Combined analyses of ion beam synthesized layers in porous silicon

International Nuclear Information System (INIS)

Ramos, A.R.; Silva, M.F. da; Silva, M.R. da; Soares, J.C.; Paszti, F.; Horvath, Z.E.; Vazsonyi, E.; Conde, O.

2001-01-01

High dose ion implantation was used to form polycrystalline silicide films on porous silicon with different native concentrations of light impurities (C and O). Porous silicon layers several μm thick were implanted with 170 KeV Cr + ions to fluences of 3x10'1 7 ions/cm 2 both at room temperature and 450 o C. Similar samples were implanted with 100 keV Co + ions to fluences of 2x10 17 ions/cm 2 at room temperature and 350 o C and 450 o C. The formed silicide compounds were studied by Rutherford backscattering spectrometry, elastic recoil detection, glancing incidence X-ray diffraction, and four point-probe sheet resistance measurements. Selected Co implanted samples were analysed by cross-section transmission electron microscopy. Results show that the light impurities were partially expelled from the forming silicide layer. Combining cross-section transmission electron microscopy with ion beam methods it was possible to show that, in the implanted region, the porous structure collapses and densities during implantation, but the underlying porous silicon remains intact. The layer structure as well as the quality and type of the formed silicide, were found to depend on the original impurity level, implantation temperature, and annealing. (author)

Investigation of the interface region between a porous silicon layer and a silicon substrate

International Nuclear Information System (INIS)

Lee, Ki-Won; Park, Dae-Kyu; Kim, Young-You; Shin, Hyun-Joon

2005-01-01

Atomic force microscopy (AFM) measurement and X-ray diffraction (XRD) analysis were performed to investigate the physical and structural characteristics of the interface region between a porous silicon layer and a silicon substrate. We discovered that, when anodization time was increased under a constant current density, the Si crystallites in the interface region became larger and formed different lattice parameters than observed in the porous silicon layer. Secondary ion mass spectrometry (SIMS) analysis also revealed that the Si was more concentrated in the interface region than in the porous silicon layer. These results were interpreted by the deficiency of the HF solution in reaching to the interface through the pores during the porous silicon formation

Solute transport in aggregated and layered porous media

International Nuclear Information System (INIS)

Koch, S.

1993-01-01

This work is a contribution to research in soil physics dealing with solute transport in porous media. The influence of structural inhomogeneities on solute transport is investigated. Detailed experiments at the laboratory scale are used to enlighten distinct processes which cannot be studied separately at field scale. Two main aspects are followed up: (i) to show the influence of aggregation of a porous medium on breakthrough time and spreading of an inert tracer and consequences on the estimation of parameter values of models describing solute transport in aggregated systems, (ii) to investigate the influences on the dispersion process when stratification is perpendicular to the direction of flow. Several concepts of modelling solute transport in soil are discussed. Models based on the convection-dispersion equation (CDE) are emphasized because they are used here to model solute transport experiments conducted with aggregated porous media. Stochastic concepts are introduced to show the limitations of the deterministic CDE approaches. Experiments are done in columns containing two kinds of solid phases and were saturated with water. The solid phases are porous and solid glass beads exhibiting a distinctly unimodal or bimodal pore size distribution. Experimental breakthrough curves (BTCs) are modelled with the CDE, a bicontinuum model with a phenomenological mass transfer rate and a bicontinuum spherical diffusion model. Experiments are also done in columns that are unsaturated containing porous materials that are layered. Flow is made at a steady rate. It is shown that layer boundaries have a severe influence on lateral mixing. They may force streamlines to converge or cause a lateral redistribution of solutes. (author) figs., tabs., 122 refs

Electric double layer capacitance on hierarchical porous carbons in an organic electrolyte

OpenAIRE

Yamada, Hirotoshi; Moriguchi, Isamu; Kudo, Tetsuichi

2008-01-01

Nanoporous carbons were prepared by using colloidal crystal as a template. Nitrogen adsorption/desorption isotherms and transmission electron microscope images revealed that the porous carbons exhibit hierarchical porous structures with meso/macropores and micropores. Electric double layer capacitor performance of the porous carbons was investigated in an organic electrolyte of 1 M LiClO4 in propylene carbonate and dimethoxy ethane. The hierarchical porous carbons exhibited large specific dou...

Electrokinetic salt removal from porous building materials using ion exchange membranes

NARCIS (Netherlands)

Kamran, K.; Van Soestbergen, M.; Pel, L.

The removal of salt from porous building materials under the influence of an applied voltage gradient normally results in high pH gradients due to the formation of protons and hydroxyl ions at the electrodes. The formed acidic and alkaline regions not only lead to disintegration of the porous

Electrokinetic salt removal from porous building materials using ion exchange membranes

NARCIS (Netherlands)

Kamran, K.; Soestbergen, van M.; Pel, L.

2012-01-01

The removal of salt from porous building materials under the influence of an applied voltage gradient normally results in high pH gradients due to the formation of protons and hydroxyl ions at the electrodes. The formed acidic and alkaline regions not only lead to disintegration of the porous

Crack Growth along Interfaces in Porous Ceramic Layers

DEFF Research Database (Denmark)

Sørensen, Bent F.; Horsewell, Andy

2001-01-01

Crack growth along porous ceramic layers was studied experimentally. Double cantilever beam sandwich specimens were loaded with pure bending moments to obtain stable crack growth. The experiments were conducted in an environmental scanning electron microscope enabling in situ observations...

Photo-EMF sensitivity of porous silicon thin layer-crystalline silicon heterojunction to ammonia adsorption.

Science.gov (United States)

Vashpanov, Yuriy; Jung, Jae Il; Kwack, Kae Dal

2011-01-01

A new method of using photo-electromotive force in detecting gas and controlling sensitivity is proposed. Photo-electromotive force on the heterojunction between porous silicon thin layer and crystalline silicon wafer depends on the concentration of ammonia in the measurement chamber. A porous silicon thin layer was formed by electrochemical etching on p-type silicon wafer. A gas and light transparent electrical contact was manufactured to this porous layer. Photo-EMF sensitivity corresponding to ammonia concentration in the range from 10 ppm to 1,000 ppm can be maximized by controlling the intensity of illumination light.

Waves propagating over a two-layer porous barrier on a seabed

Science.gov (United States)

Lin, Qiang; Meng, Qing-rui; Lu, Dong-qiang

2018-05-01

A research of wave propagation over a two-layer porous barrier, each layer of which is with different values of porosity and friction, is conducted with a theoretical model in the frame of linear potential flow theory. The model is more appropriate when the seabed consists of two different properties, such as rocks and breakwaters. It is assumed that the fluid is inviscid and incompressible and the motion is irrotational. The wave numbers in the porous region are complex ones, which are related to the decaying and propagating behaviors of wave modes. With the aid of the eigenfunction expansions, a new inner product of the eigenfunctions in the two-layer porous region is proposed to simplify the calculation. The eigenfunctions, under this new definition, possess the orthogonality from which the expansion coefficients can be easily deduced. Selecting the optimum truncation of the series, we derive a closed system of simultaneous linear equations for the same number of the unknown reflection and transmission coefficients. The effects of several physical parameters, including the porosity, friction, width, and depth of the porous barrier, on the dispersion relation, reflection and transmission coefficients are discussed in detail through the graphical representations of the solutions. It is concluded that these parameters have certain impacts on the reflection and transmission energy.

THERMAL CONSOLIDATION OF LAYERED POROUS HALF-SPACE TO VARIABLE THERMAL LOADING

Institute of Scientific and Technical Information of China (English)

BAI Bing

2006-01-01

An analytical method was derived for the thermal consolidation of layered,saturated porous half-space to variable thermal loading with time. In the coupled governing equations of linear thermoelastic media, the influences of thermo-osmosis effect and thermal filtration effect were introduced. Solutions in Laplace transform space were first obtained and then numerically inverted. The responses of a double-layered porous space subjected to exponential decaying thermal loading were studied. The influences of the differences between the properties of the two layers (e.g., the coefficient of thermal consolidation, elastic modulus) on thermal consolidation were discussed. The studies show that the coupling effects of displacement and stress fields on temperature field can be completely neglected, however, thc thermo-osmosis effect has an obvious influence on thermal responses.

Acoustic emission in a fluid saturated heterogeneous porous layer with application to hydraulic fracture

Energy Technology Data Exchange (ETDEWEB)

Nelson, J.T. (California Univ., Berkeley, CA (USA). Dept. of Mechanical Engineering Lawrence Berkeley Lab., CA (USA))

1988-11-01

A theoretical model for acoustic emission in a vertically heterogeneous porous layer bounded by semi-infinite solid regions is developed using linearized equations of motion for a fluid/solid mixture and a reflectivity method. Green's functions are derived for both point loads and moments. Numerically integrated propagators represent solutions for intermediate heterogeneous layers in the porous region. These are substituted into a global matrix for solution by Gaussian elimination and back-substitution. Fluid partial stress and seismic responses to dislocations associated with fracturing of a layer of rock with a hydraulically conductive fracture network are computed with the model. A constitutive model is developed for representing the fractured rock layer as a porous material, using commonly accepted relationships for moduli. Derivations of density, tortuosity, and sinuosity are provided. The main results of the model application are the prediction of a substantial fluid partial stress response related to a second mode wave for the porous material. The response is observable for relatively large distances, on the order of several tens of meters. The visco-dynamic transition frequency associated with parabolic versus planar fluid velocity distributions across micro-crack apertures is in the low audio or seismic range, in contrast to materials with small pore size, such as porous rocks, for which the transition frequency is ultrasonic. Seismic responses are predicted for receiver locations both in the layer and in the outlying solid regions. In the porous region, the seismic response includes both shear and dilatational wave arrivals and a second-mode arrival. The second-mode arrival is not observable outside of the layer because of its low velocity relative to the dilatational and shear wave propagation velocities of the solid region.

Effect of layer thickness and printing orientation on mechanical properties and dimensional accuracy of 3D printed porous samples for bone tissue engineering.

Directory of Open Access Journals (Sweden)

Arghavan Farzadi

Full Text Available Powder-based inkjet 3D printing method is one of the most attractive solid free form techniques. It involves a sequential layering process through which 3D porous scaffolds can be directly produced from computer-generated models. 3D printed products' quality are controlled by the optimal build parameters. In this study, Calcium Sulfate based powders were used for porous scaffolds fabrication. The printed scaffolds of 0.8 mm pore size, with different layer thickness and printing orientation, were subjected to the depowdering step. The effects of four layer thicknesses and printing orientations, (parallel to X, Y and Z, on the physical and mechanical properties of printed scaffolds were investigated. It was observed that the compressive strength, toughness and Young's modulus of samples with 0.1125 and 0.125 mm layer thickness were more than others. Furthermore, the results of SEM and μCT analyses showed that samples with 0.1125 mm layer thickness printed in X direction have more dimensional accuracy and significantly close to CAD software based designs with predefined pore size, porosity and pore interconnectivity.

POROUS MEMBRANE TEMPLATED SYNTHESIS OF POLYMER PILLARED LAYER

Institute of Scientific and Technical Information of China (English)

Zhong-wei Niu; Dan Li; Zhen-zhong Yang

2003-01-01

The anodic porous alumina membranes with a definite pore diameter and aspect ratio were used as templates to synthesize polymer pillared layer structures. The pillared polymer was produced in the template membrane pores, and the layer on the template surfaces. Rigid cured epoxy resin, polystyrene and soft hydrogel were chosen to confirm the methodology. The pillars were in the form of either tubes or fibers, which were controlled by the alumina membrane pore surface wettability. The structural features were confirmed by scanning electron microscopy results.

Influence of the anodic etching current density on the morphology of the porous SiC layer

Directory of Open Access Journals (Sweden)

Anh Tuan Cao

2014-03-01

Full Text Available In this report, we fabricated a porous layer in amorphous SiC thin films by using constant-current anodic etching in an electrolyte of aqueous diluted hydrofluoric acid. The morphology of the porous amorphous SiC layer changed as the anodic current density changed: At low current density, the porous layer had a low pore density and consisted of small pores that branched downward. At moderate current density, the pore size and depth increased, and the pores grew perpendicular to the surface, creating a columnar pore structure. At high current density, the porous structure remained perpendicular, the pore size increased, and the pore depth decreased. We explained the changes in pore size and depth at high current density by the growth of a silicon oxide layer during etching at the tips of the pores.

Spontaneous layering of porous silicon layers formed at high current densities

Energy Technology Data Exchange (ETDEWEB)

Parkhutik, Vitali; Curiel-Esparza, Jorge; Millan, Mari-Carmen [R and D Center MTM, Technical University of Valencia, Valencia (Spain); Albella, Jose [Institute of Materials Science (ICMM CSIC) Madrid (Spain)

2005-06-01

We report here a curious effect of spontaneous fracturing of the silicon layers formed in galvanostatic conditions at medium and high current densities. Instead of formation of homogeneous p-Si layer as at low currents, a stack of thin layers is formed. Each layer is nearly separated from others and possesses rather flat interfaces. The effects is observed using p{sup +}-Si wafers for the p-Si formation and starts being noticeable at above 100 mA/cm{sup 2}. We interpret these results in terms of the porous silicon growth model where generation of dynamic mechanical stress during the p-Si growth causes sharp changes in Si dissolution mechanism from anisotropic etching of individual needle-like pores in silicon to their branching and isotropic etching. At this moment p-Si layer loses its adhesion to the surface of Si wafer and another p-Si layer starts growing. One of the mechanisms triggering on the separation of p-Si layers from one another is a fluctuation of local anodic current in the pore bottoms associated with gas bubble evolution during the p-Si formation. (copyright 2005 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Microstructural and Wear Behavior Characterization of Porous Layers Produced by Pulsed Laser Irradiation in Glass-Ceramics Substrates.

Science.gov (United States)

Sola, Daniel; Conde, Ana; García, Iñaki; Gracia-Escosa, Elena; de Damborenea, Juan J; Peña, Jose I

2013-09-09

In this work, wear behavior and microstructural characterization of porous layers produced in glass-ceramic substrates by pulsed laser irradiation in the nanosecond range are studied under unidirectional sliding conditions against AISI316 and corundum counterbodies. Depending on the optical configuration of the laser beam and on the working parameters, the local temperature and pressure applied over the interaction zone can generate a porous glass-ceramic layer. Material transference from the ball to the porous glass-ceramic layer was observed in the wear tests carried out against the AISI316 ball counterface whereas, in the case of the corundum ball, the wear volume loss was concentrated in the porous layer. Wear rate and friction coefficient presented higher values than expected for dense glass-ceramics.

Microstructural and Wear Behavior Characterization of Porous Layers Produced by Pulsed Laser Irradiation in Glass-Ceramics Substrates

Directory of Open Access Journals (Sweden)

Jose I. Peña

2013-09-01

Full Text Available In this work, wear behavior and microstructural characterization of porous layers produced in glass-ceramic substrates by pulsed laser irradiation in the nanosecond range are studied under unidirectional sliding conditions against AISI316 and corundum counterbodies. Depending on the optical configuration of the laser beam and on the working parameters, the local temperature and pressure applied over the interaction zone can generate a porous glass-ceramic layer. Material transference from the ball to the porous glass-ceramic layer was observed in the wear tests carried out against the AISI316 ball counterface whereas, in the case of the corundum ball, the wear volume loss was concentrated in the porous layer. Wear rate and friction coefficient presented higher values than expected for dense glass-ceramics.

Mobility of charge carriers in porous silicon layers

International Nuclear Information System (INIS)

Forsh, P. A.; Martyshov, M. N.; Latysheva, A. P.; Vorontsov, A. S.; Timoshenko, V. Yu.; Kashkarov, P. K.

2008-01-01

The (conduction) mobility of majority charge carriers in porous silicon layers of the n and p types is estimated by joint measurements of electrical conductivity and free charge carrier concentration, which is determined from IR absorption spectra. Adsorption of donor and acceptor molecules leading to a change in local electric fields in the structure is used to identify the processes controlling the mobility in porous silicon. It is found that adsorption of acceptor and donor molecules at porous silicon of the p and n types, respectively, leads to a strong increase in electrical conductivity, which is associated with an increase in the concentration of free carrier as well as in their mobility. The increase in the mobility of charge carriers as a result of adsorption indicates the key role of potential barriers at the boundaries of silicon nanocrystals and may be due to a decrease in the barrier height as a result of adsorption

Effect of porous silicon layer on the performance of Si/oxide photovoltaic and photoelectrochemical cells

International Nuclear Information System (INIS)

Badawy, Waheed A.

2008-01-01

Photovoltaic and photoelectrochemical systems were prepared by the formation of a thin porous film on silicon. The porous silicon layer was formed on the top of a clean oxide free silicon wafer surface by anodic etching in HF/H 2 O/C 2 H 5 OH mixture (2:1:1). The silicon was then covered by an oxide film (tin oxide, ITO or titanium oxide). The oxide films were prepared by the spray/pyrolysis technique which enables doping of the oxide film by different atoms like In, Ru or Sb during the spray process. Doping of SnO 2 or TiO 2 films with Ru atoms improves the surface characteristics of the oxide film which improves the solar conversion efficiency. The prepared solar cells are stable against environmental attack due to the presence of the stable oxide film. It gives relatively high short circuit currents (I sc ), due to the presence of the porous silicon layer, which leads to the recorded high conversion efficiency. Although the open-circuit potential (V oc ) and fill factor (FF) were not affected by the thickness of the porous silicon film, the short circuit current was found to be sensitive to this thickness. An optimum thickness of the porous film and also the oxide layer is required to optimize the solar cell efficiency. The results represent a promising system for the application of porous silicon layers in solar energy converters. The use of porous silicon instead of silicon single crystals in solar cell fabrication and the optimization of the solar conversion efficiency will lead to the reduction of the cost as an important factor and also the increase of the solar cell efficiency making use of the large area of the porous structures

Periodic mixed convection in horizontal porous layer heated from below by isoflux heater

International Nuclear Information System (INIS)

Saeid, Nawaf H.; Pop, I.

2006-01-01

Numerical study for transient mixed convection in a two-dimensional horizontal porous layer heated from below by a constant heat flux source is carried out in the present paper. The transient thermal field, flow field and average Nusselt number are presented for a wide range of the Peclet number, Pe, for the particular case of Rayleigh number Ra=10x2 and the ratio of heater length to the porous layer thickness A=1, 3 and 5. It is found that for A=3 and A=5 with small values of the Peclet number, the free convection mode is dominated, while for large values, of the Peclet number, the forced convection mode is dominated. However, for moderate values the oscillatory mixed convection is observed and a periodic variation of the average Nusselt number is obtained. When the heater length is equal to the porous layer thickness (A=1) the steady-state results are obtained for the range of Pe=0.01-10. (author)

Improved tribological properties of TiC with porous nanostructured TiO2 intermediate layer

International Nuclear Information System (INIS)

Shanaghi, Ali; Ahangarani, Shahrokh; Sabour Rouhaghdam, Ali Reza; Chu, Paul K.

2011-01-01

Highlights: ► The porous TiO 2 nanoparticle coating is deposited as an intermediate layer on steel. ► A homogenous and low friction TiC nanostructure coating is deposited by plasma CVD. ► Intermediate layer can be determined the nucleation and growth of the TiC coating. ► The porous interlayer improves the friction and wear of the TiC nanostructure coating. - Abstract: The mismatch in the thermal expansion coefficients between TiC coatings and steel substrates and residual stress in the TiC degrade the tribological properties. In this work, a porous nanostructured TiO 2 coating is deposited as an intermediate layer on hot-work steel (H 11 ) before final deposition of the TiC film. This intermediate layer is expected to reduce the interfacial energy, decreases the thermal mismatch between TiC and steel, and improves the tribological properties. Grazing incidence X-ray diffraction (GIXRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), atomic force microscopy (AFM), and pin-on-disk are used to study the structure as well as tribological properties such as friction, wear, and hardness. Our results reveal that the porous TiO 2 interlayer improves the friction, wear, hardness, and elastic modulus of the system.

Catalytic reaction in a porous solid subject to a boundary layer flow

Energy Technology Data Exchange (ETDEWEB)

Mihail, R; Teddorescu, C

1978-01-01

A mathematical model of a boundary layer flowing past a catalytic slab was developed which included an analysis of the coupled mass and heat transfer and the heterogeneous chemical reaction. The porous flat plate was used to illustrate the interaction of boundary layer flow with chemical reaction within a porous catalytic body. The model yielded systems of transcendental equations which were solved numerically by means of a superposition integral in connection with a norm reduction procedure. A parametric study was conducted and an analysis of the possible multiplicity of steady states was developed and illustrated for the extreme case of infinite solid thermal conductivity. Tables, diagrams, graphs, and 12 references.

Method of producing buried porous silicon-geramanium layers in monocrystalline silicon lattices

Science.gov (United States)

Fathauer, Robert W. (Inventor); George, Thomas (Inventor); Jones, Eric W. (Inventor)

1997-01-01

Lattices of alternating layers of monocrystalline silicon and porous silicon-germanium have been produced. These single crystal lattices have been fabricated by epitaxial growth of Si and Si--Ge layers followed by patterning into mesa structures. The mesa structures are stain etched resulting in porosification of the Si--Ge layers with a minor amount of porosification of the monocrystalline Si layers. Thicker Si--Ge layers produced in a similar manner emitted visible light at room temperature.

Study on structural properties of epitaxial silicon films on annealed double layer porous silicon

International Nuclear Information System (INIS)

Yue Zhihao; Shen Honglie; Cai Hong; Lv Hongjie; Liu Bin

2012-01-01

In this paper, epitaxial silicon films were grown on annealed double layer porous silicon by LPCVD. The evolvement of the double layer porous silicon before and after thermal annealing was investigated by scanning electron microscope. X-ray diffraction and Raman spectroscopy were used to investigate the structural properties of the epitaxial silicon thin films grown at different temperature and different pressure. The results show that the surface of the low-porosity layer becomes smooth and there are just few silicon-bridges connecting the porous layer and the substrate wafer. The qualities of the epitaxial silicon thin films become better along with increasing deposition temperature. All of the Raman peaks of silicon films with different deposition pressure are situated at 521 cm -1 under the deposition temperature of 1100 °C, and the Raman intensity of the silicon film deposited at 100 Pa is much closer to that of the monocrystalline silicon wafer. The epitaxial silicon films are all (4 0 0)-oriented and (4 0 0) peak of silicon film deposited at 100 Pa is more symmetric.

Salinization effects on the water sorption of porous building materials

NARCIS (Netherlands)

Brocken, H.J.P.; Rook, W.; Adan, O.C.G.

1999-01-01

The interaction of salt transport and moisture transport plays a crucial role in some deterioration mechanisms of porous building materials. For this reason it has been an important research subject for mant' years. Yet most research was still complicated by the lack of experimental techniques

Multiscale modelling for better hygrothermal prediction of porous building materials

Directory of Open Access Journals (Sweden)

Belarbi Rafik

2018-01-01

Full Text Available The aim of this work is to understand the influence of the microstructuralgeometric parameters of porous building materials on the mechanisms of coupled heat, air and moisture transfers, in order to predict behavior of the building to control and improve it in its durability. For this a multi-scale approach is implemented. It consists of mastering the dominant physical phenomena and their interactions on the microscopic scale. Followed by a dual-scale modelling, microscopic-macroscopic, of coupled heat, air and moisture transfers that takes into account the intrinsic properties and microstructural topology of the material using X-ray tomography combined with the correlation of 3D images were undertaken. In fact, the hygromorphicbehavior under hydric solicitations was considered. In this context, a model of coupled heat, air and moisture transfer in porous building materials was developed using the periodic homogenization technique. These informations were subsequently implemented in a dynamic computation simulation that model the hygrothermalbehaviourof material at the scale of the envelopes and indoor air quality of building. Results reveals that is essential to consider the local behaviors of materials, but also to be able to measure and quantify the evolution of its properties on a macroscopic scale from the youngest age of the material. In addition, comparisons between experimental and numerical temperature and relative humidity profilesin multilayers wall and in building envelopes were undertaken. Good agreements were observed.

Transient gas flow through layered porous media

International Nuclear Information System (INIS)

Morrison, F.A. Jr.

1975-01-01

Low Reynolds number isothermal flow of an ideal gas through layered porous material was investigated analytically. Relations governing the transient flow in one dimension are obtained. An implicit, iterative, unconditionally stable finite difference scheme is developed for calculation of such flows. A computer code, SIROCCO, employing this technique has been written and implemented on the LLL computer system. A listing of the code is included. This code may be effectively applied to the evaluation of stemming plans for underground nuclear experiments. (U.S.)

Bovine serum albumin adsorption on passivated porous silicon layers

Science.gov (United States)

Lockwood, David; Boukherroub, Rabah

2005-03-01

Hydrogen-terminated porous silicon (pSi) films were fabricated through electrochemical anodization of crystalline Si in HF-based solutions. The pSi-H surface was chemically functionalized by thermal reaction with undecylenic acid to produce an organic monolayer covalently attached to the silicon surface through Si-C bonds and bearing an acid terminal group. Bovine serum albumin (BSA) was then adsorbed onto the modified surface. SEM showed that the porous films were damaged and partially lifted off the Si substrate after a prolonged BSA adsorption. Ellipsometry revealed that the BSA had penetrated ˜ 1.3 micrometers into the porous structure. The film damage results from BSA anchoring itself tightly through strong electrostatic interactions to the acid-covered Si sidewalls. A change in surface tension during BSA film formation then causes the pSi layer to buckle and lift-off the underlying Si substrate. FTIR results from the modified pSi surfaces showed the presence of strong characteristic Amide I, II and III vibrational bands after BSA adsorption.

Boundary Layer Flows in Porous Media with Lateral Mass Flux

DEFF Research Database (Denmark)

Nemati, H; H, Bararnia; Noori, F

2015-01-01

Solutions for free convection boundary layers on a heated vertical plate with lateral mass flux embedded in a saturated porous medium are presented using the Homotopy Analysis Method and Shooting Numerical Method. Homotopy Analysis Method yields an analytic solution in the form of a rapidly...

Nanomechanical properties of thick porous silicon layers grown on p- and p+-type bulk crystalline Si

International Nuclear Information System (INIS)

Charitidis, C.A.; Skarmoutsou, A.; Nassiopoulou, A.G.; Dragoneas, A.

2011-01-01

Highlights: → The nanomechanical properties of bulk crystalline Si. → The nanomechanical properties of porous Si. → The elastic-plastic deformation of porous Si compared to bulk crystalline quantified by nanoindentation data analysis. - Abstract: The nanomechanical properties and the nanoscale deformation of thick porous Si (PSi) layers of two different morphologies, grown electrochemically on p-type and p+-type Si wafers were investigated by the depth-sensing nanoindentation technique over a small range of loads using a Berkovich indenter and were compared with those of bulk crystalline Si. The microstructure of the thick PSi layers was characterized by field emission scanning electron microscopy. PSi layers on p+-type Si show an anisotropic mesoporous structure with straight vertical pores of diameter in the range of 30-50 nm, while those on p-type Si show a sponge like mesoporous structure. The effect of the microstructure on the mechanical properties of the layers is discussed. It is shown that the hardness and Young's modulus of the PSi layers exhibit a strong dependence on their microstructure. In particular, PSi layers with the anisotropic straight vertical pores show higher hardness and elastic modulus values than sponge-like layers. However, sponge-like PSi layers reveal less plastic deformation and higher wear resistance compared with layers with straight vertical pores.

One-dimensional scanning of moisture in heated porous building materials with NMR.

Science.gov (United States)

van der Heijden, G H A; Huinink, H P; Pel, L; Kopinga, K

2011-02-01

In this paper we present a new dedicated NMR setup which is capable of measuring one-dimensional moisture profiles in heated porous materials. The setup, which is placed in the bore of a 1.5 T whole-body scanner, is capable of reaching temperatures up to 500 °C. Moisture and temperature profiles can be measured quasi simultaneously with a typical time resolution of 2-5 min. A methodology is introduced for correcting temperature effects on NMR measurements at these elevated temperatures. The corrections are based on the Curie law for paramagnetism and the observed temperature dependence of the relaxation mechanisms occurring in porous materials. Both these corrections are used to obtain a moisture content profile from the raw NMR signal profile. To illustrate the methodology, a one-sided heating experiment of concrete with a moisture content in equilibrium with 97% RH is presented. This kind of heating experiment is of particular interest in the research on fire spalling of concrete, since it directly reveals the moisture and heat transport occurring inside the concrete. The obtained moisture profiles reveal a moisture peak building up behind the boiling front, resulting in a saturated layer. To our knowledge the direct proof of the formation of a moisture peak and subsequent moisture clogging has not been reported before. Copyright © 2010 Elsevier Inc. All rights reserved.

Magnetohydrodynamic boundary layer flow past a porous substrate with Beavers-Joseph boundary condition

International Nuclear Information System (INIS)

Jat, R.N.; Chaudhary, Santosh

2009-01-01

The flow of an electrically conducting fluid past a porous substrate attached to the flat plate with Beavers-Joseph boundary condition under the influence of a uniform transverse magnetic field has been studied. Taking suitable similar variables, the momentum equation is transformed to ordinary differential equation and solved by standard techniques. The energy equation is solved by considering two boundary layers, one in the porous substrate and the other above the porous substrate. The velocity and temperature distributions along with Nusselt number are discussed numerically and presented through graphs. (author)

Structure, composition and morphology of bioactive titanate layer on porous titanium surfaces

Science.gov (United States)

Li, Jinshan; Wang, Xiaohua; Hu, Rui; Kou, Hongchao

2014-07-01

A bioactive coating was produced on pore surfaces of porous titanium samples by an amendatory alkali-heat treatment method. Porous titanium was prepared by powder metallurgy and its porosity and average size were 45% and 135 μm, respectively. Coating morphology, coating structure and phase constituents were examined by SEM, XPS and XRD. It was found that a micro-network structure with sizes of cells, and redundant Ca ion was detected in the titanate layer. The concentration distribution of Ti, O, Ca and Na in the coating showed a compositional gradient from the intermediate layer toward the outer surface. These compositional gradients indicate that the coating bonded to Ti substrate without a distinct interface. After immersion into the SBF solution for 3 days, a bone-like carbonate-hydroxylapatite showing a good biocompatibility was detected on the coating surface. And the redundant Ca advanced the bioactivity of the coating. Thus, the present modification is expected to allow the use of the bioactive porous titanium as artificial bones even under load-bearing conditions.

Improved tribological properties of TiC with porous nanostructured TiO{sub 2} intermediate layer

Energy Technology Data Exchange (ETDEWEB)

Shanaghi, Ali, E-mail: alishanaghi@gmail.com [Surface Engineering Laboratory, Materials Engineering Department, Faculty of Engineering, Tarbiat Modares University, P.O. Box 14115-143, Tehran (Iran, Islamic Republic of); Department of Physics and Materials Science, City University of Hong Kong, Tat Chee Avenue, Kowloon, Hong Kong (China); Ahangarani, Shahrokh, E-mail: sh.ahangarani@gmail.com [Advanced Materials and Renewable Energies Department, Iranian Research Organization for Science and Technology, P.O. Box 15815-3538, Tehran (Iran, Islamic Republic of); Sabour Rouhaghdam, Ali Reza, E-mail: sabour01@modares.ac.ir [Surface Engineering Laboratory, Materials Engineering Department, Faculty of Engineering, Tarbiat Modares University, P.O. Box 14115-143, Tehran (Iran, Islamic Republic of); Chu, Paul K., E-mail: paul.chu@cityu.edu.hk [Department of Physics and Materials Science, City University of Hong Kong, Tat Chee Avenue, Kowloon, Hong Kong (China)

2011-12-15

Highlights: Black-Right-Pointing-Pointer The porous TiO{sub 2} nanoparticle coating is deposited as an intermediate layer on steel. Black-Right-Pointing-Pointer A homogenous and low friction TiC nanostructure coating is deposited by plasma CVD. Black-Right-Pointing-Pointer Intermediate layer can be determined the nucleation and growth of the TiC coating. Black-Right-Pointing-Pointer The porous interlayer improves the friction and wear of the TiC nanostructure coating. - Abstract: The mismatch in the thermal expansion coefficients between TiC coatings and steel substrates and residual stress in the TiC degrade the tribological properties. In this work, a porous nanostructured TiO{sub 2} coating is deposited as an intermediate layer on hot-work steel (H{sub 11}) before final deposition of the TiC film. This intermediate layer is expected to reduce the interfacial energy, decreases the thermal mismatch between TiC and steel, and improves the tribological properties. Grazing incidence X-ray diffraction (GIXRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), atomic force microscopy (AFM), and pin-on-disk are used to study the structure as well as tribological properties such as friction, wear, and hardness. Our results reveal that the porous TiO{sub 2} interlayer improves the friction, wear, hardness, and elastic modulus of the system.

Experimental investigation of convective stability in a superposed fluid and porous layer when heated from below

Science.gov (United States)

Chen, Falin; Chen, C. F.

1989-01-01

Experiments have been carried out in a horizontal superposed fluid and porous layer contained in a test box 24 cm x 12 cm x 4 cm high. The porous layer consisted of 3 mm diameter glass beads, and the fluids used were water, 60 and 90 percent glycerin-water solutions, and 100 percent glycerin. The depth ratio d, which is the ratio of the thickness of the fluid layer to that of the porous layer, varied from 0 to 1.0. Fluids of increasingly higher viscosity were used for cases with larger d in order to keep the temperature difference across the tank within reasonable limits. The size of the convection cells was inferred from temperature measurements made with embedded thermocouples and from temperature distributions at the top of the layer by use of liquid crystal film. The experimental results showed: (1) a precipitous decrease in the critical Rayleigh number as the depth of the fluid layer was increased from zero, and (2) an eightfold decrease in the critical wavelength between d = 0.1 and 0.2. Both of these results were predicted by the linear stability theory reported earlier (Chen and Chen, 1988).

Selective formation of porous layer on n-type InP by anodic etching combined with scratching

International Nuclear Information System (INIS)

Seo, Masahiro; Yamaya, Tadafumi

2005-01-01

The selective formation of porous layer on n-type InP (001) surface was investigated by using scratching with a diamond scriber followed by anodic etching in deaerated 0.5M HCl. Since the InP specimen was highly doped, the anodic etching proceeded in the dark. The potentiodynamic polarization showed the anodic current shoulder in the potential region between 0.8 and 1.3V (SHE) for the scratched area in addition to the anodic current peak at 1.7V (SHE) for the intact area. The selective formation of porous layer on the scratched are was brought by the anodic etching at a constant potential between 1.0 and 1.2V (SHE) for a certain time. The nucleation and growth of etch pits on intact area, however, took place when the time passed the critical value. The cross section of porous layer on the scratched area perpendicular to the [1-bar 10] or [110] scratching direction had a V-shape, while the cross section of porous layer on the scratched area parallel to the [1-bar 10] or [110] scratching direction had a band structure with stripes oriented to the [1-bar 11] or [11-bar 1] direction. Moreover, nano-scratching at a constant normal force in the micro-Newton range followed by anodic etching showed the possibility for selective formation of porous wire with a nano-meter width

Selective formation of porous layer on n-type InP by anodic etching combined with scratching

Energy Technology Data Exchange (ETDEWEB)

Seo, Masahiro [Graduate School of Engineering, Hokkaido University, Kita-13 Jo, Nishi-8 Chome, Kita-ku, Sapporo 060-8628 (Japan)]. E-mail: seo@elechem1-mc.eng.hokudai.ac.jp; Yamaya, Tadafumi [Graduate School of Engineering, Hokkaido University, Kita-13 Jo, Nishi-8 Chome, Kita-ku, Sapporo 060-8628 (Japan)

2005-11-10

The selective formation of porous layer on n-type InP (001) surface was investigated by using scratching with a diamond scriber followed by anodic etching in deaerated 0.5M HCl. Since the InP specimen was highly doped, the anodic etching proceeded in the dark. The potentiodynamic polarization showed the anodic current shoulder in the potential region between 0.8 and 1.3V (SHE) for the scratched area in addition to the anodic current peak at 1.7V (SHE) for the intact area. The selective formation of porous layer on the scratched are was brought by the anodic etching at a constant potential between 1.0 and 1.2V (SHE) for a certain time. The nucleation and growth of etch pits on intact area, however, took place when the time passed the critical value. The cross section of porous layer on the scratched area perpendicular to the [1-bar 10] or [110] scratching direction had a V-shape, while the cross section of porous layer on the scratched area parallel to the [1-bar 10] or [110] scratching direction had a band structure with stripes oriented to the [1-bar 11] or [11-bar 1] direction. Moreover, nano-scratching at a constant normal force in the micro-Newton range followed by anodic etching showed the possibility for selective formation of porous wire with a nano-meter width.

Improved perovskite morphology and crystallinity using porous PbI2 layers for efficient planar heterojunction solar cells

Science.gov (United States)

Jia, Xianyu; Hu, Ziyang; Xu, Jie; Huang, Like; Zhang, Jing; Zhang, Jianjun; Zhu, Yuejin

2017-12-01

We demonstrate the flexible and facile use of porous PbI2 layers to fabricate high quality perovskite films with a dense surface and without residual PbI2. PbI2 precursor solutions by adding polystyrene pore-forming agents are first spin-coated to fabricate the wet film. A porous PbI2 layer is formed by washing off polystyrene using organic solvents. The porous PbI2 layer not only serves as a channel for transporting the CH3NH3I solution but also offers extremely enlarged contact areas, facilitating interfacial reaction with CH3NH3I. Shiny smooth perovskite films with excellent electronic quality and solar cells with an efficiency up to 17% are obtained.

Characterization of transport phenomena in porous transport layers using X-ray microtomography

Science.gov (United States)

Hasanpour, S.; Hoorfar, M.; Phillion, A. B.

2017-06-01

Among different methods available for estimating the transport properties of porous transport layers (PTLs) of polymer electrolyte membrane fuel cells, X-ray micro computed tomography (X-μCT) imaging in combination with image-based numerical simulation has been recognized as a viable tool. In this study, four commercially-available single-layer and dual-layer PTLs are analyzed using this method in order to compare and contrast transport properties between different PTLs, as well as the variability within a single sheet. Complete transport property datasets are created for each PTL. The simulation predictions indicate that PTLs with high porosity show considerable variability in permeability and effective diffusivity, while PTLs with low porosity do not. Furthermore, it is seen that the Tomadakis-Sotirchos (TS) analytical expressions for porous media match the image-based simulations when porosity is relatively low but predict higher permeability and effective diffusivity for porosity values greater than 80%. Finally, the simulations show that cracks within MPL of dual-layer PTLs have a significant effect on the overall permeability and effective diffusivity of the PTLs. This must be considered when estimating the transport properties of dual-layer PTLs. These findings can be used to improve macro-scale models of product and reactant transport within fuel cells, and ultimately, fuel cell efficiency.

Neutron radiography for the characterization of porous structure in degraded building stones

International Nuclear Information System (INIS)

Barone, G; Mazzoleni, P; Raneri, S; Crupi, V; Longo, F; Majolino, D; Venuti, V; Teixeira, J

2014-01-01

As it is well known, the porous structure of stones can change due to different degradation processes that modify the characteristics of freshly quarried blocks. Their knowledge is fundamental for predicting the behavior of stones and the efficacy of conservative treatments. In this context, neutron radiography is a useful tool not only to visualize the structure of porous materials, but also to evaluate the degree of degradation and surface modifications resulting from weathering processes. Furthermore, since thermal neutrons suffer a strong attenuation by hydrogen, this technique is effective in order to investigate the amount of absorbed water in building materials. In the present work, we report a neutron radiography investigation of limestones cropping out in the South-Eastern Sicily and widely used as building stones in Baroque monuments of the Noto Valley. The analyzed samples have been submitted to cyclic salt crystallization that simulate degradation processes acting in exposed stones of buildings. The obtained results demonstrate the interest of neutron radiography to better understand deterioration processes in limestones and to acquire information useful for restoration projects

Improved Modeling Approaches for Constrained Sintering of Bi-Layered Porous Structures

DEFF Research Database (Denmark)

Tadesse Molla, Tesfaye; Frandsen, Henrik Lund; Esposito, Vincenzo

2012-01-01

Shape instabilities during constrained sintering experiment of bi-layer porous and dense cerium gadolinium oxide (CGO) structures have been analyzed. An analytical and a numerical model based on the continuum theory of sintering has been implemented to describe the evolution of bow and densificat...

Three-phase flow analysis of dense nonaqueous phase liquid infiltration in horizontally layered porous media

NARCIS (Netherlands)

Wipfler, E.L.; Dijke, van M.I.J.; Zee, van der S.E.A.T.M.

2004-01-01

We considered dense nonaqueous phase liquid (DNAPL) infiltration into a water-unsaturated porous medium that consists of two horizontal layers, of which the top layer has a lower intrinsic permeability than the bottom layer. DNAPL is the intermediate-wetting fluid with respect to the wetting water

A POROUS, LAYERED HELIOPAUSE

Energy Technology Data Exchange (ETDEWEB)

Swisdak, M.; Drake, J. F. [Institute for Research in Electronics and Applied Physics, University of Maryland, College Park, MD 20742 (United States); Opher, M., E-mail: swisdak@umd.edu, E-mail: drake@umd.edu, E-mail: mopher@bu.edu [Department of Astronomy, Boston University, 725 Commonwealth Avenue, Boston, MA 02215 (United States)

2013-09-01

The picture of the heliopause (HP)-the boundary between the domains of the Sun and the local interstellar medium (LISM)-as a pristine interface with a large rotation in the magnetic field fails to describe recent Voyager 1 (V1) data. Magnetohydrodynamic (MHD) simulations of the global heliosphere reveal that the rotation angle of the magnetic field across the HP at V1 is small. Particle-in-cell simulations, based on cuts through the MHD model at V1's location, suggest that the sectored region of the heliosheath (HS) produces large-scale magnetic islands that reconnect with the interstellar magnetic field while mixing LISM and HS plasma. Cuts across the simulation reveal multiple, anti-correlated jumps in the number densities of LISM and HS particles, similar to those observed, at the magnetic separatrices. A model is presented, based on both the observations and simulations, of the HP as a porous, multi-layered structure threaded by magnetic fields. This model further suggests that contrary to the conclusions of recent papers, V1 has already crossed the HP.

A diffusivity model for predicting VOC diffusion in porous building materials based on fractal theory

International Nuclear Information System (INIS)

Liu, Yanfeng; Zhou, Xiaojun; Wang, Dengjia; Song, Cong; Liu, Jiaping

2015-01-01

Highlights: • Fractal theory is introduced into the prediction of VOC diffusion coefficient. • MSFC model of the diffusion coefficient is developed for porous building materials. • The MSFC model contains detailed pore structure parameters. • The accuracy of the MSFC model is verified by independent experiments. - Abstract: Most building materials are porous media, and the internal diffusion coefficients of such materials have an important influences on the emission characteristics of volatile organic compounds (VOCs). The pore structure of porous building materials has a significant impact on the diffusion coefficient. However, the complex structural characteristics bring great difficulties to the model development. The existing prediction models of the diffusion coefficient are flawed and need to be improved. Using scanning electron microscope (SEM) observations and mercury intrusion porosimetry (MIP) tests of typical porous building materials, this study developed a new diffusivity model: the multistage series-connection fractal capillary-bundle (MSFC) model. The model considers the variable-diameter capillaries formed by macropores connected in series as the main mass transfer paths, and the diameter distribution of the capillary bundles obeys a fractal power law in the cross section. In addition, the tortuosity of the macrocapillary segments with different diameters is obtained by the fractal theory. Mesopores serve as the connections between the macrocapillary segments rather than as the main mass transfer paths. The theoretical results obtained using the MSFC model yielded a highly accurate prediction of the diffusion coefficients and were in a good agreement with the VOC concentration measurements in the environmental test chamber.

Stability analysis of natural convection in superposed fluid and porous layers

International Nuclear Information System (INIS)

Hirata, S.C.; Goyeau, B.; Gobin, D.; Cotta, R.M.

2005-01-01

A linear stability analysis of the onset of thermal natural convection in superposed fluid and porous layers is called out. The resulting eigenvalue problem is solved using a integral transformation technique. The effect of the variation of the Darcy number on the stability of the system is analyzed. (authors)

Stability analysis of natural convection in superposed fluid and porous layers

Energy Technology Data Exchange (ETDEWEB)

Hirata, S.C.; Goyeau, B.; Gobin, D. [Paris-11 Univ. - Paris-6, FAST - UMR CNRS 7608, 91 - Orsay (France); Cotta, R.M. [Rio de Janeiro Univ. (LTTC/PEM/EE/COPPE/UFRJ), RJ (Brazil)

2005-07-01

A linear stability analysis of the onset of thermal natural convection in superposed fluid and porous layers is called out. The resulting eigenvalue problem is solved using a integral transformation technique. The effect of the variation of the Darcy number on the stability of the system is analyzed. (authors)

Photoluminescence enhancement in porous SiC passivated by atomic layer deposited Al2O3 films

DEFF Research Database (Denmark)

Lu, Weifang; Iwasa, Yoshimi; Ou, Yiyu

2016-01-01

Porous SiC co-doped with B and N was passivated by atomic layer deposited (ALD) Al2O3 films to enhance the photoluminescence. After optimizing the deposition conditions, as high as 14.9 times photoluminescence enhancement has been achieved.......Porous SiC co-doped with B and N was passivated by atomic layer deposited (ALD) Al2O3 films to enhance the photoluminescence. After optimizing the deposition conditions, as high as 14.9 times photoluminescence enhancement has been achieved....

High-resolution synchrotron diffraction study of porous buffer InP(001) layers

Czech Academy of Sciences Publication Activity Database

Lomov, A. A.; Punegov, V. I.; Nohavica, Dušan; Chuev, M.A.; Vasiliev, A.L.; Novikov, D. V.

2014-01-01

Roč. 47, č. 5 (2014), s. 1614-1625 ISSN 0021-8898 Institutional support: RVO:67985882 Keywords : porous layers * X-ray reciprocal space mapping * indium phosphide Subject RIV: JA - Electronics ; Optoelectronics, Electrical Engineering Impact factor: 3.720, year: 2014

Optical performance of hybrid porous silicon-porous alumina multilayers

Science.gov (United States)

Cencha, L. G.; Antonio Hernández, C.; Forzani, L.; Urteaga, R.; Koropecki, R. R.

2018-05-01

In this work, we study the optical response of structures involving porous silicon and porous alumina in a multi-layered hybrid structure. We performed a rational design of the optimal sequence necessary to produce a high transmission and selective filter, with potential applications in chemical and biosensors. The combination of these porous materials can be used to exploit its distinguishing features, i.e., high transparency of alumina and high refractive index of porous silicon. We assembled hybrid microcavities with a central porous alumina layer between two porous silicon Bragg reflectors. In this way, we constructed a Fabry-Perot resonator with high reflectivity and low absorption that improves the quality of the filter compared to a microcavity built only with porous silicon or porous alumina. We explored a simpler design in which one of the Bragg reflectors is replaced by the aluminium that remains bound to the alumina after its fabrication. We theoretically explored the potential of the proposal and its limitations when considering the roughness of the layers. We found that the quality of a microcavity made entirely with porous silicon shows a limit in the visible range due to light absorption. This limitation is overcome in the hybrid scheme, with the roughness of the layers determining the ultimate quality. Q-factors of 220 are experimentally obtained for microcavities supported on aluminium, while Q-factors around 600 are reached for microcavities with double Bragg reflectors, centred at 560 nm. This represents a four-fold increase with respect to the optimal porous silicon microcavity at this wavelength.

Development and Characterization of Non-Conventional Micro-Porous Layers for PEM Fuel Cells

Directory of Open Access Journals (Sweden)

Riccardo Balzarotti

2015-07-01

Full Text Available Gas diffusion medium (GDM is a crucial component in proton exchange membrane fuel cells (PEMFCs. Being composed of a gas diffusion layer (GDL with a micro-porous layer (MPL coated onto it, it ensures a proper water management due to the highly hydrophobic materials employed in cell assembly. In current commercial applications, the desired water repellent behaviour is usually obtained by using polytetrafluoroethylene (PTFE. In this work, Fluorolink® P56 (Solvay Specialty Polymers, Milan, Italy, a commercially available, anionic, segmented high molecular weight polyfluorourethane with perfluoropolyether groups was extensively evaluated as an alternative to PTFE for micro-porous layer hydrophobization. A change in polymer used is desirable in order to simplify the production process, both in terms of ink formulation and thermal treatment, as well as to get a higher hydrophobicity and, consequently, more efficient water management. Innovative prepared samples were compared to a PTFE-based GDM, in order to assess differences both from morphological and from an electrochemical point of view.

Analytical and numerical stability analysis of Soret-driven convection in a horizontal porous layer: the effect of conducting bounding plates

Energy Technology Data Exchange (ETDEWEB)

Ouattara, B; Khouzam, A; Mojtabi, A [Universite de Toulouse (France); INPT, UPS (France); IMFT (Institut de Mecanique des Fluides de Toulouse), Allee Camille Soula, F-31400 Toulouse (France); Charrier-Mojtabi, M C, E-mail: bouattar@imft.fr, E-mail: akhouzam@imft.fr, E-mail: mojtabi@imft.fr, E-mail: cmojtabi@cict.fr [PHASE, EA 810, UFR PCA, Universite Paul Sabatier, 118 route de Narbonne, 31062 Toulouse cedex (France)

2012-06-01

The aim of this study was to investigate the effect of conducting boundaries on the onset of convection in a binary fluid-saturated porous layer. The isotropic saturated porous layer is bounded by two impermeable but thermally conducting plates, subjected to a constant heat flux. These plates have identical conductivity. Moreover, the conductivity of the plates is generally different from the porous layer conductivity. The overall layer is of large extent in both horizontal directions. The problem is governed by seven dimensionless parameters, namely the normalized porosity of the medium {epsilon}, the ratio of plates over the porous layer thickness {delta} and their relative thermal conductivities ratio d, the separation ratio {delta}, the Lewis number Le and thermal Rayleigh number Ra. In this work, an analytical and numerical stability analysis is performed. The equilibrium solution is found to lose its stability via a stationary bifurcation or a Hopf bifurcation depending on the values of the dimensionless parameters. For the long-wavelength mode, the critical Rayleigh number is obtained as Ra{sub cs}=12(1+2d{delta} )/[1+{psi} (2d{delta}Le+Le+1)] and k{sub cs}=0 for {psi}> {psi} {sub uni}> 0. This work extends an earlier paper by Mojtabi and Rees (2011 Int. J. Heat Mass Transfer 54 293-301) who considered a configuration where the porous layer is saturated by a pure fluid.

Method of model reduction and multifidelity models for solute transport in random layered porous media

Energy Technology Data Exchange (ETDEWEB)

Xu, Zhijie; Tartakovsky, Alexandre M.

2017-09-01

This work presents a hierarchical model for solute transport in bounded layered porous media with random permeability. The model generalizes the Taylor-Aris dispersion theory to stochastic transport in random layered porous media with a known velocity covariance function. In the hierarchical model, we represent (random) concentration in terms of its cross-sectional average and a variation function. We derive a one-dimensional stochastic advection-dispersion-type equation for the average concentration and a stochastic Poisson equation for the variation function, as well as expressions for the effective velocity and dispersion coefficient. We observe that velocity fluctuations enhance dispersion in a non-monotonic fashion: the dispersion initially increases with correlation length λ, reaches a maximum, and decreases to zero at infinity. Maximum enhancement can be obtained at the correlation length about 0.25 the size of the porous media perpendicular to flow.

Atmospheric methane removal by methane-oxidizing bacteria immobilized on porous building materials

NARCIS (Netherlands)

Ganendra, G; De Muynck, W; Ho, A.; Hoefman, S.; De Vos, P.; Boeckx, P.; Boon, N.

2014-01-01

Biological treatment using methane-oxidizing bacteria (MOB) immobilized on six porous carrier materials have been used to mitigate methane emission. Experiments were performed with different MOB inoculated in building materials at high (similar to 20 % (v/v)) and low (similar to 100 ppmv) methane

Pore-Network Modeling of Water and Vapor Transport in the Micro Porous Layer and Gas Diffusion Layer of a Polymer Electrolyte Fuel Cell

NARCIS (Netherlands)

Qin, C.; Hassanizadeh, S.M.; van Oosterhout, L.M.

2016-01-01

In the cathode side of a polymer electrolyte fuel cell (PEFC), a micro porous layer (MPL) added between the catalyst layer (CL) and the gas diffusion layer (GDL) plays an important role in water management. In this work, by using both quasi-static and dynamic pore-network models, water and vapor

A porous layer: an evidence for the deterioration of MOVPE InN grown at high temperature (∝650 C)

International Nuclear Information System (INIS)

Sugita, K.; Hashimoto, A.; Yamamoto, A.

2009-01-01

This paper indicates an evidence for the deterioration of the MOVPE InN during the growth at high temperature (∝650 C). It is noted that the deterioration occurs near the interface and InN film becomes porous layer during the further growth. The porous layer has high electron density. The rate-limiting process of N-face InN decomposition depends on atomic hydrogen. The atomic hydrogen produced by the decomposition of NH 3 is responsible for the deterioration of InN film. The crystal quality of InN improves with decreasing the porous layer which is important for MOVPE InN. (copyright 2009 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Laser study of phase changes in the surface layer of porous materials

International Nuclear Information System (INIS)

Wojtatowicz, T W

2001-01-01

The paper presents some aspects of the use of interference patterns observed upon reflection of laser radiation from the surface of a porous solid (laser speckles) for the study of moisture condensation in the near-surface layer. (interaction of laser radiation with matter. laser plasma)

Study the formation of porous surface layer for a new biomedical titanium alloy

Science.gov (United States)

Talib Mohammed, Mohsin; Diwan, Abass Ali; Ali, Osamah Ihsan

2018-03-01

In the present work, chemical treatment using hydrogen peroxide (H2O2) oxidation and subsequent thermal treatment was applied to create a uniform porous layer over the surface of a new metastable β-Ti alloy. The results revealed that this oxidation treatment can create a stable ultrafine porous film over the oxidized surface. This promoted the electrochemical characteristics of H2O2-treated Ti-Zr-Nb (TZN) alloy system, presenting nobler corrosion behavior in simulated body fluid (SBF) comparing with untreated sample.

Development of membrane filters with nanostructured porous layer by coating of metal nanoparticles sintered onto a micro-filter

International Nuclear Information System (INIS)

Park, Seok Joo; Park, Young Ok; Lee, Dong Geun; Ryu, Jeong In

2008-01-01

The membrane filter adhered with nanostructured porous layer was made by heat treatment after deposition of nanoparticle-agglomerates sintered in aerosol phase onto a conventional micron-fibrous metal filter as a substrate filter. The Sintered-Nanoparticle-Agglomerates-coated NanoStructured porous layer Membrane Filter (SNA-NSMF), whose the filtration performance was improved compared with the conventional metal membrane filters, was developed by adhesion of nanoparticle-agglomerates of dendrite structure sintered onto the micron-fibrous metal filter. The size of nanoparticle-agglomerates of dendrite structure decreased with increasing the sintering temperature because nanoparticle-agglomerates shrank. When shrinking nanoparticle-agglomerates were deposited and treated with heat onto the conventional micron-fibrous metal filter, pore size of nanostructured porous layer decreased. Therefore, pressure drops of SNA-NSMFs increased from 0.3 to 0.516 KPa and filtration efficiencies remarkably increased from 95.612 to 99.9993%

A diffusivity model for predicting VOC diffusion in porous building materials based on fractal theory.

Science.gov (United States)

Liu, Yanfeng; Zhou, Xiaojun; Wang, Dengjia; Song, Cong; Liu, Jiaping

2015-12-15

Most building materials are porous media, and the internal diffusion coefficients of such materials have an important influences on the emission characteristics of volatile organic compounds (VOCs). The pore structure of porous building materials has a significant impact on the diffusion coefficient. However, the complex structural characteristics bring great difficulties to the model development. The existing prediction models of the diffusion coefficient are flawed and need to be improved. Using scanning electron microscope (SEM) observations and mercury intrusion porosimetry (MIP) tests of typical porous building materials, this study developed a new diffusivity model: the multistage series-connection fractal capillary-bundle (MSFC) model. The model considers the variable-diameter capillaries formed by macropores connected in series as the main mass transfer paths, and the diameter distribution of the capillary bundles obeys a fractal power law in the cross section. In addition, the tortuosity of the macrocapillary segments with different diameters is obtained by the fractal theory. Mesopores serve as the connections between the macrocapillary segments rather than as the main mass transfer paths. The theoretical results obtained using the MSFC model yielded a highly accurate prediction of the diffusion coefficients and were in a good agreement with the VOC concentration measurements in the environmental test chamber. Copyright © 2015 Elsevier B.V. All rights reserved.

Room-temperature synthesis of three-dimensional porous ZnO@CuNi hybrid magnetic layers with photoluminescent and photocatalytic properties

Science.gov (United States)

Guerrero, Miguel; Zhang, Jin; Altube, Ainhoa; García-Lecina, Eva; Roldan, Mònica; Baró, Maria Dolors; Pellicer, Eva; Sort, Jordi

2016-01-01

Abstract A facile synthetic approach to prepare porous ZnO@CuNi hybrid films is presented. Initially, magnetic CuNi porous layers (consisting of phase separated CuNi alloys) are successfully grown by electrodeposition at different current densities using H2 bubbles as a dynamic template to generate the porosity. The porous CuNi alloys serve as parent scaffolds to be subsequently filled with a solution containing ZnO nanoparticles previously synthesized by sol-gel. The dispersed nanoparticles are deposited dropwise onto the CuNi frameworks and the solvent is left to evaporate while the nanoparticles impregnate the interior of the pores, rendering ZnO-coated CuNi 3D porous structures. No thermal annealing is required to obtain the porous films. The synthesized hybrid porous layers exhibit an interesting combination of tunable ferromagnetic and photoluminescent properties. In addition, the aqueous photocatalytic activity of the composite is studied under UV−visible light irradiation for the degradation of Rhodamine B. The proposed method represents a fast and inexpensive approach towards the implementation of devices based on metal-semiconductor porous systems, avoiding the use of post-synthesis heat treatment steps which could cause deleterious oxidation of the metallic counterpart, as well as collapse of the porous structure and loss of the ferromagnetic properties. PMID:27877868

Cooperation of micro- and meso-porous carbon electrode materials in electric double-layer capacitors

Energy Technology Data Exchange (ETDEWEB)

Zheng, Cheng [State Key Laboratory of Electroanalytical Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, 5625 Renmin Street, Changchun 130022, Jilin Province (China); Graduate University of Chinese Academy of Sciences, Beijing 100039 (China); Qi, Li; Wang, Hongyu [State Key Laboratory of Electroanalytical Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, 5625 Renmin Street, Changchun 130022, Jilin Province (China); Yoshio, Masaki [Advanced Research Center, Saga University, 1341 Yoga-machi, Saga 840-0047 (Japan)

2010-07-01

The capacitive characteristics of micro- and meso-porous carbon materials have been compared in cyclic voltammetric studies and galvanostatic charge-discharge tests. Meso-porous carbon can keep certain high capacitance values at high scan rates, whereas micro-porous carbon possesses very high capacitance values at low scan rates but fades quickly as the scan rate rises up. For better performance of electric double-layer capacitors (EDLCs), the cooperative application of both kinds of carbon materials has been proposed in the following two ways: mixing both kinds of carbons in the same electrode or using the asymmetric configuration of carbon electrodes in the same EDLC. The cooperative effect on the electrochemical performance has also been addressed. (author)

Effective optimization of surface passivation on porous silicon carbide using atomic layer deposited Al2O3

DEFF Research Database (Denmark)

Lu, Weifang; Iwasa, Yoshimi; Ou, Yiyu

2017-01-01

Porous silicon carbide (B–N co-doped SiC) produced by anodic oxidation showed strong photoluminescence (PL) at around 520 nm excited by a 375 nm laser. The porous SiC samples were passivated by atomic layer deposited (ALD) aluminum oxide (Al2O3) films, resulting in a significant enhancement...

Expanded Organic Building Units for the Construction of Highly Porous Metal-Organic Frameworks

NARCIS (Netherlands)

Kong, G.Q.; Han, Z.D.; He, Y.; Qu, S.; Zhou, W.; Yildirim, T.; Krishna, R.; Zou, C.; Chen, B.; Wu, C.D.

2013-01-01

wo new organic building units that contain dicarboxylate sites for their self-assembly with paddlewheel [Cu2(CO2)4] units have been successfully developed to construct two isoreticular porous metal-organic frameworks (MOFs), ZJU-35 and ZJU-36, which have the same tbo topologies (Reticular Chemistry

CuGaS2 and CuGaS2–ZnS Porous Layers from Solution-Processed Nanocrystals

Science.gov (United States)

Guardia, Pablo; Estradé, Sònia; Peiró, Francesca; Cabot, Andreu

2018-01-01

The manufacturing of semiconducting films using solution-based approaches is considered a low cost alternative to vacuum-based thin film deposition strategies. An additional advantage of solution processing methods is the possibility to control the layer nano/microstructure. Here, we detail the production of mesoporous CuGaS2 (CGS) and ZnS layers from spin-coating and subsequent cross-linking through chalcogen-chalcogen bonds of properly functionalized nanocrystals (NCs). We further produce NC-based porous CGS/ZnS bilayers and NC-based CGS–ZnS composite layers using the same strategy. Photoelectrochemical measurements are used to demonstrate the efficacy of porous layers, and particularly the CGS/ZnS bilayers, for improved current densities and photoresponses relative to denser films deposited from as-produced NCs. PMID:29621198

The Comparison of Engineering Properties Between Single and Double Layer Porous Asphalt made of Packing Gradation

Directory of Open Access Journals (Sweden)

Hardiman M. Y

2008-01-01

Full Text Available is paper presents the comparison of engineering properties between single and double layer porous asphalt (SLPA and DLPA made of packing gradation. Three nominal maximum aggregate sizes (NMAS were tested each made up of 10, 14, and 20 mm for SLPA. While for the DLPA with 30, 20, and 15 mm top layer are made of 10 and 14 mm NMAS, with a base layer of 20 mm NMAS. Total thickness of all mixes is 70 mm. Binders used are 60/70 penetration base bitumen and polymer binder styrene-butadiene-styrene (SBS. The result shows that the properties of SLPA mix namely permeability and resistance to abrasion loss decreases when the NMAS in SLPA decreases. The abrasion loss of DLPA mixes increases when the porous asphalt top layer thickness decreases, while drainage time value decreases. However, SLPA with 20 mm NMAS exhibits higher abrasion loss compared to all DLPA mixes.

Mesoscopic objects, porous layers and nanocomposites-Possibilities of sol-gel chemistry

International Nuclear Information System (INIS)

Piwonski, Ireneusz

2009-01-01

The goal of this study was to prepare mesoscopic objects, thin porous films and nanocomposite coatings with the use of sol-gel technique. Silica nanotubes, titania nanoparticles, porous titania and zirconia coatings as well as titania nanocomposites were successfully synthesized by changing the type of sol-gel precursor, sol composition and applying dip-coating deposition procedure in order to obtain thin films or coatings. All materials were visualized and characterized by the Atomic Force Microcscopy (AFM) technique. Moreover, characterization of titania nanocomposites was extended to the tribological tests performed by means of microtribometer operating in normal loads range of 30-100 mN. The AFM analysis of mesoscopic objects and nanoparticles showed that the diameter of synthesized silica nanotubes was 60-70 nm and the size of titania nanoparticles was 43 nm. In case of porous layers the pore size in titania and zirconia coatings oscillated between 100 and 240 nm, however their shape and distribution were irregular. Microtribological studies of nanocomposites revealed the moderate decrease of the coefficient of friction for samples containing 5, 15 and 5 wt.% of zirconia nanoparticles in titania coatings annealed at 100, 500 and 1000 deg. C respectively. An enhancement of antiwear properties was already observed for 1 wt.% of nanophase content, except the sample annealed at 500 deg. C. It was also found that the annealing at high temperatures is a primary factor which affects the reduction of friction and wear of titania coatings while the presence of nanoparticles has secondary effect. Investigations in this study carried out with the use of the AFM technique highlighted the potential and flexibility of sol-gel approach in designing of various types of advanced materials in a form of mesoscopic objects, porous coatings and composite layers. Results collected in this study clearly demonstrated that sol-gel technique can be applied effectively in preparation of

The effect of oxidation on physical properties of porous silicon layers for optical applications

Energy Technology Data Exchange (ETDEWEB)

Pirasteh, Parasteh [Laboratoire d' Optronique, CNRS-UMR FOTON 6082, Universite de Rennes 1, ENSSAT Tecnhopole Anticipa, 6 rue de Kerampont, BP 447, 22305 Lannion Cedex (France); Charrier, Joel [Laboratoire d' Optronique, CNRS-UMR FOTON 6082, Universite de Rennes 1, ENSSAT Tecnhopole Anticipa, 6 rue de Kerampont, BP 447, 22305 Lannion Cedex (France)]. E-mail: joel.charrier@univ-rennes1.fr; Soltani, Ali [Institut d' Electronique, de Microemectronique et de Nanotechnologie, CNRS-UMR 8520, Cite Scientifique Avenue Poincare, BP 69, 59652 Villeneuve d' Ascq Cedex (France); Haesaert, Severine [Laboratoire d' Optronique, CNRS-UMR FOTON 6082, Universite de Rennes 1, ENSSAT Tecnhopole Anticipa, 6 rue de Kerampont, BP 447, 22305 Lannion Cedex (France); Haji, Lazhar [Laboratoire d' Optronique, CNRS-UMR FOTON 6082, Universite de Rennes 1, ENSSAT Tecnhopole Anticipa, 6 rue de Kerampont, BP 447, 22305 Lannion Cedex (France); Godon, Christine [Laboratoire de Physique Crystalline, Institut des Materiaux Jean Rouxel, 44322 Nantes Cedex 3 (France); Errien, Nicolas [Laboratoire de Physique Crystalline, Institut des Materiaux Jean Rouxel, 44322 Nantes Cedex 3 (France)

2006-12-15

In order to understand the optical loss mechanisms in porous silicon based waveguides, structural and optical studies have been performed. Scanning and transmission electron microscopic observations of porous silicon layers are obtained before and after an oxidation process at high temperature in wet O{sub 2}. Pore size and shape of heavily p-type doped Si wafers are estimated and correlated to the optical properties of the material before and after oxidation. The refractive index was measured and compared to that determined by the Bruggeman model.

Formation of porous surface layers in reaction bonded silicon nitride during processing

Science.gov (United States)

Shaw, N. J.; Glasgow, T. K.

1979-01-01

Microstructural examination of reaction bonded silicon nitride (RBSN) has shown that there is often a region adjacent to the as-nitrided surfaces that is even more porous than the interior of this already quite porous material. Because this layer of large porosity is considered detrimental to both the strength and oxidation resistance of RBSN, a study was undertaken to determine if its formation could be prevented during processing. All test bars studied were made from a single batch of Si powder which was milled for 4 hours in heptane in a vibratory mill using high density alumina cylinders as the grinding media. After air drying the powder, bars were compacted in a single acting die and hydropressed.

Eggshell membrane-templated porous gold membranes using nanoparticles as building blocks

International Nuclear Information System (INIS)

Ashraf, S.; Khalid, Z. M.; Hussain, I.

2013-01-01

Highly porous gold membrane-like structures are formed using eggshell membrane, as such and heat denatured, as a template and gold nanoparticles as building blocks. Gold nanoparticles were produced in-situ on the eggshell membranes without using additional reducing agents. The morphology and loading of gold nanoparticles can easily be controlled by adjusting the pH and thus the redox potential of eggshell membranes. Lower pH favored the formation of irregularly-shaped but dense gold macro/ nanocrystals whereas higher pH(8-9) favored the formation of fairly uniform but less dense gold nanoparticles onto the eggshell membranes. Heat treatment of eggshell membrane-gold nanoparticle composites formed at pH 8-9 led to the formation of highly porous membrane like gold while mimicking the original structure of eggshell membrane. All these materials have been thoroughly characterized using field emission scanning electron microscopy (FESEM), energy dispersive X-ray spectroscopy (EDX), and inductively coupled plasma - atomic emission spectroscopy (ISP-AES). These highly porous membrane-like gold materials may have potential applications in catalysis, biosensors, electrode materials, optically selective coatings, heat dissipation and biofiltration. (author)

In-situ ellipsometric characterization of the growth of porous anisotropic nanocrystalline ZnO layers

Energy Technology Data Exchange (ETDEWEB)

Laha, P., E-mail: plaha@vub.ac.be; Terryn, H.; Ustarroz, J., E-mail: justarro@vub.ac.be [Research Group Electrochemical and Surface Engineering (SURF), Vrije Universiteit Brussel, Pleinlaan 2, 1050 Elsene, Brussels (Belgium); Nazarkin, M. Y., E-mail: mikleo@mail.ru; Gavrilov, S. A. [Department of Materials of Functional Electronics (MFE), National Research University of Electronic Technology, Bld. 5, Pas. 4806, Zelenograd, Moscow 124498 (Russian Federation); Volkova, A. V.; Simunin, M. M. [Department of Quantum Physics and Nanoelectronics (QPN), National Research University of Electronic Technology, Bld. 5, Pas. 4806, Zelenograd, Moscow 124498 (Russian Federation)

2015-03-09

ZnO films have increasingly been in the spotlight due to their largely varied electro-physical and optical properties. For several applications, porous anisotropic nanocrystalline layers are especially interesting. To study the growth kinetics of such films during different fabrication processes, a powerful non-destructive in-situ technique is required. In this work, both ex-situ and in-situ spectroscopic ellipsometry are used along with advanced modelling techniques that are able to take both the anisotropy and the porosity of the films into account. Scanning electron microscopy, along with nitrogen absorption methods for measuring porosity, validated the ellipsometric data and proposed model. The film, grown by chemical bath deposition, was monitored from around 700 to 1800 nm in thickness. This same principle can now be used to monitor any other porous and/or anisotropic structure in an effective in-situ manner, e.g., growth of porous anodic aluminium oxides, nano-porous silica films, etc.

CuGaS2 and CuGaS2–ZnS Porous Layers from Solution-Processed Nanocrystals

Directory of Open Access Journals (Sweden)

Taisiia Berestok

2018-04-01

Full Text Available The manufacturing of semiconducting films using solution-based approaches is considered a low cost alternative to vacuum-based thin film deposition strategies. An additional advantage of solution processing methods is the possibility to control the layer nano/microstructure. Here, we detail the production of mesoporous CuGaS2 (CGS and ZnS layers from spin-coating and subsequent cross-linking through chalcogen-chalcogen bonds of properly functionalized nanocrystals (NCs. We further produce NC-based porous CGS/ZnS bilayers and NC-based CGS–ZnS composite layers using the same strategy. Photoelectrochemical measurements are used to demonstrate the efficacy of porous layers, and particularly the CGS/ZnS bilayers, for improved current densities and photoresponses relative to denser films deposited from as-produced NCs.

Fabrication of porous TiO{sub 2} films using a spongy replica prepared by layer-by-layer self-assembly method: Application to dye-sensitized solar cells

Energy Technology Data Exchange (ETDEWEB)

Tsuge, Yosuke [Department of Applied Physics and Physico-informatics, Faculty of Science and Technology, Keio University, 3-14-1 Hiyoshi, Kohoku-ku, Yokohama-shi 223-8522 (Japan)]. E-mail: yotsuge@appi.keio.ac.jp; Inokuchi, Kohei [Department of Applied Physics and Physico-informatics, Faculty of Science and Technology, Keio University, 3-14-1 Hiyoshi, Kohoku-ku, Yokohama-shi 223-8522 (Japan); Onozuka, Katsuhiro [Department of Applied Physics and Physico-informatics, Faculty of Science and Technology, Keio University, 3-14-1 Hiyoshi, Kohoku-ku, Yokohama-shi 223-8522 (Japan); Shingo, Ohno [Research and Development Division, Bridgestone Corporation, 3-1-1 Ogawahigashi-cho, Kodaira-shi, Tokyo-to 187-8531 (Japan); Sugi, Shinichiro [Research and Development Division, Bridgestone Corporation, 3-1-1 Ogawahigashi-cho, Kodaira-shi, Tokyo-to 187-8531 (Japan); Yoshikawa, Masato [Research and Development Division, Bridgestone Corporation, 3-1-1 Ogawahigashi-cho, Kodaira-shi, Tokyo-to 187-8531 (Japan); Shiratori, Seimei [Department of Applied Physics and Physico-informatics, Faculty of Science and Technology, Keio University, 3-14-1 Hiyoshi, Kohoku-ku, Yokohama-shi 223-8522 (Japan)]. E-mail: shiratori@appi.keio.ac.jp

2006-03-21

In this study, we report the fabrication of the anatase TiO{sub 2} films with high porosity using a new spongy replica which prepared by layer-by-layer self-assembly technique. The scanning electron microscope photographs revealed that the spongy replica has an extremely porous microstructure and high surface area. Moreover, this porous replica was easily fabricated from a very flat film through the action with silver acetate solution. This method facilitated the porous TiO{sub 2} films with a high surface area. Additionally, by this method, a necking between the TiO{sub 2} films was strong and the amount of loaded dye was increased, so that the increase of forward electron transfer between the TiO{sub 2} films on the surface and the TiO{sub 2} films on the substrate. By using the fabricated porous TiO{sub 2} films as the photoelectrode for dye-sensitized solar cell, the improvement of the photocurrent-voltage characteristic was achieved, resulting in an energy conversion efficiency of Eff = 2.66% with the thickness of approximately 5 {mu}m.

Fabrication of luminescent porous silicon with stain etches and evidence that luminescence originates in amorphous layers

Science.gov (United States)

Fathauer, R. W.; George, T.; Ksendzov, A.; Lin, T. L.; Pike, W. T.; Vasquez, R. P.; Wu, Z.-C.

1992-01-01

Simple immersion of Si in stain etches of HF:HNO3:H2O or NaNO2 in aqueous HF was used to produce films exhibiting luminescence in the visible similar to that of anodically-etched porous Si. All of the luminescent samples consist of amorphous porous Si in at least the near surface region. No evidence was found for small crystalline regions within these amorphous layers.

Growth and characterization of molecular beam epitaxial GaAs layers on porous silicon

Science.gov (United States)

Lin, T. L.; Liu, J. K.; Sadwick, L.; Wang, K. L.; Kao, Y. C.

1987-01-01

GaAs layers have been grown on porous silicon (PS) substrates with good crystallinity by molecular beam epitaxy. In spite of the surface irregularity of PS substrates, no surface morphology deterioration was observed on epitaxial GaAs overlayers. A 10-percent Rutherford backscattering spectroscopy minimum channeling yield for GaAs-on-PS layers as compared to 16 percent for GaAs-on-Si layers grown under the same condition indicates a possible improvement of crystallinity when GaAs is grown on PS. Transmission electron microscopy reveals that the dominant defects in the GaAs-on-PS layers are microtwins and stacking faults, which originate from the GaAs/PS interface. GaAs is found to penetrate into the PS layers. n-type GaAs/p-type PS heterojunction diodes were fabricated with good rectifying characteristics.

Effect of aging treatment on the in vitro nickel release from porous oxide layers on NiTi

Energy Technology Data Exchange (ETDEWEB)

Huan, Z.; Fratila-Apachitei, L.E., E-mail: e.l.fratila-apachitei@tudelft.nl; Apachitei, I.; Duszczyk, J.

2013-06-01

Despite the ability of creating porous oxide layers on nickel–titanium alloy (NiTi) surface for biofunctionalization, the use of plasma electrolytic oxidation (PEO) has raised concerns over the possible increased levels of Ni release. Therefore, the primary aim of this study was to investigate the effect of aging in boiling water on Ni release from porous NiTi surfaces that have been formed by the PEO process. Based on different oxidation conditions, e.g. electrolyte composition and electrical parameters, three kinds of oxide layers with various characteristics were prepared on NiTi substrate. The process was followed by aging in boiling water for different durations. The Ni release was assessed by immersion tests in phosphate buffer saline and the Ni concentration was measured using the flame atomic absorption spectrometry. The results showed that aging in boiling water can significantly reduce the Ni release from oxidized porous samples, given that the duration of the treatment is finely adjusted according to the parameters of the as-formed oxide layer. Surface examination of the samples before and after aging in boiling water suggested that such a treatment is non-destructive while improving the corrosion resistance of oxidized samples, as evidenced by potentiodynamic polarization tests. The results of this study indicate that water boiling may be a suitable post-treatment required to minimize Ni release from porous oxides produced on NiTi by PEO for biomedical applications.

Improvement in photovoltaic properties of silicon solar cells with a doped porous silicon layer with rare earth (Ce, La) as antireflection coatings

International Nuclear Information System (INIS)

Atyaoui, Malek; Dimassi, Wissem; Atyaoui, Atef; Elyagoubi, Jalel; Ouertani, Rachid; Ezzaouia, Hatem

2013-01-01

The performance improvement of solar cells due to the formation of a porous silicon layer treated with rare earth (Ce, La) in the n + emitter of silicon n + /p junctions has been investigated. The photovoltaic properties of the cells with and without treatment of the porous silicon layer are compared. From the reflection measurements, it was shown that the cells with treated PS layers have lower reflectivity value compared to cell with untreated PS layer. The main result is that the photovoltaic energy conversion efficiency of solar cells can be enhanced by using the treated porous silicon layers with the rare earth (Ce, La) as anti-reflection coatings. -- Highlights: • The reduction of optical loss in silicon (c-Si) solar cells attracts the attention of many researches to achieve high efficiencies. • To attain this aim, the treated PS layers with rare earth (La, Ce) are suggested to be used as an (ARC) of c-Si solar cell. • The result showed a decrease in the optical losses which can explain the improved photovoltaic properties

Improvement in photovoltaic properties of silicon solar cells with a doped porous silicon layer with rare earth (Ce, La) as antireflection coatings

Energy Technology Data Exchange (ETDEWEB)

Atyaoui, Malek, E-mail: atyaoui.malek@yahoo.fr [Laboratoire de Photovoltaïque, Centre de recherches et des technologies de l' energie, technopole de Borj-Cédria, PB:95, Hammam Lif 2050 (Tunisia); Dimassi, Wissem [Laboratoire de Photovoltaïque, Centre de recherches et des technologies de l' energie, technopole de Borj-Cédria, PB:95,Hammam Lif 2050 (Tunisia); Atyaoui, Atef [Laboratoire de traitement des eaux usées, Centre de recherches et des technologies des eaux, technopole de Borj-Cédria, PB: 273, Soliman 8020 (Tunisia); Elyagoubi, Jalel; Ouertani, Rachid; Ezzaouia, Hatem [Laboratoire de Photovoltaïque, Centre de recherches et des technologies de l' energie, technopole de Borj-Cédria, PB:95,Hammam Lif 2050 (Tunisia)

2013-09-15

The performance improvement of solar cells due to the formation of a porous silicon layer treated with rare earth (Ce, La) in the n{sup +} emitter of silicon n{sup +}/p junctions has been investigated. The photovoltaic properties of the cells with and without treatment of the porous silicon layer are compared. From the reflection measurements, it was shown that the cells with treated PS layers have lower reflectivity value compared to cell with untreated PS layer. The main result is that the photovoltaic energy conversion efficiency of solar cells can be enhanced by using the treated porous silicon layers with the rare earth (Ce, La) as anti-reflection coatings. -- Highlights: • The reduction of optical loss in silicon (c-Si) solar cells attracts the attention of many researches to achieve high efficiencies. • To attain this aim, the treated PS layers with rare earth (La, Ce) are suggested to be used as an (ARC) of c-Si solar cell. • The result showed a decrease in the optical losses which can explain the improved photovoltaic properties.

Characterization of Ag-porous silicon nanostructured layer formed by an electrochemical etching of p-type silicon surface for bio-application

Science.gov (United States)

Naddaf, M.; Al-Mariri, A.; Haj-Mhmoud, N.

2017-06-01

Nanostructured layers composed of silver-porous silicon (Ag-PS) have been formed by an electrochemical etching of p-type (1 1 1) silicon substrate in a AgNO3:HF:C2H5OH solution at different etching times (10 min-30 min). Scanning electron microscopy (SEM) and energy-dispersive x-ray spectroscopy (EDS) results reveal that the produced layers consist of Ag dendrites and a silicon-rich porous structure. The nanostructuring nature of the layer has been confirmed by spatial micro-Raman scattering and x-ray diffraction techniques. The Ag dendrites exhibit a surface-enhanced Raman scattering (SERS) spectrum, while the porous structure shows a typical PS Raman spectrum. Upon increasing the etching time, the average size of silicon nanocrystallite in the PS network decreases, while the average size of Ag nanocrystals is slightly affected. In addition, the immobilization of prokaryote Salmonella typhimurium DNA via physical adsorption onto the Ag-PS layer has been performed to demonstrate its efficiency as a platform for detection of biological molecules using SERS.

Torsional surface waves in an inhomogeneous layer over a gravitating anisotropic porous half-space

International Nuclear Information System (INIS)

Gupta, Shishir; Pramanik, Abhijit

2015-01-01

The present work aims to deal with the propagation of torsional surface wave in an inhomogeneous layer over a gravitating anisotropic porous half space. The inhomogeneous layer exhibits the inhomogeneity of quadratic type. In order to show the effect of gravity the equation for the velocity of torsional wave has been obtained. It is also observed that for a layer over a homogeneous half space without gravity, the torsional surface wave does not propagate. An attempt is also made to assess the possible propagation of torsional surface waves in that medium in the absence of the upper layer. The effects of inhomogeneity factors and porosity on the phase velocity are depicted by means of graphs. (paper)

Formation and properties of the buried isolating silicon-dioxide layer in double-layer “porous silicon-on-insulator” structures

Energy Technology Data Exchange (ETDEWEB)

Bolotov, V. V.; Knyazev, E. V.; Ponomareva, I. V.; Kan, V. E., E-mail: kan@obisp.oscsbras.ru; Davletkildeev, N. A.; Ivlev, K. E.; Roslikov, V. E. [Russian Academy of Sciences, Omsk Scientific Center, Siberian Branch (Russian Federation)

2017-01-15

The oxidation of mesoporous silicon in a double-layer “macroporous silicon–mesoporous silicon” structure is studied. The morphology and dielectric properties of the buried insulating layer are investigated using electron microscopy, ellipsometry, and electrical measurements. Specific defects (so-called spikes) are revealed between the oxidized macropore walls in macroporous silicon and the oxidation crossing fronts in mesoporous silicon. It is found that, at an initial porosity of mesoporous silicon of 60%, three-stage thermal oxidation leads to the formation of buried silicon-dioxide layers with an electric-field breakdown strength of E{sub br} ~ 10{sup 4}–10{sup 5} V/cm. Multilayered “porous silicon-on-insulator” structures are shown to be promising for integrated chemical micro- and nanosensors.

Porous Hydrogen-Bonded Organic Frameworks

Directory of Open Access Journals (Sweden)

Yi-Fei Han

2017-02-01

Full Text Available Ordered porous solid-state architectures constructed via non-covalent supramolecular self-assembly have attracted increasing interest due to their unique advantages and potential applications. Porous metal-coordination organic frameworks (MOFs are generated by the assembly of metal coordination centers and organic linkers. Compared to MOFs, porous hydrogen-bonded organic frameworks (HOFs are readily purified and recovered via simple recrystallization. However, due to lacking of sufficiently ability to orientate self-aggregation of building motifs in predictable manners, rational design and preparation of porous HOFs are still challenging. Herein, we summarize recent developments about porous HOFs and attempt to gain deeper insights into the design strategies of basic building motifs.

Computer-Aided Process Planning for the Layered Fabrication of Porous Scaffold Matrices

Science.gov (United States)

Starly, Binil

Rapid Prototyping (RP) technology promises to have a tremendous impact on the design and fabrication of porous tissue replacement structures for applications in tissue engineering and regenerative medicine. The layer-by-layer fabrication technology enables the design of patient-specific medical implants and complex structures for diseased tissue replacement strategies. Combined with advancements in imaging modalities and bio-modeling software, physicians can engage themselves in advanced solutions for craniofacial and mandibular reconstruction. For example, prior to the advancement of RP technologies, solid titanium parts used as implants for mandibular reconstruction were fashioned out of molding or CNC-based machining processes (Fig. 3.1). Titanium implants built using this process are often heavy, leading to increased patient discomfort. In addition, the Young's modulus of titanium is almost five times that of healthy cortical bone resulting in stress shielding effects [1,2]. With the advent of CAD/CAM-based tools, the virtual reconstruction of the implants has resulted in significant design improvements. The new generation of implants can be porous, enabling the in-growth of healthy bone tissue for additional implant fixation and stabilization. Newer implants would conform to the external shape of the defect site that is intended to be filled in. More importantly, the effective elastic modulus of the implant can be designed to match that of surrounding tissue. Ideally, the weight of the implant can be designed to equal the weight of the tissue that is being replaced resulting in increased patient comfort. Currently, such porous structures for reconstruction can only be fabricated using RP-based metal fabrication technologies such as Electron Beam Melting (EBM), Selective Laser Sintering (SLS®), and 3D™ Printing processes.

Positron annihilation lifetime spectroscopy (PALS) application in metal barrier layer integrity for porous low- k materials

CERN Document Server

Simon, Lin; Gidley, D W; Wetzel, J T; Monnig, K A; Ryan, E T; Simon, Jang; Douglas, Yu; Liang, M S; En, W G; Jones, E C; Sturm, J C; Chan, M J; Tiwari, S C; Hirose, M

2002-01-01

Positron Annihilation Lifetime Spectroscopy (PALS) is a useful tool to pre-screen metal barrier integrity for Si-based porous low-k dielectrics. Pore size of low-k, thickness of metal barrier Ta, positronium (Ps) leakage from PALS, trench sidewall morphology, electrical test from one level metal (1LM) pattern wafer and Cu diffusion analysis were all correlated. Macro-porous low-k (pore size >=200 AA) and large scale meso-porous low-k (>50~200 AA) encounter both Ps leakage and Cu diffusion into low-k dielectric in the 0.25 mu mL/0.3 mu mS structures when using SEMATECH in-house PVD Ta 250 AA as barrier layer. For small scale meso-porous (>20~50 AA) and micro- porous (<=20 AA) low-k, no Ps leakage and no Cu diffusion into low-k were observed even with PVD Ta 50 AA, which is proved also owing to sidewall densification to seal all sidewall pores due to plasma etch and ash. For future technology, smaller pore size of porous Si-based low-k (=<50 AA) will be preferential for dense low-k like trench sidewall to...

Control of flow around a circular cylinder wrapped with a porous layer by magnetohydrodynamic

Energy Technology Data Exchange (ETDEWEB)

Bovand, M. [Department of Mechanical Engineering, Semnan Branch, Islamic Azad University, Semnan (Iran, Islamic Republic of); Rashidi, S. [Department of Mechanical Engineering, Ferdowsi University of Mashhad, Mashhad 91775-1111 (Iran, Islamic Republic of); Esfahani, J.A., E-mail: abolfazl@um.ac.ir [Department of Mechanical Engineering, Ferdowsi University of Mashhad, Mashhad 91775-1111 (Iran, Islamic Republic of); Saha, S.C.; Gu, Y.T. [School of Chemistry, Physics and Mechanical Engineering, Queensland University of Technology, GPO Box 2434, Brisbane, QLD 4001 (Australia); Dehesht, M. [School of Mechanical Engineering, Semnan University, P.O. Box 35196-45399, Semnan (Iran, Islamic Republic of)

2016-03-01

The present study focuses on the analysis of two-dimensional Magnetohydrodynamic (MHD) flow past a circular cylinder wrapped with a porous layer in different laminar flow regimes. The Darcy-Brinkman-Forchheimer model has been used for simulating flow in porous medium using finite volume based software, Fluent 6.3. In order to analyze the MHD flow, the mean and instantaneous drag and lift coefficients and stream patterns are computed to elucidate the role of Stuart number, N and Darcy number, Da. It is revealed that the magnetic fields are capable to stabilize flow and suppress the vortex shedding of vortices. The N-Re plane shows the curves for separating steady and periodic flow regimes, N{sub cr} and disappearing of vortex, N{sub diss}. For validate the solution, the obtained C{sub D} and St are compared with available results of literature. - Highlights: • The value of interaction parameter, N{sub cr}, depends on the Reynolds number. • N{sub cr} for porous-wrapped solid cylinder is less than the value of solid cylinder. • The St number of porous-wrapped cylinder is less than that of the rigid one. • When Da is decreased, St also decreases.

Experimental investigation on the evaporation of a wet porous layer inside a vertical channel with resolution of the heat equation by inverse method

International Nuclear Information System (INIS)

Terzi, A.; Foudhil, W.; Harmand, S.; Ben Jabrallah, S.

2016-01-01

Highlights: • Experimental study of the evaporation of a wet porous layer inside a vertical channel. • Resolution of the heat equation by inverse method. • The use of the porous layer is more efficient for high heating flux and low liquid inlet flow. • To improve the evaporation, the system must operate at low water inlet flow. - Abstract: In this paper, we realize an Experimental study of the evaporation of a wet porous layer inside a vertical channel. To develop this study, an experimental dispositive was realised. We measure the temperature along the plate and the evaporated flow rate using the test bed. From these measurements we note that the profiles of the temperature are divided into two areas: the heating and the evaporation zone. We also note that the use of the porous layer is more efficient for high heating flux and low liquid inlet flow. In addition, we studied different dimensionless numbers by solving the energy equation by inverse method. We note that the latent Nusselt number is more important than the sensible Nusselt Number, which proves that the flow dissipated by evaporation is greater than the one used by the film to increase its temperature.

Layer-by-layer strippable Ag multilayer films fabricated by modular assembly.

Science.gov (United States)

Li, Yan; Chen, Xiaoyan; Li, Qianqian; Song, Kai; Wang, Shihui; Chen, Xiaoyan; Zhang, Kai; Fu, Yu; Jiao, Yong-Hua; Sun, Ting; Liu, Fu-Chun; Han, En-Hou

2014-01-21

We have developed a new method to fabricate multilayer films, which uses prepared thin films as modular blocks and transfer as operation mode to build up multilayer structures. In order to distinguish it from the in situ fabrication manner, this method is called modular assembly in this study. On the basis of such concept, we have fabricated a multilayer film using the silver mirror film as the modular block and poly(lactic acid) as the transfer tool. Due to the special double-layer structure of the silver mirror film, the resulting multilayer film had a well-defined stratified architecture with alternate porous/compact layers. As a consequence of the distinct structure, the interaction between the adjacent layers was so weak that the multilayer film could be layer-by-layer stripped. In addition, the top layer in the film could provide an effective protection on the morphology and surface property of the underlying layers. This suggests that if the surface of the film was deteriorated, the top layer could be peeled off and the freshly exposed surface would still maintain the original function. The successful preparation of the layer-by-layer strippable silver multilayer demonstrates that modular assembly is a feasible and effective method to build up multilayer films capable of creating novel and attractive micro/nanostructures, having great potential in the fabrication of nanodevices and coatings.

Surface protection treatments of highly porous building stones and sustainability problems

Science.gov (United States)

Calia, Angela; Lettieri, Maria Teresa; Matera, Loredana; Sileo, Maria

2013-04-01

The growing attention to the cultural value and the potential touristic attraction of the historic towns has led to increasing activities of rehabilitation and conservation of the historical built heritage. Chemical treatments have become a common practice for the protection of the stone building surface against the decay agents and traditional methods of protection, such as the application of sacrificial layers, have been even more neglected. The use of chemical products on large scale works on the historical built heritage draws the attention towards the sustainability of the conservation treatments, that involve peculiar features with relation to the different types of stones. Sustainability is undoubtedly in terms of human and environmental impact of the used products, so that the use of new formulations based on aqueous solvent should be preferred. Sustainability also means the equilibrium between the required performances of the treatments and the preservation of the original stone properties (colour, permeability, etc), namely harmlessness and effectiveness of the treatments. This can be a critical aspect when we deal with very porous stones, namely having porosity between 30-40%, that are widely used in many countries as traditional building materials. In most cases no information - or very general recommendations - is reported in the technical sheets of the conservation products with reference to the application to these types of stones. Relevant problems of compatibility can arise from the significant amounts absorbed by the high porous structure, as well as in terms of cost effectiveness of the treatments. In this work several calcarenites with different petro-physic characteristics and porosity between 30 and 45% are concerned for the assessment of the performance of two commercial water based products for stone protection, respectively an alcoxy-siloxane with low molecular weight and a modified organo-silane. This activity is a part of the Apulia

Blistering in a porous surface layer of materials. [He ion implantation

Energy Technology Data Exchange (ETDEWEB)

Afrikanov, I.N.; Vladimirov, B.G.; Guseva, M.I.; Ivanov, S.M.; Martynenko, Yu.V.; Nikol' skij, Yu.V.; Ryazanov, A.I.

1981-03-01

The effect of porous structure on the nature and rate of radiation erosion during implantation of helium ions into nickel and the OKh15N15M3B stainless steel is studied. The investigation results showed sharp dependence of the erosion rate due to blistering on the dimension and density of pores in the by-surface layer. The rate of the surface erosion increased in one order as compared with the control specimens without pores at 1% swelling for stainless steel and 4% for nickel.

Analysis of chemical dissolution of the barrier layer of porous oxide on aluminum thin films using a re-anodizing technique

Energy Technology Data Exchange (ETDEWEB)

Vrublevsky, I. [Department of Microelectronics, Belarusian State University of Informatics and Radioelectronics, 6 Brovka street, Minsk 220013 (Belarus)]. E-mail: nil-4-2@bsuir.edu.by; Parkoun, V. [Department of Microelectronics, Belarusian State University of Informatics and Radioelectronics, 6 Brovka street, Minsk 220013 (Belarus); Sokol, V. [Department of Microelectronics, Belarusian State University of Informatics and Radioelectronics, 6 Brovka street, Minsk 220013 (Belarus); Schreckenbach, J. [Institut fuer Chemie, Technische Universitaet Chemnitz, Chemnitz D-09107 (Germany)

2005-09-30

Chemical dissolution of the barrier layer of porous oxide formed on thin aluminum films (99.9% purity) in the 4% oxalic acid after immersion in 2 mol dm{sup -3} sulphuric acid at 50 deg. C has been studied. The barrier layer thickness before and after dissolution was calculated using a re-anodizing technique. It has been shown that above 57 V the change in the growth mechanism of porous alumina films takes place. As a result, the change in the amount of regions in the barrier oxide with different dissolution rates is observed. The barrier oxide contains two layers at 50 V: the outer layer with the highest dissolution rate and the inner layer with a low dissolution rate. Above 60 V the barrier oxide contains three layers: the outer layer with a high dissolution rate, the middle layer with the highest dissolution rate and the inner layer with a low dissolution rate. We suggest that the formation of the outer layer of barrier oxide with a high dissolution rate is linked with the injection of protons or H{sub 3}O{sup +} ions from the electrolyte into the oxide film at the anodizing voltages above 57 V.

Atmospheric methane removal by methane-oxidizing bacteria immobilized on porous building materials.

Science.gov (United States)

Ganendra, Giovanni; De Muynck, Willem; Ho, Adrian; Hoefman, Sven; De Vos, Paul; Boeckx, Pascal; Boon, Nico

2014-04-01

Biological treatment using methane-oxidizing bacteria (MOB) immobilized on six porous carrier materials have been used to mitigate methane emission. Experiments were performed with different MOB inoculated in building materials at high (~20 % (v/v)) and low (~100 ppmv) methane mixing ratios. Methylocystis parvus in autoclaved aerated concrete (AAC) exhibited the highest methane removal rate at high (28.5 ± 3.8 μg CH₄ g⁻¹ building material h⁻¹) and low (1.7 ± 0.4 μg CH₄ g⁻¹ building material h⁻¹) methane mixing ratio. Due to the higher volume of pores with diameter >5 μm compared to other materials tested, AAC was able to adsorb more bacteria which might explain for the higher methane removal observed. The total methane and carbon dioxide-carbon in the headspace was decreased for 65.2 ± 10.9 % when M. parvus in Ytong was incubated for 100 h. This study showed that immobilized MOB on building materials could be used to remove methane from the air and also act as carbon sink.

Photocatalytic activity of porous multiwalled carbon nanotube-TiO{sub 2} composite layers for pollutant degradation

Energy Technology Data Exchange (ETDEWEB)

Zouzelka, Radek [J. Heyrovsky Institute of Physical Chemistry, v.i.i., Academy of Sciences of the Czech Republic, Dolejskova 3, 18223 Prague 8 (Czech Republic); Department of Physical Chemistry, University of Chemistry and Technology Prague, 16628 Prague (Czech Republic); Kusumawati, Yuly [Chimie ParisTech, PSL Research University, CNRS, Institut de Recherche de Chimie Paris (IRCP), 11 rue Pierre et Marie Curie, 75005 Paris (France); Remzova, Monika [J. Heyrovsky Institute of Physical Chemistry, v.i.i., Academy of Sciences of the Czech Republic, Dolejskova 3, 18223 Prague 8 (Czech Republic); Department of Physical Chemistry, University of Chemistry and Technology Prague, 16628 Prague (Czech Republic); Rathousky, Jiri [J. Heyrovsky Institute of Physical Chemistry, v.i.i., Academy of Sciences of the Czech Republic, Dolejskova 3, 18223 Prague 8 (Czech Republic); Pauporté, Thierry, E-mail: thierry.pauporte@chimie-paristech.fr [Chimie ParisTech, PSL Research University, CNRS, Institut de Recherche de Chimie Paris (IRCP), 11 rue Pierre et Marie Curie, 75005 Paris (France)

2016-11-05

Highlights: • A simple method for TiO{sub 2}/graphene nanocomposite layer preparation. • Stable coatings on glass substrate. • Mesoporous nanocomposite films with high internal surface area. • High photoactivity for 4-chlorophenol degradation. • Analysis of photocatalysis enhancement mechanism. - Abstract: TiO{sub 2} nanoparticles are suitable building blocks nanostructures for the synthesis of porous functional thin films. Here we report the preparation of films using brookite, P25 titania and anatase pristine nanoparticles and of nanocomposite layers combining anatase nanoparticles and multi-walled carbon nanotube (MWCNT) at various concentrations. The structure and phase composition of the layers were characterized by X-ray diffraction and Raman spectroscopy. Their morphology and texture properties were determined by scanning electron microscopy and krypton adsorption experiments, respectively. Additionally to a strong absorption in the UV range, the composites exhibited light absorption in the visible range as well. The photocatalytic performance of the layers was tested in the degradation of aqueous solutions of 4-chlorophenol serving as a model of an eco-persistent pollutant. Besides the determination of the decrease in the concentration of 4-chlorophenol, also the formation of intermediate degradation products, namely hydroquinone and benzoquinone, was followed. The presence of MWCNTs had a beneficial effect on the photocatalytic performance, a marked increase in the photocatalytic degradation rate constant being observed even at very low concentrations of MWCNTs. Compared to a P25 reference layer, the first order rate reaction constant increased by about 100% for the composite films containing MWCNTs at concentrations above 0.6 wt%. The key parameters for the enhancement of the photocatalytic performance are discussed. The presence of carbon nanotubes influences beneficially the degradation of 4-chlorophenol by an attack of the primarily

Porous germanium multilayers

Energy Technology Data Exchange (ETDEWEB)

Garralaga Rojas, Enrique; Hensen, Jan; Brendel, Rolf [Institut fuer Solarenergieforschung Hameln (ISFH), Emmerthal (Germany); Carstensen, Juergen; Foell, Helmut [Chair for General Materials Science, Faculty of Engineering, Christian-Albrechts-University of Kiel (Germany)

2011-06-15

We present the reproducible fabrication of porous germanium (PGe) single- and multilayers. Mesoporous layers form on heavily doped 4'' p-type Ge wafers by electrochemical etching in highly concentrated HF-based electrolytes with concentrations in a range of 30-50 wt.%. Direct PGe formation is accompanied by a constant dissolution of the already-formed porous layer at the electrolyte/PGe interface, hence yielding a thinner substrate after etching. This effect inhibits multilayer formation as the starting layer is etched while forming the second layer. We avoid dissolution of the porous layer by alternating the etching bias from anodic to cathodic. PGe formation occurs during anodic etching whereas the cathodic step passivates pore walls with H-atoms and avoids electropolishing. The passivation lasts a limited time depending on the etching current density and electrolyte concentration, necessitating a repetition of the cathodic step at suitable intervals. With optimized alternating bias mesoporous multilayer production is possible. We control the porosity of each single layer by varying the etching current density and the electrolyte (copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Laser-Induced Breakdown Spectroscopy (LIBS) for Monitoring the Formation of Hydroxyapatite Porous Layers

OpenAIRE

Sola, Daniel; Paulés, Daniel; Grima, Lorena; Anzano, Jesús

2017-01-01

Laser-induced breakdown spectroscopy (LIBS) is applied to characterize the formation of porous hydroxyapatite layers on the surface of 0.8CaSiO3-0.2Ca3(PO4)2 biocompatible eutectic glass immersed in simulated body fluid (SBF). Compositional and structural characterization analyses were also conducted by field emission scanning electron microscopy (FESEM), energy dispersive X-ray spectroscopy (EDX), and micro-Raman spectroscopy.

The formation and evolution of layered structures in porous media: effects of porosity and mechanical dispersion

NARCIS (Netherlands)

Schoofs, Stan; Trompert, Ron A.; Hansen, Ulrich

1999-01-01

Horizontally layered structures can develop in porous or partially molten environments, such as hydrothermal systems, magmatic intrusions and the early Earth's mantle. The porosity f of these natural environments is typically small. Since dissolved chemical elements unlike heat cannot diffuse

Preparation and Lithium-Storage Performance of a Novel Hierarchical Porous Carbon from Sucrose Using Mg-Al Layered Double Hydroxides as Template

International Nuclear Information System (INIS)

Shi, Liluo; Chen, Yaxin; Song, Huaihe; Li, Ang; Chen, Xiaohong; Zhou, Jisheng; Ma, Zhaokun

2017-01-01

Highlights: • A new hierarchical porous carbon containing slit-shaped mesopores and 3D carbon nanosheets were prepared using Mg-Al layered double hydroxides as template. • The hierarchical porous carbon electrode showed a high capacity and excellent cycle stability when used in lithium-ion battery. • The excellent performance is ascribed to its hierarchical porous structure, especially the mesoporous struture. - Abstract: Novel hierarchical porous carbons (NHPCs) containing 3D carbon nanosheets and slit-mesopores are prepared in this work, using MgAl-layered double hydroxides as template and sucrose as carbon source, and their electrochemical performances as anodes of lithium-ion batteries are also investigated. Owing to the existence of abundant carbon nanosheets and slit-mesopores, the NHPCs electrode exhibits the specific reversible capacity of 1151.9 mA h/g at the current density of 50 mA/g, which is significantly higher than other hierarchical porous carbons reported in previous literatures. The contributions of carbon nanosheets and mesopores to the electrochemical performance are further clarified by nitrogen adsorption-desorption test, electrochemical impedance spectroscopy, cyclic voltammograms and galvanostatic charge/discharge test. This work not only provides an easy and effective method to prepare hierarchical porous carbon materials, but also is beneficial for the design of high-performance anode materials for lithium ion batteries.

Film condensation on a porous vertical surface in a porous media

International Nuclear Information System (INIS)

Ebinuma, C.D.; Liu, C.Y.; Ismail, K.A.R.

1983-01-01

The problem of dry saturated steam film condensation by natural convection on a porous surface in a porous medium is presented. Through the classical Darcy law for flow in porous medium and the approximations considered in the Boundary layer theory, it is shown that the analytical solution exists only when the normal velocity to the porous wall is inversly proportional to the square root of the distance along the plate. (E.G.) [pt

Ultrafast triggered transient energy storage by atomic layer deposition into porous silicon for integrated transient electronics

Science.gov (United States)

Douglas, Anna; Muralidharan, Nitin; Carter, Rachel; Share, Keith; Pint, Cary L.

2016-03-01

Here we demonstrate the first on-chip silicon-integrated rechargeable transient power source based on atomic layer deposition (ALD) coating of vanadium oxide (VOx) into porous silicon. A stable specific capacitance above 20 F g-1 is achieved until the device is triggered with alkaline solutions. Due to the rational design of the active VOx coating enabled by ALD, transience occurs through a rapid disabling step that occurs within seconds, followed by full dissolution of all active materials within 30 minutes of the initial trigger. This work demonstrates how engineered materials for energy storage can provide a basis for next-generation transient systems and highlights porous silicon as a versatile scaffold to integrate transient energy storage into transient electronics.Here we demonstrate the first on-chip silicon-integrated rechargeable transient power source based on atomic layer deposition (ALD) coating of vanadium oxide (VOx) into porous silicon. A stable specific capacitance above 20 F g-1 is achieved until the device is triggered with alkaline solutions. Due to the rational design of the active VOx coating enabled by ALD, transience occurs through a rapid disabling step that occurs within seconds, followed by full dissolution of all active materials within 30 minutes of the initial trigger. This work demonstrates how engineered materials for energy storage can provide a basis for next-generation transient systems and highlights porous silicon as a versatile scaffold to integrate transient energy storage into transient electronics. Electronic supplementary information (ESI) available: (i) Experimental details for ALD and material fabrication, ellipsometry film thickness, preparation of gel electrolyte and separator, details for electrochemical measurements, HRTEM image of VOx coated porous silicon, Raman spectroscopy for VOx as-deposited as well as annealed in air for 1 hour at 450 °C, SEM and transient behavior dissolution tests of uniformly coated VOx on

Hierarchical Co-based Porous Layered Double Hydroxide Arrays Derived via Alkali Etching for High-performance Supercapacitors

Science.gov (United States)

Abushrenta, Nasser; Wu, Xiaochao; Wang, Junnan; Liu, Junfeng; Sun, Xiaoming

2015-08-01

Hierarchical nanoarchitecture and porous structure can both provide advantages for improving the electrochemical performance in energy storage electrodes. Here we report a novel strategy to synthesize new electrode materials, hierarchical Co-based porous layered double hydroxide (PLDH) arrays derived via alkali etching from Co(OH)2@CoAl LDH nanoarrays. This structure not only has the benefits of hierarchical nanoarrays including short ion diffusion path and good charge transport, but also possesses a large contact surface area owing to its porous structure which lead to a high specific capacitance (23.75 F cm-2 or 1734 F g-1 at 5 mA cm-2) and excellent cycling performance (over 85% after 5000 cycles). The enhanced electrode material is a promising candidate for supercapacitors in future application.

Effect of radiation on the laminar convective heat transfer through a layer of highly porous medium

International Nuclear Information System (INIS)

Lee, K.; Howell, J.R.

1986-01-01

A numerical investigation is reported of the coupled forced convective and radiative transfer through a highly porous medium. The porosity range investigated is high enough that the fluid inertia terms in the momentum equation cannot be neglected; i.e., the simple form of Darcy's law is invalid. The geometry studied is a plane layer of highly porous medium resting on one impermeable boundary and exposed to a two-dimensional laminar external flow field. The objective is to determine the effective overall heat transfer coefficients for such a geometry. The results are applicable to diverse situations, including insulation batts exposed to external flow, the heat loss and drying rates of grain fields and forest areas, and the drying of beds of porous material exposed to convective and radiative heating

Structural, optical and electrical properties of quasi-monocrystalline silicon thin films obtained by rapid thermal annealing of porous silicon layers

International Nuclear Information System (INIS)

Hajji, M.; Khardani, M.; Khedher, N.; Rahmouni, H.; Bessais, B.; Ezzaouia, H.; Bouchriha, H.

2006-01-01

Quasi-mono-crystalline silicon (QMS) layers have a top surface like crystalline silicon with small voids in the body. Such layers are reported to have a higher absorption coefficient than crystalline silicon at the interesting range of the solar spectrum for photovoltaic application. In this work we present a study of the structural, optical and electrical properties of quasimonocrystalline silicon thin films. Quasimonocrystalline silicon thin films were obtained from porous silicon, which has been annealed at a temperature ranging from 950 to 1050 deg. C under H 2 atmosphere for different annealing durations. The porous layers were prepared by conventional electrochemical anodization using a double tank cell and a HF / Ethanol electrolyte. Porous silicon is formed on highly doped p + -type silicon substrates that enable us to prevent back contacts for the anodization. Atomic Force Microscope (AFM) was used to study the morphological quality of the prepared layers. Optical properties were extracted from transmission and reflectivity spectra. Dark I-V characteristics were used to determine the electrical conductivity of quasimonocrystalline silicon thin films. Results show an important improvement of the absorption coefficient of the material and electrical conductivity reaches a value of twenty orders higher than that of starting mesoporous silicon

On the Onset of Thermal Convection in a Layer of Oldroydian Visco-Elastic Fluid Saturated by Brinkman–Darcy Porous Medium

Directory of Open Access Journals (Sweden)

Chand Ramesh

2015-12-01

Full Text Available Thermal instability in a horizontal layer of Oldroydian visco-elastic fluid in a porous medium is investigated. For porous medium the Brinkman–Darcy model is considered. A linear stability analysis based upon perturbation method and normal mode technique is used to find solution of the fluid layer confined between two free-free boundaries. The onset criterion for stationary and oscillatory convection is derived analytically. The influence of the Brinkman–Darcy, Prandtl–Darcy number, stress relaxation parameter on the stationary and oscillatory convection is studied both analytically and graphically. The sufficient condition for the validity of PES has also been derived.

Laser-Induced Breakdown Spectroscopy (LIBS for Monitoring the Formation of Hydroxyapatite Porous Layers

Directory of Open Access Journals (Sweden)

Daniel Sola

2017-12-01

Full Text Available Laser-induced breakdown spectroscopy (LIBS is applied to characterize the formation of porous hydroxyapatite layers on the surface of 0.8CaSiO3-0.2Ca3(PO42 biocompatible eutectic glass immersed in simulated body fluid (SBF. Compositional and structural characterization analyses were also conducted by field emission scanning electron microscopy (FESEM, energy dispersive X-ray spectroscopy (EDX, and micro-Raman spectroscopy.

Biodegradable polymer for sealing porous PEO layer on pure magnesium: An in vitro degradation study

International Nuclear Information System (INIS)

Alabbasi, Alyaa; Mehjabeen, Afrin; Kannan, M. Bobby; Ye, Qingsong; Blawert, Carsten

2014-01-01

Graphical abstract: - Highlights: • Poly(L-lactide) was used to seal the porous PEO layer on Mg. • The dual-layer coating improved the in vitro degradation resistance of Mg. • Localized degradation was inhibited in the dual-layer coated Mg. - Abstract: An attempt was made to seal the porous silicate-based plasma electrolytic oxidation (PEO) layer on pure magnesium (Mg) with a biodegradable polymer, poly(L-lactide) (PLLA), to delay the localized degradation of magnesium-based implants in body fluid for better in-service mechanical integrity. Firstly, a silicate-based PEO coating on pure magnesium was performed using a pulsed constant current method. In order to seal the pores in the PEO layer, PLLA was coated using a two-step spin coating method. The performance of the PEO–PLLA Mg was evaluated using electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization. The EIS results showed that the polarization resistance (R p ) of the PEO–PLLA Mg was close to two orders of magnitude higher than that of the PEO Mg. While the corrosion current density (i corr ) of the pure Mg was reduced by 65% with the PEO coating, the PEO–PLLA coating reduced the i corr by almost 100%. As expected, the R p of the PEO–PLLA Mg decreased with increase in exposure time. However, it was noted that the R p of the PEO–PLLA Mg even after 100 h was six times higher than that of the PEO Mg after 48 h exposure, and did not show any visible localized attack

Biodegradable polymer for sealing porous PEO layer on pure magnesium: An in vitro degradation study

Energy Technology Data Exchange (ETDEWEB)

Alabbasi, Alyaa; Mehjabeen, Afrin [Biomaterials and Engineering Materials (BEM) Laboratory, James Cook University, Townsville 4811, Queensland (Australia); Kannan, M. Bobby, E-mail: bobby.mathan@jcu.edu.au [Biomaterials and Engineering Materials (BEM) Laboratory, James Cook University, Townsville 4811, Queensland (Australia); Ye, Qingsong [Discipline of Dentistry, James Cook University, Townsville 4811, Queensland (Australia); Blawert, Carsten [Magnesium Innovation Centre, Institute of Materials Research, Helmholtz-Zentrum Geesthacht, Geesthacht 21502 (Germany)

2014-05-01

Graphical abstract: - Highlights: • Poly(L-lactide) was used to seal the porous PEO layer on Mg. • The dual-layer coating improved the in vitro degradation resistance of Mg. • Localized degradation was inhibited in the dual-layer coated Mg. - Abstract: An attempt was made to seal the porous silicate-based plasma electrolytic oxidation (PEO) layer on pure magnesium (Mg) with a biodegradable polymer, poly(L-lactide) (PLLA), to delay the localized degradation of magnesium-based implants in body fluid for better in-service mechanical integrity. Firstly, a silicate-based PEO coating on pure magnesium was performed using a pulsed constant current method. In order to seal the pores in the PEO layer, PLLA was coated using a two-step spin coating method. The performance of the PEO–PLLA Mg was evaluated using electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization. The EIS results showed that the polarization resistance (R{sub p}) of the PEO–PLLA Mg was close to two orders of magnitude higher than that of the PEO Mg. While the corrosion current density (i{sub corr}) of the pure Mg was reduced by 65% with the PEO coating, the PEO–PLLA coating reduced the i{sub corr} by almost 100%. As expected, the R{sub p} of the PEO–PLLA Mg decreased with increase in exposure time. However, it was noted that the R{sub p} of the PEO–PLLA Mg even after 100 h was six times higher than that of the PEO Mg after 48 h exposure, and did not show any visible localized attack.

About influence of buffer porous layers between epitaxial layers of heterostructure on distributions of concentrations of dopants in heterobipolar transistors

Directory of Open Access Journals (Sweden)

E Pankratov

2016-10-01

Full Text Available In this paper we introduce an approach to manufacture a heterobipolar transistors. Framework this approach we consider doping by diffusion or by ion implantation of required parts of a heterostructure with special configuration and optimization of annealing of dopant and/or radiation defects. In this case one have possibility to manufacture bipolar transistors, which include into itself p-n-junctions with higher sharpness and smaller dimensions. We also consider influence of presents of buffer porous layers between epitaxial layers of heterostructure on distributions of concentrations of dopants in the considered transistors. An approach to decrease value of mismatch-induced stress has been considered.

Charge Efficiency: A Functional Tool to Probe the Double-Layer Structure Inside of Porous Electrodes and Application in the Modeling of Capacitive Deionization

NARCIS (Netherlands)

Zhao, R.; Biesheuvel, P.M.; Miedema, H.; Bruning, H.; Wal, van der A.

2010-01-01

Porous electrodes are important in many physical-chemical processes including capacitive deionization (CDI), a desalination technology where ions are adsorbed from solution into the electrostatic double layers formed at the electrode/solution interface inside of two juxtaposed porous electrodes. A

Complementary study of the internal porous silicon layers formed under high-dose implantation of helium ions

Energy Technology Data Exchange (ETDEWEB)

Lomov, A. A., E-mail: lomov@ftian.ru; Myakon’kikh, A. V. [Russian Academy of Sciences, Institute of Physics and Technology (Russian Federation); Chesnokov, Yu. M. [National Research Centre “Kurchatov Institute” (Russian Federation); Shemukhin, A. A.; Oreshko, A. P. [Moscow State University (Russian Federation)

2017-03-15

The surface layers of Si(001) substrates subjected to plasma-immersion implantation of helium ions with an energy of 2–5 keV and a dose of 5 × 10{sup 17} cm{sup –2} have been investigated using high-resolution X-ray reflectivity, Rutherford backscattering, and transmission electron microscopy. The electron density depth profile in the surface layer formed by helium ions is obtained, and its elemental and phase compositions are determined. This layer is found to have a complex structure and consist of an upper amorphous sublayer and a layer with a porosity of 30–35% beneath. It is shown that the porous layer has the sharpest boundaries at a lower energy of implantable ions.

Natural convection boundary layer with suction and mass transfer in a porous medium

International Nuclear Information System (INIS)

Bestman, A.R.

1989-03-01

The free convection boundary layer flow with simultaneous heat and mass transfer in a porous medium is studied when the boundary wall moves in its own plane with suction. The study also incorporates chemical reaction for the very simple model of a binary reaction with Arrhenius activation energy. For large suction asymptotic approximate solutions are obtained for the flow variables for various values of the activation energy. (author). 10 refs, 2 figs

A combined SEM, CV and EIS study of multi-layered porous ceramic reactors for flue gas purification

DEFF Research Database (Denmark)

He, Zeming; Andersen, Kjeld Bøhm; Nygaard, Frederik Berg

2013-01-01

The effect of sintering temperature of 12-layered porous ceramic reactors (comprising 5 cells) was studied using scanning electron microscopy (SEM), cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). The difference in microstructures of the reactors was evaluated by SEM...

Influence of ferrocyanide inhibitors on the transport and crystrallization processes of sodium chloride in porous building materials

NARCIS (Netherlands)

Gupta, S.; Terheiden, K.H; Pel, L.; Sawdy - Heritage, A.M.

2012-01-01

Salt weathering leads to destruction of many valuable cultural heritage monuments and porous building materials. In order to reduce the impact of this, effective treatment methods are required. The use of crystallization inhibitors to mitigate salt damage has been proposed in the past; however, to

Porous double-layer polymer tubing for the potential use in heterogeneous continuous flow reactions.

Science.gov (United States)

Herwig, Gordon; Hornung, Christian H; Peeters, Gary; Ebdon, Nicholas; Savage, G Paul

2014-12-24

Functional polymer tubing with an OD of 1/16 or 1/8 in. was fabricated by a simple polymer coextrusion process. The tubing was made of an outer impervious polypropylene layer and an inner layer, consisting of a blend of a functional polymer, polyethylene-co-methacrylic acid, and a sacrificial polymer, polystyrene. After a simple solvent leaching step using common organic solvents, the polystyrene was removed, leaving behind a porous inner layer that contains functional carboxylic acid groups, which could then be used for the immobilization of target molecules. Solution-phase reactions using amines or isocyanates have proven successful for the immobilization of a series of small molecules and polymers. This flexible multilayered functional tubing can be easily cut to the desired length and connected via standard microfluidic fittings.

Multi-layer porous fiber-reinforced composites for implants: in vitro calcium phosphate formation in the presence of bioactive glass.

Science.gov (United States)

Nganga, Sara; Zhang, Di; Moritz, Niko; Vallittu, Pekka K; Hupa, Leena

2012-11-01

Glass-fiber-reinforced composites (FRCs), based on bifunctional methacrylate resin, have recently shown their potential for use as durable cranioplasty, orthopedic and oral implants. In this study we suggest a multi-component sandwich implant structure with (i) outer layers out of porous FRC, which interface the cortical bone, and (ii) inner layers encompassing bioactive glass granules, which interface with the cancellous bone. The capability of Bioglass(®) 45S5 granules (100-250μm) to induce calcium phosphate formation on the surface of the FRC was explored by immersing the porous FRC-Bioglass laminates in simulated body fluid (SBF) for up to 28d. In both static (agitated) and dynamic conditions, bioactive glass granules induced precipitation of calcium phosphate at the laminate surfaces as confirmed by scanning electron microscopy. The proposed dynamic flow system is useful for the in vitro simulation of bone-like apatite formation on various new porous implant designs containing bioactive glass and implant material degradation. Copyright © 2012 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Porous silicon carbide (SIC) semiconductor device

Science.gov (United States)

Shor, Joseph S. (Inventor); Kurtz, Anthony D. (Inventor)

1996-01-01

Porous silicon carbide is fabricated according to techniques which result in a significant portion of nanocrystallites within the material in a sub 10 nanometer regime. There is described techniques for passivating porous silicon carbide which result in the fabrication of optoelectronic devices which exhibit brighter blue luminescence and exhibit improved qualities. Based on certain of the techniques described porous silicon carbide is used as a sacrificial layer for the patterning of silicon carbide. Porous silicon carbide is then removed from the bulk substrate by oxidation and other methods. The techniques described employ a two-step process which is used to pattern bulk silicon carbide where selected areas of the wafer are then made porous and then the porous layer is subsequently removed. The process to form porous silicon carbide exhibits dopant selectivity and a two-step etching procedure is implemented for silicon carbide multilayers.

Porous material neutron detector

Science.gov (United States)

Diawara, Yacouba [Oak Ridge, TN; Kocsis, Menyhert [Venon, FR

2012-04-10

A neutron detector employs a porous material layer including pores between nanoparticles. The composition of the nanoparticles is selected to cause emission of electrons upon detection of a neutron. The nanoparticles have a maximum dimension that is in the range from 0.1 micron to 1 millimeter, and can be sintered with pores thereamongst. A passing radiation generates electrons at one or more nanoparticles, some of which are scattered into a pore and directed toward a direction opposite to the applied electrical field. These electrons travel through the pore and collide with additional nanoparticles, which generate more electrons. The electrons are amplified in a cascade reaction that occurs along the pores behind the initial detection point. An electron amplification device may be placed behind the porous material layer to further amplify the electrons exiting the porous material layer.

Mixed convection boundary layer flow over a vertical surface embedded in a thermally stratified porous medium

International Nuclear Information System (INIS)

Ishak, Anuar; Nazar, Roslinda; Pop, Ioan

2008-01-01

The mixed convection boundary layer flow through a stable stratified porous medium bounded by a vertical surface is investigated. The external velocity and the surface temperature are assumed to vary as x m , where x is measured from the leading edge of the vertical surface and m is a constant. Numerical solutions for the governing Darcy and energy equations are obtained. The results indicate that the thermal stratification significantly affects the surface shear stress as well as the surface heat transfer, besides delays the boundary layer separation

Effect of non-local equilibrium on minimal thermal resistance porous layered systems

International Nuclear Information System (INIS)

Leblond, Genevieve; Gosselin, Louis

2008-01-01

In this paper, the cooling of a heat-generating surface by a stacking of porous media (e.g., metallic foam) through which fluid flows parallel to the surface is considered. A two-temperature model is proposed to account for non-local thermal equilibrium (non-LTE). A scale analysis is performed to determine temperatures profiles in the boundary layer regime. The hot spot temperature is minimized with respect to the three design variables of each layer: porosity, pore diameter, and material. Global cost and mass are constrained. The optimization is performed with a hybrid genetic algorithm (GA) including local search to enhance convergence and repeatability. Results demonstrate that the optimized stacks do not operate in LTE. Therefore, we show that assuming LTE might result in underestimation of the hot spot temperature, and into different final designs as well

Porous-shaped silicon carbide ultraviolet photodetectors on porous silicon substrates

Energy Technology Data Exchange (ETDEWEB)

Naderi, N., E-mail: naderi.phd@gmail.com [Nano-Optoelectronics Research Laboratory, School of Physics, Universiti Sains Malaysia, 11800 USM, Penang (Malaysia); Hashim, M.R. [Nano-Optoelectronics Research Laboratory, School of Physics, Universiti Sains Malaysia, 11800 USM, Penang (Malaysia)

2013-03-05

Highlights: ► Porous-shaped silicon carbide thin film was deposited on porous silicon substrate. ► Thermal annealing was followed to enhance the physical properties of samples. ► Metal–semiconductor-metal ultraviolet detectors were fabricated on samples. ► The effect of annealing temperature on electrical performance of devices was studied. ► The efficiency of photodetectors was enhanced by annealing at elevated temperatures. -- Abstract: A metal–semiconductor-metal (MSM) ultraviolet photodetector was fabricated based on a porous-shaped structure of silicon carbide (SiC). For increasing the surface roughness of SiC and hence enhancing the light absorption effect in fabricated devices, porous silicon (PS) was chosen as a template; SiC was deposited on PS substrates via radio frequency magnetron sputtering. Therefore, the deposited layers followed the structural pattern of PS skeleton and formed a porous-shaped SiC layer on PS substrate. The structural properties of samples showed that the as-deposited SiC was amorphous. Thus, a post-deposition annealing process with elevated temperatures was required to convert its amorphous phase to crystalline phase. The morphology of the sputtered samples was examined via scanning electron and atomic force microscopies. The grain size and roughness of the deposited layers clearly increased upon an increase in the annealing temperature. The optical properties of sputtered SiC were enhanced due to applying high temperatures. The most intense photoluminescence peak was observed for the sample with 1200 °C of annealing temperature. For the metallization of the SiC substrates to fabricate MSM photodetectors, two interdigitated Schottky contacts of Ni with four fingers for each electrode were deposited onto all the porous substrates. The optoelectronic characteristics of MSM UV photodetectors with porous-shaped SiC substrates were studied in the dark and under UV illumination. The electrical characteristics of fabricated

Porous-shaped silicon carbide ultraviolet photodetectors on porous silicon substrates

International Nuclear Information System (INIS)

Naderi, N.; Hashim, M.R.

2013-01-01

Highlights: ► Porous-shaped silicon carbide thin film was deposited on porous silicon substrate. ► Thermal annealing was followed to enhance the physical properties of samples. ► Metal–semiconductor-metal ultraviolet detectors were fabricated on samples. ► The effect of annealing temperature on electrical performance of devices was studied. ► The efficiency of photodetectors was enhanced by annealing at elevated temperatures. -- Abstract: A metal–semiconductor-metal (MSM) ultraviolet photodetector was fabricated based on a porous-shaped structure of silicon carbide (SiC). For increasing the surface roughness of SiC and hence enhancing the light absorption effect in fabricated devices, porous silicon (PS) was chosen as a template; SiC was deposited on PS substrates via radio frequency magnetron sputtering. Therefore, the deposited layers followed the structural pattern of PS skeleton and formed a porous-shaped SiC layer on PS substrate. The structural properties of samples showed that the as-deposited SiC was amorphous. Thus, a post-deposition annealing process with elevated temperatures was required to convert its amorphous phase to crystalline phase. The morphology of the sputtered samples was examined via scanning electron and atomic force microscopies. The grain size and roughness of the deposited layers clearly increased upon an increase in the annealing temperature. The optical properties of sputtered SiC were enhanced due to applying high temperatures. The most intense photoluminescence peak was observed for the sample with 1200 °C of annealing temperature. For the metallization of the SiC substrates to fabricate MSM photodetectors, two interdigitated Schottky contacts of Ni with four fingers for each electrode were deposited onto all the porous substrates. The optoelectronic characteristics of MSM UV photodetectors with porous-shaped SiC substrates were studied in the dark and under UV illumination. The electrical characteristics of fabricated

Spatial atomic layer deposition for coating flexible porous Li-ion battery electrodes

Energy Technology Data Exchange (ETDEWEB)

Yersak, Alexander S.; Sharma, Kashish; Wallas, Jasmine M.; Dameron, Arrelaine A.; Li, Xuemin; Yang, Yongan; Hurst, Katherine E.; Ban, Chunmei; Tenent, Robert C.; George, Steven M. [Department of Chemistry and Biochemistry, University of Colorado, Boulder, Colorado 80309 and Department of Mechanical Engineering, University of Colorado, Boulder, Colorado 80309

2018-01-01

Ultrathin atomic layer deposition (ALD) coatings on the electrodes of Li-ion batteries can enhance the capacity stability of the Li-ion batteries. To commercialize ALD for Li-ion battery production, spatial ALD is needed to decrease coating times and provide a coating process compatible with continuous roll-to-roll (R2R) processing. The porous electrodes of Li-ion batteries provide a special challenge because higher reactant exposures are needed for spatial ALD in porous substrates. This work utilized a modular rotating cylinder spatial ALD reactor operating at rotation speeds up to 200 revolutions/min (RPM) and substrate speeds up to 200 m/min. The conditions for spatial ALD were adjusted to coat flexible porous substrates. The reactor was initially used to characterize spatial Al2O3 and ZnO ALD on flat, flexible metalized polyethylene terephthalate foils. These studies showed that slower rotation speeds and spacers between the precursor module and the two adjacent pumping modules could significantly increase the reactant exposure. The modular rotating cylinder reactor was then used to coat flexible, model porous anodic aluminum oxide (AAO) membranes. The uniformity of the ZnO ALD coatings on the porous AAO membranes was dependent on the aspect ratio of the pores and the reactant exposures. Larger reactant exposures led to better uniformity in the pores with higher aspect ratios. The reactant exposures were increased by adding spacers between the precursor module and the two adjacent pumping modules. The modular rotating cylinder reactor was also employed for Al2O3 ALD on porous LiCoO2 (LCO) battery electrodes. Uniform Al coverages were obtained using spacers between the precursor module and the two adjacent pumping modules at rotation speeds of 25 and 50 RPM. The LCO electrodes had a thickness of ~49 um and pores with aspect ratios of ~12-25. Coin cells were then constructed using the ALD-coated LCO electrodes and were tested to determine their battery

Comparison of salt solution and air drying methods for moisture fixation in highly porous building materials

DEFF Research Database (Denmark)

Antonov, Yovko Ivanov; Jensen, Rasmus Lund; Møldrup, Per

2017-01-01

In recent years, research has identified some bio-based, porous building materials as good or excellent regulators of moisture in buildings. The ability of a material to absorb, release and store moisture is described by vapour sorption isotherms. It is necessary input to simulations of indoor...... building materials by a standardized testing method, using saturated salt solutions. Furthermore, results from the standard method are compared to values of moisture content for the same materials, obtained by air-drying at different relative humidity. This is done with the aim to compare the findings from...... the two methods with respect to time and repeatability of the results. Derived isotherms are further used as direct input in the building simulation software BSim, which is capable of predicting indoor environment parameters by solving coupled, transient heat and moisture transport equations using finite...

Formation of multiple levels of porous silicon for buried insulators and conductors in silicon device technologies

Science.gov (United States)

Blewer, Robert S.; Gullinger, Terry R.; Kelly, Michael J.; Tsao, Sylvia S.

1991-01-01

A method of forming a multiple level porous silicon substrate for semiconductor integrated circuits including anodizing non-porous silicon layers of a multi-layer silicon substrate to form multiple levels of porous silicon. At least one porous silicon layer is then oxidized to form an insulating layer and at least one other layer of porous silicon beneath the insulating layer is metallized to form a buried conductive layer. Preferably the insulating layer and conductive layer are separated by an anodization barrier formed of non-porous silicon. By etching through the anodization barrier and subsequently forming a metallized conductive layer, a fully or partially insulated buried conductor may be fabricated under single crystal silicon.

MULTILAYER POROUS COMPOSITE FROM WASTE GLASS FOR WATER FILTRATION

Directory of Open Access Journals (Sweden)

M. P. Aji

2015-07-01

Full Text Available Multilayer porous composite have been produced through the heating process at temperature T=700oC for 2.5 h. Single layered porous composite was made with a varied mass percentage of from PEG polymer  1% to 10%. Double-layered porous composite were made by the arrangement of porosity (4:3%, (4:2% and (3:2%, while the three-layers porous composite have an arrangement (4:3:2%. Performance of multilayer porous composite for water filtration with pollutants of methylene blue 100 ppm was estimated from the absorbance spectrum. Rejection of methylene blue pollutants from single layered porous composite increases when the fraction of PEG polymer tend to be smaller in the matrix. Meanwhile, the double layered porous composite has a degradation of methylene blue pollutants are better than one layer. Triple layered porous composite have good performance for the water filtration where all the pollutants of methylene blue be able to be filtered.   Komposit pori berlapis telah dihasilkan dengan proses pemanasan pada temperatur T=700oC selama 2.5 jam. Komposit pori satu lapis dibuat dengan variasi persen massa polimer PEG 1% hingga 10%. Komposit pori dua lapis dibuat dengan susunan porositas (4:3%, (4:2% dan (3:2%, sedangkan komposit pori tiga lapis memiliki susunan porositas (4:3:2%. Kinerja komposit pori berlapis untuk filter air dengan polutan methylene blue 100 ppm diestimasi dari spektrum absorbansi. Rejeksi polutan methylene blue dari komposit pori satu lapis meningkat saat fraksi polimer PEG cenderung lebih kecil dalam matrik komposit. Sedangkan, komposit pori dua lapis memiliki kemampuan untuk degradasi polutan methylene blue yang lebih baik dari satu lapis. Komposit pori tiga lapis memiliki kinerja yang baik untuk filter air dimana seluruh polutan methylene blue mampu disaring. 

A Thermoelectric Generator Using Porous Si Thermal Isolation

Directory of Open Access Journals (Sweden)

Emmanouel Hourdakis

2013-10-01

Full Text Available In this paper we report on a thermoelectric generator (TEG using thermal isolation provided by a thick porous Si layer locally formed on the Si wafer and thermocouples composed of p-doped polycrystalline Si/Al. The “hot” contacts of the thermocouples lie on the porous Si layer, while the “cold” contacts lie on bulk crystalline Si. A housing was also designed and fabricated in order to transfer any external temperature change on the “hot” contacts of the thermocouples, the “cold” contacts being isolated from the “hot” contacts by a thick resist layer. The fabrication of the sensing element (Si die is fully compatible with batch Si processing. The output power of the thermoelectric generator depends on the porous Si isolation layer thickness, porosity, structure and morphology. For a mesoporous Si layer of 60% porosity and a macroscopic temperature differential of 10 K, an output power of 0.39 μW/cm2 was measured for a 50 μm thick porous Si layer.

A Thermoelectric Generator Using Porous Si Thermal Isolation

Science.gov (United States)

Hourdakis, Emmanouel; Nassiopoulou, Androula G.

2013-01-01

In this paper we report on a thermoelectric generator (TEG) using thermal isolation provided by a thick porous Si layer locally formed on the Si wafer and thermocouples composed of p-doped polycrystalline Si/Al. The “hot” contacts of the thermocouples lie on the porous Si layer, while the “cold” contacts lie on bulk crystalline Si. A housing was also designed and fabricated in order to transfer any external temperature change on the “hot” contacts of the thermocouples, the “cold” contacts being isolated from the “hot” contacts by a thick resist layer. The fabrication of the sensing element (Si die) is fully compatible with batch Si processing. The output power of the thermoelectric generator depends on the porous Si isolation layer thickness, porosity, structure and morphology. For a mesoporous Si layer of 60% porosity and a macroscopic temperature differential of 10 K, an output power of 0.39 μW/cm2 was measured for a 50 μm thick porous Si layer. PMID:24152923

Ta penetration into template-type porous low-k material during atomic layer deposition of TaN

International Nuclear Information System (INIS)

Furuya, Akira; Ohtsuka, Nobuyuki; Misawa, Kaori; Shimada, Miyoko; Ogawa, Shinichi

2005-01-01

Ta penetration into a planar template-type porous low-k film during atomic layer deposition of TaN has been investigated by evaluating relations between Ta penetration and number of deposition cycles, exposure time of Ta precursor per deposition cycle, substrate temperature, and porosity of the porous low-k. The precursors were pentakisdimethylaminotantalum [PDMAT:Ta(N(CH 3 ) 2 ) 5 ] and NH 3 . The porous low-k was a methylsiloxane (MSX) whose pore size in the maximum distribution and porosity of the porous low-k were 0-1.9 nm and 0%-47%. Depth profile of the Ta penetration was measured by transmission electron microscopy and energy dispersive x-ray spectroscopy. The amount of penetrated and the penetration depth depended on the porosity. It was found that the precursors penetrate into the MSX film dominantly by gas phase diffusion through pores connecting from the surface to the inside. Increased surface area of the MSX film due to the pores results in a depletion of precursor at the wafer edge, and that this depletion causes the penetration characteristics at the edge of wafer differ from those at the center of the wafer. Moreover, the thickness required for the pore sealing by additive liner deposition is discussed

Analysis of the sintering stresses and shape distortion produced in co-firing of CGO-LSM/CGO bi-layer porous structures

DEFF Research Database (Denmark)

Ni, De Wei; Esposito, Vincenzo; Schmidt, Cristine Grings

such as cracks, de-lamination and shape distortion can result as a consequence of sintering mismatch stresses caused by the strain rate difference between layers. This work seeks to understand the underlying mechanisms that occur during the co-firing of porous CGO-LSM/CGO bi-layer laminates, by evaluating...... the sintering mismatch stress and distortion development through modeling and experiments....

Steady flow in a porous layer subjected to a stream uniformly injecting from a plane; Ichiyo ni men kara fukidasu nagare ni sarasareta takoshitsu sonai no teijo nagare

Energy Technology Data Exchange (ETDEWEB)

Hasegawa, E; Horiguchi, Y; Kitazawa, K [Keio University, Tokyo (Japan). Faculty of Science and Technology

1997-08-25

A steady flow in an non-deformable porous layer subjected to a fluid stream is studied analytically and numerically. One side of the layer of sponge is bounded by a solid wall and the other by a layer of fluid. The fluid is injected uniformly from a plane, through which the fluid can pass, set up parallel to the sponge layer. The flow in the sponge layer is assumed to be governed by Darcy`s law. The problem considered is solved in terms of a similarity solution. The equations governing the fluid flows in both the porous layer and the fluid layer are reduced to a system of the ordinary differential equations. These equations are solved analytically for three cases ideal fluid flow, low Reynolds number flow and high Reynolds number flow. On the other hand, these equations are solved numerically for the general case by using the finite difference method. The distributions of the velocity and the pressure in both layers are found for various parameters. In particular, the speed which the fluid intrudes into the sponge layer due to the injection of the stream from the plane is found to be a function of dimensionless parameters. To find this speed is essential to the understanding of porous material. 15 refs., 9 figs.

Coated Porous Si for High Performance On-Chip Supercapacitors

Science.gov (United States)

Grigoras, K.; Keskinen, J.; Grönberg, L.; Ahopelto, J.; Prunnila, M.

2014-11-01

High performance porous Si based supercapacitor electrodes are demonstrated. High power density and stability is provided by ultra-thin TiN coating of the porous Si matrix. The TiN layer is deposited by atomic layer deposition (ALD), which provides sufficient conformality to reach the bottom of the high aspect ratio pores. Our porous Si supercapacitor devices exhibit almost ideal double layer capacitor characteristic with electrode volumetric capacitance of 7.3 F/cm3. Several orders of magnitude increase in power and energy density is obtained comparing to uncoated porous silicon electrodes. Good stability of devices is confirmed performing several thousands of charge/discharge cycles.

Distinguishing oil and water layers in a cracked porous medium using pulsed neutron logging data based on Hudson's crack theory

Science.gov (United States)

Zhang, Xueang; Yang, Zhichao; Tang, Bin; Wang, Renbo; Wei, Xiong

2018-05-01

During geophysical surveys, water layers may interfere with the detection of oil layers. In order to distinguish between oil and water layers in porous cracked media, research on the properties of the cracks, the oil and water layers, and their relation to pulsed neutron logging characteristics is essential. Using Hudson's crack theory, we simulated oil and water layers in a cracked porous medium with different crack parameters corresponding to the well log responses. We found that, in a cracked medium with medium-angle (40°-50°) cracks, the thermal neutron count peak value is higher and more sensitive than those in low-angle and high-angle crack environments; in addition, the thermal neutron density distribution shows more minimum values than in other cases. Further, the thermal neutron count and the rate of change for the oil layer are greater than those of the water layer, and the time spectrum count peak value for the water layer in middle-high-angle (40°-70°) cracked environments is higher than that of the oil layer. The thermal neutron density distribution sensitivity is higher in the water layer with a range of small crack angles (0°-30°) than in the oil layer with the same range of angles. In comparing the thermal neutron density distribution, thermal neutron count peak, thermal neutron density distribution sensitivity, and time spectrum maximum in the oil and water layers, we find that neutrons in medium-angle (40°-50°) cracked reservoirs are more sensitive to deceleration and absorption than those in water layers; neutrons in approximately horizontal (0°-30°) cracked water layers are more sensitive to deceleration than those in reservoirs. These results can guide future work in the cracked media neutron logging field.

White light emission from fluorescent SiC with porous surface

DEFF Research Database (Denmark)

Lu, Weifang; Ou, Yiyu; Fiordaliso, Elisabetta Maria

2017-01-01

We report for the frst time a NUV light to white light conversion in a N-B co-doped 6H-SiC (fuorescent SiC) layer containing a hybrid structure. The surface of fuorescent SiC sample contains porous structures fabricated by anodic oxidation method. After passivation by 20nm thick Al2O3, the photol......We report for the frst time a NUV light to white light conversion in a N-B co-doped 6H-SiC (fuorescent SiC) layer containing a hybrid structure. The surface of fuorescent SiC sample contains porous structures fabricated by anodic oxidation method. After passivation by 20nm thick Al2O3...... the bulk fuorescent SiC layer. A high color rendering index of 81.1 has been achieved. Photoluminescence spectra in porous layers fabricated in both commercial n-type and lab grown N-B co-doped 6H-SiC show two emission peaks centered approximately at 460nm and 530nm. Such bluegreen emission phenomenon can......, the photoluminescence intensity from the porous layer was signifcant enhanced by a factor of more than 12. Using a porous layer of moderate thickness (~10µm), high-quality white light emission was realized by combining the independent emissions of blue-green emission from the porous layer and yellow emission from...

Electrochemical properties of porous carbon black layer as an electron injector into iodide redox couple

International Nuclear Information System (INIS)

Kim, Jung-Min; Rhee, Shi-Woo

2012-01-01

Highlights: ► Carbon black (CB) porous layer for triiodide (I 3 − ) ion reduction is coated with spray coating method at 120 °C on the fluorine-doped tin oxide glass. ► The electrochemical impedance spectroscopy is analyzed for a symmetric cell and a new circuit model is applied to identify electrochemical parameters. ► Decreased particle size and increased thickness improve the catalytic activity because of the increase in the surface area and the conductivity of the CB layer. - Abstract: Electrochemical properties of carbon black (CB) porous layer as a counter electrode in dye-sensitized solar cells (DSC) are studied. CB electrode for triiodide (I 3 − ) ion reduction is coated with spray coating method on the fluorine-doped tin oxide glass at 120 °C. The CB particle size is varied from 20 nm to 90 nm and the CB electrode thickness is controlled from 1 μm to 9 μm by controlling the spraying time. The electrochemical impedance spectroscopy is analyzed for a symmetric cell and a new circuit model is applied to identify electrochemical parameters. As the CB particle size is decreased, the catalytic activity is improved because of the increase in the surface area and the conductivity of the CB layer. Increased CB electrode thickness also improves the catalytic activity and leads to the low charge transfer resistance at the electrolyte/CB electrode interface. The CB counter electrode with the particle size of 20 nm and the thickness of 9 μm for DSC shows the energy conversion efficiency of 7.2% with the highest fill factor (FF) of 65.6%, which is similar to the Pt counter electrode with FF of 65.8% and the efficiency of 7.6%.

Luminescence of porous silicon doped by erbium

International Nuclear Information System (INIS)

Bondarenko, V.P.; Vorozov, N.N.; Dolgij, L.N.; Dorofeev, A.M.; Kazyuchits, N.M.; Leshok, A.A.; Troyanova, G.N.

1996-01-01

The possibility of the 1.54 μm intensive luminescence in the silicon dense porous layers, doped by erbium, with various structures is shown. Low-porous materials of both porous type on the p-type silicon and porous silicon with wood-like structure on the n + type silicon may be used for formation of light-emitting structures

THE USE OF AIR LAYERS IN BUILDING ENVELOPES FOR ENERGY SAVING DURING AIR CONDITIONING

Directory of Open Access Journals (Sweden)

S. N. Osipov

2017-01-01

Full Text Available Since there are no large natural energy resources in Belarus, energy savings ought to be a point of the special attention. With this regard it is important to develop modern ways of savings during the process of air conditioning inside new buildings with an air layer in the enclosure, especially in translucent ones. The system of ventilation of air layers in the enclosure of a building has been introduced in which air movement is caused by the gravitational and aerodynamic forces. It makes it possible to arrange further ventilation – a natural, forced or a hybrid one. With the purpose of increasing and streamlining natural draught the partitions are used separating the different parts of air layers. For natural ventilation with the use of gravitational forces the holes in the upper and lower parts of the partitions between adjacent air layers are applied. Natural ventilation in the holes of the partitions is regulated by movable shutters, blinds or other adjusting devices. For combined or forced air exchange between adjacent zones of air layers fans are used pumping air from the air layer zones with a higher temperature to zones of air layers with lower temperature and vice versa. When air exchange is forced, in order to intensify the infiltration of air into zones of air layers jets are laid on a hard surface. In order to cool a multi-layered enclosure of a building, where the movement of air between the air layers (that have been formed by internal partitions is being fulfilled by a natural, forced or combined mode, a part of the air or the total air processed inside the building (i.e. conditioned or non-conditioned air cooler as compared with the outside one is being sent to these strata. Combined or forced flow of the air processed inside the building into the air layers is done through the ducts associated with the output channels of the air conditioners. The internal partitions are equipped with the air valve hole.

Porosity and thickness effect of porous silicon layer on photoluminescence spectra

Science.gov (United States)

Husairi, F. S.; Eswar, K. A.; Guliling, Muliyadi; Khusaimi, Z.; Rusop, M.; Abdullah, S.

2018-05-01

The porous silicon nanostructures was prepared by electrochemical etching of p-type silicon wafer. Porous silicon prepared by using different current density and fix etching time with assistance of halogen lamp. The physical structure of porous silicon measured by the parameters used which know as experimental factor. In this work, we select one of those factors to correlate which optical properties of porous silicon. We investigated the surface morphology by using Surface Profiler (SP) and photoluminescence using Photoluminescence (PL) spectrometer. Different physical characteristics of porous silicon produced when current density varied. Surface profiler used to measure the thickness of porous and the porosity calculated using mass different of silicon. Photoluminescence characteristics of porous silicon depend on their morphology because the size and distribution of pore its self will effect to their exciton energy level. At J=30 mA/cm2 the shorter wavelength produced and it followed the trend of porosity with current density applied.

Method of fabricating porous silicon carbide (SiC)

Science.gov (United States)

Shor, Joseph S. (Inventor); Kurtz, Anthony D. (Inventor)

1995-01-01

Porous silicon carbide is fabricated according to techniques which result in a significant portion of nanocrystallites within the material in a sub 10 nanometer regime. There is described techniques for passivating porous silicon carbide which result in the fabrication of optoelectronic devices which exhibit brighter blue luminescence and exhibit improved qualities. Based on certain of the techniques described porous silicon carbide is used as a sacrificial layer for the patterning of silicon carbide. Porous silicon carbide is then removed from the bulk substrate by oxidation and other methods. The techniques described employ a two-step process which is used to pattern bulk silicon carbide where selected areas of the wafer are then made porous and then the porous layer is subsequently removed. The process to form porous silicon carbide exhibits dopant selectivity and a two-step etching procedure is implemented for silicon carbide multilayers.

Porous Media and Immersed Boundary Hybrid-Modelling for Simulating Flow in Stone Cover-Layers

DEFF Research Database (Denmark)

Jensen, Bjarne; Liu, Xiaofeng; Christensen, Erik Damgaard

In this paper we present a new numerical modelling approach for coastal and marine applications where a porous media conceptual model was combined with a free surface volume-of-fluid (VOF) model and an immersed boundary method (IBM). The immersed boundary model covers the method of describing....... In this paper, the model is applied to investigate two practical cases in terms of a cover layer of stones on a flat bed under oscillatory flow at different packing densities, and a rock toe structure at a breakwater....

Analysis of boundary layer flow over a porous nonlinearly stretching sheet with partial slip at

Directory of Open Access Journals (Sweden)

Swati Mukhopadhyay

2013-12-01

Full Text Available The boundary layer flow of a viscous incompressible fluid toward a porous nonlinearly stretching sheet is considered in this analysis. Velocity slip is considered instead of no-slip condition at the boundary. Similarity transformations are used to convert the partial differential equation corresponding to the momentum equation into nonlinear ordinary differential equation. Numerical solution of this equation is obtained by shooting method. It is found that the horizontal velocity decreases with increasing slip parameter.

Convection and reaction in a diffusive boundary layer in a porous medium: nonlinear dynamics.

Science.gov (United States)

Andres, Jeanne Therese H; Cardoso, Silvana S S

2012-09-01

We study numerically the nonlinear interactions between chemical reaction and convective fingering in a diffusive boundary layer in a porous medium. The reaction enhances stability by consuming a solute that is unstably distributed in a gravitational field. We show that chemical reaction profoundly changes the dynamics of the system, by introducing a steady state, shortening the evolution time, and altering the spatial patterns of velocity and concentration of solute. In the presence of weak reaction, finger growth and merger occur effectively, driving strong convective currents in a thick layer of solute. However, as the reaction becomes stronger, finger growth is inhibited, tip-splitting is enhanced and the layer of solute becomes much thinner. Convection enhances the mass flux of solute consumed by reaction in the boundary layer but has a diminishing effect as reaction strength increases. This nonlinear behavior has striking differences to the density fingering of traveling reaction fronts, for which stronger chemical kinetics result in more effective finger merger owing to an increase in the speed of the front. In a boundary layer, a strong stabilizing effect of reaction can maintain a long-term state of convection in isolated fingers of wavelength comparable to that at onset of instability.

Selective formation of porous silicon

Science.gov (United States)

Fathauer, Robert W. (Inventor); Jones, Eric W. (Inventor)

1993-01-01

A pattern of porous silicon is produced in the surface of a silicon substrate by forming a pattern of crystal defects in said surface, preferably by applying an ion milling beam through openings in a photoresist layer to the surface, and then exposing said surface to a stain etchant, such as HF:HNO3:H2O. The defected crystal will preferentially etch to form a pattern of porous silicon. When the amorphous content of the porous silicon exceeds 70 percent, the porous silicon pattern emits visible light at room temperature.

Comparative study of Ta, TaN and Ta/TaN bi-layer barriers for Cu-ultra low-k porous polymer integration

International Nuclear Information System (INIS)

Yang, L.Y.; Zhang, D.H.; Li, C.Y.; Foo, P.D.

2004-01-01

Tantalum (Ta), TaN and bilayer Ta/TaN barriers deposited on ultra-low-k porous polymer (ULKPP) and the thermal stability of their structures are comparatively investigated using various techniques. The Ta/ultra-low-k polymer shows the smallest sheet resistance, but the poorest thermal stability, while TaN on the ultra-low-k polymer shows the highest resistance but the best thermal stability. The bi-layer Ta/TaN barrier takes the advantage of both Ta and TaN barriers and gives reasonable resistance and thermal stability. The electrical tests indicate that the Cu lines with the TaN and bi-layer Ta/TaN barriers exhibit the smaller leakage current and higher breakdown voltage compared with the Cu lines with the Ta barrier. The better thermal stability of the TaN and the bi-layer Ta/TaN barriers is mainly due to the amorphous/nanostructure and less grain boundaries of the barriers. In addition, the texture discontinuity at the Ta/TaN interfaces in the bi-layers barrier also plays an important role in reducing mutual diffusion of Ta atoms in the Ta barrier and some atoms in the ultra-low-k porous polymer

Atomic Layer Deposition on Porous Materials: Problems with Conventional Approaches to Catalyst and Fuel Cell Electrode Preparation

Directory of Open Access Journals (Sweden)

Tzia Ming Onn

2018-03-01

Full Text Available Atomic layer deposition (ALD offers exciting possibilities for controlling the structure and composition of surfaces on the atomic scale in heterogeneous catalysts and solid oxide fuel cell (SOFC electrodes. However, while ALD procedures and equipment are well developed for applications involving flat surfaces, the conditions required for ALD in porous materials with a large surface area need to be very different. The materials (e.g., rare earths and other functional oxides that are of interest for catalytic applications will also be different. For flat surfaces, rapid cycling, enabled by high carrier-gas flow rates, is necessary in order to rapidly grow thicker films. By contrast, ALD films in porous materials rarely need to be more than 1 nm thick. The elimination of diffusion gradients, efficient use of precursors, and ligand removal with less reactive precursors are the major factors that need to be controlled. In this review, criteria will be outlined for the successful use of ALD in porous materials. Examples of opportunities for using ALD to modify heterogeneous catalysts and SOFC electrodes will be given.

Radon transport model into a porous ground layer of finite capacity

Science.gov (United States)

Parovik, Roman

2017-10-01

The model of radon transfer is considered in a porous ground layer of finite power. With the help of the Laplace integral transformation, a numerical solution of this model is obtained which is based on the construction of a generalized quadrature formula of the highest degree of accuracy for the transition to the original - the function of solving this problem. The calculated curves are constructed and investigated depending on the diffusion and advection coefficients.The work was a mathematical model that describes the effect of the sliding attachment (stick-slip), taking into account hereditarity. This model can be regarded as a mechanical model of earthquake preparation. For such a model was proposed explicit finite- difference scheme, on which were built the waveform and phase trajectories hereditarity effect of stick-slip.

Structural and optical properties of vapor-etched porous GaAs

Energy Technology Data Exchange (ETDEWEB)

Smida, A.; Laatar, F. [Photovoltaic Laboratory, Centre for Research and Technology Energy, Tourist Route Soliman, BP 95, 2050 Hammam-Lif (Tunisia); Hassen, M., E-mail: mhdhassen@yahoo.fr [Photovoltaic Laboratory, Centre for Research and Technology Energy, Tourist Route Soliman, BP 95, 2050 Hammam-Lif (Tunisia); Higher Institute of Applied Science and Technology of Sousse, City Taffala (Ibn Khaldun), 4003 Sousse (Tunisia); Ezzaouia, H. [Photovoltaic Laboratory, Centre for Research and Technology Energy, Tourist Route Soliman, BP 95, 2050 Hammam-Lif (Tunisia)

2016-08-15

This paper consists to present first results concerning the structure of porous GaAs layer (por-GaAs-L) prepared by using HF/HNO{sub 3} as acidic solution in vapor etching (VE) method. In order to clarify this method, we detail here its principle and explain how por-GaAs-Ls are formed, taking into account the influencing of the exposure time of the GaAs substrate to the acid vapor. The etched GaAs layers have been investigated by UV–visible and PL analysis. One porous layer was performed to be characterised by Atomic Force Microscopy (AFM), FTIR spectroscopy, and X-Ray Diffraction (XRD). The porous structure was constituted by a nanocrystals with an average size about 6 nm. These nanocrystals were calculated from XRD peak using Scherrer's formula, AFM imaging, and also by using effective mass approximation model from effective band gap. - Highlights: • Porous GaAs layer was prepared by using Vapor etching (VE) method. • Effect of VE duration on the microstructural optical properties of the GaAs substrate • Porous structure of GaAs layer was demonstrated by using SEM and AFM microscopy.

Structural and optical properties of vapor-etched porous GaAs

International Nuclear Information System (INIS)

Smida, A.; Laatar, F.; Hassen, M.; Ezzaouia, H.

2016-01-01

This paper consists to present first results concerning the structure of porous GaAs layer (por-GaAs-L) prepared by using HF/HNO 3 as acidic solution in vapor etching (VE) method. In order to clarify this method, we detail here its principle and explain how por-GaAs-Ls are formed, taking into account the influencing of the exposure time of the GaAs substrate to the acid vapor. The etched GaAs layers have been investigated by UV–visible and PL analysis. One porous layer was performed to be characterised by Atomic Force Microscopy (AFM), FTIR spectroscopy, and X-Ray Diffraction (XRD). The porous structure was constituted by a nanocrystals with an average size about 6 nm. These nanocrystals were calculated from XRD peak using Scherrer's formula, AFM imaging, and also by using effective mass approximation model from effective band gap. - Highlights: • Porous GaAs layer was prepared by using Vapor etching (VE) method. • Effect of VE duration on the microstructural optical properties of the GaAs substrate • Porous structure of GaAs layer was demonstrated by using SEM and AFM microscopy.

Lighting emitting microstructures in porous silicon

International Nuclear Information System (INIS)

Squire, E.

1999-01-01

Experimental and theoretical techniques are used to examine microstructuring effects on the optical properties of single layer, multilayer, single and multiple microcavity structures fabricated from porous silicon. Two important issues regarding the effects of the periodic structuring of this material are discussed. Firstly, the precise role played by this microstructuring, given that the luminescence is distributed throughout the entire structure and the low porosity layers are highly absorbing at short wavelengths. The second issue examined concerns the observed effects on the optical spectra of the samples owing to the emission bandwidth of the material being greater than the optical stopband of the structure. Measurements of the reflectivity and photoluminescence spectra of different porous silicon microstructures are presented and discussed. The results are modelled using a transfer matrix technique. The matrix method has been modified to calculate the optical spectra of porous silicon specifically by accounting for the effects of dispersion, absorption and emission within the material. Layer thickness and porosity gradients have also been included in the model. The dielectric function of the two component layers (i.e. silicon and air) is calculated using the Looyenga formula. This approach can be adapted to suit other porous semiconductors if required. Examination of the experimental results have shown that the emitted light is strongly controlled by the optical modes of the structures. Furthermore, the data display an interplay of a wide variety of effects dependent upon the structural composition. Comparisons made between the experimental and calculated reflectivity and photoluminescence spectra of many different porous silicon microstructures show very good agreement. (author)

Porous silicon: Synthesis and optical properties

International Nuclear Information System (INIS)

Naddaf, M.; Awad, F.

2006-01-01

Formation of porous silicon by electrochemical etching method of both p and n-type single crystal silicon wafers in HF based solutions has been performed by using three different modes. In addition to DC and pulsed voltage, a novel etching mode is developed to prepare light-emitting porous silicon by applying and holding-up a voltage in gradient steps form periodically, between the silicon wafer and a graphite electrode. Under same equivalent etching conditions, periodic gradient steps voltage etching can yield a porous silicon layer with stronger photoluminescence intensity and blue shift than the porous silicon layer prepared by DC or pulsed voltage etching. It has been found that the holding-up of the applied voltage during the etching process for defined interval of time is another significant future of this method, which highly affects the blue shift. This can be used for tailoring a porous layer with novel properties. The actual mechanism behind the blue shift is not clear exactly, even the experimental observation of atomic force microscope and purist measurements in support with quantum confinement model. It has been seen also from Fourier Transform Infrared study that interplays between O-Si-H and Si-H bond intensities play key role in deciding the efficiency of photoluminescence emission. Study of relative humidity sensing and photonic crystal properties of pours silicon samples has confirmed the advantages of the new adopted etching mode. The sensitivity at room temperature of porous silicon prepared by periodic gradient steps voltage etching was found to be about 70% as compared to 51% and 45% for the porous silicon prepared by DC and pulsed voltage etching, respectively. (author)

Porous silicon: Synthesis and optical properties

International Nuclear Information System (INIS)

Naddaf, M.; Awad, F.

2006-06-01

Formation of porous silicon by electrochemical etching method of both p and n-type single crystal silicon wafers in HF based solutions has been performed by using three different modes. In addition to DC and pulsed voltage, a novel etching mode is developed to prepare light-emitting porous silicon by applying and holding-up a voltage in gradient steps form periodically, between the silicon wafer and a graphite electrode. Under same equivalent etching conditions, periodic gradient steps voltage etching can yield a porous silicon layer with stronger photoluminescence intensity and blue shift than the porous silicon layer prepared by DC or pulsed voltage etching. It has been found that the holding-up of the applied voltage during the etching process for defined interval of time is another significant future of this method, which highly affects the blue shift. This can be used for tailoring a porous layer with novel properties. The actual mechanism behind the blue shift is not clear exactly, even the experimental observation of atomic force microscope and purist measurements in support with quantum confinement model. It has been seen also from Fourier Transform Infrared study that interplays between O-Si-H and Si-H bond intensities play key role in deciding the efficiency of photoluminescence emission. Study of relative humidity sensing and photonic crystal properties of pours silicon samples has confirmed the advantages of the new adopted etching mode. The sensitivity at room temperature of porous silicon prepared by periodic gradient steps voltage etching was found to be about 70% as compared to 51% and 45% for the porous silicon prepared by DC and pulsed voltage etching, respectively. (author)

Structural analysis of anodic porous alumina used for resistive random access memory

International Nuclear Information System (INIS)

Lee, Jeungwoo; Nigo, Seisuke; Kato, Seiichi; Kitazawa, Hideaki; Kido, Giyuu; Nakano, Yoshihiro

2010-01-01

Anodic porous alumina with duplex layers exhibits a voltage-induced switching effect and is a promising candidate for resistive random access memory. The nanostructural analysis of porous alumina is important for understanding the switching effect. We investigated the difference between the two layers of an anodic porous alumina film using transmission electron microscopy and electron energy-loss spectroscopy. Diffraction patterns showed that both layers are amorphous, and the electron energy-loss spectroscopy indicated that the inner layer contains less oxygen than the outer layer. We speculate that the conduction paths are mostly located in the oxygen-depleted area.

Characterization of thermal, optical and carrier transport properties of porous silicon using the photoacoustic technique

International Nuclear Information System (INIS)

Sheng, Chan Kok; Mahmood Mat Yunus, W.; Yunus, Wan Md. Zin Wan; Abidin Talib, Zainal; Kassim, Anuar

2008-01-01

In this work, the porous silicon layer was prepared by the electrochemical anodization etching process on n-type and p-type silicon wafers. The formation of the porous layer has been identified by photoluminescence and SEM measurements. The optical absorption, energy gap, carrier transport and thermal properties of n-type and p-type porous silicon layers were investigated by analyzing the experimental data from photoacoustic measurements. The values of thermal diffusivity, energy gap and carrier transport properties have been found to be porosity-dependent. The energy band gap of n-type and p-type porous silicon layers was higher than the energy band gap obtained for silicon substrate (1.11 eV). In the range of porosity (50-76%) of the studies, our results found that the optical band-gap energy of p-type porous silicon (1.80-2.00 eV) was higher than that of the n-type porous silicon layer (1.70-1.86 eV). The thermal diffusivity value of the n-type porous layer was found to be higher than that of the p-type and both were observed to increase linearly with increasing layer porosity

Densification and grain growth during sintering of porous Ce0.9Gd0.1O1.95tape cast layers: A comprehensive study on heuristic methods

DEFF Research Database (Denmark)

Ni, De Wei; Schmidt, Cristine Grings; Teocoli, Francesca

2013-01-01

The sintering behavior of porous Ce0.9Gd0.1O1.95(CGO10) tape cast layers was systematically investigated to establish fundamental kinetic parameters associated to densification and grain growth. Densification and grain growth were characterized by a set of different methods to determine the domin...... and grain boundary mobility in the porous body was estimated around 10−18–10−16m3N−1s−1 at the investigated temperature range.© 2013 Elsevier Ltd. All rights reserved.......The sintering behavior of porous Ce0.9Gd0.1O1.95(CGO10) tape cast layers was systematically investigated to establish fundamental kinetic parameters associated to densification and grain growth. Densification and grain growth were characterized by a set of different methods to determine...... the dominant sintering mechanisms and kinetics, both in isothermal and at constant heating rate (iso-rate) conditions. Densification of porous CGO10 tape is thermally activated with typical activation energy which was estimated around 440–470 kJ mol−1. Grain growth showed similar thermal activation energy...

Silicon epitaxy on textured double layer porous silicon by LPCVD

International Nuclear Information System (INIS)

Cai Hong; Shen Honglie; Zhang Lei; Huang Haibin; Lu Linfeng; Tang Zhengxia; Shen Jiancang

2010-01-01

Epitaxial silicon thin film on textured double layer porous silicon (DLPS) was demonstrated. The textured DLPS was formed by electrochemical etching using two different current densities on the silicon wafer that are randomly textured with upright pyramids. Silicon thin films were then grown on the annealed DLPS, using low-pressure chemical vapor deposition (LPCVD). The reflectance of the DLPS and the grown silicon thin films were studied by a spectrophotometer. The crystallinity and topography of the grown silicon thin films were studied by Raman spectroscopy and SEM. The reflectance results show that the reflectance of the silicon wafer decreases from 24.7% to 11.7% after texturing, and after the deposition of silicon thin film the surface reflectance is about 13.8%. SEM images show that the epitaxial silicon film on textured DLPS exhibits random pyramids. The Raman spectrum peaks near 521 cm -1 have a width of 7.8 cm -1 , which reveals the high crystalline quality of the silicon epitaxy.

Porous silicon-based direct hydrogen sulphide fuel cells.

Science.gov (United States)

Dzhafarov, T D; Yuksel, S Aydin

2011-10-01

In this paper, the use of Au/porous silicon/Silicon Schottky type structure, as a direct hydrogen sulphide fuel cell is demonstrated. The porous silicon filled with hydrochlorid acid was developed as a proton conduction membrane. The Au/Porous Silicon/Silicon cells were fabricated by first creating the porous silicon layer in single-crystalline Si using the anodic etching under illumination and then deposition Au catalyst layer onto the porous silicon. Using 80 mM H2S solution as fuel the open circuit voltage of 0.4 V was obtained and maximum power density of 30 W/m2 at room temperature was achieved. These results demonstrate that the Au/Porous Silicon/Silicon direct hydrogen sulphide fuel cell which uses H2S:dH2O solution as fuel and operates at room temperature can be considered as the most promising type of low cost fuel cell for small power-supply units.

Building Honeycomb-Like Hollow Microsphere Architecture in a Bubble Template Reaction for High-Performance Lithium-Rich Layered Oxide Cathode Materials.

Science.gov (United States)

Chen, Zhaoyong; Yan, Xiaoyan; Xu, Ming; Cao, Kaifeng; Zhu, Huali; Li, Lingjun; Duan, Junfei

2017-09-13

In the family of high-performance cathode materials for lithium-ion batteries, lithium-rich layered oxides come out in front because of a high reversible capacity exceeding 250 mAh g -1 . However, the long-term energy retention and high energy densities for lithium-rich layered oxide cathode materials require a stable structure with large surface areas. Here we propose a "bubble template" reaction to build "honeycomb-like" hollow microsphere architecture for a Li 1.2 Mn 0.52 Ni 0.2 Co 0.08 O 2 cathode material. Our material is designed with ca. 8-μm-sized secondary particles with hollow and highly exposed porous structures that promise a large flexible volume to achieve superior structure stability and high rate capability. Our preliminary electrochemical experiments show a high capacity of 287 mAh g -1 at 0.1 C and a capacity retention of 96% after 100 cycles at 1.0 C. Furthermore, the rate capability is superior without any other modifications, reaching 197 mAh g -1 at 3.0 C with a capacity retention of 94% after 100 cycles. This approach may shed light on a new material engineering for high-performance cathode materials.

Multilayer porous UHMWPE scaffolds for bone defects replacement.

Science.gov (United States)

Maksimkin, A V; Senatov, F S; Anisimova, N Yu; Kiselevskiy, M V; Zalepugin, D Yu; Chernyshova, I V; Tilkunova, N A; Kaloshkin, S D

2017-04-01

Reconstruction of the structural integrity of the damaged bone tissue is an urgent problem. UHMWPE may be potentially used for the manufacture of porous implants simulating as closely as possible the porous cancellous bone tissue. But the extremely high molecular weight of the polymer does not allow using traditional methods of foaming. Porous and multilayer UHMWPE scaffolds with nonporous bulk layer and porous layer that mimics cancellous bone architecture were obtained by solid-state mixing, thermopressing and washing in subcritical water. Structural and mechanical properties of the samples were studied. Porous UHMWPE samples were also studied in vitro and in vivo. The pores of UHMWPE scaffold are open and interconnected. Volume porosity of the obtained samples was 79±2%; the pore size range was 80-700μm. Strong connection of the two layers in multilayer UHMWPE scaffolds was observed with decreased number of fusion defects. Functionality of implants based on multilayer UHMWPE scaffolds is provided by the fixation of scaffolds in the bone defect through ingrowths of the connective tissue into the pores, which ensures the maintenance of the animals' mobility. Copyright © 2016 Elsevier B.V. All rights reserved.

Polyhedral-Like NiMn-Layered Double Hydroxide/Porous Carbon as Electrode for Enhanced Electrochemical Performance Supercapacitors.

Science.gov (United States)

Yu, Mei; Liu, Ruili; Liu, Jianhua; Li, Songmei; Ma, Yuxiao

2017-11-01

Polyhedral-like NiMn-layered double hydroxide/porous carbon (NiMn-LDH/PC-x) composites are successfully synthesized by hydrothermal method (x = 1, 2 means different mass percent of porous carbon (PC) in composites). The NiMn-LDH/PC-1 composites possess specific capacitance 1634 F g -1 at a current density of 1 A g -1 , and it is much better than that of pure LDH (1095 F g -1 at 1 A g -1 ). Besides, the sample can retain 84.58% of original capacitance after 3000 cycles at 15 A g -1 . An asymmetric supercapacitor with NiMn-LDH/PC-1 as anode and activated carbon as cathode is fabricated, and the supercapacitor can achieve an energy density of 18.60 Wh kg -1 at a power density of 225.03 W kg -1 . The enhanced electrochemical performance attributes to the high faradaic pseudocapacitance of NiMn-LDH, the introduction of PC, and the 3D porous structure of LDH/PC-1 composites. The introduction of PC hinders serious agglomeration of LDH and further accelerates ions transport. The encouraging results indicate that these materials are one of the most potential candidates for energy storage devices. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Graphene synthesized on porous silicon for active electrode material of supercapacitors

Science.gov (United States)

Su, B. B.; Chen, X. Y.; Halvorsen, E.

2016-11-01

We present graphene synthesized by chemical vapour deposition under atmospheric pressure on both porous nanostructures and flat wafers as electrode scaffolds for supercapacitors. A 3nm thin gold layer was deposited on samples of both porous and flat silicon for exploring the catalytic influence during graphene synthesis. Micro-four-point probe resistivity measurements revealed that the resistivity of porous silicon samples was nearly 53 times smaller than of the flat silicon ones when all the samples were covered by a thin gold layer after the graphene growth. From cyclic voltammetry, the average specific capacitance of porous silicon coated with gold was estimated to 267 μF/cm2 while that without catalyst layer was 145μF/cm2. We demonstrated that porous silicon based on nanorods can play an important role in graphene synthesis and enable silicon as promising electrodes for supercapacitors.

Porosity-dependent fractal nature of the porous silicon surface

Energy Technology Data Exchange (ETDEWEB)

Rahmani, N.; Dariani, R. S., E-mail: dariani@alzahra.ac.ir [Department of Physics, Alzahra University, Tehran, 1993893973 (Iran, Islamic Republic of)

2015-07-15

Porous silicon films with porosity ranging from 42% to 77% were fabricated by electrochemical anodization under different current density. We used atomic force microscopy and dynamic scaling theory for deriving the surface roughness profile and processing the topography of the porous silicon layers, respectively. We first compared the topography of bare silicon surface with porous silicon and then studied the effect of the porosity of porous silicon films on their scaling behavior by using their self-affinity nature. Our work demonstrated that silicon compared to the porous silicon films has the highest Hurst parameter, indicating that the formation of porous layer due to the anodization etching of silicon surface leads to an increase of its roughness. Fractal analysis revealed that the evolution of the nanocrystallites’ fractal dimension along with porosity. Also, we found that both interface width and Hurst parameter are affected by the increase of porosity.

Electrochemical Method of Making Porous Particles Using a Constant Current Density

Science.gov (United States)

Ferrari, Mauro (Inventor); Liu, Xuewu (Inventor); Cheng, Ming-Cheng (Inventor)

2014-01-01

Provided is a particle that includes a first porous region and a second porous region that differs from the first porous region. Also provided is a particle that has a wet etched porous region and that does have a nucleation layer associated with wet etching. Methods of making porous particles are also provided.

Graphene synthesized on porous silicon for active electrode material of supercapacitors

International Nuclear Information System (INIS)

Su, B B; Chen, X Y; Halvorsen, E

2016-01-01

We present graphene synthesized by chemical vapour deposition under atmospheric pressure on both porous nanostructures and flat wafers as electrode scaffolds for supercapacitors. A 3nm thin gold layer was deposited on samples of both porous and flat silicon for exploring the catalytic influence during graphene synthesis. Micro-four-point probe resistivity measurements revealed that the resistivity of porous silicon samples was nearly 53 times smaller than of the flat silicon ones when all the samples were covered by a thin gold layer after the graphene growth. From cyclic voltammetry, the average specific capacitance of porous silicon coated with gold was estimated to 267 μF/cm 2 while that without catalyst layer was 145μF/cm 2 . We demonstrated that porous silicon based on nanorods can play an important role in graphene synthesis and enable silicon as promising electrodes for supercapacitors. (paper)

Refractive index contrast in porous silicon multilayers

Energy Technology Data Exchange (ETDEWEB)

Nava, R.; Mora, M.B. de la; Tagueena-Martinez, J. [Centro de Investigacion en Energia, Universidad Nacional Autonoma de Mexico, Temixco, Morelos (Mexico); Rio, J.A. del [Centro de Investigacion en Energia, Universidad Nacional Autonoma de Mexico, Temixco, Morelos (Mexico); Centro Morelense de Innovacion y Transferencia Tecnologica, Consejo de Ciencia y Tecnologia del Estado de Morelos (Mexico)

2009-07-15

Two of the most important properties of a porous silicon multilayer for photonic applications are flat interfaces and a relative large refractive index contrast between layers in the optical wavelength range. In this work, we studied the effect of the current density and HF electrolyte concentration on the refractive index of porous silicon. With the purpose of increasing the refractive index contrast in a multilayer, the refractive index of porous silicon produced at low current was studied in detail. The current density applied to produce the low porosity layers was limited in order to keep the electrolyte flow through the multilayer structure and to avoid deformation of layer interfaces. We found that an electrolyte composed of hydrofluoric acid, ethanol and glycerin in a ratio of 3:7:1 gives a refractive index contrast around 1.3/2.8 at 600 nm. Several multilayer structures with this refractive index contrast were fabricated, such as dielectric Bragg mirrors and microcavities. Reflectance spectra of the structures show the photonic quality of porous silicon multilayers produced under these electrochemical conditions. (copyright 2009 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Porous silicon technology for integrated microsystems

Science.gov (United States)

Wallner, Jin Zheng

With the development of micro systems, there is an increasing demand for integrable porous materials. In addition to those conventional applications, such as filtration, wicking, and insulating, many new micro devices, including micro reactors, sensors, actuators, and optical components, can benefit from porous materials. Conventional porous materials, such as ceramics and polymers, however, cannot meet the challenges posed by micro systems, due to their incompatibility with standard micro-fabrication processes. In an effort to produce porous materials that can be used in micro systems, porous silicon (PS) generated by anodization of single crystalline silicon has been investigated. In this work, the PS formation process has been extensively studied and characterized as a function of substrate type, crystal orientation, doping concentration, current density and surfactant concentration and type. Anodization conditions have been optimized for producing very thick porous silicon layers with uniform pore size, and for obtaining ideal pore morphologies. Three different types of porous silicon materials: meso porous silicon, macro porous silicon with straight pores, and macro porous silicon with tortuous pores, have been successfully produced. Regular pore arrays with controllable pore size in the range of 2mum to 6mum have been demonstrated as well. Localized PS formation has been achieved by using oxide/nitride/polysilicon stack as masking materials, which can withstand anodization in hydrofluoric acid up to twenty hours. A special etching cell with electrolytic liquid backside contact along with two process flows has been developed to enable the fabrication of thick macro porous silicon membranes with though wafer pores. For device assembly, Si-Au and In-Au bonding technologies have been developed. Very low bonding temperature (˜200°C) and thick/soft bonding layers (˜6mum) have been achieved by In-Au bonding technology, which is able to compensate the potentially

Fabricating porous silicon carbide

Science.gov (United States)

Shor, Joseph S. (Inventor); Kurtz, Anthony D. (Inventor)

1994-01-01

The formation of porous SiC occurs under electrochemical anodization. A sample of SiC is contacted electrically with nickel and placed into an electrochemical cell which cell includes a counter electrode and a reference electrode. The sample is encapsulated so that only a bare semiconductor surface is exposed. The electrochemical cell is filled with an HF electrolyte which dissolves the SiC electrochemically. A potential is applied to the semiconductor and UV light illuminates the surface of the semiconductor. By controlling the light intensity, the potential and the doping level, a porous layer is formed in the semiconductor and thus one produces porous SiC.

Hierarchically porous graphene in natural graphitic globules from silicate magmatic rocks

OpenAIRE

PONOMARCHUK V.A.; TITOV A.T.; MOROZ T.N.; PYRYAEV A.N.; PONOMARCHUK A.V.

2014-01-01

Naturally-occurring nanostructured graphites from silicate magmatic rocks, which are rare, were characterized using electron microscope and X-ray spectroscopy. This graphite consists of porous carbon, nanographite layers, microand nanotubes. The porous carbon is classified as macroporous matter with a small amount of mezopores. Evidence for the unusual properties of porous carbon are given: nanographite layers are created at the exposed surface of sample and the nanotubes occurs in the bulk o...

Combustion Characteristics of Butane Porous Burner for Thermoelectric Power Generation

Directory of Open Access Journals (Sweden)

K. F. Mustafa

2015-01-01

Full Text Available The present study explores the utilization of a porous burner for thermoelectric power generation. The porous burner was tested with butane gas using two sets of configurations: single layer porcelain and a stacked-up double layer alumina and porcelain. Six PbSnTe thermoelectric (TE modules with a total area of 54 cm2 were attached to the wall of the burner. Fins were also added to the cold side of the TE modules. Fuel-air equivalence ratio was varied between the blowoff and flashback limit and the corresponding temperature, current-voltage, and emissions were recorded. The stacked-up double layer negatively affected the combustion efficiency at an equivalence ratio of 0.20 to 0.42, but single layer porcelain shows diminishing trend in the equivalence ratio of 0.60 to 0.90. The surface temperature of a stacked-up porous media is considerably higher than the single layer. Carbon monoxide emission is independent for both porous media configurations, but moderate reduction was recorded for single layer porcelain at lean fuel-air equivalence ratio. Nitrogen oxides is insensitive in the lean fuel-air equivalence ratio for both configurations, even though slight reduction was observed in the rich region for single layer porcelain. Power output was found to be highly dependent on the temperature gradient.

Influence of thin porous Al2O3 layer on aluminum cathode to the Hα line shape in glow discharge

International Nuclear Information System (INIS)

Steflekova, V.; Sisovic, N. M.; Konjevic, N.

2009-01-01

The results of the Balmer alfa line shape study in a plane cathode-hollow anode Grimm discharge with aluminum (Al) cathode covered with thin layer of porous Al 2 O 3 are presented. The comparison with same line profile recorded with pure Al cathode shows lack of excessive Doppler broadened line wings, which are always detected in glow discharge with metal cathode. The effect is explained by the lack of strong electric field in the cathode sheath region, which is missing in the presence of thin oxide layer in, so called, spray discharge.

Porous nitrogen-enriched carbonaceous material from marine waste: chitosan-derived layered CNX catalyst for aerial oxidation of 5-hydroxymethylfurfural (HMF) to 2,5-furandicarboxylic acid

Data.gov (United States)

U.S. Environmental Protection Agency — Chitosan-derived, porous and layered nitrogen-enriched carbonaceous CNx catalyst (PLCNx) has been synthesized from marine waste and its use demonstrated in a...

High-density oxidized porous silicon

International Nuclear Information System (INIS)

Gharbi, Ahmed; Souifi, Abdelkader; Remaki, Boudjemaa; Halimaoui, Aomar; Bensahel, Daniel

2012-01-01

We have studied oxidized porous silicon (OPS) properties using Fourier transform infraRed (FTIR) spectroscopy and capacitance–voltage C–V measurements. We report the first experimental determination of the optimum porosity allowing the elaboration of high-density OPS insulators. This is an important contribution to the research of thick integrated electrical insulators on porous silicon based on an optimized process ensuring dielectric quality (complete oxidation) and mechanical and chemical reliability (no residual pores or silicon crystallites). Through the measurement of the refractive indexes of the porous silicon (PS) layer before and after oxidation, one can determine the structural composition of the OPS material in silicon, air and silica. We have experimentally demonstrated that a porosity approaching 56% of the as-prepared PS layer is required to ensure a complete oxidation of PS without residual silicon crystallites and with minimum porosity. The effective dielectric constant values of OPS materials determined from capacitance–voltage C–V measurements are discussed and compared to FTIR results predictions. (paper)

Multilayer porous UHMWPE scaffolds for bone defects replacement

International Nuclear Information System (INIS)

Maksimkin, A.V.; Senatov, F.S.; Anisimova, N.Yu.; Kiselevskiy, M.V.; Zalepugin, D.Yu.; Chernyshova, I.V.; Tilkunova, N.A.; Kaloshkin, S.D.

2017-01-01

Reconstruction of the structural integrity of the damaged bone tissue is an urgent problem. UHMWPE may be potentially used for the manufacture of porous implants simulating as closely as possible the porous cancellous bone tissue. But the extremely high molecular weight of the polymer does not allow using traditional methods of foaming. Porous and multilayer UHMWPE scaffolds with nonporous bulk layer and porous layer that mimics cancellous bone architecture were obtained by solid-state mixing, thermopressing and washing in subcritical water. Structural and mechanical properties of the samples were studied. Porous UHMWPE samples were also studied in vitro and in vivo. The pores of UHMWPE scaffold are open and interconnected. Volume porosity of the obtained samples was 79 ± 2%; the pore size range was 80–700 μm. Strong connection of the two layers in multilayer UHMWPE scaffolds was observed with decreased number of fusion defects. Functionality of implants based on multilayer UHMWPE scaffolds is provided by the fixation of scaffolds in the bone defect through ingrowths of the connective tissue into the pores, which ensures the maintenance of the animals' mobility - Highlights: • Porous UHMWPE scaffold mimics cancellous bone architecture, maintaining its flexibility. • Multilayer UHMWPE scaffold is able to simulate different types of bone tissue. • Fixation of scaffolds in the bone provides through ingrowths of the connective tissue into pores. • Multilayer UHMWPE scaffolds can be used for the formation of bone implants.

Multilayer porous UHMWPE scaffolds for bone defects replacement

Energy Technology Data Exchange (ETDEWEB)

Maksimkin, A.V. [National University of Science and Technology “MISIS”, Moscow (Russian Federation); Senatov, F.S., E-mail: senatov@misis.ru [National University of Science and Technology “MISIS”, Moscow (Russian Federation); Anisimova, N.Yu.; Kiselevskiy, M.V. [National University of Science and Technology “MISIS”, Moscow (Russian Federation); N.N. Blokhin Russian Cancer Research Center, Moscow (Russian Federation); Zalepugin, D.Yu.; Chernyshova, I.V.; Tilkunova, N.A. [State Plant of Medicinal Drugs, Moscow (Russian Federation); Kaloshkin, S.D. [National University of Science and Technology “MISIS”, Moscow (Russian Federation)

2017-04-01

Reconstruction of the structural integrity of the damaged bone tissue is an urgent problem. UHMWPE may be potentially used for the manufacture of porous implants simulating as closely as possible the porous cancellous bone tissue. But the extremely high molecular weight of the polymer does not allow using traditional methods of foaming. Porous and multilayer UHMWPE scaffolds with nonporous bulk layer and porous layer that mimics cancellous bone architecture were obtained by solid-state mixing, thermopressing and washing in subcritical water. Structural and mechanical properties of the samples were studied. Porous UHMWPE samples were also studied in vitro and in vivo. The pores of UHMWPE scaffold are open and interconnected. Volume porosity of the obtained samples was 79 ± 2%; the pore size range was 80–700 μm. Strong connection of the two layers in multilayer UHMWPE scaffolds was observed with decreased number of fusion defects. Functionality of implants based on multilayer UHMWPE scaffolds is provided by the fixation of scaffolds in the bone defect through ingrowths of the connective tissue into the pores, which ensures the maintenance of the animals' mobility - Highlights: • Porous UHMWPE scaffold mimics cancellous bone architecture, maintaining its flexibility. • Multilayer UHMWPE scaffold is able to simulate different types of bone tissue. • Fixation of scaffolds in the bone provides through ingrowths of the connective tissue into pores. • Multilayer UHMWPE scaffolds can be used for the formation of bone implants.

Preparation of hierarchical porous carbon from waste printed circuit boards for high performance electric double-layer capacitors

Science.gov (United States)

Du, Xuan; Wang, Li; Zhao, Wei; Wang, Yi; Qi, Tao; Li, Chang Ming

2016-08-01

Renewable clean energy and resources recycling have become inevitable choices to solve worldwide energy shortages and environmental pollution problems. It is a great challenge to recycle tons of waste printed circuit boards (PCB) produced every year for clean environment while creating values. In this work, low cost, high quality activated carbons (ACs) were synthesized from non-metallic fractions (NMF) of waste PCB to offer a great potential for applications of electrochemical double-layer capacitors (EDLCs). After recovering metal from waste PCB, hierarchical porous carbons were produced from NMF by carbonization and activation processes. The experimental results exhibit that some pores were formed after carbonization due to the escape of impurity atoms introduced by additives in NMF. Then the pore structure was further tailored by adjusting the activation parameters. Roles of micropores and non-micropores in charge storage were investigated when the hierarchical porous carbons were applied as electrode of EDLCs. The highest specific capacitance of 210 F g-1 (at 50 mA g-1) and excellent rate capability were achieved when the ACs possessing a proper micropores/non-micropores ratio. This work not only provides a promising method to recycle PCB, but also investigates the structure tailoring arts for a rational hierarchical porous structure in energy storage/conversion.

Optical and structural properties of protein/gold hybrid bio-nanofilms prepared by layer-by-layer method.

Science.gov (United States)

Pál, Edit; Hornok, Viktória; Sebok, Dániel; Majzik, Andrea; Dékány, Imre

2010-08-01

Lysozyme/gold thin layers were prepared by layer-by-layer (LbL) self-assembly method. The build-up of the films was followed by UV-vis-absorbance spectra, quartz crystal microbalance (QCM) and surface plasmon resonance (SPR) techniques. The structural property of films was examined by X-ray diffraction (XRD) measurements, while their morphology was studied by scanning electron microscopy (SEM) and atomic force microscopy (AFM). It was found that gold nanoparticles (NPs) had cubic crystalline structure, the primary particles form aggregates in the thin layer due to the presence of lysozyme molecules. The UV-vis measurements prove change in particle size while the colour of the film changes from wine-red to blue. The layer thickness of films was determined using the above methods and the loose, porous structure of the films explains the difference in the results. The vapour adsorption property of hybrid layers was also studied by QCM using different saturated vapours and ammonia gas. The lysozyme/Au films were most sensitive for ammonia gas among the tested gases/vapours due to the strongest interaction between the functional groups of the protein. Copyright 2010 Elsevier B.V. All rights reserved.

Preparation and Oxygen Permeability of BaCo0.7Fe0.2Nb0.1O3-δ Membrane Modified by Ce0.8Y0.2O2-δ Porous Layer on the Air Side

Directory of Open Access Journals (Sweden)

Yuan Qiang

2013-01-01

Full Text Available BaCo0.7Fe0.2Nb0.1O3−δ (BCFN dense ceramic membrane with submicron-Ce0.8Y0.2O2−δ (YDC porous layer was investigated by the partial oxidation of coke oven gas (COG in hydrogen production. XRD analysis showed this composite had good stability and no chemical reaction at high temperature. SEM and TEM characterization further showed BCFN membrane was uniformly modified by YDC porous layer (about 5~6 μm thickness formed by the accumulation of relative nanoparticles. At the respective COG flux and air flux of 108 mL/min and 173 mL/min, the oxygen permeation flux of BCFN modified by submicron-YDC porous layer reached 16.62 mL·min−1·cm−2, which was about 23.5% higher than that of pure BCFN membrane. Therefore, submicron-YDC porous layer obviously improved the oxygen permeation flux of BCFN membrane and its stability at 875°C.

Time resolved analysis of water drainage in porous asphalt concrete using neutron radiography.

Science.gov (United States)

Poulikakos, L D; Sedighi Gilani, M; Derome, D; Jerjen, I; Vontobel, P

2013-07-01

Porous asphalt as a road surface layer controls aquaplaning as rain water can drain through its highly porous structure. The process of water drainage through this permeable layer is studied using neutron radiography. Time-resolved water configuration and distribution within the porous structure are reported. It is shown that radiography depicts the process of liquid water transport within the complex geometry of porous asphalt, capturing water films, filled dead end pores and water islands. Copyright © 2013 Elsevier Ltd. All rights reserved.

Electron beam selectively seals porous metal filters

Science.gov (United States)

Snyder, J. A.; Tulisiak, G.

1968-01-01

Electron beam welding selectively seals the outer surfaces of porous metal filters and impedances used in fluid flow systems. The outer surface can be sealed by melting a thin outer layer of the porous material with an electron beam so that the melted material fills all surface pores.

POROUS-MASTIC ASPHALT-CONCRETE MIXTURES AND THEIR UTILIZATION HISTORY

Directory of Open Access Journals (Sweden)

Khudokonenko Anton Aleksandrovich

2017-11-01

Full Text Available Subject: a rapid increase in the traffic intensity and freight traffic on motor roads leads to premature destruction of road surfaces. At the same time, the actual service life of asphalt-concrete pavements rarely exceeds 4-5 years and in most cases is only 2-3 years. Most intensively defects and fractures appear on asphalt-concrete pavements in the early spring. Nowadays the overhaul intervals for the road surface coverings are significantly lower than those given by the regulatory requirements. One of the main reasons for this phenomenon is the use of obsolete technologies based on traditional materials whose properties are inadequate to resist stresses and deformations arising in the coating. This is especially evident in the climatic conditions of the south of the European part of Russia, where the upper layers of the roadway experience a much wider range of temperatures. Tighter requirements for the initial road-building materials and timely repair of the coatings allow us to increase the service life of motor roads. Research objectives: the aim of the study is to develop a new type of asphalt-concrete, such as porous-mastic one. Materials and methods: the work was carried out based on observations and published sources, a method of theoretical study and analysis. Results: the domestic and foreign experience of using the given asphalt concrete for the top layer of the coating was considered. The technology of preparation and laying of a porous-mastic asphalt-concrete mixture is presented and its advantages and disadvantages are shown. Conclusions: increasing the longevity of highways is an important and urgent task and it can be solved, in particular, due to the wide use of new technologies and non-traditional building materials that allow us to improve the quality of asphalt-concrete pavement and prolong its overhaul intervals.

Flexible single-layer ionic organic-inorganic frameworks towards precise nano-size separation

Science.gov (United States)

Yue, Liang; Wang, Shan; Zhou, Ding; Zhang, Hao; Li, Bao; Wu, Lixin

2016-02-01

Consecutive two-dimensional frameworks comprised of molecular or cluster building blocks in large area represent ideal candidates for membranes sieving molecules and nano-objects, but challenges still remain in methodology and practical preparation. Here we exploit a new strategy to build soft single-layer ionic organic-inorganic frameworks via electrostatic interaction without preferential binding direction in water. Upon consideration of steric effect and additional interaction, polyanionic clusters as connection nodes and cationic pseudorotaxanes acting as bridging monomers connect with each other to form a single-layer ionic self-assembled framework with 1.4 nm layer thickness. Such soft supramolecular polymer frameworks possess uniform and adjustable ortho-tetragonal nanoporous structure in pore size of 3.4-4.1 nm and exhibit greatly convenient solution processability. The stable membranes maintaining uniform porous structure demonstrate precisely size-selective separation of semiconductor quantum dots within 0.1 nm of accuracy and may hold promise for practical applications in selective transport, molecular separation and dialysis systems.

Single layer porous gold films grown at different temperatures

International Nuclear Information System (INIS)

Zhang Renyun; Hummelgard, Magnus; Olin, Hakan

2010-01-01

Large area porous gold films can be used in several areas including electrochemical electrodes, as an essential component in sensors, or as a conducting material in electronics. Here, we report on evaporation induced crystal growth of large area porous gold films at 20, 40 and 60 deg. C. The gold films were grown on liquid surface at 20 deg. C, while the films were grown on the wall of beakers when temperature increased to 40 and 60 deg. C. The porous gold films consisted of a dense network of gold nanowires as characterized by TEM and SEM. TEM diffraction results indicated that higher temperature formed larger crystallites of gold wires. An in situ TEM imaging of the coalescence of gold nanoparticles mimicked the process of the growth of these porous films, and a plotting of the coalescence time and the neck radius showed a diffusion process. The densities of these gold films were also characterized by transmittance, and the results showed film grown at 20 deg. C had the highest density, while the film grown at 60 deg. C had the lowest consistent with SEM and TEM characterization. Electrical measurements of these gold films showed that the most conductive films were the ones grown at 40 deg. C. The conductivities of the gold films were related to the amount of contamination, density and the diameter of the gold nanowires in the films. In addition, a gold film/gold nanoparticle hybrid was made, which showed a 10% decrease in transmittance during hybridization, pointing to applications as chemical and biological sensors.

Facile synthesis and electrochemical properties of continuous porous spheres assembled from defect-rich, interlayer-expanded, and few-layered MoS2/C nanosheets for reversible lithium storage

Science.gov (United States)

Chen, Biao; Lu, Huihui; Zhao, Naiqin; Shi, Chunsheng; Liu, Enzuo; He, Chunnian; Ma, Liying

2018-05-01

Hollow or continuous porous hierarchical MoS2/C structures with large Li-ion and electron transport kinetics, and high structural stability are urgent needs for their application in lithium ion batteries. In this regard, a novel continuous porous micro-sphere constructed from defect-rich, interlayer-expanded, and few-layered MoS2/C nanosheets is successfully synthesized through a facile one-pot hydrothermal method. The polyvinyl pyrrolidone surfactant serves as carbon source and supporter, while the CS2 works as soft template and sulfur source during hydrothermal process. The morphologies, structures, and electrochemical properties are systematically characterized. Importantly, it should be noted that the unique porous micro-spheres with merits of rich-defect, expanded-interlayer, few-layer (integrating carbon are favorable for lithium ion batteries application. When the uniform composites are used as lithium ion batteries anode materials, they deliver a high reversible capacity, excellent cycling performance (average capacity fading of 0.037% per cycle at 0.2 A g-1), and good rate capability.

Effect of gamma irradiation on the photoluminescence of porous silicon

Energy Technology Data Exchange (ETDEWEB)

Elistratova, M. A., E-mail: Marina.Elistratova@mail.ioffe.ru; Romanov, N. M. [Peter the Great St. Petersburg Polytechnic University (Russian Federation); Goryachev, D. N. [Russian Academy of Sciences, Ioffe Institute (Russian Federation); Zakharova, I. B. [Peter the Great St. Petersburg Polytechnic University (Russian Federation); Sreseli, O. M. [Russian Academy of Sciences, Ioffe Institute (Russian Federation)

2017-04-15

The effect of gamma irradiation on the luminescence properties of porous silicon produced by the electrochemical technique is studied. Changes in the photoluminescence intensity between irradiation doses and over a period of several days after the last irradiation are recorded. The quenching of photoluminescence at low irradiation doses and recovery after further irradiation are registered. It is found that porous silicon is strongly oxidized after gamma irradiation and the oxidation process continues for several days after irradiation. It is conceived that the change in the photoluminescence spectra and intensity of porous silicon after gamma irradiation is caused by a change in the passivation type of the porous surface: instead of hydrogen passivation, more stable oxygen passivation is observed. To stabilize the photoluminescence spectra of porous silicon, the use of fullerenes is proposed. No considerable changes in the photoluminescence spectra during irradiation and up to 18 days after irradiation are detected in a porous silicon sample with a thermally deposited fullerene layer. It is shown that porous silicon samples with a deposited C{sub 60} layer are stable to gamma irradiation and oxidation.

New Porous Material Made from Industrial and Municipal Waste for Building Application

Directory of Open Access Journals (Sweden)

Diana BAJARE

2014-09-01

Full Text Available The aim of this study was to find a new method for usage of the hazardous waste coming from recycling industry. Two hazardous wastes – aluminium recycling final dross or non-metallic product (NMP and lead – silica glass (LSG were investigated. It is generally considered that NMP is a process waste and subject to disposal after residual metal has been recovered from primary dross. NMP is impurities which are removed from the molten metal in dross recycling process and it could be defined as a hazardous waste product in aluminium recycling industry. LSG comes from fluorescence lamp recycling plant and could be classified as hazardous waste due to high amount of lead in the composition and re-melting problems. The new alkali activated material, which can be defined as porous building material, was created. Composition of this material consisted of aluminium recycling waste, recycled fluorescent lamp LSG, sintered kaolin clay as well as commercially available alkali flakes (NaOH and liquid glass (Na2SiO3 + nH2O. Physical and mechanical properties of the obtained material were tested. Density of the obtained material was from (460 – 550 kg/m3 and the total porosity was from 82 % – 83 %. The compressive strength of the material was in range from 1.1 MPa to 2.3 MPa. The thermal conductivity was determined. The pore microstructure was investigated and the mineralogical composition of porous material was determined. DOI: http://dx.doi.org/10.5755/j01.ms.20.3.4330

Porous Hybrid Composites of Few-Layer MoS2 Nanosheets Embedded in a Carbon Matrix with an Excellent Supercapacitor Electrode Performance.

Science.gov (United States)

Ji, Hongmei; Liu, Chao; Wang, Ting; Chen, Jing; Mao, Zhengning; Zhao, Jin; Hou, Wenhua; Yang, Gang

2015-12-22

Porous hierarchical architectures of few-layer MoS2 nanosheets dispersed in carbon matrix are prepared by a microwave-hydrothermal method followed by annealing treatment via using glucose as C source and structure-directing agent and (NH4 )2 MoS4 as both Mo and S sources. It is found that the morphology and size of the secondary building units (SBUs), the size and layer number of MoS2 nanosheets as well as the distribution of MoS2 nanosheets in carbon matrix, can be effectively controlled by simply adjusting the molar ratio of (NH4 )2 MoS4 to glucose, leading to the materials with a low charge-transfer resistance, many electrochemical active sites and a robust structure for an outstanding energy storage performance including a high specific capacitance (589 F g(-1) at 0.5 A g(-1) ), a good rate capability (364 F g(-1) at 20 A g(-1) ), and an excellent cycling stability (retention 104% after 2000 cycles) for application in supercapacitors. The exceptional rate capability endows the electrode with a high energy density of 72.7 Wh kg(-1) and a high power density of 12.0 kW kg(-1) simultaneously. This work presents a facile and scalable approach for synthesizing novel heterostructures of MoS2 -based electrode materials with an enhanced rate capability and cyclability for potential application in supercapacitor. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Preparation of freestanding GaN wafer by hydride vapor phase epitaxy on porous silicon

Science.gov (United States)

Wu, Xian; Li, Peng; Liang, Renrong; Xiao, Lei; Xu, Jun; Wang, Jing

2018-05-01

A freestanding GaN wafer was prepared on porous Si (111) substrate using hydride vapor phase epitaxy (HVPE). To avoid undesirable effects of the porous surface on the crystallinity of the GaN, a GaN seed layer was first grown on the Si (111) bare wafer. A pattern with many apertures was fabricated in the GaN seed layer using lithography and etching processes. A porous layer was formed in the Si substrate immediately adjacent to the GaN seed layer by an anodic etching process. A 500-μm-thick GaN film was then grown on the patterned GaN seed layer using HVPE. The GaN film was separated from the Si substrate through the formation of cracks in the porous layer caused by thermal mismatch stress during the cooling stage of the HVPE. Finally, the GaN film was polished to obtain a freestanding GaN wafer.

Preparation of porous carbon sphere from waste sugar solution for electric double-layer capacitor

Science.gov (United States)

Hao, Zhi-Qiang; Cao, Jing-Pei; Wu, Yan; Zhao, Xiao-Yan; Zhuang, Qi-Qi; Wang, Xing-Yong; Wei, Xian-Yong

2017-09-01

Waste sugar solution (WSS), which contains abundant 2-keto-L-gulonic acid, is harmful to the environment if discharged directly. For value-added utilization of the waste resource, a novel process is developed for preparation of porous carbon spheres by hydrothermal carbonization (HTC) of WSS followed by KOH activation. Additionally, the possible preparation mechanism of carbon spheres is proposed. The effects of hydrothermal and activation parameters on the properties of the carbon sphere are also investigated. The carbon sphere is applied to electric double-layer capacitor and its electrochemical performance is studied. These results show that the carbon sphere obtained by HTC at 180 °C for 12 h with the WSS/deionized water volume ratio of 2/3 possess the highest specific capacitance under identical activation conditions. The specific capacitance of the carbon spheres can reach 296.1 F g-1 at a current density of 40 mA g-1. Besides, excellent cycle life and good capacitance retention (89.6%) are observed at 1.5 A g-1 after 5000 cycles. This study not only provides a facile and potential method for the WSS treatment, but also achieves the high value-added recycling of WSS for the preparation of porous carbon spheres with superior electrochemical properties.

A method for the densification of ceramic layers, especially ceramic layers within solid oxide cell (SOC) technology, and products obtained by the method

DEFF Research Database (Denmark)

2013-01-01

A ceramic layer, especially for use in solid oxide cell (SOC) technology, is densified in a method comprising (a) providing a multilayer system by depositing the porous ceramic layer, which is to be densified, onto the selected system of ceramic layers on a support, (b) pre-sintering the resulting......(s) in the porous layer surface and (e) performing a thermal treatment at a temperature T2, where T2 > ?1, to obtain densification of and grain growth in the porous layer formed in step (b). The method makes it possible to obtain dense ceramic layers at temperatures, which are compatible with the other materials...... present in a ceramic multilayer system....

Porous Gold Films Fabricated by Wet-Chemistry Processes

Directory of Open Access Journals (Sweden)

Aymeric Pastre

2016-01-01

Full Text Available Porous gold films presented in this paper are formed by combining gold electroless deposition and polystyrene beads templating methods. This original approach allows the formation of conductive films (2 × 106 (Ω·cm−1 with tailored and interconnected porosity. The porous gold film was deposited up to 1.2 μm on the silicon substrate without delamination. An original zirconia gel matrix containing gold nanoparticles deposited on the substrate acts both as an adhesion layer through the creation of covalent bonds and as a seed layer for the metallic gold film growth. Dip-coating parameters and gold electroless deposition kinetics have been optimized in order to create a three-dimensional network of 20 nm wide pores separated by 20 nm thick continuous gold layers. The resulting porous gold films were characterized by GIXRD, SEM, krypton adsorption-desorption, and 4-point probes method. The process is adaptable to different pore sizes and based on wet-chemistry. Consequently, the porous gold films presented in this paper can be used in a wide range of applications such as sensing, catalysis, optics, or electronics.

Current-voltage characteristics of porous-silicon structures

International Nuclear Information System (INIS)

Diligenti, A.; Nannini, A.; Pennelli, G.; Pieri, F.; Fuso, F.; Allegrini, M.

1996-01-01

I-V DC characteristics have been measured on metal/porous-silicon structures. In particular, the measurements on metal/free-standing porous-silicon film/metal devices confirmed the result, already obtained, that the metal/porous-silicon interface plays a crucial role in the transport of any device. Four-contacts measurements on free-standing layers showed that the current linearly depends on the voltage and that the conduction process is thermally activated, the activation energy depending on the porous silicon film production parameters. Finally, annealing experiments performed in order to improve the conduction of rectifying contacts, are described

Sound transmission through double cylindrical shells lined with porous material under turbulent boundary layer excitation

Science.gov (United States)

Zhou, Jie; Bhaskar, Atul; Zhang, Xin

2015-11-01

This paper investigates sound transmission through double-walled cylindrical shell lined with poroelastic material in the core, excited by pressure fluctuations due to the exterior turbulent boundary layer (TBL). Biot's model is used to describe the sound wave propagating in the porous material. Three types of constructions, bonded-bonded, bonded-unbonded and unbonded-unbonded, are considered in this study. The power spectral density (PSD) of the inner shell kinetic energy is predicted for two turbulent boundary layer models, different air gap depths and three types of polyimide foams, respectively. The peaks of the inner shell kinetic energy due to shell resonance, hydrodynamic coincidence and acoustic coincidence are discussed. The results show that if the frequency band over the ring frequency is of interest, an air gap, even if very thin, should exist between the two elastic shells for better sound insulation. And if small density foam has a high flow resistance, a superior sound insulation can still be maintained.

Light emitting structures porous silicon-silicon substrate

International Nuclear Information System (INIS)

Monastyrskii, L.S.; Olenych, I.B.; Panasjuk, M.R.; Savchyn, V.P.

1999-01-01

The research of spectroscopic properties of porous silicon has been done. Complex of photoluminescence, electroluminescence, cathodoluminescence, thermostimulated depolarisation current analyte methods have been applied to study of geterostructures and free layers of porous silicon. Light emitting processes had tendency to decrease. The character of decay for all kinds of luminescence were different

Investigating dynamic characteristics of porous double-layered FG nanoplates in elastic medium via generalized nonlocal strain gradient elasticity

Science.gov (United States)

Reza Barati, Mohammad

2017-09-01

For the first time, a vibrating porous double-nanoplate system under in-plane periodic loads is modeled via the generalized nonlocal strain gradient theory (NSGT). Based on the proposed theory, one can examine both stiffness-softening and stiffness-hardening effects for a more accurate analysis of nanoplates. Nanopores or nanovoids are incorporated to the model based on a modified rule of mixture. Modeling of porous double-layered nanoplate is conducted according to a refined four-variable plate theory with fewer field variables than first-order plate theory. The governing equations and related classical and nonclassical boundary conditions are derived based on Hamilton's principle. These equations are solved for hinged nanoplates via Galerkin's method. It is shown that porosities, nonlocal parameter, strain gradient parameter, material gradation, interlayer stiffness, elastic foundation, side-to-thickness and aspect ratios have a notable impact on the vibration behavior of nanoporous materials.

Direct numerical simulations of mack-mode damping on porous coated cones

Science.gov (United States)

Lüdeke, H.; Wartemann, V.

2013-06-01

The flow field over a 3 degree blunt cone is investigated with respect to a hypersonic stability analysis of the boundary-layer flow at Mach 6 with porous as well as smooth walls by comparing local direct numerical simulations (DNS) and linear stability theory (LST) data. The original boundary-layer profile is generated by a finite volume solver, using shock capturing techniques to generate an axisymmetric flow field. Local boundary-layer profiles are extracted from this flow field and hypersonic Mack-modes are superimposed for cone-walls with and without a porous surface used as a passive transition-reduction device. Special care is taken of curvature effects of the wall on the mode development over smooth and porous walls.

Study of porous silicon morphologies for electron transport

International Nuclear Information System (INIS)

Pang, Y.; Demroff, H.P.; Elliott, T.S.; Lee, B.; Lu, J.; Madduri, V.B.; Mazumdar, T.K.; McIntyre, P.M.; Smith, D.D.; Trost, H.J.

1993-01-01

Field emitter devices are being developed for the gigatron, a high-efficiency, high frequency and high power microwave source. One approach being investigated is porous silicon, where a dense matrix of nanoscopic pores are galvanically etched into a silicon surface. In the present paper pore morphologies were used to characterize these materials. Using of Scanning Electron Microscope (SEM) and Transmission Electron Microscope (TEM) images of both N-type and P-type porous layers, it is found that pores propagate along the crystallographic direction, perpendicular to the surface of (100) silicon. Distinct morphologies were observed systematically near the surface, in the main bulk and near the bottom of N-type (100) silicon lift-off samples. It is seen that the pores are not cylindrical but exhibit more or less approximately square cross sections. X-ray diffraction spectra and electron diffraction patterns verified that bulk porous silicon is still a single crystal. In addition, a Scanning Tunnelling Microscope (STM) and an Atomic Force Microscope (AFM) were successfully applied to image the 40 angstrom gold film structure which was coated upon a cooled porous silicon layer. By associating the morphology study with the measured emitting current density of the Oxidized Porous Silicon Field Emission Triode (OPSFET), techniques for the surface treatment of porous silicon will be optimized

Exploring Trianglamine Derivatives and Trianglamine Coordination Complexes as Porous Organic Materials

KAUST Repository

Eziashi, Magdalene

2018-05-01

Trianglamines are triangular chiral macrocycles that were first synthesized by Gawronski’s group in Poland in the year 2000.1 Despite their unique properties; triangular pore shape, chirality, symmetric structure and tunable pore size, they are still a poorly researched class of macrocycles today. Trianglamines have yet a role to play as porous organic molecules for separation processes, as macrocyclic precursors to build increasingly complex supramolecular assemblies and as building blocks for caged porous organic structures. The aim of the Thesis work is to explore trianglamine, its derivatives, and assemblies as viable porous organic molecules for potential gas capture and separation.

Ice crystallization in porous building materials: assessing damage using real-time 3D monitoring

Science.gov (United States)

Deprez, Maxim; De Kock, Tim; De Schutter, Geert; Cnudde, Veerle

2017-04-01

Frost action is one of the main causes of deterioration of porous building materials in regions at middle to high latitudes. Damage will occur when the internal stresses due to ice formation become larger than the strength of the material. Hence, the sensitivity of the material to frost damage is partly defined by the structure of the solid body. On the other hand, the size, shape and interconnection of pores manages the water distribution in the building material and, therefore, the characteristics of the pore space control potential to form ice crystals (Ruedrich et al., 2011). In order to assess the damage to building materials by ice crystallization, lot of effort was put into identifying the mechanisms behind the stress build up. First of all, volumetric expansion of 9% (Hirschwald, 1908) during the transition of water to ice should be mentioned. Under natural circumstances, however, water saturation degrees within natural rocks or concrete cannot reach a damaging value. Therefore, linear growth pressure (Scherer, 1999), as well as several mechanisms triggered by water redistribution during freezing (Powers and Helmuth, 1953; Everett, 1961) are more likely responsible for damage due to freezing. Nevertheless, these theories are based on indirect observations and models and, thus, direct evidence that reveals the exact damage mechanism under certain conditions is still lacking. To obtain this proof, in-situ information needs to be acquired while a freezing process is performed. X-ray computed tomography has proven to be of great value in material research. Recent advances at the Ghent University Centre for Tomography (UGCT) have already allowed to dynamically 3D image crack growth in natural rock during freeze-thaw cycles (De Kock et al., 2015). A great potential to evaluate the different stress build-up mechanisms can be found in this imaging technique consequently. It is required to cover a range of materials with different petrophysical properties to achieve

Liquid phase epitaxial growth of silicon on porous silicon for photovoltaic applications

International Nuclear Information System (INIS)

Berger, S.; Quoizola, S.; Fave, A.; Kaminski, A.; Perichon, S.; Barbier, D.; Laugier, A.

2001-01-01

The aim of this experiment is to grow a thin silicon layer ( 2 atmosphere, and finally LPE silicon growth with different temperature profiles in order to obtain a silicon layer on the sacrificial porous silicon (p-Si). We observed a pyramidal growth on the surface of the (100) porous silicon but the coalescence was difficult to obtain. However, on a p-Si (111) oriented wafer, homogeneous layers were obtained. (orig.)

Three-Dimensional Porous Particles Composed of Curved, Two-Dimensional, Nano-Sized Layers for Li-Ion Batteries

Science.gov (United States)

Yushin, Gleb; Evanoff, Kara; Magasinski, Alexander

2012-01-01

Thin Si films coated on porous 3D particles composed of curved 2D graphene sheets have been synthesized utilizing techniques that allow for tunable properties. Since graphene exhibits specific surface area up to 100 times higher than carbon black or graphite, the deposition of the same mass of Si on graphene is much faster in comparison -- a factor which is important for practical applications. In addition, the distance between graphene layers is tunable and variation in the thickness of the deposited Si film is feasible. Both of these characteristics allow for optimization of the energy and power characteristics. Thicker films will allow higher capacity, but slower rate capabilities. Thinner films will allow more rapid charging, or higher power performance. In this innovation, uniform deposition of Si and C layers on high-surface area graphene produced granules with specific surface area (SSA) of 5 sq. m/g.

Al-Si alloy point contact formation and rear surface passivation for silicon solar cells using double layer porous silicon

International Nuclear Information System (INIS)

Moumni, Besma; Ben Jaballah, Abdelkader; Bessais, Brahim

2012-01-01

Lowering the rear surface recombination velocities by a dielectric layer has fascinating advantages compared with the standard fully covered Al back-contact silicon solar cells. In this work the passivation effect by double layer porous silicon (PS) (wide band gap) and the formation of Al-Si alloy in narrow p-type Si point contact areas for rear passivated solar cells are analysed. As revealed by Fourier transform infrared spectroscopy, we found that a thin passivating aluminum oxide (Al 2 O 3 ) layer is formed. Scanning electron microscopy analysis performed in cross sections shows that with bilayer PS, liquid Al penetrates into the openings, alloying with the Si substrate at depth and decreasing the contact resistivity. At the solar cell level, the reduction in the contact area and resistivity leads to a minimization of the fill factor losses.

Self-assembled hierarchical nanostructures for high-efficiency porous photonic crystals.

Science.gov (United States)

Passoni, Luca; Criante, Luigino; Fumagalli, Francesco; Scotognella, Francesco; Lanzani, Guglielmo; Di Fonzo, Fabio

2014-12-23

The nanoscale modulation of material properties such as porosity and morphology is used in the natural world to mold the flow of light and to obtain structural colors. The ability to mimic these strategies while adding technological functionality has the potential to open up a broad array of applications. Porous photonic crystals are one such technological candidate, but have typically underachieved in terms of available materials, structural and optical quality, compatibility with different substrates (e.g., silicon, flexible organics), and scalability. We report here an alternative fabrication method based on the bottom-up self-assembly of elementary building blocks from the gas phase into high surface area photonic hierarchical nanostructures at room temperature. Periodic refractive index modulation is achieved by stacking layers with different nanoarchitectures. High-efficiency porous Bragg reflectors are successfully fabricated with sub-micrometer thick films on glass, silicon, and flexible substrates. High diffraction efficiency broadband mirrors (R≈1), opto-fluidic switches, and arrays of photonic crystal pixels with size<10 μm are demonstrated. Possible applications in filtering, sensing, electro-optical modulation, solar cells, and photocatalysis are envisioned.

A parametric study of laser induced ablation-oxidation on porous silicon surfaces

International Nuclear Information System (INIS)

De Stefano, Luca; Rea, Ilaria; Nigro, M Arcangela; Della Corte, Francesco G; Rendina, Ivo

2008-01-01

We have investigated the laser induced ablation-oxidation process on porous silicon layers having different porosities and thicknesses by non-destructive optical techniques. In particular, the interaction between a low power blue light laser and the porous silicon surfaces has been characterized by variable angle spectroscopic ellipsometry and Fourier transform infrared spectroscopy. The oxidation profiles etched on the porous samples can be tuned as functions of the layer porosity and laser fluence. Oxide stripes of width less than 2 μm and with thicknesses between 100 nm and 5 μm have been produced, depending on the porosity of the porous silicon, by using a 40 x focusing objective

Modified Shrinking Core Model for Atomic Layer Deposition of TiO2 on Porous Alumina with Ultrahigh Aspect Ratio

International Nuclear Information System (INIS)

Park, Inhye; Leem, Jina; Lee, Hooyong; Min, Yosep

2013-01-01

When atomic layer deposition (ALD) is performed on a porous material by using an organometallic precursor, minimum exposure time of the precursor for complete coverage becomes much longer since the ALD is limited by Knudsen diffusion in the pores. In the previous report by Min et al. (Ref. 23), shrinking core model (SCM) was proposed to predict the minimum exposure time of diethylzinc for ZnO ALD on a porous cylindrical alumina monolith. According to the SCM, the minimum exposure time of the precursor is influenced by volumetric density of adsorption sites, effective diffusion coefficient, precursor concentration in gas phase and size of the porous monolith. Here we modify the SCM in order to consider undesirable adsorption of byproduct molecules. TiO 2 ALD was performed on the cylindrical alumina monolith by using titanium tetrachloride (TiCl 4 ) and water. We observed that the byproduct (i. e., HCl) of TiO 2 ALD can chemically adsorb on adsorption sites, unlike the behavior of the byproduct (i. e., ethane) of ZnO ALD. Consequently, the minimum exposure time of TiCl 4 (∼16 min) was significantly much shorter than that (∼71 min) of DEZ. The predicted minimum exposure time by the modified SCM well agrees with the observed time. In addition, the modified SCM gives an effective diffusion coefficient of TiCl 4 of ∼1.78 Χ 10 -2 cm 2 /s in the porous alumina monolith

Vibro-acoustics of porous materials - waveguide modeling approach

DEFF Research Database (Denmark)

Darula, Radoslav; Sorokin, Sergey V.

2016-01-01

The porous material is considered as a compound multi-layered waveguide (i.e. a fluid layer surrounded with elastic layers) with traction free boundary conditions. The attenuation of the vibro-acoustic waves in such a material is assessed. This approach is compared with a conventional Biot's mode...

A Novel Method for Fabricating Double Layers Porous Anodic Alumina in Phosphoric/Oxalic Acid Solution and Oxalic Acid Solution

Directory of Open Access Journals (Sweden)

Yanfang Xu

2016-01-01

Full Text Available A novel method for fabricating ordered double layers porous anodic alumina (DL-PAA with controllable nanopore size was presented. Highly ordered large pore layer with interpore distance of 480 nm was fabricated in phosphoric acid solution with oxalic acid addition at the potential of 195 V and the small pore layer was fabricated in oxalic acid solution at the potential from 60 to 100 V. Experimental results show that the thickness of large pore layer is linearly correlative with anodizing time, and pore diameter is linearly correlative with pore widening time. When the anodizing potential in oxalic acid solution was adjusted from 60 to 100 V, the small pore layers with continuously tunable interpore distance from 142 to 241 nm and pore density from 1.94×109 to 4.89×109 cm−2 were obtained. And the interpore distance and the pore density of small pore layers are closely correlative with the anodizing potential. The fabricated DL-PAA templates can be widely utilized for fabrication of ordered nanomaterials, such as superhydrophobic or gecko-inspired adhesive materials and metal or semiconductor nanowires.

Steam and air co-injection in removing residual TCE in unsaturated layered sandy porous media.

Science.gov (United States)

Peng, Sheng; Wang, Ning; Chen, Jiajun

2013-10-01

Steam and air co-injection is a promising technique for volatile and semi-volatile organic contaminant remediation in heterogeneous porous media. In this study, removal of trichloroethene (TCE) with steam-air co-injection was investigated through a series of 2D sandbox experiments with different layered sand structures, and through numerical simulations. The results show that a layered structure with coarse sand, in which steam and air convection are relatively rapid, resulted in a higher removal rate and a larger removal ratio than those observed in an experiment using finer sand; however, the difference was not significant, and the removal ratios from three experiments ranged from 85% to 94%. Slight downward movement of TCE was observed for Experiment 1 (TCE initially in a fine sand zone encased in a coarse sand), while no such movement was observed for Experiment 2 (TCE initially in two fine sand layers encased in a coarse sand) or 3 (TCE initially in a silty sand zone encased in a coarse sand). Simulations show accumulation of TCE at the interface of the layered sands, which indicates a capillary barrier effect in restraining the downward movement of TCE. This effect is illustrated further by a numerical experiment with homogeneous coarse sand, in which continuous downward TCE movement to the bottom of the sandbox was simulated. Another numerical experiment with higher water saturation was also conducted. The results illustrate a complicated influence of water saturation on TCE removal in a layered sand structure. Published by Elsevier B.V.

Three-dimensional porous MXene/layered double hydroxide composite for high performance supercapacitors

Science.gov (United States)

Wang, Ya; Dou, Hui; Wang, Jie; Ding, Bing; Xu, Yunling; Chang, Zhi; Hao, Xiaodong

2016-09-01

In this work, an exfoliated MXene (e-MXene) nanosheets/nickel-aluminum layered double hydroxide (MXene/LDH) composite as supercapacitor electrode material is fabricated by in situ growth of LDH on e-MXene substrate. The LDH platelets homogeneously grown on the surface of the e-MXene sheets construct a three-dimensional (3D) porous structure, which not only leads to high active sites exposure of LDH and facile liquid electrolyte penetration, but also alleviates the volume change of LDH during the charge/discharge process. Meanwhile, the e -MXene substrate forms a conductive network to facilitate the electron transport of active material. The optimized MXene/LDH composite exhibits a high specific capacitance of 1061 F g-1 at a current density of 1 A g-1, excellent capacitance retention of 70% after 4000 cycle tests at a current density of 4 A g-1 and a good rate capability with 556 F g-1 retention at 10 A g-1.

Enhancement of porous silicon photoluminescence by electroless deposition of nickel

Energy Technology Data Exchange (ETDEWEB)

Amdouni, S. [Unité de nanomatériaux et photonique, Université El Manar, Faculté des Sciences de Tunis, Département de Physique, 2092 El Manar, Tunis Tunisia (Tunisia); Rahmani, M., E-mail: rahmanimehdi79@yahoo.com [Unité de nanomatériaux et photonique, Université El Manar, Faculté des Sciences de Tunis, Département de Physique, 2092 El Manar, Tunis Tunisia (Tunisia); Zaïbi, M.-A [Unité de nanomatériaux et photonique, Université El Manar, Faculté des Sciences de Tunis, Département de Physique, 2092 El Manar, Tunis Tunisia (Tunisia); Ecole Nationale Supérieure des Ingénieurs de Tunis, Université de Tunis, 5 Avenue Taha Hussein, 1008 Tunis (Tunisia); Oueslati, M. [Unité de nanomatériaux et photonique, Université El Manar, Faculté des Sciences de Tunis, Département de Physique, 2092 El Manar, Tunis Tunisia (Tunisia)

2015-01-15

Nickel-porous silicon nanocomposites (PS/Ni) are elaborated by an electroless deposition method using NiCl{sub 2} aqueous solution. The presence of nickel ions in the porous layer is confirmed by Fourier Transformed InfraRed spectroscopy (FTIR) and Raman spectroscopy. The photoluminescence (PL) spectra of PS/Ni, prepared at different electroless durations (t{sub edp}), are analyzed. A remarkable enhancement in the integrated PL intensity of PS containing nickel was observed. The lower t{sub edp} favor the deposition of nickel in PS, hence the silicon dangling bonds at the porous surface are quenched and this was increased the PL intensity. However, for the longer t{sub edp}, the PL intensity has been considerably decreased due to the destruction of some Si nanocrystallites. The PL spectra of PS/Ni, for t{sub edp} less than 8 min, show a multiband profile indicating the creation of new luminescent centers by Ni elements which induces a strong modification in the emission mechanisms. - Highlights: • Deposition of Ni ions into porous silicon (PS) layer using the electroless method. • Formation of Ni–O bonds on the porous layer. • The photoluminescence (PL) intensity of PS is enhanced after Ni deposition. • The increase of the PL is due to the contribution of radiative centers related to Ni.

Porous (Swiss-Cheese Graphite

Directory of Open Access Journals (Sweden)

Joseph P. Abrahamson

2018-05-01

Full Text Available Porous graphite was prepared without the use of template by rapidly heating the carbonization products from mixtures of anthracene, fluorene, and pyrene with a CO2 laser. Rapid CO2 laser heating at a rate of 1.8 × 106 °C/s vaporizes out the fluorene-pyrene derived pitch while annealing the anthracene coke. The resulting structure is that of graphite with 100 nm spherical pores. The graphitizablity of the porous material is the same as pure anthracene coke. Transmission electron microscopy revealed that the interfaces between graphitic layers and the pore walls are unimpeded. Traditional furnace annealing does not result in the porous structure as the heating rates are too slow to vaporize out the pitch, thereby illustrating the advantage of fast thermal processing. The resultant porous graphite was prelithiated and used as an anode in lithium ion capacitors. The porous graphite when lithiated had a specific capacity of 200 mAh/g at 100 mA/g. The assembled lithium ion capacitor demonstrated an energy density as high as 75 Wh/kg when cycled between 2.2 V and 4.2 V.

Electronic properties of electrolyte/anodic alumina junction during porous anodizing

Energy Technology Data Exchange (ETDEWEB)

Vrublevsky, I. [Department of Microelectronics, Belarusian State University of Informatics and Radioelectronics, 6 Brovka Street, Minsk 220013 (Belarus)]. E-mail: nil-4-2@bsuir.edu.by; Jagminas, A. [Institute of Chemistry, A. Gostauto 9, LT-01108 Vilnius (Lithuania); Schreckenbach, J. [Institut fuer Chemie, Technische Universitaet Chemnitz, Chemnitz D-09107 (Germany); InnoMat GmbH, Chemnitz (Germany); Goedel, Werner A. [Institut fuer Chemie, Technische Universitaet Chemnitz, Chemnitz D-09107 (Germany)

2007-03-15

The growth of porous oxide films on aluminum (99.99% purity), formed in 4% phosphoric acid was studied as a function of the anodizing voltage (23-53 V) using a re-anodizing technique and transmission electron microscopy (TEM) study. The chemical dissolution behavior of freshly anodized and annealed at 200 deg. C porous alumina films was studied. The obtained results indicate that porous alumina has n-type semiconductive behavior during anodizing in 4% phosphoric acid. During anodising, up to 39 V in the barrier layer of porous films, one obtains an accumulation layer (the thickness does not exceed 1 nm) where the excess electrons have been injected into the solid producing a downward bending of the conductive and valence band towards the interface. The charge on the surface of anodic oxide is negative and decreases with growing anodizing voltage. At the anodizing voltage of about 39 V, the charge on the surface of anodic oxide equals to zero. Above 39 V, anodic alumina/electrolyte junction injects protons from the electrolyte. These immobile positive charges in the surface layer of oxide together with an ionic layer of hydroxyl ions concentrated near the interface create a field, which produces an upward bending of the bands.

Impact of porous SiC-doped PVA based LDS layer on electrical parameters of Si solar cells

Science.gov (United States)

Kaci, S.; Rahmoune, R.; Kezzoula, F.; Boudiaf, Y.; Keffous, A.; Manseri, A.; Menari, H.; Cheraga, H.; Guerbous, L.; Belkacem, Y.; Chalal, R.; Bozetine, I.; Boukezzata, A.; Talbi, L.; Benfadel, K.; Ouadfel, M.-A.; Ouadah, Y.

2018-06-01

Nowadays, the advanced photon management is regarded as an area of intensive research investment. Ever since the most widely used commercial photovoltaic cells are fabricated with single gap semiconductors like silicon, photon management has offered opportunities to make better use of the photons, both inside and outside the single junction window. In this study, the impact of new down shifting layer on the photoelectrical parameters of silicon based solar cell was studied. An effort to enhance the photovoltaic performance of textured silicon solar cells through the application of porous SiC particles-doped polyvinyl alcohol (PVA) layers using the spin-coating technique, is reported. Current-voltage curves under artificial illumination were used to confirm the contribution of LDS (SiC-PVA) thin layers. Experiment results revealed that LDS based on SiC particles which were etched in HF/K2S2O8 solution at T = 80 °C under UV light of 254 nm exhibited the best solar cell photoelectrical parameters due to its strong photoluminescence.

Porous nitrogen-enriched carbonaceous material from marine waste: chitosan-derived layered CNX catalyst for aerial oxidation of 5-hydroxymethylfurfural (HMF) to 2,5-furandicarboxylic acid

Science.gov (United States)

Chitosan derived porous layered nitrogen-enriched carbonaceous CNx catalyst (PLCNx) has been synthesized from marine waste and its use demonstrated in a metal-free heterogeneous selective oxidation of 5-hydroxymethyl-furfural (HMF) to 2,5-furandicarboxylic acid (FDCA) using aeria...

Infill Optimization for Additive Manufacturing - Approaching Bone-like Porous Structures

DEFF Research Database (Denmark)

Wu, Jun; Aage, Niels; Westermann, Ruediger

2018-01-01

Porous structures such as trabecular bone are widely seen in nature. These structures exhibit superior mechanical properties whilst being lightweight. In this paper, we present a method to generate bone-like porous structures asl ightweight infill for additive manufacturing. Our method builds upon...

Hydrological performance of dual-substrate-layer green roofs using porous inert substrates with high sorption capacities.

Science.gov (United States)

Wang, Xiaoou; Tian, Yimei; Zhao, Xinhua; Peng, Chenrui

2017-06-01

Given that the common medium in existing green roofs is a single layer composed of organic and inorganic substrates, seven pilot-scale dual-substrate-layer extensive green roofs (G1-G7), which include nutrition and adsorption substrate layers, were constructed in this study. The effectiveness of porous inert substrates (activated charcoal, zeolite, pumice, lava, vermiculite and expanded perlite) used as the adsorption substrate for stormwater retention was investigated. A single-substrate-layer green roof (G8) was built for comparison with G1-G7. Despite the larger total rainfall depth (mm) of six types of simulated rains (43.2, 54.6, 76.2, 87.0, 85.2 and 86.4, respectively), the total percent retention of G1-G7 varied between 14% and 82% with an average of 43%, exhibiting better runoff-retaining capacity than G8 based on the maximum potential rainfall storage depth per unit height of adsorption substrate. Regression analysis showed that there was a logarithmic relationship between cumulative rainfall depth with non-zero runoff and stormwater retention for G1-G4 and a linear relationship for G5-G8. To enhance the water retention capacity and extend the service life of dual-substrate-layer extensive green roofs, the mixture of activated charcoal and/or pumice with expanded perlite and/or vermiculite is more suitable as the adsorption substrate than the mixture containing lava and/or zeolite.

Porous squeeze-film flow

KAUST Repository

Knox, D. J.

2013-11-14

© 2013 © The authors 2013. Published by Oxford University Press on behalf of the Institute of Mathematics and its Applications. All rights reserved. The squeeze-film flow of a thin layer of Newtonian fluid filling the gap between a flat impermeable surface moving under a prescribed constant load and a flat thin porous bed coating a stationary flat impermeable surface is considered. Unlike in the classical case of an impermeable bed, in which an infinite time is required for the two surfaces to touch, for a porous bed contact occurs in a finite contact time. Using a lubrication approximation, an implicit expression for the fluid layer thickness and an explicit expression for the contact time are obtained and analysed. In addition, the fluid particle paths are calculated, and the penetration depths of fluid particles into the porous bed are determined. In particular, the behaviour in the asymptotic limit of small permeability, in which the contact time is large but finite, is investigated. Finally, the results are interpreted in the context of lubrication in the human knee joint, and some conclusions are drawn about the contact time of the cartilage-coated femoral condyles and tibial plateau and the penetration of nutrients into the cartilage.

Passivation of surface-nanostructured f-SiC and porous SiC

DEFF Research Database (Denmark)

Ou, Haiyan; Lu, Weifang; Ou, Yiyu

The further enhancement of photoluminescence from nanostructured fluorescent silicon carbide (f-SiC) and porous SiC by using atomic layer deposited (ALD) Al2O3 is studied in this paper.......The further enhancement of photoluminescence from nanostructured fluorescent silicon carbide (f-SiC) and porous SiC by using atomic layer deposited (ALD) Al2O3 is studied in this paper....

Natural convection in a porous medium: External flows

International Nuclear Information System (INIS)

Cheng, P.

1985-01-01

Early theoretical work on heat transfer in porous media focussed its attention on the onset of natural convection and cellular convection in rectangular enclosures with heating from below. Recently, increased attention has been directed to the study of natural convection in a porous medium external to heated surfaces and bodies. Boundary layer approximations were introduced, and similarly solutions have been obtained for steady natural convection boundary layers adjacent to a heated flat plate, a horizontal cylinder and a sphere as well as other two-dimensional and axisymmetric bodies of arbitrary shape. Higher order boundary layer theories have been carried out to assess the accuracy of the boundary layer approximation. The effects of entrainments at the edge of the boundary layer, the inclination angle of the heated inclined plate, and the upstream geometry on the heat transfer characteristics have been investigated based on the method of matched asymptotic expansions. The conditions for the onset of vortex instability in porous layers heated from below were determined based on linear stability analyses. The effects of no-slip boundary conditions, non-Darcy and thermal dispersion, which were neglected in all of the previous theoretical investigations, have recently been re-examined. Experimental investigations on natural convection about a vertical and inclined heated plate, a horizontal cylinder, as well as plume rise from a horizontal line source of heat have been conducted. All of this work is reviewed in this paper

Microfabricated microneedle with porous tip for drug delivery

Science.gov (United States)

Ji, Jing; Tay, Francis E. H.; Miao, Jianmin; Iliescu, Ciprian

2006-05-01

This paper presents a novel approach to fabrication of a silicon microneedle array with porous tips. Dry etching technology with SF6/O2 gas by STS's inductively coupled plasma (ICP) etch tool was used to achieve the pyramidal needle structure. A thin silicon nitride layer was deposited after a thick photoresist layer was coated and reflowed at 120 °C. The silicon nitride layer and residual photoresist on the tips of the pyramidal structures were removed using reactive ion etching (RIE). Electrochemical etching in MeCN/HF was carried out to generate porous silicon on the tips of the microneedles. The fabricated microneedle array has potential applications in drug delivery, since the porous tips can be loaded with a high molecular weight drug. Analytic solutions to the critical loadings of the fabricated microneedle structure are also presented. The variations of the square cross-section were expressed as a function of the axial coordinate to analyze the bending normal stress and critical buckling loading. This analytic method can also be used for other microneedle structures with different cross-sections.

Photo-EMF Sensitivity of Porous Silicon Thin Layer–Crystalline Silicon Heterojunction to Ammonia Adsorption

Directory of Open Access Journals (Sweden)

Kae Dal Kwack

2011-01-01

Full Text Available A new method of using photo-electromotive force in detecting gas and controlling sensitivity is proposed. Photo-electromotive force on the heterojunction between porous silicon thin layer and crystalline silicon wafer depends on the concentration of ammonia in the measurement chamber. A porous silicon thin layer was formed by electrochemical etching on p-type silicon wafer. A gas and light transparent electrical contact was manufactured to this porous layer. Photo-EMF sensitivity corresponding to ammonia concentration in the range from 10 ppm to 1,000 ppm can be maximized by controlling the intensity of illumination light.

Photo-EMF Sensitivity of Porous Silicon Thin Layer–Crystalline Silicon Heterojunction to Ammonia Adsorption

Science.gov (United States)

Vashpanov, Yuriy; Jung, Jae Il; Kwack, Kae Dal

2011-01-01

A new method of using photo-electromotive force in detecting gas and controlling sensitivity is proposed. Photo-electromotive force on the heterojunction between porous silicon thin layer and crystalline silicon wafer depends on the concentration of ammonia in the measurement chamber. A porous silicon thin layer was formed by electrochemical etching on p-type silicon wafer. A gas and light transparent electrical contact was manufactured to this porous layer. Photo-EMF sensitivity corresponding to ammonia concentration in the range from 10 ppm to 1,000 ppm can be maximized by controlling the intensity of illumination light. PMID:22319353

Heavy metal ion adsorption onto polypyrrole-impregnated porous carbon.

Science.gov (United States)

Choi, Moonjung; Jang, Jyongsik

2008-09-01

Polypyrrole-impregnated porous carbon was readily synthesized using vapor infiltration polymerization of pyrrole monomers. The results show that the functionalized polymer layer was successfully coated onto the pore surface of carbon without collapse of mesoporous structure. The modified porous carbon exhibited an improved complexation affinity for heavy metal ions such as mercury, lead, and silver ions due to the amine group of polypyrrole. The introduced polypyrrole layer could provide the surface modification to be applied for heavy metal ion adsorbents. Especially, polymer-impregnated porous carbon has an enhanced heavy metal ion uptake, which is 20 times higher than that of adsorbents with amine functional groups. Furthermore, the relationship between the coated polymer amount and surface area was also investigated in regard to adsorption capacity.

White-light emission from porous-silicon-aluminium Schottky junctions

International Nuclear Information System (INIS)

Masini, G.; La Monica, S.; Maiello, G.

1996-01-01

Porous-silicon-based white-light-emitting devices are presented. The fabrication process on different substrates is described. The peculiarities of technological steps for device fabrication (porous-silicon formation and aluminium treatment) are underlined. Doping profile of the porous layer, current-voltage characteristics, time response, lifetime tests and electroluminescence emission spectrum of the device are presented. A model for electrical behaviour of Al/porous silicon Schottky junction is presented. Electroluminescence spectrum of the presented devices showed strong similarities with white emission from crystalline silicon junctions in the breakdown region

Onset of Vibrational Convection in a Binary Fluid Saturated Non-Darcy Porous Layer Heated from Above

Directory of Open Access Journals (Sweden)

Saravanan S.

2012-07-01

Full Text Available A linear stability analysis is used to investigate the influence of mechanical vibration on the onset of thermosolutal convection in a horizontal porous layer heated and salted from above. Vibrations are considered with arbitrary amplitude and frequency. The Brinkman extended Darcy model is used to describe the flow and the Oberbeck-Boussinesq approximation is employed. Continued fraction method and Floquet theory are used to determine the convective instability threshold. It is found that the solutal Rayleigh number has the stabilizing effect. The existence of a closed disconnected loop of synchronous mode is predicted in the marginal curve for moderate values of solutal Rayleigh number and vibration amplitude.

HRTEM analysis of the nanostructure of porous silicon

International Nuclear Information System (INIS)

Martin-Palma, R.J.; Pascual, L.; Landa-Canovas, A.R.; Herrero, P.; Martinez-Duart, J.M.

2006-01-01

The nanometric structure of porous silicon makes this material to be very suitable for its use in many different fields, including optoelectronics and biological applications. In the present work, the structure of porous silicon was investigated in detail by means of cross-sectional high-resolution transmission electron microscopy and digital image processing, together with electron energy loss spectroscopy. The structure of the Si/porous silicon interface and that of the silicon nanocrystals that compose porous silicon have been analyzed in detail. A strong strain contrast in the Si/porous silicon interface caused by high stresses was observed. Accordingly, dislocation pairs are found to be a possible mechanism of lattice matching between porous silicon and the Si substrate. Finally, high relative concentration of oxygen in the porous silicon layer was observed, together with low relative electron concentration in the conduction band when compared to Si

Preparation of micro-porous gel polymer for lithium ion polymer battery

International Nuclear Information System (INIS)

Kim, Je Young; Kim, Seok Koo; Lee, Seung-Jin; Lee, Sang Young; Lee, Hyang Mok; Ahn, Soonho

2004-01-01

We have developed a micro-porous gelling polymer layer which is formed on both the sides of support polyolefin separator with wet or dry processing technique. Morphologies of gel-coated layer are dependent on the compositions and process conditions, such as solvent/non-solvent combination and stretching ratios. The micro-porous gelling layer is used for the assembly of the lithium ion polymer battery of LG Chemical Ltd. The structure of battery is given elsewhere and the battery has excellent discharge performance with 94% of 2C discharge performance at room temperature

Electrokinetics in porous media

NARCIS (Netherlands)

Luong, D.T.

2014-01-01

This thesis presents the PhD research on electrokinetics in porous media. Electrokinetic phenomena are induced by the relative motion between a fluid and a solid surface and are directly related to the existence of an electric double layer between the fluid and the solid grain surface.

Luminescence properties of Si-containing porous matrix–PbS nanoparticle systems

International Nuclear Information System (INIS)

Tarasov, S. A.; Aleksandrova, O. A.; Lamkin, I. A.; Maksimov, A. I.; Maraeva, E. V.; Mikhailov, I. I.; Moshnikov, V. A.; Musikhin, S. F.; Nalimova, S. S.; Permyakov, N. V.; Spivak, Yu. M.; Travkin, P. G.

2015-01-01

The luminescence properties of systems that contain lead-sulfide nanoparticles deposited onto substrates fabricated from porous silicon, oxidized porous silicon, and porous (tin-oxide)–(silicon-oxide) layers are studied. It is shown that the structure and composition of the matrix induce a strong effect on the luminescence spectra of colloidal quantum dots, defining their emission wavelength

Photonic Crystal Sensors Based on Porous Silicon

Directory of Open Access Journals (Sweden)

Claudia Pacholski

2013-04-01

Full Text Available Porous silicon has been established as an excellent sensing platform for the optical detection of hazardous chemicals and biomolecular interactions such as DNA hybridization, antigen/antibody binding, and enzymatic reactions. Its porous nature provides a high surface area within a small volume, which can be easily controlled by changing the pore sizes. As the porosity and consequently the refractive index of an etched porous silicon layer depends on the electrochemial etching conditions photonic crystals composed of multilayered porous silicon films with well-resolved and narrow optical reflectivity features can easily be obtained. The prominent optical response of the photonic crystal decreases the detection limit and therefore increases the sensitivity of porous silicon sensors in comparison to sensors utilizing Fabry-Pérot based optical transduction. Development of porous silicon photonic crystal sensors which allow for the detection of analytes by the naked eye using a simple color change or the fabrication of stacked porous silicon photonic crystals showing two distinct optical features which can be utilized for the discrimination of analytes emphasize its high application potential.

Photonic Crystal Sensors Based on Porous Silicon

Science.gov (United States)

Pacholski, Claudia

2013-01-01

Porous silicon has been established as an excellent sensing platform for the optical detection of hazardous chemicals and biomolecular interactions such as DNA hybridization, antigen/antibody binding, and enzymatic reactions. Its porous nature provides a high surface area within a small volume, which can be easily controlled by changing the pore sizes. As the porosity and consequently the refractive index of an etched porous silicon layer depends on the electrochemial etching conditions photonic crystals composed of multilayered porous silicon films with well-resolved and narrow optical reflectivity features can easily be obtained. The prominent optical response of the photonic crystal decreases the detection limit and therefore increases the sensitivity of porous silicon sensors in comparison to sensors utilizing Fabry-Pérot based optical transduction. Development of porous silicon photonic crystal sensors which allow for the detection of analytes by the naked eye using a simple color change or the fabrication of stacked porous silicon photonic crystals showing two distinct optical features which can be utilized for the discrimination of analytes emphasize its high application potential. PMID:23571671

Evaporation Limited Radial Capillary Penetration in Porous Media.

Science.gov (United States)

Liu, Mingchao; Wu, Jian; Gan, Yixiang; Hanaor, Dorian A H; Chen, C Q

2016-09-27

The capillary penetration of fluids in thin porous layers is of fundamental interest in nature and various industrial applications. When capillary flows occur in porous media, the extent of penetration is known to increase with the square root of time following the Lucas-Washburn law. In practice, volatile liquid evaporates at the surface of porous media, which restricts penetration to a limited region. In this work, on the basis of Darcy's law and mass conservation, a general theoretical model is developed for the evaporation-limited radial capillary penetration in porous media. The presented model predicts that evaporation decreases the rate of fluid penetration and limits it to a critical radius. Furthermore, we construct a unified phase diagram that describes the limited penetration in an annular porous medium, in which the boundaries of outward and inward liquid are predicted quantitatively. It is expected that the proposed theoretical model will advance the understanding of penetration dynamics in porous media and facilitate the design of engineered porous architectures.

Highly photocatalytic TiO_2 interconnected porous powder fabricated by sponge-templated atomic layer deposition

International Nuclear Information System (INIS)

Pan, Shengqiang; Zhao, Yuting; Huang, Gaoshan; Li, Menglin; Mei, Yongfeng; Wang, Jiao; Zheng, Lirong; Baunack, Stefan; Schmidt, Oliver G; Gemming, Thomas

2015-01-01

A titanium dioxide (TiO_2) interconnected porous structure has been fabricated by means of atomic layer deposition of TiO_2 onto a reticular sponge template. The obtained freestanding TiO_2 with large surface area can be easily taken out of the water to solve a complex separation procedure. A compact and conformal nanocoating was evidenced by morphologic characterization. A phase transition, as well as production of oxygen vacancies with increasing annealing temperature, was detected by x-ray diffraction and x-ray photoelectron spectroscopy, respectively. The photocatalytic experimental results demonstrated that the powder with appropriate annealing treatment possessed excellent photocatalytic ability due to the co-action of high surface area, oxygen vacancies and the optimal crystal structure. (paper)

Porous Materials - Structure and Properties

DEFF Research Database (Denmark)

Nielsen, Anders

1997-01-01

The paper presents some viewpoints on the description of the pore structure and the modelling of the properties of the porous building materials. Two examples are given , where it has been possible to connect the pore structure to the properties: Shrinkage of autoclaved aerated concrete...

Fabrication of p-type porous GaN on silicon and epitaxial GaN

OpenAIRE

Bilousov, Oleksandr V.; Geaney, Hugh; Carvajal, Joan J.; Zubialevich, Vitaly Z.; Parbrook, Peter J.; Giguere, A.; Drouin, D.; Diaz, Francesc; Aguilo, Magdalena; O'Dwyer, Colm

2013-01-01

Porous GaN layers are grown on silicon from gold or platinum catalyst seed layers, and self-catalyzed on epitaxial GaN films on sapphire. Using a Mg-based precursor, we demonstrate p-type doping of the porous GaN. Electrical measurements for p-type GaN on Si show Ohmic and Schottky behavior from gold and platinum seeded GaN, respectively. Ohmicity is attributed to the formation of a Ga2Au intermetallic. Porous p-type GaN was also achieved on epitaxial n-GaN on sapphire, and transport measurem...

Three-Dimensional Reconstruction of Building Roofs from Airborne LiDAR Data Based on a Layer Connection and Smoothness Strategy

Directory of Open Access Journals (Sweden)

Yongjun Wang

2016-05-01

Full Text Available A new approach for three-dimensional (3-D reconstruction of building roofs from airborne light detection and ranging (LiDAR data is proposed, and it includes four steps. Building roof points are first extracted from LiDAR data by using the reversed iterative mathematic morphological (RIMM algorithm and the density-based method. The corresponding relations between points and rooftop patches are then established through a smoothness strategy involving “seed point selection, patch growth, and patch smoothing.” Layer-connection points are then generated to represent a layer in the horizontal direction and to connect different layers in the vertical direction. Finally, by connecting neighboring layer-connection points, building models are constructed with the second level of detailed data. The key contributions of this approach are the use of layer-connection points and the smoothness strategy for building model reconstruction. Experimental results are analyzed from several aspects, namely, the correctness and completeness, deviation analysis of the reconstructed building roofs, and the influence of elevation to 3-D roof reconstruction. In the two experimental regions used in this paper, the completeness and correctness of the reconstructed rooftop patches were about 90% and 95%, respectively. For the deviation accuracy, the average deviation distance and standard deviation in the best case were 0.05 m and 0.18 m, respectively; and those in the worst case were 0.12 m and 0.25 m. The experimental results demonstrated promising correctness, completeness, and deviation accuracy with satisfactory 3-D building roof models.

Optical and electrical properties of porous silicon layer formed on the textured surface by electrochemical etching

Science.gov (United States)

Weiying, Ou; Lei, Zhao; Hongwei, Diao; Jun, Zhang; Wenjing, Wang

2011-05-01

Porous silicon (PS) layers were formed on textured crystalline silicon by electrochemical etching in HF-based electrolyte. Optical and electrical properties of the TMAH textured surfaces with PS formation are studied. Moreover, the influences of the initial structures and the anodizing time on the optical and electrical properties of the surfaces after PS formation are investigated. The results show that the TMAH textured surfaces with PS formation present a dramatic decrease in reflectance. The longer the anodizing time is, the lower the reflectance. Moreover, an initial surface with bigger pyramids achieved lower reflectance in a short wavelength range. A minimum reflectance of 3.86% at 460 nm is achieved for a short anodizing time of 2 min. Furthermore, the reflectance spectrum of the sample, which was etched in 3 vol.% TMAH for 25 min and then anodized for 20 min, is extremely flat and lies between 3.67% and 6.15% in the wavelength range from 400 to 1040 nm. In addition, for a short anodizing time, a slight increase in the effective carrier lifetime is observed. Our results indicate that PS layers formed on a TMAH textured surface for a short anodization treatment can be used as both broadband antireflection coatings and passivation layers for the application in solar cells.

Optical and electrical properties of porous silicon layer formed on the textured surface by electrochemical etching

Energy Technology Data Exchange (ETDEWEB)

Ou Weiying; Zhao Lei; Diao Hongwei; Zhang Jun; Wang Wenjing, E-mail: wjwangwj@126.com [Key Laboratory of Solar Thermal Energy and Photovoltaic System, Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190 (China)

2011-05-15

Porous silicon (PS) layers were formed on textured crystalline silicon by electrochemical etching in HF-based electrolyte. Optical and electrical properties of the TMAH textured surfaces with PS formation are studied. Moreover, the influences of the initial structures and the anodizing time on the optical and electrical properties of the surfaces after PS formation are investigated. The results show that the TMAH textured surfaces with PS formation present a dramatic decrease in reflectance. The longer the anodizing time is, the lower the reflectance. Moreover, an initial surface with bigger pyramids achieved lower reflectance in a short wavelength range. A minimum reflectance of 3.86% at 460 nm is achieved for a short anodizing time of 2 min. Furthermore, the reflectance spectrum of the sample, which was etched in 3 vol.% TMAH for 25 min and then anodized for 20 min, is extremely flat and lies between 3.67% and 6.15% in the wavelength range from 400 to 1040 nm. In addition, for a short anodizing time, a slight increase in the effective carrier lifetime is observed. Our results indicate that PS layers formed on a TMAH textured surface for a short anodization treatment can be used as both broadband antireflection coatings and passivation layers for the application in solar cells. (semiconductor technology)

Porous polymer coatings on metal microneedles for enhanced drug delivery

Science.gov (United States)

Ullah, Asad; Kim, Chul Min; Kim, Gyu Man

2018-04-01

We present a simple method to coat microneedles (MNs) uniformly with a porous polymer (PLGA) that can deliver drugs at high rates. Stainless steel (SS) MNs of high mechanical strength were coated with a thin porous polymer layer to enhance their delivery rates. Additionally, to improve the interfacial adhesion between the polymer and MNs, the MN surface was modified by plasma treatment followed by dip coating with polyethyleneimine, a polymer with repeating amine units. The average failure load (the minimum force sufficient for detaching the polymer layer from the surface of SS) recorded for the modified surface coating was 25 N, whereas it was 2.2 N for the non-modified surface. Calcein dye was successfully delivered into porcine skin to a depth of 750 µm by the porous polymer-coated MNs, demonstrating that the developed MNs can pierce skin easily without deformation of MNs; additional skin penetration tests confirmed this finding. For visual comparison, rhodamine B dye was delivered using porous-coated and non-coated MNs in gelatin gel which showed that delivery with porous-coated MNs penetrate deeper when compared with non-coated MNs. Finally, lidocaine and rhodamine B dye were delivered in phosphate-buffered saline (PBS) medium by porous polymer-coated and non-coated MNs. For rhodamine B, drug delivery with the porous-coated MNs was five times higher than that with the non-coated MNs, whereas 25 times more lidocaine was delivered by the porous-coated MNs compared with the non-coated MNs.

Porous siliconformation and etching process for use in silicon micromachining

Science.gov (United States)

Guilinger, Terry R.; Kelly, Michael J.; Martin, Jr., Samuel B.; Stevenson, Joel O.; Tsao, Sylvia S.

1991-01-01

A reproducible process for uniformly etching silicon from a series of micromechanical structures used in electrical devices and the like includes providing a micromechanical structure having a silicon layer with defined areas for removal thereon and an electrochemical cell containing an aqueous hydrofluoric acid electrolyte. The micromechanical structure is submerged in the electrochemical cell and the defined areas of the silicon layer thereon are anodically biased by passing a current through the electrochemical cell for a time period sufficient to cause the defined areas of the silicon layer to become porous. The formation of the depth of the porous silicon is regulated by controlling the amount of current passing through the electrochemical cell. The micromechanical structure is then removed from the electrochemical cell and submerged in a hydroxide solution to remove the porous silicon. The process is subsequently repeated for each of the series of micromechanical structures to achieve a reproducibility better than 0.3%.

Double-Skinned Forward Osmosis Membranes for Reducing Internal Concentration Polarization within the Porous Sublayer

KAUST Repository

Wang, Kai Yu

2010-05-19

A scheme to fabricate forward osmosis membranes comprising a highly porous sublayer sandwiched between two selective skin layers via phase inversion was proposed. One severe deficiency of existing composite and asymmetric membranes used in forward osmosis is the presence of unfavorable internal concentration polarization within the porous support layer that hinders both (i) separation (salt flux) and (ii) the performance (water flux). The double skin layers of the tailored membrane may mitigate the internal concentration polarization by preventing the salt and other solutes in the draw solution from penetrating into the membrane porous support. The prototype double-skinned cellulose acetate membrane displayed a water flux of 48.2 L·m-2·h -1 and lower reverse salt transport of 6.5 g·m -2·h-1 using 5.0 M MgCl2 as the draw solution in a forward osmosis process performed at 22 °C. This can be attributed to the effective salt rejection by the double skin layers and the low water transport resistance within the porous support layer. The prospects of utilizing the double-selective layer membranes may have potential application in forward osmosis for desalination. This study may help pave the way to improve the membrane design for the forward osmosis process. © 2010 American Chemical Society.

Double-Skinned Forward Osmosis Membranes for Reducing Internal Concentration Polarization within the Porous Sublayer

KAUST Repository

Wang, Kai Yu; Ong, Rui Chin; Chung, Tai-Shung

2010-01-01

A scheme to fabricate forward osmosis membranes comprising a highly porous sublayer sandwiched between two selective skin layers via phase inversion was proposed. One severe deficiency of existing composite and asymmetric membranes used in forward osmosis is the presence of unfavorable internal concentration polarization within the porous support layer that hinders both (i) separation (salt flux) and (ii) the performance (water flux). The double skin layers of the tailored membrane may mitigate the internal concentration polarization by preventing the salt and other solutes in the draw solution from penetrating into the membrane porous support. The prototype double-skinned cellulose acetate membrane displayed a water flux of 48.2 L·m-2·h -1 and lower reverse salt transport of 6.5 g·m -2·h-1 using 5.0 M MgCl2 as the draw solution in a forward osmosis process performed at 22 °C. This can be attributed to the effective salt rejection by the double skin layers and the low water transport resistance within the porous support layer. The prospects of utilizing the double-selective layer membranes may have potential application in forward osmosis for desalination. This study may help pave the way to improve the membrane design for the forward osmosis process. © 2010 American Chemical Society.

Heat transfer in a vertical rectangular duct filled with a porous matrix ...

African Journals Online (AJOL)

International Journal of Engineering, Science and Technology. Vol. .... non-Darcy flow concerning a flat plate having variable wall temperature in porous media ...... Boundary layer analysis for natural convection in porous enclosure: use of.

Hexagonal ZnO porous plates prepared from microwave synthesized layered zinc hydroxide sulphate via thermal decomposition

Energy Technology Data Exchange (ETDEWEB)

Machovsky, Michal, E-mail: machovsky@ft.utb.cz [Centre of Polymer Systems, University Institute, Tomas Bata University in Zlin, Nad Ovcirnou 3685, 760 01 Zlin (Czech Republic); Polymer Centre, Faculty of Technology, Tomas Bata University in Zlin, Nam. T.G. Masaryka 275, 762 72 Zlin (Czech Republic); Kuritka, Ivo, E-mail: ivo@kuritka.net [Centre of Polymer Systems, University Institute, Tomas Bata University in Zlin, Nad Ovcirnou 3685, 760 01 Zlin (Czech Republic); Polymer Centre, Faculty of Technology, Tomas Bata University in Zlin, Nam. T.G. Masaryka 275, 762 72 Zlin (Czech Republic); Sedlak, Jakub, E-mail: j1sedlak@ft.utb.cz [Centre of Polymer Systems, University Institute, Tomas Bata University in Zlin, Nad Ovcirnou 3685, 760 01 Zlin (Czech Republic); Polymer Centre, Faculty of Technology, Tomas Bata University in Zlin, Nam. T.G. Masaryka 275, 762 72 Zlin (Czech Republic); Pastorek, Miroslav, E-mail: pastorek@ft.utb.cz [Centre of Polymer Systems, University Institute, Tomas Bata University in Zlin, Nad Ovcirnou 3685, 760 01 Zlin (Czech Republic); Department of Polymer Engineering, Faculty of Technology, Tomas Bata University in Zlin, Nam. T.G. Masaryka 275, 762 72 Zlin (Czech Republic)

2013-10-15

Graphical abstract: - Highlights: • Zinc hydroxy sulphate was synthesized in 3 min via microwave hydrothermal route. • Zinc hydroxy sulphate was converted into mesh like porous ZnO by calcining at 900°. • The process of transformation is topotactic. - Abstract: Layered zinc hydroxide sulphate (ZHS) was prepared by microwave-assisted hydrothermal precipitation of zinc sulphate monohydrate with hexamethylenetetramine. Under ambient conditions, the structure of ZHS determined by X-ray diffraction (XRD) was found to be a mixture of zinc hydroxide sulphate pentahydrate Zn{sub 4}SO{sub 4}(OH){sub 6}·5H{sub 2}O and tetrahydrate Zn{sub 4}SO{sub 4}(OH){sub 6}·4H{sub 2}O. Fourier transform infrared (FTIR) spectroscopy was used for characterization of the prepared materials. Based on the interpretation of ZHS's thermal decomposition profile obtained by thermogravimetric analysis, ZnO of high purity was prepared by calcination at 900 °C for 2 h. The structure of the resulting ZnO was confirmed by the XRD. The morphology examination by scanning electron microscopy revealed a porous mesh-like ZnO structure developed from the ZHS precursor at the expense of mass removal due to the release of water and sulphate during the calcination.

From red cells to soft porous lubrication.

Science.gov (United States)

Wu, Qianhong; Zhu, Zenghao; Nathan, Rungun

2017-11-01

In this paper, we report a novel experimental study to examine the lubrication theory for highly compressible porous media (Feng & Weinbaum, JFM, 422, 282, 2000), which was applied to the frictionless motion of red cells over the endothelial surface layer (ESL). The experimental setup consists of a running conveyer belt covered with a porous sheet, and an upper planar board, i.e. planing surface. The pore pressure generation was captured when the planing surface glides over the porous sheet. If the lateral leakage was eliminated, we found that the overall pore pressure's contribution to the total lift, fair 80%, and the friction coefficient η = 0.0981, when U =5 m/s, L =0.381 m, λ = h2/h0 = 1 and k =h2/h1 = 3, where U is the velocity of the conveyor belt; L is the planing surface length; h0, h1 and h2 are the undeformed, leading and trailing edge porous layer thickness, respectively. fair increases with the increase in U, λ and L, while decreases with the increase in k. η decreases with the increase in fair. If lateral pressure leakage exists, the pore pressure generation is reduced by nearly 90%. All the results agreed well with the theoretical predictions. The study here lays the foundation for applying soft porous media for new type of bearing with significantly reduced friction. This research was supported by the National Science Foundation (NSF CBET) under Award No. 1511096.

Dual functional porous anti-reflective coatings with a photocatalytic effect based on a single layer system

Science.gov (United States)

Jilavi, M. H.; Mousavi, S. H.; Müller, T. S.; de Oliveira, P. W.

2018-05-01

Anti-reflection and photocatalytic properties are desirable for improving the optical properties of electronic devices. We describe a method of fabrication a single-layer, anti-reflective (AR) thin film with an additional photocatalytic property. The layer is deposited on glass substrates by means of a low-cost dip-coating method using a SiO2-TiO2 solution. A comparative study was undertaken to investigate the effects of TiO2 concentrations on the photocatalytic properties of the film and to determine the optimal balance between transmittance and photocatalysis. The average transmittance increases from T = 90.51% to T = 95.46 ± 0.07% for the wavelengths between 380 and 1200 nm. The structural characterization indicated the formation of thin, porous SiO2-TiO2 films with a roughness of less than 7.5 nm. The quality of the samples was evaluated by a complete test program of the mechanical, chemical and accelerated weathering stability. This results open up new possibilities for cost-effective AR coatings for the glass and solar cell industries.

A comparison of experimental methods for measuring water permeability of porous building rocks

Directory of Open Access Journals (Sweden)

Galvan, S.

2014-09-01

Full Text Available This paper compares different experimental methods for measuring water permeability in 17 different porous building rocks. Both commercial apparatus and specially made designed permeameters are used for characterising intrinsic permeability and hydraulic conductivity, k, of rocks in the range of 10−12 to 10−4 m/s (~ 10−19−10−11 m2 or ~ 10−4−104 mD. We use both falling head and constant head permeameter methods including the triaxial and modified triaxial tests and a classical constant head permeameter. Results showed that for very low and low permeability samples (k−6 m/s, triaxial conditions were found the most accurate procedures and they provided similar or slightly lower permeability values than constant and falling head methods. The latter techniques were highly recommended for permeable and high permeable porous building materials. Water permeability values were also linked to effective porosity and interpreted in terms of interparticle and vugs porosity. Finally, some modifications in the apparatus and procedures were carried out in order to assess water permeability in soft materials, which involve the use of non-saturated samples.Se comparan diferentes métodos experimentales para la medida de la permeabilidad al agua en rocas porosas usadas como material de construcción. Se usaron diferentes permeabilímetros, (comerciales y desarrollados específicamente empleando los métodos triaxial, triaxial modificado, carga constante y carga variable. Se caracterizó la permeabilidad intrínseca y conductividad hidráulica, k, con valores que var.an desde 10−12 a 10−4 m/s (~ 10−19−10−11 m2 or ~ 10−4−104 mD. Para muestras poco y muy poco permeables el ensayo con célula triaxial fue el mas reproducible. Los ensayos de carga constante son muy recomendables para rocas porosas de construcción permeables y muy permeables. Además, se definen los parámetros experimentales más apropiados para caracterizar la

The onset of double diffusive convection in a viscoelastic fluid-saturated porous layer with non-equilibrium model.

Directory of Open Access Journals (Sweden)

Zhixin Yang

Full Text Available The onset of double diffusive convection in a viscoelastic fluid-saturated porous layer is studied when the fluid and solid phase are not in local thermal equilibrium. The modified Darcy model is used for the momentum equation and a two-field model is used for energy equation each representing the fluid and solid phases separately. The effect of thermal non-equilibrium on the onset of double diffusive convection is discussed. The critical Rayleigh number and the corresponding wave number for the exchange of stability and over-stability are obtained, and the onset criterion for stationary and oscillatory convection is derived analytically and discussed numerically.

Surface Morphology Transformation Under High-Temperature Annealing of Ge Layers Deposited on Si(100).

Science.gov (United States)

Shklyaev, A A; Latyshev, A V

2016-12-01

We study the surface morphology and chemical composition of SiGe layers after their formation under high-temperature annealing at 800-1100 °C of 30-150 nm Ge layers deposited on Si(100) at 400-500 °C. It is found that the annealing leads to the appearance of the SiGe layers of two types, i.e., porous and continuous. The continuous layers have a smoothened surface morphology and a high concentration of threading dislocations. The porous and continuous layers can coexist. Their formation conditions and the ratio between their areas on the surface depend on the thickness of deposited Ge layers, as well as on the temperature and the annealing time. The data obtained suggest that the porous SiGe layers are formed due to melting of the strained Ge layers and their solidification in the conditions of SiGe dewetting on Si. The porous and dislocation-rich SiGe layers may have properties interesting for applications.

Unobstructed electron transfer on porous polyelectrolyte nanostructures and its characterization by electrochemical surface plasmon resonance

Energy Technology Data Exchange (ETDEWEB)

Davis, Bryce W.; Linman, Matthew J.; Linley, Kamara S.; Hare, Christopher D. [Department of Chemistry, University of California, Riverside, CA 92521 (United States); Cheng Quan, E-mail: quan.cheng@ucr.ed [Department of Chemistry, University of California, Riverside, CA 92521 (United States)

2010-06-01

Thin organic films with desirable redox properties have long been sought in biosensor research. We report here the development of a polymer thin film interface with well-defined hierarchical nanostructure and electrochemical behavior, and its characterization by electrochemical surface plasmon resonance (ESPR) spectroscopy. The nano-architecture build-up is monitored in real time with SPR, while the redox response is characterized by cyclic voltammetry in the same flow cell. The multilayer assembly is built on a self-assembled monolayer (SAM) of 1:1 (molar ratio) 11-ferrocenyl-1-undecanethiolate (FUT) and mercaptoundecanoic acid (MUA), and constructed using a layer-by-layer deposition of cationic poly(allylamine hydrochloride) (PAH) and anionic poly(sodium 4-styrenesulfonate) (PSS). Electron transfer (ET) on the mixed surface and the effect of the layer structures on ET are systematically studied. Under careful control, multiple layers can be deposited onto the 1:1 FUT/MUA SAM that presents unobstructed redox chemistry, indicating a highly ordered, extensively porous structure obtained under this condition. The use of SPR to trace the minute change during the electrochemical process offers neat characterization of local environment at the interface, in particular double layer region, allowing for better control over the redox functionality of the multilayers. The 1:1 SAM has a surface coverage of 4.1 +- 0.3 x 10{sup -10} mol cm{sup -2} for ferrocene molecules and demonstrates unperturbed electrochemistry activity even in the presence of a 13 nm polymer film adhered to the electrode surface. This thin layer possesses some desirable properties similar to those on a SAM while presenting approx15 nm exceedingly porous structure for high loading capacity. The high porosity allows perchlorate to freely partition into the film, leading to high current density that is useful for sensitive electrochemical measurements.

Erbium doped stain etched porous silicon

International Nuclear Information System (INIS)

Gonzalez-Diaz, B.; Diaz-Herrera, B.; Guerrero-Lemus, R.; Mendez-Ramos, J.; Rodriguez, V.D.; Hernandez-Rodriguez, C.; Martinez-Duart, J.M.

2008-01-01

In this work a simple erbium doping process applied to stain etched porous silicon layers (PSLs) is proposed. This doping process has been developed for application in porous silicon solar cells, where conventional erbium doping processes are not affordable because of the high processing cost and technical difficulties. The PSLs were formed by immersion in a HF/HNO 3 solution to properly adjust the porosity and pore thickness to an optimal doping of the porous structure. After the formation of the porous structure, the PSLs were analyzed by means of nitrogen BET (Brunauer, Emmett and Teller) area measurements and scanning electron microscopy. Subsequently, the PSLs were immersed in a saturated erbium nitrate solution in order to cover the porous surface. Then, the samples were subjected to a thermal process to activate the Er 3+ ions. Different temperatures and annealing times were used in this process. The photoluminescence of the PSLs was evaluated before and after the doping processes and the composition was analyzed by Fourier transform IR spectroscopy

Porous ceramic scaffolds with complex architectures

Science.gov (United States)

Munch, E.; Franco, J.; Deville, S.; Hunger, P.; Saiz, E.; Tomsia, A. P.

2008-06-01

This work compares two novel techniques for the fabrication of ceramic scaffolds for bone tissue engineering with complex porosity: robocasting and freeze casting. Both techniques are based on the preparation of concentrated ceramic suspensions with suitable properties for the process. In robocasting, the computer-guided deposition of the suspensions is used to build porous materials with designed three dimensional geometries and microstructures. Freeze casting uses ice crystals as a template to form porous lamellar ceramic materials. Preliminary results on the compressive strengths of the materials are also reported.

Photoacoustic emission from Au nanoparticles arrayed on thermal insulation layer.

Science.gov (United States)

Namura, Kyoko; Suzuki, Motofumi; Nakajima, Kaoru; Kimura, Kenji

2013-04-08

Efficient photoacoustic emission from Au nanoparticles on a porous SiO(2) layer was investigated experimentally and theoretically. The Au nanoparticle arrays/porous SiO(2)/SiO(2)/Ag mirror sandwiches, namely, local plasmon resonators, were prepared by dynamic oblique deposition (DOD). Photoacoustic measurements were performed on the local plasmon resonators, whose optical absorption was varied from 0.03 (3%) to 0.95 by varying the thickness of the dielectric SiO(2) layer. The sample with high absorption (0.95) emitted a sound that was eight times stronger than that emitted by graphite (0.94) and three times stronger than that emitted by the sample without the porous SiO(2) layer (0.93). The contribution of the porous SiO(2) layer to the efficient photoacoustic emission was analyzed by means of a numerical method based on a one-dimensional heat transfer model. The result suggested that the low thermal conductivity of the underlying porous layer reduces the amount of heat escaping from the substrate and contributes to the efficient photoacoustic emission from Au nanoparticle arrays. Because both the thermal conductivity and the spatial distribution of the heat generation can be controlled by DOD, the local plasmon resonators produced by DOD are suitable for the spatio-temporal modulation of the local temperature.

Hydromagnetic boundary layer micropolar fluid flow over a stretching surface embedded in a non-darcian porous medium with radiation

Directory of Open Access Journals (Sweden)

Mostafa A. A. Mahmoud

2006-01-01

Full Text Available We have studied the effects of radiation on the boundary layer flow and heat transfer of an electrically conducting micropolar fluid over a continuously moving stretching surface embedded in a non-Darcian porous medium with a uniform magnetic field. The transformed coupled nonlinear ordinary differential equations are solved numerically. The velocity, the angular velocity, and the temperature are shown graphically. The numerical values of the skin friction coefficient, the wall couple stress, and the wall heat transfer rate are computed and discussed for various values of parameters.

Modelling multiphase flow inside the porous media of a polymer electrolyte membrane fuel cell

DEFF Research Database (Denmark)

Berning, Torsten; Kær, Søren Knudsen

2011-01-01

Transport processes inside polymer electrolyte membrane fuel cells (PEMFC’s) are highly complex and involve convective and diffusive multiphase, multispecies flow through porous media along with heat and mass transfer and electrochemical reactions in conjunction with water transport through...... an electrolyte membrane. We will present a computational model of a PEMFC with focus on capillary transport of water through the porous layers and phase change and discuss the impact of the liquid phase boundary condition between the porous gas diffusion layer and the flow channels, where water droplets can...

Photovoltaic characteristics of porous silicon /(n+ - p) silicon solar cells

International Nuclear Information System (INIS)

Dzhafarov, T.D.; Aslanov, S.S.; Ragimov, S.H.; Sadigov, M.S.; Nabiyeva, A.F.; Yuksel, Aydin S.

2012-01-01

Full text : The purpose of this work is to improve the photovoltaic parameters of the screen-printed silicon solar cells by formation the nano-porous silicon film on the frontal surface of the cell. The photovoltaic characteristics of two type silicon solar cells with and without porous silicon layer were measured and compared. A remarkable increment of short-circuit current density and the efficiency by 48 percent and 20 percent, respectively, have been achieved for PS/(n + - pSi) solar cell comparing to (n + - p)Si solar cell without PS layer

Transient Infrared Measurement of Laser Absorption Properties of Porous Materials

Directory of Open Access Journals (Sweden)

Marynowicz Andrzej

2016-06-01

Full Text Available The infrared thermography measurements of porous building materials have become more frequent in recent years. Many accompanying techniques for the thermal field generation have been developed, including one based on laser radiation. This work presents a simple optimization technique for estimation of the laser beam absorption for selected porous building materials, namely clinker brick and cement mortar. The transient temperature measurements were performed with the use of infrared camera during laser-induced heating-up of the samples’ surfaces. As the results, the absorbed fractions of the incident laser beam together with its shape parameter are reported.

Transient Infrared Measurement of Laser Absorption Properties of Porous Materials

Science.gov (United States)

Marynowicz, Andrzej

2016-06-01

The infrared thermography measurements of porous building materials have become more frequent in recent years. Many accompanying techniques for the thermal field generation have been developed, including one based on laser radiation. This work presents a simple optimization technique for estimation of the laser beam absorption for selected porous building materials, namely clinker brick and cement mortar. The transient temperature measurements were performed with the use of infrared camera during laser-induced heating-up of the samples' surfaces. As the results, the absorbed fractions of the incident laser beam together with its shape parameter are reported.

Luminescence evolution of porous GaN thin films prepared via UV-assisted electrochemical etching

International Nuclear Information System (INIS)

Cheah, S.F.; Lee, S.C.; Ng, S.S.; Yam, F.K.; Abu Hassan, H.; Hassan, Z.

2015-01-01

Porous gallium nitride (GaN) thin films with different surface morphologies and free carriers properties were fabricated from Si-doped GaN thin films using ultra-violet assisted electrochemical etching approach under various etching voltages. Fluctuation of luminescence signals was observed in the photoluminescence spectra of porous GaN thin films. Taking advantage of the spectral sensitivity of infrared attenuated total reflection spectroscopy on semiconductor materials, roles of free carriers and porous structure in controlling luminescence properties of GaN were investigated thoroughly. The results revealed that enhancement in luminescence signal is not always attained upon porosification. Although porosification is correlated to the luminescence enhancement, however, free carrier is the primary factor to enhance luminescence intensity. Due to unavoidable significant reduction of free carriers from Si-doped GaN in the porosification process, control of etching depth (i.e., thickness of porous layer formed from the Si-doped layer) is critical in fabricating porous GaN thin film with enhanced luminescence response. - Highlights: • Various pore morphologies with free carrier properties are produced by Si-doped GaN. • Free carriers are important to control the luminescence signal of porous GaN. • Enhancement of luminescence signal relies on the pore depth of Si-doped layer

Making Porous Luminescent Regions In Silicon Wafers

Science.gov (United States)

Fathauer, Robert W.; Jones, Eric W.

1994-01-01

Regions damaged by ion implantation stain-etched. Porous regions within single-crystal silicon wafers fabricated by straightforward stain-etching process. Regions exhibit visible photoluminescence at room temperature and might constitute basis of novel class of optoelectronic devices. Stain-etching process has advantages over recently investigated anodic-etching process. Process works on both n-doped and p-doped silicon wafers. Related development reported in article, "Porous Si(x)Ge(1-x) Layers Within Single Crystals of Si," (NPO-18836).

Multi-layer planting as a strategy of greening the transitional space in high-rise buildings: A review

Science.gov (United States)

Prihatmanti, Rani; Taib, Nooriati

2018-03-01

The issues regarding the rapid development in the urban have resulted in the increasing number of infrastructure built, including the high-rise buildings to accommodate the urban dwellers. Lack of greeneries due to the land limitation in the urban area has increased the surface radiation as well as the air temperature that leads to the Urban Heat Island (UHI) phenomena. Where urban land is limited, growing plants vertically could be a solution. Plants, which are widely known as one of the sustainability elements in the built environment could be integrated in building as a part of urban faming by growing edible plant species. This is also to address the food security issue in the urban as well as high-density cities. Since space is limited, the function of transitional space could be optimized for the green space. This paper explores the strategy of greening transitional space in the high-rise setting. To give a maximum impact in a limited space, multi-layer planting concept could be introduced. This concept is believed that multiple layers of plants could modify the microclimate, as well as the radiation to the building, compare to single layer plant. In addition to that, the method selected also determines the efficacy of the vertical greeneries. However, there are many other limitations related to the multi-layer planting method if installed in a transitional space that needs to be further studied. Despite its limitations, the application of vertical greeneries with multi-layer planting concept could be a promising solution for greening the limited space as well as improving the thermal comfort in the high-rise building.

Grazing incidence x-ray diffraction analysis of zeolite NaA membranes on porous alumina tubes.

Science.gov (United States)

Kyotani, Tomohiro

2006-07-01

Zeolite NaA-type membranes hydrothermally synthesized on porous alumina tubes, for dehydration process, were characterized by grazing incidence 2 theta scan X-ray diffraction analysis (GIXRD). The fine structure of the membrane was studied fractionally for surface layer and for materials embedded in the porous alumina tube. The thickness of the surface layer on the porous alumina tube in the membranes used in this study was approximately 2-3 microm as determined from transmission electron microscopy with focused ion beam thin-layer specimen preparation technique (FIB-TEM). To discuss the effects of the membrane surface morphology on the GIXRD measurements, CaA-type membrane prepared by ion exchange from the NaA-type membrane and surface-damaged NaA-type membrane prepared by water leaching were also studied. For the original NaA-type membrane, 2 theta scan GIXRD patterns could be clearly measured at X-ray incidence angles (alpha) ranging from 0.1 to 2.0 deg in increments of 0.1 deg. The surface layers of the 2 - 3 microm on the porous alumina tube correspond to the alpha values up to ca. 0.2 deg. For the CaA-type and the surface-damaged NaA-type membranes, however, diffraction patterns from the surface layer could not be successfully detected and the others were somewhat broad. For all the three samples, diffraction intensities of both zeolite and alumina increased with depth (X-ray incidence angle, alpha) in the porous alumina tube region. The depth profile analysis of the membranes based on the GIXRD first revealed that amount of zeolite crystal embedded in the porous alumina tube is much larger than that in the surface layer. Thus, the 2 theta scan GIXRD is a useful method to study zeolite crystal growth mechanism around (both inside and outside) the porous alumina support during hydrothermal synthesis and to study water permeation behavior in the dehydration process.

Porous-Hybrid Polymers as Platforms for Heterogeneous Photochemical Catalysis

KAUST Repository

Haikal, Rana R.

2016-07-18

A number of permanently porous polymers containing Ru(bpy)n photosensitizer or a cobaloxime complex, as a proton-reduction catalyst, were constructed via one-pot Sonogashira-Hagihara (SH) cross-coupling reactions. This process required minimal workup to access porous platforms with control over the apparent surface area, pore volume, and chemical functionality from suitable molecular building blocks (MBBs) containing the Ru or Co complexes, as rigid and multi-topic nodes. The cobaloxime molecular building block, generated through in situ metalation, afforded a microporous solid that demonstrated noticeable catalytic activity towards hydrogen-evolution reaction (HER) with remarkable recyclability. We further demonstrated, in two cases, the ability to affect the excited state lifetime of the covalently-immobilized Ru(bpy)3 complex attained through deliberate utilization of the organic linkers of variable dimensions. Overall, this approach facilitates construction of tunable porous solids, with hybrid composition and pronounced chemical and physical stability, based on the well-known Ru(bpy)nor the cobaloxime complexes.

Porous-Hybrid Polymers as Platforms for Heterogeneous Photochemical Catalysis

KAUST Repository

Haikal, Rana R.; Wang, Xia; Hassan, Youssef S.; Parida, Manas R.; Banavoth, Murali; Mohammed, Omar F.; Pellechia, Perry J.; Fontecave, Marc; Alkordi, Mohamed H.

2016-01-01

A number of permanently porous polymers containing Ru(bpy)n photosensitizer or a cobaloxime complex, as a proton-reduction catalyst, were constructed via one-pot Sonogashira-Hagihara (SH) cross-coupling reactions. This process required minimal workup to access porous platforms with control over the apparent surface area, pore volume, and chemical functionality from suitable molecular building blocks (MBBs) containing the Ru or Co complexes, as rigid and multi-topic nodes. The cobaloxime molecular building block, generated through in situ metalation, afforded a microporous solid that demonstrated noticeable catalytic activity towards hydrogen-evolution reaction (HER) with remarkable recyclability. We further demonstrated, in two cases, the ability to affect the excited state lifetime of the covalently-immobilized Ru(bpy)3 complex attained through deliberate utilization of the organic linkers of variable dimensions. Overall, this approach facilitates construction of tunable porous solids, with hybrid composition and pronounced chemical and physical stability, based on the well-known Ru(bpy)nor the cobaloxime complexes.

Centrifugal spinning: A novel approach to fabricate porous carbon fibers as binder-free electrodes for electric double-layer capacitors

Science.gov (United States)

Lu, Yao; Fu, Kun; Zhang, Shu; Li, Ying; Chen, Chen; Zhu, Jiadeng; Yanilmaz, Meltem; Dirican, Mahmut; Zhang, Xiangwu

2015-01-01

Carbon nanofibers (CNFs), among various carbonaceous candidates for electric double-layer capacitor (EDLC) electrodes, draw extensive attention because their one-dimensional architecture offers both shortened electron pathways and high ion-accessible sites. Creating porous structures on CNFs yields larger surface area and enhanced capacitive performance. Herein, porous carbon nanofibers (PCNFs) were synthesized via centrifugal spinning of polyacrylonitrile (PAN)/poly(methyl methacrylate) (PMMA) solutions combined with thermal treatment and were used as binder-free EDLC electrodes. Three precursor fibers with PAN/PMMA weight ratios of 9/1, 7/3 and 5/5 were prepared and carbonized at 700, 800, and 900 °C, respectively. The highest specific capacitance obtained was 144 F g-1 at 0.1 A g-1 with a rate capability of 74% from 0.1 to 2 A g-1 by PCNFs prepared with PAN/PMMA weight ratio of 7/3 at 900 °C. These PCNFs also showed stable cycling performance. The present work demonstrates that PCNFs are promising EDLC electrode candidate and centrifugal spinning offers a simple, cost-effective strategy to produce PCNFs.

Photoluminescence studies on porous silicon/polymer heterostructure

International Nuclear Information System (INIS)

Mishra, J.K.; Bhunia, S.; Banerjee, S.; Banerji, P.

2008-01-01

Hybrid devices formed by filling porous silicon with MEH-PPV or poly [2-methoxy-5(2-ethylhexyloxy-p-phenylenevinylene)] have been investigated in this work. Analyses of the structures by scanning electron microscopy (SEM) demonstrated that the porous silicon layer was filled by the polymer with no significant change of the structures except that the polymer was infiltrated in the pores. The photoluminescence (PL) of the structures at 300 K showed that the emission intensity was very high as compared with that of the MEH-PPV films on different substrates such as crystalline silicon (c-Si) and indium tin oxide (ITO). The PL peak in the MEH-PPV/porous silicon composite structure is found to be shifted towards higher energy in comparison with porous silicon PL. A number of possibilities are discussed to explain the observations

Exploring Trianglamine Derivatives and Trianglamine Coordination Complexes as Porous Organic Materials

KAUST Repository

Eziashi, Magdalene

2018-01-01

, they are still a poorly researched class of macrocycles today. Trianglamines have yet a role to play as porous organic molecules for separation processes, as macrocyclic precursors to build increasingly complex supramolecular assemblies and as building blocks

Electrochromic Devices Based on Porous Tungsten Oxide Thin Films

Directory of Open Access Journals (Sweden)

Y. Djaoued

2012-01-01

Full Text Available Recent developments in the synthesis of transition metal oxides in the form of porous thin films have opened up opportunities in the construction of electrochromic devices with enhanced properties. In this paper, synthesis, characterization and electrochromic applications of porous WO3 thin films with different nanocrystalline phases, such as hexagonal, monoclinic, and orthorhombic, are presented. Asymmetric electrochromic devices have been constructed based on these porous WO3 thin films. XRD measurements of the intercalation/deintercalation of Li+ into/from the WO3 layer of the device as a function of applied coloration/bleaching voltages show systematic changes in the lattice parameters associated with structural phase transitions in LixWO3. Micro-Raman studies show systematic crystalline phase changes in the spectra of WO3 layers during Li+ ion intercalation and deintercalation, which agree with the XRD data. These devices exhibit interesting optical modulation (up to ~70% due to intercalation/deintercalation of Li ions into/from the WO3 layer of the devices as a function of applied coloration/bleaching voltages. The obtained optical modulation of the electrochromic devices indicates that, they are suitable for applications in electrochromic smart windows.

Study of the processes of carbonization and oxidation of porous silicon by Raman and IR spectroscopy

International Nuclear Information System (INIS)

Vasin, A. V.; Okholin, P. N.; Verovsky, I. N.; Nazarov, A. N.; Lysenko, V. S.; Kholostov, K. I.; Bondarenko, V. P.; Ishikawa, Y.

2011-01-01

Porous silicon layers were produced by electrochemical etching of single-crystal silicon wafers with the resistivity 10 Ω cm in the aqueous-alcohol solution of hydrofluoric acid. Raman spectroscopy and infrared absorption spectroscopy are used to study the processes of interaction of porous silicon with undiluted acetylene at low temperatures and the processes of oxidation of carbonized porous silicon by water vapors. It is established that, even at the temperature 550°C, the silicon-carbon bonds are formed at the pore surface and the graphite-like carbon condensate emerges. It is shown that the carbon condensate inhibits oxidation of porous silicon by water vapors and contributes to quenching of white photoluminescence in the oxidized carbonized porous silicon nanocomposite layer.

Novel building units with bimetallic rings in inorganic/organic hybrid chains and layers

International Nuclear Information System (INIS)

Mahenthirarajah, Thushitha; Li Yang; Lightfoot, Philip

2009-01-01

Hydrothermal synthesis has produced three new compounds constructed from novel building units containing vanadium-oxide (or oxyfluoride) subunits linked together via covalently bound cationic copper complexes. Each new compound exhibits novel structural features: [Cu(dipa)][VOF 4 ] (1) incorporates a corner-sharing octahedral vanadium(IV) oxyfluoride chain decorated by copper-(2,2'-dipyridyl amine) complexes which form intra-chain bridges. Within a similar reactant system [Cu(dipa)] 2 [V 6 O 17 ] (2) is produced, the structure of which exhibits edge-sharing trigonal bipyramidal vanadium(V) 'ladder-like' double chains which are bridged into layers by tetrahedral pyrovanadate dimers together with the copper-(2,2'-dipyridyl amine) complexes. [Cu(py) 4 ] 2 [V 4 O 12 ] (3), is a 2-D structure featuring exclusively tetrahedral vanadium(V) in four-membered ring building blocks, linked through octahedral copper-pyridine complexes to form two crystallographically different bimetallic layers. - Graphical abstract: Hydrothermal synthesis is used to prepare hybrid mixed metal oxides and oxyfluorides with novel extended connectivities

High-performance flexible supercapacitor based on porous array electrodes

Energy Technology Data Exchange (ETDEWEB)

Shieh, Jen-Yu; Tsai, Sung-Ying; Li, Bo-Yan [Institute of Electro-Optical and Materials Science, National Formosa University, 64 Wenhua Road, Huwei, Yunlin 63208, Taiwan (China); Yu, Hsin Her, E-mail: hhyu@nfu.edu.tw [Department of Biotechnology, National Formosa University, 64 Wenhua Road, Huwei, Yunlin 63208, Taiwan (China)

2017-07-01

In this study, an array of polystyrene (PS) spheres was synthesized by a dispersion-polymerization technique as a template onto which a porous polydimethylsiloxane (PDMS) microarray structure was fabricated by soft lithography. A conducting layer was coated on the surface of the microarray after a suspension of multi-walled carbon nanotubes (MWCNTs) mixed with graphene (G) had been poured into the porous array. A PDMS-based porous supercapacitor was assembled by sandwiching a separator between two porous electrodes filled with a H{sub 3}PO{sub 4}/polyvinyl alcohol (PVA) gel electrolyte. The specific capacitance, electrochemical properties, and cycle stability of the porous electrode supercapacitors were explored. The porous PDMS-electrode-based supercapacitor exhibited high specific capacitance and good cycle stability, indicating its enormous potential for future applications in wearable and portable electronic products. - Highlights: • Porous electrode was prepared using an array of polystyrene spheres as template. • The porous electrodes provided increased contact area with the electrolyte. • A gel electrolyte averted problems with leakage and poor interfacial contact. • A larger separator pore size effectively reduced the internal resistance, iR{sub drop}. • Porous PDMS supercapacitor showed superior flexibility and cycling stability.

Nonlinear dynamics of capacitive charging and desalination by porous electrodes

Science.gov (United States)

Biesheuvel, P. M.; Bazant, M. Z.

2010-03-01

The rapid and efficient exchange of ions between porous electrodes and aqueous solutions is important in many applications, such as electrical energy storage by supercapacitors, water desalination and purification by capacitive deionization, and capacitive extraction of renewable energy from a salinity difference. Here, we present a unified mean-field theory for capacitive charging and desalination by ideally polarizable porous electrodes (without Faradaic reactions or specific adsorption of ions) valid in the limit of thin double layers (compared to typical pore dimensions). We illustrate the theory for the case of a dilute, symmetric, binary electrolyte using the Gouy-Chapman-Stern (GCS) model of the double layer, for which simple formulae are available for salt adsorption and capacitive charging of the diffuse part of the double layer. We solve the full GCS mean-field theory numerically for realistic parameters in capacitive deionization, and we derive reduced models for two limiting regimes with different time scales: (i) in the “supercapacitor regime” of small voltages and/or early times, the porous electrode acts like a transmission line, governed by a linear diffusion equation for the electrostatic potential, scaled to the RC time of a single pore, and (ii) in the “desalination regime” of large voltages and long times, the porous electrode slowly absorbs counterions, governed by coupled, nonlinear diffusion equations for the pore-averaged potential and salt concentration.

X-ray and synchrotron studies of porous silicon

Energy Technology Data Exchange (ETDEWEB)

Sivkov, V. N., E-mail: svn@dm.komisc.ru [Russian Academy of Sciences, Komi Scientific Center, Ural Branch (Russian Federation); Lomov, A. A. [Russian Academy of Sciences, Physical-Technological Institute (Russian Federation); Vasil' ev, A. L. [Russian Academy of Sciences, Shubnikov Institute of Crystallography (Russian Federation); Nekipelov, S. V. [Komi State Pedagogical Institute (Russian Federation); Petrova, O. V. [Russian Academy of Sciences, Komi Scientific Center, Ural Branch (Russian Federation)

2013-08-15

The results of comprehensive studies of layers of porous silicon of different conductivity types, grown by anodizing standard Si(111) substrates in an electrolyte based on fluoric acid and ethanol with the addition of 5% of iodine and kept in air for a long time, are discussed. Measurements are performed by scanning electron microscopy, high-resolution X-ray diffraction, and ultrasoft X-ray spectroscopy using synchrotron radiation. The structural parameters of the layers (thickness, strain, and porosity) and atomic and chemical composition of the porous-silicon surface are determined. It is found that an oxide layer 1.5-2.3-nm thick is formed on the surface of the silicon skeleton. The near-edge fine structure of the Si 2p absorption spectrum of this layer corresponds to the fine structure of the 2p spectrum of well coordinated SiO{sub 2}. In this case, the fine structure in the Si 2p-edge absorption region of the silicon skeleton is identical to that of the 2p absorption spectrum of crystalline silicon.

Formation of nanosize poly(p-phenylene vinylene) in porous silicon substrate

International Nuclear Information System (INIS)

Le Rendu, P.; Nguyen, T.P.; Cheah, K.; Joubert, P.

2003-01-01

We report the results of optical investigations in porous silicon (PS)/poly(p-phenylene vinylene) (PPV) systems obtained by filling the pores of silicon wafers with polymer. By scanning electron microscopy (SEM), IR, and Raman spectroscopy, we observed that the porous silicon layer was thoroughly filled by the polymer with no significant change in the structure of the materials. This suggests that there is no interaction between the components. On the other hand, the photoluminescence (PL) spectra of the devices investigated at different temperatures (from 11 to 290 K) showed that both materials are active at low temperatures. Porous silicon has a band located at 398 nm while PPV has two bands at 528 and 570 nm. As the temperature increases, the PL intensity of porous silicon decreases and that PPV is blue shifted. A new band emerging at 473 nm may indicate an energy transfer from the porous silicon to PPV, involving short segments of the polymer. The band of PPV located at 515 nm becomes more dominant and indicates that the nanosize polymer films are formed in the pores of the silicon layer, in agreement with the results obtained by SEM, IR, and Raman analyses

Multi-layered hierarchical nanostructures for transparent monolithic dye-sensitized solar cell architectures

Science.gov (United States)

Passoni, Luca; Fumagalli, Francesco; Perego, Andrea; Bellani, Sebastiano; Mazzolini, Piero; Di Fonzo, Fabio

2017-06-01

Monolithic dye-sensitized solar cell (DSC) architectures hold great potential for building-integrated photovoltaics applications. They indeed benefit from lower weight and manufacturing costs as they avoid the use of a transparent conductive oxide (TCO)-coated glass counter electrode. In this work, a transparent monolithic DSC comprising a hierarchical 1D nanostructure stack is fabricated by physical vapor deposition techniques. The proof of concept device comprises hyperbranched TiO2 nanostructures, sensitized by the prototypical N719, as photoanode, a hierarchical nanoporous Al2O3 spacer, and a microporous indium tin oxide (ITO) top electrode. An overall 3.12% power conversion efficiency with 60% transmittance outside the dye absorption spectral window is demonstrated. The introduction of a porous TCO layer allows an efficient trade-off between transparency and power conversion. The porous ITO exhibits submicrometer voids and supports annealing temperatures above 400 °C without compromising its optoelectronical properties. After thermal annealing at 500 °C, the resistivity, mobility, and carrier concentration of the 800 nm-thick porous ITO layer are found to be respectively 2.3 × 10-3 Ω cm-1, 11 cm2 V-1 s-1, and 1.62 × 1020 cm-3, resulting in a series resistance in the complete device architecture of 45 Ω. Electrochemical impedance and intensity-modulated photocurrent/photovoltage spectroscopy give insight into the electronic charge dynamic within the hierarchical monolithic DSCs, paving the way for potential device architecture improvements.

Biodegradable polymer for sealing porous PEO layer on pure magnesium: An in vitro degradation study

Science.gov (United States)

Alabbasi, Alyaa; Mehjabeen, Afrin; Kannan, M. Bobby; Ye, Qingsong; Blawert, Carsten

2014-05-01

An attempt was made to seal the porous silicate-based plasma electrolytic oxidation (PEO) layer on pure magnesium (Mg) with a biodegradable polymer, poly(L-lactide) (PLLA), to delay the localized degradation of magnesium-based implants in body fluid for better in-service mechanical integrity. Firstly, a silicate-based PEO coating on pure magnesium was performed using a pulsed constant current method. In order to seal the pores in the PEO layer, PLLA was coated using a two-step spin coating method. The performance of the PEO-PLLA Mg was evaluated using electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization. The EIS results showed that the polarization resistance (Rp) of the PEO-PLLA Mg was close to two orders of magnitude higher than that of the PEO Mg. While the corrosion current density (icorr) of the pure Mg was reduced by 65% with the PEO coating, the PEO-PLLA coating reduced the icorr by almost 100%. As expected, the Rp of the PEO-PLLA Mg decreased with increase in exposure time. However, it was noted that the Rp of the PEO-PLLA Mg even after 100 h was six times higher than that of the PEO Mg after 48 h exposure, and did not show any visible localized attack.

S-layer architectures : extending the morphogenetic potential of S-layer protein self-assembly

International Nuclear Information System (INIS)

Schuster, D.

2013-01-01

Self-assembly of molecular building blocks is a common principle for bottom up based building principles in nature. One example are crystalline bacterial surface layers, termed S-layers, which are the most commonly observed cell surface structures in prokaryotic organisms. They recrystallize into highly ordered, porous protein meshworks with unit cell sizes of 3 to 30 nm and pore sizes of 2 to 8 nm. In this work, S-layers were self-assembled on various three dimensional scaffolds in order to fabricate novel S-layer architectures. Exploiting the stabilizing effect of silica deposited on the S-layer protein meshwork led to the construction of hollow S-layer nano-containers derived from coated liposomes. Transmission electron microscopy (TEM) techniques and release experiments with fluorescent dyes confirmed the dissolution of the supporting lipids. Silica deposition on different spherical particles in solution, as well as on planar S-layer coated surfaces, could be monitored by measuring the ζ-potential, the decline of monosilicic acid in solution, by using scanning electron microscopy (SEM) with energy dispersive X-ray (EDX) analysis or by quartz crystal microbalance with dissipation monitoring (QCM-D). Both, ζ-potential and release experiments showed differences between silicified plain liposomes and silicified S-layer coated liposomes. In addition, nanocapsules with calcium carbonate cores served as another template for the construction of silica supported S-layer architectures. These were investigated by SEM and fluorescence microscopy after fluorescence labeling. Additional coating with polyelectrolytes increased the stability of the nanocapsules. Their mechanical properties were characterized by atomic force microscopy (AFM). The influence of silica deposition was investigated by AFM and SEM. Further on, emulsomes and gas filled lipid supported microbubbles may serve as other templates for the design of spherical protein constructs although extraction of the

Natural radioactivity of building materials

International Nuclear Information System (INIS)

Mrnustik, J.

1988-01-01

Within a study of the natural radioactivity of building materials, coefficients were determined of the emanation from selected materials and raw materials, such as porous concrete, bricks, marlite, quartzite, etc. Measurements were made of ground samples using Lucas scintillation chambers which give an accuracy of determination of the coefficient of about 10%. Specific radium activity was also determined for the samples. Tabulated is a comparison of the average specific activity of radium in concrete, power plant ash and porous concrete in Czechoslovakia and abroad. It is stated that monitoring the content of natural radionuclides in building materials is an indispensable part of the production process in the building industry, this with regard to the radiation protection of the population. This will be enhanced by the new Czechoslovak standard determining methods of measuring the content of natural radionuclides and the coefficient of radon emanation, and the subsequent evaluation of the properties of building materials. (Z.M.) 3 figs., 3 tabs

Influence of Porous Aggregate on the Properties of Foamed Concrete

Directory of Open Access Journals (Sweden)

Namsone Elvija

2016-12-01

Full Text Available Nowadays energy-efficient use of building resources is getting more and more popular. Technological developments have promoted production of new building materials with improved physical, mechanical and thermal properties. Foamed concrete with porous aggregate can serve as an alternative material for the existing lightweight concrete materials. This building material shows good mechanical and thermal properties, as well as capillary absorption and shrinkage test results that attest the longevity of this building material.

Nanostructural characterization of large-scale porous alumina fabricated via anodizing in arsenic acid solution

Energy Technology Data Exchange (ETDEWEB)

Akiya, Shunta; Kikuchi, Tatsuya, E-mail: kiku@eng.hokudai.ac.jp; Natsui, Shungo; Suzuki, Ryosuke O.

2017-05-01

Highlights: • Anodic porous alumina was formed in an arsenic acid solution. • Potential difference (voltage) anodizing at 340 V was achieved. • The porous alumina was slightly ordered under the appropriate conditions. • Pore sealing behavior was not observed in boiling distilled water. • The porous alumina exhibits a white photoluminescence emission under UV irradiation. - Abstract: Anodizing of aluminum in an arsenic acid solution is reported for the fabrication of anodic porous alumina. The highest potential difference (voltage) without oxide burning increased as the temperature and the concentration of the arsenic acid solution decreased, and a high anodizing potential difference of 340 V was achieved. An ordered porous alumina with several tens of cells was formed in 0.1–0.5 M arsenic acid solutions at 310–340 V for 20 h. However, the regularity of the porous alumina was not improved via anodizing for 72 h. No pore sealing behavior of the porous alumina was observed upon immersion in boiling distilled water, and it may be due to the formation of an insoluble complex on the oxide surface. The porous alumina consisted of two different layers: a hexagonal alumina layer that contained arsenic from the electrolyte and a pure alumina honeycomb skeleton. The porous alumina exhibited a white photoluminescence emission at approximately 515 nm under UV irradiation at 254 nm.

Drying of a tape-cast layer: Numerical modelling of the evaporation process in a graded/layered material

DEFF Research Database (Denmark)

Jabbaribehnam, Mirmasoud; Jambhekar, V. A.; Hattel, Jesper Henri

2016-01-01

-phase compositional porous-media flow — for the ceramic layer — and single-phase compositional laminar free flow — for the air above it. The preliminary results show the typical expected evaporation behaviour from a porous medium initially saturated with water, and water–vapour transport to the free-flow region...

Determination of the refractive index of n+- and p-type porous Si samples

International Nuclear Information System (INIS)

Setzu, S.; Romestain, R.; Chamard, V.

2004-01-01

Photochemical etching of porous Si layers has been shown to be able to create micrometer or submicrometer-scale lateral gratings very promising for photonic applications. However, the reduced size of this lateral periodicity hinders standard measurements of refractive index variations. Therefore accurate characterizations of such gratings are usually difficult. In this paper we address this problem by reproducing on a larger scale (millimeter) the micrometer scale light-induced refractive index variations associated to the lateral periodicity. Using this procedure we perform standard X-ray and optical reflectivity measurements on our samples. One can then proceed to the determination of light-induced variations of porosity and refractive index. We present results for p-type samples, where the photo-dissolution can only be realized after the formation of the porous layer, as well as for n + -type samples, where light action can only be effective during the formation of the porous layer

Topotactic condensation of layer silicates with ferrierite-type layers forming porous tectosilicates.

Science.gov (United States)

Marler, B; Wang, Y; Song, J; Gies, H

2014-07-21

Five different hydrous layer silicates (HLSs) containing fer layers (ferrierite-type layers) were obtained by hydrothermal syntheses from mixtures of silicic acid, water and tetraalkylammonium/tetraalkylphosphonium hydroxides. The organic cations had been added as structure directing agents (SDA). A characteristic feature of the structures is the presence of strong to medium strong hydrogen bonds between the terminal silanol/siloxy groups of neighbouring layers. The five-layered silicates differ chemically only with respect to the organic cations. Structurally, they differ with respect to the arrangement of the fer layers relative to each other, which is distinct for every SDA-fer-layer system. RUB-20 (containing tetramethylammonium) and RUB-40 (tetramethylphosphonium) are monoclinic with stacking sequence AAA and shift vectors between successive layers 1a0 + 0b0 + 0.19c0 and 1a0 + 0b0 + 0.24c0, respectively. RUB-36 (diethyldimethylammonium), RUB-38 (methyltriethylammonium) and RUB-48 (trimethylisopropylammonium) are orthorhombic with stacking sequence ABAB and shift vectors 0.5a0 + 0b0± 0.36c0, 0.5a0 + 0b0 + 0.5c0 and 0.5a0 + 0b0± 0.39c0, respectively. Unprecedented among the HLSs, two monoclinic materials are made up of fer layers which possess a significant amount of ordered defects within the layer. The ordered defects involve one particular Si-O-Si bridge which is, to a fraction of ca. 50%, hydrolyzed to form nests of two ≡Si-OH groups. When heated to 500-600 °C in air, the HLSs condense to form framework silicates. Although all layered precursors were moderately to well ordered, the resulting framework structures were of quite different crystallinity. The orthorhombic materials RUB-36, -38 and -48, general formula SDA4Si36O72(OH)4, which possess very strong hydrogen bonds (d[O···O] ≈ 2.4 Å), transform into a fairly or well ordered CDO-type silica zeolite RUB-37. The monoclinic materials RUB-20 and -40, general formula SDA2Si18O36(OH)2OH, possessing

Recipes for porous building materials, More with less

NARCIS (Netherlands)

Brouwers, H.J.H.; Fischer, H.-B.; Bode, K.-A.; Beuthan, C.

2012-01-01

The building sector, comprising both buildings and infrastructure, is the largest consumer of energy and materials. As well as the huge amount of raw materials involved, enormous amounts of energy are also used for the production and transport of raw materials, building materials and products. Among

Homogenization of one-dimensional draining through heterogeneous porous media including higher-order approximations

Science.gov (United States)

Anderson, Daniel M.; McLaughlin, Richard M.; Miller, Cass T.

2018-02-01

We examine a mathematical model of one-dimensional draining of a fluid through a periodically-layered porous medium. A porous medium, initially saturated with a fluid of a high density is assumed to drain out the bottom of the porous medium with a second lighter fluid replacing the draining fluid. We assume that the draining layer is sufficiently dense that the dynamics of the lighter fluid can be neglected with respect to the dynamics of the heavier draining fluid and that the height of the draining fluid, represented as a free boundary in the model, evolves in time. In this context, we neglect interfacial tension effects at the boundary between the two fluids. We show that this problem admits an exact solution. Our primary objective is to develop a homogenization theory in which we find not only leading-order, or effective, trends but also capture higher-order corrections to these effective draining rates. The approximate solution obtained by this homogenization theory is compared to the exact solution for two cases: (1) the permeability of the porous medium varies smoothly but rapidly and (2) the permeability varies as a piecewise constant function representing discrete layers of alternating high/low permeability. In both cases we are able to show that the corrections in the homogenization theory accurately predict the position of the free boundary moving through the porous medium.

Block copolymer/homopolymer dual-layer hollow fiber membranes

KAUST Repository

Hilke, Roland; Neelakanda, Pradeep; Behzad, Ali Reza; Nunes, Suzana Pereira; Peinemann, Klaus-Viktor

2014-01-01

We manufactured the first time block copolymer dual-layer hollow fiber membranes and dual layer flat sheet membranes manufactured by double solution casting and phase inversion in water. The support porous layer was based on polystyrene

A proposed mechanism for investigating the effect of porous silicon buffer layer on TiO{sub 2} nanorods growth

Energy Technology Data Exchange (ETDEWEB)

Rahmani, N. [Department of Physics, Alzahra University, Tehran, 1993893973 (Iran, Islamic Republic of); Dariani, R.S., E-mail: dariani@alzahra.ac.ir [Department of Physics, Alzahra University, Tehran, 1993893973 (Iran, Islamic Republic of); Rajabi, M. [Deparment of Advanced Materials and Renewable Energies, Iranian Research Organization for Science and Technology (IROST), Tehran 3353136846 (Iran, Islamic Republic of)

2016-03-15

Graphical abstract: - Highlights: • TiO{sub 2} nanorods (NRs) are synthesized on silicon and porous silicon (PS) substrates by hydrothermal method. • TiO{sub 2} NRs grown on PS substrates have a better growth compared to those grown on silicon. • Also increasing substrate porosity leads to an increase in density of the NRs. • We proposed a growth mechanism to explain how can control the local surface chemical potential. - Abstract: In this study, we have synthesized TiO{sub 2} nanorods (NRs) on silicon and porous silicon (PS) substrates by hydrothermal method. The PS substrates with different porosities were fabricated by electrochemical anodization on silicon. According to the field emission electron microscopy images, TiO{sub 2} NRs grown on PS substrates have a better growth compared to those grown on silicon. Also increasing substrate porosity leads to an increase in density of the NRs. Atomic force microscopy observation demonstrates that porous layer formation due to etching of silicon surface leads to an increase of its roughness. Results indicate surface roughness evolution with porosity increasing enhances TiO{sub 2} nucleation on substrate and thus increases TiO{sub 2} NRs density. We propose a growth mechanism to explain how we can control the local surface chemical potential and thus the nucleation and alignment of TiO{sub 2} NRs by surface roughness variation. Also, photoluminescence studies show a red-shift in band gap energy of NRs compared to that of common bulk TiO{sub 2}.

Influence of the Surface Layer on the Electrochemical Deposition of Metals and Semiconductors into Mesoporous Silicon

Energy Technology Data Exchange (ETDEWEB)

Chubenko, E. B., E-mail: eugene.chubenko@gmail.com; Redko, S. V.; Sherstnyov, A. I.; Petrovich, V. A.; Kotov, D. A.; Bondarenko, V. P. [Belarusian State University of Information and RadioElectronics (Belarus)

2016-03-15

The influence of the surface layer on the process of the electrochemical deposition of metals and semiconductors into porous silicon is studied. It is shown that the surface layer differs in structure and electrical characteristics from the host porous silicon bulk. It is established that a decrease in the conductivity of silicon crystallites that form the surface layer of porous silicon has a positive effect on the process of the filling of porous silicon with metals and semiconductors. This is demonstrated by the example of nickel and zinc oxide. The effect can be used for the formation of nanocomposite materials on the basis of porous silicon and nanostructures with a high aspect ratio.

Influence of the Surface Layer on the Electrochemical Deposition of Metals and Semiconductors into Mesoporous Silicon

International Nuclear Information System (INIS)

Chubenko, E. B.; Redko, S. V.; Sherstnyov, A. I.; Petrovich, V. A.; Kotov, D. A.; Bondarenko, V. P.

2016-01-01

The influence of the surface layer on the process of the electrochemical deposition of metals and semiconductors into porous silicon is studied. It is shown that the surface layer differs in structure and electrical characteristics from the host porous silicon bulk. It is established that a decrease in the conductivity of silicon crystallites that form the surface layer of porous silicon has a positive effect on the process of the filling of porous silicon with metals and semiconductors. This is demonstrated by the example of nickel and zinc oxide. The effect can be used for the formation of nanocomposite materials on the basis of porous silicon and nanostructures with a high aspect ratio.

Optical characterization of nanocrystals in silicon rich oxide superlattices and porous silicon

International Nuclear Information System (INIS)

Agocs, E.; Petrik, P.; Milita, S.; Vanzetti, L.; Gardelis, S.; Nassiopoulou, A.G.; Pucker, G.; Balboni, R.; Fried, M.

2011-01-01

We propose to analyze ellipsometry data by using effective medium approximation (EMA) models. Thanks to EMA, having nanocrystalline reference dielectric functions and generalized critical point (GCP) model the physical parameters of two series of samples containing silicon nanocrystals, i.e. silicon rich oxide (SRO) superlattices and porous silicon layers (PSL), have been determined. The superlattices, consisting of ten SRO/SiO 2 layer pairs, have been prepared using plasma enhanced chemical vapor deposition. The porous silicon layers have been prepared using short monopulses of anodization current in the transition regime between porous silicon formation and electropolishing, in a mixture of hydrofluoric acid and ethanol. The optical modeling of both structures is similar. The effective dielectric function of the layer is calculated by EMA using nanocrystalline components (nc-Si and GCP) in a dielectric matrix (SRO) or voids (PSL). We discuss the two major problems occurring when modeling such structures: (1) the modeling of the vertically non-uniform layer structures (including the interface properties like nanoroughness at the layer boundaries) and (2) the parameterization of the dielectric function of nanocrystals. We used several techniques to reduce the large number of fit parameters of the GCP models. The obtained results are in good agreement with those obtained by X-ray diffraction and electron microscopy. We investigated the correlation of the broadening parameter and characteristic EMA components with the nanocrystal size and the sample preparation conditions, such as the annealing temperatures of the SRO superlattices and the anodization current density of the porous silicon samples. We found that the broadening parameter is a sensitive measure of the nanocrystallinity of the samples, even in cases, where the nanocrystals are too small to be visible for X-ray scattering. Major processes like sintering, phase separation, and intermixing have been

Wire rod coating process of gas diffusion layers fabrication for proton exchange membrane fuel cells

Energy Technology Data Exchange (ETDEWEB)

Kannan, A.M.; Sadananda, S.; Parker, D.; Munukutla, L. [Electronic Systems Department, Arizona State University, 7001 E Williams Field Road, Mesa, AZ 85212 (United States); Wertz, J. [Hollingsworth and Vose Co., A.K. Nicholson Research Lab, 219 Townsend Road West Groton, MA 01472 (United States); Thommes, M. [Quantachrome Instruments, 1900 Corporate Drive, Boynton Beach, FL 33426 (United States)

2008-03-15

Gas diffusion layers (GDLs) were fabricated using non-woven carbon paper as a macro-porous layer substrate developed by Hollingsworth and Vose Company. A commercially viable coating process was developed using wire rod for coating micro-porous layer by a single pass. The thickness as well as carbon loading in the micro-porous layer was controlled by selecting appropriate wire thickness of the wire rod. Slurry compositions with solid loading as high as 10 wt.% using nano-chain and nano-fiber type carbons were developed using dispersion agents to provide cohesive and homogenous micro-porous layer without any mud-cracking. The surface morphology, wetting characteristics and pore size distribution of the wire rod coated GDLs were examined using FESEM, Goniometer and Hg porosimetry, respectively. The GDLs were evaluated in single cell PEMFC under various operating conditions (temperature and RH) using hydrogen and air as reactants. It was observed that the wire rod coated micro-porous layer with 10 wt.% nano-fibrous carbon based GDLs showed the highest fuel cell performance at 85 C using H{sub 2} and air at 50% RH, compared to all other compositions. (author)

Influence of preparation and storage conditions on photoluminescence of porous silicon powder with embedded Si nanocrystals

International Nuclear Information System (INIS)

Bychto, Leszek; Balaguer, Maria; Pastor, Ester; Chirvony, Vladimir; Matveeva, Eugenia

2008-01-01

The time changes of photoluminescence (PL) characteristics of porous silicon (porSi) powder during storing in different ambients have been reported. A porous silicon material with embedded Si nanocrystals of size of few nanometers was prepared by an electrochemical method from 10 to 20 Ωcm p-type Si wafers, and both constant and pulse current anodization regimes were used. A powder with a submicron average particle size was obtained by simple mechanical lift-off of the porous layer followed by additional manual milling. The air, hexane, and water as storage media were used, and modification by a nonionic surfactant (undecylenic acid) of the porSi surface was applied in the latter case. Dependence of PL characteristics on preparation and storage conditions was then studied. A remarkable blue shift of a position of PL maximum was observed in time for porSi powders in each storage media. In water suspension a many-fold build-up (10-30) of PL intensity in a time scale of few days was accompanied by an observed blue shift. Photoluminescence time behavior of porSi powders was described by a known mechanism of the change of porSi PL from free exciton emission of Si nanocrystals to luminescence of localized oxidized states on the Si nanocrystal surface.

Influence of preparation and storage conditions on photoluminescence of porous silicon powder with embedded Si nanocrystals

Energy Technology Data Exchange (ETDEWEB)

Bychto, Leszek, E-mail: leszek.bychto@tu.koszalin.pl; Balaguer, Maria; Pastor, Ester; Chirvony, Vladimir; Matveeva, Eugenia, E-mail: eumat@upvnet.upv.e [Technical University of Valencia, Nanophotonics Technology Center (Spain)

2008-12-15

The time changes of photoluminescence (PL) characteristics of porous silicon (porSi) powder during storing in different ambients have been reported. A porous silicon material with embedded Si nanocrystals of size of few nanometers was prepared by an electrochemical method from 10 to 20 {Omega}cm p-type Si wafers, and both constant and pulse current anodization regimes were used. A powder with a submicron average particle size was obtained by simple mechanical lift-off of the porous layer followed by additional manual milling. The air, hexane, and water as storage media were used, and modification by a nonionic surfactant (undecylenic acid) of the porSi surface was applied in the latter case. Dependence of PL characteristics on preparation and storage conditions was then studied. A remarkable blue shift of a position of PL maximum was observed in time for porSi powders in each storage media. In water suspension a many-fold build-up (10-30) of PL intensity in a time scale of few days was accompanied by an observed blue shift. Photoluminescence time behavior of porSi powders was described by a known mechanism of the change of porSi PL from free exciton emission of Si nanocrystals to luminescence of localized oxidized states on the Si nanocrystal surface.

Influence of preparation and storage conditions on photoluminescence of porous silicon powder with embedded Si nanocrystals

Science.gov (United States)

Bychto, Leszek; Balaguer, Maria; Pastor, Ester; Chirvony, Vladimir; Matveeva, Eugenia

2008-12-01

The time changes of photoluminescence (PL) characteristics of porous silicon (porSi) powder during storing in different ambients have been reported. A porous silicon material with embedded Si nanocrystals of size of few nanometers was prepared by an electrochemical method from 10 to 20 Ωcm p-type Si wafers, and both constant and pulse current anodization regimes were used. A powder with a submicron average particle size was obtained by simple mechanical lift-off of the porous layer followed by additional manual milling. The air, hexane, and water as storage media were used, and modification by a nonionic surfactant (undecylenic acid) of the porSi surface was applied in the latter case. Dependence of PL characteristics on preparation and storage conditions was then studied. A remarkable blue shift of a position of PL maximum was observed in time for porSi powders in each storage media. In water suspension a many-fold build-up (10-30) of PL intensity in a time scale of few days was accompanied by an observed blue shift. Photoluminescence time behavior of porSi powders was described by a known mechanism of the change of porSi PL from free exciton emission of Si nanocrystals to luminescence of localized oxidized states on the Si nanocrystal surface.

Scattering characteristics from porous silicon

Directory of Open Access Journals (Sweden)

R. Sabet-Dariani

2000-12-01

Full Text Available   Porous silicon (PS layers come into existance as a result of electrochemical anodization on silicon. Although a great deal of research has been done on the formation and optical properties of this material, the exact mechanism involved is not well-understood yet.   In this article, first, the optical properties of silicon and porous silicon are described. Then, previous research and the proposed models about reflection from PS and the origin of its photoluminescence are reveiwed. The reflecting and scattering, absorption and transmission of light from this material, are then investigated. These experiments include,different methods of PS sample preparation their photoluminescence, reflecting and scattering of light determining different characteristics with respect to Si bulk.

Experimental, theoretical and numerical interpretation of thermodiffusion separation for a non-associating binary mixture in liquid/porous layers

International Nuclear Information System (INIS)

Ahadi, Amirhossein; Jawad, H.; Saghir, M.Z.; Giraudet, C.; Croccolo, F.; Bataller, H.

2014-01-01

Thermodiffusion in a hydrocarbon binary mixture has been investigated experimentally and numerically in a liquid-porous cavity. The solutal separation of the 50% toluene and 50% n-hexane binary mixture induced by a temperature difference at atmospheric pressure has been performed in a new thermodiffusion cell. A new optimized cell design is used in this study. The inner part of the cell is a cylindrical porous medium sandwiched between two liquid layers of the same binary hydrocarbon mixture. Experimental measurement and theoretical estimation of the molecular diffusion and thermodiffusion coefficients showed a good agreement. In order to understand the different regimes occurring in the different parts of the cell, a full transient numerical simulation of the solutal separation of the binary mixture has been performed. Numerical results showed that the lighter species, which are of n-hexane migrated toward the hot surface, while the denser species, which is toluene migrated towards the cold surface. Also, it was found that a good agreement has been reached between experimental measurements and numerical calculations for the solutal separation between the hot and cold surface for different medium porosity. In addition, we used the numerical results to analyse convection and diffusion regions in the cell precisely. (authors)

The quest for modular nanocages: Tbo -MOF as an archetype for mutual substitution, functionalization, and expansion of quadrangular pillar building blocks

KAUST Repository

Eubank, Jarrod F.

2011-09-14

A new blueprint network for the design and synthesis of porous, functional 3D metal-organic frameworks (MOFs) has been identified, namely, the tbo net. Accordingly, tbo-MOFs based on this unique (3,4)-connected net can be exclusively constructed utilizing a combination of well-known and readily targeted [M(R-BDC)]n MOF layers [i.e., supermolecular building layers (SBLs)] based on the edge-transitive 4,4 square lattice (sql) (i.e., 2D four-building units) and a novel pillaring strategy based on four proximal isophthalate ligands from neighboring SBL membered rings (i.e., two pairs from each layer) covalently cross-linked through an organic quadrangular core (e.g., tetrasubstituted benzene). Our strategy permits the rational design and synthesis of isoreticular structures, functionalized and/or expanded, that possess extra-large nanocapsule-like cages, high porosity, and potential for gas separation and storage, among others. Thus, tbo-MOF serves as an archetypal tunable, isoreticular MOF platform for targeting desired applications. © 2011 American Chemical Society.

The quest for modular nanocages: Tbo -MOF as an archetype for mutual substitution, functionalization, and expansion of quadrangular pillar building blocks

KAUST Repository

Eubank, Jarrod F.; Mouttaki, Hasnaa; Cairns, Amy; Belmabkhout, Youssef; Wojtas, Łukasz; Luebke, Ryan; Al Kordi, Mohamed; Eddaoudi, Mohamed

2011-01-01

A new blueprint network for the design and synthesis of porous, functional 3D metal-organic frameworks (MOFs) has been identified, namely, the tbo net. Accordingly, tbo-MOFs based on this unique (3,4)-connected net can be exclusively constructed utilizing a combination of well-known and readily targeted [M(R-BDC)]n MOF layers [i.e., supermolecular building layers (SBLs)] based on the edge-transitive 4,4 square lattice (sql) (i.e., 2D four-building units) and a novel pillaring strategy based on four proximal isophthalate ligands from neighboring SBL membered rings (i.e., two pairs from each layer) covalently cross-linked through an organic quadrangular core (e.g., tetrasubstituted benzene). Our strategy permits the rational design and synthesis of isoreticular structures, functionalized and/or expanded, that possess extra-large nanocapsule-like cages, high porosity, and potential for gas separation and storage, among others. Thus, tbo-MOF serves as an archetypal tunable, isoreticular MOF platform for targeting desired applications. © 2011 American Chemical Society.

2-periodic metal-organic frameworks (MOFs) as supermolecular building layers (SBLs) for making targeted 3-periodic MOFs

KAUST Repository

Eddaoudi, Mohamed; Eubank, Jarrod F.

2015-01-01

Embodiments of the present disclosure provide for chemical assemblies, multidimensional metal-organic frameworks (MOFs), supermolecular building layers (SBLs), inorganic molecular building blocks (MBBs), organic MBBs (designed ligands), methods of making each, and methods of using each, and the like. In an embodiment, the composition can be used in catalysis, separations, gas storage, and drug delivery.

2-periodic metal-organic frameworks (MOFs) as supermolecular building layers (SBLs) for making targeted 3-periodic MOFs

KAUST Repository

Eddaoudi, Mohamed

2015-09-22

Embodiments of the present disclosure provide for chemical assemblies, multidimensional metal-organic frameworks (MOFs), supermolecular building layers (SBLs), inorganic molecular building blocks (MBBs), organic MBBs (designed ligands), methods of making each, and methods of using each, and the like. In an embodiment, the composition can be used in catalysis, separations, gas storage, and drug delivery.

Fabrication of hierarchical flower-like porous ZnO nanostructures from layered ZnC2O4·3Zn(OH)2 and gas sensing properties

International Nuclear Information System (INIS)

Cui, Jiashan; Sun, Jianbo; Liu, Xin; Li, Jinwei; Ma, Xinzhi; Chen, Tingting

2014-01-01

ZnO materials with porous and hierarchical flower-like structure were synthesized through mild hydrothermal and simple calcination approach, in which the flower-like layered zinc oxalate hydroxide (ZnC 2 O 4 ·3Zn(OH) 2 ) precursor was first synthesized and then calcined at 600 °C. The obtained products were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopic (TEM), Brunauer–Emmett–Teller (BET) and thermogravimetric (TG) analysis. We proposed the possible growth mechanism of the material via studying the time evolution experiment results. In the process of reaction, oxalic acid as a structure-directing agent hydrolyzed and then formed primarily sheets-like intermediate ZnC 2 O 4 ·2H 2 O. Hexamethylenetetramine (HMT) as surfactant, with directional adsorption, leads to the formation of layered zinc oxalate hydroxide precursor. Furthermore, the gas sensitivity also can be characterized, whose results indicated that the synthesized materials had a preferable selectivity to ethanol gas. The fast response rate and reversible performance can be attributed to the produced greater specific surface area produced, which was caused by the porous and hierarchical flower-like structure.

Fabrication of hierarchical flower-like porous ZnO nanostructures from layered ZnC2O4·3Zn(OH)2 and gas sensing properties

Science.gov (United States)

Cui, Jiashan; Sun, Jianbo; Liu, Xin; Li, Jinwei; Ma, Xinzhi; Chen, Tingting

2014-07-01

ZnO materials with porous and hierarchical flower-like structure were synthesized through mild hydrothermal and simple calcination approach, in which the flower-like layered zinc oxalate hydroxide (ZnC2O4·3Zn(OH)2) precursor was first synthesized and then calcined at 600 °C. The obtained products were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopic (TEM), Brunauer-Emmett-Teller (BET) and thermogravimetric (TG) analysis. We proposed the possible growth mechanism of the material via studying the time evolution experiment results. In the process of reaction, oxalic acid as a structure-directing agent hydrolyzed and then formed primarily sheets-like intermediate ZnC2O4·2H2O. Hexamethylenetetramine (HMT) as surfactant, with directional adsorption, leads to the formation of layered zinc oxalate hydroxide precursor. Furthermore, the gas sensitivity also can be characterized, whose results indicated that the synthesized materials had a preferable selectivity to ethanol gas. The fast response rate and reversible performance can be attributed to the produced greater specific surface area produced, which was caused by the porous and hierarchical flower-like structure.

Sound transmission through stiffened double-panel structures lined with elastic porous materials

Science.gov (United States)

Mathur, Gopal P.; Tran, Boi N.; Bolton, J. S.; Shiau, Nae-Ming

This paper presents transmission loss prediction models for a periodically stiffened panel and stiffened double-panel structures using the periodic structure theory. The inter-panel cavity in the double-panels structures can be modeled as being separated by an airspace or filled with an elastic porous layer in various configurations. The acoustic behavior of elastic porous layer is described by a theory capable of accounting fully for multi-dimensional wave propagation in such materials. The predicted transmission loss of a single stiffened panel is compared with the measured data.

Porous Alumina Films with Width-Controllable Alumina Stripes

Directory of Open Access Journals (Sweden)

Huang Shi-Ming

2010-01-01

Full Text Available Abstract Porous alumina films had been fabricated by anodizing from aluminum films after an electropolishing procedure. Alumina stripes without pores can be distinguished on the surface of the porous alumina films. The width of the alumina stripes increases proportionally with the anodizing voltage. And the pores tend to be initiated close to the alumina stripes. These phenomena can be ascribed to the electric field distribution in the alumina barrier layer caused by the geometric structure of the aluminum surface.

Porous Alumina Films with Width-Controllable Alumina Stripes

Science.gov (United States)

2010-01-01

Porous alumina films had been fabricated by anodizing from aluminum films after an electropolishing procedure. Alumina stripes without pores can be distinguished on the surface of the porous alumina films. The width of the alumina stripes increases proportionally with the anodizing voltage. And the pores tend to be initiated close to the alumina stripes. These phenomena can be ascribed to the electric field distribution in the alumina barrier layer caused by the geometric structure of the aluminum surface. PMID:21170406

Fabricating solid carbon porous electrodes from powders

Science.gov (United States)

Kaschmitter, James L.; Tran, Tri D.; Feikert, John H.; Mayer, Steven T.

1997-01-01

Fabrication of conductive solid porous carbon electrodes for use in batteries, double layer capacitors, fuel cells, capacitive dionization, and waste treatment. Electrodes fabricated from low surface area (Electrodes having a higher surface area, fabricated from powdered carbon blacks, such as carbon aerogel powder, carbon aerogel microspheres, activated carbons, etc. yield high conductivity carbon compositives with excellent double layer capacity, and can be used in double layer capacitors, or for capacitive deionization and/or waste treatment of liquid streams. By adding metallic catalysts to be high surface area carbons, fuel cell electrodes can be produced.

Highly Efficient Electrocatalysts for Oxygen Reduction Reaction Based on 1D Ternary Doped Porous Carbons Derived from Carbon Nanotube Directed Conjugated Microporous Polymers

KAUST Repository

He, Yafei; Gehrig, Dominik; Zhang, Fan; Lu, Chenbao; Zhang, Chao; Cai, Ming; Wang, Yuanyuan; Laquai, Fré dé ric; Zhuang, Xiaodong; Feng, Xinliang

2016-01-01

© 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.One-dimensional (1D) porous materials have shown great potential for gas storage and separation, sensing, energy storage, and conversion. However, the controlled approach for preparation of 1D porous materials, especially porous organic materials, still remains a great challenge due to the poor dispersibility and solution processability of the porous materials. Here, carbon nanotube (CNT) templated 1D conjugated microporous polymers (CMPs) are prepared using a layer-by-layer method. As-prepared CMPs possess high specific surface areas of up to 623 m2 g-1 and exhibit strong electronic interactions between p-type CMPs and n-type CNTs. The CMPs are used as precursors to produce heteroatom-doped 1D porous carbons through direct pyrolysis. As-produced ternary heteroatom-doped (B/N/S) 1D porous carbons possess high specific surface areas of up to 750 m2 g-1, hierarchical porous structures, and excellent electrochemical-catalytic performance for oxygen reduction reaction. Both of the diffusion-limited current density (4.4 mA cm-2) and electron transfer number (n = 3.8) for three-layered 1D porous carbons are superior to those for random 1D porous carbon. These results demonstrate that layered and core-shell type 1D CMPs and related heteroatom-doped 1D porous carbons can be rationally designed and controlled prepared for high performance energy-related applications.

Highly Efficient Electrocatalysts for Oxygen Reduction Reaction Based on 1D Ternary Doped Porous Carbons Derived from Carbon Nanotube Directed Conjugated Microporous Polymers

KAUST Repository

He, Yafei

2016-10-11

© 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.One-dimensional (1D) porous materials have shown great potential for gas storage and separation, sensing, energy storage, and conversion. However, the controlled approach for preparation of 1D porous materials, especially porous organic materials, still remains a great challenge due to the poor dispersibility and solution processability of the porous materials. Here, carbon nanotube (CNT) templated 1D conjugated microporous polymers (CMPs) are prepared using a layer-by-layer method. As-prepared CMPs possess high specific surface areas of up to 623 m2 g-1 and exhibit strong electronic interactions between p-type CMPs and n-type CNTs. The CMPs are used as precursors to produce heteroatom-doped 1D porous carbons through direct pyrolysis. As-produced ternary heteroatom-doped (B/N/S) 1D porous carbons possess high specific surface areas of up to 750 m2 g-1, hierarchical porous structures, and excellent electrochemical-catalytic performance for oxygen reduction reaction. Both of the diffusion-limited current density (4.4 mA cm-2) and electron transfer number (n = 3.8) for three-layered 1D porous carbons are superior to those for random 1D porous carbon. These results demonstrate that layered and core-shell type 1D CMPs and related heteroatom-doped 1D porous carbons can be rationally designed and controlled prepared for high performance energy-related applications.

A theoretical study for the propagation of rolling noise over a porous road pavement

Science.gov (United States)

Keung Lui, Wai; Ming Li, Kai

2004-07-01

A simplified model based on the study of sound diffracted by a sphere is proposed for investigating the propagation of noise in a hornlike geometry between porous road surfaces and rolling tires. The simplified model is verified by comparing its predictions with the published numerical and experimental results of studies on the horn amplification of sound over a road pavement. In a parametric study, a point monopole source is assumed to be localized on the surface of a tire. In the frequency range of interest, a porous road pavement can effectively reduce the level of amplified sound due to the horn effect. It has been shown that an increase in the thickness and porosity of a porous layer, or the use of a double layer of porous road pavement, attenuates the horn amplification of sound. However, a decrease in the flow resistivity of a porous road pavement does little to reduce the horn amplification of sound. It has also been demonstrated that the horn effect over a porous road pavement is less dependent on the angular position of the source on the surface of tires.

Characterization of Tensile Mechanical Behavior of MSCs/PLCL Hybrid Layered Sheet

Directory of Open Access Journals (Sweden)

Azizah Intan Pangesty

2016-06-01

Full Text Available A layered construct was developed by combining a porous polymer sheet and a cell sheet as a tissue engineered vascular patch. The primary objective of this study is to investigate the influence of mesenchymal stem cells (MSCs sheet on the tensile mechanical properties of porous poly-(l-lactide-co-ε-caprolactone (PLCL sheet. The porous PLCL sheet was fabricated by the solid-liquid phase separation method and the following freeze-drying method. The MSCs sheet, prepared by the temperature-responsive dish, was then layered on the top of the PLCL sheet and cultured for 2 weeks. During the in vitro study, cellular properties such as cell infiltration, spreading and proliferation were evaluated. Tensile test of the layered construct was performed periodically to characterize the tensile mechanical behavior. The tensile properties were then correlated with the cellular properties to understand the effect of MSCs sheet on the variation of the mechanical behavior during the in vitro study. It was found that MSCs from the cell sheet were able to migrate into the PLCL sheet and actively proliferated into the porous structure then formed a new layer of MSCs on the opposite surface of the PLCL sheet. Mechanical evaluation revealed that the PLCL sheet with MSCs showed enhancement of tensile strength and strain energy density at the first week of culture which is characterized as the effect of MSCs proliferation and its infiltration into the porous structure of the PLCL sheet. New technique was presented to develop tissue engineered patch by combining MSCs sheet and porous PLCL sheet, and it is expected that the layered patch may prolong biomechanical stability when implanted in vivo.

Enhanced Stability of Li Metal Anode by using a 3D Porous Nickel Substrate

Energy Technology Data Exchange (ETDEWEB)

Yu, Lu; Canfield, Nathan L.; Chen, Shuru; Lee, Hongkyung; Ren, Xiaodi; Engelhard, Mark H.; Li, Qiuyan; Liu, Jun; Xu, Wu; Zhang, Jiguang

2018-03-02

Lithium (Li) metal is considered the “holy grail” anode for high energy density batteries, but its applications in rechargeable Li metal batteries are still hindered by the formation of Li dendrites and low Coulombic efficiency for Li plating/stripping. An effective strategy to stabilize Li metal is by embedding Li metal anode in a three-dimensional (3D) current collector. Here, a highly porous 3D Ni substrate is reported to effectively stabilize Li metal anode. Using galvanostatic intermittent titration technique combined with scanning electron microscopy, the underlying mechanism on the improved stability of Li metal anode is revealed. It is clearly demonstrated that the use of porous 3D Ni substrate can effectively suppress the formation of “dead” Li and forms a dense surface layer, whereas a porous “dead” Li layer is accumulated on the 2D Li metal which eventually leads to mass transport limitations. X-ray photoelectron spectroscopy results further revealed the compositional differences in the solid-electrolyte interphase layer formed on the Li metal embedded in porous 3D Ni substrate and the 2D copper substrate.

Preparation of activated carbon aerogels with hierarchically porous structures for electrical double layer capacitors

International Nuclear Information System (INIS)

Liu, Dong; Shen, Jun; Liu, Nianping; Yang, Huiyu; Du, Ai

2013-01-01

Activated carbon aerogels (ACAs) with hierarchically porous structures and high specific surface area have been prepared via CO 2 and KOH activation processes. The pore structures of ACAs are characterized by N 2 adsorption/desorption and scanning electron microscopy. The experimental results show that the ACAs contain three types of pores: micropores with diameters below 2 nm, small mesopores with diameters from 2 to 4 nm and large pores or channels with diameters over 30 nm. The typical sample ACAs-4, which possess pore volume of 2.73 cm 3 g −1 and specific surface area of 2119 m 2 g −1 , exhibits high specific capacitances of 250 F g −1 and 198 F g −1 at the current densities of 0.5 A g −1 and 20 A g −1 respectively in 6 M KOH aqueous solution. Furthermore, the resultant ACAs electrode materials also exhibit high power density, good cycling stability and long lifetime. With these features, ACAs are expected to be promising electrode materials for electrical double layer capacitors

Internal reforming of methane in a mono-block-layer build solid oxide fuel cell with an embedding porous pipe: Numerical analysis

International Nuclear Information System (INIS)

Ramírez-Minguela, J.J.; Mendoza-Miranda, J.M.; Muñoz-Carpio, V.D.; Rangel-Hernández, V.H.; Pérez-García, V.; Rodríguez-Muñoz, J.L.

2014-01-01

Highlights: • A MOLB-type SOFC with different biogas compositions is modeled. • Internal reforming of methane and water gas shift in the anode side are considered. • Changes in the SOFC according to the phenomena inside of them are assessed. • A new configuration for the MOLB-type geometry is proposed. • Temperature gradients effects in the new configuration are significant. - Abstract: A mono-block-layer build type (MOLB-type) geometry, composed with trapezoidal cross-section channels for fuel and air, of solid oxide fuel cell (SOFC), is modeled in this study using a three dimensional computational fluid dynamics (CFD). The model is used to obtain the performance of the SOFC considering internal reforming of methane in the anode side with different biogas compositions. From the results obtained, a new configuration for the MOLB-type geometry is proposed. The model takes into account the mass transfer, heat transfer, species transport, chemical and electrochemical reactions, detailed comparisons of species concentration, temperature and electric fields inside the cell analyzed in the present study. Results show that the biogas from local sludge has the lower temperature gradient and more homogeneous current density distributions along of the fuel cell, on the other hand, with the new configuration proposed for the MOLB-type geometry the temperature distribution inside of the fuel cell has lower temperature gradients

Observation of time-varying photoconductivity and persistent photoconductivity in porous silicon

DEFF Research Database (Denmark)

Frello, T.; Veje, E.; Leistiko, Otto

1996-01-01

We have observed time-varying photoconductivity and persistent photoconductivity in porous silicon, both with time-evolution scales of the order of several minutes or hours. The time evolutions depend on the wavelength and the intensity of the illuminating light. The data indicate the presence...... of at least two competing mechanisms, one is tentatively related to photoinduced creation of charge carriers in the silicon substrate followed by diffusion into the porous silicon layer, and the other is tentatively related to desorption of hydrogen from the porous silicon. ©1996 American Institute of Physics....

The Production of Porous Hydroxyapatite Scaffolds with Graded Porosity by Sequential Freeze-Casting.

Science.gov (United States)

Lee, Hyun; Jang, Tae-Sik; Song, Juha; Kim, Hyoun-Ee; Jung, Hyun-Do

2017-03-31

Porous hydroxyapatite (HA) scaffolds with porosity-graded structures were fabricated by sequential freeze-casting. The pore structures, compressive strengths, and biocompatibilities of the fabricated porous HA scaffolds were evaluated. The porosities of the inner and outer layers of the graded HA scaffolds were controlled by adjusting the initial HA contents of the casting slurries. The interface between the dense and porous parts was compact and tightly adherent. The porosity and compressive strengths of the scaffold were controlled by the relative thicknesses of the dense/porous parts. In addition, the porous HA scaffolds showed good biocompatibility in terms of preosteoblast cell attachment and proliferation. The results suggest that porous HA scaffolds with load-bearing parts have potential as bone grafts in hard-tissue engineering.

Luminescence and optical absorption determination in porous silicon

International Nuclear Information System (INIS)

Nogal, U.; Calderon, A.; Marin, E.; Rojas T, J. B.; Juarez, A. G.

2012-10-01

We applied the photoacoustic spectroscopy technique in order to obtain the optical absorption spectrum in porous silicon samples prepared by electrochemical anodic etching on n-type, phosphorous doped, (100)-oriented crystal-line silicon wafer with thickness of 300 μm and 1-5 ωcm resistivity. The porous layers were prepared with etching times of 13, 20, 30, 40 and 60 minutes. Also, we realized a comparison among the optical absorption spectrum with the photoluminescence and photo reflectance ones, both obtained at room temperature. Our results show that the absorption spectrum of the samples of porous silicon depends notably of the etching time an it consist of two distinguishable absorption bands, one in the Vis region and the other one in the UV region. (Author)

Single photoresist masking for local porous Si formation

International Nuclear Information System (INIS)

Hourdakis, E; Nassiopoulou, A G

2014-01-01

A simple process for local electrochemical porous Si formation on a Si wafer using a photoresist mask was developed. In this respect, the AZ9260 photoresist from MicroChemicals was used, which is easily removed by simple immersion in acetone after the electrochemical process. The photoresist layer thickness and its adhesion to the Si substrate were optimized for increased etch resistance to the anodization solution. Using the above process, mesoporous Si layers as thick as 50 μm were locally formed on the Si wafer through the photoresist mask. The developed process paves the way towards a simple industrial batch Si technology process for the fabrication of mixed Si wafers containing local porous Si areas. These wafers are very interesting for future system-on-chip (SoC) applications, including RF analog/digital and sensors/electronics SoCs. (technical note)

Effective diffusion coefficients of 3H2O in several porous materials

International Nuclear Information System (INIS)

Terashima, Yutaka; Kumaki, Toru.

1976-01-01

Diffusion coefficients of radionuclides in some porous structural materials and porous components of earth stratum are important as the basis for the safety evaluation of the storage and disposal of radioactive wastes. In our previous works, the method of analysis and experiment using a permeative type diffusion cell for measurement of effective diffusion coefficient was established, and experimental results were reported. In this paper, effective diffusion coefficients of 3 H 2 O in mortar, concrete, brick, clay layer, and sand layer were measured, and characteristics of these pore structure were discussed on the basis of tourtusity factor. (auth.)

Spreading of blood drops over dry porous substrate: complete wetting case.

Science.gov (United States)

Chao, Tzu Chieh; Arjmandi-Tash, Omid; Das, Diganta B; Starov, Victor M

2015-05-15

The process of dried blood spot sampling involves simultaneous spreading and penetration of blood into a porous filter paper with subsequent evaporation and drying. Spreading of small drops of blood, which is a non-Newtonian liquid, over a dry porous layer is investigated from both theoretical and experimental points of view. A system of two differential equations is derived, which describes the time evolution of radii of both the drop base and the wetted region inside the porous medium. The system of equations does not include any fitting parameters. The predicted time evolutions of both radii are compared with experimental data published earlier. For a given power law dependency of viscosity of blood with different hematocrit level, radii of both drop base and wetted region, and contact angle fell on three universal curves if appropriate scales are used with a plot of the dimensionless radii of the drop base and the wetted region inside the porous layer and dynamic contact angle on dimensionless time. The predicted theoretical relationships are three universal curves accounting satisfactorily for the experimental data. Copyright © 2015 The Authors. Published by Elsevier Inc. All rights reserved.

Investigation of the role of the micro-porous layer in polymer electrolyte fuel cells with hydrogen deuterium contrast neutron radiography.

Science.gov (United States)

Cho, Kyu Taek; Mench, Matthew M

2012-03-28

In this study, the high resolution hydrogen-deuterium contrast radiography method was applied to elucidate the impact of the micro-porous layer (MPL) on water distribution in the porous fuel cell media. At the steady state, deuterium replaced hydrogen in the anode stream, and the large difference in neutron attenuation of the D(2)O produced at the cathode was used to track the produced water. It was found that the water content peaked in the cathode-side diffusion media (DM) for the cell without MPL, but with an MPL on the anode and cathode DM, the peak water amount was pushed toward the anode, resulting in a relatively flattened water profile through components and demonstrating a liquid barrier effect. Additionally, the dynamic water behavior in diffusion media was analyzed to understand the effect of a MPL and operating conditions. The water content in the DM changed with applied current, although there is a significant amount of residual liquid content that does not appear to be part of capillary channels. The effect of the MPL on irreducible saturation in DM and cell performance was also investigated.

Effect of the local electric field on the formation of an ordered structure in porous anodic alumina

Science.gov (United States)

Lazarouk, S. K.; Katsuba, P. S.; Leshok, A. A.; Vysotskii, V. B.

2015-09-01

Experimental data and a model are presented, and the electric field that appears in porous alumina during electrochemical anodic oxidation of aluminum in electrolytes based on an aqueous solution of oxalic acid at a voltage of 90-250 V is calculated. It is found that the electric field in the layers with a porosity of 1-10% in growing alumina reaches 109-1010 V/m, which exceeds the electric strength of the material and causes microplasma patterns emitting visible light at the pore bottom, the self-organization of the structure of porous alumina, and the anisotropy of local porous anodizing. Moreover, other new effects are to be expected during aluminum anodizing under the conditions that ensure a high electric field inside the barrier layer of porous oxide.

The stability of second sound waves in a rotating Darcy–Brinkman porous layer in local thermal non-equilibrium

Energy Technology Data Exchange (ETDEWEB)

Eltayeb, I A; Elbashir, T B A, E-mail: ieltayeb@squ.edu.om, E-mail: elbashir@squ.edu.om [Department of Mathematics and Statistics, College of Science, Sultan Qaboos University, Muscat 123 (Oman)

2017-08-15

The linear and nonlinear stabilities of second sound waves in a rotating porous Darcy–Brinkman layer in local thermal non-equilibrium are studied when the heat flux in the solid obeys the Cattaneo law. The simultaneous action of the Brinkman effect (effective viscosity) and rotation is shown to destabilise the layer, as compared to either of them acting alone, for both stationary and overstable modes. The effective viscosity tends to favour overstable modes while rotation tends to favour stationary convection. Rapid rotation invokes a negative viscosity effect that suppresses the stabilising effect of porosity so that the stability characteristics resemble those of the classical rotating Benard layer. A formal weakly nonlinear analysis yields evolution equations of the Landau–Stuart type governing the slow time development of the amplitudes of the unstable waves. The equilibrium points of the evolution equations are analysed and the overall development of the amplitudes is examined. Both overstable and stationary modes can exhibit supercritical stability; supercritical instability, subcritical instability and stability are not possible. The dependence of the supercritical stability on the relative values of the six dimensionless parameters representing thermal non-equilibrium, rotation, porosity, relaxation time, thermal diffusivities and Brinkman effect is illustrated as regions in regime diagrams in the parameter space. The dependence of the heat transfer and the mean heat flux on the parameters of the problem is also discussed. (paper)

Numerical simulation of phase change material composite wallboard in a multi-layered building envelope

International Nuclear Information System (INIS)

Zwanzig, Stephen D.; Lian, Yongsheng; Brehob, Ellen G.

2013-01-01

Highlights: ► A numerical method to study the heat transfer through a PCM composite wallboard is presented. ► PCM wallboard can reduce energy consumption and shift peak electricity load. ► There is an optimal location for the PCM wallboard in the building envelop. ► The PCM wallboard performance depends on weather conditions. - Abstract: Phase change materials (PCMs) have the capability to store/release massive latent heat when undergoing phase change. When impregnated or encapsulated into wallboard or concrete systems, PCMs can greatly enhance their thermal energy storage capacity and effective thermal mass. When used in the building envelope PCM wallboard has the potential to improve building operation by reducing the energy requirement for maintaining thermal comfort, downsizing the AC/heating equipment, and shifting the peak load from the electrical grid. In this work we numerically studied the potential of PCM on energy saving for residential homes. For that purpose we solved the one-dimensional, transient heat equation through the multi-layered building envelope using the Crank–Nicolson discretization scheme. A source term is incorporated to account for the thermal-physical properties of the composite PCM wallboard. Using this code we examined a PCM composite wallboard incorporated into the walls and roof of a typical residential building across various climate zones. The PCM performance was studied under all seasonal conditions using the latest typical meteorological year (TMY3) data for exterior boundary conditions. Our simulations show that PCM performance highly depends on the weather conditions, emphasizing the necessity to choose different PCMs at different climate zones. Comparisons were also made between different PCM wallboard locations. Our work shows that there exists an optimal location for PCM placement within building envelope dependent upon the resistance values between the PCM layer and the exterior boundary conditions. We further

Porous SiC/SiC composites development for industrial application

International Nuclear Information System (INIS)

Maeta, S.; Hinoki, T.

2014-01-01

Silicon carbide (SiC) is promising structural materials in nuclear fields due to an excellent irradiation resistance and low activation characteristics. Conventional SiC fibers reinforced SiC matrix (SiC/SiC composites) fabricated by liquid phase sintering (LPS-SiC/SiC composites) have been required high cost and long processing time. And microstructure and mechanical property data of finally obtained LPS-SiC/SiC composites are easily scattered, because quality of the composites depend on personal skill. Thus, conventional LPS-SiC/SiC composites are inadequate for industrial use. In order to overcome these issues, the novel “porous SiC/SiC composites” have been developed by means of liquid phase sintering fabrication process. The composites consist of porous SiC matrix and SiC fibers without conventional carbon interfacial layer. The composites don’t have concerns of the degradation interfacial layer at the severe accident. Porous SiC/SiC composites preform was prepared with a thin sheet shape of SiC, sintering additives and carbon powder mixture by tape casting process which was adopted because of productive and high yielding rate fabrication process. The preform was stacked with SiC fibers and sintered in hot-press at the high temperature in argon environment. The sintered preform was decarburized obtain porous matrix structure by heat-treatment in air. Moreover, mechanical property data scattering of the obtained porous SiC/SiC composites decreased. In the flexural test, the porous SiC/SiC composites showed pseudo-ductile behavior with sufficient strength even after heat treatment at high temperature in air. From these conclusions, it was proven that porous SiC/SiC composites were reliable material at severe environment such as high temperature in air, by introducing tape casting fabrication process that could produce reproducible materials with low cost and simple way. Therefore development of porous SiC/SiC composites for industrial application was

Drying of a tape-cast layer: Numerical investigation of influencing parameters

DEFF Research Database (Denmark)

Jabbaribehnam, Mirmasoud; Shojaee Nasirabadi, Parizad; Jambhekar, V. A.

2017-01-01

, the equivalent diameter of particles of the porous medium, dp, the porosity of the porous medium, φ the initial temperature in the free-flow region, Tff, and the initial temperature in the porous-medium region, Tpm, on the characteristic drying curves of a thin ceramic layer. We, moreover, conduct a statistical...

Infrared reflectance studies of hillock-like porous zinc oxide thin films

International Nuclear Information System (INIS)

Ching, C.G.; Lee, S.C.; Ng, S.S.; Hassan, Z.; Abu Hassan, H.

2013-01-01

We investigated the infrared (IR) reflectance characteristics of hillock-like porous zinc oxide (ZnO) thin films on silicon substrates. The IR reflectance spectra of the porous samples exhibited an extra resonance hump in the reststrahlen region of ZnO compared with the as-grown sample. Oscillation fringes with different behaviors were also observed in the non-reststrahlen region of ZnO. Standard multilayer optic technique was used with the effective medium theory to analyze the observations. Results showed that the porous ZnO layer consisted of several sublayers with different porosities and thicknesses. These findings were confirmed by scanning electron microscopy measurements. - Highlights: • Multilayer porous assumption qualitatively increased the overall spectra fitting. • IR reflectance is a sensitive method to probe the multilayer porous structure. • Hillock-like porous ZnO thin films fabricated using electrochemical etching method. • The thickness and porosity of the samples were determined. • Formation of extra resonance hump was due to splitting of reststrahlen band

Selectivity Enhancement by Using Double-Layer MOX-Based Gas Sensors Prepared by Flame Spray Pyrolysis (FSP

Directory of Open Access Journals (Sweden)

Julia Rebholz

2016-09-01

Full Text Available Here we present a novel concept for the selective recognition of different target gases with a multilayer semiconducting metal oxide (SMOX-based sensor device. Direct current (DC electrical resistance measurements were performed during exposure to CO and ethanol as single gases and mixtures of highly porous metal oxide double- and single-layer sensors obtained by flame spray pyrolysis. The results show that the calculated resistance ratios of the single- and double-layer sensors are a good indicator for the presence of specific gases in the atmosphere, and can constitute some building blocks for the development of chemical logic devices. Due to the inherent lack of selectivity of SMOX-based gas sensors, such devices could be especially relevant for domestic applications.

Highly efficient forward osmosis based on porous membranes--applications and implications.

Science.gov (United States)

Qi, Saren; Li, Ye; Zhao, Yang; Li, Weiyi; Tang, Chuyang Y

2015-04-07

For the first time, forward osmosis (FO) was performed using a porous membrane with an ultrafiltration (UF)-like rejection layer and its feasibility for high performance FO filtration was demonstrated. Compared to traditional FO membranes with dense rejection layers, the UF-like FO membrane was 2 orders of magnitude more permeable. This gave rise to respectable FO water flux even at ultralow osmotic driving force, for example, 7.6 L/m(2).h at an osmotic pressure of merely 0.11 bar (achieved by using a 0.1% poly(sodium 4-styrene-sulfonate) draw solution). The membrane was applied to oil/water separation, and a highly stable FO water flux was achieved. The adoption of porous FO membranes opens a door to many new opportunities, with potential applications ranging from wastewater treatment, valuable product recovery, and biomedical applications. The potential applications and implications of porous FO membranes are addressed in this paper.

Heat and mass transfer on a MHD third grade fluid with partial slip flow past an infinite vertical insulated porous plate in a porous medium

International Nuclear Information System (INIS)

Baoku, I.G.; Olajuwon, B.I.; Mustapha, A.O.

2013-01-01

Highlights: ► We model the flow of a MHD third grade fluid, heat and mass transfer in a porous medium with partial slip flow regime. ► We examine the effects of pertinent parameters on the velocity, temperature and species concentration distributions. ► The values momentum and thermal boundary layers increase with increasing third grade parameter β. ► The consequences of increasing the permeability parameter m and partial slip parameter λ give rise to fluid velocity. ► The magnetic field parameter H decreases the momentum boundary layer and increases the concentration boundary layer. -- Abstract: The influence of third grade, partial slip and other thermophysical parameters on the steady flow, heat and mass transfer of viscoelastic third grade fluid past an infinite vertical insulated plate subject to suction across the boundary layer has been investigated. The space occupying the fluid is porous. The momentum equation is characterized by a highly nonlinear boundary value problem in which the order of the differential equation exceeds the number of available boundary conditions. An efficient numerical scheme of midpoint technique with Richardson’s extrapolation is employed to solve the governing system of coupled nonlinear equations of momentum, energy and concentration. Numerical calculations were carried out for different values of various interesting non-dimensional quantities in the slip flow regime with heat and mass transfer and were shown with the aid of figures. The values of the wall shear stress, the local rate of heat and mass transfers were obtained and tabulated. The analysis shows that as the fluid becomes more shear thickening, the momentum boundary layer decreases but the thermal boundary layer increases; the magnetic field strength is found to decrease with an increasing temperature distribution when the porous plate is insulated. The consequences of increasing the permeability parameter and Schmidt number decrease both the momentum

Adsorption and separation of propane and propylene by porous hexacyanometallates

International Nuclear Information System (INIS)

Autie-Castro, G.; Autie, M.; Reguera, E.; Moreno-Tost, R.; Rodriguez-Castellon, E.; Jimenez-Lopez, A.; Santamaria-Gonzalez, J.

2011-01-01

The separation capability for mixtures of propane and propylene by porous frameworks representatives of transition metal hexacyanometallates was studied from adsorption data under equilibrium conditions at 273.15 K and from inverse gas chromatography profiles at different column temperatures. Samples of two porous solids were considered; Cd 3 [Co(CN) 6 ] 2 , which is representative of Prussian blue analogues (cubic structure) with a porous framework related to vacancies for building block, and Zn 3 [Co(CN) 6 ] 2 (rhombohedral phase) where the porous framework results from the tetrahedral coordination for the Zn atoms. The two materials were found to be able for the mixtures separation, with the highest separation ability for the rhombohedral phase under equilibrium conditions but, in dynamic conditions the cubic one shown a better separation, which was ascribed to a kinetic contribution related to a smaller windows size.

Pseudocapacitive and hierarchically ordered porous electrode materials supercapacitors

Science.gov (United States)

Saruhan, B.; Gönüllü, Y.; Arndt, B.

2013-05-01

Commercially available double layer capacitors store energy in an electrostatic field. This forms in the form of a double layer by charged particles arranged on two electrodes consisting mostly of active carbon. Such double layer capacitors exhibit a low energy density, so that components with large capacity according to large electrode areas are required. Our research focuses on the development of new electrode materials to realize the production of electrical energy storage systems with high energy density and high power density. Metal oxide based electrodes increase the energy density and the capacitance by addition of pseudo capacitance to the static capacitance present by the double layer super-capacitor electrodes. The so-called hybrid asymmetric cell capacitors combine both types of energy storage in a single component. In this work, the production routes followed in our laboratories for synthesis of nano-porous and aligned metal oxide electrodes using the electrochemical and sputter deposition as well as anodization methods will be described. Our characterisation studies concentrate on electrodes having redox metal-oxides (e.g. MnOx and WOx) and hierarchically aligned nano-porous Li-doped TiO2-NTs. The material specific and electrochemical properties achieved with these electrodes will be presented.

Deposited Micro Porous Layer as Lubricant Carrier in Metal Forming

DEFF Research Database (Denmark)

Arentoft, Mogens; Bay, Niels; Tang, Peter Torben

2008-01-01

as lubricant reservoirs. Conventional friction tests for cold forming; ring compression and double cup extrusion tests are carried out with Molykote DX paste and mineral oil as lubricant. Both lubricants act as intended for the ring compressions test whereas only the low viscosity oil perform successfully...... in the cup extrusion test. For all specimens without the porous coating, high friction conditions are identified....

Extending the Lifespan of Porous Asphalt Concrete

NARCIS (Netherlands)

Zhang, Y.

2015-01-01

Porous Asphalt (PA) concrete is widely used as a surfacing layer on highways in the Netherlands. The service life of PA wearing courses is limited because of the fact that it is vulnerable to raveling. The possibilities of applying preventive maintenance to PA wearing courses by means of spraying

Modeling of heat and mass transfer in lateritic building envelopes

International Nuclear Information System (INIS)

Meukam, Pierre

2004-10-01

The aim of the present work is to investigate the behavior of building envelopes made of local lateritic soil bricks subjected to different climatic conditions. The analysis is developed for the prediction of the temperature, relative humidity and water content behavior within the walls. The building envelopes studied in this work consist of lateritic soil bricks with incorporation of natural pozzolan or sawdust in order to obtain small thermal conductivity and low-density materials, and limit the heat transfer between the atmospheric climate and the inside environment. In order to describe coupled heat and moisture transfer in wet porous materials, the coupled equations were solved by the introduction of diffusion coefficients. A numerical model HMtrans, developed for prediction of beat and moisture transfer in multi-layered building components, was used to simulate the temperature, water content and relative humidity profiles within the building envelopes. The results allow the prediction of the duration of the exposed building walls to the local weather conditions. They show that for any of three climatic conditions considered, relative humidity and water content do not exceed 87% and 5% respectively. There is therefore minimum possibility of water condensation in the materials studied. The durability of building envelopes made of lateritic soil bricks with incorporation of natural pozzolan or sawdust is not strongly affected by the climatic conditions in tropical and equatorial regions. (author)

Conductive polymer layers to limit transfer of fuel reactants to catalysts of fuel cells to reduce reactant crossover

Science.gov (United States)

Stanis, Ronald J.; Lambert, Timothy N.

2016-12-06

An apparatus of an aspect includes a fuel cell catalyst layer. The fuel cell catalyst layer is operable to catalyze a reaction involving a fuel reactant. A fuel cell gas diffusion layer is coupled with the fuel cell catalyst layer. The fuel cell gas diffusion layer includes a porous electrically conductive material. The porous electrically conductive material is operable to allow the fuel reactant to transfer through the fuel cell gas diffusion layer to reach the fuel cell catalyst layer. The porous electrically conductive material is also operable to conduct electrons associated with the reaction through the fuel cell gas diffusion layer. An electrically conductive polymer material is coupled with the fuel cell gas diffusion layer. The electrically conductive polymer material is operable to limit transfer of the fuel reactant to the fuel cell catalyst layer.

TiO2-Impregnated Porous Silica Tube and Its Application for Compact Air- and Water-Purification Units

Directory of Open Access Journals (Sweden)

Tsuyoshi Ochiai

2015-09-01

Full Text Available A simple, convenient, reusable, and inexpensive air- and water-purification unit including a one-end sealed porous amorphous-silica (a-silica tube coated with TiO2 photocatalyst layers has been developed. The porous a-silica layers were formed through outside vapor deposition (OVD. TiO2 photocatalyst layers were formed through impregnation and calcination onto a-silica layers. The resulting porous TiO2-impregnated a-silica tubes were evaluated for air-purification capacity using an acetaldehyde gas decomposition test. The tube (8.5 mm e.d. × 150 mm demonstrated a 93% removal rate for high concentrations (ca. 300 ppm of acetaldehyde gas at a single-pass condition with a 250 mL/min flow rate under UV irradiation. The tube also demonstrated a water purification capacity at a rate 2.0 times higher than a-silica tube without TiO2 impregnation. Therefore, the tubes have a great potential for developing compact and in-line VOC removal and water-purification units.

Membranes having aligned 1-D nanoparticles in a matrix layer for improved fluid separation

Science.gov (United States)

Revanur, Ravindra; Lulevich, Valentin; Roh, Il Juhn; Klare, Jennifer E.; Kim, Sangil; Noy, Aleksandr; Bakajin, Olgica

2015-12-22

Membranes for fluid separation are disclosed. These membranes have a matrix layer sandwiched between an active layer and a porous support layer. The matrix layer includes 1-D nanoparticles that are vertically aligned in a porous polymer matrix, and which substantially extend through the matrix layer. The active layer provides species-specific transport, while the support layer provides mechanical support. A matrix layer of this type has favorable surface morphology for forming the active layer. Furthermore, the pores that form in the matrix layer tend to be smaller and more evenly distributed as a result of the presence of aligned 1-D nanoparticles. Improved performance of separation membranes of this type is attributed to these effects.

Corrosion of porous silicon in tetramethylammonium hydroxide solution

International Nuclear Information System (INIS)

Lai, Chuan; Li, Xue-Ming; Zou, Li-Ke; Chen, Qiang; Xie, Bin; Li, Yu-Lian; Li, Xiao-Lin; Tao, Zhi

2014-01-01

Highlights: • The corrosion of porous silicon in (CH 3 ) 4 NOH solution was studied. • The residue of corrosion products was a mixture of [(CH 3 ) 4 N] 2 SiO 3 and SiO 2 . • The effect factors for porous silicon corrosion were elaborately investigated. • The additive of ethanol in (CH 3 ) 4 NOH solution could reduce the corrosion rate. • The 1.0 M (CH 3 ) 4 NOH could act as an applicable and novel corrosion solution. - Abstract: Corrosion of porous silicon in tetramethylammonium hydroxide (TMAH) solution was studied using weight loss measurements and scanning electron microscope. The effects of temperature, concentration of TMAH and volume ratio of ethanol in 1.0 M TMAH on corrosion rate and corrosion time were elaborately investigated. The residue of corrosion products were characterized as a mixture of [(CH 3 ) 4 N] 2 SiO 3 and SiO 2 . A comparative test among TMAH, KOH and NaOH illustrated that the 1.0 M TMAH could act as an applicable and novel corrosion solution to remove porous silicon layer for determining the porosity of porous silicon

Micro-length anodic porous niobium oxide for lithium-ion thin film battery applications

International Nuclear Information System (INIS)

Yoo, Jeong Eun; Park, Jiyoung; Cha, Gihoon; Choi, Jinsub

2013-01-01

The anodization of niobium in an aqueous mixture of H 3 PO 4 and HF in the potential range from 2.5 to 30 V for 2 h at 5 °C was performed, demonstrating that anodic porous niobium oxide film with a thickness of up to 2000 nm, including a surface dissolution layer, can be obtained by controlling the applied potential and composition of the electrolytes. Specifically, surface dissolution-free porous niobium oxide film with a thickness of 800 nm can be prepared in a low electrolyte concentration. The surface dissolution is observed when the concentration ratio of HF (wt.%):H 3 PO 4 (M) was more than 2:1. The discontinuous layers in the niobium oxide film were observed when the thickness was higher than 500 nm, which was ascribed to the large volume expansion of the niobium oxide grown from the niobium metal. The anodic porous niobium oxide film was used as the cathode for lithium-ion batteries in the potential range from 1.2 to 3.0 V at a current density of 7.28 × 10 − 6 A cm −2 . The first discharge capacity of ca. 53 μA h cm − 2 was obtained in 800 nm thick niobium oxide without a surface dissolution layer. - Highlights: ► Anodic porous niobium oxide film with a thickness of 2000 nm was obtained. ► Surface dissolution-free porous niobium oxide film was prepared. ► The niobium oxide film was used as the cathode for lithium-ion batteries

Experimental investigation of the effect of a passive porous coating on a hypersonic boundary layer stability on a sharp cone at an angle of attack

Science.gov (United States)

Lukashevich, S. V.; Morozov, S. O.; Shiplyuk, A. N.

2018-03-01

Experimental investigations are performed to determine the effect of the passive porous coating on the stability of the hypersonic boundary layer on the cone at small angles of attack. Measurements of the pressure disturbances on the cone surface showed that, the increase of the angle of attack leads to decrease of the second-mode amplitude, when the smooth cone side is the windward side. On the leeward side the amplitude of the disturbances increase with the angle of attack until the boundary layer is laminar. It was found that the ultrasonically absorptive coating leads to the energy decrease of the second-mode disturbances on both leeward and windward side of the sharp cone.

Vapor phase epitaxy of silicon on meso porous silicon for deposition on economical substrate and low cost photovoltaic application

International Nuclear Information System (INIS)

Quoizola, S.

2003-01-01

The silicon is more and more used in the industry. Meanwhile the production cost is a problem to solve to develop the photovoltaic cells production. This thesis presents a new technology based on the use of a meso-porous silicon upper layer,to grow the active silicon layer of 50 μm width. The photovoltaic cell is then realized, the device is removed and placed on a low cost substrate. The silicon substrate of beginning can be used again after cleaning. The first chapter presents the operating and the characteristics of the silicon photovoltaic cell. The second chapter is devoted to the growth technique, the vapor phase epitaxy, and the third chapter to the epitaxy layer. The chapter four deals with the porous silicon and the structure chosen in this study. The chapter five is devoted to the characterization of the epitaxy layer on porous silicon. The photovoltaic cells realized on these layers are presented in the last chapter. (A.L.B.)

Applying macromolecular crowding to 3D bioprinting: fabrication of 3D hierarchical porous collagen-based hydrogel constructs.

Science.gov (United States)

Ng, Wei Long; Goh, Min Hao; Yeong, Wai Yee; Naing, May Win

2018-02-27

Native tissues and/or organs possess complex hierarchical porous structures that confer highly-specific cellular functions. Despite advances in fabrication processes, it is still very challenging to emulate the hierarchical porous collagen architecture found in most native tissues. Hence, the ability to recreate such hierarchical porous structures would result in biomimetic tissue-engineered constructs. Here, a single-step drop-on-demand (DOD) bioprinting strategy is proposed to fabricate hierarchical porous collagen-based hydrogels. Printable macromolecule-based bio-inks (polyvinylpyrrolidone, PVP) have been developed and printed in a DOD manner to manipulate the porosity within the multi-layered collagen-based hydrogels by altering the collagen fibrillogenesis process. The experimental results have indicated that hierarchical porous collagen structures could be achieved by controlling the number of macromolecule-based bio-ink droplets printed on each printed collagen layer. This facile single-step bioprinting process could be useful for the structural design of collagen-based hydrogels for various tissue engineering applications.

Enhanced Properties of Porous GaN Prepared by UV Assisted Electrochemical Etching

International Nuclear Information System (INIS)

Ainorkhilah Mahmood; Ainorkhilah Mahmood; Siang, C.L.

2011-01-01

The structural and optical properties of porous GaN films on sapphire (0001) prepared by UV assisted electrochemical etching were reported in this study. SEM micrographs indicated that the shapes of the pores for both porous samples are nearly hexagonal. XRD revealed that the broadening in spectrum is due to the small size crystallites. As compared to the as grown GaN films, porous layers exhibit a substantial photoluminescence (PL) intensity enhancement with red-shifted band-edge PL peaks associated with the relaxation of compressive stress. The shift of E2(high) to the lower frequency in Raman spectra of the porous GaN films further confirms such a stress relaxation. (author)

PAT and SEM study of porous silicon formed by anodization methods

International Nuclear Information System (INIS)

Liu Jian; Wei Long; Wang Huiyao; Ma Chuangxin; Wang Baoyi

2000-01-01

The porous silicon formed by anodization of crystal silicon was studied by positron annihilation technique (PAT) and scanning electron microscopy (SEM). The PAT experiments showed that the mean life and vacancy defects increased with the increasing anodization time. While the intensities of the longest lifetime, several ns-tens ns (ortho-positronium) dropped down. Small single-crystal Si spheres with mean radius of a few μm were observed by SEM after anodization. Pits with mean radius of a few μm from the divorcement of single-crystal spheres were also observed after further anodization. The increases of vacancy defects might be that the extension of structures of porous silicon towards inner layer with anodization time and caused more vacancy defects in inner layer. The SEM observation presented another possibility of the increase of density of vacancy defects in surface layer induced by the change of structures

Unsteady MHD free convective flow past a vertical porous plate ...

African Journals Online (AJOL)

user

International Journal of Engineering, Science and Technology .... dimensional MHD boundary layer on the body with time varying temperature. ... flow of an electrically conducting fluid past an infinite vertical porous flat plate coinciding with.

Adsorption and separation of propane and propylene by porous hexacyanometallates

Energy Technology Data Exchange (ETDEWEB)

Autie-Castro, G. [Instituto de Ciencia y Tecnologia de Materiales, Universidad de La Habana (Cuba); Autie, M. [Instituto de Ciencia y Tecnologia de Materiales, Universidad de La Habana (Cuba); Centro de Ingenieria y Proyectos (CIPRO), ISPJAE, La Habana (Cuba); Reguera, E., E-mail: ereguera@yahoo.com [Instituto de Ciencia y Tecnologia de Materiales, Universidad de La Habana (Cuba); Centro de Investigacion en Ciencia Aplicada y Tecnologia Avanzada del IPN, Unidad Legaria, Mexico DF (Mexico); Moreno-Tost, R.; Rodriguez-Castellon, E.; Jimenez-Lopez, A.; Santamaria-Gonzalez, J. [Departamento de Quimica Inorganica, Cristalografia y Mineralogia, Facultad de Ciencias, Universidad de Malaga (Spain)

2011-01-15

The separation capability for mixtures of propane and propylene by porous frameworks representatives of transition metal hexacyanometallates was studied from adsorption data under equilibrium conditions at 273.15 K and from inverse gas chromatography profiles at different column temperatures. Samples of two porous solids were considered; Cd{sub 3}[Co(CN){sub 6}]{sub 2}, which is representative of Prussian blue analogues (cubic structure) with a porous framework related to vacancies for building block, and Zn{sub 3}[Co(CN){sub 6}]{sub 2} (rhombohedral phase) where the porous framework results from the tetrahedral coordination for the Zn atoms. The two materials were found to be able for the mixtures separation, with the highest separation ability for the rhombohedral phase under equilibrium conditions but, in dynamic conditions the cubic one shown a better separation, which was ascribed to a kinetic contribution related to a smaller windows size.

Hydroxyapatite nanorod-assembled porous hollow polyhedra as drug/protein carriers.

Science.gov (United States)

Yu, Ya-Dong; Zhu, Ying-Jie; Qi, Chao; Jiang, Ying-Ying; Li, Heng; Wu, Jin

2017-06-15

Hydroxyapatite (HAP) with a porous hollow structure is an ideal biomaterial owing to its excellent biocompatibility and unique architecture. In this study, HAP nanorod-assembled porous hollow polyhedra, consisting of nanorod building blocks, have been successfully prepared at room temperature or under hydrothermal circumstances using a self-sacrificing Ca(OH) 2 template strategy. The hydrothermal treatment (at 180°C for 1h) can promote the HAP nanorods to be arranged with their axial direction normal to the polyhedron surface. The HAP nanorod-assembled porous hollow polyhedra have been explored for the potential application in drug/protein delivery, using ibuprofen (IBU) as a model drug and hemoglobin (Hb) as a model protein. The experimental results indicate that the HAP nanorod-assembled porous hollow polyhedra have a relatively high drug loading capacity and protein adsorption ability, and sustained drug and protein release. The HAP nanorod-assembled porous hollow polyhedra have promising applications in various biomedical fields such as the drug and protein delivery. Copyright © 2017 Elsevier Inc. All rights reserved.

Effect of potential steps on porous silicon formation

International Nuclear Information System (INIS)

Cheng Xuan; Feng Zude; Luo Guangfeng

2003-01-01

Porous silicon microstructures were fabricated by applying potential steps through which both anodic and cathodic potentials were periodically applied to silicon wafers. The electrochemical behaviors of porous silicon layers were examined by performing polarization measurements, followed by analyzing the open-circuit potential (E ocp ) and the reaction rate in terms of corrosion current density (j corr ). The surface morphologies and surface products of porous silicon were characterized by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). It was found that the values of E ocp and j corr varied more significantly and irregularly during different polarization stages when the potentials were continuously applied to the wafer surface, while virtually unchanged after 2 min of periodic potential application. In addition, slower reaction rates were observed with applying potential steps, as indicated by smaller values of j corr . The enhancement on refreshment of silicon surfaces by periodic potential polarization significantly accelerated the growth of porous silicon. The microstructures became more uniformed and better defined due to the improved passivating nature of wafer surfaces

Modelling critical degrees of saturation of porous building materials subjected to freezing

DEFF Research Database (Denmark)

Hansen, Ernst Jan De Place

1996-01-01

of SCR based on fracture mechanics and phase geometry of two-phase materials has been developed.The degradation is modelled as being caused by different eigenstrains of the pore phase and the solid phase when freezing, leading to stress concentrations and crack propagation. Simplifications are made......Frost resistance of porous materials can be characterized by the critical degree of saturation, SCR, and the actual degree of saturation, SACT. An experimental determination of SCR is very laborious and therefore only seldom used when testing frost resistance. A theoretical model for prediction...... to describe the development of stresses and the pore structure, because a mathematical description of the physical theories explaining the process of freezing of water in porous materials is lacking.Calculations are based on porosity, modulus of elasticity and tensile strength, and parameters characterizing...

Light propagation in one-dimensional porous silicon complex systems

NARCIS (Netherlands)

Oton, C.J.; Dal Negro, L.; Gaburro, Z.; Pavesi, L.; Johnson, P.J.; Lagendijk, Aart; Wiersma, D.S.

2003-01-01

We discuss the optical properties of one-dimensional complex dielectric systems, in particular the time-resolved transmission through thick porous silicon quasiperiodic multi-layers. Both in numerical calculations and experiments we find dramatic distortion effects, i.e. pulse stretching and

Simultaneous heat and moisture transfer in soils combined with building simulation

Energy Technology Data Exchange (ETDEWEB)

Santos, G. H. dos; Mendes, N. [Pontifical Catholic University of Parana, PUCPR/CCET, Thermal Systems Laboratory (LST), Curitiba (Brazil)

2006-07-01

In order to precisely predict ground heat transfer, room air temperature and humidity, a combined model has been developed and conceived to calculate both the coupled heat and moisture transfer in soil and floor and the psychrometrics condition of indoor air. The present methodology for the soil is based on the theory of Philip and De Vries, using variable thermophysical properties for different materials. The governing equations were discretized using the finite-volume method and a three-dimensional model for describing the physical phenomena of heat and mass transfer in unsaturated moist porous soils and floor. Additionally, a lumped transient approach for a building room and a finite-volume multi-layer model for the building envelope have been developed to integrate with the soil model. Results are presented in terms of temperature, humidity and heat flux at the interface between room air and the floor, showing the importance of the approach presented and the model robustness for long-term simulations with a high time step. (author)

Mechanical Properties of Porous Titanium Structure Fabricated by Investment Casting with Pressurization/Depressurization System

International Nuclear Information System (INIS)

Kang, San; Lee, Ji-Woon; Hyun, Soong-Keun; Lee, Byong-Pil; Kim, Myoung-Gyun; Kim, Young-Jig

2014-01-01

A porous titanium structure was fabricated by investment casting with a pressurization/depressurization system, and its mechanical properties were studied. A Micro-Vickers hardness profile revealed that hardness gradually increased from the matrix to the metal/mold interface. A compression test was conducted on a single cell of the porous Ti structure. The theoretical and experimental values of yield strength were in good agreement. Such agreement suggested that the reaction layer did not affect the macro-mechanical properties of the porous Ti structure.

Experiential study on temperature and emission performance of micro burner during porous media combustion

Science.gov (United States)

Janvekar, Ayub Ahmed; Abdullah, M. Z.; Ahmad, Z. A.; Abas, A.; Ismail, A. K.; Hussien, A. A.; Kataraki, P. S.; Ishak, M. H. H.; Mazlan, M.; Zubair, A. F.

2018-05-01

Addition of porous materials in reaction zone give rise to significant improvements in combustion performance. In this work, a dual layered micro porous media burner was tested for stable flame and emissions. Reaction and preheat layer was made up of discrete (zirconia) and foam (porcelain) type of materials respectively. Three different thickness of reaction zone was tested, each with 10, 20 and 30mm. Interestingly, only 20mm thick layer can able to show better thermal efficiency of 72% as compared to 10 and 30mm. Best equivalence ratio came out to be 0.7 for surface and 0.6 for submerged flame conditions. Moreover, emission was continuously monitored to detect presence of NOx and CO, which were under controlled limits.

Irreversible membrane fouling abatement through pre-deposited layer of hierarchical porous carbons

KAUST Repository

Hamad, Juma; Dua, Rubal; Kurniasari, Novita; Kennedy, Maria Dolores; Wang, Peng; Amy, Gary L.

2014-01-01

In this work, dual-templated hierarchical porous carbons (HPCs), produced from a coupled ice-hard templating approach, are shown to be a highly effective solution to the commonly occurring problem of irreversible fouling of low-pressure membranes

Formation of Defect-Free Latex Films on Porous Fiber Supports

KAUST Repository

Lively, Ryan P.; Mysona, Joshua A.; Chance, Ronald R.; Koros, William J.

2011-01-01

a defect-free lumen-side barrier layer can be created. Film experiments examined the effect of drying rate, latex age, substrate porosity (porous vs nonporous), and substrate hydrophobicity/ hydrophilicity. Film studies show that in ideal conditions

Energy transfer in porous anodic alumina/rhodamine 110 nanocomposites

Energy Technology Data Exchange (ETDEWEB)

Elhouichet, H., E-mail: habib.elhouichet@fst.rnu.tn [Laboratoire de Physico-Chimie des Materiaux Mineraux et leurs Applications, Centre National de Recherches en Sciences des Materiaux, B.P. 95, Hammam-Lif 2050 (Tunisia); Departement de Physique, Faculte des Sciences de Tunis, University of Tunis Elmanar 2092 Tunis (Tunisia); Harima, N.; Koyama, H. [Hyogo University of Teacher Education, Kato, Hyogo 673-1494 (Japan); Gaponenko, N.V. [Belarusian State University of Informatics and Radioelectronics, P. Browki St. 6, 220013 Minsk (Belarus)

2012-09-15

We have used porous anodic alumina (PAA) films as templates for embedding rhodamine 110 (Rh110) molecules and examined their photoluminescence (PL) properties in detail. The analysis of the polarization memory (PM) of PL strongly suggests that there is a significant energy transfer from PAA to Rh110 molecules. The effect of annealing the PAA layer on the PL properties of the nanocomposite has been studied. The results show that the energy transfer becomes more efficient in annealed PAA. - Highlights: Black-Right-Pointing-Pointer Porous anodic alumina-rhodamine 110 nanocomposites are elaborated. Black-Right-Pointing-Pointer Efficient energy transfer from the host to Rh110 molecules is evidenced from measurements of photoluminescence and degree of polarization memory spectra. Black-Right-Pointing-Pointer Thermal annealing of porous anodic alumina can improve the process of excitation transfer.

Enhanced photoluminescence from porous silicon by hydrogen-plasma etching

International Nuclear Information System (INIS)

Wang, Q.; Gu, C.Z.; Li, J.J.; Wang, Z.L.; Shi, C.Y.; Xu, P.; Zhu, K.; Liu, Y.L.

2005-01-01

Porous silicon (PS) was etched by hydrogen plasma. On the surface a large number of silicon nanocone arrays and nanocrystallites were formed. It is found that the photoluminescence of the H-etched porous silicon is highly enhanced. Correspondingly, three emission centers including red, green, and blue emissions are shown to contribute to the enhanced photoluminescence of the H-etched PS, which originate from the recombination of trapped electrons with free holes due to Si=O bonding at the surface of the silicon nanocrystallites, the quantum size confinement effect, and oxygen vacancy in the surface SiO 2 layer, respectively. In particular, the increase of SiO x (x<2) formed on the surface of the H-etched porous silicon plays a very important role in enhancing the photoluminescence properties

Effective diffusion coefficients of /sup 3/H/sub 2/O in several porous materials

Energy Technology Data Exchange (ETDEWEB)

Terashima, Y [Kyoto Univ. (Japan). Faculty of Engineering; Kumaki, T

1976-12-01

Diffusion coefficients of radionuclides in some porous structural materials and porous components of earth stratum are important as the basis for the safety evaluation of the storage and disposal of radioactive wastes. In our previous works, the method of analysis and experiment using a permeative type diffusion cell for measurement of effective diffusion coefficient was established, and experimental results were reported. In this paper, effective diffusion coefficients of /sup 3/H/sub 2/O in mortar, concrete, brick, clay layer, and sand layer were measured, and characteristics of these pore structure were discussed on the basis of tourtusity factor.

Analytical and numerical investigation of double diffusion in thermally anisotropy multilayer porous medium

Energy Technology Data Exchange (ETDEWEB)

Bennacer, R. [Neuville sur Oise, LEEVAM 5 mail Gay Lussac, Cergy-Pontoise Cedex (France); Mohamad, A.A. [CEERE University of Calgary, Department of Mechanical and Manufacturing Engineering, Calgary, Alberta (Canada); Ganaoui, M.El [Faculte des Sciences et Techniques de Limoges, Limoges (France)

2005-02-01

Double-diffusive natural convection within a multilayer anisotropic porous medium is studied numerically and analytically. The domain composed of two horizontal porous layers is subjected to a uniform horizontal heat flux and a vertical mass flux, where only the lower one is thermally anisotropic. Darcy model with classical Boussinesq approximation is used in formulating the mathematical model. The effect of thermal anisotropy and the relative width of the two layers on the flow and transfers is illustrated with characterising the transitions from the diffusive to the convective solution. Results were well compared with respect to a developed analytical approach, based on a parallel flow approximation for thermally anisotropic multilayer media. (orig.)

Oxygen- and Nitrogen-Enriched 3D Porous Carbon for Supercapacitors of High Volumetric Capacity.

Science.gov (United States)

Li, Jia; Liu, Kang; Gao, Xiang; Yao, Bin; Huo, Kaifu; Cheng, Yongliang; Cheng, Xiaofeng; Chen, Dongchang; Wang, Bo; Sun, Wanmei; Ding, Dong; Liu, Meilin; Huang, Liang

2015-11-11

Efficient utilization and broader commercialization of alternative energies (e.g., solar, wind, and geothermal) hinges on the performance and cost of energy storage and conversion systems. For now and in the foreseeable future, the combination of rechargeable batteries and electrochemical capacitors remains the most promising option for many energy storage applications. Porous carbonaceous materials have been widely used as an electrode for batteries and supercapacitors. To date, however, the highest specific capacitance of an electrochemical double layer capacitor is only ∼200 F/g, although a wide variety of synthetic approaches have been explored in creating optimized porous structures. Here, we report our findings in the synthesis of porous carbon through a simple, one-step process: direct carbonization of kelp in an NH3 atmosphere at 700 °C. The resulting oxygen- and nitrogen-enriched carbon has a three-dimensional structure with specific surface area greater than 1000 m(2)/g. When evaluated as an electrode for electrochemical double layer capacitors, the porous carbon structure demonstrated excellent volumetric capacitance (>360 F/cm(3)) with excellent cycling stability. This simple approach to low-cost carbonaceous materials with unique architecture and functionality could be a promising alternative to fabrication of porous carbon structures for many practical applications, including batteries and fuel cells.

Building a Better Capacitor with Thin-Film Atomic Layer Deposition Processing

Energy Technology Data Exchange (ETDEWEB)

Pike, Christopher [North Seattle College, WA (United States)

2015-08-28

The goal of this research is to determine procedures for creating ultra-high capacity supercapacitors by using nanofabrication techniques and high k-value dielectrics. One way to potentially solve the problem of climate change is to switch the source of energy to a source that doesn’t release many tons of greenhouse gases, gases which cause global warming, into the Earth’s atmosphere. These trap in more heat from the Sun’s solar energy and cause global temperatures to rise. Atomic layer deposition will be used to create a uniform thin-film of dielectric to greatly enhance the abilities of our capacitors and will build them on the nanoscale.

Effect of Current Density on Thermal and Optical Properties of p-Type Porous Silicon

International Nuclear Information System (INIS)

Kasra Behzad; Wan Mahmood Mat Yunus; Zainal Abidin Talib; Azmi Zakaria; Afarin Bahrami

2011-01-01

The different parameters of the porous silicon (PSi) can be tuned by changing some parameters in preparation process. We have chosen the anodization as formation method, so the related parameters should be changed. In this study the porous silicon (PSi) layers were formed on p-type Si wafer. The samples were anodized electrically in a fixed etching time under some different current densities. The structural and optical properties of porous silicon (PSi) on silicon (Si) substrates were investigated using photoluminescence (PL) and Photoacoustic Spectroscopy (PAS). (author)

Frost resistance of building materials

DEFF Research Database (Denmark)

Hansen, Ernst Jan De Place

materials, has been developed.The importance of the pore structure on the development of stresses in the material during freezing is emphasized. To verify the model, experimental investigations are made on various concretes without air-entrainment and brick tiles with different porosities.Calculations......In this thesis it is shown that the critical degree of saturation is suitable as parameter for the frost resistance of porous building materials. A numerical model for prediction of critical degrees of saturation based on fracture mechanics and phase geometry of two-phase materials, e.g. porous...

Novel optical and structural properties of porous GaAs formed by anodic etching of n±GaAs in a HF:C_2H_5OH:HCl:H_2O_2:H_2O electrolyte: effect of etching time

International Nuclear Information System (INIS)

Naddaf, M.; Saad, M.

2014-01-01

Porous GaAs layers have been formed by anodic etching of n±type GaAs (10.0) substrates in a HF:C_2H_5OH:HCl:H_2O_2:H_2O electrolyte. A dramatic impact of etching time on the optical and structural properties of porous GaAs layer is demonstrated. The nano/micro-features of porous GaAs layers are revealed by scanning electron microscopy (SEM) imaging. Two-peak room temperature photoluminescence (PL), "blue-green"and "green-yellow", is obtained in all prepared porous GaAs samples. Proper adjustment of etching time is found to produce a white color layer, instead of the usual dark gray color of porous GaAs. This is found to cause vast enhancement in the intensity of the visible PL in porous GaAs layer. Chemical composition and structural characterization by means of X-ray photoelectron spectroscopic (XPS), X-ray diffraction (XRD), and micro-Raman spectroscopy, confirm that this layer is characterized with monoclinic β-Ga_2O_3 rich surface. Etching time induced-modification of structural and chemical properties of porous GaAs layer is discussed and correlated to its PL behavior. It is inferred that the "blue-green"PL in porous GaAs can be ascribed to different degrees of quantum confinement in GaAs nano crystallites, whereas, the "green-yellow"PL is highly influenced by the As_2O_3 and Ga_2O_3, content in the porous GaAs layer. In addition, the reflectance measurements reveal an anti-refection trend of behavior of porous GaAs layers in the spectral range (500-1,100 nm). (author)

Synthesis and crystal structures of a novel layered silicate SSA-1 and its microporous derivatives by topotactic transformation.

Science.gov (United States)

Takahashi, S; Kurita, Y; Ikeda, T; Miyamoto, M; Uemiya, S; Oumi, Y

2016-10-18

The synthesis of a novel layered silicate SSA-1 (SSA: silicate synthesized with a quaternary amine) was achieved in the SiO 2 -H 2 O-TEAOH (TEAOH: tetraethylammonium hydroxide - as an organic structural directing agent) system. The crystal structure of SSA-1 involved two silicate layers composed of bre [10T]-type CBU (Composite Building Unit) and TEAOH in interlayers. The topotactic transformation of SSA-1 by calcination was examined, resulting in a porous material (PML-1: porous material transformed from a layered silicate) with a 108 m 2 g -1 BET surface area and 0.035 cm 3 g -1 pore volume. PML-1 is a siliceous microporous material with silanols in the framework and possesses unique properties, such as hydrophilicity, in spite of all its silica composition. The most reasonable crystal structure of PML-1 was successfully determined on the basis of the crystal structure of SSA-1 by a combination of manual modelling, PXRD pattern simulation, DFT optimization and Rietveld analysis. Additionally, an interlayer expanded siliceous zeolite SSA-1 (IEZ-SSA-1) was also successfully prepared by silylation using trichloro(methyl)silane under acidic conditions. IEZ-SSA-1 showed hydrophilicity or hydrophobicity properties by changing the functional group of the pillar part in the interlayer. Additionally, IEZ-SSA-1 showed a large gas adsorption property (537 m 2 g -1 and 0.21 cm 3 g -1 ).

Optical properties of erbium-doped porous silicon waveguides

Energy Technology Data Exchange (ETDEWEB)

Najar, A. [Laboratoire d' Optronique UMR 6082-FOTON, Universite de Rennes 1, 6 rue de Kerampont, B P. 80518, 22305 Lannion Cedex (France); Laboratoire de Spectroscopie Raman, Faculte des Sciences de Tunis, 2092 ElManar, Tunis (Tunisia); Charrier, J. [Laboratoire d' Optronique UMR 6082-FOTON, Universite de Rennes 1, 6 rue de Kerampont, B P. 80518, 22305 Lannion Cedex (France)]. E-mail: joel.charier@univ-rennes1.fr; Ajlani, H. [Laboratoire de Spectroscopie Raman, Faculte des Sciences de Tunis, 2092 ElManar, Tunis (Tunisia); Lorrain, N. [Laboratoire d' Optronique UMR 6082-FOTON, Universite de Rennes 1, 6 rue de Kerampont, B P. 80518, 22305 Lannion Cedex (France); Elhouichet, H. [Laboratoire de Spectroscopie Raman, Faculte des Sciences de Tunis, 2092 ElManar, Tunis (Tunisia); Oueslati, M. [Laboratoire de Spectroscopie Raman, Faculte des Sciences de Tunis, 2092 ElManar, Tunis (Tunisia); Haji, L. [Laboratoire d' Optronique UMR 6082-FOTON, Universite de Rennes 1, 6 rue de Kerampont, B P. 80518, 22305 Lannion Cedex (France)

2006-12-15

Planar and buried channel porous silicon waveguides (WG) were prepared from p{sup +}-type silicon substrate by a two-step anodization process. Erbium ions were incorporated into pores of the porous silicon layers by an electrochemical method using ErCl{sub 3}-saturated solution. Erbium concentration of around 10{sup 20} at/cm{sup 3} was determined by energy-dispersive X-ray analysis performed on SEM cross-section. The luminescence properties of erbium ions in the IR range were determined and a luminescence time decay of 420 {mu}s was measured. Optical losses were studied on these WG. The increased losses after doping were discussed.

Wavelength tuning of porous silicon microcavities

International Nuclear Information System (INIS)

Mulders, J.; Reece, P.; Zheng, W.H.; Lerondel, G.; Sun, B.; Gal, M.

2002-01-01

Full text: In the last decade much attention has been given to porous silicon (PS) for optoelectronic applications, which include efficient room temperature light emission as well as microcavity formation. Due to the large specific surface area, the use of porous silicon microcavities (PSMs) has been proposed for chemical sensing. Large wavelength shifts have indicated that the optical properties of PSMs are indeed strongly dependent on the environment. In this paper, we report the shifting of the resonance frequency of high quality PSMs, with the aim of tuning a future PS device to a certain required wavelength. The PSM samples were prepared by anodically etching p + -doped (5mΩcm) bulk silicon wafer in a solution (25%) of aqueous HF and ethanol. The device structure consisted of a PS layer sandwiched between 2 stacks of thin PS layers with alternating high and low effective refractive indices (RI), i.e. distributed Bragg mirrors (DBM). The layer thickness depends on the etch time while the porosity and hence refractive index is determined by the current density as the Si is etched. The position and the width of the stop-band can be fully controlled by the design of the DBMs, with the microcavity resonance mode sitting within the stop-band. We achieved tuning of the microcavity resonance by a number of methods, including temperature dependent tuning. The temperature induced wavelength shift was found to be of the order of 10 -15 nm. Computer modeling of these changes in the reflectivity spectra allowed us to quantify the changes of the effective refractive index and the respective layer thicknesses

Mass and heat transfers in the parietal boundary layer and inside a flat porous wall submitted to effusion or transpiration; Transferts de masse et de chaleur dans la couche limite parietale et a l'interieur d'une paroi poreuse plane soumise a de l'effusion ou de la transpiration

Energy Technology Data Exchange (ETDEWEB)

Bellettre, J.

1998-12-01

The flows and the heat transfer near and inside a porous wall subjected to an internal flow are numerically and experimentally studied. Numerical simulations of the main flow are performed using a classical model of turbulence (RNG k-{xi} model). A discrete modeling of blowing through a porous plate is developed in order to predict interactions between the main flow and the injected fluid. Numerical results are in good agreement with experimental data obtained with a subsonic wind tunnel. The coupling between the heat transfer near and inside porous plates is studied for different injection rates, main flow temperatures and internal exchange surfaces of porous media. Surfaces temperatures are calculated using a nodal model of internal heat transfer, linked to the model of boundary layer submitted to injection. By comparing numerical and experimental temperatures of walls, the heat transfer coefficients inside porous media are calculated. In order to improve the thermal protection of walls, the transpiration with a liquid is studied. Experimental results, obtained with ethanol injection whereas the main flow is gaseous, show an important enhancement of the protection process. The coolant evaporation rate is calculated using measurement of mass fraction in the boundary layer and is used for the numerical study of mass transfer in the boundary layer. (author)

Modification of the properties of porous silicon on adsorption of iodine molecules

International Nuclear Information System (INIS)

Vorontsov, A. S.; Osminkina, L. A.; Tkachenko, A. E.; Konstantinova, E. A.; Elenskii, V. G.; Timoshenko, V. Yu.; Kashkarov, P. K.

2007-01-01

Infrared spectroscopy and electron spin resonance measurements are used to study the properties of porous silicon layers on adsorption of the I 2 iodine molecules. The layers are formed on the p-an n-Si single-crystal wafers. It is established that, in the atmosphere of I 2 molecules, the charge-carrier concentration in the layers produced on the p-type wafers can be noticeably increased: the concentration of holes can attain values on the order of ∼10 18 -10 19 cm -3 . In porous silicon layers formed on the n-type wafers, the adsorption-induced inversion of the type of charge carriers and the partial substitution of silicon-hydrogen bonds by silicon-iodine bonds are observed. A decrease in the concentration of surface paramagnetic defects, P b centers, is observed in the samples with adsorbed iodine. The experimental data are interpreted in the context of the model in which it is assumed that both deep and shallow acceptor states are formed at the surface of silicon nanocrystals upon the adsorption of I 2 molecules

Living fungal hyphae-templated porous gold microwires using nanoparticles as building blocks

International Nuclear Information System (INIS)

Rehman, Asma; Majeed, Muhammad Irfan; Ihsan, Ayesha; Hussain, Syed Zajif; Saif-ur-Rehman; Ghauri, Muhammad Afzal; Khalid, Zafar M.; Hussain, Irshad

2011-01-01

A simple and environmentally benign green method is reported to decorate growing fungal hyphae with high loading of gold nanoparticles, which were initially produced using aqueous tea extract as a sole reducing/stabilizing agent. Inoculation of fungal spores in aqueous suspension of nanoparticles led to the growth of intensely red-coloured fungal hyphae due to the accumulation of gold nanoparticles. Heat treatment of these hybrid materials led to the formation of porous gold microwires. This report is thus an interesting example of using green and sustainable approach to produce nanostructured materials which have potential applications in catalysis, sensing and electronics.Graphical AbstractPorous gold microwires are formed by the heat treatment of fungal hyphae–gold nanoparticle composites. These nanoparticle-loaded composites were formed by growing Aspergillus niger in gold nanoparticles suspension produced using tea extract as the sole chemical source in addition to the gold salt.

Optimization of chemical displacement deposition of copper on porous silicon.

Science.gov (United States)

Bandarenka, Hanna; Redko, Sergey; Nenzi, Paolo; Balucani, Marco; Bondarenko, Vitaly

2012-11-01

Copper (II) sulfate was used as a source of copper to achieve uniform distribution of Cu particles deposited on porous silicon. Layers of the porous silicon were formed by electrochemical anodization of Si wafers in a mixture of HF, C3H7OH and deionized water. The well-known chemical displacement technique was modified to grow the copper particles of specific sizes. SEM and XRD analysis revealed that the outer surface of the porous silicon was covered with copper particles of the crystal orientation inherited from the planes of porous silicon skeleton. The copper crystals were found to have the cubic face centering elementary cell. In addition, the traces of Cu2O cubic primitive crystalline phases were identified. The dimensions of Cu particles were determined by the Feret's analysis of the SEM images. The sizes of the particles varied widely from a few to hundreds of nanometers. A phenomenological model of copper deposition was proposed.

Novel manufacturing process for direct methanol fuel cells (DMFC) by defined layer structures; Neuartiges Herstellungsverfahren fuer Direkt-Methanol-Brennstoffzellen (DMFC) durch definierte Schichtstrukturen

Energy Technology Data Exchange (ETDEWEB)

Frey, Thomas

2007-07-17

A novel method to prepare membrane electrode assemblies (MEA) for direct methanol fuel cells (DMFC) by a layer-upon-layer fabrication onto a porous substrate is presented. The novel preparation technique is based on a single method for the fabrication of the whole MEA, e.g. spraying one functional layer onto the other, and therefore simplifies its preparation considerably. It also permits new fuel cell designs with in-plane serial connection of single cells. The new concept offers high flexibility in the choice of cell geometry as well as superior control of the structural parameters. Layer thickness, composition, catalyst and ionomer loadings can easily be varied and adapted. Cells fabricated with the new concept are especially suited for low power micro fuel cells operated at ambient conditions. In this work, process parameters enabling such a layer-upon-layer MEA preparation have been developed. Advanced catalyst inks and electrolyte solutions were formulated as precursors for each functional layer. Nafion {sup registered} as well as polyaryl-based polymers were investigated for the fabrication of dense electrolyte layers. Catalyst layers were prepared from inks containing Pt and PtRu-black catalysts which were suspended in suitable solvents with diluted proton-conducting electrolytes. The critical parameters for the layer build-up were identified and optimized afterwards. Various candidate materials for the porous substrate were characterized and selected for further investigation. Experiments and calculation models led to a concept and an advanced design for a serially connected multi-cells unit on the substrate. The inplane conductivity of the electrodes turned out to be the critical parameter resulting in high ohmic losses especially when the electrodes were applied on non-conductive substrates. Various conductive coatings were tested to selectively increase the conductivity of non-conductive substrates, which are prerequisite for serial connection. Only

Electrical Characterization of Nanopolyaniline/Porous Silicon Heterojunction at High Temperatures

Directory of Open Access Journals (Sweden)

Salah E. El-Zohary

2013-01-01

Full Text Available Nanopolyaniline/p-type porous silicon (NPANI/PSi heterojunction films were chemically fabricated via in situ polymerization. The composition and morphology of the nanopolymer were confirmed using Fourier transform infrared, scanning electron microscopy, UV-visible, and transmission electron microscopy techniques. The results indicated that the polymerization took place throughout the porous layer. The I-V measurements, performed at different temperatures, enabled the calculation of ideality factor, barrier height, and series resistance of those films. The obtained ideality factor showed a nonideal diode behavior. The series resistance was found to decrease with increasing temperature.

Thermal conductivity of a graphite bipolar plate (BPP) and its thermal contact resistance with fuel cell gas diffusion layers: Effect of compression, PTFE, micro porous layer (MPL), BPP out-of-flatness and cyclic load

Science.gov (United States)

Sadeghifar, Hamidreza; Djilali, Ned; Bahrami, Majid

2015-01-01

This paper reports on measurements of thermal conductivity of a graphite bipolar plate (BPP) as a function of temperature and its thermal contact resistance (TCR) with treated and untreated gas diffusion layers (GDLs). The thermal conductivity of the BPP decreases with temperature and its thermal contact resistance with GDLs, which has been overlooked in the literature, is found to be dominant over a relatively wide range of compression. The effects of PTFE loading, micro porous layer (MPL), compression, and BPP out-of-flatness are also investigated experimentally. It is found that high PTFE loadings, MPL and even small BPP out-of-flatness increase the BPP-GDL thermal contact resistance dramatically. The paper also presents the effect of cyclic load on the total resistance of a GDL-BPP assembly, which sheds light on the behavior of these materials under operating conditions in polymer electrolyte membrane fuel cells.

Electrochemical properties for high surface area and improved electrical conductivity of platinum-embedded porous carbon nanofibers

Science.gov (United States)

An, Geon-Hyoung; Ahn, Hyo-Jin; Hong, Woong-Ki

2015-01-01

Four different types of carbon nanofibers (CNFs) for electrical double-layer capacitors (EDLCs), porous and non-porous CNFs with and without Pt metal nanoparticles, are synthesized by an electrospinning method and their performance in electrical double-layer capacitors (EDLCs) is characterized. In particular, the Pt-embedded porous CNFs (PCNFs) exhibit a high specific surface area of 670 m2 g-1, a large mesopore volume of 55.7%, and a low electrical resistance of 1.7 × 103. The synergistic effects of the high specific surface area with a large mesopore volume, and superior electrical conductivity result in an excellent specific capacitance of 130.2 F g-1, a good high-rate performance, superior cycling durability, and high energy density of 16.9-15.4 W h kg-1 for the performance of EDLCs.

Optimum design for effective water transport through a double-layered porous hydrogel inspired by plant leaves

Science.gov (United States)

Kim, Hyejeong; Kim, Hyeonjeong; Huh, Hyungkyu; Hwang, Hyung Ju; Lee, Sang Joon

2014-11-01

Plant leaves are generally known to have optimized morphological structure in response to environmental changes for efficient water usage. However, the advantageous features of plant leaves are not fully utilized in engineering fields yet, since the optimum design in internal structure of plant leaves is unclear. In this study, the tissue organization of the hydraulic pathways inside plant leaves was investigated. Water transport through double-layered porous hydrogel models analogous to mesophyll cells was experimentally observed. In addition, computational experiment and theoretical analysis were applied to the model systems to find the optimal design for efficient water transport. As a result, the models with lower porosity or with pores distributed widely in the structure exhibit efficient mass transport. Our theoretical prediction supports that structural features of plant leaves guarantee sufficient water supply as survival strategy. This study may provide a new framework for investigating the biophysical principles governing the morphological optimization of plant leaves and for designing microfluidic devices to enhance mass transport ability. This study was supported by the National Research Foundation of Korea and funded by the Korean government.

Study of building materials impregnation processes by quasi-real-time neutron radiography

International Nuclear Information System (INIS)

Nemec, T.; Rant, J.; Apih, V.; Glumac, B.

1999-01-01

Neutron radiography (NR) is a useful non-destructive method for determination of hydrogen content in various building and technical materials. Monitoring of transport processes of moisture and hydrogenous liquids in porous building materials is enabled by fast, quasi-real-time NR methods based on novel imaging plate neutron detectors (IP-NDs). Hydrogen content in the samples is determined by quantitative analysis of measured profiles of neutron attenuation in the samples. Detailed description of quantitative NR method is presented by the authors in another accompanying contribution at this conference. Deterioration of building materials is originated by different processes that all require presence of water therefore it is essential to limit or prevent the transport of water through the porous material. In this presentation, results of a study of clay brick impregnation by silicone based hydrophobic agents will be presented. Quantitative results obtained by NR imaging successfully explained the processes that occur during the impregnation of porous materials. Efficiency of hydrophobic treatment was quantitatively evaluated

Two-dimensional lift-up problem for a rigid porous bed

Energy Technology Data Exchange (ETDEWEB)

Chang, Y.; Huang, L. H.; Yang, F. P. Y. [Department of Civil Engineering, National Taiwan University, Taipei, Taiwan (China)

2015-05-15

The present study analytically reinvestigates the two-dimensional lift-up problem for a rigid porous bed that was studied by Mei, Yeung, and Liu [“Lifting of a large object from a porous seabed,” J. Fluid Mech. 152, 203 (1985)]. Mei, Yeung, and Liu proposed a model that treats the bed as a rigid porous medium and performed relevant experiments. In their model, they assumed the gap flow comes from the periphery of the gap, and there is a shear layer in the porous medium; the flow in the gap is described by adhesion approximation [D. J. Acheson, Elementary Fluid Dynamics (Clarendon, Oxford, 1990), pp. 243-245.] and the pore flow by Darcy’s law, and the slip-flow condition proposed by Beavers and Joseph [“Boundary conditions at a naturally permeable wall,” J. Fluid Mech. 30, 197 (1967)] is applied to the bed interface. In this problem, however, the gap flow initially mainly comes from the porous bed, and the shear layer may not exist. Although later the shear effect becomes important, the empirical slip-flow condition might not physically respond to the shear effect, and the existence of the vertical velocity affects the situation so greatly that the slip-flow condition might not be appropriate. In contrast, the present study proposes a more general model for the problem, applying Stokes flow to the gap, the Brinkman equation to the porous medium, and Song and Huang’s [“Laminar poroelastic media flow,” J. Eng. Mech. 126, 358 (2000)] complete interfacial conditions to the bed interface. The exact solution to the problem is found and fits Mei’s experiments well. The breakout phenomenon is examined for different soil beds, mechanics that cannot be illustrated by Mei’s model are revealed, and the theoretical breakout times obtained using Mei’s model and our model are compared. The results show that the proposed model is more compatible with physics and provides results that are more precise.

Formation of Defect-Free Latex Films on Porous Fiber Supports

KAUST Repository

Lively, Ryan P.

2011-09-28

We present here the creation of a defect-free polyvinylidene chloride barrier layer on the lumen-side of a hollow fiber sorbent. Hollow fiber sorbents have previously been shown to be promising materials for enabling low-cost CO 2 capture, provided a defect-free lumen-side barrier layer can be created. Film experiments examined the effect of drying rate, latex age, substrate porosity (porous vs nonporous), and substrate hydrophobicity/ hydrophilicity. Film studies show that in ideal conditions (i.e., slow drying, fresh latex, and smooth nonporous substrate), a defect-free film can be formed, whereas the other permutations of the variables investigated led to defective films. These results were extended to hollow fiber sorbents, and despite using fresh latex and relatively slow drying conditions, a defective lumen-side layer resulted. XRD and DSC indicate that polyvinylidene chloride latex develops crystallinity over time, thereby inhibiting proper film formation as confirmed by SEM and gas permeation. This and other key additional challenges associated with the porous hollow fiber substrate vs the nonporous flat substrate were overcome. By employing a toluene-vapor saturated drying gas (a swelling solvent for polyvinylidene chloride) a defect-free lumen-side barrier layer was created, as investigated by gas and water vapor permeation. © 2011 American Chemical Society.

Electric Power Plants and Generation Stations, Power Plants - is a seperate layer, however, we have them included in local building layer as well, Published in 2010, 1:2400 (1in=200ft) scale, Effingham County Government.

Data.gov (United States)

NSGIC Local Govt | GIS Inventory — Electric Power Plants and Generation Stations dataset current as of 2010. Power Plants - is a seperate layer, however, we have them included in local building layer...

Synthesis of hierarchical porous materials with ZSM-5 structures via template-free sol–gel method

Directory of Open Access Journals (Sweden)

Wei Han et al

2007-01-01

Full Text Available Interests are focused on preparation of hierarchical porous materials with zeolite structures by using soft or rigid templates in order to solve diffusion and mass transfer limitations resulting from the small pore sizes of zeolites. Here we develop a convenient template-free sol–gel method to synthesize hierarchical porous materials with ZSM-5 structures. This method involves hydrothermal recrystallization of the xerogel converted from uniform ZSM-5 sol by a vacuum drying process. By utilizing this method we can manipulate the size of zeolite nanocrystals as building units of porous structures based on controlling temperature of recrystallization, consequently obtain hierarchical porous materials with different intercrystalline pore sizes and ZSM-5 structures.

Measurements of wall shear stress in a planar turbulent Couette flow with porous walls

Science.gov (United States)

Beuther, Paul

2013-11-01

Measurements of drag on a moving web in a multi-span festoon show a stronger than expected dependency on the porosity of the web. The experiments suggest a wall shear stress 3-4 times larger than non-porous webs or historical Couette flow data for solid walls. Previous DNS studies by Jimenez et al. (JFM Vol 442) of boundary layers with passive porous surfaces predict a much smaller increase in wall shear stress for a porous wall of only 40%. Other DNS studies by Quadrio et al. (JFM Vol 576) of porous walls with periodic transpiration do show a large increase in drag under certain periodic conditions of modest amplitude. Although those results are aligned in magnitude with this study, the exact reason for the observed high drag for porous webs in this present study is not understood because there was no external disturbance applied to the web. It can be hypothesized that natural flutter of the web results in a similar mechanism shown in the periodic DNS study, but when the natural flutter was reduced by increasing web tension, there was only a small decrease of the drag. A key difference in this study is that because of the multiple parallel spans in a festoon, any transpiration in one layer must act in the opposite manner on the adjacent span.

Polycrystalline Silicon Gettered by Porous Silicon and Heavy Phosphorous Diffusion

Institute of Scientific and Technical Information of China (English)

LIU Zuming(刘祖明); Souleymane K Traore; ZHANG Zhongwen(张忠文); LUO Yi(罗毅)

2004-01-01

The biggest barrier for photovoltaic (PV) utilization is its high cost, so the key for scale PV utilization is to further decrease the cost of solar cells. One way to improve the efficiency, and therefore lower the cost, is to increase the minority carrier lifetime by controlling the material defects. The main defects in grain boundaries of polycrystalline silicon gettered by porous silicon and heavy phosphorous diffusion have been studied. The porous silicon was formed on the two surfaces of wafers by chemical etching. Phosphorous was then diffused into the wafers at high temperature (900℃). After the porous silicon and diffusion layers were removed, the minority carrier lifetime was measured by photo-conductor decay. The results show that the lifetime's minority carriers are increased greatly after such treatment.

Unsteady Viscous Flow Past an Impulsively Started Porous Vertical ...

African Journals Online (AJOL)

This paper presents a new numerical approach for solving unsteady two dimensional boundary layer flow past an infinite vertical porous surface with the flow generated by Newtonian heating and impulsive motion in the presence of viscous dissipation and temperature dependent viscosity. The viscosity of the fluid under ...

Heat transfer through natural convection in a porous saturated medium between two vertical cylinders

Energy Technology Data Exchange (ETDEWEB)

Hasnaoui, M. [Faculte des Sciences Semlalia, Marrakech (Morocco); Vasseur, P.; Bilgen, E.; Robillard, L. [Ecole Polytechnique, Montreal, PQ (Canada)

1993-12-31

A numerical and analytical study of two dimensional, laminar and near steady convection in a vertical porous annular region. The mathematical model was established, basing on Darcy-Oberbeck-Boussinesq equations. The analytical resolution is in the limit where the width of the porous layer is small compared to the cylinders height and it is based on the hypothesis of the parallel flow. (Authors). 4 refs., 4 figs.

Flow and Turbulence at Rubble-Mound Breakwater Armor Layers under Solitary Wave

DEFF Research Database (Denmark)

Jensen, Bjarne; Christensen, Erik Damgaard; Sumer, B. Mutlu

2015-01-01

This paper presents the results of an experimental investigation of the flow and turbulence at the armor layer of rubble-mound breakwaters during wave action. The study focused on the details of the flow and turbulence in the armor layer and on the effect of the porous core on flow and stability....... To isolate the processes involved with the flow in the porous core, experiments were conducted with increasing complexity. Specifically, three parallel experiments were performed including (1) an impermeable smooth breakwater slope, (2) an impermeable breakwater slope with large roughness elements added...... to the breakwater, and (3) a porous breakwater where the porous core was added below the breakwater front. One breakwater slope of 1:1.5 was applied. In this paper the focus is on the details of a single sequence of wave approach, run-up, and rundown. To isolate this sequence the experiments were performed applying...

Characterization of the porous anodic alumina nanostructures with a metal interlayer on Si substrates

Energy Technology Data Exchange (ETDEWEB)

Fang, Chia-Hui; Chen, Hung-Ing; Hsiao, Jui-Ju; Wang, Jen-Cheng; Nee, Tzer-En, E-mail: neete@mail.cgu.edu.tw

2014-04-15

Porous anodic alumina (PAA) films produced by the anodization technique have made possible the mass production of porous nano-scale structures where the pore height and diameter are controllable. A metal interlayer is observed to have a significant influence on the characteristics of these PAA nanostructures. In this study, we investigate in-depth the effect of the current density on the properties of porous anodic alumina nanostructures with a metal interlayer. A thin film layer of tungsten (W) and titanium (Ti) was sandwiched between a porous anodic alumina film and a silicon (Si) substrate to form PAA/W/Si and PAA/Ti/Si structures. The material and optical characteristics of the porous anodic alumina nanostructures, with and without a metal interlayer, on silicon substrates were studied using the scanning electron microscopy, X-ray diffraction (XRD), and temperature-dependent photoluminescence (PL) measurements. The current densities of the porous anodic alumina nanostructures with the metal interlayer are higher than for the PAA/Si, resulting in an increase of the growth rate of the oxide layer. It can be observed from the X-ray diffraction curves that there is more aluminum oxide inside the structure with the metal interlayer. Furthermore, it has been found that there is a reduction in the photoluminescence intensity of the oxygen vacancy with only one electron due to the formation of oxygen vacancies inside the aluminum oxide during the re-crystallization process. This leads to competition between the two kinds of different oxygen-deficient defect centers (F+ and F centers) in the carrier recombination mechanism from the PL spectra of the porous anodic alumina nanostructures, with and without a metal interlayer, on silicon substrates. -- Highlights: • Study of porous anodic alumina (PAA) films with metal interlayers on silicon. • The highly ordered PAA film with a fairly regular nano-porous structure. • The luminescence properties of PAA films were

Control of optical transport parameters of 'porous medium – supercritical fluid' systems

Energy Technology Data Exchange (ETDEWEB)

Zimnyakov, D A; Ushakova, O V; Yuvchenko, S A [Yuri Gagarin State Technical University of Saratov, Saratov (Russian Federation); Bagratashvili, V N [M. V. Lomonosov Moscow State University, Moscow (Russian Federation)

2015-11-30

The possibility of controlling optical transport parameters (in particular, transport scattering coefficient) of porous systems based on polymer fibres, saturated with carbon dioxide in different phase states (gaseous, liquid and supercritical) has been experimentally studied. An increase in the pressure of the saturating medium leads to a rise of its refractive index and, correspondingly, the diffuse-transmission coefficient of the system due to the decrease in the transport scattering coefficient. It is shown that, in the case of subcritical saturating carbon dioxide, the small-angle diffuse transmission of probed porous layers at pressures close to the saturated vapour pressure is determined by the effect of capillary condensation in pores. The immersion effect in 'porous medium – supercritical fluid' systems, where the fluid pressure is used as a control parameter, is considered. The results of reconstructing the values of transport scattering coefficient of probed layers for different refractive indices of a saturating fluid are presented. (radiation scattering)

Photocatalytic evaluation of self-assembled porous network structure of ferric oxide film fabricated by dry deposition process

Energy Technology Data Exchange (ETDEWEB)

Park, Yunchan; Kim, Hyungsub; Lee, Geon-Yong; Pawar, Rajendra C.; Lee, Jai-Sung; Lee, Caroline Sunyong, E-mail: sunyonglee@hanyang.ac.kr

2016-09-15

Ferric oxide powder in the alpha phase (α-Fe{sub 2}O{sub 3}) was deposited on an aluminum oxide (Al{sub 2}O{sub 3}) substrate by a nanoparticle deposition system using the dry deposition method. X-ray diffraction (XRD) images confirmed that the phase of the deposited α-Fe{sub 2}O{sub 3} did not change. The deposited α-Fe{sub 2}O{sub 3} was characterized in terms of its microstructure using scanning electron microscopy (SEM). A porous network microstructure formed when small agglomerates of Fe{sub 2}O{sub 3} (SAF) were deposited. The deposition and formation mechanism of the microstructure were investigated using SEM and three-dimensional (3D) profile analysis. First, a dense coating layer formed when the film was thinner than the particle size. After that, as the film thickness increased to over 5 μm, the porous network structure formed by excavating the surface of the coating layer as it was bombarded by particles. Rhodamine B (RhB) was degraded after 6 h of exposure to the Fe{sub 2}O{sub 3} coating layer with SAF, which has good photocatalytic activity and a high porous network structure. The kinetic rate constants of the SAF and large agglomerates of Fe{sub 2}O{sub 3} (LAF) were calculated to be 0.197(h{sup −1}) and 0.128(h{sup −1}), respectively, based on the absorbance results. Using linear sweep voltammetry, we confirmed that the photoelectric effect occurred in the coating layer by measuring the resulting current under illuminated and dark conditions. - Graphical abstract: Self-assembled porous photocatalytic film fabricated by dry deposition method for water purification. - Highlights: • Different sizes of Fe{sub 2}O{sub 3} agglomerates were used to form porous network structure. • Fe{sub 2}O{sub 3} agglomerate particles were deposited using solvent-free process. • Self-assembled porous network microstructure formed better with small agglomerates of Fe{sub 2}O{sub 3}. • Fabricated porous network structure showed its potential to be used

Hydromagnetic Flow and Heat Transfer over a Porous Oscillating Stretching Surface in a Viscoelastic Fluid with Porous Medium.

Science.gov (United States)

Khan, Sami Ullah; Ali, Nasir; Abbas, Zaheer

2015-01-01

An analysis is carried out to study the heat transfer in unsteady two-dimensional boundary layer flow of a magnetohydrodynamics (MHD) second grade fluid over a porous oscillating stretching surface embedded in porous medium. The flow is induced due to infinite elastic sheet which is stretched periodically. With the help of dimensionless variables, the governing flow equations are reduced to a system of non-linear partial differential equations. This system has been solved numerically using the finite difference scheme, in which a coordinate transformation is used to transform the semi-infinite physical space to a bounded computational domain. The influence of the involved parameters on the flow, the temperature distribution, the skin-friction coefficient and the local Nusselt number is shown and discussed in detail. The study reveals that an oscillatory sheet embedded in a fluid-saturated porous medium generates oscillatory motion in the fluid. The amplitude and phase of oscillations depends on the rheology of the fluid as well as on the other parameters coming through imposed boundary conditions, inclusion of body force term and permeability of the porous medium. It is found that amplitude of flow velocity increases with increasing viscoelastic and mass suction/injection parameters. However, it decreases with increasing the strength of the applied magnetic field. Moreover, the temperature of fluid is a decreasing function of viscoelastic parameter, mass suction/injection parameter and Prandtl number.

Steady Boundary Layer Slip Flow along with Heat and Mass Transfer over a Flat Porous Plate Embedded in a Porous Medium

Science.gov (United States)

Aziz, Asim; Siddique, J. I.; Aziz, Taha

2014-01-01

In this paper, a simplified model of an incompressible fluid flow along with heat and mass transfer past a porous flat plate embedded in a Darcy type porous medium is investigated. The velocity, thermal and mass slip conditions are utilized that has not been discussed in the literature before. The similarity transformations are used to transform the governing partial differential equations (PDEs) into a nonlinear ordinary differential equations (ODEs). The resulting system of ODEs is then reduced to a system of first order differential equations which was solved numerically by using Matlab bvp4c code. The effects of permeability, suction/injection parameter, velocity parameter and slip parameter on the structure of velocity, temperature and mass transfer rates are examined with the aid of several graphs. Moreover, observations based on Schmidt number and Soret number are also presented. The result shows, the increase in permeability of the porous medium increase the velocity and decrease the temperature profile. This happens due to a decrease in drag of the fluid flow. In the case of heat transfer, the increase in permeability and slip parameter causes an increase in heat transfer. However for the case of increase in thermal slip parameter there is a decrease in heat transfer. An increase in the mass slip parameter causes a decrease in the concentration field. The suction and injection parameter has similar effect on concentration profile as for the case of velocity profile. PMID:25531301

Steady boundary layer slip flow along with heat and mass transfer over a flat porous plate embedded in a porous medium.

Science.gov (United States)

Aziz, Asim; Siddique, J I; Aziz, Taha

2014-01-01

In this paper, a simplified model of an incompressible fluid flow along with heat and mass transfer past a porous flat plate embedded in a Darcy type porous medium is investigated. The velocity, thermal and mass slip conditions are utilized that has not been discussed in the literature before. The similarity transformations are used to transform the governing partial differential equations (PDEs) into a nonlinear ordinary differential equations (ODEs). The resulting system of ODEs is then reduced to a system of first order differential equations which was solved numerically by using Matlab bvp4c code. The effects of permeability, suction/injection parameter, velocity parameter and slip parameter on the structure of velocity, temperature and mass transfer rates are examined with the aid of several graphs. Moreover, observations based on Schmidt number and Soret number are also presented. The result shows, the increase in permeability of the porous medium increase the velocity and decrease the temperature profile. This happens due to a decrease in drag of the fluid flow. In the case of heat transfer, the increase in permeability and slip parameter causes an increase in heat transfer. However for the case of increase in thermal slip parameter there is a decrease in heat transfer. An increase in the mass slip parameter causes a decrease in the concentration field. The suction and injection parameter has similar effect on concentration profile as for the case of velocity profile.

A new approach based on transfer matrix formalism to characterize porous silicon layers by reflectometry

Energy Technology Data Exchange (ETDEWEB)

Pirasteh, P. [RESO Laboratory (EA 3380), ENIB, CS 73862, 29238 Brest Cedex 3 (France); Optronics Laboratory, ENSSAT, UMR 6082, BP 80518, 6 rue de Kerampont, 22305 Lannion Cedex (France); Boucher, Y.G. [RESO Laboratory (EA 3380), ENIB, CS 73862, 29238 Brest Cedex 3 (France); Charrier, J.; Dumeige, Y. [Optronics Laboratory, ENSSAT, UMR 6082, BP 80518, 6 rue de Kerampont, 22305 Lannion Cedex (France)

2007-07-01

We use reflectometry coupled to transfer matrix formalism in order to investigate the comparative effect of surface (localized) and volume (distributed) losses inside a porous silicon monolayer. Both are modeled as fictive absorption. Surface losses are described as a Dirac-like singularity of permittivity localized at an interface whereas volume losses are described trough the imaginary part of the porous silicon complex permittivity. A good agreement with experimental data is determined by this formalism. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Study of optical absorbance in porous silicon nanowires for photovoltaic applications

KAUST Repository

Charrier, Joë l; Najar, Adel; Pirasteh, Parastesh

2013-01-01

Porous silicon nanowires (PSiNWs) layers fabrication was reported. Reflectance spectra were measured as a function of the nanowire length and were inferior to 0.1% and a strong photoluminescence (PL) signal was measured from samples. Models based

General Theory of Absorption in Porous Materials: Restricted Multilayer Theory.

Science.gov (United States)

Aduenko, Alexander A; Murray, Andy; Mendoza-Cortes, Jose L

2018-04-18

In this article, we present an approach for the generalization of adsorption of light gases in porous materials. This new theory goes beyond Langmuir and Brunauer-Emmett-Teller theories, which are the standard approaches that have a limited application to crystalline porous materials by their unphysical assumptions on the amount of possible adsorption layers. The derivation of a more general equation for any crystalline porous framework is presented, restricted multilayer theory. Our approach allows the determination of gas uptake considering only geometrical constraints of the porous framework and the interaction energy of the guest molecule with the framework. On the basis of this theory, we calculated optimal values for the adsorption enthalpy at different temperatures and pressures. We also present the use of this theory to determine the optimal linker length for a topologically equivalent framework series. We validate this theoretical approach by applying it to metal-organic frameworks (MOFs) and show that it reproduces the experimental results for seven different reported materials. We obtained the universal equation for the optimal linker length, given the topology of a porous framework. This work applied the general equation to MOFs and H 2 to create energy-storage materials; however, this theory can be applied to other crystalline porous materials and light gases, which opens the possibility of designing the next generations of energy-storage materials by first considering only the geometrical constraints of the porous materials.

Template-directed synthesis of pillared-porous carbon nanosheet architectures: High-performance electrode materials for supercapacitors

Energy Technology Data Exchange (ETDEWEB)

Fan, Zhuangjun; Liu, Yang; Yan, Jun; Wang, Qian; Wei, Tong [Key Laboratory of Superlight Materials and Surface Technology, Ministry of Education College of Material Science and Chemical Engineering, Harbin Engineering University, Harbin (China); Ning, Guoqing [State Key Laboratory of Heavy Oil Processing, China University of Petroleum, Beijing, Changping (China); Zhi, Linjie [National Center for Nanoscience and Technology of China, Zhongguancun, Beijing (China); Wei, Fei [Beijing Key Laboratory of Green Chemical Reaction Engineering and Technology, Department of Chemical Engineering, Tsinghua University, Beijing (China)

2012-04-15

3D pillared-porous carbon nanosheets with supporting carbon pillars between the carbon layers is prepared by the carbonization of pitch on porous MgO templates. This unique structure endows the high-rate transportation of electrolyte ions and electrons throughout the electrode matrix, resulting in excellent electrochemical performance. (Copyright copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

Detailed microstructure analysis of as-deposited and etched porous ZnO films

International Nuclear Information System (INIS)

Shang, Congcong; Thimont, Yohann; Barnabé, Antoine; Presmanes, Lionel; Pasquet, Isabelle; Tailhades, Philippe

2015-01-01

Graphical abstract: - Highlights: • Porous ZnO thin films were deposited by rf magnetron sputtering. • Surface enhancement factors were deduced from geometrical considerations. • Enlargement of the inter-grain spaces have been achieved by HCl chemical etching. • Microstructural parameters were deduced from SEM, AFM and optical measurements. - Abstract: ZnO nanostructured materials in thin film forms are of particular interest for photovoltaic or photocatalysis processes but they suffer from a lack of simple methods for optimizing their microstructure. We have demonstrated that microporous ZnO thin films with optimized inter grain accessibility can be produce by radio frequency magnetron sputtering process and chemical etching with 2.75 mM HCl solution for different duration. The as-deposited ZnO thin films were first characterized in terms of structure, grain size, inter grain space, open cavity depth and total thickness of the film by XRD, AFM, SEM, profilometry and optical measurements. A specific attention was dedicated to the determination of the surface enhancement factor (SEF) by using basic geometrical considerations and images treatments. In addition, the porous fraction and its distribution in the thickness have been estimated thanks to the optical simulation of the experimental UV–Visible–IR spectrums using the Bruggeman dielectric model and cross section SEM images analysis respectively. This study showed that the microstructure of the as-deposited films consists of a dense layer covered by a porous upper layer developing a SEF of 12–13 m 2 m −2 . This two layers architecture is not modified by the etching process. The etching process only affects the upper porous layer in which the overall porosity and the inter-grain space increase with the etching duration. Column diameter and total film thickness decrease at the same time when the films are soaked in the HCl bath. The microporous structure obtained after the etching process could

Thermal non-equilibrium in porous medium adjacent to vertical plate: ANN approach

Science.gov (United States)

Ahmed, N. J. Salman; Ahamed, K. S. Nazim; Al-Rashed, Abdullah A. A. A.; Kamangar, Sarfaraz; Athani, Abdulgaphur

2018-05-01

Thermal non-equilibrium in porous medium is a condition that refers to temperature discrepancy in solid matrix and fluid of porous medium. This type of flow is complex flow requiring complex set of partial differential equations that govern the flow behavior. The current work is undertaken to predict the thermal non-equilibrium behavior of porous medium adjacent to vertical plate using artificial neural network. A set of neurons in 3 layers are trained to predict the heat transfer characteristics. It is found that the thermal non-equilibrium heat transfer behavior in terms of Nusselt number of fluid as well as solid phase can be predicted accurately by using well-trained neural network.

Rationally designed porous silicon as platform for optical biosensors

International Nuclear Information System (INIS)

Priano, G.; Acquaroli, L.N.; Lasave, L.C.; Battaglini, F.; Arce, R.D.; Koropecki, R.R.

2012-01-01

Optical porous silicon multilayer structures are able to work as sensitive chemical sensors or biosensors based in their optical response. An algorithm to simulate the optical response of these multilayers was developed, considering the optical properties of the individual layers. The algorithm allows designing and customizing the porous silicon structures according to a given application. The results obtained by the simulation were experimentally verified; for this purpose different photonic structures were prepared, such as Bragg reflectors and microcavities. Some of these structures have been derivatized by the introduction of aminosilane groups on the porous silicon surface. The algorithm also permits to simulate the effects produced by a non uniform derivatization of the multilayer. - Highlights: ► Mesoporous silicon structure ► Functionalization of mesoporous silicon as sensors ► Design of the one-dimensional photonic crystal ► Simulation of non-uniformity in covering the sensor structure

Time-dependent ion selectivity in capacitive charging of porous electrodes

NARCIS (Netherlands)

Zhao, R.; Soestbergen, M.; Rijnaarts, H.H.M.; Wal, van der A.F.; Bazant, M.Z.; Biesheuvel, P.M.

2012-01-01

In a combined experimental and theoretical study, we show that capacitive charging of porous electrodes in multicomponent electrolytes may lead to the phenomenon of time-dependent ion selectivity of the electrical double layers (EDLs) in the electrodes. This effect is found in experiments on

Unsteady hydromagnetic Couette flow within a porous channel with ...

African Journals Online (AJOL)

user

International Journal of Engineering, Science and Technology. Vol. ... long parallel porous plates, taking Hall current into account, in the presence of a transverse ..... modified Hartmann boundary layer and the decaying oscillations excited by the ...... On flow of electrically conducting fluid over a flat plate in the presence of a ...

Inactivation of Avian Influenza Viruses on Porous and Non-porous Surfaces is Enhanced by Elevating Absolute Humidity.

Science.gov (United States)

Guan, J; Chan, M; VanderZaag, A

2017-08-01

This study was to evaluate the effect of absolute humidity (AH), a combined factor of temperature and relative humidity (RH), on inactivation of avian influenza viruses (AIVs) on surfaces. Suspensions of the H9N2 or H6N2 AIV were deposited onto carrier surfaces that were either porous (pine wood) or non-porous (stainless steel, synthetic rubber and glass). The inoculated carriers were incubated at 23, 35 or 45°C with 25% or 55% RH for up to 28 days. After incubation, virus was recovered and quantified by chicken embryo assays. The time required to obtain a log 10 reduction in virus infectivity (D-value) was estimated using a linear regression model. At AH of 5.2 g/m 3 (23°C & 25% RH), both viruses survived up to 14 days on the porous surface and for at least 28 days on the non-porous surfaces. The corresponding D-values for H9N2 and H6N2 were 1.49 and 6.90 days on the porous surface and 7.81 and 12.5 days on the non-porous surfaces, respectively. In comparison, at AH of 9.9 g/m 3 (35°C & 25% RH) or 11.3 g/m 3 (23°C & 55% RH), the D-values for H9N2 and H6N2 dropped to ≤0.76 day on the porous surface and to ≤1.81 days on the non-porous surfaces. As the AH continued to rise from 11.3 to 36.0 g/m 3 , the D-value for both viruses decreased further. The relationship between D-value and AH followed a form of y = ax -b for both viruses. The D-values for H9N2 virus were significantly lower (P < 0.05) than those for H6N2 virus. Exposure to ammonia gas at concentrations of 86 and 173 ppm did not significantly alter test results. The findings give evidence that increasing the AH in poultry buildings following an outbreak of disease could greatly reduce the length of time required for their decontamination. © Her Majesty the Queen in Right of Canada 2016.

Porous materials produced from incineration ash using thermal plasma technology.

Science.gov (United States)

Yang, Sheng-Fu; Chiu, Wen-Tung; Wang, To-Mai; Chen, Ching-Ting; Tzeng, Chin-Ching

2014-06-01

This study presents a novel thermal plasma melting technique for neutralizing and recycling municipal solid waste incinerator (MSWI) ash residues. MSWI ash residues were converted into water-quenched vitrified slag using plasma vitrification, which is environmentally benign. Slag is adopted as a raw material in producing porous materials for architectural and decorative applications, eliminating the problem of its disposal. Porous materials are produced using water-quenched vitrified slag with Portland cement and foaming agent. The true density, bulk density, porosity and water absorption ratio of the foamed specimens are studied here by varying the size of the slag particles, the water-to-solid ratio, and the ratio of the weights of the core materials, including the water-quenched vitrified slag and cement. The thermal conductivity and flexural strength of porous panels are also determined. The experimental results show the bulk density and the porosity of the porous materials are 0.9-1.2 g cm(-3) and 50-60%, respectively, and the pore structure has a closed form. The thermal conductivity of the porous material is 0.1946 W m(-1) K(-1). Therefore, the slag composite materials are lightweight and thermal insulators having considerable potential for building applications. Copyright © 2013 Elsevier Ltd. All rights reserved.

Free convection boundary layer flow past a horizontal flat plate embedded in porous medium filled by nano-fluid containing gyro-tactic microorganisms

Energy Technology Data Exchange (ETDEWEB)

Aziz, A. [Department of Mechanical Engineering, School of Engineering and Applied Science, Gonzaga University, Spokane, WA 99258 (United States); Khan, W.A. [Department of Engineering Sciences, National University of Sciences and Technology, Karachi 75350 (Pakistan); Pop, I. [Department of Applied Mathematics, Babes-Bolyai University, Cluj-Napoca (Romania)

2012-06-15

The steady boundary layer free convection flow past a horizontal flat plate embedded in a porous medium filled by a water-based nano-fluid containing gyro-tactic microorganisms is investigated. The Oberbeck-Boussinesq approximation is assumed in the analysis. The effects of bio-convection parameters on the dimensionless velocity, temperature, nano-particle concentration and density of motile microorganisms as well as on the local Nusselt, Sherwood and motile microorganism numbers are investigated and presented graphically. In the absence of bio-convection, the results are compared with the existing data in the open literature and found to be in good agreement. The bio-convection parameters strongly influence the heat, mass, and motile microorganism transport rates. (authors)

Flame spray deposition of porous catalysts on surfaces and in microsystems

DEFF Research Database (Denmark)

Thybo, Susanne; Jensen, Søren; Johansen, Johnny

2004-01-01

Flame spray synthesis is investigated as a method for one step synthesis and deposition of porous catalysts onto surfaces and into microreactors. Using a standard photolithographic lift-off process, catalyst can be deposited on flat surfaces in patterns with sub-millimeter feature sizes....... With shadow masks, porous catalyst layers can be deposited selectively into microchannels. Using Au/TiO$_2$ as test catalyst and CO-oxidation as test reaction, it is found that the apparent activation energy of the deposited catalyst is similar to what is normally seen for supported gold catalysts...

A composite sphere assemblage model for porous oolitic rocks: Application to thermal conductivity

Directory of Open Access Journals (Sweden)

F. Chen

2017-02-01

Full Text Available The present work is devoted to the determination of linear effective thermal conductivity of porous rocks characterized by an assemblage of grains (oolites coated by a matrix. Two distinct classes of pores, i.e. micropores or intra oolitic pores (oolite porosity and mesopores or inter oolitic pores (inter oolite porosity, are taken into account. The overall porosity is supposed to be connected and decomposed into oolite porosity and matrix porosity. Within the framework of Hashin composite sphere assemblage (CSA models, a two-step homogenization method is developed. At the first homogenization step, pores are assembled into two layers by using self-consistent scheme (SCS. At the second step, the two porous layers constituting the oolites and the matrix are assembled by using generalized self-consistent scheme (GSCS and referred to as three-phase model. Numerical results are presented for data representative of a porous oolitic limestone. It is shown that the influence of porosity on the overall thermal conductivity of such materials may be significant.

Models for seismic wave propagation in periodically layered porous media

NARCIS (Netherlands)

Kudarova, A.; Van Dalen, K.N.; Drijkoningen, G.G.

2014-01-01

Several models are discussed for seismic wave propagation in periodically layered poroelastic media where layers represent mesoscopic-scale heterogeneities that are larger than the pore and grain sizes but smaller than the wavelength. The layers behave according to Biot’s theory. Wave propagation

Mechanical grooving of oxidized porous silicon to reduce the reflectivity of monocrystalline silicon solar cells

Energy Technology Data Exchange (ETDEWEB)

Zarroug, A.; Dimassi, W.; Ouertani, R.; Ezzaouia, H. [Laboratoire de Photovoltaique, Centre des Recherches et des Technologies de l' Energie, BP. 95, Hammam-Lif 2050 (Tunisia)

2012-10-15

In this work, we are interested to use oxidized porous silicon (ox-PS) as a mask. So, we display the creating of a rough surface which enhances the absorption of incident light by solar cells and reduces the reflectivity of monocrystalline silicon (c-Si). It clearly can be seen that the mechanical grooving enables us to elaborate the texturing of monocrystalline silicon wafer. Results demonstrated that the application of a PS layer followed by a thermal treatment under O2 ambient easily gives us an oxide layer of uniform size which can vary from a nanometer to about ten microns. In addition, the Fourier transform infrared (FTIR) spectroscopy investigations of the PS layer illustrates the possibility to realize oxide layer as a mask for porous silicon. We found also that this simple and low cost method decreases the total reflectivity (copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Layer-by-layer bioassembly of cellularized polylactic acid porous membranes for bone tissue engineering

NARCIS (Netherlands)

Guduric, Vera; Metz, Carole; Siadous, Robin; Bareille, Reine; Levato, Riccardo; Engel, Elisabeth; Fricain, Jean-Christophe; Devillard, Raphaël; Luzanin, Ognjan; Catros, Sylvain

2017-01-01

The conventional tissue engineering is based on seeding of macroporous scaffold on its surface ("top-down" approach). The main limitation is poor cell viability in the middle of the scaffold due to poor diffusion of oxygen and nutrients and insufficient vascularization. Layer-by-Layer (LBL)

Porous PLGA microspheres tailored for dual delivery of biomolecules via layer-by-layer assembly.

Science.gov (United States)

Go, Dewi P; Palmer, Jason A; Mitchell, Geraldine M; Gras, Sally L; O'Connor, Andrea J

2015-05-01

Tissue engineering is a complex and dynamic process that requires varied biomolecular cues to promote optimal tissue growth. Consequently, the development of delivery systems capable of sequestering more than one biomolecule with controllable release profiles is a key step in the advancement of this field. This study develops multilayered polyelectrolyte films incorporating alpha-melanocyte stimulating hormone (α-MSH), an anti-inflammatory molecule, and basic fibroblast growth factor (bFGF). The layers were successfully formed on macroporous poly lactic-co-glycolic acid microspheres produced using a combined inkjet and thermally induced phase separation technique. Release profiles could be varied by altering layer properties including the number of layers and concentrations of layering molecules. α-MSH and bFGF were released in a sustained manner and the bioactivity of α-MSH was shown to be preserved using an activated macrophage cell assay in vitro. The system performance was also tested in vivo subcutaneously in rats. The multilayered microspheres reduced the inflammatory response induced by a carrageenan stimulus 6 weeks after implantation compared to the non-layered microspheres without the anti-inflammatory and growth factors, demonstrating the potential of such multilayered constructs for the controlled delivery of bioactive molecules. © 2014 Wiley Periodicals, Inc.

Normalized inverse characterization of sound absorbing rigid porous media.

Science.gov (United States)

Zieliński, Tomasz G

2015-06-01

This paper presents a methodology for the inverse characterization of sound absorbing rigid porous media, based on standard measurements of the surface acoustic impedance of a porous sample. The model parameters need to be normalized to have a robust identification procedure which fits the model-predicted impedance curves with the measured ones. Such a normalization provides a substitute set of dimensionless (normalized) parameters unambiguously related to the original model parameters. Moreover, two scaling frequencies are introduced, however, they are not additional parameters and for different, yet reasonable, assumptions of their values, the identification procedure should eventually lead to the same solution. The proposed identification technique uses measured and computed impedance curves for a porous sample not only in the standard configuration, that is, set to the rigid termination piston in an impedance tube, but also with air gaps of known thicknesses between the sample and the piston. Therefore, all necessary analytical formulas for sound propagation in double-layered media are provided. The methodology is illustrated by one numerical test and by two examples based on the experimental measurements of the acoustic impedance and absorption of porous ceramic samples of different thicknesses and a sample of polyurethane foam.

Microstructural and Optical Properties of Porous Alumina Elaborated on Glass Substrate

Science.gov (United States)

Zaghdoudi, W.; Gaidi, M.; Chtourou, R.

2013-03-01

A transparent porous anodized aluminum oxide (AAO) nanostructure was formed on a glass substrate using the anodization of a highly pure evaporated aluminum layer. A parametric study was carried out in order to achieve a fine control of the microstructural and optical properties of the elaborated films. The microstructural and surface morphologies of the porous alumina films were characterized by x-ray diffraction and atomic force microscopy. Pore diameter, inter-pore separation, and the porous structure as a function of anodization conditions were investigated. It was then found that the pores density decreases with increasing the anodization time. Regular cylindrical porous AAO films with a flat bottom structure were formed by chemical etching and anodization. A high transmittance in the 300-900 nm range is reported, indicating a fulfilled growth of the transparent sample (alumina) from the aluminum metal. The data showed typical interference oscillations as a result of the transparent characteristics of the film throughout the visible spectral range. The thickness and the optical constants ( n and k) of the porous anodic alumina films, as a function of anodizing time, were obtained using spectroscopic ellipsometry in the ultraviolet-visible-near infrared (UV-vis-NIR) regions.

Preparation and characterization of porous carbon–titania nanocomposite films as solar selective absorbers

International Nuclear Information System (INIS)

Cheng, B.; Wang, K.K.; Wang, K.P.; Li, M.; Jiang, W.; Cong, B.J.; Song, C.L.; Jia, S.H.; Han, G.R.; Liu, Y.

2015-01-01

Highlights: • The nanocomposites porous C/TiO 2 film were fabricated via PIPS method. • The HRTEM reveals the size of carbon nanoparticles is about 1.1 nm. • The PVP advantages residual carbon content but suppresses its crystallization. • The film exhibits high α (0.928–0.959) with low ε (0.074–0.105) for single layer. - Abstract: Newly proposed selective solar absorbers of porous carbon–titania nanocomposite films with a well-defined interconnected macropores structure were prepared via a polymer-assisted photopolymerization-induced phase-separation method. The microstructure and optical properties of as-deposited nanocomposite films were characterized and discussed in detail. The results show that non-ionic water-soluble polymer polyvinylpyrrolidone works as a sol modifier advantaging the mean size of the interconnected macropores, residual carbon content, and films thickness, but suppresses the order degree of the carbon remained in the films. The high-resolution transmission electron microscopy demonstrated that a small amount of graphite particles with size of around 1.1 nm embedded in the cavity of the porous while the wall of the porous consists of amorphous carbon and titania composites. The single layer of as-prepared porous C/TiO 2 nanocomposite films exhibits high solar absorptance (α = 0.928–0.959) with low thermal emittance (ε = 0.074–0.105), yielding an optimized photothermal conversion efficiency η = α − ε of 0.864 corresponding to a film thickness of around 338 nm, indication of such film is fair enough to serve as an excellent solar absorber

Engineered porous silicon counter electrodes for high efficiency dye-sensitized solar cells.

Science.gov (United States)

Erwin, William R; Oakes, Landon; Chatterjee, Shahana; Zarick, Holly F; Pint, Cary L; Bardhan, Rizia

2014-06-25

In this work, we demonstrate for the first time, the use of porous silicon (P-Si) as counter electrodes in dye-sensitized solar cells (DSSCs) with efficiencies (5.38%) comparable to that achieved with platinum counter electrodes (5.80%). To activate the P-Si for triiodide reduction, few layer carbon passivation is utilized to enable electrochemical stability of the silicon surface. Our results suggest porous silicon as a promising sustainable and manufacturable alternative to rare metals for electrochemical solar cells, following appropriate surface modification.

Dynamic characterization of partially saturated engineered porous media and gas diffusion layers using hydraulic admittance

Science.gov (United States)

Cheung, Perry; Fairweather, Joseph D.; Schwartz, Daniel T.

2012-09-01

Simple laboratory methods for determining liquid water distribution in polymer electrolyte membrane fuel cell gas diffusion layers (GDLs) are needed to engineer better GDL materials. Capillary pressure vs. liquid saturation measurements are attractive, but lack the ability to probe the hydraulic interconnectivity and distribution within the pore structure. Hydraulic admittance measurements of simple capillary bundles have recently been shown to nicely measure characteristics of the free-interfaces and hydraulic path. Here we examine the use of hydraulic admittance with a succession of increasingly complex porous media, starting with a laser-drilled sample with 154 asymmetric pores and progress to the behavior of Toray TGP-H090 carbon papers. The asymmetric laser-drilled sample clearly shows hydraulic admittance measurements are sensitive to sample orientation, especially when examined as a function of saturation state. Finite element modeling of the hydraulic admittance is consistent with experimental measurements. The hydraulic admittance spectra from GDL samples are complex, so we examine trends in the spectra as a function of wet proofing (0% and 40% Teflon loadings) as well as saturation state of the GDL. The presence of clear peaks in the admittance spectra for both GDL samples suggests a few pore types are largely responsible for transporting liquid water.

Rationally designed porous silicon as platform for optical biosensors

Energy Technology Data Exchange (ETDEWEB)

Priano, G. [INQUIMAE, DQIAyQF, FCEN, Universidad de Buenos Aires, Ciudad Universitaria, Pabellon 2 (C1428EHA) Buenos Aires (Argentina); Acquaroli, L.N.; Lasave, L.C. [Instituto De Desarrollo Tecnologico Para La Industria Quimica, UNL, CONICET, Gueemes 3450 (S3000GLN) Santa Fe (Argentina); Battaglini, F. [INQUIMAE, DQIAyQF, FCEN, Universidad de Buenos Aires, Ciudad Universitaria, Pabellon 2 (C1428EHA) Buenos Aires (Argentina); Arce, R.D., E-mail: rarce@intec.unl.edu.ar [Instituto De Desarrollo Tecnologico Para La Industria Quimica, UNL, CONICET, Gueemes 3450 (S3000GLN) Santa Fe (Argentina); Departamento De Materiales, Facultad De Ingenieria Quimica, UNL, Santiago del Estero 2829 (S3000) Santa Fe (Argentina); Koropecki, R.R. [Instituto De Desarrollo Tecnologico Para La Industria Quimica, UNL, CONICET, Gueemes 3450 (S3000GLN) Santa Fe (Argentina); Departamento De Materiales, Facultad De Ingenieria Quimica, UNL, Santiago del Estero 2829 (S3000) Santa Fe (Argentina)

2012-08-01

Optical porous silicon multilayer structures are able to work as sensitive chemical sensors or biosensors based in their optical response. An algorithm to simulate the optical response of these multilayers was developed, considering the optical properties of the individual layers. The algorithm allows designing and customizing the porous silicon structures according to a given application. The results obtained by the simulation were experimentally verified; for this purpose different photonic structures were prepared, such as Bragg reflectors and microcavities. Some of these structures have been derivatized by the introduction of aminosilane groups on the porous silicon surface. The algorithm also permits to simulate the effects produced by a non uniform derivatization of the multilayer. - Highlights: Black-Right-Pointing-Pointer Mesoporous silicon structure Black-Right-Pointing-Pointer Functionalization of mesoporous silicon as sensors Black-Right-Pointing-Pointer Design of the one-dimensional photonic crystal Black-Right-Pointing-Pointer Simulation of non-uniformity in covering the sensor structure.

Protein encapsulation via porous CaCO3 microparticles templating.

Science.gov (United States)

Volodkin, Dmitry V; Larionova, Natalia I; Sukhorukov, Gleb B

2004-01-01

Porous microparticles of calcium carbonate with an average diameter of 4.75 microm were prepared and used for protein encapsulation in polymer-filled microcapsules by means of electrostatic layer-by-layer assembly (ELbL). Loading of macromolecules in porous CaCO3 particles is affected by their molecular weight due to diffusion-limited permeation inside the particles and also by the affinity to the carbonate surface. Adsorption of various proteins and dextran was examined as a function of pH and was found to be dependent both on the charge of the microparticles and macromolecules. The electrostatic effect was shown to govern this interaction. This paper discusses the factors which can influence the adsorption capacity of proteins. A new way of protein encapsulation in polyelectrolyte microcapsules is proposed exploiting the porous, biocompatible, and decomposable microparticles from CaCO3. It consists of protein adsorption in the pores of the microparticles followed by ELbL of oppositely charged polyelectrolytes and further core dissolution. This resulted in formation of polyelectrolyte-filled capsules with protein incorporated in interpenetrating polyelectrolyte network. The properties of CaCO3 microparticles and capsules prepared were characterized by scanning electron microscopy, microelectrophoresis, and confocal laser scanning microscopy. Lactalbumin was encapsulated by means of the proposed technique yielding a content of 0.6 pg protein per microcapsule. Horseradish peroxidase saves 37% of activity after encapsulation. However, the thermostability of the enzyme was improved by encapsulation. The results demonstrate that porous CaCO3 microparticles can be applied as microtemplates for encapsulation of proteins into polyelectrolyte capsules at neutral pH as an optimal medium for a variety of bioactive material, which can also be encapsulated by the proposed method. Microcapsules filled with encapsulated material may find applications in the field of

Arsenic sulfide layers for dielectric reflection mirrors prepared from solution

Science.gov (United States)

Matějec, Vlastimil; Pedlikova, Jitka; BartoÅ, Ivo; Podrazký, Ondřej

2017-12-01

Chalcogenide materials due to high refractive indices, transparency in the mid-IR spectral region, nonlinear refractive indices, etc, have been employed as fibers and films in different photonic devices such as light amplifiers, optical regenerators, broadband radiation sources. Chalcogenide films can be prepared by physical methods as well as by solution-based techniques in which solutions of chalcogenides in amines are used. This paper presents results on the solution-based fabrication and optical characterization of single arsenic sulfide layers and multilayer stacks containing As2S3 layers together with porous silica layers coated on planar and fiber-optic substrates. Input As2S3 solutions for the layer fabrications were prepared by dissolving As2S3 powder in n-propylamine in a concentration of 0.50 mol/l. These solutions were applied on glass slides by dip-coating method and obtained layers were thermally treated in vacuum at temperatures up to 180 °C. Similar procedure was used for As2S3 layers in multilayer stacks. Such stacks were fabricated by repeating the application of one porous silica layer prepared by the sol-gel method and one As2S3 layer onto glass slides or silica fibers (a diameter of 0.3 mm) by using the dip-coating method. It has been found that the curing process of the applied layers has to be carefully controlled in order to obtain stacks with three pairs of such layers. Single arsenic and porous silica layers were characterized by optical microscopy, and by measuring their transmission spectra in a range of 200-2500 nm. Thicknesses and refractive indices were estimated from the spectra. Transmission spectra of planar multilayer stacks were measured, too. Interference bands have been determined from optical measurements on the multilayer stacks with a minimum transmittance of about 50% which indicates the possibility of using such stacks as reflecting mirrors.

Swelling, Functionalization, and Structural Changes of the Nanoporous Layered Silicates AMH-3 and MCM-22

KAUST Repository

Kim, Wun-gwi; Choi, Sunho; Nair, Sankar

2011-01-01

Nanoporous layered silicate materials contain 2D-planar sheets of nanoscopic thickness and ordered porous structure. In comparison to porous 3D-framework materials such as zeolites, they have advantages such as significantly increased surface area

High strength, surface porous polyether-ether-ketone for load-bearing orthopaedic implants

Science.gov (United States)

Evans, Nathan T.; Torstrick, F. Brennan; Lee, Christopher S.D.; Dupont, Kenneth M.; Safranski, David L.; Chang, W. Allen; Macedo, Annie E.; Lin, Angela; Boothby, Jennifer M.; Whittingslow, Daniel C.; Carson, Robert A.; Guldberg, Robert E.; Gall, Ken

2015-01-01

Despite its widespread clinical use in load-bearing orthopaedic implants, polyether-ether-ketone (PEEK) is often associated with poor osseointegration. In this study, a surface porous PEEK material (PEEK-SP) was created using a melt extrusion technique. The porous layer thickness was 399.6±63.3 µm and possessed a mean pore size of 279.9±31.6 µm, strut spacing of 186.8±55.5 µm, porosity of 67.3±3.1%, and interconnectivity of 99.9±0.1%. Monotonic tensile tests showed that PEEK-SP preserved 73.9% of the strength (71.06±2.17 MPa) and 73.4% of the elastic modulus (2.45±0.31 GPa) of as-received, injection molded PEEK. PEEK-SP further demonstrated a fatigue strength of 60.0 MPa at one million cycles, preserving 73.4% of the fatigue resistance of injection molded PEEK. Interfacial shear testing showed the pore layer shear strength to be 23.96±2.26 MPa. An osseointegration model in the rat revealed substantial bone formation within the pore layer at 6 and 12 weeks via µCT and histological evaluation. Ingrown bone was more closely apposed to the pore wall and fibrous tissue growth was reduced in PEEK-SP when compared to non-porous PEEK controls. These results indicate that PEEK-SP could provide improved osseointegration while maintaining the structural integrity necessary for load-bearing orthopaedic applications. PMID:25463499

Multi-layered, chemically bonded lithium-ion and lithium/air batteries

Science.gov (United States)

Narula, Chaitanya Kumar; Nanda, Jagjit; Bischoff, Brian L; Bhave, Ramesh R

2014-05-13

Disclosed are multilayer, porous, thin-layered lithium-ion batteries that include an inorganic separator as a thin layer that is chemically bonded to surfaces of positive and negative electrode layers. Thus, in such disclosed lithium-ion batteries, the electrodes and separator are made to form non-discrete (i.e., integral) thin layers. Also disclosed are methods of fabricating integrally connected, thin, multilayer lithium batteries including lithium-ion and lithium/air batteries.