surface is analysed by successively drawing localised torrent maps, included biocide efficiency assessment. (authors)

  15. Thermomechanical processing of aluminum micro-alloyed with Sc, Zr, Ti, B, and C

    Science.gov (United States)

    McNamara, Cameron T.

    Critical exploration of the minimalistic high strength low alloy aluminum (HSLA-Al) paradigm is necessary for the continued development of advanced aluminum alloys. In this study, scandium (Sc) and zirconium (Zr) are examined as the main precipitation strengthening additions, while magnesium (Mg) is added to probe the synergistic effects of solution and precipitation hardening, as well as the grain refinement during solidification afforded by a moderate growth restriction factor. Further, pathways of recrystallization are explored in several potential HSLA-Al syste =ms sans Sc. Aluminum-titanium-boron (Al-Ti-B) and aluminum-titanium-carbon (Al-Ti-C) grain refining master alloys are added to a series of Al-Zr alloys to examine both the reported Zr poisoning effect on grain size reduction and the impact on recrystallization resistance through the use of electron backscattered diffraction (EBSD) imaging. Results include an analysis of active strengthening mechanisms and advisement for both constitution and thermomechanical processing of HSLA-Al alloys for wrought or near-net shape cast components. The mechanisms of recrystallization are discussed for alloys which contain a bimodal distribution of particles, some of which act as nucleation sites for grain formation during annealing and others which restrict the growth of the newly formed grains.

  16. Enhanced corrosion resistance of carbon steel in normal sulfuric acid medium by some macrocyclic polyether compounds containing a 1,3,4-thiadiazole moiety: AC impedance and computational studies

    International Nuclear Information System (INIS)

    Bentiss, F.; Lebrini, M.; Vezin, H.; Chai, F.; Traisnel, M.; Lagrene, M.

    2009-01-01

    We report here the use of macrocyclic polyether compounds containing a 1,3,4-thiadiazole moiety (n-MCTH) in the corrosion inhibition of C38 carbon steel in 0.5 M H 2 SO 4 acid medium. The aim of this work is devoted to study the inhibition characteristics of these compounds for acid corrosion of C38 steel using electrochemical impedance spectroscopy (EIS). Data obtained from EIS show a frequency distribution and therefore a modeling element with frequency dispersion behaviour, a constant phase element (CPE) has been used. The experimental results obtained revealed that these compounds inhibited the steel corrosion in acid solution and the protection efficiency increased with increasing inhibitors concentration. The difference in their inhibitive action can be explained on the basis of the number of oxygen atoms present in the polyether ring which contribute to the chemisorption strength through the donor acceptor bond between the non bonding electron pair and the vacant orbital of metal surface. Adsorption of n-MCTH was found to follow the Langmuir's adsorption isotherm. The thermodynamic functions of adsorption process were calculated and the interpretation of the results is given. These results are complemented with quantum chemical study in order to provide an explanation of the differences between the probed inhibitors. Correlation between the inhibition efficiency and the structure of these compounds are presented.

  17. Study of the role of magnetite in the immobilisation of U(VI) by reduction to U(IV) under the presence of H{sub 2}(g) in hydrogen carbonate medium

    Energy Technology Data Exchange (ETDEWEB)

    Rovira, Miquel; Pablo, Joan de [Centre Tecnologic de Manresa (Spain); El Aamrani, Souad [Univ. Politecnica de Catalunya, Barcelona (Spain); Duro, Lara; Grive, Mireia; Bruno, Jordi [Enviros Spain SL (Spain)

    2003-01-01

    This report corresponds to the work carried out during the period March 2001-July 2002. The interaction of Uranium(VI) in hydrogen carbonate medium with commercial magnetite as well as with magnetite formed as a corrosion product on the surface of a steel coupon has been studied. The influence of the hydrogen pressure and the mass of magnetite have been two of the factors studied in detail. Results obtained with commercial magnetite indicates that uranium concentration in solution can be explained taking into account the solubility of UO{sub 2}(am) at the experimental conditions employed (pe+pH{approx}6) and at different hydrogen pressures. The uranium(VI) reduction has been clearly demonstrated by using X-Ray Absorption Near Edge Structure (XANES). Experiments performed during 30 days in hydrogen atmosphere showed a reduction of the 80% of U(VI). Results obtained by using X-Ray Photoelectron Spectroscopy also corroborate the U(VI) reduction on the surface of the magnetite. In the case of magnetite obtained on a steel coupon, it seems that the presence of zero-valent iron below the magnetite surface might account for an increase of the electronic density at the surface and, therefore causing a preferential oxidation of the structural iron in front of the experiment conducted with commercial magnetite. Uranium concentration seems also to be controlled by UO{sub 2}(am) solubility.

  18. Study of the role of magnetite in the immobilisation of U(VI) by reduction to U(IV) under the presence of H2(g) in hydrogen carbonate medium

    International Nuclear Information System (INIS)

    Rovira, Miquel; Pablo, Joan de; El Aamrani, Souad; Duro, Lara; Grive, Mireia; Bruno, Jordi

    2003-01-01

    This report corresponds to the work carried out during the period March 2001-July 2002. The interaction of Uranium(VI) in hydrogen carbonate medium with commercial magnetite as well as with magnetite formed as a corrosion product on the surface of a steel coupon has been studied. The influence of the hydrogen pressure and the mass of magnetite have been two of the factors studied in detail. Results obtained with commercial magnetite indicates that uranium concentration in solution can be explained taking into account the solubility of UO 2 (am) at the experimental conditions employed (pe+pH∼6) and at different hydrogen pressures. The uranium(VI) reduction has been clearly demonstrated by using X-Ray Absorption Near Edge Structure (XANES). Experiments performed during 30 days in hydrogen atmosphere showed a reduction of the 80% of U(VI). Results obtained by using X-Ray Photoelectron Spectroscopy also corroborate the U(VI) reduction on the surface of the magnetite. In the case of magnetite obtained on a steel coupon, it seems that the presence of zero-valent iron below the magnetite surface might account for an increase of the electronic density at the surface and, therefore causing a preferential oxidation of the structural iron in front of the experiment conducted with commercial magnetite. Uranium concentration seems also to be controlled by UO 2 (am) solubility

  19. The effects of microalloying with Cd on precipitation processes in Al-1.7 Cu-0.3 mg (At. %) alloys

    International Nuclear Information System (INIS)

    Sofyan, Bondan T.

    2002-01-01

    The present work investigates the effects of microalloying with Cd on precipitation processes in Al-1.7 Cu-0.3 mg (At. %) alloys. Analytical STEM (Scanning Transmission Electron Microscope) revealed the presence of clusters rich in Cd and Mg at early stages of ageing, which is believed to be responsible in promoting the nucleation of θ (Al,Cu) in the alloy on its (001) planes. The Cd-Mg clusters then grow as Cd-Mg-rich particles when ageing is continued beyond the peak hardness. The presence of Cd-Mg-rich clusters is thought to play an important role on the nucleation of θ phase by accommodating the misfit strain on the non-coherent rim of the phase. The accommodation of misfit strain is made available by the presence of large amount of vacancies, which is trapped by Cd and Mg atoms during quenching, around θ platelet nuclei

  20. Research on the Microstructures and Mechanical Properties of Ti Micro-Alloyed Cold Rolled Hot-Dip Galvanizing DP980 Steel

    Science.gov (United States)

    Han, Yun; Kuang, Shuang; Qi, Xiumei; Xie, Chunqian; Liu, Guanghui

    Effects of galvanizing simulation parameters on microstructures and mechanical properties of Ti-microalloyed cold rolled hot-dip galvanizing DP980 steel were investigated in this study by optical microscopy (OM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS) and tensile test. Moreover, the precipitation behavior of Ti in the experimental steel was also studied. The results show that, as the heating temperature increases, the tensile strength of experimental galvanizing DP980 steel decreases while the yield ratio and elongation of the steel are enhanced. The microstructures of experimental steels exhibit typical dual phase steel character and the volume fractions of MA islands are almost 30%. In addition, lots of nano-sized TiC precipitates can be found in the ferrite grains.

  1. Clustering, microalloying and mechanical properties in Cu/Zr-based glassy models by molecular dynamics simulations and ab-initio computations

    Energy Technology Data Exchange (ETDEWEB)

    Lekka, Ch.E.; Bokas, G.B. [University of Ioannina, Department of Materials Science and Engineering, Ioannina 45100 (Greece); Almyras, G.A. [University of Ioannina, Department of Physics, Ioannina 45110 (Greece); Papageorgiou, D.G. [University of Ioannina, Department of Materials Science and Engineering, Ioannina 45100 (Greece); Evangelakis, G.A., E-mail: gevagel@cc.uoi.gr [University of Ioannina, Department of Physics, Ioannina 45110 (Greece)

    2012-09-25

    Highlights: Black-Right-Pointing-Pointer Cu-Zr MGs consist of interpenetrating ICO-like clusters (superclusters (SCs)). Black-Right-Pointing-Pointer The SCs participate in the accommodation of the tensile deformation. Black-Right-Pointing-Pointer The SCs may exhibit a free of bonds (FoB) plane. Black-Right-Pointing-Pointer Al microalloying changes the SCs' electronic structure inducing FoB planes. Black-Right-Pointing-Pointer Control of SCs' electronic structure may lead to control of MGs' properties. - Abstract: We present results on the microstructure of Cu-Zr metallic glasses (MGs) at equilibrium and under tensile deformation by means of large scale molecular dynamics (MD) simulations and density functional theory (DFT) calculations. We found that the MGs are composed by interpenetrating icosahedral-like (ICO) clusters forming superclusters (SCs). The deformation accommodation is associated with the destruction and recreation of these ICO clusters and SCs. DFT calculations on the Cu{sub 13}Zr{sub 10} SCs with Cu-Cu core atoms revealed the presence of a free of bonds (FoB) plane that could be viewed as analog of a slip plane of the crystalline materials. The microalloying (MA) effect in a similar SC (one of the core atoms substituted by Al) yielded that Al is associated with the formation of a FoB plane. These results provide possible explanations of the experimental findings referring to the short range order, the MA effect and could potentially be used for the design of new MGs.

  2. Phase Equilibrium and Austenite Decomposition in Advanced High-Strength Medium-Mn Bainitic Steels

    Directory of Open Access Journals (Sweden)

    Adam Grajcar

    2016-10-01

    Full Text Available The work addresses the phase equilibrium analysis and austenite decomposition of two Nb-microalloyed medium-Mn steels containing 3% and 5% Mn. The pseudobinary Fe-C diagrams of the steels were calculated using Thermo-Calc. Thermodynamic calculations of the volume fraction evolution of microstructural constituents vs. temperature were carried out. The study comprised the determination of the time-temperature-transformation (TTT diagrams and continuous cooling transformation (CCT diagrams of the investigated steels. The diagrams were used to determine continuous and isothermal cooling paths suitable for production of bainite-based steels. It was found that the various Mn content strongly influences the hardenability of the steels and hence the austenite decomposition during cooling. The knowledge of CCT diagrams and the analysis of experimental dilatometric curves enabled to produce bainite-austenite mixtures in the thermomechanical simulator. Light microscopy (LM, scanning electron microscopy (SEM, and transmission electron microscopy (TEM were used to assess the effect of heat treatment on morphological details of produced multiphase microstructures.

  3. Concept medium programme

    DEFF Research Database (Denmark)

    Bjerrum, Peter

    2005-01-01

    The present essay is an attempt to determine the architectural project of the 21st century in relation to a modern conception of space as the medium of architecture, and of sociality as its program......The present essay is an attempt to determine the architectural project of the 21st century in relation to a modern conception of space as the medium of architecture, and of sociality as its program...

  4. Medium energy ion scattering (MEIS)

    International Nuclear Information System (INIS)

    Dittmann, K.; Markwitz, A.

    2009-01-01

    This report gives an overview about the technique and experimental study of medium energy ion scattering (MEIS) as a quantitative technique to determine and analyse the composition and geometrical structure of crystalline surfaces and near surface-layers by measuring the energy and yield of the backscattered ions. The use of a lower energy range of 50 to 500 keV accelerated ions impinging onto the target surface and the application of a high-resolution electrostatic energy analyser (ESA) makes medium energy ion scattering spectroscopy into a high depth resolution and surface-sensitive version of RBS with less resulting damage effects. This report details the first steps of research in that field of measurement technology using medium energetic backscattered ions detected by means of a semiconductor radiation detector instead of an ESA. The study of medium energy ion scattering (MEIS) has been performed using the 40 keV industrial ion implanter established at GNS Sciences remodelled with supplementary high voltage insulation for the ion source in order to apply voltages up to 45 kV, extra apertures installed in the beamline and sample chamber in order to set the beam diameter accurately, and a semiconductor radiation detector. For measurement purposes a beam of positive charged helium ions accelerated to an energy of about 80 keV has been used impinging onto target surfaces of lead implanted into silicon (PbSi), scandium implanted into aluminium (ScAl), aluminium foil (Al) and glassy carbon (C). First results show that it is possible to use the upgraded industrial implanter for medium energy ion scattering. The beam of 4 He 2+ with an energy up to 88 keV has been focussed to 1 mm in diameter. The 5 nA ion beam hit the samples under 2 x 10 -8 mbar. The results using the surface barrier detector show scattering events from the samples. Cooling of the detector to liquid nitrogen temperatures reduced the electronic noise in the backscattering spectrum close to zero. A

  5. Effect of coarse {gamma} grain size on the dynamic and static recrystallisation during hot working in microalloyed Nb and Nb-Ti steels

    Energy Technology Data Exchange (ETDEWEB)

    Fernandez, A.I.; Abad, R.; Lopez, B.; Rodriguez-Ibabe, J.M. [Centro de Estudios e Investigaciones Tecnicas de Guipuzcoa (CEIT), San Sebastian (Spain)

    1998-10-01

    The effect of coarse austenite grain size on the dynamic and static recrystallisation kinetics of two microalloyed Nb and Nb-Ti steels has been investigated in the present work. To characterize the dynamic recrystallisation behaviour of the austenite, continuous-torsion tests were carried out after the reheating of the specimen at different temperatures in the range 1000-1420 C. It has been observed that the occurrence of dynamic recrystallisation is dependent on the initial grain size and the deformation conditions (temperature and strain-rate). Decreasing values of the Zener-Hollomon parameter (Z) and grain size promotes dynamic recrystallisation. However for the coarser grain sizes no peaks appear on the flow curves above a determined value of Z. This value seems to decrease with increasing the grain size. An equation to predict the {epsilon}{sub p} peak strain for a wide range of grain sizes has been obtained for both steels. The effect of strain on the static recrystallisation of the austenite, having a large grain size, has been also studied. Interrupted-torsion tests were performed to determined the fractional softening. A quadratic dependence of t{sub 0.5} on strain has been observed, denoting a less dependence of recrystallisation on strain than proposed previously by other authors in the range of lower grain sizes. (orig.) 22 refs.

  6. Effect of Plastic Hot Deformation on the Hardness and Continuous Cooling Transformations of 22MnB5 Microalloyed Boron Steel

    Science.gov (United States)

    Barcellona, A.; Palmeri, D.

    2009-05-01

    The strains, transformation temperatures, microstructure, and microhardness of a microalloyed boron and aluminum precoated steel, which has been isothermally deformed under uniaxial tensile tests, have been investigated at temperatures between 873 and 1223 K, using a fixed strain rate value of 0.08 s-1. The effect of each factor, such as temperature and strain value, has been later valued considering the shift generated on the continuous cooling transformation (CCT) diagram. The experimental results consist of the starting temperatures that occur for each transformation, the microhardness values, and the obtained microstructure at the end of each thermomechanical treatment. All the thermomechanical treatments were performed using the thermomechanical simulator Gleeble 1500. The results showed that increasing hot prestrain (HPS) values generate, at the same cooling rate, lower hardness values; this means that the increasing of HPS generates a shift of the CCT diagram toward a lower starting time for each transformation. Therefore, high values of hot deformations during the hot stamping process require a strict control of the cooling process in order to ensure cooling rate values that allow maintaining good mechanical component characteristics. This phenomenon is amplified when the prestrain occurs at lower temperatures, and thus, it is very sensitive to the temperature level.

  7. The effect of cooling rate and austenite grain size on the austenite to ferrite transformation temperature and different ferrite morphologies in microalloyed steels

    International Nuclear Information System (INIS)

    Esmailian, M.

    2010-01-01

    The effect of different austenite grain size and different cooling rates on the austenite to ferrite transformation temperature and different ferrite morphologies in one Nb-microalloyed high strength low alloy steel has been investigated. Three different austenite grain sizes were selected and cooled at two different cooling rates for obtaining austenite to ferrite transformation temperature. Moreover, samples with specific austenite grain size have been quenched, partially, for investigation on the microstructural evolution. In order to assess the influence of austenite grain size on the ferrite transformation temperature, a temperature differences method is established and found to be a good way for detection of austenite to ferrite, pearlite and sometimes other ferrite morphologies transformation temperatures. The results obtained in this way show that increasing of austenite grain size and cooling rate has a significant influence on decreasing of the ferrite transformation temperature. Micrographs of different ferrite morphologies show that at high temperatures, where diffusion rates are higher, grain boundary ferrite nucleates. As the temperature is lowered and the driving force for ferrite formation increases, intragranular sites inside the austenite grains become operative as nucleation sites and suppress the grain boundary ferrite growth. The results indicate that increasing the austenite grain size increases the rate and volume fraction of intragranular ferrite in two different cooling rates. Moreover, by increasing of cooling rate, the austenite to ferrite transformation temperature decreases and volume fraction of intragranular ferrite increases.

  8. Role of Chloride in the Corrosion and Fracture Behavior of Micro-Alloyed Steel in E80 Simulated Fuel Grade Ethanol Environment

    Directory of Open Access Journals (Sweden)

    Olufunmilayo O. Joseph

    2016-06-01

    Full Text Available In this study, micro-alloyed steel (MAS material normally used in the production of auto parts has been immersed in an E80 simulated fuel grade ethanol (SFGE environment and its degradation mechanism in the presence of sodium chloride (NaCl was evaluated. Corrosion behavior was determined through mass loss tests and electrochemical measurements with respect to a reference test in the absence of NaCl. Fracture behavior was determined via J-integral tests with three-point bend specimens at an ambient temperature of 27 °C. The mass loss of MAS increased in E80 with NaCl up to a concentration of 32 mg/L; beyond that threshold, the effect of increasing chloride was insignificant. MAS did not demonstrate distinct passivation behavior, as well as pitting potential with anodic polarization, in the range of the ethanol-chloride ratio. Chloride caused pitting in MAS. The fracture resistance of MAS reduced in E80 with increasing chloride. Crack tip blunting decreased with increasing chloride, thus accounting for the reduction in fracture toughness.

  9. A comparative study of the microstructure and properties of 800 MPa microalloyed C-Mn steel welded joints by laser and gas metal arc welding

    Energy Technology Data Exchange (ETDEWEB)

    Sun, Qian [The State Key Laboratory of Rolling and Automation of Northeastern University, Shenyang 110819 (China); Di, Hong-Shuang, E-mail: hongshuangdi_ral@126.com [The State Key Laboratory of Rolling and Automation of Northeastern University, Shenyang 110819 (China); Li, Jun-Chen [The State Key Laboratory of Rolling and Automation of Northeastern University, Shenyang 110819 (China); Wu, Bao-Qiang [National Key Laboratory for Precision Hot Processing of Metals, Harbin Institute of Technology, Harbin 150001 (China); Misra, R.D.K. [Laboratory for Excellence in Advanced Steel Research, Department of Metallurgical, Material and Biomedical Engineering, University of Texas at El Paso, TX 79968 (United States)

    2016-07-04

    The differences in microstructure and mechanical properties of laser beam welded (LBW) and gas metal arc welded (GMAW) joints of 800 MPa grade Nb-Ti-Mo microalloyed C-Mn steel of 5 mm thickness were studied. The study suggested that the microstructure in welded seam (WS) of GMAW was acicular ferrite and fine grained ferrite, whereas lath martensite (LM) was obtained in WS of LBW, where inclusions were finer and did not act as nucleation sites for acicular ferrite. The microstructure of coarse-grained HAZ (CGHAZ) obtained using the two welding methods was LM and granular bainite (GB), respectively. The original austenite grain size in CGHAZ of LBW was 1/3 of GMAW. The microstructure of fine-grained HAZ and mixed-grained HAZ using the two welding methods was ferrite and M-A constituents, while that of LBW was significantly fine. The hardness of LBW welded joints was higher than the base metal (BM), which was the initiation site for tensile fracture. The tensile fracture location of GMAW welded joints was in WS. The impact toughness of LBW welded joints was excellent and the impact absorption energy was similar to BM.

  10. Characteristics of heat affected zone in SAW and SMAW welding of microalloyed steel 450 EMZ studied by means of a welding simulator

    International Nuclear Information System (INIS)

    Gonzalez Palma, R.; Carrillo Olivares, F.; Lopez Torres, E.

    1997-01-01

    In high elastic limit microalloyed steels the heat input remains limited to values around 3 kj/mm, since, from a theoretical point of view the metallurgic transformations produced in the heat affected zone (HAZ) may fragile the metal. The study of the transmission of heat in the HAZ from a theoretical point of view is carried out by solving Rosenthal's equation, which allows us to know the peak temperature reached and the heat cycle in every point of the HAZ. With these data and the CCT curves for 450 EMZ steel corresponding to our steel we will be able to determine the metallurgic transformations produced in those points, with the help of an electron microscope. The welding simulator is valuable help for laboratory study of heat cycles as it allows us to check that for the actual welding processes chosen, i.e. SMAW and SAW, and for the heat input, the transformation products obtained in the HAZ have the right toughness. (Author) 17 refs

  11. Carbon dioxide as chemical feedstock

    National Research Council Canada - National Science Library

    Aresta, M

    2010-01-01

    ... Dioxide as an Inert Solvent for Chemical Syntheses 15 Alessandro Galia and Giuseppe Filardo Introduction 15 Dense Carbon Dioxide as Solvent Medium for Chemical Processes 15 Enzymatic Catalysis in Dense Carbon Dioxide 18 Other Reactions in Dense Carbon Dioxide 19 Polymer Synthesis in Supercritical Carbon Dioxide 20 Chain Polymerizations: Synt...

  12. The Interstellar Medium

    CERN Document Server

    Lequeux, James

    2005-01-01

    Describing interstellar matter in our galaxy in all of its various forms, this book also considers the physical and chemical processes that are occurring within this matter. The first seven chapters present the various components making up the interstellar matter and detail the ways that we are able to study them. The following seven chapters are devoted to the physical, chemical and dynamical processes that control the behaviour of interstellar matter. These include the instabilities and cloud collapse processes that lead to the formation of stars. The last chapter summarizes the transformations that can occur between the different phases of the interstellar medium. Emphasizing methods over results, "The Interstellar Medium" is written for graduate students, for young astronomers, and also for any researchers who have developed an interest in the interstellar medium.

  13. Optical recording medium

    International Nuclear Information System (INIS)

    Andriech, A.; Bivol, V.; Tridukh, G.; Tsiuleanu, D.

    2002-01-01

    The invention relates of the micro- and optoelectronics, computer engineering ,in particular, to tjhe optical information media and may be used in hilography. Summary of the invention consists in that the optical image recording medium, containing a dielectric substrates, onto one surface of which there are placed in series a transparent electricity conducting layer, a photo sensitive recording layer of chalcogenic glass and a thin film electrode of aluminium, is provided with an optically transparent protective layer, applied into the thin film electrode. The result of the invention consists in excluding the dependence of chemical processes course into the medium upon environmental conditions

  14. (ajst) effect of heat treatment on wear resistance

    African Journals Online (AJOL)

    Some of the specimens were quenched in water and palm oil, while some of the quenched specimens were ... by the internal friction (hence energy dissipation) caused by these flakes. ... optical emission spectroscope (OES). The result .... medium carbon microalloy forging steel”. J. Mater Sci. ... Prentice Hall of India.

  15. Roentgen contrast medium

    International Nuclear Information System (INIS)

    Tamborski, C.

    1989-01-01

    The patent deals with a roentgen contrast medium containing a perfluorinebrominealkylether of the formula C m F 2m+1 OC n F 2n Br dispersed in water, preferentially in the presence of a non-ionic dispersing agent such as a fluorinated amidoaminoxide. 2 tabs

  16. Radon in geological medium

    Energy Technology Data Exchange (ETDEWEB)

    Hricko, J [GEOCOMPLEX, a.s., Bratislava (Slovakia)

    1996-12-31

    The paper presented deals with behavior of the radon in geological medium and with some results of the radon survey in Bratislava and Kosice regions. 1) The a{sub v} has been detected in the holes 0.80 m deep. The density of observations - 3 reference areas (one represents 20 stations) per 1 km{sup 2}. The radon risk maps in 1:25000 and 1:50000 scales have been compiled. The 56.8% of the project area lies in low radon risk, 37.6% in medium radon risk and 5.6% in high radon risk. Follow-up monitoring of the equivalent volume radon activity (EVRA) at the flats, located in the areas with high radon risk of the surface layer, has showed values several times higher than Slovak limits (Marianka, Raca, Vajnory). The evidence that neotectonic is excellent medium for rising up emanation to the subsurface layer, is shown on the map. The tectonic zone of Liscie udolie in Bratislava-Karlova Ves area has been clearly detected by profile radon survey (a{sub v} > 50 kBq/m{sup 3}). 2) At present, northern half of the area of Kosice in question was covered by radon survey. The low and medium radon risks have been observed here, while localities with high radon risk are small in extent. The part of radon risk and soil permeability map from northern Kosice area is shown. (J.K.) 3 figs., 2 refs.

  17. Radon in geological medium

    International Nuclear Information System (INIS)

    Hricko, J.

    1995-01-01

    The paper presented deals with behavior of the radon in geological medium and with some results of the radon survey in Bratislava and Kosice regions. 1) The a v has been detected in the holes 0.80 m deep. The density of observations - 3 reference areas (one represents 20 stations) per 1 km 2 . The radon risk maps in 1:25000 and 1:50000 scales have been compiled. The 56.8% of the project area lies in low radon risk, 37.6% in medium radon risk and 5.6% in high radon risk. Follow-up monitoring of the equivalent volume radon activity (EVRA) at the flats, located in the areas with high radon risk of the surface layer, has showed values several times higher than Slovak limits (Marianka, Raca, Vajnory). The evidence that neotectonic is excellent medium for rising up emanation to the subsurface layer, is shown on the map. The tectonic zone of Liscie udolie in Bratislava-Karlova Ves area has been clearly detected by profile radon survey (a v > 50 kBq/m 3 ). 2) At present, northern half of the area of Kosice in question was covered by radon survey. The low and medium radon risks have been observed here, while localities with high radon risk are small in extent. The part of radon risk and soil permeability map from northern Kosice area is shown. (J.K.) 3 figs., 2 refs

  18. Effect of medium pH on chemical selectivity of oxalic acid biosynthesis by Aspergillus niger W78C in submerged batch cultures with sucrose as a carbon source.

    Science.gov (United States)

    Walaszczyk, Ewa; Podgórski, Waldemar; Janczar-Smuga, Małgorzata; Dymarska, Ewelina

    2018-01-01

    The pH of the medium is the key environmental parameter of chemical selectivity of oxalic acid biosynthesis by Aspergillus niger . The activity of the enzyme oxaloacetate hydrolase, which is responsible for decomposition of oxaloacetate to oxalate and acetate inside the cell of the fungus, is highest at pH 6. In the present study, the influence of pH in the range of 3-7 on oxalic acid secretion by A. niger W78C from sucrose was investigated. The highest oxalic acid concentration, 64.3 g dm -3 , was reached in the medium with pH 6. The chemical selectivity of the process was 58.6% because of the presence of citric and gluconic acids in the cultivation broth in the amount of 15.3 and 30.2 g dm -3 , respectively. Both an increase and a decrease of medium pH caused a decrease of oxalic acid concentration. The obtained results confirm that pH 6 of the carbohydrate medium is appropriate for oxalic acid synthesis by A. niger , but the chemical selectivity of the process described in this paper was high in comparison to values reported previously in the literature.

  19. Application of carbon extraction replicas in grain-size measurements of high-strength steels using TEM

    International Nuclear Information System (INIS)

    Poorhaydari, Kioumars; Ivey, Douglas G.

    2007-01-01

    In this paper, the application of carbon extraction replicas in grain-size measurements is introduced and discussed. Modern high-strength microalloyed steels, used as structural or pipeline materials, have very small grains with substructures. Replicas used in transmission electron microscopes can resolve the grain boundaries and can be used for systematic measurement of grain size in cases where the small size of the grains pushes the resolution of conventional optical microscopes. The grain-size variations obtained from replicas are compared with those obtained from optical and scanning electron microscopy. An emphasis is placed on the importance of using the correct technique for imaging and the optimal magnification. Grain-size measurements are used for estimation of grain-boundary strengthening contribution to yield strength. The variation in grain size is also correlated with hardness in the base metal of several microalloyed steels, as well as the fine-grained heat-affected zone of a weld structure with several heat inputs

  20. Effects of Microalloying on the Microstructures and Mechanical Properties of Directionally Solidified Ni-33(at.%)Al-31Cr-3Mo Eutectic Alloys Investigated

    Science.gov (United States)

    Whittenberger, J. Daniel; Raj, Sai V.; Locci, Ivan E.; Salem, Jonathan A.

    2002-01-01

    Despite nickel aluminide (NiAl) alloys' attractive combination of oxidation and thermophysical properties, their development as replacements for superalloy airfoils in gas turbine engines has been largely limited by difficulties in developing alloys with an optimum combination of elevated-temperature creep resistance and room-temperature fracture toughness. Alternatively, research has focused on developing directionally solidified NiAl-based in situ eutectic composites composed of NiAl and (Cr,Mo) phases in order to obtain a desirable combination of properties a systematic investigation was undertaken at the NASA Glenn Research Center to examine the effects of small additions of 11 alloying elements (Co, Cu, Fe, Hf, Mn, Nb, Re, Si, Ta, Ti, and Zr) in amounts varying from 0.25 to 1.0 at.% on the elevated-temperature strength and room-temperature fracture toughness of directionally solidified Ni-33Al-31Cr-3Mo eutectic alloy. The alloys were grown at 12.7 mm/hr, where the unalloyed eutectic base alloy exhibited a planar eutectic microstructure. The different microstructures that formed because of these fifth-element additions are included in the table. The additions of these elements even in small amounts resulted in the formation of cellular microstructures, and in some cases, dendrites and third phases were observed. Most of these elemental additions did not improve either the elevated-temperature strength or the room-temperature fracture toughness over that of the base alloy. However, small improvements in the compression strength were observed between 1200 and 1400 K when 0.5 at.% Hf and 0.25 at.% Ti were added to the base alloy. The results of this study suggest that the microalloying of Ni-33Al-31Cr-3Mo will not significantly improve either its elevatedtemperature strength or its room-temperature fracture toughness. Thus, any improvements in these properties must be acquired by changing the processing conditions.

  1. Concept medium program

    DEFF Research Database (Denmark)

    Bjerrum, Peter

    2003-01-01

    The present essays is an attempt to dertermine the architecural project of the 21st century in realation to a modern conception of space as the medium of architecture, and of society as its program. This attempt adopts the internal point of view of an architect in describing a modern architectural...... project within the framework: concept - program, these notions being concieved as spatial representations primarily and immediately "given" to architecture....

  2. DENSE MEDIUM CYCLONE OPTIMIZATON

    Energy Technology Data Exchange (ETDEWEB)

    Gerald H. Luttrell; Chris J. Barbee; Peter J. Bethell; Chris J. Wood

    2005-06-30

    Dense medium cyclones (DMCs) are known to be efficient, high-tonnage devices suitable for upgrading particles in the 50 to 0.5 mm size range. This versatile separator, which uses centrifugal forces to enhance the separation of fine particles that cannot be upgraded in static dense medium separators, can be found in most modern coal plants and in a variety of mineral plants treating iron ore, dolomite, diamonds, potash and lead-zinc ores. Due to the high tonnage, a small increase in DMC efficiency can have a large impact on plant profitability. Unfortunately, the knowledge base required to properly design and operate DMCs has been seriously eroded during the past several decades. In an attempt to correct this problem, a set of engineering tools have been developed to allow producers to improve the efficiency of their DMC circuits. These tools include (1) low-cost density tracers that can be used by plant operators to rapidly assess DMC performance, (2) mathematical process models that can be used to predict the influence of changes in operating and design variables on DMC performance, and (3) an expert advisor system that provides plant operators with a user-friendly interface for evaluating, optimizing and trouble-shooting DMC circuits. The field data required to develop these tools was collected by conducting detailed sampling and evaluation programs at several industrial plant sites. These data were used to demonstrate the technical, economic and environmental benefits that can be realized through the application of these engineering tools.

  3. Determination of Structures and Energetics of Small- and Medium-Sized One-Carbon-Bridged Twisted Amides using ab Initio Molecular Orbital Methods: Implications for Amidic Resonance along the C-N Rotational Pathway.

    Science.gov (United States)

    Szostak, Roman; Aubé, Jeffrey; Szostak, Michal

    2015-08-21

    Twisted amides containing nitrogen at the bridgehead position are attractive practical prototypes for the investigation of the electronic and structural properties of nonplanar amide linkages. Changes that occur during rotation around the N-C(O) axis in one-carbon-bridged twisted amides have been studied using ab initio molecular orbital methods. Calculations at the MP2/6-311++G(d,p) level performed on a set of one-carbon-bridged lactams, including 20 distinct scaffolds ranging from [2.2.1] to [6.3.1] ring systems, with the C═O bond on the shortest bridge indicate significant variations in structures, resonance energies, proton affinities, core ionization energies, frontier molecular orbitals, atomic charges, and infrared frequencies that reflect structural changes corresponding to the extent of resonance stabilization during rotation along the N-C(O) axis. The results are discussed in the context of resonance theory and activation of amides toward N-protonation (N-activation) by distortion. This study demonstrates that one-carbon-bridged lactams-a class of readily available, hydrolytically robust twisted amides-are ideally suited to span the whole spectrum of the amide bond distortion energy surface. Notably, this study provides a blueprint for the rational design and application of nonplanar amides in organic synthesis. The presented findings strongly support the classical amide bond resonance model in predicting the properties of nonplanar amides.

  4. Synergetic effects of Sc and Zr microalloying and heat treatment on mechanical properties and exfoliation corrosion behavior of Al-Mg-Mn alloys

    International Nuclear Information System (INIS)

    Peng, Yongyi; Li, Shu; Deng, Ying; Zhou, Hua; Xu, Guofu; Yin, Zhimin

    2016-01-01

    Mechanical properties, exfoliation corrosion behavior and microstructure of Al-5.98Mg-0.47Mn and Al-6.01Mg-0.45Mn-0.25Sc-0.10Zr (wt%) alloy sheets under various homogenizing and annealing processes were investigated comparatively by tensile tests, electrochemical measurements, X-ray diffraction technique and microscopy methods. The as-cast alloys mainly consist of Fe and Mn enriched impurity phases, Mg and Mn enriched non-equilibrium aluminides and Mg 3 Al 2 phases. During homogenization treatment, solvable intermetallics firstly precipitate and then dissolve into matrix. The optimized homogenization processes for removing micro-segregation and obtaining maximum precipitation strengthening of secondary Al 3 (Sc, Zr) particles are 440 °C×8 h and 300 °C×8 h, respectively. Sc and Zr additions can make the yield strength of Al-Mg-Mn alloy increase by 21 MPa (6.9%), 120 MPa (61.2%) and 127 MPa (68.3%), when annealed at 270 °C, 300 °C and 330 °C, respectively, indicating that Orowan precipitation strengthening caused by secondary Al 3 (Sc, Zr) nano-particles is much greater than grain boundary strengthening from primary Al 3 (Sc, Zr) micro-particles. Increasing homogenization and annealing degrees and adding Sc and Zr all can decrease corrosion current density and improve exfoliation corrosion resistance. The exfoliation corrosion behavior is dominant by anodic dissolution occurring at the interface between intermetallics and α(Al) matrix. After homogenizing at 440 °C for 8 h and annealing at 300 °C for 1 h, yield strength, ultimate strength, elongation to failure and exfoliation corrosion rank are 196 MPa, 360 MPa, 20.2% and PA (slight pitting corrosion) in Al-Mg-Mn alloy, and reach to 316 MPa, 440 MPa, 17.0% and PA in Al-Mg-Mn-Sc-Zr alloy, respectively, revealing that high strength, high ductility and admirable corrosion resistance of Al-Mg-Mn alloys can be achieved by the synergetic effects of Sc and Zr microalloying and heat treatment.

  5. Computation as Medium

    DEFF Research Database (Denmark)

    Jochum, Elizabeth Ann; Putnam, Lance

    2017-01-01

    Artists increasingly utilize computational tools to generate art works. Computational approaches to art making open up new ways of thinking about agency in interactive art because they invite participation and allow for unpredictable outcomes. Computational art is closely linked...... to the participatory turn in visual art, wherein spectators physically participate in visual art works. Unlike purely physical methods of interaction, computer assisted interactivity affords artists and spectators more nuanced control of artistic outcomes. Interactive art brings together human bodies, computer code......, and nonliving objects to create emergent art works. Computation is more than just a tool for artists, it is a medium for investigating new aesthetic possibilities for choreography and composition. We illustrate this potential through two artistic projects: an improvisational dance performance between a human...

  6. Spiegel. Medium. Kunst

    DEFF Research Database (Denmark)

    Kacunko, Slavko

    of this kind as the marks of a meta-complex of method out of which new models of the image continually arise. The waxing intangibility of proliferating images be they of the mind, in dreams, through gestures, and the equally rampant growth of microstructuring in allocations of knowledge lay a challenge before...... to research. As a void in the apprehension of the world, the mirror obtained a scholarly perspective and the more so in areas beyond its own qualities as a medium, i.e. in images and metaphor, the paradigms of all research looking to image and text. This investigation sets out to comprehend paradoxes......, and space (albeit no expanse) is there to consider the methodological pros and cons of such a selective approach. Even in this synopsis, it has to be and can be stated that what makes for the affinities between psychological, literary and image-research approaches in research on the mirror is the shared...

  7. The diffuse interstellar medium

    Science.gov (United States)

    Cox, Donald P.

    1990-01-01

    The last 20 years of the efforts to understand the diffuse ISM are reviewed, with recent changes of fundamental aspects being highlighted. Attention is given to the interstellar pressure and its components, the weight of the ISM, the midplane pressure contributions, and pressure contributions at 1 kpc. What velocity dispersions, cosmic ray pressure, and magnetic field pressure that can be expected for a gas in a high magnetic field environment is addressed. The intercloud medium is described, with reference to the work of Cox and Slavin (1989). Various caveats are discussed and a number of areas for future investigation are identified. Steps that could be taken toward a successful phase segregation model are discussed.

  8. Cellular and physiological effects of medium-chain triglycerides.

    NARCIS (Netherlands)

    Wanten, G.J.A.; Naber, A.H.J.

    2004-01-01

    From a nutritional standpoint, saturated triglycerides with a medium (6 to 12) carbon chain length (MCT) have traditionally been regarded as biologically inert substances, merely serving as a source of fuel calories that is relatively easily accessible for metabolic breakdown compared with long

  9. Probing the nuclear medium with the K+ meson

    International Nuclear Information System (INIS)

    Chrien, R.E.

    1995-01-01

    Elastic differential cross sections for K + mesons scattered from targets of carbon and 6 Li have been measured at an incident momentum of 715 MeV/c. The ratios of scattering cross sections from these targets are not predicted by theory, and are consistent with earlier suggestions that the K + -nucleon interaction is modified in the nuclear medium

  10. Characterization of oil based nanofluid for quench medium

    Science.gov (United States)

    Mahiswara, E. P.; Harjanto, S.; Putra, W. N.; Ramahdita, G.; Yahya, S. S.; Kresnodrianto

    2018-01-01

    The choice of quench medium depends on the hardenability of the metal alloy, the thickness of the component, and the geometry of the component. Some of these will determine the cooling rate required to obtain the desired microstructure and material properties. Improper quench media will cause the material to become brittle, suffers from geometric distortion, or having a high undesirable residual stresses in the components. In heat treatment industries, oil and water are frequently used as the quench media. Recently, nanofluid as a quench medium has also been studied using several different fluids as the solvent. Examples of frequently used solvents include polymers, vegetable oils, and mineral oil. In this research, laboratory-grade carbon powder were used as nanoparticle. Oil was used as the fluid base in this research as the main observation focus. To obtain nanoscale carbon particles, planetary ball mill was used to ground laboratory grade carbon powder to decrease the particle size. This method was used to lower the cost for nanoparticle synthesis. Milling speed and duration were set at 500 rpm and 15 hours. Field Emission Scanning Electron Microscope (FE-SEM), and Energy Dispersive X-Ray (EDX) measurement were carried out to determine the particle size, material identification, particle morphology, and surface change of samples. The carbon nanoparticle content in nanofluid quench mediums for this research were varied at 0.1%, 0.2%, 0.3%, 0.4, and 0.5 % volume. Furthermore, these mediums were used to quench JIS S45C or AISI 1045 carbon steel samples which annealed at 1000°C. Hardness testing and metallography observation were then conducted to further examine the effect of different quench medium in steel samples.

  11. Mesons in the nuclear Medium

    CERN Document Server

    Kotulla, M

    2006-01-01

    We discuss recent experimental results on the modification of hadron properties in a nuclear medium. Particular emphasis is placed on an $\\omega$ production experiment performed by the CBELSA/TAPS collaboration at the ELSA accelerator. The data shows a smaller $\\omega$ meson mass together with a significant increase of its width in the nuclear medium.

  12. Process for carbonizing coal, shale, wood, etc

    Energy Technology Data Exchange (ETDEWEB)

    Matthaei, K

    1924-05-08

    A process for carbonization of coal, shale, and wood, for recovering low temperature tar and other products in a rotary retort is described. The material to be carbonized is brought directly in contact with the heating medium, that is characterized in that the heating medium streams through the retort crosswise to the longitudinal axis. The temperature of this medium in the single retort segments can be regulated.

  13. Pions in the nuclear medium

    International Nuclear Information System (INIS)

    Chanfray, G.

    1996-07-01

    We discuss various aspects of pion physics in the nuclear medium. We first study s-wave pion-nucleus interaction in connection with chiral symmetry restoration and quark condensate in the nuclear medium. We then address the question of p-wave pion-nucleus interaction and collective pionic modes in nuclei and draw the consequences for in medium ππ correlations especially in the scalar-isoscalar channel. We finally discuss the modification of the rho meson mass spectrum at finite density and/or temperature in connection with relativistic heavy ion collisions

  14. Enhanced Bio-Ethanol Production from Industrial Potato Waste by Statistical Medium Optimization

    OpenAIRE

    Izmirlioglu, Gulten; Demirci, Ali

    2015-01-01

    Industrial wastes are of great interest as a substrate in production of value-added products to reduce cost, while managing the waste economically and environmentally. Bio-ethanol production from industrial wastes has gained attention because of its abundance, availability, and rich carbon and nitrogen content. In this study, industrial potato waste was used as a carbon source and a medium was optimized for ethanol production by using statistical designs. The effect of various medium componen...

  15. Efeitos de meio de cultura, fontes de carbono e nitrogênio, pH e regime luminoso no crescimento de Mycosphaerella musicola Effects of medium, carbon and nitrogen source, pH and light on the growth of Mycosphaerella musicola

    Directory of Open Access Journals (Sweden)

    Angélica Virgínia Valois Montarroyos

    2007-03-01

    Full Text Available Este trabalho objetivou o estabelecimento de condições favoráveis ao crescimento micelial de M. musicola in vitro, pela avaliação em quatro experimentos, da influência de diferentes meios de cultura (BDA, BDA/IFB, V8, V8/IFB, V8/CaCO3 e V8/CaCO3/IFB; combinações de fontes de carbono (dextrose, maltose, sacarose e xilose e nitrogênio (peptona, glicina, nitrato de potássio e de sódio; valores de pH (6,8; 6,4; 5,7 e 4,9 e regimes luminosos (escuro contínuo, alternância luminosa e claro contínuo. Observou-se um maior crescimento de M. musicola quando cultivado nos meios de cultura BDA/IFB, V8/IFB e BDA. As fontes de carbono sacarose, maltose e dextrose quando combinadas com a peptona como fonte de nitrogênio, promoveram um maior crescimento micelial de M. musicola. O meio de cultura BDA/IFB, com o valor final de pH ajustado para 5,7, em regime de escuro contínuo, apresentou-se como o melhor para o crescimento de M. musicola.This work aimed the establishment of the best growth conditions of M. musicola mycelia in vitro through the analysis of the influence of different culture media (BDA, BDA/IFB, V8, V8/IFB, V8/CaCO3 and V8/CaCO3/IFB, combinations of carbon (dextrose, maltose, sucrose and xylose and nitrogen (peptone, glycine, potassium nitrate and sodium nitrate sources, medium pH values (6.8, 6.4, 5.7 and 4.9 and photoperiods (continuous darkness, alternating darkness/lightness and continuous lightness. At the end of the evaluation period, cultural parameters and the dry weights of colonies were annotated. BDA/IFB, V8/IFB and BDA culture media promoted the best mycelial growth. The experiments also demonstrated that dextrose and sucrose when combined with peptose as a nitrogen source, are the best carbon sources as they promoted the most vigorous mycelial growth. The use of BDA/IFB culture medium, with its final pH adjusted to 5.7, and a photoperiod of continuous darkness was the best condition for the growth of M. musicola.

  16. Medium modifications of vector mesons

    International Nuclear Information System (INIS)

    Pant, L.M.

    2004-01-01

    The omega photoproduction in nuclear medium with the ELSA facility at Bonn and the present status of the HADES collaboration to investigate the in-medium hadron properties in proton, heavy ions and hadron induced reactions at GSI, Darmstadt are presented. Efforts are under way to utilise the electron beam at Indore for experimental hadron physics in order to step into the intermediate energy nuclear physics regime. The skeletal outline of the high energy electron beam now available at CAT, Indore is discussed

  17. Medium effects in direct reactions

    International Nuclear Information System (INIS)

    Karakoc, M; Bertulani, C

    2013-01-01

    We discuss medium corrections of the nucleon-nucleon (NN) cross sections and their influence on direct reactions at intermediate energies ≳50 MeV/nucleon. The results obtained with free NN cross sections are compared with those obtained with a geometrical treatment of Pauli-blocking and Dirac-Bruecker methods. We show that medium corrections may lead to sizable modifications for collisions at intermediate energies and that they are more pronounced in reactions involving weakly bound nuclei.

  18. Light Vector Mesons in the Nuclear Medium

    Energy Technology Data Exchange (ETDEWEB)

    Wood, Michael; Nasseripour, Rakhsha; Weygand, Dennis; Djalali, Chaden; Tur, Clarisse; Mosel, Ulrich; Muehlich, Pascal; Adams, Gary; Amaryan, Moscov; Amaryan, Moskov; Ambrozewicz, Pawel; Anghinolfi, Marco; Asryan, Gegham; Avagyan, Harutyun; Baghdasaryan, Hovhannes; Baillie, Nathan; Ball, James; Baltzell, Nathan; Barrow, Steve; Battaglieri, Marco; Bedlinskiy, Ivan; Bektasoglu, Mehmet; Bellis, Matthew; Benmouna, Nawal; Berman, Barry; Biselli, Angela; Blaszczyk, Lukasz; Bouchigny, Sylvain; Boyarinov, Sergey; Bradford, Robert; Branford, Derek; Briscoe, William; Brooks, William; Burkert, Volker; Butuceanu, Cornel; Calarco, John; Careccia, Sharon; Carman, Daniel; Carnahan, Bryan; Casey, Liam; Chen, Shifeng; Cheng, Lu; Cole, Philip; Collins, Patrick; Coltharp, Philip; Crabb, Donald; Crannell, Hall; Crede, Volker; Cummings, John; Dashyan, Natalya; De Vita, Raffaella; De Sanctis, Enzo; Degtiarenko, Pavel; Denizli, Haluk; Dennis, Lawrence; Deur, Alexandre; Dharmawardane, Kahanawita; Dickson, Richard; Dodge, Gail; Doughty, David; Dugger, Michael; Dytman, Steven; Dzyubak, Oleksandr; Egiyan, Hovanes; Egiyan, Kim; Elfassi, Lamiaa; Elouadrhiri, Latifa; Eugenio, Paul; Fedotov, Gleb; Feldman, Gerald; Feuerbach, Robert; Fradi, Ahmed; Funsten, Herbert; Garcon, Michel; Gavalian, Gagik; Gilfoyle, Gerard; Giovanetti, Kevin; Girod, Francois-Xavier; Goetz, John; Gordon, Christopher; Gothe, Ralf; Griffioen, Keith; Guidal, Michel; Guler, Nevzat; Guo, Lei; Gyurjyan, Vardan; Hadjidakis, Cynthia; Hafidi, Kawtar; Hakobyan, Hayk; Hakobyan, Rafael; Hanretty, Charles; Hardie, John; Hassall, Neil; Hersman, F.; Hicks, Kenneth; Hleiqawi, Ishaq; Holtrop, Maurik; Hyde, Charles; Ilieva, Yordanka; Ireland, David; Ishkhanov, Boris; Isupov, Evgeny; Ito, Mark; Jenkins, David; Jo, Hyon-Suk; Johnstone, John; Joo, Kyungseon; Juengst, Henry; Kalantarians, Narbe; Kellie, James; Khandaker, Mahbubul; Khetarpal, Puneet; Kim, Wooyoung; Klein, Andreas; Klein, Franz; Klimenko, Alexei; Kossov, Mikhail; Krahn, Zebulun; Kramer, Laird; Kubarovsky, Valery; Kuhn, Joachim; Kuhn, Sebastian; Kuleshov, Sergey; Lachniet, Jeff; Laget, Jean; Langheinrich, Jorn; Lawrence, David; Li, Ji; Livingston, Kenneth; Lu, Haiyun; MacCormick, Marion; Markov, Nikolai; Mattione, Paul; McAleer, Simeon; McKinnon, Bryan; McNabb, John; Mecking, Bernhard; Mehrabyan, Surik; Melone, Joseph; Mestayer, Mac; Meyer, Curtis; Mibe, Tsutomu; Mikhaylov, Konstantin; Minehart, Ralph; Mirazita, Marco; Miskimen, Rory; Mokeev, Viktor; Moriya, Kei; Morrow, Steven; Moteabbed, Maryam; Mueller, James; Munevar Espitia, Edwin; Mutchler, Gordon; Nadel-Turonski, Pawel; Niccolai, Silvia; Niculescu, Gabriel; Niculescu, Maria-Ioana; Niczyporuk, Bogdan; Niroula, Megh; Niyazov, Rustam; Nozar, Mina; Osipenko, Mikhail; Ostrovidov, Alexander; Park, Kijun; Pasyuk, Evgueni; Paterson, Craig; Pereira, Sergio; Pierce, Joshua; Pivnyuk, Nikolay; Pocanic, Dinko; Pogorelko, Oleg; Pozdnyakov, Sergey; Preedom, Barry; Price, John; Prok, Yelena; Protopopescu, Dan; Raue, Brian; Riccardi, Gregory; Ricco, Giovanni; Ripani, Marco; Ritchie, Barry; Ronchetti, Federico; Rosner, Guenther; Rossi, Patrizia; Sabatie, Franck; Salamanca, Julian; Salgado, Carlos; Santoro, Joseph; Sapunenko, Vladimir; Schumacher, Reinhard; Serov, Vladimir; Sharabian, Youri; Sharov, Dmitri; Shvedunov, Nikolay; Smith, Elton; Smith, Lee; Sober, Daniel; Sokhan, Daria; Stavinsky, Aleksey; Stepanyan, Stepan; Stepanyan, Samuel; Stokes, Burnham; Stoler, Paul; Strakovski, Igor; Strauch, Steffen; Taiuti, Mauro; Tedeschi, David; Tkabladze, Avtandil; Tkachenko, Svyatoslav; Todor, Luminita; Ungaro, Maurizio; Vineyard, Michael; Vlassov, Alexander; Watts, Daniel; Weinstein, Lawrence; Williams, Michael; Wolin, Elliott; Yegneswaran, Amrit; Zana, Lorenzo; Zhang, Bin; Zhang, Jixie; Zhao, Bo; Zhao, Zhiwen

    2008-07-01

    The light vector mesons ($\\rho$, $\\omega$, and $\\phi$) were produced in deuterium, carbon, titanium, and iron targets in a search for possible in-medium modifications to the properties of the $\\rho$ meson at normal nuclear densities and zero temperature. The vector mesons were detected with the CEBAF Large Acceptance Spectrometer (CLAS) via their decays to $e^{+}e^{-}$. The rare leptonic decay was chosen to reduce final-state interactions. A combinatorial background was subtracted from the invariant mass spectra using a well-established event-mixing technique. The $\\rho$ meson mass spectrum was extracted after the $\\omega$ and $\\phi$ signals were removed in a nearly model-independent way. Comparisons were made between the $\\rho$ mass spectra from the heavy targets ($A > 2$) with the mass spectrum extracted from the deuterium target. With respect to the $\\rho$-meson mass, we obtain a small shift compatible with zero. Also, we measure widths consistent with standard nuclear many-body eff

  19. Shock propagation in a heterogeneous medium

    International Nuclear Information System (INIS)

    Elbaz, D.

    2011-01-01

    In the frame of the inertial confinement fusion in direct drive, the use of foams as ablator allows the reduction of hydrodynamic instabilities created on the target by the direct laser irradiation. The foam is made up of carbon (CH) fibers impregnated of cryogenic deuterium-tritium (DT). In the past, studies have been carried out considering this foam to be a homogeneous medium. Yet, the foam presents heterogeneous features. We study the effects of this heterogeneity on the shock velocity when the laser irradiates the target. Thanks to experimental and numerical studies, we show that the shock propagates faster in the heterogeneous medium than in the homogeneous one with the same averaged density. This velocity gap depends on the presence rate of the CH fibers in the foam, the density ratio, the adiabatic coefficient and the foam geometry. We model the foam by different ways, more and more complex. The shock velocity modification is due to the baroclinicity which, during the interaction between the shock front and the interface, creates a vorticity deposition, responsible for the shock acceleration. Accordingly, an interface, which is plane and perpendicular to the front shock, maximizes the vorticity deposition and increases the velocity gaps between heterogeneous and homogeneous media. We found a correlation between the kinetic energy behind the shock front and the velocities relative difference. We compared our results with two analytical models. However, the system is not closed, so we can't for the moment develop a predictive model. (author) [fr

  20. Characterization of water based nanofluid for quench medium

    Science.gov (United States)

    Kresnodrianto; Harjanto, S.; Putra, W. N.; Ramahdita, G.; Yahya, S. S.; Mahiswara, E. P.

    2018-04-01

    Quenching has been a valuable method in steel hardening method especially in industrial scale. The hardenability of the metal alloys, the thickness of the component, and the geometry is some factors that can affect the choice of quench medium. Improper quench media can cause the material to become too brittle, suffers some geometric distortion, and undesirable residual stress that will cause some effect on the mechanical property and fracture mechanism of a component. Recently, nanofluid as a quench medium has been used for better quenching performance and has been studied using several different fluids and nanoparticles. Some of frequently used solvents include polymers, vegetable oils, and mineral oil, and nanoparticles frequently used include CuO, ZnO, and Alumina. In this research, laboratory-grade carbon powder were used as nanoparticle. Water was used as the fluid base in this research as the main observation focus. Carbon particles were obtain using a top-down method, whereas planetary ball mill was used to ground laboratory grade carbon powder to decrease the particle size. Milling speed and duration were set at 500 rpm and 15 hours. Field Emission Scanning Electron Microscope (FE-SEM), and Energy Dispersive X-Ray (EDX) measurement were carried out to determine the particle size, material identification, particle morphology, and surface change of samples. Nanofluid was created by mixing percentage of carbon nanoparticles with water using ultrasonic vibration for 280s. The carbon nanoparticle content in nanofluid quench mediums for this research were varied at 0.1%, 0.2%, 0.3%, 0.4, and 0.5 % volume. Furthermore, these mediums were used to quench JIS S45C or AISI 1045 carbon steel samples which austenized at 1000°C. Hardness testing and metallography observation were then conducted to further check the effect of different quench medium in steel samples. Preliminary characterizations showed that carbon particles dimension after milling was still in sub

  1. [A nutrient medium for the isolation and cultivation of Campylobacter].

    Science.gov (United States)

    Temirkhanova, Z U; Gashimova, P Sh; Safonova, N V; Moroz, A F; Khazenson, L V

    1999-01-01

    Campylobacter agar, nutrient medium intended for the isolation of bacteria of the genus Campylobacter from clinical material, has been developed. The composition of the medium includes sprat hydrolysate, aerotolerant additive (ferric sulfate--oxide, sodium pyruvate, sodium pyrosulfite), sodium glutaminate, agar. The selective properties of the medium are ensured by introducing the mixture of antibiotics consisting of polymyxin B, rifampicin, amphotericin B, ristomycin. The balanced composition of Campylobacter agar ensures the aerotolerance of Campylobacter organisms and gives the optimal conditions for their growth when the inoculated material is cultivated in the atmosphere made up of the mixture of three gases (5% of oxygen, 10% of carbon dioxide, 85% of nitrogen), as well as under the conditions of a "candle vessel". The medium suppresses the development of the associative microflora diluted 10(-1). As shown in the trial of the quality of Campylobacter agar by the inoculation of material taken from patients with acute enteric infections, agricultural animals and monkeys, the medium has pronounced selective, properties with regard to extraneous microflora, while ensuring the isolation of Campylobacter on the level of the control medium.

  2. The K sup + as a probe of nuclear medium effects

    Energy Technology Data Exchange (ETDEWEB)

    Chrien, R.E.

    1992-01-01

    The study of the K+ total cross sections on a wide range of nuclei has revealed important modifications of the free-space K+ -nucleon interaction when the nucleon is embedded in a nucleus. In addition to the previously published data on carbon and deuterium we report here the extension of such measurements to lithium, silicon, and calcium. We demonstrate that the previous reported medium modifications for carbon occur quite generally. The results are discussed as evidence for partial quark deconfinement at nuclear densities.

  3. Properties of the nuclear medium

    International Nuclear Information System (INIS)

    Baldo, M; Burgio, G F

    2012-01-01

    We review our knowledge on the properties of the nuclear medium that have been studied, over many years, on the basis of many-body theory, laboratory experiments and astrophysical observations. Throughout the presentation particular emphasis is placed on the possible relationship and links between the nuclear medium and the structure of nuclei, including the limitations of such an approach. First we consider the realm of phenomenological laboratory data and astrophysical observations and the hints they can give on the characteristics that the nuclear medium should possess. The analysis is based on phenomenological models, that however have a strong basis on physical intuition and an impressive success. More microscopic models are also considered, and it is shown that they are able to give invaluable information on the nuclear medium, in particular on its equation of state. The interplay between laboratory experiments and astrophysical observations is particularly stressed, and it is shown how their complementarity enormously enriches our insights into the structure of the nuclear medium. We then introduce the nucleon–nucleon interaction and the microscopic many-body theory of nuclear matter, with a critical discussion about the different approaches and their results. The Landau–Fermi liquid theory is introduced and briefly discussed, and it is shown how fruitful it can be in discussing the macroscopic and low-energy properties of the nuclear medium. As an illustrative example, we discuss neutron matter at very low density, and it is shown how it can be treated within the many-body theory. The general bulk properties of the nuclear medium are reviewed to indicate at which stage of our knowledge we stand, taking into account the most recent developments both in theory and experiments. A section is dedicated to the pairing problem. The connection with nuclear structure is then discussed, on the basis of the energy density functional method. The possibility of

  4. Sugarcane Bagasse: A Potential Medium for Fungal Cultures

    OpenAIRE

    Arushdeep Sidana; Umar Farooq

    2014-01-01

    Worldwide, sugarcane industries produce tons of sugarcane bagasse as residual/waste material. This residual material is rich in complex lignocellulosic substances and may be used as a low cost carbon and energy source for the growth of fungal species. The present work was aimed at designing a sugarcane waste-based medium as a substitute for expensive commercial media for growing fungal cultures. Eight species of fungi, namely, Aspergillus niger, Candida albicans, Saccharomyces cerevisiae, Fus...

  5. Laser surface modification of boronickelized medium carbon steel

    Science.gov (United States)

    Bartkowska, Aneta; Pertek, Aleksandra; Kulka, Michał; Klimek, Leszek

    2015-11-01

    A two-step process was applied to produce the multicomponent boride layers. Boronickelizing consisted of nickel plating and diffusion boriding. Two different methods of heat treatment of boronickelized C45 steel were used: a typical through-hardening, and a laser surface modification with remelting. Microstructure and some mechanical properties of these layers were examined. Microstructural characterization was studied using optical microscope, Scanning Electron Microscope, energy-dispersive X-ray microanalysis, Electron Back-Scatter Diffraction and X-ray diffraction. The laser modification improved wear resistance, cohesion as well as low-cycle fatigue of the boronickelized layer. Compressive stresses, occurring after laser remelting, could be the reason for the advantageous mechanical behavior of the layer.

  6. 1 Medium Regiment, (SAHA), SAA

    African Journals Online (AJOL)

    Scientia Militaria: South African Journal of Military Studies. Journal Home · ABOUT THIS JOURNAL · Advanced Search · Current Issue · Archives · Journal Home > Vol 16, No 4 (1986) >. Log in or Register to get access to full text downloads. Username, Password, Remember me, or Register. 1 Medium Regiment, (S.A.H.A.), ...

  7. Hadron photoproduction at medium energy

    International Nuclear Information System (INIS)

    Dainton, J.B.

    1985-04-01

    Results from measurements of multibody photoproduction at medium incident photon energy (2.8 to 4.8 GeV) are presented and discussed. Particular emphasis is placed on topics which are not well understood and which therefore motivate experiments with the upgraded electron accelerator and storage ring ELSA at the University of Bonn, FR Germany. (author)

  8. Animal Locomotion in Different Mediums

    Indian Academy of Sciences (India)

    Wetlands are repositories of unique biodiversity. Wetlandorganisms are well adapted to their habitat, lying at theinterface of aquatic and terrestrial environments. In order tounderstand their adaptations in a better way, it is essential tograsp the basic properties of the medium in which variousorganisms live. This is attempted ...

  9. Carbonation of cerium oxychloride

    International Nuclear Information System (INIS)

    Peterson, E.J.; Onstott, E.I.; Bowman, M.G.

    1977-01-01

    Cerous carbonates can be used in thermochemical cycles for H production if the resulting ceric oxides can be converted back into cerous carbonates. One way is to reduce and hydrolyze ceric oxide with HCl to produce CeOCl and then to carbonate it. The reaction 3CeOCl + 3CO 2 + 8H 2 O → CeCl 3 (aq) + Ce 2 (CO 3 ) 3 . 8H 2 O was found to occur in aqueous medium if the final CeCl 3 content is low. Carbonation of CeOCl could also be conducted in acetone --H 2 O . CeClCO 3 . 3H 2 O was decomposed and characterized. The reactions which can be used for water splitting are discussed briefly

  10. Holographic Renormalization in Dense Medium

    International Nuclear Information System (INIS)

    Park, Chanyong

    2014-01-01

    The holographic renormalization of a charged black brane with or without a dilaton field, whose dual field theory describes a dense medium at finite temperature, is investigated in this paper. In a dense medium, two different thermodynamic descriptions are possible due to an additional conserved charge. These two different thermodynamic ensembles are classified by the asymptotic boundary condition of the bulk gauge field. It is also shown that in the holographic renormalization regularity of all bulk fields can reproduce consistent thermodynamic quantities and that the Bekenstein-Hawking entropy is nothing but the renormalized thermal entropy of the dual field theory. Furthermore, we find that the Reissner-Nordström AdS black brane is dual to a theory with conformal matter as expected, whereas a charged black brane with a nontrivial dilaton profile is mapped to a theory with nonconformal matter although its leading asymptotic geometry still remains as AdS space

  11. Medium modifications with recoil polarization

    Energy Technology Data Exchange (ETDEWEB)

    Brand, J.F.J. van den [Nationaal Instituut voor Kernfysica en Hoge Energiefysica, Amsterdam (Netherlands); Ent, R. [CEBAF, Newport News, VA (United States)

    1994-04-01

    The authors show that the virtual Compton scattering process allows for a precise study of the off-shell electron-nucleon vertex. In a separable model, they show the sensitivity to new unconstrained structure functions of the nucleon, beyond the usual Dirac and Pauli form factors. In addition, they show the sensitivity to bound nucleon form factors using the reaction 4He({rvec e},e{prime},{rvec p}){sup 3}H. A nucleon embedded in a nucleus represents a complex system. Firstly, the bound nucleon is necessarily off-shell and in principle a complete understanding of the dynamical structure of the nucleon is required in order to calculate its off-shell electromagnetic interaction. Secondly, one faces the possibility of genuine medium effects, such as for example quark-exchange contributions. Furthermore, the electromagnetic coupling to the bound nucleon is dependent on the nuclear dynamics through the self-energy of the nucleon in the nuclear medium.

  12. Medium modifications with recoil polarization

    International Nuclear Information System (INIS)

    Brand, J.F.J. van den; Ent, R.

    1994-01-01

    The authors show that the virtual Compton scattering process allows for a precise study of the off-shell electron-nucleon vertex. In a separable model, they show the sensitivity to new unconstrained structure functions of the nucleon, beyond the usual Dirac and Pauli form factors. In addition, they show the sensitivity to bound nucleon form factors using the reaction 4He(rvec e,e',rvec p) 3 H. A nucleon embedded in a nucleus represents a complex system. Firstly, the bound nucleon is necessarily off-shell and in principle a complete understanding of the dynamical structure of the nucleon is required in order to calculate its off-shell electromagnetic interaction. Secondly, one faces the possibility of genuine medium effects, such as for example quark-exchange contributions. Furthermore, the electromagnetic coupling to the bound nucleon is dependent on the nuclear dynamics through the self-energy of the nucleon in the nuclear medium

  13. Medium Theory and Social Systems

    DEFF Research Database (Denmark)

    Tække, Jesper

      the  possibility  for  observation both of a social micro and a social macro level from a medium perspective. In the next  section  the paper  frames  the macro  level by  a  tentative  synthesis of  the medium  theory  and  the  sociological systems theory briefly describing a socio......-evolutionary process where new media alter  the societal capacity to handle complexity  in  time and space.  In  this section it becomes probable  that  by  means  of  different  media,  social  systems  give  different  possibilities  for  actual  social  performance.  In a way,  social  systems  themselves can be......  seen as medium  for  formation. Finally  the  paper  takes  the micro  level  perspective  by  applying  the  theory  to  newsgroups,  interpreting  them as self-organizing interactive systems giving a differentiated and diversified scope for social  inclusion.  ...

  14. Accretion from an inhomogeneous medium

    International Nuclear Information System (INIS)

    Livio, M.; Soker, N.; Koo, M. de; Savonije, G.J.

    1986-01-01

    The problem of accretion by a compact object from an inhomogeneous medium is studied in the general γnot=1 case. The mass accretion rate is found to decrease with increasing γ. The rate of accretion of angular momentum is found to be significantly lower than the rate at which angular momentum is deposited into the Bondi-Hoyle, symmetrical, accretion cylinder. The consequences of the results are studied for the cases of neutron stars accreting from the winds of early-type companions and white dwarfs and main-sequence stars accreting from winds of cool giants. (author)

  15. A Heterogeneous Medium Analytical Benchmark

    International Nuclear Information System (INIS)

    Ganapol, B.D.

    1999-01-01

    A benchmark, called benchmark BLUE, has been developed for one-group neutral particle (neutron or photon) transport in a one-dimensional sub-critical heterogeneous plane parallel medium with surface illumination. General anisotropic scattering is accommodated through the Green's Function Method (GFM). Numerical Fourier transform inversion is used to generate the required Green's functions which are kernels to coupled integral equations that give the exiting angular fluxes. The interior scalar flux is then obtained through quadrature. A compound iterative procedure for quadrature order and slab surface source convergence provides highly accurate benchmark qualities (4- to 5- places of accuracy) results

  16. Charmed hadrons in nuclear medium

    International Nuclear Information System (INIS)

    Tolos, L.; Gamermann, D.; Molina, R.; Nieves, J.; Oset, E.; Garcia-Recio, C.; Ramos, A.

    2010-01-01

    We study the properties of charmed hadrons in dense matter within a coupled-channel approach which accounts for Pauli blocking effects and meson self-energies in a self-consistent manner. We analyze the behaviour in this dense environment of dynamically-generated baryonic resonances as well as the open-charm meson spectral functions. We discuss the implications of the in-medium properties of open-charm mesons on the D s0 (2317) and the predicted X(3700) scalar resonances. (authors)

  17. Development of brachytherapy medium doserate

    International Nuclear Information System (INIS)

    Atang Susila; Ari Satmoko; Ahmad Rifai; Kristiyanti

    2010-01-01

    Brachytherapy has proven to be an effective treatment for different types of cancers and it become a common treatment modality in most radiotherapy clinics. PRPN has had experience in development of Low Dose Rate Brachytherapy for cervix cancer treatment. However the treatment process using LDR device needs 5 hours in time that the patient feel uncomfort. Therefore PRPN develops Medium Dose Rate Brachytherapy with radiation activity not more than 5 Currie. The project is divided into two stages. Purchasing of TPS software and TDS design are held in 2010, and the construction will be in 2011. (author)

  18. Influence of glutamate on growth, sporulation, and spore properties of Bacillus cereus ATCC 14579 in defined medium

    NARCIS (Netherlands)

    Vries, de Y.P.; Atmadja, R.D.; Hornstra, L.M.; Vos, de W.M.; Abee, T.

    2005-01-01

    A chemically defined medium in combination with an airlift fermentor system was used to study the growth and sporulation of Bacillus cereus ATCC 14579. The medium contained six amino acids and lactate as the main carbon sources. The amino acids were depleted during exponential growth, while lactate

  19. Analysis of the influence of the multipass welding, welding preheat and welding post heat treatments on the behaviour of GMAW joints of HARDOX 400 microalloyed steel; Influencia de la tecnica de soldaduramultipasada y de los tratamientos termicos de precalentamiento y post-soldadura en el comportamiento de uniones GMAW de un acero microaleado HARDOX 400

    Energy Technology Data Exchange (ETDEWEB)

    Martinez, A.; Miguel, V.; Coello, J.; Navarro, A.; Calatayud, A.; Manjabacas, M. C.

    2011-07-01

    The microalloyed steels may be supplied in a hardened state. In these cases, the weldability can be improved by pre-heat and/or post-heat welding treatments. In this paper, the effect of those treatments and the influence of multipass welding on GMAW joints behavior are analyzed for a Hardox 400 microalloyed steel. The microstructure evaluation of the different heat affected zones of the steel has been made and the mechanical properties of those zones are obtained for different conditions as it has been mentioned. The obtained results indicate that preheating the steel leads to a beneficial action that consists on the distance increasing from the bead to the zone in which the hardness is lowest. The post heat treatment strengthens that zone and improves the joint plasticity. This benefit is higher if the joint has been made with preheating. Multipass welding has not been found to have any advantage if it is compared to a single welding pass. (Author) 18 refs.

  20. Medium modification of fragmentation functions

    International Nuclear Information System (INIS)

    Nezza, Pasquale Di

    2007-01-01

    Deep Inelastic Scattering is the cleanest process to investigate the space-time evolution of the hadronization. This was studied by the influence of the nuclear medium on lepto-production of hadrons at the Hermes experiment at DESY in semi-inclusive DIS of 27.6 GeV positrons off deuterium, nitrogen, krypton and xenon targets. The differential multiplicity for heavy targets relative to that of deuterium has been measured for the first time for various identified hadrons (φ + , φ - , φ 0 , k + , k - , p and anti-p) as a function of the virtual photon energy ?, the fraction z of this energy transferred to the hadron, and the hadron transverse momentum squared p 2 t . The distribution of the hadron transverse momentum is broadened towards high p 2 t in the nuclear medium, in a manner resembling the Cronin effect observed in collisions of heavy ions and protons with nuclei. The pt -broadening results give also important information about the pre-hadron formation time. Moreover, by studying the hadron attenuation of the leading and sub-leading hadrons, we report, for the first time, the possibility to better understand the hadron absorption and the energy loss contributions to the attenuation mechanism. (Author)

  1. Gravitational lensing in plasmic medium

    Energy Technology Data Exchange (ETDEWEB)

    Bisnovatyi-Kogan, G. S., E-mail: gkogan@iki.rssi.ru; Tsupko, O. Yu., E-mail: tsupko@iki.rssi.ru [Russian Academy of Sciences, Space Research Institute (Russian Federation)

    2015-07-15

    The influence of plasma on different effects of gravitational lensing is reviewed. Using the Hamiltonian approach for geometrical optics in a medium in the presence of gravity, an exact formula for the photon deflection angle by a black hole (or another body with a Schwarzschild metric) embedded in plasma with a spherically symmetric density distribution is derived. The deflection angle in this case is determined by the mutual combination of different factors: gravity, dispersion, and refraction. While the effects of deflection by the gravity in vacuum and the refractive deflection in a nonhomogeneous medium are well known, the new effect is that, in the case of a homogeneous plasma, in the absence of refractive deflection, the gravitational deflection differs from the vacuum deflection and depends on the photon frequency. In the presence of a plasma nonhomogeneity, the chromatic refractive deflection also occurs, so the presence of plasma always makes gravitational lensing chromatic. In particular, the presence of plasma leads to different angular positions of the same image if it is observed at different wavelengths. It is discussed in detail how to apply the presented formulas for the calculation of the deflection angle in different situations. Gravitational lensing in plasma beyond the weak deflection approximation is also considered.

  2. Unsaturated medium hydrocarbons pollution evaluation

    International Nuclear Information System (INIS)

    Di Luise, G.

    1991-01-01

    When the so called porous unsaturated medium, that's the vertical subsoil section between both the ground and water-table level, is interested by a hydrocarbons spill, the problem to evaluate the pollution becomes difficult: considering, essentially, the natural coexistence in it of two fluids, air and water, and the interactions between them. This paper reports that the problems tend to increase when a third fluid, the pollutant, immiscible with water, is introduced into the medium: a three-phases flow, which presents several analogies with the flow conditions present in an oil-reservoir, will be established. In such a situation, it would be very useful to handle the matter by the commonly used parameters in the oil reservoirs studies such as: residual saturation, relative permeability, phases mobility, to derive a first semiquantitative estimation of the pollution. The subsoil pollution form hydrocarbons agents is one of the worldwide more diffused causes of contamination: such events are generally referable to two main effects: accidental (oil pipeline breakdowns, e.g.), and continuous (underground tanks breaks, industrial plants leakages, e.g.)

  3. Is the intercloud medium pervasive

    International Nuclear Information System (INIS)

    Heiles, C.

    1980-01-01

    We consider the pervasiveness of the ''not strongly absorbing'' (NSA) H I gas, which is the intercloud medium in steady state theories of the interstellar medium. We study the question by analyzing wide emission components in nearby gas, and the absence of absorption components in distant gas. We conclude that the NSA material is deficient in the immediately local solar vicinity. In nearby regions it contains 38% of the interstellar H I; it is generally pervasive and often has internal motions which greatly increase its velocity dispersion above the 5 km s -1 minimum value. It contains large holes, perhaps ranging up to 400 pc diameter, which probably occupy 10--20% of the volume. In distant regions the NSA material seems to be pervasive outside 8 kpc galactic radius. For galactic radii between 8 and 10 kpc its thickness agrees with previous determinations of 370 pc for nearby regions. Outside 10 kpc the thickness increases dramatically. Inside 8 kpc there are no data

  4. How Does the Medium Affect the Message?

    Science.gov (United States)

    Dommermuth, William P.

    1974-01-01

    This experimental comparison of the advertising effectiveness of television, movies, radio, and print finds no support for McLuhan's idea that television is a "cool" medium and movies are a "hot" medium. (RB)

  5. 27 CFR 19.914 - Medium plants.

    Science.gov (United States)

    2010-04-01

    ... 27 Alcohol, Tobacco Products and Firearms 1 2010-04-01 2010-04-01 false Medium plants. 19.914... OF THE TREASURY LIQUORS DISTILLED SPIRITS PLANTS Distilled Spirits For Fuel Use Permits § 19.914 Medium plants. Any person wishing to establish a medium plant shall make application for and obtain in...

  6. Mapping of moveout in a TTI medium

    KAUST Repository

    Stovas, A.; Alkhalifah, Tariq Ali

    2012-01-01

    To compute moveout in a transversely isotropic medium with tilted symmetry axis is a very complicated problem. We propose to split this problem into two parts. First, to compute the moveout in a corresponding VTI medium. Second, to map the computed moveout to a TTI medium.

  7. Medium-size nuclear plants

    International Nuclear Information System (INIS)

    Vogelweith, L.; Lavergne, J.C.; Martinot, G.; Weiss, A.

    1977-01-01

    CEA (TECHNICATOME) has developed a range of pressurized water reactors of the type ''CAS compact'' which are adapted to civil ship propulsion, or to electric power production, combined possibly with heat production, up to outputs equivalent to 125 MWe. Nuclear plants equipped with these reactors are suitable to medium-size electric networks. Among the possible realizations, two types of plants are mentioned as examples: 1) Floating electron-nuclear plants; and 2) Combined electric power and desalting plants. The report describes the design characteristics of the different parts of a 125 MWe unit floating electro-nuclear plant: nuclear steam system CAS 3 G, power generating plant, floating platform for the whole plant. The report gives attention to the different possibilities according to site conditions (the plant can be kept floating, in a natural or artificial basin, it can be put aground, ...) and to safety and environment factors. Such unit can be used in places where there is a growing demand in electric power and fresh water. The report describes how the reactor, the power generating plant and multiflash distillation units of an electric power-desalting plant can be combined: choice of the ratio water output/electric power output, thermal cycle combination, choice of the gain ratio, according to economic considerations, and to desired goal of water output. The report analyses also some technical options, such as: choice of the extraction point of steam used as heat supply of the desalting station (bleeding a condensation turbine, or recovering steam at the exhaust of a backpressure turbine), design making the system safe. Lastly, economic considerations are dealt with: combining the production of fresh water and electric power provides usually a much better energy balance and a lower cost for both products. Examples are given of some types of installations which combine medium-size reactors with fresh water stations yielding from 10000 to 120000 m 3 per day

  8. [Medium energy physics at Syracuse University: Technical progress report

    International Nuclear Information System (INIS)

    Souder, P.A.

    1986-01-01

    The primary focus of research has been an experiment at the MIT-Bates Linear Accelerator Center to measure the spin-dependence of elastic scattering of electrons from carbon. The Syracuse University Medium Energy Physics Group is also part of a collaboration which will measure the tensor polarization of deuterons scattered by electrons. Finally, analysis has been completed for an experiment at LAMPF in which the first observation of the exotic ion μ + e - e - was made. 17 refs., 18 figs., 2 tabs

  9. Tattoo: a multifaceted medium of communication

    Directory of Open Access Journals (Sweden)

    Christian Wymann

    2010-11-01

    Full Text Available This article suggests the systems theoretical distinction of form/medium as a useful tool for distinguishing social phenomena that might look as if they stem from the same process. This is shown to be the case for the tattoo and tattooing. The tattoo is conceived as a medium of communication through which different forms of communication emerge. Tattooing is one of these forms of communication that shapes the medium in a particular way. The current article sheds a special light on its intricate, communicational constellation, for which the concept of parallax is suggested. Law, medicine and cosmetics as other forms of communication use the medium of tattoo in their own way as well. The form/medium distinction allows us to grasp these different forms of communication, while it shows that they share the tattoo as medium. The article’s ultimate goal is to illustrate that the tattoo figures as a multifaceted medium of communication.

  10. Perspectives in the use of carbon dioxide

    Directory of Open Access Journals (Sweden)

    Aresta Michele

    1999-01-01

    Full Text Available The mitigation of carbon dioxide is one of the scientific and technological challenges of the 2000s. Among the technologies that are under assessment, the recovery of carbon dioxide from power plants or industrial flue gases plays a strategic role. Recovered carbon dioxide can be either disposed in natural fields or used. The availability of large amounts of carbon dioxide may open new routes to its utilisation in biological, chemical and innovative technological processes. In this paper, the potential of carbon dioxide utilisation in the short-, medium-term is reviewed.

  11. Medium-Based Design: Extending a Medium to Create an Exploratory Learning Environment

    Science.gov (United States)

    Rick, Jochen; Lamberty, K. K.

    2005-01-01

    This article introduces "medium-based" design -- an approach to creating "exploratory learning environments" using the method of "extending a medium". First, the characteristics of exploratory learning environments and medium-based design are described and grounded in related work. Particular attention is given to "extending a medium" --…

  12. Dreams of a New Medium

    Directory of Open Access Journals (Sweden)

    Aden Evens

    2009-01-01

    Full Text Available Problematic at best, the desire for a transparent interface nevertheless drives much of digital culture and technology. But not the Web; or at least, not Web 1.0. Thoroughly commercialized, comfortably parsed into genres, serving billions of pages of predigested content to passive consumers, the World Wide Web as developed in the '90s unabashedly embraces its role as medium. While so many digital technologies work to hide their mediacy--drawing in the user with a total simulated sensorium, dematerializing the resistances of size and weight, untangling the knots of cables tying user to machine and machine to cubicle, minimizing the interface--Web 1.0 proudly clings to the browser as a glaring reminder of its medial character. While Web 2.0 has not forsaken the browser altogether, it nevertheless seems to offer a different sort of mediation. Arising alongside the atomization of browser functions, the ubiquitization of connectivity, and the coincidence of producer and user, Web 2.0 retains the form of a medium while reaching for the experiential logic of immediacy. This is not the immediacy of the transparent interface; rather, Web 2.0 effects an immediate relationship between the individual and culture. The interface does not disappear, but its mediacy is subsumed under the general form of cultural participation. Focusing on the "version upgrade" from Web 1.0 to 2.0, this essay will explore the implications for mediacy of this transition, noting that the fantasy of immediacy which drives Web 2.0 is layered and complex. The typical account of immediacy proposes to eliminate the interface and so construct a virtual reality (VR. But Web 2.0 mostly sidesteps the virtual, propelled instead by a fantasy of intuition in which the Web already knows what you want because it is you. Crucially, fantasies about the digital are effective: the computer's futurity inhabits our world, finding its expression in politics, advertising, budgeting, strategic planning

  13. Dust in the Diffuse Neutral Interstellar Medium

    Science.gov (United States)

    Sofia, Ulysses J.

    2008-05-01

    Studies of interstellar dust have always relied heavily upon Laboratory Astrophysics for interpretation. Laboratory values, in the broad sense that includes theory, are needed for the most basic act of measuring interstellar abundances, to the more complex determination of what grains are responsible for particular extinction. The symbiotic relationship between astronomical observations and Laboratory Astrophysics has prompted both fields to move forward, especially in the era of high-resolution ultraviolet spectroscopy when new elemental species could be interpreted and observations were able to show the limits of laboratory determinations. Thanks to this synergy, we currently have a good idea of the quantity of the most abundant elements incorporated into dust in diffuse neutral interstellar clouds: carbon, oxygen, iron, silicon and magnesium. Now the task is to figure out how, chemically and physically, those elements are integrated into interstellar grains. We can do this by comparing extinction curves to grain populations in radiative transfer models. The limitation at the present time is the availability of optical constants in the infrared through ultraviolet for species that are likely to exist in dust, i.e., those that are easy to form in the physical environments around stars and in molecular clouds. Extinction in some lines of sight can be fit within current abundance limits and with the optical constants that are available. However the inability to reproduce other extinction curves suggests that optical constants can be improved, either in quality for compounds that have been measured, or quantity in the sense of providing data for more materials. This talk will address the current state and the future of dust studies in the diffuse neutral interstellar medium. This work is supported by the grant HST-AR-10979.01-A from the Space Telescope Science Institute to Whitman College.

  14. Selection of culture medium and conditions for the production of ...

    African Journals Online (AJOL)

    defined medium–A, defined medium-B, synthetic medium, rich medium and industrial medium) showed that the synthetic medium yielded maximum yeast biomass (12.8 g/LDCW) followed by rich medium (11.7 g/L DCW) and defined medium B ...

  15. The interstellar medium in galaxies

    CERN Document Server

    1997-01-01

    It has been more than five decades ago that Henk van de Hulst predicted the observability of the 21-cm line of neutral hydrogen (HI ). Since then use of the 21-cm line has greatly improved our knowledge in many fields and has been used for galactic structure studies, studies of the interstellar medium (ISM) in the Milky Way and other galaxies, studies of the mass distribution of the Milky Way and other galaxies, studies of spiral struc­ ture, studies of high velocity gas in the Milky Way and other galaxies, for measuring distances using the Tully-Fisher relation etc. Regarding studies of the ISM, there have been a number of instrumen­ tal developments over the past decade: large CCD's became available on optical telescopes, radio synthesis offered sensitive imaging capabilities, not only in the classical 21-cm HI line but also in the mm-transitions of CO and other molecules, and X-ray imaging capabilities became available to measure the hot component of the ISM. These developments meant that Milky Way was n...

  16. Studies in medium energy physics

    International Nuclear Information System (INIS)

    Green, A.; Hoffmann, G.W.; McDonough, J.; Purcell, M.J.; Ray, R.L.; Read, D.E.; Worn, S.D.

    1991-12-01

    This document constitutes the (1991--1992) technical progress report and continuation proposal for the ongoing medium energy nuclear physics research program supported by the US Department of Energy through special Research Grant DE-FG05-88ER40444. The experiments discussed are conducted at the Los Alamos National Laboratory's (LANL) Clinton P. Anderson Meson Physics Facility (LAMPF) and the Alternating Gradient Synchrotron (AGS) facility of the Brookhaven National Laboratory (BNL). The overall motivation for the work discussed in this document is driven by three main objectives: (1) provide hadron-nucleon and hadron-nucleus scattering data which serve to facilitate the study of effective two-body interactions, test (and possibly determine) nuclear structure, and help study reaction mechanisms and dynamics; (2) provide unique, first-of-a-kind ''exploratory'' hadron-nucleus scattering data in the hope that such data will lead to discovery of new phenomena and new physics; and (3) perform precision tests of fundamental interactions, such as rare decay searches, whose observation would imply fundamental new physics

  17. Optical illusions induced by rotating medium

    Science.gov (United States)

    Zang, XiaoFei; Huang, PengCheng; Zhu, YiMing

    2018-03-01

    Different from the traditional single-function electromagnetic wave rotators (rotate the electromagnetic wavefronts), we propose that rotating medium can be extended to optical illusions such as breaking the diffraction limit and overlapping illusion. Furthermore, the homogeneous but anisotropic rotating medium is simplified by homogeneous and isotropic positive-index materials according to the effective medium theory, which is helpful for future device fabrication. Finite element simulations for the two-dimensional case are performed to demonstrate these properties.

  18. A differential medium for the enumeration of the spoilage yeast Zygosaccharomyces bailii in wine.

    Science.gov (United States)

    Schuller, D; Côrte-Real, M; Leão, C

    2000-11-01

    A collection of yeasts, isolated mostly from spoiled wines, was used in order to develop a differential medium for Zygosaccharomyces bailii. The 118 selected strains of 21 species differed in their origin and resistance to preservatives and belonged to the genera Pichia, Torulaspora, Dekkera, Debaryomyces, Saccharomycodes, Issatchenkia, Kluyveromyces, Kloeckera, Lodderomyces, Schizosaccharomyces, Rhodotorula, Saccharomyces, and Zygosaccharomyces. The design of the culture medium was based on the different ability of the various yeast species to grow in a mineral medium with glucose and formic acid (mixed-substrate medium) as the only carbon and energy sources and supplemented with an acid-base indicator. By manipulating the concentration of the acid and the sugar it was possible to select conditions where only Z. bailii strains gave rise to alkalinization, associated with a color change of the medium (positive response). The final composition of the mixed medium was adjusted as a compromise between the percentage of recovery and selectivity for Z. bailii. This was accomplished by the use of pure or mixed cultures of the yeast strains and applying the membrane filtration methodology. The microbiological analysis of two samples of contaminated Vinho Verde showed that the new medium can be considered as a differential medium to distinguish Z. bailii from other contaminating yeasts, having potential application in the microbiological control of wines and probably other beverages and foods.

  19. The impact of a carbon tax on economic growth and carbon dioxide emissions in Ireland

    NARCIS (Netherlands)

    Conefrey, Thomas; Fitz Gerald, John D.; Valeri, Laura Malaguzzi; Tol, Richard S J

    2013-01-01

    This paper analyses the medium-term effects of a carbon tax on growth and CO2 emissions in Ireland, a small open economy. We find that a double dividend exists if the carbon tax revenue is recycled through reduced income taxes. If the revenue is recycled by giving a lump-sum transfer to households,

  20. Development of a novel artificial medium based on utilization of algal photosynthetic metabolites by symbiotic heterotrophs.

    Science.gov (United States)

    Watanabe, K; Imase, M; Aoyagi, H; Ohmura, N; Saiki, H; Tanaka, H

    2008-09-01

    (i) Quantitative and qualitative analyses of photosynthetic metabolites of Chlorella sorokiniana and elucidation of the mechanism of their utilization by algal symbionts. (ii) Development of artificial medium that imitates photoautotroph-heterotroph interaction and investigation of its suitability for isolation of novel microbes from the environment. Various components, including free dissolved carbohydrates, nitrogenous compounds and vitamin, were detected and together contributed 11.1% (as carbon content) of the total photosynthetic metabolites in the medium. Utilization of these photosynthetic metabolites in algal culture broth by algal symbionts was studied. Many symbionts showed specific utilization patterns. A novel artificial extracellular released organic carbon medium, which imitated the nutritional conditions surrounding algae, was developed based on the pattern of utilization of the algal metabolites by the symbiotic heterotrophs. About 42.9% of the isolates were closely related to photoautotrophic-dependent and oligotrophic bacteria. With the novel artificial medium, it was possible to selectively isolate some bacterial strains. Synthetic bacterial growth medium is an important and basic tool for bacterial isolation from environmental samples. The current study shows that preferential separation of typical bacterial subset can be achieved by using artificial medium that mimics photosynthetic metabolites.

  1. Medium factors on anaerobic production of rhamnolipids by Pseudomonas aeruginosa SG and a simplifying medium for in situ microbial enhanced oil recovery applications.

    Science.gov (United States)

    Zhao, Feng; Zhou, Jidong; Han, Siqin; Ma, Fang; Zhang, Ying; Zhang, Jie

    2016-04-01

    Aerobic production of rhamnolipid by Pseudomonas aeruginosa was extensively studied. But effect of medium composition on anaerobic production of rhamnolipid by P. aeruginosa was unknown. A simplifying medium facilitating anaerobic production of rhamnolipid is urgently needed for in situ microbial enhanced oil recovery (MEOR). Medium factors affecting anaerobic production of rhamnolipid were investigated using P. aeruginosa SG (Genbank accession number KJ995745). Medium composition for anaerobic production of rhamnolipid by P. aeruginosa is different from that for aerobic production of rhamnolipid. Both hydrophobic substrate and organic nitrogen inhibited rhamnolipid production under anaerobic conditions. Glycerol and nitrate were the best carbon and nitrogen source. The commonly used N limitation under aerobic conditions was not conducive to rhamnolipid production under anaerobic conditions because the initial cell growth demanded enough nitrate for anaerobic respiration. But rhamnolipid was also fast accumulated under nitrogen starvation conditions. Sufficient phosphate was needed for anaerobic production of rhamnolipid. SO4(2-) and Mg(2+) are required for anaerobic production of rhamnolipid. Results will contribute to isolation bacteria strains which can anaerobically produce rhamnolipid and medium optimization for anaerobic production of rhamnolipid. Based on medium optimization by response surface methodology and ions composition of reservoir formation water, a simplifying medium containing 70.3 g/l glycerol, 5.25 g/l NaNO3, 5.49 g/l KH2PO4, 6.9 g/l K2HPO4·3H2O and 0.40 g/l MgSO4 was designed. Using the simplifying medium, 630 mg/l of rhamnolipid was produced by SG, and the anaerobic culture emulsified crude oil to EI24 = 82.5 %. The simplifying medium was promising for in situ MEOR applications.

  2. Carbon-carbon coupling reactions of medium-sized N-containing dications

    Czech Academy of Sciences Publication Activity Database

    Zins, Emilie-Laure; Schröder, Detlef

    2010-01-01

    Roč. 114, č. 19 (2010), s. 5989-5996 ISSN 1089-5639 R&D Projects: GA ČR GA203/09/1223 Grant - others: ERC (XE) HORIZOMS AdG226373 Institutional research plan: CEZ:AV0Z40550506 Keywords : C-C coupling * dications * methane * pyridine * Titan Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 2.732, year: 2010

  3. Recordable storage medium with protected data area

    NARCIS (Netherlands)

    2005-01-01

    The invention relates to a method of storing data on a rewritable data storage medium, to a corresponding storage medium, to a corresponding recording apparatus and to a corresponding playback apparatus. Copy-protective measures require that on rewritable storage media some data must be stored which

  4. Electromagnetic Sources in a Moving Conducting Medium

    DEFF Research Database (Denmark)

    Johannsen, Günther

    1971-01-01

    The problem of an arbitrary source distribution in a uniformly moving, homogeneous, isotropic, nondispersive, conducting medium is solved. The technique used is to solve the problem in the rest system of the medium and then write the result in an appropriate four-dimensional, covariant form which...

  5. Kultivasi Scenedesmus SP. Pada Medium Air Limbah

    OpenAIRE

    Kawaroe, Mujizat

    2011-01-01

    Proses fotosintesis pada mikroalga membutuhkan CO2 dan cahaya matahari serta nutrien untuk pertumbuhannya. Kultivasi Scenedesmus sp. pada medium air limbah bertujuan guna mencukupi kebutuhan mikroalga akan nutrien dan mengurangi masukan dari bahan kimia yang terkandung dalam air limbah tersebut ke lingkungan. Kultivasi Scenedesmus sp. dilakukan selama tujuh hari pada medium air limbah industri tanpa penambahan nutri...

  6. Effective medium theory for anisotropic metamaterials

    KAUST Repository

    Zhang, Xiujuan; Wu, Ying

    2015-01-01

    -dimensional metamaterial composed of a rectangular array of elliptic cylinders and derive an effective medium theory for such a metamaterial. We find that it is possible to obtain a closed-form analytical solution for the anisotropic effective medium parameters, provided

  7. Selective medium for aerobic incubation of Campylobacter

    Science.gov (United States)

    Studies were conducted on the formulation of a selective medium that could be used to isolate Campylobacter from mixed bacterial cultures using aerobic incubation. A non-selective, basal broth medium was prepared and supplemented with Bolton, Cefex, or Skirrow antibiotic mixtures. The ability of pur...

  8. Effective medium theory for anisotropic metamaterials

    KAUST Repository

    Zhang, Xiujuan

    2015-01-20

    Materials with anisotropic material parameters can be utilized to fabricate many fascinating devices, such as hyperlenses, metasolids, and one-way waveguides. In this study, we analyze the effects of geometric anisotropy on a two-dimensional metamaterial composed of a rectangular array of elliptic cylinders and derive an effective medium theory for such a metamaterial. We find that it is possible to obtain a closed-form analytical solution for the anisotropic effective medium parameters, provided the aspect ratio of the lattice and the eccentricity of the elliptic cylinder satisfy certain conditions. The derived effective medium theory not only recovers the well-known Maxwell-Garnett results in the quasi-static regime, but is also valid beyond the long-wavelength limit, where the wavelength in the host medium is comparable to the size of the lattice so that previous anisotropic effective medium theories fail. Such an advance greatly broadens the applicable realm of the effective medium theory and introduces many possibilities in the design of structures with desired anisotropic material characteristics. A real sample of a recently theoretically proposed anisotropic medium, with a near-zero index to control the flux, is achieved using the derived effective medium theory, and control of the electromagnetic waves in the sample is clearly demonstrated.

  9. Liquid-liquid extraction of plutonium and americium by cekanoic acid from alkaline medium

    International Nuclear Information System (INIS)

    Venugopal Chetty, K.; Sagar, V.; Swarup, R.

    2001-01-01

    Liquid-liquid extraction studies of plutonium and americium from aqueous carbonate medium using a high molecular weight carboxylic acid namely cekanoic acid in different diluents has been carried out. The distribution ratio (D) values for Pu(IV) and Am(III) under various parameters such as concentration of extractant, Na 2 CO 3 and initial pH were obtained. Results indicated that Pu(IV) and Am(III) could be satisfactorily extracted together or individually from aqueous carbonate medium using cekanoic acid in different diluents like carbon tetrachloride, cyclohexane, toluene, n-dodecane or solvesso-100. The D values for Pu(IV) and Am(III) also indicated the possibility of their mutual separation. The back extraction of Pu and Am with different reagents was also studied. (orig.)

  10. Growth and Development of Colletotrichum gloeosporioides f. alatae During Culture in Liquid Medium

    Directory of Open Access Journals (Sweden)

    Laura E. Cerón Rincón

    2006-01-01

    Full Text Available Some characteristics known as virulence factors for Colletotrichum sp. genus, like: weight of the produced mycelium, sporulation, poligalacturonase activity and pH medium were evaluated during the growth of C. gloeosporioides f. alatae in three liquid medium commonly used for fungi culture (Czapeck, Martin broth and potato broth and additionally (Czapeck with yam extract as the only source of carbon. After of 17 days of growth, maximum values were obtained for the above parameters in the last medium, compared with others growth media evaluated. The implemented medium with yam extract, supply nutritional requirements of the pathogen for the development of characteristic factors related with mechanism of infections that may play a role in the pathogenesis.

  11. Micropropagation of Alstroemeria in liquid medium using slow release of medium components

    NARCIS (Netherlands)

    Klerk, de G.J.M.; Brugge, ter J.

    2010-01-01

    Alstroemeria rhizomes were micropropagated on semi-solid medium (AM) and in liquid medium (LM). In LM, growth was much enhanced (ca. 70%). Adequate gas exchange was crucial. This was obtained by agitation and in static medium by a sufficient large contact area of the explant and the gaseous

  12. Utilization and optimization of a waste stream cellulose culture medium for pigment production by Penicillium spp.

    Science.gov (United States)

    Sopandi, T; Wardah, A; Surtiningsih, T; Suwandi, A; Smith, J J

    2013-03-01

    This research sought to determine optimal corn waste stream-based fermentation medium C and N sources and incubation time to maximize pigment production by an indigenous Indonesian Penicillium spp., as well as to assess pigment pH stability. A Penicillium spp. was isolated from Indonesian soil, identified as Penicillium resticulosum, and used to test the effects of carbon and nitrogen type and concentrations, medium pH, incubation period and furfural on biomass and pigment yield (PY) in a waste corncob hydrolysate basal medium. Maximum red PY (497.03 ± 55.13 mg l(-1)) was obtained with a 21 : 1 C : N ratio, pH 5.5-6.0; yeast extract-, NH(4) NO(3)-, NaNO(3)-, MgSO(4) ·7H(2) O-, xylose- or carboxymethylcellulose (CMC)-supplemented medium and 12 days (25 °C, 60-70% relative humidity, dark) incubation. C source, C, N and furfural concentration, medium pH and incubation period all influenced biomass and PY. Pigment was pH 2-9 stable. Penicillium resticulosum demonstrated microbial pH-stable-pigment production potential using a xylose or CMC and N source, supplemented waste stream cellulose culture medium. Corn derived, waste stream cellulose can be used as a culture medium for fungal pigment production. Such application provides a process for agricultural waste stream resource reuse for production of compounds in increasing demand. © 2012 The Society for Applied Microbiology.

  13. Collaborative Manufacturing for Small-Medium Enterprises

    Science.gov (United States)

    Irianto, D.

    2016-02-01

    Manufacturing systems involve decisions concerning production processes, capacity, planning, and control. In a MTO manufacturing systems, strategic decisions concerning fulfilment of customer requirement, manufacturing cost, and due date of delivery are the most important. In order to accelerate the decision making process, research on decision making structure when receiving order and sequencing activities under limited capacity is required. An effective decision making process is typically required by small-medium components and tools maker as supporting industries to large industries. On one side, metal small-medium enterprises are expected to produce parts, components or tools (i.e. jigs, fixture, mold, and dies) with high precision, low cost, and exact delivery time. On the other side, a metal small- medium enterprise may have weak bargaining position due to aspects such as low production capacity, limited budget for material procurement, and limited high precision machine and equipment. Instead of receiving order exclusively, a small-medium enterprise can collaborate with other small-medium enterprise in order to fulfill requirements high quality, low manufacturing cost, and just in time delivery. Small-medium enterprises can share their best capabilities to form effective supporting industries. Independent body such as community service at university can take a role as a collaboration manager. The Laboratory of Production Systems at Bandung Institute of Technology has implemented shared manufacturing systems for small-medium enterprise collaboration.

  14. Cost-effective medium for the production of mosquito pupicidal lipopeptide from Bacillus subtilis subsp. subtilis (VCRC B471).

    Science.gov (United States)

    Bhuvaneswari, S; Manonmani, A M; Geetha, I

    2015-03-01

    A cyclic lipopeptide (CLP), surfactin produced by a strain of Bacillus subtilis subsp. subtilis (VCRC B471) was found to exhibit mosquitocidal activity. The present study was carried out to enhance the surfactin level using low cost material in the production medium. Two carbon sources, glucose and common sugar, and two nitrogen sources, ammonium nitrate and soya were used in the study. Different concentrations of 'C' and 'N' sources were used in the production medium to enhance the production of surfactin. A new medium (SS7) containing 2% sugar, 6% soya and 0.5% common salt with micronutrients was designed which was found to enhance the production of surfactin. The crude mosquitocidal metabolite (CMM) produced in this medium was 3 g/l which was two times higher than that obtained using synthetic medium NYSM. The LC50 dosage of the CMM to the pupal stages of An. stephensi (2.3 μg/ml) was comparable to that obtained with CMM from the conventional medium. The newly designed cost-effective medium designated as sugar soya medium (SSM) enhanced the production of surfactin and the cost of production was estimated as [symbol: see text] 6 per litre, which is six times lesser than that of the conventional medium. Replacement of sodium chloride with cooking salt further reduced the cost of the medium.

  15. Carbon/carbon composite materials

    International Nuclear Information System (INIS)

    Thebault, J.; Orly, P.

    2006-01-01

    Carbon/carbon composites are singular materials from their components, their manufacturing process as well as their characteristics. This paper gives a global overview of these particularities and applications which make them now daily used composites. (authors)

  16. Photonic-resonant left-handed medium

    International Nuclear Information System (INIS)

    Shen Jianqi

    2006-01-01

    A new scheme to realize simultaneously negative permittivity and permeability in a coherent atomic vapor medium (photonic-resonant material) via a coherent driving mechanism is suggested. It is verified that the atomic system coherently driven by a strong optical field will give rise to a negative refractive index in certain probe frequency ranges. One of the most remarkable features of the present scheme is such that a slab fabricated by the left-handed vapor medium is an ideal candidate for designing perfect lenses since the photonic-resonant atomic vapor cannot only exhibit an isotropic negative refractive index, but also provide a good impedance match at the air-medium interfaces

  17. Physical processes in the interstellar medium

    CERN Document Server

    Spitzer, Lyman

    2008-01-01

    Physical Processes in the Interstellar Medium discusses the nature of interstellar matter, with a strong emphasis on basic physical principles, and summarizes the present state of knowledge about the interstellar medium by providing the latest observational data. Physics and chemistry of the interstellar medium are treated, with frequent references to observational results. The overall equilibrium and dynamical state of the interstellar gas are described, with discussions of explosions produced by star birth and star death and the initial phases of cloud collapse leading to star formation.

  18. Biodegradation of low-density polyethylene (LDPE) by isolated fungi in solid waste medium

    International Nuclear Information System (INIS)

    Zahra, Sahebnazar; Abbas, Shojaosadati Seyed; Mahsa, Mohammad-Taheri; Mohsen, Nosrati

    2010-01-01

    In this study, biodegradation of low-density polyethylene (LDPE) by isolated landfill-source fungi was evaluated in a controlled solid waste medium. The fungi, including Aspergillus fumigatus, Aspergillus terreus and Fusarium solani, were isolated from samples taken from an aerobic aged municipal landfill in Tehran. These fungi could degrade LDPE via the formation of a biofilm in a submerged medium. In the sterilized solid waste medium, LPDE films were buried for 100 days in a 1-L flask containing 400 g sterile solid waste raw materials at 28 deg. C. Each fungus was added to a separate flask. The moisture content and pH of the media were maintained at the optimal levels for each fungus. Photo-oxidation (25 days under UV-irradiation) was used as a pretreatment of the LDPE samples. The progress of the process was monitored by measurement of total organic carbon (TOC), pH, temperature and moisture. The results obtained from monitoring the process using isolated fungi under sterile conditions indicate that these fungi are able to grow in solid waste medium. The results of FT-IR and SEM analyses show that A. terreus and A. fumigatus, despite the availability of other organic carbon of materials, could utilize LDPE as carbon source. While there has been much research in the field of LDPE biodegradation under solid conditions, this is the first report of degradation of LDPE by A. fumigatus.

  19. Optimization of medium composition for apple rootstocks

    African Journals Online (AJOL)

    User

    2011-05-02

    May 2, 2011 ... Key words: Apple rootstocks, medium composition, multiplication rate, plant growth regulators (PGRs). ... be extrapolated with the same success for another .... Analysis System (SAS) software program (SAS Institute Inc. 1999).

  20. Jet multiplicity distributions: medium dependence in MLLA

    International Nuclear Information System (INIS)

    Armesto, Nestor; Pajares, Carlos; Quiroga-Arias, Paloma

    2009-01-01

    We study the medium dependence of the multiplicity distributions in the modified leading logarithmic approximation. We focus in the enhancement in the number of branchings as the partons travel trough a dense medium created in a heavy-ion collision. We study the effect of a higher number of splittings in some jet observables by introducing the medium as a constant (f med ) in the splitting functions. Having as our ansatz for the quark and gluon jets mean multiplicities left angle n G right angle =e γy and left angle n Q right angle =r -1 e γy , we study in an analytic approach the dependence with the medium (f med ) of the anomalous dimension (γ), the multiplicity ratio (r), and so the mean multiplicities. We also obtain the higher-order moments of the multiplicity distribution, what allows us to study its dispersion. (orig.)

  1. Optimization of medium composition for thermostable protease ...

    African Journals Online (AJOL)

    SERVER

    2008-04-17

    Apr 17, 2008 ... Optimization of the fermentation medium for maximization of thermostable neutral protease production by Bacillus sp. ..... Each contour curve represented an infinite number of combinations of two ..... Production in sea-water of.

  2. Fractional diffusion equation for heterogeneous medium

    International Nuclear Information System (INIS)

    Polo L, M. A.; Espinosa M, E. G.; Espinosa P, G.; Del Valle G, E.

    2011-11-01

    The asymptotic diffusion approximation for the Boltzmann (transport) equation was developed in 1950 decade in order to describe the diffusion of a particle in an isotropic medium, considers that the particles have a diffusion infinite velocity. In this work is developed a new approximation where is considered that the particles have a finite velocity, with this model is possible to describe the behavior in an anomalous medium. According with these ideas the model was obtained from the Fick law, where is considered that the temporal term of the current vector is not negligible. As a result the diffusion equation of fractional order which describes the dispersion of particles in a highly heterogeneous or disturbed medium is obtained, i.e., in a general medium. (Author)

  3. Small and medium power reactors 1987

    International Nuclear Information System (INIS)

    1987-12-01

    This TECDOC follows the publication of TECDOC-347 Small and Medium Power Reactors Project Initiation Study - Phase I published in 1985 and TECDOC-376 Small and Medium Power Reactors 1985 published in 1986. It is mainly intended for decision makers in Developing Member States interested in embarking on a nuclear power programme. It consists of two parts: 1) Guidelines for the Introduction of Small and Medium Power Reactors in Developing Countries. These Guidelines were established during the Advisory Group Meeting held in Vienna from 11 to 15 May 1987. Their purpose is to review key aspects relating to the introduction of Small and Medium Power Reactors in developing countries; 2) Up-dated Information on SMPR Concepts Contributed by Supplier Industries. According to the recommendations of the Second Technical Committee Meeting on SMPRs held in Vienna in March 1985, this part contains the up-dated information formerly published in Annex I of the above mentioned TECDOC-347. Figs

  4. Incompatibility of Contrast Medium and Trisodium Citrate

    International Nuclear Information System (INIS)

    Delcour, Christian; Bruninx, Guy

    2013-01-01

    To test the compatibility of trisodium citrate, a catheter lock solution, with iodinated contrast medium. Iohexol, iobitridol, iodixanol, ioxaglate, ioxithalamate, iomeprol, and iopromide were tested. In all tests, 2 ml of contrast medium were mixed with 2 ml of trisodium citrate solution. Iodixanol and ioxaglate provoked a highly viscous gluelike precipitation when mixed with trisodium citrate. A brief transient precipitate was observed with iohexol, iomeprol, and ioxithalamate. Permanent precipitation occurred with iobitridol and iopromide. One must be aware of the potential for precipitation when contrast medium is mixed with trisodium citrate solution. Before trisodium citrate solution is injected, the catheter should be thoroughly flushed with saline if a contrast medium has previously been injected through it.

  5. Study of niobium corrosion in alkaline medium

    International Nuclear Information System (INIS)

    Almeida, S.H. de.

    1987-01-01

    A comparative study of niobium electrochemical behaviour in NaOH and KOH solution, with concentrations between 0,5 and 6,1M is presented. The studies were done through electrochemicals assays, consisting in the corrosion potential and anodic and cathodic polarization curves, complemented by loss of mass experiments. The niobium anodic behaviour in alkaline medium is characterized by passivation occurrence, with a stable film formation. The Na oH solution in alkaline medium are more corrosible to niobium than the KOH solution. The loss of mass assays showed that the corrosion velocit is more dependente of hydroxide concentration in KOH medium than the NaOH medium. (C.G.C.) [pt

  6. Small and Medium Enterprises and Biopharmaceutical Innovations ...

    African Journals Online (AJOL)

    Erah

    Benin City, 300001 Nigeria. All rights ... are challenges facing African Small and Medium Enterprises (SMEs) in biopharmaceutical industry, the ... Network for Drug and Diagnostics recognizes .... functionality is in place, integration into the.

  7. Sharing perspectives on English-medium instruction

    CERN Document Server

    Ackerley, Katherine; Helm, Francesca

    2017-01-01

    This volume gives voice to the views and experiences of researchers, lecturers, administrative staff, teacher trainers and students with regard to the implementation of English-medium instruction in a public university based in the north-east of Italy.

  8. Medium Effects in Reactions with Rare Isotopes

    International Nuclear Information System (INIS)

    Bertulani, C A; Karakoç, M

    2012-01-01

    We discuss medium effects in knockout reactions with rare isotopes of weakly-bound nuclei at intermediate energies. We show that the poorly known corrections may lead to sizable modifications of knockout cross sections and momentum dsitributions.

  9. Effective medium theory principles and applications

    CERN Document Server

    Choy, Tuck C

    2015-01-01

    Effective medium theory dates back to the early days of the theory of electricity. Faraday in 1837 proposed one of the earliest models for a composite metal-insulator dielectric and around 1870 Maxwell and later Garnett (1904) developed models to describe a composite or mixed material medium. The subject has been developed considerably since and while the results are useful for predicting materials performance, the theory can also be used in a wide range of problems in physics and materials engineering. This book develops the topic of effective medium theory by bringing together the essentials of both the static and the dynamical theory. Electromagnetic systems are thoroughly dealt with, as well as related areas such as the CPA theory of alloys, liquids, the density functional theory etc., with applications to ultrasonics, hydrodynamics, superconductors, porous media and others, where the unifying aspects of the effective medium concept are emphasized. In this new second edition two further chapters have been...

  10. Small and medium power reactors 1987

    Science.gov (United States)

    1987-12-01

    This TECDOC follows the publication of TECDOC-347: Small and Medium Power Reactors (SMPR) Project Initiation Study, Phase 1, published in 1985 and TECDOC-376: Small and Medium Power Reactors 1985 published in 1986. It is mainly intended for decision makers in Developing Member States interested in embarking on a nuclear power program. It consists of two parts: (1) guidelines for the introduction of small and medium power reactors in developing countries. These Guidelines were established during the Advisory Group Meeting held in Vienna from 11 to 15 May 1987. Their purpose is to review key aspects relating to the introduction of small and medium power reactors in developing countries; (2) up-dated information on SMPR Concepts Contributed by Supplier Industries. According to the recommendations of the Second Technical Committee Meeting on SMPRs held in Vienna in March 1985, this part contains the up-dated information formerly published in Annex 1 of the above mentioned TECDOC-347.

  11. A cost effective cultivation medium for biocalcification of Bacillus pasteurii KCTC 3558 and its effect on cement cubes properties.

    Science.gov (United States)

    Yoosathaporn, S; Tiangburanatham, P; Bovonsombut, S; Chaipanich, A; Pathom-Aree, W

    2016-01-01

    Application of carbonate precipitation induced by Bacillus pasteurii for improving some properties of cement has been reported. However, it is not yet successful in commercial scale due to the high cost of cultivation medium. This is the first report on the application of effluent from chicken manure bio-gas plant, a high protein content agricultural waste, as an alternative growth medium for carbonate precipitation by B. pasteurii KCTC3558. Urease activity of B. pasteurii KCTC3558 cultured in chicken manure effluent medium and other three standard media were examined using phenate method. The highest urease production was achieved in chicken manure effluent medium (16.756Umg(-1) protein). Cost per liter of chicken manure effluent medium is up to 88.2% lower than other standard media. The most effective cultivation media was selected for carbonate precipitation study in cement cubes. Water absorption, voids, apparent density and compressive strength of cement cubes were measured according to the ASTM standard. The correlation between the increasing density and compressive strength of bacterial added cement cube was evident. The density of bacterial cement cube is 5.1% higher than control while the compressive strength of cement mixed with bacterial cells in chicken manure effluent medium increases up to 30.2% compared with control. SEM and XRD analysis also found the crystalline phase of calcium carbonate within bacterial cement which confirmed that the increasing density and compressive strength were resulted from bacterial carbonate precipitation. This study indicated that the effluent from chicken manure bio-gas plant could be used as an alternative cost effective culture medium for cultivation and biocalcification of B. pasteurii KCTC3558 in cement. Copyright © 2016. Published by Elsevier GmbH.

  12. Switching power converters medium and high power

    CERN Document Server

    Neacsu, Dorin O

    2013-01-01

    An examination of all of the multidisciplinary aspects of medium- and high-power converter systems, including basic power electronics, digital control and hardware, sensors, analog preprocessing of signals, protection devices and fault management, and pulse-width-modulation (PWM) algorithms, Switching Power Converters: Medium and High Power, Second Edition discusses the actual use of industrial technology and its related subassemblies and components, covering facets of implementation otherwise overlooked by theoretical textbooks. The updated Second Edition contains many new figures, as well as

  13. Carbon distribution in bainitic steel subjected to deformation

    Energy Technology Data Exchange (ETDEWEB)

    Ivanov, Yu. F., E-mail: yufi55@mail.ru [Institute of High Current Electronics SB RAS, Tomsk, 634055 (Russian Federation); National Research Tomsk State University, Tomsk, 634050 (Russian Federation); Nikitina, E. N., E-mail: Nikitina-EN@mail.ru; Gromov, V. E., E-mail: gromov@physics.sibsiu.ru [Siberian State Industrial University, Novokuznetsk, 654007 (Russian Federation)

    2015-10-27

    Analysis of the formation and evolution of carbide phase in medium carbon steel with a bainitic structure during compressive deformation was performed by means of transmission electron diffraction microscopy. Qualitative transformations in carbide phase medium size particles, their density and volume concentration depended on the degree of deformation.

  14. DYNAMIC DEFORMATION THE VISCOELASTIC TWOCOMPONENT MEDIUM

    Directory of Open Access Journals (Sweden)

    V. S. Polenov

    2015-01-01

    Full Text Available Summary. In the article are scope harmonious warping of the two-component medium, one component which are represent viscoelastic medium, hereditary properties which are described by the kernel aftereffect Abel integral-differential ratio BoltzmannVolterr, while second – compressible liquid. Do a study one-dimensional case. Use motion equation of two-component medium at movement. Look determination system these equalization in the form of damped wave. Introduce dimensionless coefficient. Combined equations happen to homogeneous system with complex factor relatively waves amplitude in viscoelastic component and in fluid. As a result opening system determinant receive biquadratic equation. Elastic operator express through kernel aftereffect Abel for space Fourier. With the help transformation and symbol series biquadratic equation reduce to quadratic equation. Come to the conclusion that in two-component viscoelastic medium exist two mode sonic waves. As a result solution of quadratic equation be found description advance of waves sonic in viscoelastic two-component medium, which physical-mechanical properties represent complex parameter. Velocity determination advance of sonic waves, attenuation coefficient, mechanical loss tangent, depending on characteristic porous medium and circular frequency formulas receive. Graph dependences of description advance of waves sonic from the temperature logarithm and with the fractional parameter γ are constructed.

  15. Selective medium for culture of Mycoplasma hyopneumoniae.

    Science.gov (United States)

    Cook, Beth S; Beddow, Jessica G; Manso-Silván, Lucía; Maglennon, Gareth A; Rycroft, Andrew N

    2016-11-15

    The fastidious porcine respiratory pathogen Mycoplasma hyopneumoniae has proven difficult to culture since it was first isolated in 1965. A reliable solid medium has been particularly challenging. Moreover, clinical and pathological samples often contain the fast-growing M. hyorhinis which contaminates and overgrows M. hyopneumoniae in primary culture. The aim of this study was to optimise the culture medium for recovery of M. hyopneumoniae and to devise a medium for selection of M. hyopneumoniae from clinical samples also containing M. hyorhinis. The solid medium devised by Niels Friis was improved by use of Purified agar and incorporation of DEAE-dextran. Addition of glucose or neutralization of acidity in liquid medium with NaOH did not improve the final yield of viable organisms or alter the timing of peak viability. Analysis of the relative susceptibility of M. hyopneumoniae and M. hyorhinis strains to four antimicrobials showed that M. hyopneumoniae is less susceptible than M. hyorhinis to kanamycin. This was consistent in all UK and Danish strains tested. A concentration of 2μg/ml of kanamycin selectively inhibited the growth of all M. hyorhinis tested, while M. hyopneumoniae was able to grow. This forms the basis of an effective selective culture medium for M. hyopneumoniae. Copyright © 2016 The Authors. Published by Elsevier B.V. All rights reserved.

  16. Reaction of titanium polonides with carbon dioxide

    International Nuclear Information System (INIS)

    Abakumov, A.S.; Malyshev, M.L.; Reznikova, N.F.

    1987-01-01

    It has been ascertained that heating titanium and tantalum in carbon dioxide to temperatures of 500 or 800 0 C alters the composition of the gas phase, causing the advent of carbon monoxide and lowering the oxygen content. Investigation of the thermal stability of titanium polonides in a carbon dioxide medium has shown that titanium mono- and hemipolonides are decomposed at temperatures below 350 0 C. The temperature dependence of the vapor pressure of polonium produced in the decomposition of these polonides in a carbon dioxide medium have been determined by a radiotensimetric method. The enthalpy of the process, calculated from this relationship, is close to the enthalpy of vaporization of elementary polonium in vacuo

  17. Organic complexing agents in low and medium level radioactive waste

    International Nuclear Information System (INIS)

    Allard, B.; Persson, G.

    1985-11-01

    Low and medium level radioactive wastes will contain various organic agents, such as ion exchange resins (mainly in the operational wastes), plastics and cellulose (mainly in the reprocessing wastes and in the decommissioning wastes) and bitumen (mainly in the reprocessing wastes). The degradation of these organics will lead to the formation of complexing agents that possibly could affect the release of radionuclides from an underground repository and the subsequent transport of these nuclides. The solution chemistry of the actinides may be totally dominated by the presence of such organic degradation products within the repository. However, hydrolysis and formation of carbonates (and possibly humates) will most likely dominate solubility and speciation outside the immediate vicinity of the repository. The minor quantities of strong complexing agents (in the reprocessing waste), notably aminopolycarboxylic acids (EDTA, DTPA) and possibly organic phosphates (DBP) could significantly affect speciation and sorption behaviour of primarily the trivalent actinides even outside the repository. (author)

  18. Influence of medium components on the expression of recombinant lipoproteins in Escherichia coli.

    Science.gov (United States)

    Tseng, Chi-Ling; Leng, Chih-Hsiang

    2012-02-01

    Bacterial lipoproteins are crucial antigens for protective immunity against bacterial pathogens. Expression of exogenous lipoproteins in Escherichia coli at high levels is thought to be an extremely difficult endeavor because it frequently results in incomplete or absent lipid modification. Previously, we identified a fusion sequence (D1) from a Neisseria meningitidis lipoprotein that induced a non-lipidated protein, E3 (the domain III of the dengue virus envelope protein), to become lipidated. However, without optimizing the growth conditions, some of the D1-fusion proteins were not lipidated. Here, we report the influence of medium components on the expression of recombinant lipoproteins in E. coli. For high-level expression of mature lipoproteins in the C43 (DE3) strain, M9 medium was better than M63 and the rich medium. Furthermore, we analyzed the influence of other media factors (including nitrogen and carbon sources, phosphate, ferrous ions, calcium, magnesium, and pH) on the levels of lipoprotein expression. The results showed that excess nitrogen sources and phosphate in M9 medium could increase the amount of immature lipoproteins, and glucose was a better carbon source than glycerol for expressing mature lipoproteins. We also found that lipoproteins tended to be completely processed in the alkaline environment, even in the nutrient-rich medium. Additional constructs expressing different immunogens or lipid signal peptides as targets were also utilized, demonstrating that these targets could be expressed as completely mature lipoproteins in the M9 medium but not in the rich medium. Our results provide the useful information for expressing mature exogenous lipoproteins in E. coli.

  19. Carbonate aquifers

    Science.gov (United States)

    Cunningham, Kevin J.; Sukop, Michael; Curran, H. Allen

    2012-01-01

    Only limited hydrogeological research has been conducted using ichnology in carbonate aquifer characterization. Regardless, important applications of ichnology to carbonate aquifer characterization include its use to distinguish and delineate depositional cycles, correlate mappable biogenically altered surfaces, identify zones of preferential groundwater flow and paleogroundwater flow, and better understand the origin of ichnofabric-related karst features. Three case studies, which include Pleistocene carbonate rocks of the Biscayne aquifer in southern Florida and Cretaceous carbonate strata of the Edwards–Trinity aquifer system in central Texas, demonstrate that (1) there can be a strong relation between ichnofabrics and groundwater flow in carbonate aquifers and (2) ichnology can offer a useful methodology for carbonate aquifer characterization. In these examples, zones of extremely permeable, ichnofabric-related macroporosity are mappable stratiform geobodies and as such can be represented in groundwater flow and transport simulations.

  20. The origin of carbon revisited: winds of carbon-stars

    International Nuclear Information System (INIS)

    Mattsson, L

    2008-01-01

    Chemical evolution models, differing in the nucleosynthesis prescriptions (yields) for carbon, nitrogen and oxygen, have been computed for the Milky Way and Andromeda (NGC 224). All models fit the observed O/H gradients well and reproduce the main characteristics of the gas distributions, but they are also designed to do so. The N/O gradient for NGC 224 cannot be reproduced without ad hoc modifications to the yields and a similar result is obtained for the Milky Way N/O gradient, although in the latter case the slopes of the gradients obtained with unmodified yields are consistent with the observed gradient. For the C/O gradients (obtained from B stars) the results are inconclusive. The C/Fe, N/Fe, O/Fe versus Fe/H, as well as C/O versus O/H trends predicted by the models for the solar neighbourhood were compared with stellar abundances from the literature. For O/Fe versus Fe/H, all models fit the data, but for C/Fe, N/Fe versus Fe/H and C/O versus O/H, only modified sets of yields provide good fits. Since in the best-fit model, the yields were modified such that carbon should be primarily produced in low-mass stars, it is quite possible that in every environment where the peak of star formation happened a few Gyr back in time, the winds of carbon stars are responsible for most of the carbon enrichment, although models with a significant contribution from high-mass stars cannot be ruled out. In the solar neighbourhood, almost two-thirds of the carbon in the interstellar medium may come from carbon stars. Finally, the challenges met by stellar evolution and nucleosynthesis modelling due to this 'carbon star hypothesis' for the origin of carbon are discussed. It is suggested that a mass-loss prescription where the mass-loss rate depends on the carbon excess may act as a self-regulating mechanism for how much carbon a carbon star can deliver to the interstellar medium.

  1. Carbon Nanotubes and Modern Nanoagriculture

    KAUST Repository

    Serag, Maged F.

    2015-01-27

    Since their discovery, carbon nanotubes have been prominent members of the nanomaterial family. Owing to their extraordinary physical, chemical, and mechanical properties, carbon nanotubes have been proven to be a useful tool in the field of plant science. They were frequently perceived to bring about valuable biotechnological and agricultural applications that still remain beyond experimental realization. An increasing number of studies have demonstrated the ability of carbon nanotubes to traverse different plant cell barriers. These studies, also, assessed the toxicity and environmental impacts of these nanomaterials. The knowledge provided by these studies is of practical and fundamental importance for diverse applications including intracellular labeling and imaging, genetic transformation, and for enhancing our knowledge of plant cell biology. Although different types of nanoparticles have been found to activate physiological processes in plants, carbon nanotubes received particular interest. Following addition to germination medium, carbon nanotubes enhanced root growth and elongation of some plants such as onion, cucumber and rye-grass. They, also, modulated the expression of some genes that are essential for cell division and plant development. In addition, multi-walled carbon nanotubes were evidenced to penetrate thick seed coats, stimulate germination, and to enhance growth of young tomato seedlings. Multi-walled carbon nanotubes can penetrate deeply into the root system and further distribute into the leaves and the fruits. In recent studies, carbon nanotubes were reported to be chemically entrapped into the structure of plant tracheary elements. This should activate studies in the fields of plant defense and wood engineering. Although, all of these effects on plant physiology and plant developmental biology have not been fully understood, the valuable findings promises more research activity in the near future toward complete scientific understanding of

  2. Evaluation of sugar yeast consumption by measuring electrical medium resistance

    Directory of Open Access Journals (Sweden)

    Martin Lucas Zamora

    2013-12-01

    Full Text Available The real-time monitoring of alcoholic fermentation (sugar consumption is very important in industrial processes. Several techniques (i.e., using a biosensor have been proposed to realize this goal. In this work, we propose a new method to follow sugar yeast consumption. This novel method is based on the changes in the medium resistance (Rm that are induced by the CO2 bubbles produced during a fermentative process. We applied a 50-mV and 700-Hz signal to 75 ml of a yeast suspension in a tripolar cell. A gold electrode was used as the working electrode, whereas an Ag/AgCl electrode and a stainless-steel electrode served as the reference and counter electrodes, respectively. We then added glucose to the yeast suspension and obtained a 700% increase in the Rm after 8 minutes. The addition of sucrose instead of glucose as the carbon source resulted in a 1200% increase in the Rm. To confirm that these changes are the result of CO2 bubbles in the fermentation medium, we designed a tetrapolar cell in which CO2 gas was insufflated at the bottom of the cell and concluded that the changes were due to CO2 bubbles produced during the fermentation. Consequently, this new method is a low-cost and rapid technology to follow the sugar consumption in yeast.

  3. Overview of medium heterogeneity and transport processes

    International Nuclear Information System (INIS)

    Tsang, Y.; Tsang, C.F.

    1993-11-01

    Medium heterogeneity can have significant impact on the behavior of solute transport. Tracer breakthrough curves from transport in a heterogeneous medium are distinctly different from that in a homogeneous porous medium. Usually the shape of the breakthrough curves are highly non-symmetrical with a fast rise at early times and very long tail at late times, and often, they consist of multiple peaks. Moreover, unlike transport in a homogeneous medium where the same transport parameters describe the entire medium, transport through heterogeneous media gives rise to breakthrough curves which have strong spatial dependence. These inherent characteristics of transport in heterogeneous medium present special challenge to the performance assessment of a potential high level nuclear waste repository with respect to the possible release of radio nuclides to the accessible environment. Since an inherently desirable site characteristic for a waste repository is that flow and transport should be slow, then transport measurements in site characterization efforts will necessarily be spatially small and temporally short compare to the scales which are of relevance to performance assessment predictions. In this paper we discuss the role of medium heterogeneity in site characterization and performance assessment. Our discussion will be based on a specific example of a 3D heterogeneous stochastic model of a site generally similar to, the Aespoe Island, the site of the Hard Rock Laboratory in Southern Sweden. For our study, alternative 3D stochastic fields of hydraulic conductivities conditioned on ''point'' measurements shall be generated. Results of stochastic flow and transport simulations would be used to address the issues of (1) the relationship of tracer breakthrough with the structure of heterogeneity, and (2) the inference from small scale testing results to large scale and long term predictions

  4. Optimization of culture conditions and medium composition for the production of micrococcin GO5 by Micrococcus sp. GO5.

    Science.gov (United States)

    Kim, Mi-Hee; Kong, Yoon-Jung; Baek, Hong; Hyun, Hyung-Hwan

    2006-01-02

    To enhance the production of micrococcin GO5, a bacteriocin produced by Micrococcus sp. GO5, cultivation conditions and medium composition were optimized. The optimal initial pH and temperature for bacteriocin production were 7.0-9.0 and 37 degrees C, respectively. Micrococcus sp. GO5 displayed the highest micrococcin GO5 activity when grown in modified MRS medium that contained lactose or sucrose, rather than glucose, as a carbon source. The maximum bacteriocin activity was obtained in modified MRS medium containing 0.5% tryptone and 1.0% yeast extract as nitrogen sources instead of the other nitrogen sources present in MRS medium. Bacteriocin production was greatly affected by the concentration of K(2)HPO(4); strain GO5 produced eight-fold more bacteriocin in medium containing 2.0-2.5% K(2)HPO(4) than in medium containing 0.2% K(2)HPO(4). The optimal concentration of MgSO(4).7H(2)O for bacteriocin production was 0.5%. The production of micrococcin GO5 was increased 32-fold in shake flask culture and 16-fold in a bioreactor using the optimized medium (TY medium), compared with culturing in MRS medium.

  5. Evaluation of Insulin Medium or Chondrogenic Medium on Proliferation and Chondrogenesis of ATDC5 Cells

    OpenAIRE

    Yao, Yongchang; Zhai, Zhichen; Wang, Yingjun

    2014-01-01

    Background. The ATDC5 cell line is regarded as an excellent cell model for chondrogenesis. In most studies with ATDC5 cells, insulin medium (IM) was used to induce chondrogenesis while chondrogenic medium (CM), which was usually applied in chondrogenesis of mesenchymal stem cells (MSCs), was rarely used for ATDC5 cells. This study was mainly designed to investigate the effect of IM, CM, and growth medium (GM) on chondrogenesis of ATDC5 cells. Methods. ATDC5 cells were, respectively, cultured ...

  6. 'That proves my point': How mediums reconstrue disconfirmation in medium-sitter interactions.

    Science.gov (United States)

    Enoksen, Anette Einan; Dickerson, Paul

    2018-04-01

    Previous research has examined how the talk of mediums attends to the epistemological status of their readings. Such work has identified that mediums frequently use question-framed propositions that are typically confirmed by the sitter, thereby conferring epistemological status on the medium. This study seeks to investigate what happens when the sitter disconfirms the propositions of the medium. The study focuses on the ways in which such disconfirmation can be responded to such that it is reconstrued as evidence of the psychic nature of the medium's reading. Televised demonstrations of psychic readings involving British and US mediums and their sitters are analysed. The results suggest that mediums rework disconfirmation as proof in several ways: first, by emphasizing the different access that sitter and medium have to knowledge (e.g., about the future); second, as evidence that the medium has access to the actual voice of the deceased (and may therefore mishear what the deceased has said to them); and third, as revealing an important truth that has hitherto been concealed from the sitter. The implications of these findings are considered for cases where speakers bring different and potentially competing, epistemological resources to an interaction. © 2018 The British Psychological Society.

  7. Biosynthesis of glycerol carbonate from glycerol by lipase in dimethyl carbonate as the solvent.

    Science.gov (United States)

    Lee, Kyung Hwa; Park, Chang-Ho; Lee, Eun Yeol

    2010-11-01

    Glycerol carbonate was synthesized from renewable glycerol and dimethyl carbonate using lipase in solvent-free reaction system in which excess dimethyl carbonate played as the reaction medium. A variety of lipases have been tested for their abilities to catalyze transesterification reaction, and Candida antartica lipase B and Novozyme 435 exhibited higher catalytic activities. The silica-coated glycerol with a 1:1 ratio was supplied to prevent two-phase formation between hydrophobic dimethyl carbonate and hydrophilic glycerol. Glycerol carbonate was successfully synthesized with more than 90% conversion from dimethyl carbonate and glycerol with a molar ratio of 10 using Novozyme 435-catalyzed transesterification at 70 °C. The Novozyme 435 [5% (w/w) and 20% (w/w)] and silica gel were more than four times recycled with good stability in a repeated batch operation for the solvent-free synthesis of glycerol carbonate.

  8. CHROMagar Orientation Medium Reduces Urine Culture Workload

    Science.gov (United States)

    Manickam, Kanchana; Karlowsky, James A.; Adam, Heather; Lagacé-Wiens, Philippe R. S.; Rendina, Assunta; Pang, Paulette; Murray, Brenda-Lee

    2013-01-01

    Microbiology laboratories continually strive to streamline and improve their urine culture algorithms because of the high volumes of urine specimens they receive and the modest numbers of those specimens that are ultimately considered clinically significant. In the current study, we quantitatively measured the impact of the introduction of CHROMagar Orientation (CO) medium into routine use in two hospital laboratories and compared it to conventional culture on blood and MacConkey agars. Based on data extracted from our Laboratory Information System from 2006 to 2011, the use of CO medium resulted in a 28% reduction in workload for additional procedures such as Gram stains, subcultures, identification panels, agglutination tests, and biochemical tests. The average number of workload units (one workload unit equals 1 min of hands-on labor) per urine specimen was significantly reduced (P < 0.0001; 95% confidence interval [CI], 0.5326 to 1.047) from 2.67 in 2006 (preimplementation of CO medium) to 1.88 in 2011 (postimplementation of CO medium). We conclude that the use of CO medium streamlined the urine culture process and increased bench throughput by reducing both workload and turnaround time in our laboratories. PMID:23363839

  9. Enhancement of docosahexaenoic acid (DHA) production from Schizochytrium sp. S31 using different growth medium conditions.

    Science.gov (United States)

    Sahin, Deniz; Tas, Ezgi; Altindag, Ulkü Hüma

    2018-01-24

    Schizochytrium species is one of the most studied microalgae for production of docosahexaenoic acid (DHA) which is an omega-3 fatty acid with positive effects for human health. However, high cost and low yield in production phase makes optimization of cultivation process inevitable. We focus on the optimization of DHA production using Schizochytrium sp. using different media supplements; glucose, fructose and glycerol as carbon variants, proteose peptone and tryptone as nitrogen variants. The highest biomass (5.61 g/L) and total fatty acid yield (1.74 g/L) were obtained in proteose peptone medium which was used as the alternative nitrogen source instead of yeast extract. The highest DHA yield (0.40 g/L) was achieved with glycerol as the carbon source although it had the second lowest biomass production after ethanol containing medium. Ethanol, as an alternative carbon source and a precursor for acetyl-CoA, increased DHA percentage in total lipid content from 29.94 to 40.04% but decreasing the biomass drastically. Considering different carbon and nitrogen sources during cultivation of Schizochytrium sp. will improve DHA production. Combination of proteose peptone and glycerol as nitrogen and carbon sources, respectively, and addition of ethanol with a proper timing will be useful to have higher DHA yield.

  10. Environmental variables evaluation on concrete structures corrosion for medium level activities repositories

    International Nuclear Information System (INIS)

    Requena, Carlos; Alvarez, Marta G.; Duffo, Gustavo S.

    2000-01-01

    The main purpose of this work was to evaluate the long term durability of reinforced concrete structures as medium-level waste container material. Electrochemical techniques have been used to evaluate the corrosion behaviour of steel rebars in several solutions simulating the liquid present in the pores of both alkaline and carbonated concrete in the presence of sulphate ions. Results shown that a decrease in p H has an adverse effect on the critical sulphate concentration. The inhibition effect of high carbonate/bicarbonate concentration is also shown. (author)

  11. The K{sup +} as a probe of nuclear medium effects

    Energy Technology Data Exchange (ETDEWEB)

    Chrien, R.E.

    1992-09-01

    The study of the K+ total cross sections on a wide range of nuclei has revealed important modifications of the free-space K+ -nucleon interaction when the nucleon is embedded in a nucleus. In addition to the previously published data on carbon and deuterium we report here the extension of such measurements to lithium, silicon, and calcium. We demonstrate that the previous reported medium modifications for carbon occur quite generally. The results are discussed as evidence for partial quark deconfinement at nuclear densities.

  12. Experimental parameters for quantitative surface analysis by medium energy ion scattering, ch. 1

    International Nuclear Information System (INIS)

    Turkenburg, W.C.; Kersten, H.H.; Colenbrander, B.G.; Jongh, A.P. de; Saris, F.W.

    1976-01-01

    A new UHV chamber for surface and surface layer analysis by collision spectroscopy of backscattered ions at medium energies is described. Experimental parameters like energy, angular and depth resolution, crystal alignment and background pressure are discussed. Formulae based on the use of an electrostatic energy analyser show that the analysis can be quantitative. Effects of beam induced build-up of a hydro-carbon layer, sputter cleaning and creation of radiation damage have been investigated for Cu (110) and Ni (110). Detection sensitivity for Carbon, Oxygen and Sulfur on Cu and Ni has been found to be 0.2, 0.1 and 0.03 of a monolayer respectively

  13. Carbon-On-Carbon Manufacturing

    Science.gov (United States)

    Mungas, Gregory S. (Inventor); Buchanan, Larry (Inventor); Banzon, Jr., Jose T. (Inventor)

    2017-01-01

    The presently disclosed technology relates to carbon-on-carbon (C/C) manufacturing techniques and the resulting C/C products. One aspect of the manufacturing techniques disclosed herein utilizes two distinct curing operations that occur at different times and/or using different temperatures. The resulting C/C products are substantially non-porous, even though the curing operation(s) substantially gasify a liquid carbon-entrained filler material that saturates a carbon fabric that makes up the C/C products.

  14. Porous carbons

    Indian Academy of Sciences (India)

    R. Narasimhan (Krishtel eMaging) 1461 1996 Oct 15 13:05:22

    Abstract. Carbon in dense as well as porous solid form is used in a variety of applications. Activated porous carbons are made through pyrolysis and activation of carbonaceous natural as well as synthetic precursors. Pyrolysed woods replicate the structure of original wood but as such possess very low surface areas and ...

  15. Carbon photonics

    Energy Technology Data Exchange (ETDEWEB)

    Konov, V I [A M Prokhorov General Physics Institute, Russian Academy of Sciences, Moscow (Russian Federation)

    2015-11-30

    The properties of new carbon materials (single-crystal and polycrystalline CVD diamond films and wafers, single-wall carbon nanotubes and graphene) and the prospects of their use as optical elements and devices are discussed. (optical elements of laser devices)

  16. Hadrons in hot and dense medium

    International Nuclear Information System (INIS)

    Mallik, S.

    2004-01-01

    We review chiral perturbation theory in some detail and construct interaction terms involving the Goldstone and the different non-Goldstone fields, in presence of external (classical) fields coupled to currents. The ensemble average of the two-point functions of the currents can now be expanded in terms of Feynman diagrams. We evaluate the one-loop diagrams in the neighbourhood of the respective poles to find the effective couplings and masses of the particles in medium. We also describe the virial formula for the self-energy of a particle in medium, giving its pole position. It proves useful if the scattering amplitude of the particle with particles in medium is known experimentally. (author)

  17. Charmonium propagation through a dense medium

    Directory of Open Access Journals (Sweden)

    Kopeliovich B.Z.

    2015-01-01

    Full Text Available Attenuation of a colourless c̄c dipole propagating with a large momentum through a hot medium originates from two sources, Debye screening (melting, and inelastic collisions with surrounding scattering centres (absorption. The former never terminates completely production of a bound charmonium in heavy ion collisions, even at very high temperatures. The latter, is controlled my the magnitude of the dipole cross section, related to the transport coefficient, which is the rate of transverse momentum broadening in the medium. A novel procedure of Lorentz boosting of the Schrödinger equation is developed, which allows to calculate the charmonium survival probability employing the path-integral technique, incorporating both melting and absorption. A novel mechanism of charmonium regeneration in a dense medium is proposed.

  18. Coherent neutrino interactions in a dense medium

    International Nuclear Information System (INIS)

    Kiers, K.; Weiss, N.

    1997-01-01

    Motivated by the effect of matter on neutrino oscillations (the MSW effect) we study in more detail the propagation of neutrinos in a dense medium. The dispersion relation for massive neutrinos in a medium is known to have a minimum at nonzero momentum p∼G F ρ/√(2). We study in detail the origin and consequences of this dispersion relation for both Dirac and Majorana neutrinos both in a toy model with only neutral currents and a single neutrino flavor and in a realistic open-quotes standard modelclose quotes with two neutrino flavors. We find that for a range of neutrino momenta near the minimum of the dispersion relation, Dirac neutrinos are trapped by their coherent interactions with the medium. This effect does not lead to the trapping of Majorana neutrinos. copyright 1997 The American Physical Society

  19. Temperature distribution in a uniformly moving medium

    International Nuclear Information System (INIS)

    Mitchell, Joseph D; Petrov, Nikola P

    2009-01-01

    We apply several physical ideas to determine the steady temperature distribution in a medium moving with uniform velocity between two infinite parallel plates. We compute it in the coordinate frame moving with the medium by integration over the 'past' to account for the influence of an infinite set of instantaneous point sources of heat in past moments as seen by an observer moving with the medium. The boundary heat flux is simulated by appropriately distributed point heat sources on the inner side of an adiabatically insulating boundary. We make an extensive use of the Green functions with an emphasis on their physical meaning. The methodology used in this paper is of great pedagogical value as it offers an opportunity for students to see the connection between powerful mathematical techniques and their physical interpretation in an intuitively clear physical problem. We suggest several problems and a challenging project that can be easily incorporated in undergraduate or graduate courses

  20. Graphene wire medium: Homogenization and application

    DEFF Research Database (Denmark)

    Andryieuski, Andrei; Chigrin, Dmitry N.; Lavrinenko, Andrei

    2012-01-01

    In this contribution we analyze numerically the optical properties of the graphene wire medium, which unit cell consists of a stripe of graphene embedded into dielectric. We propose a simple method for retrieval of the isofrequency contour and effective permittivity tensor. As an example of the g......In this contribution we analyze numerically the optical properties of the graphene wire medium, which unit cell consists of a stripe of graphene embedded into dielectric. We propose a simple method for retrieval of the isofrequency contour and effective permittivity tensor. As an example...... of the graphene wire medium application we demonstrate a reconfigurable hyperlens for the terahertz subwavelength imaging capable of resolving two sources with separation λ0/5 in the far-field....

  1. Small and medium size nuclear reactors

    International Nuclear Information System (INIS)

    Al-Mugrabi, M.A.

    1996-01-01

    The purpose of this appendix is to provide up-to-date technical information relevant to the deployment of small and medium reactors (SMRs). It summarizes the status of SMRs and discusses areas of relevance to their utilization, including seawater desalination; and in particular their simplicity, their flexibility for a variety of applications and the use of passive safety features as fundamental to most of these designs. In response to important commercial developments, the energy range of small and medium reactors is now taken as being up to around 700 MW(e). Detailed information on SMR designs can be found in the IAEA report on The Design and Development Status of Small and Medium Reactor Systems 1995. 5 refs, 2 figs, 1 tab

  2. Control of optical transport parameters of 'porous medium – supercritical fluid' systems

    Energy Technology Data Exchange (ETDEWEB)

    Zimnyakov, D A; Ushakova, O V; Yuvchenko, S A [Yuri Gagarin State Technical University of Saratov, Saratov (Russian Federation); Bagratashvili, V N [M. V. Lomonosov Moscow State University, Moscow (Russian Federation)

    2015-11-30

    The possibility of controlling optical transport parameters (in particular, transport scattering coefficient) of porous systems based on polymer fibres, saturated with carbon dioxide in different phase states (gaseous, liquid and supercritical) has been experimentally studied. An increase in the pressure of the saturating medium leads to a rise of its refractive index and, correspondingly, the diffuse-transmission coefficient of the system due to the decrease in the transport scattering coefficient. It is shown that, in the case of subcritical saturating carbon dioxide, the small-angle diffuse transmission of probed porous layers at pressures close to the saturated vapour pressure is determined by the effect of capillary condensation in pores. The immersion effect in 'porous medium – supercritical fluid' systems, where the fluid pressure is used as a control parameter, is considered. The results of reconstructing the values of transport scattering coefficient of probed layers for different refractive indices of a saturating fluid are presented. (radiation scattering)

  3. Preparation, physical-chemical characterisation and cytocompatibility of calcium carbonate cements

    OpenAIRE

    Combes, Christèle; Miao, Baoji; Bareille, Reine; Rey, Christian

    2006-01-01

    The feasibility of calcium carbonate cements involving the recrystallisation of metastable calcium carbonate varieties has been demonstrated. Calcium carbonate cement compositions presented in this paper can be prepared straightforwardly by simply mixing water (liquid phase) with two calcium carbonate phases (solid phase) which can be easily obtained by precipitation. An original cement composition was obtained by mixing amorphous calcium carbonate and vaterite with an aqueous medium. The cem...

  4. H2 molecules and the intercloud medium

    International Nuclear Information System (INIS)

    Hill, J.K.; Hollenbach, D.J.

    1976-01-01

    We discuss expected column of densities of H 2 in the intercloud medium and the possible use of molecules as indicators of intercloud physical conditions. We treat molecule formation by the H - process and on graphite grains and show that the Barlow-Silk hypothesis of a 1 eV semichemical hydrogen-graphite bond leads to a large enhancement of the intercloud molecule formation rate. Rotational excitation calculations are presented for both cloud and intercloud conditions which show, in agreement with Jura, that the presently observed optically thin H 2 absorption components are more likely to originate in cold clouds than in the intercloud medium

  5. Medium for Children’s Creativity

    DEFF Research Database (Denmark)

    Borum, Nanna; Kristensen, Kasper; Petersson, Eva

    2014-01-01

    This paper reports on an exploratory study that investigates 16 elementary school children’s interaction with two different mediums for creativity, LEGO® bricks and paper collages, drawing on the previous creativity assessment test carried out by Amabile [1]. The study is based in a playful...... on labor when working with LEGO bricks. It was also evident that the children assigned preconceived affordances to the two mediums. The results from this study should feed into to a technology enhanced playful learning environment and these are the initial steps in the design process....

  6. Heavy quark energy loss in nuclear medium

    International Nuclear Information System (INIS)

    Zhang, Benr-Wei; Wang, Enke; Wang, Xin-Nian

    2003-01-01

    Multiple scattering, modified fragmentation functions and radiative energy loss of a heavy quark propagating in a nuclear medium are investigated in perturbative QCD. Because of the quark mass dependence of the gluon formation time, the medium size dependence of heavy quark energy loss is found to change from a linear to a quadratic form when the initial energy and momentum scale are increased relative to the quark mass. The radiative energy loss is also significantly suppressed relative to a light quark due to the suppression of collinear gluon emission by a heavy quark

  7. Power converters for medium voltage networks

    CERN Document Server

    Islam, Md Rabiul; Zhu, Jianguo

    2014-01-01

    This book examines a number of topics, mainly in connection with advances in semiconductor devices and magnetic materials and developments in medium and large-scale renewable power plant technologies, grid integration techniques and new converter topologies, including advanced digital control systems for medium-voltage networks. The book's individual chapters provide an extensive compilation of fundamental theories and in-depth information on current research and development trends, while also exploring new approaches to overcoming some critical limitations of conventional grid integration te

  8. Structure and evolution of the interstellar medium

    International Nuclear Information System (INIS)

    Chieze, J.P.

    1985-10-01

    We give a two dimensional hydrodynamical analysis of HI clouds collisions in order to determine the mass spectrum of diffuse interstellar clouds. We have taken into account evaporation and abrasion by supernovae blast waves. The conditions for cloud merging or fragmentation are precised. Applications to the model of the interstellar medium of Mc Kee and Ostriker are also discussed. On the other hand, we show that molecular clouds belong to a one parameter family which can be identified to the sequence of the gravitationally unstable states of clouds bounded by the uniform pressure of the coronal phase of the interstellar medium. Hierarchical fragmentation of molecular clouds is analysed in this context [fr

  9. Medium-chain fatty acids undergo elongation before β-oxidation in fibroblasts

    International Nuclear Information System (INIS)

    Jones, Patricia M.; Butt, Yasmeen; Messmer, Bette; Boriak, Richard; Bennett, Michael J.

    2006-01-01

    Although mitochondrial fatty acid β-oxidation (FAO) is considered to be well understood, further elucidation of the pathway continues through evaluation of patients with FAO defects. The FAO pathway can be examined by measuring the 3-hydroxy-fatty acid (3-OHFA) intermediates. We present a unique finding in the study of this pathway: the addition of medium-chain fatty acids to the culture media of fibroblasts results in generation of 3-OHFAs which are two carbons longer than the precursor substrate. Cultured skin fibroblasts from normal and LCHAD-deficient individuals were grown in media supplemented with various chain-length fatty acids. The cell-free medium was analyzed for 3-OHFAs by stable-isotope dilution gas-chromatography/mass-spectrometry. Our finding suggests that a novel carbon chain-length elongation process precedes the oxidation of medium-chain fatty acids. This previously undescribed metabolic step may have important implications for the metabolism of medium-chain triglycerides, components in the dietary treatment of a number of disorders

  10. Optimizing culture medium for debittering constitutive enzyme ...

    African Journals Online (AJOL)

    STORAGESEVER

    2010-08-02

    Aug 2, 2010 ... naringinase on different matrices has been studied by many researchers (Busto et ... 10 g/L in the base medium compared to naringin control. Nitrogen ... Fermentation experiments were carried out in shaking flask for 5 days at 28°C with initial pH 6.0. † Values ..... fujikuroi mycelium in fluidized bioreactors.

  11. Jet multiplicity distributions: medium dependence in MLLA

    Energy Technology Data Exchange (ETDEWEB)

    Armesto, Nestor; Pajares, Carlos; Quiroga-Arias, Paloma [Universidade de Santiago de Compostela, Departamento de Fisica de Particulas and IGFAE, Santiago de Compostela (Spain)

    2009-07-15

    We study the medium dependence of the multiplicity distributions in the modified leading logarithmic approximation. We focus in the enhancement in the number of branchings as the partons travel trough a dense medium created in a heavy-ion collision. We study the effect of a higher number of splittings in some jet observables by introducing the medium as a constant (f{sub med}) in the splitting functions. Having as our ansatz for the quark and gluon jets mean multiplicities left angle n{sub G} right angle =e{sup {gamma}}{sup y} and left angle n{sub Q} right angle =r{sup -1}e{sup {gamma}}{sup y}, we study in an analytic approach the dependence with the medium (f{sub med}) of the anomalous dimension ({gamma}), the multiplicity ratio (r), and so the mean multiplicities. We also obtain the higher-order moments of the multiplicity distribution, what allows us to study its dispersion. (orig.)

  12. Wave propagation in thermoelastic saturated porous medium

    Indian Academy of Sciences (India)

    the existence and propagation of four waves in the medium. Three of the waves are ... predicted infinite speed for propagation of ther- mal signals. Lord and ..... saturated reservoir rock (North-sea Sandstone) is chosen for the numerical model ...

  13. Innovation in Small and Medium Firms.

    Science.gov (United States)

    Organisation for Economic Cooperation and Development, Paris (France). Committee for Scientific and Technical Personnel.

    A study analyzed the policies of 20 Organisation for Economic Cooperation and Development (OECD) member countries pertaining to small and medium enterprises (SMEs). Aims of the study were to assess the current role of SMEs as generators and users of innovations, to analyze the components of a favorable climate for innovation in SMEs, and to…

  14. The MIRI Medium Resolution Spectrometer calibration pipeline

    NARCIS (Netherlands)

    Labiano, A.; Azzollini, R.; Bailey, J.; Beard, S.; Dicken, D.; García-Marín, M.; Geers, V.; Glasse, A.; Glauser, A.; Gordon, K.; Justtanont, K.; Klaassen, P.; Lahuis, F.; Law, D.; Morrison, J.; Müller, M.; Rieke, G.; Vandenbussche, B.; Wright, G.

    2016-01-01

    The Mid-Infrared Instrument (MIRI) Medium Resolution Spectrometer (MRS) is the only mid-IR Integral Field Spectrometer on board James Webb Space Telescope. The complexity of the MRS requires a very specialized pipeline, with some specific steps not present in other pipelines of JWST instruments,

  15. Separation medium containing thermally exfoliated graphite oxide

    Science.gov (United States)

    Prud'homme, Robert K. (Inventor); Aksay, Ilhan A. (Inventor); Herrera-Alonso, Margarita (Inventor)

    2012-01-01

    A separation medium, such as a chromatography filling or packing, containing a modified graphite oxide material, which is a thermally exfoliated graphite oxide with a surface area of from about 300 m.sup.2/g to 2600 m.sup.2/g, wherein the thermally exfoliated graphite oxide has a surface that has been at least partially functionalized.

  16. Radiculography with water-soluble contraste medium

    International Nuclear Information System (INIS)

    Araujo Pinheiro, R.S. de

    1987-01-01

    The etiologic diagnosis of the lumbar pain is discussed. The radiculography with water-soluble contrast medium is used and 250 cases are studied. Some practical criteria of indication executation and interpretation of the examination are reported. (M.A.C.) [pt

  17. The Digital Medium Meets the Advertising Message.

    Science.gov (United States)

    Nisenholtz, Martin

    1994-01-01

    Discusses the likelihood that companies will use online services as an advertising medium. Topics addressed include the art of interactive marketing; advertising in the digital age; early experiments with interactive marketing, including the use of videotex and videodisc; and recent trends that set the stage for interactive marketing to personal…

  18. Influence of small and medium building engineering ...

    African Journals Online (AJOL)

    This study investigated the influence of small and medium building engineering entrepreneurship for the actualization of vision 20:2020 in Kebbi State, Nigeria. The study was conducted in Birnin Kebbi, Zuru and Argungu Local Government Areas of Kebbi State. The data were obtained from both primary and secondary ...

  19. Sound Art. Klang als Medium der Kunst

    DEFF Research Database (Denmark)

    Forskningsformidling på udstilling om lydkunst på ZKM i Karlsruhe. Lavet i samarbejde med Mats Lindström, leder af elektronmusikstudiet EMS (Stockholm). Udstillingen er en del af Morten Søndergaards (AAU) præsentation af skandinavisk lydkunst under titlen 'Unheard Avantgarde', der igen er en del ...... den store udstilling 'Sound as a Medium of Art'....

  20. Medium corrections to nucleon-nucleon interactions

    International Nuclear Information System (INIS)

    Dortmans, P.J.; Amos, K.

    1990-01-01

    The Bethe-Goldstone equations have been solved for both negative and positive energies to specify two nucleon G-matrices fully off of the energy shell. Medium correction effects of Pauli blocking and of the auxiliary potential are included in infinite matter systems characterized by fermi momenta in the range 0.5 fm -1 to 1.8 fm -1 . The Paris interaction is used as the starting potential in most calculations. Medium corrections are shown to be very significant over a large range of energies and densities. On the energy shell values of G-matrices vary markedly from those of free two nucleon (NN) t-matrices which have been solved by way of the Lippmann-Schwinger equation. Off of the energy shell, however, the free and medium corrected Kowalski-Noyes f-ratios rate are quite similar suggesting that a useful model of medium corrected G-matrices are appropriately scaled free NN t-matrices. The choice of auxiliary potential form is also shown to play a decisive role in the negative energy regime, especially when the saturation of nuclear matter is considered. 30 refs., 7 tabs., 7 figs

  1. Fluidized bed dry dense medium coal beneficiation

    CSIR Research Space (South Africa)

    North, Brian C

    2017-10-01

    Full Text Available medium beneficiation using a fluidized bed was investigated. Bed materials of sand, magnetite and ilmenite were used in a laboratory sized cylindrical fluidized bed. The materials were individually tested, as were mixes of sand and heavy minerals. Coal...

  2. Phase object retrieval through scattering medium

    Science.gov (United States)

    Zhao, Ming; Zhao, Meijing; Wu, Houde; Xu, Wenhai

    2018-05-01

    Optical imaging through a scattering medium has been an interesting and important research topic, especially in the field of biomedical imaging. However, it is still a challenging task due to strong scattering. This paper proposes to recover the phase object behind the scattering medium from one single-shot speckle intensity image using calibrated transmission matrices (TMs). We construct the forward model as a non-linear mapping, since the intensity image loses the phase information, and then a generalized phase retrieval algorithm is employed to recover the hidden object. Moreover, we show that a phase object can be reconstructed with a small portion of the speckle image captured by the camera. The simulation is performed to demonstrate our scheme and test its performance. Finally, a real experiment is set up, we measure the TMs from the scattering medium, and then use it to reconstruct the hidden object. We show that a phase object of size 32 × 32 is retrieved from 150 × 150 speckle grains, which is only 1/50 of the speckles area. We believe our proposed method can benefit the community of imaging through the scattering medium.

  3. Intergalactic medium heating by dark matter

    NARCIS (Netherlands)

    Ripamonti, E.; Mapelli, M.; Ferrara, A.

    2006-01-01

    Abstract: We derive the evolution of the energy deposition in the intergalactic medium (IGM) by dark matter (DM) decays/annihilations for both sterile neutrinos and light dark matter (LDM) particles. At z > 200 sterile neutrinos transfer a fraction f_abs~0.5 of their rest mass energy into the IGM;

  4. Nuclear matter as a nonlinear optical medium

    International Nuclear Information System (INIS)

    Hefter, E.F.; Papini, G.

    1986-01-01

    This paper is concerned with the question whether nuclear matter should be considered as a nonlinear optical medium. Taking, in a pragmatic way, quality and quantity of the results of well-established linear and nonlinear approaches as the main criterion, an affirmative answer is seen to be consistent with long-standing practices adhered to in nuclear physics

  5. Small and Medium Enterprises and Biopharmaceutical Innovations ...

    African Journals Online (AJOL)

    Small and Medium Enterprises and Biopharmaceutical Innovations in Africa: ... through biotechnological processes with links to biological sources especially those of live ... There are more than 500 biopharmaceutical products that have been ... By Country · List All Titles · Free To Read Titles This Journal is Open Access.

  6. Medium optimization for endochitinase production by recombinant ...

    African Journals Online (AJOL)

    The optimal concentrations of three factors were investigated by the response surface methodology using Box- Behnken design. The optimal medium components obtained for achieving the maximum activity of the endochitinase were as follows: Yeast extract 24.36 g/l, tryptone 20 g/l, YNB 5.0 g/l, potassium phosphate 100 ...

  7. Oyster mycelium on the liquid medium

    Directory of Open Access Journals (Sweden)

    Mariusz Gapiński

    2013-12-01

    Full Text Available The research presents the results of oyster mycelium growth on the liquid medium. The growth of 4-mycelium genius: Pleurotus citrinopileatus Singer, Pleurotus djamor Fries, Boedjin, Pleurotus erynii Fr. Kumm. and Pleurotus precoce Fr. Quel was tested. The quality and quantity of mycelium was assumed.

  8. Borromean structures in medium-heavy nuclei

    DEFF Research Database (Denmark)

    Hove, Dennis; Fedorov, Dmitri Vladimir; Fynbo, Hans Otto Uldall

    2014-01-01

    Borromean nuclear cluster structures are expected at the corresponding driplines. We locate the regions in the nuclear chart with the most promising constituents, it being protons and alpha-particles and investigate in details the properties of the possible borromean two-alpha systems in medium h...... 134Te−α−α structure in its ground state and low-lying spectrum....

  9. Carbon monoxide

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    1994-12-31

    The document identifies the main sources of carbon monoxide (CO) in the general outdoor atmosphere, describes methods of measuring and monitoring its concentration levels in the United Kingdom, and discusses the effects of carbon monoxide on human health. Following its review, the Panel has put forward a recommendation for an air quality standard for carbon monoxide in the United Kingdom of 10 ppm, measured as a running 8-hour average. The document includes tables and graphs of emissions of CO, in total and by emission source, and on the increase in blood levels of carboxyhaemoglobin with continuing exposure to CO. 11 refs., 4 figs., 4 tabs.

  10. Controls on carbon consumption during Alaskan wildland fires

    Science.gov (United States)

    Eric S. Kasischke; Elizabeth E. Hoy

    2012-01-01

    A method was developed to estimate carbon consumed during wildland fires in interior Alaska based on medium-spatial scale data (60 m cell size) generated on a daily basis. Carbon consumption estimates were developed for 41 fire events in the large fire year of 2004 and 34 fire events from the small fire years of 2006-2008. Total carbon consumed during the large fire...

  11. Recovery of perchloroethylene scrubbing medium generated in the refabrication of high-temperature gas-cooled reactor fuel

    Energy Technology Data Exchange (ETDEWEB)

    Judd, M.S.; Van Cleve, J.E. Jr.; Rainey, W.T. Jr.

    1976-11-01

    During the refabrication of high-temperature gas-cooled reactor (HTGR) fuel, perchloroethylene (C/sub 2/Cl/sub 4/) is used as the nonmoderating scrubbing medium to remove condensable hydrocarbons, carbon soot, and uranium-bearing particulates from the off-gas streams. The process by which the contaminated perchloroethylene is recycled is discussed.

  12. Recovery of perchloroethylene scrubbing medium generated in the refabrication of high-temperature gas-cooled reactor fuel

    International Nuclear Information System (INIS)

    Judd, M.S.; Van Cleve, J.E. Jr.; Rainey, W.T. Jr.

    1976-11-01

    During the refabrication of high-temperature gas-cooled reactor (HTGR) fuel, perchloroethylene (C 2 Cl 4 ) is used as the nonmoderating scrubbing medium to remove condensable hydrocarbons, carbon soot, and uranium-bearing particulates from the off-gas streams. The process by which the contaminated perchloroethylene is recycled is discussed

  13. Shortened carbon nanotubes and their influence on the electrical properties of polymer nanocomposites

    NARCIS (Netherlands)

    Inam, F.; Reece, M.J.; Peijs, A.A.J.M.

    2012-01-01

    Multi-wall carbon nanotubes of medium length (mCNTs) were aggressively tip-ultrasonicated to produce shortened and damaged carbon nanotubes (xCNTs). High-resolution electron microscopic analysis was performed to measure the dimensions of carbon nanotubes (CNTs). Thermo-gravimetric analysis and Raman

  14. Photosynthesis and Calcification by Emiliania huxleyi (Prymnesiophyceae) as a Function of Inorganic Carbon Species

    NARCIS (Netherlands)

    Buitenhuis, Erik T.; Baar, Hein J.W. de; Veldhuis, Marcel J.W.

    1999-01-01

    To test the possibility of inorganic carbon limitation of the marine unicellular alga Emiliania huxleyi (Lohmann) Hay and Mohler, its carbon acquisition was measured as a function of the different chemical species of inorganic carbon present in the medium. Because these different species are

  15. Calcium Carbonate

    Science.gov (United States)

    ... Calcium is needed by the body for healthy bones, muscles, nervous system, and heart. Calcium carbonate also ... to your pharmacist or contact your local garbage/recycling department to learn about take-back programs in ...

  16. Bio-cellulose Production by Beijerinckia fluminensis WAUPM53 and Gluconacetobacter xylinus 0416 in Sago By-product Medium.

    Science.gov (United States)

    Voon, W W Y; Muhialdin, B J; Yusof, N L; Rukayadi, Y; Meor Hussin, A S

    2018-06-19

    Bio-cellulose is the microbial extracellular cellulose that is produced by growing several microorganisms on agriculture by-products, and it is used in several food applications. This study aims to utilize sago by-product, coconut water, and the standard medium Hestrin-Schramm as the carbon sources in the culture medium for bio-cellulose production. The bacteria Beijerinkia fluminensis WAUPM53 and Gluconacetobacter xylinus 0416 were selected based on their bio-cellulose production activity. The structure was determined by Fourier transform infrared spectroscopy and scanning electron microscopy, while the toxicity safety was evaluated by brine shrimp lethality test. The results of Fourier transform infrared spectroscopy showed that the bio-cellulose produced by B. fluminensis cultivated in sago by-products was of high quality. The bio-cellulose production by B. fluminensis in the sago by-product medium was slightly higher than that in the coconut water medium and was comparable with the production in the Hestrin-Schramm medium. Brine shrimp lethality test confirmed that the bio-cellulose produced by B. fluminensis in the sago by-product medium has no toxicity, which is safe for applications in the food industry. This is the first study to determine the high potential of sago by-product to be used as a new carbon source for the bio-cellulose production.

  17. Infiltrated carbon foam composites

    Science.gov (United States)

    Lucas, Rick D. (Inventor); Danford, Harry E. (Inventor); Plucinski, Janusz W. (Inventor); Merriman, Douglas J. (Inventor); Blacker, Jesse M. (Inventor)

    2012-01-01

    An infiltrated carbon foam composite and method for making the composite is described. The infiltrated carbon foam composite may include a carbonized carbon aerogel in cells of a carbon foam body and a resin is infiltrated into the carbon foam body filling the cells of the carbon foam body and spaces around the carbonized carbon aerogel. The infiltrated carbon foam composites may be useful for mid-density ablative thermal protection systems.

  18. Carbon-climate feedbacks accelerate ocean acidification

    Science.gov (United States)

    Matear, Richard J.; Lenton, Andrew

    2018-03-01

    Carbon-climate feedbacks have the potential to significantly impact the future climate by altering atmospheric CO2 concentrations (Zaehle et al. 2010). By modifying the future atmospheric CO2 concentrations, the carbon-climate feedbacks will also influence the future ocean acidification trajectory. Here, we use the CO2 emissions scenarios from four representative concentration pathways (RCPs) with an Earth system model to project the future trajectories of ocean acidification with the inclusion of carbon-climate feedbacks. We show that simulated carbon-climate feedbacks can significantly impact the onset of undersaturated aragonite conditions in the Southern and Arctic oceans, the suitable habitat for tropical coral and the deepwater saturation states. Under the high-emissions scenarios (RCP8.5 and RCP6), the carbon-climate feedbacks advance the onset of surface water under saturation and the decline in suitable coral reef habitat by a decade or more. The impacts of the carbon-climate feedbacks are most significant for the medium- (RCP4.5) and low-emissions (RCP2.6) scenarios. For the RCP4.5 scenario, by 2100 the carbon-climate feedbacks nearly double the area of surface water undersaturated with respect to aragonite and reduce by 50 % the surface water suitable for coral reefs. For the RCP2.6 scenario, by 2100 the carbon-climate feedbacks reduce the area suitable for coral reefs by 40 % and increase the area of undersaturated surface water by 20 %. The sensitivity of ocean acidification to the carbon-climate feedbacks in the low to medium emission scenarios is important because recent CO2 emission reduction commitments are trying to transition emissions to such a scenario. Our study highlights the need to better characterise the carbon-climate feedbacks and ensure we do not underestimate the projected ocean acidification.

  19. Medium Modifications of Hadrons in Photon Induced Reactions

    International Nuclear Information System (INIS)

    Schadmand, S.

    2004-01-01

    Indications for in-medium modifications of hadron properties are reported from photoabsorption and meson production experiments. Strong medium modifications are observed in inclusive photoabsorption experiments and theoretical models investigate the in-medium dynamics of baryon resonances and their coupling to mesons. Recent experiments study the in-medium behavior of scalar and vector mesons where theoretical models expect in-medium modifications of the meson spectral functions that might be connected to partial restoration of chiral symmetry

  20. Medium dependence of multiplicity distributions in MLLA

    Energy Technology Data Exchange (ETDEWEB)

    Armesto, Nestor; Pajares, Carlos; Quiroga-Arias, Paloma [Universidade de Santiago de Compostela, Departamento de Fisica de Particulas and IGFAE, Santiago de Compostela (Spain)

    2009-06-15

    We study the modification of the multiplicity distributions in MLLA due to the presence of a QCD medium. The medium is introduced through a multiplicative constant (f{sub med}) in the soft infrared parts of the kernels of the QCD evolution equations. Using the asymptotic ansatz for mean multiplicities of the quark and gluons, left angle n{sub G} right angle =e{sup {gamma}}{sup y} and left angle n{sub Q} right angle =r {sup -1}e{sup {gamma}}{sup y}, respectively, we study two cases: fixed {gamma} as previously considered in the literature, and fixed {alpha}{sub s}. We find opposite behaviors of the dispersion of the multiplicity distributions with increasing f{sub med} in both cases. For fixed {gamma} the dispersion decreases, while for fixed {alpha}{sub s} it increases. (orig.)