  1. Monitoring alloy formation during mechanical alloying process by x-ray diffraction techniques

    International Nuclear Information System (INIS)

    Abdul Kadir Masrom; Noraizam Md Diah; Mazli Mustapha

    2002-01-01

    Monitoring alloying (MA) is a novel processing technique that use high energy impact ball mill to produce alloys with enhanced properties and microscopically homogeneous materials starting from various powder mixtures. Mechanical alloying process was originally developed to produce oxide dispersion strengthened nickel superalloys. In principal, in high-energy ball milling process, alloy is formed by the result of repeated welding, fracturing and rewelding of powder particles in a high energy ball mill. In this process a powder mixture in a ball mill is subjected to high-energy collisions among balls. MA has been shown to be capable of synthesizing a variety of materials. It is known to be capable to prepare equilibrium and non-equilibrium phases starting from blended elemental or prealloyed powders. The process ability to produce highly metastable materials such as amorphous alloys and nanostructured materials has made this process attractive and it has been considered as a promising material processing technique that could be used to produce many advanced materials at low cost. The present study explores the conditions under which aluminum alloys formation occurs by ball milling of blended aluminum and its alloying elements powders. In this work, attempt was made in producing aluminum 2024 alloys by milling of blended elemental aluminum powder of 2024 composition in a stainless steel container under argon atmosphere for up to 210 minutes. X-ray diffraction together with thermal analysis techniques has been used to monitor phase changes in the milled powder. Results indicate that, using our predetermined milling parameters, alloys were formed after 120 minutes milling. The thermal analysis data was also presented in this report. (Author)

  2. Tailored Welding Technique for High Strength Al-Cu Alloy for Higher Mechanical Properties

    Science.gov (United States)

    Biradar, N. S.; Raman, R.

    AA2014 aluminum alloy, with 4.5% Cu as major alloying element, offers highest strength and hardness values in T6 temper and finds extensive use in aircraft primary structures. However, this alloy is difficult to weld by fusion welding because the dendritic structure formed can affect weld properties seriously. Among the welding processes, AC-TIG technique is largely used for welding. As welded yield strength was in the range of 190-195 MPa, using conventional TIG technique. Welding metallurgy of AA2014 was critically reviewed and factors responsible for lower properties were identified. Square-wave AC TIG with Transverse mechanical arc oscillation (TMAO) was postulated to improve the weld strength. A systematic experimentation using 4 mm thick plates produced YS in the range of 230-240 MPa, has been achieved. Through characterization including optical and SEM/EDX was conducted to validate the metallurgical phenomena attributable to improvement in weld properties.

  3. Microstructures and Mechanical Properties of Co-Cr Dental Alloys Fabricated by Three CAD/CAM-Based Processing Techniques

    Directory of Open Access Journals (Sweden)

    Hae Ri Kim

    2016-07-01

    Full Text Available The microstructures and mechanical properties of cobalt-chromium (Co-Cr alloys produced by three CAD/CAM-based processing techniques were investigated in comparison with those produced by the traditional casting technique. Four groups of disc- (microstructures or dumbbell- (mechanical properties specimens made of Co-Cr alloys were prepared using casting (CS, milling (ML, selective laser melting (SLM, and milling/post-sintering (ML/PS. For each technique, the corresponding commercial alloy material was used. The microstructures of the specimens were evaluated via X-ray diffractometry, optical and scanning electron microscopy with energy-dispersive X-ray spectroscopy, and electron backscattered diffraction pattern analysis. The mechanical properties were evaluated using a tensile test according to ISO 22674 (n = 6. The microstructure of the alloys was strongly influenced by the manufacturing processes. Overall, the SLM group showed superior mechanical properties, the ML/PS group being nearly comparable. The mechanical properties of the ML group were inferior to those of the CS group. The microstructures and mechanical properties of Co-Cr alloys were greatly dependent on the manufacturing technique as well as the chemical composition. The SLM and ML/PS techniques may be considered promising alternatives to the Co-Cr alloy casting process.

  4. Multiple-walled BN nanotubes obtained with a mechanical alloying technique

    International Nuclear Information System (INIS)

    Rosas, G.; Sistos, J.; Ascencio, J.A.; Medina, A.; Perez, R.

    2005-01-01

    An experimental method to obtain multiple-walled nanotubes of BN using low energy is presented. The method is based on the use of mechanical alloying techniques with elemental boron powders and nitrogen gas mixed in an autoclave at room temperature. The chemical and structural characteristics of the multiple-walled nanotubes were obtained using different techniques, such as X-ray diffraction, transmission electron microscopy, EELS microanalysis, high-resolution electron microscopy images and theoretical simulations based on the multisliced approach of the electron diffraction theory. This investigation clearly illustrates the production of multiple-wall BN nanotubes at room temperature. These results open up a new kind of synthesis method with low expense and important perspectives for use in large-quantity production. (orig.)

  5. Influence of Processing Techniques on Microstructure and Mechanical Properties of a Biodegradable Mg-3Zn-2Ca Alloy.

    Science.gov (United States)

    Doležal, Pavel; Zapletal, Josef; Fintová, Stanislava; Trojanová, Zuzanka; Greger, Miroslav; Roupcová, Pavla; Podrábský, Tomáš

    2016-10-28

    New Mg-3Zn-2Ca magnesium alloy was prepared using different processing techniques: gravity casting as well as squeeze casting in liquid and semisolid states. Materials were further thermally treated; thermal treatment of the gravity cast alloy was additionally combined with the equal channel angular pressing (ECAP). Alloy processed by the squeeze casting in liquid as well as in semisolid state exhibit improved plasticity; the ECAP processing positively influenced both the tensile and compressive characteristics of the alloy. Applied heat treatment influenced the distribution and chemical composition of present intermetallic phases. Influence of particular processing techniques, heat treatment, and intermetallic phase distribution is thoroughly discussed in relation to mechanical behavior of presented alloys.

  6. Optimization of Micro-Alloying Elements for Mechanical Properties in Normalized Cast Steel Using Taguchi Technique

    Directory of Open Access Journals (Sweden)

    Chokkalingam B.

    2017-06-01

    Full Text Available In this study, Taguchi method is used to find out the effect of micro alloying elements like vanadium, niobium and titanium on the hardness and tensile strength of the normalized cast steel. Based on this method, plan of experiments were made by using orthogonal arrays to acquire the data on hardness and tensile strength. The signal to noise ratio and analysis of variance (ANOVA are used to investigate the effect of these micro alloying elements on these two mechanical properties of the micro alloyed normalized cast steel. The results indicated that in the micro alloyed normalized cast steel both these properties increases when compared to non-micro-alloyed normalized cast steel. The effect of niobium addition was found to be significantly higher to obtain higher hardness and tensile strength when compared to other micro alloying elements. The maximum hardness of 200HV and the maximum tensile strength of 780 N/mm2 were obtained in 0.05%Nb addition micro alloyed normalized cast steel. Micro-alloyed with niobium normalized cast steel have the finest and uniform microstructure and fine pearlite colonies distributed uniformly in the ferrite. The optimum condition to obtain higher hardness and tensile strength were determined. The results were verified with experiments.

  7. Characteristics of mechanical alloying of Zn-Al-based alloys

    International Nuclear Information System (INIS)

    Zhu, Y.H.; Hong Kong Polytechnic; Perez Hernandez, A.; Lee, W.B.

    2001-01-01

    Three pure elemental powder mixtures of Zn-22%Al-18%Cu, Zn-5%Al-11%Cu, and Zn-27%Al-3%Cu (in wt.%) were mechanically alloyed by steel-ball milling processing. The mechanical alloying characteristics were investigated using X-ray diffraction, scanning electron microscopy, and transmission electron microscopy techniques. It was explored that mechanical alloying started with the formation of phases from pure elemental powders, and this was followed by mechanical milling-induced phase transformation. During mechanical alloying, phases stable at the higher temperatures formed at the near room temperature of milling. Nano-structure Zn-Al-based alloys were produced by mechanical alloying. (orig.)

  8. Modified Welding Technique of a Hypo-Eutectic Al-Cu Alloy for Higher Mechanical Properties

    Science.gov (United States)

    Ghosh, B. R.; Gupta, R. K.; Biju, S.; Sinha, P. P.

    GTAW process is used for welding of pressure vessels made of hypo-eutectic Al-Cu alloy AA2219 containing 6.3% Cu. As welded Yield strength of the alloy was found to be in the range of 140-150 MPa, using conventional single pass GTAW technique on both AC and DCSP modes. Interestingly, it was also found that weld-strength decreased with increase in thickness of the weld coupons. Welding metallurgy of AA2219 Al alloy was critically reviewed and factors responsible for lower properties were identified. Multipass GTAW on DCSP mode was postulated to improve the weld strength of this alloy. A systematic experimentation using 12 mm thick plates was carried out and YS of 200 MPa has been achieved in the as welded condition. Thorough characterization including optical and electron microscopy was conducted to validate the metallurgical phenomena attributable to improvement in weld strength. This paper presents the conceptual understanding of welding metallurgy of AA2219 alloy and validation by experiments, which could lead to better weld properties using multipass GTAW on DCSP mode.

  9. Room and ultrahigh temperature structure-mechanical property relationships of tungsten alloys formed by field assisted sintering technique (FAST)

    Energy Technology Data Exchange (ETDEWEB)

    Browning, Paul N.; Alagic, Sven [Pennsylvania State University, Department of Materials Science and Engineering, State College, PA-16801 (United States); Pennsylvania State University, Applied Research Laboratory, State College, PA-16801 (United States); Kulkarni, Anil [Pennsylvania State University, Department of Nuclear and Mechanical Engineering, State College, PA-16801 (United States); Matson, Lawrence [Materials and Manufacturing Directorate, Wright Patterson Air Force Base, Dayton, OH (United States); Singh, Jogender, E-mail: jxs46@arl.psu.edu [Pennsylvania State University, Department of Materials Science and Engineering, State College, PA-16801 (United States); Pennsylvania State University, Applied Research Laboratory, State College, PA-16801 (United States)

    2016-09-30

    Tungsten based alloys have become of critical importance in a number of applications including plasma-facing materials in nuclear fusion reactors, rocket nozzles for aerospace applications, and in kinetic energy penetrators in the defense industry. Formation of components for these uses by powder metallurgical techniques has proven challenging, due to tungsten's relatively poor sinterability. Here we report the use of field assisted sintering technique (FAST) to produce high density, fine grain alloys with mechanical properties comparable or superior to that of components produced by conventional techniques. Alloys of pure tungsten, W-3 vol%TiC, W-5 vol%TiC, and W-10 vol%Ta were synthesized at 2100 °C, 35 MPa for 25 min using FAST. Microstructural characterization revealed effective reduction of grain size with TiC addition and preferential diffusion of oxygen into the center of tantalum particles in tantalum containing alloys. Tensile testing of alloys revealed TiC addition to W resulted in substantially improved ultimate tensile strength at the cost of ductility in comparison at temperatures up to 1926 °C (3500 °F) however this strengthening effect was lost at 2204 °C (4000 °F). Addition of 10 vol%Ta to W resulted in reduced hardness at room temperature, but substantially increased yield strength at the cost of slightly reduced ductility at 1926 °C and 2204 °C.

  10. Aluminum alloy weldability. Identification of weld solidification cracking mechanisms through novel experimental technique and model development

    Energy Technology Data Exchange (ETDEWEB)

    Coniglio, Nicolas

    2008-07-01

    The objective of the present thesis is to make advancements in understanding solidification crack formation in aluminum welds, by investigating in particular the aluminum 6060/4043 system. Alloy 6060 is typical of a family of Al-Mg-Si extrusion alloys, which are considered weldable only when using an appropriate filler alloy such as 4043 (Al-5Si). The effect of 4043 filler dilution (i.e. weld metal silicon content) on cracking sensitivity and solidification path of Alloy 6060 welds are investigated. Afterwards, cracking models are developed to propose mechanisms for solidification crack initiation and growth. Cracking Sensitivity. Building upon the concept that silicon improves weldability and that weldability can be defined by a critical strain rate, strain rate-composition combinations required for solidification crack formation in the Al- 6060/4043 system were determined using the newly developed Controlled Tensile Weldability (CTW) test utilizing local strain extensometer measurements. Results, presented in a critical strain rate - dilution map, show a crack - no crack boundary which reveals that higher local strain rates require higher 4043 filler dilution to avoid solidification cracking when arc welding Alloy 6060. Using the established crack - no crack boundary as a line of reference, additional parameters were examined and their influence on cracking characterized. These parameter influences have included studies of weld travel speed, weld pool contaminants (Fe, O, and H), and grain refiner additions (TiAl{sub 3} + Boron). Each parameter has been independently varied and its effect on cracking susceptibility quantified in terms of strain rate - composition combinations. Solidification Path. Solidification path of the Al-6060/4043 system was characterized using thermal analysis and phase identification. Increasing 4043 filler dilution from 0 to 16% in Alloy 6060 arc welds resulted in little effect on thermal arrests and microstructure, no effect on

  11. Mechanical Behaviour Investigation Of Aluminium Alloy Tailor Welded Blank Developed By Using Friction Stir Welding Technique

    Science.gov (United States)

    Dwi Anggono, Agus; Sugito, Bibit; Hariyanto, Agus; Subroto; Sarjito

    2017-10-01

    The objective on the research was to investigate the mechanical properties and microstructure of tailor welded blank (TWB) made from AA6061-T6 and AA1100 using friction stir welding (FSW) process. Due to the dissimilar mechanical properties of the two aluminium alloys, microhardness test was conducted to measure the hardness distribution across the weld nugget. The mixing of two distinct materials was influenced by tool rotation speed. Therefore, microstructure analysis was carried out to investigate the grain size and shape. The grain size of AA6061-T6 has increased in the heat affected zone (HAZ) while for AA1100 has decreased. In the weld nugget, it has found a hook defects in the dissimilar aluminium joining. By using monotonic tensile load, the different weld line direction was observed with the expansion in tool rotation. The joints failure were consistently on the area of AA1100 series. Furthermore, two specimens were investigated, one through the dissimilar aluminium and the other through similiar material. Inspection of the weld nugget hardness was shown that nonhomogen material intermixing during the stiring process as confirmed by microhardness measurement.

  12. COMPARISON OF THE MECHANICAL RESPONSE OF POROUS TI-6AL-4V ALLOYS PRODUCED BY DIFFERENT COMPACTION TECHNIQUES

    Directory of Open Access Journals (Sweden)

    G.İpek Selimoğlu

    2017-03-01

    Full Text Available Porous Ti-6Al-4V alloys are attractive candidates as implant materials due to their good biocompatibility combined with the porous structure leading to increased osseointegration and decreased stiffness. Accordingly, different processing techniques were employed for the production of Ti-6Al-4V foams in the literature. Among these techniques, sintering with space holder is used to produce porous Ti-6Al-4V alloys in this study. Magnesium was employed as the space holder material because of its relatively low boiling point as well as high oxygen affinity. Two different compaction techniques, die compaction with hydraulic pressing and cold isostatic pressing (CIP, were employed for obtaining green compacts. Both spherical and nonspherical Ti-6Al-4V powders were used to investigate the effect of powder shape on compaction. Processed foams were characterized in terms of both microstructural and mechanical aspects in order to investigate the effect of pressing conditions in combination with powder characteristics. It was observed that NS-CIP foam, which was produced by compacting nonspherical powders by cold isostatic press, has the highest strength. However, the S-DP foam, which was produced by die-pressing of spherical powders, has the highest toughness.

  13. Microstructure and mechanical properties of hypo/hyper-eutectic Al-Si alloys synthesized using a near-net shape forming technique

    International Nuclear Information System (INIS)

    Gupta, M.; Ling, S.

    1999-01-01

    In the present study, three aluminum-silicon alloys containing 7, 10 and 19 wt % silicon were synthesized using a novel technique commonly known as disintegrated melt deposition technique. The results following processing revealed that a yield of at least 80% can be achieved after defacing the shrinkage cavity from the as-processed ingots. Microstructural characterization studies conducted on the as-processed samples revealed an increase in the volume fraction of porosity with an increase in silicon content. Porosity levels of 1.07, 1.51 and 2.65% attained in the case of Al-7Si, Al-10Si, and Al-19Si alloys indicates the near-net shape forming capability of the disintegrated melt deposition technique. The results of aging studies conducted on the aluminum-silicon alloys revealed similar aging kinetics irrespective of different silicon content. Results of ambient temperature mechanical tests demonstrate an increase in matrix microhardness and 0.2% yield stress and decrease in ductility with an increase in silicon content in aluminum. Furthermore, the results of an attempt to investigate the effect of extrusion on Al-19Si alloy revealed that the extrusion process significantly assists in reducing porosity and improving microstructural uniformity, 0.2% yield strength, ultimate tensile strength and ductility when compared to the as-processed Al-19Si alloy. The results of microstructural characterization and mechanical properties of aluminum-silicon alloys were finally correlated with the amount of silicon in aluminum and secondary processing technique. (orig.)

  14. Analysis of micro-mechanical properties and microstructure of low-alloy steel using nanoindentation technique

    International Nuclear Information System (INIS)

    Kim, S. H.; Kweon, D. I.; Choi, Y.

    2001-01-01

    Materials for nuclear reactor degrades continuously through microstructural changes by high operation temperature and irradiation. Strength properties is the most important factor for the selection of materials and the determination of degradation degree. Adhesion properties affected by strengthening particles with the range of nm size, strength distribution in microstructres couldn't have been easily tested by the conventional mechanical testing methods. Nanoindentation technique with the μN load range and the nm residual indent size range is very useful to determine those properties. Indentation was done with AFM for indenter positioning. Hardness values could be obtained from the analysis of indentation load-depth curves and AFM images of each phases were used for characterization of phases. Finally, overall strength of multiphase materials was predicted by evaluating the micro phase constituent properties. The volume fractions of each phase were evaluated through analyzing the shape and size of each phases on AFM image. Rule-of-mixture method was applied to the prediction of overall strength. Finally, the influence of grain boundary for strength properties was analyzed from several experiments

  15. Study of deformation and fracture micro mechanisms of titanium alloy Ti-6Al-4V using electron microscopy and and X-ray diffraction techniques

    International Nuclear Information System (INIS)

    Morcelli, Aparecido Edilson

    2009-01-01

    This present work allowed the study of deformation and fracture micro mechanisms of titanium alloy Ti-6Al-4V, used commercially for the manufacture of metallic biomaterials. The techniques employed for the analysis of the material under study were: scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray diffraction (XRD). The study of the influence and behavior of the phases present in titanium alloys is important to evaluate the behavior of cracks in titanium alloys with high mechanical strength, which have fine alpha (α), beta (β) and (α±β) microstructure, linking the presence of the phases with the strength of the material. The evaluation in situ of deformation and fracture micro mechanisms were performed by TEM and was also a study of phase transformations during cooling in titanium alloys, using the techniques of bright field, dark field and diffraction of electrons in the selected area. After heat treatment differences were observed between the amount of in relation to the original microstructure of the β and α phases material for different conditions used in heat treatment applied to the alloy. The presence of lamellar microstructure formed during cooling in the β field was observed, promoting the conversion of part of the secondary alpha structure in β phase, which was trapped between the lamellar of alpha. (author)

  16. Influence of Processing Techniques on Microstructure and Mechanical Properties of a Biodegradable Mg-3Zn-2Ca Alloy

    Czech Academy of Sciences Publication Activity Database

    Doležal, P.; Zapletal, J.; Fintová, Stanislava; Trojanová, Z.; Greger, M.; Roupcová, Pavla; Podrábský, T.

    2016-01-01

    Roč. 9, č. 11 (2016), s. 1-15, č. článku 880. ISSN 1996-1944 Institutional support: RVO:68081723 Keywords : biodegradable magnesium alloy * Mg-Zn-Ca * squeeze casting * ECAP processing * microstructure * mechanical properties Subject RIV: JP - Industrial Processing Impact factor: 2.654, year: 2016 http://www.mdpi.com/1996-1944/9/11/880

  17. Microstructure and Mechanical Properties of MWCNTs Reinforced A356 Aluminum Alloys Cast Nanocomposites Fabricated by Using a Combination of Rheocasting and Squeeze Casting Techniques

    Directory of Open Access Journals (Sweden)

    Abou Bakr Elshalakany

    2014-01-01

    Full Text Available A356 hypoeutectic aluminum-silicon alloys matrix composites reinforced by different contents of multiwalled carbon nanotubes (MWCNTs were fabricated using a combination of rheocasting and squeeze casting techniques. A novel approach by adding MWCNTs into A356 aluminum alloy matrix with CNTs has been performed. This method is significant in debundling and preventing flotation of the CNTs within the molten alloy. The microstructures of nanocomposites and the interface between the aluminum alloy matrix and the MWCNTs were examined by using an optical microscopy (OM and scanning electron microscopy (SEM equipped with an energy dispersive X-ray analysis (EDX. This method remarkably facilitated a uniform dispersion of nanotubes within A356 aluminum alloy matrix as well as a refinement of grain size. In addition, the effects of weight fraction (0.5, 1.0, 1.5, 2.0, and 2.5 wt% of the CNT-blended matrix on mechanical properties were evaluated. The results have indicated that a significant improvement in ultimate tensile strength and elongation percentage of nanocomposite occurred at the optimal amount of 1.5 wt% MWCNTs which represents an increase in their values by a ratio of about 50% and 280%, respectively, compared to their corresponding values of monolithic alloy. Hardness of the samples was also significantly increased by the addition of CNTs.

  18. Magnetic properties and EXAFS study of nanocrystalline Fe2Mn0.5Cu0.5Al synthesized using mechanical alloying technique

    International Nuclear Information System (INIS)

    Nanto, Dwi; Yang, Dong-Seok; Yu, Seong-Cho

    2014-01-01

    Nanocrystalline Fe 2 Mn 0.5 Cu 0.5 Al has been synthesized by the mechanical alloying technique and studied as a function of milling time. Alloy nature of Fe 2 Mn 0.5 Cu 0.5 Al was observed in a sample milled for 96 h. The magnetic saturation is 4.0 μ B /f.u., which coincidently follows Slater–Pauling rule at 5 K. Nanocrystalline Fe 2 Mn 0.5 Cu 0.5 Al has enhanced saturate magnetization compared to any other fabrication of Fe 2 MnAl reported. Cu element plays an important role in site competes with other elements and may result in the enhancement of saturate magnetization. In accordance to the magnetic results and EXAFS pattern, it was revealed that the dynamics of magnetic properties were confirmed as structural changes of nanocrystalline Fe 2 Mn 0.5 Cu 0.5 Al

  19. Comparison of mechanical properties and microstructural characterization of CoCrMo alloy obtained via selective laser melting (SLM) and casting techniques

    Energy Technology Data Exchange (ETDEWEB)

    Mergulhao, Marcello Vertamatti; Podesta, Carlos Eduardo; Neves, Mauricio David Martins das, E-mail: marcellovertamatti@usp.br [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)

    2016-07-01

    Full text: Advances in processes using the powder metallurgy techniques are making this technology competitive compared to the other traditional manufacturing processes, especially in medicine area. The additive manufacturing technique - selective laser melting (SLM) was applied in a biomaterial of CoCrMo alloy (ASTM F75), to study the mechanical properties and microstructural characterization in comparison between the conventional technique - lost wax casting. The gas atomized powder was investigated by their physical (as apparent density, bulk density and flow rate) and the chemical properties (SEM-EDS and X-ray fluorescence). Specimens of standard samples were manufactured using these techniques to evaluate the mechanical properties as yield strength, maximum tensile, rupture tensile, elongation, elastic modulus, transverse rupture strength and the Vickers hardness. Before the mechanical tests the microstructure of specimens were examined using optical microscope (OM) and SEM-EDS. The results of mechanical properties showed a higher values in the SLM specimens compared with the obtained in the cast specimens. The micrographs revealed a typical morphology of consolidation process, like as the characterized by selected layer used in the SLM technique and the primary and secondary dendrites arms in the casting technique. (author)

  20. Mechanical properties of ordered alloys

    International Nuclear Information System (INIS)

    Kroupa, F.

    1977-06-01

    A survey is given of the metallophysical fundamentals of the mechanical properties of ordered two-phase alloys. Alloys of this type have a superlattice structure in a substitution mixed crystal. Ordering is achieved by slow cooling or by annealing below the critical temperature, during which ordering domains (antiphase domains) are formed. At a high degree of ordering, the dislocations are concentrated to form pairs, so-called super-dislocations. The mechanical properties may be selectively changed by varying different parameters (size of the ordering domains, degree of ordering, energy of the antiphase boundaries) by a special composition and heat treatment.(GSC) [de

  1. Magnesium mechanical alloys for hydrogen storage

    International Nuclear Information System (INIS)

    Ivanov, E.; Konstanchuk, I.; Stepanov, A.; Boldyrev, V.

    1985-01-01

    Metal hybrides are currently being used to store and handle hydrogen and its isotopes. They are also being tested in hydrogen compressors and in heat energy, refrigerators and in hydrogen and thermal storage devices. Metal hydrides have been proposed as one of the possible media for hydrogen storage to overcome the limitations of other techniques in regard to safety hydrogen weight and volume ration. The suitability of metal hybrides as a hydrogen storage media depends on a number of factors such as storage capacity, reactivity with hydrogen at various pressures and temperatures, and the cost of base materials. Magnesium based alloys are promising materials for storing hydrogen. They are generally made by argon melting and no attention has been payed to other fabrication techniques such as mechanical alloying or powder technique

  2. Dispersion strengthening of precipitation hardened Al-Cu-Mg alloys prepared by rapid solidification and mechanical alloying

    Science.gov (United States)

    Gilman, P. S.; Sankaran, K. K.

    1988-01-01

    Several Al-4Cu-1Mg-1.5Fe-0.75Ce alloys have been processed from either rapidly solidified or mechanically alloyed powder using various vacuum degassing parameters and consolidation techniques. Strengthening by the fine subgrains, grains, and the dispersoids individually or in combination is more effective when the alloys contain shearable precipitates; consequently, the strength of the alloys is higher in the naturally aged rather than the artificially aged condition. The strengths of the mechanically alloyed variants are greater than those produced from prealloyed powder. Properties and microstructural features of these dispersion strengthened alloys are discussed in regards to their processing histories.

  3. Mechanical and tribological properties of newly developed Tribaloy alloys

    International Nuclear Information System (INIS)

    Xu, W.; Liu, R.; Patnaik, P.C.; Yao, M.X.; Wu, X.J.

    2007-01-01

    Outstanding combination of mechanical, wear and corrosion performance has been achieved in Laves intermetallic materials, termed Tribaloy alloys. In these two-phase alloys the solid solution provides high mechanical strength and fracture toughness while the Laves intermetallic phase offers excellent wear resistance. However, conventional Tribaloy alloys usually have low tensile strength and fracture toughness compared with ductile materials due to the large volume fraction of Laves phase, which has limited their application in many cases. The present research is aimed at developing advanced Tribaloy alloys with increasing ductility. Two new cobalt base alloys were developed in this research. The specimens were fabricated with a centrifugal casting technique. The material characterization was performed using the differential scanning calorimetry (DSC), scanning electron microscope (SEM), indentation and ball-on-disc tribological techniques

  4. Mechanical behaviour of δ-phase Pu-Ga alloys

    International Nuclear Information System (INIS)

    Kaschner, G.C.; Stout, M.G.; Hecker, S.S.

    2007-01-01

    Paper describes a model to ensure prediction of the mechanical behaviour of gallium stabilized plutonium FCC-alloys representing the mechanical threshold strength (MSS) constitutive model based on the effect of temperature, of strain rate, of grain size and of alloy composition. One performed the comparative analysis of the design data derived by means of the elaborated mathematical techniques and of the published results of the mechanical tests of Pu-Ga system various alloys. The model is shown to be adequate to predict the tensile strength and the yield strength values [ru

  5. Characterization of fracture and deformation mechanism in a high strength beta titanium alloy Ti-10-2-3 using EBSD technique

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, Jalaj, E-mail: jalaj@dmrl.drdo.in; Singh, Vajinder; Ghosal, Partha; Kumar, Vikas

    2015-01-19

    In the present study, fracture toughness tested specimens in longitudinal (LT) and transverse loading (TL) directions of beta titanium alloy have been investigated using Electron Back Scattered Diffraction (EBSD) technique. The orientation images captured at three different locations i.e. machine notch, fatigue pre-crack and final fracture have been compared. The LT sample exhibits with more facets than TL sample. The faceted aspect of the crack is generally associated with quasi-cleavage mechanism. The EBSD analysis clearly points out that in the LT specimen, the hexagonal orientation has moved towards near basal during the test. This may be the reason for the observance of facets in the LT specimen. The cracking in TL specimen might have been taken over by the bcc phase as it is oriented with harder planes of cubic {001} planes. Further, the Schmid factor has also been computed based on the defined loading conditions. Significant variation has been observed in the slip plane orientations and distributions at these three locations. The Schmid analysis has highlighted the significant contribution of different slip systems towards deformation and cracking in LT and TL specimens.

  6. Intermetallic alloys: Deformation, mechanical and fracture behaviour

    International Nuclear Information System (INIS)

    Dogan, B.

    1988-01-01

    The state of the art in intermetallic alloys development with particular emphasis on deformation, mechanical and fracture behaviour is documented. This review paper is prepared to lay the ground stones for a future work on mechanical property characterization and fracture behaviour of intermetallic alloys at GKSS. (orig.)

  7. Removable partial denture alloys processed by laser-sintering technique.

    Science.gov (United States)

    Alageel, Omar; Abdallah, Mohamed-Nur; Alsheghri, Ammar; Song, Jun; Caron, Eric; Tamimi, Faleh

    2018-04-01

    Removable partial dentures (RPDs) are traditionally made using a casting technique. New additive manufacturing processes based on laser sintering has been developed for quick fabrication of RPDs metal frameworks at low cost. The objective of this study was to characterize the mechanical, physical, and biocompatibility properties of RPD cobalt-chromium (Co-Cr) alloys produced by two laser-sintering systems and compare them to those prepared using traditional casting methods. The laser-sintered Co-Cr alloys were processed by the selective laser-sintering method (SLS) and the direct metal laser-sintering (DMLS) method using the Phenix system (L-1) and EOS system (L-2), respectively. L-1 and L-2 techniques were 8 and 3.5 times more precise than the casting (CC) technique (p laser-sintered and cast alloys were biocompatible. In conclusion, laser-sintered alloys are more precise and present better mechanical and fatigue properties than cast alloys for RPDs. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 1174-1185, 2018. © 2017 Wiley Periodicals, Inc.

  8. Effects of fabrication practices and techniques on the corrosion and mechanical properties of Ni-Cr-Mo nickel based alloys UNS N10276, N06022, N06686, and N06625

    International Nuclear Information System (INIS)

    Hinshaw, E.B.; Crum, J.R.

    1996-01-01

    Ni-Cr-Mo alloys have excellent resistance to both oxidizing and reducing type environments; however, heat treating, surface condition, welding, and type of welding consumable can have a significant affect on the corrosion resistance and mechanical properties of these alloys. It is also important when performing standard ASTM intergranular corrosion tests on welded test coupons to make an accurate comparison of alloys being tested. A standard weld procedure and consistent post-weld sample conditioning method should be incorporated into the comparison test program. An evaluation of the effect of various fabrication practices on the corrosion resistance of the alloy was performed using accelerated corrosion tests ASTM G28B. The fabrication conditions examined were as-welded, welded-pickled, welded-annealed-pickled, welded annealed ground, welded-ground, using over matching filler metals, and various levels of heat input. In addition to fabrication techniques, the effect of ASTM G28B test duration on corrosion rates of UNS N10276, N06022, N06686, and N06625 was evaluated. ASTM G28A intergranular corrosion and mechanical testing using welded coupons of UNS N06625 were also performed to determine the affect of post-weld annealing and aging heat treatments on the corrosion resistance and mechanical properties of UNS N06625

  9. Mechanical behaviour of Zn-Fe alloy coated mild steel

    International Nuclear Information System (INIS)

    Panagopoulos, C.N.; Georgiou, E.P.; Agathocleous, P.E.; Giannakopoulos, K.I.

    2009-01-01

    Zinc alloy coatings containing various amounts of Fe were deposited by electrodeposition technique on a mild steel substrate. The concentration of Fe in the produced alloy coatings ranged from 0 to 14 wt.%, whereas the thickness of the coatings was about 50 μm. Structural and metallurgical characterization of the produced coatings was performed with the aid of X-ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) techniques. This study aims in investigating the mechanical behaviour of Zn-Fe coated mild steel specimens, as no research investigation concerning the tensile behaviour of Zn alloy coated ferrous alloys has been reported in the past. The experimental results indicated that the ultimate tensile strength of the Zn-Fe coated mild steel was lower than the bare mild steel. In addition, the ductility of the Zn-Fe coated mild steel was found to decrease significantly with increasing Fe content in the coating.

  10. Effect of mechanical alloying on FeCrC reinforced Ni alloys

    Energy Technology Data Exchange (ETDEWEB)

    Yilmaz, S. Osman [Univ. of Namik Kemal, Tekirdag (Turkey); Teker, Tanju [Adiyaman Univ. (Turkey). Dept. of Metallurgical and Materials Engineering; Demir, Fatih [Batman Univ. (Turkey)

    2016-05-01

    Mechanical alloying (MA) is a powder metallurgy processing technique involving cold welding, fracturing and rewelding of powder particles in a high-energy ball mill. In the present study, the intermetallic matrix composites (IMCs) of Ni-Al reinforced by M{sub 7}C{sub 3} were produced by powder metallurgical routes via solid state reaction of Ni, Al and M{sub 7}C{sub 3} particulates by mechanical alloying processes. Ni, Al and M{sub 7}C{sub 3} powders having 100 μm were mixed, mechanical alloyed and the compacts were combusted in a furnace. The mechanically alloyed (MAed) powders were investigated by X-ray diffraction (XRD), microhardness measurement, optic microscopy (OM), scanning electron microscopy (SEM) and energy dispersive spectrometry (EDS). The presence of the carbides depressed the formation of unwanted NiAl intermetallic phases. The mechanical alloyed M{sub 7}C{sub 3} particles were unstable and decomposed partially within the matrix during alloying and sintering, and the morphology of the composites changed with the dissolution ratio of M{sub 7}C{sub 3} and sintering temperature.

  11. Enhancing Microstructure and Mechanical Properties of AZ31-MWCNT Nanocomposites through Mechanical Alloying

    Directory of Open Access Journals (Sweden)

    J. Jayakumar

    2013-01-01

    Full Text Available Multiwall carbon nanotubes (MWCNTs reinforced Mg alloy AZ31 nanocomposites were fabricated by mechanical alloying and powder metallurgy technique. The reinforcement material MWCNTs were blended in three weight fractions (0.33%, 0.66%, and 1% with the matrix material AZ31 (Al-3%, zinc-1% rest Mg and blended through mechanical alloying using a high energy planetary ball mill. Specimens of monolithic AZ31 and AZ31-MWCNT composites were fabricated through powder metallurgy technique. The microstructure, density, hardness, porosity, ductility, and tensile properties of monolithic AZ31 and AZ31-MWCNT nano composites were characterized and compared. The characterization reveals significant reduction in CNT (carbon nanoTube agglomeration and enhancement in microstructure and mechanical properties due to mechanical alloying through ball milling.

  12. Synthesis of Nb-18%Al alloy by mechanical alloying method

    International Nuclear Information System (INIS)

    Dymek, S.; Wrobel, M.; Dollar, M.

    1999-01-01

    The main goal of this study was attempt to employ by mechanical alloying to produce Nb-Al alloy. The Nb-rich alloy composition was selected in order to receive the ductile niobium solid solution (Nb ss ) phase in the final, equilibrium state. This ductile phase was believed to prevent crack propagation in the consolidated alloy and thus to improve its ductility and toughness. Elemental powders of niobium (99.8% pure and -325 mesh) and aluminium (99.9% pure and -325 mesh) were used as starting materials. These powders were mixed to give the nominal compositions od 82% Nb and 18% Al (atomic percent). Mechanical alloying was carried out in a Szegvari laboratory attritor mill in an argon atmosphere with the controlled oxygen level reduced to less than 10 ppm. The total milling time was 86 hours. During the course of milling powder samples were taken out after 5, 10 and 20 hours, which allowed characterization of the powder morphology and progress of the mechanical alloying process. The changes in particle morphology during milling were examined using a scanning electron microscope and the phase analysis was performed in a X-ray diffractometer with CoK α radiation. Initially, particles' size increased and their appearance changed from the regular to one of the flaky shape. X-ray diffraction patterns of examined powders as a function of milling time are presented. Peaks from Al, through much weaker than in the starting material, were still present after 5 hours of milling but disappeared completely after 10 hours of milling. With increasing milling time, the peaks became broader and their intensities decreased. Formation of amorphous phase was observed after 86 hours of milling. This was deducted from a diffuse halo observed at the 2Θ angle of about 27 o . Intermetallic phases Nb 3 Al and Nb 2 Al were found in the consolidated material only. (author)

  13. Modeling and Analysis of Mechanical Properties of Aluminium Alloy (A413 Processed through Squeeze Casting Route Using Artificial Neural Network Model and Statistical Technique

    Directory of Open Access Journals (Sweden)

    R. Soundararajan

    2015-01-01

    Full Text Available Artificial Neural Network (ANN approach was used for predicting and analyzing the mechanical properties of A413 aluminum alloy produced by squeeze casting route. The experiments are carried out with different controlled input variables such as squeeze pressure, die preheating temperature, and melt temperature as per Full Factorial Design (FFD. The accounted absolute process variables produce a casting with pore-free and ideal fine grain dendritic structure resulting in good mechanical properties such as hardness, ultimate tensile strength, and yield strength. As a primary objective, a feed forward back propagation ANN model has been developed with different architectures for ensuring the definiteness of the values. The developed model along with its predicted data was in good agreement with the experimental data, inferring the valuable performance of the optimal model. From the work it was ascertained that, for castings produced by squeeze casting route, the ANN is an alternative method for predicting the mechanical properties and appropriate results can be estimated rather than measured, thereby reducing the testing time and cost. As a secondary objective, quantitative and statistical analysis was performed in order to evaluate the effect of process parameters on the mechanical properties of the castings.

  14. A Review of Dissimilar Welding Techniques for Magnesium Alloys to Aluminum Alloys

    Directory of Open Access Journals (Sweden)

    Liming Liu

    2014-05-01

    Full Text Available Welding of dissimilar magnesium alloys and aluminum alloys is an important issue because of their increasing applications in industries. In this document, the research and progress of a variety of welding techniques for joining dissimilar Mg alloys and Al alloys are reviewed from different perspectives. Welding of dissimilar Mg and Al is challenging due to the formation of brittle intermetallic compound (IMC such as Mg17Al12 and Mg2Al3. In order to increase the joint strength, three main research approaches were used to eliminate or reduce the Mg-Al intermetallic reaction layer. First, solid state welding techniques which have a low welding temperature were used to reduce the IMCs. Second, IMC variety and distribution were controlled to avoid the degradation of the joining strength in fusion welding. Third, techniques which have relatively controllable reaction time and energy were used to eliminate the IMCs. Some important processing parameters and their effects on weld quality are discussed, and the microstructure and metallurgical reaction are described. Mechanical properties of welds such as hardness, tensile, shear and fatigue strength are discussed. The aim of the report is to review the recent progress in the welding of dissimilar Mg and Al to provide a basis for follow-up research.

  15. A Review of Dissimilar Welding Techniques for Magnesium Alloys to Aluminum Alloys

    Science.gov (United States)

    Liu, Liming; Ren, Daxin; Liu, Fei

    2014-01-01

    Welding of dissimilar magnesium alloys and aluminum alloys is an important issue because of their increasing applications in industries. In this document, the research and progress of a variety of welding techniques for joining dissimilar Mg alloys and Al alloys are reviewed from different perspectives. Welding of dissimilar Mg and Al is challenging due to the formation of brittle intermetallic compound (IMC) such as Mg17Al12 and Mg2Al3. In order to increase the joint strength, three main research approaches were used to eliminate or reduce the Mg-Al intermetallic reaction layer. First, solid state welding techniques which have a low welding temperature were used to reduce the IMCs. Second, IMC variety and distribution were controlled to avoid the degradation of the joining strength in fusion welding. Third, techniques which have relatively controllable reaction time and energy were used to eliminate the IMCs. Some important processing parameters and their effects on weld quality are discussed, and the microstructure and metallurgical reaction are described. Mechanical properties of welds such as hardness, tensile, shear and fatigue strength are discussed. The aim of the report is to review the recent progress in the welding of dissimilar Mg and Al to provide a basis for follow-up research. PMID:28788646

  16. A Review of Dissimilar Welding Techniques for Magnesium Alloys to Aluminum Alloys.

    Science.gov (United States)

    Liu, Liming; Ren, Daxin; Liu, Fei

    2014-05-08

    Welding of dissimilar magnesium alloys and aluminum alloys is an important issue because of their increasing applications in industries. In this document, the research and progress of a variety of welding techniques for joining dissimilar Mg alloys and Al alloys are reviewed from different perspectives. Welding of dissimilar Mg and Al is challenging due to the formation of brittle intermetallic compound (IMC) such as Mg 17 Al 12 and Mg₂Al₃. In order to increase the joint strength, three main research approaches were used to eliminate or reduce the Mg-Al intermetallic reaction layer. First, solid state welding techniques which have a low welding temperature were used to reduce the IMCs. Second, IMC variety and distribution were controlled to avoid the degradation of the joining strength in fusion welding. Third, techniques which have relatively controllable reaction time and energy were used to eliminate the IMCs. Some important processing parameters and their effects on weld quality are discussed, and the microstructure and metallurgical reaction are described. Mechanical properties of welds such as hardness, tensile, shear and fatigue strength are discussed. The aim of the report is to review the recent progress in the welding of dissimilar Mg and Al to provide a basis for follow-up research.

  17. Self-Consolidation and Surface Modification of Mechanical Alloyed Ti-25.0 at.% Al Powder Mixture by Using an Electro-Discharge Technique

    Directory of Open Access Journals (Sweden)

    Chang S.Y.

    2017-06-01

    Full Text Available Electrical discharges using a capacitance of 450 μF at 0.5, 1.0, and 1.5 kJ input energies were applied in a N2 atmosphere to obtain the mechanical alloyed Ti3Al powder without applying any external pressure. A solid bulk of nanostructured Ti3Al was obtained as short as 160 μsec by the Electrical discharge. At the same time, the surface has been modified into the form of Ti and Al nitrides due to the diffusion process of nitrogen to the surface. The input energy was found to be the most important parameter to affect the formation of a solid core and surface chemistry of the compact.

  18. Inventory of alloy composition, microstructures and mechanical ...

    African Journals Online (AJOL)

    Inventory of alloy composition, microstructures and mechanical properties of automobile engine parts. ... Journal of Applied Science, Engineering and Technology ... This research work investigated the chemical compositions, microstructures and mechanical properties of the ferrous and non-ferrous auto engine parts such ...

  19. The development of additive manufacturing technique for nickel-base alloys: A review

    Science.gov (United States)

    Zadi-Maad, Ahmad; Basuki, Arif

    2018-04-01

    Nickel-base alloys are an attractive alloy due to its excellent mechanical properties, a high resistance to creep deformation, corrosion, and oxidation. However, it is a hard task to control performance when casting or forging for this material. In recent years, additive manufacturing (AM) process has been implemented to replace the conventional directional solidification process for the production of nickel-base alloys. Due to its potentially lower cost and flexibility manufacturing process, AM is considered as a substitute technique for the existing. This paper provides a comprehensive review of the previous work related to the AM techniques for Ni-base alloys while highlighting current challenges and methods to solving them. The properties of conventionally manufactured Ni-base alloys are also compared with the AM fabricated alloys. The mechanical properties obtained from tension, hardness and fatigue test are included, along with discussions of the effect of post-treatment process. Recommendations for further work are also provided.

  20. Kinetics and formation mechanism of amorphous Fe52Nb48 alloy powder fabricated by mechanical alloying

    International Nuclear Information System (INIS)

    El-Eskandarany, S.

    1999-01-01

    A single phase amorphous Fe 52 Nb 48 alloy has been synthesized through a solid state interdiffusion of pure polycrystalline Fe and Nb powders at room temperature, using a high-energy ball-milling technique. The mechanisms of metallic glass formation and competing crystallization processes in the mechanically deformed composite powders have been investigated by means of X-ray diffraction, Moessbauer spectroscopy, differential thermal analysis, scanning electron microscopy and transmission electron microscopy. The numerous intimate layered composite particles of the diffusion couples that formed during the first and intermediate stages of milling time (0-56 ks), are intermixed to form amorphous phase(s) upon heating to about 625 K by so-called thermally assisted solid state amorphization, TASSA. The amorphization heat of formation for binary system via the TASSA, ΔH a , was measured directly as a function of the milling time. Comparable with the TASSA, homogeneous amorphous alloys were fabricated directly without heating the composite multilayered particles upon milling these particles for longer milling time (86 ks-144 ks). The amorphization reaction here is attributed to the mechanical driven solid state amorphization. This single amorphous phase transforms into an order phase (μ phase) upon heating at 1088 K (crystallization temperature, T x ) with enthalpy change of crystallization, ΔH x , of -8.3 kJmol -1 . (orig.)

  1. Mechanical design of a shape memory alloy actuated prosthetic hand.

    Science.gov (United States)

    De Laurentis, Kathryn J; Mavroidis, Constantinos

    2002-01-01

    This paper presents the mechanical design for a new five fingered, twenty degree-of-freedom dexterous hand patterned after human anatomy and actuated by Shape Memory Alloy artificial muscles. Two experimental prototypes of a finger, one fabricated by traditional means and another fabricated by rapid prototyping techniques, are described and used to evaluate the design. An important aspect of the Rapid Prototype technique used here is that this multi-articulated hand will be fabricated in one step, without requiring assembly, while maintaining its desired mobility. The use of Shape Memory Alloy actuators combined with the rapid fabrication of the non-assembly type hand, reduce considerably its weight and fabrication time. Therefore, the focus of this paper is the mechanical design of a dexterous hand that combines Rapid Prototype techniques and smart actuators. The type of robotic hand described in this paper can be utilized for applications requiring low weight, compactness, and dexterity such as prosthetic devices, space and planetary exploration.

  2. Alloy design through mechanical equation of state

    International Nuclear Information System (INIS)

    Li, C.Yu.; Ellis, F.V.; Huang, F.H.

    1975-01-01

    The concept of plastic equation of state and the experimental results which are used to support this approach are introduced. It is shown that considerable savings in mechanical testing are possible in using this approach to establish the constitutive relationships for plastic deformation for a material. Advantages in data correlation and data extrapolation are also described. Examples are given to suggest that the constitutive relationships for plastic deformation obtained may be used as a useful basis for correlating the effects of composition and microstructure changes on mechanical properties and therefore serve as a guide for alloy selection. The savings in mechanical testing suggest also that the approach of plastic equation of state may be adopted for evaluating and assessing the mechanical properties of candidate alloys

  3. Mechanical Properties of Low Density Alloys at Cryogenic Temperatures

    International Nuclear Information System (INIS)

    Jiao, X. D.; Liu, H. J.; Li, L. F.; Yang, K.

    2006-01-01

    Low-density alloys include aluminum alloys, titanium alloys and magnesium alloys. Aluminum alloys and titanium alloys have been widely investigated and used as structural materials for cryogenic applications because of their light weight and good low-temperature mechanical properties.For aerospace applications, persistent efforts are being devoted to reducing weight and improving performance. Magnesium alloys are the lightest structural alloys among those mentioned above. Therefore, it is necessary to pay attention to magnesium alloys and to investigate their behaviors at cryogenic temperatures. In this paper, we have investigated the mechanical properties and microstructures of some magnesium alloys at cryogenic temperatures. Experimental results on both titanium and magnesium alloys are taken into account in considering these materials for space application

  4. Preparation and characterization of porous Mg-Zn-Ca alloy by space holder technique

    Science.gov (United States)

    Annur, D.; Lestari, Franciska P.; Erryani, A.; Sijabat, Fernando A.; G. P. Astawa, I. N.; Kartika, I.

    2018-04-01

    Magnesium had been recently researched as a future biodegradable implant material. In the recent study, porous Mg-Zn-Ca alloys were developed using space holder technique in powder metallurgy process. Carbamide (10-20%wt) was added into Mg-6Zn-1Ca (in wt%) alloy system as a space holder to create porous structure material. Sintering process was done in a tube furnace under Argon atmosphere in 610 °C for 5 hours. Porous structure of the resulted alloy was examined using Scanning Electron Microscope (SEM), while the phase formation was characterized by X-ray diffraction analysis (XRD). Further, mechanical properties of porous Mg-Zn-Ca alloy was examined through compression testing. Microstructure characterization showed higher content of Carbamide in the alloy would give different type of pores. However, compression test showed that mechanical properties of Mg-Zn-Ca alloy would decrease significantly when higher content of carbamide was added.

  5. High temperature mechanical forming of Mg alloys

    International Nuclear Information System (INIS)

    Mwembela, A.; McQueen, H.J.; Myshlyaev, M.

    2002-01-01

    Mg alloys are hot worked in the range 180-450 o C and 0.0-10 s -1 ; the present project data are compared with a wide selection of published results. The flow stresses and their dependence on temperature and strain rate are fairly similar to simple Al alloys: however, the hot ductility is much lower (≤3 in torsion). Twinning plays a significant role in Mg alloys almost independently of temperature; the twins initiate at low strains in grains poorly oriented for basal slip and in consequence become well disposed for such slip. As T rises, there is increasing formation of subgrains that spread toward the grain centers from grain and twin boundaries: this is indicative of stress concentrations inducing non-basal sup which helps provide the geometrically necessary dislocations. Above about 240 o C, dynamic (DRX) nucleates at grain and twin boundaries, preferentially at intersections; this again is evidence of non-basal slip that provides the highly misoriented cells. The boundaries in which further strain concentrates producing further DRX. The microstructure remains very heterogeneous compared to the uniform dynamically recovered substructure in Al alloys, thus giving rise to the reduced ductility. These results are employed to interpret the mechanical and microstructural behavior of Mg alloys in extrusion, rolling and forging. (author)

  6. The quasicrystalline phase formation in Al-Cu-Cr alloys produced by mechanical alloying

    Energy Technology Data Exchange (ETDEWEB)

    Sviridova, T.A.; Shevchukov, A.P.; Shelekhov, E.V. [National University of Science and Technology ' MISIS' , Moscow 119049 (Russian Federation); Diakonov, D.L. [Bardin Central Research Institute for the Iron and Steel Industry, Moscow 105005 (Russian Federation); Tcherdyntsev, V.V.; Kaloshkin, S.D. [National University of Science and Technology ' MISIS' , Moscow 119049 (Russian Federation)

    2011-06-15

    Research highlights: > Formation of decagonal quasicrystalline phase in Al-Cu-Cr alloys. > Obtained decagonal phase belongs to D{sub 3} family of decagonal quasicrystals. > Decagonal phase has 1.26 nm periodicity along 10-fold axis. > Alloys were produced by combination of mechanical alloying and subsequent annealing. > Phase composition of as-milled powders depending on annealing temperature. - Abstract: Almost single-phase decagonal quasicrystal with periodicity of 1.26 nm along 10-fold axis was produced in Al{sub 69}Cu{sub 21}Cr{sub 10} and Al{sub 72.5}Cu{sub 16.5}Cr{sub 11} alloys using combination of mechanical alloying (MA) and subsequent annealing. Phase transformations of as-milled powders depending on annealing temperature in the range of 200-800 deg. C are examined. Since the transformations can be explained based on kinetic and thermodynamic reasons it seems that applied technique (short preliminary MA followed by the annealing) permits to produce the equilibrium phases rather than metastable ones.

  7. New technique for producing the alloys based on transition metals

    International Nuclear Information System (INIS)

    Dolukhanyan, S.K.; Aleksanyan, A.G.; Shekhtman, V.Sh.; Mantashyan, A.A.; Mayilyan, D.G.; Ter-Galstyan, O.P.

    2007-01-01

    In principle new technique was elaborated for obtaining the alloys of refractory metals by their hydrides compacting and following dehydrogenation. The elaborated technique is described. The conditions of alloys formation from different hydrides of appropriate metals was investigated in detail. The influence of the process parameters such as: chemical peculiarities, composition of source hydrides, phase transformation during dehydrogenation, etc. on the alloys formation were established. The binary and tertiary alloys of α and ω phases: Ti 0 .8Zr 0 .8; Ti 0 .66Zr 0 .33; Ti 0 .3Zr 0 .8; Ti 0 .2Zr 0 .8; Ti 0 .8Hf 0 .2; Ti 0 .6Hf 0 .4Ti 0 .66Zr 0 .23Hf 0 .11; etc were recieved. Using elaborated special hydride cycle, an earlier unknown effective process for formation of alloys of transition metals was realized. The dependence of final alloy structure on the composition of initial mixture and hydrogen content in source hydrides was established

  8. In vitro mechanical integrity of hydroxyapatite coated magnesium alloy

    International Nuclear Information System (INIS)

    Kannan, M Bobby; Orr, Lynnley

    2011-01-01

    The mechanical integrity of resorbable implants during service, especially in load bearing orthopaedic applications, is critical. The high degradation rate of resorbable magnesium and magnesium-based implants in body fluid may potentially cause premature in-service failure. In this study, a magnesium alloy (AZ91) was potentiostatically coated with hydroxyapatite at different cathodic voltages in an attempt to enhance the mechanical integrity. The mechanical integrity of the uncoated and hydroxyapatite coated alloys was evaluated after in vitro testing of the coated samples in simulated body fluid (SBF). The uncoated alloy showed 40% loss in the mechanical strength after five days exposure to SBF. However, the hydroxyapatite coated alloy exposed to SBF showed 20% improvement in the mechanical strength as compared to that of the uncoated alloy. The alloy coated potentiostatically at -2 V performed better than the -3 V coated alloy. The cross-sectional analysis of the coatings revealed relatively uniform coating thickness for the -2 V coated alloy, whereas the -3 V coated alloy exhibited areas of uneven coating. This can be attributed to the increase in hydrogen evolution on the alloy during -3 V coating as compared to -2 V coating. The scanning electron micrographs of the in vitro tested alloy revealed that hydroxyapatite coating significantly reduced the localized corrosion of the alloy, which is critical for better in-service mechanical integrity. Thus, the study suggests that the in vitro mechanical integrity of resorbable magnesium-based alloy can be improved by potentiostatic hydroxyapatite coating.

  9. In vitro mechanical integrity of hydroxyapatite coated magnesium alloy.

    Science.gov (United States)

    Kannan, M Bobby; Orr, Lynnley

    2011-08-01

    The mechanical integrity of resorbable implants during service, especially in load bearing orthopaedic applications, is critical. The high degradation rate of resorbable magnesium and magnesium-based implants in body fluid may potentially cause premature in-service failure. In this study, a magnesium alloy (AZ91) was potentiostatically coated with hydroxyapatite at different cathodic voltages in an attempt to enhance the mechanical integrity. The mechanical integrity of the uncoated and hydroxyapatite coated alloys was evaluated after in vitro testing of the coated samples in simulated body fluid (SBF). The uncoated alloy showed 40% loss in the mechanical strength after five days exposure to SBF. However, the hydroxyapatite coated alloy exposed to SBF showed 20% improvement in the mechanical strength as compared to that of the uncoated alloy. The alloy coated potentiostatically at -2 V performed better than the -3 V coated alloy. The cross-sectional analysis of the coatings revealed relatively uniform coating thickness for the -2 V coated alloy, whereas the -3 V coated alloy exhibited areas of uneven coating. This can be attributed to the increase in hydrogen evolution on the alloy during -3 V coating as compared to -2 V coating. The scanning electron micrographs of the in vitro tested alloy revealed that hydroxyapatite coating significantly reduced the localized corrosion of the alloy, which is critical for better in-service mechanical integrity. Thus, the study suggests that the in vitro mechanical integrity of resorbable magnesium-based alloy can be improved by potentiostatic hydroxyapatite coating. © 2011 IOP Publishing Ltd

  10. In vitro mechanical integrity of hydroxyapatite coated magnesium alloy

    Energy Technology Data Exchange (ETDEWEB)

    Kannan, M Bobby; Orr, Lynnley, E-mail: bobby.mathan@jcu.edu.au [Discipline of Chemical Engineering, School of Engineering and Physical Sciences, James Cook University, Townsville, Queensland 4811 (Australia)

    2011-08-15

    The mechanical integrity of resorbable implants during service, especially in load bearing orthopaedic applications, is critical. The high degradation rate of resorbable magnesium and magnesium-based implants in body fluid may potentially cause premature in-service failure. In this study, a magnesium alloy (AZ91) was potentiostatically coated with hydroxyapatite at different cathodic voltages in an attempt to enhance the mechanical integrity. The mechanical integrity of the uncoated and hydroxyapatite coated alloys was evaluated after in vitro testing of the coated samples in simulated body fluid (SBF). The uncoated alloy showed 40% loss in the mechanical strength after five days exposure to SBF. However, the hydroxyapatite coated alloy exposed to SBF showed 20% improvement in the mechanical strength as compared to that of the uncoated alloy. The alloy coated potentiostatically at -2 V performed better than the -3 V coated alloy. The cross-sectional analysis of the coatings revealed relatively uniform coating thickness for the -2 V coated alloy, whereas the -3 V coated alloy exhibited areas of uneven coating. This can be attributed to the increase in hydrogen evolution on the alloy during -3 V coating as compared to -2 V coating. The scanning electron micrographs of the in vitro tested alloy revealed that hydroxyapatite coating significantly reduced the localized corrosion of the alloy, which is critical for better in-service mechanical integrity. Thus, the study suggests that the in vitro mechanical integrity of resorbable magnesium-based alloy can be improved by potentiostatic hydroxyapatite coating.

  11. Nanostructured Al–Zn–Mg–Cu–Zr alloy prepared by mechanical alloying followed by hot pressing

    International Nuclear Information System (INIS)

    Azimi, Amin; Shokuhfar, Ali; Zolriasatein, Ashkan

    2014-01-01

    Nanostructured Al–7.8 wt% Zn–2.6 wt% Mg–2 wt% Cu–0.1 wt% Zr alloy was mechanically alloyed (MA) from elemental powders and consolidated by hot press technique. The effect of the milling time and hot pressing process on microstructure was investigated by means of X-ray diffraction measurements (XRD) and analytical and scanning electron microscopy (SEM). Furthermore mechanical properties of samples with different MA time as well as pure aluminum were investigated by microhardness and compression tests. The results show that an Al–Zn–Mg–Cu–Zr homogenous supersaturated solid solution with a crystallite size of 27 nm was obtained after 40 h of milling time. Microstructure refinement and morphological changes of powders from flake to spherical shape were observed by increasing milling time. Phase and microstructural characterization of high density bulk nanostructured samples revealed that increasing milling time up to 40 h leads to formation of MgZn 2 precipitation in the alloy matrix. With increasing milling time, density of the samples and crystalline size decrease. Significant enhancement of hardness and compressive strength is observed in the aluminum alloy by increasing milling time up to 40 h which is much higher than pure aluminum. Crystallite size refinement in pure aluminum samples from micro- to nanoscales resulted in 107% and 100% improvement in compressive strength and hardness, respectively. Furthermore the compressive strength and hardness of Al–Zn–Mg–Cu–Zr alloy nanostructured samples increased to 179% and 172%, respectively, compared to nanostructured pure Al, which was produced as reference specimen. 40 h of MA was the optimum case for preparing such an Al alloy and more milling up to 50 h led to deterioration of mechanical properties

  12. Formation of nano quasicrystalline and crystalline phases by mechanical alloying

    Energy Technology Data Exchange (ETDEWEB)

    Shamah, A.M.; Ibrahim, S. [Faculty of Petroleum and Mining Engineering, Suez Canal University, Suez (Egypt); Hanna, F.F., E-mail: fariedhanna@yahoo.com [Faculty of Petroleum and Mining Engineering, Suez Canal University, Suez (Egypt)

    2011-02-03

    Research highlights: > Mechanical alloying (MA) is an important method to investigate the formation of nano sized quasicrystalline phases in Al{sub 86}Cr{sub 14}, Al{sub 84}Fe{sub 16} and Al{sub 62.5}Cu{sub 25}Fe{sub 12.5} compounds. The second part of the present work is an attempt to examine the possibility of formation of the i-phase of the Al{sub 62.5}Cu{sub 25}Fe{sub 12.5}, which lies in the region of the perfect i-phase in the ternary phase diagram, by rapid solidification method. To perform the obtained quasi phase mechanical alloying and heat treatment at the rapid solidified sample were done. - Abstract: In the present work, the formation of nano quasicrystalline icosahedral phase in Al{sub 86}Cr{sub 14}, Al{sub 84}Fe{sub 16} and Al{sub 62.5}Cu{sub 25}Fe{sub 12.5} alloys has been investigated by mechanical alloying. Mixtures of quasicrystalline and related crystalline phases have been observed under various milling conditions. The X-ray diffraction, differential thermal analysis and electrical resistivity techniques have been used for characterization and physical property measurements. The particle size was calculated by X-ray profile using Williamson-Hall plot method and it was found to be 25-50 nm size.

  13. Formation of nano quasicrystalline and crystalline phases by mechanical alloying

    International Nuclear Information System (INIS)

    Shamah, A.M.; Ibrahim, S.; Hanna, F.F.

    2011-01-01

    Research highlights: → Mechanical alloying (MA) is an important method to investigate the formation of nano sized quasicrystalline phases in Al 86 Cr 14 , Al 84 Fe 16 and Al 62.5 Cu 25 Fe 12.5 compounds. The second part of the present work is an attempt to examine the possibility of formation of the i-phase of the Al 62.5 Cu 25 Fe 12.5 , which lies in the region of the perfect i-phase in the ternary phase diagram, by rapid solidification method. To perform the obtained quasi phase mechanical alloying and heat treatment at the rapid solidified sample were done. - Abstract: In the present work, the formation of nano quasicrystalline icosahedral phase in Al 86 Cr 14 , Al 84 Fe 16 and Al 62.5 Cu 25 Fe 12.5 alloys has been investigated by mechanical alloying. Mixtures of quasicrystalline and related crystalline phases have been observed under various milling conditions. The X-ray diffraction, differential thermal analysis and electrical resistivity techniques have been used for characterization and physical property measurements. The particle size was calculated by X-ray profile using Williamson-Hall plot method and it was found to be 25-50 nm size.

  14. Mechanical alloying and sitering of TI - 10WT.% MG powders

    CSIR Research Space (South Africa)

    Machio, Christopher N

    2009-06-01

    Full Text Available A Ti-10wt.%Mg powder alloy has been produced by mechanical alloying. Elemental powders of Ti and Mg were ball milled in a Zoz-Simoloyer CM01 for 16 and 20 hours under argon. Mechanical alloying was followed by XRD, SEM and particle size analysis...

  15. Microstructure and mechanical properties of laser treated aluminium alloys

    NARCIS (Netherlands)

    deHosson, JTM; vanOtterloo, LDM; Noordhuis, J; Mazumder, J; Conde, O; Villar, R; Steen, W

    1996-01-01

    Al-Cu alloys and an Al-Cu-Mg alloy, Al 2024-T3, were exposed to laser treatments at various scan velocities. In this paper the microstructural features and mechanical properties are reported. As far as the mechanical property of the Al-Cu-Mg alloy is concerned a striking observation is a minimum in

  16. Grain refinement mechanism in A3003 alloy

    International Nuclear Information System (INIS)

    Cho, Hoon; Shin, Je-Sik; Lee, Byoung-Soo; Jo, Hyung-Ho

    2009-01-01

    In the present study, in order to find out an grain refinement mechanism, 0.1wt.% Al-10wt.%Ti master alloy was added into A3003 alloy melt contained in graphite crucible and in alumina crucible, and then the melt holding time at 750 deg. C was systematically changed from 1 min up to 120 min. It is interesting to note that the grain refinement and fading phenomena remarkably depend on the crucible material. The fading effect in the specimens using alumina crucible can be explained as the result of TiAl 3 phase dissolution into molten aluminium matrix. In the specimens using graphite crucible, the grain refinement was occurred gradually with increasing holding time. It was suggest that the continuous grain refinement is due to transition of refinement mechanism from TiAl 3 phase to TiC phase. It can be mentioned that the TiC formed from titanium and carbon solute in the aluminium melt, which came from the Al-10Ti alloy and the graphite crucible.

  17. Mechanical Behavior of an Ultrafine/Nano Grained Magnesium Alloy

    Directory of Open Access Journals (Sweden)

    Seyed Mahmood Fatemi

    2017-06-01

    Full Text Available The application of magnesium alloys is greatly limited because of their relatively low strength and ductility. An effective way to improve the mechanical properties of magnesium alloy is to refine the grains. As the race for better materials performance is never ending, attempts to develop viable techniques for microstructure refinement continue. Further refining of grain size requires, however, application of extreme value of plastic deformation on material. In this work, an AZ31 wrought magnesium alloy was processed by employing multipass accumulative back extrusion process. The obtained microstructure, texture, and room temperature compressive properties were characterized and discussed. The results indicated that grains of 80 nm to 1 μm size were formed during accumulative back extrusion, where the mean grain size of the experimental material was reduced by applying successive ABE passes. The fraction of DRX increased and the mean grain size of the ABEed alloy markedly lowered, as subsequent passes were applied. This helped to explain the higher yield stress govern the occurrence of twinning during compressive loading. Compressive yield and maximum compressive strengths were measured to increase by applying successive extrusion passes, while the strain-to-fracture dropped. The evolution of mechanical properties was explained relying on the grain refinement effect as well as texture change.

  18. Development the Mechanical Properties of (AL-Li-Cu Alloy

    Directory of Open Access Journals (Sweden)

    Ihsan Kadhom AlNaimi

    2017-11-01

    Full Text Available The aim of this research is to develop mechanical properties of a new aluminium-lithium-copper alloy. This alloy prepared under control atmosphere by casting in a permanent metal mould. The microstructure was examined and mechanical properties were tested before and after heat treatment to study the influence of heat treatment on its mechanical properties including; modulus of elasticity, tensile strength, impact, and fatigue. The results showed that the modulus of elasticity of the prepared alloy is higher than standard alloy about 2%. While the alloy that heat treated for 6 h and cooled in water, then showed a higher ultimate tensile stress comparing with as-cast alloy. The homogenous heat treatment gives best fatigue behaviour comparing with as-cast and other heat treatment alloys. Also, the impact test illustrates that the homogeneous heat treatment alloy gives the highest value.

  19. Investigation on mechanical alloying process for v-cr-ti alloys

    International Nuclear Information System (INIS)

    Stanciulescu, M.; Carlan, P.; Mihalache, M.; Bucsa, G.; Abrudeanu, M.; Galateanu, A.

    2015-01-01

    Mechanical alloying (MA) is an efficient approach for fabricating oxide-dispersion alloys and structural materials including vanadium alloys for fusion and fission application. Dissolution behaviour of the alloying elements is a key issue for optimizing the mechanical alloying process in fabricating vanadium alloys. This paper studies the MA process of V-4wt.%Cr-4wt.%Ti alloy. The outcomes of the MA powders in a planetary ball mill are reported in terms of powder particle size and morphology evolution and elemental composition. The impact of spark-plasma sintering process on the mechanically alloyed powder is analysed. An optimal set of sintering parameters, including the maximum temperature, the dwell time and the heating rate are determined. (authors)

  20. Characterization of Ni–Cr alloys using different casting techniques and molds

    International Nuclear Information System (INIS)

    Chen, Wen-Cheng; Teng, Fu-Yuan; Hung, Chun-Cheng

    2014-01-01

    This study differentiated the mechanical properties of nickel–chromium (Ni–Cr) alloys under various casting techniques (different casting molds and casting atmospheres). These techniques were sampled by a sand mold using a centrifugal machine in ambient air (group I) and electromagnetic induction in an automatic argon castimatic casting machine (group II). The specimen casting used a graphite mold by a castimatic casting machine (group III). The characteristics of the Ni–Cr alloys, yield and ultimate tensile strength, bending modulus, microhardness, diffraction phase, grindability, ability to spring back, as well as ground microstructure and pattern under different casting conditions were evaluated. The group III specimens exhibited the highest values in terms of strength, modulus, hardness, and grindability at a grind rate of 500 rpm. Moreover, group III alloys exhibited smaller grain sizes, higher ability to spring back, and greater ductility than those casted by sand investment (groups I and II). The main factor, “casting mold,” significantly influenced all mechanical properties. The graphite mold casting of the Ni–Cr dental alloys in a controlled atmosphere argon casting system provided an excellent combination of high mechanical properties and good ability to spring back, and preserved the ductile properties for application in Ni–Cr porcelain-fused system. The results can offer recommendations to assist a prosthetic technician in selecting the appropriate casting techniques to obtain the desired alloy properties. - Highlights: • Properties of Ni–Cr alloys using various casting techniques are characterized. • Alloys cast by graphite mold exhibited higher recovery angle and more ductility. • Alloys cast by graphite mold exhibited higher strength and grinding rate. • Alloys in this study increase operative room to adjust the precision for prosthesis

  1. Characterization of Ni–Cr alloys using different casting techniques and molds

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Wen-Cheng, E-mail: wencchen@fcu.edu.tw [Advanced Medical Devices and Composites Laboratory, Department of Fiber and Composite Materials, College of Engineering, Feng Chia University, Taichung 40724, Taiwan (China); Teng, Fu-Yuan [Department of Dentistry, Kaohsiung Armed Forces General Hospital, Kaohsiung 802, Taiwan (China); School of Dentistry, College of Dental Medicine, Kaohsiung Medical University, Kaohsiung 807, Taiwan (China); Hung, Chun-Cheng [School of Dentistry, College of Dental Medicine, Kaohsiung Medical University, Kaohsiung 807, Taiwan (China); Department of Dentistry, Kaohsiung Medical University Hospital, Kaohsiung 807, Taiwan (China)

    2014-02-01

    This study differentiated the mechanical properties of nickel–chromium (Ni–Cr) alloys under various casting techniques (different casting molds and casting atmospheres). These techniques were sampled by a sand mold using a centrifugal machine in ambient air (group I) and electromagnetic induction in an automatic argon castimatic casting machine (group II). The specimen casting used a graphite mold by a castimatic casting machine (group III). The characteristics of the Ni–Cr alloys, yield and ultimate tensile strength, bending modulus, microhardness, diffraction phase, grindability, ability to spring back, as well as ground microstructure and pattern under different casting conditions were evaluated. The group III specimens exhibited the highest values in terms of strength, modulus, hardness, and grindability at a grind rate of 500 rpm. Moreover, group III alloys exhibited smaller grain sizes, higher ability to spring back, and greater ductility than those casted by sand investment (groups I and II). The main factor, “casting mold,” significantly influenced all mechanical properties. The graphite mold casting of the Ni–Cr dental alloys in a controlled atmosphere argon casting system provided an excellent combination of high mechanical properties and good ability to spring back, and preserved the ductile properties for application in Ni–Cr porcelain-fused system. The results can offer recommendations to assist a prosthetic technician in selecting the appropriate casting techniques to obtain the desired alloy properties. - Highlights: • Properties of Ni–Cr alloys using various casting techniques are characterized. • Alloys cast by graphite mold exhibited higher recovery angle and more ductility. • Alloys cast by graphite mold exhibited higher strength and grinding rate. • Alloys in this study increase operative room to adjust the precision for prosthesis.

  2. Application of mechanical alloying to synthesis of intermetallic phases based alloys

    International Nuclear Information System (INIS)

    Dymek, S.

    2001-01-01

    Mechanical alloying is the process of synthesis of powder materials during milling in high energetic mills, usually ball mills. The central event in mechanical alloying is the ball-powder-ball collision. Powder particles are trapped between the colliding balls during milling and undergo deformation and/or fracture. Fractured parts are cold welded. The continued fracture and cold welding results in a uniform size and chemical composition of powder particles. The main applications of mechanical alloying are: processing of ODS alloys, syntheses of intermetallic phases, synthesis of nonequilibrium structures (amorphous alloys, extended solid solutions, nanocrystalline, quasi crystals) and magnetic materials. The present paper deals with application of mechanical alloying to synthesis Ni A l base intermetallic phases as well as phases from the Nb-Al binary system. The alloy were processed from elemental powders. The course of milling was monitored by scanning electron microscopy and X-ray diffraction. After milling, the collected powders were sieved by 45 μm grid and hot pressed (Nb alloys and NiAl) or hot extruded (NiAl). The resulting material was fully dense and exhibited fine grain (< 1 μm) and uniform distribution of oxide dispersoid. The consolidated material was compression and creep tested. The mechanical properties of mechanically alloys were superior to properties of their cast counterparts both in the room and elevated temperatures. Higher strength of mechanically alloyed materials results from their fine grains and from the presence of dispersoid. At elevated temperatures, the Nb-Al alloys have higher compression strength than NiAl-based alloys processed at the same conditions. The minimum creep rates of mechanically alloyed Nb alloys are an order of magnitude lower than analogously processed NiAl-base alloys. (author)

  3. Mechanical properties of copper-lithium alloys produced by mechanic alloyed and hot extrusion

    International Nuclear Information System (INIS)

    Castillo B, Ricardo; Gorziglia S, Ezio; Penaloza V, Augusto

    2004-01-01

    In this work are presented the progress carried out on the characterization of some physical and mechanical properties, together with the determination of the micro mechanism of fracture of the Cu-2% wt Li, that was obtained by mechanical alloying followed hot extrusion at 500 o C and 700 o C. Hardness and tensile mechanical tests were performed together with metallographic and fractographic analysis. The experimental results obtained with powders of the Cu-Li alloy studied are compared with powder of pure copper, under similar test conditions. The results show that by hot extrusion was allowed to obtain very high densification levels for the materials under study. Moreover, it was found that lithium reduce both the tensile strength and elongation, of copper by a mechanism of embrittlement. The results are compares with the literature (au)

  4. General characteristics of eutectic alloy solidification mechanisms

    International Nuclear Information System (INIS)

    Lemaignan, Clement.

    1977-01-01

    The eutectic alloy sodification was studied in binary systems: solidification of non facetted - non facetted eutectic alloy (theoretical aspects, variation of the lamellar spacing, crystallographic relation between the various phases); solidification of facetted - non facetted eutectic alloy; coupled growth out of eutectic alloy; eutectic nucleation [fr

  5. Nucleation mechanisms of refined alpha microstructure in beta titanium alloys

    Science.gov (United States)

    Zheng, Yufeng

    Due to a great combination of physical and mechanical properties, beta titanium alloys have become promising candidates in the field of chemical industry, aerospace and biomedical materials. The microstructure of beta titanium alloys is the governing factor that determines their properties and performances, especially the size scale, distribution and volume fraction of precipitate phase in parent phase matrix. Therefore in order to enhance the performance of beta titanium alloys, it is critical to obtain a thorough understanding of microstructural evolution in beta titanium alloys upon various thermal and/or mechanical processes. The present work is focusing on the study of nucleation mechanisms of refined alpha microstructure and super-refined alpha microstructure in beta titanium alloys in order to study the influence of instabilities within parent phase matrix on precipitates nucleation, including compositional instabilities and/or structural instabilities. The current study is primarily conducted in Ti-5Al-5Mo-5V-3Cr (wt%, Ti-5553), a commercial material for aerospace application. Refined and super-refined precipitates microstructure in Ti-5553 are obtained under specific accurate temperature controlled heat treatments. The characteristics of either microstructure are investigated in details using various characterization techniques, such as SEM, TEM, STEM, HRSTEM and 3D atom probe to describe the features of microstructure in the aspect of morphology, distribution, structure and composition. Nucleation mechanisms of refined and super-refined precipitates are proposed in order to fully explain the features of different precipitates microstructure in Ti-5553. The necessary thermodynamic conditions and detailed process of phase transformations are introduced. In order to verify the reliability of proposed nucleation mechanisms, thermodynamic calculation and phase field modeling simulation are accomplished using the database of simple binary Ti-Mo system

  6. Synthesis of Amorphous Powders of Ni-Si and Co-Si Alloys by Mechanical Alloying

    Science.gov (United States)

    Omuro, Keisuke; Miura, Harumatsu

    1991-05-01

    Amorphous powders of the Ni-Si and Co-Si alloys are synthesized by mechanical alloying (MA) from crystalline elemental powders using a high energy ball mill. The alloying and amorphization process is examined by X-ray diffraction, differential scanning calorimetry (DSC), and scanning electron microscopy. For the Ni-Si alloy, it is confirmed that the crystallization temperature of the MA powder, measured by DSC, is in good agreement with that of the powder sample prepared by mechanical grinding from the cast alloy ingot products of the same composition.

  7. Shape memory alloys – characterization techniques

    Indian Academy of Sciences (India)

    DSC has been used successfully to characterize the recover- ... in 1932. The effect has been observed in many alloy systems, such as Cu–Zn, Cu–Zn–Al, ..... The author is grateful to Indian Space Research Organization (ISRO), Department of.

  8. Synthesis Of NiCrAlC alloys by mechanical alloying

    International Nuclear Information System (INIS)

    Silva, A.K.; Pereira, J.I.; Vurobi Junior, S.; Cintho, O.M.

    2010-01-01

    The purpose of the present paper is the synthesis of nickel alloys (NiCrAlC), which has been proposed like a economic alternative to the Stellite family Co alloys using mechanical alloying, followed by sintering heat treatment of milled material. The NiCrAlC alloys consist of a chromium carbides dispersion in a Ni 3 Al intermetallic matrix, that is easily synthesized by mechanical alloying. The use of mechanical alloying enables higher carbides sizes and distribution control in the matrix during sintering. We are also investigated the compaction of the processed materials by compressibility curves. The milling products were characterized by X-ray diffraction, and the end product was featured by conventional metallography and scanning electronic microscopy (SEM), that enabled the identification of desired phases, beyond microhardness test, which has been shown comparable to alloys manufactured by fusion after heat treating. (author)

  9. Mechanical and irradiation properties of zirconium alloys irradiated in HANARO

    International Nuclear Information System (INIS)

    Kwon, Oh Hyun; Eom, Kyong Bo; Kim, Jae Ik; Suh, Jung Min; Jeon, Kyeong Lak

    2011-01-01

    These experimental studies are carried out to build a database for analyzing fuel performance in nuclear power plants. In particular, this study focuses on the mechanical and irradiation properties of three kinds of zirconium alloy (Alloy A, Alloy B and Alloy C) irradiated in the HANARO (High-flux Advanced Neutron Application Reactor), one of the leading multipurpose research reactors in the world. Yield strength and ultimate tensile strength were measured to determine the mechanical properties before and after irradiation, while irradiation growth was measured for the irradiation properties. The samples for irradiation testing are classified by texture. For the irradiation condition, all samples were wrapped into the capsule (07M-13N) and irradiated in the HANARO for about 100 days (E > 1.0 MeV, 1.1 10 21 n/cm 2 ). These tests and results indicate that the mechanical properties of zirconium alloys are similar whether unirradiated or irradiated. Alloy B has shown the highest yield strength and tensile strength properties compared to other alloys in irradiated condition. Even though each of the zirconium alloys has a different alloying content, this content does not seem to affect the mechanical properties under an unirradiated condition and low fluence. And all the alloys have shown the tendency to increase in yield strength and ultimate tensile strength. Transverse specimens of each of the zirconium alloys have a slightly lower irradiation growth tendency than longitudinal specimens. However, for clear analysis of texture effects, further testing under higher irradiation conditions is needed

  10. Mechanical alloying in the Fe-Cu system

    DEFF Research Database (Denmark)

    Jiang, Jianzhong; Gente, C.; Bormann, R.

    1998-01-01

    The studies of mechanical alloying on the Fe-Cu system, as a model system for those with positive heats of mixing, are reviewed. Several problems involved in the mechanical alloying process are discussed. For example, (1) whether alloying occurs on an atomic level; (2) what the solid solubility...... in the Fe-Cu system is; (3) where the positive energy is stored in the alloys; (4) what the decomposition process of the supersaturated alloys is; and (5) what type of magnetic properties the new materials have. The elucidation of these problems will shed light on the understanding of the mechanisms...... for the preparation of materials under highly non-equilibrium conditions in systems with positive heats of mixing by mechanical alloying....

  11. The microstructural mechanism for mechanical property of LY2 aluminum alloy after laser shock processing

    International Nuclear Information System (INIS)

    Luo, Kai-yu; Lu, Jin-zhong; Zhang, Ling-feng; Zhong, Jun-wei; Guan, Hai-bing; Qian, Xiao-ming

    2010-01-01

    This paper described nanoindentation techniques for measuring thin films mechanical properties, including elastic modulus and nano-hardness. The effects of laser shock processing (LSP) on elastic modulus and nano-hardness of the sample manufactured by LY2 aluminum alloy were experimentally investigated by nanoindentation techniques. Transmission electron microscope (TEM) observations of the microstructures in different regions after LSP are carried out. Experimental results showed that the values of nano-hardness and elastic modulus in the laser-shocked region were obviously increased by 58.13% and 61.74% compared to those in the non-shocked region, respectively. The influences of LSP on microstructure and grain size of LY2 aluminum alloy were discussed, and the enhancement mechanism of LSP on nano-hardness and elastic modulus was also addressed.

  12. Mechanisms affecting swelling in alloys with precipitates

    International Nuclear Information System (INIS)

    Mansur, L.K.; Haynes, M.R.; Lee, E.H.

    1980-01-01

    In alloys under irradiation many mechanisms exist that couple phase instability to cavity swelling. These are compounded with the more familiar mechanisms associated with point defect behavior and the evolution of microstructure. The mechanisms may be classified according to three modes of operation. Some affect cavity swelling directly by cavity-precipitate particle association, others operate indirectly by precipitate-induced changes in sinks other than cavities and finally there are mechanisms that are mediated by precipitate-induced changes in the host matrix. The physics of one mechanism of each type is developed in detail and the results compared where possible to experimental measurements. In particular, we develop the theory necessary to treat the effects on swelling of precipitation-induced changes in overall sink density; precipitation-induced changes in point defect trapping by solute depletion and creation of precipitate particle-matrix interfacial trap sites; and preciwill come from waste wood available locally requiring minimal energy for recovery and transportation to the site. The applicant is strongly considering the use of a solar preheating unit anium southward as well as to deeper dened al half-lives with experimental ones, over a range of 24 orders of magnitude was obtained. This is a strong argument that the alpha decay could be considered a fission process with very high mass asymmetry and charge density asymmetry

  13. Mechanical Properties of Spray Cast 7XXX Series Aluminium Alloys

    OpenAIRE

    SALAMCI, Elmas

    2014-01-01

    Mechanical properties of spray deposited and extruded 7xxx series aluminium alloys were investigated in peak aged condition. To study the influence of Zn additions on the mechanical behaviour of spray deposited materials, three alloy compositions were selected, namely: SS70 (11.5% Zn), N707 (10.9% Zn) and 7075 (5.6% Zn). After ageing treatment, notched and unnotched specimens of spray deposited alloys were subjected to tensile tests at room temperature. Experimental results showed...

  14. Study of deformation and fracture micro mechanisms of titanium alloy Ti-6Al-4V using electron microscopy and and X-ray diffraction techniques; Estudo dos micromecanismo de deformacao e fratura da liga de titanio Ti-6Al-4V utizando-se tecnicas de microscopia eletronica e difracao de raios X

    Energy Technology Data Exchange (ETDEWEB)

    Morcelli, Aparecido Edilson

    2009-07-01

    This present work allowed the study of deformation and fracture micro mechanisms of titanium alloy Ti-6Al-4V, used commercially for the manufacture of metallic biomaterials. The techniques employed for the analysis of the material under study were: scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray diffraction (XRD). The study of the influence and behavior of the phases present in titanium alloys is important to evaluate the behavior of cracks in titanium alloys with high mechanical strength, which have fine alpha ({alpha}), beta ({beta}) and ({alpha}{+-}{beta}) microstructure, linking the presence of the phases with the strength of the material. The evaluation in situ of deformation and fracture micro mechanisms were performed by TEM and was also a study of phase transformations during cooling in titanium alloys, using the techniques of bright field, dark field and diffraction of electrons in the selected area. After heat treatment differences were observed between the amount of in relation to the original microstructure of the {beta} and {alpha} phases material for different conditions used in heat treatment applied to the alloy. The presence of lamellar microstructure formed during cooling in the {beta} field was observed, promoting the conversion of part of the secondary alpha structure in {beta} phase, which was trapped between the lamellar of alpha. (author)

  15. Mechanical behaviour of aluminium-lithium alloys

    Indian Academy of Sciences (India)

    Aluminium-lithium alloys hold promise of providing a breakthrough response to the crying need for lightweight alloys for use as structurals in aerospace applications. Considerable worldwide research has gone into developing a range of these alloys over the last three decades. As a result, substantial understanding has ...

  16. Ti-Pt Alloys form mechanical milling

    CSIR Research Space (South Africa)

    Nxumalo, S

    2009-12-01

    Full Text Available C maximum in these alloys. A few researchers have studied the martensitic transformation in TiPt alloys using arc melted cast samples. In this work high temperature shape memory alloys are targeted using powder metallurgy as a processing route....

  17. Microstructure and mechanical property of dual-directional-extruded Mg alloy AZ31

    International Nuclear Information System (INIS)

    Lu Liwei; Liu Tianmo; Jiang Shan; Pan Fushen; Liu Qing; Wang Zhongchang

    2010-01-01

    We report microstructure evolution and mechanical property of Mg alloy AZ31 processed by a new deformation technique, dual-directional extrusion (DDE). Using optical microscopy, scanning electron microscopy, and electron back scatter diffraction technique, we attribute the significant refinement of original coarse grains in the DDE-processed alloy to the occurrence of dynamic recrystallization. Moreover, we find that low temperature is crucial for yielding fine grain, which consequently results in high micro-hardness and yield stress, large fracture strain, and enhanced elongation. The improved mechanical properties are comparable or even superior to those of the alloy subjected to other deformation techniques, rendering the DDE a promising way for further tailoring properties of Mg-based alloys.

  18. New mechanical chemical equilibrium in the copper-zinc alloys obtained by mechanical alloying

    International Nuclear Information System (INIS)

    Dianez, M.J; Criado, J.M; Donoso, E; Diaz, G

    2006-01-01

    A series of copper zinc alloys have been synthesized in the entire composition range Cu10Zn to Cu70Zn respectively, by mechanical alloying at room temperature in a planetary high-energy mill. A mechanism is proposed for the mechanical alloying reaction of the copper and zinc. It is made clear that the mechanical treatment considerably extends the range of composition of the α phase up to a content of 41% zinc, instead of the 36% accepted by the conventional phase diagrams. Exact determinations of the phase α reticular parameter were carried out as a function of its composition which can be used to determine the zinc content of the brass α. The results show that a brass phase α may be obtained containing 49% zinc in samples that include a mixture of phases α and β' after reaching stationary state as a function of the milling time. The stability field of phases β' and γ also displace noticeably higher values than those expected from the conventional binary Cu-Zn diagram. This behavior has been explained as a function of the nanometric texture generated by the milling (CW)

  19. Characterization of Ni-Cr alloys using different casting techniques and molds.

    Science.gov (United States)

    Chen, Wen-Cheng; Teng, Fu-Yuan; Hung, Chun-Cheng

    2014-02-01

    This study differentiated the mechanical properties of nickel-chromium (Ni-Cr) alloys under various casting techniques (different casting molds and casting atmospheres). These techniques were sampled by a sand mold using a centrifugal machine in ambient air (group I) and electromagnetic induction in an automatic argon castimatic casting machine (group II). The specimen casting used a graphite mold by a castimatic casting machine (group III). The characteristics of the Ni-Cr alloys, yield and ultimate tensile strength, bending modulus, microhardness, diffraction phase, grindability, ability to spring back, as well as ground microstructure and pattern under different casting conditions were evaluated. The group III specimens exhibited the highest values in terms of strength, modulus, hardness, and grindability at a grind rate of 500 rpm. Moreover, group III alloys exhibited smaller grain sizes, higher ability to spring back, and greater ductility than those casted by sand investment (groups I and II). The main factor, "casting mold," significantly influenced all mechanical properties. The graphite mold casting of the Ni-Cr dental alloys in a controlled atmosphere argon casting system provided an excellent combination of high mechanical properties and good ability to spring back, and preserved the ductile properties for application in Ni-Cr porcelain-fused system. The results can offer recommendations to assist a prosthetic technician in selecting the appropriate casting techniques to obtain the desired alloy properties. Copyright © 2013 Elsevier B.V. All rights reserved.

  20. Effect of alloying Mo on mechanical strength and corrosion resistance of Zr-1% Sn-1% Nb-1% Fe alloy

    International Nuclear Information System (INIS)

    Sugondo

    2011-01-01

    It had been done research on Zr-1%Sn-1%Nb-1%Fe-(x)%Mo alloy. The ingot was prepared by means of electrical electrode technique. The chemical analysis was identified by XRF, the metallography examination was perform by an optical microscope, the hardness test was done by Vickers microhardness, and the corrosion test was done in autoclave. The objective of this research were making Zr-1%Sn-1%Nb-1%Fe-(x)%Mo alloy with Mo concentration; comparing effect of Mo concentration to metal characteristics of Zr-1%Sn-1%Nb-1%Fe which covered microstructure; composition homogeneity, mechanical strength; and corrosion resistance in steam, and determining the optimal Mo concentration in Zr-1%Sn-1%Nb-1%Fe-(x)% Mo alloy for nuclear fuel cladding which had corrosion resistance and high hardness. The results were as follow: The alloying Mo refined grains at concentration in between 0,1%-0,3% and the concentration more than that could coarsened grains. The hardness of the Zr-1%Sn-1%Nb-1%Fe-(x)%Mo alloy was controlled either by the flaw or the dislocation, the intersection of the harder alloying element, the solid solution of the alloying element and the second phase formation of ZrMo 2 . The corrosion rate of the Zr-1%Sn-1%Nb-1%Fe-(x)%Mo alloy was controlled by the second phase of ZrMo 2 . The 0.3% Mo concentration in Zr-1%Sn-1%Nb-1%Fe-(x)%Mo alloy was the best for second phase formation. The Mo concentration in between 0,3-0,5% in Zr-1%Sn-1%Nb-1%Fe-(x)%Mo alloy was good for the second phase formation and the solid solution. (author)

  1. Mechanism of serrated flow in binary Al-Li alloys

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, S.; Pink, E. [Austrian Academy of Sciences, Leoben (Austria). Erich-Schmid-Inst. of Solid State Physics; Krol, J. [Polish Academy of Sciences, Krakow (Poland). Alexander-Krupkowski-Inst. of Metallurgy and Materials Science

    1996-09-15

    The work on serrated flow in Al-Li alloys has given rise to a controversy--whether serrations in these alloys are caused by lithium atoms in solid solution or by {delta}{prime}(Al{sub 3}Li)-precipitates. This controversy calls for further work to clarify the mechanism of serrated flow in the Al-Li alloys. Kumar and McShane have shown that in an Al-2.5Li-2Mg-0.14Zr alloy, non-shearable {delta}{prime}-precipitates, which are obtained in the under-aged and peak-aged conditions, might directly initiate serrated flow. However, the latter result was ambiguous because of the presence of other alloying elements, and the need to work on a binary Al-Li alloy was emphasized. The present work discusses the results from the binary Al-Li alloys.

  2. Modeling of mechanical properties in alpha/beta-titanium alloys

    Science.gov (United States)

    Kar, Sujoy Kumar

    2005-11-01

    The accelerated insertion of titanium alloys in component application requires the development of predictive capabilities for various aspects of their behavior, for example, phase stability, microstructural evolution and property-microstructure relationships over a wide range of length and time scales. In this presentation some navel aspects of property-microstructure relationships and microstructural evolution in alpha/beta Ti alloys will be discussed. Neural Network (NN) Models based on a Bayesian framework have been developed to predict the mechanical properties of alpha/beta Ti alloys. The development of such rules-based model requires the population of extensive databases, which in the present case are microstructurally-based. The steps involved in database development include producing controlled variations of the microstructure using novel approaches to heat-treatments, the use of standardized stereology protocols to characterize and quantify microstructural features rapidly, and mechanical testing of the heat-treated specimens. These databases have been used to train and test NN Models for prediction of mechanical properties. In addition, these models have been used to identify the influence of individual microstructural features on the mechanical properties, consequently guiding the efforts towards development of more robust mechanistically based models. In order to understand the property-microstructure relationships, a detailed understanding of microstructure evolution is imperative. The crystallography of the microstructure developing as a result of the solid-state beta → beta+alpha transformation has been studied in detail by employing Scanning Electron Microscopy (SEM), Orientation Imaging Microscopy (in a high resolution SEM), site-specific TEM sample preparation using focused ion beam, and TEM based techniques. The influence of variant selection on the evolution of microstructure will be specifically addressed.

  3. Local atomic order in nanocrystalline Fe-based alloys obtained by mechanical alloying

    International Nuclear Information System (INIS)

    Jartych, E.

    2003-01-01

    Using the 57 Fe Moessbauer spectroscopy, a local atomic order in nanocrystalline alloys of iron with Al, Ni, W and Mo has been determined. Alloys were prepared by mechanical alloying method. Analysis of Moessbauer spectra was performed on the basis of the local environment model in terms of Warren-Cowley parameters. It was shown that impurity atoms are not randomly distributed in the volume of the first and the second co-ordination spheres of 57 Fe nuclei and they form clusters

  4. Experimental study of microstructure, mechanical and tribological properties of cBN particulates SS316 alloy based MMCs fabricated by DMLS technique

    Energy Technology Data Exchange (ETDEWEB)

    Hussain, M.; Mandal, V.; Singh, P. K.; Kumar, P.; Kumar, V.; Das, A. K. [Indian Institute of Technology (ISM), Dhanbad (India)

    2017-06-15

    Direct metal laser sintering process (DMLS) was chosen to develop cBN particulates reinforced SS316 based Metal matrix composite (MMC) with 5 %, 7.5 % and 10 % cBN in the nitrogen gas atmosphere using continuous wave fibre laser of 400 W output capacity. Effects of process parameters such as laser power, beam scanning speed and the mixing ratio of powder on different physical properties of the developed MMC were investigated. It was found that the physical and mechanical properties such as friction and wear behavior, micro hardness and density come up with improved results. FESEM images indicate the microstructure of the composite and evidently confirms the presence of cubic boron nitride in the SS316 matrix where chromium nitride acted as a binder in the presence of nitrogen atmosphere. The Vickers hardness values of the developed MMCs with laser power 60 W and 65 W were found in the range of 276-478 HV{sub 0}.2 and 297-460 HV{sub 0}.2, respectively. It was found that Vickers hardness is directly proportional to the % of cBN in the powder mixture and the laser beam power. The wear resistance of the sintered MMCs increased with increasing cBN content in powder mixture and re- sults show that wear of MMCs are much lower than that of SS316. X-Ray diffraction (XRD) analysis of the fabricated MMC confirms the presence of different phases such as cBN, CrN, CrB{sub 2}, Cr{sub 2}N and Fe{sub 3}N as a consequence of a series of chemical reaction between cBN and different elements of SS316 in nitrogen atmosphere.

  5. Experimental study of microstructure, mechanical and tribological properties of cBN particulates SS316 alloy based MMCs fabricated by DMLS technique

    International Nuclear Information System (INIS)

    Hussain, M.; Mandal, V.; Singh, P. K.; Kumar, P.; Kumar, V.; Das, A. K.

    2017-01-01

    Direct metal laser sintering process (DMLS) was chosen to develop cBN particulates reinforced SS316 based Metal matrix composite (MMC) with 5 %, 7.5 % and 10 % cBN in the nitrogen gas atmosphere using continuous wave fibre laser of 400 W output capacity. Effects of process parameters such as laser power, beam scanning speed and the mixing ratio of powder on different physical properties of the developed MMC were investigated. It was found that the physical and mechanical properties such as friction and wear behavior, micro hardness and density come up with improved results. FESEM images indicate the microstructure of the composite and evidently confirms the presence of cubic boron nitride in the SS316 matrix where chromium nitride acted as a binder in the presence of nitrogen atmosphere. The Vickers hardness values of the developed MMCs with laser power 60 W and 65 W were found in the range of 276-478 HV_0.2 and 297-460 HV_0.2, respectively. It was found that Vickers hardness is directly proportional to the % of cBN in the powder mixture and the laser beam power. The wear resistance of the sintered MMCs increased with increasing cBN content in powder mixture and re- sults show that wear of MMCs are much lower than that of SS316. X-Ray diffraction (XRD) analysis of the fabricated MMC confirms the presence of different phases such as cBN, CrN, CrB_2, Cr_2N and Fe_3N as a consequence of a series of chemical reaction between cBN and different elements of SS316 in nitrogen atmosphere.

  6. Mechanical and corrosion resistance of a new nanostructured Ti-Zr-Ta-Nb alloy.

    Science.gov (United States)

    Raducanu, D; Vasilescu, E; Cojocaru, V D; Cinca, I; Drob, P; Vasilescu, C; Drob, S I

    2011-10-01

    In this work, a multi-elementary Ti-10Zr-5Nb-5Ta alloy, with non-toxic alloying elements, was used to develop an accumulative roll bonding, ARB-type procedure in order to improve its structural and mechanical properties. The alloy was obtained by cold crucible semi-levitation melting technique and then was ARB deformed following a special route. After three ARB cycles, the total deformation degree per layer is about 86%; the calculated medium layer thickness is about 13 μm. The ARB processed alloy has a low Young's modulus of 46 GPa, a value very close to the value of the natural cortical bone (about 20 GPa). Data concerning ultimate tensile strength obtained for ARB processed alloy is rather high, suitable to be used as a material for bone substitute. Hardness of the ARB processed alloy is higher than that of the as-cast alloy, ensuring a better behaviour as a implant material. The tensile curve for the as-cast alloy shows an elastoplastic behaviour with a quite linear elastic behaviour and the tensile curve for the ARB processed alloy is quite similar with a strain-hardening elastoplastic body. Corrosion behaviour of the studied alloy revealed the improvement of the main electrochemical parameters, as a result of the positive influence of ARB processing. Lower corrosion and ion release rates for the ARB processed alloy than for the as-cast alloy, due to the favourable effect of ARB thermo-mechanical processing were obtained. Copyright © 2011 Elsevier Ltd. All rights reserved.

  7. Synthesis and Characterization of Nanocrystalline Al-20 at. % Cu Powders Produced by Mechanical Alloying

    Directory of Open Access Journals (Sweden)

    Molka Ben Makhlouf

    2016-06-01

    Full Text Available Mechanical alloying is a powder processing technique used to process materials farther from equilibrium state. This technique is mainly used to process difficult-to-alloy materials in which the solid solubility is limited and to process materials where nonequilibrium phases cannot be produced at room temperature through conventional processing techniques. This work deals with the microstructural properties of the Al-20 at. % Cu alloy prepared by high-energy ball milling of elemental aluminum and copper powders. The ball milling of powders was carried out in a planetary mill in order to obtain a nanostructured Al-20 at. % Cu alloy. The obtained powders were characterized using scanning electron microscopy (SEM, differential scanning calorimetry (DSC and X-ray diffraction (XRD. The structural modifications at different stages of the ball milling are investigated with X-ray diffraction. Several microstructure parameters such as the crystallite sizes, microstrains and lattice parameters are determined.

  8. Microstructural characterization of mechanically alloyed Al–Cu–Mn alloy with zirconium

    Energy Technology Data Exchange (ETDEWEB)

    Prosviryakov, A.S., E-mail: pro.alex@mail.ru; Shcherbachev, K.D.; Tabachkova, N.Yu.

    2015-01-19

    An evolution of Al–Cu–Mn alloy microstructure during its mechanical alloying with zirconium 20 wt% and after subsequent annealing was studied by X-ray diffraction, light microscopy and transmission electron microscopy. The effect of milling time on powder microhardness, Al lattice parameter, lattice microstrain and crystallite size was determined.

  9. Microstructure and mechanical properties of Cu-Ni-Si alloys

    International Nuclear Information System (INIS)

    Monzen, Ryoichi; Watanabe, Chihiro

    2008-01-01

    The microstructure and mechanical properties of 0.1 wt.% Mg-added and Mg-free Cu-2.0 wt.% Ni-0.5 wt.% Si alloys aged at 400 deg. C have been examined. The addition of Mg promotes the formation of disk-shaped Ni 2 Si precipitates. The Cu-Ni-Si-Mg alloy exhibits higher strength and resistance to stress relaxation than the Cu-Ni-Si alloy. The higher strength or stress relaxation resistance is attributable to the reduction in inter-precipitate spacing by the Mg addition or the drag effect of Mg atoms on dislocation motion. The Cu-Ni-Si alloy with a large grain size of 150 μm shows higher stress relaxation resistance than the alloy with a small grain size of 10 μm because of a lower density of mobile dislocations in the former alloy

  10. Microstructure and mechanical properties of Cu-Ni-Si alloys

    Energy Technology Data Exchange (ETDEWEB)

    Monzen, Ryoichi [Division of Innovative Technology and Science, Graduate School of Natural Science and Technology, Kanzawa University, Kakuma-machi, Kanazawa 920-1192 (Japan)], E-mail: monzen@t.kanazawa-u.ac.jp; Watanabe, Chihiro [Division of Innovative Technology and Science, Graduate School of Natural Science and Technology, Kanzawa University, Kakuma-machi, Kanazawa 920-1192 (Japan)

    2008-06-15

    The microstructure and mechanical properties of 0.1 wt.% Mg-added and Mg-free Cu-2.0 wt.% Ni-0.5 wt.% Si alloys aged at 400 deg. C have been examined. The addition of Mg promotes the formation of disk-shaped Ni{sub 2}Si precipitates. The Cu-Ni-Si-Mg alloy exhibits higher strength and resistance to stress relaxation than the Cu-Ni-Si alloy. The higher strength or stress relaxation resistance is attributable to the reduction in inter-precipitate spacing by the Mg addition or the drag effect of Mg atoms on dislocation motion. The Cu-Ni-Si alloy with a large grain size of 150 {mu}m shows higher stress relaxation resistance than the alloy with a small grain size of 10 {mu}m because of a lower density of mobile dislocations in the former alloy.

  11. High-temperature deformation of a mechanically alloyed niobium-yttria alloy

    International Nuclear Information System (INIS)

    Chou, I.; Koss, D.A.; Howell, P.R.; Ramani, A.S.

    1997-01-01

    Mechanical alloying (MA) and hot isostatic pressing have been used to process two Nb alloys containing yttria particles, Nb-2 vol.%Y 2 O 3 and Nb-10 vol.%Y 2 O 3 . Similar to some thermomechanically processed nickel-based alloys, both alloys exhibit partially recrystallized microstructures, consisting of a 'necklace' of small recrystallized grains surrounding much larger but isolated, unrecrystallized, cold-worked grains. Hot compression tests from 1049 to 1347 C (0.5-0.6T MP ) of the 10% Y 2 O 3 alloy show that MA material possesses a much higher yield and creep strength than its powder-blended, fully recrystallized counterpart. In fact, the density-compensated specific yield strength of the MA Nb-10Y 2 O 3 exceeds that of currently available commercial Nb alloys. (orig.)

  12. Large-Grain Tin-Rich Perovskite Films for Efficient Solar Cells via Metal Alloying Technique.

    Science.gov (United States)

    Tavakoli, Mohammad Mahdi; Zakeeruddin, Shaik Mohammed; Grätzel, Michael; Fan, Zhiyong

    2018-03-01

    Fast research progress on lead halide perovskite solar cells has been achieved in the past a few years. However, the presence of lead (Pb) in perovskite composition as a toxic element still remains a major issue for large-scale deployment. In this work, a novel and facile technique is presented to fabricate tin (Sn)-rich perovskite film using metal precursors and an alloying technique. Herein, the perovskite films are formed as a result of the reaction between Sn/Pb binary alloy metal precursors and methylammonium iodide (MAI) vapor in a chemical vapor deposition process carried out at 185 °C. It is found that in this approach the Pb/Sn precursors are first converted to (Pb/Sn)I 2 and further reaction with MAI vapor leads to the formation of perovskite films. By using Pb-Sn eutectic alloy, perovskite films with large grain sizes up to 5 µm can be grown directly from liquid phase metal. Consequently, using an alloying technique and this unique growth mechanism, a less-toxic and efficient perovskite solar cell with a power conversion efficiency (PCE) of 14.04% is demonstrated, while pure Sn and Pb perovskite solar cells prepared in this manner yield PCEs of 4.62% and 14.21%, respectively. It is found that this alloying technique can open up a new direction to further explore different alloy systems (binary or ternary alloys) with even lower melting point. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  13. Cermet Ni-ZrO2 by mechanical alloying

    International Nuclear Information System (INIS)

    Leite, Douglas Will

    2010-01-01

    The ZrO 2 and metallic Ni Cermet obtained by Mechanical Alloying - MA is studied in the present work with the objective to prepare solid oxide fuel cells anodes (SOFC). Metallic Ni is added under three different concentrations: 30, 40 and 50% volume. The millings were conducted in SPEX vibratory mill where the influence of milling time, process control additives efficiency, type and geometry of milling vessels were studied. The study of the influence of these variables was made under particle size analysis, surface area determination and resulting material morphology. The use of teflon vessel causes contamination by carbon. On the other side, steel vessel increases the contamination by metallic impurities. The several geometries projected and analyzed for the vessels showed that vessels with larger bottom radius (R.15) showed the best results. After conformation and sintering at 1300 degree C in argon atmosphere the samples reached densities between 60 and 80% of the theoretical density. Microstructures observed by scanning electron microscopy reveal good homogeneity in the Cermet phases distribution. The mechanical alloying technique was considered a good option to obtain Ni- ZrO 2 Cermet. (author)

  14. Effect of the mechanical processing on the mechanical properties of MA956 alloy. II. Mechanical characterization

    International Nuclear Information System (INIS)

    Chao, J.; Gonzalez-Doncel, G.

    1998-01-01

    The mechanical properties at room and low temperature of MA 956 alloy in some stages of their processing route are evaluated. In this study the influence of crystallographic orientation on plastic deformation and brittle fracture, strongly anisotropic phenomena, is also considered. It is concluded that even though MA 956 alloy was designated for high temperature applications it could be also used for cryogenic temperatures applications. (Author) 8 refs

  15. Microstructure and Mechanical Behavior of High-Entropy Alloys

    Science.gov (United States)

    Licavoli, Joseph J.; Gao, Michael C.; Sears, John S.; Jablonski, Paul D.; Hawk, Jeffrey A.

    2015-10-01

    High-entropy alloys (HEAs) have generated interest in recent years due to their unique positioning within the alloy world. By incorporating a number of elements in high proportion, usually of equal atomic percent, they have high configurational entropy, and thus, they hold the promise of interesting and useful properties such as enhanced strength and alloy stability. The present study investigates the mechanical behavior, fracture characteristics, and microstructure of two single-phase FCC HEAs CoCrFeNi and CoCrFeNiMn with some detailed attention given to melting, homogenization, and thermo-mechanical processing. Ingots approaching 8 kg in mass were made by vacuum induction melting to avoid the extrinsic factors inherent to small-scale laboratory button samples. A computationally based homogenization heat treatment was given to both alloys in order to eliminate any solidification segregation. The alloys were then fabricated in the usual way (forging, followed by hot rolling) with typical thermo-mechanical processing parameters employed. Transmission electron microscopy was subsequently used to assess the single-phase nature of the alloys prior to mechanical testing. Tensile specimens (ASTM E8) were prepared with tensile mechanical properties obtained from room temperature through 800 °C. Material from the gage section of selected tensile specimens was extracted to document room and elevated temperature deformation within the HEAs. Fracture surfaces were also examined to note fracture failure modes. The tensile behavior and selected tensile properties were compared with results in the literature for similar alloys.

  16. Microstructure and mechanical behavior of Al-Li-Zr alloys

    International Nuclear Information System (INIS)

    Wang, Wego; Wells, M.G.H.

    1991-01-01

    The mechanical properties of two Al-Li-Zr alloys, A and B, are determined at various heat treatment conditions. Alloy B was found to have superior mechanical properties. It shows improvements in yield strength by 31.2-56.2 MPa and in ultimate tensile strength by 14.7-40.7 MPa, and yet still has a 20-25 percent better elongation value. The microstructure and fracture surface were studied by SEM and TEM. A fracture surface with mixed ductile samples and brittle facets was observed in both tensile and notch tensile samples. The fracture was more localized in alloy A than alloy B. Both alloys exhibited good notch toughness with a notch tensile strength to yield a strength ratio larger than one for all heat treatment conditions. 32 refs

  17. Comparison of mechanical properties for several electrical spring contact alloys

    International Nuclear Information System (INIS)

    Nordstrom, T.V.

    1976-06-01

    Work was conducted to determine whether beryllium-nickel alloy 440 had mechanical properties which made it suitable as a substitute for the presently used precious metal contact alloys Paliney 7 and Neyoro G, in certain electrical contact applications. Possible areas of applicability for the alloy were where extremely low contact resistance was not necessary or in components encountering elevated temperatures above those presently seen in weapons applications. Evaluation of the alloy involved three major experimental areas: 1) measurement of the room temperature microplastic (epsilon approximately 10 -6 ) and macroplastic (epsilon approximately 10 -3 ) behavior of alloy 440 in various age hardening conditions, 2) determination of applied stress effects on stress relaxation or contact force loss and 3) measurement of elevated temperature mechanical properties and stress relaxation behavior. Similar measurements were also made on Neyoro G and Paliney 7 for comparison. The primary results of the study show that beryllium-nickel alloy 440 is from a mechanical properties standpoint, equal or superior to the presently used Paliney 7 and Neyoro G for normal Sandia requirements. For elevated temperature applications, alloy 440 has clearly superior mechanical properties

  18. Mechanical properties of soldered joints of niobium base alloys

    International Nuclear Information System (INIS)

    Grishin, V.L.

    1980-01-01

    Mechanical properties of soldered joints of niobium alloys widely distributed in industry: VN3, VN4, VN5A, VN5AE, VN5AEP etc., 0.6-1.2 mm thick are investigated. It is found out that the usage of zirconium-vanadium, titanium-tantalum solders for welding niobium base alloys permits to obtain soldered joints with satisfactory mechanical properties at elevated temperatures

  19. Multiscale simulation of mechanical properties of TiNb alloy

    Science.gov (United States)

    Nikonov, A. Yu.

    2017-12-01

    The article presents a numerical simulation of the mechanical properties of a Ti-Nb β-alloy on three different scales. The ab-initio approach is used to estimate the concentrations of the Ti alloy with required elastic properties. On the basis of molecular dynamics simulation, we calculate the adhesive force between individual particles of the alloy. The calculated dependence is implemented within the movable cellular automata method to determine the mechanical properties of Ti-Nb depending on the interparticle free space.

  20. Investigation of a hot-pressed Nb–Ti–Al alloy: Mechanical alloying, microstructure and mechanical property

    Energy Technology Data Exchange (ETDEWEB)

    Shi, Zhiwu; Wei, Hua; Zhang, Hongyu; Jin, Tao; Sun, Xiaofeng; Zheng, Qi, E-mail: qzheng@imr.ac.cn

    2016-01-10

    The Nb–23Ti–15Al (at%) alloy was prepared by mechanical alloying (MA) and hot-pressing (HPing). The microstructure evolution of powder particles during MA and its influence on the microstructure and mechanical properties of the hot-pressed (HPed) alloy have been investigated. The powder and HPed alloy were characterized via X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results indicate that particle size increases in the first stage and then decreases in the second stage during MA; as milling speed increases, mechanically alloyed (MAed) powder with convoluted elemental lamellae, homogeneous Nb solid-solution and an amorphous phase could be obtained respectively in 24 h. Higher homogeneity in microstructure and composition of the MAed powder particles promotes the precipitation of the δ phase and refines the β and Ti(O,C) phases in the HPed alloy. Moreover, due to the phase equilibrium changes caused by Fe and Cr in the amorphous powder, σ phase appears in the alloy as a stable phase instead of the δ phase. Properly MAed powder contributes to higher hardness of the HPed alloy, for reasons of microstructure refinement and sufficient precipitating of strengthening phases.

  1. Investigation of a hot-pressed Nb–Ti–Al alloy: Mechanical alloying, microstructure and mechanical property

    International Nuclear Information System (INIS)

    Shi, Zhiwu; Wei, Hua; Zhang, Hongyu; Jin, Tao; Sun, Xiaofeng; Zheng, Qi

    2016-01-01

    The Nb–23Ti–15Al (at%) alloy was prepared by mechanical alloying (MA) and hot-pressing (HPing). The microstructure evolution of powder particles during MA and its influence on the microstructure and mechanical properties of the hot-pressed (HPed) alloy have been investigated. The powder and HPed alloy were characterized via X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results indicate that particle size increases in the first stage and then decreases in the second stage during MA; as milling speed increases, mechanically alloyed (MAed) powder with convoluted elemental lamellae, homogeneous Nb solid-solution and an amorphous phase could be obtained respectively in 24 h. Higher homogeneity in microstructure and composition of the MAed powder particles promotes the precipitation of the δ phase and refines the β and Ti(O,C) phases in the HPed alloy. Moreover, due to the phase equilibrium changes caused by Fe and Cr in the amorphous powder, σ phase appears in the alloy as a stable phase instead of the δ phase. Properly MAed powder contributes to higher hardness of the HPed alloy, for reasons of microstructure refinement and sufficient precipitating of strengthening phases.

  2. Mechanical alloying nanotechnology, materials science and powder metallurgy

    CERN Document Server

    El-Eskandarany, M Sherif

    2015-01-01

    This book is a detailed introduction to mechanical alloying, offering guidelines on the necessary equipment and facilities needed to carry out the process and giving a fundamental background to the reactions taking place. El-Eskandarany, a leading authority on mechanical alloying, discusses the mechanism of powder consolidations using different powder compaction processes. A new chapter will also be included on thermal, mechanically-induced and electrical discharge-assisted mechanical milling. Fully updated to cover recent developments in the field, this second edition also introduces new a

  3. Effect of V or Zr addition on the mechanical properties of the mechanically alloyed Al-8wt%Ti alloys

    International Nuclear Information System (INIS)

    Moon, I.H.; Lee, J.H.; Lee, K.M.; Kim, Y.D.

    1995-01-01

    Mechanical alloying (MA) of Al-Ti alloy, being a solid state process, offers the unique advantage of producing homogeneous and fine dispersions of thermally stable Al 3 Ti phase, where the formation of the fine Al 3 Ti phase by the other method is restricted from the thermodynamic viewpoint. The MA Al-Ti alloys show substantially higher strength than the conventional Al alloys at the elevated temperature due to the presence of Al 3 Ti as well as Al 4 C 3 and Al 2 O 3 , of which the last two phases were introduced during MA process. The addition of V or Zr to Al-Ti alloy was known to decrease the lattice mismatch between the intermetallic compound and the aluminum matrix, and such decrease in lattice mismatching can influence positively the high temperature mechanical strength of the MA Al-Ti by increasing the resistance to dispersoid coarsening at the elevated temperature. In the present study, therefore, the mechanical behavior of the MA Al-Ti-V and Al-Ti-Zr alloys were investigated in order to evaluate the effect of V or Zr addition on the mechanical properties of the MA Al-8Ti alloy at high temperature

  4. Environment assisted degradation mechanisms in aluminum-lithium alloys

    Science.gov (United States)

    Gangloff, Richard P.; Stoner, Glenn E.; Swanson, Robert E.

    1988-01-01

    Section 1 of this report records the progress achieved on NASA-LaRC Grant NAG-1-745 (Environment Assisted Degradation Mechanisms in Al-Li Alloys), and is based on research conducted during the period April 1 to November 30, 1987. A discussion of work proposed for the project's second year is included. Section 2 provides an overview of the need for research on the mechanisms of environmental-mechanical degradation of advanced aerospace alloys based on aluminum and lithium. This research is to provide NASA with the basis necessary to permit metallurgical optimization of alloy performance and engineering design with respect to damage tolerance, long term durability and reliability. Section 3 reports on damage localization mechanisms in aqueous chloride corrosion fatigue of aluminum-lithium alloys. Section 4 reports on progress made on measurements and mechanisms of localized aqueous corrosion in aluminum-lithium alloys. Section 5 provides a detailed technical proposal for research on environmental degradation of Al-Li alloys, and the effect of hydrogen in this.

  5. Mechanical properties and grindability of experimental Ti-Au alloys.

    Science.gov (United States)

    Takahashi, Masatoshi; Kikuchi, Masafumi; Okuno, Osamu

    2004-06-01

    Experimental Ti-Au alloys (5, 10, 20 and 40 mass% Au) were made. Mechanical properties and grindability of the castings of the Ti-Au alloys were examined. As the concentration of gold increased to 20%, the yield strength and the tensile strength of the Ti-Au alloys became higher without markedly deteriorating their ductility. This higher strength can be explained by the solid-solution strengthening of the a titanium. The Ti-40%Au alloy became brittle because the intermetallic compound Ti3Au precipitated intensively near the grain boundaries. There was no significant difference in the grinding rate and grinding ratio among all the Ti-Au alloys and the pure titanium at any speed.

  6. Porosity and mechanical properties of amorphous alloys

    International Nuclear Information System (INIS)

    Betekhtin, V.I.; Kadomtsev, A.G.; Amosova, O.V.

    2003-01-01

    The obtained experimental data on the effect of the inherent submicroporosity and its change under impact of high hydrostatic pressure or annealing on the strength, microdestruction, embrittlement temperature, the first crystallization stage and peculiarities of the surface crystallization of the amorphous alloys are analyzed. The conclusion is made on the basis of the studies on the peculiarities of the voluminous and surface crystallization of the Fe 56 Co 24 Si 5 B 15 , Fe 78 Ni 2 Si 8 B 12 , Fe 85 B 15 , Fe 58 Ni 20 Si 9 B 13 amorphous alloys that the increase in the inherent submicroporosity is one of the essential factors facilitating crystallization [ru

  7. Thermo-mechanical treatment of zirconium alloys

    International Nuclear Information System (INIS)

    Levy, I.S.

    1975-01-01

    A zirconium alloy comprising at least 95 percent Zr (Zircaloy), which has been thoroughly annealed, is greatly increased in strength without substantial loss in ductility by subjecting it to tensile creep deformation in a temperature range in which creep will occur, yet which is below the temperature for significant recovery. (U.S.)

  8. Mechanical alloying of Hf and Fe powders

    International Nuclear Information System (INIS)

    Mendoza Zelis, L.; Crespo, E.; Creus, M.; Damonte, L.C.; Sanchez, F.H.; Punte, G.

    1994-01-01

    Pure crystalline Hf and Fe powders were mixed and milled under an argon atmosphere. The evolution of the system with milling time was followed with Moessbauer effect spectroscopy and X-ray diffraction. The results indicate that in the first stages an amorphous Fe-rich alloy was gradually formed together with a solid solution of Hf in Fe beyond the solubility limit. (orig.)

  9. Mechanical behaviour of aluminium–lithium alloys

    Indian Academy of Sciences (India)

    R. Narasimhan (Krishtel eMaging) 1461 1996 Oct 15 13:05:22

    to their low ductility (Lin et al 1982; Sanders & Starke 1982, 1989; Gregson & Flower 1985;. Vasudevan ...... same in the lower strain amplitude region are found to be dependent on alloy chemistry and processing history. A comparison of the results from these studies has shown that anisotropy in the LCF properties is far ...

  10. Mechanical and microstructural characterization of the nickel base alloy (Alloy 600) after heat treatment

    International Nuclear Information System (INIS)

    Fernandes, Stela Maria de Carvalho

    1993-01-01

    The characterization of microstructural and mechanical properties of cold rolled and heat treated alloys 600 made in Brazil were investigated. The recovery and recrystallization behavior as well as solubilization and aging have been studied using optical, scanning electron and transmission electron microscopy. Microhardness and tensile testing have been carried out. The recovery process of the cold rolled alloy 600 occurred until 600 deg C and the recrystallization stage was situated between 600 and 850 deg C. The primary recrystallization temperature was obtained at 850 deg C after 1 hour (isochronal heat treatments). The aged alloy 600 shows carbide precipitation on grains bu with ductility maintenance. (author)

  11. Development of amorphous and nanocrystalline Al65Cu35-xZrx alloys by mechanical alloying

    International Nuclear Information System (INIS)

    Manna, I.; Chattopadhyay, P.P.; Banhart, F.; Fecht, H.J.

    2004-01-01

    Mechanical alloying of Al 65 Cu 35-x Zr x (x=5, 15 and 25 at.% Zr) elemental powder blends by planetary ball milling up to 50 h yields amorphous and/or nanocrystalline products. Microstructure of the milled product at different stages of milling has been characterized by X-ray diffraction, (XRD) high-resolution transmission electron microscopy (TEM) and energy dispersive X-ray spectroscopy (EDS). Among the different alloys synthesized by mechanical alloying, Al 65 Cu 20 Zr 15 yields a predominantly amorphous product, while the other two alloys develop a composite microstructure comprising nanocrystalline and amorphous solid solutions in Al 65 Cu 10 Zr 25 and nano-intermetallic phase/compound in Al 65 Cu 30 Zr 5 , respectively. The genesis of solid-state amorphization in Al 65 Cu 20 Zr 15 and Al 65 Cu 10 Zr 25 is investigated

  12. Techniques for intergranular crack formation and assessment in alloy 600 base and alloy 182 weld metals

    International Nuclear Information System (INIS)

    Lee, Tae Hyun; Hwang, Il Soon; Kim, Hong Deok; Kim, Ji Hyun

    2015-01-01

    A technique developed to produce artificial intergranular stress corrosion cracks in structural components was applied to thick, forged alloy 600 base and alloy 182 weld metals for use in the qualification of nondestructive examination techniques for welded components in nuclear power plants. An externally controlled procedure was demonstrated to produce intergranular stress corrosion cracks that are comparable to service-induced cracks in both the base and weld metals. During the process of crack generation, an online direct current potential drop method using array probes was used to measure and monitor the sizes and shapes of the cracks. A microstructural characterization of the produced cracks revealed realistic conformation of the crack faces unlike those in machined notches produced by an electrodischarge machine or simple fatigue loading using a universal testing machine. A comparison with a destructive metallographic examination showed that the characteristics, orientations, and sizes of the intergranular cracks produced in this study are highly reproducible.

  13. Microstructural characterization of low and high carbon CoCrMo alloy nanoparticles produced by mechanical milling

    Science.gov (United States)

    Simoes, T. A.; Goode, A. E.; Porter, A. E.; Ryan, M. P.; Milne, S. J.; Brown, A. P.; Brydson, R. M. D.

    2014-06-01

    CoCrMo alloys are utilised as the main material in hip prostheses. The link between this type of hip prosthesis and chronic pain remains unclear. Studies suggest that wear debris generated in-vivo may be related to post-operative complications such as inflammation. These alloys can contain different amounts of carbon, which improves the mechanical properties of the alloy. However, the formation of carbides could become sites that initiate corrosion, releasing ions and/or particles into the human body. This study analysed the mechanical milling of alloys containing both high and low carbon levels in relevant biological media, as an alternative route to generate wear debris. The results show that low carbon alloys produce significantly more nanoparticles than high carbon alloys. During the milling process, strain induces an fcc to hcp phase transformation. Evidence for cobalt and molybdenum dissolution in the presence of serum was confirmed by ICP-MS and TEM EDX techniques.

  14. Moessbauer effect study on mechanically alloyed amorphous Fe1-xTix alloys

    International Nuclear Information System (INIS)

    Chen Hong; Xu Zuxiong; Ma Ruzhang; Zhao Zhongtao; Ping Jueyun

    1994-01-01

    Amorphous Fe 1-x Ti x (x = 0.50, 0.60) powders were produced by mechanical alloying from pure elemental powders in a vibratory ball-mill. X-ray diffraction (XRD) and Moessbauer effect (ME) were used to study the progress of amorphization and the property of hydrogen absorption in Fe-Ti alloys. The amorphization process and the properties of the amorphous phase are discussed. (orig.)

  15. The effect of phosphorus on the microstructure and mechanical properties of ATI 718Plus alloy

    International Nuclear Information System (INIS)

    Wang, Minqing; Du, Jinhui; Deng, Qun; Tian, Zhiling; Zhu, Jing

    2015-01-01

    Since the discovery in the 1990s of the abnormal improvement produced by phosphorus in the stress rupture and creep life of Inconel 718 (hereafter referred to as 718), a great deal of additional research followed. However, the mechanism of the action of phosphorous in 718 is still in question. This paper details an experimental study that was intended to determine how phosphorus acts upon the microstructure and mechanical properties of Ni–Fe based alloy 718Plus. The results show that phosphorus has little effect on the strength and ductility of alloy 718Plus, but can significantly improve the stress rupture life. Phase constituents such as the δ and γ′ phases were quantitatively analyzed using electrolytic phase isolation and micro-chemical and XRD analysis as the phosphorous content of the alloy was increased. A full atom mapping of the distribution of phosphorus in the 718Plus alloy was quantitatively determined using APT (Atom Probe Tomography) technique. The results showed that there is no significant segregation of phosphorus at the γ′/γ and γ′/γ′ interface, but it significantly segregates at the grain boundaries and δ/γ interface. It was found that phosphorus is extremely depleted in the δ phase, which is believed to inhibit δ-phase precipitation by preventing δ phase nucleation and growth in the 718Plus alloy. Finally, the influence of phosphorus on the microstructure and mechanical properties of the 718Plus alloy was discussed

  16. The effect of phosphorus on the microstructure and mechanical properties of ATI 718Plus alloy

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Minqing, E-mail: minqingw@yahoo.com [Central Iron and Steel Research Institute, Beijing 100081 (China); School of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China); Beijing Key Laboratory of Advanced High Temperature Materials, Beijing 100081 (China); Du, Jinhui; Deng, Qun [Central Iron and Steel Research Institute, Beijing 100081 (China); Beijing Key Laboratory of Advanced High Temperature Materials, Beijing 100081 (China); Tian, Zhiling [Central Iron and Steel Research Institute, Beijing 100081 (China); Zhu, Jing, E-mail: jzhu@mail.tsinghua.edu.cn [School of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China)

    2015-02-25

    Since the discovery in the 1990s of the abnormal improvement produced by phosphorus in the stress rupture and creep life of Inconel 718 (hereafter referred to as 718), a great deal of additional research followed. However, the mechanism of the action of phosphorous in 718 is still in question. This paper details an experimental study that was intended to determine how phosphorus acts upon the microstructure and mechanical properties of Ni–Fe based alloy 718Plus. The results show that phosphorus has little effect on the strength and ductility of alloy 718Plus, but can significantly improve the stress rupture life. Phase constituents such as the δ and γ′ phases were quantitatively analyzed using electrolytic phase isolation and micro-chemical and XRD analysis as the phosphorous content of the alloy was increased. A full atom mapping of the distribution of phosphorus in the 718Plus alloy was quantitatively determined using APT (Atom Probe Tomography) technique. The results showed that there is no significant segregation of phosphorus at the γ′/γ and γ′/γ′ interface, but it significantly segregates at the grain boundaries and δ/γ interface. It was found that phosphorus is extremely depleted in the δ phase, which is believed to inhibit δ-phase precipitation by preventing δ phase nucleation and growth in the 718Plus alloy. Finally, the influence of phosphorus on the microstructure and mechanical properties of the 718Plus alloy was discussed.

  17. Mechanical strenght and niobium and niobium-base alloys substructures

    International Nuclear Information System (INIS)

    Monteiro, W.A.; Andrade, A.H.P. de

    1986-01-01

    Niobium and some of its alloys have been used in several fields of technological applications such as the aerospace, chemical and nuclear industries. This is due to its excelent mechanical stringth at high temperatures and reasonable ductility at low temperatures. In this work, we review the main features of the relationship mechanical strength - substructure in niobium and its alloys, taking into account the presence of impurities, the influence of initial thermal and thermo - mechanical treatments as well as the irradiation by energetic particles. (Author) [pt

  18. Corrosion-electrochemical and mechanical properties of aluminium-berylium alloys alloyed by rare-earth metals

    International Nuclear Information System (INIS)

    Safarov, A.M.; Odinaev, Kh.E.; Shukroev, M.Sh.; Saidov, R.Kh.

    1997-01-01

    In order to study influence of rare earth metals on corrosion-electrochemical and mechanical properties of aluminium-berylium alloys the alloys contain 1 mass % beryllium and different amount of rare earth metals were obtained.-electrochemical and mechanical properties of aluminium-berylium alloys. The electrochemical characteristics of obtained alloys, including stationary potential, potentials of passivation beginning and full passivation, potentials of pitting formation and re passivation were defined.

  19. Microstructural, mechanical characterisation and fractography of As-cast Ti-Al alloy

    International Nuclear Information System (INIS)

    Hamzah, E.; Ong, W.R.; Tamin, M.N.

    2007-01-01

    The effect of alloying element, namely chromium (Cr) on the microstructures, mechanical characterization and fracture surface of gamma titanium aluminide (Ti Al) has been studied. Micro-hardness and fatigue crack growth tests were performed on as-cast samples with composition of Ti-48at%Al and Ti-48%Al-2at%Cr. Prior to the micro-hardness tests; samples were metallurgically prepared for microstructural and structural analysis using optical microscope and scanning electron microscope. Field emission scanning electron microscope (FESEM) technique was employed to investigate the fracture surface of sample after fatigue crack growth test. Micro-hardness tests results showed increasing hardness value of Ti-48Al alloys when chromium is added. Both titanium aluminide alloys exhibited a nearly lamellae microstructure. However, finer laths of plates in lamellar structure have been observed in Ti-48at%Al-2at%Cr. FESEM micrograph of surface fracture indicates a mixed mode of failure for both alloys. (author)

  20. Mechanical properties of Fe3Al-based alloys with addition of carbon, niobium and titanium

    International Nuclear Information System (INIS)

    Zhang Zhengrong; Liu Wenxi

    2006-01-01

    Several Fe 3 Al-based iron aluminides with the addition of alloying elements carbon, niobium and titanium were produced by vacuum induction melting (VIM) and hot spinning forging. Analytic techniques including transmission electron microscopy (TEM), scanning electron microscopy (SEM) and X-ray diffraction (XRD) were used in studying the microstructure and fracture manner of these alloys. The results show that due to the addition of alloying elements, the superlattice dislocations tend towards multiple slipping, leaving behind on their slip plane ribbons of square-shaped slip-induced antiphase boundaries. The elongation of Fe 3 Al in tension at room temperature increased to about 10% by the addition of suitable alloying elements, the usage of thermo-mechanical processing that has the function of refining grains and substructures, and subsequent annealing

  1. Mechanical Properties and Corrosion Characteristics of Thermally Aged Alloy 22

    International Nuclear Information System (INIS)

    Rebak, R B; Crook, P

    2002-01-01

    Alloy 22 (UNS N06022) is a candidate material for the external wall of the high level nuclear waste containers for the potential repository site at Yucca Mountain. In the mill-annealed (MA) condition, Alloy 22 is a single face centered cubic phase. When exposed to temperatures on the order of 600 C and above for times higher than 1 h, this alloy may develop secondary phases that reduce its mechanical toughness and corrosion resistance. The objective of this work was to age Alloy 22 at temperatures between 482 C and 760 C for times between 0.25 h and 6,000 h and to study the mechanical and corrosion performance of the resulting material. Aging was carried out using wrought specimens as well as gas tungsten arc welded (GTAW) specimens. Mechanical and corrosion testing was carried out using ASTM standards. Results show-that the higher the aging temperature and the longer the aging time, the lower the impact toughness of the aged material and the lower its corrosion resistance. However, extrapolating both mechanical and corrosion laboratory data predicts that Alloy 22 will remain corrosion resistant and mechanically robust for the projected lifetime of the waste container

  2. Microstructures and mechanical properties of an Osprey aluminium 7000 alloy

    International Nuclear Information System (INIS)

    Cottignies, L.; Brechet, Y.; Audier, M.; Livet, F.; Louchet, F.; Sainfort, P.

    1993-01-01

    An alloy from the 7000 serie obtained by the Osprey process has been studied both from the microstructural (TEM, SAXS) and from the mechanical viewpoint. The modelling of the mechanical properties and of their anisotropy was performed using both models from physical metallurgy and a self consistent elastoplastic model. (orig.)

  3. Microstructure and Mechanical Properties of a Laser Treated Al Alloy

    NARCIS (Netherlands)

    Noordhuis, J.; Hosson, J.Th.M. De

    An Al-Cu-Mg alloy, Al 2024-T3, was exposed to laser treatments at various scan velocities. In this paper the microstructural features and mechanical properties are reported. As far as the mechanical property is concerned a striking observation is a minimum in the hardness value at a laser scan

  4. The physical metallurgy of mechanically-alloyed, dispersion-strengthened Al-Li-Mg and Al-Li-Cu alloys

    Science.gov (United States)

    Gilman, P. S.

    1984-01-01

    Powder processing of Al-Li-Mg and Al-Li-Cu alloys by mechanical alloying (MA) is described, with a discussion of physical and mechanical properties of early experimental alloys of these compositions. The experimental samples were mechanically alloyed in a Szegvari attritor, extruded at 343 and 427 C, and some were solution-treated at 520 and 566 C and naturally, as well as artificially, aged at 170, 190, and 210 C for times of up to 1000 hours. All alloys exhibited maximum hardness after being aged at 170 C; lower hardness corresponds to the solution treatment at 566 C than to that at 520 C. A comparison with ingot metallurgy alloys of the same composition shows the MA material to be stronger and more ductile. It is also noted that properly aged MA alloys can develop a better combination of yield strength and notched toughness at lower alloying levels.

  5. Effect of diluted alloying elements on mechanical properties of iron

    International Nuclear Information System (INIS)

    Hassan, A.A.S.

    1996-01-01

    Iron and its alloys have extensive applications. The effect of solute additions on mechanical properties of iron was investigated to check the efficiency of solute atoms on strength and surface e life. Additions in the range of 0.1 wt.% and 0.3 wt.% of alloying elements of Cu,Ni and Si were used. Samples of grains size ranged from 6-40 m which have been prepared by annealing followed by furnace cooling. The recrystallization temperature increases with alloying addition (475 degree C for Fe-0.3 wt. % C alloy compared to 375 degree C for pure iron). Si and Cu additions inhibit grain growth of iron whereas Ni addition enhances it.Addition of Si or Ni to iron induced softening below room temperature whereas addition of Cu caused hardening. The work hardening parameters decreased due to alloying additions. The strength coefficient K was 290 M N/m2 for Fe-03 wt % Ni compared to 340 M N/m2 for pure iron. The work hardening exponent n is 0.12 for fe-0.3 wt. Cu alloy compared to 0.17 for pure iron. All the investigated alloys fulfilled the Hall-Petch relation at liquid Nitrogen and at room temperature. Alloying addition which caused softening addition which caused hardening increased the Half-Petch parameters. Ni addition favors ductility of iron whereas Cu addition reduces it. Alloying additions generally lead to brittle fracture and decrease the crack resistance of iron. 9 tabs., 55 figs., 103 refs

  6. Mechanical properties and microstructure of copper alloys and copper alloy-stainless steel laminates for fusion reactor high heat flux applications

    Science.gov (United States)

    Leedy, Kevin Daniel

    A select group of copper alloys and bonded copper alloy-stainless steel panels are under consideration for heat sink applications in first wall and divertor structures of a planned thermonuclear fusion reactor. Because these materials must retain high strengths and withstand high heat fluxes, their material properties and microstructures must be well understood. Candidate copper alloys include precipitate strengthened CuNiBe and CuCrZr and dispersion strengthened Cu-Alsb2Osb3 (CuAl25). In this study, uniaxial mechanical fatigue tests were conducted on bulk copper alloy materials at temperatures up to 500sp°C in air and vacuum environments. Based on standardized mechanical properties measurement techniques, a series of tests were also implemented to characterize copper alloy-316L stainless steel joints produced by hot isostatic pressing or by explosive bonding. The correlation between mechanical properties and the microstructure of fatigued copper alloys and the interface of copper alloy-stainless steel laminates was examined. Commercial grades of these alloys were used to maintain a degree of standardization in the materials testing. The commercial alloys used were OMG Americas Glidcop CuAl25 and CuAl15; Brush Wellman Hycon 3HP and Trefimetaux CuNiBe; and Kabelmetal Elbrodur and Trefimetaux CuCrZr. CuAl25 and CuNiBe alloys possessed the best combination of fatigue resistance and microstructural stability. The CuAl25 alloy showed only minimal microstructural changes following fatigue while the CuNiBe alloy consistently exhibited the highest fatigue strength. Transmission electron microscopy observations revealed that small matrix grain sizes and high densities of submicron strengthening phases promoted homogeneous slip deformation in the copper alloys. Thus, highly organized fatigue dislocation structure formation, as commonly found in oxygen-free high conductivity Cu, was inhibited. A solid plate of CuAl25 alloy hot isostatically pressed to a 316L stainless steel

  7. FUNDAMENTAL MECHANISMS OF CORROSION OF ADVANCED LIGHT WATER REACTOR FUEL CLADDING ALLOYS AT HIGH BURNUP

    International Nuclear Information System (INIS)

    Lott, Randy G.

    2003-01-01

    OAK (B204) The corrosion behavior of nuclear fuel cladding is a key factor limiting the performance of nuclear fuel elements, improved cladding alloys, which resist corrosion and radiation damage, will facilitate higher burnup core designs. The objective of this project is to understand the mechanisms by which alloy composition, heat treatment and microstructure affect corrosion rate. This knowledge can be used to predict the behavior of existing alloys outside the current experience base (for example, at high burn-up) and predict the effects of changes in operation conditions on zirconium alloy behavior. Zirconium alloys corrode by the formation f a highly adherent protective oxide layer. The working hypothesis of this project is that alloy composition, microstructure and heat treatment affect corrosion rates through their effect on the protective oxide structure and ion transport properties. The experimental task in this project is to identify these differences and understand how they affect corrosion behavior. To do this, several microstructural examination techniques including transmission electron microscope (TEM), electrochemical impedance spectroscopy (EIS) and a selection of fluorescence and diffraction techniques using synchrotron radiation at the Advanced Photon Source (APS) were employed

  8. Mechanical behavior and coupling between mechanical and oxidation in alloy 718: effect of solide solution elements

    International Nuclear Information System (INIS)

    Max, Bertrand

    2014-01-01

    Alloy 718 is the superalloy the most widely used in industry due to its excellent mechanical properties, as well as oxidation and corrosion resistance in wide range of temperatures and solicitation modes. Nevertheless, it is a well-known fact that this alloy is sensitive to stress corrosion cracking and oxidation assisted cracking under loading in the range of temperatures met in service. Mechanisms explaining this phenomenon are not well understood: nevertheless, it is well established that a relation exists between a change in fracture mode and the apparition of plastic instabilities phenomenon. During this study, the instability phenomenon, Portevin-Le Chatelier effect, in alloy 718 was studied by tensile tests in wide ranges of temperatures and strain rates. Different domains of plastic instabilities have been evidenced. Their characteristics suggest the existence of interactions between dislocations and different types of solute elements: interstitials for lower temperatures and substitutionals for higher testing temperatures. Mechanical spectroscopy tests have been performed on alloy 718 and various alloys which composition is comparable to that of alloy 718. These tests prove the mobility of molybdenum atoms in the alloy in the studied temperature range. Specific tests have been performed to study interaction phenomenon between plasticity and oxidation. These results highlight the strong effect of plastic strain rate on both mechanical behavior and intergranular cracking in alloy 718. The subsequent discussion leads to propose hypothesis on coupling effects between deformation mechanisms and oxidation assisted embrittlement in the observed cracking processes. (author)

  9. In vitro degradation and mechanical integrity of calcium-containing magnesium alloys in modified-simulated body fluid.

    Science.gov (United States)

    Kannan, M Bobby; Raman, R K Singh

    2008-05-01

    The successful applications of magnesium-based alloys as degradable orthopaedic implants are mainly inhibited due to their high degradation rates in physiological environment and consequent loss in the mechanical integrity. This study examines the degradation behaviour and the mechanical integrity of calcium-containing magnesium alloys using electrochemical techniques and slow strain rate test (SSRT) method, respectively, in modified-simulated body fluid (m-SBF). Potentiodynamic polarisation and electrochemical impedance spectroscopy (EIS) results showed that calcium addition enhances the general and pitting corrosion resistances of magnesium alloys significantly. The corrosion current was significantly lower in AZ91Ca alloy than that in AZ91 alloy. Furthermore, AZ91Ca alloy exhibited a five-fold increase in the surface film resistance than AZ91 alloy. The SSRT results showed that the ultimate tensile strength and elongation to fracture of AZ91Ca alloy in m-SBF decreased only marginally (approximately 15% and 20%, respectively) in comparison with these properties in air. The fracture morphologies of the failed samples are discussed in the paper. The in vitro study suggests that calcium-containing magnesium alloys to be a promising candidate for their applications in degradable orthopaedic implants, and it is worthwhile to further investigate the in vivo corrosion behaviour of these alloys.

  10. Mechanical properties of martensitic alloy AISI 422

    International Nuclear Information System (INIS)

    Huang, F.H.; Hu, W.L.; Hamilton, M.L.

    1992-09-01

    HT9 is a martensitic stainless steel that has been considered for structural applications in liquid metal reactors (LMRs) as well as in fusion reactors. AISI 422 is a commercially available martensitic stainless steel that closely resembles HT9, and was studied briefly under the auspices of the US LMR program. Previously unpublished tensile, fracture toughness and charpy impact data on AISI 422 were reexamined for potential insights into the consequences of the compositional differences between the two alloys, particularly with respect to current questions concerning the origin of the radiation-induced embrittlement observed in HT9. 8 refs, 8 figs

  11. Fracture mechanics behaviour of neutron irradiated Alloy A-286

    International Nuclear Information System (INIS)

    Mills, W.J.; James, L.A.

    The effect of fast-neutron irradiation on the fatigue-crack propagation and fracture toughness behaviour of Alloy A-286 was characterized using fracture mechanics techniques. The fracture toughness was found to decrease continuously with increasing irradiation damage at both 24 deg. C and 427 deg. C. In the unirradiated and low fluence conditions, specimens displayed appreciable plasticity prior to fracture, and equivalent Ksub(Ic) values were determined from Jsub(Ic) fracture toughness results. At high irradiation exposure levels, specimens exhibited a brittle Ksub(Ic) fracture mode. The 427 deg. C fracture toughness fell from 129 MPa√m in the unirradiated condition to 35 MPa√m at an exposure of 16.2 dpa (total fluence of 5.2x10 22 n/cm 2 ). Room temperature fracture toughness values were consistently 40 to 60 percent higher than the 427 deg. C values. Electron fractography revealed that the reduction in fracture resistance was attributed to a fracture mechanism transition from ductile microvoid coalescence to channel fracture. Fatigue-crack propagation tests were conducted at 427 deg. C on specimens irradiated at 2.4 dpa and 16.2 dpa. Crack growth rates at the lower exposure level were comparable to those in unirradiated material, while those at the higher exposure were slightly higher than in unirradiated material. (author)

  12. Refinement and fracture mechanisms of as-cast QT700-6 alloy by alloying method

    Directory of Open Access Journals (Sweden)

    Min-qiang Gao

    2017-01-01

    Full Text Available The as-cast QT700-6 alloy was synthesized with addition of a certain amount of copper, nickel, niobium and stannum elements by alloying method in a medium frequency induction furnace, aiming at improving its strength and toughness. Microstructures of the as-cast QT700-6 alloy were observed using a scanning-electron microscope (SEM and the mechanical properties were investigated using a universal tensile test machine. Results indicate that the ratio of pearlite/ferrite is about 9:1 and the graphite size is less than 40 μm in diameter in the as-cast QT700-6 alloy. The predominant refinement mechanism is attributed to the formation of niobium carbides, which increases the heterogeneous nucleus and hinders the growth of graphite. Meanwhile, niobium carbides also exist around the grain boundaries, which improve the strength of the ductile iron. The tensile strength and elongation of the as-cast QT700-6 alloy reach over 700 MPa and 6%, respectively, when the addition amount of niobium is 0.8%. The addition of copper and nickel elements contributed to the decrease of eutectoid transformation temperature, resulting in the decrease of pearlite lamellar spacing (about 248 nm, which is also beneficial to enhancing the tensile strength. The main fracture mechanism is cleavage fracture with the appearance of a small amount of dimples.

  13. Microstructure, mechanical and tribological behavior of hot-pressed mechanically alloyed Al–Zn–Mg–Cu powders

    International Nuclear Information System (INIS)

    Azimi, A.; Fallahdoost, H.; Nejadseyfi, O.

    2015-01-01

    Highlights: • Nanocrystalline Al7050 alloy was synthesized by mechanical alloying. • Longer milling time led to increasing porosity in hot-pressed samples. • Significant improvement in strength and wear resistance was obtained by increasing the milling time up to 40 h. - Abstract: This research focuses on the preparation of Al7050 alloy via mechanical alloying and hot pressing techniques. The effect of milling time on the microstructure and densification response was investigated by X-ray diffraction (XRD) and scanning electron microscope (SEM). Furthermore, the mechanical properties of the samples including microhardness, compression strength, and wear resistance were examined as a function of milling time. The results of the experiments proved that by increasing the milling time the crystallite size was reduced, which has a significant effect on improving the mechanical properties. In addition, porosity formation increased when the milling time was increased due to reduction of the compressibility of finer particles. By increasing the milling time to more than 40 h, a relatively invariable crystallite size was obtained and it was observed that the porosities expanded in the samples. Therefore, the compressive strength, hardness, and wear resistance were enhanced up to 40 h milling time and then the strengthening effect was relatively diminished. On observing surfaces with SEM, the dominant wear mechanism was recognized as abrasion, delamination and adhesion

  14. Solid solution in Al-4.5 wt% Cu produced by mechanical alloying

    International Nuclear Information System (INIS)

    Fogagnolo, J.B.; Amador, D.; Ruiz-Navas, E.M.; Torralba, J.M.

    2006-01-01

    Mechanical alloying has been used to produce oxide dispersion strengthened alloys, intermetallic compounds, aluminium alloys and to obtain nanostructured and amorphous materials, as well as to extend the solid solution limit. In this work, Al and Cu elemental powders were subjected to high-energy milling to produce Al-4.5 wt% Cu powder alloy. The powders obtained were characterized by scanning electron microscopy, X-ray diffraction (XRD) and differential scanning calorimetry (DSC), aiming to explore if the copper is present in solid solution or as small particles after high-energy milling. Related to the formation of a supersaturated solid solution, the results of scanning electron microscopy and X-ray diffraction are non-conclusive: the copper could be dispersed with a very small size, undetectable to both techniques. The Al 2 Cu precipitation at temperatures between 160 and 230 deg. C, verified by DSC and XRD analyses, substantiated that mechanical alloying had produced a supersaturated solid solution of copper in aluminium. The crystallite size as a function of milling time and annealing temperature was also determined by X-ray techniques

  15. The effect of remelting various combinations of new and used cobalt-chromium alloy on the mechanical properties and microstructure of the alloy

    Directory of Open Access Journals (Sweden)

    Sharad Gupta

    2012-01-01

    Conclusion: Repeated remelting of base metal alloy for dental casting without addition of new alloy can affect the mechanical properties of the alloy. Microstructure analysis shows deterioration upon remelting. However, the addition of 25% and 50% (by weight of new alloy to the remelted alloy can bring about improvement both in mechanical properties and in microstructure.

  16. Microstructures and mechanical properties of two-phase alloys based on NbCr{sub 2}

    Energy Technology Data Exchange (ETDEWEB)

    Chen, K.C.; Kotula, P.G.; Cady, C.M.; Mauro, M.E.; Thoma, D.J.

    1999-07-01

    A two-phase, NbCrTi alloy (bcc + C15 Laves phase) has been developed using several alloy design methodologies. In efforts to understand processing-microstructure-property relationships, different processing routes were employed. The resulting microstructures and mechanical properties are discussed and compared. Plasma arc melted (PAM) samples served to establish baseline, as-cast properties. In addition, a novel processing technique, involving decomposition of a supersaturated and metastable precursor phase during hot isostatic pressing (HIP), was used to produce a refined, equilibrium two-phase microstructure. Quasi-static compression tests as a function of temperature were performed on both alloy types. Different deformation mechanisms were encountered based upon temperature and microstructure.

  17. Mechanical properties, corrosion, and biocompatibility of Mg-Zr-Sr-Dy alloys for biodegradable implant applications.

    Science.gov (United States)

    Ding, Yunfei; Lin, Jixing; Wen, Cuie; Zhang, Dongmei; Li, Yuncang

    2017-11-28

    This study investigates the microstructure, mechanical properties, corrosion behavior, and biocompatibility of magnesium (Mg)-based Mg1Zr2SrxDy (x = 0, 1, 1.63, 2.08 wt %) alloys for biodegradable implant applications. The corrosion behavior of the Mg-based alloys has been evaluated in simulated body fluid using an electrochemical technique and hydrogen evolution. The biocompatibility of the Mg-based alloys has been assessed using SaSO2 cells. Results indicate that the addition of Dy to Mg-Zr-Sr alloy showed a positive impact on the corrosion behavior and significantly decreased the degradation rates of the alloys. The degradation rate of Mg1Zr2Sr1.0Dy decreased from 17.61 to 12.50 mm year -1 of Mg1Zr2Sr2.08Dy based on the hydrogen evolution. The ultimate compressive strength decreased from 270.90 MPa for Mg1Zr2Sr1Dy to 236.71 MPa for Mg1Zr2Sr2.08Dy. An increase in the addition of Dy to the Mg-based alloys resulted in an increase in the volume fraction of the Mg 2 Dy phase, which mitigated the galvanic effect between the Mg 17 Sr 2 phase and the Mg matrix, and led to an increase in the corrosion resistance of the base alloy. The biocompatibility of the Mg-based alloys was enhanced with decreasing corrosion rates. Mg1Zr2Sr2.08Dy exhibited the lowest corrosion rate and the highest biocompatibility compared with the other Mg-based alloys. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2017. © 2017 Wiley Periodicals, Inc.

  18. Thermal Plasma Spheroidization of High-Nitrogen Stainless Steel Powder Alloys Synthesized by Mechanical Alloying

    Science.gov (United States)

    Razumov, Nikolay G.; Popovich, Anatoly A.; Wang, QingSheng

    2018-03-01

    This paper presents the results of experimental studies on the treatment of Fe-23Cr-11Mn-1N high-nitrogen stainless steel powder alloys, synthesized by the mechanical alloying (MA) of elemental powders in the flow of a thermal plasma. Fe-23Cr-11Mn-1N high-nitrogen stainless steel powder alloys were prepared by MA in the attritor under an argon atmosphere. For spheroidization of Fe-23Cr-11Mn-1N high-nitrogen stainless steel powder alloys, the TekSphero 15 plant manufactured by Tekna Plasma Systems Inc was used. The studies have shown the possibility of obtaining Fe-23Cr-11Mn-1N high-nitrogen spherical powders steel alloys from the powder obtained by MA. According to the results of a series of experiments, it was found that the results of plasma spheroidization of powders essentially depend on the size of the fraction due to some difference in the particle shape and flowability, and on the gas regime of the plasma torch. It is established that during the plasma spheroidization process, some of the nitrogen leaves the alloy. The loss rate of nitrogen depends on the size of the initial particles.

  19. Fabrication and Magnetic Properties of Co₂MnAl Heusler Alloys by Mechanical Alloying.

    Science.gov (United States)

    Lee, Chung-Hyo

    2018-02-01

    We have applied mechanical alloying (MA) to produce nanocrystalline Co2MnAl Heusler alloys using a mixture of elemental Co50Mn25Al25 powders. An optimal milling and heat treatment conditions to obtain a Co2MnAl Heusler phase with fine microstructure were investigated by X-ray diffraction, differential scanning calorimeter and vibrating sample magnetometer measurements. α-(Co, Mn, Al) FCC phases coupled with amorphous phase are obtained after 3 hours of MA without any evidence for the formation of Co2MnAl alloys. On the other hand, a Co2MnAl Heusler alloys can be obtained by the heat treatment of all MA samples up to 650 °C. X-ray diffraction result shows that the average grain size of Co2MnAl Heusler alloys prepared by MA for 5 h and heat treatment is in the range of 95 nm. The saturation magnetization of MA powders decreases with MA time due to the magnetic dilution by alloying with nonmagnetic Mn and Al elements. The magnetic hardening due to the reduction of the grain size with ball milling is also observed. However, the saturation magnetization of MA powders after heat treatment increases with MA time and reaches to a maximum value of 105 emu/g after 5 h of MA. It can be also seen that the coercivity of 5 h MA sample annealed at 650 °C is fairly low value of 25 Oe.

  20. Hydrogen uptake characteristics of mechanically alloyed Ti-V-Ni

    International Nuclear Information System (INIS)

    Cauceglia, Dorian; Hampton, Michael D.; Lomness, Janice K.; Slattery, Darlene K.; Resan, Mirna

    2006-01-01

    It has been well established that hydrogen will react directly and reversibly with a large number of metals and alloys to form metallic hydrides. Extensive research has been done over the years to improve properties of these hydrogen purification and recovery media and in developing new compounds for this purpose. In the present study, the hydrogen uptake characteristics of mechanically alloyed titanium-vanadium-nickel have been studied. Thermal and composition data were obtained for the Ti-V-Ni system prepared by mechanical alloying at a ball-to-powder mass ratio of 10:1. It was found that this material would absorb up to approximately 1.0 wt% hydrogen at near ambient temperature and ambient pressure of hydrogen

  1. EBSD characterization of low temperature deformation mechanisms in modern alloys

    Science.gov (United States)

    Kozmel, Thomas S., II

    For structural applications, grain refinement has been shown to enhance mechanical properties such as strength, fatigue resistance, and fracture toughness. Through control of the thermos-mechanical processing parameters, dynamic recrystallization mechanisms were used to produce microstructures consisting of sub-micron grains in 9310 steel, 4140 steel, and Ti-6Al-4V. In both 9310 and 4140 steel, the distribution of carbides throughout the microstructure affected the ability of the material to dynamically recrystallize and determined the size of the dynamically recrystallized grains. Processing the materials at lower temperatures and higher strain rates resulted in finer dynamically recrystallized grains. Microstructural process models that can be used to estimate the resulting microstructure based on the processing parameters were developed for both 9310 and 4140 steel. Heat treatment studies performed on 9310 steel showed that the sub-micron grain size obtained during deformation could not be retained due to the low equilibrium volume fraction of carbides. Commercially available aluminum alloys were investigated to explain their high strain rate deformation behavior. Alloys such as 2139, 2519, 5083, and 7039 exhibit strain softening after an ultimate strength is reached, followed by a rapid degradation of mechanical properties after a critical strain level has been reached. Microstructural analysis showed that the formation of shear bands typically preceded this rapid degradation in properties. Shear band boundary misorientations increased as a function of equivalent strain in all cases. Precipitation behavior was found to greatly influence the microstructural response of the alloys. Additionally, precipitation strengthened alloys were found to exhibit similar flow stress behavior, whereas solid solution strengthened alloys exhibited lower flow stresses but higher ductility during dynamic loading. Schmid factor maps demonstrated that shear band formation behavior

  2. Mechanical Characterization and Corrosion Testing of X608 Al Alloy

    Energy Technology Data Exchange (ETDEWEB)

    Prabhakaran, Ramprashad; Choi, Jung-Pyung; Stephens, Elizabeth V.; Catalini, David; Lavender, Curt A.; Rohatgi, Aashish

    2016-02-07

    This paper describes the mechanical characterization and corrosion testing of X608 Al alloy that is being considered for A-pillar covers for heavy-duty truck applications. Recently, PNNL developed a thermo-mechanical process to stamp A-pillar covers at room temperature using this alloy, and the full-size prototype was successfully stamped by a tier-1 supplier. This study was conducted to obtain additional important information related to the newly developed forming process, and to further improve its mechanical properties. The solutionization temperature, pre-strain and paint-bake heat-treatment were found to influence the alloy’s fabricability and mechanical properties. Natural aging effect on the formability was investigated by limiting dome height (LDH) tests. Preliminary corrosion experiments showed that the employed thermo-mechanical treatments did not significantly affect the corrosion behavior of Al X608.

  3. Hot mechanical behaviour of dispersion strengthened Cu alloys

    International Nuclear Information System (INIS)

    Garcia G, Jose; Espinoza G, Rodrigo; Palma H, Rodrigo; Sepulveda O, Aquiles

    2003-01-01

    This work is part of a research project which objective is the improvement of the high-temperature mechanical properties of copper, without an important decrease of the electrical or thermal conduction properties. The general hypothesis is that this will be done by the incorporation of nanometric ceramic dispersoids for hindering the dislocation and grain boundaries movement. In this context, the object of the present work is the study of the resistance to hot deformation of dispersion-strengthened copper alloys which have prepared by reactive milling. Two different alloys, Cu-2,39wt.%Ti-0.56wt.%C and Cu-1.18wt.%Al, were prepared so as obtain a copper matrix reinforced with nanometric TiC y Al 2 O 3 particles with a nominal total amount of 5 vol.%. The particles were developed by an in-situ formation process during milling. The materials were prepared in an attritor mill, and consolidated by extrusion at 750 o C, with an area reduction rate of 10:1. The resistance to hot deformation was evaluated by hot compression tests at 500 and 850 o C, at initial strain rates of 10 -3 and 10 -4 s-1. To evaluate the material softening due temperature, annealing at 400, 650 y 900 o C during 1h were applied; after that, hardness was measured at room temperature. Both studies alloys presented a higher resistance to hot deformation than pure copper, with or without milling. Moreover, the Cu-Ti-C alloy presented a mechanical resistance higher than that of the Cu-Al one. Both alloys presented strain-stress compression curves with a typical hot-work shape: an initial maximum followed by a stationary plateau. The Cu-Ti-C alloy had a higher hardness and did not present a hardness decay even after annealings at the higher temperature imposed (900 o C), while the Cu-Al alloy did exhibit a strong decay of hardness after the annealing at 900 o C. The best behaviour exhibited by the Cu-Ti C alloy, was attributed to the formation of a major quantity of dispersoids that in the Cu-Al alloy. In

  4. Chemical durability and degradation mechanisms of HT9 based alloy waste forms with variable Zr content

    Energy Technology Data Exchange (ETDEWEB)

    Olson, L. N. [Savannah River Site (SRS), Aiken, SC (United States). Savannah River National Lab. (SRNL)

    2015-10-30

    In Corrosion studies were undertaken on alloy waste forms that can result from advanced electrometallurgical processing techniques to better classify their durability and degradation mechanisms. The waste forms were based on the RAW3-(URe) composition, consisting primarily of HT9 steel and other elemental additions to simulate nuclear fuel reprocessing byproducts. The solution conditions of the corrosion studies were taken from an electrochemical testing protocol, and meant to simulate conditions in a repository. The alloys durability was examined in alkaline and acidic brines.

  5. Effect Of Cooling Rate On Thermal And Mechanical Properties Of Cu-%24.2Mn Alloy

    International Nuclear Information System (INIS)

    Celik, H.

    2010-01-01

    In this research, different heat and mechanical treatments have been applied to the Cu-%24.2Mn and some samples have been obtained from this alloy. On these samples, phase transformations have been formed by thermal and mechanical effect. Morphological, mechanical and crystallographic properties of the phase transformations have been examined by using different physical methods. Austenite phase has been obtained in the samples which have been applied slow and rapid cooling according to the SEM analysis. It has been observed that the grain size obtained by the rapid cooling is smaller than the grain size obtained by the slow cooling. Therefore, it has been concluded that the cooling process differences, changes the grain size of the alloy. Compression stress has been applied to the alloy in order to search the deformation effect on the austenite phase transformation. The structural features of the phase transformations have been examined. Slip lines and martensite structural were observed on the surface of the alloys after the deformation. Changes in phase structure of the alloy are also examined by means of XRD technique.

  6. Mechanical behavior of aluminum-lithium alloys at cryogenic temperatures

    International Nuclear Information System (INIS)

    Glazer, J.; Verzasconi, S.L.; Sawtell, R.R.; Morris, J.W. Jr.

    1987-01-01

    The cryogenic mechanical properties of aluminum-lithium alloys are of interest because these alloys are attractive candidate materials for cryogenic tankage. Previous work indicates that the strength-toughness relationship for alloy 2090-T81 (Al-2.7Cu-2.2Li-0.12Zr by weight) improves significantly as temperature decreases. The subject of this investigation is the mechanism of this improvement. Deformation behavior was studied since the fracture morphology did not change with temperature. Tensile failures in 2090-T81 and -T4 occur at plastic instability. In contrast, in the binary aluminum-lithium alloy studied here they occur well before plastic instability. For all three materials, the strain hardening rate in the longitudinal direction increases as temperature decreases. This increase is associated with an improvement in tensile elongation at low temperatures. In alloy 2090-T4, these results correlate with a decrease in planar slip at low temperatures. The improved toughness at low temperatures is believed to be due to increased stable deformation prior to fracture

  7. Characterization of Dispersion Strengthened Copper Alloy Prepared by Internal Oxidation Combined with Mechanical Alloying

    Science.gov (United States)

    Zhao, Ziqian; Xiao, Zhu; Li, Zhou; Zhu, Mengnan; Yang, Ziqi

    2017-11-01

    Cu-3.6 vol.% Al2O3 dispersion strengthened alloy was prepared by mechanical alloying (MA) of internal oxidation Cu-Al powders. The lattice parameter of Cu matrix decreased with milling time for powders milled in argon, while the abnormal increase of lattice parameter occurred in the air resulting from mechanochemical reactions. With a quantitative analysis, the combined method makes residual aluminum oxidized completely within 10-20 h while mechanical alloying method alone needs longer than 40 h. Lamellar structure formed and the thickness of lamellar structure decreased with milling time. The size of Al2O3 particles decreased from 46 to 22 nm after 40 h milling. After reduction, core-shell structure was found in MAed powders milled in the air. The compacted alloy produced by MAed powders milled in the argon had an average hardness and electrical conductivity of 172.2 HV and 82.1% IACS while the unmilled alloy's were 119.8 HV and 74.1% IACS due to the Al2O3 particles refinement and residual aluminum in situ oxidization.

  8. Kinetic process of mechanical alloying in Fe50Cu50

    DEFF Research Database (Denmark)

    Huang, J.Y.; Jiang, Jianzhong; Yasuda, H.

    1998-01-01

    It is shown that mechanical alloying in the immiscible Fe-Cu system is governed by the atomic shear event and shear-induced diffusion process. We found that an alpha-to-gamma phase transformation, as evidenced by the Nishiyama-Wasserman orientation relationship, occurs by simultaneous shearing...

  9. FeSiBAlNiMo High Entropy Alloy Prepared by Mechanical Alloying

    Czech Academy of Sciences Publication Activity Database

    Bureš, R.; Hadraba, Hynek; Fáberová, M.; Kollár, P.; Füzer, J.; Roupcová, Pavla; Strečková, M.

    2017-01-01

    Roč. 131, č. 4 (2017), s. 771-773 ISSN 0587-4246 R&D Projects: GA ČR(CZ) GA14-25246S Institutional support: RVO:68081723 Keywords : Entropy * Mechanical alloying * Nanocrystals * Sintering Subject RIV: JG - Metallurgy OBOR OECD: Materials engineering Impact factor: 0.469, year: 2016

  10. Effects of Eutectic Si and Secondary Dendrite Arm Spacing on the Mechanical Properties of Al-Si-Cu Cast Alloys

    International Nuclear Information System (INIS)

    Lee, Kyungmin; Kim, Yumi; Kim, Youngman; Hong, Sungkil; Choi, Seweon; Kim, Youngchan; Kang, Changseok

    2014-01-01

    The present study aims at investigating the effects of eutectic Si and Secondary dendrite arm spacing (SDAS) on mechanical properties of Al-Si-Cu alloy. Heat treatment and controlling of solidification rate affect to microstructure of Al-Si-Cu alloy. Al-Si-Cu alloy was dissolved in an electric furnace. The alloy cast in STD61 mold which had been pre-heated to 95 ℃ and 200 ℃. Eutectic Si and SDAS were finer as cooling rate increased. Image analysis technique has been utilized to examine the microstructure. Microstructure observation results showed that T6 heat treatment has a strong influence eutectic Si particle morphology. The mechanical properties, such as tensile strength, yield strength, elongation, were improved by ASTM E8 standard. Tensile properties of the Al-Si-Cu alloys prepared by different cooling rates were the same as each other by T6 heat treatment.

  11. Preparation of Mn-Zn nanoferrite by mechanical alloying

    International Nuclear Information System (INIS)

    Nasresfahani, M.

    2007-01-01

    Full text: In this research Mn-Zn nanoferrite (Mn x Zn 1-x Fe 2 O 4 ;X=0.3,0.5,0.7)were prepared by mechanical alloying of a mixture of 2 single phase ferrites, MnFe 2 O 4 and ZnFe 2 O 4 . First, ZnFe 2 O 4 and MnFe 2 O 4 were obtained by conventional ceramic technique. In this technique a mixture of related raw materials(ZnO and MnO 2 from merck company and Fe 2 O 3 domestic source) was first mixed and calcined at 1100 C for 3h in air. The starting materials used to prepare Mn-Zn nanoferrite were MnFe 2 O 4 and ZnFe 2 O 4 mixed in the ratio appropriate for the reaction: xMnFe 2 O 4+(1-x) ZnFe 2 O 4 MnxZn 1-x Fe 2 O 4 and milled at different times in SPEX8000M mixer/mill. XRD investigations was used to study the phase formation of the as-milled mixed ferrite. Using XRD patterns and Scherrer's formula, mean crystallite size of the single phase samples were calculated and were in the 10-20 nm. Saturation magnetization(Ms) of the powders was measured at room temperature by a very sensitive home made permeameter. The measured Ms values show that they are smaller than the Ms values associated with the same compound prepared by conventional ceramic technique. The decrease is due to the surface effect in nanoparticles, which can be explained on core-sell model. (authors)

  12. Fabrication of nanocrystalline alloys Cu–Cr–Mo super satured solid solution by mechanical alloying

    Energy Technology Data Exchange (ETDEWEB)

    Aguilar, C., E-mail: claudio.aguilar@usm.cl [Departamento de Ingeniería Metalúrgica y Materiales, Universidad Técnica Federico Santa María, Av. España 1680, Valparaíso (Chile); Guzmán, D. [Departamento de Ingeniería en Metalurgia, Facultad de Ingeniería, Universidad de Atacama y Centro Regional de Investigación y Desarrollo Sustentable de Atacama (CRIDESAT), Av. Copayapu 485, Copiapó (Chile); Castro, F.; Martínez, V.; Cuevas, F. de las [Centro de Estudios e Investigaciones Técnicas de Gipuzkoa, Paseo de Manuel Lardizábal, N° 15, 20018 San Sebastián (Spain); Lascano, S. [Departamento de Ingeniería Mecánica, Universidad Técnica Federico Santa María, Av. España 1680, Valparaíso (Chile); Muthiah, T. [Departamento de Ingeniería Metalúrgica y Materiales, Universidad Técnica Federico Santa María, Av. España 1680, Valparaíso (Chile)

    2014-08-01

    This work discusses the extension of solid solubility of Cr and Mo in Cu processed by mechanical alloying. Three alloys processed, Cu–5Cr–5Mo, Cu–10Cr–10Mo and Cu–15Cr–15Mo (weight%) using a SPEX mill. Gibbs free energy of mixing values 10, 15 and 20 kJ mol{sup −1} were calculated for these three alloys respectively by using the Miedema's model. The crystallite size decreases and dislocation density increases when the milling time increases, so Gibbs free energy storage in powders increases by the presence of crystalline defects. The energy produced by crystallite boundaries and strain dislocations were estimated and compared with Gibbs free energy of mixing values. The energy storage values by the presence of crystalline defects were higher than Gibbs free energy of mixing at 120 h for Cu–5Cr–5Mo, 130 h for Cu–10Cr–10Mo and 150 h for Cu–15Cr–15Mo. During milling, crystalline defects are produced that increases the Gibbs free energy storage and thus the Gibbs free energy curves are moved upwards and hence the solubility limit changes. Therefore, the three alloys form solid solutions after these milling time, which are supported with the XRD results. - Highlights: • Extension of solid solution Cr and Mo in Cu achieved by mechanical alloying. • X-ray characterization of Cu–Cr–Mo system processed by mechanical alloying. • Thermodynamics analysis of formation of solid solution of the Cu–Cr–Mo system.

  13. Al-Cu-Li and Al-Mg-Li alloys: Phase composition, texture, and anisotropy of mechanical properties (Review)

    Science.gov (United States)

    Betsofen, S. Ya.; Antipov, V. V.; Knyazev, M. I.

    2016-04-01

    The results of studying the phase transformations, the texture formation, and the anisotropy of the mechanical properties in Al-Cu-Li and Al-Mg-Li alloys are generalized. A technique and equations are developed to calculate the amounts of the S1 (Al2MgLi), T1 (Al2CuLi), and δ' (Al3Li) phases. The fraction of the δ' phase in Al-Cu-Li alloys is shown to be significantly higher than in Al-Mg-Li alloys. Therefore, the role of the T1 phase in the hardening of Al-Cu-Li alloys is thought to be overestimated, especially in alloys with more than 1.5% Li. A new model is proposed to describe the hardening of Al-Cu-Li alloys upon aging, and the results obtained with this model agree well with the experimental data. A texture, which is analogous to that in aluminum alloys, is shown to form in sheets semiproducts made of Al-Cu-Li and Al-Mg-Li alloys. The more pronounced anisotropy of the properties of lithium-containing aluminum alloys is caused by a significant fraction of the ordered coherent δ' phase, the deformation mechanism in which differs radically from that in the solid solution.

  14. Mechanisms of diffusional phase transformations in metals and alloys

    CERN Document Server

    Aaronson, Hubert I; Lee, Jong K

    2010-01-01

    Developed by the late metallurgy professor and master experimentalist Hubert I. Aaronson, this collection of lecture notes details the fundamental principles of phase transformations in metals and alloys upon which steel and other metals industries are based. Mechanisms of Diffusional Phase Transformations in Metals and Alloys is devoted to solid-solid phase transformations in which elementary atomic processes are diffusional jumps, and these processes occur in a series of so-called nucleation and growth through interface migration. Instead of relying strictly on a pedagogical approach, it doc

  15. SOLUTION TREATMENT EFFECT ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF AUTOMOTIVE CAST ALLOY

    Directory of Open Access Journals (Sweden)

    Eva Tillová

    2012-02-01

    Full Text Available The contribution describes influence of the heat treatment (solution treatment at temperature 545°C and 565°C with different holding time 2, 4, 8, 16 and 32 hours; than water quenching at 40°C and natural aging at room temperature during 24 hours on mechanical properties (tensile strength and Brinell hardness and microstructure of the secondary AlSi12Cu1Fe automotive cast alloy. Mechanical properties were measured in line with EN ISO. A combination of different analytical techniques (light microscopy, scanning electron microscopy (SEM were therefore been used for study of microstructure. Solution treatment led to changes in microstructure includes the spheroidization and coarsening of eutectic silicon. The dissolution of precipitates and the precipitation of finer hardening phase further increase the hardness and tensile strength of the alloy. Optimal solution treatment (545°C/4 hours most improves mechanical properties and there mechanical properties are comparable with mechanical properties of primary AlSi12Cu1Fe alloy. Solution treatment at 565 °C caused testing samples distortion, local melting process and is not applicable for this secondary alloy with 12.5 % Si.

  16. Mechanical alloying of Cu-xCr (x = 3, 5 and 8 wt.%) alloys

    International Nuclear Information System (INIS)

    Aguilar, C.; Ordonez, S.; Guzman, D.; Rojas, P.A.

    2010-01-01

    This work studies the structural evolution of Cu-xCr (x = 3, 5 and 8 wt.%) alloys processed by mechanical alloying using X-ray diffraction profiles, scanning microscopy and microhardness analysis. X-ray diffraction analysis using the modified Williamson-Hall and Warren-Averbach methods were used to determine structural properties, such as crystallite size, stacking fault probability and energy, dislocation density, lattice parameters and crystallite size distribution of metallic powder as a function of Cr amount and milling time. Lattice defects increase the Gibbs free energy and the Gibbs free energy curves shift upward, therefore the solubility limit change.

  17. Dynamic mechanical properties of straight titanium alloy arch wires.

    Science.gov (United States)

    Kusy, R P; Wilson, T W

    1990-10-01

    Eight straight-wire materials were studied: an orthodontic titanium-molybdenum (Ti-Mo) product, TMA; three orthodontic nickel-titanium (Ni-Ti) products, Nitinol, Titanal, and Orthonol; three prototype alloys, a martensitic, an austenitic, and a biphasic alloy; and a hybrid shape-memory-effect product, Biometal. Each wire was prepared with a length-to-cross-sectional area of at least 3600 cm-1. With an Autovibron Model DDV-II-C used in the tensile mode, each sample was scanned from -120 to +200 degrees C at 2 degrees C/min. From the data base, plots of the log storage modulus, log tan delta, and percent change in length vs. temperature were generated. Results showed that the dynamic mechanical properties of the alloys within this TI system are quite different. The Ti-Mo alloy, TMA, was invariant with temperature, having a modulus of 7.30 x 10(11) dyne/cm2 (10.6 x 10(6) psi). The three cold-worked alloys--Nitinol, Titanal, and Orthonol--appeared to be similar, having a modulus of 5.74 x 10(11) dyne/cm2 (8.32 x 10(6) psi). The biphasic shape-memory alloy displayed a phase transformation near ambient temperature; whereas the hybrid shape-memory product, Biometal, underwent a 3-5% change in length during its transformation between 95 and 125 degrees C. Among the Ni-Ti wires tested, several different types of alloys were represented by this intermetallic material.

  18. Nanoscale shape-memory alloys for ultrahigh mechanical damping.

    Science.gov (United States)

    San Juan, Jose; Nó, Maria L; Schuh, Christopher A

    2009-07-01

    Shape memory alloys undergo reversible transformations between two distinct phases in response to changes in temperature or applied stress. The creation and motion of the internal interfaces between these phases during such transformations dissipates energy, making these alloys effective mechanical damping materials. Although it has been shown that reversible phase transformations can occur in nanoscale volumes, it is not known whether these transformations have a sample size dependence. Here, we demonstrate that the two phases responsible for shape memory in Cu-Al-Ni alloys are more stable in nanoscale pillars than they are in the bulk. As a result, the pillars show a damping figure of merit that is substantially higher than any previously reported value for a bulk material, making them attractive for damping applications in nanoscale and microscale devices.

  19. Structural and magnetic properties of nanocrystalline Fe–Co–Ni alloy processed by mechanical alloying

    International Nuclear Information System (INIS)

    Raanaei, Hossein; Eskandari, Hossein; Mohammad-Hosseini, Vahid

    2016-01-01

    In this present work, a nanostructured iron–cobalt–nickel alloy with Fe_5_0Co_3_0Ni_2_0 composition has been processed by mechanical alloying. The structural and magnetic properties have been investigated by X-ray diffraction, scanning electron microscopy, energy dispersive X-ray spectroscopy and vibrating sample magnetometer. It is shown that the crystallize size reaches to about 18.7 nm after 32 h milling time. A remarkable decrease in coercivity after 16 h milling time and also a continuous increase in remanent magnetization during the mechanical alloying process are observed. Heat treatment of the samples milled at 32 and 48 h demonstrates the crystalline constituent elements and also Fe_3O_4 crystalline phase. - Highlights: • This article focuses on mechanical alloying of Fe_5_0Co_3_0Ni_2_0 composition. • Structural and magnetic properties were investigated. • Saturation magnetization was increased sharply after 16 h of milling time. • The heat treatment revealed the signature of Fe_3O_4 as well as FeNi_3 and Co crystalline phases.

  20. Structural and magnetic properties of nanocrystalline Fe–Co–Ni alloy processed by mechanical alloying

    Energy Technology Data Exchange (ETDEWEB)

    Raanaei, Hossein, E-mail: hraanaei@yahoo.com [Department of Physics, Persian Gulf University, Bushehr 75169 (Iran, Islamic Republic of); Eskandari, Hossein [Department of Mechanical Engineering, Persian Gulf University, Bushehr 75169 (Iran, Islamic Republic of); Mohammad-Hosseini, Vahid [Department of Physics, Persian Gulf University, Bushehr 75169 (Iran, Islamic Republic of)

    2016-01-15

    In this present work, a nanostructured iron–cobalt–nickel alloy with Fe{sub 50}Co{sub 30}Ni{sub 20} composition has been processed by mechanical alloying. The structural and magnetic properties have been investigated by X-ray diffraction, scanning electron microscopy, energy dispersive X-ray spectroscopy and vibrating sample magnetometer. It is shown that the crystallize size reaches to about 18.7 nm after 32 h milling time. A remarkable decrease in coercivity after 16 h milling time and also a continuous increase in remanent magnetization during the mechanical alloying process are observed. Heat treatment of the samples milled at 32 and 48 h demonstrates the crystalline constituent elements and also Fe{sub 3}O{sub 4} crystalline phase. - Highlights: • This article focuses on mechanical alloying of Fe{sub 50}Co{sub 30}Ni{sub 20} composition. • Structural and magnetic properties were investigated. • Saturation magnetization was increased sharply after 16 h of milling time. • The heat treatment revealed the signature of Fe{sub 3}O{sub 4} as well as FeNi{sub 3} and Co crystalline phases.

  1. Nickel-Titanium Alloys: Corrosion "Proof" Alloys for Space Bearing, Components and Mechanism Applications

    Science.gov (United States)

    DellaCorte, Christopher

    2010-01-01

    An intermetallic nickel-titanium alloy, 60NiTi (60 wt% Ni, 40 wt% Ti), is shown to be a promising candidate tribological material for space mechanisms. 60NiTi offers a broad combination of physical properties that make it unique among bearing materials. 60NiTi is hard, electrically conductive, highly corrosion resistant, readily machined prior to final heat treatment, and is non-magnetic. Despite its high Ti content, 60NiTi is non-galling even under dry sliding. No other bearing alloy, metallic or ceramic, encompasses all of these attributes. Since 60NiTi contains such a high proportion of Ti and possesses many metallic properties, it was expected to exhibit poor tribological performance typical of Ti alloys, namely galling type behavior and rapid lubricant degradation. In this poster-paper, the oil-lubricated behavior of 60NiTi is presented.

  2. Mechanical Properties of Magnesium-Rare Earth Alloy Systems: A Review

    Directory of Open Access Journals (Sweden)

    Sravya Tekumalla

    2014-12-01

    Full Text Available Magnesium-rare earth based alloys are increasingly being investigated due to the formation of highly stable strengthening phases, activation of additional deformation modes and improvement in mechanical properties. Several investigations have been done to study the effect of rare earths when they are alloyed to pure magnesium and other Mg alloys. In this review, the mechanical properties of the previously investigated different magnesium-rare earth based binary alloys, ternary alloys and other higher alloys with more than three alloying elements are presented.

  3. Microstructure and mechanical properties of thixoformed A319 aluminium alloy

    International Nuclear Information System (INIS)

    Salleh, M.S.; Omar, M.Z.; Syarif, J.; Alhawari, K.S.; Mohammed, M.N.

    2014-01-01

    Highlights: • A319 was successfully thixoformed at 50% liquid, i.e. at 571 °C. • T6 heat treatment has increased the strength and hardness of the thixoformed alloy. • The elongation after T6 heat treatment is even significantly improved. • The iron-rich intermetallic phase reduces the strength of the thixoformed alloy. - Abstract: Thixoforming is a viable technology for forming alloys in a semisolid state into near net-shaped products. In the present study, the effect of a thixoforming process on the microstructure and mechanical properties of A319 aluminium alloy was investigated. The ingots obtained from the cooling slope were thixoformed in a press after they remained at 571 °C for 5 min, yielding a microstructure predominantly composed of α-Al globules and inter-globular Si particles. Some of the thixoformed samples were treated with an ageing process (T6) and then, hardness and tensile samples were prepared from the as-cast, as-thixoformed and thixoformed T6. All the thixoformed samples were characterised using optical microscopy, scanning electron microscopy (SEM), energy dispersive X-ray (EDX) and X-ray diffraction (XRD) as well as hardness measurements and tensile tests. The results indicate that the mechanical properties of the thixoformed A319 alloy increased after the T6 heat treatment (hardness of 124.2 ± 3.2 HV, tensile strength of 298 ± 3.0 MPa, yield strength of 201 ± 2.6 MPa and elongation to fracture of 4.5 ± 0.3%). The fracture samples from the tensile test were analysed, revealing that the iron-rich intermetallic observed in the samples reduced the tensile strength and ductility of the thixoformed A319 alloys

  4. Effect of Mechanical Alloying Atmospheres and Oxygen Concentration on Mechanical Properties of ODS Ferritic Steels

    International Nuclear Information System (INIS)

    Noh, Sanghoon; Choi, Byoungkwon; Han, Changhee; Kim, Kibaik; Kang, Sukhoon; Chun, Youngbum; Kim, Taekyu

    2013-01-01

    Finely dispersed nano-oxide particles with a high number density in the homogeneous grain matrix are essential to achieve superior mechanical properties at high temperatures, and these unique microstructures can be obtained through the mechanical alloying (MA) and hot consolidation process. The microstructure and mechanical property of ODS steel significantly depends on its powder property and the purity after the MA process. These contents should be carefully controlled to improve the mechanical property at elevated temperature. In particular, appropriate the control of oxygen concentration improves the mechanical property of ODS steel at high temperature. An effective method is to control the mechanical alloying atmosphere by high purity inert gas. In the present study, the effects of mechanical alloying atmospheres and oxygen concentration on the mechanical property of ODS steel were investigated. ODS ferritic alloys were fabricated in various atmospheres, and the HIP process was used to investigate the effects of MA atmospheres and oxygen concentration on the microstructure and mechanical property. ODS ferritic alloys milled in an Ar-H 2 mixture, and He is effective to reduce the excess oxygen concentration. The YH 2 addition made an extremely reduced oxygen concentration by the internal oxygen reduction reaction and resulted in a homogeneous microstructure and superior creep strength

  5. Synergistic alloying effect on microstructural evolution and mechanical properties of Cu precipitation-strengthened ferritic alloys

    International Nuclear Information System (INIS)

    Wen, Y.R.; Li, Y.P.; Hirata, A.; Zhang, Y.; Fujita, T.; Furuhara, T.; Liu, C.T.; Chiba, A.; Chen, M.W.

    2013-01-01

    We report the influence of alloying elements (Ni, Al and Mn) on the microstructural evolution of Cu-rich nanoprecipitates and the mechanical properties of Fe–Cu-based ferritic alloys. It was found that individual additions of Ni and Al do not give rise to an obvious strengthening effect, compared with the binary Fe–Cu parent alloy, although Ni segregates at the precipitate/matrix interface and Al partitions into Cu-rich precipitates. In contrast, the co-addition of Ni and Al results in the formation of core–shell nanoprecipitates with a Cu-rich core and a B2 Ni–Al shell, leading to a dramatic improvement in strength. The coarsening rate of the core–shell precipitates is about two orders of magnitude lower than that of monolithic Cu-rich precipitates in the binary and ternary Fe–Cu alloys. Reinforcement of the B2 Ni–Al shells by Mn partitioning further improves the strength of the precipitation-strengthened alloys by forming ultrastable and high number density core–shell nanoprecipitates

  6. Mechanical characterization and constitutive modeling of Mg alloy sheets

    International Nuclear Information System (INIS)

    Mekonen, M. Nebebe; Steglich, D.; Bohlen, J.; Letzig, D.; Mosler, J.

    2012-01-01

    Highlights: ► Material characterization of the Mg alloys AZ31 and ZE10 at elevated temperatures. ► Distortion of the yield locus does not depend on the strain rate. ► Novel constitutive model suitable for the analysis of sheet forming of magnesium. ► Strain-dependent r-values are included within the model. ► The model is thermodynamically consistent and accounts for distortional hardening. - Abstract: In this paper, an experimental mechanical characterization of the magnesium alloys ZE10 and AZ31 is performed and a suitable constitutive model is established. The mechanical characterization is based on uniaxial tensile tests. In order to avoid poor formability at room temperature, the tests were conducted at elevated temperature (200 °C). The uniaxial tensile tests reveal sufficient ductility allowing sheet forming processes at this temperature. The differences in yield stresses and plastic strain ratios (r-values) confirm the anisotropic response of the materials under study. The constitutive model is established so that the characteristic mechanical features observed in magnesium alloys such as anisotropy and compression-tension asymmetry can be accommodated. This model is thermodynamically consistent, incorporates rate effect, is formulated based on finite strain plasticity theory and is applicable in sheet forming simulations of magnesium alloys. More precisely, a model originally proposed by Cazacu and Barlat in 2004 and later modified to account for the evolution of the material anisotropy is rewritten in a thermodynamically consistent framework. The calibrated constitutive model is shown to capture the characteristic mechanical features observed in magnesium alloy sheets.

  7. Evaluation of the mechanical properties of powder metallurgy Ti-6Al-7Nb alloy.

    Science.gov (United States)

    Bolzoni, L; Ruiz-Navas, E M; Gordo, E

    2017-03-01

    Titanium and its alloys are common biomedical materials owing to their combination of mechanical properties, corrosion resistance and biocompatibility. Powder metallurgy (PM) techniques can be used to fabricate biomaterials with tailored properties because changing the processing parameters, such as the sintering temperature, products with different level of porosity and mechanical performances can be obtained. This study addresses the production of the biomedical Ti-6Al-7Nb alloy by means of the master alloy addition variant of the PM blending elemental approach. The sintering parameters investigated guarantee that the complete diffusion of the alloying elements and the homogenization of the microstructure is achieved. The sintering of the Ti-6Al-7Nb alloy induces a total shrinkage between 7.4% and 10.7% and the level of porosity decreases from 6.2% to 4.7% with the increment of the sintering temperature. Vickers hardness (280-300 HV30) and tensile properties (different combination of strength and elongation around 900MPa and 3%) are achieved. Copyright © 2016 Elsevier Ltd. All rights reserved.

  8. Amorphization of Fe-based alloy via wet mechanical alloying assisted by PCA decomposition

    Energy Technology Data Exchange (ETDEWEB)

    Neamţu, B.V., E-mail: Bogdan.Neamtu@stm.utcluj.ro [Materials Science and Engineering Department, Technical University of Cluj-Napoca, 103-105, Muncii Avenue, 400641, Cluj-Napoca (Romania); Chicinaş, H.F.; Marinca, T.F. [Materials Science and Engineering Department, Technical University of Cluj-Napoca, 103-105, Muncii Avenue, 400641, Cluj-Napoca (Romania); Isnard, O. [Université Grenoble Alpes, Institut NEEL, F-38042, Grenoble (France); CNRS, Institut NEEL, 25 rue des martyrs, BP166, F-38042, Grenoble (France); Pană, O. [National Institute for Research and Development of Isotopic and Molecular Technologies, 65-103 Donath Street, 400293, Cluj-Napoca (Romania); Chicinaş, I. [Materials Science and Engineering Department, Technical University of Cluj-Napoca, 103-105, Muncii Avenue, 400641, Cluj-Napoca (Romania)

    2016-11-01

    Amorphization of Fe{sub 75}Si{sub 20}B{sub 5} (at.%) alloy has been attempted both by wet and dry mechanical alloying starting from a mixture of elemental powders. Powder amorphization was not achieved even after 140 hours of dry mechanical alloying. Using the same milling parameters, when wet mechanical alloying was used, the powder amorphization was achieved after 40 h of milling. Our assumption regarding the powder amorphization capability enhancement by contamination with carbon was proved by X-ray Photoelectron Spectroscopy (XPS) measurements which revealed the presence of carbon in the chemical composition of the wet mechanically alloyed sample. Using shorter milling times and several process control agents (PCA) (ethanol, oleic acid and benzene) with different carbon content it was proved that the milling duration required for powder amorphization is linked to the carbon content of the PCA. Differential Scanning Calorimetry (DSC), thermomagnetic (TG) and X-ray Diffraction (XRD) measurements performed to the heated samples revealed the fact that, the crystallisation occurs at 488 °C, thus leading to the formation of Fe{sub 3}Si and Fe{sub 2}B. Thermogravimetry measurements performed under H{sub 2} atmosphere, showed the same amount of contamination with C, which is about 2.3 wt%, for the amorphous samples regardless of the type of PCA. Saturation magnetisation of the wet milled samples decreases upon increasing milling time. In the case of the amorphous samples wet milled with benzene up to 20 h and with oleic acid up to 30 h, the saturation magnetisation has roughly the same value, indicating the same degree of contamination. The XRD performed on the samples milled using the same parameters, revealed that powder amorphization can be achieved even via dry milling, just by adding the equivalent amount of elemental C calculated from the TG plots. This proves that in this system by considering the atomic species which can contaminate the powder, they can be

  9. A new technique to modify hypereutectic Al-24%Si alloys by a Si-P master alloy

    Energy Technology Data Exchange (ETDEWEB)

    Wu Yaping; Wang Shujun; Li Hui [Key Laboratory of Liquid Structure and Heredity of Materials, Ministry of Education, Shandong University, 73 Jingshi Road, Jinan 250061 (China); Liu Xiangfa [Key Laboratory of Liquid Structure and Heredity of Materials, Ministry of Education, Shandong University, 73 Jingshi Road, Jinan 250061 (China)], E-mail: xfliu@sdu.edu.cn

    2009-05-27

    The modification effect of a Si-P master alloy on Al-24%Si alloy was investigated by using electron probe micro-analyzer (EPMA) and optical microscopy (OM). The dissolution problem of the Si-P master alloys was solved by changing the sequence of addition. When the Si-P master alloy was added into Al melt before the addition of silicon, the best modification effect could be achieved. The modification parameters of the master alloy on Al-24%Si alloy were optimized through designing and analyzing the orthogonal experiment, and their influences on the modification effect were discussed. The results show that the influence of temperature on the modification effect is the greatest, followed by the addition level, and the holding time is the least. The optimized modification parameters are the modification temperature of 810 deg. C, the addition level of 0.35 wt.%, the holding time of 30 min + 50 min whose meaning is that the Si-P master alloy is added firstly to the molten Al, and silicon is added 30 min later, then holding another 50 min. In addition, the modification mechanism of the Si-P master alloy on Al-24%Si alloy was also discussed.

  10. Characterization and corrosion behaviour of CoNi alloys obtained by mechanical alloying

    Energy Technology Data Exchange (ETDEWEB)

    Olvera, S. [Instituto Politécnico Nacional, ESIQIE, Departamento de Ingeniería en Metalurgia y Materiales, México, D. F. (Mexico); Universidad Autónoma de Madrid, Facultad de Ciencias, Departamento de Química-Física Aplicada, 28049 Madrid (Spain); Sánchez-Marcos, J. [Universidad Autónoma de Madrid, Facultad de Ciencias, Departamento de Química-Física Aplicada, 28049 Madrid (Spain); Palomares, F.J. [Instituto de Ciencia de Materiales de Madrid, ICMM-CSIC, Cantoblanco, 28049 Madrid (Spain); Salas, E. [Spline Spanish CRG Beamline at the European Synchrotron Radiation Facilities, ESRF, BP 220-38043, Grenoble Cedex (France); Arce, E.M. [Instituto Politécnico Nacional, ESIQIE, Departamento de Ingeniería en Metalurgia y Materiales, México, D. F. (Mexico); Herrasti, P., E-mail: pilar.herrasti@uam.es [Universidad Autónoma de Madrid, Facultad de Ciencias, Departamento de Química-Física Aplicada, 28049 Madrid (Spain)

    2014-07-01

    CoNi alloys including Co{sub 30}Ni{sub 70}, Co{sub 50}Ni{sub 50} and Co{sub 70}Ni{sub 30} were prepared via mechanical alloying using Co and Ni powders. The crystallinity and short-range order were studied using X-ray diffraction and X-ray absorption spectroscopy. The results show that the milling process increases the number of vacancies, especially around the Co atoms, while the milling time decreases the crystalline size and enhances the crystallinity. X-ray photoelectron spectroscopy was used to characterise the chemical composition of the samples surface. The magnetic properties were analysed using zero-field cooling, field cooling and a magnetic hysteresis loops. The magnetic saturation moment is approximately 1.05 μ{sub B}/atom; this value decreases with the mechanical alloying time, and it is proportional to the cobalt concentration. The polarization and impedance curves in different media (NaCl, H{sub 2}SO{sub 4} and NaOH) showed similar corrosion resistance values. The corrosion resistance increased in the order NaCl, H{sub 2}SO{sub 4} and NaOH. A good passivation layer was formed in NaOH due to the cobalt and nickel oxides on the particle surfaces. - Highlights: • Ni{sub x}Co{sub 100-x} alloys were synthesized by mechanical alloying • Milling time decrease size and enhances crystallinity. • Oxygen is not present in a significant percentage in bulk but is detected on the surface. • Magnetic saturation moment is 1.05 mB/atom and decrease with mechanical allowing time • Corrosion resistance is higher in NaOH than in NaCl or HCl solutions.

  11. Characterization and corrosion behaviour of CoNi alloys obtained by mechanical alloying

    International Nuclear Information System (INIS)

    Olvera, S.; Sánchez-Marcos, J.; Palomares, F.J.; Salas, E.; Arce, E.M.; Herrasti, P.

    2014-01-01

    CoNi alloys including Co 30 Ni 70 , Co 50 Ni 50 and Co 70 Ni 30 were prepared via mechanical alloying using Co and Ni powders. The crystallinity and short-range order were studied using X-ray diffraction and X-ray absorption spectroscopy. The results show that the milling process increases the number of vacancies, especially around the Co atoms, while the milling time decreases the crystalline size and enhances the crystallinity. X-ray photoelectron spectroscopy was used to characterise the chemical composition of the samples surface. The magnetic properties were analysed using zero-field cooling, field cooling and a magnetic hysteresis loops. The magnetic saturation moment is approximately 1.05 μ B /atom; this value decreases with the mechanical alloying time, and it is proportional to the cobalt concentration. The polarization and impedance curves in different media (NaCl, H 2 SO 4 and NaOH) showed similar corrosion resistance values. The corrosion resistance increased in the order NaCl, H 2 SO 4 and NaOH. A good passivation layer was formed in NaOH due to the cobalt and nickel oxides on the particle surfaces. - Highlights: • Ni x Co 100-x alloys were synthesized by mechanical alloying • Milling time decrease size and enhances crystallinity. • Oxygen is not present in a significant percentage in bulk but is detected on the surface. • Magnetic saturation moment is 1.05 mB/atom and decrease with mechanical allowing time • Corrosion resistance is higher in NaOH than in NaCl or HCl solutions

  12. Formation of Al70Cu20Fe10 icosahedral quasicrystal by mechanically alloyed method

    International Nuclear Information System (INIS)

    Yin Shilong; Bian Qing; Qian Liying; Zhang Aimei

    2007-01-01

    The structural evolutions of the mechanically alloyed ternary Al 70 Cu 20 Fe 10 powders with the milling time and the annealing treatment have been studied by X-ray diffraction (XRD), transmission electronic microscopy (TEM) and X-ray absorption fine-structure spectroscopy (XAFS) techniques. Results show that an Al 2 Cu compound forms with short-time milling, while a Cu 9 Al 4 compound forms with long-time milling. Fe can react with Al-Cu alloy by annealing treatment. Al 7 Cu 2 Fe compound with tetragonal structure or Al (Cu, Fe) solid solution with cubic structure may form at lower temperature, while a quasicrystal phase of Al 65 Cu 20 Fe 15 alloy may form at higher temperature

  13. Structure and mechanical properties of Al-3Fe rapidly solidified alloy

    International Nuclear Information System (INIS)

    Karakoese, Ercan; Keskin, Mustafa

    2011-01-01

    The Al based Al-3 wt%Fe alloy was prepared by conventionally casting (ingot) and further processed the melt-spinning technique and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) together with energy dispersive spectroscopy (EDS), differential scanning calorimetry (DSC) and the Vickers microhardness tester. The rapidly solidified (RS) binary alloys were composed of supersaturated α-Al solid solution and finely dispersed intermetallic phases. Experimental results showed that the mechanical properties of RS alloys were enhanced, which can be attributed to significant changes in the microstructure. The dependence of microhardness H V on the solidification rate (V) was analysed. These results showed that with the increasing values of V, the values of H V increased.

  14. Study of localized corrosion in aluminum alloys by the scanning reference electrode technique

    Science.gov (United States)

    Danford, M. D.

    1995-01-01

    Localized corrosion in 2219-T87 aluminum (Al) alloy, 2195 aluminum-lithium (Al-Li) alloy, and welded 2195 Al-Li alloy (4043 filler) have been investigated using the relatively new scanning reference electrode technique (SRET). Anodic sites are more frequent and of greater strength in the 2195 Al-Li alloy than in the 2219-T87 Al alloy, indicating a greater tendency toward pitting for the latter. However, the overall corrosion rates are about the same for these two alloys, as determined using the polarization resistance technique. In the welded 2195 Al-Li alloy, the weld bean is entirely cathodic, with rather strongly anodic heat affected zones (HAZ) bordering both sides, indicating a high probability of corrosion in the HAZ parallel to the weld bead.

  15. Stress corrosion of alloy 600: mechanism proposition

    International Nuclear Information System (INIS)

    Magnin, T.

    1993-01-01

    A fissuring model by stress corrosion based on interactions corrosion-plasticity on the fissure top is proposed to describe the generally intergranular bursting of INCONEL 600 in the PWR. The calculation shows, and some observations check experimentally, that a pseudo intergranular cracking bound to the zigzag micro facets formation along the joints may be so that a completely intergranular bursting. This pseudo intergranular mode makes up a signature of the proposed mechanism. It may be suggested that it may exist one continuity mechanism between the trans and intergranular cracking by stress corrosion of ductile cubic centered faces materials. 2 figs

  16. Studies on Al-Cu-Li-Mg-Ag-Zr alloy processed through vacuum induction melting (VIM) technique

    International Nuclear Information System (INIS)

    Nayan, Niraj; Govind; Nair, K. Suseelan; Mittal, M.C.; Sudhakaran, K.N.

    2007-01-01

    A new technique of lithium addition has been adapted for the processing of Al-Cu-Li-Ag-Mg-Zr alloy, which gives more than 90% recovery of lithium throughout the billet. Processing studies on this alloy include casting, three step homogenization, to avoid incipient melting, and mechanical working particularly forging and rolling. The products in the form of sheets were subjected to various T6 (solution treatment + water quenching + aging) tempers. Mechanical properties were evaluated at room temperature and correlated with microstructure. Characterizations using optical microscope and post-fracture analysis have been carried out using Scanning electron microscope (SEM). Experimental investigation shows highest mechanical properties for the Al-1.3%Li alloy in T6 (500 deg. C/1 h + WQ + 190 deg. C/24 h) condition

  17. Mechanical properties of a high-strength Al{sub 90}Mn{sub 8}Ce{sub 2} alloy

    Energy Technology Data Exchange (ETDEWEB)

    Li, J.C.; Zhao, Z.K.; Jiang, Q. [Key Laboratory of Automobile Materials, Ministry of Education and Department of Materials Science and Engineering, Jilin University, Changchun 130025 (China)

    2003-03-01

    A lightweight alloy with excellent strength and wear resistance, Al{sub 90}Mn{sub 8}Ce{sub 2}, has been manufactured in bulk by powder metallurgy. The best colligative mechanical properties of the alloy made by this technique are achieved by pressing at 753 K, where the porosity reaches a minimum, and the plasticity a maximum. (Abstract Copyright [2003], Wiley Periodicals, Inc.)

  18. Thermal, electrical and mechanical properties during cristallization of the amorphous alloy Co33Zr67

    International Nuclear Information System (INIS)

    Nicolaus, M.M.

    1992-01-01

    Topic of this work is to study the crystallization process of amorphous CO 33 Zr 67 alloy and to characterize its thermal, electrical and mechanical properties. Studies were carried out by calorimetry, vibrating-Reed technique, electrical-resistance measurement, dilatometry, X-ray diffraction and electron-transmission-microscopy. Results of microstructure analysis, kinetic analysis, specific heat, dilatometry (isothermal and non-isothermal) and electrical resistance are discussed in detail here

  19. Elevated temperature mechanical properties of a rapidly solidified A1-Fe-V-Si alloy

    International Nuclear Information System (INIS)

    Mitra, S.

    1992-01-01

    Dispersion strengthened Al alloys based on the Al-Fe-V-Si quartenary system have recently been developed using rapid solidification techniques. Rapid solidification techniques which resulted in the above mentioned alloys have also been used to manufacture another commercial alloy, FVS 1212, with 37 volume % of dispersoid. The alloy has shown excellent resistance to coarsening at high temperatures and to creep deformation. Elevated temperature exposure of FVS 1212, for times up to 100 hours, resulted in a significant loss in room temperature mechanical properties only beyond 500 degrees C while 1000 hours at 425 degrees C did not result in any degradation of mechanical but no detailed study of the tensile behavior of FVS 1212 at slow strain rates and elevated temperatures has been reported to date. This paper reports that the present study was undertaken to investigate the tensile behavior of FVS 1212 from room temperature to 400 degrees C at strain rates of 6.56 x 10 - 5/sec and 6.56 x 10 -6 /sec. The study focussed on dynamic strain aging effects and strain hardening behavior, while the effect of strain rate on the flow behavior at elevated temperatures was also evaluated

  20. Mechanical properties and structure of magnesium alloy AS31

    Directory of Open Access Journals (Sweden)

    A. Hanus

    2008-07-01

    Full Text Available Contemporary materials should possess high mechanical properties, physical and chemical, as well as technological ones, to ensure long and reliable use. The non-ferrous metals alloys used nowadays, including the magnesium alloys, meet the above-mentioned requirements and expectations regarding the contemporary materials.Magnesium alloys are primarily used in aeronautical and automobile industry in wide variety of structural characteristics because of their favorable combination of tensile strength (160 to 365 MPa, elastic modulus (45 GPa, and low density (1 740 kg/m3, which is two-thirds that of aluminum. Magnesium alloys have high strength-to-weight ratio (tensile strength/density, comparable to those of other structural metals. [1-6]Knowledge of the relaxation properties of metal materials at high temperatures is necessary for the verification of susceptibility of castings to the creation of defects during the production process. Temperature limits of materials where highest tension values are generated may be detected with tensile tests under high temperatures. The generated tensions in the casting are a cause of the creation and development of defects. At acoustic emission (hereinafter called the "AE" use, tensile tests at high temperatures may, among other things, be used for analysis of the AE signal sources and set, in more detail, the temperature limit of elastic-plastic deformations existence in the material under examination. The results of the temperature drop where tension at casting cooling is generated or its release at heating are basic data for controlled cooling mode (and temperature of casting knocking out of the form as well as necessary for the thermal mode for the casting tension reduction. [7-9]Knowledge of elastic-plastic properties at elevated temperatures is often important for complex evaluation of magnesium alloys. Objective of the work was focused on determination of changes of elastic-plastic properties of magnesium

  1. Evaluation of interfacial microstructures in dissimilar joints of aluminum alloys to steel using nanoindentation technique

    International Nuclear Information System (INIS)

    Ogura, Tomo; Hirose, Akio; Saito, Yuichi; Ueda, Keisuke

    2009-01-01

    The characteristics of interfacial microstructures with additional elements in dissimilar 6000 system aluminum/steel joints were basically evaluated using tensile test, EPMA, TEM and nanoindentation. For Si (and Cu)-added alloy (S1 and SC), EPMA analysis showed that Si (and Cu) was enrichment in the reaction layers, which were formed during diffusion bonding. SAED pattern clarified that the reaction compounds at the interface changed from AlFe intermetalic compounds to AlFeSi intermetalic compounds by Si addition. Nanoindentation technique was successfully applied to the interfacial microstructures to understand directly the nanoscopic mechanical properties in the interfacial microstructures. The hardness and Young's modulus of Al 3 Fe intermetalic compounds was lower than those of Al 2 Fe 5 intermetalic compounds. Moreover, the hardness and Young's modulus of AlFeSi(Cu) compounds were lower than those of Al 3 Fe, indicating that the crystal system changed from orthorhombic structure to cubic structure. Joint strength of SC/steel joints was higher than that of the aluminum alloy with no additional element (Base)/ steel joint, indicating that interfacial microstructure was modified by the addition of Si and Cu to the 6000 system aluminum alloy. These results suggest that the nanoscopic mechanical properties at the interface microstructures affect greatly the macroscopic deformation behavior of the aluminum /steel dissimilar joints.

  2. Investigating deformation processes in AM60 magnesium alloy using the acoustic emission technique

    International Nuclear Information System (INIS)

    Mathis, K.; Chmelik, F.; Janecek, M.; Hadzima, B.; Trojanova, Z.; Lukac, P.

    2006-01-01

    Microstructure changes in an AM60 magnesium alloy were monitored using the acoustic emission (AE) technique during tensile tests in the temperature range from 20 to 300 deg. C. The correlation of the AE signal and the deformation processes is discussed. It is shown, using transmission electron and light microscopy, that the character of the AE response is associated with various modes of mechanical twinning at lower temperatures, whereas at higher temperatures also the influence of non-basal dislocations on the AE response must be taken into account

  3. Evaluation of mechanical properties of Aluminum-Copper cold sprayed and alloy 625 wire arc sprayed coatings

    Science.gov (United States)

    Bashirzadeh, Milad

    This study examines microstructural-based mechanical properties of Al-Cu composite deposited by cold spraying and wire arc sprayed nickel-based alloy 625 coating using numerical modeling and experimental techniques. The microhardness and elastic modulus of samples were determined using the Knoop hardness technique. Hardness in both transverse and longitudinal directions on the sample cross-sections has been measured. An image-based finite element simulation algorithm was employed to determine the mechanical properties through an inverse analysis. In addition mechanical tests including, tensile, bending, and nano-indentation tests were performed on alloy 625 wire arc sprayed samples. Overall, results from the experimental tests are in relatively good agreement for deposited Al-Cu composites and alloy 625 coating. However, results obtained from numerical simulation are significantly higher in value than experimentally obtained results. Examination and comparison of the results are strong indications of the influence of microstructure characteristics on the mechanical properties of thermally spray deposited coatings.

  4. Vanadium alloys for structural applications in fusion systems: A review of vanadium alloy mechanical and physical properties

    Energy Technology Data Exchange (ETDEWEB)

    Loomis, B.A.; Smith, D.L.

    1991-12-16

    The current knowledge is reviewed on (1) the effects of neutron irradiation on tensile strength and ductility, ductile-brittle transition temperature, creep, fatigue, and swelling of vanadium-base alloys, (2) the compatibility of vanadium-base alloys with liquid lithium, water, and helium environments, and (3) the effects of hydrogen and helium on the physical and mechanical properties of vanadium alloys that are potential candidates for structural materials applications in fusion systems. Also, physical and mechanical properties issues are identified that have not been adequately investigated in order to qualify a vanadium-base alloy for the structural material in experimental fusion devices and/or in fusion reactors.

  5. Powder-metallurgy preparation of NiTi shape-memory alloy using mechanical alloying and spark-plasma sintering.

    Czech Academy of Sciences Publication Activity Database

    Novák, P.; Moravec, H.; Vojtěch, V.; Knaislová, A.; Školáková, A.; Kubatík, Tomáš František; Kopeček, Jaromír

    2017-01-01

    Roč. 51, č. 1 (2017), s. 141-144 ISSN 1580-2949 R&D Projects: GA ČR(CZ) GA14-03044S Institutional support: RVO:61389021 ; RVO:68378271 Keywords : mechanical alloying * spark plasma sintering * NiTi * shape memory alloy Subject RIV: JG - Metallurgy; JG - Metallurgy (FZU-D) OBOR OECD: Materials engineering ; Materials engineering (FZU-D) Impact factor: 0.436, year: 2016 https://www.researchgate.net/publication/313900224_Powder-metallurgy_preparation_of_NiTi_shape-memory_alloy_using_mechanical_alloying_and_spark-plasma_sintering

  6. Vanadium alloys for structural applications in fusion systems: A review of vanadium alloy mechanical and physical properties

    International Nuclear Information System (INIS)

    Loomis, B.A.; Smith, D.L.

    1991-01-01

    The current knowledge is reviewed on (1) the effects of neutron irradiation on tensile strength and ductility, ductile-brittle transition temperature, creep, fatigue, and swelling of vanadium-base alloys, (2) the compatibility of vanadium-base alloys with liquid lithium, water, and helium environments, and (3) the effects of hydrogen and helium on the physical and mechanical properties of vanadium alloys that are potential candidates for structural materials applications in fusion systems. Also, physical and mechanical properties issues are identified that have not been adequately investigated in order to qualify a vanadium-base alloy for the structural material in experimental fusion devices and/or in fusion reactors

  7. Test techniques for fracture mechanics testing

    International Nuclear Information System (INIS)

    Schwalbe, K.H.

    1980-01-01

    Test methods for fracture mechanics tests are described. Two groups of techniques are distinguished: Those for measurement of stable crack growth and those for determination of the loading parameters. (orig.) [de

  8. Emerging Dynamic Design Techniques for Mechanical and ...

    Indian Academy of Sciences (India)

    Emerging Dynamic Design Techniques for Mechanical ... through this school to bring about an awareness of the state-of-art of the software and ... those mentioned above, cannot be ensured on the basis of approaches involving numerical.

  9. Dynamic Mechanical Behaviors of 6082-T6 Aluminum Alloy

    Directory of Open Access Journals (Sweden)

    Peng Yibo

    2013-01-01

    Full Text Available The structural components of high speed trains are usually made of aluminum alloys, for example, 6082. The dynamic mechanical behavior of the material is one of key factors considered in structural design and safety assessment. In this paper, dynamic mechanical experiments were conducted with strain rate ranging from 0.001 s−1 to 100 s−1 using Instron tensile testing machine. The true stress-strain curves were fitted based on experimental data. Johnson-Cook model of 6082-T6 aluminum alloy was built to investigate the effect of strain and strain rate on flow stress. It has shown that the flow stress was sensitive to the strain rate. Yield strength and tensile strength increased with a high strain rate, which showed strain rate effect to some extent. Fracture analysis was carried out by using Backscattered Electron imaging (BSE. As strain rate increased, more precipitates were generated in fracture.

  10. Acoustic emission from zirconium alloys during mechanical and fracture testing

    International Nuclear Information System (INIS)

    Coleman, C.E.

    1986-10-01

    The application of acoustic emission during the mechanical and fracture testing of zirconium alloys is reviewed. Acoustic emission is successful in following delayed hydride cracking quantitatively. It is especially useful when great sensitivity is required. Application to fatigue, tensile deformation and stress corrosion cracking appears promising but requires more work to separate phenomena before it can be used quantitatively. This report is based on an invited review for the American Society of Non-Destructive Testing Handbook: Volume 5, Acoustic Emission Testing

  11. Mechanical alloying of the FeNi-Ag system

    International Nuclear Information System (INIS)

    Gonzalez, G.; Ibarra, D.; Ochoa, J.; Villalba, R.; Sagarzazu, A.

    2007-01-01

    The Fe-Ni-Ag system is of particular interest for its potential applications as soft magnetic granular material with small magnetic grains embedded in a non-magnetic metal matrix. Under equilibrium conditions: Fe-Ag and Ni-Ag are immiscible and Fe-Ni shows complete solubility. These materials are particularly important for magnetoresistivity properties. The properties of these alloys are closely related to their microstructure; therefore, a detailed study of the transformations occurring during milling was undertaken using pre-alloyed Fe x Ni 100-x (x = 30, 50 and 70) further milled with different Ag content to give the following alloys compositions (Fe x -Ni 100-x ) 100-y Ag y (y = 5, 20, 60). Consolidation of the mechanically alloyed powders by sintering at 950 o C was performed. Morphological and structural characterization of the sintered powders was carried out by scanning and transmission electron microscopy and X-ray diffraction. Fe 30 Ni 70 and Fe 50 Ni 50 formed ordered FeNi 3 compound. Fe 70 Ni 30 showed the formation of a mixture of γ-(Fe,Ni) and α-Fe(Ni) solid solutions. The mixture of these systems with Ag showed the metal solid solutions surrounded by Ag islands of Fe x Ni y -Ag, There was also evidence of Ag diffusing into the γ-(Fe,Ni). High Ag content (60%) shows formation of islands of FeNi surrounded by Ag. Sintering is always improved with the Ag content

  12. Projection operator techniques in nonequilibrium statistical mechanics

    International Nuclear Information System (INIS)

    Grabert, H.

    1982-01-01

    This book is an introduction to the application of the projection operator technique to the statistical mechanics of irreversible processes. After a general introduction to the projection operator technique and statistical thermodynamics the Fokker-Planck and the master equation approach are described together with the response theory. Then, as applications the damped harmonic oscillator, simple fluids, and the spin relaxation are considered. (HSI)

  13. Structural investigations of mechanical properties of Al based rapidly solidified alloys

    International Nuclear Information System (INIS)

    Karakoese, Ercan; Keskin, Mustafa

    2011-01-01

    Highlights: → Rapid solidification processing (RSP) involves exceptionally high cooling rates. → We correlate the microstructure of the intermetallic Al 3 Fe, Al 2 Cu and Al 3 Ni phases with the cooling rate. → The solidification rate is high enough to retain most of alloying elements in the Al matrix. → The rapid solidification has effect on the phase constitution. -- Abstract: In this study, Al based Al-3 wt.%Fe, Al-3 wt.%Cu and Al-3 wt.%Ni alloys were prepared by conventional casting. They were further processed using the melt-spinning technique and characterized by the X-ray diffraction (XRD), scanning electron microscopy (SEM) together with energy dispersive spectroscopy (EDS), transmission electron microscope (TEM), differential scanning calorimetry (DSC) and the Vickers microhardness tester. The rapidly solidified (RS) binary alloys were composed of supersaturated α-Al solid solution and finely dispersed intermetallic phases. Experimental results showed that the mechanical properties of RS alloys were enhanced, which can be attributed to significant changes in the microstructure. RS samples were measured using a microhardness test device. The dependence of microhardness H V on the solidification rate (V) was analysed. These results showed that with the increasing values of V, the values of H V increased. The enthalpies of fusion for the same alloys were determined by DSC.

  14. Studies of the mechanisms involved in the laser surface hardening process of aluminum base alloys

    International Nuclear Information System (INIS)

    Silva, Luciana Ventavele da

    2011-01-01

    The Al-Si alloys are widely used in industry to replace the steel and gray cast iron in high-tech sectors. The commercial importance of these alloys is mainly due to its low weight, excellent wear (abrasion) and corrosion resistance, high resistance at elevated temperatures, low coefficient of thermal expansion and lesser fuel consumption that provide considerable reduction of emission of pollutants. In this work, Al-Si alloy used in the automotive industry to manufacture pistons of internal combustion engines, was undergone to surface treatments using LASER remelting (Nd:YAG, λ = 1.06 μm, pulsed mode). The LASER enables various energy concentrations with accurate transfer to the material without physical contact. The intense energy transfer causes the occurrence of structural changes in the superficial layer of the material. Experiments with single pulses and trails were conducted under various conditions of LASER processing in order to analyze microstructural changes resulting from treatments and their effects on the hardness. For the characterization of hardened layer was utilized the following techniques: optical microscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), x-ray mapping, Vickers microhardness and maximum roughness tests. The high cooling rate caused a change in the alloy structure due to the refinement of the primary eutectic silicon particles, resulting in increase of the mechanical properties (hardness) of the Al-Si alloy. (author)

  15. Fabrication and Characterization of novel W80Ni10Nb10 alloy produced by mechanical alloying

    Science.gov (United States)

    Saxena, R.; Patra, A.; Karak, S. K.; Pattanaik, A.; Mishra, S. C.

    2016-02-01

    Nanostructured tungsten (W) based alloy with nominal composition of W80Ni10Nb10 (in wt. %) was synthesized by mechanical alloying of elemental powders of tungsten (W), nickel (Ni), niobium (Nb) in a high energy planetary ball-mill for 20 h using chrome steel as grinding media and toluene as process control agent followed by compaction at 500 MPa pressure for 5 mins and sintering at 1500°C for 2 h in Ar atmosphere. The phase evolution and the microstructure of the milled powder and consolidated product were investigated by X-ray diffraction (XRD), Scanning electron microscopy (SEM) and Transmission electron microscopy (TEM). The crystallite size of W in W80Ni10Nb10 powder was reduced from 100 μm at 0 h to 45.6 nm at 10 h and 34.1 nm at 20 h of milling whereas lattice strain increases to 35% at 20 h of milling. The dislocation density shows sharp increase up to 5 h of milling and the rate of increase drops beyond 5 to 20 h of milling. The lattice parameter of tungsten in W80Ni10Nb10 expanded upto 0.04% at 10 h of milling and contracted upto 0.02% at 20 h of milling. The SEM micrograph revealed the presence of spherical and elongated particles in W80Ni10Nb10 powders at 20 h of milling. The particle size decreases from 100 μm to 2 μm with an increase in the milling time from 0 to 20 hours. The crystallite size of W in milled W80Ni10Nb10 alloy as evident from bright field TEM image was in well agreement with the measured crystallite size from XRD. Structure of W in 20 h milled W80Ni10Nb10 alloy was identified by indexing of selected area diffraction (SAD) pattern. Formation of NbNi intermetallic was evident from XRD pattern and SEM micrograph of sintered alloy. Maximum sinterability of 90.8% was achieved in 20 h milled sintered alloy. Hardness and wear study was also conducted to investigate the mechanical behaviour of the sintered product. Hardness of W80Ni10Nb10 alloy reduces with increasing load whereas wear rate increases with increasing load. The evaluated

  16. Corrosion fatigue of biomedical metallic alloys: mechanisms and mitigation.

    Science.gov (United States)

    Antunes, Renato Altobelli; de Oliveira, Mara Cristina Lopes

    2012-03-01

    Cyclic stresses are often related to the premature mechanical failure of metallic biomaterials. The complex interaction between fatigue and corrosion in the physiological environment has been subject of many investigations. In this context, microstructure, heat treatments, plastic deformation, surface finishing and coatings have decisive influence on the mechanisms of fatigue crack nucleation and growth. Furthermore, wear is frequently present and contributes to the process. However, despite all the effort at elucidating the mechanisms that govern corrosion fatigue of biomedical alloys, failures continue to occur. This work reviews the literature on corrosion-fatigue-related phenomena of Ti alloys, surgical stainless steels, Co-Cr-Mo and Mg alloys. The aim was to discuss the correlation between structural and surface aspects of these materials and the onset of fatigue in the highly saline environment of the human body. By understanding such correlation, mitigation of corrosion fatigue failure may be achieved in a reliable scientific-based manner. Different mitigation methods are also reviewed and discussed throughout the text. It is intended that the information condensed in this article should be a valuable tool in the development of increasingly successful designs against the corrosion fatigue of metallic implants. Copyright © 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  17. Decagonal quasicrystalline phase in as-cast and mechanically alloyed Al–Cu–Cr alloys

    International Nuclear Information System (INIS)

    Shevchukov, A.P.; Sviridova, T.A.; Kaloshkin, S.D.; Tcherdyntsev, V.V.; Gorshenkov, M.V.; Churyukanova, M.N.; Zhang, D.; Li, Z.

    2014-01-01

    Highlights: ► Microstructure of as-cast Al–Cu–Cr alloys was investigated. ► Composition of decagonal quasicrystalline phase was determined. ► Single-phase decagonal quasicrystalline powder was obtained. ► Phase composition changes during heating were controlled using DSC and X-ray diffraction. -- Abstract: Microstructure and phase composition of three Al-rich as-cast alloys of Al–Cu–Cr system were investigated by X-ray diffraction analysis (XRD) and scanning electron microscopy (SEM). The decagonal quasicrystalline phase is contained in all alloys under study and has grains with faceted shape, its composition lies in the range of 71–73 at.% Al, 11–12 at.% Cu and 15–18 at.% Cr. The heating in calorimeter of the mechanically alloyed Al 73 Cu 11 Cr 16 powder up to 600 °C leads to the formation of the pure decagonal phase. Total thermal effect in the temperature range 250–600 °C corresponding to the quasicrystalline phase formation is about 15 kJ/mol

  18. Effect of Alloy Elements on Microstructures and Mechanical Properties in Al-Mg-Si Alloys

    Science.gov (United States)

    Kato, Yoshikazu; Hisayuki, Koji; Sakaguchi, Masashi; Higashi, Kenji

    Microstructures and mechanical properties in the modified Al-Mg-Si alloys with variation in the alloy elements and their contents were investigated to enhance higher strength and ductility. Optimizing both the alloy element design and the industrial processes including heat-treatments and extrusion technology was carried out along the recent suggestion from the first principles calculation. The investigation concluded that the addition of Fe and/or Cu could recovery their lost ductility, furthermore increase their tensile strength up to 420 MPa at high elongation of 24 % after T6 condition for Al-0.8mass%Mg-1.0mass%Si-0.8mass%Cu-0.5mass%Fe alloy with excess Si content. The excellent combination between strength and ductility could be obtained by improvement to the grain boundary embitterment caused by grain boundary segregation of Si as a result from the interaction of Si with Cu or Fe with optimizing the amount of Cu and Fe contents.

  19. Formation of amorphous Ti-50at.%Pt by solid state reactions during mechanical alloying

    CSIR Research Space (South Africa)

    Mahlatji, ML

    2013-10-01

    Full Text Available Mechanical alloying of an equiatomic mixture of crystalline elemental powders of Ti and Pt in a high-energy ball mill results in formation of an amorphous alloy by solid-state reactions. Mechanical alloying was carried out in an argon atmosphere...

  20. Phase evolution and thermal stability of 2 Mg–Cu alloys processed by mechanical alloying

    Energy Technology Data Exchange (ETDEWEB)

    Martínez, C., E-mail: carola.martinezu@usach.cl [Departamento de Ingeniería Metalúrgica, Facultad de Ingeniería, Universidad de Santiago de Chile, Av. Lib. Bernardo O’Higgins 3363, Casilla de correo 10233, Santiago (Chile); Ordoñez, S., E-mail: stella.ordonez@usach.cl [Departamento de Ingeniería Metalúrgica, Facultad de Ingeniería, Universidad de Santiago de Chile, Av. Lib. Bernardo O’Higgins 3363, Casilla de correo 10233, Santiago (Chile); Guzmán, D. [Departamento de Ingeniería en Metalurgia, Facultad de Ingeniería, Universidad de Atacama y CRIDESAT, Av. Copayapu 485, Casilla de Correo 240, Copiapó (Chile); Serafini, D. [Departamento de Física, Facultad de Ciencia, Universidad de Santiago de Chile, Av. Lib. Bernardo O’Higgins 3363, Casilla de correo 307, Santiago (Chile); Iturriza, I. [CEIT, Manuel de Lardizábal 15, 20018 San Sebastián, España (Spain); Bustos, O. [Departamento de Ingeniería Metalúrgica, Facultad de Ingeniería, Universidad de Santiago de Chile, Av. Lib. Bernardo O’Higgins 3363, Casilla de correo 10233, Santiago (Chile)

    2013-12-25

    Highlights: •Study of phase evolution of elemental powders Mg and Cu by mechanical alloying. •The presence of an amorphous precursor which crystallizes to Mg{sub 2}Cu can be observed. •Establishing the sequence of phase transformations leading to the formation of Mg{sub 2}Cu. •The feasibility to obtain Mg{sub 2}Cu by means two possible routes has been established. -- Abstract: Phase evolution during mechanical alloying (MA) of elemental Mg and Cu powders and their subsequent heat treatment is studied. Elemental Mg and Cu powders in a 2:1 atomic ratio were mechanically alloyed in a SPEX 8000D mill using a 10:1 ball-to-powder ratio. X-ray diffraction (XRD) shows that the formation of the intermetallic Mg{sub 2}Cu takes place between 3 and 4 h of milling, although traces of elemental Cu are still present after 10 h of milling. The thermal behavior of different powder mixtures was evaluated by differential scanning calorimetry (DSC). The combination of DSC, heat treatment and XRD has shown a sequence of phase transformations that results in the intermetallic Mg{sub 2}Cu from an amorphous precursor. This amorphous phase is converted into Mg{sub 2}Cu by heating at low temperature (407 K). Short MA times and the formation of the amorphous precursor, together with its subsequent transformation into Mg{sub 2}Cu at low temperatures; represent an advantageous alternative route for its preparation.

  1. Design, processing and characterization of mechanically alloyed galfenol & lightly rare-earth doped FeGa alloys as smart materials for actuators and transducers

    Science.gov (United States)

    Taheri, Parisa

    Smart materials find a wide range of application areas due to their varied response to external stimuli. The different areas of application can be in our day to day life, aerospace, civil engineering applications, and mechatronics to name a few. Magnetostrictive materials are a class of smart materials that can convert energy between the magnetic and elastic states. Galfenol is a magnetostrictive alloy comprised primarily of the elements iron (Fe) and gallium (Ga). Galfenol exhibits a unique combination of mechanical and magnetostrictive (magnetic) properties that legacy smart materials do not. Galfenol's ability to function while in tension, mechanical robustness and high Curie temperature (600 °C) is attracting interest for the alloy's use in mechanically harsh and elevated temperature environments. Applications actively being investigated include transducers for down-hole use, next-generation fuel injectors, sensing, and energy harvesting devices. Understanding correlations between microstructure, electronic structure, and functional response is key to developing novel magnetostrictive materials for sensor and actuator technologies. To this end, in the first part of this thesis we report successful fabrication and investigation of magnetic and magnetostrictive properties of mechanically alloyed Fe81Ga19 compounds. For the first time, we could measure magnetostrictive properties of mechanically alloyed FeGa compounds. A maximum saturation magnetostriction of 41 ppm was achieved which is comparable to those measured from polycrystalline FeGa alloys prepared by other processing techniques, namely gas atomization and cold rolling. Overall, this study demonstrates the feasibility of large-scale production of FeGa polycrystalline alloys powders by a simple and cost-effective mechanical alloying technique. In the second part of this work, we report for the first time, experimental results pertaining to successful fabrication and advanced characterization of a series

  2. Synthesis of the Mg2Ni alloy prepared by mechanical alloying using a high energy ball mill

    International Nuclear Information System (INIS)

    Iturbe G, J. L.; Lopez M, B. E.; Garcia N, M. R.

    2010-01-01

    Mg 2 Ni was synthesized by a solid state reaction from the constituent elemental powder mixtures via mechanical alloying. The mixture was ball milled for 10 h at room temperature in an argon atmosphere. The high energy ball mill used here was fabricated at ININ. A hardened steel vial and three steel balls of 12.7 mm in diameter were used for milling. The ball to powder weight ratio was 10:1. A small amount of powder was removed at regular intervals to monitor the structural changes. All the steps were performed in a little lucite glove box under argon gas, this glove box was also constructed in our Institute. The structural evolution during milling was characterized by X-ray diffraction and scanning electron microscopy techniques. The hydrogen reaction was carried out in a micro-reactor under controlled conditions of pressure and temperature. The hydrogen storage properties of mechanically milled powders were evaluated by using a thermogravimetric analysis system. Although homogeneous refining and alloying take place efficiently by repeated forging, the process time can be reduced to one fiftieth of the time necessary for conventional mechanical milling and attrition. (Author)

  3. Synthesis of the Mg{sub 2}Ni alloy prepared by mechanical alloying using a high energy ball mill

    Energy Technology Data Exchange (ETDEWEB)

    Iturbe G, J. L.; Lopez M, B. E. [ININ, Departamento de Quimica, Carretera Mexico-Toluca s/n, 52750 Ocoyoacac, Estado de Mexico (Mexico); Garcia N, M. R., E-mail: joseluis.iturbe@inin.gob.m [UNAM, Facultad de Estudios Superiores Zaragoza, Batalla 5 de Mayo s/n, Esq. Fuerte de Loreto, Col. Ejercito de Oriente, 09230 Mexico D. F. (Mexico)

    2010-07-01

    Mg{sub 2}Ni was synthesized by a solid state reaction from the constituent elemental powder mixtures via mechanical alloying. The mixture was ball milled for 10 h at room temperature in an argon atmosphere. The high energy ball mill used here was fabricated at ININ. A hardened steel vial and three steel balls of 12.7 mm in diameter were used for milling. The ball to powder weight ratio was 10:1. A small amount of powder was removed at regular intervals to monitor the structural changes. All the steps were performed in a little lucite glove box under argon gas, this glove box was also constructed in our Institute. The structural evolution during milling was characterized by X-ray diffraction and scanning electron microscopy techniques. The hydrogen reaction was carried out in a micro-reactor under controlled conditions of pressure and temperature. The hydrogen storage properties of mechanically milled powders were evaluated by using a thermogravimetric analysis system. Although homogeneous refining and alloying take place efficiently by repeated forging, the process time can be reduced to one fiftieth of the time necessary for conventional mechanical milling and attrition. (Author)

  4. Effect of Al and Y2O3 on Mechanical Properties in Mechanically Alloyed Nanograin Ni-Based Alloys.

    Science.gov (United States)

    Kim, Chung Seok; Kim, Il-Ho

    2015-08-01

    The effects of aluminum and Y2O3 on the mechanical properties in nano grain Ni-based alloys have been investigated. The test specimens are prepared by mechanical alloying at an Ar atmosphere. The addition of Y2O3 and Al may cause an increase in the tensile strength at room temperature, 400 °C and 600 °C. However, it was confirmed that the increase of tensile strength at room temperature and 400 °C was predominantly caused by addition of Y2O3, while that at 600 °C was mainly due to addition of Al. These results can be attributed to the dispersion strengthening of Y2O3, preventing the formation of Cr2O3 and the change of fracture mode at 600 °C by the addition of Al.

  5. Influence of temperature and rate of deformation on mechanical properties of a low alloyed niobium alloy

    International Nuclear Information System (INIS)

    Borisenko, V.A.; Krashchenko, V.P.; Statsenko, V.E.; Kharchenko, V.K.

    1979-01-01

    The technique for indirect temperature measurements of wire samples is suggested and justified. Temperature dependences are investigated of strength and plasticity characteristics of niobium alloy alloyed with zirconium in the range of 20-1100 deg C at two deformation rates: 1.1x10 -3 and 5.3x10 -3 sec -1 . Deformation aging at both deformation rates in the temperature range of 0.25-0.42 Tsub(m) takes place in the form of the increase of σsub(B) and σsub(0.2) strength characteristics and discontinuous yield. The σsub(B) and σsub(0.2) level in this interval is higher for a lesser deformation rate, than for a higher one. Maxima on temperature strength dependence curves move to the side of high temperatures. In the 20-900 deg C temperature range rate alterations slightly affect plasticity characteristics

  6. Microstructure and mechanical behavior of ODS and non-ODS Fe–14Cr model alloys produced by spark plasma sintering

    International Nuclear Information System (INIS)

    Auger, M.A.; Castro, V. de; Leguey, T.; Muñoz, A.; Pareja, R.

    2013-01-01

    In this work the spark plasma sintering (SPS) technique has been explored as an alternative consolidation route for producing ultra-fine grained Fe–14Cr model alloys containing a dispersion of oxide nanoparticles. Elemental powders of Fe and Cr, and nanosized Y 2 O 3 powder have been mechanically alloyed in a planetary ball mill and rapidly sintered in a spark plasma furnace. Two alloys, with nominal compositions Fe–14%Cr and Fe–14%Cr–0.3%Y 2 O 3 (wt.%), have been fabricated and their microstructure and mechanical properties investigated. The results have been compared with those obtained for other powder metallurgy processed alloys of the same composition but consolidated by hot isostatic pressing. The SPS technique under the present conditions has produced Fe–14Cr materials that apparently exhibit different microstructures yielding inferior mechanical properties than the counterpart material consolidated by hot isostatic pressing. Although the presence of a dispersion of Y-rich particles is evident, the oxide dispersion strengthened (ODS) Fe–14Cr alloy consolidated by SPS exhibits poor tensile properties. The extensive decoration of the powder particle surfaces with Cr-rich precipitates and the residual porosity appear to be responsible for the impaired properties of this ODS alloy consolidated by SPS

  7. Microstructure and mechanical behavior of ODS and non-ODS Fe–14Cr model alloys produced by spark plasma sintering

    Energy Technology Data Exchange (ETDEWEB)

    Auger, M.A.; Castro, V. de [Departamento de Física, Universidad Carlos III de Madrid, 28911 Leganés (Spain); Leguey, T., E-mail: leguey@fis.uc3m.es [Departamento de Física, Universidad Carlos III de Madrid, 28911 Leganés (Spain); Muñoz, A.; Pareja, R. [Departamento de Física, Universidad Carlos III de Madrid, 28911 Leganés (Spain)

    2013-05-15

    In this work the spark plasma sintering (SPS) technique has been explored as an alternative consolidation route for producing ultra-fine grained Fe–14Cr model alloys containing a dispersion of oxide nanoparticles. Elemental powders of Fe and Cr, and nanosized Y{sub 2}O{sub 3} powder have been mechanically alloyed in a planetary ball mill and rapidly sintered in a spark plasma furnace. Two alloys, with nominal compositions Fe–14%Cr and Fe–14%Cr–0.3%Y{sub 2}O{sub 3} (wt.%), have been fabricated and their microstructure and mechanical properties investigated. The results have been compared with those obtained for other powder metallurgy processed alloys of the same composition but consolidated by hot isostatic pressing. The SPS technique under the present conditions has produced Fe–14Cr materials that apparently exhibit different microstructures yielding inferior mechanical properties than the counterpart material consolidated by hot isostatic pressing. Although the presence of a dispersion of Y-rich particles is evident, the oxide dispersion strengthened (ODS) Fe–14Cr alloy consolidated by SPS exhibits poor tensile properties. The extensive decoration of the powder particle surfaces with Cr-rich precipitates and the residual porosity appear to be responsible for the impaired properties of this ODS alloy consolidated by SPS.

  8. Multimodal Nanoscale Characterization of Transformation and Deformation Mechanisms in Several Nickel Titanium Based Shape Memory Alloys

    Science.gov (United States)

    Casalena, Lee

    The development of viable high-temperature shape memory alloys (HTSMAs) demands a coordinated multimodal characterization effort linking nanoscale crystal structure to macroscale thermomechanical properties. In this work, several high performance NiTi-based shape memory alloys are comprehensively explored with the goal of gaining insight into the complex transformation and deformation mechanisms responsible for their remarkable behavior. Through precise control of alloying and aging parameters, microstructures are optimized to enhance properties such as high-temperature strength and stability. These are crucial requirements for the development of advanced applications such as actuators and adaptive components that operate in demanding automotive and aerospace environments. An array of NiTiHf and NiTiAu alloys are at the core of this effort, offering the possibility of increased capability over traditional pneumatic and hydraulic systems, while simultaneously reducing weight and energy requirements. NiTi-20Hf alloys exhibit a favorable balance of properties, including high strength, stability, and work output at temperatures in excess of 150 °C. The raw material cost of Hf is also much lower compared with Pt, Pd, and Au containing counterparts. Advanced scanning transmission electron microscopy (STEM) and synchrotron X-ray characterization techniques are used to explore unusual nanoscale effects of precipitate-matrix interactions, coherency strain, and dislocation activity in these alloys. Novel use of the 4D STEM strain mapping technique is used to quantify strain fields associated with precipitates, which are being coupled with new phase field modeling approaches to particle/defect interactions. Volume fractions of nanoscale precipitates are measured using STEM-based tomography techniques, atom probe tomography, and synchrotron diffraction of bulk samples. Plastic deformation of the HTSMA austenite phase is shown to occur through B2 type slip for the first time

  9. An XRD technique for quantitative phase analysis of Al-U-Zr alloy

    International Nuclear Information System (INIS)

    Khan, K.B.; Kulkarni, N.K.; Jain, G.C.

    2003-01-01

    In several nuclear research reactors all over the world, Al-U alloy is used as fuel. To stabilise less brittle phase UAl 3 in Al-U alloy, a small amount of Zr (1 to 3 wt% ) is added. A rapid, non destructive and simple x-ray diffraction technique has been developed for quantitative phase analysis Al-U-Zr alloy system containing UAl 4 , UAl 3 and Al. (author)

  10. Development of various welding techniques for refractory and reactive metals and alloys

    International Nuclear Information System (INIS)

    Tonpe, Sunil; Saibaba, N.

    2016-01-01

    Nuclear Fuel Complex (NFC), Hyderabad, India with its excellent manufacturing facilities, produces nuclear fuel and structural components for nuclear reactors. NFC has taken up the challenging job of production of various critical components made out of refractory and reactive metals and alloys for nuclear and aerospace applications as an indigenization import substitute program. Refractory metals are prime candidates for many high temperature aerospace components because of refractory metal's high melting points and inherent creep resistance. The use of refractory metals is often limited because of their poor room temperature properties, inadequate oxidation resistance at elevated temperatures, difficulties associated with joining or welding etc. These advanced materials demand stringent requirement with respect to chemistry, dimensional tolerances, mechanical and metallurgical properties. This paper discusses in detail various welding techniques adopted in NFC for refractory and reactive metals and alloys such as Nb, Zr, Ti, Ta, Zircaloy, Titanium-half alloy etc. to manufacture various components and assemblies required for nuclear and aerospace applications

  11. Al2O3 Coatings on Magnesium Alloy Deposited by the Fluidized Bed (FB Technique

    Directory of Open Access Journals (Sweden)

    Gabriele Baiocco

    2018-01-01

    Full Text Available Magnesium alloys are widely employed in several industrial domains for their outstanding properties. They have a high strength-weight ratio, with a density that is lower than aluminum (33% less, and feature good thermal properties, dimensional stability, and damping characteristics. However, they are vulnerable to oxidation and erosion-corrosion phenomena when applied in harsh service conditions. To avoid the degradation of magnesium, several coating methods have been presented in the literature; however, all of them deal with drawbacks that limit their application in an industrial environment, such as environmental pollution, toxicity of the coating materials, and high cost of the necessary machinery. In this work, a plating of Al2O3 film on a magnesium alloy realized by the fluidized bed (FB technique and using alumina powder is proposed. The film growth obtained through this cold deposition process is analyzed, investigating the morphology as well as tribological and mechanical features and corrosion behavior of the plated samples. The resulting Al2O3 coatings show consistent improvement of the tribological and anti-corrosive performance of the magnesium alloy.

  12. Al₂O₃ Coatings on Magnesium Alloy Deposited by the Fluidized Bed (FB) Technique.

    Science.gov (United States)

    Baiocco, Gabriele; Rubino, Gianluca; Tagliaferri, Vincenzo; Ucciardello, Nadia

    2018-01-09

    Magnesium alloys are widely employed in several industrial domains for their outstanding properties. They have a high strength-weight ratio, with a density that is lower than aluminum (33% less), and feature good thermal properties, dimensional stability, and damping characteristics. However, they are vulnerable to oxidation and erosion-corrosion phenomena when applied in harsh service conditions. To avoid the degradation of magnesium, several coating methods have been presented in the literature; however, all of them deal with drawbacks that limit their application in an industrial environment, such as environmental pollution, toxicity of the coating materials, and high cost of the necessary machinery. In this work, a plating of Al₂O₃ film on a magnesium alloy realized by the fluidized bed (FB) technique and using alumina powder is proposed. The film growth obtained through this cold deposition process is analyzed, investigating the morphology as well as tribological and mechanical features and corrosion behavior of the plated samples. The resulting Al₂O₃ coatings show consistent improvement of the tribological and anti-corrosive performance of the magnesium alloy.

  13. Effect of heat treatment on Fe-B-Si-Nb alloy powder prepared by mechanical alloying

    Directory of Open Access Journals (Sweden)

    Rodrigo Estevam Coelho

    2005-06-01

    Full Text Available The effect of heat treatment on crystallization behavior of Fe73.5B15Si10Nb1.5 alloy powder prepared by mechanical alloying was studied. The powder samples were prepared by mechanical alloying (MA and for different milling times (1, 5, 25, 70 and 100 hours. Crystalline powders of iron, boron, silicon and niobium were sealed with tungsten carbide balls in a cylindrical vial under nitrogen atmosphere. The ball-to-powder weight ratio was 20 to 1. A Fritsch Pulverizette 5 planetary ball mill was used for MA the powders at room temperature and at 250 rpm. To study the microstructural evolution, a small amount of powder was collected after different milling times and examined by X-ray diffraction, using CuKalpha radiation (lambda = 0.15418 nm. The crystallization behavior was studied by differential thermal analysis, from 25 up to 1000 °C at a heating rate of 25 °C min-1.

  14. Mechanical behaviour of Zn–Al–Cu–Mg alloys: Deformation mechanisms of as-cast microstructures

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Zhicheng; Sandlöbes, Stefanie; Wu, Liang; Hu, Weiping; Gottstein, Günter; Korte-Kerzel, Sandra, E-mail: Korte-Kerzel@imm.rwth-aachen.de

    2016-01-10

    We study the effects of dilute Mg addition on the microstructure formation and mechanical properties of a ZnAl4Cu1 alloy. On the basis of the composition of the commercial alloy Z410 (4 wt% Al, 1 wt% Cu, and 0.04 wt% Mg), three laboratory alloys with different Mg contents (0.04 wt%, 0.21 wt% and 0.31 wt%) are characterised in terms of their mechanical properties and microstructures using ex-situ and in-situ tensile tests in conjunction with scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD). Increasing Mg content causes the precipitation of Mg{sub 2}Zn{sub 11} phase precipitates and refined lamellar spacings in the eutectoid phase. The alloy with a medium Mg content (0.21 wt%) exhibits the highest yield strength both at room temperature and at elevated temperatures. Further, we show that dilute Mg alloying causes an improvement of the ductility of ZnAl4Cu1 base-alloys, especially at elevated temperatures. In addition, the alloys reveal two distinct deformation regimes distinguishable close to room temperature and at commonly employed strain rates, with work hardening and brittle fracture exhibited at room temperature and/or elevated strain rate (5×10{sup −4} s{sup −1}), and work softening and ductile fracture at elevated temperature and/or low strain rate (6×10{sup −6} s{sup −1}). The deformation mechanisms and fracture behaviour in both regimes are investigated and the underlying physical mechanisms of the observed phenomena are discussed.

  15. Mechanical behaviour of Zn–Al–Cu–Mg alloys: Deformation mechanisms of as-cast microstructures

    International Nuclear Information System (INIS)

    Wu, Zhicheng; Sandlöbes, Stefanie; Wu, Liang; Hu, Weiping; Gottstein, Günter; Korte-Kerzel, Sandra

    2016-01-01

    We study the effects of dilute Mg addition on the microstructure formation and mechanical properties of a ZnAl4Cu1 alloy. On the basis of the composition of the commercial alloy Z410 (4 wt% Al, 1 wt% Cu, and 0.04 wt% Mg), three laboratory alloys with different Mg contents (0.04 wt%, 0.21 wt% and 0.31 wt%) are characterised in terms of their mechanical properties and microstructures using ex-situ and in-situ tensile tests in conjunction with scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD). Increasing Mg content causes the precipitation of Mg_2Zn_1_1 phase precipitates and refined lamellar spacings in the eutectoid phase. The alloy with a medium Mg content (0.21 wt%) exhibits the highest yield strength both at room temperature and at elevated temperatures. Further, we show that dilute Mg alloying causes an improvement of the ductility of ZnAl4Cu1 base-alloys, especially at elevated temperatures. In addition, the alloys reveal two distinct deformation regimes distinguishable close to room temperature and at commonly employed strain rates, with work hardening and brittle fracture exhibited at room temperature and/or elevated strain rate (5×10"−"4 s"−"1), and work softening and ductile fracture at elevated temperature and/or low strain rate (6×10"−"6 s"−"1). The deformation mechanisms and fracture behaviour in both regimes are investigated and the underlying physical mechanisms of the observed phenomena are discussed.

  16. Structure and mechanical properties of Al-Si-Fe alloys prepared by short-term mechanical alloying and Spark Plasma Sintering

    Czech Academy of Sciences Publication Activity Database

    Průša, J.; Vojtěch, D.; Bláhová, M.; Michalcová, A.; Kubatík, Tomáš František; Čížek, J.

    2015-01-01

    Roč. 75, June (2015), s. 65-75 ISSN 0261-3069 Institutional support: RVO:61389021 Keywords : Aluminium alloy s * Mechanical Properties * Microstructure * Mechanical alloy ing * Spark-Plasma Sintering Subject RIV: JG - Metallurgy Impact factor: 3.997, year: 2015 http://www.sciencedirect.com/science/article/pii/S0261306915000990#

  17. Effect Of Milling Time On Microstructure Of AA6061 Composites Fabricated Via Mechanical Alloying

    Directory of Open Access Journals (Sweden)

    Tomiczek B.

    2015-06-01

    Full Text Available The aim of this work is to determine the effect of manufacturing conditions, especially milling time, on the microstructure and crystallite size of a newly developed nanostructural composite material with the aluminium alloy matrix reinforced with halloysite nanotubes. Halloysite, being a clayey mineral of volcanic origin, is characterized by high porosity and large specific surface area. Thus it can be used as an alternative reinforcement in metal matrix composite materials. In order to obtain this goal, composite powders with fine microstructures were fabricated using high-energy mechanical alloying, cold compacting and hot extrusion techniques. The obtained composite powders of aluminium alloy reinforced with 5, 10 and 15 wt% of halloysite nanotubes were characterized with SEM, TEM and XRD analysis. It has been proven that the use of mechanical alloying leads to a high degree of deformation, which, coupled with a decreased grain size below 100 nm and the dispersion of the refined reinforcing particles–reinforces the material very well.

  18. Influence of Sc on microstructure and mechanical properties of Al-Si-Mg-Cu-Zr alloy

    Science.gov (United States)

    Li, Yukun; Du, Xiaodong; Zhang, Ya; Zhang, Zhen; Fu, Junwei; Zhou, Shi'ang; Wu, Yucheng

    2018-02-01

    In the present study, the effects of Mg, Cu, Sc and Zr combined additions on the microstructure and mechanical properties of hypoeutectic Al-Si cast alloy were systematically investigated. Characterization techniques such as optical microscopy (OM), scanning electron microscope (SEM), energy dispersive spectrometer (EDS), electron back-scatter diffraction (EBSD), atomic force microscopy (AFM), transmission electron microscope (TEM), Brinell hardness tester and universal testing machine were employed to analyze the microstructure and mechanical properties. The results showed that Sc served as modifier on the microstructure of Al-3Si-0.45Mg-0.45Cu-0.2Zr alloys, including modification of eutectic Si and grains. Extraordinarily, grain refinement was found to be related to the primary particles, which exhibited a close orientation to matrix. After T6 heat treatment, the grain structures were composed of nano-scaled secondary Al3(Sc, Zr) precipitates and spherical eutectic Si. Combined with T6 heat treatment, the highest hardness, yield strength, ultimate tensile strength and elongation were achieved in 0.56 wt.% Sc-modified alloy. Interestingly, the strength and ductility had a similar tendency. This paper demonstrated that combined additions of Mg, Cu, Sc and Zr could significantly improve the microstructure and performance of the hypoeutectic Al-Si cast alloy.

  19. Optimisation of the mechanical alloying process for odsferritic steels for generation IV reactors application

    International Nuclear Information System (INIS)

    Stanciulescu, M.; Carlan, P.; Mihalache, M.; Abrudeanu, M.

    2016-01-01

    ODS ferritic steels appear as promising materials for fusion and Gen IV fission reactors, offering high temperature performance, corrosion and irradiation resistance and meeting low activation criteria. Mechanical alloying (MA) is a powder metallurgy technique efficient for fabricating advanced materials, and has been used for strengthening structural materials including Fe-Cr alloys. In this paper a high-energy ball mill is used to study the microstructural evolution of 14YW alloy during the mechanical alloying process. The elemental powders are milled at a rotation speed of 250rot/min in cycles of 10min milling and 5min pause, with a ball-to-powder ration of 10:1 and in argon protective atmosphere. After 72 hours milling, the morphology and element distribution of the MA powders is investigated by scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) analysis, respectively. It is observed that the particles size increases in the first milling stages and then decreases with the milling time. Changes in the material composition are analysed by X-ray diffraction (DRX). It seems that after milling part of the W remains non-dissolved in the Fe-Cr matrix retarding the solid solution formation. (authors)

  20. Microstructure and mechanical properties of ARB processed Mg-3%Gd alloy

    DEFF Research Database (Denmark)

    Wu, J.Q.; Huang, S.; Wang, Y.H.

    2015-01-01

    by accumulative roll-bonding (ARB) at 400℃ to 4 cycles followed by annealing at various temperatures. The microstructures after annealing were characterized by the electron backscatter diffraction technique and the mechanical properties were measured by a tensile test. It was found that the alloy has a good...... combination of strength and ductility after 2 cycle ARB processing followed by annealing at 290℃ for 1h. The strength is 2.3 times higher than that of the fully annealed coarse grained alloy, and the elongation is comparable with that of fully annealed coarse grained counterpart. The good mechanical...... properties were related to the fine-sized heterogeneous microstructures and weakened texture....

  1. Development of a high specific stiffness mechanically milled FeAl intermetallic alloy

    Energy Technology Data Exchange (ETDEWEB)

    Baccino, R; San Filippo, D; Martel, P; Moret, F

    1996-12-31

    Powder metallurgy techniques such as gas atomization and mechanical milling have been used to develop a FeAl alloy with enhanced ductility and strength at both low and high temperature. The improvement method combines ductility increase by grain boundary strengthening, grain size reduction and oxide dispersion strengthening. The material has been characterized and tested in the form of extruded bars. Microstructure, order and texture of as-extruded and heat treated samples have been studied by TEM, X-ray diffraction and Moessbauer spectroscopy. Physical and mechanical properties of the material are compared to some conventional engineering alloys in order to discuss the conceivable applications in aeronautical and automotive industries. (authors). 22 refs., 4 figs., 2 tabs.

  2. Giant magnetoresistive properties of FexAu100-x alloys produced by mechanical alloying

    International Nuclear Information System (INIS)

    Socolovsky, L.M.; Sanchez, F.H.; Shingu, P.H.

    2001-01-01

    The Fe x Au 100- x alloys were produced for the first time by mechanical alloying. Resistance of samples with iron concentrations of x=15, 20, 25, and 30 at% were measured at 77 K under an applied field of 14 kOe. A maximum in magnetoresistive ratio (Δρ/ρ) of 3.5% was obtained for Fe 25 Au 75 . Samples were annealed in order to enhance magnetoresistive properties. These samples exhibit larger ratios, primarily due to the elimination of defects. X-ray diffraction Moessbauer spectroscopy and magnetoresistance measurements were performed, in order to correlate bulk and hyperfine magnetic properties with crystalline structure. X-ray diffractograms show an FCC structure, with no evidence for a BCC one

  3. Fabrication of spherical high-nitrogen stainless steel powder alloys by mechanical alloying and thermal plasma spheroidization

    Science.gov (United States)

    Razumov, Nikolay G.; Wang, Qing Sheng; Popovich, Anatoly A.; Shamshurin, Aleksey I.

    2018-04-01

    This paper describes the results of experimental studies on the treatment of Fe-23Cr-11Mn-1N high-nitrogen stainless steel powder alloys, synthesized by the mechanical alloying (MA) of elemental powders in the flow of a radio frequency thermal plasma. The as-milled powder with irregular particles were successfully converted into spherical high-nitrogen stainless steel powder alloy. Measurement of the residual nitrogen content in the obtained powder, shown that during the plasma spheroidization process, part of the nitrogen escapes from the alloy.

  4. Cr-Ni ALLOY ELECTRODEPOSITION AND COMPARISON WITH CONVENTIONAL PURE Cr COATING TECHNIQUE

    Directory of Open Access Journals (Sweden)

    M. Moniruzzaman

    2012-12-01

    Full Text Available Cr coating is widely used as the outer surface of precision parts due to its attractive appearance and superior corrosion resistance properties. It is obtained by electrodeposition via a conventional bath with hexavalent Cr ions. This manufacturing technique has many drawbacks, such as very low efficiency and high operating temperature and it is hazardous to health. In this work, we studied a Cr-Ni alloy deposition technique and compared the alloy coating properties to those with conventional Cr coating. Sequential two-step alloy electrodeposition was also compared. We took varying concentrations of Cr, Ni and complexing agents for the electrodeposition of Cr-Ni alloy and sequential Cr-Ni alloy coating on mild steel. Operating parameters, i.e. current density and temperature, were varied to examine their effects on the coating properties. The coatings thus obtained were characterized by visual observation, corrosion test, microhardness measurement, morphology and chemical analysis. The Cr-Ni alloy coating was found to be more corrosion resistant in 5% NaCl solution and harder than the pure Cr coating obtained by conventional electrodeposition. Toxic gas was produced in a much lower extent in the alloy coating than the conventional Cr coating technique. Again, the two-step Cr-Ni alloy coating was found better in terms of corrosion resistance as well as hardness compared to the Cr-Ni alloy coating. The process was also found to be much more environmentally friendly.

  5. Elemental analysis of brazing alloy samples by neutron activation technique

    International Nuclear Information System (INIS)

    Eissa, E.A.; Rofail, N.B.; Hassan, A.M.; El-Shershaby, A.; Walley El-Dine, N.

    1996-01-01

    Two brazing alloy samples (C P 2 and C P 3 ) have been investigated by Neutron activation analysis (NAA) technique in order to identify and estimate their constituent elements. The pneumatic irradiation rabbit system (PIRS), installed at the first egyptian research reactor (ETRR-1) was used for short-time irradiation (30 s) with a thermal neutron flux of 1.6 x 10 1 1 n/cm 2 /s in the reactor reflector, where the thermal to epithermal neutron flux ratio is 106. Long-time irradiation (48 hours) was performed at reactor core periphery with thermal neutron flux of 3.34 x 10 1 2 n/cm 2 /s, and thermal to epithermal neutron flux ratio of 79. Activation by epithermal neutrons was taken into account for the (1/v) and resonance neutron absorption in both methods. A hyper pure germanium detection system was used for gamma-ray acquisitions. The concentration values of Al, Cr, Fe, Co, Cu, Zn, Se, Ag and Sb were estimated as percentages of the sample weight and compared with reported values. 1 tab

  6. Elemental analysis of brazing alloy samples by neutron activation technique

    Energy Technology Data Exchange (ETDEWEB)

    Eissa, E A; Rofail, N B; Hassan, A M [Reactor and Neutron physics Department, Nuclear Research Centre, Atomic Energy Authority, Cairo (Egypt); El-Shershaby, A; Walley El-Dine, N [Physics Department, Faculty of Girls, Ain Shams Universty, Cairo (Egypt)

    1997-12-31

    Two brazing alloy samples (C P{sup 2} and C P{sup 3}) have been investigated by Neutron activation analysis (NAA) technique in order to identify and estimate their constituent elements. The pneumatic irradiation rabbit system (PIRS), installed at the first egyptian research reactor (ETRR-1) was used for short-time irradiation (30 s) with a thermal neutron flux of 1.6 x 10{sup 1}1 n/cm{sup 2}/s in the reactor reflector, where the thermal to epithermal neutron flux ratio is 106. Long-time irradiation (48 hours) was performed at reactor core periphery with thermal neutron flux of 3.34 x 10{sup 1}2 n/cm{sup 2}/s, and thermal to epithermal neutron flux ratio of 79. Activation by epithermal neutrons was taken into account for the (1/v) and resonance neutron absorption in both methods. A hyper pure germanium detection system was used for gamma-ray acquisitions. The concentration values of Al, Cr, Fe, Co, Cu, Zn, Se, Ag and Sb were estimated as percentages of the sample weight and compared with reported values. 1 tab.

  7. Phase transformations during sintering of mechanically alloyed TiPt

    CSIR Research Space (South Africa)

    Nxumalo, S

    2010-10-01

    Full Text Available Page 307 SMA alloys have been successfully used in several applications including medical, automotive and aerospace as stents, couplings and actuators. The most successful shape memory alloys currently are the NiTi alloys. These are however...

  8. Effects of hot rolling and titanium content on the microstructure and mechanical properties of high boron Fe–B alloys

    International Nuclear Information System (INIS)

    He, Lin; Liu, Ying; Li, Jun; Li, Binghong

    2012-01-01

    Highlights: ► The content of B is 1.8 wt.% in the high boron Fe–B alloys. ► Hot-rolling improves the mechanical properties, especially the elongation. ► The Ti content affects the microstructure and mechanical properties. ► Eutectic boride can be eliminated when the atomic ratio of Ti/B is no less than 0.5. ► Alloy exhibits balanced mechanical properties when the atomic ratio of Ti/B is 0.5. -- Abstract: High boron Fe–B alloys (1.8 wt.% B) with different titanium contents are fabricated by Vacuum Induction Melting (VIM) technique. The integrated mechanical properties of the as-cast alloys are poor, especially the ductility. In this investigation, hot-rolling technology is used to improve the microstructure and mechanical properties. The microstructure analysis shows that hot rolling can reduce the size and improve the distribution of the reinforcements. The mechanical properties testing indicates that the yield strength is unchanged basically, but the tensile strength and elongation are improved greatly by hot rolling, especially the elongation. The content of titanium also has great effects on the microstructures and mechanical properties of the hot-rolled alloys. For the hot-rolled alloys, with the titanium content increasing, the ultimate tensile strength and yield strength first decrease slightly and then increase. The elongation and impact toughness are improved significantly. In particular, when the atomic ratio of Ti to B is 0.5, the reinforcements are almost entirely TiB 2 and uniformly distributed in the Fe-matrix. The ternary Fe–B–Ti alloy exhibits balanced mechanical properties: yield strength, ultimate tensile strength, elongation and impact toughness are 334 MPa, 602 MPa, 16.2% and 213 kJ/m 2 , respectively.

  9. Microstructure and mechanical properties of lost foam cast 356 alloys

    Directory of Open Access Journals (Sweden)

    Qi-gui Wang

    2015-05-01

    Full Text Available Microstructure and mechanical properties of lost foam cast aluminum alloys have been investigated in both primary A356 (0.13% Fe and secondary 356 (0.47%. As expected, secondary 356 shows much higher content of Fe-rich intermetallic phases, and in particular the porosity in comparison with primary A356. The average area percent and size (length of Fe-rich intermetallics change from about 0.5% and 6 祄 in A356 to 2% and 25 祄 in 356 alloy. The average area percent and maximum size of porosity also increase from about 0.4% and 420 祄 to 1.4% and 600 祄, respectively. As a result, tensile ductility decreases about 60% and ultimate tensile strength declines about 8%. Lower fatigue strength was also experienced in the secondary 356 alloy. Low cycle fatigue (LCF strength decreased from 187 MPa in A356 to 159 MPa in 356 and high cycle fatigue (HCF strength also declined slightly from 68 MPa to 64 MPa.

  10. Solid state amorphisation in binary systems prepared by mechanical alloying

    International Nuclear Information System (INIS)

    Gonzalez, G.; Sagarzazu, A.; Bonyuet, D.; D'Angelo, L.; Villalba, R.

    2009-01-01

    In the present work a detailed study of amorphisation in different systems prepared by mechanical alloying under the same experimental conditions was carried out, milling up to 50 and 100 h in some cases. The systems studied were: AlTi, AlNi, AlFe, FeNi, FeCo, NiMo, NiW, NiCo, MoW, CoMo. These systems were chosen to study the effect of Al-transition metal, transition metal-transition metal and also systems with large and small negative heat of mixing, different and similar crystal structures, atomic sizes and diffusion coefficients. Calculations based on the Miedema model for alloy formation and amorphisation on all the alloys studied were performed. The experimental results from X-ray diffraction and transmission electron microscopy showed that the systems based on Fe (FeNi, FeCo and FeAl) did not amorphised, even after milling for 100 h, and formed a stable solid solution with a nanometric grain size of 7 nm. The systems NiMo, NiW, MoW and CoMo (systems with small negative heat of mixing), showed amorphisation after 50 h of milling. NiAl and TiAl form an intermediate amorphous phase after around 20 h of milling and with further milling they recrystallize into a fcc solid solution. Agreement between the theoretical calculations based on the Miedema model and the experimental results was found in most of the systems.

  11. Rotary bending fatigue properties of Inconel 718 alloys by ultrasonic nanocrystal surface modification technique

    Directory of Open Access Journals (Sweden)

    Jun-Hyong Kim

    2015-08-01

    Full Text Available This study investigates the influence of ultrasonic nanocrystal surface modification (UNSM technique on fatigue properties of SAE AMS 5662 (solution treatment of Inconel 718 alloys. The fatigue properties of the specimens were investigated using a rotary bending fatigue tester. Results revealed that the UNSM-treated specimens showed longer fatigue life in comparison with those of the untreated specimens. The improvement in fatigue life of the UNSM-treated specimens is attributed mainly to the induced compressive residual stress, increased hardness, reduced roughness and refined grains at the top surface. Fractured surfaces were analysed using a scanning electron microscopy (SEM in order to give insight into the effectiveness of UNSM technique on fracture mechanisms and fatigue life.

  12. Effect of processing of mechanical alloying and powder metallurgy on microstructure and properties of Cu-Al-Ni-Mn alloy

    International Nuclear Information System (INIS)

    Xiao Zhu; Li Zhou; Fang Mei; Xiong Shiyun; Sheng Xiaofei; Zhou Mengqi

    2008-01-01

    The fabrication conditions of Cu-Al-Ni-Mn alloy powder by mechanical alloying and powder metallurgy have been systematically studied. The mechanically alloyed powder (MAed powder) was fabricated at a speed between 100 rpm and 300 rpm for various milling times with and without process control agent (PCA). With an increasing of milling time, the size of crystallite grain decreases. Only the Cu diffraction pattern appear as the rotation speed is up to 300 rpm for 25 h. The elemental powders with PCA agglomerate slightly, but the degree of alloying is lower than that without PCA. The shape memory recovery of the quenched sample hot-extruded at extrusion rate of 50:1 is measured to be 100% recovered in 250 deg. C oil bath for 40 s after deformed to 4.0%. After aging at 120 deg. C for 10 days, the shape memory recovery of the alloy remains 98%

  13. Microstructure and magnetic behavior of Cu–Co–Si ternary alloy synthesized by mechanical alloying and isothermal annealing

    Energy Technology Data Exchange (ETDEWEB)

    Chabri, Sumit, E-mail: sumitchabri2006@gmail.com [Department of Metallurgy & Materials Engineering, Indian Institute of Engineering Science and Technology, Shibpur, Howrah 711103 (India); Bera, S. [Department of Metallurgical & Materials Engineering, National Institute of Technology, Durgapur 713209 (India); Mondal, B.N. [Department of Central Scientific Services, Indian Association for the Cultivation of Science, Jadavpur, Kolkata 700032 (India); Basumallick, A.; Chattopadhyay, P.P. [Department of Metallurgy & Materials Engineering, Indian Institute of Engineering Science and Technology, Shibpur, Howrah 711103 (India)

    2017-03-15

    Microstructure and magnetic behavior of nanocrystalline 50Cu–40Co–10Si (at%) alloy prepared by mechanical alloying and subsequent isothermal annealing in the temperature range of 450–650 °C have been studied. Phase evolution during mechanical alloying and isothermal annealing is characterized by X-ray diffraction (XRD), differential thermal analyzer (DTA), high resolution transmission electron microscopy (HRTEM) and magnetic measurement. Addition of Si has been found to facilitate the metastable alloying of Co in Cu resulting into the formation of single phase solid solution having average grain size of 9 nm after ball milling for 50 h duration. Annealing of the ball milled alloy improves the magnetic properties significantly and best combination of magnetic properties has been obtained after annealing at 550 °C for 1 h duration.

  14. REGULARITIES AND MECHANISM OF FORMATION OF STRUCTURE OF THE MECHANICALLY ALLOYED COMPOSITIONS GROUND ON THE BASIS OF METAL SYSTEMS

    Directory of Open Access Journals (Sweden)

    F. G. Lovshenko

    2014-01-01

    Full Text Available Experimentally determined regularities and mechanism of formation of structure of the mechanically alloyed compositions foundations on the basis of the widely applied in mechanical engineering metals – iron, nickel, aluminum, copper are given. 

  15. The effect of processing techniques on microstructural and tribological properties of copper-based alloys

    International Nuclear Information System (INIS)

    Vencl, Aleksandar; Rajkovic, Viseslava; Zivic, Fatima; Mitrović, Slobodan; Cvijović-Alagić, Ivana; Jovanovic, Milan T.

    2013-01-01

    Three copper-based alloys, i.e. two composites reinforced with Al 2 O 3 particles and fabricated through PM route and Cu–Cr–Zr alloy processed by the vacuum melting and casting technique were the object of this investigation. Light microscope, scanning electron microscope (SEM) equipped with electron X-ray spectrometer (EDS) and transmission electron microscope (TEM) were used for microstructural characterization. The ball-on-disc nanotribometer served for wear and friction tests applying low sliding speeds (6, 8 and 10 mm/s) at constant load (1 N). The objective of the paper was to investigate the effect of different processing techniques on microstructure, thermal stability and the tribological characteristics of composites and copper ingot alloy. Nano-sized Al 2 O 3 particles (less than 100 nm in size) are present not only in the copper matrix of Cu–2.5 wt.% Al composite, obtained by internal oxidation, but they are also formed at the grain boundaries preventing the grain growth and providing very small grain size. During the high temperature annealing (in the range 300–950 o C) composites behaved much better than the ingot alloy. The highest thermal stability showed Cu–2.5 wt.% Al composite. The pinning effect of nano-sized Al 2 O 3 particles prevents the grain growth slowing down recrystallization of this composite up to 900 o C. Micro-sized Al 2 O 3 particles in Cu–5 wt.% Al 2 O 3 composite, processed by mechanical annealing, are not effective in preventing dislocation motion and the grain growth, whereas microstructure of Cu–0.4 wt.% Cr–0.08 wt.% Zr ingot alloy was completely recrystallized around 550 o C. Cu–2.5 wt.% Al composite showed the best wear resistance, approximately 2.5 times higher than that of Cu–5 wt.% Al 2 O 3 composite. High hardness and nano-sized Al 2 O 3 particles size combined with the fine-grain structure are the main parameters leading to the improved wear resistance of the Cu–2.5Al composite.

  16. Formation of nano sized ODS clusters in mechanically alloyed NiAl-(Y,Ti,O) alloys

    International Nuclear Information System (INIS)

    Kim, Yong Deog; Bae Seong Man; Wirth, Brian D.

    2012-01-01

    The Reactor Pressure Vessel (RPV) is the key component in determining the lifetime of nuclear power plants because it is subject to the significant aging degradation by irradiation and thermal aging, and there is no practical method for replacing that component. Advanced reactors with much larger capacity than current reactor require the usage of higher strength materials inevitably. The SA508 Gr.4N Ni-Cr-Mo low alloy steel, in which Ni and Cr contents are larger than in conventional RPV steels, could be a promising RPV material offering improved strength and toughness from its tempered martensitic microstructure. For a structural integrity of RPV, the effect of neutron irradiation on the material property is one of the key issues. The RPV materials suffer from the significant degradation of transition properties by the irradiation embrittlement when its strength is increased by a hardening mechanism. Therefore, the potential for application of SA508 Gr.4N steel as the structural components for nuclear power reactors depends on its ability to maintain adequate transition properties against the operating neutron does. However, it is not easy to fine the data on the irradiation effect on the mechanical properties of SA508 Gr.4N steel. In this study, the irradiation embrittlement of SA508 Gr.4N Ni-Cr-Mo low alloy steel was evaluated by using specimens irradiated in research reactor. For comparison, the variations of mechanical properties by neutron irradiation for commercial SA508 Gr.3 Mn-Mo-Ni low alloy steel were also evaluated

  17. Amorphization of Fe-Nb by mechanical alloying

    International Nuclear Information System (INIS)

    Yang, J.Y.; Zhang, T.J.; Cui, K.; Li, X.G.; Zhang, J.

    1996-01-01

    Elemental powder mixtures of Fe x Nb 1-x were mechanically alloyed in a planetary ball mill. Powders milled for different times were characterized by X-ray diffraction, transmission and scanning electron microscopy, differential thermal analysis and microhardness measurement. The results show that powders with 0.30≤x≤0.70 could be amorphized after 30 h milling; the maximum hardness (Hv) of milled Fe 50 Nb 50 powders attained was 1490. Based on a thermodynamical analysis, the glass forming range of the Fe-Nb system was calculated, and found to agree with the experimental result very well. (orig.)

  18. Selective Laser Melting Technique of Co-Cr Dental Alloys: A Review of Structure and Properties and Comparative Analysis with Other Available Techniques.

    Science.gov (United States)

    Koutsoukis, Theodoros; Zinelis, Spiros; Eliades, George; Al-Wazzan, Khalid; Rifaiy, Mohammed Al; Al Jabbari, Youssef S

    2015-06-01

    The aim of this study was to review the effect of selective laser melting (SLM) procedure on the properties of dental structures made of Co-Cr alloys and to evaluate its quality and compare it to those produced by conventional casting and milling fabrication techniques. A computerized database search using PubMed and Scopus was conducted for peer-reviewed scientific research studies regarding the use of SLM in Co-Cr dental alloys with no restrictions for publication years. The search engines provided hundreds of results, and only 48 scientific research papers, case studies, or literature reviews were considered relevant for this review. The innovative manufacturing concept of SLM offers many advantages compared with casting and milling fabrication techniques. SLM provides different microstructure from casting and milling with minimal internal porosity and internal fitting, marginal adaptation, and comparable bond strength to porcelain. Mechanical and electrochemical properties of SLM structures are enhanced compared to cast, while clinical longevity of single-metal ceramic crowns is comparable to Au-Pt dental alloy. The SLM technique provides dental prosthetic restorations more quickly and less expensively without compromising their quality compared with restorations prepared by casting and milling techniques. The current SLM devices provide metallic restorations made of Co-Cr alloys for removable and fixed partial dentures without compromising the alloy or restoration properties at a fraction of the time and cost, showing great potential to replace the aforementioned fabrication techniques in the long term; however, further clinical studies are essential to increase the acceptance of this technology by the worldwide dental community. © 2015 by the American College of Prosthodontists.

  19. Weldability and joining techniques for advanced fossil energy system alloys

    Energy Technology Data Exchange (ETDEWEB)

    Lundin, C.D.; Qiao, C.Y.P.; Liu, W.; Yang, D.; Zhou, G.; Morrison, M. [Univ. of Tennessee, Knoxville, TN (United States)

    1998-05-01

    The efforts represent the concerns for the basic understanding of the weldability and fabricability of the advanced high temperature alloys so necessary to affect increases in the efficiency of the next generation Fossil Energy Power Plants. The effort was divided into three tasks with the first effort dealing with the welding and fabrication behavior of 310HCbN (HR3C), the second task details the studies aimed at understanding the weldability of a newly developed 310TaN high temperature stainless (a modification of 310 stainless) and Task 3 addressed the cladding of austenitic tubing with Iron-Aluminide using the GTAW process. Task 1 consisted of microstructural studies on 310HCbN and the development of a Tube Weldability test which has applications to production welding techniques as well as laboratory weldability assessments. In addition, the evaluation of ex-service 310HCbN which showed fireside erosion and cracking at the attachment weld locations was conducted. Task 2 addressed the behavior of the newly developed 310 TaN modification of standard 310 stainless steel and showed that the weldability was excellent and that the sensitization potential was minimal for normal welding and fabrication conditions. The microstructural evolution during elevated temperature testing was characterized and the second phase particles evolved upon aging were identified. Task 3 details the investigation undertaken to clad 310HCbN tubing with Iron Aluminide and developed welding conditions necessary to provide a crack free cladding. The work showed that both a preheat and a post-heat was necessary for crack free deposits and the effect of a third element on the cracking potential was defined together with the effect of the aluminum level for optimum weldability.

  20. Crystalline-to-amorphous phase transformation in mechanically alloyed Fe50W50 powders

    International Nuclear Information System (INIS)

    Sherif El-Eskandarany, M.S.; Sumiyama, K.; Suzuki, K.

    1997-01-01

    A mechanical alloying process via a ball milling technique has been applied for preparing amorphous Fe 50 W 50 alloy powders. The results have shown that during the first and second stages of milling (0 to 360 ks) W atoms emigrate to Fe lattices to form nanocrystalline b.c.c. Fe-W solid solution, with a grain size of about 7 nm in diameter. After 720 ks of the milling time, this solid solution was transformed to an amorphous Fe-W alloy coexisting with the residual fraction of the unprocessed W powders. During the last stage of milling (720 to 1,440 ks) all of this residual W powder reacts with the amorphous phase to form a homogeneous Fe 50 W 50 amorphous alloy. The crystallization temperature and the enthalpy change of crystallization of amorphous Fe 50 W 50 powders milled for 1,440 ks were measured to be 860 K and -9kJ/mol, respectively. The amorphous Fe 50 W 50 powder produced is almost paramagnetic at room temperature. The powder comprises homogeneous and smooth spheres with an average size of about 0.5 microm in diameter

  1. Mechanical behavior of novel W alloys produced by HIP

    International Nuclear Information System (INIS)

    Pastor, J.Y.; Martin, A.; Llorca, J.; Monge, M.A.; Pareja, R.

    2007-01-01

    Full text of publication follows: W appears to be one of the candidate materials being considered for making plasma-facing components (PFCs) in a future fusion power reactor because of its refractory characteristics, low tritium retention and low sputtering yielding. However, its use in PFCs requires the development of W materials that, in addition to these properties, maintains good mechanical properties at high temperatures. In W, high temperature strength and creep resistance may be effectively increased by solid-solution and dispersion strengthening. Sintering could be a suitable method to produce solid-solution and dispersion strengthening in W alloys for these applications if their recrystallization temperature is high enough and the grain growth is restrained. The aim of the present work is to investigate the mechanical properties of W materials produced by liquid phase sintering using Ti as sintering activator and nanoparticles of Y 2 O 3 as strengthening dispersoids. The mechanical behaviour of pure W and W alloys, having 0.5 wt % Y 2 O 3 , X Wt % Ti and 0.5 wt % Y 2 O 3 + X wt % Ti prepared by powder metallurgy have been studied (0≤X≤4). Three point bending tests have been performed on 2 x 2 x 25 mm 3 specimens cut from ingots consolidated by a two-stage hot isostatic pressing process. The bending strength, fracture toughness and elastic modulus have been determined as a function of temperature. The fracture surfaces have been analyzed to find the fracture mode and investigate the temperature dependence of the mechanical properties and fracture mechanisms. The effect of the Y 2 O 3 dispersion and Ti content on the mechanical properties is also investigated. (authors)

  2. Mechanical behavior of novel W alloys produced by HIP

    Energy Technology Data Exchange (ETDEWEB)

    Pastor, J.Y.; Martin, A.; Llorca, J. [Madrid Univ. Politecnica, Dept de Ciencia de Materiales (Spain); Monge, M.A.; Pareja, R. [Madrid Univ. Carlos 3, Dept. de Fisica (Spain)

    2007-07-01

    Full text of publication follows: W appears to be one of the candidate materials being considered for making plasma-facing components (PFCs) in a future fusion power reactor because of its refractory characteristics, low tritium retention and low sputtering yielding. However, its use in PFCs requires the development of W materials that, in addition to these properties, maintains good mechanical properties at high temperatures. In W, high temperature strength and creep resistance may be effectively increased by solid-solution and dispersion strengthening. Sintering could be a suitable method to produce solid-solution and dispersion strengthening in W alloys for these applications if their recrystallization temperature is high enough and the grain growth is restrained. The aim of the present work is to investigate the mechanical properties of W materials produced by liquid phase sintering using Ti as sintering activator and nanoparticles of Y{sub 2}O{sub 3} as strengthening dispersoids. The mechanical behaviour of pure W and W alloys, having 0.5 wt % Y{sub 2}O{sub 3}, X Wt % Ti and 0.5 wt % Y{sub 2}O{sub 3} + X wt % Ti prepared by powder metallurgy have been studied (0{<=}X{<=}4). Three point bending tests have been performed on 2 x 2 x 25 mm{sup 3} specimens cut from ingots consolidated by a two-stage hot isostatic pressing process. The bending strength, fracture toughness and elastic modulus have been determined as a function of temperature. The fracture surfaces have been analyzed to find the fracture mode and investigate the temperature dependence of the mechanical properties and fracture mechanisms. The effect of the Y{sub 2}O{sub 3} dispersion and Ti content on the mechanical properties is also investigated. (authors)

  3. Cryogenic mechanical properties of Al-Cu-Li-Zr alloy 2090

    International Nuclear Information System (INIS)

    Glazer, J.; Dalder, E.N.C.; Emigh, R.A.; Verzasconi, S.L.; Yu, W.

    1986-01-01

    The mechanical properties of aluminum-lithium alloy 2090-T8E41 were evaluated at 298 K, 77 K, and 4 K. Previously reported tensile and fracture toughness properties at room temperature were confirmed. This alloy exhibits substantially improved properties at cryogenic temperatures; the strength, elongation, fracture toughness and fatigue crack growth resistance all improve simultaneously as the testing temperature decreases. This alloy has cryogenic properties superior to those of aluminum alloys currently used for cryogenic applications

  4. Rapid analysis of molybdenum contents in molybdenum master alloys by X-ray fluorescence technique

    International Nuclear Information System (INIS)

    Tongkong, P.

    1985-01-01

    Determination of molybdenum contents in molybdenum master alloy had been performed using energy dispersive x-ray fluorescence (EDX) technique where analysis were made via standard additions and calibration curves. Comparison of EDX technique with other analyzing techniques, i.e., wavelength dispersive x-ray fluorescence, neutron activation analysis and inductive coupled plasma spectrometry, showed consistency in the results. This technique was found to yield reliable results when molybdenum contents in master alloys were in the range of 13 to 50 percent using HPGe detector or proportional counter. When the required error was set at 1%, the minimum analyzing time was found to be 30 and 60 seconds for Fe-Mo master alloys with molybdenum content of 13.54 and 49.09 percent respectively. For Al-Mo master alloys, the minimum times required were 120 and 300 seconds with molybdenum content of 15.22 and 47.26 percent respectively

  5. On the phase evolution of AlCoCrCuFeMnSix high entropy alloys prepared by mechanical alloying and arc melting route

    Science.gov (United States)

    Kumar, Anil; Chopkar, Manoj

    2018-05-01

    Effect of Si addition on phase formation of AlCoCrCuFeMnSix (x=0, 0.3, 0.6 and 0.9) high entropy alloy have been investigated in this work. The alloys are prepared by mechanical alloying and vacuum arc melting technique. The X-ray diffraction results reveals the formation of mixture of face centered and body centered cubic solid solution phases in milled powders. The addition of Si favours body centered cubic structure formation during milling process. Whereas, after melting the milled powders, body centered phases formed during milling is partial transformed into sigma phases. XRD results were also correlated with the SEM elemental mapping of as casted samples. Addition of Si favours σ phase formation in the as cast samples.

  6. Mechanical properties and thermal stability of Al–Fe–Ni alloys prepared by centrifugal atomisation and hot extrusion

    International Nuclear Information System (INIS)

    Průša, F.; Vojtěch, D.; Michalcová, A.; Marek, I.

    2014-01-01

    In this work, Al–12Fe and Al–7Fe–5Ni (wt%) alloys prepared by a novel technique including centrifugal atomisation and hot extrusion were studied. The microstructures were investigated using light microscopy, electron scanning microscopy, transmission electron microscopy and X-ray diffraction. The mechanical properties were determined by Vickers hardness measurements and compressive stress–strain tests. To study the thermal stability, the mechanical properties were also measured after 100 h of annealing at 300 °C and 400 °C. In addition, creep tests at a stress of 120 MPa and a temperature of 300 °C were performed. The investigated materials were composed of fine-grained α-Al and intermetallic phases identified as Al 13 Fe 4 and Al 9 FeNi. The Vickers hardness and compressive yield strength were 68 HV5 and 183 MPa, respectively, for the Al–12Fe alloy and 73 HV5 and 226 MPa, respectively, for the Al–7Fe–5Ni alloy. After long-term annealing, the change in the mechanical properties was negligible, indicating the excellent thermal stability of both materials. The creep tests confirmed the highest thermal stability of the Al–7Fe–5Ni alloy with a total compressive creep strain of 15%. The “thermally stable” casting Al–12Si–1Cu–1Mg–1Ni alloy treated by the T6 regime was used as a reference material. The casting alloy exhibited sufficient mechanical properties (hardness and compressive yield strength) at room temperature. However, annealing remarkably softened and reduced its compressive yield strength to almost 50% of the initial values. Additionally, the total creep strain of the casting reference material was almost three times higher than that of the Al–7Fe–5Ni alloy. It has been proven that centrifugally atomised materials quickly compacted via hot extrusion can compete or even exceed the properties of common casting aluminium alloys that are used in automotive industry

  7. Influence of scandium on the microstructure and mechanical properties of A319 alloy

    International Nuclear Information System (INIS)

    Emadi, Daryoush; Rao, A.K. Prasada; Mahfoud, Musbah

    2010-01-01

    Recycling of aluminum scrap alloys by melting is gaining its importance in foundry sector. During recycling, some of the alloying elements present in scrap alloys eventually become trace/tramp impurities in the recycled alloy. These elements could potentially affect the alloy's microstructure and hence its mechanical properties. In the present work, an attempt has been made to investigate the effect of one of such trace elements on the microstructure and mechanical properties of A319 alloy. The element chosen for the present investigation is scandium (Sc). This paper discusses the effects of the additions of trace amount of Sc on the microstructure and mechanical properties of A319 alloy in as-cast, T6 and T7 heat treated conditions.

  8. Effects of La2O3 Content and Rolling on Microstructure and Mechanical Properties of ODS Molybdenum Alloys

    Science.gov (United States)

    Ma, Jingling; Li, Wuhui; Wang, Guangxin; Li, Yaqiong; Guo, Hongbo; Zhao, Zeliang; Li, Wei

    2017-10-01

    In order to study the effects of La2O3 content and rolling on microstructure and mechanical properties of Mo-La2O3 alloys, Mo-0.5% (1%) La2O3 alloys were prepared by liquid-solid doping technique, subsequently rolled either by a single-direction rolling or a cross-rolling. As a result, three different materials were prepared for this study. After being annealed at 1800 °C, the single-directionally rolled Mo-1% La2O3 alloy shows the best mechanical properties in terms of strength, hardness, and sagging deformation among the three materials. This is attributed to the observation that the alloy is only recovered with a microstructure of subgrains and dislocations. The single-directionally rolled Mo-0.5% La2O3 exhibits the worst mechanical property among the three materials. In this material, coarse grains, but no subgrains and dislocations, can be observed after annealing, indicating that it is fully recrystallized. For the cross-rolled Mo-1% La2O3 alloy, grains of dispersed sizes, but no dislocations, are visible after annealing, implying that this alloy is partially recrystallized. Accordingly, the mechanical property of this material is in between the other two materials. Thus, the mechanical properties of the three materials can be well understood based on OM, SEM, and TEM results. Overall, the single-directionally rolled Mo-1% La2O3 alloy possesses good mechanical properties and is more suitable for high-temperature applications.

  9. TIG and MIG welding of 6061 and 7020 aluminium alloys. Microstructural studies and mechanical properties

    International Nuclear Information System (INIS)

    Gomez de Salazar, J.M.; Urena, A.; Villauriz, E.; Manzanedo, S.; Barrena, I.

    1998-01-01

    The aluminium alloys of the 6XXX and 7XXX series, are actually considered of medium and high strength, and are been profusely used in different industries such as aeronautical, automotive, etc.However, its wide application as structural material needs of the proper development of their joining process. The present work describes the results obtained from the microstructural evaluation, both with optical and scanning electronic micros copies (OM) and SEM), and of the mechanical one (hardness changes) of the weld produced in the alloys using different arc welding techniques: FTAW (TIG) and GMAW (MIG). For the last one, a filler metal with a composition of Al-5Mg, AWS denomination A5.10-92 (AA5356), has been used. (Author) 5 refs

  10. Fractographic Observations on the Mechanism of Fatigue Crack Growth in Aluminium Alloys

    Science.gov (United States)

    Alderliesten, R. C.; Schijve, J.; Krkoska, M.

    Special load histories are adopted to obtain information about the behavior of the moving crack tip during the increasing and decreasing part of a load cycle. It is associated with the crack opening and closure of the crack tip. Secondly, modern SEM techniques are applied for observations on the morphology of the fractures surfaces of a fatigue crack. Information about the cross section profiles of striations are obtained. Corresponding locations of the upper and the lower fracture surface are also explored in view of the crack extension mechanism. Most experiments are carried out on sheet specimens of aluminum alloys 2024-T3, but 7050-T7451 specimens are also tested in view of a different ductility of the two alloys.

  11. Modeling of mechanical properties for ferrous shape memory alloy

    International Nuclear Information System (INIS)

    Wada, Manabu; Ide, Yusuke; Mizote, Shinichiro; Naoi, Hisashi; Tsukimori, Kazuyuki

    2002-08-01

    In order to acquire technical data that are necessary for manufacture and design of the simulation test device for analyzing the core mechanics of Fast Breeder Reactor, ferrous shape memory alloy of Fe-28%Mn-6%Si-5%Cr is melted, forged and heat-treated. The microstructures are austenite. The specimens are deformed of up to 16% work-strain by tensile and compressive test, resulting in appearance of epsilon-martensite that is induced by stress. Then, heating at 673K for 10 minutes causes austenitic transformation from epsilon-martensite and shape memory strains are measured. We also investigate shape memory character of specimens, which are given, so called 'training treatment' of 5% pre-strain and recovery heat treatment. As a result, there is little difference between tensile and compressive test without training treatment and shape memory strain is 2% after being given 5% work-strain and recovery heat treatment. On the other hand, training treatment is remarkable and shape memory strain reaches to 3.7% after 5% work-strain. We analyze shape recovery character of this alloy specimen at three-point bending by using finite element method, and indicate possibility that its deformation behavior can be estimated from mechanical properties' data obtained at tensile and compressive test. (author)

  12. Mechanically alloyed PrFeB nanocrystalline magnets

    International Nuclear Information System (INIS)

    Kaszuwara, W.; Leonowicz, M.

    1998-01-01

    Mechanically alloyed PrFeB nanocrystalline magnets were prepared by extensive ball milling of Pr, Fe and Fe 80 B 20 powders, followed by diffusion annealing. After milling, the material consisted of nanocrystalline α-Fe crystallites embedded in amorphous Pr-rich matrix. Thermomagnetic and calorimetric investigations of the transformations which occurred during annealing showed that the amorphous phase crystallised at 240 C, leading to the formation of crystalline Pr having lattice constants 10% greater than those shown in the ASTM data. This fact indicated that mechanical alloying and low temperature annealing led to the formation of a solid solution of either Fe or B in Pr, which does not exist in the equilibrium state. The Pr 2 Fe 14 B phase was subsequently formed within a temperature range of 420-620 C. The magnetic properties of magnets depend on the phase structure and grain size. Milling time appears to be a decisive processing parameter for the tailoring of the magnetic properties. Depending on the phase structure, the coercivities varied from 100 to 1200 kA/m and, respectively, the remanences from 0.98 T to 0.6 T. The highest maximum energy product was 80 kJ/m 3 . (orig.)

  13. The Analysis of the General Performance and Mechanical Behavior of Unirradiated FeCrAl Alloys Before and After Welding

    Energy Technology Data Exchange (ETDEWEB)

    Gussev, Maxim N. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Field, Kevin G. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Yamamoto, Yukinori [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2016-06-03

    The present report summarizes and discusses the preliminary results for the in-depth characterization of the modern, nuclear-grade FeCrAl alloys currently under development. The alloys were designed for enhanced radiation tolerance and weldability, and the research is currently being pursued by the Department of Energy (DOE) Nuclear Energy Enabling Technologies (NEET) program. Last year, seven candidate FeCrAl alloys with well-controlled chemistry and microstructures were designed and produced; welding was performed under well-controlled conditions. The structure and general performance of unirradiated alloys were assessed using standardized and advanced microstructural characterization techniques and mechanical testing. The primary objective is to identify the best candidate alloy, or at a minimum to identify the contributing factors that increase the weldability and radiation tolerance of FeCrAl alloys, therefore enabling future generations of FeCrAl alloys to deliver better performance parameters. This report is structured so as to describe these critical assessments of the weldability; radiation tolerance will be reported on in later reports from this program.

  14. Mössbauer and XRD study of the Fe65Si35 alloy obtained by mechanical alloying

    International Nuclear Information System (INIS)

    Vélez, G. Y.; Rodríguez, R. R.; Melo, C. A.; Pérez Alcázar, G. A.; Zamora, Ligia E.; Tabares, J. A.

    2011-01-01

    A study was made on the alloy Fe 65 Si 35 using x-ray diffraction and Mössbauer spectrometry. The alloy was obtained by mechanical alloying in a high energy planetary mill, with milling times of 15, 30, 50, 75 and 100 h. The results show that in the alloys two structural phases are present, a Fe-Si BCC disordered phase and ferromagnetic, and a Fe-Si SC phase, whose nature is paramagnetic and which decreases with milling time. In the temporal evolution of the milling two stages are differentiated: one between 15 and 75 h of milling, in which silicon atoms diffuse into the bcc matrix of iron and its effect is to reduce the hyperfine magnetic field; the other, after 75 h of milling, where the alloy is consolidated, the effect of the milling is only to increase the disorder of the system, increasing the magnetic order.

  15. Microstructural Evolution and Mechanical Property Development of Selective Laser Melted Copper Alloys

    Science.gov (United States)

    Ventura, Anthony Patrick

    Selective Laser Melting (SLM) is an additive manufacturing technology that utilizes a high-power laser to melt metal powder and form a part layer-by-layer. Over the last 25 years, the technology has progressed from prototyping polymer parts to full scale production of metal component. SLM offers several advantages over traditional manufacturing techniques; however, the current alloy systems that are researched and utilized for SLM do not address applications requiring high electrical and thermal conductivity. This work presents a characterization of the microstructural evolution and mechanical property development of two copper alloys fabricated via SLM and post-process heat treated to address this gap in knowledge. Tensile testing, conductivity measurement, and detailed microstructural characterization was carried out on samples in the as-printed and heat treated conditions. A single phase solid solution strengthened binary alloy, Cu-4.3Sn, was the first alloy studied. Components were selectively laser melted from pre-alloyed Cu-4.3Sn powder and heat treated at 873 K (600 °C) and 1173 K (900 °C) for 1 hour. As-printed samples were around 97 percent dense with a yield strength of 274 MPa, an electrical conductivity of 24.1 %IACS, and an elongation of 5.6%. Heat treatment resulted in lower yield strength with significant increases in ductility due to recrystallization and a decrease in dislocation density. Tensile sample geometry and surface finish also showed a significant effect on measured yield strength but a negligible change in measured ductility. Microstructural characterization indicated that grains primarily grow epitaxially with a sub-micron cellular solidification sub-structure. Nanometer scale tin dioxide particles identified via XRD were found throughout the structure in the tin-rich intercellular regions. The second alloy studied was a high-performance precipitation hardening Cu-Ni-Si alloy, C70250. Pre-alloyed powder was selectively laser melted to

  16. Multi-spectroscopic techniques to evaluate the toxicity of alloyed CdSeS quantum dots

    International Nuclear Information System (INIS)

    Zhan Hongju; Zhou Peijiang; Ding Ling; He Zhenyu; Ma Rong

    2012-01-01

    Alloyed CdSeS quantum dots (QDs) were successfully synthesized in aqueous phase using microwave irradiation. UV–vis spectroscopy, fluorescence spectroscopy, transmission electron microscopy (TEM) and X-ray diffraction (XRD) techniques proved that the prepared alloyed QDs are composed of a CdSe-rich core and thick CdS shell with homogeneous size distributions. In order to study its biological toxicity, multi-spectroscopic techniques were adopted to investigate their conjugation with BSA. Fluorescence quenching methods indicated the prepared CdSeS QDs strongly quenched the fluorescence of BSA due to the formation of non-fluorescence ground-state complex. UV–vis absorbance spectra, synchronous fluorescence spectra and CD spectra further confirmed the alloyed CdSeS QDs binded with BSA and destroyed their hydrogen bonding networks, which induced the conformation changes of this macromolecule. - Highlights: ► Synthesis of alloyed CdSeS QDs in aqueous phase via microwave irradiation. ► Characterization of alloyed QDs by PL, UV–vis, XRD and TEM techniques. ► Evidence of static quenching between alloyed QDs and BSA. ► Evidence of the conformation change of BSA molecules induced by alloyed QDs.

  17. Influence of niobium addition on the high temperature mechanical properties of a centrifugally cast HP alloy

    International Nuclear Information System (INIS)

    Andrade, A.R.; Bolfarini, C.; Ferreira, L.A.M.; Vilar, A.A.A.; Souza Filho, C.D.; Bonazzi, L.H.C.

    2015-01-01

    The influence of niobium addition on the mechanical properties at high temperature of HP alloy has been investigated. Two HP alloys were centrifugally cast with a similar chemical composition differing only in the niobium content. Low strain rate high temperature tensile tests and creep-rupture tests were performed in the range of 900–1100 °C, and the results compared between the alloys. According to the results, the high temperature mechanical behavior of both alloys is controlled by several factors like solid solution, network of eutectic carbides, intradendritic precipitation and dendrite spacing. A significant increase in the mechanical properties for the HP alloy with niobium addition was found within the temperature range of 900–1050 °C. Beyond this temperature the mechanical behavior of both alloys is basically the same

  18. Microstructure features and mechanical properties of a UFG Al-Mg-Si alloy produced via SPD

    International Nuclear Information System (INIS)

    Bobruk, E; Kazykhanov, V; Valiev, R; Murashkin, M; Sabirov, I

    2014-01-01

    The effect of equal channel angular pressing in parallel channels (ECAP-PC) and subsequient artificial ageing on the microstructure and room temperature mechanical properties of the commercial aluminum alloys 6063 (Al-0.6Mg-0.5Si, wt.%) and 6010 (Al-0.8Mg-1.0Si-0.15Cu-0.25Mn, wt.%) was investigated. It was shown that mechanical strength of the ECAP-PC processed Al alloys is higher compared to that achieved in these alloys after conventional thermo-mechanical processing. Prior ECAP- PC solution treatment and post-ECAP-PC artificial aging can additionally increase the mechanical strength of both Al alloys. Under optimal artificial ageing conditions, the yield strength (YS) of 299 MPa and ultimate tensile strength (UTS) of 308 MPa was achieved in the 6063 alloy, whereas YS of 423 MPa and UTS of 436 MPa was achieved in the 6010 alloy

  19. Experimental approach and micro-mechanical modeling of the mechanical behavior of irradiated zirconium alloys

    International Nuclear Information System (INIS)

    Onimus, F.

    2003-12-01

    Zirconium alloys cladding tubes containing nuclear fuel of the Pressurized Water Reactors constitute the first safety barrier against the dissemination of radioactive elements. Thus, it is essential to predict the mechanical behavior of the material in-reactor conditions. This study aims, on the one hand, to identify and characterize the mechanisms of the plastic deformation of irradiated zirconium alloys and, on the other hand, to propose a micro-mechanical modeling based on these mechanisms. The experimental analysis shows that, for the irradiated material, the plastic deformation occurs by dislocation channeling. For transverse tensile test and internal pressure test this channeling occurs in the basal planes. However, for axial tensile test, the study revealed that the plastic deformation also occurs by channeling but in the prismatic and pyramidal planes. In addition, the study of the macroscopic mechanical behavior, compared to the deformation mechanisms observed by TEM, suggested that the internal stress is higher in the case of irradiated material than in the case of non-irradiated material, because of the very heterogeneous character of the plastic deformation. This analysis led to a coherent interpretation of the mechanical behavior of irradiated materials, in terms of deformation mechanisms. The mechanical behavior of irradiated materials was finally modeled by applying homogenization methods for heterogeneous materials. This model is able to reproduce adequately the mechanical behavior of the irradiated material, in agreement with the TEM observations. (author)

  20. Microstructural and mechanical properties analysis of extruded Sn–0.7Cu solder alloy

    Directory of Open Access Journals (Sweden)

    Abdoul-Aziz Bogno

    2015-01-01

    Full Text Available The properties and performance of lead-free solder alloys such as fluidity and wettability are defined by the alloy composition and solidification microstructure. Rapid solidification of metallic alloys is known to result in refined microstructures with reduced microsegregation and improved mechanical properties of the final products as compared to normal castings. The rapidly solidified Sn-based solders by melt spinning were shown to be suitable for soldering with low temperature and short soldering duration. In the present study, rapidly solidified Sn–0.7 wt.%Cu droplets generated by impulse atomization (IA were achieved as well as directional solidification under transient conditions at lower cooling rate. This paper reports on a comparative study of the rapidly solidified and the directionally solidified samples. Different but complementary characterization techniques were used to fully analyze the solidification microstructures of the samples obtained under the two cooling regimes. These include X-ray diffractometry (XRD and scanning electron microscopy (SEM. In order to compare the tensile strength and elongation to fracture of the directionally solidified ingot and strip castings with the atomized droplet, compaction and extrusion of the latter were carried out. It was shown that more balanced and superior tensile mechanical properties are available for the hot extruded samples from compacted as-atomized Sn–0.7 wt.%Cu droplets. Further, elongation-to-fracture was 2–3× higher than that obtained for the directionally solidified samples.

  1. Microstructural and magnetic behavior of nanostructured soft alloys prepared by mechanical grinding and gas atomization

    International Nuclear Information System (INIS)

    Marin, P.; Lopez, M.; Garcia-Escorial, A.; Lieblich, M.

    2007-01-01

    Nanocrystalline powder of Fe-Si-B-Cu-Nb has been obtained by means of mechanical milling of the corresponding nanocrystalline ribbons. Gas atomization technique has been used to minimize the magnetic hardening due to stress effects observed in ball-milled samples. Fe-Si-B-Cu-Nb and Fe-Si nanocrystalline samples have been prepared by gas atomization. The aim of our work is to analyse the particle size dependence of coercivity in this nanostructured alloys and to show the analogies and differences between ball-milled and gas atomized samples

  2. Effect of hydrogen charging on the mechanical properties of medium strength aluminium alloys 2091 and 2014

    DEFF Research Database (Denmark)

    Bandopadhyay, A.; Ambat, Rajan; Dwarakadasa, E.S.

    1992-01-01

    Cathodic hydrogen charging in 3.5% NaCl solution altered the mechanical properties of 2091-T351 (Al-Cu-Li-Mg-Zr) determined by a slow (10(-3)/s) strain rate tensile testing technique. UTS and YS decreased in the caw of 2091-T351 and 2014-T6(Al-Cu-Mn-Si-Mg) with increase in charging current density....... Elongation showed a decrease with increase in charging current density for both the alloys. However, elongation occurring throughout the gauge length in uncharged specimens changed over to localized deformation, thus increasing the reduction in area in charged specimens. A transition in fracture mode from...

  3. Structure and mechanical properties of TiZr binary alloy after Al addition

    International Nuclear Information System (INIS)

    Jiang, X.J.; Jing, R.; Liu, C.Y.; Ma, M.Z.; Liu, R.P.

    2013-01-01

    Microstructure and mechanical properties of hot-rolled TiZrAl alloys were studied. The results showed that the microstructure of all alloys mainly consisted of lamellar α phase. The thickness of the lamellar α phase gradually increased with increasing aluminum content. Moreover, large numbers of stacking faults was observed in Ti–25Zr–15Al (at%) alloy. The aluminum addition strongly affected the mechanical properties of the TiZrAl alloys. With increased aluminum contents, the strength increased evidently, whereas, the elongation decreased. Ti–25Zr–15Al (at%) with the highest aluminum contents in all alloys, possessed the highest tensile strength (σ b =1319 MPa), i.e. strengthened by 41% compared with Ti–25Zr (at%) alloy, and still retained the elongation of 5.5%. According to the classical size and/or modulus misfits model, the effect of aluminum addition was significant in TiZr alloys because of the considerable misfits between aluminum and zirconium

  4. INFLUENCE OF MECHANICAL ALLOYING AND LEAD CONTENT ON MICROSTRUCTURE, HARDNESS AND TRIBOLOGICAL BEHAVIOR OF 6061 ALUMINIUM ALLOYS

    Directory of Open Access Journals (Sweden)

    M. Paidpilli

    2017-03-01

    Full Text Available In the present work, one batch of prealloyed 6061Al powder was processed by mixing and another one was ball milled with varying amount of lead content (0-15 vol. %. These powders were compacted at 300MPa and sintered at 590˚C under N2. The instrumented hardness and the young’s modulus of as-sintered 6061Al-Pb alloys were examined as a function of lead content and processing route. The wear test under dry sliding condition has been performed at varying loads (10-40 N using pin-on-disc tribometer. The microstructure and worn surfaces have been investigated using SEM to evaluate the change in topographical features due to mechanical alloying and lead content. The mechanically alloyed materials showed improved wear characteristics as compared to as-mixed counterpart alloys. Delamination of 6061Al-Pb alloys decreases up to an optimum lead composition in both as-mixed and ball-milled 6061Al-Pb alloys. The results indicated minimum wear rate for as-mixed and ball-milled 6061Al alloy at 5 and 10 vol. % Pb, respectively.

  5. Preparation of a high strength Al–Cu–Mg alloy by mechanical alloying and press-forming

    International Nuclear Information System (INIS)

    Tang Huaguo; Cheng Zhiqiang; Liu Jianwei; Ma Xianfeng

    2012-01-01

    Highlights: ► A high strength aluminum alloy of Al–2 wt.%Mg–2 wt.%Cu has been prepared by mechanical alloying and press-forming. ► The alloy only consists of solid solution α-Al. ► The grains size of α-Al was about 300 nm–5 μm. ► The solid solution strengthening and the grain refinement strengthening are the main reasons for such a high strength. - Abstract: A high strength aluminum alloy, with the ratio of 96 wt.%Al–2 wt.%Mg–2 wt.%Cu, has been prepared by mechanical alloying and press-forming. The alloy exhibited a high tensile strength of 780 MPa and a high microhardness of 180 HV. X-ray diffraction characterizations confirmed that the alloy only consists of a solid solution α-Al. Microstructure characterizations revealed that the grain size of α-Al was about 300 nm–5 μm. The solid solution strengthening and the grain refinement strengthening were considered to be the reason for such a high strength.

  6. Preparation of a high strength Al-Cu-Mg alloy by mechanical alloying and press-forming

    Energy Technology Data Exchange (ETDEWEB)

    Tang Huaguo [State Key Laboratory of Rare Earth Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China); Cheng Zhiqiang [College of Resources and Environment, Jilin Agricultural University, Changchun 130118 (China); Liu Jianwei [State Key Laboratory of Rare Earth Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China); Ma Xianfeng, E-mail: xfma@ciac.jl.cn [State Key Laboratory of Rare Earth Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China)

    2012-07-30

    Highlights: Black-Right-Pointing-Pointer A high strength aluminum alloy of Al-2 wt.%Mg-2 wt.%Cu has been prepared by mechanical alloying and press-forming. Black-Right-Pointing-Pointer The alloy only consists of solid solution {alpha}-Al. Black-Right-Pointing-Pointer The grains size of {alpha}-Al was about 300 nm-5 {mu}m. Black-Right-Pointing-Pointer The solid solution strengthening and the grain refinement strengthening are the main reasons for such a high strength. - Abstract: A high strength aluminum alloy, with the ratio of 96 wt.%Al-2 wt.%Mg-2 wt.%Cu, has been prepared by mechanical alloying and press-forming. The alloy exhibited a high tensile strength of 780 MPa and a high microhardness of 180 HV. X-ray diffraction characterizations confirmed that the alloy only consists of a solid solution {alpha}-Al. Microstructure characterizations revealed that the grain size of {alpha}-Al was about 300 nm-5 {mu}m. The solid solution strengthening and the grain refinement strengthening were considered to be the reason for such a high strength.

  7. Ineffective cough and mechanical mucociliary clearance techniques.

    Science.gov (United States)

    Fernández-Carmona, A; Olivencia-Peña, L; Yuste-Ossorio, M E; Peñas-Maldonado, L

    Cough is a fundamental defense mechanism for keeping the airway free of foreign elements. Life-threatening situations may arise when cough proves ineffective as a result of muscle weakness or altered mucociliary function. When a patient is unable to cough effectively, techniques are required to either reinforce or replace cough capacity. The use of mechanical systems that facilitate or substitute cough function is increasingly common in Intensive Care Units, where it is relatively frequent to find situations of ineffective cough due to different clinical causes. This review examines the current clinical practice recommendations referred to the indication and use of mechanical cough assist and intrapulmonary percussive ventilation systems. Copyright © 2017 Elsevier España, S.L.U. y SEMICYUC. All rights reserved.

  8. Effects of Ce Addition and Isothermal Aging on the Elevated Temperature Tensile Properties of Mechanically Alloyed Al-Ti Alloys

    Energy Technology Data Exchange (ETDEWEB)

    Kim, JunKi; Oh, YoungMin; Kim, YongDeog; Kim, SeonJin [Hanyang Univ., Seoul (Korea, Republic of); Kim, ByungChul [KOREA ATOMIC RESEARCH INSTITUTE, TAEJON (Korea, Republic of)

    1997-05-01

    The room and elevated temperature tensile strength of mechanically alloyed Al-8wt%. Ti alloy increased by substituting Ce for Ti up to 25at.%. However, further substitution of Ce for Ti decreased the tensile strength. It was considered to be due to the decrease of volume fraction of Ce contained dispersoid. In the meantime, the decrease of tensile strength due to the isothermal aging was effectively reduced by the addition of Ce at 400 deg. C but not 510 deg. C. The activation energies for the deformation of Al-80wt.%(Ti+Ce)alloys measured at the temperature between 300 deg. C{approx}510 deg. C were about 1.3{approx}1.9 times higher than that for pure Al self-diffusion(142 kJ/mole). Thus, it was considered that the elevated temperature deformation of Al-8wt.%(Ti+Ce)alloys was governed by Orowan mechanism (author). 9 refs. 6 figs.

  9. Degradation of the Mechanical Properties of Zirconium-base alloys due to Interaction with Hydrogen

    International Nuclear Information System (INIS)

    Bertolino, Graciela

    2001-01-01

    Security aspects and the purpose to extend the nuclear power plants lifetime motivate the renovated interest on the influence of the environment and radiation on the mechanical properties of in-reactor materials.Zirconium based alloys are the family of alloys most extensively used in nuclear core components.A consequence of the interaction of the in-reactor environment with these alloys is the formation of brittle phase Zr hydride, a process that greatly affects the component integrity.In this work we present a experimental study of the hydrogen influence on the Z ry-4 mechanical properties at different temperatures.As a complement we also present results of a finite elements simulations of the fracture process.We performed standard metallurgical and mechanical characterization in commercial Z ry-4 samples to obtain their basic properties. Different hydrogen pickup techniques were applied to obtain H concentration of charged samples between 10 and 2000 ppm, homogeneous or mainly localized at the crack tip zone.To obtain the fracture toughness of the alloys specimens were tested using elastoplastic fracture mechanics techniques.Specifically we implement J-integral methodology with partial unloading compliance measurements.Tests were performed in a temperature range of 20 to 200 o C.The negative influence of the H content on material toughness probed to be important even at very small concentrations, with an effect that decreases when temperature increases.While there was observed no change in the fracture mechanism in homogeneous charged samples, specimens charged under a superimposed stress field fractured by brittle mode when were tested at 20 to 70 o C. SEM observations of the crack growth, the fracture surface morphology and precipitates content showed the influence of the precipitates on fracture at different H concentrations.At least three stages with different fracture behavior depending on H content were identified.Complementary to the experimental work we

  10. Studies on post weld heat treatment of dissimilar aluminum alloys by laser beam welding technique

    Science.gov (United States)

    Srinivas, B.; Krishna, N. Murali; Cheepu, Muralimohan; Sivaprasad, K.; Muthupandi, V.

    2018-03-01

    The present study mainly focuses on post weld heat treatment (PWHT) of AA5083 and AA6061 alloys by joining these using laser beam welding at three different laser power and two different beam spot sizes and three different welding speeds. Effects of these parameters on microstructural and mechanical properties like hardness, tensile strength were studied at PWHT condition and significant changes had been observed. The PWHT used was artificial aging technique. The microstructural observations revealed that there was a appreciable changes were taken place in the grain size. The microhardness observations proven that the change in the hardness profile in AA6061 was appreciable than in the AA5083. The tensile strength of 246 MPa was recorded as highest. The fractured surfaces observed are predominantly ductile in nature.

  11. Influence of boron addition on the grain refinement and mechanical properties of AZ91 Mg alloy

    International Nuclear Information System (INIS)

    Suresh, M.; Srinivasan, A.; Ravi, K.R.; Pillai, U.T.S.; Pai, B.C.

    2009-01-01

    This article reports the effect of boron addition on the grain refinement efficiency and mechanical properties of AZ91 magnesium alloy. The results show that the addition of boron in the form of Al-4B master alloy, significantly refines the grain size of AZ91 alloy. This refinement is due to the presence of AlB 2 particles, which act as potential nucleants for Mg grains. Improved mechanical properties are obtained with the addition of boron due to the finer grains.

  12. The Synthesis of Nanostructured WC-Based Hardmetals Using Mechanical Alloying and Their Direct Consolidation

    Directory of Open Access Journals (Sweden)

    N. Al-Aqeeli

    2014-01-01

    Full Text Available Tungsten carbide- (WC- based hardmetals or cemented carbides represent an important class of materials used in a wide range of industrial applications which primarily include cutting/drilling tools and wear resistant components. The introduction and processing of nanostructured WC-based cemented carbides and their subsequent consolidation to produce dense components have been the subject of several investigations. One of the attractive means of producing this class of materials is by mechanical alloying technique. However, one of the challenging issues in obtaining the right end-product is the possible loss of the nanocrystallite sizes due to the undesirable grain growth during powder sintering step. Many research groups have engaged in multiple projects aiming at exploring the right path of consolidating the nanostructured WC-based powders without substantially loosing the attained nanostructure. The present paper highlights some key issues related to powder synthesis and sintering of WC-based nanostructured materials using mechanical alloying. The path of directly consolidating the powders using nonconventional consolidation techniques will be addressed and some light will be shed on the advantageous use of such techniques. Cobalt-bonded hardmetals will be principally covered in this work along with an additional exposure of the use of other binders in the WC-based hardmetals.

  13. Microstructure and Mechanical Property of Aluminum Alloy Plate AA 7055

    Directory of Open Access Journals (Sweden)

    CHEN Junzhou

    2017-10-01

    Full Text Available Through-thickness microstructure and mechanical property of AA 7055-T7751 aluminum alloy plate were investigated by using electron backscattered diffraction (EBSD, transmission electron microscope (TEM and small angle X-ray scattering(SAXS. The results indicate an inhomogeneous distribution of microstructure through the thickness. The degree of recrystallization decreases gradually from 69% to 19.1%, as deepening from the surface to the center of the plate. The size of subgrains decreases from 10 μm at the surface to around 2 μm at the center. Strong texture of rolling type is observed near the center but the intensity decreases gradually as nearing the surface and the shear texture becomes the dominant. High density of plate-like η' phases are observed in the alloy, indicating the sufficient precipitation. η' precipitates of this condition are around 3.7 nm in radius, 1-3 nm in thickness and are found coherent with the Al matrix with a coherent strain of 0.0133, showing a strong strengthening effect. The heterogeneity in grain scale does not influence the distribution and the morphology of precipitates. The yield strength (L direction varies linearly along the thickness direction of the plate, fitting an equation of σy=-38.7S+604.8 (0≤S≤1. The variation of yield strength is related to the heterogeneity of grain structure.

  14. Corrosion-electrochemical behaviour and mechanical properties ofaluminium alloy-321, alloyed by barium

    International Nuclear Information System (INIS)

    Ganiev, I.; Mukhiddinov, G.N.; Kargapolova, T.V.; Mirsaidov, U.

    1995-01-01

    The purpose of present work is studying of influence of barium additionson electrochemical corrosion of casting aluminium-copper alloy Al-321,containing as base alloying components copper, chromium, manganese, titanium,zirconium, cadmium

  15. Mechanical properties of depleted uranium-2 w/o molybdenum alloy

    International Nuclear Information System (INIS)

    Deel, O.L.; Burian, R.J.

    1979-01-01

    The primary objective of this program is to develop data and techniques for determining the dynamic impact response of radioactive-material shipping-container systems for environmental control and safety overview and assessment. One phase of this program is the dynamic testing of 1/8-, 1/4-, and 1/2-scale models of uranium-shielded truck casks. These linearly scaled models are fabricated from the same materials typically used in full-size prototype casks. In order to analytically evaluate the results of dynamic tests, it is necessary to know the mechanical properties of the materials of construction. Since the properties of cast uranium--molybdenum alloys vary significantly with casting and heat-treating techniques, it is necessary to fully characterize the mechanical properties of the uranium used in the model tests. This report presents the results of these studies. The uranium alloy exhibited a tensile strength equal to or greater than that reported by others. As indicated by the percentage of elongation and reduction in area, the ductility was lower. Comparative data for the other mechanical properties measured were not found in the literature

  16. Experimental Study on Dissimilar Friction Stir welding of Aluminium Alloys (5083-H111 and 6082-T6) to investigate the mechanical properties

    Science.gov (United States)

    Kumar, H. M. Anil; Venkata Ramana, V.; Pawar, Mayur

    2018-03-01

    Friction stir welding is an innovative technology in the joining realm of metals and alloys. This technique is highly economical and suitable especially for non ferrous alloys compared to ferrous alloys. It finds many applications in various fields of aeronautics, automobile, ship building industries etc. The paper presents the comparative results of mechanical properties such as tensile strength, microstructure, macro structure and hardness on the similar and dissimilar aluminum alloys AA5083-H111 and AA6082-T6 under certain selected variables - constant tool rotational speed, its tilt angle, welding speed using friction stir welding process. It is observed from the experimental results that joint efficiency of dissimilar aluminium alloys is higher than the similar aluminum alloys.

  17. Comparative study of the microstructures and mechanical properties of direct laser fabricated and arc-melted Al{sub x}CoCrFeNi high entropy alloys

    Energy Technology Data Exchange (ETDEWEB)

    Joseph, Jithin, E-mail: jithin@deakin.edu.au [Institute for Frontier Materials, Deakin University, Waurn Ponds 3216 (Australia); Jarvis, Tom; Wu, Xinhua [Monash Centre for Additive Manufacturing, Monash University, Clayton 3168 (Australia); Stanford, Nicole; Hodgson, Peter; Fabijanic, Daniel Mark [Institute for Frontier Materials, Deakin University, Waurn Ponds 3216 (Australia)

    2015-05-01

    High entropy alloys (HEA) are a relatively new metal alloy system that have promising potential in high temperature applications. These multi-component alloys are typically produced by arc-melting, requiring several remelts to achieve chemical homogeneity. Direct laser fabrication (DLF) is a rapid prototyping technique, which produces complex components from alloy powder by selectively melting micron-sized powder in successive layers. However, studies of the fabrication of complex alloys from simple elemental powder blends are sparse. In this study, DLF was employed to fabricate bulk samples of three alloys based on the Al{sub x}CoCrFeNi HEA system, where x was 0.3, 0.6 and 0.85 M fraction of Al. This produced FCC, FCC/BCC and BCC crystal structures, respectively. Corresponding alloys were also produced by arc-melting, and all microstructures were characterised and compared longitudinal and transverse to the build/solidification direction by x-ray diffraction, glow discharge optical emission spectroscopy and scanning electron microscopy (EDX and EBSD). Strong similarities were observed between the single phase FCC and BCC alloys produced by both techniques, however the FCC/BCC structures differed significantly. This has been attributed to a difference in the solidification rate and thermal gradient in the melt pool between the two different techniques. Room temperature compression testing showed very similar mechanical behaviour and properties for the two different processing routes. DLF was concluded to be a successful technique to manufacture bulk HEA's.

  18. Structure and Mechanical Properties of Al-Cu-Fe-X Alloys with Excellent Thermal Stability

    Directory of Open Access Journals (Sweden)

    Andrea Školáková

    2017-11-01

    Full Text Available In this work, the structure and mechanical properties of innovative Al-Cu-Fe based alloys were studied. We focused on preparation and characterization of rapidly solidified and hot extruded Al-Cu-Fe, Al-Cu-Fe-Ni and Al-Cu-Fe-Cr alloys. The content of transition metals affects mechanical properties and structure. For this reason, microstructure, phase composition, hardness and thermal stability have been investigated in this study. The results showed exceptional thermal stability of these alloys and very good values of mechanical properties. Alloying by chromium ensured the highest thermal stability, while nickel addition refined the structure of the consolidated alloy. High thermal stability of all tested alloys was described in context with the transformation of the quasicrystalline phases to other types of intermetallics.

  19. Structure and Mechanical Properties of Al-Cu-Fe-X Alloys with Excellent Thermal Stability.

    Science.gov (United States)

    Školáková, Andrea; Novák, Pavel; Mejzlíková, Lucie; Průša, Filip; Salvetr, Pavel; Vojtěch, Dalibor

    2017-11-05

    In this work, the structure and mechanical properties of innovative Al-Cu-Fe based alloys were studied. We focused on preparation and characterization of rapidly solidified and hot extruded Al-Cu-Fe, Al-Cu-Fe-Ni and Al-Cu-Fe-Cr alloys. The content of transition metals affects mechanical properties and structure. For this reason, microstructure, phase composition, hardness and thermal stability have been investigated in this study. The results showed exceptional thermal stability of these alloys and very good values of mechanical properties. Alloying by chromium ensured the highest thermal stability, while nickel addition refined the structure of the consolidated alloy. High thermal stability of all tested alloys was described in context with the transformation of the quasicrystalline phases to other types of intermetallics.

  20. Ageing and memory effects in a mechanically alloyed nanoparticle system

    International Nuclear Information System (INIS)

    Osth, Michael; Herisson, Didier; Nordblad, Per; De Toro, Jose A.; Riveiro, Jose M.

    2007-01-01

    Ageing and memory experiments have been performed to explore the non-equilibrium dynamics of the mechanically alloyed nanoparticle system Fe 30 Ag 40 W 30 , which comprises a heterogeneous ensemble of magnetic particles with average moment ∼ 10 2 μ B dispersed in a metallic non-magnetic matrix. This system has earlier, from critical slowing down analysis, been reported to enter a spin glass like state at low temperatures [J. A. de Toro et al., Phys. Rev. B 69, (2004) 224407]. The wait time dependence of the magnetic relaxation observed after the application of a weak magnetic field and the memory of the thermal history in the low temperature phase recorded on continuous heating in a weak applied field show similar features as observed in corresponding experiments on canonical spin glasses

  1. The microstructure of mechanically alloyed nanocrystalline aluminium-magnesium

    Energy Technology Data Exchange (ETDEWEB)

    Gubicza, J. [Dept. of General Physics, Eoetvoes Univ., Budapest (Hungary); Dept. of Solid State Physics, Eoetvoes Univ., Budapest (Hungary); Kassem, M. [Dept. of Materials Science and Engineering, Faculty of Petroleum and Mining, Suez Canal Univ., Suez (Egypt); Ungar, T. [Dept. of General Physics, Eoetvoes Univ., Budapest (Hungary)

    2004-07-01

    The effect of the nominal Mg content and the milling time on the microstructure of mechanically alloyed Al(Mg) solid solutions is studied. The crystallite size distribution and the dislocation structure are determined by X-ray diffraction peak profile analysis. Magnesium gradually goes into solid solution during ball milling and after 3 h almost all of the Mg atoms are soluted into the Al matrix. With increasing milling time the Mg content in solid solution, the dislocation density as well as the hardness are increasing, whereas the crystallite size is decreasing. A similar tendency of these parameters is observed at a particular duration of ball milling with increasing of the nominal Mg content. At the same time for a long milling period the dislocation density slightly decreases together with a slight reduction of the hardness. (orig.)

  2. Mechanical alloying of TiFe intermetallic for hydrogen storage

    International Nuclear Information System (INIS)

    Vega, L.E.R.; Leiva, D.R.; Silva, W.B.; Ishikawa, T.T.; Botta, W.J.; Leal Neto, R.M.

    2016-01-01

    Elementary powders of Ti and Fe in the stoichiometric ratio 50:50 were submitted to mechanical alloying for 2, 6, 10 and 20 h in a planetary ball mill. The synthesis of TiFe intermetallic with high yield was achieved for all milling times. The structural characterization of the samples revealed the trend of the particles to form agglomerates and the formation of cracks. H-absorption capacities of 0,74; 0,90; 0,97 and 0,95 wt. % (at room temperature and 20 bar of H2) were obtained for processing times of 2, 6, 10 and 20 h, respectively, without using a thermal activation process after milling. (author)

  3. Precipitation structures and mechanical properties of Al-Li-Zr alloy containing V

    International Nuclear Information System (INIS)

    Ying, J.K.; Ohashi, T.

    1999-01-01

    It is known that Al-Li alloys possess high elastic modulus and low density, and the metastable δ' (Al 3 Li) precipitate in these alloys affords considerable strengthening effect. However, with the strengthening resulting from the precipitation of δ' which is coherent with the matrix, these alloys suffer from low ductility and fracture toughness. It seems that the loss of ductility is the slip localization which occurs as a result of slip planes during deformation in connection with the specific hardening mechanism. As a result it indicates typical intergranular fracture. On the one hand, zirconium is used in many aluminum alloys to inhibit recrystallization during alloy processing. When zirconium is present in the alloy grain refinement occurs, which consequently, is considered as a factor that reduces the slip distance, and lowers the stress concentration across grain boundaries and at grain boundary triple points. Nevertheless, if only zirconium is added in Al-Li alloy it still shows intergranular fracture. By Zedaris et al., equilibrium phase Al 3 (Zr,V) in Al-Zr alloy containing V reduces the lattice mismatch along the c-axis with Al and, the L1 2 -structure metastable precipitates Al 3 (Zr,V) in Al-Zr-V alloys are stable at elevated temperature. Therefore, it is interesting to elucidate the effect of V in Al-Li-Zr alloy at the precipitation structures and mechanical properties of these alloys

  4. Corrosion mechanisms of aluminum alloys in waters of low conductivity

    International Nuclear Information System (INIS)

    Haddad, Roberto E; Lanazani, Liliana; Rodriguez, Sebastian

    2006-01-01

    After completing their burn cycle, nuclear fuels in experimental reactors made with aluminum alloys have to remain for long periods in distilled water, in interim storage. While aluminum alloys are resistant to corrosion in pure water, severe deterioration occurs in elements that have been immersed for periods of up to 30 years. Pitting-like surface alterations can even occur in nuclear quality waters (conductivity below 5 μS/cm and dissolved ions content below detection thresholds) in time periods of less than one year. An important factor that could become a potential promoter of this phenomena is the presence of dust particles and others, that could settle on the metallic surface, generating a locally aggressive medium. A simple immersion experiment demonstrates that these points can become initiation sites for pitting with very low concentrations of chlorides (under 10 ppm), especially if the electrochemical potential is increased by contact with another metallic material, even staying below the pitting potential in this medium. There are several corrosion mechanisms acting simultaneously, depending on the nature of the deposits. Pitting under glass particles has been detected, which may be related to a simple crevice corrosion process. In the case of iron oxides, however, the results depend on the type of oxide. Pits more than 100 microns deep have been obtained in 7 day immersion tests, so in spent fuel storage sites these mechanisms could easily cause penetration of the 500 micron aluminum plates during the time covering the interim storage under water, which could be decades, with similar chemical conditions (CW)

  5. Carbonitriding of low alloy steels: Mechanical and metallurgical responses

    Energy Technology Data Exchange (ETDEWEB)

    Dal' Maz Silva, W., E-mail: waltermateriais@me.com [Institut Jean Lamour – UMR CNRS–Université de Lorraine, 7198, Parc de Saurupt, Nancy 54011 (France); Institut de Recherche Technologique M2P, Metz 57070 (France); Dulcy, J., E-mail: jacky.dulcy@univ-lorraine.fr [Institut Jean Lamour – UMR CNRS–Université de Lorraine, 7198, Parc de Saurupt, Nancy 54011 (France); Ghanbaja, J., E-mail: jaafar.ghanbaja@univ-lorraine.fr [Institut Jean Lamour – UMR CNRS–Université de Lorraine, 7198, Parc de Saurupt, Nancy 54011 (France); Redjaïmia, A., E-mail: abdelkrim.redjaimia@univ-lorraine.fr [Institut Jean Lamour – UMR CNRS–Université de Lorraine, 7198, Parc de Saurupt, Nancy 54011 (France); Michel, G., E-mail: gregory.michel@irt-m2p.fr [Institut de Recherche Technologique M2P, Metz 57070 (France); Thibault, S., E-mail: simon.thibault@safran.fr [Safran Tech, Magny les Hameaux (France); Belmonte, T., E-mail: thierry.belmonte@univ-lorraine.fr [Institut Jean Lamour – UMR CNRS–Université de Lorraine, 7198, Parc de Saurupt, Nancy 54011 (France)

    2017-05-02

    Metallurgical and mechanical responses of alloys 16NiCrMo13 and 23MnCrMo5 to the addition of carbon and/or nitrogen were investigated. Diffusion profiles of these interstitial elements were established by atmospheric pressure carburizing, austenitic nitriding, and a sequence of carburizing and nitriding – the carbonitriding. All treatments were performed at 1173 K under CO-H{sub 2} and/or NH{sub 3} based atmospheres. After enrichment, each sample was (i) room-temperature oil-quenched and (ii) immersed in boiling nitrogen prior to (iii) the stress relief treatment. Cross-section hardness profiles were evaluated after each of these steps. Electron probe microanalysis (EPMA) allowed for the determination of both carbon and nitrogen diffusion profiles after quenching. In order to estimate the fraction of nitrides formed during the enrichment of the alloys, these measured profiles were employed in the simulation of local equilibrium at each evaluated position. This allowed for the computation of total solid solution interstitial content, which was expressed in atomic fraction. Plots of as-quenched hardness against the square root of the computed interstitial content, i.e. the sum of solution carbon and the remaining nitrogen, show the complementary character of these elements in determining the mechanical properties of the materials prior to stress relief treatment. Tempering of carbon-nitrogen martensite resulted in hardness drop to a lesser degree than the one measured on carbon martensite with equivalent interstitial content. In order to investigate this behavior, transmission electron microscopy (TEM) analyses were performed. Results showed the precipitation of two morphologies of Fe{sub 16}N{sub 2} in the nitrogen-rich case and image analysis confirmed the simulated fraction of nitrides.

  6. Porous Nb-Ti-Ta alloy scaffolds for bone tissue engineering: Fabrication, mechanical properties and in vitro/vivo biocompatibility.

    Science.gov (United States)

    Liu, Jue; Ruan, Jianming; Chang, Lin; Yang, Hailin; Ruan, Wei

    2017-09-01

    Porous Nb-Ti-Ta (at.%) alloys with the pore size of 100-600μm and the porosity of 50%-80% were fabricated by the combination of the sponge impregnation technique and sintering method. The results revealed that the pores were well connected with three-dimensional (3D) network structure, which showed morphological similarity to the anisotropic porous structure of human bones. The results also showed that the alloys could provide the compressive Young's modulus of 0.11±0.01GPa to 2.08±0.09GPa and the strength of 17.45±2.76MPa to 121.67±1.76MPa at different level of porosity, indicating that the mechanical properties of the alloys are similar to those of human bones. Pore structure on the compressive properties was also discussed on the basis of the deformation mode. The relationship between compressive properties and porosity was well consistent with the Gibson-Ashby model. The mechanical properties could be tailored to match different requirements of the human bones. Moreover, the alloys had good biocompatibility due to the porous structure with higher surface, which were suitable for apatite formation and cell adhesion. In conclusion, the porous Nb-Ti-Ta alloy is potentially useful in the hard tissue implants for the appropriate mechanical properties as well as the good biocompatible properties. Copyright © 2017. Published by Elsevier B.V.

  7. Techniques for chemical characterization of zirconium and its alloys

    International Nuclear Information System (INIS)

    Iyer, K.V.; Bassan, M.K.T.; Sudersanan, M.

    2002-01-01

    Chemical characterization of zirconium and its alloys such as zircaloy, Zr-Nb, etc for minor and trace constituents like Nb, Ti, Fe, Cr, Ni, Sn, Al etc has been carried out. Zirconium, being a major constituent, has been determined by gravimetry as zirconium oxide while other constituents like Nb, Ti, Fe have been determined by spectrophotometric methods. Other metals of importance at trace level have been estimated by AAS or ICPAES. The judicious use of both conventional and modern instrumental methods of analysis helps in the characterization of zirconium and its alloys for various major and minor constituents. The role of matrix effect in the determination was also investigated and methods have been worked out based on a preliminary separation of zirconium by a hydroxide precipitation. (author)

  8. Sputtering. [as deposition technique in mechanical engineering

    Science.gov (United States)

    Spalvins, T.

    1976-01-01

    This paper primarily reviews the potential of using the sputtering process as a deposition technique; however, the manufacturing and sputter etching aspects are also discussed. Since sputtering is not regulated by classical thermodynamics, new multicomponent materials can be developed in any possible chemical composition. The basic mechanism for dc and rf sputtering is described. Sputter-deposition is described in terms of the unique advantageous features it offers such as versatility, momentum transfer, stoichiometry, sputter-etching, target geometry (coating complex surfaces), precise controls, flexibility, ecology, and sputtering rates. Sputtered film characteristics, such as strong adherence and coherence and film morphology, are briefly evaluated in terms of varying the sputtering parameters. Also described are some of the specific industrial areas which are turning to sputter-deposition techniques.

  9. Mechanical system diagnostics using vibration testing techniques

    Science.gov (United States)

    Mcleod, Catherine D.; Raju, P. K.; Crocker, M. J.

    1990-01-01

    The 'Cepstrum' technique of vibration-path identification allows the recovery of the transfer function of a system with little knowledge as to its excitation force, by means of a mathematical manipulation of the system output in conjunction with subtraction of part of the output and suitable signal processing. An experimental program has been conducted to evaluate the usefulness of this technique in the cases of simple, cantilever-beam and free-free plate structures as well as in that of a complex mechanical system. On the basis of the transfer functions thus recovered, it was possible to evaluate the shifts in the resonance frequencies of a structure due to the presence of defects.

  10. Microstructure and mechanical properties of as-cast Zr-Nb alloys.

    Science.gov (United States)

    Kondo, Ryota; Nomura, Naoyuki; Suyalatu; Tsutsumi, Yusuke; Doi, Hisashi; Hanawa, Takao

    2011-12-01

    On the basis of the microstructures and mechanical properties of as-cast Zr-(0-24)Nb alloys the effects of phase constitution on the mechanical properties and magnetic susceptibility are discussed in order to develop Zr alloys for use in magnetic resonance imaging (MRI). The microstructures were evaluated using an X-ray diffractometer, an optical microscope, and a transmission electron microscope; the mechanical properties were evaluated by a tensile test. The α' phase was dominantly formed with less than 6 mass% Nb content. The ω phase was formed in Zr-(6-20)Nb alloys, but disappeared from Zr-22Nb. The β phase dominantly existed in Zr-(9-24)Nb alloys. The mechanical properties as well as the magnetic susceptibility of the Zr-Nb alloys varied depending on the phase constitution. The Zr-Nb alloys consisting of mainly α' phase showed high strength, moderate ductility, and a high Young's modulus, retaining low magnetic susceptibility. Zr-Nb alloys containing a larger volume of ω phase were found to be brittle and, thus, should be avoided, despite their low magnetic susceptibility. When the Zr-Nb alloys consisted primarily of β phase the effect of ω phase weakened the mechanical properties, thereby leading to an increase in ductility, even with an increase in magnetic susceptibility. The minimum value of Young's modulus was obtained for Zr-20Nb, because this composition was the phase boundary between the β and ω phases. However, the magnetic susceptibility of the alloy was half that of Ti-6Al-4V alloys. Zr-Nb alloys consisting of α' or β phase have excellent mechanical properties with low magnetic susceptibility and, thus, these alloys could be useful for medical devices used in MRI. Copyright © 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  11. Mechanical behavior and strengthening mechanisms in ultrafine grain precipitation-strengthened aluminum alloy

    International Nuclear Information System (INIS)

    Ma, Kaka; Wen, Haiming; Hu, Tao; Topping, Troy D.; Isheim, Dieter; Seidman, David N.; Lavernia, Enrique J.; Schoenung, Julie M.

    2014-01-01

    To provide insight into the relationships between precipitation phenomena, grain size and mechanical behavior in a complex precipitation-strengthened alloy system, Al 7075 alloy, a commonly used aluminum alloy, was selected as a model system in the present study. Ultrafine-grained (UFG) bulk materials were fabricated through cryomilling, degassing, hot isostatic pressing and extrusion, followed by a subsequent heat treatment. The mechanical behavior and microstructure of the materials were analyzed and compared directly to the coarse-grained (CG) counterpart. Three-dimensional atom-probe tomography was utilized to investigate the intermetallic precipitates and oxide dispersoids formed in the as-extruded UFG material. UFG 7075 exhibits higher strength than the CG 7075 alloy for each equivalent condition. After a T6 temper, the yield strength (YS) and ultimate tensile strength (UTS) of UFG 7075 achieved 734 and 774 MPa, respectively, which are ∼120 MPa higher than those of the CG equivalent. The strength of as-extruded UFG 7075 (YS: 583 MPa, UTS: 631 MPa) is even higher than that of commercial 7075-T6. More importantly, the strengthening mechanisms in each material were established quantitatively for the first time for this complex precipitation-strengthened system, accounting for grain-boundary, dislocation, solid-solution, precipitation and oxide dispersoid strengthening contributions. Grain-boundary strengthening was the predominant mechanism in as-extruded UFG 7075, contributing a strength increment estimated to be 242 MPa, whereas Orowan precipitation strengthening was predominant in the as-extruded CG 7075 (∼102 MPa) and in the T6-tempered materials, and was estimated to contribute 472 and 414 MPa for CG-T6 and UFG-T6, respectively

  12. Mechanical Design Optimization Using Advanced Optimization Techniques

    CERN Document Server

    Rao, R Venkata

    2012-01-01

    Mechanical design includes an optimization process in which designers always consider objectives such as strength, deflection, weight, wear, corrosion, etc. depending on the requirements. However, design optimization for a complete mechanical assembly leads to a complicated objective function with a large number of design variables. It is a good practice to apply optimization techniques for individual components or intermediate assemblies than a complete assembly. Analytical or numerical methods for calculating the extreme values of a function may perform well in many practical cases, but may fail in more complex design situations. In real design problems, the number of design parameters can be very large and their influence on the value to be optimized (the goal function) can be very complicated, having nonlinear character. In these complex cases, advanced optimization algorithms offer solutions to the problems, because they find a solution near to the global optimum within reasonable time and computational ...

  13. Characterization of wear mechanism by tribo-corrosion of nickel base alloys

    International Nuclear Information System (INIS)

    Ionescu, C.C.

    2012-01-01

    Some components of nuclear power plants, as steam generator tubes are made from Ni base alloys. These components are exposed to severe environment of high temperature and high pressure and submitted to contact mechanical stresses. These Ni - based alloys properties are determined by their ability to form on their surface an inner protective barrier film mainly composed of Cr 2 O 3 . The steam generator tubes are among the most difficult components to maintain, on the hand, because of their safety importance and secondly, the exchange tubes are subject to various degradation mechanisms, because of the harsh conditions of work. Wear by tribo-corrosion is a physicochemical aging mechanism which occurs in the management of the nuclear power plants life time. Tribo-corrosion is an irreversible process which involves mechanical and chemical / electrochemical interactions between surfaces in relative motion, in the presence of a corrosive environment. The goal of this study was to quantify in terms of quantity and quality the wear generated by tribo-corrosion process on Ni - Cr model alloys. Two model alloys: Ni -15Cr and Ni -30Cr were used to highlight, evaluate and compare the influence of the chromium content on the formation of the protective oxide layer and the role played by the latter one on the kinetics and mechanisms of wear by tribo-corrosion. The tribo-corrosion experiments were performed by using a pin-on-disc tribometer under controlled electrochemical conditions in LiOH - H 3 BO 3 solution. The corrosion - wear degradation of the protective layer during continuous and intermittent unidirectional sliding tests was investigated by a three-stage tribo-corrosion protocol. In the first stage, electrochemical techniques (open circuit potential measurements and electrochemical impedance measurements) were used without applying unidirectional sliding to monitor and evaluate the characteristics of protective oxide layer formed on the surface of the two model alloys

  14. Metallurgical and Mechanical Characterization of High Temperature Titanium Alloys Joined by Friction Stir Welding

    Science.gov (United States)

    Gangwar, Kapil Dev

    flow has been done by scanning electron microscopy (SEM), and electron dispersive spectroscopy (EDS). Hardness profiles on the transverse cross section of the weld have been measured in order to relate the deformation of main constituents, α {hexagonal close packed (hcp)}, and β {body centered cubic (bcc)} that provides a new paradigm into grain refinement mechanism. Material flow and evolving microstructure along with distribution of corresponding elements distribution was characterized by SEM, and EDS respectively. For the case of dissimilar alloys (Ti-6242 & Ti-54M, and Ti-6242 & Ti-64 ) a necklace shaped macrostructure has been observed in the WN consisting of untransformed α migrating from the side of Ti-6242, and of basket-weave morphology (prior β grains transforming into α+β decorated with grain boundary α) of Ti-54M. Microhardness characterization undoubtedly reveals distinct boundaries between weld nugget and parent material. However, to understand the constitutive behavior of the thermo mechanically affected zone (TMAZ) on the advancing side (ADV), or retreating side (RET) and of WN, digital image correlation (DIC) technique has been adapted to develop strain maps in transverse tensile specimens. Improved mechanical properties of TMAZ on the ADV in comparison with RET TMAZ are in accordance with hardness values. Occurrence of fracture on the RET side, and morphology of the fractured surface have also been discussed. Based on the fractured morphology, it can be said that the presence of distinct and clustered island like morphologies in the form of transcrystalline and intercrystalline fracture is a results of microstructure that evolves due to difference in β transus temperature of two alloys. The mechanical properties are analyzed and discussed in that regard. Evolving volume fraction of phases along with their crystallographic orientation has also been elucidated. Evolution of texture has been discussed in terms of (100)_α,(002)_α,(110)_β,(101

  15. Effect of Zn addition on microstructure and mechanical properties of an Al–Mg–Si alloy

    Directory of Open Access Journals (Sweden)

    Lizhen Yan

    2014-04-01

    Full Text Available In the present work, an Al–0.66Mg–0.85Si–0.2Cu alloy with Zn addition was investigated by electron back scattering diffraction (EBSD, high resolution electron microscopy (HREM, tensile and Erichsen tests. The mechanical properties of the alloy after pre-aging met the standards of sheet forming. After paint baking, the yield strength of the alloy was improved apparently. GP(II zones and ηʹ phases were formed during aging process due to Zn addition. With the precipitation of GP zones, β″ phases, GP(II zones and ηʹ phases, the alloys displayed excellent mechanical properties.

  16. The effect of tungsten on mechanical properties of the Ti-9% Al-3% Zr alloy

    International Nuclear Information System (INIS)

    Nartova, T.T.; Grigor'ev, I.P.; Stepanov, Yu.N.; Tarasova, O.B.

    1979-01-01

    The effect of tungsten (from 0 to 10 %) on mechanical properties of the ternary Ti-9 %, Al-3 % Zr alloy, has been studied. The microstructure, tensile properties at 20 and 600 deg C and Vickers hardness in as-forged and as-annealed states have been studied. The experiments have shown that the ultimate strength increases with tungsten content. Titanium alloys with 9 % Al and 3 % Zr in the case of varying tungsten content at 20 deg C fracture by brittle mechanism. The dUctility of the annealed alloy does not rise at 20 deg C, but at the test temperature of 600 deg C the alloy becomes ductile

  17. Experimental techniques for the study of radiation damage in metals and alloys

    International Nuclear Information System (INIS)

    Novion, C.H. de.

    1983-06-01

    In this review, one presents the main experimental techniques used to study point defects and defect clusters introduced by irradiation in metals and alloys; emphasis will be put on some recent techniques. In particular, the studies allowing to analyse the very small agglomerates of point defects (Huang and small angle scattering, positron annihilation, electron microscopy) will be compared [fr

  18. Comparative study of structure formation and mechanical behavior of age-hardened Ti–Nb–Zr and Ti–Nb–Ta shape memory alloys

    Energy Technology Data Exchange (ETDEWEB)

    Inaekyan, K. [Ecole de Technologie Superieure, 1100, Notre-Dame Str. West, Montreal Quebec H3C 1K3 (Canada); Brailovski, V., E-mail: vladimir.brailovski@etsmtl.ca [Ecole de Technologie Superieure, 1100, Notre-Dame Str. West, Montreal Quebec H3C 1K3 (Canada); Prokoshkin, S. [National University of Science and Technology “MISIS”, Leninskiy prosp. 4, Moscow 119049 (Russian Federation); Pushin, V. [Institute of Metal Physics, Ural Branch of Russian Academy of Sciences, 18, S. Kovalevskoy Str., Ekaterinburg 620199 (Russian Federation); Dubinskiy, S.; Sheremetyev, V. [Ecole de Technologie Superieure, 1100, Notre-Dame Str. West, Montreal Quebec H3C 1K3 (Canada); National University of Science and Technology “MISIS”, Leninskiy prosp. 4, Moscow 119049 (Russian Federation)

    2015-05-15

    This work sets out to study the peculiar effects of aging treatment on the structure and mechanical behavior of cold-rolled and annealed biomedical Ti–21.8Nb–6.0Zr (TNZ) and Ti–19.7Nb–5.8Ta (TNT) (at.%) shape memory alloys by means of transmission electron microscopy, X-ray diffractometry, functional fatigue and thermomechanical testing techniques. Dissimilar effects of aging treatment on the mechanical behavior of Zr- and Ta-doped alloys are explained by the differences in the ω-phase formation rate, precipitate size, fraction and distribution, and by their effect on the alloys' critical stresses and transformation temperatures. Even short-time aging of the TNZ alloy leads to its drastic embrittlement caused by “overaging”. On the contrary, during aging of the TNT alloy, formation of finely dispersed ω-phase precipitates is gradual and controllable, which makes it possible to finely adjust the TNT alloy functional properties using precipitation hardening mechanisms. To create in this alloy nanosubgrained dislocation substructure containing highly-dispersed coherent nanosized ω-phase precipitates, the following optimum thermomechanical treatment is recommended: cold rolling (true strain 0.37), followed by post-deformation annealing (600 °C, 15–30 min) and age-hardening (300 °C, 30 min) thermal treatments. It is shown that in TNT alloy, pre-transition diffraction effects (diffuse reflections) can “mask” the β-phase substructure and morphology of secondary phases. - Highlights: • TNZ alloy is characterized by much higher ω-phase precipitation rate than TNT alloy. • Difference in precipitation rates is linked to the difference in Zr and Ta diffusion mobility. • Aging of nanosubgrained TNZ alloy worsens its properties irrespective of the aging time. • Aging time of nanosubgrained TNT alloy can be optimized to improve its properties.

  19. The growth mechanism of grain boundary carbide in Alloy 690

    International Nuclear Information System (INIS)

    Li, Hui; Xia, Shuang; Zhou, Bangxin; Peng, Jianchao

    2013-01-01

    The growth mechanism of grain boundary M 23 C 6 carbides in nickel base Alloy 690 after aging at 715 °C was investigated by high resolution transmission electron microscopy. The grain boundary carbides have coherent orientation relationship with only one side of the matrix. The incoherent phase interface between M 23 C 6 and matrix was curved, and did not lie on any specific crystal plane. The M 23 C 6 carbide transforms from the matrix phase directly at the incoherent interface. The flat coherent phase interface generally lies on low index crystal planes, such as (011) and (111) planes. The M 23 C 6 carbide transforms from a transition phase found at curved coherent phase interface. The transition phase has a complex hexagonal crystal structure, and has coherent orientation relationship with matrix and M 23 C 6 : (111) matrix //(0001) transition //(111) carbide , ¯ > matrix // ¯ 10> transition // ¯ > carbide . The crystal lattice constants of transition phase are c transition =√(3)×a matrix and a transition =√(6)/2×a matrix . Based on the experimental results, the growth mechanism of M 23 C 6 and the formation mechanism of transition phase are discussed. - Highlights: • A transition phase was observed at the coherent interfaces of M 23 C 6 and matrix. • The transition phase has hexagonal structure, and is coherent with matrix and M 23 C 6 . • The M 23 C 6 transforms from the matrix directly at the incoherent phase interface

  20. Generalized corrosion of nickel base alloys in high temperature aqueous media: a contribution to the comprehension of the mechanisms

    International Nuclear Information System (INIS)

    Marchetti-Sillans, L.

    2007-11-01

    In France, nickel base alloys, such as alloy 600 and alloy 690, are the materials constituting steam generators (SG) tubes of pressurized water reactors (PWR). The generalized corrosion resulting from the interaction between these alloys and the PWR primary media leads, on the one hand, to the formation of a thin protective oxide scale (∼ 10 nm), and on the other hand, to the release of cations in the primary circuit, which entails an increase of the global radioactivity of this circuit. The goal of this work is to supply some new comprehension elements about nickel base alloys corrosion phenomena in PWR primary media, taking up with underlining the effects of metallurgical and physico-chemical parameters on the nature and the growth mechanisms of the protective oxide scale. In this context, the passive film formed during the exposition of alloys 600, 690 and Ni-30Cr, in conditions simulating the PWR primary media, has been analyzed by a set of characterization techniques (SEM, TEM, PEC and MPEC, XPS). The coupling of these methods leads to a fine description, in terms of nature and structure, of the multilayered oxide forming during the exposition of nickel base alloys in primary media. Thus, the protective part of the oxide scale is composed of a continuous layer of iron and nickel mixed chromite, and Cr 2 O 3 nodules dispersed at the alloy / mixed chromite interface. The study of protective scale growth mechanisms by tracers and markers experiments reveals that the formation of the mixed chromite is the consequence of an anionic mechanism, resulting from short circuits like grain boundaries diffusion. Besides, the impact of alloy surface defects has also been studied, underlining a double effect of this parameter, which influences the short circuits diffusion density in oxide and the formation rate of Cr 2 O 3 nodules. The sum of these results leads to suggest a description of the nickel base alloys corrosion mechanisms in PWR primary media and to tackle some

  1. Change in mechanical properties of low-alloyed molybdenum alloys at two-stage strengthening during aging

    International Nuclear Information System (INIS)

    Bernshtejn, L.M.; Zakharov, A.M.; Arbuzov, V.K.

    1977-01-01

    Change in mechanical properties of hardened low-alloyed molybdenum alloys (Mo-Zr-C and Mo-Zr-Nb-C) at two-stage strengthening during ageing at 1400 deg C is studied. The initial strengthening maximum following ageing for 5 hr is caused by separation of dispersed ZrC particles and is accompanied by worsened plasticity, a development characteristic of precipitation hardening processes. The second increase in strength after a 10-hr ageing is not accompanied by reduced plasticity, this being characteristic of strengthening as a result of reconstruction of the dislocation structure. Niobium (0.16 wt.%) added to Mo-Zr-C alloys simultaneously increases their plastic and strength properties. The said effect is caused by prevention of premature decomposition of alloys on account of increased low-temperature plasticity, which permits to obtain high resistance to plastic deformation

  2. Comparative Study by MS and XRD of Fe50Al50 Alloys Produced by Mechanical Alloying, Using Different Ball Mills

    International Nuclear Information System (INIS)

    Rojas Martinez, Y.; Perez Alcazar, G. A.; Bustos Rodriguez, H.; Oyola Lozano, D.

    2005-01-01

    In this work we report a comparative study of the magnetic and structural properties of Fe 50 Al 50 alloys produced by mechanical alloying using two different planetary ball mills with the same ball mass to powder mass relation. The Fe 50 Al 50 sample milled during 48 h using the Fritsch planetary ball mill pulverisette 5 and balls of 20 mm, presents only a bcc alloy phase with a majority of paramagnetic sites, whereas that sample milled during the same time using the Fritsch planetary ball mill pulverisette 7 with balls of 15 mm, presents a bcc alloy phase with paramagnetic site (doublet) and a majority of ferromagnetic sites which include pure Fe. However for 72 h of milling this sample presents a bcc paramagnetic phase, very similar to that prepared with the first system during 48 h. These results show that the conditions used in the first ball mill equipment make more efficient the milling process.

  3. Production of NbC reinforced aluminum matrix composites by mechanical alloying

    International Nuclear Information System (INIS)

    Silva, Marina Judice; Cardoso, Katia Regina; Travessa, Dilermando Nagle

    2014-01-01

    Aluminum and their alloys are key materials for the automotive and aerospace industries. The dispersion of hard ceramic particles in the Al soft matrix produces lightweight composites with interesting properties, as environmental resistance, high specific strength and stiffness, high thermal and electrical conductivity, and good wear resistance, encouraging their technological use. Powder metallurgy techniques like mechanical alloying (MA) are very attractive to design metal matrix composites, as they are able to achieve a homogeneous distribution of well dispersed particles inside the metal matrix. In this work, pure aluminum has been reinforced with particles of Niobium carbide (NbC), an extremely hard and stable refractory ceramic. NbC is frequently used as a grain growth inhibitor in micro-alloyed steel due to their low solubility in austenite. In the present work, NbC is expected to act as a reinforcing phase by its fine dispersion into the aluminum matrix, produced by MA. Composite powders produced after different milling times (up to 50h), with 10 and 20% (volume) of NbC were characterized by diffraction laser particle size analysis, scanning electron microscopy (SEM) and by X-ray diffraction (DRX), in order to establish a relationship between the milling time and the characteristics of the powder produced, as size and morphology, crystallite size and reinforcement distribution. This characterization is important in defining the MA process for production of composites for further consolidation by hot extrusion process. (author)

  4. Study and understanding of the ageing mechanisms in lead-calcium alloys

    International Nuclear Information System (INIS)

    Rossi, F.

    2006-12-01

    The data available in the literature about ageing and over-ageing of lead-calcium alloys are often incomplete and inconsistent. It is undoubtedly due to the experimental difficulties encountered to observe the structure transformations which are numerous. As a result there is a certain confusion among the results of the different authors. Moreover, small variations in the process parameters and chemical composition may have some influence on the alloy behaviour. This work enabled us to obtain a set of TTT diagrams, more realistic and accurate than the ones available in the literature. Experimental techniques developed (particularly the preservation of the cold chain with is essential for the guaranty of the results repeatability), enabled particularly the study of the first transformations and better control the five stages of ageing and over-ageing. Our work have enabled to determine precisely the kinetics and the mechanisms of the transformations. This work constitutes a thorough analysis of the ageing and over-ageing of theses alloys. (author)

  5. Production of NbC reinforced aluminum matrix composites by mechanical alloying

    Energy Technology Data Exchange (ETDEWEB)

    Silva, Marina Judice; Cardoso, Katia Regina; Travessa, Dilermando Nagle, E-mail: dilermando.travessa@unifesp.br [Universidade Federal de Sao Paulo (UNIFESP), Sao Jose dos Campos, SP (Brazil). Instituto de Ciencia e Tecnologia

    2014-07-01

    Aluminum and their alloys are key materials for the automotive and aerospace industries. The dispersion of hard ceramic particles in the Al soft matrix produces lightweight composites with interesting properties, as environmental resistance, high specific strength and stiffness, high thermal and electrical conductivity, and good wear resistance, encouraging their technological use. Powder metallurgy techniques like mechanical alloying (MA) are very attractive to design metal matrix composites, as they are able to achieve a homogeneous distribution of well dispersed particles inside the metal matrix. In this work, pure aluminum has been reinforced with particles of Niobium carbide (NbC), an extremely hard and stable refractory ceramic. NbC is frequently used as a grain growth inhibitor in micro-alloyed steel due to their low solubility in austenite. In the present work, NbC is expected to act as a reinforcing phase by its fine dispersion into the aluminum matrix, produced by MA. Composite powders produced after different milling times (up to 50h), with 10 and 20% (volume) of NbC were characterized by diffraction laser particle size analysis, scanning electron microscopy (SEM) and by X-ray diffraction (DRX), in order to establish a relationship between the milling time and the characteristics of the powder produced, as size and morphology, crystallite size and reinforcement distribution. This characterization is important in defining the MA process for production of composites for further consolidation by hot extrusion process. (author)

  6. Mechanical response of nitrogen ion implanted NiTi shape memory alloy

    International Nuclear Information System (INIS)

    Kucharski, S.; Levintant-Zayonts, N.; Luckner, J.

    2014-01-01

    Highlights: • The effect of ion implantation process on shape memory alloy was investigated. • In the implantation process both surface layer and bulk material are modified. • The microstructure is modified and superelastic effect is destroyed in surface layer. • The parameters of superelastic phenomena are changed in bulk material. - Abstract: In the paper a change of material (mechanical) parameters of NiTi shape memory alloy subjected to ion implantation treatment is investigated. The spherical indentation tests in micro- and nano-scale and tension test have been performed to study an evolution of local superelastic effect in different volumes of nonimplanted and nitrogen ion implanted NiTi alloy. The differential scanning calorimetry has been applied to measure the change of characteristic temperatures due to ion implantation treatment. The structure of implanted material has been investigated using electron microscopy technique. It has been found that the ion implantation process changes the properties not only in a thin surface layer but also in bulk material. In the layer the pseudoelastic effect is destroyed, and in the substrate is preserved, however its parameters are changed. The characteristic phase transformation temperatures in substrate are also modified

  7. Simple thermodynamic model of the extension of solid solution of Cu-Mo alloys processed by mechanical alloying

    International Nuclear Information System (INIS)

    Aguilar, C.; Guzman, D.; Rojas, P.A.; Ordonez, Stella; Rios, R.

    2011-01-01

    Highlights: → Extension of solid solution in Cu-Mo systems achieved by mechanical alloying. → Simple thermodynamic model to explain extension of solid solution of Mo in Cu. → Model gives results that are consistent with the solubility limit extension reported in other works. - Abstract: The objective of this work is proposing a simple thermodynamic model to explain the increase in the solubility limit of the powders of the Cu-Mo systems or other binary systems processed by mechanical alloying. In the regular solution model, the effects of crystalline defects, such as; dislocations and grain boundary produced during milling were introduced. The model gives results that are consistent with the solubility limit extension reported in other works for the Cu-Cr, Cu-Nb and Cu-Fe systems processed by mechanical alloying.

  8. Fabrication and mechanical behavior of bulk nanoporous Cu via chemical de-alloying of Cu–Al alloys

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Fei, E-mail: chenfei027@gmail.com [State Key Lab of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070 (China); Chen, Xi; Zou, Lijie; Yao, Yao; Lin, Yaojun; Shen, Qiang [State Key Lab of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070 (China); Lavernia, Enrique J. [Department of Chemical Engineering and Materials Science, University of California at Irvine, Irvine, CA 92697 (United States); Zhang, Lianmeng, E-mail: lmzhang@whut.edu.cn [State Key Lab of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070 (China)

    2016-04-13

    We report on a study of the influence of microstructure on the mechanical behavior of bulk nanoporous Cu fabricated by chemical de-alloying of Cu{sub 50}Al{sub 50}, Cu{sub 40}Al{sub 60}, Cu{sub 33}Al{sub 67} and Cu{sub 30}Al{sub 70} (at%) alloys. The precursor Cu–Al alloys were fabricated using arc melting and bulk nanoporous Cu was obtained by subsequent de-alloying of Cu–Al alloys in 20 wt% NaOH aqueous solution at a temperature of 65 °C. We studied the microstructure of the precursor Cu–Al alloys, as well as that of the as de-alloyed bulk nanoporous Cu, using X-ray diffraction, scanning electron microscopy and energy dispersive spectrometry. Moreover, the compressive strength of bulk nanoporous Cu was measured and the relationship between microstructure and mechanical properties was studied. Our results show that the microstructure of bulk nanoporous Cu is characterized by bi-continuous interpenetrating ligament-channels with a ligament size of 130±20 nm (for Cu{sub 50}Al{sub 50}), 170±20 nm (for Cu{sub 40}Al{sub 60}) and 160±10 nm (for Cu{sub 33}Al{sub 67}). Interestingly the microstructure of de-alloyed Cu{sub 30}Al{sub 70} is bimodal with nanopores (100's nm) and interspersed featureless regions a few microns in size. The compressive strength increased with decreasing volume fraction of porosity; as porosity increased 56.3±2% to 73.9±2%, the compressive strength decreased from 17.18±1 MPa to 2.71±0.5 MPa.

  9. Investigation of corrosion resistance of alloys with high mechanical characteristics in some environments of food industry

    International Nuclear Information System (INIS)

    Tremoureux, Yves

    1978-01-01

    This research thesis aimed at improving knowledge in the field of stress-free corrosion of alloys with high mechanical characteristics in aqueous environments, at highlighting some necessary aspects of their behaviour during cleaning or disinfection, and at selecting alloys which possess a good stress-free corrosion resistance in view of a later investigation of their stress corrosion resistance. After a presentation of the metallurgical characteristics of high mechanical strength alloys and the report of a bibliographical study on corrosion resistance of these alloys, the author presents and discusses the results obtained in the study of a possible migration of metallic ions in a milk product which is submitted to a centrifugation, and of the corrosion resistance of selected alloys with respect to the different media they will be in contact with during ultra-centrifugation. The following alloys have been used in this research: Marval 18, Marphynox, Marval X12, 17-4PH steel, Inconel 718 [fr

  10. Corrosion mechanism of a Ni-based alloy in supercritical water: Impact of surface plastic deformation

    International Nuclear Information System (INIS)

    Payet, Mickaël; Marchetti, Loïc; Tabarant, Michel; Chevalier, Jean-Pierre

    2015-01-01

    Highlights: • The dissolution of Ni and Fe cations occurs during corrosion of Ni-based alloys in SCW. • The nature of the oxide layer depends locally on the alloy microstructure. • The corrosion mechanism changes when cold-work increases leading to internal oxidation. - Abstract: Ni–Fe–Cr alloys are expected to be a candidate material for the generation IV nuclear reactors that use supercritical water at temperatures up to 600 °C and pressures of 25 MPa. The corrosion resistance of Alloy 690 in these extreme conditions was studied considering the surface finish of the alloy. The oxide scale could suffer from dissolution or from internal oxidation. The presence of a work-hardened zone reveals the competition between the selective oxidation of chromium with respect to the oxidation of nickel and iron. Finally, corrosion mechanisms for Ni based alloys are proposed considering the effects of plastically deformed surfaces and the dissolution.

  11. A study on the composition optimization and mechanical properties of Al-Mg-Si cast alloys

    International Nuclear Information System (INIS)

    Zhang, X.H.; Su, G.C.; Han, Y.Y.; Ai, X.H.; Yan, W.L.

    2010-01-01

    The mechanical properties of Al-Mg-Si cast alloys with different chemical compositions were investigated using an orthogonal test method. The optimized chemical compositions of Al alloy are given in wt% as follows: 7.0%Si-0.35%Mg-2.0%Cu-0.2%Mn-0.2%Ni-0.1%V-0.8%RE-89.35%Al. The optimized Al-Mg-Si alloy with metal mold casting had excellent mechanical properties. The softening resistance of the optimized alloy was better than that of ZL101 at elevated temperatures. The scanning electron microscopy fractographs of the tensile samples of ZL101 and optimized Al alloy at different magnifications revealed that all the specimens were fractured in a ductile manner, consisting of well-developed dimples over the entire surface. The alloys failed in a mixed-mode fracture, comprised predominantly of transgranular shears and a small amount of quasi-cleavages.

  12. Mechanical properties of Fe-Mn-Cu-Al alloy systems and optimization of their composition

    International Nuclear Information System (INIS)

    Tkachenko, I.F.; Baranov, A.A.

    1981-01-01

    Studied is the separate and combined effect of Cu and Al on mechanical properties of the Fe-Mn-Al-Cu system alloys using a simplex- lattice method of experiment planning. Heat treated specimens in the form of plates have been subjected to mechanical tests. It is shown that mechanical properties of studied alloys change sufficiently in the result of tempering in heterogeneous (α+γ) region. Studied alloys have the most favourable conbination of characteristics of strength, plasticity and impact strength after tempering at 630 deg C during 2 hours. Diagrams are obtained which characterizes dependence of mechanical properties of alloys on their composition. They permit to select optimum compositions of alloys with the necessary combination of strength, plasticity and impact strength [ru

  13. Study on Strengthening and Toughening Mechanisms of Aluminum Alloy 2618-Ti at Elevated Temperature

    Science.gov (United States)

    Kun, Ma; Tingting, Liu; Ya, Liu; Xuping, Su; Jianhua, Wang

    2018-01-01

    The tensile properties of the alloy 2618 and 2618-Ti were tested using a tensile testing machine. The morphologies of the fracture of tensile samples were observed using scanning electron microscopy. The strengthening and toughening mechanisms of alloy 2618-Ti at elevated temperature were systematically investigated based on the analyses of experimental results. The results showed that the tensile strength of alloy 2618-Ti is much higher than that of alloy 2618 at the temperature range of 250 and 300 °C. But the elongation of alloy 2618-Ti is much higher than that of alloy 2618 at the temperature range of 200 and 300 °C. The equal-strength temperature of intragranular and grain boundary of alloy 2618-Ti is about 235 °C. When the temperature is lower than 235 °C, the strengthening of alloy 2618-Ti is ascribed to the strengthening effect of fine grains and dispersed Al3Ti/Al18Mg3Ti2 phase. When the temperature is higher than 235 °C, the strengthening effect of alloy 2618-Ti is mainly attributed to the load transfer of Al3Ti and Al18Mg3Ti2 particles. The toughening of alloy 2618-Ti at elevated temperature is mainly ascribed to the fine grain microstructure, excellent combination between matrix and dispersed Al3Ti/Al18Mg3Ti2 particles as well as the recrystallization of the alloy at elevated temperature.

  14. Development of casting techniques for uranium and uranium alloys

    International Nuclear Information System (INIS)

    Singh, S.P.

    2003-01-01

    The casting process concerning furnace set-up, mould temperatures, pouring temperatures, out gassing, post heating, casting recovery and crucible and mould clean-up is discussed. Some applications of casting theory can be made in practice, but experience in handling the metal is most valuable in the successful solution of a new problem. The casting of uranium alloys using induction stirring of the melt to promote homogeneity in the casting is described. A few remarks are made concerning safety aspects associated with the casting of uranium

  15. Aerobic rice mechanization: techniques for crop establishment

    Science.gov (United States)

    Khusairy, K. M.; Ayob, H.; Chan, C. S.; Fauzi, M. I. Mohamed; Mohamad Fakhrul, Z. O.; Shahril Shah, G. S. M.; Azlan, O.; Rasad, M. A.; Hashim, A. M.; Arshad, Z.; E, E. Ibrahim; Saifulizan, M. N.

    2015-12-01

    Rice being the staple food crops, hundreds of land races in it makes the diversity of rice crops. Aerobic rice production was introduced which requires much less water input to safeguard and sustain the rice production and conserve water due to decreasing water resources, climatic changes and competition from urban and industrial users. Mechanization system plays an important role for the success of aerobic rice cultivation. All farming activities for aerobic rice production are run on aerobic soil conditions. Row seeder mechanization system is developed to replace conventional seeding technique on the aerobic rice field. It is targeted for small and the large scale aerobic rice farmers. The aero - seeder machine is used for the small scale aerobic rice field, while the accord - seeder is used for the large scale aerobic rice field. The use of this mechanization machine can eliminate the tedious and inaccurate seeding operations reduce labour costs and increases work rate. The machine is easy to operate and it can increase crop establishment rate. It reduce missing hill, increasing planting and crop with high yield can be produce. This machine is designed for low costs maintenance and it is easy to dismantle and assemble during maintenance and it is safe to be used.

  16. About some corrosion mechanisms of AZ91D magnesium alloy

    International Nuclear Information System (INIS)

    Ballerini, Gaia; Bardi, Ugo; Bignucolo, Roberto; Ceraolo, Giuseppe

    2005-01-01

    The present work is dedicated to a study of the corrosion resistance of AZ91D (91% Mg) alloy in wet environments. Three industrial alloys obtained by die-casting or sand casting were subjected to salt spray corrosion tests (ASTM-B117 standard) and immersion tests. Weight loss kinetic curves were measured. Surface analysis was performed by X-ray photoelectron diffraction (XPS). After corrosion the sand cast alloy presents a surface mainly enriched in hydroxides and carbonates while the die-cast alloy presents a surface enriched also in mixed Mg-Al oxides. The quantitative analysis of the rate Mg/Al shows an enrichment in aluminium for the die-cast alloys in comparison to the sand cast alloy

  17. New X-Ray Technique to Characterize Nanoscale Precipitates in Aged Aluminum Alloys

    Science.gov (United States)

    Sitdikov, V. D.; Murashkin, M. Yu.; Valiev, R. Z.

    2017-10-01

    This paper puts forward a new technique for measurement of x-ray patterns, which enables to solve the problem of identification and determination of precipitates (nanoscale phases) in metallic alloys of the matrix type. The minimum detection limit of precipitates in the matrix of the base material provided by this technique constitutes as little as 1%. The identification of precipitates in x-ray patterns and their analysis are implemented through a transmission mode with a larger radiation area, longer holding time and higher diffractometer resolution as compared to the conventional reflection mode. The presented technique has been successfully employed to identify and quantitatively describe precipitates formed in the Al alloy of the Al-Mg-Si system as a result of artificial aging. For the first time, the x-ray phase analysis has been used to identify and measure precipitates formed during the alloy artificial aging.

  18. Solid-state reactions during mechanical alloying of ternary Fe–Al–X (X=Ni, Mn, Cu, Ti, Cr, B, Si) systems: A review

    Energy Technology Data Exchange (ETDEWEB)

    Hadef, Fatma, E-mail: hadef77@yahoo.fr [Laboratoire de Recherche sur la Physico-Chimie des Surfaces et Interfaces, LRPCSI, Université 20 Août 1955, BP 26, Route d’El-Haddaiek, Skikda 21000 (Algeria); Département de Physique, Faculté des Sciences, Université 20 Août 1955, BP 26, Route d’El-Haddaiek, Skikda 21000 (Algeria)

    2016-12-01

    The last decade has witnessed an intensive research in the field of nanocrystalline materials due to their enhanced properties. A lot of processing techniques were developed in order to synthesis these novel materials, among them mechanical alloying or high-energy ball milling. In fact, mechanical alloying is one of the most common operations in the processing of solids. It can be used to quickly and easily synthesize a variety of technologically useful materials which are very difficult to manufacture by other techniques. One advantage of MA over many other techniques is that is a solid state technique and consequently problems associated with melting and solidification are bypassed. Special attention is being paid to the synthesis of alloys through reactions mainly occurring in solid state in many metallic ternary Fe–Al–X systems, in order to improve mainly Fe–Al structural and mechanical properties. The results show that nanocrystallization is the common result occurring in all systems during MA process. The aim of this work is to illustrate the uniqueness of MA process to induce phase transformation in metallic Fe–Al–X (X=Ni, Mn, Cu, Ti, Cr, B, Si) systems. - Highlights: • A review of state of the art on binary Fe–Al alloys was presented. • Structural and microstructural properties of MA ternary Fe–Al–X alloys were summerized. • MA process is a powerful tool for producing metallic alloys at the nanometer scale.

  19. New Leaf Gilding Alloys: Physico-Chemistry, Colour, Mechanical Behavior

    OpenAIRE

    Darque-Ceretti , Evelyne; Aucouturier , Marc; Felder , Eric; Burr , Alain; Robcis , Dominique; Thomas , Caroline

    2015-01-01

    International audience; In the frame of a systematic investigation on leaf gilding history and processes, in a research program intending to propose gold leaf alloys specially devoted to restoration, new gold alloys containing low concentration additions of In or Pd were designed and leaves were elaborated in collaboration with the goldbeater Dauvet. The influence of those elements on the colour change induced by alloying was obtained by colorimetry. The microstructural and metallurgical prop...

  20. Mechanical Properties of Titanium and Aluminum Alloys at Cryogenic Temperatures

    Science.gov (United States)

    1962-03-01

    aluminum alloys. Table I is a tabulation of the chemical composition of the tita - nium alloys. The bar was 5/8 inch in diameter and the sheet 0.060 inch...Ti-6AI-4V Tensile azid yield strength data for both bar and sheet of this tita - nium alloy are shown in Figure A-3. Bar and sheet data show approxi...not recommended for low temperature applications. The remainder of the tita - nium alloys were tested from room temperature to -452 F. In general, Ti

  1. Investigation of impingement attack mechanism of copper alloy condenser tubes

    Energy Technology Data Exchange (ETDEWEB)

    Fukumura, Takuya; Nakajima, Nobuo; Arioka, Koji; Totsuka, Nobuo; Nakagawa, Tomokazu [Institute of Nuclear Safety System Inc., Mihama, Fukui (Japan)

    2001-09-01

    In order to investigate generation and growth mechanisms of impingement attacks of sea water against copper alloy condenser tubes used in condensers of nuclear power plants, we took out condenser tubes from actual condensers, cut them into several pieces and carried out several material tests mainly for impinged spots. In addition water flow inside of a pit was analyzed. From the results of the investigation, it was found that all of impingement attacks were found in the marks left by sessile organisms and none were found in downstream of the marks as frequently proposed so far. At the pits generated inside the marks, iron coating was striped and zinc content was deficient in some cases. Combining these data and the result of flow analysis, we considered the following mechanism of the impingement attacks: sessile organisms clinging to the surface of the condenser tube and growth, occlusion of the tube, extinction and decomposition of sessile organisms, pollution corrosion under the organisms and cavity formation, occlusion removal by the cleaning, generation of impingement attacks by flow collision inside the cavity, growth of the impingement attacks. (author)

  2. A Technique for Dynamic Corrosion Testing in Liquid Lead Alloys

    Energy Technology Data Exchange (ETDEWEB)

    Loewen, Eric Paul; Davis, Cliff Bybee; Mac Donald, Philip Elsworth

    2001-04-01

    An experimental apparatus for the investigation of the flow-assisted dissolution and precipitation (corrosion) of potential fuel cladding and structural materials to be used in liquid lead alloy cooled reactors has been designed. This experimental project is part of a larger research effort between Idaho National Engineering and Environmental Laboratory (INEEL) and Massachusetts Institute of Technology to investigate the suitability of lead, lead-bismuth, and other lead alloys for cooling fast reactors designed to produce low-cost electricity as well as for actinide burning. The INEEL forced convection corrosion cell consists of a small heated vessel with a shroud and gas flow system. The gas flow rates, heat input, and shroud and vessel dimensions have been adjusted so that a controlled coolant flow rate, temperature, and oxygen potential are created within the downcomer located between the shroud and vessel wall. The ATHENA computer code was used to design the experimental apparatus and estimate the fluid conditions. The corrosion cell will test steel that is commercially available in the U. S. to temperatures above 650oC.

  3. Effect of Nb on magnetic and mechanical properties of TbDyFe alloys

    Science.gov (United States)

    Wang, Naijuan; Liu, Yuan; Zhang, Huawei; Chen, Xiang; Li, Yanxiang

    2018-03-01

    The intrinsic brittleness in giant magnetostrictive material TbDyFe alloy has devastating influence on the machinability and properties of the alloy, thus affecting its applications. The purpose of this paper is to study the mechanical properties of the TbDyFe alloy by alloying with Nb element. The samples (Tb0.3Dy0.7)xFe2xNby (y = 0, 0.01, 0.04, 0.07, 0.1; 3x + y = 1) were melted in an arc melting furnace under high purity argon atmosphere. The microstructure, magnetostrictive properties and mechanical performance of the alloys were studied systematically. The results showed that NbFe2 phases were observed in the alloys with the addition of Nb. Moreover, both the NbFe2 phases and rare earth (RE)-rich phases were increased with the increasing of Nb element. The mechanical properties results revealed that the fracture toughness of the alloy with the addition of Nb enhanced 1.5-5 times of the Nb-free alloy. Both the NbFe2 phase and the RE-rich phase had the ability to prevent crack propagation, so that they can strengthen the REFe2 body. However, NbFe2 phase is a paramagnetic phase, which can reduce the magnetostrictive properties of the alloy by excessive precipitation.

  4. Structure, mechanical properties and grindability of dental Ti-10Zr-X alloys

    International Nuclear Information System (INIS)

    Ho, W.-F.; Cheng, C.-H.; Pan, C.-H.; Wu, S.-C.; Hsu, H.-C.

    2009-01-01

    This study aimed to investigate the structure, mechanical properties and grindability of a binary Ti-Zr alloy added to a series of alloying elements (Nb, Mo, Cr and Fe). The phase and structure of Ti-10Zr-X alloys were evaluated using an X-ray diffraction (XRD) for phase analysis and optical microscope for microstructure of the etched alloys. Three-point bending tests were performed using a desk-top mechanical tester. Grindability was evaluated by measuring the amount of metal volume removed after grinding for 1 min at each of the four rotational speeds of the wheel (500, 750, 1000 or 1200 m/min). Results were compared with c.p. Ti, which was chosen as a control. Results indicated that the phase/crystal structure, microstructure, mechanical properties and grindability of the Ti-10Zr alloy can be significantly changed by adding small amounts of alloying elements. The alloying elements Nb, Mo, Cr and Fe contributed significantly to increasing the grinding ratio under all grinding conditions, although the grinding rate of all the metals was found to be largely dependent on grinding speed. The Ti-10Zr-1Mo alloy showed increases in microhardness (63%), bending strength (40%), bending modulus (30%) and elastic recovery angle (180%) over those of c.p. Ti, and was also found to have better grindability. The Ti-10Zr-1Mo alloy could therefore be used for prosthetic dental applications if other conditions necessary for dental casting are met

  5. Effect of Al on Grain Refinement and Mechanical Properties of Mg-3Nd Casting Alloy

    Science.gov (United States)

    Wang, Lei; Feng, Yicheng; Wang, Liping; Chen, Yanhong; Guo, Erjun

    2018-05-01

    The effect of Al on the grain refinement and mechanical properties of as-cast Mg-3Nd alloy was investigated systematically by a series of microstructural analysis, solidification analysis and tensile tests. The results show that Al has an obvious refining effect on the as-cast Mg-3Nd alloy. With increasing Al content, the grain size of the as-cast Mg-3Nd alloy decreases firstly, then increases slightly after the Al content reaching 3 wt.%, and the minimum grain size of the Mg-3Nd alloy is 48 ± 4.0 μm. The refining mechanism can be attributed to the formation of Al2Nd particles, which play an important role in the heterogeneous nucleation. The strength and elongation of the Mg-3Nd alloy refined by Al also increase with increasing Al content and slightly decrease when the Al content is more than 3 wt.%, and the strengthening mechanism is attributed to the grain refinement as well as dispersed intermetallic particles. Furthermore, the microstructural thermal stability of the Mg-3Nd-3Al alloy is higher than that of the Mg-3Nd-0.5Zr alloy. Overall, the Mg-3Nd alloy with Al addition is a novel alloy with wide and potential application prospects.

  6. Cu-based shape memory alloys with enhanced thermal stability and mechanical properties

    International Nuclear Information System (INIS)

    Chung, C.Y.; Lam, C.W.H.

    1999-01-01

    Cu-based shape memory alloys were developed in the 1960s. They show excellent thermoelastic martensitic transformation. However the problems in mechanical properties and thermal instability have inhibited them from becoming promising engineering alloys. A new Cu-Zn-Al-Mn-Zr Cu-based shape memory alloy has been developed. With the addition of Mn and Zr, the martensitic transformation behaviour and the grain size ca be better controlled. The new alloys demonstrates good mechanical properties with ultimate tensile strenght and ductility, being 460 MPa and 9%, respectively. Experimental results revealed that the alloy has better thermal stability, i.e. martensite stabilisation is less serious. In ordinary Cu-Zn-Al alloys, martensite stabilisation usually occurs at room temperature. The new alloy shows better thermal stability even at elevated temperature (∝150 C, >A f =80 C). A limited small amount of martensite stabilisation was observed upon ageing of the direct quenched samples as well as the step quenched samples. This implies that the thermal stability of the new alloy is less dependent on the quenching procedure. Furthermore, such minor martensite stabilisation can be removed by subsequent suitable parent phase ageing. The new alloy is ideal for engineering applications because of its better thermal stability and better mechanical properties. (orig.)

  7. Effect of ternary alloying elements on microstructure and mechanical property of Nb-Si based refractory intermetallic alloy

    International Nuclear Information System (INIS)

    Kim, W.Y.; Kim, H.S.; Kim, S.K.; Ra, T.Y.; Kim, M.S.

    2005-01-01

    Microstructure and mechanical property at room temperature and at 1773 K of Nb-Si based refractory intermetallic alloys were investigated in terms of compression and fracture toughness test. Mo and V were chosen as ternary alloying elements because of their high melting points, atomic sizes smaller than Nb. Both ternary alloying elements were found to have a significant role in modifying the microstructure from dispersed structure to eutectic-like structure in Nb solid solution/Nb 5 Si 3 intermetallic composites. The 0.2% offset yield strength at room temperature increased with increasing content of ternary elements in Nb solid solution and volume fraction of Nb 5 Si 3 . At 1773 K, Mo addition has a positive role in increasing the yield strength. On the other hand, V addition has a role in decreasing the yield strength. The fracture toughness of ternary alloys was superior to binary alloys. Details will be discussed in correlation with ternary alloying, volume fraction of constituent phase, and the microstructure. (orig.)

  8. Effect of low-temperature thermomechanical treatment on mechanical properties of low-alloying molybdenum alloys with carbide hardening

    International Nuclear Information System (INIS)

    Bernshtejn, L.M.; Zakharov, A.M.; Veller, M.V.

    1978-01-01

    Presented are results of testing low-temperature thermomechanical treatment of low-alloying molybdenum alloys, including quenching from 2100 deg C, 40% deformation by hydroextrusion and aging at the temperature of 1200-1400 deg C. Tensile tests at room temperature with the following processing of results have shown that low-temperature thermomechanical treatment of low-alloying molybdenum alloys of Mo-Zr-C and Mo-Zr-Nb-C systems leads to a significant increase in low-temperature mechanical properties (strength properties - by 30-35%, ductility - by 30-40%) as compared with conventional heat treatment (aging after quenching). The treatment proposed increases resistance to small, as well as large plastic deformations, and leads to a simultaneous rise of strength and plastic properties at all stages of tensile test. Alloying of the Mo-Zr-C system with niobium increases both strength and plastic characteristics as compared with alloys without niobium when testing samples, subjected to low temperature thermomechanical treatment and conventional heat treatment at room temperature

  9. Zr-based conversion layer on Zn-Al-Mg alloy coated steel sheets: insights into the formation mechanism

    International Nuclear Information System (INIS)

    Lostak, Thomas; Maljusch, Artjom; Klink, Björn; Krebs, Stefan; Kimpel, Matthias; Flock, Jörg; Schulz, Stephan; Schuhmann, Wolfgang

    2014-01-01

    Zr-based conversion layers are considered as environmentally friendly alternatives replacing trication phosphatation in the automotive industry. Based on excellent electronic barrier properties they provide an effective corrosion protection of the metallic substrate. In this work, thin protective layers were grown on novel Zn-Al-Mg alloy coated steel sheets by increasing the local pH-value at the sample surface leading to deposition of a Zr-based conversion layer. For this purpose Zn-Al-Mg alloy (ZM) coated steel sheets were treated in an aqueous model conversion solution containing well-defined amounts of hexafluorozirconic acid (H 2 ZrF 6 ) and characterized after different immersion times with SKPFM and field emission SEM (FE-SEM)/EDX techniques. A deposition mechanism of Zr-based conversion coatings on microstructural heterogeneous Zn-Al-Mg alloy surfaces was proposed

  10. Influence of Sn content on microstructural and mechanical properties of centrifugal cast Ti-Nb-Sn biomedical alloys

    International Nuclear Information System (INIS)

    Lopes, E.S.N.; Contieri, R.J.; Caram, R.; Costa, A.M.S.

    2010-01-01

    The arc voltaic centrifugal casting is an interesting alternative in terms of economic and technological development in the production of components based on materials with high reactivity and high melting point, such as titanium alloys. In this work, Ti-30Nb (wt. %) with additions of Sn (2, 4, 6, 8 and 10 wt. %) were formed by casting process. Characterization of the samples included optical microscopy, scanning electron microscopy, X-ray diffraction, Vickers hardness and elastic modulus measures by acoustic techniques. It was observed that the microstructure of the samples investigated is composed by dendritic structures, with clear segregation of alloying elements. The Vickers hardness and the elastic modulus decreased with the addition of Sn. The results show that the mechanical behavior of Ti-Nb alloys can be controlled within certain limits, by adding Sn. (author)

  11. Effect of erbium modification on the microstructure, mechanical and corrosion characteristics of binary Mg–Al alloys

    Energy Technology Data Exchange (ETDEWEB)

    Seetharaman, Sankaranarayanan, E-mail: seetharaman.s@nus.edu.sg [Department of Mechanical Engineering, National University of Singapore, 9 Engineering Drive 1, 117576 (Singapore); Blawert, Carsten [Helmholtz-Zentrum Geesthacht, Magnesium Innovation Centre, Max-Planck-Straße 1, D-21502, Geesthacht (Germany); Ng, Baoshu Milton [Department of Mechanical Engineering, National University of Singapore, 9 Engineering Drive 1, 117576 (Singapore); Wong, Wai Leong Eugene [School of Mechanical and Systems Engineering, New Castle University International Singapore, 180 Ang Mo Kio Avenue 8, 569830 (Singapore); Goh, Chwee Sim [ITE Technology Development Centre, ITE College Central, 2 Ang Mo Kio Drive, 567720 (Singapore); Hort, Norbert [Helmholtz-Zentrum Geesthacht, Magnesium Innovation Centre, Max-Planck-Straße 1, D-21502, Geesthacht (Germany); Gupta, Manoj, E-mail: mpegm@nus.edu.sg [Department of Mechanical Engineering, National University of Singapore, 9 Engineering Drive 1, 117576 (Singapore)

    2015-11-05

    In this study, new erbium modified Mg–Al alloys were developed by integrating trace erbium (in the form of Al{sub 94.67}Er{sub 5.33} master alloy) into pure Mg using disintegrated melt deposition technique. The developed Er- modified Mg–Al alloys were investigated for their microstructural, mechanical and corrosion characteristics in comparison with their unmodified counterparts. Microstructural investigation revealed (i) improved purity, (ii) (marginal) grain refinement, (iii) more uniform second phase distribution and (iv) Al{sub 3}Er phase formation due to Er modification. Mechanical property measurements revealed an overall enhancement under indentation, tension and compression loads. A remarkable improvement in tensile ductility (without adverse effects on strength) by +19%, +29%, and +58% was obtained in Mg–3Al–0.1Er, Mg–6Al–0.3Er and Mg–9Al–0.5Er when compared to Mg–3Al, Mg–6Al and Mg–9Al respectively. While the Mg–6Al–0.3Er alloy exhibited best ductility, the Mg–9Al–0.5Er has the best strength under both tension and compression loads. Corrosion characteristics evaluated by hydrogen evolution, salt spray and electrochemical impedance experiments revealed improved corrosion resistance of Er modified Mg–Al alloys by the enhanced purity levels and the formation of Al–Er phases. - Highlights: • New erbium modified Mg–Al alloys successfully synthesized using DMD method. • Erbium modification promoted Al{sub 3}Er formation and improved the purity. • Remarkable improvement in tensile ductility obtained after erbium modification. • The developed erbium modified Mg–Al alloys exhibit improved corrosion resistance.

  12. Effect of erbium modification on the microstructure, mechanical and corrosion characteristics of binary Mg–Al alloys

    International Nuclear Information System (INIS)

    Seetharaman, Sankaranarayanan; Blawert, Carsten; Ng, Baoshu Milton; Wong, Wai Leong Eugene; Goh, Chwee Sim; Hort, Norbert; Gupta, Manoj

    2015-01-01

    In this study, new erbium modified Mg–Al alloys were developed by integrating trace erbium (in the form of Al 94.67 Er 5.33 master alloy) into pure Mg using disintegrated melt deposition technique. The developed Er- modified Mg–Al alloys were investigated for their microstructural, mechanical and corrosion characteristics in comparison with their unmodified counterparts. Microstructural investigation revealed (i) improved purity, (ii) (marginal) grain refinement, (iii) more uniform second phase distribution and (iv) Al 3 Er phase formation due to Er modification. Mechanical property measurements revealed an overall enhancement under indentation, tension and compression loads. A remarkable improvement in tensile ductility (without adverse effects on strength) by +19%, +29%, and +58% was obtained in Mg–3Al–0.1Er, Mg–6Al–0.3Er and Mg–9Al–0.5Er when compared to Mg–3Al, Mg–6Al and Mg–9Al respectively. While the Mg–6Al–0.3Er alloy exhibited best ductility, the Mg–9Al–0.5Er has the best strength under both tension and compression loads. Corrosion characteristics evaluated by hydrogen evolution, salt spray and electrochemical impedance experiments revealed improved corrosion resistance of Er modified Mg–Al alloys by the enhanced purity levels and the formation of Al–Er phases. - Highlights: • New erbium modified Mg–Al alloys successfully synthesized using DMD method. • Erbium modification promoted Al 3 Er formation and improved the purity. • Remarkable improvement in tensile ductility obtained after erbium modification. • The developed erbium modified Mg–Al alloys exhibit improved corrosion resistance

  13. Phase Evolution and Mechanical Properties of AlCoCrFeNiSi x High-Entropy Alloys Synthesized by Mechanical Alloying and Spark Plasma Sintering

    Science.gov (United States)

    Kumar, Anil; Swarnakar, Akhilesh Kumar; Chopkar, Manoj

    2018-05-01

    In the current investigation, AlCoCrFeNiSi x (x = 0, 0.3, 0.6 and 0.9 in atomic ratio) high-entropy alloy systems are prepared by mechanical alloying and subsequently consolidated by spark plasma sintering. The microstructural and mechanical properties were analyzed to understand the effect of Si addition in AlCoCrFeNi alloy. The x-ray diffraction analysis reveals the supersaturated solid solution of the body-centered cubic structure after 20 h of ball milling. However, the consolidation promotes the transformation of body-centered phases partially into the face-centered cubic structure and sigma phases. A recently proposed geometric model based on the atomic stress theory has been extended for the first time to classify single phase and multi-phases on the high-entropy alloys prepared by mechanical alloying and spark plasma sintering process. Improved microhardness and better wear resistance were achieved as the Si content increased from 0 to 0.9 in the present high-entropy alloy.

  14. Characterization of low alloy ferritic steel–Ni base alloy dissimilar metal weld interface by SPM techniques, SEM/EDS, TEM/EDS and SVET

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Siyan; Ding, Jie; Ming, Hongliang; Zhang, Zhiming; Wang, Jianqiu, E-mail: wangjianqiu@imr.ac.cn

    2015-02-15

    The interface region of welded A508–Alloy 52 M is characterized by scanning probe microscope (SPM) techniques, scanning electron microscopy (SEM)/energy dispersive spectroscopy (EDS), transmission electron microscopy (TEM)/Energy Dispersive Spectroscopy (EDS) and scanning vibrate electrode technique (SVET). The regions along the welded A508–Alloy 52 M interface can be categorized into two types according to their different microstructures. In the type-I interface region, A508 and Alloy 52 M are separated by the fusion boundary, while in the type-II interface region, A508 and Alloy 52 M are separated by a martensite zone. A508, martensite zone and grain boundaries in Alloy 52 M are ferromagnetic while the Alloy 52 M matrix is paramagnetic. The Volta potentials measured by scanning Kelvin probe force microscopy (SKPFM) of A508, martensite zone and Alloy 52 M follow the order: V{sub 52} {sub M} > V{sub A508} > V{sub martensite}. The corrosion behavior of A508–Alloy 52 M interface region is galvanic corrosion, in which Alloy 52 M is cathode while A508 is anode. The martensite dissolves faster than Alloy 52 M, but slower than A508 in the test solution. - Highlights: • The A508–Alloy 52 M interface regions can be categorized into two types. • The chromium depleted region is observed along the Alloy 52 M grain boundary. • The Alloy 52 M grain boundaries which are close to the interface are ferromagnetic. • Martensite zone has lower Volta potential but higher corrosion resistance than A508.

  15. Mechanical and bio-corrosion properties of quaternary Mg–Ca–Mn–Zn alloys compared with binary Mg–Ca alloys

    International Nuclear Information System (INIS)

    Bakhsheshi-Rad, H.R.; Idris, M.H.; Abdul-Kadir, M.R.; Ourdjini, A.; Medraj, M.; Daroonparvar, M.; Hamzah, E.

    2014-01-01

    Highlights: • Quaternary alloy show better mechanical and corrosion properties than binary alloy. • Mg–2Ca–0.5Mn–2Zn alloy showed suitable mechanical properties for bone application. • The improved corrosion resistance with addition of Mn and Zn into the Mg–Ca alloy. • Formation of protective surface film Mn-containing magnesium on quaternary alloy. • Secondary phases have strong effect on micro-galvanic corrosion of Mg alloys. - Abstract: Binary Mg–xCa alloys and the quaternary Mg–Ca–Mn–xZn were studied to investigate their bio-corrosion and mechanical properties. The surface morphology of specimens was characterized by X-ray diffraction (XRD), Fourier-transformed infrared spectroscopy (FTIR), scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). The results of mechanical properties show that the yield strength (YS), ultimate tensile strength (UTS) and elongation of quaternary alloy increased significantly with the addition of zinc (Zn) up to 4 wt.%. However, further addition of Zn content beyond 4 wt.% did not improve yield strength and ultimate tensile strength. In contrast, increasing calcium (Ca) content has a deleterious effect on binary Mg–Ca alloys. Compression tests of the magnesium (Mg) alloys revealed that the compression strength of quaternary alloy was higher than that of binary alloy. However, binary Mg–Ca alloy showed higher reduction in compression strength after immersion in simulated body fluid. The bio-corrosion behaviour of the binary and quaternary Mg alloys were investigated using immersion tests and electrochemical tests. Electrochemical tests shows that the corrosion potential (E corr ) of binary Mg–2Ca significantly shifted toward nobeler direction from −1996.8 to −1616.6 mV SCE with the addition of 0.5 wt.% manganese (Mn) and 2 wt.% Zn content. However, further addition of Zn to 7 wt.% into quaternary alloy has the reverse effect. Immersion tests show that the quaternary

  16. Study of Al-Si Alloy Oxygen Saturation on Its Microstructure and Mechanical Properties

    Directory of Open Access Journals (Sweden)

    Arkady Finkelstein

    2017-07-01

    Full Text Available One of the main goals of modern materials research is obtaining different microstructures and studying their influence on the mechanical properties of metals; aluminum alloys are particularly of interest due to their advanced performance. Traditionally, their required properties are obtained by alloying process, modification, or physical influence during solidification. The present work describes a saturation of the overheated AlSi7Fe1 casting alloy by oxides using oxygen blowing approach in overheated alloy. Changes in metals’ microstructural and mechanical properties are also described in the work. An Al10SiFe intermetallic complex compound was obtained as a preferable component to Al2O3 precipitation on it, and its morphology was investigated by scanning electron microscopy. The mechanical properties of the alloy after the oxygen blowing treatment are discussed in this work.

  17. Mechanical characterization of Ti-12Mo-13Nb alloy for biomedical application hot swaged and aged

    Energy Technology Data Exchange (ETDEWEB)

    Gabriel, Sinara Borborema; Rezende, Monica Castro; Almeida, Luiz Henrique de, E-mail: sinara@metalmat.ufrj.br [Universidade Federal do Rio de Janeiro (UFRJ), Rio de Janeiro, RJ (Brazil). Departamento de Engenharia Metalurgica e de Materiais; Dille, Jean [Universite Libre de Bruxelles, Brussels (Belgium); Mei, Paulo [Universidade Estadual de Campinas (UNICAMP), Campinas, SP (Brazil). Departamento de Engenharia Mecanica; Baldan, Renato; Nunes, Carlos Angelo [Universidade de Sao Paulo (USP), Lorena, SP (Brazil). Departamento de Engenharia de Materiais

    2015-07-01

    Beta titanium alloys were developed for biomedical applications due to the combination of its mechanical properties including low elasticity modulus, high strength, fatigue resistance, good ductility and with excellent corrosion resistance. With this perspective a metastable beta titanium alloy Ti-12Mo-13Nb was developed with the replacement of both vanadium and aluminum from the traditional alloy Ti-6Al-4V. This paper presents the microstructure, mechanical properties of the Ti-12Mo-13Nb hot swaged and aged at 500 deg C for 24 h under high vacuum and then water quenched. The alloy structure was characterized by X-ray diffraction and transmission electron microscopy. Tensile tests were carried out at room temperature. The results show a microstructure consisting of a fine dispersed α phase in a β matrix and good mechanical properties including low elastic modulus. The results indicate that Ti-12Mo-13Nb alloy can be a promising alternative for biomedical application. (author)

  18. Study of Al-Si Alloy Oxygen Saturation on Its Microstructure and Mechanical Properties.

    Science.gov (United States)

    Finkelstein, Arkady; Schaefer, Arseny; Chikova, Оlga; Borodianskiy, Konstantin

    2017-07-11

    One of the main goals of modern materials research is obtaining different microstructures and studying their influence on the mechanical properties of metals; aluminum alloys are particularly of interest due to their advanced performance. Traditionally, their required properties are obtained by alloying process, modification, or physical influence during solidification. The present work describes a saturation of the overheated AlSi₇Fe₁ casting alloy by oxides using oxygen blowing approach in overheated alloy. Changes in metals' microstructural and mechanical properties are also described in the work. An Al 10 SiFe intermetallic complex compound was obtained as a preferable component to Al₂O₃ precipitation on it, and its morphology was investigated by scanning electron microscopy. The mechanical properties of the alloy after the oxygen blowing treatment are discussed in this work.

  19. Migration mechanisms of self-interstitial atoms and their clusters in Fe-Cr alloys

    International Nuclear Information System (INIS)

    Terentyev, D.; Malerba, L.

    2006-06-01

    The mobility of self-interstitial atoms (SIAs) and their clusters in pure iron and iron-chromium alloys was studied by atomic scale modelling techniques. Molecular dynamics (MD) was used to simulate thermally activated motion, i.e. diffusion, and its mechanisms whereas molecular statics was used to estimate energies of interactions of SIA and SIA clusters with Cr-impurities. It is shown that the presence of Cr atoms reduces the diffusivity of SIAs and their clusters in a non monotonic way with increasing Cr concentration. The main reason for this reduction is the presence of a long-range attractive interaction between self-interstitials in the crowdion configuration and Cr atoms. The migration mechanisms behind this effect are discussed relying on the results obtained from the MD simulations. (author)

  20. Microstructure characterization of nanocrystalline TiC synthesized by mechanical alloying

    International Nuclear Information System (INIS)

    Ghosh, B.; Pradhan, S.K.

    2010-01-01

    Nanocrystalline TiC is produced by mechanical milling the stoichiometric mixture of α-Ti and graphite powders at room temperature under argon atmosphere within 35 min of milling through a self-propagating combustion reaction. Microstructure characterization of the unmilled and ball-milled samples was done by both X-ray diffraction and electron microscopy. It reveals the fact that initially graphite layers were oriented along and in the course of milling, thin graphite layers were distributed evenly among the grain boundaries of α-Ti particles. Both α-Ti and TiC lattices contain stacking faults of different kinds. The grain size distribution obtained from the Rietveld's method and electron microscopy studies ensure that nanocrystalline TiC particles with almost uniform size (∼13 nm) can be prepared by mechanical alloying technique. The result obtained from X-ray analysis corroborates well with the microstructure characterization of nanocrystalline TiC by electron microscopy.

  1. Grain boundary sliding mechanism during high temperature deformation of AZ31 Magnesium alloy

    Energy Technology Data Exchange (ETDEWEB)

    Roodposhti, Peiman Shahbeigi, E-mail: pshahbe@ncsu.edu [North Carolina State University (United States); University of Connecticut (United States); Sarkar, Apu; Murty, Korukonda Linga [North Carolina State University (United States); Brody, Harold [University of Connecticut (United States); Scattergood, Ronald [North Carolina State University (United States)

    2016-07-04

    High temperature tensile creep tests were conducted on AZ31 Magnesium alloy at low stress range of 1–13 MPa to clarify the existence of grain boundary sliding (GBS) mechanism during creep deformation. Experimental data within the GBS regime shows the stress exponent is ~2 and the activation energy value is close to that for grain boundary diffusion. Analyses of the fracture surface of the sample revealed that the GBS provides many stress concentrated sites for diffusional cavities formation and leads to premature failure. Scanning electron microscopy images show the appearances of both ductile and brittle type fracture mechanism. X-ray diffraction line profile analysis (based on Williamson-Hall technique) shows a reduction in dislocation density due to dynamic recovery (DRV). A correlation between experimental data and Langdon's model for GBS was also demonstrated.

  2. Friction stir processing: a new grain refinement technique to achieve high strain rate superplasticity in commercial alloys

    Energy Technology Data Exchange (ETDEWEB)

    Mishra, R.S. [Missouri Univ., Rolla, MO (United States). Dept. of Metallurgical Engineering; Mahoney, M.W. [Rockwell International Corp., Thousand Oaks, CA (United States). Science Center

    2001-07-01

    Friction stir processing is a new thermo-mechanical processing technique that leads to a microstructure amenable for high strain rate superplasticity in commercial aluminum alloys. Friction stirring produces a combination of very fine grain size and high grain boundary misorientation angles. Preliminary results on a 7075 Al demonstrate high strain rate superplasticity in the temperature range of 430-510 C. For example, an elongation of >1000% was observed at 490 C and 1 x 10{sup -2} s{sup -1}. This demonstrates a new possibility to economically obtain a superplastic microstructure in commercial aluminum alloys. Based on these results, a three-step manufacturing process to fabricate complex shaped components can be envisaged: cast sheet or hot-pressed powder metallurgy sheet + friction stir processing + superplastic forging or forming. (orig.)

  3. Strengthening and elongation mechanism of Lanthanum-doped Titanium-Zirconium-Molybdenum alloy

    Energy Technology Data Exchange (ETDEWEB)

    Hu, Ping, E-mail: huping1985@126.com [School of Metallurgy Engineering, Xi’an University of Architecture and Technology, Xi’an 710055 (China); Jinduicheng Molybdenum Co., Ltd., Xi’an 710068 (China); Hu, Bo-liang; Wang, Kuai-she; Song, Rui; Yang, Fan [School of Metallurgy Engineering, Xi’an University of Architecture and Technology, Xi’an 710055 (China); Yu, Zhi-tao [Ruifulai Tungsten & Molybdenum Co., Ltd., Xi’an 721914 (China); Tan, Jiang-fei [School of Metallurgy Engineering, Xi’an University of Architecture and Technology, Xi’an 710055 (China); Cao, Wei-cheng; Liu, Dong-xin; An, Geng [Jinduicheng Molybdenum Co., Ltd., Xi’an 710068 (China); Guo, Lei [Ruifulai Tungsten & Molybdenum Co., Ltd., Xi’an 721914 (China); Yu, Hai-liang [School of Mechanical, Materials and Mechatronics Engineering, University of Wollongong, NSW 2522 (Australia)

    2016-12-15

    The microstructural contributes to understand the strengthening and elongation mechanism in Lanthanum-doped Titanium-Zirconium-Molybdenum alloy. Lanthanum oxide particles not only act as heterogeneous nucleation core, but also act as the second phase to hinder the grain growth during sintering crystallization. The molybdenum substrate formed sub-grain under the effect of second phase when the alloy rolled to plate.

  4. High Energy Metallic Mechanical Alloys for New Explosives and Incendiary Devices with Controllable Explosion Parameters

    National Research Council Canada - National Science Library

    Shtessel, Emil

    2001-01-01

    .... Sets of Al-Mg, Al-Mg-H, B-Mg, Al-B, and Ti-B mechanical alloys were prepared. X-ray diffraction, electron microscopy, and laser diffraction were used to characterize structures, morphology, and sizes of the produced alloys, respectively...

  5. Powder metallurgy preparation of Al-Cu-Fe quasicrystals using mechanical alloying and Spark Plasma Sintering

    Czech Academy of Sciences Publication Activity Database

    Novák, P.; Kubatík, Tomáš František; Vystrčil, J.; Hendrych, R.; Kříž, J.; Mlynár, J.; Vojtěch, D.

    2014-01-01

    Roč. 52, September (2014), s. 131-137 ISSN 0966-9795 Institutional support: RVO:61389021 Keywords : Nanostructure intermetallics * Ternary alloys systems * Mechanical alloying and milling * Sintering * Diffraction Subject RIV: JG - Metallurgy Impact factor: 2.131, year: 2014 http://www.sciencedirect.com/science/article/pii/S0966979514001198#

  6. Textures and mechanical behavior of Mg-3.3%Li alloy after ECAP

    International Nuclear Information System (INIS)

    Liu, T.; Wang, Y.D.; Wu, S.D.; Lin Peng, R.; Huang, C.X.; Jiang, C.B.; Li, S.X.

    2004-01-01

    The texture evolutions of the Mg-3.3%Li alloy after the equal channel angular pressing (ECAP) with two different routes have been investigated by neutron diffraction. The substantial enhancement of mechanical properties of the alloy after ECAP has been explained by the texture modifications and microstructure changes

  7. On the mechanism of dispersion hardening in molybdenum-carbide alloy systems

    International Nuclear Information System (INIS)

    Shulepov, V.I.; Yudkovskij, S.I.; Batenina, O.I. et al.

    1975-01-01

    The effect of heat treatment of the forming alloys of the Mo-Ti-C and Mo-Ti-Zr-C systems (at the temperatures below the recrystallization temperature) on the structure, distribution of carbon and mechanical properties of the alloys is studied. It is shown that the dispersion-strengthened state of the molybdenum alloys may be obtained on the account of the deformation ageing effect, rather than through the use of the standard heat-treatment procedure (hardening plus ageing). On the basis of the experimental results a theoretical explanation of strengthening of the high-alloy molybdenum-titanum-carbon system is given

  8. Synthesis Of NiCrAlC alloys by mechanical alloying; Sintese de ligas NiCrAlC por moagem de alta energia

    Energy Technology Data Exchange (ETDEWEB)

    Silva, A.K.; Pereira, J.I.; Vurobi Junior, S.; Cintho, O.M., E-mail: alissonkws@gmail.co [Universidade Estadual de Ponta Grossa (UEPG), PR (Brazil)

    2010-07-01

    The purpose of the present paper is the synthesis of nickel alloys (NiCrAlC), which has been proposed like a economic alternative to the Stellite family Co alloys using mechanical alloying, followed by sintering heat treatment of milled material. The NiCrAlC alloys consist of a chromium carbides dispersion in a Ni{sub 3}Al intermetallic matrix, that is easily synthesized by mechanical alloying. The use of mechanical alloying enables higher carbides sizes and distribution control in the matrix during sintering. We are also investigated the compaction of the processed materials by compressibility curves. The milling products were characterized by X-ray diffraction, and the end product was featured by conventional metallography and scanning electronic microscopy (SEM), that enabled the identification of desired phases, beyond microhardness test, which has been shown comparable to alloys manufactured by fusion after heat treating. (author)

  9. The microstructure and mechanical properties of a welded molybdenum alloy

    International Nuclear Information System (INIS)

    Wadsworth, J.; Morse, G.R.; Chewey, P.M.

    1983-01-01

    Wrought Ti-Zr-Mo (TZM) alloy has been welded using electron beam, laser and tungsten-inert gas welding techniques. The microstructure, tensile properties and fracture surfaces of these welded samples have been examined. Although the welds have been found to be defect free, a disparity in grain size leading to large strength differences exists between the weld and parent metal. Tensile tests have revealed that fusion zone strengths are typical of those expected for the grain size in the weld metal. However, brittle behavior is also always observed, with fracture initiating at grain boundaries and propagating by intergranular and cleavage modes. Auger electron spectroscopy analysis has eliminated oxygen or other interstitial elements as sources of grain boundary embrittlement. It is proposed that brittle behavior is a result of local high strain rates in the weld zone. These local high strain rates arise from the strength difference between the wrought parent metal and the weld metal as a result of the strong grain size dependence of TZM. It is shown that, either by reducing the strain rate of testing or by removing the grain size difference between the parent and weld metals by heat treatment, significant ductility can in fact be achieved in tensile-tested butt-welded TZM. Thus, it is proposed that TZM welds are not inherently brittle as had commonly been believed. (Auth.)

  10. Thermal Mechanical Processing Effects on Microstructure Evolution and Mechanical Properties of the Sintered Ti-22Al-25Nb Alloy.

    Science.gov (United States)

    Wang, Yuanxin; Lu, Zhen; Zhang, Kaifeng; Zhang, Dalin

    2016-03-11

    This work illustrates the effect of thermal mechanical processing parameters on the microstructure and mechanical properties of the Ti-22Al-25Nb alloy prepared by reactive sintering with element powders, consisting of O, B2 and Ti₃Al phases. Tensile and plane strain fracture toughness tests were carried out at room temperature to understand the mechanical behavior of the alloys and its correlation with the microstructural features characterized by scanning and transmission electron microscopy. The results show that the increased tensile strength (from 340 to 500 MPa) and elongation (from 3.6% to 4.2%) is due to the presence of lamellar O/B2 colony and needle-like O phase in B2 matrix in the as-processed Ti-22Al-25Nb alloys, as compared to the coarse lath O adjacent to B2 in the sintered alloys. Changes in morphologies of O phase improve the fracture toughness ( K IC ) of the sintered alloys from 7 to 15 MPa·m -1/2 . Additionally, the fracture mechanism shifts from cleavage fracture in the as-sintered alloys to quasi-cleavage fracture in the as-processed alloys.

  11. Microstructure, mechanical property, corrosion behavior, and in vitro biocompatibility of Zr-Mo alloys.

    Science.gov (United States)

    Zhou, F Y; Wang, B L; Qiu, K J; Li, L; Lin, J P; Li, H F; Zheng, Y F

    2013-02-01

    In this study, the microstructure, mechanical properties, corrosion behaviors, and in vitro biocompatibility of Zr-Mo alloys as a function of Mo content after solution treatment were systemically investigated to assess their potential use in biomedical application. The experimental results indicated that Zr-1Mo alloy mainly consisted of an acicular structure of α' phase, while ω phase formed in Zr-3Mo alloy. In Zr-5Mo alloy, retained β phase and a small amount of precipitated α phase were observed. Only the retained β phase was obtained in Zr-10Mo alloy. Zr-1Mo alloy exhibited the greatest hardness, bending strength, and modulus among all experimental Zr-Mo alloys, while β phase Zr-10Mo alloy had a low modulus. The results of electrochemical corrosion indicated that adding Mo into Zr improved its corrosion resistance which resulted in increasing the thermodynamic stability and passivity of zirconium. The cytotoxicity test suggested that the extracts of the studied Zr-Mo alloys produced no significant deleterious effect to fibroblast cells (L-929) and osteoblast cells (MG 63), indicating an excellent in vitro biocompatibility. Based on these facts, certain Zr-Mo alloys potentially suitable for different biomedical applications were proposed. Copyright © 2012 Wiley Periodicals, Inc.

  12. Alloying Behavior and Properties of FeSiBAlNiCo x High Entropy Alloys Fabricated by Mechanical Alloying and Spark Plasma Sintering

    Science.gov (United States)

    Wang, Wen; Li, Boyu; Zhai, Sicheng; Xu, Juan; Niu, Zuozhe; Xu, Jing; Wang, Yan

    2018-02-01

    In this paper, FeSiBAlNiCo x (x = 0.2, 0.8) high-entropy alloy (HEA) powders were fabricated by mechanical alloying process, and the powders milled for 140 h were sintered by spark plasma sintering (SPS) technique. The microstructures and properties of as-milled powders and as-sintered samples were investigated. The results reveal that the final milling products (140 h) of both sample powders present the fully amorphous structure. The increased Co contents obviously enhance the glass forming ability and thermal stability of amorphous HEA powders, which are reflected by the shorter formation time of fully amorphous phase and the higher onset crystallization temperature, respectively. According to coercivity, the as-milled FeSiBAlNiCo x (x = 0.2, 0.8) powders (140 h) are the semi-hard magnetic materials. FeSiBAlNiCo0.8 HEA powders possess the highest saturation magnetization and largest remanence ratio. The SPS-ed products of both bulk HEAs are composed of body-centered cubic solid solution, and FeSi and FeB intermetallic phases. They possess the high relative density above 97% and excellent microhardness exceeding 1150 HV. The as-sintered bulks undergo the remarkable increase in saturation magnetization compared with the as-milled state. The SPS-ed FeSiBAlNiCo0.8 HEA exhibits the soft magnetic properties. The electrochemical corrosion test is carried out in 3.5% NaCl solution. The SPS-ed FeSiBAlNiCo0.2 HEA reveals the better passivity with low passive current density, and the higher pitting resistance with wide passive region.

  13. Study on microstructure and strengthening mechanism of AZ91-Y magnesium alloy

    Science.gov (United States)

    Cai, Huisheng; Guo, Feng; Su, Juan; Liu, Liang; Chen, Baodong

    2018-03-01

    AZ91-Y magnesium alloy with different thicknesses were prepared by die casting process. The main existence forms of Y in alloy and the effects of Y on microstructure and mechanical properties of alloy were studied, the main reason for the change of mechanical properties and fracture mechanism were analyzed. The results show that, yttrium exists mainly in the forms of Al2Y phase and trace solid solution in α-Mg. Yttrium can refine the grain of α-Mg, reduce the amount of eutectic β-Mg17Al12 phase and promote its discrete distribution. The room temperature tensile strength and elongation of alloy increased first and then decreased with the increase of Y content. The designed alloys containing 0.6% Y (measured containing 0.63% Y) have better mechanical properties. The change of mechanical properties of alloy is a comprehensive reflection of the effect of solid solution, grain refinement and second phase. The cracking of Al2Y phase and β-Mg17Al12 phase and crack propagation through Al2Y phase and β-Mg17Al12 phase are the main fracture mechanism of magnesium alloy containing yttrium. The cooling rate does not change the trend of the influence of Y, but affects the degree of influence of Y.

  14. Structure and Mechanical Properties of Al-Li Alloys as Cast

    Directory of Open Access Journals (Sweden)

    Augustyn-Pieniążek J.

    2013-06-01

    Full Text Available The high mechanical properties of the Al-Li-X alloys contribute to their increasingly broad application in aeronautics, as an alternative for the aluminium alloys, which have been used so far. The aluminium-lithium alloys have a lower specific gravity, a higher nucleation and crack spread resistance, a higher Young’s module and they characterize in a high crack resistance at lower temperatures. The aim of the research planned in this work was to design an aluminium alloy with a content of lithium and other alloy elements. The research included the creation of a laboratorial melt, the microstructure analysis with the use of light microscopy, the application of X-ray methods to identify the phases existing in the alloy, and the microhardness test.

  15. Effect of Mo content on thermal and mechanical properties of Mo–Ru–Rh–Pd alloys

    International Nuclear Information System (INIS)

    Masahira, Yusuke; Ohishi, Yuji; Kurosaki, Ken; Muta, Hiroaki; Yamanaka, Shinsuke; Komamine, Satoshi; Fukui, Toshiki; Ochi, Eiji

    2015-01-01

    Metallic inclusions are precipitated in irradiated oxide fuels. The composition of the phases varies with the burnup and the conditions such as temperature gradients and oxygen potential of the fuel. In the present work, Mo x/(0.7+x) (Ru 0.5 Rh 0.1 Pd 0.1 ) (0.7)/(0.7+x) (x = 0, 0.05, 0.1, 0.15, 0.2, and 0.25) alloys were prepared by arc melting, followed by annealing in a high vacuum. The thermal and mechanical properties of the alloys such as elastic moduli, Debye temperature, micro-Vickers hardness, electrical resistivity, and thermal conductivity have been evaluated to elucidate the effect of Mo content on these physical properties of the alloys. The alloys with lower Mo contents show higher thermal conductivity. The thermal conductivity of the alloy with x = 0 is almost twice of that of the alloy with x = 0.25. The thermal conductivities of the alloys are dominated by electronic contribution, which has been evaluated using the Wiedemann–Franz–Lorenz relation from the electrical resistivity data. It is confirmed that the variation of the Mo contents of the alloys considerably affects the mechanical and thermal properties of the alloys

  16. Structure, mechanical properties, and grindability of dental Ti-Zr alloys.

    Science.gov (United States)

    Ho, Wen-Fu; Chen, Wei-Kai; Wu, Shih-Ching; Hsu, Hsueh-Chuan

    2008-10-01

    Structure, mechanical properties and grindability of a series of binary Ti-Zr alloys with zirconium contents ranging from 10 to 40 wt% have been investigated. Commercially pure titanium (c.p. Ti) was used as a control. Experimental results indicated that the diffraction peaks of all the Ti-Zr alloys matched those for alpha Ti. No beta-phase peaks were found. The hardness of the Ti-Zr alloys increased as the Zr contents increased, and ranged from 266 HV (Ti-10Zr) to 350 HV (Ti-40Zr). As the concentration of zirconium in the alloys increased, the strength, elastic recovery angles and hardness increased. Moreover, the elastically recoverable angle of Ti-40Zr was higher than of c.p. Ti by as much as 550%. The grindability of each metal was found to be largely dependent on the grinding conditions. The Ti-40Zr alloy had a higher grinding rate and grinding ratio than c.p. Ti at low speed. The grinding rate of the Ti-40Zr alloy at 500 m/min was about 1.8 times larger than that of c.p. Ti, and the grinding ratio was about 1.6 times larger than that of c.p. Ti. Our research suggested that the Ti-40Zr alloy has better mechanical properties, excellent elastic recovery capability and improved grindability at low grinding speed. The Ti-40Zr alloy has a great potential for use as a dental machining alloy.

  17. Microstructure and mechanical properties of Ti-Zr-Cr biomedical alloys.

    Science.gov (United States)

    Wang, Pan; Feng, Yan; Liu, Fengchao; Wu, Lihong; Guan, Shaokang

    2015-06-01

    The Ti-15Zr-xCr (0≤x≤10, wt.%) alloys were investigated to develop new biomedical materials. It was found that the phase constitutions and mechanical properties strongly depended on the Cr content. The Ti-15Zr alloy was comprised of α' phase and a small fraction of β phase was detected with adding 1wt.% Cr. With addition of 5wt.% or more, the β phase was completely retained. In addition, the ω phase was detected in the Ti-15Zr-5Cr alloy and Ti-15Zr-7Cr alloy which exhibited the highest compressive Young's modulus and the lowest ductility. On the other hand, all the Ti-15Zr-xCr alloys without ω phase exhibited high microhardness, high yield strength and superior ductility. Furthermore, the elastic energy of Ti-15Zr-10Cr alloy (5.89MJ/m(3)) with only β phase and that of Ti-15Zr-3Cr alloy (4.04MJ/m(3)) with α' phase and small fraction of β phase was higher than the elastic energy of c.p. Ti (1.25MJ/m(3)). This study demonstrated that Ti-15Zr-3Cr alloy and Ti-15Zr-10Cr alloy with superior mechanical properties are potential materials for biomedical applications. Copyright © 2015. Published by Elsevier B.V.

  18. Nanocrystalline Al-based alloys - lightweight materials with attractive mechanical properties

    International Nuclear Information System (INIS)

    Latuch, J; Cieslak, G; Dimitrov, H; Krasnowski, M; Kulik, T

    2009-01-01

    In this study, several ways of bulk nanocrystalline Al-based alloys' production by high-pressure compaction of powders were explored. The effect of chemical composition and compaction parameters on the structure, quality and mechanical properties of the bulk samples was studied. Bulk nanocrystalline Al-Mm-Ni-(Fe,Co) alloys were prepared by ball-milling of amorphous ribbons followed by consolidation. The maximum microhardness (540 HV0.1) was achieved for the samples compacted at 275 deg. C under 7.7 GPa (which resulted in an amorphous bulk) and nanocrystallised at 235 deg. C for 20 min. Another group of the produced materials were bulk nanocrystalline Al-Si-(Ni,Fe)-Mm alloys obtained by ball-milling of nanocrystalline ribbons and consolidation. The hardness of these samples achieved the value five times higher (350HV) than that of commercial 4xxx series Al alloys. Nanocrystalline Al-based alloys were also prepared by mechanical alloying followed by hot-pressing. In this group of materials, there were Al-Fe alloys containing 50-85 at.% of Al and ternary or quaternary Al-Fe-(Ti, Si, Ni, Mg, B) alloys. Microhardness of these alloys was in the range of 613 - 1235 HV0.2, depending on the composition.

  19. Evaluation of strain caused by coherent precipitates in an Al alloy using TEM techniques

    Energy Technology Data Exchange (ETDEWEB)

    Hernandez-Rivera, J.L., E-mail: jose.hernandez@cimav.edu.mx [Centro de Investigacion en Materiales Avanzados (CIMAV), Laboratorio Nacional de Nanotecnologia, Miguel de Cervantes 120, Z.C. 31109, Chihuahua (Mexico); Universidad del Valle de Mexico, Robles 600, Fraccionamiento Jacarandas, Z. C. 78220, San Luis Potosi (Mexico); Rivera, J.J. Cruz; Garay-Reyes, C.G.; Azpeitia, M. Ramos; Zuniga-Alonso, I. [Facultad de Ingenieria-Instituto de Metalurgia, Universidad Autonoma de San Luis Potosi, Sierra Leona 550, Lomas 2a seccion, Z.C. 78210, San Luis Potosi (Mexico); Martinez-Sanchez, R. [Centro de Investigacion en Materiales Avanzados (CIMAV), Laboratorio Nacional de Nanotecnologia, Miguel de Cervantes 120, Z.C. 31109, Chihuahua (Mexico)

    2012-11-15

    Elastic strains, caused by GP zones in an aged Al alloy, were determined quantitatively using two techniques: Dark Field In-line Holography (DFH) and High Resolution Transmission Electron Microscopy-Geometric Phase Analysis (HRTEM-GPA). The results obtained by both techniques showed that the elastic strain was not uniform along the precipitate-matrix interface. In some areas, it was found that strain had negligible value and this was attributed to the loss of coherence between the lattices. It is suggested that a possible explanation for this fact could be a variation in the 'vacancies pump mechanism' kinetics. To obtain a better interpretation of the experimental deformation maps, a reference GP precipitate-matrix structure was built using QSTEM software. The main advantages of DFH over HRTEM-GPA were a bigger field of view and low electron dose requirements without spatial resolution loss. Another difference found was that crystalline defects such as dislocations were evidenced by HRTEM-GPA in contrast to the result obtained by DFH. However, strain measurements were affected by mask size effect in the former. - Highlights: Black-Right-Pointing-Pointer Strain around GP precipitates was not uniform and was in a more relaxed state. Black-Right-Pointing-Pointer Strain values determined by HRTEM had more artifacts compared with holography ones. Black-Right-Pointing-Pointer Strain distribution was attributed to differences in the release of vacancies. Black-Right-Pointing-Pointer Holography showed important advantages over HRTEM regarding field of view mainly.

  20. Application of slip-band visualization technique to tensile analysis of laser-welded aluminum alloy

    Science.gov (United States)

    Muchiar, -; Yoshida, Sanichiro J.; Widiastuti, Rini; Kusnowo, A.; Takahashi, Kunimitsu; Sato, Shunichi

    1997-03-01

    Recently we have developed a new optical interferometric technique capable of visualizing slip band occurring in a deforming solid-state object. In this work we applied this technique to a tensile analysis of laser-welded aluminum plate samples, and successfully revealed stress concentration that shows strong relationships with the tensile strength and the fracture mechanism. We believe that this method is a new, convenient way to analyze the deformation characteristics of welded objects and evaluate the quality of welding. The analysis has been made for several types of aluminum alloys under various welding conditions, and has shown the following general results. When the penetration is deep, a slip band starts appearing at the fusion zone in an early stage of the elastic region of the strain-stress curve and stays there till the sample fractures at that point. When the penetration is shallow, a slip band appears only after the yield point and moves vigorously over the whole surface of the sample till a late stage of plastic deformation when the slip band stays at the fusion zone where the sample eventually fractures. When the penetration depth is medium, some intermediate situation of the above two extreme cases is observed.

  1. Novel technique for determination of alloy composition with the help of chronopotentiometry

    International Nuclear Information System (INIS)

    Rizwan, R.; Mehmood, M.

    2006-01-01

    Single phase gamma (Ni/sub 5/Zn/sub 21/) nanocrystalline zinc-nickel alloy coatings were prepared by electrodeposition in chloride bath. Cyclic voltammetry as well as reverse Chronopotentiometry was performed on platinum substrate. Both of these techniques are well known for determination of phases present in alloy in electrochemistry. A new model is introduced for determining composition of the electrodeposited alloy (Zn-Ni) with the help of Chronopotentiometry. EDX of deposits was also performed. Relative percentages of zinc and nickel determined from Chronopotentiometry were almost same to the results obtained from EDX. So by use of this model, Chronopotentiometry can be used as useful characterization technique for in-situ determination of composition during electrodeposition. X -ray diffraction was performed and it confirms the presence of single phase deposits. Current efficiency of the deposits remain above 90%. Surface compactness of deposits is verified with the help of SEM. (author)

  2. Self-brazing Mechanism of Aluminum Alloy at Medium Temperature

    Directory of Open Access Journals (Sweden)

    CHENG Fang-jie

    2018-01-01

    Full Text Available ZnCl2 and SnCl2 were added to the AlF3-CsF eutectic flux, which can be used for connecting aluminum alloy sheet by self-brazing at medium temperature. The influence of the amount of ZnCl2 and SnCl2 and the size of the T-joint area on the interface microstructure and the self-brazing joint mechanical properties was investigated. The interface microstructure, chemical compositions, defects and tensile fractography of the self-brazing joints were analyzed by metallographic microscope, scanning electron microscope and energy dispersive spectroscopy. The results show that the joints are soundly bonded when both the mass fractions of ZnCl2 and SnCl2 are about 4%; the replacement reactions between Zn2+, Sn2+ of flux and Al atoms of base metal occur during brazing, then the liquid metals of Sn and Zn appear, a great degree of Zn which has high solid solution with Al spreads rapidly to the base metal; Sn is distributed along the interface forming a low melting point metal layer with Zn and Al; the brazing of joints with small area can be realized easily; there are a lot of dimples on the fracture surface and the tensile strength of the brazing joint reaches (58±5MPa.

  3. A mechanism for the hydrogen uptake process in zirconium alloys

    International Nuclear Information System (INIS)

    Cox, B.

    1999-01-01

    Hydrogen uptake data for thin Zircaloy-2 specimens in steam at 300-400 C have been analysed to show that there is a decrease in the rate of uptake with respect to the rate of oxidation when the terminal solid solubility (TSS) of hydrogen in the metal is exceeded. In order for TSS to be reached during pre-transition oxidation a very thin 0.125 mm Zircaloy sheet was used. The specimens had been pickled initially removing all Zr 2 (Fe/Ni) particles from the initial surfaces, yet the initial hydrogen uptake rates were still much higher than for Zircaloy-4 or a binary Zr/Fe alloy that did not contain phases that dissolve readily during pickling. Cathodic polarisation at room temperature in CuSO 4 solution showed that small cracks or pores formed the cathodic sites in pre-transition oxide films. Some were at pits resulting from the initial dissolution of the Zr 2 (Fe/Ni) phase; others were not; none were at the remaining intermetallics in the original surface. These small cracks are thought to provide the ingress routes for hydrogen. A microscopic steam starvation process at the bottoms of these small cracks or pores, leading to the accumulation of hydrogen adjacent to the oxide/metal interface, and causing breakdown of the passive oxide forming at the bottom of the flaw, is thought to provide the mechanism for the hydrogen uptake process during both pre-transition and post-transition oxidation. (orig.)

  4. Mechanical properties of low alloy high phosphorus weathering steel

    Directory of Open Access Journals (Sweden)

    Jena B.K.

    2015-01-01

    Full Text Available Mechanical behaviour of two low alloy steels (G11 and G12 was studied with respect to different phosphorus contents. Tensile strength and yield strength increased while percentage elongation at fracture decreased on increasing phosphorus content. The SEM and light optical photomicrograph of low phosphorus steel (G11 revealed ferrite and pearlite microstructure. On increasing phosphorus content from 0.25 wt.% to 0.42 wt.%, the morphology of grain changed from equiaxed shape to pan-cake shape and grain size also increased. The Charpy V notch (CVN impact energy of G11 and G12 steel at room temperature was 32 J and 4 J respectively and their fractographs revealed brittle rupture with cleavage facets for both the steels. However, the fractograph of G11 steel after tensile test exhibited ductile mode of fracture with conical equiaxed dimple while that of G12 steel containing 0.42 wt. % P exhibited transgranular cleavage fracture. Based on this study, G11 steel containing 0.25 wt. % P could be explored as a candidate material for weathering application purpose where the 20°C toughness requirement is 27 J as per CSN EN10025-2:2004 specification.

  5. Reforming water to generate hydrogen using mechanical alloy

    International Nuclear Information System (INIS)

    Pena F, D. L.

    2016-01-01

    The objective of this research was to generate a hydrogen production system by means of mechanical milling, in which 0.1 g of magnesium were weighed using a volume of 300 μL for each water solvent (H_2O) and methanol (CH_3OH) in a container to start mechanical milling for 2, 4 and 6 h. Once the mechanical milling was finished, the hydrogen that was produced every two hours was measured to determine the appropriate milling time in the production, also in each period of time samples of the powders produced during the milling of Mg were taken, in this process we used characterization techniques such as: X-ray diffraction at an angle of 2θi 5 and 2θf 90 degrees and scanning electron microscopy, taking micrographs of 100, 500, 1000 and 5000 magnifications. According to the mechanical milling results hydrogen was obtained when using water, as well as with methanol. In the techniques of X-ray diffraction characterization different results were obtained before and after the milling, since by the diffractogram s is possible to observe how the magnesium to be put in the mechanical milling along with the water and methanol was diminishing to be transformed into hydroxide and magnesium oxide, as well as in the micrographs taken with scanning electron microscopy the change in the magnesium morphology to hydroxide and magnesium oxide is observed. (Author)

  6. Microstructure evaluation of Al-Al2O3 composite produced by mechanical alloying method

    International Nuclear Information System (INIS)

    Zebarjad, S.M.; Sajjadi, S.A.

    2006-01-01

    Mechanical alloying process using ball-milling techniques, has received much attention as a powerful tool for fabrication of several advanced materials, including amorphous, quasicrystals, nanocrystalline and composite materials, etc. This research is focused on production of Al-Al 2 O 3 composite materials by mechanical alloying method and on investigation of its microstructure. For this purpose a horizontal ball mill was designed and manufactured. Aluminum and alumina powders, with specified size and weight percent, were added to the mill. The mixed powders were milled at different times. The milled powders were pressed and sintered under argon gas control. Microstructure of produced composite was investigated by scanning electron microscope. The results show that increasing milling time causes to make fine alumina powders as well as uniform distribution within aluminum, also in steady-state stage increasing milling time has not significant effect on their size distribution within aluminum. The results of atomic analysis of initial and milled powders at different times show that at the beginning of milling, the powders will tend to absorb iron and gradually their susceptibility decrease until steady-state condition is prevailed. The result of infrared spectroscopy does not show any evidence of compounds except alumina

  7. Metallurgical Mechanisms Controlling Mechanical Properties of Aluminum Alloy 2219 Produced By Electron Beam Freeform Fabrication

    Science.gov (United States)

    Domack, Marcia S.; Taminger, Karen M. B.; Begley, Matthew

    2006-01-01

    The electron beam freeform fabrication (EBF3) layer-additive manufacturing process has been developed to directly fabricate complex geometry components. EBF3 introduces metal wire into a molten pool created on the surface of a substrate by a focused electron beam. Part geometry is achieved by translating the substrate with respect to the beam to build the part one layer at a time. Tensile properties have been demonstrated for electron beam deposited aluminum and titanium alloys that are comparable to wrought products, although the microstructures of the deposits exhibit features more typical of cast material. Understanding the metallurgical mechanisms controlling mechanical properties is essential to maximizing application of the EBF3 process. In the current study, mechanical properties and resulting microstructures were examined for aluminum alloy 2219 fabricated over a range of EBF3 process variables. Material performance was evaluated based on tensile properties and results were compared with properties of Al 2219 wrought products. Unique microstructures were observed within the deposited layers and at interlayer boundaries, which varied within the deposit height due to microstructural evolution associated with the complex thermal history experienced during subsequent layer deposition. Microstructures exhibited irregularly shaped grains, typically with interior dendritic structures, which were described based on overall grain size, morphology, distribution, and dendrite spacing, and were correlated with deposition parameters. Fracture features were compared with microstructural elements to define fracture paths and aid in definition of basic processing-microstructure-property correlations.

  8. A novel high-strength and highly corrosive biodegradable Fe-Pd alloy: Structural, mechanical and in vitro corrosion and cytotoxicity study.

    Science.gov (United States)

    Čapek, Jaroslav; Msallamová, Šárka; Jablonská, Eva; Lipov, Jan; Vojtěch, Dalibor

    2017-10-01

    Recently, iron-based materials have been considered as candidates for the fabrication of biodegradable load-bearing implants. Alloying with palladium has been found to be a suitable approach to enhance the insufficient corrosion rate of iron-based alloys. In this work, we have extensively compared the microstructure, the mechanical and corrosion properties, and the cytotoxicity of an FePd2 (wt%) alloy prepared by three different routes - casting, mechanical alloying and spark plasma sintering (SPS), and mechanical alloying and the space holder technique (SHT). The properties of the FePd2 (wt%) were compared with pure Fe prepared in the same processes. The preparation route significantly influenced the material properties. Materials prepared by SPS possessed the highest values of mechanical properties (CYS~750-850MPa) and higher corrosion rates than the casted materials. Materials prepared by SHT contained approximately 60% porosity; therefore, their mechanical properties reached the lowest values, and they had the highest corrosion rates, approximately 0.7-1.2mm/a. Highly porous FePd2 was tested in vitro according to the ISO 10993-5 standard using L929 cells, and two-fold diluted extracts showed acceptable cytocompatibility. In general, alloying with Pd enhanced both mechanical properties and corrosion rates and did not decrease the cytocompatibility of the studied materials. Copyright © 2017 Elsevier B.V. All rights reserved.

  9. Structure and Mechanical Properties of Powdered Quasicrystalline Al94Fe3Cr3 Alloy Consolidated by Quasi-Hydrostatic Compression

    Directory of Open Access Journals (Sweden)

    Alexandra I. Yurkova

    2017-10-01

    Full Text Available Background. Quasicrystalline Al-based alloys belong to the class of the state-of-the-art metal materials for the application in light engineering constructions, primarily in aviation and the motor transport industry. These materials are commonly made in the form of powders, which is due to the high productivity of powder metallurgy methods. Therefore, the powder consolidation methods are of great importance in the production of products, which is associated with certain difficulties, and consequently, they should be chosen considering not only the quasicrystals’ propensity to brittle fracture but also the metastable nature of the quasicrystalline phases. Certain possibilities in this direction are provided by the quasi-hydrostatic compression method, which can provide a non-trivial combination of strength and ductility properties of materials. Objective. The aim of the paper is to investigate the effect of high pressure under quasi-hydrostatic compression on the formation of structure, phase composition and mechanical properties of the quasicrystalline Al94Fe3Cr3 alloy. Methods. 40 μm Al94Fe3Cr3 alloy quasicrystalline powder was fabricated by water-atomisation technique. Consolidation of quasicrystalline powder was performed by quasi-hydrostatic compression technique in high-pressure cells at room temperature at a pressure of 2.5, 4, and 6 hPa. Structure, phase composition and mechanical characteristics of Al94Fe3Cr3 alloy were performed by scanning electron microscopy (SEM, X-ray diffraction andmicromechanical tests. Results. Using the phase X-ray analysis and SEM, the content of the quasicrystalline icosahedral phase (i-phase in the Al94Fe3Cr3 alloy structure was completely preserved after its consolidation at different pressures (2.5, 4, and 6 hPa under quasi-hydrostatic compression at room temperature. Despite the high pressure applied in the consolidation process, the morphology of quasicrystalline phase particles located in the a

  10. Mechanical properties and grindability of dental cast Ti-Nb alloys.

    Science.gov (United States)

    Kikuchi, Masafumi; Takahashi, Masatoshi; Okuno, Osamu

    2003-09-01

    Aiming at developing a dental titanium alloy with better mechanical properties and machinability than unalloyed titanium, a series of Ti-Nb alloys with Nb concentrations up to 30% was made. They were cast into magnesia-based molds using a dental casting machine and the mechanical properties and grindability of the castings were examined. The hardness of the alloys with Nb concentrations of 5% and above was significantly higher than that of titanium. The yield strength and tensile strength of the alloys with Nb concentrations of 10% and above were significantly higher than those of titanium, while the elongation was significantly lower. A small addition of niobium to titanium did not contribute to improving the grindability of titanium. The Ti-30% Nb alloy exhibited significantly better grindability at low grinding speed with higher hardness, strength, and Young's modulus than titanium, presumably due to precipitation of the omega phase in the beta matrix.

  11. Microstructure, mechanical behavior and biocompatibility of powder metallurgy Nb-Ti-Ta alloys as biomedical material.

    Science.gov (United States)

    Liu, Jue; Chang, Lin; Liu, Hairong; Li, Yongsheng; Yang, Hailin; Ruan, Jianming

    2017-02-01

    Microstructures, mechanical properties, apatite-forming ability and in vitro experiments were studied for Nb-25Ti-xTa (x=10, 15, 20, 25, 35at.%) alloys fabricated by powder metallurgy. It is confirmed that the alloys could achieve a relative density over 80%. Meanwhile, the increase in Ta content enhances the tensile strength, elastic modulus and hardness of the as-sintered alloys. When increasing the sintering temperatures, the microstructure became more homogeneous for β phase, resulting in a decrease in the modulus and strength. Moreover, the alloys showed a good biocompatibility due to the absence of cytotoxic elements, and were suitable for apatite formation and cell adhesion. In conclusion, Nb-25Ti-xTa alloys are potentially useful in biomedical applications with their mechanical and biological properties being evaluated in this work. Copyright © 2016 Elsevier B.V. All rights reserved.

  12. Development of laser welding techniques for vanadium alloys

    International Nuclear Information System (INIS)

    Strain, R.V.; Leong, K.H.; Smith, D.L.

    1996-01-01

    Laser welding is potentially advantageous because of its flexibility and the reduced amount of material affected by the weld. Bead-on-plate and butt welds were previously performed to depths of about 4 mm with a 6-kW CO 2 laser on V-4%Cr-4%Ti and V-5%Cr-5%Ti alloys. These welds were made at a speed of 0.042 m/s using argon purging at a flow rate of 2.8 m 3 /s. The purge was distributed with a diffuser nozzle aimed just behind the laser beam during the welding operation. The fusion zones of welds made under these conditions consisted of very fine, needle-shaped grains and were also harder than the bulk metal (230-270 dph, compared to ∼180 dph for the bulk metal). A limited number of impact tests showed that the as-welded ductile-brittle transition temperatures (DBTT) was above room temperature, but heat treatment at 1000 degrees C for 1 h in vacuum reduced the DBTT to <-25 degrees C. Activities during this reporting period focused on improvements in the purging system and determination of the effect of welding speed on welds. A 2-kW continuous YAG laser at Lumonics Corp. in Livonia, MI, was used to make 34 test welds for this study

  13. Mechanism of magnetic recovery in the disorder-order transformation of Fe70Al30 mechanically deformed alloys

    International Nuclear Information System (INIS)

    Rodriguez, D. Martin; Apinaniz, E.; Plazaola, F.; Garitaonandia, J.S.; Jimenez, J.A.; Schmool, D.S.; Cuello, G.J.

    2005-01-01

    The degree of order in Fe-Al intermetallic alloys has an important influence on their magnetic properties. Moreover, the deformation of ordered alloys causes a dramatic increase of magnetization. If deformed alloys are heated, their magnetic properties decrease again. The reordering process was monitored by neutron diffraction, Moessbauer spectroscopy, and calorimetric measurements on the Fe 70 Al 30 crushed alloy. This indicates that the reordering process occurs in two stages. In the first (150-200 deg. C) new small B2 phase domains are nucleated due to vacancy migration. A second reordering stage occurs between 300 and 450 deg. C, where dislocation motion induces B2 domain growth and A2 phase elimination. The main mechanism responsible for this decrease of magnetization during the reordering process is the decrease of the disordered A2 phase content in the alloy

  14. Structure and magnetic properties of nanostructured MnNi alloys fabricated by mechanical alloying and annealing treatments

    Science.gov (United States)

    Jalal, T.; Hossein Nedjad, S.; Khalili Molan, S.

    2013-05-01

    A nearly equiatomic MnNi alloy was fabricated from the elemental powders by means of mechanical alloying in a planetary ball milling apparatus. X-ray diffraction (XRD), scanning electron microscopy (SEM), differential scanning calorimetry (DSC), and measurements of magnetization were conducted to identify the structural states and properties of the prepared alloys. After ball milling for 20 h, a disordered face-centered cubic (f.c.c.) solid solution was formed which increased in lattice parameter by further milling up to 50 h. An exothermic reaction took place at around 300-400°C during continuous heating of the disordered f.c.c. solid solution. This reaction is attributed to a structural ordering leading to the formation of a face-centered tetragonal (f.c.t.) phase with L10 type ordering. Examination of the magnetic properties indicated that the structural ordering increases remnant magnetization and decreases coerecivity.

  15. Modification mechanism of eutectic silicon in Al–6Si–0.3Mg alloy with scandium

    Energy Technology Data Exchange (ETDEWEB)

    Patakham, Ussadawut [Manufacturing and Systems Engineering Program, Department of Production Engineering, Faculty of Engineering, King Mongkut’s University of Technology Thonburi, 126 Pracha-Utid Rd., Bangmod, Tungkhru, Bangkok 10140 (Thailand); Kajornchaiyakul, Julathep [National Metal and Material Technology Center, National Science and Technology Development Agency, 114 Thailand Science Park, Klong Nueng, Klong Luang, Pathumthani 12120 (Thailand); Limmaneevichitr, Chaowalit, E-mail: chaowalit.lim@kmutt.ac.th [Manufacturing and Systems Engineering Program, Department of Production Engineering, Faculty of Engineering, King Mongkut’s University of Technology Thonburi, 126 Pracha-Utid Rd., Bangmod, Tungkhru, Bangkok 10140 (Thailand)

    2013-10-25

    Highlights: •Morphologies and growth of Sc and Sr-modified eutectic silicon resemble those of dendrites. •Crystal orientation of eutectic aluminum depends on growth characteristics of eutectic silicon. •We report strong evidence of the occurrence of an impurity-induced twinning mechanism. -- Abstract: The modification mechanism of eutectic silicon in Al–6Si–0.3Mg alloy with scandium was studied. The crystallographic orientation relationships between primary dendrites and the eutectic phase of unmodified and modified Al–6Si–0.3 Mg alloys were determined using electron backscatter diffraction (EBSD). The orientation of aluminum modified with scandium in the eutectic phase was different from that of the neighboring primary dendrites. This result implies that eutectic aluminum grows epitaxially from the surrounding primary aluminum dendrites in the unmodified alloy and that eutectic aluminum grows competitively from the surrounding primary aluminum dendrites in the modified alloy. The pole figure maps of eutectic Si in the [1 0 0], [1 1 0] and [1 1 1] axes of the unmodified and Sc-modified alloys were different, suggesting that the eutectic Al and Si crystals in modified alloy growth are more isotropic and cover a larger set of directions. The lattice fringes of Si of the alloys with and without Sc modification were different in the TEM results. The lattice fringes of Si in modified alloy were found to be multiple twins. However, this was not observed in the unmodified alloy. The growth characteristic of eutectic Si crystal in modified alloy suggests the occurrence of multiple twinning reactions and the formation of a high density of twins. This modification mechanism by Sc is explained by the results of scanning electron microscopy (SEM), electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) analysis, which provide strong evidence of the occurrence of the impurity-induced twinning (IIT) mechanism.

  16. Modeling mechanical properties of cast aluminum alloy using artificial neural network

    International Nuclear Information System (INIS)

    Jokhio, M.H.; Panhwar, M.I.

    2009-01-01

    Modeling is widely used to investigate the mechanical properties of engineering materials due to increasing demand of low cost and high strength to weight ratio for many engineering applications. The aluminum casting alloys are cost competitive material and possess the desired properties. The mechanical properties largely depend upon composition of alloys and their processing method. Alloy design involves controlling mechanical properties via optimization of the composition and processing parameters. For optimization the possible root is empirical modeling and its more refined version is the analysis of the wide range of data using ANN (Artificial Neural Networks) modeling. The modeling of mechanical properties of the aluminum alloys are the main objective of present work. For this purpose, some data were collected and experimentally prepared using conventional casting method. A MLP (Multilayer Perceptron) network was developed, which is trained by using the error back propagation algorithm. (author)

  17. In-situ electron microscopy studies on the tensile deformation mechanisms in aluminium 5083 alloy

    CSIR Research Space (South Africa)

    Motsi, G

    2014-10-01

    Full Text Available In this study tensile deformation mechanisms of aluminium alloy 5083 were investigated under observations made from SEM equipped with a tensile stage. Observations during tensile testing revealed a sequence of surface deformation events...

  18. Effects of Yb on the mechanical properties and microstructures of an Al-Mg alloy

    International Nuclear Information System (INIS)

    Song Min; Wu Zhenggang; He Yuehui

    2008-01-01

    This paper reported a first study of the effects of Yb on the microstructures and mechanical properties of an extruded Al-Mg alloy. It has been shown that the addition of 0.3 wt.% Yb decreases the mechanical properties of the alloy since Mg- and Yb-containing constituents decrease the concentration of Mg solute atoms in Al matrix, and thus the solution strengthening effect. However, the addition of 1 wt.% Yb substantially improves the mechanical behavior of the alloy because the concentration of Yb solute atoms in Al matrix is high enough to generate solution strengthening effect. The improvement in the mechanical properties is due to the large work-hardening and high dislocation density caused by the interaction between dislocations and Yb and Mg solute atoms. The Yb and Mg atoms inhibit the dynamic recovery and recrystallization of the alloy, thus provide a uniformly distributed dislocation structure with high density

  19. Time evolution of morphology in mechanically alloyed Fe-Cu

    KAUST Repository

    Wille, Catharina Gabriele; Al-Kassab, Talaá t; Kirchheim, Reiner

    2011-01-01

    Being widely accessible as well as already utilised in many applications, Fe-Cu acts as an ideal binary model alloy to elaborate the enforced nonequilibrium enhanced solubility in such a solution system that shows a limited regime of miscibility

  20. Enhancement of magnetic properties of Co{sub 2}MnSi Heusler alloy prepared by mechanical alloying method

    Energy Technology Data Exchange (ETDEWEB)

    Rabie, Naeemeh; Gordani, Gholam Reza; Ghasemi, Ali, E-mail: ali13912001@yahoo.com

    2017-07-15

    Highlights: • Ferromagnetic Heusler alloys of Co{sub 2}MnSi were synthesized at low temperature. • There is an at least 30% reduction in the phase formation temperature. • Saturation magnetization of alloy was increased significantly after annealing. - Abstract: Ferromagnetic Heusler alloys of Co{sub 2}MnSi were synthesized by mechanical alloying method at low temperature. The effect of milling time and annealing process on structural and magnetic properties of ferromagnetic alloy samples were studied by X-ray diffraction, scanning electron microscopy and vibration sample magnetometer methods, respectively. Structural characteristics such as crystallite size, phase percentage, and lattice parameter determined using the Rietveld method. The values of these parameters were obtained 362.9 nm, 5.699 Å and 98.7%, respectively for annealed sample. Magnetization studies show that the Co2MnSi phase is formed at 15 h of milling and is optimized after 20 h of milling. VSM results showed that saturation magnetization (M{sub s}) of milled samples reduces from 112 to 75 (emu/g) with increasing milling time and then increased gradually to 95 emu/g. The effect of post-annealing on the structural and magnetic properties of milled samples was also investigated. The saturation magnetization of annealed sample (120 emu/g) is higher than the optimum milled sample (95 emu/g) due to increasing preferential ordered L2{sub 1} structure.

  1. Enhancement of magnetic properties of Co2MnSi Heusler alloy prepared by mechanical alloying method

    International Nuclear Information System (INIS)

    Rabie, Naeemeh; Gordani, Gholam Reza; Ghasemi, Ali

    2017-01-01

    Highlights: • Ferromagnetic Heusler alloys of Co 2 MnSi were synthesized at low temperature. • There is an at least 30% reduction in the phase formation temperature. • Saturation magnetization of alloy was increased significantly after annealing. - Abstract: Ferromagnetic Heusler alloys of Co 2 MnSi were synthesized by mechanical alloying method at low temperature. The effect of milling time and annealing process on structural and magnetic properties of ferromagnetic alloy samples were studied by X-ray diffraction, scanning electron microscopy and vibration sample magnetometer methods, respectively. Structural characteristics such as crystallite size, phase percentage, and lattice parameter determined using the Rietveld method. The values of these parameters were obtained 362.9 nm, 5.699 Å and 98.7%, respectively for annealed sample. Magnetization studies show that the Co2MnSi phase is formed at 15 h of milling and is optimized after 20 h of milling. VSM results showed that saturation magnetization (M s ) of milled samples reduces from 112 to 75 (emu/g) with increasing milling time and then increased gradually to 95 emu/g. The effect of post-annealing on the structural and magnetic properties of milled samples was also investigated. The saturation magnetization of annealed sample (120 emu/g) is higher than the optimum milled sample (95 emu/g) due to increasing preferential ordered L2 1 structure.

  2. Structural characteristics and elevated temperature mechanical properties of AJ62 Mg alloy

    Energy Technology Data Exchange (ETDEWEB)

    Kubásek, J., E-mail: Jiri.Kubasek@vscht.cz; Vojtěch, D.; Martínek, M.

    2013-12-15

    Structure and mechanical properties of the novel casting AJ62 (Mg–6Al–2Sr) alloy developed for elevated temperature applications were studied. The AJ62 alloy was compared to commercial casting AZ91 (Mg–9Al–1Zn) and WE43 (Mg–4Y–3RE) alloys. The structure was examined by scanning electron microscopy, x-ray diffraction and energy dispersive spectrometry. Mechanical properties were characterized by Viskers hardness measurements in the as-cast state and after a long-term heat treatment at 250 °C/150 hours. Compressive mechanical tests were also carried out both at room and elevated temperatures. Compressive creep tests were conducted at a temperature of 250 °C and compressive stresses of 60, 100 and 140 MPa. The structure of the AJ62 alloy consisted of primary α-Mg dendrites and interdendritic nework of the Al{sub 4}Sr and massive Al{sub 3}Mg{sub 13}Sr phases. By increasing the cooling rate during solidification from 10 and 120 K/s the average dendrite arm thickness decreased from 18 to 5 μm and the total volume fraction of the interdendritic phases from 20% to 30%. Both factors slightly increased hardness and compressive strength. The room temperature compressive strength and hardness of the alloy solidified at 30 K/s were 298 MPa and 50 HV 5, i.e. similar to those of the as-cast WE43 alloy and lower than those of the AZ91 alloy. At 250 °C the compressive strength of the AJ62 alloy decreased by 50 MPa, whereas those of the AZ91 and WE43 alloys by 100 and 20 MPa, respectively. The creep rate of the AJ62 alloy was higher than that of the WE43 alloy, but significantly lower in comparison with the AZ91 alloy. Different thermal stabilities of the alloys were discussed and related to structural changes during elevated temperature expositions. - Highlights: • Small effect of cooling rate on the compressive strength and hardness of AJ 62 • A bit lower compressive strength of AJ 62 compared to AZ91 at room temperature • Higher resistance of the AJ 62

  3. Microstructural evolution of Ni40Zr60 alloy during early stage of mechanical alloying of intermetallic compounds NiZr2 and Ni11Zr9

    International Nuclear Information System (INIS)

    Lee Peeyew; Koch, C.C.

    1994-01-01

    The microstructural change of Ni 40 Zr 60 alloy during mechanical alloying of mixtures of the intermetallic compounds NiZr 2 and Ni 11 Zr 9 has been studied by transmission electron microscopy. A specific ''cauliflower'' phase was formed during early stage of mechanical alloying process. It is suggested that the solid state reaction between intermetallic compounds NiZr 2 and Ni 11 Zr 9 is not the only origin for the formation of the ''cauliflower'' phase. ((orig.))

  4. Mechanical properties and thermal stability of Al–Fe–Ni alloys prepared by centrifugal atomisation and hot extrusion

    Energy Technology Data Exchange (ETDEWEB)

    Průša, F., E-mail: Filip.Prusa@vscht.cz; Vojtěch, D.; Michalcová, A.; Marek, I.

    2014-05-01

    In this work, Al–12Fe and Al–7Fe–5Ni (wt%) alloys prepared by a novel technique including centrifugal atomisation and hot extrusion were studied. The microstructures were investigated using light microscopy, electron scanning microscopy, transmission electron microscopy and X-ray diffraction. The mechanical properties were determined by Vickers hardness measurements and compressive stress–strain tests. To study the thermal stability, the mechanical properties were also measured after 100 h of annealing at 300 °C and 400 °C. In addition, creep tests at a stress of 120 MPa and a temperature of 300 °C were performed. The investigated materials were composed of fine-grained α-Al and intermetallic phases identified as Al{sub 13}Fe{sub 4} and Al{sub 9}FeNi. The Vickers hardness and compressive yield strength were 68 HV5 and 183 MPa, respectively, for the Al–12Fe alloy and 73 HV5 and 226 MPa, respectively, for the Al–7Fe–5Ni alloy. After long-term annealing, the change in the mechanical properties was negligible, indicating the excellent thermal stability of both materials. The creep tests confirmed the highest thermal stability of the Al–7Fe–5Ni alloy with a total compressive creep strain of 15%. The “thermally stable” casting Al–12Si–1Cu–1Mg–1Ni alloy treated by the T6 regime was used as a reference material. The casting alloy exhibited sufficient mechanical properties (hardness and compressive yield strength) at room temperature. However, annealing remarkably softened and reduced its compressive yield strength to almost 50% of the initial values. Additionally, the total creep strain of the casting reference material was almost three times higher than that of the Al–7Fe–5Ni alloy. It has been proven that centrifugally atomised materials quickly compacted via hot extrusion can compete or even exceed the properties of common casting aluminium alloys that are used in automotive industry.

  5. Mechanical properties of aluminium-uranium alloy and aluminium commercially pure at several temperatures

    International Nuclear Information System (INIS)

    Quadros, N.F. de.

    1976-01-01

    The mechanical properties of Ai-U (18,4 wt %) alloy with and without heat treatment were determined, and they were compared with the mechanical properties of aluminum alloy of commercial purity, AI-1100, at tempiratures of 25, 500, 550 and 600 0 C, the changes of both the yield point stress and the ultimate tensile strength as a function of temperature may be described through two emperical relationships. A fractography study was also made [pt

  6. Structure and Mechanical Properties of Al-Cu-Fe-X Alloys with Excellent Thermal Stability

    OpenAIRE

    Školáková, Andrea; Novák, Pavel; Mejzlíková, Lucie; Průša, Filip; Salvetr, Pavel; Vojtěch, Dalibor

    2017-01-01

    In this work, the structure and mechanical properties of innovative Al-Cu-Fe based alloys were studied. We focused on preparation and characterization of rapidly solidified and hot extruded Al-Cu-Fe, Al-Cu-Fe-Ni and Al-Cu-Fe-Cr alloys. The content of transition metals affects mechanical properties and structure. For this reason, microstructure, phase composition, hardness and thermal stability have been investigated in this study. The results showed exceptional thermal stability of these allo...

  7. Microstructure and mechanical properties of AC AlSi9CuX alloys

    OpenAIRE

    L.A. Dobrzański; R. Maniara; M. Krupiński; J.H. Sokołowski

    2007-01-01

    Purpose: In order to gain a better understanding of how to control the as-cast microstructure, it is important to understand the evaluation of microstructure during solidification and understanding how influence the changes of chemical concentration on this microstructure and mechanical properties. In this research, the effect of Cu content on the microstructure and mechanical properties of AC AlSi9CuX series alloys has been investigated.Design/methodology/approach: The experimental alloy ...

  8. Investigation of the mechanism of mercury removal from a silver dental amalgam alloy

    Directory of Open Access Journals (Sweden)

    M. DJURDJEVIC

    2004-12-01

    Full Text Available An investigation of silver dental amalgam decomposition and the mercury removal mechanism was performed. The decomposition process was analysed during thermal treatment in the temperature interval from 400 °C to 850 °C and for times from 0.5 to 7.5 h. The chemical compositions of the silver dental amalgam alloy and the treated alloy were tested and microstructure analysis using optical and scanning electron microscopy was carried out. The phases were identified using energy disperse electron probe microanalysis. A mechanism for the mercury removal process from silver dental amalgam alloy is suggested.

  9. In vitro and in vivo corrosion, cytocompatibility and mechanical properties of biodegradable Mg-Y-Ca-Zr alloys as implant materials.

    Science.gov (United States)

    Chou, Da-Tren; Hong, Daeho; Saha, Partha; Ferrero, Jordan; Lee, Boeun; Tan, Zongqing; Dong, Zhongyun; Kumta, Prashant N

    2013-11-01

    This study introduces a class of biodegradable Mg-Y-Ca-Zr alloys novel to biological applications and presents evaluations for orthopedic and craniofacial implant applications. Mg-Y-Ca-Zr alloys were processed using conventional melting and casting techniques. The effects of increasing Y content from 1 to 4 wt.% as well as the effects of T4 solution treatment were assessed. Basic material phase characterization was conducted using X-ray diffraction, optical microscopy and scanning electron microscopy. Compressive and tensile tests allowed for the comparison of mechanical properties of the as-cast and T4-treated Mg-Y-Ca-Zr alloys to pure Mg and as-drawn AZ31. Potentiodynamic polarization tests and mass loss immersion tests were used to evaluate the corrosion behavior of the alloys. In vitro cytocompatibility tests on MC3T3-E1 pre-osteoblast cells were also conducted. Finally, alloy pellets were implanted into murine subcutaneous tissue to observe in vivo corrosion as well as local host response through H&E staining. SEM/EDS analysis showed that secondary phase intermetallics rich in yttrium were observed along the grain boundaries, with the T4 solution treatment diffusing the secondary phases into the matrix while increasing the grain size. The alloys demonstrated marked improvement in mechanical properties over pure Mg. Increasing the Y content contributed to improved corrosion resistance, while solution-treated alloys resulted in lower strength and compressive strain compared to as-cast alloys. The Mg-Y-Ca-Zr alloys demonstrated excellent in vitro cytocompatibility and normal in vivo host response. The mechanical, corrosion and biological evaluations performed in this study demonstrated that Mg-Y-Ca-Zr alloys, especially with the 4 wt.% Y content, would perform well as orthopedic and craniofacial implant biomaterials. Copyright © 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  10. Microstructures and formation mechanism of W–Cu composite coatings on copper substrate prepared by mechanical alloying method

    International Nuclear Information System (INIS)

    Meng, Yunfei; Shen, Yifu; Chen, Cheng; Li, Yongcan; Feng, Xiaomei

    2013-01-01

    In the present work, high-energy mechanical alloying (MA) method was applied to prepare tungsten–copper composite coatings on pure copper surface using a planetary ball mill. During mechanical alloying process, grains on the surface layer of substrate were refined and the substrate surface was activated as a result of repeated collisions by a large number of flying balls along with powder particles. The repeated ball-to-substrate collisions resulted in the deposition of coatings. The microstructures and elemental and phase composition of mechanically alloyed coatings at different milling durations during mechanical alloying process were studied using scanning electron microscopy (SEM), X-ray diffraction (XRD), energy dispersive X-ray spectroscopy (EDS). Microhardness tests were carried out to examine the mechanical properties of the coatings. The results showed that the coatings and the substrates were well bonded, and with the increase of the milling duration, multi-layered coatings with different structures were generated and the coatings became denser. The microhardness tests showed that the maximum microhardness of the coatings reached HV 0.1 228, showing a threefold improvement upon the substrate. And the cross-sectional microhardness values of the processed sample changed gradually, which gave a proof for the cushioning and sustaining functions of the multi-layered coatings. A reasonable formation mechanism of coatings on bulk materials with metallic immiscible system by mechanical alloying method was presented.

  11. Experimental simulation techniques for the evaluation of structural changes in metals and alloys

    International Nuclear Information System (INIS)

    Lucki, Georgi

    1992-01-01

    In this work, high-doses irradiation in nuclear reactor were simulated using a cyclotron in order to study mechanical, electric, magnetic and structural changes in materials. Results of such simulations for portland cement, binary alloys and stainless steels are presented and discussed. 15 refs., 11 figs., 1 tab

  12. Mechanical properties of friction stir welded aluminum alloys 5083 and 5383

    Directory of Open Access Journals (Sweden)

    Jeom Kee Paik

    2009-09-01

    Full Text Available The use of high-strength aluminum alloys is increasing in shipbuilding industry, particularly for the design and construction of war ships, littoral surface craft and combat ships, and fast passenger ships. While various welding methods are used today to fabricate aluminum ship structures, namely gas metallic arc welding (GMAW, laser welding and friction stir welding (FSW, FSW technology has been recognized to have many advantages for the construction of aluminum structures, as it is a low-cost welding process. In the present study, mechanical properties of friction stir welded aluminum alloys are examined experimentally. Tensile testing is undertaken on dog-bone type test specimen for aluminum alloys 5083 and 5383. The test specimen includes friction stir welded material between identical alloys and also dissimilar alloys, as well as unwelded (base alloys. Mechanical properties of fusion welded aluminum alloys are also tested and compared with those of friction stir welded alloys. The insights developed from the present study are documented together with details of the test database. Part of the present study was obtained from the Ship Structure Committee project SR-1454 (Paik, 2009, jointly funded by its member agencies.

  13. Effect of strontium on the texture and mechanical properties of extruded Mg–1%Mn alloys

    International Nuclear Information System (INIS)

    Borkar, Hemant; Hoseini, Majid; Pekguleryuz, Mihriban

    2012-01-01

    Highlights: ► Mg–1%Mn and Mg–1%Mn–(0.3–2)Sr alloys were extruded at elevated temperature. ► Strontium additions refine extruded microstructure of M1 alloys. ► Sr additions weaken the basal texture of extruded M1, improve the ductility and reduce the yield asymmetry. ► Texture weakening with increasing strontium additions is the result of particle stimulated nucleation (PSN). - Abstract: Magnesium–manganese, M1, alloy is preferred for extrusion applications due to its extrudability. It is mainly used as a sacrificial anode or as a creep resistant alloy at elevated temperatures in the nuclear industry. Since Mn does not provide a significant strengthening effect, the alloy is not considered for structural applications. The basal texture which forms after extrusion orients the basal planes parallel to the extrusion direction causing anisotropy in mechanical properties. This basal texture, as well as the low strength of the alloy are the main challenges in its widespread applications. In this study, the effect of Sr addition on the texture and mechanical properties of M1 alloy was studied. M1–Sr alloys showed weakened texture by developing random texture components during extrusion. The texture randomisation is attributed to particle stimulated nucleation (PSN) around Mg–Sr intermetallics during recrystallisation. M1–Sr compositions are found to show improved strength and ductility as well as reduced yield asymmetry.

  14. Influence of melting and filtration processes on the structure and mechanical properties of aluminum alloys

    Directory of Open Access Journals (Sweden)

    M. Dudyk

    2008-10-01

    Full Text Available In the article are presented the results of the study on the applied upgrading processes such as refining, modification and filtration of thenear eutectics alloy EN AC- 44000, AlSi11, (AK11, cast into the chill. The upgrading processes applied to the said alloy caused, incomparison to the alloy which was not upgraded, significant differences in the shape of the crystallization curves, obtained in the graphicrecord of the ATD-AED method. It was demonstrated the existence of connections between the thermal and electric phenomena duringsolidification and crystallization of the studied silumin. The obtained results of the metallographic analysis showed the occurrence of theimpurities within the alloy structure in the form of porosity and oxides following the metallurgical processing (in pig sows. The primarystudies on microstructure of the cast ceramic filters have demonstrated the purposefulness of introduction of the filtration process to thetechnology of aluminum alloys manufacturing. The microstructures of the filters cast with the studied alloys illustrate the extent anddeployment of the impurities retained (in the filter during the process of samples casting for measurement of the mechanical strengthproperties. On the example of the near eutectics alloy AK11, it has been demonstrated, that in comparison to the refined alloy there isa possibility to obtain significant improvement of mechanical properties, and especially elongation A5 and impact strength KCV.

  15. Microstructures and mechanical properties of age-formed 7050 aluminum alloy

    International Nuclear Information System (INIS)

    Chen, J.F.; Zhen, L.; Jiang, J.T.; Yang, L.; Shao, W.Z.; Zhang, B.Y.

    2012-01-01

    Highlights: ► Age-forming leads to the grain elongation in 7050 alloy. ► Age-forming varies the texture components in 7050 alloy. ► Age-forming promotes precipitates growth and PFZ enlargement in 7050 alloy. ► Age-forming induces to descend apparently elongation in 7050 alloy. ► The effect of age-forming on microstructure and properties is discussed in-depth. - Abstract: The effects of age-forming on microstructures and mechanical properties of 7050 Al alloy were investigated in this work. The alloy was subjected to age-forming as well as stress-free ageing at 160 °C for 6, 12, 18 and 24 h, and its microstructures were characterized by electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM). It was shown that creep might lead to grain elongation during age-forming, and the applied stress induces the coarsening of precipitates in 7050 Al alloy. The texture in the alloy was also influenced by age-forming. Consequently, the differences in microstructures result in differences in mechanical properties of age-forming versus traditional stress-free ageing. The ultimate tensile strength of age-formed samples were slightly lower than that of stress-free aged samples, while the yield strength of age-formed samples were apparently lower than that of stress-free aged samples. Specifically, the elongation of samples age-formed displays apparently decrease.

  16. Microstructural evolution and mechanical properties of Ti–Zr beta titanium alloy after laser surface remelting

    International Nuclear Information System (INIS)

    Yao, Y.; Li, X.; Wang, Y.Y.; Zhao, W.; Li, G.; Liu, R.P.

    2014-01-01

    Highlights: • The surface mechanical properties of the alloy have been greatly improved. • Its grain size was decreased from 100 μm to 10 μm. • The metastable ω with the size of 20–50 nm was observed in the alloy after LSR. • The strengthening effect is mainly due to fine microstructure and strengthened phase. -- Abstract: The effects of laser surface remelting (LSR) on the microstructural evolution and surface mechanical properties of Ti–Zr beta titanium alloy were investigated. The surfaces of the Ti–Zr alloy was re-melted using a CO 2 laser. X-ray diffraction, Scanning electron microscope, Transmission electron microscope, nanoindentation, and microhardness analyses were performed to evaluate the microstructural and mechanical properties of the alloy. The results showed that the alloy microstructure in the remelting region was greatly refined and homogeneous compared with that in the base material because of the rapid remelting and resolidifying. Meanwhile, the metastable hexagonal ω phases with the size of 20–50 nm was found and uniformly distributed throughout the β matrix after LSR. Phase transformation and microstructural refinement were the major microstructural changes in the alloys after LSR. The microhardness and elastic modulus in the remelted region clearly increased by 92.9% and 21.78%, respectively, compared with those in the region without laser processing. The strengthening effect of LSR on the mechanical properties of the Ti–Zr alloy was also addressed. Our results indicated that LSR was an effective method of improving the surface mechanical properties of alloys

  17. Synthesis of alumina-metal nanocomposites by mechanical alloying

    International Nuclear Information System (INIS)

    Osso, D.; Caer, G. le; Begin-Colin, S.; Mocellin, A.; Matteazzi, P.

    1993-01-01

    The synthesis of nanometer-sized α-Al 2 O 3 -metal composites can be performed by room temperature ball-milling of mixtures of metal-oxides and aluminium as shown by Matteazzi and Le Caer. The average crystallite size of the alumina-metal composite so obtained is in general about 10nm. Such composites may also be prepared by direct grinding of a mixture of α-Al 2 O 3 and of a metal or an alloy. The present work is devoted to the study of the reaction mechanisms by X-Ray diffraction and 57 Fe Moessbauer spectroscopy for the α-Al 2 O 3 -Cr, α-Al 2 O 3 -Fe, α-Al 2 O 3 -(Fe-Cr) and α-Al 2 O 3 -Ti systems. Moessbauer spectroscopy shows that non-completely reduced Fe, partly in the form of Fe 2+ , still exists at the end of the synthesis and belongs to a ternary Al-Fe-O oxide in α-Al 2 O 3 -Fe composites although it cannot be indexed by X-Ray diffraction. The Fe 2+ component is mainly associated with iron environments in or similar to those of hercynite. Species like Fe 3+ in Al 2 O 3 or in grain boundaries are observed, Fe 4+ and Fe 0 cannot be excluded. Differences are obtained by reactive milling and by direct milling the reaction products. Reactive milling of Al-TiO 2 (anatase) yields α-Al 2 O 3 -Ti nanocomposites. The transient formation of a high-pressure orthorhombic form of TiO 2 of the α-PbO 2 type is observed. (orig.)

  18. The mechanical properties of magnesium matrix composites reinforced with 10 wt.% W14Al86 alloy particles

    International Nuclear Information System (INIS)

    Tang, H.G.; Ma, X.F.; Zhao, W.; Cai, S.G.; Zhao, B.; Qiao, Z.H.

    2007-01-01

    The Mg-based metal matrix composite reinforced by 10 wt.% W 14 Al 86 alloy particles has been prepared by mechanical alloying and press-forming process. X-ray diffraction studies confirm the formation of the composite. Microstructure characterization of the samples reveals the uniform distribution of fine W 14 Al 86 alloy. Mechanical properties characterization revealed that the reinforcement of W 14 Al 86 alloy lead to a significant increase in hardness and tensile strength of Mg and AZ91

  19. Mitigation of wear damage by laser surface alloying technique

    CSIR Research Space (South Africa)

    Adebiyi, ID

    2016-04-01

    Full Text Available stream_source_info Adebiyi_2016.pdf.txt stream_content_type text/plain stream_size 1481 Content-Encoding UTF-8 stream_name Adebiyi_2016.pdf.txt Content-Type text/plain; charset=UTF-8 Advanced Manufacturing Techniques...

  20. Optimization of pulsed TIG welding process parameters on mechanical properties of AA 5456 Aluminum alloy weldments

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, A. [Department of Mechanical Engineering, National Institute of Technology, Warangal 506 004 (India)], E-mail: adepu_kumar7@yahoo.co.in; Sundarrajan, S. [Scientist ' G' , Defence Research and Development Laboratory, Hyderabad 500 028 (India)

    2009-04-15

    The present work pertains to the improvement of mechanical properties of AA 5456 Aluminum alloy welds through pulsed tungsten inert gas (TIG) welding process. Taguchi method was employed to optimize the pulsed TIG welding process parameters of AA 5456 Aluminum alloy welds for increasing the mechanical properties. Regression models were developed. Analysis of variance was employed to check the adequacy of the developed models. The effect of planishing on mechanical properties was also studied and observed that there was improvement in mechanical properties. Microstructures of all the welds were studied and correlated with the mechanical properties.

  1. Optimization of pulsed TIG welding process parameters on mechanical properties of AA 5456 Aluminum alloy weldments

    International Nuclear Information System (INIS)

    Kumar, A.; Sundarrajan, S.

    2009-01-01

    The present work pertains to the improvement of mechanical properties of AA 5456 Aluminum alloy welds through pulsed tungsten inert gas (TIG) welding process. Taguchi method was employed to optimize the pulsed TIG welding process parameters of AA 5456 Aluminum alloy welds for increasing the mechanical properties. Regression models were developed. Analysis of variance was employed to check the adequacy of the developed models. The effect of planishing on mechanical properties was also studied and observed that there was improvement in mechanical properties. Microstructures of all the welds were studied and correlated with the mechanical properties

  2. Development and evaluation of a magnesium-zinc-strontium alloy for biomedical applications--alloy processing, microstructure, mechanical properties, and biodegradation.

    Science.gov (United States)

    Guan, Ren-guo; Cipriano, Aaron F; Zhao, Zhan-yong; Lock, Jaclyn; Tie, Di; Zhao, Tong; Cui, Tong; Liu, Huinan

    2013-10-01

    A new biodegradable magnesium-zinc-strontium (Mg-Zn-Sr) alloy was developed and studied for medical implant applications. This first study investigated the alloy processing (casting, rolling, and heat treatment), microstructures, mechanical properties, and degradation properties in simulated body fluid (SBF). Aging treatment of the ZSr41 alloy at 175 °C for 8h improved the mechanical properties when compared to those of the as-cast alloy. Specifically, the aged ZSr41 alloy had an ultimate tensile strength of 270 MPa, Vickers hardness of 71.5 HV, and elongation at failure of 12.8%. The mechanical properties of the ZSr41 alloy were superior as compared with those of pure magnesium and met the requirements for load-bearing medical implants. Furthermore, the immersion of the ZSr41 alloy in SBF showed a degradation mode that progressed cyclically, alternating between pitting and localized corrosion. The steady-state average degradation rate of the aged ZSr41 alloy in SBF was 0.96 g/(m(2)·hr), while the pH of SBF immersion solution increased. The corrosion current density of the ZSr41 alloy in SBF solution was 0.41 mA/mm(2), which was much lower than 1.67 mA/mm(2) for pure Mg under the same conditions. In summary, compared to pure Mg, the mechanical properties of the new ZSr41 alloy improved while the degradation rate decreased due to the addition of Zn and Sr alloying elements and specific processing conditions. The superior mechanical properties and corrosion resistance of the new ZSr41 alloy make it a promising alloy for next-generation implant applications. Copyright © 2013 Elsevier B.V. All rights reserved.

  3. Pore structure and mechanical properties of directionally solidified porous aluminum alloys

    Directory of Open Access Journals (Sweden)

    Komissarchuk Olga

    2014-01-01

    Full Text Available Porous aluminum alloys produced by the metal-gas eutectic method or GASAR process need to be performed under a certain pressure of hydrogen, and to carry over melt to a tailor-made apparatus that ensures directional solidification. Hydrogen is driven out of the melt, and then the quasi-cylindrical pores normal to the solidification front are usually formed. In the research, the effects of processing parameters (saturation pressure, solidification pressure, temperature, and holding time on the pore structure and porosity of porous aluminum alloys were analyzed. The mechanical properties of Al-Mg alloys were studied by the compressive tests, and the advantages of the porous structure were indicated. By using the GASAR method, pure aluminum, Al-3wt.%Mg, Al-6wt.%Mg and Al-35wt.%Mg alloys with oriented pores have been successfully produced under processing conditions of varying gas pressure, and the relationship between the final pore structure and the solidification pressure, as well as the influences of Mg quantity on the pore size, porosity and mechanical properties of Al-Mg alloy were investigated. The results show that a higher pressure of solidification tends to yield smaller pores in aluminum and its alloys. In the case of Al-Mg alloys, it was proved that with the increasing of Mg amount, the mechanical properties of the alloys sharply deteriorate. However, since Al-3%Mg and Al-6wt.%Mg alloys are ductile metals, their porous samples have greater compressive strength than that of the dense samples due to the existence of pores. It gives the opportunity to use them in industry at the same conditions as dense alloys with savings in weight and material consumption.

  4. Mechanical and corrosion properties of newly developed biodegradable Zn-based alloys for bone fixation.

    Science.gov (United States)

    Vojtěch, D; Kubásek, J; Serák, J; Novák, P

    2011-09-01

    In the present work Zn-Mg alloys containing up to 3wt.% Mg were studied as potential biodegradable materials for medical use. The structure, mechanical properties and corrosion behavior of these alloys were investigated and compared with those of pure Mg, AZ91HP and casting Zn-Al-Cu alloys. The structures were examined by light and scanning electron microscopy (SEM), and tensile and hardness testing were used to characterize the mechanical properties of the alloys. The corrosion behavior of the materials in simulated body fluid with pH values of 5, 7 and 10 was determined by immersion tests, potentiodynamic measurements and by monitoring the pH value evolution during corrosion. The surfaces of the corroded alloys were investigated by SEM, energy-dispersive spectrometry and X-ray photoelectron spectroscopy. It was found that a maximum strength and elongation of 150MPa and 2%, respectively, were achieved at Mg contents of approximately 1wt.%. These mechanical properties are discussed in relation to the structural features of the alloys. The corrosion rates of the Zn-Mg alloys were determined to be significantly lower than those of Mg and AZ91HP alloys. The former alloys corroded at rates of the order of tens of microns per year, whereas the corrosion rates of the latter were of the order of hundreds of microns per year. Possible zinc doses and toxicity were estimated from the corrosion behavior of the zinc alloys. It was found that these doses are negligible compared with the tolerable biological daily limit of zinc. Copyright © 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  5. Electrocatalysts of platinum, cobalt and nickel prepared by mechanical alloying for the oxygen reduction reaction in H2SO4 0.5M

    International Nuclear Information System (INIS)

    Garcia C, M.A.; Fernandez V, S.M.; Vargas G, J.R.

    2007-01-01

    Metallic powders of Pt, Co and Nickel were processed by mechanical alloyed and electrocatalysts were synthesized for the oxygen reduction reaction, applicable in fuel cells. The structural and morphological characterization was carried out using X-ray Diffraction, scanning electron microscopy and transmission electron microscopy. It was found that the alloyed powders formed agglomerates that consist of crystalline particles of nano metric size. Its were obtained polarization curves by the Electrode of Rotational Disk technique in a solution of H 2 SO 4 0.5 M, used as electrolyte, to evaluate the electrocatalytic activity of mechanically alloyed powders. Tafel graphics were built to determine the kinetic parameters of each electro catalyst. The PtCoNi alloy exhibited the biggest electrocatalytic activity, with the smallest over potential for the oxygen reduction reaction. (Author)

  6. Magnesium and its alloys as degradable biomaterials: corrosion studies using potentiodynamic and EIS electrochemical techniques

    Directory of Open Access Journals (Sweden)

    Wolf Dieter Müller

    2007-03-01

    Full Text Available Magnesium is potentially useful for orthopaedic and cardiovascular applications. However, the corrosion rate of this metal is so high that its degradation occurs before the end of the healing process. In industrial media the behaviour of several magnesium alloys have been probed to be better than magnesium performance. However, the information related to their corrosion behaviour in biological media is insufficient. The aim of this work is to study the influence of the components of organic fluids on the corrosion behaviour of Mg and AZ31 and LAE442 alloys using potentiodynamic, potentiostatic and EIS techniques. Results showed localized attack in chloride containing media. The breakdown potential decreased when chloride concentration increased. The potential range of the passivation region was extended in the presence of albumin. EIS measurements showed that the corrosion behaviour of the AZ31 was very different from that of LAE442 alloy in chloride solutions.

  7. Studies of localized corrosion in welded aluminum alloys by the scanning reference electrode technique

    Science.gov (United States)

    Danford, M. D.; Nunes, A. C.

    1995-01-01

    Localized corrosion in welded samples of 2219-T87 Al alloy (2319 filler), 2090 Al-Li alloy (4043 and 2319 fillers), and 2195 Al-Li alloy (4043 and 2319 fillers) has been investigated using the relatively new scanning reference electrode technique. The weld beads are cathodic in all cases, leading to reduced anode/cathode ratios. A reduction in anode/cathode ratio leads to an increase in the corrosion rates of the welded metals, in agreement with results obtained in previous electrochemical and stress corrosion studies involving the overall corrosion rates of welded samples. The cathodic weld beads are bordered on both sides by strong anodic regions, with high propensity for corrosion.

  8. Improved mechanical performance and delayed corrosion phenomena in biodegradable Mg-Zn-Ca alloys through Pd-alloying.

    Science.gov (United States)

    González, S; Pellicer, E; Fornell, J; Blanquer, A; Barrios, L; Ibáñez, E; Solsona, P; Suriñach, S; Baró, M D; Nogués, C; Sort, J

    2012-02-01

    The influence of partial substitution of Mg by Pd on the microstructure, mechanical properties and corrosion behaviour of Mg(72-x)Zn(23)Ca(5)Pd(x) (x=0, 2 and 6 at.%) alloys, synthesized by copper mould casting, is investigated. While the Mg(72)Zn(23)Ca(5) alloy is mainly amorphous, the addition of Pd decreases the glass-forming ability, thus favouring the formation of crystalline phases. From a mechanical viewpoint, the hardness increases with the addition of Pd, from 2.71 GPa for x=0 to 3.9 GPa for x=6, mainly due to the formation of high-strength phases. In turn, the wear resistance is maximized for an intermediate Pd content (i.e., Mg(70)Zn(23)Ca(5)Pd(2)). Corrosion tests in a simulated body fluid (Hank's solution) indicate that Pd causes a shift in the corrosion potential towards more positive values, thus delaying the biodegradability of this alloy. Moreover, since the cytotoxic studies with mouse preosteoblasts do not show dead cells after culturing for 27 h, these alloys are potential candidates to be used as biomaterials. Copyright © 2011 Elsevier Ltd. All rights reserved.

  9. Microstructure evolution and mechanical properties of Ti−22Al−25Nb alloy joints brazed with Ti−Ni−Nb alloy

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Y.; Cai, X.Q.; Yang, Z.W., E-mail: tjuyangzhenwen@163.com; Qiu, Q.W.; Wang, D.P.; Liu, Y.C.

    2016-10-01

    Ti{sub 45}Ni{sub 45}Nb{sub 10} (at.%) brazing alloy, fabricated by arc melting, was successfully used to braze Ti−22Al−25Nb (at.%) alloy. The microstructures of Ti{sub 45}Ni{sub 45}Nb{sub 10} brazing alloy and Ti−22Al−25Nb alloy brazed joints were analyzed using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), electron backscatter diffraction (EBSD), and micro-area X-ray diffraction (XRD). The effects of the brazing parameters on the interfacial microstructure and mechanical properties of the Ti−22Al−25Nb alloy brazed joints were investigated. The results showed that the joint was primarily comprised of two characteristic zones: diffusion zone I and central zone II, and the reaction phases formed in the brazed joint were the B2, O, τ{sub 3}, and Ti{sub 2}Ni phase. The crystal orientation of B2 phase in diffusion zone I was consistent with that in the Ti−22Al−25Nb substrate. The O phase was precipitated from the B2 phase. As the brazing temperature or holding time increased, τ{sub 3} was gradually replaced by the B2 phase, and the Ti{sub 2}Ni phase decreased and ultimately disappeared. The maximum shear strength achieved at room temperature was 318 MPa when the joint was brazed at 1180 °C for 20 min, whereas it was 278 MPa at 650 °C. Crack primarily propagated in the τ{sub 3} compound, which was extremely hard and brittle, and partially traversed the B2 and O phases. - Highlights: • Ti{sub 45}Ni{sub 45}Nb{sub 10} alloy was successfully developed to braze Ti−22Al−25Nb alloy. • Ti−22Al−25Nb alloy was transformed from B2 phase into the O + B2 duplex phase after brazing. • Crystal orientation of B2 in joint was dependent on metal substrate. • Correlation between joint microstructure and mechanical properties was revealed. • Ti−22Al−25Nb brazed joint had excellent ambient and high temperature strength.

  10. Microstructure and mechanical properties of Mg-6Al magnesium alloy with yttrium and neodymium

    Directory of Open Access Journals (Sweden)

    Chen Jun

    2009-05-01

    Full Text Available The effects of rare earth (RE elements Y and Nd on the microstructure and mechanical properties of Mg-6Al magnesium alloy were investigated. The results show that a proper level of RE elements can obviously refi ne the microstructure of Mg-6Al magnesium alloys, reduce the quantity of β-Mg17Al12 phase and form Al2Y and Al2Nd phases. The combined addition of Y and Nd dramatically enhances the tensile strength of the alloys in the temperature range of 20-175℃. When the content of RE elements is up to 1.8%, the values of tensile strength at room temperature and at 150℃ simultaneously reach their maximum of 253 MPa and 196 MPa, respectively. The main mechanisms of enhancement in the mechanical properties of Mg-6Al alloy with Y and Nd are the grain refi ning strengthening and the dispersion strengthening.

  11. Obtention of uranium-molybdenum alloy ingots technique to avoid carbon contamination

    Energy Technology Data Exchange (ETDEWEB)

    Pedrosa, Tercio A.; Paula, Joao Bosco de; Reis, Sergio C.; Brina, Jose Giovanni M.; Faeda, Kelly Cristina M.; Ferraz, Wilmar B., E-mail: tap@cdtn.b, E-mail: jbp@cdtn.b, E-mail: jgmb@cdtn.b, E-mail: ferrazw@cdtn.b [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil)

    2011-07-01

    The replacement of high enriched uranium (U{sup 235} > 85 wt%) by low enriched uranium (U{sup 235} < 20wt%) nuclear fuels in research and test reactors is being implemented as an initiative of the Reduced Enrichment for Research and Test Reactors (RERTR) program, conceived in the USA since mid-70s, in order to avoid nuclear weapons proliferation. Such replacement implies in the use of compounds or alloys with higher uranium densities. Among the several uranium alloys investigated since then, U-Mo presents great application potential due to its physical properties and good behavior during irradiation, which makes it an important option as a nuclear fuel material for the Brazilian Multipurpose Reactor - RMB. The development of the plate-type nuclear fuel based on U-Mo alloy is being performed at the Nuclear Technology Development Centre (CDTN) and also at IPEN. The carbon contamination of the alloy is one of the great concerns during the melting process. It was observed that U-Mo alloy is more critical considering carbon contamination when using graphite crucibles. Alternative melting technique was implemented at CDTN in order to avoid carbon contamination from graphite crucible using Yttria stabilized ZrO{sub 2} crucibles. Ingots with low carbon content and good internal quality were obtained. (author)

  12. Kinetics of chloride ion adsorption on stainless alloys by in situ contact electric resistance technique

    International Nuclear Information System (INIS)

    Marichev, V.A.

    2008-01-01

    As the primary reason for pitting of stainless alloys, chloride adsorption is not adequately studied, e.g. kinetic investigations of chloride adsorption are actually absent. We discuss and partly reconsider some well-known facts (e.g. halides order: Cl - > Br - > I - ), disputed points (chloride penetration in passive film), and still unknown aspects of chloride adsorption. For the first time, we report kinetic studies of chloride adsorption on stainless alloys by in situ contact electric resistance technique. The peak-like character of kinetic curves has been found for all studied stainless alloys, but not for pure iron and nickel. This has been considered as a sequence of the substantial charge transfer during chloride adsorption. Opposite to typical d metals, stainless materials are alloys of early and late transition metals having unfilled d-bands with increased number of d-electron vacancies. Such electronic structure is favorable for adsorption of electron donating adsorbates like halide ions. Experimental data of this work are more compatible with possibility of chloride penetration into the passive films on stainless alloys that also might involve a transformation of primary oxy-hydroxide films into oxy-chloride films

  13. Composition analysis of Ta-W alloy using NAA and EDXRF techniques

    International Nuclear Information System (INIS)

    Swain, K.K.; Remya Devi, P.S.; Chavan, Trupti A.; Verma, R.; Reddy, A.V.R.

    2015-01-01

    Tantalum-Tungsten (Ta-W) alloy is a high strength alloy and is used in corrosion resistant chemical process equipment's including heat exchangers, condensers, heating and cooling coils and reaction vessels. Ta-W alloy is also used as ion extraction plate during laser Isotope separation of uranium and hence the composition is critical for its optimal application. The composition of the alloy was determined by neutron activation analysis (NAA) and energy dispersive X-ray fluorescence spectrometry (EDXRF) techniques. Ta-W alloy sample was received from Nuclear Fuel Complex (NFC), Hyderabad. For NAA, samples (50 - 500 mg) were sealed in polyethylene. High purity Ta foil (30 - 40 mg) and W foil (10 - 20 mg) were packed and used as comparators. Samples and standards were irradiated in the graphite reflector position of Advanced Heavy Water Reactor Critical Facility (AHWR CF) reactor, BARC, Mumbai for 4 hours. After suitable decay period, radioactivity assay was carried out using a 45% relative efficiency high purity germanium (HPGe) detector coupled to MCA with 8 k conversion gain

  14. Microstructure and mechanical properties of diamond films on titanium-aluminum-vanadium alloy

    Science.gov (United States)

    Catledge, Shane Aaron

    The primary focus of this dissertation is the investigation of the processing-structure-property relationships of diamond films deposited on Ti-6Al-4V alloy by microwave plasma chemical vapor deposition (MPCVD). By depositing a well-adhered protective layer of diamond on an alloy component, its hardness, wear-resistance, performance, and overall lifetime could be significantly increased. However, due to the large thermal expansion mismatch between the diamond film and metal (and the corresponding residual stress induced in the film), film adhesion is typically unsatisfactory and often results in immediate delamination after processing. Therefore, it is a major goal of this research to improve adhesion of the diamond film to the alloy substrate. Through the use of innovative processing techniques involving MPCVD deposition conditions and methane (CH4), nitrogen (N2), and hydrogen (H2) chemistry, we have achieved diamond films which consistently adhere to the alloy substrate. In addition, we have discovered that, with the appropriate choice of deposition conditions, the film structure can be tailored to range from highly crystalline, well-faceted diamond to nanocrystalline diamond with extremely low surface roughness (as low as 27 nm). The relationship between processing and structure was studied using in-situ optical emission spectroscopy, micro-Raman spectroscopy, surface profilometry, glancing-angle x-ray diffraction, and scanning electron microscopy. We observe that when nitrogen is added to the H2/CH4 feedgas mixture, a carbon-nitrogen (CN) emission band arises and its relative abundance to the carbon dimer (C2) gas species is shown to have a pronounced influence on the diamond film structure. By appropriate choice of deposition chemistry and conditions, we can tailor the diamond film structure and its corresponding properties. The mechanical properties of interest in this thesis are those relating to the integrity of the film/substrate interface, as well as the

  15. Fracture toughness testing on ferritic alloys using the electropotential technique

    International Nuclear Information System (INIS)

    Huang, F.H.; Wire, G.L.

    1981-01-01

    Fracture toughness measurements as done conventionally require large specimens (5 x 5 x 2.5 cm) which would be prohibitively expensive to irradiate over the fluence and temperature ranges required for first wall design. To overcome this difficulty a single specimen technique for J intergral fracture toughness measurements on miniature specimens (1.6 cm OD x 0.25 cm thick) was developed. Comparisons with specimens three times as thick show that the derived J/sub 1c/ is constant, validating the specimen for first wall applications. The electropotential technique was used to obtain continuous crack extension measurements, allowing a ductile fracture resistence curve to be constructed from a single specimen. The irradiation test volume required for fracture toughness measurements using both miniature specimens and single specimen J measurements was reduced a factor of 320, making it possible to perform a systematic exploration of irradiation temperature and dose variables as required for qualification of HT-9 and 9Cr-1Mo base metal and welds for first wall application. Fracture toughness test results for HT-9 and 9Cr-1Mo from 25 to 539 0 C are presented to illustrate the single specimen technique

  16. Microstructure and mechanical characteristics of laser coating-texturing alloying dimples

    International Nuclear Information System (INIS)

    Wan Daping; Chen Bingkui; Shao Yimin; Wang Shilong; Hu Dejin

    2008-01-01

    A novel laser coating-texturing (LCT) technique was proposed to achieve appropriate surface topographies and frictional behaviour. The LCT process was realized by applying laser pulses at very high repetition rate to produce innumerable micro-craters with required shape profile on the surface of the workpiece. Moreover, surface alloying of the dimples was carried out by melting submicron WC-TiC-Co alloy powder on the substrates. Morphology and microstructures of the texturing layers were characterised using optical microscopy (OM), scanning electron microscopy (SEM), and X-ray diffraction (XRD). Mechanical properties of the textured samples were evaluated by abrasive resistance tests and microhardness measurement. Experimental results show that good fusion bonding between the texturing layers and the substrate has been formed, and the texturing layers are mainly composed of dense and hard fine-grained structures. The abrasive wear resistance of the laser coating-textured surface was 10 times higher than that of the substrates. The average surface microhardness values were as high as 830 HV.

  17. Morphology, microstructure, and mechanical properties of laser-welded joints in GH909 alloy

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Chunming; Cai, Yuanzheng; Hu, Chongjing; Zhang, Xiong; Yan, Fei; Hu, Xiyuan [Huazhong University of Science and Technology, Wuhan (China)

    2017-05-15

    The experimental laser welding of GH909 alloy was conducted in this study. The morphology, microstructure, and mechanical properties of laser-welded joints were analyzed by scanning electron microscopy, energy diffraction spectroscopy, and other techniques. Results revealed that the microstructure of the welded joints mainly consisted of tiny cellular structures, dendritic structures, and equiaxed crystals. Pores appeared in the interdendritic regions because of the insufficient local feeding of molten metal during solidification. Nb segregation in the heat-affected zone caused liquation cracking, whereas C segregation further induced the formation of carbide precipitates along the grain boundaries during the welding thermal cycle. The instability of the keyhole significantly promoted the escape of the metal vapor/plasma from the hole; as a result, porosity defects formed in the weld. The average tensile strength of the test joints was 756 MPa, which is 93.1 % of that of the base metal. The average microhardness of the weld zone (250 HV) was higher than that of the GH909 alloy substrate (208 HV), peaking at 267 HV. Microcracks appeared along the grain boundaries, proving that the grain boundaries were the weakest areas in the joint.

  18. Precise Analysis of Microstructural Effects on Mechanical Properties of Cast ADC12 Aluminum Alloy

    Science.gov (United States)

    Okayasu, Mitsuhiro; Takeuchi, Shuhei; Yamamoto, Masaki; Ohfuji, Hiroaki; Ochi, Toshihiro

    2015-04-01

    The effects of microstructural characteristics (secondary dendrite arm spacing, SDAS) and Si- and Fe-based eutectic structures on the mechanical properties and failure behavior of an Al-Si-Cu alloy are investigated. Cast Al alloy samples are produced using a special continuous-casting technique with which it is easy to control both the sizes of microstructures and the direction of crystal orientation. Dendrite cells appear to grow in the casting direction. There are linear correlations between SDAS and tensile properties (ultimate tensile strength σ UTS, 0.2 pct proof strength σ 0.2, and fracture strain ɛ f). These linear correlations, however, break down, especially for σ UTS vs SDAS and ɛ f vs SDAS, as the eutectic structures become more than 3 μm in diameter, when the strength and ductility ( σ UTS and ɛ f) decrease significantly. For eutectic structures larger than 3 μm, failure is dominated by the brittle eutectic phases, for which SDAS is no longer strongly correlated with σ UTS and ɛ f. In contrast, a linear correlation is obtained between σ 0.2 and SDAS, even for eutectic structures larger than 3 μm, and the eutectic structure does not have a strong effect on yield behavior. This is because failure in the eutectic phases occurs just before final fracture. In situ failure observation during tensile testing is performed using microstructural and lattice characteristics. From the experimental results obtained, models of failure during tensile loading are proposed.

  19. Investigate The Effect Of Welding Parameters On Mechanical Properties During The Welding Of Al-6061 Alloy

    Directory of Open Access Journals (Sweden)

    Rajendra Prasad

    2017-10-01

    Full Text Available Friction welding is a solid state welding technique which is being used in recent times to weld similar as well as dissimilar metals for getting defect free weld. Many combinations like low carbon to stainless steel austenitic to ferrite stainless steel aluminium to copper and titanium to aluminium or steel have been tried out by various solid state welding processes with quite good results. In the present work the 3 level full factorial design has been employed to investigate the effect of welding parameters on tensile strength toughness and heat generation during the welding of Al-6061 alloy. Mathematical relationships between friction welding parameters and mechanical properties like heat generation tensile strength and toughness have also been developed. An attempt has also been made to examine the fracture surfaces of test specimens using SEM. It has been found that welding speed is the most significant parameter thats affect the heat generation tensile strength and toughness. it has been found that tensile strength and toughness during welding increases with increased in welding speed while tensile strength and toughness initially increased as the welding time increases after that it decreased with increase in welding time. The difference in weight of alloying elements can be clearly seen by analyzing spectrum of elements.

  20. Application of damping mechanism model and stacking fault probability in Fe-Mn alloy

    International Nuclear Information System (INIS)

    Huang, S.K.; Wen, Y.H.; Li, N.; Teng, J.; Ding, S.; Xu, Y.G.

    2008-01-01

    In this paper, the damping mechanism model of Fe-Mn alloy was analyzed using dislocation theory. Moreover, as an important parameter in Fe-Mn based alloy, the effect of stacking fault probability on the damping capacity of Fe-19.35Mn alloy after deep-cooling or tensile deformation was also studied. The damping capacity was measured using reversal torsion pendulum. The stacking fault probability of γ-austenite and ε-martensite was determined by means of X-ray diffraction (XRD) profile analysis. The microstructure was observed using scanning electronic microscope (SEM). The results indicated that with the strain amplitude increasing above a critical value, the damping capacity of Fe-19.35Mn alloy increased rapidly which could be explained using the breakaway model of Shockley partial dislocations. Deep-cooling and suitable tensile deformation could improve the damping capacity owning to the increasing of stacking fault probability of Fe-19.35Mn alloy

  1. Characterization of mechanical properties of pseudoelastic shape memory alloys under harmonic excitation

    Science.gov (United States)

    Böttcher, J.; Jahn, M.; Tatzko, S.

    2017-12-01

    Pseudoelastic shape memory alloys exhibit a stress-induced phase transformation which leads to high strains during deformation of the material. The stress-strain characteristic during this thermomechanical process is hysteretic and results in the conversion of mechanical energy into thermal energy. This energy conversion allows for the use of shape memory alloys in vibration reduction. For the application of shape memory alloys as vibration damping devices a dynamic modeling of the material behavior is necessary. In this context experimentally determined material parameters which accurately represent the material behavior are essential for a reliable material model. Subject of this publication is the declaration of suitable material parameters for pseudoelastic shape memory alloys and the methodology of their identification from experimental investigations. The used test rig was specifically designed for the characterization of pseudoelastic shape memory alloys.

  2. Microstructure and mechanical properties of Al-3Fe alloy processed by equal channel angular extrusion

    International Nuclear Information System (INIS)

    Fuxiao, Yu; Fang, Liu; Dazhi, Zhao; Toth, Laszlo S

    2014-01-01

    Al-Fe alloys are attractive for applications at temperatures beyond those normally associated with the conventional aluminum alloys. Under proper solidification condition, a full eutectic microstructure can be generated in Al-Fe alloys at Fe concentration well in excess of the eutectic composition of 1.8 wt.% Fe. The microstructure in this case is characterized by the metastable regular eutectic Al-Al 6 Fe fibers of nano-scale in diameter, instead of the equilibrium eutectic Al-Al 3 Fe phase. In this study, the microstructure and mechanical properties of the Al-3Fe alloy with metastable Al 6 Fe particles deformed by equal channel angular extrusion were investigated. Severe plastic deformation results in a microstructure consisting of submicron equiaxed Al grains with a uniform distribution of submicron Al 6 Fe particles on the grain boundaries. The room temperature tensile properties of the alloy with this microstructure will be presented

  3. Development and evaluation of a magnesium–zinc–strontium alloy for biomedical applications — Alloy processing, microstructure, mechanical properties, and biodegradation

    International Nuclear Information System (INIS)

    Guan, Ren-guo; Cipriano, Aaron F.; Zhao, Zhan-yong; Lock, Jaclyn; Tie, Di; Zhao, Tong; Cui, Tong; Liu, Huinan

    2013-01-01

    A new biodegradable magnesium–zinc–strontium (Mg–Zn–Sr) alloy was developed and studied for medical implant applications. This first study investigated the alloy processing (casting, rolling, and heat treatment), microstructures, mechanical properties, and degradation properties in simulated body fluid (SBF). Aging treatment of the ZSr41 alloy at 175 °C for 8 h improved the mechanical properties when compared to those of the as-cast alloy. Specifically, the aged ZSr41 alloy had an ultimate tensile strength of 270 MPa, Vickers hardness of 71.5 HV, and elongation at failure of 12.8%. The mechanical properties of the ZSr41 alloy were superior as compared with those of pure magnesium and met the requirements for load-bearing medical implants. Furthermore, the immersion of the ZSr41 alloy in SBF showed a degradation mode that progressed cyclically, alternating between pitting and localized corrosion. The steady-state average degradation rate of the aged ZSr41 alloy in SBF was 0.96 g/(m 2 ·hr), while the pH of SBF immersion solution increased. The corrosion current density of the ZSr41 alloy in SBF solution was 0.41 mA/mm 2 , which was much lower than 1.67 mA/mm 2 for pure Mg under the same conditions. In summary, compared to pure Mg, the mechanical properties of the new ZSr41 alloy improved while the degradation rate decreased due to the addition of Zn and Sr alloying elements and specific processing conditions. The superior mechanical properties and corrosion resistance of the new ZSr41 alloy make it a promising alloy for next-generation implant applications. - Highlights: • Developed a new biodegradable magnesium–zinc–strontium (Mg–Zn–Sr) alloy for medical implant applications • Reported Mg–Zn–Sr alloy processing and microstructure characterization • Improved mechanical properties of Mg alloy after aging treatment • Improved degradation properties of Mg alloy in simulated body fluid

  4. Development of plastic elongation in nanocrystalline and amorphous Ni–W dual phase alloys by brushing technique

    International Nuclear Information System (INIS)

    Nakayama, S.; Adachi, H.; Yamasaki, T.

    2015-01-01

    Highlights: • A novel agitation technique called the brushing technique is proposed. • A homogeneous material can be obtained with the brushing technique. • The brushed material exhibits large plastic elongation with work hardening. - Abstract: A novel agitation technique, referred to as the “brushing technique” is proposed to treat the surface of a Ni–W alloy film during electrodeposition. This technique was developed to directly remove hydrogen bubbles on the film surface and to apply Ni ions to the interfacial layer with the substrate. The intrinsic mechanical properties of the Ni–W electrodeposits are then evaluated with respect to application. High resolution transmission electron microscopy observations revealed that both treated and untreated films have nanocrystallites of approximately 5 nm in diameter and an amorphous phase. There was a compositional difference of about. 1.4 at% W between the face side and the reverse side of the film that was not subjected to the brushing technique, whereas this difference was absent in the film subjected to the brushing technique. In addition, the brushing technique reduced the surface roughness of the film and decreased the number of defects. As a result, a large plastic strain of about. 2.9% was observed with work hardening under tensile testing

  5. Effects of silicon on mechanical properties of AM60 magnesium alloy

    Directory of Open Access Journals (Sweden)

    Hu Yong

    2012-08-01

    Full Text Available Silicon was added to improve the tensile, wear and creep behaviors of AM60 magnesium alloy in this study. The investigation has been undertaken by means of universal testing machine, HBE-3000A Brinell hardness tester, M-2000 friction-wear machine, DMA-Q800 creep machine, optical microscopy (OM and scanning electron microscopy (SEM. The results indicate that the Chinese script type Mg2Si particles are formed by adding Si into the AM60 magnesium alloy. The ultimate tensile strength and hardness of the AM60 magnesium alloy increases with the Si addition, and the ultimate tensile strength and hardness of the AM60+1.0wt.%Si alloy are increased by 12% and 19.8%, respectively in comparison with that of the AM60 magnesium alloy. The wear property and the high temperature creep property of the AM60 magnesium alloy are also improved with Si addition. The wear mechanisms of the AM60 and AM60+1.0wt.%Si alloys are adhesive wear and abrasion wear, respectively. While, the elongation of the AM60 magnesium alloy decreases with the addition of Si. The optimum Si addition content is 1.0wt.%.

  6. Effect of Cu content on wear resistance and mechanical behavior of Ti-Cu binary alloys

    Science.gov (United States)

    Yu, Feifei; Wang, Hefeng; Yuan, Guozheng; Shu, Xuefeng

    2017-04-01

    Arc melting with nonconsumable tungsten electrode and water-cooled copper crucible was used to fabricate Ti-Cu binary alloys with different Cu contents in an argon atmosphere. The compositions and phase structures of the fabricated alloys were investigated by glow discharge optical emission spectroscopy (GDOES) and X-ray diffraction (XRD). Nanoindentation tests through continuous stiffness measurement were then performed at room temperature to analyze the mechanical behaviors of the alloys. Results indicated that the composition of each Ti-Cu binary alloy was Ti(100- x) Cu x ( x = 43, 60, 69, and 74 at.%). The XRD analysis results showed that the alloys were composed of different phases, indicating that different Cu contents led to the variations in alloy hardness. The wear tests results revealed that elemental Cu positively affects the wear resistance properties of the Ti-Cu alloys. Nanoindentation testing results showed that the moduli of the Ti-Cu alloys were minimally changed at increasing Cu content, whereas their hardness evidently increased according to the wear test results.

  7. Microstructure and mechanical properties of an extruded Mg-8Bi-1Al-1Zn (wt%) alloy

    Energy Technology Data Exchange (ETDEWEB)

    Meng, Shuaiju [School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300130 (China); Yu, Hui, E-mail: yuhuidavid@gmail.com [School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300130 (China); Materials Commercialization Center, Korea Institute of Materials Science, Changwon 51508 (Korea, Republic of); Zhang, Huixing [Mechanical and Material School, Tianjin Sino-German University of Applied Sciences, Tianjin 300350 (China); Cui, Hongwei [School of Materials Science and Engineering, Shangdong University of Technology, Zibo 255049 (China); Park, Sung Hyuk [School of Materials Science and Engineering, Kyungpook National University, Daegu 702701 (Korea, Republic of); Zhao, Weiming [School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300130 (China); You, Bong Sun [Materials Commercialization Center, Korea Institute of Materials Science, Changwon 51508 (Korea, Republic of)

    2017-04-06

    In this study, the microstructural evolution and mechanical properties of a newly developed rare earth free Mg-8Bi-1Al-1Zn (BAZ811, in wt%) alloy were investigated and compared with those of a commercial AZ31 alloy. The as-extruded BAZ811 alloy with much finer grain size shows more homogeneous dynamical recrystallized (DRXed) microstructure and weaker basal texture than those of AZ31 alloy. In addition, compared with bimodal structure AZ31 alloy containing only relatively coarse and sparse Al{sub 8}Mn{sub 5} phases, the coexistence of strip-like fragmented Mg{sub 3}Bi{sub 2} precipitate and nano-size Mg{sub 3}Bi{sub 2} particles in the microstructure was observed in BAZ811 alloy. Moreover, the BAZ811 alloy exhibits a tensile yield stress of 291 MPa, an ultimate tensile strength of 331 MPa, an elongation to failure of 14.6% as well as a reduction in yield asymmetry, which is mainly attributed to the combined effects of grain refinement and micro-scale broken Mg{sub 3}Bi{sub 2} particles together with nano-scale spherical Mg{sub 3}Bi{sub 2} precipitates. The strain hardening behavior of both BAZ811 and AZ31 alloys were also discussed in terms of microstructure variation.

  8. Characterization of phase changes during fabrication of copper alloys, crystalline and non-crystalline, prepared by mechanical alloying

    Directory of Open Access Journals (Sweden)

    Paula Rojas

    2016-09-01

    Full Text Available The manufacture of alloys in solid state has many differences with the conventional melting (casting process. In the case of high energy milling or mechanical alloying, phase transformations of the raw materials are promoted by a large amount of energy that is introduced by impact with the grinding medium; there is no melting, but the microstructural changes go from microstructural refinement to amorphization in solid state. This work studies the behavior of pure metals (Cu and Ni, and different binary alloys (Cu-Ni and Cu-Zr, under the same milling/mechanical alloying conditions. After high-energy milling, X ray diffraction (XRD patterns were analyzed to determine changes in the lattice parameter and find both microstrain and crystallite sizes, which were first calculated using the Williamson-Hall (W-H method and then compared with the transmission electron microscope (TEM images. Calculations showed a relatively appropriate approach to observations with TEM; however, in general, TEM observations detect heterogeneities, which are not considered for the W-H method. As for results, in the set of pure metals, we show that pure nickel undergoes more microstrain deformations, and is more abrasive than copper (and copper alloys. In binary systems, there was a complete solid solution in the Cu-Ni system and a glass-forming ability for the Cu-Zr, as a function of the Zr content. Mathematical methods cannot be applied when the systems have amorphization because there are no equations representing this process during milling. A general conclusion suggests that, under the same milling conditions, results are very different due to the significant impact of the composition: nickel easily forms a solid solution, while with a higher zirconium content there is a higher degree of glassforming ability.

  9. Structural evolution of Cu{sub (1−X)}Y{sub X} alloys prepared by mechanical alloying: Their thermal stability and mechanical properties

    Energy Technology Data Exchange (ETDEWEB)

    Mula, Suhrit, E-mail: smulafmt@iitr.ernet.in [Department of Metallurgical and Materials Engineering, Indian Institute of Technology Roorkee, Roorkee 247667 (India); Setman, Daria [Physics of Nanostructured Materials, University of Vienna, Boltzmanngasse 5, A-1090 Wien (Austria); Youssef, Khaled [Department of Materials Science and Technology, Qatar University, P.O. Box 2713, Doha (Qatar); Scattergood, R.O.; Koch, Carl C [Department of Materials Science and Engineering, NC State University, Raleigh, NC 27695 (United States)

    2015-04-05

    Highlights: • Metastable solid solutions were prepared from Cu–Y nonequilibrium compositions by mechanical alloying. • Gibbs free energy change as per Miedema’s model confirms the formation of metastable alloys. • High Y content alloys showed high thermal stability during extensive annealing at high temperatures. • Stabilized alloys showed very high hardness and improved yield strength. • Mechanisms of high thermal stability and improved mechanical properties were discussed. - Abstract: In the present study, an attempt has been made to synthesize copper based disordered solid solutions by mechanical alloying (MA) of non-equilibrium compositions. The blended compositions of Cu–1% Y, Cu–3% Y, Cu–5% Y and Cu–7.5% Y (at.%) (all the compositions will be addressed as % only hereafter until unless it is mentioned) were ball-milled for 8 h, and then annealed at different temperatures (200–800 °C) for different length of duration (1–5 h) under high purity argon + 2 vol.% H{sub 2} atmosphere. X-ray diffraction (XRD) analysis and Gibbs free energy change calculation confirm the formation of disordered solid solution (up to 7.5%) of Y in Cu after milling at a room temperature for 8 h. The XRD grain size was calculated to be as low as 7 nm for 7.5% Y and 22 nm for 1% Y alloy. The grain size was retained within 35 nm even after annealing for 1 h at 800 °C. Transmission electron microscopy (TEM) analysis substantiates the formation of ultra-fine grained nanostructures after milling. Microhardness value of the as-milled samples was quite high (3.0–4.75 GPa) compared to that of pure Cu. The hardness value increased with increasing annealing temperatures up to 400 °C for the alloys containing 3–7.5% Y, and thereafter it showed a decreasing trend. The increase in the hardness after annealing is attributed to the formation of uniformly distributed ultrafine intermetallic phases in the nanocrystalline grains. The stabilization effect is achieved due to

  10. The effects of Mg addition on the microstructure and mechanical properties of thixoformed Al–5%Si–Cu alloys

    International Nuclear Information System (INIS)

    Salleh, M.S.; Omar, M.Z.; Syarif, J.

    2015-01-01

    Highlights: • The average globule size of α-Al decreased when Mg amount is increased. • T6 heat treatment has increased the strength of the thixoformed alloys. • The elongation after T6 heat treatment is even significantly improved. • Thixoformed alloy with high Mg content shows a brittle type fracture. • Thixoformed alloy in T6 condition shows a ductile type fracture. - Abstract: In this study, the effects of different amounts of magnesium (Mg) on the microstructures and tensile properties of thixoformed Al–5%Si–Cu alloys were investigated. Three different alloys containing various amounts of Mg (0.5, 0.8 and 1.2 wt%) were prepared through the cooling slope casting technique, before they were thixoformed using a compression press. Several of the thixoformed samples were then treated with a T6 heat treatment, that is, solution treatment at 525 °C for 8 h, quenching in warm water at 60 °C, followed by aging at 155 °C for 4 h. All of the samples were then characterised by optical microscopy (OM), scanning electron microscopy (SEM) energy dispersive X-ray (EDX) spectroscopy and X-ray diffraction (XRD) analysis as well as by tensile tests. The results revealed that magnesium was able to refine the size of α-Al globules and the eutectic silicon in the samples. It was also observed that a compact π-Al 9 FeMg 3 Si 5 phase was formed when the magnesium content was 0.8 wt% and 1.2 wt%. The mechanical properties of the thixoformed alloys improved significantly after the T6 heat treatment. The highest attainment was recorded by the latter alloy (i.e. with 1.2 wt%Mg) with its ultimate tensile strength (UTS) as high as 306 MPa, yield strength (YS), 264 MPa, and elongation to fracture of 1.8%. The fracture of thixoformed alloy with a low Mg content (0.5 wt%) showed a combination of dimple and cleavage fracture, whereas in the alloy that contained the highest Mg content (1.2 wt%), cleavage fracture was observed

  11. The effects of Mg addition on the microstructure and mechanical properties of thixoformed Al–5%Si–Cu alloys

    Energy Technology Data Exchange (ETDEWEB)

    Salleh, M.S., E-mail: shukor@utem.edu.my [Department of Mechanical and Materials Engineering, Faculty of Engineering and Built Environment, Universiti Kebangsaan Malaysia, 43600 Selangor (Malaysia); Department of Manufacturing Process, Faculty of Manufacturing Engineering, Universiti Teknikal Malaysia Melaka, Hang Tuah Jaya, 76100 Durian Tunggal, Melaka (Malaysia); Omar, M.Z., E-mail: zaidi@eng.ukm.my [Department of Mechanical and Materials Engineering, Faculty of Engineering and Built Environment, Universiti Kebangsaan Malaysia, 43600 Selangor (Malaysia); Syarif, J., E-mail: syarif@eng.ukm.my [Department of Mechanical and Materials Engineering, Faculty of Engineering and Built Environment, Universiti Kebangsaan Malaysia, 43600 Selangor (Malaysia)

    2015-02-05

    Highlights: • The average globule size of α-Al decreased when Mg amount is increased. • T6 heat treatment has increased the strength of the thixoformed alloys. • The elongation after T6 heat treatment is even significantly improved. • Thixoformed alloy with high Mg content shows a brittle type fracture. • Thixoformed alloy in T6 condition shows a ductile type fracture. - Abstract: In this study, the effects of different amounts of magnesium (Mg) on the microstructures and tensile properties of thixoformed Al–5%Si–Cu alloys were investigated. Three different alloys containing various amounts of Mg (0.5, 0.8 and 1.2 wt%) were prepared through the cooling slope casting technique, before they were thixoformed using a compression press. Several of the thixoformed samples were then treated with a T6 heat treatment, that is, solution treatment at 525 °C for 8 h, quenching in warm water at 60 °C, followed by aging at 155 °C for 4 h. All of the samples were then characterised by optical microscopy (OM), scanning electron microscopy (SEM) energy dispersive X-ray (EDX) spectroscopy and X-ray diffraction (XRD) analysis as well as by tensile tests. The results revealed that magnesium was able to refine the size of α-Al globules and the eutectic silicon in the samples. It was also observed that a compact π-Al{sub 9}FeMg{sub 3}Si{sub 5} phase was formed when the magnesium content was 0.8 wt% and 1.2 wt%. The mechanical properties of the thixoformed alloys improved significantly after the T6 heat treatment. The highest attainment was recorded by the latter alloy (i.e. with 1.2 wt%Mg) with its ultimate tensile strength (UTS) as high as 306 MPa, yield strength (YS), 264 MPa, and elongation to fracture of 1.8%. The fracture of thixoformed alloy with a low Mg content (0.5 wt%) showed a combination of dimple and cleavage fracture, whereas in the alloy that contained the highest Mg content (1.2 wt%), cleavage fracture was observed.

  12. Investigating the Thermal and Phase Stability of Nanocrystalline Ni-W Produced by Electrodeposition, Sputtering, and Mechanical Alloying

    Science.gov (United States)

    Marvel, Christopher Jonathan

    The development of nanocrystalline materials has been increasingly pursued over the last few decades. They have been shown to exhibit superior properties compared to their coarse-grain counterparts, and thus present a tremendous opportunity to revolutionize the performance of nanoscale devices or bulk structural materials. However, nanocrystalline materials are highly prone to grain growth, and if the nanocrystalline grains coarsen, the beneficial properties are lost. There is a strong effort to determine the most effective thermal stability mechanisms to avoid grain growth, but the physical nature of nanocrystalline grain growth is still unclear due to a lack of detailed understanding of nanocrystalline microstructures. Furthermore, the influence of contamination has scarcely been explored with advanced transmission electron microscopy techniques, nor has there been a direct comparison of alloys fabricated with different bulk processes. Therefore, this research has applied aberration-corrected scanning transmission electron microscopy to characterize nanocrystalline Ni-W on the atomic scale and elucidate the physical grain growth behavior. Three primary objectives were pursued: (1) explore the thermal stability mechanisms of nanocrystalline Ni-W, (2) evaluate the phase stability of Ni-W and link any findings to grain growth behavior, and (3) compare the influences of bulk fabrication processing, including electrodeposition, DC magnetron sputtering, and mechanical alloying, on the thermal stability and phase stability of Ni-W. Several thermal stability mechanisms were identified throughout the course of this research. First and foremost, W-segregation was scarcely observed to grain boundaries, and it is unclear if W-segregation improves thermal stability contrary to most reports in the 2 literature. Long-range Ni4W chemical ordering was observed in alloys with more than 20 at.% W, and it is likely Ni4W domains reduce grain boundary mobility. In addition, lattice

  13. Effect of mechanical vibrations on the wear behavior of AZ91 Mg alloy

    Science.gov (United States)

    Chaturvedi, V.; Pandel, U.; Sharma, A.

    2018-02-01

    AZ91 Mg alloy is the most promising alloy used for structural applications. The vibration induced methods are effective and economic viable in term of mechanical properties. Sliding wear tests were performed on AZ91 Mg alloy using a pin-on- disc configuration. Wear rates were measured at 5 N and 10N at a sliding velocity of 1m/s for varied frequency within the range of 5- 25Hz and a constant amplitude of 2mm. Microstructures of worn surfaces and wear debris were characterized by field emission scanning electron microscopy (FESEM). It is observed that wear resistance of vibrated AZ91 alloy at 15Hz frequency ad 2mm amplitude was superior than cast AZ91 Mg alloy. Finer grain size and equiaxed grain shape both are important parameters for better wear resistance in vibrated AZ91 Mg alloys. FESEM analysis revealed that wear is considerably affected due to frictional heat generated by the relative motion between AZ91 Mg alloy and EN31 steel surface. No single mechanism was responsible for material loss.

  14. The microstructure, mechanical and friction properties of protective diamond like carbon films on magnesium alloy

    Science.gov (United States)

    Zou, Y. S.; Wu, Y. F.; Yang, H.; Cang, K.; Song, G. H.; Li, Z. X.; Zhou, K.

    2011-12-01

    Protective hard coatings deposited on magnesium alloys are believed to be effective for overcoming their poor wear properties. In this work, diamond-like carbon (DLC) films as hard protective films were deposited on AZ91 magnesium alloy by arc ion plating under negative pulse bias voltages ranging from 0 to -200 V. The microstructure, composition and mechanical properties of the DLC films were analyzed by scanning electron microscopy, Raman spectroscopy, X-ray photoelectron spectroscopy and nanoindentation. The tribological behavior of uncoated and coated AZ91 magnesium alloy was investigated using a ball-on-disk tribotester. The results show that the negative pulse bias voltage used for film deposition has a significant effect on the sp3 carbon content and mechanical properties of the deposited DLC films. A maximum sp3 content of 33.3% was obtained at -100 V, resulting in a high hardness of 28.6 GPa and elastic modulus of 300.0 GPa. The DLC films showed very good adhesion to the AZ91 magnesium alloy with no observable cracks and delamination even during friction testing. Compared with the uncoated AZ91 magnesium alloy, the magnesium alloy coated with DLC films exhibits a low friction coefficient and a narrow, shallow wear track. The wear resistance and surface hardness of AZ91 magnesium alloy can be significantly improved by coating a layer of DLC protective film due to its high hardness and low friction coefficient.

  15. The microstructure, mechanical and friction properties of protective diamond like carbon films on magnesium alloy

    International Nuclear Information System (INIS)

    Zou, Y.S.; Wu, Y.F.; Yang, H.; Cang, K.; Song, G.H.; Li, Z.X.; Zhou, K.

    2011-01-01

    Protective hard coatings deposited on magnesium alloys are believed to be effective for overcoming their poor wear properties. In this work, diamond-like carbon (DLC) films as hard protective films were deposited on AZ91 magnesium alloy by arc ion plating under negative pulse bias voltages ranging from 0 to -200 V. The microstructure, composition and mechanical properties of the DLC films were analyzed by scanning electron microscopy, Raman spectroscopy, X-ray photoelectron spectroscopy and nanoindentation. The tribological behavior of uncoated and coated AZ91 magnesium alloy was investigated using a ball-on-disk tribotester. The results show that the negative pulse bias voltage used for film deposition has a significant effect on the sp 3 carbon content and mechanical properties of the deposited DLC films. A maximum sp 3 content of 33.3% was obtained at -100 V, resulting in a high hardness of 28.6 GPa and elastic modulus of 300.0 GPa. The DLC films showed very good adhesion to the AZ91 magnesium alloy with no observable cracks and delamination even during friction testing. Compared with the uncoated AZ91 magnesium alloy, the magnesium alloy coated with DLC films exhibits a low friction coefficient and a narrow, shallow wear track. The wear resistance and surface hardness of AZ91 magnesium alloy can be significantly improved by coating a layer of DLC protective film due to its high hardness and low friction coefficient.

  16. The microstructure, mechanical and friction properties of protective diamond like carbon films on magnesium alloy

    Energy Technology Data Exchange (ETDEWEB)

    Zou, Y.S., E-mail: yshzou75@gmail.com [School of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing, Jiangsu, 210094 (China); Wu, Y.F.; Yang, H.; Cang, K. [School of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing, Jiangsu, 210094 (China); Song, G.H. [School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, Liaoning, 110178 (China); Li, Z.X.; Zhou, K. [School of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing, Jiangsu, 210094 (China)

    2011-12-01

    Protective hard coatings deposited on magnesium alloys are believed to be effective for overcoming their poor wear properties. In this work, diamond-like carbon (DLC) films as hard protective films were deposited on AZ91 magnesium alloy by arc ion plating under negative pulse bias voltages ranging from 0 to -200 V. The microstructure, composition and mechanical properties of the DLC films were analyzed by scanning electron microscopy, Raman spectroscopy, X-ray photoelectron spectroscopy and nanoindentation. The tribological behavior of uncoated and coated AZ91 magnesium alloy was investigated using a ball-on-disk tribotester. The results show that the negative pulse bias voltage used for film deposition has a significant effect on the sp{sup 3} carbon content and mechanical properties of the deposited DLC films. A maximum sp{sup 3} content of 33.3% was obtained at -100 V, resulting in a high hardness of 28.6 GPa and elastic modulus of 300.0 GPa. The DLC films showed very good adhesion to the AZ91 magnesium alloy with no observable cracks and delamination even during friction testing. Compared with the uncoated AZ91 magnesium alloy, the magnesium alloy coated with DLC films exhibits a low friction coefficient and a narrow, shallow wear track. The wear resistance and surface hardness of AZ91 magnesium alloy can be significantly improved by coating a layer of DLC protective film due to its high hardness and low friction coefficient.

  17. Mechanical Characterisation and Biomechanical and Biological Behaviours of Ti-Zr Binary-Alloy Dental Implants

    Directory of Open Access Journals (Sweden)

    Aritza Brizuela-Velasco

    2017-01-01

    Full Text Available The objective of the study is to characterise the mechanical properties of Ti-15Zr binary alloy dental implants and to describe their biomechanical behaviour as well as their osseointegration capacity compared with the conventional Ti-6Al-4V (TAV alloy implants. The mechanical properties of Ti-15Zr binary alloy were characterised using Roxolid© implants (Straumann, Basel, Switzerland via ultrasound. Their biomechanical behaviour was described via finite element analysis. Their osseointegration capacity was compared via an in vivo study performed on 12 adult rabbits. Young’s modulus of the Roxolid© implant was around 103 GPa, and the Poisson coefficient was around 0.33. There were no significant differences in terms of Von Mises stress values at the implant and bone level between both alloys. Regarding deformation, the highest value was observed for Ti-15Zr implant, and the lowest value was observed for the cortical bone surrounding TAV implant, with no deformation differences at the bone level between both alloys. Histological analysis of the implants inserted in rabbits demonstrated higher BIC percentage for Ti-15Zr implants at 3 and 6 weeks. Ti-15Zr alloy showed elastic properties and biomechanical behaviours similar to TAV alloy, although Ti-15Zr implant had a greater BIC percentage after 3 and 6 weeks of osseointegration.

  18. Experimental study of the zirconium alloy oxidation under high pressure of steam and modelling of the mechanisms

    International Nuclear Information System (INIS)

    Dali, Yacoub

    2007-01-01

    The corrosion of the cladding materials used for the fuel rods is one of the limiting factor of their lifetime in light water reactors. In this field, the aim of the nuclear industry is today to increase the time and the number of cycles and to submit the claddings in zirconium alloys to higher corrosive conditions. In this way, new alloys devoted to replace the standard Zircaloy-4, for instance Nb containing alloys, have been recently developed and licensed and show better corrosion resistance. A better understanding of the corrosion mechanisms of the zirconium alloys is necessary to predict the corrosion behaviour of these materials. In this work, the oxidation rate of model alloys of two metallurgic families has been studied in steam in a pressure range between 100 milli-bars and 100 bars. The Zircaloy type alloys contain as alloying elements oxygen and/or tin and/or iron and chromium. For the Zr-Nb family, three niobium contents have been studied, respectively 0.2, 0.4 and 1 weight percent of niobium. Our objectives were to understand the variations of the reactivity between the low pressure and the high pressure range, in quantifying the dependency of the corrosion rate with the steam pressure and the alloying element concentrations. The segregation process of the niobium at the surface has also been studied on the Zr-Nb alloys. During this work, a magnetic suspension thermo-balance has been developed and used to follow in-situ the corrosion rate at high pressure of water vapour. The oxide layers have been characterized by many techniques, macro and micro-photo-electrochemistry, XRD, FEG-SEM, XPS, HR-TEM and SIMS. For the Zircaloy type alloys, we have confirmed the major role of the intermetallic precipitates Zr(Fe,Cr) 2 on the corrosion resistance. Unlike the standard Zircaloy-4, for which the oxidation rate does not depend on the pressure of the water vapour and is thus limited by the vacancy diffusion in the oxide layer, we have shown that the rate of the

  19. Mechanical and corrosion properties of binary Mg–Dy alloys for medical applications

    International Nuclear Information System (INIS)

    Yang Lei; Huang Yuanding; Peng Qiuming; Feyerabend, Frank; Kainer, Karl Ulrich; Willumeit, Regine; Hort, Norbert

    2011-01-01

    Microstructure, mechanical and corrosion properties of binary magnesium–dysprosium (Mg-5, 10, 15, 20 wt.% Dy) alloys were investigated for medical applications. In the as-cast condition, the distribution of Dy is quite inhomogeneous. Mg–10Dy alloy exhibits a moderate tensile and compression yield strength, and the best elongation and corrosion resistance. After T4 (solutionizing) treatment, the distribution of Dy becomes homogeneous. The tensile and compression yield strength of all Mg–Dy alloys decreases. The elongation remains unchanged, while the corrosion resistance is largely improved after T4 treatment.

  20. Mechanical and corrosion properties of binary Mg-Dy alloys for medical applications

    Energy Technology Data Exchange (ETDEWEB)

    Yang Lei, E-mail: lei.yang@hzg.de [Helmholtz-Zentrum Geesthacht, Institute of Materials Research, Max-Planck-Str. 1, D-21502 Geesthacht (Germany); Yuanding, Huang; Qiuming, Peng; Feyerabend, Frank; Kainer, Karl Ulrich; Willumeit, Regine; Hort, Norbert [Helmholtz-Zentrum Geesthacht, Institute of Materials Research, Max-Planck-Str. 1, D-21502 Geesthacht (Germany)

    2011-12-15

    Microstructure, mechanical and corrosion properties of binary magnesium-dysprosium (Mg-5, 10, 15, 20 wt.% Dy) alloys were investigated for medical applications. In the as-cast condition, the distribution of Dy is quite inhomogeneous. Mg-10Dy alloy exhibits a moderate tensile and compression yield strength, and the best elongation and corrosion resistance. After T4 (solutionizing) treatment, the distribution of Dy becomes homogeneous. The tensile and compression yield strength of all Mg-Dy alloys decreases. The elongation remains unchanged, while the corrosion resistance is largely improved after T4 treatment.

  1. Mechanisms Governing the Creep Behavior of High Temperature Alloys for Generation IV Nuclear Energy Systems

    International Nuclear Information System (INIS)

    Vasudevan, Vijay; Carroll, Laura; Sham, Sam

    2015-01-01

    This research project, which includes collaborators from INL and ORNL, focuses on the study of alloy 617 and alloy 800H that are candidates for applications as intermediate heat exchangers in GEN IV nuclear reactors, with an emphasis on the effects of grain size, grain boundaries and second phases on the creep properties; the mechanisms of dislocation creep, diffusional creep and cavitation; the onset of tertiary creep; and theoretical modeling for long-term predictions of materials behavior and for high temperature alloy design.

  2. Acoustic emission on thermoelastic martensitic transformations in alloys in the course of mechanical loading

    International Nuclear Information System (INIS)

    Plotnikov, V.A.; Kokhanenko, D.V.

    2004-01-01

    The connection of the emission process with the process of the deformation accumulation and relaxation in the cycle of the martensitic transformations is studied. The martensitic transformations cycling was investigated by cycling change in the temperature in the Ti 50 Ni 50 Cu 10 alloys. The deformation accumulation and recovery is observed in the alloys undergoing the thermoelastic martensitic transformations under the mechanical loading conditions. The acoustic emission, accompanying the martensitic transformations, reflects the peculiarities of the alloy deformation behavior by the martensitic transformations. The anomalous acoustic effect correlates with the reversible deformation accumulation and does not correlates with the irreversible deformation accumulation [ru

  3. Microstructure and mechanical properties of sintered Ti Binary alloys for dental applications

    Energy Technology Data Exchange (ETDEWEB)

    Yilmaz Atay, H.; Haro Rodriguez, M.; Amigo Mata, A.; Vicente Escuder, V.; Amigo Borras, V.

    2016-07-01

    Biomaterials have shown rapid growth in the field of elderly population demands with the prolongation of human life. One of those biomaterials, titanium, has excellent properties and biocompatibility though it may cause weakening in the structures due to its higher stiffness. In this study, powder metallurgy process was used to produce Ti-Cr, Ti-Mo and Ti-Cu metal alloys to overcome this problem. Metal powders were mixed by mechanical alloying. After pressing and sintering, alloys structures were investigated. Characterizations were carried out by size analyzer, SEM-EDX, optical microscope and three points bending test. (Author)

  4. Mechanisms Governing the Creep Behavior of High Temperature Alloys for Generation IV Nuclear Energy Systems

    Energy Technology Data Exchange (ETDEWEB)

    Vasudevan, Vijay [Univ. of Cincinnati, OH (United States); Carroll, Laura [Idaho National Lab. (INL), Idaho Falls, ID (United States); Sham, Sam [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2015-04-06

    This research project, which includes collaborators from INL and ORNL, focuses on the study of alloy 617 and alloy 800H that are candidates for applications as intermediate heat exchangers in GEN IV nuclear reactors, with an emphasis on the effects of grain size, grain boundaries and second phases on the creep properties; the mechanisms of dislocation creep, diffusional creep and cavitation; the onset of tertiary creep; and theoretical modeling for long-term predictions of materials behavior and for high temperature alloy design.

  5. Recovery of the mechanical properties on the Al-4wt%Cu alloy

    International Nuclear Information System (INIS)

    Chemingui, M; Kassis, K; Khitouni, M; Masmoudi, J; Kolsi, A W

    2010-01-01

    The recovery of the mechanical properties on the Al-4%wtCu alloy was investigated by indentation after cold rolling. The microstructural evolution was performed using optical and scanning electron microscopies. The annealing at 200 deg. C of the quenched and rolled alloy gives higher mechanical qualities. At temperatures up to 200 deg. C, the alloy has no softening by recovery, but on the contrary a hardening behaviour was observed. This later is attributed to the presence of the intermediate θ'' and θ' phases. Nevertheless, the ageing in high temperature product the coalescence of iron particles and of Al 2 Cu precipitates. These phases are essentially localized in the grain boundaries, which caused the damage of the alloy.

  6. Effect of deformation and annealing on mechanical properties of nickel-rhenium alloys

    International Nuclear Information System (INIS)

    Mashkova, V.M.

    1978-01-01

    Studied have been the mechanical properties of nickel-rhenium alloys, depending on the extent of deformation and heat treatment leading to softening. The mechanical properties of the alloys have been estimated by the results of the tensile tests of wire samples. The softening of the alloy at different temperatures is judged about by the variation in hardness. The results of the study indicate that the most abrupt reduction in the hardness of the cold-hardened metal occurs at 900-1,000 deg C and the hold-time of 1 min. Increase in the hold-time at such temperature almost does not reduce the hardness. It is established that in order to soften nickel-rhenium alloys in the process of the cold-deformation at brief annealings in the air the hold-time should not exceed 5 min at 800-900 deg C

  7. Microscopic mechanisms contributing to the synchronous improvement of strength and plasticity (SISP) for TWIP copper alloys.

    Science.gov (United States)

    Liu, R; Zhang, Z J; Li, L L; An, X H; Zhang, Z F

    2015-04-01

    In this study, the concept of "twinning induced plasticity (TWIP) alloys" is broadened, and the underlying intrinsic microscopic mechanisms of the general TWIP effect are intensively explored. For the first aspect, "TWIP copper alloys" was proposed following the concept of "TWIP steels", as they share essentially the same strengthening and toughening mechanisms. For the second aspect, three intrinsic features of twinning: i.e. "dynamic development", "planarity", as well as "orientation selectivity" were derived from the detailed exploration of the deformation behavior in TWIP copper alloys. These features can be considered the microscopic essences of the general "TWIP effect". Moreover, the effective cooperation between deformation twinning and dislocation slipping in TWIP copper alloys leads to a desirable tendency: the synchronous improvement of strength and plasticity (SISP). This breakthrough against the traditional trade-off relationship, achieved by the general "TWIP effect", may provide useful strategies for designing high-performance engineering materials.

  8. The formation mechanism of mechanically alloyed Fe-20 at% Al powder

    Energy Technology Data Exchange (ETDEWEB)

    Hadef, F., E-mail: hadef77@yahoo.fr [Laboratoire de Recherche sur la Physico-Chimie des Surfaces et Interfaces, LRPCSI, Universite 20 Aout 1955, BP 26, Route d' El-Hadaiek, Skikda 21000 (Algeria); Otmani, A. [Laboratoire de Recherche sur la Physico-Chimie des Surfaces et Interfaces, LRPCSI, Universite 20 Aout 1955, BP 26, Route d' El-Hadaiek, Skikda 21000 (Algeria); Djekoun, A. [Laboratoire de Magnetisme et Spectroscopie des Solides, LM2S, Universite Badji Mokhtar, BP 12 Annaba 23000 (Algeria); Greneche, J.M. [LUNAM, Universite du Maine, Institut des Molecules et Materiaux du Mans, UMR CNRS 6283, 72085 Le Mans (France)

    2013-01-15

    The formation mechanism of the mechanically alloyed Fe-20 at% Al, from elemental Fe and Al powders, has been investigated. The experimental results indicate the formation of a nanocrystalline bcc {alpha}-Fe(Al) solid solution with a lattice parameter close to a{sub {alpha}-Fe(Al)}=0.2890 nm, where each Fe atom is surrounded by (6Fe+2Al) in the first coordination sphere. The reaction mechanism of MA process seems to be controlled by a diffusion phenomenon. Aluminum particles undergo an important refinement to the nanometer scale and then they stick on Fe particles of large sizes. A large number of clear Al/Fe interface areas were generated. The short diffusion path and the presence of high concentration of defects accelerated the solid state reaction. - Highlights: Black-Right-Pointing-Pointer A nanocrystalline bcc {alpha}-Fe(Al) solid solution is formed from elemental Fe and Al powders. Black-Right-Pointing-Pointer The reaction mechanism of MA process seems to be controlled by a diffusion phenomenon. Black-Right-Pointing-Pointer Each Fe atom is surrounded by (6Fe+2Al) in the first coordination sphere.

  9. The analysis of the mechanical properties of F75 Co-Cr alloy for use in selective laser melting (SLM manufacturing of removable partial dentures (RPD

    Directory of Open Access Journals (Sweden)

    D. Jevremovic

    2012-04-01

    Full Text Available The presented work discusses the applicability of the selective laser melting technique (SLM in manufacture of removable partial denture (RPD frameworks with the emphasis on material properties. The paper presents initial results of a conducted test of the mechanical properties of the F75 Co-Cr dental alloy used with selective laser melting.

  10. Review on structural fatigue of NiTi shape memory alloys: Pure mechanical and thermo-mechanical ones

    Directory of Open Access Journals (Sweden)

    Guozheng Kang

    2015-11-01

    Full Text Available Structural fatigue of NiTi shape memory alloys is a key issue that should be solved in order to promote their engineering applications and utilize their unique shape memory effect and super-elasticity more sufficiently. In this paper, the latest progresses made in experimental and theoretical analyses for the structural fatigue features of NiTi shape memory alloys are reviewed. First, macroscopic experimental observations to the pure mechanical and thermo-mechanical fatigue features of the alloys are summarized; then the state-of-arts in the mechanism analysis of fatigue rupture are addressed; further, advances in the construction of fatigue failure models are provided; finally, summary and future topics are outlined.

  11. Generation of Articulated Mechanisms by Optimization Techniques

    DEFF Research Database (Denmark)

    Kawamoto, Atsushi

    2004-01-01

    optimization [Paper 2] 3. Branch and bound global optimization [Paper 3] 4. Path-generation problems [Paper 4] In terms of the objective of the articulated mechanism design problems, the first to third papers deal with maximization of output displacement, while the fourth paper solves prescribed path...... generation problems. From a mathematical programming point of view, the methods proposed in the first and third papers are categorized as deterministic global optimization, while those of the second and fourth papers are categorized as gradient-based local optimization. With respect to design variables, only...... directly affects the result of the associated sensitivity analysis. Another critical issue for mechanism design is the concept of mechanical degrees of freedom and this should be also considered for obtaining a proper articulated mechanism. The thesis treats this inherently discrete criterion in some...

  12. Properties of Mechanically Alloyed W-Ti Materials with Dual Phase Particle Dispersion

    Czech Academy of Sciences Publication Activity Database

    Lukáč, František; Vilémová, Monika; Nevrlá, Barbara; Klečka, Jakub; Chráska, Tomáš; Molnárová, O.

    2017-01-01

    Roč. 7, č. 1 (2017), č. článku 3. ISSN 2075-4701 R&D Projects: GA ČR(CZ) GA15-15609S Institutional support: RVO:61389021 Keywords : tungsten-titanium alloys * mechanical alloying * particle dispersion * pulsed electric current sintering * thermal conductivity * bending strength Subject RIV: JJ - Other Materials OBOR OECD: Materials engineering Impact factor: 1.984, year: 2016

  13. Reactor irradiation and helium-3 effects on mechanical properties of alpha-titanium alloys

    International Nuclear Information System (INIS)

    Tebus, V.N.; Alekseev, Eh.F.; Golikov, I.V.

    1990-01-01

    Dependence of α-titanium alloy mechanical properties on test temperature and neutron fluence is investigated. Irradiation is shown to result in material hardening and in their plasticity reduction, but residual plasticity remains rather high. Additional reduction of plasticity results in helium-3 introduced in materials under irradiation. Restoration of properties is observed at test temperature higher 500 deg C. Irradiation by fast neutrons up to high fluences (1.4·10 23 cm -2 ) results in essential alloy softening

  14. Effect of ECAP on microstructure and mechanical properties of cast AZ91 magnesium alloy

    International Nuclear Information System (INIS)

    Chung, C W; Gao, W; Ding, R G; Chiu, Y L

    2010-01-01

    An as-cast AZ91 magnesium alloy was processed by Equal Channel Angular Pressing (ECAP) at 320 0 C. The microstructure and mechanical properties were studied. It has been found that ECAP refines both the grains and precipitates, thus modifies the strength and ductility of the processed alloy. After the first pass of ECAP, the yield stress improves significantly from 71 MPa to 140 MPa.

  15. Microstructures and Mechanical Properties of Inconel 718 Alloy at Ultralow Temperatures

    Science.gov (United States)

    Yao, C. G.; Lv, H. J.; Yi, D. Q.; Meng, S.; Xiao, L. R.; Wang, B.

    2018-05-01

    The microstructures and mechanical properties of powder metallurgy Inconel 718 alloy were investigated in the temperatures range between 25 and - 253 °C. Tensile strength increased with the decrease in temperature, while the ductility first increased and then decreased. There was no significant change in impact toughness. When the temperature was - 253 °C, a zigzag stress-strain curve was observed for the alloy, owing to the interaction of dislocation glide and twinning, which effectively maintained the relatively good ductility.

  16. The structure and mechanical properties of as-cast Zr-Ti alloys

    International Nuclear Information System (INIS)

    Hsu, H.-C.; Wu, S.-C.; Sung, Y.-C.; Ho, W.-F.

    2009-01-01

    This study has investigated the structure and mechanical properties of pure Zr and a series of binary Zr-Ti alloys in order to determine their potential application as dental implant materials. The titanium contents of these alloys range from 10 to 40 wt.% and were prepared by arc melting in inert gas. This study evaluated the phase and structure of these Zr-Ti alloys using an X-ray diffraction (XRD) for phase analysis, and an optical microscope for microstructure analysis of the etched alloys. Three-point bending tests were performed to evaluate the mechanical properties of all specimens. The experimental results indicated that the pure Zr and Zr-10Ti comprised entirely of an acicular hexagonal structure of α' phase. When the Ti content increased to 20 wt.%, a significant amount of β phase was retained. However, when the Ti content increased to 40 wt.%, only the equi-axed, retained β phase was observed in the cast alloy. Moreover, the hardness values and bending strengths of the Zr-Ti alloys decreased with an increasing Ti content. Among pure Zr and Zr-Ti alloys, the α'-phase Zr-10Ti alloy has the greatest hardness and bending strength. The pure Zr and Zr-Ti alloys exhibit a similar elastic modulus ranging from 68 GPa (Zr-30Ti) to 78 GPa (Zr-40Ti). Based on the results of elastic moduli, pure Zr and Zr-Ti alloys are found to be suitable for implant materials due to lower modulus. Like bending strength, the elastically recoverable angle of Zr-Ti alloys decreased as the concentration of Ti increased. In the current search for a better implant material, the Zr-10Ti alloy exhibited the highest bending strength/modulus ratios as large as 25.3, which are higher than that of pure Zr (14.9) by 70%, and commercially pure Ti (8.7) by 191%. Thus, Zr-Ti alloy's low modulus, ductile property, excellent elastic recovery capability and impressive strength confirm that it is a promising candidate for dental implant materials.

  17. Structural and magnetic study of mechanically deformed Fe rich FeAlSi ternary alloys

    International Nuclear Information System (INIS)

    Legarra, E.; Apiñaniz, E.; Plazaola, F.

    2012-01-01

    Highlights: ► Addition of Si to binary Fe–Al alloys makes the disordering more difficult. ► Si addition opposes the large volume increase found in FeAl alloys with deformation. ► Disordering induces a redistribution of non-ferrous atoms around Fe atoms in Fe 75 Al 25−x Si x and Fe 70 Al 30−x Si x . ► Addition of Si to binary Fe 75 Al 25 and Fe 70 Al 30 alloys opposes the magnetic behavior induced by Al in the magnetism of Fe. ► Si inhibits the para-ferro transition found in Fe 60 Al 40 alloy with disordering. - Abstract: In this work we study systematically the influence of different Al/Si ratios on the magnetic and structural properties of mechanically disordered powder Fe 75 Al 25−x Si x , Fe 70 Al 30−x Si x and Fe 60 Al 40−x Si x alloys by means of Mössbauer spectroscopy, X-ray diffraction and magnetic measurements. In order to obtain different stages of disorder the alloys were deformed by different methods: crushing induction melted alloys and ball milling annealed (ordered) alloys using different number of balls and speed. X-ray and Mössbauer data show that mechanical deformation induces the disordered A2 structure in these alloys. The results indicate that addition of Si to binary Fe–Al alloys makes the disordering more difficult. In addition, X-ray diffraction patterns show that the normalized lattice parameter variation of the disordered alloys of each composition decreases monotonically with Si content, indicating clearly that Si addition opposes the large volume increase found in FeAl alloys with deformation. The study of the hyperfine fields indicates that there is a redistribution of non-ferrous atoms around Fe atoms with the disordering; indeed, there is an inversion of the behavior of the hyperfine field of the Fe atoms. On the other hand, the magnetic measurements indicate that addition of Si to binary Fe 75 Al 25 and Fe 70 Al 30 alloys opposes the magnetic behavior induced by Al in the magnetism of Fe.

  18. Microstructural, mechanical and electrochemical behaviour of a 7017 Al–Zn–Mg alloy of different tempers

    Energy Technology Data Exchange (ETDEWEB)

    Rout, Prasanta Kumar, E-mail: prasantonnet55@yahoo.com; Ghosh, M.M.; Ghosh, K.S., E-mail: ksghosh2001@yahoo.co.uk

    2015-06-15

    The aim of the investigation is to assess the microstructural features and associated physical, mechanical and electrochemical properties of a 7017 Al–Zn–Mg alloy of various tempers. A 7017 Al–Zn–Mg alloy was subjected to different ageing schedules to produce under-(T4), peak-(T6), over-(T7) and highly over-aged tempers. Optical microscopy, hardness measurement, electrical conductivity measurement, tensile testing and SEM fractographs, differential scanning calorimetry (DSC), transmission electron microscopy (TEM), and electrochemical polarization studies have been used to characterize the alloy tempers. Hardness measurement and tensile testing showed the characteristic age hardening phenomenon of aluminium alloys. Optical and TEM micrographs have revealed the variation in size of matrix strengthening η′ (MgZn{sub 2}) and also the size and distribution of grain boundary η (MgZn{sub 2}) precipitate with ageing time. DSC thermograms exhibiting exothermic and endothermic peaks indicated the characteristic solid state reaction sequence of the 7017 alloy. Potentiodynamic polarization study of the 7017 alloy of various tempers in 3.5 wt.% NaCl solution at near neutral pH showed typical active metal dissolution behaviour, but at pH 12 an active–passive–transpassive transition behaviour has been observed. - Graphical abstract: TEM micrograph of the 7017 aluminium alloy of various tempers (a, b) under aged (T4), (c, d) peak aged (T6), (e, f) over aged (T7) and (g, h) highly over-aged. Display Omitted - Highlights: • 7017 Al-Zn-Mg alloy was subjected to different artificial ageing treatments. • Characterization of 7017 alloy tempers by hardness, tensile, DSC, TEM and electrochemical behaviour. • Structure-properties relationship of the 7017 Al-Zn-Mg alloy of various tempers.

  19. Effects of different production technologies on mechanical and metallurgical properties of precious metal denture alloys

    Science.gov (United States)

    Ferro, Paolo; Battaglia, Eleonora; Capuzzi, Stefano; Berto, Filippo

    2017-12-01

    Precious metal alloys can be supplied in traditional plate form or innovative drop form with high degree of purity. The aim of the present work is to evaluate the influence of precious metal alloy form on metallurgical and mechanical properties of the final dental products with particular reference to metal-ceramic bond strength and casting defects. A widely used alloy for denture was selected; its nominal composition was close to 55 wt% Pd - 34 wt% Ag - 6 wt% In - 3 wt% Sn. Specimens were produced starting from the alloy in both plate and drop forms. A specific test method was developed to obtain results that could be representative of the real conditions of use. In order to achieve further information about the adhesion behaviour and resistance, the fracture surfaces of the samples were observed using `Scanning Electron Microscopy (SEM)'. Moreover, material defects caused by the moulding process were studied. The form of the alloy before casting does not significantly influence the shear bond strength between the metal and the ceramic material (p-value=0,976); however, according to SEM images, products from drop form alloy show less solidification defects compared to products obtained with plate form alloy. This was attributed to the absence of polluting additives used in the production of drop form alloy. This study shows that the use of precious metal denture alloys supplied in drop form does not affect the metal-ceramic bond strength compared to alloys supplied in the traditional plate form. However, compared to the plate form, the drop form is found free of solidification defects, less expensive to produce and characterized by minor environmental impacts.

  20. Mechanisms of improving the cyclic stability of V-Ti-based hydrogen storage electrode alloys

    International Nuclear Information System (INIS)

    Miao He; Wang Weiguo

    2010-01-01

    Research highlights: → The corrosion resistance of V-based phase is much lower than that of C14 Laves phase of V-Ti-based alloys. → The addition of Cr which mostly distributes in V-based phase can effectively increase the anti-corrosion ability of V-Ti-based alloys. → The addition of Cr which mostly distributes in V-based phase can effectively increase the anti-corrosion ability of V-Ti-based alloys. - Abstract: In this work, the mechanisms of improving the cyclic stability of V-Ti-based hydrogen storage electrode alloys were investigated systemically. Several key factors for example corrosion resistance, pulverization resistance and oxidation resistance were evaluated individually. The V-based solid solution phase has much lower anti-corrosion ability than C14 Laves phase in KOH solution, and the addition of Cr in V-Ti-based alloys can suppress the dissolution of the main hydrogen absorption elements of the V-based phase in the alkaline solution. During the charge/discharge cycling, the alloy particles crack or break into several pieces, which accelerates their corrosion/oxidation and increases the contact resistance of the alloy electrodes. Proper decreasing the Vickers hardness and enhancing the fracture toughness can increase the pulverization resistance of the alloy particles. The oxidation layer thickness on the alloy particle surface obviously increases during charge/discharge cycling. This deteriorates their electro-catalyst activation to the electrochemical reaction, and leads to a quick degradation. Therefore, enhancing the oxide resistance can obviously improve the cyclic stability of V-Ti-based hydrogen storage electrode alloys.

  1. Effect of Cu addition on the microstructure and mechanical properties of Al–30 wt% Zn alloy

    International Nuclear Information System (INIS)

    Abd El-Rehim, A.F.; Sakr, M.S.; El-Sayed, M.M.; Abd El-Hafez, M.

    2014-01-01

    Highlights: • This paper describes a novel work on the effect of Cu addition on the Al–30 wt% Zn alloy. • The 1 wt% Cu alloy revealed the best hardness of the alloys. • The results indicated two deformation temperature regions (below and above 548 K). - Abstract: The effect of 0.5, 1, 1.5 and 2 wt% Cu addition on the microstructure and mechanical properties of Al–30 wt% Zn alloy has been investigated by stress–strain tests carried out in the temperature range from 508 to 608 K. The work-hardening parameters of the test alloys decreased with increasing the deformation temperature and exhibited discontinuity at 548 K, resulting two deformation temperature regions, the low-temperature region (below 548 K) and high-temperature region (above 548 K). The activation energy of fracture mechanisms has been calculated and found to be 19.6 and 33.2 kJ/mol at the low and high temperature regions respectively. The operating mechanisms of work-hardening of the test alloys were confirmed by the analysis of X-ray diffraction patterns

  2. Microstructure, mechanical and corrosion properties of Mg-Dy-Gd-Zr alloys for medical applications.

    Science.gov (United States)

    Yang, L; Huang, Y; Feyerabend, F; Willumeit, R; Mendis, C; Kainer, K U; Hort, N

    2013-11-01

    In previous investigations, a Mg-10Dy (wt.%) alloy with a good combination of corrosion resistance and cytocompatibility showed great potential for use as a biodegradable implant material. However, the mechanical properties of Mg-10Dy alloy are not satisfactory. In order to allow the tailoring of mechanical properties required for various medical applications, four Mg-10(Dy+Gd)-0.2Zr (wt.%) alloys were investigated with respect to microstructure, mechanical and corrosion properties. With the increase in Gd content, the number of second-phase particles increased in the as-cast alloys, and the age-hardening response increased at 200°C. The yield strength increased, while the ductility reduced, especially for peak-aged alloys with the addition of Gd. Additionally, with increasing Gd content, the corrosion rate increased in the as-cast condition owing to the galvanic effect, but all the alloys had a similar corrosion rate (~0.5 mm year(-1)) in solution-treated and aged condition. Copyright © 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  3. The effect warming time of mechanical properties and structural phase aluminum alloy nickel

    International Nuclear Information System (INIS)

    Husna Al Hasa, M.; Anwar Muchsin

    2011-01-01

    Ferrous aluminum alloys as fuel cladding will experience the process of heat treatment above the recrystallization temperature. Temperature and time of heat treatment will affect the nature of the metal. Heating time allows will affect change in mechanical properties, thermal and structure of the metal phase. This study aims to determine the effect of time of heat treatment on mechanical properties and phase metal alloys. Testing the mechanical properties of materials, especially violence done by the method of Vickers. Observation of microstructural changes made by metallographic-optical and phase structure were analyzed Based on the x-ray diffraction patterns Elemental analysis phase alloy compounds made by EDS-SEM. Test results show the nature of violence AlFeNiMg alloy by heating at 500°C with a warm-up time 1 hour, 2 hours and 3 hours respectively decreased range 94.4 HV, 87.6 HV and 85.1 HV. The nature of violence AlFeNi alloy showed a decrease in line with the longer heating time. Metallographic-optical observations show the microstructural changes with increasing heating time. Microstructure shows the longer the heating time trend equi axial shaped grain structure of growing and the results showed a trend analyst diffraction pattern formation and phase θ α phase (FeAl3) in the alloy. (author)

  4. Simulation of Intergranular Ductile Cracking in β Titanium Alloys Based on a Micro-Mechanical Damage Model.

    Science.gov (United States)

    Li, Huan; Li, Jinshan; Tang, Bin; Fan, Jiangkun; Yuan, Huang

    2017-10-30

    The intergranular crack propagation of the lamellar structure β titanium alloys is investigated by using a modified Gurson-type damage model. The representative microstructure of the lamellar alloy, which consists of the soft α phase layer surrounding the hard grain interiors, is generated based on an advanced Voronoi algorithm. Both the normal fracture due to void growth and the shear fracture associated with void shearing are considered for the grain boundary α layer. The individual phase properties are determined according to the experimental nanoindentation result and the macroscopic stress-strain curve from a uni-axial tensile test. The effects of the strain hardening exponent of the grain interiors and the void shearing mechanism of the grain boundary α layer on fracture toughness and the intergranular crack growth behavior are emphatically studied. The computational predictions indicate that fracture toughness can be increased with increasing the strain hardening ability of the grain interiors and void shearing can be deleterious to fracture toughness. Based on the current simulation technique, qualitative understanding of relationships between the individual phase features and the fracture toughness of the lamellar alloys can be obtained, which provides useful suggestions to the heat treatment process of the β titanium alloys.

  5. A systematic study of mechanical properties, corrosion behavior and biocompatibility of AZ31B Mg alloy after ultrasonic nanocrystal surface modification.

    Science.gov (United States)

    Hou, Xiaoning; Qin, Haifeng; Gao, Hongyu; Mankoci, Steven; Zhang, Ruixia; Zhou, Xianfeng; Ren, Zhencheng; Doll, Gary L; Martini, Ashlie; Sahai, Nita; Dong, Yalin; Ye, Chang

    2017-09-01

    Magnesium alloys have tremendous potential for biomedical applications due to their good biocompatibility, osteoconductivity, and degradability, but can be limited by their poor mechanical properties and fast corrosion in the physiological environment. In this study, ultrasonic nanocrystal surface modification (UNSM), a recently developed surface processing technique that utilizes ultrasonic impacts to induce plastic strain on metal surfaces, was applied to an AZ31B magnesium (Mg) alloy. The mechanical properties, corrosion resistance, and biocompatibility of the alloy after UNSM treatment were studied systematically. Significant improvement in hardness, yield stress and wear resistance was achieved after the UNSM treatment. In addition, the corrosion behavior of UNSM-treated AZ31B was not compromised compared with the untreated samples, as demonstrated by the weight loss and released element concentrations of Mg and Al after immersion in alpha-minimum essential medium (α-MEM) for 24h. The in vitro biocompatibility of the AZ31B Mg alloys toward adipose-derived stem cells (ADSCs) before and after UNSM processing was also evaluated using a cell culture study. Comparable cell attachments were achieved between the two groups. These studies showed that UNSM could significantly improve the mechanical properties of Mg alloys without compromising their corrosion rate and biocompatibility in vitro. These findings suggest that UNSM is a promising method to treat biodegradable Mg alloys for orthopaedic applications. Copyright © 2017 Elsevier B.V. All rights reserved.

  6. Mechanical decontamination techniques for floor drain systems

    International Nuclear Information System (INIS)

    Palau, G.L.

    1987-01-01

    The unprecedented nature of cleanup activities at Three Mile Island Unit 2 (TMI-2) following the 1979 accident has necessitated the development of new techniques to deal with radiation and contamination in the plant. One of these problems was decontamination of floor drain systems, which had become highly contaminated with various forms of dirt and sludge containing high levels of fission products and fuel from the damaged reactor core. The bulk of this contamination is loosely adherent to the drain pipe walls; however, significant amounts of contamination have become incorporated into pipe wall oxide and corrosion layers and embedded in microscopic pits and fissures in the pipe wall material. The need to remove this contamination was recognized early in the TMI-2 cleanup effort. A program consisting of development and laboratory testing of floor drain decontamination techniques was undertaken early in the cleanup with support from the Electric Power Research Institute (EPRI). Based on this initial research, two techniques were judged to show promise for use at TMI-2: a rotating brush hone system and a high-pressure water mole nozzle system. Actual use of these devices to clean floor drains at TMI-2 has yielded mixed decontamination results. The decontamination effectiveness that has been obtained is highly dependent on the nature of the contamination in the drain pipe and the combination of decontamination techniques used

  7. Causes and mechanisms of thermal embrittlement and corrosion cracking of complex α-titanium alloys

    International Nuclear Information System (INIS)

    Ushkov, S.S.; Rybin, V.V.; Razuvaeva, I.N.; Nesterova, E.V.; Gunbina, O.A.

    1995-01-01

    Effect of aging under 500 deg C on mechanical and corrosion-mechanical properties of Ti-6Al base titanium α-alloys with zirconium and carbon additions is studied. Using electron microscopy one determines the reasons of reduction of plasticity and of corrosion-mechanical strength of alloys after aging. It is determined that in the given alloys there are two different processes with occurrence different kinetics: the first one-formation of grain-boundary precipitations of Ti 2 (Fe, Ni) intermetallic compound responsible for plasticity reduction; and the second one-homogeneous decomposition of Ti-Al solid solution responsible for reduction of corrosion-mechanical properties. 14 refs., 6 figs

  8. Development in corrosion resistance by microstructural refinement in Zr-16 SS 304 alloy using suction casting technique

    Energy Technology Data Exchange (ETDEWEB)

    Das, N., E-mail: nirupamd@barc.gov.in; Sengupta, P.; Abraham, G.; Arya, A.; Kain, V.; Dey, G.K.

    2016-08-15

    Highlights: • Grain refinement was made in Zr–16 wt.% SS alloy while prepared by suction casting process. • Distribution of Laves phase, e.g., Zr{sub 2}(Fe, Cr) was raised in suction cast (SC) Zr–16 wt.% SS. • Corrosion resistance was improved in SC alloy compared to that of arc-melt-cast alloy. • Grain refinement in SC alloy assisted for an increase in its corrosion resistance. - Abstract: Zirconium (Zr)-stainless steel (SS) hybrid alloys are being considered as baseline alloys for developing metallic-waste-form (MWF) with the motivation of disposing of Zr and SS base nuclear metallic wastes. Zr–16 wt.% SS, a MWF alloy optimized from previous studies, exhibit significant grain refinement and changes in phase assemblages (soft phase: Zr{sub 2}(Fe, Cr)/α-Zr vs. hard phase: Zr{sub 3}(Fe, Ni)) when prepared by suction casting (SC) technique in comparison to arc-cast-melt (AMC) route. Variation in Cr-distribution among different phases are found to be low in suction cast alloy, which along with grain refinement restricted Cr-depletion at the Zr{sub 2}(Fe, Cr)/Zr interfaces, prone to localized attack. Hence, SC alloy, compared to AMC alloy, showed lower current density, higher potential at the breakdown of passivity and higher corrosion potential during polarization experiments (carried out under possible geological repository environments, viz., pH 8, 5 and 1) indicating its superior corrosion resistance.

  9. Microstructure and Mechanical Properties of Inconel 625 Alloy on Low Carbon Steel by Heat Treatment after Overlay Welding

    International Nuclear Information System (INIS)

    Kim, Seungpil; Jang, Jaeho; Kim, Jungsoo; Kim, Byung Jun; Sohn, Keun Yong; Nam, Dae-Geun

    2016-01-01

    Overlay welding technique is one of methods used to improve metal mechanical properties such as strength, toughness and corrosion resistance. Generally, Inconel 625 alloy is used for overlay welding layer on low carbon steels for economic consideration. However, the method produces some problems in the microstructure of the cast structure and some defects, caused by the elevated temperatures of the overlay process. To resolve these problems, heat treatments are required. In this study, Inconel 625 alloy was welded on a low carbon steel by the overlay welding process to investigate the resulting microstructure and mechanical properties. A double heat treatment was performed to improve the mechanical properties of the welding and substrate layers. It was found that Inconel 625 alloy had an austenite microstructure after the first heat treatment, but the low carbon steel had a ferrite-pearlite microstructure after the second heat treatment. After the double heat treatment, the sample showed the optimum hardness because of grain refinement and homogenization of the microstructure.

  10. Microstructure and Mechanical Properties of Inconel 625 Alloy on Low Carbon Steel by Heat Treatment after Overlay Welding

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Seungpil; Jang, Jaeho; Kim, Jungsoo; Kim, Byung Jun; Sohn, Keun Yong; Nam, Dae-Geun [Korea Institute of Industrial Technology, Busan (Korea, Republic of)

    2016-08-15

    Overlay welding technique is one of methods used to improve metal mechanical properties such as strength, toughness and corrosion resistance. Generally, Inconel 625 alloy is used for overlay welding layer on low carbon steels for economic consideration. However, the method produces some problems in the microstructure of the cast structure and some defects, caused by the elevated temperatures of the overlay process. To resolve these problems, heat treatments are required. In this study, Inconel 625 alloy was welded on a low carbon steel by the overlay welding process to investigate the resulting microstructure and mechanical properties. A double heat treatment was performed to improve the mechanical properties of the welding and substrate layers. It was found that Inconel 625 alloy had an austenite microstructure after the first heat treatment, but the low carbon steel had a ferrite-pearlite microstructure after the second heat treatment. After the double heat treatment, the sample showed the optimum hardness because of grain refinement and homogenization of the microstructure.

  11. Development of simultaneous wire feeding mechanism for nano alloy powder synthesis

    Energy Technology Data Exchange (ETDEWEB)

    Rhee, Chang Kyu [KAERI, Taejon (Korea, Republic of); Kotov, Yury A.; Samatov, Oleg M.; Beketov, Igor V.; Azarkevich, Evgeny I.; Muzarkaev, Aidar M. [Institute of Electrophysics (Russian Federation)

    2002-12-01

    In accordance with the Local Lab project, it was necessary to design a mechanism for simultaneous feed of two wires to the explosion chamber and consider the possibility of developing a model for selection of wire parameters. The goal of the work is to explore the possibility of producing powdered mixtures, alloys and intermetallic compounds by a simultaneous electric explosion of two wires made of different metals. A mechanism providing a synchronous feed of two wires to the explosion chamber and their simultaneous electric explosion extends considerably the capabilities of the electric explosion method in production of nanopowders. In this work, we developed simultaneous wire feeding mechanism for alloy nano powders successfully.

  12. Development of simultaneous wire feeding mechanism for nano alloy powder synthesis

    International Nuclear Information System (INIS)

    Rhee, Chang Kyu; Kotov, Yury A.; Samatov, Oleg M.; Beketov, Igor V.; Azarkevich, Evgeny I.; Muzarkaev, Aidar M.

    2002-12-01

    In accordance with the Local Lab project, it was necessary to design a mechanism for simultaneous feed of two wires to the explosion chamber and consider the possibility of developing a model for selection of wire parameters. The goal of the work is to explore the possibility of producing powdered mixtures, alloys and intermetallic compounds by a simultaneous electric explosion of two wires made of different metals. A mechanism providing a synchronous feed of two wires to the explosion chamber and their simultaneous electric explosion extends considerably the capabilities of the electric explosion method in production of nanopowders. In this work, we developed simultaneous wire feeding mechanism for alloy nano powders successfully

  13. Magnetic transition induced by mechanical deformation in Fe{sub 60}Al{sub 40−x}Si{sub x} ternary alloys

    Energy Technology Data Exchange (ETDEWEB)

    Legarra, E., E-mail: estibaliz.legarra@ehu.es [Dpto. Electricidad y Electronica, Universidad del Pais Vasco (UPV/EHU), CP. 644, 48080 Bilbao (Spain); Apiñaniz, E. [Dpto. Fisica Aplicada I, Universidad del Pais Vasco, Alameda de Urquijo s/n, 48013 Bilbao (Spain); Plazaola, F. [Dpto. Electricidad y Electronica, Universidad del Pais Vasco (UPV/EHU), CP. 644, 48080 Bilbao (Spain); Jimenez, J.A. [Centro Nacional de Investigaciones Metalurgicas (CENIM), Avda. Gregorio del amo 8, 28040 Madrid (Spain)

    2014-02-15

    Highlights: • Fe{sub 60}Al{sub 40−x}Si{sub x} alloys were disordered by means of planetary ball milling technique. • Paramagnetic to ferromagnetic transition is observed with disordering. • Si addition hinders the disordering process and the increase of the lattice parameter. • Si addition promotes the paramagnetic to ferromagnetic transition. -- Abstract: We have used Mössbauer spectroscopy and X-ray diffraction to study the influence of different Al/Si ratios on the structural and magnetic properties of the mechanically deformed Fe{sub 60}Al{sub 40−x}Si{sub x} alloys. The results indicate that ternary alloys also present the magnetic transition with disordering observed in binary Fe{sub 60}Al{sub 40} alloys. Besides, Si introduction has two opposite contributions. From a structural point of view, hinders the disordering process, but, from a magnetic point of view promotes the magnetic transition.

  14. Effect of temperature on synthesis and properties of aluminum-magnesium mechanical alloys

    International Nuclear Information System (INIS)

    Umbrajkar, Swati M.; Schoenitz, Mirko; Jones, Steven R.; Dreizin, Edward L.

    2005-01-01

    The synthesis of an Al 0.7 Mg 0.3 mechanical alloy was studied using a planetary mill. Several distinct temperature regimes of mechanical alloying were achieved using milling jars equipped with finned heat sinks and an external air conditioner installed to cool the entire milling chamber. Wireless temperature sensors were attached to the milling jars to monitor the process temperature. Intermediate and final products were collected and were analyzed by electron microscopy and X-ray diffraction. The temperature history of the milling jars exhibited two peaks during mechanical alloying. The first peak occurred when particles of the starting powders deformed to produce flakes. The second peak was observed when the flakes agglomerated and re-fragmented forming layered composites that served as precursors for the mechanical alloy. The temperature of milling affected the magnesium solubility of the produced Al-Mg mechanical alloys. Decreasing the milling temperature from ∼70-80 deg. C to 20-30 deg. C resulted in an increase of the dissolved Mg concentration in Al from 2-3 at.% to ∼25 at.% for the Al 0.7 Mg 0.3 composition. The formation of intermetallic phases was favored at higher milling temperatures, where high solubilities cannot be achieved

  15. Effect of temperature on synthesis and properties of aluminum-magnesium mechanical alloys

    Energy Technology Data Exchange (ETDEWEB)

    Umbrajkar, Swati M. [New Jersey Institute of Technology, Department of Mechanical Engineering, Newark, NJ 07102-1982 (United States); Schoenitz, Mirko [New Jersey Institute of Technology, Department of Mechanical Engineering, Newark, NJ 07102-1982 (United States); Jones, Steven R. [New Jersey Institute of Technology, Department of Mechanical Engineering, Newark, NJ 07102-1982 (United States); Dreizin, Edward L. [New Jersey Institute of Technology, Department of Mechanical Engineering, Newark, NJ 07102-1982 (United States)]. E-mail: dreizin@njit.edu

    2005-10-27

    The synthesis of an Al{sub 0.7}Mg{sub 0.3} mechanical alloy was studied using a planetary mill. Several distinct temperature regimes of mechanical alloying were achieved using milling jars equipped with finned heat sinks and an external air conditioner installed to cool the entire milling chamber. Wireless temperature sensors were attached to the milling jars to monitor the process temperature. Intermediate and final products were collected and were analyzed by electron microscopy and X-ray diffraction. The temperature history of the milling jars exhibited two peaks during mechanical alloying. The first peak occurred when particles of the starting powders deformed to produce flakes. The second peak was observed when the flakes agglomerated and re-fragmented forming layered composites that served as precursors for the mechanical alloy. The temperature of milling affected the magnesium solubility of the produced Al-Mg mechanical alloys. Decreasing the milling temperature from {approx}70-80 deg. C to 20-30 deg. C resulted in an increase of the dissolved Mg concentration in Al from 2-3 at.% to {approx}25 at.% for the Al{sub 0.7}Mg{sub 0.3} composition. The formation of intermetallic phases was favored at higher milling temperatures, where high solubilities cannot be achieved.

  16. Transport mechanisms in the laser alloying of metals

    Science.gov (United States)

    Pawlak, Ryszard; Tomczyk, Mariusz; Walczak, Maria

    2003-10-01

    This article presents some investigations of a laser alloyed surface layer of nickel doped with gold and of copper doped with aluminum. The velocity of the convectino flow in the laser pool predicted by computation implies that there may exist good miscibility for the range of components different from those obtained by the conventional method. This indicates a predominant role of the Marangoni convection for mixing elements. Some metallurgical cross-sections of Ni-Au; Mo-Au; Cu-Al; Cu-Au layers, alloyed by an Nd-YAG laser, for different contents of doping elements are presented. They may be interesting information about miscibility of these metals during laser pulse τ1=4ms.

  17. Effects of Sm addition on microstructure and mechanical properties of a Mg-10Y alloy

    Directory of Open Access Journals (Sweden)

    Li Quanan

    2014-01-01

    Full Text Available To further increase the mechanical properties, 0.5wt.% Sm was introduced to a Mg-10Y alloy in this study. The effects of Sm addition on the microstructures and mechanical properties of the Mg-10Y alloy, especially the aged Mg-10Y alloy, were investigated. The microstructure observation and tensile tests were performed by using an optical microscopy, a scanning electron microscopy and a universal material testing machine, respectively. The phase analysis was performed using X-ray diffractometer. The results show that the 0.5wt.% Sm addition can not only promote the formation of fine and dispersed Mg24Y5 phases, but also improve their morphology and distribution; it also increases the thermal stability of Mg24Y5 phases. Sm addition is seen to increase the ultimate tensile strength of Mg-10Y alloy at elevated temperatures (200, 250, 300 and 350 ℃, while decrease the elongation. But the elongation is still up to 7.5% even at 350 ℃. In the range of 250 ℃ to 300℃, the ultimate tensile strength of the alloy reaches its maximum (with a range average of 235 MPa and is not sensitive to the temperature change, which is very useful to the application of heat-resistant magnesium alloys. Even at 350 ℃, the ultimate tensile strength of Mg-10Y-0.5Sm is still up to 155 MPa. Considering both of the ultimate tensile strength and elongation, the maximum application temperature of the Mg-10Y-0.5Sm alloy can be up to 300 ℃. The strengthening mechanisms of Mg-10Y-0.5Sm alloy are mainly attributed to dispersion strengthening of Mg24Y5 phase particles with a certain solubility of Sm and grain refinement strengthening of α-Mg matrix.

  18. Development of mechanical properties in a CaO added AZ31 magnesium alloy processed by equal-channel angular pressing

    International Nuclear Information System (INIS)

    Bae, Seong-Hwan; Jung, Ki Ho; Shin, Young-Chul; Yoon, Duk Jae; Kawasaki, Megumi

    2016-01-01

    Processing through the application of equal-channel angular pressing (ECAP) is recognized as one of the attractive severe plastic deformation techniques where the processed bulk metals generally achieve ultrafine-grained microstructure leading to improved physical characteristics and mechanical properties. Magnesium has received much attention to date for its lightweight, high strength and excellent elasticity. Mg alloys with addition of CaO is reported to provide the successful casting procedure without usage of greenhouse gas, SF 6 , whereas it is generally used for preventing the oxidation of Mg during casting. In the present investigation, a CaO added AZ31 (AZ31-CaO) magnesium alloy was processed by ECAP at elevated temepratures with a few steps of reduction which result in significant grain refinement to ~ 1.5 μm after 6 passes. Compression testing at room temperature demonstrated the AZ31-CaO alloy after ECAP showed enhanced yield strength more than the as-processed commercial AZ31 alloy while both alloys maintained ductility in spite of significant reduction in grain size. The improved strength in the AZ31-CaO alloy was attributed to the formation of fine Al 2 Ca precipitates which experience breaking-up through ECAP and accelerate the microstructural refinement. Moreover, the preservation of ductility was attributed to the enhancement of strain hardening capability in the AZ31 alloy at room temperature. This study discusses the feasibility of using ECAP to improve both strength and ductility on magnesium alloys by applying the diagram describing the paradox of strength and ductility. - Highlights: • AZ31 and AZ31-CaO magnesium alloys were processed by ECAP up to 6 passes. • AZ31-CaO alloy after ECAP showed improved yield strength without losing ductility. • CaO in AZ31 forms fine Al 2 Ca accelerating microstructural refinement during ECAP. • Feasibility of using ECAP was shown to improve both strength and ductility in Mg.

  19. Effects of heat treatment on the microstructure and mechanical properties of AA2618 DC cast alloy

    International Nuclear Information System (INIS)

    Elgallad, E.M.; Shen, P.; Zhang, Z.; Chen, X.-G.

    2014-01-01

    Highlights: • The microstructure and mechanical properties of AA2618 DC cast alloy were studied. • The Al 2 CuMg, Al 2 Cu, Al 7 Cu 4 Ni, Al 7 Cu 2 (Fe,Ni) and Al 9 FeNi phases were identified. • Solution treatment at 530 °C for 5 h is the optimum solution treatment. • Different combinations of strength and ductility can be achieved. • The strengthening of AA2618 DC cast alloy was caused by GPB zones and S′ phase. - Abstract: Direct chill (DC) cast ingot plates of AA2618 alloy have been increasingly used for large-mold applications in the plastics and automotive industries. The effects of different heat treatments on the microstructure and mechanical properties of AA2618 DC cast alloy were investigated using scanning electron microscopy (SEM), transmission electron microscopy (TEM) and hardness and tensile testing. The as-cast microstructure contained a considerable amount of coarse intermetallic phases, including Al 2 CuMg, Al 2 Cu, Al 7 Cu 4 Ni, Al 7 Cu 2 (Fe,Ni) and Al 9 FeNi, resulting in poor mechanical properties. Solution treatment at 530 °C for 5 h dissolved the first three phases into the solid solution and consequently improved the mechanical properties of the alloy. By utilizing the appropriate aging temperature and time, different combinations of strength and ductility could be obtained to fulfill the design requirements of large-mold applications. The strengthening of AA2618 DC cast alloy under the aging conditions studied was caused by GPB zones and S′ precipitates. The evolution of both precipitates in terms of their size and density was observed to have a significant effect on the mechanical properties of the alloy

  20. Microstructure, mechanical properties, bio-corrosion properties and antibacterial properties of Ti-Ag sintered alloys.

    Science.gov (United States)

    Chen, Mian; Zhang, Erlin; Zhang, Lan

    2016-05-01

    In this research, Ag element was selected as an antibacterial agent to develop an antibacterial Ti-Ag alloy by a powder metallurgy. The microstructure, phase constitution, mechanical properties, corrosion resistance and antibacterial properties of the Ti-Ag sintered alloys have been systematically studied by X-ray diffraction (XRD), scanning electron microscope (SEM), compressive test, electrochemical measurements and antibacterial test. The effects of the Ag powder size and the Ag content on the antibacterial property and mechanical property as well as the anticorrosion property have been investigated. The microstructure results have shown that Ti-Ag phase, residual pure Ag and Ti were the mainly phases in Ti-Ag(S75) sintered alloy while Ti2Ag was synthesized in Ti-Ag(S10) sintered alloy. The mechanical test indicated that Ti-Ag sintered alloy showed a much higher hardness and the compressive yield strength than cp-Ti but the mechanical properties were slightly reduced with the increase of Ag content. Electrochemical results showed that Ag powder size had a significant effect on the corrosion resistance of Ti-Ag sintered alloy. Ag content increased the corrosion resistance in a dose dependent way under a homogeneous microstructure. Antibacterial tests have demonstrated that antibacterial Ti-Ag alloy was successfully prepared. It was also shown that the Ag powder particle size and the Ag content influenced the antibacterial activity seriously. The reduction in the Ag powder size was benefit to the improvement in the antibacterial property and the Ag content has to be at least 3wt.% in order to obtain a strong and stable antibacterial activity against Staphylococcus aureus bacteria. The bacterial mechanism was thought to be related to the Ti2Ag and its distribution. Copyright © 2016 Elsevier B.V. All rights reserved.

  1. Effect of La addition on the microstructure and mechanical properties of Mg–6 wt% Zn alloys

    Energy Technology Data Exchange (ETDEWEB)

    Du, Yuzhou, E-mail: duyuzhou@xaut.edu.cn [School of Materials Science and Engineering, Xi' an University of Technology, Xi' an 710048 (China); School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001 (China); Zheng, Mingyi, E-mail: zhenghe@hit.edu.cn [School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001 (China); Qiao, Xiaoguang [School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001 (China); Peng, Wenqiang [Institute of Chemical Materials, China Academy of Engineering Physics, Mianyang 621999 (China); Jiang, Bailing [School of Materials Science and Engineering, Xi' an University of Technology, Xi' an 710048 (China)

    2016-09-15

    The Mg–6 wt% Zn alloys microalloyed with different amounts of La were cast and extruded. The second phase in the as-cast Mg–Zn alloy is Mg{sub 4}Zn{sub 7}, which was replaced by Mg–Zn–La intermetallics with orthorhombic structure after La addition. Microalloying with La refined the grain size of dynamic recrystallization slightly, which was due to La solute atom in α-Mg alloy. Addition of La weakened the texture and gave rise to the formation of non-basal texture component, attributing to the existence of La in the form of solute atoms in matrix. The ductility was enhanced significantly by adding La to Mg–6 wt% Zn alloy, while the strength was reduced. Such phenomenon was related to the weakening texture of the La containing alloys. The Mg–6Zn–0.2La (wt%) alloy exhibited a superior ductility with the elongation-to-fracture up to 35%. However, with further increasing of La content to 1 wt%, the strength of the as-extruded Mg–Zn–La alloys was not improved but the ductility was reduced, suggesting that small addition of La is preferred for the improvement of mechanical properties.

  2. Study on Friction and Wear Characteristics of Aluminum Alloy Hydraulic Valve Body and Its Antiwear Mechanism

    Directory of Open Access Journals (Sweden)

    Rong Li

    2017-03-01

    Full Text Available In order for the working status of the aluminum alloyed hydraulic valve body to be controlled in actual conditions, a new friction and wear design device was designed for the cast iron and aluminum alloyed valve bodies comparison under the same conditions. The results displayed that: (1 The oil leakage of the aluminum alloyed hydraulic valve body was higher than the corresponding oil leakage of the iron body during the initial running stage. Besides during a later running stage, the oil leakage of the aluminum alloyed body was lower than corresponding oil leakage of the iron body; (2 The actual oil leakage of different materials consisted of two parts: the foundation leakage that was the leakage of the valve without wear and wear leakage that was caused by the worn valve body; (3 The aluminum alloyed valve could rely on the dust filling furrow and melting mechanism that led the body surface to retain dynamic balance, resulting in the valve leakage preservation at a low level. The aluminum alloy modified valve body can meet the requirements of hydraulic leakage under pressure, possibly constituting this alloy suitable for hydraulic valve body manufacturing.

  3. Mechanical properties of molybdenum alloyed liquid phase-sintered tungsten-based composites

    International Nuclear Information System (INIS)

    Kemp, P.B.; German, R.M.

    1995-01-01

    Tungsten-based composites are fabricated from mixed elemental powders using liquid phase sintering, usually with a nickel-iron matrix. During sintering, the tungsten undergoes grain growth, leading to microstructure coarsening that lowers strength but increases ductility. Often the desire is to increase strength at the sacrifice of ductility, and historically, this has been performed by postsintering deformation. There has been considerable research on alloying to adjust the as-sintered mechanical properties to match those of swaged alloys. Prior reports cover many additions, seemingly including much of the periodic table. Unfortunately, many of the modified alloys proved disappointing, largely due to degraded strength at the tungsten-matrix interface. Of these modified alloys, the molybdenum-containing systems exhibit a promising combination of properties, cost, and processing ease. For example, the 82W-8Mo-7Ni-3Fe alloy gives a yield strength that is 34% higher than the equivalent 90W-7Ni-3Fe alloy (from 535 to 715 MPa) but with a 33% decrease in fracture elongation (from 30 to 20% elongation). This article reports on experiments geared to promoting improved properties in the W-Mo-Ni-Fe alloys. However, unlike the prior research which maintained a constant Ni + Fe content and varied the W:Mo ratio, this study considers the Mo:(Ni + Fe) ratio effect for 82, 90, and 93 wt pct W

  4. Effect of Fe-Content on the Mechanical Properties of Recycled Al Alloys during Hot Compression

    Directory of Open Access Journals (Sweden)

    Hongzhou Lu

    2017-07-01

    Full Text Available It is unavoidable that Fe impurities will be mixed into Al alloys during recycling of automotive aluminum parts, and the Fe content has a significant effect on the mechanical properties of the recycled Al alloys. In this work, hot compression tests of two Fe-containing Al alloys were carried out at elevated temperatures within a wide strain rate range from 0.01 s−1 to 10 s−1. The effect of Fe content on the peak stress of the stress vs. strain curves, strain rate sensitivity and activation energy for dynamic recrystallization are analyzed. Results show that the recycled Al alloy containing 0.5 wt % Fe exhibits higher peak stresses and larger activation energy than the recycled Al alloy containing 0.1 wt % Fe, which results from the fact that there are more dispersed AlMgFeSi and/or AlFeSi precipitates in the recycled Al alloy containing 0.5 wt % Fe as confirmed by SEM observation and energy spectrum analysis. It is also shown that the Fe content has little effect on the strain rate sensitivity of the recycled Al alloys.

  5. Age hardening in mechanically alloyed Al-Mg-Li-C-O

    Energy Technology Data Exchange (ETDEWEB)

    Papazian, J.M. (Corporate Research Center, Grumman Corporation, Bethpage, NY (USA)); Gilman, P. (Allied-Signal Inc., Morristown, NJ (USA))

    1990-05-01

    The age-hardening behavior of a series of mechanically alloyed Al-Mg-Li-C-O alloys containing 3.0-4.0 wt.% Mg and 1.3-1.75 wt.% Li was studied using hardness tests, differential scanning calorimetry (DSC) and transmission electron microscopy. The hardness tests showed an increased hardness after 100degC aging in all the alloys containing at least 1.5 at.% Li. Likewise, the calorimetry results showed the presence of pronounced precipitate dissolution peaks in these same alloys after 100degC aging. The volume fraction of precipitates formed (as measured by the dissolution enthalpies of the DSC peaks) increased systematically with increasing solute content. Transmission electron microscopy after 100 and 190degC aging showed images and diffraction spots similar to those of {delta}' (Al{sub 3}Li). Comparison of the DSC results with results from binary Al-Li and Al-Mg alloys indicated that the precipitates formed in the Al-Mg-Li-C-O alloys were similar to those formed in binary Al-Li alloys, and that the primary role of the magnesium was to lower the solid solubility of lithium. (orig.).

  6. Investigations of intermetallic alloy hydriding mechanisms. Annual progress report, May 1 1979-April 30, 1980

    International Nuclear Information System (INIS)

    Livesay, B.R.; Larsen, J.W.

    1980-05-01

    Investigations are being conducted on mechanisms involved with the hydrogen-metal interactions which control the absorption and desorption processes in intermetallic compounds. The status of the following investigations is reported: modeling of hydride formation; microbalance investigations; microstructure investigations; flexure experiments; resistivity experiments; and nuclear backscattering measurements. These investigations concern fundamental hydrogen interaction mechanisms involved in storage alloys

  7. Mechanical properties and microstructure of laser treated Al-Cu-Mg alloys

    NARCIS (Netherlands)

    Hosson, J.Th.M. De; Noordhuis, J.

    1993-01-01

    The mechanical properties and microstructural features of Al-Cu-Mg alloys were investigated, as exposed to laser treatments at various scan velocities. As far as the mechanical property is concerned a striking observation is a minimum in the hardness value at a laser scan velocity of 1/2 cm/s.