WorldWideScience

Sample records for low-modulus pmma cement

  1. Low-modulus PMMA bone cement modified with castor oil.

    Science.gov (United States)

    López, Alejandro; Hoess, Andreas; Thersleff, Thomas; Ott, Marjam; Engqvist, Håkan; Persson, Cecilia

    2011-01-01

    Some of the current clinical and biomechanical data suggest that vertebroplasty causes the development of adjacent vertebral fractures shortly after augmentation. These findings have been attributed to high injection volumes as well as high Young's moduli of PMMA bone cements compared to that of the osteoporotic cancellous bone. The aim of this study was to evaluate the use of castor oil as a plasticizer for PMMA bone cements. The Young's modulus, yield strength, maximum polymerization temperature, doughing time, setting time and the complex viscosity curves during curing, were determined. The cytotoxicity of the materials extracts was assessed on cells of an osteoblast-like cell line. The addition of up to 12 wt% castor oil decreased yield strength from 88 to 15 MPa, Young's modulus from 1500 to 446 MPa and maximum polymerization temperature from 41.3 to 25.6°C, without affecting the setting time. However, castor oil seemed to interfere with the polymerization reaction, giving a negative effect on cell viability in a worst-case scenario.

  2. 21 CFR 888.3027 - Polymethylmethacrylate (PMMA) bone cement.

    Science.gov (United States)

    2010-04-01

    ... 21 Food and Drugs 8 2010-04-01 2010-04-01 false Polymethylmethacrylate (PMMA) bone cement. 888... Polymethylmethacrylate (PMMA) bone cement. (a) Identification. Polymethylmethacrylate (PMMA) bone cement is a device...: Polymethylmethacrylate (PMMA) Bone Cement.” [67 FR 46855, July 17, 2002] ...

  3. Microindentation of Polymethyl Methacrylate (PMMA Based Bone Cement

    Directory of Open Access Journals (Sweden)

    F. Zivic

    2011-12-01

    Full Text Available Characterization of polymethyl methacrylate (PMMA based bone cement subjected to cyclical loading using microindentation technique is presented in this paper. Indentation technique represents flexible mechanical testing due to its simplicity, minimal specimen preparation and short time needed for tests. The mechanical response of bone cement samples was studied. Realised microindentation enabled determination of the indentation testing hardness HIT and indentation modulus EIT of the observed bone cement. Analysis of optical photographs of the imprints showed that this technique can be effectively used for characterization of bone cements.

  4. PMMA/Ca2+ bone cements. Hydrolytic properties and bioactivity

    Directory of Open Access Journals (Sweden)

    Mónica L. Hernández

    2012-01-01

    Full Text Available Bone cements of poly (methyl methacrylate (PMMA have been used for about 40 years to fix artificial prosthesis to bone structure. The aim of this study was to evaluate the absorption, solubility, degradation and bioactivity of novel formulations of PMMA/Ca2+ bone cements. These properties were evaluated using a fractional experimental design. Hydrolytic parameters were determined, from which we found that 7/8 of the formulations for absorption and 6/8 for solubility fulfill the ISO 4049:2000 requirements. The final degradation values ranged between 1 and 5%, except for one of the formulations. Besides, some formulations showed bioactivity after seven days of immersion in SBF solution.

  5. A modified PMMA cement (Sub-cement) for accelerated fatigue testing of cemented implant constructs using cadaveric bone.

    Science.gov (United States)

    Race, Amos; Miller, Mark A; Mann, Kenneth A

    2008-10-20

    Pre-clinical screening of cemented implant systems could be improved by modeling the longer-term response of the implant/cement/bone construct to cyclic loading. We formulated bone cement with degraded fatigue fracture properties (Sub-cement) such that long-term fatigue could be simulated in short-term cadaver tests. Sub-cement was made by adding a chain-transfer agent to standard polymethylmethacrylate (PMMA) cement. This reduced the molecular weight of the inter-bead matrix without changing reaction-rate or handling characteristics. Static mechanical properties were approximately equivalent to normal cement. Over a physiologically reasonable range of stress-intensity factor, fatigue crack propagation rates for Sub-cement were higher by a factor of 25+/-19. When tested in a simplified 2 1/2-D physical model of a stem-cement-bone system, crack growth from the stem was accelerated by a factor of 100. Sub-cement accelerated both crack initiation and growth rate. Sub-cement is now being evaluated in full stem/cement/femur models.

  6. Effects of Incorporating Carboxymethyl Chitosan into PMMA Bone Cement Containing Methotrexate.

    Directory of Open Access Journals (Sweden)

    Bo-Ming Liu

    Full Text Available Treatment of bone metastases usually includes surgical resection with local filling of methotrexate (MTX in polymethyl methacrylate (PMMA cement. We investigated whether incorporating carboxymethyl chitosan (CMCS in MTX-PMMA cement might overcome disadvantages associated with MTX. To determine the optimal CMCS+MTX concentration to suppress the viability of cancer cells, an integrated microfluidic chip culturing highly metastatic lung cancer cells (H460 was employed. The mechanical properties, microstructure, and MTX release of (CMCS+MTX-PMMA cement were evaluated respectively by universal mechanical testing machine, scanning electron microscopy (SEM, and incubation in simulated body fluid with subsequent HPLC-MS. Implants of MTX-PMMA and (CMCS+MTX-PMMA cement were evaluated in vivo in guinea pig femurs over time using spiral computed tomography with three-dimensional image reconstruction, and SEM at 6 months. Viability of H460 cells was significantly lowest after treatment with 57 μg/mL CMCS + 21 μg/mL MTX, which was thus used in subsequent experiments. Incorporation of 1.6% (w/w CMCS to MTX-PMMA significantly increased the bending modulus, bending strength, and compressive strength by 5, 2.8, and 5.2%, respectively, confirmed by improved microstructural homogeneity. Incorporation of CMCS delayed the time-to-plateau of MTX release by 2 days, but increased the fraction released at the plateau from 3.24% (MTX-PMMA to 5.34%. Relative to the controls, the (CMCS+MTX-PMMA implants integrated better with the host bone. SEM revealed pores in the cement of the (CMCS+MTX-PMMA implants that were not obvious in the controls. In conclusion, incorporation of CMCS in MTX-PMMA appears a feasible and effective modification for improving the anti-tumor properties of MTX-PMMA cement.

  7. A Novel Composite PMMA-based Bone Cement with Reduced Potential for Thermal Necrosis.

    Science.gov (United States)

    Lv, Yang; Li, Ailing; Zhou, Fang; Pan, Xiaoyu; Liang, Fuxin; Qu, Xiaozhong; Qiu, Dong; Yang, Zhenzhong

    2015-06-03

    Percutaneous vertebroplasty (VP) and balloon kyphoplasty (BKP) are now widely used to treat patients who suffer painful vertebral compression fractures. In each of these treatments, a bone cement paste is injected into the fractured vertebral body/bodies, and the cement of choice is a poly(methyl methacrylate) (PMMA) bone cement. One drawback of this cement is the very high exothermic temperature, which, it has been suggested, causes thermal necrosis of surrounding tissue. In the present work, we prepared novel composite PMMA bone cement where microcapsules containing a phase change material (paraffin) (PCMc) were mixed with the powder of the cement. A PCM absorbs generated heat and, as such, its presence in the cement may lead to reduction in thermal necrosis. We determined a number of properties of the composite cement. Compared to the values for a control cement (a commercially available PMMA cement used in VP and BKP), each composite cement was found to have significantly lower maximum exothermic temperature, increased setting time, significantly lower compressive strength, significantly lower compressive modulus, comparable biocompatibility, and significantly smaller thermal necrosis zone. Composite cement containing 20% PCMc may be suitable for use in VP and BKP and thus deserves further evaluation.

  8. Antibiotic-eluting hydrophilized PMMA bone cement with prolonged bactericidal effect for the treatment of osteomyelitis.

    Science.gov (United States)

    Oh, Eun Jo; Oh, Se Heang; Lee, In Soo; Kwon, Oh Soo; Lee, Jin Ho

    2016-05-01

    Osteomyelitis is still considered to be one of the major challenges for orthopedic surgeons despite advanced antiseptic surgical procedures and pharmaceutical therapeutics. In this study, hydrophilized poly(methyl methacrylate) (PMMA) bone cements containing Pluronic F68 (EG79PG28EG79) as a hydrophilic additive and vancomycin (F68-VAcements) were prepared to allow the sustained release of the antibiotic for adequate periods of time without any significant loss of mechanical properties. The compressive strengths of the bone cements with Pluronic F68 compositions less than 7 wt% were not significantly different compared with the control vancomycin-loaded bone cement (VAcement). TheF68 (7 wt%)-VAcement showed sustained release of the antibiotic for up to 11 weeks and almost 100% release from the bone cement. It also prohibited the growth ofS. aureus(zone of inhibition) over six weeks (the required period to treat osteomyelitis), and it did not show any notable cytotoxicity. From an animal study using a femoral osteomyelitis rat model, it was observed that theF68 (7 wt%)-VAcement was effective for the treatment of osteomyelitis, probably as a result of the prolonged release of antibiotic from the PMMA bone cement. On the basis of these findings, it can be suggested that the use of Pluronic F68 as a hydrophilic additive for antibiotic-eluting PMMA bone cement can be a promising strategy for the treatment of osteomyelitis. © The Author(s) 2016.

  9. Graphene oxide versus graphene for optimisation of PMMA bone cement for orthopaedic applications.

    Science.gov (United States)

    Paz, E; Forriol, F; Del Real, J C; Dunne, N

    2017-08-01

    Graphene (G) and graphene oxide (GO) nano-sized powders with loadings ranging from 0.1 to 1.0wt% were investigated as reinforced agents for polymethyl methacrylate (PMMA) bone cements. The mechanical properties (i.e. bend strength, bend modulus, compression strength, fracture toughness and fatigue performance) and the thermal properties (i.e. maximum temperature, setting time, curing heat and residual monomer) of the resultant nanocomposites were characterised. The mechanical performance of G-PMMA and GO-PMMA bone cements has been improved at low loadings (≤0.25wt%), especially the fracture toughness and fatigue performance. These improvements were attributed to the fact that the G and GO induced deviations in the crack fronts and hampered crack propagation. The high functionalisation of GO compared with G resulted in greater enhancements because it facilitated the creation of a stronger interfacial adhesion between the GO and PMMA. The use of loadings ≥0.25wt% showed a detriment in the mechanical performance as consequence of the formation of agglomerates as well as to an increase in the porosity. The increase in the residual monomer and the decrease in the curing heat, observed with the increase in the level of G and GO added, suggests that such materials retard and inhibit the curing reaction at high levels of loading by interfering in the radical reaction. Copyright © 2017 Elsevier B.V. All rights reserved.

  10. Influence of multiwall carbon nanotube functionality and loading on mechanical properties of PMMA/MWCNT bone cements.

    Science.gov (United States)

    Ormsby, Ross; McNally, Tony; Mitchell, Christina; Dunne, Nicholas

    2010-08-01

    Poly (methyl methacrylate) (PMMA) bone cement-multi walled carbon nanotube (MWCNT) nanocomposites with weight loadings ranging from 0.1 to 1.0 wt% were prepared. The MWCNTs investigated were unfunctionalised, carboxyl and amine functionalised MWCNTs. Mechanical properties of the resultant nanocomposite cements were characterised as per international standards for acrylic resin cements. These mechanical properties were influenced by the type and wt% loading of MWCNT used. The morphology and degree of dispersion of the MWCNTs in the PMMA matrix at different length scales were examined using field emission scanning electron microscopy. Improvements in mechanical properties were attributed to the MWCNTs arresting/retarding crack propagation through the cement by providing a bridging effect and hindering crack propagation. MWCNTs agglomerations were evident within the cement microstructure, the degree of these agglomerations was dependent on the weight fraction and functionality of MWCNTs incorporated into the cement.

  11. Preliminary focus on the mechanical and antibacterial activity of a PMMA-based bone cement loaded with gold nanoparticles

    Directory of Open Access Journals (Sweden)

    T. Russo

    2017-09-01

    As reported in the literature, the stress distribution may be altered in bones after the implantation of a total joint prosthesis. Some scientific works have also correlated uncemented TKA to a progressive decrease of bone density below the tibial component. Antibiotic-loaded bone cements are commonly employed in conjunction with systemic antibiotics to treat infections. Furthermore, nanoparticles with antimicrobial activity have been widely analysed. Accordingly, the current research was focused on a preliminary analysis of the mechanical and antibacterial activity of a PMMA-based bone cement loaded with gold nanoparticles. The obtained results demonstrated that nanocomposite cements with a specific concentration of gold nanoparticles improved the punching performance and antibacterial activity. However, critical aspects were found in the optimization of the nanocomposite bone cement.

  12. Experimental ex-vivo validation of PMMA-based bone cements loaded with magnetic nanoparticles enabling hyperthermia of metastatic bone tumors

    Directory of Open Access Journals (Sweden)

    Mariem Harabech

    2017-05-01

    Full Text Available Percutaneous vertebroplasty comprises the injection of Polymethylmethacrylate (PMMA bone cement into vertebrae and can be used for the treatment of compression fractures of vertebrae. Metastatic bone tumors can cause such compression fractures but are not treated when injecting PMMA-based bone cement. Hyperthermia of tumors can on the other hand be attained by placing magnetic nanoparticles (MNPs in an alternating magnetic field (AMF. Loading the PMMA-based bone cement with MNPs could both serve vertebra stabilization and metastatic bone tumor hyperthermia when subjecting this PMMA-MNP to an AMF. A dedicated pancake coil is designed with a self-inductance of 10 μH in series with a capacitance of 0.1 μF that acts as resonant inductor-capacitor circuit to generate the AMF. The thermal rise is appraised in beef vertebra placed at 10 cm from the AMF generating circuit using optical temperatures sensors, i.e. in the center of the PMMA-MNP bone cement, which is located in the vicinity of metastatic bone tumors in clinical applications; and in the spine, which needs to be safeguarded to high temperature exposures. Results show a temperature rise of about 7 °C in PMMA-MNP whereas the temperature rise in the spine remains limited to 1 °C. Moreover, multicycles heating of PMMA-MNP is experimentally verified, validating the technical feasibility of having PMMA-MNP as basic component for percutaneous vertebroplasty combined with hyperthermia treatment of metastatic bone tumors.

  13. A small punch test technique for characterizing the elastic modulus and fracture behavior of PMMA bone cement used in total joint replacement.

    Science.gov (United States)

    Giddings, V L; Kurtz, S M; Jewett, C W; Foulds, J R; Edidin, A A

    2001-07-01

    Polymethylmethacrylate (PMMA) bone cement is used in total joint replacements to anchor implants to the underlying bone. Establishing and maintaining the integrity of bone cement is thus of critical importance to the long-term outcome of joint replacement surgery. The goal of the present study was to evaluate the suitability of a novel testing technique, the small punch or miniaturized disk bend test, to characterize the elastic modulus and fracture behavior of PMMA. We investigated the hypothesis that the crack initiation behavior of PMMA during the small punch test was sensitive to the test temperature. Miniature disk-shaped specimens, 0.5 mm thick and 6.4 mm in diameter, were prepared from PMMA and Simplex-P bone cement according to manufacturers' instructions. Testing was conducted at ambient and body temperatures, and the effect of test temperature on the elastic modulus and fracture behavior was statistically evaluated using analysis of variance. For both PMMA materials, the test temperature had a significant effect on elastic modulus and crack initiation behavior. At body temperature, the specimens exhibited "ductile" crack initiation, whereas at room temperature "brittle" crack initiation was observed. The small punch test was found to be a sensitive and repeatable test method for evaluating the mechanical behavior of PMMA. In light of the results of this study, future small punch testing should be conducted at body temperature.

  14. Static coefficient of friction between stainless steel and PMMA used in cemented hip and knee implants.

    Science.gov (United States)

    Nuño, N; Groppetti, R; Senin, N

    2006-11-01

    Design of cemented hip and knee implants, oriented to improve the longevity of artificial joints, is largely based on numerical models. The static coefficient of friction between the implant and the bone cement is necessary to characterize the interface conditions in these models and must be accurately provided. The measurement of this coefficient using a repeatable and reproducible methodology for materials used in total hip arthroplasty is missing from the literature. A micro-topographic surface analysis characterized the surfaces of the specimens used in the experiments. The coefficient of friction between stainless steel and bone cement in dry and wet conditions using bovine serum was determined using a prototype computerized sliding friction tester. The effects of surface roughness (polished versus matt) and of contact pressure on the coefficient of friction have also been investigated. The serum influences little the coefficient of friction for the matt steel surface, where the mechanical interactions due to higher roughness are still the most relevant factor. However, for polished steel surfaces, the restraining effect of proteins plays a very relevant role in increasing the coefficient of friction. When the coefficient of friction is used in finite element analysis, it is used for the debonded stem-cement situation. It can thus be assumed that serum will propagate between the stem and the cement mantle. The authors believe that the use of a static coefficient of friction of 0.3-0.4, measured in the present study, is appropriate in finite element models.

  15. Gentamicin release from commercially-available gentamicin-loaded PMMA bone cements in a prosthesis-related interfacial gap model and their antibacterial efficacy

    Directory of Open Access Journals (Sweden)

    van der Mei Henny C

    2010-11-01

    Full Text Available Abstract Background Around about 1970, a gentamicin-loaded poly (methylmethacrylate (PMMA bone cement brand (Refobacin Palacos R was introduced to control infection in joint arthroplasties. In 2005, this brand was replaced by two gentamicin-loaded follow-up brands, Refobacin Bone Cement R and Palacos R + G. In addition, another gentamicin-loaded cement brand, SmartSet GHV, was introduced in Europe in 2003. In the present study, we investigated differences in gentamicin release and the antibacterial efficacy of the eluent between these four cement brands. Methods 200 μm-wide gaps were made in samples of each cement and filled with buffer in order to measure the gentamicin release. Release kinetics were related to bone cement powder particle characteristics and wettabilities of the cement surfaces. Gaps were also inoculated with bacteria isolated from infected prostheses for 24 h and their survival determined. Gentamicin release and bacterial survival were statistically analysed using the Student's t-test. Results All three Palacos variants showed equal burst releases but each of the successor Palacos cements showed significantly higher sustained releases. SmartSet GHV showed a significantly higher burst release, while its sustained release was comparable with original Palacos. A gentamicin-sensitive bacterium did not survive in the high gentamicin concentrations in the interfacial gaps, while a gentamicin-resistant strain did, regardless of the type of cement used. Survival was independent of the level of burst release by the bone cement. Conclusions Although marketed as the original gentamicin-loaded Palacos cement, orthopaedic surgeons should be aware that the successor cements do not appear to have the same release characteristics as the original one. Overall, high gentamicin concentrations were reached inside our prosthesis-related interfacial gap model. These concentrations may be expected to effectively decontaminate the prosthesis

  16. Theoretical prediction and experimental determination of the effect of mold characteristics on temperature and monomer conversion fraction profiles during polymerization of a PMMA-based bone cement.

    Science.gov (United States)

    Vallo, Claudia I

    2002-01-01

    The present work is concerned with applications of a kinetic model for free-radical polymerization of a polymethylmethacrylate-based bone cement. Autocatalytic behavior at the first part of the reaction as well as a diffusion control phenomenon near vitrification are described by the model. Comparison of theoretical computations with experimental measurements for the temperature evolution during batch casting demonstrated the capacity of the proposed model to represent the kinetic behavior of the polymerization reaction. Temperature evolution and monomer conversion were simulated for the cure of the cement in molds made of different materials. The maximum monomer conversion fraction was markedly influenced by the physical properties of the mold material. The unreacted monomer acts as a plasticizer that influences the mechanical behavior of the cement. Hence, the same cement formulation cured in molds of different materials may result in different mechanical response because of the differences in the amounts of residual monomer. Standardization of the mold type to prepare specimens for the mechanical characterization of bone cements is recommended. Theoretical prediction of temperature evolution during hip replacement indicated that for cement thickness lower than 6 mm the peak temperature at the bone-cement interface was below the limit stated for thermal injury (50 degrees C for more than 1 min). The use of thin cement layers is recommended to diminish the risk of thermal injury; however, it is accompanied by an increase in the amount of unreacted monomer present in the cured material. Copyright 2002 Wiley Periodicals, Inc. J Biomed Mater Res (Appl Biomater) 63: 627-642, 2002

  17. A Research on Low Modulus Distributed Fiber Optical Sensor for Pavement Material Strain Monitoring.

    Science.gov (United States)

    Meng, Lingjian; Wang, Linbing; Hou, Yue; Yan, Guannan

    2017-10-19

    The accumulated irreversible deformation in pavement under repeated vehicle loadings will cause fatigue failure of asphalt concrete. It is necessary to monitor the mechanical response of pavement under load by using sensors. Previous studies have limitations in modulus accommodation between the sensor and asphalt pavement, and it is difficult to achieve the distributed monitoring goal. To solve these problems, a new type of low modulus distributed optical fiber sensor (DOFS) for asphalt pavement strain monitoring is fabricated. Laboratory experiments have proved the applicability and accuracy of the newly-designed sensor. This paper presents the results of the development.

  18. Phase Holograms In PMMA

    Science.gov (United States)

    Maker, Paul D.; Muller, Richard E.

    1994-01-01

    Complex, computer-generated phase holograms written in thin films of poly(methyl methacrylate) (PMMA) by process of electron-beam exposure followed by chemical development. Spatial variations of phase delay in holograms quasi-continuous, as distinquished from stepwise as in binary phase holograms made by integrated-circuit fabrication. Holograms more precise than binary holograms. Greater continuity and precision results in decreased scattering loss and increased imaging efficiency.

  19. The mechanical study of acrylic bone cement reinforced with carbon nanotube

    International Nuclear Information System (INIS)

    Nien, Yu-Hsun; Huang, Chiao-li

    2010-01-01

    Bone cement is used as filler between prosthesis and bone for fixation and force distribution. The major composition of bone cement is polymethylmethacrylate (PMMA). Some disadvantages of PMMA bone cement are found such as significant poor mechanical properties which may cause failure of the cement. In this paper, we exploited carbon nanotube to enhance the mechanical properties of bone cement. The mechanical properties of the bone cement were characterized using tensile and compressive analysis as well as dynamic mechanical analysis (DMA). The result shows that carbon nanotube is able to enhance the mechanical properties of the modified bone cement.

  20. The mechanical study of acrylic bone cement reinforced with carbon nanotube

    Energy Technology Data Exchange (ETDEWEB)

    Nien, Yu-Hsun, E-mail: nienyh@yuntech.edu.tw [Department of Chemical and Materials Engineering, National Yunlin University of Science and Technology, Douliou, Yunlin 64002, Taiwan (China); Huang, Chiao-li [Department of Chemical and Materials Engineering, National Yunlin University of Science and Technology, Douliou, Yunlin 64002, Taiwan (China)

    2010-05-25

    Bone cement is used as filler between prosthesis and bone for fixation and force distribution. The major composition of bone cement is polymethylmethacrylate (PMMA). Some disadvantages of PMMA bone cement are found such as significant poor mechanical properties which may cause failure of the cement. In this paper, we exploited carbon nanotube to enhance the mechanical properties of bone cement. The mechanical properties of the bone cement were characterized using tensile and compressive analysis as well as dynamic mechanical analysis (DMA). The result shows that carbon nanotube is able to enhance the mechanical properties of the modified bone cement.

  1. Mechanical and microstructural characterization of new nickel-free low modulus β-type titanium wires during thermomechanical treatments

    Energy Technology Data Exchange (ETDEWEB)

    Guillem-Martí, J. [Biomaterials, Biomechanics and Tissue Engineering Group, Department of Materials Science and Metallurgy, Technical University of Catalonia (UPC), ETSEIB, Av. Diagonal 647, 08028 Barcelona (Spain); Biomedical Research Networking Centre in Bioengineering, Biomaterials and Nanomedicine (CIBER-BBN), Campus Río Ebro, Edificio I+D Bloque 5, 1a planta, C/ Poeta Mariano Esquillor s/n, 50018 Zaragoza (Spain); Centre for Research in NanoEngineering (CRNE) – UPC, C/Pascual i Vila 15, 08028 Barcelona (Spain); Herranz-Díez, C. [Biomaterials, Biomechanics and Tissue Engineering Group, Department of Materials Science and Metallurgy, Technical University of Catalonia (UPC), ETSEIB, Av. Diagonal 647, 08028 Barcelona (Spain); Biomedical Research Networking Centre in Bioengineering, Biomaterials and Nanomedicine (CIBER-BBN), Campus Río Ebro, Edificio I+D Bloque 5, 1a planta, C/ Poeta Mariano Esquillor s/n, 50018 Zaragoza (Spain); Shaffer, J.E. [Fort Wayne Metals Research Products Corporation, 9609 Ardmore Avenue, 46809 Fort Wayne (United States); Gil, F.J. [Biomaterials, Biomechanics and Tissue Engineering Group, Department of Materials Science and Metallurgy, Technical University of Catalonia (UPC), ETSEIB, Av. Diagonal 647, 08028 Barcelona (Spain); Biomedical Research Networking Centre in Bioengineering, Biomaterials and Nanomedicine (CIBER-BBN), Campus Río Ebro, Edificio I+D Bloque 5, 1a planta, C/ Poeta Mariano Esquillor s/n, 50018 Zaragoza (Spain); Centre for Research in NanoEngineering (CRNE) – UPC, C/Pascual i Vila 15, 08028 Barcelona (Spain); and others

    2015-06-11

    NiTi alloy is the only practical shape memory alloy (SMA) in biomedical use because of its excellent mechanical stability and functionality. However, it is estimated that between 4.5% and 28.5% of the population are hypersensitive to nickel metal, with a higher prevalence in females. Therefore, developing nickel-free low modulus β-type titanium alloys showing shape memory or super elastic behavior would have a great interest in the biomaterials field. Homogeneous 127 μm diameter Ti25Hf21Nb wires were produced and compared to straight annealed Ti–50.8 at% Ni (Nitinol) and 90% cold-drawn 316L wires. Microstructural changes taking place during the heat treatment of cold-worked Ti25Hf21Nb wires were investigated. Large plastic deformation during wire drawing and subsequent annealing led to nano-crystallization and amorphization which may contribute to the observed superelasticity. Mechanical properties were characterized using cyclic uniaxial tension and rotary beam fatigue test modes. A modulus of elasticity of less than 60 GPa and axial recoverable strain of greater than 3% were observed with stress hysteresis resembling a reversible stress-induced martensitic transformation at higher temperatures. The new Ti25Hf21Nb alloy is an important candidate for developing Ni-free SMAs in the future.

  2. Mechanical and microstructural characterization of new nickel-free low modulus β-type titanium wires during thermomechanical treatments

    International Nuclear Information System (INIS)

    Guillem-Martí, J.; Herranz-Díez, C.; Shaffer, J.E.; Gil, F.J.

    2015-01-01

    NiTi alloy is the only practical shape memory alloy (SMA) in biomedical use because of its excellent mechanical stability and functionality. However, it is estimated that between 4.5% and 28.5% of the population are hypersensitive to nickel metal, with a higher prevalence in females. Therefore, developing nickel-free low modulus β-type titanium alloys showing shape memory or super elastic behavior would have a great interest in the biomaterials field. Homogeneous 127 μm diameter Ti25Hf21Nb wires were produced and compared to straight annealed Ti–50.8 at% Ni (Nitinol) and 90% cold-drawn 316L wires. Microstructural changes taking place during the heat treatment of cold-worked Ti25Hf21Nb wires were investigated. Large plastic deformation during wire drawing and subsequent annealing led to nano-crystallization and amorphization which may contribute to the observed superelasticity. Mechanical properties were characterized using cyclic uniaxial tension and rotary beam fatigue test modes. A modulus of elasticity of less than 60 GPa and axial recoverable strain of greater than 3% were observed with stress hysteresis resembling a reversible stress-induced martensitic transformation at higher temperatures. The new Ti25Hf21Nb alloy is an important candidate for developing Ni-free SMAs in the future

  3. Nanoparticulate fillers improve the mechanical strength of bone cement.

    Science.gov (United States)

    Gomoll, Andreas H; Fitz, Wolfgang; Scott, Richard D; Thornhill, Thomas S; Bellare, Anuj

    2008-06-01

    Polymethylmethacrylate (PMMA-) based bone cement contains micrometer-size barium sulfate or zirconium oxide particles to radiopacify the cement for radiographic monitoring during follow-up. Considerable effort has been expended to improve the mechanical qualities of cements, largely through substitution of PMMA with new chemical structures. The introduction of these materials into clinical practice has been complicated by concerns over the unknown long-term risk profile of these new structures in vivo. We investigated a new composite with the well characterized chemical composition of current cements, but with nanoparticles instead of the conventional, micrometer-size barium sulfate radiopacifier. In this study, we replaced the barium sulfate microparticles that are usually present in commercial PMMA cements with barium sulfate nanoparticles. The resultant "microcomposite" and "nanocomposite" cements were then characterized through morphological investigations such as ultra-small angle X-ray scattering (USAXS) and scanning electron microscopy (SEM). Mechanical characterization included compression, tensile, compact tension, and fatigue testing. SEM and USAXS showed excellent dispersion of nanoparticles. Substitution of nanoparticles for microparticles resulted in a 41% increase in tensile strain-to-failure (p = 0.002) and a 70% increase in tensile work-of-fracture (p = 0.005). The nanocomposite cement also showed a two-fold increase in fatigue life compared to the conventional, microcomposite cement. In summary, nanoparticulate substitution of radiopacifiers substantially improved the in vitro mechanical properties of PMMA bone cement without changing the known chemical composition.

  4. Signal-inducing bone cements for MRI-guided spinal cementoplasty: evaluation of contrast-agent-based polymethylmethacrylate cements

    International Nuclear Information System (INIS)

    Bail, Hermann Josef; Tsitsilonis, Serafim; Wichlas, Florian; Sattig, Christoph; Papanikolaou, Ioannis; Teichgraeber, Ulf Karl Mart

    2012-01-01

    The purpose of this work is to evaluate two signal-inducing bone cements for MRI-guided spinal cementoplasty. The bone cements were made of polymethylmethacrylate (PMMA, 5 ml monomeric, 12 g polymeric) and gadoterate meglumine as a contrast agent (CA, 0-40 μl) with either saline solution (NaCl, 2-4 ml) or hydroxyapatite bone substitute (HA, 2-4 ml). The cement's signal was assessed in an open 1-Tesla MR scanner, with T1W TSE and fast interventional T1W TSE pulse sequences, and the ideal amount of each component was determined. The compressive and bending strength for different amounts of NaCl and HA were evaluated. The cement's MRI signal depended on the concentration of CA, the amount of NaCl or HA, and the pulse sequence. The signal peaks were recorded between 1 and 10 μl CA per ml NaCl or HA, and were higher in fast T1W TSE than in T1W TSE images. The NaCl-PMMA-CA cements had a greater MRI signal intensity and compressive strength; the HA-PMMA-CA cements had a superior bending strength. Concerning the MR signal and biomechanical properties, these cements would permit MRI-guided cementoplasty. Due to its higher signal and greater compressive strength, the NaCl-PMMA-CA compound appears to be superior to the HA-PMMA-CA compound. (orig.)

  5. Chemical and physical properties of bone cement for vertebroplasty

    Directory of Open Access Journals (Sweden)

    Po-Liang Lai

    2013-08-01

    Full Text Available Vertebral compression fracture is the most common complication of osteoporosis. It may result in persistent severe pain and limited mobility, and significantly impacts the quality of life. Vertebroplasty involves a percutaneous injection of bone cement into the collapsed vertebrae by fluorescent guide. The most commonly used bone cement in percutaneous vertebroplasty is based on the polymerization of methylmethacrylate monomers to polymethylmethacrylate (PMMA polymers. However, information on the properties of bone cement is mostly published in the biomaterial sciences literature, a source with which the clinical community is generally unfamiliar. This review focuses on the chemistry of bone cement polymerization and the physical properties of PMMA. The effects of altering the portions and contents of monomer liquid and polymer powders on the setting time, polymerization temperature, and compressive strength of the cement are also discussed. This information will allow spine surgeons to manipulate bone cement characteristics for specific clinical applications and improve safety.

  6. PMMA Wettability Caused by Ultraviolet Radiation

    OpenAIRE

    Dehtjars, J; Lancere, L; Poļaka, N; Soudnikovich, A; Tjuļkins, F; Valters, V

    2010-01-01

    The article is targeted to explore ultraviolet radiation (UV) influence on PMMAf or eye prostheses. UV beingt he Sun lightc omponenta nd could effect PMMA surface that in turn contributesi nteractionw ith tear. PMMA wettabilityw as poweredb y UV.

  7. Ferroelectric Phase Diagram of PVDF:PMMA

    OpenAIRE

    Li, Mengyuan; Stingelin, Natalie; Michels, Jasper J.; Spijkman, Mark-Jan; Asadi, Kamal; Feldman, Kirill; Blom, Paul W. M.; de Leeuw, Dago M.

    2012-01-01

    We have investigated the ferroelectric phase diagram of poly(vinylidene fluoride) (PVDF) and poly(methyl methacrylate) (PMMA). The binary nonequilibrium temperature composition diagram was determined and melting of alpha- and beta-phase PVDF was identified. Ferroelectric beta-PVDF:PMMA blend films were made by melting, ice quenching, and subsequent annealing above the glass transition temperature of PMMA, close to the melting temperature of PVDF. Addition of PMMA suppresses the crystallizatio...

  8. PMMA embolization to the left dorsal foot artery during percutaneous vertebroplasty for spinal metastases.

    Science.gov (United States)

    Iliopoulos, Panagiotis; Panagiotis, Iliopoulos; Korovessis, Panagiotis; Panagiotis, Korovessis; Vitsas, Vasilios; Vasilios, Vitsas

    2014-05-01

    Distal arterial embolization to the foot with PMMA during vertebral augmentation has not been previously reported. We report a rare case of distal PMMA embolization to the dorsal foot artery during ipsilateral percutaneous lumbar vertebral augmentation in a patient with spinal osteolytic metastases. A 68-year-old woman was admitted because of severe disabling low back pain. Plain roentgenograms, MRI and CT-scan revealed osteolysis in the L4 and L5 vertebral bodies with prevertebral soft tissue involvement. Percutaneous vertebroplasty with PMMA was performed in L2 to L5 vertebrae under general anesthesia. Intraoperatively, leakage into the segmental vessels L3 and L5 was observed. Four hours after the procedure the clinical diagnosis of acute ischemia and drop foot on the left was made. CT-angiography justified linear cement leakage in the course of the left third lumbar vein and fifth lumbar artery, and to the ipsilateral common iliac artery. The patient was treated with low molecular heparin and the ischemia resolved without further sequelae 1 week postoperatively. PMMA leakage is a complication associated with vertebroplasty and kyphoplasty. Although the outcome of the PMMA embolization to the vessels resolved without sequelae, in our case spine surgeons and interventional radiologists should be aware on this rare complication in patients with osteolytic vertebral metastases even when contemporary cement containment techniques are used.

  9. Irradiation effect on PP/PMMA and PP/PP-g-PMMA matrices

    International Nuclear Information System (INIS)

    Marsongko; Soebianto, Yanti S.

    1998-01-01

    The effects of PMMA and PP-g-PMMA on the oxidation of polypropylene (PP) have been studied. The mixing was done in Laboplastomill at the temperature of 200 o C, and screw speed of 20 rpm, for 5 minutes. The PMMA concentrations were 1, 2, 5, and 10% by weight, and PP-g-PMMA (12% grafting) 5, 10, and 20% by weight. Mechanical properties (tensile strength (Tb) and elongation at break (Eb)( of the mixture decreased with the increase of PMMA content over 5%. The addition of PMMA over 3% produced non-transparent film. Electron beam irradiation at the dose of 5, 10, 30, and 50 kGy was carried out to accelerate the matrix oxidation is accelerated. The optimum properties of PP/PMMA blends can be achieved by addition of maximum 2% PMMA either direct as PMMA or as compatibilizer (PP-g-PMMA). (authors)

  10. Experimental study with domestic bone cement in the percutaneous vertebroplasty

    International Nuclear Information System (INIS)

    Ni Caifang; Liu Xisheng; Chen Long; Yang Huilin; Tang Tiansi; Ding Yi

    2004-01-01

    Objective: To study the feasibility of injecting domestic bone cement in the process of the percutaneous vertebroplasty. Methods: (1) Various types cement were disposed with domestic PMMA. The concretionary phases of cement were observed according to the stages and holding time. Then the most ideal ratio of the mixed cement was selected and ten cement columns were made with this ratio, which was taken as the trial group. The other ten referring to was taken as the contrast one. The biological mechanics was measured with a load and the data of the results were compared. (2) Twenty thoracic and lumbar adjacent bodies were removed intact from five human corpses. These bodies were divided into two groups, in one group PMMA were injected, the other was severed as the contrast one. Then in these twenty vertebral bodies the biological mechanics was measured and the treatment effect was evaluated. (3) In 12 healthy dogs PVP in lumber was tried so as to observe the operational difficulty during the process of injected this bone cement and CT was used to evaluate the result of PMMA, diffusion and the complications caused by it. Results: The most ideal ratio was 4:2.6:1 (g, ml, ml) between powder, monome and contrast. After injecting this kind of cement, the loading strength of these vertebral bodies was increased remarkably (P<0.01). Conclusion: Injecting domestic bone cement provides the theoretical foundations for the clinical application of PVP. (author)

  11. Cermet cements.

    Science.gov (United States)

    McLean, J W

    1990-01-01

    Cermet ionomer cements are sintered metal/glass powders, which can be made to react with poly(acids). These new cements are significantly more resistant to abrasion than regular glass ionomer cements and are widely accepted as core build-up materials and lining cements. They can strengthen teeth and provide the clinician with an opportunity to treat early dental caries.

  12. Nanofunctionalized zirconia and barium sulfate particles as bone cement additives

    Directory of Open Access Journals (Sweden)

    Riaz Gillani

    2009-12-01

    Full Text Available Riaz Gillani1, Batur Ercan1, Alex Qiao3, Thomas J Webster1,21Division of Engineering, 2Department of Orthopaedics, Brown University, Providence, RI, USA; 3G3 Technology Innovations, LLC, Pittsford, NY, USAAbstract: Zirconia (ZrO2 and barium sulfate (BaSO4 particles were introduced into a methyl methacrylate monomer (MMA solution with polymethyl methacrylate (PMMA beads during polymerization to develop the following novel bone cements: bone cements with unfunctionalized ZrO2 micron particles, bone cements with unfunctionalized ZrO2 nanoparticles, bone cements with ZrO2 nanoparticles functionalized with 3-(trimethoxysilylpropyl methacrylate (TMS, bone cements with unfunctionalized BaSO4 micron particles, bone cements with unfunctionalized BaSO4 nanoparticles, and bone cements with BaSO4 nanoparticles functionalized with TMS. Results demonstrated that in vitro osteoblast (bone-forming cell densities were greater on bone cements containing BaSO4 ceramic particles after four hours compared to control unmodified bone cements. Osteoblast densities were also greater on bone cements containing all of the ceramic particles after 24 hours compared to unmodified bone cements, particularly those bone cements containing nanofunctionalized ceramic particles. Bone cements containing ceramic particles demonstrated significantly altered mechanical properties; specifically, under tensile loading, plain bone cements and bone cements containing unfunctionalized ceramic particles exhibited brittle failure modes whereas bone cements containing nanofunctionalized ceramic particles exhibited plastic failure modes. Finally, all bone cements containing ceramic particles possessed greater radio-opacity than unmodified bone cements. In summary, the results of this study demonstrated a positive impact on the properties of traditional bone cements for orthopedic applications with the addition of unfunctionalized and TMS functionalized ceramic nanoparticles

  13. Influence of Nano-HA Coated Bone Collagen to Acrylic (Polymethylmethacrylate Bone Cement on Mechanical Properties and Bioactivity.

    Directory of Open Access Journals (Sweden)

    Tao Li

    Full Text Available This research investigated the mechanical properties and bioactivity of polymethylmethacrylate (PMMA bone cement after addition of the nano-hydroxyapatite(HA coated bone collagen (mineralized collagen, MC.The MC in different proportions were added to the PMMA bone cement to detect the compressive strength, compression modulus, coagulation properties and biosafety. The MC-PMMA was embedded into rabbits and co-cultured with MG 63 cells to exam bone tissue compatibility and gene expression of osteogenesis.15.0%(wt impregnated MC-PMMA significantly lowered compressive modulus while little affected compressive strength and solidification. MC-PMMA bone cement was biologically safe and indicated excellent bone tissue compatibility. The bone-cement interface crosslinking was significantly higher in MC-PMMA than control after 6 months implantation in the femur of rabbits. The genes of osteogenesis exhibited significantly higher expression level in MC-PMMA.MC-PMMA presented perfect mechanical properties, good biosafety and excellent biocompatibility with bone tissues, which has profoundly clinical values.

  14. Effect of process variables on the preparation of artificial bone cements

    Energy Technology Data Exchange (ETDEWEB)

    Santos Junior, J.G.F.; Melo, P.A.; Pinto, J.C., E-mail: pinto@peq.coppe.ufrj.br, E-mail: jjunior@peq.coppe.ufrj.br, E-mail: melo@peq.coppe.ufrj.br [Coordenacao dos Programas de Pos-Graduacao de Engenharia (COPPE/UFRJ), RJ (Brazil). Programa de Engenharia Quimica; Pita, V.J.R.R., E-mail: vjpita@ima.ufrj.br [Universidade Federal do Rio de Janeiro (UFRJ), RJ (Brazil). Instituto de Macromoleculas; Nele, M., E-mail: nele@eq.ufrj.br [Universidade Federal do Rio de Janeiro (UFRJ), RJ (Brazil). Escola de Quimica

    2013-10-15

    The present work concerns the preparation of bone cements based on poly(methyl methacrylate) (PMMA), used mainly for prosthesis fixation and cavity filling for correction of human bone failures. A typical bone cement recipe contains methyl methacrylate, which polymerizes in situ during cement application. An inherent problem of this reaction is the large amount of heat released during the cement preparation, which may lead to irreparable damage of living tissues. Optimization of PMMA-based bone cement recipes is thus an important step towards safe and reliable clinical usage of these materials. Important process variables related to the reaction temperature profile and the mixing of the recipe constituents were studied in order to allow for the adequate production of bone cements. It is shown that the average molar mass and size of the PMMA particles used in the production of the bone cement, as well as incorporation of radiopaque contrast, co-monomers and fillers into the bone recipe play fundamental roles in the course of the polymerization reaction. Furthermore, the injection vessel geometry may interfere dramatically with the temperature profile and the time for its occurrence. Finally, it has been observed that the morphology of the PMMA particles strongly affects the mixing of the bone cement components. (author)

  15. Effect of process variables on the preparation of artificial bone cements

    Directory of Open Access Journals (Sweden)

    J. G. F. Santos Jr.

    2013-12-01

    Full Text Available The present work concerns the preparation of bone cements based on poly(methyl methacrylate (PMMA, used mainly for prosthesis fixation and cavity filling for correction of human bone failures. A typical bone cement recipe contains methyl methacrylate, which polymerizes in situ during cement application. An inherent problem of this reaction is the large amount of heat released during the cement preparation, which may lead to irreparable damage of living tissues. Optimization of PMMA-based bone cement recipes is thus an important step towards safe and reliable clinical usage of these materials. Important process variables related to the reaction temperature profile and the mixing of the recipe constituents were studied in order to allow for the adequate production of bone cements. It is shown that the average molar mass and size of the PMMA particles used in the production of the bone cement, as well as incorporation of radiopaque contrast, co-monomers and fillers into the bone recipe play fundamental roles in the course of the polymerization reaction. Furthermore, the injection vessel geometry may interfere dramatically with the temperature profile and the time for its occurrence. Finally, it has been observed that the morphology of the PMMA particles strongly affects the mixing of the bone cement components.

  16. Improved biological performance of low modulus Ti-24Nb-4Zr-7.9Sn implants due to surface modification by anodic oxidation

    Energy Technology Data Exchange (ETDEWEB)

    Gao, Y. [School of Stomatology, Fourth Military Medical University, Xi' an 710032 (China); Gao, B., E-mail: gaobo_fmmu@163.com [School of Stomatology, Fourth Military Medical University, Xi' an 710032 (China); Wang, R. [Fengtai Health Center of Navy Outpatient Department, Beijing 100071 (China); Wu, J.; Zhang, L.J. [School of Stomatology, Fourth Military Medical University, Xi' an 710032 (China); Hao, Y.L.; Tao, X.J. [Institute of Metal Research Chinese Academy of Sciences, Shenyang 110016 (China)

    2009-02-15

    Dental implants are usually made from commercially pure titanium or titanium alloys. The purpose of this study was to evaluate the influence of surface treatment to low modulus Ti-24Nb-4Zr-7.9Sn (TNZS) on cell and bone responses. The TNZS alloy samples were modified using anodic oxidation (AD). Surface oxide properties were characterized by using various surface analytic techniques, involving scanning electron microscopy (SEM) equipped with energy dispersive spectrometer (EDS), X-ray diffractometry (XRD) and surface profilometer. During the AD treatment, porous titanium oxide layer was formed and Ca ions were incorporated into the oxide layer. The viability and morphology of osteoblasts on Ca-incorporated TNZS were studied. The bone responses of Ca-incorporated TNZS were evaluated by pull-out tests and morphological analysis after implantation in rabbit tibiae. The non-treated Ti and TNZS samples were used as the control. Significant increases in cell viability and pull-out forces (p < 0.05) were observed for Ca-incorporated TNZS implants compared with those for the control groups. Porous structures supplied positive guidance cues for osteoblasts to attach. The enhanced cell and bone responses to Ca-incorporated TNZS implants could be explained by the surface chemistry and microtopography.

  17. Dielectric properties of PMMA/Soot nanocomposites.

    Science.gov (United States)

    Clayton, Lanetra M; Cinke, Martin; Meyyappan, M; Harmon, Julie P

    2007-07-01

    Dielectric analysis (DEA) of relaxation behavior in poly(methyl methacrylate) (PMMA) soot nanocomposites is described herein. The soot, an inexpensive material, consists of carbon nanotubes, amorphous and graphitic carbon and metal particles. Results are compared to earlier studies on PMMA/multi-walled nanotube (MWNT) composites and PMMA/single-walled nanotube (SWNT) composites. The beta relaxation process appeared to be unaffected by the presence of the soot, as was noted earlier in nanotube composites. The gamma relaxation region in PMMA, normally dielectrically inactive, was "awakened" in the PMMA/soot composite. This occurrence is consistent with previously published data on nanotube composites. The dielectric permittivity, s', increased with soot content. The sample with 1% soot exhibited a permittivity (at 100 Hz and 25 degrees C) of 7.3 as compared to 5.1 for neat PMMA. Soot increased the dielectric strength, deltaE, of the composites. The 1% soot sample exhibited a dielectric strength of 6.38, while the neat PMMA had a value of 2.95 at 40 degrees C. The symmetric broadening term (alpha) was slightly higher for the 1% composite at temperatures near the secondary relaxation and near the primary relaxation, but all samples deviated from symmetrical semi-circular behavior (alpha = 1). The impact of the soot filler is seen more clearly in dielectric properties than in mechanical properties studies conducted earlier.

  18. Osteo-odonto-keratoprosthesis (OOKP) and the testing of three different adhesives for bonding bovine teeth with optical poly-(methyl methacrylate) (PMMA) cylinder.

    Science.gov (United States)

    Weisshuhn, K; Berg, I; Tinner, D; Kunz, C; Bornstein, M M; Steineck, M; Hille, K; Goldblum, D

    2014-07-01

    Preparation of the lamina during osteo-odonto-keratoprosthesis (OOKP) design is complex, and its longevity and watertightness important. To date, only acrylic bone cements have been used for bonding the optical cylinder to the tooth dentine. Our aim was to evaluate different dental adhesives for OOKP preparation. Specimens of bovine teeth were produced by preparing 1.5-mm thick dentine slices with holes having a diameter of 3.5 mm. Each group (n=10 per group) was luted with either classic poly-(methyl methacrylate) (PMMA) bone cement, universal resin cement or glass ionomer cement. All specimens underwent force measurement using a uniaxial traction machine. The highest mean force required to break the bond was measured for PMMA bone cement (128.2 N) followed by universal resin cement (127.9 N), with no statistically significant difference. Glass ionomer cement showed significantly lower force resistance (78.1 N). Excellent bonding strength combined with easy application was found for universal resin cement, and thus, it is a potential alternative to acrylic bone cement in OOKP preparation. Published by the BMJ Publishing Group Limited. For permission to use (where not already granted under a licence) please go to http://group.bmj.com/group/rights-licensing/permissions.

  19. Enriching PMMA nanospheres with adjustable charges as novel templates for multicolored dye-PMMA nanocomposites

    International Nuclear Information System (INIS)

    Wang Xumei; Xu Shuping; Xu Weiqing; Liang Chongyang; Li Hongrui; Sun Fei

    2011-01-01

    Multicolored fluorescent dye loaded PMMA nanospheres were synthesized by the electrostatic adsorption of dye molecules on the charged PMMA nanospheres, whose charges were adjusted by choosing different initiators. The charged PMMA nanospheres have a wider capacity and advantage for combining the charged dyes. The fluorescent dye-PMMA composite nanospheres possess the advantages of higher brightness, longer lifetime and stronger resistance to photobleaching relative to dye molecules. Dye leakage remained lower than 5% over one week. These fluorescent nanospheres have been used in biological labels in cell imaging. They can easily stain blood cancer cells without further surface modification.

  20. Improved sample holders for the PMMA dosimeters

    International Nuclear Information System (INIS)

    Kobayashi, Toshikazu; Sone, Koji; Iso, Katsuaki

    1994-01-01

    PMMA dosimeters are widely used for high dose dosimetry. Dose is determined by measuring the change in optical density of the irradiated PMMA dosimeter element. Measurement precision depends on the mounting method of a dosimeter element in the sample room of a spectrophotometer. We tried to prepare three types of holders, (holders A, B and C in Figs. 1-3), according to the shape of PMMA dosimeter elements. We measured optical density of the irradiated PMMA dosimeter elements by using the three types of holders. It is revealed that the holder of the type A gives more precise results for the Red 4034 or Gammachrome YR dosimeter than that of the type B. The measurements with a spectrophotometer using the type C holder gives better results for the Red acrylic dosimeter than the case of the measurements by the exclusive reader. (author)

  1. Incorporation of multiwalled carbon nanotubes to acrylic based bone cements: effects on mechanical and thermal properties.

    Science.gov (United States)

    Ormsby, Ross; McNally, Tony; Mitchell, Christina; Dunne, Nicholas

    2010-02-01

    Polymethyl methacrylate (PMMA) bone cement-multiwalled carbon nanotube (MWCNT) nanocomposites with a weight loading of 0.1% were prepared using 3 different methods of MWCNT incorporation. The mechanical and thermal properties of the resultant nanocomposite cements were characterised in accordance with the international standard for acrylic resin cements. The mechanical properties of the resultant nanocomposite cements were influenced by the type of MWCNT and method of incorporation used. The exothermic polymerisation reaction for the PMMA bone cement was significantly reduced when thermally conductive functionalised MWCNTs were added. This reduction in exotherm translated in a decrease in thermal necrosis index value of the respective nanocomposite cements, which potentially could reduce the hyperthermia experienced in vivo. The morphology and degree of dispersion of the MWCNTs in the PMMA matrix at different scales were analysed using scanning electron microscopy. Improvements in mechanical properties were attributed to the MWCNTs arresting/retarding crack propagation through the cement by providing a bridging effect into the wake of the crack, normal to the direction of crack growth. MWCNT agglomerations were evident within the cement microstructure, the degree of these agglomerations was dependent on the method used to incorporate the MWCNTs into the cement. Copyright 2009. Published by Elsevier Ltd.

  2. Fungicidal PMMA-Undecylenic Acid Composites

    OpenAIRE

    Milica Petrović; Debora Bonvin; Heinrich Hofmann; Marijana Mionić Ebersold

    2018-01-01

    Undecylenic acid (UA), known as antifungal agent, still cannot be used to efficiently modify commercial dental materials in such a way that this affects Candida. Actually, issues with Candida infections and fungal resistance compromise the use of Poly(methyl-methacrylate) (PMMA) as dental material. The challenge remains to turn PMMA into an antifugal material, which can ideally affect both sessile (attached) and planktonic (free-floating) Candida cells. We aimed to tackle this challenge by de...

  3. Tensile Properties and Integrity of Clean Room and Low-Modulus Disposable Nitrile Gloves: A Comparison of Two Dissimilar Glove Types

    Science.gov (United States)

    Phalen, Robert N.; Wong, Weng kee

    2012-01-01

    Background: The selection of disposable nitrile exam gloves is complicated by (i) the availability of several types or formulations, (ii) product variability, and (iii) an inability of common quality control tests to detect small holes in the fingers. Differences in polymer formulation (e.g. filler and plasticizer/oil content) and tensile properties are expected to account for much of the observed variability in performance. Objectives: This study evaluated the tensile properties and integrity (leak failure rates) of two glove choices assumed to contain different amounts of plasticizers/oils. The primary aims were to determine if the tensile properties and integrity differed and if associations existed among these factors. Additional physical and chemical properties were evaluated. Methods: Six clean room and five low-modulus products were evaluated using the American Society for Testing and Materials Method D412 and a modified water-leak test to detect holes capable of passing a virus or chemical agent. Results: Significant differences in the leak failure rates and tensile properties existed between the two glove types (P ≤ 0.05). The clean room gloves were about three times more likely to have leak failures (chi-square; P = 0.001). No correlation was observed between leak failures and tensile properties. Solvent extract, an indication of added plasticizer/oil, was not associated with leak failures. However, gloves with a maximum modulus gloves were a better choice for protection against aqueous chemical or biological penetration. The observed variability between glove products indicated that glove selection cannot rely solely on glove type or manufacturer labeling. Measures of modulus and AD may aid in the selection process, in contrast with common measures of tensile strength and elongation at break. PMID:22201179

  4. In vivo performance of a reduced-modulus bone cement

    Science.gov (United States)

    Forehand, Brett Ramsey

    Total joint replacement has become one of the most common procedures in the area of orthopedics and is often the solution in patients with diseased or injured hip joints. Component loosening is a significant problem and is primarily caused by bone resorption at the bone-cement interface in cemented implants. It is our hypothesis that localized shear stresses are responsible for the resorption. It was previously shown analytically that local stresses at the interface could be reduced by using a cement of lower modulus. A new reduced modulus cement, polybutyl methylmethacrylate (PBMMA), was developed to test the hypothesis. PBMMA was formulated to exist as polybutyl methacrylate filler in a polymethyl methacrylate matrix. The success of PBMMA cement is based largely on the fact that the polybutyl component of the cement will be in the rubbery state at body temperature. In vitro characterization of the cement was undertaken previously and demonstrated a modulus of approximately one-eighth that of conventional bone cement, polymethyl methacrylate (PMMA) and increased fracture toughness. The purpose of this experiment was to perform an in vivo comparison of the two cements. A sheep model was selected. Total hip arthroplasty was performed on 50 ewes using either PBMMA or PMMA. Radiographs were taken at 6 month intervals. At one year, the contralateral femur of each sheep was implanted so that each animal served as its own control, and the animals were sacrificed. The stiffness of the bone-cement interface of the femoral component within the femur was assessed by applying a torque to the femoral component and demonstrated a significant difference in loosening between the cements when the specimens were tested in external rotation (p sheep had a greater amount of loosening for each subject, 59% versus 4% for standard PMMA. A radiographic analysis demonstrated more signs of loosening in the PMMA series of subjects. A brief histological examination showed similar bony

  5. Cement-Polymer Composite Containers for Radioactive Wastes Disposal

    International Nuclear Information System (INIS)

    Ghattas, N.K.; Eskander, S.B.; Bayoumi, T.A.; Saleh, H.M.

    2009-01-01

    Improving cement-composite containers using polymer as organic additives was studied extensively. Both unsaturated styrenated polyester (SPE) and polymethyl methacrylate (PMMA) were used to fill the pores in cement containers that used for disposal of radioactive wastes. Two different techniques were adopted for the addition of organic polymers based on their viscosity. The low density PMMA was added using impregnation technique. On the other hand high density SPE was mixed with cement paste as a premix process. Predetermined weight of dried borate radioactive powder waste simulate was introduced into the Cement-polymer composite (CPC) container and then closed before subjecting it to leaching characterization. The effect of the organic polymers on the hydration of cement matrix and on the properties of the obtained CPC container has been studied using X-ray diffraction, IR-analysis, thermal effects and weight loss. Porosity, pore parameters and rate of release were also determined. The results obtained showed that for the candidate CPC container positive effect of polymer dominates and an improvement in the retardation rate of PMMA release radionuclides was observed

  6. Cement Formation

    DEFF Research Database (Denmark)

    Telschow, Samira; Jappe Frandsen, Flemming; Theisen, Kirsten

    2012-01-01

    Cement production has been subject to several technological changes, each of which requires detailed knowledge about the high multiplicity of processes, especially the high temperature process involved in the rotary kiln. This article gives an introduction to the topic of cement, including...... an overview of cement production, selected cement properties, and clinker phase relations. An extended summary of laboratory-scale investigations on clinkerization reactions, the most important reactions in cement production, is provided. Clinker formations by solid state reactions, solid−liquid and liquid......−liquid reactions are discussed, as are the influences of particles sizes on clinker phase formation. Furthermore, a mechanism for clinker phase formation in an industrial rotary kiln reactor is outlined....

  7. Preparation and Characterization of Injectable Brushite Filled-Poly (Methyl Methacrylate Bone Cement

    Directory of Open Access Journals (Sweden)

    Lucas C. Rodriguez

    2014-09-01

    Full Text Available Powder-liquid poly (methyl methacrylate (PMMA bone cements are widely utilized for augmentation of bone fractures and fixation of orthopedic implants. These cements typically have an abundance of beneficial qualities, however their lack of bioactivity allows for continued development. To enhance osseointegration and bioactivity, calcium phosphate cements prepared with hydroxyapatite, brushite or tricalcium phosphates have been introduced with rather unsuccessful results due to increased cement viscosity, poor handling and reduced mechanical performance. This has limited the use of such cements in applications requiring delivery through small cannulas and in load bearing. The goal of this study is to design an alternative cement system that can better accommodate calcium-phosphate additives while preserving cement rheological properties and performance. In the present work, a number of brushite-filled two-solution bone cements were prepared and characterized by studying their complex viscosity-versus-test frequency, extrusion stress, clumping tendency during injection through a syringe, extent of fill of a machined void in cortical bone analog specimens, and compressive strength. The addition of brushite into the two-solution cement formulations investigated did not affect the pseudoplastic behavior and handling properties of the materials as demonstrated by rheological experiments. Extrusion stress was observed to vary with brushite concentration with values lower or in the range of control PMMA-based cements. The materials were observed to completely fill pre-formed voids in bone analog specimens. Cement compressive strength was observed to decrease with increasing concentration of fillers; however, the materials exhibited high enough strength for consideration in load bearing applications. The results indicated that partially substituting the PMMA phase of the two-solution cement with brushite at a 40% by mass concentration provided the best

  8. Study of the gamma irradiation effects on the PMMA/HA and PMMA/SW

    Energy Technology Data Exchange (ETDEWEB)

    Silva, P., E-mail: silva@ivic.v [Instituto Venezolano de Investigaciones Cientificas, Centro de Fisica, Carretera Panamericana Km. 11, Caracas 1020-A (Venezuela, Bolivarian Republic of); Albano, C. [Universidad Central de Venezuela, Facultad de Ingenieria (Venezuela, Bolivarian Republic of); Instituto Venezolano de Investigaciones Cientificas, Centro de Quimica (Venezuela, Bolivarian Republic of); Perera, R. [Departamento de Mecanica, Universidad Simon Bolivar, Caracas 1080-A (Venezuela, Bolivarian Republic of); Dominguez, N. [Instituto Venezolano de Investigaciones Cientificas, Centro de Quimica (Venezuela, Bolivarian Republic of)

    2010-03-15

    The behavior of the poly(methyl methacrylate) (PMMA) under the action of gamma radiation has been sufficiently studied. In this work, we present results from melt flow index (MFI), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC) and electron paramagnetic resonance (EPR) of PMMA composites with hydroxyapatite (HA) and seaweed residues (SW) irradiated with gamma rays at 1.08 kGy/h. Composites of PMMA/HA and PMMA/SW with 10%, 20% and 30% of the filler were prepared. The results show an increase in the MFI values with the integral dose of radiation, being consistent with chain-scission reactions. No EPR signal was observed in pure PMMA, while in the composites, the typical EPR signal of the PMMA radicals was observed, which increased with the amount of HA or SW. When comparing the relative intensities of the EPR signals for both types of composites, a slight increase in the concentration of free radicals generated in the sample with SW respect to that of PMMA/HA composite was obtained. A decay of the total free radical concentration was observed as time elapsed.

  9. Fungicidal PMMA-Undecylenic Acid Composites

    Directory of Open Access Journals (Sweden)

    Milica Petrović

    2018-01-01

    Full Text Available Undecylenic acid (UA, known as antifungal agent, still cannot be used to efficiently modify commercial dental materials in such a way that this affects Candida. Actually, issues with Candida infections and fungal resistance compromise the use of Poly(methyl-methacrylate (PMMA as dental material. The challenge remains to turn PMMA into an antifugal material, which can ideally affect both sessile (attached and planktonic (free-floating Candida cells. We aimed to tackle this challenge by designing PMMA-UA composites with different UA concentrations (3–12%. We studied their physico-chemical properties, the antifungal effect on Candida and the cytotoxicity toward human cells. We found that UA changes the PMMA surface into a more hydrophilic one. Mainly, as-preparation composites with ≥6% UA reduced sessile Candida for >90%. After six days, the composites were still efficiently reducing the sessile Candida cells (for ~70% for composites with ≥6% UA. Similar results were recorded for planktonic Candida. Moreover, the inhibition zone increased along with the UA concentration. The antifungal effect of UA was also examined at the surface of an UA-loaded agar and the minimal inhibitory concentration (MIC90 was below the lowest-studied 0.0125% UA. Furthermore, the embedded filamentation test after 24 h and 48 h showed complete inhibition of the Candida growth at 0.4% UA.

  10. Fungicidal PMMA-Undecylenic Acid Composites

    Science.gov (United States)

    Petrović, Milica; Hofmann, Heinrich

    2018-01-01

    Undecylenic acid (UA), known as antifungal agent, still cannot be used to efficiently modify commercial dental materials in such a way that this affects Candida. Actually, issues with Candida infections and fungal resistance compromise the use of Poly(methyl-methacrylate) (PMMA) as dental material. The challenge remains to turn PMMA into an antifugal material, which can ideally affect both sessile (attached) and planktonic (free-floating) Candida cells. We aimed to tackle this challenge by designing PMMA-UA composites with different UA concentrations (3–12%). We studied their physico-chemical properties, the antifungal effect on Candida and the cytotoxicity toward human cells. We found that UA changes the PMMA surface into a more hydrophilic one. Mainly, as-preparation composites with ≥6% UA reduced sessile Candida for >90%. After six days, the composites were still efficiently reducing the sessile Candida cells (for ~70% for composites with ≥6% UA). Similar results were recorded for planktonic Candida. Moreover, the inhibition zone increased along with the UA concentration. The antifungal effect of UA was also examined at the surface of an UA-loaded agar and the minimal inhibitory concentration (MIC90) was below the lowest-studied 0.0125% UA. Furthermore, the embedded filamentation test after 24 h and 48 h showed complete inhibition of the Candida growth at 0.4% UA. PMID:29316713

  11. Fungicidal PMMA-Undecylenic Acid Composites.

    Science.gov (United States)

    Petrović, Milica; Bonvin, Debora; Hofmann, Heinrich; Mionić Ebersold, Marijana

    2018-01-08

    Undecylenic acid (UA), known as antifungal agent, still cannot be used to efficiently modify commercial dental materials in such a way that this affects Candida . Actually, issues with Candida infections and fungal resistance compromise the use of Poly(methyl-methacrylate) (PMMA) as dental material. The challenge remains to turn PMMA into an antifugal material, which can ideally affect both sessile (attached) and planktonic (free-floating) Candida cells. We aimed to tackle this challenge by designing PMMA-UA composites with different UA concentrations (3-12%). We studied their physico-chemical properties, the antifungal effect on Candida and the cytotoxicity toward human cells. We found that UA changes the PMMA surface into a more hydrophilic one. Mainly, as-preparation composites with ≥6% UA reduced sessile Candida for >90%. After six days, the composites were still efficiently reducing the sessile Candida cells (for ~70% for composites with ≥6% UA). Similar results were recorded for planktonic Candida . Moreover, the inhibition zone increased along with the UA concentration. The antifungal effect of UA was also examined at the surface of an UA-loaded agar and the minimal inhibitory concentration (MIC90) was below the lowest-studied 0.0125% UA. Furthermore, the embedded filamentation test after 24 h and 48 h showed complete inhibition of the Candida growth at 0.4% UA.

  12. Viability of permanent PMMA spacer with combined free fasciocutaneous tissue transfer for failed charcot reconstruction: A 38 month prospective case report

    Directory of Open Access Journals (Sweden)

    Tammer Elmarsafi

    Full Text Available Introduction: Charcot Neuroarthropathy is a complex lower extremity pathology which predisposes the afflicted limb to ulcerations, osteomyelitis, and risk of major amputation. Charcot Neuroarthropathy often requires osseous reconstruction, which can be complicated with osteomyelitis and hardware infection. When soft tissue and osseous deficits must be concomitantly addressed, the use of PMMA spacers can be combined with free tissue transfers. Presentation of case: 71 year old Caucasian male with Diabetic Charcot Neuroarthopathy underwent osseous reconstruction with internal hardware. The surgical site was complicated by acute infection, osteomyelitis, exposed hardware requiring removal, and multiple surgical débridement. The degree of soft tissue and osseous deficit post-débridement required complex reconstruction. Discussion: The osseous deficit was addressed with the use of a permanent PMMA cement spacer. The soft tissue deficit was reconstructed with a free tissue transfer. This case report demonstrates the long term viability and utility of the use of permanent cement spacers when combined with free tissue transfer for closure of complex diabetic foot wounds. This case is an example of a multidisciplinary team approach to limb salvage with successful long term outcome; a plantigrade stable functional foot in an ambulatory highly active patient. Follow up time since initial intervention was 38 months. Conclusion: The use of a permanent PMMA cement spacer does not preclude free tissue transfer in complex host lower extremity reconstruction. A multidisciplinary team approach is a vital component to successful salvage outcomes. Keywords: Diabetes, Charcot neuroarthropathy, Ulcer, Cement spacer, Free tissue transfer, Osteomyelitis

  13. Microencapsulation of rifampicin: A technique to preserve the mechanical properties of bone cement.

    Science.gov (United States)

    Sanz-Ruiz, Pablo; Carbó-Laso, Esther; Del Real-Romero, Juan Carlos; Arán-Ais, Francisca; Ballesteros-Iglesias, Yolanda; Paz-Jiménez, Eva; Sánchez-Navarro, Magdalena; Pérez-Limiñana, María Ángeles; Vaquero-Martín, Javier

    2018-01-01

    Two-stage exchange with antibiotic-loaded bone cement spacers remains the gold standard for chronic periprosthetic joint infection (PJI). Rifampicin is highly efficient on stationary-phase staphylococci in biofilm; however, its addition to PMMA to manufacture spacers prevents polymerization and reduces mechanical properties. Isolation of rifampicin during polymerization by microencapsulation could allow manufacturing rifampicin-loaded bone cement maintaining elution and mechanical properties. Microcapsules of rifampicin with alginate, polyhydroxybutyratehydroxyvalerate (PHBV), ethylcellulose and stearic acid (SA) were synthesized. Alginate and PHBV microcapsules were added to bone cement and elution, compression, bending, hardness, setting time and microbiological tests were performed. Repeated measures ANOVA and Bonferroni post-hoc test were performed, considering a p cement specimens containing alginate microcapsules eluted more rifampicin than PHBV microcapsules or non-encapsulated rifampicin over time (p Cement with alginate microcapsules showed similar behavior in hardness tests to control cement over the study period (73 ± 1.68H D ). PMMA with alginate microcapsules exhibited the largest zones of inhibition in microbiological tests. Statistically significant differences in mean diameters of zones of inhibition between PMMA loaded with alginate-rifampicin (p = 0.0001) and alginate-PHBV microcapsules (p = 0.0001) were detected. Rifampicin microencapsulation with alginate is the best choice to introduce rifampicin in PMMA preserving mechanical properties, setting time, elution, and antimicrobial properties. The main applicability of this study is the opportunity for obtaining rifampicin-loaded PMMA by microencapsulation of rifampicin in alginate microparticles, achieving high doses of rifampicin in infected tissues, increasing the successful of PJI treatment. © 2017 Orthopaedic Research Society. Published by Wiley Periodicals, Inc. J Orthop Res

  14. CEMENT SLURRIES FOR GEOTHERMAL WELLS CEMENTING

    Directory of Open Access Journals (Sweden)

    Nediljka Gaurina-Međimurec

    1994-12-01

    Full Text Available During a well cementing special place belongs to the cement slurry design. To ensure the best quality of cementing, a thorough understanding of well parameters is essential, as well as behaviour of cement slurry (especially at high temperatures and application of proven cementing techniques. Many cement jobs fail because of bad job planning. Well cementing without regarding what should be accomplished, can lead to well problems (channels in the cement, unwanted water, gas or fluid production, pipe corrosion and expensive well repairs. Cementing temperature conditions are important because bot-tomhole circulating temperatures affect slurry thickening time, arheology, set time and compressive strength development. Knowing the actual temperature which cement encounters during placement allows the selection of proper cementing materials for a specific application. Slurry design is affected by well depth, bottom hole circulating temperature and static temperature, type or drilling fluid, slurry density, pumping time, quality of mix water, fluid loss control, flow regime, settling and free water, quality of cement, dry or liquid additives, strength development, and quality of the lab cement testing and equipment. Most Portland cements and Class J cement have shown suitable performances in geot-hermal wells. Cement system designs for geothermal wells differ from those for conventional high temperature oil and gas wells in the exclusive use of silica flour instead of silica sand, and the avoidance of fly ash as an extender. In this paper, Portland cement behaviour at high temperatures is described. Cement slurry and set cement properties are also described. Published in literature, the composition of cement slurries which were tested in geothermal conditions and which obtained required compressive strength and water permeability are listed. As a case of our practice geothermal wells Velika Ciglena-1 and Velika Ciglena-la are described.

  15. Lunar cement

    Science.gov (United States)

    Agosto, William N.

    1992-01-01

    With the exception of water, the major oxide constituents of terrestrial cements are present at all nine lunar sites from which samples have been returned. However, with the exception of relatively rare cristobalite, the lunar oxides are not present as individual phases but are combined in silicates and in mixed oxides. Lime (CaO) is most abundant on the Moon in the plagioclase (CaAl2Si2O8) of highland anorthosites. It may be possible to enrich the lime content of anorthite to levels like those of Portland cement by pyrolyzing it with lunar-derived phosphate. The phosphate consumed in such a reaction can be regenerated by reacting the phosphorus product with lunar augite pyroxenes at elevated temperatures. Other possible sources of lunar phosphate and other oxides are discussed.

  16. Thermal Degradation of Nanocomposited PMMA/TiO2 Nanocomposites

    International Nuclear Information System (INIS)

    Hafizah, Nik Noor; Mamat, Mohamad Hafiz; Rusop, Mohamad; Said, Che Mohamad Som; Abidin, Mohd Hanafiah

    2013-01-01

    The polymer nanocomposite is a new choice to conventionally filled polymers. The lack of proper binding between the filler and the polymer can lead the decrease of the thermal and other properties of the nanocomposites. In this study, the nanocomposited PMMA/TiO 2 nanocomposites were prepared using sonication and solution casting method at different weight percent TiO 2 . The aims of adding TiO 2 in the PMMA is to study the effects of TiO 2 nanofiller on the thermal properties nanocomposites. FESEM results show the higher amounts of TiO 2 in PMMA increase the rough surface morphology of the samples. Further, the Raman results reveal that the TiO 2 nanofiller were successfully intercalated into the PMMA matrix. In addition, the thermal properties of nanocomposited PMMA/TiO 2 nanocomposites were increased with the addition of TiO 2 in the PMMA.

  17. Mechanical properties and antibiotic release characteristics of poly(methyl methacrylate)-based bone cement formulated with mesoporous silica nanoparticles.

    Science.gov (United States)

    Letchmanan, Kumaran; Shen, Shou-Cang; Ng, Wai Kiong; Kingshuk, Poddar; Shi, Zhilong; Wang, Wilson; Tan, Reginald B H

    2017-08-01

    The influence of mesoporous silica nanoparticles (MSNs) loaded with antibiotics on the mechanical properties of functional poly(methyl methacrylate)-(PMMA) based bone cements is investigated. The incorporation of MSNs to the bone cements (8.15wt%) shows no detrimental effects on the biomechanical properties of the freshly solidified bone cements. Importantly, there are no significant changes in the compression strength and bending modulus up to 6 months of aging in PBS buffer solution. The preserved mechanical properties of MSN-functionalized bone cements is attributed to the unchanged microstructures of the cements, as more than 96% of MSNs remains in the bone cement matrix to support the cement structures after 6 months of aging. In addition, the MSN-functionalized bone cements are able to increase the drug release of gentamicin (GTMC) significantly as compared with commercially available antibiotic-loaded bone cements. It can be attributed to the loaded nano-sized MSNs with uniform pore channels which build up an effective nano-network path enable the diffusion and extended release of GTMC. The combination of excellent mechanical properties and sustainable drug delivery efficiency demonstrates the potential applicability of MSN-functionalized PMMA bone cements for orthopedic surgery to prevent post-surgery infection. Copyright © 2017 Elsevier Ltd. All rights reserved.

  18. Fracture toughness of titanium–cement interfaces: effects of fibers and loading angles

    Directory of Open Access Journals (Sweden)

    Khandaker M

    2014-04-01

    Full Text Available Morshed Khandaker,1 Khatri Chhetri Utsaha,1 Tracy Morris21Department of Engineering and Physics, 2Department of Mathematics and Statistics, University of Central Oklahoma, Edmond, OK, USAAbstract: Ideal implant–cement or implant–bone interfaces are required for implant fixation and the filling of tissue defects created by disease. Micron- to nanosize osseointegrated features, such as surface roughness, fibers, porosity, and particles, have been fused with implants for improving the osseointegration of an implant with the host tissue in orthopedics and dentistry. The effects of fibers and loading angles on the interface fracture toughness of implant–cement specimens with and without fibers at the interface are not yet known. Such studies are important for the design of a long-lasting implant for orthopedic applications. The goal of this study was to improve the fracture toughness of an implant–cement interface by deposition of micron- to nanosize fibers on an implant surface. There were two objectives in the study: 1 to evaluate the influence of fibers on the fracture toughness of implant–cement interfaces with and without fibers at the interfaces, and 2 to evaluate the influence of loading angles on implant–cement interfaces with and without fibers at the interfaces. This study used titanium as the implant, poly(methyl methacrylate (PMMA as cement, and polycaprolactone (PCL as fiber materials. An electrospinning unit was fabricated for the deposition of PCL unidirectional fibers on titanium (Ti plates. The Evex tensile test stage was used to determine the interface fracture toughness (KC of Ti–PMMA with and without PCL fibers at 0°, 45°, and 90° loading angles, referred to in this article as tension, mixed, and shear tests. The study did not find any significant interaction between fiber and loading angles (P>0.05, although there was a significant difference in the KC means of Ti–PMMA samples for the loading angles (P<0

  19. Au nanoparticles in PMMA matrix: In situ synthesis and the effect of Au nanoparticles on PMMA conductivity

    International Nuclear Information System (INIS)

    Yilmaz, Eda; Suzer, Sefik

    2010-01-01

    Thin PMMA films with and without gold nanoparticles were subjected to ±10 V d.c. and a.c. (square wave) excitations in various frequencies while recording their XPS spectra, and the resulting differences due to charging were examined. Both pure PMMA films and films containing gold nanoparticles showed charging shifts, but those of pure PMMA were more extensive than of PMMA containing gold nanoparticles, suggesting enhanced conductivity, induced by the incorporated gold nanoparticles. Non-charging behavior for these films was also observed with the increase of gold nanoparticle concentration. Gold nanoparticles were in situ synthesized and photo-patterned within the polymer films by UV irradiation.

  20. Studies to compare radioactivity of bone cements and their ingredient X-ray contrast media

    International Nuclear Information System (INIS)

    Hopf, C.; Gloebel, B.; Hopf, T.; Universitaet des Saarlandes, Homburg/Saar; Universitaet des Saarlandes, Homburg/Saar

    1990-01-01

    Various PMMA bone cements/containing zirconium oxide (ZrO 2 ) as an X-ray contrast medium and zirconium oxides of several manufacturers were tested for their radioactivity by means of a gamma spectrometer. All the bone cements tested (Implast, Palacos R, and Sulfix-6) showed a certain degree of radioactivity. The radiation source in the bone cement is the added zirconium oxide, which is polluted by radioactive elements. The examination of various zirconium oxides showed some high radioactive emissions. (orig./GDG) [de

  1. Effect of the sterilization process on physical and mechanical properties of the bonacryl bone cement

    International Nuclear Information System (INIS)

    Morejon, L.; Delgado, J.A.; Aguero, L.; Rapado, M.; Ginebra, M.P.; Gil, F.J.; Mendizabal, E.

    2008-01-01

    The use of bone cements of poly(methyl methacrylate) (PMMA) to fix artificial prosthesis to the human body is a habitual method in orthopedic surgery. The hip and the knee joints have a very complex biomechanics and support high loads, for these reasons, acrylic bone cements have to comply with international standards in order to secure the biofuncionality and durability of the implant. In this work we report the effect of sterilization by ethylene oxide or gamma radiation on the BONACRYL Cuban cement. We determined how sterilization methods affect the molecular weight of the polymer as well as its quasi-static mechanical properties. The results demonstrated that the gamma radiation modifies the molecular weight of the PMMA although the compression and bending strength were not affected by the sterilization process applied. (authors)

  2. TEM specimen preparation of semiconductor-PMMA-metal interfaces

    International Nuclear Information System (INIS)

    Thangadurai, P.; Lumelsky, Yulia; Silverstein, Michael S.; Kaplan, Wayne D.

    2008-01-01

    Transmission electron microscopy (TEM) cross-section specimens of PMMA in contact with gold and Si were prepared by focused ion beam (FIB) and compared with plan-view PMMA specimens prepared by a dip-coating technique. The specimens were characterized by TEM and electron energy loss spectroscopy (EELS). In the cross-section specimens, the thin films of PMMA were located in a Si-PMMA-Au multilayer. Different thicknesses of PMMA films were spin-coated on the Si substrates. The thickness of the TEM specimens prepared by FIB was estimated using EELS to be 0.65 of the plasmon mean-free-path. Along the PMMA-Au interface, Au particle diffusion into the PMMA was observed, and the size of the Au particles was in the range of 2-4 nm. Dip-coating of PMMA directly on Cu TEM grids resulted in thin specimens with a granular morphology, with a thickness of 0.58 of the plasmon mean-free-path. The dip-coated specimens were free from ion milling induced artifacts, and thus serve as control specimens for comparison with the cross-sectioned specimens prepared by FIB

  3. Radiofrequency-activated PMMA-augmentation through cannulated pedicle screws: A cadaver study to determine the biomechanical benefits in the osteoporotic spine.

    Science.gov (United States)

    Karius, T; Deborre, C; Wirtz, D C; Burger, C; Prescher, A; Fölsch, A; Kabir, K; Pflugmacher, R; Goost, H

    2017-01-01

    PMMA-augmentation of pedicle screws strengthens the bone-screw-interface reducing cut-out risk. Injection of fluid cement bears a higher risk of extravasation, with difficulty of application because of inconsistent viscosity and limited injection time. To test a new method of cement augmentation of pedicle screws using radiofrequency-activated PMMA, which is suspected to be easier to apply and have less extravasations. Twenty-seven fresh-frozen human cadaver lumbar spines were divided into 18 osteoporotic (BMD ≤ 0.8 g/cm2) and 9 non-osteoporotic (BMD > 0.8 g/cm2) vertebral bodies. Bipedicular cannulated pedicle screws were implanted into the vertebral bodies; right screws were augmented with ultra-high viscosity PMMA, whereas un-cemented left pedicle screws served as negative controls. Cement distribution was controlled with fluoroscopy and CT scans. Axial pullout forces of the screws were measured with a material testing machine, and results were analyzed statistically. Fluoroscopy and CT scans showed that in all cases an adequately big cement depot with homogenous form and no signs of extravasation was injected. Pullout forces showed significant differences (p < 0.001) between the augmented and non-augmented pedicle screws for bone densities below 0.8 g/cm2 (661.9 N ± 439) and over 0.8 g/cm2 (744.9 N ± 415). Pullout-forces were significantly increased in osteoporotic as well as in non-osteoporotic vertebral bodies without a significant difference between these groups using this standardized, simple procedure with increased control and less complications like extravasation.

  4. Synthesis of TiO(2)-PMMA nanocomposite: using methacrylic acid as a coupling agent.

    Science.gov (United States)

    Khaled, S M; Sui, Ruohong; Charpentier, Paul A; Rizkalla, Amin S

    2007-03-27

    Inorganic-polymer nanocomposites are of significant interest for emerging materials due to their improved properties and unique combination of properties. Methacrylic acid (MA), a functionalization agent that can chemically link TiO2 nanomaterials (n-TiO2) and polymer matrix, was used to modify the surface of n-TiO2 using a Ti-carboxylic coordination bond. Then, the double bond in MA was copolymerized with methyl methacrylate (MMA) to form a n-TiO2-PMMA nanocomposite. The resulting n-TiO2-PMMA nanocomposite materials were characterized by using thermal analysis, electron microscopy, and elemental analysis. The dynamic mechanical properties (Young's and shear modulus) were measured using an ultrasonic pulse technique. The electron microscopy results showed a good distribution of the nanofillers in the polymer matrix. The glass transition temperature, thermal degradation temperature, and dynamic elastic moduli of the nanocomposites were shown to increase with an increase in the weight percentage of nanofibers in the composite. The resulting nanocomposites exhibited improved elastic properties and have potential application in dental composites and bone cements.

  5. Study of the structure of concrete with C-14-PMMA method

    Science.gov (United States)

    Muuri, E.; Tikkanen, O.; Ikonen, J.; Siitari-Kauppi, M.; Autio, M.

    2017-12-01

    Cement is used widely in the construction industry and, additionally, in the waste management industry for the stabilization of hazardous materials because of its capacity for both physical and chemical immobilization of contaminants. Cementitious materials have also been suggested as the backfilling materials, for example, in deep geological repositories for the final disposal of spent nuclear fuel. As a result, it is necessary to study the structure of the materials in different conditions. In this study, the structure of concrete was studied with the polymethylmetacrylate (PMMA) method in samples from the construction industry. The spatial distribution of porosity was characterized using this autoradiography method that involves the impregnation of a dried rock sample of hand specimen size with 14C-labelled methyl methacrylate (MMA) in vacuum, thermally initiated polymerization, film and digital autoradiography, and porosity calculation routines relying on digital image processing techniques [1]. Three main components are clearly visible on the PMMA autoradiographs of the studied concrete samples, because of their contrasted porosity (Fig 1.). Ground matrix cement shows even porosity; 27.0±4.7 %. The other two phases are mineral grains and bubbles, which are classified into four categories against their size and quantity. Fig 1. The scanned surface of the concrete sample (left) and the corresponding autoradiograph (right), where the darkest areas are caused by larger activity, and thus, larger porosity. The exposure time used for the autoradiogram was three days. J. Sammaljärvi, L. Jokelainen, J. Ikonen, M. Siitari-Kauppi, Eng. Geol. 135-136, 52-59 (2012).

  6. Effect of barium-coated halloysite nanotube addition on the cytocompatibility, mechanical and contrast properties of poly(methyl methacrylate) cement.

    Science.gov (United States)

    Jammalamadaka, Uday; Tappa, Karthik; Weisman, Jeffery A; Nicholson, James Connor; Mills, David K

    2017-01-01

    Halloysite nanotubes (HNTs) were investigated as a platform for tunable nanoparticle composition and enhanced opacity in poly(methyl methacrylate) (PMMA) bone cement. Halloysite has been widely used to increase the mechanical properties of various polymer matrices, in stark contrast to other fillers such as barium sulfate that provide opacity but also decrease mechanical strength. The present work describes a dry deposition method for successively fabricating barium sulfate nanoparticles onto the exterior surface of HNTs. A sintering process was used to coat the HNTs in barium sulfate. Barium sulfate-coated HNTs were then added to PMMA bone cement and the samples were tested for mechanical strength and tailored opacity correlated with the fabrication ratio and the amount of barium sulfate-coated HNTs added. The potential cytotoxic effect of barium-coated HNTs in PMMA cement was also tested on osteosarcoma cells. Barium-coated HNTs were found to be completely cytocompatible, and cell proliferation was not inhibited after exposure to the barium-coated HNTs embedded in PMMA cement. We demonstrate a simple method for the creation of barium-coated nanoparticles that imparted improved contrast and material properties to native PMMA. An easy and efficient method for coating clay nanotubes offers the potential for enhanced imaging by radiologists or orthopedic surgeons.

  7. The Mechanical Behavior of Bone Cement in THR in the Presense of Cavities

    Directory of Open Access Journals (Sweden)

    A. Benouis

    2014-06-01

    Full Text Available In this work we analyze three-dimensionally using the finite element method, the level and the Von Mises stress equivalent distribution induced around a cavity and between two cavities located in the proximal and distal bone cement polymethylmethacrylate (PMMA. The effects of the position around two main axes (vertical and horizontal of the cavity with respect to these axes, of the cavity - cavity interdistance and of the type of loading (static on the mechanical behavior of cement orthopedic are highlighted. We show that the breaking strain of the cement is largely taken when the cement in its proximal-lateral part contains cavities very close adjacent to each other. This work highlights not only the effect of the density of cavities, in our case simulated by cavity-cavity interdistance, but also the nature of the activity of the patient (patient standing corresponding to static efforts on the mechanical behavior of cement.

  8. Approach to osteomyelitis treatment with antibiotic loaded PMMA.

    Science.gov (United States)

    Wentao, Zhang; Lei, Guangyu; Liu, Yang; Wang, Wei; Song, Tao; Fan, Jinzhu

    2017-01-01

    To reduce the incidence of osteomyelitis infection, local antibiotic impregnated delivery systems are commonly used as a promising and effective approach to deliver high antibiotic concentrations at the infection site. The objective of this review was to provide a literature review regarding approach to osteomyelitis treatment with antibiotic loaded PMMA. Literature study regarding osteomyelitis treatment with antibiotic loaded carriers using key terms Antibiotic, osteomyelitis, biodegradable PMMA through published articles. Hands searching of bibliographies of identified articles were also undertaken. We concluded that Antibiotic-impregnated PMMA beads are useful options for the treatment of osteomyelitis for prolonged drug therapy. Copyright © 2016 Elsevier Ltd. All rights reserved.

  9. Producing cement

    Energy Technology Data Exchange (ETDEWEB)

    Stone, E G

    1923-09-12

    A process and apparatus are described for producing Portland cement in which pulverized shale is successively heated in a series of inclined rotary retorts having internal stirrers and oil gas outlets, which are connected to condensers. The partially treated shale is removed from the lowermost retort by a conveyor, then fed separately or conjointly into pipes and thence into a number of vertically disposed retorts. Each of these retorts may be fitted interiorly with vertical arranged conveyors which elevate the shale and discharge it over a lip, from whence it falls to the bottom of the retorts. The lower end of each casing is furnished with an adjustable discharge door through which the spent shale is fed to a hopper, thence into separate trucks. The oil gases generated in the retorts are exhausted through pipes to condensers. The spent shale is conveyed to a bin and mixed while hot with ground limestone. The admixed materials are then ground and fed to a rotary kiln which is fired by the incondensible gases derived from the oil gases obtained in the previous retorting of the shale. The calcined materials are then delivered from the rotary kiln to rotary coolers. The waste gases from the kiln are utilized for heating the retorts in which the ground shale is heated for the purpose of extracting therefrom the contained hydrocarbon oils and gases.

  10. Study of PMMA materials for a digital optical module

    Science.gov (United States)

    Spina, Roberto; Tricarico, Luigi; Berardi, Vincenzo; De Rosa, Gianfranca; Ruggeri, Alan C.; Mastrorilli, Piero

    2018-05-01

    This work illustrates the material characterization to realize of a prototypal polymeric cover of a Digital Optical Module for the Hyper-Kamiokande neutrino experiment. The cover was made of a high transmittance poly-methyl methacrylate (PMMA), used as a glass substitute. The main objective of the present research is to investigate the structural and optical properties of PMMA, evaluating the respect of the project specification.

  11. Outcomes of osteoporotic trochanteric fractures treated with cement-augmented dynamic hip screw

    Science.gov (United States)

    Gupta, Rakesh Kumar; Gupta, Vinay; Gupta, Navdeep

    2012-01-01

    Background: Dynamic hip screw (DHS) has been the standard treatment for stable trochanteric fracture patterns, but complications of lag screw cut out from a superior aspect, due to inadequate bone anchorage, occur frequently in elderly osteoporotic patients. Polymethylmethacrylate (PMMA) has been used as an augmentation tool to facilitate fixation stability in cadaveric femora for biomechanical studies and in pathological fractures. However, there are very few reports on the utilization of PMMA cement to prevent these complications in fresh intertrochanteric fractures. A prospective study was conducted to evaluate the outcome and efficacy of PMMA augmented DHS in elderly osteoporotic patients with intertrochanteric fractures. Materials and Methods: The study included 64 patients (AO type31-A2.1 in eight, A2.2 in 29, A2.3 in 17 patients, and 31-A3.1 in five, A3.2 in three, and A3.3 in two patients) with an average age of 72 years (60 – 94 years) of which 60 were available for final followup. PMMA augmentation of DHS was performed in all cases by injecting PMMA cement into the femoral head with a custommade gun designed by the authors. The clinical outcome was rated as per the Salvati and Wilson scoring system at the time of final followup of one year. Results were graded as excellent (score > 31), good (score 24 – 31), fair (score 16 – 23), and poor (score < 16). Results: Fracture united in all patients and the average time to union was 13.8 weeks (range 12 – 16 weeks). At an average followup of 18 months (range 12 – 24 months), no incidence of varus collapse or superior screw cut out was observed in any of the patients in spite of weightbearing ambulation from the early postoperative period. There was no incidence of avascular necrosis (AVN) or cement penetration into the joint in our series. Most of the patients were able to regain their prefracture mobility status with a mean hip pain score of 8.6. Conclusion: Cement augmentation of DHS appears to be an

  12. Outcomes of osteoporotic trochanteric fractures treated with cement-augmented dynamic hip screw

    Directory of Open Access Journals (Sweden)

    Rakesh Kumar Gupta

    2012-01-01

    Full Text Available Background: Dynamic hip screw (DHS has been the standard treatment for stable trochanteric fracture patterns, but complications of lag screw cut out from a superior aspect, due to inadequate bone anchorage, occur frequently in elderly osteoporotic patients. Polymethylmethacrylate (PMMA has been used as an augmentation tool to facilitate fixation stability in cadaveric femora for biomechanical studies and in pathological fractures. However, there are very few reports on the utilization of PMMA cement to prevent these complications in fresh intertrochanteric fractures. A prospective study was conducted to evaluate the outcome and efficacy of PMMA augmented DHS in elderly osteoporotic patients with intertrochanteric fractures. Materials and Methods: The study included 64 patients (AO type31-A2.1 in eight, A2.2 in 29, A2.3 in 17 patients, and 31-A3.1 in five, A3.2 in three, and A3.3 in two patients with an average age of 72 years (60 − 94 years of which 60 were available for final followup. PMMA augmentation of DHS was performed in all cases by injecting PMMA cement into the femoral head with a custommade gun designed by the authors. The clinical outcome was rated as per the Salvati and Wilson scoring system at the time of final followup of one year. Results were graded as excellent (score > 31, good (score 24 − 31, fair (score 16 − 23, and poor (score < 16. Results: Fracture united in all patients and the average time to union was 13.8 weeks (range 12 − 16 weeks. At an average followup of 18 months (range 12 − 24 months, no incidence of varus collapse or superior screw cut out was observed in any of the patients in spite of weightbearing ambulation from the early postoperative period. There was no incidence of avascular necrosis (AVN or cement penetration into the joint in our series. Most of the patients were able to regain their prefracture mobility status with a mean hip pain score of 8.6. Conclusion: Cement augmentation of DHS appears

  13. Effect of barium-coated halloysite nanotube addition on the cytocompatibility, mechanical and contrast properties of poly(methyl methacrylate cement

    Directory of Open Access Journals (Sweden)

    Jammalamadaka U

    2017-06-01

    Full Text Available Uday Jammalamadaka,1 Karthik Tappa,1 Jeffery A Weisman,1 James Connor Nicholson,2 David K Mills1,3 1Center for Biomedical Engineering and Rehabilitation Science, 2Nanosystems Engineering, 3The School of Biological Sciences, Louisiana Tech University, Ruston, LA, USA Abstract: Halloysite nanotubes (HNTs were investigated as a platform for tunable nanoparticle composition and enhanced opacity in poly(methyl methacrylate (PMMA bone cement. Halloysite has been widely used to increase the mechanical properties of various polymer matrices, in stark contrast to other fillers such as barium sulfate that provide opacity but also decrease mechanical strength. The present work describes a dry deposition method for successively fabricating barium sulfate nanoparticles onto the exterior surface of HNTs. A sintering process was used to coat the HNTs in barium sulfate. Barium sulfate-coated HNTs were then added to PMMA bone cement and the samples were tested for mechanical strength and tailored opacity correlated with the fabrication ratio and the amount of barium sulfate-coated HNTs added. The potential cytotoxic effect of barium-coated HNTs in PMMA cement was also tested on osteosarcoma cells. Barium-coated HNTs were found to be completely cytocompatible, and cell proliferation was not inhibited after exposure to the barium-coated HNTs embedded in PMMA cement. We demonstrate a simple method for the creation of barium-coated nanoparticles that imparted improved contrast and material properties to native PMMA. An easy and efficient method for coating clay nanotubes offers the potential for enhanced imaging by radiologists or orthopedic surgeons. Keywords: barium, bone cement, halloysite, imaging, PMMA, sintering

  14. Strengthening of Poly Methyl Methacrylate (PMMA) through Electron Irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Yoo, Sung Ho; Lim, Hyung San; Ha, Jun Mok; Cho, Sung Oh [KAIST, Daejeon (Korea, Republic of)

    2015-05-15

    Poly Methyl Methacrylate (PMMA) was previously known to show the deteriorating mechanical properties when irradiated with electrons. This is true for low electron irradiation does, but it was found, through experimentation, that at high irradiation dose, PMMA demonstrates improved mechanical properties. With enough electron irradiation dose, the scissions can form new links amongst one another to achieve stability that surpasses that of the PMMA in pre-irradiation treatment state. With higher irradiation dosage and beam strength, hardness of irradiated PMMA could be increased to a much greater extent. Electrons with 50keV of energy can only penetrate around 30 μm of PMMA, thus increasing the beam energy could potentially allow for hardening of not just the surface of the PMMA samples, but the whole samples themselves. Furthermore, Pencil Hardness Test is a method to roughly analyze a material's hardness and does not provide an accurate feedback on the mechanical properties of the material of interest. Hence, a more thorough and effective method of measuring data from the use of equipment such as IZOD Impact Tester, Strain-Stress Tester and Haze Meter will be utilized in the future.

  15. Asphalt cement poisoning

    Science.gov (United States)

    ... petroleum material that hardens when it cools. Asphalt cement poisoning occurs when someone swallows asphalt. If hot ... found in: Road paving materials Roofing materials Tile cements Asphalt may also be used for other purposes.

  16. Radioactivity of bone cement

    International Nuclear Information System (INIS)

    Scherer, M.A.; Winkler, R.; Ascherl, R.; Lenz, E.

    1993-01-01

    A total of 14 samples of different types of bone cement from five different manufacturers were examined for their radioactivity. Each of the investigated bone cements showed a low radioactivity level, i.e. between [de

  17. Ultrafine portland cement performance

    Directory of Open Access Journals (Sweden)

    C. Argiz

    2018-04-01

    Full Text Available By mixing several binder materials and additions with different degrees of fineness, the packing density of the final product may be improved. In this work, ultrafine cement and silica fume mixes were studied to optimize the properties of cement-based materials. This research was performed in mortars made of two types of cement (ultrafine Portland cement and common Portland cement and two types of silica fume with different particle-size distributions. Two Portland cement replacement ratios of 4% and 10% of silica fume were selected and added by means of a mechanical blending method. The results revealed that the effect of the finer silica fume mixed with the coarse cement enhances the mechanical properties and pore structure refinement at a later age. This improvement is somewhat lower in the case of ultrafine cement with silica fume.

  18. Neutron diffraction from holographic gratings in PMMA

    International Nuclear Information System (INIS)

    Havermeyer, F.; Kraetzig, E.; Rupp, R.A.; Schubert, D.W.

    1999-01-01

    Complete text of publication follows. By definition photorefractive materials change the refractive index for light under the action of light. Using the spatially modulated light intensity pattern from the interference of two plane waves, volume phase gratings with accurately defined spacings can be produced. Depending on the material there are many physical origins for these gratings, but in most cases they are linked to a density modulation and, consequently, to a refractive index grating for neutrons. By diffraction of light or neutrons from such gratings even small refractive index changes down to Δn ∼ 10 -7 - 10 -9 can be measured. In our photopolymer system PMMA/MMA (poly(methyl methacrylate) with a content of 10-20% of the residual monomer methyl methacrylate) inhomogeneous illumination leads to local post-polymerisation processes of the residual monomer. The resulting light-optical refractive index grating is caused by the modulation of the monomer/polymer ratio as well as by the modulation of the total density. Only by the unique combination of methods for light and neutron diffraction, available at HOLONS (Holography and Neutron Scattering, instrument at the GKSS research centre), both contributions can be separated. We discuss the angular dependence of the neutron diffraction efficiency for weakly and strongly (efficiencies up to 60% have been achieved) modulated gratings and propose a simple model for the evaluation of the gratings. (author)

  19. Sulfur polymer cement concrete

    International Nuclear Information System (INIS)

    Weber, H.H.; McBee, W.C.

    1990-01-01

    Sulfur-based composite materials formulated using sulfur polymer cement (SPC) and mineral aggregates are described and compared with conventional portland cement based materials. Materials characteristics presented include mechanical strength, chemical resistance, impact resistance, moisture permeation, and linear shrinkage during placement and curing. Examples of preparation and placement of sulfur polymer cement concrete (SC) are described using commercial scale equipment. SC applications presented are focused into hostile chemical environments where severe portland cement concrete (PCC) failure has occurred

  20. In vitro and in vivo biological responses to a novel radiopacifying agent for bone cement

    Science.gov (United States)

    Wang, J.S; Diaz, J; Sabokbar, A; Athanasou, N; Kjellson, F; Tanner, K.E; McCarthy, I.D; Lidgren, L

    2005-01-01

    Iodixanol (IDX) and iohexol (IHX) have been investigated as possible radiopacification agents for polymethylmethacrylate (PMMA) bone cement, to replace the currently used barium sulphate and zirconia. IDX and IHX are both water-soluble iodine-based contrast media and for the last 20 years have been used extensively in clinical diagnostic procedures such as contrast media enhanced computed tomography, angiography and urography. One of the major reasons to remove the current radiopacifying agents is their well-documented cytotoxicity and their potential to increase bone resorption. Using in vitro bone resorption assays, the effect of PMMA particles plus IDX or IHX to induce osteoclast formation and lacunar resorption on dentine slices has been investigated. These responses have been compared with the in vitro response to PMMA particles containing the conventional radiopacifying agents, that is, barium sulphate and zirconia. In parallel, the in vivo reaction, in terms of new bone formation, to particles of these materials has been tested using a bone harvest chamber in rabbit tibiae. In vitro cell culture showed that PMMA containing IHX resulted in significantly less bone resorption than PMMA containing the conventional opacifiers. In vivo testing, however, showed no significant differences between the amounts of new bone formed around cement samples containing the two iodine-based opacifying agents in particulate form, although both led to fewer inflammatory cells than particles of PMMA containing zirconia. Our results suggest that a non-ionic radiopacifier could be considered as an alternative to the conventional radiopacifying agents used in biomaterials in orthopaedic surgery. PMID:16849166

  1. Activity of Fosfomycin- and Daptomycin-Containing Bone Cement on Selected Bacterial Species Being Associated with Orthopedic Infections

    Directory of Open Access Journals (Sweden)

    Sigrun Eick

    2017-01-01

    Full Text Available The purpose of this study was to determine activity of fosfomycin/gentamicin and daptomycin/gentamicin-containing PMMA bone-cement against Staphylococcus aureus (MRSA, MSSA, Staphylococcus epidermidis, Enterococcus faecium (VRE, and E. coli (ESBL; only fosfomycin. Test specimens of the bone cement were formed and bacteria in two concentrations were added one time or repeatedly up to 96 h. All fosfomycin-containing cement killed ultimately all MSSA, Staphylococcus epidermidis, and E. coli within 24 h; growth of MRSA was suppressed up to 48 h. Activity of daptomycin-containing cement depended on the concentration; the highest concentrated bone cement used (1.5 g daptomycin/40 g of powder was active against all one-time added bacteria. When bacteria were added repeatedly to fosfomycin-containing cement, growth was suppressed up to 96 h and that of MRSA and VRE only up to 24 h. The highest concentration of daptomycin suppressed the growth of repeated added bacteria up to 48 h (VRE until 96 h (MSSA, MRSA. In conclusion, PMMA bone cement with 1.5 g of daptomycin and 0.5 g of gentamicin may be an alternative in treatment of periprosthetic infections caused by Gram-positive bacteria.

  2. Preparation and characterization of transparent PMMA-cellulose-based nanocomposites.

    Science.gov (United States)

    Kiziltas, Esra Erbas; Kiziltas, Alper; Bollin, Shannon C; Gardner, Douglas J

    2015-01-01

    Nanocomposites of polymethylmethacrylate (PMMA) and cellulose were made by a solution casting method using acetone as the solvent. The nanofiber networks were prepared using three different types of cellulose nanofibers: (i) nanofibrillated cellulose (NFC), (ii) cellulose nanocrystals (CNC) and (iii) bacterial cellulose from nata de coca (NDC). The loading of cellulose nanofibrils in the PMMA varied between 0.25 and 0.5 wt%. The mechanical properties of the composites were evaluated using a dynamic mechanical thermal analyzer (DMTA). The flexural modulus of the nanocomposites reinforced with NDC at the 0.5 wt% loading level increased 23% compared to that of pure PMMA. The NFC composite also exhibited a slightly increased flexural strength around 60 MPa while PMMA had a flexural strength of 57 MPa. The addition of NDC increased the storage modulus (11%) compared to neat PMMA at room temperature while the storage modulus of PPMA/CNC nanocomposite containing 0.25 and 0.5 wt% cellulose increased about 46% and 260% to that of the pure PMMA at the glass transition temperature, respectively. Thermogravimetric analysis (TGA) indicated that there was no significant change in thermal stability of the composites. The UV-vis transmittance of the CNF nanocomposites decreased by 9% and 27% with the addition of 0.25 wt% CNC and NDC, respectively. This work is intended to spur research and development activity for application of CNF reinforced PMMA nanocomposites in applications such as: packaging, flexible screens, optically transparent films and light-weight transparent materials for ballistic protection. Copyright © 2015 Elsevier Ltd. All rights reserved.

  3. Creep behavior of bone cement: a method for time extrapolation using time-temperature equivalence.

    Science.gov (United States)

    Morgan, R L; Farrar, D F; Rose, J; Forster, H; Morgan, I

    2003-04-01

    The clinical lifetime of poly(methyl methacrylate) (PMMA) bone cement is considerably longer than the time over which it is convenient to perform creep testing. Consequently, it is desirable to be able to predict the long term creep behavior of bone cement from the results of short term testing. A simple method is described for prediction of long term creep using the principle of time-temperature equivalence in polymers. The use of the method is illustrated using a commercial acrylic bone cement. A creep strain of approximately 0.6% is predicted after 400 days under a constant flexural stress of 2 MPa. The temperature range and stress levels over which it is appropriate to perform testing are described. Finally, the effects of physical aging on the accuracy of the method are discussed and creep data from aged cement are reported.

  4. Influence of HAp on the polymerization processes of a possible radioactive bone cement

    Energy Technology Data Exchange (ETDEWEB)

    Montaño, Carlos J.; Campos, Tarcísio P.R., E-mail: carlmont@ucm.es, E-mail: tprcampos@yahoo.com.br [Universidade Federal de Minas Gerais (UFMG), Belo Horizonte (Brazil). Dept. de Engenharia Nuclear. Lab. de Radiações Ionizantes; Silva, Adolfo H.M.; Araujo, Maria H., E-mail: adolfohmoraes@ufmg.br, E-mail: mharaujo1993@gmail.com [Universidade Federal de Minas Gerais (RMN/UFMG), Belo Horizonte (Brazil). Dept. de Ressonância Magnética Nuclear

    2017-07-01

    Polymethylmethacrylate PMMA is an acrylic that has been already proposed as a composite to adhere together the fractured bone structures. Subsequently, augmentation bone cements have incorporated Calcium Biophosphonates as vital part of its components to increase the biocompatibility with osseous tissues. Minimally invasive percutaneous techniques such as Vertebroplasty and Kyphoplasty have been developed to reduce surgical impact on patients, but in turn have been reported undesirable effects as extravasation of the cement outside of the planning target volume due to the compression of the internal bone fluids or other tissues. An in situ variable that helps favoring of the PMMA polymerization process is the temperature; however, it may bring deleterious effects. On the methodology, an assay was addressed varying the Hydroxyapatite HAp concentration. Also the cement processing was modified by setting water as a vehicle for particle dispersion. The ratios of HAp/PMMA concentrations were: 0.00000, 0.02167, 0.09062, 0.16619 and 0.50000 mixed in PMMA and liquid catalyst and monomer. The thermal profiles were measured during polymerization and analyzed. Nuclear magnetic resonance NMR analysis was carried out on the polymerization process in an aqueous state to monitor the H-H{sub 2}O proton signal. As results, an increasing in the cement hardness time was found in the proportion of the HAp concentration. The highest τ polymerization time was found for the x{sub 5} concentration and the signal from the water trapped in the HAp amorphous lattice was determined around ∼5 ppm in the {sup 1}H NMR spectra. (author)

  5. Influence of HAp on the polymerization processes of a possible radioactive bone cement

    International Nuclear Information System (INIS)

    Montaño, Carlos J.; Campos, Tarcísio P.R.; Silva, Adolfo H.M.; Araujo, Maria H.

    2017-01-01

    Polymethylmethacrylate PMMA is an acrylic that has been already proposed as a composite to adhere together the fractured bone structures. Subsequently, augmentation bone cements have incorporated Calcium Biophosphonates as vital part of its components to increase the biocompatibility with osseous tissues. Minimally invasive percutaneous techniques such as Vertebroplasty and Kyphoplasty have been developed to reduce surgical impact on patients, but in turn have been reported undesirable effects as extravasation of the cement outside of the planning target volume due to the compression of the internal bone fluids or other tissues. An in situ variable that helps favoring of the PMMA polymerization process is the temperature; however, it may bring deleterious effects. On the methodology, an assay was addressed varying the Hydroxyapatite HAp concentration. Also the cement processing was modified by setting water as a vehicle for particle dispersion. The ratios of HAp/PMMA concentrations were: 0.00000, 0.02167, 0.09062, 0.16619 and 0.50000 mixed in PMMA and liquid catalyst and monomer. The thermal profiles were measured during polymerization and analyzed. Nuclear magnetic resonance NMR analysis was carried out on the polymerization process in an aqueous state to monitor the H-H 2 O proton signal. As results, an increasing in the cement hardness time was found in the proportion of the HAp concentration. The highest τ polymerization time was found for the x 5 concentration and the signal from the water trapped in the HAp amorphous lattice was determined around ∼5 ppm in the 1 H NMR spectra. (author)

  6. ULTRA-LIGHTWEIGHT CEMENT

    International Nuclear Information System (INIS)

    Fred Sabins

    2001-01-01

    The objective of this project is to develop an improved ultra-lightweight cement using ultralight hollow glass spheres (ULHS). Work reported herein addresses Task 1: Assess Ultra-Lightweight Cementing Problems and Task 3: Test Ultra-Lightweight Cements. Results reported this quarter include a review and summary of Halliburton Energy Services (HES) and BJ Services historical performance data for lightweight cement applications. These data are analyzed and compared to ULHS cement and foamed cement performances. Similar data is expected from Schlumberger, and an analysis of this data will be completed in the following phases of the project. Quality control testing of materials used to formulate ULHS cements in the laboratory was completed to establish baseline material performance standards. A testing protocol was developed employing standard procedures as well as procedures tailored to evaluate ULHS and foamed cement. This protocol is presented and discussed. Results of further testing of ULHS cements are presented along with an analysis to establish cement performance design criteria to be used during the remainder of the project. Finally, a list of relevant literature on lightweight cement performance is compiled for review during the next quarter

  7. ULTRA-LIGHTWEIGHT CEMENT

    International Nuclear Information System (INIS)

    Fred Sabins

    2001-01-01

    The objective of this project is to develop an improved ultra-lightweight cement using ultra-lightweight hollow glass spheres (ULHS). Work reported herein addresses Task 1: Assess Ultra-Lightweight Cementing Issues, Task 2: Review Russian Ultra-Lightweight Cement Literature, Task 3: Test Ultra-Lightweight Cements, and Task 8: Develop Field ULHS Cement Blending and Mixing Techniques. Results reported this quarter include: preliminary findings from a literature review focusing on problems associated with ultra-lightweight cements; summary of pertinent information from Russian ultra-lightweight cement literature review; laboratory tests comparing ULHS slurries to foamed slurries and sodium silicate slurries for two different applications; and initial laboratory studies with ULHS in preparation for a field job

  8. Production of bone cement composites: effect of fillers, co-monomer and particles properties

    Energy Technology Data Exchange (ETDEWEB)

    Santos Junior, J.G.F.; Melo, P.A.; Pinto, J.C., E-mail: jjunior@peq.coppe.ufrj.b, E-mail: melo@peq.coppe.ufrj.b, E-mail: pinto@peq.coppe.ufrj.b [Coordenacao dos Programas de Pos-Graduacao de Engenharia. (PEQ/COPPE/UFRJ), RJ (Brazil). Programa de Engenharia Quimica; Pita, V.J.R.R., E-mail: vjpita@ima.ufrj.b [Universidade Federal do Rio de Janeiro (IMA/UFRJ), RJ (Brazil). Inst. de Macromoleculas Eloisa Mano; Nele, M. [Universidade Federal do Rio de Janeiro (EQ/UFRJ), RJ (Brazil). Escola de Quimica

    2011-04-15

    Artificial bone cements (BCs) based on poly(methyl methacrylate) (PMMA) powders and methyl methacrylate (MMA) liquid monomer also present in their formulation small amounts of other substances, including a chemical initiator compound and radiopaque agents. Because inadequate mixing of the recipe components during the manufacture of the bone cement may compromise the mechanical properties of the final pieces, new techniques to incorporate the fillers into the BC and their effect upon the mechanical properties of BC pieces were investigated in the present study. PMMA powder composites were produced in situ in the reaction vessel by addition of X-ray contrasts to the reacting MMA mixture. It is shown that this can lead to much better mechanical properties of test pieces, when compared to standard bone cement formulations, because enhanced dispersion of the radiopaque agents can be achieved. Moreover, it is shown that the addition of hydroxyapatite (HA) and acrylic acid (AA) to the bone cement recipe can be beneficial for the mechanical performance of the final material. It is also shown that particle morphology can exert a tremendous effect upon the performance of test pieces, indicating that the suspension polymerization step should be carefully controlled when optimization of the bone cement formulation is desired. (author)

  9. Production of bone cement composites: effect of fillers, co-monomer and particles properties

    Directory of Open Access Journals (Sweden)

    J. G. F. Santos Jr.

    2011-06-01

    Full Text Available Artificial bone cements (BCs based on poly(methyl methacrylate (PMMA powders and methyl methacrylate (MMA liquid monomer also present in their formulation small amounts of other substances, including a chemical initiator compound and radiopaque agents. Because inadequate mixing of the recipe components during the manufacture of the bone cement may compromise the mechanical properties of the final pieces, new techniques to incorporate the fillers into the BC and their effect upon the mechanical properties of BC pieces were investigated in the present study. PMMA powder composites were produced in-situ in the reaction vessel by addition of X-ray contrasts to the reacting MMA mixture. It is shown that this can lead to much better mechanical properties of test pieces, when compared to standard bone cement formulations, because enhanced dispersion of the radiopaque agents can be achieved. Moreover, it is shown that the addition of hydroxyapatite (HA and acrylic acid (AA to the bone cement recipe can be beneficial for the mechanical performance of the final material. It is also shown that particle morphology can exert a tremendous effect upon the performance of test pieces, indicating that the suspension polymerization step should be carefully controlled when optimization of the bone cement formulation is desired.

  10. UVO radiation effects on carbon nanotube/PMMA composites and their neutron reflectivity measurements

    International Nuclear Information System (INIS)

    Najafi, Ebi; Koo, J. S.; Shin, K. W.

    2003-01-01

    Carbon nanotube(CNT)-Poly(methyl methacrylate)(PMMA) nanocomposite thin films have been studied. By irradiation of short wavelength ultraviolet(UV) light with ozone, the surface modification and stripping effects on their CNT/PMMA thin films was studied as a function of weight % of CNT in PMMA matrices. The experimental evidence indicates that the presence of CNT in PMMA matrix lowers significantly the stripping rate of the composites. In addition, changes of the rheological properties (i.e. diffusion coefficient) of PMMA molecules due to the presence of CNTs were also studied, in order to determine the microscopic interaction between diffusion coefficients of PMMA with and without CNTs was minimal

  11. Investigation of the histology and interfacial bonding between carbonated hydroxyapatite cement and bone

    International Nuclear Information System (INIS)

    Mao Keya; Hao Libo; Tang Peifu; Wang Zheng; Wen Ning; Du Mingkui; Wang Jifang; Wang Yan; Yang Yun; Li Jiangtao

    2009-01-01

    An ideal bone implant should facilitate the formation of a new bone layer as an osteo-integrated interface between bone and the implanted biomaterials. In the present work, the interface between carbonated hydroxyapatite (CHA) cement and bone was evaluated by interfacial bonding strength measurements and histological characterizations. CHA cement was implanted into a mongrel dog's femoral supracondylar and below the tibial plateau area, and was then tested ex vivo by, respectively, detaching and pullout experiments. Polymethylmethacrylate (PMMA) was used as a control. CHA cement could be directly injected and solidified in situ to repair bone defects. Histology results showed that CHA bonded with bone through gradual remodeling and was replaced by new bone tissue, which is an attribute for excellent biocompatibility. The interfacial bonding strength increased with implantation time. After 16 weeks implantation, the measured detaching force and the pullout force between CHA and bone were 281 ± 16 N and 512.5 ± 14.5 N, respectively. These values were several times higher compared to 5 days implantation. In contrast, the control showed a fibrous microstructure between PMMA and bone, and the detaching force and the pullout force decreased with implantation time. The results strongly suggest that CHA can form a better osteo-integrated interface compared to PMMA, and could be used as an ideal biomaterial for bone defect repair.

  12. Tribological and mechanical investigation of acrylic-based nanocomposite coatings reinforced with PMMA-grafted-MWCNT

    Energy Technology Data Exchange (ETDEWEB)

    Al-Kawaz, A. [UPR22/CNRS, Institut Charles Sadron, Université de Strasbourg, 23 Rue du Loess, BP 84047, F-67034 Strasbourg Cedex 2 (France); Rubin, A., E-mail: anne.rubin@ics-cnrs.unistra.fr [UPR22/CNRS, Institut Charles Sadron, Université de Strasbourg, 23 Rue du Loess, BP 84047, F-67034 Strasbourg Cedex 2 (France); Badi, N.; Blanck, C.; Jacomine, L. [UPR22/CNRS, Institut Charles Sadron, Université de Strasbourg, 23 Rue du Loess, BP 84047, F-67034 Strasbourg Cedex 2 (France); Janowska, I.; Pham-Huu, C. [Institute of Chemistry and Processes for Energy, Environment and Health (UMR 7515) CNRS - University of Strasbourg, 25 Rue Becquerel Strasbourg, 67087 Cedex 08 (France); Gauthier, C. [UPR22/CNRS, Institut Charles Sadron, Université de Strasbourg, 23 Rue du Loess, BP 84047, F-67034 Strasbourg Cedex 2 (France)

    2016-06-01

    The chemical functionalization of carbon nanotubes (CNTs) could improve their chemical compatibility. Poly(methyl methacrylate) (PMMA)-functionalized multi-walled carbon nanotubes (MWCNTs) are prepared by in situ atom transfer radical polymerization (ATRP) using a “grafting from” approach. It allows the control of the thickness of the polymer layer grafted on MWCNTs from two parameters: the feed ratio of MMA to MWCNT, the volume fraction of solvent to MMA. This work compared the effect of several PMMA-grafted-MWNCT fillers embedded into a PMMA matrix, PMMA-grafted-MWCNT/PMMA, and obtained by solution mixing technique. We studied the tribological performances of 20 μm coatings of these nanocomposites deposited on neat PMMA. The percentage of embedded fillers is kept low to maintain the transparency of the PMMA. The coefficient of friction was found to relatively decrease with the increase of the weight fraction of polymer grafted to the surface of MWCNT. Moreover the elastic modulus also increased with increasing the weight fraction of PMMA coated MWCNT. - Highlights: • Synthesis of MWCNT-PMMA nanoparticles by ATRP “grafting from” approach. • PMMA-grafted-MWCNT/PMMA coatings with good mechanical properties. • High tribological performance of PMMA-grafted-MWCNT/PMMA coatings.

  13. PMMA to Polystyrene bonding for polymer based microfluidic systems

    KAUST Repository

    Fan, Yiqiang

    2013-03-29

    A thermal bonding technique for Poly (methylmethacrylate) (PMMA) to Polystyrene (PS) is presented in this paper. The PMMA to PS bonding was achieved using a thermocompression method, and the bonding strength was carefully characterized. The bonding temperature ranged from 110 to 125 C with a varying compression force, from 700 to 1,000 N (0.36-0.51 MPa). After the bonding process, two kinds of adhesion quantification methods were used to measure the bonding strength: the double cantilever beam method and the tensile stress method. The results show that the bonding strength increases with a rising bonding temperature and bonding force. The results also indicate that the bonding strength is independent of bonding time. A deep-UV surface treatment method was also provided in this paper to lower the bonding temperature and compression force. Finally, a PMMA to PS bonded microfluidic device was fabricated successfully. © 2013 Springer-Verlag Berlin Heidelberg.

  14. Dielectric properties of PMMA-SiO2 hybrid films

    KAUST Repository

    Morales-Acosta, M. D.; Quevedo-Ló pez, Manuel Angel Quevedo; Alshareef, Husam N.; Gnade, Bruce E.; Ramí rez-Bon, Rafael

    2010-01-01

    Organic-inorganic hybrid films were synthesized by a modified sol-gel process. PMMASiO2 films were prepared using methylmethacrylate (MMA), tetraethil-orthosilicate (TEOS) as silicon dioxide source, and 3-trimetoxi-silil-propil-methacrylate (TMSPM) as coupling agent. FTIR measurements were performed on the hybrid films to confirm the presence of PMMA-SiO2 bonding. In addition, metal-insulator-metal (MIM) devices were fabricated to study the dielectric constant of the films as function of frequency (1 KHz to 1 MHz). Electrical results show a weak trend of the dielectric constant of the hybrid films with MMA molar ratio. More importantly, the PMMA-SiO2 hybrid films showed a higher dielectric constant than SiO2 and PMMA layers, which is likely due to the presence of additional C-O-C bond. © (2010) Trans Tech Publications.

  15. Dielectric properties of PMMA-SiO2 hybrid films

    KAUST Repository

    Morales-Acosta, M. D.

    2010-03-01

    Organic-inorganic hybrid films were synthesized by a modified sol-gel process. PMMASiO2 films were prepared using methylmethacrylate (MMA), tetraethil-orthosilicate (TEOS) as silicon dioxide source, and 3-trimetoxi-silil-propil-methacrylate (TMSPM) as coupling agent. FTIR measurements were performed on the hybrid films to confirm the presence of PMMA-SiO2 bonding. In addition, metal-insulator-metal (MIM) devices were fabricated to study the dielectric constant of the films as function of frequency (1 KHz to 1 MHz). Electrical results show a weak trend of the dielectric constant of the hybrid films with MMA molar ratio. More importantly, the PMMA-SiO2 hybrid films showed a higher dielectric constant than SiO2 and PMMA layers, which is likely due to the presence of additional C-O-C bond. © (2010) Trans Tech Publications.

  16. PMMA/MWCNT nanocomposite for proton radiation shielding applications

    Science.gov (United States)

    Li, Zhenhao; Chen, Siyuan; Nambiar, Shruti; Sun, Yonghai; Zhang, Mingyu; Zheng, Wanping; Yeow, John T. W.

    2016-06-01

    Radiation shielding in space missions is critical in order to protect astronauts, spacecraft and payloads from radiation damage. Low atomic-number materials are efficient in shielding particle-radiation, but they have relatively weak material properties compared to alloys that are widely used in space applications as structural materials. However, the issues related to weight and the secondary radiation generation make alloys not suitable for space radiation shielding. Polymers, on the other hand, can be filled with different filler materials for reinforcement of material properties, while at the same time provide sufficient radiation shielding function with lower weight and less secondary radiation generation. In this study, poly(methyl-methacrylate)/multi-walled carbon nanotube (PMMA/MWCNT) nanocomposite was fabricated. The role of MWCNTs embedded in PMMA matrix, in terms of radiation shielding effectiveness, was experimentally evaluated by comparing the proton transmission properties and secondary neutron generation of the PMMA/MWCNT nanocomposite with pure PMMA and aluminum. The results showed that the addition of MWCNTs in PMMA matrix can further reduce the secondary neutron generation of the pure polymer, while no obvious change was found in the proton transmission property. On the other hand, both the pure PMMA and the nanocomposite were 18%-19% lighter in weight than aluminum for stopping the protons with the same energy and generated up to 5% fewer secondary neutrons. Furthermore, the use of MWCNTs showed enhanced thermal stability over the pure polymer, and thus the overall reinforcement effects make MWCNT an effective filler material for applications in the space industry.

  17. Evaluation of an injectable bioactive borate glass cement to heal bone defects in a rabbit femoral condyle model

    Energy Technology Data Exchange (ETDEWEB)

    Cui, Xu [Institute of Bioengineering and Information Technology Materials, Tongji University, Shanghai 200092 (China); Center for Human Tissues and Organs Degeneration, Shenzhen Institute of Advanced Technology, Chinese Academy of Science, Shenzhen 518055 (China); Huang, Wenhai [Institute of Bioengineering and Information Technology Materials, Tongji University, Shanghai 200092 (China); Zhang, Yadong, E-mail: zhangyadong6@126.com [Department of Spine Surgery, Shanghai East Hospital, School of Medicine, Tongji University, Shanghai 200120 (China); Huang, Chengcheng; Yu, Zunxiong; Wang, Lei; Liu, Wenlong; Wang, Ting [Center for Human Tissues and Organs Degeneration, Shenzhen Institute of Advanced Technology, Chinese Academy of Science, Shenzhen 518055 (China); Zhou, Jie; Wang, Hui; Zhou, Nai; Wang, Deping [Institute of Bioengineering and Information Technology Materials, Tongji University, Shanghai 200092 (China); Pan, Haobo, E-mail: hb.pan@siat.ac.cn [Center for Human Tissues and Organs Degeneration, Shenzhen Institute of Advanced Technology, Chinese Academy of Science, Shenzhen 518055 (China); Rahaman, Mohamed N., E-mail: rahaman@mst.edu [Department of Spine Surgery, Shanghai East Hospital, School of Medicine, Tongji University, Shanghai 200120 (China); Department of Materials Science and Engineering, Missouri University of Science and Technology, Rolla, MO 65409-0340 (United States)

    2017-04-01

    There is a need for synthetic biomaterials to heal bone defects using minimal invasive surgery. In the present study, an injectable cement composed of bioactive borate glass particles and a chitosan bonding solution was developed and evaluated for its capacity to heal bone defects in a rabbit femoral condyle model. The injectability and setting time of the cement in vitro decreased but the compressive strength increased (8 ± 2 MPa to 31 ± 2 MPa) as the ratio of glass particles to chitosan solution increased (from 1.0 g ml{sup −1} to 2.5 g ml{sup −1}). Upon immersing the cement in phosphate-buffered saline, the glass particles reacted and converted to hydroxyapatite, imparting bioactivity to the cement. Osteoblastic MC3T3-E1 cells showed enhanced proliferation and alkaline phosphatase activity when incubated in media containing the soluble ionic product of the cement. The bioactive glass cement showed a better capacity to stimulate bone formation in rabbit femoral condyle defects at 12 weeks postimplantation when compared to a commercial calcium sulfate cement. The injectable bioactive borate glass cement developed in this study could provide a promising biomaterial to heal bone defects by minimal invasive surgery. - Highlights: • New class of injectable bone cement composed of bioactive borate glass particles and chitosan bonding phase was created. • The cement is biocompatible and bioactive, and has a much lower temperature increase during setting than PMMA cement. • The cement has a more controllable degradation rate and higher strength over a longer time than calcium sulfate cement. • The cement showed a better ability to heal bone defects than calcium sulfate over a twelve-week implantation period.

  18. Incorporation of fluconazole in copolymer PMMA-g-PEG derivatives

    International Nuclear Information System (INIS)

    Silveira, B.M.; Santos, V.M.R. dos; Novack, K.M.; Lopes, S.A.

    2014-01-01

    The graft copolymer PMMA-g-PEG went through chemical transformations in its chain through acetylation, halogenation, methylation and esterification followed by hydrolysis reactions. Subsequently, the copolymer PMMA-g-PEG derivatives passed through the process of emulsification and incorporation of the drug fluconazole. Derivatives copolymers were characterized by infrared spectroscopy (FTIR), X-ray diffraction (XRD) and scanning electron microscopy (SEM) after incorporation in order to evaluate their effectiveness. The efficiency of incorporation was observed and it was also verified that the complexity of polymer chain influence in the incorporated fluconazole content. (author)

  19. Study of anisotropic mechanical properties for aeronautical PMMA

    Directory of Open Access Journals (Sweden)

    Wei Shang

    Full Text Available For the properties of polymer are relative to its structure, the main purpose of the present work is to investigate the mechanical properties of the aeronautical PMMA which has been treated by the directional tensile technology. Isodyne images reveal the stress state in directional PMMA. And then, an anisotropic mechanical model is established. Furthermore, all mechanical parameters are measured by the digital image correlation method. Finally, based on the anisotropic mechanical model and mechanical parameters, the FEM numerical simulation and experimental methods are applied to analyze the fracture mechanical properties along different directions.

  20. Printed wax masks for 254 nm deep-UV pattering of PMMA-based microfluidics

    KAUST Repository

    Fan, Yiqiang; Liu, Yang; Li, Huawei; Foulds, Ian G.

    2012-01-01

    This paper reports a new technique for masking deep-UV exposure of poly(methyl methacrylate) (PMMA) using a printed wax mask. This technique provides an inexpensive and bulk fabrication method for PMMA structures. The technique involves the direct

  1. The effect of cement on hip stem fixation: a biomechanical study.

    Science.gov (United States)

    Çelik, Talip; Mutlu, İbrahim; Özkan, Arif; Kişioğlu, Yasin

    2017-06-01

    This study presents the numerical analysis of stem fixation in hip surgery using with/without cement methods since the use of cement is still controversial based on the clinical studies in the literature. Many different factors such as stress shielding, aseptic loosening, material properties of the stem, surgeon experiences etc. play an important role in the failure of the stem fixations. The stem fixation methods, cemented and uncemented, were evaluated in terms of mechanical failure aspects using computerized finite element method. For the modeling processes, three dimensional (3D) femur model was generated from computerized tomography (CT) images taken from a patient using the MIMICS Software. The design of the stem was also generated as 3D CAD model using the design parameters taken from the manufacturer catalogue. These 3D CAD models were generated and combined with/without cement considering the surgical procedure using SolidWorks program and then imported into ANSYS Workbench Software. Two different material properties, CoCrMo and Ti6Al4V, for the stem model and Poly Methyl Methacrylate (PMMA) for the cement were assigned. The material properties of the femur were described according to a density calculated from the CT images. Body weight and muscle forces were applied on the femur and the distal femur was fixed for the boundary conditions. The calculations of the stress distributions of the models including cement and relative movements of the contacts examined to evaluate the effects of the cement and different stem material usage on the failure of stem fixation. According to the results, the use of cement for the stem fixation reduces the stress shielding but increases the aseptic loosening depending on the cement crack formations. Additionally, using the stiffer material for the stem reduces the cement stress but increases the stress shielding. Based on the results obtained in the study, even when taking the disadvantages into account, the cement usage

  2. PMMA-hydroxyapatite composite material retards fatigue failure of augmented bone compared to augmentation with plain PMMA: in vivo study using a sheep model.

    Science.gov (United States)

    Arabmotlagh, Mohammad; Bachmaier, Samuel; Geiger, Florian; Rauschmann, Michael

    2014-11-01

    Polymethylmethacrylate (PMMA) is the most commonly used void filler for augmentation of osteoporotic vertebral fracture, but the differing mechanical features of PMMA and osteoporotic bone result in overload and failure of adjacent bone. The aim of this study was to compare fatigue failure of bone after augmentation with PMMA-nanocrystalline hydroxyapatite (HA) composite material or with plain PMMA in a sheep model. After characterization of the mechanical properties of a composite material consisting of PMMA and defined amounts (10, 20, and 30% volume fraction) of HA, the composite material with 30% volume fraction HA was implanted in one distal femur of sheep; plain PMMA was implanted in the other femur. Native non-augmented bone served as control. Three and 6 months after implantation, the augmented bone samples were exposed to cyclic loading and the evolution of damage was investigated. The fatigue life was highest for the ovine native bone and lowest for bone-PMMA specimens. Bone-composite specimens showed significantly higher fatigue life than the respective bone-PMMA specimens in both 3- and 6-month follow-up groups. These results suggest that modification of mechanical properties of PMMA by addition of HA to approximate those of cancellous bone retards fatigue failure of the surrounding bone compared to augmented bone with plain PMMA. © 2014 Wiley Periodicals, Inc.

  3. Synthesis and magnetic properties of bulk transparent PMMA/Fe-oxide nanocomposites

    Science.gov (United States)

    Li, Shanghua; Qin, Jian; Fornara, Andrea; Toprak, Muhammet; Muhammed, Mamoun; Kim, Do Kyung

    2009-05-01

    PMMA/Fe-oxide nanocomposites are fabricated by a chemical method. Monodispersed Fe-oxide nanoparticles are well dispersed in the PMMA matrix by in situ polymerization, resulting in a bulk transparent polymeric nanocomposite. The magnetic behavior of the PMMA/Fe-oxide nanocomposites is investigated. The transparent PMMA/Fe-oxide nanocomposite has potentially interesting magneto-optic applications without compromising the advantages of a lightweight, noncorrosive polymeric material with very high transparency even for bulk samples.

  4. Synthesis and magnetic properties of bulk transparent PMMA/Fe-oxide nanocomposites

    International Nuclear Information System (INIS)

    Li Shanghua; Qin Jian; Fornara, Andrea; Toprak, Muhammet; Muhammed, Mamoun; Kim, Do Kyung

    2009-01-01

    PMMA/Fe-oxide nanocomposites are fabricated by a chemical method. Monodispersed Fe-oxide nanoparticles are well dispersed in the PMMA matrix by in situ polymerization, resulting in a bulk transparent polymeric nanocomposite. The magnetic behavior of the PMMA/Fe-oxide nanocomposites is investigated. The transparent PMMA/Fe-oxide nanocomposite has potentially interesting magneto-optic applications without compromising the advantages of a lightweight, noncorrosive polymeric material with very high transparency even for bulk samples.

  5. Glass transition temperature of PMMA/modified alumina nanocomposite: Molecular dynamic study

    OpenAIRE

    Mohammadi, Maryam; Davoodi, Jamal; Javanbakht, Mahdi; Rezaei, Hamidreza

    2017-01-01

    In this study, the effect of alumina and modified alumina nanoparticles in a PMMA/alumina nanocomposite was investigated. To attain this goal, the glass transition behavior of poly methyl methacrylate (PMMA), PMMA/alumina and PMMA/hydroxylated alumina nanocomposites were investigated by molecular dynamic simulations (MD). All the MD simulations were performed using the Materials Studio 6.0 software package of Accelrys. To obtain the glass transition temperature, the variation of density vs. t...

  6. MALDI-TOF MS/MS measurements of PMMA

    NARCIS (Netherlands)

    Becer, C.R.; Baumgaertel, A.; Gottschaldt, M.; Schubert, U.S.

    2008-01-01

    The polymer poly(Me methacrylate) (PMMA) was analyzed using the matrix-assisted laser desorption ionization time-of-flight mass spectrometry (MALDI-TOF MS) technique. The MALDI-TOF MS app. was coupled with a collision-induced dissocn. (CID) unit. The performance of the MALDI-TOF/TOF MS method in

  7. Characterization of advanced polymethylmethacrylate (PMMA) targets for TNSA laser irradiation

    Czech Academy of Sciences Publication Activity Database

    Torrisi, L.; Cutroneo, Mariapompea; Semián, Vladimír; Ceccio, G.

    2015-01-01

    Roč. 351, OCT (2015), s. 580-587 ISSN 0169-4332 R&D Projects: GA ČR(CZ) GBP108/12/G108; GA MŠk LM2011019 Institutional support: RVO:61389005 Keywords : PMMA * TNSA * ion acceleration * laser-generating plasma Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 3.150, year: 2015

  8. PMMA highlights the layering transition of PDMS in Langmuir films

    NARCIS (Netherlands)

    Bernardini, C.; Stoyanov, S.D.; Cohen Stuart, M.A.; Arnaudov, L.N.; Leermakers, F.A.M.

    2011-01-01

    We report a system consisting of a mixed Langmuir monolayer, made of water-insoluble, spreadable, fluid-like polymers polydimethylsiloxane (PDMS) and polymethylmethacrylate (PMMA) with a minority P(DMS-b-MMA) copolymer. We have performed both Langmuir trough pressure/area isotherm measurements and

  9. Memory and threshold switching in thin film PMMA polymer

    International Nuclear Information System (INIS)

    Rabah, K.V.O.

    1995-05-01

    Threshold switching between two impedance states have been observed at room temperature in a polymethylmethacrylate (PMMA) thin film sandwiched between two evaporated Al-metal electrodes. The cell's I-V characteristics were found to exhibit memory property. (author). 19 refs, 4 figs

  10. Proton beam writing of passive waveguides in PMMA

    International Nuclear Information System (INIS)

    Sum, T.C.; Bettiol, A.A.; Seng, H.L.; Rajta, I.; Kan, J.A. van; Watt, F.

    2003-01-01

    Symmetric y-branch buried channel waveguides in poly-methylmethacrylate (PMMA) were fabricated by proton beam writing using a focused sub-micron beam of 1.5 and 2.0 MeV protons with a dose ranging from 25 to 160 nC/mm 2 (i.e. ∼1.6 x 10 13 to 1.0 x 10 14 particles/cm 2 ) and beam currents of approximately 5-10 pA. The proton beam modifies the PMMA (i.e. changes the refractive index), forming buried channel waveguides near the end of range. The buried channel waveguides were end-coupled with monochromatic light (633 nm) and the transmitted intensity profiles were measured, indicating an intensity distribution of 0.45/0.55 from each branch. The surface compaction of the PMMA as a result of the irradiation for doses up to 160 nC/mm 2 was also investigated. From these investigations, the optimal fabrication conditions for proton beam writing of PMMA were established. Waveguides of arbitrary design can be easily fabricated using proton beam writing, making the technique ideal for the rapid prototyping of optical circuits

  11. Blue-shifted photoluminescence of Alq3 dispersed in PMMA

    Indian Academy of Sciences (India)

    Administrator

    Abstract. Alq3 is known to emit bright green light under UV excitation. Blue shift of the emission was reported in recent literature. This was ascribed to the presence of various isomers/crystallographic modifica- tions obtained through train sublimation. Here a blue shift was reported for Alq3 dispersed in PMMA. No iso-.

  12. Electrical conductivity of polyaniline doped PVC–PMMA polymer

    Indian Academy of Sciences (India)

    methyl methacrylate) (PMMA) thin films has been measured by studying the – characteristics at various temperatures in the range 323–363 K. The results are presented in the form of – characteristics and analysis has been made by ...

  13. 21 CFR 886.1385 - Polymethylmethacrylate (PMMA) diagnostic contact lens.

    Science.gov (United States)

    2010-04-01

    ... 21 Food and Drugs 8 2010-04-01 2010-04-01 false Polymethylmethacrylate (PMMA) diagnostic contact lens. 886.1385 Section 886.1385 Food and Drugs FOOD AND DRUG ADMINISTRATION, DEPARTMENT OF HEALTH AND... directly on the globe or cornea of the eye for diagnosis or therapy of intraocular abnormalities. (b...

  14. Advanced cementation concepts

    International Nuclear Information System (INIS)

    Howard, C.G.

    1989-10-01

    The purpose of this programme of work was to investigate whether improvements could be made to existing formulations for cement suitable for the immobilization of intermediate level radioactive waste. Two additives were selected, microsilica and limestone flour. Improvements to the cement were only slight. (author)

  15. Preparation of hydraulic cement

    Energy Technology Data Exchange (ETDEWEB)

    1921-08-28

    A process for the preparation of hydraulic cement by the use of oil-shale residues is characterized in that the oil-shale refuse is mixed with granular basic blast-furnace slag and a small amount of portland cement and ground together.

  16. Low force cementation.

    Science.gov (United States)

    Wilson, P R

    1996-07-01

    The marginal adaptation of full coverage restorations is adversely affected by the introduction of luting agents of various minimum film thicknesses during the cementation process. The increase in the marginal opening may have long-term detrimental effects on the health of both pulpal and periodontal tissues. The purpose of this study was to determine the effects of varying seating forces (2.5, 12.5, 25 N), venting, and cement types on post-cementation marginal elevation in cast crowns. A standardized cement space of 40 microns was provided between a machined gold crown and a stainless steel die. An occlusal vent was placed that could be opened or closed. The post-cementation crown elevation was measured, following the use of two commercially available capsulated dental cements (Phosphacap, and Ketac-cem Applicap). The results indicate that only the combination of Ketac-Cem Applicap and crown venting produced post-cementation crown elevation of less than 20 microns when 12.5 N seating force was used. Higher forces (25 N) and venting were required for comparable seating when using Phosphacap (19 microns). The amount of force required to allow maximum seating of cast crowns appears to be cement specific, and is reduced by effective venting procedures.

  17. Cementation process study

    International Nuclear Information System (INIS)

    Park, H.H.; Han, K.W.; Ahn, S.J.; Choi, K.S.; Lee, M.W.; Ryu, Y.K.

    1985-01-01

    In the cementation process study, in 1984, design of the waste treatment simulator was finished for the first step. We can experience not only the operation of solidification system but the design and construction of comming large scale plant through the design of cementation process. (Author)

  18. Polyaniline emeraldine base nanofibers as a radiostabilizing agent for PMMA

    International Nuclear Information System (INIS)

    Araujo, Patricia L.B.; Ferreira, Carlas C.; Araujo, Elmo S.

    2007-01-01

    Polyaniline (PANI) presents antioxidant and radical-scavenging properties. Substances having these characteristics are good candidates for radioprotecting agents. Some studies have also shown results pointing out to biocompatibility and biodegradability of PANI. These characteristics are desirable for substances in contact with biological tissues and have important implications for inclusion of PANI in physical mixtures with conventional radiosterilizable polymers. In this work, nanofibers of polyaniline emeraldine doped with (±)-camphor-10-sulfonic acid (PANI-(±)-CSA) were prepared by self-assembly method. Polyaniline emeraldine base (PANI-EB) nanofibers were obtained after dedoping with NH 4 OH and used as additives in films of commercial poly (methyl methacrylate) (PMMA). In order to assess possible radiostabilizing effects of PANI-EB and its aniline monomer (An) on the PMMA matrix, films containing 0.075 and 0.15% (wt/wt) of these substances were submitted to gamma irradiation from 25 to 75 kGy doses. Variation on viscosity-average molar mass (Mv) of the PMMA matrix at 25 kGy dose showed that samples containing An and PANI-EB nanofibers in amounts of 0.15% (wt/wt) underwent less degradation than control sample. When nanofibers were used as additives, no measurable variation of Mv could be detected in PMMA samples at this dose. At 75 kGy, all composites containing PANI-EB nanofibers underwent less degradation than control samples, suggesting that these additives are able to retain their action at doses higher than standard sterilization dose. These evidences show that PANI-EB nanofibers could be useful additives in commercial PMMA used in medical applications. FTIR spectroscopic characterization and scanning electron microscopy (SEM) of PANI samples were also performed. (author)

  19. In Vivo Evaluation of an Injectable Premixed Radiopaque Calcium Phosphate Cement

    Directory of Open Access Journals (Sweden)

    Jonas Åberg

    2011-01-01

    Full Text Available In this work a radiopaque premixed calcium phosphate cement (pCPC has been developed and evaluated in vivo. Radiopacity was obtained by adding 0–40 % zirconia to the cement paste. The effects of zirconia on setting time, strength and radiopacity were evaluated. In the in vivo study a 2 by 3.5 mm cylindrical defect in a rat vertebrae was filled with either the pCPC, PMMA or bone chips. Nano-SPECT CT analysis was used to monitor osteoblast activity during bone regeneration. The study showed that by adding zirconia to the cement the setting time becomes longer and the compressive strength is reduced. All materials evaluated in the in vivo study filled the bone defect and there was a strong osteoblast activity at the injury site. In spite of the osteoblast activity, PMMA blocked bone healing and the bone chips group showed minimal new bone formation. At 12 weeks the pCPC was partially resorbed and replaced by new bone with good bone ingrowth. The radiopaque pCPC may be considered to be used for minimal invasive treatment of vertebral fractures since it has good handling, radiopacity and allows healing of cancellous bone in parallel with the resorption of the cement.

  20. Study of mechanical behavior of PMMA in bending and after UV irradiation and gamma radiation; Estudo do comportamento mecanico do PMMA sob flexao apos irradiacao UV e gama

    Energy Technology Data Exchange (ETDEWEB)

    Todt, M.L.; Kienen, V.D.; Azevedo, E.C., E-mail: helunica@yahoo.com.br [Universidade Tecnologica Federal do Parana (UTFPR), Curitiba, PR (Brazil)

    2014-07-01

    PMMA is a polymer that has density similar to water and refractive index alike to glass. It has been used in the substitution to roofing tiles and coverages, affording to be exposed to UV radiation and gamma radiation. This paper had the objective to study the effect in the flexural proprieties of the PMMA exposed to these types of radiations and the evaluation of the wettability through a contact angle measurer. The PMMA specimens have been submitted to 1500 h of UVA radiation, 1500 h of UVC radiation and to 25kGy of gamma radiation. The results show that the PMMA. (author)

  1. Minimally Invasive Technique for PMMA Augmentation of Fenestrated Screws

    Directory of Open Access Journals (Sweden)

    Jan-Helge Klingler

    2015-01-01

    Full Text Available Purpose. To describe the minimally invasive technique for cement augmentation of cannulated and fenestrated screws using an injection cannula as well as to report its safety and efficacy. Methods. A total of 157 cannulated and fenestrated pedicle screws had been cement-augmented during minimally invasive posterior screw-rod spondylodesis in 35 patients from January to December 2012. Retrospective evaluation of cement extravasation and screw loosening was carried out in postoperative plain radiographs and thin-sliced triplanar computed tomography scans. Results. Twenty-seven, largely prevertebral cement extravasations were detected in 157 screws (17.2%. None of the cement extravasations was causing a clinical sequela like a new neurological deficit. One screw loosening was noted (0.6% after a mean follow-up of 12.8 months. We observed no cementation-associated complication like pulmonary embolism or hemodynamic insufficiency. Conclusions. The presented minimally invasive cement augmentation technique using an injection cannula facilitates convenient and safe cement delivery through polyaxial cannulated and fenestrated screws during minimally invasive screw-rod spondylodesis. Nevertheless, the optimal injection technique and design of fenestrated screws have yet to be identified. This trial is registered with German Clinical Trials DRKS00006726.

  2. A Study on the Effect of Nano Alumina Particles on Fracture Behavior of PMMA

    Directory of Open Access Journals (Sweden)

    Arezou Sezavar

    2015-04-01

    Full Text Available In the current research, the role of nano-sized alumina on deformation and fracture mechanism of Poly Methyl Methacrylate (PMMA was investigated. For this purpose, PMMA matrix nanocomposite reinforced with different wt% of alumina (i.e., 5, 10 and 15 were fabricated using the compression molding technique. Tensile properties of produced nanocomposites were studied using Zwick Z250 apparatus at cross head speed of about 5 mm/min. In order to specify the role of alumina nanoparticles on deformation and fracture mechanism of PMMA, microscopic evaluation was performed using scanning electron microscope (SEM. The achieved results prove that tensile properties of PMMA depend on alumina wt%. For example, addition of 15 wt% alumina to PMMA causes an increase of about 25% modulus of elasticity. Micrographs taken from the fracture surface of PMMA and its nanocomposites show deformation and fracture mechanism of PMMA changes as alumina is added to it.

  3. Crevice corrosion of biomedical alloys: a novel method of assessing the effects of bone cement and its chemistry.

    Science.gov (United States)

    Bryant, Michael; Hu, Xinming; Farrar, Richard; Brummitt, Ken; Freeman, Robert; Neville, Anne

    2013-07-01

    In this study, five commercially available poly(methyl methacrylate) PMMA bone cements were tested to investigate the effects of antibiotics on the severity of crevice corrosion. Bone cements with varying chemistry were also tested. A test method was developed in part reference to ASTM F746-04. Cylindrical specimens were fitted with a bone cement tapered collar, creating consistent crevice conditions. Crevice corrosion was then studied using potentiodynamic polarization techniques in 0.9% NaCl solution (pH7.4) at 37°C. Surface analyses using a light microscope and scanning electron microscopy were also conducted to investigate the surface morphology after accelerated electrochemical testing. Initial testing of commercially available bone cements indicated that different PMMA bone cements can affect the initiation and propagation mechanism of crevice corrosion. Further studies, utilising electrochemical and mass spectroscopy techniques, have identified that the addition of radiopaque agent and antibiotics affect the initiation mechanisms of 316L stainless steel, whilst significantly increasing the extent of propagation in CoCrMo alloys. Copyright © 2013 Wiley Periodicals, Inc.

  4. CT volumetry of intravertebral cement after kyphoplasty. Comparison of polymethylmethacrylate and calcium phosphate in a 12-month follow-up

    International Nuclear Information System (INIS)

    Libicher, M.; Noeldge, G.; Kauffmann, G.W.; Vetter, M.; Wolf, I.; Meinzer, H.P.; Kasperk, C.; Grafe, I.; Fonseca, K.D.; Meeder, P.J.; Hillmeier, J.

    2005-01-01

    This study was intended to measure the volume of intravertebral cement after balloon kyphoplasty with high resolution computed tomography (CT) and dedicated software. Volume changes of biocompatible calcium phosphate cement (CPC) were detected during a follow-up of 12 months. Measurements were compared with a control group of patients treated with polymethylmethacrylate (PMMA). Twenty-three vertebrae (14 CPC, 9 PMMA) of 12 patients were examined with CT using an identical imaging protocol. Dedicated software was used to quantify intravertebral cement volume in subvoxel resolution by analyzing each cement implant with a density-weighted algorithm. The mean volume reduction of CPC was 0.08 ml after 12 months, which corresponds to an absorption rate of 2 vol%. However, the difference did not reach significance level (P>0.05). The mean error estimate was 0.005 ml, indicating excellent precision of the method. CT volumetry appears a precise tool for measurement of intravertebral cement volume. CT volumetry offers the possibility of in vivo measurement of CPC resorption. (orig.)

  5. Modified pavement cement concrete

    Science.gov (United States)

    Botsman, L. N.; Ageeva, M. S.; Botsman, A. N.; Shapovalov, S. M.

    2018-03-01

    The paper suggests design principles of pavement cement concrete, which covers optimization of compositions and structures at the stage of mixture components selection due to the use of plasticizing agents and air-retaining substances that increase the viability of a concrete mixture. It also demonstrates advisability of using plasticizing agents together with air-retaining substances when developing pavement concrete compositions, which provides for the improvement of physical and mechanical properties of concrete and the reduction of cement binding agent consumption thus preserving strength indicators. The paper shows dependences of the main physical-mechanical parameters of concrete on cement consumption, a type and amount of additives.

  6. Radioactive waste cementation

    International Nuclear Information System (INIS)

    Soriano B, A.

    1996-01-01

    This research was carried out to develop the most adequate technique to immobilize low and medium-activity radioactive waste. different brands of national cement were used, portland and pozzolanic cement. Prismatic and cylindrical test tubes were prepared with different water/cement (W/C) relationship. Additives such a as clay and bentonite were added in some other cases. Later, the properties of these test tubes were evaluated. Properties such as: mechanical resistance, immersion resistance, lixiviation and porosity resistance. Cement with the highest mechanical resistance values, 62,29 MPa was pozzolanic cement for a W/C relationship of 0,35. It must be mentioned that the other types of cements reached a mechanical resistance over 10 MPa, a value indicated by the international standards for transportation and storage of low and medium-activity radioactive waste at a superficial level. However, in the case of immersion resistance, Sol cement (portland type I) with a W/C relationship of 0,35 reached a compression resistance over 61,92 MPa; as in the previous cases, the other cements reached a mechanical resistance > 10 MPa. Regarding porosity, working with W/C relationships = 0,35 0,40 and 0,45, without additives and with additives, the percentage of porosity found for all cements is lower than 40% percentage indicated by international standards. With regard to the lixiviation test, pozzolanic cement best retained Cesium-137 and Cobalt-60, and increased its advantages when bentonite was added, obtaining a lixiviation rate of 2,02 x E-6 cm/day. Sol cement also improved its properties when bentonite was added and obtained a lixiviation rate of 2,84 x E-6 cm/day for Cesium-137. However, Cobalt-60 is almost completely retained with the 3 types of cement with or without additives, reaching the limits indicated by the international standards for the lixiviation rate of beta-gamma emitter < 5,00E-4 cm/day. Characterizing the final product involves the knowledge of its

  7. Tympanoplasty with ionomeric cement

    DEFF Research Database (Denmark)

    Kjeldsen, A D; Grøntved, A M

    2000-01-01

    with isolated erosion of the long incus process have been treated with a new surgical technique in which the ossicular chain was rebuilt with ionomeric cement. The results in hearing performance (mean pure-tone average (PTA) 0.5, 1 and 2 kHz) were evaluated pre- and post-surgery, and compared to those...... of > 10 dB, in 4 there was a slight improvement and in 2 a decline. The difference was not statistically significant. Hearing improvement using ionomeric cement in type II tympanoplasty was satisfactory. Reconstruction of the ossicular chain with ionomeric cement is recommended, as the procedure is easy...

  8. Patterning of PMMA microfluidic parts using screen printing process

    Science.gov (United States)

    Ahari Kaleibar, Aminreza; Rahbar, Mona; Haiducu, Marius; Parameswaran, Ash M.

    2010-02-01

    An inexpensive and rapid micro-fabrication process for producing PMMA microfluidic components has been presented. Our proposed technique takes advantages of commercially available economical technologies such as the silk screen printing and UV patterning of PMMA substrates to produce the microfluidic components. As a demonstration of our proposed technique, we had utilized a homemade deep-UV source, λ=254nm, a silk screen mask made using a local screen-printing shop and Isopropyl alcohol - water mixture (IPA-water) as developer to quickly define the microfluidic patterns. The prototyped devices were successfully bonded, sealed, and the device functionality tested and demonstrated. The screen printing based technique can produce microfluidic channels as small as 50 micrometers quite easily, making this technique the most cost-effective, fairly high precision and at the same time an ultra economical plastic microfluidic components fabrication process reported to date.

  9. Vibration Properties of a Steel-PMMA Composite Beam

    OpenAIRE

    He, Yuyang; Jin, Xiaoxiong

    2015-01-01

    A steel-polymethyl methacrylate (steel-PMMA) beam was fabricated to investigate the vibration properties of a one-dimensional phononic crystal structure. The experimental system included an excitation system, a signal acquisition system, and a data analysis and processing system. When an excitation signal was exerted on one end of the beam, the signals of six response points were collected with acceleration sensors. Subsequent signal analysis showed that the beam was attenuated in certain fre...

  10. Preparation and Faraday rotation of Bi-YIG/PMMA nanocomposite

    Science.gov (United States)

    Fu, H. P.; Hong, R. Y.; Wu, Y. J.; Di, G. Q.; Xu, B.; Zheng, Y.; Wei, D. G.

    Bismuth-substituted yttrium iron garnet (Bi-YIG) nanoparticles (NPs) were prepared by coprecipitation and subsequent heating treatment. Thermal gravity-differential thermal analysis was performed to investigate the thermal behavior of the Bi-YIG precursors and to decide the best annealing temperature. Phase formation of garnet NPs was investigated by X-ray powder diffraction. The size of Bi-YIG NPs was investigated by transmission electron microscopy, and the magnetic properties of Bi-YIG NPs were measured using a vibrating sample magnetometer. The results show that the temperature needed for the transformation of Bi-YIG from the amorphous phase to the garnet phase decreases with increasing Bi content, and Bi-YIG NPs with sizes of 28-78 nm are obtained after heating treatment at 650-1000 °C. The saturation magnetization of Bi-YIG NPs increases as the Bi content increases. Moreover, the Faraday rotation of polymethyl methacrylate (PMMA) slices doped with Bi-YIG NPs was investigated. The results indicate that the angle of Faraday rotation increases with increasing Bi content in PMMA composites, and the maximum value of the figure of merit is 1.46°, which is comparable to the value of a sputtered film. The Bi-YIG NPs-doped PMMA slices are new promising materials for magneto-optical devices.

  11. Characterisation and optical vapour sensing properties of PMMA thin films

    Energy Technology Data Exchange (ETDEWEB)

    Capan, I. [Balikesir University, Science and Arts Faculty, Physics Department, 10100 Balikesir (Turkey)], E-mail: inci.capan@gmail.com; Tarimci, C. [Ankara University, Faculty of Engineering, Department of Engineering Physics, 06100, Tandogan, Ankara (Turkey); Hassan, A.K. [Sheffield Hallam University, Materials and Engineering Research Institute, City Campus, Pond Street, Sheffield S1 1WB (United Kingdom); Tanrisever, T. [Balikesir University, Science and Arts Faculty, Chemistry Department, 10100 Balikesir (Turkey)

    2009-01-01

    The present article reports on the characterisation of spin coated thin films of poly (methyl methacrylate) (PMMA) for their use in organic vapour sensing application. Thin film properties of PMMA are studied by UV-visible spectroscopy, atomic force microscopy and surface plasmon resonance (SPR) technique. Results obtained show that homogeneous thin films with thickness in the range between 6 and 15 nm have been successfully prepared when films were spun at speeds between 1000-5000 rpm. Using SPR technique, the sensing properties of the spun films were studied on exposures to several halohydrocarbons including chloroform, dichloromethane and trichloroethylene. Data from measured kinetic response have been used to evaluate the sensitivity of the studied films to the various analyte molecules in terms of normalised response (%) per unit concentration (ppm). The highest PMMA film sensitivity of 0.067 normalised response per ppm was observed for chloroform vapour, for films spun at 1000 rpm. The high film's sensitivity to chloroform vapour was ascribed mainly to its solubility parameter and molar volume values. Effect of film thickness on the vapour sensing properties is also discussed.

  12. the Danish cement industry

    OpenAIRE

    la Cour, Lisbeth Funding; Møllgård, Peter

    2001-01-01

    We test econometrically whether the sole Danish producer of cement holds a dominant position in the Danish market for (grey) cement. In import penetration tests, we find that its pricing and quantity decisions are independent of import price and quantity, implying that it can act to a considerable extent independently of its competitors. We also test whether it can act independently of its customers and find that its demand is inelastic with respect to its price. It thus holds a dominant posi...

  13. HDAC inhibitor-loaded bone cement for advanced local treatment of osteosarcoma and chondrosarcoma.

    Science.gov (United States)

    Tonak, Marcus; Becker, Marc; Graf, Claudine; Eckhard, Lukas; Theobald, Matthias; Rommens, Pol-Maria; Wehler, Thomas C; Proschek, Dirk

    2014-11-01

    The treatment of osteosarcoma, especially wide resection, is challenging. An additional local drug therapy after resection using anti-neoplastic bone cement (Polymethylmethacrylate (PMMA)) could help improve the outcome of therapy. In this study, we evaluated the effects of PMMA loaded with valproic acid (VPA) and suberoylanilide hydroxamic acid (SAHA) on the cell activity of a SaOs-2 cell culture, as well as the elution rate of the drugs out of the bone cement. In our experiments, we used the SaOs-2 osteosarcoma and the SW1353 chondrosarcoma cell line. Bone cement clots (5 g) were prepared and loaded with different drug concentrations of VPA (25 mg and 50 mg) and SAHA (1 mg, 2.5 mg and 5 mg). Two control groups were established, one with a native cement clot, the other with human mesenchymal stem cells, in order to evaluate toxicity on non tumor-cells. Cell activity was measured using an Alamar Blue assay on days 1, 2, 3, 4 and 7. The cement clots were additionally examined in a material testing unit for biomechanical and structural changes. Tumor cells showed a significant and complete reduction of activity under therapy with VPA and SAHA. Drug release of VPA was extensive between days 0 and 3 and decreased progressively to day 7. Cumulative drug concentration in the medium continuously increased. Biomechanical testing of the cement clots showed no differences in stability and architecture compared to the control group. SaOs-2 and SW1353 cells with medium from native cement clots without drug therapy presented a cell activity of 100% in all groups and during all measurements. Human mesenchymal stem cells were not significantly affected during therapy with VPA and low concentrations of SAHA. In contrast, cell activity of human mesenchymal stem cells was significantly reduced under therapy with higher concentrations of SAHA, with an approximately linear decrease between days 0-3 and a rapidly decreasing activity between days 4-7. A local cytotoxic therapy in the

  14. Bone-Cement: The New Medical Quick Fix

    Directory of Open Access Journals (Sweden)

    Dinesh Bhatia

    2010-01-01

    Full Text Available

    Bone Cement is being widely used in vertebroplasty, a minimally invasive surgical procedure to treat spinal fractures and collapsed vertebrae. It is being labeled as a concrete success in medical field. It is being used to treat fractures due to osteoporosis, menopause, steroids, hyperthyroidism and chronic obstructive pulmonary diseases.  In this technique a needle with bone cement (PMMA, polymethylmethacrylate is injected into the collapsed vertebra after administering local anesthesia to patient. It solidifies within few minutes and provides support to damaged bone resulting in relief to the patient. It also prevents the movement between different parts of the broken bone. Hence it requires a short hospital stay for the patient and the procedure can be performed with much ease and at significant lower costs. Patient can resume normal activity within a day or so. Bone cement is now being referred to as the quick medical fix material for early repair of fractures.

  15. Refractive index depth profile in PMMA due to proton irradiation

    International Nuclear Information System (INIS)

    Szilasi, S.Z.; Rajta, I.; Budai, J.; Toth, Z.; Petrik, P.; Baradacs, E.

    2006-01-01

    Complete text of publication follows. During Proton Beam Writing the beam damage causes chain scissioning in the polymer resist material (e.g. PMMA (Polymethyl methacrylate)), producing smaller molecular weight chains. Hydrogen implantation also takes place at the end of range. Compaction of the sample has been observed too, which means that the sample density becomes higher at the places where proton irradiation occurred. Furthermore, P-beam Writing has been successfully used to create buried channel waveguides in PMMA [1], since proton irradiation increases the refractive index. There are two ways of fabricating waveguides using P-beam Writing, one of them applies direct micromachining of the high refractive index core followed by the coating of a lower refractive index cladding layer. In this application the refractive indices of the substrate, the core and the cladding have to be known, which should be homogeneous within the whole structure. The other method allows producing buried waveguides. In this case proton beam writing is used to modify the refractive index along the ion path in the sample, where most of the ion energy is deposited near the end of range also known as the Bragg peak. For polymers 10 -3 refractive index change has been reported, which is usually sufficient for forming waveguides. Those measurements of the refractive index change have been performed by the refracted near field technique. In this work we used ellipsometry, in order to measure the optical parameters of the P-beam treated sample near the surface, and along the Bragg curve. Ellipsometry measures the change in the polarization state of light occurring during reflection. This change is related to the quality of the reflecting surface (i.e. the physical structure, layer thicknesses, optical constants, surface roughness, etc.). >From these measurements the refractive index and the extinction coefficient can be determined rather accurately, which makes ellipsometry a powerful tool

  16. Pre-clinical evaluation of the mechanical properties of a low-stiffness cement-injectable hip stem.

    Science.gov (United States)

    Eldesouky, Ibrahim; Harrysson, Ola; Marcellin-Little, Denis J; West, Harvey; El-Hofy, Hassan

    2017-11-01

    In total hip arthroplasty (THA), the femoral stem can be fixed with or without bone cement. Cementless stem fixation is recommended for young and active patients as it eliminates the risk of loss of fixation at the bone-cement and cement-implant interfaces. Cementless fixation, however, suffers from a relatively high early revision rate. In the current research, a novel low-stiffness hip stem was designed, fabricated and tested. The stem design provided the option to inject biodegradable bone cement that could enhance initial stem stability. The stem was made of Ti6Al4V alloy. The proximal portion of the stem was porous, with cubic cells. The stem was fabricated using electron beam melting (EBM) technology and tested in compression and bending. Finite-element analysis was used to evaluate stem performance under a dynamic load representing a stair descending cycle and compare it to the performance of a solid stem with similar geometry. The von Mises stresses and maximum principal strains generated within the bone increased after porous stem insertion compared to solid stem insertion. The low-modulus stem tested in this study has acceptable mechanical properties and generates strain patterns in bone that appear compatible with clinical use.

  17. The surface properties of PS/PMMA blends nanostructured polymeric layers

    International Nuclear Information System (INIS)

    Prosycevas, I.; Tamulevicius, S.; Guobiene, A.

    2004-01-01

    Solvent cast thin films of blends polystyrene (PS) and poly (methylmethacrylate) (PMMA) with nominal compositions ranging from 25/75 wt.%/v% (w/v) up to 75/25 w/v PS/PMMA with toluene as the mutual solvent on crystalline Si (100) and silica substrates has been studied. Films of PS and PMMA blends have been examined by atomic force microscopy (AFM) and ellipsometry. The blend films with less than 50% PMMA bulk concentration generally exhibit pitted surfaces; the pit size varies with film thickness and bulk composition. When the PMMA bulk concentration is greater than 50%, the film surface can be described as island-like phase-separated structure. The surface segregation and morphology are explained in terms of solubility of the two polymers in the solvent and rewetting of PMMA relative to PS

  18. Preparing patterned carbonaceous nanostructures directly by overexposure of PMMA using electron-beam lithography

    Energy Technology Data Exchange (ETDEWEB)

    Duan Huigao; Zhao Jianguo; Zhang Yongzhe; Xie Erqing [School of Physical Science and Technology, Lanzhou University, Lanzhou 730000 (China); Han Li [Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190 (China)], E-mail: duanhg@gmail.com, E-mail: xieeq@lzu.edu.cn

    2009-04-01

    The overexposure process of poly(methyl methacrylate) (PMMA) was studied in detail using electron-beam lithography. It was found that PMMA films could be directly patterned without development due to the electron-beam-induced collapse of PMMA macromolecular chains. By analyzing the evolution of surface morphologies and compositions of the overexposed PMMA films, it was also found that the transformation of PMMA from positive to negative resist was a carbonization process, so patterned carbonaceous nanostructures could be prepared directly by overexposure of PMMA using electron-beam lithography. This simple one-step process for directly obtaining patterned carbonaceous nanostructures has promising potential application as a tool to make masks and templates, nanoelectrodes, and building blocks for MEMS and nanophotonic devices.

  19. Characterization and bacterial anti-adherent effect on modified PMMA denture acrylic resin containing platinum nanoparticles

    OpenAIRE

    Nam, Ki-Young

    2014-01-01

    PURPOSE This study characterized the synthesis of a modified PMMA (Polymethyl methacrylate) denture acrylic loading platinum nanoparticles (PtN) and assessed its bacterial inhibitory efficacy to produce novel antimicrobial denture base material. MATERIALS AND METHODS Polymerized PMMA denture acrylic disc (20 mm × 2 mm) specimens containing 0 (control), 10, 50, 100 and 200 mg/L of PtN were fabricated respectively. The obtained platinum-PMMA nanocomposite (PtNC) was characterized by TEM (transm...

  20. Material properties and in vitro biocompatibility of a newly developed bone cement

    Directory of Open Access Journals (Sweden)

    Elke Mitzner

    2009-01-01

    Full Text Available In this study mechanical properties and biocompatibility (In Vitro of a new bone cement were investigated. A new platform technology named COOL is a variable composite of dissolved, chemically modified PMMA and different bioceramics. COOL cures at body temperature via a classical cementation reaction. Compressive strengths ranging from 3.6 ± 0.8 to 62.8 ± 1.3 MPa and bending strengths ranging from 9.9 ± 2.4 to 26.4 ± 3.0 MPa were achieved with different COOL formulations. Porosity varied between 31 and 43%. Varying the components of each formulation mechanical properties and porosity could be adjusted. In Vitro biocompatibility studies with primary human osteoblasts (pHOB in direct contact with different COOL formulations, did not reveal any signs of toxicity. In contrast to Refobacin® R, cells incubated with COOL showed similar density, viability and ALP activity compared to control, if specimen were added immediately to the cell monolayer after preparation. In conclusion, COOL has promising mechanical properties in combination with high biocompatibility In Vitro and combines different advantages of both CPCs and PMMA cements by avoiding some of the respective shortcomings.

  1. Cement for Oil Well Cementing Operations in Ghana

    African Journals Online (AJOL)

    Michael

    For Portland cement to qualify as oil well cement, the chemical and physical properties must meet ..... Reservoir Engineering, Stanford University,. Stanford, California, pp. ... Construction”, PhD Thesis, Kwame Nkrumah. University of Science ...

  2. ULTRA-LIGHTWEIGHT CEMENT

    Energy Technology Data Exchange (ETDEWEB)

    Fred Sabins

    2001-10-23

    The objective of this project is to develop an improved ultra-lightweight cement using ultra-lightweight hollow glass spheres (ULHS). Work reported herein addresses tasks performed in the fourth quarter as well as the other three quarters of the past year. The subjects that were covered in previous reports and that are also discussed in this report include: Analysis of field laboratory data of active cement applications from three oil-well service companies; Preliminary findings from a literature review focusing on problems associated with ultra-lightweight cements; Summary of pertinent information from Russian ultra-lightweight cement literature review; and Comparison of compressive strengths of ULHS systems using ultrasonic and crush methods Results reported from the fourth quarter include laboratory testing of ULHS systems along with other lightweight cement systems--foamed and sodium silicate slurries. These comparison studies were completed for two different densities (10.0 and 11.5 lb/gal) and three different field application scenarios. Additional testing included the mechanical properties of ULHS systems and other lightweight systems. Studies were also performed to examine the effect that circulation by centrifugal pump during mixing has on breakage of ULHS.

  3. A simulator study of adverse wear with metal and cement debris contamination in metal-on-metal hip bearings.

    Science.gov (United States)

    Halim, T; Clarke, I C; Burgett-Moreno, M D; Donaldson, T K; Savisaar, C; Bowsher, J G

    2014-03-01

    Third-body wear is believed to be one trigger for adverse results with metal-on-metal (MOM) bearings. Impingement and subluxation may release metal particles from MOM replacements. We therefore challenged MOM bearings with relevant debris types of cobalt-chrome alloy (CoCr), titanium alloy (Ti6Al4V) and polymethylmethacrylate bone cement (PMMA). Cement flakes (PMMA), CoCr and Ti6Al4V particles (size range 5 µm to 400 µm) were run in a MOM wear simulation. Debris allotments (5 mg) were inserted at ten intervals during the five million cycle (5 Mc) test. In a clean test phase (0 Mc to 0.8 Mc), lubricants retained their yellow colour. Addition of metal particles at 0.8 Mc turned lubricants black within the first hour of the test and remained so for the duration, while PMMA particles did not change the colour of the lubricant. Rates of wear with PMMA, CoCr and Ti6Al4V debris averaged 0.3 mm(3)/Mc, 4.1 mm(3)/Mc and 6.4 mm(3)/Mc, respectively. Metal particles turned simulator lubricants black with rates of wear of MOM bearings an order of magnitude higher than with control PMMA particles. This appeared to model the findings of black, periarticular joint tissues and high CoCr wear in failed MOM replacements. The amount of wear debris produced during a 500 000-cycle interval of gait was 30 to 50 times greater than the weight of triggering particle allotment, indicating that MOM bearings were extremely sensitive to third-body wear. Cite this article: Bone Joint Res 2015;4:29-37. ©2015 The British Editorial Society of Bone & Joint Surgery.

  4. Formation of hydrated layers in PMMA thin films in aqueous solution

    Energy Technology Data Exchange (ETDEWEB)

    Akers, Peter W. [School of Chemical Sciences, University of Auckland, Auckland (New Zealand); Nelson, Andrew R.J. [The Bragg Institute, Australian Nuclear Science and Technology Organisation, Menai, NSW (Australia); Williams, David E. [School of Chemical Sciences, University of Auckland, Auckland (New Zealand); MacDiarmid Institute of Advanced Materials and Nanotechnology, Wellington (New Zealand); McGillivray, Duncan J., E-mail: d.mcgillivray@auckland.ac.nz [School of Chemical Sciences, University of Auckland, Auckland (New Zealand); MacDiarmid Institute of Advanced Materials and Nanotechnology, Wellington (New Zealand)

    2015-10-30

    Graphical abstract: - Highlights: • Homogeneous thin PMMA films prepared on Si/SiOx substrates and measured in air and water. • Reproducible formation of highly hydrated layer containing 50% water at the PMMA/SiOx interface. • When heated the films swell at 50 °C without loss of material. • Upon re-cooling to 25 °C the surface roughens and material is lost. - Abstract: Neutron reflectometry (NR) measurements have been made on thin (70–150 Å) poly(methylmethacrylate) (PMMA) films on Si/SiOx substrates in aqueous conditions, and compared with parameters measured using ellipsometry and X-Ray reflectometry (XRR) on dry films. All techniques show that the thin films prepared using spin-coating techniques were uniform and had low roughness at both the silicon and subphase interfaces, and similar surface energetics to thicker PMMA films. In aqueous solution, NR measurements at 25 °C showed that PMMA forms a partially hydrated layer at the SiOx interface 10 Å under the film, while the bulk film remains intact and contains around 4% water. Both the PMMA film layer and the sublayer showed minimal swelling over a period of 24 h. At 50 °C, PMMA films in aqueous solution roughen and swell, without loss of PMMA material at the surface. After cooling back to 25 °C, swelling and roughening increases further, with loss of material from the PMMA layer.

  5. 3D-printed PMMA Preform for Hollow-core POF Drawing

    DEFF Research Database (Denmark)

    Zubel, M. G.; Fasano, Andrea; Woyessa, Getinet

    2016-01-01

    In this paper we report the first, to our knowledge, 3D-printed hollow-core poly(methyl methacrylate) (PMMA) preform for polymer optical fibre drawing. It was printed of commercial PMMA by means of fused deposition modelling technique. The preform was drawn to cane, proving good enough quality...... of drawing process and the PMMA molecular weight to be appropriate for drawing. This ascertains that the manufacturing process provides preforms suitable for hollow-core fibre drawing. The paper focuses on maximisation of transparency of PMMA 3D printouts by optimising printing process parameters: nozzle...... temperature, printing speed and infill...

  6. Study of mechanical behavior of PMMA in bending and after UV irradiation and gamma radiation

    International Nuclear Information System (INIS)

    Todt, M.L.; Kienen, V.D.; Azevedo, E.C.

    2014-01-01

    PMMA is a polymer that has density similar to water and refractive index alike to glass. It has been used in the substitution to roofing tiles and coverages, affording to be exposed to UV radiation and gamma radiation. This paper had the objective to study the effect in the flexural proprieties of the PMMA exposed to these types of radiations and the evaluation of the wettability through a contact angle measurer. The PMMA specimens have been submitted to 1500 h of UVA radiation, 1500 h of UVC radiation and to 25kGy of gamma radiation. The results show that the PMMA. (author)

  7. Formation of hydrated layers in PMMA thin films in aqueous solution

    International Nuclear Information System (INIS)

    Akers, Peter W.; Nelson, Andrew R.J.; Williams, David E.; McGillivray, Duncan J.

    2015-01-01

    Graphical abstract: - Highlights: • Homogeneous thin PMMA films prepared on Si/SiOx substrates and measured in air and water. • Reproducible formation of highly hydrated layer containing 50% water at the PMMA/SiOx interface. • When heated the films swell at 50 °C without loss of material. • Upon re-cooling to 25 °C the surface roughens and material is lost. - Abstract: Neutron reflectometry (NR) measurements have been made on thin (70–150 Å) poly(methylmethacrylate) (PMMA) films on Si/SiOx substrates in aqueous conditions, and compared with parameters measured using ellipsometry and X-Ray reflectometry (XRR) on dry films. All techniques show that the thin films prepared using spin-coating techniques were uniform and had low roughness at both the silicon and subphase interfaces, and similar surface energetics to thicker PMMA films. In aqueous solution, NR measurements at 25 °C showed that PMMA forms a partially hydrated layer at the SiOx interface 10 Å under the film, while the bulk film remains intact and contains around 4% water. Both the PMMA film layer and the sublayer showed minimal swelling over a period of 24 h. At 50 °C, PMMA films in aqueous solution roughen and swell, without loss of PMMA material at the surface. After cooling back to 25 °C, swelling and roughening increases further, with loss of material from the PMMA layer.

  8. A Simplified Method of Opacifying and Mixing Acrylic Cement for Percutaneous Vertebroplasty: A Clinical and In Vitro Study

    International Nuclear Information System (INIS)

    Teng Gaojun; He Shicheng; Deng Gang; Guo Jinhe; Fang Wen; Zhu Guangyu

    2005-01-01

    The objective of this study was to simplify the opacifying mixing process of the bone cement and contrast used for percutaneous vertebroplasty (PVP). We performed a biomechanical study of polymethyl methacrylate (PMMA) (Corinplast TM 3) using three different mixtures of PMMA, monomer, and contrast: group I, 2:1; group II, 3:2; group III, 3:2:1 ratio of powder/monomer/iodinated contrast (Omnipaque). In vitro biomechanical testing of ultimate compressive strength was carried out in all samples. Following the conclusion of a proper bone cement mixture regimen drawn from the in vitro study, PVP was performed in 125 patients: 58 with cancer, 12 with hemangioma, and 54 with osteoporotic fracture. The ultimate compressive strength in group III was decreased by 38% compared to groups II and I. Proper fluoroscopic visualization was achieved in all PVP procedures using this mixture. There were no major complications associated with injection of the cement mixture. Complete (CR) and partial response (PR) was obtained in 64% and 32.8%, respectively. No further vertebral collapse occurred during follow-up. The regimen using iodinated contrast for cement visualization during PVP provides a simple and convenient new method for mixing. Although the biomechanical strength is altered by the contrast medium added, it seems insignificant in clinical practice based on the authors' limited experience

  9. Radiative flux emitted by a burning PMMA slab

    International Nuclear Information System (INIS)

    Parent, G; Acem, Z; Collin, A; Berfroi, R; Boulet, P; Pizzo, Y; Mindykowski, P; Kaiss, A; Porterie, B

    2012-01-01

    The degradation of a PMMA sample has been studied based on experimental results obtained for the radiation emission by a burning slab. Observations of the infrared emission perpendicular to the plate, in the range where the optically thin flame is weakly emitting, indicate a plate temperature close to 680 K which is an indication on the surface temperature during the degradation process. Observations from the side allow a flame characterization without the plate emission superimposition. This is a promising way for evaluating data regarding the flame characteristics: temperature, gaz concentration and soot volumetric fraction.

  10. Concrete = aggregate, cement, water?

    International Nuclear Information System (INIS)

    Jelinek, J.

    1990-01-01

    Concrete for the Temelin nuclear power plant is produced to about 70 different formulae. For quality production, homogeneous properties of aggregates, accurate proportioning devices, technological discipline and systematic inspections and tests should be assured. The results are reported of measuring compression strength after 28 days for different concrete samples. The results of such tests allow reducing the proportion of cement, which brings about considerable savings. Reduction in cement quantities can also be achieved by adding ash to the concrete mixes. Ligoplast, a plasticizer addition is used for improving workability. (M.D). 8 figs

  11. Technology Roadmaps: Cement

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    2009-07-01

    To support its roadmap work focusing on key technologies for emissions reductions, the International Energy Agency (IEA) also investigated one particular industry: cement. Cement production includes technologies that are both specific to this industry and those that are shared with other industries (e.g., grinding, fuel preparation, combustion, crushing, transport). An industry specific roadmap provides an effective mechanism to bring together several technology options. It outlines the potential for technological advancement for emissions reductions in one industry, as well as potential cross-industry collaboration.

  12. Safety and feasibility of percutaneous vertebroplasty with radioactive {sup 153}Sm PMMA in an animal model

    Energy Technology Data Exchange (ETDEWEB)

    Lu Jun [Department of Radiotherapy, Xijing Hospital, Fourth Military Medical University, 15 West Changle Road, Xi' an 710032, Shaanxi Province (China); Deng Jinglan, E-mail: dengjinglan@gmail.com [Department of Nuclear Medicine, Xijing Hospital, Fourth Military Medical University, 15 West Changle Road, Xi' an 710032, Shaanxi Province (China); Zhao Haitao [Department of Radiology, Xijing Hospital, Fourth Military Medical University, 15 West Changle Road, Xi' an 710032, Shaanxi Province (China); Shi Mei [Department of Radiotherapy, Xijing Hospital, Fourth Military Medical University, 15 West Changle Road, Xi' an 710032, Shaanxi Province (China); Wang Jing [Department of Nuclear Medicine, Xijing Hospital, Fourth Military Medical University, 15 West Changle Road, Xi' an 710032, Shaanxi Province (China); Zhao Lina [Department of Radiotherapy, Xijing Hospital, Fourth Military Medical University, 15 West Changle Road, Xi' an 710032, Shaanxi Province (China)

    2011-05-15

    Purpose: We investigated the safety and feasibility of the combination of samarium-153-ethylenediamine tetramethylene phosphonate ({sup 153}Sm-EDTMP)-incorporated bone cement (BC) with percutaneous vertebroplasty (PVP) in dogs. Methods and materials: {sup 153}Sm-EDTMP-incorporated BC was prepared by combining solid {sup 153}Sm-EDTMP and polymethylmethacrylate (PMMA) immediately before PVP. It was then injected into the vertebrae of four healthy mongrel dogs (two males and two females) by PVP under CT guidance. Each dog was subjected to five PVP sessions at a {sup 153}Sm-EDTMP dose of 30-70 mCi. The suppressive effect of local injection of {sup 153}Sm-EDTMP on the hematopoietic system was evaluated through counting of peripheral blood cells. Distribution of {sup 153}Sm-EDTMP-incorporated BC and the status of tissues adjacent to injected vertebrae were evaluated with SPECT, CT and MRI. Histopathology was carried out to assess the influence of PVP on the vertebra and adjacent tissues at the microscopic level. Results: PVP was done successfully, and all dogs exhibited normal behavior and stable physical signs after procedures. {sup 153}Sm-EDTMP-incorporated BC was concentrated mainly in target vertebrae, and the peripheral blood cells remained within normal range. The spinal cord and tissues around BC did not exhibit signs of injury even when the dosage of {sup 153}Sm-EDTMP increased from 30 mCi to 70 mCi. Conclusion: A dose lower than 70 mCi of {sup 153}Sm is safe when it was injected into vertebrae. {sup 153}Sm-EDTMP-incorporated BC did not influence the effect of PVP. This means might strengthen anti-tumor activity locally for vertebra with osseous metastasis without damaging adjacent tissues.

  13. Reducing cement's CO2 footprint

    Science.gov (United States)

    van Oss, Hendrik G.

    2011-01-01

    The manufacturing process for Portland cement causes high levels of greenhouse gas emissions. However, environmental impacts can be reduced by using more energy-efficient kilns and replacing fossil energy with alternative fuels. Although carbon capture and new cements with less CO2 emission are still in the experimental phase, all these innovations can help develop a cleaner cement industry.

  14. Cement Mason's Curriculum. Instructional Units.

    Science.gov (United States)

    Hendirx, Laborn J.; Patton, Bob

    To assist cement mason instructors in providing comprehensive instruction to their students, this curriculum guide treats both the skills and information necessary for cement masons in commercial and industrial construction. Ten sections are included, as follow: related information, covering orientation, safety, the history of cement, and applying…

  15. Cementation of liquid radioactive waste

    International Nuclear Information System (INIS)

    Efremenkov, V.

    2004-01-01

    The cementation methods for immobilisation of radioactive wastes are discussed in terms of methodology, chemistry and properties of the different types of cements as well as the worldwide experience in this field. Two facilities for cementation - DEWA and MOWA - are described in details

  16. Cementing a wellbore using cementing material encapsulated in a shell

    Energy Technology Data Exchange (ETDEWEB)

    Aines, Roger D.; Bourcier, William L.; Duoss, Eric B.; Spadaccini, Christopher M.; Cowan, Kenneth Michael

    2016-08-16

    A system for cementing a wellbore penetrating an earth formation into which a pipe extends. A cement material is positioned in the space between the wellbore and the pipe by circulated capsules containing the cement material through the pipe into the space between the wellbore and the pipe. The capsules contain the cementing material encapsulated in a shell. The capsules are added to a fluid and the fluid with capsules is circulated through the pipe into the space between the wellbore and the pipe. The shell is breached once the capsules contain the cementing material are in position in the space between the wellbore and the pipe.

  17. Cementing a wellbore using cementing material encapsulated in a shell

    Energy Technology Data Exchange (ETDEWEB)

    Aines, Roger D.; Bourcier, William L.; Duoss, Eric B.; Floyd, III, William C.; Spadaccini, Christopher M.; Vericella, John J.; Cowan, Kenneth Michael

    2017-03-14

    A system for cementing a wellbore penetrating an earth formation into which a pipe extends. A cement material is positioned in the space between the wellbore and the pipe by circulated capsules containing the cement material through the pipe into the space between the wellbore and the pipe. The capsules contain the cementing material encapsulated in a shell. The capsules are added to a fluid and the fluid with capsules is circulated through the pipe into the space between the wellbore and the pipe. The shell is breached once the capsules contain the cementing material are in position in the space between the wellbore and the pipe.

  18. Comparison of Flexural Strength of Different CAD/CAM PMMA-Based Polymers.

    Science.gov (United States)

    Alp, Gülce; Murat, Sema; Yilmaz, Burak

    2018-01-28

    To compare the flexural strength of different computer-aided design/computer-aided manufacturing (CAD/CAM) poly(methyl methacrylate)-based (PMMA) polymers and conventional interim resin materials after thermocycling. Rectangular-shaped specimens (n = 15, for each material) (25 × 2 × 2 mm 3 ) were fabricated from 3 CAD/CAM PMMA-based polymers (Telio CAD [T]; M-PM-Disc [M]; Polident-PMMA [P]), 1 bis-acrylate composite resin (Protemp 4 [PT]), and 1 conventional PMMA (ArtConcept Artegral Dentine [C]) according to ISO 10477:2004 Standards (Dentistry-Polymer-Based Crown and Bridge Materials). The specimens were subjected to 10,000 thermocycles (5 to 55°C). Three-point flexural strength of the specimens was tested in a universal testing machine at a 1.0 mm/min crosshead speed, and the flexural strength data (σ) were calculated (MPa). The flexural strength values were statistically analyzed using 1-way ANOVA, and Tukey HSD post-hoc test for multiple comparisons (α = 0.05). Flexural strength values ranged between 66.1 ± 13.1 and 131.9 ± 19.8 MPa. There were significant differences among the flexural strengths of tested materials, except for between T and P CAD/CAM PMMA-based polymers (p > 0.05). CAD/CAM PMMA-based polymer M had the highest flexural strength and conventional PMMA had the lowest (p CAD/CAM PMMA-based T and P polymers had significantly higher flexural strength than the bis-acrylate composite resin (p CAD/CAM PMMA-based M (p CAD/CAM PMMA-based polymers was greater than the flexural strength of bis-acrylate composite resin, which had a greater flexural strength compared to conventional PMMA resin. © 2018 by the American College of Prosthodontists.

  19. The mechanical effect of the existing cement mantle on the in-cement femoral revision.

    LENUS (Irish Health Repository)

    Keeling, Parnell

    2012-08-01

    Cement-in-cement revision hip arthroplasty is an increasingly popular technique to replace a loose femoral stem which retains much of the original cement mantle. However, some concern exists regarding the retention of the existing fatigued and aged cement in such cement-in-cement revisions. This study investigates whether leaving an existing fatigued and aged cement mantle degrades the mechanical performance of a cement-in-cement revision construct.

  20. Evaluation relaxed volume of .sub.a-./sub.PMMA and .sub.a-./sub.PMMA/CB from heating

    Czech Academy of Sciences Publication Activity Database

    Hadač, J.; Slobodian, P.; Sáha, P.; Říha, Pavel

    2014-01-01

    Roč. 108, special issue 1 (2014), s. 50-58 ISSN 0009-2770 Grant - others:GA MŠk(CZ) EE.2.3.20.0104; GA MŠk(CZ) ED2.1.00/03.0111 Institutional research plan: CEZ:AV0Z20600510 Institutional support: RVO:67985874 Keywords : isobaric heating * physical aging * PMMA * volume relaxation * polymer/carbon black composite Subject RIV: BK - Fluid Dynamics Impact factor: 0.272, year: 2014 http://www.chemicke-listy.cz/docs/full/2014_s1_s50-s58.pdf

  1. Integration of a Graphite/PMMA CompositeElectrode into a Poly(methyl methacrylate) (PMMA) Substrate for Electrochemical Detection in Microchips

    Science.gov (United States)

    Regel, Anne; Lunte, Susan

    2013-01-01

    Traditional fabrication methods for polymer microchips, the bonding of two substrates together to form the microchip, can make the integration of carbon electrodes difficult. We have developed a simple and inexpensive method to integrate graphite/PMMA composite electrodes (GPCEs) into a PMMA substrate. These substrates can be bonded to other PMMA layers using a solvent-assisted thermal bonding method. The optimal composition of the GPCEs for electrochemical detection was determined using cyclic voltammetry with dopamine as a test analyte. Using the optimized GPCEs in an all-PMMA flow cell with flow injection analysis, it was possible to detect 50 nM dopamine under the best conditions. These electrodes were also evaluated for the detection of dopamine and catechol following separation by microchip electrophoresis (ME). PMID:23670816

  2. Viscoelastic-Viscoplastic Modelling of the Scratch Response of PMMA

    Directory of Open Access Journals (Sweden)

    G. Kermouche

    2013-01-01

    Full Text Available This paper aims at understanding how to model the time-dependent behavior of PMMA during a scratch loading at a constant speed and at middle strain levels. A brief experimental study is first presented, consisting of the analysis of microscratches carried out at various scratching velocities and normal loads. The loading conditions have been chosen in such a way that neither (viscoelasticity nor (viscoplasticity of the PMMA may be neglected a priori. The main analyzed parameter is the tip penetration depth measured during the steady state. Then, a finite element model is used to investigate the potential of classical elastic-viscoplastic constitutive models to reproduce these experimental results. It is mainly shown that these models lead to unsatisfying results. More specifically, it is pointed out here that the time-independent Young modulus used in such models is not suitable. To take into account this feature, a viscoelastic-viscoplastic model based on the connection in series of a viscoelastic part with a viscoplastic part is proposed. It is shown that it leads to more acceptable results, which points out the importance of viscoelasticity in the scratch behavior of solid polymers.

  3. Modification of PMMA/graphite nanocomposites through ion beam technique

    Science.gov (United States)

    Singhal, Prachi; Rattan, Sunita; Avasthi, Devesh Kumar; Tripathi, Ambuj

    2013-08-01

    Swift heavy ion (SHI) irradiation is a special technique for inducing physical and chemical modifications in bulk materials. In the present work, the SHI hs been used to prepare nanocomposites with homogeneously dispersed nanoparticles. The nanographite was synthesized from graphite using the intercalation-exfoliation method. PMMA Poly(methyl methacrylate)/graphite nanocomposites have been synthesized by in situ polymerization. The prepared PMMA/graphite nanocomposite films were irradiated with SHI irradiation (Ni ion beam, 80 MeV and C ion beam, 50 MeV) at a fluence of 1×1010 to 3×1012 ions/cm2. The nanocomposite films were characterized by scanning electron microscope (SEM) and were evaluated for their electrical and sensor properties. After irradiation, significant changes in surface morphology of nanocomposites were observed as evident from the SEM images, which show the presence of well-distributed nanographite platelets. The irradiated nanocomposites exhibit better electrical and sensor properties for the detection of nitroaromatics with marked improvement in sensitivity as compared with unirradiated nanocomposites.

  4. Influence of temperature in polymethylmethacrylate (PMMA) dosemeters response

    International Nuclear Information System (INIS)

    Napolitano, Celia Marina; Ferreira, Danilo Cardenuto; Camargo, Fabio de; Goncalves, Josemary Angelica Correa; Tobias, Carmen Cecilia Bueno

    2005-01-01

    The use of gamma irradiation sterilization processes in medical products and food preservation has encouraged the emergence of industrial facilities responsible for generation of doses as high as a few dozen kGy. The characterization of this radiation field requires the use of dosimeters with high spatial resolution, high resistance to radiation damage, maintenance of information absorbed doses at a time suitable for the analysis and processing of data, easy handling, etc. The dosimeters that meet most of these requirements are based on polymethylmethacrylate (PMMA) with dyes sensitive to radiation. The dose that can be measured with these dosimeters extends from 100Gy to 50kGy, with the estimated accuracies by manufacturers from 2 to 3%. However, in practice, there are procedures that require irradiation in different conditions of temperature, which results in changes in the response of the dosimeter. This way, considering the irradiations made in the center of radiation technology of Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP - Brazilian nuclear and energy research institute -, has studied the effect of temperature on the response of routine dosimeters PMMA type where the operational characteristics of Gammachrome YR dosimeters type and Red Perspex are being investigated respect to temperature and dose, whose results will be presented in this paper

  5. Hypothermic manipulation of bone cement can extend the handling time during vertebroplasty

    Directory of Open Access Journals (Sweden)

    Lai Po-Liang

    2012-10-01

    Full Text Available Abstract Background Polymethylmethacrylate (PMMA is commonly used for clinical applications. However, the short handling time increases the probability of a surgeon missing the crucial period in which the cement maintains its ideal viscosity for a successful injection. The aim of this article was to illustrate the effects a reduction in temperature would have on the cement handling time during percutaneous vertebroplasty. Methods The injectability of bone cement was assessed using a cement compressor. By twisting the compressor, the piston transmits its axial load to the plunger, which then pumps the bone cement out. The experiments were categorized based on the different types of hypothermic manipulation that were used. In group I (room temperature, sham group, the syringes were kept at 22°C after mixing the bone cement. In group 2 (precooling the bone cement and the container, the PMMA powder and liquid, as well as the beaker, spatula, and syringe, were stored in the refrigerator (4°C overnight before mixing. In group 3 (ice bath cooling, the syringes were immediately submerged in ice water after mixing the bone cement at room temperature. Results The average liquid time, paste time, and handling time were 5.1 ± 0.7, 3.4 ± 0.3, and 8.5 ± 0.8 min, respectively, for group 1; 9.4 ± 1.1, 5.8 ± 0.5, and 15.2 ± 1.2 min, respectively, for group 2; and 83.8 ± 5.2, 28.8 ± 6.9, and 112.5 ± 11.3 min, respectively, for group 3. The liquid and paste times could be increased through different cooling methods. In addition, the liquid time (i.e. waiting time for ice bath cooling was longer than for that of the precooling method (p Conclusions Both precooling (i.e. lowering the initial temperature and ice bath cooling (i.e. lowering the surrounding temperature can effectively slow polymerization. Precooling is easy for clinical applications, while ice bath cooling might be more suitable for multiple-level vertebroplasty. Clinicians can take

  6. Hypothermic manipulation of bone cement can extend the handling time during vertebroplasty.

    Science.gov (United States)

    Lai, Po-Liang; Tai, Ching-Lung; Chu, I-Ming; Fu, Tsai-Sheng; Chen, Lih-Huei; Chen, Wen-Jer

    2012-10-16

    Polymethylmethacrylate (PMMA) is commonly used for clinical applications. However, the short handling time increases the probability of a surgeon missing the crucial period in which the cement maintains its ideal viscosity for a successful injection. The aim of this article was to illustrate the effects a reduction in temperature would have on the cement handling time during percutaneous vertebroplasty. The injectability of bone cement was assessed using a cement compressor. By twisting the compressor, the piston transmits its axial load to the plunger, which then pumps the bone cement out. The experiments were categorized based on the different types of hypothermic manipulation that were used. In group I (room temperature, sham group), the syringes were kept at 22°C after mixing the bone cement. In group 2 (precooling the bone cement and the container), the PMMA powder and liquid, as well as the beaker, spatula, and syringe, were stored in the refrigerator (4°C) overnight before mixing. In group 3 (ice bath cooling), the syringes were immediately submerged in ice water after mixing the bone cement at room temperature. The average liquid time, paste time, and handling time were 5.1 ± 0.7, 3.4 ± 0.3, and 8.5 ± 0.8 min, respectively, for group 1; 9.4 ± 1.1, 5.8 ± 0.5, and 15.2 ± 1.2 min, respectively, for group 2; and 83.8 ± 5.2, 28.8 ± 6.9, and 112.5 ± 11.3 min, respectively, for group 3. The liquid and paste times could be increased through different cooling methods. In addition, the liquid time (i.e. waiting time) for ice bath cooling was longer than for that of the precooling method (p < 0.05). Both precooling (i.e. lowering the initial temperature) and ice bath cooling (i.e. lowering the surrounding temperature) can effectively slow polymerization. Precooling is easy for clinical applications, while ice bath cooling might be more suitable for multiple-level vertebroplasty. Clinicians can take advantage of the improved injectability without any

  7. Effect of barium-coated halloysite nanotube addition on the cytocompatibility, mechanical and contrast properties of poly(methyl methacrylate) cement

    OpenAIRE

    Jammalamadaka U; Tappa K; Weisman JA; Nicholson JC; Mills DK

    2017-01-01

    Uday Jammalamadaka,1 Karthik Tappa,1 Jeffery A Weisman,1 James Connor Nicholson,2 David K Mills1,3 1Center for Biomedical Engineering and Rehabilitation Science, 2Nanosystems Engineering, 3The School of Biological Sciences, Louisiana Tech University, Ruston, LA, USA Abstract: Halloysite nanotubes (HNTs) were investigated as a platform for tunable nanoparticle composition and enhanced opacity in poly(methyl methacrylate) (PMMA) bone cement. Halloysite has been widely used to increase ...

  8. Complex Permittivity of Polyaniline-Carbon Nanotube and Nanofibre Composites in the X-band. PMMA Composites

    National Research Council Canada - National Science Library

    Makeiff, Darren A; Huber, Trisha; Saville, Paul

    2005-01-01

    ... the complex permittivity from transmission-reflection waveguide measurements in the X-band (8-12 GHz). PMMA composites containing PAni-MWNT or PAni-CNFs poorer, while PMMA composites containing PAni and MWNT mixed ex situ...

  9. Synthesis and characterization of PMMA/clay nanocomposites prepared by in situ polymerization assisted by sonication

    International Nuclear Information System (INIS)

    Prado, Bruna R.; Bartoli, Julio R.; Ito, Edson N.

    2015-01-01

    In this work is presented the synthesis of nanocomposites of poly(methyl methacrylate), PMMA, with organically montmorillonite (OMMT) modified clays by in situ polymerization assisted by sonication. A statistically designed experiment was used, central composing design (CCD), to study the effect of synthesis variables on the dispersion of nanoparticles in PMMA matrix. The processing and formulation factors studied were: energy of sonication and Flory-Huggins interaction parameter between PMMA and organoclay. The structural (XRD) and morphological (TEM) characterizations of the PMMA/OMMT nanocomposites are compared with the literature. It was observed significant exfoliation of OMMT modified with hydroxyl groups in the nanocomposites of PMMA, mainly at the low ultrasonic energy level (90 and 105 kJ) studied. (author)

  10. Validation of a measuring technique with computed tomography for cement penetration into trabecular bone underneath the tibial tray in total knee arthroplasty on a cadaver model

    International Nuclear Information System (INIS)

    Verburg, Hennie; Ridder, Laurens C van de; Verhoeven, Vincent WJ; Pilot, Peter

    2014-01-01

    In total knee arthroplasty (TKA), cement penetration between 3 and 5 mm beneath the tibial tray is required to prevent loosening of the tibia component. The objective of this study was to develop and validate a reliable in vivo measuring technique using CT imaging to assess cement distribution and penetration depth in the total area underneath a tibia prosthesis. We defined the radiodensity ranges for trabecular tibia bone, polymethylmethacrylate (PMMA) cement and cement-penetrated trabecular bone and measured the percentages of cement penetration at various depths after cementing two tibia prostheses onto redundant femoral heads. One prosthesis was subsequently removed to examine the influence of the metal tibia prostheses on the quality of the CT images. The percentages of cement penetration in the CT slices were compared with percentages measured with photographs of the corresponding transversal slices. Trabecular bone and cement-penetrated trabecular bone had no overlap in quantitative scale of radio-density. There was no significant difference in mean HU values when measuring with or without the tibia prosthesis. The percentages of measured cement-penetrated trabecular bone in the CT slices of the specimen were within the range of percentages that could be expected based on the measurements with the photographs (p = 0.04). CT scan images provide valid results in measuring the penetration and distribution of cement into trabecular bone underneath the tibia component of a TKA. Since the proposed method does not turn metal elements into artefacts, it enables clinicians to assess the width and density of the cement mantle in vivo and to compare the results of different cementing methods in TKA

  11. Outcome of long-axis percutaneous sacroplasty for the treatment of sacral insufficiency fractures with a radiofrequency-induced, high-viscosity bone cement

    Energy Technology Data Exchange (ETDEWEB)

    Eichler, Katrin [University of Frankfurt, Department of Diagnostic and Interventional Radiology, Frankfurt (Germany); J. W. Goethe University of Frankfurt, Institute for Diagnostic and Interventional Radiology, Frankfurt (Germany); Zangos, Stephan; Vogl, Thomas J. [University of Frankfurt, Department of Diagnostic and Interventional Radiology, Frankfurt (Germany); Mack, Martin G. [Radiology Munich, Munich (Germany); Marzi, Ingo [University of Frankfurt, Department of Trauma, Hand and Reconstructive Surgery, Frankfurt (Germany)

    2014-04-15

    Our goal was to assess the technical results in patients who underwent long-axis sacroplasty for the treatment of sacral insufficiency fractures (SIF) by radiofrequency-induced high-viscosity bone cement augmentation. Twelve patients with bilateral sacral fractures were treated by augmentation with radiofrequency-activated, high-viscosity polymethylmethacrylate (PMMA) bone cement under local anesthesia. CT-guided sacroplasty was performed by using a long-axis approach through a single entry point. Thirty-six vertebrae were treated in 12 sessions under a combination of CT and fluoroscopic guidance using a bilateral access and a cavity-creating osteotome prior to remote-controlled, hydraulically driven cement injection. The visual analogue scale (VAS) score before sacroplasty and at 1 and 3 months after the treatment was obtained. PMMA leaks were evaluated retrospectively using the post-interventional CT. The mean amount of high-viscosity PMMA injected per patient was 7.8 ml. No major adverse events were observed. In the first 4 days after the procedure, the mean VAS score decreased from 8.1 ± 1.9 to mean 3.1 ± 1.2 and was followed by a gradual but continuous decrease throughout the rest of the follow-up period at 24 weeks (mean 2.2 ± 1.1) and 48 weeks (mean 2.1 ± 1.4). CT fluoroscopy-guided sacral augmentation was safe and effective in all 12 patients with osteoporotic SIF. (orig.)

  12. Cement-base bearing pads mortar for connections in the precast concrete: study of surface roughness

    Directory of Open Access Journals (Sweden)

    M. K. El Debs

    Full Text Available Bearing pads are used in precast concrete connections to avoid concentrated stresses in the contact area between the precast elements. In the present research, the bearing pads are Portland cement mortar with styrene-butadiene latex (SB, lightweight aggregate (expanded vermiculite-term and short fibers (polypropylene, glass and PVA, in order to obtain a material with low modulus of elasticity and high tenacity, compared with normal Portland cement mortar. The objective of this paper is to analyze the influence of surface roughness on the pads and test other types of polypropylene fibers. Tests were carried out to characterize the composite and test on bearing pads. Characterization tests show compressive strength of 41MPa and modulus of elasticity of 12.8GPa. The bearing pads tests present 30% reduction of stiffness in relation to a reference mortar. The bearing pads with roughness on both sides present a reduction up to 30% in stiffness and an increase in accumulated deformation of more than 120%, regarding bearing pads with both sides smooth.

  13. Mineral resource of the month: hydraulic cement

    Science.gov (United States)

    van Oss, Hendrik G.

    2012-01-01

    Hydraulic cements are the binders in concrete and most mortars and stuccos. Concrete, particularly the reinforced variety, is the most versatile of all construction materials, and most of the hydraulic cement produced worldwide is portland cement or similar cements that have portland cement as a basis, such as blended cements and masonry cements. Cement typically makes up less than 15 percent of the concrete mix; most of the rest is aggregates. Not counting the weight of reinforcing media, 1 ton of cement will typically yield about 8 tons of concrete.

  14. Cement-latex grouting mortar for cementing boreholes

    Energy Technology Data Exchange (ETDEWEB)

    Kateev, I S; Golyshkina, L A; Gorbunova, I V; Kurochkin, B M; Vakula, Ya V

    1980-01-01

    The need for the development of cement-latex grouting mortar for the purpose of separating strata when reinforcing boreholes at deposits in the Tatar Associated SSR is evaluated. Results of studies of the physical and mechanical properties of cement-latex grouting mortar systems (mortar plus brick) are presented. Formulas for preparing cement-latex grouting mortor are evaluated and results of industrial tests of such mortars shown.

  15. US cement industry

    Energy Technology Data Exchange (ETDEWEB)

    Nisbet, M.A.

    1997-12-31

    This paper describes the cement and concrete industry, and provides data on energy use and carbon dioxide emissions. The potential impact of an energy tax on the industry is briefly assessed. Opportunities identified for reducing carbon dioxide emissions include improved energy efficiency, alternative fuels, and alternative materials. The key factor in determining CO{sub 2} emissions is the level of domestic production. The projected improvement in energy efficiency and the relatively slow growth in domestic shipments indicate that CO{sub 2} emissions in 2000 should be about 5% above the 1990 target. However, due to the cyclical nature of cement demand, emissions will probably be above target levels during peak demand and below target levels during demand troughs. 7 figs., 2 tabs.

  16. Observation on the role of osteoporotic vertebra augmented with calcium sulfate cement in vivo

    International Nuclear Information System (INIS)

    Zhu Xuesong; Shi Qin; Zhang Zhiming; Geng Dechun; Mao Haiqing; Chen Chunmao; Wang Genlin; Yang Huilin

    2010-01-01

    Objective: To observe the biomechanical and histological performance of calcium sulfate cement (CSC) in osteoporotic vertebral bodies. Methods: Bone voids were created in L 2 ∼ L 5 vertebras of twelve female osteoporotic mature sheep. CSC and polymethylmethacrylate (PMMA) were injected into one bone voids randomly, L 1 and L 6 vertebrae served as the normal control. Six sheep were sacrificed at the 2nd week and the 24th week after operation respectively. Overall observation,biomechanical test and undecalcified bone histology analyses were performed. Results: Biomechanical analysis showed that the vertebrae could be augmented by CSC and PMMA. The biomechanical properties of the vertebrae augmented with CSC were weakened more than that in the PMMA and normal group at the 2nd week, increased significantly at the 24th week. Histological observation showed that CSC was mostly absorbed at the 24th week, mature bone trabecula was seen in the defect area. Conclusion: The osteoporotic vertebrae can be augmented instantly by CSC. As time goes on, CSC can promote bone remodeling, and enhance the vertebrae. It is an alternation for vertebroplasty and kyphoplasty. (authors)

  17. Laser-induced damage study of polymer PMMA

    International Nuclear Information System (INIS)

    Mansour, N.

    2001-01-01

    This article presents the results of bulk laser-induced damage measurements in polymer PMMA at 532 nm and 1064 nm for nanosecond laser pulses. The damage thresholds were measured for focused spot sizes ranging over two orders of magnitude. In this work, self-focusing effects were verified to be absent by measurements of breakdown thresholds using both linearly and circularly polarized light. At both 1064 nm and 532 nm, the dependence of the breakdown field, E B , on the spot size, ω, was empirically determined to be E B = C/√ω, where C depends on the wavelength. The extracted value for C(λ) at 1064 nm is larger by a factor of 5 than at 532 nm. Possible reasons for this strong dispersion and mechanism for laser-induced damage in polymer materials will be discussed

  18. Effects of interruption of irradiation on Harwell Red Perspex (PMMA)

    International Nuclear Information System (INIS)

    Khayet Tebourbi, Mohamed anouar abdelaziz

    2010-01-01

    Harwell Red Perspex PMMA (Polymethylmethacrylate) is a dosimeter very much used in the industrial treatments by Radiations ionizing. The purpose of this work is to test the response of this dosimeter for radiation processes having undergone one or more interruptions. This experimental study based on the development of a factorial experimental design on two levels showed that the response of this dosimeter increases for the interrupted treatments. The value of the estimated amount of response increase is all the more significant as the temperature during the interruption is high. Also it made possible to determine a mathematical model binding the value of the amount posted to the factors of influence: Temperature, target amount, a number of interruptions and duration of each interruption.

  19. Long term strain behavior of PMMA based polymer optical fibers

    DEFF Research Database (Denmark)

    Bundalo, Ivan-Lazar; Nielsen, Kristian; Woyessa, Getinet

    2015-01-01

    We are reporting on the viscoelasticity of PMMA based Fiber Bragg Grating (FBG) strain sensors when exposed to repeated sequences of long term strain and relaxation with various duty-cycles. In terms of the FBG wavelength and how it follows the strain cycle, we have shown that in the small strain...... regime (up to 1%) an elastic-dominated fast relaxing range, which is followed by a mainly viscous relaxation, depends both on the strain level and on the strain duration. For a small ratio of the strain-relax durations, this fast relaxation range stays almost the same. However, with increasing strain...... duration, for the same relaxation time, this range will be shortened, which might influence the sensing capabilities of the fiber sensor....

  20. Structural and Electrochemical Analysis of PMMA Based Gel Electrolyte Membranes

    Directory of Open Access Journals (Sweden)

    Chithra M. Mathew

    2015-01-01

    Full Text Available New gel polymer electrolytes containing poly(vinylidene chloride-co-acrylonitrile and poly(methyl methacrylate are prepared by solution casting method. With the addition of 60 wt.% of EC to PVdC-AN/PMMA blend, ionic conductivity value 0.398×10-6 S cm−1 has been achieved. XRD and FT-IR studies have been conducted to investigate the structure and complexation in the polymer gel electrolytes. The FT-IR spectra show that the functional groups C=O and C≡N play major role in ion conduction. Thermal stability of the prepared membranes is found to be about 180°C.

  1. Vibration Properties of a Steel-PMMA Composite Beam

    Directory of Open Access Journals (Sweden)

    Yuyang He

    2015-01-01

    Full Text Available A steel-polymethyl methacrylate (steel-PMMA beam was fabricated to investigate the vibration properties of a one-dimensional phononic crystal structure. The experimental system included an excitation system, a signal acquisition system, and a data analysis and processing system. When an excitation signal was exerted on one end of the beam, the signals of six response points were collected with acceleration sensors. Subsequent signal analysis showed that the beam was attenuated in certain frequency ranges. The lumped mass method was then used to calculate the bandgap of the phononic crystal beam to analyze the vibration properties of a beam made of two different materials. The finite element method was also employed to simulate the vibration of the phononic crystal beam, and the simulation results were consistent with theoretical calculations. The existence of the bandgap was confirmed experimentally and theoretically, which allows for the potential applications of phononic crystals, including wave guiding and filtering, in integrated structures.

  2. Chemical environment in cements

    International Nuclear Information System (INIS)

    Glasser, F.B.; Angus, M.J.; McCulloch, C.E.; Macphee, D.; Rahman, A.A.

    1984-01-01

    The alkalinity of Portland cements is responsible for precipitation and low solubility of many radwastes species. The sources of alkalinity are evaluated and two chemical models, based on experimental and theoretical data presented enabling the effect of blending agents (PFA, silica fume, etc.) to be evaluated and the alkalinity of the system at longer ages predicted. The data take the form of a solubility model which is applicable to non-heat generating wastes. 7 refs., 10 figs

  3. Performance of Cement Containing Laterite as Supplementary Cementing Material

    Directory of Open Access Journals (Sweden)

    Abbas Bukhari, Z. S.

    2013-03-01

    Full Text Available The utilization of different industrial waste, by-products or other materials such as ground granulated blast furnace slag, silica fume, fly ash, limestone, and kiln dust, etc. as supplemen- tary cementing materials has received considerable attention in recent years. A study has been conducted to look into the performance of laterite as Supplementary Cementing Materials (SCM. The study focuses on compressive strength performance of blended cement containing different percentage of laterite. The cement is replaced accordingly with percentage of 2 %, 5 %, 7 % and 10 % by weight. In addition, the effect of use of three chemically different laterites have been studied on physical performance of cement as in setting time, Le-Chatlier expansion, loss on ignition, insoluble residue, free lime and specifically compressive strength of cement cubes tested at the age of 3, 7, and 28 days. The results show that the strength of cement blended with laterite as SCM is enhanced. Key words: Portland cement, supplementary cementing materials (SCM, laterite, compressive strength KUI – 6/2013 Received January 4, 2012 Accepted February 11, 2013

  4. Thermoluminescence glow curves of irradiated PMMA and low density polyethylene

    International Nuclear Information System (INIS)

    Matsuda, Koji; Nakase, Yoshiaki; Kumakiri, Yasuhito; Tsuji, Yoshio.

    1985-03-01

    Light emission from polymers is observed when polymers preirradiated with ionizing radiation at low temperature are heated gradually. The light emission is supposedly resulted from recombination of electrons with active centers produced in polymers or from some other processes involving charge transfer, but no definite explanation has been given at present on the thermoluminescent centers. This report describes our studies on the effects of impurities contained in polymers and pressure of ambient gases on the thermoluminescent glow curve of PMMA and low density polyethylene, which are often used for plastic film dosimeters. In the glow curve of PMMA, only one peak was observed at 110 K in an H 2 or He atmosphere at 760 Torr, but the intensity of the peak decreased with decreasing the H 2 or He gas pressure. At 10 -5 Torr H 2 or He atmosphere the peak disappered, and two sharp peaks appeared in the temperature range from 200 to 250 K. On the other hand, in the glow curve of low density polyethylene, three peaks were observed at 120 K, 180 K and 250 K in the presence of H 2 or He gas at 760 Torr. The effects of pressure of ambient gases and impurities in the polyethylene on these peaks indicate that the peak at 120 K is due to luminescent center produced on the surface or just below the surface of the matrix by collision of excited atoms or molecules of gases with polymer molecules, the peak at 120 K is originated from impurities in the matrix, and the peak at 250 0 K corresponds to luminescent center produced in polyethylene matrix. (author)

  5. Impact of X-ray irradiation on PMMA thin films

    Energy Technology Data Exchange (ETDEWEB)

    Iqbal, Saman, E-mail: saman.khan343@gmail.com [Physics Department, University of Engineering and Technology, Lahore (Pakistan); Rafique, Muhammad Shahid [Physics Department, University of Engineering and Technology, Lahore (Pakistan); Anjum, Safia [Physics Department, Lahore College for Woman University, Lahore (Pakistan); Hayat, Asma [Physics Department, University of Engineering and Technology, Lahore (Pakistan); Iqbal, Nida [Faculty of Biomedical Engineering and Health Science, Universiti Teknologi Malaysia (UTM) (Malaysia)

    2012-10-15

    Highlights: Black-Right-Pointing-Pointer PMMA thin films were deposited at 300 Degree-Sign C and 500 Degree-Sign C using PLD technique. Black-Right-Pointing-Pointer These films were irradiated with different fluence of laser produced X-rays. Black-Right-Pointing-Pointer Irradiation affects the ordered packing as well as surface morphology of film. Black-Right-Pointing-Pointer Hardness of film decreases up to certain value of X-ray fluence. Black-Right-Pointing-Pointer Absorption in UV-visible range exhibits a non linear behavior. - Abstract: The objective of this project is to explore the effect of X-ray irradiation of thin polymeric films deposited at various substrate temperatures. pulsed laser deposition (PLD) technique is used for the deposition of PMMA thin films on glass substrate at 300 Degree-Sign C and 500 Degree-Sign C. These films have been irradiated with various X-rays fluences ranging from 2.56 to 5.76 mJ cm{sup -2}. Characterization of the films (before and after the irradiation) is done with help of X-ray Diffractrometer, Optical Microscope, Vickers hardness tester and UV-vis spectroscopy techniques. From XRD data, it is revealed that ordered packing has been improved for the films deposited at 300 Degree-Sign C. However after irradiation the films exhibited the amorphous behavior regardless of the X-ray fluence. Film deposited at 500 Degree-Sign C shows amorphous structure before and after irradiation. Hardness and particle size of thin film have also increased with the increasing substrate temperature. However, the irradiation has reverse effect i.e. the particle size as well as the hardness has reduced. Irradiation has also enhanced the absorption in the UV-visible region.

  6. Impact of X-ray irradiation on PMMA thin films

    International Nuclear Information System (INIS)

    Iqbal, Saman; Rafique, Muhammad Shahid; Anjum, Safia; Hayat, Asma; Iqbal, Nida

    2012-01-01

    Highlights: ► PMMA thin films were deposited at 300 °C and 500 °C using PLD technique. ► These films were irradiated with different fluence of laser produced X-rays. ► Irradiation affects the ordered packing as well as surface morphology of film. ► Hardness of film decreases up to certain value of X-ray fluence. ► Absorption in UV–visible range exhibits a non linear behavior. - Abstract: The objective of this project is to explore the effect of X-ray irradiation of thin polymeric films deposited at various substrate temperatures. pulsed laser deposition (PLD) technique is used for the deposition of PMMA thin films on glass substrate at 300 °C and 500 °C. These films have been irradiated with various X-rays fluences ranging from 2.56 to 5.76 mJ cm −2 . Characterization of the films (before and after the irradiation) is done with help of X-ray Diffractrometer, Optical Microscope, Vickers hardness tester and UV–vis spectroscopy techniques. From XRD data, it is revealed that ordered packing has been improved for the films deposited at 300 °C. However after irradiation the films exhibited the amorphous behavior regardless of the X-ray fluence. Film deposited at 500 °C shows amorphous structure before and after irradiation. Hardness and particle size of thin film have also increased with the increasing substrate temperature. However, the irradiation has reverse effect i.e. the particle size as well as the hardness has reduced. Irradiation has also enhanced the absorption in the UV–visible region.

  7. Phase holograms in PMMA with proximity effect correction

    Science.gov (United States)

    Maker, Paul D.; Muller, R. E.

    1993-01-01

    Complex computer generated phase holograms (CGPH's) have been fabricated in PMMA by partial e-beam exposure and subsequent partial development. The CGPH was encoded as a sequence of phase delay pixels and written by the JEOL JBX-5D2 E-beam lithography system, a different dose being assigned to each value of phase delay. Following carefully controlled partial development, the pattern appeared rendered in relief in the PMMA, which then acts as the phase-delay medium. The exposure dose was in the range 20-200 micro-C/sq cm, and very aggressive development in pure acetone led to low contrast. This enabled etch depth control to better than plus or minus lambda(sub vis)/60. That result was obtained by exposing isolated 50 micron square patches and measuring resist removal over the central area where the proximity effect dose was uniform and related only to the local exposure. For complex CGPH's with pixel size of the order of the e-beam proximity effect radius, the patterns must be corrected for the extra exposure caused by electrons scattered back up out of the substrate. This has been accomplished by deconvolving the two-dimensional dose deposition function with the desired dose pattern. The deposition function, which plays much the same role as an instrument response function, was carefully measured under the exact conditions used to expose the samples. The devices fabricated were designed with 16 equal phase steps per retardation cycle, were up to 1 cm square, and consisted of up to 100 million 0.3-2.0 micron square pixels. Data files were up to 500 MB long and exposure times ranged to tens of hours. A Fresnel phase lens was fabricated that had diffraction limited optical performance with better than 85 percent efficiency.

  8. CT-guided vertebroplasty: analysis of technical results, extraosseous cement leakages, and complications in 500 procedures

    Energy Technology Data Exchange (ETDEWEB)

    Pitton, Michael Bernhard; Herber, Sascha; Koch, Ulrike; Oberholzer, Katja; Dueber, Christoph [Johannes Gutenberg-University of Mainz, Department of Diagnostic and Interventional Radiology, Mainz (Germany); Drees, Philip [University Hospital, Johannes Gutenberg-University of Mainz, Department of Orthopedic Surgery, Mainz (Germany)

    2008-11-15

    The aim of this study was to analyze the technical results, the extraosseous cement leakages, and the complications in our first 500 vertebroplasty procedures. Patients with osteoporotic vertebral compression fractures or osteolytic lesions caused by malignant tumors were treated with CT-guided vertebroplasty. The technical results were documented with CT, and the extraosseous cement leakages and periinterventional clinical complications were analyzed as well as secondary fractures during follow-up. Since 2002, 500 vertebroplasty procedures have been performed on 251 patients (82 male, 169 female, age 71.5 {+-} 9.8 years) suffering from osteoporotic compression fractures (n = 217) and/or malignant tumour infiltration (n = 34). The number of vertebrae treated per patient was 1.96 {+-} 1.29 (range 1-10); the numbers of interventions per patient and interventions per vertebra were 1.33 {+-} 0.75 (range 1-6) and 1.01 {+-} 0.10, respectively. The amount of PMMA cement was 4.5 {+-} 1.9 ml and decreased during the 5-year period of investigation. The procedure-related 30-day mortality was 0.4% (1 of 251 patients) due to pulmonary embolism in this case. The procedure-related morbidity was 2.8% (7/251), including one acute coronary syndrome beginning 12 h after the procedure and one missing patellar reflex in a patients with a cement leak near the neuroformen because of osteolytic destruction of the respective pedicle. Additionally, one patient developed a medullary conus syndrome after a fall during the night after vertebroplasty, two patients reached an inadequate depth of conscious sedation, and two cases had additional fractures (one pedicle fracture, one rib fracture). The overall CT-based cement leak rate was 55.4% and included leakages predominantly into intervertebral disc spaces (25.2%), epidural vein plexus (16.0%), through the posterior wall (2.6%), into the neuroforamen (1.6%), into paravertebral vessels (7.2%), and combinations of these and others. During follow

  9. CT-guided vertebroplasty: analysis of technical results, extraosseous cement leakages, and complications in 500 procedures

    International Nuclear Information System (INIS)

    Pitton, Michael Bernhard; Herber, Sascha; Koch, Ulrike; Oberholzer, Katja; Dueber, Christoph; Drees, Philip

    2008-01-01

    The aim of this study was to analyze the technical results, the extraosseous cement leakages, and the complications in our first 500 vertebroplasty procedures. Patients with osteoporotic vertebral compression fractures or osteolytic lesions caused by malignant tumors were treated with CT-guided vertebroplasty. The technical results were documented with CT, and the extraosseous cement leakages and periinterventional clinical complications were analyzed as well as secondary fractures during follow-up. Since 2002, 500 vertebroplasty procedures have been performed on 251 patients (82 male, 169 female, age 71.5 ± 9.8 years) suffering from osteoporotic compression fractures (n = 217) and/or malignant tumour infiltration (n = 34). The number of vertebrae treated per patient was 1.96 ± 1.29 (range 1-10); the numbers of interventions per patient and interventions per vertebra were 1.33 ± 0.75 (range 1-6) and 1.01 ± 0.10, respectively. The amount of PMMA cement was 4.5 ± 1.9 ml and decreased during the 5-year period of investigation. The procedure-related 30-day mortality was 0.4% (1 of 251 patients) due to pulmonary embolism in this case. The procedure-related morbidity was 2.8% (7/251), including one acute coronary syndrome beginning 12 h after the procedure and one missing patellar reflex in a patients with a cement leak near the neuroformen because of osteolytic destruction of the respective pedicle. Additionally, one patient developed a medullary conus syndrome after a fall during the night after vertebroplasty, two patients reached an inadequate depth of conscious sedation, and two cases had additional fractures (one pedicle fracture, one rib fracture). The overall CT-based cement leak rate was 55.4% and included leakages predominantly into intervertebral disc spaces (25.2%), epidural vein plexus (16.0%), through the posterior wall (2.6%), into the neuroforamen (1.6%), into paravertebral vessels (7.2%), and combinations of these and others. During follow-up (15

  10. Barium aluminate cement: its application

    International Nuclear Information System (INIS)

    Drozdz, M.; Wolek, W.

    1975-01-01

    The technology of manufacturing barium aluminate cement from barium sulfate and alumina, using a rotary kiln for firing the clinker is described. The method of granulation of the homogenized charge was used. Conditions of using the ''to mud'' method in industry were indicated. The physical and chemical properties of barium aluminate cement are determined and the quality of several batches of cement prepared on a semi-industrial scale and their suitability for making highly refractory concretes are tested. The optimal composition of the concretes is determined as a function of the mixing water and barium aluminate cement contents. Several experimental batches of concretes were used in the linings of furnaces in the steel industry. The suitability of these cements for use in fields other than steelmaking is examined. It is established that calcium aluminate cement has certain limited applications [fr

  11. Polyaniline nanofibers as a new gamma radiation stabilizer agent for PMMA

    Directory of Open Access Journals (Sweden)

    2007-06-01

    Full Text Available Polyanilines are reported to exhibit stabilizing effects in rubber mixtures submitted to gamma-irradiation and thermo-oxidative treatment. Such abilities may be explained by their action as radical scavengers. Since radical formation followed by main chain scission is a widely accepted mechanism for radiolytic degradation of PMMA, polyaniline is a promising additive for commercial plastics submitted to radiosterilization processing. In this work, we investigated the ability of polyaniline emeraldine salt nanofibers (PANF-HCl in preventing radiation damage on PMMA matrix. Effects of gamma-irradiation on PMMA/PANF-HCl composites films were assessed by comparison of the variation of viscosity-average molar mass (Mv of PMMA at 25 kGy dose when compared to commercial PMMA films. Samples containing 0.15% PANF-HCl (wt/wt retained 92% of the initial Mv after irradiation while control sample presented 42% of Mv retention. When exposed to 60-200 kGy doses, PANF-HCl embedded into PMMA matrix preserved their oxidation state but started to exhibit mild deprotonation. PANF-HCl nanofibers were characterized by Diffuse Reflection Infrared Fourier Transform Spectroscopy (DRIFTS and Scanning Electronic Microscopy (SEM. PMMA/PANF-HCl composites films were characterized by SEM and UV-VIS spectroscopy.

  12. Hydrophilic film polymerized on the inner surface of PMMA tube by an atmospheric pressure plasma jet

    Science.gov (United States)

    Yin, Mengmeng; Huang, Jun; Yu, Jinsong; Chen, Guangliang; Qu, Shanqing

    2017-07-01

    Polymethyl methacrylate (PMMA) tube is widely used in biomedical and mechanical engineering fields. However, it is hampered for some special applications as the inner surface of PMMA tube exhibts a hydrophobic characteristic. The aim of this work is to explore the hydrophilic modification of the inner surface of the PMMA tubes using an atmospheric pressure plasma jet (APPJ) system that incorporates the acylic acid monomer (AA). Polar groups were grafted onto the inner surface of PMMA tube via the reactive radicals (•OH, •H, •O) generated in the Ar/O2/AA plasma, which were observed by the optical emission spectroscopy (OES). The deposition of the PAA thin layer on the PMMA surface was verified through the ATR-FTIR spectra, which clearly showed the strengthened stretching vibration of the carbonyl group (C=O) at 1700 cm-1. The XPS data show that the carbon ratios of C-OH/R and COOH/R groups increased from 9.50% and 0.07% to 13.49% and 17.07% respectively when a discharge power of 50 W was used in the APPJ system. As a result, the static water contat angle (WCA) of the modified inner surface of PMMA tube decreased from 100° to 48°. Furthermore, the biocompatibility of the APP modified PMMA tubes was illustrated by the study of the adhesion of the cultured MC3T3-E1 osteocyte cells, which exhibted a significantly enhanced adhesion density.

  13. Selective Electroless Nickel Plating on PMMA using Chloroform Pre-Treatment

    Science.gov (United States)

    Sipes, Nicholas

    In the past 5 years, we have discovered that chloroform promotes the adhesion of thin gold films to Poly(methyl methacrylate) surfaces. Based on this new understanding of the interaction of chloroform with PMMA and metal atoms, we were curious to see if chloroform would promote the adhesion of Nickel to PMMA deposited by electroless plating. My goal was to selectively electroless plate Nickel onto PMMA. Chloroform was spun-cast onto 1 inch square PMMA substrates. I used electrical tape to shield one half of the PMMA from the chloroform during spin-casting; this allowed for a direct comparison of treated vs. untreated. The samples were then put through hydrochloric acid and a series of baths provided by Transene Company Inc. to electrolessly deposit nickel on the sample. After many trials, there was a clear distinction in the adhesion strength of the Nickel to the plain PMMA surface vs. the chloroform pre-treated surface. Showing that it is possible to create chloroform sites via spin-casting for electroless nickel plating on PMMA opens up the challenge to better understand the chemistry taking place and to perfect the electroless plating process.

  14. Reflectance spectroscopy of PMMA implanted with 50 keV silicon ions

    Energy Technology Data Exchange (ETDEWEB)

    Florian, Bojana [Bulgarian Institute of Metrology, 2 Prof. P. Mutafchiev Str., 1797 Sofia (Bulgaria); Stefanov, Ivan [Department of Quantum Electronics, Faculty of Physics, Sofia University, 5 James Bourchier Blvd., 1164 Sofia (Bulgaria); Hadjichristov, Georgi [Institute of Solid State Physics, 72 Tzarigradsko Chaussee Blvd., 1784 Sofia (Bulgaria)

    2009-07-01

    Recently, the modification of the specular reflectivity of PMMA implanted with low-energy (50 keV) silicon ions was studied and nano-clusters formed in PMMA by Si{sup +} implantation were evidenced by Raman spectroscopy and electrical measurements. Further, the optical loss due to off-specular (diffuse) reflectivity of this ion-implanted polymer is also of practical interest for applications such as micro-optical lenses, diffraction gratings, Fresnel lenses, waveguides, etc. We examined both specular and diffuse reflectivity of Si{sup +} implanted PMMA in the UV-Vis-NIR. The effect from Si{sup +} implantation in the dose range 10{sup 14}-10{sup 17} ions/cm{sup 2} is linked to the structure formed in PMMA where the buried ion-implanted layer has a thickness up to 100 nm. As compared to the pristine PMMA, an enhancement of the reflectivity of Si{sup +} implanted PMMA is observed, that is attributed to the modification of the subsurface region of PMMA upon the ion implantation.

  15. Synthesis and investigation of PMMA films with homogeneously dispersed multiwalled carbon nanotubes

    International Nuclear Information System (INIS)

    Pantoja-Castro, M.A.; Pérez-Robles, J.F.; González-Rodríguez, H.; Vorobiev-Vasilievitch, Y.; Martínez-Tejada, H.V.; Velasco-Santos, C.

    2013-01-01

    Multiwalled carbon nanotubes (MWNT) modified by 2.2′-azoiso-butyronitrile (AIBN) were incorporated into methyl methacrylate (MMA) by sonochemistry method, resulting in homogenous dispersion of MWNT, which makes possible to obtain flexible conductive polymer-matrix nanocomposites films of PMMA, with MWNT concentrations ranging from 0 to 0.5 wt%. Modified MWNT (AIBN-MWNT) were studied by Fourier transform infrared (FT-IR), Raman spectroscopy, X-ray Photoelectron Spectroscopy (XPS) and through visual observations in order to compare the dispersion in 2-propanone and toluene with that of pristine MWNT. Synthesized PMMA-AIBN-MWNT films were studied by FT-IR and Raman spectroscopy. Using FT-IR for the AIBN-MWNT it was not possible to identify any group or groups attached to the nanotubes. Raman spectroscopy shows a small modification in the Lorentzian peaks ratio I D/G of AIBN-MWNT, meanwhile XPS showed that atomic compositions does not change for AIBN-MWNT compared to the pristine nanotubes. Also by impedance it was analyzed the conductivity of PMMA-MWNT films and the results showed a threshold percolation at 0.5 wt%. FT-IR and Raman analyses for PMMA-AIBN-MWNT composite indicate a covalent bonding between PMMA and MWNT due to the opening of π-bonds of the nanotubes, which is related with a possible proposed reaction scheme. - Graphical abstract: Display Omitted - Highlights: • We used sonochemistry-in situ polymerization to disperse MWNT very soon in PMMA. • A high and homogenous dispersion of MWNT in PMMA was achieved. • The modification of MWNT by AIBN was analyzed using Raman. • A covalent bonding between PMMA and MWNT was analyzed by FT-IR and Raman. • According to the results of PMMA-MWNT it was proposed a scheme reaction

  16. Synthesis and investigation of PMMA films with homogeneously dispersed multiwalled carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Pantoja-Castro, M.A., E-mail: m_pantojaq@yahoo.com.mx [Facultad de Ingeniería Química, Universidad Michoacana de San Nicolás de Hidalgo, Av. J. Múgica S/N Col., Villa Universidad, CP 58040 Morelia, Michoacán (Mexico); Pérez-Robles, J.F. [Centro de Investigación y de Estudios Avanzados del IPN, Unidad Querétaro, Libramiento Norponiente #2000, Fracc. Real de Juriquilla, CP 76230 Querétaro (Mexico); González-Rodríguez, H. [Facultad de Ingeniería Química, Universidad Michoacana de San Nicolás de Hidalgo, Av. J. Múgica S/N Col., Villa Universidad, CP 58040 Morelia, Michoacán (Mexico); Vorobiev-Vasilievitch, Y. [Centro de Investigación y de Estudios Avanzados del IPN, Unidad Querétaro, Libramiento Norponiente #2000, Fracc. Real de Juriquilla, CP 76230 Querétaro (Mexico); Martínez-Tejada, H.V. [Instituto de Energía, Materiales y Medio Ambiente, Universidad Pontificia Bolivariana, Circular 1 No. 70-01, Bloque 22, Medellín (Colombia); Velasco-Santos, C. [Centro de Física Aplicada y Tecnología Avanzada, Universidad Autónoma de México, Av. Boulevard Juriquilla, No. 3001 Juriquilla, CP 76230 Querétaro (Mexico)

    2013-07-15

    Multiwalled carbon nanotubes (MWNT) modified by 2.2′-azoiso-butyronitrile (AIBN) were incorporated into methyl methacrylate (MMA) by sonochemistry method, resulting in homogenous dispersion of MWNT, which makes possible to obtain flexible conductive polymer-matrix nanocomposites films of PMMA, with MWNT concentrations ranging from 0 to 0.5 wt%. Modified MWNT (AIBN-MWNT) were studied by Fourier transform infrared (FT-IR), Raman spectroscopy, X-ray Photoelectron Spectroscopy (XPS) and through visual observations in order to compare the dispersion in 2-propanone and toluene with that of pristine MWNT. Synthesized PMMA-AIBN-MWNT films were studied by FT-IR and Raman spectroscopy. Using FT-IR for the AIBN-MWNT it was not possible to identify any group or groups attached to the nanotubes. Raman spectroscopy shows a small modification in the Lorentzian peaks ratio I{sub D/G} of AIBN-MWNT, meanwhile XPS showed that atomic compositions does not change for AIBN-MWNT compared to the pristine nanotubes. Also by impedance it was analyzed the conductivity of PMMA-MWNT films and the results showed a threshold percolation at 0.5 wt%. FT-IR and Raman analyses for PMMA-AIBN-MWNT composite indicate a covalent bonding between PMMA and MWNT due to the opening of π-bonds of the nanotubes, which is related with a possible proposed reaction scheme. - Graphical abstract: Display Omitted - Highlights: • We used sonochemistry-in situ polymerization to disperse MWNT very soon in PMMA. • A high and homogenous dispersion of MWNT in PMMA was achieved. • The modification of MWNT by AIBN was analyzed using Raman. • A covalent bonding between PMMA and MWNT was analyzed by FT-IR and Raman. • According to the results of PMMA-MWNT it was proposed a scheme reaction.

  17. Stability of reinforced cemented backfills

    International Nuclear Information System (INIS)

    Mitchell, R.J.; Stone, D.M.

    1987-01-01

    Mining with backfill has been the subject of several international meetings in recent years and a considerable research effort is being applied to improve both mining economics and ore recovery by using backfill for ground support. Classified mill tailings sands are the most commonly used backfill material but these fine sands must be stabilized before full ore pillar recovery can be achieved. Normal portland cement is generally used for stabilization but the high cost of cement prohibits high cement usage. This paper considers the use of reinforcements in cemented fill to reduce the cement usage. It is concluded that strong cemented layers at typical spacings of about 3 meters in a low cement content bulk fill can reinforce the fill and reduce the overall cement usage. Fibre reinforcements introduced into strong layers or into bulk fills are also known to be effective in reducing cement usage. Some development work is needed to produce the ideal type of anchored fibre in order to realize economic gains from fibre-reinforced fills

  18. Durability and Mechanical Performance of PMMA/Stone Sludge Nanocomposites for Acrylic Solid Surface Applications

    Directory of Open Access Journals (Sweden)

    Samah EL-Bashir

    2017-11-01

    Full Text Available Acrylic solid surface sheets were prepared by mixing different kinds of stone sludge fillers (SSF in Poly (methyl methacrylate (PMMA nanocomposites. PMMA nanocomposite syrups were made using free radical polymerization of methylmethacrylate (MMA, then two kinds of nanofillers were added, namely, hydrophilic nanosilica and clay Halloysite nanotubules (HNTs. Acrylic solid surface sheets were manufactured by mixing the syrups with SSFs. The morphology of the produced sheets was studied using optical, and Scanning Electron Microscopy (SEM that revealed the uniform distribution of stone sludge in the polymeric matrix. The study of the physical properties showed promising mechanical performance and durability of PMMA/SSF nanocomposites for acrylic solid surface applications.

  19. Using dehydrated cement paste as new type of cement additive

    NARCIS (Netherlands)

    Yu, R.; Shui, Z.H.; Dong, J

    2013-01-01

    This paper presents an experimental study, including evaluation and modification, on using dehydrated cement paste (DCP) as a new type of cement additive. After a series of processes, normal DCP (N-DCP) was produced as before and a modified form of DCP (M-DCP) was produced as well. The cementitious

  20. Biomass for green cement

    Energy Technology Data Exchange (ETDEWEB)

    Cumming, R. [Lafarge Canada Inc., Calgary, AB (Canada)

    2006-07-01

    Lafarge examined the use of waste biomass products in its building materials and provided background information on its operations. Cement kiln infrastructure was described in terms of providing access to shipping, rail and highways; conveying and off-loading equipment; having large storage facilities; and, offering continuous monitoring and stack testing. The presentation identified the advantages and disadvantages of a few different biomass cases such as coal; scrap tires; non-recyclable household waste; and processed biomass. A chart representing landfill diversion rates was presented and the presentation concluded with a discussion of energy recovery and recycling. 1 tab., figs.

  1. Deformation and stress in PMMA during hard X-ray exposure for deep lithography

    International Nuclear Information System (INIS)

    Moldovan, N.

    1999-01-01

    The availability of high-energy, high-flux, collimated synchrotrons radiation has extended the application of deep X-ray lithography (DXRL) to thickness values of the PMMA resist of several millimeters. Some of the most severe limitations come from plastic deformation, stress, and cracks induced in PMMA during exposure and development. We have observed and characterized these phenomena quantitatively. Profilometry measurements revealed that the PMMA is subjected either to local shrinkage or to expansion, while compression and expansion evolve over time. Due to material loss and crosslinking, the material undergoes a shrinkage, while the radiation-induced decomposition generates gases expanding the polymer matrix. The overall dynamics of the material microrelief and stress during and after the exposure depend on the balance between compaction and outgassing. These depend in turn on the exposure conditions (spectrum; dose, dose rate, seaming, temperature), post-exposure storage conditions, PMMA material properties and thickness, and also on the size and geometry of the exposed patterns

  2. Structural, optical and photo thermal properties of Er3+:Y2O3 doped PMMA nanocomposite

    Science.gov (United States)

    Tabanli, Sevcan; Eryurek, Gonul

    2018-02-01

    Thermal decomposition technique was employed to synthesize of phosphors of yttria (Y2O3) doped with erbium (Er3+) ions. After the synthesized procedure, the nano-sized crystalline powders were annealed at 800oC for 24 h. Annealed powders were embedded in poly(methyl methacrylate) (PMMA) by free radical polymerization to fabricate nanocomposite polymer materials. The crystalline structure of the powder and doped PMMA nanocomposite samples were determined using X-ray diffraction technique. Scherrer's equation and the FW1/5/4/5M method were used to determine average crystalline size and grain size distributions, respectively. The spectroscopic properties of the powders and doped PMMA nanocomposites were studied by measuring the upconversion emission spectra under near-infrared laser excitation at room temperature. The laser-induced photo thermal behaviors of Er3+:Y2O3 nano-powders and doped PMMA nanocomposite were investigated using the fluorescence intensity ratio (FIR) technique.

  3. Printed wax masks for 254 nm deep-UV pattering of PMMA-based microfluidics

    KAUST Repository

    Fan, Yiqiang

    2012-01-13

    This paper reports a new technique for masking deep-UV exposure of poly(methyl methacrylate) (PMMA) using a printed wax mask. This technique provides an inexpensive and bulk fabrication method for PMMA structures. The technique involves the direct printing of the mask onto a polymer sheet using a commercial wax printer. The wax layer was then transferred to a PMMA substrate using a thermal laminator, exposed using deep-UV (with a wavelength of 254 nm), developed in an IPA:water solution, and completed by bonding on a PMMA cap layer. A sample microfluidic device fabricated with this method is also presented, with the microchannel as narrow as 50 μm. The whole process is easy to perform without the requirement for any microfabrication facilities. © 2012 IOP Publishing Ltd.

  4. Microwave-assisted activation for electroless nickel plating on PMMA microspheres

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Yen-Chung [Graduate School of Defense Science, Chung Cheng Institute of Technology, National Defense University, Tao-Yuan, Taiwan 335 (China); Materials and Electro-optics Research Division, Chung Shan Institute of Science and Technology, Tao-Yuan, Taiwan 325 (China); Liu, Robert Lian-Huey [Graduate School of Defense Science, Chung Cheng Institute of Technology, National Defense University, Tao-Yuan, Taiwan 335 (China); Department of Chemical and Materials Engineering, Minghsin University of Science and Technology, Hsinchu Taiwan 304 (China); Chen, Xin-Liang [Graduate School of Defense Science, Chung Cheng Institute of Technology, National Defense University, Tao-Yuan, Taiwan 335 (China); Shu, Hsiou-Jeng [Materials and Electro-optics Research Division, Chung Shan Institute of Science and Technology, Tao-Yuan, Taiwan 325 (China); Ger, Ming-Der, E-mail: mingderger@gmail.com [Department of Chemical and Materials Engineering, Chung Cheng Institute of Technology, National Defense University, Tao-Yuan, Taiwan 335 (China)

    2011-05-15

    A novel microwave-assisted activation method for electroless plating on PMMA microspheres is presented in this study. When the microwave irradiation was applied during the activation step, the amount of the Pd species adsorbed on PMMA surfaces was much higher than that of sample pretreated with a conventional activation process without microwave irradiation. With this activation method, it was also shown that the adsorbed Pd species with a size of 4-6 nm were uniformly distributed on the surfaces of the PMMA microspheres, thus a smooth and uniform nickel-phosphorus coating on the PMMA microspheres was obtained by subsequent electroless plating. The samples after each step were characterized by XPS, TEM, ICP and SEM.

  5. Characterisation and vapour sensing properties of spin coated thin films of anthracene labelled PMMA polymer

    Energy Technology Data Exchange (ETDEWEB)

    Capan, I., E-mail: inci.capan@gmail.com [Balikesir University, Faculty of Art and Sciences, Department of Physics, Cagis Campus, 10145 Balikesir (Turkey); Tarimci, C., E-mail: Celik.Tarimci@eng.ankara.edu.tr [Ankara University, Faculty of Engineering, Department of Engineering Physics, 06100, Ankara (Turkey); Erdogan, M., E-mail: merdogan@balikesir.edu.tr [Balikesir University, Faculty of Art and Sciences, Department of Physics, Cagis Campus, 10145 Balikesir (Turkey); Hassan, A.K., E-mail: A.Hassan@shu.ac.uk [Materials and Engineering Research Institute, Sheffield Hallam University, Sheaf Building, Pond Street, Sheffield S1 1WB (United Kingdom)

    2009-05-05

    In the present article thin films of poly (methyl methacrylate) (PMMA) polymer labelled with anthracene (Ant-PMMA) prepared by spin coating are characterised by UV-visible spectroscopy, surface plasmon resonance (SPR), spectroscopic ellipsometry (SE) and Atomic Force Microscopy (AFM) and their organic vapour sensing properties are investigated. Ant-PMMA films' thickness are determined by performing theoretical fitting to experimental data measured using SPR and SE. Results obtained show that the spin-cast films are of good uniformity with an average thickness of 6-8 nm. Organic vapour sensing properties are studied using SPR technique during exposures to different volatile organic compounds (VOCs). Ant-PMMA films' response to the selected VOCs has been examined in terms of solubility parameters and molar volumes of the solvents, and the films were found to be largely sensitive to benzene vapour compared to other studied analytes.

  6. Characterisation and vapour sensing properties of spin coated thin films of anthracene labelled PMMA polymer

    International Nuclear Information System (INIS)

    Capan, I.; Tarimci, C.; Erdogan, M.; Hassan, A.K.

    2009-01-01

    In the present article thin films of poly (methyl methacrylate) (PMMA) polymer labelled with anthracene (Ant-PMMA) prepared by spin coating are characterised by UV-visible spectroscopy, surface plasmon resonance (SPR), spectroscopic ellipsometry (SE) and Atomic Force Microscopy (AFM) and their organic vapour sensing properties are investigated. Ant-PMMA films' thickness are determined by performing theoretical fitting to experimental data measured using SPR and SE. Results obtained show that the spin-cast films are of good uniformity with an average thickness of 6-8 nm. Organic vapour sensing properties are studied using SPR technique during exposures to different volatile organic compounds (VOCs). Ant-PMMA films' response to the selected VOCs has been examined in terms of solubility parameters and molar volumes of the solvents, and the films were found to be largely sensitive to benzene vapour compared to other studied analytes.

  7. Printed wax masks for 254 nm deep-UV pattering of PMMA-based microfluidics

    International Nuclear Information System (INIS)

    Fan, Yiqiang; Liu, Yang; Li, Huawei; Foulds, Ian G

    2012-01-01

    This paper reports a new technique for masking deep-UV exposure of poly(methyl methacrylate) (PMMA) using a printed wax mask. This technique provides an inexpensive and bulk fabrication method for PMMA structures. The technique involves the direct printing of the mask onto a polymer sheet using a commercial wax printer. The wax layer was then transferred to a PMMA substrate using a thermal laminator, exposed using deep-UV (with a wavelength of 254 nm), developed in an IPA:water solution, and completed by bonding on a PMMA cap layer. A sample microfluidic device fabricated with this method is also presented, with the microchannel as narrow as 50 µm. The whole process is easy to perform without the requirement for any microfabrication facilities. (technical note)

  8. Porous asymmetric SiO2-g-PMMA nanoparticles produced by phase inversion

    KAUST Repository

    Munirasu, Selvaraj; Nunes, Suzana Pereira

    2014-01-01

    of functionalized nanoparticles in different solvents and immersion in water. The resulting asymmetrically porous morphology and nanoparticle assembly was characterized by scanning electron and atomic force microscopy. The PMMA functionalized SiO2 hybrid material

  9. Process of preparing hydraulic cement

    Energy Technology Data Exchange (ETDEWEB)

    1919-12-11

    A process of preparing hydraulic cement from oil shale or shale coke is characterized in that the oil shale or shale coke after the distillation is burned long and hot to liberate the usual amount of carbonic acid and then is fine ground to obtain a slow hardening hydraulic cement.

  10. Health hazards of cement dust

    International Nuclear Information System (INIS)

    Meo, Sultan A.

    2004-01-01

    ven in the 21st century, millions of people are working daily in a dusty environment. They are exposed to different types of health hazards such as fume, gases and dust, which are risk factors in developing occupational disease. Cement industry is involved in the development of structure of this advanced and modern world but generates dust during its production. Cement dust causes lung function impairment, chronic obstructive lung disease, restrictive lung disease, pneumoconiosis and carcinoma of the lungs, stomach and colon. Other studies have shown that cement dust may enter into the systemic circulation and thereby reach the essentially all the organs of body and affects the different tissues including heart, liver, spleen, bone, muscles and hairs and ultimately affecting their micro-structure and physiological performance. Most of the studies have been previously attempted to evaluate the effects of cement dust exposure on the basis of spirometry or radiology, or both. However, collective effort describing the general effects of cement dust on different organ and systems in humans or animals, or both has not been published. Therefore, the aim of this review is to gather the potential toxic effects of cement dust and to minimize the health risks in cement mill workers by providing them with information regarding the hazards of cement dust. (author)

  11. Ceramic microspheres for cementing applications

    NARCIS (Netherlands)

    2011-01-01

    A method and apparatus for manufacturing ceramic microspheres from industrial slag. The microspheres have a particle size of about 38 microns to about 150 microns. The microspheres are used to create a cement slurry having a density of at least about 11 lbs/g. The resultant cement slurry may then be

  12. Ceramic microspheres for cementing applications

    NARCIS (Netherlands)

    2010-01-01

    A method and apparatus for manufacturing ceramic microspheres from industrial slag. The microspheres have a particle size of about 38 microns to about 150 microns. The microspheres are used to create a cement slurry having a density of at least about 11 lbs/g. The resultant cement slurry may then be

  13. Ceramic microspheres for cementing applications

    NARCIS (Netherlands)

    2012-01-01

    A method and apparatus for manufacturing ceramic microspheres from industrial slag. The microspheres have a particle size of about 38 microns to about 150 microns. The microspheres are used to create a cement slurry having a density of at least about 11 lbs/g. The resultant cement slurry may then be

  14. Influence of Graphene Oxide on the Tribological and Electrical Properties of PMMA Composites

    Directory of Open Access Journals (Sweden)

    Jiale Song

    2013-01-01

    Full Text Available The graphene oxide (GO was obtained by Hummers' method using natural graphite as raw materials. Then, the GO/poly(methyl methacrylate (PMMA nanocomposites were prepared by in situ polymerization. The tribological and electrical properties of nanocomposites were studied. As a result, the frictional coefficient of GO/PMMA nanocomposites was prominently improved with the content of the graphene oxide increasing. The electrical properties of nanocomposites were slightly increased when adding the graphene oxide.

  15. Comparative study between optical densitometry and spectrophotometry for evaluation of PMMA dosimeters

    International Nuclear Information System (INIS)

    Louback, Luana Trevenzoli; Meira-Belo, Luiz C.

    2011-01-01

    The use of dosimetric systems based on color changes in PMMA is standardized by ISO/ASTM 51276:2002(E). In a general way, the evaluation of doses in these materials is done correlating the optical absorbance of the material and the absorbed dose. Usually, the absorbance is measured using a spectrophotometer at a wavelength suitably chosen. In the present work, it was performed a comparative study between the techniques of spectrophotometry and optical densitometry in dyed PMMA dosimeters type Harwell RED 4034 and PMMA samples commercially available in Brazil. The main results of this study were the determination of the radiochromic response for different samples of PMMA and the determination of the calibration conditions using a 60 Co beam. The studied materials are suitable for use as routine dosimeters, covering the range of the 500Gy to 100kGy. A direct comparison between the red dyed PMMA and the Harwell RED 4034 Perspex showed that the stabilization time and the fading of the radiochromic information in red dyed PMMA samples is higher than in RED 4034. However, both effects occur on period of weeks, which does not preclude its routine use. Furthermore, the increase in absorbance due to exposure to radiation, determined by the difference between specific absorbance of the irradiated sample and a non-irradiated one, is significantly higher in PMMA with red dyed that the RED 4034. In fact, the amplitude of absorbance peak of a sample irradiated with red dyed PMMA 2kGy and read at 602nm has the same order of magnitude from a peak of RED 4034 irradiated with 10 kGy and read at 640nm. A direct consequence of this fact is the real possibility of using simpler equipment (optical densitometer in this case) to measure the optical absorbance and evaluates the absorbed dose. (author)

  16. Incorporation of fluconazole in copolymer PMMA-g-PEG derivatives; Incorporacao de fluconazol em ineditos derivados do copolimero PMMA-g-PEG

    Energy Technology Data Exchange (ETDEWEB)

    Silveira, B.M.; Santos, V.M.R. dos; Novack, K.M.; Lopes, S.A., E-mail: vmrebello@yahoo.com.br [Universidade Federal de Ouro Preto (UFOP), MG (Brazil)

    2014-07-01

    The graft copolymer PMMA-g-PEG went through chemical transformations in its chain through acetylation, halogenation, methylation and esterification followed by hydrolysis reactions. Subsequently, the copolymer PMMA-g-PEG derivatives passed through the process of emulsification and incorporation of the drug fluconazole. Derivatives copolymers were characterized by infrared spectroscopy (FTIR), X-ray diffraction (XRD) and scanning electron microscopy (SEM) after incorporation in order to evaluate their effectiveness. The efficiency of incorporation was observed and it was also verified that the complexity of polymer chain influence in the incorporated fluconazole content. (author)

  17. Corrosion resistant cemented carbide

    International Nuclear Information System (INIS)

    Hong, J.

    1990-01-01

    This paper describes a corrosion resistant cemented carbide composite. It comprises: a granular tungsten carbide phase, a semi-continuous solid solution carbide phase extending closely adjacent at least a portion of the grains of tungsten carbide for enhancing corrosion resistance, and a substantially continuous metal binder phase. The cemented carbide composite consisting essentially of an effective amount of an anti-corrosion additive, from about 4 to about 16 percent by weight metal binder phase, and with the remaining portion being from about 84 to about 96 percent by weight metal carbide wherein the metal carbide consists essentially of from about 4 to about 30 percent by weight of a transition metal carbide or mixtures thereof selected from Group IVB and of the Periodic Table of Elements and from about 70 to about 96 percent tungsten carbide. The metal binder phase consists essentially of nickel and from about 10 to about 25 percent by weight chromium, the effective amount of an anti-corrosion additive being selected from the group consisting essentially of copper, silver, tine and combinations thereof

  18. Polymeric phase change nanocomposite (PMMA/Fe:ZnO) for electronic packaging application

    Science.gov (United States)

    Maji, Pranabi; Choudhary, Ram Bilash; Majhi, Malati

    2018-01-01

    This paper reported the effect of Fe-doped ZnO (Fe:ZnO) nanoparticles on the structural, morphological, thermal, optical and dielectric properties of PMMA matrix. Fe-doped ZnO nanoparticle was synthesized by co-precipitation method, after its surface modification incorporated into the PMMA matrix by free radical polymerization method. The phase analysis and crystal structure were investigated by XRD and FTIR technique. These studies confirmed the chemical structure of the PMMA/Fe:ZnO nanocomposite. FESEM image showed the pyramidal shape and high porosity of PMMA/Fe:ZnO nanocomposite. Thermal analysis of the sample was carried out by thermo-gravimetric analyzer. PMMA/Fe:ZnO nanocomposite was found to have better thermal stability compared to pure one. Broadband dielectric spectroscopic technique was used to investigate the transition of electrical properties of Fe-doped ZnO nanoparticle reinforced PMMA matrix in temperature range 313-373 K. The results elucidated a phase transition from glassy to rubbery state at 344 K.

  19. Influence of Doping Concentration on Dielectric, Optical, and Morphological Properties of PMMA Thin Films

    Directory of Open Access Journals (Sweden)

    Lyly Nyl Ismail

    2012-01-01

    Full Text Available PMMA thin films were deposited by sol gel spin coating method on ITO substrates. Toluene was used as the solvent to dissolve the PMMA powder. The PMMA concentration was varied from 30 ~ 120 mg. The dielectric properties were measured at frequency of 0 ~ 100 kHz. The dielectric permittivity was in the range of 7.3 to 7.5 which decreased as the PMMA concentration increased. The dielectric loss is in the range of 0.01 ~ –0.01. All samples show dielectric characteristics which have dielectric loss is less than 0.05. The optical properties for thin films were measured at room temperature across 200 ~ 1000 nm wavelength region. All samples are highly transparent. The energy band gaps are in the range of 3.6 eV to 3.9 eV when the PMMA concentration increased. The morphologies of the samples show that all samples are uniform and the surface roughness increased as the concentration increased. From this study, it is known that, the dielectric, optical, and morphology properties were influenced by the amount of PMMA concentration in the solution.

  20. Studying of Perovskite Nanoparticles in PMMA Matrix Used As Light Converter for Silicon Solar Cell

    Directory of Open Access Journals (Sweden)

    Lipiński M.

    2017-09-01

    Full Text Available The nanoparticles of CH3NH3PbBr3 hybrid perovskites were synthesized. These perovskite nanoparticles we embedded in polymethyl methacrylate (PMMA in order to obtain the composite, which we used as light converter for silicon solar cells. It was shown that the composite emit the light with the intensity maximum at about 527 nm when exited by a short wavelength (300÷450 nm of light. The silicon solar cells were used to examine the effect of down-conversion (DC process by perovskite nanoparticles embedded in PMMA. For experiments, two groups of monocrystalline silicon solar cells were used. The first one included the solar cells without surface texturization and antireflection coating. The second one included the commercial cells with surface texturization and antireflection coating. In every series of the cells one part of the cells were covered by composite (CH3NH3PbBr3 in PMMA layer and second part of cells by pure PMMA for comparison. It was shown that External Quantum Efficiency EQE of the photovoltaic cells covered by composite (CH3NH3PbBr3 in PMMA layer was improved in both group of the cells but unfortunately the Internal Quantum Efficiency was reduced. This reduction was caused by high absorption of the short wavelength light and reabsorption of the luminescence light. Therefore, the CH3NH3PbBr3 perovskite nanoparticles embedded in PMMA matrix were unable to increase silicon solar cell efficiency in the tested systems.

  1. Two dimensional PMMA nanofluidic device fabricated by hot embossing and oxygen plasma assisted thermal bonding methods

    Science.gov (United States)

    Yin, Zhifu; Sun, Lei; Zou, Helin; Cheng, E.

    2015-05-01

    A method for obtaining a low-cost and high-replication precision two-dimensional (2D) nanofluidic device with a polymethyl methacrylate (PMMA) sheet is proposed. To improve the replication precision of the 2D PMMA nanochannels during the hot embossing process, the deformation of the PMMA sheet was analyzed by a numerical simulation method. The constants of the generalized Maxwell model used in the numerical simulation were calculated by experimental compressive creep curves based on previously established fitting formula. With optimized process parameters, 176 nm-wide and 180 nm-deep nanochannels were successfully replicated into the PMMA sheet with a replication precision of 98.2%. To thermal bond the 2D PMMA nanochannels with high bonding strength and low dimensional loss, the parameters of the oxygen plasma treatment and thermal bonding process were optimized. In order to measure the dimensional loss of 2D nanochannels after thermal bonding, a dimension loss evaluating method based on the nanoindentation experiments was proposed. According to the dimension loss evaluating method, the total dimensional loss of 2D nanochannels was 6 nm and 21 nm in width and depth, respectively. The tensile bonding strength of the 2D PMMA nanofluidic device was 0.57 MPa. The fluorescence images demonstrate that there was no blocking or leakage over the entire microchannels and nanochannels.

  2. Optical properties of Sr3B2O6:Dy3+/PMMA polymer nanocomposites

    Science.gov (United States)

    Khursheed, Sumara; Kumar, Vinay; Singh, Vivek K.; Sharma, Jitendra; Swart, H. C.

    2018-04-01

    The paper presents a facile way to synthesize luminescent polymer nanocomposite (PNC) films consisting of nanophosphors (NPs) of rare earth ions doped alkaline earth borates (Sr3B2O6:Dy3+) dispersed in a polymer (PMMA) matrix via a solution casting method and the results of their detailed structural and optical properties measurements. The PNC films were characterized using X-ray diffraction (XRD), Photoluminescence (PL), and differential scanning calorimetry (DSC). The crystallinity of the dispersed NPs did not suffer on account of being dispersed in the PMMA. The Rhombohedral structure and the formation of a single phase of Sr3B2O6:Dy3+ were confirmed by the XRD data of both the NP powders and the PNC films with an average particle size of 43 nm. Also, the observed PL emission and excitation spectra of the PNC films amply suggested that embedding of the nanophosphors in the PMMA matrix preserves their typical luminescence emission. The chromaticity coordinates (x = 0.37, y = 0.39) of the PNC films also validated the yellowish white emission of the nanophosphor. DSC scans on the PMMA only and the Sr3B2O6:Dy3+/PMMA films suggested an increase in the thermal stability of the PNC films as compared to pure PMMA although no significant change in the glass transition temperature was observed.

  3. Adhesion of Candida albicans to Vanillin Incorporated Self-Curing Orthodontic PMMA Resin.

    Science.gov (United States)

    Zam, K.; Sawaengkit, P.; Thaweboon, S.; Thaweboon, B.

    2018-02-01

    It has been observed that there is an increase in Candida carriers during the treatment with orthodontic removable appliance. Vanillin is flavouring agent, which is known to have antioxidant and antimicrobial properties. The aim of this study was to evaluate the effect of vanillin incorporated PMMA on adhesion of Candida albicans. A total of 36 orthodontic self-curing PMMA resin samples were fabricated. The samples were divided into 3 groups depending on percentage of vanillin incorporated (0.1%, 0.5% and PMMA without vanillin as control). PMMA samples were coated with saliva. The adhesion assay was performed with C. albicans (ATCC 10231). The adherent yeast cells were stained with crystal violet and counted under microscope by random selection of 3 fields at 10X magnification. The statistical analyses performed by Kruskal Wallis and Mann Whitney non-parametric test. It was found that the PMMA resin samples with vanillin incorporation significantly reduced the adhesion of C. albicans as compared to the control group. This study indicates that vanillin incorporated resin can impede the adhesion of C. albicans to about 45 - 56 %. With further testing and development, vanillin can be employed as an antifungal agent to prevent adhesion of C. albicans to orthodontic self-curing PMMA resin.

  4. Enhancement in insulation and mechanical properties of PMMA nanocomposite foams infused with multi-walled carbon nanotubes.

    Science.gov (United States)

    Yeh, Jui-Ming; Chang, Kung-Chin; Peng, Chih-Wei; Lai, Mei-Chun; Hwang, Shyh-Shin; Lin, Hong-Ru; Liou, Shir-Joe

    2011-08-01

    In this study, PMMA/CNTs composite materials with carboxyl-multi walled carbon nanotubes (c-MWNTs) or untreated MWNTs were prepared via in-situ bulk polymerization. The as-prepared PMMA/CNTs composite materials were then characterized by Fourier-Transformation infrared (FTIR) spectroscopy, and transmission electron microscopy (TEM). The molecular weights of PMMA extracted from PMMA/CNTs composite materials and bulk PMMA were determined by gel permeation chromatography (GPC) with THF used as the eluant. The PMMA/CNTs composite materials were used to produce foams by a batch process in an autoclave using nitrogen as foaming agent. The cellular microstructure, insulation and compressive mechanical properties of PMMA/CNTs composite foams were also investigated in detail. Compared to neat PMMA foam, the presence of CNTs increases in cell density and reduces cell size. The insulation and compressive mechanical properties of PMMA/CNTs composite foams were found to improve substantially those of neat PMMA foam. In particular, 22.6% decrease in thermal conductivity, 19.7% decrease in dielectric constant and 160% increase in compressive modulus were observed with the addition of 0.3 wt% carboxyl-multi walled carbon nanotubes (c-MWNTs).

  5. Investigation of optical properties of Ag: PMMA nanocomposite structures

    Science.gov (United States)

    Ponelyte, S.; Palevicius, A.; Guobiene, A.; Puiso, J.; Prosycevas, I.

    2010-05-01

    In the recent years fundamental research involving the nanodimensional materials has received enormous momentum for observing and understanding new types of plasmonic materials and their physical phenomena occurring in the nanoscale. Mechanical and optical properties of these polymer based nanocomposite structures depend not only on type, dimensions and concentration of filler material, but also on a kind of polymer matrix used. By proper selection of polymer matrix and nanofillers, it is possible to engineer nanocomposite materials with certain favorable properties. One of the most striking features of nanocomposite materials is that they can expose unique optical properties that are not intrinsic to natural materials. In these researches, nanocomposite structures were formed using polymer (PMMA) as a matrix, and silver nanoparticles as fillers. By hot embossing procedure a diffraction grating was imprinted on formed layers. The effect of UV exposure time on nanocomposite structures morphology, optical (diffraction effectiveness, absorbance) and mechanical properties was investigated. Results were confirmed by UV-VIS spectrometer, Laser Diffractometer, PMT- 3 and AFM. Investigations proposed new nanocomposite structures as plasmonic materials with improved optical and mechanical properties, which may be applied for a number of technological applications: micro-electro-mechanical devices, optical devices, various plasmonic sensors, or even in DNA nanotechnology.

  6. Alternative PMB produced from recycling waste PMMA/ATH

    Directory of Open Access Journals (Sweden)

    Marjan TUŠAR

    2014-06-01

    Full Text Available With development of production processes in refineries production of bitumen is decreasing, as well as the quality of produced bitumen. On the market this brings increased demand for bitumen accompanied by the demand for additives to improve such low quality bitumen. Many different types of additives are used, but most commonly SBS is added. Usage of additives bring additional direct costs, due to market price of additives and indirect cost due to adjustments in the technological process as such as additional mixing device in bitumen tanks, elevated temperature of asphalt or prolongation in mixing time. A topic of our research was development low price asphalt additive from waste poly-methyl methacrylate filled with a fine dispersion aluminium trihydrate (PMMA/ATH. Additionally with paraffin wax it was used as modifying agents for 70/100 paving grade bitumen. With regard to performance of modified asphalt mixtures, it was found that both additives considerably reduce moisture susceptibility and formation of ruts. With laboratory tests and field trial we found that combined technology PMA (polymer modified asphalt and WMA (warm mix asphalt technologies resulted in optimized production and excellent performance of pavement material.

  7. Solvent Bonding for Fabrication of PMMA and COP Microfluidic Devices.

    Science.gov (United States)

    Wan, Alwin M D; Moore, Thomas A; Young, Edmond W K

    2017-01-17

    Thermoplastic microfluidic devices offer many advantages over those made from silicone elastomers, but bonding procedures must be developed for each thermoplastic of interest. Solvent bonding is a simple and versatile method that can be used to fabricate devices from a variety of plastics. An appropriate solvent is added between two device layers to be bonded, and heat and pressure are applied to the device to facilitate the bonding. By using an appropriate combination of solvent, plastic, heat, and pressure, the device can be sealed with a high quality bond, characterized as having high bond coverage, bond strength, optical clarity, durability over time, and low deformation or damage to microfeature geometry. We describe the procedure for bonding devices made from two popular thermoplastics, poly(methyl-methacrylate) (PMMA), and cyclo-olefin polymer (COP), as well as a variety of methods to characterize the quality of the resulting bonds, and strategies to troubleshoot low quality bonds. These methods can be used to develop new solvent bonding protocols for other plastic-solvent systems.

  8. Synthesis and characterization of Supeparamagnetics Microspheres (PMMA via suspension polymerization

    Directory of Open Access Journals (Sweden)

    Paulo Emilio Feuser

    2014-02-01

    Full Text Available Magnetics nanoparticles (NPMs has found many applications in biomedical and technological areas. The objective of this work is the preparation and characterization of PMMA microspheres containing NPMs coated with oleic acid (NPMs-AO. For the preparation of MNPs-AO was used the coprecipitation method in an aqueous medium. For the preparation of the superparamagnetic microspheres used in suspension polymerization technique. The microspheres showed a size distribution particles of approximately 150um and a spherical morphology. From the analysis of gel permeation chromatography (GPC determined the number average molecular weight (Mw of the magnetics microspheres and there was a variation in the Mw depending on the concentration of MNPs-AO in this reaction. To analyze the magnetic properties used the vibrating sample magnetometer (MAV. The microspheres showed superparamagnetic properties and a value of saturation magnetization (Ms of about 8 emu/g MNPs. Therefore you can conclude that it is possible to obtain superparamagnetics microspheres for a particular application, either, biomedical or technological.

  9. Low modulus Ti–Nb–Hf alloy for biomedical applications

    Energy Technology Data Exchange (ETDEWEB)

    González, M., E-mail: Marta.Gonzalez.Colominas@upc.edu [Department of Materials Science and Metallurgy, Universitat Politècnica de Catalunya (UPC), Avda. Diagonal 647, 08028 Barcelona (Spain); Materials Science, Elisava Escola Superior de Disseny i Enginyeria de Barcelona, La Rambla 30-32, 08002 Barcelona (Spain); Peña, J. [Department of Materials Science and Metallurgy, Universitat Politècnica de Catalunya (UPC), Avda. Diagonal 647, 08028 Barcelona (Spain); Materials Science, Elisava Escola Superior de Disseny i Enginyeria de Barcelona, La Rambla 30-32, 08002 Barcelona (Spain); Gil, F.J.; Manero, J.M. [Department of Materials Science and Metallurgy, Universitat Politècnica de Catalunya (UPC), Avda. Diagonal 647, 08028 Barcelona (Spain); Ciber-BBN (Spain)

    2014-09-01

    β-Type titanium alloys with a low elastic modulus are a potential strategy to reduce stress shielding effect and to enhance bone remodeling in implants used to substitute failed hard tissue. For biomaterial application, investigation on the mechanical behavior, the corrosion resistance and the cell response is required. The new Ti25Nb16Hf alloy was studied before and after 95% cold rolling (95% C.R.). The mechanical properties were determined by tensile testing and its corrosion behavior was analyzed by potentiostatic equipment in Hank's solution at 37 °C. The cell response was studied by means of cytotoxicity evaluation, cell adhesion and proliferation measurements. The stress–strain curves showed the lowest elastic modulus (42 GPa) in the cold worked alloy and high tensile strength, similar to that of Ti6Al4V. The new alloy exhibited better corrosion resistance in terms of open circuit potential (E{sub OCP}), but was similar in terms of corrosion current density (i{sub CORR}) compared to Ti grade II. Cytotoxicity studies revealed that the chemical composition of the alloy does not induce cytotoxic activity. Cell studies in the new alloy showed a lower adhesion and a higher proliferation compared to Ti grade II presenting, therefore, mechanical features similar to those of human cortical bone and, simultaneously, a good cell response. - Highlights: • Presents low elastic modulus and high strength and elastic deformability. • Exhibits good biocompatibility in terms of cytotoxicity and cell response. • Corrosion resistance of this alloy is good, similar to that of Ti grade II. • Potential candidate for implants used to substitute failed hard tissue.

  10. 21 CFR 888.4200 - Cement dispenser.

    Science.gov (United States)

    2010-04-01

    ... 21 Food and Drugs 8 2010-04-01 2010-04-01 false Cement dispenser. 888.4200 Section 888.4200 Food... DEVICES ORTHOPEDIC DEVICES Surgical Devices § 888.4200 Cement dispenser. (a) Identification. A cement dispenser is a nonpowered syringe-like device intended for use in placing bone cement (§ 888.3027) into...

  11. A cement based syntactic foam

    International Nuclear Information System (INIS)

    Li Guoqiang; Muthyala, Venkata D.

    2008-01-01

    In this study, a cement based syntactic foam core was proposed and experimentally investigated for composite sandwich structures. This was a multi-phase composite material with microballoon dispersed in a rubber latex toughened cement paste matrix. A trace amount of microfiber was also incorporated to increase the number of mechanisms for energy absorption and a small amount of nanoclay was added to improve the crystal structure of the hydrates. Three groups of cement based syntactic foams with varying cement content were investigated. A fourth group of specimens containing pure cement paste were also prepared as control. Each group contained 24 beam specimens. The total number of beam specimens was 96. The dimension of each beam was 30.5 cm x 5.1 cm x 1.5 cm. Twelve foam specimens from each group were wrapped with plain woven 7715 style glass fabric reinforced epoxy to prepare sandwich beams. Twelve cubic foam specimens, three from each group, with a side length of 5.1 cm, were also prepared. Three types of testing, low velocity impact test and four-point bending test on the beam specimens and compression test on the cubic specimens, were conducted to evaluate the impact energy dissipation, stress-strain behavior, and residual strength. Scanning electron microscope (SEM) was also used to examine the energy dissipation mechanisms in the micro-length scale. It was found that the cement based syntactic foam has a higher capacity for dissipating impact energy with an insignificant reduction in strength as compared to the control cement paste core. When compared to a polymer based foam core having similar compositions, it was found that the cement based foam has a comparable energy dissipation capacity. The developed cement based syntactic foam would be a viable alternative for core materials in impact-tolerant composite sandwich structures

  12. Crown and bridge cements: clinical applications.

    Science.gov (United States)

    Bunek, Sabiha S; Powers, John M

    2012-12-01

    Cement selection can be confusing because factors such as substrate, the type of restoration, and patient needs must be considered. Some substrates require additional treatment before cementation. This article describes the most commonly used traditional crown and bridge cements (GI and RMGI) used for metal and metal-ceramic restorations, and resin cements used for all-ceramic restorations. Advantages, disadvantages, indications, and contraindications of cements have been reviewed. Recommended uses of cements for metal, ceramic, and laboratory composite restorations have been presented. General guidelines for surface treatment ot silica- and zirconia-based restorations when using resin cements have been discussed.

  13. Cement/slag chemistry studies

    International Nuclear Information System (INIS)

    Glasser, F.P.; Macphee, D.; Atkins, M.; Beckley, N.; Carson, S.O.; Wilding, C.R.; McHugh, G.

    1988-01-01

    The performance of cement-based matrices intended for radwaste immobilization is assessed. The long-term performance of the matrix is characterized by thermodynamic evaluation of experimental data. The results are presented in a general form, amenable to a range of specific formulations. The interaction of specific radwaste components with cements has been studied, using Iodine as an example. It occurs as both I - and IO 3 - species, but these differ sharply in sorption characteristics. The effect of ionizing radiation of the pH and E h of cement matrices is reported. (author)

  14. Cements in Radioactive Waste Disposal

    International Nuclear Information System (INIS)

    Glasser, F.P.

    2013-01-01

    The use of cement and concrete to immobilise radioactive waste is complicated by the wide- ranging nature of inorganic cementing agents available as well as the range of service environments in which cement is used and the different functions expected of cement. For example, Portland cement based concretes are widely used as structural materials for construction of vaults and tunnels. These constructions may experience a long pre-closure performance lifetime during which they are required to protect against collapse and ingress of water: strength and impermeability are key desirable characteristics. On the other hand, cement and concrete may be used to form backfills, ranging in permeability. Permeable formulations allow gas readily to escape, while impermeable barriers retard radionuclide transport and reduce access of ground water to the waste. A key feature of cements is that, while fresh, they pass through a fluid phase and can be formed into any shape desired or used to infiltrate other materials thereby enclosing them into a sealed matrix. Thereafter, setting and hardening is automatic and irreversible. Where concrete is used to form structural elements, it is also natural to use cement in other applications as it minimises potential for materials incompatibility. Thus cement- mainly Portland cement- has been widely used as an encapsulant for storage, transport and as a radiation shield for active wastes. Also, to form and stabilise structures such as vaults and silos. Relative to other potential matrices, cement also has a chemical immobilisation potential, reacting with and binding with many radionuclides. The chemical potential of cements is essentially sacrificial, thus limiting their performance lifetime. However performance may also be required in the civil engineering sense, where strength is important, so many factors, including a geochemical description of service conditions, may require to be assessed in order to predict performance lifetime. The

  15. Cements in Radioactive Waste Disposal

    Energy Technology Data Exchange (ETDEWEB)

    Glasser, F. P. [University of Aberdeen, Scotland (United Kingdom)

    2013-09-15

    The use of cement and concrete to immobilise radioactive waste is complicated by the wide- ranging nature of inorganic cementing agents available as well as the range of service environments in which cement is used and the different functions expected of cement. For example, Portland cement based concretes are widely used as structural materials for construction of vaults and tunnels. These constructions may experience a long pre-closure performance lifetime during which they are required to protect against collapse and ingress of water: strength and impermeability are key desirable characteristics. On the other hand, cement and concrete may be used to form backfills, ranging in permeability. Permeable formulations allow gas readily to escape, while impermeable barriers retard radionuclide transport and reduce access of ground water to the waste. A key feature of cements is that, while fresh, they pass through a fluid phase and can be formed into any shape desired or used to infiltrate other materials thereby enclosing them into a sealed matrix. Thereafter, setting and hardening is automatic and irreversible. Where concrete is used to form structural elements, it is also natural to use cement in other applications as it minimises potential for materials incompatibility. Thus cement- mainly Portland cement- has been widely used as an encapsulant for storage, transport and as a radiation shield for active wastes. Also, to form and stabilise structures such as vaults and silos. Relative to other potential matrices, cement also has a chemical immobilisation potential, reacting with and binding with many radionuclides. The chemical potential of cements is essentially sacrificial, thus limiting their performance lifetime. However performance may also be required in the civil engineering sense, where strength is important, so many factors, including a geochemical description of service conditions, may require to be assessed in order to predict performance lifetime. The

  16. Characterization and bacterial anti-adherent effect on modified PMMA denture acrylic resin containing platinum nanoparticles.

    Science.gov (United States)

    Nam, Ki-Young

    2014-06-01

    This study characterized the synthesis of a modified PMMA (Polymethyl methacrylate) denture acrylic loading platinum nanoparticles (PtN) and assessed its bacterial inhibitory efficacy to produce novel antimicrobial denture base material. Polymerized PMMA denture acrylic disc (20 mm × 2 mm) specimens containing 0 (control), 10, 50, 100 and 200 mg/L of PtN were fabricated respectively. The obtained platinum-PMMA nanocomposite (PtNC) was characterized by TEM (transmission electron microscopy), SEM/EDX (scanning electron microscope/energy dispersive X-ray spectroscopy), thermogravimetric and atomic absorption spectrophotometer analysis. In antimicrobial assay, specimens were placed on the cell culture plate, and 100 µL of microbial suspensions of S. mutans (Streptococcus mutans) and S. sobrinus (Streptococcus sobrinus) were inoculated then incubated at 37℃ for 24 hours. The bacterial attachment was tested by FACS (fluorescence-activated cell sorting) analysis after staining with fluorescent probe. PtN were successfully loaded and uniformly immobilized into PMMA denture acrylic with a proper thermal stability and similar surface morphology as compared to control. PtNC expressed significant bacterial anti-adherent effect rather than bactericidal effect above 50 mg/L PtN loaded when compared to pristine PMMA (P=.01) with no or extremely small amounts of Pt ion eluted. This is the first report on the synthesis and its antibacterial activity of Pt-PMMA nanocomposite. PMMA denture acrylic loading PtN could be a possible intrinsic antimicrobial denture material with proper mechanical characteristics, meeting those specified for denture bases. For clinical application, future studies including biocompatibility, color stability and warranting the long-term effect were still required.

  17. Towards completely miscible PMMA nanocomposites reinforced by shear-stiff, nano-mica.

    Science.gov (United States)

    Ziadeh, Mazen; Weiss, Stephan; Fischer, Bianca; Förster, Stephan; Altstädt, Volker; Müller, Axel H E; Breu, Josef

    2014-07-01

    Optimizing the reinforcement of polymers with nanoplatelets requires optimization of the aspect ratio and the moduli of the filler while providing a complete stress transfer. Employing a novel shear-stiff, nano-mica with large aspect ratio, we focus on maximizing the interfacial interaction between filler and matrix. External surfaces of the nano-mica were selectively modified by a polycationic macro-initiator and two PMMA-polymer brushes of length below and above critical entanglement length, respectively, and the mechanical properties of the three PMMA nanocomposites were measured. The multiple electrostatic anchoring groups of the macro-initiator not only provide reliable adhesion but at the same time allow the variation of the degree of protonation providing a local match between the charge densities of the clay surface and the adsorbed macro-initiator. PMMA coating of the nano-mica via surface initiated polymerization yielded long-term stable suspensions in THF that showed birefringence of a nematic phase. Solution blending of the PMMA coated nano-mica allows for dispersing single clay tactoids in the translucent PMMA nanocomposites at 5 wt% clay loading as determined by transmission electron microscopy (TEM). Although significantly improved mechanical properties could be achieved as compared to nanocomposites made with conventional clay fillers, the full potential - as expressed by Halpin-Tsai equations - of the PMMA coated nano-mica can still not be completely utilized. This is attributed to the non-wetting character of the densely packed PMMA brushes attached to planar nanoplatelets. Copyright © 2014 Elsevier Inc. All rights reserved.

  18. Optical Properties and Surface Morphology of Nano-composite PMMA: TiO2 Thin Films

    International Nuclear Information System (INIS)

    Lyly Nyl Ismail; Ahmad Fairoz Aziz; Habibah Zulkefle

    2011-01-01

    There are two nano-composite PMMA: TiO 2 solutions were prepared in this research. First solution is nano-composite PMMA commercially available TiO 2 nanopowder and the second solution is nano-composite PMMA with self-prepared TiO 2 powder. The self-prepared TiO 2 powder is obtained by preparing the TiO 2 sol-gel. Solvo thermal method were used to dry the TiO 2 sol-gel and obtained TiO 2 crystal. Ball millers were used to grind the TiO 2 crystal in order to obtained nano sized powder. Triton-X was used as surfactant to stabilizer the composite between PMMA: TiO 2 . Besides comparing the nano-composite solution, we also studied the effect of the thin films thickness on the optical properties and surface morphology of the thin films. The thin films were deposited by sol-gel spin coating method on glass substrates. The optical properties and surface characterization were measured with UV-VIS spectrometer equipment and atomic force microscopy (AFM). The result showed that nano-composite PMMA with self prepared TiO 2 give high optical transparency than nano-composite PMMA with commercially available TiO 2 nano powder. The results also indicate as the thickness is increased the optical transparency are decreased. Both AFM images showed that the agglomerations of TiO 2 particles are occurred on the thin films and the surface roughness is increased when the thickness is increased. High agglomeration particles exist in the AFM images for nano-composite PMMA: TiO 2 with TiO 2 nano powder compare to the other nano-composite solution. (author)

  19. Nano-graphene oxide incorporated into PMMA resin to prevent microbial adhesion.

    Science.gov (United States)

    Lee, Jung-Hwan; Jo, Jeong-Ki; Kim, Dong-Ae; Patel, Kapil Dev; Kim, Hae-Won; Lee, Hae-Hyoung

    2018-04-01

    Although polymethyl methacrylate (PMMA) is widely used as a dental material, a major challenge of using this substance is its poor antimicrobial (anti-adhesion) effects, which increase oral infections. Here, graphene-oxide nanosheets (nGO) were incorporated into PMMA to introduce sustained antimicrobial-adhesive effects by increasing the hydrophilicity of PMMA. After characterizing nGO and nGO-incorporated PMMA (up to 2wt%) in terms of morphology and surface characteristics, 3-point flexural strength and hardness were evaluated. The anti-adhesive effects were determined for 4 different microbial species with experimental specimens and the underlying anti-adhesive mechanism was investigated by a non-thermal oxygen plasma treatment. Sustained antimicrobial-adhesive effects were characterized with incubation in artificial saliva for up to 28 days. The typical nanosheet morphology was observed for nGO. Incorporating nGO into PMMA roughened its surface and increased its hydrophilicity without compromising flexural strength or surface hardness. An anti-adhesive effect after 1h of exposure to microbial species in artificial saliva was observed in nGO-incorporated specimens, which accelerated with increasing levels of nGO without significant cytotoxicity to oral keratinocytes. Plasma treatment of native PMMA demonstrated that the antimicrobial-adhesive effects of nGO incorporation were at least partially due to increased hydrophilicity, not changes in the surface roughness. A sustained antimicrobial-adhesive property against Candida albicans was observed in 2% nGO for up to 28 days. The presence of sustained anti-adhesion properties in nGO-incorporated PMMA without loading any antimicrobial drugs suggests the potential usefulness of this compound as a promising antimicrobial dental material for dentures, orthodontic devices and provisional restorative materials. Copyright © 2018 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  20. PS-b-PMMA/PLA blends for nanoporous templates with hierarchical and tunable pore size

    Science.gov (United States)

    Nguyen, Thi-Hoa; Vayer, Marylène; Sinturel, Christophe

    2018-01-01

    Blends of poly(styrene)-block-poly(methyl methacrylate) (PS-b-PMMA) and poly(lactide) (PLA) were deposited in the form of thin films on the surface of modified silicon wafers and exposed to tetrahydrofuran (THF) vapor annealing. It was shown that in specific experimental conditions, a core-shell morphology consisting in cylinders with a PMMA shell and a PLA core, within a continuous matrix of PS, was formed. In this case, PLA naturally segregated in the core of the PMMA cylinders, minimizing the PS/PLA interaction, which constitutes the most incompatible pair (the interaction strength between the various components was confirmed in thin films of the corresponding polymer blends). Compared to other block copolymer/homopolymer blends described in the literature, this system exhibits unexpected high increase of the characteristic lengths of the system (center-to-center distance and diameter). This was attributed to a partial solubilization of the PLA in the PMMA corona (the two polymers are highly compatible), inducing an enhanced level of PS and PLA stretching caused by the strong repulsion between these two polymers. The selective extraction of the PLA yielded to porous domains with small dimensions (6 ± 2.5 nm), reaching the performances that are currently attained in highly incompatible block polymers with low molecular weight. Further PMMA removal revealed a second porosity level, with higher pores diameter and center-to-center distance compared to the neat PS-b-PMMA system. This work highlights how PS-b-PMMA, that currently represents one of the industrial standards nanoporous template precursors, can be modified in an easy and costless approach using PLA homopolymer addition.

  1. Does cement mantle thickness really matter?

    OpenAIRE

    Caruana, J.

    2008-01-01

    The thickness of the cement mantle around the femoral component of total hip replacements is a contributing factor to aseptic loosening and revision. Nevertheless, various designs of stems and surgical tooling lead to cement mantles of differing thicknesses. This thesis is concerned with variability in cement thickness around the Stanmore Hip, due to surgical approach, broach size and stem orientation, and its effects on stress and cracking in the cement. The extent to which cement mantle thi...

  2. Alternative Fuels in Cement Production

    DEFF Research Database (Denmark)

    Larsen, Morten Boberg

    The substitution of alternative for fossil fuels in cement production has increased significantly in the last decade. Of these new alternative fuels, solid state fuels presently account for the largest part, and in particular, meat and bone meal, plastics and tyre derived fuels (TDF) accounted...... for the most significant alternative fuel energy contributors in the German cement industry. Solid alternative fuels are typically high in volatile content and they may differ significantly in physical and chemical properties compared to traditional solid fossil fuels. From the process point of view......, considering a modern kiln system for cement production, the use of alternative fuels mainly influences 1) kiln process stability (may accelerate build up of blockages preventing gas and/or solids flow), 2) cement clinker quality, 3) emissions, and 4) decreased production capacity. Kiln process stability...

  3. Calcium Aluminate Cement Hydration Model

    Directory of Open Access Journals (Sweden)

    Matusinović, T.

    2011-01-01

    Full Text Available Calcium aluminate cement (AC is a very versatile special cement used for specific applications. As the hydration of AC is highly temperature dependent, yielding structurally different hydration products that continuously alter material properties, a good knowledge of thermal properties at early stages of hydration is essential. The kinetics of AC hydration is a complex process and the use of single mechanisms models cannot describe the rate of hydration during the whole stage.This paper examines the influence of temperature (ϑ=5–20 °C and water-to-cement mass ratio (mH /mAC = 0.4; 0.5 and 1.0 on hydration of commercial iron-rich AC ISTRA 40 (producer: Istra Cement, Pula, Croatia, which is a part of CALUCEM group, Figs 1–3. The flow rate of heat generation of cement pastes as a result of the hydration reactions was measured with differential microcalorimeter. Chemically bonded water in the hydrated cement samples was determined by thermo-gravimetry.Far less heat is liberated when cement and water come in contact for the first time, Fig. 1, than in the case for portland cement (PC. Higher water-to-cement ratio increases the heat evolved at later ages (Fig. 3 due to higher quantity of water available for hydration. A significant effect of the water-to-cement ratio on the hydration rate and hydration degree showed the importance of water as being the limiting reactant that slows down the reaction early. A simplified stoichiometric model of early age AC hydration (eq. (8 based on reaction schemes of principal minerals, nominally CA, C12A7 and C4AF (Table 1, was employed. Hydration kinetics after the induction period (ϑ < 20 °C had been successfully described (Fig. 4 and Table 2 by a proposed model (eq. (23 which simultaneously comprised three main mechanisms: nucleation and growth, interaction at phase boundary, and mass transfer. In the proposed kinetic model the nucleation and growth is proportional to the amount of reacted minerals (eq

  4. Rheological measurements on cement grouts

    International Nuclear Information System (INIS)

    Dalton, M.J.

    1986-06-01

    This report describes the techniques which have been developed at Winfrith for assessing the rheological properties of cement grouts. A discussion of the theory of rheology and its application to cement is given and the methodology for calibrating a special paddle measuring system for a commercial viscometer is described. The use of the system for determining flow curves, equilibrium viscosity, viscosity as a function of shearing time and structure changes is also discussed. (author)

  5. Cement pulmonary embolism after vertebroplasty.

    Science.gov (United States)

    Sifuentes Giraldo, Walter Alberto; Lamúa Riazuelo, José Ramón; Gallego Rivera, José Ignacio; Vázquez Díaz, Mónica

    2013-01-01

    In recent years, the use of vertebral cementing techniques for vertebroplasty and kyphoplasty has spread for the treatment of pain associated with osteoporotic vertebral compression fractures. This is also associated with the increased incidence of complications related with these procedures, the most frequent being originated by leakage of cementation material. Cement can escape into the vertebral venous system and reach the pulmonary circulation through the azygous system and cava vein, producing a cement embolism. This is a frequent complication, occurring in up to 26% of patients undergoing vertebroplasty but, since most patients have no clinical or hemodynamical repercussion, this event usually goes unnoticed. However, some serious, and even fatal cases, have been reported. We report the case of a 74-year-old male patient who underwent vertebroplasty for persistent pain associated with osteoporotic L3 vertebral fracture and who developed a cement leak into the cava vein and right pulmonary artery during the procedure. Although he developed a pulmonary cement embolism, the patient remained asymptomatic and did not present complications during follow-up. Copyright © 2012 Elsevier España, S.L. All rights reserved.

  6. Calcium Orthophosphate Cements and Concretes

    Directory of Open Access Journals (Sweden)

    Sergey V. Dorozhkin

    2009-03-01

    Full Text Available In early 1980s, researchers discovered self-setting calcium orthophosphate cements, which are a bioactive and biodegradable grafting material in the form of a powder and a liquid. Both phases form after mixing a viscous paste that after being implanted, sets and hardens within the body as either a non-stoichiometric calcium deficient hydroxyapatite (CDHA or brushite, sometimes blended with unreacted particles and other phases. As both CDHA and brushite are remarkably biocompartible and bioresorbable (therefore, in vivo they can be replaced with newly forming bone, calcium orthophosphate cements represent a good correction technique for non-weight-bearing bone fractures or defects and appear to be very promising materials for bone grafting applications. Besides, these cements possess an excellent osteoconductivity, molding capabilities and easy manipulation. Furthermore, reinforced cement formulations are available, which in a certain sense might be described as calcium orthophosphate concretes. The concepts established by calcium orthophosphate cement pioneers in the early 1980s were used as a platform to initiate a new generation of bone substitute materials for commercialization. Since then, advances have been made in the composition, performance and manufacturing; several beneficial formulations have already been introduced as a result. Many other compositions are in experimental stages. In this review, an insight into calcium orthophosphate cements and concretes, as excellent biomaterials suitable for both dental and bone grafting application, has been provided.

  7. Synthesis of PMMA-b-PU-b-PMMA tri-block copolymers through ARGET ATRP in the presence of air

    Directory of Open Access Journals (Sweden)

    P. Krol

    2013-03-01

    Full Text Available ARGET (activators regenerated by electron transfer ATRP (atom transfer radical polymerization has been successfully performed (in flasks fitted with rubber septa without the need for use of Schlenk line in the presence of limited amount of air and with a very small (370 ppm amount of copper catalyst together with an appropriate reducing agent Cu(0. Novelty of this work is that the poly(methyl methacrylate-block-polyurethane-block-poly(methyl methacrylate triblock copolymers were synthesized for the first time through ARGET ATRP, by using tertiary bromine-terminated polyurethane as a macroinitiator (MBP-PU-MBP, CuBr2 or CuCl2 as a catalyst and N,N,N',N",N"-pentamethyldiethylenetriamine (PMDETA or 2,2'-bipyridine (Bpy as a complexing agent. As the polymerization time increases, both the monomer conversion and ln([M]0/[M] increased and the molecular weight of copolymer increases linearly with increasing conversion. Theoretical number-average molecular weight (Mn, th of the tri-block copolymers was found to be comparable with number-average molecular weight determined by GPC analyses (Mn, GPC. These results indicate that the formation of the tri-block copolymers was through atom transfer radical polymerization mechanism. 1H and 13C NMR spectral methods were employed to confirm chemical structures of synthesized macroinitiator and tri-block copolymers. Mole percentage of PMMA in the tri-block copolymers was calculated using 1H NMR spectroscopy and was found to be comparable with the GPC results. Additionally, the studies of surface properties (confocal microscopy and SFE of tri-block copolymer coatings confirmed the presence of MMA segments.

  8. Photoluminescent behaviors of several kinds of europium ternary complexes doped in PMMA

    International Nuclear Information System (INIS)

    Liu, H.-G.; Lee, Yong-Ill; Park, Seongtae; Jang, Kiwan; Kim, Sang Su

    2004-01-01

    Four kinds of europium ternary complexes; Eu(DBM) 3 phen, Eu(DBM) 3 (DB-bpy), Eu(DBM) 3 (DN-bpy) and Eu(DBM) 3 biq (DBM, phen, DB-bpy, DN-bpy and biq refer to Dibenzoylmethane, 1,10-phenanthroline, 4,4'-Di-tert-butyl-2,2'-dipyridyl, 4,4'-Dinonyl-2,2'-dipyridyl and 2,2'-Biquinoline, respectively), were doped in poly(methyl methacrylate) (PMMA) matrix. The luminescence properties of the composites were investigated by emission spectroscopy and lifetime measurements. It was found that the composites formed by the three complexes, Eu(DBM) 3 phen, Eu(DBM) 3 (DB-bpy), and Eu(DBM) 3 (DN-bpy), exhibit strong luminescence and similar emission spectral characteristics to Eu(III). Whereas, Eu(DBM) 3 biq shows large differences in its luminescence spectrum compared to those of other complexes. The luminescence was very weak and broad. The emission spectral features of Eu(III) in the Eu(DBM) 3 biq/PMMA systems change with the molar ratios of the complex and PMMA. The lifetime of 5 D 0 level of Eu(III) in Eu(DBM) 3 biq/PMMA systems is shorter than those in the other systems. The luminescence intensity of Eu(III) in Eu(DBM) 3 biq/PMMA systems decreases gradually when exposed to UV-light while the broad emission band becomes stronger

  9. Interphase and magnetotransport of LSMO-PMMA nanocomposites obtained by a sonochemical method

    Energy Technology Data Exchange (ETDEWEB)

    Romero, Mariano [Centro NanoMat/Cryssmat Lab/Cátedra de Física – DETEMA – Facultad de Química – Universidad de la República (Uruguay); Centro Interdisciplinario de Nanotecnología, Química y Física de Materiales – Universidad de la República (Uruguay); Pardo, Helena, E-mail: hpardo@fq.edu.uy [Centro NanoMat/Cryssmat Lab/Cátedra de Física – DETEMA – Facultad de Química – Universidad de la República (Uruguay); Centro Interdisciplinario de Nanotecnología, Química y Física de Materiales – Universidad de la República (Uruguay); Faccio, Ricardo [Centro NanoMat/Cryssmat Lab/Cátedra de Física – DETEMA – Facultad de Química – Universidad de la República (Uruguay); Centro Interdisciplinario de Nanotecnología, Química y Física de Materiales – Universidad de la República (Uruguay); Tumelero, Milton A. [Laboratorio de filmes finos e superficies – Departamento de Física – Universidad Federal de Santa Catarina, Florianópolis (Brazil); and others

    2015-05-15

    In this report, we studied the structural, microstructural and compositional trends in a manganite-polymethylmethacrilate (LSMO-PMMA) nanocomposite prepared by a sonochemical method focusing in the study of its interphase and its correlation with magnetotransport. Differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), Raman scattering and X-ray powder diffraction (XRPD) studies showed evidence of PMMA reactivity with partial decomposition at the LSMO nanoparticles interface. Additionally, grazing incidence small angle X-ray scattering (GISAXS) and high resolution transmission electron microscopy (HRTEM) showed information about the microstructure and the separation between nanoparticles in these nanocomposite materials. An enhancement in the low field magnetoresistance (LFMR) respect to pure LSMO was observed for a 20% weight fraction addition of PMMA in the high temperature regime (205–305 K) probably due to the increase in the magnetic disorder at the grain boundaries caused by the ultrasonic treatment. Nevertheless, lower PMMA weight fraction addition showed no enhancement in LFMR respect to pure LSMO, probably in agreement with the higher decomposition rate observed at the interphase. - Highlights: • We report the synthesis of LSMO-PMMA nanocomposites by a sonochemical method. • Compositional and microstructural trends were obtained from the interphase. • This method showed long-range homogeneity and enhancement of grain boundary disorder. • The enhancement on the LFMR respect to pure manganite was obtained at higher temperatures.

  10. Toward transparent nanocomposites based on polystyrene matrix and PMMA-grafted CeO2 nanoparticles.

    Science.gov (United States)

    Parlak, Onur; Demir, Mustafa M

    2011-11-01

    The association of transparent polymer and nanosized pigment particles offers attractive optical materials for various potential and existing applications. However, the particles embedded into polymers scatter light due to refractive index (RI) mismatch and reduce transparency of the resulting composite material. In this study, optical composites based on polystyrene (PS) matrix and poly(methyl methacrylate) (PMMA)-grafted CeO(2) hybrid particles were prepared. CeO(2) nanoparticles with an average diameter of 18 ± 8 nm were precipitated by treating Ce(NO(3))·6H(2)O with urea in the presence of a polymerizable surfactant, 3-methacyloxypropyltrimethoxy silane. PMMA chains were grafted on the surface of the nanoparticles upon free radical in situ solution polymerization. While blending of unmodified CeO(2) particles with PS resulted in opaque films, the transparency of the composite films was remarkably enhanced when prepared by PMMA-grafted CeO(2) hybrid particles, particularly those having a PMMA thickness of 9 nm. The improvement in transparency is presumably due to the reduction in RI mismatch between CeO(2) particles and the PS matrix when using PMMA chains at the interface.

  11. A safe and cost-effective PMMA carbon source for MgB{sub 2}

    Energy Technology Data Exchange (ETDEWEB)

    Ranot, Mahipal; Shinde, K. P.; Oh, Y. S.; Kang, S. H.; Chung, K. C. [Korea Institute of Materials Science, Changwon (Korea, Republic of); Jang, S. H. [Kiswire Advanced Technology Ltd, Daejeon (Korea, Republic of); Sinha, B. B. [National Centre for Nanoscience and Nanotechnology, University of Mumbai, Mumbai (India); Bhardwaj, A. [Dept. of Physics, Sungkyunkwan University, Suwon (Korea, Republic of)

    2017-03-15

    Carbon is proven to be very effective in pinning the magnetic vortices and improving the superconducting performance of MgB2 at high fields. In this work, we have used polymethyl methacrylate (PMMA) polymer as a safe and cost effective carbon source. The effects of molecular weight of PMMA on crystal structure, microstructure as well as on superconducting properties of MgB2 were studied. X-ray diffraction analysis revealed that there is a noticeable shift in (100) and (110) Bragg reflections towards higher angles, while no shift was observed in (002) reflections for MgB2 doped with different molecular weights of PMMA. This indicates that carbon could be substituted in the boron honeycomb layers without affecting the interlayer interactions. As compared to undoped MgB2, substantial enhancement in Jc(H) properties was obtained for PMMA-doped MgB2 samples both at 5 K and 20 K. The enhancement could be attributed to the effective carbon substitution for boron and the refinement of crystallite size by PMMA doping.

  12. Studies on the Properties of Plasticizer and Lithium Salt on PMMA-based Solid Polymer Electrolytes

    International Nuclear Information System (INIS)

    Chew, K. W.; Tan, C. G.; Osman, Z.

    2010-01-01

    The effects of plasticizer and lithium salt on PMMA-based solid polymer electrolyte have been investigated. In current project, three system samples consisted of pure poly(methyl methacrylate (PMMA) system, plasticized poly(methyl methacrylate)(PMMA-EC) system and the LiCF 3 SO 3 salted-poly(methyl methacrylate) containing a fixed amount of plasticizer ([PMMA-EC]-LiCF 3 SO 3 ) system have been prepared using solution casting technique. The conductivities of the films from each system are characterized by impedance spectroscopy and infrared spectrum. With the addition of plasticizer, results show improvement on the ionic conductivity value where the value of 6.25x10 -10 Scm -1 is obtained. This may be due to the nature of plasticizer that softens the polymer and hence enhanced the ionic transportation across the polymer. The room temperature conductivity for the highest conducting sample in the ([PMMA-EC]-LiCF 3 SO 3 ) system is 1.36x10 -5 Scm -1 . Fourier Transform Infrared Spectroscopy (FTIR) indicates complexation between the polymer and the plasticizer and the polymer, the plasticizer and the salts, and the result of XRD further supports the observation.

  13. Deep-UV patterning of commercial grade PMMA for low-cost, large-scale microfluidics

    International Nuclear Information System (INIS)

    Haiducu, M; Rahbar, M; Foulds, I G; Johnstone, R W; Sameoto, D; Parameswaran, M

    2008-01-01

    Although PMMA can be exposed using a variety of exposure sources, deep-UV at 254 nm is of interest because it is relatively inexpensive. Additionally, deep-UV sources can be readily scaled to large area exposures. Moreover, this paper will show that depths of over 100µm can be created in commercial grade PMMA using an uncollimated source. These depths are sufficient for creating microfluidic channels. This paper will provide measurements of the dissolution depth of commercial grade PMMA as a function of the exposure dose and etch time, using an IPA:H 2 O developer. Additionally, experiments were run to characterize the dependence of the dissolution rate on temperature and agitation. The patterned substrates were thermally bonded to blank PMMA pieces to enclose the channels and ports were drilled into the reservoirs. The resulting fluidic systems were then tested for leakage. The work herein presents the patterning, development and system behaviour of a complete microfluidics system based on commercial grade PMMA

  14. Interphase and magnetotransport of LSMO-PMMA nanocomposites obtained by a sonochemical method

    International Nuclear Information System (INIS)

    Romero, Mariano; Pardo, Helena; Faccio, Ricardo; Tumelero, Milton A.

    2015-01-01

    In this report, we studied the structural, microstructural and compositional trends in a manganite-polymethylmethacrilate (LSMO-PMMA) nanocomposite prepared by a sonochemical method focusing in the study of its interphase and its correlation with magnetotransport. Differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), Raman scattering and X-ray powder diffraction (XRPD) studies showed evidence of PMMA reactivity with partial decomposition at the LSMO nanoparticles interface. Additionally, grazing incidence small angle X-ray scattering (GISAXS) and high resolution transmission electron microscopy (HRTEM) showed information about the microstructure and the separation between nanoparticles in these nanocomposite materials. An enhancement in the low field magnetoresistance (LFMR) respect to pure LSMO was observed for a 20% weight fraction addition of PMMA in the high temperature regime (205–305 K) probably due to the increase in the magnetic disorder at the grain boundaries caused by the ultrasonic treatment. Nevertheless, lower PMMA weight fraction addition showed no enhancement in LFMR respect to pure LSMO, probably in agreement with the higher decomposition rate observed at the interphase. - Highlights: • We report the synthesis of LSMO-PMMA nanocomposites by a sonochemical method. • Compositional and microstructural trends were obtained from the interphase. • This method showed long-range homogeneity and enhancement of grain boundary disorder. • The enhancement on the LFMR respect to pure manganite was obtained at higher temperatures

  15. Nano clay-enhanced calcium phosphate cements and hydrogels for biomedical applications

    Science.gov (United States)

    Jammalamadaka, Udayabhanu

    Biomaterials are used as templates for drug delivery, scaffolds in tissue engineering, grafts in surgeries, and support for tissue regeneration. Novel biomaterial composites are needed to meet multifaceted requirements of compatibility, ease of fabrication and controlled drug delivery. Currently used biomaterials in orthopedics surgeries suffer limitations in toxicity and preventing infections. Polymethyl methacrylate (PMMA) used as bone cement suffers from limitations of thermal necrosis and monomer toxicity calls for development of better cementing biomaterials. A biodegradable/bioresorbable cement with good mechanical properties is needed to address this short coming. Metal implants used in fixing fractures or total joint replacement needs improvements in preventing biofilm formation and better tissue integration. This research addressed the above mentioned research gaps by formulating novel biomaterial composites. Calcium phosphate cements are the alternative bone cements that are bioresorbable and promote tissue integration. These cements lack sufficient mechanical strengths to be used in load bearing sites. The addition of nanoparticles is hypothesized to improve the mechanical properties without inducing toxicity to the tissue. This hypothesis was tested by evaluating compression and flexural strengths in addition to cytocompatibility tests. Results indicate that addition of nano-clay particles (halloysites nanotubes) improved the compressive strength and osteoinductive properties of calcium phosphate cements. To address the research need of preventing implant failure due to infection and aseptic loosening, novel coatings are needed. Hydrogels are well establish for their ability to mimic in vivo environment, promote cell viability and as drug delivery vehicles. Use of composites of hydrogels and drug-loaded nanoparticles to prevent infection was evaluated. Cytocompatibility results indicate good cell viability. Antibacterial results show sustained release

  16. Low pH Cements

    International Nuclear Information System (INIS)

    Savage, David; Benbow, Steven

    2007-05-01

    The development of low-pH cements for use in geological repositories for radioactive waste stems from concerns over the potential for deleterious effects upon the host rock and other EBS materials (notably bentonite) under the hyperalkaline conditions (pH > 12) of cement pore fluids. Low pH cement (also known as low heat cement) was developed by the cement industry for use where large masses of cement (e.g. dams) could cause problems regarding heat generated during curing. In low pH cements, the amount of cement is reduced by substitution of materials such as fly ash, blast furnace slag, silica fume, and/or non-pozzolanic silica flour. SKB and Posiva have ruled out the use of blast furnace slag and fly-ash and are focusing on silica fume as a blending agent. Currently, no preferred composition has been identified by these agencies. SKB and Posiva have defined a pH limit ≤ 11 for cement grout leachates. To attain this pH, blending agents must comprise at least 50 wt % of dry materials. Because low pH cement has little, or no free portlandite, the cement consists predominantly of calcium silicate hydrate (CSH) gel with a Ca/Si ratio ≤ 0.8. Although there are potential implications for the performance of the spent fuel and cladding due to the presence of hyperalkaline fluids from cement, the principal focus for safety assessment lies with the behaviour of bentonite. There are a number of potential constraints on the interaction of hyperalkaline cement pore fluids with bentonite, including mass balance, thermodynamic issues, mass transport, and kinetics, but none of these is likely to be limiting if conventional OPC cements are employed in repository construction. Nevertheless: Low-pH cements may supply approximately 50 % less hydroxyl ions than conventional OPC for a given volume of cement, but mass balance constraints are complicated by the uncertainty concerning the type of secondary minerals produced during cement-bentonite interaction. The change of aqueous

  17. Low pH Cements

    Energy Technology Data Exchange (ETDEWEB)

    Savage, David; Benbow, Steven [Quintessa Ltd., Henley-on-Thames (United Kingdom)

    2007-05-15

    The development of low-pH cements for use in geological repositories for radioactive waste stems from concerns over the potential for deleterious effects upon the host rock and other EBS materials (notably bentonite) under the hyperalkaline conditions (pH > 12) of cement pore fluids. Low pH cement (also known as low heat cement) was developed by the cement industry for use where large masses of cement (e.g. dams) could cause problems regarding heat generated during curing. In low pH cements, the amount of cement is reduced by substitution of materials such as fly ash, blast furnace slag, silica fume, and/or non-pozzolanic silica flour. SKB and Posiva have ruled out the use of blast furnace slag and fly-ash and are focusing on silica fume as a blending agent. Currently, no preferred composition has been identified by these agencies. SKB and Posiva have defined a pH limit {<=} 11 for cement grout leachates. To attain this pH, blending agents must comprise at least 50 wt % of dry materials. Because low pH cement has little, or no free portlandite, the cement consists predominantly of calcium silicate hydrate (CSH) gel with a Ca/Si ratio {<=} 0.8. Although there are potential implications for the performance of the spent fuel and cladding due to the presence of hyperalkaline fluids from cement, the principal focus for safety assessment lies with the behaviour of bentonite. There are a number of potential constraints on the interaction of hyperalkaline cement pore fluids with bentonite, including mass balance, thermodynamic issues, mass transport, and kinetics, but none of these is likely to be limiting if conventional OPC cements are employed in repository construction. Nevertheless: Low-pH cements may supply approximately 50 % less hydroxyl ions than conventional OPC for a given volume of cement, but mass balance constraints are complicated by the uncertainty concerning the type of secondary minerals produced during cement-bentonite interaction. The change of aqueous

  18. Development of cement material using inorganic additives

    International Nuclear Information System (INIS)

    Toyohara, Masumitsu; Satou, Tatsuaki; Wada, Mikio; Ishii, Tomoharu; Matsuo, Kazuaki.

    1997-01-01

    Inorganic admixtures to enhance the fluidity of cement material was developed. These admixtures turned into easy to immobilize the miscellaneous radioactive waste using cement material. It was found that the ζ potential of cement particles was directly proportional to the content of the inorganic admixtures in cement paste and the particles of cement were dispersed at the high ζ potential. The condensed sodium phosphate, which was the main component of the inorganic admixtures, retarded the dissolution of Ca 2+ ion from the cement, and generated the colloids by incorporating dissolved Ca 2+ ion. The cement material containing the inorganic admixtures was found to have the same mechanical strength and adsorption potential of radionuclides in comparison to normal cement materials. It was confirmed that the cement material containing the inorganic admixture was effectively filled gaps of miscellaneous radioactive waste. (author)

  19. Development of high-performance blended cements

    Science.gov (United States)

    Wu, Zichao

    2000-10-01

    This thesis presents the development of high-performance blended cements from industrial by-products. To overcome the low-early strength of blended cements, several chemicals were studied as the activators for cement hydration. Sodium sulfate was discovered as the best activator. The blending proportions were optimized by Taguchi experimental design. The optimized blended cements containing up to 80% fly ash performed better than Type I cement in strength development and durability. Maintaining a constant cement content, concrete produced from the optimized blended cements had equal or higher strength and higher durability than that produced from Type I cement alone. The key for the activation mechanism was the reaction between added SO4 2- and Ca2+ dissolved from cement hydration products.

  20. Multifunctional PMMA@Fe3O4@DR Magnetic Materials for Efficient Adsorption of Dyes

    Directory of Open Access Journals (Sweden)

    Bing Yu

    2017-10-01

    Full Text Available Magnetic porous microspheres are widely used in modern wastewater treatment technology due to their simple and quick dye adsorption and separation functions. In this article, we prepared porous polymethylmethacrylate (PMMA microspheres by the seed-swelling method, followed by in situ formation of iron oxide (Fe3O4 nanoparticles within the pore. Then, we used diazo-resin (DR to encapsulate the porous magnetic microspheres and achieve PMMA@Fe3O4@DR magnetic material. We studied the different properties of magnetic microspheres by different dye adsorption experiments before and after the encapsulation and demonstrated that the PMMA@Fe3O4@DR microspheres can be successfully used as a reusable absorbent for fast and easy removal of anionic and aromatic dyes from wastewater and can maintain excellent magnetic and adsorption properties in harsh environments.

  1. Influence of dopant concentration on the electrical properties of the CdSe-PMMA nanocomposite

    Energy Technology Data Exchange (ETDEWEB)

    Kaur, Ramneek; Tripathi, S. K., E-mail: surya@pu.ac.in, E-mail: surya-tr@yahoo.com [Department of Physics, Center of Advanced Study in Physics, Panjab University, Chandigarh-160 014 (India)

    2016-05-06

    This paper reports the synthesis and electrical characterization of CdSe-PMMA nanocomposite. CdSe-PMMA nanocomposite has been prepared by ex-situ technique through chemical route. The influence of three different Ag doping concentrations on the electrical properties has been studied in the temperature range ∼ 303-353 K. Transmission electron micrograph reveals the spherical morphology of the CdSe nanoparticles and their proper dispersion in the PMMA matrix. The electrical conduction of the polymer nanocomposites is through thermally activated process with single activation energy. With Ag doping, initially the activation energy increases upto 0.2 % Ag doping concentration but with further increase in Ag concentration, it decreases. This behavior has been discussed on the basis of randomly oriented grain boundaries and defect states. Thus, the results indicate that the transport properties of the polymer nanocomposites can be tailored by controlled doping concentration.

  2. Reinforcement of a PMMA resin for fixed interim prostheses with nanodiamonds.

    Science.gov (United States)

    Protopapa, Popi; Kontonasaki, Eleana; Bikiaris, Dimitrios; Paraskevopoulos, Konstantinos M; Koidis, Petros

    2011-01-01

    The aim of this study was to investigate the possible reinforcement of Nanodiamonds (ND) in a PMMA resin for fixed interim restorations. The fracture toughness (K(Ic)), impact strength and the dynamic thermomechanical properties (T(g), E´, E´´, tanδ) of a series of PMMA-ND nanocomposites with different amounts of ND were evaluated. The fracture toughness increased as the ND percentage increased up to 0.38% wt but a greater amount of ND induced a decrease in K(Ic). Impact strength and Young's modulus were also increased by increasing nanoparticles content, indicating the reinforcing effect of ND. Dynamic mechanical properties were also affected. By increasing the ND content an increase of storage modulus was recorded, while glass transition was shifted at higher temperatures. Under the limitations of this study, it can be suggested that reinforcing PMMA with ND nanoparticles -especially at low concentrations- may increase the overall performance of fixed interim prostheses.

  3. Influence of dopant concentration on the electrical properties of the CdSe-PMMA nanocomposite

    International Nuclear Information System (INIS)

    Kaur, Ramneek; Tripathi, S. K.

    2016-01-01

    This paper reports the synthesis and electrical characterization of CdSe-PMMA nanocomposite. CdSe-PMMA nanocomposite has been prepared by ex-situ technique through chemical route. The influence of three different Ag doping concentrations on the electrical properties has been studied in the temperature range ∼ 303-353 K. Transmission electron micrograph reveals the spherical morphology of the CdSe nanoparticles and their proper dispersion in the PMMA matrix. The electrical conduction of the polymer nanocomposites is through thermally activated process with single activation energy. With Ag doping, initially the activation energy increases upto 0.2 % Ag doping concentration but with further increase in Ag concentration, it decreases. This behavior has been discussed on the basis of randomly oriented grain boundaries and defect states. Thus, the results indicate that the transport properties of the polymer nanocomposites can be tailored by controlled doping concentration.

  4. Electrostatic nanopatterning of PMMA by AFM charge writing for directed nano-assembly

    International Nuclear Information System (INIS)

    Ressier, L; Nader, V Le

    2008-01-01

    Electrostatic nanopatterning of poly(methylmethacrylate) (PMMA) thin films by atomic force microscopy (AFM) charge writing was investigated using Kelvin force microscopy (KFM). The lateral size of the electrostatic patterns and the amount of injected charges are closely correlated and can be controlled by the height of the voltage pulses applied to the AFM tip and the tip-sample separation during the writing process. Charge retention measurements show that PMMA has excellent charge storage properties in air under relative humidities from 1% to 60% and withstands immersion in ultra-pure water. This study thus reveals that PMMA is a very promising electret to create efficient electrostatic nanopatterns for directed self-assembly of nanoscale objects, including the broad range of colloidal particles or molecules in aqueous solutions

  5. Photoluminescence of PMMA doped with fluorescein and carbosilane dendrimer and lasing in PBG resonance cavity

    International Nuclear Information System (INIS)

    Li Chunfang; Jin Feng; Dong Xianzi; Chen Weiqiang; Duan Xuanming

    2007-01-01

    Carbosilane dendrimers with terminal allyl groups were synthesized and used to encapsulate the allyl derivative of fluorescein (allyl-FL) doped in PMMA. The optical property of this system was investigated and the results showed that the concentration of allyl-FL in PMMA could be increased to 4.5 wt% without decrease of the luminescence efficiency by adding the dendrimer into the system. The allyl-FL/dendrimer/PMMA film was embedded into a resonance cavity composed of two pieces of photonic band gap (PBG) materials to form a new-type solid-state laser. A laser emission at 589 nm was obtained when excited with a third harmonic generation (THG) of a pulsed Nd:YAG laser (355 nm) and its full-width at half-maximum of the spectrum was 1.7 nm

  6. A PMMA coated PMN–PT single crystal resonator for sensing chemical agents

    International Nuclear Information System (INIS)

    Frank, Michael; Kassegne, Sam; Moon, Kee S

    2010-01-01

    A highly sensitive lead magnesium niobate–lead titanate (PMN–PT) single crystal resonator coated with a thin film of polymethylmethacrylate (PMMA) useful for detecting chemical agents such as acetone, methanol, and isopropyl alcohol is presented. Swelling of the cured PMMA polymer layer in the presence of acetone, methanol, and isopropyl alcohol vapors is sensed as a mass change transduced to an electrical signal by the PMN–PT thickness shear mode sensor. Frequency change in the PMN–PT sensor is demonstrated to vary according to the concentration of the chemical vapor present within the sensing chamber. For acetone, the results indicate a frequency change more than 6000 times greater than that which would be expected from a quartz crystal microbalance coated with PMMA. This study is the first of its kind to demonstrate vapor loading of adsorbed chemical agents onto a polymer coated PMN–PT resonator

  7. Polymer-cement interactions towards improved wellbore cement fracture sealants

    Science.gov (United States)

    Beckingham, B. S.; Iloejesi, C.; Minkler, M. J.; Schindler, A. K.; Beckingham, L. E.

    2017-12-01

    Carbon capture, utilization, and storage (CCUS) in deep geologic formations is a promising means of reducing point source emissions of CO2. In these systems, CO2 is captured at the source and then injected to be utilized (eg. in enhanced oil recovery or as a working fluid in enhanced geothermal energy plants) or stored in geologic formations such as depleted oil and gas reservoirs or saline aquifers. While CCUS in subsurface systems could aid in reducing atmospheric CO2 emissions, the potential for CO2 leakage from these systems to overlying formations remains a major limitation and poses a significant risk to the security of injected CO2. Thus, improved materials for both initial wellbore isolation and repairing leakage pathways that develop over time are sought. One approach for the repair of cement fractures in wellbore (and other) systems is the injection of polymer materials into the fracture with a subsequent environmentally dependent (temperature, pressure, pH, etc.) densification or solidification. Here, we aim to investigate novel polymer materials for use to repair leaking wellbores in the context of CCUS. We synthesize and fully characterize a series of novel polymer materials and utilize a suite of analysis techniques to examine polymer-cement interactions at a range of conditions (namely temperature, pressure and pH). Initial findings will be leveraged to design novel polymer materials for further evaluation in polymer-cement composite cores, cement fracture healing, and the aging behavior of healed cements.

  8. Solvent exfoliated graphene for reinforcement of PMMA composites prepared by in situ polymerization

    International Nuclear Information System (INIS)

    Wang, Jialiang; Shi, Zixing; Ge, Yu; Wang, Yan; Fan, Jinchen; Yin, Jie

    2012-01-01

    Graphene (GP)-based polymer nanocomposites have attracted considerable scientific attention due to its pronounced improvement in mechanical, thermal and electrical properties compared with pure polymers. However, the preparation of well-dispersed and high-quality GP reinforced polymer composites remains a challenge. In this paper, a simple and facile approach for preparation of poly(methyl methacrylate) (PMMA) functionalized GP (GPMMA) via in situ free radical polymerization is reported. Fourier transform infrared (FTIR), X-ray photoelectron spectra (XPS), Raman, transmission electron microscope (TEM) and thermogravimetric analysis (TGA) are used to confirm the successful grafting of PMMA chains onto the GP sheets. Composite films are prepared by incorporating different amounts of GPMMA into the PMMA matrix through solution-casting method. Compared with pure PMMA, PMMA/GPMMA composites show simultaneously improved Young's modulus, tensile stress, elongation at break and thermal stability by addition of only 0.5 wt% GPMMA. The excellent reinforcement is attributed to good dispersion of high-quality GPMMA and strong interfacial adhesion between GPMMA and PMMA matrix as evidenced by scanning electron microscope (SEM) images of the fracture surfaces. Consequently, this simple protocol has great potential in the preparation of various high-performance polymer composites. Highlights: ► Functionalization of solvent exfoliated graphene by in situ polymerization. ► A simple and scalable method for preparing high-quality graphene. ► Functionalized graphene can be well-dispersed and have a strong interfacial adhesion with the polymer matrix. ► The nanocomposites exhibit a remarkable improvement of thermal and mechanical properties.

  9. A FEM simulation study of the solid state hydrostatic extrusion of PMMA

    Science.gov (United States)

    Costa, André L. M.; Riffel, Douglas B.; Misiolek, Wojciech Z.; Valberg, Henry S.

    2018-05-01

    Solid state hydrostatic extrusion (SSHE) of polymers below glass transition temperature is used to obtain highly oriented structures. Experimental studies on the SSHE of polymethyl-methacrylate (PMMA) have been made since early eighties but there is no information on internal temperature, stress and strain distribution. In this work we have made 3D FEM simulations of SSHE of PMMA by using the commercial DEFORM package with experimental flow curves and thermal properties from literature. The initial temperature of tooling and workpiece was 90°C, ram speeds were 1.0 and 10.0 mm/min with extrusion ratio R = 3.0. For a comparative analysis, SSHE simulation of the AA7108 aluminum alloy at 400°C was also performed. These ranges of parameters were chosen in order to encompass the parameters found in previously mentioned experiments. The best correlation with experimental hydrostatic pressure was verified for a shear friction coefficient at the material-conical die interface m = 0.50. Force-displacement curve for PMMA presented a constitutive and thermal softening in contrast to a constant force curve for aluminum. The internal temperature in the deformation zone increased in a characteristic "owl's face" profile in contrast to quasi-constant profile of aluminum alloy. In both PMMA and aluminum the stress is hydrostatic inside the container, but the stress profiles are significantly different inside the deformation zone. As expected, the strain and strain-rate profiles are practically the same for the two materials, but the temperature profile has promoted slightly differences in material flow. The velocity gradient from center to surface is higher in PMMA than aluminum. It's supposed that during hydrostatic extrusion solid PMMA has a characteristic thermally-inducted mechanical behavior.

  10. Preventive effects of a phospholipid polymer coating on PMMA on biofilm formation by oral streptococci

    Science.gov (United States)

    Shibata, Yukie; Yamashita, Yoshihisa; Tsuru, Kanji; Ishihara, Kazuhiko; Fukazawa, Kyoko; Ishikawa, Kunio

    2016-12-01

    The regulation of biofilm formation on dental materials such as denture bases is key to oral health. Recently, a biocompatible phospholipid polymer, poly(2-methacryloyloxyethyl phosphorylcholine-co-n-butyl methacrylate) (PMB) coating, was reported to inhibit sucrose-dependent biofilm formation by Streptococcus mutans, a cariogenic bacterium, on the surface of poly(methyl methacrylate) (PMMA) denture bases. However, S. mutans is a minor component of the oral microbiome and does not play an important role in biofilm formation in the absence of sucrose. Other, more predominant oral streptococci must play an indispensable role in sucrose-independent biofilm formation. In the present study, the effect of PMB coating on PMMA was evaluated using various oral streptococci that are known to be initial colonizers during biofilm formation on tooth surfaces. PMB coating on PMMA drastically reduced sucrose-dependent tight biofilm formation by two cariogenic bacteria (S. mutans and Streptococcus sobrinus), among seven tested oral streptococci, as described previously [N. Takahashi, F. Iwasa, Y. Inoue, H. Morisaki, K. Ishihara, K. Baba, J. Prosthet. Dent. 112 (2014) 194-203]. Streptococci other than S. mutans and S. sobrinus did not exhibit tight biofilm formation even in the presence of sucrose. On the other hand, all seven species of oral streptococci exhibited distinctly reduced glucose-dependent soft biofilm retention on PMB-coated PMMA. We conclude that PMB coating on PMMA surfaces inhibits biofilm attachment by initial colonizer oral streptococci, even in the absence of sucrose, indicating that PMB coating may help maintain clean conditions on PMMA surfaces in the oral cavity.

  11. Synthesis and characterization of PMMA/clay nanocomposites prepared by in situ polymerization assisted by sonication; Sintese e caracterizacao de nanocompositos de PMMA/MMTO via polimerizacao in situ assistida por ultrassom

    Energy Technology Data Exchange (ETDEWEB)

    Prado, Bruna R.; Bartoli, Julio R., E-mail: bartoli@unicamp.br [Universidade Estadual de Campinas (UNICAMP), Campinas, SP (Brazil); Ito, Edson N. [Universidade Federal do Rio Grande do Norte (UFRN), Natal, RN (Brazil)

    2015-07-01

    In this work is presented the synthesis of nanocomposites of poly(methyl methacrylate), PMMA, with organically montmorillonite (OMMT) modified clays by in situ polymerization assisted by sonication. A statistically designed experiment was used, central composing design (CCD), to study the effect of synthesis variables on the dispersion of nanoparticles in PMMA matrix. The processing and formulation factors studied were: energy of sonication and Flory-Huggins interaction parameter between PMMA and organoclay. The structural (XRD) and morphological (TEM) characterizations of the PMMA/OMMT nanocomposites are compared with the literature. It was observed significant exfoliation of OMMT modified with hydroxyl groups in the nanocomposites of PMMA, mainly at the low ultrasonic energy level (90 and 105 kJ) studied. (author)

  12. Bragg grating writing in PMMA microstructured polymer optical fibers in less than 7 minutes

    DEFF Research Database (Denmark)

    Bundalo, Ivan-Lazar; Nielsen, Kristian; Markos, Christos

    2014-01-01

    We demonstrate fiber Bragg grating (FBG) writing in PMMA microstructured Polymer Optical Fibers (mPOFs) using UV Phase Mask technique with writing times shorter than 10 min. The shortest writing time was 6 minutes and 50 seconds and the longest writing time was 8 min and 50 sec. The FBGs were...... written in a 125 x00B5;m PMMA mPOF having 3-rings of holes, the reflection peaks were centred at 632.6 nm and have a reflectivity as high as 26 dB. We also demonstrate how the writing dynamics depends on the intensity of the writing beam....

  13. Influence of amine-grafted multi-walled carbon nanotubes on physical and rheological properties of PMMA-based nanocomposites

    International Nuclear Information System (INIS)

    Kim, Ki-Seok; Park, Soo-Jin

    2011-01-01

    In this work, poly(methyl methacrylate) (PMMA) was grafted onto amine treated multi-walled carbon nanotubes (NH-MWNTs) and the physical and rheological properties of the NH-MWNTs-g-PMMA nanocomposites were investigated. The graft reaction of NH-MWNTs and the PMMA matrix was confirmed from the change of the N 1S peaks, including those of amine oxygen and amide oxygen, by X-ray photoelectron spectroscopy (XPS). The thermal and mechanical properties of the NH-MWNT-g-PMMA nanocomposites were enhanced by the graft reaction between NH-MWNTs and PMMA matrix. In addition, the viscosity of the nanocomposites was increased with the addition of NH-MWNTs. Storage (G') and loss modulus (G'') were significantly increased by increase in the NH-MWNT content compared to acid-treated MWNTs/PMMA nanocomposites. This increase was attributed to the strong interaction by the grafting reaction between NH-MWNTs and the PMMA matrix. - Graphical abstract: This describes the increase of mechanical properties in NH-MWNTs-g-PMMA hybrid composites with different NH-MWNT contents. Highlights: → Aminized carbon nanotubes are used as reinforcement for poly(methylmethacrylate). → Poly(methylmethacrylate) is grafted on aminized carbon nanotubes by thermal reaction. → Grafting of carbon nanotubes and polymer provide enhanced physical properties. → It was due to the strong interaction between carbon nanotubes and polymer matrix.

  14. Candida albicans biofilms and MMA surface treatment influence the adhesion of soft denture liners to PMMA resin

    Directory of Open Access Journals (Sweden)

    Martinna de Mendonça e Bertolini

    2014-01-01

    Full Text Available The effect of Candida albicans biofilms and methyl methacrylate (MMA pretreatment on the bond strength between soft denture liners and polymethyl methacrylate (PMMA resin was analyzed. Specimens were prepared and randomly divided with respect to PMMA pretreatment, soft liner type (silicone-based or PMMA-based, and presence or absence of a C. albicans biofilm. Samples were composed of a soft denture liner bonded between two PMMA bars. Specimens (n = 10 were incubated to produce a C. albicans biofilm or stored in sterile PBS for 12 days. The tensile bond strength test was performed and failure type was determined using a stereomicroscope. Surface roughness (SR and scanning electron microscopy (SEM analysis were performed on denture liners (n = 8. Highest bond strength was observed in samples containing a silicone-based soft liner and stored in PBS, regardless of pretreatment (p < 0.01. Silicone-based specimens mostly underwent adhesive failures, while samples containing PMMA-based liners predominantly underwent cohesive failures. The silicone-based specimens SR decreased after 12 days of biofilm accumulation or PBS storage, while the SR of PMMA-based soft liners increased (p < 0.01. The PMMA-based soft liners surfaces presented sharp valleys and depressions, while silicone-based specimens surfaces exhibited more gentle features. In vitro exposure to C. albicans biofilms reduced the adhesion of denture liners to PMMA resin, and MMA pretreatment is recommended during relining procedures.

  15. Seepage/Cement Interactions

    International Nuclear Information System (INIS)

    Carpenter, D.

    2000-01-01

    The Development Plan (CRWMS M andO 1999a) pertaining to this task defines the work scopes and objectives for development of various submodels for the Physical and Chemical Environment Abstraction Model for TSPA-LA. The Development Plan (CRWMS M andO 1999a) for this specific task establishes that an evaluation be performed of the chemical reactions between seepage that has entered the drift and concrete which might be used in the repository emplacement drifts. The Development Plan (CRWMS M andO 1999a) then states that the potential effects of these water/grout reactions on chemical conditions in the drift be assessed factoring in the influence of carbonation and the relatively small amount of grout. This task is also directed at: (1) developing a conceptualization of important cement/seepage interactions and potential impacts on EBS performance, (2) performing a screening analysis to assess the importance of cement/seepage interactions. As the work progresses and evolves on other studies, specifically the Engineered Barrier System: Physical and Chemical Environment (P andCE) Model (in progress), many of the issues associated with items 1 and 2, above, will be assessed. Such issues include: (1) Describing the mineralogy of the specified cementitious grout and its evolution over time. (2) Describing the composition of the water before contacting the grout. (3) Developing reasonable upper-bound estimates for the composition of water contacting grout, emphasizing pH and concentrations for anions such as sulfate. (4) Evaluating the equilibration of cement-influenced water with backfill and gas-phase CO 2 . (5) Developing reasonable-bound estimates for flow rate of affected water into the drift. The concept of estimating an ''upper-bound'' range for reaction between the grout and the seepage, particularly in terms of pH is based on equilibrium being established between the seepage and the grout. For example, this analysis can be based on equilibrium being established as

  16. Microfluidic DNA microarrays in PMMA chips: streamlined fabrication via simultaneous DNA immobilization and bonding activation by brief UV exposure

    DEFF Research Database (Denmark)

    Sabourin, David; Petersen, J; Snakenborg, Detlef

    2010-01-01

    This report presents and describes a simple and scalable method for producing functional DNA microarrays within enclosed polymeric, PMMA, microfluidic devices. Brief (30 s) exposure to UV simultaneously immobilized poly(T)poly(C)-tagged DNA probes to the surface of unmodified PMMA and activated...... the surface for bonding below the glass transition temperature of the bulk PMMA. Functionality and validation of the enclosed PMMA microarrays was demonstrated as 18 patients were correctly genotyped for all eight mutation sites in the HBB gene interrogated. The fabrication process therefore produced probes...... with desired hybridization properties and sufficient bonding between PMMA layers to allow construction of microfluidic devices. The streamlined fabrication method is suited to the production of low-cost microfluidic microarray-based diagnostic devices and, as such, is equally applicable to the development...

  17. 76 FR 76760 - Gray Portland Cement and Cement Clinker From Japan

    Science.gov (United States)

    2011-12-08

    ... and Cement Clinker From Japan Determination On the basis of the record \\1\\ developed in the subject... duty order on gray Portland cement and cement clinker from Japan would be likely to lead to... and Cement Clinker from Japan: Investigation No. 731- TA-461 (Third Review). By order of the...

  18. Seating load parameters impact on dental ceramic reinforcement conferred by cementation with resin-cements.

    LENUS (Irish Health Repository)

    Addison, Owen

    2010-09-01

    Cementation of all-ceramic restorations with resin-cements has been demonstrated to reduce the incidence of fracture in service. The aim was to investigate the influence of loading force and loading duration applied during cementation on the reinforcement conferred by a resin-cement on a leucite reinforced glass-ceramic.

  19. The Effects of Lithium Triflate (LiCF3SO3) on the PMMA-based Solid Polymer Electrolytes

    International Nuclear Information System (INIS)

    Chew, K. W.; Chen, S. S.; Pang, W. L.; Tan, C. G.; Osman, Z.

    2010-01-01

    The effects of Lithium triflate salt (LiCF 3 SO 3 ), on the poly (methyl methacrylate)(PMMA)-based solid polymer electrolytes plasticized with propylene carbonate (PC) solvated in Tetrahydrofuran (THF) have been studied through a.c impedance spectroscopy and infrared spectroscopy. Lithium triflate was incorporated into the predetermined PMMA/PC system that has the highest value of ionic conductivity. In current investigations, four combination systems: Pure PMMA, (PMMA+PC) systems, (PMMA+LiCF 3 SO 3 ) and (PMMA+PC+LiCF 3 SO 3 ) systems were prepared using the solution cast method. Solutions were stirred for numerous hours to obtain a homogenous solution before it is poured into the petri dishes under ambient temperature to form the solid electrolyte thin film. The films were then removed from petri discs and transferred into the dessicator for further drying prior to the different tests. From the characterization done through the a.c impedance spectroscopy, the highest room temperature ionic conductivity in the pure PMMA sample, (PMMA+PC) system and (PMMA+LiCF 3 SO 3 ) system is 2.83x10 -12 Scm -1 , 4.39x10 -11 Scm -1 and 3.93x10 -6 Scm -1 respectively. The conductivity for (PMMA+PC+LiCF 3 SO 3 ) system was obtained with the 30 wt% of lithium triflate, which is 2.48x10 -5 Scm -1 . Infrared spectroscopy shows that complexation occurred between the polymer and the plasticizer, and the polymer and plasticizer and salt. The interactions have been studied in the C=O band, C-O-C band and the O-CH 3 band.

  20. Cement radwaste solidification studies third annual report

    International Nuclear Information System (INIS)

    Brown, D.J.; James, J.M.; Lee, D.J.; Smith, D.L.; Walker, A.T.

    1982-03-01

    This report summarises cement radwaste studies carried out at AEE Winfrith during 1981 on the encapsulation of medium and low active waste in cement. During the year more emphasis has been placed on the work which is directly related to the solidification of SGHWR active sludge. Information has been obtained on the properties of 220 dm 3 drums of cemented waste. The use of cement grouts for the encapsulation of solid items has also been investigated during 1981. (U.K.)

  1. Characterization of cement-stabilized Cd wastes

    International Nuclear Information System (INIS)

    Maria Diez, J.; Madrid, J.; Macias, A.

    1996-01-01

    Portland cement affords both physical and chemical immobilization of cadmium. The immobilization has been studied analyzing the pore fluid of cement samples and characterizing the solid pastes by X-ray diffraction. The influence of cadmium on the cement hydration and on its mechanical properties has been also studied by isothermal conduction calorimetry and by the measure of strength and setting development. Finally, the effect of cement carbonation on the immobilization of cadmium has been analyzed

  2. Substantial global carbon uptake by cement carbonation

    OpenAIRE

    Xi, Fengming; Davis, Steven J.; Ciais, Philippe; Crawford-Brown, Douglas; Guan, Dabo; Pade, Claus; Shi, Tiemao; Syddall, Mark; Lv, Jie; Ji, Lanzhu; Bing, Longfei; Wang, Jiaoyue; Wei, Wei; Yang, Keun-Hyeok; Lagerblad, Björn

    2016-01-01

    Calcination of carbonate rocks during the manufacture of cement produced 5% of global CO2 emissions from all industrial process and fossil-fuel combustion in 20131, 2. Considerable attention has been paid to quantifying these industrial process emissions from cement production2, 3, but the natural reversal of the process—carbonation—has received little attention in carbon cycle studies. Here, we use new and existing data on cement materials during cement service life, demolition, and secondar...

  3. Cementation unit for radioactive wastes

    International Nuclear Information System (INIS)

    Dellamano, Jose Claudio; Vicente, Roberto; Lima, Jose Rodrigues de

    2001-01-01

    This communication describes the waste cementation process and facility developed at Instituto de Pesquisas Energeticas e Nucleares - IPEN. The process is based on 200 litres batch operation, in drum mixing, with continuous cement feeding. The equipment is a single recoverable helicoidal mixer and a turning table that allows the drum to rotate during the mixing operation, simulating a planetary mixer. The facility was designed to treat contact handled liquids and wet solid wastes, but can be adapted for shielded equipment and remote operation. (author)

  4. 21 CFR 872.3275 - Dental cement.

    Science.gov (United States)

    2010-04-01

    ... 21 Food and Drugs 8 2010-04-01 2010-04-01 false Dental cement. 872.3275 Section 872.3275 Food and... DENTAL DEVICES Prosthetic Devices § 872.3275 Dental cement. (a) Zinc oxide-eugenol—(1) Identification... filling or as a base cement to affix a temporary tooth filling, to affix dental devices such as crowns or...

  5. Cement production from coal conversion residues

    International Nuclear Information System (INIS)

    Brown, L.D.; Clavenna, L.R.; Eakman, J.M.; Nahas, N.C.

    1981-01-01

    Cement is produced by feeding residue solids containing carbonaceous material and ash constituents obtained from converting a carbonaceous feed material into liquids and/or gases into a cement-making zone and burning the carbon in the residue solids to supply at least a portion of the energy required to convert the solids into cement

  6. Multicomponent modelling of Portland cement hydration reactions

    NARCIS (Netherlands)

    Ukrainczyk, N.; Koenders, E.A.B.; Van Breugel, K.

    2012-01-01

    The prospect of cement and concrete technologies depends on more in depth understanding of cement hydration reactions. Hydration reaction models simulate the development of the microstructures that can finally be used to estimate the cement based material properties that influence performance and

  7. Stretching DNA in polymer nanochannels fabricated by thermal imprint in PMMA

    DEFF Research Database (Denmark)

    Thamdrup, Lasse Højlund; Klukowska, A.; Kristensen, Anders

    2008-01-01

    . The stamp is compatible with molecular vapor deposition ( MVD), used for applying a durable chlorosilane based antistiction coating, and allows for imprint up to a temperature of 270 degrees C. The extension of YOYO-1 stained T4 GT7 bacteriophage DNA inside the PMMA nanochannels has been experimentally...

  8. Rewritable 3D bit optical data storage in a PMMA-based photorefractive polymer

    Energy Technology Data Exchange (ETDEWEB)

    Day, D.; Gu, M. [Swinburne Univ. of Tech., Hawthorn, Vic. (Australia). Centre for Micro-Photonics; Smallridge, A. [Victoria Univ., Melbourne (Australia). School of Life Sciences and Technology

    2001-07-04

    A cheap, compact, and rewritable high-density optical data storage system for CD and DVD applications is presented by the authors. Continuous-wave illumination under two-photon excitation in a new poly(methylmethacrylate) (PMMA) based photorefractive polymer allows 3D bit storage of sub-Tbyte data. (orig.)

  9. An approach to correlate experimental and theoretical thermal conductivity of MWNT/PMMA polymer composites

    International Nuclear Information System (INIS)

    Verma, M; Patidar, D; Sharma, K B; Saxena, N S

    2015-01-01

    In this paper an effort is made to correlate temperature dependent effective thermal conductivity measured by experimental method to theoretical results obtained from different models. MWNT/PMMA polymer nanocomposites were prepared by solution casting method, with different wt% of MWNT (0, 0.05, 0.1, 0.2, 0.3, 0.5, 1, 5, 10 wt%) dispersed in the PMMA matrix. The effective thermal conductivity from 30 °C to 110 °C is measured by Hot Disk Thermal Constant Analyser, based on transient plane source technique. Experimental study reveals that effective thermal conductivity increases with increasing concentration of MWNT in PMMA and increases exponentially at high temperatures for high (5, 10) wt% samples. This behavior of effective thermal conductivity is explained in terms of the interactions between polymer–MWNT and MWNT–MWNT. Consequently these results were found to be in agreement with theoretical models such as Series, Parallel, Lewis/Neilson and empirical formula. The discrepancy found in Lewis/Neilson model at high temperature for high wt% of MWNT in PMMA is due to some change in values of parameters incorporated in the model. (paper)

  10. Significance of polymethylmethacrylate (PMMA) modification by zinc oxide nanoparticles for fungal biofilm formation.

    Science.gov (United States)

    Cierech, Mariusz; Kolenda, Adam; Grudniak, Anna M; Wojnarowicz, Jacek; Woźniak, Bartosz; Gołaś, Marlena; Swoboda-Kopeć, Ewa; Łojkowski, Witold; Mierzwińska-Nastalska, Elżbieta

    2016-08-20

    The objective of this study was to obtain a material composite with antifungal properties for dentures to be used as an alternative protocol in denture stomatitis treatment and prevention. Denture stomatitis is still a clinical problem in patients particularly vulnerable to this disease. Composites of PMMA and doped ZnO-NPs (weight concentrations, 2.5%, 5%, 7.5%) and PMMA with sprayed solvothermal and hydrothermal ZnO-NPs were tested. The following investigations of newly formed biomaterials were undertaken: influence on Candida albicans solution, biofilm staining, XTT analysis and a quantitative analysis of adhered C. albicans. These studies evidenced the antifungal activity of both nanocomposites PMMA-ZnO-NPs and the efficacy of sputtering of zinc oxide nanoparticles on the PMMA. The study of the biofilm deposition on the surface showed that antifungal properties increase with increasing concentration of ZnO-NPs. The XTT assay in conjunction with testing the turbidity of solutions may indicate the mechanism by which ZnO-NPs exert their effect on the increased induction of antioxidative stress in microorganism cells. The denture base made of the aforesaid materials may play a preventive role in patients susceptible to fungal infections. Based on the results obtained a modified treatment of stomatitis Type II (Newton's classification) complicated by fungal infection was proposed. Copyright © 2016 Elsevier B.V. All rights reserved.

  11. Interphase and magnetotransport of LSMO-PMMA nanocomposites obtained by a sonochemical method

    Science.gov (United States)

    Romero, Mariano; Pardo, Helena; Faccio, Ricardo; Tumelero, Milton A.; Plá Cid, Cristiani Campos; Castiglioni, Jorge; Pasa, André A.; Mombrú, Álvaro W.

    2015-05-01

    In this report, we studied the structural, microstructural and compositional trends in a manganite-polymethylmethacrilate (LSMO-PMMA) nanocomposite prepared by a sonochemical method focusing in the study of its interphase and its correlation with magnetotransport. Differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), Raman scattering and X-ray powder diffraction (XRPD) studies showed evidence of PMMA reactivity with partial decomposition at the LSMO nanoparticles interface. Additionally, grazing incidence small angle X-ray scattering (GISAXS) and high resolution transmission electron microscopy (HRTEM) showed information about the microstructure and the separation between nanoparticles in these nanocomposite materials. An enhancement in the low field magnetoresistance (LFMR) respect to pure LSMO was observed for a 20% weight fraction addition of PMMA in the high temperature regime (205-305 K) probably due to the increase in the magnetic disorder at the grain boundaries caused by the ultrasonic treatment. Nevertheless, lower PMMA weight fraction addition showed no enhancement in LFMR respect to pure LSMO, probably in agreement with the higher decomposition rate observed at the interphase.

  12. Silicon-ion-implanted PMMA with nanostructured ultrathin layers for plastic electronics

    Science.gov (United States)

    Hadjichristov, G. B.; Ivanov, Tz E.; Marinov, Y. G.

    2014-12-01

    Being of interest for plastic electronics, ion-beam produced nanostructure, namely silicon ion (Si+) implanted polymethyl-methacrylate (PMMA) with ultrathin nanostructured dielectric (NSD) top layer and nanocomposite (NC) buried layer, is examined by electric measurements. In the proposed field-effect organic nanomaterial structure produced within the PMMA network by ion implantation with low energy (50 keV) Si+ at the fluence of 3.2 × 1016 cm-2 the gate NSD is ion-nanotracks-modified low-conductive surface layer, and the channel NC consists of carbon nanoclusters. In the studied ion-modified PMMA field-effect configuration, the gate NSD and the buried NC are formed as planar layers both with a thickness of about 80 nm. The NC channel of nano-clustered amorphous carbon (that is an organic semiconductor) provides a huge increase in the electrical conduction of the material in the subsurface region, but also modulates the electric field distribution in the drift region. The field effect via the gate NSD is analyzed. The most important performance parameters, such as the charge carrier field-effect mobility and amplification of this particular type of PMMA- based transconductance device with NC n-type channel and gate NSD top layer, are determined.

  13. Reinforcement of a PMMA resin for interim fixed prostheses with silica nanoparticles.

    Science.gov (United States)

    Topouzi, Marianthi; Kontonasaki, Eleana; Bikiaris, Dimitrios; Papadopoulou, Lambrini; Paraskevopoulos, Konstantinos M; Koidis, Petros

    2017-05-01

    Fractures in long span provisional/interim restorations are a common complication. Adequate fracture toughness is necessary to resist occlusal forces and crack propagation, so these restorations should be constructed with materials of improved mechanical properties. The aim of this study was to investigate the possible reinforcement of neat silica nanoparticles and trietoxyvinylsilane-modified silica nanoparticles in a PMMA resin for fixed interim restorations. Composite PMMA-Silica nanoparticles powders were mixed with PMMA liquid and compact bar shaped specimens were fabricated according to the British standard BS EN ISO 127337:2005. The single-edge notched method was used to evaluate fracture toughness (three-point bending test), while the dynamic thermomechanical properties (Storage Modulus, Loss Modulus, tanδ) of a series of nanocomposites with different amounts of nanoparticles (0.25%, 0.50%, 0.75%, 1% w.t.) were evaluated. Statistical analysis was performed and the statistically significant level was set to pPMMA resins used in fixed provisional restorations. Copyright © 2017 Elsevier Ltd. All rights reserved.

  14. The Effect of H2SO4 Concentration on the Ionic Conductivity of Liquid PMMA Oligomer

    International Nuclear Information System (INIS)

    Norashima Kamaluddin; Famiza Abdul Latif; Han, C.C.; Ruhani Ibrahim; Sharil Fadli Mohamad Zamri; Norashima Kamaluddin; Famiza Abdul Latif; Han, C.C.; Ruhani Ibrahim; Sharil Fadli Mohamad Zamri

    2015-01-01

    To date gel and film type polymer electrolytes have been widely synthesized due to their wide range of electrical properties. However these types of polymer electrolytes exhibit poor mechanical stability and poor electrode-electrolyte contact hence deprive the overall performance of a battery system. Therefore, in order to indulge the advantages of polymer as electrolyte, a new class of polymer electrolyte was synthesized and investigated. In this study, liquid poly(methyl methacrylate) (PMMA) electrolyte was synthesized using the simplest free radical polymerization technique using benzoyl peroxide as the initiator. At this stage, it was found that this liquid PMMA oligomer (MW=3000 g/ mole) has a potential as electrolyte in electrochemical devices. It was found that an ionic conductivity of ∼10 -7 S/ cm at room temperature can be achieved when only small volume of high molarity of sulfuric acid (H 2 SO 4 ) was doped in the liquid PMMA oligomer. The properties of this liquid PMMA oligomer were further investigated using Fourier Transform Infrared Spectroscopy (FTIR). (author)

  15. Fabrication of γ-MPS-Modified HNT-PMMA Nanocomposites by Ultrasound-Assisted Miniemulsion Polymerization

    Science.gov (United States)

    Buruga, Kezia; Kalathi, Jagannathan T.

    2018-04-01

    Halloysite nanotubes (HNTs) were modified with γ-methacryloxypropyltrimethoxysilane (γ-MPS) to improve their interaction with the polymer, and the modified HNTs (MHNTs) were subsequently used for the synthesis of MHNT-polymethylmethacrylate (PMMA) nanocomposites by miniemulsion polymerization assisted by ultrasound. Reduced agglomeration of HNTs due to modification with γ-MPS was evident from scanning electron microscopy analysis. Modification of HNTs and exfoliation of MHNTs in the polymer nanocomposite were confirmed by the presence of their respective characteristic peaks in Fourier-transform infrared spectra and x-ray diffraction patterns. Transmission electron microscopic analysis showed that the surface of the MHNTs differed significantly from that of unmodified HNTs. MHNT-PMMA nanocomposite exhibited significantly higher glass-transition temperature (T g) compared with neat PMMA or unmodified HNT-PMMA nanocomposite. Hence, such modification of HNTs along with miniemulsion polymerization assisted by ultrasound is a promising approach to achieve better dispersion of HNTs in the polymer and to obtain nanocomposites with enhanced properties.

  16. Covalent bonding of PMMA, PBMA, and poly(HEMA) to hydroxyapatite particles

    NARCIS (Netherlands)

    Liu, Q.; de Wijn, J.R.; van Blitterswijk, Clemens

    1998-01-01

    In our earlier study, we showed that the surface hydroxyl groups of hydroxyapatite have the ability to react with organic isocyanate groups. In this study, the feasibility of grafting poly(methyl methacrylate) (PMMA), poly(n-butyl methacrylate) (PBMA), and Poly(hydroxyethyl methacrylate)

  17. The presence of nanostructured Al2O3 in PMMA-based gel electrolytes

    Czech Academy of Sciences Publication Activity Database

    Krejza, O.; Velická, Jana; Sedlaříková, M.; Vondrák, Jiří

    2008-01-01

    Roč. 178, č. 2 (2008), s. 774-778 ISSN 0378-7753 R&D Projects: GA AV ČR(CZ) KJB208130604; GA ČR(CZ) GA104/06/1471 Institutional research plan: CEZ:AV0Z40320502 Keywords : poly mer electrolyte * PMMA * ionic conductivity Subject RIV: CG - Electrochemistry Impact factor: 3.477, year: 2008

  18. Porous asymmetric SiO2-g-PMMA nanoparticles produced by phase inversion

    KAUST Repository

    Munirasu, Selvaraj

    2014-07-22

    A new kind of asymmetric organic-inorganic porous structure has been proposed. Asymmetric lattices of polymer grafted silica nanoparticles were manufactured by casting and phase inversion in water. Silica nanoparticles were first functionalized with 3-(dimethylethoxysilyl)propyl-2-bromoisobutyrate, followed by grafting of poly(methylmethacrylate) (PMMA) segments, performed by atom-transfer radical polymerization. Mechanically stable self-standing films were prepared by casting a dispersion of functionalized nanoparticles in different solvents and immersion in water. The resulting asymmetrically porous morphology and nanoparticle assembly was characterized by scanning electron and atomic force microscopy. The PMMA functionalized SiO2 hybrid material in acetone or acetone/dioxane led to the best-assembled structures. Porous asymmetric membranes were prepared by adding free PMMA and PMMA terminated with hydrophilic hydroxyl group. Nitrogen flow of 2800 L m-2 h -1 was measured at 1.3 bar demonstrating the porosity and potential application for membrane technology. © 2014 Springer Science+Business Media New York.

  19. 2 filler on the dielectric permittivity and electrical modulus of PMMA

    Indian Academy of Sciences (India)

    plex in solution phase.9 Debye theory of dipolar relaxation apprehends the ... present a study on the effect of Zn(NO3)2 filler in PMMA matrix, with a view to .... 3.4 EDX analysis. The quantitative and qualitative elemental analyses of the.

  20. The effect of enhancing the hydrophobicity of OMMT on the characteristics of PMMA/OMMT nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Yamagata, Shuichi, E-mail: shuic@den.hokudai.ac.jp [Department of Orthodontics, Graduate School of Dental Medicine, Hokkaido University, Kita 13 Nishi 7, Kita-ku, Sapporo 060-8586 (Japan); Hamba, Yusuke [Department of Orthodontics, Graduate School of Dental Medicine, Hokkaido University, Kita 13 Nishi 7, Kita-ku, Sapporo 060-8586 (Japan); Akasaka, Tsukasa [Department of Biomedical Materials and Engineering, Graduate School of Dental Medicine, Hokkaido University, Kita 13 Nishi 7, Kita-ku, Sapporo 060-8586 (Japan); Ushijima, Natsumi [Support Section for Education and Research, Graduate School of Dental Medicine, Hokkaido University, Kita 13 Nishi 7, Kita-ku, Sapporo 060-8586 (Japan); Uo, Motohiro [Advanced Biomaterials, Department of Restorative Sciences, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University, 1-5-45, Yushima, Bunkyo-ku, Tokyo 113-8549 (Japan); Iida, Junichiro [Department of Orthodontics, Graduate School of Dental Medicine, Hokkaido University, Kita 13 Nishi 7, Kita-ku, Sapporo 060-8586 (Japan); Watari, Fumio [Department of Biomedical Materials and Engineering, Graduate School of Dental Medicine, Hokkaido University, Kita 13 Nishi 7, Kita-ku, Sapporo 060-8586 (Japan)

    2012-12-01

    Highlights: Black-Right-Pointing-Pointer PMMA/OMMT nanocomposites were fabricated using a solution intercalation method. Black-Right-Pointing-Pointer The silicate platelets were largely well dispersed independent of the hydrophobicity. Black-Right-Pointing-Pointer The partially exfoliation of the silicate layers were observed. Black-Right-Pointing-Pointer The flexural modulus of the nanocomposites increased favorably. Black-Right-Pointing-Pointer The strain at breakage of the nanocomposites remained suitable for our use. - Abstract: Transparent poly(methyl methacrylate)/organically modified montmorillonite (PMMA/OMMT) nanocomposites were fabricated using a solution intercalation method. Two grades of OMMT modified with quaternary alkylammonium ions and containing different amounts of organic matter, NZ70 and NX, were used. X-ray diffraction patterns showed that the peaks regarded as a (0 0 1) d-spacing and a second peak were shifted toward lower 2{theta} values, implying the expansion or the partial exfoliation of the silicate layers, respectively. TEM images showed that the silicate platelets were largely well dispersed independent of the hydrophobicity, although some aggregates were observed. The flexural modulus of the PMMA/OMMT nanocomposites increased favorably with an increasing amount of OMMT of either grade. However, only the NX displayed comparable strain at breakage to that of the PMMA. These results suggest that the highly hydrophobic grade NX shows great promise for use in nanocomposites made via solution intercalation.

  1. The effect of alumina nanofillers size and shape on mechanical behavior of PMMA matrix composite

    Directory of Open Access Journals (Sweden)

    Ben Hasan Somaya Ahmed

    2014-01-01

    Full Text Available Composites with the addition of alumina nanofillers show improvement in mechanical properties. The PMMA polymer was used as a matrix and two different types of nanofillers, having extremely different shapes were added in the matrix to form the composite. Reinforcements were based on alumina nanoparticles having either spherical shape or whiskers having the length to diameter ratio of 100. The influence of alumina fillers size, shape and fillers loading on mechanical properties of prepared composite were studied using the nanoindentation measurements and dynamic mechanical analysis. It was observed that both alumina whiskers and alumina spherical nanoparticles added in the PMMA matrix improved the mechanical properties of the composite but the improvement was significantly higher with alumina whisker reinforcement. The concentration of the reinforcing alumina spherical nanoparticles and alumina whiskers in PMMA matrix varied up to 5 wt. %. The best performance was obtained by the addition of 3 wt. % of alumina whiskers in the PMMA matrix with regard to mechanical properties of the obtained composite.

  2. FIB NANOPATTERNING OF METAL FILMS ON PMMA SUBSTRATES: NON-SPUTTERING MODE

    DEFF Research Database (Denmark)

    Tavares, Luciana; Adashkevich, Vadzim; Chiriaev, Serguei

    polymer materials, which results in material shrinkage in the irradiated areas [2]. In this work, we demonstrate that this mechanism can be used for nanopatterning thin metal films deposited on PMMA resist spin-coated onto a silicon substrate. For this purpose, the samples were irradiated with He+ FIB...

  3. Correlation between MWCNT aspect ratio and the mechanical properties of composites of PMMA and MWCNTs

    Science.gov (United States)

    Mu, Mulan; Teblum, Eti; Figiel, Łukasz; Nessim, Gilbert Daniel; McNally, Tony

    2018-04-01

    The correlation between MWCNT aspect ratio and the quasi-static and dynamic mechanical properties of composites of MWCNTs and PMMA was studied for relatively long MWCNT lengths, in the range 0.3 mm to 5 mm (aspect ratios up to 5 × 105) and at low loading (0.15 wt%). The height of the MWCNTs prepared were modulated by controlling the amount of water vapour introduced in the reactor limiting Ostwald ripening of the catalyst, the formation of amorphous carbon and any increase in CNT diameter. The Tg of PMMA increased by up to 4 °C on addition of the longest tubes as they have the ability to form physical junctions with the polymer chains which lead to enhanced PMMA-MWCNTs interactions and increased mechanical properties, Young’s modulus by 20% on addition of 5 mm long MWCNTs. Predictions of the Young’s modulus of the composites of PMMA and MWCNT with the Mori-Tanaka theory show that future micromechanical models should account for MWCNT agglomeration and polymer-nanotube interactions as a function of CNT length.

  4. Study of Polymeric Luminescent Blend (PC/PMMA) Doped with Europium Complex under Gamma-Iradiation

    International Nuclear Information System (INIS)

    Parra, D. F.

    2006-01-01

    Spectroscopic properties of blends formed by bisphenol-A polycarbonate (PC) and poly(methyl methacrylate) (PMMA) doped with europium in organic complex were studied. Polymeric luminescent blends are potential materials for many applications; however, little information has been reported concerning the stability under thermal and radiation conditions. Luminescent films were synthesized from europium thenoyltrifluoroacetonate at different concentrations doped in PC/PMMA blends. Films produced of the luminescent polymer blend were irradiated in a 60 C o source. Their luminescent properties, in the solid state, as well as, the thermal oxidative resistance after gamma irradiation was investigated. These systems were characterized by elemental analysis, thermogravimetry (TGA), differential scanning calorimetry (DSC) and infrared spectroscopy (FTIR). Based on TGA data, the thermal stability of PC/PMMA:(tta)3 system is higher than the polymer blend. The DSC results indicated that those new systems are chemically stables. The emission spectra of the Eu 3 +-tta complex doped in the PC/PMMA recorded at 298 and 77 K exhibited the characteristic bands arising from the 5 D 0 →7 F J transitions (J = 0-6). The luminescence intensity decreases with increasing of precursor concentration in the doped polymer obtained by chemical reaction. This result is different from that of samples obtained by physical method in melting doping. The blend was irradiated under ionizing radiation of 60 C o source. After irradiation of the luminescent films the physical properties of luminescence, thermal and oxidative stability were evaluated.(Fapesp and Cnpq financial support)

  5. The effect of enhancing the hydrophobicity of OMMT on the characteristics of PMMA/OMMT nanocomposites

    International Nuclear Information System (INIS)

    Yamagata, Shuichi; Hamba, Yusuke; Akasaka, Tsukasa; Ushijima, Natsumi; Uo, Motohiro; Iida, Junichiro; Watari, Fumio

    2012-01-01

    Highlights: ► PMMA/OMMT nanocomposites were fabricated using a solution intercalation method. ► The silicate platelets were largely well dispersed independent of the hydrophobicity. ► The partially exfoliation of the silicate layers were observed. ► The flexural modulus of the nanocomposites increased favorably. ► The strain at breakage of the nanocomposites remained suitable for our use. - Abstract: Transparent poly(methyl methacrylate)/organically modified montmorillonite (PMMA/OMMT) nanocomposites were fabricated using a solution intercalation method. Two grades of OMMT modified with quaternary alkylammonium ions and containing different amounts of organic matter, NZ70 and NX, were used. X-ray diffraction patterns showed that the peaks regarded as a (0 0 1) d-spacing and a second peak were shifted toward lower 2θ values, implying the expansion or the partial exfoliation of the silicate layers, respectively. TEM images showed that the silicate platelets were largely well dispersed independent of the hydrophobicity, although some aggregates were observed. The flexural modulus of the PMMA/OMMT nanocomposites increased favorably with an increasing amount of OMMT of either grade. However, only the NX displayed comparable strain at breakage to that of the PMMA. These results suggest that the highly hydrophobic grade NX shows great promise for use in nanocomposites made via solution intercalation.

  6. Improved osteoblast response to UV-irradiated PMMA/TiO2 nanocomposites with controllable wettability.

    Science.gov (United States)

    Shayan, Mahdis; Jung, Youngsoo; Huang, Po-Shun; Moradi, Marzyeh; Plakseychuk, Anton Y; Lee, Jung-Kun; Shankar, Ravi; Chun, Youngjae

    2014-12-01

    Osteoblast response was evaluated with polymethylmethacrylate (PMMA)/titanium dioxide (TiO2) nanocomposite thin films that exhibit the controllable wettability with ultraviolet (UV) treatment. In this study, three samples of PMMA/TiO2 were fabricated with three different compositional volume ratios (i.e., 25/75, 50/50, and 75/25) followed by UV treatment for 0, 4, and 8 h. All samples showed the increased hydrophilicity after UV irradiation. The films fabricated with the greater amount of TiO2 and treated with the longer UV irradiation time increased the hydrophilicity more. The partial elimination of PMMA on the surface after UV irradiation created a durable hydrophilic surface by (1) exposing higher amount of TiO2 on the surface, (2) increasing the hydroxyl groups on the TiO2 surface, and (3) producing a mesoporous structure that helps to hold the water molecules on the surface longer. The partial elimination of PMMA on the surface was confirmed by Fourier transform infrared spectroscopy. Surface profiler and atomic force microscopy demonstrated the increased surface roughness after UV irradiation. Both scanning electron microscopy and energy-dispersive X-ray spectroscopy demonstrated that particles containing calcium and phosphate elements appeared on the 8 h UV-treated surface of PMMA/TiO2 25/75 samples after 4 days soaking in Dulbecco's Modified Eagle Medium. UV treatment showed the osteoblast adhesion improved on all the surfaces. While all UV-treated hydrophilic samples demonstrated the improvement of osteoblast cell adhesion, the PMMA/TiO2 25/75 sample after 8 h UV irradiation (n = 5, P value = 0.000) represented the best cellular response as compared to other samples. UV-treated PMMA/TiO2 nanocomposite thin films with controllable surface properties represent a high potential for the biomaterials used in both orthopedic and dental applications.

  7. Preparation of Transparent Bulk TiO2/PMMA Hybrids with Improved Refractive Indices via an in Situ Polymerization Process Using TiO2 Nanoparticles Bearing PMMA Chains Grown by Surface-Initiated Atom Transfer Radical Polymerization.

    Science.gov (United States)

    Maeda, Satoshi; Fujita, Masato; Idota, Naokazu; Matsukawa, Kimihiro; Sugahara, Yoshiyuki

    2016-12-21

    Transparent TiO 2 /PMMA hybrids with a thickness of 5 mm and improved refractive indices were prepared by in situ polymerization of methyl methacrylate (MMA) in the presence of TiO 2 nanoparticles bearing poly(methyl methacrylate) (PMMA) chains grown using surface-initiated atom transfer radical polymerization (SI-ATRP), and the effect of the chain length of modified PMMA on the dispersibility of modified TiO 2 nanoparticles in the bulk hybrids was investigated. The surfaces of TiO 2 nanoparticles were modified with both m-(chloromethyl)phenylmethanoyloxymethylphosphonic acid bearing a terminal ATRP initiator and isodecyl phosphate with a high affinity for common organic solvents, leading to sufficient dispersibility of the surface-modified particles in toluene. Subsequently, SI-ATRP of MMA was achieved from the modified surfaces of the TiO 2 nanoparticles without aggregation of the nanoparticles in toluene. The molecular weights of the PMMA chains cleaved from the modified TiO 2 nanoparticles increased with increases in the prolonging of the polymerization period, and these exhibited a narrow distribution, indicating chain growth controlled by SI-ATRP. The nanoparticles bearing PMMA chains were well-dispersed in MMA regardless of the polymerization period. Bulk PMMA hybrids containing modified TiO 2 nanoparticles with a thickness of 5 mm were prepared by in situ polymerization of the MMA dispersion. The transparency of the hybrids depended significantly on the chain length of the modified PMMA on the nanoparticles, because the modified PMMA of low molecular weight induced aggregation of the TiO 2 nanoparticles during the in situ polymerization process. The refractive indices of the bulk hybrids could be controlled by adjusting the TiO 2 content and could be increased up to 1.566 for 6.3 vol % TiO 2 content (1.492 for pristine PMMA).

  8. Facile synthesis, dielectric properties and electrocatalytic activities of PMMA-NiFe2O4 nanocomposite

    International Nuclear Information System (INIS)

    Maji, Pranabi; Choudhary, Ram Bilash

    2017-01-01

    The paper deals with the dielectric and catalytic properties of poly (methyl methacrylate)-nikel ferrite (PMMA-NiFe 2 O 4 ) nanocomposite. The nanocomposite was prepared by using a general and facile synthesis strategy. Fourier transform infrared (FTIR) and X-ray diffraction (XRD) spectra confirmed the formation of PMMA-NiFe 2 O 4 nanocomposite. Field effect scanning electron microscopic (FESEM) and transmission electron microscopic (TEM) images revealed that NiFe 2 O 4 nanoparticles were uniformly distributed and were tightly adhered with PMMA matrix owing to surface modification with 3-methacryloyloxy propyl trimethoxy silane (KH-570). Thermal stability was enhanced by incorporation of NiFe 2 O 4 nanofillers. The nanocomposite showed high dielectric constant and low dielectric loss. The achieved dielectric and thermal property inferred the potential application of this material in energy storage and embedded electronics devices. Further, the as prepared nanocomposite also offered a remarkable electrochemical performance towards hydrogen peroxide (H 2 O 2 ) sensing. - Highlights: • PMMA-NiFe 2 O 4 nanocomposite was synthesized via free radical polymerization. • The nanocomposite exhibited high value of dielectric constant (51) and tanδ (0.3). • Thermal stability of the PMMA matrix was improved by the incorporation of NiFe 2 O 4. • The H 2 O 2 detection limit was estimated 44 μM when signal to noise (S/N) ration was 3. • The electrochemical sensitivity of H 2 O 2 was calculated 0.6727 μA mM -1 .

  9. Pullout characteristics of percutaneous pedicle screws with different cement augmentation methods in elderly spines: An in vitro biomechanical study.

    Science.gov (United States)

    Charles, Y P; Pelletier, H; Hydier, P; Schuller, S; Garnon, J; Sauleau, E A; Steib, J-P; Clavert, P

    2015-05-01

    Vertebroplasty prefilling or fenestrated pedicle screw augmentation can be used to enhance pullout resistance in elderly patients. It is not clear which method offers the most reliable fixation strength if axial pullout and a bending moment is applied. The purpose of this study is to validate a new in vitro model aimed to reproduce a cut out mechanism of lumbar pedicle screws, to compare fixation strength in elderly spines with different cement augmentation techniques and to analyze factors that might influence the failure pattern. Six human specimens (82-100 years) were instrumented percutaneously at L2, L3 and L4 by non-augmented screws, vertebroplasty augmentation and fenestrated screws. Cement distribution (2 ml PMMA) was analyzed on CT. Vertebral endplates and the rod were oriented at 45° to the horizontal plane. The vertebral body was held by resin in a cylinder, linked to an unconstrained pivot, on which traction (10 N/s) was applied until rupture. Load-displacement curves were compared to simultaneous video recordings. Median pullout forces were 488.5 N (195-500) for non-augmented screws, 643.5 N (270-1050) for vertebroplasty augmentation and 943.5 N (750-1084) for fenestrated screws. Cement augmentation through fenestrated screws led to significantly higher rupture forces compared to non-augmented screws (P=0.0039). The pullout force after vertebroplasty was variable and linked to cement distribution. A cement bolus around the distal screw tip led to pullout forces similar to non-augmented screws. A proximal cement bolus, as it was observed in fenestrated screws, led to higher pullout resistance. This cement distribution led to vertebral body fractures prior to screw pullout. The experimental setup tended to reproduce a pullout mechanism observed on radiographs, combining axial pullout and a bending moment. Cement augmentation with fenestrated screws increased pullout resistance significantly, whereas the fixation strength with the vertebroplasty

  10. Electrically conductive Portland cement concrete.

    Science.gov (United States)

    1986-01-01

    There is a need for an effective, simple-to-install secondary anode system for use in the cathodic protection of reinforced concrete bridge decks. In pursuit of such a system, carbon fibers and carbon black were incorporated in portland cement concre...

  11. Polymer reinforcement of cement systems

    International Nuclear Information System (INIS)

    Swamy, R.N.

    1979-01-01

    In the last couple of decades several cement- and concrete-based composites have come into prominence. Of these, cement-polymer composites, like cement-fibre composites, have been recognised as very promising, and considerable research and development on their properties, fabrication methods and application are in progress. Of the three types of concrete materials which incorporate polymers to form composites, polymer impregnated concrete forms a major development in which hardened concrete is impregnated with a liquid monomer which is subsequently polymerized to form a rigid polymer network in the pores of the parent material. In this first part of the extensive review of the polymer reinforcement of cement systems, the process technology of the various monomer impregnation techniques and the properties of the impregnated composite are assessed critically. It is shown that the high durability and superior performance of polymer impregnated concrete can provide an economic and competitive alternative in in situ strengthening, and in other areas where conventional concrete can only at best provide adequate performance. The review includes a section on radiation-induced polymerization. (author)

  12. Photocatalytic degradation of p-phenylenediamine with TiO2-coated magnetic PMMA microspheres in an aqueous solution

    International Nuclear Information System (INIS)

    Chen, Y.-H.; Liu, Y.-Y.; Lin, R.-H.; Yen, F.-S.

    2009-01-01

    This study investigates the photocatalytic degradation of p-phenylenediamine (PPD) with titanium dioxide-coated magnetic poly(methyl methacrylate) (TiO 2 /mPMMA) microspheres. The TiO 2 /mPMMA microspheres are employed as novel photocatalysts with the advantages of high photocatalytic activity, magnetic separability, and good durability. The scanning electron microscopy (SEM), energy dispersive spectrometer (EDS), and transmission electron microscopy (TEM) images of the TiO 2 /mPMMA microspheres are used to characterize the morphology, element content, and distribution patterns of magnetite and TiO 2 nanoparticles. The BET-specific surface area and saturation magnetization of the TiO 2 /mPMMA microspheres are observed as 2.21 m 2 /g and 4.81 emu/g, respectively. The photocatalytic degradation of PPD are performed under various experimental conditions to examine the effects of initial PPD concentration, TiO 2 /mPMMA microsphere dosage, and illumination condition on the eliminations of PPD and chemical oxygen demand (COD) concentrations. Good repeatability of photocatalytic performance with the use of the TiO 2 /mPMMA microspheres has been demonstrated in the multi-run experiments. The photocatalytic kinetics for the reductions of PPD and COD associated with the initial PPD concentration, UV radiation intensity, and TiO 2 /mPMMA microsphere dosage are proposed. The relationships between the reduction percentages of COD and PPD are clearly presented

  13. Mechanical properties of multi-walled carbon nanotube (MWCNT)/polymethyl methacrylite (PMMA) nanocomposite prepared via the coagulation method

    Science.gov (United States)

    Ismail, Noor Mazni; Aziz, Azizan; Jaafar, Mariatti

    2012-06-01

    Multi-walled carbon nanotube (MWCNT) is well known as one of the best candidates for reinforcing the next generation of high performance nanocomposites due to its excellent mechanical properties. In this study, MWCNTs were dispersed in polymethyl methacrylite (PMMA) matrix to enhance its mechanical strength. MWCNT/PMMA were prepared by simple coagulation method and then hot-pressed to create nanocomposite film consists of rich nanotubes. Samples were prepared in respect to various high filler loading (1%, 3%, 5%, 7% and 10% wt.). Standard ASTM D790 flexural test was used to evaluate the mechanical properties of the composites. The morphology and surface fracture were observed via scanning electron microscope. The properties of the composites where found to be better than the neat PMMA. Flexural strength & flexural modulus of MWCNT/PMMA nanocomposite showed an improvement up to 24.1% and 107.7% compared to the neat PMMA, respectively. These studies therefore demonstrate that MWCNT/PMMA prepared by coagulation method able to successfully improve mechanical properties of PMMA.

  14. Effect of Sr2TiMnO6 fillers on mechanical, dielectric and thermal behaviour of PMMA polymer

    Directory of Open Access Journals (Sweden)

    P. Thomas

    2015-09-01

    Full Text Available Composites of poly(methyl methacrylate (PMMA and Sr2TiMnO6 (STMO were fabricated via melt mixing followed by hot pressing technique. These were characterized using X-ray diffraction (XRD, thermo gravimetric analysis (TGA, differential scanning calorimetry (DSC, thermo mechanical analysis (TMA and impedance analyser for their structural, thermal and dielectric properties. The coefficient of thermal expansion (CTE was measured between 40°C and 100°C for pure PMMA is 115.2 ppm/°C, which was decreased to 78.58 ppm/°C when the STMO content was increased to 50 wt.% in PMMA. There was no difference in the glass transition (Tg temperature of the PMMA polymer and their composites. However, the FTIR analysis indicated possible interaction between the PMMA and STMO. The density and the hardness were increased as the STMO content increased in the PMMA matrix. Permittivity was found to be as high as 30.9 at 100 Hz for the PMMA+STMO-50 wt.% composites, indicating the possibility of using these materials for capacitor applications. The thermal stability of polymer was enhanced by incorporation of STMO fillers.

  15. [Cement augmentation on the spine : Biomechanical considerations].

    Science.gov (United States)

    Kolb, J P; Weiser, L; Kueny, R A; Huber, G; Rueger, J M; Lehmann, W

    2015-09-01

    Vertebral compression fractures are the most common osteoporotic fractures. Since the introduction of vertebroplasty and screw augmentation, the management of osteoporotic fractures has changed significantly. The biomechanical characteristics of the risk of adjacent fractures and novel treatment modalities for osteoporotic vertebral fractures, including pure cement augmentation by vertebroplasty, and cement augmentation of screws for posterior instrumentation, are explored. Eighteen human osteoporotic lumbar spines (L1-5) adjacent to vertebral bodies after vertebroplasty were tested in a servo-hydraulic machine. As augmentation compounds we used standard cement and a modified low-strength cement. Different anchoring pedicle screws were tested with and without cement augmentation in another cohort of human specimens with a simple pull-out test and a fatigue test that better reflects physiological conditions. Cement augmentation in the osteoporotic spine leads to greater biomechanical stability. However, change in vertebral stiffness resulted in alterations with the risk of adjacent fractures. By using a less firm cement compound, the risk of adjacent fractures is significantly reduced. Both screw augmentation techniques resulted in a significant increase in the withdrawal force compared with the group without cement. Augmentation using perforated screws showed the highest stability in the fatigue test. The augmentation of cement leads to a significant change in the biomechanical properties. Differences in the stability of adjacent vertebral bodies increase the risk of adjacent fractures, which could be mitigated by a modified cement compound with reduced strength. Screws that were specifically designed for cement application displayed greatest stability in the fatigue test.

  16. CO2 Capture by Cement Raw Meal

    DEFF Research Database (Denmark)

    Pathi, Sharat Kumar; Lin, Weigang; Illerup, Jytte Boll

    2013-01-01

    The cement industry is one of the major sources of CO2 emissions and is likely to contribute to further increases in the near future. The carbonate looping process has the potential to capture CO2 emissions from the cement industry, in which raw meal for cement production could be used...... as the sorbent. Cyclic experiments were carried out in a TGA apparatus using industrial cement raw meal and synthetic raw meal as sorbents, with limestone as the reference. The results show that the CO2 capture capacities of the cement raw meal and the synthetic raw meal are comparable to those of pure limestone...... that raw meal could be used as a sorbent for the easy integration of the carbonate looping process into the cement pyro process for reducing CO2 emissions from the cement production process....

  17. Leaching of tritium from a cement composite

    International Nuclear Information System (INIS)

    Matsuzuru, Hideo; Ito, Akihiko

    1978-10-01

    Leaching of tritium from cement composites into an aqueous phase has been studied to evaluate the safety of incorporation of the tritiated liquid waste into cement. Leaching tests were performed by the method recommended by the International Atomic Energy Agency. The Leaching fraction was measured as functions of waste-cement ratio (Wa/C), temperature of leachant and curing time. The tritium leachability of cement in the long term test follows the order: alumina cement portland cement slag cement. The fraction of tritium leached increases with increasing Wa/C and temperature and decreasing curing period. A deionized water as a leachant gives a slightly higher leachability than synthetic sea water. The amount leached of tritium from a 200 l drum size specimen was estimated on the basis of the above results. (author)

  18. Through BHA (Bottom Hole Assembly) cementing with proprietary cementing technology

    Energy Technology Data Exchange (ETDEWEB)

    Fanguy, Charles ' Joey' ; Mueller, Dan T. [BJ Services Company, Houston, TX (United States); Garrett, J.C. [Palm Energy Partners, LLC, Metairie, LA (United States)

    2004-07-01

    There are many problems that can arise when drilling into sub-normally pressured or naturally fractured zones. Lost circulation is one problem that is commonly encountered while drilling oil and gas wells. Lost circulation can lead to increased costs associated with drilling due to rig time, spreadsheet costs, and expensive mud system losses. Cement is one of the most effective treatment options, although it is not normally considered the first option because most operators are forced to trip out of the wellbore and utilize a squeeze packer. This is not always a viable option because of potential well control issues associated with the hydrostatic pressure reduction due to the losses of the whole mud. One treatment option that is commonly overlooked is pumping cement slurries through the bottom hole assembly and drill bit. This is generally not attempted for a variety of reasons. These reasons include: I Concern about 'squeezing off' of the cement in the bit II Lack of potential quality control associated with mixing 'on the fly' III Lack of the ability to test the actual mixed slurry samples The use of a pre-mixed, storable cement slurry has eliminated the concerns associated with pumping cement slurries through mud motors, MWD tools, BHA's, and drill bits. This advanced cement technology has been successfully utilized while reducing the risks associated with these lost circulation treatments. In addition, this technology has eliminated the costs associated with using a squeeze packer and the rig time required for several trips out of the wellbore. The paper will describe the premixed slurry properties and QA/QC procedures that are required for successful through the bit operations. This paper will also provide case histories of successful through the bit operation, as well as background information leading to the treatments. The case histories include successful through the bit remediation of severe lost circulation zones and as well the

  19. Analysis of cement-treated clay behavior by micromechanical approach

    OpenAIRE

    Zhang , Dong-Mei; Yin , Zhenyu; Hicher , Pierre Yves; Huang , Hong-Wei

    2013-01-01

    International audience; Experimental results show the significant influence of cement content on the mechanical properties of cement-treated clays. Cementation is produced by mixing a certain amount of cement with the saturated clay. The purpose of this paper is to model the cementation effect on the mechanical behavior of cement-treated clay. A micromechanical stress-strain model is developed considering explicitly the cementation at inter-cluster contacts. The inter-cluster bonding and debo...

  20. Fatigue Resistance of Filled NR with PMMA-Wrapped and Rare Earth-Doped Alumina-Siloxane Gel

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    Poly (methyl methacrylate) (PMMA) was used to wrap alumina-siloxane sol which was produced by water glass, aluminum nitrate and α-methacrylic acid, and as a result, alumina-siloxane gel wrapped by PMMA was obtained. Meanwhile, rare earth ions were employed to dope in the course of reaction, and the formed rare earth doped PMMA microcapsule powder was filled into natural rubber (NR). It is found through the analysis of mechanical properties that Young′s modulus universally improves and a remarkable resistance to fatigue is displayed. Retention rate of tensile strength is twice that of the controlled sample after ten thousand times of extension fatigue.

  1. Synthesis of Portland cement and calcium sulfoaluminate-belite cement for sustainable development and performance

    Science.gov (United States)

    Chen, Irvin Allen

    Portland cement concrete, the most widely used manufactured material in the world, is made primarily from water, mineral aggregates, and portland cement. The production of portland cement is energy intensive, accounting for 2% of primary energy consumption and 5% of industrial energy consumption globally. Moreover, portland cement manufacturing contributes significantly to greenhouse gases and accounts for 5% of the global CO2 emissions resulting from human activity. The primary objective of this research was to explore methods of reducing the environmental impact of cement production while maintaining or improving current performance standards. Two approaches were taken, (1) incorporation of waste materials in portland cement synthesis, and (2) optimization of an alternative environmental friendly binder, calcium sulfoaluminate-belite cement. These approaches can lead to less energy consumption, less emission of CO2, and more reuse of industrial waste materials for cement manufacturing. In the portland cement part of the research, portland cement clinkers conforming to the compositional specifications in ASTM C 150 for Type I cement were successfully synthesized from reagent-grade chemicals with 0% to 40% fly ash and 0% to 60% slag incorporation (with 10% intervals), 72.5% limestone with 27.5% fly ash, and 65% limestone with 35% slag. The synthesized portland cements had similar early-age hydration behavior to commercial portland cement. However, waste materials significantly affected cement phase formation. The C3S--C2S ratio decreased with increasing amounts of waste materials incorporated. These differences could have implications on proportioning of raw materials for cement production when using waste materials. In the calcium sulfoaluminate-belite cement part of the research, three calcium sulfoaluminate-belite cement clinkers with a range of phase compositions were successfully synthesized from reagent-grade chemicals. The synthesized calcium sulfoaluminate

  2. The cement recycling of the earthquake disaster debris by Hachinohe Cement Co., Ltd

    International Nuclear Information System (INIS)

    Kataoka, Masayuki

    2015-01-01

    A tremendous quantity of earthquake disaster debris and tsunami sediment was resulted by the Great East Japan Earthquake on March 11, 2011. Hachinohe Cement Co., Ltd., a Sumitomo Osaka Cement subsidiary, was the first cement industry company to receive and process such waste materials outside of their usual prefecture area, while the company is performing their treatment and recycling services locally in Hachinohe City and Aomori Prefecture. This report provides an explanation about the recycling mechanism of waste materials and by-products in cement manufacturing process, and introduces an example of actual achievements for the disaster debris treatment by utilizing the cement recycling technologies at the Hachinohe Cement Plant. (author)

  3. Evaluation of flexural strength and surface properties of prepolymerized CAD/CAM PMMA-based polymers used for digital 3D complete dentures.

    Science.gov (United States)

    Arslan, Mustafa; Murat, Sema; Alp, Gulce; Zaimoglu, Ali

    2018-01-01

    The objectives of this in vitro study were to evaluate the flexural strength (FS), surface roughness (Ra), and hydrophobicity of polymethylmethacrylate (PMMA)-based computer-aided design/computer-aided manufacturing (CAD/CAM) polymers and to compare the properties of different CAD/CAM PMMA-based polymers with conventional heat-polymerized PMMA following thermal cycling. Twenty rectangular-shaped specimens (64 × 10 × 3.3 mm) were fabricated from three CAD/CAM PMMA-based polymers (M-PM Disc [M], AvaDent Puck Disc [A], and Pink CAD/CAM Disc Polident [P], and one conventional heat-polymerized PMMA (Promolux [C]), according to ISO 20795-1:2013 standards. The specimens were divided into two subgroups (n = 10), a control and a thermocycled group. The specimens in the thermocycled group were subjected to 5000 thermal cycling procedures (5 to 55°C; 30 s dwell times). The Ra value was measured using a profilometer. Contact angle (CA) was assessed using the sessile drop method to evaluate surface hydrophobicity. In addition, the FS of the specimens was tested in a universal testing machine at a crosshead speed of 1.0 mm/min. Surface texture of the materials was assessed using scanning electron microscope (SEM). The data were analyzed using two-way analysis of variance (ANOVA), followed by Tukey's HSD post-hoc test (α CAD/CAM PMMA-based polymers showed significantly higher FS than conventional heat-polymerized PMMA for each group (P CAD/CAM PMMA-based polymer [P] showed the highest FS, whereas conventional PMMA [C] showed the lowest FS before and after thermal cycling (P 0.05). In the thermocycled group, the lowest Ra value was observed for CAD/CAM PMMA-based polymer [M] (P CAD/CAM PMMA-based polymers [A] and [P], and conventional PMMA [C] had similar Ra values (P > 0.05). Conventional PMMA [C] had a significantly lower CA and consequently lower hydrophobicity compared to the CAD/CAM polymers in the control group (P CAD/CAM PMMA-based polymer [A] and conventional PMMA [C

  4. Use sulfoferritic cements in construction

    Science.gov (United States)

    Samchenko, Svetlana V.; Zorin, Dmitriy A.

    2018-03-01

    Currently, high-rise construction has received increasing attention around the world. In the big cities under construction is less space and one solution is the high-rise construction. However, high-rise buildings use special requirements, such as strength, thermal insulation, wind load and others. When concrete is exposed to continuous loads by wind or to mechanical loads, it undergoes abrasion. Resistance to this process depends on the characteristics of materials that the concrete and finishing seams are made of. Research on increasing impact and abrasion resistance of calcium sulfoferrite-based cement stone from the perspective of formation of cement stone structure will be instrumental in developing durable materials for application in high-rise construction.

  5. Concrete research using blended cements

    International Nuclear Information System (INIS)

    Butler, W.B.

    2001-01-01

    Concrete research increasingly involves the use of mixes containing one or more of the supplementary cementitious materials (SCMs), often in conjunction with chemical admixtures. The influence of materials is commonly evaluated on the basis of water/ cement or water/ binder ratio and SCM content as a percentage of total binder, with dosage level of chemical admixture varied to maintain workability. As a result, more than one variable is introduced at a time and the objectives of the research may not be achieved. The significance of water/ cement ratio and addition rates of admixtures are examined from a practical standpoint with suggestions for more appropriate means of evaluation of the influence of individual materials. Copyright (2001) The Australian Ceramic Society

  6. The density of cement phases

    International Nuclear Information System (INIS)

    Balonis, M.; Glasser, F.P.

    2009-01-01

    The densities of principal crystalline phases occurring in Portland cement are critically assessed and tabulated, in some cases with addition of new data. A reliable and self-consistent density set for crystalline phases was obtained by calculating densities from crystallographic data and unit cell contents. Independent laboratory work was undertaken to synthesize major AFm and AFt cement phases, determine their unit cell parameters and compare the results with those recorded in the literature. Parameters were refined from powder diffraction patterns using CELREF 2 software. A density value is presented for each phase, showing literature sources, in some cases describing limitations on the data, and the weighting attached to numerical values where an averaging process was used for accepted data. A brief discussion is made of the consequences of the packing of water to density changes in AFm and AFt structures.

  7. Self-Assembled Structures of PMAA-PMMA Block Copolymers : Synthesis, Characterization, and Self-Consistent Field Computations

    NARCIS (Netherlands)

    Li, Feng; Schellekens, Mike; de Bont, Jens; Peters, Ron; Overbeek, Ad; Leermakers, Frans A. M.; Tuinier, Remco

    2015-01-01

    Block copolymers composed of methacrylic acid (MAA) and methyl methacrylate (MMA) blocks are interesting candidates for replacing surfactants in emulsion polymerization methods. Here the synthesis and experimental characterization of well-defined PMAA-PMMA block copolymers made via RAFT

  8. Dosimetric characteristics of methyl polymethacrylate (PMMA) commercially named as Clarex, for doses between 10 krad and 10 Mrad

    International Nuclear Information System (INIS)

    Castro Rubio Poli, D. de.

    1978-01-01

    The possibility to use the PMMA - commercially named as Clarex - for dosimetric control of industrial radiation process, taking advantage of the charges induced by ionizing radiation on the PMMA optical properties, was studied. Although theoretically other radiation effects could be eventually correlated with the dose absorbed in the PMMA (i.e., charge of mechanical or electrical properties) the dosimetric techniques based on the ultraviolet absorption spectrum modifications, near of visible region, have the advantage of their simplicity, swiftness and precision. A study on both the factors affecting the measurement reproducibility (temperature, humidity etc.) and some posterior effects that occur in the irradiated PMMA, has been acomplished. Other possible errors sources (sample thickness variation, spectrophotometer inaccuracy etc.) are also investigated. It has been concluded that the Clarex can be used as a good precision dosimeter within the interval of approximately 10 krad to 10 Mrad by measuring the optical density changes around 315 nm, provided some care is taken during handling. (Author) [pt

  9. Self-assembled structures of PMAA-PMMA block copolymers: Synthesis, characterization, and self-consistent field computations

    NARCIS (Netherlands)

    Li, F.; Schellekens, J.; Bont, de J.A.M.; Peters, R.; Overbeek, A.; Leermakers, F.A.M.; Tuinier, R.

    2015-01-01

    Block copolymers composed of methacrylic acid (MAA) and methyl methacrylate (MMA) blocks are interesting candidates for replacing surfactants in emulsion polymerization methods. Here the synthesis and experimental characterization of well-defined PMAA–PMMA block copolymers made via RAFT

  10. Glass ionomer cement: literature review

    OpenAIRE

    Sérgio Spezzia

    2017-01-01

    Introduction: In the dental area preventive actions occur in an attempt to avoid the installation of caries, a disease that has an increased prevalence in the population and which is a Public Health problem. Some resources are used for such, such as: performing early diagnosis and the option for conservative treatments of minimal intervention. The glass ionomer cement (CIV), coming from its beneficial characteristics that meet current trends, is closely related to the precepts of Preventive a...

  11. WHITE CEMENT IN SUSTAINABLE DEVELOPMENT

    OpenAIRE

    Y.C.P RAMANA BABU; B.SAI DOONDI; N. M .V .VAMSI KRISHNA; K.PRASANTHI

    2013-01-01

    India is one among the fast developing countries in the world in the areas of Infrastructure. Now a day, Carbon monoxide (CO) and carbon dioxide (CO2) are the temporary atmospheric pollutants in the environment chiefly emitted from the fuel burning vehicles and street lights which lead to global warming and pose a major threat tothe survival and sustainable development. This paper deals with the principal purpose of use of white cement in pavement design which will take care of the Green hous...

  12. Structural, thermal, optical properties and cytotoxicity of PMMA/ZnO fibers and films: Potential application in tissue engineering

    International Nuclear Information System (INIS)

    Balen, Rodrigo; Vidotto da Costa, Wilian; Lara Andrade, Jéssica de; Piai, Juliana Francis; Muniz, Edvani Curti; Companhoni, Mychelle Vianna; Nakamura, Tânia Ueda

    2016-01-01

    Highlights: • Films and fibers of PMMA/ZnO nanocomposite were prepared. • ZnO NPs incorporated into PMMA fibers reduces their diameter and beads presence. • PMMA films containing ZnO exhibit higher thermal stability than pure polymer. • PMMA/ZnO nanocomposites show improved optical properties compared to pure polymer. • PMMA/ZnO shows potential for applications in tissue engineering. - Abstract: Films and fibers of PMMA/ZnO nanocomposites (100/0, 99/01, 97/03, 95/05, 90/10, and 85/15 wt.%) were produced by casting and electrospinning, respectively. Their structural, thermal, and optical properties were investigated by XRD, SEM, TGA, PAS, and PL. The incorporation of ZnO NPs reduced the diameter of PMMA fibers and the presence of beads. The surfaces of the fibers exhibited greater hydrophobicity, compared to the films, with contact angles of around 120° and 94°, respectively. PMMA films containing ZnO exhibited higher thermal stability than the pure polymer, while the corresponding fibers did not show any changes in thermal stability. The dispersion of the ZnO NPs at the surface and in the bulk of the nanocomposites appeared to be relatively homogeneous. ZnO improved the optical properties of the PMMA, with an intense absorption band near 370 nm observed for all the nanocomposites, which also exhibited luminescence with emission in the near-UV region, both attributed to ZnO. Biological tests demonstrated that fibers and films with up to 1% of ZnO exhibited good performance in the proliferation of fibroblast cells, indicating their potential for applications in tissue engineering. The fibers provided higher cell viability than the films, presumably due to their greater surface area and/or more suitable surface morphology. Nanocomposites with 15% ZnO inhibited cell proliferation, due to the cytotoxicity of the ZnO NPs. Although several applications of PMMA have been suggested by biomedical researchers, until now there have been no reports on the specific

  13. Structural, thermal, optical properties and cytotoxicity of PMMA/ZnO fibers and films: Potential application in tissue engineering

    Energy Technology Data Exchange (ETDEWEB)

    Balen, Rodrigo; Vidotto da Costa, Wilian; Lara Andrade, Jéssica de; Piai, Juliana Francis [Programa de Pós-Graduação em Química, Departamento de Química, Universidade Estadual de Maringá, Av. Colombo 5790, 87020-900, Zona Sete, Maringá, PR (Brazil); Muniz, Edvani Curti [Programa de Pós-Graduação em Química, Departamento de Química, Universidade Estadual de Maringá, Av. Colombo 5790, 87020-900, Zona Sete, Maringá, PR (Brazil); Programa de Pós-Graduação em Biotecnologia Aplicada à Agricultura, Universidade Paranaense (UNIPAR), 87502-210, Umuarama, PR (Brazil); Programa de Pós- Graduação em Ciências de Materiais & Engenharia, Universidade Tecnológica Federal do Paraná (UTFPR-LD), 86036-370, Londrina, PR (Brazil); Companhoni, Mychelle Vianna; Nakamura, Tânia Ueda [Departamento de Ciências Básicas da Saúde, Universidade Estadual de Maringá, Av. Colombo 5790, 87020-900, Zona Sete, Maringá, PR (Brazil); and others

    2016-11-01

    Highlights: • Films and fibers of PMMA/ZnO nanocomposite were prepared. • ZnO NPs incorporated into PMMA fibers reduces their diameter and beads presence. • PMMA films containing ZnO exhibit higher thermal stability than pure polymer. • PMMA/ZnO nanocomposites show improved optical properties compared to pure polymer. • PMMA/ZnO shows potential for applications in tissue engineering. - Abstract: Films and fibers of PMMA/ZnO nanocomposites (100/0, 99/01, 97/03, 95/05, 90/10, and 85/15 wt.%) were produced by casting and electrospinning, respectively. Their structural, thermal, and optical properties were investigated by XRD, SEM, TGA, PAS, and PL. The incorporation of ZnO NPs reduced the diameter of PMMA fibers and the presence of beads. The surfaces of the fibers exhibited greater hydrophobicity, compared to the films, with contact angles of around 120° and 94°, respectively. PMMA films containing ZnO exhibited higher thermal stability than the pure polymer, while the corresponding fibers did not show any changes in thermal stability. The dispersion of the ZnO NPs at the surface and in the bulk of the nanocomposites appeared to be relatively homogeneous. ZnO improved the optical properties of the PMMA, with an intense absorption band near 370 nm observed for all the nanocomposites, which also exhibited luminescence with emission in the near-UV region, both attributed to ZnO. Biological tests demonstrated that fibers and films with up to 1% of ZnO exhibited good performance in the proliferation of fibroblast cells, indicating their potential for applications in tissue engineering. The fibers provided higher cell viability than the films, presumably due to their greater surface area and/or more suitable surface morphology. Nanocomposites with 15% ZnO inhibited cell proliferation, due to the cytotoxicity of the ZnO NPs. Although several applications of PMMA have been suggested by biomedical researchers, until now there have been no reports on the specific

  14. Enhanced Red Emission in Ultrasound-Assisted Sol-Gel Derived ZnO/PMMA Nanocomposite

    Directory of Open Access Journals (Sweden)

    Van-Tuan Mai

    2018-01-01

    Full Text Available Cost-effective methods for preparing ZnO nanostructures are of importance for the deployment of ZnO in many applications including n-type conduits, catalysts, nanophosphor, and optoelectronics. Herein, we present a room-temperature sol-gel method with the aid of ultrasonication to prepare white-emitting ZnO nanoparticles (NPs. X-ray diffraction and electron microscopic analyses revealed that the size and shape of ZnO NPs can be controlled simply by changing the concentration of the Zn precursor. The ZnO NPs had a broad photoluminescence emission, ranging from 450 nm to 800 nm, while their composite in PMMA matrix showed an enhancement in the red region induced by ZnO-PMMA interfacial band-bending effects. The results demonstrated herein promise a simple tool for control over size, shape, and emission of ZnO materials for diverse applications.

  15. A comparative study on CdS: PEO and CdS: PMMA nanocomposite solid films

    International Nuclear Information System (INIS)

    Padmaja, S.; Jayakumar, S.; Balaji, R.; Vaideki, K.

    2016-01-01

    Cadmium Sulphide (CdS) nanoparticles were reinforced in Poly(ethylene Oxide) (PEO) and Poly(methyl methacrylate) (PMMA) matrices by in situ technique. The presence of CdS in PEO and PMMA matrix was confirmed using X-ray photoelectron spectroscopy (XPS). Fourier Transform Infrared spectroscopy (FTIR) analysis disclosed the co-ordination of CdS in the matrices. Thermal analysis of the nanocomposites was carried out using Differential Scanning calorimetric studies (DSC). The optical studies using UV–vis spectroscopy were carried out to find the band gap of the materials and the absorption onset. The CdS particle size in the matrices was found by Effective Mass Approximation (EMA) model using the band gap values and was confirmed by TEM studies. The surface trapped emissions of the nanocomposites were observed from the photoluminescence (PL) spectra. The distribution of CdS particles in the polymer matrices were presented by Atomic force microscopic studies (AFM).

  16. Synthesis and biological evaluation of PMMA/MMT nanocomposite as denture base material.

    Science.gov (United States)

    Zheng, Junping; Su, Qiang; Wang, Chen; Cheng, Gang; Zhu, Ran; Shi, Jin; Yao, Kangde

    2011-04-01

    Inorganic-polymer nanocomposites are of significant interest for emerging materials due to their improved properties and unique combination of properties. Poly (methylmethacrylate) (PMMA)/montmorillonite (MMT) nanocomposites were prepared by in situ suspension polymerization with dodecylamine used as MMT-modifier. X-ray diffraction (XRD) and transmission electron microscopy (TEM) were used to characterize the structures of the nanocomposites. Cytotoxicity test, hemolysis test, acute systemic toxicity test, oral mucous membrane irritation test, guinea-pig maximization test and mouse bone-marrow micronucleus test were used to evaluate the biocompatibility of PMMA/MMT nanocomposites. The results indicated that an exfoliated nanocomposite was achieved, and the resulting nanocomposites exhibited excellent biocompatibility as denture base material and had potential application in dental materials.

  17. A comparative study on CdS: PEO and CdS: PMMA nanocomposite solid films

    Energy Technology Data Exchange (ETDEWEB)

    Padmaja, S. [Thin film centre, PSG College of Technology, Coimbatore (India); Jayakumar, S., E-mail: s_jayakumar_99@yahoo.com [Department of Physics, PSG Institute of Technology and Applied Research, Coimbatore (India); Balaji, R.; Vaideki, K. [Thin film centre, PSG College of Technology, Coimbatore (India)

    2016-08-15

    Cadmium Sulphide (CdS) nanoparticles were reinforced in Poly(ethylene Oxide) (PEO) and Poly(methyl methacrylate) (PMMA) matrices by in situ technique. The presence of CdS in PEO and PMMA matrix was confirmed using X-ray photoelectron spectroscopy (XPS). Fourier Transform Infrared spectroscopy (FTIR) analysis disclosed the co-ordination of CdS in the matrices. Thermal analysis of the nanocomposites was carried out using Differential Scanning calorimetric studies (DSC). The optical studies using UV–vis spectroscopy were carried out to find the band gap of the materials and the absorption onset. The CdS particle size in the matrices was found by Effective Mass Approximation (EMA) model using the band gap values and was confirmed by TEM studies. The surface trapped emissions of the nanocomposites were observed from the photoluminescence (PL) spectra. The distribution of CdS particles in the polymer matrices were presented by Atomic force microscopic studies (AFM).

  18. Characterization and human gingival fibroblasts biocompatibility of hydroxyapatite/PMMA nanocomposites for provisional dental implant restoration

    Science.gov (United States)

    Zhang, Jingchao; Liao, Juan; Mo, Anchun; Li, Yubao; Li, Jidong; Wang, Xuejiang

    2008-11-01

    The aim of this study was to determine nHA/PMMA composites (H/P) in an optimal ratio with improved cytocompatibility as well as valid physical properties for provisional dental implant restoration. 20 wt.%, 30 wt.%, 40 wt.% and 50 wt.% H/P were developed and characterized using XPS, bending strength test and SEM. Human gingival fibroblasts cultured in extracts or directly on sample discs were investigated by fluorescent staining and MTT assay. Chemical integration in nHA/PMMA interface was indicated by XPS. Typical fusiform cells with adhesion spots were detected on H/P discs. MTT results also indicated higher cell viability in 30 wt.% and 40 wt.% H/P discs ( P provisional fixed crowns (PFC) is 0.4:1.

  19. Temperature-dependent self-assembly and rheological behavior of a thermoreversible pmma-P n BA-PMMA triblock copolymer gel

    Energy Technology Data Exchange (ETDEWEB)

    Zabet, Mahla; Mishra, Satish; Boy, Ramiz; Walters, Keisha B.; Naskar, Amit K.; Kundu, Santanu (UO); (ORNL); (MSSU)

    2017-03-25

    Self-assembly and mechanical properties of triblock copolymers in a mid-block selective solvent are of interest in many applications. Herein, we report physical assembly of an ABA triblock copolymer, [PMMA–PnBA–PMMA] in two different mid-block selective solvents, n-butanol and 2-ethyl-1-hexanol. Gel formation resulting from end-block associations and the corresponding changes in mechanical properties have been investigated over a temperature range of -80 °C to 60 °C, from near the solvent melting points to above the gelation temperature. Shear-rheometry, thermal analysis, and small-angle neutron scattering data reveal formation and transition of structure in these systems from a liquid state to a gel state to a percolated cluster network with decrease in temperature. The aggregated PMMA end-blocks display a glass transition temperature. Our results provide new understanding into the structural changes of a self-assembled triblock copolymer gel over a large length scale and wide temperature range.

  20. Relationship between the mechanical properties of epoxy/PMMA-b-PnBA-b-PMMA block copolymer blends and their three-dimensional nanostructures

    Directory of Open Access Journals (Sweden)

    H. Kishi

    2017-10-01

    Full Text Available Nanostructures of diglycidyl ether of bisphenol-A epoxy/poly(methyl methacrylate-b-poly(n-butyl acrylate-b-poly(methyl methacrylate (PMMA-b-PnBA-b-PMMA triblock copolymer (BCP blends were studied in relation to their mechanical properties. Three types of self-assembled nanostructures, such as spheres, random cylinders, and curved lamella, were controlled in phenol novolac-cured epoxy blends with a wide range of BCP content. Three types of nanostructures were observed using two-dimensional and three-dimensional transmission electron microscopy (TEM. The 3D-TEM, dynamic viscoelastic analyses, and theoretical model on the elastic modulus clarified that the spheres and the random cylinders, consisted of epoxy-immiscible PnBA phases, were discontinuously dispersed in the epoxy matrix. In contrast, the curved lamella formed co-continuous nanostructure, in which both the PnBA and epoxy phases formed continuous channels. The fracture toughness (critical strain energy release rate, GIC and the flexural moduli of elasticity (E of the cured blends were evaluated for various amounts of BCP content. The highest GIC was obtained from the random cylindrical nanostructured blends in the three types of nanostructures with the same PnBA content. The lowest E was obtained for the curved lamella with co-continuous nanostructures. The details of deformation and fracture events were observed using optical and electron microscopy, and the mechanical properties are discussed in relation to the nanostructures.

  1. Modernization of Byuzmeyinsky Cement Plant

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    2001-03-01

    With an objective of saving energy and reducing greenhouse gas emission, investigations and discussions were given on a modernization project for Byuzmeyinsky Cement Factory, the only cement factory in Turkmenistan. Byuzmeyinsky Cement Factory uses the wet process which consumes a large amount of energy, is inferior in production efficiency and quality, and discharging a great amount of greenhouse effect gas. The present project will execute change of the raw material crusher into a vertical roll mill for one of the four wet kilns, and change of the facilities for raw material powder mixing and storing and clinker manufacturing into dry-type facilities using the NSP system. As a result of the discussions, the energy saving effect would be 86,321 tons of crude oil equivalent annually, and the greenhouse gas emission reducing effect would be 224,467 t-CO2 annually. The total fund amount required for the project is estimated to be 90,211,000 dollars. With regard to the profitability, the internal financial profit rate would be 9.71% after tax, and the ROE would be 18.62%, whereas the project is considered feasible. (NEDO)

  2. A Twofold Comparison between Dual Cure Resin Modified Cement and Glass Ionomer Cement for Orthodontic Band Cementation.

    Science.gov (United States)

    Attar, Hanaa El; Elhiny, Omnia; Salem, Ghada; Abdelrahman, Ahmed; Attia, Mazen

    2016-12-15

    To test the solubility of dual cure resin modified resin cement in a food simulating solution and the shear bond strength compared to conventional Glass ionomer cement. The materials tested were self-adhesive dual cure resin modified cement and Glass Ionomer (GIC). Twenty Teflon moulds were divided into two groups of tens. The first group was injected and packed with the modified resin cement, the second group was packed with GIC. To test the solubility, each mould was weighed before and after being placed in an analytical reagent for 30 days. The solubility was measured as the difference between the initial and final drying mass. To measure the Shear bond strength, 20 freshly extracted wisdom teeth were equally divided into two groups and embedded in self-cure acrylic resin. Four mm sections of stainless steel bands were cemented to the exposed buccal surfaces of teeth under a constant load of 500 g. Shear bond strength was measured using a computer controlled materials testing machine and the load required to deband the samples was recorded in Newtons. GIC showed significantly higher mean weight loss and an insignificant lower Shear bond strength, compared to dual cure resin Cement. It was found that dual cure resin modified cement was less soluble than glass ionomer cement and of comparable bond strength rendering it more useful clinically for orthodontic band cementation.

  3. Nd:YAG-laser-based time-domain reflectometry measurements of the intrinsic reflection signature from PMMA fiber splices

    Science.gov (United States)

    Lawson, Christopher M.; Michael, Robert R., Jr.; Dressel, Earl M.; Harmony, David W.

    1991-12-01

    Optical time domain reflectometry (OTDR) measurements have been performed on polished polymethylmethacrylate (PMMA) plastic fiber splices. After the dominant splice reflection sources due to surface roughness, inexact index matching, and fiber core misalignment were eliminated, an intrinsic OTDR signature 3 - 8 dB above the Rayleigh backscatter floor remained with all tested fibers. This minimum splice reflectivity exhibits characteristics that are consistent with sub-surface polymer damage and can be used for detection of PMMA fiber splices.

  4. Use of Incineration Solid Waste Bottom Ash as Cement Mixture in Cement Production

    Science.gov (United States)

    Jun, N. H.; Abdullah, M. M. A. B.; Jin, T. S.; Kadir, A. A.; Tugui, C. A.; Sandu, A. V.

    2017-06-01

    Incineration solid waste bottom ash was use to examine the suitability as a substitution in cement production. This study enveloped an innovative technology option for designing new equivalent cement that contains incineration solid waste bottom ash. The compressive strength of the samples was determined at 7, 14, 28 and 90 days. The result was compared to control cement with cement mixture containing incineration waste bottom ash where the result proved that bottom ash cement mixture able achieve its equivalent performance compared to control cement which meeting the requirement of the standards according to EN 196-1. The pozzolanic activity index of bottom ash cement mixture reached 0.92 at 28 days and 0.95 at 90 and this values can be concluded as a pozzolanic material with positive pozzolanic activity. Calcium hydroxide in Portland cement decreasing with the increasing replacement of bottom ash where the reaction occur between Ca(OH)2 and active SiO2.

  5. Natural cement as the precursor of Portland cement: Methodology for its identification

    International Nuclear Information System (INIS)

    Varas, M.J.; Alvarez de Buergo, M.; Fort, R.

    2005-01-01

    When cements appeared in the 19th century, they took the place of traditional binding materials (lime, gypsum, and hydraulic lime) which had been used until that time. Early cements can be divided into two groups, natural and artificial (Portland) cements. Natural cements were introduced first, but their widespread usage was short-lived as they were quickly replaced by artificial cements (Portland), still the most important and predominant today. The main differences between natural and artificial cements arise during the manufacturing process. The final properties of the cements are greatly influenced by differences in the raw materials and burning temperatures employed. The aim of this paper is to assess the efficiency of traditional analytical techniques (petrographic microscopy, X-ray diffraction (XRD), scanning electron microscopy (SEM), and Fourier transform infrared spectroscopy (FTIR)) used to differentiate natural and artificial cements

  6. Effects of cement particle size distribution on performance properties of Portland cement-based materials

    Energy Technology Data Exchange (ETDEWEB)

    Bentz, D.P.; Garboczi, E.J.; Haecker, C.J.; Jensen, O.M.

    1999-10-01

    The original size, spatial distribution, and composition of Portland cement particles have a large influence on hydration kinetics, microstructure development, and ultimate properties of cement-based materials. In this paper, the effects of cement particle size distribution on a variety of performance properties are explored via computer simulation and a few experimental studies. Properties examined include setting time, heat release, capillary porosity percolation, diffusivity, chemical shrinkage, autogenous shrinkage, internal relative humidity evolution, and interfacial transition zone microstructure. The effects of flocculation and dispersion of the cement particles in the starting microstructures on resultant properties are also briefly evaluated. The computer simulations are conducted using two cement particle size distributions that bound those commonly in use today and three different water-to-cement ratios: 0.5, 0.3, and 0.246. For lower water-to-cement ratio systems, the use of coarser cements may offer equivalent or superior performance, as well as reducing production costs for the manufacturer.

  7. Different photoluminescent properties of binary and ternary europium chelates doped in PMMA

    International Nuclear Information System (INIS)

    Liu Hongguo; Park, Seongtae; Jang, Kiwan; Zhang Wansong; Seo, Hyo-Jin; Lee, Yong-Ill

    2003-01-01

    Two kinds of europium-β-diketone chelates, binary Eu(DBM) 3 and ternary Eu(DBM) 3 phen were doped in poly(methyl methacrylate) (PMMA). These chelates show very different photoluminescent (PL) behaviors: the hypersensitive 5 D 0 → 7 F 2 emission bands of Eu(DBM) 3 phen change slightly with the molar ratios, while those of Eu(DBM) 3 change obviously and regularly with the molar ratios. The results of the luminescent lifetimes of 5 D 0 levels show that the binary chelate exists as two kinds of species in the doped systems, and the lifetimes and contents of each species change with the molar ratios, while the ternary chelate exists as one kind of species in the doped systems. X-ray diffraction (XRD) patterns of the binary chelate doped systems give some diffraction peaks that are different from those of pure chelate and change with the molar ratios, indicating new kinds of crystal structures formed, and consequently, the first coordination sphere of Eu 3+ ion changes; while those of the ternary chelate doped systems just show amorphous diffraction halos of the host, indicating that the ternary chelate exist in an amorphous state and disperse well in the host. The FTIR spectra of PMMA also change gradually with increasing the molar ratios of the doped two kinds of chelates, and the XRD patterns show that the amorphous halos of PMMA in the doped systems are different from those of pure PMMA and change with the molar ratios, too, suggesting the interaction between the guest and the host

  8. Effects of modified Clay on the morphology and thermal stability of PMMA/clay nanocomposites

    International Nuclear Information System (INIS)

    Tsai, Tsung-Yen; Lin, Mei-Ju; Chuang, Yi-Chen; Chou, Po-Chiang

    2013-01-01

    The potential to improve the mechanical, thermal, and optical properties of poly(methyl methacrylate) (PMMA)/clay nanocomposites prepared with clay containing an organic modifier was investigated. Pristine sodium montmorillonite clay was modified using cocoamphodipropionate, which absorbs UVB in the 280–320 nm range, via ion exchange to enhance the compatibility between the clay platelets and the methyl methacrylate polymer matrix. PMMA/clay nanocomposites were synthesized via in situ free-radical polymerization. Three types of clay with various cation-exchange capacities (CEC) were used as inorganic layered materials in these organic–inorganic hybrid nanocomposites: CL42, CL120, and CL88 with CEC values of 116, 168, and 200 meq/100 g of clay, respectively. We characterized the effects of the organoclay dispersion on UV resistance, effectiveness as an O 2 gas barrier, thermal stability, and mechanical properties of PMMA/clay nanocomposites. Gas permeability analysis demonstrated the excellent gas barrier properties of the nanocomposites, consistent with the intercalated or exfoliated morphologies observed. The optical properties were assessed using UV–Visible spectroscopy, which revealed that these materials have good optical clarity, UV resistance, and scratch resistance. The effect of the dispersion capability of organoclay on the thermal properties of PMMA/clay nanocomposites was investigated by thermogravimetric analysis and differential scanning calorimetry; these analyses revealed excellent thermal stability of some of the modified clay nanocomposites. - Highlights: ► We control the dispersion morphology by protonation of K2 into the clay. ► The CL120 and CL88, with the higher CEC, are more random intercalated by K2. ► We report these materials have good optical clarity, and UV resistance

  9. Preparation and characterization of ZnO-PMMA resin nanocomposites for denture bases.

    Science.gov (United States)

    Cierech, Mariusz; Wojnarowicz, Jacek; Szmigiel, Dariusz; Bączkowski, Bohdan; Grudniak, Anna Maria; Wolska, Krystyna Izabela; Łojkowski, Witold; Mierzwińska-Nastalska, Elżbieta

    2016-01-01

    The aim of the paper was to investigate the antifungal activity of zinc oxide nanoparticles (ZnONPs) against Candida albicans. Some attempts have been made to find out the best way to introduce ZnONPs into polymethyl methacrylate (PMMA) resin material and to determine some parameters of a newly formed composite. Zinc oxide nanoparticles were manufactured and their basic physical parameters were determined (average particle size, density, specific surface area). Minimal inhibitory concentration (MIC) of ZnONPs was determined for the Candida albicans standard strain. The average size of ZnO conglomerates in the monomer solution of PMMA resin was measured using a dynamic light scattering instrument. PMMA resin samples with incorporated ZnONPs were produced. The morphology of nanopowder and the newly formed composite was examined under a scanning electron microscope (SEM). In addition, the roughness parameter of PMMA resin material was investigated before and after ZnONPs modification. Nanopowder with the average particle size of 30 nm, density of 5.24 g/cm3 and surface area of 39 m2/g was obtained. MIC was determined at the level of 0.75 mg/mL. The average size of ZnO conglomerates in the monomer solution of acrylic resin dropped by 11 times after ultrasound activation. SEM examination of a newly formed composite showed a successful introduction of ZnONPs confirmed by the energy dispersive X-ray spectroscopy (EDS) analysis. There were no statistically significant differences in the biomaterial roughness before and after the modification of ZnONPs. Zinc oxide nanoparticles were successfully incorporated into acrylic resin used for the production of denture bases. The presence of nanoparticles with sizes below 100 nm was confirmed. Nevertheless a newly created composite needs to be further investigated to improve its homogeneity, and to check its microbiological properties, strength and biocompatibility prior to its possible clinical use.

  10. Studies of PMMA sintering foils with and without coating by magnetron sputtering Pd

    Czech Academy of Sciences Publication Activity Database

    Cutroneo, Mariapompea; Macková, Anna; Torrisi, L.; Vad, K.; Csik, A.; Ando, L.; Švecová, B.

    2017-01-01

    Roč. 406, SEP (2017), s. 42-47 ISSN 0168-583X R&D Projects: GA MŠk LM2015056; GA ČR(CZ) GBP108/12/G108 Institutional support: RVO:61389005 Keywords : opaque PMMA * beads * RBS Subject RIV: BG - Nuclear, Atomic and Molecular Physics, Colliders OBOR OECD: Nuclear physics Impact factor: 1.109, year: 2016

  11. Synthesis of PMMA-co-PMAA copolymer brush on multi-wall carbon nanotubes

    Czech Academy of Sciences Publication Activity Database

    Slobodian, P.; Svoboda, P.; Říha, Pavel; Bořuta, R.; Sáha, P.

    2012-01-01

    Roč. 2, č. 3 (2012), s. 221-226 ISSN 2161-4881 Grant - others:OP VaVpI(XE) CZ.1.05/2.1.00/03.0111; UTB Zlín(CZ) IGA/FT/2012/ 022 Institutional research plan: CEZ:AV0Z20600510 Keywords : carbon nanotubes * functionalization * PMMA * PMAA * polymer brush Subject RIV: JI - Composite Materials

  12. Efficient refolding and immobilization of PMMA-tag-fused single-chain Fv antibodies for sensitive immunological detection on a PMMA plate.

    Science.gov (United States)

    Kumada, Yoichi; Ishikawa, Yasuyuki; Fujiwara, Yusuke; Takeda, Rui; Miyamoto, Ryosuke; Niwa, Daisuke; Momose, Shun; Kang, Bongmun; Kishimoto, Michimasa

    2014-09-01

    In this study, we investigated the efficient refolding and site-specific immobilization of single-chain variable fragments (scFvs) genetically fused with a poly(methylmethacrylate)-binding peptide (PMMA-tag). According to the results of an aggregation test of a scFv-PM in the presence of 0.5 M urea, aggregation was hardly detectable at a weak-alkaline pH (8.5) with lower concentrations of NaCl. Consequently, more than 93% recovery of the anti-RNase scFv-PM model was attained, when it was refolded by dialysis against 50 mM TAPS (pH8.5). These results suggested that the apparent isoelectric point (pI) of a target scFv was decreased to a great extent by the genetic fusion of a PMMA-tag containing 5 acidic amino acids, and, thus, the solubility of the scFv-PM in its semi-denatured form was considerably improved. We also designed alternative peptide-tags composed of plural aspartic acid residues (D5, D10 and D15-tags) to decrease the apparent pI value of the fusion protein. As a consequence, scFv-D5, scFv-D10 and scFv-D15 were also efficiently refolded with yields of more than 95%. It is noteworthy that even scFv-PS-D15, which had both a positively charged polystyrene-binding peptide (PS-tag) and a negatively charged D15-tag, was serially connected at the C-terminal region of scFvs, and also refolded with a yield of 96.1%. These results clearly indicate that controlling the apparent pI value of scFvs by the fusion of oligo-peptides composed of acidic amino acids at the C-terminus resulted in a high degree of recovery via dialysis refolding. According to the results of a sandwich ELISA using scFv-PMs, scFv-D15 and scFv-PS-D15 as ligands, high antigen-binding signals were detected from both the PMMA and phi-PS plates immobilized with scFv-PMs. Furthermore, the high antigen-binding activity of scFv-PMs was maintained in an adsorption state when it was immobilized on the surface of not only PMMA, but also hydrophilic PS (phi-PS) and polycarbonate (PC). These results

  13. Cement replacement materials. Properties, durability, sustainability

    International Nuclear Information System (INIS)

    Ramezanianpour, Ali Akbar

    2014-01-01

    The aim of this book is to present the latest findings in the properties and application of Supplementary Cementing Materials and blended cements currently used in the world in concrete. Sustainability is an important issue all over the world. Carbon dioxide emission has been a serious problem in the world due to the greenhouse effect. Today many countries agreed to reduce the emission of CO2. Many phases of cement and concrete technology can affect sustainability. Cement and concrete industry is responsible for the production of 7% carbon dioxide of the total world CO2 emission. The use of supplementary cementing materials (SCM), design of concrete mixtures with optimum content of cement and enhancement of concrete durability are the main issues towards sustainability in concrete industry.

  14. The cement solidification systems at LANL

    International Nuclear Information System (INIS)

    Veazey, G.W.

    1990-01-01

    There are two major cement solidification systems at Los Alamos National Laboratory. Both are focused primarily around treating waste from the evaporator at TA-55, the Plutonium Processing Facility. The evaporator receives the liquid waste stream from TA-55's nitric acid-based, aqueous-processing operations and concentrates the majority of the radionuclides in the evaporator bottoms solution. This is sent to the TA-55 cementation system. The evaporator distillate is sent to the TA-50 facility, where the radionuclides are precipitated and then cemented. Both systems treat TRU-level waste, and so are operated according to the criteria for WIPP-destined waste, but they differ in both cement type and mixing method. The TA-55 systems uses Envirostone, a gypsum-based cement and in-drum prop mixing; the TA-50 systems uses Portland cement and drum tumbling for mixing

  15. Characterization of experimental cements with endodontic goal

    International Nuclear Information System (INIS)

    Dantas, A.M.X.; Sousa, W.J.B.; Oliveira, E.D.C.; Carrodeguas, R.G.; Fook, M.V. Lia; Universidade Estadual da Paraiba

    2017-01-01

    The present study aimed to characterize experimental endodontic cements using as comparative parameter MTA cement. Two experimental endodontic cements were assessed: one based on 95% tri-strontium aluminate and 5% gypsum (CE1) and another based on 50% Sr_3Al_2O_6 and 50% non-structural white cement (CE2). Experimental cements were manipulated and characterized by scanning electron microscopy (SEM), coupled to EDS mode, X-ray diffractometer (XRD) and Thermogravimetric (TG) analysis. Data analysis demonstrated that the particles of the materials used presented varied shapes and sizes, with similar elements and crystalline behavior. However, CE1 presented increased mass loss. Experimental cements presents similarities to MTA, nevertheless, further studies are encourage to determinate comparative properties with the commercially material. (author)

  16. Modelling porewater chemistry in hydrated Portland cement

    International Nuclear Information System (INIS)

    Berner, U.R.

    1987-01-01

    Extensive employment of concrete is foreseen in radioactive waste repositories. A prerequisite for modelling the interactions between concrete and formation waters is characterization of the concrete system. Available experimental data from high pressure squeezing of cement pore-water indicate that, besides the high pH due to alkali hydroxide dissolution, cement composition itself influences the solubility determining solid phases. A model which simulates the hydration of Portland cement assuming complete hydration of the main clinker minerals is presented. The model also includes parameters describing the reactions between the cement and blending agents. Comparison with measured pore-water data generally gives a consistent picture and, as expected, the model gives correct predictions for pure Portland cements. For blended cements, the required additional parameters can, to some extent, be derived from pore-water analysis. 14 references, 1 figure, 4 tables

  17. Chemistry of cements for nuclear applications

    International Nuclear Information System (INIS)

    Barrett, P.; Glasser, F.P.

    1992-01-01

    In recent times the nuclear industry has thrown up challenges which cannot be met by the application of conventional civil and materials engineering knowledge. The contributions in this volume investigate all aspects of cement performance. The scope of the papers demonstrates the current balance of activities which have as their objective the elucidation of kinetics and immobilization, determining material interactions and of assessing future performance. The papers reflect the varied goals of the sponsors who include national governments, the Commission of the European Communities and the nuclear industries. In six parts attention is paid to the durability of cement and concrete in repository environment; interactions between cement, waste components and ground water; properties and performance of cement materials; leach behavior and mechanisms, diffusional properties of cement and concrete, including porosity-permeability relationships; and thermodynamics of cementitious systems and modelling of cement performance

  18. Influence of ligands on the photoluminescent properties of Eu3+ in europium β-diketonate/PMMA-doped systems

    International Nuclear Information System (INIS)

    Liu, H.-G.; Park, Seongtae; Jang, Kiwan; Feng, X.-S.; Kim, Changdae; Seo, H.-J.; Lee, Y.-I.

    2004-01-01

    Three kinds of europium β-diketonates Eu(DBM) 3 , Eu(BA) 3 and Eu(TTA) 3 (DBM: Dibenzoylmethane; BA: 1-Benzoylacetone; TTA: Thenoyltrifluoroacetone) were doped in poly(methyl methacrylate) (PMMA) matrix. The doped systems were studied by using photoluminescent (PL) spectroscopy, emission decay experiments and X-ray diffractometry. Eu(III) ions in the doped Eu(DBM) 3 /PMMA systems have two distinct symmetric sites and the emission band changes greatly with the compositions. Eu(III) in the Eu(BA) 3 /PMMA systems gives only one symmetric site in the doped systems and the emission band changes slightly with the compositions. Although two distinct symmetric sites of Eu(III) can be distinguished in the doped systems of Eu(TTA) 3 /PMMA, the two sites have similar 5 D 0 lifetimes and the luminescent spectra almost do not change with the compositions. XRD reveals that crystallites were formed in the doped Eu(DBM) 3 /PMMA systems that have different crystalline structure from that of the chelate, and Eu(BA) 3 and Eu(TTA) 3 exist in amorphous state in the doped systems. The difference between the PL properties and structures of the doped systems for the three kinds of chelates should be attributed to different interactions between the chelate molecules and between the chelate and PMMA

  19. NaF-loaded core-shell PAN-PMMA nanofibers as reinforcements for Bis-GMA/TEGDMA restorative resins.

    Science.gov (United States)

    Cheng, Liyuan; Zhou, Xuegang; Zhong, Hong; Deng, Xuliang; Cai, Qing; Yang, Xiaoping

    2014-01-01

    A kind of core-shell nanofibers containing sodium fluoride (NaF) was produced and used as reinforcing materials for dimethacrylate-based dental restorative resins in this study. The core-shell nanofibers were prepared by coaxial-electrospinning with polyacrylonitrile (PAN) and poly(methyl methacrylate) (PMMA) solutions as core and shell fluids, respectively. The produced PAN-PMMA nanofibers varied in fiber diameter and the thickness of PMMA shell depending on electrospinning parameters. NaF-loaded nanofibers were obtained by incorporating NaF nanocrystals into the core fluid at two loadings (0.8 or 1.0wt.%). Embedment of NaF nanocrystals into the PAN core did not damage the core-shell structure. The addition of PAN-PMMA nanofibers into Bis-GMA/TEGDMA clearly showed the reinforcement due to the good interfacial adhesion between fibers and resin. The flexural strength (Fs) and flexural modulus (Ey) of the composites decreased slightly as the thickness of PMMA shell increasing. Sustained fluoride releases with minor initial burst release were achieved from NaF-loaded core-shell nanofibers and the corresponding composites, which was quite different from the case of embedding NaF nanocrystals into the dental resin directly. The study demonstrated that NaF-loaded PAN-PMMA core-shell nanofibers were not only able to improve the mechanical properties of restorative resin, but also able to provide sustained fluoride release to help in preventing secondary caries. © 2013.

  20. Morphology and dielectric properties of poly hydroxybutyrate(PHB)/polymethyl methacrylat(PMMA) blends with some antimicrobial applications

    International Nuclear Information System (INIS)

    Abou aiad, T.H.M.

    2005-01-01

    Poly(3-hydroxy)butyrate (PHB) is microbial polyester presenting the advantages of biodegradability and biocompatibility but suffers from several problems as it is brittle and has low abilities for some chemical modifications. To overcome such problems a reactive blending was done with a glassy acrylic polymer, poly(methyl methacrylate) (PMMA) with different compositions. The dielectric response of poly [(7)-3-hydroxybutyrate] (PHB)/(PMMA) was investigated as a function of frequency (100 Hz to 100 KHz) and at different temperatures from 20 to 160 degree C above the glass transition temperature of PHB. The results revealed the existence of a single relaxation process indicating that there is miscibility between amorphous fractions of PHB and PMMA. Subsequently a continuous decrease in relaxation strength occurred, indicating considerable changes in molecular mobility. The results provide further evidence that molecular mobility in the amorphous regions decreases significantly and this would be the reason for the embrittlement detected on ageing at room temperature. Also the morphological study of such blends don't show macro phase separation of PMMA on the surface scan which may be attributed to the compatibility in melt between PHB and PMMA particle in the PHB matrix. The biological activity of such investigated systems was tested against a representative number of pathogenic organisms by determining the minimum inhibitory concentration (MIC). The activity was found to increase by increasing the amount of PMMA in the blend

  1. Adsorption of Carbon Dioxide onto Tetraethylenepentamine Impregnated PMMA Sorbents with Different Pore Structure

    Energy Technology Data Exchange (ETDEWEB)

    Jo, Dong Hyun; Park, Cheonggi; Jung, Hyunchul; Kim, Sung Hyun [Korea University, Seoul (Korea, Republic of)

    2015-02-15

    Poly(methyl methacrylate) (PMMA) supports and amine additives were investigated to adsorb CO{sub 2}. PMMA supports were fabricated by using different ratio of pore forming agents (porogen) to control the BET specific surface area, pore volume and distribution. Toluene and xylene are used for porogens. Supported amine sorbents were prepared by wet impregnation of tetraethylenepentamine (TEPA) on PMMA supports. So we could identify the effect of the pore structure of supports and the quantity of impregnated TEPA on the adsorption capacity. The increased amount of toluene as pore foaming agent resulted in the decreased average pore diameter and the increased BET surface area. Polymer supports with huge different pore distribution could be fabricated by controlling the ratio of porogen. After impregnation, the support with micropore structure is supposed the pore blocking and filling effect so that it has low CO{sub 2} capacity and kinetics due to the difficulty of diffusing. Macropore structure indicates fast adsorption capacity and low influence of amine loading. In case of support with mesopore, it has high performance of adsorption capacity and kinetics. So high surface area and meso-/macro- pore structure is suitable for CO{sub 2} capture.

  2. Research on Continuous Injection Direct Rolling Process for PMMA Optical Plate

    Directory of Open Access Journals (Sweden)

    HaiXiong Wang

    2014-06-01

    Full Text Available Continuous injection direct rolling (CIDR combined intermittent injection and rolling process is a new technology for molding optical polymer plates with microstructured patterns; research on forming PMMA optical plates is an aspect of it in this paper. The equipment of CIDR process consists of plastic injection module, precision rolling module, and automatic coiling module. Based on the establishing mathematical CIDR models, numerical analysis was used to explode the distribution of velocity, temperature, and pressure in injection-rolling zone. The simulation results show that it is feasible to control the temperature, velocity, and injection-rolling force, so it can form polymer plate under certain process condition. CIDR experiment equipment has been designed and produced. PMMA optical plate was obtained by CIDR experiments, longitudinal thickness difference is 0.005 mm/200 mm, horizontal thickness difference is 0.02/200 mm, transmittance is 86.3%, Haze is 0.61%, and the difference is little compared with optical glasses. So it can be confirmed that CIDR process is practical to produce PMMA optical plates.

  3. Use of lead (II) sulfide nanoparticles as stabilizer for PMMA exposed to gamma irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Garcia, Olga Pinheiro; Albuquerque, Marilia Cordeiro Carneiro de; Aquino, Katia Aparecida da Silva; Araujo, Elmo Silvano de, E-mail: aquino@ufpe.br [Universidade Federal de Pernambuco (UFPE), Recife, PE (Brazil). Dept. de Energia Nuclear; Araujo, Patricia Lopes Barros de [Universidade Federal Rural de Pernambuco (UFRPE), Recife, PE (Brazil)

    2015-03-15

    Lead (II) sulfide (PbS) were synthesized by sonochemical method and crystals with cubic structure exhibit aggregated nanoparticles with size in the range of 50-100 nm. Commercial Poly(methyl methacrylate) (PMMA) containing the PbS nanoparticles (PbS-NP) exposed to gamma irradiation were investigated and both the viscosity-average molar mass (Mv ) and degradation index (DI) values were measured. Ours results showed decreases in molar mass when the systems were gamma irradiated, i. e., random scission effects that take place in the main chain. On the other hand, DI results showed that the addition of PbS-NP at 0.3 wt% into the PMMA matrix decreased 100% the number of main chain scissions. Results about the free radical scavenger action of the PbS-NP were obtained by use of 2,2-diphenyl-1-(2,4,6-trinitrophenyl)-hydrazyl radical (DPPH) and are discussed in this study. Analysis of infrared spectra, refraction index, mechanical, and thermal properties showed influence of the PbS-NP in the physical behavior of PMMA. (author)

  4. Spectroscopic analysis of PMMA/PVC blends containing CoCl2

    Directory of Open Access Journals (Sweden)

    N.S. Alghunaim

    2015-01-01

    Full Text Available Composites of polymethyl methacrylate (PMMA and polyvinyl chloride (PVC polymer blend containing different concentrations (⩽10 wt. of cobalt chloride (CoCl2 were prepared by casting techniques. The changes of the structural, spectroscopic, optical and thermal parameters of the samples are studied using different tools. FT-IR spectroscopy confirmed the complexation between the blends and Co+2-ions. The decrease or increase of IR band intensity with some shifts of other bands suggests an interaction and compatibility between PMMA/PVC blends with CoCl2 take place. The Ultra violet and visible (UV/Vis spectra indicated that the presence of band gap energy depends on increasing of CoCl2 contents. The absorption intensity of the samples doped with CoCl2 becomes faint lower than the pure blend. The values of energy gap for direct and indirect transition decreases with the increase of CoCl2 due to the presence of charge transfer between PMMA/PVC and CoCl2. The thermogravimetric analysis (TGA curves for all the samples have the same behavior and more steps of decomposition were observed. The reduction of mass loss for samples containing CoCl2 compared to the pure blend was observed and it was attributed to crosslink formation between the blend and CoCl2.

  5. Synthesis and fluorescence properties of some difluoroboron β-diketonate complexes and composite containing PMMA

    Science.gov (United States)

    Xing, Dongye; Hou, Yanjun; Niu, Haijun

    2018-03-01

    A series of difluoroboron β-diketonate complexes, containing the indon-β-diketonate ligand carrying methyl or methoxyl substituents was synthesized. The crystal structures of the complexes were confirmed by single crystal X-ray diffraction studies. The fluorescence properties of compounds were studied in solution state, solid state and on PMMA polymer matrix. The photophysical data of compounds 2a-2d exhibited strong fluorescence and photostability under the ultraviolet light (Hg lamp). The complex 2b showed higher fluorescence intensity in solution state as compared to other complexes of the series. The complexes 2c and 2d showed higher fluorescence intensity in the solid state, which are ascribed to the stronger π-π interactions between ligands in the solid state. The introduction of methoxyl or methyl groups on the benzene rings enhanced the absorption intensity, emission intensity, quantum yields and fluorescence lifetimes due to their electron-donating nature. Furthermore, the complex 2b was doped into the PMMA to produce hybrid materials, where the PMMA matrix acted as sensitizer for the central boron ion to enhance the fluorescence emission intensity and quantum yields.

  6. Study of SiO2/PMMA/CE tri-component interpenetrating polymer network composites

    International Nuclear Information System (INIS)

    Wang Junlong; Wang Chuang; Jiao Gengsheng; Wang Qiuya

    2010-01-01

    A technology of conjugated tri-component interpenetrating polymer networks was applied to synthesize a nano-SiO 2 /polymethylmethacrylate (PMMA)/cyanate (CE) composite through an asynchronous synthesis way. The microstructure of the composite was characterized using infrared spectroscopy (IR) and transmission electron microscopy (TEM). The mechanical properties were measured in German-made DL-1000B and XCL-40 universal material test machines, respectively. Results showed that both the impact strength and the flexural strength were in the optimum status when 3% SiO 2 /PMMA/CE was chosen as a sample with the PMMA/CE ratio of 20/80. Compared with the strengths of pure cyanate, those of the composite were raised by 137.28% and 31.29%, respectively. When 3% nano-SiO 2 was added, the impact strength was increased by 29.96% and the flexural strength by 20.05%, compared with the strengths of polymers without SiO 2 . Analysis and measurements by IR and TEM indicated that no chemical reactions took place among components in the composite. The interpenetration of the conjugated tri-component improved the loading capacity of the polymer, hence the toughness enhancement of cyanate.

  7. Thin-Film LSCs Based on PMMA Nanohybrid Coatings: Device Optimization and Outdoor Performance

    Directory of Open Access Journals (Sweden)

    S. M. El-Bashir

    2013-01-01

    Full Text Available This study concerns the design optimization of thin-film luminescent solar concentrators (TLSCs based on polymethylmethacrylate (PMMA/silica nanohybrid films doped with coumarin dyestuffs specialized in coloring plastics. Two designs of TLSCs had been prepared and characterized. The first consists of a transparent nanohybrid layer coated on a fluorescent PMMA substrate. The second design is the ordinary configuration in which fluorescent nanohybrid layer is coated on a transparent PMMA substrate. The investigation of the spectral properties and efficiency parameters recommended the best solar energy conversion efficiency for the second design. The outdoor performance of optimized TLSC was also evaluated under clear sky conditions of Riyadh city, and the hourly values of the optical efficiency, ηopt, were calculated for one year. The best performance was achieved in summer since the short circuit current for PV cell was doubled after being attached to TLSC and the value of ηopt reached 40% which is higher than other values recorded before due to the abundant solar energy potential in the Arabian Peninsula.

  8. Environmental Impacts on the Strength Parameters of Mineral-Acrylic (PMMA/ATH Facade Panels

    Directory of Open Access Journals (Sweden)

    Aleksander Byrdy

    2015-01-01

    Full Text Available Composite mineral-acrylic panels consist in 80% of natural minerals produced from bauxite (aluminium hydroxides (ATH and in 20% from acrylic resin (polymethyl methacrylate (PMMA. This material due to high usability is widely used in interior finishes. Recently, the mineral-acrylic panels have been used as external claddings of buildings. So far, there are several dozen elevations realized worldwide. Due to the variability of the strength parameters of PMMA acrylic resins depending on the environmental influence, a number of tests on samples of mineral-acrylic panels to verify their suitability for use in climate conditions in Central Europe were performed. The studies determined the change of the material parameters after being subjected to aging process in conditions of high temperature, high relative humidity, freeze-thaw cycles, and UV radiation. In the studies parameters such as flexural strength and modulus of elasticity were measured at a reference temperature of 23°C. In raised and lowered temperatures only the tensile strength tests were conducted. Due to the lack of information in the available literature, the authors carried out tests of the temperature influence on the PMMA/ATH composite modulus of elasticity and flexural strength which is crucial in designing process.

  9. Tooling device design for vibration-assisted high speed shaping of PMMA

    International Nuclear Information System (INIS)

    Mostofa, Md. Golam; Noh, J. H.; Kim, H. Y.; Ahn, J. H.; Kang, D. B.

    2010-01-01

    PMMA optical components that are used as one of the most important parts of high precision equipment and machines are increasingly replacing the glass due to the various advantages of PMMA. Especially in Light Guide Panels, the PMMA sheet that is used in Liquid Crystal Displays plays an important role in scattering the incident light and requires very fine machining as the sheet is directly related to the optical characteristics of the panels. The High Speed End milling and High Speed Shaping processes that are widely adopted and applied to the precise machining of Light Incident Plane still have quality problems, such as cracks, breakages, poor waviness, and straightness. This paper presents the tooling device design for machining a Light Incident Plane through vibration-assisted High Speed Shaping for increasing the optical quality by minimizing the above-mentioned problems. The cutting tool and the tool post presented in this paper are designed by the authors to increase the magnitude of the cutting stroke by adopting the resonant frequency without weakening the stiffness and to reduce vibrations during even high speed feeding. The dynamic characteristics of the cutting tool and the tool post are evaluated through simulation and experiment as well. The results reveal very appropriate dynamic characteristics for vibration-assisted High Speed Shaping

  10. The mechanical effect of the existing cement mantle on the in-cement femoral revision.

    Science.gov (United States)

    Keeling, Parnell; Lennon, Alexander B; Kenny, Patrick J; O'Reilly, Peter; Prendergast, Patrick J

    2012-08-01

    Cement-in-cement revision hip arthroplasty is an increasingly popular technique to replace a loose femoral stem which retains much of the original cement mantle. However, some concern exists regarding the retention of the existing fatigued and aged cement in such cement-in-cement revisions. This study investigates whether leaving an existing fatigued and aged cement mantle degrades the mechanical performance of a cement-in-cement revision construct. Primary cement mantles were formed by cementing a polished stem into sections of tubular steel. If in the test group, the mantle underwent conditioning in saline to simulate ageing and was subject to a fatigue of 1 million cycles. If in the control group no such conditioning or fatigue was carried out. The cement-in-cement procedure was then undertaken. Both groups underwent a fatigue of 1 million cycles subsequent to the revision procedure. Application of a Mann-Whitney test on the recorded subsidence (means: 0.51, 0.46, n=10+10, P=0.496) and inducible displacement (means: 0.38, 0.36, P=0.96) revealed that there was no statistical difference between the groups. This study represents further biomechanical investigation of the mechanical behaviour of cement-in-cement revision constructs. Results suggest that pre-revision fatigue and ageing of the cement may not be deleterious to the mechanical performance of the revision construct. Thus, this study provides biomechanical evidence to back-up recent successes with this useful revision technique. Copyright © 2012 Elsevier Ltd. All rights reserved.

  11. Sustainable Development of the Cement Industry and Blended Cements to Meet Ecological Challenges

    OpenAIRE

    Sobolev, Konstantin

    2003-01-01

    The world production of cement has greatly increased in the past 10 years. This trend is the most significant factor affecting technological development and the updating of manufacturing facilities in the cement industry. Existing technology for the production of cement clinker is ecologically damaging; it consumes much energy and natural resources and also emits pollutants. A new approach to the production of blended or high-volume mineral additive (HVMA) cement helps to improve its ecologi...

  12. Pulmonary Cement Embolism following Percutaneous Vertebroplasty

    Directory of Open Access Journals (Sweden)

    Ümran Toru

    2014-01-01

    Full Text Available Percutaneous vertebroplasty is a minimal invasive procedure that is applied for the treatment of osteoporotic vertebral fractures. During vertebroplasty, the leakage of bone cement outside the vertebral body leads to pulmonary cement embolism, which is a serious complication of this procedure. Here we report a 48-year-old man who was admitted to our hospital with dyspnea after percutaneous vertebroplasty and diagnosed as pulmonary cement embolism.

  13. Tritium sorption by cement and subsequent release

    International Nuclear Information System (INIS)

    Ono, F.; Tanaka, S.; Yamawaki, M.

    1994-01-01

    In a fusion reactor or tritium handling facilities, contamination of concrete by tritium and subsequent release from it to the reactor or experimental rooms is a matter of problem for safety control of tritium and management of operational environment. In order to evaluate these tritium behavior, interaction of tritiated water with concrete or cement should be clarified. In the present study, HTO sorption and subsequent release from cement were studied by combining various experimental methods. From the basic studies on tritium-cement interactions, it has become possible to evaluate tritium uptake by cement or concrete and subsequent tritium release behavior as well as tritium removing methods from them

  14. Immobilisation of ion exchange resins in cement

    International Nuclear Information System (INIS)

    Howard, C.G.; Jolliffe, C.B.; Lee, D.J.

    1990-09-01

    The removal of activity from spent decontaminating solutions eg LOMI can be achieved using organic ion exchange resins. These resins can be successfully immobilised in cement based matrices. The optimum cement system contained 10% ordinary Portland cement 84% gg blast furnace slag, 6% microsilica with a water cement ratio of 0.5 and a dry resin loading of 36% with respect to total weight. This formulation was successfully scaled up to 200 litres giving a product with acceptable compressive strength, dimensional stability and elastic modulus. Storage of samples under water appears to have no detrimental effects on the product's properties. (author)

  15. Immobilisation of ion exchange resins in cement

    International Nuclear Information System (INIS)

    Howard, C.G.; Jolliffe, C.B.; Lee, D.J.

    1990-09-01

    The removal of activity from spent decontaminating solutions eg LOMI can be achieved using organic ion exchange resins. These resins can be successfully immobilised in cement based matrices. The optimum cement system contained 10% ordinary Portland cement, 84% gg blast furnace slag, 6% microsilica with a water cement ratio of 0.5 and a dry resin loading of 36% with respect to total weight. This formulation was successfully scaled up to 200 litres giving a product with acceptable compressive strength, dimensional stability and elastic modulus. Storage of samples under water appears to have no detrimental effects on the products' properties. (author)

  16. Use of rubber crumbs in cement concrete

    Science.gov (United States)

    Longvinenko, A. A.

    2018-03-01

    Rubber crumb obtained from worn out tires has been increasingly used over the last 15-20 years, especially in manufacture of asphalt and cement concrete mixtures. This review pays principal attention to application of the rubber crumb to cement concrete mixtures. Use of the rubber crumb in cement concrete is not as successful as in asphalt concrete mixtures, due to incompatibility problems linked to chemical composition and a significant difference in rigidity between the rubber crumb and concrete mixture aggregates. Different methods are proposed and studied to mitigate the adverse influence and increase the beneficial effects of the rubber crumb when added to cement concrete.

  17. Controls on Cementation in a Chalk Reservoir

    DEFF Research Database (Denmark)

    Meireles, Leonardo Teixeira Pinto; Hussein, A.; Welch, M.J.

    2017-01-01

    In this study, we identify different controls on cementation in a chalk reservoir. Biot’s coefficient, a measure of cementation, stiffness and strength in porous rocks, is calculated from logging data (bulk density and sonic Pwave velocity). We show that Biot’s coefficient is correlated...... that some degree of pore filling cementation occurred in Kraka (Alam, 2010). Lack of correlation between Biot’s coefficient and Gamma Ray (GR) indicates that the small amount of clay present is generally located in the pore space, thus not contributing to frame stiffness. While there was no compositional...... control on cementation via clay, we could infer that stratigraphy impacts on the diagenetic process....

  18. Immobilisation of radwaste in cement based matrices

    International Nuclear Information System (INIS)

    Glasser, F.P.; Macphee, D.; Atkins, M.; Pointer, C.; Cowie, J.; Wilding, C.R.; Mattingley, N.J.; Evans, P.A.

    1989-01-01

    The solubilities and influence on cement pH are reported for calcium aluminate and aluminosulphate hydrates. The solubility of Ca(OH) 2 is reported to 700 bars. Polymerization of C-S-H is investigated by NMR. Specific interactions of U 6+ and iodine (I - , IO 3 - ) with cement components are described. The impact of radiation on cements and the influence of higher temperature are documented. The role of dissolved Ca and CO 2 in groundwaters as dissolution media for cements are reported. (author)

  19. Integer programming of cement distribution by train

    Science.gov (United States)

    Indarsih

    2018-01-01

    Cement industry in Central Java distributes cement by train to meet daily demand in Yogyakarta and Central Java area. There are five destination stations. For each destination station, there is a warehouse to load cements. Decision maker of cement industry have a plan to redesign the infrastructure and transportation system. The aim is to determine how many locomotives, train wagons, and containers and how to arrange train schedules with subject to the delivery time. For this purposes, we consider an integer programming to minimize the total of operational cost. Further, we will discuss a case study and the solution the problem can be calculated by LINGO software.

  20. Prediction of hydroxyl concentrations in cement pore water using a numerical cement hydration model

    NARCIS (Netherlands)

    Eijk, van R.J.; Brouwers, H.J.H.

    2000-01-01

    In this paper, a 3D numerical cement hydration model is used for predicting alkali and hydroxyl concentrations in cement pore water. First, this numerical model is calibrated for Dutch cement employing both chemical shrinkage and calorimetric experiments. Secondly, the strength development of some

  1. Evaluation of cement thixotropy for the cement of oil wells in areas ...

    African Journals Online (AJOL)

    ... economical for cementing job operations in wells with loss zones. The results also show that the effect of LHF is positive, since in addition to his contribution to long term performances, especially the durability of hardened concrete, it improves the thixotropy of cement made of plaster. Keywords: cementing; lost circulation; ...

  2. Geotechnical Properties of Clayey Soil Stabilized with Cement ...

    African Journals Online (AJOL)

    ADOWIE PERE

    2017-12-31

    Dec 31, 2017 ... ... to investigate the different effects of cement-sawdust ash and cement on a ... Keywords: Cement, Saw dust, strength test subgrade material, highway construction ... characteristics of lateritic soil stabilized with sawdust ash.

  3. Opposed-Flow Flame Spread in a Narrow Channel Apparatus over Thin PMMA Sheets

    Science.gov (United States)

    Bornand, G. R.; Olson, Sandra L.; Miller, F. J.; Pepper, J. M.; Wichman, I. S.

    2013-01-01

    Flame spread tests have been conducted over polymethylmethacrylate (PMMA) samples in San Diego State University's Narrow Channel Apparatus (SDSU NCA). The Narrow Channel Apparatus (NCA) has the ability to suppress buoyant flow in horizontally spreading flames, and is currently being investigated as a possible replacement or complement to NASA's current material flammability test standard for non-metallic solids, NASA-STD-(I)-6001B Test 1. The buoyant suppression achieved with a NCA allows for tests to be conducted in a simulated microgravity atmosphere-a characteristic that Test 1 lacks since flames present in Test 1 are buoyantly driven. The SDSU NCA allows for flame spread tests to be conducted with varying opposed flow oxidizer velocities, oxygen percent by volume, and total pressure. Also, since the test sample is placed symmetrically between two confining plates so that there is a gap above and below the sample, this gap can be adjusted. This gap height adjustment allows for a compromise between heat loss from the flame to the confining boundaries and buoyancy suppression achieved by those boundaries. This article explores the effect gap height has on the flame spread rate for 75 µm thick PMMA at 1 atm pressure and 21% oxygen concentration by volume in the SDSU NCA. Flame spread results from the SDSU NCA for thin cellulose fuels have previously been compared to results from tests in actual microgravity at various test conditions with the same sample materials and were found to be in good agreement. This article also presents results from the SDSU NCA for PMMA at 1 atm pressure, opposed oxidizer velocity ranging from 3 to 35 cm/s, oxygen concentration by volume at 21%, 30 %, and 50% and fuel thicknesses of 50 and 75 µm. These results are compared to results obtained in actual microgravity for PMMA obtained at the 4.5s drop tower of MGLAB in Gifu, Japan, and the 5.2s drop tower at NASA's Zero-Gravity Research Facility in Cleveland, OH. This comparison confirms

  4. Erosion of water-based cements evaluated by volumetric and gravimetric methods.

    Science.gov (United States)

    Nomoto, Rie; Uchida, Keiko; Momoi, Yasuko; McCabe, John F

    2003-05-01

    To compare the erosion of glass ionomer, zinc phosphate and polycarboxylate cements using volumetric and gravimetric methods. For the volumetric method, the eroded depth of cement placed in a cylindrical cavity in PMMA was measured using a dial gauge after immersion in an eroding solution. For the gravimetric method, the weight of the residue of a solution in which a cylindrical specimen had been immersed was measured. 0.02 M lactic acid solution (0.02 M acid) and 0.1 M lactic acid/sodium lactate buffer solution (0.1 M buffer) were used as eroding solutions. The pH of both solutions was 2.74 and the test period was 24 h. Ranking of eroded depth and weight of residue was polycarboxylate>zinc phosphate>glass ionomers. Differences in erosion were more clearly defined by differences in eroded depth than differences in weight of residue. In 0.02 M acid, the erosion of glass ionomer using the volumetric method was effected by the hygroscopic expansion. In 0.1 M buffer, the erosion for polycarboxylate and zinc phosphate using the volumetric method was much greater than that using the gravimetric method. This is explained by cryo-SEM images which show many holes in the surface of specimens after erosion. It appears that zinc oxide is dissolved leaving a spongy matrix which easily collapses under the force applied to the dial gauge during measurement. The volumetric method that employs eroded depth of cement using a 0.1 M buffer solution is able to quantify erosion and to make material comparisons.

  5. Incorporation of antibiotics effective against multidrug resistant pathogens into PMMA for cranio maxillofacial implants

    Science.gov (United States)

    2018-04-12

    sit until dough phase was reached, and was then rolled into the mold shown in Figure 1. The mold was pressed between steel plates and placed into a...further analysis. Compression testing Compression testing was carried out with reference to ISO 5833: Implants for surgery — Acrylic resin cements ...Parra-Ruiz J. Elution kinetics, antimicrobial activity, and mechanical properties of 11 different antibiotic loaded acrylic bone cement . Diagn Microbiol

  6. Rietveld analysis, powder diffraction and cement

    International Nuclear Information System (INIS)

    Peterson, V.

    2002-01-01

    Full text: Phase quantification of cement is essential in its industrial use, however many methods are inaccurate and/or time consuming. Powder diffraction is one of the more accurate techniques used for quantitative phase analysis of cement. There has been an increase in the use of Rietveld refinement and powder diffraction for the analysis and phase quantification of cement and its components in recent years. The complex nature of cement components, existence of solid solutions, polymorphic variation of phases and overlapping phase peaks in diffraction patterns makes phase quantification of cements by powder diffraction difficult. The main phase in cement is alite, a solid solution of tricalcium silicate. Tricalcium silicate has been found to exist in seven modifications in three crystal systems, including triclinic, monoclinic, and rhombohedral structures. Hence, phase quantification of cements using Rietveld methods usually involves the simultaneous modelling of several tricalcium silicate structures to fit the complex alite phase. An industry ordinary Portland cement, industry and standard clinker, and a synthetic tricalcium silicate were characterised using neutron, laboratory x-ray and synchrotron powder diffraction. Diffraction patterns were analysed using full-profile Rietveld refinement. This enabled comparison of x-ray, neutron and synchrotron data for phase quantification of the cement and examination of the tricalcium silicate. Excellent Rietveld fits were achieved, however the results showed that the quantitative phase analysis results differed for some phases in the same clinker sample between various data sources. This presentation will give a short introduction about cement components including polymorphism, followed by the presentation of some problems in phase quantification of cements and the role of Rietveld refinement in solving these problems. Copyright (2002) Australian X-ray Analytical Association Inc

  7. Compressive Strength and Physical Properties Behavior of Cement Mortars with addition of Cement Klin Dust

    OpenAIRE

    Auday A Mehatlaf

    2017-01-01

    Cement Klin Dust (CKD) was the waste of almost cement industry factories, so that in this paper utilization of CKD as filler in cement and/or concrete was the main objective. CKD from the Karbala cement factory had been used and analysis to know the chemical composition of the oxides was done. In this paper cement mortars with different weight percentages of CKD (0,5,10,20,30,40) had been prepared. Physical properties such as density and porosity were done in different age curing (3, 7, 28) d...

  8. Facile synthesis of hollow Sn-Co@PMMA nanospheres as high performance anodes for lithium-ion batteries via galvanic replacement reaction and in situ polymerization

    Science.gov (United States)

    Yu, Xiaohui; Jiang, Anni; Yang, Hongyan; Meng, Haowen; Dou, Peng; Ma, Daqian; Xu, Xinhua

    2015-08-01

    Polymethyl methacrylate (PMMA)-coated hollow Sn-Co nanospheres (Sn-Co@PMMA) with superior electrochemical performance had been synthesized via a facile galvanic replacement method followed by an in situ emulsion polymerization route. The properties were investigated in detail and results show that the hollow Sn-Co nanospheres were evenly coated with PMMA. Benefiting from the protection of the PMMA layers, the hollow Sn-Co@PMMA nanocomposite is capable of retaining a high capacity of 590 mAh g-1 after 100 cycles with a coulomb efficiency above 98%, revealing better electrochemical properties compared with hollow Sn-Co anodes. The PMMA coating could help accommodate the mechanical strain caused by volume expansion and stabilize the solid electrolyte interphase (SEI) film formed on the electrode. Such a facile process could be further extended to other anode materials for lithium-ion batteries.

  9. A Study on the Manufacturing Properties of Crack Self-Healing Capsules Using Cement Powder for Addition to Cement Composites

    OpenAIRE

    Choi, Yun-Wang; Oh, Sung-Rok; Choi, Byung-Keol

    2017-01-01

    We fabricated crack self-healing capsules using cement powder for mixing into cement composites and evaluated the properties of the capsule manufacturing process in this study. The manufacture of the self-healing capsules is divided into core production processing of granulating cement in powder form and a coating process for creating a wall on the surfaces of the granulated cement particles. The produced capsules contain unhardened cement and can be mixed directly with the cement composite m...

  10. Analysis of Chemical Composition of Portland Cement in Ghana: A Key to Understand the Behavior of Cement

    OpenAIRE

    Bediako, Mark; Amankwah, Eric Opoku

    2015-01-01

    The performance of Portland cement in concrete or mortar formation is very well influenced by chemical compositions among other factors. Many engineers usually have little information on the chemical compositions of cement in making decisions for the choice of commercially available Portland cement in Ghana. This work analyzed five different brands of Portland cement in Ghana, namely, Ghacem ordinary Portland cement (OPC) and Portland limestone cement (PLC), CSIR-BRRI Pozzomix, Dangote OPC, a...

  11. Influence of Cements Containing Calcareous Fly Ash as a Main Component Properties of Fresh Cement Mixtures

    Science.gov (United States)

    Gołaszewski, Jacek; Kostrzanowska-Siedlarz, Aleksandra; Ponikiewski, Tomasz; Miera, Patrycja

    2017-10-01

    The main goal of presented research was to examine usability of cements containing calcareous fly ash (W) from technological point of view. In the paper the results of tests concerning the influence of CEM II and CEM IV cements containing fly ash (W) on rheological properties, air content, setting times and plastic shrinkage of mortars are presented and discussed. Moreover, compatibility of plasticizers with cements containing fly ash (W) was also studied. Additionally, setting time and hydration heat of cements containing calcareous fly ash (W) were determined. In a broader aspect, the research contributes to promulgation of the possibility of using calcareous fly ash (W) in cement and concrete technology, what greatly benefits the environment protection (utilization of waste fly ash). Calcareous fly ash can be used successfully as the main component of cement. Cements produced by blending with processed fly ash or cements produced by interginding are characterized by acceptable technological properties. In respect to CEM I cements, cements containing calcareous fly ash worsen workability, decrease air content, delay setting time of mixtures. Cements with calcareous fly ash show good compatibility with plasticizers.

  12. Photocatalytic degradation of p-phenylenediamine with TiO{sub 2}-coated magnetic PMMA microspheres in an aqueous solution

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Y.-H. [Department of Chemical Engineering and Biotechnology, National Taipei University of Technology, 1, Sec. 3, Chung-Hsiao E. Road, Taipei 106, Taiwan (China)], E-mail: yhchen1@ntu.edu.tw; Liu, Y.-Y.; Lin, R.-H.; Yen, F.-S. [Department of Chemical and Material Engineering, National Kaohsiung University of Applied Sciences, 415 Chien Kung Road, Kaohsiung 807, Taiwan (China)

    2009-04-30

    This study investigates the photocatalytic degradation of p-phenylenediamine (PPD) with titanium dioxide-coated magnetic poly(methyl methacrylate) (TiO{sub 2}/mPMMA) microspheres. The TiO{sub 2}/mPMMA microspheres are employed as novel photocatalysts with the advantages of high photocatalytic activity, magnetic separability, and good durability. The scanning electron microscopy (SEM), energy dispersive spectrometer (EDS), and transmission electron microscopy (TEM) images of the TiO{sub 2}/mPMMA microspheres are used to characterize the morphology, element content, and distribution patterns of magnetite and TiO{sub 2} nanoparticles. The BET-specific surface area and saturation magnetization of the TiO{sub 2}/mPMMA microspheres are observed as 2.21 m{sup 2}/g and 4.81 emu/g, respectively. The photocatalytic degradation of PPD are performed under various experimental conditions to examine the effects of initial PPD concentration, TiO{sub 2}/mPMMA microsphere dosage, and illumination condition on the eliminations of PPD and chemical oxygen demand (COD) concentrations. Good repeatability of photocatalytic performance with the use of the TiO{sub 2}/mPMMA microspheres has been demonstrated in the multi-run experiments. The photocatalytic kinetics for the reductions of PPD and COD associated with the initial PPD concentration, UV radiation intensity, and TiO{sub 2}/mPMMA microsphere dosage are proposed. The relationships between the reduction percentages of COD and PPD are clearly presented.

  13. Investigation of optical properties of PMMA opals and inverse opals with YVO4-Eu nano-phosphors

    International Nuclear Information System (INIS)

    Thakur, Shashi; Gathania, Arvind K.

    2015-01-01

    In recent years, opals and inverse opals have attracted the attention of researchers because of their potential applications in photonic devices. The idea of the periodic photonic crystal was proposed by Yablonovitch and John. The photonic crystals are in analogy with crystalline solid: electromagnetic waves propagating in the photonic crystal experienced periodic spatial variation of dielectric constant, as the de Broglie wave propagation in crystalline solids experienced periodic variation of the atomic potential. In the present work we synthesized the PMMA spheres using colloidal crystallization method and PMMA colloidal multilayer crystal were developed on the quartz substrate by self-assembly vertical deposition method. Afterward PMMA microspheres were infiltrated with YVO 4 -Eu nano-phosphors followed by heating at 500 °C and above to form the inverse opals. Transmission spectra for pure PMMA, infiltrated PMMA and inverse opal of PMMA are obtained. The colloidal crystal multilayer shows a stop band at 596nm, which arises from the Bragg reflection of the (111) planes. The central position of this band gap is shifted to 608nm because of the change in the refractive index of the structure after infiltration. As the calcination was carried out at 500 °C and 600 °C, the central position of the band shifted to 483nm and 500nm respectively, because of the change in the effective refractive index of the structure and shrinkage in the direction perpendicular to the film. The resulting structure still exhibits a band gap, as the crystalline ordering is kept after the crystal is inverted. The intensity of inverse opals of PMMA is very small as compared to the bulk powder briefing the application of microstructures for the low voltage light emitting diodes (LEDs). The results show band gap and luminescent characteristics strongly depend upon infiltration. (author)

  14. Effects of the molar mass of the matrix on electrical properties, structure and morphology of plasticized PANI-PMMA blends

    International Nuclear Information System (INIS)

    Gmati, Fethi; Fattoum, Arbi; Bohli, Nadra; Mohamed, Abdellatif Belhadj

    2008-01-01

    The effects of the molar mass of polymethylmethacrylate (PMMA) on electrical, structural and morphological properties of conductive polyaniline-polymethylmethacrylate blends have been studied. We have plasticized the PMMA matrix by using dioctyl phthalate (DioPh). Three different molar masses of PMMA, 15 000, 120 000 and 350 000 g mol -1 , have been used. The x-ray diffraction analysis showed amorphous structure for all our studied PANI-PMMA blend films. The SEM micrographs showed more aggregation with the lowest molar mass of PMMA matrix. The direct current (dc) and alternating current (ac) electrical conductivities have been investigated in the temperature range 20-300 K and frequency range 7-1 x 10 8 Hz. The results of this study indicate an increase of the conductivity when the molar mass of PMMA decreases. With the lowest molar mass of PMMA (15 000 g mol -1 ), we obtained the lowest percolation threshold (p c ∼0.3%). The dc conductivity is governed by Mott's three-dimensional variable range hopping (3D VRH) model; different Mott's parameters have been evaluated. At high frequencies, the ac conductivity follows the power law σ(ω,T) = A(T)ω s(T,ω) , which is characteristic for charge transport in disordered materials by hopping or tunnelling processes. The observed decrease in the frequency exponent s with increasing temperature suggests that the correlated barrier hopping (CBH) model best describes the ac conduction mechanism. All our blends are well described by the scaling law σ(ω)/σ dc = 1+(ω/ω c ) n with n∼0.51-0.52

  15. Complications with PMMA compared with other materials used in cranioplasty: a systematic review and meta-analysis

    Directory of Open Access Journals (Sweden)

    Rafaella de Souza LEÃO

    2018-06-01

    Full Text Available Abstract Polymethyl methacrylate (PMMA has been considered a suitable material for cranioplasty. However, no consensus has been reached concerning the best material for cranioplasty with regard to minimizing complications. Thus, this systematic review and meta-analysis aimed to compare the complication rates of PMMA with those of autologous bone and titanium mesh. This review was registered with PROSPERO (CRD42016042725. Systematic searches were conducted on PubMed/MEDLINE, Scopus, and Web of Science. The focus question was, “Do PMMA prostheses used in cranioplasty have complications rates similar to those of autologous bone and titanium mesh?” A meta-analysis of complication rates was performed on the basis of dichotomous outcomes assessed by risk ratio (RR with corresponding 95% confidence intervals (CI. From 1014 data sources, 11 articles were selected according to eligibility criteria. These articles involved 1,256 individuals and 1,278 cranioplasties using autologous bone (n = 408, PMMA (n = 379, or titanium (n = 151. The follow-up period ranged from 63 days to 54.3 months. No difference was observed between the complication rates of PMMA and autologous bone (p = 0.94; RR, 0.98; 95%CI, 0.54–1.75 or between PMMA and titanium (p = 0.38; RR, 1.59; 95%CI, 0.57–4.48. Sub-analysis of the reasons for craniotomy (trauma/non-trauma was conducted, which revealed no significant difference (p = 0.91; RR, 0.95; 95%CI, 0.37–2.42. The meta-analysis indicated that the use of PMMA yields complication rates that are near those of autologous bone and titanium mesh.

  16. Modifications in optical and structural properties of PMMA/PCTFE blend films as a function of PCTFE concentration

    Energy Technology Data Exchange (ETDEWEB)

    Tripathi, J., E-mail: jtripathi00@gmail.com [Dept. of Physics, ISLE, IPS Academy, Indore (India); Sharma, A. [Dept. of Physics, Manipal University Jaipur, Jaipur (India); Tripathi, S. [UGC-DAE Consortium for Scientific Research, Indore (India); Bisen, R. [Dept. of Physics, ISLE, IPS Academy, Indore (India); Agrawal, A. [Dept. of Elect. and Commun., Global Engineering College, Jabalpur (India)

    2017-06-15

    The poly (methyl methacrylate) (PMMA) polymer blend films were prepared by solution casting method with varying PolyChloroTriFluoroEthylene (PCTFE) concentrations (1–5 wt %). The crystallinity, bonding behavior and disorder in the films were investigated with X-ray diffraction (XRD), Fourier transform infrared (FTIR), UV–visible and ellipsometry techniques, while surface morphology was studied using Atomic force microscopy (AFM). The nanocrystalline nature of PMMA is seen to be preserved in the blends although there are clear indications of bond modifications. The addition of PCTFE results in the improvement of overall crystallinity of the films via the interaction among PMMA and degraded PCTFE molecules when the films are casted from diluted solutions. In agreement, corresponding disorder in terms of Urbach energy shows a decreasing trend upon inclusion of more and more PCTFE molecules. Micro-Raman spectra are dominated by fluorescence background, which is proposed as arising from degraded PCTFE. Supporting this, FTIR spectra also shows modifications in bonding as a function of PCTFE percentage, but this bond modification is not enough to produce refractive index variation in the sample, which is dominated by the host PMMA contribution for all the PCTFE concentrations. The study suggests the useful range of PCTFE concentration in which PMMA host properties can be modified for optimizing optical and structural properties without much degradation of PCTFE. - Highlights: • PMMA blend films with varying PCTFE concentrations (1–5 wt%) were prepared. • Nanocrystalline nature of PMMA is preserved in spite of bond modifications. • Addition of PCTFE results in improvement of overall crystallinity of the films. • Urbach energy shows a decreasing Disorder upon inclusion of more PCTFE molecules. • FTIR spectra show bond modifications without changing refractive index.

  17. The influence of cement type and temperature on chloride binding in cement paste

    DEFF Research Database (Denmark)

    Jensen, Ole Mejlhede; Korzen, Migge Sofie Hoffmann; Skibsted, Jørgen

    1998-01-01

    This paper describes effects of cement type and temperature on chloride binding in cement paste, which is an important subject in relation to life-time modelling of reinforced concrete structures. The influence of cement type on chloride binding is investigated by substituting cement with pure...... cement clinker. Both theoretical considerations and experimental data for chloride binding in cement pastes are presented. A physico-chemically based model to describe the influence of temperature on physical binding of chloride is presented. Solid-state 27Al and 29Si magic-angle spinning (MAS) nuclear...... magnetic resonance (NMR) spectroscopy has been used for quantification of the anhydrous and hydrated aluminate and silicate phases in the chloride exposed cement pastes. The 27Al isotropic chemical shift and nuclear quadrupole coupling is reported for a synthetic sample of Friedel's salt, Ca2Al(OH)6Cl×2H2O....

  18. Feasibility of producing nano cement in a traditional cement factory in Iraq

    Directory of Open Access Journals (Sweden)

    Sada Abdalkhaliq Hasan Alyasri

    2017-12-01

    Full Text Available This study investigates the economic feasibility of producing nano cement through the establishment of a production line within an existing cement factory. Creating a nano cement production line within the Alkufa Cement factory in Iraq is selected as a case study. Evaluation measures including internal rate of return (IRR, net present value (NPV and breakeven point (BEP are used to evaluate the possible gain that can be achieved from this option. The results demonstrated a positive NPV. The IRR is found to be 26.8% and BEP is reached within 3 years after the establishment of the line. This indicates that producing nano cement in the existing cement factory is economically feasible and can be more advantageous than the ordinary cement.

  19. Is it cement to be? Downhole cement that uses zeolite additive may offer lightweight alternative

    Energy Technology Data Exchange (ETDEWEB)

    Mahoney, J.

    2001-05-01

    C2C Zeolite Corporation produces zeolites from a large deposit near Cache Creek, British Columbia, and processes them for use as an additive in downhole cement well casings. Early research indicates that zeolites can significantly improve the way downhole cement is made in the oil industry. Zeolites are made up mostly of silicates of aluminum and calcium. They have a great ability to absorb water, resulting in a lighter and more fluid cement than is currently available. C2C claims that zeolites will reduce cement weight, column pressure and operator costs. The cost benefits of using lighter cement downhole includes easier moving, processing and handling of the mix. Initial research suggests that zeolites might prove to be viable alternatives to other cement lighteners such as silica fumes or flyash. Zeolite-based cement also performed reasonably well in freeze-thaw tests and showed good adhesion and no evidence of shrinkage in downhole tests. 3 figs.

  20. Cements in radioactive waste management. Characterization requirements of cement products for acceptance and quality assurance purposes

    International Nuclear Information System (INIS)

    Rahman, A.A.; Glasser, F.P.

    1987-01-01

    Cementitious materials are used as immobilizing matrices for low (LLW) and medium-level wastes (MLW) and are also components of the construction materials in the secondary barriers and the repositories. This report has concerned itself with a critical assessment of the quality assurance aspects of the immobilization and disposal of MLW and LLW cemented wastes. This report has collated the existing knowledge of the use and potential of cementitious materials in radioactive waste immobilization and highlighted the physico-chemical parameters. Subject areas include an assessment of immobilization objectives and cement as a durable material, waste stream and matrix characterization, quality assurance concepts, nature of cement-based systems, chemistry and modelling of cement hydration, role and effect of blending agents, radwaste-cement interaction, assessment of durability, degradative and radiolytic processes in cements and the behaviour of cement-based matrices and their near-field interactions with the environment and the repository conditions

  1. Shrinkage Properties of Cement Stabilized Gravel

    DEFF Research Database (Denmark)

    Lund, Mia Schou Møller; Hansen, Kurt Kielsgaard

    2014-01-01

    Cement stabilized gravel is an attractive material in road construction because its strength prop-erties are accommodating the increasingly higher requirements to the bearing capacity of a base course. However, reflection cracking of cement stabilized gravel is a major concern. In this pa...

  2. Development and design of a cementation process

    International Nuclear Information System (INIS)

    Vicente, R.

    1986-01-01

    The conceptual design of a facility for the immobilization of intermediate level liquid waste in cement is presented. The cementation process adopted a vibration assisted mixing process. The solidified waste is packed in 200 litres drum with barite concrete lining. The waste package is classified as Type A package for transport. (Author) [pt

  3. Development and design of a cementation process

    International Nuclear Information System (INIS)

    Vicente, R.

    1987-01-01

    The conceptual design of a facility for the immobilization of intermediate-level liquid wastes in cement is presented. The cementation process adopted a vibration assisted mixing process. The solidified waste is packed in 200 litres drum with barite concrete lining. The waste package is classified as Type A package for transport. (Author) [pt

  4. Investigation of a Hardened Cement Paste Grout

    DEFF Research Database (Denmark)

    Esteves, Luis Pedro; Sørensen, Eigil Verner

    This report documents a series of tests performed on a hardened cement paste grout delivered by the client, Det Norske Veritas A/S.......This report documents a series of tests performed on a hardened cement paste grout delivered by the client, Det Norske Veritas A/S....

  5. Chloride ingress in cement paste and mortar

    DEFF Research Database (Denmark)

    Jensen, Ole Mejlhede; Hansen, Per Freiesleben; Coats, Alison M.

    1999-01-01

    In this paper chloride ingress in cement paste and mortar is followed by electron probe microanalysis. The influence of several paste and exposure parameters on chloride ingress are examined (e.g., water-cement ratio, silica fume addition, exposure time, and temperature), The measurements...

  6. Basic Chemistry for the Cement Industry.

    Science.gov (United States)

    Turner, Mason

    This combined student workbook and instructor's guide contains nine units for inplant classes on basic chemistry for employees in the cement industry. The nine units cover the following topics: chemical basics; measurement; history of cement; atoms; bonding and chemical formulas; solids, liquids, and gases; chemistry of Portland cement…

  7. Facial skeletal augmentation using hydroxyapatite cement.

    Science.gov (United States)

    Shindo, M L; Costantino, P D; Friedman, C D; Chow, L C

    1993-02-01

    This study investigates the use of a new calcium phosphate cement, which sets to solid, microporous hydroxyapatite, for facial bone augmentation. In six dogs, the supraorbital ridges were augmented bilaterally with this hydroxyapatite cement. On one side, the hydroxyapatite cement was placed directly onto the bone within a subperiosteal pocket. On the opposite side, the cement was contained within a collagen membrane tubule and then inserted into a subperiosteal pocket. The use of collagen tubules facilitated easy, precise placement of the cement. All implants maintained their original augmented height throughout the duration of the study. They were well tolerated without extrusion or migration, and there was no significant sustained inflammatory response. Histologic studies, performed at 3, 6, and 9 months revealed that when the cement was placed directly onto bone, progressive replacement of the implant by bone (osseointegration of the hydroxyapatite with the underlying bone) without a loss of volume was observed. In contrast, when the cement-collagen tubule combination was inserted, primarily a fibrous union was noted. Despite such fibrous union, the hydroxyapatite-collagen implant solidly bonded to the underlying bone, and no implant resorption was observed. Hydroxyapatite cement can be used successfully for the experimental augmentation of the craniofacial skeleton and may be applicable for such uses in humans.

  8. Elaborating the History of Our Cementing Societies

    DEFF Research Database (Denmark)

    Cao, Zhi; Shen, Lei; Løvik, Amund N.

    2017-01-01

    Modern cities and societies are built fundamentally based on cement and concrete. The global cement production has risen sharply in the past decades due largely to urbanization and construction. Here we deployed a top-down dynamic material flow analysis (MFA) model to quantify the historical deve...

  9. TECHNOLOGICAL CHANGES IN THE CEMENT MANUFACTURING INDUSTRY.

    Science.gov (United States)

    WESSON, CARL E.

    THE PURPOSE OF THIS STUDY IS TO PRESENT A PRELIMINARY PICTURE OF OCCUPATIONAL CHANGES BROUGHT ABOUT IN THE MANUFACTURE OF CEMENT AS A RESULT OF INTRODUCING AUTOMATED EQUIPMENT. ONE AUTOMATED AND SEVERAL CONVENTIONAL TYPE CEMENT PLANTS WERE STUDIED. ANALYSIS OF DATA OBTAINED THROUGH RESEARCH AND DATA COLLECTED DURING THE STUDY REVEALED THAT…

  10. Pre-portland cements and geopolymers

    Czech Academy of Sciences Publication Activity Database

    Hanzlíček, Tomáš; Perná, Ivana; Ertl, Z.; Miller, S.M.

    2012-01-01

    Roč. 9, č. 1 (2012), s. 57-62 ISSN 1214-9705 Institutional research plan: CEZ:AV0Z30460519 Keywords : caementum * cement itious * calcareous cement Subject RIV: JN - Civil Engineering Impact factor: 0.530, year: 2011 http://www.irsm.cas.cz/materialy/acta_content/2012_01/5_Hanzlicek.pdf

  11. Contact dermatitis in cement workers in Isfahan

    Directory of Open Access Journals (Sweden)

    Iraji Fariba

    2006-01-01

    Full Text Available BACKGROUND: Due to recent industrialization and inadequately protected workers or in other words poor supervision on constructive workers habits in our large city of Isfahan cement contact dermatitis is relatively high especially among cement factory workers and constructive personnel. PURPOSES: To investigate the prevalence rate of cement contact dermatitis in cement factory workers in Isfahan. METHODS: A case-control clinical study was carried out by randomly selecing 150 factory workders and 150 official clerks in a cement factory in Isfahan in 2001. After a complete physical examination, data was recorded in observational checklists. FINDINGS: The percentages of contact dermatitis prevalences in the first and the second groups were 22% and 5.3% respectively. About 60% of cement workers with contact dermatitis were between 30-40 years of age. There was a direct relationship with age in both groups of the workers. In the high-exposure group, the hand eczema along was 70% but in the other group the percentage of involvement was the same in exposed and unexposed anatomical areas. CONCLUSIONS: There was a direct relationship between occurrence and the severity of involvement and duration of contact in the first group. Cent percent of cement workers had contact dermatitis after 10 or less years, but the percentage among the other group was 35%. LIMITATION: Irritant contact dermatitis to cement has not been detected.

  12. Influence of cement compressive strength and porosity on augmentation performance in a model of orthopedic screw pull-out.

    Science.gov (United States)

    Pujari-Palmer, Michael; Robo, Celine; Persson, Cecilia; Procter, Philip; Engqvist, Håkan

    2018-01-01

    still produce a significant improvement in screw pull-out force. When the correlation strength of all the tested models were compared both cement porosity and compressive strength accurately predicted pull-out force (R 2 =1.00, R 2 =0.808), though prediction accuracy depended upon the strength of the material surrounding the Sawbone. The correlations strength was low for bone with no, or weak, cortical fixation (R 2 =0.56, 0.36). Higher strength and lower porosity CPCs also produced greater pull-out force (1-1.5kN) than commercial CPC (0.2-0.5kN), but lower pull-out force than PMMA (2-3kN). The results of this study suggest that the likelihood of screw fixation failure may be reduced by selecting calcium phosphate cements with lower porosity and higher compressive strength, in patients with healthy bone mineral density and/or sufficient cortical thickness. This is of particular clinical relevance when fixation with metal plates is indicated, or where the augmentation volume is limited. Copyright © 2017 Elsevier Ltd. All rights reserved.

  13. Synthesis of transparent ZnO/PMMA nanocomposite films through free-radical copolymerization of asymmetric zinc methacrylate acetate and in-situ thermal decomposition

    Energy Technology Data Exchange (ETDEWEB)

    Zhang Lin [Department of Chemistry, Nanchang University, 999 Xuefu Avenue, Nanchang 330031 (China); Institute of Polymers, Nanchang University, 999 Xuefu Avenue, Nanchang 330031 (China); Li Fan, E-mail: lfan@ncu.edu.cn [Institute of Polymers, Nanchang University, 999 Xuefu Avenue, Nanchang 330031 (China); Chen Yiwang, E-mail: ywchen@ncu.edu.cn [Department of Chemistry, Nanchang University, 999 Xuefu Avenue, Nanchang 330031 (China); Institute of Polymers, Nanchang University, 999 Xuefu Avenue, Nanchang 330031 (China); Wang Xiaofeng [Institute of Polymers, Nanchang University, 999 Xuefu Avenue, Nanchang 330031 (China)

    2011-08-15

    In this paper, a new and simple approach for in-situ preparation of transparent ZnO/poly(metyl methacrylate) (ZnO/PMMA) nanocomposite films was developed. Poly(methyl methacrylate)-co-poly(zinc methacrylate acetate) (PMMA-co-PZnMAAc) copolymer was synthesized via free-radical polymerization between methyl methacrylate (MMA) and zinc methacrylate acetate (ZnMAAc), where asymmetric ZnMAAc with only one terminal double bond (C=C) was applied to act as the precursor for ZnO nanocrystals and could avoid cross-link. Subsequently, transparent ZnO/PMMA nanocomposite films were obtained by in-situ thermal decomposition. Scanning electron microscope (SEM) image revealed that ZnO nanocrystals were homogeneously dispersed in PMMA matrix. With thermal decomposition time increasing, the absorption intensity in UV region and photoluminescence intensity of ZnO/PMMA nanocomposite films enhanced. However, the optical properties diminished when the thermal decomposition temperature increased. The TGA measurement displayed ZnO/PMMA nanocomposite films prepared by the in-situ synthesis method possessed better thermal stability compared with those prepared by the physical blending method and pristine PMMA films. - Highlights: > ZnO/PMMA hybrid films were prepared via free-radical polymerization and in-situ thermal decomposition. > ZnO NCs are homogeneously dispersed in the PMMA matrix and these films have good optical properties. > Thermal stability of these films is improved compared with those of physically blending ones.

  14. Synthesis of transparent ZnO/PMMA nanocomposite films through free-radical copolymerization of asymmetric zinc methacrylate acetate and in-situ thermal decomposition

    International Nuclear Information System (INIS)

    Zhang Lin; Li Fan; Chen Yiwang; Wang Xiaofeng

    2011-01-01

    In this paper, a new and simple approach for in-situ preparation of transparent ZnO/poly(metyl methacrylate) (ZnO/PMMA) nanocomposite films was developed. Poly(methyl methacrylate)-co-poly(zinc methacrylate acetate) (PMMA-co-PZnMAAc) copolymer was synthesized via free-radical polymerization between methyl methacrylate (MMA) and zinc methacrylate acetate (ZnMAAc), where asymmetric ZnMAAc with only one terminal double bond (C=C) was applied to act as the precursor for ZnO nanocrystals and could avoid cross-link. Subsequently, transparent ZnO/PMMA nanocomposite films were obtained by in-situ thermal decomposition. Scanning electron microscope (SEM) image revealed that ZnO nanocrystals were homogeneously dispersed in PMMA matrix. With thermal decomposition time increasing, the absorption intensity in UV region and photoluminescence intensity of ZnO/PMMA nanocomposite films enhanced. However, the optical properties diminished when the thermal decomposition temperature increased. The TGA measurement displayed ZnO/PMMA nanocomposite films prepared by the in-situ synthesis method possessed better thermal stability compared with those prepared by the physical blending method and pristine PMMA films. - Highlights: → ZnO/PMMA hybrid films were prepared via free-radical polymerization and in-situ thermal decomposition. → ZnO NCs are homogeneously dispersed in the PMMA matrix and these films have good optical properties. → Thermal stability of these films is improved compared with those of physically blending ones.

  15. Leach characterization of cement encapsulated wastes

    International Nuclear Information System (INIS)

    Roy, D.M.; Scheetz, B.E.; Wakeley, L.D.; Barnes, M.W.

    1982-01-01

    Matrix encapsulation of defense nuclear waste as well as intermediate-level commercial wastes within a low-temperature cementitious composite were investigated. The cements for this study included both as-received and modified calcium silicate and calcium aluminate cements. Specimens were prepared following conventional formulation techniques designed to produce dense monoliths, followed by curing at 60 0 C. An alternative preparation procedure is contrasted in which the specimens were ''warm'' pressed in a uniaxial press at 150 0 C at 50,000 psi for 0.5 h. Specimens of the waste/cement composites were leached in deionized water following three different procedures which span a wide range of temperatures and solution saturation conditions. Aluminate and compositionally adjusted silicate cements exhibited a better retentivity for Cs and Sr than did the as-received silicate cement. 15 refs

  16. Conditioning of radioactive waste solutions by cementation

    International Nuclear Information System (INIS)

    Vejmelka, P.; Rudolph, G.; Kluger, W.; Koester, R.

    1992-02-01

    For the cementation of the low and intermediate level evaporator concentrates resulting from the reprocessing of spent fuel numerous experiments were performed to optimize the waste form composition and to characterize the final waste form. Concerning the cementation process, properties of the waste/cement suspension were investigated. These investigations include the dependence of viscosity, bleeding, setting time and hydration heat from the waste cement slurry composition. For the characterization of the waste forms, the mechanical, thermal and chemical stability were determined. For special cases detailed investigations were performed to determine the activity release from waste packages under defined mechanical and thermal stresses. The investigations of the interaction of the waste forms with aqueous solutions include the determination of the Cs/Sr release, the corrosion resistance and the release of actinides. The Cs/Sr release was determined in dependence of the cement type, additives, setting time and sample size. (orig./DG) [de

  17. Energetically Modified Cement (EMC) - Performance Mechanism

    Energy Technology Data Exchange (ETDEWEB)

    Ronin, Vladimir; Elfgren, Lennart [Luleaa Univ. of Technology (Sweden). Centre for High Performance Cement

    2003-03-01

    Energetically Modified Cements, EMC, made of intensively milled cement (50%) and fillers (50%) of quartz or fly ash have been compared to blends of Ordinary Portland Cement, OPC, and fillers. The EMCs have better properties than other blends and are comparable to unblended OPC. This remarkable fact can probably be explained as follows. The grinding process reduces the size of both cement grains and fillers. This combined with the creation of micro defects gives the ground cement a very high degree of hydration. The increased early hydration and a better distribution of hydration products results in an extensive pore size refinement of the hardened binder. This pore size refinement leads to a favorably reduced permeability and diffusivity and very good mechanical properties.

  18. Cement analysis using d + D neutrons

    International Nuclear Information System (INIS)

    Womble, Phillip C.; Paschal, Jon; Moore, Ryan

    2005-01-01

    In the cement industry, the primary concern is quality control. The earlier the cement industry can institute quality control upon their product, the more significant their savings in labor, energy and material. We are developing a prototype cement analyzer using pulsed neutrons from a d-D electronic neutron generator with the goal of ensuring quality control of cement in an on-line manner. By utilizing a low intensity d-D neutron source and a specially-designed moderator assembly, we are able to produce one of the safest neutron-based systems in the market. Also, this design includes some exciting new methods of data acquisition which may substantially reduce the final installation costs. In our proof-of-principle measurements, we were able to measure the primary components of cement (Al, Si, Ca and Fe) to limits required for the raw materials, the derived mixes and the clinkers utilizing this neutron generator

  19. Dentin-cement Interfacial Interaction

    Science.gov (United States)

    Atmeh, A.R.; Chong, E.Z.; Richard, G.; Festy, F.; Watson, T.F.

    2012-01-01

    The interfacial properties of a new calcium-silicate-based coronal restorative material (Biodentine™) and a glass-ionomer cement (GIC) with dentin have been studied by confocal laser scanning microscopy (CLSM), scanning electron microscopy (SEM), micro-Raman spectroscopy, and two-photon auto-fluorescence and second-harmonic-generation (SHG) imaging. Results indicate the formation of tag-like structures alongside an interfacial layer called the “mineral infiltration zone”, where the alkaline caustic effect of the calcium silicate cement’s hydration products degrades the collagenous component of the interfacial dentin. This degradation leads to the formation of a porous structure which facilitates the permeation of high concentrations of Ca2+, OH-, and CO32- ions, leading to increased mineralization in this region. Comparison of the dentin-restorative interfaces shows that there is a dentin-mineral infiltration with the Biodentine, whereas polyacrylic and tartaric acids and their salts characterize the penetration of the GIC. A new type of interfacial interaction, “the mineral infiltration zone”, is suggested for these calcium-silicate-based cements. PMID:22436906

  20. Cement and concrete options paper

    International Nuclear Information System (INIS)

    1999-10-01

    Greenhouse gas emissions associated with the production of concrete are projected to increase from 10.5 million tonnes in 1990 to almost 14 million tonnes in 2010. Over half of this amount will be non-energy related emissions of carbon dioxide resulting from the conversion of limestone to lime. According to this report by industry experts, the industry has an excellent record of improving energy efficiency and there are few easy gains remaining. Nevertheless, improvements in energy efficiency and fuel use, increased use of concrete where it can be shown to result in net reduction of GHG emissions, and partial replacement of cement by supplementary cementitious materials that involve no additional generation of GHGs, could yield an approximate reduction in carbon dioxide emissions of nearly seven million tons in 2010. The industry proposes three measures to realise these benefits: (1) encouraging replacement of fossil fuels by otherwise waste material, (2) encouraging increased use of concrete in constructing houses and roads, and (3) encouraging increased use of supplementary cementing materials. The industry is opposed to carbon or energy taxes that increase the cost of doing business, on the grounds that such taxes would adversely affect the industry's competitive position internationally. tabs

  1. Chemical alteration of cement hydrates by dissolution

    International Nuclear Information System (INIS)

    Sugiyama, Daisuke; Fujita, Tomonari; Nakanishi, Kiyoshi

    2000-01-01

    Cementitious material is a potential waste packaging and backfilling material for the radioactive waste disposal, and is expected to provide both physical and chemical containment. In particular, the sorption of radionuclides onto cementitious material and the ability to provide a high pH condition are very important parameters when considering the release of radionuclides from radioactive wastes. For the long term, in the geological disposal environment, cement hydrates will be altered by, for example, dissolution, chemical reaction with ions in the groundwater, and hydrothermal reaction. Once the composition or crystallinity of the constituent minerals of a cement hydrate is changed by these processes, the pH of the repository buffered by cementitious material and its sorption ability might be affected. However, the mechanism of cement alteration is not yet fully understood. In this study, leaching experiments of some candidate cements for radioactive waste disposal were carried out. Hydrated Ordinary Portland Cement (OPC), Blast Furnace Slag blended cement (OPC/BFS) and Highly containing Flyash and Silicafume Cement (HFSC) samples were contacted with distilled water at liquid:solid ratios of 10:1, 100:1 and 1000:1 at room temperature for 200 days. In the case of OPC, Ca(OH) 2 dissolved at high liquid:solid ratios. The specific surface area of all cement samples increased by leaching process. This might be caused by further hydration and change of composition of constituent minerals. A model is presented which predicts the leaching of cement hydrates and the mineral composition in the hydrated cement solid phase, including the incongruent dissolution of CSH gel phases and congruent dissolution of Ca(OH) 2 , Ettringite and Hydrotalcite. Experimental results of dissolution of Ca-O-H and Ca-Si-O-H phases were well predicted by this model. (author)

  2. CONCRETE BASED ON MODIFIED DISPERSE CEMENT SYSTEM

    Directory of Open Access Journals (Sweden)

    D. V. Rudenko

    2016-08-01

    Full Text Available Purpose. The article considers definition of the bond types occurring in a modified cement concrete matrix, and the evaluation of the quality of these links in a non-uniform material to determine the geometrical and physical relationships between the structure and the cement matrix modifiers. Methodology. To achieve this purpose the studies covered the microstructure of dispersed modified concrete cement matrix, the structure formation mechanism of the modified cement concrete system of natural hardening; as well as identification of the methods of sound concrete strength assessment. Findings. The author proposed a model of the spatial structure of the concrete cement matrix, modified by particulate reinforcement crystal hydrates. The initial object of study is a set of volume elements (cells of the cement matrix and the system of the spatial distribution of reinforcing crystallohydrates in these volume elements. It is found that the most dangerous defects such as cracks in the concrete volume during hardening are formed as a result of internal stresses, mainly in the zone of cement matrix-filler contact or in the area bordering with the largest pores of the concrete. Originality. The result of the study is the defined mechanism of the process of formation of the initial strength and stiffness of the modified cement matrix due to the rapid growth of crystallohydrates in the space among the dispersed reinforcing modifier particles. Since the lack of space prevents from the free growth of crystals, the latter cross-penetrate, forming a dense structure, which contributes to the growth of strength. Practical value. Dispersed modifying cement matrix provides a durable concrete for special purposes with the design performance characteristics. The developed technology of dispersed cement system modification, the defined features of its structure formation mechanism and the use of congruence principle for the complex of technological impacts of physical

  3. Influence of the PMMA and the ISO slab phantom for calibrating personal dosemeters

    International Nuclear Information System (INIS)

    Ginjaume, M.; Ortega, X.; Barbosa, A.

    2000-01-01

    Wide agreement has been achieved among the main Bodies and Organisations involved in standardisation of radiation protection, related to the operational quantities for personal dosimetry. Since their definition in 1985, several reports have been published to clarify and define the experimental set up to be used for the calibration of dosemeters in terms of the above-mentioned quantities. Among these lines, ICRU 47 has listed five different phantoms that are used for calibration and whose results were accurate, within accepted uncertainties. However, to achieve uniformity in calibration procedures, the 30 cm x 30 cm x 15 cm PMMA slab phantom was recommended. The secondary calibration Laboratory from the Institut de Techniques Energetiques at the Technical University of Catalonia (UPC) agreed with the Spanish Nacional Laboratory to adopt the recommended PMMA phantom but to improve the accuracy of the calibration procedure, by introducing a correction factor for backscatter differences in a PMMA and an ICRU slab phantom. Such corrections were of the order of 8% for the low-energy X-ray qualities. Recently, ISO in ISO 4037-3, has proposed the ISO water slab phantom which consists of a 30 cm x 30 cm x 15 cm water phantom with PMMA walls (front wall 2.5 mm thick). This new phantom could be substituted by the above mentioned PMMA phantom for radiation qualities with mean energy equal or above that of 137 Cs. The aim of this work is to compare the influence of both phantoms when calibrating personal dosemeters with photons. A set of four TL personal dosemeters that are used in the UPC personal dosimetry Service and an electronic personal dosemeter (SIEMENS EPD-2) were calibrated in terms of H p (10) and H p (0.07) using the two proposed phantoms. Calibration factors for ISO X-ray narrow spectra, 137 Cs and 60 Co were experimentally obtained for each phantom and compared. In the TL measurements, differences were found to be within TL statistical uncertainty, provided that a

  4. Facile synthesis of monodisperse superparamagnetic Fe{sub 3}O{sub 4}/PMMA composite nanospheres with high magnetization

    Energy Technology Data Exchange (ETDEWEB)

    Lan Fang; Liu Kexia; Jiang Wen; Zeng Xiaobo; Wu Yao; Gu Zhongwei, E-mail: Yaowu_amanda@126.com, E-mail: zwgu@scu.edu.cn [National Engineering Research Center for Biomaterials, Sichuan University, Chengdu 610064 (China)

    2011-06-03

    Monodisperse superparamagnetic Fe{sub 3}O{sub 4}/polymethyl methacrylate (PMMA) composite nanospheres with high saturation magnetization were successfully prepared by a facile novel miniemulsion polymerization method. The ferrofluid, MMA monomer and surfactants were co-sonicated and emulsified to form stable miniemulsion for polymerization. The samples were characterized by DLS, TEM, FTIR, XRD, TGA and VSM. The diameter of the Fe{sub 3}O{sub 4}/PMMA composite nanospheres by DLS was close to 90 nm with corresponding polydispersity index (PDI) as small as 0.099, which indicated that the nanospheres have excellent homogeneity in aqueous medium. The TEM results implied that the Fe{sub 3}O{sub 4}/PMMA composite nanospheres had a perfect core-shell structure with about 3 nm thin PMMA shells, and the core was composed of many homogeneous and closely packed Fe{sub 3}O{sub 4} nanoparticles. VSM and TGA showed that the Fe{sub 3}O{sub 4}/PMMA composite nanospheres with at least 65% high magnetite content were superparamagnetic, and the saturation magnetization was as high as around 39 emu g{sup -1} (total mass), which was only decreased by 17% compared with the initial bare Fe{sub 3}O{sub 4} nanoparticles.

  5. The improvement of the mechanical properties of PMMA denture base by Al2O3 particles with nitrile rubber

    Science.gov (United States)

    Alhareb, Ahmed Omran; Akil, Hazizan Md; Ahmad, Zainal Arifin

    2017-07-01

    Poly methyl methacrylate (PMMA) is mostly used for fabrication of denture base by heat-curing technique. Therefore, the purpose of this study is to investigate the effect of Al2O3 filler as toughening particles together with nitrile butadiene rubber (NBR) particles as impact modifier were used to reinforce PMMA denture base materials on the impact strength (IS) and fracture toughness (KIC). PMMA powder was mixed with liquid methyl methacrylate (MMA) and ethylene glycol dimethacrylate (EGDMA) as crosslinking agent. The powder components are PMMA, benzoyl peroxide, NBR (5, 7.5 and 10 wt%), and Al2O3 filler (5 wt%) treated by silane. The liquid components are 90% of methyl methacrylate and 10 % ethylene glycol dimethacryate. FTIR analyses confirmed that the Al2O3 filler was successfully treated with silane as coupling agent. The morphology of fracture surfaces was characterized using field emission scanning electron microscopy (FESEM). The results shown that IS and KIC improved significantly when using treated the Al2O3 filler. IS has increased to 56% (8.26 KJ/m2) and 73% (2.77 MPa.m1/2) for KIC when treated Al2O3 filler compared to unreinforced PMMA matrix. Statistical analyses of data results were significantly improved (PNBR with treated Al2O3 filler compared to other the compositions.

  6. Investigation of the ferroelectric switching behavior of P(VDF-TrFE)-PMMA blended films for synaptic device applications

    International Nuclear Information System (INIS)

    Kim, E J; Kim, K A; Yoon, S M

    2016-01-01

    Synaptic plasticity can be mimicked by electronic synaptic devices. By using ferroelectric thin films as gate insulator for thin-film transistors (TFT), channel conductance can be defined as the synaptic plasticity, and gradually modulated by the variations in amounts of aligned ferroelectric dipoles. Poly(vinylidene fluoride-trifluoroethylene) [P(VDF-TrFE)]-poly(methyl methacrylate) (PMMA) blended films are chosen and their switching kinetics are investigated by using the Kolmogorov-Avrami-Ishibashi model. The switching time for ferroelectric polarization is sensitively influenced by the amplitude of applied electric field and volumetric ratio of ferroelectric beta-phases in the P(VDF-TrFE)-PMMA films. The switching time of the P(VDF-TrFE) increases with decreasing the pulse amplitude and/or the ratio of ferroelectric beta-phases by incorporation of PMMA. The activation electric field is also found to increase as the increase in blended amount of PMMA. Synapse TFTs are fabricated using the P(VDF-TrFE)-PMMA as gate insulator and In-Ga-Zn-O active channels. The drain currents of the synapse TFTs gradually increased when the voltage pulse signals with given duration are repeatedly applied. This suggests that the synaptic weights can be modulated by the number of external pulse signals, and that the proposed synapse TFT can be applied for mimicking the operations of bio-synapses. (paper)

  7. Effect of plasma fluorination variables on the deposition and growth of partially fluorinated polymer over PMMA films

    Directory of Open Access Journals (Sweden)

    Giovana da Silva Padilha

    2013-01-01

    Full Text Available In this work, an investigation was made of the modification of film surface of Poly(methylmethacrylate (PMMA using the plasma polymerization technique. PMMA films 10 µm thick were obtained by Spin-Coating starting from a chloroform solution (15.36% w/w. The films were exposed to the plasma of CHF3 at different gas pressures and exposure times to increase the thickness of fluorinated polymers onto PMMA films. The plasma fluorinated optical films were characterized by gravimetry, FTIR-ATR, contact angle of wetting, SEM and AFM. The surface fluorination of PMMA films can be inferred by the increase in contact angle under all experimental conditions, and confirmed with FTIR-ATR analysis. Gravimetry showed an increase of the fluorinated polymer layer over PMMA films, being 1.55 µm thick at 0.7 torr and 40 minutes of plasma exposure. The SEM analysis showed a well-defined layer of fluorinated polymer, with fluorine being detected in the EDS analysis. The film roughness for the fluorinated polymers was around of 200 Å, quite satisfactory for a 1.55 µm cladding.

  8. Tuning the Interfacial Mechanical Behaviors of Monolayer Graphene/PMMA Nanocomposites.

    Science.gov (United States)

    Wang, Guorui; Dai, Zhaohe; Liu, Luqi; Hu, Hai; Dai, Qing; Zhang, Zhong

    2016-08-31

    The van der Waals (vdW) force dominated interface between graphene and polymer matrix creates weak points in the mechanical sense. Chemical functionalization was expected to be an effective approach in transfer of the outstanding performance of graphene across multiple length scales up to the macroscopic level, due to possible improvements in the interfacial adhesion. However, published works showed the contradiction that improvements, insensitivity, or even worsening of macro-mechanical performance have all been reported in graphene-based polymer nanocomposites. Particularly central cause of such discrepancy is the variations in graphene/polymer interfacial chemistry, which is critical in nanocomposites with vast interfacial area. Herein, O3/H2O gaseous mixture was utilized to oxidize monolayer graphene sheet with controlled functionalization degrees. Hydrogen bonds (H bonds) are expected to form between oxidized graphene sheet/poly(methyl methacrylate) (PMMA) at the interface. On the basis of in situ tensile-micro Raman spectroscopy, the impacts of bonding types (vdW and H-bonds) on both key interfacial parameters (such as interfacial shear strength and critical length) and failure modes of graphene/PMMA nanocomposite were clarified for the first time at the microscopic level. Our results show that owing to improved interfacial interaction via H bonds, the interface tends to be stiffening and strengthening. Moreover, the mechanical properties of the functionalized graphene/PMMA interface will be set by the competition between the enhanced interfacial adhesion and the degraded elastic modulus of graphene, which was caused by structural defects in the graphene sheet during the functionalization process and could lead to catastrophic failure of graphene sheets in our experimental observation. Our results will be helpful to design various nanofiller-based nanocomposites with high mechanical performance.

  9. Microscale Investigation of Arsenic Distribution and Species in Cement Product from Cement Kiln Coprocessing Wastes

    Directory of Open Access Journals (Sweden)

    Yufei Yang

    2013-01-01

    Full Text Available To improve the understanding of the immobilization mechanism and the leaching risk of Arsenic (As in the cement product from coprocessing wastes using cement kiln, distribution and species of As in cement product were determined by microscale investigation methods, including electron probe microanalysis (EPMA and X-ray absorption spectroscopy. In this study, sodium arsenate crystals (Na3AsO412H2O were mixed with cement production raw materials and calcined to produce cement clinker. Then, clinker was mixed water to prepare cement paste. EPMA results showed that As was generally distributed throughout the cement paste. As content in calcium silicate hydrates gel (C-S-H was in low level, but higher than that in other cement mineral phases. This means that most of As is expected to form some compounds that disperse on the surfaces of cement mineral phases. Linear combination fitting (LCF of the X-ray absorption near edge structure spectra revealed that As in the cement paste was predominantly As(V and mainly existed as Mg3(AsO42, Ca3(AsO42, and Na2HAsO4.

  10. Cement-in-cement acetabular revision with a constrained tripolar component.

    Science.gov (United States)

    Leonidou, Andreas; Pagkalos, Joseph; Luscombe, Jonathan

    2012-02-17

    Dislocation of a total hip replacement (THR) is common following total hip arthroplasty (THA). When nonoperative management fails to maintain reduction, revision surgery is considered. The use of constrained acetabular liners has been extensively described. Complete removal of the old cement mantle during revision THA can be challenging and is associated with significant complications. Cement-in-cement revision is an established technique. However, the available clinical and experimental studies focus on femoral stem revision. The purpose of this study was to present a case of cement-in-cement acetabular revision with a constrained component for recurrent dislocations and to investigate the current best evidence for this technique. This article describes the case of a 74-year-old woman who underwent revision of a Charnley THR for recurrent low-energy dislocations. A tripolar constrained acetabular component was cemented over the primary cement mantle following removal of the original liner by reaming, roughening the surface, and thoroughly irrigating and drying the primary cement. Clinical and radiological results were good, with the Oxford Hip Score improving from 11 preoperatively to 24 at 6 months postoperatively. The good short-term results of this case and the current clinical and biomechanical data encourage the use of the cement-in-cement technique for acetabular revision. Careful irrigation, drying, and roughening of the primary surface are necessary. Copyright 2012, SLACK Incorporated.

  11. Detecting Poor Cement Bonding and Zonal Isolation Problems Using Magnetic Cement Slurries

    KAUST Repository

    Nair, Sriramya D.; Patzek, Tadeusz; van Oort, Eric

    2017-01-01

    There has been growing interest in the use of magnetorheological fluids to improve displacement efficiency of fluids (drilling fluids, spacer fluids, cement slurries) in the eccentric casing annuli. When magnetic particles are mixed with the cement slurry for improved displacement, they provide an excellent opportunity for sensing the presence and quality of cement in the annulus. This work focuses on using sophisticated 3D computational electromagnetics to simulate the use of a magnetic cement slurry for well cement monitoring. The main goal is to develop a new tool, which is capable of locating magnetic cement slurry that is placed behind a stainless steel casing. An electromagnetic coil was used to generate a magnetic field inside the borehole. It was found that when a current was passed through the electric coils, magnetic field lines passed through the stainless steel casing, the cement annulus and the rock formation. Three sensors were placed inside the cased borehole and the magnetic field strength variations were observed at these locations. Various factors that have a significant influence on zonal isolation were considered. These include, effect of debonding between casing and cement annulus, effect of changing annuli thickness, influence of a fracture in the rock formation, effect of changing magnetic permeability of cement and finally influence of annuli eccentricity. Based on the results shown in the paper along with the next generation of supersensitive magnetic sensors that are being developed, the magnetic approach appears to be a viable alternative for evaluating the quality of the cement annulus to ensure good zonal isolation.

  12. Sustainable Development of the Cement Industry and Blended Cements to Meet Ecological Challenges

    Directory of Open Access Journals (Sweden)

    Konstantin Sobolev

    2003-01-01

    Full Text Available The world production of cement has greatly increased in the past 10 years. This trend is the most significant factor affecting technological development and the updating of manufacturing facilities in the cement industry. Existing technology for the production of cement clinker is ecologically damaging; it consumes much energy and natural resources and also emits pollutants. A new approach to the production of blended or high-volume mineral additive (HVMA cement helps to improve its ecological compatibility. HVMA cement technology is based on the intergrinding of portland cement clinker, gypsum, mineral additives, and a special complex admixture. This new method increases the compressive strength of ordinary cement, improves durability of the cement-based materials, and - at the same time - uses inexpensive natural mineral additives or industrial by-products. This improvement leads to a reduction of energy consumption per unit of the cement produced. Higher strength, better durability, reduction of pollution at the clinker production stage, and decrease of landfill area occupied by industrial by-products, all provide ecological advantages for HVMA cement.

  13. Detecting Poor Cement Bonding and Zonal Isolation Problems Using Magnetic Cement Slurries

    KAUST Repository

    Nair, Sriramya D.

    2017-10-02

    There has been growing interest in the use of magnetorheological fluids to improve displacement efficiency of fluids (drilling fluids, spacer fluids, cement slurries) in the eccentric casing annuli. When magnetic particles are mixed with the cement slurry for improved displacement, they provide an excellent opportunity for sensing the presence and quality of cement in the annulus. This work focuses on using sophisticated 3D computational electromagnetics to simulate the use of a magnetic cement slurry for well cement monitoring. The main goal is to develop a new tool, which is capable of locating magnetic cement slurry that is placed behind a stainless steel casing. An electromagnetic coil was used to generate a magnetic field inside the borehole. It was found that when a current was passed through the electric coils, magnetic field lines passed through the stainless steel casing, the cement annulus and the rock formation. Three sensors were placed inside the cased borehole and the magnetic field strength variations were observed at these locations. Various factors that have a significant influence on zonal isolation were considered. These include, effect of debonding between casing and cement annulus, effect of changing annuli thickness, influence of a fracture in the rock formation, effect of changing magnetic permeability of cement and finally influence of annuli eccentricity. Based on the results shown in the paper along with the next generation of supersensitive magnetic sensors that are being developed, the magnetic approach appears to be a viable alternative for evaluating the quality of the cement annulus to ensure good zonal isolation.

  14. Processing influence on the morphology of PVDF/PMMA blends examined by scanning electron microscopy

    International Nuclear Information System (INIS)

    Freire, Estevao; Forte, Maria M.C.; Monteiro, Elisabeth E.C.

    2011-01-01

    PVDF/PMMA blends were melt blended in proportions of 20, 40 e 60% PVDF by weight in two different mixers, a low shear and a high shear mixer. The compositions obtained were examined by scanning electron microscopy. The results were correlated with the two types of processing and showed that the type of mixer affects the morphology of the blend. The morphologies obtained corroborated the NMR analysis demonstrating the phase separation phenomena and the effect of the type of mixer used in this study. (author)

  15. Characterization of three types of plastic detectors containing PMMA for nuclear dosimetry

    International Nuclear Information System (INIS)

    Abdelmalek, Adel

    2008-01-01

    The characterization of the dosimeters Harwell PMMA is an essential procedure in industrial dosimetry. It comprises studies of stability in the short and medium term, calibration and fractionation of amounts. Measurements were taken in specific term of absorbance by using a spectrophotometer UV-Screw and a thickness gauge. The results obtained present the calibration curves of these sensors, the time of stability post-irradiation corresponding for the reading of the dosimeters as well as the effect of fractionation of amount on the response of the dosimeters. These results are based on a suitable metrological study of the realised experiments. (Author)

  16. BDK-doped core microstructured PMMA optical fiber for effective Bragg grating photo-inscription

    DEFF Research Database (Denmark)

    Hu, Xuehao; Woyessa, Getinet; Kinet, Damien

    2017-01-01

    An endlessly single-mode doped microstructured poly(methyl methacrylate) (PMMA) optical fiber is produced for effective fiber Bragg grating (FBG) photo-inscription by means of a 400 nm femtosecond pulsed laser and the phase mask technique. The fiber presents a uniform benzyl dimethyl ketal (BDK......) distribution in its core without drastic loss increase. It was produced using the selected center hole doping technique, and the BDK dopant acts as a photoinitiator. In this Letter, we report a rapidly growing process of the grating reflection band. For an 11 mW mean laser power, the FBG reflectivity reaches...

  17. BDK-doped core microstructured PMMA optical fiber for effective Bragg grating photo-inscription.

    Science.gov (United States)

    Hu, Xuehao; Woyessa, Getinet; Kinet, Damien; Janting, Jakob; Nielsen, Kristian; Bang, Ole; Caucheteur, Christophe

    2017-06-01

    An endlessly single-mode doped microstructured poly(methyl methacrylate) (PMMA) optical fiber is produced for effective fiber Bragg grating (FBG) photo-inscription by means of a 400 nm femtosecond pulsed laser and the phase mask technique. The fiber presents a uniform benzyl dimethyl ketal (BDK) distribution in its core without drastic loss increase. It was produced using the selected center hole doping technique, and the BDK dopant acts as a photoinitiator. In this Letter, we report a rapidly growing process of the grating reflection band. For an 11 mW mean laser power, the FBG reflectivity reaches 83% in only 40 s.

  18. Parameters of Alumina Cement and Portland Cement with Addition of Chalcedonite Meal

    Science.gov (United States)

    Kotwa, Anna

    2017-10-01

    Aluminous cement is a quick binder with special properties. It is used primarily to make non-standard monolithic components exposed to high temperatures, + 1300°C. It is also a component of adhesives and mortars. It has a very short setting time. It is characterized by rapid increase in mechanical strength and resistance to aggressive sulphates. It can be used in reinforced concrete structures. Laying of concrete, construction mortar made of alumina cement can be carried out even at temperatures of -10°C. This article discusses a comparison of the parameters of hardened mortar made of alumina cement GÓRKAL 40 and Portland cement CEM I 42.5R. The mortars contain an addition of chalcedonite meal with pozzolanic properties, with particle size of less than 0.063μm. The meal was added in amounts of 5% and 20% of cement weight. Chalcedonite meal used in the laboratory research is waste material, resulting from chalcedonite aggregate mining. It has the same properties as the rock from which it originates. We have compared the parameters of hardened mortar i.e. compressive strength, water absorption and capillarity. The addition of 20% chalcedonite meal to mortars made from aluminous cement will decrease durability by 6.1% relative to aluminous cement mortar without addition of meal. Considering the results obtained during the absorbency tests, it can be stated that the addition of chalcedonite meal reduces weight gains in mortars made with cement CEM I 42.5 R and alumina cement. Use of alumina cement without addition of meal in mortars causes an increase of mass by 248% compared to Portland cement mortars without additions, in the absorption tests. The addition of chalcedonite meal did not cause increased weight gain in the capillary action tests. For the alumina cement mortars, a lesser weight gains of 24.7% was reported, compared to the Portland cement mortar after 28 days of maturing.

  19. Environmental Assessment of Different Cement Manufacturing ...

    Science.gov (United States)

    Due to its high environmental impact and energy intensive production, the cement industry needs to adopt more energy efficient technologies to reduce its demand for fossil fuels and impact on the environment. Bearing in mind that cement is the most widely used material for housing and modern infrastructure, the aim of this paper is to analyse the Emergy and Ecological Footprint of different cement manufacturing processes for a particular cement plant. There are several mitigation measures that can be incorporated in the cement manufacturing process to reduce the demand for fossil fuels and consequently reduce the CO2 emissions. The mitigation measures considered in this paper were the use of alternative fuels and a more energy efficient kiln process. In order to estimate the sustainability effect of the aforementioned measures, Emergy and Ecological Footprint were calculated for four different scenarios. The results show that Emergy, due to the high input mass of raw material needed for clinker production, stays at about the same level. However, for the Ecological Footprint, the results show that by combining the use of alternative fuels together with a more energy efficient kiln process, the environmental impact of the cement manufacturing process can be lowered. The research paper presents an analysis of the sustainability of cement production , a major contributor to carbon emissions, with respect to using alternative fuels and a more efficient kiln. It show

  20. Correlating cement characteristics with rheology of paste

    International Nuclear Information System (INIS)

    Vikan, H.; Justnes, H.; Winnefeld, F.; Figi, R.

    2007-01-01

    The influence of cement characteristics such as cement fineness and clinker composition on the 'flow resistance' measured as the area under the shear stress-shear rate flow curve has been investigated. Three different types of plasticizers namely naphthalene sulphonate-formaldehyde condensate, polyether grafted polyacrylate, and lignosulphonate have been tested in this context on 6 different cements. The flow resistance correlated well with the cement characteristic (Blaine.{d.cC 3 A + [1 - d].C 3 S}) where the factor d represents relative reactivity of cubic C 3 A and C 3 S while cC 3 A and C 3 S represent the content of these minerals. It was found to be either a linear or exponential function of the combined cement characteristic depending on plasticizer type and dosage. The correlation was valid for a mix of pure cement and cement with fly ash, limestone filler (4%), as well as pastes with constant silica fume dosage, when the mineral contents were determined by Rietveld analysis of X-ray diffractograms

  1. Effect of Cement Grades on some properties of Sandcrete ...

    African Journals Online (AJOL)

    The purpose of this study is to investigate the effects of cement grade on some properties of sandcrete. The cement used for this work was Ordinary Portland cement (Dangote brand) of grade 42.5 and 32.5 meeting the requirement of ASTM C150 type 1 cement. Three types of fine aggregate was also used to produce ...

  2. Energy economy and industrial ecology in the Brazilian cement sector

    International Nuclear Information System (INIS)

    Tavares, Marina Elisabete Espinho; Schaeffer, Roberto

    1999-01-01

    The article discusses the following issues of the Brazilian cement sector: the Brazilian cement main types specification, cement quantities evolution produced in Brazil from 1987 to 1997, energy conservation in the cement production process with additives, energy economy cost estimates from the utilization of additives, and several technologies energy economy cost used in the industrial sector

  3. Synthesis and Characterization of the in Situ Bulk Polymerization of PMMA Containing Graphene Sheets Using Microwave Irradiation

    Directory of Open Access Journals (Sweden)

    Mohammad A. Aldosari

    2013-03-01

    Full Text Available Polymethylmethacrylate–graphene (PMMA/RGO nanocomposites were prepared via in situ bulk polymerization using two different preparation techniques. In the first approach, a mixture of graphite oxide (GO and methylmethacrylate monomers (MMA were polymerized using a bulk polymerization method with a free radical initiator. After the addition of the reducing agent hydrazine hydrate (HH, the product was reduced via microwave irradiation (MWI to obtain R-(GO-PMMA composites. In the second approach, a mixture of graphite sheets (RGO and MMA monomers were polymerized using a bulk polymerization method with a free radical initiator to obtain RGO-(PMMA composites. The composites were characterized by FTIR, 1H-NMR and Raman spectroscopy and XRD, SEM, TEM, TGA and DSC. The results indicate that the composite obtained using the first approach, which involved MWI, had a better morphology and dispersion with enhanced thermal stability compared with the composites prepared without MWI.

  4. Fast bragg grating inscription in PMMA polymer optical fibres: Impact of thermal pre-treatment of preforms

    DEFF Research Database (Denmark)

    Marques, Carlos A. F.; Pospori, Andreas; Demirci, Gökhan

    2017-01-01

    In this work, fibre Bragg gratings (FBGs) were inscribed in two different undoped poly- (methyl methacrylate) (PMMA) polymer optical fibres (POFs) using different types of UV lasers and their inscription times, temperature and strain sensitivities are investigated. The POF Bragg gratings (POFBGs......) were inscribed using two UV lasers: a continuous UV HeCd @325 nm laser and a pulsed UV KrF @248 nm laser. Two PMMA POFs are used in which the primary and secondary preforms (during the two-step drawing process) have a different thermal treatment. The PMMA POFs drawn in which the primary or secondary...... preform is not specifically pre-treated need longer inscription time than the fibres drawn where both preforms have been pre-annealed at 80 °C for 2 weeks. Using both UV lasers, for the latter fibre much less inscription time is needed compared to another homemade POF. The properties of a POF fabricated...

  5. PMMA to SU-8 bonding for polymer based lab-on-a-chip systems with integrated optics

    DEFF Research Database (Denmark)

    Olsen, Brian Bilenberg; Nielsen, Theodor; Clausen, Bjarne Hans

    2004-01-01

    We present an adhesive bonding technique developed for SU-8 based "lab-on-a-chip"- systems with integrated optical components. Microfluidic channels and optical components (e.g. wave-guides) are defined in SU-8 photoresist on a Pyrex glass substrate. The microfluidic channels are sealed by a second...... Pyrex substrate, bonded on top of the cross-linked SU-8 structure using an inter- mediate layer of 950K molecular weight poly-methylmethacrylate (PMMA). Due to a lower refractive index of PMMA, this bonding technique offers optical waveguiding in the SU-8 structures in combination with good sealing...... of the microfluidic channels. The bonding technique is investigated with respect to bonding temperature in the range of 50 - 150 degr. C and at bonding forces of 1000 N and 2000 N on a 4-inch wafer. A maximum bonding strength of 16 MPa is achieved for the PMMA to SU-8 bonding at a bonding temperature of 110 degr. C...

  6. Thermal behavior of asphalt cements

    International Nuclear Information System (INIS)

    Claudy, P.M.; Letoffe, J.M.; Martin, D.; Planche, J.P.

    1998-01-01

    Asphalt cements are highly complex mixtures of hydrocarbon molecules whose thermal behavior is of prime importance for petroleum and road industry. From DSC, the determination of several thermal properties of asphalts is given, e.g. glass-transition temperature and crystallized fraction content.The dissolution of a pure n-paraffin C n H 2n+2 in an asphalt, as seen by DSC, should be a single peak. For 20 g of these glasses change with time and temperature. The formation of the crystallized phases is superposed to the enthalpic relaxation of the glasses, making a kinetic study very difficult. (Copyright (c) 1998 Elsevier Science B.V., Amsterdam. All rights reserved.)

  7. Operating experience with KRAFTWERK UNION cementation line

    International Nuclear Information System (INIS)

    Podmaka, L.; Tomik, L.

    1988-01-01

    A facility is described designed for fixation in a cement matrix of the radioactive concentrate produced by thickening waste water from the Bohunice nuclear power plant. The cementation line output is 0.6 m 3 concentrate/h. The concentrate is put in 200 l drums. The individual operating units, cement management, air conditioning, dosimetric monitoring and the building part are described. The requirements for the operators and the assessment of the quality of raw materials and the product are discussed. (M.D.). 3 figs., 4 refs

  8. Synthesis of pure Portland cement phases

    DEFF Research Database (Denmark)

    Wesselsky, Andreas; Jensen, Ole Mejlhede

    2009-01-01

    Pure phases commonly found in Portland cement clinkers are often used to test cement hydration behaviour in simplified experimental conditions. The synthesis of these phases is covered in this paper, starting with a description of phase relations and possible polymorphs of the four main phases...... in Portland cement, i.e. tricalcium silicate, dicalcium silicate, tricalcium aluminate and tetracalcium alumino ferrite. Details of the The process of solid state synthesis are is described in general including practical advice on equipment and techniques. Finally In addition, some exemplary mix compositions...

  9. Estimation and measurement of porosity change in cement paste

    International Nuclear Information System (INIS)

    Lee, Eunyong; Jung, Haeryong; Kwon, Ki-jung; Kim, Do-Gyeum

    2011-01-01

    Laboratory-scale experiments were performed to understand the porosity change of cement pastes. The cement pastes were prepared using commercially available Type-I ordinary Portland cement (OPC). As the cement pastes were exposed in water, the porosity of the cement pastes sharply increased; however, the slow decrease of porosity was observed as the dissolution period was extended more than 50 days. As expected, the dissolution reaction was significantly influenced by w/c ratio and the ionic strength of solution. A thermodynamic model was applied to simulate the porosity change of the cement pastes. It was highly influenced by the depth of the cement pastes. There was porosity increase on the surface of the cement pastes due to dissolution of hydration products, such as portlandite, ettringite, and CSH. However, the decrease of porosity was estimated inside the cement pastes due to the precipitation of cement minerals. (author)

  10. Compressive Strength and Physical Properties Behavior of Cement Mortars with addition of Cement Klin Dust

    Directory of Open Access Journals (Sweden)

    Auday A Mehatlaf

    2017-12-01

    Full Text Available Cement Klin Dust (CKD was the waste of almost cement industry factories, so that in this paper utilization of CKD as filler in cement and/or concrete was the main objective. CKD from the Karbala cement factory had been used and analysis to know the chemical composition of the oxides was done. In this paper cement mortars with different weight percentages of CKD (0,5,10,20,30,40 had been prepared. Physical properties such as density and porosity were done in different age curing (3, 7, 28 day. In addition, mechanical properties included the coefficient of thermal conductivity and compressive strength had also observed with different age (3,7, and 28 for all prepared specimens. From the obtained the experimental results and their discussion, it was clear that the addition (20% of CKD had the good results in cement mortars.  

  11. Development of form stable Poly(methyl methacrylate) (PMMA) coated thermal phase change material for solar water heater applications

    Science.gov (United States)

    Munusamy, Y.; Shanmugam, S.; Shi-Ying, Kee

    2018-04-01

    Phase change material (PCM) is one of the most popular and widely used thermal energy storage material in solar water heater because it able to absorb and release a large amount of latent heat during a phase change process over a narrow temperature range. However the practical application of PCM is limited by two major issues; 1) leakage which leads to material loss and corrosion of tank and 2) large volume change during phase change process which cause pressure build up in the tank. In this work, form-stable PCM was prepared by coating myristic acid with Poly(methyl methacrylate) (PMMA) to prevent leakage of PCM. PMMA was mixed with different weight percentage (0.1, 0.2, 0.3, 0.4 and 0.5 wt%) of dicumyl peroxide (DCP). The purpose of adding DCP to PMMA is to crosslink the polymer and to increase the mechanical strength of PMMA to hold the myristic acid content inside the coating during the phase change process. Leakage test results showed that PMMA mixed with 0.1% DCP exhibit 0% leakage. This result is further supported by Field Emission Scanning Electron Microscopy (FESEM) images and Fourier transform infrared spectroscopy (FTIR) analysis results, where a compact and uniform coating without cracks were formed for PCM coated with PMMA with 0.1% DCP. Differential scanning calorimetry (DSC) results shows that the melting point of form-stable PCM is 55°C, freezing point is 50°C, the latent heat of melting and freezing is 67.59 J/g.

  12. Characterization and chemical activity of Portland cement and two experimental cements with potential for use in dentistry.

    Science.gov (United States)

    Camilleri, J

    2008-09-01

    To evaluate the chemical activity of Portland cement and two other cement types with similar chemical composition to mineral trioxide aggregate with the aim of developing these cements for further applications in dentistry. The chemical composition of the three cement types namely Portland cement, calcium sulpho-aluminate cement and calcium fluoro-aluminate cement was evaluated by elemental analysis using energy dispersive analysis with X-ray under the scanning electron microscope and by X-ray diffraction analysis (XRD) to determine the phases. The constituents of the hydration reaction by-products were evaluated by XRD analysis of the set cements at 1, 7, 28 and 56 days and by analysis of the leachate by ion chromatography. The pH of both cements and leachate was determined at different time intervals. Cements admixed with micro-silica were also tested to determine the effect of micro-silica on the reaction by-products. All three cement types were composed of tricalcium silicate as the main constituent phase. The hydration reaction of Portland cement produced calcium hydroxide. However, this was not present in the other cements tested at all ages. Admixed micro-silica had little or no effect on the cements with regard to reaction by-products. The pH of all cements tested was alkaline. Both the experimental calcium sulpho-aluminate cement and calcium fluoro-aluminate cement had different hydration reactions to that of Portland cement even though calcium silicate was the major constituent element of both cement types. No calcium hydroxide was produced as a by-product to cement hydration. Micro-silica addition to the cement had no effect on the hydration reaction.

  13. 76 FR 50252 - Gray Portland Cement and Cement Clinker From Japan; Scheduling of an Expedited Five-Year Review...

    Science.gov (United States)

    2011-08-12

    ... INTERNATIONAL TRADE COMMISSION [Investigation No. 731-TA-461 (Third Review)] Gray Portland Cement and Cement Clinker From Japan; Scheduling of an Expedited Five-Year Review Concerning the Antidumping Duty Order on Gray Portland Cement and Cement Clinker From Japan AGENCY: United States International...

  14. Influence of Cement Particle-Size Distribution on Early Age Autogenous Strains and Stresses in Cement-Based Materials

    DEFF Research Database (Denmark)

    Bentz, Dale P.; Jensen, Ole Mejlhede; Hansen, Kurt Kielsgaard

    2001-01-01

    The influence of cement particle-size distribution on autogenous strains and stresses in cement pastes of identical water-to-cement ratios is examined for cement powders of four different finenesses. Experimental measurements include chemical shrinkage, to quantify degree of hydration; internal r...

  15. Preparation and Properties of PTFE-PMMA Core-Shell Nanoparticles and Nanocomposites

    Directory of Open Access Journals (Sweden)

    Diego Antonioli

    2012-01-01

    Full Text Available The preparation of polytetrafluoroethylene-poly(methyl methacrylate (PTFE-PMMA core-shell particles was described, featuring controlled size and narrow size distribution over a wide compositional range, through a seeded emulsion polymerization starting from a PTFE seed of 26 nanometers. Over the entire MMA/PTFE range, the particle size increases as the MMA/PTFE ratio increases. A very precise control over the particle size can be exerted by properly adjusting the ratio between the monomer and the PTFE seed. Particles in the 80–240 nm range can be prepared with uniformity indexes suited to build 2D and 3D colloidal crystals. These core-shell particles were employed to prepare nanocomposites with different compositions, through an annealing procedure at a temperature higher than the glass transition temperature of the shell forming polymer. A perfect dispersion of the PTFE particles within the PMMA matrix was obtained and optically transparent nanocomposites were prepared containing a very high PTFE amount.

  16. Electrical percolation, morphological and dispersion properties of MWCNT/PMMA nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Coelho, Paulo Henrique da Silva Leite; Marchesin, Marcel Silva; Morales, Ana Rita; Bartoli, Julio Roberto, E-mail: piyke.coelho@gmail.com [Universidade de Campinas (UNICAMP), SP (Brazil). Escola de Engenharia Quimica

    2014-08-15

    Nanocomposites of poly (methyl methacrylate) (PMMA) and carbon nanotubes have a high potential for applications where conductivity and low specific weight are required. This piece of work concerns investigations of the level of dispersion and morphology on the electrical properties of in situ polymerized nanocomposites in different concentrations of multi-walled carbon nanotubes (MWCNT) in a PMMA matrix. The electrical conductivity was measured by the four point probe. The morphology and dispersion was analyzed by Transmission Electron Microscopy (TEM) and Small Angle X-ray Scattering (SAXS). The correlation between electrical conductivity and the MWCNT amount, presented a typical percolation behavior, whose electrical percolation threshold determined by power law relationship was 0.2 vol. (%) The exponent t from the percolation power law indicated the formation of a 3D network of randomly arranged MWCNT. SAXS detected that the structures are intermediate to disks or spheres indicating fractal geometry for the MWCNT aggregates instead of isolated rods. HR-TEM images allowed us to observe the MWCNT individually dispersed into the matrix, revealing their distribution without preferential space orientation and absence of significant damage to the walls. The combined results of SAXS and HR-TEM suggest that MWCNT into the polymeric matrix might present interconnected aggregates and some dispersed single structures. (author)

  17. Preparation and characterization of PMMA graded microporous foams via one-step supercritical carbon dioxide foaming

    International Nuclear Information System (INIS)

    Yuan Huan; Li Junguo; Xiong Yuanlu; Luo Guoqiang; Shen Qiang; Zhang Lianmeng

    2013-01-01

    Supercritical carbon dioxide (ScCO 2 ) foaming which is inexpensive and environmental friendly has been widely used to prepare polymer-based microporous materials. In this paper, PMMA graded microporous materials were foamed by PMMA matrix after an unstable saturation process which was done under supercritical condition of 28MPa and 50 °C. The scanning electron microscopy (SEM) was utilized to observe the morphology of the graded foam. A gas adsorption model was proposed to predict the graded gas concentration in the different region of the polymer matrix. The SEM results showed that the solid and foam region of the graded foam can be connected without laminated layers. With the increasing thickness position of the graded microporous foam, the cell size increased from 3.4 to 27.5 μm, while the cell density decreased from 1.04 × 10 9 to 1.96 × 10 7 cells/cm 3 . It also found that the gradient microporous structure of the foam came from graded gas concentration which was obtained in the initial saturation process.

  18. Transparent CuInS2/PMMA nanocomposites luminescent in the visible and NIR region

    International Nuclear Information System (INIS)

    Gugula, Krzysztof; Bredol, Michael

    2014-01-01

    Nanocomposites combining functional nanoparticles and transparent polymers allow for stabilization of filler properties over long periods of time while retaining transparency of the polymer matrix. Here we employ CuInS 2 /ZnS quantum dots (QDs), ternary visible- and NIR-emitting semiconductors as wavelength-tunable luminescent fillers. Luminescence in the near infrared (NIR) is of particular interest in medicine which allows deep penetration into human tissue enabling in vivo diagnostics and treatment, while visible emitters may serve as color converters in displays or lighting. To stabilize the optical properties of QDs and prevent agglomeration, polymethyl metacrylate (PMMA) was chosen as a matrix. These novel polymer nanocomposites (PNCs) show good optical properties and stability under ambient conditions, and can be easily deposited over large areas. High-quality QDs and hydrophobic functionalization with long-chain hydrocarbons are a prerequisite for embedding into a PMMA matrix. Transparent PNC films without visible scattering losses were obtained for 1 wt-% QD loading with respect to the polymer. Partial transparency is retained up to 10 wt-% QD loading and vanishes rapidly at higher loading. Luminescence properties increase up to 5 wt-% and then decrease rapidly due to QD agglomeration and reabsorption between adjacent particles. Potential applications include converter materials for medical applications, laser layers, displays and white LEDs. (orig.)

  19. Monolithic Magneto-Optical Nanocomposites of Barium Hexaferrite Platelets in PMMA.

    Science.gov (United States)

    Ferk, Gregor; Krajnc, Peter; Hamler, Anton; Mertelj, Alenka; Cebollada, Federico; Drofenik, Miha; Lisjak, Darja

    2015-06-12

    The incorporation of magnetic barium hexaferrite nanoparticles in a transparent polymer matrix of poly(methyl methacrylate) (PMMA) is reported for the first time. The barium hexaferrite nanoplatelets doped with Sc(3+), i.e., BaSc0.5Fe11.5O12 (BaHF), having diameters in the range 20 to 130 nm and thicknesses of approximately 5 nm, are synthesized hydrothermally and stabilized in 1-butanol with dodecylbenzenesulfonic acid. This method enables the preparation of monolithic nanocomposites by admixing the BaHF suspension into a liquid monomer, followed by in-situ, bulk free-radical polymerization. The PMMA retains its transparency for loadings of BaHF nanoparticles up to 0.27 wt.%, meaning that magnetically and optically anisotropic, monolithic nanocomposites can be synthesized when the polymerization is carried out in a magnetic field. The excellent dispersion of the magnetic nanoparticles, coupled with a reasonable control over the magnetic properties achieved in this investigation, is encouraging for the magneto-optical applications of these materials.

  20. Electrical percolation, morphological and dispersion properties of MWCNT/PMMA nanocomposites

    International Nuclear Information System (INIS)

    Coelho, Paulo Henrique da Silva Leite; Marchesin, Marcel Silva; Morales, Ana Rita; Bartoli, Julio Roberto

    2014-01-01

    Nanocomposites of poly (methyl methacrylate) (PMMA) and carbon nanotubes have a high potential for applications where conductivity and low specific weight are required. This piece of work concerns investigations of the level of dispersion and morphology on the electrical properties of in situ polymerized nanocomposites in different concentrations of multi-walled carbon nanotubes (MWCNT) in a PMMA matrix. The electrical conductivity was measured by the four point probe. The morphology and dispersion was analyzed by Transmission Electron Microscopy (TEM) and Small Angle X-ray Scattering (SAXS). The correlation between electrical conductivity and the MWCNT amount, presented a typical percolation behavior, whose electrical percolation threshold determined by power law relationship was 0.2 vol. (%) The exponent t from the percolation power law indicated the formation of a 3D network of randomly arranged MWCNT. SAXS detected that the structures are intermediate to disks or spheres indicating fractal geometry for the MWCNT aggregates instead of isolated rods. HR-TEM images allowed us to observe the MWCNT individually dispersed into the matrix, revealing their distribution without preferential space orientation and absence of significant damage to the walls. The combined results of SAXS and HR-TEM suggest that MWCNT into the polymeric matrix might present interconnected aggregates and some dispersed single structures. (author)

  1. One-pot synthesis and transfer of PMMA/Ag photonic nanocomposites by pulsed laser deposition

    Science.gov (United States)

    Karoutsos, V.; Koutselas, I.; Orfanou, P.; Mpatzaka, Th.; Vasileiadis, M.; Vassilakopoulou, A.; Vainos, N. A.; Perrone, A.

    2015-08-01

    Nanocomposite films comprising metallic nanoparticles in polymer matrices find increasing use in emerging photonic, electronic and microsystem applications owing to their tailored advanced functionalities. The versatile development of such films based on poly-methyl-methacrylate (PMMA) matrix having embedded Ag nanoparticles is addressed here. Two low-cost one-pot chemical methods for the synthesis of bulk target nanocomposite materials are demonstrated. These nanocomposites are subsequently transferred via pulsed laser deposition using 193 nm ArF excimer laser radiation, producing films maintaining the structural and functional properties. Both target- and laser-deposited materials have been thoroughly characterized using microscopic, spectroscopic and thermal analysis methods. Infrared spectra demonstrated the close molecular PMMA chain similarity for both target and film materials, though structural alterations identified by thermal analysis proved the enhanced characteristics of films grown. High-resolution electron microscopy proved the transfer of Ag nanoparticles sized 10-50 nm. Visible absorption peaked in the spectral range of 430-440 nm and attributed to the Ag nanocomposite plasmonic response verifying the transfer of the functional performance from target to film.

  2. Nanoscale surface modifications to control capillary flow characteristics in PMMA microfluidic devices

    Directory of Open Access Journals (Sweden)

    Mukhopadhyay Subhadeep

    2011-01-01

    Full Text Available Abstract Polymethylmethacrylate (PMMA microfluidic devices have been fabricated using a hot embossing technique to incorporate micro-pillar features on the bottom wall of the device which when combined with either a plasma treatment or the coating of a diamond-like carbon (DLC film presents a range of surface modification profiles. Experimental results presented in detail the surface modifications in the form of distinct changes in the static water contact angle across a range from 44.3 to 81.2 when compared to pristine PMMA surfaces. Additionally, capillary flow of water (dyed to aid visualization through the microfluidic devices was recorded and analyzed to provide comparison data between filling time of a microfluidic chamber and surface modification characteristics, including the effects of surface energy and surface roughness on the microfluidic flow. We have experimentally demonstrated that fluid flow and thus filling time for the microfluidic device was significantly faster for the device with surface modifications that resulted in a lower static contact angle, and also that the incorporation of micro-pillars into a fluidic device increases the filling time when compared to comparative devices.

  3. Nanocryl Coating of PMMA Complete Denture Base Materials to Prevent Scratching.

    Science.gov (United States)

    Fathi, Hawa M; Benonn, Hajer A; Johnson, Anthony

    2017-09-01

    The surface of polymethylmethacrylate (PMMA) is vulnerable to indentation by hard objects that may contribute to abrade the material surface and subject it to wear. This phenomenon promotes an increase in the surface roughness leading to microbial colonisation which can endanger the general health of wearers and damage the intra-oral prosthesis. The aim of this study is to investigate the effect of three different nanocryl coating agents (Easy Glaze, G-Coat Plus and Formulation XP) on surface roughness and thickness of PMMA material after a simulating cleaning process utilizing an electric toothbrush and three different dentifrices (pastes and immersion). Acrylic uncoated discs were used as a control group. The results showed that the G-Coat Plus coating agent had less changes in the surface roughness and thickness layer whereas the immersion cleaner revealed less abrasion effect compared with the paste cleaners which could be considered the most suitable cleaner to provide lower abrasivenes and good removal of organic debris. However, using nanofilled sealants did not demonstrate significant improvement in reducing surface roughness p ⟩ 0.05. Nevertheless, it could provide some protection against wearing to the acrylic resin surface during tooth brushing and may provide better resistance to microbial colonisation. Copyright© 2017 Dennis Barber Ltd.

  4. Sensitive methanol sensor based on PMMA-G-CNTs nanocomposites deposited onto glassy carbon electrodes.

    Science.gov (United States)

    Rahman, Mohammed M; Hussein, Mahmoud A; Alamry, Khalid A; Al Shehry, Faten M; Asiri, Abdullah M

    2016-04-01

    A new series of polymethyl methacrylate-graphene-carbon nanotubes crossbred nanocomposites in the form of PMMA-G-CNTs has been synthesized using simple dissolution procedure in organic media. The desired nanocomposites have been prepared using different loading (2 ∼ 30%) from consequently mixed GNPs/CNTs ratio and confirmed by various characterization techniques utilized to corroborate the assembly of these new hybrid series including X-ray diffraction analysis, Fourier transform infrared spectroscopy and scanning electron microscopy. The PMMA-G-CNTs nanocomposites were deposited on flat glassy carbon electrodes (GCE) to result in a sensor that has a fast response toward methanol in the phosphate buffer phase. Features including high sensitivity, low-sample volume, reliability, reproducibility, ease of integration, long-term stability, and enhanced electrochemical responses are investigated. The calibration plot is linear (r(2)=0.9895) over the 1.0 nmol L(-1) to 10.0 mmol L(-1) methanol concentration ranges. The sensitivity and detection limit is 13.491 µA cm(-2) mmol L(-2) and 0.39 ± 0.1 nmol L(-1) (at a signal-to-noise-ratio, SNR of 3), respectively. With such excellent features of analytical parameters, the developed sensor provides a new strategy for determination of methanol in biomedical and environmental analytes with satisfactory results. Copyright © 2015 Elsevier B.V. All rights reserved.

  5. Use of Almond Shells and Rice Husk as Fillers of Poly(Methyl Methacrylate) (PMMA) Composites.

    Science.gov (United States)

    Sabbatini, Alessandra; Lanari, Silvia; Santulli, Carlo; Pettinari, Claudio

    2017-07-28

    In recent years, wood fibres have often been applied as the reinforcement of thermoplastic materials, such as polypropylene, whereas their use in combination with thermosetting resin has been less widespread. This study concerns the production of PMMA-based composites by partly replacing alumina trihydrate (ATH) with wood waste fillers, namely rice husks and almond shells, which would otherwise be disposed by incineration. The amount of filler introduced was limited to 10% as regards rice husks and 10 or 15% almond shells, since indications provided by reactivity tests and viscosity measurements did not suggest the feasibility of total replacement of ATH. As a matter of fact, the introduction of these contents of wood waste filler in PMMA-based composite did not result in any significant deterioration of its mechanical properties (Charpy impact, Rockwell M hardness and flexural performance). Some reduction of these properties was only observed in the case of introduction of 15% almond shells. A further issue concerned the yellowing of the organic filler under exposure to UV light. On the other hand, a very limited amount of water was absorbed, never exceeding values around 0.6%, despite the significant porosity revealed by the filler's microscopic evaluation. These results are particularly interesting in view of the application envisaged for these composites, i.e., wood replacement boards.

  6. Angle-resolved reflection spectroscopy of high-quality PMMA opal crystal

    Science.gov (United States)

    Nemtsev, Ivan V.; Tambasov, Igor A.; Ivanenko, Alexander A.; Zyryanov, Victor Ya.

    2018-02-01

    PMMA opal crystal was prepared by a simple hybrid method, which includes sedimentation, meniscus formation and evaporation. We investigated three surfaces of this crystal by angle-resolved reflective light spectroscopy and SEM study. The angle-resolved reflective measurements were carried out in the 400-1100 nm range. We have determined the high-quality ordered surface of the crystal region. Narrow particle size distribution of the surface has been revealed. The average particle diameter obtained with SEM was nearly 361 nm. The most interesting result was that reflectivity of the surface turned out up to 98% at normal light incidence. Using a fit of dependences of the maximum reflectivity wavelength from an angle based on the Bragg-Snell law, the wavelength of maximum 0° reflectivity, the particle diameter and the fill factor have been determined. For the best surface maximum reflectivity wavelength of a 0° angle was estimated to be 869 nm. The particle diameter and fill factor were calculated as 372 nm and 0.8715, respectively. The diameter obtained by fitting is in excellent agreement with the particle diameter obtained with SEM. The reflectivity maximum is assumed to increase significantly when increasing the fill factor. We believe that using our simple approach to manufacture PMMA opal crystals will significantly increase the fabrication of high-quality photonic crystal templates and thin films.

  7. Effects of nanoparticles on the compatibility of PEO-PMMA block copolymers.

    Science.gov (United States)

    Mu, Dan; Li, Jian-Quan; Li, Wei-Dong; Wang, Song

    2011-12-01

    The compatibility of six kinds of designed poly(ethylene oxide)-block-poly(methyl methacrylate) (PEO-b-PMMA) copolymers was studied at 270, 298 and 400 K via mesoscopic modeling. The values of the order parameters depended on both the structures of the block copolymers and the simulation temperature, while the values of the order parameters of the long chains were higher than those of the short ones; temperature had a more obvious effect on long chains than on the short ones. Plain copolymers doped with poly(ethylene oxide) (PEO) or poly(methyl methacrylate) (PMMA) homopolymer showed different order parameter values. When a triblock copolymer had the same component at both ends and was doped with one of its component polymers as a homopolymer (such as A5B6A5 doped with B6 or A5 homopolymer), the value of its order parameter depended on the simulation temperature. The highest order parameter values were observed for A5B6A5 doped with B6 at 400 K and for A5B6A5 doped with A5 at 270 K. A study of copolymers doped with nanoparticles showed that the mesoscopic phase was influenced by not only the properties of the nanoparticles, such as the size and density, but also the compositions of the copolymers. Increasing the size of the nanoparticles used as a dopant had the most significant effect on the phase morphologies of the copolymers.

  8. Three-dimensional space charge distribution measurement in electron beam irradiated PMMA

    International Nuclear Information System (INIS)

    Imaizumi, Yoichi; Suzuki, Ken; Tanaka, Yasuhiro; Takada, Tatsuo

    1996-01-01

    The localized space charge distribution in electron beam irradiated PMMA was investigated using pulsed electroacoustic method. Using a conventional space charge measurement system, the distribution only in the depth direction (Z) can be measured assuming the charges distributed uniformly in the horizontal (X-Y) plane. However, it is difficult to measure the distribution of space charge accumulated in small area. Therefore, we have developed the new system to measure the three-dimensional space charge distribution using pulsed electroacoustic method. The system has a small electrode with a diameter of 1mm and a motor-drive X-Y stage to move the sample. Using the data measured at many points, the three-dimensional distribution were obtained. To estimate the system performance, the electron beam irradiated PMMA was used. The electron beam was irradiated from transmission electron microscope (TEM). The depth of injected electron was controlled using the various metal masks. The measurement results were compared with theoretically calculated values of electron range. (author)

  9. Bosch-like method for creating high aspect ratio poly(methyl methacrylate) (PMMA) structures

    KAUST Repository

    Haiducu, Marius

    2012-02-02

    This paper presents a method for etching millimetre-deep trenches in commercial grade PMMA using deep-UV at 254 nm. The method is based on consecutive cycles of irradiation and development of the exposed areas, respectively. The exposure segment is performed using an inexpensive, in-house built irradiation box while the development part is accomplished using an isopropyl alcohol (IPA):H2O developer. The method was tested and characterized by etching various dimension square test structures in commercial grade, mirrored acrylic. The undercut of the sidewalls due to the uncollimated nature of the irradiation light was dramatically alleviated by using a honeycomb metallic grid in between the irradiation source and the acrylic substrate and by rotating the latter using a direct current (DC) motor-driven stage. By using an extremely affordable set-up and non-toxic, environmentally friendly materials and substances, this process represents an excellent alternative to microfabricating microfluidic devices in particular and high aspect ratio structures in general using PMMA as substrate. © 2012 SPIE.

  10. Traceable size determination of PMMA nanoparticles based on Small Angle X-ray Scattering (SAXS)

    Energy Technology Data Exchange (ETDEWEB)

    Gleber, G; Cibik, L; Mueller, P; Krumrey, M [Physikalisch-Technische Bundesanstalt (PTB), Abbestrasse 2-12, 10587 Berlin (Germany); Haas, S; Hoell, A, E-mail: gudrun.gleber@ptb.d [Helmholtz-Zentrum-Berlin fuer Materialien und Energie (HZB), Albert-Einstein-Strasse 15, 12489 Berlin (Germany)

    2010-10-01

    The size and size distribution of PMMA nanoparticles has been investigated with SAXS (small angle X-ray scattering) using monochromatized synchrotron radiation. The uncertainty has contributions from the wavelength or photon energy of the radiation, the scattering angle and the fit procedure for the obtained scattering curves. The wavelength can be traced back to the lattice constant of silicon, and the scattering angle is traceable via geometric measurements of the detector pixel size and the distance between the sample and the detector. SAXS measurements and data evaluations have been performed at different distances and photon energies for two PMMA nanoparticle suspensions with low polydispersity and nominal diameters of 108 nm and 192 nm, respectively, as well as for a mixture of both. The relative variation of the diameters obtained for different experimental conditions was below {+-} 0.3 %. The determined number-weighted mean diameters of (109.0 {+-} 0.7) nm and (188.0 {+-} 1.3) nm, respectively, are close to the nominal values.

  11. Traceable size determination of PMMA nanoparticles based on Small Angle X-ray Scattering (SAXS)

    Science.gov (United States)

    Gleber, G.; Cibik, L.; Haas, S.; Hoell, A.; Müller, P.; Krumrey, M.

    2010-10-01

    The size and size distribution of PMMA nanoparticles has been investigated with SAXS (small angle X-ray scattering) using monochromatized synchrotron radiation. The uncertainty has contributions from the wavelength or photon energy of the radiation, the scattering angle and the fit procedure for the obtained scattering curves. The wavelength can be traced back to the lattice constant of silicon, and the scattering angle is traceable via geometric measurements of the detector pixel size and the distance between the sample and the detector. SAXS measurements and data evaluations have been performed at different distances and photon energies for two PMMA nanoparticle suspensions with low polydispersity and nominal diameters of 108 nm and 192 nm, respectively, as well as for a mixture of both. The relative variation of the diameters obtained for different experimental conditions was below ± 0.3 %. The determined number-weighted mean diameters of (109.0 ± 0.7) nm and (188.0 ± 1.3) nm, respectively, are close to the nominal values.

  12. Traceable size determination of PMMA nanoparticles based on Small Angle X-ray Scattering (SAXS)

    International Nuclear Information System (INIS)

    Gleber, G; Cibik, L; Mueller, P; Krumrey, M; Haas, S; Hoell, A

    2010-01-01

    The size and size distribution of PMMA nanoparticles has been investigated with SAXS (small angle X-ray scattering) using monochromatized synchrotron radiation. The uncertainty has contributions from the wavelength or photon energy of the radiation, the scattering angle and the fit procedure for the obtained scattering curves. The wavelength can be traced back to the lattice constant of silicon, and the scattering angle is traceable via geometric measurements of the detector pixel size and the distance between the sample and the detector. SAXS measurements and data evaluations have been performed at different distances and photon energies for two PMMA nanoparticle suspensions with low polydispersity and nominal diameters of 108 nm and 192 nm, respectively, as well as for a mixture of both. The relative variation of the diameters obtained for different experimental conditions was below ± 0.3 %. The determined number-weighted mean diameters of (109.0 ± 0.7) nm and (188.0 ± 1.3) nm, respectively, are close to the nominal values.

  13. Micro flow-through PCR in a PMMA chip fabricated by KrF excimer laser.

    Science.gov (United States)

    Yao, Liying; Liu, Baoan; Chen, Tao; Liu, Shibing; Zuo, Tiechuan

    2005-09-01

    As the third PCR technology, micro flow-through PCR chip can amplify DNA specifically in an exponential fashion in vitro. Nowadays many academies in the world have successfully amplified DNA using their own-made flow-through PCR chip. In this paper, the ablation principle of PMMA at 248 nm excimer laser was studied, then a PMMA based flow-through PCR chip with 20 cycles was fabricated by excimer laser at 19 kv and 18 mm/min. The chip was bonded together with another cover chip at 105( composite function)C, 160 N and 20 minutes. In the end, it was integrated with electrical thermal thin films and Pt 100 temperature sensors. The temperature controllers was built standard PID digital temperature controller, the temperature control precision was +/- 0.2( composite function)C. The temperature grads between the three temperature zones were 16.5 and 22.2( composite function)C respectively, the gaps between the temperature zones could realize heat insulation.

  14. Dose intercomparison study involving Fricke, ethanol chlorobenzene, PMMA and alanine dosimeters

    International Nuclear Information System (INIS)

    Lanuza, L.G.; Cabalfin, E.G.; Kojima, T.; Tachibana, H.

    1999-01-01

    A dose intercomparison study was carried out between the Philippine Nuclear Research Institute (PNRI) and Takasaki Radiation Chemistry Research Establishment, Japan Atomic Energy Research Institute (JAERI) to determine reliability of the dosimetry systems being used by PNRI employing ethanol chlorobenzene (ECB), Fricke and alanine dosimeters. The Fricke and ECB dosimeters were prepared at PNRI while the alanine-polystyrene dosimeter was provided by JAERI. Fricke or ECB dosimeters were irradiated together with alanine at PNRI gamma irradiation facilities. Analyses of the Fricke and ECB dosimeters were performed at PNRI while alanine dosimeters were analyzed at JAERI. A comparison study between alanine and polymethylmethacrylate (PMMA, Radix RN15) dosimeters was also undertaken at JAERI. The dosimeters were irradiated together under different irradiation conditions using the gamma irradiation facilities of JAERI and Radia Industry Co. Ltd. (Japan). Evaluations of PMMA and alanine dosimeters were both performed at JAERI. Result of the dose intercomparison of PNRI with the International Atomic Energy Agency through the International Dose Assurance Service (IDAS) is also presented. (author)

  15. Dose intercomparison study involving Fricke, ethanol chlorobenzene, PMMA and alanine dosimeters

    Energy Technology Data Exchange (ETDEWEB)

    Lanuza, L G; Cabalfin, E G [Philippine Nuclear Research Institute, Quezon City (Philippines); Kojima, T; Tachibana, H [Takasaki Radiation Chemistry Research Establishment, Japan Atomic Energy Research institute, Takasaki (Japan)

    1999-03-01

    A dose intercomparison study was carried out between the Philippine Nuclear Research Institute (PNRI) and Takasaki Radiation Chemistry Research Establishment, Japan Atomic Energy Research Institute (JAERI) to determine reliability of the dosimetry systems being used by PNRI employing ethanol chlorobenzene (ECB), Fricke and alanine dosimeters. The Fricke and ECB dosimeters were prepared at PNRI while the alanine-polystyrene dosimeter was provided by JAERI. Fricke or ECB dosimeters were irradiated together with alanine at PNRI gamma irradiation facilities. Analyses of the Fricke and ECB dosimeters were performed at PNRI while alanine dosimeters were analyzed at JAERI. A comparison study between alanine and polymethylmethacrylate (PMMA, Radix RN15) dosimeters was also undertaken at JAERI. The dosimeters were irradiated together under different irradiation conditions using the gamma irradiation facilities of JAERI and Radia Industry Co. Ltd. (Japan). Evaluations of PMMA and alanine dosimeters were both performed at JAERI. Result of the dose intercomparison of PNRI with the International Atomic Energy Agency through the International Dose Assurance Service (IDAS) is also presented. (author) 8 refs, 3 figs, 4 tabs

  16. Topography and surface free energy of DPPC layers deposited on a glass, mica, or PMMA support.

    Science.gov (United States)

    Jurak, Malgorzata; Chibowski, Emil

    2006-08-15

    An investigation of energetic properties of 1,2-dipalmitoyl-sn-glycero-3-phosphocholine (DPPC) layers deposited on glass, mica, and PMMA (poly(methyl methacrylate)) surfaces was carried out by means of contact angles measurements (advancing and receding) for three probe liquids (diiodomethane, water, and formamide). DPPC was deposited on the surfaces from water (on glass and mica) or methanol (on PMMA) solutions. The topography of the tested surfaces was determined with a help of scanning electron microscopy (SEM) and atomic force microscopy (AFM). Using the measured contact angles, the total apparent surface free energy and its components of the studied layers were determined from van Oss et al.'s (Lifshitz-van der Waals and acid-base components, LWAB) and contact angle hysteresis (CAH) approaches. It allowed us to learn about changes in the surface free energy of the layers (hydrophobicity/hydrophilicity) depending on their number and kind of support. It was found that the changes in the energy greatly depended on the surface properties of the substrate as well as the statistical number of monolayers of DPPC. However, principal changes took place for first three monolayers.

  17. Lithography exposure characteristics of poly(methyl methacrylate) (PMMA) for carbon, helium and hydrogen ions

    Science.gov (United States)

    Puttaraksa, Nitipon; Norarat, Rattanaporn; Laitinen, Mikko; Sajavaara, Timo; Singkarat, Somsorn; Whitlow, Harry J.

    2012-02-01

    Poly(methyl methacrylate) is a common polymer used as a lithographic resist for all forms of particle (photon, ion and electron) beam writing. Faithful lithographic reproduction requires that the exposure dose, Θ, lies in the window Θ0⩽ΘChiang Mai and Jyväskylä to determine the exposure characteristics in terms of fluence for 2 MeV protons, 3 MeV 4He and 6 MeV 12C ions, respectively. After exposure the samples were developed in 7:3 by volume propan-2-ol:de-ionised water mixture. At low fluences, where the fluence is below the clearing fluence, the exposed regions were characterised by rough regions, particularly for He with holes around the ion tracks. As the fluence (dose) increases so that the dose exceeds the clearing dose, the PMMA is uniformly removed with sharp vertical walls. When Θ exceeds the cross-linking onset fluence, the bottom of the exposed regions show undissolved PMMA.

  18. Femtosecond laser direct generation of 3D-microfluidic channels inside bulk PMMA.

    Science.gov (United States)

    Roth, Gian-Luca; Esen, Cemal; Hellmann, Ralf

    2017-07-24

    We report on laser direct generation of 3D-microchannels for microfluidic applications inside PMMA bulk material by focused femtosecond pulses. Inner lying channels with cross sectional areas from 100 µm 2 to 4400 µm 2 are directly created in the volume of a PMMA substrate. Using the presented process, the channel length is fundamentally unlimited. Here we demonstrate a channel length of 6 meters inside a substrate with dimensions of 20 × 20 × 1.1 mm. The formation of the micro channels is based on nonlinear absorption around the focal volume that triggers a material modification. The modified volume can be selectively opened to form the channel by a subsequent annealing process. The cross section of the channel is strongly influenced by the energy distribution and illumination around the focal volume determined by the optical setup and process design. The 3D channel layout can easily be realized by moving the specimen using 3D motorized stage, allowing freely chosen complex shaped channel architectures. Within a comprehensive parameter study, varying laser power, number of multi-passes, writing speed and writing depths, we identify an optimized process in terms of attainable channel height, width and aspect ratio, as well as process stability and reproducibility. The proof of concept for an application in three dimensional microfluidic systems is provided by florescence microscopy using a dye rhodamine B solution in isopropanol.

  19. Chemical changes in PMMA as a function of depth due to proton beam irradiation

    International Nuclear Information System (INIS)

    Szilasi, S.Z.; Huszank, R.; Szikra, D.; Vaczi, T.; Rajta, I.; Nagy, I.

    2011-01-01

    Highlights: → Chemical changes were investigated as a function of depth in proton irradiated PMMA → The depth profile of numerous functional groups was determined along the depth → The degree of chemical modification strongly depends on the LET of protons → At low-fluences the zone of maximal modification is restricted to the Bragg peak → At higher fluences the zone of max. modification extends towards the sample surface. - Abstract: In this work we determined depth profiles of the chemical change in PMMA irradiated with 2 MeV protons by infrared spectroscopic and micro-Raman measurements. The measurements were carried out on 10 μm thin stacked foil samples using an infrared spectrometer in universal attenuated total reflectance (UATR) and transmission modes; while the thick samples were analyzed with a confocal micro-Raman spectrometer. The depth profiles of the changes formed due to the various delivered fluences were compared to each other. The measurements show the strong dependence of the degree of modification on the energy transfer from the decelerating protons. Depth profiles reveal that at the fluences applied in this work the entire irradiated volume suffered some chemical modifications. In case of low-fluence samples the zone of maximal modification is restricted only to the Bragg peak, but with increasing fluences the region of maximal modification extends towards the sample surface.

  20. Theoretical and Experimental Study on Vibration Propagation in PMMA Components in Ultrasonic Bonding Process

    Directory of Open Access Journals (Sweden)

    Yibo Sun

    2017-03-01

    Full Text Available Ultrasonic bonding has an increasing application in the micro assembly of polymeric micro-electro mechanical systems (MEMS with high requirements for fusion precision. In the ultrasonic bonding process, the propagation of ultrasonic vibration in polymer components is related to the interfacial fusion, which can be used as a monitoring parameter to control ultrasonic energy. To study the vibration propagation in viscoelastic polymer components, finite element analysis on the bonding of poly methyl methacrylate (PMMA micro connector to substrate for microfluidic system is carried out. Curves of propagated vibration amplitude corresponding to interfacial temperatures are obtained. The ultrasonic vibration propagated in PMMA components are measured through experiments. The theoretical and experimental results are contrasted to analyze the change mechanism of vibration propagation related to temperature. Based on the ultrasonic bonding process controlled by the feedback of vibration propagation, interfacial fusions at different vibration propagation states are obtained through experiments. Interfacial fusion behavior is contrasted to the propagated vibration amplitude in theoretical and experimental studies. The relation between vibration propagation and fusion degree is established with the proper parameter range for the obtained high quality bonding.

  1. Effect of Abutment Modification and Cement Type on Retention of Cement-Retained Implant Supported Crowns

    OpenAIRE

    Farzin, Mitra; Torabi, Kianoosh; Ahangari, Ahmad Hasan; Derafshi, Reza

    2014-01-01

    Objective: Provisional cements are commonly used to facilitate retrievability of cement-retained fixed implant restorations; but compromised abutment preparation may affect the retention of implant-retained crowns.The purpose of this study was to investigate the effect of abutment design and type of luting agent on the retentive strength of cement-retained implant restorations. Materials and Method: Two prefabricated abutments were attached to their corresponding analogs and embedded in an ac...

  2. Foamed cement for squeeze cementing low-pressure, highly permeable reservoirs

    International Nuclear Information System (INIS)

    Chmllowski, W.; Kondratoff, L.B.

    1992-01-01

    Four different cement squeezing techniques have been used on wells producing from the Keg River formation in the Rainbow Lake area of Alberta, Canada. This paper evaluates 151 cement squeeze treatments performed at 96 wellsites and compares the use of foam cement vs. conventional squeeze treatments and techniques. Discussion includes key aspects, such as candidate selection, slurry design, treatment design, economic evaluation, and operational considerations

  3. Hydration of fly ash cement and microstructure of fly ash cement pastes

    Energy Technology Data Exchange (ETDEWEB)

    Shiyuan, H.

    1981-01-01

    The strength development and hydration of fly ash cement and the influence of addition of gypsum on those were studied at normal and elevated temperatures. It was found that an addition of a proper amount of gypsum to fly ash cement could accelerate the pozzolanic reaction between CH and fly ash, and as a result, increase the strength of fly ash cement pastes after 28 days.

  4. Cement stabilization of hazardous and radioactive electroplating sludge

    International Nuclear Information System (INIS)

    Langton, C.A.; Pickett, J.B.; Martin, M.L.

    1991-01-01

    Cement stabilization was evaluated for treatment of nickel and uranium in electroplating sludge at the Savannah River Site. Waste forms were prepared by pretreating the sludge and the solidifying it in a variety of cement, cement plus flyash, and cement-flyash-slag mixes. The sludge was also treated by one-step filtration-solidification. Leaching results and processing data indicate the cement solidification is an effective method of treating hazardous-low-level electroplating waste

  5. experimental study of cement grout: rheological behavior and sedimentation

    OpenAIRE

    Rosquoët , Frédéric; Alexis , Alain ,; Khelidj , Abdelhafid; Phelipot-Mardelé , Annabelle

    2002-01-01

    International audience; Three basic elements (cement, water and admixture) usually make up injectable cement grouts used for prestressed cable coating, repair and consolidation of masonry, soil grouting, etc... The present study was divided into two parts. First, in order to characterize rheologically fresh cement paste with W/C ratios (water/cement ratio) varying between 0.35 and 1, an experimental study was carried out and has revealed that the cement past behaves like a shear-thinning mate...

  6. Nanoscaled Mechanical Properties of Cement Composites Reinforced with Carbon Nanofibers

    OpenAIRE

    Barbhuiya, Salim; Chow, PengLoy

    2017-01-01

    This paper reports the effects of carbon nanofibers (CNFs) on nanoscaled mechanical properties of cement composites. CNFs were added to cement composites at the filler loading of 0.2 wt % (by wt. of cement). Micrographs based on scanning electron microscopy (SEM) show that CNFs are capable of forming strong interfacial bonding with cement matrices. Experimental results using nanoindentation reveal that the addition of CNFs in cement composites increases the proportions of high-density calcium...

  7. Effect of Cement Composition in Lampung on Concrete Strength

    OpenAIRE

    Riyanto, Hery

    2014-01-01

    The strength and durability of concrete depends on the composition of its constituent materials ie fine aggregate, coarse aggregate, cement, water and other additives. The cement composition is about 10% acting as a binder paste material fine and coarse aggregates. In the Lampung market there are several brands of portland cement used by the community to make concrete construction. Although there is a standard of the government of portland cement composition, yet each brand of cement has diff...

  8. Thermally induced self-assembly of cylindrical nanodomains in low molecular weight PS-b-PMMA thin films

    International Nuclear Information System (INIS)

    Seguini, Gabriele; Giammaria, Tommaso J; Lupi, Federico Ferrarese; Perego, Michele; Sparnacci, Katia; Antonioli, Diego; Gianotti, Valentina; Laus, Michele; Vita, Francesco; Placentino, Immacolata F; Francescangeli, Oriano; Hilhorst, Jan; Ferrero, Claudio

    2014-01-01

    The phase behaviour in thin films of an asymmetric polystyrene-b-polymethylmethacrylate (PS-b-PMMA) block copolymer with a molecular weight of 39 kg mol −1 was assessed at a wide range of temperatures and times. Cylindrical PMMA structures featuring a diameter close to 10 nm and perpendicularly oriented with respect to the substrate were obtained at 180 ° C in relatively short annealing times (t ≤ 30 min) by means of a simple thermal treatment performed in a standard rapid thermal processing machine. (paper)

  9. Facile synthesis of hollow Sn–Co@PMMA nanospheres as high performance anodes for lithium-ion batteries via galvanic replacement reaction and in situ polymerization

    Energy Technology Data Exchange (ETDEWEB)

    Yu, Xiaohui; Jiang, Anni; Yang, Hongyan; Meng, Haowen; Dou, Peng; Ma, Daqian [School of Materials Science and Engineering, Tianjin University, Tianjin 300072 (China); Xu, Xinhua, E-mail: xhxutju@gmail.com [School of Materials Science and Engineering, Tianjin University, Tianjin 300072 (China); Tianjin Key Laboratory of Composite and Functional Materials, Tianjin 300072 (China)

    2015-08-30

    Highlights: • Hollow Sn–Co nanospheres were synthesized via a facile galvanic replacement method. • PMMA layers were uniform coated on the surface of Sn–Co composites via in situ emulsion polymerization. • The coating layers are beneficial to suppress the aggregation and stabilize the SEI formation on the surface. • Excellent cycling stability and rate capability were obtained by coating PMMA protective layers on the surface of hollow Sn–Co nanospheres. - Abstract: Polymethyl methacrylate (PMMA)-coated hollow Sn–Co nanospheres (Sn–Co@PMMA) with superior electrochemical performance had been synthesized via a facile galvanic replacement method followed by an in situ emulsion polymerization route. The properties were investigated in detail and results show that the hollow Sn–Co nanospheres were evenly coated with PMMA. Benefiting from the protection of the PMMA layers, the hollow Sn–Co@PMMA nanocomposite is capable of retaining a high capacity of 590 mAh g{sup −1} after 100 cycles with a coulomb efficiency above 98%, revealing better electrochemical properties compared with hollow Sn–Co anodes. The PMMA coating could help accommodate the mechanical strain caused by volume expansion and stabilize the solid electrolyte interphase (SEI) film formed on the electrode. Such a facile process could be further extended to other anode materials for lithium-ion batteries.

  10. Electron Beam Lithography of HSQ and PMMA Resists and Importance of their Properties to Link the Nano World to the Micro World

    NARCIS (Netherlands)

    Kaleli, B.; Aarnink, Antonius A.I.; Smits, Sander M.; Hueting, Raymond Josephus Engelbart; Wolters, Robertus A.M.; Schmitz, Jurriaan

    2010-01-01

    In this work we investigated the properties of HSQ and PMMA resists focusing on contrast and line width for ebeam lithography (EBL) application. HSQ was found to be a good candidate to have desired line widths but the contrast we obtained was less than it was for PMMA. Since the fluorine based

  11. Volume holographic storage and multiplexing in blends of PMMA and a block methacrylic azopolymer, using 488 nm light pulses in the range of 100 ms to 1 s

    DEFF Research Database (Denmark)

    Forcen, Patricia; Oriol, Luis; Sanchez, Carlos

    2008-01-01

    Blends of polymethylmethacrylate (PMMA) and diblock methacrylic azopolymers have been investigated for holographic storage with short light pulses. Transmission electron microscopy measurements show that the dilution of the block copolymer in PMMA changes the microstructure from a lamellar to a s...

  12. Facile synthesis of hollow Sn–Co@PMMA nanospheres as high performance anodes for lithium-ion batteries via galvanic replacement reaction and in situ polymerization

    International Nuclear Information System (INIS)

    Yu, Xiaohui; Jiang, Anni; Yang, Hongyan; Meng, Haowen; Dou, Peng; Ma, Daqian; Xu, Xinhua

    2015-01-01

    Highlights: • Hollow Sn–Co nanospheres were synthesized via a facile galvanic replacement method. • PMMA layers were uniform coated on the surface of Sn–Co composites via in situ emulsion polymerization. • The coating layers are beneficial to suppress the aggregation and stabilize the SEI formation on the surface. • Excellent cycling stability and rate capability were obtained by coating PMMA protective layers on the surface of hollow Sn–Co nanospheres. - Abstract: Polymethyl methacrylate (PMMA)-coated hollow Sn–Co nanospheres (Sn–Co@PMMA) with superior electrochemical performance had been synthesized via a facile galvanic replacement method followed by an in situ emulsion polymerization route. The properties were investigated in detail and results show that the hollow Sn–Co nanospheres were evenly coated with PMMA. Benefiting from the protection of the PMMA layers, the hollow Sn–Co@PMMA nanocomposite is capable of retaining a high capacity of 590 mAh g −1 after 100 cycles with a coulomb efficiency above 98%, revealing better electrochemical properties compared with hollow Sn–Co anodes. The PMMA coating could help accommodate the mechanical strain caused by volume expansion and stabilize the solid electrolyte interphase (SEI) film formed on the electrode. Such a facile process could be further extended to other anode materials for lithium-ion batteries

  13. INFLUENCE OF WINE ACID ON RHEOLOGICAL PROPERTIES OF WELL BORE CEMENT SLURRIES AND HARDENED CEMENT PROPERTIES

    Directory of Open Access Journals (Sweden)

    Nediljka Gaurina-Međimurec

    1989-12-01

    Full Text Available Adaptation of commercial types of domestic cements for use in cementing the deep wells is a process by which Yugoslav oil industry tends to solve problems of completion of those wells independently. In order to design a domestic, cheep and effective retarder, tests of applicability of wine acid on cement slurries have been carried out. Besides examining the necessary wine acid content to achieve desirable Theological properties, the influence of this additive on properties of hardened cement samples has been tested too (the paper is published in Croatian.

  14. Potential risks of using cement-augmented screws for spinal fusion in patients with low bone quality.

    Science.gov (United States)

    Martín-Fernández, M; López-Herradón, A; Piñera, A R; Tomé-Bermejo, F; Duart, J M; Vlad, M D; Rodríguez-Arguisjuela, M G; Alvarez-Galovich, L

    2017-08-01

    Dramatic increases in the average life expectancy have led to increases in the variety of degenerative changes and deformities observed in the aging spine. The elderly population can present challenges for spine surgeons, not only because of increased comorbidities, but also because of the quality of their bones. Pedicle screws are the implants used most commonly in spinal surgery for fixation, but their efficacy depends directly on bone quality. Although polymethyl methacrylate (PMMA)-augmented screws represent an alternative for patients with osteoporotic vertebrae, their use has raised some concerns because of the possible association between cement leakages (CLs) and other morbidities. To analyze potential complications related to the use of cement-augmented screws for spinal fusion and to investigate the effectiveness of using these screws in the treatment of patients with low bone quality. A retrospective single-center study. This study included 313 consecutive patients who underwent spinal fusion using a total of 1,780 cement-augmented screws. We analyzed potential complications related to the use of cement-augmented screws, including CL, vascular injury, infection, screw extraction problems, revision surgery, and instrument failure. There are no financial conflicts of interest to report. A total of 1,043 vertebrae were instrumented. Cement leakage was observed in 650 vertebrae (62.3%). There were no major clinical complications related to CL, but two patients (0.6%) had radicular pain related to CL at the S1 foramina. Of the 13 patients (4.1%) who developed deep infections requiring surgical debridement, two with chronic infections had possible spondylitis that required instrument removal. All patients responded well to antibiotic therapy. Revision surgery was performed in 56 patients (17.9%), most of whom had long construction. A total of 180 screws were removed as a result of revision. There were no problems with screw extraction. These results

  15. Basalt waste added to Portland cement

    Directory of Open Access Journals (Sweden)

    Thiago Melanda Mendes

    2016-08-01

    Full Text Available Portland cement is widely used as a building material and more than 4.3 billion tons were produced in 2014, with increasing environmental impacts by this industry, mainly through CO2 emissions and consumption of non-removable raw materials. Several by-products have been used as raw materials or fuels to reduce environmental impacts. Basaltic waste collected by filters was employed as a mineral mixture to Portland cement and two fractions were tested. The compression strength of mortars was measured after 7 days and Scanning Electron Microscopy (SEM and Electron Diffraction Scattering (EDS were carried out on Portland cement paste with the basaltic residue. Gains in compression strength were observed for mixtures containing 2.5 wt.% of basaltic residue. Hydration products observed on surface of basaltic particles show the nucleation effect of mineral mixtures. Clinker substitution by mineral mixtures reduces CO2 emission per ton of Portland cement.

  16. Subgrade stabilization alternatives to lime and cement.

    Science.gov (United States)

    2010-04-15

    This project involved four distinct research activities, (1) the influence of temperature on lime-stabilized soils, (2) the influence of temperature on cement-stabilized soils (3) temperature modeling of stabilized subgrade and (4) use of calcium chl...

  17. Cement materials for cesium and iodine confinement

    International Nuclear Information System (INIS)

    Nicolas, G.; Lequeux, N.; Boch, P.; Prene, S.

    2001-01-01

    The following topics were dealt with: radioactive waste storage, cement materials reacting with radioactive cesium and iodine, chemical barrier formation against radioactive pollution, ceramization, long term stability, XRD, PIXE analysis

  18. Recycled concrete aggregate in portland cement concrete.

    Science.gov (United States)

    2013-01-01

    Aggregates can be produced by crushing hydraulic cement concrete and are known as recycled concrete : aggregates (RCA). This report provides results from a New Jersey Department of Transportation study to identify : barriers to the use of RCA in new ...

  19. Recycled materials in Portland cement concrete

    Science.gov (United States)

    2000-06-01

    This report pertains to a comprehensive study involving the use of recycled materials in Portland cement concrete. Three different materials were studied including crushed glass (CG), street sweepings (SS), and recycled concrete (RC). Blast furnace s...

  20. Pore structure in blended cement pastes

    DEFF Research Database (Denmark)

    Canut, Mariana Moreira Cavalcanti

    Supplementary cementitious materials (SCMs), such as slag and fly ash, are increasingly used as a substitute for Portland cement in the interests of improvement of engineering properties and sustainability of concrete. According to studies improvement of engineering properties can be explained by...... on assumptions of degree of reaction and product densities gave for plain cement pastes results comparable to MIP data.......Supplementary cementitious materials (SCMs), such as slag and fly ash, are increasingly used as a substitute for Portland cement in the interests of improvement of engineering properties and sustainability of concrete. According to studies improvement of engineering properties can be explained...... supplement each other. Cement pastes (w/b=0.4) with and without slag and fly ash cured at two moisture (sealed and saturated) and temperature (20 and 55ºC) conditions were used to investigate the combined impact of SCMs addition and curing on the pore structure of pastes cured up to two years. Also...