  1. Structural, multiferroic, dielectric and magnetoelectric properties of (1-x)Ba0.85Ca0.15Ti0.90Zr0.10O3-(x)CoFe2O4 lead-free composites

    Science.gov (United States)

    Negi, N. S.; Kumar, Rakesh; Sharma, Hakikat; Shah, J.; Kotnala, R. K.

    2018-06-01

    High performance lead-free multiferroic composites with strong magnetoelectric coupling effect are desired to replace lead-based ceramics in multifunctional device applications due to increasing environmental issues. We report crystal structure, ferroelectric, magnetic, dielectric and magnetoelectric properties of (1-x)Ba0.85Ca0.15Ti0.90Zr0.10O3-(x)CoFe2O4 (BCTZ-CFO) lead-free composites with x = 0.1, 0.3, 0.5, 0.7 and 0.9 synthesized by chemical solution method. BCTZ power was synthesized by sol-gel method while CFO was prepared by metallo-organic decomposition (MOD) method. The XRD results confirm successful formation of the BCTZ-CFO composites without presence of any impurity phase. At room temperature, the BCTZ-CFO composites show multiferroic behavior characterized by ferroelectric and ferromagnetic hysteresis curves. The composite having 10 wt% of CFO exhibited maximum polarization, remnant polarization and coercive field of Ps ∼ 5.1 μC/cm2, Pr ∼ 1.4 μC/cm2 and Ec ∼ 11.6 kV/cm respectively. The BCTZ-CFO composite with 90 wt% of CFO incorporation exhibits improved ferromagnetic properties with Ms ∼ 32 emu/g, Mr ∼ 11.7 emu/g and Hc ∼ 504 Oe. Mӧssbauer spectra analysis show two sets of six-line hyperfine patterns for BCTZ-CFO composites, indicating the presence of Fe3+ ions in both A and B sites. Increasing BCTZ content was found to decrease the hyperfine field strength at both sites and is consistent with the decreasing magnetic moment observed for the samples. The maximum dielectric constant value ε‧ ∼ 678 is obtained at 1 MHz for composite with 10 wt% of CFO phase. The results indicate that the BCTZ-CFO composites are potential lead-free room temperature multiferroic systems.

  2. Multiferroics and magnetoelectrics: thin films and nanostructures

    Energy Technology Data Exchange (ETDEWEB)

    Martin, L W; Crane, S P; Chu, Y-H; Holcomb, M B; Gajek, M; Huijben, M; Yang, C-H; Balke, N; Ramesh, R [Department of Materials Science and Engineering, University of California, Berkeley, CA 94720 (United States); Department of Physics, University of California, Berkeley, CA 94720 (United States); Materials Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA 94720 (United States)], E-mail: lwmartin@lbl.gov

    2008-10-29

    Multiferroic materials, or materials that simultaneously possess two or more ferroic order parameters, have returned to the forefront of materials research. Driven by the desire to achieve new functionalities-such as electrical control of ferromagnetism at room temperature-researchers have undertaken a concerted effort to identify and understand the complexities of multiferroic materials. The ability to create high quality thin film multiferroics stands as one of the single most important landmarks in this flurry of research activity. In this review we discuss the basics of multiferroics including the important order parameters and magnetoelectric coupling in materials. We then discuss in detail the growth of single phase, horizontal multilayer, and vertical heterostructure multiferroics. The review ends with a look to the future and how multiferroics can be used to create new functionalities in materials.

  3. Multiferroics and magnetoelectrics: thin films and nanostructures

    Science.gov (United States)

    Martin, L. W.; Crane, S. P.; Chu, Y.-H.; Holcomb, M. B.; Gajek, M.; Huijben, M.; Yang, C.-H.; Balke, N.; Ramesh, R.

    2008-10-01

    Multiferroic materials, or materials that simultaneously possess two or more ferroic order parameters, have returned to the forefront of materials research. Driven by the desire to achieve new functionalities—such as electrical control of ferromagnetism at room temperature—researchers have undertaken a concerted effort to identify and understand the complexities of multiferroic materials. The ability to create high quality thin film multiferroics stands as one of the single most important landmarks in this flurry of research activity. In this review we discuss the basics of multiferroics including the important order parameters and magnetoelectric coupling in materials. We then discuss in detail the growth of single phase, horizontal multilayer, and vertical heterostructure multiferroics. The review ends with a look to the future and how multiferroics can be used to create new functionalities in materials.

  4. Multiferroics and magnetoelectrics: thin films and nanostructures

    International Nuclear Information System (INIS)

    Martin, L W; Crane, S P; Chu, Y-H; Holcomb, M B; Gajek, M; Huijben, M; Yang, C-H; Balke, N; Ramesh, R

    2008-01-01

    Multiferroic materials, or materials that simultaneously possess two or more ferroic order parameters, have returned to the forefront of materials research. Driven by the desire to achieve new functionalities-such as electrical control of ferromagnetism at room temperature-researchers have undertaken a concerted effort to identify and understand the complexities of multiferroic materials. The ability to create high quality thin film multiferroics stands as one of the single most important landmarks in this flurry of research activity. In this review we discuss the basics of multiferroics including the important order parameters and magnetoelectric coupling in materials. We then discuss in detail the growth of single phase, horizontal multilayer, and vertical heterostructure multiferroics. The review ends with a look to the future and how multiferroics can be used to create new functionalities in materials.

  5. Size effects on magnetoelectric response of multiferroic composite with inhomogeneities

    Energy Technology Data Exchange (ETDEWEB)

    Yue, Y.M. [Shanghai Institute of Applied Mathematics and Mechanics, Shanghai Key Laboratory of Mechanics in Energy Engineering, Department of Mechanics, Shanghai University, Shanghai 200072 (China); Xu, K.Y., E-mail: kyxu@shu.edu.cn [Shanghai Institute of Applied Mathematics and Mechanics, Shanghai Key Laboratory of Mechanics in Energy Engineering, Department of Mechanics, Shanghai University, Shanghai 200072 (China); Chen, T. [Shanghai Institute of Applied Mathematics and Mechanics, Shanghai Key Laboratory of Mechanics in Energy Engineering, Department of Mechanics, Shanghai University, Shanghai 200072 (China); Aifantis, E.C. [Laboratory of Mechanics and Materials (LMM), Aristotle University of Thessaloniki, Thessaloniki GR-54124 (Greece); Michigan Technological University, Houghton, MI 49931 (United States); King Abdulaziz University, Jeddah 21589 (Saudi Arabia); School of Mechanics and Engineering, Southwest Jiaotong University, Chengdu, 610031 (China); International Laboratory for Modern Functional Materials, ITMO University, St. Petersburg 191002 (Russian Federation)

    2015-12-01

    This paper investigates the influence of size effects on the magnetoelectric performance of multiferroic composite with inhomogeneities. Based on a simple model of gradient elasticity for multiferroic materials, the governing equations and boundary conditions are obtained from an energy variational principle. The general formulation is applied to consider an anti-plane problem of multiferroic composites with inhomogeneities. This problem is solved analytically and the effective magnetoelectric coefficient is obtained. The influence of the internal length (grain size or particle size) on the effective magnetoelectric coefficients of piezoelectric/piezomagnetic nanoscale fibrous composite is numerically evaluated and analyzed. The results suggest that with the increase of the internal length of piezoelectric matrix (PZT and BaTiO{sub 3}), the magnetoelectric coefficient increases, but the rate of increase is ratcheting downwards. If the internal length of piezoelectric matrix remains unchanged, the magnetoelectric coefficient will decrease with the increase of internal length scale of piezomagnetic nonfiber (CoFe{sub 2}O{sub 3}). In a composite consisiting of a piezomagnetic matrix (CoFe{sub 2}O{sub 3}) reinforced with piezoelectric nanofibers (BaTiO{sub 3}), an increase of the internal length in the piezomagnetic matrix, results to a decrease of the magnetoelectric coefficient, with the rate of decrease diminishing.

  6. Size effects on magnetoelectric response of multiferroic composite with inhomogeneities

    Science.gov (United States)

    Yue, Y. M.; Xu, K. Y.; Chen, T.; Aifantis, E. C.

    2015-12-01

    This paper investigates the influence of size effects on the magnetoelectric performance of multiferroic composite with inhomogeneities. Based on a simple model of gradient elasticity for multiferroic materials, the governing equations and boundary conditions are obtained from an energy variational principle. The general formulation is applied to consider an anti-plane problem of multiferroic composites with inhomogeneities. This problem is solved analytically and the effective magnetoelectric coefficient is obtained. The influence of the internal length (grain size or particle size) on the effective magnetoelectric coefficients of piezoelectric/piezomagnetic nanoscale fibrous composite is numerically evaluated and analyzed. The results suggest that with the increase of the internal length of piezoelectric matrix (PZT and BaTiO3), the magnetoelectric coefficient increases, but the rate of increase is ratcheting downwards. If the internal length of piezoelectric matrix remains unchanged, the magnetoelectric coefficient will decrease with the increase of internal length scale of piezomagnetic nonfiber (CoFe2O3). In a composite consisiting of a piezomagnetic matrix (CoFe2O3) reinforced with piezoelectric nanofibers (BaTiO3), an increase of the internal length in the piezomagnetic matrix, results to a decrease of the magnetoelectric coefficient, with the rate of decrease diminishing.

  7. Designing asymmetric multiferroics with strong magnetoelectric coupling

    Science.gov (United States)

    Lu, Xuezeng; Xiang, Hongjun; Rondinelli, James; Materials Theory; Design Group Team

    2015-03-01

    Multiferroics offer exciting opportunities for electric-field control of magnetism. Single-phase multiferroics suitable for such applications at room temperature need much more study. Here, we propose the concept of an alternative type of multiferroics, namely, the ``asymmetric multiferroic.'' In asymmetric multiferroics, two locally stable ferroelectric states are not symmetrically equivalent, leading to different magnetic properties between these two states. Furthermore, we predict from first principles that a Fe-Cr-Mo superlattice with the LiNbO3-type structure is such an asymmetric multiferroic. The strong ferrimagnetism, high ferroelectric polarization, and significant dependence of the magnetic transition temperature on polarization make this asymmetric multiferroic an ideal candidate for realizing electric-field control of magnetism at room temperature. Our study suggests that the asymmetric multiferroic may provide an alternative playground for voltage control of magnetism and find its applications in spintronics and quantum computing.

  8. Magnetoelectric Interactions in Lead-Based and Lead-Free Composites.

    Science.gov (United States)

    Bichurin, Mirza; Petrov, Vladimir; Zakharov, Anatoly; Kovalenko, Denis; Yang, Su Chul; Maurya, Deepam; Bedekar, Vishwas; Priya, Shashank

    2011-04-06

    Magnetoelectric (ME) composites that simultaneously exhibit ferroelectricity and ferromagnetism have recently gained significant attention as evident by the increasing number of publications. These research activities are direct results of the fact that multiferroic magnetoelectrics offer significant technological promise for multiple devices. Appropriate choice of phases with co-firing capability, magnetostriction and piezoelectric coefficient, such as Ni-PZT and NZFO-PZT, has resulted in fabrication of prototype components that promise transition. In this manuscript, we report the properties of Ni-PZT and NZFO-PZT composites in terms of ME voltage coefficients as a function of frequency and magnetic DC bias. In order to overcome the problem of toxicity of lead, we have conducted experiments with Pb-free piezoelectric compositions. Results are presented on the magnetoelectric performance of Ni-NKN, Ni-NBTBT and NZFO-NKN, NZFO-NBTBT systems illustrating their importance as an environmentally friendly alternative.

  9. Magnetoelectric Interactions in Lead-Based and Lead-Free Composites

    Directory of Open Access Journals (Sweden)

    Shashank Priya

    2011-04-01

    Full Text Available Magnetoelectric (ME composites that simultaneously exhibit ferroelectricity and ferromagnetism have recently gained significant attention as evident by the increasing number of publications. These research activities are direct results of the fact that multiferroic magnetoelectrics offer significant technological promise for multiple devices. Appropriate choice of phases with co-firing capability, magnetostriction and piezoelectric coefficient, such as Ni-PZT and NZFO-PZT, has resulted in fabrication of prototype components that promise transition. In this manuscript, we report the properties of Ni-PZT and NZFO-PZT composites in terms of ME voltage coefficients as a function of frequency and magnetic DC bias. In order to overcome the problem of toxicity of lead, we have conducted experiments with Pb-free piezoelectric compositions. Results are presented on the magnetoelectric performance of Ni-NKN, Ni-NBTBT and NZFO-NKN, NZFO-NBTBT systems illustrating their importance as an environmentally friendly alternative.

  10. Multiferroics and magnetoelectrics: thin films and nanostructures

    NARCIS (Netherlands)

    Martin, L.W.; Crane, S.P.; Chu, Y.H.; Holcomb, M.B.; Gajek, M.; Huijben, Mark; Yang, C.H.; Balke, N.; Ramesh, R.

    2008-01-01

    Multiferroic materials, or materials that simultaneously possess two or more ferroic order parameters, have returned to the forefront of materials research. Driven by the desire to achieve new functionalities—such as electrical control of ferromagnetism at room temperature—researchers have

  11. Multiferroic and magnetoelectric materials – Developments and perspectives

    Directory of Open Access Journals (Sweden)

    Shvartsman V. V.

    2012-06-01

    Full Text Available Multiferroic (MF materials with simultaneous magnetic and electric long range order and occasionally, mutual magnetoelectric (ME coupling, have recently attracted considerable interest. The small linear ME effect has been shown to control spintronic devices very efficiently, e.g. via the classic ME antiferromagnet Cr2O3 using exchange bias. Similar nano-engineering concepts exist also for type-I MF single phase materials, whose magnetic and polar orders have distinct origins like BiFeO3. Strong ME coupling occurs in type-II multiferroics, where ferroelectricity is due to spiral spin order as in TbMnO3. Record high ME response coming close to applicability arises in stress-strain coupled multiphase magnetoelectrics such as PZT/FeBSiC composites. Higher order ME response in disordered systems (“type-III multiferroics” extends the conventional MF scenario toward ME quantum paraelectric and multiglass materials with polarization-induced control of magnetic exchange, as e.g. in EuTiO3, Sr0.98Mn0.02TiO3, and PbFe0.5Nb0.5O3.

  12. Enhanced magnetoelectric coupling in a composite multiferroic system via interposing a thin film polymer

    Science.gov (United States)

    Xiao, Zhuyun; Mohanchandra, Kotekar P.; Lo Conte, Roberto; Ty Karaba, C.; Schneider, J. D.; Chavez, Andres; Tiwari, Sidhant; Sohn, Hyunmin; Nowakowski, Mark E.; Scholl, Andreas; Tolbert, Sarah H.; Bokor, Jeffrey; Carman, Gregory P.; Candler, Rob N.

    2018-05-01

    Enhancing the magnetoelectric coupling in a strain-mediated multiferroic composite structure plays a vital role in controlling magnetism by electric fields. An enhancement of magnetoelastic coupling between ferroelectric single crystal (011)-cut [Pb(Mg1/3Nb2/3)O3](1-x)-[PbTiO3]x (PMN-PT, x≈ 0.30) and ferromagnetic polycrystalline Ni thin film through an interposed benzocyclobutene polymer thin film is reported. A nearly twofold increase in sensitivity of remanent magnetization in the Ni thin film to an applied electric field is observed. This observation suggests a viable method of improving the magnetoelectric response in these composite multiferroic systems.

  13. The magnetoelectric coupling effect in multiferroic composites based on PZT–ferrite

    Energy Technology Data Exchange (ETDEWEB)

    Bartkowska, J.A., E-mail: joanna.bartkowska@us.edu.pl

    2015-01-15

    In the multiferroic materials, the dielectric and magnetic properties are closely correlated through the coupling interaction between the ferroelectric and magnetic order. We attempted to determine the values of magnetoelectric coupling coefficient, from the temperature dependences of the dielectric permittivity for the ferroelectric–ferromagnetic composite PZT–ferrite type, namely PSZTC–NiZn and PBZTN–NiZn. The main component of the ferroelectric–ferromagnetic composite was PZT type powder (with ferroelectric properties), which was synthesized using sintering of a mixture of simple oxides in solid phase. The second element of the ferroelectric–ferromagnetic composite was the ferrite powder (with ferromagnetic properties). Ferrite powder was synthesized using calcination. Next, the mixed components were synthesized using sintering of the mixture of simple oxides in a solid phase (compaction by a free sintering method). The temperature dependences of the dielectric permittivity (ε) for the different frequencies and for both multiferroic composites were investigated. Based on dielectric measurements and theoretical considerations, the values of the magnetoelectric coupling coefficient were specified. - Highlights: • The magnetoelectric effect at two different ferroelectric–ferromagnetic composites based on a PZT and nickel–zinc ferrite. • Multiferroics composite incorporate both ferroelectric and magnetic phases. • The mechanism of the magnetoelectric coupling between ferroelectric and magnetic properties, in multiferroic composites, is caused by the strain. • The determination of the magnetoelectric coupling coefficient based on a theoretical model and the measurements of dielectric permittivity.

  14. The magnetoelectric coupling effect in multiferroic composites based on PZT–ferrite

    International Nuclear Information System (INIS)

    Bartkowska, J.A.

    2015-01-01

    In the multiferroic materials, the dielectric and magnetic properties are closely correlated through the coupling interaction between the ferroelectric and magnetic order. We attempted to determine the values of magnetoelectric coupling coefficient, from the temperature dependences of the dielectric permittivity for the ferroelectric–ferromagnetic composite PZT–ferrite type, namely PSZTC–NiZn and PBZTN–NiZn. The main component of the ferroelectric–ferromagnetic composite was PZT type powder (with ferroelectric properties), which was synthesized using sintering of a mixture of simple oxides in solid phase. The second element of the ferroelectric–ferromagnetic composite was the ferrite powder (with ferromagnetic properties). Ferrite powder was synthesized using calcination. Next, the mixed components were synthesized using sintering of the mixture of simple oxides in a solid phase (compaction by a free sintering method). The temperature dependences of the dielectric permittivity (ε) for the different frequencies and for both multiferroic composites were investigated. Based on dielectric measurements and theoretical considerations, the values of the magnetoelectric coupling coefficient were specified. - Highlights: • The magnetoelectric effect at two different ferroelectric–ferromagnetic composites based on a PZT and nickel–zinc ferrite. • Multiferroics composite incorporate both ferroelectric and magnetic phases. • The mechanism of the magnetoelectric coupling between ferroelectric and magnetic properties, in multiferroic composites, is caused by the strain. • The determination of the magnetoelectric coupling coefficient based on a theoretical model and the measurements of dielectric permittivity

  15. Diffraction studies on the origin of giant magneto-electric effects in multiferroics

    International Nuclear Information System (INIS)

    Arima, Taka-hisa

    2009-01-01

    Magnetic ferroelectrics termed multiferroics often exhibit a giant magneto-electric response such as an appearance, disappearance, and rotation of ferroelectric polarization by the application of a magnetic field. In most multiferroics, long-wavelength spiral magnetic order arises from the competition among some magnetic exchange interactions. Spin-polarized neutron diffraction studies reveal that the ferroelectric polarization direction corresponds to the helicity of spiral magnetism. A change in magnetic order with the application of a magnetic field has been investigated for various multiferroics by means of synchrotron x-ray diffraction, because it can provide us some information about the periodicity and type of magnetic order. (author)

  16. Designing switchable near room-temperature multiferroics via the discovery of a novel magnetoelectric coupling

    Science.gov (United States)

    Feng, J. S.; Xu, Ke; Bellaiche, Laurent; Xiang, H. J.

    2018-05-01

    Magnetoelectric (ME) coupling is the key ingredient for realizing the cross-control of magnetism and ferroelectricity in multiferroics. However, multiferroics are not only rare, especially at room-temperature, in nature but also the overwhelming majority of known multiferroics do not exhibit highly-desired switching of the direction of magnetization when the polarization is reversed by an electric field. Here, we report group theory analysis and ab initio calculations demonstrating, and revealing the origin of, the existence of a novel form of ME coupling term in a specific class of materials that does allow such switching. This term naturally explains the previously observed electric field control of magnetism in the first known multiferroics, i.e., the Ni–X boracite family. It is also presently used to design a switchable near room-temperature multiferroic (namely, LaSrMnOsO6 perovskite) having rather large ferroelectric polarization and spontaneous magnetization, as well as strong ME coupling.

  17. A novel perovskite oxide chemically designed to show multiferroic phase boundary with room-temperature magnetoelectricity

    Science.gov (United States)

    Fernández-Posada, Carmen M.; Castro, Alicia; Kiat, Jean-Michel; Porcher, Florence; Peña, Octavio; Algueró, Miguel; Amorín, Harvey

    2016-09-01

    There is a growing activity in the search of novel single-phase multiferroics that could finally provide distinctive magnetoelectric responses at room temperature, for they would enable a range of potentially disruptive technologies, making use of the ability of controlling polarization with a magnetic field or magnetism with an electric one (for example, voltage-tunable spintronic devices, uncooled magnetic sensors and the long-searched magnetoelectric memory). A very promising novel material concept could be to make use of phase-change phenomena at structural instabilities of a multiferroic state. Indeed, large phase-change magnetoelectric response has been anticipated by a first-principles investigation of the perovskite BiFeO3-BiCoO3 solid solution, specifically at its morphotropic phase boundary between multiferroic polymorphs of rhombohedral and tetragonal symmetries. Here, we report a novel perovskite oxide that belongs to the BiFeO3-BiMnO3-PbTiO3 ternary system, chemically designed to present such multiferroic phase boundary with enhanced ferroelectricity and canted ferromagnetism, which shows distinctive room-temperature magnetoelectric responses.

  18. Continuous Magnetoelectric Control in Multiferroic DyMnO3 Films with Twin-like Domains

    Science.gov (United States)

    Lu, Chengliang; Deniz, Hakan; Li, Xiang; Liu, Jun-Ming; Cheong, Sang-Wook

    2016-02-01

    The magnetic control of ferroelectric polarization is currently a central topic in the multiferroic researches, owing to the related gigantic magnetoelectric coupling and fascinating physics. Although a bunch of novel magnetoelectric effect have been discovered in multiferroics of magnetic origin, the manipulation of polarization was found to be fundamentally determined by the microscopic origin in a certain multiferroic phase, hindering the development of unusual magnetoelectric control. Here, we report emergent magnetoelectric control in DyMnO3/Nb:SrTiO3 (001) films showing twin-like domain structure. Our results demonstrate interesting magnetically induced partial switch of polarization due to the coexistence of polarizations along both the a-axis and c-axis enabled by the twin-like domain structure in DyMnO3 films, despite the polarization-switch was conventionally believed to be a one-step event in the bulk counterpart. Moreover, a continuous and periodic control of macroscopic polarization by an in-plane rotating magnetic field is evidenced in the thin films. This distinctive magnetic manipulation of polarization is the consequence of the cooperative action of the twin-like domains and the dual magnetic origin of polarization, which promises additional applications using the magnetic control of ferroelectricity.

  19. Magnetoelectric coupling characteristics in multiferroic heterostructures with different thickness of nanocrystalline soft magnetic alloy

    Science.gov (United States)

    Chen, Lei; Wang, Yao

    2016-05-01

    Magnetoelectric(ME) coupling characteristics in multiferroic heterostructures with different thickness of nanocrystalline soft magnetic alloy has been investigated at low frequency. The ME response with obvious hysteresis, self-biased and dual-peak phenomenon is observed for multiferroic heterostructures, which results from strong magnetic interactions between two ferromagnetic materials with different magnetic properties, magnetostrictions and optimum bias magnetic fields Hdc,opti. The proposed multiferroic heterostructures not only enhance ME coupling significantly, but also broaden dc magnetic bias operating range and overcomes the limitations of narrow bias range. By optimizing the thickness of nanocrystalline soft magnetic alloy Tf, a significantly zero-biased ME voltage coefficient(MEVC) of 14.8mV/Oe (185 mV/cmṡ Oe) at Tf = 0.09 mm can be obtained, which is about 10.8 times as large as that of traditional PZT/Terfenol-D composite with a weak ME coupling at zero bias Hdc,zero. Furthermore, when Tf increases from 0.03 mm to 0.18 mm, the maximum MEVC increases nearly linearly with the increased Tf at Hdc,opti. Additionally, the experimental results demonstrate the ME response for multiferroic heterostructures spreads over a wide magnetic dc bias operating range. The excellent ME performance provides a promising and practicable application for both highly sensitive magnetic field sensors without bias and ME energy harvesters.

  20. Atomically engineered ferroic layers yield a room-temperature magnetoelectric multiferroic

    Science.gov (United States)

    Mundy, Julia A.; Brooks, Charles M.; Holtz, Megan E.; Moyer, Jarrett A.; Das, Hena; Rébola, Alejandro F.; Heron, John T.; Clarkson, James D.; Disseler, Steven M.; Liu, Zhiqi; Farhan, Alan; Held, Rainer; Hovden, Robert; Padgett, Elliot; Mao, Qingyun; Paik, Hanjong; Misra, Rajiv; Kourkoutis, Lena F.; Arenholz, Elke; Scholl, Andreas; Borchers, Julie A.; Ratcliff, William D.; Ramesh, Ramamoorthy; Fennie, Craig J.; Schiffer, Peter; Muller, David A.; Schlom, Darrell G.

    2016-09-01

    Materials that exhibit simultaneous order in their electric and magnetic ground states hold promise for use in next-generation memory devices in which electric fields control magnetism. Such materials are exceedingly rare, however, owing to competing requirements for displacive ferroelectricity and magnetism. Despite the recent identification of several new multiferroic materials and magnetoelectric coupling mechanisms, known single-phase multiferroics remain limited by antiferromagnetic or weak ferromagnetic alignments, by a lack of coupling between the order parameters, or by having properties that emerge only well below room temperature, precluding device applications. Here we present a methodology for constructing single-phase multiferroic materials in which ferroelectricity and strong magnetic ordering are coupled near room temperature. Starting with hexagonal LuFeO3—the geometric ferroelectric with the greatest known planar rumpling—we introduce individual monolayers of FeO during growth to construct formula-unit-thick syntactic layers of ferrimagnetic LuFe2O4 (refs 17, 18) within the LuFeO3 matrix, that is, (LuFeO3)m/(LuFe2O4)1 superlattices. The severe rumpling imposed by the neighbouring LuFeO3 drives the ferrimagnetic LuFe2O4 into a simultaneously ferroelectric state, while also reducing the LuFe2O4 spin frustration. This increases the magnetic transition temperature substantially—from 240 kelvin for LuFe2O4 (ref. 18) to 281 kelvin for (LuFeO3)9/(LuFe2O4)1. Moreover, the ferroelectric order couples to the ferrimagnetism, enabling direct electric-field control of magnetism at 200 kelvin. Our results demonstrate a design methodology for creating higher-temperature magnetoelectric multiferroics by exploiting a combination of geometric frustration, lattice distortions and epitaxial engineering.

  1. A simple model for the magnetoelectric interaction in multiferroics

    International Nuclear Information System (INIS)

    Filho, Cesar J Calderon; Barberis, Gaston E

    2011-01-01

    The (anti)ferromagnetic and ferroelectric transitions in some multiferroic compounds seem to be strongly correlated. Even for systems that do not show spontaneous ferroelectricity such as the LiMPO 4 (M = Mn, Fe, Co, Ni) compounds, the coupling between magnetic and electric degrees of freedom is evident experimentally. Here, we present a simple numerical calculation to simulate this coupling that leads to the two transitions. We assume a magnetic sublattice consisting of classical magnetic moments coupled to a separated nonmagnetic sublattice consisting of classical electric dipoles. The coupling between them is realized through a phenomenological spin-lattice Hamiltonian, and the solution is obtained using the Monte Carlo technique. In the simplest version, the magnetic system is 2D Ising (anti)ferromagnetic lattice, with nearest neighbors interactions only, and the electric moments are permanent moments, coupled electrically. Within this approximation, the second order magnetic transition induces ferroelectricity in the electric dipoles. We show that these calculations can be extended to other magnetic systems, (x-y model and 3D Heisenberg) and to systems where the electric moments are created by strains, generated via spin-lattice coupling, so the model can be applied to model realistic systems such as the olivines mentioned above.

  2. Anisotropic magnetoelectric characteristics in five-layer magnetization-graded multiferroic composites

    Directory of Open Access Journals (Sweden)

    Lei Chen

    2017-05-01

    Full Text Available We investigate the anisotropic magnetoelectric(ME characteristics for the five-layer magnetization-graded multiferroic composites(MGMC. The magnetic anisotropy and corresponding anisotropic magnetomechanical effect, demagnetization effect and magneto-mechanical damping’s dependence on magnetic field direction result in an obvious anisotropic ME coupling effect. The experimental results show that ME voltage coefficient in H33 mode is remarkably larger than the other ones (H11, H31 and H13 over the whole Hdc range. Correspondingly, ∂VME/∂Hdc arrives about 420mV/Oe at an optimum bias magnetic field of 46Oe, which is approximately 40 times larger than that of the previous reported composite. Furthermore, it also demonstrates an obvious angular dependence on dc magnetic field. Taking advantage of these specifications, the MGMC can be used to detect weak dc magnetic field and its spatial orientation.

  3. Controlled self-assembly of multiferroic core-shell nanoparticles exhibiting strong magneto-electric effects

    Energy Technology Data Exchange (ETDEWEB)

    Sreenivasulu, Gollapudi; Hamilton, Sean L.; Lehto, Piper R.; Srinivasan, Gopalan, E-mail: srinivas@oakland.edu [Physics Department, Oakland University, Rochester, Michigan 48309-4401 (United States); Popov, Maksym [Physics Department, Oakland University, Rochester, Michigan 48309-4401 (United States); Radiophysics Department, Taras Shevchenko National University of Kyiv, Kyiv 01601 (Ukraine); Chavez, Ferman A. [Chemistry Department, Oakland University, Rochester, Michigan 48309-4401 (United States)

    2014-02-03

    Ferromagnetic-ferroelectric composites show strain mediated coupling between the magnetic and electric sub-systems due to magnetostriction and piezoelectric effects associated with the ferroic phases. We have synthesized core-shell multiferroic nano-composites by functionalizing 10–100 nm barium titanate and nickel ferrite nanoparticles with complementary coupling groups and allowing them to self-assemble in the presence of a catalyst. The core-shell structure was confirmed by electron microscopy and magnetic force microscopy. Evidence for strong strain mediated magneto-electric coupling was obtained by static magnetic field induced variations in the permittivity over 16–18 GHz and polarization and by electric field induced by low-frequency ac magnetic fields.

  4. Multiferroic and magnetoelectric properties of Ba{sub 0.85}Ca{sub 0.15}Zr{sub 0.1}Ti{sub 0.9}O{sub 3}–CoFe{sub 2}O{sub 4} core–shell nanocomposite

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, Ajith S; Lekha, C.S. Chitra; Vivek, S. [Department of Physics, Central University of Kerala, Kasaragod 671314 (India); Saravanan, Venkata [Department of Physics, Central University of Tamil Nadu, Thiruvarur 610101 (India); Nandakumar, K. [School of Pure and Applied Physics, Mahatma Gandhi University, Kottayam 686560 (India); Nair, Swapna S., E-mail: swapna.s.nair@gmail.com [Department of Physics, Central University of Kerala, Kasaragod 671314 (India)

    2016-11-15

    Lead-free magnetoelectric (ME) composites with remarkable ME coupling are required for the realization of eco-friendly multifunctional devices. This work demonstrates the ME properties of Ba{sub 0.85}Ca{sub 0.15}Zr{sub 0.1}Ti{sub 0.9}O{sub 3}–CoFe{sub 2}O{sub 4} (BCZT–CFO) core–shell composites synthesized via co-sol–gel technique. Room temperature ferroelectric and ferromagnetic characterization have shown that the samples are magnetic and ferroelectric along with an adequate magnetoelectric coupling of 12.15 mV/(cm Oe). The strong dependence of electric parameters on applied magnetic DC bias fields demonstrated in ferroelectric and magnetoelectric measurements provide a framework for the development of potential magnetoelectric devices. Also, the high sensitivity of magnetoelectric coupling towards the applied AC magnetic field can be used for its application in magnetoelectric sensors. - Highlights: • The magnetoelectric multiferroic BCZT–CFO nanocomposite is synthesized via sol–gel route. • The XRD measurements show no phases other than BCZT and CFO. • The microstructure analysis employing TEM indicates that the majority of particles formed are having core–shell structure. • The capacitance, resistance and ferroelectric polarization are magnetically tunable. • The composite showed a high magnetoelectric response.

  5. Magnetoelectric coupling in multiferroic BaTiO3-CoFe2O4 composite nanofibers via electrospinning

    Science.gov (United States)

    Fu, Bi; Lu, Ruie; Gao, Kun; Yang, Yaodong; Wang, Yaping

    2015-07-01

    Magnetoelectric (ME) coupling in Pb-based multiferroic composites has been widely investigated due to the excellent piezoelectric property of lead zirconate titanate (PZT). In this letter, we report a strategy to create a hybrid Pb-free ferroelectric and ferromagnetic material and detect its ME coupling at the nanoscale. Hybrid Pb-free multiferroic BaTiO3-CoFe2O4 (BTO-CFO) composite nanofibers (NFs) were generated by sol-gel electrospinning. The perovskite structure of BTO and the spinel structure of CFO nanograins were homogenously distributed in the composite NFs and verified by bright-field transmission electron microscopy observations along the perovskite [111] zone axis. Multiferroicity was confirmed by amplitude-voltage butterfly curves and magnetic hysteresis loops. ME coupling was observed in terms of a singularity on a dM/dT curve at the ferroelectric Curie temperature (TC) of BaTiO3. The lateral ME coefficient was investigated by the evolution of the piezoresponse under an external magnetic field of 1000 Oe and was estimated to be α31 =0.78× 104 \\text{mV cm}-1 \\text{Oe}-1 . These findings could enable the creation of nanoscale Pb-free multiferroic composite devices.

  6. Magnetic reconstruction induced magnetoelectric coupling and spin-dependent tunneling in Ni/KNbO_3/Ni multiferroic tunnel junctions

    International Nuclear Information System (INIS)

    Zhang, Hu; Dai, Jian-Qing; Song, Yu-Min

    2016-01-01

    We investigate the magnetoelectric coupling and spin-polarized tunneling in Ni/KNbO_3/Ni multiferroic tunnel junctions with asymmetric interfaces based on density functional theory. The junctions have two stable polarization states. We predict a peculiar magnetoelectric effect in such junctions originating from the magnetic reconstruction of Ni near the KO-terminated interface. This reconstruction is induced by the reversal of the ferroelectric polarization of KNbO_3. Furthermore, the change in the magnetic ordering filters the spin-dependent current. This effect leads to a change in conductance by about two orders of magnitude. As a result we obtain a giant tunneling electroresistance effect. In addition, there exist sizable tunneling magnetoresistance effects for two polarization states. - Highlights: • We study the ME coupling and electron tunneling in Ni/KNbO_3/Ni junctions. • There is magnetic reconstruction of Ni atoms near the KO-terminated interface. • A peculiar magnetoelectric coupling effect is obtained. • Predicted giant tunneling electroresistance effects.

  7. Strong and anisotropic magnetoelectricity in composites of magnetostrictive Ni and solid-state grown lead-free piezoelectric BZT–BCT single crystals

    Directory of Open Access Journals (Sweden)

    Haribabu Palneedi

    2017-03-01

    Full Text Available Aimed at developing lead-free magnetoelectric (ME composites with performances as good as lead (Pb-based ones, this study employed (001 and (011 oriented 82BaTiO3-10BaZrO3-8CaTiO3 (BZT–BCT piezoelectric single crystals, fabricated by the cost-effective solid-state single crystal growth (SSCG method, in combination with inexpensive, magnetostrictive base metal Nickel (Ni. The off-resonance, direct ME coupling in the prepared Ni/BZT–BCT/Ni laminate composites was found to be strongly dependent on the crystallographic orientation of the BZT–BCT single crystals, as well as the applied magnetic field direction. Larger and anisotropic ME voltage coefficients were observed for the composite made using the (011 oriented BZT–BCT single crystal. The optimized ME coupling of 1 V/cm Oe was obtained from the Ni/(011 BZT–BCT single crystal/Ni composite, in the d32 mode of the single crystal, when a magnetic field was applied along its [100] direction. This performance is similar to that reported for the Ni/Pb(Mg1/3Nb2/3O3-Pb(Zr,TiO3 (PMN–PZT single crystal/Ni, but larger than that obtained from the Ni/Pb(Zr,TiO3 ceramic/Ni composites. The results of this work demonstrate that the use of lead-free piezoelectric single crystals with special orientations permits the selection of desired anisotropic properties, enabling the realization of customized ME effects in composites.

  8. Magnetoelectric coupling and spin-dependent tunneling in Fe/PbTiO3/Fe multiferroic heterostructure with a Ni monolayer inserted at one interface

    International Nuclear Information System (INIS)

    Dai, Jian-Qing; Zhang, Hu; Song, Yu-Min

    2015-01-01

    We report on first-principles calculations of a Ni monolayer inserted at one interface in the epitaxial Fe/PbTiO 3 /Fe multiferroic heterostructure, focusing on the magnetoelectric coupling and the spin-dependent transport properties. The results of magnetoelectric coupling calculations reveal an attractive approach to realize cumulative magnetoelectric effects in the ferromagnetic/ferroelectric/ferromagnetic superlattices. The underlying physics is attributed to the combinations of several different magnetoelectric coupling mechanisms such as interface bonding, spin-dependent screening, and different types of magnetic interactions. We also demonstrate that inserting a Ni monolayer at one interface in the Fe/PbTiO 3 /Fe multiferroic tunnel junction is an efficient method to produce considerable tunneling electroresistance effect by modifying the tunnel potential barrier and the interfacial electronic structure. Furthermore, coexistence of tunneling magnetoresistance and tunneling electroresistance leads to the emergence of four distinct resistance states, which can be served as a multistate-storage device. The complicated influencing factors including bulk properties of the ferromagnetic electrodes, decay rates of the evanescent states in the tunnel barrier, and the specific interfacial electronic structure provide us promising opportunities to design novel multiferroic tunnel junctions with excellent performances

  9. Magnetoelectric coupling and spin-dependent tunneling in Fe/PbTiO{sub 3}/Fe multiferroic heterostructure with a Ni monolayer inserted at one interface

    Energy Technology Data Exchange (ETDEWEB)

    Dai, Jian-Qing, E-mail: djqkust@sina.com; Zhang, Hu; Song, Yu-Min [School of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093 (China)

    2015-08-07

    We report on first-principles calculations of a Ni monolayer inserted at one interface in the epitaxial Fe/PbTiO{sub 3}/Fe multiferroic heterostructure, focusing on the magnetoelectric coupling and the spin-dependent transport properties. The results of magnetoelectric coupling calculations reveal an attractive approach to realize cumulative magnetoelectric effects in the ferromagnetic/ferroelectric/ferromagnetic superlattices. The underlying physics is attributed to the combinations of several different magnetoelectric coupling mechanisms such as interface bonding, spin-dependent screening, and different types of magnetic interactions. We also demonstrate that inserting a Ni monolayer at one interface in the Fe/PbTiO{sub 3}/Fe multiferroic tunnel junction is an efficient method to produce considerable tunneling electroresistance effect by modifying the tunnel potential barrier and the interfacial electronic structure. Furthermore, coexistence of tunneling magnetoresistance and tunneling electroresistance leads to the emergence of four distinct resistance states, which can be served as a multistate-storage device. The complicated influencing factors including bulk properties of the ferromagnetic electrodes, decay rates of the evanescent states in the tunnel barrier, and the specific interfacial electronic structure provide us promising opportunities to design novel multiferroic tunnel junctions with excellent performances.

  10. Magnetoelectric coupling in multiferroic heterostructure of rf-sputtered Ni–Mn–Ga thin film on PMN–PT

    International Nuclear Information System (INIS)

    Teferi, M.Y.; Amaral, V.S.; Lounrenco, A.C.; Das, S.; Amaral, J.S.; Karpinsky, D.V.; Soares, N.; Sobolev, N.A.; Kholkin, A.L.; Tavares, P.B.

    2012-01-01

    In this paper, we report a preparation of multiferroic heterostructure from thin film of Ni–Mn–Ga (NMG) alloy and lead magnesium niobate–lead titanate (PMN–PT) with effective magnetoelectric (ME) coupling between the film as ferromagnetic material and PMN–PT as piezoelectric material. The heterostructure was prepared by relatively low temperature (400 °C) deposition of the film on single crystal of piezoelectric PMN–PT substrate using rf magnetron co-sputtering of Ni 50 Mn 50 and Ni 50 Ga 50 targets. Magnetic measurements by Superconducting Quantum Interference Design (SQIUD) Magnetometer and Vibrating Sample Magnetometer (VSM) on the film revealed that the film is in ferromagnetically ordered martensitic state at room temperature with saturation magnetization of ∼240 emu/cm 3 and Curie temperature of ∼337 K. Piezoresponse force microscopy (PFM) measurement done at room temperature on the substrate showed the presence of expected hysteresis loop confirming the stability of the piezoelectric state of the substrate after deposition. Room temperature ME voltage coefficient (α ME ) of the heterostructure was measured as a function of applied bias dc magnetic field in Longitudinal–Transverse (L–T) ME coupling mode by lock-in technique. A maximum ME coefficient α ME of 3.02 mV/cm Oe was measured for multiferroic NMG/PMN–PT heterostructure which demonstrates that there is ME coupling between the film as ferromagnetic material and PMN–PT as piezoelectric material. - Highlights: ► Multiferroic NMG/PMN–PT heterostructure prepared by depositing NMG alloy thin film on PMN–PT substrate. ► The film is in ferromagnetically ordered martensite state at room temperature. ► The substrate maintains its piezoelectric state after deposition. ► The heterostructure exhibits ME effect with maximum of α ME of 3.02 mV/cm Oe.

  11. Magnetoelectric excitations in multiferroic Ni.sub.3./sub.TeO.sub.6./sub.

    Czech Academy of Sciences Publication Activity Database

    Skiadopoulou, Styliani; Borodavka, Fedir; Kadlec, Christelle; Kadlec, Filip; Retuerto, M.; Deng, Z.; Greenblatt, M.; Kamba, Stanislav

    2017-01-01

    Roč. 95, č. 18 (2017), 1-6, č. článku 184435. ISSN 2469-9950 R&D Projects: GA MŠk(CZ) LH15122; GA ČR GA15-08389S Institutional support: RVO:68378271 Keywords : multiferroics * electromagnons * THz * Raman * IR spectroscopy Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 3.836, year: 2016

  12. Effect of double layer thickness on magnetoelectric coupling in multiferroic BaTiO3-Bi0.95Gd0.05FeO3 multilayers

    Science.gov (United States)

    Hohenberger, S.; Lazenka, V.; Temst, K.; Selle, S.; Patzig, C.; Höche, T.; Grundmann, M.; Lorenz, M.

    2018-05-01

    The effect of double-layer thickness and partial substitution of Bi3+ by Gd3+ is demonstrated for multiferroic BaTiO3–BiFeO3 2–2 heterostructures. Multilayers of 15 double layers of BaTiO3 and Bi0.95Gd0.05FeO3 were deposited onto (0 0 1) oriented SrTiO3 substrates by pulsed laser deposition with various double layer thicknesses. X-ray diffraction and high resolution transmission electron microscopy investigations revealed a systematic strain tuning with layer thickness via coherently strained interfaces. The multilayers show increasingly enhanced magnetoelectric coupling with reduced double layer thickness. The maximum magnetoelectric coupling coefficient was measured to be as high as 50.8 V cm‑1 Oe‑1 in 0 T DC bias magnetic field at room temperature, and 54.9 V cm‑1 Oe‑1 above 3 T for the sample with the thinnest double layer thickness of 22.5 nm. This enhancement is accompanied by progressively increasing perpendicular magnetic anisotropy and compressive out-of-plane strain. To understand the origin of the enhanced magnetoelectric coupling in such multilayers, the temperature and magnetic field dependency of is discussed. The magnetoelectric performance of the Gd3+ substituted samples is found to be slightly enhanced when compared to unsubstituted BaTiO3–BiFeO3 multilayers of comparable double-layer thickness.

  13. Room-temperature paramagnetoelectric effect in magnetoelectric multiferroics Pb(Fe.sub.1/2./sub.Nb.sub.1/2./sub.)O.sub.3./sub. and its solid solution with PbTiO.sub.3./sub.

    Czech Academy of Sciences Publication Activity Database

    Laguta, Valentyn; Morozovska, A. N.; Eliseev, E. A.; Raevski, I. P.; Raevskaya, S. I.; Sitalo, E.I.; Prosandeev, S. A.; Bellaiche, L.

    2016-01-01

    Roč. 51, č. 11 (2016), s. 5330-5342 ISSN 0022-2461 R&D Projects: GA ČR GA13-11473S Institutional support: RVO:68378271 Keywords : multiferroic * antiferromagnetic * ferroelectrics * magnetoelectric effect * Landau theory Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.599, year: 2016

  14. Performance of magnetoelectric PZT/Ni multiferroic system for energy harvesting application

    Science.gov (United States)

    Gupta, Reema; Tomar, Monika; Kumar, Ashok; Gupta, Vinay

    2017-03-01

    Magnetoelectric (ME) coefficient of Lead Zirconium Titanate (PZT) thin films has been probed for possible energy harvesting applications. Single phase PZT thin films have been deposited on nickel substrate (PZT/Ni) using pulsed laser deposition (PLD) technique. The effect of PLD process parameters on the ME coupling coefficient in the prepared systems has been investigated. The as grown PZT films on Ni substrate were found to be polycrystalline with improved ferroelectric and ferromagnetic properties. The electrical switching behavior of the PZT thin films were verified using capacitance voltage measurements, where well defined butterfly loops were obtained. The ME coupling coefficient was estimated to be in the range of 94.5 V cm-1 Oe-1-130.5 V cm-1 Oe-1 for PZT/Ni system, which is large enough for harnessing electromagnetic energy for subsequent applications.

  15. Rich magnetoelectric phase diagrams of multiferroic single-crystal α -NaFeO2

    Science.gov (United States)

    Terada, Noriki; Ikedo, Yuta; Sato, Hirohiko; Khalyavin, Dmitry D.; Manuel, Pascal; Miyake, Atsushi; Matsuo, Akira; Tokunaga, Masashi; Kindo, Koichi

    2017-07-01

    The magnetic and dielectric properties of the multiferroic triangular lattice magnet compound α -NaFeO2 were studied by magnetization, specific heat, dielectric permittivity, and pyroelectric current measurements and by neutron diffraction experiments using single crystals grown by a hydrothermal synthesis method. This work produced magnetic field (in the monoclinic a b -plane, Ba b, and along the c*-axis, Bc) versus temperature magnetic phase diagrams, including five and six magnetically ordered phases in Ba b and along Bc, respectively. In zero magnetic field, two spin-density-wave orderings with different k vectors—(0 ,q ,1/2 ) in phase I and (qa,qb,qc ) in phase II—appeared at T =9.5 and 8.25 K, respectively. Below T =5 K, a commensurate order with k =(0.5 ,0 ,0.5 ) was stabilized as the ground state in phase III. Both Ba b≥3 T and Bc≥5 T were found to induce ferroelectric phases at the lowest temperature (2 K), with an electric polarization that was not confined to any highly symmetric directions in phases IVa b (3.3 ≤Ba b≤8.5 T), Va b (8.5 ≤Ba b≤13.6 T), IVc (5.0 ≤Bc≤8.5 T), and Vc (8.5 ≤Bc≤13.5 T). In phase VIc, within a narrow temperature region in Bc, the polarization was confined to the a b plane. For each of the ferroelectric phases, the k vector was (qa,qb,qc ), and noncollinear structures were identified, including a general spiral in IVa b an a b cycloid in IVc and Vc, and a proper screw in VIc, along with a triclinic 11' magnetic point group allowing polarization in the general direction. Comparing the polarization direction to the magnetic structures in the ferroelectric phases, we conclude that the extended inverse Dzyaloshinskii-Moriya mechanism expressed by the orthogonal components p1∝ri j×(Si×Sj) and p2∝Si×Sj can explain the polarization directions. Based on calculations incorporating exchange interactions up to fourth-nearest-neighbor (NN) couplings, we infer that competition among antiferromagnetic second NN

  16. Piezoelectric control of magnetoelectric coupling driven non-volatile memory switching and self cooling effects in FE/FSMA multiferroic heterostructures

    Science.gov (United States)

    Singh, Kirandeep; Kaur, Davinder

    2017-02-01

    The manipulation of magnetic states and materials' spin degree-of-freedom via a control of an electric (E-) field has been recently pursued to develop magnetoelectric (ME) coupling-driven electronic data storage devices with high read/write endurance, fast dynamic response, and low energy dissipation. One major hurdle for this approach is to develop reliable materials which should be compatible with prevailing silicon (Si)-based complementary metal-oxide-semiconductor (CMOS) technology, simultaneously allowing small voltage for the tuning of magnetization switching. In this regard, multiferroic heterostructures where ferromagnetic (FM) and ferroelectric (FE) layers are alternatively grown on conventional Si substrates are promising as the piezoelectric control of magnetization switching is anticipated to be possible by an E-field. In this work, we study the ferromagnetic shape memory alloys based PbZr0.52Ti0.48O3/Ni50Mn35In15 (PZT/Ni-Mn-In) multiferroic heterostructures, and investigate their potential for CMOS compatible non-volatile magnetic data storage applications. We demonstrate the voltage-impulse controlled nonvolatile, reversible, and bistable magnetization switching at room temperature in Si-integrated PZT/Ni-Mn-In thin film multiferroic heterostructures. We also thoroughly unveil the various intriguing features in these materials, such as E-field tuned ME coupling and magnetocaloric effect, shape memory induced ferroelectric modulation, improved fatigue endurance as well as Refrigeration Capacity (RC). This comprehensive study suggests that these novel materials have a great potential for the development of unconventional nanoscale memory and refrigeration devices with self-cooling effect and enhanced refrigeration efficiency, thus providing a new venue for their applications.

  17. Magnetoelectric effect in antiferromagnetic multiferroic Pb(Fe.sub.1/2./sub. N b.sub.1/2./sub.)O.sub.3./sub. and its solid solutions with PbTi O.sub.3./sub.

    Czech Academy of Sciences Publication Activity Database

    Laguta, Valentyn; Stephanovich, V. A.; Raevski, I. P.; Raevskaya, S. I.; Titov, V.V.; Smotrakov, V. G.; Eremkin, V. V.

    2017-01-01

    Roč. 95, č. 1 (2017), 1-13, č. článku 014207. ISSN 1098-0121 R&D Projects: GA MŠk LO1409; GA MŠk LM2015088; GA ČR GA13-11473S Institutional support: RVO:68378271 Keywords : multiferroic * antiferromagnetic * ferroelectrics * magnetoelectric effect * Landau theory Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.)

  18. TE and TM modes polaritons in multilayer system comprise of a PML-type magnetoelectric multiferroics and ferroelectrics

    International Nuclear Information System (INIS)

    Gunawan, Vincensius; Widiyandari, Hendri

    2016-01-01

    In this paper, we report our study on both bulk and surface polaritons generated in Multilayer system. The multilayer consists of ferroelectric and multiferroic with canted spins structure. The effective medium approximation is employed to derive the dispersion relation for both bulk and surface modes. Surface and bulk polaritons are calculated numerically for the case of Transverse electric (TE) and Transverse magnetic (TM) modes. Example results are presented using parameters appropriate for BaMnF 4 /BaAl 2 O 4 . We found in both TE and TM modes, that the region where the surface modes may exist is affected by the volume fraction of the multiferroics. The region of the surface modes decrease when the volume fraction of the multiferroic is reduced. This region decrement suppress the surface polariton curves which result in shortening the surface modes curves. (paper)

  19. Magnetoelectric coupling study in multiferroic Pb(Fe0.5Nb0.5)O3 ceramics through small and large electric signal standard measurements

    International Nuclear Information System (INIS)

    Raymond, Oscar; Siqueiros, Jesus M.; Font, Reynaldo; Portelles, Jorge

    2011-01-01

    Multifunctional multiferroic materials such as the single phase compound Pb(Fe 0.5 Nb 0.5 )O 3 (PFN), where ferroelectric and antiferromagnetic order coexist, are very promising and have great interest from the academic and technological points of view. In this work, coupling of the ferroelectric and magnetic moments is reported. For this study, a combination of the small signal response using the impedance spectroscopy technique and the electromechanical resonance method with the large signal response through standard ferroelectric hysteresis measurement, has been used with and without an applied magnetic field. The measurements to determine the electrical properties of the ceramic were performed as functions of the bias and poling electric fields. A simultaneous analysis of the complex dielectric constant ε-tilde, impedance Z-tilde, electric modulus M-tilde, admittance Y-tilde, and the electromechanical parameters and coupling factors is presented. The results are correlated with a previous study of structural, morphological, small signal dielectric frequency-temperature response, and the ferroelectric hysteretic, magnetic and magnetodielectric behaviors. The observed shifts of the resonance and antiresonance frequency values can be associated with change of the ferroelectric domain size favored by the readjustment of the oxygen octahedron when the magnetic field is applied. From P-E hysteresis loops obtained without and with an external applied magnetic field, a dc magnetoelectric coupling effect with maximum value of 4 kV/cm T (400 mV/cm Oe) was obtained.

  20. Surface and bulk polaritons in a PML-type magnetoelectric multiferroic with canted spins: TE and TM polarization

    Energy Technology Data Exchange (ETDEWEB)

    Gunawan, V; Stamps, R L, E-mail: slamev01@student.uwa.edu.au [School of Physics M013, University of Western Australia, 35 Stirling Highway, Crawley, Western Australia 6009 (Australia)

    2011-03-16

    We present a theory for surface polaritons on ferroelectric-antiferromagnetic materials with canted spin structure. A small uniform canted moment is allowed, resulting in a weak ferromagnetism directed in the plane parallel to the surface. Surface and bulk polariton modes for a semi-infinite film are calculated for the case of transverse electric (TE) and transverse magnetic (TM) polarization. Example results are presented using parameters appropriate for BaMnF{sub 4}. We find that the surface modes are non-reciprocal for the TE polarization due to the magnetoelectric interaction, and the non-reciprocity can be controlled by an applied electric field. Example results for attenuated total reflection (ATR) are calculated. The magnetoelectric interaction also gives rise to 'leaky' surface modes in the case of TM polarization. These are pseudo-surface waves that exist in the pass band, and dissipate energy into the bulk of the material. We show that these pseudo-surface mode frequencies and properties can be modified by temperature and the application of external electric or magnetic fields.

  1. Collaborative Research: Polymeric Multiferroics

    Energy Technology Data Exchange (ETDEWEB)

    Ren, Shenqiang [Temple Univ., Philadelphia, PA (United States). College of Engineering

    2017-04-20

    The goal of this project is to investigate room temperature magnetism and magnetoelectric coupling of polymeric multiferroics. A new family of molecular charge-transfer crystals has been emerged as a fascinating opportunity for the development of all-organic electrics and spintronics due to its weak hyperfine interaction and low spin-orbit coupling; nevertheless, direct observations of room temperature magnetic spin ordering have yet to be accomplished in organic charge-transfer solids. Furthermore, room temperature magnetoelectric coupling effect hitherto known multiferroics, is anticipated in organic donor-acceptor complexes because of magnetic field effects on charge-transfer dipoles, yet this is also unexplored. The PI seeks to fundamental understanding of the control of organic crystals to demonstrate and explore room temperature multiferroicity. The experimental results have been verified through the theoretical modeling.

  2. Lead-Free Piezoelectrics

    CERN Document Server

    Nahm, Sahn

    2012-01-01

    Ecological restrictions in many parts of the world are demanding the elimination of Pb from all consumer items. At this moment in the piezoelectric ceramics industry, there is no issue of more importance than the transition to lead-free materials. The goal of Lead-Free Piezoelectrics is to provide a comprehensive overview of the fundamentals and developments in the field of lead-free materials and products to leading researchers in the world. The text presents chapters on demonstrated applications of the lead-free materials, which will allow readers to conceptualize the present possibilities and will be useful for both students and professionals conducting research on ferroelectrics, piezoelectrics, smart materials, lead-free materials, and a variety of applications including sensors, actuators, ultrasonic transducers and energy harvesters.

  3. Lead-free piezoceramics.

    Science.gov (United States)

    Saito, Yasuyoshi; Takao, Hisaaki; Tani, Toshihiko; Nonoyama, Tatsuhiko; Takatori, Kazumasa; Homma, Takahiko; Nagaya, Toshiatsu; Nakamura, Masaya

    2004-11-04

    Lead has recently been expelled from many commercial applications and materials (for example, from solder, glass and pottery glaze) owing to concerns regarding its toxicity. Lead zirconium titanate (PZT) ceramics are high-performance piezoelectric materials, which are widely used in sensors, actuators and other electronic devices; they contain more than 60 weight per cent lead. Although there has been a concerted effort to develop lead-free piezoelectric ceramics, no effective alternative to PZT has yet been found. Here we report a lead-free piezoelectric ceramic with an electric-field-induced strain comparable to typical actuator-grade PZT. We achieved this through the combination of the discovery of a morphotropic phase boundary in an alkaline niobate-based perovskite solid solution, and the development of a processing route leading to highly textured polycrystals. The ceramic exhibits a piezoelectric constant d33 (the induced charge per unit force applied in the same direction) of above 300 picocoulombs per newton (pC N(-1)), and texturing the material leads to a peak d33 of 416 pC N(-1). The textured material also exhibits temperature-independent field-induced strain characteristics.

  4. Magnetoelectric effect in lead free piezoelectric Bi{sub 1/2}Na{sub 1/2}TiO{sub 3}–modified CFO based magnetostrictive (Co{sub 0.6}Zn{sub 0.4}Fe{sub 1.7} Mn{sub 0.3}O{sub 4}) particulate nanocomposite prepared by sol-gel method

    Energy Technology Data Exchange (ETDEWEB)

    Thakur, Megha [Nanotechnology Research Laboratory, Desh Bhagat University, Mandi Govindgarh 147330, Punjab (India); Sharma, Puneet [School of Physics & Materials Science, Thapar University, Patiala 147004, Punjab (India); Kumari, Mukesh; Singh, Anoop Pratap [Magnetics & Advanced ceramics laboratory, Department of Physics, Indian Institute of Technology, Delhi 110016 (India); Tyagi, Mintu, E-mail: mintutyagi@deshbhagatuniversity.in [Nanotechnology Research Laboratory, Desh Bhagat University, Mandi Govindgarh 147330, Punjab (India)

    2017-03-15

    Lead free magnetoelectric composites that comprise Co{sub 0.6}Zn{sub 0.4}Fe{sub 1.7}Mn{sub 0.3}O{sub 4} (CZFMO) and Bi{sub 1/2}Na{sub 1/2}TiO{sub 3} (BNT) were synthesized using sol-gel method and it's structural, dielectric, magnetic, ferroelectric and magnetoelectric (ME) properties were studied. The X-ray diffraction displayed the single phase formation of parent phases and the presence of two phases in the composites. The temperature dependent dielectric spectra of samples indicates two anomalies at ~220 °C and ~320 °C were ascribed to ferroelectric to antiferroelectric, and anti-ferroelectric to paraelectric phase transitions respectively. Room temperature (RT) magnetic measurements show that composites are soft magnetic. The composite with x=0.2, showed the large value of ME voltage coefficient (α{sub E})~58 mV/cmOe. Moreover, these ME composites provide a great opportunity as potential lead free systems for multifunctional devices. - Highlights: • In this work, Modified CFO based lead free particulate nanocomposites with significantly high value of ME coupling coefficient α{sub E} ~52 mV/cmOe have been prepared. • This sufficient high value of α{sub E} in such composites is obtained by manipulating/improving the piezomagnetic component. • The studies on BNT based particulate ME composites are very scarce in literature. However, no report is available in on the modified CFO based lead free particulate composites.

  5. Multiferroic magnetoelectric coupling effect of bilayer La1.2Sr1.8Mn2O7/PbZr0.3Ti0.7O3 complex thin film

    Science.gov (United States)

    Liang, K.; Zhou, P.; Ma, Z. J.; Qi, Y. J.; Mei, Z. H.; Zhang, T. J.

    2017-05-01

    Magnetoelectric (ME) coupling effect of 2-2-type ferromagnetic/ferroelectric bi-layer multiferroic epitaxial thin film (La1.2Sr1.8Mn2O7/PbZr0.3Ti0.7O3, LSMO/PZT) on SrRuO3 (SRO) substrate is investigated systematically by using Landau-Ginzburg-Devonshire (LGD) thermodynamic theory and modified constitutive equations. The calculating results clarify the detail relationships between ME coupling response and the residual strain, the volume fraction of constituent phases, the interface coupling coefficients, the magnetic field and the temperature. It also shows that improved ME coupling response can be modulated by these parameters. External magnetic fields (H1) induced ME coupling effect could be enhanced around Curie Temperature (Tc) of ferromagnetic phase and ME voltage coefficient (αE31) approaches a maximum at H1 ∼ 4.5 kOe near Tc. The remarkable variations of ME coupling response can be used to provide useful guidelines on the design of multifunctional devices.

  6. "Metamagnetoelectric" effect in multiferroics

    Science.gov (United States)

    Fouokeng, G. C.; Fodouop, F. Kuate; Tchoffo, M.; Fai, L. C.; Randrianantoandro, N.

    2018-05-01

    We present a theoretical calculation of magnetoelectric properties in a quasi-two dimensional spin chain externally controlled by a static electric field in y-direction and magnetic field in z-direction. Given the diversity of properties in functional materials and their applications in physics, the multiferroic model is investigated. By using the Fermi-Dirac statistics of quantum gases and the Landau theory, we assess the effects of the Dzyaloshinskii-Moriya interaction and the electric polarization on the magnetoelectric coupling that induces at low temperature the "metamagnetoelectric" effet, and likewise affects the ferroelectricity induced through symmetry mechanisms and magnetic properties of the multiferroic system. In fact, the variation of the induced polarisation due to spin arrangement through the Dzyaloshinskii-Moriya interaction gives rise to a multistep interdependent metamagnetic and metaelectric transitions which are settled up by the corresponding Dzyaloshinskii-Moriya parameter and the system then exhibits a spin gap that results from an electric and a magnetic demagnetization field range. This metamagnetoelectric effect observed in these multiferroic materials model is seem to be highly tunable via the external electric and magnetic fields and thus can be crucial in the design of new mechanisms for the processing and storage of data and other spintronic applications.

  7. Electric-field control of electronic transport properties and enhanced magnetoresistance in La0.7Sr0.3MnO3/0.5BaZr0.2Ti0.8O3-0.5Ba0.7Ca0.3TiO3 lead-free multiferroic structures

    Science.gov (United States)

    Yan, Jian-Min; Gao, Guan-Yin; Liu, Yu-Kuai; Wang, Fei-Fei; Zheng, Ren-Kui

    2017-10-01

    We report the fabrication of lead-free multiferroic structures by depositing ferromagnetic La0.7Sr0.3MnO3 (LSMO) polycrystalline films on polished 0.5BaZr0.2Ti0.8O3-0.5Ba0.7Ca0.3TiO3 (BZT-BCT) piezoelectric ceramic substrates. By applying electric fields to the BZT-BCT along the thickness direction, the resistivity of LSMO films can be effectively manipulated via the piezoelectric strain of the BZT-BCT. Moreover, the LSMO polycrystalline films exhibit almost temperature independent and significantly enhanced magnetoresistance (MR) below TC. At T = 2 K and H = 8 T, the MR of polycrystalline films is approximately two orders of magnitude higher than that of LSMO epitaxial films grown on (LaAlO3)0.3(SrAl1/2Ta1/2O3)0.7 single-crystal substrates. The enhanced MR mainly results from the spin-polarized tunneling of charge carriers across grain boundaries. The LSMO/BZT-BCT structures with electric-field controllable modulation of resistivity and enhanced MR effect may have potential applications in low-energy consumption and environmentally friendly electronic devices.

  8. Local manifestations of a static magnetoelectric effect in nanostructured BaTiO3-BaFe12O9 composite multiferroics

    Science.gov (United States)

    Trivedi, Harsh; Shvartsman, Vladimir V.; Lupascu, Doru C.; Medeiros, Marco S. A.; Pullar, Robert C.; Kholkin, Andrei L.; Zelenovskiy, Pavel; Sosnovskikh, Andrey; Shur, Vladimir Ya.

    2015-02-01

    A study on magnetoelectric phenomena in the barium titanate-barium hexaferrite (BaTiO3-BaFe12O19) composite system, using high resolution techniques including switching spectroscopy piezoresponse force microscopy (SSPFM) and spatially resolved confocal Raman microscopy (CRM), is presented. It is found that both the local piezoelectric coefficient and polarization switching parameters change on the application of an external magnetic field. The latter effect is rationalized by the influence of magnetostrictive stress on the domain dynamics. Processing of the Raman spectral data using principal component analysis (PCA) and self-modelling curve resolution (SMCR) allowed us to achieve high resolution phase distribution maps along with separation of average and localized spectral components. A significant effect of the magnetic field on the Raman spectra of the BaTiO3 phase has been revealed. The observed changes are comparable with the classical pressure dependent studies on BaTiO3, confirming the strain mediated character of the magnetoelectric coupling in the studied composites.

  9. Domain switching in single-phase multiferroics

    Science.gov (United States)

    Jia, Tingting; Cheng, Zhenxiang; Zhao, Hongyang; Kimura, Hideo

    2018-06-01

    Multiferroics are a time-honoured research subject by reason for their tremendous application potential in the information industry, such as in multi-state information storage devices and new types of sensors. An outburst of studies on multiferroicity has been witnessed in the 21st century, although this field has a long research history since the 19th century. Multiferroicity has now become one of the hottest research topics in condensed matter physics and materials science. Numerous efforts have been made to investigate the cross-coupling phenomena among ferroic orders such as ferroelectricity, (anti-)ferromagnetism, and ferroelasticity, especially the coupling between electric and magnetic orderings that would account for the magnetoelectric (ME) effect in multiferroic materials. The magnetoelectric properties and coupling behavior of single phase multiferroics are dominated by their domain structures. It was also noted that, however, the multiferroic materials exhibit very complicated domain structures. Studies on domain structure characterization and domain switching are a crucial step in the exploration of approaches to the control and manipulation of magnetic (electric) properties using an electric (magnetic) field or other means. In this review, following a concise outline of our current basic knowledge on the magnetoelectric (ME) effect, we summarize some important research activities on domain switching in single-phase multiferroic materials in the form of single crystals and thin films, especially domain switching behavior involving strain and the related physics in the last decade. We also introduce recent developments in characterization techniques for domain structures of ferroelectric or multiferroic materials, which have significantly advanced our understanding of domain switching dynamics and interactions. The effects of a series of issues such as electric field, magnetic field, and stress effects on domain switching are been discussed as well. It

  10. Evidence for two spin-glass transitions with magnetoelastic and magnetoelectric couplings in the multiferroic (B i1 -xB ax) (F e1 -xT ix ) O3 system

    Science.gov (United States)

    Kumar, Arun; Kaushik, S. D.; Siruguri, V.; Pandey, Dhananjai

    2018-03-01

    For disordered Heisenberg systems with small single ion anisotropy (D ), two spin-glass (SG) transitions below the long-range ordered (LRO) phase transition temperature (Tc) have been predicted theoretically for compositions close to the percolation threshold. Experimental verification of these predictions is still controversial for conventional spin glasses. We show that multiferroic spin-glass systems can provide a unique platform for verifying these theoretical predictions via a study of change in magnetoelastic and magnetoelectric couplings, obtained from an analysis of diffraction data, at the spin-glass transition temperatures (TSG). Results of macroscopic (dc M (H , T ), M(t ), ac susceptibility [χ (ω, T )], and specific heat (Cp)) and microscopic (x-ray and neutron scattering) measurements are presented on disordered BiFe O3 , a canonical Heisenberg system with small single ion anisotropy, which reveal appearance of two spin-glass phases, SG1 and SG2, in coexistence with the LRO phase below the Almeida-Thouless (A-T) and Gabey-Toulouse (G-T) lines. It is shown that the temperature dependence of the integrated intensity of the antiferromagnetic (AFM) peak shows dips with respect to the Brillouin function behavior around the SG1 and SG2 transition temperatures. The temperature dependence of the unit cell volume departs from the Debye-Grüneisen behavior below the SG1 transition and the magnitude of departure increases significantly with decreasing temperature up to the electromagnon driven transition temperature below which a small change of slope occurs followed by another similar change of slope at the SG2 transition temperature. The ferroelectric polarization also changes significantly at the two spin-glass transition temperatures. These results, obtained using microscopic techniques, clearly demonstrate that the SG1 and SG2 transitions occur on the same magnetic sublattice and are intrinsic to the system. We also construct a phase diagram showing all

  11. Multiferroic oxide thin films and heterostructures

    KAUST Repository

    Lu, Chengliang

    2015-05-26

    Multiferroic materials promise a tantalizing perspective of novel applications in next-generation electronic, memory, and energy harvesting technologies, and at the same time they also represent a grand scientific challenge on understanding complex solid state systems with strong correlations between multiple degrees of freedom. In this review, we highlight the opportunities and obstacles in growing multiferroic thin films with chemical and structural integrity and integrating them in functional devices. Besides the magnetoelectric effect, multiferroics exhibit excellent resistant switching and photovoltaic properties, and there are plenty opportunities for them to integrate with other ferromagnetic and superconducting materials. The challenges include, but not limited, defect-related leakage in thin films, weak magnetism, and poor control on interface coupling. Although our focuses are Bi-based perovskites and rare earth manganites, the insights are also applicable to other multiferroic materials. We will also review some examples of multiferroic applications in spintronics, memory, and photovoltaic devices.

  12. Magnetoelectric polymer nanocomposite for flexible electronics

    International Nuclear Information System (INIS)

    Alnassar, M.; Alfadhel, A.; Ivanov, Yu. P.; Kosel, J.

    2015-01-01

    This paper reports the fabrication and characterization of a new type of magnetoelectric polymer nanocomposite that exhibits excellent ferromagnetism and ferroelectricity simultaneously at room temperature. The multiferroic nanocomposite consists of high aspect ratio ferromagnetic iron nanowires embedded inside a ferroelectric co-polymer poly(vinylindene fluoride-trifluoroethylene), P(VDF-TrFE). The nanocomposite has been fabricated via a simple low temperature spin coating technique. Structural, ferromagnetic, ferroelectric, and magnetoelectric properties of the developed nanocomposite have been characterized. The nanocomposite films showed isotropic magnetic properties due to the random orientation of the iron nanowires inside the film. In addition, the embedded nanowires did not hinder the ferroelectric phase development of the nanocomposite. The developed nanocomposite showed a high magnetoelectric coupling response of 156 mV/cmOe measured at 3.1 kOe DC bias field. This value is among the highest reported magnetoelectric coupling in two phase particulate polymer nanocomposites

  13. Magnetoelectric polymer nanocomposite for flexible electronics

    KAUST Repository

    Al-Nassar, Mohammed Y.

    2015-03-06

    This paper reports the fabrication and characterization of a new type of magnetoelectric polymer nanocomposite that exhibits excellent ferromagnetism and ferroelectricity simultaneously at room temperature. The multiferroic nanocomposite consists of high aspect ratio ferromagnetic iron nanowires embedded inside a ferroelectric co-polymer poly(vinylindene fluoride-trifluoroethylene), P(VDF-TrFE). The nanocomposite has been fabricated via a simple low temperature spin coating technique. Structural, ferromagnetic, ferroelectric, and magnetoelectric properties of the developed nanocomposite have been characterized. The nanocomposite films showed isotropic magnetic properties due to the random orientation of the iron nanowires inside the film. In addition, the embedded nanowires did not hinder the ferroelectric phase development of the nanocomposite. The developed nanocomposite showed a high magnetoelectric coupling response of 156 mV/cmOe measured at 3.1 kOe DC bias field. This value is among the highest reported magnetoelectric coupling in two phase particulate polymer nanocomposites.

  14. Magnetoelectric polymer nanocomposite for flexible electronics

    KAUST Repository

    Al-Nassar, Mohammed Y.; Alfadhel, Ahmed; Ivanov, Yurii P.; Kosel, Jü rgen

    2015-01-01

    This paper reports the fabrication and characterization of a new type of magnetoelectric polymer nanocomposite that exhibits excellent ferromagnetism and ferroelectricity simultaneously at room temperature. The multiferroic nanocomposite consists of high aspect ratio ferromagnetic iron nanowires embedded inside a ferroelectric co-polymer poly(vinylindene fluoride-trifluoroethylene), P(VDF-TrFE). The nanocomposite has been fabricated via a simple low temperature spin coating technique. Structural, ferromagnetic, ferroelectric, and magnetoelectric properties of the developed nanocomposite have been characterized. The nanocomposite films showed isotropic magnetic properties due to the random orientation of the iron nanowires inside the film. In addition, the embedded nanowires did not hinder the ferroelectric phase development of the nanocomposite. The developed nanocomposite showed a high magnetoelectric coupling response of 156 mV/cmOe measured at 3.1 kOe DC bias field. This value is among the highest reported magnetoelectric coupling in two phase particulate polymer nanocomposites.

  15. Voltage control of magnetism in multiferroic heterostructures.

    Science.gov (United States)

    Liu, Ming; Sun, Nian X

    2014-02-28

    Electrical tuning of magnetism is of great fundamental and technical importance for fast, compact and ultra-low power electronic devices. Multiferroics, simultaneously exhibiting ferroelectricity and ferromagnetism, have attracted much interest owing to the capability of controlling magnetism by an electric field through magnetoelectric (ME) coupling. In particular, strong strain-mediated ME interaction observed in layered multiferroic heterostructures makes it practically possible for realizing electrically reconfigurable microwave devices, ultra-low power electronics and magnetoelectric random access memories (MERAMs). In this review, we demonstrate this remarkable E-field manipulation of magnetism in various multiferroic composite systems, aiming at the creation of novel compact, lightweight, energy-efficient and tunable electronic and microwave devices. First of all, tunable microwave devices are demonstrated based on ferrite/ferroelectric and magnetic-metal/ferroelectric composites, showing giant ferromagnetic resonance (FMR) tunability with narrow FMR linewidth. Then, E-field manipulation of magnetoresistance in multiferroic anisotropic magnetoresistance and giant magnetoresistance devices for achieving low-power electronic devices is discussed. Finally, E-field control of exchange-bias and deterministic magnetization switching is demonstrated in exchange-coupled antiferromagnetic/ferromagnetic/ferroelectric multiferroic hetero-structures at room temperature, indicating an important step towards MERAMs. In addition, recent progress in electrically non-volatile tuning of magnetic states is also presented. These tunable multiferroic heterostructures and devices provide great opportunities for next-generation reconfigurable radio frequency/microwave communication systems and radars, spintronics, sensors and memories.

  16. Terahertz Magnetoelectric Resonance Enhanced by Mutual Coupling of Electromagnons

    Science.gov (United States)

    Takahashi, Y.; Yamasaki, Y.; Tokura, Y.

    2013-07-01

    Both electric- and magnetic-dipole active spin excitations, i.e., electromagnons, which mediate the dynamical magnetoelectric effect, have been investigated for a multiferroic perovskite of manganite by optical spectroscopy at terahertz frequencies. Upon the magnetoelectric resonance at 1 meV in the multiferroic phase with the bc-plane spin cycloidal order, a gigantic dynamical magnetoelectric effect has been observed as a nonreciprocal directional dichroism or birefringence. The light k-vector-dependent difference (Δκ=κ+-κ-) of the extinction coefficient (κ±) is as large as Δκ˜1 or 2Δκ/(κ++κ-)˜0.7 at the lowest-lying electromagnon energy. We clarified the mutual coupling of the Eω∥a-polarized electromagnons of the different origins, leading to the enhancement of the magnetoelectric resonance.

  17. Lead-free primary explosives

    Science.gov (United States)

    Huynh, My Hang V.

    2010-06-22

    Lead-free primary explosives of the formula (cat).sub.Y[M.sup.II(T).sub.X(H.sub.2O).sub.6-X].sub.Z, where T is 5-nitrotetrazolate, and syntheses thereof are described. Substantially stoichiometric equivalents of the reactants lead to high yields of pure compositions thereby avoiding dangerous purification steps.

  18. Magnetoelectric effects in manganites

    Science.gov (United States)

    Jeen, Hyoung Jeen

    Research on manganites has been conducted for more than half century. Recent discoveries of colossal responses to external fields such as colossal magnetoresistance effects and correlation among spin, orbital, and lattice in phase separated manganites and multiferroic manganites have motivated me to understand these materials. The main purpose of this dissertation is to understand magnetoelectric effects in phase separated (La1-yPr y)1-xCaxMnO3 (LPCMO) thin films and multiferroic BiMnO3 (BMO) thin films. First, high quality phase separated manganite thin films have been successfully grown. To grow the high quality manganite thin films, extensive effort was devoted to fine tuning of oxygen pressure, temperature, and laser fluence during film growth. As-grown films were characterized with various ex-situ techniques: magnetization measurements, transport measurements, x-ray diffraction, atomic force microscopy, and/or transmission electron microscopy to remove the effects of impurities and unwanted strains except substrate induced strain. Second, three major results were obtained in high quality phase separated LPCMO thin films. These results are based on the dynamic nature of phases in LPCMO. 1) LPCMO thin films showed single domain to multi-domain transition during cooling. This transition can be tuned by substrate stress induced in-plane magnetic anisotropy. 2) Evidence for the origin of colossal electroresistance (CER) effect has been observed. The CER is triggered by dielectrophoresis, or movements of ferromagnetic metallic (FMM) phase, which is manifested in anisotropic transport properties in microfabricated LPCMO cross structures. This fluidic nature of the FMM phase in LPCMO under high electric fields lead to exotic magnetoelectric effects. 3) Electric field effects on magnetotransport properties have been observed. This phenomena can also be tuned by the combined effect of substrate strain and current flow. This combined effect of electric and magnetic

  19. Magnetoelectric force microscopy based on magnetic force microscopy with modulated electric field.

    Science.gov (United States)

    Geng, Yanan; Wu, Weida

    2014-05-01

    We present the realization of a mesoscopic imaging technique, namely, the Magnetoelectric Force Microscopy (MeFM), for visualization of local magnetoelectric effect. The basic principle of MeFM is the lock-in detection of local magnetoelectric response, i.e., the electric field-induced magnetization, using magnetic force microscopy. We demonstrate MeFM capability by visualizing magnetoelectric domains on single crystals of multiferroic hexagonal manganites. Results of several control experiments exclude artifacts or extrinsic origins of the MeFM signal. The parameters are tuned to optimize the signal to noise ratio.

  20. Magnetoelectric Nanocomposites for Flexible Electronics

    KAUST Repository

    Al-Nassar, Mohammed Y.

    2015-09-01

    Flexibility, low cost, versatility, miniaturization and multi-functionality are key aspects driving research and innovation in many branches of the electronics industry. With many anticipated emerging applications, like wearable, transparent and biocompatible devices, interest among the research community in pursuit for novel multifunctional miniaturized materials have been amplified. In this context, multiferroic polymer-based nanocomposites, possessing both ferroelectricity and ferromagnetism, are highly appealing. Most importantly, these nanocomposites possess tunable ferroelectric and ferromagnetic properties based on the parameters of their constituent materials as well as the magnetoelectric effect, which is the coupling between electric and magnetic properties. This tunability and interaction is a fascinating fundamental research field promising tremendous potential applications in sensors, actuators, data storage and energy harvesting. This dissertation work is devoted to the investigation of a new class of multiferroic polymer-based flexible nanocomposites, which exhibits excellent ferromagnetism and ferroelectricity simultaneously at room temperature, with the goal of understanding and optimizing the origin of their magnetoelectric coupling. The nanocomposites consist of high aspect ratio ferromagnetic nanowires (NWs) embedded inside a ferroelectric co-polymer, poly(vinylindene fluoride-trifluoroethylene), P(VDF-TrFE) matrix. First, electrochemical deposition of ferromagnetic NWs inside anodic aluminum oxide membranes is discussed. Characterization of electrodeposited iron, nickel and highly magnetostrictive iron-gallium alloy NWs was done using XRD, electron and magnetic force microscopy. Second, different nanocomposite films have been fabricated by means of spin coating and drop casting techniques. The effect of incorporation of NWs inside the ferroelectric polymer on its electroactive phase is discussed. The remanent and saturation polarization as well

  1. Non-collinear magnetism in multiferroic perovskites.

    Science.gov (United States)

    Bousquet, Eric; Cano, Andrés

    2016-03-31

    We present an overview of the current interest in non-collinear magnetism in multiferroic perovskite crystals. We first describe the different microscopic mechanisms giving rise to the non-collinearity of spins in this class of materials. We discuss, in particular, the interplay between non-collinear magnetism and ferroelectric and antiferrodistortive distortions of the perovskite structure, and how this can promote magnetoelectric responses. We then provide a literature survey on non-collinear multiferroic perovskites. We discuss numerous examples of spin cantings driving weak ferromagnetism in transition metal perovskites, and of spin-induced ferroelectricity as observed in the rare-earth based perovskites. These examples are chosen to best illustrate the fundamental role of non-collinear magnetism in the design of multiferroicity.

  2. Dielectric and polarization studies of magnetoelectric coupling in non-relaxor Pb(Fe.sub.1/2./sub.Ta.sub.1/2./sub.)O.sub.3./sub. multiferroic ceramics

    Czech Academy of Sciences Publication Activity Database

    Savinov, Maxim; Bednyakov, Petr; Raevskaya, S. I.; Gusev, A.A.; Isupov, V.P.; Raevski, I. P.; Titov, V.V.; Chen, H.; Kovrigina, S.A.; Chou, C.-C.; Minasyan, T.A.; Malitskaya, M. A.

    2017-01-01

    Roč. 509, č. 1 (2017), s. 80-91 ISSN 0015-0193 Institutional support: RVO:68378271 Keywords : lead iron tantalate * PFT * dielectric permittivity * phase transition * hysteresis loops * magnetoelectric coupling Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 0.551, year: 2016

  3. Multiferroic Memories

    Directory of Open Access Journals (Sweden)

    Amritendu Roy

    2012-01-01

    Full Text Available Multiferroism implies simultaneous presence of more than one ferroic characteristics such as coexistence of ferroelectric and magnetic ordering. This phenomenon has led to the development of various kinds of materials and conceptions of many novel applications such as development of a memory device utilizing the multifunctionality of the multiferroic materials leading to a multistate memory device with electrical writing and nondestructive magnetic reading operations. Though, interdependence of electrical- and magnetic-order parameters makes it difficult to accomplish the above and thus rendering the device to only two switchable states, recent research has shown that such problems can be circumvented by novel device designs such as formation of tunnel junction or by use of exchange bias. In this paper, we review the operational aspects of multiferroic memories as well as the materials used for these applications along with the designs that hold promise for the future memory devices.

  4. Spin-driven ferroelectricity and magneto-electric effects in frustrated magnetic systems

    International Nuclear Information System (INIS)

    Arima, Taka-hisa

    2011-01-01

    The interplay between magnetism and electricity in matter has become a central issue of condensed-matter physics. This review focuses on the ferroelectricity induced by magnetic order mostly in frustrated magnets, which is nowadays referred to as magneto-electric (ME) multiferroic, or often only as multiferroic. Some distinct types of microscopic origins relevant to the spin-driven ferroelectricity are discussed in detail. Then one sees that the frustration-based spin-driven ferroelectrics can exhibit nonlinear and giant ME responses of phase-transition type and of domain-control type, in contrast to the conventional magnetoelectrics hosting linear ME effects. (author)

  5. Weak ferromagnetism and magnetoelectric effect in multiferroic xBa{sub 0.95}Sr{sub 0.05}TiO{sub 3}–(1−x)BiFe{sub 0.9}Gd{sub 0.1}O{sub 3} relaxors

    Energy Technology Data Exchange (ETDEWEB)

    Miah, M.J. [Department of Physics, Bangladesh University of Engineering and Technology (Bangladesh); Department of Physics, Comilla University, Comilla (Bangladesh); Khan, M.N.I. [Materials Science Division, Atomic Energy Center, Dhaka (Bangladesh); Hossain, A.K.M. Akther, E-mail: akmhossain@phy.buet.ac.bd [Department of Physics, Bangladesh University of Engineering and Technology (Bangladesh)

    2016-03-01

    Multiferroic xBa{sub 0.95}Sr{sub 0.05}TiO{sub 3}–(1−x)BiFe{sub 0.9}Gd{sub 0.1}O{sub 3} [xBST–(1−x)BFGO], where x=0.00−0.40, have been synthesized by the conventional solid-state reaction method. The crystalline phase, microstructure, relaxor behavior, ac conductivity, impedance spectroscopy, dc magnetic properties, complex initial permeability and magnetoelectric coefficient of these solid solutions have been investigated. The crystal structure is found to change from rhombohedral in BFGO rich compositions to cubic when x≥0.30. Room temperature dielectric properties are investigated within the frequency range from 1 kHz to 1 MHz and found to increase with BST content. The frequency dependence of high temperature dielectric measurements indicated that the composites with x≥0.20, exhibit relaxor ferroelectric behavior. The ac conductivity obeys the Jonscher’s universal power law and BST helps to enhance the electrical conductivity of the composites. Studies of impedance spectroscopy suggest that only grains have the contribution to the conductivity mechanism in this material. Magnetizations as a function of applied magnetic field measurements show weak ferromagnetism for 0.10≤x≤0.30 composites. The maximum value of remnant magnetization is found to be 0.565×10{sup 3} A/m (=0.08 emu/g) for x=0.25 which is better than previously reported BaTiO{sub 3}–BiFeO{sub 3} systems. The complex initial permeability is found to improve with the increase in BST concentration due to the reduction of oxygen vacancies. In addition, an enhanced magnetoelectric (ME) coupling is also observed and determined by the ME coefficient. The maximum value of ME coefficient is found to be 21.71×10{sup −4} V/A (=1.67 mV/cm Oe) for the x=0.25 composition. The BST–BFGO solid solutions show high-performance multiferroic properties and can be selected for further investigation. - Highlights: • Phase pure multiferroic xBa{sub 0.95}Sr{sub 0.05}TiO{sub 3}–(1−x)BiFe{sub 0

  6. Electric-Field-Induced Magnetization Reversal in a Ferromagnet-Multiferroic Heterostructure

    Science.gov (United States)

    Heron, J. T.; Trassin, M.; Ashraf, K.; Gajek, M.; He, Q.; Yang, S. Y.; Nikonov, D. E.; Chu, Y.-H.; Salahuddin, S.; Ramesh, R.

    2011-11-01

    A reversal of magnetization requiring only the application of an electric field can lead to low-power spintronic devices by eliminating conventional magnetic switching methods. Here we show a nonvolatile, room temperature magnetization reversal determined by an electric field in a ferromagnet-multiferroic system. The effect is reversible and mediated by an interfacial magnetic coupling dictated by the multiferroic. Such electric-field control of a magnetoelectric device demonstrates an avenue for next-generation, low-energy consumption spintronics.

  7. Spintronics with multiferroics

    Science.gov (United States)

    Béa, H.; Gajek, M.; Bibes, M.; Barthélémy, A.

    2008-10-01

    In this paper, we review the recent research on the functionalization of multiferroics for spintronics applications. We focus more particularly on antiferromagnetic and ferroelectric BiFeO3 and its integration in several types of architectures. For instance, when used as a tunnel barrier, BiFeO3 allows the observation of a large tunnel magnetoresistance with Co and (La,Sr)MnO3 ferromagnetic electrodes. Also, its antiferromagnetic and magnetoelectric properties have been exploited to induce an exchange coupling with a ferromagnet. The mechanisms of such an exchange coupling open ways to electrically control magnetization and possibly the logic state of spintronics devices. We also discuss recent results concerning the use of ferromagnetic and ferroelectric (La,Bi)MnO3 as an active tunnel barrier in magnetic tunnel junctions with Au and (La,Sr)MnO3 electrodes. A four-resistance-state device has been obtained, with two states arising from a spin filtering effect due to the ferromagnetic character of the barrier and two resulting from the ferroelectric behavior of the (La,Bi)MnO3 ultrathin film. These results show that the additional degree of freedom provided by the ferroelectric polarization brings novel functionalities to spintronics, either as a extra order parameter for multiple-state memory elements, or as a handle for gate-controlled magnetic memories.

  8. Spintronics with multiferroics

    International Nuclear Information System (INIS)

    Bea, H; Gajek, M; Bibes, M; Barthelemy, A

    2008-01-01

    In this paper, we review the recent research on the functionalization of multiferroics for spintronics applications. We focus more particularly on antiferromagnetic and ferroelectric BiFeO 3 and its integration in several types of architectures. For instance, when used as a tunnel barrier, BiFeO 3 allows the observation of a large tunnel magnetoresistance with Co and (La,Sr)MnO 3 ferromagnetic electrodes. Also, its antiferromagnetic and magnetoelectric properties have been exploited to induce an exchange coupling with a ferromagnet. The mechanisms of such an exchange coupling open ways to electrically control magnetization and possibly the logic state of spintronics devices. We also discuss recent results concerning the use of ferromagnetic and ferroelectric (La,Bi)MnO 3 as an active tunnel barrier in magnetic tunnel junctions with Au and (La,Sr)MnO 3 electrodes. A four-resistance-state device has been obtained, with two states arising from a spin filtering effect due to the ferromagnetic character of the barrier and two resulting from the ferroelectric behavior of the (La,Bi)MnO 3 ultrathin film. These results show that the additional degree of freedom provided by the ferroelectric polarization brings novel functionalities to spintronics, either as a extra order parameter for multiple-state memory elements, or as a handle for gate-controlled magnetic memories.

  9. Spintronics with multiferroics

    Energy Technology Data Exchange (ETDEWEB)

    Bea, H; Gajek, M; Bibes, M; Barthelemy, A [Unite Mixte de Physique CNRS/Thales, Route departementale 128, F-91767 Palaiseau (France); Universite Paris-Sud, 91405 Orsay (France)], E-mail: agnes.barthelemy@thalesgroup.com

    2008-10-29

    In this paper, we review the recent research on the functionalization of multiferroics for spintronics applications. We focus more particularly on antiferromagnetic and ferroelectric BiFeO{sub 3} and its integration in several types of architectures. For instance, when used as a tunnel barrier, BiFeO{sub 3} allows the observation of a large tunnel magnetoresistance with Co and (La,Sr)MnO{sub 3} ferromagnetic electrodes. Also, its antiferromagnetic and magnetoelectric properties have been exploited to induce an exchange coupling with a ferromagnet. The mechanisms of such an exchange coupling open ways to electrically control magnetization and possibly the logic state of spintronics devices. We also discuss recent results concerning the use of ferromagnetic and ferroelectric (La,Bi)MnO{sub 3} as an active tunnel barrier in magnetic tunnel junctions with Au and (La,Sr)MnO{sub 3} electrodes. A four-resistance-state device has been obtained, with two states arising from a spin filtering effect due to the ferromagnetic character of the barrier and two resulting from the ferroelectric behavior of the (La,Bi)MnO{sub 3} ultrathin film. These results show that the additional degree of freedom provided by the ferroelectric polarization brings novel functionalities to spintronics, either as a extra order parameter for multiple-state memory elements, or as a handle for gate-controlled magnetic memories.

  10. Dynamic response in a finite size composite multiferroic thin film

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Zidong, E-mail: Zidong.Wang@auckland.ac.nz; Grimson, Malcolm J. [Department of Physics, The University of Auckland, Auckland 1010 (New Zealand)

    2016-03-28

    Composite multiferroics, heterostructures of ferromagnetic and ferroelectric materials, are characterized by a remarkable magnetoelectric effect at the interface. Previous work has supported the ferromagnetic structure with magnetic spins and the ferroelectric with pseudospins which act as electric dipoles in a microscopic model, coupled with a magnetoelectric interaction [Wang and Grimson, J. Appl. Phys. 118, 124109 (2015)]. In this work, by solving the stochastic Landau-Lifshitz-Gilbert equation, the electric-field-induced magnetization switching in a twisted boundary condition has been studied, and a behavior of domain wall in the ferromagnetic structure is discussed.

  11. Induced motion of domain walls in multiferroics with quadratic interaction

    Energy Technology Data Exchange (ETDEWEB)

    Gerasimchuk, Victor S., E-mail: viktor.gera@gmail.com [National Technical University of Ukraine “Kyiv Polytechnic Institute”, Peremohy Avenue 37, 03056 Kiev (Ukraine); Shitov, Anatoliy A., E-mail: shitov@mail.ru [Donbass National Academy of Civil Engineering, Derzhavina Street 2, 86123 Makeevka, Donetsk Region (Ukraine)

    2013-10-15

    We theoretically study the dynamics of 180-degree domain wall of the ab-type in magnetic materials with quadratic magnetoelectric interaction in external alternating magnetic and electric fields. The features of the oscillatory and translational motions of the domain walls and stripe structures depending on the parameters of external fields and characteristics of the multiferroics are discussed. The possibility of the domain walls drift in a purely electric field is established. - Highlights: • We study DW and stripe DS in multiferroics with quadratic magnetoelectric interaction. • We build up the theory of oscillatory and translational (drift) DW and DS motion. • DW motion can be caused by crossed alternating electric and magnetic fields. • DW motion can be caused by alternating “pure” electric field. • DW drift velocity is formed by the AFM and Dzyaloshinskii interaction terms.

  12. Multifunctional magnetoelectric materials for device applications

    International Nuclear Information System (INIS)

    Ortega, N; Katiyar, Ram S; Kumar, Ashok; Scott, J F

    2015-01-01

    Over the past decade magnetoelectric (ME) mutiferroic (MF) materials and their devices are one of the highest priority research topics that has been investigated by the scientific ferroics community to develop the next generation of novel multifunctional materials. These systems show the simultaneous existence of two or more ferroic orders, and cross-coupling between them, such as magnetic spin, polarisation, ferroelastic ordering, and ferrotoroidicity. Based on the type of ordering and coupling, they have drawn increasing interest for a variety of device applications, such as magnetic field sensors, nonvolatile memory elements, ferroelectric photovoltaics, nano-electronics etc. Since single-phase materials exist rarely in nature with strong cross-coupling properties, intensive research activity is being pursued towards the discovery of new single-phase multiferroic materials and the design of new engineered materials with strong magneto-electric (ME) coupling. This review article summarises the development of different kinds of multiferroic material: single-phase and composite ceramic, laminated composite and nanostructured thin films. Thin-film nanostructures have higher magnitude direct ME coupling values and clear evidence of indirect ME coupling compared with bulk materials. Promising ME coupling coefficients have been reported in laminated composite materials in which the signal to noise ratio is good for device fabrication. We describe the possible applications of these materials. (topical review)

  13. Electric field mediated non-volatile tuning magnetism in CoPt/PMN-PT heterostructure for magnetoelectric memory devices

    Science.gov (United States)

    Yang, Y. T.; Li, J.; Peng, X. L.; Wang, X. Q.; Wang, D. H.; Cao, Q. Q.; Du, Y. W.

    2016-02-01

    We report a power efficient non-volatile magnetoelectric memory in the CoPt/(011)PMN-PT heterostructure. Two reversible and stable electric field induced coercivity states (i.e., high-HC or low-HC) are obtained due to the strain mediated converse magnetoelectric effect. The reading process of the different coercive field information written by electric fields is demonstrated by using a magnetoresistance read head. This result shows good prospects in the application of novel multiferroic devices.

  14. Lead free solder mechanics and reliability

    CERN Document Server

    Pang, John Hock Lye

    2012-01-01

    Lead-free solders are used extensively as interconnection materials in electronic assemblies and play a critical role in the global semiconductor packaging and electronics manufacturing industry. Electronic products such as smart phones, notebooks and high performance computers rely on lead-free solder joints to connect IC chip components to printed circuit boards. Lead Free Solder: Mechanics and Reliability provides in-depth design knowledge on lead-free solder elastic-plastic-creep and strain-rate dependent deformation behavior and its application in failure assessment of solder joint reliability. It includes coverage of advanced mechanics of materials theory and experiments, mechanical properties of solder and solder joint specimens, constitutive models for solder deformation behavior; numerical modeling and simulation of solder joint failure subject to thermal cycling, mechanical bending fatigue, vibration fatigue and board-level drop impact tests. This book also: Discusses the mechanical prope...

  15. Magnetoelectricity in composites

    CERN Document Server

    Bichurin, Mirza

    2011-01-01

    Magnetoelectric composites, which simultaneously exhibit ferroelectricity and ferromagnetism, have recently stimulated a sharply increasing number of research activities for their scientific interest and significant technological promise in the novel multifunctional devices. Natural single-phase compounds are rare, and their magnetoelectric responses are either relatively weak or occurs at temperatures too low for practical applications. In contrast, composites, which incorporate both ferroelectric and ferri-/ferromagnetic phases, typically yield giant magnetoelectric coupling response above r

  16. Magnetodielectric coupling in multiferroic holmium iron garnets

    International Nuclear Information System (INIS)

    Malar Selvi, M.; Chakraborty, Deepannita; Venkateswaran, C.

    2017-01-01

    Single phase magneto-electric multiferroics require a large magnetic or electric field for producing magneto-electric (ME) and magnetodielectric (MD) effects. For utilizing these effects in devices investigations on the room temperature and low field MD studies are necessary. Recently, efforts have been largely devoted to the investigation of rare earth iron garnets. In the physical method, the preparation of rare earth iron garnet requires high sintering temperature and processing time. To solve these problems, ball milling assisted microwave sintering technique is used to prepare nanocrystalline holmium iron garnets (Ho_3Fe_5O_1_2). Magnetic and dielectric properties of the prepared sample are investigated. These properties get enhanced in nanocrystalline form when compared to the bulk. The MD coupling of the prepared sample is evident from the anomaly in the temperature dependent dielectric constant plot and the ME coupling susceptibility is derived from the room temperature MD measurements. - Highlights: • Formation of single phase Holmium iron garnet reported. • Ball milling assisted microwave sintering reduces the sintering temperature and time. • Holmium iron garnet shows enhanced magnetic and dielectric properties. • Pyromagnetic and pyroelectric measurements confirm the magnetoelectric coupling. • Room temperature magnetodielectric measurements show the nonlinear behaviour.

  17. Characterization of energy conversion of multiferroic PFN and PFN:Mn

    Directory of Open Access Journals (Sweden)

    Lucjan Kozielski

    2013-12-01

    Full Text Available Characterization of energy conversion of multiferroic materials is concerned with multifunctional properties of materials, a topic that is fascinating from the scientific point of view and important for the modern technology. The complex characterization of multiferroic structures suffers at present from lack of a systematic experimental approach and deficiency of multifunctional magnetoelectric properties testing capabilities. Compactness and high frequency energy conversion capacity are the main reasons of invention and improvement of sophisticated materials which are prepared for high-speed computer memories and broadband transducer devices. As a consequence, one can easily notice an intense search for new materials for generation, transformation and amplification of magnetic and electric energies. In this scenario, the combination of excellent piezoelectric and magnetic properties makes lead iron niobate Pb(Fe1/2Nb1/2O3 (PFN an attractive host material for application in integrated magnetoelectric energy conversion applications. PFN multiferroic materials are attractive for commercial electroceramics due to high value of dielectric permittivity and magnetoelectric coefficients as well as relatively easy synthesis process. However, synthesis of PFN ceramics is mostly connected with formation of the secondary unwanted pyrochlore phase associated with dramatic decrease of ferroelectric properties. The authors have successfully reduced this negative phenomenon by Mn doping and finally present high piezoelectric and magnetoelectric energy conversion efficiency in fabricated PMFN ceramics.

  18. Lattice strain induced multiferroicity in PZT-CFO particulate composite

    Science.gov (United States)

    Pradhan, Lagen Kumar; Pandey, Rabichandra; Kumar, Rajnish; Kar, Manoranjan

    2018-02-01

    Lead Zirconate Titanate [Pb(Zr0.52Ti0.48)O3/PZT] and Cobalt Ferrite [CoFe2O4/CFO] based multiferroic composites [(1-x)PZT-(x)CFO] with (x = 0.10-0.40) have been prepared to study its magnetoelectric (ME) and multiferroic properties. X-ray diffraction method along with the Rietveld refinement technique reveals that the crystal symmetries corresponding to PZT and CFO exist independently in the composites. The effect of interfacial strain on lattice distortion in PZT has been observed. It is well correlated with the magnetoelectric coupling of the composites. Dispersion behavior of dielectric constant with frequency can be explained by the modified Debye model. Different relaxation phenomena have been observed in PZT-CFO particulate composites. The ferroelectric properties of composites decrease with the increase in percentage of CFO in the composite. Both saturation (Ms) and remanent (Mr) magnetization increase with the increase in CFO content in the composite. The maximum ME coupling was found to be 1.339 pC/cm2 Oe for the composition (0.80) PZT-(0.20) CFO at the application of maximum magnetic field of 50 Oe. The multiferroic properties in CFO-PZT can be explained by the lattice strain at the CFO-PZT interfaces.

  19. Giant magnetoelectric effect in pure manganite-manganite heterostructures

    Energy Technology Data Exchange (ETDEWEB)

    Paul, Sanjukta; Pankaj, Ravindra; Yarlagadda, Sudhakar; Majumdar, Pinaki; Littlewood, Peter B.

    2017-11-01

    Obtaining strong magnetoelectric couplings in bulk materials and heterostructures is an ongoing challenge. We demonstrate that manganite heterostructures of the form (Insulator) /(LaMnO3)(n)/Interface/(CaMnO3)(n)/(Insulator) show strong multiferroicity in magnetic manganites where ferroelectric polarization is realized by charges leaking from LaMnO3 to CaMnO3 due to repulsion. Here, an effective nearest-neighbor electron-electron (electron-hole) repulsion (attraction) is generated by cooperative electron-phonon interaction. Double exchange, when a particle virtually hops to its unoccupied neighboring site and back, produces magnetic polarons that polarize antiferromagnetic regions. Thus a striking giant magnetoelectric effect ensues when an external electrical field enhances the electron leakage across the interface.

  20. Magnetoelectric Energy Harvesting

    Science.gov (United States)

    2014-11-20

    zirconate titanate ( PZT ). The non-linear electromechanically coupled phase transition associated with field and stress driven phase transformations...The magnetoelectric coefficient , ME, as estimated from experimental results is: = > 40 × (1) where E is the electric

  1. Magnetic structure driven ferroelectricity and large magnetoelectric coupling in antiferromagnet Co4Nb2O9

    Science.gov (United States)

    Srivastava, P.; Chaudhary, S.; Maurya, V.; Saha, J.; Kaushik, S. D.; Siruguri, V.; Patnaik, S.

    2018-05-01

    Synthesis and extensive structural, pyroelectric, magnetic, dielectric and magneto-electric characterizations are reported for polycrystalline Co4Nb2O9 towards unraveling the multiferroic ground state. Magnetic measurements confirm that Co4Nb2O9 becomes an anti-ferromagnet at around 28 K. Associated with the magnetic phase transition, a sharp peak in pyroelectric current indicates the appearance of strong magneto-electric coupling below Neel temperature (TN) along with large coupling constant upto 17.8 μC/m2T. Using temperature oscillation technique, we establish Co4Nb2O9 to be a genuine multiferroic with spontaneous electric polarization in the anti-ferromagnetic state in the absence of magnetic field poling. This is in agreement with our low temperature neutron diffraction studies that show the magnetic structure of Co4Nb2O9 to be that of a non-collinear anti-ferromagnet with ferroelectric ground state.

  2. Electric-field-adjustable time-dependent magnetoelectric response in martensitic FeRh alloy

    Czech Academy of Sciences Publication Activity Database

    Fina, I.; Quintana, A.; Padilla-Pantoja, J.; Martí, Xavier; Macià, F.; Sánchez, F.; Foerster, M.; Aballe, L.; Fontcuberta, J.; Sort, J.

    2017-01-01

    Roč. 9, č. 18 (2017), s. 15577-15582 ISSN 1944-8244 R&D Projects: GA MŠk(CZ) LM2011026; GA ČR GB14-37427G EU Projects: European Commission(XE) 268066 - 0MSPIN Institutional support: RVO:68378271 Keywords : magnetoelectric * martensitic alloy * multiferroic * piezoelectric * thin film Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 7.504, year: 2016

  3. NASA-DoD Lead-Free Electronics Project

    Science.gov (United States)

    Kessel, Kurt

    2010-01-01

    This slide presentation reviews the current state of the lead-free electronics project. It characterizes the test articles, which were built with lead-free solder and lead-free component finishes. The tests performed and reported on are: thermal cycling, combine environments testing, mechanical shock testing, vibration testing and drop testing.

  4. Engineering Nano-Structured Multiferroic Thin Films

    Science.gov (United States)

    Cheung, Pui Lam

    Multiferroics exhibit remarkable tunabilities in their ferromagnetic, ferroelectric and magnetoelectric properties that provide the potential in enabling the control of magnetizations by electric field for the next generation non-volatile memories, antennas and motors. In recent research and developments in integrating single-phase ferroelectric and ferromagnetic materials, multiferroic composite demonstrated a promising magnetoelectric (ME) coupling for future applications. Atomic layer deposition (ALD) technique, on the other hand, allows fabrications of complex multiferroic nanostructures to investigate interfacial coupling between the two materials. In this work, radical-enhanced ALD of cobalt ferrite (CFO) and thermal ALD of lead zirconate titanate (PZT) were combined in fabricating complex multiferroic architectures in investigating the effect of nanostructuring and magnetic shape anisotropy on improving ME coupling. In particular, 1D CFO nanotubes and nanowires; 0D-3D CFO/PZT mesoporous composite; and 1D-1D CFO/PZT core-shell nanowire composite were studied. The potential implementation of nanostructured multiferroic composites into functioning devices was assessed by quantifying the converse ME coupling coefficient. The synthesis of 1D CFO nanostructures was realized by ALD of CFO in anodic aluminum oxide (AAO) membranes. This work provided a simple and inexpensive route to create parallel and high aspect ratio ( 55) magnetic nanostructures. The change in magnetic easy axis of (partially filled) CFO nanotubes from perpendicular to parallel in (fully-filled) nanowires indicated the significance of the geometric factor in controlling magnetizations and ME coupling. The 0D-3D CFO/PZT mesoporous composite demonstrated the optimizations of the strain transfer could be achieved by precise thickness control. 100 nm of mesoporous PZT was synthesized on Pt/TiOx/SiO2/Si using amphiphilic diblock copolymers as a porous ferroelectric template (10 nm pore diameter) for

  5. Phase transitions and domain structures in multiferroics

    Science.gov (United States)

    Vlahos, Eftihia

    2011-12-01

    Thin film ferroelectrics and multiferroics are two important classes of materials interesting both from a scientific and a technological prospective. The volatility of lead and bismuth as well as environmental issues regarding the toxicity of lead are two disadvantages of the most commonly used ferroelectric random access memory (FeRAM) materials such as Pb(Zr,Ti)O3 and SrBi2Ta2O9. Therefore lead-free thin film ferroelectrics are promising substitutes as long as (a) they can be grown on technologically important substrates such as silicon, and (b) their T c and Pr become comparable to that of well established ferroelectrics. On the other hand, the development of functional room temperature ferroelectric ferromagnetic multiferroics could lead to very interesting phenomena such as control of magnetism with electric fields and control of electrical polarization with magnetic fields. This thesis focuses on the understanding of material structure-property relations using nonlinear optical spectroscopy. Nonlinear spectroscopy is an excellent tool for probing the onset of ferroelectricity, and domain dynamics in strained ferroelectrics and multiferroics. Second harmonic generation was used to detect ferroelectricity and the antiferrodistortive phase transition in thin film SrTiO3. Incipient ferroelectric CaTiO3 has been shown to become ferroelectric when strained with a combination of SHG and dielectric measurements. The tensorial nature of the induced nonlinear polarization allows for probing of the BaTiO3 and SrTiO3 polarization contributions in nanoscale BaTiO3/SrTiO3 superlattices. In addition, nonlinear optics was used to demonstrate ferroelectricity in multiferroic EuTiO3. Finally, confocal SHG and Raman microscopy were utilized to visualize polar domains in incipient ferroelectric and ferroelastic CaTiO3.

  6. Magnetoelectric effect in metal–PZT laminates

    Indian Academy of Sciences (India)

    Magnetoelectric (ME) composites are two-phase composites consisting of piezoelectric and piezomagnetic materials as the participating constituents. These magnetoelectric composites when placed under external magnetic field, show electrical polarization (magnetoelectric output). The ME coupling is mediated by ...

  7. Interface engineered ferrite@ferroelectric core-shell nanostructures: A facile approach to impart superior magneto-electric coupling

    Science.gov (United States)

    Abraham, Ann Rose; Raneesh, B.; Das, Dipankar; Oluwafemi, Oluwatobi Samuel; Thomas, Sabu; Kalarikkal, Nandakumar

    2018-04-01

    The electric field control of magnetism in multiferroics is attractive for the realization of ultra-fast and miniaturized low power device applications like nonvolatile memories. Room temperature hybrid multiferroic heterostructures with core-shell (0-0) architecture (ferrite core and ferroelectric shell) were developed via a two-step method. High-Resolution Transmission Electron Microscopy (HRTEM) images confirm the core-shell structure. The temperature dependant magnetization measurements and Mossbauer spectra reveal superparamagnetic nature of the core-shell sample. The ferroelectric hysteresis loops reveal leaky nature of the samples. The results indicate the promising applications of the samples for magneto-electric memories and spintronics.

  8. Evidence for multiferroic characteristics in NdCrTiO5

    International Nuclear Information System (INIS)

    Saha, J.; Sharma, G.; Patnaik, S.

    2014-01-01

    We report NdCrTiO 5 to be an unusual multiferroic material with large magnetic field dependent electric polarization. While magneto-electric coupling in this two magnetic sub-lattice oxide is well established, the purpose of this study is to look for spontaneous symmetry breaking at the magnetic transition. The conclusions are based on extensive magnetization, dielectric and polarization measurements around its antiferromagnetic ordering temperature of 18 K. Room temperature X-ray diffraction pattern of NdCrTiO 5 reveals that the sample is single phase with an orthorhombic crystal structure that allows linear magneto-electric coupling. DC magnetization measurement shows magnetization downturn at 11 K together with a small kink corresponding to the Cr +3 sub-lattice ordering at ∼18 K. An anomaly in dielectric constant is observed around the magnetic ordering temperature that increases substantially with increasing magnetic field. Through detailed pyroelectric current measurements at zero magnetic field, particularly as a function of thermal cycling, we establish that NdCrTiO 5 is a genuine multiferroic material that is possibly driven by collinear magneto-striction. - Highlights: • We provide evidence for multiferroicity in NdCrTiO 5 . • Large magnetic field dependent electric polarization is confirmed. • Sign reversal of pyroelectric current upon thermal cycling proves genuine ferroelectricity. • A model based on collinear magneto-striction is proposed. • A new class of multiferroic materials with large ME coupling is established

  9. Large microwave tunability of GaAs-based multiferroic heterostructure for applications in monolithic microwave integrated circuits

    International Nuclear Information System (INIS)

    Chen Yajie; Gao Jinsheng; Vittoria, C; Harris, V G; Heiman, D

    2010-01-01

    Microwave magnetoelectric coupling in a ferroelectric/ferromagnetic/semiconductor multiferroic (MF) heterostructure, consisting of a Co 2 MnAl epitaxial film grown on a GaAs substrate bonded to a lead magnesium niobate-lead titanate (PMN-PT) crystal, is reported. Ferromagnetic resonance measurements were carried out at X-band under the application of electric fields. Results indicate a frequency tuning of 125 MHz for electric field strength of 8 kV cm -1 resulting in a magnetoelectric coupling coefficient of 3.4 Oe cm kV -1 . This work explores the potential of electronically controlled MF devices for use in future monolithic microwave integrated circuits.

  10. Terfenol-D/Pb(Zr,Ti)O{sub 3} disk-ring multiferroic heterostructures coupled through normal stresses

    Energy Technology Data Exchange (ETDEWEB)

    Li, Lei; Chen, Xiang Ming [Zhejiang University, Laboratory of Dielectric Materials, Department of Materials Science and Engineering, Hangzhou (China)

    2010-03-15

    Disk-ring multiferroic heterostructures composed of Terfenol-D and Pb(Zr,Ti)O{sub 3} (PZT) were prepared and characterized, for which the ferromagnetic and ferroelectric phases were coupled through normal stresses instead of the shear stresses that acted in most of the previous multiferroic heterostructures. High low-frequency magnetoelectric coefficients of 0.10-0.75 V cm{sup -1} Oe{sup -1} were attained for the disk-ring heterostructures, which indicated the strong magnetoelectric coupling. Moreover, a symmetrical resonant peak was observed for dE{sub 3}/dH{sub 3} in the frequency range of 1-200 kHz, while another weak peak with asymmetrical shape also existed at a lower frequency for dE{sub 3}/dH{sub 1}, which was due to the combination of two vibration modes. (orig.)

  11. Large magnetoelectric coupling in magnetically short-range ordered Bi₅Ti₃FeO₁₅ film.

    Science.gov (United States)

    Zhao, Hongyang; Kimura, Hideo; Cheng, Zhenxiang; Osada, Minoru; Wang, Jianli; Wang, Xiaolin; Dou, Shixue; Liu, Yan; Yu, Jianding; Matsumoto, Takao; Tohei, Tetsuya; Shibata, Naoya; Ikuhara, Yuichi

    2014-06-11

    Multiferroic materials, which offer the possibility of manipulating the magnetic state by an electric field or vice versa, are of great current interest. However, single-phase materials with such cross-coupling properties at room temperature exist rarely in nature; new design of nano-engineered thin films with a strong magneto-electric coupling is a fundamental challenge. Here we demonstrate a robust room-temperature magneto-electric coupling in a bismuth-layer-structured ferroelectric Bi₅Ti₃FeO₁₅ with high ferroelectric Curie temperature of ~1000 K. Bi₅Ti₃FeO₁₅ thin films grown by pulsed laser deposition are single-phase layered perovskit with nearly (00l)-orientation. Room-temperature multiferroic behavior is demonstrated by a large modulation in magneto-polarization and magneto-dielectric responses. Local structural characterizations by transmission electron microscopy and Mössbauer spectroscopy reveal the existence of Fe-rich nanodomains, which cause a short-range magnetic ordering at ~620 K. In Bi₅Ti₃FeO₁₅ with a stable ferroelectric order, the spin canting of magnetic-ion-based nanodomains via the Dzyaloshinskii-Moriya interaction might yield a robust magneto-electric coupling of ~400 mV/Oe·cm even at room temperature.

  12. Theory of multiferroics

    International Nuclear Information System (INIS)

    Nagaosa, Naoto

    2009-01-01

    Theories of multiferroics are reviewed with a stress on the role of relativistic spin-orbit interaction and spin current. Ground state electric polarization induced by the non-collinear spin structures, and its dynamical fluctuation, i.e., electro-magnon are discussed. Treatments of the non-perturbative large amplitude thermal and quantum fluctuations are also described. (author)

  13. Progress in engineering high strain lead-free piezoelectric ceramics

    International Nuclear Information System (INIS)

    Leontsev, Serhiy O; Eitel, Richard E

    2010-01-01

    Environmental concerns are strongly driving the need to replace the lead-based piezoelectric materials currently employed as multilayer actuators. The current review describes both compositional and structural engineering approaches to achieve enhanced piezoelectric properties in lead-free materials. The review of the compositional engineering approach focuses on compositional tuning of the properties and phase behavior in three promising families of lead-free perovskite ferroelectrics: the titanate, alkaline niobate and bismuth perovskites and their solid solutions. The 'structural engineering' approaches focus instead on optimization of microstructural features including grain size, grain orientation or texture, ferroelectric domain size and electrical bias field as potential paths to induce large piezoelectric properties in lead-free piezoceramics. It is suggested that a combination of both compositional and novel structural engineering approaches will be required in order to realize viable lead-free alternatives to current lead-based materials for piezoelectric actuator applications. (topical review)

  14. Progress in engineering high strain lead-free piezoelectric ceramics

    Science.gov (United States)

    Leontsev, Serhiy O; Eitel, Richard E

    2010-01-01

    Environmental concerns are strongly driving the need to replace the lead-based piezoelectric materials currently employed as multilayer actuators. The current review describes both compositional and structural engineering approaches to achieve enhanced piezoelectric properties in lead-free materials. The review of the compositional engineering approach focuses on compositional tuning of the properties and phase behavior in three promising families of lead-free perovskite ferroelectrics: the titanate, alkaline niobate and bismuth perovskites and their solid solutions. The ‘structural engineering’ approaches focus instead on optimization of microstructural features including grain size, grain orientation or texture, ferroelectric domain size and electrical bias field as potential paths to induce large piezoelectric properties in lead-free piezoceramics. It is suggested that a combination of both compositional and novel structural engineering approaches will be required in order to realize viable lead-free alternatives to current lead-based materials for piezoelectric actuator applications. PMID:27877343

  15. Magnetoelectric Coupling in CuO Nanoparticles for Spintronics Applications

    Science.gov (United States)

    Kaur, Mandeep; Tovstolytkin, Alexandr; Lotey, Gurmeet Singh

    2018-05-01

    Multiferroic copper oxide (CuO) nanoparticles have been synthesized by colloidal synthesis method. The morphological, structural, magnetic, dielectric and magnetodielectric property has been investigated. The structural study reveals the monoclinic structure of CuO nanoparticles. Transmission electron microscopy images disclose that the size of the CuO nanoparticles is 18 nm and the synthesized nanoparticles are uniform in size and dispersion. Magnetic study tells the weak ferromagnetic character of CuO nanoparticles with coercivity and retentivity value 206 Oe and 0.060 emu/g respectively. Dielectric study confirms that the dielectric constant of CuO nanoparticles is around 1091 at low frequency. The magnetoelectric coupling in the synthesized CuO nanoparticles has been calculated by measuring magnetodielectric coupling coefficient.

  16. Giant multiferroic effects in topological GeTe-Sb2Te3 superlattices

    International Nuclear Information System (INIS)

    Tominaga, Junji; Kolobov, Alexander V; Fons, Paul J; Wang, Xiaomin; Saito, Yuta; Nakano, Takashi; Hase, Muneaki; Murakami, Shuichi; Herfort, Jens; Takagaki, Yukihiko

    2015-01-01

    Multiferroics, materials in which both magnetic and electric fields can induce each other, resulting in a magnetoelectric response, have been attracting increasing attention, although the induced magnetic susceptibility and dielectric constant are usually small and have typically been reported for low temperatures. The magnetoelectric response usually depends on d-electrons of transition metals. Here we report that in [(GeTe) 2 (Sb 2 Te 3 ) l ] m superlattice films (where l and m are integers) with topological phase transition, strong magnetoelectric response may be induced at temperatures above room temperature when the external fields are applied normal to the film surface. By ab initio computer simulations, it is revealed that the multiferroic properties are induced due to the breaking of spatial inversion symmetry when the p-electrons of Ge atoms change their bonding geometry from octahedral to tetrahedral. Finally, we demonstrate the existence in such structures of spin memory, which paves the way for a future hybrid device combining nonvolatile phase-change memory and magnetic spin memory. (focus issue paper)

  17. Magnetoelectric Jones dichroism

    International Nuclear Information System (INIS)

    Andrews, D L; Daniels, G J; Stedman, G E

    2003-01-01

    Recent work on liquids has verified a novel magnetoelectrical birefringence predicted by Jones. Co-present static electric and magnetic fields generate a differential response to optical polarizations positively or negatively tilted against a plane orthogonal to the one containing the static field vectors. Reports indicated a dichroic counterpart; establishing its theory is the present aim. Results are trilinearly dependent on the irradiance, and the static electric and magnetic fields. For isotropic fluids a scalar quantifies propensity for Jones dichroism. In field-polarized fluids a second scalar also contributes; temperature dependence enables determination of both parameters. (letter to the editor)

  18. Additional magnetoelectric effect in electrode-arrayed magnetoelectric composite

    Directory of Open Access Journals (Sweden)

    D. A. Pan

    2014-11-01

    Full Text Available An electrode-arrayed magnetoelectric (ME composite was proposed, in which the positive and negative electrodes of the PZT-5H plate (Pb(Zr0.52Ti0.48O3 were equally divided into a 2 × 5 array, while the PZT plate remained intact. The ME voltage coefficients of these 10 sections were measured individually and in parallel/series modes. The magnetoelectric coefficient is doubled compared with un-arrayed condition, when the 10 sections are connected in parallel/series using an optimized connecting sequence derived from the charge matching rule. This scheme can also be applied to other types of layered magnetoelectric composites to obtain additional magnetoelectric effect from the original composite structure.

  19. The Symmetry of Multiferroics

    OpenAIRE

    Harris, A. Brooks

    2006-01-01

    This paper represents a detailed instruction manual for constructing the Landau expansion for magnetoelectric coupling in incommensurate ferroelectric magnets. The first step is to describe the magnetic ordering in terms of symmetry adapted coordinates which serve as complex valued magnetic order parameters whose transformation properties are displayed. In so doing we use the previously proposed technique to exploit inversion symmetry, since this symmetry had been universally overlooked. Havi...

  20. Magnetoelectric effect in Cr2O3 thin films

    Science.gov (United States)

    He, Xi; Wang, Yi; Sahoo, Sarbeswar; Binek, Christian

    2008-03-01

    Magnetoelectric materials experienced a recent revival as promising components of novel spintronic devices [1, 2, 3]. Since the magnetoelectric (ME) effect is relativistically small in traditional antiferromagnetic compounds like Cr2O3 (max. αzz 4ps/m ) and also cross- coupling between ferroic order parameters is typically small in the modern multiferroics, it is a challenge to electrically induce sufficient magnetization required for the envisioned device applications. A straightforward approach is to increase the electric field at constant voltage by reducing the thickness of the ME material to thin films of a few nm. Since magnetism is known to be affected by geometrical confinement thickness dependence of the ME effect in thin film Cr2O3 is expected. We grow (111) textured Cr2O3 films with various thicknesses below 500 nm and study the ME effect for various ME annealing conditions as a function of temperature with the help of Kerr-magnetometry. [1] P. Borisov et al. Phys. Rev. Lett. 94, 117203 (2005). [2] Ch. Binek, B.Doudin, J. Phys. Condens. Matter 17, L39 (2005). [3] R. Ramesh and Nicola A. Spaldin 2007 Nature Materials 6 21.

  1. Ferroelectric domain switching dynamics and memristive behaviors in BiFeO3-based magnetoelectric heterojunctions

    Science.gov (United States)

    Huang, Weichuan; Liu, Yukuai; Luo, Zhen; Hou, Chuangming; Zhao, Wenbo; Yin, Yuewei; Li, Xiaoguang

    2018-06-01

    The ferroelectric domain reversal dynamics and the corresponding resistance switching as well as the memristive behaviors in epitaxial BiFeO3 (BFO, ~150 nm) based multiferroic heterojunctions were systematically investigated. The ferroelectric domain reversal dynamics could be described by the nucleation-limited-switching model with the Lorentzian distribution of logarithmic domain-switching times. By engineering the domain states, multi and even continuously tunable resistances states, i.e. memristive states, could be non-volatilely achieved. The resistance switching speed can be as fast as 30 ns in the BFO-based multiferroic heterojunctions with a write voltage of ~20 V. By reducing the thickness of BFO, the La0.6Sr0.4MnO3/BFO (~5 nm)/La0.6Sr0.4MnO3 multiferroic tunnel junction (MFTJ) shows an even a quicker switching speed (20 ns) with a much lower operation voltage (~4 V). Importantly, the MFTJ exhibits a tunable interfacial magnetoelectric coupling related to the ferroelectric domain switching dynamics. These findings enrich the potential applications of multiferroic BFO based devices in high-speed, low-power, and high-density memories as well as future neuromorphic computational architectures.

  2. NASA-DoD Lead-Free Electronics Project

    Science.gov (United States)

    Kessel, Kurt

    2011-01-01

    Original Equipment Manufacturers (OEMs). depots. and support contractors have to be prepared to deal with an electronics supply chain thaI increasingly provides parts with lead-free finishes. some labeled no differently and intenningled with their SnPb counterparts. Allowance oflead-free components presents one of the greatest risks to the reliability of military and aerospace electronics. The introduction of components with lead-free lenninations, tennination finishes, or circuit boards presents a host of concerns to customers. suppliers, and maintainers of aerospace and military electronic systems such as: 1. Electrical shorting due to tin whiskers; 2. Incompatibility oflead-free processes and parameters (including higher melting points of lead-free alloys) with other materials in the system; and 3. Unknown material properties and incompatibilities that could reduce solder joint re liability.

  3. Eight-logic memory cell based on multiferroic junctions

    International Nuclear Information System (INIS)

    Yang Feng; Zhou, Y C; Tang, M H; Liu Fen; Ma Ying; Zheng, X J; Zhao, W F; Xu, H Y; Sun, Z H

    2009-01-01

    A model is proposed for a device combining a multiferroic tunnel junction with a magnetoelectric (ME) film in which the magnetic configuration is controlled by the electric field. Calculations embodying the Green's function approach show that the magnetic polarization can be switched on and off by an electric field in the ME film due to the effect of elastic coupling interaction. Using a model including the spin-filter effect and screening of polarization charges, we have produced eight logic states of tunnelling resistance in the tunnel junction and have obtained corresponding laws that control them. The results provide some insights into the realization of an eight-logic memory cell. (fast track communication)

  4. Electric field control of magnon-induced magnetization dynamics in multiferroics.

    Science.gov (United States)

    Risinggård, Vetle; Kulagina, Iryna; Linder, Jacob

    2016-08-24

    We consider theoretically the effect of an inhomogeneous magnetoelectric coupling on the magnon-induced dynamics of a ferromagnet. The magnon-mediated magnetoelectric torque affects both the homogeneous magnetization and magnon-driven domain wall motion. In the domains, we predict a reorientation of the magnetization, controllable by the applied electric field, which is almost an order of magnitude larger than that observed in other physical systems via the same mechanism. The applied electric field can also be used to tune the domain wall speed and direction of motion in a linear fashion, producing domain wall velocities several times the zero field velocity. These results show that multiferroic systems offer a promising arena to achieve low-dissipation magnetization rotation and domain wall motion by exciting spin-waves.

  5. Temperature dependence of electric field tunable ferromagnetic resonance lineshape in multiferroic heterostructure

    Directory of Open Access Journals (Sweden)

    Fenglong Wang

    2016-11-01

    Full Text Available Herein, we experimentally investigate the effect of temperature on the electric field tunable ferromagnetic resonance (FMR in a ferroelectric/ferromagnetic heterostructure, and demonstrate the tuning of abnormal change in FMR using the polarization of the ferroelectric layer above 200 K. The FMR was found to be almost unchanged under different electric field strength at 100 K owing to frozen polarization, which causes extremely weak magnetoelectric coupling. More interestingly, negative effective linewidth was observed when an electric field greater than 10 kV/cm was applied above 220 K. The simultaneous electrical control of magnetization and its damping via FMR based on linear magnetoelectric coupling are directly relevant to use of composite multiferroics for a wide range of devices.

  6. Magnetic Field Control of Cycloidal Domains and Electric Polarization in Multiferroic BiFeO3

    Science.gov (United States)

    Bordács, S.; Farkas, D. G.; White, J. S.; Cubitt, R.; DeBeer-Schmitt, L.; Ito, T.; Kézsmárki, I.

    2018-04-01

    The magnetic field induced rearrangement of the cycloidal spin structure in ferroelectric monodomain single crystals of the room-temperature multiferroic BiFeO3 is studied using small-angle neutron scattering. The cycloid propagation vectors are observed to rotate when magnetic fields applied perpendicular to the rhombohedral (polar) axis exceed a pinning threshold value of ˜5 T . In light of these experimental results, a phenomenological model is proposed that captures the rearrangement of the cycloidal domains, and we revisit the microscopic origin of the magnetoelectric effect. A new coupling between the magnetic anisotropy and the polarization is proposed that explains the recently discovered magnetoelectric polarization perpendicular to the rhombohedral axis.

  7. Magnetoelectric properties of microwave sintered BiFeO{sub 3} and Bi{sub 0.90}La{sub 0.10}Fe{sub 0.95}Mn{sub 0.05}O{sub 3} nanoceramics

    Energy Technology Data Exchange (ETDEWEB)

    Kolte, Jayant, E-mail: jayantkolte@gmail.com [Department of Metallurgical Engineering and Materials Science, Indian Institute of Technology Bombay, Mumbai (India); Daryapurkar, A.S., E-mail: asdarypaurkar@gmail.com [Department of Basic Sciences, Indian Institute of Information Technology, Nagpur (India); Agarwal, Mohit, E-mail: mohit2705@gmail.com [Department of Electronics and Communication Engineering, Thapar University, Patiala, Punjab (India); Gulwade, D.D., E-mail: devidasgulwade@gmail.com [Department of Physics, V.E.S. College of Arts, Commerce and Science, Chembur, Mumbai (India); Gopalan, P., E-mail: pgopalan@iitb.ac.in [Department of Metallurgical Engineering and Materials Science, Indian Institute of Technology Bombay, Mumbai (India)

    2017-06-01

    Multiferroic materials have attracted the attention of scientific community all over the world due to smart functionality and attractive applications such as in magnetoelectric memory and magnetoelectric sensors. In this paper, we report on the ferroelectric, magnetic and magnetoelectric properties of microwave sintered BiFeO{sub 3} (BFO) and Bi{sub 0.90}La{sub 0.10}Fe{sub 0.95}Mn{sub 0.05}O{sub 3} (BLFMO) ceramics. The ferromagnetic and paramagnetic components have been deconvoluted using standard magnetization equation. The ferromagnetic saturation and paramagnetic susceptibility for BFO are found to be 0.046 emu/g and 1.17 × 10{sup -5} emu/g·Oe respectively. The magnetization in BLFMO increases enormously as compared to BFO due to suppression of cycloid spin. The magnetoelectric voltage coefficient for BFO is 3.37 mV/cm·Oe, while for BLFMO it is 10.11 mV/cm·Oe. As compared to BFO, BLFMO exhibits improved ferroelectric, magnetic and magnetoelectric properties. - Highlights: • Ferromagnetic and paramagnetic components calculated from total magnetization. • Magnetoelectric and magnetodielectric coefficients of BFO and BLFMO were measured. • BFO shows linear change in magnetoelectric voltage coefficient with ac magnetic field. • Both BFO and BLFMO follows Ginzburg Landau equation for multiferroics. • Relative to BFO, BLFMO exhibits leakage current that is three order lower.

  8. Nanoscale ferroelectrics and multiferroics key processes and characterization issues, and nanoscale effects

    CERN Document Server

    Alguero, Miguel

    2016-01-01

    This book reviews the key issues in processing and characterization of nanoscale ferroelectrics and multiferroics, and provides a comprehensive description of their properties, with an emphasis in differentiating size effects of extrinsic ones like boundary or interface effects. Recently described nanoscale novel phenomena are also addressed. Organized into three parts it addresses key issues in processing (nanostructuring), characterization (of the nanostructured materials) and nanoscale effects. Taking full advantage of the synergies between nanoscale ferroelectrics and multiferroics, it covers materials nanostructured at all levels, from ceramic technologies like ferroelectric nanopowders, bulk nanostructured ceramics and thick films, and magnetoelectric nanocomposites, to thin films, either polycrystalline layer heterostructures or epitaxial systems, and to nanoscale free standing objects with specific geometries, such as nanowires and tubes at different levels of development. The book is developed from t...

  9. Film size-dependent voltage-modulated magnetism in multiferroic heterostructures

    Science.gov (United States)

    Hu, J.-M.; Shu, L.; Li, Z.; Gao, Y.; Shen, Y.; Lin, Y. H.; Chen, L. Q.; Nan, C. W.

    2014-01-01

    The electric-voltage-modulated magnetism in multiferroic heterostructures, also known as the converse magnetoelectric (ME) coupling, has drawn increasing research interest recently owing to its great potential applications in future low-power, high-speed electronic and/or spintronic devices, such as magnetic memory and computer logic. In this article, based on combined theoretical analysis and experimental demonstration, we investigate the film size dependence of such converse ME coupling in multiferroic magnetic/ferroelectric heterostructures, as well as exploring the interaction between two relating coupling mechanisms that are the interfacial strain and possibly the charge effects. We also briefly discuss some issues for the next step and describe new device prototypes that can be enabled by this technology. PMID:24421375

  10. High Energy, Lead-Free Ignition Formulation for Thermate

    National Research Council Canada - National Science Library

    Tracy, Gene

    2002-01-01

    ... in the AN-Ml4 thermate grenade. This lead-free formulation has provided reliable ignition of the XM89 over a temperature range of -25 degrees F - 120 degrees F when using the M201 Al fuze as the initiator...

  11. FAST TRACK COMMUNICATION: Eight-logic memory cell based on multiferroic junctions

    Science.gov (United States)

    Yang, Feng; Zhou, Y. C.; Tang, M. H.; Liu, Fen; Ma, Ying; Zheng, X. J.; Zhao, W. F.; Xu, H. Y.; Sun, Z. H.

    2009-04-01

    A model is proposed for a device combining a multiferroic tunnel junction with a magnetoelectric (ME) film in which the magnetic configuration is controlled by the electric field. Calculations embodying the Green's function approach show that the magnetic polarization can be switched on and off by an electric field in the ME film due to the effect of elastic coupling interaction. Using a model including the spin-filter effect and screening of polarization charges, we have produced eight logic states of tunnelling resistance in the tunnel junction and have obtained corresponding laws that control them. The results provide some insights into the realization of an eight-logic memory cell.

  12. Multiferroic Properties of o-LuMnO3 Controlled by b-Axis Strain

    Science.gov (United States)

    Windsor, Y. W.; Huang, S. W.; Hu, Y.; Rettig, L.; Alberca, A.; Shimamoto, K.; Scagnoli, V.; Lippert, T.; Schneider, C. W.; Staub, U.

    2014-10-01

    Strain is a leading candidate for controlling magnetoelectric coupling in multiferroics. Here, we use x-ray diffraction to study the coupling between magnetic order and structural distortion in epitaxial films of the orthorhombic (o-) perovskite LuMnO3. An antiferromagnetic spin canting in the E-type magnetic structure is shown to be related to the ferroelectrically induced structural distortion and to a change in the magnetic propagation vector. By comparing films of different orientations and thicknesses, these quantities are found to be controlled by b-axis strain. It is shown that compressive strain destabilizes the commensurate E-type structure and reduces its accompanying ferroelectric distortion.

  13. Response of multiferroic composites inferred from a fast-Fourier-transform-based numerical scheme

    International Nuclear Information System (INIS)

    Brenner, Renald; Bravo-Castillero, Julián

    2010-01-01

    The effective response and the local fields within periodic magneto-electric multiferroic composites are investigated by means of a numerical scheme based on fast Fourier transforms. This computational framework relies on the iterative resolution of coupled series expansions for the magnetic, electric and strain fields. By using an augmented Lagrangian formulation, a simple and robust procedure which makes use of the uncoupled Green operators for the elastic, electrostatics and magnetostatics problems is proposed. Its accuracy is assessed in the cases of laminated and fibrous two-phase composites for which analytical solutions exist

  14. Effect of annealing temperature on the magnetoelectric properties of CoFe{sub 2}O{sub 4}/Pt/Pb(Zr{sub 0.52}Ti{sub 0.48})O{sub 3} multilayer films

    Energy Technology Data Exchange (ETDEWEB)

    Eum, You Jeong; Hwang, Sung Ok; Koo, Chang Young; Lee, Jai Yeoul; Lee, Hee Young [Yeungnam University, Gyeongsan (Korea, Republic of); Ryu, Jung Ho [Korea Institute of Materials Science, Changwon (Korea, Republic of); Park, Jung Min [Osaka University, Osaka (Japan)

    2014-08-15

    CoFe{sub 2}O{sub 4}(CoFO)/Pt/Pb(Zr{sub 0.52}Ti{sub 0.48})O{sub 3} (PZT) multilayer films were grown on Pt/Ti/SiO{sub 2}/Si substrates. A thin Pt layer was inserted between the ferrimagnetic and the ferroelectric layers in order to suppress diffusion at high temperatures and thereby to prevent possible interfacial reactions. The effect of annealing on the film's microstructure and multiferroic properties was then investigated using thin film stacks heat-treated at temperatures ranging from 550 to 650 .deg. C. The magnetoelectric coefficients were calculated from the magnetoelectric voltages measured using a magnetoelectric measurement system. The effect of annealing temperature on the magnetoelectric coupling in the CoFO/Pt/PZT multilayer thin film is discussed in detail.

  15. The single-phase multiferroic oxides: from bulk to thin film

    International Nuclear Information System (INIS)

    Prellier, W; Singh, M P; Murugavel, P

    2005-01-01

    Complex perovskite oxides exhibit a rich spectrum of properties, including magnetism, ferroelectricity, strongly correlated electron behaviour, superconductivity and magnetoresistance, which have been research areas of great interest among the scientific and technological community for decades. There exist very few materials which exhibit multiple functional properties; one such class of materials is called the multiferroics. Multiferroics are interesting because they exhibit simultaneously ferromagnetic and ferroelectric polarizations and a coupling between them. Due to the nontrivial lattice coupling between the magnetic and electronic domains (the magnetoelectric effect), the magnetic polarization can be switched by applying an electric field; likewise the ferroelectric polarization can be switched by applying a magnetic field. As a consequence, multiferroics offer rich physics and novel devices concepts, which have recently become of great interest to researchers. In this review article the recent experimental status, for both the bulk single phase and the thin film form, has been presented. Current studies on the ceramic compounds in the bulk form including Bi(Fe,Mn)O 3 , REMnO 3 and the series of REMn 2 O 5 single crystals (RE = rare earth) are discussed in the first section and a detailed overview on multiferroic thin films grown artificially (multilayers and nanocomposites) is presented in the second section. (topical review)

  16. Lead palladium titanate: A room-temperature multiferroic

    Science.gov (United States)

    Gradauskaite, Elzbieta; Gardner, Jonathan; Smith, Rebecca M.; Morrison, Finlay D.; Lee, Stephen L.; Katiyar, Ram S.; Scott, James F.

    2017-09-01

    There have been a large number of papers on bismuth ferrite (BiFe O3 ) over the past few years, trying to exploit its room-temperature magnetoelectric multiferroic properties. Although these are attractive, BiFe O3 is not the ideal multiferroic due to weak magnetization and the difficulty in limiting leakage currents. Thus there is an ongoing search for alternatives, including such materials as gallium ferrite (GaFe O3 ). In the present work we report a comprehensive study of the perovskite PbT i1 -xP dxO3 with 0

  17. Spectroscopic studies of the ferroelectric and magnetic phase transitions in multiferroic Sr.sub.1-x./sub.Ba.sub.x./sub.MnO.sub.3./sub.

    Czech Academy of Sciences Publication Activity Database

    Goian, Veronica; Kadlec, Filip; Kadlec, Christelle; Dabrowski, B.; Kolesnik, S.; Chmaissem, O.; Nuzhnyy, Dmitry; Kempa, Martin; Bovtun, Viktor; Savinov, Maxim; Hejtmánek, Jiří; Prokleška, J.; Kamba, Stanislav

    2016-01-01

    Roč. 28, č. 17 (2016), 1-7, č. článku 175901. ISSN 0953-8984 R&D Projects: GA ČR GP14-14122P; GA ČR GA15-08389S; GA MŠk(CZ) LH15122 Institutional support: RVO:68378271 Keywords : multiferroics * soft and central modes * phonons * magnetoelectric effect * spin-phonon effect Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.649, year: 2016

  18. Lead-Free Experiment in a Space Environment

    Science.gov (United States)

    Blanche, J. F.; Strickland, S. M.

    2012-01-01

    This Technical Memorandum addresses the Lead-Free Technology Experiment in Space Environment that flew as part of the seventh Materials International Space Station Experiment outside the International Space Station for approximately 18 months. Its intent was to provide data on the performance of lead-free electronics in an actual space environment. Its postflight condition is compared to the preflight condition as well as to the condition of an identical package operating in parallel in the laboratory. Some tin whisker growth was seen on a flight board but the whiskers were few and short. There were no solder joint failures, no tin pest formation, and no significant intermetallic compound formation or growth on either the flight or ground units.

  19. Magnetoelectric control of spin currents

    Energy Technology Data Exchange (ETDEWEB)

    Gómez, J. E.; Vargas, J. M.; Avilés-Félix, L.; Butera, A. [Centro Atómico Bariloche, Instituto de Nanociencia y Nanotecnología (CNEA) and Conicet, 8400 Bariloche, Río Negro (Argentina)

    2016-06-13

    The ability to control the spin current injection has been explored on a hybrid magnetoelectric system consisting of a (011)-cut ferroelectric lead magnesium niobate-lead titanate (PMNT) single crystal, a ferromagnetic FePt alloy, and a metallic Pt. With this PMNT/FePt/Pt structure we have been able to control the magnetic field position or the microwave excitation frequency at which the spin pumping phenomenon between FePt and Pt occurs. We demonstrate that the magnetoelectric heterostructure operating in the L-T (longitudinal magnetized-transverse polarized) mode couples the PMNT crystal to the magnetostrictive FePt/Pt bilayer, displaying a strong magnetoelectric coefficient of ∼140 Oe cm kV{sup −1}. Our results show that this mechanism can be effectively exploited as a tunable spin current intensity emitter and open the possibility to create an oscillating or a bistable switch to effectively manipulate spin currents.

  20. Characterization of lead-free solders for electronic packaging

    Science.gov (United States)

    Ma, Hongtao

    The characterization of lead-free solders, especially after isothermal aging, is very important in order to accurately predict the reliability of solder joints. However, due to lack of experimental testing standards and the high homologous temperature of solder alloys (Th > 0.5T m even at room temperature), there are very large discrepancies in both the tensile and creep properties provided in current databases for both lead-free and Sn-Pb solder alloys. In this research, mechanical measurements of isothermal aging effects and the resulting changes in the materials behavior of lead-free solders were performed. A novel specimen preparation procedure was developed where the solder uniaxial test specimens are formed in high precision rectangular cross-section glass tubes using a vacuum suction process. Using specimens fabricated with the developed procedure, isothermal aging effects and viscoplastic material behavior evolution have been characterized for 95.5Sn-4.0Ag-0.5Cu (SAC405) and 96.5Sn-3.0Ag-0.5Cu (SAC305) lead-free solders, which are commonly used as the solder ball alloy in lead-free BGAs and other components. Analogous tests were performed with 63Sn-37Pb eutectic solder samples for comparison purposes. Up to 40% reduction in tensile strength was observed for water quenched specimens after two months of aging at room temperature. Creep deformation also increased dramatically with increasing aging durations. Microstructural changes during room temperature aging were also observed and recorded for the solder alloys and correlated with the observed mechanical behavior changes. Aging effects at elevated temperatures for up to 6 months were also investigated. Thermal aging caused significant tensile strength loss and deterioration of creep deformation. The thermal aging results also showed that after an initial tensile strength drop, the Sn-Pb eutectic solder reached a relatively stable stage after 200 hours of aging. However, for SAC alloy, both the tensile and

  1. A concept for a magnetic field detector underpinned by the nonlinear dynamics of coupled multiferroic devices

    Science.gov (United States)

    Beninato, A.; Emery, T.; Baglio, S.; Andò, B.; Bulsara, A. R.; Jenkins, C.; Palkar, V.

    2013-12-01

    Multiferroic (MF) composites, in which magnetic and ferroelectric orders coexist, represent a very attractive class of materials with promising applications in areas, such as spintronics, memories, and sensors. One of the most important multiferroics is the perovskite phase of bismuth ferrite, which exhibits weak magnetoelectric properties at room temperature; its properties can be enhanced by doping with other elements such as dysprosium. A recent paper has demonstrated that a thin film of Bi0.7Dy0.3FeO3 shows good magnetoelectric coupling. In separate work it has been shown that a carefully crafted ring connection of N (N odd and N ≥ 3) ferroelectric capacitors yields, past a critical point, nonlinear oscillations that can be exploited for electric (E) field sensing. These two results represent the starting point of our work. In this paper the (electrical) hysteresis, experimentally measured in the MF material Bi0.7Dy0.3FeO3, is characterized with the applied magnetic field (B) taken as a control parameter. This yields a "blueprint" for a magnetic (B) field sensor: a ring-oscillator coupling of N = 3 Sawyer-Tower circuits each underpinned by a mutliferroic element. In this configuration, the changes induced in the ferroelectric behavior by the external or "target" B-field are quantified, thus providing a pathway for very low power and high sensitivity B-field sensing.

  2. Magnetoelectric coupling in the Haldane spin-chain system Dy2BaNiO5

    Science.gov (United States)

    Singh, Kiran; Basu, Tathamay; Chowki, S.; Mahapotra, N.; Iyer, Kartik K.; Paulose, P. L.; Sampathkumaran, E. V.

    2013-09-01

    We report the results of various measurements, namely magnetization, complex dielectric permittivity, and electric polarization (P), on Dy2BaNiO5 as a function of temperature (T) and magnetic field (H), apart from heat capacity (C), with the primary motivation of exploring the existence of magnetoelectric (ME) coupling among Haldane spin-chain systems. The M(T) and C(T) data establish long-range magnetic ordering at 58 K. The most noteworthy observations are: (i) Distinct anomalies are observed in the dielectric constant (ɛ') vs T and loss (tanδ) vs T at different temperatures (i.e., 12.5, 30, 50, and 58 K); at low temperatures, three magnetic-field-induced transitions are observed in ɛ' vs H at 6, 40, and 60 kOe. These transition temperatures and critical magnetic fields track those obtained from magnetization data, establishing the existence of strong magnetoelectric coupling in this compound. (ii) Correspondingly, electric polarization could be observed as a function of T and H in the magnetically ordered state, thereby indicating magnetism-induced ferroelectricity in this compound; this result suggests that this compound is a possible multiferroic material among spin =1 (nickel-containing) compounds, with successive magnetic transitions and strong magnetoelectric coupling.

  3. Interface Magnetoelectric Coupling in Co/Pb(Zr,Ti)O3.

    Science.gov (United States)

    Vlašín, Ondřej; Jarrier, Romain; Arras, Rémi; Calmels, Lionel; Warot-Fonrose, Bénédicte; Marcelot, Cécile; Jamet, Matthieu; Ohresser, Philippe; Scheurer, Fabrice; Hertel, Riccardo; Herranz, Gervasi; Cherifi-Hertel, Salia

    2016-03-23

    Magnetoelectric coupling at multiferroic interfaces is a promising route toward the nonvolatile electric-field control of magnetization. Here, we use optical measurements to study the static and dynamic variations of the interface magnetization induced by an electric field in Co/PbZr0.2Ti0.8O3 (Co/PZT) bilayers at room temperature. The measurements allow us to identify different coupling mechanisms. We further investigate the local electronic and magnetic structure of the interface by means of transmission electron microscopy, soft X-ray magnetic circular dichroism, and density functional theory to corroborate the coupling mechanism. The measurements demonstrate a mixed linear and quadratic optical response to the electric field, which results from a magneto-electro-optical effect. We propose a decomposition method of the optical signal to discriminate between different components involved in the electric field-induced polarization rotation of the reflected light. This allows us to extract a signal that we can ascribe to interface magnetoelectric coupling. The associated surface magnetization exhibits a clear hysteretic variation of odd symmetry with respect to the electric field and nonzero remanence. The interface coupling is remarkably stable over a wide frequency range (1-50 kHz), and the application of a bias magnetic field is not necessary for the coupling to occur. These results show the potential of exploiting interface coupling with the prospect of optimizing the performance of magnetoelectric memory devices in terms of stability, as well as fast and dissipationless operation.

  4. Room temperature magnetoelectric coupling and electrical properties of Ni doped Co - ferrite - PZT nanocomposites

    Science.gov (United States)

    Chakraborty, Sarit; Mandal, S. K.; Dey, P.; Saha, B.

    2018-04-01

    Multiferroic magnetoelectric materials are very interesting for the researcher for the potential application in device preparation. We have prepared 0.3Ni0.5Co0.5Fe2O4 - 0.7PbZr0.58Ti0.42O3 magnetoelectric nanocomposites through chemical pyrophoric reaction process followed by solid state reaction and represented magnetoelectric coupling coefficient, thermally and magnetically tunable AC electrical properties. For the structural characterization XRD pattern and SEM micrograph have been analyzed. AC electrical properties reveal that the grain boundaries resistances are played dominating role in the conduction process in the system. Dielectric studies are represents that the dielectric polarization is decreased with frequency as well as magnetic field where it increases with increasing temperature. The dielectric profiles also represents the electromechanical resonance at a frequency of ˜183 kHz. High dielectric constant and low dielectric loss at room temperature makes the material very promising for the application of magnetic field sensor devices.

  5. Acoustic wave coupled magnetoelectric effect

    International Nuclear Information System (INIS)

    Gao, J.S.; Zhang, N.

    2016-01-01

    Magnetoelectric (ME) coupling by acoustic waveguide was developed. Longitudinal and transversal ME effects of larger than 44 and 6 (V cm −1 Oe −1 ) were obtained with the waveguide-coupled ME device, respectively. Several resonant points were observed in the range of frequency lower than 47 kHz. Analysis showed that the standing waves in the waveguide were responsible for those resonances. The frequency and size dependence of the ME effects were investigated. A resonant condition about the geometrical size of the waveguide was obtained. Theory and experiments showed the resonant frequencies were closely influenced by the diameter and length of the waveguide. A series of double-peak curves of longitudinal magnetoelectric response were obtained, and their significance was discussed initially. - Highlights: • Magnetoelectric (ME) coupling by acoustic waveguide was developed. • The frequency and size dependence of the ME effects were investigated. • A resonant condition about the geometrical size of the waveguide was obtained. • A series of double-peak curves of longitudinal magnetoelectric response were obtained, and their significance was discussed initially.

  6. Lead-free piezoceramics – Where to move on?

    Directory of Open Access Journals (Sweden)

    Chang-Hyo Hong

    2016-03-01

    Full Text Available Lead-free piezoceramics aiming at replacing the market-dominant lead-based ones have been extensively searched for more than a decade worldwide. Some noteworthy outcomes such as the advent of commercial products for certain applications have been reported, but the goal, i.e., the invention of a lead-free piezocermic, the performance of which is equivalent or even superior to that of PZT-based piezoceramics, does not seem to be fulfilled yet. Nevertheless, the academic effort already seems to be culminated, waiting for a guideline to a future research direction. We believe that a driving force for a restoration of this research field needs to be found elsewhere, for example, intimate collaborations with related industries. For this to be effectively realized, it would be helpful for academic side to understand the interests and demands of the industry side as well as to provide the industry with new scientific insights that would eventually lead to new applications. Therefore, this review covers some of the issues that are to be studied further and deeper, so-to-speak, lessons from the history of piezoceramics, and some technical issues that could be useful in better understanding the industry demands. As well, the efforts made in the industry side will be briefly introduced for the academic people to catch up with the recent trends and to be guided for setting up their future research direction effectively.

  7. Possible Lead Free Nanocomposite Dielectrics for High Energy Storage Applications

    Directory of Open Access Journals (Sweden)

    Srinivas Kurpati

    2017-03-01

    Full Text Available There is an increasing demand to improve the energy density of dielectric capacitors for satisfying the next generation material systems. One effective approach is to embed high dielectric constant inclusions such as lead zirconia titanate in polymer matrix. However, with the increasing concerns on environmental safety and biocompatibility, the need to expel lead (Pb from modern electronics has been receiving more attention. Using high aspect ratio dielectric inclusions such as nanowires could lead to further enhancement of energy density. Therefore, the present brief review work focuses on the feasibility of development of a lead-free nanowire reinforced polymer matrix capacitor for energy storage application. It is expected that Lead-free sodium Niobate nanowires (NaNbO3 and Boron nitride will be a future candidate to be synthesized using simple hydrothermal method, followed by mixing them with polyvinylidene fluoride (PVDF/ divinyl tetramethyl disiloxanebis (benzocyclobutene matrix using a solution-casting method for Nanocomposites fabrication. The energy density of NaNbO3 and BN based composites are also be compared with that of lead-containing (PbTiO3/PVDF Nano composites to show the feasibility of replacing lead-containing materials from high-energy density dielectric capacitors. Further, this paper explores the feasibility of these materials for space applications because of high energy storage capacity, more flexibility and high operating temperatures. This paper is very much useful researchers who would like to work on polymer nanocomposites for high energy storage applications.

  8. Lead-free bearing alloys for engine applications

    Science.gov (United States)

    Ratke, Lorenz; Ågren, John; Ludwig, Andreas; Tonn, Babette; Gránásy, László; Mathiesen, Ragnvald; Arnberg, Lars; Anger, Gerd; Reifenhäuser, Bernd; Lauer, Michael; Garen, Rune; Gust, Edgar

    2005-10-01

    Recent developments to reduce the fuel consumption, emission and air pollution, size and weight of engines for automotive, truck, ship propulsion and electrical power generation lead to temperature and load conditions within the engines that cannot be borne by conventional bearings. Presently, only costly multilayer bearings with electroplated or sputtered surface coatings can cope with the load/speed combinations required. Ecological considerations in recent years led to a ban by the European Commission on the use of lead in cars a problem for the standard bronze-lead bearing material. This MAP project is therefore developing an aluminium-based lead-free bearing material with sufficient hardness, wear and friction properties and good corrosion resistance. Only alloys made of components immiscible in the molten state can meet the demanding requirements. Space experimentation plays a crucial role in optimising the cast microstructure for such applications.

  9. Excitation of spin waves in BiFeO3 multiferroic film by the slot line transducer

    Science.gov (United States)

    Korneev, V. I.; Popkov, A. F.; Solov'yov, S. V.

    2018-01-01

    Analysis of the efficiency of magnetoelectric excitation of spin-waves in BiFeO3 multiferroic films by a slot line is performed based on the solution of dynamic Ginzburg-Landau equations for the antiferromagnetic vector. The excitation efficiency is determined by the magnitude of the conversion coefficient of the electromagnetic wave to the spin wave by the slot line transducer or in other words, losses on conversion in the slot line. Calculations are made for a homogeneous antiferromagnetic state of the multiferroic in the presence of a sufficiently large magnetic field and for a spatially modulated spin state (SMSS) at zero magnetic field. It is shown that in the case of a homogeneous antiferromagnetic state, the losses on the excitation of spin waves exceed the excitation efficiency in the SMSS state; however, as the frequency approaches the spin excitation gap, it falls and becomes lower than in the SMSS state. Spin wave excitation in the presence of antiferromagnetic cycloid strongly depends on the relation of the slot width of the transducer to the cycloid periodicity and on the magnitude of the shift of the position of the transducer along the cycloid on its period. The usage of multiferroics for delay lines in the considered frequency range from 100 to 600 GHz requires significant reduction in conversion and propagation losses. More promising seems multiferroic usage in phase shifters and switches for this range.

  10. Magnetization manipulation in multiferroic devices.

    Science.gov (United States)

    Gajek, Martin; Martin, Lane; Hao Chu, Ying; Huijben, Mark; Barry, Micky; Ramesh, Ramamoorthy

    2008-03-01

    Controlling magnetization by purely electrical means is a a central topic in spintronics. A very recent route towards this goal is to exploit the coupling between multiple ferroic orders which coexist in multiferroic materials. BiFeO3 (BFO) displays antiferromagnetic and ferroelectric orderings at room temperature and can thus be used as an electrically controllable pinning layer for a ferromagnetic electrode. Furthermore BFO remains ferroelectric down to 2nm and can therefore be integrated as a tunnel barrier in MTJ's. We will describe these two architecture schemes and report on our progresses towards the control of magnetization via the multiferroic layer in those structures.

  11. Ferroelectricity down to at least 2 nm in multiferroic BiFeO3 epitaxial thin films

    International Nuclear Information System (INIS)

    Bea, H.; Fusil, S.; Bouzehouane, K.; Sirena, M.; Herranz, G.; Jacquet, E.; Contour, J.-P.; Barthelemy, A.; Bibes, M.

    2006-01-01

    We report here on the preservation of ferroelectricity down to 2 nm in BiFeO 3 ultrathin films. The electric polarization can be switched reversibly and is stable over several days. Our findings insight on the fundamental problem of ferroelectricity at low thickness and confirm the potential of BiFeO 3 as a lead-free ferroelectric and multiferroic material for nanoscale devices. (author)

  12. Conductivity, dielectric behaviour and magnetoelectric effect in ...

    Indian Academy of Sciences (India)

    intensity of the magnetic field. The maximum value of ME coefficient was observed for 75% ferroelectric phase composite. Keywords. Conductivity; dielectric behaviour; magnetoelectric effect; CuFe2O4; BaTiO3. 1. Introduction. Magnetoelectric composites consist of two phases viz. piezoelectric and piezomagnetic. The ME ...

  13. Predicting Magnetoelectric Coupling in Layered and Graded Composites

    Directory of Open Access Journals (Sweden)

    Mirza Bichurin

    2017-07-01

    Full Text Available Magnetoelectric (ME interaction in magnetostrictive-piezoelectric multiferroic structures consists in inducing the electric field across the structure in an applied magnetic field and is a product property of magnetostriction and piezoelectricity in components. ME voltage coefficient that is the ratio of induced electric field to applied magnetic field is the key parameter of ME coupling strength. It has been known that the ME coupling strength is dictated by the product of the piezoelectric and piezomagnetic coefficients of initial phases. As a result, using the laminates with graded piezoelectric and piezomagnetic parameters are a new pathway to the increase in the ME coupling strength. Recently developed models predict stronger ME interactions in composites based on graded components compared to homogeneous ones. We discuss predicting the ME coupling strength for layered structures of homogeneous and compositionally graded magnetostrictive and piezoelectric components based on the graphs of ME voltage coefficients against composite parameters. For obtaining the graphs, we developed equations for ME output in applied magnetic field for possible modes of operation and layered structure configurations. In particular, our studies have been performed on low-frequency ME coupling, enhanced ME effect in electromechanical resonance (EMR region for longitudinal and bending modes. Additionally, ME coupling at magnetic resonance in magnetostrictive component and at overlapping the EMR and magnetic resonance is investigated. We considered symmetric trilayers and asymmetric bilayers of magnetostrictive and piezoelectric components and multilayered structures based on compositionally stepped initial components.

  14. An Approach for Impression Creep of Lead Free Microelectronic Solders

    Science.gov (United States)

    Anastasio, Onofrio A.

    2002-06-01

    Currently, the microelectronics industry is transitioning from lead-containing to lead-free solders in response to legislation in the EU and Japan. Before an alternative alloy can be designated as a replacement for current Pb-Sn extensive testing must be accomplished. One major characteristic of the alloy that must be considered is creep. Traditionally, creep testing requires numerous samples and a long tin, which thwarts the generation of comprehensive creep databases for difficult to prepare samples such as microelectronic solder joints. However, a relatively new technique, impression creep enables us to rapidly generate creep data. This test uses a cylindrical punch with a flat end to make an impression on the surface of a specimen under constant load. The steady state velocity of the indenter is found to have the same stress and temperature dependence as the conventional unidirectional creep test using bulk specimens. This thesis examines impression creep tests of eutectic Sn-Ag. A testing program and apparatus was developed constructed based on a servo hydraulic test frame. The apparatus is capable of a load resolution of 0.01N with a stability of plus/minus 0.1N, and a displacement resolution of 0.05 microns with a stability of plus/minus 0.1 microns. Samples of eutectic Sn-Ag solder were reflowed to develop the microstructure used in microelectronic packaging. Creep tests were conducted at various stresses and temperatures and showed that coarse microstructures creep more rapidly than the microstructures in the tested regime.

  15. The Magnetoelectric Effect of a Ni0.3Zn0.62Cu0.08Fe2O4 - PbFe0.5Nb0.5O3 Multilayer Composite

    Directory of Open Access Journals (Sweden)

    Guzdek P.

    2014-10-01

    Full Text Available The magnetoelectric effect in multiferroic materials has been widely studied for its fundamental interest and practical applications. The magnetoelectric effect observed for single phase materials like Cr2O3, BiFeO3, and Pb(Fe0.5Nb0.5O3 is usually small. A much larger effect can be obtained in composites consisting of magnetostrictive and piezoelectric phases. This paper investigates the magnetoelectric effect of a multilayer (laminated structure consisting of 6 nickel ferrite and 7 PFN relaxor layers. It describes the synthesis and tape casting process for Ni0.3Zn0.62Cu0.08Fe2O4 ferrite and relaxor PbFe0.5Nb0.5O3 (PFN. Magnetic hysteresis, ZFC - FC curves and dependencies of magnetization versus temperature for PFN relaxor and magnetoelectric composite were measured with a vibrating sample magnetometer (VSM in an applied magnetic field up to 85 kOe at a temperature range of 10 – 400 K. Magnetoelectric effect at room temperature was investigated as a function of a static magnetic field (0.3 - 6.5 kOe and the frequency of sinusoidal magnetic field (0.01 - 6.5 kHz. At lower magnetic field, the magnetoelectric coefficient increases slightly before reaching a maximum and then decreases. The magnetoelectric coefficient aME increases continuously as the frequency is raised, although this increase is less pronounced in the 1-6.5 kHz range. Maximum values of the magnetoelectric coefficient attained for the layered composites exceed about 50 mV/(Oe cm.

  16. Room-temperature multiferroic and magnetocapacitance effects in M-type hexaferrite BaFe{sub 10.2}Sc{sub 1.8}O{sub 19}

    Energy Technology Data Exchange (ETDEWEB)

    Tang, Rujun, E-mail: tangrj@suda.edu.cn, E-mail: yanghao@nuaa.edu.cn; Zhou, Hao; You, Wenlong [Jiangsu Key Laboratory of Thin Films, College of Physics, Optoelectronics and Energy, Soochow University, Suzhou 215006 (China); Yang, Hao, E-mail: tangrj@suda.edu.cn, E-mail: yanghao@nuaa.edu.cn [College of Science, Nanjing University of Aeronautics and Astronautics, Nanjing 211106 (China)

    2016-08-22

    The room-temperature multiferroic and magnetocapacitance (MC) effects of polycrystalline M-type hexaferrite BaFe{sub 10.2}Sc{sub 1.8}O{sub 19} have been investigated. The results show that the magnetic moments of insulating BaFe{sub 10.2}Sc{sub 1.8}O{sub 19} can be manipulated by the electric field at room temperature, indicating the existence of magnetoelectric coupling. Moreover, large MC effects are also observed around the room temperature. A frequency dependence analysis shows that the Maxwell-Wagner type magnetoresistance effect is the dominant mechanism for MC effects at low frequencies. Both the magnetoelectric-type and non-magnetoelectric-type spin-phonon couplings contribute to the MC effects at high frequencies with the former being the dominant mechanism. The above results show that the hexaferrite BaFe{sub 10.2}Sc{sub 1.8}O{sub 19} is a room-temperature multiferroic material that can be potentially used in magnetoelectric devices.

  17. Tuning the photovoltaic effect of multiferroic CoFe{sub 2}O{sub 4}/Pb(Zr, Ti)O{sub 3} composite films by magnetic fields

    Energy Technology Data Exchange (ETDEWEB)

    Pan, Dan-Feng; Chen, Guang-Yi; Bi, Gui-Feng [National Laboratory of Solid State Microstructures and Department of Physics, Nanjing University, Nanjing 210093 (China); Zhang, Hao [Department of Physics and Astronomy, University of Kentucky, Lexington, Kentucky 40506-0055 (United States); Liu, Jun-Ming; Wang, Guang-Hou; Wan, Jian-Guo, E-mail: wanjg@nju.edu.cn [National Laboratory of Solid State Microstructures and Department of Physics, Nanjing University, Nanjing 210093 (China); Collaborative Innovation Center of Advanced Microstructures, Nanjing University, Nanjing 210093 (China)

    2016-05-30

    The 0–3 type CoFe{sub 2}O{sub 4}-Pb(Zr,Ti)O{sub 3} (CFO-PZT) multiferroic composite films have been prepared by a sol-gel process and spin-coating technique. A confirmable photovoltaic effect is observed under ultraviolet light irradiation. Moreover, this photovoltaic effect can be tuned by external magnetic fields. The maximum magnetic modulation ratios of short-circuit current density and open-circuit voltage can reach as high as 13.7% and 12.8% upon the application of 6 kOe DC magnetic field. Through remnant polarization measurements under various magnetic fields and detailed analysis of the energy band structures, we elucidate the mechanism of tuning photovoltaic effect by magnetic fields and attribute it to the combination of two factors. One is the decreased ferroelectric-polarization-induced depolarization electric field and another is the band structure reconstruction at CFO-PZT interfaces, both of which are dominated by the magnetoelectric coupling via interfacial stress transferring at nanoscale. This work makes some attempts of coupling photo-induced effects with magnetoelectric effect in multiferroic materials and will widen the practical ranges of multiferroic-based applications.

  18. Review of multi-layered magnetoelectric composite materials and devices applications

    Science.gov (United States)

    Chu, Zhaoqiang; PourhosseiniAsl, MohammadJavad; Dong, Shuxiang

    2018-06-01

    Multiferroic materials with the coexistence of at least two ferroic orders, such as ferroelectricity, ferromagnetism, or ferroelasticity, have recently attracted ever-increasing attention due to their potential for multifunctional device applications, including magnetic and current sensors, energy harvesters, magnetoelectric (ME) random access memory and logic devices, tunable microwave devices, and ME antenna. In this article, we provide a review of the recent and ongoing research efforts in the field of multi-layered ME composites. After a brief introduction to ME composites and ME coupling mechanisms, we review recent advances in multi-layered ME composites as well as their device applications based on the direct ME effect, magnetic sensors in particular. Finally, some remaining challenges and future perspective of ME composites and their engineering applications will be discussed.

  19. Theory of magnetoelectric coupling in 2-2-type magnetostrictive/piezoelectric composite film with texture

    International Nuclear Information System (INIS)

    Liu Chaoqian; Fei Weidong; Li Weili

    2008-01-01

    It is well accepted that textures in polycrystalline films have significant effects on film properties. The magnetoelectric (ME) coupling in a 2-2-type multiferroic composite film was theoretically discussed using Landau-Ginsburg-Devonshire theory, where the influences of dispersive texture and residual stress were considered. As an example, the 2-2-type CoFe 2 O 4 /BaTiO 3 composite film was theoretically analysed, wherein the case of both the magnetostrictive phase and the piezoelectric phase with (0 0 1)-oriented texture was considered. Our results show that the ME coupling is enhanced with the texture degree of the piezoelectric phase and/or the magnitude of the residual tensile stress, but weakened with the magnitude of residual compressive stress. With increasing texture degree of the magnetostrictive phase, the ME coupling is enhanced when the texture degree is smaller than a critical value, but weakened when the texture degree is larger than the critical value

  20. Ferroelectric ferrimagnetic LiFe2F6 : Charge-ordering-mediated magnetoelectricity

    Science.gov (United States)

    Lin, Ling-Fang; Xu, Qiao-Ru; Zhang, Yang; Zhang, Jun-Jie; Liang, Yan-Ping; Dong, Shuai

    2017-12-01

    Trirutile-type LiFe2F6 is a charge-ordered material with an Fe2 +/Fe3 + configuration. Here, its physical properties, including magnetism, electronic structure, phase transition, and charge ordering, are studied theoretically. On one hand, the charge ordering leads to improper ferroelectricity with a large polarization. On the other hand, its magnetic ground state can be tuned from the antiferromagnetic to ferrimagnetic by moderate compressive strain. Thus, LiFe2F6 can be a rare multiferroic with both large magnetization and polarization. Most importantly, since the charge ordering is the common ingredient for both ferroelectricity and magnetization, the net magnetization may be fully switched by flipping the polarization, rendering intrinsically strong magnetoelectric effects and desirable functions.

  1. Generation of localized strain in a thin film piezoelectric to control individual magnetoelectric heterostructures

    Energy Technology Data Exchange (ETDEWEB)

    Cui, Jizhai; Liang, Cheng-Yen; Sepulveda, Abdon; Carman, Gregory P.; Lynch, Christopher S., E-mail: cslynch@seas.ucla.edu [Department of Mechanical and Aerospace Engineering, University of California, Los Angeles, California 90095 (United States); Paisley, Elizabeth A.; Ihlefeld, Jon F. [Electronic, Optical, and Nano Materials Department, Sandia National Laboratories, Albuquerque, New Mexico 87185 (United States)

    2015-08-31

    Experimental results demonstrate the ability of a surface electrode pattern to produce sufficient in-plane strain in a PbZr{sub 0.52}Ti{sub 0.48}O{sub 3} (PZT) thin film clamped by a Si substrate to control magnetism in a 1000 nm diameter Ni ring. The electrode pattern and the Ni ring/PZT thin film heterostructure were designed using a finite element based micromagnetics code. The magnetoelectric heterostructures were fabricated on the PZT film using e-beam lithography and characterized using magnetic force microscopy. Application of voltage to the electrodes moved one of the “onion” state domain walls. This method enables the development of complex architectures incorporating strain-mediated multiferroic devices.

  2. KNN–NTK composite lead-free piezoelectric ceramic

    Energy Technology Data Exchange (ETDEWEB)

    Matsuoka, T., E-mail: ta-matsuoka@mg.ngkntk.co.jp; Kozuka, H.; Kitamura, K.; Yamada, H.; Kurahashi, T.; Yamazaki, M.; Ohbayashi, K. [NGK SPARK PLUG Co., Ltd., 2808 Iwasaki, Komaki, Aichi 485-8510 (Japan)

    2014-10-21

    A (K,Na)NbO₃-based lead-free piezoelectric ceramic was successfully densified. It exhibited an enhanced electromechanical coupling factor of kₚ=0.52, a piezoelectric constant d₃₃=252 pC/N, and a frequency constant Nₚ=3170 Hz m because of the incorporation of an elaborate secondary phase composed primarily of KTiNbO₅. The ceramic's nominal composition was 0.92K₀.₄₂Na₀.₄₄Ca₀.₀₄Li₀.₀₂Nb₀.₈₅O₃–0.047K₀.₈₅Ti₀.₈₅Nb₁.₁₅O₅–0.023BaZrO₃ –0.0017Co₃O₄–0.002Fe₂O₃–0.005ZnO, abbreviated herein as KNN–NTK composite. The KNN–NTK ceramic exhibited a dense microstructure with few microvoids which significantly degraded its piezoelectric properties. Elemental maps recorded using transmission electron microscopy with energy-dispersive X-ray spectroscopy (TEM–EDS) revealed regions of high concentrations of Co and Zn inside the NTK phase. In addition, X-ray diffraction patterns confirmed that a small portion of the NTK phase was converted into K₂(Ti,Nb,Co,Zn)₆O₁₃ or CoZnTiO₄ by a possible reaction between Co and Zn solutes and the NTK phase during a programmed sintering schedule. TEM studies also clarified a distortion around the KNN/NTK interfaces. Such an NTK phase filled voids between KNN particles, resulting in an improved chemical stability of the KNN ceramic. The manufacturing process was subsequently scaled to 100 kg per batch for granulated ceramic powder using a spray-drying technique. The properties of the KNN–NTK composite ceramic produced using the scaled-up method were confirmed to be identical to those of the ceramic prepared by conventional solid-state reaction sintering. Consequently, slight changes in the NTK phase composition and the distortion around the KNN/NTK interfaces affected the KNN–NTK composite ceramic's piezoelectric characteristics.

  3. Tunable features of magnetoelectric transformers.

    Science.gov (United States)

    Dong, Shuxiang; Zhai, Junyi; Priya, Shashank; Li, Jie-Fang; Viehland, Dwight

    2009-06-01

    We have found that magnetostrictive FeBSiC alloy ribbons laminated with piezoelectric Pb(Zr,Ti)O(3) fiber can act as a tunable transformer when driven under resonant conditions. These composites were also found to exhibit the strongest resonant magnetoelectric voltage coefficient of 750 V/cm-Oe. The tunable features were achieved by applying small dc magnetic biases of -5 transformer features can be attributed to large changes in the piezomagnetic coefficient and permeability of the magnetostrictive phase under H(dc).

  4. Growth of multiferroic Gd1-xYxMnO3 single crystals by optical floating zone technique

    International Nuclear Information System (INIS)

    Sarguna, R.M.; Ganesamoorthy, S.; Sridharan, V.; Subramanian, N.

    2014-01-01

    Rare earth manganites RMnO 3 with distorted perovskite structure are excellent multiferroic materials. The discovery of magnetic spin driven ferroelectricity in orthorhombic manganites (TbMnO 3 ) has sparked a surge in research into understanding the fundamental mechanism of multiferroic behavior. These systems fall under the category of type-2 multiferroics, the change of spatially modulated magnetic moment from sinusoidal to cycloidal gives rise to electric polarization. The magnetic structure depends upon the Mn-O-Mn bond angle. GdMnO 3 shows multiferroic properties only in the presence of applied magnetic field. When a magnetic field is applied along the b-axis, GdMnO 3 enters a ferroelectric state with an electric polarisation along the c-axis. By altering the Mn-O-Mn angle it is expected that GdMnO 3 will show multiferroic property even in the absence of magnetic field like TbMnO 3 . To alter the Mn-O-Mn bond angle GdMnO 3 was substituted with Y having lower ionic radius at Gd site. The effect of Y doping at the rare-earth site in GdMnO 3 investigated on polycrystalline samples of Gd 1-x Y x MnO 3 demonstrated a magneto-electric coupling in x=0.1-0.4. Single crystals are expected to give much amplified signal in respect of ferroelectric and magnetic properties. In this work we have grown Y substituted Gd 1-x Y x MnO 3 (x = 0.2, 0.3 and 0.4) by optical floating zone technique under different gas atmosphere. Growth rate of 1-2 mm/h yielded crack free crystals. Quality of the crystals was checked using Laue diffraction. Effect of growth rate and atmosphere pressure will be presented in this talk. (author)

  5. Tunnel junctions with multiferroic barriers

    Science.gov (United States)

    Gajek, Martin; Bibes, Manuel; Fusil, Stéphane; Bouzehouane, Karim; Fontcuberta, Josep; Barthélémy, Agnès; Fert, Albert

    2007-04-01

    Multiferroics are singular materials that can exhibit simultaneously electric and magnetic orders. Some are ferroelectric and ferromagnetic and provide the opportunity to encode information in electric polarization and magnetization to obtain four logic states. However, such materials are rare and schemes allowing a simple electrical readout of these states have not been demonstrated in the same device. Here, we show that films of La0.1Bi0.9MnO3 (LBMO) are ferromagnetic and ferroelectric, and retain both ferroic properties down to a thickness of 2nm. We have integrated such ultrathin multiferroic films as barriers in spin-filter-type tunnel junctions that exploit the magnetic and ferroelectric degrees of freedom of LBMO. Whereas ferromagnetism permits read operations reminiscent of magnetic random access memories (MRAM), the electrical switching evokes a ferroelectric RAM write operation. Significantly, our device does not require the destructive ferroelectric readout, and therefore represents an advance over the original four-state memory concept based on multiferroics.

  6. Electric-field control of spin waves in multiferroic BiFeO3: Theory

    Science.gov (United States)

    de Sousa, Rogério; Rovillain, P.; Gallais, Y.; Sacuto, A.; Méasson, M. A.; Colson, D.; Forget, A.; Bibes, M.; Barthélémy, A.; Cazayous, M.

    2011-03-01

    Our recent experiment demonstrated gigantic (30%) electric-field tuning of magnon frequencies in multiferroic BiFeO3. We demonstrate that the origin of this effect is related to two linear magnetoelectric interactions that couple the component of electric field perpendicular to the ferroelectric vector to a quadratic form of the Néel vector. We calculate the magnon spectra due to each of these interactions and show that only one of them is consistent with experimental data. At high electric fields, this interaction induces a phase transition to a homogeneous state, and the multi-magnon spectra will fuse into two magnon frequencies. We discuss the possible microscopic mechanisms responsible for this novel interaction and the prospect for applications in magnonics. We acknowledge support from NSERC-Discovery (Canada) and the Agence Nationale pour la Recherche (France).

  7. Lead Free Frangible Ammunition Exposure at United States Air Force Small Arms Firing Ranges, 2005 - 2007

    National Research Council Canada - National Science Library

    Moran, Michael P; Ott, Darrin K

    2008-01-01

    ...) has performed related to health concerns expressed by Security Forces Combat Arms (CATM) instructors regarding exposure to contaminants generated during the discharge of lead free frangible ammunition...

  8. Optical Diode Effect at Spin-Wave Excitations of the Room-Temperature Multiferroic BiFeO_{3}.

    Science.gov (United States)

    Kézsmárki, I; Nagel, U; Bordács, S; Fishman, R S; Lee, J H; Yi, Hee Taek; Cheong, S-W; Rõõm, T

    2015-09-18

    Multiferroics permit the magnetic control of the electric polarization and the electric control of the magnetization. These static magnetoelectric (ME) effects are of enormous interest: The ability to read and write a magnetic state current-free by an electric voltage would provide a huge technological advantage. Dynamic or optical ME effects are equally interesting, because they give rise to unidirectional light propagation as recently observed in low-temperature multiferroics. This phenomenon, if realized at room temperature, would allow the development of optical diodes which transmit unpolarized light in one, but not in the opposite, direction. Here, we report strong unidirectional transmission in the room-temperature multiferroic BiFeO_{3} over the gigahertz-terahertz frequency range. The supporting theory attributes the observed unidirectional transmission to the spin-current-driven dynamic ME effect. These findings are an important step toward the realization of optical diodes, supplemented by the ability to switch the transmission direction with a magnetic or electric field.

  9. Theoretical study of the multiferroic properties in M-doped (M=Co, Cr, Mg) ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Bahoosh, S.G. [Max Planck Institute of Microstructure Physics, Weinberg 2, 06120 Halle (Germany); Apostolov, A.T. [University of Architecture, Civil Engineering and Geodesy, Faculty of Hydrotechnics, Department of Physics, 1, Hristo Smirnenski Blvd., 1046 Sofia (Bulgaria); Apostolova, I.N. [University of Forestry, Faculty of Forest Industry, 10, Kl. Ohridsky Blvd., 1756 Sofia (Bulgaria); Trimper, S. [Institute of Physics, Martin-Luther-University, D-06099 Halle (Germany); Wesselinowa, Julia M. [University of Sofia, Department of Physics, Blvd. J. Bouchier 5, 1164 Sofia (Bulgaria)

    2015-01-01

    The origin of multiferroism is still an open problem in ZnO. We propose a microscopic model to clarify the occurrence of multiferroism in this material. Using Green's function technique we study the influence of ion doping and size effects on the magnetization and polarization of ZnO thin films. The calculations for magnetic Co- and Cr-ions are based on the s–d model, the transverse Ising model in terms of pseudo-spins and a biquadratic magnetoelectric coupling, whereas in case of nonmagnetic Mg-ions the model takes into account the Coulomb interaction and an indirect coupling between the pseudo-spins via the conduction electrons. We show that the magnetization M exhibits a maximum for a fixed concentration of the doping ions. Furthermore M increases with decreasing film thickness N. The polarization increases with increasing concentration of the dopant and decreasing N. The results are in good agreement with the experimental data. - Highlights: • The paper analyzes the multiferroic properties of doped ZnO thin films by a microscopic model. • The magnetization exhibits a maximum at a fixed doping concentration. • The polarization increases with growing dopant concentration. • The ferroelectric transition temperature is enhanced for increasing dopant concentration.

  10. Thermodynamic and neutron diffraction studies on multiferroic NdMn{sub 2}O{sub 5}

    Energy Technology Data Exchange (ETDEWEB)

    Chattopadhyay, S.; Balédent, V.; Auban-Senzier, P.; Pasquier, C.; Doubrovsky, C. [Laboratoire de Physique des Solides, Université Paris-Sud, CNRS-UMR 8502, 91405 Orsay (France); Greenblatt, M. [Department of Chemistry and Chemical Biology, Rutgers, The State University of New Jersey, Piscataway, NJ 08854 (United States); Foury-Leylekian, P., E-mail: pascale.foury@u-psud.fr [Laboratoire de Physique des Solides, Université Paris-Sud, CNRS-UMR 8502, 91405 Orsay (France)

    2015-03-01

    Magnetically frustrated RMn{sub 2}O{sub 5} oxides have attracted considerable attention in recent years, because most of the members of this family show spin ordering induced dielectric polarization along with strong magneto-electric coupling. Although the true origin of the ferroelectricity is still a matter of debate, it has been observed that the magneto-electric phase diagram can be substantially tuned with the variation of rare earth elements. In this work, we have chosen NdMn{sub 2}O{sub 5} as the compound of our interest since it lies exactly in between the ferroelectric and non-ferroelectric members of this family and also, because there are few investigations performed on RMn{sub 2}O{sub 5} systems with large rare earth atoms . With the combination of heat capacity, magnetic susceptibility, dielectric permittivity, powder X-ray diffraction, and powder neutron diffraction measurements, it has been found that NdMn{sub 2}O{sub 5} undergoes an incommensurate magnetic ordering around 30 K followed by a possible ferroelectric-like transition at ∼26 K. Another lock-in kind of magnetic transition appears when the temperature is decreased to ∼15 K. With further lowering of temperature, an antiferromagnetic ordering, which is presumably associated with the Nd{sup 3+}, is achieved near 4 K. This study thus sheds light on a new compound of the RMn{sub 2}O{sub 5} series presenting different multiferroic properties.

  11. Understanding the spin-driven polarizations in Bi MO3 (M = 3 d transition metals) multiferroics

    Science.gov (United States)

    Kc, Santosh; Lee, Jun Hee; Cooper, Valentino R.

    Bismuth ferrite (BiFeO3) , a promising multiferroic, stabilizes in a perovskite type rhombohedral crystal structure (space group R3c) at room temperature. Recently, it has been reported that in its ground state it possess a huge spin-driven polarization. To probe the underlying mechanism of this large spin-phonon response, we examine these couplings within other Bi based 3 d transition metal oxides Bi MO3 (M = Ti, V, Cr, Mn, Fe, Co, Ni) using density functional theory. Our results demonstrate that this large spin-driven polarization is a consequence of symmetry breaking due to competition between ferroelectric distortions and anti-ferrodistortive octahedral rotations. Furthermore, we find a strong dependence of these enhanced spin-driven polarizations on the crystal structure; with the rhombohedral phase having the largest spin-induced atomic distortions along [111]. These results give us significant insights into the magneto-electric coupling in these materials which is essential to the magnetic and electric field control of electric polarization and magnetization in multiferroic based devices. Research is supported by the US Department of Energy, Office of Science, Basic Energy Sciences, Materials Science and Engineering Division and the Office of Science Early Career Research Program (V.R.C) and used computational resources at NERSC.

  12. Electric modulation of conduction in multiferroic Ca-doped BiFeO3 films

    Science.gov (United States)

    Yang, C.-H.; Seidel, J.; Kim, S. Y.; Rossen, P. B.; Yu, P.; Gajek, M.; Chu, Y. H.; Martin, L. W.; Holcomb, M. B.; He, Q.; Maksymovych, P.; Balke, N.; Kalinin, S. V.; Baddorf, A. P.; Basu, S. R.; Scullin, M. L.; Ramesh, R.

    2009-06-01

    Many interesting materials phenomena such as the emergence of high-Tc superconductivity in the cuprates and colossal magnetoresistance in the manganites arise out of a doping-driven competition between energetically similar ground states. Doped multiferroics present a tantalizing evolution of this generic concept of phase competition. Here, we present the observation of an electronic conductor-insulator transition by control of band-filling in the model antiferromagnetic ferroelectric BiFeO3 through Ca doping. Application of electric field enables us to control and manipulate this electronic transition to the extent that a p-n junction can be created, erased and inverted in this material. A `dome-like' feature in the doping dependence of the ferroelectric transition is observed around a Ca concentration of ~1/8, where a new pseudo-tetragonal phase appears and the electric modulation of conduction is optimized. Possible mechanisms for the observed effects are discussed on the basis of the interplay of ionic and electronic conduction. This observation opens the door to merging magnetoelectrics and magnetoelectronics at room temperature by combining electronic conduction with electric and magnetic degrees of freedom already present in the multiferroic BiFeO3.

  13. Current Problems and Possible Solutions in High-Temperature Lead-Free Soldering

    Czech Academy of Sciences Publication Activity Database

    Kroupa, Aleš; Andersson, D.; Hoo, N.; Pearce, J.; Watson, A.; Dinsdale, A.; Mucklejohn, S.

    2012-01-01

    Roč. 21, č. 5 (2012), s. 629-637 ISSN 1059-9495 Institutional support: RVO:68081723 Keywords : lead-free soldering, * materials for high-temperature LF * new technologies for HT lead-free soldering Subject RIV: BJ - Thermodynamics Impact factor: 0.915, year: 2012

  14. Structural Secrets of Multiferroic Interfaces

    Science.gov (United States)

    Meyerheim, H. L.; Klimenta, F.; Ernst, A.; Mohseni, K.; Ostanin, S.; Fechner, M.; Parihar, S.; Maznichenko, I. V.; Mertig, I.; Kirschner, J.

    2011-02-01

    We present an experimental and theoretical study of the geometric structure of ultrathin BaTiO3 films grown on Fe(001). Surface x-ray diffraction reveals that the films are terminated by a BaO layer, while the TiO2 layer is next to the top Fe layer. Cations in termination layers have incomplete oxygen shells inducing strong vertical relaxations. Onset of polarization is observed at a minimum thickness of two unit cells. Our findings are supported by first-principles calculations providing a quantitative insight into the multiferroic properties on the atomic scale.

  15. Sensitivity Enhancement in Magnetic Sensors Based on Ferroelectric-Bimorphs and Multiferroic Composites

    Directory of Open Access Journals (Sweden)

    Gollapudi Sreenivasulu

    2016-02-01

    Full Text Available Multiferroic composites with ferromagnetic and ferroelectric phases have been studied in recent years for use as sensors of AC and DC magnetic fields. Their operation is based on magneto-electric (ME coupling between the electric and magnetic subsystems and is mediated by mechanical strain. Such sensors for AC magnetic fields require a bias magnetic field to achieve pT-sensitivity. Novel magnetic sensors with a permanent magnet proof mass, either on a ferroelectric bimorph or a ferromagnetic-ferroelectric composite, are discussed. In both types, the interaction between the applied AC magnetic field and remnant magnetization of the magnet results in a mechanical strain and a voltage response in the ferroelectric. Our studies have been performed on sensors with a Nd-Fe-B permanent magnet proof mass on (i a bimorph of oppositely-poled lead zirconate titanate (PZT platelets and (ii a layered multiferroic composite of PZT-Metglas-Ni. The sensors have been characterized in terms of sensitivity and equivalent magnetic noise N. Noise N in both type of sensors is on the order of 200 pT/√Hz at 1 Hz, a factor of 10 improvement compared to multiferroic sensors without a proof mass. When the AC magnetic field is applied at the bending resonance for the bimorph, the measured N ≈ 700 pT/√Hz. We discuss models based on magneto-electro-mechanical coupling at low frequency and bending resonance in the sensors and theoretical estimates of ME voltage coefficients are in very good agreement with the data.

  16. Sensitivity Enhancement in Magnetic Sensors Based on Ferroelectric-Bimorphs and Multiferroic Composites.

    Science.gov (United States)

    Sreenivasulu, Gollapudi; Qu, Peng; Petrov, Vladimir; Qu, Hongwei; Srinivasan, Gopalan

    2016-02-20

    Multiferroic composites with ferromagnetic and ferroelectric phases have been studied in recent years for use as sensors of AC and DC magnetic fields. Their operation is based on magneto-electric (ME) coupling between the electric and magnetic subsystems and is mediated by mechanical strain. Such sensors for AC magnetic fields require a bias magnetic field to achieve pT-sensitivity. Novel magnetic sensors with a permanent magnet proof mass, either on a ferroelectric bimorph or a ferromagnetic-ferroelectric composite, are discussed. In both types, the interaction between the applied AC magnetic field and remnant magnetization of the magnet results in a mechanical strain and a voltage response in the ferroelectric. Our studies have been performed on sensors with a Nd-Fe-B permanent magnet proof mass on (i) a bimorph of oppositely-poled lead zirconate titanate (PZT) platelets and (ii) a layered multiferroic composite of PZT-Metglas-Ni. The sensors have been characterized in terms of sensitivity and equivalent magnetic noise N. Noise N in both type of sensors is on the order of 200 pT/√Hz at 1 Hz, a factor of 10 improvement compared to multiferroic sensors without a proof mass. When the AC magnetic field is applied at the bending resonance for the bimorph, the measured N ≈ 700 pT/√Hz. We discuss models based on magneto-electro-mechanical coupling at low frequency and bending resonance in the sensors and theoretical estimates of ME voltage coefficients are in very good agreement with the data.

  17. Multiferroic oxide thin films and heterostructures

    KAUST Repository

    Lu, Chengliang; Hu, Weijin; Tian, Yufeng; Wu, Tao

    2015-01-01

    Multiferroic materials promise a tantalizing perspective of novel applications in next-generation electronic, memory, and energy harvesting technologies, and at the same time they also represent a grand scientific challenge on understanding complex

  18. Lead-free piezoelectric materials and ultrasonic transducers for medical imaging

    Directory of Open Access Journals (Sweden)

    Elaheh Taghaddos

    2015-06-01

    Full Text Available Piezoelectric materials have been vastly used in ultrasonic transducers for medical imaging. In this paper, firstly, the most promising lead-free compositions with perovskite structure for medical imaging applications have been reviewed. The electromechanical properties of various lead-free ceramics, composites, and single crystals based on barium titanate, bismuth sodium titanate, potassium sodium niobate, and lithium niobate are presented. Then, fundamental principles and design considerations of ultrasonic transducers are briefly described. Finally, recent developments in lead-free ultrasonic probes are discussed and their acoustic performance is compared to lead-based transducers. Focused transducers with different beam focusing methods such as lens focusing and mechanical shaping are explained. Additionally, acoustic characteristics of lead-free probes including the pulse-echo results as well as their imaging capabilities for various applications such as phantom imaging, in vitro intravascular ultrasound imaging of swine aorta, and in vivo or ex vivo imaging of human eyes and skin are reviewed.

  19. TOPICAL REVIEW: Progress in engineering high strain lead-free piezoelectric ceramics

    Science.gov (United States)

    Leontsev, Serhiy O.; Eitel, Richard E.

    2010-08-01

    Environmental concerns are strongly driving the need to replace the lead-based piezoelectric materials currently employed as multilayer actuators. The current review describes both compositional and structural engineering approaches to achieve enhanced piezoelectric properties in lead-free materials. The review of the compositional engineering approach focuses on compositional tuning of the properties and phase behavior in three promising families of lead-free perovskite ferroelectrics: the titanate, alkaline niobate and bismuth perovskites and their solid solutions. The 'structural engineering' approaches focus instead on optimization of microstructural features including grain size, grain orientation or texture, ferroelectric domain size and electrical bias field as potential paths to induce large piezoelectric properties in lead-free piezoceramics. It is suggested that a combination of both compositional and novel structural engineering approaches will be required in order to realize viable lead-free alternatives to current lead-based materials for piezoelectric actuator applications.

  20. High-Temperature Lead-Free Solder Alternatives: Possibilities and Properties

    DEFF Research Database (Denmark)

    High-temperature solders have been widely used as joining materials to provide stable interconnections that resist a severe thermal environment and also to facilitate the drive for miniaturization. High-lead containing solders have been commonly used as high-temperature solders. The development...... of high-temperature lead-free solders has become an important issue for both the electronics and automobile industries because of the health and environmental concerns associated with lead usage. Unfortunately, limited choices are available as high-temperature lead-free solders. This work outlines...... the criteria for the evaluation of a new high-temperature lead-free solder material. A list of potential ternary high-temperature lead-free solder alternatives based on the Au-Sn and Au-Ge systems is proposed. Furthermore, a comprehensive comparison of the high-temperature stability of microstructures...

  1. Magnetoelectric Response in Multiferroic SrFe12O19 Ceramics.

    Directory of Open Access Journals (Sweden)

    Guolong Tan

    Full Text Available We report here realization of ferroelectricity, ferromagnetism and magnetocapacitance effect in singleSrFe12O19ceramic at room temperature. The ceramics demonstrate a saturated polarization hysteresis loop, two nonlinear I-V peaks and large anomaly of dielectric constant near Curie temperature, which confirm the intrinsic ferroelectricity of SrFe12O19 ceramicswith subsequent heat-treatment in O2atmosphere. The remnant polarization of the SrFe12O19 ceramic is estimated to be 103μC/cm2. The ceramic also exhibits strong ferromagnetic characterization, the coercive field and remnant magnetic moment are 6192Oe and 35.8emu/g, respectively. Subsequent annealing SrFe12O19 ceramics in O2 plays a key role on revealing its intrinsic ferroelectricity and improving the ferromagnetism through transforming Fe2+ into Fe3+. By applying a magnetic field, the capacitance demonstrates remarkable change along with B field, the maximum rate of change in ε (Δε(B/ε(0 is 1174%, which reflects a giant magnetocapacitance effect in SrFe12O19. XPS and molecular magnetic moment measurements confirmed the transformation of Fe2+ into Fe3+ and removal of oxygen vacancies upon O2 heat treatment. These combined functional responses in SrFe12O19 ceramics opens substantial possibilities for applications in novel electric devices.

  2. Hidden magnetic states emergent under electric field, in a room temperature composite magnetoelectric multiferroic

    Czech Academy of Sciences Publication Activity Database

    Clarkson, J.D.; Fina, I.; Liu, Z.Q.; Lee, Y.; Kim, J.; Frontera, C.; Cordero, K.; Wisotzki, S.; Sánchez, F.; Sort, J.; Hsu, S.L.; Ko, C.; Aballe, L.; Foerster, M.; Wu, J.; Christen, H.M.; Heron, J.T.; Schlom, D. G.; Salahuddin, S.; Kioussis, N.; Fontcuberta, J.; Martí, Xavier; Ramesh, R.

    2017-01-01

    Roč. 7, č. 1 (2017), s. 1-7, č. článku 15460. ISSN 2045-2322 R&D Projects: GA ČR GB14-37427G Institutional support: RVO:68378271 Keywords : antiferromagnetic phase-transition * total-energy calculations * wave basis-set Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 4.259, year: 2016

  3. Sample-size resonance, ferromagnetic resonance and magneto-permittivity resonance in multiferroic nano-BiFeO{sub 3}/paraffin composites at room temperature

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Lei; Li, Zhenyu; Jiang, Jia; An, Taiyu; Qin, Hongwei; Hu, Jifan, E-mail: hujf@sdu.edu.cn

    2017-01-01

    In the present work, we demonstrate that ferromagnetic resonance and magneto-permittivity resonance can be observed in appropriate microwave frequencies at room temperature for multiferroic nano-BiFeO{sub 3}/paraffin composite sample with an appropriate sample-thickness (such as 2 mm). Ferromagnetic resonance originates from the room-temperature weak ferromagnetism of nano-BiFeO{sub 3}. The observed magneto-permittivity resonance in multiferroic nano-BiFeO{sub 3} is connected with the dynamic magnetoelectric coupling through Dzyaloshinskii–Moriya (DM) magnetoelectric interaction or the combination of magnetostriction and piezoelectric effects. In addition, we experimentally observed the resonance of negative imaginary permeability for nano BiFeO{sub 3}/paraffin toroidal samples with longer sample thicknesses D=3.7 and 4.9 mm. Such resonance of negative imaginary permeability belongs to sample-size resonance. - Highlights: • Nano-BiFeO{sub 3}/paraffin composite shows a ferromagnetic resonance. • Nano-BiFeO{sub 3}/paraffin composite shows a magneto-permittivity resonance. • Resonance of negative imaginary permeability in BiFeO{sub 3} is a sample-size resonance. • Nano-BiFeO{sub 3}/paraffin composite with large thickness shows a sample-size resonance.

  4. Sample-size resonance, ferromagnetic resonance and magneto-permittivity resonance in multiferroic nano-BiFeO3/paraffin composites at room temperature

    International Nuclear Information System (INIS)

    Wang, Lei; Li, Zhenyu; Jiang, Jia; An, Taiyu; Qin, Hongwei; Hu, Jifan

    2017-01-01

    In the present work, we demonstrate that ferromagnetic resonance and magneto-permittivity resonance can be observed in appropriate microwave frequencies at room temperature for multiferroic nano-BiFeO 3 /paraffin composite sample with an appropriate sample-thickness (such as 2 mm). Ferromagnetic resonance originates from the room-temperature weak ferromagnetism of nano-BiFeO 3 . The observed magneto-permittivity resonance in multiferroic nano-BiFeO 3 is connected with the dynamic magnetoelectric coupling through Dzyaloshinskii–Moriya (DM) magnetoelectric interaction or the combination of magnetostriction and piezoelectric effects. In addition, we experimentally observed the resonance of negative imaginary permeability for nano BiFeO 3 /paraffin toroidal samples with longer sample thicknesses D=3.7 and 4.9 mm. Such resonance of negative imaginary permeability belongs to sample-size resonance. - Highlights: • Nano-BiFeO 3 /paraffin composite shows a ferromagnetic resonance. • Nano-BiFeO 3 /paraffin composite shows a magneto-permittivity resonance. • Resonance of negative imaginary permeability in BiFeO 3 is a sample-size resonance. • Nano-BiFeO 3 /paraffin composite with large thickness shows a sample-size resonance.

  5. Effects of Al substitution and thermal annealing on magnetoelectric Ba0.5Sr1.5Zn2Fe12O22 investigated by the enhancement factor of 57Fe nuclear magnetic resonance.

    Science.gov (United States)

    Kwon, Sangil; Kang, Byeongki; Kim, Changsoo; Jo, Euna; Lee, Soonchil; Chai, Yi Sheng; Chun, Sae Hwan; Kim, Kee Hoon

    2014-04-09

    The magnetoelectric properties of hexaferrite Ba0.5Sr1.5Zn2Fe12O22 are significantly improved by Al substitution and thermal annealing. Measuring the enhancement factor of 57Fe NMR, we found direct microscopic evidence that the magnetic moments of the L and S blocks are rotated by a magnetic field in such a way as to increase the net magnetic moment of a magnetic unit, even after the field is removed. Al substitution makes magnetoelectric property arise easily by suppressing the easy-plane anisotropy. The effect of thermal annealing is to stabilize the multiferroic state by reducing the number of pinning sites and the electron spin fluctuation. The transverse conic structure gradually changes to the alternating longitudinal conic structure where spins fluctuate more severely.

  6. Theory of orbital magnetoelectric response

    International Nuclear Information System (INIS)

    Malashevich, Andrei; Souza, Ivo; Coh, Sinisa; Vanderbilt, David

    2010-01-01

    We extend the recently developed theory of bulk orbital magnetization to finite electric fields, and use it to calculate the orbital magnetoelectric (ME) response of periodic insulators. Working in the independent-particle framework, we find that the finite-field orbital magnetization can be written as a sum of three gauge-invariant contributions, one of which has no counterpart at zero field. The extra contribution is collinear with and explicitly dependent on the electric field. The expression for the orbital magnetization is suitable for first-principles implementations, allowing one to calculate the ME response coefficients by numerical differentiation. Alternatively, perturbation-theory techniques may be used, and for that purpose we derive an expression directly for the linear ME tensor by taking the first field-derivative analytically. Two types of terms are obtained. One, the 'Chern-Simons' term, depends only on the unperturbed occupied orbitals and is purely isotropic. The other, 'Kubo' terms, involve the first-order change in the orbitals and give isotropic as well as anisotropic contributions to the response. In ordinary ME insulators all terms are generally present, while in strong Z 2 topological insulators only the Chern-Simons term is allowed, and is quantized. In order to validate the theory, we have calculated under periodic boundary conditions the linear ME susceptibility for a 3D tight-binding model of an ordinary ME insulator, using both the finite-field and perturbation-theory expressions. The results are in excellent agreement with calculations on bounded samples.

  7. Colossal magnetodielectric effect caused by magnetoelectric effect ...

    Indian Academy of Sciences (India)

    -D laminate composite under low magnetic field. When the composite is placed in an external a.c. magnetic field, magnetoelectric effect is produced, as a result, the dielectric properties of the Pb(Zr,Ti)O3 is changed, i.e. magnetodielectric effect ...

  8. Colossal magnetodielectric effect caused by magnetoelectric effect ...

    Indian Academy of Sciences (India)

    The colossal magnetodielectric effect is reported in Pb(Zr,Ti)O3/Terfenol-D laminate composite under low magnetic field. When the composite is placed in an external a.c. magnetic field, magnetoelectric effect is produced, as a result, the dielectric properties of the Pb(Zr,Ti)O3 is changed, i.e. magnetodielectric effect. Both the ...

  9. Linear Magnetoelectric Effect by Orbital Magnetism

    NARCIS (Netherlands)

    Scaramucci, A.; Bousquet, E.; Fechner, M.; Mostovoy, M.; Spaldin, N. A.

    2012-01-01

    We use symmetry analysis and first-principles calculations to show that the linear magnetoelectric effect can originate from the response of orbital magnetic moments to the polar distortions induced by an applied electric field. Using LiFePO4 as a model compound we show that spin-orbit coupling

  10. Magnetically tunable dielectric, impedance and magnetoelectric response in MnFe{sub 2}O{sub 4}/(Pb{sub 1−x}Sr{sub x})TiO{sub 3} composites thin films

    Energy Technology Data Exchange (ETDEWEB)

    Bala, Kanchan, E-mail: bala.kanchan1987@gmail.com [Department of Physics, Himachal Pradesh University, Shimla 171005 (India); Kotnala, R.K. [CSIR, National Physical Laboratory, Dr. K.S. Krishnan Road, New Delhi 110012 (India); Negi, N.S., E-mail: nsn_phy_hpu@yahoo.com [Department of Physics, Himachal Pradesh University, Shimla 171005 (India)

    2017-02-15

    We have synthesized piezomagnetic–piezoelectric composites thin films MnFe{sub 2}O{sub 4}/(Pb{sub 1−x}Sr{sub x})TiO{sub 3}, where x=0.1, 0.2, and 0.3, using the metalorganic deposition (MOD) reaction method. The structural and microstructural analysis using the X-ray diffraction (XRD), AFM, and SEM reveals the presence of homogenous growth of both pervoskite and spinel phases in the composite films. Our results show that all the composites films exhibit good multiferroic as well as considerable magnetoelectric coupling. The impedance (Z′ and Z″) and electrical modulus (M′ and M″) Nyquist plots show distinct electrical responses with the magnetic field. Our analyses suggest that this electrical response arises due to the coexistence of the high resistive phase and the comparatively conductive phase in the MFO/PST composite films. The maximum magnetoelectric coefficient (α) is found to be 4.29 V Oe{sup −1} cm{sup −1} and 2.82 V Oe{sup −1} cm{sup −1} for compositions x=0.1 and 0.2. These values are substantially larger than those reported for bilayer composites thin films in literature and make them interesting for room temperature device applications. - Highlights: • Influence of Sr doping on multiferroic and magnetoelectric properties composites thin films of MnFe{sub 2}O{sub 4} and (Pb, Sr)TiO{sub 3}. • Dielectric constant and dielectric loss with application of magnetic field. • Magnetically tunable AC electrical properties. • Magnetoelectric coupling in MnFe{sub 2}O{sub 4}/(Pb, Sr)TiO{sub 3} composite films by passive method.

  11. Magnetoelectric effect in (BiFeO3x–(BaTiO31-x solid solutions

    Directory of Open Access Journals (Sweden)

    Kowal Karol

    2015-03-01

    Full Text Available The aim of the present work was to study magnetoelectric effect (ME in (BiFeO3x-(BaTiO31-x solid solutions in terms of technological conditions applied in the samples fabrication process. The rapidly growing interest in these materials is caused by their multiferroic behaviour, i.e. coexistence of both electric and magnetic ordering. It creates possibility for many innovative applications, e.g. in steering the magnetic memory by electric field and vice versa. The investigated samples of various chemical compositions (i.e. x = 0.7, 0.8 and 0.9 were prepared by the solid-state sintering method under three sets of technological conditions differing in the applied temperature and soaking time. Measurements of the magnetoelectric voltage coefficient αME were performed using a dynamic lock-in technique. The highest value of αME was observed for 0.7BiFeO3-0.3BaTiO3 solid solution sintered at the highest temperature (T = 1153 K after initial electrical poling despite that the soaking time was reduced 10 times in this case.

  12. Voltage Control of Two-Magnon Scattering and Induced Anomalous Magnetoelectric Coupling in Ni–Zn Ferrite

    Energy Technology Data Exchange (ETDEWEB)

    Xue, Xu [Electronic Materials; amp,; Dong, Guohua [Electronic Materials; amp,; Zhou, Ziyao [Electronic Materials; amp,; Xian, Dan [Collaborative Innovation Center of High-End Manufacturing; Hu, Zhongqiang [Electronic Materials; amp,; Ren, Wei [Electronic Materials; amp,; Collaborative Innovation Center of High-End Manufacturing; Ye, Zuo-Guang [Electronic Materials; amp,; Department; Chen, Wei [Materials; Jiang, Zhuang-De [Collaborative Innovation Center of High-End Manufacturing; Liu, Ming [Electronic Materials; amp,; Collaborative Innovation Center of High-End Manufacturing

    2017-12-01

    Controlling spin dynamics through modulation of spin interactions in a fast, compact, and energy-efficient way is compelling for its abundant physical phenomena and great application potential in next-generation voltage controllable spintronic devices. In this work, we report electric field manipulation of spin dynamics-the two-magnon scattering (TMS) effect in Ni0.5Zn0.5Fe2O4 (NZFO)/Pb(Mg2/3Nb1/3)-PbTiO3 (PMN-PT) multiferroic heterostructures, which breaks the bottleneck of magnetostatic interaction-based magnetoelectric (ME) coupling in multiferroics. An alternative approach allowing spin-wave damping to be controlled by external electric field accompanied by a significant enhancement of the ME effect has been demonstrated. A two-way modulation of the TMS effect with a large magnetic anisotropy change up to 688 Oe has been obtained, referring to a 24 times ME effect enhancement at the TMS critical angle at room temperature. Furthermore, the anisotropic spin-freezing behaviors of NZFO were first determined via identifying the spatial magnetic anisotropy fluctuations. A large spin-freezing temperature change of 160 K induced by the external electric field was precisely determined by electron spin resonance.

  13. Voltage Control of Two-Magnon Scattering and Induced Anomalous Magnetoelectric Coupling in Ni-Zn Ferrite.

    Science.gov (United States)

    Xue, Xu; Dong, Guohua; Zhou, Ziyao; Xian, Dan; Hu, Zhongqiang; Ren, Wei; Ye, Zuo-Guang; Chen, Wei; Jiang, Zhuang-De; Liu, Ming

    2017-12-13

    Controlling spin dynamics through modulation of spin interactions in a fast, compact, and energy-efficient way is compelling for its abundant physical phenomena and great application potential in next-generation voltage controllable spintronic devices. In this work, we report electric field manipulation of spin dynamics-the two-magnon scattering (TMS) effect in Ni 0.5 Zn 0.5 Fe 2 O 4 (NZFO)/Pb(Mg 2/3 Nb 1/3 )-PbTiO 3 (PMN-PT) multiferroic heterostructures, which breaks the bottleneck of magnetostatic interaction-based magnetoelectric (ME) coupling in multiferroics. An alternative approach allowing spin-wave damping to be controlled by external electric field accompanied by a significant enhancement of the ME effect has been demonstrated. A two-way modulation of the TMS effect with a large magnetic anisotropy change up to 688 Oe has been obtained, referring to a 24 times ME effect enhancement at the TMS critical angle at room temperature. Furthermore, the anisotropic spin-freezing behaviors of NZFO were first determined via identifying the spatial magnetic anisotropy fluctuations. A large spin-freezing temperature change of 160 K induced by the external electric field was precisely determined by electron spin resonance.

  14. Raman spectra, photoluminescence, magnetism and magnetoelectric coupling in pure and Fe doped BaTiO{sub 3} nanostructures

    Energy Technology Data Exchange (ETDEWEB)

    Verma, Kuldeep Chand, E-mail: kuldeep0309@yahoo.co.in [Akal School of Physics, Eternal University, Baru Sahib, Sirmour, Himachal Pradesh 173 101 (India); Gupta, Vinay [Department of Physics and Astrophysics, University of Delhi, Delhi 110 007 (India); Kaur, Jaspreet [Akal School of Physics, Eternal University, Baru Sahib, Sirmour, Himachal Pradesh 173 101 (India); Kotnala, R.K. [National Physical Laboratory, New Delhi 110 012 (India)

    2013-11-25

    Highlights: •Multiferroic nanostructures by surfactant free hydrothermal method. •Stoichiometric effect on nanostructures. •Raman spectroscopy and Photoluminescence. •Transmission electron microscopy. •Magnetoelectric coupling. -- Abstract: Structural, microstructural, Raman spectroscopy, photoluminescence, saturation magnetization and magnetoelectric (ME) measurement of BaTiO{sub 3} (BFT0) and BaFe{sub 0.01}Ti{sub 0.99}O{sub 3} (BFT1) nanostructures have been studied. BFT0 and BFT1 were prepared by a hydrothermal method of processing temperature 180 °C/48 h. The X-ray diffraction pattern shows the coexistence of cubic/tetragonal and hexagonal phases for BFT0 and cubic/tetragonal for BFT1. The Raman spectra confirm the coexistence of tetragonal and hexagonal phases in BFT0 and cubic in BFT1. Transmission electron microscopy images show nanorods of hexagonal shaped faces for BFT0 and cubic shaped nanowires for BFT1. The resulting mechanism of the formation of these nanostructures is discussed. The experimental and theoretical results by photoluminescence are related to the degree of disorder existing in both BFT0 and BFT1 and suggest the presence of localized states existing inside of the band gap which are directly affected for degree of order–disorder. A strong ferromagnetism in BFT1 and diamagnetism in BFT0 is observed by magnetic hysteresis. As BFT1 is ferromagnetic, the value of linear coefficient, α called Magnetoelectric (ME) coefficient is calculated as ∼16 mV/Oe cm at a fixed frequency of 850 Hz. This ME coefficient α corresponds to induction of polarization by a magnetic field or of magnetization by an electric field. The observed optimum dc bias field at which the maximum ME coupling occurs is ∼750 Oe.

  15. Raman spectra, photoluminescence, magnetism and magnetoelectric coupling in pure and Fe doped BaTiO3 nanostructures

    International Nuclear Information System (INIS)

    Verma, Kuldeep Chand; Gupta, Vinay; Kaur, Jaspreet; Kotnala, R.K.

    2013-01-01

    Highlights: •Multiferroic nanostructures by surfactant free hydrothermal method. •Stoichiometric effect on nanostructures. •Raman spectroscopy and Photoluminescence. •Transmission electron microscopy. •Magnetoelectric coupling. -- Abstract: Structural, microstructural, Raman spectroscopy, photoluminescence, saturation magnetization and magnetoelectric (ME) measurement of BaTiO 3 (BFT0) and BaFe 0.01 Ti 0.99 O 3 (BFT1) nanostructures have been studied. BFT0 and BFT1 were prepared by a hydrothermal method of processing temperature 180 °C/48 h. The X-ray diffraction pattern shows the coexistence of cubic/tetragonal and hexagonal phases for BFT0 and cubic/tetragonal for BFT1. The Raman spectra confirm the coexistence of tetragonal and hexagonal phases in BFT0 and cubic in BFT1. Transmission electron microscopy images show nanorods of hexagonal shaped faces for BFT0 and cubic shaped nanowires for BFT1. The resulting mechanism of the formation of these nanostructures is discussed. The experimental and theoretical results by photoluminescence are related to the degree of disorder existing in both BFT0 and BFT1 and suggest the presence of localized states existing inside of the band gap which are directly affected for degree of order–disorder. A strong ferromagnetism in BFT1 and diamagnetism in BFT0 is observed by magnetic hysteresis. As BFT1 is ferromagnetic, the value of linear coefficient, α called Magnetoelectric (ME) coefficient is calculated as ∼16 mV/Oe cm at a fixed frequency of 850 Hz. This ME coefficient α corresponds to induction of polarization by a magnetic field or of magnetization by an electric field. The observed optimum dc bias field at which the maximum ME coupling occurs is ∼750 Oe

  16. Advancement on Lead-Free Organic-Inorganic Halide Perovskite Solar Cells: A Review.

    Science.gov (United States)

    Sani, Faruk; Shafie, Suhaidi; Lim, Hong Ngee; Musa, Abubakar Ohinoyi

    2018-06-14

    Remarkable attention has been committed to the recently discovered cost effective and solution processable lead-free organic-inorganic halide perovskite solar cells. Recent studies have reported that, within five years, the reported efficiency has reached 9.0%, which makes them an extremely promising and fast developing candidate to compete with conventional lead-based perovskite solar cells. The major challenge associated with the conventional perovskite solar cells is the toxic nature of lead (Pb) used in the active layer of perovskite material. If lead continues to be used in fabricating solar cells, negative health impacts will result in the environment due to the toxicity of lead. Alternatively, lead free perovskite solar cells could give a safe way by substituting low-cost, abundant and non toxic material. This review focuses on formability of lead-free organic-inorganic halide perovskite, alternative metal cations candidates to replace lead (Pb), and possible substitutions of organic cations, as well as halide anions in the lead-free organic-inorganic halide perovskite architecture. Furthermore, the review gives highlights on the impact of organic cations, metal cations and inorganic anions on stability and the overall performance of lead free perovskite solar cells.

  17. Magnetoelectric coupling effect in transition metal modified polycrystalline BiFeO{sub 3} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Sreenivas Puli, Venkata, E-mail: pvsri123@gmail.com [Department of Physics and Engineering Physics, Tulane University, New Orleans, LA 70118 (United States); Department of Physics and Institute of Functional Nanomaterials, University of Puerto Rico, San Juan, PR 00936 (United States); Kumar Pradhan, Dhiren [Department of Physics and Institute of Functional Nanomaterials, University of Puerto Rico, San Juan, PR 00936 (United States); Gollapudi, Sreenivasulu [Department of Physics, Oakland University, Rochester, MI 48309-4401 (United States); Coondoo, Indrani [Department of Materials and Ceramic and CICECO, University of Aveiro, 3810-193 Aveiro (Portugal); Panwar, Neeraj [Department of Physics, Central University of Rajasthan, Bandar Sindri, Kishangarh 305801, Rajasthan (India); Adireddy, Shiva; Chrisey, Douglas B. [Department of Physics and Engineering Physics, Tulane University, New Orleans, LA 70118 (United States); Katiyar, Ram S. [Department of Physics and Institute of Functional Nanomaterials, University of Puerto Rico, San Juan, PR 00936 (United States)

    2014-11-15

    Rare-earth (Sm) and transition metal (Co) modified polycrystalline BiFeO{sub 3} (BFO) thin films have been deposited on Pt/TiO{sub 2}/SiO{sub 2}/Si substrate successfully through pulsed laser deposition (PLD) technique. Piezoelectric, leakage current and temperature dependent dielectric and magnetic behaviour were investigated for the films. Typical “butterfly-shaped” loop were observed in BSFCO films with an effective piezoelectric constant (d{sub 33}) ∼94 pm/V at 0.6 MV/cm. High dielectric constant ∼900 and low dielectric loss ∼0.25 were observed at room temperature. M–H loops have shown relatively high saturation magnetization ∼35 emu/cm{sup 3} at a maximum field of H ∼20 kOe. Enhanced magnetoelectric coupling response is observed under applied magnetic field. The multiferroic, piezoelectric, leakage current behaviours were explored. Such studies should be helpful in designing multiferroic materials based on BSFCO films. - Highlights: • Transition metal modified polycrystalline BiFeO{sub 3} thin films prepared using PLD. • High ME-coupling response was observed in co-substituted BiFeO{sub 3} thin films. • High magnetization ∼35 emu/cm{sup 3} at a maximum field of H ∼20 kOe. • Low leakage current might be due to co-substitution in BiFeO{sub 3} thin films. • A notable piezoelectric constant d{sub 33} ∼94 pm/V was found in BiFeO{sub 3} thin films.

  18. Magnetoelectric coupling effect in transition metal modified polycrystalline BiFeO3 thin films

    International Nuclear Information System (INIS)

    Sreenivas Puli, Venkata; Kumar Pradhan, Dhiren; Gollapudi, Sreenivasulu; Coondoo, Indrani; Panwar, Neeraj; Adireddy, Shiva; Chrisey, Douglas B.; Katiyar, Ram S.

    2014-01-01

    Rare-earth (Sm) and transition metal (Co) modified polycrystalline BiFeO 3 (BFO) thin films have been deposited on Pt/TiO 2 /SiO 2 /Si substrate successfully through pulsed laser deposition (PLD) technique. Piezoelectric, leakage current and temperature dependent dielectric and magnetic behaviour were investigated for the films. Typical “butterfly-shaped” loop were observed in BSFCO films with an effective piezoelectric constant (d 33 ) ∼94 pm/V at 0.6 MV/cm. High dielectric constant ∼900 and low dielectric loss ∼0.25 were observed at room temperature. M–H loops have shown relatively high saturation magnetization ∼35 emu/cm 3 at a maximum field of H ∼20 kOe. Enhanced magnetoelectric coupling response is observed under applied magnetic field. The multiferroic, piezoelectric, leakage current behaviours were explored. Such studies should be helpful in designing multiferroic materials based on BSFCO films. - Highlights: • Transition metal modified polycrystalline BiFeO 3 thin films prepared using PLD. • High ME-coupling response was observed in co-substituted BiFeO 3 thin films. • High magnetization ∼35 emu/cm 3 at a maximum field of H ∼20 kOe. • Low leakage current might be due to co-substitution in BiFeO 3 thin films. • A notable piezoelectric constant d 33 ∼94 pm/V was found in BiFeO 3 thin films

  19. Exchange bias and strain effect co-modulated magnetic symmetry in La0.6Sr0.4MnO3/orthorhombic-YMnO3 multiferroic heterostructures

    Science.gov (United States)

    Zheng, Dongxing; Gong, Junlu; Jin, Chao; Li, Peng; Feng, Liefeng; Bai, Haili

    2017-06-01

    The exchange bias and strain effect co-modulated magnetic symmetry in all oxide La0.6Sr0.4MnO3 (LSMO) and orthorhombic YMnO3 (YMO) multiferroic heterostructures were studied. Because of the lattice mismatch between the LSMO and YMO layers, the LSMO layer exhibits a 90° rotation growth on the YMO layer. The strain induced growth not only leads to a 90° phase shift in the anisotropic magnetoresistance (AMR) curves, but also brings a two-fold symmetric magnetoelastic coupling energy along the LSMO [1 1 0] direction. With the incorporation of magnetoelastic coupling energy and exchange coupling energy, the exchange bias induced torque shows a phase shift and causes the asymmetry of the peak position and value in the AMR curves. This work illustrates a modulated magnetic symmetry in ferromagnetic/multiferroic systems by interfacial exchange coupling and strain effect, which will benefit the design of magnetoelectric devices.

  20. Exchange bias and strain effect co-modulated magnetic symmetry in La0.6Sr0.4MnO3/orthorhombic-YMnO3 multiferroic heterostructures

    KAUST Repository

    Zheng, Dongxing

    2017-05-03

    The exchange bias and strain effect co-modulated magnetic symmetry in all oxide La0.6Sr0.4MnO3 (LSMO) and orthorhombic YMnO3 (YMO) multiferroic heterostructures were studied. Because of the lattice mismatch between the LSMO and YMO layers, the LSMO layer exhibits a 90° rotation growth on the YMO layer. The strain induced growth not only leads to a 90° phase shift in the anisotropic magnetoresistance (AMR) curves, but also brings a two-fold symmetric magnetoelastic coupling energy along the LSMO $[1\\\\,1\\\\,0]$ direction. With the incorporation of magnetoelastic coupling energy and exchange coupling energy, the exchange bias induced torque shows a phase shift and causes the asymmetry of the peak position and value in the AMR curves. This work illustrates a modulated magnetic symmetry in ferromagnetic/multiferroic systems by interfacial exchange coupling and strain effect, which will benefit the design of magnetoelectric devices.

  1. Exchange bias and strain effect co-modulated magnetic symmetry in La0.6Sr0.4MnO3/orthorhombic-YMnO3 multiferroic heterostructures

    KAUST Repository

    Zheng, Dongxing; Gong, Junlu; Jin, Chao; Li, Peng; Feng, Liefeng; Bai, Haili

    2017-01-01

    The exchange bias and strain effect co-modulated magnetic symmetry in all oxide La0.6Sr0.4MnO3 (LSMO) and orthorhombic YMnO3 (YMO) multiferroic heterostructures were studied. Because of the lattice mismatch between the LSMO and YMO layers, the LSMO layer exhibits a 90° rotation growth on the YMO layer. The strain induced growth not only leads to a 90° phase shift in the anisotropic magnetoresistance (AMR) curves, but also brings a two-fold symmetric magnetoelastic coupling energy along the LSMO $[1\\,1\\,0]$ direction. With the incorporation of magnetoelastic coupling energy and exchange coupling energy, the exchange bias induced torque shows a phase shift and causes the asymmetry of the peak position and value in the AMR curves. This work illustrates a modulated magnetic symmetry in ferromagnetic/multiferroic systems by interfacial exchange coupling and strain effect, which will benefit the design of magnetoelectric devices.

  2. Bias magnetic field and test period dependences of direct and converse magnetoelectric hysteresis of tri-layered magnetoelectric composite

    Science.gov (United States)

    Zhou, Yun; Li, Xiao-Hong; Wang, Jian-Feng; Zhou, Hao-Miao; Cao, Dan; Jiao, Zhi-Wei; Xu, Long; Li, Qi-Hao

    2018-04-01

    The direct and converse magnetoelectric hysteresis behavior for a tri-layered composite has been comparatively investigated and significant similarities have been observed. The results show that both the direct and converse magnetoelectric hysteresis is deeply affected by the bias magnetic field and test period. The test time hysteresis caused by a fast varying bias magnetic field can be reduced by prolonging the test period. The observed coercive field, remanence, and ratio of remanence of the direct and converse magnetoelectric effects with the test period obey an exponential decay law. A hysteretic nonlinear magnetoelectric theoretical model for the symmetrical tri-layered structure has been proposed based on a nonlinear constitutive model and pinning effect. The numerical calculation shows that the theoretical results are in good agreement with the experimental results. These findings not only provide insight into the examination and practical applications of magnetoelectric materials, but also propose a theoretical frame for studying the hysteretic characteristics of the magnetoelectric effect.

  3. PCBs with immersion tin finish - some experiences with lead-free reflow process

    Energy Technology Data Exchange (ETDEWEB)

    Bukat, K.; Koziol, G.; Sitek, J.; Borecki, J.; Hackiewicz, H. [Tele and Radio Research Inst., Warsaw (Poland); Merkle, H.; Schroeder, S. [Ormecon Chemie GmbH and Co. KG, Ammersbek (Germany); Girulska, A.; Gardela, K. [Eldos Sp. z o.o., Wroclaw (Poland)

    2004-07-01

    Substitution of lead-free solders in electronic assemblies requires changes in the conventional SnPb finishes of PCBs. The Craft project ''PRINT'' objectives respond to this challenge. Its main goal is to develop and implement the new technology of high solderability immersion tin for printed circuit boards at small and medium enterprises. The subject of the research was organic based immersion tin coating which would fulfil demands of SMT. In the paper the results of reflow soldering process on PCBs covered by Ormecon registered immersion tin finish with using lead-free solder pastes will be described. Solderability of tin coating as well as wettability of lead-free solder paste will be presented. (orig.)

  4. Key questions and responses regarding the transition to use of lead-free ammunition

    DEFF Research Database (Denmark)

    Thomas, Vernon G.; Kanstrup, Niels; Gremse, Carl

    2015-01-01

    Questions and concerns about the use of lead-free ammunition in hunting were encountered during the Oxford Lead Symposium. Many originated from commonly-held, but unsubstantiated, reports that have hindered the transition to use of lead-free ammunition in the UK and elsewhere. This paper examines...... and answers the principal reservations raised about the use of lead-free hunting ammunition. The issue of how the evidence for lead exposure and toxicity to wildlife from discharged lead shot cartridges could be better communicated to the public to enhance adoption of lead–free ammunition is addressed....... The paper presents evidence to assuage concerns about the effectiveness and nontoxicity of lead ammunition substitutes, their suitability for British shooting and weapons, and their role in wildlife health protection. Collectively, these answers to concerns could lower the public resistance to use of lead...

  5. Performance of Lead-Free versus Lead-Based Hunting Ammunition in Ballistic Soap

    Science.gov (United States)

    Gremse, Felix; Krone, Oliver; Thamm, Mirko; Kiessling, Fabian; Tolba, René Hany; Rieger, Siegfried; Gremse, Carl

    2014-01-01

    Background Lead-free hunting bullets are an alternative to lead-containing bullets which cause health risks for humans and endangered scavenging raptors through lead ingestion. However, doubts concerning the effectiveness of lead-free hunting bullets hinder the wide-spread acceptance in the hunting and wildlife management community. Methods We performed terminal ballistic experiments under standardized conditions with ballistic soap as surrogate for game animal tissue to characterize dimensionally stable, partially fragmenting, and deforming lead-free bullets and one commonly used lead-containing bullet. The permanent cavities created in soap blocks are used as a measure for the potential wound damage. The soap blocks were imaged using computed tomography to assess the volume and shape of the cavity and the number of fragments. Shots were performed at different impact speeds, covering a realistic shooting range. Using 3D image segmentation, cavity volume, metal fragment count, deflection angle, and depth of maximum damage were determined. Shots were repeated to investigate the reproducibility of ballistic soap experiments. Results All bullets showed an increasing cavity volume with increasing deposited energy. The dimensionally stable and fragmenting lead-free bullets achieved a constant conversion ratio while the deforming copper and lead-containing bullets showed a ratio, which increases linearly with the total deposited energy. The lead-containing bullet created hundreds of fragments and significantly more fragments than the lead-free bullets. The deflection angle was significantly higher for the dimensionally stable bullet due to its tumbling behavior and was similarly low for the other bullets. The deforming bullets achieved higher reproducibility than the fragmenting and dimensionally stable bullets. Conclusion The deforming lead-free bullet closely resembled the deforming lead-containing bullet in terms of energy conversion, deflection angle, cavity shape

  6. Physical properties of lead free solders in liquid and solid state

    Energy Technology Data Exchange (ETDEWEB)

    Mhiaoui, Souad

    2007-04-17

    The European legislation prohibits the use of lead containing solders in Europe. However, lead free solders have a higher melting point (typical 20%) and their mechanical characteristics are worse. Additional problems are aging and adhesion of the solder on the electronic circuits. Thus, research activities must focus on the optimization of the properties of Sn-Ag-Cu based lead free solders chosen by the industry. Two main objectives are treated in this work. In the center of the first one is the study of curious hysteresis effects of metallic cadmium-antimony alloys after thermal cycles by measuring electronic transport phenomena (thermoelectric power and electrical resistivity). The second objective, within the framework of ''cotutelle'' between the universities of Metz and of Chemnitz and supported by COST531, is to study more specifically lead free solders. A welding must well conduct electricity and well conduct and dissipate heat. In Metz, we determined the electrical conductivity, the thermoelectric power and the thermal conductivity of various lead free solders (Sn-Ag-Cu, Sn-Cu, Sn-Ag, Sn-Sb) as well in the liquid as well in the solid state. The results have been compared to classical lead-tin (Pb-Sn) solders. In Chemnitz we measured the surface tension, the interfacial tension and the density of lead free solders. We also measured the viscosity of these solders without and with additives, in particular nickel. These properties were related to the industrial problems of wettability and spreadability. Lastly, we solidified alloys under various conditions. We observed undercooling. We developed a technique of mixture of nanocrystalline powder with lead free solders ''to sow'' the liquid bath in order to obtain ''different'' solids which were examined using optical and electron microscopy. (orig.)

  7. Performance of lead-free versus lead-based hunting ammunition in ballistic soap.

    Directory of Open Access Journals (Sweden)

    Felix Gremse

    Full Text Available BACKGROUND: Lead-free hunting bullets are an alternative to lead-containing bullets which cause health risks for humans and endangered scavenging raptors through lead ingestion. However, doubts concerning the effectiveness of lead-free hunting bullets hinder the wide-spread acceptance in the hunting and wildlife management community. METHODS: We performed terminal ballistic experiments under standardized conditions with ballistic soap as surrogate for game animal tissue to characterize dimensionally stable, partially fragmenting, and deforming lead-free bullets and one commonly used lead-containing bullet. The permanent cavities created in soap blocks are used as a measure for the potential wound damage. The soap blocks were imaged using computed tomography to assess the volume and shape of the cavity and the number of fragments. Shots were performed at different impact speeds, covering a realistic shooting range. Using 3D image segmentation, cavity volume, metal fragment count, deflection angle, and depth of maximum damage were determined. Shots were repeated to investigate the reproducibility of ballistic soap experiments. RESULTS: All bullets showed an increasing cavity volume with increasing deposited energy. The dimensionally stable and fragmenting lead-free bullets achieved a constant conversion ratio while the deforming copper and lead-containing bullets showed a ratio, which increases linearly with the total deposited energy. The lead-containing bullet created hundreds of fragments and significantly more fragments than the lead-free bullets. The deflection angle was significantly higher for the dimensionally stable bullet due to its tumbling behavior and was similarly low for the other bullets. The deforming bullets achieved higher reproducibility than the fragmenting and dimensionally stable bullets. CONCLUSION: The deforming lead-free bullet closely resembled the deforming lead-containing bullet in terms of energy conversion

  8. A Feasibility Study of Lead Free Solders for Level 1 Packaging Applications

    DEFF Research Database (Denmark)

    Chidambaram, Vivek; Hald, John; Hattel, Jesper Henri

    2009-01-01

    An attempt has been made to determine the lead free ternary combinations that satisfied the solidification requirement for a solder used in level 1 packaging applications, using the CALPHAD approach. The segregation profiles of the promising candidates were analyzed after scrutinizing the equilib......An attempt has been made to determine the lead free ternary combinations that satisfied the solidification requirement for a solder used in level 1 packaging applications, using the CALPHAD approach. The segregation profiles of the promising candidates were analyzed after scrutinizing...

  9. Equivalent circuit method research of resonant magnetoelectric characteristic in magnetoelectric laminate composites using nonlinear magnetostrictive constitutive model

    International Nuclear Information System (INIS)

    Zhou, Hao-Miao; Li, Chao; Xuan, Li-Ming; Zhao, Ji-Xiang; Wei, Jing

    2011-01-01

    This paper analyzes the magnetoelectric (ME) response around the resonance frequency in the magnetostrictive/piezoelectric/magnetostrictive (MPM) magnetoelectric laminate composites. Following the equivalent circuit method and considering the mechanical loss, we select the nonlinear magnetostrictive constitutive model to present a novel explicit nonlinear expression for the resonant magnetoelectric (ME) coefficient of the magnetoelectric laminate composites. Compared with the experimental results, the predicted resonant ME coefficient of the explicit expression shows a good agreement both qualitatively and quantitatively. Also, when the electromechanical coupling factor of the piezoelectric material, k 31 p , is small, this explicit expression can be reduced to the existing model. On this basis, this paper considers and predicts the magnetoelectric conversion characteristics of the magnetoelectric laminate composites, calculates and analyzes the influences of the thickness ratio of magnetostrictive layer and piezoelectric material, bias magnetic field, and saturation magnetostrictive coefficient on the resonant ME coefficient. This research can provide a theoretical basis for the preparation of magnetoelectric devices with good magnetoelectric conversion characteristics, such as magnetoelectric sensors, energy harvesting transducers, microwave devices etc

  10. Development of magnetoelectric nanocomposite for soft technology

    Science.gov (United States)

    Bitla, Yugandhar; Chu, Ying-Hao

    2018-06-01

    The proliferation of flexible and stretchable electronics has led to substantial advancements in principles, material combinations and technologies. The integration of magnetoelectric systems in soft electronics is inevitable by virtue of their extensive applications. Recently, 2D layered materials have emerged as potential candidates due to their excellent flexibility and atomic-scale thickness scalability in addition to their interesting physics. This paper presents a new perspective on the development of magnetoelectric nanocomposites through materials engineering on a pliant mica with excellent mechanical, thermal and chemical stabilities. The unique features of 2D muscovite mica and the power of van der Waals epitaxy are expected to contribute significantly to the emerging transparent soft-technology research applications.

  11. Multiferroic tunnel junctions and ferroelectric control of magnetic state at interface (invited)

    KAUST Repository

    Yin, Y. W.

    2015-03-03

    As semiconductor devices reach ever smaller dimensions, the challenge of power dissipation and quantum effect place a serious limit on the future device scaling. Recently, a multiferroic tunnel junction (MFTJ) with a ferroelectric barrier sandwiched between two ferromagnetic electrodes has drawn enormous interest due to its potential applications not only in multi-level data storage but also in electric field controlled spintronics and nanoferronics. Here, we present our investigations on four-level resistance states, giant tunneling electroresistance (TER) due to interfacial magnetoelectric coupling, and ferroelectric control of spin polarized tunneling in MFTJs. Coexistence of large tunneling magnetoresistance and TER has been observed in manganite/(Ba, Sr)TiO3/manganite MFTJs at low temperatures and room temperature four-resistance state devices were also obtained. To enhance the TER for potential logic operation with a magnetic memory, La0.7Sr0.3MnO3/BaTiO3/La0.5Ca0.5MnO3 /La0.7Sr0.3MnO3 MFTJs were designed by utilizing a bilayer tunneling barrier in which BaTiO3 is ferroelectric and La0.5Ca0.5MnO3 is close to ferromagnetic metal to antiferromagnetic insulator phase transition. The phase transition occurs when the ferroelectric polarization is reversed, resulting in an increase of TER by two orders of magnitude. Tunneling magnetoresistance can also be controlled by the ferroelectric polarization reversal, indicating strong magnetoelectric coupling at the interface.

  12. Magneto-Electric Dipole Antenna Arrays

    OpenAIRE

    Gupta, Shulabh; Jiang, Li Jun; Caloz, Christophe

    2014-01-01

    A planar magneto-electric (ME) dipole antenna array is proposed and demonstrated by both full-wave analysis and experiments. The proposed structure leverages the infinite wavelength propagation characteristic of composite right/left-handed (CRLH) transmission lines to form high-gain magnetic radiators combined with radial conventional electric radiators, where the overall structure is excited by a single differential feed. The traveling-wave type nature of the proposed ME-dipole antenna enabl...

  13. The thermodynamic database COST MP0602 for materials for high-temperature lead-free soldering

    Czech Academy of Sciences Publication Activity Database

    Kroupa, Aleš; Dinsdale, A.; Watson, A.; Vřešťál, J.; Zemanová, Adéla; Brož, P.

    2012-01-01

    Roč. 48, č. 3 (2012), s. 339-346 ISSN 1450-5339 R&D Projects: GA MŠk LD11024 Institutional support: RVO:68081723 Keywords : CALPHAD method * lead-free solders * thermodynamic database Subject RIV: BJ - Thermodynamics Impact factor: 1.435, year: 2012

  14. Fundamentals of lead-free solder interconnect technology from microstructures to reliability

    CERN Document Server

    Lee, Tae-Kyu; Kim, Choong-Un; Ma, Hongtao

    2015-01-01

    This unique book provides an up-to-date overview of the fundamental concepts behind lead-free solder and interconnection technology. Readers will find a description of the rapidly increasing presence of electronic systems in all aspects of modern life as well as the increasing need for predictable reliability in electronic systems. The physical and mechanical properties of lead-free solders are examined in detail, and building on fundamental science, the mechanisms responsible for damage and failure evolution, which affect reliability of lead-free solder joints are identified based on microstructure evolution.  The continuing miniaturization of electronic systems will increase the demand on the performance of solder joints, which will require new alloy and processing strategies as well as interconnection design strategies. This book provides a foundation on which improved performance and new design approaches can be based.  In summary, this book:  Provides an up-to-date overview on lead-free soldering tech...

  15. Giant piezoelectricity in potassium-sodium niobate lead-free ceramics.

    Science.gov (United States)

    Wang, Xiaopeng; Wu, Jiagang; Xiao, Dingquan; Zhu, Jianguo; Cheng, Xiaojing; Zheng, Ting; Zhang, Binyu; Lou, Xiaojie; Wang, Xiangjian

    2014-02-19

    Environment protection and human health concern is the driving force to eliminate the lead from commercial piezoelectric materials. In 2004, Saito et al. [ Saito et al., Nature , 2004 , 432 , 84 . ] developed an alkali niobate-based perovskite solid solution with a peak piezoelectric constant d33 of 416 pC/N when prepared in the textured polycrystalline form, intriguing the enthusiasm of developing high-performance lead-free piezoceramics. Although much attention has been paid on the alkali niobate-based system in the past ten years, no significant breakthrough in its d33 has yet been attained. Here, we report an alkali niobate-based lead-free piezoceramic with the largest d33 of ∼490 pC/N ever reported so far using conventional solid-state method. In addition, this material system also exhibits excellent integrated performance with d33∼390-490 pC/N and TC∼217-304 °C by optimizing the compositions. This giant d33 of the alkali niobate-based lead-free piezoceramics is ascribed to not only the construction of a new rhombohedral-tetragonal phase boundary but also enhanced dielectric and ferroelectric properties. Our finding may pave the way for "lead-free at last".

  16. Reliability and microstructure of lead-free solder joints in industrial electronics after accelerated thermal aging

    NARCIS (Netherlands)

    Scaltro, F.; Biglari, M.H.; Kodentsov, A.; Yakovleva, O.; Brom, E.

    2009-01-01

    The reliability of lead-free (LF) solder joints in surface-mounted device components (SMD) has been investigated after thermo-cycle testing. Kirkendall voids have been observed at the interface component/solder together with the formation of fractures. The evolution, the morphology and the elemental

  17. Electrochemical migration of lead-free solder alloys in Na2SO4 environment

    DEFF Research Database (Denmark)

    Medgyes, Balint; Ádám, Sándor; Tar, Lajos

    2017-01-01

    The effect of sulphate ion concentration on electrochemical migration of lead-free solder alloys was investigated with the use of water drop tests, by applying an in-situ optical and electrical inspection system. According to the Mean-Time-To-Failure (MTTF) values it was found that in the case of...

  18. Flexible Piezoelectric Touch Sensor by Alignment of Lead-Free Alkaline Niobate Microcubes in PDMS

    NARCIS (Netherlands)

    Deutz, D.B.; Mascarenhas, N.T.; Schelen, J.B.J.; de Leeuw, D.M.; van der Zwaag, S.; Groen, W.A.

    2017-01-01

    A highly sensitive, lead-free, and flexible piezoelectric touch sensor is reported based on composite films of alkaline niobate K0.485Na0.485Li0.03NbO3 (KNLN) powders aligned in a polydimethylsiloxane (PDMS) matrix. KNLN powder is fabricated by

  19. Tuning the competition between ferromagnetism and antiferromagnetism in a half-doped manganite through magnetoelectric coupling

    Energy Technology Data Exchange (ETDEWEB)

    Yi, Di [University of California; Liu, Jian [University of California, Berkeley & LBNL; Okamoto, Satoshi [ORNL; Jagannatha, Suresha [Lawrence Berkeley National Laboratory (LBNL); Chen, Yi-Chun [National Cheng Kung University, Tainan, Taiwan; Yu, Pu [Tsinghua University; Chu, Ying-Hao [National Chiao Tung University, Hsinchu, Taiwan; Arenholz, Elke [Lawrence Berkeley National Laboratory (LBNL); Ramesh, Ramamoorthy [University of California, Berkeley

    2013-01-01

    We investigate the possibility of controlling the magnetic phase transition of the heterointerface between a half-doped manganite La0:5Ca0:5MnO3 and a multiferroic BiFeO3 (BFO) through magnetoelectric coupling. Using macroscopic magnetometry and element-selective x-ray magnetic circular dichroism at the Mn and Fe L edges, we discover that the ferroelectric polarization of BFO controls simultaneously the magnetization of BFO and La0.5Ca0.5MnO3 (LCMO). X-ray absorption spectra at the oxygen K edge and linear dichroism at the Mn L edge suggest that the interfacial coupling is mainly derived from the superexchange between Mn and Fe t2g spins. The combination of x-ray absorption spectroscopy and mean-field theory calculations reveals that the d-electron modulation of Mn cations changes the magnetic coupling in LCMO, which controls the enhanced canted moments of interfacial BFO via the interfacial coupling. Our results demonstrate that the competition between ferromagnetic and antiferromagnetic instability can be modulated by an electric field at the heterointerface, providing another pathway for the electrical field control of magnetism.

  20. Advances in Lead-Free Piezoelectric Materials for Sensors and Actuators

    Directory of Open Access Journals (Sweden)

    Jacob L. Jones

    2010-03-01

    Full Text Available Piezoelectrics have widespread use in today’s sensor and actuator technologies. However, most commercially available piezoelectric materials, e.g., Pb [ZrxTi1-x] O3 (PZT,are comprised of more than 60 weight percent lead (Pb. Dueto its harmful effects, there is a strong impetus to identify new lead-free replacement materials with comparable properties to those of PZT. This review highlights recent developments in several lead-free piezoelectric materials including BaTiO3, Na0.5Bi0.5TiO3, K0.5Bi0.5TiO3, Na0.5K0.5NbO3, and their solid solutions. The factors that contribute to strong piezoelectric behavior are described and a summary of the properties for the various systems is provided.

  1. Properties and Microstructures of Sn-Bi-X Lead-Free Solders

    Directory of Open Access Journals (Sweden)

    Fan Yang

    2016-01-01

    Full Text Available The Sn-Bi base lead-free solders are proposed as one of the most popular alloys due to the low melting temperature (eutectic point: 139°C and low cost. However, they are not widely used because of the lower wettability, fatigue resistance, and elongation compared to traditional Sn-Pb solders. So the alloying is considered as an effective way to improve the properties of Sn-Bi solders with the addition of elements (Al, Cu, Zn, Ga, Ag, In, Sb, and rare earth and nanoparticles. In this paper, the development of Sn-Bi lead-free solders bearing elements and nanoparticles was reviewed. The variation of wettability, melting characteristic, electromigration, mechanical properties, microstructures, intermetallic compounds reaction, and creep behaviors was analyzed systematically, which can provide a reference for investigation of Sn-Bi base solders.

  2. Finite element analysis of vibration energy harvesting using lead-free piezoelectric materials: A comparative study

    Directory of Open Access Journals (Sweden)

    Anuruddh Kumar

    2014-06-01

    Full Text Available In this article, the performance of various piezoelectric materials is simulated for the unimorph cantilever-type piezoelectric energy harvester. The finite element method (FEM is used to model the piezolaminated unimorph cantilever structure. The first-order shear deformation theory (FSDT and linear piezoelectric theory are implemented in finite element simulations. The genetic algorithm (GA optimization approach is carried out to optimize the structural parameters of mechanical energy-based energy harvester for maximum power density and power output. The numerical simulation demonstrates the performance of lead-free piezoelectric materials in unimorph cantilever-based energy harvester. The lead-free piezoelectric material K0.5Na0.5NbO3-LiSbO3-CaTiO3 (2 wt.% has demonstrated maximum mean power and maximum mean power density for piezoelectric energy harvester in the ambient frequency range of 90–110 Hz. Overall, the lead-free piezoelectric materials of K0.5Na0.5NbO3-LiSbO3 (KNN-LS family have shown better performance than the conventional lead-based piezoelectric material lead zirconate titanate (PZT in the context of piezoelectric energy harvesting devices.

  3. Fabrication and Characterization of Aligned Flexible Lead-Free Piezoelectric Nanofibers for Wearable Device Applications

    Directory of Open Access Journals (Sweden)

    Sang Hyun Ji

    2018-03-01

    Full Text Available Flexible lead-free piezoelectric nanofibers, based on BNT-ST (0.78Bi0.5Na0.5TiO3-0.22SrTiO3 ceramic and poly(vinylidene fluoride-trifluoroethylene (PVDF-TrFE copolymers, were fabricated by an electrospinning method and the effects of the degree of alignment in the nanofibers on the piezoelectric characteristics were investigated. The microstructure of the lead-free piezoelectric nanofibers was observed by field emission scanning electron microscope (FE-SEM and the orientation was analyzed by fast Fourier transform (FFT images. X-ray diffraction (XRD analysis confirmed that the phase was not changed by the electrospinning process and maintained a perovskite phase. Polarization-electric field (P-E loops and piezoresponse force microscopy (PFM were used to investigate the piezoelectric properties of the piezoelectric nanofibers, according to the degree of alignment—the well aligned piezoelectric nanofibers had higher piezoelectric properties. Furthermore, the output voltage of the aligned lead-free piezoelectric nanofibers was measured according to the vibration frequency and the bending motion and the aligned piezoelectric nanofibers with a collector rotation speed of 1500 rpm performed the best.

  4. Ultrasonic Transducer Fabricated Using Lead-Free BFO-BTO+Mn Piezoelectric 1-3 Composite

    Directory of Open Access Journals (Sweden)

    Yan Chen

    2015-05-01

    Full Text Available Mn-doped 0.7BiFeO3-0.3BaTiO3 (BFO-0.3BTO+Mn 1% mol lead-free piezoelectric ceramic were fabricated by traditional solid state reaction. The phase structure, microstructure, and ferroelectric properties were investigated. Additionally, lead-free 1–3 composites with 60% volume fraction of BFO-BTO+Mn ceramic were fabricated for ultrasonic transducer applications by a conventional dice-and-fill method. The BFO-BTO+Mn 1-3 composite has a higher electromechanical coupling coefficient (kt = 46.4% and lower acoustic impedance (Za ~ 18 MRayls compared with that of the ceramic. Based on this, lead-free piezoelectric ceramic composite, single element ultrasonic transducer with a center frequency of 2.54 MHz has been fabricated and characterized. The single element transducer exhibits good performance with a broad bandwidth of 53%. The insertion loss of the transducer was about 33.5 dB.

  5. First principles studies of multiferroic materials

    International Nuclear Information System (INIS)

    Picozzi, Silvia; Ederer, Claude

    2009-01-01

    Multiferroics, materials where spontaneous long-range magnetic and dipolar orders coexist, represent an attractive class of compounds, which combine rich and fascinating fundamental physics with a technologically appealing potential for applications in the general area of spintronics. Ab initio calculations have significantly contributed to recent progress in this area, by elucidating different mechanisms for multiferroicity and providing essential information on various compounds where these effects are manifestly at play. In particular, here we present examples of density-functional theory investigations for two main classes of materials: (a) multiferroics where ferroelectricity is driven by hybridization or purely structural effects, with BiFeO 3 as the prototype material, and (b) multiferroics where ferroelectricity is driven by correlation effects and is strongly linked to electronic degrees of freedom such as spin-, charge-, or orbital-ordering, with rare-earth manganites as prototypes. As for the first class of multiferroics, first principles calculations are shown to provide an accurate qualitative and quantitative description of the physics in BiFeO 3 , ranging from the prediction of large ferroelectric polarization and weak ferromagnetism, over the effect of epitaxial strain, to the identification of possible scenarios for coupling between ferroelectric and magnetic order. For the second class of multiferroics, ab initio calculations have shown that, in those cases where spin-ordering breaks inversion symmetry (e.g. in antiferromagnetic E-type HoMnO 3 ), the magnetically induced ferroelectric polarization can be as large as a few μC cm -2 . The examples presented point the way to several possible avenues for future research: on the technological side, first principles simulations can contribute to a rational materials design, aimed at identifying spintronic materials that exhibit ferromagnetism and ferroelectricity at or above room temperature. On the

  6. Study of multiferroic properties of Bi2Fe2WO9 ceramic for device application

    Directory of Open Access Journals (Sweden)

    Jyoshna Rout

    2016-09-01

    Full Text Available The Bi2Fe2WO9 ceramic was prepared using a standard solid-state reaction technique. Preliminary analysis of X-ray diffraction pattern revealed the formation of single-phase compound with orthorhombic crystal symmetry. The surface morphology of the material captured using scanning electron microscope (SEM exhibits formation of a densely packed microstructure. Comprehensive study of dielectric properties showed two anomalies at 200∘C and 450∘C: first one may be related to magnetic whereas second one may be related to ferroelectric phase transition. The field dependent magnetic study of the material shows the existence of small remnant magnetization (Mr of 0.052emμ/g at room temperature. The existence of magneto-electric (ME coupling coefficient along with above properties confirms multi-ferroic characteristics of the compound. Selected range temperature and frequency dependent electrical parameters (impedance, modulus, conductivity of the compound shows that electric properties are correlated to its microstructure. Detailed studies of frequency dependence of ac conductivity suggest that the material obeys Jonscher’s universal power law.

  7. Effects of magnetic correlation on the electric properties in multiferroic materials

    International Nuclear Information System (INIS)

    Zhai, Liang-Jun; Wang, Huai-Yu

    2015-01-01

    The effects of magnetic correlation on the electric properties in the multiferroic materials are studied, where the phase transition temperature of the magnetic subsystem T m is lower than that of the electric subsystem T e . A Heisenberg-type Hamiltonian and a transverse Ising model are employed to describe the ferromagnetic and ferroelectric subsystems, respectively. We find that the magnetic correlation can influence the electric properties above the T m , and magnetic transverse and longitudinal correlations have opposite functions. In the curves of temperature dependence of polarization, kinks appear at T m which is dominated by the sharp change of decreasing rate of the magnetic correlation. The kinks can be eliminated by an external magnetic field. The magnetic transverse and longitudinal correlations play contrary roles on the manipulation of polarization by the external magnetic field. - Highlights: • Both magnetic longitudinal and transverse correlations can influence the electric subsystem through magnetoelectric (ME) coupling at any temperature. • The magnetic longitudinal and transverse correlations have contrary effects in influencing the phase transition temperature of electric subsystem. • The electric phase transition temperature decrease with the ME coupling strength, while it was not so by mean-field theory. • An external field can make the influence smoother around the transition point, and can enhance the electric polarization. • Magnetic longitudinal and transverse correlations have contrary effects on the manipulation of polarization by magnetic field at temperature above the magnetic phase transition point

  8. Temperature Dependence of the Resonant Magnetoelectric Effect in Layered Heterostructures

    Directory of Open Access Journals (Sweden)

    Dmitrii A. Burdin

    2017-10-01

    Full Text Available The dependence of the resonant direct magnetoelectric effect on temperature is studied experimentally in planar composite structures. Samples of rectangular shapes with dimensions of 5 mm × 20 mm employed ferromagnetic layers of either an amorphous (metallic glass alloy or nickel with a thickness of 20–200 μm and piezoelectric layers of single crystalline langatate material or lead zirconate titanate piezoelectric ceramics with a thickness of 500 μm. The temperature of the samples was varied in a range between 120 and 390 K by blowing a gaseous nitrogen stream around them. It is shown that the effective characteristics of the magnetoelectric effect—such as the mechanical resonance frequency fr, the quality factor Q and the magnitude of the magnetoelectric coefficient αE at the resonance frequency—are contingent on temperature. The interrelations between the temperature changes of the characteristics of the magnetoelectric effect and the temperature variations of the following material parameters—Young’s modulus Y, the acoustic quality factor of individual layers, the dielectric constant ε, the piezoelectric modulus d of the piezoelectric layer as well as the piezomagnetic coefficients λ(n of the ferromagnetic layer—are established. The effect of temperature on the characteristics of the nonlinear magnetoelectric effect is observed for the first time. The results can be useful for designing magnetoelectric heterostructures with specified temperature characteristics, in particular, for the development of thermally stabilized magnetoelectric devices.

  9. Fabrication and properties of multiferroic nanocomposite films

    KAUST Repository

    Al-Nassar, Mohammed Y.; Ivanov, Yurii P.; Kosel, Jü rgen

    2015-01-01

    A new type of multiferroic polymer nanocomposite is presented, which exhibits excellent ferromagnetism and ferroelectricity simultaneously at room temperature. The multiferroic nanocomposite consists of a ferroelectric copolymer poly(vinylindene fluoride-trifluoroethylene) [P(VDF-TrFE)] and high aspect ratio ferromagnetic nickel (Ni) nanowires (NWs), which were grown inside anodic aluminum oxide membranes. The fabrication of nanocomposite films with Ni NWs embedded in P(VDF-TrFE) has been successfully carried out via a simple low-temperature spin-coating technique. Structural, ferromagnetic, and ferroelectric properties of the developed nanocomposite have been investigated. The remanent and saturation polarization as well as the coercive field of the ferroelectric phase are slightly affected by the incorporation of the NWs as well as the thickness of the films. While the former two decrease, the last increases by adding the NWs or increasing the thickness. The ferromagnetic properties of the nanocomposite films are found to be isotropic.

  10. Magnetic properties of nano-multiferroic materials

    Science.gov (United States)

    Ramam, Koduri; Diwakar, Bhagavathula S.; Varaprasad, Kokkarachedu; Swaminadham, Veluri; Reddy, Venu

    2017-11-01

    Latent magnetization in the multiferroics can be achieved via the structural distortion with respect to particle size and destroying the spiral spin structure, which plays the vital role in high-performance applications. In this investigation, multifunctional single phase Bi1-xLaxFe1-yCoyO3 nanomaterials were synthesized by co-precipitation technique. The chemical composition, phase genesis, morphology and thermal characteristics of the Bi1-xLaxFe1-yCoyO3 were studied by FTIR, XRD, SEM/EDS, TEM and TGA. XRD studies confirmed single phase distorted rhombohedral structure in Bi1-xLaxFe1-yCoyO3. The novelty in magnetic behavior of the Bi0.85La0.15Fe0.75Co0.25O3 multiferroic at room temperature showed both ferro and anti-ferromagnetic nature with higher order remanent magnetization among other nanocomposites in this study. This magnetic anomaly in Bi0.85La0.15Fe0.75Co0.25O3 is due to doping and size effects on the crystal structure that leads to spin-orbit interactions. Besides, Bi0.85La0.15Fe0.75Co0.25O3 integrated graphene oxide (GO) nanocomposite has shown the change in the magnetic hysteresis that indicates the effect of the semiconducting behavior of GO on the ordered magnetic moments in the multiferroic. This kind of magnetic anomaly could form advanced multiferroic devices.

  11. Magnetic susceptibility of multiferroics and chemical ordering

    Czech Academy of Sciences Publication Activity Database

    Maryško, Miroslav; Laguta, Valentyn; Raevski, I. P.; Kuzian, R. O.; Olekhnovich, N.M.; Pushkarev, A.V.; Radyush, Yu.V.; Raevskaya, S. I.; Titov, V.V.; Kubrin, S.P.

    2017-01-01

    Roč. 7, č. 5 (2017), s. 1-6, č. článku 056409. ISSN 2158-3226 R&D Projects: GA ČR GA13-11473S Institutional support: RVO:68378271 Keywords : multiferroic * spin glass * antiferromagnetic * ferroelectrics Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 1.568, year: 2016

  12. Interventional Angiography: Radiation Protection for the Examiner by using Lead-free Gloves.

    Science.gov (United States)

    Kamusella, Peter; Scheer, Fabian; Lüdtke, Christopher Wilhelm; Wiggermann, Philipp; Wissgott, Christian; Andresen, Reimer

    2017-07-01

    The radiation exposure to unprotected parts of the body requires special attention for the interventional radiologist. During angiographic procedures, hands are exposed to the direct X-ray beam and scattered radiation. The aim of the study was to evaluate the radiation exposure of examiners hand with the use of lead-free X-ray protective gloves in clinical practice in terms of shielding and sense of touch. The aim of the study was to evaluate the radiation exposure of examiners hand with the use of lead-free X-ray protective gloves in clinical practice in terms of shielding and sense of touch. Phantom measurements were conducted in the direct X-ray beam and the area of scattered radiation with and without shielding. Examiner measurements were determined in interventional angiographies in clinical routine of the lower limb in antegrade puncture technique through the femoral artery. In 24 out of 50 interventions, an elastic natural rubber latex glove with lead-free metal shielding against radiation was used. All measurements were performed with a direct dosimeter. After the intervention, an opinion of the examiner was requested for evaluation of the sense of touch. Phantom measurements; when using the protective glove in the direct X-ray beam, a significant increase of the Dose Area Product (DAP) (1084.2-1603.8 mGy*cm 2 ; 67.6%; pgloves were used, a significant increase of the DAP (6183.2-10462.9 mGy*cm 2 ; 59.1%; pgloves is characterized by a shielding effect against X-ray scattered radiation, without restricting the sense of touch. A significant reduction in radiation doses to the examiner can be accomplished with these gloves in the area of scattered radiation only. If the gloves were used in the direct X-ray beam, especially while the artery puncture was performed, a significant increase of the dose values was observed.

  13. Room temperature large self-biased magnetoelectric effect in non-lead based piezoelectric and magnetostrictive (0−3) particulate composite system

    International Nuclear Information System (INIS)

    Kumari, Mukesh; Prakash, Chandra; Chatterjee, Ratnamala

    2017-01-01

    In this work, room temperature magnetoelectric properties of (0−3) particulate composites of non lead based piezoelectric BNTKNNLTS [0.97(Bi 0.5 Na 0.5 TiO 3 )–0.03(K 0.47 Na 0.47 Li 0.06 Nb 0.74 Sb 0.06 Ta 0.2 O 3 ) and magnetostrictive CZFMO (Co 0.6 Zn 0.4 Fe 1.7 Mn 0.3 O 4 ) are presented. Composite samples of (1-x)(BNTKNNLTS)-x(CZFMO) , with x=0.1 and 0.5, are synthesized by solid state reaction route. X-ray diffraction confirms the single phase formation of parent phases and the presence of two phases in the composites. Similar sintering conditions of the two individual components lead to optimal ferroelectric and ferromagnetic properties in the composites. A large self-biased magnetoelectric (ME) coupling ~74 mV/cm.Oe for the sample with x=0.1 (measured in longitudinally magnetized-transversely polarized configuration) is observed at room temperature. - Highlights: • Modified BNT-CFO based (0−3) particulate composites have been synthesized. • Similar sintering conditions of two components lead to optimal multiferroicity. • A large self-biased ME coupling ~74 mV/cm. Oe is obtained at room temperature.

  14. Magnetoelectric coupling mechanisms in YMn2-xFexO5 and NdFe3(BO3)4 revealed by resonant X-ray diffraction

    International Nuclear Information System (INIS)

    Partzsch, Sven

    2014-01-01

    Multiferroic materials with a coupled ordering of electric and magnetic moments could be used to build energy-efficient, magnetic computer memory that is written with an electrical field. To understand the interaction between the magnetic and electric ordering in such materials, two examples, namely yttrium manganate YMn 2 O 5 and neodymium iron borate NdFe 3 (BO 3 ) 4 , are studied by means of resonant x-ray diffraction. The important role of a pure electronic contribution to the ferroelectric polarization is shown in YMn 2 O 5 . Furthermore, substitution of Fe can change the magnetic order of YMn 2 O 5 from antiferromagnetic into ferrimagnetic, allowing the storage of easily readable magnetic information. Therefore the change of the magnetic structure upon small Fe substitution is studied. Although most of the magnetic structure of the parent compound is kept, the Fe moments have larger components along the c-direction. In NdFe 3 (BO 3 ) 4 the microscopic origin of the magnetoelectric coupling is addressed as the consequence of the frustration of the Fe and Nd magnetic sublattices. The application of an electrical field shifts the balance from the helical to the collinear magnetic domains, revealing again the strong magnetoelectric coupling.

  15. Performance testing of lead free primers: blast waves, velocity variations, and environmental testing

    OpenAIRE

    Courtney, Elya; Courtney, Amy; Summer, Peter David; Courtney, Michael

    2014-01-01

    Results are presented for lead free primers based on diazodinitrophenol (DDNP)compared with tests on lead styphnate based primers. First, barrel friction measurements in 5.56 mm NATO are presented. Second, shot to shot variations in blast waves are presented as determined by detonating primers in a 7.62x51mm rifle chamber with a firing pin, but without any powder or bullet loaded and measuring the blast wave at the muzzle with a high speed pressure transducer. Third, variations in primer blas...

  16. Mechanical performances of lead-free solder joint connections with applications in the aerospace domain

    Directory of Open Access Journals (Sweden)

    Georgiana PADURARU

    2016-03-01

    Full Text Available The paper presents some theoretical and experimental aspects regarding the tribological performances of lead-free solder joint connections, with application in the aerospace domain. In order to highlight the mechanical and tribological properties of solder joint in correlation with different pad finishes, there were made some mechanical determinations using a dedicated Share Test System. The theoretical model highlights the link between the experimental results and the influence of gravitational acceleration on the mechanical and functional integrity of the electronic assemblies that works in vibration environment. The paper novelty is provided by the interdisciplinary experiment that offers results that can be used in the mechanical, tribological, electronical and aerospace domains.

  17. Processing and characterization of lead-free ceramics on the base of sodium-potassium niobate

    Science.gov (United States)

    Politova, E. D.; Golubko, N. V.; Kaleva, G. M.; Mosunov, A. V.; Sadovskaya, N. V.; Stefanovich, S. Yu.; Kiselev, D. A.; Kislyuk, A. M.; Panda, P. K.

    Lead-free sodium-potassium niobate-based piezoelectric materials are most intensively studied in order to replace the widely used Pb-based ones. In this work, the effects of modification of compositions by donor and acceptor dopants in the A- and B-sites of perovskite lattice on structure, dielectric, ferroelectric, and piezoelectric properties of ceramics from Morphotropic Phase Boundary in the (1-x)(K0.5Na0.5)NbO3-xBaTiO3 system and in compositions with x=0.05 and 0.06 additionally doped by Ni3+ cations have been studied.

  18. Texturation of lead-free BaTiO3-based piezoelectric ceramics

    OpenAIRE

    Ngueteu-Kamlo , A; Levassort , F; Pham Thi , M; Marchet , Pascal

    2014-01-01

    International audience; Nowadays, piezoelectric ceramics are integrated in a wide range of devices, in particular in ultrasonic applications (underwater sonar systems, medical imaging, non-destructive testing…). Most of them use Pb(Zr,Ti)O3 (PZT). However, due to health care and environmental problems, lead content must be reduced in such applications [1]. Recent reviews demonstrated that few lead-free materials families can be considered: the alkaline-niobates (K0.5Na0.5NbO3), the alkaline-b...

  19. Processing and characterization of lead-free ceramics on the base of sodium–potassium niobate

    Directory of Open Access Journals (Sweden)

    E. D. Politova

    2018-02-01

    Full Text Available Lead-free sodium–potassium niobate-based piezoelectric materials are most intensively studied in order to replace the widely used Pb-based ones. In this work, the effects of modification of compositions by donor and acceptor dopants in the A- and B-sites of perovskite lattice on structure, dielectric, ferroelectric, and piezoelectric properties of ceramics from Morphotropic Phase Boundary in the (1−x(K0.5Na0.5NbO3–xBaTiO3 system and in compositions with x=0.05 and 0.06 additionally doped by Ni3+ cations have been studied.

  20. Transition metal modified bulk BiFeO{sub 3} with improved magnetization and linear magneto-electric coupling

    Energy Technology Data Exchange (ETDEWEB)

    Puli, Venkata Sreenivas, E-mail: pvsri123@gmail.com [Department of Physics and Institute for Functional Nanomaterials, University of Puerto Rico, San Juan, PR 00936 (Puerto Rico); Kumar, A.; Panwar, N.; Panwar, I.C.; Katiyar, R.S. [Department of Physics and Institute for Functional Nanomaterials, University of Puerto Rico, San Juan, PR 00936 (Puerto Rico)

    2011-08-11

    Highlights: > Present composition (Bi{sub 0.9}Sm{sub 0.10}Fe{sub 0.95}Co{sub 0.05}O{sub 3} (BSFCO) have shown very high magnetization compared to parent BFO. > The magnetic hysteresis loops are well saturated with high saturation magnetization 2.89 emu/gm (unpoled and unleached) and 2.18 emu/gm (poled and unleached) respectively. > Converse ME coupling were found 0.8e-10 s m{sup -1} (H||E) and 0.6-0.8 x 10{sup -10} s m{sup -1} (H-perpendicular E) which are better than the single phase multiferroic obeying linear ME coupling. - Abstract: At present BiFeO{sub 3} (BFO) is the most attractive and sole example, which possesses low magnetization value, high leakage current and low polarization in ceramic form. Single-phase room temperature multiferroics are rare in nature. This paper deals with the improved magnetic and observed linear magneto-electric coupling in Co and Sm co-doped BiFeO{sub 3} ceramics synthesized by sol-gel process at low temperature {approx}600 deg. C. As synthesized Bi{sub 0.9}Sm{sub 0.10}Fe{sub 0.95}Co{sub 0.05}O{sub 3} (BSFCO) showed high impurities phases (20%) over wide range of calcination temperatures. Impurity phases reduced drastically from 20% to 5% after leaching with nitric acid. However the electrical and the magnetic properties were almost the same for both phases. Well-defined magnetic hysteresis with high magnetic moment was found at room temperature. Ferroelectric polarization studies demonstrated similar values and shape as reported in literature for the pure bulk BFO. Linear magneto-electric (ME) coupling and weak ME coefficient ({alpha}) {approx} 0.6 e-10 s m{sup -1} were observed in the co-doped BFO. The origin of the strong ferromagnetic property in our samples may be due to the presence of rare earth and transition metal ions at the lattice sites of BFO or due to impurity phase, since we have not seen any change in magnetization with reduction of impurity phase the later effect is more unlikely.

  1. Composition-driven enhanced magnetic properties and magnetoelectric coupling in Gd substituted BiFeO{sub 3} nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Vijayasundaram, S.V., E-mail: vijayasundaramsv@gmail.com [Department of Physics, Presidency College, Chennai 600005 (India); Suresh, G. [Department of Physics, Park College of Engineering and Technology, Coimbatore 641659 (India); Department of Urology, Singapore General Hospital, Singapore 169856 (Singapore); Mondal, R.A. [Department of Physics, Hindustan University, Chennai 603103 (India); Kanagadurai, R. [Department of Physics, Presidency College, Chennai 600005 (India)

    2016-11-15

    Bi{sub 1-x}Gd{sub x}FeO{sub 3} (x=0, 0.05 and 0.1) samples were synthesized by modified sol–gel process. X-ray diffraction studies confirmed that the crystal structures of Gd substituted samples remain stable for x<0.1, while compositional-driven structural phase transition from rhombohedral to orthorhombic was observed in the case of x=0.1. The average particle sizes of pure and Gd substituted BiFeO{sub 3} nanoparticles were found to be in the range 62–46 nm. The size of the oblate spherical particles decreased with increasing Gd concentration. XPS studies revealed the trivalent oxidation states of Bi and Fe ions along with sample purity. Pure BiFeO{sub 3} exhibited linear M–H loop indicating its antiferromagnetic characteristics, whereas obvious non-linear M–H loops were observed in Gd substituted samples. In contrast to the observed room temperature magnetization (0.36 emu/g) under 40 kOe for BiFeO{sub 3}, the sample with 10% Gd exhibited appreciable enhancement of magnetization (1.88 emu/g). A leaky type P–E hysteresis loop was observed for the pure one, whereas concave-like ferroelectric loops were obtained for Gd substituted samples. The possible origins of enhanced multiferroic properties have been explained on the basis of substituent, its concentration, phase purity, particle size, structural distortion and the modified magnetic structure. The measurement of magnetoelectric studies at room temperature revealed the coupling between magnetic and ferroelectric ordering, which is desirable for multifunctional device applications of multiferroics. - Highlights: • The substitution of Gd in BiFeO{sub 3} (BFO) nanoparticles led to structural distortion. • Average sizes of the substituted samples are less than the spin period of BFO. • Gd-substitution altered the original magnetic structure of BFO (AFM – FM). • M{sub r} of a substituted sample is an order of magnitude higher than that of BFO. • All the samples show magnetoelectric coupling

  2. Transition metal modified bulk BiFeO3 with improved magnetization and linear magneto-electric coupling

    International Nuclear Information System (INIS)

    Puli, Venkata Sreenivas; Kumar, A.; Panwar, N.; Panwar, I.C.; Katiyar, R.S.

    2011-01-01

    Highlights: → Present composition (Bi 0.9 Sm 0.10 Fe 0.95 Co 0.05 O 3 (BSFCO) have shown very high magnetization compared to parent BFO. → The magnetic hysteresis loops are well saturated with high saturation magnetization 2.89 emu/gm (unpoled and unleached) and 2.18 emu/gm (poled and unleached) respectively. → Converse ME coupling were found 0.8e-10 s m -1 (H||E) and 0.6-0.8 x 10 -10 s m -1 (H-perpendicular E) which are better than the single phase multiferroic obeying linear ME coupling. - Abstract: At present BiFeO 3 (BFO) is the most attractive and sole example, which possesses low magnetization value, high leakage current and low polarization in ceramic form. Single-phase room temperature multiferroics are rare in nature. This paper deals with the improved magnetic and observed linear magneto-electric coupling in Co and Sm co-doped BiFeO 3 ceramics synthesized by sol-gel process at low temperature ∼600 deg. C. As synthesized Bi 0.9 Sm 0.10 Fe 0.95 Co 0.05 O 3 (BSFCO) showed high impurities phases (20%) over wide range of calcination temperatures. Impurity phases reduced drastically from 20% to 5% after leaching with nitric acid. However the electrical and the magnetic properties were almost the same for both phases. Well-defined magnetic hysteresis with high magnetic moment was found at room temperature. Ferroelectric polarization studies demonstrated similar values and shape as reported in literature for the pure bulk BFO. Linear magneto-electric (ME) coupling and weak ME coefficient (α) ∼ 0.6 e-10 s m -1 were observed in the co-doped BFO. The origin of the strong ferromagnetic property in our samples may be due to the presence of rare earth and transition metal ions at the lattice sites of BFO or due to impurity phase, since we have not seen any change in magnetization with reduction of impurity phase the later effect is more unlikely.

  3. Evaluation of covalency of ions in lead-free perovskite-type dielectric oxides

    Directory of Open Access Journals (Sweden)

    Naohisa Takesue

    2017-10-01

    Full Text Available Electronic states of ions in lead-free perovskite-type dielectric oxides have been investigated with a first-principle cluster calculation. For this calculation a double-perovskite cluster model based upon the simple cubic ABO3 was used; A and B are both the cations, and O is the oxygen anion. Systematic variations of ionic species for A and B, and lengths of the model cube edge were given to the model. Results of charge transfers of the ions show that their magnitudes depend on the edge length; the lager length leads to the higher transfer magnitude. This tendency implies spatial tolerance of the ions to the clusters, and are expected to correlate with electric polarizability and dipole reversibility of this kind of oxides. The density of states and the overlap population indicate that the higher cation valence causes the higher covalency of the anions. Considering all results together provides us an idea to obtain lead-free high-performance ferroelectrics, as high as the lead-based solid solutions.

  4. Silver Niobate Lead-Free Antiferroelectric Ceramics: Enhancing Energy Storage Density by B-Site Doping.

    Science.gov (United States)

    Zhao, Lei; Gao, Jing; Liu, Qing; Zhang, Shujun; Li, Jing-Feng

    2018-01-10

    Lead-free dielectric ceramics with high recoverable energy density are highly desired to sustainably meet the future energy demand. AgNbO 3 -based lead-free antiferroelectric ceramics with double ferroelectric hysteresis loops have been proved to be potential candidates for energy storage applications. Enhanced energy storage performance with recoverable energy density of 3.3 J/cm 3 and high thermal stability with minimal energy density variation (<10%) over a temperature range of 20-120 °C have been achieved in W-modified AgNbO 3 ceramics. It is revealed that the W 6+ cations substitute the B-site Nb 5+ and reduce the polarizability of B-site cations, leading to the enhanced antiferroelectricity, which is confirmed by the polarization hysteresis and dielectric tunability. It is believed that the polarizability of B-site cations plays a dominant role in stabilizing the antiferroelectricity in AgNbO 3 system, in addition to the tolerance factor, which opens up a new design approach to achieve stable antiferroelectric materials.

  5. Effect of gamma radiation on micromechanical hardness of lead-free solder joint

    Energy Technology Data Exchange (ETDEWEB)

    Paulus, Wilfred [Universiti Kebangsaan Malaysia, Bangi, 43600 Kajang, Selangor (Malaysia); Malaysian Nuclear Agency, Bangi, 43000 Kajang, Selangor (Malaysia); Rahman, Irman Abdul; Jalar, Azman; Kamil, Insan; Bakar, Maria Abu [Universiti Kebangsaan Malaysia, Bangi, 43600 Kajang, Selangor (Malaysia); Yusoff, Wan Yusmawati Wan [Universiti Pertahanan Nasional Malaysia, Kem Sg. Besi, 57000 Kuala Lumpur (Malaysia)

    2015-09-25

    Lead-free solders are important material in nano and microelectronic surface mounting technology for various applications in bio medicine, environmental monitoring, spacecraft and satellite instrumentation. Nevertheless solder joint in radiation environment needs higher reliability and resistance to any damage caused by ionizing radiations. In this study a lead-free 99.0Sn0.3Ag0.7Cu wt.% (SAC) solder joint was developed and subjected to various doses of gamma radiation to investigate the effects of the ionizing radiation to micromechanical hardness of the solder. Averaged hardness of the SAC joint was obtained from nanoindentation test. The results show a relationship between hardness values of indentations and the increment of radiation dose. Highest mean hardness, 0.2290 ± 0.0270 GPa was calculated on solder joint which was exposed to 5 Gray dose of gamma radiation. This value indicates possible radiation hardening effect on irradiated solder. The hardness gradually decreased to 0.1933 ± 0.0210 GPa and 0.1631 ± 0.0173 GPa when exposed to doses 50 and 500 gray respectively. These values are also lower than the hardness of non irradiated sample which was calculated as 0.2084 ± 0.0.3633 GPa indicating possible radiation damage and needs further related atomic dislocation study.

  6. High Quantum Yield Blue Emission from Lead-Free Inorganic Antimony Halide Perovskite Colloidal Quantum Dots.

    Science.gov (United States)

    Zhang, Jian; Yang, Ying; Deng, Hui; Farooq, Umar; Yang, Xiaokun; Khan, Jahangeer; Tang, Jiang; Song, Haisheng

    2017-09-26

    Colloidal quantum dots (QDs) of lead halide perovskite have recently received great attention owing to their remarkable performances in optoelectronic applications. However, their wide applications are hindered from toxic lead element, which is not environment- and consumer-friendly. Herein, we utilized heterovalent substitution of divalent lead (Pb 2+ ) with trivalent antimony (Sb 3+ ) to synthesize stable and brightly luminescent Cs 3 Sb 2 Br 9 QDs. The lead-free, full-inorganic QDs were fabricated by a modified ligand-assisted reprecipitation strategy. A photoluminescence quantum yield (PLQY) was determined to be 46% at 410 nm, which was superior to that of other reported halide perovskite QDs. The PL enhancement mechanism was unraveled by surface composition derived quantum-well band structure and their large exciton binding energy. The Br-rich surface and the observed 530 meV exciton binding energy were proposed to guarantee the efficient radiative recombination. In addition, we can also tune the inorganic perovskite QD (Cs 3 Sb 2 X 9 ) emission wavelength from 370 to 560 nm via anion exchange reactions. The developed full-inorganic lead-free Sb-perovskite QDs with high PLQY and stable emission promise great potential for efficient emission candidates.

  7. Characterization of the microstructure of tin-silver lead free solder

    Energy Technology Data Exchange (ETDEWEB)

    Hurtony, Tamás, E-mail: hurtony@ett.bme.hu [Department of Electronics Technology, Budapest University of Technology and Economics, Egry József utca 18, Budapest, H-1111 (Hungary); Szakál, Alex; Almásy, László [Neutron Spectroscopy Department, Wigner Research Centre for Physics, Budapest (Hungary); Len, Adél [Neutron Spectroscopy Department, Wigner Research Centre for Physics, Budapest (Hungary); Faculty of Engineering and Information Technology, University of Pécs (Hungary); Kugler, Sándor [Department of Theoretical Physics, Budapest University of Technology and Economics (Hungary); Bonyár, Attila; Gordon, Péter [Department of Electronics Technology, Budapest University of Technology and Economics, Egry József utca 18, Budapest, H-1111 (Hungary)

    2016-07-05

    Reliability and lifetime are the two most relevant design considerations in the production of safety critical assemblies. For example in a modern automobile dozens of electronic assemblies are integrated in which thousands of solder joints are mounting the electronic components to the printed circuit boards. There exists no standardised and universal observation method for characterising the fine microstructure of such solder joints. Previously we have developed a new method for the quantitative characterization of lead-free solder alloys and in present study the validity of the proposed method is demonstrated. Microstructure of Sn-3.5Ag lead free solder alloy was investigated by electrochemical impedance spectroscopy. Solder samples were solidified with different cooling rates in order to induce differences in the microstructure. Microstructure of the ingots was revealed by selective electrochemical etching. Electrochemical impedance spectra (EIS) were measured before and after the selective etching process. The complex impedance spectra contain information about microstructure of the solder alloys. Comparison and modelling of two EIS spectra allowed obtaining a characteristic parameter of surface structure of the etched specimens. The EIS measurements were complemented with small angle neutron scattering measurements and scanning electron microscopy, in order to correlate the EIS parameter with the magnitude of the interface of the β-Sn and Ag{sub 3}Sn phases.

  8. Lead-free piezoelectrics based on potassium-sodium niobate with giant d(33).

    Science.gov (United States)

    Zhang, Binyu; Wu, Jiagang; Cheng, Xiaojing; Wang, Xiaopeng; Xiao, Dingquan; Zhu, Jianguo; Wang, Xiangjian; Lou, Xiaojie

    2013-08-28

    High-performance lead-free piezoelectrics (d33 > 400 pC/N) based on 0.96(K0.5Na0.5)0.95Li0.05Nb1-xSbxO3-0.04BaZrO3 with the rhombohedral-tetragonal (R-T) phase boundary have been designed and prepared. The R-T phase boundary lies the composition range of 0.04 ≤ x ≤ 0.07, and the dielectric and piezoelectric properties of the ceramics with the compositions near the phase boundary are significantly enhanced. In addition, the ceramic with x = 0.07 has a giant d33 of ~425 pC/N, which is comparable to that (~416 pC/N) of textured KNN-based ceramics (Saito, Y.; Takao, H.; Tani, T.; Nonoyama, T.; Takatori, K.; Homma, T.; Nagaya, T.; Nakamura, M. Nature 2004, 432, 84). The underlying physical mechanisms for enhanced piezoelectric properties are addressed. We believe that the material system is the most promising lead-free piezoelectric candidates for the practical applications.

  9. Low temperature synthesis & characterization of lead-free BCZT ceramics using molten salt method

    Science.gov (United States)

    Jai Shree, K.; Chandrakala, E.; Das, Dibakar

    2018-04-01

    Piezoelectric properties are greatly influenced by the synthesis route, microstructure, stoichiometry of the chemical composition, purity of the starting materials. In this study, molten salt method was used to prepare lead-free BCZT ceramics. Molten salt method is one of the simplestmethods to prepare chemically-purified, single phase powders in high yield often at lower temperatures and shorten reaction time. Calcination of the molten salt synthesized powders resulted in asingle-phase perovskite structure at 1000 °C which is ˜ 350 °C less than the conventional solid-sate reaction method. With increasing calcination temperature the average template size was increased (˜ 0.5-2 µm). Formation of well dispersive templates improves the sinterability at lower temperatures. Lead-free BCZT ceramics sintered at 1500 °C for 2 h resulted in homogenous and highly dense microstructure with ˜92% of the theoretical density and a grain size of ˜ 35 µm. This highly dense microstructure could enhance the piezoelectric properties of the system.

  10. Requirements for the transfer of lead-free piezoceramics into application

    Directory of Open Access Journals (Sweden)

    Jurij Koruza

    2018-03-01

    Full Text Available The recent review for the Restriction of Hazardous Substances Directive (RoHS by the expert committee, appointed by the European Union, stated that the replacement of PZT “… may be scientifically and technologically practical to a certain degree …”, although replacement “… is scientifically and technically still impractical in the majority of applications.” Thus, two decades of sustained research and development may be approaching fruition, at first limited to a minority of applications. Therefore, it is of paramount importance to assess the viability of lead-free piezoceramics over a broad range of application-relevant properties. These are identified and discussed in turn: 1. Cost, 2. Reproducibility, 3. Mechanical and Thermal Properties, 4. Electrical Conductivity, and 5. Lifetime. It is suggested that the worldwide efforts into the development of lead-free piezoceramics now require a broader perspective to bring the work to the next stage of development by supporting implementation into real devices. Guidelines about pertinent research requirements into a wide range of secondary properties, measurement techniques, and salient literature are provided.

  11. Review and Perspectives of Aurivillius Structures as a Lead-Free Piezoelectric System

    Directory of Open Access Journals (Sweden)

    Alberto Moure

    2018-01-01

    Full Text Available According to the EU-Directives 2002/95/EC, 2002/96/EC, lead-based piezoceramics must be substituted in the future with more environmentally friendly alternatives, only when a reliable alternative is found. This is why an increasing interest has grown in the research community to find lead free piezoelectric materials that fulfil the requirements for this substitution. Different families of compounds have been shown to be possible candidates for this use, such as bismuth and niobates based perovskites, pyrochlores, etc. However, a material with piezoelectric coefficients similar to those of PZT (lead zirconate titanate, Pb[ZrxTi1-x]O3 has not been yet found. Besides, each of these families has its specific characteristics in terms of remnant polarization, coercive field or application temperature. Thus, the choice of each material should be made according to the specific needs of the application. In this sense, Aurivillius-type structure materials (also known as Bismuth Layered Structure Ferroelectrics, BLSF can take advantage of their specific properties for uses as Lead Free Piezoelectric systems. Some of them have a high Curie temperature, which make them good candidates to be used as high temperature piezoelectrics; high coercive fields, which facilitates their use as actuators; or a high switching fatigue resistance, which can be useful for future applications as Ferroelectric Random Access Memories (FERAM.

  12. Resonance line shape, strain and electric potential distributions of composite magnetoelectric sensors

    Directory of Open Access Journals (Sweden)

    Martina Gerken

    2013-06-01

    Full Text Available Multiferroic composite magnetoelectric (ME sensors are based on the elastic coupling of a magnetostrictive phase and a piezoelectric phase. A deformation of the magnetostrictive phase causes strain in the piezoelectric phase and thus an induced voltage. Such sensors may be applied both for static as well as for dynamic magnetic field measurements. Particularly high sensitivities are achieved for operation at a mechanical resonance. Here, the resonance line shape of layered (2-2 composite cantilever ME sensors at the first bending-mode resonance is investigated theoretically. Finite element method (FEM simulations using a linear material model reveal an asymmetric resonance profile and a zero-response frequency for the ME coefficient. Frequency-dependent strain and electric potential distributions inside the magnetoelectric composite are studied for the case of a magnetostrictive-piezoelectric bilayer. It is demonstrated that a positive or a negative voltage may be induced across the piezoelectric layer depending on the position of the neutral plane. The frequency-dependent induced electric potential is investigated for structured cantilevers that exhibit magnetostriction only at specific positions. For static operation an induced voltage is obtained locally at positions with magnetostriction. In addition to this direct effect a resonance-assisted effect is observed for dynamic operation. Magnetostriction in a limited area of the cantilever causes a global vibration of the cantilever. Thus, deformation of the piezoelectric layer and an induced electric potential also occur in areas of the cantilever without magnetostriction. The direct and the resonance-assisted pathway may induce voltages of equal or of opposite sign. The net induced voltage results from the superposition of the two effects. As the resonance-assisted induced voltage changes sign upon passing the resonance frequency, while the direct component is constant, an asymmetric line

  13. Deposition of magnetoelectric hexaferrite thin films on substrates of silicon

    Energy Technology Data Exchange (ETDEWEB)

    Zare, Saba; Izadkhah, Hessam; Vittoria, Carmine

    2016-12-15

    Magnetoelectric M-type hexaferrite thin films (SrCo{sub 2}Ti{sub 2}Fe{sub 8}O{sub 19}) were deposited using Pulsed Laser Deposition (PLD) technique on Silicon substrate. A conductive oxide layer of Indium-Tin Oxide (ITO) was deposited as a buffer layer with the dual purposes of 1) to reduce lattice mismatch between the film and silicon and 2) to lower applied voltages to observe magnetoelectric effects at room temperature on Silicon based devices. The film exhibited magnetoelectric effects as confirmed by vibrating sample magnetometer (VSM) techniques in voltages as low as 0.5 V. Without the oxide conductive layer the required voltages to observe magnetoelectric effects was typically about 1000 times larger. The magnetoelectric thin films were characterized by X-ray diffractometer, scanning electron microscope, energy-dispersive spectroscopy, vibrating sample magnetometer, and ferromagnetic resonance techniques. We measured saturation magnetization of 650 G, and coercive field of about 150 Oe for these thin films. The change in remanence magnetization was measured in the presence of DC voltages and the changes in remanence were in the order of 15% with the application of only 0.5 V (DC voltage). We deduced a magnetoelectric coupling, α, of 1.36×10{sup −9} s m{sup −1} in SrCo{sub 2}Ti{sub 2}Fe{sub 8}O{sub 19} thin films.

  14. Development, Characterization and Piezoelectric Fatigue Behavior of Lead-Free Perovskite Piezoelectric Ceramics

    Science.gov (United States)

    Patterson, Eric Andrew

    Much recent research has focused on the development lead-free perovskite piezoelectrics as environmentally compatible alternatives to lead zirconate titanate (PZT). Two main categories of lead free perovskite piezoelectric ceramic systems were investigated as potential replacements to lead zirconate titanate (PZT) for actuator devices. First, solid solutions based on Li, Ta, and Sb modified (K0.5Na0.5)NbO3 (KNN) lead-free perovskite systems were created using standard solid state methods. Secondly, Bi-based materials a variety of compositions were explored for (1-x)(Bi 0.5Na0.5)TiO3-xBi(Zn0.5Ti0.5)O 3 (BNT-BZT) and Bi(Zn0.5Ti0.5)O3-(Bi 0.5K0.5)TiO3-(Bi0.5Na0.5)TiO 3 (BZT-BKT-BNT). It was shown that when BNT-BKT is combined with increasing concentrations of Bi(Zn1/2i1/2)O3 (BZT), a transition from normal ferroelectric behavior to a material with large electric field induced strains was observed. The higher BZT containing compositions are characterized by large hysteretic strains(> 0.3%) with no negative strains that might indicate domain switching. This work summarizes and analyzes the fatigue behavior of the new generation of Pb-free piezoelectric materials. In piezoelectric materials, fatigue is observed as a degradation in the electromechanical properties under the application of a bipolar or unipolar cyclic electrical load. In Pb-based materials such as lead zirconate titanate (PZT), fatigue has been studied in great depth for both bulk and thin film applications. In PZT, fatigue can result from microcracking or electrode effects (especially in thin films). Ultimately, however, it is electronic and ionic point defects that are the most influential mechanism. Therefore, this work also analyzes the fatigue characteristics of bulk polycrystalline ceramics of the modified-KNN and BNT-BKT-BZT compositions developed. The defect chemistry that underpins the fatigue behavior will be examined and the results will be compared to the existing body of work on PZT. It will

  15. Moving towards the magnetoelectric graphene transistor

    International Nuclear Information System (INIS)

    Cao, Shi; Xiao, Zhiyong; Kwan, Chun-Pui; Zhang, Kai; Bird, Jonathan P.

    2017-01-01

    Here, the interfacial charge transfer between mechanically exfoliated few-layer graphene and Cr 2 O 3 (0001) surfaces has been investigated. Electrostatic force microscopy and Kelvin probe force microscopy studies point to hole doping of few-layer graphene, with up to a 150 meV shift in the Fermi level, an aspect that is confirmed by Raman spectroscopy. Density functional theory calculations furthermore confirm the p-type nature of the graphene/chromia interface and suggest that the chromia is able to induce a significant carrier spin polarization in the graphene layer. A large magnetoelectrically controlled magneto-resistance can therefore be anticipated in transistor structures based on this system, a finding important for developing graphene-based spintronic applications.

  16. Mesoscale Interfacial Dynamics in Magnetoelectric Nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Shashank, Priya [Virginia Polytechnic Inst. and State Univ. (Virginia Tech), Blacksburg, VA (United States)

    2009-12-14

    Biphasic composites are the key towards achieving enhanced magnetoelectric response. In order understand the control behavior of the composites and resultant symmetry of the multifunctional product tensors, we need to synthesized model material systems with the following features (i) interface formation through either deposition control or natural decomposition; (ii) a very high interphase-interfacial area, to maximize the ME coupling; and (iii) an equilibrium phase distribution and morphology, resulting in preferred crystallographic orientation relations between phases across the interphase-interfacial boundaries. This thought process guided the experimental evolution in this program. We initiated the research with the co-fired composites approach and then moved on to the thin film laminates deposited through the rf-magnetron sputtering and pulsed laser deposition process

  17. Tuning the electrocaloric enhancement near the morphotropic phase boundary in lead-free ceramics

    Science.gov (United States)

    Le Goupil, Florian; McKinnon, Ruth; Koval, Vladimir; Viola, Giuseppe; Dunn, Steve; Berenov, Andrey; Yan, Haixue; Alford, Neil Mcn.

    2016-06-01

    The need for more energy-efficient and environmentally-friendly alternatives in the refrigeration industry to meet global emission targets has driven efforts towards materials with a potential for solid state cooling. Adiabatic depolarisation cooling, based on the electrocaloric effect (ECE), is a significant contender for efficient new solid state refrigeration techniques. Some of the highest ECE performances reported are found in compounds close to the morphotropic phase boundary (MPB). This relationship between performance and the MPB makes the ability to tune the position of the MPB an important challenge in electrocaloric research. Here, we report direct ECE measurements performed on MPB tuned NBT-06BT bulk ceramics with a combination of A-site substitutions. We successfully shift the MPB of these lead-free ceramics closer to room temperature, as required for solid state refrigeration, without loss of the criticality of the system and the associated ECE enhancement.

  18. Effect of surface oxide on the melting behavior of lead-free solder nanowires and nanorods

    International Nuclear Information System (INIS)

    Gao Fan; Rajathurai, Karunaharan; Cui, Qingzhou; Zhou, Guangwen; NkengforAcha, Irene; Gu Zhiyong

    2012-01-01

    Lead-free nanosolders have shown promise in nanowire and nanoelectronics assembly. Among various important parameters, melting is the most fundamental property affecting the assembly process. Here we report that the melting behavior of tin and tin/silver nanowires and nanorods can be significantly affected by the surface oxide of nanosolders. By controlling the nanosolder reflow atmosphere using a flux, the surface oxide of the nanowires/nanorods can be effectively removed and complete nanosolder melting can be achieved. The complete melting of the nanosolders leads to the formation of nanoscale to microscale spherical solder balls, followed by Ostwald ripening phenomenon. The contact angle of the microscale solder balls formed on Si substrate was measured by direct electron microscopic imaging. These results provide new insights into micro- and nanoscale phase transition and liquid droplet coalescence from nanowires/nanorods to spheroids, and are relevant to nanoscale assembly and smaller ball grid array formation.

  19. Extrinsic Contribution and Instability Properties in Lead-Based and Lead-Free Piezoceramics

    Directory of Open Access Journals (Sweden)

    José Eduardo García

    2015-11-01

    Full Text Available Piezoceramic materials generally exhibit a notable instability of their functional properties when they work under real external conditions. This undesirable effect, known as nonlinear behavior, is mostly associated with the extrinsic contribution to material response. In this article, the role of the ferroelectric domain walls’ motion in the nonlinear response in the most workable lead-based and lead-free piezoceramics is reviewed. Initially, the extrinsic origin of the nonlinear response is discussed in terms of the temperature dependence of material response. The influence of the crystallographic phase and of the phase boundaries on the material response are then reviewed. Subsequently, the impact of the defects created by doping in order to control the extrinsic contribution is discussed as a way of tuning material properties. Finally, some aspects related to the grain-size effect on the nonlinear response of piezoceramics are surveyed.

  20. Interfacial Reaction of Sn-Ag-Cu Lead-Free Solder Alloy on Cu: A Review

    Directory of Open Access Journals (Sweden)

    Liu Mei Lee

    2013-01-01

    Full Text Available This paper reviews the function and importance of Sn-Ag-Cu solder alloys in electronics industry and the interfacial reaction of Sn-Ag-Cu/Cu solder joint at various solder forms and solder reflow conditions. The Sn-Ag-Cu solder alloys are examined in bulk and in thin film. It then examines the effect of soldering conditions to the formation of intermetallic compounds such as Cu substrate selection, structural phases, morphology evolution, the growth kinetics, temperature and time is also discussed. Sn-Ag-Cu lead-free solder alloys are the most promising candidate for the replacement of Sn-Pb solders in modern microelectronic technology. Sn-Ag-Cu solders could possibly be considered and adapted in miniaturization technologies. Therefore, this paper should be of great interest to a large selection of electronics interconnect materials, reliability, processes, and assembly community.

  1. Reliability of lead-free solder joints with different PCB surface finishes under thermal cycling

    Energy Technology Data Exchange (ETDEWEB)

    Xia Yanghua [State Key Laboratory of Functional Materials for Informatics, Shanghai Institute of Microsystem and Information Technology, Chinese Academy of Sciences, Shanghai 200050 (China)], E-mail: xia_yanghua@hotmail.com; Xie Xiaoming [State Key Laboratory of Functional Materials for Informatics, Shanghai Institute of Microsystem and Information Technology, Chinese Academy of Sciences, Shanghai 200050 (China)

    2008-04-24

    The reliability of lead-free electronic assemblies under thermal cycling was investigated. Thin small outline package (TSOP) devices with FeNi leads were reflow soldered on FR4 PCB (printed circuit board) with Sn3.0Ag0.5Cu (wt%) solder. The effects of different PCB finishes (organic solderability preservative (OSP) and electroless nickel immersion gold (ENIG)) were studied. The results show that OSP finish reveals better performance than its ENIG counterparts. The crack originates at the fringe of heel fillet in both cases. The propagation of crack in the ENIG case is along the device/solder interface, while in the case of OSP, the crack extends parallel to the solder/PCB interface. When the OSP finishes are employed, many Cu6Sn5 precipitates form inside the bulk solder and have a strengthening effect on the solder joint, resulting in better reliability performance as compared to those with ENIG finishes.

  2. Salient features, response and operation of Lead-Free Gulmarg Neutron Monitor

    International Nuclear Information System (INIS)

    Mufti, S.; Chatterjee, S.; Ishtiaq, P.M.; Darzi, M.A.; Mir, T.A.; Shah, G.N.

    2016-01-01

    Lead-Free Gulmarg Neutron Monitor (LFGNM) provides continuous ground level intensity measurements of atmospheric secondary neutrons produced in interactions of primary cosmic rays with the Earth's constituent atmosphere. We report the LFGNM detector salient features and simulation of its energy response for 10"−"1"1 MeV to 10"4 MeV energy incident neutrons using the FLUKA Monte Carlo package. An empirical calibration of the LFGNM detector carried out with a Pu–Be neutron source for maximising its few MeV neutron counting sensitivity is also presented. As an illustration of its functionality a single representative transient solar modulation event recorded by LFGNM depicting Forbush decrease in integrated neutron data for which the geospace consequences are well known is also presented. Performance of LFGNM under actual observation conditions for effectively responding to transient solar modulation is seen to compare well with other world-wide conventional neutron monitors.

  3. Effect of rare earth substitution on properties of barium strontium titanate ceramic and its multiferroic composite with nickel cobalt ferrite

    International Nuclear Information System (INIS)

    Pahuja, Poonam; Kotnala, R.K.; Tandon, R.P.

    2014-01-01

    Highlights: • Rare earth ions Dy 3+ , Gd 3+ and Sm 3+ have been substituted in Ba 0.95 Sr 0.05 TiO 3 (BST). • Ni 0.8 Co 0.2 Fe 2 O 4 has been used as ferrimagnetic phase to obtain composites. • Substitution of these ions increases dielectric constant of BST and composites. • Magnetoelectric coefficient of composites increases on substitution of these ions. - Abstract: Effect of substitution of rare earth ions (Dy 3+ , Gd 3+ and Sm 3+ ) on various properties of Ba 0.95 Sr 0.05 TiO 3 (BST) i.e. the composition Ba 0.95−1.5x Sr 0.05 R x TiO 3 (where x = 0.00, 0.01, 0.02, 0.03 and R are rare earths Dy, Gd, Sm) and that of their multiferroic composite with Ni 0.8 Co 0.2 Fe 2 O 4 (NCF) has been studied. Shifting of peaks corresponding to different compositions in the X-ray diffraction pattern confirmed the substitution of rare earth ions at both Ba 2+ and Ti 4+ sites in BST. It is clear from scanning electron microscopy (SEM) images that rare earth substitution in BST increases its grain size in both pure and composite samples. Substitution of rare earth ions results in increase in value of dielectric constant of pure and composite samples. Sm substitution in BST significantly decreases its Curie temperature. Dy substituted pure and composite samples possess superior ferroelectric properties as confirmed by polarization vs electric field (P–E) loops. Composite samples containing Dy, Gd and Sm substituted BST as ferroelectric phase possess lower values of remanent and saturation magnetizations in comparison to composite sample containing pure BST as ferroelectric phase (BSTC). Rare earth substituted composite samples possess higher value of magnetoelectric coefficient as compared to that for BSTC

  4. A novel method for direct solder bump pull testing using lead-free solders

    Science.gov (United States)

    Turner, Gregory Alan

    This thesis focuses on the design, fabrication, and evaluation of a new method for testing the adhesion strength of lead-free solders, named the Isotraction Bump Pull method (IBP). In order to develop a direct solder joint-strength testing method that did not require customization for different solder types, bump sizes, specific equipment, or trial-and-error, a combination of two widely used and accepted standards was created. First, solder bumps were made from three types of lead free solder were generated on untreated copper PCB substrates using an in-house fabricated solder bump-on-demand generator, Following this, the newly developed method made use of a polymer epoxy to encapsulate the solder bumps that could then be tested under tension using a high precision universal vertical load machine. The tests produced repeatable and predictable results for each of the three alloys tested that were in agreement with the relative behavior of the same alloys using other testing methods in the literature. The median peak stress at failure for the three solders tested were 2020.52 psi, 940.57 psi, and 2781.0 psi, and were within one standard deviation of the of all data collected for each solder. The assumptions in this work that brittle fracture occurred through the Intermetallic Compound layer (IMC) were validated with the use of Energy-Dispersive X-Ray Spectrometry and high magnification of the fractured surface of both newly exposed sides of the test specimens. Following this, an examination of the process to apply the results from the tensile tests into standard material science equations for the fracture of the systems was performed..

  5. Electrically Induced Strain and Polarization Fatigue in Lead-Free Ceramics

    Science.gov (United States)

    Sommer, Daniel

    Piezoelectric ceramics have traditionally been used in commercial applications such as actuators and sensors. By far the most popular piezoceramics currently in use are Pb(Zr,Ti)O3-based (PZT) ceramics. PZT ceramics are able to produce large strain and polarization with the application of an electric field, and this is due to the Morphotropic phase boundary (MPB). A MPB is associated with the boundary between tetragonal and rhombohedral perovskite phases. A disadvantage of PZT ceramics is that they contain ? 60 wt. % of lead. Since lead is toxic, this poses an environmental and health hazard because lead is released into the surroundings during fabrication and disposal. Because of this, there is a push to discover lead-free alternatives that have comparable properties to PZT but none of the health risks. One possibility is Bi 1/2(Na0.8K0.2)1/2Ti0.985 Ta0.015O3 (BNKT-1.5Ta). In addition to comparable electrical properties, any lead-free alternatives must have decent fatigue resistance to be useful for applications. This thesis focuses on the fatigue properties of BNKT-1.5Ta. The composition demonstrates high strain for a given applied electric field. To determine the fatigue resistance of BNKT-1.5Ta, data was gathered on how strain and polarization changed over number of cycles. Furthermore, fatigue tests at different temperatures were performed to ascertain if temperature affected fatigue life. X-ray diffraction (XRD) patterns and dielectric measurements were also collected to further examine any change in crystal structure and relative permittivity, respectively, before and after cycling.

  6. Magnetoelectric properties of Pb free Bi2FeTiO6: A theoretical investigation

    Science.gov (United States)

    Patra, Lokanath; Ravindran, P.

    2018-05-01

    The structural, electronic, magnetic and ferroelectric properties of Pb free double perovskite multiferroic Bi2FeTiO6 are investigated using density functional theory within the general gradient approximation (GGA) method. Our structural optimization using total energy calculations for different potential structures show a minimum energy for a non-centrosymmetric rhombohedral structure with R3c space group. Bi2FeTiO6 is found to be an antiferromagnetic insulator with C-type magnetic ordering with bandgap value of 0.3 eV. The calculated magnetic moment of 3.52 μB at Fe site shows the high spin arrangement of 3d electrons which is also confirmed by our orbital projected density of states analysis. We have analyzed the characteristics of bonding present between the constituents of Bi2FeTiO6 with the help of calculated partial density of states and Born effective charges. The ground state of the nearest centrosymmetric structure is found to be a G-type antiferromagnet with half metallicity showing that by the application of external electric field we can not only get a polarized state but also change the magnetic ordering and electronic structure in the present compound indicating strong magnetoelectric coupling. The cation sites the coexistence of Bi 6s lone pair (bring disproportionate charge distribution) and Ti4+ d0 ions which brings covalency produces off-center displacement and favors a non-centrosymmetric ground state and thus ferroelectricity. Our Berry phase calculation gives a polarization of 48 µCcm-2 for Bi2FeTiO6.

  7. Ferrielectricity in DyMn2O5: A golden touchstone for multiferroicity of RMn2O5 family

    Directory of Open Access Journals (Sweden)

    J.-M. Liu

    2015-06-01

    Full Text Available The RMn2O5 manganite compounds represent one class of multiferroic family with magnetic origins, which has been receiving continuous attention in the past decade. So far, our understanding of the magnetic origins for ferroelectricity in RMn2O5 is associated with the nearly collinear antiferromagnetic structure of Mn ions, while the exchange striction induced ionic displacements are the consequence of the spin frustration competitions. While this scenario may be applied to almost all RMn2O5 members, its limitation is either clear: the temperature-dependent behaviors of electric polarization and its responses to external stimuli are seriously materials dependent. These inconsistences raise substantial concern with the state-of-the-art physics of ferroelectricity in RMn2O5. In this mini-review, we present our recent experimental results on the roles of the 4f moments from R ions which are intimately coupled with the 3d moments from Mn ions. DyMn2O5 is a golden figure for illustrating these roles. It is demonstrated that the spin structure accommodates two nearly collinear sublattices which generate respectively two ferroelectric (FE sublattices, enabling DyMn2O5 an emergent ferrielectric (FIE system rarely identified in magnetically induced FEs. The evidence is presented from several aspects, including FIE-like phenomena and magnetoelectric responses, proposed structural model, and experimental check by nonmagnetic substitutions of the 3d and 4f moments. Additional perspectives regarding possible challenges in understanding the multiferroicity of RMn2O5 as a generalized scenario are discussed.

  8. Dynamic state switching in nonlinear multiferroic cantilevers

    Science.gov (United States)

    Wang, Yi; Onuta, Tiberiu-Dan; Long, Christian J.; Lofland, Samuel E.; Takeuchi, Ichiro

    2013-03-01

    We demonstrate read-write-read-erase cyclical mechanical-memory properties of all-thin-film multiferroic heterostructured Pb(Zr0.52Ti0.48) O3 / Fe0.7Ga0.3 cantilevers when a high enough voltage around the resonant frequency of the device is applied on the Pb(Zr0.52Ti0.48) O3 piezo-film. The device state switching process occurs due to the presence of a hysteresis loop in the piezo-film frequency response, which comes from the nonlinear behavior of the cantilever. The reference frequency at which the strain-mediated Fe0.7Ga0.3 based multiferroic device switches can also be tuned by applying a DC magnetic field bias that contributes to the increase of the cantilever effective stiffness. The switching dynamics is mapped in the phase space of the device measured transfer function characteristic for such high piezo-film voltage excitation, providing additional information on the dynamical stability of the devices.

  9. Discovery of Enhanced Magnetoelectric Coupling through Electric Field Control of Two-Magnon Scattering within Distorted Nanostructures.

    Science.gov (United States)

    Xue, Xu; Zhou, Ziyao; Dong, Guohua; Feng, Mengmeng; Zhang, Yijun; Zhao, Shishun; Hu, Zhongqiang; Ren, Wei; Ye, Zuo-Guang; Liu, Yaohua; Liu, Ming

    2017-09-26

    Electric field control of dynamic spin interactions is promising to break through the limitation of the magnetostatic interaction based magnetoelectric (ME) effect. In this work, electric field control of the two-magnon scattering (TMS) effect excited by in-plane lattice rotation has been demonstrated in a La 0.7 Sr 0.3 MnO 3 (LSMO)/Pb(Mn 2/3 Nb 1/3 )-PbTiO 3 (PMN-PT) (011) multiferroic heterostructure. Compared with the conventional strain-mediated ME effect, a giant enhancement of ME effect up to 950% at the TMS critical angle is precisely determined by angular resolution of the ferromagnetic resonance (FMR) measurement. Particularly, a large electric field modulation of magnetic anisotropy (464 Oe) and FMR line width (401 Oe) is achieved at 173 K. The electric-field-controllable TMS effect and its correlated ME effect have been explained by electric field modulation of the planar spin interactions triggered by spin-lattice coupling. The enhancement of the ME effect at various temperatures and spin dynamics control are promising paradigms for next-generation voltage-tunable spintronic devices.

  10. Multiferroic iron oxide thin films at room temperature

    Czech Academy of Sciences Publication Activity Database

    Gich, M.; Fina, I.; Morelli, Alessio; Sánchez, F.; Alexe, M.; Gazquez, J.; Fontcuberta, J.; Roig, A.

    2014-01-01

    Roč. 26, č. 27 (2014), s. 4645-4652 ISSN 0935-9648 Institutional support: RVO:68378271 Keywords : multiferroic * iron oxide * thin film Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 17.493, year: 2014

  11. Chapter 23. Single and Heterostructure Multiferroic Thin Films

    OpenAIRE

    Barbier , Antoine

    2018-01-01

    International audience; Multiferroic oxide materials exhibiting several long range ferroic orders are of high interest because of their wide range of potential applications. The incorporation of their genuine properties in new devices, offering additional physical properties, requires often elaborating them in form of thin films. Retaining their multiferroic characteristics is very challenging. However, thin films can be structured on the nanometer scale and additional degrees of freedom, suc...

  12. Surfaces and Interfaces of Magnetoelectric Oxide Systems

    Science.gov (United States)

    Cao, Shi

    Magnetoelectric materials Cr2O3, hexagonal LuFeO 3 and YbFeO3 are studied in this thesis. The surface of chromia (Cr2O3) has a surface electronic structure distinct from the bulk. Our work shows that placing a Cr2O3 single crystal into a single domain state will result in net Cr2O 3 spin polarization at the boundary, even in the presence of a gold overlayer. From the Cr 2p3/2 X-ray magnetic circular dichroism signal, there is clear evidence of interface polarization with overlayers of both Pd and Pt on chromia. Cobalt thin films on Cr2O3(0001) show larger magnetic contrast in magnetic force microscopy indicating enhancement of perpendicular anisotropy induced by Cr2O3. The interfacial charge transfer between mechanically exfoliated few-layer graphene and Cr2O3(0001) surfaces has been investigated showing hole doping of few-layer graphene. Density functional theory calculations furthermore confirm the p-type nature of the graphene on top of chromia, and suggest that the chromia is able to induce a significant carrier spin polarization in the graphene layer. The surface termination and the nominal valence states for hexagonal LuFeO3 thin films were characterized. The stable surface terminates in a Fe-O layer. This is consistent wit the results of density functional calculations. The structural transition at about 1000 °C, from the hexagonal to the orthorhombic phase of LuFeO3, has been investigated in thin films of LuFeO3. The electronic structure for the conduction bands of both hexagonal and orthorhombic LuFeO3 thin films have been measured. Dramatic differences in both the spectral features and the linear dichroism are observed. We have also studied the ferrimagnetism in h-YbFeO3 by measuring the magnetization of Fe and Yb separately. The results directly show antialignment of magnetization of Yb and Fe ions in h-YbFeO3 at low temperature, with an exchange field on Yb of about 17 kOe. All ferrimagnets, by default, are magnetoelectrics. These findings directly

  13. Self-Biased 215MHz Magnetoelectric NEMS Resonator for Ultra-Sensitive DC Magnetic Field Detection

    Science.gov (United States)

    Nan, Tianxiang; Hui, Yu; Rinaldi, Matteo; Sun, Nian X.

    2013-06-01

    High sensitivity magnetoelectric sensors with their electromechanical resonance frequencies electromechanical systems (NEMS) resonator with an electromechanical resonance frequency of 215 MHz based on an AlN/(FeGaB/Al2O3) × 10 magnetoelectric heterostructure for detecting DC magnetic fields. This magnetoelectric NEMS resonator showed a high quality factor of 735, and strong magnetoelectric coupling with a large voltage tunable sensitivity. The admittance of the magnetoelectric NEMS resonator was very sensitive to DC magnetic fields at its electromechanical resonance, which led to a new detection mechanism for ultra-sensitive self-biased RF NEMS magnetoelectric sensor with a low limit of detection of DC magnetic fields of ~300 picoTelsa. The magnetic/piezoelectric heterostructure based RF NEMS magnetoelectric sensor is compact, power efficient and readily integrated with CMOS technology, which represents a new class of ultra-sensitive magnetometers for DC and low frequency AC magnetic fields.

  14. Study of lead free ferroelectrics using overlay technique on thick film microstrip ring resonator

    Directory of Open Access Journals (Sweden)

    Shridhar N. Mathad

    2016-03-01

    Full Text Available The lead free ferroelectrics, strontium barium niobates, were synthesized via the low cost solid state reaction method and their fritless thick films were fabricated by screen printing technique on alumina substrate. The X band response (complex permittivity at very high frequencies of Ag thick film microstrip ring resonator perturbed with strontium barium niobates (SrxBa1-xNb2O6 in form of bulk and thick film was measured. A new approach for determination of complex permittivity (ε′ and ε′′ in the frequency range 8–12 GHz, using perturbation of Ag thick film microstrip ring resonator (MSRR, was applied for both bulk and thick film of strontium barium niobates (SrxBa1-xNb2O6. The microwave conductivity of the bulk and thick film lie in the range from 1.779 S/cm to 2.874 S/cm and 1.364 S/cm to 2.296 S/cm, respectively. The penetration depth of microwave in strontium barium niobates is also reported.

  15. Lead-free, air-stable all-inorganic cesium bismuth halide perovskite nanocrystals

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Bin; Hong, Feng; Mao, Xin; Li, Yajuan [State Key Laboratory of Molecular Reaction Dynamics, Dalian Institute of Chemical Physics, Chinese Academy of Science (China); University of the Chinese Academy of Sciences, Beijing (China); Chen, Junsheng [State Key Laboratory of Molecular Reaction Dynamics, Dalian Institute of Chemical Physics, Chinese Academy of Science (China); Department of Chemical Physics and NanoLund, Chemical Center, Lund University (Sweden); Zheng, Kaibo; Pullerits, Tonu [Department of Chemical Physics and NanoLund, Chemical Center, Lund University (Sweden); Yang, Songqiu; Deng, Weiqiao; Han, Keli [State Key Laboratory of Molecular Reaction Dynamics, Dalian Institute of Chemical Physics, Chinese Academy of Science (China)

    2017-10-02

    Lead-based perovskite nanocrystals (NCs) have outstanding optical properties and cheap synthesis conferring them a tremendous potential in the field of optoelectronic devices. However, two critical problems are still unresolved and hindering their commercial applications: one is the fact of being lead-based and the other is the poor stability. Lead-free all-inorganic perovskite Cs{sub 3}Bi{sub 2}X{sub 9} (X=Cl, Br, I) NCs are synthesized with emission wavelength ranging from 400 to 560 nm synthesized by a facile room temperature reaction. The ligand-free Cs{sub 3}Bi{sub 2}Br{sub 9} NCs exhibit blue emission with photoluminescence quantum efficiency (PLQE) about 0.2 %. The PLQE can be increased to 4.5 % when extra surfactant (oleic acid) is added during the synthesis processes. This improvement stems from passivation of the fast trapping process (2-20 ps). Notably, the trap states can also be passivated under humid conditions, and the NCs exhibited high stability towards air exposure exceeding 30 days. (copyright 2017 Wiley-VCH Verlag GmbH and Co. KGaA, Weinheim)

  16. Lead-free LiNbO3 nanowire-based nanocomposite for piezoelectric power generation

    Science.gov (United States)

    2014-01-01

    In a flexible nanocomposite-based nanogenerator, in which piezoelectric nanostructures are mixed with polymers, important parameters to increase the output power include using long nanowires with high piezoelectricity and decreasing the dielectric constant of the nanocomposite. Here, we report on piezoelectric power generation from a lead-free LiNbO3 nanowire-based nanocomposite. Through ion exchange of ultra-long Na2Nb2O6-H2O nanowires, we synthesized long (approximately 50 μm in length) single-crystalline LiNbO3 nanowires having a high piezoelectric coefficient (d33 approximately 25 pmV-1). By blending LiNbO3 nanowires with poly(dimethylsiloxane) (PDMS) polymer (volume ratio 1:100), we fabricated a flexible nanocomposite nanogenerator having a low dielectric constant (approximately 2.7). The nanogenerator generated stable electric power, even under excessive strain conditions (approximately 105 cycles). The different piezoelectric coefficients of d33 and d31 for LiNbO3 may have resulted in generated voltage and current for the e33 geometry that were 20 and 100 times larger than those for the e31 geometry, respectively. This study suggests the importance of the blending ratio and strain geometry for higher output-power generation in a piezoelectric nanocomposite-based nanogenerator. PACS 77.65.-j; 77.84.-s; 73.21.Hb PMID:24386884

  17. An equivalent dipole analysis of PZT ceramics and lead-free piezoelectric single crystals

    Directory of Open Access Journals (Sweden)

    Andrew J. Bell

    2016-06-01

    Full Text Available The recently proposed Equivalent Dipole Model for describing the electromechanical properties of ionic solids in terms of 3 ions and 2 bonds has been applied to PZT ceramics and lead-free single crystal piezoelectric materials, providing analysis in terms of an effective ionic charge and the asymmetry of the interatomic force constants. For PZT it is shown that, as a function of composition across the morphotropic phase boundary, the dominant bond compliance peaks at 52% ZrO2. The stiffer of the two bonds shows little composition dependence with no anomaly at the phase boundary. The effective charge has a maximum value at 50% ZrO2, decreasing across the phase boundary region, but becoming constant in the rhombohedral phase. The single crystals confirm that both the asymmetry in the force constants and the magnitude of effective charge are equally important in determining the values of the piezoelectric charge coefficient and the electromechanical coupling coefficient. Both are apparently temperature dependent, increasing markedly on approaching the Curie temperature.

  18. Lead-Free Antiferroelectric Silver Niobate Tantalate with High Energy Storage Performance.

    Science.gov (United States)

    Zhao, Lei; Liu, Qing; Gao, Jing; Zhang, Shujun; Li, Jing-Feng

    2017-08-01

    Antiferroelectric materials that display double ferroelectric hysteresis loops are receiving increasing attention for their superior energy storage density compared to their ferroelectric counterparts. Despite the good properties obtained in antiferroelectric La-doped Pb(Zr,Ti)O 3 -based ceramics, lead-free alternatives are highly desired due to the environmental concerns, and AgNbO 3 has been highlighted as a ferrielectric/antiferroelectric perovskite for energy storage applications. Enhanced energy storage performance, with recoverable energy density of 4.2 J cm -3 and high thermal stability of the energy storage density (with minimal variation of ≤±5%) over 20-120 °C, can be achieved in Ta-modified AgNbO 3 ceramics. It is revealed that the incorporation of Ta to the Nb site can enhance the antiferroelectricity because of the reduced polarizability of B-site cations, which is confirmed by the polarization hysteresis, dielectric tunability, and selected-area electron diffraction measurements. Additionally, Ta addition in AgNbO 3 leads to decreased grain size and increased bulk density, increasing the dielectric breakdown strength, up to 240 kV cm -1 versus 175 kV cm -1 for the pure counterpart, together with the enhanced antiferroelectricity, accounting for the high energy storage density. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  19. Effect of Strain Rate on Joint Strength and Failure Mode of Lead-Free Solder Joints

    Science.gov (United States)

    Lin, Jian; Lei, Yongping; Fu, Hanguang; Guo, Fu

    2018-03-01

    In surface mount technology, the Sn-3.0Ag-0.5Cu solder joint has a shorter impact lifetime than a traditional lead-tin solder joint. In order to improve the impact property of SnAgCu lead-free solder joints and identify the effect of silver content on tensile strength and impact property, impact experiments were conducted at various strain rates on three selected SnAgCu based solder joints. It was found that joint failure mainly occurred in the solder material with large plastic deformation under low strain rate, while joint failure occurred at the brittle intermetallic compound layer without any plastic deformation at a high strain rate. Joint strength increased with the silver content in SnAgCu alloys in static tensile tests, while the impact property of the solder joint decreased with increasing silver content. When the strain rate was low, plastic deformation occurred with failure and the tensile strength of the Sn-3.0Ag-0.5Cu solder joint was higher than that of Sn-0.3Ag-0.7Cu; when the strain rate was high, joint failure mainly occurred at the brittle interface layer and the Sn-0.3Ag-0.7Cu solder joint had a better impact resistance with a thinner intermetallic compound layer.

  20. Piezoelectric Active Humidity Sensors Based on Lead-Free NaNbO3 Piezoelectric Nanofibers

    Directory of Open Access Journals (Sweden)

    Li Gu

    2016-06-01

    Full Text Available The development of micro-/nano-scaled energy harvesters and the self-powered sensor system has attracted great attention due to the miniaturization and integration of the micro-device. In this work, lead-free NaNbO3 piezoelectric nanofibers with a monoclinic perovskite structure were synthesized by the far-field electrospinning method. The flexible active humidity sensors were fabricated by transferring the nanofibers from silicon to a soft polymer substrate. The sensors exhibited outstanding piezoelectric energy-harvesting performance with output voltage up to 2 V during the vibration process. The output voltage generated by the NaNbO3 sensors exhibited a negative correlation with the environmental humidity varying from 5% to 80%, where the peak-to-peak value of the output voltage generated by the sensors decreased from 0.40 to 0.07 V. The sensor also exhibited a short response time, good selectively against ethanol steam, and great temperature stability. The piezoelectric active humidity sensing property could be attributed to the increased leakage current in the NaNbO3 nanofibers, which was generated due to proton hopping among the H3O+ groups in the absorbed H2O layers under the driving force of the piezoelectric potential.

  1. Nanoscale characterization and local piezoelectric properties of lead-free KNN-LT-LS thin films

    Science.gov (United States)

    Abazari, M.; Choi, T.; Cheong, S.-W.; Safari, A.

    2010-01-01

    We report the observation of domain structure and piezoelectric properties of pure and Mn-doped (K0.44,Na0.52,Li0.04)(Nb0.84,Ta0.1,Sb0.06)O3 (KNN-LT-LS) thin films on SrTiO3 substrates. It is revealed that, using piezoresponse force microscopy, ferroelectric domain structure in such 500 nm thin films comprised of primarily 180° domains. This was in accordance with the tetragonal structure of the films, confirmed by relative permittivity measurements and x-ray diffraction patterns. Effective piezoelectric coefficient (d33) of the films were calculated using piezoelectric displacement curves and shown to be ~53 pm V-1 for pure KNN-LT-LS thin films. This value is among the highest values reported for an epitaxial lead-free thin film and shows a great potential for KNN-LT-LS to serve as an alternative to PZT thin films in future applications.

  2. Ultrahigh Piezoelectric Properties in Textured (K,Na)NbO3 -Based Lead-Free Ceramics.

    Science.gov (United States)

    Li, Peng; Zhai, Jiwei; Shen, Bo; Zhang, Shujun; Li, Xiaolong; Zhu, Fangyuan; Zhang, Xingmin

    2018-02-01

    High-performance lead-free piezoelectric materials are in great demand for next-generation electronic devices to meet the requirement of environmentally sustainable society. Here, ultrahigh piezoelectric properties with piezoelectric coefficients (d 33 ≈700 pC N -1 , d 33 * ≈980 pm V -1 ) and planar electromechanical coupling factor (k p ≈76%) are achieved in highly textured (K,Na)NbO 3 (KNN)-based ceramics. The excellent piezoelectric properties can be explained by the strong anisotropic feature, optimized engineered domain configuration in the textured ceramics, and facilitated polarization rotation induced by the intermediate phase. In addition, the nanodomain structures with decreased domain wall energy and increased domain wall mobility also contribute to the ultrahigh piezoelectric properties. This work not only demonstrates the tremendous potential of KNN-based ceramics to replace lead-based piezoelectrics but also provides a good strategy to design high-performance piezoelectrics by controlling appropriate phase and crystallographic orientation. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  3. Finite Element Study on Acoustic Energy Harvesting Using Lead-Free Piezoelectric Ceramics

    Science.gov (United States)

    Kumar, Anuruddh; Sharma, Anshul; Kumar, Rajeev; Vaish, Rahul

    2018-02-01

    In this article, a numerical investigation is performed for ambient acoustic energy harvesting at a low-frequency acoustic signal. A model of a quarter-wavelength resonator with a rectangular cross section is constructed, and piezoelectric-laminated bimorph plates are placed inside the system. Finite element modeling is implemented to numerically formulate the piezoelectric energy harvester. With the application of acoustic pressure at the open end of the resonator, amplified acoustic pressure inside the tube vibrates the piezolaminated bimorphs inside the tube, thus generating electric potential on the piezoelectric layers. To generate higher voltage and power in the acoustic harvester, multiple piezolaminated plates are positioned inside the resonator. The lead-free piezoelectric material K0.475Na0.475Li0.05 (Nb0.92Ta0.05Sb0.03)O3 (KNLNTS) is laminated on the host structure as a layer of piezoelectric material for the acoustic energy harvester. With the application of an acoustic sound pressure of 1 dB at the opening of the tube, a maximum output voltage of 16.3 V is measured at the first natural frequency, while the maximum power calculated is 0.033 mW. Maximum voltage is obtained when five piezoelectric bimorphs are place inside the resonator. At the second natural frequency, the maximum voltage measured is 8.40 V, obtained when eight piezoelectric bimorphs are placed inside the resonator, and the maximum power calculated is 0.020 mW.

  4. Development of a Flexible Lead-Free Piezoelectric Transducer for Health Monitoring in the Space Environment

    Directory of Open Access Journals (Sweden)

    Marco Laurenti

    2015-11-01

    Full Text Available In this work we report on the fabrication process for the development of a flexible piezopolymeric transducer for health monitoring applications, based on lead-free, piezoelectric zinc oxide (ZnO thin films. All the selected materials are compatible with the space environment and were deposited by the RF magnetron sputtering technique at room temperature, in view of preserving the total flexibility of the structures, which is an important requirement to guarantee coupling with cylindrical fuel tanks whose integrity we want to monitor. The overall transducer architecture was made of a c-axis-oriented ZnO thin film coupled to a pair of flexible Polyimide foils coated with gold (Au electrodes. The fabrication process started with the deposition of the bottom electrode on Polyimide foils. The ZnO thin film and the top electrode were then deposited onto the Au/Polyimide substrates. Both the electrodes and ZnO layer were properly patterned by wet-chemical etching and optical lithography. The assembly of the final structure was then obtained by gluing the upper and lower Polyimide foils with an epoxy resin capable of guaranteeing low outgassing levels, as well as adequate thermal and electrical insulation of the transducers. The piezoelectric behavior of the prototypes was confirmed and evaluated by measuring the mechanical displacement induced from the application of an external voltage.

  5. Nanoscale characterization and local piezoelectric properties of lead-free KNN-LT-LS thin films

    Energy Technology Data Exchange (ETDEWEB)

    Abazari, M; Safari, A [Glenn Howatt Electroceramics Laboratories, Department of Materials Science and Engineering, Rutgers-The state University of New Jersey, Piscataway, NJ 08854 (United States); Choi, T; Cheong, S-W [Rutgers Center for Emergent Materials, Department of Physics and Astronomy, Rutgers-The state University of New Jersey, Piscataway, NJ 08854 (United States)

    2010-01-20

    We report the observation of domain structure and piezoelectric properties of pure and Mn-doped (K{sub 0.44},Na{sub 0.52},Li{sub 0.04})(Nb{sub 0.84},Ta{sub 0.1},Sb{sub 0.06})O{sub 3} (KNN-LT-LS) thin films on SrTiO{sub 3} substrates. It is revealed that, using piezoresponse force microscopy, ferroelectric domain structure in such 500 nm thin films comprised of primarily 180{sup 0} domains. This was in accordance with the tetragonal structure of the films, confirmed by relative permittivity measurements and x-ray diffraction patterns. Effective piezoelectric coefficient (d{sub 33}) of the films were calculated using piezoelectric displacement curves and shown to be {approx}53 pm V{sup -1} for pure KNN-LT-LS thin films. This value is among the highest values reported for an epitaxial lead-free thin film and shows a great potential for KNN-LT-LS to serve as an alternative to PZT thin films in future applications.

  6. High-Performance Red-Light Photodetector Based on Lead-Free Bismuth Halide Perovskite Film.

    Science.gov (United States)

    Tong, Xiao-Wei; Kong, Wei-Yu; Wang, You-Yi; Zhu, Jin-Miao; Luo, Lin-Bao; Wang, Zheng-Hua

    2017-06-07

    In this study, we developed a sensitive red-light photodetector (RLPD) based on CsBi 3 I 10 perovskite thin film. This inorganic, lead-free perovskite was fabricated by a simple spin-coating method. Device analysis reveals that the as-assembled RLPD was very sensitive to 650 nm light, with an on/off ratio as high as 10 5 . The responsivity and specific detectivity of the device were estimated to be 21.8 A/W and 1.93 × 10 13 Jones, respectively, which are much better than those of other lead halide perovskite devices. In addition, the device shows a fast response (rise time: 0.33 ms; fall time: 0.38 ms) and a high external quantum efficiency (4.13 × 10 3 %). It is also revealed that the RLPD has a very good device stability even after storage for 3 months under ambient conditions. In summary, we suggest that the CsBi 3 I 10 perovskite photodetector developed in this study may have potential applications in future optoelectronic systems.

  7. Methylammonium Bismuth Iodide as a Lead-Free, Stable Hybrid Organic-Inorganic Solar Absorber.

    Science.gov (United States)

    Hoye, Robert L Z; Brandt, Riley E; Osherov, Anna; Stevanović, Vladan; Stranks, Samuel D; Wilson, Mark W B; Kim, Hyunho; Akey, Austin J; Perkins, John D; Kurchin, Rachel C; Poindexter, Jeremy R; Wang, Evelyn N; Bawendi, Moungi G; Bulović, Vladimir; Buonassisi, Tonio

    2016-02-18

    Methylammonium lead halide (MAPbX3 ) perovskites exhibit exceptional carrier transport properties. But their commercial deployment as solar absorbers is currently limited by their intrinsic instability in the presence of humidity and their lead content. Guided by our theoretical predictions, we explored the potential of methylammonium bismuth iodide (MBI) as a solar absorber through detailed materials characterization. We synthesized phase-pure MBI by solution and vapor processing. In contrast to MAPbX3, MBI is air stable, forming a surface layer that does not increase the recombination rate. We found that MBI luminesces at room temperature, with the vapor-processed films exhibiting superior photoluminescence (PL) decay times that are promising for photovoltaic applications. The thermodynamic, electronic, and structural features of MBI that are amenable to these properties are also present in other hybrid ternary bismuth halide compounds. Through MBI, we demonstrate a lead-free and stable alternative to MAPbX3 that has a similar electronic structure and nanosecond lifetimes. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  8. Study on interfacial reaction between lead-free solders and alternative surface finishes

    International Nuclear Information System (INIS)

    Siti Rabiatul Aisha; Ourdjini, A.; Saliza Osman

    2007-01-01

    This study investigates the interfacial reactions occurring during reflow soldering between Sn-Ag-Cu lead-free solder and two surface finishes: electroless nickel/ immersion gold (ENIG) and immersion silver (IAg). The study focuses on interfacial reactions evolution and growth kinetics of intermetallic compounds (IMC) formed during soldering and isothermal ageing at 150 degree Celsius for up to 2000 hours. Optical and scanning electron microscopy were used to measure IMC thickness and examine the morphology of IMC respectively, whereas the IMC phases were identified by energy dispersive X-ray analysis (EDX). The results showed that the IMC formed on ENIG finish is thinner compared to that formed on IAg finish. For IAg surface finish, Cu 6 Sn 5 IMCs with scallop morphology are formed at the solder/ surface finish interface after reflow while a second IMC, Cu 3 Sn was formed between the copper and Cu 6 Sn 5 IMC after the isothermal ageing treatment. For ENIG surface finish both (Cu,Ni) 6 Sn 5 and (Ni,Cu) 3 Sn 4 are formed after soldering. Isothermal aging of the solder joints formed on ENIG finish was found to have a significant effect on the morphology of the intermetallics by transforming to more spherical and denser morphology in addition to increase i their thickness with increased ageing time. (author)

  9. Synthesis and characterization of lead-free ternary component BST–BCT–BZT ceramic capacitors

    Directory of Open Access Journals (Sweden)

    Venkata Sreenivas Puli

    2014-04-01

    Full Text Available Polycrystalline sample of lead-free 1/3(Ba0.70Sr0.30TiO3 + 1/3(Ba0.70Ca0.30TiO3 + 1/3(BaZr0.20Ti0.80O3(BST-BCT-BZT ceramic was synthesized by solid state reaction method. Phase purity and crystal structure of as-synthesized materials was confirmed by X-ray diffraction (XRD. Temperature-dependent dielectric permittivity studies demonstrated frequency-independent behavior, indicating that the studied sample has typical diffuse phase transition behavior with partial thermal hysteresis. A ferroelectric phase transition between cubic and tetragonal phase was noticed near room temperature (~ 330 K. Bulk P–E hysteresis loop showed a saturation polarization of 20.4 μC/cm2 and a coercive field of ~ 12.78 kV/cm at a maximum electric field of ~ 115 kV/cm. High dielectric constant (ε ~ 5773, low dielectric loss (tan δ ~ 0.03 were recorded at room temperature. Discharge energy density of 0.44 J/cm3 and charge energy density of 1.40 J/cm3 were calculated from nonlinear ferroelectric hysteresis loop at maximum electric field. Dielectric constant at variable temperatures and electric fields, ferroelectric to paraelectric phase transition and energy storage properties were thoroughly discussed.

  10. An equivalent dipole analysis of PZT ceramics and lead-free piezoelectric single crystals

    Science.gov (United States)

    Bell, Andrew J.

    2016-04-01

    The recently proposed Equivalent Dipole Model for describing the electromechanical properties of ionic solids in terms of 3 ions and 2 bonds has been applied to PZT ceramics and lead-free single crystal piezoelectric materials, providing analysis in terms of an effective ionic charge and the asymmetry of the interatomic force constants. For PZT it is shown that, as a function of composition across the morphotropic phase boundary, the dominant bond compliance peaks at 52% ZrO2. The stiffer of the two bonds shows little composition dependence with no anomaly at the phase boundary. The effective charge has a maximum value at 50% ZrO2, decreasing across the phase boundary region, but becoming constant in the rhombohedral phase. The single crystals confirm that both the asymmetry in the force constants and the magnitude of effective charge are equally important in determining the values of the piezoelectric charge coefficient and the electromechanical coupling coefficient. Both are apparently temperature dependent, increasing markedly on approaching the Curie temperature.

  11. Wetting behaviour of lead-free Sn-based alloys on Cu and Ni substrates

    International Nuclear Information System (INIS)

    Amore, S.; Ricci, E.; Borzone, G.; Novakovic, R.

    2008-01-01

    The present work was carried out in the framework of the study of new lead-free solder alloys for technical applications in electronic devices. In the focus of this characterisation the wetting behaviour of several Sn-rich alloys belonging to the In-Sn, Au-Sn and Cu-Sn systems has been studied by measuring the contact angle variations on Cu and Ni substrates as a function of time and temperature. The interface between the alloy and the substrate has been analysed by the use of optical microscopy and scanning electron microscopy combined with energy-dispersive X-ray spectrometry in order to study the reaction between the alloy and the solid substrate and the possible formation of different compounds at the interface. A remarkable effect of the two different substrates on the behaviour of the contact angle as a function of temperature and on the morphology of the interface between the liquid solder and the solid substrate was observed for the In-Sn and Cu-Sn, while the Au-Sn system shows a very similar wetting behaviour on Cu and Ni

  12. Endurance of lead-free assembly under board level drop test and thermal cycling

    Energy Technology Data Exchange (ETDEWEB)

    Xia Yanghua [State Key Laboratory of Functional Materials for Informatics, Shanghai Institute of Microsystem and Information Technology, Chinese Academy of Sciences, Shanghai 200050 (China)], E-mail: xia_yanghua@hotmail.com; Xie Xiaoming [State Key Laboratory of Functional Materials for Informatics, Shanghai Institute of Microsystem and Information Technology, Chinese Academy of Sciences, Shanghai 200050 (China)

    2008-06-12

    The reliability of lead-free electronic assemblies under board level drop test and thermal cycling was investigated. TSOP (thin small outline package) devices with FeNi leads were reflow soldered on FR4 PCB (printed circuit board) with Sn3.0Ag0.5Cu (wt%) solder. The effects of different PCB finishes (organic solderability preservative (OSP) and electroless nickel immersion gold (ENIG)) on the reliability performance were studied. The results show that the assemblies with ENIG finishes reveal better reliability performance than its OSP counterparts under drop test, however, the OSP samples outperform those with ENIG finishes under thermal cycling. The failure mechanism is different under these two test conditions: the solder joints fracture into the intermetallic compounds (IMCs) layer under drop test, and cracks initiate in the bulk solder under thermal cycling. The surface finishes have an effect on the failure mode. The propagation of crack in the ENIG case is along the device/solder interface, while in the case of OSP, the crack extends parallel to the solder/PCB interface.

  13. Comparative shear tests of some low temperature lead-free solder pastes

    Science.gov (United States)

    Branzei, Mihai; Plotog, Ioan; Varzaru, Gaudentiu; Cucu, Traian C.

    2016-12-01

    The range of electronic components and as a consequence, all parts of automotive electronic equipment operating temperatures in a vehicle is given by the location of that equipment, so the maximum temperature can vary between 358K and 478K1. The solder joints could be defined as passive parts of the interconnection structure of automotive electronic equipment, at a different level, from boards of electronic modules to systems. The manufacturing costs reduction necessity and the RoHS EU Directive3, 7 consequences generate the trend to create new Low-Temperature Lead-Free (LTLF) solder pastes family9. In the paper, the mechanical strength of solder joints and samples having the same transversal section as resistor 1206 case type made using the same LTLF alloys into Vapour Phase Soldering (VPS) process characterized by different cooling rates (slow and rapid) and two types of test PCBs pads finish, were benchmarked at room temperature. The presented work extends the theoretical studies and experiments upon heat transfer in VPSP in order to optimize the technology for soldering process (SP) of automotive electronic modules and could be extended for home and modern agriculture appliances industry. The shear forces (SF) values of the LTLF alloy samples having the same transversal section as resistor 1206 case type will be considered as references values of a database useful in the new solder alloy creation processes and their qualification for automotive electronics domain.

  14. Enhanced interfacial thermal transport in pnictogen tellurides metallized with a lead-free solder alloy

    Energy Technology Data Exchange (ETDEWEB)

    Devender,; Ramanath, Ganpati, E-mail: Ramanath@rpi.edu [Department of Materials Science and Engineering, Rensselaer Polytechnic Institute, Troy, New York 12180 (United States); Lofgreen, Kelly; Devasenathipathy, Shankar; Swan, Johanna; Mahajan, Ravi [Intel Corporation, Assembly Test and Technology Development, Chandler, Arizona 85226 (United States); Borca-Tasciuc, Theodorian [Department of Mechanical Aerospace and Nuclear Engineering, Rensselaer Polytechnic Institute, Troy, New York 12180 (United States)

    2015-11-15

    Controlling thermal transport across metal–thermoelectric interfaces is essential for realizing high efficiency solid-state refrigeration and waste-heat harvesting power generation devices. Here, the authors report that pnictogen chalcogenides metallized with bilayers of Sn{sub 96.5}Ag{sub 3}Cu{sub 0.5} solder and Ni barrier exhibit tenfold higher interfacial thermal conductance Γ{sub c} than that obtained with In/Ni bilayer metallization. X-ray diffraction and x-ray spectroscopy indicate that reduced interdiffusion and diminution of interfacial SnTe formation due to Ni layer correlates with the higher Γ{sub c}. Finite element modeling of thermoelectric coolers metallized with Sn{sub 96.5}Ag{sub 3}Cu{sub 0.5}/Ni bilayers presages a temperature drop ΔT ∼ 22 K that is 40% higher than that obtained with In/Ni metallization. Our results underscore the importance of controlling chemical intermixing at solder–metal–thermoelectric interfaces to increase the effective figure of merit, and hence, the thermoelectric cooling efficiency. These findings should facilitate the design and development of lead-free metallization for pnictogen chalcogenide-based thermoelectrics.

  15. Lead-free piezoelectric KNN-BZ-BNT films with a vertical morphotropic phase boundary

    Directory of Open Access Journals (Sweden)

    Wen Chen

    2015-07-01

    Full Text Available The lead-free piezoelectric 0.915K0.5Na0.5NbO3-0.075BaZrO3-0.01Bi0.5Na0.5TiO3 (0.915KNN-0.075BZ-0.01BNT films were prepared by a chemical solution deposition method. The films possess a pure rhomobohedral perovskite phase and a dense surface without crack. The temperature-dependent dielectric properties of the specimens manifest that only phase transition from ferroelectric to paraelectric phase occurred and the Curie temperature is 217 oC. The temperature stability of ferroelectric phase was also supported by the stable piezoelectric properties of the films. These results suggest that the slope of the morphotropic phase boundary (MPB for the solid solution formed with the KNN and BZ in the films should be vertical. The voltage-induced polarization switching, and a distinct piezo-response suggested that the 0.915 KNN-0.075BZ-0.01BNT films show good piezoelectric properties.

  16. Intrinsic Defect Physics in Indium-based Lead-free Halide Double Perovskites.

    Science.gov (United States)

    Xu, Jian; Liu, Jian-Bo; Liu, Bai-Xin; Huang, Bing

    2017-09-21

    Lead-free halide double perovskites (HDPs) are expected to be promising photovoltaic (PV) materials beyond organic-inorganic halide perovskite, which is hindered by its structural instability and toxicity. The defect- and stability-related properties of HDPs are critical for the use of HDPs as important PV absorbers, yet their reliability is still unclear. Taking Cs 2 AgInBr 6 as a representative, we have systemically investigated the defect properties of HDPs by theoretical calculations. First, we have determined the stable chemical potential regions to grow stoichiometric Cs 2 AgInBr 6 without structural decomposition. Second, we reveal that Ag-rich and Br-poor are the ideal chemical potential conditions to grow n-type Cs 2 AgInBr 6 with shallow defect levels. Third, we find the conductivity of Cs 2 AgInBr 6 can change from good n-type, to poorer n-type, to intrinsic semiconducting depending on the growth conditions. Our studies provided important guidance for experiments to fabricate Pb-free perovskite-based solar cell devices with superior PV performances.

  17. Dielectric response and pyroelectric properties of lead-free ferroelectric Ba3(VO42

    Directory of Open Access Journals (Sweden)

    Biswajit Pati

    2015-03-01

    Full Text Available The current paper presents results of dielectric response, pyroelectric behavior and conductivity study of lead-free ferroelectric barium orthovanadate (Ba3(VO42 or Ba3V2O8 ceramic, for a wide range of temperature and frequency. An X-ray diffraction study suggests the formation of a single-phase compound in trigonal crystal system. The SEM micrograph of gold-coated pellet sample shows well-defined and homogeneous morphology. Detailed studies of dielectric parameters (εr and tan δ of the compound as a function of temperature and frequency reveal their independence over a wide range of temperature and frequency. The nature of Polarization versus electric field (P–E hysteresis loop of Ba3V2O8 at room temperature suggests its ferroelectric nature. The temperature dependence of pyroelectric coefficient and figure of merits of the sample support its dielectric response. The nature of variation of dc conductivity with temperature confirms the Arrhenius and negative temperature coefficient of resistance (NTCR behavior of the material.

  18. Electrical properties and temperature stability of a new kind of lead-free piezoelectric ceramics

    International Nuclear Information System (INIS)

    Wang Yuanyu; Wu Jiagang; Xiao Dingquan; Zhang Bin; Wu Wenjuan; Shi Wei; Zhu Jianguo

    2008-01-01

    0.995[(K 0.50 Na 0.50 ) 0.94 Li 0.06 ]NbO 3 -0.005AETiO 3 (AE=Ca, Sr, Mg, Ba) lead-free piezoelectric ceramics were prepared by normal sintering. The effects of the AETiO 3 and poling temperature on the electrical properties of the ceramics were carefully studied, and the temperature stability of the electrical properties of the ceramics was also investigated. The experimental results show that the ceramics with Li and CaTiO 3 possess the pure phase, Li and AETiO 3 improves the electrical properties of the pure (K 0.50 Na 0.50 )NbO 3 ceramics, the poling temperature near tetragonal and orthorhombic phase transition will enhance the piezoelectric properties of the ceramics and the KNLN-CT ceramics exhibit good temperature stability of electrical properties for tetragonal and orthorhombic phase transition below room temperature. The KNLN-CT ceramics exhibit relatively good properties: d 33 = 172 pC N -1 , k p = 0.43, tan δ = 0.032, ε r = 771 and T c = 465 deg. C. As a result, the KNLN-CT ceramic is promising candidate material for piezoelectric devices.

  19. Self-lubricating tribological characterization of lead free Fe-Cu based plain bearing material

    Directory of Open Access Journals (Sweden)

    Shuhaib Mushtaq

    2017-03-01

    Full Text Available The negative impact of lead on environment and thereby its reciprocity on the health of mankind, there is a growing emphasis on resisting the usage of lead in bearings. Owing to this, new bearing materials that provide comparable tribological performance to that of lead containing alloys are being developed. In this study, lead free Fe-Cu based powders with addition of elements such as tin, molybdenum disulfide and Nano boron nitride (BN have been developed by powder metallurgy (PM technique in order to improve the tribological and mechanical properties. The powder mixtures were compressed at a pressure of 500 MPa, and then sintered in dry hydrogen atmosphere at 9000C for 50 minutes. The mechanical and tribological properties obtained due to addition of the said elements is presented in this study. The tribological behavior of the selected alloys is analyzed by reciprocating-sliding tests under dry conditions. The morphology of wear scars and the microstructure of the wear surfaces were investigated. The material with 2.5 wt.% of Sn exhibited the highest value of hardness, the material with 7.5 wt.% of Nano BN comparably shows the low coefficient of friction and wear rate as compared with 5 wt.% of Nano BN.

  20. An intrinsic approach to forces in magnetoelectric media

    International Nuclear Information System (INIS)

    Tucker, R.W.; Walton, T.J.

    2009-01-01

    This paper offers a conceptually straightforward method for the calculation of stresses in polarisable media based on the notion of a drive form and its property of being closed in spacetimes with symmetry. After an outline of the notation required to exploit the powerful exterior calculus of differential forms, a discussion of the relation between Killing isometries and conservation laws for smooth and distributional drive forms is given. Instantaneous forces on isolated spacetime domains and regions with interfaces are defined, based on manifestly covariant equations of motion. The remaining sections apply these notions to media that sustain electromagnetic stresses, with emphasis on homogeneous magnetoelectric material. An explicit calculation of the average pressure exerted by a monochromatic wave normally incident on a homogeneous, magnetoelectric slab in vacuo is presented and the concluding section summarizes how this pressure depends on the parameters in the magnetoelectric tensors for the medium.

  1. Inverse bilayer magnetoelectric thin film sensor

    Energy Technology Data Exchange (ETDEWEB)

    Yarar, E.; Piorra, A.; Quandt, E., E-mail: eq@tf.uni-kiel.de [Chair for Inorganic Functional Materials, Institute for Materials Science, Faculty of Engineering, Kiel University, Kaiserstraße 2, D-24143 Kiel (Germany); Salzer, S.; Höft, M.; Knöchel, R. [Microwave Laboratory, Institute of Electrical and Information Engineering, Faculty of Engineering, Kiel University, Kaiserstraße 2, D-24143 Kiel (Germany); Hrkac, V.; Kienle, L. [Chair for Synthesis and Real Structure, Institute for Materials Science, Faculty of Engineering, Kiel University, Kaiserstraße 2, D-24143 Kiel (Germany)

    2016-07-11

    Prior investigations on magnetoelectric (ME) thin film sensors using amorphous FeCoSiB as a magnetostrictive layer and AlN as a piezoelectric layer revealed a limit of detection (LOD) in the range of a few pT/Hz{sup 1/2} in the mechanical resonance. These sensors are comprised of a Si/SiO{sub 2}/Pt/AlN/FeCoSiB layer stack, as dictated by the temperatures required for the deposition of the layers. A low temperature deposition route of very high quality AlN allows the reversal of the deposition sequence, thus allowing the amorphous FeCoSiB to be deposited on the very smooth Si substrate. As a consequence, the LOD could be enhanced by almost an order of magnitude reaching 400 fT/Hz{sup 1/2} at the mechanical resonance of the sensor. Giant ME coefficients (α{sub ME}) as high as 5 kV/cm Oe were measured. Transmission electron microscopy investigations revealed highly c-axis oriented growth of the AlN starting from the Pt-AlN interface with local epitaxy.

  2. Unidirectional magnetoelectric-field multiresonant tunneling

    International Nuclear Information System (INIS)

    Kamenetskii, E O; Hollander, E; Joffe, R; Shavit, R

    2015-01-01

    Unidirectional multi-resonant tunneling of the magnetoelectric (ME) field excitations through a subwavelength (regarding the scales of regular electromagnetic radiation) vacuum or isotropic-dielectric regions has been observed in two-port microwave structures having a quasi-2D ferrite disk with magnetic dipolar mode (MDM) oscillations. The excitations manifest themselves as Fano-resonance peaks in the scattering-matrix parameters at the stationary states of the MDM spectrum. The ME near-field excitations are quasimagnetostatic fields ∇-vector × H-vector =0 with non-zero helicity parameter: F=(1/(16π))Im{ E-vector ⋅( ∇-vector × E-vector ) ∗ }. Topological phase properties of ME fields are determined by edge chiral currents of MDM oscillations. We show that while for a given direction of a bias magnetic field (in other words, for a given direction of time), the ME field excitations are considered as ‘forward’ tunneling processes, in the opposite direction of a bias magnetic field (the opposite direction of time), there are ‘backward’ tunneling processes. Unidirectional ME field resonant tunneling is observed due to the distinguishable topology of the ‘forward’ and ‘backward’ ME field excitations. We establish a close connection between the Fano-resonance unidirectional tunneling and the topology of the ME fields in different microwave structures. (paper)

  3. Magnetoelectric polymer-based composites fundamentals and applications

    CERN Document Server

    Martins, Pedro

    2017-01-01

    The first book on this topic provides a comprehensive and well-structured overview of the fundamentals, synthesis and emerging applications of magnetoelectric polymer materials. Following an introduction to the basic aspects of polymer based magnetoelectric materials and recent developments, subsequent chapters discuss the various types as well as their synthesis and characterization. There then follows a review of the latest applications, such as memories, sensors and actuators. The book concludes with a look at future technological advances. An essential reference for entrants to the field as well as for experienced researchers.

  4. Artificial immune system for effective properties optimization of magnetoelectric composites

    Science.gov (United States)

    Poteralski, Arkadiusz; Dziatkiewicz, Grzegorz

    2018-01-01

    The optimization problem of the effective properties for magnetoelectric composites is considered. The effective properties are determined by the semi-analytical Mori-Tanaka approach. The generalized Eshelby tensor components are calculated numerically by using the Gauss quadrature method for the integral representation of the inclusion problem. The linear magnetoelectric constitutive equation is used. The effect of orientation of the electromagnetic materials components is taken into account. The optimization problem of the design is formulated and the artificial immune system is applied to solve it.

  5. Electric field-induced magnetoresistance in spin-valve/piezoelectric multiferroic laminates for low-power spintronics

    International Nuclear Information System (INIS)

    Huong Giang, D.T.; Thuc, V.N.; Duc, N.H.

    2012-01-01

    Electric field-induced magnetic anisotropy has been realized in the spin-valve-based {Ni 80 Fe 20 /Cu/Fe 50 Co 50 /IrMn}/piezoelectric multiferroic laminates. In this system, electric-field control of magnetization is accomplished by strain mediated magnetoelectric coupling. Practically, the magnetization in the magnetostrictive FeCo layer of the spin-valve structure rotates under an effective compressive stress caused by the inverse piezoelectric effect in external electrical fields. This phenomenon is evidenced by the magnetization and magnetoresistance changes under the electrical field applied across the piezoelectric layer. The result shows great potential for advanced low-power spintronic devices. - Highlights: ► Investigate electric field-induced magnetic anisotropy in spin-valve/piezoelectric. ► Magnetization, magnetoresistance changes under electric field across piezoelectric. ► Magnetization in magnetostrictive FeCo-layer rotates under a compressive stress. ► This advance shows great implications for low-power electronics and spintronics.

  6. Conduction at domain walls in oxide multiferroics

    Science.gov (United States)

    Seidel, J.; Martin, L. W.; He, Q.; Zhan, Q.; Chu, Y.-H.; Rother, A.; Hawkridge, M. E.; Maksymovych, P.; Yu, P.; Gajek, M.; Balke, N.; Kalinin, S. V.; Gemming, S.; Wang, F.; Catalan, G.; Scott, J. F.; Spaldin, N. A.; Orenstein, J.; Ramesh, R.

    2009-03-01

    Domain walls may play an important role in future electronic devices, given their small size as well as the fact that their location can be controlled. Here, we report the observation of room-temperature electronic conductivity at ferroelectric domain walls in the insulating multiferroic BiFeO3. The origin and nature of the observed conductivity are probed using a combination of conductive atomic force microscopy, high-resolution transmission electron microscopy and first-principles density functional computations. Our analyses indicate that the conductivity correlates with structurally driven changes in both the electrostatic potential and the local electronic structure, which shows a decrease in the bandgap at the domain wall. Additionally, we demonstrate the potential for device applications of such conducting nanoscale features.

  7. Potassium Sodium Niobate-Based Lead-Free Piezoelectric Multilayer Ceramics Co-Fired with Nickel Electrodes

    Directory of Open Access Journals (Sweden)

    Shinichiro Kawada

    2015-11-01

    Full Text Available Although lead-free piezoelectric ceramics have been extensively studied, many problems must still be overcome before they are suitable for practical use. One of the main problems is fabricating a multilayer structure, and one solution attracting growing interest is the use of lead-free multilayer piezoelectric ceramics. The paper reviews work that has been done by the authors on lead-free alkali niobate-based multilayer piezoelectric ceramics co-fired with nickel inner electrodes. Nickel inner electrodes have many advantages, such as high electromigration resistance, high interfacial strength with ceramics, and greater cost effectiveness than silver palladium inner electrodes. However, widely used lead zirconate titanate-based ceramics cannot be co-fired with nickel inner electrodes, and silver palladium inner electrodes are usually used for lead zirconate titanate-based piezoelectric ceramics. A possible alternative is lead-free ceramics co-fired with nickel inner electrodes. We have thus been developing lead-free alkali niobate-based multilayer ceramics co-fired with nickel inner electrodes. The normalized electric-field-induced thickness strain (Smax/Emax of a representative alkali niobate-based multilayer ceramic structure with nickel inner electrodes was 360 pm/V, where Smax denotes the maximum strain and Emax denotes the maximum electric field. This value is about half that for the lead zirconate titanate-based ceramics that are widely used. However, a comparable value can be obtained by stacking more ceramic layers with smaller thicknesses. In the paper, the compositional design and process used to co-fire lead-free ceramics with nickel inner electrodes are introduced, and their piezoelectric properties and reliabilities are shown. Recent advances are introduced, and future development is discussed.

  8. Efficient Lead-Free Solar Cells Based on Hollow {en}MASnI3 Perovskites.

    Science.gov (United States)

    Ke, Weijun; Stoumpos, Constantinos C; Spanopoulos, Ioannis; Mao, Lingling; Chen, Michelle; Wasielewski, Michael R; Kanatzidis, Mercouri G

    2017-10-18

    Tin-based perovskites have very comparable electronic properties to lead-based perovskites and are regarded as possible lower toxicity alternates for solar cell applications. However, the efficiency of tin-based perovskite solar cells is still low and they exhibit poor air stability. Here, we report lead-free tin-based solar cells with greatly enhanced performance and stability using so-called "hollow" ethylenediammonium and methylammonium tin iodide ({en}MASnI 3 ) perovskite as absorbers. Our results show that en can improve the film morphology and most importantly can serve as a new cation to be incorporated into the 3D MASnI 3 lattice. When the cation of en becomes part of the 3D structure, a high density of SnI 2 vacancies is created resulting in larger band gap, larger unit cell volume, lower trap-state density, and much longer carrier lifetime compared to classical MASnI 3 . The best-performing {en}MASnI 3 solar cell has achieved a high efficiency of 6.63% with an open circuit voltage of 428.67 mV, a short-circuit current density of 24.28 mA cm -2 , and a fill factor of 63.72%. Moreover, the {en}MASnI 3 device shows much better air stability than the neat MASnI 3 device. Comparable performance is also achieved for cesium tin iodide solar cells with en loading, demonstrating the broad scope of this approach.

  9. Extending lead-free hybrid photovoltaic materials to new structures: thiazolium, aminothiazolium and imidazolium iodobismuthates.

    Science.gov (United States)

    Li, Tianyue; Wang, Qifei; Nichol, Gary S; Morrison, Carole A; Han, Hongwei; Hu, Yue; Robertson, Neil

    2018-05-09

    We report on the synthesis, crystal structures, optoelectronic properties and solar cell device studies of three novel organic-inorganic iodobismuthates - [C3H4NS]3[Bi2I9] ([TH]3[Bi2I9]), [C3H4N2]3[Bi2I9] ([IM]3[Bi2I9]) and [C3H5N2S][BiI4] ([AT][BiI4]) as lead-free light harvesters. [TH]3[Bi2I9] and [IM]3[Bi2I9] show zero-dimensional structures, whereas a one-dimensional edge-sharing chain structure of BiI6-octahedra was observed in [AT][BiI4], with interchain short II contacts also giving rise to the possibility of three-dimensional charge transport ability. Accordingly, greater energy dispersion in the band structure of [AT][BiI4] can be observed, and less contribution from the organic moities at the conduction band minimum in [AT][BiI4] than [TH]3[Bi2I9] have been confirmed by density functional theory calculations. Moreover, bandgap values are redshifted from 2.08 eV for [TH]3[Bi2I9] and 2.00 eV for [IM]3[Bi2I9] to 1.78 eV for [AT][BiI4], determined by UV-Vis reflectance spectroscopy. Power conversion efficiency of 0.47% has been achieved by using ([AT][BiI4]) as the light absorber in a hole-conductor-free, fully printable solar cell, with relatively good reproducibility. We also note the observation of a capacitance effect for the first time in a photovoltaic device with bismuth-based solar absorber, which may be related to the mesoporous carbon counter-electrode.

  10. Effect of phosphorus element on the comprehensive properties of Sn-Cu lead-free solder

    International Nuclear Information System (INIS)

    Li Guangdong; Shi Yaowu; Hao Hu; Xia Zhidong; Lei Yongping; Guo Fu

    2010-01-01

    In the present work, the effect of phosphorus on the creep fatigue properties of Sn-Cu eutectic lead-free solder was carried out. The experimental results show that the melting temperature was almost not changed with adding small amount of P element. However, the addition of trace P element led to the decrease in the property of creep fatigue. The fractography analysis by a scanning electron microscopy (SEM) shows that ductile fracture was the dominant failure behavior in the process of creep fatigue test of Sn0.7Cu and Sn0.7Cu0.005P specimens. It should be pointed out that there is significant difference in the fractographs between the joints of Sn0.7Cu solder and Sn0.7Cu0.005P solder. In the fractograph of Sn0.7Cu solder joint, the microstructure is prolonged along testing direction, and the dimples were more than the fractograph of Sn0.7Cu0.005P solder joint. In addition, the voids could be found on the Sn0.7Cu0.005P solder joint, and trace P addition may increase the rate of forming void of Sn0.7Cu solder joint. The voids can potentially lead to crack initiation or propagation sites in the solder joint. As a result, the creep fatigue of solder joint containing P such as Sn0.7Cu0.005P offers worse property compared to Sn0.7Cu solder joint.

  11. Lead-Free MA2CuCl(x)Br(4-x) Hybrid Perovskites.

    Science.gov (United States)

    Cortecchia, Daniele; Dewi, Herlina Arianita; Yin, Jun; Bruno, Annalisa; Chen, Shi; Baikie, Tom; Boix, Pablo P; Grätzel, Michael; Mhaisalkar, Subodh; Soci, Cesare; Mathews, Nripan

    2016-02-01

    Despite their extremely good performance in solar cells with efficiencies approaching 20% and the emerging application for light-emitting devices, organic-inorganic lead halide perovskites suffer from high content of toxic, polluting, and bioaccumulative Pb, which may eventually hamper their commercialization. Here, we present the synthesis of two-dimensional (2D) Cu-based hybrid perovskites and study their optoelectronic properties to investigate their potential application in solar cells and light-emitting devices, providing a new environmental-friendly alternative to Pb. The series (CH3NH3)2CuCl(x)Br(4-x) was studied in detail, with the role of Cl found to be essential for stabilization. By exploiting the additional Cu d-d transitions and appropriately tuning the Br/Cl ratio, which affects ligand-to-metal charge transfer transitions, the optical absorption in this series of compounds can be extended to the near-infrared for optimal spectral overlap with the solar irradiance. In situ formation of Cu(+) ions was found to be responsible for the green photoluminescence of this material set. Processing conditions for integrating Cu-based perovskites into photovoltaic device architectures, as well as the factors currently limiting photovoltaic performance, are discussed: among them, we identified the combination of low absorption coefficient and heavy mass of the holes as main limitations for the solar cell efficiency. To the best of our knowledge, this is the first demonstration of the potential of 2D copper perovskite as light harvesters and lays the foundation for further development of perovskite based on transition metals as alternative lead-free materials. Appropriate molecular design will be necessary to improve the material's properties and solar cell performance filling the gap with the state-of-the-art Pb-based perovskite devices.

  12. Fluxless flip-chip bonding using a lead-free solder bumping technique

    Science.gov (United States)

    Hansen, K.; Kousar, S.; Pitzl, D.; Arab, S.

    2017-09-01

    With the LHC exceeding the nominal instantaneous luminosity, the current barrel pixel detector (BPIX) of the CMS experiment at CERN will reach its performance limits and undergo significant radiation damage. In order to improve detector performance in high luminosity conditions, the entire BPIX is replaced with an upgraded version containing an additional detection layer. Half of the modules comprising this additional layer are produced at DESY using fluxless and lead-free bumping and bonding techniques. Sequential solder-jetting technique is utilized to wet 40-μm SAC305 solder spheres on the silicon-sensor pads with electroless Ni, Pd and immersion Au (ENEPIG) under-bump metallization (UBM). The bumped sensors are flip-chip assembled with readout chips (ROCs) and then reflowed using a flux-less bonding facility. The challenges for jetting low solder volume have been analyzed and will be presented in this paper. An average speed of 3.4 balls per second is obtained to jet about 67 thousand solder balls on a single chip. On average, 7 modules have been produced per week. The bump-bond quality is evaluated in terms of electrical and mechanical properties. The peak-bump resistance is about 17.5 mΩ. The cross-section study revealed different types of intermetallic compounds (IMC) as a result of interfacial reactions between UBM and solder material. The effect of crystalline phases on the mechanical properties of the joint is discussed. The mean shear strength per bump after the final module reflow is about 16 cN. The results and sources of yield loss of module production are reported. The achieved yield is 95%.

  13. Pyroelectric and dielectric properties of lead-free ferroelectric Ba3Nb2O8 ceramic

    International Nuclear Information System (INIS)

    Pati, Biswajit; Choudhary, R.N.P.; Das, Piyush R.; Parida, B.N.; Padhee, R.

    2014-01-01

    Graphical abstract: - Highlights: • Barium orthoniobate (lead-free perovskite) crystallizes as palmierite with structural stability. • The material exhibits ferroelectric phase transition of diffuse-type suitable for devices. • The low values of ε r and tan δ at high frequencies makes it a potential candidate for microwave applications. • The material has very good pyroelectric properties for detector application. • The material exhibits smaller value of dc activation energy. - Abstract: The present study highlights ferroelectric phase transition, dielectric, pyroelectric properties and conduction mechanism of highly crystallized barium orthoniobate (Ba 3 Nb 2 O 8 ) ceramic, prepared by a solid-state reaction technique. X-ray diffraction studies show the formation of a single-phase compound in hexagonal crystal system. Detailed studies of dielectric parameters (ε r and tan δ) of the compound as a function of temperature and frequency reveal their independence over a wide range of temperature and frequency. An anomaly in ε r suggests the possible existence of a ferroelectric–paraelectric phase transition of diffuse-type in the material. The low dielectric loss and moderate relative permittivity make this material (with certain modification) a potential candidate for microwave applications. Studies of pyroelectric properties reveal that the materials have reasonably high figure of merit useful for fabrication of pyroelectric detectors. The low-leakage current and negative temperature coefficient of resistance (NTCR) behavior of the sample have been verified from J–E plots. The nature of variation of dc conductivity with temperature confirms the Arrhenius and NTCR behavior of the material

  14. Effect of phosphorus element on the comprehensive properties of Sn-Cu lead-free solder

    Energy Technology Data Exchange (ETDEWEB)

    Li Guangdong, E-mail: liguangdong@emails.bjut.edu.c [College of Materials Science and Engineering, Beijing University of Technology, 100 Ping Le Yuan, Chaoyang District, Beijing 100124 (China); Shi Yaowu; Hao Hu; Xia Zhidong; Lei Yongping; Guo Fu [College of Materials Science and Engineering, Beijing University of Technology, 100 Ping Le Yuan, Chaoyang District, Beijing 100124 (China)

    2010-02-18

    In the present work, the effect of phosphorus on the creep fatigue properties of Sn-Cu eutectic lead-free solder was carried out. The experimental results show that the melting temperature was almost not changed with adding small amount of P element. However, the addition of trace P element led to the decrease in the property of creep fatigue. The fractography analysis by a scanning electron microscopy (SEM) shows that ductile fracture was the dominant failure behavior in the process of creep fatigue test of Sn0.7Cu and Sn0.7Cu0.005P specimens. It should be pointed out that there is significant difference in the fractographs between the joints of Sn0.7Cu solder and Sn0.7Cu0.005P solder. In the fractograph of Sn0.7Cu solder joint, the microstructure is prolonged along testing direction, and the dimples were more than the fractograph of Sn0.7Cu0.005P solder joint. In addition, the voids could be found on the Sn0.7Cu0.005P solder joint, and trace P addition may increase the rate of forming void of Sn0.7Cu solder joint. The voids can potentially lead to crack initiation or propagation sites in the solder joint. As a result, the creep fatigue of solder joint containing P such as Sn0.7Cu0.005P offers worse property compared to Sn0.7Cu solder joint.

  15. Life cycle assessment (LCA of lead-free solders from the environmental protection aspect

    Directory of Open Access Journals (Sweden)

    Mitovski Aleksandra M.

    2009-01-01

    Full Text Available Life-cycle assessment (LCA presents a relatively new approach, which allows comprehensive environmental consequences analysis of a product system over its entire life. This analysis is increasingly being used in the industry, as a tool for investigation of the influence of the product system on the environment, and serves as a protection and prevention tool in ecological management. This method is used to predict possible influences of a certain material to the environment through different development stages of the material. In LCA, the product systems are evaluated on a functionally equivalent basis, which, in this case, was 1000 cubic centimeters of an alloy. Two of the LCA phases, life-cycle inventory (LCA and life-cycle impact assessment (LCIA, are needed to calculate the environmental impacts. Methodology of LCIA applied in this analysis aligns every input and output influence into 16 different categories, divided in two subcategories. The life-cycle assessment reaserch review of the leadfree solders Sn-Cu, SAC (Sn-Ag-Cu, BSA (Bi-Sb-Ag and SABC (Sn-Ag-Bi-Cu respectively, is given in this paper, from the environmental protection aspect starting from production, through application process and finally, reclamation at the end-of-life, i.e. recycling. There are several opportunities for reducing the overall environmental and human health impacts of solder used in electronics manufacturing based on the results of the LCA, such as: using secondary metals reclaimed through post-industrial recycling; power consumption reducing by replacing older, less efficient reflow assembly equipment, or by optimizing the current equipment to perform at the elevated temperatures required for lead-free soldering, etc. The LCA analysis was done comparatively in relation to widely used Sn-Pb solder material. Additionally, the impact factors of material consumption, energy use, water and air reserves, human health and ecotoxicity have been ALSO considered including

  16. Magnetoelectric coupling of a magnetoelectric flux gate sensor in vibration noise circumstance

    Directory of Open Access Journals (Sweden)

    Zhaoqiang Chu

    2018-01-01

    Full Text Available A magnetoelectric (ME flux gate sensor (MEFGS consisting of piezoelectric PMN-PT single crystals and ferromagnetic amorphous alloy ribbon in a self-differential configuration is featured with the ability of weak magnetic anomaly detection. Here, we further investigated its ME coupling and magnetic field detection performance in vibration noise circumstance, including constant frequency, impact, and random vibration noise. Experimental results show that the ME coupling coefficient of MEFGS is as high as 5700 V/cm*Oe at resonant frequency, which is several orders magnitude higher than previously reported differential ME sensors. It was also found that under constant and impact vibration noise circumstance, the noise reduction and attenuation factor of MEFGS are over 17 and 85.7%, respectively. This work is important for practical application of MEFGS in real environment.

  17. In-situ Investigation of Lead-free Solder Alloy Formation Using a Hot-plate Microscope

    DEFF Research Database (Denmark)

    Bergmann, René; Tang, Peter Torben; Hansen, Hans Nørgaard

    2007-01-01

    This work presents the advantages of using a hot-plate microscope for investigation of new (high-temperature) lead- free solders as in-situ analysis tool and preparation equipment. A description of the equipment and the preparation method is given and some examples are outlined. The formation...

  18. Transmission electron microscopy investigation of the microstructural mechanisms for the piezoelectricity in lead-free perovskite ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Ma, Cheng [Iowa State Univ., Ames, IA (United States)

    2012-01-01

    Lead-free materials with superior piezoelectricity are in increasingly urgent demand in the current century, because the industrial standard Pb(Zr,Ti)O3-based piezoelectrics, which contain over 60 weight% of the toxic element lead, pose severe environmental hazards. Although significant research efforts have been devoted in the past decade, no effective lead-free substitute for Pb(Zr,Ti)O3 has been identified yet. One of the primary hindrances to the development of lead-free piezoelectrics lies in the ignorance of the microstructural mechanism for the electric-field-induced strains in the currently existing compositions. In this dissertation, the microstructural origin for the high piezoelectricity in (1-x)(Bi1/2Na1/2)TiO3-xBaTiO3 [(1-x)BNT-xBT], the most widely studied lead-free piezoelectric system, has been elucidated.

  19. Magnetoelectric coupling in layered LSMO/PZT nanostructures

    International Nuclear Information System (INIS)

    Leufke, Philipp M.

    2014-01-01

    Multiferroic thin film composites with electric field-effect driven magnetoelectric (ME) coupling offer the possibility to reversibly tune magnetic properties in materials intended for device applications. The structural and functional versatility of such artificial heterostructures makes them attractive not only for various data processing, storage and sensor applications but also for studying the fundamental ME coupling mechanisms. La 1-x Sr x MnO 3 (LSMO)/PbZr y Ti 1-y O 3 (PZT) is an ideal choice for such a composite, combining the unrivaled ferroelectric (FE) properties of PZT with the multiple electronic and magnetic phenomena exhibited by the mixed valency manganite LSMO. The main physical feature used in realization of the LSMO/PZT ME composites is a striking sensitivity of LSMO magnetism to the charge carrier density. Here, the low-doping region is of particular interest, where the competition between the fundamental magnetic coupling mechanisms, Double-Exchange (DE) versus Superexchange (SE), is most distinctive. In the present work an unconventional sputtering technique - the Large-Distance Magnetron Sputtering (LDMS) method - has been established, which allowed for epitaxial deposition of these heterostructures with highest crystallinity and markedly smooth interfaces, necessary for effective field-effect control of magnetism. The large target-substrate distance effectively suppressed the destructive oxygen ion bombardment, inherently connected with oxide sputtering, and yielded an outstanding lateral uniformity of the film stack. The latter was vital for the fabrication of large capacitor structures of several square millimeter area that were required for detecting the ME coupling in a Superconductive Quantum Interference Device (SQUID) magnetometer. The growth of LSMO on various single crystalline substrates was mastered by exploring a vast deposition parameter space, encompassing Radio Frequency (RF) and Direct Current (DC) sputtering. Commensurately

  20. Magnetoelectric coupling in layered LSMO/PZT nanostructures

    Energy Technology Data Exchange (ETDEWEB)

    Leufke, Philipp M.

    2014-01-29

    Multiferroic thin film composites with electric field-effect driven magnetoelectric (ME) coupling offer the possibility to reversibly tune magnetic properties in materials intended for device applications. The structural and functional versatility of such artificial heterostructures makes them attractive not only for various data processing, storage and sensor applications but also for studying the fundamental ME coupling mechanisms. La{sub 1-x}Sr{sub x}MnO{sub 3} (LSMO)/PbZr{sub y}Ti{sub 1-y}O{sub 3} (PZT) is an ideal choice for such a composite, combining the unrivaled ferroelectric (FE) properties of PZT with the multiple electronic and magnetic phenomena exhibited by the mixed valency manganite LSMO. The main physical feature used in realization of the LSMO/PZT ME composites is a striking sensitivity of LSMO magnetism to the charge carrier density. Here, the low-doping region is of particular interest, where the competition between the fundamental magnetic coupling mechanisms, Double-Exchange (DE) versus Superexchange (SE), is most distinctive. In the present work an unconventional sputtering technique - the Large-Distance Magnetron Sputtering (LDMS) method - has been established, which allowed for epitaxial deposition of these heterostructures with highest crystallinity and markedly smooth interfaces, necessary for effective field-effect control of magnetism. The large target-substrate distance effectively suppressed the destructive oxygen ion bombardment, inherently connected with oxide sputtering, and yielded an outstanding lateral uniformity of the film stack. The latter was vital for the fabrication of large capacitor structures of several square millimeter area that were required for detecting the ME coupling in a Superconductive Quantum Interference Device (SQUID) magnetometer. The growth of LSMO on various single crystalline substrates was mastered by exploring a vast deposition parameter space, encompassing Radio Frequency (RF) and Direct Current (DC

  1. SU-E-P-09: Radiation Transmission Measurements and Evaluation of Diagnostic Lead-Based and Lead-Free Aprons

    Energy Technology Data Exchange (ETDEWEB)

    Syh, J [Willis-Knighton Medical Center, Shreveport, LA (United States)

    2014-06-01

    Purpose: This study was conducted to ensure that various lead shield apron manufacturers provided accurate attenuation factors regardless of whether the apron was made of lead-based or lead-free equivalent material. Methods: A calibrated ionization survey meter was placed at chest height and 36 cm horizontally away from a solid water phantom on a simulator couch. Measurements were done with or without apron. Radiation field was set to 24cmx24cm with the phantom at 100cm source-to-surface distance. Irradiation time was set for 1 minute at voltages of 60, 80, 100 and 120 kVp. Current was set at 6mA. Results: Between 60 kVp and 120 kVp, the transmission through 0.50 mm of lead-based apron was between 1.0% and 6.5% with a mean value of 3.2% and a standard deviation (s.d.) of 1.4%. The transmissions through the 0.50 mm lead-free aprons were 1.0 % to 12.0% with a mean value of 6.1% and s.d. of 2.6%. At 120 kVp, the transmission value was 6.5% for 0.50 mm lead-based apron and 11.1% to 12.0% for 0.50 mm lead-free aprons. The radiation transmissions at 80 kVp, measured in two different 0.5 mm lead-free aprons, were 4.3% each. However, only 1.4% transmission was found through the lead-based apron. Overall, the radiation transmitted through the lead-based apron was 1/3 transmission of lead-free at 80kVp, and half value of lead-free aprons at 100 and 120 kVp. Conclusion: Even though lead-based and lead-free aprons all claimed to have the same lead equivalent thickness, the transmission might not be the same. The precaution was needed to exercise diligence in quality assurance program to assure adequate protection to staff who wear it during diagnostic procedures. The requirement for aprons not only should be in certain thickness to meet state regulation but also to keep reasonably achievable low exposure with the accurate labeling from manufacturers.

  2. SU-E-P-09: Radiation Transmission Measurements and Evaluation of Diagnostic Lead-Based and Lead-Free Aprons

    International Nuclear Information System (INIS)

    Syh, J

    2014-01-01

    Purpose: This study was conducted to ensure that various lead shield apron manufacturers provided accurate attenuation factors regardless of whether the apron was made of lead-based or lead-free equivalent material. Methods: A calibrated ionization survey meter was placed at chest height and 36 cm horizontally away from a solid water phantom on a simulator couch. Measurements were done with or without apron. Radiation field was set to 24cmx24cm with the phantom at 100cm source-to-surface distance. Irradiation time was set for 1 minute at voltages of 60, 80, 100 and 120 kVp. Current was set at 6mA. Results: Between 60 kVp and 120 kVp, the transmission through 0.50 mm of lead-based apron was between 1.0% and 6.5% with a mean value of 3.2% and a standard deviation (s.d.) of 1.4%. The transmissions through the 0.50 mm lead-free aprons were 1.0 % to 12.0% with a mean value of 6.1% and s.d. of 2.6%. At 120 kVp, the transmission value was 6.5% for 0.50 mm lead-based apron and 11.1% to 12.0% for 0.50 mm lead-free aprons. The radiation transmissions at 80 kVp, measured in two different 0.5 mm lead-free aprons, were 4.3% each. However, only 1.4% transmission was found through the lead-based apron. Overall, the radiation transmitted through the lead-based apron was 1/3 transmission of lead-free at 80kVp, and half value of lead-free aprons at 100 and 120 kVp. Conclusion: Even though lead-based and lead-free aprons all claimed to have the same lead equivalent thickness, the transmission might not be the same. The precaution was needed to exercise diligence in quality assurance program to assure adequate protection to staff who wear it during diagnostic procedures. The requirement for aprons not only should be in certain thickness to meet state regulation but also to keep reasonably achievable low exposure with the accurate labeling from manufacturers

  3. Strong Nonvolatile Magnon-Driven Magnetoelectric Coupling in Single-Crystal Co /[PbMg1/3Nb2/3O3] 0.71[PbTiO3]0.29 Heterostructures

    Science.gov (United States)

    Zhou, Cai; Shen, Lvkang; Liu, Ming; Gao, Cunxu; Jia, Chenglong; Jiang, Changjun

    2018-01-01

    The ability to manipulate the magnetism on interfacing ferromagnetic and ferroelectric materials via electric fields to achieve an emergent multiferroic response has enormous potential for nanoscale devices with novel functionalities. Herein, a strong electric-field control of the magnetism modulation is reported for a single-crystal Co (14 nm )/(001 )Pb (Mg1/3Nb2/3) 0.7Ti0.3O3 (PMN-PT) heterostructure by fabricating an epitaxial Co layer on a PMN-PT substrate. Electric-field-tuned ferromagnetic resonance exhibits a large resonance field shift, with a 120-Oe difference between that under positive and negative remanent polarizations, which demonstrates nonvolatile electric-field control of the magnetism. Further, considering the complexity of the twofold symmetry magnetic anisotropy, the linear change of the fourfold symmetry magnetic anisotropy, relating to the single-crystal cubic magnetocrystal anisotropy of the Co thin film, is resolved and quantified to exert a magnon-driven, strong direct magnetoelectric effect on the Co /PMN -PT interface. These results are promising for future multiferroic devices.

  4. Orientation dependence of magnetoelectric coefficient in 1-3-type BaTiO3/CoFe2O4

    Science.gov (United States)

    Jian, Gang; Shao, Hui; Zhang, Cheng; Yan, Chao; Zhao, Ning; Song, Bo; Wong, C. P.

    2018-03-01

    Orientation dependence of magnetoelectric coefficient αE33 in 1-3-type BaTiO3/CoFe2O4 composites was calculated in arbitrary directions by three-dimensional coordinate transformation method. The space distributions of pc11‧, pc12‧, e31‧ for piezoelectric phase and mc11‧, mc12‧, q31‧ for magnetic phase were obtained independently using relative experimental data and original matrices for 4mm BaTiO3 and m3m CoFe2O4. Elastic stiffness coefficients show little orientation differences, while e31‧ and q31‧ exhibit high dependence on crystal orientation, with the MAX absolute e31‧ = 2.96 C/m2 and the MAX q31‧ = 556 × 10-12 m/A are found at θ = 0° and θ = 0°, ϕ = 45°, respectively. For space distribution of αE33‧, BaTiO3||[0 0 1]/CoFe2O4||[0 0 1] combination has the maximum value which applies to both 1-3 p/m (1.485 V/A) and 1-3 m/p composites (1.529 V/A). Volume fraction is quite independent of orientations of both piezoelectric and magnetic phases and the volume fraction for magnetic phase f around 0.5 obtains the largest αE33. The results suggest an approach to significantly enhancing magnetoelectric coefficient of composite multiferroic materials through crystal orientation controls of single crystals and textured ceramics.

  5. Room temperature large self-biased magnetoelectric effect in non-lead based piezoelectric and magnetostrictive (0−3) particulate composite system

    Energy Technology Data Exchange (ETDEWEB)

    Kumari, Mukesh [Magnetics & Advanced Ceramics Laboratory, Indian Institute of Technology, Delhi-110016 India (India); Prakash, Chandra [Solid State Physics Laboratory Timarpur, Delhi-110054 India (India); Chatterjee, Ratnamala, E-mail: rmala@physics.iitd.ac.in [Magnetics & Advanced Ceramics Laboratory, Indian Institute of Technology, Delhi-110016 India (India)

    2017-05-01

    In this work, room temperature magnetoelectric properties of (0−3) particulate composites of non lead based piezoelectric BNTKNNLTS [0.97(Bi{sub 0.5}Na{sub 0.5}TiO{sub 3})–0.03(K{sub 0.47}Na{sub 0.47}Li{sub 0.06}Nb{sub 0.74}Sb{sub 0.06}Ta{sub 0.2}O{sub 3}) and magnetostrictive CZFMO (Co{sub 0.6}Zn{sub 0.4}Fe{sub 1.7}Mn{sub 0.3}O{sub 4}) are presented. Composite samples of (1-x)(BNTKNNLTS)-x(CZFMO){sub ,} with x=0.1 and 0.5, are synthesized by solid state reaction route. X-ray diffraction confirms the single phase formation of parent phases and the presence of two phases in the composites. Similar sintering conditions of the two individual components lead to optimal ferroelectric and ferromagnetic properties in the composites. A large self-biased magnetoelectric (ME) coupling ~74 mV/cm.Oe for the sample with x=0.1 (measured in longitudinally magnetized-transversely polarized configuration) is observed at room temperature. - Highlights: • Modified BNT-CFO based (0−3) particulate composites have been synthesized. • Similar sintering conditions of two components lead to optimal multiferroicity. • A large self-biased ME coupling ~74 mV/cm. Oe is obtained at room temperature.

  6. Exploring Electric Polarization Mechanisms in Multiferroic Oxides

    Energy Technology Data Exchange (ETDEWEB)

    Tyson, Trevor A. [New Jersey Institute of Technology (NJIT), Newark, NJ (United States)

    2017-01-24

    Multiferroic oxides are a class of systems which exhibit coupling between the electrical polarization and the magnetization. These materials show promise to lead to devices in which ferromagnetic memory can be written with magnetic fields or magnetic bits can be written by an electric field. The work conducted in our research focuses on single phase materials. We studied the detailed coupling of the spin and lattice correlations in these systems. In the first phase of the proposal, we explored the complex spin spiral systems and low temperature behavior of hexagonal layered REMnO3 (RE= rare earth, Y and Sc) system following the detailed structural changes which occurred on crossing into the magnetic states. The techniques were applied to other layered materials such as superconductors and thermoelectric where the same layered motif exists. The second phase of the proposal focused on understanding the mechanisms involved in the onset high temperature ferroelectricity ion hexagonal REMnO3 and at low temperature in E-Type magnetic ordered perovskite REMnO3. We wsynthesized preovskite small A site multiferroics by high pressure and high temperature methods. Detailed measurement of the structural properties and dynamics were conducted over a range of length scales from atomic to mesoscopic scale using, x-ray absorption spectroscopy, x-ray diffuse scattering, x-ray and neutron pair distribution analysis and high resolution x-ray diffraction. Changes in vibration modes which occur with the onset of polarization were probed with temperature and pressure dependent infrared absorption spectroscopy. In addition the orthorhombic system (small radius RE ions) which is believed to exhibit electronically driven ferroelectricity and is also not understood was examined. The multiple length scale synchrotron based measurements may assist in developing more detailed models of these materials and possibly lead to device applications. The experimental

  7. Electromechanical properties of engineered lead free potassium sodium niobate based materials =

    Science.gov (United States)

    Rafiq, Muhammad Asif

    K0.5Na0.5NbO3 (KNN), is the most promising lead free material for substituting lead zirconate titanate (PZT) which is still the market leader used for sensors and actuators. To make KNN a real competitor, it is necessary to understand and to improve its properties. This goal is pursued in the present work via different approaches aiming to study KNN intrinsic properties and then to identify appropriate strategies like doping and texturing for designing better KNN materials for an intended application. Hence, polycrystalline KNN ceramics (undoped, non-stoichiometric; NST and doped), high-quality KNN single crystals and textured KNN based ceramics were successfully synthesized and characterized in this work. Polycrystalline undoped, non-stoichiometric (NST) and Mn doped KNN ceramics were prepared by conventional ceramic processing. Structure, microstructure and electrical properties were measured. It was observed that the window for mono-phasic compositions was very narrow for both NST ceramics and Mn doped ceramics. For NST ceramics the variation of A/B ratio influenced the polarization (P-E) hysteresis loop and better piezoelectric and dielectric responses could be found for small stoichiometry deviations (A/B = 0.97). Regarding Mn doping, as compared to undoped KNN which showed leaky polarization (P-E) hysteresis loops, B-site Mn doped ceramics showed a well saturated, less-leaky hysteresis loop and a significant properties improvement. Impedance spectroscopy was used to assess the role of Mn and a relation between charge transport - defects and ferroelectric response in K0.5Na0.5NbO3 (KNN) and Mn doped KNN ceramics could be established. At room temperature the conduction in KNN which is associated with holes transport is suppressed by Mn doping. Hence Mn addition increases the resistivity of the ceramic, which proved to be very helpful for improving the saturation of the P-E loop. At high temperatures the conduction is dominated by the motion of ionized oxygen

  8. NASA-DoD Lead-Free Electronics Project. DRAFT Joint Test Report

    Science.gov (United States)

    Kessel, Kurt

    2011-01-01

    The use of conventional tin-lead (SnPb) in circuit board manufacturing is under ever-increasing political scrutiny due to increasing regulations concerning lead. The "Restriction of Hazardous Substances" (RoHS) directive enacted by the European Union (EU) and a pact between the United States National Electronics Manufacturing Initiative (NEMI), Europe's Soldertec at Tin Technology Ltd. and the Japan Electronics and Information Technology Industries Association (JEITA) are just two examples where worldwide legislative actions and partnerships/agreements are affecting the electronics industry. As a result, many global commercial-grade electronic component suppliers are initiating efforts to transition to lead-free (Pb-free) in order to retain their worldwide market. Pb-free components are likely to find their way into the inventory of aerospace or military assembly processes under current government acquisition reform initiatives. Inventories "contaminated" by Pb-free will result in increased risks associated with the manufacturing, product reliability, and subsequent repair of aerospace and military electronic systems. Although electronics for military and aerospace applications are not included in the RoHS legislation, engineers are beginning to find that the commercial industry's move towards RoHS compliance has affected their supply chain and changed their parts. Most parts suppliers plan to phase out their non-compliant, leaded production and many have already done so. As a result, the ability to find leaded components is getting harder and harder. Some buyers are now attempting to acquire the remaining SnPb inventory, if it's not already obsolete. Original Equipment Manufacturers (OEMs), depots, and support contractors have to be prepared to deal with an electronics supply chain that increasingly provides more and more parts with Pb-free finishes-some labeled no differently than their Pb counterparts-while at the same time providing the traditional Pb parts

  9. Control of Chiral Magnetism Through Electric Fields in Multiferroic Compounds above the Long-Range Multiferroic Transition.

    Science.gov (United States)

    Stein, J; Baum, M; Holbein, S; Finger, T; Cronert, T; Tölzer, C; Fröhlich, T; Biesenkamp, S; Schmalzl, K; Steffens, P; Lee, C H; Braden, M

    2017-10-27

    Polarized neutron scattering experiments reveal that type-II multiferroics allow for controlling the spin chirality by external electric fields even in the absence of long-range multiferroic order. In the two prototype compounds TbMnO_{3} and MnWO_{4}, chiral magnetism associated with soft overdamped electromagnons can be observed above the long-range multiferroic transition temperature T_{MF}, and it is possible to control it through an electric field. While MnWO_{4} exhibits chiral correlations only in a tiny temperature interval above T_{MF}, in TbMnO_{3} chiral magnetism can be observed over several kelvin up to the lock-in transition, which is well separated from T_{MF}.

  10. Properties and Microstructures of Sn-Ag-Cu-X Lead-Free Solder Joints in Electronic Packaging

    Directory of Open Access Journals (Sweden)

    Lei Sun

    2015-01-01

    Full Text Available SnAgCu solder alloys were considered as one of the most popular lead-free solders because of its good reliability and mechanical properties. However, there are also many problems that need to be solved for the SnAgCu solders, such as high melting point and poor wettability. In order to overcome these shortcomings, and further enhance the properties of SnAgCu solders, many researchers choose to add a series of alloying elements (In, Ti, Fe, Zn, Bi, Ni, Sb, Ga, Al, and rare earth and nanoparticles to the SnAgCu solders. In this paper, the work of SnAgCu lead-free solders containing alloying elements and nanoparticles was reviewed, and the effects of alloying elements and nanoparticles on the melting temperature, wettability, mechanical properties, hardness properties, microstructures, intermetallic compounds, and whiskers were discussed.

  11. Fabrication of Radiation Shielding Glasses Based on Lead-free High Refractive Index Glasses Prepared from Local Sand

    International Nuclear Information System (INIS)

    Dararutana, Pisutti; Dutchaneepet, Jirapan; Sirikulrat, Narin

    2007-08-01

    Full text: Lead glasses that show high refractive index are the best know and most popular for radiation shielding. Due to harmful effects of lead and considering the health as well as the environmental issues, lead-free glasses were developed. In this work, content of Chumphon sand was fixed at 40 % (by weight) as a main composition but concentrations of BaCO3 were varied from 6 to 30 % (by weight). It was found that the absorption coefficient of the glass samples containing 30 % BaCO3 was 0.233 cm-1 for Ba-133. The density was also measured. It can be concluded that the prepared lead free glasses offered adequate shielding to gamma radiation in comparison with the lead ones. These glasses were one of the environmental friendly materials

  12. Self-assembly of multiferroic core-shell particulate nanocomposites through DNA-DNA hybridization and magnetic field directed assembly of superstructures

    Energy Technology Data Exchange (ETDEWEB)

    Sreenivasulu, Gollapudi; Srinivasan, Gopalan, E-mail: srinivas@oakland.edu, E-mail: chavez@oakland.edu [Department of Physics, Oakland University, Rochester, MI 48309-4401 (United States); Lochbiler, Thomas A.; Panda, Manashi; Chavez, Ferman A., E-mail: srinivas@oakland.edu, E-mail: chavez@oakland.edu [Department of Chemistry, Oakland University, Rochester, MI 48309-4401 (United States)

    2016-04-15

    Multiferroic composites of ferromagnetic and ferroelectric phases are of importance for studies on mechanical strain mediated coupling between the magnetic and electric subsystems. This work is on DNA-assisted self-assembly of superstructures of such composites with nanometer periodicity. The synthesis involved oligomeric DNA-functionalized ferroelectric and ferromagnetic nanoparticles, 600 nm BaTiO{sub 3} (BTO) and 200 nm NiFe{sub 2}O{sub 4} (NFO), respectively. Mixing BTO and NFO particles, possessing complementary DNA sequences, resulted in the formation of ordered core-shell heteronanocomposites held together by DNA hybridization. The composites were imaged by scanning electron microscopy and scanning microwave microscopy. The presence of heteroassemblies along with core-shell architecture is clearly observed. The reversible nature of the DNA hybridization allows for restructuring the composites into mm-long linear chains and 2D-arrays in the presence of a static magnetic field and ring-like structures in a rotating-magnetic field. Strong magneto-electric (ME) coupling in as-assembled composites is evident from static magnetic field H induced polarization and low-frequency magnetoelectric voltage coefficient measurements. Upon annealing the nanocomposites at high temperatures, evidence for the formation of bulk composites with excellent cross-coupling between the electric and magnetic subsystems is obtained by H-induced polarization and low-frequency ME voltage coefficient. The ME coupling strength in the self-assembled composites is measured to be much stronger than in bulk composites with randomly distributed NFO and BTO prepared by direct mixing and sintering.

  13. Colloidal Nanocrystals of Lead-Free Double-Perovskite (Elpasolite) Semiconductors: Synthesis and Anion Exchange To Access New Materials.

    Science.gov (United States)

    Creutz, Sidney E; Crites, Evan N; De Siena, Michael C; Gamelin, Daniel R

    2018-02-14

    Concerns about the toxicity and instability of lead-halide perovskites have driven a recent surge in research toward alternative lead-free perovskite materials, including lead-free double perovskites with the elpasolite structure and visible bandgaps. Synthetic approaches to this class of materials remain limited, however, and no examples of heterometallic elpasolites as nanomaterials have been reported. Here, we report the synthesis and characterization of colloidal nanocrystals of Cs 2 AgBiX 6 (X = Cl, Br) elpasolites using a hot-injection approach. We further show that postsynthetic modification through anion exchange and cation extraction can be used to convert these nanocrystals to new materials including Cs 2 AgBiI 6 , which was previously unknown experimentally. Nanocrystals of Cs 2 AgBiI 6 , synthesized via a novel anion-exchange protocol using trimethylsilyl iodide, have strong absorption throughout the visible region, confirming theoretical predictions that this material could be a promising photovoltaic absorber. The synthetic methodologies presented here are expected to be broadly generalizable. This work demonstrates that nanocrystal ion-exchange reactivity can be used to discover and develop new lead-free halide perovskite materials that may be difficult or impossible to access through direct synthesis.

  14. Lead-Free Hybrid Perovskite Absorbers for Viable Application: Can We Eat the Cake and Have It too?

    Science.gov (United States)

    Liang, Lusheng; Gao, Peng

    2018-02-01

    Many years since the booming of research on perovskite solar cells (PSCs), the hybrid perovskite materials developed for photovoltaic application form three main categories since 2009: (i) high-performance unstable lead-containing perovskites, (ii) low-performance lead-free perovskites, and (iii) moderate performance and stable lead-containing perovskites. The search for alternative materials to replace lead leads to the second group of perovskite materials. To date, a number of these compounds have been synthesized and applied in photovoltaic devices. Here, lead-free hybrid light absorbers used in PV devices are focused and their recent developments in related solar cell applications are reviewed comprehensively. In the first part, group 14 metals (Sn and Ge)-based perovskites are introduced with more emphasis on the optimization of Sn-based PSCs. Then concerns on halide hybrids of group 15 metals (Bi and Sb) are raised, which are mainly perovskite derivatives. At the same time, transition metal Cu-based perovskites are also referred. In the end, an outlook is given on the design strategy of lead-free halide hybrid absorbers for photovoltaic applications. It is believed that this timely review can represent our unique view of the field and shed some light on the direction of development of such promising materials.

  15. Composition-driven magnetic and structural phase transitions in Bi1-xPrxFe1-xMnxO3 multiferroics

    Science.gov (United States)

    Khomchenko, V. A.; Ivanov, M. S.; Karpinsky, D. V.; Paixão, J. A.

    2017-09-01

    Magnetic ferroelectrics continue to attract much attention as promising multifunctional materials. Among them, BiFeO3 is distinguished by exceptionally high transition temperatures and, thus, is considered as a prototype room-temperature multiferroic. Since its properties are known to be strongly affected by chemical substitution, recognition of the doping-related factors determining the multiferroic behavior of the material would pave the way towards designing the structures with enhanced magnetoelectric functionality. In this paper, we report on the crystal structure and magnetic and local ferroelectric properties of the Bi1-xPrxFe1-xMnxO3 (x ≤ 0.3) compounds prepared by a solid state reaction method. The polar R3c structure specific to the parent BiFeO3 has been found to be unstable with respect to doping for x ≳ 0.1. Depending on the Pr/Mn concentration, either the antipolar PbZrO3-like or nonpolar PrMnO3-type structure can be observed. It has been shown that the non-ferroelectric compounds are weak ferromagnetic with the remanent/spontaneous magnetization linearly decreasing with an increase in x. The samples containing the polar R3c phase exhibit a mixed antiferromagnetic/weak ferromagnetic behavior. The origin of the magnetic phase separation taking place in the ferroelectric phase is discussed as related to the local, doping-introduced structural heterogeneity contributing to the suppression of the cycloidal antiferromagnetic ordering characteristic of the pure BiFeO3.

  16. An analytical nonlinear magnetoelectric coupling model of laminated composites under combined pre-stress and magnetic bias loadings

    International Nuclear Information System (INIS)

    Zhou, Hao-Miao; Qu, Shao-Xing; Ou, Xiao-Wei; Xiao, Ying; Wu, Hua-Ping

    2013-01-01

    Based on the equivalent circuit method, this paper adopts the nonlinear magnetostrictive constitutive relations to establish an analytical nonlinear magnetoelectric coefficient model for magnetostrictive/piezoelectric/magnetostrictive laminated magnetoelectric composites. When the pre-stress is set to zero in the model, the predicted results of the magnetoelectric coefficient coincide well with the available experimental results both qualitatively and quantitatively. Using the model, we can qualitatively predict the influence of the pre-stress, magnetic bias fields and the volume fraction of the magnetostrictive material on the magnetoelectric coefficient. The predicted results show that the influences of the pre-stress on the magnetoelectric coefficient, which varies with the magnetic bias field, before and after reaching the magnetoelectric coefficient maximum, are opposite. That is, the influence of the pre-stress on curves of the magnetoelectric coefficient reverses when the magnetoelectric coefficient reaches its maximum. Therefore, the correct setting of the pre-stress can lower the applied magnetic bias field and improve the magnetoelectric coefficient. The established nonlinear magnetoelectric effect model can provide a theoretical basis for regulating the magnetoelectric coefficient by the pre-stress and magnetic bias field and make it possible to design high-precision miniature magnetoelectric devices. (paper)

  17. A low frequency vibration energy harvester using magnetoelectric laminate composite

    International Nuclear Information System (INIS)

    Ju, Suna; Chae, Song Hee; Choi, Yunhee; Lee, Seungjun; Ji, Chang-Hyeon; Lee, Hyang Woon

    2013-01-01

    In this paper, we present a vibration energy harvester using magnetoelectric laminate composite and a springless spherical permanent magnet as a proof mass. The harvester utilizes a freely movable spherical permanent magnet to transform external vibration into a time varying magnetic field applied to the magnetoelectric transducer. The laminate composite consists of a Ni–Mn–Ga-based MSMA (magnetic shape memory alloy) element and a PZT (lead zirconate titanate) plate. A proof-of-concept harvester has been fabricated and characterized at various input accelerations and frequencies. A maximum open circuit voltage of 1.18 V has been obtained in response to a 3g vibration at 17 Hz with the fabricated device. Moreover, a maximum output voltage of 10.24 V and output power of 4.1 μW have been achieved on a 950 Ω load, when the fabricated energy harvester was mounted on a smartphone and shaken by hand. (paper)

  18. Two-dimensional multiferroics in monolayer group IV monochalcogenides

    Science.gov (United States)

    Wang, Hua; Qian, Xiaofeng

    2017-03-01

    Low-dimensional multiferroic materials hold great promises in miniaturized device applications such as nanoscale transducers, actuators, sensors, photovoltaics, and nonvolatile memories. Here, using first-principles theory we predict that two-dimensional (2D) monolayer group IV monochalcogenides including GeS, GeSe, SnS, and SnSe are a class of 2D semiconducting multiferroics with giant strongly-coupled in-plane spontaneous ferroelectric polarization and spontaneous ferroelastic lattice strain that are thermodynamically stable at room temperature and beyond, and can be effectively modulated by elastic strain engineering. Their optical absorption spectra exhibit strong in-plane anisotropy with visible-spectrum excitonic gaps and sizable exciton binding energies, rendering the unique characteristics of low-dimensional semiconductors. More importantly, the predicted low domain wall energy and small migration barrier together with the coupled multiferroic order and anisotropic electronic structures suggest their great potentials for tunable multiferroic functional devices by manipulating external electrical, mechanical, and optical field to control the internal responses, and enable the development of four device concepts including 2D ferroelectric memory, 2D ferroelastic memory, and 2D ferroelastoelectric nonvolatile photonic memory as well as 2D ferroelectric excitonic photovoltaics.

  19. Enhanced room temperature multiferroicity in Gd doped BFO

    CSIR Research Space (South Africa)

    Pradhan, SK

    2009-01-01

    Full Text Available deficient Gd doped multiferroic BFO system. At particular doping level of Gd, this bulk ceramics showed spectacular M~H behavior at room temperature which is likely to open a new avenue for the potential applications in information storing technology as well...

  20. Multiferroicity in oxide thin films and heterostructures

    International Nuclear Information System (INIS)

    Glavic, Artur

    2012-01-01

    In this work a variety of different systems of transition metal oxides ABO 3 (perovskite materials, where B stands for a transition metal and A for a rare earth element) were produced as thin films and heterostructures and analyzed for the structural, magnetic and ferroelectric properties. For the epitaxial film preparation mostly pulse laser deposition (PLD) was applied. For one series high pressure oxide sputter deposition was used as well. The bulk multiferroics TbMnO 3 and DyMnO 3 , which develop their electric polarization due to a cycloidal magnetic order, have been prepared as single layers with thicknesses between 2 and 200 nm on YAlO 3 substrates using PLD and sputter deposition. The structural characterization of the surfaces and crystal structure where performed using X-ray reflectometry and diffraction, respectively. These yielded low surface roughness and good epitaxial growth. The magnetic behavior was macroscopically measured with SQUID magnetometry and microscopically with polarized neutron diffraction and resonant magnetic X-ray scattering. While all investigated samples showed antiferromagnetic order, comparable with the collinear magnetic phase of their bulk materials, only the sputter deposited samples exhibited the multiferroic low temperature cycloidal order. The investigation of the optical second harmonic generation in a TbMnO 3 sample could proof the presence of a ferroelectric order in the low temperature phase. The respective transition temperatures of the thin films have been very similar to those of the bulk materials. In contrast an increase in the rare earth ordering temperature has been observed, which reduces the Mn order slightly, an effect not known from bulk TbMnO 3 crystals. The coupling of the antiferromagnetic order in TbMnO 3 to ferromagnetic layers of LaCoO 3 was investigated in super-lattices containing 20 bilayers produced with PLD on the same substrates. The SQUID magnetometry yielded a strong influence of the

  1. The theoretical ultimate magnetoelectric coefficients of magnetoelectric composites by optimization design

    International Nuclear Information System (INIS)

    Wang, H.-L.; Liu, B.

    2014-01-01

    This paper investigates what is the largest magnetoelectric (ME) coefficient of ME composites, and how to realize it. From the standpoint of energy conservation, a theoretical analysis is carried out on an imaginary lever structure consisting of a magnetostrictive phase, a piezoelectric phase, and a rigid lever. This structure is a generalization of various composite layouts for optimization on ME effect. The predicted theoretical ultimate ME coefficient plays a similar role as the efficiency of ideal heat engine in thermodynamics, and is used to evaluate the existing typical ME layouts, such as the parallel sandwiched layout and the serial layout. These two typical layouts exhibit ME coefficient much lower than the theoretical largest values, because in the general analysis the stress amplification ratio and the volume ratio can be optimized independently and freely, but in typical layouts they are dependent or fixed. To overcome this shortcoming and achieve the theoretical largest ME coefficient, a new design is presented. In addition, it is found that the most commonly used electric field ME coefficient can be designed to be infinitely large. We doubt the validity of this coefficient as a reasonable ME effect index and consider three more ME coefficients, namely the electric charge ME coefficient, the voltage ME coefficient, and the static electric energy ME coefficient. We note that the theoretical ultimate value of the static electric energy ME coefficient is finite and might be a more proper measure of ME effect

  2. A nonlinear magnetoelectric model for magnetoelectric layered composite with coupling stress

    International Nuclear Information System (INIS)

    Shi, Yang; Gao, Yuanwen

    2014-01-01

    Based on a linear piezoelectric relation and a nonlinear magnetostrictive constitutive relation, A nonlinear magnetoelectric (ME) effect model for flexural layered ME composites is established in in-plane magnetic field. In the proposed model, the true coupling stress and the equivalent piezomagnetic coefficient are taken into account and obtained through an iterative approach. Some calculations on nonlinear ME coefficient are conducted and discussed. Our results show that for both the flexural bilayer and trilayer composites, the true coupling stress in the composites first increase and then approach to a constant value with the increase of applied magnetic fields, affecting the nonlinear ME effect significantly. With consideration of the true coupling stress, the ME effect is smaller than that without consideration of the true coupling stress. Moreover, the proposed theoretical model predicts that the ME coefficient of the trilayer composite (does not generate the bending deflection) is much larger than that of bilayer composite (generates the bending deflection), which is in well agreement with the previous works. The influences of the applied magnetic field on the true coupling stress and fraction ratio corresponding to the extreme ME coefficients of layered structures are also investigated. - Highlights: • This paper develops a nonlinear model for layered ME composite. • The true coupling stress is obtained through an iterative approach. • The influences of coupling stress and flexural deformation are discussed. • The dependence of ME coefficient on magnetic field is studied

  3. Landau-Ginzburg description of anomalous properties of novel room temperature multiferroics Pb(Fe{sub 1/2}Ta{sub 1/2}){sub x}(Zr{sub 0.53}Ti{sub 0.47}){sub 1-x}O{sub 3} and Pb(Fe{sub 1/2}Nb{sub 1/2}){sub x}(Zr{sub 0.53}Ti{sub 0.47}){sub 1−x}O{sub 3}

    Energy Technology Data Exchange (ETDEWEB)

    Glinchuk, Maya D.; Eliseev, Eugene A. [Institute for Problems of Materials Science, National Academy of Sciences of Ukraine, Krjijanovskogo 3, 03142 Kyiv (Ukraine); Morozovska, Anna N., E-mail: anna.n.morozovska@gmail.com [Institute of Physics, National Academy of Sciences of Ukraine, 46, pr. Nauky, 03028 Kyiv (Ukraine)

    2016-01-14

    Landau-Ginzburg thermodynamic formalism is used for the description of the anomalous ferroelectric, ferromagnetic, and magnetoelectric properties of Pb(Fe{sub 1/2}Ta{sub 1/2}){sub x}(Zr{sub 0.53}Ti{sub 0.47}){sub 1−x}O{sub 3} and Pb(Fe{sub 1/2}Nb{sub 1/2}){sub x}(Zr{sub 0.53}Ti{sub 0.47}){sub 1−x}O{sub 3} micro-ceramics. We calculated temperature, composition, and external field dependences of ferroelectric, ferromagnetic, and antiferromagnetic phases transition temperatures, remanent polarization, magnetization, hysteresis loops, dielectric permittivity, and magnetoelectric coupling. Special attention was paid to the comparison of developed theory with experiments. It appeared possible to describe adequately main experimental results including a reasonable agreement between the shape of calculated and measured hysteresis loops and remnant polarization. Since Landau-Ginzburg thermodynamic formalism appertains to single domain properties of a ferroic, we did not aim to describe quantitatively the coercive field under the presence of realistic poly-domain switching. Information about linear and nonlinear magnetoelectric coupling coefficients was extracted from the experimental data. From the fitting of experimental data with theoretical formula, we obtained the composition dependence of Curie-Weiss constant that is known to be inversely proportional to harmonic (linear) dielectric stiffness, as well as the strong nonlinear dependence of anharmonic parameters in free energy. Keeping in mind the essential influence of these parameters on multiferroic properties, the obtained results open the way to govern practically all the material properties with the help of suitable composition choice. A forecast of the strong enough influence of antiferrodistortive order parameter on the transition temperatures and so on the phase diagrams and properties of multiferroics are made on the basis of the developed theory.

  4. First-principles approach to the dynamic magnetoelectric couplings for the non-reciprocal directional dichroism in BiFeO3

    International Nuclear Information System (INIS)

    Lee, Jun Hee; Fishman, Randy S; Kézsmáki, István

    2016-01-01

    Due to the complicated magnetic and crystallographic structures of BiFeO 3 , its magnetoelectric (ME) couplings and microscopic model Hamiltonian remain poorly understood. By employing a first-principles approach, we uncover all possible ME couplings associated with the spin-current (SC) and exchange-striction (ES) polarizations, and construct an appropriate Hamiltonian for the long-range spin-cycloid in BiFeO 3 . First-principles calculations are used to understand the microscopic origins of the ME couplings. We find that inversion symmetries broken by ferroelectric and antiferroelectric distortions induce the SC and the ES polarizations, which cooperatively produce the dynamic ME effects in BiFeO 3 . A model motivated by first principles reproduces the absorption difference of counter-propagating light beams called non-reciprocal directional dichroism. The current paper focuses on the spin-driven (SD) polarizations produced by a dynamic electric field, i.e. the dynamic ME couplings. Due to the inertial properties of Fe, the dynamic SD polarizations differ significantly from the static SD polarizations. Our systematic approach can be generally applied to any multiferroic material, laying the foundation for revealing hidden ME couplings on the atomic scale and for exploiting optical ME effects in the next generation of technological devices such as optical diodes. (paper)

  5. Properties and Microstructures of Sn-Ag-Cu-X Lead-Free Solder Joints in Electronic Packaging

    OpenAIRE

    Sun, Lei; Zhang, Liang

    2015-01-01

    SnAgCu solder alloys were considered as one of the most popular lead-free solders because of its good reliability and mechanical properties. However, there are also many problems that need to be solved for the SnAgCu solders, such as high melting point and poor wettability. In order to overcome these shortcomings, and further enhance the properties of SnAgCu solders, many researchers choose to add a series of alloying elements (In, Ti, Fe, Zn, Bi, Ni, Sb, Ga, Al, and rare earth) and nanoparti...

  6. TOPICAL REVIEW: First principles studies of multiferroic materials

    Science.gov (United States)

    Picozzi, Silvia; Ederer, Claude

    2009-07-01

    Multiferroics, materials where spontaneous long-range magnetic and dipolar orders coexist, represent an attractive class of compounds, which combine rich and fascinating fundamental physics with a technologically appealing potential for applications in the general area of spintronics. Ab initio calculations have significantly contributed to recent progress in this area, by elucidating different mechanisms for multiferroicity and providing essential information on various compounds where these effects are manifestly at play. In particular, here we present examples of density-functional theory investigations for two main classes of materials: (a) multiferroics where ferroelectricity is driven by hybridization or purely structural effects, with BiFeO3 as the prototype material, and (b) multiferroics where ferroelectricity is driven by correlation effects and is strongly linked to electronic degrees of freedom such as spin-, charge-, or orbital-ordering, with rare-earth manganites as prototypes. As for the first class of multiferroics, first principles calculations are shown to provide an accurate qualitative and quantitative description of the physics in BiFeO3, ranging from the prediction of large ferroelectric polarization and weak ferromagnetism, over the effect of epitaxial strain, to the identification of possible scenarios for coupling between ferroelectric and magnetic order. For the second class of multiferroics, ab initio calculations have shown that, in those cases where spin-ordering breaks inversion symmetry (e.g. in antiferromagnetic E-type HoMnO3), the magnetically induced ferroelectric polarization can be as large as a few µC cm-2. The examples presented point the way to several possible avenues for future research: on the technological side, first principles simulations can contribute to a rational materials design, aimed at identifying spintronic materials that exhibit ferromagnetism and ferroelectricity at or above room temperature. On the

  7. Luminescence investigations of rare earth doped lead-free borate glasses modified by MO (M = Ca, Sr, Ba)

    Energy Technology Data Exchange (ETDEWEB)

    Janek, Joanna, E-mail: janek.joanna@gmail.com; Sołtys, Marta; Żur, Lidia; Pietrasik, Ewa; Pisarska, Joanna; Pisarski, Wojciech A.

    2016-09-01

    Series of lead-free borate glasses with different oxide modifiers and lanthanide ions were prepared. The effect of oxide modifiers MO (M = Ca, Sr, Ba) on spectroscopic properties of trivalent Ln{sup 3+} (Ln = Eu, Er, Pr) were systematically investigated. Especially, the luminescence spectra of Ln{sup 3+}-doped lead-free borate glasses are presented and discussed in relation to the impact of selective components (CaO, SrO and BaO). Several spectroscopic parameters, such as the fluorescence intensity ratio R/O (Eu{sup 3+}) and measured luminescence lifetimes for the {sup 5}D{sub 0} (Eu{sup 3+}), {sup 4}I{sub 13/2} (Er{sup 3+}) and {sup 1}D{sub 2} (Pr{sup 3+}) excited states of lanthanide ions were analyzed in details. The research proved that spectroscopic properties of trivalent Ln{sup 3+} depend significantly on kind of presence oxide modifiers MO (M = Ca, Sr, Ba) in glass host matrices. - Highlights: • Luminescence of Ln{sup 3+}-doped borate glasses was presented and discussed. • Effect of glass modifiers on spectroscopic properties of rare earths was studied. • Measured luminescence lifetimes of Ln{sup 3+} (Ln = Eu, Er, Pr) were analyzed. • Luminescence intensity ratios R/O (Eu{sup 3+}) were determined.

  8. Lead-free sliding overplate for highly loaded big end bearings; Bleifreie Laufschicht fuer hochbelastete Haupt- und Pleuellager

    Energy Technology Data Exchange (ETDEWEB)

    Graham, N.; Schnell, L.; Arnold, G. [Federal-Mogul Wiesbaden GmbH and Co. KG (Germany)

    2003-10-01

    Lead has always been an important metal in plain bearing technology. Completely lead-free solutions for high-end engine applications are still not considered to be technically achievable. Therefore, the European End of Life Directive (2000/53/EC), which took effect on 1 July 2003, lists copper-based lead/bronze bearings as an exception. The bearing group of Federal-Mogul has now announced its exit from the lead industry and addresses the issue layer by layer. A recently introduced adaptive bearing offers a lead-free overplate for high-performance internal combustion engine applications. This new bearing changes its technical characteristics during the running-in phase. (orig.) [German] Blei war schon immer eine wichtige Komponente in der Gleitlagertechnik. Bis heute gelten vollstaendig bleifreie Loesungen fuer hochbelastete Gleitlager als technisch nicht machbar. Deshalb nennt die europaeische Altautoverordnung (2000/53/EG), die seit dem 1. Juli 2003 in Kraft ist, als Ausnahme die kupferbasierten Bleibronzelager. Die Gleitlagergruppe von Federal-Mogul hat jetzt ihren Rueckzug aus der Verarbeitung von Blei angekuendigt und geht das Thema Schicht fuer Schicht an. Ein kuerzlich eingefuehrtes, anpassungsfaehiges Lager fuer High-End-Verbrennungsmotoren verfuegt ueber eine bleifreie Laufschicht. Bei diesem neuen Lager veraendern sich die technischen Eigenschaften waehrend der Einlaufphase. (orig.)

  9. Laser soldering of Sn-Ag-Cu and Sn-Zn-Bi lead-free solder pastes

    Science.gov (United States)

    Takahashi, Junichi; Nakahara, Sumio; Hisada, Shigeyoshi; Fujita, Takeyoshi

    2004-10-01

    It has reported that a waste of an electronics substrate including lead and its compound such as 63Sn-37Pb has polluted the environment with acid rain. For that environment problem the development of lead-free solder alloys has been promoted in order to find out the substitute for Sn-Pb solders in the United States, Europe, and Japan. In a present electronics industry, typical alloys have narrowed down to Sn-Ag-Cu and Sn-Zn lead-free solder. In this study, solderability of Pb-free solder that are Sn-Ag-Cu and Sn-Zn-Bi alloy was studied on soldering using YAG (yttrium aluminum garnet) laser and diode laser. Experiments were peformed in order to determine the range of soldering parameters for obtaining an appropriate wettability based on a visual inspection. Joining strength of surface mounting chip components soldered on PCB (printed circuit board) was tested on application thickness of solder paste (0.2, 0.3, and 0.4 mm). In addition, joining strength characteristics of eutectic Sn-Pb alloy and under different power density were examined. As a result, solderability of Sn-Ag-Cu (Pb-free) solder paste are equivalent to that of coventional Sn-Pb solder paste, and are superior to that of Sn-Zn-Bi solder paste in the laser soldering method.

  10. Multiferroic behavior on nanometric La2/3Ca1/3MnO3 / BaTiO3 bilayers

    Science.gov (United States)

    Prieto, Pedro; Ordoñez, John Edward; Gomez, Maria Elena; Lopera, Wilson

    2014-03-01

    We have deposited bilayers of the FM La2/3Ca1/3MnO3 and FE BaTiO3 as a route to design systems with artificial magnetoelectric coupling on LCMO/BTO/Nb:STO system. We maintain a fixed magnetic layer thickness (tLCMO = 48 nm) and varying the thickness of the ferroelectric layer (tBTO = 20, 50, 100 nm). We analyze the influence of the thickness ratio (tBTO/ tLCMO) in electrical and magnetic properties of manganite. From X-ray diffraction analysis we observed that the samples grew textured. Magnetization and transport measurements indicate a possible multiferroic behavior in the bilayer. We found an increase in the Curie and metal-insulator transition temperature in the bilayer in comparison with those for LCMO (48nm)/STO. Hysteresis loops on bilayers show ferromagnetic behavior. This work has been supported by the ``El Patrimonio Autónomo Fondo Nacional de Financiamiento para CT&I FJC'' Colciencias-CENM Research Projects: No. 1106-48-925531 and CI7917-CC 10510 contract 0002-2013 COLCIENCIAS-UNIVALLE.

  11. Defect-Induced Hedgehog Polarization States in Multiferroics

    Science.gov (United States)

    Li, Linze; Cheng, Xiaoxing; Jokisaari, Jacob R.; Gao, Peng; Britson, Jason; Adamo, Carolina; Heikes, Colin; Schlom, Darrell G.; Chen, Long-Qing; Pan, Xiaoqing

    2018-03-01

    Continuous developments in nanotechnology require new approaches to materials synthesis that can produce novel functional structures. Here, we show that nanoscale defects, such as nonstoichiometric nanoregions (NSNRs), can act as nano-building blocks for creating complex electrical polarization structures in the prototypical multiferroic BiFeO3 . An array of charged NSNRs are produced in BiFeO3 thin films by tuning the substrate temperature during film growth. Atomic-scale scanning transmission electron microscopy imaging reveals exotic polarization rotation patterns around these NSNRs. These polarization patterns resemble hedgehog or vortex topologies and can cause local changes in lattice symmetries leading to mixed-phase structures resembling the morphotropic phase boundary with high piezoelectricity. Phase-field simulations indicate that the observed polarization configurations are mainly induced by charged states at the NSNRs. Engineering defects thus may provide a new route for developing ferroelectric- or multiferroic-based nanodevices.

  12. Modeling of Magnetoelectric Interaction in Magnetostrictive-Piezoelectric Composites

    Directory of Open Access Journals (Sweden)

    M. I. Bichurin

    2012-01-01

    Full Text Available The paper dwells on the theoretical modeling of magnetoelectric (ME effect in layered and bulk composites based on magnetostrictive and piezoelectric materials. Our analysis rests on the simultaneous solution of elastodynamic or elastostatic and electro/magnetostatic equations. The expressions for ME coefficients as the functions of material parameters and volume fractions of components are obtained. Longitudinal, transverse, and in-plane cases are considered. The use of the offered model has allowed to present the ME effect in ferrite cobalt-barium titanate, ferrite cobalt-PZT, ferrite nickel-PZT, and lanthanum strontium manganite-PZT composites adequately.

  13. Phenomenological treatment of the gigantic magnetoelectric effect in some ferroelectromagnets

    International Nuclear Information System (INIS)

    Chupis, I.E.

    2005-01-01

    It is shown that observed in DyMn 2 O 5 and TbMnO 3 colossal changes of dielectric constant and electric polarization with magnetic field are possible in the ferroelectromagnets with close magnetic and ferroelectric transition temperatures and a small value of electric polarization. The appearance of electric polarization in commensurate magnetic state of TbMnO 3 and the reorientation of electric polarization by magnetic field was interpreted as a result of a renormalization of the ferroelectric energy by the magnetoelectric interaction. The existence of a weak ferromagnetic moment along c-axis in TbMnO 3 commensurate phase was predicted

  14. Charge, spin and orbital order in the candidate multiferroic material LuFe2O4

    International Nuclear Information System (INIS)

    Groot, Joost de

    2012-01-01

    This thesis is a detailed study of the magnetic, structural and orbital order parameters of the candidate multiferroic material LuFe 2 O 4 . Multiferroic oxides with a strong magnetoelectric coupling are of high interest for potential information technology applications, but they are rare because the traditional mechanism of ferroelectricity is incompatible with magnetism. Consequently, much attention is focused on various unconventional mechanisms of ferroelectricity. Of these, ferroelectricity originating from charge ordering (CO) is particularly intriguing because it potentially combines large electric polarizations with strong magneto-electric coupling. However, examples of oxides where this mechanism occurs are exceedingly rare and none is really well understood. LuFe 2 O 4 is often cited as the prototypical example of CO-based ferroelectricity. In this material, the order of Fe valences has been proposed to render the triangular Fe/O bilayers polar by making one of the two layers rich in Fe 2+ and the other rich in Fe 3+ , allowing for a possible ferroelectric stacking of the individual bilayers. Because of this new mechanism for ferroelectricity, and also because of the high transition temperatures of charge order (T CO ∝320K) and ferro magnetism (T N ∝240 K) LuFe 2 O 4 has recently attracted increasing attention. Although these polar bilayers are generally accepted in the literature for LuFe 2 O 4 , direct proof is lacking. An assumption-free experimental determination of whether or not the CO in the Fe/O bilayers is polar would be crucial, given the dependence of the proposed mechanism of ferroelectricity from CO in LuFe 2 O 4 on polar bilayers. This thesis starts with a detailed characterization of the macroscopic magnetic properties, where growing ferrimagnetic contributions observed in magnetization could be ascribed to increasing oxygen off-stoichiometry. The main focus is on samples exhibiting a sharp magnetic transition to long-range spin order

  15. Effects of metallic nanoparticle doped flux on the interfacial intermetallic compounds between lead-free solder ball and copper substrate

    International Nuclear Information System (INIS)

    Sujan, G.K.; Haseeb, A.S.M.A.; Afifi, A.B.M.

    2014-01-01

    Lead free solders currently in use are prone to develop thick interfacial intermetallic compound layers with rough morphology which are detrimental to the long term solder joint reliability. A novel method has been developed to control the morphology and growth of intermetallic compound layers between lead-free Sn–3.0Ag–0.5Cu solder ball and copper substrate by doping a water soluble flux with metallic nanoparticles. Four types of metallic nanoparticles (nickel, cobalt, molybdenum and titanium) were used to investigate their effects on the wetting behavior and interfacial microstructural evaluations after reflow. Nanoparticles were dispersed manually with a water soluble flux and the resulting nanoparticle doped flux was placed on copper substrate. Lead-free Sn–3.0Ag–0.5Cu solder balls of diameter 0.45 mm were placed on top of the flux and were reflowed at a peak temperature of 240 °C for 45 s. Angle of contact, wetting area and interfacial microstructure were studied by optical microscopy, field emission scanning electron microscopy and energy-dispersive X-ray spectroscopy. It was observed that the angle of contact increased and wetting area decreased with the addition of cobalt, molybdenum and titanium nanoparticles to flux. On the other hand, wettability improved with the addition of nickel nanoparticles. Cross-sectional micrographs revealed that both nickel and cobalt nanoparticle doping transformed the morphology of Cu 6 Sn 5 from a typical scallop type to a planer one and reduced the intermetallic compound thickness under optimum condition. These effects were suggested to be related to in-situ interfacial alloying at the interface during reflow. The minimum amount of nanoparticles required to produce the planer morphology was found to be 0.1 wt.% for both nickel and cobalt. Molybdenum and titanium nanoparticles neither appear to undergo alloying during reflow nor have any influence at the solder/substrate interfacial reaction. Thus, doping of flux

  16. Effects of metallic nanoparticle doped flux on the interfacial intermetallic compounds between lead-free solder ball and copper substrate

    Energy Technology Data Exchange (ETDEWEB)

    Sujan, G.K., E-mail: sgkumer@gmail.com; Haseeb, A.S.M.A., E-mail: haseeb@um.edu.my; Afifi, A.B.M., E-mail: amalina@um.edu.my

    2014-11-15

    Lead free solders currently in use are prone to develop thick interfacial intermetallic compound layers with rough morphology which are detrimental to the long term solder joint reliability. A novel method has been developed to control the morphology and growth of intermetallic compound layers between lead-free Sn–3.0Ag–0.5Cu solder ball and copper substrate by doping a water soluble flux with metallic nanoparticles. Four types of metallic nanoparticles (nickel, cobalt, molybdenum and titanium) were used to investigate their effects on the wetting behavior and interfacial microstructural evaluations after reflow. Nanoparticles were dispersed manually with a water soluble flux and the resulting nanoparticle doped flux was placed on copper substrate. Lead-free Sn–3.0Ag–0.5Cu solder balls of diameter 0.45 mm were placed on top of the flux and were reflowed at a peak temperature of 240 °C for 45 s. Angle of contact, wetting area and interfacial microstructure were studied by optical microscopy, field emission scanning electron microscopy and energy-dispersive X-ray spectroscopy. It was observed that the angle of contact increased and wetting area decreased with the addition of cobalt, molybdenum and titanium nanoparticles to flux. On the other hand, wettability improved with the addition of nickel nanoparticles. Cross-sectional micrographs revealed that both nickel and cobalt nanoparticle doping transformed the morphology of Cu{sub 6}Sn{sub 5} from a typical scallop type to a planer one and reduced the intermetallic compound thickness under optimum condition. These effects were suggested to be related to in-situ interfacial alloying at the interface during reflow. The minimum amount of nanoparticles required to produce the planer morphology was found to be 0.1 wt.% for both nickel and cobalt. Molybdenum and titanium nanoparticles neither appear to undergo alloying during reflow nor have any influence at the solder/substrate interfacial reaction. Thus, doping

  17. Piezoelectric and ferroelectric properties of lead-free niobium-rich potassium lithium tantalate niobate single crystals

    Energy Technology Data Exchange (ETDEWEB)

    Li, Jun, E-mail: lijuna@hit.edu.cn [Department of Physics, Harbin Institute of Technology, Harbin 150001 (China); Li, Yang [Department of chemistry, Harbin Institute of Technology, Harbin 150001 (China); Zhou, Zhongxiang [Department of Physics, Harbin Institute of Technology, Harbin 150001 (China); Guo, Ruyan; Bhalla, Amar S. [Multifunctional Electronic Materials and Device Research Lab, Department of Electrical and Computer Engineering, The University of Texas at San Antonio, San Antonio 78249 (United States)

    2014-01-01

    Graphical abstract: - Highlights: • Lead-free K{sub 0.95}Li{sub 0.05}Ta{sub 1−x}Nb{sub x}O{sub 3} single crystals were grown using the top-seeded melt growth method. • The piezoelectric and ferroelectric properties of as-grown crystals were systematically investigated. • The piezoelectric properties are very attractive, e.g. for x = 0.60 composition, k{sub t} ≈ 70%, k{sub 31} ≈ 70%, k{sub 33} ≈ 77%, d{sub 31} ≈ 230 pC/N, d{sub 33} ≈ 600 pC/N. • The coercive fields of P–E hysteresis loops are quite small, about or less than 1 kV/mm. - Abstract: Lead-free potassium lithium tantalate niobate single crystals with the composition of K{sub 0.95}Li{sub 0.05}Ta{sub 1−x}Nb{sub x}O{sub 3} (abbreviated as KLTN, x = 0.51, 0.60, 0.69, 0.78) were grown using the top-seeded melt growth method. Their piezoelectric and ferroelectric properties in as-grown crystals have been systematically investigated. The phase transitions and Curie temperatures were determined from dielectric and pyroelectric measurements. Piezoelectric coefficients and electromechanical coupling factors in thickness mode, length-extensional mode and longitudinal mode were obtained. The piezoelectric properties are very attractive, e.g. for x = 0.60 composition, k{sub t} ≈ 70%, k{sub 31} ≈ 70%, k{sub 33} ≈ 77%, d{sub 31} ≈ 230 pC/N, d{sub 33} ≈ 600 pC/N are comparable to the lead-based PZT composition. The polarization versus electric field hysteresis loops show saturated shapes. In short, lead-free niobium-rich KLTN system possesses comparable properties to those in important lead-based piezoelectric material nowadays.

  18. Preparation and characterization of single-crystal multiferroic nanofiber composites

    Energy Technology Data Exchange (ETDEWEB)

    Ren, Zhaohui; Xiao, Zhen; Yin, Simin; Mai, Jiangquan; Liu, Zhenya; Xu, Gang; Li, Xiang; Shen, Ge [State Key Lab of Silicon Materials, Department of Material Science and Engineering, Cyrus Tang Center for Sensor Materials and Applications, Zhejiang University, Hangzhou 310027 (China); Han, Gaorong, E-mail: hgr@zju.edu.cn [State Key Lab of Silicon Materials, Department of Material Science and Engineering, Cyrus Tang Center for Sensor Materials and Applications, Zhejiang University, Hangzhou 310027 (China)

    2013-03-05

    Graphical abstract: One-dimensional single-crystal multiferroic composites composed of PbTiO{sub 3} nanofiber-CoFe{sub 2}O{sub 4} nanodot have been prepared for the first time by a facile in situ solid state sintering method. The composites demonstrate ferroelectricity and ferromagnetism as well as strong coupling between them. Highlights: ► 1D single-crystal multiferroic PTO-CFO was prepared via in situ solid state sintering method. ► A simple epitaxial growth relation has been found between the PTO–CFO composites. ► The composites reveal ferroelectricity and ferromagnetism as well as coupling between them. -- Abstract: One-dimensional single-crystal multiferroic composites consisting of PbTiO{sub 3} (PTO) nanofiber-CoFe{sub 2}O{sub 4} (CFO) nanodot were prepared using an in situ solid state sintering method, where pre-perovskite PTO nanofibers and CFO nanodots were used as precursors. Structural analyses by using transmission electron microscopy, scanning electron microscopy and X-ray diffraction determined a epitaxial growth relation between the PTO nanofiber and the CFO nanodot. Ferromagnetism and ferroelectricity of the nanofiber composites were investigated by using vibarting sample magnetometer (VSM) and piezoresponse force microscopy (PFM)

  19. Lead Free Electric Primer

    Science.gov (United States)

    2011-10-06

    fluorocarbon-based polymer (PolyChloroTriFluoroEthylene). No longer produced by 3M, this material is available from sources in Japan . This material contains...2. Filter 3. Vacuum dry MIC 4. Lightly grind MIC (mortar and pestle ) 5. Add hexane 6. Add BTATz 7. Magnetic stirring (20 min.) 8. Add

  20. Dielectric and piezoelectric properties of lead-free (Bi,Na)TiO3-based thin films

    Science.gov (United States)

    Abazari, M.; Safari, A.; Bharadwaja, S. S. N.; Trolier-McKinstry, S.

    2010-02-01

    Dielectric and piezoelectric properties of morphotropic phase boundary (Bi,Na)TiO3-(Bi,K)TiO3-BaTiO3 epitaxial thin films deposited on SrRuO3 coated SrTiO3 substrates were reported. Thin films of 350 nm thickness exhibited small signal dielectric permittivity and loss tangent values of 750 and 0.15, respectively, at 1 kHz. Ferroelectric hysteresis measurements indicated a remanent polarization value of 30 μC/cm2 with a coercive field of 85-100 kV/cm. The thin film transverse piezoelectric coefficient (e31,f) of these films after poling at 600 kV/cm was found to be -2.2 C/m2. The results indicate that these BNT-based thin films are a potential candidate for lead-free piezoelectric devices.

  1. Nanodomain Engineered (K, Na)NbO3 Lead-Free Piezoceramics: Enhanced Thermal and Cycling Reliabilities

    DEFF Research Database (Denmark)

    Yao, Fang-Zhou; Wang, Ke; Cheng, Li-Qian

    2015-01-01

    - based materials, accepting the drawbacks of high temperature and cycling instabilities. Here, we present that CaZrO3-modified (K, Na)NbO3 piezoceramics not only possess excellent performance at ambient conditions benefiting from nanodomain engineering, but also exhibit superior stability against......The growing environmental concerns have been pushing the development of viable green alternatives for lead-based piezoceramics to be one of the priorities in functional ceramic materials. A polymorphic phase transition has been utilized to enhance piezoelectric properties of lead-free (K, Na)NbO3...... temperature fluctuation and electrical fatigue cycling. It was found that the piezoelectric coefficient d33 is temperature independent under 4 kV/mm, which can be attributed to enhanced thermal stability of electric field engineered domain configuration; whereas the electric field induced strain exhibits...

  2. Role of sintering time, crystalline phases and symmetry in the piezoelectric properties of lead-free KNN-modified ceramics

    International Nuclear Information System (INIS)

    Rubio-Marcos, F.; Marchet, P.; Merle-Mejean, T.; Fernandez, J.F.

    2010-01-01

    Lead-free KNN-modified piezoceramics of the system (Li,Na,K)(Nb,Ta,Sb)O 3 were prepared by conventional solid-state sintering. The X-ray diffraction patterns revealed a perovskite phase, together with some minor secondary phase, which was assigned to K 3 LiNb 6 O 17 , tetragonal tungsten-bronze (TTB). A structural evolution toward a pure tetragonal structure with the increasing sintering time was observed, associated with the decrease of TTB phase. A correlation between higher tetragonality and higher piezoelectric response was clearly evidenced. Contrary to the case of the LiTaO 3 modified KNN, very large abnormal grains with TTB structure were not detected. As a consequence, the simultaneous modification by tantalum and antimony seems to induce during sintering a different behaviour from the one of LiTaO 3 modified KNN.

  3. Role of sintering time, crystalline phases and symmetry in the piezoelectric properties of lead-free KNN-modified ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Rubio-Marcos, F., E-mail: frmarcos@icv.csic.es [Electroceramic Department, Instituto de Ceramica y Vidrio, CSIC, Kelsen 5, 28049 Madrid (Spain); Marchet, P.; Merle-Mejean, T. [SPCTS, UMR 6638 CNRS, Universite de Limoges, 123, Av. A. Thomas, 87060 Limoges (France); Fernandez, J.F. [Electroceramic Department, Instituto de Ceramica y Vidrio, CSIC, Kelsen 5, 28049 Madrid (Spain)

    2010-09-01

    Lead-free KNN-modified piezoceramics of the system (Li,Na,K)(Nb,Ta,Sb)O{sub 3} were prepared by conventional solid-state sintering. The X-ray diffraction patterns revealed a perovskite phase, together with some minor secondary phase, which was assigned to K{sub 3}LiNb{sub 6}O{sub 17}, tetragonal tungsten-bronze (TTB). A structural evolution toward a pure tetragonal structure with the increasing sintering time was observed, associated with the decrease of TTB phase. A correlation between higher tetragonality and higher piezoelectric response was clearly evidenced. Contrary to the case of the LiTaO{sub 3} modified KNN, very large abnormal grains with TTB structure were not detected. As a consequence, the simultaneous modification by tantalum and antimony seems to induce during sintering a different behaviour from the one of LiTaO{sub 3} modified KNN.

  4. Mechanical confinement for improved energy storage density in BNT-BT-KNN lead-free ceramic capacitors

    Energy Technology Data Exchange (ETDEWEB)

    Chauhan, Aditya; Patel, Satyanarayan; Vaish, Rahul, E-mail: rahul@iitmandi.ac.in [School of Engineering, Indian Institute of Technology Mandi, 175 001 (India)

    2014-08-15

    With the advent of modern power electronics, embedded circuits and non-conventional energy harvesting, the need for high performance capacitors is bound to become indispensible. The current state-of-art employs ferroelectric ceramics and linear dielectrics for solid state capacitance. However, lead-free ferroelectric ceramics propose to offer significant improvement in the field of electrical energy storage owing to their high discharge efficiency and energy storage density. In this regards, the authors have investigated the effects of compressive stress as a means of improving the energy storage density of lead-free ferroelectric ceramics. The energy storage density of 0.91(Bi{sub 0.5}Na{sub 0.5})TiO{sub 3}-0.07BaTiO{sub 3}-0.02(K{sub 0.5}Na{sub 0.5})NbO{sub 3} ferroelectric bulk ceramic was analyzed as a function of varying levels of compressive stress and operational temperature .It was observed that a peak energy density of 387 mJ.cm{sup -3} was obtained at 100 MPa applied stress (25{sup o}C). While a maximum energy density of 568 mJ.cm{sup -3} was obtained for the same stress at 80{sup o}C. These values are indicative of a significant, 25% and 84%, improvement in the value of stored energy compared to an unloaded material. Additionally, material's discharge efficiency has also been discussed as a function of operational parameters. The observed phenomenon has been explained on the basis of field induced structural transition and competitive domain switching theory.

  5. Evolution of phase structure and giant strain at low driving fields in Bi-based lead-free incipient piezoelectrics

    International Nuclear Information System (INIS)

    Maqbool, Adnan; Hussain, Ali; Malik, Rizwan Ahmed; Rahman, Jamil Ur; Zaman, Arif; Song, Tae Kwon; Kim, Won-Jeong; Kim, Myong-Ho

    2015-01-01

    Graphical abstract: - Highlights: • Nb-doped BNBT–SZ ceramics were prepared by conventional solid state method. • A giant normalized strain of 825 pm/V at 4 kV/mm was achieved. • A large strain of 0.20% triggered at a relatively low field of 3 kV/mm. • Highest strain obtained in BNT-based ceramics at such a low driving field. • Ferroelectric to ergodic-relaxor phase transition occurred with Nb-doping. - Abstract: Lead-free 0.99[(Bi 0.5 Na 0.5 ) 0.935 Ba 0.065 Ti (1–x) Nb x O 3 ]–0.01SrZrO 3 (BNBTNb100x–SZ, with Nb100x = 0–1) ceramics were prepared by the conventional mixed oxide route. X-ray diffraction and Raman scattering was utilized for the structural evolution of Nb-modified BNBT–SZ ceramics at average and short-scale localized structure. Temperature dependent dielectric properties showed ferroelectric–ergodic relaxor (FE–ER) transition in Nb-modified BNBT–SZ ceramics by producing a significant disruption of the long-range FE order. A giant normalized strain of 825 pm/V at 4 kV/mm was achieved at Nb1.0. Interestingly, at a relatively low applied field of 3 kV/mm, the Nb0.75 sample displayed a large electric field-induced strain (EFIS) response of 0.20%, which is highest value obtained in non-textured lead-free BNT-based ceramics at such low driving field. The structural distortion induced by doping and electric poling is correlated with the dielectric, ferroelectric and EFIS response, and the evolution of giant strain was ascribed to reversible field induced phase transition from ER–FE phase

  6. Mechanical confinement for improved energy storage density in BNT-BT-KNN lead-free ceramic capacitors

    Directory of Open Access Journals (Sweden)

    Aditya Chauhan

    2014-08-01

    Full Text Available With the advent of modern power electronics, embedded circuits and non-conventional energy harvesting, the need for high performance capacitors is bound to become indispensible. The current state-of-art employs ferroelectric ceramics and linear dielectrics for solid state capacitance. However, lead-free ferroelectric ceramics propose to offer significant improvement in the field of electrical energy storage owing to their high discharge efficiency and energy storage density. In this regards, the authors have investigated the effects of compressive stress as a means of improving the energy storage density of lead-free ferroelectric ceramics. The energy storage density of 0.91(Bi0.5Na0.5TiO3-0.07BaTiO3-0.02(K0.5Na0.5NbO3 ferroelectric bulk ceramic was analyzed as a function of varying levels of compressive stress and operational temperature .It was observed that a peak energy density of 387 mJ.cm-3 was obtained at 100 MPa applied stress (25oC. While a maximum energy density of 568 mJ.cm-3 was obtained for the same stress at 80oC. These values are indicative of a significant, 25% and 84%, improvement in the value of stored energy compared to an unloaded material. Additionally, material's discharge efficiency has also been discussed as a function of operational parameters. The observed phenomenon has been explained on the basis of field induced structural transition and competitive domain switching theory.

  7. Co-existence of tetragonal and monoclinic phases and multiferroic properties for x ⩽ 0.30 in the (1 − x)Pb(Zr{sub 0.52}Ti{sub 0.48})O{sub 3}–(x)BiFeO{sub 3} system

    Energy Technology Data Exchange (ETDEWEB)

    Sharma, Subhash; Singh, Vikash [Department of Physics and Materials Science and Engineering, Jaypee Institute of Information Technology, A-10, Sector-62, Noida 201307, Uttar Pradesh (India); Kotnala, R.K. [National Physical Laboratory (CSIR), Dr. K.S. Krishnan Marg, New Delhi 110012 (India); Ranjan, Rajeev [Department of Materials Engineering, Indian Institute of Science, Bangalore 560012 (India); Dwivedi, R.K., E-mail: rk.dwivedi@jiit.ac.in [Department of Physics and Materials Science and Engineering, Jaypee Institute of Information Technology, A-10, Sector-62, Noida 201307, Uttar Pradesh (India)

    2014-11-25

    Highlights: • Synthesis of (1 − x)PbZr{sub 0.52}Ti{sub 0.48}O{sub 3}–(x)BiFeO{sub 3} with x ⩽ 0.30 by sol–gel method. • Structural phase transformation with x has been revealed by Rietveld analysis. • Raman analysis supports structural phase transition. • Occurrence of MC is a strong evidence of magneto-electric coupling. • Enhance magnetization is obtained in the dominant monoclinic phase for x ⩾0.15. - Abstract: Compositions with x ⩽ 0.30 in the system (1 − x)Pb(Zr{sub 0.52}Ti{sub 0.48})O{sub 3}–(x)BiFeO{sub 3} were synthesized by sol–gel method. Rietveld analysis of X-ray diffraction data reveals tetragonal structure (P4mm) for x ⩽ 0.05 and monoclinic (Cm) phase along with the existence of tetragonal phase for 0.10 ⩽ x ⩽ 0.25 and monoclinic phase for x = 0.30. Transformation of E(2TO) and E + B1 vibrational modes in the range 210–250 cm{sup −1} (present for x ⩽ 0.25) into A′ + A″ modes at ∼236 cm{sup −1} for x = 0.30, and occurrence of new vibrational modes A′ and A″ in Raman spectra for x ⩾ 0.10 unambiguously support the presence of monoclinic phase. Occurrence of remnant polarisation and enhanced magnetization with concentration of BiFeO{sub 3} indicates superior multiferroic properties. Variation of magneto-capacitance with applied magnetic field is a strong evidence of magneto-electric multiferroic coupling in these materials.

  8. Topological magnetoelectric effects in microwave far-field radiation

    Energy Technology Data Exchange (ETDEWEB)

    Berezin, M.; Kamenetskii, E. O.; Shavit, R. [Microwave Magnetic Laboratory, Department of Electrical and Computer Engineering, Ben Gurion University of the Negev, Beer Sheva (Israel)

    2016-07-21

    Similar to electromagnetism, described by the Maxwell equations, the physics of magnetoelectric (ME) phenomena deals with the fundamental problem of the relationship between electric and magnetic fields. Despite a formal resemblance between the two notions, they concern effects of different natures. In general, ME-coupling effects manifest in numerous macroscopic phenomena in solids with space and time symmetry breakings. Recently, it was shown that the near fields in the proximity of a small ferrite particle with magnetic-dipolar-mode (MDM) oscillations have the space and time symmetry breakings and the topological properties of these fields are different from the topological properties of the free-space electromagnetic fields. Such MDM-originated fields—called magnetoelectric (ME) fields—carry both spin and orbital angular momenta. They are characterized by power-flow vortices and non-zero helicity. In this paper, we report on observation of the topological ME effects in far-field microwave radiation based on a small microwave antenna with a MDM ferrite resonator. We show that the microwave far-field radiation can be manifested with a torsion structure where an angle between the electric and magnetic field vectors varies. We discuss the question on observation of the regions of localized ME energy in far-field microwave radiation.

  9. Magnetoelectric properties of magnetic/ferroelectric multilayer thin films

    Energy Technology Data Exchange (ETDEWEB)

    Hwang, Sung-Ok; Eum, You-Jeong; Koo, Chang-Young; Lee, Hee-Young [Yeungnam University, Gyeongsan (Korea, Republic of); Park, Jung-Min [Osaka University, Osaka (Japan); Ryu, Jung-Ho [Korea Institute of Materials Science, Changwon (Korea, Republic of)

    2014-07-15

    Magnetic/ferroelectric multilayer thin films using PbZr{sub 0.52}Ti{sub 0.48}O{sub 3} (PZT) and two different magnetic materials, i.e., Terfenol-D and CuFe{sub 2}O{sub 4} (CuFO) layers, were fabricated, and their magnetoelectric (ME) coupling behavior was investigated. The PZT layer was first coated onto Pt/Ti/SiO{sub 2}/Si substrate by sol-gel spin coating method. Pt layer, which served as an electrode and a diffusion barrier, was grown on the PZT layer by using the ion-beam sputtering method. The ME voltage coefficients were calculated from the ME voltage data measured utilizing a magnetoelectric test system. The Terfenol-D/Pt/PZT films were found to show a higher in-plane ME voltage coefficient than that the CuFO/Pt/PZT films due primarily to the higher magnetostriction coefficient of Terfenol-D.

  10. Physics considerations in targeted anticancer drug delivery by magnetoelectric nanoparticles

    Science.gov (United States)

    Stimphil, Emmanuel; Nagesetti, Abhignyan; Guduru, Rakesh; Stewart, Tiffanie; Rodzinski, Alexandra; Liang, Ping; Khizroev, Sakhrat

    2017-06-01

    In regard to cancer therapy, magnetoelectric nanoparticles (MENs) have proven to be in a class of its own when compared to any other nanoparticle type. Like conventional magnetic nanoparticles, they can be used for externally controlled drug delivery via application of a magnetic field gradient and image-guided delivery. However, unlike conventional nanoparticles, due to the presence of a non-zero magnetoelectric effect, MENs provide a unique mix of important properties to address key challenges in modern cancer therapy: (i) a targeting mechanism driven by a physical force rather than antibody matching, (ii) a high-specificity delivery to enhance the cellular uptake of therapeutic drugs across the cancer cell membranes only, while sparing normal cells, (iii) an externally controlled mechanism to release drugs on demand, and (iv) a capability for image guided precision medicine. These properties separate MEN-based targeted delivery from traditional biotechnology approaches and lay a foundation for the complementary approach of technobiology. The biotechnology approach stems from the underlying biology and exploits bioinformatics to find the right therapy. In contrast, the technobiology approach is geared towards using the physics of molecular-level interactions between cells and nanoparticles to treat cancer at the most fundamental level and thus can be extended to all the cancers. This paper gives an overview of the current state of the art and presents an ab initio model to describe the underlying mechanisms of cancer treatment with MENs from the perspective of basic physics.

  11. Magnetoelectric effect in structures which consist from ferrimagnetic and piezoelectric components

    International Nuclear Information System (INIS)

    Koronovs'kij, V.Je.

    2007-01-01

    Magnetoelectric (ME) properties of the structure which consists from mechanically connected magnetostriction and piezoelectric plates were investigated on example of the yttrium-ferrite-garnet (YIG) - piezoelectric. The laser polarimeter is using

  12. Improving the magnetoelectric performance of Metglas/PZT laminates by annealing in a magnetic field.

    Science.gov (United States)

    Freeman, E; Harper, J; Goel, N; Gilbert, I; Unguris, J; Schiff, S J; Tadigadapa, S

    2017-01-01

    A comprehensive investigation of magnetostriction optimization in Metglas 2605SA1 ribbons is performed to enhance magnetoelectric performance. We explore a range of annealing conditions to relieve remnant stress and align the magnetic domains in the Metglas, while minimizing unwanted crystallization. The magnetostriction coefficient, magnetoelectric coefficient, and magnetic domain alignment are correlated to optimize magnetoelectric performance. We report on direct magnetostriction observed by in-plane Doppler vibrometer and domain imagining using scanning electron microscopy with polarization analysis for a range of annealing conditions. We find that annealing in an oxygen-free environment at 400 °C for 30 min yields an optimal magnetoelectric coefficient, magnetostriction and magnetostriction coefficient. The optimized ribbons had a magnetostriction of 50.6 ± 0.2 μ m m -1 and magnetoelectric coefficient of 79.3 ± 1.5 μ m m -1 mT -1 . The optimized Metglas 2605SA1 ribbons and PZT-5A (d 31 mode) sensor achieves a magnetic noise floor of approximately 600 pT Hz -1/2 at 100 Hz and a magnetoelectric coefficient of 6.1 ± 0.03 MV m -1 T -1 .

  13. Improving the magnetoelectric performance of Metglas/PZT laminates by annealing in a magnetic field

    Science.gov (United States)

    Freeman, E.; Harper, J.; Goel, N.; Gilbert, I.; Unguris, J.; Schiff, S. J.; Tadigadapa, S.

    2017-08-01

    A comprehensive investigation of magnetostriction optimization in Metglas 2605SA1 ribbons is performed to enhance magnetoelectric performance. We explore a range of annealing conditions to relieve remnant stress and align the magnetic domains in the Metglas, while minimizing unwanted crystallization. The magnetostriction coefficient, magnetoelectric coefficient, and magnetic domain alignment are correlated to optimize magnetoelectric performance. We report on direct magnetostriction observed by in-plane Doppler vibrometer and domain imagining using scanning electron microscopy with polarization analysis for a range of annealing conditions. We find that annealing in an oxygen-free environment at 400 {}\\circ {{C}} for 30 min yields an optimal magnetoelectric coefficient, magnetostriction and magnetostriction coefficient. The optimized ribbons had a magnetostriction of 50.6 ± 0.2 μ {{m}} {{{m}}}-1 and magnetoelectric coefficient of 79.3 ± 1.5 µm m-1 mT-1. The optimized Metglas 2605SA1 ribbons and PZT-5A (d31 mode) sensor achieves a magnetic noise floor of approximately 600 pT {{{H}}{{z}}}-1/2 at 100 Hz and a magnetoelectric coefficient of 6.1 ± 0.03 MV m-1 T-1.

  14. Studies of electrical conductivity and complex initial permeability of multiferroic xBa{sub 0.95}Sr{sub 0.05}TiO{sub 3}-(1-x)BiFe{sub 0.90}Gd{sub 0.10}O{sub 3} ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Miah, Mohammad J., E-mail: mmjulhash@yahoo.com [Department of Physics, Bangladesh University of Engineering & Technology, Dhaka (Bangladesh); Department of Physics, Comilla University, Comilla (Bangladesh); Khan, M. N. I. [Materials Science Division, Atomic Energy Center, Dhaka (Bangladesh); Hossain, A. K. M. Akther [Department of Physics, Bangladesh University of Engineering & Technology, Dhaka (Bangladesh)

    2016-07-12

    Multiferroic xBa{sub 0.95}Sr{sub 0.05}TiO{sub 3}-(1-x)BiFe{sub 0.90}Gd{sub 0.10}O{sub 3} [xBST-(1-x)BFGO] (x = 0.00, 0.10 and 0.20) ceramics were prepared by the standard solid-state reaction technique. Crystal structure of the ceramics was determined by X-ray diffraction pattern. All the compositions exhibited rhombohedral crystal structure. The tolerance factor ‘t’ varied from 0.847 to 0.864. The AC conductivity spectrum followed the Jonscher’s power law. The Nyquist plots indicated that only grains have the contribution to the resistance in this material and the values of grain resistance (R{sub g}) increased with BST content. The real part of complex initial permeability decreased with the increase in frequency and increased with increasing BST content. Magnetoelectric coefficient was determined for all compositions. The maximum value of magnetoelectric coefficient was found to be 1.467 mV.cm{sup −1}.Oe{sup −1} for x = 0.20.

  15. Giant Piezoelectricity and High Curie Temperature in Nanostructured Alkali Niobate Lead-Free Piezoceramics through Phase Coexistence.

    Science.gov (United States)

    Wu, Bo; Wu, Haijun; Wu, Jiagang; Xiao, Dingquan; Zhu, Jianguo; Pennycook, Stephen J

    2016-11-30

    Because of growing environmental concerns, the development of lead-free piezoelectric materials with enhanced properties has become of great interest. Here, we report a giant piezoelectric coefficient (d 33 ) of 550 pC/N and a high Curie temperature (T C ) of 237 °C in (1-x-y)K 1-w Na w Nb 1-z Sb z O 3- xBiFeO 3- yBi 0.5 Na 0.5 ZrO 3 (KN w NS z -xBF-yBNZ) ceramics by optimizing x, y, z, and w. Atomic-resolution polarization mapping by Z-contrast imaging reveals the intimate coexistence of rhombohedral (R) and tetragonal (T) phases inside nanodomains, that is, a structural origin for the R-T phase boundary in the present KNN system. Hence, the physical origin of high piezoelectric performance can be attributed to a nearly vanishing polarization anisotropy and thus low domain wall energy, facilitating easy polarization rotation between different states under an external field.

  16. The micro-droplet behavior of a molten lead-free solder in an inkjet printing process

    International Nuclear Information System (INIS)

    Tsai, M H; Chou, H H; Hwang, W S

    2009-01-01

    An experimental investigation on the droplet formation of molten Sn3.0 wt%Ag0.5 wt%Cu alloy by an inkjet printing process was conducted. The printing process used a piezoelectric print head with a nozzle orifice diameter of 50 µm. Micro-droplets of a molten lead-free solder were ejected at 230 °C. The print head was driven by a bipolar pulse 40 V in amplitude. The major variables for this study were two pulse times; t rise /t finalrise and t fall , as well as N 2 back-pressure in the molten solder reservoir. Under various printing conditions, extrusion of the liquid column, contraction of liquid thread and pinch-off of liquid thread at nozzle exit were observed by monitoring the dynamics of the molten solder droplet ejection process. The droplet formation was found to be insensitive to t rise and t finalrise in the range of 250–1000 µs. The behavior of droplet formation was, however, significantly affected by the transfer rate, t fall , in the range of 30–60 µs and t fall of 50 µs yielded the most desirable condition of single droplet formation. The N 2 back-pressure was also found to be critical, where a back pressure between 10 and 21 kPa could give the desirable single-droplet formation condition

  17. Elevated-Temperature Mechanical Properties of Lead-Free Sn-0.7Cu- xSiC Nanocomposite Solders

    Science.gov (United States)

    Mohammadi, A.; Mahmudi, R.

    2018-02-01

    Mechanical properties of Sn-0.7 wt.%Cu lead-free solder alloy reinforced with 0 vol.%, 1 vol.%, 2 vol.%, and 3 vol.% 100-nm SiC particles have been assessed using the shear punch testing technique in the temperature range from 25°C to 125°C. The composite materials were fabricated by the powder metallurgy route by blending, compacting, sintering, and finally extrusion. The 2 vol.% SiC-containing composite showed superior mechanical properties. In all conditions, the shear strength was adversely affected by increasing test temperature, and the 2 vol.% SiC-containing composite showed superior mechanical properties. Depending on the test temperature, the shear yield stress and ultimate shear strength increased, respectively, by 3 MPa to 4 MPa and 4 MPa to 5.5 MPa, in the composite materials. The strength enhancement was mostly attributed to the Orowan particle strengthening mechanism due to the SiC nanoparticles, and to a lesser extent to the coefficient of thermal expansion mismatch between the particles and matrix in the composite solder. A modified shear lag model was used to predict the total strengthening achieved by particle addition, based on the contribution of each of the above mechanisms.

  18. Effect of trace elements on the interface reactions between two lead-free solders and copper or nickel substrates

    Directory of Open Access Journals (Sweden)

    Soares D.

    2007-01-01

    Full Text Available Traditional Sn-Pb solder alloys are being replaced, because of environmental and health concerns about lead toxicity. Among some alternative alloy systems, the Sn-Zn and Sn-Cu base alloy systems have been studied and reveal promising properties. The reliability of a solder joint is affected by the solder/substrate interaction and the nature of the layers formed at the interface. The solder/substrate reactions, for Sn-Zn and Sn-Cu base solder alloys, were evaluated in what concerns the morphology and chemical composition of the interface layers. The effect of the addition of P, at low levels, on the chemical composition of the layers present at the interface was studied. The phases formed at the interface between the Cu or Ni substrate and a molten lead-free solder at 250ºC, were studied for different stage times and alloy compositions. The melting temperatures, of the studied alloys, were determined by Differential Scanning Calorimetry (DSC. Identification of equilibrium phases formed at the interface layer, and the evaluation of their chemical composition were performed by Scanning Electron Microscopy (SEM/EDS. Different interface characteristics were obtained, namely for the alloys containing Zn. The obtained IML layer thickness was compared, for both types of alloy systems.

  19. Effects of improved process for CuO-doped NKN lead-free ceramics on high-power piezoelectric transformers.

    Science.gov (United States)

    Yang, Song-Ling; Tsai, Cheng-Che; Liou, Yi-Cheng; Hong, Cheng-Shong; Li, Bing-Jing; Chu, Sheng-Yuan

    2011-12-01

    In this paper, the effects of the electrical proper- ties of CuO-doped (Na(0.5)K(0.5))NbO(3) (NKN) ceramics prepared separately using the B-site oxide precursor method (BO method) and conventional mixed-oxide method (MO method) on high-power piezoelectric transformers (PTs) were investigated. The performances of PTs made with these two substrates were compared. Experimental results showed that the output power and temperature stability of PTs could be enhanced because of the lower resonant impedance of the ceramics prepared using the BO method. In addition, the output power of PTs was more affected by the resonant impedance than by the mechanical quality factor (Q(m)) of the ceramics. The PTs fabricated with ceramics prepared using the BO method showed a high efficiency of more than 94% and a maximum output power of 8.98 W (power density: 18.3 W/cm(3)) with temperature increase of 3°C under the optimum load resistance (5 kΩ) and an input voltage of 150 V(pp). This output power of the lead-free disk-type PTs is the best reported so far.

  20. Characterization of exposure to byproducts from firing lead-free frangible ammunition in an enclosed, ventilated firing range.

    Science.gov (United States)

    Grabinski, Christin M; Methner, Mark M; Jackson, Jerimiah M; Moore, Alexander L; Flory, Laura E; Tilly, Trevor; Hussain, Saber M; Ott, Darrin K

    2017-06-01

    U.S. Air Force small arms firing ranges began using copper-based, lead-free frangible ammunition in the early 2000s due to environmental and health concerns related to the use of lead-based ammunition. Exposure assessments at these firing ranges have routinely detected chemicals and metals in amounts much lower than their mass-based occupational exposure limits, yet, instructors report work-related health concerns including respiratory distress, nausea, and headache. The objective of this study at one firing range was to characterize the aerosol emissions produced by weapons during firing events and evaluate the ventilation system's effectiveness in controlling instructor exposure to these emissions. The ventilation system was assessed by measuring the range static air pressure differential and the air velocity at the firing line. Air flow patterns were near the firing line. Instructor exposure was sampled using a filter-based air sampling method for metals and a wearable, real-time ultrafine particle counter. Area air sampling was simultaneously performed to characterize the particle size distribution, morphology, and composition. In the instructor's breathing zone, the airborne mass concentration of copper was low (range = free frangible ammunition. Using an ultrafine particle counter appears to be an alternative method of assessing ventilation effectiveness in removing ultrafine particulate produced during firing events.

  1. Investigating the Formation Process of Sn-Based Lead-Free Nanoparticles with a Chemical Reduction Method

    International Nuclear Information System (INIS)

    Zhang, W.; Zhao, B.; Gao, Y.; Zhang, W.; Zhao, B.; Zou, Ch.; Zhai, Q.; Gao, Y.; Gao, Y.; Acquah, S.F.A.

    2013-01-01

    Nanoparticles of a promising lead-free solder alloy (Sn 3.5 Ag (wt.%, Sn Ag) and Sn 3.0 Ag 0.5 Cu (wt.%, SAC)) were synthesized through a chemical reduction method by using anhydrous ethanol and 1,10-phenanthroline as the solvent and surfactant, respectively. To illustrate the formation process of Sn-Ag alloy based nanoparticles during the reaction, X-ray diffraction (XRD) was used to investigate the phases of the samples in relation to the reaction time. Different nucleation and growth mechanisms were compared on the formation process of the synthesized nanoparticles. The XRD results revealed different reaction process compared with other researchers. There were many contributing factors to the difference in the examples found in the literature, with the main focus on the formation mechanism of crystal nuclei, the solubility and ionizability of metal salts in the solvent, the solid solubility of Cu in Ag nuclei, and the role of surfactant on the growth process. This study will help define the parameters necessary for the control of both the composition and size of the nanoparticles

  2. Hybrid input-output approach to metal production and its application to the introduction of lead-free solders.

    Science.gov (United States)

    Nakamura, Shinichiro; Murakami, Shinsuke; Nakajima, Kenichi; Nagasaka, Tetsuya

    2008-05-15

    The production process of metals such as copper, lead, and zinc is characterized by mutual interconnections and interdependence, as well as by the occurrence of a large number of byproducts, which include precious or rare metals, such as gold, silver, bismuth, and indium. On the basis of the framework of waste input-output (WIO), we present a hybrid 10 model that takes full account of the mutual interdependence among the metal production processes and the interdependence between them and all the other production sectors of the economy as well. The combination of a comprehensive representation of the whole national economy and the introduction of process knowledge of metal production allows for a detailed analysis of different materials-use scenarios under the consideration of full supply chain effects. For illustration, a hypothetical case study of the introduction of lead-free solder involving the production of silver as a byproduct of copper and lead smelting processes was developed and implemented using Japanese data. To meet the increased demand for the recovery and recycling of silver resources from end-of-life products, the final destination of metal silver in terms of products and user categories was estimated, and the target components with the highest silver concentration were identified.

  3. Microstructure and adhesion strength of Sn-9Zn-xAg lead-free solders wetted on Cu substrate

    International Nuclear Information System (INIS)

    Chang, T.-C.; Chou, S.-M.; Hon, M.-H.; Wang, M.-C.

    2006-01-01

    The microstructure and adhesion strength of the Sn-9Zn-xAg lead-free solders wetted on Cu substrates have been investigated by differential scanning calorimetry, optical microscopy, scanning electron microscopy, energy dispersive spectrometry and pull-off testing. The liquidus temperatures of the Sn-9Zn-xAg solder alloys are 222.1, 226.7, 231.4 and 232.9 deg. C for x = 2.5, 3.5, 5.0 and 7.5 wt%, respectively. A flat interface can be obtained as wetted at 350 deg. C at a rate of 11.8 mm/s. The adhesion strength of the Sn-9Zn-xAg/Cu interfaces decreases from 23.09 ± 0.31 to 12.32 ± 1.40 MPa with increasing Ag content from 2.5 to 7.5 wt% at 400 deg. C. After heat treatment at 150 deg. C, the adhesion strength of the Sn-9Zn-xAg/Cu interface decreases with increasing aging time

  4. Methodology for Analyzing Strain States During In-Situ Thermomechanical Cycling in Individual Lead Free Solder Joints Using Synchrotron Radiation

    International Nuclear Information System (INIS)

    Zhou, Bite; Bieler, Thomas R.; Lee, Tae-Kyu; Liu, Kuo-Chuan

    2009-01-01

    To examine how a lead-free solder joint deforms in a thermal cycling environment, both the elastic and plastic stress and strain behavior must be understood. Methods to identify evolution of the internal strain (stress) state during thermal cycling are described. A slice of a package containing a single row of solder joints was thermally cycled from 0 C to 100 C with a period of about 1 h with concurrent acquisition of transmission Laue patterns using synchrotron radiation. These results indicated that most joints are single crystals, with some being multicrystals with no more than a few Sn grain orientations. Laue patterns were analyzed to estimate local strains in different crystal directions at different temperatures during a thermal cycle. While the strains perpendicular to various crystal planes all vary in a similar way, the magnitude of strain varies. The specimens were subsequently given several hundred additional thermal cycles and measured again to assess changes in the crystal orientations. These results show that modest changes in crystal orientations occur during thermal cycling.

  5. Influence of the linear magneto-electric effect on the lateral shift of light reflected from a magneto-electric film

    International Nuclear Information System (INIS)

    Dadoenkova, Yu S; Petrov, R V; Bichurin, M I; Bentivegna, F F L; Dadoenkova, N N; Lyubchanskii, I L

    2016-01-01

    We present a theoretical investigation of the lateral shift of an infrared light beam reflected from a magnetic film deposited on a non-magnetic dielectric substrate, taking into account the linear magneto-electric interaction in the magnetic film. We use the stationary phase method to evaluate the lateral shift. It is shown that the magneto-electric coupling leads to a six-fold enhancement of the lateral shift amplitude of a p-(s-) polarized incident beam reflected into a s-(p-) polarized beam. A reversal of the magnetization in the film leads to a nonreciprocal sign change of the lateral shift. (paper)

  6. X-ray protective clothing. Does DIN 6857-1 allow an objective comparison between lead-free and lead-composite materials?

    International Nuclear Information System (INIS)

    Eder, H.; Schlattl, H.; Hoeschen, C.

    2010-01-01

    Purpose: The validity of DIN 6857-1 to establish lead equivalence for protective clothing is evaluated by Monte Carlo simulations and measurements. Materials and Methods: Commercially available protective clothing made of lead, lead-free and lead-composite materials has been tested regarding its protective efficacy. The analysis has been performed on the one hand in accordance with the test conditions described in the manufacturing standard DIN EN 61331-3 and on the other hand following the new DIN 6857-1 standard. Additionally, measurements have been carried out under simulated patient conditions by using an Alderson-Rando phantom. Results: Following DIN EN 61331-3, the lead-free protective clothing achieved the required protective efficacy only at a restricted tube-voltage range. The test according to DIN 6857-1 showed that the protective criteria were fulfilled only by one lead-composite apron, but not by the three lead-free aprons examined. Thus, in order to guarantee the same protection as lead between 50 and 120 kV, the conditions of DIN 6857-1 must be fulfilled. Conclusion: A modification of DIN EN 61331-3 to account for secondary radiation is strongly advised in the case of lead-free materials. In summary, most of the protective lead-free aprons in use should be used with care, particularly for examinations with a high dose. (orig.)

  7. Unfolding of Vortices into Topological Stripes in a Multiferroic Material

    Science.gov (United States)

    Wang, X.; Mostovoy, M.; Han, M. G.; Horibe, Y.; Aoki, T.; Zhu, Y.; Cheong, S.-W.

    2014-06-01

    Multiferroic hexagonal RMnO3 (R =rare earths) crystals exhibit dense networks of vortex lines at which six domain walls merge. While the domain walls can be readily moved with an applied electric field, the vortex cores so far have been impossible to control. Our experiments demonstrate that shear strain induces a Magnus-type force pulling vortices and antivortices in opposite directions and unfolding them into a topological stripe domain state. We discuss the analogy between this effect and the current-driven dynamics of vortices in superconductors and superfluids.

  8. Study of local correlations of magnetic and multiferroic compounds

    CERN Multimedia

    Alves, E J

    We propose to study magnetic and multiferroic strongly correlated electron materials using radioactive nuclear probe techniques, at ISOLDE . Following the strategy of a previous project, IS390, our aim is to provide local and element selective information on some of the mechanisms that rule structural, charge and orbital correlations, electronic and magnetic interactions and the coupling of the associated degrees of freedom. The main technique used is Perturbed Angular Correlations (PAC), which allows combined magnetic and electric hyperfine studies. This study is complemented by the use of conventional characterisation techniques, and the investigation of relevant macroscopic properties.

  9. Electronic conduction in doped multiferroic BiFeO3

    Science.gov (United States)

    Yang, Chan-Ho; Seidel, Jan; Kim, Sang-Yong; Gajek, M.; Yu, P.; Holcomb, M. B.; Martin, L. W.; Ramesh, R.; Chu, Y. H.

    2009-03-01

    Competition between multiple ground states, that are energetically similar, plays a key role in many interesting material properties and physical phenomena as for example in high-Tc superconductors (electron kinetic energy vs. electron-electron repulsion), colossal magnetoresistance (metallic state vs. charge ordered insulating state), and magnetically frustrated systems (spin-spin interactions). We are exploring the idea of similar competing phenomena in doped multiferroics by control of band-filling. In this paper we present systematic investigations of divalent Ca doping of ferroelectric BiFeO3 in terms of structural and electronic conduction properties as well as diffusion properties of oxygen vacancies.

  10. Magnetic force driven magnetoelectric effect in bi-cantilever composites

    Science.gov (United States)

    Zhang, Ru; Wu, Gaojian; Zhang, Ning

    2017-12-01

    The magnetic force driven magnetoelectric (ME) effect in bi-cantilever Mn-Zn-Ferrite /PZT composites is presented. Compared with single cantilever, the ME voltage coefficient in bi-cantilever composite is a little lower and the resonance frequency is higher, but the bi-cantilever structure is advantageous for integration. When the magnetic gap is 3 mm, the ME voltage coefficient can achieve 6.2 Vcm-1Oe-1 at resonance under optimum bias field Hm=1030 Oe; when the magnetic gap is 1.5 mm, the ME voltage coefficient can get the value as high as 4.4 Vcm-1Oe-1 under much lower bias field H=340 Oe. The stable ME effect in bi-cantilever composites has important potential application in the design of new type ME device.

  11. Equivalent Circuit for Magnetoelectric Read and Write Operations

    Science.gov (United States)

    Camsari, Kerem Y.; Faria, Rafatul; Hassan, Orchi; Sutton, Brian M.; Datta, Supriyo

    2018-04-01

    We describe an equivalent circuit model applicable to a wide variety of magnetoelectric phenomena and use spice simulations to benchmark this model against experimental data. We use this model to suggest a different mode of operation where the 1 and 0 states are represented not by states with net magnetization (like mx , my, or mz) but by different easy axes, quantitatively described by (mx2-my2), which switches from 0 to 1 through the write voltage. This change is directly detected as a read signal through the inverse effect. The use of (mx2-my2) to represent a bit is a radical departure from the standard convention of using the magnetization (m ) to represent information. We then show how the equivalent circuit can be used to build a device exhibiting tunable randomness and suggest possibilities for extending it to nonvolatile memory with read and write capabilities, without the use of external magnetic fields or magnetic tunnel junctions.

  12. Theory of Magnetoelectric Properties of 2D Systems

    Science.gov (United States)

    Chen, S. C.; Wu, J. Y.; Lin, C. Y.; Lin, M. F.

    2017-12-01

    This book addresses important advances in diverse quantization phenomena. 'Theory of Magnetoelectric Properties of 2D Systems' develops the generalized tight-binding model in order to comprehend the rich quantization phenomena in 2D materials. The unusual effects, taken into consideration simultaneously, mainly come from the multi-orbital hybridization, the spin-orbital coupling, the intralayer and interlayer atomic interactions, the layer number, the stacking configuration, the site-energy difference, the magnetic field, and the electric field. The origins of the phenomena are discussed in depth, particularly focusing on graphene, tinene, phosphorene and MoS2, with a broader model also drawn. This model could be further used to investigate electronic properties of 1D and 3D condensed-matter systems, and this book will prove to be a valuable resource to researchers and graduate students working in 2D materials science.

  13. Resonance of magnetization excited by voltage in magnetoelectric heterostructures

    Science.gov (United States)

    Yu, Guoliang; Zhang, Huaiwu; Li, Yuanxun; Li, Jie; Zhang, Dainan; Sun, Nian

    2018-04-01

    Manipulation of magnetization dynamics is critical for spin-based devices. Voltage driven magnetization resonance is promising for realizing low-power information processing systems. Here, we show through Finite Element Method (FEM) simulations that magnetization resonance in nanoscale magnetic elements can be generated by a radio frequency (rf) voltage via the converse magnetoelectric (ME) effect. The magnetization dynamics induced by voltage in a ME heterostructures is simulated by taking into account the magnetoelastic and piezoelectric coupling mechanisms among magnetization, strain and voltage. The frequency of the excited magnetization resonance is equal to the driving rf voltage frequency. The proposed voltage driven magnetization resonance excitation mechanism opens a way toward energy-efficient spin based device applications.

  14. Microwave magnetoelectric fields: An analytical study of topological characteristics

    Energy Technology Data Exchange (ETDEWEB)

    Joffe, R., E-mail: ioffr1@gmail.com [Microwave Magnetic Laboratory, Department of Electrical and Computer Engineering, Ben Gurion University of the Negev, Beer Sheva (Israel); Department of Electrical and Electronics Engineering, Shamoon College of Engineering, Beer Sheva (Israel); Shavit, R.; Kamenetskii, E.O. [Microwave Magnetic Laboratory, Department of Electrical and Computer Engineering, Ben Gurion University of the Negev, Beer Sheva (Israel)

    2015-10-15

    The near fields originated from a small quasi-two-dimensional ferrite disk with magnetic-dipolar-mode (MDM) oscillations are the fields with broken dual (electric-magnetic) symmetry. Numerical studies show that such fields – called the magnetoelectric (ME) fields – are distinguished by the power-flow vortices and helicity parameters (E.O. Kamenetskii, R. Joffe, R. Shavit, Phys. Rev. E 87 (2013) 023201). These numerical studies can well explain recent experimental results with MDM ferrite disks. In the present paper, we obtain analytically topological characteristics of the ME-field modes. For this purpose, we used a method of successive approximations. In the second approximation we take into account the influence of the edge regions of an open ferrite disk, which are excluded in the first-approximation solving of the magnetostatic (MS) spectral problem. Based on the analytical method, we obtain a “pure” structure of the electric and magnetic fields outside the MDM ferrite disk. The analytical studies can display some fundamental features that are non-observable in the numerical results. While in numerical investigations, one cannot separate the ME fields from the external electromagnetic (EM) radiation, the present theoretical analysis allows clearly distinguish the eigen topological structure of the ME fields. Importantly, this ME-field structure gives evidence for certain phenomena that can be related to the Tellegen and bianisotropic coupling effects. We discuss the question whether the MDM ferrite disk can exhibit properties of the cross magnetoelectric polarizabilities. - Highlights: • We obtain analytically topological characteristics of the ME-field modes. • We take into account the influence of the edge regions of an open ferrite disk. • We obtain a “pure” structure of the electromagnetic fields outside the ferrite disk. • Analytical studies show features that are non-observable in the numerical results. • ME-field gives evidence for

  15. Microwave magnetoelectric fields: An analytical study of topological characteristics

    International Nuclear Information System (INIS)

    Joffe, R.; Shavit, R.; Kamenetskii, E.O.

    2015-01-01

    The near fields originated from a small quasi-two-dimensional ferrite disk with magnetic-dipolar-mode (MDM) oscillations are the fields with broken dual (electric-magnetic) symmetry. Numerical studies show that such fields – called the magnetoelectric (ME) fields – are distinguished by the power-flow vortices and helicity parameters (E.O. Kamenetskii, R. Joffe, R. Shavit, Phys. Rev. E 87 (2013) 023201). These numerical studies can well explain recent experimental results with MDM ferrite disks. In the present paper, we obtain analytically topological characteristics of the ME-field modes. For this purpose, we used a method of successive approximations. In the second approximation we take into account the influence of the edge regions of an open ferrite disk, which are excluded in the first-approximation solving of the magnetostatic (MS) spectral problem. Based on the analytical method, we obtain a “pure” structure of the electric and magnetic fields outside the MDM ferrite disk. The analytical studies can display some fundamental features that are non-observable in the numerical results. While in numerical investigations, one cannot separate the ME fields from the external electromagnetic (EM) radiation, the present theoretical analysis allows clearly distinguish the eigen topological structure of the ME fields. Importantly, this ME-field structure gives evidence for certain phenomena that can be related to the Tellegen and bianisotropic coupling effects. We discuss the question whether the MDM ferrite disk can exhibit properties of the cross magnetoelectric polarizabilities. - Highlights: • We obtain analytically topological characteristics of the ME-field modes. • We take into account the influence of the edge regions of an open ferrite disk. • We obtain a “pure” structure of the electromagnetic fields outside the ferrite disk. • Analytical studies show features that are non-observable in the numerical results. • ME-field gives evidence for

  16. First-principles approach to the dynamic magnetoelectric couplings for the non-reciprocal directional dichroism in BiFeO3

    Science.gov (United States)

    Lee, Jun Hee; Kézsmáki, István; Fishman, Randy S.

    2016-04-01

    Due to the complicated magnetic and crystallographic structures of BiFeO3, its magnetoelectric (ME) couplings and microscopic model Hamiltonian remain poorly understood. By employing a first-principles approach, we uncover all possible ME couplings associated with the spin-current (SC) and exchange-striction (ES) polarizations, and construct an appropriate Hamiltonian for the long-range spin-cycloid in BiFeO3. First-principles calculations are used to understand the microscopic origins of the ME couplings. We find that inversion symmetries broken by ferroelectric and antiferroelectric distortions induce the SC and the ES polarizations, which cooperatively produce the dynamic ME effects in BiFeO3. A model motivated by first principles reproduces the absorption difference of counter-propagating light beams called non-reciprocal directional dichroism. The current paper focuses on the spin-driven (SD) polarizations produced by a dynamic electric field, i.e. the dynamic ME couplings. Due to the inertial properties of Fe, the dynamic SD polarizations differ significantly from the static SD polarizations. Our systematic approach can be generally applied to any multiferroic material, laying the foundation for revealing hidden ME couplings on the atomic scale and for exploiting optical ME effects in the next generation of technological devices such as optical diodes. This manuscript has been written by UT-Battelle, LLC under Contract No. DE-AC05-00OR22725 with the US Department of Energy. The United States Government retains and the publisher, by accepting the article for publication, acknowledges that the United States Government retains a non-exclusive, paid-up, irrevocable, world-wide license to publish or reproduce the published form of this manuscript, or allow others to do so, for United States Government purposes. The Department of Energy will provide public access to these results of federally sponsored research in accordance with the DOE Public Access Plan.

  17. The effect of graphene on the intermetallic and joint strength of Sn-3.5Ag lead-free solder

    Science.gov (United States)

    Mayappan, R.; Salleh, A.; Andas, J.

    2017-09-01

    Solder has been widely used in electronic industry as interconnection for electronic packaging. European Union and Japan have restricted the use of Sn-Pb solder as it contains lead which can harmful to human health and environment. Due to this, many researches have been done in order to find a suitable replacement for the lead solder. Although many lead-free solders are available, the Sn-3.5Ag solder with the addition of graphene seem to be a suitable candidate. In this study, a 0.07 wt% graphene nanosheet was added into the Sn-3.5Ag solder and this composite solder was prepared under powder metallurgy method. The solder was reacted with copper substrate at 250 °C for one minute. For joint strength analysis, two copper strips were soldered together. The solder joint was aged at temperature 100 °C for 500 hours. Scanning Electron Microscope (SEM) was used to observe the interfacial reaction and Instron machine was used to determine the joint strength. Cu6Sn5 intermetallic layer was formed at the interface between the Cu substrate and the solders. Composite solder showed the retardation of the intermetallic growth compared to the plain solder. The thickness value of the intermetallic was used to calculate the growth rate the IMC. The graphene nanosheets added solder has lower growth rate which is 3.86 × 10-15 cm2/s compared to the plain solder 7.15 × 10-15 cm2/s. Shear strength analysis show that the composite solder has higher joint compared to the plain solder.

  18. High energy storage density over a broad temperature range in sodium bismuth titanate-based lead-free ceramics.

    Science.gov (United States)

    Yang, Haibo; Yan, Fei; Lin, Ying; Wang, Tong; Wang, Fen

    2017-08-18

    A series of (1-x)Bi 0.48 La 0.02 Na 0.48 Li 0.02 Ti 0.98 Zr 0.02 O 3 -xNa 0.73 Bi 0.09 NbO 3 ((1-x)LLBNTZ-xNBN) (x = 0-0.14) ceramics were designed and fabricated using the conventional solid-state sintering method. The phase structure, microstructure, dielectric, ferroelectric and energy storage properties of the ceramics were systematically investigated. The results indicate that the addition of Na 0.73 Bi 0.09 NbO 3 (NBN) could decrease the remnant polarization (P r ) and improve the temperature stability of dielectric constant obviously. The working temperature range satisfying TCC 150  °C  ≤±15% of this work spans over 400 °C with the compositions of x ≥ 0.06. The maximum energy storage density can be obtained for the sample with x = 0.10 at room temperature, with an energy storage density of 2.04 J/cm 3 at 178 kV/cm. In addition, the (1-x)LLBNTZ-xNBN ceramics exhibit excellent energy storage properties over a wide temperature range from room temperature to 90 °C. The values of energy storage density and energy storage efficiency is 0.91 J/cm 3 and 79.51%, respectively, for the 0.90LLBNTZ-0.10NBN ceramic at the condition of 100 kV/cm and 90 °C. It can be concluded that the (1-x)LLBNTZ-xNBN ceramics are promising lead-free candidate materials for energy storage devices over a broad temperature range.

  19. Boosting the Recoverable Energy Density of Lead-Free Ferroelectric Ceramic Thick Films through Artificially Induced Quasi-Relaxor Behavior.

    Science.gov (United States)

    Peddigari, Mahesh; Palneedi, Haribabu; Hwang, Geon-Tae; Lim, Kyung Won; Kim, Ga-Yeon; Jeong, Dae-Yong; Ryu, Jungho

    2018-06-08

    Dielectric ceramic film capacitors, which store energy in the form of electric polarization, are promising for miniature pulsed power electronic device applications. For a superior energy storage performance of the capacitors, large recoverable energy density, along with high efficiency, high power density, fast charge/discharge rate, and good thermal/fatigue stability, is desired. Herein, we present highly dense lead-free 0.942[Na 0.535 K 0.480 NbO 3 ]-0.058LiNbO 3 (KNNLN) ferroelectric ceramic thick films (∼5 μm) demonstrating remarkable energy storage performance. The nanocrystalline KNNLN thick film fabricated by aerosol deposition (AD) process and annealed at 600 °C displayed a quasi-relaxor ferroelectric behavior, which is in contrast to the typical ferroelectric nature of the KNNLN ceramic in its bulk form. The AD film exhibited a large recoverable energy density of 23.4 J/cm 3 , with an efficiency of over 70% under the electric field of 1400 kV/cm. Besides, an ultrahigh power density of 38.8 MW/cm 3 together with a fast discharge speed of 0.45 μs, good fatigue endurance (up to 10 6 cycles), and thermal stability in a wide temperature range of 20-160 °C was also observed. Using the AD process, we could make a highly dense microstructure of the film containing nano-sized grains, which gave rise to the quasi-relaxor ferroelectric characteristics and the remarkable energy storage properties.

  20. Interconnection of thermal parameters, microstructure and mechanical properties in directionally solidified Sn–Sb lead-free solder alloys

    Energy Technology Data Exchange (ETDEWEB)

    Dias, Marcelino; Costa, Thiago [Department of Manufacturing and Materials Engineering, University of Campinas — UNICAMP, 13083-860 Campinas, SP (Brazil); Rocha, Otávio [Federal Institute of Education, Science and Technology of Pará — IFPA, 66093-020 Belém, PA (Brazil); Spinelli, José E. [Department of Materials Engineering, Federal University of São Carlos — UFSCar, 13565-905 São Carlos, SP (Brazil); Cheung, Noé, E-mail: cheung@fem.unicamp.br [Department of Manufacturing and Materials Engineering, University of Campinas — UNICAMP, 13083-860 Campinas, SP (Brazil); Garcia, Amauri [Department of Manufacturing and Materials Engineering, University of Campinas — UNICAMP, 13083-860 Campinas, SP (Brazil)

    2015-08-15

    Considerable effort is being made to develop lead-free solders for assembling in environmental-conscious electronics, due to the inherent toxicity of Pb. The search for substitute alloys of Pb–Sn solders has increased in order to comply with different soldering purposes. The solder must not only meet the expected levels of electrical performance but may also have appropriate mechanical strength, with the absence of cracks in the solder joints. The Sn–Sb alloy system has a range of compositions that can be potentially included in the class of high temperature solders. This study aims to establish interrelations of solidification thermal parameters, microstructure and mechanical properties of Sn–Sb alloys (2 wt.%Sb and 5.5 wt.%Sb) samples, which were directionally solidified under cooling rates similar to those of reflow procedures in industrial practice. A complete high-cooling rate cellular growth is shown to be associated with the Sn–2.0 wt.%Sb alloy and a reverse dendrite-to-cell transition is observed for the Sn–5.5 wt.%Sb alloy. Strength and ductility of the Sn–2.0 wt.%Sb alloy are shown not to be affected by the cellular spacing. On the other hand, a considerable variation in these properties is associated with the cellular region of the Sn–5.5 wt.%Sb alloy casting. - Graphical abstract: Display Omitted - Highlights: • The microstructure of the Sn–2 wt.%Sb alloy is characterized by high-cooling rates cells. • Reverse dendrite > cell transition occurs for Sn–5.5 wt.%Sb alloy: cells prevail for cooling rates > 1.2 K/s. • Sn–5.5 wt.%Sb alloy: the dendritic region occurs for cooling rates < 0.9 K/s. • Sn–5.5 wt.%Sb alloy: tensile properties are improved with decreasing cellular spacing.

  1. Determination of temperature dependency of material parameters for lead-free alkali niobate piezoceramics by the inverse method

    Directory of Open Access Journals (Sweden)

    K. Ogo

    2016-06-01

    Full Text Available Sodium potassium niobate (NKN piezoceramics have been paid much attention as lead-free piezoelectric materials in high temperature devices because of their high Curie temperature. The temperature dependency of their material parameters, however, has not been determined in detail up to now. For this purpose, we exploit the so-called Inverse Method denoting a simulation-based characterization approach. Compared with other characterization methods, the Inverse Method requires only one sample shape of the piezoceramic material and has further decisive advantages. The identification of material parameters showed that NKN is mechanically softer in shear direction compared with lead zirconate titanate (PZT at room temperature. The temperature dependency of the material parameters of NKN was evaluated in the temperature range from 30 °C to 150 °C. As a result, we figured out that dielectric constants and piezoelectric constants show a monotonous and isotropic increment with increasing temperature. On the other hand, elastic stiffness constant c 44 E of NKN significantly decreased in contrast to other elastic stiffness constants. It could be revealed that the decrement of c 44 E is associated with an orthorhombic-tetragonal phase transition. Furthermore, ratio of elastic compliance constants s 44 E / s 33 E exhibited similar temperature dependent behavior to the ratio of piezoelectric constants d15/d33. It is suspected that mechanical softness in shear direction is one origin of the large piezoelectric shear mode of NKN. Our results show that NKN are suitable for high temperature devices, and that the Inverse Method should be a helpful approach to characterize material parameters under their practical operating conditions for NKN.

  2. Investigation Of The Effects Of Reflow Profile Parameters On Lead-free Solder Bump Volumes And Joint Integrity

    Science.gov (United States)

    Amalu, E. H.; Lui, Y. T.; Ekere, N. N.; Bhatti, R. S.; Takyi, G.

    2011-01-01

    The electronics manufacturing industry was quick to adopt and use the Surface Mount Technology (SMT) assembly technique on realization of its huge potentials in achieving smaller, lighter and low cost product implementations. Increasing global customer demand for miniaturized electronic products is a key driver in the design, development and wide application of high-density area array package format. Electronic components and their associated solder joints have reduced in size as the miniaturization trend in packaging continues to be challenged by printing through very small stencil apertures required for fine pitch flip-chip applications. At very narrow aperture sizes, solder paste rheology becomes crucial for consistent paste withdrawal. The deposition of consistent volume of solder from pad-to-pad is fundamental to minimizing surface mount assembly defects. This study investigates the relationship between volume of solder paste deposit (VSPD) and the volume of solder bump formed (VSBF) after reflow, and the effect of reflow profile parameters on lead-free solder bump formation and the associated solder joint integrity. The study uses a fractional factorial design (FFD) of 24-1 Ramp-Soak-Spike reflow profile, with all main effects and two-way interactions estimable to determine the optimal factorial combination. The results from the study show that the percentage change in the VSPD depends on the combination of the process parameters and reliability issues could become critical as the size of solder joints soldered on the same board assembly vary greatly. Mathematical models describe the relationships among VSPD, VSBF and theoretical volume of solder paste. Some factors have main effects across the volumes and a number of interactions exist among them. These results would be useful for R&D personnel in designing and implementing newer applications with finer-pitch interconnect.

  3. Are lead-free hunting rifle bullets as effective at killing wildlife as conventional lead bullets? A comparison based on wound size and morphology

    Energy Technology Data Exchange (ETDEWEB)

    Trinogga, Anna, E-mail: anna_trinogga@gmx.de; Fritsch, Guido; Hofer, Heribert; Krone, Oliver

    2013-01-15

    Fragmentation of the lead core of conventional wildlife hunting rifle bullets causes contamination of the target with lead. The community of scavenger species which feed on carcasses or viscera discarded by hunters are regularly exposed to these lead fragments and may die by acute or chronic lead intoxication, as demonstrated for numerous species such as white-tailed eagles (Haliaeetus albicilla) where it is among the most important sources of mortality. Not only does hunting with conventional ammunition deposit lead in considerable quantities in the environment, it also significantly delays or threatens the recovery of endangered raptor populations. Although lead-free bullets might be considered a suitable alternative that addresses the source of these problems, serious reservations have been expressed as to their ability to quickly and effectively kill a hunted animal. To assess the suitability of lead-free projectiles for hunting practice, the wounding potential of conventional bullets was compared with lead-free bullets under real life hunting conditions. Wound dimensions were regarded as good markers of the projectiles' killing potential. Wound channels in 34 killed wild ungulates were evaluated using computed tomography and post-mortem macroscopical examination. Wound diameters caused by conventional bullets did not differ significantly to those created by lead-free bullets. Similarly, the size of the maximum cross-sectional area of the wound was similar for both bullet types. Injury patterns suggested that all animals died by exsanguination. This study demonstrates that lead-free bullets are equal to conventional hunting bullets in terms of killing effectiveness and thus equally meet the welfare requirements of killing wildlife as painlessly as possible. The widespread introduction and use of lead-free bullets should be encouraged as it prevents environmental contamination with a seriously toxic pollutant and contributes to the conservation of a wide

  4. Are lead-free hunting rifle bullets as effective at killing wildlife as conventional lead bullets? A comparison based on wound size and morphology

    International Nuclear Information System (INIS)

    Trinogga, Anna; Fritsch, Guido; Hofer, Heribert; Krone, Oliver

    2013-01-01

    Fragmentation of the lead core of conventional wildlife hunting rifle bullets causes contamination of the target with lead. The community of scavenger species which feed on carcasses or viscera discarded by hunters are regularly exposed to these lead fragments and may die by acute or chronic lead intoxication, as demonstrated for numerous species such as white-tailed eagles (Haliaeetus albicilla) where it is among the most important sources of mortality. Not only does hunting with conventional ammunition deposit lead in considerable quantities in the environment, it also significantly delays or threatens the recovery of endangered raptor populations. Although lead-free bullets might be considered a suitable alternative that addresses the source of these problems, serious reservations have been expressed as to their ability to quickly and effectively kill a hunted animal. To assess the suitability of lead-free projectiles for hunting practice, the wounding potential of conventional bullets was compared with lead-free bullets under real life hunting conditions. Wound dimensions were regarded as good markers of the projectiles' killing potential. Wound channels in 34 killed wild ungulates were evaluated using computed tomography and post-mortem macroscopical examination. Wound diameters caused by conventional bullets did not differ significantly to those created by lead-free bullets. Similarly, the size of the maximum cross-sectional area of the wound was similar for both bullet types. Injury patterns suggested that all animals died by exsanguination. This study demonstrates that lead-free bullets are equal to conventional hunting bullets in terms of killing effectiveness and thus equally meet the welfare requirements of killing wildlife as painlessly as possible. The widespread introduction and use of lead-free bullets should be encouraged as it prevents environmental contamination with a seriously toxic pollutant and contributes to the conservation of a wide variety

  5. Polarization-tuned diode behaviour in multiferroic BiFeO3 thin films

    KAUST Repository

    Yao, Yingbang; Zhang, Bei; Chen, Long; Yang, Yang; Wang, Zhihong; Alshareef, Husam N.; Zhang, Xixiang

    2012-01-01

    Asymmetric rectifying I-V behaviour of multiferroic BiFeO3 (BFO) thin films grown on transparent ITO-coated glass was quantitatively studied as a function of ferroelectric polarization. Different polarized states were established by unipolar

  6. Electrical, magnetic, and direct and converse magnetoelectric properties of (1−x)Pb(Zr{sub 0.52}Ti{sub 0.48})O{sub 3}−(x)CoFe{sub 2}O{sub 4} (PZT–CFO) magnetoelectric composites

    Energy Technology Data Exchange (ETDEWEB)

    Peng, Jian-hong, E-mail: pjhhj@sohu.com [College of Physics and Electronic Information Engineering, Qinghai University for Nationalities, Xining 810007 (China); College of Physics and Information Technology, Shaanxi Normal University, Xi' an 710062 (China); Hojamberdiev, Mirabbos, E-mail: hmirabbos@gmail.com [Materials and Structures Laboratory, Tokyo Institute of Technology, 4259 Nagatsuta, Midori, Yokohama, Kanagawa 226-8503 (Japan); Li, Hai-qing; Mao, Duo-lu; Zhao, Yuan-juan [College of Physics and Electronic Information Engineering, Qinghai University for Nationalities, Xining 810007 (China); Liu, Peng; Zhou, Jian-ping; Zhu, Gang-qiang [College of Physics and Information Technology, Shaanxi Normal University, Xi' an 710062 (China)

    2015-03-15

    In this work, hydrothermal synthesis and ceramic sintering process were applied to fabricate (1−x)Pb(Zr{sub 0.52}Ti{sub 0.48})O{sub 3}−(x)CoFe{sub 2}O{sub 4} (PZT–CFO) (x=0.20, 0.35, and 0.50) magnetoelectric (ME) composites. The X-ray diffraction (XRD) studies revealed that no chemical reaction occurred between individual PZT and CFO phases and confirmed the manifestation of PZT and CFO phases within the ME composite. Scanning electron microscopy (SEM) was used to investigate the microstructure and connectivity scheme in the ME composites. The dielectric constant (ε) and loss tangent (tan δ) were determined as functions of frequency and temperature for all the composites prepared. The polarization–electric field (P–E) and magnetization–magnetic field (M–H) hysteresis loops obtained indicate that both ferroelectric and ferromagnetic properties coexist in the ME composites prepared. The direct (DME) and converse magnetoelectric effects (CME) were measured only for the PZT–CFO20 (20 mol% CoFe{sub 2}O{sub 4}) composite sintered at 1100 °C for 4 h. The maximum values of ME voltage coefficient α{sub ME}(dE/dH) and ME susceptibility coefficient α{sub me} (dH/dE) were 226 mV cm{sup −1} Oe{sup −1} at frequency of 75.1 kHz and 1.15×10{sup −8} s/m at frequency of 66.8 kHz, respectively. - Highlights: • PZT–CFO composite was prepared by hydrothermal method and ceramic sintering process. • Effect of CoFe{sub 2}O{sub 4} content on the electrical and magnetic properties is studied. • CoFe{sub 2}O{sub 4} particles are uniformly distributed in the PZT matrix. • P–E and M–H hysteresis loops confirm room-temperature multiferroic characteristics. • T{sub m} shifts to higher values with the increase in the measurement frequency.

  7. Engineering Nanoscale Multiferroic Composites for Memory Applications with Atomic Layer Deposition of Pb(ZrxTi1-x)O3 Thin Films

    Science.gov (United States)

    Chien, Diana

    This work focuses on the development of atomic layer deposition (ALD) for lead zirconate titanate, Pb(ZrxTi1-x)O 3 (PZT). Leveraging the surface-reaction controlled process based on alternating self-limiting surface reactions, PZT can be synthesized not only with elemental precision to realize the desired composition (Zr/Ti = 52/48) but also with outstanding conformality. The latter enables the integration of PZT with a ferromagnetic phase to realize multiferroism (MF) and magnetoelectric (ME) effect. Since PZT is one of the best known ferroelectric and piezoelectric materials due the large displacements of the Pb ions at the morphotropic phase boundary, PZT based MF composites could lead to stronger ME coupling through strain coupling at the interface. Specifically, ALD PZT thin films were synthesized by using beta-diketonate metalorganic precursors Pb(TMHD)2, Zr(TMHD)4, and Ti(O.i-Pr) 2(TMHD)2 and H2O. The number of local cycles and global cycles were regulated to achieve the desired stoichiometry and thickness, respectively. ALD of PZT was studied to obtain (100) textured PZT on Pt (111) oriented platinized silicon substrates. In order to attain a highly oriented PZT thin film, a (100) textured PbTiO3 seed layer was required because PZT orientation is governed by nucleation. MF nanocomposites were engineered using ALD PZT thin films to achieve controlled complex nanoscale structures, enabling porosity to be studied as a new additional parameter for nanocomposite architectures to enhance ME effect. Specifically, 3--6 nm-thick ALD PZT thin films were deposited to uniformly coat the walls of mesoporous cobalt ferrite (CFO) template. The PZT/CFO nanocomposites were electrically poled ex-situ and the change in magnetic moment was measured. The inverse magnetoelectric coupling coefficient, a, was determined to be 85.6 Oe-cm/mV. The in-plane results show no significant change in magnetization (1--4%) as a function of electric field, which was expected due to the effect

  8. Lead-free (K0.5Na0.5)NbO3 thin films by pulsed laser deposition driving MEMS-based piezoelectric cantilevers

    NARCIS (Netherlands)

    Nguyen, Duc Minh; Dekkers, Jan M.; Houwman, Evert Pieter; Vu, H.T.; Vu, Hung N.; Rijnders, Augustinus J.H.M.

    2016-01-01

    Thin film capacitors of the lead-free (K0.5Na0.5)NbO3 (KNN) with (100) orientation were grown on Pt/Ti/SiO2/SOI (silicon-on-insulator) substrates by pulsed laser deposition. The films are pure phases and do not show other crystal orientations. The remnant polarization Pr, saturation polarization

  9. Structural phase transition and multiferroic properties of Bi0.8A0.2Fe0.8Mn0.2O3 (A = Ca, Sr)

    Science.gov (United States)

    Rout, Jyoshna; Choudhary, R. N. P.

    2018-05-01

    The multiferroic BiFeO3 and Bi0.8A0.2Fe0.8Mn0.2O3 (A = Ca, Sr) have been synthesized using direct mechanosynthesis. Detailed investigations were made on the influence of Ca-Mn and Sr-Mn co-substitutions on the structure change, electric and magnetic properties of the BFO. Rietveld refinement on the XRD pattern of the modified samples clarifies the structural transition from R3c:H (parent BiFeO3) to the biphasic structure (R3c: H + Pnma). Scanning electron micrographs confirmed the polycrystalline nature of the materials and each of the microstructure comprised of uniformly distributed grains with less porosity. The dielectric measurements reveal that enhancement in dielectric properties due to the reduction of oxygen vacancies by substitutional ions. Studies of frequency-dependence of impedance and related parameters exhibit that the electrical properties of the materials are strongly dependent on temperature, and bear a good correlation with its microstructure. The bulk resistance (evaluated from impedance studies) is found to decrease with increasing temperature for all the samples. The alternating current (ac) conductivity spectra show a typical signature of an ionic conducting system, and are found to obey Jonscher's universal power law. Preliminary studies of magnetic characteristics of the samples reveal enhanced magnetization for Ca-Mn co-substituted sample. The magnetoelectric coefficient as the function of applied dc magnetizing field under fixed ac magnetic field 15.368 Oe is measured and this ME coefficient αME corresponds to induction of polarization by a magnetic field.

  10. Resonant magnetoelectric response of cantilevers with magnetostrictive and piezoelectric layers on opposite sides of the substrate

    Directory of Open Access Journals (Sweden)

    Matthias C. Krantz

    2013-06-01

    Full Text Available A theory is derived for the bending-mode magnetoelectric coefficients at resonance for magnetostrictive and piezoelectric layers on opposite sides of a substrate. Results are given for the transverse ME coefficient in the Metglas-Si-AlN system with magnetic field excitation parallel and electric polarization perpendicular to the cantilever. The center-substrate layer sequence is found to produce about 50 % enhancement of the magnetoelectric effect compared to magnetoelectric bilayers on one side of a substrate. Up to about 10 % additional enhancement of the ME effect is predicted if the magnetostrictive and piezoelectric layers are separated from the substrate by spacer layers with lower Youngs modulus. Lowest order bending mode resonance frequencies are given.

  11. Electromagnetic wave propagation in time-dependent media with antisymmetric magnetoelectric coupling

    International Nuclear Information System (INIS)

    Lin, Shi-Rong; Zhang, Ruo-Yang; Ma, Yi-Rong; Jia, Wei; Zhao, Qing

    2016-01-01

    Highlights: • Time-dependent permittivity combined with antisymmetric magnetoelectric coupling will yield a novel linear birefringence. • Distinct dynamical behaviors of these two birefringent modes are analyzed. • As a new nonlinear optical effect, a scheme utilizing optical Kerr effect in moving media is proposed. - Abstract: This paper deals with electromagnetic wave propagation in time-dependent media with an antisymmetric magnetoelectric coupling and an isotropic time-dependent permittivity. We identify a new mechanism of linear birefringence, originated from the combined action of the time-dependent permittivity and the antisymmetric magnetoelectric coupling. Permittivity with linear and exponential temporal variations exemplifies the creation and control of these two distinct types of linear birefringent modes. As a novel nonlinear optical effect, a scheme utilizing optical Kerr effect in moving media is proposed for the realization of the predicted birefringence.

  12. Electromagnetic wave propagation in time-dependent media with antisymmetric magnetoelectric coupling

    Energy Technology Data Exchange (ETDEWEB)

    Lin, Shi-Rong [School of Physics, Beijing Institute of Technology, Beijing 100081 (China); Zhang, Ruo-Yang [Theoretical Physics Division, Chern Institute of Mathematics, Nankai University, Tianjin 300071 (China); Ma, Yi-Rong; Jia, Wei [School of Physics, Beijing Institute of Technology, Beijing 100081 (China); Zhao, Qing, E-mail: qzhaoyuping@bit.edu.cn [School of Physics, Beijing Institute of Technology, Beijing 100081 (China)

    2016-07-29

    Highlights: • Time-dependent permittivity combined with antisymmetric magnetoelectric coupling will yield a novel linear birefringence. • Distinct dynamical behaviors of these two birefringent modes are analyzed. • As a new nonlinear optical effect, a scheme utilizing optical Kerr effect in moving media is proposed. - Abstract: This paper deals with electromagnetic wave propagation in time-dependent media with an antisymmetric magnetoelectric coupling and an isotropic time-dependent permittivity. We identify a new mechanism of linear birefringence, originated from the combined action of the time-dependent permittivity and the antisymmetric magnetoelectric coupling. Permittivity with linear and exponential temporal variations exemplifies the creation and control of these two distinct types of linear birefringent modes. As a novel nonlinear optical effect, a scheme utilizing optical Kerr effect in moving media is proposed for the realization of the predicted birefringence.

  13. The multimodal magnetoelectric effect in the ring-shaped magnetostrictive-piezoelectric bulk composites

    Science.gov (United States)

    Radchenko, G. S.; Filippov, D. A.; Laletin, V. M.

    2015-11-01

    The theoretical and experimental investigation of the direct magnetoelectric effect in the ring-type structures made of the bulk magnetostrictive-piezoelectric composites has been presented. The analytical expression for the magnetoelectric voltage coefficient has been obtained using the effective parameters method. The frequency dependence of this parameter is also analyzed. The dependence of the resonant frequency and the amplitude of this effect of the geometrical parameters of the ring for the first and second oscillation modes are presented. The experimental investigation of the direct magnetoelectric effect for the ring-type composite specimens consisting of the nickel ferrite spinel-PZT bulk composite is done. The obtained experimental data are in good agreement with the theoretical predictions.

  14. A theory of the inverse magnetoelectric effect in layered magnetostrictive-piezoelectric structures

    Science.gov (United States)

    Filippov, D. A.; Radchenko, G. S.; Firsova, T. O.; Galkina, T. A.

    2017-05-01

    A theory of the inverse magnetoelectric effect in layered structures has been presented. The theory is based on solving the equations of elastodynamics and electrostatics separately for the magnetostrictive and piezoelectric phases, taking into account the conditions at the interface between the phases. Expressions for the coefficient of inverse magnetoelectric conversion through the parameters characterizing the magnetostrictive and piezoelectric phases have been obtained. Theoretical dependences of the inverse magnetoelectric conversion coefficient on the frequency of the alternating-current electric field for the three-layer PZT-Ni-PZT structure and the two-layer terfenol- D-PZT structure have been calculated. The results of the calculations are in good agreement with the experimental data.

  15. Growth and characterization of lead-free (K,Na)NbO3-based piezoelectric single crystals

    International Nuclear Information System (INIS)

    Liu, Hairui

    2016-01-01

    Lead-free piezoelectric materials have received increasing attention in the last decade, driven by environmental issues and health concerns. Of considerable interest is the (K,Na)NbO 3 (KNN)-based system, which possesses a relatively high Curie temperature and good piezoelectric properties. Abundant publications on KNN-based polycrystalline ceramics increased the interest in studying their single-crystalline form, based on two major concerns. The first concern refers to the negative role of grain interactions on the electromechanical response. The second concern deals with domain engineering. The relationship between external electric field direction, crystallographic orientation, and spontaneous polarization vectors for a specific structure can be more readily established in single crystals and thus offers a pathway for an in-depth understanding of fundamental mechanism and potential applications. The exciting enhancement of both piezoelectric and ferroelectric response in lead-based single crystals also encourages the further exploration of KNN-based piezoelectric crystals, as they possess the same perovskite structure. The main goal of this thesis is to find possible approaches for improved electromechanical properties in KNN-based piezoelectric single crystals. In Chapter 2, the current development of KNN-based single crystals as piezoelectrics is reviewed, following a short introduction of fundamental knowledge on piezoelectrics and ferroelectrics. Both submerged-seed solution growth and top-seeded solution growth techniques were employed to produce single crystals, as described detailed in Chapter 3. Emphasis is subsequently placed on issues of the crystal growth process, effective methods to enhance electrical properties, and crystallographic orientation-dependent electrical properties in Li-, Ta-, and/or Sb-substituted KNN single crystals. The main conclusions from the crystal growth aspect are presented in Chapter 4 and can be summarized as follows: (i

  16. Growth and characterization of lead-free (K,Na)NbO{sub 3}-based piezoelectric single crystals

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Hairui

    2016-10-19

    Lead-free piezoelectric materials have received increasing attention in the last decade, driven by environmental issues and health concerns. Of considerable interest is the (K,Na)NbO{sub 3} (KNN)-based system, which possesses a relatively high Curie temperature and good piezoelectric properties. Abundant publications on KNN-based polycrystalline ceramics increased the interest in studying their single-crystalline form, based on two major concerns. The first concern refers to the negative role of grain interactions on the electromechanical response. The second concern deals with domain engineering. The relationship between external electric field direction, crystallographic orientation, and spontaneous polarization vectors for a specific structure can be more readily established in single crystals and thus offers a pathway for an in-depth understanding of fundamental mechanism and potential applications. The exciting enhancement of both piezoelectric and ferroelectric response in lead-based single crystals also encourages the further exploration of KNN-based piezoelectric crystals, as they possess the same perovskite structure. The main goal of this thesis is to find possible approaches for improved electromechanical properties in KNN-based piezoelectric single crystals. In Chapter 2, the current development of KNN-based single crystals as piezoelectrics is reviewed, following a short introduction of fundamental knowledge on piezoelectrics and ferroelectrics. Both submerged-seed solution growth and top-seeded solution growth techniques were employed to produce single crystals, as described detailed in Chapter 3. Emphasis is subsequently placed on issues of the crystal growth process, effective methods to enhance electrical properties, and crystallographic orientation-dependent electrical properties in Li-, Ta-, and/or Sb-substituted KNN single crystals. The main conclusions from the crystal growth aspect are presented in Chapter 4 and can be summarized as follows

  17. Electrically Controllable Spontaneous Magnetism in Nanoscale Mixed Phase Multiferroics

    Energy Technology Data Exchange (ETDEWEB)

    He, Q.; Chu, Y. H.; Heron, J. T.; Yang, S. Y.; Wang, C. H.; Kuo, C. Y.; Lin, H. J.; Yu, P.; Liang, C. W.; Zeches, R. J.; Chen, C. T.; Arenholz, E.; Scholl, A.; Ramesh, R.

    2010-08-02

    The emergence of enhanced spontaneous magnetic moments in self-assembled, epitaxial nanostructures of tetragonal (T-phase) and rhombohedral phases (R-phase) of the multiferroic BiFeO{sub 3} system is demonstrated. X-ray magnetic circular dichroism based photoemission electron microscopy (PEEM) was applied to investigate the local nature of this magnetism. We find that the spontaneous magnetization of the R-phase is significantly enhanced above the canted antiferromagnetic moment in the bulk phase, as a consequence of a piezomagnetic coupling to the adjacent T-phase and the epitaxial constraint. Reversible electric field control and manipulation of this magnetic moment at room temperature is shown using a combination of piezoresponse force microscopy and PEEM studies.

  18. A review on all-perovskite multiferroic tunnel junctions

    Directory of Open Access Journals (Sweden)

    Yuewei Yin

    2017-12-01

    Full Text Available Although the basic concept was proposed only about 10 years ago, multiferroic tunnel junctions (MFTJs with a ferroelectric barrier sandwiched between two ferromagnetic electrodes have already drawn considerable interests, driven mainly by its potential applications in multi-level memories and electric field controlled spintronics. The purpose of this article is to review the recent progress of all-perovskite MFTJs. Starting from the key functional properties of the tunneling magnetoresistance, tunneling electroresistance, and tunneling electromagnetoresistance effects, we discuss the main origins of the tunneling electroresistance effect, recent progress in achieving multilevel resistance states in a single device, and the electrical control of spin polarization and transport through the ferroelectric polarization reversal of the tunneling barrier.

  19. Separating read and write units in multiferroic devices.

    Science.gov (United States)

    Roy, Kuntal

    2015-06-18

    Strain-mediated multiferroic composites, i.e., piezoelectric-magnetostrictive heterostructures, hold profound promise for energy-efficient computing in beyond Moore's law era. While reading a bit of information stored in the magnetostrictive nanomagnets using a magnetic tunnel junction (MTJ), a material selection issue crops up since magnetostrictive materials in general cannot be utilized as the free layer of the MTJ. This is an important issue since we need to achieve a high magnetoresistance for technological applications. We show here that magnetically coupling the magnetostrictive nanomagnet and the free layer e.g., utilizing the magnetic dipole coupling between them can circumvent this issue. By solving stochastic Landau-Lifshitz-Gilbert equation of magnetization dynamics in the presence of room-temperature thermal fluctuations, we show that such design can eventually lead to a superior energy-delay product.

  20. Characteristics and controllability of vortices in ferromagnetics, ferroelectrics, and multiferroics.

    Science.gov (United States)

    Zheng, Yue; Chen, W J

    2017-08-01

    Topological defects in condensed matter are attracting e significant attention due to their important role in phase transition and their fascinating characteristics. Among the various types of matter, ferroics which possess a switchable physical characteristic and form domain structure are ideal systems to form topological defects. In particular, a special class of topological defects-vortices-have been found to commonly exist in ferroics. They often manifest themselves as singular regions where domains merge in large systems, or stabilize as novel order states instead of forming domain structures in small enough systems. Understanding the characteristics and controllability of vortices in ferroics can provide us with deeper insight into the phase transition of condensed matter and also exciting opportunities in designing novel functional devices such as nano-memories, sensors, and transducers based on topological defects. In this review, we summarize the recent experimental and theoretical progress in ferroic vortices, with emphasis on those spin/dipole vortices formed in nanoscale ferromagnetics and ferroelectrics, and those structural domain vortices formed in multiferroic hexagonal manganites. We begin with an overview of this field. The fundamental concepts of ferroic vortices, followed by the theoretical simulation and experimental methods to explore ferroic vortices, are then introduced. The various characteristics of vortices (e.g. formation mechanisms, static/dynamic features, and electronic properties) and their controllability (e.g. by size, geometry, external thermal, electrical, magnetic, or mechanical fields) in ferromagnetics, ferroelectrics, and multiferroics are discussed in detail in individual sections. Finally, we conclude this review with an outlook on this rapidly developing field.

  1. Magnetoelectric antiferromagnets as platforms for the manipulation of solitons

    Science.gov (United States)

    Zarzuela, Ricardo; Kim, Se Kwon; Tserkovnyak, Yaroslav

    2018-01-01

    We study the magnetic dynamics of magnetoelectric antiferromagnetic thin films, where an unconventional boundary ferromagnetism coexists with the bulk Néel phase below the Néel temperature. The spin exchange between the two order parameters yields an effective low-energy theory that is formally equivalent to that of a ferrimagnet. Dynamics of domain walls and skyrmions are analyzed within the collective-variable approach, from which we conclude that they behave as massive particles moving in a viscous medium subjected to a gyrotropic force. We find that the film thickness can be used as a control parameter for the motion of these solitons. In this regard, it is shown that an external magnetic field can drive the dynamics of domain walls, whose terminal velocity is tunable with the sample thickness. Furthermore, the classification of the skyrmion dynamics is sensitive to the spatial modulation of the sample thickness, which can be easily engineered with the present (thin-film) deposition techniques. Current-driven spin transfer can trigger drifting orbits of skyrmions, which can be utilized as racetracks for these magnetic textures.

  2. Acoustic spin pumping in magnetoelectric bulk acoustic wave resonator

    Directory of Open Access Journals (Sweden)

    N. I. Polzikova

    2016-05-01

    Full Text Available We present the generation and detection of spin currents by using magnetoelastic resonance excitation in a magnetoelectric composite high overtone bulk acoustic wave (BAW resonator (HBAR formed by a Al-ZnO-Al-GGG-YIG-Pt structure. Transversal BAW drives magnetization oscillations in YIG film at a given resonant magnetic field, and the resonant magneto-elastic coupling establishes the spin-current generation at the Pt/YIG interface. Due to the inverse spin Hall effect (ISHE this BAW-driven spin current is converted to a dc voltage in the Pt layer. The dependence of the measured voltage both on magnetic field and frequency has a resonant character. The voltage is determined by the acoustic power in HBAR and changes its sign upon magnetic field reversal. We compare the experimentally observed amplitudes of the ISHE electrical field achieved by our method and other approaches to spin current generation that use surface acoustic waves and microwave resonators for ferromagnetic resonance excitation, with the theoretically expected values.

  3. All-Silicon Switchable Magnetoelectric Effect through Interlayer Exchange Coupling.

    Science.gov (United States)

    Liu, Hang; Sun, Jia-Tao; Fu, Hui-Xia; Sun, Pei-Jie; Feng, Y P; Meng, Sheng

    2017-07-19

    The magnetoelectric (ME) effect originating from the effective coupling between electric field and magnetism is an exciting frontier in nanoscale science such as magnetic tunneling junction (MTJ), ferroelectric/piezoelectric heterojunctions etc. The realization of switchable ME effect under external electric field in d0 semiconducting materials of single composition is needed especially for all-silicon spintronics applications because of its natural compatibility with current industry. We employ density functional theory (DFT) to reveal that the pristine Si(111)-3×3 R30° (Si3 hereafter) reconstructed surfaces of thin films with a thickness smaller than eleven bilayers support a sizeable linear ME effect with switchable direction of magnetic moment under external electric field. This is achieved through the interlayer exchange coupling effect in the antiferromagnetic regime, where the spin-up and spin-down magnetized density is located on opposite surfaces of Si3 thin films. The obtained coefficient for the linear ME effect can be four times larger than that of ferromagnetic Fe films, which fail to have the reversal switching capabilities. The larger ME effect originates from the spin-dependent screening of the spin-polarized Dirac fermion. The prediction will promote the realization of well-controlled and switchable data storage in all-silicon electronics. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  4. Acoustic spin pumping in magnetoelectric bulk acoustic wave resonator

    Energy Technology Data Exchange (ETDEWEB)

    Polzikova, N. I., E-mail: polz@cplire.ru; Alekseev, S. G.; Pyataikin, I. I.; Kotelyanskii, I. M.; Luzanov, V. A.; Orlov, A. P. [Kotel’nikov Institute of Radio Engineering and Electronics of Russian Academy of Sciences, Mokhovaya 11, building 7, Moscow, 125009 (Russian Federation)

    2016-05-15

    We present the generation and detection of spin currents by using magnetoelastic resonance excitation in a magnetoelectric composite high overtone bulk acoustic wave (BAW) resonator (HBAR) formed by a Al-ZnO-Al-GGG-YIG-Pt structure. Transversal BAW drives magnetization oscillations in YIG film at a given resonant magnetic field, and the resonant magneto-elastic coupling establishes the spin-current generation at the Pt/YIG interface. Due to the inverse spin Hall effect (ISHE) this BAW-driven spin current is converted to a dc voltage in the Pt layer. The dependence of the measured voltage both on magnetic field and frequency has a resonant character. The voltage is determined by the acoustic power in HBAR and changes its sign upon magnetic field reversal. We compare the experimentally observed amplitudes of the ISHE electrical field achieved by our method and other approaches to spin current generation that use surface acoustic waves and microwave resonators for ferromagnetic resonance excitation, with the theoretically expected values.

  5. Tunable characteristics of bending resonance frequency in magnetoelectric laminated composites

    Institute of Scientific and Technical Information of China (English)

    Chen Lei; Li Ping; Wen Yu-Mei; Zhu Yong

    2013-01-01

    As the magnetoelectric (ME) effect in piezoelectric/magnetostrictive laminated composites is mediated by mechanical deformation,the ME effect is significantly enhanced in the vicinity of resonance frequency.The bending resonance frequency (fr) of bilayered Terfenol-D/PZT (MP) laminated composites is studied,and our analysis predicts that (i) the bending resonance frequency of an MP laminated composite can be tuned by an applied dc magnetic bias (Hdc) due to the △E effect; (ii) the bending resonance frequency of the MP laminated composite can be controlled by incorporating FeCuNbSiB layers with different thicknesses.The experimental results show that with Hdc increasing from 0Oe (1 Oe=79.5775 A/m)to 700 Oe,the bending resonance frequency can be shifted in a range of 32.68 kHz ≤ fr ≤ 33.96 kHz.In addition,with the thickness of the FeCuNbSiB layer increasing from 0 μm to 90 μm,the bending resonance frequency of the MP laminated composite gradually increases from 33.66 kHz to 39.18 kHz.This study offers a method of adjusting the strength of dc magnetic bias or the thicknesses of the FeCuNbSiB layer to tune the bending resonance frequency for ME composite,which plays a guiding role in the ME composite design for real applications.

  6. A non-commutative formula for the isotropic magneto-electric response

    International Nuclear Information System (INIS)

    Leung, Bryan; Prodan, Emil

    2013-01-01

    A non-commutative formula for the isotropic magneto-electric response of disordered insulators under magnetic fields is derived using the methods of non-commutative geometry. Our result follows from an explicit evaluation of the Ito derivative with respect to the magnetic field of the non-commutative formula for the electric polarization reported in Schulz-Baldes and Teufel (2012 arXiv:1201.4812v1). The quantization, topological invariance and connection to a second Chern number of the magneto-electric response are discussed in the context of three-dimensional, disordered, time-reversal or inversion symmetric topological insulators. (paper)

  7. Thermal effects in magnetoelectric memories with stress-mediated switching

    International Nuclear Information System (INIS)

    Giordano, S; Dusch, Y; Tiercelin, N; Pernod, P; Preobrazhensky, V

    2013-01-01

    Heterostructures with magneto-electro-elastic coupling (e.g. multiferroics) are of paramount importance for developing new sensors, actuators and memories. With the progressive miniaturization of these systems it is necessary to take into account possible thermal effects, which may influence the normal operating regime. As a paradigmatic example we consider a recently introduced non-volatile memory element composed of a magnetostrictive nanoparticle embedded in a piezoelectric matrix. The distributions of the physical fields in this matrix/inclusion configuration are determined by means of the Eshelby theory, the magnetization dynamics is studied through the Landau–Lifshitz–Gilbert formalism, and the statistical mechanics is introduced with the Langevin and Fokker–Planck methodologies. As result of the combination of such techniques we determine the switching time between the states of the memory, the error probability and the energy dissipation of the writing process. They depend on the ratio k B T/v where T is the absolute temperature and v is the volume of the magnetoelastic particle. (paper)

  8. Charge, spin and orbital order in the candidate multiferroic material LuFe{sub 2}O{sub 4}

    Energy Technology Data Exchange (ETDEWEB)

    Groot, Joost de

    2012-06-28

    This thesis is a detailed study of the magnetic, structural and orbital order parameters of the candidate multiferroic material LuFe{sub 2}O{sub 4}. Multiferroic oxides with a strong magnetoelectric coupling are of high interest for potential information technology applications, but they are rare because the traditional mechanism of ferroelectricity is incompatible with magnetism. Consequently, much attention is focused on various unconventional mechanisms of ferroelectricity. Of these, ferroelectricity originating from charge ordering (CO) is particularly intriguing because it potentially combines large electric polarizations with strong magneto-electric coupling. However, examples of oxides where this mechanism occurs are exceedingly rare and none is really well understood. LuFe{sub 2}O{sub 4} is often cited as the prototypical example of CO-based ferroelectricity. In this material, the order of Fe valences has been proposed to render the triangular Fe/O bilayers polar by making one of the two layers rich in Fe{sup 2+} and the other rich in Fe{sup 3+}, allowing for a possible ferroelectric stacking of the individual bilayers. Because of this new mechanism for ferroelectricity, and also because of the high transition temperatures of charge order (T{sub CO} {proportional_to}320K) and ferro magnetism (T{sub N}{proportional_to}240 K) LuFe{sub 2}O{sub 4} has recently attracted increasing attention. Although these polar bilayers are generally accepted in the literature for LuFe{sub 2}O{sub 4}, direct proof is lacking. An assumption-free experimental determination of whether or not the CO in the Fe/O bilayers is polar would be crucial, given the dependence of the proposed mechanism of ferroelectricity from CO in LuFe{sub 2}O{sub 4} on polar bilayers. This thesis starts with a detailed characterization of the macroscopic magnetic properties, where growing ferrimagnetic contributions observed in magnetization could be ascribed to increasing oxygen off-stoichiometry. The

  9. (C6H13N)2BiI5: A One-Dimensional Lead-Free Perovskite-Derivative Photoconductive Light Absorber.

    Science.gov (United States)

    Zhang, Weichuan; Tao, Kewen; Ji, Chengmin; Sun, Zhihua; Han, Shiguo; Zhang, Jing; Wu, Zhenyue; Luo, Junhua

    2018-04-16

    Lead-free organic-inorganic hybrid perovskites have recently attracted intense interest as environmentally friendly, low-cost, chemically stable light absorbers. Here, we reported a new one-dimensional (1D) zigzag chainlike light-absorbing hybrid material of (C 6 H 13 N) 2 BiI 5 , in which the corner-sharing octahedral bismuth halide chains are surrounded by organic cations of tetramethylpiperidinium. This unique zigzag 1D hybrid perovskite-derivative material shows a narrow direct band gap of 2.02 eV and long-lived photoluminescence, which is encouraging for optoelectronic applications. Importantly, it behaves as a typical semiconducting material and displays obvious photoresponse in the visible-light range. This work opens a potential pathway for the further application of 1D lead-free hybrids.

  10. High-Pressure Band-Gap Engineering in Lead-Free Cs 2 AgBiBr 6 Double Perovskite

    Energy Technology Data Exchange (ETDEWEB)

    Li, Qian [Department of Chemistry, Southern University of Science and Technology, SUSTech, Shenzhen Guangdong 518055 P.R. China; College of Chemistry, Nankai University, Tianjin 300071 P.R. China; Wang, Yonggang [High Pressure Synergetic Consortium, HPSynC, Geophysical Laboratory, Carnegie Institution of Washington, Argonne IL 60439 USA; Pan, Weicheng [Wuhan National Laboratory for Optoelectronics, WNLO and School of Optical and Electronic Information, Huazhong University of Science and Technology, HUST, Wuhan 430074 P.R. China; Yang, Wenge [High Pressure Synergetic Consortium, HPSynC, Geophysical Laboratory, Carnegie Institution of Washington, Argonne IL 60439 USA; Zou, Bo [State Key Laboratory of Superhard Materials, Jilin University, Changchun 130012 P.R. China; Tang, Jiang [Wuhan National Laboratory for Optoelectronics, WNLO and School of Optical and Electronic Information, Huazhong University of Science and Technology, HUST, Wuhan 430074 P.R. China; Quan, Zewei [Department of Chemistry, Southern University of Science and Technology, SUSTech, Shenzhen Guangdong 518055 P.R. China

    2017-11-15

    Novel inorganic lead-free double perovskites with improved stability are regarded as alternatives to state-of-art hybrid lead halide perovskites in photovoltaic devices. The recently discovered Cs2AgBiBr6 double perovskite exhibits attractive optical and electronic features, making it promising for various optoelectronic applications. However, its practical performance is hampered by the large band gap. In this work, remarkable band gap narrowing of Cs2AgBiBr6 is, for the first time, achieved on inorganic photovoltaic double perovskites through high pressure treatments. Moreover, the narrowed band gap is partially retainable after releasing pressure, promoting its optoelectronic applications. This work not only provides novel insights into the structure–property relationship in lead-free double perovskites, but also offers new strategies for further development of advanced perovskite devices.

  11. Measurement of erosion of stainless steel by molten lead-free solder using micro-focus x-ray CT system

    International Nuclear Information System (INIS)

    Nishikawa, Hiroshi; Takemoto, Tadashi; Kang, Songai

    2009-01-01

    The severe erosion damage, which is caused by a molten lead-free solder, of wave solder equipment made into stainless steel has been encountered in operation. Then, the higher maintenance frequency and reduced life time of wave solder machine component is a serious issue in a manufacturing process. In this study, the evaluation method of erosion of stainless steel by molten lead-free solders was investigated using micro-focus X-ray systems for fluoroscopic and computed tomography (CT). As a result, it was found that the fluoroscopic image could truly reconstruct the cross-shape of the stainless steel sample after immersion test without destruction. In the case of X-ray systems for fluoroscopic and CT used in this study, three-dimensional data can be obtained. Therefore, it was possible to easily check the whole picture of the test sample after immersion test and to decide the maximum erosion depth of test sample. (author)

  12. Prediction of activities of all components in the lead-free solder systems Bi-In-Sn and Bi-In-Sn-Zn

    International Nuclear Information System (INIS)

    Tao Dongping

    2008-01-01

    The activities of components of the ternary lead-free solder systems Al-Sn-Zn at 973 K, Zn-Cu-Sn at 1023 K and Bi-In-Sn at 1000 and 1050 K have been predicted by a novel molecular interaction volume model-MIVM and the results are in good agreement with experimental data. Then the activities of all components of the Bi-In-Sn at 550 K and the Bi-In-Sn-Zn quaternary system at 700 K have been further predicted and the results are reasonable and reliable. This shows that the model may be a superior alternative for describing interfacial chemical reactions between lead-free solder alloys and common base materials and for the calculation of their phase diagrams because MIVM has certain physical meaning from the viewpoint of statistical thermodynamics and requires only two infinite dilute activity coefficients for each sub-binary system

  13. High-pressure band-gap engineering in lead-free Cs{sub 2}AgBiBr{sub 6} double perovskite

    Energy Technology Data Exchange (ETDEWEB)

    Li, Qian [Department of Chemistry, Southern University of Science and Technology, SUSTech, Shenzhen, Guangdong (China); College of Chemistry, Nankai University, Tianjin (China); Wang, Yonggang; Yang, Wenge [High Pressure Synergetic Consortium, HPSynC, Geophysical Laboratory, Carnegie Institution of Washington, Argonne, IL (United States); Pan, Weicheng; Tang, Jiang [Wuhan National Laboratory for Optoelectronics, WNLO and School of Optical and Electronic Information, Huazhong University of Science and Technology, HUST, Wuhan (China); Zou, Bo [State Key Laboratory of Superhard Materials, Jilin University, Changchun (China); Quan, Zewei [Department of Chemistry, Southern University of Science and Technology, SUSTech, Shenzhen, Guangdong (China)

    2017-12-11

    Novel inorganic lead-free double perovskites with improved stability are regarded as alternatives to state-of-art hybrid lead halide perovskites in photovoltaic devices. The recently discovered Cs{sub 2}AgBiBr{sub 6} double perovskite exhibits attractive optical and electronic features, making it promising for various optoelectronic applications. However, its practical performance is hampered by the large band gap. In this work, remarkable band gap narrowing of Cs{sub 2}AgBiBr{sub 6} is, for the first time, achieved on inorganic photovoltaic double perovskites through high pressure treatments. Moreover, the narrowed band gap is partially retainable after releasing pressure, promoting its optoelectronic applications. This work not only provides novel insights into the structure-property relationship in lead-free double perovskites, but also offers new strategies for further development of advanced perovskite devices. (copyright 2017 Wiley-VCH Verlag GmbH and Co. KGaA, Weinheim)

  14. Assessment of the effects of the Japanese shift to lead-free solders and its impact on material substitution and environmental emissions by a dynamic material flow analysis

    International Nuclear Information System (INIS)

    Fuse, Masaaki; Tsunemi, Kiyotaka

    2012-01-01

    Lead-free electronics has been extensively studied, whereas their adoption by society and their impact on material substitution and environmental emissions are not well understood. Through a material flow analysis (MFA), this paper explores the life cycle flows for solder-containing metals in Japan, which leads the world in the shift to lead-free solders in electronics. The results indicate that the shift has been progressing rapidly for a decade, and that substitutes for lead in solders, which include silver and copper, are still in the early life cycle stages. The results also show, however, that such substitution slows down during the late life cycle stages owing to long electronic product lifespans. This deceleration of material substitution in the solder life cycle may not only preclude a reduction in lead emissions to air but also accelerate an increase in silver emissions to air and water. As an effective measure against ongoing lead emissions, our scenario analysis suggests an aggressive recycling program for printed circuit boards that utilizes an existing recycling scheme. -- Highlights: ► We model the life cycle flows for solder-containing metals in Japan. ► The Japanese shift to lead-free solders progresses rapidly for a decade. ► Substitution for lead in solders slows down during the late life cycle stages. ► The deceleration of substitution precludes a reduction in lead emissions to air.

  15. Effect of poling process on piezoelectric properties of BCZT - 0.08 wt.% CeO{sub 2} lead-free ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Chandrakala, E.; Praveen, J. Paul; Das, Dibakar, E-mail: ddse@uohyd.ernet.in [School of Engineering Sciences & Technology, University of Hyderabad, Hyderabad 500046 (India)

    2016-05-06

    The properties of lead free piezoelectric materials can be tuned by suitable doping in the A and B sites of the perovskite structure. In the present study, cerium has been identified as a dopant to investigate the piezoelectric properties of lead-free BCZT system. BCZT – 0.08 wt.%CeO{sub 2} lead-free ceramics have been synthesized using sol-gel technique and the effects of CeO{sub 2} dopant on their phase structure and piezoelectric properties were investigated systematically. Poling conditions, such as temperature, electric field, and poling time have been optimized to get enhanced piezoelectric response. The optimized poling conditions (50°C, 3Ec and 30min) resulted in high piezoelectric charge coefficient d{sub 33} ~ 670pC/N, high electromechanical coupling coefficient k{sub p} ~ 60% and piezoelectric voltage coefficient g{sub 33} ~ 14 mV.m/N for BCZT – 0.08wt.% CeO{sub 2} ceramics.

  16. Growth and characterization of epitaxial thin films and multiferroic heterostructures of ferromagnetic and ferroelectric materials

    Science.gov (United States)

    Mukherjee, Devajyoti

    Multiferroic materials exhibit unique properties such as simultaneous existence of two or more of coupled ferroic order parameters (ferromagnetism, ferroelectricity, ferroelasticity or their anti-ferroic counterparts) in a single material. Recent years have seen a huge research interest in multiferroic materials for their potential application as high density non-volatile memory devices. However, the scarcity of these materials in single phase and the weak coupling of their ferroic components have directed the research towards multiferroic heterostructures. These systems operate by coupling the magnetic and electric properties of two materials, generally a ferromagnetic material and a ferroelectric material via strain. In this work, horizontal heterostructures of composite multiferroic materials were grown and characterized using pulsed laser ablation technique. Alternate magnetic and ferroelectric layers of cobalt ferrite and lead zirconium titanate, respectively, were fabricated and the coupling effect was studied by X-ray stress analysis. It was observed that the interfacial stress played an important role in the coupling effect between the phases. Doped zinc oxide (ZnO) heterostructures were also studied where the ferromagnetic phase was a layer of manganese doped ZnO and the ferroelectric phase was a layer of vanadium doped ZnO. For the first time, a clear evidence of possible room temperature magneto-elastic coupling was observed in these heterostructures. This work provides new insight into the stress mediated coupling mechanisms in composite multiferroics.

  17. Origin of Ferrimagnetism and Ferroelectricity in Room-Temperature Multiferroic ɛ -Fe2O3

    Science.gov (United States)

    Xu, K.; Feng, J. S.; Liu, Z. P.; Xiang, H. J.

    2018-04-01

    Exploring and identifying room-temperature multiferroics is critical for developing better nonvolatile random-access memory devices. Recently, ɛ -Fe2O3 was found to be a promising room-temperature multiferroic with a large polarization and magnetization. However, the origin of the multiferroicity in ɛ -Fe2O3 is still puzzling. In this work, we perform density-functional-theory calculations to reveal that the spin frustration between tetrahedral-site Fe3 + spins gives rise to the unexpected ferrimagnetism. For the ferroelectricity, we identify a low-energy polarization switching path with an energy barrier of 85 meV /f .u . by performing a stochastic surface walking simulation. The switching of the ferroelectric polarization is achieved by swapping the tetrahedral Fe ion with the octahedral Fe ion, different from the usual case (e.g., in BaTiO3 and BiFeO3 ) where the coordination number remains unchanged after the switching. Our results not only confirm that ɛ -Fe2O3 is a promising room-temperature multiferroic but also provide guiding principles to design high-performance multiferroics.

  18. Active damping of multiferroic composite plates using 1-3 piezoelectric composites

    Science.gov (United States)

    Kattimani, S. C.

    2017-12-01

    A layer-wise shear deformation theory is used to analyze the smart damping of multiferroic composite or magneto-electro-elastic (MEE) plates. The intent of this analysis is to investigate the need for incorporating additional smart elements for controlling the vibrations of multiferroic composite plates. Active constrained layer damping (ACLD) treatment has been incorporated to alleviate the vibration of MEE plate. A layer of viscoelastic material is used as constrained layer for the ACLD treatment. The coupled constitutive equations of multiferroic (ferroelectric and ferromagnetic) composite materials along with the total potential energy principle are used to derive the finite element formulation for the overall multiferroic or MEE plate. Maxwell’s electrostatic and electromagnetic relations are used to compute the electric and magnetic potential distribution. Influence of obliquely reinforced piezoelectric fibers in the piezoelectric layer of the ACLD treatment has also been investigated. In order to investigate the importance of using ACLD treatment for an active damping of multiferroic or MEE plate, an active control of MEE plate has also been analyzed by providing the control voltage directly to the piezoelectric layers of the MEE substrate plate without using the ACLD treatment. The present study suggests that for an optimal control of MEE plates, the smartness element such as the ACLD treatment is essentially required.

  19. Stress induced magnetic-domain evolution in magnetoelectric composites

    Science.gov (United States)

    Trivedi, Harsh; Shvartsman, Vladimir V.; Lupascu, Doru C.; Medeiros, Marco S. A.; Pullar, Robert C.

    2018-06-01

    Local observation of the stress mediated magnetoelectric (ME) effect in composites has gained a great deal of interest over the last decades. However, there is an apparent lack of rigorous methods for a quantitative characterization of the ME effect at the local scale, especially in polycrystalline microstructures. In the present work, we address this issue by locally probing the surface magnetic state of barium titante–hexagonal barium ferrite (BaTiO3–BaFe12O19) ceramic composites using magnetic force microscopy (MFM). The effect of the piezoelectrically induced local stress on the magnetostrictive component (BaFe12O19, BaM) was observed in the form of the evolution of the magnetic domains. The local piezoelectric stress was induced by applying a voltage to the neighboring BaTiO3 grains, using a conductive atomic force microscopy tip. The resulting stochastic evolution of magnetic domains was studied in the context of the induced magnetoelastic anisotropy. In order to overcome the ambiguity in the domain changes observed by MFM, certain generalizations about the observed MFM contrast are put forward, followed by application of an algorithm for extracting the average micromagnetic changes. An average change in domain wall thickness of 50 nm was extracted, giving a lower limit on the corresponding induced magnetoelastic anisotropy energy. Furthermore, we demonstrate that this induced magnetomechanical energy is approximately equal to the K1 magnetocrystalline anisotropy constant of BaM, and compare it with a modeled value of applied elastic energy density. The comparison allowed us to judge the quality of the interfaces in the composite system, by roughly gauging the energy conversion ratio.

  20. Field-induced reentrant magnetoelectric phase in LiNiPO4

    DEFF Research Database (Denmark)

    Toft-Petersen, Rasmus; Fogh, Ellen; Kihara, Takumi

    2017-01-01

    Using pulsed magnetic fields up to 30 T we have measured the bulk magnetization and electrical polarization of LiNiPO4 and have studied its magnetic structure by time-of-flight neutron Laue diffraction. Our data establish the existence of a reentrant magnetoelectric phase between 19 T and 21 T. W...

  1. Nonlinear magnetoelectric effect in paraelectric state of Co4Nb2O9 single crystal

    Czech Academy of Sciences Publication Activity Database

    Cao, Ym.; Deng, Gc.; Beran, Přemysl; Feng, Zj.; Kang, Bj.; Zhang, Jc.; Guiblin, N.; Dkhil, B.; Ren, W.; Cao, Sx.

    2017-01-01

    Roč. 7, č. 10 (2017), č. článku 14079. ISSN 2045-2322 Institutional support: RVO:61389005 Keywords : magnetoelectric * single crystal * neutron diffraction Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 4.259, year: 2016

  2. Dynamic Magnetostriction of CoFe2 O4 and Its Role in Magnetoelectric Composites

    Science.gov (United States)

    Aubert, A.; Loyau, V.; Pascal, Y.; Mazaleyrat, F.; LoBue, M.

    2018-04-01

    Applications of magnetostrictive materials commonly involve the use of the dynamic deformation, i.e., the piezomagnetic effect. Usually, this effect is described by the strain derivative ∂λ /∂H , which is deduced from the quasistatic magnetostrictive curve. However, the strain derivative might not be accurate to describe dynamic deformation in semihard materials as cobalt ferrite (CFO). To highlight this issue, dynamic magnetostriction measurements of cobalt ferrite are performed and compared with the strain derivative. The experiment shows that measured piezomagnetic coefficients are much lower than the strain derivative. To point out the direct application of this effect, low-frequency magnetoelectric (ME) measurements are also conducted on bilayers CFO /Pb (Zr ,Ti )O3 . The experimental data are compared with calculated magnetoelectric coefficients which include a measured dynamic coefficient and result in very low relative error (measured for several amplitudes of the alternating field Hac, and a nonlinear response is revealed. Based on these results, a trilayer CFO/Pb (Zr ,Ti )O3 /CFO is made exhibiting a high magnetoelectric coefficient of 578 mV /A (approximately 460 mV /cm Oe ) in an ac field of 38.2 kA /m (about 48 mT) at low frequency, which is 3 times higher than the measured value at 0.8 kA /m (approximately 1 mT). We discuss the viability of using semihard materials like cobalt ferrite for dynamic magnetostrictive applications such as the magnetoelectric effect.

  3. An easy way to measure accurately the direct magnetoelectric voltage coefficient of thin film devices

    Energy Technology Data Exchange (ETDEWEB)

    Poullain, Gilles, E-mail: gilles.poullain@ensicaen.fr; More-Chevalier, Joris; Cibert, Christophe; Bouregba, Rachid

    2017-01-15

    Tb{sub x}Dy{sub 1−x}Fe{sub 2}/Pt/Pb(Zr{sub x}, Ti{sub 1−x})O{sub 3} thin films were grown on Pt/TiO{sub 2}/SiO{sub 2}/Si substrate by multi-target sputtering. The magnetoelectric voltage coefficient α{sup Η}{sub ΜΕ} was determined at room temperature using a lock-in amplifier. By adding, in series in the circuit, a capacitor of the same value as that of the device under test, we were able to demonstrate that the magnetoelectric device behaves as a voltage source. Furthermore, a simple way to subtract the stray voltage arising from the flow of eddy currents in the measurement set-up, is proposed. This allows the easy and accurate determination of the true magnetoelectric voltage coefficient. A large α{sup Η}{sub ΜΕ} of 8.3 V/cm. Oe was thus obtained for a Terfenol-D/Pt/PZT thin film device, without DC magnetic field nor mechanical resonance. - Highlights: • Magnetoelectric device behaves as a voltage source. • A simple way to subtract eddy currents during the measurement, is proposed.

  4. Electrically driven magnetic relaxation in multiferroic LuFe2O4

    International Nuclear Information System (INIS)

    Wang Fen; Li Changhui; Zou Tao; Liu Yi; Sun Young

    2010-01-01

    We report the electrical control of magnetization in multiferroic LuFe 2 O 4 by applying short current pulses. The magnitude of the induced magnetization change depends on the pulse width and current density. The voltage variation during the applied current pulses evidences an electric-field-induced breakdown of charge order and excludes the role of Joule heating. This current driven magnetization change can be interpreted with a three-temperature model in which the delocalized electrons accelerate spin relaxation through a strong spin-charge coupling inherent to multiferroicity. The electrically assisted magnetic relaxation provides a new approach for electrical control of magnetization.

  5. Multicaloric effect in bi-layer multiferroic composites

    International Nuclear Information System (INIS)

    Vopson, M. M.; Zhou, D.; Caruntu, G.

    2015-01-01

    The multicaloric effect was theoretically proposed in 2012 and, despite numerous follow up studies, the effect still awaits experimental confirmation. The main limitation is the fact that the multicaloric effect is only observed at a temperature equal to the transition temperature of the magnetic and electric phases coexisting within a multiferroic (MF) (i.e., T ≈ T c m  ≈ T c e ). Such condition is hard to fulfill in single phase MFs and a solution is to develop suitable composite MF materials. Here, we examine the multicaloric effect in a bi-layer laminated composite MF in order to determine the optimal design parameters for best caloric response. We show that magnetically induced multicaloric effect requires magnetic component of heat capacity smaller than that of the electric phase, while the layer thickness of the magnetic phase must be at least 5 times the thickness of the electric phase. The electrically induced multicaloric effect requires the magnetic layer to be 10% of the electric phase thickness, while its heat capacity must be larger than that of the electric phase. These selection rules are generally applicable to bulk as well as thin film MF composites for optimal multicaloric effect

  6. Heat-Assisted Multiferroic Solid-State Memory.

    Science.gov (United States)

    Lepadatu, Serban; Vopson, Melvin M

    2017-08-25

    A heat-assisted multiferroic solid-state memory design is proposed and analysed, based on a PbNbZrSnTiO₃ antiferroelectric layer and Ni 81 Fe 19 magnetic free layer. Information is stored as magnetisation direction in the free layer of a magnetic tunnel junction element. The bit writing process is contactless and relies on triggering thermally activated magnetisation switching of the free layer towards a strain-induced anisotropy easy axis. A stress is generated using the antiferroelectric layer by voltage-induced antiferroelectric to ferroelectric phase change, and this is transmitted to the magnetic free layer by strain-mediated coupling. The thermally activated strain-induced magnetisation switching is analysed here using a three-dimensional, temperature-dependent magnetisation dynamics model, based on simultaneous evaluation of the stochastic Landau-Lifshitz-Bloch equation and heat flow equation, together with stochastic thermal fields and magnetoelastic contributions. The magnetisation switching probability is calculated as a function of stress magnitude and maximum heat pulse temperature. An operating region is identified, where magnetisation switching always occurs, with stress values ranging from 80 to 180 MPa, and maximum temperatures normalised to the Curie temperature ranging from 0.65 to 0.99.

  7. Progress in Dual (Piezoelectric-Magnetostrictive Phase Magnetoelectric Sintered Composites

    Directory of Open Access Journals (Sweden)

    Rashed Adnan Islam

    2012-01-01

    presented which will lead to development of high-performance magnetoelectric materials.

  8. Electrocaloric effect and luminescence properties of lanthanide doped (Na1/2Bi1/2)TiO3 lead free materials

    International Nuclear Information System (INIS)

    Zannen, M.; Lahmar, A.; Asbani, B.; El Marssi, M.; Khemakhem, H.; Kutnjak, Z.; Es Souni, M.

    2015-01-01

    Polycrystalline lead-free Sodium Bismuth Titanate (NBT) ferroelectric ceramics doped with rare earth (RE) element are prepared using solid state reaction method. Optical, ferroelectric, and electrocaloric properties were investigated. The introduction of RE 3+ ions in the NBT host lattice shows different light emissions over the wavelength range from visible to near infrared region. The ferroelectric P-E hysteresis loops exhibit an antiferroelectric-like character near room temperature indicating possible existence of a morphotropic phase boundary. The enhanced electrocaloric response was observed in a broad temperature range due to nearly merged phase transitions. Coexistence of optical and electrocaloric properties is very promising for photonics or optoelectronic device applications

  9. Structural defects in multiferroic BiMnO3 studied by transmission electron microscopy and electron energy-loss spectroscopy

    International Nuclear Information System (INIS)

    Yang, H.; Chi, Z. H.; Yao, L. D.; Zhang, W.; Li, F. Y.; Jin, C. Q.; Yu, R. C.

    2006-01-01

    The multiferroic material BiMnO 3 synthesized under high pressure has been systematically studied by transmission electron microscopy and electron energy-loss spectroscopy, and some important structural defects are revealed in this multiferroic material. The frequently observed defects are characterized to be Σ3(111) twin boundaries, Ruddlesden-Popper [Acta Crystallogr. 11, 54 (1958)] antiphase boundaries, and a p p superdislocations connected with a small segment of Ruddlesden-Popper defect. These defects are present initially in the as-synthesized sample. In addition, we find that ordered voids (oxygen vacancies) are easily introduced into the multiferroic BiMnO 3 by electron-beam irradiation

  10. Internal friction and longitudinal modulus behaviour of multiferroic PbZr0.52Ti0.48O3+Ni0.93Co0.02Mn0.05Fe1.95O4-δ particulate composites

    International Nuclear Information System (INIS)

    Ramana, M Venkata; Sreenivasulu, G; Reddy, N Ramamanohar; Kumar, K V Siva; Murty, B S; Murthy, V R K

    2007-01-01

    Multiferroic particulate composites with composition xNi 0.93 Co 0.02 Mn 0.5 Fe 1.95 O 4-δ + (1 - x)PbZr 0.52 Ti 0.48 O 3 where the molar fraction x varies as 0, 0.1, 0.2, 0.3, 0.4 and 0.5 were prepared by the conventional ceramic method. The presence of two phases was confirmed by x-ray diffraction and scanning electron microscopy. The temperature variation of the longitudinal modulus (L) and the internal friction (Q -1 ) of these particulate composites at 104.387 kHz was studied in the wide temperature range 30-420 deg. C. The temperature variation of the longitudinal modulus (L) in each composition of these particulate composites showed two abrupt minima. One minimum coincided with the ferroelectric-paraelectric Curie transition temperature (θ E ) and the other with the ferrimagnetic-paramagnetic Curie transition (θ M ) temperature. The internal friction (Q -1 ) measurements also showed two sharp peaks in each composition corresponding to those temperatures where the minima were noticed in the temperature variation of the longitudinal modulus behaviour. The Curie transition temperature of pure ferrite was found to be 560 deg. C. Addition of 10% of ferrite to ferroelectric in a magnetoelectric (ME) composite resulted in a 360 deg. C fall in θ M and with a further increase in ferrite content the θ M variation was found to be very nominal. However, no significant ferroelectric Curie transition temperature shift could be noticed. This behaviour is explained in the light of structural phase transitions in these multiferroic particulate composites. These ME composites were prepared with a view to using them as ME sensors and transducers

  11. Lead-free Ba0.8Ca0.2(ZrxTi1−x)O3 ceramics with large electrocaloric effect

    International Nuclear Information System (INIS)

    Asbani, B.; Dellis, J.-L.; Lahmar, A.; Gagou, Y.; El Marssi, M.; Courty, M.; Djellab, K.; Amjoud, M.; Mezzane, D.; Kutnjak, Z.

    2015-01-01

    The electrocaloric effect was investigated in lead-free Zr doped Ba 0.8 Ca 0.2 (Zr x Ti 1−x )O 3 (BCTZ) ceramics synthesized by a conventional sintering process. Room-temperature x-ray diffraction analysis showed that the tetragonal structure is obtained in BCTZ for x ≤ 0.08 and a pseudo cubic phase for x > 0.08. The dielectric spectroscopy and calorimetry revealed that the Curie temperature decreases as a consequence of Zr doping and that the BCTZ exhibits a first order ferroelectric phase transition. The electrocaloric effect was determined by the calculation of the electrocaloric change of temperature (ΔT) using the Maxwell relation based on the P–E hysteresis loops measured at different temperatures. A large electrocaloric responsivity ΔT/ΔE = 0.34 × 10 −6  Km/V was found for x = 0.04, which significantly exceeds of values found so far in other lead-free electrocaloric materials

  12. First-principles study of electronic and optical properties of lead-free double perovskites Cs2NaBX6 (B = Sb, Bi; X = Cl, Br, I)

    Science.gov (United States)

    Zhao, Shuai; Yamamoto, Kumiko; Iikubo, Satoshi; Hayase, Shuzi; Ma, Tingli

    2018-06-01

    Organolead halide perovskite is regarded as the most promising light-harvesting material for next-generation solar cells; however, the intrinsic instability and toxicity of lead are still of great concern. Bismuth is ecofriendly and has electronic properties similar to those of lead, which has gradually attracted interest for optoelectronic applications. However, the valence state of bismuth is different from that of lead, eliminating the possibility of replacing lead by bismuth in organolead halide perovskites. To address this matter, one feasible strategy is to construct B-site double perovskites by the combination of Bi3+ and B+ in 1:1 ratio. In this work, lead-free halide double perovskites of the form Cs2NaBX6 (B = Sb, Bi; X = Cl, Br, I) were investigated by first-principles calculations. The electronic properties, optical absorption coefficients, and thermodynamic stability of these compounds were investigated to ascertain their potential application in solar energy conversion. The results provide theoretical support for the exploration of lead-free perovskite materials in potential optoelectronic applications.

  13. Lead-free soldering: Investigation of the Cu-Sn-Sb system along the Sn:Sb = 1:1 isopleth

    Energy Technology Data Exchange (ETDEWEB)

    Yuan, Y. [State Key Laboratory of Powder Metallurgy, Central South University, Changsha, Hunan 410083 (China); Department of Chemistry and Industrial Chemistry, University of Genoa, INSTM UdR Genoa, Via Dodecaneso 31, I-16146 Genoa (Italy); Borzone, G., E-mail: borzone@chimica.unige.it [Department of Chemistry and Industrial Chemistry, University of Genoa, INSTM UdR Genoa, Via Dodecaneso 31, I-16146 Genoa (Italy); Zanicchi, G.; Delsante, S. [Department of Chemistry and Industrial Chemistry, University of Genoa, INSTM UdR Genoa, Via Dodecaneso 31, I-16146 Genoa (Italy)

    2011-02-03

    Research highlights: > In the electronics industry, the solder alloys commonly used for assembly belong to the Sn-Pb system. Fulfilment of the EU RoHS (reduction of hazardous substances) requires the development of new lead-free alloys for applications in electronics, with the same or possibly better characteristics than the traditional Sn-Pb alloys. > This research concerns the investigation of the constitutional properties of the Cu-Sn-Sb system which is considered as lead-free replacement for high-temperature applications. - Abstract: The Cu-Sn-Sb system has been experimentally investigated by a combination of optical microscopy, differential scanning calorimetry (DSC) and electron probe microanalysis (EPMA). DSC was used to identify a total number of five invariant ternary reactions and the Sn:Sb = 1:1 isopleth section up to 65 at.% Cu was constructed by combining the DSC data with the EPMA analyses of annealed alloys and literature information. The composition limits of the binary phases were detected.

  14. Electrochemical Behavior of Sn-9Zn- xTi Lead-Free Solders in Neutral 0.5M NaCl Solution

    Science.gov (United States)

    Wang, Zhenghong; Chen, Chuantong; Jiu, Jinting; Nagao, Shijo; Nogi, Masaya; Koga, Hirotaka; Zhang, Hao; Zhang, Gong; Suganuma, Katsuaki

    2018-05-01

    Electrochemical techniques were employed to study the electrochemical corrosion behavior of Sn-9Zn- xTi ( x = 0, 0.05, 0.1, 0.2 wt.%) lead-free solders in neutral 0.5M NaCl solution, aiming to figure out the effect of Ti content on the corrosion properties of Sn-9Zn, providing information for the composition design of Sn-Zn-based lead-free solders from the perspective of corrosion. EIS results reveal that Ti addition was involved in the corrosion product layer and changed electrochemical interface behavior from charge transfer control process to diffusion control process. The trace amount of Ti addition (0.05 wt.%) can refine the microstructure and improve the corrosion resistance of Sn-9Zn solder, evidenced by much lower corrosion current density ( i corr) and much higher total resistance ( R t). Excess Ti addition (over 0.1 wt.%) led to the formation of Ti-containing IMCs, which were confirmed as Sn3Ti2 and Sn5Ti6, deteriorating the corrosion resistance of Sn-9Zn- xTi solders. The main corrosion products were confirmed as Sn3O(OH)2Cl2 mixed with small amount of chlorine/oxide Sn compounds.

  15. Large Piezoelectric Strain with Superior Thermal Stability and Excellent Fatigue Resistance of Lead-Free Potassium Sodium Niobate-Based Grain Orientation-Controlled Ceramics.

    Science.gov (United States)

    Quan, Yi; Ren, Wei; Niu, Gang; Wang, Lingyan; Zhao, Jinyan; Zhang, Nan; Liu, Ming; Ye, Zuo-Guang; Liu, Liqiang; Karaki, Tomoaki

    2018-03-19

    Environment-friendly lead-free piezoelectric materials with high piezoelectric response and high stability in a wide temperature range are urgently needed for various applications. In this work, grain orientation-controlled (with a 90% ⟨001⟩ c -oriented texture) (K,Na)NbO 3 -based ceramics with a large piezoelectric response ( d 33 *) = 505 pm V -1 and a high Curie temperature ( T C ) of 247 °C have been developed. Such a high d 33 * value varies by less than 5% from 30 to 180 °C, showing a superior thermal stability. Furthermore, the high piezoelectricity exhibits an excellent fatigue resistance with the d 33 * value decreasing within only by 6% at a field of 20 kV cm -1 up to 10 7 cycles. These exceptional properties can be attributed to the vertical morphotropic phase boundary and the highly ⟨001⟩ c -oriented textured ceramic microstructure. These results open a pathway to promote lead-free piezoelectric ceramics as a viable alternative to lead-based piezoceramics for various practical applications, such as actuators, transducers, sensors, and acoustic devices, in a wide temperature range.

  16. Design and Development for Capacitive Humidity Sensor Applications of Lead-Free Ca,Mg,Fe,Ti-Oxides-Based Electro-Ceramics with Improved Sensing Properties via Physisorption

    Science.gov (United States)

    Tripathy, Ashis; Pramanik, Sumit; Manna, Ayan; Bhuyan, Satyanarayan; Azrin Shah, Nabila Farhana; Radzi, Zamri; Abu Osman, Noor Azuan

    2016-01-01

    Despite the many attractive potential uses of ceramic materials as humidity sensors, some unavoidable drawbacks, including toxicity, poor biocompatibility, long response and recovery times, low sensitivity and high hysteresis have stymied the use of these materials in advanced applications. Therefore, in present investigation, we developed a capacitive humidity sensor using lead-free Ca,Mg,Fe,Ti-Oxide (CMFTO)-based electro-ceramics with perovskite structures synthesized by solid-state step-sintering. This technique helps maintain the submicron size porous morphology of the developed lead-free CMFTO electro-ceramics while providing enhanced water physisorption behaviour. In comparison with conventional capacitive humidity sensors, the presented CMFTO-based humidity sensor shows a high sensitivity of up to 3000% compared to other materials, even at lower signal frequency. The best also shows a rapid response (14.5 s) and recovery (34.27 s), and very low hysteresis (3.2%) in a 33%–95% relative humidity range which are much lower values than those of existing conventional sensors. Therefore, CMFTO nano-electro-ceramics appear to be very promising materials for fabricating high-performance capacitive humidity sensors. PMID:27455263

  17. High frequency transducer for vessel imaging based on lead-free Mn-doped (K0.44Na0.56)NbO3 single crystal

    Science.gov (United States)

    Ma, Jinpeng; Xue, Saidong; Zhao, Xiangyong; Wang, Feifei; Tang, Yanxue; Duan, Zhihua; Wang, Tao; Shi, Wangzhou; Yue, Qingwen; Zhou, Huifang; Luo, Haosu; Fang, Bijun

    2017-08-01

    We report a high frequency ultrasonic transducer up to 50 MHz for vessel imaging based on a lead-free (K0.44Na0.56)NbO3-0.5 mol. % Mn (Mn-KNN) single crystal, which has a high electromechanical coupling coefficient kt of 0.64 and a large thickness frequency constant Nt of 3210 kHz . mm. The Krimholtz, Leedom, and Mattaei (KLM) equivalent circuit model was utilized to simulate and optimize the pulse-echo response combined with PiezoCAD software. Theoretically, a high -6 dB bandwidth of 74.94% was obtained at a center frequency of 50.47 MHz and optimized matching conditions. The experimental results showed a center frequency of 51.8 MHz with a -6 dB bandwidth of 70.2%. The excellent global performance makes this lead-free single-crystal transducer quite potential in an environmentally friendly vessel imaging transducer.

  18. Preparation and piezoelectric properties of (K0.5Na0.5)NbO3 lead-free piezoelectric ceramics with pressure-less sintering

    International Nuclear Information System (INIS)

    Du Hongliang; Li Zhimin; Tang Fusheng; Qu Shaobo; Pei Zhibin; Zhou Wancheng

    2006-01-01

    Lead-free piezoelectric ceramics (K 0.5 Na 0.5 )NbO 3 (abbreviated as KNN) with the relative density of 97.6% have been synthesized by press-less sintering owing to the careful control of processing conditions. The phase structure of KNN ceramics with different sintering temperature and heating rate was analyzed. Results show that the pure perovskite phase with orthorhombic symmetry is in all ceramics specimens. The effect of heating rate and sintering temperature on microstructure and piezoelectric properties of KNN ceramics was investigated. The densification behavior and piezoelectric properties of KNN ceramics were enhanced by improving heating rate and sintering temperature. Pure KNN ceramics sintered at 1120 deg. C with heating rate of 5 deg. C/min showed optimized densification and piezoelectric properties (ρ = 4.4 g/cm 3 , d 33 = 120 pC/N -1 , k p = 0.40 and T c = 400 deg. C). The results show that KNN is a promising candidate for lead-free piezoelectric ceramics

  19. Structural Anomalies and Multiferroic Behavior in Magnetically Frustrated TbMn2O5

    NARCIS (Netherlands)

    Chapon, L.C.; Blake, G.R.; Gutmann, M.J.; Park, S.; Hur, N.; Radaelli, P.G.; Cheong, S-W.

    2004-01-01

    We have studied the magnetostructural phase diagram of multiferroic TbMn2O5 as a function of temperature and magnetic field by neutron diffraction. Dielectric and magnetic anomalies are found to be associated with steps in the magnetic propagation vector, including a rare example of a

  20. Induction of novel macroscopic properties by local symmetry violations in spin-spiral multiferroics

    Science.gov (United States)

    Meier, D.; Leo, N.; Becker, P.; Bohaty, L.; Ramesh, R.; Fiebig, M.

    2011-03-01

    Incommensurate (IC) structures are omnipresent in strongly correlated electron systems as high-TC superconductors, CMR manganites, as well as multiferroics. In each case they are origin of a pronounced symmetry reduction reflecting the complexity of the underlying microscopic interactions. Macroscopically, this can lead to new phases and possibilities to gain control of the host material. Here we report how the IC nature of a spin-spiral multiferroic induces new physical properties by renormalizing the relevant length scales of the system. Local symmetry violations directly manifest in the macroscopic response of the material and co-determine the multiferroic order giving rise to additional domain states. These usually hidden degrees of freedom become visible when non-homogenous fields are applied and condition for instance the second harmonic generation. Our study shows that incommensurabilities play a vital role in the discussion of the physical properties of multiferroics -- they represent a key ingredient for further enhancing the functionality of this class of materials. This work was supported by the DFG through the SFB 608. D.M. thanks the AvH for financial support.

  1. A multiferroic material to search for the permanent electric dipole moment of the electron

    Czech Academy of Sciences Publication Activity Database

    Rushchanskii, K.Z.; Kamba, Stanislav; Goian, Veronica; Vaněk, Přemysl; Savinov, Maxim; Prokleška, J.; Nuzhnyy, Dmitry; Knížek, Karel; Laufek, F.; Eckel, S.; Lamoreaux, S.K.; Sushkov, A.; Ležaič, M.; Spaldin, N.A.

    2010-01-01

    Roč. 9, č. 8 (2010), s. 649-654 ISSN 1476-1122 R&D Projects: GA ČR(CZ) GA202/09/0682 Institutional research plan: CEZ:AV0Z10100520 Keywords : multiferroics * electric dipole moment of the electron * dielectric and magnetic properties Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 29.897, year: 2010

  2. The magnetic and multiferroic properties in BiMnO{sub 3}

    Energy Technology Data Exchange (ETDEWEB)

    Zhai, Liang-Jun, E-mail: zhailiangjun@jsut.edu.cn [The School of Mathematics and Physics, Jiangsu University of Technology, Changzhou 213001 (China); Wang, Huai-Yu [Department of Physics, Tsinghua University, Beijing 100084 (China)

    2017-03-15

    In this paper, the magnetic and multiferroic properties in the multiferroic material BiMnO{sub 3} are studied. A Heisenberg type Hamiltonian for BiMnO{sub 3} is proposed, in which the nearest and farther neighbors are considered. Thermodynamic quantities such as magnetization and magnetic susceptibility for different magnetic orderings under high pressure or magnetic field are calculated, and the simulation results fit the experimental results. Farther neighboring exchanges can result in the coexistence of the ferromagnetic ordering and certain antiferromagnetic ordering with no centrosymmetry. Our study demonstrates that the BiMnO{sub 3} should be the type-II multiferroic, and the ferromagnetic and ferroelectric orderings could coexist. The magnetic field control of ferroelectric polarization is also studied. The ferroelectric polarization is always suppressed by the external magnetic field. - Highlights: • A Hamiltonian including the nearest and farther neighbors of BiMnO{sub 3} is proposed. • Thermodynamic quantities for different magnetic orderings are calculated. • It is shown that BiMnO{sub 3} should be the type-II multiferroic. • The obtained results fit the experimental results quite well. • The mechanism of magnetic control of polarization is also studied.

  3. Ultrathin Limit of Exchange Bias Coupling at Oxide Multiferroic/Ferromagnetic Interfaces

    NARCIS (Netherlands)

    Huijben, Mark; Yu, P.; Martin, L.W.; Molegraaf, Hajo; Chu, Y.H.; Holcomb, M.B.; Balke, N.; Rijnders, Augustinus J.H.M.; Ramesh, R.

    2013-01-01

    Exchange bias coupling at the multiferroic- ferromagnetic interface in BiFeO3/La0.7Sr0.3MnO3 heterostructures exhibits a critical thickness for ultrathin BiFeO3 layers of 5 unit cells (2 nm). Linear dichroism measurements demonstrate the dependence on the BiFeO3 layer thickness with a strong

  4. Lieb-Mattis ferrimagnetic superstructure and superparamagnetism in Fe-based double perovskite multiferroics

    Czech Academy of Sciences Publication Activity Database

    Kuzian, R. O.; Laguta, Valentyn; Richter, J.

    2014-01-01

    Roč. 90, č. 13 (2014), "134415-1"-"134415-13" ISSN 1098-0121 R&D Projects: GA ČR GA13-11473S Institutional support: RVO:68378271 Keywords : multiferroics * superantiferromagnetism * DFT calculations Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 3.736, year: 2014

  5. Multiferroic properties of Pb2Fe2O5 ceramics

    International Nuclear Information System (INIS)

    Wang, Min; Tan, Guolong

    2011-01-01

    Research highlights: → Simultaneous occurrence of ferromagnetism and ferroelectricity in Pb 2 Fe 2 O 5 ceramics. → The off-centers of shifted Pb 2+ ions as well as the FeO 6 octahedra in the 'Pb 2 Fe 2 O 5 ' lead to a ferroelectric polarization. → Pb 2 Fe 2 O 5 ceramic demonstrates ferromagnetic order state due to the spin arrangement in the double chains of FeO 5 tetrahedral pyramids. -- Abstract: Pb 2 Fe 2 O 5 (PFO) powders in monoclinic structure have been synthesized using lead acetate in glycerin and ferric acetylacetonate as the precursor. The powders were pressed into pellets, which were sintered into ceramics at 800 o C for 1 h. The morphology and structure have been determined by X-ray diffraction (XRD) and field emission scanning electron microscopy (FESEM). Polarization was observed in Pb 2 Fe 2 O 5 ceramics at room temperature, exhibiting a clear ferroelectric hysteresis loop. The remanent polarization of Pb 2 Fe 2 O 5 ceramic is estimated to be Pr ∼ 0.22 μC/cm 2 . The origin of the polarization may be attributed to the off-centers of shifted Pb 2+ ions as well as the FeO 6 octahedra in the perovskite-based structure of Pb 2 Fe 2 O 5 . Magnetic hysteresis loop was also observed at room temperature. The Pb 2 Fe 2 O 5 ceramic shows coexistence of ferroelectricity and ferromagnetism. It provides a new field of research for complex oxides with multiferroic properties.

  6. Current—voltage characteristics of lead zirconate titanate/nickel bilayered hollow cylindrical magnetoelectric composites

    International Nuclear Information System (INIS)

    De-An, Pan; Shen-Gen, Zhang; Jian-Jun, Tian; Li-Jie, Qiao; Jun-Sai, Sun; Volinsky, Alex A.

    2010-01-01

    Current–voltage measurements obtained from lead zirconate titanate/nickel bilayered hollow cylindrical magnetoelectric composite showed that a sinusoidal current applied to the copper coil wrapped around the hollow cylinder circumference induces voltage across the lead zirconate titanate layer thickness. The current–voltage coefficient and the maximum induced voltage in lead zirconate titanate at 1 kHz and resonance (60.1 kHz) frequencies increased linearly with the number of the coil turns and the applied current. The resonance frequency corresponds to the electromechanical resonance frequency. The current–voltage coefficient can be significantly improved by optimizing the magnetoelectric structure geometry and/or increasing the number of coil turns. Hollow cylindrical lead zirconate titanate/nickel structures can be potentially used as current sensors. (condensed matter: electronic structure, electrical, magnetic, and optical properties)

  7. Piezoelectric and Magnetoelectric Thick Films for Fabricating Power Sources in Wireless Sensor Nodes

    Directory of Open Access Journals (Sweden)

    Jong-Jin Choi

    2009-08-01

    Full Text Available In this manuscript, we review the progress made in the synthesis of thick film-based piezoelectric and magnetoelectric structures for harvesting energy from mechanical vibrations and magnetic field. Piezoelectric compositions in the system Pb(Zr,TiO3–Pb(Zn1/3Nb2/3O3 (PZNT have shown promise for providing enhanced efficiency due to higher energy density and thus form the base of transducers designed for capturing the mechanical energy. Laminate structures of PZNT with magnetostrictive ferrite materials provide large magnitudes of magnetoelectric coupling and are being targeted to capture the stray magnetic field energy. We analyze the models used to predict the performance of the energy harvesters and present a full system description.

  8. NiCo-lead zirconium titanate-NiCo trilayered magnetoelectric composites prepared by electroless deposition

    International Nuclear Information System (INIS)

    Zhou, M. H.; Wang, Y. G.; Bi, K.; Fan, H. P.; Zhao, Z. S.

    2015-01-01

    The NiCo layers with various Ni/Co atomic ratio have been successfully electroless deposited on PZT layers by varying the bath composition. As the cobalt atomic ratio in the deposited layer increases from 17.2 to 54.8 wt%, the magnetostrictive coefficient decreases. The magnetoelectric effect depends strongly on the magnetostrictive properties of magnetostrictive phase. The magnetoelectric coefficient of NiCo/PZT/NiCo trilayers increases with Ni/Co atomic ratio of the deposited NiCo layers increasing from 45:55 to 83:17. A maximum ME voltage coefficient of α E,31 = 2.8 V ⋅ cm −1 ⋅ Oe −1 is obtained at a frequency of about 88 kHz, which makes these trilayers suitable for applications in actuators, transducers and sensors

  9. A shear-mode magnetoelectric heterostructure for harvesting external magnetic field energy

    Science.gov (United States)

    He, Wei; Zhang, Jitao; Lu, Yueran; Yang, Aichao; Qu, Chiwen; Yuan, Shuai

    2017-03-01

    In this paper, a magnetoelectric (ME) energy harvester is presented for scavenging external magnetic field energy. The proposed heterostructure consists of a Terfenol-D plate, a piezoelectric PZT5H plate, a NdFeB magnet, and two concentrators. The external magnetic field is concentrated to the Terfenol-D plate and the PZT5H plate working in shear-mode, which can potentially increase the magnetoelectric response. Experiments have been performed to verify the feasibility of the harvester. Under the magnetic field of 0.6 Oe, the device produces a RMS voltage of 0.53 V at the resonant frequency of 32.6 kHz. The corresponding output power reaches 44.96 μW across a 3.1 kΩ matching resistor.

  10. NiCo-lead zirconium titanate-NiCo trilayered magnetoelectric composites prepared by electroless deposition

    Energy Technology Data Exchange (ETDEWEB)

    Zhou, M. H.; Wang, Y. G.; Bi, K., E-mail: bike@bupt.edu.cn [State Key Laboratory of Information Photonics and Optical Communications and School of Science, Beijing University of Posts and Telecommunications, Beijing 100876 (China); Fan, H. P. [School of Mechanical and Electrical Engineering, Qingdao Technological University Qindao College, Qingdao 266106 (China); Zhao, Z. S. [Shandong Engineering Consulting Institute, Jinan 250013 (China)

    2015-04-15

    The NiCo layers with various Ni/Co atomic ratio have been successfully electroless deposited on PZT layers by varying the bath composition. As the cobalt atomic ratio in the deposited layer increases from 17.2 to 54.8 wt%, the magnetostrictive coefficient decreases. The magnetoelectric effect depends strongly on the magnetostrictive properties of magnetostrictive phase. The magnetoelectric coefficient of NiCo/PZT/NiCo trilayers increases with Ni/Co atomic ratio of the deposited NiCo layers increasing from 45:55 to 83:17. A maximum ME voltage coefficient of α{sub E,31} = 2.8 V ⋅ cm{sup −1} ⋅ Oe{sup −1} is obtained at a frequency of about 88 kHz, which makes these trilayers suitable for applications in actuators, transducers and sensors.

  11. Soft x-ray resonant diffraction study of magnetic structure in magnetoelectric Y-type hexaferrite

    Science.gov (United States)

    Ueda, H.; Tanaka, Y.; Wakabayashi, Y.; Kimura, T.

    2018-05-01

    The effect of magnetic field on the magnetic structure associated with magnetoelectric properties in a Y-type hexaferrite, Ba1.3Sr0.7CoZnFe11AlO22, was investigated by utilizing the soft x-ray resonant diffraction technique. In this hexaferrite, the so-called alternating longitudinal conical phase is stabilized at room temperature and zero magnetic field. Below room temperature, however, this phase is transformed into the so-called transverse conical phase by applying an in-plane magnetic field (≈ 0.3 T). The transverse conical phase persists even after removing the magnetic field. The magnetoelectricity, which is magnetically-induced electric polarization, observed in the hexaferrite is discussed in terms of the temperature-dependent magnetic structure at zero field.

  12. Gigantic optical magnetoelectric effect in CuB2O4

    International Nuclear Information System (INIS)

    Saito, Mitsuru; Taniguchi, Kouji; Arima, Taka-hisa

    2008-01-01

    Although it has been well known that materials in which both space inversion and time reversal symmetries are broken can host optical magneto-electric effect, i.e., change in optical constants with the reversal of propagating direction of light, the largest change in absorption ever reported on this effect was 0.2%. Here we show that optical absorption in noncentrosymmetric weak ferromagnetic material CuB 2 O 4 changes by more than 100% with reversal of a low magnetic field of 300 Oe. The gigantic optical magneto-electric effect is ascribed to the canted antiferromagnetic spin ordering of square-coordinated Cu 2+ sites, where the local inversion is slightly broken. (author)

  13. Ferroics and Multiferroics for Dynamically Controlled Terahertz Wave Propagation

    Science.gov (United States)

    Dutta, Moumita

    The terahertz (THz) region of electromagnetic spectra, referred roughly to the frequency range of 100 GHz (0.1 THz) to 10 THz, is the bridging gap between the microwave and infrared spectral bands. Previously confined only to astronomy and analytical sciences due to the unavailability of technology, with the recent advancements in non-linear optics, this novel field has now started emerging as a promising area of research and study. Considerable efforts are underway to fill this 'THz gap' by developing efficient THz sources, detectors, switches, modulators etc. Be it any field, to realize this regime as one of the active frontiers, it is essential to have an efficient control over the wave propagation. In this research, functional materials (ferroics/multiferroics) have been explored to attain dynamic control over the THz beam propagation. The objective is to expand the horizon by enabling different family of materials to be incorporated in the design of THz modulators, exploiting the novel properties they exhibit. To reach that goal, following a comprehensive but selective (to dielectrics) review on the current-status of this research field, some preliminary studies on ferroic materials have been performed to understand the crux of ferroism and the novel functionalities they have to offer. An analytical study on microstructural and nanoscale properties of solid-solution ferroelectric Pb(Zr0.52Ti 0.48)O3 (PZT) and composite bio-ferroic seashells have been performed to elucidate the significance of structure-property relationship in intrinsic ferroelectrics. Moving forward, engineered ferroelectricity has been demonstrated. A precise control over fabrication parameters has been exploited to introduce oxygen-vacancy defined nanoscale polar-domains in centrosymmetric BaZrO3. Realizing that structure-property relationship can significantly influence the material properties and therefore the device performance, models for figure of merit analysis have been developed for

  14. DC magnetic field sensing based on the nonlinear magnetoelectric effect in magnetic heterostructures

    International Nuclear Information System (INIS)

    Burdin, Dmitrii; Chashin, Dmitrii; Ekonomov, Nikolai; Fetisov, Leonid; Fetisov, Yuri; Shamonin, Mikhail

    2016-01-01

    Recently, highly sensitive magnetic field sensors using the magnetoelectric effect in composite ferromagnetic-piezoelectric layered structures have been demonstrated. However, most of the proposed concepts are not useful for measuring dc magnetic fields, because the conductivity of piezoelectric layers results in a strong decline of the sensor’s sensitivity at low frequencies. In this paper, a novel functional principle of magnetoelectric sensors for dc magnetic field measurements is described. The sensor employs the nonlinear effect of voltage harmonic generation in a composite magnetoelectric structure under the simultaneous influence of a strong imposed ac magnetic field and a weak dc magnetic field to be measured. This physical effect arises due to the nonlinear dependence of the magnetostriction in the ferromagnetic layer on the magnetic field. A sensor prototype comprising of a piezoelectric fibre transducer sandwiched between two layers of the amorphous ferromagnetic Metglas ® alloy was fabricated. The specifications regarding the magnetic field range, frequency characteristics, and noise level were studied experimentally. The prototype showed the responsivity of 2.5 V mT −1 and permitted the measurement of dc magnetic fields in the range of ∼10 nT to about 0.4 mT. Although sensor operation is based on the nonlinear effect, the sensor response can be made linear with respect to the measured magnetic field in a broad dynamic range extending over 5 orders of magnitude. The underlying physics is explained through a simplified theory for the proposed sensor. The functionality, differences and advantages of the magnetoelectric sensor compare well with fluxgate magnetometers. The ways to enhance the sensor performance are considered. (paper)

  15. Magnetoelectric Transverse Gradient Sensor with High Detection Sensitivity and Low Gradient Noise

    OpenAIRE

    Zhang, Mingji; Or, Siu Wing

    2017-01-01

    We report, theoretically and experimentally, the realization of a high detection performance in a novel magnetoelectric (ME) transverse gradient sensor based on the large ME effect and the magnetic field gradient (MFG) technique in a pair of magnetically-biased, electrically-shielded, and mechanically-enclosed ME composites having a transverse orientation and an axial separation. The output voltage of the gradient sensor is directly obtained from the transverse MFG-induced difference in ME vo...

  16. Artificial dispersion via high-order homogenization: magnetoelectric coupling and magnetism from dielectric layers

    Science.gov (United States)

    Liu, Yan; Guenneau, Sébastien; Gralak, Boris

    2013-01-01

    We investigate a high-order homogenization (HOH) algorithm for periodic multi-layered stacks. The mathematical tool of choice is a transfer matrix method. Expressions for effective permeability, permittivity and magnetoelectric coupling are explored by frequency power expansions. On the physical side, this HOH uncovers a magnetoelectric coupling effect (odd-order approximation) and artificial magnetism (even-order approximation) in moderate contrast photonic crystals. Comparing the effective parameters' expressions of a stack with three layers against that of a stack with two layers, we note that the magnetoelectric coupling effect vanishes while the artificial magnetism can still be achieved in a centre-symmetric periodic structure. Furthermore, we numerically check the effective parameters through the dispersion law and transmission property of a stack with two dielectric layers against that of an effective bianisotropic medium: they are in good agreement throughout the low-frequency (acoustic) band until the first stop band, where the analyticity of the logarithm function of the transfer matrix () breaks down. PMID:24101891

  17. First-Principles Study of Enhanced Magnetoelectric Effects at the Fe/MgO(001) Interface

    Science.gov (United States)

    Niranjan, M. K.; Jaswal, S. S.; Tsymbal, E. Y.; Duan, C.-G.

    2010-03-01

    The magnetoelectric effect allows affecting magnetic properties of materials by electric fields with potential for technological applications such as electrically controlled magnetic data storage. In this study we explore, using first-principles methods, the magnetoelectric effect at the Fe/MgO(001) interface^,1. By explicitly introducing an electric field in our density-functional calculations we demonstrate that the magnetic moment of Fe atoms at the interface changes linearly as a function of the applied electric field with the surface magnetoelectric coefficient being strongly enhanced as compared to that for the clean Fe(001) surface.^1 The effect originates from the increased screening charge associated with a large dielectric constant of MgO. The influence of electric field on relative occupancy of the Fe-3d orbitals leads to significant change in the surface magnetocrystalline anisotropy. These results are compared with the available experimental work.^2 Our results indicate that using high-k dielectrics at the interface with ferromagnetic metals may be very effective in controlling the magnetic properties by electric fields thereby leading to interesting device applications. ^1 C.-G. Duan et al., Phys. Rev. Lett. 101, 137201 (2008). ^2 T. Maruyama et al., Nat. Nanotech., 4, 158 (2009).

  18. Giant and universal magnetoelectric coupling in soft materials and concomitant ramifications for materials science and biology

    Science.gov (United States)

    Liu, Liping; Sharma, Pradeep

    2013-10-01

    Magnetoelectric coupling—the ability of a material to magnetize upon application of an electric field and, conversely, to polarize under the action of a magnetic field—is rare and restricted to a rather small set of exotic hard crystalline materials. Intense research activity has recently ensued on materials development, fundamental scientific issues, and applications related to this phenomenon. This tantalizing property, if present in adequate strength at room temperature, can be used to pave the way for next-generation memory devices such as miniature magnetic random access memories and multiple state memory bits, sensors, energy harvesting, spintronics, among others. In this Rapid Communication, we prove the existence of an overlooked strain mediated nonlinear mechanism that can be used to universally induce the giant magnetoelectric effect in all (sufficiently) soft dielectric materials. For soft polymer foams—which, for instance, may be used in stretchable electronics—we predict room-temperature magnetoelectric coefficients that are comparable to the best known (hard) composite materials created. We also argue, based on a simple quantitative model, that magnetoreception in some biological contexts (e.g., birds) most likely utilizes this very mechanism.

  19. Surface Morphology Study of Nanostructured Lead-Free Solder Alloy Sn-Ag-Cu Developed by Electrodeposition: Effect of Current Density Investigation

    Directory of Open Access Journals (Sweden)

    Sakinah Mohd Yusof

    2013-10-01

    Full Text Available Normal 0 false false false IN X-NONE X-NONE MicrosoftInternetExplorer4 Nanostructured lead-free solder Sn-Ag-Cu (SAC was developed by electrodeposition method at room temperature. Electrolite bath which comprised of the predetermined quantity of tin methane sulfonate, copper sulfate and silver sulfate were added sequentially to MSA solution. The methane sulphonic acid (MSA based ternary Sn-Ag-Cu bath was developed by using tin methane sulfonate as a source of Sn ions while the Cu+ and Ag+ ions were obtained from their respective sulfate salts. The rate of the electrodeposition was controlled by variation of current density. The addition of the buffer, comprising of sodium and ammonium acetate helped in raising the pH solution. During the experimental procedure, the pH of solution, composition of the electrolite bath, and the electrodeposition time were kept constant. The electrodeposited rate, deposit composition and microstructure were investigated as the effect of current density. The electrodeposited solder alloy was characterized for their morphology using Field Emission Scanning Electron Microscope (FESEM. In conclusion, vary of current density will play significant role in the surface morphology of nanostructured lead-free solder SAC developed. Normal 0 false false false IN X-NONE X-NONE MicrosoftInternetExplorer4 /* Style Definitions */ table.MsoNormalTable {mso-style-name:"Table Normal"; mso-tstyle-rowband-size:0; mso-tstyle-colband-size:0; mso-style-noshow:yes; mso-style-priority:99; mso-style-qformat:yes; mso-style-parent:""; mso-padding-alt:0cm 5.4pt 0cm 5.4pt; mso-para-margin:0cm; mso-para-margin-bottom:.0001pt; mso-pagination:widow-orphan; font-size:11.0pt; font-family:"Calibri","sans-serif"; mso-ascii-font-family:Calibri; mso-ascii-theme-font:minor-latin; mso-fareast-font-family:"Times New Roman"; mso-fareast-theme-font:minor-fareast; mso-hansi-font-family:Calibri; mso-hansi-theme-font:minor-latin; mso-bidi-font-family:"Times New

  20. An ultrasonic therapeutic transducers using lead-free Na0.5K0.5NbO3-CuNb2O6 ceramics

    International Nuclear Information System (INIS)

    Yang, Ming-Ru; Chu, Sheng-Yuan; Tsai, Cheng-Che

    2010-01-01

    Research highlights: → In this paper, CN was added to NKN ceramics to decrease the sintering temperature and to improve the density and piezoelectric characteristics. The influence of CuNb 2 O 6 (CN) content on the microstructure, electrical properties, temperature stability, and mechanical properties of the synthesized samples was investigated. Results show that the samples synthesized with CN-doped not only improved the density but also exhibited superior piezoelectric characteristic, temperature stability of resonance frequency (TCF), and elastic stiffness coefficient than those of pure NKN piezoelectric ceramics. → The bulk density (4.47 g/cm 3 ), k p (40%), k t (45%), Q m (1642), C 33 D (19.64 x 10 10 N/m 2 ), TCF (-0.011%/ o C) and TCC (0.135%/ o C) values for NKN-01CN ceramics obtained from experiments show excellent 'hard' piezoelectric properties. Furthermore, a lead-free NKN-01CN ultrasonic therapeutic transducer was successfully driven by a self-tuning circuit. - Abstract: In this work, we reports on the CuNb 2 O 6 (CN) modified lead-free Na 0.5 K 0.5 NbO 3 (NKN) based piezoelectric ceramics were synthesized by solid-state reaction methods and sintered at 1075 o C for 3 h. A secondary phase of K 4 CuNb 8 O 23 was found in the XRD pattern of NKN-based ceramics as the CN dopants is 1 mol%. Microstructural analyses of un-doped and CN-doped ceramics were performed in a scanning electron microscope. The influence of CN content on the microstructure, electrical properties, temperature stability, and mechanical properties of the synthesized ceramics was investigated. The results show that the synthesized ceramics with CN-doped not only had improved density but also exhibited superior piezoelectric characteristics, temperature stability of resonance frequency (TCF), and a better elastic stiffness coefficient than those of pure NKN piezoelectric ceramics. The bulk density (4.47 g/cm 3 ), k p (40%), k t (45%), Q m (1642), C 33 D (19.64 x 10 10 N/m 2 ), TCF (-0

  1. Role of rare-earth ionic radii on the spin-phonon coupling in multiferroic ordered double perovskites

    Czech Academy of Sciences Publication Activity Database

    Macedo Filho, R.B.; Barbosa, D.A.B.; Reichlová, Helena; Martí, Xavier; de Menezes, A.S.; Ayala, A.P.; Paschoal, C.W.A.

    2015-01-01

    Roč. 7, č. 2 (2015), 075201 ISSN 2053-1591 Institutional support: RVO:68378271 Keywords : double perovskites * spin-phonon coupling * multiferroics Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.968, year: 2015

  2. BiFeO3-doped (Na0.5K0.5NbO3 lead-free piezoelectric ceramics

    Directory of Open Access Journals (Sweden)

    Xueyi Sun et al

    2008-01-01

    Full Text Available Lead-free piezoelectric ceramics (1−x(Na0.5K0.5NbO3-xBiFeO3 (x=0~0.07 were synthesized by the solid-state reaction. Differential scanning calorimetry (DSC measurements revealed that an increase in the amount of BiFeO3 dopant resulted in a decrease in the orthorhombic-tetragonal and tetragonal-cubic phase transition temperature of the material. One percent BiFeO3 additive suppressed grain growth, which not only benefits the sintering of ceramics but also enhances the piezoelectric and ferroelectric properties, where d33=145pC/N, kp=0.31, Qm=80, Pr=11.3 μC cm−2 and Ec=16.5 kV cm−1. As xBF>0.01, both piezoelectric and ferroelectric properties decreased rapidly with an increasing amount of dopant.

  3. Structural, microstructural, dielectric and ferroelectric properties of lead free Ba0.85Ca0.15Zr0.1Ti0.9O3 ceramic

    Science.gov (United States)

    Sharma, Sarita; Sharma, Hakikat; Negi, N. S.

    2018-05-01

    Lead free Ba0.85Ca0.15Zr0.1Ti0.9O3(BCTZ) ceramic has been synthesized by sol-gel method. Properties of material are studied at different sintering temperatures for 5 hours. Structural and microstructural properties are analyzed by using X-ray diffractrometer (XRD) and scanning electron microscopy (SEM) at annealing temperature of 850°C and 1050°C XRD pattern confirm the perovskite structure of the material without any unwanted phases crystalinity increased with increase of sintering temperature so as roughness and porosity is decreased as shown by SEM micrographs. There is large improvement in density with rise of sintering temperature which also leads to drastic change in ferroelectric and dielectric properties.

  4. Correlation between the structure and the piezoelectric properties of lead-free (K,Na,Li)(Nb,Ta,Sb)O3 ceramics studied by XRD and Raman spectroscopy.

    Science.gov (United States)

    Rubio-Marcos, Fernando; Marchet, Pascal; Romero, Juan José; Fernández, Jose F

    2011-09-01

    This article reviews on the use of Raman spectroscopy for the study of (K,Na,Li)(Nb,Ta,Sb)O(3) lead-free piezoceramics. Currently, this material appears to be one of the most interesting and promising alternatives to the well-known PZT piezoelectric materials. In this work, we prepare piezoceramics with different stoichiometries and study their structural, ferroelectric, and piezoelectric properties. By using both Raman spectroscopy and X-ray diffraction, we establish a direct correlation between the structure and the properties. The results demonstrate that the wavenumber of the A(1g) vibration is proportional to the tetragonality, the remnant polarization, and the piezoelectric coefficients of these materials. Thus, Raman spectroscopy appears as a very useful technique for a fast evaluation of the crystalline structure and the ferroelectric/ piezoelectric properties.

  5. Effect of Different HTM Layers and Electrical Parameters on ZnO Nanorod-Based Lead-Free Perovskite Solar Cell for High-Efficiency Performance

    Directory of Open Access Journals (Sweden)

    Farhana Anwar

    2017-01-01

    Full Text Available Simulation has been done using SCAPS-1D to examine the efficiency of CH3NH3SnI3-based solar cells including various HTM layers such as spiro-OMeTAD, Cu2O, and CuSCN. ZnO nanorod array has been considered as an ETM layer. Device parameters such as thickness of the CH3NH3SnI3 layer, defect density of interfaces, density of states, and metal work function were studied. For optimum parameters of all three structures, efficiency of 20.21%, 20.23%, and 18.34% has been achieved for spiro-OMeTAD, Cu2O, and CuSCN, respectively. From the simulations, an alternative lead-free perovskite solar cell is introduced with the CH3NH3SnI3 absorber layer, ZnO nanorod ETM layer, and Cu2O HTM layer.

  6. Enhanced multiferroic properties in (1–y)BiFeO{sub 3}–yNi{sub 0.50}Cu{sub 0.05}Zn{sub 0.45}Fe{sub 2}O{sub 4} composites

    Energy Technology Data Exchange (ETDEWEB)

    Mazumdar, S.C. [Department of Physics, Bangladesh University of Engineering and Technology, Dhaka 1000 (Bangladesh); Department of Physics, Comilla University, Comilla (Bangladesh); Khan, M.N.I. [Materials Science Division, Atomic Energy Centre, Dhaka 1000 (Bangladesh); Islam, Md. Fakhrul [Department of Glass and Ceramic Engineering, Bangladesh University of Engineering and Technology, Dhaka 1000 (Bangladesh); Hossain, A.K.M. Akther, E-mail: akmhossain@phy.buet.ac.bd [Department of Physics, Bangladesh University of Engineering and Technology, Dhaka 1000 (Bangladesh)

    2015-09-15

    Multiferroic composites (1–y)BiFeO{sub 3}–yNi{sub 0.50}Cu{sub 0.05}Zn{sub 0.45}Fe{sub 2}O{sub 4} (y=0.0, 0.1, 0.2, 0.3 and 0.4) are synthesized by the standard solid state reaction method. The X-ray diffraction analysis affirms the formation of both the component phases and also reveals that there is no chemical reaction between them. From the energy-dispersive X-ray spectroscopy study it is observed that the percentage of the elements in the component phases is well consistent with the nominal composition of the composites. Field Emission Scanning Electron Microscopy analysis shows almost homogeneous mixture of the two phases. The real part of the initial permeability increases (up to 67%) and the loss decreases with the ferrite content in the composites which is important in application point of view. Dielectric constant (ε′), loss tangent and AC conductivity are measured as a function of frequency at room temperature. The highest ε′ is obtained for 0.6BiFeO{sub 3}–0.4Ni{sub 0.50}Cu{sub 0.05}Zn{sub 0.45}Fe{sub 2}O{sub 4} composite. The dielectric dispersion at lower frequency (<10{sup 5} Hz) is due to the interfacial polarization. The complex impedance spectroscopy is used to correlate between the electrical properties of the studied samples with their microstructures. Two semicircular arcs corresponding to both grain and grain boundary contribution to electrical properties have been observed in all the studied samples. The maximum magnetoelectric voltage coefficient is found to be ∼38 mV cm{sup −1} Oe{sup −1} for the composite with 80% ferroelectric+20% ferrite phases. The present composite might be a promising candidate as multiferroic materials showing effective electric and magnetic properties. - Highlights: • XRD shows coexistance of ferroelectric and ferrimagnetic phases and no third phase. • The multiferroic composites show enhanced initial permeability and low loss. • Dielectric constant exhibits excellent high frequency stability

  7. Enhanced Energy-Storage Density and High Efficiency of Lead-Free CaTiO3-BiScO3 Linear Dielectric Ceramics.

    Science.gov (United States)

    Luo, Bingcheng; Wang, Xiaohui; Tian, Enke; Song, Hongzhou; Wang, Hongxian; Li, Longtu

    2017-06-14

    A novel lead-free (1 - x)CaTiO 3 -xBiScO 3 linear dielectric ceramic with enhanced energy-storage density was fabricated. With the composition of BiScO 3 increasing, the dielectric constant of (1 - x)CaTiO 3 -xBiScO 3 ceramics first increased and then decreased after the composition x > 0.1, while the dielectric loss decreased first and increased. For the composition x = 0.1, the polarization was increased into 12.36 μC/cm 2 , 4.6 times higher than that of the pure CaTiO 3 . The energy density of 0.9CaTiO 3 -0.1BiScO 3 ceramic was 1.55 J/cm 3 with the energy-storage efficiency of 90.4% at the breakdown strength of 270 kV/cm, and the power density was 1.79 MW/cm 3 . Comparison with other lead-free dielectric ceramics confirmed the superior potential of CaTiO 3 -BiScO 3 ceramics for the design of ceramics capacitors for energy-storage applications. First-principles calculations revealed that Sc subsitution of Ti-site induced the atomic displacement of Ti ions in the whole crystal lattice, and lattice expansion was caused by variation of the bond angles and lenghths. Strong hybridization between O 2p and Ti 3d was observed in both valence band and conduction band; the hybridization between O 2p and Sc 3d at high conduction band was found to enlarge the band gap, and the static dielectric tensors were increased, which was the essential for the enhancement of polarization and dielectric properties.

  8. Novel optically active lead-free relaxor ferroelectric (Ba0.6Bi0.2Li0.2)TiO3

    International Nuclear Information System (INIS)

    Borkar, Hitesh; Rao, Vaibhav; Barvat, Arun; Pal, Prabir; Kumar, Ashok; Dutta, Soma; Tomar, M; Gupta, Vinay; Scott, J F

    2016-01-01

    We discovered a near-room-temperature lead-free relaxor-ferroelectric (Ba 0.6 Bi 0.2 Li 0.2 )TiO 3 (BBLT) having A-site compositionally disordered ABO 3 perovskite structure. Microstructure-property relations revealed that the chemical inhomogeneities and development of local polar nano-regions (PNRs) are responsible for dielectric dispersion as a function of probe frequencies and temperatures. Rietveld analysis indicates mixed crystal structure with 80% tetragonal structure (space group P4mm) and 20% orthorhombic structure (space group Amm2), which is confirmed by the high resolution transmission electron diffraction (HRTEM). Dielectric constant and tangent loss dispersion with and without illumination of light obey nonlinear Vogel–Fulcher (VF) relations. The material shows slim polarization–hysteresis (P – E) loops and excellent displacement coefficients (d 33 ∼ 233 pm V −1 ) near room temperature, which gradually diminish near the maximum dielectric dispersion temperature (T m ) . The underlying physics for light-sensitive dielectric dispersion was probed by x-ray photon spectroscopy (XPS), which strongly suggests that mixed valence of bismuth ions, especially Bi 5+ ions, comprise most of the optically active centers. Ultraviolet photoemission measurements showed most of the Ti ions are in 4 +  states and sit at the centers of the TiO 6 octahedra; along with asymmetric hybridization between O 2 p and Bi 6 s orbitals, this appears to be the main driving force for net polarization. This BBLT material may open a new path for environmental friendly lead-free relaxor-ferroelectric research. (paper)

  9. Low sintering temperature and high piezoelectric properties of Li-doped (Ba,Ca)(Ti,Zr)O3 lead-free ceramics

    International Nuclear Information System (INIS)

    Chen, Xiaoming; Ruan, Xuezheng; Zhao, Kunyun; He, Xueqing; Zeng, Jiangtao; Li, Yongsheng; Zheng, Liaoying; Park, Chul Hong; Li, Guorong

    2015-01-01

    Highlights: • Li-doped Ba 0.85 Ca 0.15 Ti 0.9 Zr 0.1 O 3 (BCZT) lead-free piezoceramics were prepared by the two-step synthesis and solid-state reaction method. • Their sintering temperature decreases from about 1540 °C down to about 1400 °C. • With the proper addition of Li, the densities and grain sizes of ceramics increase. • The ceramics not only have the characteristics of hard piezoceramics but also possesses the features of soft piezoceramics at low sintering temperature. - Abstract: Li-doped Ba 0.85 Ca 0.15 Ti 0.9 Zr 0.1 O 3 (BCZT) lead-free piezoelectric ceramics were prepared by the two-step synthesis and the solid-state reaction method. The density and grain size of ceramics sufficiently increases by Li-doped sintering aid, and their sintering temperature decreases from about 1540 °C down to about 1400 °C. X-ray diffraction reveals that the phase structure of Li-doped BCTZ ceramics is changed with the sintering temperature, which is consistent with their phase transition observed by the temperature-dependent dielectric curves. The well-poled Li-doped BCZT ceramics show a high piezoelectric constant d 33 (512 pC/N) and a planar electromechanical coupling factor k p (0.49), which have the characteristics of soft Pb(Zr,Ti)O 3 (PZT) piezoceramic, on the other hand, the mechanical quality factor Q m is about 190, which possesses the features of hard PZT piezoceramics. The enhanced properties of the Li-doped BCZT are explained by the combination of Li-doped effect and sintering effect on the microstructure and the phase transition around room temperature

  10. Room temperature multiferroic properties of Pb(Fe{sub 0.5}Nb{sub 0.5})O{sub 3}–Co{sub 0.65}Zn{sub 0.35}Fe{sub 2}O{sub 4} composites

    Energy Technology Data Exchange (ETDEWEB)

    Pradhan, Dhiren K., E-mail: dhirenkumarp@gmail.com, E-mail: rkatiyar@hpcf.upr.edu; Katiyar, Ram S., E-mail: dhirenkumarp@gmail.com, E-mail: rkatiyar@hpcf.upr.edu [Department of Physics and Institute of Functional Nanomaterials, University of Puerto Rico, San Juan, Puerto Rico 00936 (United States); Puli, Venkata S. [Department of Physics and Engineering Physics, Tulane University, New Orleans, Louisiana 70118 (United States); Narayan Tripathy, Satya; Pradhan, Dillip K. [Department of Physics, National Institute of Technology, Rourkela 769008 (India); Scott, J. F. [Department of Physics and Institute of Functional Nanomaterials, University of Puerto Rico, San Juan, Puerto Rico 00936 (United States); Department of Physics, Cavendish Laboratory, University of Cambridge, Cambridge (United Kingdom)

    2013-12-21

    We report the crystal structure, magnetic, ferroelectric, dielectric, and magneto-dielectric properties of [Pb(Fe{sub 0.5}Nb{sub 0.5})O{sub 3}]{sub (1−x)}[Co{sub 0.65}Zn{sub 0.35}Fe{sub 2}O{sub 4}]{sub x}: (x = 0.1, 0.2, 0.3, and 0.4) composites. Rietveld refinement results of X-ray diffraction patterns confirm the formation of these composites for all x values. All the composites show well-saturated ferroelectric and ferromagnetic hysteresis (multiferroic-composite behavior) at room temperature. With increase in Co{sub 0.65}Zn{sub 0.35}Fe{sub 2}O{sub 4} (CZFO) content an increase in saturation magnetization, and decrease in saturation polarization, remanent polarization, and dielectric constant are observed. The ferroelectric phase transition temperature increases with increase in CZFO content. All of the compositions undergo second-order ferroelectric phase transitions, which can be explained by Landau-Devonshire theory. The recoverable energy density (∼0.20 to 0.04 J/cm{sup 3}) and charge-curve energy density (∼0.84 to 0.11 J/cm{sup 3}) decrease with increase in the CZFO content. The room-temperature magneto-dielectric measurements provide direct evidence of magneto-electric coupling via strain at room temperature.

  11. Low sintering temperature and high piezoelectric properties of Li-doped (Ba,Ca)(Ti,Zr)O{sub 3} lead-free ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Xiaoming [Key Laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); University of Chinese Academy of Sciences, Beijing 100039 (China); School of Materials Science and Engineering, East China University of Science and Technology, Shanghai 200237 (China); Ruan, Xuezheng; Zhao, Kunyun [Key Laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); He, Xueqing [School of Materials and Metallurgy, Northeastern University, Shenyang 110004 (China); Zeng, Jiangtao, E-mail: zjt@mail.sic.ac.cn [Key Laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); Li, Yongsheng [School of Materials Science and Engineering, East China University of Science and Technology, Shanghai 200237 (China); Zheng, Liaoying [Key Laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); Park, Chul Hong [Department of Physics Education, Pusan National University, Pusan 609735 (Korea, Republic of); Li, Guorong [Key Laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China)

    2015-05-25

    Highlights: • Li-doped Ba{sub 0.85}Ca{sub 0.15}Ti{sub 0.9}Zr{sub 0.1}O{sub 3} (BCZT) lead-free piezoceramics were prepared by the two-step synthesis and solid-state reaction method. • Their sintering temperature decreases from about 1540 °C down to about 1400 °C. • With the proper addition of Li, the densities and grain sizes of ceramics increase. • The ceramics not only have the characteristics of hard piezoceramics but also possesses the features of soft piezoceramics at low sintering temperature. - Abstract: Li-doped Ba{sub 0.85}Ca{sub 0.15}Ti{sub 0.9}Zr{sub 0.1}O{sub 3} (BCZT) lead-free piezoelectric ceramics were prepared by the two-step synthesis and the solid-state reaction method. The density and grain size of ceramics sufficiently increases by Li-doped sintering aid, and their sintering temperature decreases from about 1540 °C down to about 1400 °C. X-ray diffraction reveals that the phase structure of Li-doped BCTZ ceramics is changed with the sintering temperature, which is consistent with their phase transition observed by the temperature-dependent dielectric curves. The well-poled Li-doped BCZT ceramics show a high piezoelectric constant d{sub 33} (512 pC/N) and a planar electromechanical coupling factor k{sub p} (0.49), which have the characteristics of soft Pb(Zr,Ti)O{sub 3} (PZT) piezoceramic, on the other hand, the mechanical quality factor Q{sub m} is about 190, which possesses the features of hard PZT piezoceramics. The enhanced properties of the Li-doped BCZT are explained by the combination of Li-doped effect and sintering effect on the microstructure and the phase transition around room temperature.

  12. Sm/Ti co-substituted bismuth ferrite multiferroics: reciprocity between tetragonality and piezoelectricity.

    Science.gov (United States)

    Jha, Pardeep K; Jha, Priyanka A; Singh, Prabhakar; Ranjan, Rajeev; Dwivedi, R K

    2017-10-04

    BiFeO 3 (BFO) systems co-modified with Ti, Sm and Sm-Ti have been investigated for piezoelectricity together with dielectric and multiferroic properties. Structural studies revealed the coexistence of orthorhombic and rhombohedral (R3c) phases for x > 0.12. Impurity phases were shown to have hardly any effect on the remanent magnetization, which rather depends on the Fe-O-Fe bond angle. The dielectric loss was reduced considerably by substitution. A correlation between the piezoelectric coefficient and tetragonality was observed in these samples. BFO co-substituted with Sm-Ti exhibited a high piezoelectric coefficient with better ferroic properties, which revealed a unique combination of green piezoelectricity and multiferroicity.

  13. Synthesis, characterization, properties, and applications of nanosized ferroelectric, ferromagnetic, or multiferroic materials

    International Nuclear Information System (INIS)

    Dhak, Debasis; Das, Soma; Communication Engineering.); Dhak, Prasanta

    2015-01-01

    Recently, there has been an enormous increase in research activity in the field of ferroelectrics and ferromagnetics especially in multiferroic materials which possess both ferroelectric and ferromagnetic properties simultaneously. However, the ferroelectric, ferromagnetic, and multiferroic properties should be further improved from the utilitarian and commercial viewpoints. Nanostructural materials are central to the evolution of future electronics and information technologies. Ferroelectrics and ferromagnetics have already been established as a dominant branch in electronics sector because of their diverse applications. The ongoing dimensional downscaling of materials to allow packing of increased numbers of components into integrated circuits provides the momentum for evolution of nanostructural devices. Nanoscaling of the above materials can result in a modification of their functionality. Furthermore, nanoscaling can be used to form high density arrays of nanodomain nanostructures, which is desirable for miniaturization of devices

  14. Multiferroic properties of BiFeO3/BaTiO3 multilayered thin films

    International Nuclear Information System (INIS)

    Sharma, Savita; Tomar, Monika; Kumar, Ashok; Puri, Nitin K.; Gupta, Vinay

    2014-01-01

    Multilayered structures of multiferroic BiFeO 3 (BFO) and ferroelectric BaTiO 3 (BTO) have been fabricated using pulsed laser deposition (PLD). Ferromagnetic and ferroelectric properties of the multilayered system (BFO/BTO) have been investigated. It could be inferred that the magnetization increases with the incorporation of BTO buffer layer, which indicates a coupling between the ferroelectric and ferromagnetic orders. Vibrating sample magnetometer (VSM) measurements performed on the prepared multiferroic samples show that the magnetization is significantly increased (M s =56.88 emu/cm 3 ) for the multilayer system with more number of layers (four) keeping the total thickness of the multilayered system constant (350 nm) meanwhile maintaining the sufficiently enhanced ferroelectric properties (P r =29.68 µC/cm 2 )

  15. Low-field Switching Four-state Nonvolatile Memory Based on Multiferroic Tunnel Junctions

    Science.gov (United States)

    Yau, H. M.; Yan, Z. B.; Chan, N. Y.; Au, K.; Wong, C. M.; Leung, C. W.; Zhang, F. Y.; Gao, X. S.; Dai, J. Y.

    2015-08-01

    Multiferroic tunneling junction based four-state non-volatile memories are very promising for future memory industry since this kind of memories hold the advantages of not only the higher density by scaling down memory cell but also the function of magnetically written and electrically reading. In this work, we demonstrate a success of this four-state memory in a material system of NiFe/BaTiO3/La0.7Sr0.3MnO3 with improved memory characteristics such as lower switching field and larger tunneling magnetoresistance (TMR). Ferroelectric switching induced resistive change memory with OFF/ON ratio of 16 and 0.3% TMR effect have been achieved in this multiferroic tunneling structure.

  16. Ambient template synthesis of multiferroic MnWO4 nanowires and nanowire arrays

    International Nuclear Information System (INIS)

    Zhou Hongjun; Yiu Yuen; Aronson, M.C.; Wong, Stanislaus S.

    2008-01-01

    The current report describes the systematic synthesis of polycrystalline, multiferroic MnWO 4 nanowires and nanowire arrays with controllable chemical composition and morphology, using a modified template-directed methodology under ambient room-temperature conditions. We were able to synthesize nanowires measuring 55±10, 100±20, and 260±40 nm in diameter, respectively, with lengths ranging in the microns. Extensive characterization of as-prepared samples has been performed using X-ray diffraction, scanning electron microscopy, transmission electron microscopy (TEM), high-resolution TEM, and energy-dispersive X-ray spectroscopy. Magnetic behavior in these systems was also probed. - Graphical abstract: Systematic synthesis of crystalline, multiferroic MnWO4 nanowires and nanowire arrays with controllable chemical composition and morphology, using a modified template-directed methodology under ambient room-temperature conditions

  17. Coupling of order parameters, chirality, and interfacial structures in multiferroic materials.

    Science.gov (United States)

    Conti, Sergio; Müller, Stefan; Poliakovsky, Arkady; Salje, Ekhard K H

    2011-04-13

    We study optimal interfacial structures in multiferroic materials with a biquadratic coupling between two order parameters. We discover a new duality relation between the strong coupling and the weak coupling regime for the case of isotropic gradient terms. We analyze the phase diagram depending on the coupling constant and anisotropy of the gradient term, and show that in a certain regime the secondary order parameter becomes activated only in the interfacial region.

  18. Structure-property relationships of multiferroic materials: A nano perspective

    Science.gov (United States)

    Bai, Feiming

    The integration of sensors, actuators, and control systems is an ongoing process in a wide range of applications covering automotive, medical, military, and consumer electronic markets. Four major families of ceramic and metallic actuators are under development: piezoelectrics, electrostrictors, magnetostrictors, and shape-memory alloys. All of these materials undergo at least two phase transformations with coupled thermodynamic order parameters. These transformations lead to complex domain wall behaviors, which are driven by electric fields (ferroelectrics), magnetic fields (ferromagnetics), or mechanical stress (ferroelastics) as they transform from nonferroic to ferroic states, contributing to the sensing and actuating capabilities. This research focuses on two multiferroic crystals, Pb(Mg1/3Nb 2/3)O3-PbTiO3 and Fe-Ga, which are characterized by the co-existence and coupling of ferroelectric polarization and ferroelastic strain, or ferro-magnetization and ferroelastic strain. These materials break the conventional boundary between piezoelectric and electrostrictors, or magnetostrictors and shape-memory alloys. Upon applying field or in a poled condition, they yield not only a large strain but also a large strain over field ratio, which is desired and much benefits for advanced actuator and sensor applications. In this thesis, particular attention has been given to understand the structure-property relationships of these two types of materials from atomic to the nano/macro scale. X-ray and neutron diffraction were used to obtain the lattice structure and phase transformation characteristics. Piezoresponse and magnetic force microscopy were performed to establish the dependence of domain configurations on composition, thermal history and applied fields. It has been found that polar nano regions (PNRs) make significant contributions to the enhanced electromechanical properties of PMN-x%PT crystals via assisting intermediate phase transformation. With increasing PT

  19. Crystal growth of hexaferrite architecture for magnetoelectrically tunable microwave semiconductor integrated devices

    Science.gov (United States)

    Hu, Bolin

    Hexaferrites (i.e., hexagonal ferrites), discovered in 1950s, exist as any one of six crystallographic structural variants (i.e., M-, X-, Y-, W-, U-, and Z-type). Over the past six decades, the hexaferrites have received much attention owing to their important properties that lend use as permanent magnets, magnetic data storage materials, as well as components in electrical devices, particularly those operating at RF frequencies. Moreover, there has been increasing interest in hexaferrites for new fundamental and emerging applications. Among those, electronic components for mobile and wireless communications especially incorporated with semiconductor integrated circuits at microwave frequencies, electromagnetic wave absorbers for electromagnetic compatibility, random-access memory (RAM) and low observable technology, and as composite materials having low dimensions. However, of particular interest is the magnetoelectric (ME) effect discovered recently in the hexaferrites such as SrScxFe12-xO19 (SrScM), Ba2--xSrxZn 2Fe12O22 (Zn2Y), Sr4Co2Fe 36O60 (Co2U) and Sr3Co2Fe 24O41 (Co2Z), demonstrating ferroelectricity induced by the complex internal alignment of magnetic moments. Further, both Co 2Z and Co2U have revealed observable magnetoelectric effects at room temperature, representing a step toward practical applications using the ME effect. These materials hold great potential for applications, since strong magnetoelectric coupling allows switching of the FE polarization with a magnetic field (H) and vice versa. These features could lead to a new type of storage devices, such as an electric field-controlled magnetic memory. A nanoscale-driven crystal growth of magnetic hexaferrites was successfully demonstrated at low growth temperatures (25--40% lower than the temperatures required often for crystal growth). This outcome exhibits thermodynamic processes of crystal growth, allowing ease in fabrication of advanced multifunctional materials. Most importantly, the

  20. Multiferroic fluoride BaCoF4 Thin Films Grown Via Molecular Beam Epitaxy

    Science.gov (United States)

    Borisov, Pavel; Johnson, Trent; García-Castro, Camilo; Kc, Amit; Schrecongost, Dustin; Cen, Cheng; Romero, Aldo; Lederman, David

    Multiferroic materials exhibit exciting physics related to the simultaneous presence of multiple long-range orders, in many cases consisting of antiferromagnetic (AF) and ferroelectric (FE) orderings. In order to provide a new, promising route for fluoride-based multiferroic material engineering, we grew multiferroic fluoride BaCoF4 in thin film form on Al2O3 (0001) substrates by molecular beam epitaxy. The films grow with the orthorhombic b-axis out-of-plane and with three in-plane structural twin domains along the polar c-axis directions. The FE ordering in thin films was verified by FE remanent hysteresis loops measurements at T = 14 K and by room temperature piezoresponse force microscopy (PFM). An AF behavior was found below Neel temperature TN ~ 80 K, which is in agreement with the bulk properties. At lower temperatures two additional magnetic phase transitions at 19 K and 41 K were found. First-principles calculations demonstrated that the growth strain applied to the bulk BaCoF4 indeed favors two canted spin orders, along the b- and a-axes, respectively, in addition to the main AF spin order along the c-axis. Supported by FAME (Contract 2013-MA-2382), WV Research Challenge Grant (HEPC.dsr.12.29), and DMREF-NSF 1434897.

  1. Growth of Ca, Zr co-doped BaTiO3 lead-free ferroelectric single crystal and its room-temperature piezoelectricity

    Directory of Open Access Journals (Sweden)

    Donglin Liu

    2017-09-01

    Full Text Available Lead-free Ca, Zr co-doped BaTiO3 (BCZT single crystal with a dimension up to 2mm×2mm×2mm was grown by a spontaneous nucleation technique using KF as the flux. The composition of the studied single crystal was defined to be Ba0.798Ca0.202Zr0.006Ti0.994O3, corresponding to a tetragonal phase at room temperature. The oriented single crystal exhibited a quasi-static piezoelectric constant of approximately 232 pC/N. The effective piezoelectric coefficient d33* of the single domain crystal obtained under a unipolar electric field of 35 kV/cm was 179 pm/V. Rayleigh analysis was used to identify the intrinsic and extrinsic contributions to the room-temperature piezoelectricity of BCZT single crystal. The extrinsic contribution was estimated up to 40% due to the irreversible domain wall movement. Furthermore a sixth-order polynomial of Landau expansion was employed to analyze the intrinsic contribution to piezoelectricity of BCZT single crystal. The large energy barriers inhibited polarization rotations, leading to the relatively low piezoelectricity.

  2. Fabrication of Lead-Free Bi0.5Na0.5TiO3 Thin Films by Aqueous Chemical Solution Deposition

    Directory of Open Access Journals (Sweden)

    Mads Christensen

    2017-02-01

    Full Text Available Piezoelectric ceramics are widely used in actuator applications, and currently the vast majority of these devices are based on Pb ( Zr , Ti O 3 , which constitutes environmental and health hazards due to the toxicity of lead. One of the most promising lead-free material systems for actuators is based on Bi 0 . 5 Na 0 . 5 TiO 3 (BNT, and here we report on successful fabrication of BNT thin films by aqueous chemical solution deposition. The precursor solution used in the synthesis is based on bismuth citrate stabilized by ethanolamine, NaOH , and a Ti-citrate prepared from titanium tetraisopropoxide and citric acid. BNT thin films were deposited on SrTiO 3 and platinized silicon substrates by spin-coating, and the films were pyrolized and annealed by rapid thermal processing. The BNT perovskite phase formed after calcination at 500 °C in air. The deposited thin films were single phase according to X-ray diffraction, and the microstructures of the films shown by electron microscopy were homogeneous and dense. Decomposition of the gel was thoroughly investigated, and the conditions resulting in phase pure materials were identified. This new aqueous deposition route is low cost, robust, and suitable for development of BNT based thin film for actuator applications.

  3. Evolving morphotropic phase boundary in lead-free (Bi1/2Na1/2)TiO3-BaTiO3 piezoceramics

    Science.gov (United States)

    Jo, Wook; Daniels, John E.; Jones, Jacob L.; Tan, Xiaoli; Thomas, Pamela A.; Damjanovic, Dragan; Rödel, Jürgen

    2011-01-01

    The correlation between structure and electrical properties of lead-free (1-x)(Bi1/2Na1/2)TiO3-xBaTiO3 (BNT-100xBT) polycrystalline piezoceramics was investigated systematically by in situ synchrotron diffraction technique, combined with electrical property characterization. It was found that the morphotropic phase boundary (MPB) between a rhombohedral and a tetragonal phase evolved into a morphotropic phase region with electric field. In the unpoled material, the MPB was positioned at the transition from space group R3m to P4mm (BNT-11BT) with optimized permittivity throughout a broad single-phase R3m composition regime. Upon poling, a range of compositions from BNT-6BT to BNT-11BT became two-phase mixture, and maximum piezoelectric coefficient was observed in BNT-7BT. It was shown that optimized electrical properties are related primarily to the capacity for domain texturing and not to phase coexistence.

  4. Evolving morphotropic phase boundary in lead-free (Bi1/2Na1/2)TiO3-BaTiO3 piezoceramics

    International Nuclear Information System (INIS)

    Jo, Wook; Roedel, Juergen; Daniels, John E.; Jones, Jacob L.; Tan Xiaoli; Thomas, Pamela A.; Damjanovic, Dragan

    2011-01-01

    The correlation between structure and electrical properties of lead-free (1-x)(Bi 1/2 Na 1/2 )TiO 3 -xBaTiO 3 (BNT-100xBT) polycrystalline piezoceramics was investigated systematically by in situ synchrotron diffraction technique, combined with electrical property characterization. It was found that the morphotropic phase boundary (MPB) between a rhombohedral and a tetragonal phase evolved into a morphotropic phase region with electric field. In the unpoled material, the MPB was positioned at the transition from space group R3m to P4mm (BNT-11BT) with optimized permittivity throughout a broad single-phase R3m composition regime. Upon poling, a range of compositions from BNT-6BT to BNT-11BT became two-phase mixture, and maximum piezoelectric coefficient was observed in BNT-7BT. It was shown that optimized electrical properties are related primarily to the capacity for domain texturing and not to phase coexistence.

  5. Fabrication of lead-free piezoelectric Li2CO3-added (Ba,Ca)(Ti,Sn)O3 ceramics under controlled low oxygen partial pressure and their properties

    Science.gov (United States)

    Noritake, Kouta; Sakamoto, Wataru; Yuitoo, Isamu; Takeuchi, Teruaki; Hayashi, Koichiro; Yogo, Toshinobu

    2018-02-01

    Reduction-resistant lead-free (Ba,Ca)(Ti,Sn)O3 piezoceramics with high piezoelectric constants were fabricated by optimizing the amount of Li2CO3 added. Oxygen partial pressure was controlled during the sintering of (Ba,Ca)(Ti,Sn)O3 ceramics in a reducing atmosphere using H2-CO2 gas. Enhanced grain growth and a high-polarization state after poling treatment were achieved by adding Li2CO3. Optimizing the amount of Li2CO3 added to (Ba0.95Ca0.05)(Ti0.95Sn0.05)O3 ceramics sintered under a low oxygen partial pressure resulted in improved piezoelectric properties while maintaining the high sintered density. The prepared Li2CO3-added ceramic samples had homogeneous microstructures with a uniform dispersion of each major constituent element. However, the residual Li content in the 3 mol % Li2CO3-added (Ba0.95Ca0.05)(Ti0.95Sn0.05)O3 ceramics after sintering was less than 0.3 mol %. Sintered bodies of this ceramic prepared in a CO2 (1.5%)-H2 (0.3%)/Ar reducing atmosphere (PO2 = 10-8 atm at 1350 °C), exhibited sufficient electrical resistivity and a piezoelectric constant (d 33) exceeding 500 pC/N. The piezoelectric properties of this nonreducible ceramic were comparable or superior to those of the same ceramic sintered in air.

  6. Lead-Free Sn-Ce-O Composite Coating on Cu Produced by Pulse Electrodeposition from an Aqueous Acidic Sulfate Electrolyte

    Science.gov (United States)

    Sharma, Ashutosh; Das, Karabi; Das, Siddhartha

    2017-10-01

    Pulse-electrodeposited Sn-Ce-O composite solder coatings were synthesized on a Cu substrate from an aqueous acidic solution containing stannous sulfate (SnSO4·3H2O), sulfuric acid (H2SO4), and Triton X-100 as an additive. The codeposition was achieved by adding nano-cerium oxide powder in varying concentrations from 5 g/L to 20 g/L into the electrolytic bath. Microstructural characterization was carried out using x-ray diffraction (XRD), scanning electron microscopy, and transmission electron microscopy. The XRD analysis showed that the deposits consist mainly of tetragonal β (Sn) with reduced cerium oxide species. The composite coatings thus obtained exhibit a smaller grain size, possess higher microhardness, and a lower melting point than the monolithic Sn coating. The electrical resistivity of the developed composites increases, however, but lies within the permissible limits for current lead-free solder applications. Also, an optimum balance of properties in terms of microhardness, adhesion, melting point and resistivity can be obtained with 0.9 wt.% cerium oxide in the Sn matrix, which enables potential applications in solder joints and packaging.

  7. Effect of Multiple Reflow Cycles and Al2O3 Nanoparticles Reinforcement on Performance of SAC305 Lead-Free Solder Alloy

    Science.gov (United States)

    Tikale, Sanjay; Prabhu, K. Narayan

    2018-05-01

    The effect of Al2O3 nanoparticles reinforcement on melting behavior, microstructure evolution at the interface and joint shear strength of 96.5Sn3Ag0.5Cu (SAC305) lead-free solder alloy subjected to multiple reflow cycles was investigated. The reinforced SAC305 solder alloy compositions were prepared by adding Al2O3 nanoparticles in different weight fractions (0.05, 0.1, 0.3 and 0.5 wt.%) through mechanical dispersion. Cu/solder/Cu micro-lap-shear solder joint specimens were used to assess the shear strength of the solder joint. Differential scanning calorimetry was used to investigate the melting behavior of SAC305 solder nanocomposites. The solder joint interfacial microstructure was studied using scanning electron microscopy. The results showed that the increase in melting temperature (T L) and melting temperature range of the SAC305 solder alloy by addition of Al2O3 nanoparticles were not significant. In comparison with unreinforced SAC305 solder alloy, the reinforcement of 0.05-0.5 wt.% of Al2O3 nanoparticles improved the solder wettability. The addition of nanoparticles in minor quantity effectively suppressed the Cu6Sn5 IMC growth, improved the solder joint shear strength and ductility under multiple reflow cycles. However, the improvement in solder properties was less pronounced on increasing the nanoparticle content above 0.1 wt.% of the solder alloy.

  8. Effect of MnO doping on the structure, microstructure and electrical properties of the (K,Na,Li)(Nb,Ta,Sb)O3 lead-free piezoceramics

    International Nuclear Information System (INIS)

    Rubio-Marcos, F.; Marchet, P.; Vendrell, X.; Romero, J.J.; Remondiere, F.; Mestres, L.; Fernandez, J.F.

    2011-01-01

    Highlights: · MnO doping effects on structure and properties of (K,Na,Li)(Nb,Ta,Sb)O 3 piezoceramics. · The structure changes towards an orthorhombic symmetry for higher MnO concentrations. · High doping levels induce a tetragonal tungsten-bronze secondary phase. · Mn 2+ doping modifies the phase transition temperature and the piezoelectric properties. · Manganese doping increases the mechanical quality factor Q m . - Abstract: Mn 2+ -doped (K,Na,Li)(Nb,Ta,Sb)O 3 lead-free piezoelectric ceramics have been prepared by a conventional sintering technique. The effects of Mn 2+ doping on the phase structure, microstructure and ferro-piezoelectric properties of the ceramics have been evaluated. MnO doping modifies the (K,Na,Li)(Nb,Ta,Sb)O 3 structure, giving rise to the appearance of a TTB-like secondary phase and to changes on the orthorhombic to tetragonal phase transition temperature. The modification of this temperature induces a reduction of the piezoelectric constants, which is accompanied by an increase on the mechanical quality factor. Mn 2+ ions incorporate into the perovskite structure in different off ways depending on their concentration.

  9. Magnetoelectric Effect in Gallium Arsenide-Nickel-Tin-Nickel Multilayer Structures

    Science.gov (United States)

    Filippov, D. A.; Tikhonov, A. A.; Laletin, V. M.; Firsova, T. O.; Manicheva, I. N.

    2018-02-01

    Experimental data have been presented for the magnetoelectric effect in nickel-tin-nickel multilayer structures grown on a GaAs substrate by cathodic electrodeposition. The method of fabricating these structures has been described, and the frequency dependence of the effect has been demonstrated. It has been shown that tin used as an intermediate layer reduces mechanical stresses due to the phase mismatch at the Ni-GaAs interface and, thus, makes it possible to grow good structures with a 70-μm-thick Ni layer. The grown structures offer good adhesion between layers and a high Q factor.

  10. Optical activity of oriented molecular systems in terms of the magnetoelectric tensor of gyrotropy

    International Nuclear Information System (INIS)

    Arteaga, Oriol

    2014-01-01

    The optical activity of oriented molecular systems is investigated using bianisotropic material constitutives for Maxwell's equations. It is shown that the circular birefringence and circular dichroism for an oriented system can be conveniently expressed in terms of the two components of the symmetric magnetoelectric tensor of gyrotropy that are perpendicular to this direction of light propagation. This description establishes a direct link between the optical activity measured at a certain direction and the tensors that describe the oscillating electric and magnetic dipole and electric quadrupole moments induced by the optical wave. (paper)

  11. Shape and size effects on layered Ni/PZT/Ni composites magnetoelectric performance

    Energy Technology Data Exchange (ETDEWEB)

    Pan, D A; Zhang, S G; Qiao, L J [School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China); Volinsky, Alex A [Department of Mechanical Engineering, University of South Florida, Tampa FL 33620 (United States)], E-mail: lqiao@ustb.edu.cn

    2008-09-07

    This paper presents the magnetoelectric (ME) effect in trilayered Ni/PZT/Ni composites which is related to their size and shape. The ME composites with the same interfacial areas but different geometrical shapes have different ME voltage coefficients. Longitudinal resonant modes in the rectangular and triangular trilayered ME composites were studied. One should choose optimized size, shape and working frequency of the ME composites in order to gain the maximum ME effect. This study plays a guiding role for trilayered ME composites design for real applications. (fast track communication)

  12. Magnetoelectric effect in a sandwich structure of gallium arsenide–nickel–tin–nickel

    Science.gov (United States)

    Galichyan, T. A.; Filippov, D. A.; Tihonov, A. A.; Laletin, V. M.; Firsova, T. O.; Manicheva, I. N.

    2018-04-01

    The results of investigation of the magnetoelectric effect in a nickel-tin-nickel sandwich structure obtained by galvanic deposition of gallium arsenide on a substrate are presented. The technology of constructing such structures is described and the experimental results of the frequency dependence of the effect are presented. It is shown that the use of tin as an intermediate layer reduces the mechanical stresses resulting from the incommensurability of the phases, which permits obtaining qualitative structures with the nickel thickness of about 70 μm. The resulting structures exhibit good adhesion between the layers and have a high quality factor.

  13. Eddy-current effect on resonant magnetoelectric coupling in magnetostrictive-piezoelectric laminated composites

    Science.gov (United States)

    Liu, Guoxi; Zhang, Chunli; Chen, Weiqiu; Dong, Shuxiang

    2013-07-01

    An analytical model of resonant magnetoelectric (ME) coupling in magnetostrictive (MS)-piezoelectric (PE) laminated composites in consideration of eddy-current effect in MS layer using equivalent circuit method is presented. Numerical calculations show that: (1) the eddy-current has a strong effect on ME coupling in MS-PE laminated composites at resonant frequency; and (2) the resonant ME coupling is then significantly dependent on the sizes of ME laminated composites, which were neglected in most previous theoretical analyses. The achieved results provide a theoretical guidance for the practice engineering design, manufacture, and application of ME laminated composites and devices.

  14. Resistive switching via the converse magnetoelectric effect in ferromagnetic multilayers on ferroelectric substrates.

    Science.gov (United States)

    Pertsev, N A; Kohlstedt, H

    2010-11-26

    A voltage-controlled resistive switching is predicted for ferromagnetic multilayers and spin valves mechanically coupled to a ferroelectric substrate. The switching between low- and high-resistance states results from the strain-driven magnetization reorientations by about 90°, which are shown to occur in ferromagnetic layers with a high magnetostriction and weak cubic magnetocrystalline anisotropy. Such reorientations, not requiring external magnetic fields, can be realized experimentally by applying moderate electric field to a thick substrate (bulk or membrane type) made of a relaxor ferroelectric having ultrahigh piezoelectric coefficients. The proposed multiferroic hybrids exhibiting giant magnetoresistance may be employed as electric-write nonvolatile magnetic memory cells with nondestructive readout.

  15. Origin of the magnetic-field controlled polarization reversal in multiferroic TbMn2 O 5

    Science.gov (United States)

    Leo, N.; Meier, D.; Pisarev, R. V.; Park, S.; Cheong, S.-W.; Fiebig, M.

    2011-03-01

    The interplay of multi-dimensional complex magnetic order parameters leads to interesting effects like magnetically induced ferroelectricity. A particular interesting example is TbMn 2 O5 because of the associated magnetic-field controllable electric polarization. By optical second harmonic generation we show that the gigantic magnetoelectric effect originates in three independent ferroelectric contributions. Two of these are manganese-generated. The third contribution is related to the magnetism of the Tb 3+ sublattice and has not been identified so far. It mediates the remarkable magnetic-field induced polarization reversal. This model is verified by experiments on the isostructural YMn 2 O5 where Y3+ ions are nonmagnetic and only two polarization contributions are present and no magnetoelectric coupling is observed. These results underline the importance of the 3 d - 4 f -interaction for the intricate magnetoelectric coupling in the class of isostructural RMn 2 O5 compounds. This work was supported by the DFG through SFB 608.

  16. Effect of cooling rate during solidification of Sn-9Zn lead-free solder alloy on its microstructure, tensile strength and ductile-brittle transition temperature

    Energy Technology Data Exchange (ETDEWEB)

    Prabhu, K.N., E-mail: prabhukn_2002@yahoo.co.in [Department of Metallurgical and Materials Engineering, National Institute of Technology Karnataka, Surathkal, Mangalore 575 025 (India); Deshapande, Parashuram; Satyanarayan [Department of Metallurgical and Materials Engineering, National Institute of Technology Karnataka, Surathkal, Mangalore 575 025 (India)

    2012-01-30

    Highlights: Black-Right-Pointing-Pointer Effect of cooling rate on tensile and impact properties of Sn-9Zn alloy was assessed. Black-Right-Pointing-Pointer Both DBTT and UTS of the solder alloy increased with increase in cooling rate. Black-Right-Pointing-Pointer An optimum cooling rate during solidification would minimize DBTT and maximize UTS. - Abstract: Solidification rate is an important variable during processing of materials, including soldering, involving solidification. The rate of solidification controls the metallurgical microstructure at the solder joint and hence the mechanical properties. A high tensile strength and a lower ductile-brittle transition temperature are necessary for reliability of solder joints in electronic circuits. Hence in the present work, the effect of cooling rate during solidification on microstructure, impact and tensile properties of Sn-9Zn lead-free solder alloy was investigated. Four different cooling media (copper and stainless steel moulds, air and furnace cooling) were used for solidification to achieve different cooling rates. Solder alloy solidified in copper mould exhibited higher cooling rate as compared to other cooling media. The microstructure is refined as the cooling rate was increased from 0.03 to 25 Degree-Sign C/s. With increase in cooling rate it was observed that the size of Zn flakes became finer and distributed uniformly throughout the matrix. Ductile-to-brittle transition temperature (DBTT) of the solder alloy increased with increase in cooling rate. Fractured surfaces of impact test specimens showed cleavage like appearance and river like pattern at very low temperatures and dimple like appearance at higher temperatures. The tensile strength of the solder alloy solidified in Cu and stainless moulds were higher as compared to air and furnace cooled samples. It is therefore suggested that the cooling rate during solidification of the solder alloy should be optimum to maximize the strength and minimize the

  17. Effect of cooling rate during solidification of Sn–9Zn lead-free solder alloy on its microstructure, tensile strength and ductile–brittle transition temperature

    International Nuclear Information System (INIS)

    Prabhu, K.N.; Deshapande, Parashuram; Satyanarayan

    2012-01-01

    Highlights: ► Effect of cooling rate on tensile and impact properties of Sn–9Zn alloy was assessed. ► Both DBTT and UTS of the solder alloy increased with increase in cooling rate. ► An optimum cooling rate during solidification would minimize DBTT and maximize UTS. - Abstract: Solidification rate is an important variable during processing of materials, including soldering, involving solidification. The rate of solidification controls the metallurgical microstructure at the solder joint and hence the mechanical properties. A high tensile strength and a lower ductile–brittle transition temperature are necessary for reliability of solder joints in electronic circuits. Hence in the present work, the effect of cooling rate during solidification on microstructure, impact and tensile properties of Sn–9Zn lead-free solder alloy was investigated. Four different cooling media (copper and stainless steel moulds, air and furnace cooling) were used for solidification to achieve different cooling rates. Solder alloy solidified in copper mould exhibited higher cooling rate as compared to other cooling media. The microstructure is refined as the cooling rate was increased from 0.03 to 25 °C/s. With increase in cooling rate it was observed that the size of Zn flakes became finer and distributed uniformly throughout the matrix. Ductile-to-brittle transition temperature (DBTT) of the solder alloy increased with increase in cooling rate. Fractured surfaces of impact test specimens showed cleavage like appearance and river like pattern at very low temperatures and dimple like appearance at higher temperatures. The tensile strength of the solder alloy solidified in Cu and stainless moulds were higher as compared to air and furnace cooled samples. It is therefore suggested that the cooling rate during solidification of the solder alloy should be optimum to maximize the strength and minimize the DBTT.

  18. Lead-free piezoelectric (K,Na)NbO3-based ceramic with planar-mode coupling coefficient comparable to that of conventional lead zirconate titanate

    Science.gov (United States)

    Ohbayashi, Kazushige; Matsuoka, Takayuki; Kitamura, Kazuaki; Yamada, Hideto; Hishida, Tomoko; Yamazaki, Masato

    2017-06-01

    We developed a (K,Na)NbO3-based lead-free piezoelectric ceramic with a KTiNbO5 system, (K1- x Na x )0.86Ca0.04Li0.02Nb0.85O3-δ-K0.85Ti0.85Nb1.15O5-BaZrO3-Fe2O3-MgO (K1- x N x N-NTK-FM). K1- x N x N-NTK-FM ceramic exhibits a very dense microstructure and a coupling coefficient of k p = 0.59, which is almost comparable to that of conventional lead zirconate titanate (PZT). The (K,Na)NbO3-based ceramic has the Γ15 mode for a wide x range. The nanodomains of orthorhombic (K,Na)NbO3 with the M3 mode coexist within the tetragonal Γ15 mode (K,Na)NbO3 matrix. Successive phase transition cannot occur with increasing x. The maximum k p is observed at approximately the minimum x required to generate the M3 mode phase. Unlike the behavior at the morphotropic phase boundary (MPB) in PZT, the characteristics of K1- x N x N-NTK-FM ceramic in this region changed moderately. This gentle phase transition seems to be a relaxor, although the diffuseness degree is not in line with this hypothesis. Furthermore, piezoelectric properties change from “soft” to “hard” upon the M3 mode phase aggregation.

  19. Effects of aging time on the mechanical properties of Sn–9Zn–1.5Ag–xBi lead-free solder alloys

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Chih-Yao [Department of Materials Science and Engineering, National Cheng Kung University, 1 Ta-Hsueh Road, Tainan 70101, Taiwan (China); Hon, Min-Hsiung [Department of Materials Science and Engineering, National Cheng Kung University, 1 Ta-Hsueh Road, Tainan 70101, Taiwan (China); Department of Mechanical Engineering, National Kaohsiung University of Applied Sciences, 415 Chien-Kung Road, Kaohsiung 80782, Taiwan (China); Wang, Moo-Chin, E-mail: mcwang@kmu.edu.tw [Department of Fragrance and Cosmetic Science, Kaohsiung Medical University, 100, Shih-Chuan 1st Road, Kaohsiung 80728, Taiwan (China); Chen, Ying-Ru; Chang, Kuo-Ming; Li, Wang-Long [Institute of Nanotechnology and Microsystems Engineering, National Cheng Kung University, No. 1, University Road, Tainan 70101, Taiwan (China)

    2014-01-05

    Highlights: • The microstructure of these solder alloys are composed of Sn-rich phase and Ag{sub 3}Sn. • The grain size of Sn–9Zn–1.5Ag–xBi solder alloys increases with rose aging time. • The maximum yield strength is 112.7 ± 2.2 MPa for Sn–9Zn–1.5Ag–3Bi solder alloys. • TEM observed that Bi appears as oblong shape fine particles. -- Abstract: The effects of aging time on the mechanical properties of the Sn–9Zn–1.5Ag–xBi lead-free solder alloys are investigated using scanning electron microscopy (SEM), X-ray diffraction (XRD), transmission electron microscopy (TEM), selected area electron diffraction (SAED), energy dispersive spectrometry (EDS) and a universal testing machine. The experimental results show that the microstructure of Sn–9Zn–1.5Ag–xBi solder alloys is composed of Sn-rich phase and AgZn{sub 3}. No other intermetallic compounds (IMCs) with Bi content was observed in the solder matrix for Sn–9Zn–1.5Ag solder alloys with various Bi contents before and after aging at 150 °C for different durations. The lattice parameter increases significantly with increasing aging time or Bi addition. The size of Sn-rich grain increased gradually with aging time increased, but decreases with Bi content increases. The maximum yield strength is 112.7 ± 2.2 MPa for Sn–9Zn–1.5Ag–3Bi solder alloy before aging.

  20. Mechanical bending strength of (Bi0.5Na0.5 TiO3-based lead-Free piezoelectric ceramics

    Directory of Open Access Journals (Sweden)

    Hiroaki Takahashi

    2017-09-01

    Full Text Available (Bi0.5Na0.5TiO3 [BNT] is expected as one of candidate lead-free materials because these ceramics show relatively good high-power piezoelectric properties. In this study, we tried to understand the bending strength and fracture behavior of the BNT-based ceramics. To measure the bending strength, a three-point bending test on the basis of JIS was conducted using 12.0 × 4.0 × 1.0 mm3 specimens. An average bending strength, σA, of pure BNT ceramics sintered at 1100 °C for 2, 12 and 24 h were 217, 195 and 187 MPa, respectively. It is cleared that the σA increased with decreasing the sintering time, (grain size and pore size. We also investigated the bending strength of Nb2O5 doped BNT ceramics [BNT-Nb x, x = 0.05 ∼ 1.5 wt%] and MnCO3 doped BNT ceramics [BNT-Mn x, x = 0.5 and 1.0 wt%]. Values of the σA of BNT-Nb 0.5 and BNT-Mn 0.5 were 222, and 188 MPa, respectively. It is clarified that soft dopants (Nb can improve the bending strength of BNT-based ceramics. Additionally, hot-pressed BNT [HP-BNT] were sintered at 1050 °C for 5 h, and the σA of HP-BNT was 245 MPa.