Sample records for low-temperature electron irradiation

  1. Defects in low temperature electron irradiated InP

    International Nuclear Information System (INIS)

    Suski, J.; Bourgoin, J.

    1984-01-01

    n and p-InP has been irradiated at 25K with 1MeV electrons and the created defects were studied by deep level transient spectroscopy (DLTS) in the range 25K-400K. In n-InP, four traps are directly observed, with low introduction rates except for one. They anneal in three stages, and four new centers of still lower concentration appear after 70 0 C heat treatment. In p-InP, two dominant traps stable up to approx.= 400K with introduction rates close to the theoretical ones, which might be primary defects are found, while another one is clearly a secondary defect likely associated to Zn dopant. At least two of the low concentration irradiation induced electron traps, created between 25K and 100K are also secondary defects, which implies a mobility of some primary defects down to 100K at least. (author)

  2. A low temperature cryostat with a refrigerator for studying electron irradiation effects on solids

    International Nuclear Information System (INIS)

    Oka, Takashi; Yoshida, Toshio; Kitagawa, Michiharu; Yanai, Masayoshi

    1976-01-01

    A low temperature cryostat with a small cryogenic refrigerator is described which is convenient for studying irradiation effects of the energetic electrons on solids. It allows a sample to be kept about 12 K without irradiation and 15 K under the irradiation at a heating rate of 1.5 w. The sample temperature can be changed up to room temperature by adjusting the power of an attached heater and the pressure of a compressor for the refrigerator. The optical and electrical properties of the sample can be measured under and after irradiation. (auth.)

  3. Defect reactions on the phosphorus sublattice in low-temperature electron-irradiated InP

    International Nuclear Information System (INIS)

    Sibille, A.; Suski, J.

    1985-01-01

    This Rapid Communication describes several thermally or electronically stimulated defect reactions involving the dominant deep centers in low-temperature (25--300 K) electron-irradiated InP. Some of these reactions result in an increased concentration of the centers, thereby revealing the existence of a secondary production mechanism of the related defects. Low-energy irradiations allows one to select the type of the ejected atom (P) and gives direct evidence that only a phosphorus species, interstitial or vacancy, is involved in the creation-reaction-annealing events

  4. Electron migration in hydrated biopolymers following pulsed irradiation at low temperatures

    International Nuclear Information System (INIS)

    Lith, D. van.

    1987-01-01

    Charge migration in biopolymer-water mixtures and the effect of water concentration on the charge migration is investigated by measuring the electrical conductivity and the light emission with the pulse radiolysis technique. A preliminary account of the microwave conductivity observed in hydrated DNA and collagen at low temperature after pulsed irradiation is given. The results show that when hydrated DNA or collagen are irradiated at low temperatures, conductivity transients with microsecond lifetime are observed. It is tentatively concluded that these transients are due to the highly mobile dry electron. The effect of water concentration on mobility, lifetime and migration distance of the electron is discussed. The effect of additives to the hydrated systems on the behaviour of the electron is described. It is shown that the observed effects of the additives confirm the earlier conclusions that the dry electron is the species responsible for the radiation induced conductivity. The water concentration in the DNA- and collagen-systems could be varied only between zero and approximately fifty percent, due to inhomogeneities which occur at higher water concentrations. Experiments on gelatin, a biopolymer which forms homogeneous samples with levels of hydration varying from almost zero to 100% water (ice) are described. Both the radiation induced and the dark microwave conductivity have been studied as a function of water content. Preliminary results of a study of the light emission from pulse irradiated DNA-water mixtures are reported in an attempt to establish a relation between the observed electron migration and the formation of excited states via charge neutralization. (Auth.)

  5. Further study of the glassy low-temperature properties of irradiated crystalline quartz: neutron and electron irradiation

    International Nuclear Information System (INIS)

    Laermans, C.; Daudin, B.

    1979-01-01

    Recently it has been shown that a quartz crystal after light fast neutron irradiation shows low temperature hypersonic properties which are similar to those found in glasses although the sample was still crystalline. Additional measurements have been carried out in the neutron-irradiated sample and a sample irradiated with high energy electrons has also been investigated. (Fast neutron dose 6 x 10 18 n/cm 2 , 2 MeV electron dose 3 x 10 19 e/cm 2 ). A magnetic field up to 1.5 T was found to have no influence in the hypersonic saturation behaviour of the neutron-irradiated sample (9 GHz, 1.65 K) and thermal conductivity measurements are consistent with a number of two level systems (2 LS) an order of magnitude lower than in vitreous silica as found before. Low temperature hypersonic measurements as a function of acoustic intensity and temperature as well as thermal conductivity measurements give no evidence for the presence of 2 LS in the electron irradiated sample. Considering the damage created in both samples this indicates that 2 LS are probably not related to point defects

  6. Low temperature electron beam irradiation effects on the lactate dehydrogenase activity

    International Nuclear Information System (INIS)

    Catana, D.; Hategan, Alina; Oproiu, C.; Popescu, Alina; Hategan, Dora; Morariu, V. V.

    1998-01-01

    The direct and indirect effects of 5 MeV electron beam irradiation in the range 0-400 Gy at 20 deg. C, -3 deg. C and -196 deg. C on the global enzymatic activity of lactate dehydrogenase (LDH) have been studied. Our results showed a monoexponential decrease in the enzymatic activity of irradiated LDH at all irradiation temperatures independently of direct or indirect action of radiation. The temperature gradient used to lower the temperature of the samples to -196 deg. C drastically influences the results. Our data suggest that freeze-thawing in two steps down to -196 deg. C make LDH insensitive to irradiation, while one step freeze-thawing procedure results in a gradual activity loss with increasing dose irradiation. This data can be interpreted in terms of different conformational changes during the particular freeze-thawing process. (authors)

  7. Low-temperature annealing of radiation defects in electron-irradiated gallium phosphide

    International Nuclear Information System (INIS)

    Kolb, A.A.; Megela, I.G.; Buturlakin, A.P.; Goyer, D.B.

    1990-01-01

    The isochronal annealing of radiation defects in high-energy electron irradiated n-GaP monocrystals within the 77 to 300 K range has been investigated by optical and electrical techniques. The changes in conductance and charge carrier mobility as functions of annealing temperature as well as the variation of optical absorption spectra of GaP under irradiation and annealing provide evidence that most of radiation defects are likely secondary complexes of defects

  8. A low temperature cryostat with a refrigerator for studying electron-irradiation effects on solids, 2

    International Nuclear Information System (INIS)

    Oka, Takashi; Yoshida, Toshio; Shono, Yoshihiko

    1978-01-01

    A convenient cryostat with a small cryogenic refrigerator for studying electron-irradiation effects on solids is reported. The lowest temperature at the sample room is about 10 K or less. In a temperature region below 80 K, the sample temperature can be controlled within 0.05 K. (auth.)

  9. Observation of magnetically anisotropic defects during stage I recovery in nickel after low-temperature electron irradiation

    International Nuclear Information System (INIS)

    Forsch, K.; Hemmerich, J.; Knoll, H.; Lucki, G.

    1974-01-01

    The measurement of defect-induced changes of magnetic anisotropy in a nickel single crystal after low-temperature electron irradiation was undertaken. A dynamic measuring method was used after reorienting a certain fraction of the radiation-induced defects in an external magnetic field of 5 kOe. In the temperature range of recovery stage I sub(C,D,E) (45 to 60 k) the crystallographic direction dependence of defect-induced anisotropy could be determined. The results show that in this temperature range the (100) split interstitial is mobile and able to reorient. The obtained data are further discussed with respect to existing information on magnetic after effect and resistivity annealing in electron-irradiated nickel

  10. Study of the effect of neutron and electron irradiations on the low temperature thermal conductivity of germanium and silicon

    International Nuclear Information System (INIS)

    Vandevyver, M.

    1967-06-01

    The main results obtained from this work are the following: 1 Neutron irradiation (at 300 deg. K) produces lattice defects in germanium and silicon, and a corresponding very large lowering of the thermal conductivity is observed in the low temperature region (4-300 ). The results obtained have been explained with the help of the following hypotheses: for silicon a scattering of phonons by the stress fields produced by the defects; for germanium, a supplementary scattering of the electron phonon type. 2 Annealing treatments carried out on these materials above 373 deg. K restored the thermal conductivity over the whole temperature range of the measurements (4-300 deg. K); in the case of both germanium and silicon there were two steps in the annealing process. 3 A study of the thermal conductivity of germanium (initially P or N) after an electronic irradiation showed that the scattering of phonons could depend on the state of charge of the defects thus produced. (author) [fr

  11. Low-temperature electron irradiation induced defects in gallium arsenide: bulk and surface acoustic wave studies

    International Nuclear Information System (INIS)

    Brophy, M.J. Jr.

    1985-01-01

    Irradiation of GaAs with 2.25 to 2.5 MeV electrons at temperatures below 190 K produces two peaks in ultrasonic attenuation versus temperature. The defects responsible for both peaks have trigonal symmetry and were observed in n-type and semi-insulating GaAs with bulk and surface acoustic waves (SAW) respectively. Bulk waves at eight frequencies between 9 and 130 MHz and SAW at 73 and 145 MHz were used. The reorientation kinetics of both peaks follow the Arrhenius law. The annealing of both peaks was studied with isochronal and isothermal anneals in the temperature range 200 to 335 K. Peak I anneals with a spectrum of activation energies in the range 0.7-1.1 eV between 220 and 335 K. Peak II anneals with a single activation energy of about 1.1 eV above 300K. The different annealing characteristics indicate that these peaks represent two distinct defects. The annealing above 300 K has not been seen in electrical resistivity measurements, but was observed in earlier length change experiments. Irradiation of GaAs:Cr produces no Cr-radiation defect complexes. The attenuation peak associated with Cr 2+ decrease with electron dose, but starts to recover at 150 K

  12. Wolte 5. low temperature electronics

    International Nuclear Information System (INIS)

    Balestra, F.; Dieudonne, F.; Jomaah, J.

    2002-01-01

    This book present the latest research and development results in advanced materials, technologies, devices, circuits and systems for low temperature electronics. The main themes of the papers are ranging from physics and fundamental aspects, modeling and simulation, to device and circuit design. The topics include advanced process and characterization, novel devices and cryogenic instrumentation. The papers are divided into nine sections, reflecting the main research efforts in different areas: i) deep submicron silicon MOSFETs, ii) alternative MOSFETs (SOI, innovating device architectures), iii) III-V devices, iv) other semiconductor devices (Ge devices, p-n junctions, IR sensors, semiconductor microcrystals), v) emerging devices and phenomena (nano Si-based devices, conduction and fluctuations mechanisms), vi) superconducting materials, vii) superconducting detectors, viii) superconducting devices and circuits (RSFQ, SIS mixers, metal-superconducting-semiconductor structures), ix) low temperature electronics for space applications. Six invited papers presented by internationally recognized authors, and 39 contributed papers are presented. The invited papers provide an excellent overview of today's status and progress, as well as tomorrow's challenges and trends in this important discipline for many cryogenic applications. (authors)

  13. Minimizing material damage using low temperature irradiation

    International Nuclear Information System (INIS)

    Craven, E.; Hasanain, F.; Winters, M.

    2012-01-01

    Scientific advancements in healthcare driven both by technological breakthroughs and an aging and increasingly obese population have lead to a changing medical device market. Complex products and devices are being developed to meet the demands of leading edge medical procedures. Specialized materials in these medical devices, including pharmaceuticals and biologics as well as exotic polymers present a challenge for radiation sterilization as many of these components cannot withstand conventional irradiation methods. The irradiation of materials at dry ice temperatures has emerged as a technique that can be used to decrease the radiation sensitivity of materials. The purpose of this study is to examine the effect of low temperature irradiation on a variety of polymer materials, and over a range of temperatures from 0 °C down to −80 °C. The effectiveness of microbial kill is also investigated under each of these conditions. The results of the study show that the effect of low temperature irradiation is material dependent and can alter the balance between crosslinking and chain scission of the polymer. Low temperatures also increase the dose required to achieve an equivalent microbiological kill, therefore dose setting exercises must be performed under the environmental conditions of use. - Highlights: ► A study is performed to quantify low temperature irradiation effects on polymer materials and BIs. ► Low temperature irradiation alters the balance of cross-linking and chain scissoning in polymers. ► Low temperatures provide radioprotection for BIs. ► Benefits of low temperatures are application specific and must be considered when dose setting.

  14. The influence of electron irradiation at the various temperatures and annealing on carriers mobility at the low temperatures in neutron transmutation doped gallium arsenide

    International Nuclear Information System (INIS)

    Korshunov, F.P.; Kurilovich, N.F.; Prokhorenko, T.A.; Troshchinskii, V.T.; Shesholko, V.K.

    1999-01-01

    The influence of electron irradiation at the various temperatures and annealing on measured at T=100 K carriers mobility in neutron transmutation doped GaAs have been investigated. It was detected that rate of mobility decreasing with irradiation dose increasing decreases when irradiation temperature increases. It was shown that at the same time it take place the radiation defects creating and their particular or full annealing (in the dependence on irradiation temperature). Radiation stimulated annealing (annealing that take place during irradiation at the elevated temperatures) is more effective than the annealing at the same temperatures that take place after crystals are irradiated at room temperature. It means that any defects annealing during irradiation at elevated temperatures take place at more low temperatures than that during annealing after irradiation at room temperature

  15. Minimizing material damage using low temperature irradiation

    Science.gov (United States)

    Craven, E.; Hasanain, F.; Winters, M.

    2012-08-01

    Scientific advancements in healthcare driven both by technological breakthroughs and an aging and increasingly obese population have lead to a changing medical device market. Complex products and devices are being developed to meet the demands of leading edge medical procedures. Specialized materials in these medical devices, including pharmaceuticals and biologics as well as exotic polymers present a challenge for radiation sterilization as many of these components cannot withstand conventional irradiation methods. The irradiation of materials at dry ice temperatures has emerged as a technique that can be used to decrease the radiation sensitivity of materials. The purpose of this study is to examine the effect of low temperature irradiation on a variety of polymer materials, and over a range of temperatures from 0 °C down to -80 °C. The effectiveness of microbial kill is also investigated under each of these conditions. The results of the study show that the effect of low temperature irradiation is material dependent and can alter the balance between crosslinking and chain scission of the polymer. Low temperatures also increase the dose required to achieve an equivalent microbiological kill, therefore dose setting exercises must be performed under the environmental conditions of use.

  16. Low temperature irradiation creep of tungsten and molybdenum

    International Nuclear Information System (INIS)

    Pouchou, J.-L.

    1975-12-01

    It is demonstrated that the mechanism of stress biased nucleation of dislocation loops may contribute significantly to the low temperature irradiation creep. This is achieved by measuring length and electrical resistivity changes at liquid hydrogen temperature, under fission fragments bombardement. From these measurements (correlated with some electron microscopy observations of irradiated samples), the following three stages of deformation appear: at low doses (smaller than 10 -2 displacement per atom) the deformation is mainly an increase in volume due to point defects. The study of this stage gives the formation volume of a Frenkel pair, and the number of point defects created by an initial fission fragment; for doses higher than 10 -2 d.p.a., the point defects saturation is reached. At this stage, vacancies and interstitials collapse into loops, the nucleation of which is polarized by the applied stress. At zero stress, the corresponding creep rate is zero. At high stresses (>50 kg/mm 2 ), creep rate saturates at value of the order of 10 -21 (FF/cm 3 ) -1 ; because of the recombinations of loops, the creep rate decreases continuously during irradiation. The recombinations lead to a dense dislocation network (formed at doses of 1 d.p.a.), the climb of which oriented by the applied stress gives rise to a steady state creep. The creep rate is smaller, by at least one order of magnitude, than that which is observed in the stage of loop formation [fr

  17. Colloid bands in silver chloride induced by reactor irradiation at low temperature

    International Nuclear Information System (INIS)

    Atobe, K.; Okada, M.; Nakagawa, M.

    1978-01-01

    It is well known that no trapped electron center exists stably in irradiated silver chlorides even at low temperatures. On the other hand, irradiation by ultra-violet light at room temperature produces a broad absorption (colloid bands) on the long wavelength side of the fundamental absorption. In this report, it is shown that one of the colloid bands appears in undoped AgCl crystals by reactor irradiation at low temperature (20 K) and the other colloid band by thermal annealing after the irradiation. The relation between the bands, which correspond to two types of colloidal silver, is represented. (author)

  18. Aspects of Low Temperature Irradiation in Neutron Activation Analysis

    International Nuclear Information System (INIS)

    Brune, D.

    1968-08-01

    Neutron irradiation of the sample while frozen in a cooling device inserted in a reactor channel has been carried out in the analysis of iodine in aqueous samples as well as of mercury in biological tissue and water. For the simultaneous irradiation of a large number of aqueous solutions the samples were arranged in a suitable geometry in order to avoid mutual flux perturbation effects. The influence of the neutron temperature on the activation process has been discussed. Potential applications of the low temperature irradiation technique are outlined

  19. Aspects of Low Temperature Irradiation in Neutron Activation Analysis

    Energy Technology Data Exchange (ETDEWEB)

    Brune, D

    1968-08-15

    Neutron irradiation of the sample while frozen in a cooling device inserted in a reactor channel has been carried out in the analysis of iodine in aqueous samples as well as of mercury in biological tissue and water. For the simultaneous irradiation of a large number of aqueous solutions the samples were arranged in a suitable geometry in order to avoid mutual flux perturbation effects. The influence of the neutron temperature on the activation process has been discussed. Potential applications of the low temperature irradiation technique are outlined.

  20. Low temperature irradiation effects on plastic deformation in BCC metals

    International Nuclear Information System (INIS)

    Aono, Yasuhisa

    1984-01-01

    Low temperature electron beam experiment was carried out on high purity iron and molybdenum single crystals, and its effect on the plastic deformation was examined. As the characteristics of the irradiated iron below 77 K, remarkable softening occurred in all orientations. This phenomenon is based on the interaction of self interstitial atoms and screw dislocations, and the other features such as the absorption of interstitial atoms into screw dislocations and the slip on maximum shearing stress planes were shown. On the other hand, the aggregate of interstitial atoms formed by annealing showed the different plastic characteristics from those of interstitial atoms, and gave the results corresponding to respective stages of the electric resistance recovery curves. Regarding molybdenum, the transfer of its self interstitial atoms is near 40 K, therefore at 77 K, cluster is formed, and it largely affects abnormal slip, which is one of the features of the plasticity of molybdenum. The peculiar dependence of the yield stress on the crystalline orientation was shown. The property of the interaction of the aggregate of interstitial atoms formed and grown by the annealing from 77 K to 500 K with dislocations corresponded to the information of defects obtained by the X-ray research of Maeta, and the similarity to the aggregate of iron was observed. (Kako, I.)

  1. Low temperature irradiation facility at Kyoto University Reactor (KUR)

    International Nuclear Information System (INIS)

    Atobe, Kozo; Okada, Moritami; Yoshida, Hiroyuki; Kodaka, Hisao; Miyata, Kiyomi.

    1977-01-01

    A new refrigeration system has been substituted to the low temperature irradiation facility at KUR instead of the previous one, since April in 1975. The model 1204 CTi He liquifier was designed to be modified for the refrigerator with the capacity of 30 watts at 10 K. The refrigeration capacity of 38 watts at 10 K was defined using a special cryostat and transfer-tubes, and the lowest temperature of about 18 K was measured using the irradiation loop without reactor operation. The reconstructed facility enables us to hold the many specimens simultaneously in the sample chamber of the irradiation loop at about 25 K during reactor operation of 5 MW. The irradiation dose has been reached about 6.6 x 10 16 n sub(f)/cm 2 and 6.1 x 10 17 n sub(th)/cm 2 with the normal reactor operation cycle of up to 77 hours. The stable operation condition of the machine and the special safety system for the refrigeration system enable us to maintain easily the facility with a constant operation condition for such a long time irradiation. Many kinds of low temperature neutron irradiation experiments are carried out using the facility, which techniques are partially reported. (auth.)

  2. National Low-Temperature Neutron-Irradiation Facility

    International Nuclear Information System (INIS)

    Coltman, R.R. Jr.; Klabunde, C.E.; Young, F.W. Jr.

    1983-08-01

    The Materials Sciences Division of the United States Department of Energy will establish a National Low Temperature Neutron Irradiation Facility (NLTNIF) which will utilize the Bulk Shielding Reactor (BSR) located at Oak Ridge National Laboratory. The facility will provide high radiation intensities and special environmental and testing conditions for qualified experiments at no cost to users. This report describes the planned experimental capabilities of the new facility

  3. In Situ Irradiation and Measurement of Triple Junction Solar Cells at Low Intensity, Low Temperature (LILT) Conditions

    Science.gov (United States)

    Harris, R.D.; Imaizumi, M.; Walters, R.J.; Lorentzen, J.R.; Messenger, S.R.; Tischler, J.G.; Ohshima, T.; Sato, S.; Sharps, P.R.; Fatemi, N.S.

    2008-01-01

    The performance of triple junction InGaP/(In)GaAs/Ge space solar cells was studied following high energy electron irradiation at low temperature. Cell characterization was carried out in situ at the irradiation temperature while using low intensity illumination, and, as such, these conditions reflect those found for deep space, solar powered missions that are far from the sun. Cell characterization consisted of I-V measurements and quantum efficiency measurements. The low temperature irradiations caused substantial degradation that differs in some ways from that seen after room temperature irradiations. The short circuit current degrades more at low temperature while the open circuit voltage degrades more at room temperature. A room temperature anneal after the low temperature irradiation produced a substantial recovery in the degradation. Following irradiation at both temperatures and an extended room temperature anneal, quantum efficiency measurement suggests that the bulk of the remaining damage is in the (In)GaAs sub-cell

  4. low temperature irradiation effects in iron-alloys and ceramics

    International Nuclear Information System (INIS)

    Kuramoto, Eiichi; Abe, Hironobu; Tanaka, Minoru; Nishi, Kazuya; Tomiyama, Noriyuki.

    1991-01-01

    Electron beam irradiation at 77K and neutron irradiation at 20K were carried out on Fe-Cr and Fe-Cr-Ni alloys and ZnO and graphite system ceramics, and by measuring positron annihilation lifetime, the micro-information about irradiation-introduced defects was obtained. The temperature of the movement of atomic vacancies in pure iron is about 200K, but it was clarified that by the addition of Cr, it was not much affected. However, in the case of high concentration Cr alloys, the number of atomic vacancies which take part in the formation of micro-voids decreased as compared with the case of pure iron. It is considered that among the irradiation defects of ZnO, O-vac. restored below 300degC. It is considered that in the samples without irradiation, the stage of restoration exists around 550degC, which copes with structural defects. By the measurement of graphite without irradiation, the positron annihilation lifetime corresponding with the interface of matrix and crystal grains, grain boundaries and internal surfaces was almost determined. The materials taken up most actively in the research and development of nuclear fusion reactor materials are austenitic and ferritic stainless steels, and their irradiation defects have been studied. (K.I.)

  5. Electron-dislocation interaction at low temperatures. Progress report

    International Nuclear Information System (INIS)

    1978-01-01

    The interaction of mobile dislocations with electrons in copper and copper alloys has shown that dislocation motion in copper, at low temperature, can be treated as an analog of an underdamped oscillator. We have also shown that the viscous drag on mobile dislocations in type II superconductors can be treated as an acoustic attenuation of an elastic wave

  6. Moessbauer spectroscopy of He irradiated austenitic stainless steel SUS304 at low temperature

    International Nuclear Information System (INIS)

    Horii, Kiyomasa; Ishibashi, Tetsu; Toriyama, Tamotsu; Wakabayashi, Hidehiko; Iijima, Hiroshi; Kawasaki, Katsunori; Hayashi, Nobuyuki; Sakamoto, Isao.

    1996-01-01

    SUS 304 austenitic stainless steel causes the magnetic transition at 60 K, and the Young's modulus lowers. In addition, its composition elements have the large (n,α) reaction cross section to high energy neutrons, and helium is apt to be generated, and this is a factor that lowers the material strength. In the He-irradiated parts in austenitic stainless steel, the precursory state of martensite transformation should exist, and its effect is considered to be observable by carrying out low temperature Moessbauer spectroscopy. As to the preparation of He-irradiation samples, the SUS 304 foils used and the irradiation conditions are described. The measurement of low temperature Moessbauer spectra for the samples without irradiation and with irradiation is reported. In order to determine the magnetic transition point, the thermal scanning measurement was carried out for the samples without or with irradiation. The martensite transformation was measured by X-ray diffraction and transmission type Moessbauer spectroscopy. In order to observe the state of the sample surfaces, the measurement by internal conversion electron Moessbauer spectroscopy was performed. These results and the temperature dependence of the Moessbauer spectra for the irradiated parts are reported. (K.I.)

  7. Moessbauer spectroscopy of He irradiated austenitic stainless steel SUS304 at low temperature

    Energy Technology Data Exchange (ETDEWEB)

    Horii, Kiyomasa; Ishibashi, Tetsu; Toriyama, Tamotsu; Wakabayashi, Hidehiko; Iijima, Hiroshi [Musashi Inst. of Tech., Tokyo (Japan); Kawasaki, Katsunori; Hayashi, Nobuyuki; Sakamoto, Isao

    1996-04-01

    SUS 304 austenitic stainless steel causes the magnetic transition at 60 K, and the Young`s modulus lowers. In addition, its composition elements have the large (n,{alpha}) reaction cross section to high energy neutrons, and helium is apt to be generated, and this is a factor that lowers the material strength. In the He-irradiated parts in austenitic stainless steel, the precursory state of martensite transformation should exist, and its effect is considered to be observable by carrying out low temperature Moessbauer spectroscopy. As to the preparation of He-irradiation samples, the SUS 304 foils used and the irradiation conditions are described. The measurement of low temperature Moessbauer spectra for the samples without irradiation and with irradiation is reported. In order to determine the magnetic transition point, the thermal scanning measurement was carried out for the samples without or with irradiation. The martensite transformation was measured by X-ray diffraction and transmission type Moessbauer spectroscopy. In order to observe the state of the sample surfaces, the measurement by internal conversion electron Moessbauer spectroscopy was performed. These results and the temperature dependence of the Moessbauer spectra for the irradiated parts are reported. (K.I.)

  8. Geometric component of charge pumping current in nMOSFETs due to low-temperature irradiation

    Science.gov (United States)

    Witczak, S. C.; King, E. E.; Saks, N. S.; Lacoe, R. C.; Shaneyfelt, M. R.; Hash, G. L.; Hjalmarson, H. P.; Mayer, D. C.

    2002-12-01

    The geometric component of charge pumping current was examined in n-channel metal-oxide-silicon field effect transistors (MOSFETs) following low-temperature irradiation. In addition to the usual dependencies on channel length and gate bias transition time, the geometric component was found to increase with radiation-induced oxide-trapped charge density and decreasing temperature. A postirradiation injection of electrons into the gate oxide reduces the geometric component along with the density of oxide-trapped charge, which clearly demonstrates that the two are correlated. A fit of the injection data to a first-order model for trapping kinetics indicates that the electron trapping occurs predominantly at a single type of Coulomb-attractive trap site. The geometric component results primarily from the bulk recombination of channel electrons that fail to transport to the source or drain during the transition from inversion to accumulation. The radiation response of these transistors suggests that Coulomb scattering by oxide-trapped charge increases the bulk recombination at low temperatures by impeding electron transport. These results imply that the geometric component must be properly accounted for when charge pumping irradiated n-channel MOSFETs at low temperatures.

  9. Low Temperature Diffusion Transformations in Fe-Ni-Ti Alloys During Deformation and Irradiation

    Science.gov (United States)

    Sagaradze, Victor; Shabashov, Valery; Kataeva, Natalya; Kozlov, Kirill; Arbuzov, Vadim; Danilov, Sergey; Ustyugov, Yury

    2018-03-01

    The deformation-induced dissolution of Ni3Ti intermetallics in the matrix of austenitic alloys of Fe-36Ni-3Ti type was revealed in the course of their cascade-forming neutron irradiation and cold deformation at low temperatures via employment of Mössbauer method. The anomalous deformation-related dissolution of the intermetallics has been explained by the migration of deformation-induced interstitial atoms from the particles into a matrix in the stress field of moving dislocations. When rising the deformation temperature, this process is substituted for by the intermetallics precipitation accelerated by point defects. A calculation of diffusion processes has shown the possibility of the realization of the low-temperature diffusion of interstitial atoms in configurations of the crowdions and dumbbell pairs at 77-173 K. The existence of interstitial atoms in the Fe-36Ni alloy irradiated by electrons or deformed at 77 K was substantiated in the experiments of the electrical resistivity measurements.

  10. Electron microscopic observation at low temperature on superconductors

    International Nuclear Information System (INIS)

    Yokota, Yasuhiro; Hashimoto, Hatsujiro; Yoshida, Hiroyuki.

    1991-01-01

    The authors have observed superconducting materials with a high resolution electron microscope at liquid helium temperature. First, observation was carried out on Nb system intermetallic compounds such as Nb 3 Al and Nb 3 Sn of Al 5 type and Nb 3 Ge of 11 type at extremely low temperature. Next, the observation of high temperature superconductive ceramics in the state of superconductivity was attempted. In this paper, first the development of the liquid helium sample holder for a 400 kV electron microscope to realize the observation is reported. Besides, the sample holder of Gatan Co. and an extremely low temperature, high resolution electron microscope with a superconducting lens are described. The purpose of carrying out the electron microscope observation of superconductors at low temperature is the direct observation of the crystalline lattice image in the state of superconductivity. Also the structural transformation from tetragonal crystals to rhombic crystals in Al 5 type superconductors can be observed. The results of observation are reported. (K.I.)

  11. 12th International Workshop on Low Temperature Electronics

    International Nuclear Information System (INIS)

    2017-01-01

    The present volume of the Journal of Physics: Conference Series represents contributions from participants of the 12th International Workshop on Low Temperature Electronics held in Tempe, Arizona, USA from September 18-21, 2016. The conference was organized by the School of Earth and Space Exploration at Arizona State University.The International Workshop on Low Temperature Electronics (WOLTE) is a biennial conference devoted to the presentation and exchange of the most recent advances in the field of low temperature electronics and its applications. This international forum is open to everyone in the field.The technical program included oral presentations and posters on fundamental properties of cryogenic materials, cryogenic transistors, quantum devices and systems, astronomy and physics instrumentation, and fabrication of cryogenic devices. More than 50 scientists and engineers from various academic, government, and industrial institutions in Europe, Asia, and the Americas attended the conference.We would like to thank all speakers for their presentations and all attendees for their participation. We would also like to express our sincerest gratitude to our sponsors: Lake Shore Cryotronics, ASU NewSpace, ASU School of Earth and Space Exploration, and IRA A. Fulton Schools of Engineering for making this conference possible. (paper)

  12. Positron annihilation lifetime study of low temperature irradiated metals

    Energy Technology Data Exchange (ETDEWEB)

    Kuramoto, Eiichi [Kyushu Univ., Kasuga, Fukuoka (Japan). Research Inst. for Applied Mechanics

    1997-11-01

    Positron annihilation lifetime measurements have been made for electron and neutron irradiated Fe, Fe-Cr, Fe-Cu, Fe-Si, Fe-16Cr-17Ni specimens, and isochronal annealing behaviors were obtained for these metals and alloys. It was found that vacancies start to migrate at about 200 K in Fe and form microvoids, but by the addition of small amount of alloying elements this behavior was changed depending on the alloying elements. Positron lifetime calculations were made to explain the experimental results using EAM (embedded atom method) type potential for the lattice relaxation and the atomic superposition method for the lifetime calculation. Fairly good agreements were obtained for the positron lifetime in a vacancy in Fe and other alloys. (author)

  13. Positronium formation at low temperatures: The role of trapped electrons

    DEFF Research Database (Denmark)

    Hirade, T.; Maurer, F.H.J.; Eldrup, Morten Mostgaard

    2000-01-01

    Measurements have been carried out of electron spin densities (by electron spin resonance technique) and positronium (Ps) formation probability as functions of Co-60 gamma-irradiation dose in poly(methyl methacrylate) and linear poly(ethylene) at 77 K. We observe a linear relationship between...

  14. Low-temperature crystallization of amorphous silicon and amorphous germanium by soft X-ray irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Heya, Akira, E-mail: heya@eng.u-hyogo.ac.jp [Department of Materials Science and Chemistry, University of Hyogo, 2167 Shosha, Himeji, Hyogo 671–2280 (Japan); Kanda, Kazuhiro [Laboratory of Advanced Science and Technology for Industry (LASTI), University of Hyogo, 3-2-1 Koto, Kamigori, Hyogo 678–1205 (Japan); Toko, Kaoru; Sadoh, Taizoh [Department of Electronics, Kyushu University, 744 Nishi-ku, Motooka, Fukuoka 819–0395 (Japan); Amano, Sho [Laboratory of Advanced Science and Technology for Industry (LASTI), University of Hyogo, 3-2-1 Koto, Kamigori, Hyogo 678–1205 (Japan); Matsuo, Naoto [Department of Materials Science and Chemistry, University of Hyogo, 2167 Shosha, Himeji, Hyogo 671–2280 (Japan); Miyamoto, Shuji [Laboratory of Advanced Science and Technology for Industry (LASTI), University of Hyogo, 3-2-1 Koto, Kamigori, Hyogo 678–1205 (Japan); Miyao, Masanobu [Department of Electronics, Kyushu University, 744 Nishi-ku, Motooka, Fukuoka 819–0395 (Japan); Mochizuki, Takayasu [Laboratory of Advanced Science and Technology for Industry (LASTI), University of Hyogo, 3-2-1 Koto, Kamigori, Hyogo 678–1205 (Japan)

    2013-05-01

    The low-temperature-crystallization effects of soft X-ray irradiation on the structural properties of amorphous Si and amorphous Ge films were investigated. From the differences in crystallization between Si and Ge, it was found that the effects of soft X-ray irradiation on the crystallization strongly depended on the energy band gap and energy level. The crystallization temperatures of the amorphous Si and amorphous Ge films decreased from 953 K to 853 K and 773 K to 663 K, respectively. The decrease in crystallization temperature was also related to atoms transitioning into a quasi-nucleic phase in the films. The ratio of electron excitation and migration effects to thermal effects was controlled using the storage-ring current (photon flux density). Therefore, we believe that low-temperature crystallization can be realized by controlling atomic migration through electron excitation. - Highlights: • This work investigates the crystallization mechanism for soft X-ray irradiation. • The soft X-ray crystallization depended on the energy band gap and energy level. • The decrease in the crystallization temperature for Si and Ge films was 100 K. • This decrement was related to atoms transitioning into a quasi-nucleic phase.

  15. Low temperature gamma-ray irradiation effects on polymer materials

    International Nuclear Information System (INIS)

    Kudoh, Hisaaki; Kasai, Noboru; Sasuga, Tsuneo; Seguchi, Tadao

    1995-01-01

    The gamma radiation induced degradation of glass fiber reinforced plastic (GFRP) and polymethylmethacrylate (PMMA) at 77K was examined by flexural test and gas analysis after irradiation and compared by the irradiation at room temperature. The decrease in flexural strength at break was much less at 77K than at RT. The evolution of CH 4 , CO and CO 2 was also depressed at 77K. The temperature dependence of the degradation closely relates to the local molecular motion of matrix resin during irradiation. Polytetrafluoroethylene (PTFE) was also studied by irradiation at RT, 77K and 4K in terms of tensile elongation and molecular weight. The degradation was much less at 77K and 4K than at RT, and the same between 77K and 4K. (author)

  16. Stored energy in fusion magnet materials irradiated at low temperatures

    International Nuclear Information System (INIS)

    Chaplin, R.L.; Kerchner, H.R.; Klabunde, C.E.; Coltman, R.R.

    1989-08-01

    During the power cycle of a fusion reactor, the radiation reaching the superconducting magnet system will produce an accumulation of immobile defects in the magnet materials. During a subsequent warm-up cycle of the magnet system, the defects will become mobile and interact to produce new defect configurations as well as some mutual defect annihilations which generate heat-the release of stored energy. This report presents a brief qualitative discussion of the mechanisms for the production and release of stored energy in irradiated materials, a theoretical analysis of the thermal response of irradiated materials, theoretical analysis of the thermal response of irradiated materials during warm-up, and a discussion of the possible impact of stored energy release on fusion magnet operation 20 refs

  17. Mechanical properties of low temperature proton irradiated single crystal copper

    International Nuclear Information System (INIS)

    Schildcrout, M.

    1975-01-01

    Single crystal copper samples, of varying degrees of cold work, were irradiated near either liquid helium or liquid nitrogen temperature by 10.1-MeV protons. The internal friction and dynamic Young's modulus were observed as a function of either temperature or integrated proton flux. The primary effect of irradiation was to produce dislocation pinning. The initial pinning rate was found to be very sensitive to cold work. During irradiation it was found that heavily cold worked samples (25 percent compression) exhibited, almost exclusively, exponential pinning given by Y = e/sup --lambda phi/. This is attributed to the immobilization, rather than shortening, of loop lengths and is characterized by the pinning constant lambda. Exponential pinning was also found, to a smaller degree, in less heavily cold worked samples. Cold work appears to reduce the ''effective volume'' within which the defect clusters produced by irradiation, can immobilize dislocation segments. The bulk effect was observed after dislocation pinning was completed. Expressed in terms of the fractional change in Young's modulus per unit concentration of irradiation induced defects, it was measured at liquid helium temperature to be --18.5 +- 3. An anelastic process occurring near 10 0 K for low kHz frequencies and due to stress-induced ordering of point defects produced by irradiation has also been studied. The peak height per unit fluence was found to decrease with increasing cold work. The peak was not observed in samples compressed 25 percent. For the most carefully handled sample the activation energy was (1.28 +- 0.05) x 10 -2 eV, the attempt frequency was 10/sup 11.6 +- .8/ s -1 , the shape factor was 0.20, and the half width of the peak was 11 percent larger than the theoretical value calculated from the Debye equation for a single relaxation process

  18. Strain acceleration of the low temperature irradiated zirconium

    International Nuclear Information System (INIS)

    Fortis, Ana M.; Coccoz, Guillermina D. H.

    2003-01-01

    The strain of a Zr-0,06 at.% 235 U specimen irradiated during 4800 h in the RA-3 at a temperature near 40 C degrees is presented. An equivalent neutron fluence of 3.1 x 10 26 n m -2 was achieved by means of the generation of fission fragment within the material. The experimental conditions are described and a sudden strain acceleration independent of the neutron flux variations occurred during irradiation is shown. This behavior is compared with previous data obtained at different temperatures. (author)

  19. Effect of low temperature reactor irradiation on organic insulators in superconducting magnets, (4)

    International Nuclear Information System (INIS)

    Kato, Teruo; Takamura, Saburo

    1983-01-01

    In order to study effects of irradiation at low temperature on insulating materials of superconducting magnets, flexural and impact tests are carried out at 4.2K without warmup after low temperature irradiation for several fiber reinforced plastics. The used materials are glass fiber reinforced epoxies and polyimide, and carbon fiber reinforced epoxies. After irradiation of 1.1 X 10 9 rad, the reduction in flexural strength of G-10 CR is about 70% and that of G-11 CR about 25%. No change are observed in strength of glass fiber reinforced polyimide by low temperature irradiation. Other kinds of glass fiber reinforced epoxies show a reduction in strength but the flexural strength of carbon fiber reinforced epoxies increases a small by irradiation. Irradiation effect of these materials on impact value is similar to that on flexural strength. (author)

  20. Enhanced low-temperature oxidation of zirconium alloys under irradiation

    International Nuclear Information System (INIS)

    Cox, B.; Fidleris, V.

    1989-01-01

    The linear growth of relatively thick (>300 nm) interference-colored oxide films on zirconium alloy specimens exposed in the Advanced Test Reactor (ATR) coolant at ≤55 o C was unexpected. Initial ideas were that this was a photoconduction effect. Experiments to study photoconduction in thin anodic zirconium oxide (ZrO 2 ) films in the laboratory were initiated to provide background data. It was found that, in the laboratory, provided a high electric field was maintained across the oxide during ultraviolet (UV) irradiation, enhanced growth of oxide occurred in the irradiated area. Similarly enhanced growth could be obtained on thin thermally formed oxide films that were immersed in an electrolyte with a high electric field superimposed. This enhanced growth was found to be caused by the development of porosity in the barrier oxide layer by an enhanced local dissolution and reprecipitation process during UV irradiation. Similar porosity was observed in the oxide films on the ATR specimens. Since it is not thought that a high electric field could have been present in this instance, localized dissolution of fast-neutron primary recoil tracks may be the operative mechanism. In all instances, the specimens attempt to maintain the normal barrier-layer oxide thickness, which causes the additional oxide growth. Similar mechanisms may have operated during the formation of thick loosely adherent, porous oxides in homogeneous reactor solutions under irradiation, and may be the cause of enhanced oxidation of zirconium alloys in high-temperature water-cooled reactors in some water chemistries. (author)

  1. Low temperature irradiation of vitrifiable mixtures of unsaturated monomers

    International Nuclear Information System (INIS)

    Kaetsu, I.; Ito, A.; Hayashi, K.

    1975-01-01

    A specific mixture containing at least one polymerizable unsaturated monomer which is not vitrifiable by itself can advantageously be polymerized by irradiating the mixture at a temperature not higher than 100 0 C above glass transition temperature of the mixture with an ionizing radiation and/or a light. 12 claims, 6 drawings, figures

  2. Neutron Irradiation Tests of Calibrated Cryogenic Sensors at Low Temperatures

    CERN Document Server

    Junquera, T; Thermeau, J P; Casas-Cubillos, J

    1998-01-01

    This paper presents the advancement of a program being carried out in view of selecting the cryogenic temperature sensors to be used in the LHC accelerator. About 10,000 sensors will be installed around the 26.6 km LHC ring, and most of them will be exposed to high radiation doses during the accelerator lifetime. The following thermometric sensors : carbon resistors, thin films, and platinum resistors, have been exposed to high neutron fluences (>10$^15$ n/cm$^2$) at the ISN (Grenoble, France) Cryogenic Irradiation Test Facility. A cryostat is placed in a shielded irradiation vault where a 20 MeV deuteron beam hits a Be target, resulting in a well collimated and intense neutron beam. The cryostat, the on-line acquisition system, the temperature references and the main characteristics of the irradiation facility are described. The main interest of this set-up is its ability to monitor online the evolution of the sensors by comparing its readout with temperature references that are in principle insensitive to t...

  3. Direct observation of cascade defect formation at low temperatures in ion-irradiated metals

    International Nuclear Information System (INIS)

    Muroga, T.; Hirooka, K.; Ishino, S.

    1984-01-01

    Direct transmission electron microscopy observations of cascade defect formation have been carried out in gold, Type 316 stainless steel, and aluminum irradiated by Al + , Ar - , and Xe + ions with energies between 80 and 400 keV. By utilizing a link of an ion accelerator to an electron microscope, in situ observations at low temperature (-150 0 C) have become possible. In gold, subcascade structures are clearly observed in all cases. Obvious dependence on projectile mass and energy is observed for cascade structure and vacancy clustering efficiency in gold and for defect visibility in aluminum and Type 316 stainless steel. A computer simulation calculation using MARLOWE shows subcascade distributions a little smaller in size and larger in number than the present observation

  4. Change in digestibility of gamma-irradiated starch by low temperature cooking

    International Nuclear Information System (INIS)

    Kume, T.; Ishigaki, I.; Rahman, S.

    1988-01-01

    Combination effect of irradiation and low temperature cooking on starch digestibility has been investigated as a basic research for application of radiosterilization on starch fermentation. The digestion of corn starch by glucoamylase after cooking at low temperature was enhanced by γ-irradiation and the required cooking temperature was decreased from 75-80 0 C to 65 0 C by 25 kGy. Gelatinization of starches except tapioca starch was enhanced by irradiation and it corresponds to the digestibility. The digestibility of potato starch which has a high viscosity was especially enhanced at low temperature cooking because the viscosity was markedly decreased by irradiation. These results show that the irradiation of starches is useful not only for the sterilization of fermentation broth but also for the enhancement of digestion. (orig.) [de

  5. Change in digestibility of gamma-irradiated starch by low temperature cooking

    Energy Technology Data Exchange (ETDEWEB)

    Kume, T.; Ishigaki, I.; Rahman, S.

    1988-04-01

    Combination effect of irradiation and low temperature cooking on starch digestibility has been investigated as a basic research for application of radiosterilization on starch fermentation. The digestion of corn starch by glucoamylase after cooking at low temperature was enhanced by ..gamma..-irradiation and the required cooking temperature was decreased from 75-80/sup 0/C to 65/sup 0/C by 25 kGy. Gelatinization of starches except tapioca starch was enhanced by irradiation and it corresponds to the digestibility. The digestibility of potato starch which has a high viscosity was especially enhanced at low temperature cooking because the viscosity was markedly decreased by irradiation. These results show that the irradiation of starches is useful not only for the sterilization of fermentation broth but also for the enhancement of digestion.

  6. Low temperature processed InGaZnO thin film transistor using the combination of hydrogen irradiation and annealing

    Energy Technology Data Exchange (ETDEWEB)

    Park, Hyun-Woo; Choi, Min-Jun; Jo, Yongcheol; Chung, Kwun-Bum, E-mail: kbchung@dongguk.edu

    2014-12-01

    Highlights: • We studied the low temperature process of InGaZnO oxide thin film transistor. • Hydorgen irradiation was used for low temperature process below 150 °C. • Using hydrogen irradiation, field effect mobility of IGZO TFT was enhanced to ∼5 cm{sup 2} /Vs. • We examined the origin of improvement of device performance via electronic structure. - Abstract: Device performance of radio frequency (RF) sputtered InGaZnO (IGZO) thin film transistors (TFTs) were improved using combination post-treatment with hydrogen irradiation and low temperature annealing at 150 °C. Under the combination treatment, IGZO TFTs were significantly enhanced without changing physical structure and chemical composition. On the other hand, the electronic structure represents a dramatically modification of the chemical bonding states, band edge states below the conduction band, and band alignment. Compared to the hydrogen irradiation or low temperature annealing, the combination treatment induces the increase of oxygen deficient chemical bonding states, the shallow band edge state below the conduction band, and the smaller energy difference of conduction band offset, which can generate the increase in charge carrier and enhance the device performance.

  7. Low Temperature Irradiation Embrittlement of Reactor Pressure Vessel Steels

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Jy-An John [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2015-08-01

    The embrittlement trend curve development project for HFIR reactor pressure vessel (RPV) steels was carried out with three major tasks. Which are (1) data collection to match that used in HFIR steel embrittlement trend published in 1994 Journal Nuclear Material by Remec et. al, (2) new embrittlement data of A212B steel that are not included in earlier HFIR RPV trend curve, and (3) the adjustment of nil-ductility-transition temperature (NDTT) shift data with the consideration of the irradiation temperature effect. An updated HFIR RPV steel embrittlement trend curve was developed, as described below. NDTT( C) = 23.85 log(x) + 203.3 log (x) + 434.7, with 2- uncertainty of 34.6 C, where parameter x is referred to total dpa. The developed update HFIR RPV embrittlement trend curve has higher embrittlement rate compared to that of the trend curve developed in 1994.

  8. Radiation damage relative to transmission electron microscopy of biological specimens at low temperature: a review

    International Nuclear Information System (INIS)

    Glaeser, R.M.; Taylor, K.A.

    1978-01-01

    When biological specimens are irradiated by the electron beam in the electron microscope, the specimen structure is damaged as a result of molecular excitation, ionization, and subsequent chemical reactions. The radiation damage that occurs in the normal process of electron microscopy is known to present severe limitations for imaging high resolution detail in biological specimens. The question of radiation damage at low temperatures has therefore been investigated with the view in mind of reducing somewhat the rate at which damage occurs. The radiation damage protection found for small molecule (anhydrous) organic compounds is generally rather limited or even non-existent. However, large molecule, hydrated materials show as much as a 10-fold reduction at low temperature in the rate at which radiation damage occurs, relative to the damage rate at room temperature. In the case of hydrated specimens, therefore, low temperature electron microscopy offers an important advantage as part of the overall effort required in obtaining high resolution images of complex biological structures. (author)

  9. Low temperature modification of gamma-irradiation effect on peas. II.Low temperature effect on the radio-sensitivity and the chlorophyll mutations

    International Nuclear Information System (INIS)

    Najdenova, N.; Vasileva, M.

    1976-01-01

    Dry pea seeds of cv.Ramonskii 77 with 11-12% moisture were γ-irradiated by 60 Co in doses 5, 15, 20 and 30 krad. Low temperature (-78 deg C) was effected in the form of dry ice for a 24 h period prior to, at the time of and post irradiation. As control were used: (a) dry non-irradiated seeds, stored at room temperature; (b) non-irradiated seeds subjected to low temperature (-78 deg C) for a 24 h period. and (c) seeds irradiated by the named doses, stored at room temperature until the time of irradiation. Treated and control seeds were sown in the field. Germination, survival rate and sterility were recorded in M 1 , while in M 2 chlorophyll mutations were scored. Results obtained showed that low temperature modification effect on the various irradiation doses depended on the time of its application; low temperature (-78 deg C) treatment prior to seed irradiation with doses 15, 20 and 30 krad increased germination percentage, plant survival and yield components in M 1 . The post-irradiation treatment did not have a significant effect on gamma-rays; highest protection effect was obtained in case seeds were irradiated at low temperature and then received supplementary treatment at high temperature. In this way the damaging effect of radiation was reduced to a maximum degree; low temperature treatment prior to irradiation with doses of 15 and 20 krad or at the time of irradiation with doses of 15, 20 and 30 krad resulted in a considerably wider chlorophyll mutation spectrum. (author)

  10. Thermoluminescence analysis of co-doped NaCl at low temperature irradiations

    Energy Technology Data Exchange (ETDEWEB)

    Cruz-Zaragoza, E., E-mail: ecruz@nucleares.unam.m [Instituto de Ciencias Nucleares, Universidad Nacional Autonoma de Mexico, A.P. 70-543, 04510 Mexico D.F. (Mexico); Ortiz, A. [Instituto de Ciencias Nucleares, Universidad Nacional Autonoma de Mexico, A.P. 70-543, 04510 Mexico D.F. (Mexico); Unidad Profesional Interdisciplinaria de Ingenieria y Tecnologias Avanzadas, IPN, Av. Instituto Politecnico Nacional 2580, Col. La Laguna Ticoman, 07340 Mexico D.F. (Mexico); Furetta, C. [Touro University Rome, Circne Gianicolense 15-17, 00153 Rome (Italy); Flores J, C.; Hernandez A, J.; Murrieta S, H. [Instituto de Fisica, Universidad Nacional Autonoma de Mexico, A.P. 20-364, 01000 Mexico D.F. (Mexico)

    2011-02-15

    The thermoluminescent response and kinetics parameters of NaCl, doubly activated by Ca-Mn and Cd-Mn ions, exposed to gamma radiation are analyzed. The doped NaCl samples were irradiated at relative low temperature, i.e. at the liquid nitrogen temperature (LNT) and at dry ice temperature (DIT), and the glow curves obtained after 2 Gy of gamma irradiation were analyzed using the computerized glow curve deconvolution (CGCD). An evident variation in the glow curve structure after LNT and DIT was observed. It seems that different kinds of trapping levels are activated at relative low temperature. The original two prominent peaks in compositions A (Ca,Mn) and B (Ca,Mn) have been changed in only one main peak with satellites in the low temperature side of the glow curves. In compositions C (Cd,Mn) and D (Cd,Mn), low temperature peaks become stronger and prominent than the high temperature peaks; this effect could be explained considering that the trapping probability for low temperature traps, the one very close to the conduction band, is enhanced by low temperatures during irradiation.

  11. Batch scale storage of sprouting foods by irradiation combined with natural low temperature; pt. 2

    International Nuclear Information System (INIS)

    Byun, M.W.; Lee, C.H.; Cho, H.O.; Kwon, J.H.; Yang, H.S.

    1982-01-01

    Two varieties of potatoes, Irish cobbler and Shimabara stored for seven and nine months respectively by irradiation combined with natural low temperature (year-round temperature change: 2-17degC) on a batch scale were investigated on the suitability for processing of potato chip. Nine months after storage, irradiated potatoes (Irish cobbler) tended to maintain somewhat better texture and sensory quality than untreated in potatoe chip processing. Peel rate, closely related to potato chip yield, of untreated potatoes were 20-25% higher than those of irradiated and Agtron color determination of potato chip from both irradiated were commercially acceptable. Preservation of potatoes by irradiation combined with natural low temperature was evaluated as an alternative method of the supply for raw materials of potato chip processing in the off-season in Korea. (Author)

  12. Batch scale strength of garlic by irradiation combined with natural low temperature

    International Nuclear Information System (INIS)

    Cho, H.O.; Kwon, J.H.; Byun, M.W.

    1984-01-01

    An attempt was made on the development of a commercial scale storage method of garlic by irradiation. Irradiated garlics with 50, 100 and 150 Gy were stored at natural low temperature storage room (12±6°C, 75-85% RH) and the physicochemical properties during the 10 months storage were investigated. The unirradiated garlic was mostly sprouted after 8 months storage, whereas the sprouting of all irradiated groups was completely inhibited until 10 months storage, The rotting rate and weigh loss of garlic after 10 months storage were reduced by 25 to 54% at 100 Gy irradiation compared with those of an unirradiated group. The moisture content remained relatively constant during the whole storage period. The total sugar content was increased with storage period. Ascorbic acid content was also decreased until 8 months storage but its content was rapidly increased along with sprouting. Garlic was marketable after 10 months storage by 100 Gy irradiation combined with natural low temperature. (author)

  13. Alleviation of Low-Temperature Photoinhibition in Gamma-Irradiated Red Pepper (Capsicum annuum L.) Plants

    International Nuclear Information System (INIS)

    Kim, J.H.; Kim, J.S.; An, B.C.; Chung, B.Y.

    2006-01-01

    We studied the radiation-induced stress resistance in red pepper leaves under conditions of low-temperature photoinhibition or artificially induced photo-oxidative stress. Plants irradiated with 4, 8, or 16-Gy gamma rays were more resistant to both stress factors than were the controls. However, exposure to a low temperature for 12 h with illumination or photo-oxidative treatment for 1 h differentially affected the irradiated leaves, although they had similar stress intensities as defined by their maximal photochemical efficiencies (Fv/Fm)

  14. Low-Temperature Electron Beam-Induced Transformations of Cesium Lead Halide Perovskite Nanocrystals

    Science.gov (United States)

    2017-01-01

    Cesium lead halide perovskite (CsPbX3, with X = Br, Cl, I) nanocrystals have been found to undergo severe modifications under the high-energy electron beam irradiation of a transmission electron microscope (80/200 keV). In particular, in our previous work, together with halogen desorption, Pb2+ ions were found to be reduced to Pb0 and then diffused to form lead nanoparticles at temperatures above −40 °C. Here, we present a detailed irradiation study of CsPbBr3 nanocrystals at temperatures below −40 °C, a range in which the diffusion of Pb0 atoms/clusters is drastically suppressed. Under these conditions, the irradiation instead induces the nucleation of randomly oriented CsBr, CsPb, and PbBr2 crystalline domains. In addition to the Br desorption, which accompanies Pb2+ reduction at all the temperatures, Br is also desorbed from the CsBr and PbBr2 domains at low temperatures, leading to a more pronounced Br loss, thus the final products are mainly composed of Cs and Pb. The overall transformation involves the creation of voids, which coalesce upon further exposure, as demonstrated in both nanosheets and nanocuboids. Our results show that although low temperatures hinder the formation of Pb nanoparticles in CsPbBr3 nanocrystals when irradiated, the nanocrystals are nevertheless unstable. Consequently, we suggest that an optimum combination of temperature range, electron energy, and dose rate needs to be carefully chosen for the characterization of halide perovskite nanocrystals to minimize both the Pb nanoparticle formation and the structural decomposition. PMID:28983524

  15. Effects of irradiation at low temperature on V-4Cr-4Ti

    International Nuclear Information System (INIS)

    Alexander, D.J.; Snead, L.L.; Zinkle, S.J.

    1996-01-01

    Irradiation at low temperatures (100 to 275 degrees C) to 0.5 dpa causes significant embrittlement and changes in the subsequent room temperature tensile properties of V-4Cr-4Ti. The yield strength and microhardness at room temperature increase with increasing irradiation temperature. The tensile flow properties at room temperature show large increases in strength and a complete loss of work hardening capacity with no uniform ductility. Embrittlement, as measured by an increase in the ductile-to-brittle transition temperature, increases with increasing irradiation temperature, at least up to 275 degrees C. This embrittlement is not due to pickup of O or other interstitial solutes during the irradiation

  16. Effects of irradiation at low temperature on V-4Cr-4Ti

    Energy Technology Data Exchange (ETDEWEB)

    Alexander, D.J.; Snead, L.L.; Zinkle, S.J. [Oak Ridge National Lab., TN (United States)] [and others

    1996-10-01

    Irradiation at low temperatures (100 to 275{degrees}C) to 0.5 dpa causes significant embrittlement and changes in the subsequent room temperature tensile properties of V-4Cr-4Ti. The yield strength and microhardness at room temperature increase with increasing irradiation temperature. The tensile flow properties at room temperature show large increases in strength and a complete loss of work hardening capacity with no uniform ductility. Embrittlement, as measured by an increase in the ductile-to-brittle transition temperature, increases with increasing irradiation temperature, at least up to 275{degrees}C. This embrittlement is not due to pickup of O or other interstitial solutes during the irradiation.

  17. Low Temperature Irradiation Applied to Neutron Activation Analysis of Mercury In Human Whole Blood

    International Nuclear Information System (INIS)

    Brune, D.

    1966-02-01

    The distribution of mercury in human whole blood has been studied by means of neutron activation analysis. During the irradiation procedure the samples were kept at low temperature by freezing them in a cooling device in order to prevent interferences caused by volatilization and contamination. The mercury activity was separated by means of distillation and ion exchange techniques

  18. Report of the Working Group on low-temperature neutron irradiation

    International Nuclear Information System (INIS)

    1982-07-01

    This report summarizes deliberations at a Working Group meeting sponsored by the Department of Energy, Division of Materials Sciences for the purpose of: (1) assessing the need for maintaining a low temperature neutron irradiation program in the United States; and (2) recommending a course of action based on this assessment

  19. Low Temperature Irradiation Applied to Neutron Activation Analysis of Mercury In Human Whole Blood

    Energy Technology Data Exchange (ETDEWEB)

    Brune, D

    1966-02-15

    The distribution of mercury in human whole blood has been studied by means of neutron activation analysis. During the irradiation procedure the samples were kept at low temperature by freezing them in a cooling device in order to prevent interferences caused by volatilization and contamination. The mercury activity was separated by means of distillation and ion exchange techniques.

  20. The proceedings of 1993-workshop on 'development and application of facilities for low temperature irradiation as well as controlled irradiation'

    International Nuclear Information System (INIS)

    Kuramoto, Eiichi; Okada, Moritami

    1993-03-01

    This is the proceedings of 1992-workshop of the working group on 'Development and Application of Facilities for Low Temperature Irradiation as well as Controlled Irradiation' held at the Research Reactor Institute of Kyoto University on February 23 and 24, 1993. In this workshop until now, studies on irradiation effects in many materials irradiated at lower and higher temperatures have been reported. It has been clearly defined that a careful choice of irradiation conditions is most important. At the present time, a setting plan of exactly controlled irradiation facility, which is able to irradiate with higher temperatures, is in progress. On the other hand, a plan of vertical low temperature irradiation facility has not yet been performed for lack of funds. In last year, a middle scale plan of low temperature irradiation facility, which is possible to irradiate a fast-neutron dose above 10 17 n/cm 2 at about 5K, was proposed in this workshop. In this proceedings, the advanced facility is required to construct to the KUR as soon as possible by many of the workshop members. (author)

  1. Temperature dependence of the deformation behavior of 316 stainless steel after low temperature neutron irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Pawel-Robertson, J.E.; Rowcliffe, A.F.; Grossbeck, M.L. [Oak Ridge National Lab., TN (United States)] [and others

    1996-10-01

    The effects of low temperature neutron irradiation on the tensile behavior of 316 stainless steel have been investigated. A single heat of solution annealed 316 was irradiated to 7 and 18 dpa at 60, 200, 330, and 400{degrees}C. The tensile properties as a function of dose and as a function of temperature were examined. Large changes in yield strength, deformation mode, strain to necking, and strain hardening capacity were seen in this irradiation experiment. The magnitudes of the changes are dependent on both irradiation temperature and neutron dose. Irradiation can more than triple the yield strength over the unirradiated value and decrease the strain to necking (STN) to less than 0.5% under certain conditions. A maximum increase in yield strength and a minimum in the STN occur after irradiation at 330{degrees}C but the failure mode remains ductile.

  2. Model of electron capture in low-temperature glasses

    International Nuclear Information System (INIS)

    Bartczak, W.M.; Swiatla, D.; Kroh, J.

    1983-01-01

    The new model of electron capture by a statistical variety of traps in glassy matrices is proposed. The electron capture is interpreted as the radiationless transition (assisted by multiphonon emission) of the mobile electron to the localized state in the trap. The conception of 'unfair' and 'fair' traps is introduced. The 'unfair' trap captures the mobile electron by the shallow excited state. In contrast, the 'fair' trap captures the electron by the ground state. The model calculations of the statistical distributions of the occupied electron traps are presented and discussed with respect to experimental results. (author)

  3. Development of a Low Temperature Irradiation Capsule for Research Reactor Materials

    International Nuclear Information System (INIS)

    Choo, Kee Nam; Cho, Man Soon; Lee, Cheol Yong; Yang, Sung Woo; Shin, Yoon Taek; Park, Seng Jae; Kang, Suk Hoon; Kang, Young Hwan; Park, Sang Jun

    2013-01-01

    A new capsule design was prepared and tested at HANARO for a neutron irradiation of core materials of research reactors as a part of the research reactor development project. Irradiation testing of the materials including graphite, beryllium, and zircaloy-4 that are supposed to be used as core materials in research reactors was required for irradiation at up to 8 reactor operation cycles at low temperature (<100 .deg. C). Therefore, three instrumented capsules were designed and fabricated for an evaluation of the neutron irradiation properties of the core materials (Graphite, Be, Zircaloy-4) of research reactors. The capsules were first designed and fabricated to irradiate materials at low temperature (<100 .deg. C) for a long cycle of 8 irradiation cycles at HANARO. Therefore, the safety of the new designed capsule should be fully checked before irradiation testing. Out-pile performance and endurance testing before HANARO irradiation testing was performed using a capsule under a 110% condition of a reactor coolant flow amount. The structural integrity of the capsule was analyzed in terms of a vibration-induced fatigue cracking of a rod tip of the capsule that is suspected to be the most vulnerable part of a capsule. Another two capsules were irradiated at HANARO for 4 cycles, and one capsule was transferred to a hot cell to examine the integrity of the rod tip of the capsule. After confirming the soundness of the 4 cycle-irradiated capsule, the remaining capsule was irradiated at up to 8 cycles at HANARO. Based on the structural integrity analysis of the capsule, an improved capsule design will be suggested for a longer irradiation test at HANARO

  4. Batch scale storage of sprouting foods by irradiation combined with natural low temperature; pt. 1

    International Nuclear Information System (INIS)

    Cho, H.O.; Kwon, J.H.; Yang, H.S.; Byun, M.W.; Lee, C.H.

    1982-01-01

    In order to develop the commercial storage method of potatoes by irradiation combined with natural low temperature, two varieties of potatoes, Irish cobbler and Shimabara were stored at natural low temperature storage room (450x650x250cm; year round temperature change, 2-17 degC; 70-85% R.H.) on a batch scale followed by irradiation with optimum dose level. Irish cobbler and Shimabara were 100% sprouted after 3 months storage in control, whereas in 15Krad irradiated group, sprouting was completely inhibited at Irish cobbler for 9 months storage, and at Shimabara for 12 months. The extent of loss due to rot attack after 9 months storage was 6% in control, 6-8% in 10-15Krad irradiated group at Irish cobbler and weight loss was 16.5% in control, 5.1-5.6% in irradiated group, whereas rotting rate of Shimabara after 12 months storage was 100% in control, 15% in irradiated group and the weight loss of its was 12.6% in control, 7.3-7.4% in irradiated group. The moisture content in whole storage period of two varieties were 72-82% without remarkable changes. The total sugar and ascorbic acid contents were slightly decreased according to the dose increase and elapse of storage period, whereas reducing sugar content was increased. Irish cobbler was 90% markrtable after 9 months storage and 85% in Shimabara after 12 months storage. (Author)

  5. Low-temperature formation of high-quality gate oxide by ultraviolet irradiation on spin-on-glass

    International Nuclear Information System (INIS)

    Usuda, R.; Uchida, K.; Nozaki, S.

    2015-01-01

    Although a UV cure was found to effectively convert a perhydropolysilazane (PHPS) spin-on-glass film into a dense SiO x film at low temperature, the electrical characteristics were never reported in order to recommend the use of PHPS as a gate-oxide material that can be formed at low temperature. We have formed a high-quality gate oxide by UV irradiation on the PHPS film, and obtained an interface midgap trap density of 3.4 × 10 11  cm −2 eV −1 by the UV wet oxidation and UV post-metallization annealing (PMA), at a temperature as low as 160 °C. In contrast to the UV irradiation using short-wavelength UV light, which is well known to enhance oxidation by the production of the excited states of oxygen, the UV irradiation was carried out using longer-wavelength UV light from a metal halide lamp. The UV irradiation during the wet oxidation of the PHPS film generates electron-hole pairs. The electrons ionize the H 2 O molecules and facilitate dissociation of the molecules into H and OH − . The OH − ions are highly reactive with Si and improve the stoichiometry of the oxide. The UV irradiation during the PMA excites the electrons from the accumulation layer, and the built-in electric field makes the electron injection into the oxide much easier. The electrons injected into the oxide recombine with the trapped holes, which have caused a large negative flat band voltage shift after the UV wet oxidation, and also ionize the H 2 O molecules. The ionization results in the electron stimulated dissociation of H 2 O molecules and the decreased interface trap density

  6. Low-temperature formation of high-quality gate oxide by ultraviolet irradiation on spin-on-glass

    Energy Technology Data Exchange (ETDEWEB)

    Usuda, R.; Uchida, K.; Nozaki, S., E-mail: nozaki@ee.uec.ac.jp [Graduate School of Informatics and Engineering, The University of Electro-Communications, 1-5-1 Chofugaoka, Chofu-shi, Tokyo 182-1515 (Japan)

    2015-11-02

    Although a UV cure was found to effectively convert a perhydropolysilazane (PHPS) spin-on-glass film into a dense SiO{sub x} film at low temperature, the electrical characteristics were never reported in order to recommend the use of PHPS as a gate-oxide material that can be formed at low temperature. We have formed a high-quality gate oxide by UV irradiation on the PHPS film, and obtained an interface midgap trap density of 3.4 × 10{sup 11 }cm{sup −2} eV{sup −1} by the UV wet oxidation and UV post-metallization annealing (PMA), at a temperature as low as 160 °C. In contrast to the UV irradiation using short-wavelength UV light, which is well known to enhance oxidation by the production of the excited states of oxygen, the UV irradiation was carried out using longer-wavelength UV light from a metal halide lamp. The UV irradiation during the wet oxidation of the PHPS film generates electron-hole pairs. The electrons ionize the H{sub 2}O molecules and facilitate dissociation of the molecules into H and OH{sup −}. The OH{sup −} ions are highly reactive with Si and improve the stoichiometry of the oxide. The UV irradiation during the PMA excites the electrons from the accumulation layer, and the built-in electric field makes the electron injection into the oxide much easier. The electrons injected into the oxide recombine with the trapped holes, which have caused a large negative flat band voltage shift after the UV wet oxidation, and also ionize the H{sub 2}O molecules. The ionization results in the electron stimulated dissociation of H{sub 2}O molecules and the decreased interface trap density.

  7. Electron-dislocation interaction at low temperatures. Progress report

    International Nuclear Information System (INIS)

    1976-01-01

    Studies of the interaction of mobile dislocations with electrons have shown that dislocation motion can be, in part, described by treating the dislocation as an underdamped oscillator. In particular, studies in lead alloys have shown tht dislocation motion can be considered as the motion of string, slightly damped by electrons, without regard for any other lattice friction. In addition we have shown that silver solutes, in lead crystals, occupy, partially, interstitial sites. Finally, we have shown that dislocations in copper interact, unexpectedly, with electrons. This is shown by measuring the influence of a magnetic field on the flow stress of copper crystals at 4.2 0 K

  8. Study of the effect of neutron and electron irradiations on the low temperature thermal conductivity of germanium and silicon; Etude de l'effet des irradiations neutronique et electronique sur la conductibilite thermique aux basses temperatures du germanium et du silicium

    Energy Technology Data Exchange (ETDEWEB)

    Vandevyver, M [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

    1967-06-15

    The main results obtained from this work are the following: 1 Neutron irradiation (at 300 deg. K) produces lattice defects in germanium and silicon, and a corresponding very large lowering of the thermal conductivity is observed in the low temperature region (4-300 ). The results obtained have been explained with the help of the following hypotheses: for silicon a scattering of phonons by the stress fields produced by the defects; for germanium, a supplementary scattering of the electron phonon type. 2 Annealing treatments carried out on these materials above 373 deg. K restored the thermal conductivity over the whole temperature range of the measurements (4-300 deg. K); in the case of both germanium and silicon there were two steps in the annealing process. 3 A study of the thermal conductivity of germanium (initially P or N) after an electronic irradiation showed that the scattering of phonons could depend on the state of charge of the defects thus produced. (author) [French] Les principaux resultats obtenus au cours de ce travail sont les suivants : 1 Les irradiations neutroniques (a 300 deg. K) introduisent des defauts de reseau dans le germanium et le silicium et l'on observe correlativement pour ces materiaux, une tres importante diminution de conductibilite thermique dans le domaine des basses temperatures (4-300 deg. K). Les resultats obtenus ont pu etre interpretes en admettant principalement: pour le silicium, une diffusion des phonons par les champs de contrainte dus aux defauts; pour le germanium, une diffusion additionnelle du type electron-phonon. 2 Des recuits effectues sur ces materiaux au-dessus de 373 deg. K ont montre une restauration de la conductibilite thermique dans tout l'intervalle de temperature de mesure (4-300 deg. K) et comportant pour le germanium et le silicium, deux etapes de recuit 3 L'etude de la conductibilite thermique de germanium (initialement N ou P) apres une irradiation electronique, a montre que la diffusion des phonons

  9. Nonlocal collisionless and collisional electron transport in low temperature plasmas

    Science.gov (United States)

    Kaganovich, Igor

    2009-10-01

    The purpose of the talk is to describe recent advances in nonlocal electron kinetics in low-pressure plasmas. A distinctive property of partially ionized plasmas is that such plasmas are always in a non-equilibrium state: the electrons are not in thermal equilibrium with the neutral species and ions, and the electrons are also not in thermodynamic equilibrium within their own ensemble, which results in a significant departure of the electron velocity distribution function from a Maxwellian. These non-equilibrium conditions provide considerable freedom to choose optimal plasma parameters for applications, which make gas discharge plasmas remarkable tools for a variety of plasma applications, including plasma processing, discharge lighting, plasma propulsion, particle beam sources, and nanotechnology. Typical phenomena in such discharges include nonlocal electron kinetics, nonlocal electrodynamics with collisionless electron heating, and nonlinear processes in the sheaths and in the bounded plasmas. Significant progress in understanding the interaction of electromagnetic fields with real bounded plasma created by this field and the resulting changes in the structure of the applied electromagnetic field has been one of the major achievements of the last decade in this area of research [1-3]. We show on specific examples that this progress was made possible by synergy between full scale particle-in-cell simulations, analytical models, and experiments. In collaboration with Y. Raitses, A.V. Khrabrov, Princeton Plasma Physics Laboratory, Princeton, NJ, USA; V.I. Demidov, UES, Inc., 4401 Dayton-Xenia Rd., Beavercreek, OH 45322, USA and AFRL, Wright-Patterson AFB, OH 45433, USA; and D. Sydorenko, University of Alberta, Edmonton, Canada. [4pt] [1] D. Sydorenko, A. Smolyakov, I. Kaganovich, and Y. Raitses, IEEE Trans. Plasma Science 34, 895 (2006); Phys. Plasmas 13, 014501 (2006); 14 013508 (2007); 15, 053506 (2008). [0pt] [2] I. D. Kaganovich, Y. Raitses, D. Sydorenko, and

  10. Low-temperature epitaxy of silicon by electron beam evaporation

    Energy Technology Data Exchange (ETDEWEB)

    Gorka, B. [Hahn-Meitner-Institut Berlin, Kekulestr. 5, 12489 Berlin (Germany); Dogan, P. [Hahn-Meitner-Institut Berlin, Kekulestr. 5, 12489 Berlin (Germany)], E-mail: pinar.dogan@hmi.de; Sieber, I.; Fenske, F.; Gall, S. [Hahn-Meitner-Institut Berlin, Kekulestr. 5, 12489 Berlin (Germany)

    2007-07-16

    In this paper we report on homoepitaxial growth of thin Si films at substrate temperatures T{sub s} = 500-650 deg. C under non-ultra-high vacuum conditions by using electron beam evaporation. Si films were grown at high deposition rates on monocrystalline Si wafers with (100), (110) and (111) orientations. The ultra-violet visible reflectance spectra of the films show a dependence on T{sub s} and on the substrate orientation. To determine the structural quality of the films in more detail Secco etch experiments were carried out. No etch pits were found on the films grown on (100) oriented wafers. However, on films grown on (110) and (111) oriented wafers different types of etch pits could be detected. Films were also grown on polycrystalline silicon (poly-Si) seed layers prepared by an Aluminum-Induced Crystallisation (AIC) process on glass substrates. Electron Backscattering Diffraction (EBSD) shows that the film growth proceeds epitaxially on the grains of the seed layer. But a considerably higher density of extended defects is revealed by Secco etch experiments.

  11. Formation of hot spots in a superconductor observed by low-temperature scanning electron microscopy

    International Nuclear Information System (INIS)

    Eichele, R.; Seifert, H.; Huebener, R.P.

    1981-01-01

    Low-temperature scanning electron microscopy can be used for the direct observation of hot spots in a superconductor. Experiments performed at 2.10 K with tim films demonstrating the method are reported

  12. Low-temperature radiative recombination of electrons with bare nuclei

    International Nuclear Information System (INIS)

    Omidvar, K.

    1993-01-01

    Aside from empirical formulas, the radiative-recombination cross section and coefficient are usually given in tabulated forms instead of analytic formulas. Here, we give analytic expressions in the form of expansions for the recombination cross section as a function of the electron energy E for low E, and for the recombination coefficient as a function of the temperature T for low T. The expansion coefficients are combinations of confluent hypergeometric functions, and are tabulated for a large number of the final principal and angular-momentum quantum numbers n and l. It is shown that the recombination cross section for arbitrary nuclear charge number Z is independent of Z, while the recombination coefficient for T/Z 2 much-lt 1.58x10 5 K increases as Z 2 . Excellent agreement is found with the published tabulated values

  13. Thermal conductivity of beryllium under low temperature high dose neutron irradiation

    International Nuclear Information System (INIS)

    Chakin, V.P.; Latypov, R.N.; Suslov, D.N.; Kupriyanov, I.B.

    2004-01-01

    Thermal conductivity of compact beryllium of several Russian grades such as TE-400, TE-56, TE-30, TIP and DIP differing in the production technology, grain size and impurity content has been investigated. The thermal diffusivity of beryllium was measured on the disks in the initial and irradiated conditions using the pulse method in the range from room temperature to 200degC. The thermal conductivity was calculated using the table values for the beryllium thermal capacity. The specimens and beryllium neutron source fragments were irradiation in the SM reactor at 70degC and 200degC to a neutron fluence of (0.5-11.4)·10 22 cm -2 (E>0.1 MeV) and in the BOR-60 reactor at 400degC to 16·10 22 cm -2 (E>0.1MeV), respectively. The low-temperature irradiation leads to the drop decrease of the beryllium thermal conductivity and the effect depends on the irradiation parameters. The paper analyses the effect of irradiation parameters (temperature, neutron fluence), measurement temperature and structural factors on beryllium conductivity. The experiments have revealed that the short time post-irradiation annealing at high temperature results in partial reduction of the thermal conductivity of irradiated beryllium. (author)

  14. Low temperature electron microscopy and electron diffraction of the purple membrane of Halobacterium halobium

    International Nuclear Information System (INIS)

    Hayward, S.B.

    1978-09-01

    The structure of the purple membrane of Halobacterium halobium was studied by high resolution electron microscopy and electron diffraction, primarily at low temperature. The handedness of the purple membrane diffraction pattern with respect to the cell membrane was determined by electron diffraction of purple membranes adsorbed to polylysine. A new method of preparing frozen specimens was used to preserve the high resolution order of the membranes in the electron microscope. High resolution imaging of glucose-embedded purple membranes at room temperature was used to relate the orientation of the diffraction pattern to the absolute orientation of the structure of the bacteriorhodopsin molecule. The purple membrane's critical dose for electron beam-induced damage was measured at room temperature and at -120 0 C, and was found to be approximately five times greater at -120 0 C. Because of this decrease in radiation sensitivity, imaging of the membrane at low temperature should result in an increased signal-to-noise ratio, and thus better statistical definition of the phases of weak reflections. Higher resolution phases may thus be extracted from images than can be determined by imaging at room temperature. To achieve this end, a high resolution, liquid nitrogen-cooled stage was built for the JEOL-100B. Once the appropriate technology for taking low dose images at very high resolution has been developed, this stage will hopefully be used to determine the high resolution structure of the purple membrane

  15. Existing and projected neutron sources and low-temperature irradiation facilities in Germany

    International Nuclear Information System (INIS)

    Boening, K.

    1984-01-01

    In this paper, a contribution given at the Kyoto University Research Reactor Institute to the temporal meeting on the design of the facilities for high flux, low temperature irradiation is summarized. The following five subjects were discussed. The project of modernizing the swimming pool type research reactor FRM with 4 MW power at Munich is to achieve relatively high thermal neutron flux, and an extremely compact core is designed. The existing low temperature irradiation facility (LTIF) of the FRM is the most powerful in the world, and has been successfully operated more than 20 years. The fast and thermal neutron fluxes are 2.9 x 10 13 and 3.5 x 10 13 /cm 2 sec, respectively. The experimental techniques in the LTIF of the FRM, such as a measuring cryostat, the mounting of irradiated samples and so on, are described. The installation of new LTIFs in connection with the projects of advanced neutron sources in Germany is likely to be made in the modernized FRM at Garching, in the spallation neutron source SNQ at KFA Juelich and so on. The interesting problems in fundamental and applied researches with LTIFs, and the unusual application of LTIFs are shown. (Kako, I.)

  16. National Low-Temperature Neutron Irradiation Facility (NLTNIF). The status of development

    International Nuclear Information System (INIS)

    Coltman, R.R. Jr.; Kerchner, H.R.; Klabunde, C.E.; Young, F.W. Jr.

    1985-12-01

    In May 1983, the Department of Energy authorized the establishment of a National Low-Temperature Neutron Irradiation Facility (NLTNIF) at ORNL's Bulk Shielding Reactor (BSR). The NLTNIF, which will be available for qualified experiments at no cost to users, will provide a combination of high radiation intensities and special environmental and testing conditions that have not been previously available in the US. Since the DOE authorization, work has proceeded on the design and construction of the new facility without interruption. This report describes the present status of the development of the NLTNIF and the anticipated schedule for completion and performance testing. There is a table of the major specifications and capabilities and a schematic layout of the irradiation cryostate for design and dimensioning of test and experiment assemblies

  17. Degradation of glass-fiber reinforced plastics by low temperature irradiation

    International Nuclear Information System (INIS)

    Nishijima, S.; Nishiura, T.; Ueno, S.; Tsukazaki, Y.; Okada, T.; Okada, T.M.; Miyata, K.; Kodaka, H.

    1998-01-01

    Low-temperature irradiation effects of glass-fiber reinforced plastics (GFRP) have been investigated in terms of mechanical properties such as interlaminar shear strength and creep, in order to obtain the selection standard of insulating materials of superconducting magnets used for fusion reactor. It was revealed that the degradation of interlaminar shear strength was strongly dependent of characteristics of matrix and/or glass/epoxy interface. Especially, the research has been carried out towards the creep behaviour of epoxy which is the matrix of GFRP, by both experimental and simulation method. It was suggested that the synergistic effects was observed in creep test. From the molecular dynamics simulation it was found that the cage effects was the one of the main reason of the stress effects of creep behavior under irradiation. (author)

  18. Low-temperature synthesis of allyl dimethylamine by selective heating under microwave irradiation used for water treatment

    International Nuclear Information System (INIS)

    Tian Binghui; Luan Zhaokun; Li Mingming

    2005-01-01

    Low-temperature synthesis of allyl dimethylamine (ADA) by selective heating under microwave irradiation (MI) used for water treatment is investigated. The effect of MI, ultrasound irradiation (UI) and conventional heating on yield of ADA, reaction time and the flocculation efficiency of polydiallyl dimethylammunion chloride (PDADMAC) prepared form ADA were studied. The results show that by selective heating at low temperature, MI not only increases yield of ADA and reduces reaction time, but also greatly enhances the flocculation efficiency of PDADMAC

  19. Mechanical properties of 1950's vintage 304 stainless steel weldment components after low temperature neutron irradiation

    International Nuclear Information System (INIS)

    Sindelar, R.L.; Caskey, G.R. Jr.; Thomas, J.K.; Hawthorne, J.R.; Hiser, A.L.; Lott, R.A.; Begley, J.A.; Shogan, R.P.

    1991-01-01

    The reactor vessels of the nuclear production reactors at the Savannah River Site (SRS) were constructed in the 1950's from Type 304 stainless steel plates welded with Type 308 stainless steel filler using the multipass metal inert gas process. An irradiated mechanical properties database has been developed for the vessel with materials from archival primary coolant system piping irradiated at low temperatures (75 to 150 degrees C) in the State University of New York at Buffalo reactor (UBR) and the High Flux Isotope Reactor (HFIR) to doses of 0.065 to 2.1 dpa. Fracture toughness, tensile, and Charpy-V impact properties of the weldment components (base, weld, and weld heat-affected-zone (HAZ)) have been measured at temperatures of 25 degrees C and 125 degrees C in the L-C and C-L orientations for materials in both the irradiated and unirradiated conditions for companion specimens. Fracture toughness and tensile properties of specimens cut from an SRS reactor vessel sidewall with doses of 0.1 and 0.5 dpa were also measured at temperatures of 25 and 125 degrees C. The irradiated materials exhibit hardening with loss of work hardenability and a reduction in toughness relative to the unirradiated materials. The HFIR-irradiated materials show an increase in yield strength between about 20% and 190% with a concomitant tensile strength increase between about 15% to 30%. The elastic-plastic fracture toughness parameters and Charpy-V energy absorption both decrease and show only a slight sensitivity to dose. The irradiation-induced decrease in the elastic-plastic fracture toughness (J def at 1 mm crack extension) is between 20% to 65%; the range of J 1C values are 72.8 to 366 kJ/m 2 for the irradiated materials. Similarly, Charpy V-notch results show a 40% to 60% decrease in impact energies

  20. Low temperature irradiation effects on iron boron based amorphous metallic alloys

    International Nuclear Information System (INIS)

    Audouard, A.

    1982-09-01

    Three Fe-B amorphous alloys (Fe 80 B 20 , Fe 27 Mo 2 B 20 and Fe 75 B 25 ) and the crystallized Fe 3 B alloy have been irradiated at the temperature of liquid hydrogen. Electron irradiation and irradiation by 10 B fission fragments induce point defects in amorphous alloys. These defects are characterized by an intrinsic resistivity and a formation volume. The threshold energy for the displacement of iron atoms has also been calculated. Irradiation by 235 U fission fragments induces some important structural modifications in the amorphous alloys [fr

  1. Atomic force microscopy and transmission electron microscopy analyses of low-temperature laser welding of the cornea.

    Science.gov (United States)

    Matteini, Paolo; Sbrana, Francesca; Tiribilli, Bruno; Pini, Roberto

    2009-07-01

    Low-temperature laser welding of the cornea is a technique used to facilitate the closure of corneal cuts. The procedure consists of staining the wound with a chromophore (indocyanine green), followed by continuous wave irradiation with an 810 nm diode laser operated at low power densities (12-16 W/cm(2)), which induces local heating in the 55-65 degrees C range. In this study, we aimed to investigate the ultrastructural modifications in the extracellular matrix following laser welding of corneal wounds by means of atomic force microscopy and transmission electron microscopy. The results evidenced marked disorganization of the normal fibrillar assembly, although collagen appeared not to be denatured under the operating conditions we employed. The mechanism of low-temperature laser welding may be related to some structural modifications of the nonfibrillar extracellular components of the corneal stroma.

  2. Continuous Emission Spectrum Measurement for Electron Temperature Determination in Low-Temperature Collisional Plasmas

    International Nuclear Information System (INIS)

    Liu Qiuyan; Li Hong; Chen Zhipeng; Xie Jinlin; Liu Wandong

    2011-01-01

    Continuous emission spectrum measurement is applied for the inconvenient diagnostics of low-temperature collisional plasmas. According to the physical mechanism of continuous emission, a simplified model is presented to analyze the spectrum in low temperature plasma. The validity of this model is discussed in a wide range of discharge parameters, including electron temperature and ionization degree. Through the simplified model, the continuous emission spectrum in a collisional argon internal inductively coupled plasma is experimentally measured to determine the electron temperature distribution for different gas pressures and radio-frequency powers. The inverse Abel transform is also applied for a better spatially resoluted results. Meanwhile, the result of the continuous emission spectrum measurement is compared to that of the electrostatic double probes, which indicates the effectiveness of this method. (low temperature plasma)

  3. Use of the National Low-Temperature Neutron Irradiation Facility (NLTNIF) for fusion materials research

    International Nuclear Information System (INIS)

    Coltman, R.R. Jr.; Kerchner, H.R.; Klabunde, C.E.

    1986-01-01

    In May 1983 the Division of Materials Sciences, Office of Basic Energy Sciences of the Department of Energy authorized the establishment of a National Low-Temperature Neutron Irradiation Facility (NLTNIF) at ORNL's Bulk Shielding Reactor (BSR). The NLTNIF, which will be available for qualified experiments at no cost to users, will provide a combination of high radiation intensities and special environmental and testing conditions that have not been previously available in the US. Since the DOE authorization, work has proceeded on the design and construction of the new facility without interruption. This report describes the present status of the development of NLTNIF and, for the information of new candidate users, a recounting of the major specifications and capabilities is also given

  4. A theoretical model of accelerated irradiation creep at low temperatures by transient interstitial absorption

    International Nuclear Information System (INIS)

    Stoller, R.E.; Grossbeck, M.L.; Mansur, L.K.

    1990-01-01

    A theoretical model has been developed using the reaction rate theory of radiation effects to explain experimental results that showed higher than expected values of irradiation creep at low temperatures in the Oak Ridge Research Reactor. The customary assumption that the point defect concentrations are at steady state was not made; rather, the time dependence of the vacancy and interstitial concentrations and the creep rate were explicitly calculated. For temperatures below about 100 to 200 degree C, the time required for the vacancy concentration to reach steady state exceeds the duration of the experiment. For example, if materials parameters typical of austenitic stainless steel are used, the calculated vacancy transient dose at 100 degree C is about 100 dpa. At 550 degree C this transient is over by 10 -8 dpa. During the time that the vacancy population remains lower than its steady state value, dislocation climb is increased since defects of primarily one type are being absorbed. Using the time-dependent point defect concentrations, the dislocation climb velocity has been calculated as a function of time and a climb-enabled glide creep model had been invoked. The extended transient time for the vacancies leads to high creep rates at low temperatures. In agreement with the experimental observations, a minimum in the temperature dependence of creep is predicted at a temperature between 50 and 350 degree C. The temperature at which the minimum occurs decreases as the irradiation dose increases. Predicted values of creep at 8 dpa are in good agreement with the results of the ORR-MFE-6J/7J experiment

  5. The Use of Low Temperature Detectors for Direct Measurements of the Mass of the Electron Neutrino

    Directory of Open Access Journals (Sweden)

    A. Nucciotti

    2016-01-01

    Full Text Available Recent years have witnessed many exciting breakthroughs in neutrino physics. The detection of neutrino oscillations has proved that neutrinos are massive particles, but the assessment of their absolute mass scale is still an outstanding challenge in today particle physics and cosmology. Since low temperature detectors were first proposed for neutrino physics experiments in 1984, there has been tremendous technical progress: today this technique offers the high energy resolution and scalability required to perform competitive experiments challenging the lowest electron neutrino masses. This paper reviews the thirty-year effort aimed at realizing calorimetric measurements with sub-eV neutrino mass sensitivity using low temperature detectors.

  6. Reactions of metal-substituted myoglobins with excess electrons studied by pulse radiolysis and low-temperature gamma-radiolysis

    International Nuclear Information System (INIS)

    Miki, Hideho; Nakajima, Atushi; Ogasawara, Masaaki; Tamura, Mamoru

    1990-01-01

    Reactions of metal-substituted myoglobins with excess electrons in electron-pulse-irradiated aqueous solutions at room temperature and γ-irradiated aqueous matrices at 77 K were studied for the purpose of probing the functional role of heme iron. The rate constants for the reactions of various myoglobins with hydrated electrons were not much different from each other, and were close to those of diffusion-controlled reactions. In contrast, the reduction rates of myoglobins with dithionite depended markedly on the kind of central metals in the myoglobins. The difference was interpreted in terms of Marcus' theory for electron-transfer reactions. Effects of the 6-coordinate structure of the cobalt(III) species on the reaction with dithionite was also discussed. The steady-state optical-absorption measurements of γ-irradiated matrices containing cobaltimyoglobin at 77 K demonstrated the reduction of cobalt(III) species by excess electrons produced by the action of ionizing radiation. It was shown, by electron-spin resonance spectroscopy, that a 6-coordinated cobalt(II) species produced at 77 K transformed to a 5-coordinate one at higher temperatures, as reported previously. However, structural relaxation was not observed by optical spectroscopy either in the solutions or in the low-temperature matrices. It was concluded, therefore, that the intermediate 6-coordinate cobalt(II) species gave an optical absorption spectrum which was indistinguishable from that of the relaxed 5-coordinate cobalt(II) species. (author)

  7. Low temperature irradiation effects on iron-boron based amorphous metallic alloys

    International Nuclear Information System (INIS)

    Audouard, Alain.

    1983-01-01

    Three iron-boron amorphous alloys and the crystalline Fe 3 B alloy have been irradiated at liquid hydrogen temperature. 2,4 MeV electron irradiation induces the creation of point defects in the amorphous alloys as well as in the crystalline Fe 3 B alloy. These point defects can be assimilated to iron ''Frenkel pairs''. They have been characterized by determining their intrinsic electrical resistivity and their formation volume. The displacement threshold energy of iron atoms has also been determined. 10 B fission fragments induce, in these amorphous alloys, displacement cascades which lead to stable vacancy rich zones. This irradiation also leads to a structural disorder in relation with the presence of defects. 235 U fission fragments irradiation modifies drastically the structure of the amorphous alloys. The results have been interpreted on the basis of the coexistence of two opposite processes which induce local disorder and crystallisation respectively [fr

  8. Internal friction measurements of Mo after low-temperature proton irradiation

    International Nuclear Information System (INIS)

    Tanimoto, H.; Mizubayashi, H.; Masuda, R.; Okuda, S.; Tagishi, Y.

    1992-01-01

    Internal friction measurements are performed in Mo after 20 MeV proton irradiation in order to clarify the behavior of self-interstitial atoms (SIA's) in Mo. In the low dose range, strong dislocation pinning suggesting the free migration of defects is observed at about 40 K and weak pinning at about 25 K. The features are very similar to those reported after neutron irradiation except that the 25 K pinning is much smaller after proton irradiation. The result suggests that the migration of free SIA's is responsible for the 40 K pinning and that of SIA-defect clusters, probably di-SIA's, formed during irradiation for the 25 K pinning. In the high dose range, the relaxation peaks are observed at about 13 and 41 K, where the close similarities are found between the present peaks and the corresponding peaks reported after neutron irradiation except that the peak height of the 41 K peak per unit concentration of Frenkel pairs (FP) tends to increase strongly with decreasing dose here. The latter fact suggests the strong interaction between SIA's. Then the smallness of the 41 K peak reported after electron irradiation with very high dose could be explained by an increased interaction between SIA's, but not by the two-dimensional migration of SIA's as proposed by Jacques and Robrock. Deformation given prior to irradiation causes a drastic decrease in the modulus defects associated with FP's (so-called bulk effect) and in the 13 K peak height. After neutron irradiation, no such effect of deformation was reported. A possible origin for this difference is discussed. (orig.)

  9. Crystal growth and electronic structure of low-temperature phase SrMgF{sub 4}

    Energy Technology Data Exchange (ETDEWEB)

    Atuchin, Victor V. [Laboratory of Optical Materials and Structures, Institute of Semiconductor Physics, SB RAS, Novosibirsk 630090 (Russian Federation); Functional Electronics Laboratory, Tomsk State University, Tomsk 634050 (Russian Federation); Laboratory of Semiconductor and Dielectric Materials, Novosibirsk State University, Novosibirsk 630090 (Russian Federation); Goloshumova, Alina A. [Laboratory of Crystal Growth, Institute of Geology and Mineralogy, SB RAS, Novosibirsk 630090 (Russian Federation); Isaenko, Ludmila I. [Laboratory of Semiconductor and Dielectric Materials, Novosibirsk State University, Novosibirsk 630090 (Russian Federation); Laboratory of Crystal Growth, Institute of Geology and Mineralogy, SB RAS, Novosibirsk 630090 (Russian Federation); Jiang, Xingxing [BCCRD, Key Laboratory of Functional Crystals and Laser Technology, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Lobanov, Sergey I. [Laboratory of Crystal Growth, Institute of Geology and Mineralogy, SB RAS, Novosibirsk 630090 (Russian Federation); Zhang, Zhaoming [Australian Nuclear Science & Technology Organisation, Lucas Heights, NSW 2234 (Australia); Lin, Zheshuai, E-mail: zslin@mail.ipc.ac.cn [BCCRD, Key Laboratory of Functional Crystals and Laser Technology, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190 (China)

    2016-04-15

    Using the vertical Bridgman method, the single crystal of low temperature phase SrMgF{sub 4} is obtained. The crystal is in a very good optical quality with the size of 10×7×5 mm{sup 3}. Detailed photoemission spectra of the element core levels are determined by a monochromatic AlKa (1486.6 eV) X-ray source. Moreover, the first-principles calculations are performed to investigate the electronic structure of SrMgF{sub 4}. A good agreement between experimental and calculated results is achieved. It is demonstrated that almost all the electronic orbitals are strongly localized and the hybridization with the others is very small, but the Mg–F bonds covalency is relatively stronger than that of Sr–F bonds. - Graphical abstract: Large size of low-temperature phase SrMgF{sub 4} crystal was obtained (right) and its electronic structure was investigated by X-ray photoelectron spectroscopy and first-principles calculation (left). - Highlights: • Large size single crystal of low-temperature phase SrMgF{sub 4} is obtained. • Electronic structure of SrMgF{sub 4} is measured by X-ray photoelectron spectroscopy. • Partial densities of states are determined by first-principles calculation. • Good agreement between experimental and calculated results is achieved. • Strong ionic characteristics of chemical bonds are exhibited in SrMgF{sub 4}.

  10. Low temperature irradiation of iron, zirconium and copper by 10 to 16 MeV protons

    Energy Technology Data Exchange (ETDEWEB)

    Omar, A M

    1978-01-01

    A theoretical analysis of scattering and radiation damage parameters is carried out for 14 MeV neutrons and 10-17 MeV protons on Fe, Ni, Cu, Zr, Nb, and Au. Damage energies are computed for the interactions using both elastic and non-elastic data. The results show that proton encounters deposit a greater damage energy than 14 MeV neutrons. To examine the theoretical results, electrical resistivity measurements are undertaken for Fe, Zr and Cu irradiated at 12 to 17.5K with 10 to 16 MeV protons. Post-irradiation annealing is carried out in situ using a closed-cycle helium-cooled cryostat. Values of the resistivity damage rate are compared with values estimated from the theoretical damage-energy results. Also, the observed stage I recovery is analysed in terms of the corresponding recovery reported for electron and fast-neutron irradiations. The relation between the 16 MeV proton data and published data estimated from a fusion reactor spectrum is discussed. It is also shown that protons create a damage structure similar to a superposition of the damage structures generated by electrons and fast neutrons. The sample state of imperfection is shown to influence the induced damage state in proton irradiation.

  11. The LXCat project: Electron scattering cross sections and swarm parameters for low temperature plasma modeling

    International Nuclear Information System (INIS)

    Pancheshnyi, S.; Biagi, S.; Bordage, M.C.; Hagelaar, G.J.M.; Morgan, W.L.; Phelps, A.V.; Pitchford, L.C.

    2012-01-01

    Graphical abstract: LXCat is an open-access website containing data needed for low temperature plasma modeling as well as on-line tools useful for their manipulation. Highlights: ► LXCat: an open-access website with data for low temperature plasma modeling. ► Contains compilations of electron scattering cross sections and transport data. ► Data from different contributors for many neutral, ground-state species. ► On-line tools for browsing, plotting, up/downloading data. ► On-line Boltzmann solver for calculating electron swarm parameters. - Abstract: LXCat is a dynamic, open-access, website for collecting, displaying, and downloading ELECtron SCATtering cross sections and swarm parameters (mobility, diffusion coefficient, reaction rates, etc.) required for modeling low temperature, non-equilibrium plasmas. Contributors set up individual databases, and the available databases, indicated by the contributor’s chosen title, include mainly complete sets of electron-neutral scattering cross sections, although the option for introducing partial sets of cross sections exists. A database for measured swarm parameters is also part of LXCat, and this is a growing activity. On-line tools include options for browsing, plotting, and downloading cross section data. The electron energy distribution functions (edfs) in low temperature plasmas are in general non-Maxwellian, and LXCat provides an option for execution of an on-line Boltzmann equation solver to calculate the edf in homogeneous electric fields. Thus, the user can obtain electron transport and rate coefficients (averages over the edfs) in pure gases or gas mixtures over a range of values of the reduced electric fields strength, E/N, the ratio of the electric field strength to the neutral density, using cross sections from the available databases. New contributors are welcome and anyone wishing to create a database and upload data can request a username and password. LXCat is part of a larger, community

  12. Irradiation and annealing effects of deuteron irradiated NbTi and V3Ga multifilamentary composite wires at low temperature

    International Nuclear Information System (INIS)

    Seibt, E.

    1975-01-01

    To study the effects of low-temperature irradiation on technological type II-superconductors, NbTi and V 3 Ga multifilamentary composite wires, the critical current I/sub c/ and transition temperature T/sub c/ were measured before and after irradiation with 50-MeV deuterons at 10 and 15 0 K, respectively. While the irradiation effects on I/sub c/ and T/sub c/ of NbTi are substantially unaffected, the V 3 Ga wires undergo a reduction in I/sub c/ of about 50 percent and T/sub c/ decreases from 14.7 +- 0.1 0 K to 12.3 +- 0.1 0 K at a total deuteron flux of 2.6 x 10 17 cm -2 . Annealing experiments at room temperature and 100 0 C show only a small recovery of the superconducting properties up to 15 percent. The field dependence of the volume pinning force densities P/sub V/ was determined and the results are shown to be consistent with a qualitative dynamic pinning model

  13. Organic materials irradiated at very low temperature and at different stopping powers: examples of polyethylene and of cyclohexane molecules trapped in matrix

    International Nuclear Information System (INIS)

    Melot, M.

    2003-10-01

    This thesis concerns the formation mechanisms of defects created in organic materials during irradiation under vacuum, at very low temperature and at different electronic stopping powers. Analysis have been realised by infrared spectroscopy. The first part concerns polyethylene. Irradiating at 8 K allows to dissociate the direct irradiation effects (in cage reactions) and the radical recombination effects. According to the considered chemical groups, the radical mobility leads to very different changes for the formation radiochemical yields. The second part concerns the irradiation of cyclohexane molecules trapped in a solid argon matrix. We evaluate the contribution of intermolecular and intramolecular reactions. The intermolecular reactions have limited consequences when using low ionising radiations but are crucial for heavy ion irradiations. (author)

  14. Apparent increase in the thickness of superconducting particles at low temperatures measured by electron holography

    International Nuclear Information System (INIS)

    Hirsch, J.E.

    2013-01-01

    We predict that superconducting particles will show an apparent increase in thickness at low temperatures when measured by electron holography. This will result not from a real thickness increase, rather from an increase in the mean inner potential sensed by the electron wave traveling through the particle, originating in expansion of the electronic wavefunction of the superconducting electrons and resulting negative charge expulsion from the interior to the surface of the superconductor, giving rise to an increase in the phase shift of the electron wavefront going through the sample relative to the wavefront going through vacuum. The temperature dependence of the observed phase shifts will yield valuable new information on the physics of the superconducting state of metals. - Highlights: • A new property of superconducting particles is predicted. • Electron holography will show an apparent increase in thickness at low temperatures. • This will result from a predicted increase in the mean inner potential. • This will originate in expulsion of electrons from the interior to the surface. • This is not predicted by the conventional BCS theory of superconductivity

  15. Low temperature calorimetry and transmission electron microscopy of helium bubbles in Cu

    International Nuclear Information System (INIS)

    Syskakis, E.

    1985-08-01

    Helium has been introduced into 100 μm thick pure Cu specimens by implantation of α-particles at T = 300 K. Post-implantation annealing of the specimens at high temperatures caused helium to precipitate into bubbles. We have measured the low-temperature heat capacity of helium confined in bubbles of average radius of less than 100 A. The size of the bubbles was obtained by transmission electron microscope investigations. We have observed that helium liquifies at low temperatures and undergoes the transition to the superfluid state in bubbles of average radius larger than 35 A. The confining geometry of bubbles is new and possesses unique features for investigations of confined helium. It provides the possibility to study properties of extremely small, spherical, completely isolated Bose ''particles'' consisting of 10 4 helium atoms each. Furthermore, as we show, it can be known with better accuracy than formerly investigated confining geometries. (orig./BHO)

  16. Apparent increase in the thickness of superconducting particles at low temperatures measured by electron holography.

    Science.gov (United States)

    Hirsch, J E

    2013-10-01

    We predict that superconducting particles will show an apparent increase in thickness at low temperatures when measured by electron holography. This will result not from a real thickness increase, rather from an increase in the mean inner potential sensed by the electron wave traveling through the particle, originating in expansion of the electronic wavefunction of the superconducting electrons and resulting negative charge expulsion from the interior to the surface of the superconductor, giving rise to an increase in the phase shift of the electron wavefront going through the sample relative to the wavefront going through vacuum. The temperature dependence of the observed phase shifts will yield valuable new information on the physics of the superconducting state of metals. Copyright © 2013 Elsevier B.V. All rights reserved.

  17. SiGe Based Low Temperature Electronics for Lunar Surface Applications

    Science.gov (United States)

    Mojarradi, Mohammad M.; Kolawa, Elizabeth; Blalock, Benjamin; Cressler, John

    2012-01-01

    The temperature at the permanently shadowed regions of the moon's surface is approximately -240 C. Other areas of the lunar surface experience temperatures that vary between 120 C and -180 C during the day and night respectively. To protect against the large temperature variations of the moon surface, traditional electronics used in lunar robotics systems are placed inside a thermally controlled housing which is bulky, consumes power and adds complexity to the integration and test. SiGe Based electronics have the capability to operate over wide temperature range like that of the lunar surface. Deploying low temperature SiGe electronics in a lander platform can minimize the need for the central thermal protection system and enable the development of a new generation of landers and mobility platforms with highly efficient distributed architecture. For the past five years a team consisting of NASA, university and industry researchers has been examining the low temperature and wide temperature characteristic of SiGe based transistors for developing electronics for wide temperature needs of NASA environments such as the Moon, Titan, Mars and Europa. This presentation reports on the status of the development of wide temperature SiGe based electronics for the landers and lunar surface mobility systems.

  18. Role of lattice structure and low temperature resistivity in fast-electron-beam filamentation in carbon

    International Nuclear Information System (INIS)

    Dance, R J; Butler, N M H; Gray, R J; MacLellan, D A; Rusby, D R; Xu, H; Neely, D; McKenna, P; Scott, G G; Robinson, A P L; Zielbauer, B; Bagnoud, V; Desjarlais, M P

    2016-01-01

    The influence of low temperature (eV to tens-of-eV) electrical resistivity on the onset of the filamentation instability in fast-electron transport is investigated in targets comprising of layers of ordered (diamond) and disordered (vitreous) carbon. It is shown experimentally and numerically that the thickness of the disordered carbon layer influences the degree of filamentation of the fast-electron beam. Strong filamentation is produced if the thickness is of the order of 60 μm or greater, for an electron distribution driven by a sub-picosecond, mid-10 20 Wcm −2 laser pulse. It is shown that the position of the vitreous carbon layer relative to the fast-electron source (where the beam current density and background temperature are highest) does not have a strong effect because the resistive filamentation growth rate is high in disordered carbon over a wide range of temperatures up to the Spitzer regime. (paper)

  19. Nonlocal effects in a bounded low-temperature plasma with fast electrons

    International Nuclear Information System (INIS)

    DeJoseph, C. A. Jr.; Demidov, V. I.; Kudryavtsev, A. A.

    2007-01-01

    Effects associated with nonlocality of the electron energy distribution function (EEDF) in a bounded, low-temperature plasma containing fast electrons, can lead to a significant increase in the near-wall potential drop, leading to self-trapping of fast electrons in the plasma volume, even if the density of this group is only a small fraction (∼0.001%) of the total electron density. If self-trapping occurs, the fast electrons can substantially increase the rate of stepwise excitation, supply additional heating to slow electrons, and reduce their rate of diffusion cooling. Altering the source terms of these fast electrons will, therefore, alter the near-wall sheath and, through modification of the EEDF, a number of plasma parameters. Self-trapping of fast electrons is important in a variety of plasmas, including hollow-cathode discharges and capacitive rf discharges, and is especially pronounced in an afterglow plasma, which is a key phase of any pulse-modulated discharge. In the afterglow, the electron temperature is less than a few tenths of an electron volt, and the fast electrons will have energies typically greater than an electron volt. It is shown that in the afterglow plasma of noble gases, fast electrons, arising from Penning ionization of metastable atoms, can lead to the above condition and significantly change the plasma and sheath properties. Similar effects can be important in technologically relevant electronegative gas plasmas, where fast electrons can arise due to electron detachment in collisions of negative ions with atomic species. Both experimental and modeling results are presented to illustrate these effects

  20. Low-temperature (200 C or below) fabrication of diamond films for electronic application

    International Nuclear Information System (INIS)

    Hiraki, A.

    2003-01-01

    Fabrication of Diamond (including Diamond Like Carbon: DLC) films as electronic materials, for example: to be used as electron-emitter, requires several following conditions. They are: 1 ) Low temperature fabrication (or deposition on several substrates and sometimes ones with low melting point, like glasses) below 400 C, 2) Wide area film deposition onto wide substrates of several square inches, like Si wafer and glass substrate, 3) Reproducible deposition of well defined film quality, 4) others. In these respects, we have initiated, in the author's laboratories at Osaka University and Kochi University of Technology, a quite new approach to satisfy the above requirements by using microwave plasma CVD under a magnetic field to be called as m agneto-active plasma CVD . The films fabricated by the magnets-active plasma CVD and also recently by cathodic arc methods combined with cur special nano-seeding method, have been utilized for electron emitter to exhibit very high efficiency. (Author)

  1. Electron beam irradiating device

    Energy Technology Data Exchange (ETDEWEB)

    Shinohara, K

    1969-12-20

    The efficiency of an electron beam irradiating device is heightened by improving the irradiation atmosphere and the method of cooling the irradiation window. An irradiation chamber one side of which incorporates the irradiation windows provided at the lower end of the scanner is surrounded by a suitable cooling system such as a coolant piping network so as to cool the interior of the chamber which is provided with circulating means at each corner to circulate and thus cool an inert gas charged therewithin. The inert gas, chosen from a group of such gases which will not deleteriously react with the irradiating equipment, forms a flowing stream across the irradiation window to effect its cooling and does not contaminate the vacuum exhaust system or oxidize the filament when penetrating the equipment through any holes which the foil at the irradiation window may incur during the irradiating procedure.

  2. Effects of low-temperature pretreatment on enhancing properties of refuse-derived fuel via microwave irradiation.

    Science.gov (United States)

    Liu, Zhen; Wang, Han-Qing; Zhou, Yue-Yun; Zhang, Xiao-Dong; Liu, Jian-Wen

    2017-07-01

    The present study focuses on pretreatment of enhancing the properties of refuse-derived fuel (RDF) via low-temperature microwave irradiation. These improved properties include lower chlorine content, a more porous surface structure and better combustion characteristics. In this study, low-temperature microwave irradiation was carried out in a modified microwave apparatus and the range of temperature was set to be 220-300℃. We found that the microwave absorbability of RDF was enhanced after being partly carbonized. Moreover, with the increasing of the final temperature, the organochlorine removal ratio was greatly increased to 80% and the content of chlorine was dramatically decreased to an extremely low level. It was also interesting to find that the chlorine of RDF was mainly released as HCl rather than organic chloride volatiles. The finding is just the same as the polyvinyl chloride pyrolysis process. In addition, pores and channels emerged during the modifying operation and the modified RDF has better combustibility and combustion stability than traditional RDF. This work revealed that low-temperature modification of RDF via microwave irradiation is significant for enhancing the quality of RDF and avoiding HCl erosion of equipment substantially.

  3. A new disordering mechanism in A15 type compounds submitted to low temperature irradiation or to quenching from high temperatures

    International Nuclear Information System (INIS)

    Fluekiger, R.

    1984-05-01

    A new diffusion mechanism describing the changes of the long range order parameter in A15 type compounds after both quenching from high temperatures or low temperature irradiation with high energy particles is presented. It is based on the occupation of nonequilibrium or 'virtual' sites centered halfway between two neighbouring A atoms on 6c sites, arising from the instability of a single 6c vacancy recently found by Welch and coworkers by pair potential calculations. After low temperature irradiation, the occupation of this interstitial site creates the necessary conditions for A B site exchanges over several interatomic distances by focused replacement collision sequences. Due to the occupation of a certain concentration of virtual sites, atomic 'overlapping' is not only possible between A atoms on the chains or between A and B atoms (due to deviations from perfect ordering),but also between B atoms on BBB sequences. The latter are retained after low temperature irradiation only and are responsible for the observed lattice expansion and static displacement. (orig.) [de

  4. Resonance scattering and low-temperature electron mobility in HgTe-based gapless solid solutions

    International Nuclear Information System (INIS)

    Raikh, M.Eh.; Ehfros, A.L.

    1986-01-01

    Low-temperature electron mobility in a gapless semiconductor conditioned by electron resonance scattering on neutral acceptors, the levels of which are located in narrow vicinity near the Fermi level, is calculated. Mobility turns to be inverse proportional to density of acceptor states at the Fermi level. If donor concentration is rather high, then presence of a Coulomb gap at the Fermi level in the density of acceptor states conditioned by long-range character of Coulomb interaction should be taken into account for calculation of mobility. The Fermi level is placed in the tail of the acceptor state density at rather low donor concentration, and the Coulomb gap is absent at the Fermi level. A case of high acceptor concentration, when the acceptor states are delocalized at the Fermi level, is also considered

  5. Study by internal friction of curing low temperature irradiation defects in graphite

    International Nuclear Information System (INIS)

    Rouby, Dominique.

    1974-01-01

    Micromechanical properties and anelastic effects of neutrons irradiated graphites at 300 and 77 0 K are investigated by internal friction analysis and elasticity modulus variations. Defects created by irradiation are studied and evolution versus dose and annealing is followed [fr

  6. Physical nature of structural and phase transformations in Cu-Al α solid solutions upon low-temperature irradiation and subsequent annealing

    Science.gov (United States)

    Petrenko, P. V.; Kulish, N. P.; Mel'nikova, N. A.; Grabovskii, Yu. E.

    2013-12-01

    Methods of X-ray diffraction analysis and measurements of residual resistivity have been used to study effects of electron irradiation in the temperature range of 250-330 K on the structural and phase state of the Cu-15 at % Al solid solution. The results obtained are explained by the presence in the Cu-Al alloys of an inhomogeneous short-range order of two types, i.e., low-temperature, α2 type; and high-temperature, γ2 type.

  7. Development of Ultra Low-Temperature Electronics for the AEgIS Experiment

    CERN Document Server

    Kaltenbacher, Thomas; Kellerbauer, Alban; Doser, Michael; Caspers, Friedhelm

    This thesis presents the development of electronics for operation at cryogenic temperatures, with particular emphasis on the cryogenic electronics required for the Antimatter Experiment: Gravity, Interferometry, Spectroscopy (AEgIS) experiment at the European Organisation for Nuclear Research (CERN). The research is focused on a highly sensitive charged particle detection system for a Penning trap, on cryogenic low-pass filters and on a low-loss DC-contact RF switch. The detection system consists of a high quality factor tuned circuit including a superconducting coil, and a low-noise amplifier. Since the experimental setup of the AEgIS experiment requires it, the developed electronics must reliably operate at 4.2 K (~269C) and in high constant magnetic field of more than 1 Tesla. Therefore, the performance of the cryogenic electronic designs were carefully evaluated at low-temperature/high magnetic field, the result of which have important implications for the AEgIS experiment. Moreover, a new possibility of ...

  8. Structural changes of organic solids caused by irradiation: raman study at very low temperatures

    International Nuclear Information System (INIS)

    Hase, Hirotomo; Ishioka, Kunie; Miyatake, Yoko.

    1995-01-01

    In this paper we first describe a simple liquid helium cryostat and a device of making and mounting organic solid samples. We then present the Raman spectra for irradiated ethanol crystal that were obtained by using the new cryostat and demonstrate how the Raman method is useful for getting insight into structural changes of organic solids caused by irradiation. (J.P.N.)

  9. Impact behavior of 9-Cr and 12-Cr ferritic steels after low-temperature irradiation

    International Nuclear Information System (INIS)

    Klueh, R.L.; Vitek, J.M.; Corwin, W.R.; Alexander, D.J.

    1987-01-01

    Miniature Charpy impact specimens of 9Cr-1MoVNb and 12Cr-1MoVW steels and these steels with 1 and 2% Ni were irradiated in the High-Flux Isotope Reactor (HFIR) at 50 0 C to displacement damage levels of up to 9 dpa. Nickel was added to study the effect of transmutation helium. Irradiation caused an increase in the ductile-brittle transition temperature (DBTT). The 9Cr-1MoVNb steels, with and without nickel, showed a larger shift than the 12Cr-1MoVW steels, with and without nickel. The results indicated that helium also increased the DBTT. The same steels were previously irradiated at higher temperatures. From the present and past tests, the effect of irradiation temperature on the DBTT behavior can be evaluated. For the 9Cr-1MoVNb steel, there is a continuous decrease in the magnitude of the DBTT increase up to an irradiation temperature of about 400 0 C, after which the shift drops rapidly to zero at about 450 0 C. The DBTT of the 12Cr-1MoVW steel shows a maximum increase at an irradiation temperature of about 400 0 C and less of an increase at either higher or lower irradiation temperatures

  10. Optical properties of CsI single crystals irradiated with neutrons at low temperature

    International Nuclear Information System (INIS)

    Okada, M.; Atobe, K.; Itatani, N.; Ozawa, K.

    1998-01-01

    Optical properties of the irradiation-induced-defects in neutron-irradiated CsI single crystals have been investigated. The nominally pure CsI crystals are irradiated by reactor fast neutrons (E>0.1 MeV) with a fluence of 1.4 x 10 15 n/cm 2 at 20 K and by γ-rays from 60 Co source to a dose of 1.5 x 10 4 Gy at liquid nitrogen temperature (LNT). After the irradiations, isochronal annealings are performed to investigate the thermal behavior of the defects. The glow peaks of the thermoluminescence (TL) in each sample irradiated with neutrons at 20 K and with γ-rays at LNT are observed at about 100, 160 and 220 K. In the neutron-irradiated samples at 20 K, the emission band at 338 nm is observed at LNT. It is supposed that this emission band occurs by an excitation of γ-rays from 134 Cs, which is radioactivated by thermal neutrons among the reactor radiations. It is confirmed that the temperature dependence of the 338 nm band is similar with that of the emission band due to the self-trapped exciton which is introduced into the non-irradiated samples illuminated by higher energy photons. (orig.)

  11. Optical properties of CsI single crystals irradiated with neutrons at low temperature

    Energy Technology Data Exchange (ETDEWEB)

    Okada, M. [Kyoto Univ., Kumatori, Osaka (Japan). Research Reactor Inst.; Nakagawa, M. [Faculty of Education, Kagawa Univ., Takamatsu, Kagawa (Japan); Atobe, K. [Faculty of Science, Naruto Univ. of Education, Naruto, Tokushima (Japan); Itatani, N.; Ozawa, K. [Horiba Ltd., Minamiku, Kyoto (Japan)

    1998-05-01

    Optical properties of the irradiation-induced-defects in neutron-irradiated CsI single crystals have been investigated. The nominally pure CsI crystals are irradiated by reactor fast neutrons (E>0.1 MeV) with a fluence of 1.4 x 10{sup 15} n/cm{sup 2} at 20 K and by {gamma}-rays from {sup 60}Co source to a dose of 1.5 x 10{sup 4} Gy at liquid nitrogen temperature (LNT). After the irradiations, isochronal annealings are performed to investigate the thermal behavior of the defects. The glow peaks of the thermoluminescence (TL) in each sample irradiated with neutrons at 20 K and with {gamma}-rays at LNT are observed at about 100, 160 and 220 K. In the neutron-irradiated samples at 20 K, the emission band at 338 nm is observed at LNT. It is supposed that this emission band occurs by an excitation of {gamma}-rays from {sup 134}Cs, which is radioactivated by thermal neutrons among the reactor radiations. It is confirmed that the temperature dependence of the 338 nm band is similar with that of the emission band due to the self-trapped exciton which is introduced into the non-irradiated samples illuminated by higher energy photons. (orig.) 13 refs.

  12. Lipid and carotenoid production by Rhodotorula glutinis under irradiation/high-temperature and dark/low-temperature cultivation.

    Science.gov (United States)

    Zhang, Zhiping; Zhang, Xu; Tan, Tianwei

    2014-04-01

    The capacity of lipid and carotenoid production by Rhodotorula glutinis was investigated under different irradiation conditions, temperatures and C/N ratios. The results showed that dark/low-temperature could enhance lipid content, while irradiation/high-temperature increased the yields of biomass and carotenoid. The optimum C/N ratio for production was between 80 and 100. A two-stage cultivation strategy was used for lipid and carotenoid production in a 5L fermenter. In the first stage, the maximum biomass reached 28.1g/L under irradiation/high-temperature. Then, the cultivation condition was changed to dark/low-temperature, and C/N ratio was adjusted to 90. After the second stage, the biomass, lipid content and carotenoid reached 86.2g/L, 26.7% and 4.2mg/L, respectively. More significantly, the yields of biomass and lipid were 43.1% and 11.5%, respectively. Lipids contained 79.7% 18C and 16.8% 16C fatty acids by GC analysis. HPLC quantified the main carotenoids were β-carotene (68.4%), torularhodin (21.5%) and torulene (10.1%). Crown Copyright © 2014. Published by Elsevier Ltd. All rights reserved.

  13. Irradiation in combination with low temperature storage for preservation of semi-dried mango and longan

    International Nuclear Information System (INIS)

    Noomhorm, A.; Karki, D.B.; Rao, M.S.

    1996-01-01

    Semi dried mango (30% m.c.) and longan (16% m.c.) packed in low density polyethylene were irradiated at doses of 0, 2, 4, 6 and 8 kGy using Cobalt-60 and stored at 14 degree C and 30 degree C. Irradiation had no significant effect (p > 0.05) on acidity, total and reducing sugars, total carotenes, vitamin C content and sensory quality of the product. An irradiation dose of 2 kGy was sufficient to prevent the growth of microorganisms but a high dose of 8 kGy failed to reduce the viable yeast-mold count to neutrality. Irradiation of semi-dried mango and longan at a minimum dose of 2 kGy and subsequent storage at 14 degree C prolonged the shelf life without significant changes in quality

  14. Irradiation in combination with low temperature storage for preservation of semi-dried mango and longan

    Energy Technology Data Exchange (ETDEWEB)

    Noomhorm, A; Karki, D B; Rao, M S [Agricultural and Food Engineering Program, School of Environment, Resources and Development, Asian Institute of Technology, Bangkok (Thailand)

    1996-12-01

    Semi dried mango (30% m.c.) and longan (16% m.c.) packed in low density polyethylene were irradiated at doses of 0, 2, 4, 6 and 8 kGy using Cobalt-60 and stored at 14 degree C and 30 degree C. Irradiation had no significant effect (p > 0.05) on acidity, total and reducing sugars, total carotenes, vitamin C content and sensory quality of the product. An irradiation dose of 2 kGy was sufficient to prevent the growth of microorganisms but a high dose of 8 kGy failed to reduce the viable yeast-mold count to neutrality. Irradiation of semi-dried mango and longan at a minimum dose of 2 kGy and subsequent storage at 14 degree C prolonged the shelf life without significant changes in quality

  15. Thermal conductivity degradation of graphites due to neutron irradiation at low temperature

    International Nuclear Information System (INIS)

    Snead, L.L.; Burchell, T.D.

    1995-01-01

    Several graphites and carbon/carbon composites (C/C's) have been irradiated with fission neutrons near 150 C and at fluences up to a displacement level of 0.24 dpa. The unirradiated room temperature thermal conductivity of these materials varied from 114 W/m K for H-451 isotropic graphite, to 670 W/m K for a unidirectional FMI-1D C/C composite. At the irradiation temperature a saturation reduction in thermal conductivity was seen to occur at displacement levels of approximately 0.1 dpa. All materials were seen to degrade to approximately 10 to 14% of their original thermal conductivity after irradiation. The significant recovery of thermal conductivity due to post-irradiation isochronal anneals is also presented. (orig.)

  16. Effect of low temperature neutron irradiation on the magnetoresistivity in stabilizer materials for a superconducting magnet

    International Nuclear Information System (INIS)

    Nakata, Kiyotomo; Tada, Naobumi; Masaoka, Isao; Takamura, Saburo.

    1985-01-01

    Magnetoresistivity changes caused by neutron irradiation at 5 K, annealing up to 300 K and cyclic irradiation are studied in copper and aluminuim stabilizer materials at 4.2 K. The radiation-induced resistivity in Al is about three times as large as that in Cu, and the resistivities in both Al and Cu are independent of the purity and the degree of cold-work of the samples. The radiation-induced magnetoresistivity of the high purity Cu with R.R.R. (R sub(298 K)/R sub(4.2 K)) of 1400 is larger than that of the impure Cu with R.R.R. of 300 and 280. The magnetoresistivities of the high purity Cu and Al with R.R.R. of 1500 increase with the magetic field. Magnetoresistivity change with the magnetic field in the irradiated Cu mostly follows Kohler's rule, and that in the irradiated Al does not follow the rule at high magnetic fields. By the annealing at 300 K after the irradiation, the radiation-induced resistivity is completely annihilated in the Al, but about 20 % of the resistivity retains in the full-annealed Cu and the retained resistivity is accumulated during the cyclic irradiation. Though the accumulated resistivity in the cold-worked Cu is smaller than that in the full-annealed one, the resistivity before irradiation in the cold-worked samples is very large. From the above results, the full-annealed Cu with R.R.R. of about 300 is considered to be the best material as a stabilizer used under irradiation. (author)

  17. Chitin and Cellulose Processing in Low-Temperature Electron Beam Plasma

    Directory of Open Access Journals (Sweden)

    Tatiana Vasilieva

    2017-11-01

    Full Text Available Polysaccharide processing by means of low-temperature Electron Beam Plasma (EBP is a promising alternative to the time-consuming and environmentally hazardous chemical hydrolysis in oligosaccharide production. The present paper considers mechanisms of the EBP-stimulated destruction of crab shell chitin, cellulose sulfate, and microcrystalline cellulose, as well as characterization of the produced oligosaccharides. The polysaccharide powders were treated in oxygen EBP for 1–20 min at 40 °C in a mixing reactor placed in the zone of the EBP generation. The chemical structure and molecular mass of the oligosaccharides were analyzed by size exclusion and the reversed phase chromatography, FTIR-spectroscopy, XRD-, and NMR-techniques. The EBP action on original polysaccharides reduces their crystallinity index and polymerization degree. Water-soluble products with lower molecular weight chitooligosaccharides (weight-average molecular mass, Mw = 1000–2000 Da and polydispersity index 2.2 and cellulose oligosaccharides with polymerization degrees 3–10 were obtained. The 1H-NMR analysis revealed 25–40% deacetylation of the EBP-treated chitin and FTIR-spectroscopy detected an increase of carbonyl- and carboxyl-groups in the oligosaccharides produced. Possible reactions of β-1,4-glycosidic bonds’ destruction due to active oxygen species and high-energy electrons are given.

  18. Low Temperature Graphene Growth and Its Applications in Electronic and Optical Devices

    Science.gov (United States)

    Chugh, Sunny

    Graphene, a two dimensional allotrope of carbon in a honeycomb lattice, has gathered wide attention due to its excellent electrical, thermal, optical and mechanical properties. It has extremely high electron/hole mobility, very high thermal conductivity and fascinating optical properties, and combined with its mechanical strength and elasticity, graphene is believed to find commercial applications in existing as well as novel technologies. One of the biggest reasons behind the rapid development in graphene research during the last decade is the fact that laboratory procedures to obtain high quality graphene are rather cheap and simple. However, any new material market is essentially driven by the progress in its large scale commercial production with minimal costs, with properties that are suited for different applications. And it is in this aspect that graphene is still required to make a huge progress before its commercial benefits can be derived. Laboratory graphene synthesis techniques such as mechanical exfoliation, liquid phase exfoliation and SiC graphene growth pose several challenges in terms of cost, reliability and scalability. To this end, Chemical Vapor Deposition (CVD) growth of graphene has emerged as a widely used synthesis method that overcomes these problems. Unfortunately, conventional thermal CVD requires a high temperature of growth and a catalytic metal substrate, making the undesirable step of graphene transfer a necessity. Besides requiring a catalyst, the high temperature of growth also limits the range of growth substrates. In this work, I have successfully demonstrated low temperature ( 550 °C) growth of graphene directly on dielectric materials using a Plasma-Enhanced CVD (PECVD) process. The PECVD technique described here solves the issues faced by conventional CVD methods and provides a direct route for graphene synthesis on arbitrary materials at relatively low temperatures. Detailed growth studies, as described here, illustrate the

  19. Low-temperature deuteron irradiation of differently reacted Nb3Sn superconductors

    International Nuclear Information System (INIS)

    Maier, P.; Seibt, E.

    1978-01-01

    Irradiation measurements with 50 MeV deuterons at 18 K and subsequent annealing measurements were performed on Nb 3 Sn single and multifilamentary superconductors at the Helium-Bath Irradiation Facility of the Karlsruhe Cyclotron. The critical current densities jsub(c) of Nb 3 Sn bronze-reacted wire samples at various reaction temperatures (Tsub(R)=650,700,750,800 and 850 0 C) with equal layer thickness were measured for integral deuteron fluxes up to PHIsub(t)=0.7x10 18 cm -2 . After a decrease in jsub(c) of 85% at maximum dose a relatively small annealing effect (4 to 10%) was observed at ambient temperatures. The maximum value of the normalized critical current density, jsub(c)/jsub(c0), at PHIsub(t)approximately=10 17 cm -2 increases with increasing reaction temperature. The difference in volume pinning forces before and after irradiation increases less than linear (approximately√PHIsub(t)) with the irradiation dose. An almost linear dependence between the inverse grain diameter (dsub(K) -1 )) and volume pinning force is obtained both before and after irradiation. (Auth.)

  20. Low temperature internal friction on γ-irradiated polyvinylidene fluoride (PVDF)

    International Nuclear Information System (INIS)

    Callens, A.; Eersels, L.; De Batist, R.

    1978-01-01

    A least-squares fitting of the below room temperature part of the internal friction spectra, obtained by the torsion pendulum technique on as-received and γ-irradiated (up to 1 Grad) strips and fibres of polyvinylidene fluoride by a superposition of single Debye functions, reveals that the spectral component features are determined not only by purely amorphous chain characteristics but also by the dose-dependence of crystallinity. A careful analysis of the relaxation spectra confirms that at least one relaxation effect (approximately 236 K) is created upon irradiation. The analysis of the dose dependence of the characteristics of the β (glass transition; approximately 220 K) and βsub(u) (apparent upper glass transition; approximately 270 K) relaxations, suggests the probable influence of crystallinity on the molecular motion in the amorphous phase. The increase of the intensity of the γ relaxation (approximately 190 K) is related to the irradiation-induced crystallite degradation. (author)

  1. Silicotungstate, a Potential Electron Transporting Layer for Low-Temperature Perovskite Solar Cells.

    Science.gov (United States)

    Choi, Yoon Ho; Kim, Hyun Bin; Yang, In Seok; Sung, Sang Do; Choi, Young Sik; Kim, Jeongho; Lee, Wan In

    2017-08-02

    Thin films of a heteropolytungstate, lithium silicotungstate (Li 4 SiW 12 O 40 , termed Li-ST), prepared by a solution process at low temperature, were successfully applied as electron transporting layer (ETL) of planar-type perovskite solar cells (PSCs). Dense and uniform Li-ST films were prepared on FTO glass by depositing a thin Li-ST buffer layer, followed by coating of a main Li-ST layer. The film thickness was controlled by varying the number of coating cycles, consisting of spin-coating and thermal treatment at 150 °C. In particular, by employing 60 nm-thick Li-ST layer obtained by two cycles of coating, the fabricated CH 3 NH 3 PbI 3 PSC device demonstrates the photovoltaic conversion efficiency (PCE) of 14.26% with J SC of 22.16 mA cm -2 , V OC of 0.993 mV and FF of 64.81%. The obtained PCE is significantly higher than that of the PSC employing a TiO 2 layer processed at the same temperature (PCE = 12.27%). Spectroscopic analyses by time-resolved photoluminescence and pulsed light-induced transient measurement of photocurrent indicate that the Li-ST layer collects electrons from CH 3 NH 3 PbI 3 more efficiently and also exhibits longer electron lifetime than the TiO 2 layer thermally treated at 150 °C. Thus, Li-ST is considered to be a promising ETL material that can be applied for the fabrication of flexible PSC devices.

  2. Separation of {sup 51}Cr by Means of the Szilard-Chalmers Effect from Potassium Chromate Irradiated at Low Temperature

    Energy Technology Data Exchange (ETDEWEB)

    Brune, D

    1967-08-15

    The recombination of {sup 51}Cr in K{sub 2}CrO{sub 4} at low temperature as well as under dilute conditions has been investigated. Crystals of K{sub 2}CrO{sub 4} and a 1 % solution of this compound have been irradiated in a thermal column of a nuclear reactor. Lowering of the temperature was observed to cause a decrease in retention. Chemical separations have been carried out both at 0 C and at 20 deg C. The degree of enrichment was determined by reactivating one part of the solution after separation of the hexavalent chromium. Irradiation of K{sub 2}CrO{sub 4} in the frozen aqueous solution was observed to favour the degree of enrichment. The fate of the {sup 51}Cr recoil nuclide has been discussed in the light of the thermal spike theory.

  3. Separation of 51Cr by Means of the Szilard-Chalmers Effect from Potassium Chromate Irradiated at Low Temperature

    International Nuclear Information System (INIS)

    Brune, D.

    1967-08-01

    The recombination of 51 Cr in K 2 CrO 4 at low temperature as well as under dilute conditions has been investigated. Crystals of K 2 CrO 4 and a 1 % solution of this compound have been irradiated in a thermal column of a nuclear reactor. Lowering of the temperature was observed to cause a decrease in retention. Chemical separations have been carried out both at 0 C and at 20 deg C. The degree of enrichment was determined by reactivating one part of the solution after separation of the hexavalent chromium. Irradiation of K 2 CrO 4 in the frozen aqueous solution was observed to favour the degree of enrichment. The fate of the 51 Cr recoil nuclide has been discussed in the light of the thermal spike theory

  4. Low temperature fatigue crack propagation in neutron irradiated Type 316 steel and weld metal

    International Nuclear Information System (INIS)

    Lloyd, G.J.; Walls, J.D.; Gravenor, J.

    1981-02-01

    The fast cycling fatigue crack propagation characteristics of Type 316 steel and weld metal have been investigated at 380 0 C after irradiation to 1.72-1.92x10 20 n/cm 2 (E>1MeV) and 2.03x10 21 n/cm 2 (E>1MeV) at the same temperature. With mill-annealed Type 316 steel, modest decreases in the rates of crack propagation were observed for both dose levels considered, whereas for cold-worked Type 316 steel irradiation to 2.03x10 21 n/cm 2 (E>1MeV) caused increases in the rate of crack propagation. For Type 316 weld metal, increases in the rate of crack propagation were observed for both dose levels considered. The diverse influences of irradiation upon fatigue crack propagation in these materials are explained by considering a simple continuum mechanics model of crack propagation together with the results of control tensile experiments made on similarly irradiated materials. (author)

  5. Density changes in amorphous Pd80Si20 during low temperature ion irradiation

    International Nuclear Information System (INIS)

    Schumacher, G.; Birtcher, R.C.; Rehn, L.E.

    1994-11-01

    Density changes in amorphous Pd 80 Si 20 during ion irradiation below 100K were detected by in situ HVEM measurements of the changes in specimen length as a function of ion fluence. A decrease in mass density as a function of the ion fluence was observed. The saturation value of the change in mass density was determined to be approximately -1.2%

  6. Proceedings of 1991-workshops of the working group on 'Development and application of facilities for low temperature irradiation as well as controlled irradiation'

    International Nuclear Information System (INIS)

    Kuramoto, Eiichi; Okada, Moritami

    1992-09-01

    This is the proceedings of 1991-workshops of the working group on 'Development and Application of Facilities for Low Temperature Irradiation as well as Controlled Irradiation' held at the Research Reactor Institute of Kyoto University on July 25, 1991 and on February 28, 1992. In the present proceedings, it is emphasized that the study of radiation damages in various materials must be performed under carefully controlled irradiation conditions (irradiation temperature, neutron spectrum and so forth) during reactor irradiations. Especially, it is pointed out that a middle scale reactor such as KUR is suitable for the precise control of neutron spectra. Several remarkable results, which are made through experiments using the Low Temperature Irradiation Facility in KUR (KUR-LTL), are reported. Also, possible advanced research programs are discussed including the worldwide topics on the radiation damages in metals, semi-conductors and also insulators. Further, the present status of KUR-LTL is reported and the advanced plan of the facility is proposed. (author)

  7. Low-temperature irradiation of niobium with 15-MeV neutrons

    International Nuclear Information System (INIS)

    Kerchner, H.R.; Coltman, R.R. Jr.; Klabunde, C.E.; Sekula, S.T.

    1978-01-01

    Niobium was irradiated at 4.2 K with high energy d-Be neutrons to a fluence of 3.7x10 15 n/cm 2 . The neutrons were generated at the Oak Ridge Isochronous Cyclotron by the breakup reaction of 40-MeV deuterons in a thick Be target. The resulting neutron energy spectrum was broadly peaked near 15 MeV. The 0.012-cm-diameter wire sample (RRR=200) was situated in a uniform transverse magnetic field. The critical current, flux flow resistance, and normal state resistance were measured by using a standard four-terminal technique. The critical current density and the flux flow resistivity were observed to increase with irradiation and to decrease toward the preirradiation values with subsequent isochronal annealing between 4.2 K and 360 K. Using recent theories of flux line lattice deformation, the elementary pinning force is deduced and the result is compared to theoretical calculations. (Auth.)

  8. The effect of low-temperature neutron irradiation on the critical current of some superconducting materials

    International Nuclear Information System (INIS)

    Takamura, S.; Okuda, S.

    1978-01-01

    The critical current densities of pure V and Nb single crystals, single core Nb-50 wt% Ti coated with Cu and Nb 3 Sn were measured after fast neutron irradiation at about 5 K and during subsequent annealings. The peak effect was observed in V and Nb single cyrstals immediately after irradiation. In V, the peak effect disappeared after subsequent annealing above 200 K (in the so-called stage III recovery where vacancies are considered to anneal out in V). In contrast, in Nb the peak effect did not disappear even after annealing at 300 K (above the stage III recovery of Nb). Furthermore, in V the peak effect showed a remarkable recovery at 120 K where about 50% of the resistivity increase recovered. The elementary force of the fluxoid-defect interaction was estimated in V single crystals. (Auth.)

  9. The effect of composition, electron irradiation and quenching on ...

    Indian Academy of Sciences (India)

    The ionic conductivity at room temperature exhibits a characteristic double peak for the composition = 20 and 70. Both electron beam irradiation and quenching at low temperature have resulted in an increase in conductivity by 1–2 orders of magnitude. The enhancement of conductivity upon irradiation and quenching is ...

  10. Breakdown of the independent electron picture in mesoscopic samples at low temperatures: The hunt for the Unicorn

    Science.gov (United States)

    Webb, R. A.

    1998-03-01

    A variety of experiments are discussed where, at low temperatures, it appears that the non-interacting picture of electrons in a Fermi liquid description of a mesoscopic sample is breaking down. Specifically, experiments on the temperature dependence of the phase-coherence time, energy relaxation rate, spin-flip scattering time, persistent currents in normal metals and transmission through a barrier in the fractional quantum Hall regime all display low-temperature properties which can not be accounted for in the independent electron picture.

  11. Low-temperature positron-lifetime studies of proton-irradiated silicon

    DEFF Research Database (Denmark)

    Mäkinen, S.; Rajainmäki, H.; Linderoth, Søren

    1990-01-01

    The positron-lifetime technique has been used to identify defects created in high-purity single-crystal silicon by irradiation with 12-MeV protons at 15 K, and the evolution of the defects has been studied by subsequent annealings between 20 and 650 K. Two clear annealing steps were seen...... in the samples, the first starting at 100 K and the other at 400 K. The first is suggested to be a result of the migration of free, negatively charged monovacancies, and the second is connected to the annealing of some vacancy-impurity complexes, probably negatively charged vacancy-oxygen pairs. The specific...

  12. Low temperature thermal annealing in fast neutron-irradiated potassium permanganate

    Energy Technology Data Exchange (ETDEWEB)

    Owens, C W; Lecington, W C [New Hampshire Univ., Durham (USA). Dept. of Chemistry

    1975-01-01

    The effect of thermal annealing on the retention of recoil /sup 54/Mn as permanganate in crystalline KMnO/sub 4/ irradiated with fast neutrons at liquid nitrogen temperature has been studied. The retention after 4 hrs of annealing increases from about 8% at -196/sup 0/ to a maximum of 61% at 180/sup 0/, then decreases at higher temperatures. A single activation energy (approximately 0.01 eV) applies to the thermal annealing process between -196/sup 0/ and -40/sup 0/. Extrapolation of the data suggests that below -229/sup 0/ no thermal annealing would occur.

  13. Internal friction in Al alloys after neutron irradiation at low temperature

    International Nuclear Information System (INIS)

    Takamura, S.; Kobiyama, M.

    1985-01-01

    Internal friction and elastic modulus of dilute Al alloys have been measured after fast neutron irradiation at about 5 K. The internal friction spectra in Al-Pb, Al-Si, Al-Zn, Al-Ag, Al-Sn and Al-In are very similar. This result suggests that the configuration of the interstitial-solute atom complex in these alloys is very similar. In Al-Mg, the main complexes have the configuration with nearly symmetry, but its internal friction spectrum is different from that of the above-mentioned alloys. The internal friction spectra and their annealing behavior in Al-Be, Al-Mn, Al-Fe and Al-Cu demonstrate that the configuration of their interstitial-solute atom complex seems to be different from each other and the main complex in these alloys is immobile until stage III. (author)

  14. Effects of low temperature neutron irradiation on the mechanical properties of iron single crystals

    International Nuclear Information System (INIS)

    Kitajima, K.; Abe, H.; Takamura, S.; Okuda, S.

    1975-01-01

    Measurements were made on tensile properties and their recovery characteristics of single crystals of pure iron and iron containing carbon of 4 to 60 ppm irradiated in reactor to the dose of 3 x 10 16 to approximately 3 x 10 17 nvt (greater than 0.1 MeV) at approximately 5 0 K. The yield stress showed large softening at less than or equal to 90 0 K saturating to a value nearly independent of orientations for greater than or equal to 1 x 10 17 nvt. The softening recovered and hardening set in at several temperature stages. The activation energies of the recovery and the activation parameters of plastic deformations at various annealing stages were determined. Carbon suppressed the softening and its recovery but much enhanced the hardening at the stage of 300 to approximately 400 0 K

  15. Micromachined Joule-Thomson coolers for cooling low-temperature detectors and electronics

    Science.gov (United States)

    ter Brake, Marcel; Lerou, P. P. P. M.; Burger, J. F.; Holland, H. J.; Derking, J. H.; Rogalla, H.

    2017-11-01

    The performance of electronic devices can often be improved by lowering the operating temperature resulting in lower noise and larger speed. Also, new phenomena can be applied at low temperatures, as for instance superconductivity. In order to fully exploit lowtemperature electronic devices, the cryogenic system (cooler plus interface) should be `invisible' to the user. It should be small, low-cost, low-interference, and above all very reliable (long-life). The realization of cryogenic systems fulfilling these requirements is the topic of research of the Cooling and Instrumentation group at the University of Twente. A MEMS-based cold stage was designed and prototypes were realized and tested. The cooler operates on basis of the Joule-Thomson effect. Here, a high-pressure gas expands adiabatically over a flow restriction and thus cools and liquefies. Heat from the environment (e.g., an optical detector) can be absorbed in the evaporation of the liquid. The evaporated working fluid returns to the low-pressure side of the system via a counter-flow heat exchanger. In passing this heat exchanger, it takes up heat from the incoming high-pressure gas that thus is precooled on its way to the restriction. The cold stage consists of a stack of three glass wafers. In the top wafer, a high-pressure channel is etched that ends in a flow restriction with a height of typically 300 nm. An evaporator volume crosses the center wafer into the bottom wafer. This bottom wafer contains the lowpressure channel thus forming a counter-flow heat exchanger. A design aiming at a net cooling power of 10 mW at 96 K and operating with nitrogen as the working fluid was optimized based on the minimization of entropy production. The optimum cold finger measures 28 mm x 2.2 mm x 0.8 mm operating with a nitrogen flow of 1 mg/s at a high pressure of 80 bar and a low pressure of 6 bar. The design and fabrication of the coolers will be discussed along with experimental results.

  16. Suppression of carbon desorption from 4H-SiC by irradiating a remote nitrogen plasma at a low temperature

    Science.gov (United States)

    Shimabayashi, Masaharu; Kurihara, Kazuaki; Sasaki, Koichi

    2018-05-01

    We remotely irradiated a nitrogen plasma onto the carbon-side surface of 4H-SiC at a low temperature, and examined the effect of sample cooling on the characteristics of the nitride layer. An improved nitride layer, which had higher concentrations of carbon and silicon and a lower concentration of oxygen, was formed in the region at depths of more than 0.6–0.9 nm from the top surface. The depth of the fragile nitride layer in the top region, where no improved characteristics of the nitride layer were observed, became smaller with sample cooling. In addition, on the basis of the experimental results, we discussed the difference in the activation energy of the nitriding reaction of 4H-SiC supported by atomic nitrogen and molecular nitrogen in the metastable \\text{A}3Σ \\text{u} + state.

  17. Failure criteria for low-temperature irradiated organic composite insulation systems

    International Nuclear Information System (INIS)

    Schutz, J.B.; Fabian, P.E.

    1997-01-01

    Composite insulation systems in fusion magnet applications are often subjected to conditions of combined through thickness compression and shear at varying stress ratios. Characterization of insulation system strength under these conditions requires unidirectional shear and compression tests, as well as biaxial shear/compression testing to define the systems failure envelope. An appropriate failure criteria would reduce the number of tests required to define this envelope, and would give designers a better estimate of material strengths at intermediate stress ratios. Biaxial shear/compression testing requires the use of metallic sandwich specimens, which are susceptible to activation during irradiation. A reliable failure criteria which eliminates the need for biaxial characterization would also reduce the difficulty and expense involved in radiation effects characterization while still providing a complete failure envelope. Several generalized failure criteria, taken from classical composites analysis, were reformulated for application in the shear/compression quadrant. The maximum stress and Tsai-Hill criteria were found to be inadequate to represent the biaxial failure envelope. The generalized Tsai-Wu tensor quadratic failure criterion was also examined. Application of this criterion requires through thickness tensile strength data. Through thickness tensile strengths of insulation systems have not been routinely characterized, but limited data are available. Utilizing unidirectional through thickness tension, compression, and interlaminar shear strength data, the Tsai-Wu failure criteria was found to agree well with biaxial shear/compression test data

  18. Internal friction of Fe-B alloys neutron irradiated at low temperature

    International Nuclear Information System (INIS)

    Kitajima, Kazunori; Futagami, Koji; Abe, Hironobu; Yoshida, Hiroyuki.

    1975-01-01

    Measurements were made on the internal friction of Fe-B alloys irradiated by neutron at 16 0 K to the dose of 3x10 16 nvt (>1 MeV) and 6x10 17 nvt (thermal). Boron was used to enhance the production of defects by the nuclear transformation B 10 (n,α)Li 7 . Relaxation peaks were found in specimens containing dispersed fine precipitates of NbB 2 in range of B 500--7200 wt ppm and Nb 2000--30000 wt ppm. The most prominent peak is the one with the peak temperature of 169 0 K at the frequency of 264 c/sec. Activation energy determined from the peak shift is 0.28+-0.01 eV, which is nearly equal to that of migration of self-interstitial reported on pure iron. However activation energy of the decay of peaks by annealing is about 0.7 eV. Interpretation was presented that the peak may be attributed to re-orientation of self-interstitials loosely bound to a boron atom. (auth.)

  19. Dielectric properties of the ITER TFMC insulation after low temperature reactor irradiation

    International Nuclear Information System (INIS)

    Humer, K.; Weber, H.W.; Hastik, R.; Hauser, H.; Gerstenberg, H.

    2001-01-01

    The insulation system for the Toroidal Field Model Coil of ITER is a fiber reinforced plastic (FRP) laminate, which consists of a combined Kapton/R-glass-fiber reinforcement tape, vacuum-impregnated with an epoxy DGEBA system. Pure disk shaped laminates, disk shaped FRP/stainless-steel sandwiches, and conductor insulation prototypes were irradiated at 5 K in a fission reactor up to a fast neutron fluence of 10 22 m -2 (E>0.1MeV) to investigate the radiation induced degradation of the dielectric strength of the insulation system. After warm-up to room temperature, swelling, weight loss, and the breakdown strength were measured at 77 K. The sandwich swells by 4% at a fluence of 5x10 21 m -2 and by 9% at 1x10 22 m -2 . The weight loss of the FRP is 2% at 1x10 22 m -2 . The dielectric strength remained unchanged over the whole dose range. (author)

  20. Electron irradiation of zeolites

    International Nuclear Information System (INIS)

    Wang, S.X.; Wang, L.M.; Ewing, R.C.

    1999-01-01

    Three different zeolites (analcime, natrolite, and zeolite-Y) were irradiated with 200 keV and 400 keV electrons. All zeolites amorphized under a relatively low electron fluence. The transformation from the crystalline-to-amorphous state was continuous and homogeneous. The electron fluences for amorphization of the three zeolites at room temperature were: 7.0 x 10 19 e - /cm 2 (analcime), 1.8 x 10 20 e - /cm 2 (natrolite), and 3.4 x 10 20 e - /cm 2 (zeolite-Y). The different susceptibilities to amorphization are attributed to the different channel sizes in the structures which are the pathways for the release of water molecules and Na + . Natrolite formed bubbles under electron irradiation, even before complete amorphization. Analcime formed bubbles after amorphization. Zeolite-Y did not form bubbles under irradiation. The differences in bubble formation are attributed to the different channel sizes of the three zeolites. The amorphization dose was also measured at different temperatures. An inverse temperature dependence of amorphization dose was observed for all three zeolites: electron dose for amorphization decreased with increasing temperature. This unique temperature effect is attributed to the fact that zeolites are thermally unstable. A semi-empirical model was derived to describe the temperature effect of amorphization in these zeolites

  1. Radiation clusters formation and evolution in FCC metals at low-temperature neutron irradiation up to small damage fluences

    International Nuclear Information System (INIS)

    Kozlov, A.V.; Shcherbakov, E.N.; Asiptsov, O.I.; Skryabin, L.A.; Portnykh, I.A.

    2006-01-01

    Methods of transmission electron microscopy and precision size measurements are used to study the formation of radiation-induced clusters in FCC metals (Ni, Pt, austenitic steels EhI-844, ChS-68) irradiated with fast neutron (E>0.1 MeV) fluences from 7 x 10 21 up to 3.5 x 10 22 m -2 at a temperature of 310 K. Using statistical thermodynamic methods the process of radiation clusters formation and evolution is described quantitatively. The change in the concentration of point defects under irradiation as well as size variations of irradiated specimens on annealing are calculated [ru

  2. The kinetics of low-temperature electron-phonon relaxation in a metallic film following instantaneous heating of the electrons

    International Nuclear Information System (INIS)

    Bezuglyi, A.I.; Shklovskii, V.A.

    1997-01-01

    The theoretical analysis of experiments on pulsed laser irradiation of metallic films sputtered on insulating supports is usually based on semiphenomenological dynamical equations for the electron and phonon temperatures, an approach that ignores the nonuniformity and the nonthermal nature of the phonon distribution function. In this paper we discuss a microscopic model that describes the dynamics of the electron-phonon system in terms of kinetic equations for the electron and phonon distribution functions. Such a model provides a microscopic picture of the nonlinear energy relaxation of the electron-phonon system of a rapidly heated film. We find that in a relatively thick film the energy relaxation of electrons consists of three stages: the emission of nonequilibrium phonons by 'hot' electrons, the thermalization of electrons and phonons due to phonon reabsorption, and finally the cooling of the thermalized electron-phonon system as a result of phonon exchange between film and substrate. In thin films, where there is no reabsorption of nonequilibrium phonons, the energy relaxation consists of only one stage, the first. The relaxation dynamics of an experimentally observable quantity, the phonon contribution to the electrical conductivity of the cooling film, is directly related to the dynamics of the electron temperature, which makes it possible to use the data of experiments on the relaxation of voltage across films to establish the electron-phonon and phonon-electron collision times and the average time of phonon escape from film to substrate

  3. Sewage sludge irradiation with electrons

    International Nuclear Information System (INIS)

    Tauber, M.

    1976-01-01

    The disinfection of sewage sludge by irradiation has been discussed very intensively in the last few months. Powerful electron accelerators are now available and the main features of the irradiation of sewage sludge with fast electrons are discussed and the design parameters of such installations described. AEG-Telefunken is building an irradiation plant with a 1.5 MeV, 25 mA electron accelerator, to study the main features of electron irradiation of sewage sludge. (author)

  4. Precipitation in 20 Cr-25 Ni type stainless steel irradiated at low temperatures in a thermal reactor (AGR)

    International Nuclear Information System (INIS)

    Taylor, C.

    1983-01-01

    The effects of irradiation on the microstructure of AGR fuel rod cladding have been studied by analytical electron microscopy. Two alloys were investigated, the standard 20 Cr-25 Ni steel stabilised with Nb and a variant containing less Nb but strengthened with a dispersion of TiN precipitates. Irradiation at 360 deg C to 480 deg C produced (Ni, Si)-rich precipitates in both alloys; additionally the standard alloy contained (Ni, Nb, Si)-rich precipitates when irradiated at 440 deg C to 640 deg C. While similar features have been observed in other austenitic stainless steels irradiated in fast reactors, where the lattice-damage rate is greater than in a thermal reactor, their formation is not predicted by isothermal equilibrium diagrams. It is suggested here that the phases are irradiation-induced and that the total displacement damage is the controlling factor. Cladding solution-treated above 1050 deg C then irradiated at 2 -based reactor coolant occurred in cladding with low levels of cold-work at the outer surface, also resulting in Cr-rich carbide formation. (author)

  5. Low temperature scanning electron microscopic studies on the interaction of globodera rostochiensis woll. and trichoderma harzianum rifai

    International Nuclear Information System (INIS)

    Saifullah, A.; Khan, N.U.

    2014-01-01

    Low temperature scanning electron microscopic (LTSEM) studies revealed that Trichoderma harzianum infected mature potato cysts nematode eggs by penetrating directly the cyst wall or via natural opening of mouth. Mycelial penetration on cyst wall or egg surface has been seen. The penetration of cyst wall or egg surface was either chemical or mechanical (directly or with appresorium) or both. Freeze fractionation showed the presence of mycelia inside the eggs. (author)

  6. In-situ study of cascade defects in silver by simultaneous transmission electron microscopy and electrical resistivity measurements at low temperatures

    International Nuclear Information System (INIS)

    Haga, K.; King, W.E.; Merkle, K.L.; Meshii, M.

    1985-12-01

    A helium-cooled double-tilt specimen stage for transmission electron microscopy (TEM) with the capability of simultaneous electrical resistivity measurements was constructed and used to study defect-production, migration, clustering and recovery processes in ion-irradiated silver. Vacuum-evaporated thin film specimens were irradiated with 1 MeV Kr + -ions up to a dose of 4.0 x 10 10 ions/cm 2 , at T = 10 0 K in the microscope, using the HVEM-tandem accelerator ion beam interface system in the Argonne National Laboratory Electron Microscopy Center. Cascade defect formation during ion bombardment at the low temperature was directly observed both by TEM and electrical resistivity measurements. Ion bombardment created groups of defect clusters with strong strain fields which gave rise to TEM contrast. The specimen resistivity was increased by 16% during the irradiation. Subsequent microstructural changes and resistivity recovery during isochronal annealing were monitored up to room temperature. 58.3% of the irradiation induced resistivity was recovered, while significant reduction in the size of black spot defect clusters was observed by TEM. A small fraction of clusters disappeared, while no nucleation of new defect clusters was observed

  7. Irradiations at low temperatures. 1. part: devices designs; Les irradiations aux basses temperatures. Premiere partie: conception des dispositifs

    Energy Technology Data Exchange (ETDEWEB)

    Conte, R.R. [Commissariat a l' Energie Atomique, Fontenay-aux-Roses (France). Centre d' Etudes Nucleaires

    1969-07-01

    After an attempt to sort out the irradiation devices, the different refrigeration systems used: stored liquid or refrigerators, are presented. Some financial aspects of these two systems are discussed. For a long run, 1000 hr per year (100 hr for He) the refrigerator become less expensive than stored liquid devices. Some ideas about the principal criterions in the device design are discussed. Finally a few elements making easier the calculation of the different parts of a cryostat are given. (author) [French] Apres un essai de classification des dispositifs d'irradiation, on presente les divers modes de refrigeration: liquides stockes ou refrigerateurs. On discute quelques aspects financiers des deux principes. Il apparait que pour des durees de fonctionnement d'environ 1 000 heures par an les refrigerateurs deviennent plus rentables (-100 heures pour He). On classe ensuite quelques idees sur les principaux criteres de conception des dispositifs. Enfin on donne quelques elements facilitant le calcul des differentes parties d'un cryostat. (auteur)

  8. Irradiations at low temperatures. 1. part: devices designs; Les irradiations aux basses temperatures. Premiere partie: conception des dispositifs

    Energy Technology Data Exchange (ETDEWEB)

    Conte, R R [Commissariat a l' Energie Atomique, Fontenay-aux-Roses (France). Centre d' Etudes Nucleaires

    1969-07-01

    After an attempt to sort out the irradiation devices, the different refrigeration systems used: stored liquid or refrigerators, are presented. Some financial aspects of these two systems are discussed. For a long run, 1000 hr per year (100 hr for He) the refrigerator become less expensive than stored liquid devices. Some ideas about the principal criterions in the device design are discussed. Finally a few elements making easier the calculation of the different parts of a cryostat are given. (author) [French] Apres un essai de classification des dispositifs d'irradiation, on presente les divers modes de refrigeration: liquides stockes ou refrigerateurs. On discute quelques aspects financiers des deux principes. Il apparait que pour des durees de fonctionnement d'environ 1 000 heures par an les refrigerateurs deviennent plus rentables (-100 heures pour He). On classe ensuite quelques idees sur les principaux criteres de conception des dispositifs. Enfin on donne quelques elements facilitant le calcul des differentes parties d'un cryostat. (auteur)

  9. A cryogen-free low temperature scanning tunneling microscope capable of inelastic electron tunneling spectroscopy

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Shuai; Huang, Di [State Key Laboratory of Surface Physics, Key Laboratory of Micro and Nano Photonic Structures (MOE), and Department of Physics, Fudan University, Shanghai 200433 (China); Wu, Shiwei, E-mail: swwu@fudan.edu.cn [State Key Laboratory of Surface Physics, Key Laboratory of Micro and Nano Photonic Structures (MOE), and Department of Physics, Fudan University, Shanghai 200433 (China); Collaborative Innovation Center of Advanced Microstructures, Fudan University, Shanghai 200433 (China)

    2016-06-15

    The design and performance of a cryogen-free low temperature scanning tunneling microscope (STM) housed in ultrahigh vacuum (UHV) are reported. The cryogen-free design was done by directly integrating a Gifford-McMahon cycle cryocooler to a Besocke-type STM, and the vibration isolation was achieved by using a two-stage rubber bellow between the cryocooler and a UHV-STM interface with helium exchange gas cooling. A base temperature of 15 K at the STM was achieved, with a possibility to further decrease by using a cryocooler with higher cooling power and adding additional low temperature stage under the exchange gas interface. Atomically sharp STM images and high resolution dI/dV spectra on various samples were demonstrated. Furthermore, we reported the inelastic tunneling spectroscopy on a single carbon monoxide molecule adsorbed on Ag(110) surface with a cryogen-free STM for the first time. Being totally cryogen-free, the system not only saves the running cost significantly but also enables uninterrupted data acquisitions and variable temperature measurements with much ease. In addition, the system is capable of coupling light to the STM junction by a pair of lens inside the UHV chamber. We expect that these enhanced capabilities could further broaden our views to the atomic-scale world.

  10. A cryogen-free low temperature scanning tunneling microscope capable of inelastic electron tunneling spectroscopy.

    Science.gov (United States)

    Zhang, Shuai; Huang, Di; Wu, Shiwei

    2016-06-01

    The design and performance of a cryogen-free low temperature scanning tunneling microscope (STM) housed in ultrahigh vacuum (UHV) are reported. The cryogen-free design was done by directly integrating a Gifford-McMahon cycle cryocooler to a Besocke-type STM, and the vibration isolation was achieved by using a two-stage rubber bellow between the cryocooler and a UHV-STM interface with helium exchange gas cooling. A base temperature of 15 K at the STM was achieved, with a possibility to further decrease by using a cryocooler with higher cooling power and adding additional low temperature stage under the exchange gas interface. Atomically sharp STM images and high resolution dI/dV spectra on various samples were demonstrated. Furthermore, we reported the inelastic tunneling spectroscopy on a single carbon monoxide molecule adsorbed on Ag(110) surface with a cryogen-free STM for the first time. Being totally cryogen-free, the system not only saves the running cost significantly but also enables uninterrupted data acquisitions and variable temperature measurements with much ease. In addition, the system is capable of coupling light to the STM junction by a pair of lens inside the UHV chamber. We expect that these enhanced capabilities could further broaden our views to the atomic-scale world.

  11. Using electron irradiation to probe iron-based superconductors

    Science.gov (United States)

    Cho, Kyuil; Kończykowski, M.; Teknowijoyo, S.; Tanatar, M. A.; Prozorov, R.

    2018-06-01

    High-energy electron irradiation at low temperatures is an efficient and controlled way to create vacancy–interstitial Frenkel pairs in a crystal lattice, thereby inducing nonmagnetic point-like scattering centers. In combination with London penetration depth and resistivity measurements, the electron irradiation was used as a phase-sensitive probe to study the superconducting order parameter in iron-based superconductors (FeSCs), lending strong support to sign-changing s ± pairing. Here, we review the key results of the effect of electron irradiation in FeSCs.

  12. Final report on neutron irradiation at low temperature to investigate plastic instability and a high temperature to study cavitation

    International Nuclear Information System (INIS)

    Singh, B.N.; Eldrup, M.; Golubov, S.I.; Edwards, D.J.; Jung, P.

    2005-01-01

    Effects of neutron irradiation on defect accumulation and physical and mechanical properties of pure iron and F82H and EUROFER 97 ferritic-martensitic steels have been investigated. Tensile specimens were neutron irradiated to a dose level of 0,23 dpa at 333 and 573 K. Electrical resistivity and tensile properties were measured both in the unirradiated and irradiated condition. Some additional specimens of pure iron were irradiated at 333 K to doses of 10-3, 10-2 and 10-1 dpa and tensile tested at 333 K. To investigate the effect of helium on cavity nucleation and growth, specimens of pure iron and EUROFER 97 were implanted with different amounts of helium at 323 K and subsequently neutron irradiated to doses of 10-3, 10-2 and 10-1 dpa at 323 K. Defect microstructures were investigated using positron annihilation spectroscopy (PAS) and transmission electron microscopy (TEM). Numerical calculations, based on the production bias model (PBM) were carried out to study the details of evolution of cavities with and without helium generation. The phenomena of dislocation decoration and raft formation, which are important for understanding radiation hardening and plastic flow localization, have been studied using the Kinetic Monte Carlo (KMC) code during a realistic dynamic irradiation of bcc iron at 300 K. Molecular dynamics (MD) simulations have been carried out to study the stress dependencies of dislocation velocity and drag coefficient for an edge dislocation decorated with small SIA loops.The present report describes both experimental procedure and calculational methodology employed in the present work. The main results of all these investigations, both experimental and theoretical, are highlighted with appropriate examples. Finally, a brief summary is given of the main results conclusions. (au)

  13. High field electron-spin transport and observation of the Dyakonov-Perel spin relaxation of drifting electrons in low temperature-grown gallium arsenide

    International Nuclear Information System (INIS)

    Miah, M. Idrish

    2008-01-01

    High field electron-spin transport in low temperature-grown gallium arsenide is studied. We generate electron spins in the samples by optical pumping. During transport, we observe the Dyakonov-Perel (DP) [M.I. Dyakonov, V.I. Perel, Zh. Eksp. Teor. Fiz. 60 (1971) 1954] spin relaxation of the drifting electrons. The results are discussed and are compared with those obtained in calculations of the DP spin relaxation frequency of the hot electrons. A good agreement is obtained

  14. High field electron-spin transport and observation of the Dyakonov-Perel spin relaxation of drifting electrons in low temperature-grown gallium arsenide

    Energy Technology Data Exchange (ETDEWEB)

    Miah, M. Idrish [Nanoscale Science and Technology Centre, Griffith University, Nathan, Brisbane, QLD 4111 (Australia); Biomolecular and Physical Sciences, Griffith University, Nathan, Brisbane, QLD 4111 (Australia); Department of Physics, University of Chittagong, Chittagong-4331 (Bangladesh)], E-mail: m.miah@griffith.edu.au

    2008-11-17

    High field electron-spin transport in low temperature-grown gallium arsenide is studied. We generate electron spins in the samples by optical pumping. During transport, we observe the Dyakonov-Perel (DP) [M.I. Dyakonov, V.I. Perel, Zh. Eksp. Teor. Fiz. 60 (1971) 1954] spin relaxation of the drifting electrons. The results are discussed and are compared with those obtained in calculations of the DP spin relaxation frequency of the hot electrons. A good agreement is obtained.

  15. Electron dynamics of Cs covered Cu(111). A scanning tunneling spectroscopy inverstigation at low temperatures

    International Nuclear Information System (INIS)

    Hofe, T. von

    2005-01-01

    During this Ph.D. a scanning tunneling microscope operating in ultra-high vacuum and at low temperatures was assembled and modified to allow operation at variable temperatures. Also, an additional vibration isolation stage was conceived and mounted. Measurements were performed on Cu(111)-Cs for different coverages. For a coverage of Θ=0:05 ML, the layer shows a commensurate (√(19) x √(19)R23.4 ) structure which may be stabilized by surface-state mediated adatom interactions. For higher coverages, the layer is incommensurate and rotated with respect to the substrate, where the angle of rotation depends on the coverage. At the saturation coverage Θ=0:25 ML, the layer, although commensurate, reveals many defects. The binding energy of the quantum well state (QWS) confined to the Cs layer decreases with increasing coverage as has been observed before for other systems. The lifetime of the QWS decreases with increasing binding energy. The comparatively short lifetime for Cu(111)-p(2 x 2)Cs led to the introduction of Brillouin Zone Backfolding as a new lifetime-limiting process. Acquisition of dispersion relations of the QWS for different coverages revealed that the effective mass of the excitations increases with decreasing binding energy. (Orig.)

  16. METHES: A Monte Carlo collision code for the simulation of electron transport in low temperature plasmas

    Science.gov (United States)

    Rabie, M.; Franck, C. M.

    2016-06-01

    We present a freely available MATLAB code for the simulation of electron transport in arbitrary gas mixtures in the presence of uniform electric fields. For steady-state electron transport, the program provides the transport coefficients, reaction rates and the electron energy distribution function. The program uses established Monte Carlo techniques and is compatible with the electron scattering cross section files from the open-access Plasma Data Exchange Project LXCat. The code is written in object-oriented design, allowing the tracing and visualization of the spatiotemporal evolution of electron swarms and the temporal development of the mean energy and the electron number due to attachment and/or ionization processes. We benchmark our code with well-known model gases as well as the real gases argon, N2, O2, CF4, SF6 and mixtures of N2 and O2.

  17. Optoelectronic devices, low temperature preparation methods, and improved electron transport layers

    KAUST Repository

    Eita, Mohamed S.; El, Labban Abdulrahman; Usman, Anwar; Beaujuge, Pierre; Mohammed, Omar F.

    2016-01-01

    An optoelectronic device such as a photovoltaic device which has at least one layer, such as an electron transport layer, which comprises a plurality of alternating, oppositely charged layers including metal oxide layers. The metal oxide can be zinc

  18. The DNA electronic specific heat at low temperature: The role of aperiodicity

    Energy Technology Data Exchange (ETDEWEB)

    Sarmento, R.G. [Departamento de Física, Universidade Federal do Rio Grande do Norte, 59072-970, Natal, RN (Brazil); Mendes, G.A. [Departamento de Biofísica e Farmacologia, Universidade Federal do Rio Grande do Norte, 59072-970, Natal, RN (Brazil); Albuquerque, E.L., E-mail: eudenilson@gmail.com [Departamento de Biofísica e Farmacologia, Universidade Federal do Rio Grande do Norte, 59072-970, Natal, RN (Brazil); Fulco, U.L. [Departamento de Biofísica e Farmacologia, Universidade Federal do Rio Grande do Norte, 59072-970, Natal, RN (Brazil); Vasconcelos, M.S. [Escola de Ciências e Tecnologia, Universidade Federal do Rio Grande do Norte, 59072-970, Natal, RN (Brazil); Ujsághy, O. [Department of Theoretical Physics and Condensed Matter Research Group of the Hungarian Academy of Sciences, Budapest University of Technology and Economics, Budafoki út 8, H-1521 Budapest (Hungary); Freire, V.N. [Departamento de Física, Universidade Federal do Ceará, 60455-760, Fortaleza, CE (Brazil); Caetano, E.W.S. [Instituto Federal de Educação, Ciência e Tecnologia do Ceará, 60040-531, Fortaleza, CE (Brazil)

    2012-07-16

    The electronic specific heat spectra at constant volume (C{sub V}) of a long-range correlated extended ladder model, mimicking a DNA molecule, is theoretically analyzed for a stacked array of a double-stranded structure made up from the nucleotides guanine G, adenine A, cytosine C and thymine T. The role of the aperiodicity on C{sub V} is discussed, considering two different nucleotide arrangements with increasing disorder, namely the Fibonacci and the Rudin–Shapiro quasiperiodic structures. Comparisons are made for different values of the band fillings, considering also a finite segment of natural DNA, as part of the human chromosome Ch22. -- Highlights: ► Quasiperiodic sequence to mimic the DNA nucleotides arrangement. ► Electronic tight-binding Hamiltonian model. ► Electronic density of states. ► Electronic specific heat spectra.

  19. In-Situ Microprobe Observations of Dispersed Oil with Low-Temperature Low-Vacuum Scanning Electron Microscope

    International Nuclear Information System (INIS)

    Mohsen, H.T.

    2010-01-01

    A low cost cryostat stage from high heat capacity material is designed and constructed, in attempt to apply size distribution techniques for examination of oil dispersions. Different materials were tested according to their heat capacity to keep the liquid under investigation in frozen state as long as possible during the introduction of the cryostat stage to the low-vacuum scanning electron microscope. Different concentrations of non ionic surfactant were added to artificially contaminated with 10000 ppm Balayeam base oil in 3.5 % saline water, where oil and dispersing liquid have been added and shacked well to be investigated under the microscope as fine frozen droplets. The efficiency of dispersion was examined using low temperature low-vacuum scanning electron microscope. The shape and size distributions of freeze oil droplets were studied by digital imaging processing technique in conjunction with scanning electron microscope counting method. Also elemental concentration of oil droplets was analyzed.

  20. Scattering of magnetized electrons at the boundary of low temperature plasmas

    Science.gov (United States)

    Krüger, Dennis; Trieschmann, Jan; Brinkmann, Ralf Peter

    2018-02-01

    Magnetized technological plasmas with magnetic fields of 10-200 mT, plasma densities of 1017-1019 m-3, gas pressures of less than 1 Pa, and electron energies from a few to (at most) a few hundred electron volts are characterized by electron Larmor radii r L, that are small compared to all other length scales of the system, including the spatial scale L of the magnetic field and the collisional mean free path λ. In this regime, the classical drift approximation applies. In the boundary sheath of these discharges, however, that approximation breaks down: The sheath penetration depth of electrons (a few to some ten Debye length λ D; depending on the kinetic energy; typically much smaller than the sheath thickness of tens/hundreds of λ D) is even smaller than r L. For a model description of the electron dynamics, an appropriate boundary condition for the plasma/sheath interface is required. To develop such, the interaction of magnetized electrons with the boundary sheath is investigated using a 3D kinetic single electron model that sets the larger scales L and λ to infinity, i.e. neglects magnetic field gradients, the electric field in the bulk, and collisions. A detailed comparison of the interaction for a Bohm sheath (which assumes a finite Debye length) and a hard wall model (representing the limit {λ }{{D}}\\to 0; also called the specular reflection model) is conducted. Both models are found to be in remarkable agreement with respect to the sheath-induced drift. It is concluded that the assumption of specular reflection can be used as a valid boundary condition for more realistic kinetic models of magnetized technological plasmas.

  1. Electron irradiation of power transistors

    International Nuclear Information System (INIS)

    Hower, P.L.; Fiedor, R.J.

    1982-01-01

    A method for reducing storage time and gain parameters in a semiconductor transistor includes the step of subjecting the transistor to electron irradiation of a dosage determined from measurements of the parameters of a test batch of transistors. Reduction of carrier lifetime by proton bombardment and gold doping is mentioned as an alternative to electron irradiation. (author)

  2. Spectrophotometric investigation into iodine-electron donor systems at low temperature

    International Nuclear Information System (INIS)

    Gorodyskij, V.A.; Morachevskij, A.A.

    1978-01-01

    Iodine-sec. butanol (n-donor) and iodine - hexene - 1 (π-donor) have been investigated for the first time by the spectrophotometric method in the wide temeprature range (77-293 K). The existence of complexes with a charge transfer of the type, which is characterized by the long-wave absorption band in electron spectra, is determined in the systems

  3. Determination of the electron energy distribution function of a low temperature plasma from optical emission spectroscopy

    Energy Technology Data Exchange (ETDEWEB)

    Dodt, Dirk Hilar

    2009-01-05

    The experimental determination of the electron energy distribution of a low pressure glow discharge in neon from emission spectroscopic data has been demonstrated. The spectral data were obtained with a simple overview spectrometer and analyzed using a strict probabilistic, Bayesian data analysis. It is this Integrated Data Analysis (IDA) approach, which allows the significant extraction of non-thermal properties of the electron energy distribution function (EEDF). The results bear potential as a non-invasive alternative to probe measurements. This allows the investigation of spatially inhomogeneous plasmas (gradient length smaller than typical probe sheath dimensions) and plasmas with reactive constituents. The diagnostic of reactive plasmas is an important practical application, needed e.g. for the monitoring and control of process plasmas. Moreover, the experimental validation of probe theories for magnetized plasmas as a long-standing topic in plasma diagnostics could be addressed by the spectroscopic method. (orig.)

  4. Recombination of H3+ and D3+ ions with electrons in low temperature plasma

    International Nuclear Information System (INIS)

    Glosik, J; Plasil, R.; Pysanenko, A.; Poterya, V.; Kudrna, P.; Zakouril, P.

    2002-01-01

    From the decaying plasma (stationary afterglow) in the mixture of He, Ar and H 2 (or D 2 ) we determined the overall recombination rate constant (α eff ) of the recombination of H 3 + and D 3 + ions with electrons at thermal energies. We observed dependence of recombination rate coefficients on partial pressure of hydrogen (and deuterium), which indicates that observed recombination is the three-body process proceeding most probably via formation of long lived intermediate state. From the obtained data we conclude that binary dissociative recombination of H 3 + and D 3 + ions with electrons is very slow with rate coefficient α DR -9 cm 3 s -1 and α DR -9 cm 3 s -1 , respectively. (author)

  5. Determination of the electron energy distribution function of a low temperature plasma from optical emission spectroscopy

    International Nuclear Information System (INIS)

    Dodt, Dirk Hilar

    2009-01-01

    The experimental determination of the electron energy distribution of a low pressure glow discharge in neon from emission spectroscopic data has been demonstrated. The spectral data were obtained with a simple overview spectrometer and analyzed using a strict probabilistic, Bayesian data analysis. It is this Integrated Data Analysis (IDA) approach, which allows the significant extraction of non-thermal properties of the electron energy distribution function (EEDF). The results bear potential as a non-invasive alternative to probe measurements. This allows the investigation of spatially inhomogeneous plasmas (gradient length smaller than typical probe sheath dimensions) and plasmas with reactive constituents. The diagnostic of reactive plasmas is an important practical application, needed e.g. for the monitoring and control of process plasmas. Moreover, the experimental validation of probe theories for magnetized plasmas as a long-standing topic in plasma diagnostics could be addressed by the spectroscopic method. (orig.)

  6. The characteristics of carbon nanotubes grown at low temperature for electronic device application

    Energy Technology Data Exchange (ETDEWEB)

    Park, Yong Seob [Department of Photoelectronics Information, Chosun College of Science and Technology, Gwangju (Korea, Republic of); Yi, Junsin [School of Information and Communications Engineering, Sungkyunkwan University, Suwon, 440–746 (Korea, Republic of); Lee, Jaehyeong, E-mail: jaehyeong@skku.edu [School of Information and Communications Engineering, Sungkyunkwan University, Suwon, 440–746 (Korea, Republic of)

    2013-11-01

    For the application of carbon nanotubes (CNTs) in flexible electronic devices, the CNTs were grown on Corning 1737 glass substrate by microwave plasma enhanced chemical vapor deposition (MPECVD) method. To deposit the catalyst layer, TiN buffer layer of 200 nm thickness and Ni catalyst layer of 60 nm were first deposited on the glass by r.f. magnetron sputtering method. The CH{sub 4} and H{sub 2} gases are used as the synthesis gas of CNTs and the working pressure was about 2.13 kPa, and the substrate bias was about − 200 V. The growth time was from 2 min to 5 min and the microwave power was about 800 W. The substrate temperature as the main parameter was changed from 400 °C to 550 °C. The structural properties of CNTs synthesized with the substrate temperature were investigated using Raman, field emission scanning electron microscopy, and transmission electron microscopy methods. The surface and electrical properties of CNTs grown by MPECVD method were studied by scanning probe microscopy and four-point probe methods. We obtained the multi-walled CNTs (MW-CNTs). Multi-walled CNTs were vertically grown on Ni/TiN/glass substrates below 500 °C without any glass deformations. As the substrate temperature was increased, the crystallinity of CNTs was improved. Ni catalyst was found at the tip of CNT by the TEM observation and the grown CNTs were found to have a multi-walled with bamboo like structure. - Highlights: • Synthesis of vertically aligned carbon nanotubes. • Effects of substrate temperature on carbon nanotubes properties. • Improvement of the crystallinity with increasing substrate temperature. • Reduction of sheet resistance with increasing substrate temperature.

  7. Binary recombination of para- and ortho-H3+ with electrons at low temperatures.

    Science.gov (United States)

    Dohnal, P; Hejduk, M; Varju, J; Rubovic, P; Roucka, S; Kotrík, T; Plasil, R; Johnsen, R; Glosík, J

    2012-11-13

    Results of an experimental study of binary recombination of para- and ortho-H(3)(+) ions with electrons are presented. Near-infrared cavity-ring-down absorption spectroscopy was used to probe the lowest rotational states of H(3)(+) ions in the temperature range of 77-200 K in an H(3)(+)-dominated afterglow plasma. By changing the para/ortho abundance ratio, we were able to obtain the binary recombination rate coefficients for pure and para-H(3)(+) and ortho-H(3)(+). The results are in good agreement with previous theoretical predictions.

  8. Low temperature sintering of Ag nanoparticles/graphene composites for paper based writing electronics

    International Nuclear Information System (INIS)

    Wang, Fuliang; He, Hu; Zhu, Haixin

    2016-01-01

    With the great demand in the applications of flexible electronics, the methods leading to improvements in the electrical and mechanical performance have been widely investigated. In this work, we firstly prepared a hybrid composite ink using Ag nanoparticles and graphene. Then, a hot-press sintering process was deployed to obtain the desired electrical tracks which could be applied in flexible electronics. We have systematically investigated the effects of sintering time, pressure and temperature, as well as the different percentage of weight (wt%) of graphene for the electrical and mechanical performance of sintered electrical tracks. We achieved reasonably low electrical resistivity at low sintering temperature (120 °C). Specifically, the resistivity reaches 6.19  ×  10 −8 Ω · m which is just 3.87 times higher than the value of bulk silver. Additionally, the prepared hybrid composite ink obtained better electrical reliability against bending test comparing with Ag nanoparticle ink. Finally, the optimal wt% of graphene and potential effect to the electrical and mechanical performance were also investigated. (paper)

  9. Reduction of radiation-induced vitamin losses by irradiation of food-stuffs at low temperatures and by exclusion of atmospheric oxygen

    International Nuclear Information System (INIS)

    Diehl, J.F.

    1979-01-01

    The protective effect of low temperatures during irradiation on vitamin B 1 and E levels in foods is not abolished by subsequent storage or heating. Egg powder irradiated at 1 Mrad in the presence of air and stored for 4 months at ambient temperature lost 68% of its thiamin content when irradiated at 20 0 C, 33% when irradiated at -30 0 C. Sunflower oil irradiated at 3 Mrad in the presence of air and subsequently heated for 1 hour at 180 0 C lost 98% of its α-tocopherol content when irradiated at 20 0 C, 65% when irradiated at -30 0 C. Exclusion of atmospheric oxygen by packaging under nitrogen reduced the loss of α-tocopherol in irradiated (0.1 Mrad) rolled oats after 8 months of storage from 56 to 5% and the loss of thiamin from 86 to 26%. Vacuum packaging was equally effective during the first 3 months and somewhat less effective during the following 5 months. Packaging under carbon dioxide showed no advantage over packaging in air. Sensory evaluation of rolled oats, raw or cooked, 1 and 3 months after irradiation with 0.1 Mrad indicated no significant quality difference between unirradiated and irradiated samples packaged under nitrogen. (orig.) [de

  10. High sensitivity ethanol gas sensor based on Sn - doped ZnO under visible light irradiation at low temperature

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Peishuo; Pan, Guofeng; Zhang, Bingqiang; Zhen, Jiali; Sun, Yicai, E-mail: pgf@hebut.edu.cn [Institute of Microelectronic, Hebei University of Technology, Tianjin (China)

    2014-07-15

    Pure ZnO and 5at%, 7at%, 9at% Sn - doped ZnO materials are prepared by the chemical co - precipitation method. They were annealed by furnace at temperature range of 300 - 700ºC in air for 1h. The ZnO materials are characterized by X - ray diffraction (XRD) and scanning electron microscopy (SEM). The results show that the Sn - doped ZnO materials appear rough porous structures. The maximum sensitivity can be achieved by doping the amount of 7 at%. It has much better sensing performance towards ethanol vapor under visible light irradiation. The response and recovery time are ~1s and ~5s, respectively. The mechanism for the improvement in the sensing properties can be explained with the surface adsorption theory and the photoactivation theory. (author)

  11. Low temperature electron microscopy on the cubic-tetragonal transformation of V3Si

    Science.gov (United States)

    Onozuka, T.; Ohnishi, N.; Hirabayashi, M.

    1988-04-01

    The cubic-tetragonal martensitic transition of V3Si and its precursor have been investigated in the temperature range from 13 K to 80 K using a 1 MV electron microscope with a double-tilting cold stage. Below the transition temperature Tm = 19 K, fine twin lamellae appear parallel to {110} plane traces, being connected continuously with mottled striations having the same orientation. Fine striations along {110} traces or so-called tweeds are observed below 50 K at the precursor of the structural phase transition. The image contrast of mottled striations and tweed patterns is attributed to the presence of lattice distortion owing to the softening of the shear modulus. Reversible changes of the patterns recorded with a TV-VTR system during cooling and heating processes were discussed briefly.

  12. Low temperature x-ray analysis and electron microscopy of a new family of superconducting materials

    International Nuclear Information System (INIS)

    Ossipyan, Yu.A.; Borodin, V.A.; Goncharov, V.A.; Kondakov, S.F.; Khasanov, S.S.; Chernyshova, L.M.; Shekhtman, V.S.; Shmyt'ko, I.M.; Stchegolev, N.F.

    1987-01-01

    Recent findings in the field of high temperature superconductivity require that structural aspects of the behavior of this class of materials be investigated in detail in a wide temperature interval. A series of superconducting ceramics on the base of lanthanum and yttrium oxides (La/sub 2-x/Sr/sub x/CuO 4 ; x = 0, 2 and YBaCuO) have been obtained in the solid state Physics Institute of the Academy of Sciences of the USSR. This paper presents the results of the analysis of powder and sintered materials, using X-ray diffractometers (DRON), scanning electron microscope and special devices, enabling the investigations to be carried out within 4.2 K - 573 K

  13. Singlet oxygen in the low-temperature plasma of an electron-beam-sustained discharge

    International Nuclear Information System (INIS)

    Vagin, N. P.; Ionin, A. A.; Klimachev, Yu. M.; Kotkov, A. A.; Kochetov, I. V.; Napartovich, A. P.; Podmar'kov, Yu. P.; Rulev, O. A.; Seleznev, L. V.; Sinitsyn, D. V.; Frolov, M. P.; Yuryshev, N. N.

    2006-01-01

    Results are presented from experimental and theoretical studies of the production of singlet delta oxygen in a pulsed electron-beam-sustained discharge ignited in a large (∼18-1) volume at a total gas mixture pressure of up to 210 Torr. The measured yield of singlet oxygen reaches 10.5%. It is found that varying the reduced electric field from ∼2 to ∼11 kV/(cm atm) slightly affects singlet oxygen production. It is shown experimentally that an increase in the gas mixture pressure or the specific input energy reduces the duration of singlet oxygen luminescence. The calculated time evolution of the singlet oxygen concentration is compared with experimental results

  14. Optoelectronic devices, low temperature preparation methods, and improved electron transport layers

    KAUST Repository

    Eita, Mohamed S.

    2016-08-04

    An optoelectronic device such as a photovoltaic device which has at least one layer, such as an electron transport layer, which comprises a plurality of alternating, oppositely charged layers including metal oxide layers. The metal oxide can be zinc oxide. The plurality of layers can be prepared by layer-by-layer processing in which alternating layers are built up step-by-step due to electrostatic attraction. The efficiency of the device can be increased by this processing method compared to a comparable method like sputtering. The number of layers can be controlled to improve device efficiency. Aqueous solutions can be used which is environmentally friendly. Annealing can be avoided. A quantum dot layer can be used next to the metal oxide layer to form a quantum dot heterojunction solar device.

  15. Novel low-temperature processing of low noise SDDs with on-detector electronics

    International Nuclear Information System (INIS)

    Sonsky, J.; Koornneef, R.; Huizenga, J.; Hollander, R.W.; Nanver, L.K.; Scholtes, T.; Roozeboom, F.; Eijk, C.W.E. van

    2004-01-01

    We have developed a fabrication process (SMART700 deg. process) for monolithic integration of p-channel JFETs and silicon detectors. Processing steps of the SMART700 deg. do not exceed 700 deg. C. The integrated p-JFET has a minimum gate length of 1 μm. A relatively large width can be chosen to achieve a reasonable transconductance, while the JFET capacitance still matches the small capacitance of a detector. The feedback capacitor was also realized on-chip as a double-metal capacitor. In this paper we describe DC and noise characteristics of a silicon drift detector (SDD) with a p-JFET (W/L=100/1) and a feedback capacitor integrated in the read-out anode (smart-SDD). The device has a transconductance of 1-3 mS, a top gate capacitance of ∼140 fF and a low leakage current ( 2 at room temperature). The smart-SDD with an active area of 3.8 mm 2 has reached an energy resolution of ∼50 rms electrons at a temperature of 213 K. This relatively poor energy resolution is due to generation-recombination noise caused by defects produced by a deep n-implantation. Rapid thermal annealing (RTA) and excimer laser annealing (ELA) techniques are experimented to remove the implantation damage. The noise of p-JFETs annealed with RTA and ELA is also presented

  16. Low temperature atmospheric microplasma jet array for uniform treatment of polymer surface for flexible electronics

    Science.gov (United States)

    Wang, Tao; Wang, Xiaolin; Yang, Bin; Chen, Xiang; Yang, Chunsheng; Liu, Jingquan

    2017-07-01

    In this paper, the uniformity of polymer film etching by an atmospheric pressure He/O2 microplasma jet array (μPJA) is first investigated with different applied voltage. Plasma characteristics of μPJA were recorded by optical discharge images. Morphologies and chemical compositions of polymer film etched by μPJA were analyzed by optical microscopy, scanning electron microscopy (SEM), energy dispersive x-ray spectroscopy (EDS) and x-ray photoelectron spectroscopy (XPS). By increasing the applied voltage from 8.5 kV to 16.4 kV, the non-uniformity of the luminous intensity of the plasma jets increases. It is interesting that the plasma treated regions are actually composed of an etched region and modification region, with distinct morphologies and chemical compositions. The diameters of the etched parylene-C film show the increase of non-uniformity with higher applied voltage. SEM results show that the non-uniformity of surface morphologies of both the modification regions and etched regions increases with the increase of applied voltage. EDS and XPS results also present the significant effect of higher applied voltage on the non-uniformity of surface chemical compositions of both modification and etched regions. The Coulomb interaction of the streamer heads and the hydrodynamic interaction between the plasma jets and the surrounding air are considered to be responsible for this phenomenon. The results shown in this work can help improve the processing quality of polymer film etched by an atmospheric pressure microplasma jet array and two applications are demonstrated to illustrate the uniform downstream surface treatment.

  17. Effects of carbon ion irradiation on survival rate, catalase and peroxidase activity of alfalfa M1 under low temperature stress

    International Nuclear Information System (INIS)

    Wang Shuyang; Li Jinghua; Jiang Boling

    2014-01-01

    In this study, three kinds of alfalfa including Zhonglan 1, BC-04-477 and Ta Cheng were treated with different doses of "1"2C"6"+ (75 keV) heavy ion radiation, and then the influence of survival rate, catalase (CAT) and peroxidase (POD) activity of M1 with low temperature stress were tested. The results showed that under the condition of 400 Gy radiation dose, the survival rate and CAT activity of Zhonglan 1 under low temperature stress have increased by 33.3%, 56.3% respectively compared with those of the control group, while there was no difference in POD activity between those two groups. The survival rate, CAT and POD activity of BC-04-477 treated with low temperature have been improved by 33.3%, 69.2%, 5.1% respectively compared with those of the control group when the radiation dose was 400 Gy. Compared with those of the control group, the survival rate, CAT and POD activity of Ta Cheng under low temperature stress have been improved by 25%, 26%,22.8% respectively when the radiation dose was 800 Gy. These results indicate that the viability and the cold resistance ability of Zhong Lan 1, BC-04-477 and Ta Cheng can be improved by "1"2C"6"+ radiation. (authors)

  18. Influence of gamma irradiation and low temperature storage on the quality and shelf life of squid (Doryteuthis sibogae

    Directory of Open Access Journals (Sweden)

    Manjanaik, B.

    2017-08-01

    Full Text Available Irradiation is considered as an efficient method for the reduction of microorganisms in food. It has been used to improve the safety and shelf life of food products. The present investigation is aimed at studying the influence of gamma irradiation (3 and 5 kGy and subsequent storage at refrigeration temperature (4oC on the chemical, microbial qualities and extended shelf life of squid (Doryteuthis sibogae. The total volatile base nitrogen (TVB-N and trimethyl amine nitrogen values (TMA-N of the irradiated squid samples significantly decreased in comparison with the control (non-irradiated stored at 4oC. The thiobarbituric acid values for the irradiated squid was significantly lower than of the non-irradiated samples stored at 4oC (p<0.05. The pH value of the squid was affected significantly by both, irradiation dose and storage temperature (p<0.05. The total microbial load for the non-irradiated squid samples was higher than those of irradiated samples at 4oC temperature. The results revealed that the combination of irradiation and refrigerated storage resulted in a significant reduction of microbial growth and stabilized the biochemical characteristics of squid.

  19. A Low-Temperature Electron Microscopy and Electron Diffraction Study of La1.84Sr0.16CuO4

    Science.gov (United States)

    Onozuka, Takashi; Omori, Mamoru; Hirabayashi, Makoto; Syono, Yasuhiko

    1987-10-01

    A high-Tc superconducting compound, La1.84Sr0.16CuO4, has been investigated by electron microscopy and electron diffraction in the range from 10 K to ambient temperature. The tetragonal K2NiF4-type structure undergoes an orthorhombic distortion below about 130 K. In the low-temperature phase, extra diffraction spots and twin lamellae are observed reversibly on cooling and heating in situ. Based on the observed results, a plausible structure model with orthorhombic distortion is proposed.

  20. A low-temperature electron microscopy and electron diffraction study of La1.84Sr0.16CuO4

    International Nuclear Information System (INIS)

    Onozuka, Takashi; Omori, Mamoru; Hirabayashi, Makoto; Syono, Yasuhiko

    1987-01-01

    A high-T c superconducting compound, La 1.84 Sr 0.16 CuO 4 , has been investigated by electron microscopy and electron diffraction in the range from 10 K to ambient temperature. The tetragonal K 2 NiF 4 -type structure undergoes an orthorhombic distortion below about 130 K. In the low-temperature phase, extra diffraction spots and twin lamellae are observed reversibly on cooling and heating in situ. Based on the observed results, a plausible structure model with orthorhombic distortion is proposed. (author)

  1. Low-temperature electron microscopy and electron diffraction study of La/sub 1. 84/Sr/sub 0. 16/CuO/sub 4/

    Energy Technology Data Exchange (ETDEWEB)

    Onozuka, Takashi; Omori, Mamoru; Hirabayashi, Makoto; Syono, Yasuhiko

    1987-10-01

    A high-T/sub c/ superconducting compound, La/sub 1.84/Sr/sub 0.16/CuO/sub 4/, has been investigated by electron microscopy and electron diffraction in the range from 10 K to ambient temperature. The tetragonal K/sub 2/NiF/sub 4/-type structure undergoes an orthorhombic distortion below about 130 K. In the low-temperature phase, extra diffraction spots and twin lamellae are observed reversibly on cooling and heating in situ. Based on the observed results, a plausible structure model with orthorhombic distortion is proposed

  2. Effects of low-temperature fusion neutron irradiation on critical properties of a monofilament niobium-tin superconductor

    International Nuclear Information System (INIS)

    Guinan, M.W.; Van Konynenburg, R.A.; Mitchell, J.B.

    1984-01-01

    The objective of this work was to irradiate a Nb 3 Sn superconductor with 14.8 MeV neutrons at 4 K and measure critical current in transverse fields of up to 12 T, irradiating up to a fluence sufficient to decrease the critical current to below its initial value. Critical temperatures were also to be measured. The samples were to be kept near 4 K between the irradiation and the measurement of critical properties. This work is directed toward establishing an engineering design fluence limit for Nb 3 Sn when used in fusion reactor superconducting magnets

  3. Effects of low-temperature fusion neutron irradiation on critical properties of a monofilament niobium-tin superconductor

    Energy Technology Data Exchange (ETDEWEB)

    Guinan, M.W.; Van Konynenburg, R.A.; Mitchell, J.B.

    1984-03-22

    The objective of this work was to irradiate a Nb/sub 3/Sn superconductor with 14.8 MeV neutrons at 4 K and measure critical current in transverse fields of up to 12 T, irradiating up to a fluence sufficient to decrease the critical current to below its initial value. Critical temperatures were also to be measured. The samples were to be kept near 4 K between the irradiation and the measurement of critical properties. This work is directed toward establishing an engineering design fluence limit for Nb/sub 3/Sn when used in fusion reactor superconducting magnets.

  4. The influence of neutron-irradiation at low temperatures on the dielectric parameters of 3C-SiC

    Energy Technology Data Exchange (ETDEWEB)

    Engelbrecht, J.A.A., E-mail: Japie.Engelbrecht@nmmu.ac.za [Physics Department, Nelson Mandela Metropolitan University, P.O. Box 77000, Port Elizabeth 6031 (South Africa); Deyzel, G.; Minnaar, E.G.; Goosen, W.E. [Physics Department, Nelson Mandela Metropolitan University, P.O. Box 77000, Port Elizabeth 6031 (South Africa); Rooyen, I.J. van [Fuel Performance and Design Department, Idaho National Laboratory, P.O. Box 1625, Idaho Falls, ID 83415-6188 (United States)

    2014-04-15

    3C-SiC wafers were irradiated with neutrons of various fluences and at low (200–400 °C) irradiation temperatures. Fourier transform infrared (FTIR) reflectance spectra were obtained for the samples, and the spectra used to extract the dielectric parameters for each specimen, using statistical curve-fitting procedures. Analysis of all data revealed trends in reflectance peak heights as well as in the dielectric parameters. The surface roughness of the irradiated samples was measured by atomic force spectroscopy (AFM) and certain trends could be ascribed to surface roughness.

  5. The influence of neutron-irradiation at low temperatures on the dielectric parameters of 3C-SiC

    International Nuclear Information System (INIS)

    Engelbrecht, J.A.A.; Deyzel, G.; Minnaar, E.G.; Goosen, W.E.; Rooyen, I.J. van

    2014-01-01

    3C-SiC wafers were irradiated with neutrons of various fluences and at low (200–400 °C) irradiation temperatures. Fourier transform infrared (FTIR) reflectance spectra were obtained for the samples, and the spectra used to extract the dielectric parameters for each specimen, using statistical curve-fitting procedures. Analysis of all data revealed trends in reflectance peak heights as well as in the dielectric parameters. The surface roughness of the irradiated samples was measured by atomic force spectroscopy (AFM) and certain trends could be ascribed to surface roughness.

  6. Radiation defects in electron-irradiated InP crystals

    International Nuclear Information System (INIS)

    Brailovskii, E.Yu.; Karapetyan, F.K.; Megela, I.G.; Tartachnik, V.P.

    1982-01-01

    The results are presented of formation and annealing of defects in InP crystals at 1 to 50 MeV electron irradiation. The recovery of electrical properties in the range of 77 to 970 K during annealing processes is studied. Five low temperature annealing states in n-InP and the reverse annealing in p-InP are observed at 77 to 300 K. Four annealing stages at temperatures higher than 300 K are present. When the electron energy is increased more complicated thermostable defects are formed, and at 50 MeV electron energy besides of the point defect clusters are formed, which anneal at temperatures of 800 to 970 K. It is shown that the peculiarities of the Hall mobility at irradiation and annealing are caused by the scattering centres E/sub c/ - 0.2 eV. The 'limiting' position of the Fermi level in electron irradiated InP crystals is discussed. (author)

  7. Amorphous Tin Oxide as a Low-Temperature-Processed Electron-Transport Layer for Organic and Hybrid Perovskite Solar Cells

    KAUST Repository

    Barbe, Jeremy

    2017-02-08

    Chemical bath deposition (CBD) of tin oxide (SnO) thin films as an electron-transport layer (ETL) in a planar-heterojunction n-i-p organohalide lead perovskite and organic bulk-heterojunction (BHJ) solar cells is reported. The amorphous SnO (a-SnO) films are grown from a nontoxic aqueous bath of tin chloride at a very low temperature (55 °C) and do not require postannealing treatment to work very effectively as an ETL in a planar-heterojunction n-i-p organohalide lead perovskite or organic BHJ solar cells, in lieu of the commonly used ETL materials titanium oxide (TiO) and zinc oxide (ZnO), respectively. Ultraviolet photoelectron spectroscopy measurements on the glass/indium-tin oxide (ITO)/SnO/methylammonium lead iodide (MAPbI)/2,2′,7,7′-tetrakis(N,N-di-p-methoxyphenylamine)-9,9′-spirobifluorene device stack indicate that extraction of photogenerated electrons is facilitated by a perfect alignment of the conduction bands at the SnO/MAPbI interface, while the deep valence band of SnO ensures strong hole-blocking properties. Despite exhibiting very low electron mobility, the excellent interfacial energetics combined with high transparency (E > 4 eV) and uniform substrate coverage make the a-SnO ETL prepared by CBD an excellent candidate for the potentially low-cost and large-scale fabrication of organohalide lead perovskite and organic photovoltaics.

  8. Progress on Low-Temperature Pulsed Electron Deposition of CuInGaSe2 Solar Cells

    Directory of Open Access Journals (Sweden)

    Massimo Mazzer

    2016-03-01

    Full Text Available The quest for single-stage deposition of CuInGaSe2 (CIGS is an open race to replace very effective but capital intensive thin film solar cell manufacturing processes like multiple-stage coevaporation or sputtering combined with high pressure selenisation treatments. In this paper the most recent achievements of Low Temperature Pulsed Electron Deposition (LTPED, a novel single stage deposition process by which CIGS can be deposited at 250 °C, are presented and discussed. We show that selenium loss during the film deposition is not a problem with LTPED as good crystalline films are formed very close to the melting temperature of selenium. The mechanism of formation of good ohmic contacts between CIGS and Mo in the absence of any MoSe2 transition layers is also illustrated, followed by a brief summary of the measured characteristics of test solar cells grown by LTPED. The 17% efficiency target achieved by lab-scale CIGS devices without bandgap modulation, antireflection coating or K-doping is considered to be a crucial milestone along the path to the industrial scale-up of LTPED. The paper ends with a brief review of the open scientific and technological issues related to the scale-up and the possible future applications of the new technology.

  9. Binary and ternary recombination of [image omitted] and [image omitted] ions with electrons in low temperature plasma

    Science.gov (United States)

    Glosík, J.; Plašil, R.; Kotrík, T.; Dohnal, P.; Varju, J.; Hejduk, M.; Korolov, I.; Roučka, Š.; Kokoouline, V.

    2010-09-01

    Measurements of recombination rate coefficients of binary and ternary recombination of ? and ? ions with electrons in a low temperature plasma are described. The experiments were carried out in the afterglow plasma in helium with a small admixture of Ar and parent gas (H2 or D2). For both ions a linear increase of measured apparent binary recombination rate coefficients (αeff) with increasing helium density was observed: αeff = αBIN + K He[He]. From the measured dependencies, we have obtained for both ions the binary (αBIN) and the ternary (K He) rate coefficients and their temperature dependence. For the description of observed ternary recombination a mechanism with two subsequent rate determining steps is proposed. In the first step, in ? + e- (or ? + e-) collision, a rotationally excited long-lived Rydberg molecule ? (or ? ) is formed. In the following step ? (or ? ) collides with a He atom of the buffer gas and this collision prevents autoionization of ? (or ? ). Lifetimes of the formed ? (or ? ) and corresponding ternary recombination rate coefficients have been calculated. The theoretical and measured binary and ternary recombination rate coefficients obtained for ? and ? ions are in good agreement.

  10. Inverted Organic Solar Cells with Low-Temperature Al-Doped-ZnO Electron Transport Layer Processed from Aqueous Solution

    Directory of Open Access Journals (Sweden)

    Qianni Zhang

    2018-01-01

    Full Text Available The aqueous-based Zn-ammine complex solutions represent one of the most promising routes to obtain the ZnO electron transport layer (ETL at a low temperature in inverted organic solar cells (OSCs. However, to dope the ZnO film processed from the Zn-ammine complex solutions is difficult since the introduction of metal ions into the Zn-ammine complex is a nontrivial process as ammonium hydroxide tends to precipitate metal salts due to acid-base neutralization reactions. In this paper, we investigate the inverted OSCs with Al-doped-ZnO ETL made by immersion of metallic Al into the Zn-ammine precursor solution. The effects of ZnO layer with different immersion time of Al on film properties and solar cell performance have been studied. The results show that, with the Al-doped-ZnO ETL, an improvement of the device performance could be obtained compared with the device with the un-doped ZnO ETL. The improved device performance is attributed to the enhancement of charge carrier mobility leading to a decreased charge carrier recombination and improved charge collection efficiency. The fabricated thin film transistors with the same ZnO or AZO films confirm the improved electrical characteristics of the Al doped ZnO film.

  11. Microstructure of V-4Cr-4Ti alloy after low-temperature irradiation by ions and neutrons

    International Nuclear Information System (INIS)

    Gazda, J.; Meshii, M.; Chung, H.M.

    1998-01-01

    Mechanical properties of V-4Cr-4Ti alloy were investigated after low-temperature ( ++ ) and dual ion beams (350-keV He + simultaneously with 4.5-MeV Ni ++ ). TEM observations showed the formation of a high density of point-defect clusters and dislocation loops (<30 nm diameter) distributed uniformly in the specimens. Mechanical-property testing showed embrittlement of the alloy. TEM investigations of deformed microstructures were used to determine the causes of embrittlement and yielded observation of dislocation channels propagating through the undeformed matrix. Channels are the sole slip paths and cause early onset of necking and loss of work-hardening in this alloy. Based on a review of the available literature, suggestions are made for further research of slip localization in V-base alloys

  12. Low-temperature electron properties of Heusler alloys Fe2VAl and Fe2CrAl: Effect of annealing

    International Nuclear Information System (INIS)

    Podgornykh, S. M.; Svyazhin, A. D.; Shreder, E. I.; Marchenkov, V. V.; Dyakina, V. P.

    2007-01-01

    We present the results of measurements of low-temperature heat capacity, as well as electrical and magnetic properties of Heusler alloys Fe 2 VAl and Fe 2 CrAl prepared in different ways using various heat treatment regimes. The density of states at the Fermi level is estimated. A contribution of ferromagnetic clusters in the low-temperature heat capacity of the Fe 2 VAl alloy is detected. The change in the number and volume of clusters as a result of annealing of an alloy affects the behavior of their low-temperature heat capacity, resistivity, and magnetic properties

  13. Final report on neutron irradiation at low temperature to investigate plastic instability and at high temperature to study caviation

    DEFF Research Database (Denmark)

    Singh, B.N; Eldrup, Morten Mostgaard; Golubov, D.J.

    2005-01-01

    Effects of neutron irradiation on defect accumulation and physical and mechanical properties of pure iron and F82H and EUROFER 97 ferritic-martensitic steels have been investigated. Tensile specimens were neutron irradiated to a dose level of 0,23 dpa at333 and 573 K. Electrical resistivity......, based on the production bias model (PBM) were carried out to study the details of evolution of cavitieswith and without helium generation. The phenomena of dislocation decoration and raft formation, which are important for understanding radiation hardening and plastic flow localization, have been...... studied using the Kinetic Monte Carlo (KMC) code during arealistic dynamic irradiation of bcc iron at 300 K. Molecular dynamics (MD) simulations have been carried out to study the stress dependencies of dislocation velocity and drag coefficient for an edge dislocation decorated with small SIA loops...

  14. Investigation of the internal electric field distribution under in situ x-ray irradiation and under low temperature conditions by the means of the Pockels effect

    International Nuclear Information System (INIS)

    Prekas, G; Sellin, P J; Veeramani, P; Davies, A W; Lohstroh, A; Oezsan, M E; Veale, M C

    2010-01-01

    The internal electric field distribution in cadmium zinc telluride (CdZnTe) x-ray and γ-ray detectors strongly affects their performance in terms of charge transport and charge collection properties. In CdZnTe detectors the electric field distribution is sensitively dependent on not only the nature of the metal contacts but also on the working conditions of the devices such as the temperature and the rate of external irradiation. Here we present direct measurements of the electric field profiles in CdZnTe detectors obtained using the Pockels electo-optic effect whilst under in situ x-ray irradiation. These data are also compared with alpha particle induced current pulses obtained by the transient current technique, and we discuss the influence of both low temperature and x-ray irradiation on the electric field evolution. Results from these studies reveal strong distortion of the electric field consistent with the build-up of space charge at temperatures below 250 K, even in the absence of external irradiation. Also, in the presence of x-ray irradiation levels a significant distortion in the electric field is observed even at room temperature which matches well the predicted theoretical model.

  15. The investigation of the magnetic after-effect in iron-alpha after neutron irradiation at low temperature

    International Nuclear Information System (INIS)

    Mensch, W.

    1986-01-01

    The present thesis investigates the magnetic after-effect for neutron irradiated, polycrystalline iron-alpha for the temperature range 10 to 400 K by means of susceptibility measurements. 24 maxima of magnetic after-effect are found, which are related to different classes of defects. (BHO)

  16. Organic materials irradiated at very low temperature and at different stopping powers: examples of polyethylene and of cyclohexane molecules trapped in matrix; Materiaux organiques irradies a tres basse temperature et a differents pouvoirs d'arret: cas du polyethylene et des molecules de cyclohexane isolees en matrice

    Energy Technology Data Exchange (ETDEWEB)

    Melot, M

    2003-10-15

    This thesis concerns the formation mechanisms of defects created in organic materials during irradiation under vacuum, at very low temperature and at different electronic stopping powers. Analysis have been realised by infrared spectroscopy. The first part concerns polyethylene. Irradiating at 8 K allows to dissociate the direct irradiation effects (in cage reactions) and the radical recombination effects. According to the considered chemical groups, the radical mobility leads to very different changes for the formation radiochemical yields. The second part concerns the irradiation of cyclohexane molecules trapped in a solid argon matrix. We evaluate the contribution of intermolecular and intramolecular reactions. The intermolecular reactions have limited consequences when using low ionising radiations but are crucial for heavy ion irradiations. (author)

  17. The effect of low temperature neutron irradiation and annealing on the thermal conductivity of advanced carbon-based materials

    International Nuclear Information System (INIS)

    Barabash, V.; Mazul, I.; Latypov, R.; Pokrovsky, A.; Wu, C.H.

    2002-01-01

    Several carbon-based materials (carbon fibre composites NB 31, NS 31 and UAM-92, doped graphite RGTi-91), were irradiated at about 90 deg. C in the damage dose range 0.0021-0.13 dpa. Significant reduction of the thermal conductivity of all materials was observed (e.g. at damage dose of ∼0.13 dpa the thermal conductivity degraded up to level of ∼2-3% of the initial values). However, saturation of this effect was observed starting at a dose of ∼0.06 dpa. The effect of annealing at 250 and 350 deg. C on the recovery of thermal conductivity of NB 31 and NS 31 was studied and it was shown this annealing can significantly improve thermal conductivity (∼2.5-3 times). The data on the degradation of the thermal conductivity after additional irradiation after annealing is also reported

  18. A study by internal friction of defects produced in iron and nickel irradiated at very low temperatures; Etude au moyen du frottement interne des defauts crees par irradiation a tres basse temperature dans le fer et le nickel

    Energy Technology Data Exchange (ETDEWEB)

    Keating-Hart, G de [Commissariat a l' Energie Atomique, Grenoble (France). Centre d' Etudes Nucleaires

    1969-07-01

    This work represents a contribution to the study of point defects in metals. After a brief review of the theory of internal friction we will discuss some technical innovations aimed at increasing the flexibility of the apparatus at our disposal. These innovations have allowed us to extend our range of measurements down to 20 deg. K. We will then discuss our experimental results. Firstly, we describe preliminary experiments on electron irradiated iron and the evidence for a laminar structure. Secondly, we present and account of the first measurements on nickel after neutron irradiation at 27 deg. K. We will compare the results with those obtained by other methods in this laboratory. Essentially we have observed transitory peaks at low temperature due to close Frenkel pairs and we have noticed the absence of a peak which would correspond to the magnetic after effect band of stage I{sub E}. An attempt is made to explain the disappearance of the observed peaks upon the application of an internal saturating magnetic field. (author) [French] Ce memoire constitue une contribution a l'etude des defauts ponctuels dans les metaux. Apres un bref apercu theorique sur le frottement interne, nous presenterons quelques realisations techniques destinees a accroitre les possibilites des instruments qui nous ont ete confies. Ces dernieres nous ont permis d'etendre la gamme des mesures jusqu'a 20 deg. K. Nous parlerons ensuite de nos resultats experimentaux. En premier lieu, ceux obtenus au cours de premieres experiences, sur le fer irradie aux electrons mettent en evidence des structures de laminage. En second lieu, nous exposerons les premieres mesures realisees sur du nickel irradie aux neutrons; nous comparerons ces resultats avec ceux obtenus par d'autres moyens experimentaux dans le laboratoire. Nous avons observe essentiellement des pics fugitifs a basse temperature dus aux paires proches de Frenckel et nous avons constate l'absence d'un pic correspondant a la bande de tramage

  19. Next generation non-vacuum, maskless, low temperature nanoparticle ink laser digital direct metal patterning for a large area flexible electronics.

    Directory of Open Access Journals (Sweden)

    Junyeob Yeo

    Full Text Available Flexible electronics opened a new class of future electronics. The foldable, light and durable nature of flexible electronics allows vast flexibility in applications such as display, energy devices and mobile electronics. Even though conventional electronics fabrication methods are well developed for rigid substrates, direct application or slight modification of conventional processes for flexible electronics fabrication cannot work. The future flexible electronics fabrication requires totally new low-temperature process development optimized for flexible substrate and it should be based on new material too. Here we present a simple approach to developing a flexible electronics fabrication without using conventional vacuum deposition and photolithography. We found that direct metal patterning based on laser-induced local melting of metal nanoparticle ink is a promising low-temperature alternative to vacuum deposition- and photolithography-based conventional metal patterning processes. The "digital" nature of the proposed direct metal patterning process removes the need for expensive photomask and allows easy design modification and short turnaround time. This new process can be extremely useful for current small-volume, large-variety manufacturing paradigms. Besides, simple, scalable, fast and low-temperature processes can lead to cost-effective fabrication methods on a large-area polymer substrate. The developed process was successfully applied to demonstrate high-quality Ag patterning (2.1 µΩ·cm and high-performance flexible organic field effect transistor arrays.

  20. Next generation non-vacuum, maskless, low temperature nanoparticle ink laser digital direct metal patterning for a large area flexible electronics.

    Science.gov (United States)

    Yeo, Junyeob; Hong, Sukjoon; Lee, Daehoo; Hotz, Nico; Lee, Ming-Tsang; Grigoropoulos, Costas P; Ko, Seung Hwan

    2012-01-01

    Flexible electronics opened a new class of future electronics. The foldable, light and durable nature of flexible electronics allows vast flexibility in applications such as display, energy devices and mobile electronics. Even though conventional electronics fabrication methods are well developed for rigid substrates, direct application or slight modification of conventional processes for flexible electronics fabrication cannot work. The future flexible electronics fabrication requires totally new low-temperature process development optimized for flexible substrate and it should be based on new material too. Here we present a simple approach to developing a flexible electronics fabrication without using conventional vacuum deposition and photolithography. We found that direct metal patterning based on laser-induced local melting of metal nanoparticle ink is a promising low-temperature alternative to vacuum deposition- and photolithography-based conventional metal patterning processes. The "digital" nature of the proposed direct metal patterning process removes the need for expensive photomask and allows easy design modification and short turnaround time. This new process can be extremely useful for current small-volume, large-variety manufacturing paradigms. Besides, simple, scalable, fast and low-temperature processes can lead to cost-effective fabrication methods on a large-area polymer substrate. The developed process was successfully applied to demonstrate high-quality Ag patterning (2.1 µΩ·cm) and high-performance flexible organic field effect transistor arrays.

  1. Apparatus for irradiation with electron beam

    International Nuclear Information System (INIS)

    Uehara, K.; Ito, A.; Nishimune, K.; Fujita, K.

    1976-01-01

    An irradiation apparatus with high energy electrons is disclosed in which a wire shaped or linear object to be irradiated is moved back and forth many times under an electron window so as to irradiate it with an electron beam. According to one feature of the invention, an electron beam, which leaks through gaps between the objects to be irradiated or which penetrates the objects to be irradiated, is reversed by a magnetic field approximately perpendicular to the scanning face of the electron beam by means of a magnet which is disposed under the objects to be irradiated, and the reversed electron beam is thereby again applied to the objects to be irradiated. A high utilization rate of the electron beam is accomplished, and the objects can be thereby uniformly irradiated with the electron beam. 4 claims, 6 drawing figures

  2. Investigation of the magnetic aftereffect in dilute Fe-Ni alloys after low-temperature neutron irradiation

    International Nuclear Information System (INIS)

    Blythe, H.J.; Walz, F.; Kronmueller, H.

    1982-01-01

    Dilute Fe alloys containing up to 0.5 at% Ni, neutron-irradiated at 77 K, exhibit a very complicated relaxation spectrum during anneal in the temperature range 30 to 350 K. This behaviour, in which individual peaks transform from one into another, is investigated in detail. All maxima occurring in the temperature range 30 to 140 K are found to be of Debye-type with relaxation times obeying an Arrhenius equation tau = tau 0 exp (Q/kT). The major processes of these spectra are computer-analysed in order to determine their activation parameters Q and tau 0 . The complicated peak genealogy, as observed on anneal, is attributed to the presence of two configurations of reorientating Fe interstitial atoms which form small clusters together with substitutionally and interstitially dissolved Ni atoms. (author)

  3. Modification of low temperature deposited LiMn2O4 thin film cathodes by oxygen plasma irradiation

    International Nuclear Information System (INIS)

    Chen, Chen Chung; Chiu, Kuo-Feng; Lin, Kun Ming; Lin, Hsin Chih

    2009-01-01

    Lithium manganese oxides have been deposited by radio frequency magnetron sputter deposition with relatively lower annealing temperatures and then post-treated with a radio frequency (rf) driven oxygen plasma. Following oxygen plasma irradiation, the film properties were modified, and the performance of the thin film cathode has been enhanced. The electrochemical properties of the treated thin-film cathodes were characterized and compared. The results showed that the samples with moderate plasma treatment also maintained good cyclic properties as cycled at a wide range potential window of 2.0 V-4.5 V. Its electrochemical properties were significantly improved by this process, even though the films were prepared under low annealing temperature.

  4. Extending the shelf-life of cocoyam leaves(xanthosoma sagitifolium) through blanching, irradiation and low temperature storage

    International Nuclear Information System (INIS)

    Afrifa, J.T.

    2013-07-01

    Cocoyam leaf (Xanthosoma sagiitifolium) (,Kontommire') is arguably one of the most readily available and cheap indigenous leafy vegetable that is commonly consumed in Ghana. It is noted to be a good source of minerals, vitamins and soluble fibre when consumed in its fresh (not raw though) state. However, this vegetable is highly perishable. Dehydration methods and jute sack storage are usually used for its preservation. However, these lead to discolouration, loss of some nutrients, and exposure to microbial contamination thus reducing the general acceptability by consumers. In view of this, a study was conducted to process and preserve the leaves in their fresh state. Preservation methods investigated were: refrigeration, steam blanching, gamma irradiation and a combination of these methods. The effect of the various preservation methods on some physicochemical properties (moisture content and dry matter by gravimetric method, vitamin C (ascorbic acid) was determined by iodometric titration method, crude protein was determined by Kjeldahl method, colour change using a Minolta CR310 colorimeter, pH using the Mettler Toledo pH meter (model:T3KfTLH); phytochemical properties (total phenolic using the Folin ciocalteau method and total flavonoids using aluminium chloride colorimetric method); microbial quality (total viable count, total coliforms, yeast and moulds count using serial dilution); consumer acceptance using a 9-point hedonic scale to assess the colour, texture and odour. The best packaging material for effective storage was also investigated. Fresh, fully opened leaves of cocoyam which were two (2) weeks old were collected from the Biotechnology and Nuclear Agriculture Research Institute (BNARI) farm and used for the study. They were decontaminated by washing in fifty (50) % of brine solution and shredded and apportioned for the various treatments, packaged into zip-lock polyethylene bags and hermetically sealed bags. The shelf-life study lasted for

  5. Synthesis and characterization polymer composites prepared by low-temperature post-irradiation polymerization of C_2F_4 in the presence of graphene-like material

    International Nuclear Information System (INIS)

    Shulga, Y.M.; Kiryukhin, D.P.; Vasilets, V.N.

    2015-01-01

    Polymer polytetrafluoroethylene (Ptfe)-microwave exfoliated graphene oxide (MEGO) composites containing up to 80 wt.% PTFE were prepared by low-temperature post-irradiation polymerization of C_2F_4 in the presence of the graphene-like material. Composites were characterized by elemental analysis, XPS, NMR, and DSC techniques. The melting point of PTFE in the composite (332.5°C) was higher than that of pure PTFE by 8.8°C. The measured values of the melting enthalpy (ΔHm=51.5 and 45.4 J/g) were used to calculate the extent of crystallinity in the PTFE and PTFE-MEGO composite (0.63 and 0.55, respectively). No - CF_3 end groups typical of commercial PTFE have been detected in the PTFE-MEGO composites. (authors)

  6. UV irradiation/cold shock-mediated apoptosis is switched to bubbling cell death at low temperatures.

    Science.gov (United States)

    Chen, Szu-Jung; Lin, Pei-Wen; Lin, Hsin-Ping; Huang, Shenq-Shyang; Lai, Feng-Jie; Sheu, Hamm-Ming; Hsu, Li-Jin; Chang, Nan-Shan

    2015-04-10

    When COS7 fibroblasts and other cells were exposed to UVC irradiation and cold shock at 4°C for 5 min, rapid upregulation and nuclear accumulation of NOS2, p53, WWOX, and TRAF2 occurred in 10-30 min. By time-lapse microscopy, an enlarging gas bubble containing nitric oxide (NO) was formed in the nucleus in each cell that finally popped out to cause "bubbling death". Bubbling occurred effectively at 4 and 22°C, whereas DNA fragmentation was markedly blocked at 4°C. When temperature was increased to 37°C, bubbling was retarded and DNA fragmentation occurred in 1 hr, suggesting that bubbling death is switched to apoptosis with increasing temperatures. Bubbling occurred prior to nuclear uptake of propidium iodide and DAPI stains. Arginine analog Nω-LAME inhibited NO synthase NOS2 and significantly suppressed the bubbling death. Unlike apoptosis, there were no caspase activation and flip-over of membrane phosphatidylserine (PS) during bubbling death. Bubbling death was significantly retarded in Wwox knockout MEF cells, as well as in cells overexpressing TRAF2 and dominant-negative p53. Together, UV/cold shock induces bubbling death at 4°C and the event is switched to apoptosis at 37°C. Presumably, proapoptotic WWOX and p53 block the protective TRAF2 to execute the bubbling death.

  7. Electron accelerator technology research in food irradiation

    International Nuclear Information System (INIS)

    Jin Jianqiao; Ye Mingyang; Zhang Yue; Yang Bin; Xu Tao; Kong Xiangshan

    2014-01-01

    Electronic accelerator was applied to instead of cobalt sources for food irradiation, to keep food quality and to improve the effect of the treatment. Appropriate accelerator parameters lead to optimal technique. The irradiation effect is associated with the relationship between uniformity and irradiating speed, the effect of cargo size on radiation penetration, as well as other factors that affect the irradiation effects. Industrialization of electron accelerator irradiation will be looked to the future. (authors)

  8. Positron lifetime measurements on electron irradiated amorphous alloys

    International Nuclear Information System (INIS)

    Moser, P.; Hautojaervi, P.; Chamberod, A.; Yli-Kauppila, J.; Van Zurk, R.

    1981-08-01

    Great advance in understanding the nature of point defects in crystalline metals has been achieved by employing positron annihilation technique. Positrons detect vacancy-type defects and the lifetime value of trapped positrons gives information on the size of submicroscopic vacancy aglomerates and microvoids. In this paper it is shown that low-temperature electron irradiations can result in a considerable increase in the positron lifetimes in various amorphous alloys because of the formation of vacancy-like defects which, in addition of the pre-existing holes, are able to trap positrons. Studied amorphous alloys were Fe 80 B 20 , Pd 80 Si 20 , Cu 50 Ti 50 , and Fe 40 Ni 40 P 14 B 6 . Electron irradiations were performed with 3 MeV electrons at 20 K to doses around 10 19 e - /cm 2 . After annealing positron lifetime spectra were measured at 77 K

  9. Low temperature experiments in radiation biophysics

    International Nuclear Information System (INIS)

    Moan, J.

    1977-01-01

    The reasons for performing experiments in radiation biophysics at low temperatures, whereby electron spectra may be studied, are explained. The phenomenon of phosphorescence spectra observed in frozen aqueous solutions of tryptophan and adenosine is also described. Free radicals play an important part in biological radiation effects and may be studied by ESR spectroscopy. An ESR spectrum of T 1 bacteriophages irradiated dry at 130K is illustrated and discussed. Hydrogen atoms, which give lines on the spectrum, are believed to be those radiation products causing most biological damage in a dry system. Low temperature experiments are of great help in explaining the significance of direct and indirect effects. This is illustrated for the case of trypsin. (JIW)

  10. Dynamics of modification of Ni/n-GaN Schottky barrier diodes irradiated at low temperature by 200 MeV Ag14+ ions

    International Nuclear Information System (INIS)

    Kumar, Ashish; Kumar, Tanuj; Kanjilal, D.; Hähnel, A.; Singh, R.

    2014-01-01

    Ni/GaN Schottky barrier diodes were irradiated with 200 MeV Ag ions up to fluence of 1 × 10 11 ions/cm 2 at the substrate temperature of 80 K. Post-irradiation current-voltage measurements showed that the ideality factor, n increased and the reverse leakage current, I R decreased with increase in fluence. But Schottky barrier height, ϕ b increased only marginally with increase in ion fluence. In situ resistivity measurements showed orders of magnitude increase in resistivity of GaN epitaxial film with irradiation fluence. Cross-sectional transmission electron microscopy images revealed the presence of defect clusters in bulk GaN after irradiation

  11. Spectral studies of intermediate species formed in one-electron reactions of bovine liver catalase at room and low temperatures. A comparison with peroxidase reactions

    International Nuclear Information System (INIS)

    Metodiewa, D.; Dunford, H.B.

    1992-01-01

    The reactions of native bovine catalase with superoxide and solvated electrons have been investigated using three different methods for generating these reducing substrates: γ-radiolysis of oxygenated or deaerated buffer solutions in the presence of an OH radical scavenger; either xanthine or acetaldehyde with xanthine oxidase; and low-temperature (77 K) γ-radiolysis of buffered ethylene glycol/water solutions with subsequent annealing of samples at 183 K. (Author)

  12. Velocity distribution of electrons in time-varying low-temperature plasmas: progress in theoretical procedures over the past 70 years

    Science.gov (United States)

    Makabe, Toshiaki

    2018-03-01

    A time-varying low-temperature plasma sustained by electrical powers with various kinds of fRequencies has played a key role in the historical development of new technologies, such as gas lasers, ozonizers, micro display panels, dry processing of materials, medical care, and so on, since World War II. Electrons in a time-modulated low-temperature plasma have a proper velocity spectrum, i.e. velocity distribution dependent on the microscopic quantum characteristics of the feed gas molecule and on the external field strength and the frequency. In order to solve and evaluate the time-varying velocity distribution, we have mostly two types of theoretical methods based on the classical and linear Boltzmann equations, namely, the expansion method using the orthogonal function and the procedure of non-expansional temporal evolution. Both methods have been developed discontinuously and progressively in synchronization with those technological developments. In this review, we will explore the historical development of the theoretical procedure to evaluate the electron velocity distribution in a time-varying low-temperature plasma over the past 70 years.

  13. Crystallographic study and self irradiation damage on plutonium at low temperature; Etude cristallographique et effets de l'auto-irradiation sur le plutonium a basse temperature

    Energy Technology Data Exchange (ETDEWEB)

    Solente, P [Commissariat a l' Energie Atomique, Fontenay-aux-Roses (France). Centre d' Etudes Nucleaires

    1965-05-01

    We have studied the variation of the parameters of {alpha} plutonium and aluminium stabilised {delta} alloys at low temperature, in order to verify the existence of an antiferromagnetic transition at low temperature. The effects of {alpha} particles on the length of a polycrystal of {alpha} plutonium at 4,2 deg. K are also presented at 18 deg. K a plutonium shows no crystallographic change from its structure at room temperature. The thermal expansion coefficients along the 3 axis seem to be positive at this temperature. Therefore a magnetic contribution on thermal expansion coefficients must be small. A dilatation anomaly of {delta}Pu has been observed at 100 deg. K, together with an anomaly of the diffraction lines intensity. No sur-structure line has been observed at 20 deg. K. The length of {alpha} plutonium Increases with time at a rate of about 5 x 10{sup -6} per hour when held in liquid helium. This effect is attributed to the creation of Frenkel pairs. (author) [French] On presente une etude cristallographique a basse temperature du plutonium {alpha} et stabilise {delta} par des additions d'aluminium en vue de verifier l'existence d'une transformation antiferromagnetique a basse temperature. L'effet des particules {alpha} a 4,2 deg. K sur la longueur d'un polycristal de plutonium {alpha} a egalement ete etudie. Il a ete determine que le plutonium {alpha} ne mange pas de phase allotropique Jusqu'a 18 deg. K, les coefficients de dilatation des trois axes de la maille semblent rester positifs. Une eventuelle contribution magnetique sur les coefficients de dilatation devrait donc etre faible. Une legere anomalie de dilatation de Pu {delta} a ete observee a 100 deg. K ainsi qu'une anomalie d'intensite des raies de diffraction. Aucune raie de surstructure n'a ete observee. Le plutonium {alpha} s'allonge lorsqu'il est plonge dans l'helium liquide d'un taux de l'ordre de 5 x 10{sup -6}/heure. Cet effet a ete attribuee a la creation de paires de Frenkel. (auteur)

  14. Low-temperature thermal expansion

    International Nuclear Information System (INIS)

    Collings, E.W.

    1986-01-01

    This chapter discusses the thermal expansion of insulators and metals. Harmonicity and anharmonicity in thermal expansion are examined. The electronic, magnetic, an other contributions to low temperature thermal expansion are analyzed. The thermodynamics of the Debye isotropic continuum, the lattice-dynamical approach, and the thermal expansion of metals are discussed. Relative linear expansion at low temperatures is reviewed and further calculations of the electronic thermal expansion coefficient are given. Thermal expansions are given for Cu, Al and Ti. Phenomenologic thermodynamic relationships are also discussed

  15. Radiation detection at very low temperature. DRTBT 1991 Aussois - Course collection

    International Nuclear Information System (INIS)

    Salce, B.; Godfrin, H.; Dumoulin, L.; Garoche, Pierre; Pannetier, B.; Equer, B.; Hubert, PH.; Urbina, C.; Lamarre, J.M.; Brison, J.P.; Lesueur, D.; Bret, J.L.; Ayela, F.; Coron, N.; Gonzalez-Mestres, L.

    1991-12-01

    This publication gather several courses which propose or address: Thermal conduction, Kapitza resistance, Metal-insulator transition, Thermal properties and specific heat at low temperature, Thermometry, Low temperature superconductors, Defects due to irradiations in solids, Semiconducting detectors, Techniques of protection of a measurement assembly at low temperatures against perturbations, Noise reduction by impedance matching converter at low temperature, Low noise electronics and measurement, Low radio-activities, SQUID and electrometer, Results and expectations related to bolometers, Infrared and sub-millimetre radiation in astrophysics, Neutrinos, dark matter and heavy ions

  16. Mechanical properties of electron beam welds of 316LN austenitic steels at low temperature for ITER gravity support system

    International Nuclear Information System (INIS)

    Lee, P.Y.; Huo, B.L.; Kuai, K.W.

    2007-01-01

    The gravity support system in ITER not only sustains magnet system, the vacuum vessel and in-vessel components, but also endures several large forces, such as electromagnetic force, thermal load and seismic loads. Based on the ITER design report, the maximum displacement of the gravity support system is estimated to be 32 mm in radial direction at the top flange of the flexible plates during the TF coil cool down from room temperature to 80 k. Welds are located in the peak stress region and subject to cyclic loads in the top flange is a potential problem. Therefore, the mechanical properties of the welds are extremely important for this system. 316LN austenitic stainless steel has been selected as the gravity support structure materials. However, there is still lack of the related mechanical data of the welding components of 316LN stainless steel at present. In this study, we are systematically investigated the mechanical properties of the welding components at low temperature. (authors)

  17. Recovery behavior of high purity cubic SiC polycrystals by post-irradiation annealing up to 1673 K after low temperature neutron irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Idris, Mohd Idzat, E-mail: idzat.i.aa@m.titech.ac.jp [Department of Nuclear Engineering, Graduate School of Science and Engineering, Tokyo Institute of Technology, 2-12-1, Ookayama, Meguro-ku, Tokyo 152-8550 Japan (Japan); The National University of Malaysia, School of Applied Physics, Faculty of Science and Technology, 43600 Bangi Selangor (Malaysia); Yamazaki, Saishun; Yoshida, Katsumi; Yano, Toyohiko [Research Laboratory for Nuclear Reactors, Tokyo Institute of Technology, 2-12-1, Ookayama, Meguro-ku, Tokyo 152-8550 Japan (Japan)

    2015-10-15

    Two kinds of high purity cubic (β) SiC polycrystals, PureBeta-SiC and CVD-SiC, were irradiated in the BR2 reactor (Belgium) up to a fluence of 2.0–2.5 × 10{sup 24} (E > 0.1 MeV) at 333–363 K. Changes in macroscopic lengths were examined by post-irradiation thermal annealing using a precision dilatometer up to 1673 K with a step-heating method. The specimen was held at each temperature step for 6 h and the change in length of the specimen was recorded during each isothermal annealing step from 373 K to 1673 K with 50 K increments. The recovery curves were analyzed with the first order model, and rate constants at each annealing step were obtained. Recovery of defects, induced by neutron irradiation in high purity β-SiC, has four stages of different activation energies. At 373–573 K, the activation energy of PureBeta-SiC and CVD-SiC was in the range of 0.17–0.24 eV and 0.12–0.14 eV; 0.002–0.04 eV and 0.006–0.04 eV at 723–923 K; 0.20–0.27 eV and 0.26–0.31 eV at 923–1223 K; and 1.37–1.38 eV and 1.26–1.29 eV at 1323–1523 K, respectively. Below ∼1223 K the recombination occurred possibly for closely positioned C and Si Frenkel pairs, and no long range migration is deemed essential. Nearly three-fourths of recovery, induced by neutron irradiation, occur by this mechanism. In addition, at 1323–1523 K, recombination of slightly separated C Frenkel pairs and more long-range migration of Si interstitials may have occurred for PureBeta-SiC and CVD-SiC specimens. Migration of both vacancies may be restricted up to ∼1523 K. Comparing to hexagonal α-SiC, high purity β-SiC recovered more quickly in the lower annealing temperature range of less than 873 K, in particular less than 573 K. - Highlights: • Two kinds of high purity cubic (β) SiC polycrystals were irradiated. • Macroscopic lengths were examined by post-irradiation thermal annealing. • The recovery curves were analyzed with first order model.

  18. Low-temperature system for simultaneous counting of conversion electrons and backscattered [gamma]-rays in Moessbauer effect experiment

    Energy Technology Data Exchange (ETDEWEB)

    Ruskov, Todor (Institute for Nuclear Research and Nuclear Energy, Tsarigradsko shosse 72, Sofia 1784 (Bulgaria)); Passage, Guener (Institute for Nuclear Research and Nuclear Energy, Tsarigradsko shosse 72, Sofia 1784 (Bulgaria)); Rastanawi, Abdallah (Institute for Nuclear Research and Nuclear Energy, Tsarigradsko shosse 72, Sofia 1784 (Bulgaria)); Radev, Rumen (Institute for Nuclear Research and Nuclear Energy, Tsarigradsko shosse 72, Sofia 1784 (Bulgaria))

    1994-12-01

    A system for simultaneous detection of conversion electrons, emitted after resonant exciting of [sup 57]Fe, and resonant backscattered [gamma]-rays and X-rays, accompanying the conversion electrons, is described. The system includes a helium proportional counter, for detection of conversion electrons, and a toroidal ''Keisch-type'' proportional counter, connected to the vacuum part of a helium cryostat. ((orig.))

  19. Electron and photon-beam induced reactions of adsorbed disilane: Low-temperature thin-film growth

    International Nuclear Information System (INIS)

    Bozso, F.; Avouris, Ph.

    1991-01-01

    Electrons and photons of sufficient energy can cause fragmentation and desorption of adsorbed molecules or fragments of them, by inducing electronic excitations to dissociative states. The surface species after such excitations are mostly of highly reactive radical character, which readily react with the substrate and with other molecular or radical species in the adsorbed layer. This paper discusses the adsorption, thermal and electron/photon-beam induced reactions of disilane, oxygen and ammonia on Si(111)-7x7, and the electron/photon-induced growth of silicon, silicon dioxide and silicon nitride films at 100K

  20. Low-temperature, solution-processed aluminum-doped zinc oxide as electron transport layer for stable efficient polymer solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Zhu, Qianqian [College of Materials Science and Engineering, Qingdao University of Science and Technology, Qingdao 266042 (China); Qingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao 266101 (China); Bao, Xichang, E-mail: baoxc@qibebt.ac.cn [Qingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao 266101 (China); Yu, Jianhua [College of Materials Science and Engineering, Qingdao University of Science and Technology, Qingdao 266042 (China); Zhu, Dangqiang [Qingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao 266101 (China); Zhang, Qian [College of Materials Science and Engineering, Qingdao University of Science and Technology, Qingdao 266042 (China); Gu, Chuantao [Qingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao 266101 (China); Dong, Hongzhou [College of Materials Science and Engineering, Qingdao University of Science and Technology, Qingdao 266042 (China); Yang, Renqiang [Qingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao 266101 (China); Dong, Lifeng, E-mail: DongLifeng@qust.edu.cn [College of Materials Science and Engineering, Qingdao University of Science and Technology, Qingdao 266042 (China); Department of Physics, Hamline University, St. Paul, MN 55104 (United States)

    2016-04-30

    A simple low-temperature solution-processed zinc oxide (ZnO) and aluminum-doped ZnO (AZO) were synthesized and investigated as an electron transport layer (ETL) for inverted polymer solar cells. A solar cell with a blend of poly(4,8-bis-alkyloxy-benzo[1,2-b:4,5-b′] dithiophene-alt-alkylcarbonyl-thieno [3,4-b] thiophene) and (6,6)-phenyl-C71-butyric acid methyl ester as an active layer and AZO as ETL demonstrates a high power conversion efficiency (PCE) of 7.36% under the illumination of AM 1.5G, 100 mW/cm{sup 2}. Compared to the cells with ZnO ETL (PCE of 6.85%), the PCE is improved by 7.45% with the introduction of an AZO layer. The improved PCE is ascribed to the enhanced short circuit current density, which results from the electron transport property of the AZO layer. Moreover, AZO is a more stable interfacial layer than ZnO. The PCE of the solar cells with AZO as ETL retain 85% of their original value after storage for 120 days, superior to the 39% of cells with ZnO ETL. The results above indicate that a simple low-temperature solution-processed AZO film is an efficient and economical ETL for high-performance inverted polymer solar cells. Due to its environmental friendliness, good electrical properties, and simple preparation approach, AZO has the potential to be applied in high-performance, large-scale industrialization of solar cells and other electronic devices. - Highlights: • ZnO and AZO were synthesized by a simple low-temperature solution-processed method. • AZO films show high transmittance and conductivity. • The photovoltaic performance can be improved with AZO as ETL. • AZO-based devices demonstrate excellent stability, with 85% retained after 120 days.

  1. Dose distributions in electron irradiated plastic tubing

    International Nuclear Information System (INIS)

    Miller, A.; Pederson, W.B.

    1981-01-01

    Plastic tubes have been crosslinked by irradiation at a 10 MeV linear electron accelerator and at a 400 keV DC electron accelerator at different irradiation geometries. The diameter of the different tubes was 20, 33 and 110 millimeters. Dose distributions have been measured with thin radiochromic dye films, indicating that in all cases irradiation from two sides is a necessary and sufficient condition for obtaining a satisfactory dose distribution. (author)

  2. Effects of low temperature periodic annealing on the deep-level defects in 200 keV proton irradiated AlGaAs-GaAs solar cells

    Science.gov (United States)

    Li, S. S.; Chiu, T. T.; Loo, R. Y.

    1981-01-01

    The GaAs solar cell has shown good potential for space applications. However, degradation in performance occurred when the cells were irradiated by high energy electrons and protons in the space environment. The considered investigation is concerned with the effect of periodic thermal annealing on the deep-level defects induced by the 200 keV protons in the AlGaAs-GaAs solar cells. Protons at a fluence of 10 to the 11th P/sq cm were used in the irradiation cycle, while annealing temperatures of 200 C (for 24 hours), 300 C (six hours), and 400 C (six hours) were employed. The most likely candidate for the E(c) -0.71 eV electron trap observed in the 200 keV proton irradiated samples may be due to GaAs antisite, while the observed E(v) +0.18 eV hole trap has been attributed to the gallium vacancy related defect. The obtained results show that periodic annealing in the considered case does not offer any advantages over the one time annealing process.

  3. Microstructural evolution in modified 9Cr-1Mo ferritic/martensitic steel irradiated with mixed high-energy proton and neutron spectra at low temperatures

    International Nuclear Information System (INIS)

    Sencer, B.H.; Garner, F.A.; Gelles, D.S.; Bond, G.M.; Maloy, S.A.

    2002-01-01

    Modified 9Cr-1Mo ferritic/martensitic steel was exposed at 32-57 deg. C to a mixed proton/neutron particle flux and spectrum at the Los Alamos Neutron Science Center. The microstructure of unirradiated 9Cr-1Mo consists of laths, dislocations and carbides. Examination of electron diffraction patterns obtained from extraction replicas of unirradiated 9Cr-1Mo revealed that the precipitate microstructure was primarily dominated by M 23 C 6 carbides. The post-irradiation microstructure contained black-spot damage in addition to precipitates and dislocations. Examination of electron diffraction patterns revealed diffuse rings from M 23 C 6 carbides, indicating amorphization and/or nanocrystallinity. Crystalline MC carbides were also found. No cavity formation was found although a significant amount of helium and hydrogen generation had been generated. TEM-EDS examination of extraction replicas for carbides from unirradiated and irradiated samples did not show any detectable changes in composition of either M 23 C 6 or MC carbides. There was also no evident change in carbide size. Lattice images of M 23 C 6 carbides revealed an amorphous microstructure following irradiation, but MC carbides were still crystalline

  4. All-inkjet-printed flexible electronics fabrication on a polymer substrate by low-temperature high-resolution selective laser sintering of metal nanoparticles

    International Nuclear Information System (INIS)

    Ko, Seung H; Pan Heng; Grigoropoulos, Costas P; Luscombe, Christine K; Frechet, Jean M J; Poulikakos, Dimos

    2007-01-01

    All-printed electronics is the key technology to ultra-low-cost, large-area electronics. As a critical step in this direction, we demonstrate that laser sintering of inkjet-printed metal nanoparticles enables low-temperature metal deposition as well as high-resolution patterning to overcome the resolution limitation of the current inkjet direct writing processes. To demonstrate this process combined with the implementation of air-stable carboxylate-functionalized polythiophenes, high-resolution organic transistors were fabricated in ambient pressure and room temperature without utilizing any photolithographic steps or requiring a vacuum deposition process. Local thermal control of the laser sintering process could minimize the heat-affected zone and the thermal damage to the substrate and further enhance the resolution of the process. This local nanoparticle deposition and energy coupling enable an environmentally friendly and cost-effective process as well as a low-temperature manufacturing sequence to realize large-area, flexible electronics on polymer substrates

  5. Radiation defects in electron-irradiated InP crystals

    Energy Technology Data Exchange (ETDEWEB)

    Brailovskii, E.Yu.; Karapetyan, F.K.; Megela, I.G.; Tartachnik, V.P. (AN Ukrainskoj SSR, Kiev. Inst. Yadernykh Issledovanij)

    1982-06-16

    The results are presented of formation and annealing of defects in InP crystals at 1 to 50 MeV electron irradiation. The recovery of electrical properties in the range of 77 to 970 K during annealing processes is studied. Five low temperature annealing states in n-InP and the reverse annealing in p-InP are observed at 77 to 300 K. Four annealing stages at temperatures higher than 300 K are present. When the electron energy is increased more complicated thermostable defects are formed, and at 50 MeV electron energy besides of the point defect clusters are formed, which anneal at temperatures of 800 to 970 K. It is shown that the peculiarities of the Hall mobility at irradiation and annealing are caused by the scattering centres E/sub c/ - 0.2 eV. The 'limiting' position of the Fermi level in electron irradiated InP crystals is discussed.

  6. Pulse radiolysis study in ethanol and N-propanol of the solvated electron formation and reactivity at low temperatures

    International Nuclear Information System (INIS)

    Bono Merino, M.R.

    1978-01-01

    The electron solvation process in polar media has been studied in liquid ethanol and n-propanol at temperatures near their melting points. The results show that using the change of absorption at a given wavelength to determine the solvation time leads to a value which varies with the wavelength considered. Furthermore, for n-propanol it appears that the process occurs without a definite order. Studies of the spectral shifts show that the passage from the initial to the final spectrum (solvated electron spectrum) involves intermediate transient spectra which probably correspond to partly solvated states of the electron. The interpretation of these various results points out the ambiguity of the kinetic measurements: the simultaneous existence of several partly solvated states of the electron is not consistent with the hypothesis previously admitted that the molar extinction coefficient at a given wavelength is unique and does not vary with time. The reaction of the solvated electron with acetone has been studied in ethanol in the temperature range from +25 to -105 0 C: this reaction is diffusion controlled [fr

  7. O3 Layers via Spray Pyrolysis at Low Temperatures and Their Application in High Electron Mobility Transistors

    KAUST Repository

    Isakov, Ivan

    2017-04-06

    The growth mechanism of indium oxide (InO) layers processed via spray pyrolysis of an aqueous precursor solution in the temperature range of 100-300 °C and the impact on their electron transporting properties are studied. Analysis of the droplet impingement sites on the substrate\\'s surface as a function of its temperature reveals that Leidenfrost effect dominated boiling plays a crucial role in the growth of smooth, continuous, and highly crystalline InO layers via a vapor phase-like process. By careful optimization of the precursor formulation, deposition conditions, and choice of substrate, this effect is exploited and ultrathin and exceptionally smooth layers of InO are grown over large area substrates at temperatures as low as 252 °C. Thin-film transistors (TFTs) fabricated using these optimized InO layers exhibit superior electron transport characteristics with the electron mobility reaching up to 40 cm V s, a value amongst the highest reported to date for solution-processed InO TFTs. The present work contributes enormously to the basic understanding of spray pyrolysis and highlights its tremendous potential for large-volume manufacturing of high-performance metal oxide thin-film transistor electronics.

  8. O3 Layers via Spray Pyrolysis at Low Temperatures and Their Application in High Electron Mobility Transistors

    KAUST Repository

    Isakov, Ivan; Faber, Hendrik; Grell, Max; Wyatt-Moon, Gwenhivir; Pliatsikas, Nikos; Kehagias, Thomas; Dimitrakopulos, George P.; Patsalas, Panos P.; Li, Ruipeng; Anthopoulos, Thomas D.

    2017-01-01

    The growth mechanism of indium oxide (InO) layers processed via spray pyrolysis of an aqueous precursor solution in the temperature range of 100-300 °C and the impact on their electron transporting properties are studied. Analysis of the droplet impingement sites on the substrate's surface as a function of its temperature reveals that Leidenfrost effect dominated boiling plays a crucial role in the growth of smooth, continuous, and highly crystalline InO layers via a vapor phase-like process. By careful optimization of the precursor formulation, deposition conditions, and choice of substrate, this effect is exploited and ultrathin and exceptionally smooth layers of InO are grown over large area substrates at temperatures as low as 252 °C. Thin-film transistors (TFTs) fabricated using these optimized InO layers exhibit superior electron transport characteristics with the electron mobility reaching up to 40 cm V s, a value amongst the highest reported to date for solution-processed InO TFTs. The present work contributes enormously to the basic understanding of spray pyrolysis and highlights its tremendous potential for large-volume manufacturing of high-performance metal oxide thin-film transistor electronics.

  9. Electron cyclotron heating and current drive approach for low-temperature startup plasmas using O-X-EBW mode conversion

    International Nuclear Information System (INIS)

    Batchelor, D.B.; Bigelow, T.S.

    1997-01-01

    A mechanism for heating and driving currents in very overdense plasmas is considered based on a double-mode conversion: Ordinary mode to Extraordinary mode to electron Bernstein wave. The possibility of using this mechanism for plasma buildup and current ramp in the National Spherical Torus Experiment is investigated

  10. Amorphous Tin Oxide as a Low-Temperature-Processed Electron-Transport Layer for Organic and Hybrid Perovskite Solar Cells

    KAUST Repository

    Barbe, Jeremy; Tietze, Max Lutz; Neophytou, Marios; Banavoth, Murali; Alarousu, Erkki; El Labban, Abdulrahman; Abulikemu, Mutalifu; Yue, Wan; Mohammed, Omar F.; McCulloch, Iain; Amassian, Aram; Del Gobbo, Silvano

    2017-01-01

    Chemical bath deposition (CBD) of tin oxide (SnO) thin films as an electron-transport layer (ETL) in a planar-heterojunction n-i-p organohalide lead perovskite and organic bulk-heterojunction (BHJ) solar cells is reported. The amorphous SnO (a

  11. Mechanical-property changes of structural composite materials after low-temperature proton irradiation: Implications for use in SSC magnet systems

    International Nuclear Information System (INIS)

    Morena, J.; Snead, C.L. Jr.; Czajkowski, C.; Skaritka, J.

    1993-01-01

    Longterm physical, mechanical, electrical, and other properties of advanced composites, plastics, and other polymer materials are greatly affected by high-energy proton, neutron, electron, and gamma radiation. The effects of high-energy particles on materials is a critical design parameter to consider when choosing polymeric structural, nonstructural, and elastomeric matrix resin systems. Polymer materials used for filled resins, laminates, seals, gaskets, coatings, insulation and other nonmetallic components must be chosen carefully, and reference data viewed with caution. Most reference data collected in the high-energy physics community to date reflects material property degradation using other than proton irradiations. In most instances, the data were collected for room-temperature irradiations, not 4.2 K or other cryogenic temperatures, and at doses less than 10 8 --10 9 Rad. Energetic proton (and the accompanying spallation-product particles) provide good simulation fidelity to the expected radiation fields predicted for the cold-mass regions of the SSC magnets, especially the corrector magnets. The authors present here results for some structural composite materials which were part of a larger irradiation-characterization of polymeric materials for SSC applications

  12. Electronic properties of polyamide-PPy/metal junction and electrical conductivity of a typical sample at low temperatures

    International Nuclear Information System (INIS)

    Suenel, N.; Sedef, A.G.; Parlak, M.; Toppare, L.

    2005-01-01

    Electronic properties of junctions fabricated by polyamide-polypyrrole composite films polymerized with adjusted doping concentration and various metal contacts (In, Al, Au and Ag) were investigated. For the junctions giving good rectification I 0 , n and φ b were specified. Conductivity of polyamide-polypyrrole composite polymer was obtained as a function of temperature in the 70-320 K range and was found to obey the VRH model. In addition the Mott parameters were evaluated

  13. Electronic properties of polyamide-PPy/metal junction and electrical conductivity of a typical sample at low temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Suenel, N. [Gaziosmanpasa University, Physics Department, Tasliciftlik Kampasu, Tokat (Turkey)]. E-mail: nsunel@gop.edu.tr; Sedef, A.G. [Gaziosmanpasa University, Physics Department, Tasliciftlik Kampasu, Tokat (Turkey); Parlak, M. [Middle East Technical University, Physics Department, Ankara (Turkey); Toppare, L. [Middle East Technical University, Chemistry Department, Ankara (Turkey)

    2005-05-15

    Electronic properties of junctions fabricated by polyamide-polypyrrole composite films polymerized with adjusted doping concentration and various metal contacts (In, Al, Au and Ag) were investigated. For the junctions giving good rectification I{sub 0}, n and {phi}{sub b} were specified. Conductivity of polyamide-polypyrrole composite polymer was obtained as a function of temperature in the 70-320 K range and was found to obey the VRH model. In addition the Mott parameters were evaluated.

  14. Corrosion of electron-irradiated Zr-2.5Nb and Zircaloy-2

    Energy Technology Data Exchange (ETDEWEB)

    Woo, O.-T.; McDougall, G.M.; Hutcheon, R.M.; Urbanic, V.F.; Griffiths, M.; Coleman, C.E

    2000-07-01

    We used 10-MeV electrons to rapidly produce radiation damage in zirconium alloys, investigated whether electrons produced the same microstructural changes as neutrons, then performed post-irradiation corrosion tests to determine whether electron-irradiated materials displayed similar corrosion behavior to neutron-irradiated materials. Two irradiations were completed using 10-MeV electrons with the beam normal to thin disks of material of 4 diameter slightly larger than the beam. The beam distribution. and disk cooling were designed to produce radial temperature and dose distributions having maxima at the disk center. A high-temperature irradiation was performed on annealed Zr-2.5Nb disks, achieving a central dose of 1.3 dpa and at a central temperature of {approx}450 deg C. After irradiation, the samples contained needle-like {beta}-Nb precipitates in the {alpha}-Zr matrix similar to those produced by neutrons. A low-temperature irradiation was performed on half-moon disks of Zr-2.5Nb and Zircaloy-2 pressure tube materials at 310 deg C central temperature and 1.3-dpa central dose. Dislocation loops were observed, again similar to those produced in neutron-irradiated materials. Some of the high-temperature electron-irradiated disks were exposed to 300 deg C moist air (saturated with D{sub 2}O), and in separate tests, high- and low-temperature irradiated disks were corroded in 300 deg C D{sub 2}0 (11.0 pD at room temperature) in an autoclave. Measurements of oxide thickness by Fourier Transform Infrared Reflectance (FTIR) spectroscopy showed that electron irradiation reduced the corrosion rate of Zr-2.5Nb compared with that of unirradiated material, as observed for neutron irradiation. For exposures to moist air and to D{sub 2}O, the theoretical deuterium uptakes for the electron-irradiated materials were, respectively, about 4 times and 1.5 to 2 times those for the unirradiated materials. This is also in good agreement with results for neutron-irradiated pressure

  15. Corrosion of electron-irradiated Zr-2.5Nb and Zircaloy-2

    International Nuclear Information System (INIS)

    Woo, O.-T.; McDougall, G.M.; Hutcheon, R.M.; Urbanic, V.F.; Griffiths, M.; Coleman, C.E.

    2000-01-01

    We used 10-MeV electrons to rapidly produce radiation damage in zirconium alloys, investigated whether electrons produced the same microstructural changes as neutrons, then performed post-irradiation corrosion tests to determine whether electron-irradiated materials displayed similar corrosion behavior to neutron-irradiated materials. Two irradiations were completed using 10-MeV electrons with the beam normal to thin disks of material of 4 diameter slightly larger than the beam. The beam distribution. and disk cooling were designed to produce radial temperature and dose distributions having maxima at the disk center. A high-temperature irradiation was performed on annealed Zr-2.5Nb disks, achieving a central dose of 1.3 dpa and at a central temperature of ∼450 deg C. After irradiation, the samples contained needle-like β-Nb precipitates in the α-Zr matrix similar to those produced by neutrons. A low-temperature irradiation was performed on half-moon disks of Zr-2.5Nb and Zircaloy-2 pressure tube materials at 310 deg C central temperature and 1.3-dpa central dose. Dislocation loops were observed, again similar to those produced in neutron-irradiated materials. Some of the high-temperature electron-irradiated disks were exposed to 300 deg C moist air (saturated with D 2 O), and in separate tests, high- and low-temperature irradiated disks were corroded in 300 deg C D 2 0 (11.0 pD at room temperature) in an autoclave. Measurements of oxide thickness by Fourier Transform Infrared Reflectance (FTIR) spectroscopy showed that electron irradiation reduced the corrosion rate of Zr-2.5Nb compared with that of unirradiated material, as observed for neutron irradiation. For exposures to moist air and to D 2 O, the theoretical deuterium uptakes for the electron-irradiated materials were, respectively, about 4 times and 1.5 to 2 times those for the unirradiated materials. This is also in good agreement with results for neutron-irradiated pressure tube materials. Thus, 10-Me

  16. Green coffee decontamination by electron beam irradiation

    International Nuclear Information System (INIS)

    Nemtanu, Monica R.; Brasoveanu, Mirela; Grecu, Maria Nicoleta; Minea, R.

    2005-01-01

    Microbiological load of green coffee is a real problem considering that it is extremely sensitive to contamination. Irradiation is a decontamination method for a lot of foodstuffs, being a feasible, very effective and environment friendly one. Beans and ground green coffee were irradiated with electron beams up to 40 kGy. Microbial load, rheological behavior, electron paramagnetic resonance (EPR) and visible spectroscopy were carried out. The results show that electron beam irradiation of green coffee could decontaminate it without severe changes in its properties

  17. Structural changes induced by electron irradiation

    International Nuclear Information System (INIS)

    Koike, J.; Pedraza, D.F.

    1993-01-01

    Highly oriented pyrolytic graphite was irradiated at room temperature with 300 kV electrons. Transmission electron microscopy and electron energy loss spectroscopy were employed to study the structural changes produced by irradiation. The occurrence of a continuous ring intensity in the selected area diffraction (SAD) pattern obtained on a specimen irradiated with the electron beam parallel to the c-crystallographic axis indicated that microstructural changes had occurred. However, from the SAD pattern obtained for the specimens tilted relative to the irradiation direction, it was found that up to a fluence of 1.1x10 27 e/m 2 graphite remained crystalline. An SAD pattern of a specimen irradiated with the electron beam perpendicular to the c-axis confirmed the persistence of crystalline order. High resolution electron microscopy showed that ordering along the c-axis direction remained. A density reduction of 8.9% due to irradiation was determined from the plasmon frequency shift. A qualitative model is proposed to explain these observations. A new determination of the threshold displacement energy, Ed, of carbon atoms in graphite was done by examining the appearance of a continuous ring in the SAD pattern at various electron energies. A value of 30 eV was obtained whether the incident electron beam was parallel or perpendicular to the c-axis, demonstrating that Ed is independent of the displacement direction

  18. Electron microscopy of boron carbide before and after electron irradiation

    International Nuclear Information System (INIS)

    Stoto, T.; Zuppiroli, L.; Beauvy, M.; Athanassiadis, T.

    1984-06-01

    The microstructure of boron carbide has been studied by electron microscopy and related to the composition of the material. After electron irradiations in an usual transmission electron microscope and in a high voltage electron microscope at different temperatures and fluxes no change of these microstructures have been observed but a sputtering of the surface of the samples, which has been studied quantitatively [fr

  19. Electron spin resonance identification of irradiated fruits

    International Nuclear Information System (INIS)

    Raffi, J.J.; Agnel, J.-P.L.

    1989-01-01

    The electron spin resonance spectrum of achenes, pips, stalks and stones from irradiated fruits (stawberry, raspberry, red currant, bilberry, apple, pear, fig, french prune, kiwi, water-melon and cherry) always displays, just after γ-treatment, a weak triplet (a H ∼30 G) due to a cellulose radical; its left line (lower field) can be used as an identification test of irradiation, at least for strawberries, raspberries, red currants or bilberries irradiated in order to improve their storage time. (author)

  20. Impact of Gate Dielectric in Carrier Mobility in Low Temperature Chalcogenide Thin Film Transistors for Flexible Electronics

    KAUST Repository

    Salas-Villasenor, A. L.; Mejia, I.; Hovarth, J.; Alshareef, Husam N.; Cha, D. K.; Ramirez-Bon, R.; Gnade, B. E.; Quevedo-Lopez, M. A.

    2010-01-01

    Cadmium sulfide thin film transistors were demonstrated as the n-type device for use in flexible electronics. CdS thin films were deposited by chemical bath deposition (70° C) on either 100 nm HfO2 or SiO2 as the gate dielectrics. Common gate transistors with channel lengths of 40-100 μm were fabricated with source and drain aluminum top contacts defined using a shadow mask process. No thermal annealing was performed throughout the device process. X-ray diffraction results clearly show the hexagonal crystalline phase of CdS. The electrical performance of HfO 2 /CdS -based thin film transistors shows a field effect mobility and threshold voltage of 25 cm2 V-1 s-1 and 2 V, respectively. Improvement in carrier mobility is associated with better nucleation and growth of CdS films deposited on HfO2. © 2010 The Electrochemical Society.

  1. Impact of Gate Dielectric in Carrier Mobility in Low Temperature Chalcogenide Thin Film Transistors for Flexible Electronics

    KAUST Repository

    Salas-Villasenor, A. L.

    2010-06-29

    Cadmium sulfide thin film transistors were demonstrated as the n-type device for use in flexible electronics. CdS thin films were deposited by chemical bath deposition (70° C) on either 100 nm HfO2 or SiO2 as the gate dielectrics. Common gate transistors with channel lengths of 40-100 μm were fabricated with source and drain aluminum top contacts defined using a shadow mask process. No thermal annealing was performed throughout the device process. X-ray diffraction results clearly show the hexagonal crystalline phase of CdS. The electrical performance of HfO 2 /CdS -based thin film transistors shows a field effect mobility and threshold voltage of 25 cm2 V-1 s-1 and 2 V, respectively. Improvement in carrier mobility is associated with better nucleation and growth of CdS films deposited on HfO2. © 2010 The Electrochemical Society.

  2. In situ observation of low temperature growth of Ge on Si(1 1 1) by reflection high energy electron diffraction

    International Nuclear Information System (INIS)

    Grimm, Andreas; Fissel, Andreas; Bugiel, Eberhard; Wietler, Tobias F.

    2016-01-01

    Highlights: • Investigation of the initial stages of epitaxial growth of Ge on Si(1 1 1) in situ by RHEED. • Impact of growth temperature on strain evolution for temperatures between 200 °C and 400 °C. • Epitaxy with a high degree of structural perfection already at growth temperature of 200 °C. • Ordered interfacial dislocation networks already at 200 °C. • Tensile strain contribution of Si(1 1 1) 7 × 7-surface reconstruction to strain relaxation process for epitaxial growth of Ge. - Abstract: In this paper we investigate the initial stages of epitaxial growth of Ge on Si(1 1 1) and the impact of growth temperature on strain evolution in situ by reflection high energy electron diffraction (RHEED) for temperatures between 200 °C and 400 °C. The change in surface morphology from a flat wetting layer to subsequent islanding that is characteristic for Stranski–Krastanov growth is monitored by spot intensity analysis. The corresponding critical layer thickness is determined to 3.1 < d c < 3.4 ML. In situ monitoring of the strain relaxation process reveals a contribution of the Si(1 1 1) 7 × 7-surface reconstruction to the strain relaxation process. High resolution transmission electron microscopy confirms that the Ge islands exhibit a high degree of structural perfection and an ordered interfacial misfit dislocation network already at a growth temperature of 200 °C is established. The temperature dependency of island shape, density and height is characterized by atomic force microscopy and compared to the RHEED investigations.

  3. Development of a highly efficient conversion electron Moessbauer spectroscopy (CEMS) detector for low temperature (xPb1-x)Te bilayers

    International Nuclear Information System (INIS)

    Pombo, Carlos Jose da Silva Matos

    2006-01-01

    The 57 Fe Moessbauer spectroscopy is a nuclear, non-destructive technique used for the investigation of structural, magnetic and hyperfine properties of several materials. It is a powerful tool in characterizing materials in physics, metallurgy, geology and biology field areas, especially magnetic materials, alloys and minerals containing Fe. Lately, the Conversion Electron Moessbauer Spectroscopy (CEMS) is widely used in making studies on ultra-thin magnetic films, as well as other nanostructured materials. In case of magnetic nanostructures, low temperature (LT) studies are especially important due to the possibility of dealing with superparamagnetic effects. In this work it was developed a CEMS measurement system for low temperatures ( R ) and an optical cryostat (Model SVT-400, Janis Research Co, USA), from which the project was originally conceived at the Applied Physics / Moessbauer spectroscopy Department from University of Duisburg-Essen, Germany. The LT-CEMS system was fully built, tested and successfully applied in a preliminary characterization of Fe/(Eu x Pb 1-x )Te(111) bilayers with use of a 15 angstrom, 57 Fe probe layer, with reasonable results at sample temperatures as low as 8 K. (author)

  4. High energy electron irradiation of flowable materials

    International Nuclear Information System (INIS)

    Offermann, B.P.

    1975-01-01

    In order to efficiently irradiate a flowable material with high energy electrons, a hollow body is disposed in a container for the material and the material is caused to flow in the form of a thin layer across a surface of the body from or to the interior of the container while the material flowing across the body surface is irradiated. (U.S.)

  5. Low-temperature growth and electronic structures of ambipolar Yb-doped zinc tin oxide transparent thin films

    Science.gov (United States)

    Oh, Seol Hee; Ferblantier, Gerald; Park, Young Sang; Schmerber, Guy; Dinia, Aziz; Slaoui, Abdelilah; Jo, William

    2018-05-01

    The compositional dependence of the crystal structure, optical transmittance, and surface electric properties of the zinc tin oxide (Zn-Sn-O, shortened ZTO) thin films were investigated. ZTO thin films with different compositional ratios were fabricated on glass and p-silicon wafers using radio frequency magnetron sputtering. The binding energy of amorphous ZTO thin films was examined by a X-ray photoelectron spectroscopy. The optical transmittance over 70% in the visible region for all the ZTO films was observed. The optical band gap of the ZTO films was changed as a result of the competition between the Burstein-Moss effect and renormalization. An electron concentration in the films and surface work function distribution were measured by a Hall measurement and Kelvin probe force microscopy, respectively. The mobility of the n- and p-type ZTO thin films have more than 130 cm2/V s and 15 cm2/V s, respectively. We finally constructed the band structure which contains band gap, work function, and band edges such as valence band maximum and conduction band minimum of ZTO thin films. The present study results suggest that the ZTO thin film is competitive compared with the indium tin oxide, which is a representative material of the transparent conducting oxides, regarding optoelectronic devices applications.

  6. Food irradiation by low energy electrons

    International Nuclear Information System (INIS)

    Bird, J.R.

    1985-01-01

    For some special cases, the use of low energy electrons has advantages over the use of gamma-rays or higher energy electrons for the direct irradiation of food. These advantages arise from details of the interaction processes which are responsible for the production of physical, chemical and biological effects. Factors involved include depth of penetration, dose distribution, irradiation geometry, the possible production of radioactivity and costs

  7. WORKSHOP: Low temperature devices

    International Nuclear Information System (INIS)

    Anon.

    1987-01-01

    With extraterrestrial neutrinos (whether from the sun or further afield) continuing to make science news, and with the search for the so far invisible 'dark matter' of the universe a continual preoccupation, physicists from different walks of life (solid state, low temperature, particles, astrophysics) gathered at a workshop on low temperature devices for the detection of neutrinos and dark matter, held from 12-13 March at Ringberg Castle on Lake Tegernsee in the Bavarian Alps, and organized by the Max Planck Institute for Physics and Astrophysics in Munich

  8. WORKSHOP: Low temperature devices

    Energy Technology Data Exchange (ETDEWEB)

    Anon.

    1987-06-15

    With extraterrestrial neutrinos (whether from the sun or further afield) continuing to make science news, and with the search for the so far invisible 'dark matter' of the universe a continual preoccupation, physicists from different walks of life (solid state, low temperature, particles, astrophysics) gathered at a workshop on low temperature devices for the detection of neutrinos and dark matter, held from 12-13 March at Ringberg Castle on Lake Tegernsee in the Bavarian Alps, and organized by the Max Planck Institute for Physics and Astrophysics in Munich.

  9. Crystalline structure of polypropylene in blends with thermoplastic elastomers after electron beam irradiation

    International Nuclear Information System (INIS)

    Steller, Ryszard; Zuchowska, Danuta; Meissner, Wanda; Paukszta, Dominik; Garbarczyk, Jozef

    2006-01-01

    Isotactic polypropylene (PP) was blended in extruder with 0-50% addition of styrene-ethylene/butylene-styrene (SEBS) and styrene-butadiene-styrene (SBS) block copolymers. Granulated blends were irradiated with electron beam (60 kGy) and 1 week later processed with injection molding machine. Properties of samples molded from irradiated and non-irradiated granulates were investigated using DSC, WAXS, MFR, SEM and mechanical and solubility tests. It was found that the SEBS based systems are more resistant to irradiation in comparison to similar blends with SBS copolymer. Such behavior can be explained by the presence of double bonds in elastic SBS block. Irradiation of PP-SBS blends leads to considerable structure changes of crystalline and amorphous PP phases and elastic SBS phase. It indicates creation of new (inter)phase consisting of products of grafting and cross-linking reactions. Irradiated PP-SBS blends show significant improvement of impact strength at low temperatures

  10. Modeling thermal spike driven reactions at low temperature and application to zirconium carbide radiation damage

    Science.gov (United States)

    Ulmer, Christopher J.; Motta, Arthur T.

    2017-11-01

    The development of TEM-visible damage in materials under irradiation at cryogenic temperatures cannot be explained using classical rate theory modeling with thermally activated reactions since at low temperatures thermal reaction rates are too low. Although point defect mobility approaches zero at low temperature, the thermal spikes induced by displacement cascades enable some atom mobility as it cools. In this work a model is developed to calculate "athermal" reaction rates from the atomic mobility within the irradiation-induced thermal spikes, including both displacement cascades and electronic stopping. The athermal reaction rates are added to a simple rate theory cluster dynamics model to allow for the simulation of microstructure evolution during irradiation at cryogenic temperatures. The rate theory model is applied to in-situ irradiation of ZrC and compares well at cryogenic temperatures. The results show that the addition of the thermal spike model makes it possible to rationalize microstructure evolution in the low temperature regime.

  11. Apparatus for electron beam irradiation of objects

    International Nuclear Information System (INIS)

    Dmitriev, S.P.; Ivanov, A.S.; Sviniin, M.P.; Fedotov, M.T.

    1984-01-01

    This patent provides an apparatus for electron beam irradiation of objects, comprising a shaper of a ribbon-shaped electron beam and a deflecting electromagnet having a frame-type magnetic circuit and used to direct said electron beam onto an irradiated object substantially at an angle of 90 degrees. The deflecting electromagnet has two poles extended over the width of the irradiated object and comprises two windings embracing said poles and connected to a d.c. source. The deflecting electromagnet is arranged in such a manner that the trajectories of the electrons at an area from the shaper to the electromagnet are inclined to the plane of the frame of its magnetic circuit

  12. Self-interstitials and Frenkel pairs in electron-irradiated germanium

    International Nuclear Information System (INIS)

    Carvalho, A.; Jones, R.; Goss, J.; Janke, C.; Coutinho, J.; Oberg, S.; Briddon, P.R.

    2007-01-01

    First principles calculations were used to study the structures and electrical levels of the self-interstitial in Ge. We considered the possibility of structural changes consequent with change in charge state and show these have important implications in the mobility and electrical activity of the defect. The theoretical model is compared to the results of low temperature electron irradiation in germanium reported in the literature

  13. Electron irradiation of dry food products

    International Nuclear Information System (INIS)

    Gruenewald, Th.

    1983-01-01

    The interest of the industrial food producer is increasing in having the irradiation facility installed in the food processing chain. The throughput of the irradiator should be high and the residence time of the product in the facility should be short. These conditions can be accomplished by electron irradiators. To clarify the irradiation conditions spices taken out of the industrial process, food grade salt, sugar, and gums as models of dry food products were irradiated. With a radiation dose of 10 kGy microbial load can be reduced on 10**4 microorganisms/g. The sensory properties of the spices were not changed in an atypical way. For food grade salt and sugar changes of colour were observed which are due to lattice defects or initiated browning. The irradiation of several gums led only in some cases to an improvement of the thickness properties in the application below 50 deg C, in most cases the thickness effect was reduced. The products were packaged before irradiation. But it would be possible also to irradiate the products without packaging moving the product through the irradiation field in a closed conveyor system. (author)

  14. Electron irradiation of dry food products

    Energy Technology Data Exchange (ETDEWEB)

    Gruenewald, Th [Bundesbahn-Zentralamt, Minden (Germany, F.R.)

    1983-01-01

    The interest of the industrial food producer is increasing in having the irradiation facility installed in the food processing chain. The throughput of the irradiator should be high and the residence time of the product in the facility should be short. These conditions can be accomplished by electron irradiators. To clarify the irradiation conditions spices taken out of the industrial process, food grade salt, sugar, and gums as models of dry food products were irradiated. With a radiation dose of 10 kGy microbial load can be reduced on 10**4 microorganisms/g. The sensory properties of the spices were not changed in an atypical way. For food grade salt and sugar changes of colour were observed which are due to lattice defects or initiated browning. The irradiation of several gums led only in some cases to an improvement of the thickness properties in the application below 50 deg C, in most cases the thickness effect was reduced. The products were packaged before irradiation. But it would be possible also to irradiate the products without packaging moving the product through the irradiation field in a closed conveyor system.

  15. Spectroscopy of electron irradiated polymers in electron microscope

    International Nuclear Information System (INIS)

    Faraj, S.H.; Salih, S.M.

    1981-01-01

    The damage induced by energetic electrons in the course of irradiation of polymers in a transmission electron microscope was investigated spectroscopically. Damage on the molecular level has been detected at very low exposure doses. These effects have been induced by electron doses less than that received by the specimen when it is situated at its usual place of the specimen stage in the electron microscope by a factor of 1,000. (author)

  16. Low Temperature (180°C Growth of Smooth Surface Germanium Epilayers on Silicon Substrates Using Electron Cyclotron Resonance Chemical Vapor Deposition

    Directory of Open Access Journals (Sweden)

    Teng-Hsiang Chang

    2014-01-01

    Full Text Available This paper describes a new method to grow thin germanium (Ge epilayers (40 nm on c-Si substrates at a low growth temperature of 180°C using electron cyclotron resonance chemical vapor deposition (ECR-CVD process. The full width at half maximum (FWHM of the Ge (004 in X-ray diffraction pattern and the compressive stain in a Ge epilayer of 683 arcsec and 0.12% can be achieved. Moreover, the Ge/Si interface is observed by transmission electron microscopy to demonstrate the epitaxial growth of Ge on Si and the surface roughness is 0.342 nm. The thin-thickness and smooth surface of Ge epilayer grown on Si in this study is suitable to be a virtual substrate for developing the low cost and high efficiency III-V/Si tandem solar cells in our opinion. Furthermore, the low temperature process can not only decrease costs but can also reduce the restriction of high temperature processes on device manufacturing.

  17. Irradiation of Gemstones using Electron Beam

    International Nuclear Information System (INIS)

    Sarada Idris; Mohd Suhaimi Jusoh; Siti Aiasah Hashim

    2011-01-01

    Gemstone irradiation treatment using radiation is one of the studies conducted in the ALURTRON. The purpose of radiation is to study the effects of radiation on the gems. Through studies conducted on freshwater pearls and stones such as Topaz, Kunzite, TOURMALINE, Aquamarine, Quartz and so on, electron beam irradiation method can highlight the jewel colors but also to reduce the effects of haze on gemstones. The dose of radiation used is 25 kGy to 200 kGy. (author)

  18. Low temperatures - hot topic

    Energy Technology Data Exchange (ETDEWEB)

    Anon.

    1988-09-15

    Neutrino mass measurements, next-generation double beta experiments, solar neutrino detection, searches for magnetic monopoles and the challenge of discovering what most of the Universe is made of (dark matter), not to mention axions (cosmic and solar), supersymmetric neutral particles and cosmic neutrinos. All this physics could use cryogenic techniques. Thus the second European Workshop on Low Temperature Devices for the Detection of Low Energy Neutrinos and Dark Matter, held at LAPP (Annecy) in May, covered an active and promising field.

  19. Low temperatures - hot topic

    International Nuclear Information System (INIS)

    Anon.

    1988-01-01

    Neutrino mass measurements, next-generation double beta experiments, solar neutrino detection, searches for magnetic monopoles and the challenge of discovering what most of the Universe is made of (dark matter), not to mention axions (cosmic and solar), supersymmetric neutral particles and cosmic neutrinos. All this physics could use cryogenic techniques. Thus the second European Workshop on Low Temperature Devices for the Detection of Low Energy Neutrinos and Dark Matter, held at LAPP (Annecy) in May, covered an active and promising field

  20. Low temperature carbonization

    Energy Technology Data Exchange (ETDEWEB)

    Abbott, A A

    1934-01-10

    A process is described in which coal is passed through a distillation chamber in one retort at a comparatively low temperature, then passing the coal through a distillation chamber of a second retort subjected to a higher temperature, thence passing the coal through the distillation chamber of a third retort at a still higher temperature and separately collecting the liquid and vapors produced from each retort.

  1. Sweating at low temperature

    International Nuclear Information System (INIS)

    Chalaye, H.; Launay, J.P.

    1980-11-01

    Tests of penetration liquids normally used between 10 and 40 0 C have shown that the arrangement of operationaal conditions (penetration and revealing times) was not sufficient to maintain their sensitivity below 10 0 C, thereby confirming that this temperature is a limit below which such products cannot be employed. The results achieved with a penetrant and a tracer specially devised for low temperatures (SHERWIN B 305 + D100) are satisfactory between 0 0 C and 15 0 C [fr

  2. MCNPX calculations for electron irradiated semiconductor detectors

    International Nuclear Information System (INIS)

    Sedlackova, K.; Necas, V.; Sagatova, A.; Zatko, B.

    2014-01-01

    This study aimed to treat some practical problems of (not only) semiconductor material irradiation by high energy electron beam using MCNPX simulation code. The relation between the absorbed dose and the fluency was found and the energy distribution of electron flux density was simulated on the top and back side of 270 μm thick GaAs, SiC and Si detectors. Furthermore, the dose depth profiles were calculated for GaAs, SiC and Si materials irradiated by 4 and 5 MeV electron beams. For the GaAs detector, a very good agreement with the experiment was shown. To match the absolute values of the absorbed dose with experimentally obtained values, the electron source emissivity has to be determined in relation to the electron beam setting parameters. (authors)

  3. Formation of novel reactive intermediate by electron-laser dual beam irradiation

    International Nuclear Information System (INIS)

    Ishida, Akito; Takamuku, Setsuo

    1992-01-01

    The pulse radiolysis system of the Institute of Scientific and Industrial Research, Osaka University, (ISIR) has been progressed to observe a highly reactive species, which is produced by successive irradiation of electron and laser or of CW-UV-light and electron. The dual beam irradiation system, which consists of the beam synchronization system, the optical alignment, and the measurement system, is described in detail. Dual beam irradiation studies on 2-methylbenzophenone and some compounds with a C=N bond have been carried out by use of this system. Pulse radiolysis of 2-methylbenzophenone in benzene induced formation of an unstable photoenol via the triplet state, which was irradiated by a visible laser pulse to give dihydroanthrone. Pulse radiolysis of syn-benzalaniline and a nitrileylide in 2-methyltetrahydrofuran, which were produced by steady state photoirradiation at low temperature, enabled us to observe their very unstable radical anions. (author)

  4. Heavy mediums and materials (physics of the condensed state). Study of disordered systems at low temperature. Specific heat measurement in neutron irradiated quartz

    International Nuclear Information System (INIS)

    De Sa, L.

    1987-09-01

    Specific heat of neutron irradiated silicas presents characteristics evolving with radiation dose and is a good way to study properties of disordered systems. Results obtained and comparison with other experiments allow to follow amorphization and defects created by irradiation and raise hypothesis about the evolution of microscopic structure of these materials [fr

  5. Electron-irradiation-induced phase transformation in alumina

    International Nuclear Information System (INIS)

    Chen, C.L.; Arakawa, K.; Lee, J.-G.; Mori, H.

    2010-01-01

    In this study, electron-irradiation-induced phase transformations between alumina polymorphs were investigated by high-resolution transmission electron microscopy. It was found that the electron-irradiation-induced α → κ' phase transformation occurred in the alumina under 100 keV electron irradiation. It is likely that the knock-on collision between incident electrons and Al 3+ cations is responsible for the occurrence of electron-irradiation-induced phase transformation from α-alumina to κ'-alumina.

  6. Electron beam irradiation technology for environmental conservation

    International Nuclear Information System (INIS)

    Tokunaga, Okihiro; Arai, Hidehiko; Hashimoto, Shoji

    1992-01-01

    This paper reviews research and development of application of electron beam (EB) irradiation technology for treatment of flue gas and waste water, and for disinfection of sewage sludge. Feasibility studies on EB purification of flue gases have been performed with pilot-scale experiments in Japan, the USA and Germany, and is being carried out in Poland for flue gases from iron-sintering furnaces or coal burning boilers. Based on results obtained by experiments using simulated flue gas, pilot scale test for treatment of flue gas of low-sulfur containing coal combustion has recently started in Japan. Organic pollutants in waste water and ground water have been found to be decomposed by EB irradiation. Synergetic effect of EB irradiation and ozone addition was found to improve the decomposition efficiency. Electron beam irradiation technology for disinfection of water effluent from water treatment plants was found to avoid formation of chlorinated organic compounds which are formed in using chlorine. Efficient process for composting of sewage sludge disinfected by EB irradiation has been developed by small scale and pilot scale experiments. In the new process, disinfection by EB irradiation and composing can be done separately and optimum temperature for composting can be, therefore, selected to minimize period of composting. (author)

  7. Influence of structural disorder on low-temperature behavior of penetration depth in electron-doped high-TC thin films

    International Nuclear Information System (INIS)

    Lanfredi, A.J.C.; Sergeenkov, S.; Araujo-Moreira, F.M.

    2006-01-01

    To probe the influence of structural disorder on low-temperature behavior of magnetic penetration depth, λ(T), in electron-doped high-T C superconductors, a comparative study of high-quality Pr 1.85 Ce 0.15 CuO 4 (PCCO) and Sm 1.85 Ce 0.15 CuO 4 (SCCO) thin films is presented. The λ(T) profiles are extracted from conductance-voltage data using a highly-sensitive home-made mutual-inductance technique. The obtained results confirm a d-wave pairing mechanism in both samples (with nodal gap parameter Δ 0 /k B T C =2.0 and 2.1 for PCCO and SCCO films, respectively), substantially modified by impurity scattering (which is more noticeable in less homogeneous SCCO films) at the lowest temperatures. More precisely, Δλ(T)=λ(T)-λ(0) is found to follow the Goldenfeld-Hirschfeld interpolation formulae Δλ(T)/λ(0)=AT 2 /(T+T 0 ) with T 0 =ln(2)k B Γ 1/2 Δ 0 1/2 being the crossover temperature which demarcates pure and impure scattering processes (T 0 /T C =0.13 and 0.26 for PCCO and SCCO films, respectively). The value of the extracted impurity scattering rate Γ correlates with the quality of our samples and is found to be much higher in less homogeneous films with lower T C

  8. Low-temperature H2-4He and H2-3He targets for operation on an electron beam

    International Nuclear Information System (INIS)

    Gol'dshtejn, V.A.; Lubyanyj, V.V.

    1981-01-01

    Structures and basic characteristics of H 2 - 4 He and H 2 - 3 He low temperature targets are given. Technique of 3 He target filling is described. Initial target cooling up to liquid 4 He temperature and its filling up take near approximately 1 h, at that 4 He flow rate equals 15 l. Repeated filling up of 4 He takes 20 min, and target filling up with 3 He - 10-15 min. Good thermal insulation of a cryostat and targets permits the 4 He target to be operated with an electron beam of a mean current of up to 0.5 μA without filling up 4 He for 70 h. At that flow rate of liquid 4 He amounts to 0.2 l/h, and liquid hydrogen - 0.04 l/h. It is concluded that H 2 - 4 He and H 2 - 3 He targets are reliable and simple in operation and permit to work with accelerated particle beams of intensity corresponding to power release >= 0.5 W without corrections for density change [ru

  9. Electronic defect study on low temperature processed Cu(In,Ga)Se2 thin-film solar cells and the influence of an Sb layer

    International Nuclear Information System (INIS)

    Van Puyvelde, L; Lauwaert, J; Devulder, W; Detavernier, C; Vrielinck, H; Tempez, A; Nishiwaki, S; Pianezzi, F; Tiwari, A N

    2015-01-01

    A way to lower the manufacturing cost of Cu(In,Ga)Se 2 (CIGS) thin-film solar cells is to use flexible polymer substrates instead of rigid glass. Because such substrates require lower temperature during absorber deposition, the grain growth of the absorber layer can be hindered which leads to a lower cell performance. Partial compensation of this efficiency loss might be accomplished by growing the absorber in the presence of Sb, which is reported to promote grain growth. In this work CIGS solar cells, deposited on glass substrates, at a reduced substrate temperature with a thin Sb layer (7, 12 nm) on top of the Mo contact are investigated. The diffusion profile of Sb is measured with plasma profiling time of flight mass spectrometry. The beneficial effect of Sb on efficiency and grain size is shown in quantum efficiency measurements and with scanning electron microscopy, respectively. Electric spectroscopy is used to explore the possible effects on the defect structure, more in particular on the dominant shallow acceptor. Admittance spectra exhibit a capacitance step to the geometric capacitance plateau at low temperature (5–60 K). Analyzing this capacitance step, we obtained a good estimate of the activation energy of the intrinsic defects that provide the p-type conductivity of the CIGS absorber. The measurements did not show a change in the nature of the dominant acceptor upon Sb treatment. (paper)

  10. AECL IMPELA electron beam industrial irradiators

    International Nuclear Information System (INIS)

    Labrie, J.P.; Drewell, N.H.; Ebrahim, N.A.; Lawrence, C.B.; Mason, V.A.; Ungrin, J.; White, B.F.

    1989-01-01

    A family of industrial irradiators is being developed by AECL to cover an electron-beam energy range from 5 to 18 MeV at beam powers between 20 and 250 kW. The IMPELA family of irradiators is designed for push button, reliable operation. The major irradiator components are modular, allowing for later upgrades to meet increased demands in either electron or X-ray mode. Interface between the control system, irradiator availability and dose quality assurance is in conformance with the most demanding specifications. The IMPELA irradiators use a klystron-driven, standing-wave, L-band accelerator structure with direct injection from a rugged, triode electron gun. Direct control of the accelerating field during the beam pulse ensures constant output beam energy, independent of beam power. The first member of the family, the IMPELA 10/50 (10 MeV, 50 kW), is in the final stages of assembly at Chalk River Nuclear Laboratories. The IMPELA 10/50 is constructed around a 3.25 m long, high-power-capacity accelerator structure operated at a duty factor of 5%. Beam loading exceeds 60%. The rf power is provided by a 2 MW/150 kW modulated-anode klystron protected from load mismatches by a circulator. This prototype will be used to demonstrate the reliability and dose uniformity targets of the IMPELA family. Full beam operation of the IMPELA 10/50 is scheduled for early 1989. (orig.)

  11. Preparation of anatase TiO{sub 2} thin film by low temperature annealing as an electron transport layer in inverted polymer solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Noh, Hongche [Department of Chemical Engineering, Hanyang University, Seoul 133-791 (Korea, Republic of); Oh, Seong-Geun, E-mail: seongoh@hanyang.ac.kr [Department of Chemical Engineering, Hanyang University, Seoul 133-791 (Korea, Republic of); Im, Seung Soon, E-mail: imss007@hanyang.ac.kr [Department of Organic and Nano Engineering, Hanyang University, Seoul 133-791 (Korea, Republic of)

    2015-04-01

    Highlights: • Anatase thin film of TiO{sub 2} was prepared by low temperature annealing. • Anatase TiO{sub 2} colloidal solution was obtained from amorphous form through solvothermal process. • Anatase TiO{sub 2} colloidal solution was used to prepare thin film on ITO glass. • Polymer solar cell fabricated on anatase TiO{sub 2} thin film showed 2.6% of PCE. - Abstract: To prepare the anatase TiO{sub 2} thin films on ITO glass, amorphous TiO{sub 2} colloidal solution was synthesized through the simple sol-gel method by using titanium (IV) isopropoxide as a precursor. This amorphous TiO{sub 2} colloidal solution was spread on ITO glass by spin-coating, then treated at 450 °C to obtain anatase TiO{sub 2} film (for device A). For other TiO{sub 2} films, amorphous TiO{sub 2} colloidal solution was treated through solvothermal process at 180 °C to obtain anatase TiO{sub 2} colloidal solution. This anatase TiO{sub 2} colloidal solution was spread on ITO glass by spin coating, and then annealed at 200 °C (for device B) and 130 °C (for device C), respectively. The average particle size of amorphous TiO{sub 2} colloidal solution was about 1.0 nm and that of anatase TiO{sub 2} colloidal solution was 10 nm. The thickness of TiO{sub 2} films was about 15 nm for all cases. When inverted polymer solar cells were fabricated by using these TiO{sub 2} films as an electron transport layer, the device C showed the highest PCE (2.6%) due to the lack of defect, uniformness and high light absorbance of TiO{sub 2} films. The result of this study can be applied for the preparation of inverted polymer solar cell using TiO{sub 2} films as a buffer layer at low temperature on plastic substrate by roll-to roll process.

  12. Low temperature destructive distillation

    Energy Technology Data Exchange (ETDEWEB)

    1938-07-05

    A process is given and apparatus is described for the destructive distillation at low temperature of coal, oil shale, and the like by subjection to the action of a stream of hot gases or superhearted steam, flowing in a closed circuit. Subsequent treatment of the distillation residues with a gas stream containing oxygen results in combustion of the carbon-containing material therein brings to a high temperature the solid residue, in which the process comprises subsequently contacting the hot solid residue with the fluid stream effecting the distillation.

  13. User Support of Electron Irradiation Facility

    International Nuclear Information System (INIS)

    Park, S. H.; Cha, H. K.; Lee, B. C.

    2007-06-01

    The KAERI (Korean Atomic Energy Research Institute) high-power electron beam irradiation facility, operating at the energies between 0.3 MeV and 10 MeV,has provided irradiation services to users in industries, universities, and institutes via 'Project of utilization and cooperation of users of a large research facility' since 2004. A great attraction of many researchers, almost 750 persons so far according to surveys, to e-beam irradiation technology as well as the growth of participants on Workshop on Electron Beam Applications from 121 to 176 indicate the increase of demands of irradiation service. Comparing to the cases of advanced nations in this area, such as America, Japan, China, and Russia, Korea is relatively much behind in radiation technology. It is mainly due to the lack of governmental supports and investments. Active support and investment on construction and operation of electron beam user facilities would be principal factors on developments of advanced technologies. In this project, we would like to satisfy users' requests by developing the effective managing and operating system for prompt services, processes, and QA and to ultimately assist users to create additional new results, by maximizing the utilization of all available resources and activating the developments of technologies of electron beam processing

  14. Low temperature distillation

    Energy Technology Data Exchange (ETDEWEB)

    Vandegrift, J N; Postel, C

    1929-04-09

    To recover gas, oil tars, and coked residues by low temperature distillation from bituminous coals, lignites, oil shales, and the like, the raw material is fed from a hopper into a rotary retort which is zonally heated, the temperature being greatest at the discharge end. The material is heated first to a relatively low temperature, thereby removing the moisture and lighter volatiles which are withdrawn through a pipe by the suction of a pump, while the higher boiling point volatiles and fixed gases are withdrawn by suction through an outlet from the higher temperature zone. The vapors withdrawn from the opposite ends of the retort pass through separate vapor lines and condensers, and the suction in each end of the retort, caused by the pumps, is controlled by valves, which also control the location of the neutral point in the retort formed by said suction. Air and inert gas may be introduced into the retort from pipe and stack respectively through a pipe, and steam may be admitted into the high temperature zone through a pipe.

  15. Low-temperature carbonization

    Energy Technology Data Exchange (ETDEWEB)

    Strankmuller, J

    1954-01-01

    The low-temperature carbonization plant at Boehlen in Eastern Germany (the first in which Lurgi type ovens were installed) worked with a throughput of 300 tons of brown-coal briquets per day per oven since 1936, later increased to 365 tons per day. The rising demand for low-temperature tar for hydrogenation purposes led to development of a modified oven of 450 tons throughput. This was achieved by stepping up the flow of the circulating gas and air mixture from 420,000 to 560,000 cubic feet per hour and by additional rows of V-shaped deflectors across the width of the oven chamber, which break up and loosen the charge, thus reducing cooling-gas pressure and allowing a greater flow of scavenging gas. The distance traversed by each briquet is nearly doubled, and the temperature gradient is less. It is claimed that the tar and the coke from modified ovens are of comparable quality. The compressive strength of the briquets was found to have an appreciable effect on the output. Better qts the chemistry, mechanism and thermodynamics of the Fischer-Tropsch reaction and aectromagnetic radiation.

  16. Cold priming drives the sub-cellular antioxidant systems to protect photosynthetic electron transport against subsequent low temperature stress in winter wheat

    DEFF Research Database (Denmark)

    Li, Xiangnan; Cai, Jian; Liu, Fulai

    2014-01-01

    Low temperature seriously depresses the growth of wheat through inhibition of photosynthesis, while earlier cold priming may enhance the tolerance of plants to subsequent low temperature stress. Here, winter wheat plants were firstly cold primed (5.2°C lower temperature than the ambient temperatu......-cellular antioxidant systems, depressing the oxidative burst in photosynthetic apparatus, hereby enhanced the tolerance to subsequent low temperature stress in winter wheat plants.......Low temperature seriously depresses the growth of wheat through inhibition of photosynthesis, while earlier cold priming may enhance the tolerance of plants to subsequent low temperature stress. Here, winter wheat plants were firstly cold primed (5.2°C lower temperature than the ambient temperature......, viz., 10.0°C) at the Zadoks growth stage 28 (i.e.re-greening stage, starting on 20th of March) for 7d, and after 14d of recovery the plants were subsequently subjected to a 5d low temperature stress (8.4°C lower than the ambient temperature, viz., 14.1°C) at the Zadoks growth stage 31 (i...

  17. Electron spin resonance study of radicals in irradiated polyethylene

    International Nuclear Information System (INIS)

    Fujimura, Takashi

    1979-02-01

    In order to elucidate radiation effect in polyethylene, the nature and behavior of radicals produced in polyethylene and the model compound of polyethylene irradiated at 77 0 K were studied by using electron spin resonance. The structure of radical pairs, which are composed of two radicals produced very closely each other, was investigated in drawn polyethylene and the single crystal of n-eicosane. The radical pairs of intrachain type and interchain type were found in polyethylene and n-eicosane respectively. It was suggested that these two types of radical pairs are the precursors of double bonds and crosslinks respectively. The thermal decay reactions of radicals themselves produced in irradiated polyethylene were investigated. It was made clear that the short range distances between two radicals play an important role in the decay reaction of alkyl radicals at low temperatures. The trapping regions of radicals were studied and it was clarified that allyl radicals, which are produced by the reaction of alkyl radicals with double bonds, are trapped both in the crystalline and non-crystalline regions. (author)

  18. Thermal conductivity of electron-irradiated graphene

    Science.gov (United States)

    Weerasinghe, Asanka; Ramasubramaniam, Ashwin; Maroudas, Dimitrios

    2017-10-01

    We report results of a systematic analysis of thermal transport in electron-irradiated, including irradiation-induced amorphous, graphene sheets based on nonequilibrium molecular-dynamics simulations. We focus on the dependence of the thermal conductivity, k, of the irradiated graphene sheets on the inserted irradiation defect density, c, as well as the extent of defect passivation with hydrogen atoms. While the thermal conductivity of irradiated graphene decreases precipitously from that of pristine graphene, k0, upon introducing a low vacancy concentration, c reduction of the thermal conductivity with the increasing vacancy concentration exhibits a weaker dependence on c until the amorphization threshold. Beyond the onset of amorphization, the dependence of thermal conductivity on the vacancy concentration becomes significantly weaker, and k practically reaches a plateau value. Throughout the range of c and at all hydrogenation levels examined, the correlation k = k0(1 + αc)-1 gives an excellent description of the simulation results. The value of the coefficient α captures the overall strength of the numerous phonon scattering centers in the irradiated graphene sheets, which include monovacancies, vacancy clusters, carbon ring reconstructions, disorder, and a rough nonplanar sheet morphology. Hydrogen passivation increases the value of α, but the effect becomes very minor beyond the amorphization threshold.

  19. Polymeric materials obtained by electron beam irradiation

    International Nuclear Information System (INIS)

    Dragusin, M.; Moraru, R.; Martin, D.; Radoiu, M.; Marghitu, S.; Oproiu, C.

    1995-01-01

    Research activities in the field of electron beam irradiation of monomer aqueous solution to produce polymeric materials used for waste waters treatment, agriculture and medicine are presented. The technologies and special features of these polymeric materials are also described. The influence of the chemical composition of the solution to ba irradiated, absorbed dose level and absorbed dose rate level are discussed. Two kinds of polyelectrolytes, PA and PV types and three kinds of hydrogels, pAAm, pAAmNa and pNaAc types, the production of which was first developed with IETI-10000 Co-60 source and then adapted to the linacs built in Accelerator Laboratory, are described. (author)

  20. Survival of plant tissue at super-low temperatures v. An electron microscope study of ice in cortical cells cooled rapidly.

    Science.gov (United States)

    Sakai, A; Otsuka, K

    1967-12-01

    Experiments were carried out with cortical cells in twig bark of mulberry trees in winter in order to clarify the mechanism of survival at super-low temperatures with rapid cooling and rewarming. Attention was given to the relation between the existence of intracellular ice crystals and survival.Cortical cells were cooled rapidly by direct immersion into liquid nitrogen or isopentane cooled at various temperatures. After immersion, they were freeze-substituted with absolute ethanol at -78 degrees . They were then embedded, sectioned and examined under the electron microscope for the presence and distribution of cavities left after ice removal.Cells were found to remain alive and contain no ice cavities when immersed rapidly into isopentane baths kept below -60 degrees . Those cells at intermediate temperatures from -20 degrees to -45 degrees , were almost all destroyed. It was also observed that many ice cavities were contained in the cells immersed rapidly into isopentane baths at -30 degrees . The data seem to indicate that no ice crystals were formed when cooled rapidly by direct immersion into isopentane baths below -60 degrees or into liquid nitrogen.The tissue sections immersed in liquid nitrogen were rapidly transferred to isopentane baths at temperatures ranging from -70 degrees to -10 degrees before rapid rewarming. There was little damage when samples were held at temperatures below -50 degrees for 10 minutes or below -60 degrees for 16 hours. No cavities were found in these cells. Above -45 degrees , and especially at -30 degrees , however, all cells were completely destroyed even when exposed only for 1 minute. Many ice cavities were observed throughout these cells. The results obtained may be explained in terms of the growth rate of intracellular ice crystals.

  1. Positron lifetime studies of electron irradiated copper

    International Nuclear Information System (INIS)

    Hadnagy, T.D.

    1976-01-01

    Single-crystal copper was irradiated with 4.5-MeV electrons producing simple Frenkel defects as well as a significant concentration of divacancies. Mean positron lifetime characteristics, which are sensitive to the presence of vacancies and multivacancies in copper, was monitored after isochronal anneals between 80 and 800 0 K to determine the relative change of characteristic mean lifetimes and their associated intensities. Also a study of the dependence of the mean positron lifetime on the total electron fluence was made and compared with existing theories relating these lifetimes to vacancy or multivacancy concentrations. Numerical data from curve fitting procedures using a conventional trapping model for defect-induced changes in positron lifetimes indicate that upon irradiation with 4.5-MeV electrons at 80 0 K, about 8 percent of the defects produced are divacancy units. Divacancy units appear to be several times more effective in trapping positrons than are monovacancies. Further, the experimental data suggest that the stage III annealing processes in electron-irradiated copper most probably involve the motion and removal of both monovacancies and divacancies. A conglomerate (multivacancy) unit appears to exist as a stable entity even after annealing procedures are carried out at temperatures slightly above the stage III region. Such a stable unit could serve as a nucleation center for the appearance of voids

  2. Effect of low-temperature storage, gamma irradiation and iso-propyl-N-(3-chlorophenyl carbamate) treatment on the processing quality of potatoes

    International Nuclear Information System (INIS)

    Liu, M.S.; Chen, R.Y.; Tsai, M.J.

    1990-01-01

    In Taiwan commercial storage of potatoes (CV Kennebec, Wu-Foon, Cardinal) at 2°C. 85% RH, can supply the fresh market all year round. However, reducing sugar and total sugar which accumulate in the tubers will reduce the processing quality of potatoes. Reconditioning of tubers from cold stores was undertaken at ambient temperature (20°C) for up to 6 weeks. The optimum temperature for Kennebec and Cardinal reconditioning ranged from 20 to 25°C. However, after storage at 2°C for a long period, the sugar content of potato tubers cannot be reduced to a satisfactory level. When newly harvested potatoes were pretreated with CIPC (300–500 μg litre −1 ) and stored at 10°C, 80 % RH, sprouting was inhibited effectively. The quality of potatoes was retained well and reducing sugar remained at a low level for up to 8 months. MENA was found to be ineffective. Gamma irradiation of potatoes at 0.175-0 20·0-10–0.125 and 0.125 kGy for Cardinal, Kennebec and Wu-Foon respectively was found to be effective in controlling the sprouting of tubers stored at 10°C, 80 % RH, for 9 months. A rapid increase in sugar content was found in irradiated Cardinal and Wu-Foon after storage for 7 months, while the reducing sugar in irradiated Kennebec was still below 0°2 % after 8 month's storage. Gamma irradiation had no adverse effect on the ascorbic acid content, and higher firmness retention was obtained in irradiated tubers throughout storage at 10°C

  3. Stress relaxation under cyclic electron irradiation

    International Nuclear Information System (INIS)

    Bystrov, L.N.; Reznitskij, M.E.

    1990-01-01

    The kinetics of deformation process in a relaxating sample under 2 MeV electron cyclic irradiation was studied experimentally. The Al-Mg alloys with controllable and different (in dislocation density precipitate presence and their character) structure were used in experiments. It was established that after the beam was switched on the deformation rate increased sharply and then, during prolonged irradiation, in a gradual manner. After the switching-off the relaxation rate decreases by jumps up to values close to extrapolated rates of pre-radiation relaxation. The exhibition of these effects with radiation switching-off and switchin-on is dependent on the initial rate of thermal relaxation, the test temperature, the preliminary cold deformation and the dominating deformation dislocation mechanism. The preliminary cold deformation and test temperature elevation slightly decrease the effect of instantaneous relaxation acceleration with the irradiation switch-on. 17 refs., 5 figs

  4. Radiation stability of low-temperature resistance thermometers

    International Nuclear Information System (INIS)

    Neklyudov, I.M.; Petrusenko, Yu.T.; Sleptsov, A.N.; Logvinenko, S.P.; Mikhina, G.F.; Rossoshanskij, O.A.

    1989-01-01

    The effect of low temperature (∼ 5 and 11 K) irradiation with E=30 MeV electrons and the subsequent annealing at 180 and 300 K on gauge dependences R(T) of resistance thermometers (RT) on the basis of p-GaAs, Ni and In is investigated. For GaAs-RT the dependence of electroresistance R(4.2 K) on the irradiation fluence is shown to be non monotonic. The annealing at 180 and 300 K does not restore GaAs-RT thermometric characteristics but it leads to their further degradation. The annealing of Ni and In irradiated RT's at T>180 K leads to total restoring of their electrophysical properties. 16 refs.; 5 figs.; 1 tab

  5. Electrical conductivity of In2O3 and Ga2O3 after low temperature ion irradiation; implications for instrinsic defect formation and charge neutrality level.

    Science.gov (United States)

    Vines, L; Bhoodoo, C; von Wenckstern, H; Grundmann, M

    2017-12-13

    The evolution of sheet resistance of n-type In 2 O 3 and Ga 2 O 3 exposed to bombardment with MeV 12 C and 28 Si ions at 35 K is studied in situ. While the sheet resistance of Ga 2 O 3 increased by more than eight orders of magnitude as a result of ion irradiation, In 2 O 3 showed a more complex defect evolution and became more conductive when irradiated at the highest doses. Heating up to room temperature reduced the sheet resistivity somewhat, but Ga 2 O 3 remained highly resistive, while In 2 O 3 showed a lower resistance than as deposited samples. Thermal admittance spectroscopy and deep level transient spectroscopy did not reveal new defect levels for irradiation up to [Formula: see text] cm -2 . A model where larger defect complexes preferentially produce donor like defects in In 2 O 3 is proposed, and may reveal a microscopic view of a charge neutrality level within the conduction band, as previously proposed.

  6. Electrical conductivity of In2O3 and Ga2O3 after low temperature ion irradiation; implications for instrinsic defect formation and charge neutrality level

    Science.gov (United States)

    Vines, L.; Bhoodoo, C.; von Wenckstern, H.; Grundmann, M.

    2018-01-01

    The evolution of sheet resistance of n-type In2O3 and Ga2O3 exposed to bombardment with MeV 12C and 28Si ions at 35 K is studied in situ. While the sheet resistance of Ga2O3 increased by more than eight orders of magnitude as a result of ion irradiation, In2O3 showed a more complex defect evolution and became more conductive when irradiated at the highest doses. Heating up to room temperature reduced the sheet resistivity somewhat, but Ga2O3 remained highly resistive, while In2O3 showed a lower resistance than as deposited samples. Thermal admittance spectroscopy and deep level transient spectroscopy did not reveal new defect levels for irradiation up to 2 × 1012 cm-2. A model where larger defect complexes preferentially produce donor like defects in In2O3 is proposed, and may reveal a microscopic view of a charge neutrality level within the conduction band, as previously proposed.

  7. Low Temperature Plasma Medicine

    Science.gov (United States)

    Graves, David

    2013-10-01

    Ionized gas plasmas near room temperature are used in a remarkable number of technological applications mainly because they are extraordinarily efficient at exploiting electrical power for useful chemical and material transformations near room temperature. In this tutorial address, I will focus on the newest area of low temperature ionized gas plasmas (LTP), in this case operating under atmospheric pressure conditions, in which the temperature-sensitive material is living tissue. LTP research directed towards biomedical applications such as sterilization, surgery, wound healing and anti-cancer therapy has seen remarkable growth in the last 3-5 years, but the mechanisms responsible for the biomedical effects have remained mysterious. It is known that LTP readily create reactive oxygen species (ROS) and reactive nitrogen species (RNS). ROS and RNS (or RONS), in addition to a suite of other radical and non-radical reactive species, are essential actors in an important sub-field of aerobic biology termed ``redox'' (or oxidation-reduction) biology. I will review the evidence suggesting that RONS generated by plasmas are responsible for their observed therapeutic effects. Other possible bio-active mechanisms include electric fields, charges and photons. It is common in LTP applications that synergies between different mechanisms can play a role and I will review the evidence for synergies in plasma biomedicine. Finally, I will address the challenges and opportunities for plasma physicists to enter this novel, multidisciplinary field.

  8. Low-Temperature Supercapacitors

    Science.gov (United States)

    Brandon, Erik J.; West, William C.; Smart, Marshall C.

    2008-01-01

    An effort to extend the low-temperature operational limit of supercapacitors is currently underway. At present, commercially available non-aqueous supercapacitors are rated for a minimum operating temperature of -40 C. A capability to operate at lower temperatures would be desirable for delivering power to systems that must operate in outer space or in the Polar Regions on Earth. Supercapacitors (also known as double-layer or electrochemical capacitors) offer a high power density (>1,000 W/kg) and moderate energy density (about 5 to 10 Wh/kg) technology for storing energy and delivering power. This combination of properties enables delivery of large currents for pulsed applications, or alternatively, smaller currents for low duty cycle applications. The mechanism of storage of electric charge in a supercapacitor -- at the electrical double-layer formed at a solid-electrode/liquid-electrolyte interface -- differs from that of a primary or secondary electrochemical cell (i.e., a battery) in such a manner as to impart a long cycle life (typically >10(exp 6) charge/discharge cycles).

  9. Exhaust gas treatment by electron beam irradiation

    International Nuclear Information System (INIS)

    Shibamura, Yokichi; Suda, Shoichi; Kobayashi, Toshiki

    1991-01-01

    Among global environmental problems, atmospheric pollution has been discussed since relatively old days, and various countermeasures have been taken, but recently in connection with acid rain, the efficient and economical treatment technology is demanded. As the denitration and desulfurization technology for the exhaust gas from the combustion of fossil fuel, the incineration of city trash and internal combustion engines, three is the treatment method by electron beam irradiation. By irradiating electron beam to exhaust gas, nitrogen oxides and sulfur oxides are oxidized to nitric acid and sulfuric acid, and by promoting the neutralization of these acids with injected alkali, harmless salts are recovered. This method has the merit that nitrogen oxides and surfur oxides can be removed efficiently with a single system. In this report, as for the exhaust gas treatment by electron beam irradiation, its principle, features, and the present status of research and development are described, and in particular, the research on the recent exhaust gas treatment in city trash incineration is introduced. This treatment method is a dry process, accordingly, waste water disposal is unnecessary. The reaction products are utilized as fertilizer, and waste is not produced. (K.I.)

  10. Electron irradiation effects on lithium peroxide

    Science.gov (United States)

    Kikkawa, Jun; Shiotsuki, Taishi; Shimo, Yusuke; Koshiya, Shogo; Nagai, Takuro; Nito, Takehiro; Kimoto, Koji

    2018-03-01

    In this study, electron irradiation effects on lithium peroxide (Li2O2), which is an important discharge product of Li-air (or Li-O2) batteries, were investigated using selected-area electron diffraction (SAED) and high-energy resolution electron energy-loss spectroscopy (EELS). The results obtained show that Li2O2 to Li2O transformation occurs with 80 and 300 keV incident electrons under high electron dose rates at 20 and -183 °C. The Li2O2 to Li2O transformation rate for 300 keV was 1/5 of that for 80 keV with the irradiation taking place at -183 °C. We also present a series of the EELS spectra that can be used as a criterion to judge the molar ratio of Li2O to Li2O2 in the general systems where Li2O2 and Li2O coexist.

  11. A NEXAFS and mass spectrometry study of cysteine, cystine and insulin irradiated with intermediate energy (0.8 keV) electrons

    Energy Technology Data Exchange (ETDEWEB)

    Simões, G., E-mail: simoes.grazieli@gmail.com [Instituto de Química, Universidade Federal do Rio de Janeiro, Cidade Universitária, 21941-909 Rio de Janeiro (Brazil); Rodrigues, F.N. [Instituto de Química, Universidade Federal do Rio de Janeiro, Cidade Universitária, 21941-909 Rio de Janeiro (Brazil); Instituto Federal de Educação, Ciência e Tecnologia do Rio de Janeiro, Maracanã, 20270-021 Rio de Janeiro (Brazil); Bernini, R.B. [Instituto de Química, Universidade Federal do Rio de Janeiro, Cidade Universitária, 21941-909 Rio de Janeiro (Brazil); Instituto Federal de Educação, Ciência e Tecnologia do Rio de Janeiro, Duque de Caxias, 25050-100 Rio de Janeiro (Brazil); Castro, C.S.C. [Instituto Nacional de Metrologia, Qualidade e Tecnologia – Inmetro, 25250-020 Rio de Janeiro (Brazil); Souza, G.G.B. de, E-mail: gerson@iq.ufrj.br [Instituto de Química, Universidade Federal do Rio de Janeiro, Cidade Universitária, 21941-909 Rio de Janeiro (Brazil)

    2014-03-01

    Highlights: • Structural modifications in sulfur containing biomolecules were investigated. • Significant modifications were observed in insulin irradiated NEXAFS spectra. • Degradation of insulin can be observed even at low temperature. • Alterations in insulin spectrum were characterized according to the state of sulfur. - Abstract: We have performed a NEXAFS (S 1s) and mass spectrometry study of solid samples of cysteine, cystine and insulin irradiated with 0.8 keV electrons. The measured mass spectra point out to processes of desulfurization, deamination, decarbonylation and decarboxylation in the irradiated biomolecules. Electron beam irradiation was also conducted at low temperatures in order to evaluate the possible contribution from thermal degradation processes. The NEXAFS spectra of irradiated cysteine and cystine did not show substantial changes when compared to the same spectra obtained using non-irradiated samples. The sulfur K-edge photoabsorption spectrum of irradiated insulin, however, showed clear modifications when compared to the spectrum of the non-irradiated protein, even when the irradiation was conducted at low temperature. Using an empirical combination of the photoabsorption spectra of cysteine and cystine (which are associated respectively with reduced and oxidized forms of sulfur) we have been able to reproduce the absorption spectrum of irradiated insulin.

  12. Kinetics and spectroscopy of low temperature plasmas

    CERN Document Server

    Loureiro, Jorge

    2016-01-01

    This is a comprehensive textbook designed for graduate and advanced undergraduate students. Both authors rely on more than 20 years of teaching experience in renowned Physics Engineering courses to write this book addressing the students’ needs. Kinetics and Spectroscopy of Low Temperature Plasmas derives in a full self-consistent way the electron kinetic theory used to describe low temperature plasmas created in the laboratory with an electrical discharge, and presents the main optical spectroscopic diagnostics used to characterize such plasmas. The chapters with the theoretical contents make use of a deductive approach in which the electron kinetic theory applied to plasmas with basis on the electron Boltzmann equation is derived from the basic concepts of Statistical and Plasma Physics. On the other hand, the main optical spectroscopy diagnostics used to characterize experimentally such plasmas are presented and justified from the point of view of the Atomic and Molecular Physics. Low temperature plasmas...

  13. Use of electron accelerators in food irradiation

    International Nuclear Information System (INIS)

    Sanyal, Bhaskar

    2013-01-01

    Preservation of food by ionizing radiations involves controlled application of energy of radiation to agricultural commodities, foods and food ingredients, for improving storage life, hygiene and safety. Insects and microbes cause major economic losses to stored crops. Many of our food products are contaminated with diseases causing germs and toxin producing molds. Without improvement in microbial quality and getting properly treated to overcome quarantine barriers our agricultural products cannot get international markets. In this respect electron accelerators have immense potential in commercial radiation processing of foods. Both low and high dose applications with increased process rates can be achieved using accelerators to cover a wide spectrum of food commodities approved for commercial radiation processing as per the recent gazette notification under Atomic Energy (Radiation Processing of Food and Allied Products) Rule, 2012. The effectiveness of processing of food by ionizing radiation depends on proper delivery of absorbed dose and its reliable measurement. For food destined for international trade, it is important that the dosimetry used for dose determination is carried out accurately and that the process is monitored in accordance with the internationally accepted procedures. Experiments using alanine-EPR system were carried out to optimize the process parameters of 10 MeV electron beam for commercial irradiation of food. Different food commodities namely, mango, potato and rawa (semolina) were irradiated to measure the absorbed dose distribution. The actual depth dose profile in food products and useful scan width of the electron beam were determined for commercial radiation processing of food using electron beam. (author)

  14. Determination of the electron beam irradiated area

    International Nuclear Information System (INIS)

    Zarbout, K.; Kallel, A.; Moya, G.

    2005-01-01

    The investigation of the charge trapping properties of non-conductive materials open the way to an understanding of the degradation of their characteristics due to ageing and catastrophic phenomena, such as breakdown, which originate from the rapid relaxation of trapped charges. The defects, in particular those introduced during the fabrication process, are responsible for the charging phenomena which limit the technological performances and the reliability of these materials. Several characterisation techniques have been developed and among them the one which uses the electron beam of the scanning Electron Microscope (SEM). The study of the charge trapping properties in non-conductive solids by using the electron beam of a SEM requires the knowledge of the current beam and injected charges densities. These densities depend on the irradiated sample area. For this reason, we report in this work two experimental procedures allowing a direct determination of the irradiated area size by the incident defocused beam. The first is based on the charging effect of oxide surfaces (SiO2, MgO, AL2O3) and the second is derived from the electron beam lithography technique. The latter procedure constitutes a convenient experimental method

  15. Commercializing ALURTRONs electron beam irradiation services

    International Nuclear Information System (INIS)

    Siti Aiasah Hashim; Mohd Sidek Othman; Shari Jahar; Sarada Idris; Naurah Mohd Isa; Muhamad Zahidee Taat

    2010-01-01

    ALURTRON has been the nation's sole electron irradiation service provider for research sectors. The main irradiation is done by utilising the EPS 3000 Cockcroft-Walton type 3.0 MeV, 90 k Watts electron beam machine (EBM). With more than 15 years experience in the operation and maintenance of the EPS, the challenge is now to commercialize the service at a larger and profitable scale. Medical products sterilization at commercial level has been ruled out since the energy is insufficient to penetrate dense and non-homogenous items. Recently, the demand for irradiation of wire and heat shrinkable tubes is showing bigger commercial potential. Therefore, prudent planning considerations need to be taken to ensure profitable return to the agency. Calculations were made to estimate ALURTRON service capacity, based on the existing EBM and its auxiliary systems. Details of the calculation including all the variables are presented. Results indicated that Alurtron should be able to process a minimum of 1000 km of small wires per month, running at 150 m/ min, working in two shifts, 5 days a week. The projected revenue is dependent on the charges imposed on the basis of total length delivered. (author)

  16. A study of point defects created by electron irradiation of dilute iron-carbon alloys

    International Nuclear Information System (INIS)

    Leveque, J.L.

    1969-10-01

    Resistivity and magnetic after effect (m.a.e.) measurements are used to study the influence of carbon atoms on the annealing process of point defects created by electron irradiation (3 MeV) at low temperature (20 deg. K). The presence of the carbon atoms has a strong influence on the recovery sub-stage I E and stage III. For the former, the carbon impurity traps the freely migrating iron interstitial. For the latter the effect is interpreted as being due to formation during annealing, of a carbon vacancy pair. A pronounced m.a.e. band is attributed to the reorientation of this carbon vacancy complex. All these results are coherent with the interpretation of a low temperature migrating free interstitial. (author) [fr

  17. Electron irradiation experiments in support of fusion materials development

    International Nuclear Information System (INIS)

    Gelles, D.S.; Ohnuki, S.; Takahashi, H.; Matsui, H.; Kohno, Y.

    1991-11-01

    Microstructural evolution in response to 1 MeV irradiation has been investigated for three simple ferritic alloys, pure beryllium, pure vanadium, and two simple vanadium alloys over a range of temperatures and doses. Microstructural evolution in Fe-3, -9, and -18Cr ferritic alloys is found to consist of crenulated, faulted a loops and circular, unfaulted a/2 loops at low temperatures, but with only unfaulted loops at high temperatures. The complex dislocation evolution is attributed to sigma phase precipifaults arising from chromium segregation to point defect sinks. Beryllium is found to be resistant to electron damage; the only effect observed was enhanced dislocation mobility. Pure vanadium, V-5Fe, and V-1Ni microstructural response was complicated by precipitation on heating to 400 degrees C and above, but dislocation evolution was investigated in the range of room temperature to 300 degrees C and at 600 degrees C. The three materials behaved similarly, except that pure vanadium showed more rapid dislocation evolution. This difference does not explain the enhanced swelling observed in vanadium alloys

  18. WEBEXPIR: Windowless target electron beam experimental irradiation

    International Nuclear Information System (INIS)

    Dierckx, Marc; Schuurmans, Paul; Heyse, Jan; Rosseel, Kris; Tichelen, Katrien Van; Nactergal, Benoit; Vandeplassche, Dirk; Aoust, Thierry; Abs, Michel; Guertin, Arnaud; Buhour, Jean-Michel; Cadiou, Arnaud; Abderrahim, Hamid Ait

    2008-01-01

    The windowless target electron beam experimental irradiation (WEBEXPIR) program was set-up as part of the MYRRHA/XT-ADS R and D effort on the spallation target design to investigate the interaction of a proton beam with a liquid lead-bismuth eutectic (LBE) free surface. In particular, possible free surface distortion or shockwave effects in nominal conditions and during sudden beam on/off transient situations, as well as possible enhanced evaporation were assessed. An experiment was conceived at the IBA TT-1000 Rhodotron, where a 7 MeV electron beam was used to simulate the high power deposition at the MYRRHA/XT-ADS LBE free surface. The geometry and the LBE flow characteristics in the WEBEXPIR set-up were made as representative as possible of the actual situation in the MYRRHA/XT-ADS spallation target. Irradiation experiments were carried out at beam currents of up to 10 mA, corresponding to 40 times the nominal beam current necessary to reproduce the MYRRHA/XT-ADS conditions. Preliminary analyses show that the WEBEXPIR free surface flow was not disturbed by the interaction with the electron beam and that vacuum conditions stayed well within the design specifications

  19. Electron spin resonance and optical studies on the radiolysis of carbon tetrachloride. II. Structure and reaction of CClṡ-4 radical anion in tetramethylsilane low-temperature solids

    Science.gov (United States)

    Muto, Hachizo; Nunome, Keichi

    1991-04-01

    An electron spin resonance (ESR) and optical study of carbon tetrachloride radical anion has been made to provide for a better understanding of the radiolysis of CCl4, following CClṡ+4 cation previously studied. It was found that the anion was metastably trapped in tetramethylsilane (TMS) matrices γ irradiated at 4 or 77 K. The g tensor and the hyperfine coupling tensors of all atoms of the radical were determined from ESR spectral simulation by using 12 CCl4 and the 13C enriched compound: g∥=2.004-5, g1=2.015,(A∥,A⊥) =(24.3,18.3) mT for 13C, (0.9, 0.2) mT for one 35Cl atom, and (A1,A2=A3)=(1.98,0.45) mT for the other three equivalent 35Cl atoms. From these parameters and a consideration on the g anisotropy combined with the optical data, the anion was found to have a predissociating molecular structure (CCl3ṡṡṡCl) ˙- with C3v symmetry, where the unpaired electron occupies A*1γ antibonding orbital. The carbon atom has a large spin density and near sp3 hybridization: ρp=0.62, ρs=0.18, ρp/ρs=3.4, and three Cl atoms and the other Cl atom have the spin densities ρp=0.10 and ρp=0.05, respectively. The species had two optical absorptions at λmax=265 and 370 nm which were assigned to the Eγ-A*1γ and A1γ-A*1γ electronic transitions, respectively. The anion converted to CCl ṡ3 radical by warming to ˜150 K in the TMS matrix. The present results have given unequivocal ESR and optical spectroscopic evidence and support for the assignment of the 370 nm band reported in the radiolyses of organic solutions containing CCl4.

  20. Electron beam irradiation of fluoropolymers containing polyethers

    Science.gov (United States)

    Bucio, E.; Burillo, G.; Tapia, F.; Adem, E.; Cedillo, G.; Cassidy, P. E.

    2009-02-01

    A highly fluorinated monomer, 1,3-bis(1,1,1,3,3,3-hexafluoro-2-pentafluorophenyl methoxy-2-propyl)benzene (12F-FBE) was polymerized with some diphenols by polycondensation and then was electron beam irradiated between 100 and 1000 kGy to determine degradation radiochemistry yield ( Gs) by gel permeation chromatography (GPC). The samples were characterized after irradiation by DSC, FTIR, and nuclear magnetic resonance (NMR). The fluoropolymers show apparent degradation in mechanical properties at 300 kGy, except 12F-FBE polymerized with biphenol and bisphenol A, when they did not show any apparent physical change up to 300 kGy; and continue to be flexible and transparent, with a radiochemical yield scission ( Gs) of 0.75, 0.53, 0.88, and 0.38 for 12F-FBE/SDL aliphatic, 12F-FBE/biphenol, 12F-FBE/bisphenol A, and 12F-FBE/bisphenol O, respectively. The number average molecular weights for three of the polymers decrease upon 1000 kGy irradiation to 10% of their original values; however, the polymer from bisphenol A is much more stable and its Mn decreases to only 24% of original.

  1. Electron beam irradiation of fluoropolymers containing polyethers

    International Nuclear Information System (INIS)

    Bucio, E.; Burillo, G.; Tapia, F.; Adem, E.; Cedillo, G.; Cassidy, P.E.

    2009-01-01

    A highly fluorinated monomer, 1,3-bis(1,1,1,3,3,3-hexafluoro-2-pentafluorophenyl methoxy-2-propyl)benzene (12F-FBE) was polymerized with some diphenols by polycondensation and then was electron beam irradiated between 100 and 1000 kGy to determine degradation radiochemistry yield (G s ) by gel permeation chromatography (GPC). The samples were characterized after irradiation by DSC, FTIR, and nuclear magnetic resonance (NMR). The fluoropolymers show apparent degradation in mechanical properties at 300 kGy, except 12F-FBE polymerized with biphenol and bisphenol A, when they did not show any apparent physical change up to 300 kGy; and continue to be flexible and transparent, with a radiochemical yield scission (G s ) of 0.75, 0.53, 0.88, and 0.38 for 12F-FBE/SDL aliphatic, 12F-FBE/biphenol, 12F-FBE/bisphenol A, and 12F-FBE/bisphenol O, respectively. The number average molecular weights for three of the polymers decrease upon 1000 kGy irradiation to 10% of their original values; however, the polymer from bisphenol A is much more stable and its M n decreases to only 24% of original

  2. FTIR spectroscopy of electron irradiated polymers

    International Nuclear Information System (INIS)

    Finch, D.S.

    1988-04-01

    The chemical changes in electron beam irradiated polymers, in particular PVC, are considered in order to relate the formation of conjugated structures to changes in the electrical properties. Infrared spectroscopy has been used to measure these changes. Fourier Transform techniques and computing facilities make better data processing possible. A method for base line interpretation is demonstrated whereby a shift parallel to the abscisal axis in a region of the polymer that is non absorbing is used to evaluate the baseline. This technique has proved to be highly reproducible providing that the polymer films to be examined are optically homogeneous. Evaluation of the rate of decay of the total area of the carbon chlorine region of the polymer has been compared with the chlorine decay curve analysed by the measurement of x-ray emission during irradiation of bulk samples. The significant reduction in the evolution of atomic chlorine through x-ray analysis has been attributed to the trapping of HCl within the polymer film and its subsequent slow diffusion out of the polymer. With PVC, one of the main products as a result of irradiation is the formation of conjugated sequences. These were studied by the use of uv-visible spectroscopy. (author)

  3. Windowless Electron Beam Experimental Irradiation WEBExplr

    International Nuclear Information System (INIS)

    Heyse, J.

    2009-01-01

    The design of the MYRRHA/XT-ADS, the European eXperimental Accelerator Driven System for the demonstration of Transmutation, includes a high power windowless spallation target operating with liquid LBE (Lead-Bismuth Eutectic) that will be irradiated with a 600 MeV proton beam at currents of up to 2.5 mA. When considering such a high power windowless target design, a number of questions need to be addressed, such as the stability of the free surface flow and its ability to remove the power deposited by the proton beam by forced convection, the compatibility of a large hot LBE reservoir with the beam line vacuum and the outgassing of the LBE in the spallation target circuit. These issues have been studied during previous experiments supported by numerical simulations. Another crucial point in the development of the spallation target is the demonstration of the safe and stable operation of the free LBE surface during irradiation with a high power proton beam. As a first step in this program, the WEBExpIr (Windowless target Electron Beam Experimental Irradiation) experiment was set up. The purpose of the WEBExpIr experiment was to investigate the influence of LBE surface heating caused by a charged particle beam in a situation representative of the MYRRHA/XT-ADS. More in particular, we wanted to assess possible free surface distortion or shockwave effects in nominal conditions and during sudden beam on/off transient situations, as well as possible enhanced evaporation

  4. On the nature of low temperature anomalies of metallic glass inelastic properties

    International Nuclear Information System (INIS)

    Spivak, L.V.; Khonik, V.A.

    1997-01-01

    Low-temperature (30 60 Nb 40 metallic glass (MG) exposed to the preliminary cold deformation via rolling, to high-temperature homogeneous deformation or to electrolytic hydrogen absorption were investigated. Conclusion is made that the published low-temperature peaks of the internal friction in quick-hardened cold-deformed or hydrogen absorbed MGs are of the common dislocation-like nature. Effect of 2 MeV electron irradiation on the temperature dependence of the internal friction and on the elasticity module of hydrogenated specimens was investigated, as well [ru

  5. Electronic structure and transport in the low-temperature thermoelectric CsBi4Te6: Semiclassical transport equations

    DEFF Research Database (Denmark)

    Lykke, Lars; Iversen, Bo Brummerstedt; Madsen, Georg

    2006-01-01

    The band structure of the low-temperature thermoelectric material, CsBi4Te6, is calculated and analyzed using the semiclassic transport equations. It is shown that to obtain a quantitative agreement with measured transport properties, a band gap of 0.08 eV must be enforced. A gap in reasonable...... agreement with experiment was obtained using the generalized gradient functional of Engel and Vosko [E. Engel and S. H. Vosko, Phys. Rev. B 47, 13164 (1993)]. We found that the experimental p-type sample has a carrier concentration close to optimal. Furthermore, the conduction bands have a form equally well...

  6. Low temperature formation of ferroelectric PbTiO3 films by laser ablation with 2nd laser irradiation; Reiki hikari laser heiyo laser ablation ho ni yoru kyoyudentai PbTiO3 usumaku no teion keisei

    Energy Technology Data Exchange (ETDEWEB)

    Tabata, H.; Kawai, T. [Osaka University, Osaka (Japan)

    1997-08-20

    The unique advantage of the pulsed laser deposition is its ability to produce highly oriented stoichiometric films at a low substrate temperature. Ferroelectric PbTiO3 thin films have been formed using 2nd laser assisted laser ablaion technique at low temperature, i.e., 350degC, on Sr7iO3 single-crystal substrates and Pt/MgO electrodes. The second laser irradiation at the substrate surface is quite effective for crystallization of the films at low substrate temperature below 400degC. The suitable energy density (fluence) of the irradiation laser is in the range of 30-100 mJ/cm{sup 2}. X-ray diffraction patterns of PbTiO3 thin films show c-axis orientation, with a rocking angle of 1.0 - 0.5deg. These films exhibit ferroelectric hysteresis loop. The dielectric constant and remanent polalyzation of the PbTiO3 films are in the range of 120-150 and 60-80 {mu}C/cm{sup 2}, respectively. 31 refs., 10 figs., 1 tab.

  7. Electron paramagnetic resonance study on n-type electron-irradiated 3C-SiC

    Energy Technology Data Exchange (ETDEWEB)

    Carlsson, P; Rabia, K; Son, N T; Janzen, E [Department of Physics, Chemistry and Biology, Linkoeping University, SE-581 83 Linkoeping (Sweden); Ohshima, T; Morishita, N; Itoh, H [Japan Atomic Energy Research Institute, Takasaki 370-1292 (Japan); Isoya, J [University of Tsukuba, Tsukuba 305-8550 (Japan)], E-mail: paca@ifm.liu.se

    2008-03-15

    Electron Paramagnetic Resonance (EPR) was used to study defects in n-type 3C-SiC films irradiated by 3-MeV electrons at room temperature with a dose of 2x10{sup 18} cm{sup -2}. After electron irradiation, two new EPR spectra with an effective spin S = 1, labeled L5 and L6, were observed. The L5 center has C{sub 3v} symmetry with g = 2.004 and a fine-structure parameter D = 436.5x10{sup -4} cm{sup -1}. The L5 spectrum was only detected under light illumination and it could not be detected after annealing at {approx}550{sup 0}C. The principal z-axis of the D tensor is parallel to the <111>-directions, indicating the location of spins along the Si-C bonds. Judging from the symmetry and the fact that the signal was detected under illumination in n-type material, the L5 center may be related to the divacancy in the neutral charge state. The L6 center has a C{sub 2v}-symmetry with an isotropic g-value of g = 2.003 and the fine structure parameters D = 547.7x10{sup -4} cm{sup -1} and E = 56.2x10{sup -4} cm{sup -1}. The L6 center disappeared after annealing at a rather low temperature ({approx}200 deg. C), which is substantially lower than the known annealing temperatures for vacancy-related defects in 3C-SiC. This highly mobile defect may be related to carbon interstitials.

  8. Electron spin resonance and E.N.D.O.R. double resonance study of free radicals produced by gamma irradiation of imidazole single crystals

    International Nuclear Information System (INIS)

    Lamotte, B.

    1970-01-01

    Gamma irradiation of imidazole single crystals at 300 deg. K gives two radicals. Identification and detailed studies of their electronic and geometric structure have been made by ESR and ENDOR techniques. A study of the hydrogen bonded protons hyperfine tensor is made and let us conclude to the inexistence of movement and tunneling of these protons. The principal low temperature radical, produced by gamma irradiation at 77 deg. K has been also studied by ESR and a model has been proposed. (author) [fr

  9. Application of electron beam irradiation. 4. Treatment of pollutants by electron beam irradiation

    International Nuclear Information System (INIS)

    Tokunaga, Okihiro; Arai, Hidehiko

    1994-01-01

    Electron beam irradiation is capable of dissolving and removing pollutants, such as sulfur oxides, nitrogen oxides, and organic compounds, by easy production of OH radicals in flue gas and water. This paper deals with current status in the search for techniques for treating flue gas and waste water, using electron beam irradiation. Pilot tests have been conducted during the period 1991-1994 for the treatment of flue gas caused by coal and garbage burning and road tunnels. Firstly, techniques for cleaning flue gas with electron beams are outlined, with special reference to their characteristics and process of research development. Secondly, the application of electron beam irradiation in the treatment of waste water is described in terms of the following: (1) disinfection of sewage, (2) cleaning of water polluted with toxic organic compounds, (3) treatment for eliminating sewage sludge, (4) promotion of sewage sludge sedimentation, (5) disinfection and composting of sewage sludge, and (6) regeneration of activated carbon used for the treatment of waste water. (N.K.)

  10. The electron irradiation effects in different structures of diodes

    International Nuclear Information System (INIS)

    Li Quanfen; Wang Jiaxu

    1993-01-01

    This paper describes the different electron irradiation effects in different structures of diodes and the different results produced by different irradiation ways. From this work, we can know how to choose proper manufacture arts and comprehensive factors according to the structures of diodes and the irradiation conditions

  11. Sprout inhibition of potatoes by electron irradiation, (2)

    International Nuclear Information System (INIS)

    Furuta, Junichiro; Hiraoka, Eiichi; Okamoto, Shinichi; Fujishiro, Masatoshi; Kanazawa, Tamotsu; Ohnishi, Tokuhiro; Tsujii, Yukio; Hori, Shiro

    1982-01-01

    Sprouting of potatoes are inhibited usually by the gamma-ray irradiation. The buds of potatoes exist in a very thin layer near surface of each tuber. So the inhibition will be performed sufficiently by surface irradiation using electron beams. To irradiate all surfaces of each potato uniformly, the authors prepare a new apparatus which is a conveyer passing under an electron beam scanner of accelerator rotating the potatoes by many rotating rollers. The sprout inhibition experiment of potatoes was performed by following three methods to obtain the performance of this apparatus, and the results were compared. 1) turn over irradiation method --- potatoes were arranged in one layer in plastic baskets and were irradiated on the conveyor. After irradiation, the potatoes were turned over and were irradiated again. 2) rotating irradiation method --- potatoes were rotated on the rotating roller apparatus set on the conveyer and were passed under the electron beam scanner. 3) rotating irradiation method with an improved rotating roller apparatus --- the rotating rollers have many protuberances on their surface to irradiate all of potato surface more uniform. 550 keV electron beams by Cockcroft-Walton type accelerator were used for the irradiation and the irradiated dose was 5 to 20 krad. 40 pieces of potates, ''Danshaku'' variety yielded in June 1981, were irradiated for each dose in the beginning of August. Prior to these irradiation experiments, the dose and dose uniformity were checked by the agar color dosimeters. After the irradiation, potatoes were stored in natural condition and their sprouting was observed. The potatoes irradiated by the improved rotating roller apparatus were almost completely sprout-inhibited by 20 krad irradiation. (author)

  12. Design of electron detection system for pulse electron irradiator

    International Nuclear Information System (INIS)

    Anjar Anggraini H; Agus Purwadi; Lely Susita RM; Bambang Siswanto; Agus Wijayanto

    2016-01-01

    Design of electron detection system for pulse electron irradiator has been conducted on the Plasma Cathode Electron Source by Rogowski coil technique. Rogowski coil has ability to capture the induced magnetic field of the electric current, subsequent induced magnetic field will provide voltage after passing integrator. This diagnostic used combination of copper wire, ferrite and RC integrator. The design depends on the pulse width and the value of plasma current that passes through the coil, thus the number of windings, coil area and integrator can be designed. For plasma spots current of IDPS expected to be 10 A and pulse width 10 μs the Rogowski coil using MnZn ferrite with inductance L = 0.275 mH and permeability μr = 200 H/m. For the current of plasma arc ADPS expected to be 100 A and pulse width 100 μs by using inductance L=1.9634 mH and permeability μr = 6256 H/m. Electron current in extraction system expected to be 30 A and pulse width 100 μs the Rogowski coil using inductance L=51.749 mH and permeability μr= 4987 H/m. Design integrator used is the type of RC integrator. (author)

  13. LOW TEMPERATURE CATHODE SUPPORTED ELECTROLYTES

    Energy Technology Data Exchange (ETDEWEB)

    Harlan U. Anderson

    2000-03-31

    This project has three main goals: Thin Films Studies, Preparation of Graded Porous Substrates and Basic Electrical Characterization and Testing of Planar Single Cells. During this time period substantial progress has been made in developing low temperature deposition techniques to produce dense, nanocrystalline yttrium-stabilized zirconia films on both dense oxide and polymer substrates. Progress has been made in the preparation and characterization of thin electrolytes and porous LSM substrates. Both of these tasks are essentially on or ahead of schedule. In our proposal, we suggested that the ZrO{sub 2}/Sc system needed to be considered as a candidate as a thin electrolyte. This was because microcrystalline ZrO{sub 2}/Sc has a significantly higher ionic conductivity than YSZ, particularly at the lower temperatures. As a result, some 0.5 micron thick film of ZrO{sub 2}/16% Sc on an alumina substrate (grain size 20nm) was prepared and the electrical conductivity measured as a function of temperature and oxygen activity. The Sc doped ZrO{sub 2} certainly has a higher conductivity that either 20nm or 2400nm YSZ, however, electronic conductivity dominates the conductivity for oxygen activities below 10{sup -15}. Whereas for YSZ, electronic conductivity is not a problem until the oxygen activity decreases below 10{sup -25}. These initial results show that the ionic conductivity of 20nm YSZ and 20nm ZrO{sub 2}/16% Sc are essentially the same and the enhanced conductivity which is observed for Sc doping in microcrystalline specimens is not observed for the same composition when it is nanocrystalline. In addition they show that the electronic conductivity of Sc doped ZrO{sub 2} is at least two orders of magnitude higher than that observed for YSZ. The conclusion one reaches is that for 0.5 to 1 micron thick nanocrystalline films, Sc doping of ZrO{sub 2} has no benefits compared to YSZ. As a result, electrolyte films of ZrO{sub 2}/Sc should not be considered as candidates

  14. Simulation model for electron irradiated IGZO thin film transistors

    Science.gov (United States)

    Dayananda, G. K.; Shantharama Rai, C.; Jayarama, A.; Kim, Hyun Jae

    2018-02-01

    An efficient drain current simulation model for the electron irradiation effect on the electrical parameters of amorphous In-Ga-Zn-O (IGZO) thin-film transistors is developed. The model is developed based on the specifications such as gate capacitance, channel length, channel width, flat band voltage etc. Electrical parameters of un-irradiated IGZO samples were simulated and compared with the experimental parameters and 1 kGy electron irradiated parameters. The effect of electron irradiation on the IGZO sample was analysed by developing a mathematical model.

  15. Study by electron spin resonance (ESR) of 60 Co irradiated grains and farinaceous derivatives

    International Nuclear Information System (INIS)

    Catanni, Marta Mattos.

    1995-01-01

    The electron spin resonance (ESR) spectroscopy is being pointed out as one of the most promising techniques to determine whether a food has been irradiated. In this work, the ESR spectrum of paramagnetic radicals produced by gamma irradiation of grains and flour derivatives using a 60 Co source was investigated. Samples of grains (wheat and barley), flours (wheat, maniac, rye, soy bean and maize), bran and starch have been irradiated with doses between 0.2 and 70 KGy. It was shown that all varieties of grains and flours presented similar ESR spectra with variation in the free radicals signal intensity. Measurements at 9.5 and 34.5 GHz shown that spectra were composed probably by the superposition of four paramagnetic species with g-factors closed to that of the free electron (2 triplets, 1 doublet and 1 singlet). Hyperfine interactions and the correspondingly line widths were estimated through an spectrum computer simulation. It was established that ESR signal intensities increased with the irradiation dose for all samples. Up to the commercial admissible dose limit (1 kGy), the increase of ESR signal shown a linear behavior with the dose. The signal stability varied significantly with storage conditions and sample humidity. For 1 kGy-irradiated samples stored at room temperature and 14% humidity, the ESR radiation signals were possible to be detected up to 5 days after irradiation. When the same samples were stored at low temperatures (0 0 C) or freeze-dried (almost 0% humidity) the ESR signals were detected until 6 months after irradiation. Similar ESR spectrum found for grains and flours was obtained for diverse starchy food products. It was verified that it is possible to identify for a long time irradiated starchy foods when they are commercialized dehydrated or frozen. (author). 66 refs., 35 figs., 17 tabs

  16. Coating composition curable by electron beam irradiation

    International Nuclear Information System (INIS)

    Masuda, Hiromasa; Iijima, Ken-ichi.

    1971-01-01

    Here is provided a coating composition curable with low dose of electron beams to give a smooth coating film having no surface tackiness. In one example, 126 parts of melamine was reacted with 682 parts of formalin followed by 697 parts of β-hydroxyethyl acrylate to produce component (A) (viscosity 780 cp). On the other hand, 900 parts of tung oil was reacted with 343 parts of maleic anhydride followed by 22 parts of dimethylaminoethyl methacrylate and 406 parts of β-hydroxyethyl acrylate. The resulting product was diluted with 508 parts of methyl methacrylate to give component (B) (dark red, viscous substance). 900 parts of (A), 100 parts of (B), 0.5 part of bees wax and 0.2 part of paraffin wax were blended together. A sized material was coated with the mixture and irradiated with electron beams (6 Mrad) in the presence of air. A smooth film free from surface tackiness was obtained. β-hydroxyethyl acrylate may be replaced by other hydroxyalkyl esters of α,β-unsaturated acids, and melamine may be replaced by urea, benzoguanamine or acetoguanamine. Tung oil may be replaced by linseed, safflower, soybean, rice, oiticica or cotton seed oil. A more flexible film is obtained by using component (B) in a larger proportion. (A)/(B) ratio should be in the range of 90/10 to 10/90 by wt. (Kaichi, S.)

  17. Temperature, stress, and annealing effects on the luminescence from electron-irradiated silicon

    Science.gov (United States)

    Jones, C. E.; Johnson, E. S.; Compton, W. D.; Noonan, J. R.; Streetman, B. G.

    1973-01-01

    Low-temperature photoluminescence spectra are presented for Si crystals which have been irradiated with high-energy electrons. Studies of isochronal annealing, stress effects, and the temperature dependences of the luminescence are used to discuss the nature of the luminescent transitions and the properties of defects. Two dominant bands present after room-temperature anneal of irradiated material are discussed, and correlations of the properties of these bands are made with known Si defects. A band between 0.8 and 1.0 eV has properties which are related to those of the divacancy, and a band between 0.6 and 0.8 eV has properties related to those of the Si-G15(K) center. Additional peaks appear in the luminescence after high-temperature anneal; the influence of impurities and the effects of annealing of these lines are discussed.

  18. Neutron irradiation damage of nuclear graphite studied by high-resolution transmission electron microscopy and Raman spectroscopy

    Energy Technology Data Exchange (ETDEWEB)

    Krishna, R. [Dalton Cumbrian Facility, Dalton Nuclear Institute, The University of Manchester, Westlakes Science & Technology Park, Moor Row, Whitehaven, Cumbria, CA24 3HA (United Kingdom); Jones, A.N., E-mail: Abbie.Jones@manchester.ac.uk [Nuclear Graphite Research Group, School of MACE, The University of Manchester, Manchester, M13 9PL (United Kingdom); McDermott, L.; Marsden, B.J. [Nuclear Graphite Research Group, School of MACE, The University of Manchester, Manchester, M13 9PL (United Kingdom)

    2015-12-15

    Nuclear graphite components are produced from polycrystalline artificial graphite manufacture from a binder and filler coke with approximately 20% porosity. During the operational lifetime, nuclear graphite moderator components are subjected to fast neutron irradiation which contributes to the change of material and physical properties such as thermal expansion co-efficient, young's modulus and dimensional change. These changes are directly driven by irradiation-induced changes to the crystal structure as reflected through the bulk microstructure. It is therefore of critical importance that these irradiation changes and there implication on component property changes are fully understood. This work examines a range of irradiated graphite samples removed from the British Experimental Pile Zero (BEPO) reactor; a low temperature, low fluence, air-cooled Materials Test Reactor which operated in the UK. Raman spectroscopy and high-resolution transmission electron microscopy (HRTEM) have been employed to characterise the effect of increased irradiation fluence on graphite microstructure and understand low temperature irradiation damage processes. HRTEM confirms the structural damage of the crystal lattice caused by irradiation attributed to a high number of defects generation with the accumulation of dislocation interactions at nano-scale range. Irradiation-induced crystal defects, lattice parameters and crystallite size compared to virgin nuclear graphite are characterised using selected area diffraction (SAD) patterns in TEM and Raman Spectroscopy. The consolidated ‘D’peak in the Raman spectra confirms the formation of in-plane point defects and reflected as disordered regions in the lattice. The reduced intensity and broadened peaks of ‘G’ and ‘D’ in the Raman and HRTEM results confirm the appearance of turbulence and disordering of the basal planes whilst maintaining their coherent layered graphite structure. - Highlights: • Irradiated graphite

  19. Neutron irradiation damage of nuclear graphite studied by high-resolution transmission electron microscopy and Raman spectroscopy

    International Nuclear Information System (INIS)

    Krishna, R.; Jones, A.N.; McDermott, L.; Marsden, B.J.

    2015-01-01

    Nuclear graphite components are produced from polycrystalline artificial graphite manufacture from a binder and filler coke with approximately 20% porosity. During the operational lifetime, nuclear graphite moderator components are subjected to fast neutron irradiation which contributes to the change of material and physical properties such as thermal expansion co-efficient, young's modulus and dimensional change. These changes are directly driven by irradiation-induced changes to the crystal structure as reflected through the bulk microstructure. It is therefore of critical importance that these irradiation changes and there implication on component property changes are fully understood. This work examines a range of irradiated graphite samples removed from the British Experimental Pile Zero (BEPO) reactor; a low temperature, low fluence, air-cooled Materials Test Reactor which operated in the UK. Raman spectroscopy and high-resolution transmission electron microscopy (HRTEM) have been employed to characterise the effect of increased irradiation fluence on graphite microstructure and understand low temperature irradiation damage processes. HRTEM confirms the structural damage of the crystal lattice caused by irradiation attributed to a high number of defects generation with the accumulation of dislocation interactions at nano-scale range. Irradiation-induced crystal defects, lattice parameters and crystallite size compared to virgin nuclear graphite are characterised using selected area diffraction (SAD) patterns in TEM and Raman Spectroscopy. The consolidated ‘D’peak in the Raman spectra confirms the formation of in-plane point defects and reflected as disordered regions in the lattice. The reduced intensity and broadened peaks of ‘G’ and ‘D’ in the Raman and HRTEM results confirm the appearance of turbulence and disordering of the basal planes whilst maintaining their coherent layered graphite structure. - Highlights: • Irradiated graphite exhibits

  20. Effects of short-range order on electronic properties of Zr-Ni glasses as seen from low-temperature specific heat

    International Nuclear Information System (INIS)

    Kroeger, D.M.; Koch, C.C.; Scarbrough, J.O.; McKamey, C.G.

    1984-01-01

    Measurements of the low-temperature specific heat C/sub p/ of liquid-quenched Zr-Ni glasses for a large number of compositions in the range from 55 to 74 at. % Zr revealed an unusual composition dependence of the density of states at the Fermi level, N(E/sub F/). Furthermore, for some compositions the variation of C/sub p/ near the superconducting transition temperature T/sub c/ indicated the presence of two superconducting phases, i.e., two superconducting transitions were detected. Comparison of the individual T/sub c/'s in phase-separated samples to the composition dependence of T/sub c/ for all of the samples suggests that amorphous phases with compositions near 60 and 66.7 at. % Zr occur. We discuss these results in terms of an ''association model'' for liquid alloys (due to Sommer), in which associations of unlike atoms with definite stoichiometries are assumed to exist in equilibrium with unassociated atoms. We conclude that in the composition range studied, associate clusters with the compositions Zr 3 Ni 2 and Zr 2 Ni occur. In only a few cases are the clusters sufficiently large, compared with the superconducting coherence length, for separate superconducting transitions to be observed. The variation of N(E/sub F/) with composition is discussed, as well as the effects of this chemical short-range ordering on the crystallization behavior and glass-forming tendency

  1. Effects of short-range order on electronic properties of Zr-Ni glasses as seen from low-temperature specific heat

    Science.gov (United States)

    Kroeger, D. M.; Koch, C. C.; Scarbrough, J. O.; McKamey, C. G.

    1984-02-01

    Measurements of the low-temperature specific heat Cp of liquid-quenched Zr-Ni glasses for a large number of compositions in the range from 55 to 74 at.% Zr revealed an unusual composition dependence of the density of states at the Fermi level, N(EF). Furthermore, for some compositions the variation of Cp near the superconducting transition temperature Tc indicated the presence of two superconducting phases, i.e., two superconducting transitions were detected. Comparison of the individual Tc's in phase-separated samples to the composition dependence of Tc for all of the samples suggests that amorphous phases with compositions near 60 and 66.7 at.% Zr occur. We discuss these results in terms of an "association model" for liquid alloys (due to Sommer), in which associations of unlike atoms with definite stoichiometries are assumed to exist in equilibrium with unassociated atoms. We conclude that in the composition range studied, associate clusters with the compositions Zr3Ni2 and Zr2Ni occur. In only a few cases are the clusters sufficiently large, compared with the superconducting coherence length, for separate superconducting transitions to be observed. The variation of N(EF) with composition is discussed, as well as the effects of this chemical short-range ordering on the crystallization behavior and glass-forming tendency.

  2. Low temperature recovery of radiation damage in vanadium

    International Nuclear Information System (INIS)

    Klabunde, C.E.; Coltman, R.R. Jr.; Williams, J.M.

    1975-01-01

    Some kind of order may emerge from the numerous anomalies in the low-temperature recovery of irradiated V if it is assumed that Stage I (first recovery by interstitial migration) occurs below 4 0 K. Present supporting evidence includes: from both thermal neutron and fission neutron damage studies (1) a continuous, nearly structureless recovery from 4 to 43 0 K independent of dose; (2) a nonlinear, decreasing damage rate at 4 0 K; and (3) from 6 0 K electron irradiations near threshold energy there is derived a Frenkel pair resistivity which is so small as to suggest significant loss of defects during irradiation. The assumption of a very low-lying Stage I also helps to explain several other unusual aspects of the data, especially those relating to the sharp recovery peak at 47 0 K. This is clearly a single first-order process (with a measured activation energy of 0.13 eV), but it has a strong positive dependence of population percentage upon dose, opposite to Stage II impurity detrapping peaks in several fcc metals. Also, the peak has a strong negative dependence upon irradiation temperature when equal doses put in at 4 and 31 0 K are compared

  3. Electron trapping during irradiation in reoxidized nitrided oxide

    International Nuclear Information System (INIS)

    Mallik, A.; Vasi, J.; Chandorkar, A.N.

    1993-01-01

    Isochronal detrapping experiments have been performed following irradiation under different gate biases in reoxidized nitrided oxide (RNO) MOS capacitors. These show electron trapping by the nitridation-induced electron traps at low oxide fields during irradiation. A difference in the detrapping behavior of trapped holes and electrons is observed, with trapped holes being detrapped at relatively lower temperatures compared to trapped electrons. Electron trapping shows a strong dependence on tile magnitude of the applied gate bias during irradiation but is independent of its polarity. Conventional oxide devices, as expected, do not show any electron trapping during irradiation by the native electron traps. Finally, a comparison of the isochronal detrapping behavior following irradiation and following avalanche injection of electrons has been made to estimate the extent of electron trapping. The results show that electron trapping by the nitridation-induced electron traps does not play the dominant role in improving radiation performance of RNO, though its contribution cannot be completely neglected for low oxide field irradiations

  4. Comparison of electron-irradiation and gamma-irradiation as a decontamination treatment of spices

    International Nuclear Information System (INIS)

    Hayashi, Toru; Todoriki, Setsuko; Mamun.

    1993-01-01

    Electron-irradiation at 10 kGy decontaminated all the eight kinds of spices (black pepper, white pepper, nutmeg, red pepper, parsley, paprika, laurel and onion powder) to the microbial levels lower than 10 2 /g. Similar sterilization effects by the irradiation were observed on heat-resistant bacterial spores. The 10 kGy irradiation did not significantly affect the contents of essential oils and colors of the spices. These results indicate that electron-irradiation at 10 kGy effectively decontaminates spices without notable adverse effect on the qualities. The disinfecting effect of electron beams on spices was smaller than that of gamma-rays. (author)

  5. Effect of electron beam irradiation on seed germination

    Energy Technology Data Exchange (ETDEWEB)

    Han, Seunghee; Bae, Youngmin [Changwon Univ., Changwon (Korea, Republic of)

    2013-07-01

    Effect of electron beam irradiation on seed germination was investigated in this research. Electron beam of 0.5, 1.0, 1.5 and 2.0 kGy was irradiated to the seeds of lettuce, green onion and cucumber, and the irradiated seeds were incubated at 25 .deg. Cn Nitsch medium solidified with 0.2% Phytagel. Germination percentage and the length of the sprouts were determined after 72 hours. Germination percentage of lettuce seeds was greatly reduced by the irradiation, and that of the green onion and cucumber were moderately reduced or unchanged by the irradiation. Although average length of the lettuce sprouts was reduced severely, that of the green onion and cucumber was unchanged or moderately reduced. Conclusively, electron beam irradiation might be a useful way of disinfecting some plant seeds including green onion and cucumber.

  6. Effect of electron beam irradiation on seed germination

    International Nuclear Information System (INIS)

    Han, Seunghee; Bae, Youngmin

    2013-01-01

    Effect of electron beam irradiation on seed germination was investigated in this research. Electron beam of 0.5, 1.0, 1.5 and 2.0 kGy was irradiated to the seeds of lettuce, green onion and cucumber, and the irradiated seeds were incubated at 25 .deg. Cn Nitsch medium solidified with 0.2% Phytagel. Germination percentage and the length of the sprouts were determined after 72 hours. Germination percentage of lettuce seeds was greatly reduced by the irradiation, and that of the green onion and cucumber were moderately reduced or unchanged by the irradiation. Although average length of the lettuce sprouts was reduced severely, that of the green onion and cucumber was unchanged or moderately reduced. Conclusively, electron beam irradiation might be a useful way of disinfecting some plant seeds including green onion and cucumber

  7. Electronically stimulated deep-center reactions in electron-irradiated InP: Comparison between experiment and recombination-enhancement theories

    International Nuclear Information System (INIS)

    Sibille, A.

    1987-01-01

    We present a detailed study of the recombination enhancement of several defect reactions involving the main deep centers in low-temperature electron-irradiated InP. A fairly good agreement is obtained with the Weeks-Tully-Kimerling theory for the activation energies of the enhanced process. On the other hand, a thorough investigation of a thermally and electronically stimulated defect transformation shows evidence that one major approximation (local vibrational equilibrium) fails, and that the recently proposed [H. Sumi, Phys. Rev. B 29, 4616 (1984)] mechanism of coherent recombination on deep centers is responsible for altered reaction rates at high injection levels

  8. Cost evaluation of irradiation system with electron accelerator

    International Nuclear Information System (INIS)

    Kashiwagi, M.

    2003-01-01

    The features of electron beam irradiation system using electron accelerator are direct energy pour into the irradiated material, no third material mixture such as catalyst, suitable for mass production and easy operation and maintenance work available. These features can bring the various applications such as cross-linking action, graft polymerization, radical polymerization and others. The selection of electron accelerator ratings is made under consideration of quality, width and thickness of irradiated material, production amount, dose required for reaction and irradiation atmosphere. Especially in a case of irradiation of wire with high insulation material such as polyethylene, the consideration of maximum thickness toward irradiation direction is necessary to avoid the discharge (Lichtenberg discharge) by charged-up electrons inside insulation material. Therefore, the acceleration voltage should be selected to make the maximum penetration larger than maximum irradiation thickness. The actual model case of estimate the irradiation cost was selected that the irradiation object was polyethylene insulated wire up to AWG no.14, irradiation amount was 5,000 km/month, necessary dose was 200 kGy, operation time was 22 d/month and 8 h/day and actual operation efficiency was considered loss time such as bobbin changing as 80%. The selected ratings of electron accelerator were acceleration voltage of 800 kV, beam current of 100 mA and irradiation width of 180 cm with irradiation pulleys stand of 60 turns x 3 lanes. The initial total cost was estimated as 3 M$(US) and operation cost was evaluated as 215 k$(US). Therefore, the irradiation cost of wire was evaluated as 0.0036 $/m. (author)

  9. On mutual electron and phonon drag and low-temperature anomalies of thermoelectric and thermomagnetic effects in HgSe:Fe crystal

    International Nuclear Information System (INIS)

    Kuleev, I.G.; Arapova, I.Yu.

    2000-01-01

    Different approaches to solving the set of transport equations for a nonequilibrium electron-phonon system in the magnetic field are considered. The effect of mutual drag of electron and phonon on the magnetic field dependence of the Nernst-Ettingshausen coefficients is analyzed. A detailed analysis of the dependence of the iron content in HgSe:Fe crystals with regard to the mutual electron and phonon drag is carried out. Kinetic coefficients corresponding to these approaches to the solutions are calculated for conductors with the degenerate statistics of the current carriers [ru

  10. Electron irradiation induced nanocrystal formation in Cu-borosilicate glass

    Energy Technology Data Exchange (ETDEWEB)

    Sabri, Mohammed Mohammed; Möbus, Günter, E-mail: g.moebus@sheffield.ac.uk [University of Sheffield, Department of Materials Science and Engineering (United Kingdom)

    2016-03-15

    Nanoscale writing of Cu nanoparticles in glasses is introduced using focused electron irradiation by transmission electron microscopy. Two types of copper borosilicate glasses, one with high and another with low Cu loading, have been tested at energies of 200–300 keV, and formation of Cu nanoparticles in a variety of shapes and sizes using different irradiation conditions is achieved. Electron energy loss spectroscopy analysis, combined with high-resolution transmission electron microscopy imaging, confirmed the irradiation-induced precipitated nanoparticles as metallic, while furnace annealing of the glass triggered dendrite-shaped particles of copper oxide. Unusual patterns of nanoparticle rings and chains under focused electron beam irradiation are also presented. Conclusively, electron beam patterning of Cu-loaded glasses is a promising alternative route to well-established femtosecond laser photoreduction of Cu ions in glass.

  11. Identification of irradiated chicken meat using electron spin resonance spectroscopy

    International Nuclear Information System (INIS)

    Chawla, S.P.; Thomas, Paul

    2004-01-01

    Studies were carried out on detection of irradiation treatment in chicken using electron spin resonance (ESR) spectroscopy. The effect of gamma- irradiation treatment on radiation induced signal in different types of chicken namely, broiler, deshi and layers was studied. Irradiation treatment induced a characteristic ESR signal that was not detected in non-irradiated samples. The shape of the signal was not affected by type of the bone. The intensity of radiation induced ESR signal was affected by factors such as absorbed radiation dose, bone type irradiation temperature, post-irradiation storage, post-irradiation cooking and age of the bird. Deep-frying resulted in the formation of a symmetric signal that had a different shape and was weaker than the radiation induced signal. This technique can be effectively used to detect irradiation treatment in bone-in chicken meat even if stored and/or subjected to various traditional cooking procedures. (author)

  12. Dose controlled low energy electron irradiator for biomolecular films.

    Science.gov (United States)

    Kumar, S V K; Tare, Satej T; Upalekar, Yogesh V; Tsering, Thupten

    2016-03-01

    We have developed a multi target, Low Energy Electron (LEE), precise dose controlled irradiator for biomolecular films. Up to seven samples can be irradiated one after another at any preset electron energy and dose under UHV conditions without venting the chamber. In addition, one more sample goes through all the steps except irradiation, which can be used as control for comparison with the irradiated samples. All the samples are protected against stray electron irradiation by biasing them at -20 V during the entire period, except during irradiation. Ethernet based communication electronics hardware, LEE beam control electronics and computer interface were developed in house. The user Graphical User Interface to control the irradiation and dose measurement was developed using National Instruments Lab Windows CVI. The working and reliability of the dose controlled irradiator has been fully tested over the electron energy range of 0.5 to 500 eV by studying LEE induced single strand breaks to ΦX174 RF1 dsDNA.

  13. Dose controlled low energy electron irradiator for biomolecular films

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, S. V. K., E-mail: svkk@tifr.res.in; Tare, Satej T.; Upalekar, Yogesh V.; Tsering, Thupten [Tata Institute of Fundamental Research, Homi Bhabha Road, Colaba, Mumbai 400 005 (India)

    2016-03-15

    We have developed a multi target, Low Energy Electron (LEE), precise dose controlled irradiator for biomolecular films. Up to seven samples can be irradiated one after another at any preset electron energy and dose under UHV conditions without venting the chamber. In addition, one more sample goes through all the steps except irradiation, which can be used as control for comparison with the irradiated samples. All the samples are protected against stray electron irradiation by biasing them at −20 V during the entire period, except during irradiation. Ethernet based communication electronics hardware, LEE beam control electronics and computer interface were developed in house. The user Graphical User Interface to control the irradiation and dose measurement was developed using National Instruments Lab Windows CVI. The working and reliability of the dose controlled irradiator has been fully tested over the electron energy range of 0.5 to 500 eV by studying LEE induced single strand breaks to ΦX174 RF1 dsDNA.

  14. ESR investigataions of electron-beam irradiated cellulose nitrate

    International Nuclear Information System (INIS)

    Chipara, M.I.; Catana, D.; Grecu, V.; Romero, J.R.; Chipara, D.

    1994-01-01

    Electron spin resonance investigations on an electron-beam irradiated solid state nuclear track detector, based on cellulose nitrate (KODAK LR-311) are reported. The nature of free radicals induced in polymers by irradiation is discussed. The dependence of resonance spectral parameters on irradiation times, as well as on storage time and temperature, is studied. The experimental results are related to the stability of latent tracks and its is concluded that the free radicals induced by irradiation are located within the latent tracks. We have shown that both latent track and free radical thermal fading obey an Arrhenius-like dependence, with the same activation energy. (Author)

  15. ESR investigataions of electron-beam irradiated cellulose nitrate

    Energy Technology Data Exchange (ETDEWEB)

    Chipara, M.I.; Catana, D. [Institute of Atomic Physics, Bucharest (Romania); Grecu, V.; Romero, J.R. [Bucharest Univ. (Romania). Faculty of Physics; Coca, S. [Chemical Research Inst., Bucharest (Romania); Chipara, D. [Research Inst. for Electrotechnics, Bucharest (Romania)

    1994-10-01

    Electron spin resonance investigations on an electron-beam irradiated solid state nuclear track detector, based on cellulose nitrate (KODAK LR-311) are reported. The nature of free radicals induced in polymers by irradiation is discussed. The dependence of resonance spectral parameters on irradiation times, as well as on storage time and temperature, is studied. The experimental results are related to the stability of latent tracks and its is concluded that the free radicals induced by irradiation are located within the latent tracks. We have shown that both latent track and free radical thermal fading obey an Arrhenius-like dependence, with the same activation energy. (Author).

  16. ESR investigations of electron-beam irradiated cellulose nitrate

    International Nuclear Information System (INIS)

    Chipara, M.I.; Grecu, V.; Catana, D.; Romero, J.R.; Coca, S.; Chipara, M.D.

    1994-01-01

    Electron spin resonance investigations on an electron-beam irradiated solid state nuclear track detector, based on cellulose nitrate (KODAK LR-311), are reported. The nature of free radicals induced in polymers by irradiation is discussed. The dependence of resonance spectral parameters on irradiation times, as well as on storage time and temperature, is studied. The experimental results are related to the stability of latent tracks and it is concluded that the free radicals induced by irradiation are located within the latent tracks. We have shown that both latent track and free radical thermal fading obey an Arrhenius-like dependence, with the same activation energy. (Author)

  17. Electron beam influence on the carbon contamination of electron irradiated hydroxyapatite thin films

    International Nuclear Information System (INIS)

    Hristu, Radu; Stanciu, Stefan G.; Tranca, Denis E.; Stanciu, George A.

    2015-01-01

    Highlights: • Carbon contamination mechanisms of electron-beam-irradiated hydroxyapatite. • Atomic force microscopy phase imaging used to detect carbon contamination. • Carbon contamination dependence on electron energy, irradiation time, beam current. • Simulation of backscattered electrons confirms the experimental results. - Abstract: Electron beam irradiation which is considered a reliable method for tailoring the surface charge of hydroxyapatite is hindered by carbon contamination. Separating the effects of the carbon contamination from those of irradiation-induced trapped charge is important for a wide range of biological applications. In this work we focus on the understanding of the electron-beam-induced carbon contamination with special emphasis on the influence of the electron irradiation parameters on this phenomenon. Phase imaging in atomic force microscopy is used to evaluate the influence of electron energy, beam current and irradiation time on the shape and size of the resulted contamination patterns. Different processes involved in the carbon contamination of hydroxyapatite are discussed

  18. Precipitation in Ni-Si during electron and ion irradiation

    Science.gov (United States)

    Lucas, G. E.; Zama, T.; Ishino, S.

    1986-11-01

    This study was undertaken to further investigate how the nature of the irradiation condition affects precipitation in a dilute Ni-Si system. Transmission electron microscopy (TEM) discs of a solution annealed Ni alloy containing 5 at% Si were irradiated with 400 keV Ar + ions, 200 keV He + ions and 1 MeV electrons at average displacement rates in the range 2 × 10 -5dpa/s to 2 × 10 -3dpa/s at temperatures in the range 25°C to 450°C. Samples irradiated with electrons were observed in situ in an HVEM, while ion irradiated specimens were examined in a TEM after irradiation. Precipitation of Ni 3Si was detected by the appearance of superlattice spots in the electron diffraction patterns. It was found that as the mass of the irradiating species increased, the lower bound temperature at which Ni 3Si precipitation was first observed increased. For electron irradiation, the lower bound temperature at 2 × 10 -3dpa/s was ˜125°C, whereas for 400 keV Ar + irradiation at a similar average displacement rate the lower boundary was approximately 325°C. This suggests that cascade disordering competes with radiation induced solute segregation.

  19. Precipitation in Ni-Si during electron and ion irradiation

    International Nuclear Information System (INIS)

    Lucas, G.E.; Zama, T.; Ishino, S.

    1986-01-01

    This study was undertaken to further investigate how the nature of the irradiation condition affects precipitation in a dilute Ni-Si system. Transmission electron microscopy (TEM) discs of a solution annealed Ni alloy containing 5 at% Si were irradiated with 400 keV Ar + ions, 200 keV He + ions and 1 MeV electrons at average displacement rates in the range 2x10 -5 dpa/s to 2x10 -3 dpa/s at temperatures in the range 25 0 C to 450 0 C. Samples irradiated with electrons were observed in situ in an HVEM, while ion irradiated specimens were examined in a TEM after irradiation. Precipitation of Ni 3 Si was detected by the appearance of superlattice spots in the electron diffraction patterns. It was found that as the mass of the irradiating species increased, the lower bound temperature at which Ni 3 Si precipitation was first observed increased. For electron irradiation, the lower bound temperature at 2x10 -3 dpa/s was ∝125 0 C, whereas for 400 keV Ar + irradiation at a similar average displacement rate the lower boundary was approximately 325 0 C. This suggests that cascade disordering competes with radiation induced solute segregation. (orig.)

  20. Electron irradiation-induced defects in {beta}-SiC

    Energy Technology Data Exchange (ETDEWEB)

    Oshima, Ryuichiro [Osaka Prefectural Univ., Sakai (Japan). Reseach Inst. for Advanced Science and Technology

    1996-04-01

    To add information of point defects in cubic crystal SiC, polycrystal {beta}-SiC on the market was used as sample and irradiated by neutron and electron. In situ observation of neutron and electron irradiation-induced defects in {beta}-SiC were carried out by ultra high-voltage electronic microscope (UHVEM) and ordinary electronic microscope. The obtained results show that the electron irradiation-induced secondary defects are micro defects less than 20 nm at about 1273K, the density of defects is from 2x10{sup 17} to 1x10{sup 18}/cc, the secondary defects may be hole type at high temperature and the preexistant defects control nuclear formation of irradiation-induced defects, effective sink. (S.Y.)

  1. Vol. 5: Low Temperature Physics

    International Nuclear Information System (INIS)

    Sitenko, A.

    1993-01-01

    Problems of modern physics and the situation with physical research in Ukraine are considered. Programme of the conference includes scientific and general problems. Its proceeding are published in 6 volumes. The papers presented in this volume refer to low-temperature physics

  2. Certification testing at low temperatures

    International Nuclear Information System (INIS)

    Noss, P.W.; Ammerman, D.J.

    2004-01-01

    Regulations governing the transport of radioactive materials require that most hypothetical accident condition tests or analyses consider the effects of the environmental temperature that most challenges package performance. For many packages, the most challenging temperature environment is the cold condition (-29 C according to U.S. regulations), primarily because the low temperature causes the highest free drop impact forces due to the higher strength of many energy-absorbing materials at this temperature. If it is decided to perform low temperature testing, it is only necessary that the relevant parts of the package have the required temperature prior to the drop. However, the details of performing a drop at low temperature can have a large influence on testing cost and technical effectiveness. The selection of the test site, the chamber and type of chilling equipment, instrumentation, and even the time of year are all important. Control of seemingly minor details such as the effect on internal pressure, placement of monitoring thermocouples, the thermal time constant of the test article, and icing of equipment are necessary to ensure a successful low temperature test. This paper will discuss these issues and offer suggestions based on recent experience

  3. Science with low temperature detectors

    International Nuclear Information System (INIS)

    Sadoulet, B.; Lawrence Berkeley National Lab., CA; California Univ., Berkeley

    1996-01-01

    The novel technique of particle detection with low temperature detectors opens a number of new scientific opportunities. We review some of these, focusing on three generic applications: far infrared bolometry taking as an example the cosmic microwave background, X-ray spectroscopy for astrophysics and biological applications, and massive calorimeters for dark matter searches and neutrino physics. (orig.)

  4. Changing in tool steels wear resistance under electron irradiation

    International Nuclear Information System (INIS)

    Braginskaya, A.E.; Manin, V.N.; Makedonskij, A.V.; Mel'nikova, N.A.; Pakchanin, L.M.; Petrenko, P.V.

    1983-01-01

    The tool steels and alloys wear resistance under dry friction after electron irradiation has been studied. Electron irradiation of a wide variety of steels is shown to increase wear resistance. In this case phase composition and lattice parameters changes are observed both in matrix and carbides. The conclusion is drawn that an appreciable increase of steel wear resistance under electron irradiation can be explained both by carbide phase volume gain and changes in it's composition and the formation of carbide phase submicroscopic heterogeneities and, possibly, complexes of defects

  5. Effects of electron beam irradiation on cut flowers and mites

    International Nuclear Information System (INIS)

    Dohino, Toshiyuki; Tanabe, Kazuo

    1994-01-01

    Two spotted spider mite, Tetranychus urticae KOCH were irradiated with electron beams (2.5MeV) to develop an alternative quarantine treatment for imported cut flowers. The tolerance of eggs increased with age (1-5-day-old). Immature stages (larva-teleiochrysalis) irradiated at 0.4-0.8kGy increased tolerance with their development. Mated mature females irradiated at 0.4kGy or higher did not produce viable eggs, although temporary recovery was observed at 0.2kGy. Adult males were sterilized at 0.4kGy because non-irradiated virgin females mated with yielded female progeny malformed and sterilized. Various effects of electron beam irradiation were observed when nine species of cut flowers were irradiated in 5MeV Dynamitron accelerator. Chrysanthemum and rose were most sensitive among cut flowers. (author)

  6. Development of UV absorbing PET through Electron Irradiation

    International Nuclear Information System (INIS)

    Kim, Jung Woo; Lee, Na Eun; Lim, Hyung San; Park, Yang Jeong; Cho, Sung Oh

    2017-01-01

    Experiment to increase UV absorbance through electron beam irradiation on PET was performed. Moreover, surface hardness and roughness of each sample were observed to find the key factor increasing UV absorbance. PET sheets were irradiated with an electron beam at various fluences. The irradiated samples, as well as pristine sample, were subjected to UV-visible spectral study(UV-Vis), pencil hardness test, and scanning electron microscopy(SEM) experiment. In this study, PET samples irradiated at several conditions were analyzed through various measurements. UV absorbance-another meaning of transmittance in this study- of irradiated PET sample increased compared with pristine sample as fluence was increased in UV-Visible spectroscopy experiment.

  7. Effect of electron beam irradiation on fisheries water

    International Nuclear Information System (INIS)

    Sarala Selambakkannu; Khomsaton Abu Bakar; Jamaliah Shariff; Suhairi Alimon

    2012-01-01

    This paper studies about water obtained from fish pond of fisheries research centre. Usual water quality parameters such as pH, COD, Turbidity and Ammonia content were analyzed before and after irradiation. Electron beam irradiation was used to irradiate the water with the dose 100 kGy, 200 kGy and 300 kGy. Only high dose was applied on this water as only a limited amount of samples was supplied. All the parameters indicated a slight increase after irradiation except for the ammonia content, which showed a gradual decrease as irradiation dose increases. Sample condition was changed before irradiation in order to obtain more effective results in the following batch. The water sample from fisheries was diluted with distilled water to the ratio of 1:1.This was followed with irradiation at 100 kGy, 200 kGy and 300 kGy. The results still showed an increase in all parameters after irradiation except for ammonia content. For the following irradiation batch, the pH of the sample was adjusted to pH 4 and pH 8 before irradiation. For this sample the irradiation dose selected was only 100 kGy. A higher value of ammonia was observed for the sample with pH 4 after irradiation. Other parameters were almost the same as the first two batches. (author)

  8. Electron beam irradiation on cation exchanger used for strontium recovery

    International Nuclear Information System (INIS)

    Watanabe, Sou; Nakamura, Masahiro; Nomura, Kazunori; Nakajima, Yasuo; Okamoto, Yoshihiro

    2014-01-01

    Titanate is promising material for radioactive Sr recovery from liquid waste generated in the nuclear facilities. "9"0Sr is one of the most important nuclides in order to release the liquid waste into the environment due to its strong beta-ray decay energy. Although the titanate is applied to radioactive Sr decontamination facility, their resistance to irradiations from radioactive elements adsorbed is not widely investigated so far. In this study, durability of a hydrous titanic acid ion exchanger against beta-ray irradiation were evaluated through electron beam irradiation, elution behaviour of Sr after the irradiation and local structural analysis of the titanate. 1.4 MGy irradiation led to 1% of Sr elution, and the elution could be attributed to defects of O in the titanate induced by the irradiation. Chemical state of Ti of the titanate must be stable up to 2.7 MGy irradiation. (author)

  9. Manufacturing Demonstration Facility: Low Temperature Materials Synthesis

    International Nuclear Information System (INIS)

    Graham, David E.; Moon, Ji-Won; Armstrong, Beth L.; Datskos, Panos G.; Duty, Chad E.; Gresback, Ryan; Ivanov, Ilia N.; Jacobs, Christopher B.; Jellison, Gerald Earle; Jang, Gyoung Gug; Joshi, Pooran C.; Jung, Hyunsung; Meyer, Harry M.; Phelps, Tommy

    2015-01-01

    The Manufacturing Demonstration Facility (MDF) low temperature materials synthesis project was established to demonstrate a scalable and sustainable process to produce nanoparticles (NPs) for advanced manufacturing. Previous methods to chemically synthesize NPs typically required expensive, high-purity inorganic chemical reagents, organic solvents and high temperatures. These processes were typically applied at small laboratory scales at yields sufficient for NP characterization, but insufficient to support roll-to-roll processing efforts or device fabrication. The new NanoFermentation processes described here operated at a low temperature (~60 C) in low-cost, aqueous media using bacteria that produce extracellular NPs with controlled size and elemental stoichiometry. Up-scaling activities successfully demonstrated high NP yields and quality in a 900-L pilot-scale reactor, establishing this NanoFermentation process as a competitive biomanufacturing strategy to produce NPs for advanced manufacturing of power electronics, solid-state lighting and sensors.

  10. Manufacturing Demonstration Facility: Low Temperature Materials Synthesis

    Energy Technology Data Exchange (ETDEWEB)

    Graham, David E. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Moon, Ji-Won [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Armstrong, Beth L. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Datskos, Panos G. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Duty, Chad E. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Gresback, Ryan [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Ivanov, Ilia N. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Jacobs, Christopher B. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Jellison, Gerald Earle [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Jang, Gyoung Gug [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Joshi, Pooran C. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Jung, Hyunsung [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Meyer, III, Harry M. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Phelps, Tommy [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2015-06-30

    The Manufacturing Demonstration Facility (MDF) low temperature materials synthesis project was established to demonstrate a scalable and sustainable process to produce nanoparticles (NPs) for advanced manufacturing. Previous methods to chemically synthesize NPs typically required expensive, high-purity inorganic chemical reagents, organic solvents and high temperatures. These processes were typically applied at small laboratory scales at yields sufficient for NP characterization, but insufficient to support roll-to-roll processing efforts or device fabrication. The new NanoFermentation processes described here operated at a low temperature (~60 C) in low-cost, aqueous media using bacteria that produce extracellular NPs with controlled size and elemental stoichiometry. Up-scaling activities successfully demonstrated high NP yields and quality in a 900-L pilot-scale reactor, establishing this NanoFermentation process as a competitive biomanufacturing strategy to produce NPs for advanced manufacturing of power electronics, solid-state lighting and sensors.

  11. Technology of irradiation of liquids by electron beams

    International Nuclear Information System (INIS)

    Tofaute, K.

    1979-01-01

    The methods of pretreatment, the technical details of the irradiating equipment, the applied radiation doses and the general requirements of the effectively working system are described. The extent of reinfection is compared in cases of heat-treated and electron-irradiated mud. The latter method gave significantly better results. (L.E.)

  12. Regeneration of used activated carbon by electron beam irradiation

    International Nuclear Information System (INIS)

    Arai, H.; Hosono, M.; Zhu, G.; Miyata, T.

    1992-01-01

    The adsorbing power of granular activated carbons which adsorbed sodium laurylsulfate were most effectively recovered by irradiation of high energy electron beams in nitrogen stream, and the carbon was hardly lost by irradiation. The regeneration was induced mainly by microscopic heating of adsorption sites. Regeneration was also confirmed by adsorption endotherms. Regeneration cost was tentatively evaluated. (author)

  13. Effects of electron beam irradiation on tin dioxide gas sensors

    Indian Academy of Sciences (India)

    WINTEC

    sensitivity increases more rapidly under high doses of irra- diation than under low doses of irradiation. The electron beam irradiation effects were simulated and the mecha- nism was discussed. Acknowledgements. The authors gratefully acknowledge financial support from the MOST 973 program, grant no. 2006CB705604 ...

  14. Electron spin resonance in neutron-irradiated graphite. Dependence on temperature and effect of annealing; Resonance paramagnetique du graphite irradie aux neutrons. Variation en fonction de la temperature et experiences de recuit

    Energy Technology Data Exchange (ETDEWEB)

    Kester, T [Commissariat a l' Energie Atomique, Grenoble (France). Centre d' Etudes Nucleaires, Laboratoire de resonance magnetique

    1967-09-01

    The temperature dependence of the electron spin resonance signal from neutron irradiated graphite has been studied. The results lead to an interpretation of the nature of the paramagnetic centers created by irradiation. In annealing experiments on graphite samples, which had been irradiated at low temperature, two annealing peaks and one anti-annealing peak were found. Interpretations are proposed for these peaks. (author) [French] Le graphite irradie aux neutrons a ete etudie par resonance paramagnetique electronique en fonction de la temperature. La nature des centres paramagnetiques crees par irradiation est interpretee a l'aide des resultats. Des experiences de recuit sur des echantillons de graphite irradie a 77 deg. K ont permis de mettre en evidence deux pics de recuit et un pic d'anti-recuit, pour lesquels des interpretations sont proposees. (auteur)

  15. Low temperature and self catalytic growth of ultrafine ITO nanowires by electron beam evaporation method and their optical and electrical properties

    International Nuclear Information System (INIS)

    Kumar, R. Rakesh; Rao, K. Narasimha; Rajanna, K.; Phani, A.R.

    2014-01-01

    Highlights: • ITO nanowires were grown by e-beam evaporation method. • ITO nanowires growth done at low substrate temperature of 350 °C. • Nanowires growth was carried out without use of catalyst and reactive oxygen gas. • Nanowires growth proceeds via self catalytic VLS growth. • Grown nanowires have diameter 10–20 nm and length 1–4 μm long. • ITO nanowire films have shown good antireflection property. - Abstract: We report the self catalytic growth of Sn-doped indium oxide (ITO) nanowires (NWs) over a large area glass and silicon substrates by electron beam evaporation method at low substrate temperatures of 250–400 °C. The ITO NWs growth was carried out without using an additional reactive oxygen gas and a metal catalyst particle. Ultrafine diameter (∼10–15 nm) and micron long ITO NWs growth was observed in a temperature window of 300–400 °C. Transmission electron microscope studies confirmed single crystalline nature of the NWs and energy dispersive spectroscopy studies on the NWs confirmed that the NWs growth proceeds via self catalytic vapor-liquid-solid (VLS) growth mechanism. ITO nanowire films grown on glass substrates at a substrate temperature of 300–400 °C have shown ∼2–6% reflection and ∼70–85% transmission in the visible region. Effect of deposition parameters was systematically investigated. The large area growth of ITO nanowire films would find potential applications in the optoelectronic devices

  16. Space-charge dynamics of polymethylmethacrylate under electron beam irradiation

    CERN Document Server

    Gong, H; Ong, C K

    1997-01-01

    Space-charge dynamics of polymethylmethacrylate (PMMA) under electron beam irradiation has been investigated employing a scanning electron microscope. Assuming a Gaussian space-charge distribution, the distribution range (sigma) has been determined using a time-resolved current method in conjunction with a mirror image method. sigma is found to increase with irradiation time and eventually attain a stationary value. These observations have been discussed by taking into account radiation-induced conductivity and charge mobility. (author)

  17. Automatic low-temperature calorimeter

    International Nuclear Information System (INIS)

    Malyshev, V.M.; Mil'ner, G.A.; Shibakin, V.F.; Sorkin, E.L.

    1986-01-01

    This paper describes a low-temperature adiabatic calorimeter with a range of 1.5-500K. The system for maintaining adiabatic conditions is implemented by two resitance thermometers, whose sensitivity at low temperatures is several orders higher than that of thermocouples. The calorimeter cryostat is installed in an STG-40 portable Dewar flask. The calorimeter is controlled by an Elektronika-60 microcomputer. Standard platinum and germanium thermometers were placed inside of the calorimeter to calibrate the thermometers of the calorimeter and the shield, and the specific heats of specimens of OSCh 11-4 copper and KTP-8 paste were measured to demonstrate the possibilities of the described calorimeter. Experience with the calorimeter has shown that a thorough study of the dependence of heat capacity on temperature (over 100 points for one specimen) can be performed in one or two dats

  18. Method of determining the position of an irradiated electron beam

    International Nuclear Information System (INIS)

    Fukuda, Wataru.

    1967-01-01

    The present invention relates to the method of determining the position of a radiated electron beam, in particular, the method of detecting the position of a p-n junction by a novel method when irradiating the electron beam on to the semi-conductor wafer, controlling the position of the electron beam from said junction. When the electron beam is irradiated on to the semi-conductor wafer which possesses the p-n junction, the position of the p-n junction may be ascertained to determine the position of the irradiated electron beam by detecting the electromotive force resulting from said p-n junction with a metal disposed in the proximity of but without mechanical contact with said semi-conductor wafer. Furthermore, as far as a semi-conductor wafer having at least one p-n junction is concerned, the present invention allows said p-n junction to be used to determine the position of an irradiated electron beam. Thus, according to the present invention, the electromotive force of the electron beam resulting from the p-n junction may easily be detected by electrostatic coupling, enabling the position of the irradiated electron beam to be accurately determined. (Masui, R.)

  19. Waste treatment by microwave and electron beam irradiation

    International Nuclear Information System (INIS)

    Martin, D.; Craciun, G.; Manaila, E.; Ighigeanu, D; Oproiu, C.; Iacob, N.; Togoe, I.; Margaritescu, I.

    2007-01-01

    Comparative results obtained by applying separate and combined (successive and simultaneous) electron beam (EB) and microwave (MW) irradiation to waste treatment, such as food residuals (minced beef, wheat bran and wheat flour) and sewage sludge performed from a food industry wastewater treatment station (vegetable oil plant), are presented. The research results demonstrated that the simultaneous EB and MW irradiation produces the biggest reduction of microorganisms. The tests also demonstrated that the irradiation time and the upper limit of required EB absorbed dose, which ensures a complete sterilization effect, could be reduced by a factor of two by an additional use of MW energy to EB irradiation

  20. Sterilization of ground spices by electron beams irradiation

    International Nuclear Information System (INIS)

    Hashigiwa, Masayuki; Nakachi, Ayako; Kobayashi, Hiroshi

    1999-01-01

    Each ground spice (Black Pepper, Turmeric, Ginger, Paprika and Basil), which was packaged into polyethylene film, was irradiated by electron beams at 5 different levels: 2, 4, 6, 8 and 10 kGy. Bacteriological tests for total bacterial count were carried out on spices before and after irradiation, but the tests for microfiora were carried out only before irradiation. Total bacterial count decreased in proportion to the level of electron beams. But the decreasing rate for Turmeric, Ginger and Basil was lower compared with that of other spices. The reason seems that rate of contamination by B. pumilus, which is thought as radiation resistant bacteria, was higher on these spices. (author)

  1. Sterilization of ground spices by electron beams irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Hashigiwa, Masayuki; Nakachi, Ayako; Kobayashi, Hiroshi [K. Kobayashi and Co., Ltd., Kako, Hyogo (Japan)

    1999-09-01

    Each ground spice (Black Pepper, Turmeric, Ginger, Paprika and Basil), which was packaged into polyethylene film, was irradiated by electron beams at 5 different levels: 2, 4, 6, 8 and 10 kGy. Bacteriological tests for total bacterial count were carried out on spices before and after irradiation, but the tests for microfiora were carried out only before irradiation. Total bacterial count decreased in proportion to the level of electron beams. But the decreasing rate for Turmeric, Ginger and Basil was lower compared with that of other spices. The reason seems that rate of contamination by B. pumilus, which is thought as radiation resistant bacteria, was higher on these spices. (author)

  2. The reaction rates of electrons with native and irradiated ribonuclease

    International Nuclear Information System (INIS)

    Schuessler, H.; Ebert, M.; Davies, J.V.

    1977-01-01

    The rate of reaction of hydrated electrons with proteins depends, amongst other things, on the conformational structure of the protein, and irradiation itself causes conformational changes in proteins. A study has been made of variations in the reaction rates of hydrated electrons with RNase pre-irradiated by the Linac or by a 60 Co γ-source. The reaction rate constants varied with the pre-irradiation dose, the concentration of phosphate buffer, the enzyme concentration and also the presence of 10 -2 M ethanol. These variations serve to emphasize the importance of the tertiary structure of biological molecules in irradiation processes and have significant implications in the mathematical analysis of the inactivation of enzymes in steady-state irradiation processes. (U.K.)

  3. An easy-to-fabricate low-temperature TiO2 electron collection layer for high efficiency planar heterojunction perovskite solar cells

    Directory of Open Access Journals (Sweden)

    B. Conings

    2014-08-01

    Full Text Available Organometal trihalide perovskite solar cells arguably represent the most auspicious new photovoltaic technology so far, as they possess an astonishing combination of properties. The impressive and brisk advances achieved so far bring forth highly efficient and solution processable solar cells, holding great promise to grow into a mature technology that is ready to be embedded on a large scale. However, the vast majority of state-of-the-art perovskite solar cells contains a dense TiO2 electron collection layer that requires a high temperature treatment (>450 °C, which obstructs the road towards roll-to-roll processing on flexible foils that can withstand no more than ∼150 °C. Furthermore, this high temperature treatment leads to an overall increased energy payback time and cumulative energy demand for this emerging photovoltaic technology. Here we present the implementation of an alternative TiO2 layer formed from an easily prepared nanoparticle dispersion, with annealing needs well within reach of roll-to-roll processing, making this technology also appealing from the energy payback aspect. Chemical and morphological analysis allows to understand and optimize the processing conditions of the TiO2 layer, finally resulting in a maximum obtained efficiency of 13.6% for a planar heterojunction solar cell within an ITO/TiO2/CH3NH3PbI3-xClxpoly(3-hexylthiophene/Ag architecture.

  4. Strengthening of Poly Methyl Methacrylate (PMMA) through Electron Irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Yoo, Sung Ho; Lim, Hyung San; Ha, Jun Mok; Cho, Sung Oh [KAIST, Daejeon (Korea, Republic of)

    2015-05-15

    Poly Methyl Methacrylate (PMMA) was previously known to show the deteriorating mechanical properties when irradiated with electrons. This is true for low electron irradiation does, but it was found, through experimentation, that at high irradiation dose, PMMA demonstrates improved mechanical properties. With enough electron irradiation dose, the scissions can form new links amongst one another to achieve stability that surpasses that of the PMMA in pre-irradiation treatment state. With higher irradiation dosage and beam strength, hardness of irradiated PMMA could be increased to a much greater extent. Electrons with 50keV of energy can only penetrate around 30 μm of PMMA, thus increasing the beam energy could potentially allow for hardening of not just the surface of the PMMA samples, but the whole samples themselves. Furthermore, Pencil Hardness Test is a method to roughly analyze a material's hardness and does not provide an accurate feedback on the mechanical properties of the material of interest. Hence, a more thorough and effective method of measuring data from the use of equipment such as IZOD Impact Tester, Strain-Stress Tester and Haze Meter will be utilized in the future.

  5. Application of electron beam irradiation, (1). Development and application of electron beam processors

    International Nuclear Information System (INIS)

    Katsumura, Yosuke

    1994-01-01

    This paper deals with characteristics, equipment (principle and kinds), present conditions, and future issues in the application of electron beam irradiation. Characteristics of electron beams are described in terms of the following: chemical and biological effects of radiation; energy and penetrating power of electron beams; and principle and kinds of electron beam accelerator. Industrial application of electron beam irradiation has advantages of high speed procedure and producibility, less energy, avoidance of poisonous gas, and extreme reduction of organic solvents to be used. The present application of electron beam irradiation cen be divided into the following: (1) hardening of resin or coated membrane; (2) improvement of macromolecular materials; (3) environmental protection; (4) sterilization; (5) food sterilization. The present equipment for electron beam irradiation is introduced according to low energy, medium energy, and high energy equipment. Finally, future issues focuses on (1) the improvement of traceability system and development of electron dosimetric techniques and (2) food sterilization. (N.K.)

  6. Electrical properties of gallium arsenide irradiated with electrons and neutrons

    International Nuclear Information System (INIS)

    Kol'chenko, T.I.; Lomako, V.M.

    1975-01-01

    A study was made of changes in the electrical properties of GaAs doped with Te, S, Se, Si, Ge, Sn (n 0 approximately 10 16 -10 18 cm -3 ) and irradiated either with 2.5-28 MeV electrons or with fast reactor neutrons. An analysis of changes in the electron density indicated that the rate of carrier removal by electron bombardment was independent of the dopant but was governed by isolated radiation defects. The change in the mobility due to irradiation with 2.5-10 MeV electrons was also governed by isolated defects. When the electron energy was increased to 28 MeV the main contribution to the change in the mobility was made by defect clusters. In the neutron-irradiation case the changes in the carrier density and mobility were mainly due to defect clusters and the nature of changes in the electrical properties was again independent of the dopant

  7. Electron irradiation effect on single crystal of niobium

    International Nuclear Information System (INIS)

    Otero, M.P.; Lucki, G.

    1984-01-01

    The effect of electron irradiation (900 KeV) on gliding dislocations of single crystal Nb with its tensile axe in the [941] orientation was observed for the in-situ deformation in a high voltage electron microscope (HVEM) at Argonne National Laboratory. The experimental was carried out by the 1 hour-electron irradiation with no stress applied. Straight dislocations actuating as sinks for the electron produced defects became helicoidal as the irradiation proceeded. Frenkel pairs were created in Nb for electron energies > = 650 KeV and, as the single vacancies do not undergo long-range migration in Nb at temperatures much below 620 K, the defects that are entrapped by the dislocations are self-interstitials produced by electron displacement. Applying the stress it was possible to observe that modified dislocations did not glide while the dislocations not affected by the irradiation are visibly in movement. This important result explains the neutron and electron-irradiation induced work-hardening effect for Nb that was previously observed. (Author) [pt

  8. Electron microscope study of irradiated beryllium oxide

    International Nuclear Information System (INIS)

    Bisson, A.A.

    1965-06-01

    The beryllium oxide is studied first by fractography, before and after irradiation, using sintered samples. The fractures are examined under different aspects. The higher density sintered samples, with transgranular fractures are the most interesting for a microscopic study. It is possible to mark the difference between the 'pores' left by the sintering process and the 'bubbles' of gases that can be produced by former thermal treatments. After irradiation, the grain boundaries are very much weakened. By annealing, it is possible to observe the evolution of the gases produced by the reaction (n, 2n) and (n. α) and gathered on the grain boundaries. The irradiated beryllium oxide is afterwards studied by transmission. For that, a simple method has been used: little chips of the crushed material are examined. Clusters of point defects produced by neutrons are thus detected in crystals irradiated at the three following doses: 6 x 10 19 , 9 x 10 19 and 2 x 10 20 n f cm -2 at a temperature below 100 deg. C. For the irradiation at 6 x 10 19 n f cm -2 , the defects are merely visible, but at 2 x l0 20 n f cm -2 the crystals an crowded with clusters and the Kikuchi lines have disappeared from the micro-diffraction diagrams. The evolution of the clusters into dislocation loops is studied by a series of annealings. The activation energy (0,37 eV) calculated from the annealing curves suggests that it must be interstitials that condense into dislocation loops. Samples irradiated at high temperatures (650, 900 and 1100 deg. C) are also studied. In those specimens the size of the loops is not the same as the equilibrium size obtained after out of pile annealing at the same temperature. Those former loops are more specifically studied and their Burgers vector is determined by micro-diffraction. (author) [fr

  9. Introduction and recovery of point defects in electron-irradiated ZnO

    International Nuclear Information System (INIS)

    Tuomisto, F.; Saarinen, K.; Look, D.C.; Farlow, G.C.

    2005-01-01

    We have used positron annihilation spectroscopy to study the introduction and recovery of point defects in electron-irradiated n-type ZnO. The irradiation (E el =2 MeV, fluence 6x10 17 cm -2 ) was performed at room temperature, and isochronal annealings were performed from 300 to 600 K. In addition, monochromatic illumination of the samples during low-temperature positron measurements was used in identification of the defects. We distinguish two kinds of vacancy defects: the Zn and O vacancies, which are either isolated or belong to defect complexes. In addition, we observe negative-ion-type defects, which are attributed to O interstitials or O antisites. The Zn vacancies and negative ions act as compensating centers and are introduced at a concentration [V Zn ]≅c ion ≅2x10 16 cm -3 . The O vacancies are introduced at a 10-times-larger concentration [V O ]≅3x10 17 cm -3 and are suggested to be isolated. The O vacancies are observed as neutral at low temperatures, and an ionization energy of 100 meV could be fitted with the help of temperature-dependent Hall data, thus indicating their deep donor character. The irradiation-induced defects fully recover after the annealing at 600 K, in good agreement with electrical measurements. The Zn vacancies recover in two separate stages, indicating that the Zn vacancies are parts of two different defect complexes. The O vacancies anneal simultaneously with the Zn vacancies at the later stage, with an activation energy of E V,O m =1.8±0.1 eV. The negative ions anneal out between the two annealing stages of the vacancies

  10. Elemental process of amorphization induced by electron irradiation in Si

    International Nuclear Information System (INIS)

    Yamasaki, Jun; Takeda, Seiji; Tsuda, Kenji

    2002-01-01

    We recently found that amorphization is induced in Si by electron irradiation. Examining the amorphization systematically, we have established the diagram of steady states under electron irradiation, either amorphous Si (a-Si) or crystalline Si (c-Si) as a function of incident electron energy, electron dose, and irradiation temperature. Utilizing transmission electron microscopy, electron energy filtered diffraction and electron energy-loss spectroscopy, we have characterized the atomic structure, the electronic structure, and the thermal stability of a-Si induced by electron irradiation. Based on the experimental data, we have also concluded that the amorphization is caused by the accumulation of not point defects but small cascade damages. Analyzing the change in the intensity of halo diffraction rings during amorphization, we have clarified that the smallest cascade damage that contributes to amorphization includes only about four Si atoms. This presumably supports the amorphization mechanism that four self-interstitial atoms form the quasistable structure I4 in c-Si and it becomes an amorphous embryo

  11. Primary photoluminescence in as-neutron (electron) -irradiated n-type 6H-SiC

    International Nuclear Information System (INIS)

    Zhong, Z.Q.; Wu, D.X.; Gong, M.; Wang, O.; Shi, S.L.; Xu, S.J.; Chen, X.D.; Ling, C.C.; Fung, S.; Beling, C.D.; Brauer, G.; Anwand, W.; Skorupa, W.

    2006-01-01

    Low-temperature photoluminescence spectroscopy has revealed a series of features labeled S 1 , S 2 , S 3 in n-type 6H-SiC after neutron and electron irradiation. Thermal annealing studies showed that the defects S 1 , S 2 , S 3 disappeared at 500 deg. C. However, the well-known D 1 center was only detected for annealing temperatures over 700 deg. C. This experimental observation not only indicated that the defects S 1 , S 2 , S 3 were a set of primary defects and the D 1 center was a kind of secondary defect, but also showed that the D 1 center and the E 1 , E 2 observed using deep level transient spectroscopy might not be the same type of defects arising from the same physical origin

  12. Paraelasticity in electron-irradiated molybdenum

    International Nuclear Information System (INIS)

    Beuneu, Brigitte; Quere, Yves.

    1981-11-01

    The relaxation of a radiation-induced point defect-most probably the rotation of a dumbell-is observed during isothermal anneals of irradiated molybdenum by resistivity measurements. The recovery of close pairs is not affected, in first analysis, by the presence of a uniaxial stress

  13. Electron microscopy at reduced levels of irradiation

    International Nuclear Information System (INIS)

    Kuo, I.A.M.

    1975-05-01

    Specimen damage by electron radiation is one of the factors that limits high resolution electron microscopy of biological specimens. A method was developed to record images of periodic objects at a reduced electron exposure in order to preserve high resolution structural detail. The resulting image would tend to be a statistically noisy one, as the electron exposure is reduced to lower and lower values. Reconstruction of a statistically defined image from such data is possible by spatial averaging of the electron signals from a large number of identical unit cells. (U.S.)

  14. Thermoluminescent system for low temperatures

    International Nuclear Information System (INIS)

    Rosa, L.A.R. da; Caldas, L.V.E.; Leite, N.G.

    1988-09-01

    A system for measurements of the thermoluminescent glow curve, the thermoluminescent emission spectrum and the optical absorption spectrum of solid samples, from liquid nitrogen temperature up to 473 K, is reported. A specially designed temperature programmer provides a linear heating of the sample at a wide range of selectable heating rates, as also long term steady-state temperatures for annealing and isothermal decay studies. The system operates at a pressure of 1.33 x 10 -3 Pa. Presently it is being used for lithium fluoride low temperature thermoluminescent studies. (author) [pt

  15. Mechanical pumping at low temperature

    International Nuclear Information System (INIS)

    Perin, J.P.; Claudet, G.; Disdier, F.

    1995-01-01

    This novel concept consist of a mechanical pump able to run at low temperature (25K). Since gas density varies inversely with temperature, this pump would deliver much higher mass flow rate than at room temperature for a given size. Advantages of this concept are order of magnitude reduction in size, weight, when compared to a conventional pump scaled to perform the same mass flow rate at room temperature. This pump would be a solution to allow continuously tritium extraction and minimize the mass inventory. (orig.)

  16. Ammonia synthesis at low temperatures

    DEFF Research Database (Denmark)

    Rod, Thomas Holm; Logadottir, Ashildur; Nørskov, Jens Kehlet

    2000-01-01

    have been carried out to evaluate its feasibility. The calculations suggest that it might be possible to catalytically produce ammonia from molecular nitrogen at low temperatures and pressures, in particular if energy is fed into the process electrochemically. (C) 2000 American Institute of Physics.......Density functional theory (DFT) calculations of reaction paths and energies for the industrial and the biological catalytic ammonia synthesis processes are compared. The industrial catalyst is modeled by a ruthenium surface, while the active part of the enzyme is modeled by a MoFe6S9 complex...

  17. Polymerization of vinyl stearate multilayers by electron beam irradiation

    International Nuclear Information System (INIS)

    Nishii, Masanobu; Hatada, Motoyoshi

    1975-01-01

    Studies on the radiation-induced polymerization of vinyl stearate (VST) multilayers were carried out. The VST multilayers built-up on an aluminum plated glass plate by Langmuir-Blodgett technique were irradiated with electron beams from a Van de Graaff electron accelerator in nitrogen atmosphere. The structure of the multilayers and the effects of irradiation were investigated by X-ray diffractometry, contact angle measurement, multireflection infrared spectroscopy, and scanning electron microscopy. The VST multilayers became insoluble to methanol by the irradiation, and the multi-reflection infrared spectrum of the VST multilayers turned into that of poly (VST) with increasing dosage. The polymerization proceeded during the irradiation at the temperature range between -10 0 and 10 0 C, and the conversion attained to 90% within 2.5 minutes (total dose, 5.6 Mrads). The multilayers irradiated above 13 Mrads turned into the polymer film insoluble to benzene, indicating that the polymer chains were cross-linked by the irradiation. Stearic acid which was formed by the irradiation of VST at nitrogen-water interface as a hydrolysis product was not detected in this system. (auth.)

  18. Postharvest quality of cut roses following electron-beam irradiation

    International Nuclear Information System (INIS)

    Chang, A.Y.; Gladon, R.J.; Gleason, M.L.; Parker, S.K.; Agnew, N.H.; Olson, D.G.

    1997-01-01

    Cut Rosa x hybrida L. 'Royalty' flowers were used to determine the efficacy of electron-beam irradiation for increasing postharvest quality and decreasing petal infection by Botrytis cinerea Pers. In an experiment for determining the injury threshold, roses received electron-beam irradiation of 0, 0.5, 1, 2, and 4 kGy. Irradiation dosages greater than or equal to 4 kGy caused necrosis on petal tissue and decreased postharvest life at 20 degrees C. In a second experiment to evaluate postharvest quality, roses were irradiated at 0, 0.25, 0.5, 0.75, and 1 kGy. Dosages of 0.25 and 0.5 kGy slowed the rate of flower bud opening for 2 days but did not decrease postharvest quality when compared with nonirradiated roses. Roses that received irradiation dosages of 0.75 and 1 kGy showed unacceptable quality. In a third experiment, roses that had or had not been inoculated with B. cinerea were irradiated at 0, 0.25, 0.5, and 0.75 kGy. Irradiation did not control B. cinerea populations, and rose quality decreased as dosage increased. In a fourth experiment to determine the effect of irradiation on B. cinerea, conidia on water-agar plates exposed to dosages less than or equal to 1, 2, and 4 kGy germinated at rates of approximately 90%, 33%, and 2%, respectively, within 24 h

  19. Preparation of PbSe nanoparticles by electron beam irradiation

    Indian Academy of Sciences (India)

    A novel method has been developed by electron beam irradiation to prepare PbSe nanoparticles. 2 MeV 10mA GJ-2-II electronic accelerator was used as radiation source. Nanocrystalline PbSe was prepared rapidly at room temperature under atmospheric pressure without any kind of toxic reagents. The structure and ...

  20. Silver nanoparticles: synthesis and size control by electron irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Bogle, K A; Dhole, S D; Bhoraskar, V N [Microtron Accelerator Laboratory, Department of Physics, University of Pune, Pune-411007 (India)

    2006-07-14

    Silver nanoparticles were synthesized by irradiating solutions, prepared by mixing AgNO{sub 3} and poly-vinyl alcohol (PVA), with 6 MeV electrons. The electron-irradiated solutions and the thin coatings cast from them were characterized using the ultraviolet-visible (UV-vis), x-ray diffraction (XRD), transmission electron microscopy (TEM) and scanning electron microscopy (SEM) techniques. During electron irradiation, the process of formation of the silver nanoparticles appeared to be initiated at an electron fluence of {approx}2 x 10{sup 13} e cm{sup -2}. This was evidenced from the solution, which turned yellow and exhibited the characteristic plasmon absorption peak around 455 nm. Silver nanoparticles of different sizes in the range 60-10 nm, with a narrow size distribution, could be synthesized by varying the electron fluence from 2 x 10{sup 13} to 3 x 10{sup 15} e cm{sup -2}. Silver nanoparticles of sizes in the range 100-200 nm were also synthesized by irradiating an aqueous AgNO{sub 3} solution with 6 MeV electrons.

  1. Total Dose Effects on Bipolar Integrated Circuits at Low Temperature

    Science.gov (United States)

    Johnston, A. H.; Swimm, R. T.; Thorbourn, D. O.

    2012-01-01

    Total dose damage in bipolar integrated circuits is investigated at low temperature, along with the temperature dependence of the electrical parameters of internal transistors. Bandgap narrowing causes the gain of npn transistors to decrease far more at low temperature compared to pnp transistors, due to the large difference in emitter doping concentration. When irradiations are done at temperatures of -140 deg C, no damage occurs until devices are warmed to temperatures above -50 deg C. After warm-up, subsequent cooling shows that damage is then present at low temperature. This can be explained by the very strong temperature dependence of dispersive transport in the continuous-time-random-walk model for hole transport. For linear integrated circuits, low temperature operation is affected by the strong temperature dependence of npn transistors along with the higher sensitivity of lateral and substrate pnp transistors to radiation damage.

  2. 'The future of the electron beam irradiation service business'

    International Nuclear Information System (INIS)

    Yamase, Yutaka

    1998-01-01

    The high energy electron beam has less penetration power in comparison with the gamma ray which has been used from before. However, the dose rate of the electron beam is considerably high in comparison with the gamma ray with more than several thousand times. Therefore, the irradiation of the product can be done in a short time, and there are cheap characteristics further in the irradiation cost as well. And, an electron beam is the technology which is very easy to accept in the country of a nuclear allergy constitution like our country so that it may not use radioactive substance. This time, I'd like to think about the present condition of the electron beam irradiation service business and a future based on the experience of Tsukuba EBcenter until now. (J.P.N.)

  3. Electron beam dosimetry for a thin-layer absorber irradiated by 300-keV electrons

    International Nuclear Information System (INIS)

    Kijima, Toshiyuki; Nakase, Yoshiaki

    1993-01-01

    Depth-dose distributions in thin-layer absorbers were measured for 300-keV electrons from a scanning-type irradiation system, the electrons having penetrated through a Ti-window and an air gap. Irradiations of stacks of cellulose triacetate(CTA) film were carried out using either a conveyor (i.e. dynamic irradiation) or fixed (i.e. static) irradiation. The sample was irradiated using various angles of incidence of electrons, in order to examine the effect of obliqueness of electron incidence at low-energy representative of routine radiation curing of thin polymeric or resin layers. Dynamic irradiation gives broader and shallower depth-dose distributions than static irradiation. Greater obliqueness of incident electrons gives results that can be explained in terms of broader and shallower depth-dose distributions. The back-scattering of incident electrons by a metal(Sn) backing material enhances the absorbed dose in a polymeric layer and changes the overall distribution. It is suggested that any theoretical estimations of the absorbed dose in thin layers irradiated in electron beam curing must be accomplished and supported by experimental data such as that provided by this investigation. (Author)

  4. Low Temperature Waste Immobilization Testing Vol. I

    Energy Technology Data Exchange (ETDEWEB)

    Russell, Renee L.; Schweiger, Michael J.; Westsik, Joseph H.; Hrma, Pavel R.; Smith, D. E.; Gallegos, Autumn B.; Telander, Monty R.; Pitman, Stan G.

    2006-09-14

    The Pacific Northwest National Laboratory (PNNL) is evaluating low-temperature technologies to immobilize mixed radioactive and hazardous waste. Three waste forms—alkali-aluminosilicate hydroceramic cement, “Ceramicrete” phosphate-bonded ceramic, and “DuraLith” alkali-aluminosilicate geopolymer—were selected through a competitive solicitation for fabrication and characterization of waste-form properties. The three contractors prepared their respective waste forms using simulants of a Hanford secondary waste and Idaho sodium bearing waste provided by PNNL and characterized their waste forms with respect to the Toxicity Characteristic Leaching Procedure (TCLP) and compressive strength. The contractors sent specimens to PNNL, and PNNL then conducted durability (American National Standards Institute/American Nuclear Society [ANSI/ANS] 16.1 Leachability Index [LI] and modified Product Consistency Test [PCT]) and compressive strength testing (both irradiated and as-received samples). This report presents the results of these characterization tests.

  5. Behaviour of some fresh fruits under electron-beam irradiation

    International Nuclear Information System (INIS)

    Ferdes, O.; Stroia, A.L.; Potcoava, A.; Cojocaru, M.; Mihnea, R.; Oproiu, C.

    1994-01-01

    The use of ionizing radiation in preservation of fruits and vegetables is widely recognized. In this paper it is presented a study of the effect of electron-beam irradiation of some fresh, early and perishable fruits, like strawberries, cherries, and sour cherries concerning their shelf-life time extension. The irradiations were performed on common varieties in normal conditions to the IPTRD's electron-beam accelerator (Bucharest-Magurele) having the following parameters: flow current 10 μA, power 60 W and electron mean energy 6.23 MeV. The irradiation doses varied between 0.5-3.0 kGy and the dose rates between 100-1500 Gy/min. It was observed the fruit preservation capability of the treatment and it was analysed the main characteristics as organoleptic properties, weight of dry component, acidity, total and reducing sugars, ascorbic acid content and others. It was evidenced an increase in freshness and shelf-life extension by 5-7 days for strawberries and up to two weeks for cherries without any significant changes in the values of the considered parameters. Otherwise, for the applied doses, the electron-beam irradiation did not produce any significant changes in the values of fruit characteristic parameters. The results lead to the conclusion that the electron-beam irradiation is a good technological solution for fresh fruit processing. (Author) 1 Tab., 7 Refs

  6. Electron beam irradiation of gemstone for color enhancement

    Science.gov (United States)

    Idris, Sarada; Ghazali, Zulkafli; Hashim, Siti A'iasah; Ahmad, Shamshad; Jusoh, Mohd Suhaimi

    2012-09-01

    Numerous treatment of gemstones has been going on for hundreds of years for enhancing color and clarity of gems devoid of these attributes. Whereas previous practices included fraudulent or otherwise processes to achieve the color enhancement, the ionizing radiation has proven to be a reliable and reproducible technique. Three types of irradiation processes include exposure to gamma radiation, electron beam irradiation and the nuclear power plants. Electron Beam Irradiation of Gemstone is a technique in which a gemstone is exposed to highly ionizing radiation electron beam to knock off electrons to generate color centers culminating in introduction of deeper colors. The color centers may be stable or unstable. Below 9MeV, normally no radioactivity is introduced in the exposed gems. A study was conducted at Electron Beam Irradiation Centre (Alurtron) for gemstone color enhancement by using different kind of precious gemstones obtained from Pakistan. The study shows that EB irradiation not only enhances the color but can also improves the clarity of some type of gemstones. The treated stones included kunzite, tourmaline, topaz, quartz, aquamarine and cultured pearls. Doses ranging from 25 kGy to 200 KGy were employed to assess the influence of doses on color and clarity and to select the optimum doses. The samples used included both the natural and the faceted gemstones. It is concluded that significant revenue generation is associated with the enhancement of the color in clarity of gemstones which are available at very cheap price in the world market.

  7. Electron beam irradiation of gemstone for color enhancement

    Energy Technology Data Exchange (ETDEWEB)

    Idris, Sarada; Ghazali, Zulkafli; Hashim, Siti A' iasah; Ahmad, Shamshad; Jusoh, Mohd Suhaimi [Malaysian Nuclear Agency, Bangi, Selangor (Malaysia); School of Chemicals and Material Engineering, NUST Islamabad (Pakistan); Malaysian Nuclear Agency, Bangi, Selangor (Malaysia)

    2012-09-26

    Numerous treatment of gemstones has been going on for hundreds of years for enhancing color and clarity of gems devoid of these attributes. Whereas previous practices included fraudulent or otherwise processes to achieve the color enhancement, the ionizing radiation has proven to be a reliable and reproducible technique. Three types of irradiation processes include exposure to gamma radiation, electron beam irradiation and the nuclear power plants. Electron Beam Irradiation of Gemstone is a technique in which a gemstone is exposed to highly ionizing radiation electron beam to knock off electrons to generate color centers culminating in introduction of deeper colors. The color centers may be stable or unstable. Below 9MeV, normally no radioactivity is introduced in the exposed gems. A study was conducted at Electron Beam Irradiation Centre (Alurtron) for gemstone color enhancement by using different kind of precious gemstones obtained from Pakistan. The study shows that EB irradiation not only enhances the color but can also improves the clarity of some type of gemstones. The treated stones included kunzite, tourmaline, topaz, quartz, aquamarine and cultured pearls. Doses ranging from 25 kGy to 200 KGy were employed to assess the influence of doses on color and clarity and to select the optimum doses. The samples used included both the natural and the faceted gemstones. It is concluded that significant revenue generation is associated with the enhancement of the color in clarity of gemstones which are available at very cheap price in the world market.

  8. Electron beam irradiation of gemstone for color enhancement

    International Nuclear Information System (INIS)

    Idris, Sarada; Ghazali, Zulkafli; Hashim, Siti A'iasah; Ahmad, Shamshad; Jusoh, Mohd Suhaimi

    2012-01-01

    Numerous treatment of gemstones has been going on for hundreds of years for enhancing color and clarity of gems devoid of these attributes. Whereas previous practices included fraudulent or otherwise processes to achieve the color enhancement, the ionizing radiation has proven to be a reliable and reproducible technique. Three types of irradiation processes include exposure to gamma radiation, electron beam irradiation and the nuclear power plants. Electron Beam Irradiation of Gemstone is a technique in which a gemstone is exposed to highly ionizing radiation electron beam to knock off electrons to generate color centers culminating in introduction of deeper colors. The color centers may be stable or unstable. Below 9MeV, normally no radioactivity is introduced in the exposed gems. A study was conducted at Electron Beam Irradiation Centre (Alurtron) for gemstone color enhancement by using different kind of precious gemstones obtained from Pakistan. The study shows that EB irradiation not only enhances the color but can also improves the clarity of some type of gemstones. The treated stones included kunzite, tourmaline, topaz, quartz, aquamarine and cultured pearls. Doses ranging from 25 kGy to 200 KGy were employed to assess the influence of doses on color and clarity and to select the optimum doses. The samples used included both the natural and the faceted gemstones. It is concluded that significant revenue generation is associated with the enhancement of the color in clarity of gemstones which are available at very cheap price in the world market.

  9. Evolution of low-temperature phases in a low-temperature structural transition of a La cuprate

    International Nuclear Information System (INIS)

    Inoue, Y.; Horibe, Y.; Koyama, Y.

    1997-01-01

    The microstructure produced by a low-temperature structural phase transition in La 1.5 Nd 0.4 Sr 0.1 CuO 4 has been examined by transmission electron microscopy with the help of imaging plates. The low-temperature transition was found to be proceeded not only by the growth of the Pccn/low-temperature-tetragonal phases nucleated along the twin boundary but also by the nucleation and growth of the phases in the interior of the low-temperature-orthorhombic domain. In addition, because the map of the octahedron tilt as an order parameter is not identical to that of the spontaneous strain accompanied by the transition, the microstructure below the transition is understood to be a very complex mixture of the low-temperature phases. copyright 1997 The American Physical Society

  10. Bulk and interface defects in electron irradiated InP

    International Nuclear Information System (INIS)

    Peng Chen; Sun Heng-hui

    1989-01-01

    Systematic studies on the structure of defects in InP caused by electron irradiation are conducted based on experimental measurements and theoretical calculations. The rates of introduction and annealing-out temperatures of In and P vancancies are estimated using proper theoretical models. These calculations reveal that after room temperature irradiation only complexes may exist. It is also supported by our experimental data that the sum of introducing rates of three detected levels are less than the theoretical value calculated for single vacancies. According to our equation on the relation between interface states and DLTS signal and from the results of computer calculation we believe that the broad peak appearing in the DLTS diagram before irradiation is related to interface states. Its disappearance after electron irradiation suggests the reduction of interface states; this is further confirmed by the reduction of surface recombination rate derived from the results of surface photovoltage measurement

  11. Manufacture of electron beam irradiation vessel and its characteristics

    International Nuclear Information System (INIS)

    Kanazawa, Takao; Haruyama, Yasuyuki; Yotsumoto, Keiichi

    1992-05-01

    Electron beam irradiation vessel, which is used for the irradiation of samples under an inert or a vacuum atmosphere, is made by considering the temperature control during or after irradiation. The vessel was composed of the temperature controlable samples supporting plate, beam slit with water cooling plate and the insert of thermosensor. The four samples supporting plate was produced with the materials made up of aluminium, stainless steel (SUS304), and copper. The stainless steel supporting plate has a heater inside the cooling pipes for the high temperature treatment of samples without exposure to atmosphere after the irradiation. In this report, the temperature distribution and dose characteristics such as dose distribution and effects of backscattered electron were studied by using several supporting plate and the comparison of the experimental results with the simulated results was also carried out. (author)

  12. Analytical electron microscopy of neutron-irradiated reactor alloys

    International Nuclear Information System (INIS)

    Thomas, L.E.

    1982-01-01

    Exposure to the high neutron fluxes and temperatures from 400 to 650 0 C in the core region of a fast breeder reactor profoundly alters the microstructure and properties of structural steels and superalloys. The development of irradiation-induced voids, dislocations and precipitates, as well as segregation of alloying elements on a microscopic scale has been related to macroscopic swelling, creep, hardening and embrittlement which occur during prolonged exposures in reactor. Microanalytical studies using TEM/STEM methods, primarily energy dispersive x-ray (EDX) microanalysis, have greatly aided understanding of alloy behavior under irradiation. The main uses of analytical electron microscopy in studying irradiated alloys have been the identification of irradiation-induced precipitates and determination of the changes in local composition due to irradiation-induced solute segregation

  13. Electron beam irradiation effect on nanostructured molecular sieve catalysts

    International Nuclear Information System (INIS)

    Yuan Zhongyong; Zhou Wuzong; Parvulescu, Viorica; Su Baolian

    2003-01-01

    Electron impact can induce chemical changes on particle surfaces of zeolites and molecular sieve catalysts. Some experimental observations of electron irradiation effect on molecular sieve catalysts are presented, e.g., electron-beam-induced growth of bare silver nanowires from zeolite crystallites, formation of vesicles in calcium phosphate, migration of microdomains in iron-oxide doped mesoporous silicas, structural transformation from mesostructured MCM-41 to microporous ZSM-5, etc. The formation mechanisms of the surface structures are discussed

  14. Clarification of leachate from reclaimed ground by electron beam irradiation

    International Nuclear Information System (INIS)

    Yamazaki, Masao; Sawai, Teruko; Shimokawa, Toshinari; Sawai, Takeshi

    1985-01-01

    To decompose organic matters such as humic acid and fulvous acid in the leachate from reclaimed ground, an electron beam irradiation technique was examined because of availability of higher dose rate than a 60 Co γ-ray source. This paper describes results of the above-mentioned preliminary examination. Test water was collected from No.15 dumping site at the Tokyo Bay. Irradiation sample was prepared by filtration with a filter and decarbonation with sulfuric acid. Fulvous acid solution by eliminating humic acid was also served for the examination. Electron beam irradiation of the sample solution was made with a Van de Graaf accelerator by 1.5 MeV, 140 Gy/sec of irradiation condition and with a dynamitron by 2.0 MeV, 25 kGy/pass of the condition. It was clarified that oxygen bubbling velocity during the irradiation did not affect much for the decrease rate of total organic matters (TOC) within 0.5 to 3.0 1/min of an experimental condition. As for radiation doses and TOC decrease, TOC was decreased much for lower dose rate irradiation (Van de Graaf accelerator), lower initial TOC concentration, or addition of hydrogen peroxide. For the combined treatment of radiation and flocculation to aim at irradiation dose decrease, fulvous acid solution was served for the test. Lower dose irradiation with a 60 Co source showed better TOC elimination and it was concluded that combination with flocculation was effective for the dose reduction. It was also found experimentally that TOC decrease behavior by the both radiation source was different due to temperature effect and further study should be made for the development of the practical electron beam irradiation technique. (Takagi, S.)

  15. (100) faceted anion voids in electron irradiated fluorite

    International Nuclear Information System (INIS)

    Johnson, E.

    1979-01-01

    High fluence electron irradiation of fluorite crystals in the temperature range 150 to 320 K results in formation of a simple cubic anion void superlattice. Above 320 K the damage structure changes to a random distribution of large [001] faceted anion voids. This voidage behaviour, similar to that observed in a range of irradiated metals, is discussed in terms points defect rather than conventional colour centre terminology. (Auth.)

  16. Low temperature radiation embrittlement for reactor vessel steels

    International Nuclear Information System (INIS)

    Ginding, I.A.; Chirkina, L.A.

    1978-01-01

    General conceptions of cold brittleness of bcc metals are in a review. Considered are experimental data and theoretical representations about the effect of irradiation conditions, chemical composition, phase and structural constitutions, grain size, mechanical and thermomechanical treatments on low-temperature irradiation embrittlement of reactor vessel steels. Presented are the methods for increasing radiation stability of metals (carbon and Cr-Mo steels) used in manufacturing reactor vessels

  17. Void shrinkage in stainless steel during high energy electron irradiation

    International Nuclear Information System (INIS)

    Singh, B.N.; Foreman, A.J.E.

    1976-03-01

    During irradiation of thin foils of an austenitic stainless steel in a high voltage electron microscope, steadily growing voids have been observed to suddenly shrink and disappear at the irradiation temperature of 650 0 Cthe phenomenon has been observed in specimens both with and withoutimplanted helium. Possible mechanisms for void shrinkage during irradiation are considered. It is suggested that the dislocation-pipe-diffusion of vacancies from or of self-interstitial atoms to the voids can explain the shrinkage behaviour of voids observed during our experiments. (author)

  18. New polymer electrolytes for low temperature fuel cells

    Energy Technology Data Exchange (ETDEWEB)

    Sundholm, F.; Elomaa, M.; Ennari, J.; Hietala, S.; Paronen, M. [Univ. of Helsinki (Finland). Lab. of Polymer Chemistry

    1998-12-31

    Proton conducting polymer membranes for demanding applications, such as low temperature fuel cells, have been synthesised and characterised. Pre-irradiation methods are used to introduce sulfonic acid groups, directly or using polystyrene grafting, in stable, preformed polymer films. The membranes produced in this work show promise for the development of cost-effective, highly conducting membranes. (orig.)

  19. Recent progress in low-temperature silicon detectors

    International Nuclear Information System (INIS)

    Abreu, M.; D'Ambrosio, N.; Bell, W.; Berglund, P.; Borchi, E.; Boer, W. de; Borer, K.; Bruzzi, M.; Buontempo, S.; Casagrande, L.; Chapuy, S.; Cindro, V.; Devine, S.R.H.; Dezillie, B.; Dierlamm, A.; Dimcovski, Z.; Eremin, V.; Esposito, A.; Granata, V.; Grigoriev, E.; Grohmann, S.; Hauler, F.; Heijne, E.; Heising, S.; Hempel, O.; Herzog, R.; Haerkoenen, J.; Janos, S.; Jungermann, L.; Konorov, I.; Li, Z.; Lourenco, C.; De Masi, R.; Menichelli, D.; Mikuz, M.; Niinikoski, T.O.; O'Shea, V.; Pagano, S.; Palmieri, V.G.; Paul, S.; Pretzl, K.; Smith, K.; Solano, B. Pere; Sousa, P.; Pirollo, S.; Rato Mendes, P.; Ruggiero, G.; Sonderegger, P.; Tuominen, E.; Verbitskaya, E.; Da Via, C.; Watts, S.; Wobst, E.; Zavrtanik, M.

    2003-01-01

    The CERN RD39 Collaboration studies the possibility to extend the detector lifetime in a hostile radiation environment by operating them at low temperatures. The outstanding illustration is the Lazarus effect, which showed a broad operational temperature range around 130 K for neutron irradiated silicon detectors

  20. Chamber for uniaxial pressure application at low temperatures

    International Nuclear Information System (INIS)

    Grillo, M.L.N.; Carmo, L.C.S. do; Picon, A.P.

    1984-08-01

    A chamber for alignment of low temperature ferroelastic domains in crystals by the use of uniaxial stress was built. The system allows the use of EPR and optical techniques, as well as X-ray irradiation at temperatures as low as 77K. (Author) [pt

  1. Electronic control system for irradiation probes

    International Nuclear Information System (INIS)

    Gluza, E.; Neumann, J.; Zahalka, F.

    1980-01-01

    The EROS-78 system for the supply and power control of six heating sections of the irradiation probe of the CHOUCA type placed in the reactor vessel is described. The system allows temperature control at the location of the heat sensor with an accuracy of +-1% of the rated value within the region of 100 to 1000 degC. The equipment is provided with its own quartz controlled clock. The temperature is picked up by a chromel-alumel jacket thermocouple. The power input of the heating elements is thyristor controlled. (J.B.)

  2. Effects of electron irradiation on LDPE/MWCNT composites

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Jianqun [School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001 (China); Li, Xingji, E-mail: lxj0218@hit.edu.cn [School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001 (China); Liu, Chaoming; Rui, Erming [School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001 (China); Wang, Liqin [School of Mechatronics, Harbin Institute of Technology, Harbin 150001 (China)

    2015-12-15

    In this study, mutiwalled carbon nanotubes (MWCNTs) were incorporated into low density polyethylene (LDPE) in different concentrations (2%, 4% and 8%) using a melt blending process. Structural, thermal stability and tensile property of the unirradiated/irradiated LDPE/MWCNT composites by 110 keV electrons were investigated by means of scanning electron microscopy (SEM), small angle X-ray scattering (SAXS), Raman spectroscopy, electron paramagnetic resonance (EPR) spectroscopy, thermogravimetric analysis (TGA) and uniaxial tensile techniques. Experimental results show that the addition of MWCNTs obviously increases the ultimate tensile strength of LDPE and decreases the elongation at break, which is attributed to the homogeneous distribution of the MWCNTs in LDPE and intense interaction between MWCNTs and LDPE matrix. Also, the electron irradiation further increases the ultimate tensile strength of LDPE/MWCNT composites, which can be ascribed to the more intense interaction between MWCNTs and LDPE matrix, and the formation of crosslinking sites in LDPE matrix induced by the electron irradiation. The addition of MWCNTs significantly enhances thermal stability of the LDPE due to the hindering effect and the scavenging free radicals, while the electron irradiation decreases thermal stability of the LDPE/MWCNT composites since the structure of the MWCNTs and LDPE matrix damages.

  3. The Low temperature CFB gasifier

    DEFF Research Database (Denmark)

    Stoholm, P.; Nielsen, Rasmus Glar; Fock, Martin W.

    2003-01-01

    %) particle separation by the hot secondary cyclone. The next LT-CFB experiment, currently under preparation, is expected to be on either municipal/industrial waste or animal manure. Eventually a 500 kW LT-CFB test plant scheduled for commission during summer 2003, and the anticipated primary LT......The Low Temperature Circulating Fluidised Bed (LT-CFB) gasification process aims at avoiding problems due to ash deposition and agglomeration when using difficult fuels such as agricultural biomass and many waste materials. This, as well as very simple gas cleaning, is achieved by pyrolysing...... the fuel at around 650?C in a CFB reaction chamber and subsequently gasifying the char at around 730oC in a slowly fluidised bubbling bed chamber located in the CFB particle recirculation path. In this paper the novel LT-CFB concept is further described together with the latest test results from the 50 k...

  4. Low Temperature Hydrogen Antihydrogen Interactions

    International Nuclear Information System (INIS)

    Armour, E. A. G.; Chamberlain, C. W.

    2001-01-01

    In view of current interest in the trapping of antihydrogen (H-bar) atoms at low temperatures, we have carried out a full four-body variational calculation to determine s-wave elastic phase shifts for hydrogen antihydrogen scattering, using the Kohn Variational Principle. Terms outside the Born-Oppenheimer approximation have been taken into account using the formalism of Kolos and Wolniewicz. As far as we are aware, this is the first time that these terms have been included in an H H-bar scattering calculation. This is a continuation of earlier work on H-H-bar interactions. Preliminary results differ substantially from those calculated using the Born-Oppenheimer approximation. A method is outlined for reducing this discrepancy and taking the rearrangement channel into account.

  5. Mechanical pumping at low temperature

    Energy Technology Data Exchange (ETDEWEB)

    Perin, J.P.; Claudet, G.; Disdier, F.

    1994-12-31

    This new concept consists of a mechanical pump able to run at low temperature (25 K). Since gas density varies inversely with temperature, the pump could deliver much higher mass flow rate than at room temperature for a given size. Advantages of this concept are reduction of an order of magnitude in size and weight when compared to a conventional pump scaled to perform the same mass flow rate at room temperature. Results obtained at 80 K and 25 K with a Holweck type molecular drag pump of 100 mm diameter and with few stages of a turbomolecular pump running at the same temperatures, are given. This pump would be a solution to allow continuous tritium extraction and minimize the mass inventory for the ITER (International Tokamak Experiment Reactor). 5 figs., 2 tabs., 4 refs.

  6. Radiosensitivity of chlorella after medium energy accelerated electron irradiation

    International Nuclear Information System (INIS)

    Roux, J.C.

    1966-06-01

    The survival curves (capability of multiplication) of chlorella pyrenoidosa after irradiations can be used for soft electrons (0.65 and 1 MeV), hence penetrating into only 2 to 4 millimeters of water: the algae are laying on porous membranes and the doses are calculated from the power of the electron beam measured by the electric current on a metallic target or by Fricke's dosimetry. With these techniques, it is showed and discussed the part of anoxia in the radioprotection (magnitude or reduction of the dose calculated from the slope of survival curves: 2.5 ) that is more important than the restoration studied by the fractionation of the dose. The 0.65 and 1 MeV electrons have a biologic effect lesser than 180 keV X-rays (RBE - relative biological efficiency - calculated on the slope of survival curves is 0.92 in aerated irradiation, 0.56 in the deoxygenated irradiation). (author) [fr

  7. Degradation behaviour of fiber reinforced plastic under electron beam irradiation

    International Nuclear Information System (INIS)

    Sonoda, Katsumi; Yamamoto, Yasushi; Hashimoto, Osamu

    1989-01-01

    Various mechanical properties of four kinds of glass fiber-reinforced plastics irradiated with electron beams were examined at three temperatures; room temperature, 123 K and 77 K. Dynamic viscoelastic properties were measured, and fractography by means of scanning electron microscopy was observed in order to clarify degradation behaviour. A considerable decrease in interlaminar shear strength (ILSS) at room temperature was observed above 60 MGy. On the other hand, the three-point bending strength at 77 K and the ILSS at 123 K decreased with increasing irradiation. Fractography reveals that the degradation of the interface layer between matrix resin and fiber plays an important role in the strength reduction at 123 K and 77 K. These findings suggest that the interface between matrix resin and fiber loses its bondability at 123 K arid 77 K after electron beam irradiation. (author)

  8. Electron beam irradiation effect on GaN HEMT

    International Nuclear Information System (INIS)

    Lou Yinhong; Guo Hongxia; Zhang Keying; Wang Yuanming; Zhang Fengqi

    2011-01-01

    In this work, GaN HEMTs (High Electron Mobility Transistor) were irradiated by 0.8 and 1.2 MeV electron beams, and the irradiation effects were investigated. The results show that the device damage caused by 0.8 MeV electrons is more serious than that by 1.2 MeV electrons. Saturation drain current increase and threshold voltage negative shift are due to trapped positive charge from ionization in the AlGaN layer and N, Ga vacancy from non-ionizing energy loss in the GaN layer. Electron traps and trapped positive charges from non-ionizing in the AlGaN layer act as trap-assisted-tunneling centers that increase the gate leakage current.(authors)

  9. The use of electron accelerators for fresh fruit irradiation

    International Nuclear Information System (INIS)

    Ferdes, O.; Minea, R.

    2000-01-01

    There are presented the results of tests concerning the effects of accelerated electron-beam to some early fresh fruits like strawberries, cherries, sour-cherries and apples. The irradiation were performed on common varieties, in normal conditions, to the NILPRP-Electron Accelerator Laboratory facility consisting in electron-beam accelerators which have the following parameters: - mean beam current, 5 μA; - electron mean energy approximately, 7 MeV; - pulse period, 3.5 μs. The doses varied between 0.5-3.0 kGy and the dose rate was about 1500 Gy/min. It was determined the fruit shelf life and there were analysed the main organoleptic and nutritional properties, as: size, shape, colour, dry weight, acidity, total and reducing sugars, ascorbic acid content and other. For the electron-beam treated fruits it was pointed out an increase in freshness and shelf life extension by 5-7 days for strawberries and more than two weeks for cherries. Otherwise, for the applied doses, the electron-beam irradiation did not produce any significant changes in the fruit characteristic values. These results lead to the conclusion that the electron accelerators could be successfully used as a technological solution for the fresh fruits processing, in view of shelf life extension. There are presented also some technical and economical considerations on the feasibility of this technology and on the use of electron-beam machines for food irradiation. (authors)

  10. Determination of electronic stopping powers of 0.05–1 MeV/u {sup 131}Xe ions in C-, Ni- and Au-absorbers with calorimetric low temperature detectors

    Energy Technology Data Exchange (ETDEWEB)

    Echler, A., E-mail: artur.echler@iamp.physik.uni-giessen.de [GSI Helmholtz Center for Heavy Ion Research, Darmstadt (Germany); Institute for Atomic and Molecular Physics, University of Giessen (Germany); Institute for Physics, University of Mainz (Germany); Egelhof, P.; Grabitz, P. [GSI Helmholtz Center for Heavy Ion Research, Darmstadt (Germany); Institute for Physics, University of Mainz (Germany); Kettunen, H. [Department of Physics, University of Jyväskylä (Finland); Kraft-Bermuth, S. [Institute for Atomic and Molecular Physics, University of Giessen (Germany); Laitinen, M. [Department of Physics, University of Jyväskylä (Finland); Müller, K. [Institute for Atomic and Molecular Physics, University of Giessen (Germany); Rossi, M.; Trzaska, W.H.; Virtanen, A. [Department of Physics, University of Jyväskylä (Finland)

    2017-01-15

    A new experimental system for precise determination of electronic stopping powers of heavy ions has been set up at the accelerator laboratory of the University of Jyväskylä. The new setup, combining an established B-ToF system and an array of calorimetric low temperature detectors (CLTDs), has been used for the determination of electronic stopping powers of 0.05–1 MeV/u {sup 131}Xe ions in carbon, nickel and gold. Thereby advantage of the improved linearity and energy resolution of CLTDs as compared to the previously used ionization detector was taken to reduce energy calibration errors and to increase sensitivity for the energy loss determination, in particular at very low energies. The total uncertainties of 3–4% for C- and Ni-targets, and 5–7% for Au-targets, respectively, are dominated by the target properties, i.e. thickness determination and inhomogeneities. The results are compared to data from literature and to predictions of different theoretical computer codes. In the high energy part of the examined energy range the results are in good agreement with previously published data, while new stopping power data for very heavy ions in different Z{sub 2}-materials have been obtained at lower energies. Moreover, unexpectedly strong channeling effects for the transmission of the {sup 131}Xe ions in thin, partly polycrystalline nickel and gold target foils have been observed and investigated.

  11. Recovery of electron irradiated V-Ga alloys

    International Nuclear Information System (INIS)

    Leguey, T.; Monge, M.; Pareja, R.; Hodgson, E.R.

    2000-01-01

    The recovery characteristics of electron-irradiated V-Ga alloys with 1.2 and 4.6 at.% Ga have been investigated by positron annihilation spectroscopy (PAS). It is found that vacancies created by electron irradiation become mobile in these alloys at ∼293 K. This temperature is noticeably lower than that in pure V and V-Ti alloys. The vacancies aggregate into microvoids in V-4.6Ga, but do not in V-1.2Ga. The results indicate that vacancies are bound to Ga-interstitial impurity pairs

  12. Evolution of graphene nanoribbons under low-voltage electron irradiation

    KAUST Repository

    Zhu, Wenpeng

    2012-01-01

    Though the all-semiconducting nature of ultrathin graphene nanoribbons (GNRs) has been demonstrated in field-effect transistors operated at room temperature with ∼105 on-off current ratios, the borderline for the potential of GNRs is still untouched. There remains a great challenge in fabricating even thinner GNRs with precise width, known edge configurations and specified crystallographic orientations. Unparalleled to other methods, low-voltage electron irradiation leads to a continuous reduction in width to a sub-nanometer range until the occurrence of structural instability. The underlying mechanisms have been investigated by the molecular dynamics method herein, combined with in situ aberration-corrected transmission electron microscopy and density functional theory calculations. The structural evolution reveals that the zigzag edges are dynamically more stable than the chiral ones. Preferential bond breaking induces atomic rings and dangling bonds as the initial defects. The defects grow, combine and reconstruct to complex edge structures. Dynamic recovery is enhanced by thermal activation, especially in cooperation with electron irradiation. Roughness develops under irradiation and reaches a plateau less than 1 nm for all edge configurations after longtime exposure. These features render low-voltage electron irradiation an attractive technique in the fabrication of ultrathin GNRs for exploring the ultimate electronic properties. © 2012 The Royal Society of Chemistry.

  13. Absorption and luminescence of crystalline quartz under electron nanosecond irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Gritsenko, B P; Lisitsyn, V M; Stepanchuk, V N [Tomskij Politekhnicheskij Inst. (USSR)

    1981-02-01

    The purpose of the study is continuation of investigations of principal regularities of production and destruction of short-lived defects in quartz and accompanying luminescence under electron pulse irradiation. For investigation purposes samples of crystalline synthetic quartz have been used. The irradiation has been performed at 80-400 K temperatures by means of an electron pulse accelerator with parameters: electron flow pulse duration 10 ns, pulse current density up to 1000 A/cm/sup 2/, electron mean energy 200 keV. Temperature-time characteristics of absorption and luminescence spectrum are studied. It has been found that quartz irradiation by electron pulses of nanosecond duration leads to appearance of short-lived bands of optical absorption at 4.1 and 5.15 eV to which by kinetic parameters correspond luminescence bands at 2.6 and 3.1 eV, respectively. The enumerated absorption bands are induced by quartz irradiation independently of the prehistory and phase state of the sample and are caused obviously by intrinsic radiation defects. Possible models of such defects are suggested.

  14. The Low Temperature Microgravity Physics Facility Project

    Science.gov (United States)

    Chui, T.; Holmes, W.; Lai, A.; Croonquist, A.; Eraker, J.; Abbott, R.; Mills, G.; Mohl, J.; Craig, J.; Balachandra, B.; hide

    2000-01-01

    We describe the design and development of the Low Temperature Microgravity Physics Facility, which is intended to provide a unique environment of low temperature and microgravity for the scientists to perform breakthrough investigations on board the International Space Station.

  15. Evaluation of electron beam irradiation for disinfection of turmeric fingers

    Energy Technology Data Exchange (ETDEWEB)

    Yasumoto, Kyoden; Fujino, Masayuki; Supriyadi (Kyoto Univ., Uji (Japan). Research Inst. for Food Science); Suzuki, Tetsuya; Hayashi, Toru

    1991-08-01

    Turmeric finger as one of the most popular spices has been widely used for food manufacturing. However, it has also been a major cause of bacterial infestation of food materials especially in curry, ham and sausage manufacturing. In this study decontamination of bacteria in turmeric finger by electron beam irradiation was evaluated by comparing with several other decontamination methods: i.e., boiling, microwave irradiation, treatment by twin screw extruder and gamma-ray irradiation. By estimation of colony counting on nutrient agar plate, turmeric finger without any treatment gave total viable cell at 10{sup 8}/g. Turmeric finger which was irradiated by electron beam at 10 kGy dose dramatically reduced thermotolerant cell population below self restriction level (<1000/g), which has been required by food hygiene law. The same level of sterilization effect was obtained only by gamma-ray irradiation at 10 kGy and 20 kGy. On the other hand, although treatment through twin screw extruder slightly reduced bacterial numbers, neither boiling nor microwave irradiation gave sufficient decontamination effect on turmeric fingers. (author).

  16. Evaluation of electron beam irradiation for disinfection of turmeric fingers

    International Nuclear Information System (INIS)

    Yasumoto, Kyoden; Fujino, Masayuki; Supriyadi; Suzuki, Tetsuya; Hayashi, Toru.

    1991-01-01

    Turmeric finger as one of the most popular spices has been widely used for food manufacturing. However, it has also been a major cause of bacterial infestation of food materials especially in curry, ham and sausage manufacturing. In this study decontamination of bacteria in turmeric finger by electron beam irradiation was evaluated by comparing with several other decontamination methods: i.e., boiling, microwave irradiation, treatment by twin screw extruder and gamma-ray irradiation. By estimation of colony counting on nutrient agar plate, turmeric finger without any treatment gave total viable cell at 10 8 /g. Turmeric finger which was irradiated by electron beam at 10 kGy dose dramatically reduced thermotolerant cell population below self restriction level (<1000/g), which has been required by food hygiene law. The same level of sterilization effect was obtained only by gamma-ray irradiation at 10 kGy and 20 kGy. On the other hand, although treatment through twin screw extruder slightly reduced bacterial numbers, neither boiling nor microwave irradiation gave sufficient decontamination effect on turmeric fingers. (author)

  17. Evaluation of electron beam irradiation for disinfection of turmeric fingers

    International Nuclear Information System (INIS)

    Yasumoto, K.; Fujino, M.; Supriyadi; Suzuki, T.; Hayashi, T.

    1991-01-01

    Turmeric finger as one of the most popular spices has been widely used for food manufacturing. However, it has also been a major cause of bacterial infestation of food materials especially in curry, ham and sausage manufacturing. In this study decontamination of bacteria in turmeric finger by electron beam irradiation was evaluated by comparing with several other decontamination methods: i.e., boiling, microwave irradiation, treatment by twin screw extruder and gamma-ray irradiation. By estimation of colony counting on nutrient agar plate, turmeric finger without any treatment gave total viable cell at 10 8 /g. Turmeric finger which was irradiated by electron beam at 10kGy dose dramatically reduced thermotolerant cell population below self restriction level (<1000/g), which has been required by food hygiene law. The same level of sterilization effect was obtained only by gamma-ray irradiation at 10kGy and 20kGy. On the other hand, although treatment through twin screw extruder slightly reduced bacterial numbers, neither boiling nor microwave irradiation gave sufficient decontamination effect on turmeric fingers

  18. 1-Chloronaphthalene decomposition in air using electron beam irradiation

    International Nuclear Information System (INIS)

    Chmielewski, A.G.; Sun, Y.; Bulka, S.; Zimek, Z.

    2006-01-01

    A method for the preparation of model gas containing 1-chloronaphthalene can be referred to 1,1-DCE (dichloroethene). A pulsed electron beam (EB) accelerator ILU-6 (2.0 MeV max., 20 kW max.) was used as an irradiation source. The absorbed dose rate inside the irradiation vessel was 10.835 kGy/min. Total absorbed dose was adjusted by changing irradiation time of the Pyrex glass vessels. 1-Chloronaphthalene concentration was analyzed using gas-chromatography. It has been found, that 1-chloronaphthalene can be decomposed in air or N 2 using EB irradiation. Decomposition efficiency of 1-chloronaphthalene in air is higher than that in N 2 . Positive charge transfer reactions and OH radicals' reaction may play a main role in 1-chloronaphthalene decomposition process

  19. Application of electron irradiation to food containers and packaging materials

    International Nuclear Information System (INIS)

    Ueno, Koji

    2010-01-01

    Problems caused by microbial contamination and hazardous chemicals have attracted much attention in the food industry. The number of systems such as hygienic management systems and Hazard Analysis Critical Control Point (HACCP) systems adopted in the manufacturing process is increasing. As manufacturing process control has become stricter, stricter control is also required for microbial control for containers and packaging materials (from disinfection to sterilization). Since safe and reliable methods for sterilizing food containers and packaging materials that leave no residue are required, electron beam sterilization used for medical equipment has attracted attention from the food industry. This paper describes an electron irradiation facility, methods for applying electron beams to food containers and packaging materials, and products irradiated with electron beams. (author)

  20. Trapped electrons in irradiated single crystals of polyhydroxy compounds

    International Nuclear Information System (INIS)

    Box, H.C.; Budzinski, E.E.; Freund, H.G.; Potter, W.R.

    1979-01-01

    The intermolecular trapping of electrons has been observed in single crystals of dulcitol and L(+) arabinose x-irradiated at 4.2 0 K. Attribution of a major component of the ESR absorption to trapped electrons is based upon the character of the hyperfine pattern, which arises from multiple anisotropic hyperfine interactions with exchangeable protons, and on the g value of the absorption, which is always less than the free spin value. The removal of the trapped electron absorption upon irradiation with visible light has also been demonstrated. In these experiments all of the electrons are trapped in identical sites. This circumstance provides some important advantages in the study of the factors affecting the stabilization of charge in an environment of polarizable molecules

  1. Study of irradiation effects in the silicon carbide cubic polytype by photoluminescence and electron spin resonance spectroscopies

    International Nuclear Information System (INIS)

    Lefevre, J.

    2008-01-01

    This experimental work has consisted in the study of point defects induced by an electronic irradiation in the cubic crystallographic structure of silicon carbide with low temperature photoluminescence and electron spin resonance spectroscopies. The first one of these measurement tools has allowed to estimate the displacement threshold energy in the silicon sub-lattice and then to analyze the thermal stability of the irradiation defects in the low temperature range: (10-300 K) and then in the high temperature range: (300-1400 K). Besides, on the base of a recent theoretical model, this thesis has confirmed the proposition of the isolated silicon antisite for the D1 center whose running beyond the nominal running temperature of fission nuclear reactors (generation IV), for which SiC is in part intended, seems to be particularly problematic. Measurements carried out by ESR under lighting have at last allowed to detect a new defect in its metastable spin state S=1, possibly associated to a silicon interstitial configuration. (O.M.)

  2. The Low Temperature CFB Gasifier

    DEFF Research Database (Denmark)

    Stoholm, P.; Nielsen, Rasmus Glar; Richardt, K.

    2004-01-01

    straw, animal manure and waste and for co-firing the product gas in existing, e.g. coal fired power plant boilers. The aim is to prevent fouling, agglomeration and high temperature corrosion caused by potassium and chlorine and other fuel components when producing electricity. So far 92 hours......The Low Temperature Circulating Fluidised Bed (LT-CFB) gasification process is described together with the 50 kW and the 500 kW test plants and latest test results. The LT-CFB process is especially developed for medium and large scale (few to >100 MW) gasification of problematic bio-fuels like...... of experiments with the 50 kW test plant with two extremely difficult types of straw has shown low char losses and high retentions of ash including e.g. potassium. Latest 27 hours of experiments with dried, high ash pig- and hen manure has further indicated the concepts high fuel flexibility. The new 500 kW test...

  3. Low-temperature nuclear orientation

    International Nuclear Information System (INIS)

    Stone, N.J.; Postma, H.

    1986-01-01

    This book comprehensively surveys the many aspects of the low temperature nuclear orientation method. The angular distribution of radioactive emissions from nuclei oriented by hyperfine interactions in solids, is treated experimentally and theoretically. A general introductory chapter is followed by formal development of the theory of the orientation process and the anisotropic emission of decay products from oriented nuclei, applied to radioactive decay and to reactions. Five chapters on applications to nuclear physics cover experimental studies of alpha, beta and gamma emission, nuclear moment measurement and level structure information. Nuclear orientation studies of parity non-conservation and time reversal asymmetry are fully described. Seven chapters cover aspects of hyperfine interactions, magnetic and electric, in metals, alloys and insulating crystals, including ordered systems. Relaxation phenomena and the combined technique of NMR detection using oriented nuclei are treated at length. Chapters on the major recent development of on-line facilities, giving access to short lived nuclei far from stability, on the use of nuclear orientation for thermometry below 1 Kelvin and on technical aspects of the method complete the main text. Extensive appendices, table of relevant parameters and over 1000 references are included to assist the design of future experiments. (Auth.)

  4. Challenges in validating radiation sterilization with low energy electron irradiation

    International Nuclear Information System (INIS)

    Miller, A.; Helt-Hansen, J.

    2011-01-01

    Complete text of publication follows. Low energy electron irradiation (80-300 keV) is used increasingly for sterilization or decontamination in connection with isolators for aseptic filling lines in the pharmaceutical industry. It is not defined how validation for this process shall be carried out. A method can be derived from the medical device standard for radiation sterilization, ISO 11137, because the principles described in this standard can be applied to almost any industrial irradiation process. The validations elements are: Process definition, concerning specification of the dose required for the process and the maximum acceptable dose for the product. Installation qualification, concerning acceptance the irradiation facility. Operational qualification, concerning characterization of the facility. Performance qualification, concerning setting up the process. Process control, concerning routine monitoring. The limited penetration of the low energy electrons leads to problems with respect to executing these validation steps. This paper discusses these problems, and shows with examples how they can be solved.

  5. Impact of electron irradiation on particle track etching response in ...

    Indian Academy of Sciences (India)

    In the present work, attempts have been made to investigate the modification in particle track etching response of polyallyl diglycol carbonate (PADC) due to impact of 2 MeV electrons. PADC samples pre-irradiated to 1, 10, 20, 40, 60, 80 and 100 Mrad doses of 2 MeV electrons were further exposed to 140 MeV 28Si beam ...

  6. Effects of electron beam irradiation on inorganic exchanger AMP

    International Nuclear Information System (INIS)

    Rao, K.L.N.; Mathew, C.; Deshpande, R.S.; Jadhav, A.V.; Pande, B.M.; Shukla, J.P.

    1996-01-01

    The heteropolyacid salt inorganic exchanger ammonium molybdophosphate (AMP) was subjected to an electron dose upto 2 MGy to assess any possible radiation damage. The breakthrough and total exchange capacity of AMP for Cs + from simulated fission product solutions were determined for both control and irradiated samples. The scanning electron microscopy (SEM) and energy dispersive x-ray analysis (EDX) were deployed to examine any marked microscopic changes taking place in this exchanger. (author). 3 refs., 3 figs

  7. Design for a low temperature ion implantation and luminescence cryostat

    International Nuclear Information System (INIS)

    Noonan, J.R.; Kirkpatrick, C.G.; Myers, D.R.; Streetman, B.G.

    1976-01-01

    Several simple design changes of a conventional liquid helium optical Dewar can significantly improve the cryostat's versatility for use in low temperature particle irradiation. A bellows assembly provides precise sample positioning and allows convenient access for electrical connections. A heat exchanger consisting of thin walled tubing with a 'goose neck' bend provides a simple, effective means of cooling the sample as well as excellent thermal isolation of the sample holder from the coolant reservoir during controlled anneals. The addition of a vane-type vacuum valve, optical windows, and a rotatable tailpiece facilitates the study of optical properties of materials following low temperature ion implantation. (author)

  8. A 20 keV electron gun system for the electron irradiation experiments

    International Nuclear Information System (INIS)

    Mahapatra, S.K.; Dhole, S.D.; Bhoraskar, V.N.

    2005-01-01

    An electron gun consisting of cathode, focusing electrode, control electrode and anode has been designed and fabricated for the electron irradiation experiments. This electron gun can provide electrons of any energy over the range 1-20 keV, with current upto 50 μA. This electron gun and a Faraday cup are mounted in the cylindrical chamber. The samples are fixed on the Faraday cup and irradiated with electrons at a pressure ∼10 -7 mbar. The special features of this electron gun system are that, at any electron energy above 1 keV, the electron beam diameter can be varied from 5 to 120 mm on the Faraday cup mounted at a distance of 200 mm from the anode in the chamber. The variation in the electron current over the beam spot of 120 mm diameter is less than 15% and the beam current stability is better than 5%. This system is being used for studying the irradiation effects of 1-20 keV energy electrons on the space quality materials in which the irradiation time may vary from a few tens of seconds to hours

  9. A 20 keV electron gun system for the electron irradiation experiments

    Energy Technology Data Exchange (ETDEWEB)

    Mahapatra, S.K. [Department of Physics, University of Pune, Pune 411007 (India); Dhole, S.D. [Department of Physics, University of Pune, Pune 411007 (India); Bhoraskar, V.N. [Department of Physics, University of Pune, Pune 411007 (India)]. E-mail: vnb@physics.unipune.ernet.in

    2005-01-01

    An electron gun consisting of cathode, focusing electrode, control electrode and anode has been designed and fabricated for the electron irradiation experiments. This electron gun can provide electrons of any energy over the range 1-20 keV, with current upto 50 {mu}A. This electron gun and a Faraday cup are mounted in the cylindrical chamber. The samples are fixed on the Faraday cup and irradiated with electrons at a pressure {approx}10{sup -7} mbar. The special features of this electron gun system are that, at any electron energy above 1 keV, the electron beam diameter can be varied from 5 to 120 mm on the Faraday cup mounted at a distance of 200 mm from the anode in the chamber. The variation in the electron current over the beam spot of 120 mm diameter is less than 15% and the beam current stability is better than 5%. This system is being used for studying the irradiation effects of 1-20 keV energy electrons on the space quality materials in which the irradiation time may vary from a few tens of seconds to hours.

  10. The Low Temperature Microgravity Physics Experiments Project

    Science.gov (United States)

    Holmes, Warren; Lai, Anthony; Croonquist, Arvid; Chui, Talso; Eraker, J. H.; Abbott, Randy; Mills, Gary; Mohl, James; Craig, James; Balachandra, Balu; hide

    2000-01-01

    The Low Temperature Microgravity Physics Facility (LTMPF) is being developed by NASA to provide long duration low temperature and microgravity environment on the International Space Station (ISS) for performing fundamental physics investigations. Currently, six experiments have been selected for flight definition studies. More will be selected in a two-year cycle, through NASA Research Announcement. This program is managed under the Low Temperature Microgravity Physics Experiments Project Office at the Jet Propulsion Laboratory. The facility is being designed to launch and returned to earth on a variety of vehicles including the HII-A and the space shuttle. On orbit, the facility will be connected to the Exposed Facility on the Japanese Experiment Module, Kibo. Features of the facility include a cryostat capable of maintaining super-fluid helium at a temperature of 1.4 K for 5 months, resistance thermometer bridges, multi-stage thermal isolation system, thermometers capable of pico-Kelvin resolution, DC SQUID magnetometers, passive vibration isolation, and magnetic shields with a shielding factor of 80dB. The electronics and software architecture incorporates two VME buses run using the VxWorks operating system. Technically challenging areas in the design effort include the following: 1) A long cryogen life that survives several launch and test cycles without the need to replace support straps for the helium tank. 2) The minimization of heat generation in the sample stage caused by launch vibration 3) The design of compact and lightweight DC SQUID electronics. 4) The minimization of RF interference for the measurement of heat at pico-Watt level. 5) Light weighting of the magnetic shields. 6) Implementation of a modular and flexible electronics and software architecture. The first launch is scheduled for mid-2003, on an H-IIA Rocket Transfer Vehicle, out of the Tanegashima Space Center of Japan. Two identical facilities will be built. While one facility is onboard

  11. Amorphization kinetics of Zr3Fe under electron irradiation

    International Nuclear Information System (INIS)

    Motta, A.T.; Howe, L.M.; Okamoto, P.R.

    1994-11-01

    Previous investigations using 40 Ar ion bombardments have revealed that Zr 3 Fe, which has an orthorhombic crystal structure, undergoes an irradiation-induced transformation from the crystalline to the amorphous state. In the present investigation, 0.9 MeV electron irradiations were performed at 28 - 220 K in a high-voltage electron microscope (HVEM). By measuring the onset, spread and final size of the amorphous region, factoring in the Gaussian distribution of the beam, a kinetic description of the amorphization in terms of dose, dose rate and temperature was obtained. The critical temperature for amorphization by electron irradiation was found to be ∼ 220 K, compared with 570 - 625 K for 40 Ar ion irradiation. Also, the dose-to-amorphization increased exponentially with temperature. Results indicated that the rate of growth of the amorphous region under the electron beam decreased with increasing temperature and the dose-to-amorphization decreased with increasing dose rate. The size of the amorphous region saturated after a given dose, the final size decreasing with increasing temperature, and it is argued that this is related to the existence of a critical dose rate, which increases with temperature, and below which no amorphization occurs. (author). 26 refs., 6 figs

  12. Amorphization kinetics of Zr3Fe under electron irradiation

    International Nuclear Information System (INIS)

    Motta, A.T.; Howe, L.M.; Okamoto, P.R.

    1992-10-01

    0.9 MeV electron irradiations were performed at 28--220 K in a high-voltage electron microscope (HVEM). By measuring onset, spread and final size of the amorphous region, factoring in the Guassian distribution of the beam, a kinetic description of the amorphization in terms of dose, dose rate and temperature was obtained. The critical temperature for amorphization by electron irradiation was found to be ∼220 K, compared to 570--625 K for 40 Ar ion irradiation. Also, the dose-to-amorphization increased exponentially with temperature. Results indicated that the rate of growth of the amorphous region under the electron beam decreased with increasing temperature and the does-to-amorphization decreased with increasing dose rate. The size of the amorphous region saturated after a region dose, the final size decreasing with increasing temperature, and it was argued that this is related to the existence of a critical dose rate, which increased with temperature, below which no amorphization occurred. The above observations can be understood in the framework of the kinetics of damage accumulation under irradiation

  13. Electron spin resonance investigations on polycarbonate irradiated with U ions

    Energy Technology Data Exchange (ETDEWEB)

    Chipara, M.I.; Reyes-Romero, J

    2001-12-01

    Electron spin resonance investigations on polycarbonate irradiated with uranium ions are reported. The dependence of the resonance line parameters (line intensity, line width, double integral) on penetration depth and dose is studied. The nature of free radicals induced in polycarbonate by the incident ions is discussed in relation with the track structure. The presence of severe exchange interactions among free radicals is noticed.

  14. Efficient indium-tin-oxide free inverted organic solar cells based on aluminum-doped zinc oxide cathode and low-temperature aqueous solution processed zinc oxide electron extraction layer

    International Nuclear Information System (INIS)

    Chen, Dazheng; Zhang, Chunfu; Wang, Zhizhe; Zhang, Jincheng; Tang, Shi; Wei, Wei; Sun, Li; Hao, Yue

    2014-01-01

    Indium-tin-oxide (ITO) free inverted organic solar cells (IOSCs) based on aluminum-doped zinc oxide (AZO) cathode, low-temperature aqueous solution processed zinc oxide (ZnO) electron extraction layer, and poly(3-hexylthiophene-2, 5-diyl):[6, 6]-phenyl C 61 butyric acid methyl ester blend were realized in this work. The resulted IOSC with ZnO annealed at 150 °C shows the superior power conversion efficiency (PCE) of 3.01%, if decreasing the ZnO annealing temperature to 100 °C, the obtained IOSC also shows a PCE of 2.76%, and no light soaking issue is observed. It is found that this ZnO film not only acts as an effective buffer layer but also slightly improves the optical transmittance of AZO substrates. Further, despite the relatively inferior air-stability, these un-encapsulated AZO/ZnO IOSCs show comparable PCEs to the referenced ITO/ZnO IOSCs, which demonstrates that the AZO cathode is a potential alternative to ITO in IOSCs. Meanwhile, this simple ZnO process is compatible with large area deposition and plastic substrates, and is promising to be widely used in IOSCs and other relative fields.

  15. Electron beam irradiation facility for low to high dose irradiation applications

    International Nuclear Information System (INIS)

    Petwal, V.C.; Wanmode, Yashwant; Verma, Vijay Pal; Bhisikar, Abhay; Dwivedi, Jishnu; Shrivastava, P.; Gupta, P.D.

    2013-01-01

    Electron beam based irradiation facilities are becoming more and more popular over the conventional irradiator facilities due to many inherent advantages such as tunability of beam energy, availability of radiation both in electron mode and X-ray mode, wide range of the dose rate, control of radiation from a ON-OFF switch and other safety related merits. A prototype experimental facility based on electron accelerator has been set-up at RRCAT to meet the low-dose, medium dose and high-dose requirements for radiation processing of food, agricultural and medical products. The facility can be operated in the energy range from 7-10 MeV at variable power level from 0.05-3 kW to meet the dose rate requirement of 100 Gy to kGy. The facility is also equipped with a Bremsstrahlung converter optimized for X-ray irradiation at 7.5 MV. Availability of dose delivery in wide range with precision control and measurement has made the facility an excellent tool for researchers interested in electron/X-ray beam irradiation. A precision dosimetry lab based on alanine EPR and radiochromic film dosimetry system have been established to characterize the radiation field and precise dose measurements. Electron beam scattering technique has been developed to achieve low dose requirement for EB irradiation of various seeds such as groundnut, wheat, soybeans, moong beans, black gram etc. for mutation related studies. This paper describes various features of the facility together with the dosimetric measurements carried out for qualification of the facility and recent irradiation experiments carried out using this facility. (author)

  16. Immunological aspect of the electron-beam irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Ikeda, K [Hyogo College of Medicine, Nishinomiya (Japan)

    1978-05-01

    In the present study, sciatic nerve tissues of the cat were emulsified with the complete Freund's adjuvant and injected into the foot-pads of the guinea pig. Frozen and frozen-irradiated feline sciatic nerve tissues were treated in the similar manner, and their encephalitogenicity was comparatively studied. Affected animals became skinny, weak in the hind limbs and sometimes solid their tails. Antigenic mixtures of the fresh peripheral nerves with adjuvant have sensitized 75% (15 out of 20) of guinea pigs, whereas none of the 41 animals manifested any sign of experimental allergic neuritis (EAN) after intradermal Frozen-preserved peripheral nerve-adjuvant mixtures gave rise to EAN in 29% (6 out of 21) of guinea pigs. The present results appear to show that the electron-beam irradiation might have modified the specific chemical structures of the myelin basic protein to completely suppress the encephalitogenicity of the peripheral nerve-tissues. High-voltage cathode irradiations would be capable of depressing the antigenicity of the transplantation immunology when the antigenic determinants have the chemical structures in common with the encephalitogenic antigens. Excessive amount of the irradiation used to result in severe tissue damages, therefore, an optimum dosis of electron-beams should be determined for each tissue destined for grafting. As the frozen peripheral nerve-adjuvant mixtures have been less encephalitogenic, freezing alone might well be considered partially to improve the acceptability of the grafts. Cryopreservation of the irradiated allografts would be worth further studying.

  17. Immunological aspect of the electron-beam irradiation

    International Nuclear Information System (INIS)

    Ikeda, Kimiyuki

    1978-01-01

    In the present study, sciatic nerve tissues of the cat were emulsified with the complete Freund's adjuvant and injected into the foot-pads of the guinea pig. Frozen and frozen-irradiated feline sciatic nerve tissues were treated in the similar manner, and their encephalitogenicity was comparatively studied. Affected animals became skinny, weak in the hind limbs and sometimes solid their tails. Antigenic mixtures of the fresh peripheral nerves with adjuvant have sensitized 75% (15 out of 20) of guinea pigs, whereas none of the 41 animals manifested any sign of experimental allergic neuritis (EAN) after intradermal Frozen-preserved peripheral nerve-adjuvant mixtures gave rise to EAN in 29% (6 out of 21) of guinea pigs. The present results appear to show that the electron-beam irradiation might have modified the specific chemical structures of the myelin basic protein to completely suppress the encephalitogenicity of the peripheral nerve-tissues. High-voltage cathode irradiations would be capable of depressing the antigenicity of the transplantation immunology when the antigenic determinants have the chemical structures in common with the encephalitogenic antigens. Excessive amount of the irradiation used to result in severe tissue damages, therefore, an optimum dosis of electron-beams should be determined for each tissue destined for grafting. As the frozen peripheral nerve-adjuvant mixtures have been less encephalitogenic, freezing alone might well be considered partially to improve the acceptability of the grafts. Cryopreservation of the irradiated allografts would be worth further studying. (author)

  18. Task 08/41, Low temperature loop at the RA reactor, Review I of materials planned for irradiation within the five-year plan of nuclear power development in Federal Peoples Republic of Yugoslavia; Zadatak 08/41, Niskotemperaturna petlja u reaktoru 'A', Pregled I materijala predvidjenih za ozracivanje petogodisnjim planom razvoja nuklearne energije FNRJ

    Energy Technology Data Exchange (ETDEWEB)

    Milenkovic, S; Milasin, N [Institute of Nuclear Sciences Boris Kidric, Vinca, Beograd (Serbia and Montenegro)

    1961-12-15

    For the purpose of designing the low-temperature loop at the RA reactor, a list of materials that would be irradiated in the reactor was made. This review includes materials which should be irradiated in for isotope production and materials to be irradiated for research and testing purposes. The neutron flux needed for materials testing should be much higher than presently available neutron flux of 10{sup 12} n/cm{sup 2} sec. [Serbo-Croat] Za potrebe projektovanja niskotemperaturne petlje na reaktoru RA nacinjen je pregled materijala za ozracivanje u reaktoru. Pregled sadrzi materijale za ozracivanje u cilju proizvodnje izotopa i materijale za specijalna ozracivanja u cilju ispitivanja materijala. Za ispitivanje materijala potreban bi bio fluks neutron koji je znatno veci od raspolozivog fluksa od 10{sup 12} n/cm{sup 2} sec.

  19. Texture of low temperature isotropic pyrocarbons

    International Nuclear Information System (INIS)

    Pelissier, Joseph; Lombard, Louis.

    1976-01-01

    Isotropic pyrocarbon deposited on fuel particles was studied by transmission electron microscopy in order to determine its texture. The material consists of an agglomerate of spherical growth features similar to those of carbon black. The spherical growth features are formed from the cristallites of turbostratic carbon and the distribution gives an isotropic structure. Neutron irradiation modifies the morphology of the pyrocarbon. The spherical growth features are deformed and the coating becomes strongly anisotropic. The transformation leads to the rupture of the coating caused by strong irradiation doses [fr

  20. Improvement in properties of plastic teeth by electron beam irradiation

    International Nuclear Information System (INIS)

    Sano, Yuko; Ishikawa, Shun-ichi; Seguchi, Tadao

    2011-01-01

    Improvement of the comfort and esthetics of artificial plastic teeth is desirable for the recently increasing numbers of elderly in society. Plastic teeth made of polycarbonate (PC) were modified by electron beam (EB) irradiation under specific conditions, and the change in the chemical properties of the PC was investigated. The water absorption, glucose attachment, level of bis-phenol-A (BPA) extraction, maltose adhesion, and mucin adhesion on the PC teeth were measured before and after EB irradiation. EB irradiation to a dose of 3.5 kGy at 150 o C in a nitrogen gas atmosphere reduced the water absorption by 20%, glucose absorption by 40%, maltose adhesion by 20%, and the amount of various amino acids, formed as the hydrolysis products of mucin, adhering on the PC teeth were reduced by 60-99%. The BPA content was lower than the detection limit for analysis of both the original and the EB irradiated PC teeth. - Highlights: → Radiation improvement of polycarbonate for plastic teeth by EB irradiation 3.5 kGy at 150 o C in inert gas. → Water and glucose absorption and maltose adhesion on PC teeth were much reduced. → Bis-phenol-A content from PC teeth was lower than the detection limit after irradiation.

  1. Investigation of the effect of some irradiation parameters on the response of various types of dosimeters to electron irradiation

    International Nuclear Information System (INIS)

    Farah, K.; Kuntz, F.; Kadri, O.; Ghedira, L.

    2004-01-01

    Several undyed and dyed polymer films are commercially available for dosimetry in intense radiation fields, especially for radiation processing of food and sterilisation of medical devices. The effects of temperature during irradiation and post-irradiation stability, on the response of these dosimeters are of importance to operators of irradiation facilities. The present study investigates the effects of temperature during irradiation by 2.2 MeV electrons beam accelerator and post irradiation storage on the response of several types of dosimeter films. All dosimeters showed a significant effect of temperature during irradiation and post-irradiation storage

  2. Investigation of the effect of some irradiation parameters on the response of various types of dosimeters to electron irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Farah, K. E-mail: k.farah@cnstn.rnrt.tn; Kuntz, F.; Kadri, O.; Ghedira, L

    2004-10-01

    Several undyed and dyed polymer films are commercially available for dosimetry in intense radiation fields, especially for radiation processing of food and sterilisation of medical devices. The effects of temperature during irradiation and post-irradiation stability, on the response of these dosimeters are of importance to operators of irradiation facilities. The present study investigates the effects of temperature during irradiation by 2.2 MeV electrons beam accelerator and post irradiation storage on the response of several types of dosimeter films. All dosimeters showed a significant effect of temperature during irradiation and post-irradiation storage.

  3. Field enhanced luminescence of irradiated organics due to electron tunnelling

    International Nuclear Information System (INIS)

    Charlesby, A.

    1981-01-01

    Many organic materials, following exposure to high energy radiation at low temperatures, continue to emit light for long periods. One possible mechanism is that electrons trapped near their parent cations can tunnel back over long times depending on trap depth and distance. This luminescence can be greatly enhanced by the post-radiation application of an external electric field. Calculations on the kinetics of recombination by tunnelling for various trap depths and distances are extended to allow for the effect of an electrical field subsequently applied. The quantitative results lead to two methods of assessing trap depth, depending on immediate light enhancement and on its subsequent decay. The effect of field reversal is also explained. (author)

  4. Comparison of initial damage rates using neutron and electron irradiations

    International Nuclear Information System (INIS)

    Goldstone, J.A.R.

    1978-08-01

    The purpose of this experiment was twofold: (1) The number of interstitials that pin dislocations was studied as a function of neutron energy. (2) By comparison with electron irradiations on the sample, a correlation between the predicted and measured numbers of defects was found. All irradiations were performed on the same high purity copper sample. The sample was machined in the form of a cantilever beam with a flexural resonant frequency of 770 Hz. Changes in Young's modulus at constant strain amplitude were monitored continuously through changes in the resonant frequency of the sample. These changes in the modulus can be related to the number of pinning points added to dislocation lines, which are in turn related to the number of free interstitials produced. Neutron energy dependence experiments were done from 2 to 24 MeV on the copper sample and at 14 MeV on a gold sample. By equating pinning rates from electron and neutron irradiations and using the free interstitial production rate obtained from electron irradiations, an estimate of the free interstitial production cross section for neutrons of 2 to 24 MeV was made

  5. Development of an irradiation device for electron beam wastewater treatment

    International Nuclear Information System (INIS)

    Rela, Paulo Roberto

    2003-01-01

    When domestic or industrial effluents with synthetic compounds are disposed without an adequate treatment, they impact negatively the environment with damages to aquatic life and for the human being. Both population and use of goods and services that contribute for the hazardous waste are growing. Hazardous regulations are becoming more restrictive and technologies, which do not destroy these products, are becoming less acceptable. The electron beam radiation process is an advanced oxidation process, that produces highly reactive radicals resulting in mineralization of the contaminant. In this work was developed an irradiation system in order to optimize the interaction of electron beam delivered from the accelerator with the processed effluent. It is composed by an irradiation device where the effluent presents to the electron beam in an up flow stream and a process control unit that uses the calorimetric principle. The developed irradiation device has a different configuration from the devices used by others researchers that are working with this technology. It was studied the technical and economic feasibility, comparing with the literature the results of the irradiation device demonstrated that it has a superior performance, becoming an process for use in disinfection and degradation of hazardous organic compounds of wastewater from domestic and industrial origin, contributing as an alternative technology for Sanitary Engineering. (author)

  6. Response of zircon to electron and Ne+ irradiation

    International Nuclear Information System (INIS)

    Devanathan, R.; Weber, W.J.; Boatner, L.A.

    1997-01-01

    Zircon (ZrSiO 4 ) is an actinide host phase in vitreous ceramic nuclear waste forms and a potential host phase for the disposition of excess weapons plutonium. In the present work, the effects of 800 and 900 keV electron and 1 MeV Ne + irradiations on the structure of single crystals of ZrSiO 4 have been investigated. The microstructural evolution during the irradiations was studied in situ using a high-voltage electron microscope interfaced to an ion accelerator at Argonne National Laboratory. The results indicate that electron irradiation at 15 K cannot amorphize ZrSiO 4 even at fluences an order of magnitude higher than that required for amorphization by 1.5 MeV Kr + ions. However, the material is readily amorphized by 1 MeV Ne + irradiation at 15 K. The temperature dependence of this amorphization is discussed in light of previous studies of radiation damage in ZrSiO 4

  7. Radiation safety of gamma and electron irradiation facilities

    International Nuclear Information System (INIS)

    1992-01-01

    There are currently some 160 gamma irradiation facilities and over 600 electron beam facilities in operation throughout virtually all Member States of the IAEA. The most widespread uses of these facilities are for the sterilization of medical and pharmaceutical products, the preservation of foodstuffs, polymer synthesis and modification, and the eradication of insect infestation. The safety record of this industry has been very good. Nevertheless, there is a potential for accidents with serious consequences. Gamma and electron beam facilities produce very high dose rates during irradiation, so that a person accidentally present in the irradiation chamber can receive a lethal dose within minutes or seconds. Precautions against uncontrolled entry must therefore be taken. Furthermore, gamma irradiation facilities contain large amounts of radioactivity and if the mechanism for retracting the source is damaged, the source may remain exposed, inhibiting direct access to carry out remedial work. Contamination can result from corroded or damaged sources, and decontamination can be very expensive. These aspects clearly indicate the need to achieve a high degree of safety and reliability in the facilities. This can be accomplished by effective quality control together with careful design, manufacture, installation, operation and decommissioning. The guidance in this Safety Series publication is intended for competent authorities responsible for regulating the use of radiation sources as well as the manufacturers, suppliers, installers and users of gamma and electron beam facilities. 20 refs, 6 figs

  8. Effect of ammonia and electron beam irradiation on lignocelulosic materials

    International Nuclear Information System (INIS)

    Mastro, N.L. del; Gennari, S.M.; Castagnet, A.C.G.

    1986-01-01

    Reports on some of the effects produced on sugarcane bagasse and eucaliptus wood saccharification by combining irradiation and NH 3 treatment. The samples irradiated at 10 5 Gy, 2x10 5 Gy and 5x10 5 Gy with an electron accelerator were treated with anhydrous gaseous ammonia. Cellulase complex from T. reesei was used for hydrolysis assays. Bromatological analysis and 'in vitro' digestibility tests were performed. The combination of EBI and ammonia treatments produced and increase in the saccharification yield, 'in vitro' digestibility and protein content for the two kinds of sample. (Author) [pt

  9. Segregation of a copper-nickel alloy after electron irradiation

    International Nuclear Information System (INIS)

    Wagner, W.

    1979-09-01

    In the present work measurement of diffuse neutron scattering are used to determine short range segregation effects of the alloy Cu 0 sub(.) 414 Ni 0 sub(.) 586 after thermal annealing and 3 MeV electron irradiation in the temperature range between 370 K and 600 K. In addition neutron small angle scattering measurement are performed after irradiation to study possible long range segregation effects. Residual resistivity measurements are performed in parallel in order tp orientate the relatively expensive neutron scattering measurements with respect to the residual changes (orig./KBI) [de

  10. The application analysis of high energy electron accelerator in food irradiation processing

    International Nuclear Information System (INIS)

    Deng Wenmin; Chen Hao; Feng Lei; Zhang Yaqun; Chen Xun; Li Wenjun; Xiang Chengfen; Pei Ying; Wang Zhidong

    2012-01-01

    Irradiation technology of high energy electron accelerator has been highly concerned in food processing industry with its fast development, especially in the field of food irradiation processing. In this paper, equipment and research situation of high energy electron accelerator were collected, meanwhile, the similarities and differences between high energy electron beam and 60 Co γ-rays were discussed. In order to provide more references of high energy electron beam irradiation, the usages of high energy electron in food irradiation processing was prospected. These information would promote the development of domestic food irradiation industry and give a useful message to irradiation enterprises and researchers. (authors)

  11. Electron microbeam specifications for use in cell irradiation experiments

    International Nuclear Information System (INIS)

    Kim, E.-H.; Choi, M.-C.; Lee, D.-H.; Chang, M.; Kang, C.-S.

    2003-01-01

    The microbeam irradiation system was devised originally to identify the hit and unhit cells by confining the beam within the target cell. The major achievement through the microbeam experiment studies has turned out to be the discovery of the 'bystander effect'. Microbeam experiments have been performed with alpha and proton beams in major and with soft x-rays in minor. The study with electron microbeam has been deferred mainly due to the difficulty in confining the electron tracks within a single target cell. In this paper, the electron microbeam irradiation system under development in Korea is introduced in terms of the beam specifications. The KIRAMS electron microbeam irradiation system consists of an electron gun, a vacuum chamber for beam collimation into 5 μm in diameter and a biology stage. The beam characteristics in terms of current and energy spectrum of the electrons entering a target cell and its neighbor cells were investigated by Monte Carlo simulation for the electron source energies of 25, 50, 75 and 100 keV. Energy depositions in the target cell and the neighbor cells were also calculated. The beam attenuation in current and energy occurs while electrons pass through the 2 μm-thick Mylar vacuum window, 100 μm-thick air gap and the 2 μm-thick Mylar bottom of cell dish. With 25 keV electron source, 80 % of decrease in current and 30 % of decrease in average energy were estimated before entering the target cell. With 75 keV electron source, on the other hand, 55 % of decrease in current and less than 1 % of decrease in average energy were estimated. Average dose per single collimated electron emission was 0.067 cGy to the target cell nucleus of 5 μm in diameter and 0.030 cGy to the cytoplasm of 2.5 μm in thickness with 25 keV electron source while they were 0.15 cGy and 0.019 cGy, respectively, with 75 keV electron source. The multiple scattering of electrons resulted in energy deposition in the neighbor cells as well. Dose to the first

  12. Plastic coating on paper by electron beam irradiation

    International Nuclear Information System (INIS)

    Ametani, Kazuo; Tsuchiya, Mitsuaki; Sawai, Takeshi

    1984-01-01

    It has been known long since that the resin system of unsaturated polyester and vinylmonomer mixture cures by irradiation. Ford of USA for the first time industrialized the radiation curing reaction of resins for the coating of automobile parts. Thereafter, accompanying the development and technical advance of the low energy electron beam irradiation apparatus which is suitable to surface treatment such as coating and easy to handle and the development of resins, the electron beam curing method has become to be utilized for coating hardboard and wooden doors, coating automobile tire rims, adhering printing papers and others. The electron beam curing method has advantage such as energy conservation, resource saving and little pollution because solvent is not used, high production rate and small floor space. In glossing industry, for the purpose of developing the techniques to apply electron beam curing method to glazed paper production, the selection of the composition of resins suitable to glazed papers, the irradiating condition and the properties of cured films were examined. The films withstanding bending can be obtained at low dose with urethane group, ester group or the combination of monomers. (Kako, I.)

  13. Quantitative analysis of complexes in electron irradiated CZ silicon

    International Nuclear Information System (INIS)

    Inoue, N.; Ohyama, H.; Goto, Y.; Sugiyama, T.

    2007-01-01

    Complexes in helium or electron irradiated silicon are quantitatively analyzed by highly sensitive and accurate infrared (IR) absorption spectroscopy. Carbon concentration (1x10 15 -1x10 17 cm -3 ) and helium dose (5x10 12 -5x10 13 cm -2 ) or electron dose (1x10 15 -1x10 17 cm -2 ) are changed by two orders of magnitude in relatively low regime compared to the previous works. It is demonstrated that the carbon-related complex in low carbon concentration silicon of commercial grade with low electron dose can be detected clearly. Concentration of these complexes is estimated. It is clarified that the complex configuration and thermal behavior in low carbon and low dose samples is simple and almost confined within the individual complex family compared to those in high concentration and high dose samples. Well-established complex behavior in electron-irradiated sample is compared to that in He-irradiated samples, obtained by deep level transient spectroscopy (DLTS) or cathodoluminescence (CL), which had close relation to the Si power device performance

  14. A structure development in electron-irradiated type Ia diamond

    International Nuclear Information System (INIS)

    Novikov, N.V.; Ositinskaya, T.D.; Tkach, V.N.

    1998-01-01

    A type Ia diamond crystal with nitrogen impurity in different forms was irradiated by 3.5 MeV electrons with increasing doses 5 centre dot 10 16 , 2 centre dot 10 17 , 4 centre dot 10 17 , 2 centre dot 10 18 e/cm 2 and investigated before and after each dose by positron annihilation, EPR, and optical spectroscopy. After irradiation with the highest dose, the effect of development of a visible defective structure of the crystal is revealed. A description of this effect and data of EPR and IR-measurements depending on irradiation doses are presented. First results of cathodoluminescence (CL) studies in the form CL-topograms and CL-spectra for difference zones of the crystal are also given

  15. Improvement of carbon fiber surface properties using electron beam irradiation

    International Nuclear Information System (INIS)

    Pino, E.S.; Machado, L.D.B.; Giovedi, C.

    2007-01-01

    Carbon fiber-reinforced advance composites have been used for structural applications, mainly on account of their mechanical properties. The main factor for a good mechanical performance of carbon fiber-reinforced composite is the interfacial interaction between its components, which are carbon fiber and polymeric matrix. The aim of this study is to improve the surface properties of the carbon fiber using ionizing radiation from an electron beam to obtain better adhesion properties in the resultant composite. EB radiation was applied on the carbon fiber itself before preparing test specimens for the mechanical tests. Experimental results showed that EB irradiation improved the tensile strength of carbon fiber samples. The maximum value in tensile strength was reached using doses of about 250 kGy. After breakage, the morphology aspect of the tensile specimens prepared with irradiated and non-irradiated car- bon fibers were evaluated. SEM micrographs showed modifications on the carbon fiber surface. (authors)

  16. Tailoring crystallinity and configuration of silica nanotubes by electron irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Taguchi, Tomitsugu, E-mail: taguchi.tomitsugu@jaea.go.jp; Yamaguchi, Kenji

    2015-05-01

    Highlights: •Single-crystal SiO{sub 2} nanotubes were successfully synthesized for the first time. •The single-crystal SiO{sub 2} was α-crystobalite. •Desired area of single-crystal nanotube can be changed to amorphous by electron irradiation. •The configuration of nanotube can be controlled using the focused electron irradiation technique. -- Abstract: SiO{sub 2} nanotubes show potential in applications such as nanoscale electronic and optical devices, bioseparation, biocatalysis, and nanomedicine. As-grown SiO{sub 2} nanotubes in the previous studies always have an amorphous wall, and here we demonstrate the successful synthesis of single-crystal nanotubes for the first time by the heat treatment of SiC nanotubes at 1300 °C for 10 h under low-vacuum conditions. According to TEM observations, the single-crystal SiO{sub 2} was α-cristobalite. We also demonstrate that single-crystal SiO{sub 2} nanotubes can be transformed into amorphous SiO{sub 2} nanotubes by electron beam irradiation. Moreover, we synthesized a crystalline/amorphous SiO{sub 2} composite nanotube, in which crystalline and amorphous SiO{sub 2} coexisted in different localized regions. In addition, for biomedical applications such as drug delivery systems, controlling the configuration of the open end, the diameter, and capsulation of SiO{sub 2} nanotubes is crucial. We can also obturate, capsulate, and cut a SiO{sub 2} nanotube, as well as modify the inner diameter of the nanotube at a specific, nanometer-sized region using the focused electron beam irradiation technique.

  17. Defect creation rates in CdTe irradiated by electrons

    International Nuclear Information System (INIS)

    Caillot, M.

    1978-01-01

    Up to now, the defect creation rates in CdTe irradiated by electrons were unknown. They have been calculated for different electron kinetic energies. As the samples studied are thick, the energy loss when the electrons penetrate the material has been taken into account. The cross-sections of Cd and Te displacements vs the depth of electron penetration were determined for different electron kinetic energies, and the defect creation rates obtained for each sublattice. These creation rates have been compared with those deduced from experiments and it was found that the experimental creation rates were lower than the calculated ones. This discrepancy can be explained in terms of creation of neutral Frenkel pairs. (Auth.)

  18. Irradiation of aluminium alloy materials with electron beam

    International Nuclear Information System (INIS)

    Konno, Osamu; Masumoto, Kazuyoshi

    1982-01-01

    It is a theme with a room for discussion to employ the stainless steel composed of longer half-life materials for the vacuum system of accelerators, from the viewpoint of radiation exposure. Therefore, it is desirable to use aluminium of shorter half-life in place of stainless steel. As a result of investigation on the above theme in the 1.2 GeV electron linac project in Tohoku University, it has been concluded that aluminium alloy vacuum chambers can reduce exposure dose by about one or two figures as compared with stainless steel ones. Of course, aluminium alloy contains trace amounts of Mg, Si, Ti, Cr, Mn, Fe, Zn, Cu and others. Therefore, four kinds of aluminium alloy considered to be usable have been examined for induced radioactivity by electron beam irradiation. Stainless steel SUS 304 has been also irradiated for comparison. Radiation energy has been 30 MeV and 200 MeV. When stainless steel and aluminium alloy were compared, aluminium alloy was very effective for reducing surface dose in low energy irradiation. In 200 MeV irradiation, the dose ratio of aluminium alloy to stainless steel became 1/30 to 1/100 after one week, though the dose difference between these two materials became smaller in 100 days or more after irradiation. If practical inspection and repair are implemented during the period from a few days to one week after shutdown, the aluminium alloy is preferable for exposure dose reduction even in high energy irradiation. (Wakatsuki, Y.)

  19. Electron beam irradiation effects on carbon fiber reinforced PEEK composite

    International Nuclear Information System (INIS)

    Sasuga, Tsuneo; Hagiwara, Miyuki; Odajima, Tosikazu; Sakai, Hideo; Nakakura, Toshiyuki; Masutani, Masahiro.

    1987-03-01

    Carbon fiber(CF) reinforced composites, using polyarylether-sulfone (PES) or polyarylether-ether-ketone (PEEK) as matrix material, were prepared and their electron beam irradiation effects were studied on the basis of changes in mechanical and dynamic viscoelastic properties and observation of fracture surfaces. The flexural strength of PES-CF composite decreased to 70 % of the initial strength after the irradiation of 3 MGy and 40 % after 15 MGy. The change in the profile of stress-strain (S-S) curves and fractographic observation by electron microscopy indicated that this composite irradiated with over 3 MGy was fractured by delamination caused by to the degradation of matrix polymer. The mechanical properties of PEEK-CF composite were scarcely decreased even after irradiated up to 180 MGy and this composite showed very high radiation resistance. The change in the profile of S-S curves and fractographic observation showed that this composite fractured due to destruction of fiber in the dose range less than 180 MGy, indicating that PEEK was excellent matrix material used in high radiation field. PEEK-PES-CF composite which was composed of the carbon fibers coated with PES solution showed less radiation resistance compared with PEEK-CF composite; the flexural strength decreased to 85 % of the initial value after the irradiation with 90 MGy. It was revealed from the changes in the profile of S-S curve that the specimen irradiated over 120 MGy was fractured due to not only fiber destruction but delamination. Deterioration mechanism of PEEK-PES-CF composite was studied by dynamic viscoelastic measurements in connection with the damage on matrix-fiber interface. It was suggested that the deterioration in mechanical properties of this composite was caused by the degradation of PES that coated on the surface of the carbon fibers. (author)

  20. A permanent magnet electron beam spread system used for a low energy electron irradiation accelerator

    International Nuclear Information System (INIS)

    Huang Jiang; Xiong Yongqian; Chen Dezhi; Liu Kaifeng; Yang Jun; Li Dong; Yu Tiaoqin; Fan Mingwu; Yang Bo

    2014-01-01

    The development of irradiation processing industry brings about various types of irradiation objects and expands the irradiation requirements for better uniformity and larger areas. This paper proposes an innovative design of a permanent magnet electron beam spread system. By clarifying its operation principles, the author verifies the feasibility of its application in irradiation accelerators for industrial use with the examples of its application in electron accelerators with energy ranging from 300 keV to 1 MeV. Based on the finite element analyses of electromagnetic fields and the charged particle dynamics, the author also conducts a simulation of electron dynamics in magnetic field on a computer. The results indicate that compared with the traditional electron beam scanning system, this system boosts the advantages of a larger spread area, non-power supply, simple structure and low cost, etc., which means it is not only suitable for the irradiation of objects with the shape of tubes, strips and panels, but can also achieve a desirable irradiation performance on irregular constructed objects of large size. (authors)

  1. Virus inactivation studies using ion beams, electron and gamma irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Smolko, Eduardo E. [Laboratorio de Polimeros, Grupo Aplicaciones Industriales, Unidad de Aplicaciones Tecnologicas y Agropecuarias, Centro Atomico Ezeiza, Comision Nacional de Energia Atomica, Pbro. Juan Gonzalez y Aragon 15, C.P. B1802AYA Ezeiza, Buenos Aires (Argentina)]. E-mail: smolko@cae.cnea.gov.ar; Lombardo, Jorge H. [Biotech S.A., C.P. 1754 Buenos Aires (Argentina)

    2005-07-01

    Known methods of virus inactivation are based on the chemical action of some substances such as acetylethylenimine, betapropiolactone, glycidalaldehyde, formaldehyde, etc. In such a process, the viral suspension should be kept at room or higher temperatures for 24-48 h. Under these conditions, physical and chemical agents act to degrade the virus antigenic proteins. On the contrary with ionizing radiations at low temperatures, the treatment does not cause such degradation allowing the study of different viral functions. In this work, particle ({alpha}, d and ss) and {gamma} irradiations were used for partial and total inactivation of Foot and Mouth Disease Virus (FMDV), Rauscher Leukemia Virus (RLV) and Herpes Simplex Virus (HSV). Obtention of the D{sub 37} dose from survival curves and the application of the target theory, permitted the determination of molecular weight of the nucleic acid genomes, EBR values and useful information for vaccine preparation. For RLV virus, a two target model of the RNA genome was deduced in accordance with biological information while from data from the literature and our own work on the structure of the scrapie prion, considering the molecular weight obtained by application of the theory, a new model for prion replication is presented, based on a trimer molecule.

  2. Virus inactivation studies using ion beams, electron and gamma irradiation

    International Nuclear Information System (INIS)

    Smolko, Eduardo E.; Lombardo, Jorge H.

    2005-01-01

    Known methods of virus inactivation are based on the chemical action of some substances such as acetylethylenimine, betapropiolactone, glycidalaldehyde, formaldehyde, etc. In such a process, the viral suspension should be kept at room or higher temperatures for 24-48 h. Under these conditions, physical and chemical agents act to degrade the virus antigenic proteins. On the contrary with ionizing radiations at low temperatures, the treatment does not cause such degradation allowing the study of different viral functions. In this work, particle (α, d and ss) and γ irradiations were used for partial and total inactivation of Foot and Mouth Disease Virus (FMDV), Rauscher Leukemia Virus (RLV) and Herpes Simplex Virus (HSV). Obtention of the D 37 dose from survival curves and the application of the target theory, permitted the determination of molecular weight of the nucleic acid genomes, EBR values and useful information for vaccine preparation. For RLV virus, a two target model of the RNA genome was deduced in accordance with biological information while from data from the literature and our own work on the structure of the scrapie prion, considering the molecular weight obtained by application of the theory, a new model for prion replication is presented, based on a trimer molecule

  3. Detection of electron beam irradiated crude drugs by electron spin resonance (ESR)

    International Nuclear Information System (INIS)

    Yamaoki, Rumi; Kimura, Shojiro; Aoki, Kenji; Nishimoto, Susumu

    2007-01-01

    Perillae Herba, Sennae Folium, Cinnamomi Cortex, Phellodendri Cortex, Ginseng Radix, Glycyrrhizae Radix, Paeoniae Radix, and Zingiberis Rhizoma were irradiated with electron beam (5 MeV) and organic radicals were detected by ESR measurement, before and after irradiation (10 kGy). A single line spectrum was detected at around g=2.005 in non-irradiated crude drugs, and radical concentrations were high in the leaf varieties of crude drugs. After irradiation, the signal intensity around g=2.005 increased, and a new subsignal was detected as a 3 mT shoulder of this signal. Broad, asymmetrically divided signals were also detected in irradiated root varieties of crude drugs. The free radical localized on the organic components of irradiated crude drugs tended to decrease with the water content. After irradiation, signal intensity reduced and reached a steady state after about 1 to 2 months. However, specificity of the ESR signal shape appearing after irradiation continued to be detectable for 6 months in leaf varieties and for a year in bark and root varieties of crude drugs. Consequently, it was concluded that ESR could be applied as an initial screening procedure to detect irradiated crude drugs. (author)

  4. Color formation study of irradiated polymers by electron beam

    International Nuclear Information System (INIS)

    Nardi, Daniela Teves

    2004-01-01

    Color formation on national and commercial polymers (polymethyl methacrylate, polystyrene and polycarbonate) irradiated by electrons beam was investigated by colorimetry (CIELab), electron spectroscopy resonance (ESR), photoacoustic infrared spectroscopy (FTIR-PAS) and differential exploratory calorimetry (DSC). The heat effect on colorimetric properties was investigated after heating (110 deg C for 1 hour) of irradiated polymers at 150 kGy. The rule of oxygen in colorimetric properties of irradiated polycarbonate was investigated in the air presence and absence (p = 10 -3 mmHg). The visual aspect did not agree with colorimetric parameters only for polycarbonate. Yellow color and darkness were induced by radiation for all studied polymers varying only the intensity and behavior in function of post-irradiation time and heating. Polymethyl methacrylate and polystyrene ESR spectra showed that radicals could be responsible by yellow color centers. Wherever, in polycarbonate, color centers were not due radical species. The nature of color centers for any studied polymer was not study by FTIR-PAS because there were no changes in FTIR-PAS spectra neither in function of dose nor heating. Polycarbonate was the most radiosensible and polystyrene was the most radioresistant of all studied polymers in concern of colorimetric properties. (author)

  5. Improvement of carbon fibre surface properties using electron beam irradiation

    International Nuclear Information System (INIS)

    Eddy Segura Pino; Luci Diva Brocardo Machado; Claudia Giovedi

    2006-01-01

    Carbon fiber-reinforced advance composites have been used for structural applications, mainly due to their mechanical properties, and additional features such as high strength-to-weight ratio, stiffness-to-weight ratio, corrosion resistance and wear properties. The main factor for a good mechanical performance of carbon fiber-reinforced composite is the interfacial interaction between the components that are fiber and polymeric matrix. The greatest challenge is to improve adhesion between components having elasticity modulus which differ by orders of magnitude and furthermore they are immiscible in each other. Another important factor is the sizing material on the carbon fiber, which protects the carbon fiber filaments and must be compatible with the matrix material in order to improve the adhesion process. The interaction of ionizing radiation from electron beam can induce in the irradiated material the formation of very active centers and free radicals. Further evolution of these active species can significantly modify structure and properties not only in the irradiated polymeric matrix but also on the fiber surface. So that, fiber and matrix play an important role in the production of chemical bonds, which promote better adhesion between both materials improving the composite mechanical performance. The aim of this work was to improve the surface properties of the carbon fiber surface using ionizing radiation from an electron beam in order to obtain improvement of the adhesion properties in the resulted composite. Commercial carbon fiber roving of high tensile strength with 12 000 filaments named 12 k, and sizing material of epoxy resin modified by ester groups was studied. EB irradiation has been carried out at the Institute for Nuclear and Energy Research (IPEN) facilities using a 1.5 MeV 37.5 kW Dynamitron electron accelerator model JOB-188. Rovings of carbon fibers with 1.78 g cm -3 density and 0.13 mm thickness were irradiated with 0.555 MeV, 6.43 mA and

  6. Origin of the Degradation of Triple Junction Solar Cells at low Temperature

    Directory of Open Access Journals (Sweden)

    Park Seonyong

    2017-01-01

    Full Text Available The degradation of solar cells under irradiation by high energy particles (electrons, protons is the consequence of the introduction of defects trapping minority carriers, which are then not collected by the junction. However, at low temperature, defects located in the space charge region can also induce a tunneling current that results in an apparent decreases of the maximum power. The degradation produced by this tunneling current can depend on temperature, since the concentration of defects created by an irradiation is usually temperature dependent, and can be larger than the degradation associated with carrier recombination. For instance, as we shall see below, an irradiation with 1 MeV electrons at 120 K with a fluence of 3.0 × 1015 /cm2 induces a decrease of less than 10 % in the short-circuit current (Isc and open-circuit voltage (Voc of triple junction (TJ cells, but a decrease of about 40 % in the maximum power (Pmax, which implies that more than half of the total degradation of Pmax should be assigned to another loss mechanism, tunneling in this case. In this work, we demonstrate that this additional degradation must indeed be ascribed to a tunneling process and we investigate the variation of the tunneling current versus fluence induced by electron irradiation in TJ cells, in order to tentatively ascribe the tunneling components to specific sub-cells.

  7. Electron spin resonance of gamma, electron, neutron and fission fragments irradiated K2SO4

    International Nuclear Information System (INIS)

    Kamali, J.; Walton, G.N.

    1985-01-01

    The electron spin resonance (ESR) of K 2 SO 4 irradiated by γ, electron, neutron and fission fragments has been investigated. The ESR spectra are attributed mainly to the formation of SO 3 - , SO 4 - , SO 2 - , and O 3 - radical ions. The most intense radical ion observed was due to the SO 3 - , and the other radicals were relatively much lower in intensity. Thermal annealing showed a significant decrease in the concentration of radical ions. The concentration of SO 3 - was measured in γ-irradiated K 2 SO 4 and K 2 SO 4 containing fission fragments. In fission fragments irradiated K 2 SO 4 , the G-value observed for SO 3 - radical formation was about eight times higher than that of γ-irradiated K 2 SO 4 . This was attributed to the high LET (Linear Energy Transfer) of the fission fragments. (author)

  8. Bulk Cutting of Carbon Nanotubes Using Electron Beam Irradiation

    Science.gov (United States)

    Ziegler, Kirk J. (Inventor); Rauwald, Urs (Inventor); Hauge, Robert H. (Inventor); Schmidt, Howard K. (Inventor); Smalley, Richard E. (Inventor); Kittrell, W. Carter (Inventor); Gu, Zhenning (Inventor)

    2013-01-01

    According to some embodiments, the present invention provides a method for attaining short carbon nanotubes utilizing electron beam irradiation, for example, of a carbon nanotube sample. The sample may be pretreated, for example by oxonation. The pretreatment may introduce defects to the sidewalls of the nanotubes. The method is shown to produces nanotubes with a distribution of lengths, with the majority of lengths shorter than 100 tun. Further, the median length of the nanotubes is between about 20 nm and about 100 nm.

  9. Positron lifetime study of electron-irradiated epoxy resins

    International Nuclear Information System (INIS)

    Suevegh, K.; Vertes, A.; Wojnarovits, L.; Foeldiak, G.; Liszkai, L.; Kajcsos, Zs.

    1990-01-01

    Two bisphenol-A type epoxy resins were irradiated by electron beam and studied afterwards by positron lifetime spectroscopy. An interesting result is that despite of the considerable amount of free-radicals, no inhibition of positronium formation was observed in the two epoxies. Nevertheless, several serious differences were detected between the studied polymers. The results suggest that the radiation-resistant properties of epoxies depend strongly on the amount of the curing agent. (author) 8 refs.; 2 figs

  10. Technological aspects of UO2 sintering at low temperature

    International Nuclear Information System (INIS)

    Thern, Gerardo G.; Dominguez, Carlos A.; Benitez, Ana M.; Marajofsky, Adolfo

    1999-01-01

    Within the Fuel Cycle Program of CNEA, the knowledge that plant personnel has on sintering at low temperature was evaluated, because this process could decrease costs for UO 2 and (U,Gd)O 2 pellets production, simplify the furnace maintenance and facilitate the automation of the production process, specially convenient for uranium recovery. By applying this technology, some companies have achieved production at pilot-scale and irradiated a significant number of pellets. (author)

  11. Thermoluminescence in KBr:D electron irradiated at room temperature

    International Nuclear Information System (INIS)

    Paredes Campoy, J.C.; Lopez Carranza, E.

    1991-07-01

    The thermoluminescence of KBr:D samples electron irradiated at room temperature after thermal annealing at 673 K for 1 hour have been studied in the temperature range 360-730 K. The experimental TL-curve was discomposed by computer analysis in seven overlapping TL peaks, giving for them the order of the kinetics of thermal stimulation, the activation energy, the frequency factor, the relative values of the electronic concentration in traps at the initial heating temperature and the temperature at the maximum of the peak. (author). 18 refs, 1 fig., 3 tabs

  12. Positron annihilation in hydrogenated and electron-irradiated titanium alloys

    International Nuclear Information System (INIS)

    Mukashev, K.M.; Zaikin, Yu.A.

    2002-01-01

    Important information on hydrogen behavior in titanium can be obtained from studies of radiation damage in previously hydrogenated metal. For this purpose annealed titanium samples were hydrogenated at the temperature 500 deg. C during 1 hour. Then both the original annealed samples and hydrogenated samples were irradiated by 4 MeV electrons in the fluence range 3·10 7 -1·10 19 cm - 2 at the temperature 60 deg. C. It is known that electron irradiation in these conditions predominantly creates vacancy-type defects with an average radius R ν =0.81 Angstrom. It was stated that annihilation probability after electron irradiation of previously hydrogenated titanium samples always has some intermediate values between those characteristic for hydrogenated and irradiated states of previously annealed metal. This is a reason to suppose that radiation defects of the vacancy type in previously hydrogenated titanium combine with hydrogen atoms in favorable conditions of their partial ionization. The estimated value of the average radius for such a complex is R ν =1.1 Angstrom, that is higher than vacancy size but lower than an atom radius. No dose dependence of hydrogen interaction with radiation defects was observed in our experiments.The results of isochrone annealing of the materials under study have shown that the single annealing recovery stage with activation energy E a equal to 1.22 eV is observed in electron irradiated but not previously hydrogenated titanium in the temperature range 170-240 deg. C. Electron irradiation of the previously hydrogenated metal shifts beginning of the first recovery stage to the temperature about 225-230 deg. C and finishes near the temperature 330 deg. C. Therefore, the bound state vacancy-hydrogen in titanium is characterized by higher temperature range of dissociation and annealing with activation energy equal to 1.38 eV. However, subsequent measurements, of the angular distribution of annihilation photons (ADAP) have demonstrated

  13. Dosimetry study for electron beam irradiation in radiation processing

    International Nuclear Information System (INIS)

    Sunaga, Hiromi; Haruyama, Yasuyuki; Takizawa, Haruki; Kojima, Takuji; Yotsumoto, Keiichi

    1995-01-01

    For certain critical applications such as medical device sterilization and food irradiation, accurate calibration of electron energy and absorbed dose is required to assure the quality of irradiated products. To meet this requirement, TRCRE, JAERI has carried out research and development on high dose radiation dosimetry for electron beams in the energy range used in radiation processing (0.15 - 3.0 MeV). JAERI has developed a simultaneous electron beam energy and dosimeter calibration system that consist of a total absorption calorimeter, an electron current density meter, and a stacked thin-film dosimeter set. For low energy electrons, where it is important to measure the depth-dose profile in materials with high depth resolution, we studied the feasibility of a method using Gafchromic film dosimeters. This film, which has an 8-μm thick sensitive layer, is combined with a stepped array of absorber films of the same thickness to produce a high-resolution depth-dose profile on the Gafchromic film. The depth-dose profile obtained in this manner has about five times greater resolution than conventional radiochromic film dosimetry. (author)

  14. Space-charge-limited currents in electron-irradiated dielectrics

    International Nuclear Information System (INIS)

    Nunes de Oliveira, L.; Gross, B.

    1975-01-01

    This paper develops the theory of steady-state currents generated in a dielectric placed between positively or negatively biased electrodes and irradiated with a partially penetrating electron beam. The dielectric is divided into an irradiated region (IR), which extends from the electrode of incidence to the extrapolated range of the beam, and a nonirradiated region (NIR). In the IR the primary beam generates an electron-hole plasma. Its end plane acts as a virtual electrode embedded in the dielectric. Currents are space-charge limited in the NIR and Ohmic in the IR which is characterized by a uniform radiation-induced conductivity. Depending on the polarity of the electrode bias, electrons or holes are drawn from the IR into the NIR. The theory correctly predicts an apparent threshold effect for the inset of steady-state currents: the current amplitudes remain small as long as the electron range is smaller than half the sample thickness, and increase strongly only afterwards. Calculated current curves for different beam energies are in satisfactory agreement with experimental results. The role of the electron beam as a virtual electrode is discussed

  15. Disinfection of wastewaters: high-energy electron vs gamma irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Farooq, S [King Fahd Univ. of Petroleum and Minerals, Dhahran (Saudi Arabia). Dept. of Civil Engineering; Kurucz, C N; Waite, T D [Miami Univ., Coral Gables, FL (United States); Cooper, W J [Florida International Univ., Miami, FL (United States). Drinking Water Research Center

    1993-07-01

    A study was undertaken to examine the sensitivity of a wastewater population of coliphage, total coliforms and total flora present in raw sewage and secondary effluent after irradiating with similar doses delivered by a high-energy electron beam and [gamma]-radiation. The electron beam study was conducted on a large scale at the Virginia Key Wastewater Treatment Plant, Miami, Florida. The facility is equipped with a 1.5 MeV, 50 mA electron accelerator, with a wastewater flow rate of 8ls[sup -1]. Concurrent [gamma]-radiation studies were conducted at laboratory scale using a 5000 Ci, [sup 60]Co [gamma]-source. Three logs reduction of all three test organisms were observed at an electron beam dose of 500 krads, while at least four logs reduction were observed at the same dose utilizing the [gamma]'source. (Author).

  16. Work related to increasing the exploitation and experimental possibilities of the RA reactor, 05. Independent CO2 loop for cooling the samples irradiated in the RA vertical experimental channels (IIV), Part I, IZ-240-o379-1963, Vol. I, Head of the low temperature RA reactor coolant loop

    International Nuclear Information System (INIS)

    Pavicevic, M.

    1963-07-01

    The objective of the project was to design the head of the CO 2 coolant loop for cooling the materials during irradiation in the RA reactor. Six heads of coolant loops will be placed in the RA reactor, two in the region of heavy water in the experimental channels VEK-6 and four in the graphite reflector in the channels VEK-G. Materials for irradiation are metallurgy and chemical samples. In addition to the project objectives, this volume includes technical specifications of the coolant loop head, thermal calculations, calculations of mechanical stress, antireactivity and activation of the construction materials, cost estimation, scheme of the coolant loop head, diagrams of CO 2 gas temperature, thermal neutron flux distribution, design specifications of two proposed solutions for head of low temperature coolant loop [sr

  17. Low temperature study of nonstoichiometric titanium carbide

    International Nuclear Information System (INIS)

    Tashmetov, M.Yu.

    2005-05-01

    By low temperature neutron diffraction method was studied structure in nonstoichiometric titanium carbide from room temperature up to 12K. It is found of low temperature phase in titanium carbide- TiC 0.71 . It is established region and borders of this phase. It is determined change of unit cell parameter. (author)

  18. Low-temperature plasma modelling and simulation

    NARCIS (Netherlands)

    Dijk, van J.

    2011-01-01

    Since its inception in the beginning of the twentieth century, low-temperature plasma science has become a major ¿eld of science. Low-temperature plasma sources and gas discharges are found in domestic, industrial, atmospheric and extra-terrestrial settings. Examples of domestic discharges are those

  19. Thermal conductivity at very low temperature

    Energy Technology Data Exchange (ETDEWEB)

    Locatelli, M [CEA Centre d' Etudes Nucleaires de Grenoble, 38 (France). Service des Basses Temperatures

    1976-06-01

    The interest of low and very low temperatures in solid physics and especially that of thermal measurements is briefly mentioned. Some notes on the thermal conductivity of dielectrics, the method and apparatus used to measure this property at very low temperatures (T<1.5K) and some recent results of fundamental and applied research are then presented.

  20. The effect of simultaneous electron and Kr+ irradiation on amorphization of CuTi

    International Nuclear Information System (INIS)

    Koike, J.; Okamoto, P.R.; Rehn, L.E.; Meshii, M.

    1989-01-01

    CuTi was irradiated with 1-MeV electrons and Kr + ions simultaneously at temperatures from 10 to 423 K. Retardation of Kr + -induced amorphization was observed with simultaneous electron irradiation at 295 and 423 K. The retardation effect increased with increasing irradiation temperature and relative electron-to-Kr dose rate. In contrast, simultaneous irradiation below 100 K showed an additive effect of electron- and Kr + -induced amorphization. The results can be explained by the mobility point defects introduced by electron irradiation interacting with Kr + -induced displacement cascades. 6 refs., 6 figs

  1. Strong anisotropy in the low temperature Compton profiles of ...

    Indian Academy of Sciences (India)

    Compton profiles of momentum distribution of conduction electrons in the orthorhombic phase of -Ga metal at low temperature are calculated in the band model for the three crystallographic directions (100), (010), and (001). Unlike the results at room temperature, previously reported by Lengeler, Lasser and Mair, the ...

  2. Vulcanization of rubber mixtures by simultaneous electron beam and microwave irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Martin, D. E-mail: martin@ifin.nipne.ro; Ighigeanu, D.; Mateescu, E.; Craciun, G.; Ighigeanu, A

    2002-08-01

    The comparative results obtained by applying separate electron beam (EB) irradiation and simultaneous EB and microwave (MW) irradiation to vulcanization of rubber mixtures based on natural rubber and polybutadiene rubber with carbon black are presented. In the absence of MW, EB irradiation doses of 200-250 kGy are required in order to obtain a higher vulcanization degree. The irradiation doses as well as irradiation times were markedly diminished, from 2 to 6 times, by simultaneous EB and MW irradiation.

  3. Lifetime of Macroradicals in UHMWPE Irradiated with Electron Beam

    International Nuclear Information System (INIS)

    Costa, L.

    2006-01-01

    Interaction of high energy radiation with UHMWPE leads to the scission of C-C and C-H bonds both in the amorphous and in the criystalline phase, giving H radicals, macroradicals and trans vinylene double bonds. If oxygen is present, alkyl macroradicals react immediately with it and the oxidation chain process begins. In this case the main products are hydroperoxides. In our laboratory ultra high molecular weight polyethylene (medical grade GUR 1050) has been irradiated with electron beam in vacuum and in presence of oxygen at room temperature. Electron beam irradiation has been considered in order to neglect irradiation time, that is shorter (maximum 2 minutes) than gamma irradiation time and negligible compared to the following observation time. UHMWPE irradiated has been examined with two different techniques, FTIR and EPR spectroscopy. Micro FTIR Spectroscopy has been carried out on UHMWPE to evaluate hydroperoxide concentration in samples irradiated in presence of oxygen. Hydroperoxides and their distribution inside samples can be observed very well with FTIR microscopy after a derivatization process (with NO). The obtained hydroperoxide profile decreases when distance from the outer surface increases till it achieves a plateau. The first decrease can be attributed to macroradicals reaction with oxygen, that can diffuse only in the amorphous phase. Value obtained in the centre of block is correlated only with oxygen dissolved in UHMWPE before irradiation. If radicals live for some hours, oxygen can diffuse into UHMWPE during the macroradicals lifetime and the hydroperoxides profile is a curve similar to that obtained. Comparing the oxygen diffusion curve, calculated in the function of Fick's law, with the hydroperoxide profile, we have obtained a good agreement when oxygen diffusion is calculated over two hours. This means that the macroradicals must survive at least for two hours in the amorphous phase. EPR Spectroscopy was undertaken to explore the nature of

  4. ESR low-temperature investigations on water-containing biological substances to determine type, concentration and kinetics of the free radicals induced by irradiation with X-rays and β-radiation

    International Nuclear Information System (INIS)

    Fell, H.A.

    1975-01-01

    In the present work, ESR investigations on pure water and further biological interesting substances with high water content were carried out. In order to stabilize the free primary radicals occurring after irradiation, it was necessary to cool down the samples to the temperature of liquid helium. Methods were developed which enabled irradiation of the pure sample substance at this temperature to be performed. Two different kinds of radiation were applied, X-ray and β-radiation, and the results were compared with one another. The problem of transporting the irradiated sample from the place of irradiation to the measuring position maintaining 4.2 K was solved. A device was constructed to study the radical kinetics with whose assistance the samples can be brought to a pre-chosen temperature for a certain time. A calibration of the ESR spectrometer as well as the use of a secondary standard was necessary for the quantitative determination of the radical concentration. The type and concentration of the primary radicals occurring were investigated in the measured samples as well as the reduction of the radical concentration with increasing temperature determined. The measured values were compared with theoretical considerations. The effect of the radicals on biological systems at various temperatures was discussed. (orig./LH) [de

  5. Radiation doses inside industrial irradiation installation with linear electron accelerator

    Energy Technology Data Exchange (ETDEWEB)

    Lima, Alexandre R., E-mail: alexandre.lima@cnen.gov.br [Comissao Nacional de Energia Nuclear (CNEN), Rio de Janeiro, RJ (Brazil); Pelegrineli, Samuel Q.; Alo, Gabriel F., E-mail: samuelfisica@yahoo.com.br, E-mail: gabriel.alo@aceletron.com.br [Aceletron Irradiacao Industrial, Aceletrica Comercio e Representacoes Ltda, Rio de Janeiro, RJ (Brazil); Silva, Francisco C.A. Da, E-mail: dasilva@ird.gov.br [Instituto de Radioprotecao e Dosimetria (IRD/CNEN-RJ), Rio de Janeiro, RJ (Brazil)

    2015-07-01

    Aceletron Industrial Irradiation Company is the unique installation in South America to provide industrial irradiation service using two linear electron accelerators of 18 kW and 10 MeV energy. The electron beam technology allows using electrons to irradiate many goods and materials, such as hospital and medical equipment, cosmetics, herbal products, polymers, peat, gemstones and food. Aceletron Company uses a concrete bunker with 3.66 m of thickness to provide the necessary occupational and environmental radiation protection of X-rays produced. The bunker is divided in main four areas: irradiation room, maze, tower and pit. Inside the irradiation room the x-rays radiation rates are measured in two ways: direct beam and 90 deg C. The rates produced in the conveyor system using 10 MeV energy are 500 Gy/min/mA and 15 Gy/min/mA, respectively. For a 1.8 mA current, the rates produced are 900 Gy/min and 27 Gy/min, respectively. Outside the bunker the radiation rate is at background level, but in the tower door and modulation room the radiation rate is 10 μSv/h. In 2014, during a routine operation, an effective dose of 30.90 mSv was recorded in a monthly individual dosimeter. After the investigation, it was concluded that the dose was only in the dosimeter because it felt inside the irradiation room. As Aceletron Company follows the principles of safety culture, it was decided to perform the radiation isodose curves, inside the four areas of the installation, to know exactly the hotspots positions, exposure times and radiation doses. Five hotspots were chosen taking into account worker's routes and possible operational places. The first experiment was done using a package with three TLD and OSLD dosimeters to obtain better statistical results. The first results for the five hotspots near the accelerator machine showed that the radiation dose rates were between 26 Gy/h and 31 Gy/h. The final measurements were performed using a package with one TLD and one OSLD

  6. Radiation doses inside industrial irradiation installation with linear electron accelerator

    International Nuclear Information System (INIS)

    Lima, Alexandre R.; Pelegrineli, Samuel Q.; Alo, Gabriel F.; Silva, Francisco C.A. Da

    2015-01-01

    Aceletron Industrial Irradiation Company is the unique installation in South America to provide industrial irradiation service using two linear electron accelerators of 18 kW and 10 MeV energy. The electron beam technology allows using electrons to irradiate many goods and materials, such as hospital and medical equipment, cosmetics, herbal products, polymers, peat, gemstones and food. Aceletron Company uses a concrete bunker with 3.66 m of thickness to provide the necessary occupational and environmental radiation protection of X-rays produced. The bunker is divided in main four areas: irradiation room, maze, tower and pit. Inside the irradiation room the x-rays radiation rates are measured in two ways: direct beam and 90 deg C. The rates produced in the conveyor system using 10 MeV energy are 500 Gy/min/mA and 15 Gy/min/mA, respectively. For a 1.8 mA current, the rates produced are 900 Gy/min and 27 Gy/min, respectively. Outside the bunker the radiation rate is at background level, but in the tower door and modulation room the radiation rate is 10 μSv/h. In 2014, during a routine operation, an effective dose of 30.90 mSv was recorded in a monthly individual dosimeter. After the investigation, it was concluded that the dose was only in the dosimeter because it felt inside the irradiation room. As Aceletron Company follows the principles of safety culture, it was decided to perform the radiation isodose curves, inside the four areas of the installation, to know exactly the hotspots positions, exposure times and radiation doses. Five hotspots were chosen taking into account worker's routes and possible operational places. The first experiment was done using a package with three TLD and OSLD dosimeters to obtain better statistical results. The first results for the five hotspots near the accelerator machine showed that the radiation dose rates were between 26 Gy/h and 31 Gy/h. The final measurements were performed using a package with one TLD and one OSLD

  7. Application of electron paramagnetic resonance to identify irradiated soybean

    International Nuclear Information System (INIS)

    Bhaskar, S.; Behere, Arun; Sharma, Arun

    2006-01-01

    Full text: Electron paramagnetic resonance spectroscopy was applied to study free radicals in soy bean seed after gamma irradiation and to establish the potential of these radiation induced free radicals as the indicator of the radiation treatment. The radiation doses administered to the samples were 1 to 30 kGy. A stable doublet signal was detected at g = 2.0279 with hyperfine coupling constant of 2.8 mT, produced only by radiolysis. This signal can be used to identify irradiated soy bean seed samples. With the increase of the radiation dose the central line intensity and the intensities of the satellite lines showed almost a linear rise having linear correlation factors of 0.99724 and 0.99996, respectively. Thermal treatment at 373 deg K in air was studied. No line specific to thermolysis was observed. The spectrometer was operated with power 0.253 mW, microwave frequency 9.74 GHz, modulation frequency 100 kHz and scan range 10 mT. To study the stability of the signal, EPR spectra were obtained from the irradiated skin part of soy bean seeds samples following 1 and 90 days of storage after radiation treatment. The two satellite lines of g left = 2.0279 and g right 1.99529 were detected in all samples. This suggests that the signal is associated with a stable radical and therefore, the detection of a particular free radical as a marker of irradiation is proposed

  8. Irradiation Effects of Electron Beam on Optical Fibers

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Jin Kyu; Cho, Gyu Seong [KAIST, Daejeon (Korea, Republic of); Choi, Hong Gu; Oh, Kyung Hwan [Yonsei University, Seoul (Korea, Republic of); Cho, Ho Jin [Nucron Co. Ltd., Seoul (Korea, Republic of)

    2009-10-15

    The surveillance or monitoring systems used in space station, nuclear power plant and nuclear waste repository, are often equipped with optical fibers to remotely locating expensive camera systems so as to protect them from direct irradiation. Especially in nuclear power plant and nuclear waste repository, irradiation by gamma-ray and beta-ray are most concerned. The effective life-time of such surveillance system may depend on the soundness of the optical fiber because it is the component to be exposed the high intensity of radiation field by purpose. Though the degradation of mechanical properties such as hardness and elasticity may occur but the degradation of the optical property such as spectral transmittance is the most possible cause of the effective life-time limitation. Generally 30 % reduction of light signal transmittance is considered as the life-time threshold point of such optical systems. In this paper, we studied irradiation effects on spectral transparency of various commonly-used optical fibers with high energy electron beam to conveniently simulate the both gamma-ray and beta-ray irradiation situation.

  9. Electron beam irradiation effects on xanthan gum. Rheological aspects

    International Nuclear Information System (INIS)

    Vieira, F.F.; Del Mastro, N.L.

    2001-01-01

    The paper describes the application of electron beam irradiation to xanthum gum as used as ingredient by the food or cosmetics industry in order to establish their radiosensitivity. The edible powder of xanthum gum samples were irradiated in 1mm thick layers of Petri dishes covered by a transparent PVC of films using an EB accelerator Dynamitron (Radiation Dynamics Inc.) model JOB 188, dose rate 11.17 kGy/s, 0.637 MeV, 1.78 mA, 5 kGy per passage, 3.36 m min -1 with doses of 5, 10, 20 and 50kGy. One % aqueous solutions from irradiated and non-irradiated xanthum gum were prepared and the radiation effects were measured following viscosity changes at 25 deg. C using a Brookfield viscometer; model DVIII, spindel L, with Rheocalc software. Viscosity measurements were performed according to our previous experience and the results are the mean of at least 3 experiments

  10. An experimental investigation of wastewater treatment using electron beam irradiation

    Science.gov (United States)

    Emami-Meibodi, M.; Parsaeian, M. R.; Amraei, R.; Banaei, M.; Anvari, F.; Tahami, S. M. R.; Vakhshoor, B.; Mehdizadeh, A.; Fallah Nejad, N.; Shirmardi, S. P.; Mostafavi, S. J.; Mousavi, S. M. J.

    2016-08-01

    Electron beam (EB) is used for disinfection and treatment of different types of sewage and industrial wastewater. However, high capital investment required and the abundant energy consumed by this process raise doubts about its cost-effectiveness. In this paper, different wastewaters, including two textile sewages and one municipal wastewater are experimentally studied under different irradiation strategies (i.e. batch, 60 l/min and 1000 m3/day) in order to establish the reliability and the optimum conditions for the treatment process. According to the results, EB improves the efficiency of traditional wastewater treatment methods, but, for textile samples, coagulation before EB irradiation is recommended. The cost estimation of EB treatment compared to conventional methods shows that EB has been more expensive than chlorination and less expensive than activated sludge. Therefore, EB irradiation is advisable if and only if conventional methods of textile wastewater treatment are insufficient or chlorination of municipal wastewater is not allowed for health reasons. Nevertheless, among the advanced oxidation processes (AOP), EB irradiation process may be the most suitable one in industrial scale operations.

  11. Optical properties of electron-irradiated gallium phosphide

    International Nuclear Information System (INIS)

    Brailovskii, E.Yu.; Grigoryan, N.E.; Eritsyan, G.N.

    1980-01-01

    Results of optical absorption and photoconductivity measurements in the 0.1 to 2.4 eV range of GaP crystals irradiated with 7.5 and 50 MeV electrons are presented. The absorption of irradiated crystals near the edge can be represented by two exponential regions. In the free carrier absorption region one can observe as a result of irradiation a decrease of the power index p in the dependence α proportional to lambdap. Photoconductivity with long-time relaxation takes place in the spectral interval where the additional absorption is observed. The quenching of residual conductivity can be observed at hν=1.0eV. Variations in absorption and photoconductivity are attributed to the 'tails' of density states near the zone edges arising at introduction of both point defects and disordered regions. At hν=2.1eV one can observe a resonance band which is attributed to intra-centre transitions on point defects. A recovery of the optical properties of GaP at annealing is studied. In heavily irradiated GaP crystals point defects can form gatherings which display themselves as disordered regions. (author)

  12. Physicochemical Study of Irradiated polypropylene/Organo :Modified Montmorillonite Composites by Using Electron Beam Irradiation Technique

    International Nuclear Information System (INIS)

    Hassan, M.S.

    2008-01-01

    Polypropylene/ Organo modified montmorillonite composites (PP/ OMMT) were prepared by melt blending with a twin screw extruder. The thermal properties by thermo gravimetric analysis (TGA), the dispersion of OMMT of macromolecules by X-ray diffraction (XRD), mechanical properties and the morphology by scanning electron microscopy (SEM) were investigated. The effect of electron beam irradiation on these properties was also studied. The results showed an intercalation between the silicate layers and the PP polymer matrix. The (PP/ OMMT) composites exhibit higher thermal stability and lower mechanical properties than pure polypropylene

  13. Oxidative decomposition of aromatic hydrocarbons by electron beam irradiation

    Science.gov (United States)

    Han, Do-Hung; Stuchinskaya, Tatiana; Won, Yang-Soo; Park, Wan-Sik; Lim, Jae-Kyong

    2003-05-01

    Decomposition of aromatic volatile organic compounds (VOCs) under electron beam irradiation was studied in order to examine the kinetics of the process, to characterize the reaction product distribution and to develop a process of waste gas control technology. Toluene, ethylbenzene, o-, m-, p-xylenes and chlorobenzene were used as target materials. The experiments were carried out at doses ranging from 0.5 to 10 kGy, using a flow reactor utilized under electron beam irradiation. Maximum degrees of decomposition carried out at 10 kGy in air environment were 55-65% for “non-chlorinated” aromatic VOC and 85% for chlorobenzene. It was found that a combination of aromatic pollutants with chlorobenzene would considerably increase the degradation value up to nearly 50% compared to the same compounds in the absence of chlorine groups. Based on our experimental observation, the degradation mechanism of the aromatic compounds combined with chloro-compound suggests that a chlorine radical, formed from EB irradiation, induces a chain reaction, resulting in an accelerating oxidative destruction of aromatic VOCs.

  14. Experiments on Quantum Hall Topological Phases in Ultra Low Temperatures

    International Nuclear Information System (INIS)

    Du, Rui-Rui

    2015-01-01

    This project is to cool electrons in semiconductors to extremely low temperatures and to study new states of matter formed by low-dimensional electrons (or holes). At such low temperatures (and with an intense magnetic field), electronic behavior differs completely from ordinary ones observed at room temperatures or regular low temperature. Studies of electrons at such low temperatures would open the door for fundamental discoveries in condensed matter physics. Present studies have been focused on topological phases in the fractional quantum Hall effect in GaAs/AlGaAs semiconductor heterostructures, and the newly discovered (by this group) quantum spin Hall effect in InAs/GaSb materials. This project consists of the following components: 1) Development of efficient sample cooling techniques and electron thermometry: Our goal is to reach 1 mK electron temperature and reasonable determination of electron temperature; 2) Experiments at ultra-low temperatures: Our goal is to understand the energy scale of competing quantum phases, by measuring the temperature-dependence of transport features. Focus will be placed on such issues as the energy gap of the 5/2 state, and those of 12/5 (and possible 13/5); resistive signature of instability near 1/2 at ultra-low temperatures; 3) Measurement of the 5/2 gaps in the limit of small or large Zeeman energies: Our goal is to gain physics insight of 5/2 state at limiting experimental parameters, especially those properties concerning the spin polarization; 4) Experiments on tuning the electron-electron interaction in a screened quantum Hall system: Our goal is to gain understanding of the formation of paired fractional quantum Hall state as the interaction pseudo-potential is being modified by a nearby screening electron layer; 5) Experiments on the quantized helical edge states under a strong magnetic field and ultralow temperatures: our goal is to investigate both the bulk and edge states in a quantum spin Hall insulator under

  15. Electron arc therapy: chest wall irradiation of breast cancer patients

    International Nuclear Information System (INIS)

    McNeely, L.K.; Jacobson, G.M.; Leavitt, D.D.; Stewart, J.R.

    1988-01-01

    From 1980 to October 1985 we treated 45 breast cancer patients with electron arc therapy. This technique was used in situations where optimal treatment with fixed photon or electron beams was technically difficult: long scars, recurrent tumor extending across midline or to the posterior thorax, or marked variation in depth of target tissue. Forty-four patients were treated following mastectomy: 35 electively because of high risk of local failure, and 9 following local recurrence. One patient with advanced local regional disease was treated primarily. The target volume boundaries on the chest wall were defined by a foam lined cerrobend cast which rested on the patient during treatment, functioning as a tertiary collimator. A variable width secondary collimator was used to account for changes in the radius of the thorax from superior to inferior border. All patients had computerized tomography performed to determine Internal Mammary Chain depth and chest wall thickness. Electron energies were selected based on these thicknesses and often variable energies over different segments of the arc were used. The chest wall and regional node areas were irradiated to 45 Gy-50 Gy in 5-6 weeks by this technique. The supraclavicular and upper axillary nodes were treated by a direct anterior photon field abutted to the superior edge of the electron arc field. Follow-up is from 10-73 months with a median of 50 months. No major complications were observed. Acute and late effects and local control are comparable to standard chest wall irradiation. The disadvantages of this technique are that the preparation of the tertiary field defining cast and CT treatment planning are labor intensive and expensive. The advantage is that for specific clinical situations large areas of chest wall with marked topographical variation can be optimally, homogeneously irradiated while sparing normal uninvolved tissues

  16. New crosslinked polyvinyl chloride insulated wire by electron beam irradiation

    International Nuclear Information System (INIS)

    Takahata, Norio; Shingyouchi, Kazuo; Sato, Masakatsu; Sasaki, Hidemi; Terunuma, Haruji

    1978-01-01

    The polyvinyl chloride-coated wires crosslinked by electron beam irradiation have made rapid progress as electric and electronic wiring material and grown to hold a firm position in this field. In response to the requirements for wires with the advance of electronic equipments, Hitachi Cable Ltd. developed a peculiar graft polymer consisting of chlorinated polyethylene and polyvinyl chloride. To this polymer, the characteristics of a very wide range from toughness to flexibility can be given, and the crosslinked polyvinyl chloride wires utilizing these characteristics were put in practical use. Many kinds of the wires were developed as follows; 105 deg. C rating crosslinked vinyl-coated wires authorized by UL and CSA standards, crosslinked vinyl-coated wires with excellent flexibility, high strength crosslinked vinyl-coated wires with thin coating and crosslinked vinyl-coated wires for automobiles. They are expected to be developed into other new fields and applications. (Kobatake, H.)

  17. A set of dosimetry systems for electron beam irradiation

    International Nuclear Information System (INIS)

    Lin Min; Lin Jingwen; Chen Yundong; Li Huazhi; Xiao Zhenhong; Gao Juncheng

    1999-01-01

    To follow the rapid development of radiation processing with electron beams, it is urgent to set up a set of dosimetric standards to provide Quality Assurance (QA) of electron beam irradiation and unify the values of the quality of the absorbed dose measurements for electron beams. This report introduces a set of dosimetry systems established in Radiometrology Center of China Institute of Atomic Energy (RCCIAE), which have been or will be used as dosimetric standards in the Nuclear Industry System (NIS) in China. For instance, the potassium (silver) dichromate and ceric-cerous sulfate dosimetry systems will be used as standard dosimeters, while alanine-ESR dosimetry system as a transfer dosimeter, and FJL-01 CTA as a routine dosimeter. (author)

  18. Comparison of three techniques for skin total irradiation with electrons

    International Nuclear Information System (INIS)

    Batista, Delano V.S.; Bardella, Lucia H.; Rosa, Luiz A.R. da

    2011-01-01

    This paper compared three techniques of skin total irradiation with electrons: 1) horizontal positioning, 2) vertical positioning - rotatory technique and 3) vertical positioning - six fields technique. For that, a anthropomorphic phantom was positioned according to the recommendation for each technique and was i radiated at the linear accelerator by using the 6 MeV electrons. Radiochromic films were positioned on the surface in various regions of the phantom for measurement of absorbed dose. A ionization chamber was positioned inside of equivalent issue plates for dose evaluation due to the photons produced by electron stopping. The technique 2 and 3 have shown too similar in the results and number or discrepant points (8 and 10 respectively) of prescription lower than the technique 1 (22 points). The total body dose of photons of the 1, 2 and 3 techniques was 2.2%, 5.3% and 5.2% respectively

  19. Radiation Safety of Gamma, Electron and X Ray Irradiation Facilities. Specific Safety Guide (Spanish Edition)

    International Nuclear Information System (INIS)

    2015-01-01

    The objective of this Safety Guide is to provide recommendations on how to meet the requirements of the BSS with regard to irradiation facilities. This Safety Guide provides specific, practical recommendations on the safe design and operation of gamma, electron and X ray irradiators for use by operating organizations and the designers of these facilities, and by regulatory bodies. SCOPE. The facilities considered in this publication include five types of irradiator, whether operated on a commercial basis or for research and development purposes. This publication is concerned with radiation safety issues and not with the uses of irradiators, nor does it cover the irradiation of product or its quality management. The five types of irradiator are: - Panoramic dry source storage irradiators; - Underwater irradiators, in which both the source and the product being irradiated are under water; - Panoramic wet source storage irradiators; - Electron beam irradiation facilities, in which irradiation is performed in an area that is potentially accessible to personnel, but that is kept inaccessible during the irradiation process; - X ray irradiation facilities, in which irradiation is performed in an area that is potentially accessible to personnel, but that is kept inaccessible during the irradiation process. Consideration of non-radiation-related risks and of the benefits resulting from the operation of irradiators is outside the scope of this Safety Guide. The practices of radiotherapy and radiography are also outside the scope of this Safety Guide. Category I gamma irradiators (i.e. 'self-shielded' irradiators) are outside the scope of this Safety Guide

  20. Electron-irradiation-induced crystallization of amorphous orthophosphates

    International Nuclear Information System (INIS)

    Meldrum, A.; Ewing, R.C.; Boatner, L.A.

    1996-12-01

    Amorphous LaPO 4 , EuPO 4 , GdPO 4 , ScPO 4 , and fluorapatite [Ca 5 (PO 4 ) 3 F] were irradiated by electron beam in a TEM. Irradiations were done at -150 to 300 C, 80 to 200 keV, and current densities from 0.3 to 16 A/cm 2 . In all cases, the materials crystallized to form a randomly oriented polycrystalline assemblage. Crystallization is driven dominantly by inelastic processes, although ballistic collisions with target nuclei can be important above 175 keV, particularly in apatite. Using a high current density, crystallization is so fast that continuous lines of crystallites can be ''drawn'' on the amorphous matrix