The sub-zero Celsius treatment of precipitation hardenable semi-austenitic stainless steel

DEFF Research Database (Denmark)

Villa, Matteo; Hansen, Mikkel Fougt; Somers, Marcel A. J.

2015-01-01

A precipitation hardenable semi-austenitic stainless steel AISI 632 grade was austenitized according to industrial specifications and thereafter subjected to isothermal treatment at sub-zero Celsius temperatures. During treatment, austenite transformed to martensite. The isothermal austenite-to-martensite...... treatment. Magnetometry showed that the additional thermal step in boiling nitrogen yields a minor increment of the fraction of martensite, but has a noteworthy accelerating effect on the transformation kinetics, which more pronounced when the isothermal holding is performed at a higher temperature. Data...... is interpreted in terms of instantaneous nucleation of martensite during cooling followed by time dependent growth during isothermal holding....

On the grain boundary hardening in a B-bearing 304 austenitic stainless steel

International Nuclear Information System (INIS)

Yao, X.X.

1999-01-01

The precipitates, (Cr,Fe) 23 (C,B) 6 carbides and (Cr,Fe) 2 B borides, formed along the grain boundaries in a 304 austenitic stainless steel containing boron of 33 ppm after solution treatment at 1100 C for 1 h followed by isothermal ageing for 0.5 h at temperatures ranging from 750 to 1050 C have been identified. The influence of these precipitates on the grain boundary hardening has been investigated by means of micro-Vickers hardness measurements. It is found that the degree of grain boundary hardening below 900 C decreases, while it increases above 900 C with increasing ageing temperature. The dissolution of (Cr,Fe) 23 (C,B) 6 carbides and the precipitation of (Cr,Fe) 2 B borides are associated with the changes of grain boundary hardening in this B-bearing 304 austenitic stainless steel between 750 and 1100 C. The non-equilibrium boron segregation enhances the grain boundary hardening when the ageing temperature is above 900 C. (orig.)

Isothermal martensite formation at sub-zero temperatures

DEFF Research Database (Denmark)

Stojko, Allan; Hansen, Mikkel Fougt; Slycke, Jan

2010-01-01

austenitized and quenched in oil and thereafter investigated with vibrating sample agnetometry, which allows a quantitative assessment of the fraction of retained austenite as a function of the subzero temperature and time. Isothermal martensite formation was observed on interrupting the continuous cooling (5...... with a continuation of the martensitic transformation. On prolonged isothermal holding a volume reduction was observed for AISI 52100, but not for AISI 1070. A mechanism is proposed that explains the occurrence of isothermal martensite formation....

Martensitic transformation behaviour in sensitized SUS304 austenitic stainless steel during isothermal holding at low temperature

International Nuclear Information System (INIS)

Lee, Jae-hwa; Fukuda, Takashi; Kakeshita, Tomoyuki

2009-01-01

We investigated martensitic transformation behaviour in sensitized SUS304 austenitic stainless steel to determine the stability of the austenitic phase at low temperatures. We found that a specimen that was sensitized at 973 K for 100 h exhibits an isothermal martensitic transformation when the specimen is held in the temperature range between 60 and 260 K. We constructed a time-temperature-transformation (TTT) diagram corresponding to the formation of 0.5 vol. % α'-martensite. A magnetization measurement was used to evaluate the volume fraction of a'-martensite. The TTT diagram shows a double-C curve with two noses located at about 100 and 200 K. In-situ optical microscope observations reveal that the double C-curve is due to two different transformation sequences. That is, the upper part of the C-curve is due to a direct γ → α' martensitic transformation and the lower part of the C-curve is due to a successive γ → ψ → α' martensitic transformation. The direct γ → α' transformation occurs in the vicinity of grain boundaries while the successive γ → ψ' → α' transformation occurs near the centre of grains. A scanning electron microscope observation reveals that carbide particles of M 23 C 6 are formed in the grain boundaries. The concentration difference between the centre of the grains and regions near grain boundaries is the reason for the difference in the isothermal transformation sequence for the sensitized SUS304 stainless steel.

Corrosion of austenitic steels and their components in vanadium-containing chloride melts

Science.gov (United States)

Abramov, A. V.; Polovov, I. B.; Rebrin, O. I.; Lisienko, D. G.

2014-08-01

The corrosion of austenitic 12Kh18N10T, 10Kh17N13M2T, and 03Kh17N14M3 steels and their components (Cr, Fe, Ni, Mo) in NaCl-KCl-VCl2 melts with 5 wt % V at 750°C is studied. The rates and mechanisms of corrosion of the materials under these conditions are determined. The processes that occur during contact of the metals and steels with vanadium-containing chloride electrolytes are investigated.

Effect of austenitization conditions on kinetics of isothermal transformation of austenite of structural steels

International Nuclear Information System (INIS)

Konopleva, E.V.; Bayazitov, V.M.; Abramov, O.V.; Kozlova, A.G.

1987-01-01

Effect of austenization of kinetics of pearlite and bainite transformations for steels with different carbon content differing by alloying character and degree has been investigated. Austenization temperature increase is shown to leads to retardation of ferrite-pearlite transformation in low- and medium-carbon alloyed steels. Step-like holding in the region of austenite stable state (850, 950 deg) after high-temperature heating (1100 deg C) increases the rate of transformation partially recovering its kinetics and decomposition velocity after low-temperature heating in steels alloyed advantageously with carbide-forming elements (08Kh2G2F, 30Kh3) and does not affect kinetics in the 35Kh, 30KhGSN2A, 45N5 steels. Increase of heating temperature and growth of an austenite grain cause considerable acceleration of bainite transformation, increase of the temperaure of bainite transformation beginning and increase of the transformation amplitude in the 08Kh2G2F, 30Kh3 steels and affect weakly kinetics in steels with mixed alloying (30KhGSN2A) or low-alloy one (35Kh). The bainite transformation rate in the 45N5 steelite does not depend on austenization. The effect of additional acceleration of bainite transformation as a result holding after high-temperature heating in those steels, where activation of transformation occurs with increase of heating temperature

In-situ characterization of transformation plasticity during an isothermal austenite-to-bainite phase transformation

International Nuclear Information System (INIS)

Holzweissig, M.J.; Canadinc, D.; Maier, H.J.

2012-01-01

This paper elucidates the stress-induced variant selection process during the isothermal austenite-to-bainite phase transformation in a tool steel. Specifically, a thorough set of experiments combining electron backscatter diffraction and in-situ digital image correlation (DIC) was carried out to establish the role of superimposed stress level on the evolution of transformation plasticity (TP) strains. The important finding is that TP increases concomitant with the superimposed stress level, and strain localization accompanies phase transformation at all stress levels considered. Furthermore, TP strain distribution within the whole material becomes more homogeneous with increasing stress, such that fewer bainitic variants are selected to grow under higher stresses, yielding a more homogeneous strain distribution. In particular, the bainitic variants oriented along [101] and [201] directions are favored to grow parallel to the loading axis and are associated with large TP strains. Overall, this very first in-situ DIC investigation of the austenite-to-bainite phase transformation in steels evidences the clear relationship between the superimposed stress level, variant selection, and evolution of TP strains. - Highlights: ► Local variations of strain were observed by DIC throughout the phase transformation. ► The study clearly established the role of the stress-induced variant selection. ► Variant selection is a key parameter that governs distortion.

Effect of Precipitation on Cryogenic Toughness in Isothermally Aged Austenitic Stainless Steel

Science.gov (United States)

Saucedo-Muñoz, M. L.; Lopez-Hirata, V. M.; Avila-Davila, E. O.; Villegas-Cardenas, J. D.; Gonzalez-Velazquez, J. L.

2017-03-01

The effect of grain-boundary precipitates on cryogenic impact toughness of two corrosion steels (standard AISI 316 and a steel with a nitrogen additive) is studied. The steels are aged at 600 - 900°C with a hold of up to 1000 min. The KCV impact toughness at -196°C is determined. It is shown that the impact toughness of the nitrogen-containing steel decreases under cooling after the aging at 700 and 800°C more considerably than that of steel 316 after aging at 800 and 900°C. The causes of the embrittlement of the nitrogen-containing steel are determined.

In-situ characterization of transformation plasticity during an isothermal austenite-to-bainite phase transformation

Energy Technology Data Exchange (ETDEWEB)

Holzweissig, M.J., E-mail: martinh@mail.upb.de [University of Paderborn, Lehrstuhl fuer Werkstoffkunde (Materials Science), 33095 Paderborn (Germany); Canadinc, D., E-mail: dcanadinc@ku.edu.tr [Koc University, Advanced Materials Group, Department of Mechanical Engineering, 34450 Istanbul (Turkey); Maier, H.J., E-mail: hmaier@mail.upb.de [University of Paderborn, Lehrstuhl fuer Werkstoffkunde (Materials Science), 33095 Paderborn (Germany)

2012-03-15

This paper elucidates the stress-induced variant selection process during the isothermal austenite-to-bainite phase transformation in a tool steel. Specifically, a thorough set of experiments combining electron backscatter diffraction and in-situ digital image correlation (DIC) was carried out to establish the role of superimposed stress level on the evolution of transformation plasticity (TP) strains. The important finding is that TP increases concomitant with the superimposed stress level, and strain localization accompanies phase transformation at all stress levels considered. Furthermore, TP strain distribution within the whole material becomes more homogeneous with increasing stress, such that fewer bainitic variants are selected to grow under higher stresses, yielding a more homogeneous strain distribution. In particular, the bainitic variants oriented along [101] and [201] directions are favored to grow parallel to the loading axis and are associated with large TP strains. Overall, this very first in-situ DIC investigation of the austenite-to-bainite phase transformation in steels evidences the clear relationship between the superimposed stress level, variant selection, and evolution of TP strains. - Highlights: Black-Right-Pointing-Pointer Local variations of strain were observed by DIC throughout the phase transformation. Black-Right-Pointing-Pointer The study clearly established the role of the stress-induced variant selection. Black-Right-Pointing-Pointer Variant selection is a key parameter that governs distortion.

Microstructural evolution during isothermal aging and strain-induced transformation followed by isothermal aging in Co-Cr-Mo-C alloy: A comparative study

International Nuclear Information System (INIS)

Lashgari, H.R.; Zangeneh, Sh.; Hasanabadi, F.; Saghafi, M.

2010-01-01

The present study was undertaken to investigate the effects of isothermal aging (at 850 deg. C for 4, 8, 16 and 24 h) and strain-induced transformation (engineering strains of 10% and 20%) followed by isothermal aging (at 850 deg. C for 4, 8 and 16 h) on the microstructural evolution of a Co-28Cr-5Mo-0.3C alloy. The obtained results showed that isothermal aging at 850 deg. C resulted in the formation of lamellar-type carbides at the grain boundaries. Moreover, X-ray diffraction analysis indicated that isothermal aging of solution treated specimens at 850 deg. C for 24 h did not lead to complete fcc phase transformation to hcp one. In contrast with the isothermally aged specimens, applying plastic deformation to the solutionized samples accelerated the completion and saturation of fcc(metastable) → hcp transformation after 8 h aging at 850 deg. C. In addition, the X-ray diffraction results indicated that implementing isothermal aging of the strain-induced specimens at the higher aging time (16 h) caused the formation of (1 1 1) fcc and (2 0 0) fcc diffraction peaks again. Also, the strain-induced specimens followed by isothermal aging showed higher amount of microhardness as compared with the other specimens aged solely.

Evolution behavior of nanohardness after thermal-aging and hydrogen-charging on austenite and strain-induced martensite in pre-strained austenitic stainless steel

Science.gov (United States)

Zheng, Yuanyuan; Zhou, Chengshuang; Hong, Yuanjian; Zheng, Jinyang; Zhang, Lin

2018-05-01

Nanoindentation has been used to study the effects of thermal-aging and hydrogen on the mechanical property of the metastable austenitic stainless steel. Thermal-aging at 473 K decreases the nanohardness of austenite, while it increases the nanohardness of strain-induced ɑ‧ martensite. Hydrogen-charging at 473 K increases the nanohardness of austenite, while it decreases the nanohardness of strain-induced ɑ‧ martensite. The opposite effect on austenite and ɑ‧ martensite is first found in the same pre-strained sample. This abnormal evolution behavior of hardness can be attributed to the interaction between dislocation and solute atoms (carbon and hydrogen). Carbon atoms are difficult to move and redistribute in austenite compared with ɑ‧ martensite. Therefore, the difference in the diffusivity of solute atoms between austenite and ɑ‧ martensite may result in the change of hardness.

A review on nickel-free nitrogen containing austenitic stainless steels for biomedical applications.

Science.gov (United States)

Talha, Mohd; Behera, C K; Sinha, O P

2013-10-01

The field of biomaterials has become a vital area, as these materials can enhance the quality and longevity of human life. Metallic materials are often used as biomaterials to replace structural components of the human body. Stainless steels, cobalt-chromium alloys, commercially pure titanium and its alloys are typical metallic biomaterials that are being used for implant devices. Stainless steels have been widely used as biomaterials because of their very low cost as compared to other metallic materials, good mechanical and corrosion resistant properties and adequate biocompatibility. However, the adverse effects of nickel ions being released into the human body have promoted the development of "nickel-free nitrogen containing austenitic stainless steels" for medical applications. Nitrogen not only replaces nickel for austenitic structure stability but also much improves steel properties. Here we review the harmful effects associated with nickel and emphatically the advantages of nitrogen in stainless steel, as well as the development of nickel-free nitrogen containing stainless steels for medical applications. By combining the benefits of stable austenitic structure, high strength, better corrosion and wear resistance and superior biocompatibility in comparison to the currently used austenitic stainless steel (e.g. 316L), the newly developed nickel-free high nitrogen austenitic stainless steel is a reliable substitute for the conventionally used medical stainless steels. Copyright © 2013 Elsevier B.V. All rights reserved.

Stainless austenitic steels strengthened due to reversible phase transformations and by ageing

International Nuclear Information System (INIS)

Sagaradze, V.V.; Kositsyna, I.I.; Ozhiganov, A.V.

1981-01-01

The effect of the reversible phase transformations, consisting in the conduction of the direct and reverse martensite transformations and aging, during which the intermetallide γ'-phase of the composition Ni 3 Ti is formed, on the streng-thening of alloys in the Fe-Cr-Ni-Ti system is considered. Stainless austenitic steels Kh12N12T3 and Kh12N14T3, which acquire high mechanical properties: σsub(0.2)=685-785 MPa, σsub(B)=1275 MPa, delta >= 20%, as a result of reversible phase transformations and aging, are suggested. After the reversible phase transformations and ageing the steels possess a high resistance to γ-α-transformation during cold treatment [ru

Experimental and computational study of nitride precipitation in a CrMnN austenitic stainless steel

International Nuclear Information System (INIS)

Pettersson, Niklas; Frisk, Karin; Fluch, Rainer

2017-01-01

The austenitic CrMnN stainless steels are high-strength, tough, and non-magnetic, and are used in oil field applications. The steels have high alloying contents, and precipitation of Cr-nitrides and/or intermetallic phases can occur when cooling through the temperature region 950–700 °C. The nitride precipitates appear in the grain boundaries but can be difficult to observe in the microstructure due to their small size. However, there is an effect of precipitation on corrosion and impact strength and a modelling approach to predict precipitation is valuable for alloy and process development. In the present work precipitation simulations were applied to a CrMnN steel composition, and coupled to experimental investigations after heat treatments at 700 and 800 °C. The early stages, with short heat-treatment times, were studied. The simulations were performed using TC-PRISMA, a software for calculation of multiphase precipitation kinetics, using multicomponent nucleation and growth models. Dedicated thermodynamic and kinetic databases were used for the simulations. The main precipitate was identified by experiments and simulations to be the Cr 2 N nitride, and the precipitation during isothermal heat treatments was investigated. Isothermal precipitation diagrams are simulated, and the influence of precipitation kinetics on toughness is discussed.

Experimental and computational study of nitride precipitation in a CrMnN austenitic stainless steel

Energy Technology Data Exchange (ETDEWEB)

Pettersson, Niklas, E-mail: niklas.pettersson@swerea.se [Swerea KIMAB AB, P.O. Box 7047, 164 07 Kista (Sweden); Frisk, Karin [Swerea KIMAB AB, P.O. Box 7047, 164 07 Kista (Sweden); Fluch, Rainer [Böhler Edelstahl Gmbh, Mariazeller Strasse 25, 8605 Kapfenberg (Austria)

2017-01-27

The austenitic CrMnN stainless steels are high-strength, tough, and non-magnetic, and are used in oil field applications. The steels have high alloying contents, and precipitation of Cr-nitrides and/or intermetallic phases can occur when cooling through the temperature region 950–700 °C. The nitride precipitates appear in the grain boundaries but can be difficult to observe in the microstructure due to their small size. However, there is an effect of precipitation on corrosion and impact strength and a modelling approach to predict precipitation is valuable for alloy and process development. In the present work precipitation simulations were applied to a CrMnN steel composition, and coupled to experimental investigations after heat treatments at 700 and 800 °C. The early stages, with short heat-treatment times, were studied. The simulations were performed using TC-PRISMA, a software for calculation of multiphase precipitation kinetics, using multicomponent nucleation and growth models. Dedicated thermodynamic and kinetic databases were used for the simulations. The main precipitate was identified by experiments and simulations to be the Cr{sub 2}N nitride, and the precipitation during isothermal heat treatments was investigated. Isothermal precipitation diagrams are simulated, and the influence of precipitation kinetics on toughness is discussed.

Austenite strengthening and softening during hot deformation

International Nuclear Information System (INIS)

Tushinskij, L.I.; Vlasov, V.S.; Kazimirova, I.E.; Tokarev, A.O.

1981-01-01

Processes of formation of austenite structure of 20 and 12Kh18N10T steels during hot deformation and postdeformation isothermal holdings have been investigated by the methods of analysis of curves of hot deformation, high-temperature metallography and light microscopy. Deformation has been exercised by extention in vacuum with average 4x10 -2 s -1 rate. Deformation temperatures of steel 20 are 930 and 1000 deg C, of steel 12Kh18N10T - 1100 deg C. It is stated that dynamic recrystallization takes place in both investigated steels during hot deformation. In the carbonic steel it is developed by shifting sections of high-angular boundaries, flow stress in this case remains constant. Recrystallization is developed by subgrain coalescence in austenite steel, that brings about preservation of increased defect density in recrystallized volumes. As a result strengthening of steel is continued up to fracture during the increase of the deformation degree. Postdeformation weakening of 12Kh18N10T steel is slowed down as compared with weakening of carbonic steel [ru

Effect of aging on the tribological and mechanical properties of a high-nitrogen stainless austenitic steel

International Nuclear Information System (INIS)

Korshunov, L.G.; Chernenko, N.L.; Tereshchenko, N.A.; Uvarov, A.I.

2005-01-01

The effect of aging, associated with predominant precipitation of vanadium nitrides (VN), on tribological and mechanical properties of austenitic steel 10Kh18AG18N5MF hardened from 1100 Deg C is studied. Metallographic, X-ray diffraction and electron microscopical methods are used to study structural transformations proceeding in the steel on aging as well as on friction loading under conditions of dry slipping friction in steel-abrasive and steel-steel pairs. It is shown that the aging at temperatures of 600-700 Deg C resulting in a considerable increase of strength properties of the steel demonstrates a relatively weak positive effect on steel resistance to abrasive and adhesive wear. It is stated that the use of aging by continuous mechanism permits attaining favourable mechanical and tribological properties in vanadium-alloying nitrogen-bearing austenitic steels [ru

Precipitation behavior during thin slab thermomechanical processing and isothermal aging of copper-bearing niobium-microalloyed high strength structural steels: The effect on mechanical properties

Energy Technology Data Exchange (ETDEWEB)

Misra, R.D.K., E-mail: dmisra@louisiana.edu [Center for Structural and Functional Materials, University of Louisiana at Lafayette, P.O. Box 44130, Lafayette, LA 70503 (United States); Jia, Z. [Center for Structural and Functional Materials, University of Louisiana at Lafayette, P.O. Box 44130, Lafayette, LA 70503 (United States); O' Malley, R. [Nucor Steel Decatur, LLC Sheet Mill, 4301, Iverson Blvd., Trinity, AL 35673 (United States); Jansto, S.J. [CBMM-Reference Metals Company, 1000 Old Pond Road, Bridgeville, PA 15017 (United States)

2011-11-15

Highlights: {yields} Copper does not significantly influence toughness. {yields} Copper precipitation during aging occurs at dislocations. {yields} Precipitation of copper and carbides is mutually exclusive. - Abstract: We describe here the precipitation behavior of copper and fine-scale carbides during thermo-mechanical processing and isothermal aging of copper-bearing niobium-microalloyed high strength steels. During thermo-mechanical processing, precipitation of {epsilon}-copper occurs in polygonal ferrite and at the austenite-ferrite interface. In contrast, during isothermal aging, nucleation of {epsilon}-copper precipitation occurs at dislocations. In the three different chemistries investigated, the increase in strength associated with copper during aging results only in a small decrease in impact toughness, implying that copper precipitates do not seriously impair toughness, and can be considered as a viable strengthening element in microalloyed steels. Precipitation of fine-scale niobium carbides occurs extensively at dislocations and within ferrite matrix together with vanadium carbides. In the presence of titanium, titanium carbides act as a nucleus for niobium carbide formation. Irrespective of the nature of carbides, copper precipitates and carbides are mutually exclusive.

Precipitation behavior during thin slab thermomechanical processing and isothermal aging of copper-bearing niobium-microalloyed high strength structural steels: The effect on mechanical properties

International Nuclear Information System (INIS)

Misra, R.D.K.; Jia, Z.; O'Malley, R.; Jansto, S.J.

2011-01-01

Highlights: → Copper does not significantly influence toughness. → Copper precipitation during aging occurs at dislocations. → Precipitation of copper and carbides is mutually exclusive. - Abstract: We describe here the precipitation behavior of copper and fine-scale carbides during thermo-mechanical processing and isothermal aging of copper-bearing niobium-microalloyed high strength steels. During thermo-mechanical processing, precipitation of ε-copper occurs in polygonal ferrite and at the austenite-ferrite interface. In contrast, during isothermal aging, nucleation of ε-copper precipitation occurs at dislocations. In the three different chemistries investigated, the increase in strength associated with copper during aging results only in a small decrease in impact toughness, implying that copper precipitates do not seriously impair toughness, and can be considered as a viable strengthening element in microalloyed steels. Precipitation of fine-scale niobium carbides occurs extensively at dislocations and within ferrite matrix together with vanadium carbides. In the presence of titanium, titanium carbides act as a nucleus for niobium carbide formation. Irrespective of the nature of carbides, copper precipitates and carbides are mutually exclusive.

Phase Equilibrium and Austenite Decomposition in Advanced High-Strength Medium-Mn Bainitic Steels

Directory of Open Access Journals (Sweden)

Adam Grajcar

2016-10-01

Full Text Available The work addresses the phase equilibrium analysis and austenite decomposition of two Nb-microalloyed medium-Mn steels containing 3% and 5% Mn. The pseudobinary Fe-C diagrams of the steels were calculated using Thermo-Calc. Thermodynamic calculations of the volume fraction evolution of microstructural constituents vs. temperature were carried out. The study comprised the determination of the time-temperature-transformation (TTT diagrams and continuous cooling transformation (CCT diagrams of the investigated steels. The diagrams were used to determine continuous and isothermal cooling paths suitable for production of bainite-based steels. It was found that the various Mn content strongly influences the hardenability of the steels and hence the austenite decomposition during cooling. The knowledge of CCT diagrams and the analysis of experimental dilatometric curves enabled to produce bainite-austenite mixtures in the thermomechanical simulator. Light microscopy (LM, scanning electron microscopy (SEM, and transmission electron microscopy (TEM were used to assess the effect of heat treatment on morphological details of produced multiphase microstructures.

Expanded austenite in nitrided layers deposited on austenitic and super austenitic stainless steel grades

International Nuclear Information System (INIS)

Casteletti, L.C.; Fernandes, F.A.P.; Heck, S.C.; Gallego, J.

2010-01-01

In this work nitrided layers deposited on austenitic and super austenitic stainless steels were analyzed through optical microscopy and X-rays diffraction analysis (XRD). It was observed that the formation of N supersaturated phase, called expanded austenite, has promoted significant increment of hardness (> 1000HV). XRD results have indicated the anomalous displacement of the diffracted peaks, in comparison with the normal austenite. This behavior, combined with peaks broadening, it was analyzed in different nitriding temperatures which results showed good agreement with the literature. (author)

Influence of aging condition and reversion austenite on fatigue property of the 300 grade 18Ni maraging steel

International Nuclear Information System (INIS)

Moriyama, Michihiko; Takaki, Setsuo; Kawagoishi, Norio

2000-01-01

The influence of aging condition on fatigue strength of the 300 grade 18Ni maraging steel has been investigated in relation to the behavior of age hardening and the formation of reversion austenite. In this study, rotating bending fatigue tests were performed for three series of specimens with different aging condition; as solution-treated without aging, aged for various time at 753 K which is the temperature applied for the industrial aging treatment, and over-aged to form a small amount of reversion austenite. Effect of reversion austenite on fatigue strength was examined using specimens with the same static strength which had been controlled by varying aging temperature and time, namely under-aging or over-aging. The main results obtained are as follows. (1) In the case of 753 K aging, the fatigue limits of specimens aged for 11 ks to 48 ks were nearly the same value, although an under-aged (2.8 ks) specimen has as much lower value as a solution-treated specimen without aging treatment. (2) A small amount of reversion austenite is effective for increasing fatigue resistance. For instance, 2 vol% of austenite was enough for improving fatigue limit of the maraging steel used, from 580 MPa to 640 MPa at the same hardness level of Hv 610. (author)

Isothermal martensite formation at sub-zero temperatures

DEFF Research Database (Denmark)

Stojko, Allan; Hansen, Mikkel Fougt; Slycke, Jan

2012-01-01

, quenched in oil, and thereafter investigated with vibrating sample magnetometry, which allows a quantitative assessment of the fraction of retained austenite as a function of the sub-zero temperature and time. Isothermal martensite formation was observed on interrupting the continuous cooling (5 K...... with a continuation of the martensitic transformation. On prolonged isothermal holding, a volume reduction was observed for AISI 52100, but not for AISI 1070. Copyright © 2011 by ASTM International....

Characterization of bainitic/martensitic structures formed in isothermal treatments below the M

NARCIS (Netherlands)

Navarro Lopez, A.; Hidalgo Garcia, J.; Sietsma, J.; Santofimia Navarro, M.J.

2017-01-01

Advanced Multiphase High Strength Steels are generally obtained by applying isothermal treatments around the martensite start temperature (M_s). Previous investigations have shown that bainitic ferrite can form from austenite in isothermal treatments below M_s, where its

Low temperature thermal ageing embrittlement of austenitic stainless steel welds and its electrochemical assessment

International Nuclear Information System (INIS)

Chandra, K.; Kain, Vivekanand; Raja, V.S.; Tewari, R.; Dey, G.K.

2012-01-01

Highlights: ► Embrittlement study of austenitic stainless steel welds after ageing up to 20,000 h. ► Spinodal decomposition and G-phase precipitation in ferrite at 400 °C. ► Spinodal decomposition of ferrite at 335 and 365 °C. ► Large decrease in corrosion resistance due to G-phase precipitation. ► Good correlation between electrochemical properties and the degree of embrittlement. - Abstract: The low temperature thermal ageing embrittlement of austenitic stainless steel welds is investigated after ageing up to 20,000 h at 335, 365 and 400 °C. Spinodal decomposition and G-phase precipitation after thermal ageing were identified by transmission electron microscopy. Ageing led to increase in hardness of the ferrite phase while there was no change in the hardness of austenite. The degree of embrittlement was evaluated by non-destructive methods, e.g., double-loop and single-loop electrochemical potentiokinetic reactivation tests. A good correlation was obtained between the electrochemical properties and hardening of the ferrite phase of the aged materials.

Comparative Study of Hardening Mechanisms During Aging of a 304 Stainless Steel Containing α'-Martensite

Science.gov (United States)

Jeong, S. W.; Kang, U. G.; Choi, J. Y.; Nam, W. J.

2012-09-01

Strain aging and hardening behaviors of a 304 stainless steel containing deformation-induced martensite were investigated by examining mechanical properties and microstructural evolution for different aging temperature and time. Introduced age hardening mechanisms of a cold rolled 304 stainless steel were the additional formation of α'-martensite, hardening of α'-martensite, and hardening of deformed austenite. The increased amount of α'-martensite at an aging temperature of 450 °C confirmed the additional formation of α'-martensite as a hardening mechanism in a cold rolled 304 stainless steel. Additionally, the increased hardness in both α'-martensite and austenite phases with aging temperature proved that hardening of both α'-martensite and austenite phases would be effective as hardening mechanisms in cold rolled and aged 304 stainless steels. The results suggested that among hardening mechanisms, hardening of an α'-martensite phase, including the diffusion of interstitial solute carbon atoms to dislocations and the precipitation of fine carbide particles would become a major hardening mechanism during aging of cold rolled 304 stainless steels.

Isothermal martensitic transformation as an internal-stress-increasing process

International Nuclear Information System (INIS)

Liu, Y.; Xie, Z.L.; Haenninen, H.; Humbeeck, J. van; Pietikaeinen, J.

1995-01-01

Based on the results that the magnitude of the stabilization of retained austenite increases with increasing the amount of martensite transformed, it has been assumed that the martensitic transformation is accompanied with an increase in internal resisting stress which subsequently results in the stabilization of retained austenite. By simplifying this internal resisting stress to be a type of hydrostatic compressive stress acting on retained austenite due to surrounding martensite plates, a thermodynamical analysis for an isothermal martensitic transformation under applied hydrostatic pressure has been performed. The calculated results, to some extent, show a good agreement with the experimental data. (orig.)

Influence of delta ferrite on corrosion susceptibility of AISI 304 austenitic stainless steel

Directory of Open Access Journals (Sweden)

Lawrence O. Osoba

2016-12-01

Full Text Available In the current study, the influence of delta (δ ferrite on the corrosion susceptibility of AISI 304 austenitic stainless steel was evaluated in 1Molar concentration of sulphuric acid (H2SO4 and 1Molar concentration of sodium chloride (NaCl. The study was performed at ambient temperature using electrochemical technique—Tafel plots to evaluate the corrosive tendencies of the austenitic stainless steel sample. The as-received (stainless steel specimen and 60% cold-worked (stainless steel specimens were isothermally annealed at 1,100°C for 2 h and 1 h, respectively, and quenched in water. The results obtained show that the heat-treated specimen and the 60% cold-worked plus heat-treated specimen exhibited higher corrosion susceptibility than the as-received specimen, which invariably contained the highest fraction of δ ferrite particles. The finding shows that the presence of δ ferrite, in which chromium (Cr, the main corrosion inhibitor segregates, does not degrade and or reduces the resistance to aqueous corrosion of the austenitic stainless steel material.

Precipitation and impact toughness of Nb–V stabilised 18Cr–2Mo ferritic stainless steel during isothermal aging

International Nuclear Information System (INIS)

Han, Jian; Li, Huijun; Barbaro, Frank; Jiang, Laizhu; Zhu, Zhixiong; Xu, Haigang; Ma, Li

2014-01-01

The effect of isothermal aging on precipitation behaviour and Charpy impact toughness of Nb–V stabilised 18Cr–2Mo ferritic stainless steel was investigated by means of Thermo-Calc prediction, scanning electron microscopy, transmission electron microscopy, X-ray diffraction and Charpy impact toughness testing. The results show that, niobium, vanadium carbides and nitrides, Fe 2 Nb (Laves phase) and Cr 23 C 6 formed after 2 h aging at 800 °C, and the equilibrium solvus temperature of Fe 2 Nb phase increases to above 750 °C, higher than the calculated temperature (730 °C) using Thermo-Calc. After isothermal aging at 750–950 °C, 2 h aging resulted in a decrease in toughness due to the formation of precipitation, especially (Nb,V)(C,N) and Fe 2 Nb. When isothermally aged at 800 °C for up to 24 h, the coarsening rate of Fe 2 Nb particle is much higher than that of (Nb,V)(C,N), and the impact toughness of the steel is dependent on quantity and sizes of (Nb,V)(C,N) and Fe 2 Nb particles

Precipitation and impact toughness of Nb–V stabilised 18Cr–2Mo ferritic stainless steel during isothermal aging

Energy Technology Data Exchange (ETDEWEB)

Han, Jian, E-mail: jh595@uowmail.edu.au [School of Mechanical, Materials and Mechatronic Engineering, University of Wollongong, Wollongong, NSW 2522 (Australia); Li, Huijun [School of Mechanical, Materials and Mechatronic Engineering, University of Wollongong, Wollongong, NSW 2522 (Australia); Barbaro, Frank [School of Mechanical, Materials and Mechatronic Engineering, University of Wollongong, Wollongong, NSW 2522 (Australia); CBMM Technology Suisse, 14, Rue du Rhone, Geneve 1204 (Switzerland); Jiang, Laizhu [Baoshan Iron and Steel Co., Ltd., Shanghai 200431 (China); Zhu, Zhixiong [School of Mechanical, Materials and Mechatronic Engineering, University of Wollongong, Wollongong, NSW 2522 (Australia); Xu, Haigang; Ma, Li [Baoshan Iron and Steel Co., Ltd., Shanghai 200431 (China)

2014-08-26

The effect of isothermal aging on precipitation behaviour and Charpy impact toughness of Nb–V stabilised 18Cr–2Mo ferritic stainless steel was investigated by means of Thermo-Calc prediction, scanning electron microscopy, transmission electron microscopy, X-ray diffraction and Charpy impact toughness testing. The results show that, niobium, vanadium carbides and nitrides, Fe{sub 2}Nb (Laves phase) and Cr{sub 23}C{sub 6} formed after 2 h aging at 800 °C, and the equilibrium solvus temperature of Fe{sub 2}Nb phase increases to above 750 °C, higher than the calculated temperature (730 °C) using Thermo-Calc. After isothermal aging at 750–950 °C, 2 h aging resulted in a decrease in toughness due to the formation of precipitation, especially (Nb,V)(C,N) and Fe{sub 2}Nb. When isothermally aged at 800 °C for up to 24 h, the coarsening rate of Fe{sub 2}Nb particle is much higher than that of (Nb,V)(C,N), and the impact toughness of the steel is dependent on quantity and sizes of (Nb,V)(C,N) and Fe{sub 2}Nb particles.

Parametrical limits of SCC-susceptibility of austenitic and austenitic-ferritic Cr-Ni steels

International Nuclear Information System (INIS)

Starosvetskij, D.I.; Baru, R.L.; Bondarenko, A.I.; Bogoyavlenskij, V.L.; Timonin, V.A.

1990-01-01

Comparative investigations into corrosion cracking (CC) of austenitic (12Kh18N10T) and austenitic-ferritic (08Kh22N6T) chromium-nickel steels are performed for various chloride media in a wide range of chloride concentrations and temperatures. It is shown that the ratio between steels in terms of their CC-susceptibility is not definite and can undergo a reversal depending on parameters of medium, level and conditions of loading. Differences in mechanisms of corrosion cracking of austenitic and austenitic-ferritic steels are established

Modeling of kinetics of isothermal idiomorphic ferrite formation in a medium carbon vanadium-titanium microalloyed steel

International Nuclear Information System (INIS)

Capdevila, C.; Caballer, E. G.; Garcia de Andres, C.

2002-01-01

A theoretical model is presented in this work to calculate the evolution of isothermal austenite-to-idiomorphic ferrite transformation in a medium carbon vanadium-titanium microalloyed steel. This model has been developed on the basis of the study of the nucleation and growth kinetics of idiomorphic ferrite, considering the influence of the nature, size and distribution of the inclusions, which are responsible of the intragranular nucleation of idiomorphic ferrite. Moreover, the influence of the austenite grain size on the isothermal decomposition of austenite in idiomorphic ferrite has been thoroughly analysed. An excellent agreement (85% in R''2) has been obtained between experimental and predicted values of volume fraction of idiomorphic ferrite. (Author) 32 refs

Precipitation and mechanical properties of Nb-modified ferritic stainless steel during isothermal aging

International Nuclear Information System (INIS)

Yan Haitao; Bi Hongyun; Li Xin; Xu Zhou

2009-01-01

The influence of isothermal aging on precipitation behavior and mechanical properties of Nb-modified ferritic stainless steel was investigated using Thermo-calc software, scanning electron microscopy and transmission electron microscopy. It was observed that TiN, NbC and Fe 2 Nb formed in the investigated steel and the experimental results agreed well with the results calculated by Thermo-calc software. During isothermal aging at 800 deg. C, the coarsening rate of Fe 2 Nb is greater than that of NbC, and the calculated average sizes of NbC and Fe 2 Nb of the aged specimen agreed with the experimental results. In addition, the tensile strength and micro-hardness of the ferritic stainless steel increased with increased aging time from 24 h to 48 h. But aging at 800 deg. C for 96 h caused the coarsening of the precipitation, which led to a decrease of tensile strength and micro-hardness

Low-temperature nitriding of austenitic steel in a vibrofluidized bed

Science.gov (United States)

Baraz, V. R.; Grachev, S. V.

1999-11-01

The prospects for use of a vibrofluidized bed (VFB) for low-temperature nitrogen saturation of high-strength austenitic steel based on Cr-Ni-Mn (12Kh17N8G2S2MF) are considered. The positive effect of preliminary plastic deformation on the intensity of nitriding is described. The temperature and time parameters of nitriding in a VFB for strain-aging austenitic steel 12Kh17N8G2S2MF are shown to be adequate for the regimes of the final heat-treatment operation of aging. This creates the possibility of combining the operations of surface alloying and strain aging into a single cycle. This combined treatment increases substantially the resistance of the steel to cyclic loads while preserving the strength parameters. It is shown that the presented method of low-temperature nitriding in a VFB is expedient for improving the service characteristics of austenitic steel 12Kh17N8G2S2MF used for production of force springs of automobile brake systems.

Formation and stabilization of reversed austenite in supermartensitic stainless steel

DEFF Research Database (Denmark)

Nießen, Frank; Grumsen, Flemming Bjerg; Hald, John

2017-01-01

of the reversed austenite phase fraction. Annealing at higher temperatures led to a gradual increase in hardness which was caused by formation of fresh martensite from reversed austenite. It was demonstrated that stabilization of reversed austenite is primarily based on chemical stabilization by partitioning......The formation and stabilization of reversed austenite upon inter-critical annealing was investigated in a X4CrNiMo16-5-1 (EN 1.4418) supermartensitic stainless steel by means of scanning electron microscopy, electron backscatter-diffraction, transmission electron microscopy, energy-dispersive X......-ray spectroscopy and dilatometry. The results were supported by thermodynamics and kinetics models, and hardness measurements. Isothermal annealing for 2 h in the temperature range of 475 to 650 °C led to gradual softening of the material which was related to tempering of martensite and the steady increase...

Static strain aging type AISI-304 austenitic stainless steel

International Nuclear Information System (INIS)

Trindade, M.B.

1981-03-01

Static strain aging of type AISI-304 austenitic stainless steel was studied from room temperature up to 623K by conducting tests in which the load was held approximately constant, continuously relaxing and unloaded. The aging times varied between 10s and 100h, using a plastic pre deformation of 9% in most of the cases. The static strain aging of 304 steel furnished an activation energy of 23,800 cal/mol. This implies that vacancies play an important role on the aging process. The curve of the variation of the discontinuous yielding with aging time presented different stages, to which specific mathematical expressions were developed. These facts permited the conclusion that Snoek type mechanisms are responsible for the aging in such conditions. (Author) [pt

Thermal fatigue of a 304L austenitic stainless steel: simulation of the initiation and of the propagation of the short cracks in isothermal and aniso-thermal fatigue

International Nuclear Information System (INIS)

Haddar, N.

2003-04-01

The elbow pipes of thermal plants cooling systems are submitted to thermal variations of short range and of variable frequency. These variations bound to temperature changes of the fluids present a risk of cracks and leakages. In order to solve this problem, EDF has started the 'CRECO RNE 808' plan: 'thermal fatigue of 304L austenitic stainless steels' to study experimentally on a volume part, the initiation and the beginning of the propagation of cracks in thermal fatigue on austenitic stainless steels. The aim of this study is more particularly to compare the behaviour and the damage of the material in mechanic-thermal fatigue (cycling in temperature and cycling in deformation) and in isothermal fatigue (the utmost conditions have been determined by EDF for the metal: Tmax = 165 degrees C and Tmin = 90 degrees C; the frequency of the thermal variations can reach a Hertz). A lot of experimental results are given. A model of lifetime is introduced and validated. (O.M.)

Stress distributions due to hydrogen concentrations in electrochemically charged and aged austenitic stainless steel

International Nuclear Information System (INIS)

Rozenak, P.; Loew, A.

2008-01-01

As a result of hydrogen concentration gradients in type austenitic stainless steels, formed during electrochemical charging and followed by hydrogen loss during aging, at room temperature, surface stresses were developed. These stresses were measured by X-ray technique and the crack formation thus induced could be studied using equilibrium stress equations. After various electrochemical charging and aging times, X-ray diffraction patterns obtained from samples indicated that the reflected and broadened diffraction peaks are the result of the formation of a non-uniform but continuous solid solution in the austenitic matrix. Since both hydrogen penetrations during charging and hydrogen release during aging are diffusion controlled processes and huge hydrogen concentration gradients in the thin surface layer, at depths comparable with the depth of X-ray penetration, are observed. The non-uniform hydrogen concentration in the austenitic matrix, results to the non-uniform expansion of the atomic microstructure and latter inevitably leads to the development of internal stresses. The internal stresses development formulae's are very similar to those relating to non-uniform heating of the materials, where thermal stresses appear due to non-uniform expansion or contraction. The relevant well developed theory is applicable in our case of non-uniform hydrogen concentrations in a solid solution of electrochemically charged and aged austenitic matrix. A few cracks were present on the surface after some minutes of electrochemical charging and the severity of cracking increased as hydrogen was lost during subsequent aging. This is consistent with the expectation of high compressive stresses in the bulk of the specimen during charging and high tensile surface stresses (at the level of 1 x 10 11 Pa) during the aging process. These stresses can induce the formation of surface cracks during the aging process after electrochemical charging in the AISI 316 stainless steel

X-Ray Diffraction Profile Analysis for Characterizing Isothermal Aging Behavior of M250 Grade Maraging Steel

Science.gov (United States)

Mahadevan, S.; Jayakumar, T.; Rao, B. P. C.; Kumar, Anish; Rajkumar, K. V.; Raj, Baldev

2008-08-01

X-ray diffraction (XRD) studies were carried out to characterize aging behavior of M250 grade maraging steel samples subjected to isothermal aging at 755 K for varying durations of 0.25, 1, 3, 10, 40, 70, and 100 hours. Earlier studies had shown typical features of precipitation hardening, wherein the hardness increased to a peak value due to precipitation of intermetallics and decreased upon further aging (overaging) due to reversion of martensite to austenite. Intermetallic precipitates, while coherent, are expected to increase the microstrain in the matrix. Hence, an attempt has been made in the present study to understand the microstructural changes in these samples using XRD line profile analysis. The anisotropic broadening with diffraction angle observed in the simple Williamson Hall (WH) plot has been addressed using the modified WH (mWH) approach, which takes into account the contrast caused by dislocations on line profiles, leading to new scaling factors in the WH plot. The normalized mean square strain and crystallite size estimated from mWH have been used to infer early precipitation and to characterize aging behavior. The normalized mean square strain has been used to determine the Avrami exponent in the Johnson Mehl Avrami (JMA) equation, which deals with the kinetics of precipitation. The Avrami exponent thus determined has matched well with values found by other methods, as reported in literature.

Interface segregation behavior in thermal aged austenitic precipitation strengthened stainless steel

Energy Technology Data Exchange (ETDEWEB)

Li, Hui [Key Laboratory for Microstructures, Shanghai University, Shanghai 200444 (China); Technical Department, Jiuli Hi-Tech Metals Co., Ltd., Huzhou 313008 (China); Song, Hui [Key Laboratory for Microstructures, Shanghai University, Shanghai 200444 (China); Liu, Wenqing, E-mail: wqliu@staff.shu.edu.cn [Key Laboratory for Microstructures, Shanghai University, Shanghai 200444 (China); Institute of Materials, Shanghai University, Shanghai 200072 (China); Xia, Shuang; Zhou, Bangxin [Institute of Materials, Shanghai University, Shanghai 200072 (China); Su, Cheng; Ding, Wenyan [Technical Department, Jiuli Hi-Tech Metals Co., Ltd., Huzhou 313008 (China)

2015-12-15

The segregation of various elements at grain boundaries, precipitate/matrix interfaces were analyzed using atom probe tomography in an austenitic precipitation strengthened stainless steel aged at 750 °C for different time. Segregation of P, B and C at all types of interfaces in all the specimens were observed. However, Si segregated at all types of interfaces only in the specimen aged for 16 h. Enrichment of Ti at grain boundaries was evident in the specimen aged for 16 h, while Ti did not segregate at other interfaces. Mo varied considerably among interface types, e.g. from segregated at grain boundaries in the specimens after all the aging time to never segregate at γ′/γ phase interfaces. Cr co-segregated with C at grain boundaries, although carbides still did not nucleate at grain boundaries yet. Despite segregation tendency variations in different interface types, the segregation tendency evolution variation of different elements depending aging time were analyzed among all types of interfaces. Based on the experimental results, the enrichment factors, Gibbs interface excess and segregation free energies of segregated elements were calculated and discussed. - Highlights: • Solute atoms segregated at interfaces were analyzed in an austenitic stainless steel. • The comparison of segregation in different interfaces was studied by APT. • The evolution of interface segregation during aging treatment was discussed.

Microstructure Evolution and Mechanical Behavior of a CMnSiAl TRIP Steel Subjected to Partial Austenitization Along with Quenching and Partitioning Treatment

Science.gov (United States)

Kong, H.; Chao, Q.; Cai, M. H.; Pavlina, E. J.; Rolfe, B.; Hodgson, P. D.; Beladi, H.

2018-02-01

The present study investigated the microstructure evolution and mechanical behavior in a low carbon CMnSiAl transformation-induced plasticity (TRIP) steel, which was subjected to a partial austenitization at 1183 K (910 °C) followed by one-step quenching and partitioning (Q&P) treatment at different isothermal holding temperatures of [533 K to 593 K (260 °C to 320 °C)]. This thermal treatment led to the formation of a multi-phase microstructure consisting of ferrite, tempered martensite, bainitic ferrite, fresh martensite, and retained austenite, offering a superior work-hardening behavior compared with the dual-phase microstructure (i.e., ferrite and martensite) formed after partial austenitization followed by water quenching. The carbon enrichment in retained austenite was related to not only the carbon partitioning during the isothermal holding process, but also the carbon enrichment during the partial austenitization and rapid cooling processes, which has broadened our knowledge of carbon partitioning mechanism in conventional Q&P process.

Effect of Prior Austenite Grain Size on the Morphology of Nano-Bainitic Steels

Science.gov (United States)

Singh, Kritika; Kumar, Avanish; Singh, Aparna

2018-04-01

The strength in nanostructured bainitic steels primarily arises from the fine platelets of bainitic ferrite embedded in carbon-enriched austenite. However, the toughness is dictated by the shape and volume fraction of the retained austenite. Therefore, the exact determination of processing-morphology relationships is necessary to design stronger and tougher bainite. In the current study, the morphology of bainitic ferrite in Fe-0.89C-1.59Si-1.65Mn-0.37Mo-1Co-0.56Al-0.19Cr (wt pct) bainitic steel has been investigated as a function of the prior austenite grain size (AGS). Specimens were austenitized at different temperatures ranging from 900 °C to 1150 °C followed by isothermal transformation at 300 °C. Detailed microstructural characterization has been carried out using scanning electron microscopy and X-ray diffraction. The results showed that the bainitic laths transformed in coarse austenite grains are finer resulting in higher hardness, whereas smaller austenite grains lead to the formation of thicker bainitic laths with a large fraction of blocky type retained austenite resulting in lower hardness.

Mechanical property degradation and microstructural evolution of cast austenitic stainless steels under short-term thermal aging

Science.gov (United States)

Lach, Timothy G.; Byun, Thak Sang; Leonard, Keith J.

2017-12-01

Mechanical testing and microstructural characterization were performed on short-term thermally aged cast austenitic stainless steels (CASS) to understand the severity and mechanisms of thermal-aging degradation experienced during extended operation of light water reactor (LWR) coolant systems. Four CASS materials-CF3, CF3M, CF8, and CF8M-were thermally aged for 1500 h at 290 °C, 330 °C, 360 °C, and 400 °C. All four alloys experienced insignificant change in strength and ductility properties but a significant reduction in absorbed impact energy. The primary microstructural and compositional changes during thermal aging were spinodal decomposition of the δ-ferrite into α/α‧, precipitation of G-phase in the δ-ferrite, segregation of solute to the austenite/ferrite interphase boundary, and growth of M23C6 carbides on the austenite/ferrite interphase boundary. These changes were shown to be highly dependent on chemical composition, particularly the concentration of C and Mo, and aging temperature. The low C, high Mo CF3M alloys experienced the most spinodal decomposition and G-phase precipitation coinciding the largest reduction in impact properties.

Corrosion behavior of austenitic steels and their components in niobium-containing chloride melts

Science.gov (United States)

Abramov, A. V.; Polovov, I. B.; Rebrin, O. I.; Volkovich, V. A.; Lisienko, D. G.

2014-02-01

The mechanism of corrosion of austenitic steels 12Kh18N10T, 10Kh17N13M2T, and 03Kh17N14M3 and metals Cr, Fe, Ni, and Mo in a NaCl-KCl-NbCl n ( n = 3.5, Nb content is 5 ± 0.1 wt %) melt at 750°C is studied. The metal and steel corrosion rates under these conditions are determined. The character of material fracture and the mechanisms of material corrosion are found.

An investigation on microstructure and mechanical propertiesof a Nb-microalloyed nano/ultrafine grained 201 austenitic stainless steel

Energy Technology Data Exchange (ETDEWEB)

Samaei Baghbadorani, H., E-mail: h.samaeibaghbadorani@ma.iut.ac.ir [Department of Materials Engineering, Isfahan University of Technology, 84156-83111 Isfahan (Iran, Islamic Republic of); Kermanpur, A. [Department of Materials Engineering, Isfahan University of Technology, 84156-83111 Isfahan (Iran, Islamic Republic of); Najafizadeh, A. [Department of Materials Engineering, Isfahan University of Technology, 84156-83111 Isfahan (Iran, Islamic Republic of); Fould Institute of Technology, Fouldshare 84916-63763 (Iran, Islamic Republic of); Behjati, P.; Rezaee, A.; Moallemi, M. [Department of Materials Engineering, Isfahan University of Technology, 84156-83111 Isfahan (Iran, Islamic Republic of)

2015-06-11

The present study was aimed to investigate the mechanical properties of a nano/ultrafine grained Nb-containing 201 austenitic stainless steel. For this purpose, 90% cold rolled sheets with fully martensitic microstructure were isothermally annealed at 900 °C for different times of 1 to 1800 s, leading to the reversion of strain- induced α′-martensite to austenite and significant grain refinement. Ferritescopy, X-ray diffractometery and optical/electron microscopy techniques along with hardness measurements and tensile tests were used to study the evolution in microstructure and mechanical properties in the course of annealing. It was found that heavy cold-rolling promoted formation of Nb-rich carbonitrides which effectively retarded the growth of fine reverted austenite grains. The obtained results showed that the complete transformation of martensite to austenite took about 60 s with the corresponding austenite grain size of about 90 nm. This sample had an ultrahigh yield strength of 1170 MPa, which was almost four times higher than that of the raw material and outstanding elongation of 37%. Further, the true stress–strain curves of the reversion annealed samples revealed two distinct uniform elongation stages (stage I and stage II), whereas, the onset of stage II was concurrent with pronounced strain hardening. This was related to the sharp increase in the formation of α′-martensite upon tensile straining.

Reverted austenite in PH 13-8 Mo maraging steels

International Nuclear Information System (INIS)

Schnitzer, Ronald; Radis, Rene; Noehrer, Matthias; Schober, Michael; Hochfellner, Rainer; Zinner, Silvia; Povoden-Karadeniz, E.; Kozeschnik, Ernst; Leitner, Harald

2010-01-01

The mechanical properties of maraging steels are strongly influenced by the presence of reverted austenite. In this study, the morphology and chemical composition of reverted austenite in a corrosion resistant maraging steel was characterized using transmission electron microscopy (TEM) and atom probe tomography (APT). Two types of austenite, i.e. granular and elongated, are present after aging at 575 o C, whereby the content of the latter increases during aging. The investigations revealed that the austenite phase is enriched in Ni, which prevents the transformation to martensite during cooling. Inside and next to the austenitc areas, Mo and Cr-rich carbides, which form during the aging treatment, were found. Various aging treatments were performed to obtain the activation energy for the formation of reverted austenite. Additionally, the experimental data are compared with thermodynamic and kinetic simulations. Based on these results and the chemical composition changes of the phases, a model for the formation of reverted austenite is presented. It is concluded that precipitation of B2-ordered NiAl and formation of reverted austenite take place simultaneously during aging and that dissolution of precipitates is not essential for the initial formation of reverted austenite.

The mechanical features of isothermally annealed duplex stainless steel

International Nuclear Information System (INIS)

Sustarsic, B.; Godec, M.; Jenko, M.; Tuma, J.V.; Marini, B.; Toffolon Masclet, C.; Forget, P.

2011-01-01

Cast duplex stainless steels are frequently used for structural parts of nuclear power plants and other thermo-energetic objects. The ageing behaviour of the cast 258 type stainless steel has been studied in the frame of IMT Slovenia and CEA bilateral cooperation. The results of testing of French and Sloven partners are compared and analysed. The steel samples have been isothermally annealed for 10.000 and 30.000 hours at 300 and 350 C. ICP-AES bulk chemical analysis of samples, microstructure investigations with light (LM) and scanning electron microscope (SEM), micro-chemical analysis with SEM/EDS, as well as SEM/EBSD phase analyses have been performed. Tensile test specimens have been made from the aged samples and standard tensile test at room temperature was performed. The SEM fractography of fractured surfaces was also performed. Microhardness measurements of ferrite and austenite phase were determined on polished metallographic samples. The results of mechanical testing and fractographic examinations are reported and discussed in this paper. Microhardness of ferrite is drastically increased with time and temperature of ageing due to spinodal decomposition. But, hardness of austenite remains practically unchanged. Tensile properties changed, similarly. Yield point and tensile strength increased but ductility significantly decreased. In accordance with ductility decrease the nature of fractured surface changed from typical ductile to brittle and dimpled to cleavage, respectively. (authors)

Effects of Aging and W Addition on the Microstructure of Fe-Cr-Mn-N Stainless Steels

International Nuclear Information System (INIS)

Jeon, Yu Taek; Joo, Uk Hyon; Park, Yong Soo; Kim, Young Sik

2000-01-01

The effects of aging treatment on the precipitation behaviors of Fe-Cr-Mn-N stainless steels were studied using a transmission electron microscopy, scanning electron microscopy, optical microscopy and XRD. In the austenitic stainless steel having a single phase. M23C6 carbides were first precipitated in the grain boundary by aging and then grew from grain boundary into grain with aging time. Carbides showed lamellar structures. It was shown from the analysis of spot patterns that carbides had a coherent relation with matrix and their lattice parameter was roughly three times that of austenite. During initial stages of M23C6 carbide precipitation, the iron content was quite high. With increasing aging time, the chromium content was increased. As the tungsten was added to improve the corrosion resistance of the Fe-Cr-Mn-N stainless steels, ferrite phase was formed. This ferrite phase was decomposed to chi(χ) phase and secondary austenite. Chi phase was mainly enriched with tungsten, chromium and tungsten were depleted in the secondary austenite due to the formation of chi phase. M23C6 carbides were also formed in the grain boundary. Nickel stabilized the austenite phase and decreased the ferrite volume fraction. But nickel content was not sufficient to suppress the formation of ferrite, and precipitation behaviors were not changed

Solubility of niobium in austenite in the presence of Nb(C,N)

International Nuclear Information System (INIS)

Mei, P.R.; Bresciani Filho, E.

1983-01-01

It was developed some equations to calculate the solubility of niobium in austenite in the presence of NbC sub(0.87) or NbN. These equations were applied to steels with carbon, nitrogen and niobium content varying from 10 -3 to 1 wt %, and for 800-1300 0 C temperature range. The results obtained were compared with experimental data from literature, and showed a good agreement. Using those equations, it was developed an algorithm to calculate the solubility of niobium in austenite in the presence of niobium carbonitride (NbC sub(x) N sub(y)). The results obtained by this method were compared with experimental data, and also showed a good agreement. (Author) [pt

Characterization of the austenitic stability of metastable austenitic stainless steel with regard to its formability

Science.gov (United States)

Schneider, Matthias; Liewald, Mathias

2018-05-01

During the last decade, the stainless steel market showed a growing volume of 3-5% p.a.. The austenitic grades are losing market shares to ferritic or 200-series grades due to the high nickel price, but still playing the most important role within the stainless steel market. Austenitic stainless steel is characterized by the strain-induced martensite formation, causing the TRIP-effect (Transformation Induced Plasticity) which is responsible for good formability and high strength. The TRIP-effect itself is highly dependent on the forming temperature, the strain as well as the chemical composition which has a direct influence on the stability of the austenite. Today the austenitic stability is usually characterized by the so called Md30-temperature, which was introduced by Angel and enhanced by several researches, particularly Nohara. It is an empirical formula based on the chemical composition and the grain size of a given material, calculating the temperature which is necessary to gain a 50 % martensite formation after 30 % of elongation in a tensile test. A higher Md30-temperature indicates a lower stability and therefore a higher tendency towards martensite formation. The main disadvantage of Md30 -temperature is the fact that it is not based on forming parameters and only describes a single point instead of the whole forming process. In this paper, an experimental set up for measuring martensite and temperature evolution in a non-isothermal tensile test is presented, which is based on works of Hänsel and Schmid. With this set up, the martensite formation rate for different steels of the steel grade EN 1.4301 and EN 1.4310 is measured. Based on these results a new austenitic stability criterion is defined. This criterion and the determined Md30-temperatures are related to the stretch formability of the materials. The results show that the new IFU criterion is with regard to the formability a much more useful characteristic number for metastable austenitic steels

Corrosion behavior of austenitic stainless steel containing Ti

International Nuclear Information System (INIS)

Cha, Sueng Ok; Choe, Han Cheol; Kim, Kwan Hyu

1998-01-01

Corrosion behavior of austenitic stainless steel containing Ti has been studied by using electrochemical techniques. The samples containing Ti from 0.1 to 1.0 wt% were solutionized at 1050 .deg. C for 1hr and then sensitized at 650 .deg. C for 5hr under argon atmosphere. Microstructure and phase analysis of the samples after heat treatment and corrosion tests were carried out by using XRD. TEM, SEM and optical microscope. The amount of δ-ferrite and TiC precipitates in matrix increased as the Ti content increased. In the sensitized samples, Cr 23 C 6 precipitates were observed at γ/δ interface. Degree Of Sensitization(DOS) was lower than 1.0 in all of the solutionized samples and the sensitized samples of Ti content above 0.4% wt% whereas the sensitized samples of Ti content lower than 0.4 wt% showed DOS higher than 1.0. Intergranular attack appeared mainly at grain boundaries in the sensitized sample containing 0.1 wt% Ti and at the γ/δ interface of the higher Ti content. In the latter, however, the attack was not so severe. Pitting potential(E pit ) and repassivation potential(E rep ) of the solutionized and sensitized samples were increased with increasing Ti content. The number and size of the pits decreased with increasing Ti content in the sensitized samples. The pits nucleated at Cr 23 C 6 site and the γ/δ interface

The Formation of Martensitic Austenite During Nitridation of Martensitic and Duplex Stainless Steels

Science.gov (United States)

Zangiabadi, Amirali; Dalton, John C.; Wang, Danqi; Ernst, Frank; Heuer, Arthur H.

2017-01-01

Isothermal martensite/ferrite-to-austenite phase transformations have been observed after low-temperature nitridation in the martensite and δ-ferrite phases in 15-5 PH (precipitation hardening), 17-7 PH, and 2205 (duplex) stainless steels. These transformations, in the region with nitrogen concentrations of 8 to 16 at. pct, are consistent with the notion that nitrogen is a strong austenite stabilizer and substitutional diffusion is effectively frozen at the paraequilibrium temperatures of our experiments. Our microstructural and diffraction analyses provide conclusive evidence for the martensitic nature of these phase transformations.

Crystallography of sigma phase precipitation in superaustenitic Fe-22Cr-21Ni-6Mo-0.3N stainless steels

International Nuclear Information System (INIS)

Lee, Tae Ho; Jung, Yun Chul; Kim, Sung Joon

1999-01-01

The crystallographic features of sigma phase precipitation in super austenitic Fe-22Cr-21Ni-6Mo-(0.3N) stainless steels during isothermal aging were investigated utilizing transmission electron microscopy. The sigma phase precipitated along the austenite grain boundaries even after solution treatment due to higher Mo contents and remained stable throughout aging at 900 .deg. C up to 168 hours. The sigma phase observed in this study was found to be ternary Fe-Cr-Mo sigma phase and had tetragonal structure with lattice parameters of a=9.17A and c=4.74A. The orientation relationships between the sigma phase and austenite were determined from the analyses of selected area diffraction patterns taken by various zone axes and stereo graphic analyses. The orientation relationships between sigma and austenite phases obtained in this study were as follows; 1) (110) γ ll (110) σ , [111] γ ll [001] σ and (112) γ ll (110) σ , [111] γ ll [001] σ and 2) (110) γ ll (110) σ , [112] γ ll [113] σ and (111) γ ll (332) σ , [112] γ ll [113] σ . However, the former orientation relationship was predominant throughout aging and the latter orientation relationship was scarcely observed in very limited aging condition

Analysis of the non-isothermal austenite-martensite transformation in 13% Cr-type martensitic stainless steels

International Nuclear Information System (INIS)

Garcia-De-Andris, C.; Alvarez, L.F.

1996-01-01

In martensitic stainless steels, as in other alloyed containing carbide-forming elements, the carbide dissolution and precipitation processes that take place during heat treatment can cause modifications to the chemical composition of the austenite phase of these steels. The chemical composition of this phase is a fundamental factor for the evolution of the martensitic transformation. As a result of their influence on the dissolution and precipitation processes, the parameters of the quenching heat treatment exert a strong influence on the behavior of the martensitic transformation in these steels. In the present study, the effect of the heating temperature and the cooling rate on the martensitic transformation in two 13% Cr-type martensitic stainless steels with different carbon contents were properly evaluated. (author)

The CCT diagram of the austenite transformations of the 45 steel during isothermal cooling. Dilatometric and microscopic analysis

International Nuclear Information System (INIS)

Wierszyllowski, I.; Wieczorek, S.

2003-01-01

The CCT diagram of the austenite transformations of the 45 steel during isochronal cooling makes possible to develop equations that enables prediction of structure and properties after conventional heat treatment. Dilatometric method was applied in order to work out such diagram for 45 steel austenitized at 1050 o C. Structures appeared during applied cooling rates were presented. Shapes of dilatometric diagrams described austenite transformations and microstructures are mutually related. During austenite to ferrite transformations separation for equiaxial and coniferous ferrite was possible. The border cooling rate at which coniferous ferrite starts to precipitate was determined as well as M s and M f temperatures. Shape of CCT diagram developed with use of isochronal cooling is different from conventional one. Obtained results were discussed on the literature basis. (author)

Thermal aging evaluation of cast austenitic stainless steel pipe

International Nuclear Information System (INIS)

Song, T. H.; Jung, I. S.

2002-01-01

24 years have been passed since Kori Unit 1 began its commercial operation, and 19 years have been passed since Kori Unit 2 began its commercial operation. As the end point of design life become closer, plant life extension and periodic safety assessment is paid more and more attention to by utility company. In this paper, the methodologies and results of cast austenitic stainless steel pipe thermal aging evaluations of both units have been presented in association with aging time of 10, 20, and 30 years and operating temperature, respectively. Life extension cases respectively. As a result of this, at the operating temperature of 280 .deg. C, thermal aging was not a problem as long as Charpy V-notch room temperature minimum impact energy is concerned. However, more than 300 .deg. C and 30 years of operating condition, we should perform detailed fracture mechanics analysis with CMTR of NPP pipe

Expanded austenite in nitrided layers deposited on austenitic and super austenitic stainless steel grades; Analise da austenita expandida em camadas nitretadas em acos inoxidaveis austeniticos e superaustenitico

Energy Technology Data Exchange (ETDEWEB)

Casteletti, L.C.; Fernandes, F.A.P.; Heck, S.C. [Universidade de Sao Paulo (EESC/USP), Sao Carlos, SP (Brazil). Escola de Engenharia. Dept. de Engenharia de Materais, Aeronautica e Automobilistica; Oliveira, A.M. [Instituto de Educacao, Ciencia e Tecnologia do Maranhao (IFMA), Sao Luis, MA (Brazil); Gallego, J., E-mail: gallego@dem.feis.unesp.b [UNESP, Ilha Solteira, SP (Brazil). Dept. Engenharia Mecanica

2010-07-01

In this work nitrided layers deposited on austenitic and super austenitic stainless steels were analyzed through optical microscopy and X-rays diffraction analysis (XRD). It was observed that the formation of N supersaturated phase, called expanded austenite, has promoted significant increment of hardness (> 1000HV). XRD results have indicated the anomalous displacement of the diffracted peaks, in comparison with the normal austenite. This behavior, combined with peaks broadening, it was analyzed in different nitriding temperatures which results showed good agreement with the literature. (author)

Oscillations of non-isothermal N/S boundary with a high frequency and large amplitude

International Nuclear Information System (INIS)

Bezuglyj, A.I.; Shklovskij, V.A.

2016-01-01

Within the framework of the phenomenological approach based on the heat balance equation and the dependence of the critical temperature of the superconductor on the current value theoretically investigated the impact of high-frequency current of high amplitude and arbitrary shape on the non-isothermal balance of the oscillating N/S interface in a long superconductor. We introduce a self-consistent average temperature field of rapidly oscillating non-isothermal N/S boundary (heat kink), which allows to go beyond the well-known concept of mean-square heating and consider the impact of current waveform. With regard to experiments on the effects of microwave high-power radiation on the current-voltage characteristics (CVC) of superconducting films, we give the classification of the families of the CVC for inhomogeneous superconductors which carry a current containing a high frequency component of large amplitude. Several characteristics have hysteresis of thermal nature.

Precipitation behavior of the lower bainitic carbide in a medium-carbon steel containing Si, Mn and Mo

International Nuclear Information System (INIS)

Liu, J.; Luo, C.P.

2006-01-01

The fine microstructure, crystallographic features and ε-carbides precipitation behavior of lower bainite produced by isothermal transformation in a medium-carbon steel containing Si, Mn and Mo were investigated using transmission electronic microscopy. It was found that the microstructure produced by isothermal reaction at 320 deg. C was composed of a large amount of plate-like lower bainite with retained austenite embedded between the plates, and ε-carbides precipitated within them. Midrib and subunits were readily visible in the lower bainite plate. The bainite plate kept a G-T orientation relationship (OR) with the austenite. Selected area electron diffraction patterns of 'three phases in four variants' and analysis indicated that two variants of ε-carbides precipitated in a single bainitic ferrite plate. The two (or three) variants of ε-carbides can simultaneously keep a Jack OR with its 'bainite matrix', while keeping no fixed OR with the austenite. The crystallographic features of ε-carbides precipitated within the bainite were the same as those observed in tempered martensite. The results indicated that the bainitic transformation bore an analogy to the martensitic one in carbide precipitation

Effects of Ion-Nitriding on the Pitting Behavior of Austenitic Stainless Steels Containing Mo

International Nuclear Information System (INIS)

Cho, Yong Seok; Choe, Han Cheol; Kim, Kwan Hyu

1994-01-01

Austenitic stainless steels(ASS) containing 1-4wt% Mo were ion-nitrided at 550 .deg. C for 20hrs and 30hrs, and their pitting behavior was examined by the electrochemical measurements. The formation of multiphase surface layers composed of the ε-{(Fe, Cr) 2- 3N} and the γ'-{(Fe, Cr) 4 N} phases was observed after ion-nitriding. The compound layers were approximately 50 μm thick after nitriding for 20hrs and 70 μm thick after 30hrs. Anodic polarization curves indicated that passive current density(I p ) and critical current density(I c ) increased, and corrosion potential(E corr ) decreased as a results of ion-nitriding. As the Mo content in the ion-nitrided ASS increased, passivation breakdown potential(E b ) and repassivation potential(E r ) increased, whereas I c and I p decreased. The pit nucleation time of the ASS nitrided for 20hrs was 10 minutes, while that of the 30hr nitrided samples was 3 minutes. The nucleation and growth of pits were significantly increased with the decreasing of Mo content as well as the increasing of ion-nitriding time

Peculiarities of austenitic state in premartensitic temperature range

International Nuclear Information System (INIS)

Sarrak, V.I.; Suvorova, S.O.

1982-01-01

A review of works on the study of austenite behaviour in premartensitic temperature range carried out using the investigation methods of resistance to microplastic deformation, mechanical properties and internal friction, is presented. The investigation is carried out using carbon-free iron-nickel alloy N31, alloy 40N24 and alloy 50Kh20N10. It is established that in premartensitic temperature range at a certain temperature Msub(elast.) exceeding by approximately 35 deg C the starting temperature of martensitic transformation, austenite state changes sharply: mechanical instability as to microplastic deformation appears. It manifests itself in an anomalous decrease of resistance to microplastic deformation at the temperature approaching the beginning of martensitic transformation. Martensitic transformation develops under tension in an elastic region. At the temperature above Msub(elast.) martensitic transformation develops only under the effect of plastic deformation. Decrease of temperature of martensitic transformation start as a result of microplastic deformation and subsequent ageing is connected with blocking of possible places of martensite initiation

Peculiarities of austenitic state in premartensitic temperature range

Energy Technology Data Exchange (ETDEWEB)

Sarrak, V.I.; Suvorova, S.O.

A review of works on the study of austenite behaviour in premartensitic temperature range carried out using the investigation methods of resistance to microplastic deformation, mechanical properties and internal friction, is presented. The investigation is carried out using carbon-free iron-nickel alloy N31, alloy 40N24 and alloy 50Kh20N10. It is established that in premartensitic temperature range at a certain temperature Msub(elast.) exceeding by approximately 35 deg C the starting temperature of martensitic transformation austenite state changes sharply: mechanical instability as to microplastic deformation appears. It manifests itself in an anomalous decrease of resistance to microplastic deformation at the temperature approaching the beginning of martensitic transformation. Martensitic transformation develops under tension in an elastic region. At the temperature above Msub(elast.) martensitic transformation develops only under the effect of plastic deformation. Decrease of temperature of martensitic transformation start as a result of microplastic deformation and subsequent ageing is connected with blocking of possible places of martensite initiation.

Identification of Precipitates in Cr-Mn-N Based Steel After Thermal Exposures

Directory of Open Access Journals (Sweden)

Ondruška Michal

2014-06-01

Full Text Available The paper deals with the identification of precipitates in the Cr-Mn-N steels after thermal exposure. The purpose of the study is to clarify the M2N precipitation by isothermal annealing at the temperatures of 750 and 900 °C with a holding time of 5, 10, 30 min, 1 hr. and 10 hrs. Microstructure of austenitic steel was characterised by the typical presence of annealing twins. Stepwise etching was observed at the holding time of 5 and 10 minutes, but at the holding time of 30 minutes, secondary particles were precipitated at the grain boundaries. Corrosion tests revealed that holding time significantly affected steel structure. M2N is the dominant precipitate, but the occurrence of σ-phase was occasionally observed especially at the interface of discontinuous precipitation and austenitic matrix. Slight increase of hardness at the grain boundaries was caused due to the precipitation of secondary phases during isothermal holding. The maximum hardness of 294 HV was measured on the sample isothermally annealed at 750 °C and holding for 10 hrs. The research provides theoretical basis for the heat affecting of steels, such as, for example, in welding.

Effect of silicon on the structure, tribological behaviour, and mechanical properties of nitrogen-containing chromium-manganese austenitic steels

International Nuclear Information System (INIS)

Korshunov, L.G.; Chernenko, N.L.; Gojkhenberg, Yu.N.

2003-01-01

The effect of silicon in quantity of 3.5-4.5 mass. % on tribological behaviour is studied for nitrogen-bearing (0.20-0.52 mass. % of nitrogen) chromium-manganese austenitic steels (10Kh15G23S4A0.20, 10Kh16G17N3S4A0.30, 10Kh19G20NS4A0.50, 12Kh19G19NS2A0.50, 10Kh18G19A0.50, 08Kh16G8N10S4A0.18). Mechanical properties and corrosion resistance of the steels are determined. Using metallographic, x-ray diffraction and electron microscopical methods a study is made into structural transformations running in the steels considered under friction and static tension. It is shown that additional silicon alloying of nitrogen-bearing chromium-manganese austenitic steels results in an essential increase of adhesion wear resistance of the materials on retention of low friction coefficient (f=0.25-0.33). A strong silicon effect on steel tribological behaviour is related with planar slip activation and with an increase of austenite strength and heat resistance [ru

Topological characterization of static strain aging of type AISI 304 austenitic stainless steel

International Nuclear Information System (INIS)

Monteiro, S.N.; Miranda, P.E.V. de

1981-01-01

Static strain aging of type AISI 304 austenitic stainless steel was studied from room temperature up to 623K by conducting tests in which the load was held approximately constant. The aging times varied between 10s and 100h, using a plastic pre-deformation of 9%. The static strain aging of 304 steel furnished an activation energy of 23.800 cal/mol. This implies that vacancies play an important role on the aging process. The curve of the variation of the discontinuous yielding with aging time presented different stages, to which specific mathematical expressions were developed. These facts permited the conclusion that Snock type mechanisms are responsible for the aging in such conditions. (Author) [pt

Synergy between molybdenum and nitrogen on the pitting corrosion and passive film resistance of austenitic stainless steels as a pH-dependent effect

Energy Technology Data Exchange (ETDEWEB)

Loable, Carole, E-mail: carole.loable@lepmi.grenoble-inp.fr [Univ. Grenoble Alpes, LEPMI, F-38000 Grenoble (France); CNRS, LEPMI, F-38000 Grenoble (France); Dep. Eng. Quimica, Instituto Superior Técnico-Universidade de Lisboa, Av. Rovisco Pais, 1049 001 Lisbon (Portugal); Viçosa, Isadora N., E-mail: inogueira@poli.ufrj.br [Univ. Grenoble Alpes, LEPMI, F-38000 Grenoble (France); CNRS, LEPMI, F-38000 Grenoble (France); Mesquita, Thiago J., E-mail: Thiago.mesquita@total.com [CRU Ugitech, Avenue Paul Girod, 73403 Ugine Cedex (France); Mantel, Marc, E-mail: Marc.Mantel@ugitech.com [CRU Ugitech, Avenue Paul Girod, 73403 Ugine Cedex (France); Université Grenoble Alpes, SIMAP, F-38000 Grenoble (France); CNRS, SIMAP, F-38000 Grenoble (France); Nogueira, Ricardo P., E-mail: rnogueira@pi.ac.ae [Univ. Grenoble Alpes, LEPMI, F-38000 Grenoble (France); CNRS, LEPMI, F-38000 Grenoble (France); Department of Chemical Engineering, The Petroleum Institute, P.O. Box 2533, Abu Dhabi (United Arab Emirates); Berthomé, Gregory, E-mail: gregory.berthome@simap.grenoble-inp.fr [Université Grenoble Alpes, SIMAP, F-38000 Grenoble (France); CNRS, SIMAP, F-38000 Grenoble (France); Chauveau, Eric, E-mail: eric.chauveau@ugitech.fr [Department of Chemical Engineering, The Petroleum Institute, P.O. Box 2533, Abu Dhabi (United Arab Emirates); Roche, Virginie, E-mail: virginie.roche@lepmi.grenoble-inp.fr [Univ. Grenoble Alpes, LEPMI, F-38000 Grenoble (France); CNRS, LEPMI, F-38000 Grenoble (France)

2017-01-15

This paper brings up some insights upon the pH dependence of the synergistic effect of Mo and N on the localized corrosion resistance of austenitic stainless steels. The objective of this work is to study the synergetic effect of Mo and N additions on corrosion and passive film properties of austenitic grades. A comparison between Mo containing (3 wt% Mo); Mo and N containing (3 wt% Mo and 0.1% N) and free Mo or free Mo and N grades of highly controlled laboratory heats was done considering their localized corrosion resistance and oxide film formation in different aggressive conditions, from neutral to alkaline pH. The passive layer was characterized by EIS and XPS analyses. The combined effect of Mo and N on the pitting potential was confirmed to be synergistic, and not just the addition of their individual effects. Moreover, this effect was found to be pH-dependent, being very positive in acid to neutral conditions whereas it was almost inexistent in high pH. - Highlights: • Laboratory austenitic stainless steels with Mo and/or N were tested. • Mo and N acted synergistically to improve pitting resistance. • Synergistic effect is pH-dependent. • N clearly enhanced the repassivation of austenitic SS in presence of Mo.

Synergy between molybdenum and nitrogen on the pitting corrosion and passive film resistance of austenitic stainless steels as a pH-dependent effect

International Nuclear Information System (INIS)

Loable, Carole; Viçosa, Isadora N.; Mesquita, Thiago J.; Mantel, Marc; Nogueira, Ricardo P.; Berthomé, Gregory; Chauveau, Eric; Roche, Virginie

2017-01-01

This paper brings up some insights upon the pH dependence of the synergistic effect of Mo and N on the localized corrosion resistance of austenitic stainless steels. The objective of this work is to study the synergetic effect of Mo and N additions on corrosion and passive film properties of austenitic grades. A comparison between Mo containing (3 wt% Mo); Mo and N containing (3 wt% Mo and 0.1% N) and free Mo or free Mo and N grades of highly controlled laboratory heats was done considering their localized corrosion resistance and oxide film formation in different aggressive conditions, from neutral to alkaline pH. The passive layer was characterized by EIS and XPS analyses. The combined effect of Mo and N on the pitting potential was confirmed to be synergistic, and not just the addition of their individual effects. Moreover, this effect was found to be pH-dependent, being very positive in acid to neutral conditions whereas it was almost inexistent in high pH. - Highlights: • Laboratory austenitic stainless steels with Mo and/or N were tested. • Mo and N acted synergistically to improve pitting resistance. • Synergistic effect is pH-dependent. • N clearly enhanced the repassivation of austenitic SS in presence of Mo.

Numerical simulation of Cr2N age-precipitation in high nitrogen stainless steels

International Nuclear Information System (INIS)

Dai, Q.X.; Yuan, Z.Z.; Luo, X.M.; Cheng, X.N.

2004-01-01

At the temperature raging from 700 to 950 deg. C, the Cr 2 N age-precipitation in high nitrogen austenitic stainless steels Fe24Mn18Cr3Ni0.62N was investigated in this paper. A qualitative mathematical model of Cr 2 N age-precipitation, ln t S = f (Me,1/T), was established based on the thermodynamics and kinetics and phase transformation theories. Satisfactory results were obtained by means of the test of artificial neural network. This mathematical model can be applied to the calculation design and predication of Cr 2 N age-precipitation in high nitrogen stainless steels

Effect of deformation temperature on niobium clustering, precipitation and austenite recrystallisation in a Nb–Ti microalloyed steel

International Nuclear Information System (INIS)

Kostryzhev, Andrii G.; Al Shahrani, Abdullah; Zhu, Chen; Ringer, Simon P.; Pereloma, Elena V.

2013-01-01

The effect of deformation temperature on Nb solute clustering, precipitation and the kinetics of austenite recrystallisation were studied in a steel containing 0.081C–0.021Ti–0.064 Nb (wt%). Thermo-mechanical processing was carried out using a Gleeble 3500 simulator. The austenite microstructure was studied using a combination of optical microscopy, transmission electron microscopy, and atom probe microscopy, enabling a careful characterisation of grain size, as well as Nb-rich clustering and precipitation processes. A correlation between the austenite recrystallisation kinetics and the chemistry, size and number density of Nb-rich solute atom clusters, and NbTi(C,N) precipitates was established via the austenite deformation temperature. Specifically, we have determined thresholds for the onset of recrystallisation: for deformation levels above 75% and temperatures above 825 °C, Nb atom clusters <8 nm effectively suppressed austenite recrystallisation

Thermal fatigue of a 304L austenitic stainless steel: simulation of the initiation and of the propagation of the short cracks in isothermal and aniso-thermal fatigue; Fatigue thermique d'un acier inoxydable austenitique 304L: simulation de l'amorcage et de la croissance des fissures courtes en fatigue isotherme et anisotherme

Energy Technology Data Exchange (ETDEWEB)

Haddar, N

2003-04-01

The elbow pipes of thermal plants cooling systems are submitted to thermal variations of short range and of variable frequency. These variations bound to temperature changes of the fluids present a risk of cracks and leakages. In order to solve this problem, EDF has started the 'CRECO RNE 808' plan: 'thermal fatigue of 304L austenitic stainless steels' to study experimentally on a volume part, the initiation and the beginning of the propagation of cracks in thermal fatigue on austenitic stainless steels. The aim of this study is more particularly to compare the behaviour and the damage of the material in mechanic-thermal fatigue (cycling in temperature and cycling in deformation) and in isothermal fatigue (the utmost conditions have been determined by EDF for the metal: Tmax = 165 degrees C and Tmin = 90 degrees C; the frequency of the thermal variations can reach a Hertz). A lot of experimental results are given. A model of lifetime is introduced and validated. (O.M.)

Carbide precipitation kinetics in austenite of a Nb-Ti-V microalloyed steel

International Nuclear Information System (INIS)

Jung, Jae-Gil; Park, June-Soo; Kim, Jiyoung; Lee, Young-Kook

2011-01-01

Highlights: → Carbide precipitation kinetic was fastest at 950 deg. C and accelerated by strain. → Nucleation sites for (Nb,Ti)C above 950 deg. C were mainly undissolved (Ti,Nb)(C,N). → Strain enabled (Nb,Ti)C to nucleate on all sides of (Ti,Nb)(C,N) above 950 deg. C. → Strain changed nucleation sites from (Ti,Nb)(C,N) to dislocations below 900 deg. C. → Strain also accelerated the change in particle composition to equilibrium one. - Abstract: The isothermal precipitation kinetics of carbides in both strain-free and strained austenite (γ) of a microalloyed steel were quantitatively investigated through the electrical resistivity and transmission electron microscopy. The (Nb,Ti)C carbides at the interfaces of the undissolved (Ti,Nb)(C,N) carbonitrides were observed at all temperatures in strain-free γ. However, for strain-induced precipitation, above 950 deg. C, the precipitation of (Nb,Ti)C carbides near the undissolved (Ti,Nb)(C,N) carbonitrides was predominant due to the recrystallization of strained γ. Meanwhile, the fine (Nb,Ti,V)C carbides were homogeneously precipitated in non-recrystallized γ at 850 deg. C and 900 deg. C, as well as near the undissolved (Ti,Nb)(C,N) particles. The electrical resistivity method was successfully used to quantitatively measure the isothermal precipitation kinetics of carbides in both strain-free and strained γ. The precipitation-time-temperature diagrams of the carbide in strain-free and strained γ, with nose temperatures of 950 deg. C, were generated and the precipitation kinetics were greatly accelerated by the applied strain.

Development of a kinetic model for bainitic isothermal transformation in transformation-induced plasticity steels

International Nuclear Information System (INIS)

Li, S.; Zhu, R.; Karaman, I.; Arróyave, R.

2013-01-01

In this work, we modify existing models to simulate the kinetics of bainitic transformation during the bainitic isothermal transformation (BIT) stage of a typical two-stage heat treatment – BIT is preceded by an intercritical annealing treatment – for TRIP steels. This effort is motivated by experiments performed in a conventional TRIP steel alloy (Fe–0.32C–1.42Mn–1.56Si) that suggest that thermodynamics alone are not sufficient to predict the amount of retained austenite after BIT. The model implemented in this work considers the non-homogeneous distribution of carbon – resulting from finite carbon diffusion rates – within the retained austenite during bainitic transformation. This non-homogeneous distribution is responsible for average austenite carbon enrichments beyond the so-called T 0 line, the temperature at which the chemical driving force for the bainitic transformation is exhausted. In order to attain good agreement with experiments, the existence of carbon-rich austenite films adjacent to bainitic ferrite plates is posited. The presence of this austenite film is motivated by earlier experimental work published by other groups in the past decade. The model is compared with experimental results and good qualitative agreement is found

On Microstructure and Microhardness of Isothermally Aged UNS S32760 and the Effect on Toughness and Corrosion Behavior

Science.gov (United States)

Elsabbagh, Fady M.; Hamouda, Rawia M.; Taha, Mohamed A.

2014-01-01

This paper investigates the microstructure and secondary phase precipitations obtained in UNS S32760 super duplex stainless steel and their effect on impact toughness and corrosion resistance. The heat treatment included first solution annealing at 1150 °C followed by water quenching, then isothermal heating at different temperatures from 350 to 950 °C for different times, ranging from less than 1 min to 600 min, followed by water quenching again. Microscopic investigation, microhardness tests, and x-ray diffraction (XRD) analysis were used to identify the microstructure and secondary phase precipitations formed by heat treatment. The study indicates a fair correlation between the microscopic observations and microhardness results, while XRD analysis defined the phase's chemistry and confirmed the microscopic and hardness results. In addition to the austenite (γ) and ferrite (α) phases of the duplex structure, secondary phases of (σ, χ, and chromium nitrides) are observed at a high temperature range, while (ά) and (aged ά) are observed at a lower temperature range. It is concluded that the microhardness test can be used to identify the phases appearing in the microstructure, which results in fair prediction for the TTT diagram and σ-phase range. The variation of toughness and corrosion resistance by heat treatment differs depending on the secondary phase formation.

Localized corrosion and stress corrosion cracking behavior of austenitic stainless steel weldments containing retained ferrite. Annual progress report, June 1, 1978--March 31, 1979

International Nuclear Information System (INIS)

Savage, W.F.; Duquette, D.J.

1979-03-01

Localized corrosion and stress corrosion cracking experiments have been performed on single phase 304 stainless steel alloys and autogeneous weldments containing retained delta ferrite as a second phase. The results of the pitting experiments show that the pressure of delta ferrite decreases localized corrosion resistance with pits initiating preferentially at delta ferrite--gamma austenite interphase boundaries. This increased susceptibility is reversible with elevated temperature heat treatments which revert the metastable ferrite phase to the equilibrium austenite phase

The low-temperature aging embrittlement in a 2205 duplex stainless steel

International Nuclear Information System (INIS)

Weng, K.L.; Chen, H.R.; Yang, J.R.

2004-01-01

The effect of isothermal treatment (at temperatures ranging between 400 and 500 deg. C) on the embrittlement of a 2205 duplex stainless steel (with 45 ferrite-55 austenite, vol.%) has been investigated. The impact toughness and hardness of the aged specimens were measured, while the corresponding fractography was studied. The results show that the steel is susceptible to severe embrittlement when exposed at 475 deg. C; this aging embrittlement is analogous with that of the ferritic stainless steels, which is ascribed to the degenerated ferrite phase. High-resolution transmission electron microscopy reveals that an isotropic spinodal decomposition occurred during aging at 475 deg. C in the steel studied; the original δ-ferrite decomposed into a nanometer-scaled modulated structure with a complex interconnected network, which contained an iron-rich BCC phase (α) and a chromium-enriched BCC phase (α'). It is suggested that the locking of dislocations in the modulated structure leads to the severe embrittlement

Effect of prolonged isothermal heat treatment on the mechanical behavior of advanced NANOBAIN steel

Science.gov (United States)

Avishan, Behzad

2017-09-01

The microstructural evolution and consequent changes in strength and ductility of advanced NANOBAIN steel during prolonged isothermal heat-treatment stages were investigated. The microstructure and mechanical properties of nanostructured bainite were not expected to be influenced by extending the heat-treatment time beyond the optimum value because of the autotempering phenomenon and high tempering resistance. However, experimental results indicated that the microstructure was thermodynamically unstable and that prolonged austempering resulted in carbon depletion from high-carbon retained austenite and carbide precipitations. Therefore, austenite became thermally less stable and partially transformed into martensite during cooling to room temperature. Prolonged austempering did not lead to the typical tempering sequence of bainite, and the sizes of the microstructural constituents were independent of the extended heat-treatment times. This independence, in turn, resulted in almost constant ultimate tensile strength values. However, microstructural variations enhanced the yield strength and the hardness of the material at extended isothermal heat-treatment stages. Finally, although microstructural changes decreased the total elongation and impact toughness, considerable combinations of mechanical properties could still be achieved.

Technical basis for the extension of ASME Code Case N-494 for assessment of austenitic piping

International Nuclear Information System (INIS)

Bloom, J.M.

1995-01-01

In 1990, the ASME Boiler and Pressure Vessel Code for Nuclear Components approved Code Case N-494 as an alternative procedure for evaluating laws in Light Water Reactor alterative procedure for evaluating flaws in Light Water Reactor (LWR) ferritic piping. The approach is an alternative to Appendix H of the ASME Code and alloys the user to remove some unnecessary conservatism in the existing procedure by allowing the use of pipe specific material properties. The Code Case is an implementation of the methodology of the Deformation Plasticity Failure Assessment diagram (DPFAD). The key ingredient in the application of DPFAD is that the material stress-strain curve must be in the format of a simple power law hardening stress-strain curve such as the Ramberg-Osgood (R-O) model. Ferritic materials can be accurately fit by the R-O model and, therefore, it was natural to use the DPFAD methodology for the assessment of LWR ferritic piping. An extension of Code Case N-494 to austenitic piping required a modification of the existing DPFAD methodology. The Code Case N-494 approach was revised using the PWFAD procedure in the same manner as in the development of the original N-494 approach for ferritic materials. A lower bound stress-strain curve was used to generate a PWFAD curve for the geometry of a part-through wall circumferential flaw in a cylinder under tension. Earlier work demonstrated that a cylinder under axial tension with a 50% flaw depth, 90 degrees in circumference, and radius to thickness of 10, produced a lower bound FAD curve. Validation of the new proposed Code Case procedure for austenitic piping was performed using actual pipe test data. Using the lower bound PWFAD curve, pipe test results were conservatively predicted. The resultant development of ht PWFAD curve for austenitic piping led to a revision of Code Case N-494 to include a procedure for assessment of flaws in austenitic piping

Diffusion of nitrogen in austenitic phase: Application to nitriding of stainless steels

Directory of Open Access Journals (Sweden)

Torchane Lazhar

2014-04-01

Full Text Available The nitriding treatment of the martensitic stainless steels aims to harden and to introduce compressive stresses on the surface of steel. Hardening is resulting of the martensitic transformation of the austenitic matrix enriched into nitrogen during cooling and of the germination and the nitride growth. In order to preserve the stainless character of the nitrided layer, it is imperative to control precipitation within the zone affected by the treatment. Our task consists in showing that is possible to control the composition of the gas atmosphere containing ammonia and argon and to carry out on the surface of nitrided samples at 1050°C two types of configuration of layers : a single phase layer made up by martensite enriched in nitrogen α’N and or a two phase layer made up by austenite γN and martensite α’N enriched in nitrogen.

Study of effect of austenite prehistory of 03Ch20N16AG6 steel on it structure and properties

Energy Technology Data Exchange (ETDEWEB)

Demchuk, I S; Krakhmalev, V I; Manninen, A I [Leningradskij Politekhnicheskij Inst. (USSR)

1981-01-01

Effect of preliminary cold working and different procedures of thermal treatment on structure and mechanical properties of stable austenite of 03Kh20N16AG6 steel is found out. It is shown that the degree of defectability of initial austenite structure predetermines the further deformation behaviour of the steel (level of strength characteristics, plasticity storage, hardening degree etc.) in the wide temperature range. Close connection of structural changes with properties should determine the choice of preliminary treatment of stable austenitic steel as applied to concrete condition of operation.

Phase transformation by fatigue in austenitic stainless steel

International Nuclear Information System (INIS)

Jo, Y.S.; Kwun, S.I.

1988-01-01

The effect of strain induced martensite on the fatigue behavior of AISI 304 austenitic stainless steel was investigated. During low cycle fatigue, the austenitic stainless steel showed a continuous cyclic hardening until fracture. The extent of cyclic hardening increased with decreasing austenite stability. The austenite stability was controlled by different aging time and temperature, which resulted in different carbide morphologies. The fatigue crack propagation rate near ΔK th varied also with the austenite stability inside the plastic zone at the crack up. Especially, the near-threshold fatigue crack propagation rate of the grain boundary carbide precipitated condition was the lowest. This was considered to be due to the roughness induced closure caused by intergranular facet. A new model for the intergranular facet formation and the fatigue crack propagation of grain boundary carbide precipitated condition was proposed. (Author)

Characterization of microstructure and texture across dissimilar super duplex/austenitic stainless steel weldment joint by austenitic filler metal

International Nuclear Information System (INIS)

Eghlimi, Abbas; Shamanian, Morteza; Eskandarian, Masoomeh; Zabolian, Azam; Szpunar, Jerzy A.

2015-01-01

The evolution of microstructure and texture across an as-welded dissimilar UNS S32750 super duplex/UNS S30403 austenitic stainless steel joint welded by UNS S30986 (AWS A5.9 ER309LMo) austenitic stainless steel filler metal using gas tungsten arc welding process was evaluated by optical micrography and EBSD techniques. Due to their fabrication through rolling process, both parent metals had texture components resulted from deformation and recrystallization. The weld metal showed the highest amount of residual strain and had large austenite grain colonies of similar orientations with little amounts of skeletal ferrite, both oriented preferentially in the < 001 > direction with cub-on-cube orientation relationship. While the super duplex stainless steel's heat affected zone contained higher ferrite than its parent metal, an excessive grain growth was observed at the austenitic stainless steel's counterpart. At both heat affected zones, austenite underwent some recrystallization and formed twin boundaries which led to an increase in the fraction of high angle boundaries as compared with the respective base metals. These regions showed the least amount of residual strain and highest amount of recrystallized austenite grains. Due to the static recrystallization, the fraction of low degree of fit (Σ) coincident site lattice boundaries, especially Σ3 boundaries, was increased in the austenitic stainless steel heat affected zone, while the formation of subgrains in the ferrite phase increased the content of < 5° low angle boundaries at that of the super duplex stainless steel. - Graphical abstract: Display Omitted - Highlights: • Extensive grain growth in the HAZ of austenitic stainless steel was observed. • Intensification of < 100 > orientated grains was observed adjacent to both fusion lines. • Annealing twins with Σ3 CSL boundaries were formed in the austenite of both HAZ. • Cub-on-cube OR was observed between austenite and ferrite in the weld

Characterization of microstructure and texture across dissimilar super duplex/austenitic stainless steel weldment joint by austenitic filler metal

Energy Technology Data Exchange (ETDEWEB)

Eghlimi, Abbas, E-mail: a.eghlimi@ma.iut.ac.ir [Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111 (Iran, Islamic Republic of); Shamanian, Morteza [Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111 (Iran, Islamic Republic of); Eskandarian, Masoomeh [Department of Materials Engineering, Shiraz University, Shiraz 71348-51154 (Iran, Islamic Republic of); Zabolian, Azam [Department of Natural Resources, Isfahan University of Technology, Isfahan 84156-83111 (Iran, Islamic Republic of); Szpunar, Jerzy A. [Department of Mechanical Engineering, University of Saskatchewan, Saskatoon, SK S7N 5A9 (Canada)

2015-08-15

The evolution of microstructure and texture across an as-welded dissimilar UNS S32750 super duplex/UNS S30403 austenitic stainless steel joint welded by UNS S30986 (AWS A5.9 ER309LMo) austenitic stainless steel filler metal using gas tungsten arc welding process was evaluated by optical micrography and EBSD techniques. Due to their fabrication through rolling process, both parent metals had texture components resulted from deformation and recrystallization. The weld metal showed the highest amount of residual strain and had large austenite grain colonies of similar orientations with little amounts of skeletal ferrite, both oriented preferentially in the < 001 > direction with cub-on-cube orientation relationship. While the super duplex stainless steel's heat affected zone contained higher ferrite than its parent metal, an excessive grain growth was observed at the austenitic stainless steel's counterpart. At both heat affected zones, austenite underwent some recrystallization and formed twin boundaries which led to an increase in the fraction of high angle boundaries as compared with the respective base metals. These regions showed the least amount of residual strain and highest amount of recrystallized austenite grains. Due to the static recrystallization, the fraction of low degree of fit (Σ) coincident site lattice boundaries, especially Σ3 boundaries, was increased in the austenitic stainless steel heat affected zone, while the formation of subgrains in the ferrite phase increased the content of < 5° low angle boundaries at that of the super duplex stainless steel. - Graphical abstract: Display Omitted - Highlights: • Extensive grain growth in the HAZ of austenitic stainless steel was observed. • Intensification of < 100 > orientated grains was observed adjacent to both fusion lines. • Annealing twins with Σ3 CSL boundaries were formed in the austenite of both HAZ. • Cub-on-cube OR was observed between austenite and ferrite in the weld

Characterization of aging-induced microstructural changes in M250 maraging steel using magnetic parameters

Energy Technology Data Exchange (ETDEWEB)

Rajkumar, K.V. [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India); Vaidyanathan, S. [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India); Kumar, Anish [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India); Jayakumar, T. [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India)]. E-mail: tjk@igcar.gov.in; Raj, Baldev [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India); Ray, K.K. [Indian Institute of Technology, Kharagpur 721302 (India)

2007-05-15

The best combinations of mechanical properties (yield stress and fracture toughness) of M250 maraging steel is obtained through short-term thermal aging (3-10 h) at 755 K. This is attributed to the microstructure containing precipitation of intermetallic phases in austenite-free low-carbon martensite matrix. Over-aged microstructure, containing reverted austenite degrades the mechanical properties drastically. Hence, it necessitates identification of a suitable non-destructive evaluation (NDE) technique for detecting any reverted austenite unambiguously during aging. The influence of aging on microstructure, room temperature hardness and non-destructive magnetic parameters such as coercivity (H {sub c}), saturation magnetization (M {sub s}) and magnetic Barkhausen emission (MBE) RMS peak voltage is studied in order to derive correlations between these parameters in aged M250 maraging steel. Hardness was found to increase with precipitation of intermetallics during initial aging and decrease at longer durations due to austenite reversion. Among the different magnetic parameters studied, MBE RMS peak voltage was found to be very sensitive to austenite reversion (non-magnetic phase) as they decreased drastically up on initiation of austenite reversion. Hence, this parameter can be effectively utilized to detect and quantify the reverted austenite in maraging steel specimen. The present study clearly indicates that the combination of MBE RMS peak voltage and hardness can be used for unambiguous characterization of microstructural features of technological and practical importance (3-10 h of aging duration at 755 K) in M250 grade maraging steel.

Characterization of aging-induced microstructural changes in M250 maraging steel using magnetic parameters

International Nuclear Information System (INIS)

Rajkumar, K.V.; Vaidyanathan, S.; Kumar, Anish; Jayakumar, T.; Raj, Baldev; Ray, K.K.

2007-01-01

The best combinations of mechanical properties (yield stress and fracture toughness) of M250 maraging steel is obtained through short-term thermal aging (3-10 h) at 755 K. This is attributed to the microstructure containing precipitation of intermetallic phases in austenite-free low-carbon martensite matrix. Over-aged microstructure, containing reverted austenite degrades the mechanical properties drastically. Hence, it necessitates identification of a suitable non-destructive evaluation (NDE) technique for detecting any reverted austenite unambiguously during aging. The influence of aging on microstructure, room temperature hardness and non-destructive magnetic parameters such as coercivity (H c ), saturation magnetization (M s ) and magnetic Barkhausen emission (MBE) RMS peak voltage is studied in order to derive correlations between these parameters in aged M250 maraging steel. Hardness was found to increase with precipitation of intermetallics during initial aging and decrease at longer durations due to austenite reversion. Among the different magnetic parameters studied, MBE RMS peak voltage was found to be very sensitive to austenite reversion (non-magnetic phase) as they decreased drastically up on initiation of austenite reversion. Hence, this parameter can be effectively utilized to detect and quantify the reverted austenite in maraging steel specimen. The present study clearly indicates that the combination of MBE RMS peak voltage and hardness can be used for unambiguous characterization of microstructural features of technological and practical importance (3-10 h of aging duration at 755 K) in M250 grade maraging steel

Characterization of aging-induced microstructural changes in M250 maraging steel using magnetic parameters

Science.gov (United States)

Rajkumar, K. V.; Vaidyanathan, S.; Kumar, Anish; Jayakumar, T.; Raj, Baldev; Ray, K. K.

2007-05-01

The best combinations of mechanical properties (yield stress and fracture toughness) of M250 maraging steel is obtained through short-term thermal aging (3-10 h) at 755 K. This is attributed to the microstructure containing precipitation of intermetallic phases in austenite-free low-carbon martensite matrix. Over-aged microstructure, containing reverted austenite degrades the mechanical properties drastically. Hence, it necessitates identification of a suitable non-destructive evaluation (NDE) technique for detecting any reverted austenite unambiguously during aging. The influence of aging on microstructure, room temperature hardness and non-destructive magnetic parameters such as coercivity ( Hc), saturation magnetization ( Ms) and magnetic Barkhausen emission (MBE) RMS peak voltage is studied in order to derive correlations between these parameters in aged M250 maraging steel. Hardness was found to increase with precipitation of intermetallics during initial aging and decrease at longer durations due to austenite reversion. Among the different magnetic parameters studied, MBE RMS peak voltage was found to be very sensitive to austenite reversion (non-magnetic phase) as they decreased drastically up on initiation of austenite reversion. Hence, this parameter can be effectively utilized to detect and quantify the reverted austenite in maraging steel specimen. The present study clearly indicates that the combination of MBE RMS peak voltage and hardness can be used for unambiguous characterization of microstructural features of technological and practical importance (3-10 h of aging duration at 755 K) in M250 grade maraging steel.

Interface segregation behavior in thermal aged austenitic precipitation strengthened stainless steel.

Science.gov (United States)

Li, Hui; Song, Hui; Liu, Wenqing; Xia, Shuang; Zhou, Bangxin; Su, Cheng; Ding, Wenyan

2015-12-01

The segregation of various elements at grain boundaries, precipitate/matrix interfaces were analyzed using atom probe tomography in an austenitic precipitation strengthened stainless steel aged at 750 °C for different time. Segregation of P, B and C at all types of interfaces in all the specimens were observed. However, Si segregated at all types of interfaces only in the specimen aged for 16 h. Enrichment of Ti at grain boundaries was evident in the specimen aged for 16 h, while Ti did not segregate at other interfaces. Mo varied considerably among interface types, e.g. from segregated at grain boundaries in the specimens after all the aging time to never segregate at γ'/γ phase interfaces. Cr co-segregated with C at grain boundaries, although carbides still did not nucleate at grain boundaries yet. Despite segregation tendency variations in different interface types, the segregation tendency evolution variation of different elements depending aging time were analyzed among all types of interfaces. Based on the experimental results, the enrichment factors, Gibbs interface excess and segregation free energies of segregated elements were calculated and discussed. Copyright © 2015 Elsevier B.V. All rights reserved.

The natural aging of austenitic stainless steels irradiated with fast neutrons

Science.gov (United States)

Rofman, O. V.; Maksimkin, O. P.; Tsay, K. V.; Koyanbayev, Ye. T.; Short, M. P.

2018-02-01

Much of today's research in nuclear materials relies heavily on archived, historical specimens, as neutron irradiation facilities become ever more scarce. These materials are subject to many processes of stress- and irradiation-induced microstructural evolution, including those during and after irradiation. The latter of these, referring to specimens "naturally aged" in ambient laboratory conditions, receives far less attention. The long and slow set of rare defect migration and interaction events during natural aging can significantly change material properties over decadal timescales. This paper presents the results of natural aging carried out over 15 years on austenitic stainless steels from a BN-350 fast breeder reactor, each with its own irradiation, stress state, and natural aging history. Natural aging is shown to significantly reduce hardness in these steels by 10-25% and partially alleviate stress-induced hardening over this timescale, showing that materials evolve back towards equilibrium even at such a low temperature. The results in this study have significant implications to any nuclear materials research program which uses historical specimens from previous irradiations, challenging the commonly held assumption that materials "on the shelf" do not evolve.

Modelización de la formación isotérmica de ferrita idiomórfica en aceros de medio carbono microaleados con vanadio-titanio

Directory of Open Access Journals (Sweden)

Capdevila, C.

2002-06-01

Full Text Available A theoretical model is presented in this work to calculate the evolution of isothermal austenite-to-idiomorphic ferrite transformation in a medium carbon vanadium-titanium microalloyed steel. This model has been developed on the basis of the study of the nucleation and growth kinetics of idiomorphic ferrite, considering the influence of the nature, size and distribution of the inclusions, which are responsible of the intragranular nucleation of idiomorphic ferrite. Moreover, the influence of the austenite grain size on the isothermal decomposition of austenite in idiomorphic ferrite has been thoroughly analysed. An excellent agreement (85 % in R has been obtained between experimental and predicted values of volume fraction of idiomorphic ferrite.

En este trabajo se presenta un modelo teórico para calcular la evolución con el tiempo de la transformación isotérmica de la austenita en ferrita idiomórfica en un acero de medio carbono microaleado con vanadio-titanio. En dicho modelo, desarrollado en base al estudio de la cinética de nucleación y crecimiento de ferrita idiomórfica, se ha valorado la influencia de la naturaleza, tamaño y distribución de las inclusiones responsables de la nucleación intragranular de ferrita. Así mismo, se ha analizado, con detenimiento, la influencia que tiene el tamaño de grano austenítico. El modelo ha sido validado experimentalmente, mostrándose un excelente acuerdo (85 % en R entre los resultados experimentales y los predichos por el modelo de transformación propuesto en este trabajo.

Methods allowing in-situ aging evaluation of austenitic-ferritic molded steels

International Nuclear Information System (INIS)

Paris, D.; Massoud, J.P.; Chicois, J.; Borelly, R.; Shoji, T.; Yi, Y.

1997-01-01

The molded elbows of the primary coolant circuit of the PWR type reactors are made with austenitic-ferritic stainless molded steel which is embrittled at the service temperature. To complement with the control programs lead from bench-scale experiments, it is wished to dispose to methods allowing to verify directly on the component that the estimated aging level is effectively reached. The development of non-destructive methods comes up against difficulties: the obtained signals are generally of weak amplitude; they have to be relevant of aging; the measures having not be carrying out on the component at the initial state, we do not dispose of a reference for each component. These difficulties are illustrated by the development of three methods: the electromagnetic sorting, the ferromagnetic noise and an electrochemical method. Two methods seem to be promising: the thermoelectric power and the small angle neutron scattering. (O.M.)

Experimental study of a laboratory concrete material representative of containment buildings: desorption isotherms and permeability determination

International Nuclear Information System (INIS)

Semete, P.; Fevrier, B.; Delorme, J.; Sanahuja, J.; Desgree, P.; Le Pape, Y.

2015-01-01

The isotherm sorption curve is a first order parameter for the calculations of concrete drying and/or creep using Finite Element Analysis. An experimental campaign was undertaken by EDF MMC in order to characterize the first desorption isotherm at room temperature of a laboratory material representative of concrete containment buildings. Long term drying tests were carried out on cement paste and on three samples geometries on concrete (with radial and axial one-dimensional drying on thin disks and multi-dimensional drying on Representative Elementary Volumes). The measurements results (porosity, densities and mass loss curves) are provided and the isotherms obtained for the four different configurations are compared. Several analyses of the results are proposed including the assessment of a criterion for the determination of the moisture content final balance (estimation of the asymptotic mass loss) and the back-analysis of equivalent permeability. (authors)

Austin: austenitic steel irradiation E 145-02 Irradiation Report

International Nuclear Information System (INIS)

Genet, F.; Konrad, J.

1987-01-01

Safety measures for nuclear reactors require that the energy which might be liberated in a reactor core during an accident should be contained within the reactor pressure vessel, even after very long irradiation periods. Hence the need to know the mechanical properties at high deformation velocity of structure materials that have received irradiation damage due to their utilization. The stainless steels used in the structures of reactors undergo damage by both thermal and fast neutrons, causing important changes in the mechanical properties of these materials. Various austenitic steels available as structural materials were irradiated or are under irradiation in various reactors in order to study the evolution of the mechanical properties at high deformation velocity as a function of the irradiation damage rate. The experiment called AUSTIN (AUstenitic STeel IrradiatioN) 02 was performed by the JRC Petten Establishment on behalf of Ispra in support of the reactor safety programme

Microstructure characterization in domestically-made TP310HNbN austenitic stainless steel after creep test

Science.gov (United States)

Guo, Yan; Lin, Lin; Hou, Shufang; Wang, Bohan

Microstructure characterization of domestically-made TP310HNbN austenitic stainless steel after creep test was investigated by means of transmission electron microscopy (TEM) and scanning electron microscopy (SEM). The results revealed that M23C6 carbides precipitated both inside grains and at the grain boundaries and NbCrN particles were located inside grains for creep-rupture samples. It was clear that sigma phase and NbC particles precipitated inside grains for the creep-rupture sample at 670 C. M23C6 carbides with lattice parameter of three times of the austenite matrix grow in a cube to cube orientation relationship with the matrix. The amount of M23C6 carbide particles obviously increased with the testing time prolonged. Deformation hardening induced an enhanced hardness nearby rupture surface for the creep-rupture samples with a short testing time. For the domestically-made TP310HNbN steel, great attention should be paid to the distribution, size and amount of sigma phase and M23C6 during service.

Discontinuous precipitation in a nickel-free high nitrogen austenitic stainless steel on solution nitriding

Science.gov (United States)

Mohammadzadeh, Roghayeh; Akbari, Alireza; Grumsen, Flemming B.; Somers, Marcel A. J.

2017-10-01

Chromium-rich nitride precipitates in production of nickel-free austenitic stainless steel plates via pressurised solution nitriding of Fe-22.7Cr-2.4Mo ferritic stainless steel at 1473 K (1200 °C) under a nitrogen gas atmosphere was investigated. The microstructure, chemical and phase composition, morphology and crystallographic orientation between the resulted austenite and precipitates were investigated using optical microscopy, X-ray Diffraction (XRD), Scanning and Transmission Electron Microscopy (TEM) and Electron Back Scatter Diffraction (EBSD). On prolonged nitriding, Chromium-rich nitride precipitates were formed firstly close to the surface and later throughout the sample with austenitic structure. Chromium-rich nitride precipitates with a rod or strip-like morphology was developed by a discontinuous cellular precipitation mechanism. STEM-EDS analysis demonstrated partitioning of metallic elements between austenite and nitrides, with chromium contents of about 80 wt.% in the precipitates. XRD analysis indicated that the Chromium-rich nitride precipitates are hexagonal (Cr, Mo)2N. Based on the TEM studies, (Cr, Mo)2N precipitates presented a (1 1 1)γ//(0 0 2)(Cr, Mo)2N, ?γ//?(Cr, Mo)2N orientation relationship with respect to the austenite matrix. EBSD studies revealed that the austenite in the regions that have transformed into austenite and (Cr, Mo)2N have no orientation relation to the untransformed austenite.

Thermal and mechanical stability of retained austenite in aluminum-containing multiphase TRIP steels

CERN Document Server

Zwaag, S; Kruijver, S O; Sietsma, J

2002-01-01

Stability of retained austenite is the key issue to understand transformation-induced plasticity (TRIP) effect. In this work, both thermal stability and mechanical stability are investigated by thermo-magnetic as well as in situ conventional X-ray diffraction and micro synchrotron radiation diffraction measurements. The thermal stability in a 0.20C-1.52Mn-0.25Si-0.96Al (wt%) TRIP steel is studied in the temperature range between 5 and 300 K under a constant magnetic field of 5T. It is found that almost all austenite transforms thermally to martensite upon cooling to 5K and M sub s and M sub f temperatures are analyzed to be 355 and 115 K. Transformation kinetics on the fraction versus temperature relation are well described by a model based on thermodynamics. From the in situ conventional X-ray and synchrotron diffraction measurements in a 0.17C-1.46Mn-0.26Si-1.81Al (wt%) steel, the volume fraction of retained austenite is found to decrease as the strain increases according to Ludwigson and Berger relation. T...

High temperature strength and aging behavior of 12%Cr-15%Mn austenitic steels

International Nuclear Information System (INIS)

Miyahara, Kazuya; Bae, Dong-Su; Sakai, Hidenori; Hosoi, Yuzo

1993-01-01

High Mn-Cr austenitic steels are still considered to be an important high temperature structural material from the point of view of reduced radio-activation. The objective of the present study is to make a fundamental research of mechanical properties and microstructure of 12%Cr-15%Mn austenitic steels. Especially the effects of alloying elements of V and Ti on the mechanical properties and microstructure evolution of high Mn-Cr steels were studied. Precipitation behaviors of carbides, nitrides and σ phase are investigated and their remarkable effects on the high temperature strength are found. The addition of V was very effective for strengthening the materials with the precipitation of fine VN. Ti was also found to be beneficial for the improvement of high temperature strength properties. The results of high temperature strengths of the 12Cr-15Mn austenitic steels were compared with those of the other candidate and/or reference materials, for example, JFMS (modified 9Cr-2Mo ferritic stainless steel) and JPCAs (modified 316 austenitic stainless steels). (author)

Response of cast austenitic stainless steel to low temperature plasma carburizing.

OpenAIRE

Sun, Yong

2008-01-01

The response of a cast 316 type austenitic stainless steel to the novel low temperature plasma carburizing process has been investigated in this work. The cast steel has a dendritic structure with a mix of austenite, ferrite and carbide phases. The results show that such a complex structure responds well to the carburizing process, and the inter-dendrite regions containing ferrite and carbides can be transformed to expanded austenite to form a continuous and uniform layer supersat...

Studies on the ageing of a magnesium-strontium nitrate pyrotechnic composition using isothermal microcalorimetry and thermal analysis techniques

International Nuclear Information System (INIS)

Tuukkanen, I.; Brown, S.D.; Charsley, E.L.; Goodall, S.J.; Rooney, J.J.; Griffiths, T.T.; Lemmetyinen, H.

2004-01-01

The ageing behaviour of a pyrotechnic composition containing equal parts by mass of magnesium and strontium nitrate has been followed by isothermal microcalorimetry. The measurements were carried out on the samples at 50 deg. C and 65% relative humidity in air using closed ampoules. The results have been compared to those obtained for magnesium powder under the same conditions. Following an initial induction period, the pyrotechnic compositions reacted at a much faster rate than magnesium powder alone. The main reaction products were found to be magnesium hydroxide and strontium nitrite; the amounts formed have been correlated with the cumulative heats of ageing. In addition, the influence of the ageing process on the pyrotechnic reaction has been studied by high temperature differential scanning calorimetry (DSC) and by modulated temperature DSC

Microstructural evolution in austenitic heat-resistant cast steel 35Cr25Ni12NNbRE during long-term service

International Nuclear Information System (INIS)

Liu Jiangwen; Jiao Dongling; Luo Chengping

2010-01-01

The microstructural evolution of austenitic heat-resistant cast steel 35Cr25Ni12NNbRE during aging and long-term service was investigated using optical microscope (OM), X-ray diffraction (XRD), scanning electron microscope (SEM) and transmission electron microscope (TEM). The microstructure of the as cast steel consists of the dendritic austenite, the block-like eutectic carbide M 7 C 3 spreaded among austenitic dendrite, and a small quantity of M 23 C 6 carbide. The microstructure of the steel aged at 600 deg. C consists of eutectic carbide M 23 C 6 transformed from eutectic carbide M 7 C 3 and dendritic austenite in which fine secondary carbide particles M 23 C 6 precipitated. The precipitated carbide M 23 C 6 kept a cubic-cubic orientation relationship (OR) with austenite matrix. There existed a carbide precipitation free zone (PFZ) around the eutectic carbide. For the long-term serviced samples, the secondary carbide precipitated in the austenite strikingly increased and the PFZ disappeared. Part of the M 23 C 6 transformed into M 6 C, which always kept a twin OR, [114] M 6 C //[110] A //[110] M 23 C 6 , with the austenite and the M 23 C 6 secondary carbide. In addition, a small quantity of σ phase FeCr and ε-Cr 2 N were also identified. The effects of alloy composition and service condition on the microstructural evolution of the steel were discussed.

Studies on Stress Corrosion Cracking of Super 304H Austenitic Stainless Steel

Science.gov (United States)

Prabha, B.; Sundaramoorthy, P.; Suresh, S.; Manimozhi, S.; Ravishankar, B.

2009-12-01

Stress corrosion cracking (SCC) is a common mode of failure encountered in boiler components especially in austenitic stainless steel tubes at high temperature and in chloride-rich water environment. Recently, a new type of austenitic stainless steels called Super304H stainless steel, containing 3% copper is being adopted for super critical boiler applications. The SCC behavior of this Super 304H stainless steel has not been widely reported in the literature. Many researchers have studied the SCC behavior of steels as per various standards. Among them, the ASTM standard G36 has been widely used for evaluation of SCC behavior of stainless steels. In this present work, the SCC behavior of austenitic Fe-Cr-Mn-Cu-N stainless steel, subjected to chloride environments at varying strain conditions as per ASTM standard G36 has been studied. The environments employed boiling solution of 45 wt.% of MgCl2 at 155 °C, for various strain conditions. The study reveals that the crack width increases with increase in strain level in Super 304H stainless steels.

The interfacial orientation relationship of oxide nanoparticles in a hafnium-containing oxide dispersion-strengthened austenitic stainless steel

Energy Technology Data Exchange (ETDEWEB)

Miao, Yinbin, E-mail: miao2@illinois.edu [Department of Nuclear, Plasma and Radiological Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801 (United States); Mo, Kun [Nuclear Engineering Division, Argonne National Laboratory, Lemont, IL 60493 (United States); Cui, Bai [Department of Mechanical and Materials Engineering, University of Nebraska-Lincoln, Lincoln, NE 68588 (United States); Department of Material Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801 (United States); Chen, Wei-Ying [Department of Nuclear, Plasma and Radiological Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801 (United States); Miller, Michael K.; Powers, Kathy A. [Center for Nanophase Materials Sciences, Oak Ridge National Laboratory, Oak Ridge, TN 37830 (United States); McCreary, Virginia; Gross, David [Department of Material Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801 (United States); Almer, Jonathan [X-ray Science Division, Argonne National Laboratory, Lemont, IL 60493 (United States); Robertson, Ian M. [Department of Material Science and Engineering, University of Wisconsin-Madison, Madison, WA 53706 (United States); Department of Material Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801 (United States); Stubbins, James F. [Department of Nuclear, Plasma and Radiological Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801 (United States)

2015-03-15

This work reports comprehensive investigations on the orientation relationship of the oxide nanoparticles in a hafnium-containing austenitic oxide dispersion-strengthened 316 stainless steel. The phases of the oxide nanoparticles were determined by a combination of scanning transmission electron microscopy–electron dispersive X-ray spectroscopy, atom probe tomography and synchrotron X-ray diffraction to be complex Y–Ti–Hf–O compounds with similar crystal structures, including bixbyite Y{sub 2}O{sub 3}, fluorite Y{sub 2}O{sub 3}–HfO{sub 2} solid solution and pyrochlore (or fluorite) Y{sub 2}(Ti,Hf){sub 2−x}O{sub 7−x}. High resolution transmission electron microscopy was used to characterize the particle–matrix interfaces. Two different coherency relationships along with one axis-parallel relation between the oxide nanoparticles and the steel matrix were found. The size of the nanoparticles significantly influences the orientation relationship. The results provide insight into the relationship of these nanoparticles with the matrix, which has implications for interpreting material properties as well as responses to radiation. - Highlights: • The oxide nanoparticles in a hafnium-containing austenitic ODS were characterized. • The nanoparticles are Y–Hf–Ti–O enriched phases according to APT and STEM–EDS. • Two coherency and an axis-parallel orientation relationships were found by HR-TEM. • Particle size has a prominent effect on the orientation relationship (OR). • Formation mechanism of the oxide nanoparticles was discussed based on the ORs.

Investigation of a new methodology in high temperature oxidation application to commercial austenitic steels

Energy Technology Data Exchange (ETDEWEB)

Vangeli, P.; Ivarsson, B. [Avesta Sheffield, R and D (Sweden)

2001-07-01

Avesta Sheffield R and D has evaluated a scaling temperature for heat resistant steels from laboratory gravimetric measurements of cyclic exposures. In this paper, this old method is described. A new methodology, based on the results of isothermal and cyclic tests, is proposed and discussed. It includes isothermal and cyclic oxidation kinetics of different commercial austenitic steels. Oxidation of Avesta Sheffield 153MA, 253MA and 353MA and standard commercial heat resistant steels 309S, 310S and A800 have been investigated under isothermal and cyclic conditions, in air, in the temperature range 800-1200 C. For all alloys, oxidation rates obey a parabolic law below a critical temperature. The activation energies have been calculated. Kinetics of the cyclic tests show that a critical mass change corresponding to a critical thickness of the oxide scale is responsible for the spallation start. This thickness depends on the composition of the alloys, and is very much increased by alloying minor elements like Ce. (orig.)

Low-Temperature Aging of Delta-Ferrite in 316L SS Welds; Changes in Mechanical Properties and Etching Properties

Science.gov (United States)

Abe, Hiroshi; Shimizu, Keita; Watanabe, Yutaka

Thermal aging embrittlement of LWR components made of stainless cast (e.g. CF-8 and CF-8M) is a potential degradation issue, and careful attention has been paid on it. Although welds of austenitic stainless steels (SSs) have γ-δ duplex microstructure, which is similar to that of the stainless cast, examination on thermal aging characteristics of the SS welds is very limited. In order to evaluate thermal aging behavior of weld metal of austenitic stainless steel, the 316L SS weld metal has been prepared and changes in mechanical properties and in etching properties at isothermal aging at 335°C have been investigated. The hardness of the ferrite phase has increased with aging, while the hardness of austenite phase has stayed same. It has been suggested that spinodal decomposition has occurred in δ-ferrite by the 335°C aging. The etching rates of δ-ferrite at immersion test in 5wt% hydrochloric acid solution have been also investigated using an AFM technique. The etching rate of ferrite phase has decreased consistently with the increase in hardness of ferrite phase. It has been thought that this characteristic is also caused by spinodal decomposition of ferrite into chromium-rich (α') and iron-rich (α).

Method for the calculation of volumetric fraction of retained austenite through the software for analysis of digital images

International Nuclear Information System (INIS)

Lombardo, S.; Costa, F.H.; Hashimoto, T.M.; Pereira, M.S.; Abdalla, A.J.

2010-01-01

In order to calculate the volume fraction of the retained austenite in aeronautic multiphase steels, it was used a digital analysis software for image processing. The materials studied were steels AISI 43XX with carbon content between 30, 40 and 50%, heat treated by conventional quenching and isothermal cooling in bainitic and intercritical region, characterized by optical microscopy, etching by reagent Sodium Metabisulfite (10%) for 30 seconds, with forced drying. The results were compared with the methods of X-Ray Diffraction and Magnetic Saturation through photomicrographs, showing that with this technic it is possible to quantify the percentage of retained austenite in the martensitic matrix, in the different types of steels. (author)

The stress rupture properties of austenitic steel weld metals

International Nuclear Information System (INIS)

Wood, D.S.

Elevated temperature stress rupture data on Mo containing and Mo free austenitic weld metals have been collected from French, Dutch, German and UK sources and the results analysed. The stress rupture strength of Mo containing weld metal is significantly higher than that of Mo free weld metal. At 10,000h the rupture strength of Mo containing weld metal is higher than that of Type 316 steel whereas the Mo free weld metal is about 20% lower than that of Type 304 steel. Austenitic weld metal can give low stress rupture ductility values. It is concluded that there are insufficient data to permit reliable extrapolations to long times and it is recommended that long term tests are performed to overcome this situation

Transformation of deformation martensite into austenite in stainless steels at various heating rates

International Nuclear Information System (INIS)

Gojkhenberg, Yu.N.; Shtejnberg, M.M.

1978-01-01

Under isothermal conditions and with continuous preheating at defferent rates, the inverse transformation of deformation martensite that is obtained through reductions to small, medium and great degrees, has been studied. It has been established that depending on the preheat rate, the temperature of the end α → ν of rebuilding varies according to a curve having a maximum. The ascending branch of that curve is connected with the diffusion-controlled shear transformation, whereas the descending branch with the transition to the martensite reaction of austenite formation. As the deformation degree increases, the temperature of the end of the inverse transformation decreases. As a result, recrystallization of austenite proceeds only after completing α → ν transition, when heating the steels deformed to the medium degree at rates of at least 25 deg/sec and after high reductions at rates of at least 0.8 deg/sec

Partial-Isothermally-Treated Low Alloy Ultrahigh Strength Steel with Martensitic/Bainitic Microstructure

Science.gov (United States)

Luo, Quanshun; Kitchen, Matthew; Patel, Vinay; Filleul, Martin; Owens, Dave

We introduce a new strengthening heat treatment of a Ni-Cr-Mo-V alloyed spring steel by partial isothermal salt-bath and subsequent air-cooling and tempering. Detailed isothermal treatments were made at temperatures below or above the Ms point (230°C). The salt bath time was controlled between 10 and 80 minutes. Through the new treatment, the candidate steel developed ultrahigh tensile strength 2,100 MPa, yield strength 1,800 MPa, elongation 8-10 %, hardness 580-710 HV, and V-notch Charpy toughness 10-12 J. Optical and electron microscopic observations and X-ray diffraction revealed multi-phase microstructures of bainitic/martensitic ferrites, fine carbide precipitates and retained austenite. Carbon partitioning during the bainitic/martensitic transformation was investigated for its remarkable influence on the strengthening mechanism.

Morphology change of retained austenite during austempering of carbide-free bainitic steel

Energy Technology Data Exchange (ETDEWEB)

Hofer, Christina, E-mail: christina.hofer@unileoben.ac.at [Department of Physical Metallurgy and Materials Testing, Montanuniversität Leoben, Franz-Josef-Straße 18, 8700 Leoben (Austria); Winkelhofer, Florian [Research and Development - Business Unit Coil, voestalpine Stahl GmbH, voestalpine‐Straße 3, A-4020 Linz (Austria); Clemens, Helmut; Primig, Sophie [Department of Physical Metallurgy and Materials Testing, Montanuniversität Leoben, Franz-Josef-Straße 18, 8700 Leoben (Austria)

2016-05-10

A change in the mechanical properties of a carbide-free bainitic steel was observed during prolonged holding at austempering temperature after termination of the bainitic transformation. To determine the origin of the property change, the microstructure was investigated by correlative electron microscopy. Although the retained austenite content remains the same during prolonged holding, its morphology changes from thin films separating the individual bainitic sub-units to a more globular structure. Since films of austenite contain a higher C concentration, the blocky austenite becomes gradually enriched in C during this morphology change. The more homogeneous distribution of the C after prolonged austempering leads to higher deformability as a result of a more pronounced TRIP effect. - Highlights: • Higher deformability after prolonged austempering of carbide-free bainite. • Microstructure-property relationship revealed by correlative electron microscopy. • Change in austenite morphology. • Spherodization of film austenite; C enrichment & homogenization of blocky austenite.

Effect of Cr Contents and Heat Treating on Reverted Austenite in Maraging Steel Weldments

Science.gov (United States)

Kim, S. W.; Lee, H. W.

2018-05-01

By conducting flux cored arc welding (FCAW) on maraging steels with Cr contents of 1.4 and 5.2 wt%, this study observed the effects of Cr content and heat treating on reverted austenite formation in welded maraging steel. Aging treatment was carried out at the temperatures of 450, 480 and 530 °C for 3 h in each condition. As the aging temperature increased, reverted austenite was formed along the interdendritic and intercellular grain boundaries, and the proportion of reverted austenite increased with increasing Cr addition. The aging process led to the segregation of Ti and Mo along the interdendritic and intercellular grain boundaries. Some of the welded specimens were subjected to solution heat treatment at 820 and 1250 °C for 1 h after welding, resulting in a decrease in reverted austenite fraction.

Effect of the isothermal transformation temperature on the fine structure of steel-12Kh1MF

International Nuclear Information System (INIS)

Mints, I.I.; Berezina, T.G.; Lanskaya, K.A.

1976-01-01

For detailed analysis of bainite and pearlite in steel 12Kh1MF, homogeneous structures were obtained by isothermal annealing at 350, 450, 500, and 650 0 for 1 h. Isothermal transformation of austenite leads to the formation of bainite at 350-500 0 and pearlite at 650 0 . The austenitizing temperature was 980 0 for both types of samples, with holding for 20 min. For comparison, the plates were quenched from 980 0 and 1050 0 in ice-cold brine. The investigation was conducted with use of light and electron microscopes and x-ray analysis. The long-term strength was also determined. Isothermal treatment of steel 12Kh1MF at 350-500 0 C leads to the formation of a structure consisting of upper and lower bainite. At 500 0 the structure consists primarily of upper bainite, and at 350 0 of lower bainite. With tempering of the steel with a structure of upper and lower bainite at 730 0 for 3 h the dislocations undergo redistribution of the polygonization type within ferrite needles, with development of a cellular substructure. The acicular structure of the matrix is retained in this case. The density and evenness of the distribution of carbides is higher in upper bainite than in lower bainite. Steel 12Kh1MF with a structure of upper bainite is more susceptible to recrystallization as compared with a structure of lower bainite, which is responsible for the higher heat resistance of the latter

Microstructure Evolution and the Resulted Influence on Localized Corrosion in Al-Zn-Mg-Cu Alloy during Non-Isothermal Ageing

Directory of Open Access Journals (Sweden)

Jun-Zhou Chen

2018-05-01

Full Text Available A non-isothermal ageing process was proposed for an Al-Zn-Mg-Cu alloy aiming to accommodate the slow heating/cooling procedure during the ageing of large components. The evolution of microstructure and microchemistry was analyzed by using transmission electron microscopy, high-angle annular dark field imaging, and energy dispersive spectrometry. The age-hardening of the alloy was examined to evaluate the strengthening behavior during the non-isothermal process. The corrosion behavior was investigated via observing the specimens immersed in EXCO solution (solution for Exfoliation Corrosion Susceptibility test in 2xxx and 7xxx series aluminum alloys, referring ASTM G34-01. Secondary precipitation was observed during the cooling stage, leading to increased precipitate number density. The distribution of grain boundary precipitates transits from discontinuous to continuous at the cooling stage, due to the secondary precipitation’s linking-up effect. The solutes’ enrichment on grain boundary precipitates and the depletion in precipitate-free zones develops during the heating procedure, but remains invariable during the cooling procedure. The corrosion in NIA (Non-isothermal Ageing treated specimens initiates from pitting and then transits to intergranular corrosion and exfoliation corrosion. The transition from pitting to intergranular corrosion is very slow for specimens heated to 190 °C, but accelerates slightly as the cooling procedure proceeds. The transition to exfoliation corrosion is observed to be quite slow in all specimens in non-isothermal aged to over-aged condition, suggesting a corrosion resistance comparable to that of RRA condition.

Microstructure Evolution and the Resulted Influence on Localized Corrosion in Al-Zn-Mg-Cu Alloy during Non-Isothermal Ageing.

Science.gov (United States)

Chen, Jun-Zhou; Li, Guo-Ai; Cai, Xin; Jiang, Jian-Tang; Shao, Wen-Zhu; Yang, Li; Zhen, Liang

2018-05-03

A non-isothermal ageing process was proposed for an Al-Zn-Mg-Cu alloy aiming to accommodate the slow heating/cooling procedure during the ageing of large components. The evolution of microstructure and microchemistry was analyzed by using transmission electron microscopy, high-angle annular dark field imaging, and energy dispersive spectrometry. The age-hardening of the alloy was examined to evaluate the strengthening behavior during the non-isothermal process. The corrosion behavior was investigated via observing the specimens immersed in EXCO solution (solution for Exfoliation Corrosion Susceptibility test in 2xxx and 7xxx series aluminum alloys, referring ASTM G34-01). Secondary precipitation was observed during the cooling stage, leading to increased precipitate number density. The distribution of grain boundary precipitates transits from discontinuous to continuous at the cooling stage, due to the secondary precipitation’s linking-up effect. The solutes’ enrichment on grain boundary precipitates and the depletion in precipitate-free zones develops during the heating procedure, but remains invariable during the cooling procedure. The corrosion in NIA (Non-isothermal Ageing) treated specimens initiates from pitting and then transits to intergranular corrosion and exfoliation corrosion. The transition from pitting to intergranular corrosion is very slow for specimens heated to 190 °C, but accelerates slightly as the cooling procedure proceeds. The transition to exfoliation corrosion is observed to be quite slow in all specimens in non-isothermal aged to over-aged condition, suggesting a corrosion resistance comparable to that of RRA condition.

Study of the Sensitization on the Grain Boundary in Austenitic Stainless Steel Aisi 316

Directory of Open Access Journals (Sweden)

Kocsisová Edina

2014-12-01

Full Text Available Intergranular corrosion (IGC is one of the major problems in austenitic stainless steels. This type of corrosion is caused by precipitation of secondary phases on grain boundaries (GB. Precipitation of the secondary phases can lead to formation of chromium depleted zones in the vicinity of grain boundaries. Mount of the sensitization of material is characterized by the degree of sensitization (DOS. Austenitic stainless steel AISI 316 as experimental material had been chosen. The samples for the study of sensitization were solution annealed on 1100 °C for 60 min followed by water quenching and then sensitization by isothermal annealing on 700 °C and 650 °C with holding time from 15 to 600 min. Transmission electron microscopy (TEM was used for identification of secondary phases. Electron backscattered diffraction (EBSD was applied for characterization of grain boundary structure as one of the factors which influences on DOS.

High temperature oxidation behavior of austenitic stainless steel AISI 304 in steam of nanofluids contain nanoparticle ZrO2

International Nuclear Information System (INIS)

Prajitno, Djoko Hadi; Syarif, Dani Gustaman

2014-01-01

The objective of this study is to evaluate high temperature oxidation behavior of austenitic stainless steel SS 304 in steam of nanofluids contain nanoparticle ZrO 2 . The oxidation was performed at high temperatures ranging from 600 to 800°C. The oxidation time was 60 minutes. After oxidation the surface of the samples was analyzed by different methods including, optical microscope, scanning electron microscope (SEM) and X-ray diffraction (XRD). X-ray diffraction examination show that the oxide scale formed during oxidation of stainless steel AISI 304 alloys is dominated by iron oxide, Fe 2 O 3 . Minor element such as Cr 2 O 3 is also appeared in the diffraction pattern. Characterization by optical microscope showed that cross section microstructure of stainless steel changed after oxidized with the oxide scale on the surface stainless steels. SEM and x-ray diffraction examination show that the oxide of ZrO 2 appeared on the surface of stainless steel. Kinetic rate of oxidation of austenite stainless steel AISI 304 showed that increasing oxidation temperature and time will increase oxidation rate

STRUCTURAL STABILITY OF HIGH NITROGEN AUSTENITIC STAINLESS STEELS

Directory of Open Access Journals (Sweden)

Jana Bakajová

2011-05-01

Full Text Available This paper deals with the structural stability of an austenitic stainless steel with high nitrogen content. The investigated steel was heat treated at 800°C using different annealing times. Investigation was carried out using light microscopy, transmission electron microscopy and thermodynamic calculations. Three phases were identified by electron diffraction: Cr2N, sigma – phase and M23C6. The thermodynamic prediction is in good agreement with the experimental result. The only is the M23C6 carbide phase which is not thermodynamically predicted. Cr2N is the majority secondary phase and occurs in the form of discrete particles or cells (lamellas of Cr2N and austenite.

Effect of nitrogen and boron on weldability of austenitic stainless steels

International Nuclear Information System (INIS)

Bhaduri, A.K.; Albert, S.K.; Srinivasan, G.; Divya, M.; Das, C.R.

2012-01-01

Hot cracking is a major problem in the welding of austenitic stainless steels, particularly the fully austenitic grades. A group of alloys of enhanced-nitrogen 316LN austenitic stainless steel is being developed for structural components of the Indian Fast Reactor programme. Studying the hot cracking behaviour of this nitrogen-enhanced austenitic stainless steel is an important consideration during welding, as this material solidifies without any residual delta ferrite in the primary austenitic mode. Nitrogen has potent effects on the solidification microstructure, and hence has a strong influence on the hot cracking behaviour. Different heats of this material were investigated, which included fully austenitic stainless steels containing 0.070.22 wt% nitrogen. Also, borated austenitic stainless steels, such as type 304B4, have been widely used in the nuclear applications primarily due to its higher neutron absorption efficiency. Weldability is a major concern for this alloy due to the formation of low melting eutectic phase that is enriched with iron, chromium, molybdenum and boron. Fully austenitic stainless steels are prone to hot cracking during welding in the absence of a small amount of delta ferrite, especially for compositions rich in elements like boron that increases the tendency to form low melting eutectics. Detailed weldability investigations were carried out on a grade 304B4 stainless steel containing 1.3 wt% boron. Among the many approaches that have been used to determine the hot cracking susceptibility of different alloys, Variable-Restraint (Varestraint) weld test and Hot Ductility (Gleeble) tests are commonly used to evaluate the weldability of austenitic alloys. Hence, investigations on these materials consisted of detailed metallurgical characterization and weldability studies that included studying both the fusion zone and liquation cracking susceptibility, using Varestraint tests at 0.254.0%, strain levels and Gleeble (thermo

Change of austenite state before martensite transformation and Msub(el) temperature

International Nuclear Information System (INIS)

Sarrak, V.I.; Suvorova, S.O.

1978-01-01

The N31 alloy austenite behaviour in the premartensite temperature range is investigated. To study the austenite state the method of resistance to microplastic deformation sensitive to the structural state of metals is used. The resistance to microplastic deformation was determined by amplitude dependence of internal friction. The Msub(el) temperature is found at which the change of austenite state is observed due to the appearence of elastic nuclei of martensite below the Msub(el) temperature

Evaluation of bond strength of isothermally aged plasma sprayed thermal barrier coating

Energy Technology Data Exchange (ETDEWEB)

Kim, Dae Jin; Lee, Dong Hoon; Koo, Jae Mean; Song, Sung Jin; Seok, Chang Sung [Sungkyunkwan University, Suwon (Korea, Republic of); Kim, Mun Young [Korea Plant Service and Engineering Co., Ltd., Seongnam (Korea, Republic of)

2008-07-15

In this study, disk type of thermal barrier coating system for gas turbine blade was isothermally aged in the furnace changing exposure time and temperature. For each aging condition, bond tests for three samples were conducted for evaluating degradation of adhesive or cohesive strength of thermal barrier coating system. For as-sprayed condition, the location of fracture in the bond test was in the middle of epoxy which have bond strength of 57 MPa. As specimens are degraded by thermal aging, bond strength gradually decreased and the location of failure was also changed from within top coat at the earlier stage of thermal aging to the interface between top coat and TGO at the later stage due to the delamination in the coating.

Fatigue behavior of austenitic steels. Subproject. Mechanism oriented investigation of the fatigue behavior of austenitic steel X6CrNiNb1810 in the HCF and VHCF regime. Final report; Ermuedungsverhalten Austenit. Teilprojekt. Mechanismenorientierte Untersuchung des Ermuedungsverhaltens des austenitischen Stahles X6CrNiNb1810 im HCF- und VHCF-Bereich. Abschlussbericht

Energy Technology Data Exchange (ETDEWEB)

Sorich, A.; Smaga, M.; Eifler, D.

2015-01-23

In addition to load cycles in the Low Cycle Fatigue (LCF)-regime due to start up and shut down procedures of power plants, in some components additional high-frequency loadings in the High Cycle Fatigue (HCF)- and Very High Cycle Fatigue (VHCF)-regime occur. These loadings are induced e.g. by stresses due to thermal cyclic fluctuations and fluid dynamic processes. Therefore it is necessary to characterize experimentally the cyclic deformation behavior of metastable austenitic steels at operating temperature particularly in the HCF- and VHCF-regime and to develop a nondestructive method to detect fatigue processes. This joint research project was conducted in cooperation between the Institute of Materials Science and Engineering (WKK) of the University of Kaiserslautern and the Fraunhofer-Institute for Non-Destructive Testing (IZFP) in Saarbruecken. WKK was focused on experimental investigations to characterize the cyclic deformation behavior of the metastable austenitic steel in the HCF- and VHCF-range, taking into account cyclic hardening and softening processes and in particular to consider fatigue-induced changes in microstructure. The IZFP has focused on the development and application of a testing concept based on electromagnetic ultrasonic measurements. The isothermal cyclic deformation behavior of the metastable austenitic steel X6CrNiNb1810 (1.4550, AISI 347) at 300 C in the HCF-range is characterized by cyclic softening until specimen failure. At strain amplitudes of 0.10 % ≤ ε{sub a,t} ≤ 0.15 % and the stress amplitude σ{sub a} = 160 MPa cyclic softening is followed by cyclic hardening, which results in a significant increase in life time, up to the limiting number of cycles, which was defined at N{sub I} = 10{sup 7} in HCF-regime. The cyclic hardening is determined by a transformation induced phase formation from face-centered cubic (fcc) austenite to body-centered cubic (bcc) α{sup '}-martensite and/or in hexagonal (hcp) ε-martensite. In

Influence of Ti on the Hot Ductility of High-manganese Austenitic Steels

Science.gov (United States)

Liu, Hongbo; Liu, Jianhua; Wu, Bowei; Su, Xiaofeng; Li, Shiqi; Ding, Hao

2017-07-01

The influence of Ti addition ( 0.10 wt%) on hot ductility of as-cast high-manganese austenitic steels has been examined over the temperature range 650-1,250 °C under a constant strain rate of 10-3 s-1 using Gleeble3500 thermal simulation testing machine. The fracture surfaces and particles precipitated at different tensile temperatures were characterized by means of scanning electron microscope and X-ray energy dispersive spectrometry (SEM-EDS). Hot ductility as a function of reduction curves shows that adding 0.10 wt% Ti made the ductility worse in the almost entire range of testing temperatures. The phases' equilibrium diagrams of precipitates in Ti-bearing high-Mn austenitic steel were calculated by the Thermo-Calc software. The calculation result shows that 0.1 wt% Ti addition would cause Ti(C,N) precipitated at 1,499 °C, which is higher than the liquidus temperature of high-Mn austenitic steel. It indicated that Ti(C,N) particles start forming in the liquid high-Mn austenitic steel. The SEM-EDS results show that Ti(C,N) and TiC particles could be found along the austenite grain boundaries or at triple junction, and they would accelerate the extension of the cracks along the grain boundaries.

Precipitation sequence and its effect on age hardening of alumina-forming austenitic stainless steel

Energy Technology Data Exchange (ETDEWEB)

Moon, Joonoh, E-mail: mjo99@kims.re.kr [Ferrous Alloy Department, Advanced Metallic Materials Division, Korea Institute of Materials Science, Changwon, Gyeongnam 642-831 (Korea, Republic of); Lee, Tae-Ho [Ferrous Alloy Department, Advanced Metallic Materials Division, Korea Institute of Materials Science, Changwon, Gyeongnam 642-831 (Korea, Republic of); Heo, Yoon-Uk [Graduate Institute of Ferrous Technology, Pohang University of Science and Technology, 77 Cheongam-ro, Nam-gu, Gyeongbuk 790-784 (Korea, Republic of); Han, Young-Soo [Neutron Science Division, Korea Atomic Energy Research Institute, Daejeon 305-353 (Korea, Republic of); Kang, Jun-Yun; Ha, Heon-Young [Ferrous Alloy Department, Advanced Metallic Materials Division, Korea Institute of Materials Science, Changwon, Gyeongnam 642-831 (Korea, Republic of); Suh, Dong-Woo [Graduate Institute of Ferrous Technology, Pohang University of Science and Technology, 77 Cheongam-ro, Nam-gu, Gyeongbuk 790-784 (Korea, Republic of)

2015-10-01

The precipitation sequence during ageing of Fe–14Cr–20Ni–0.9Nb–2.5Al based alumina-forming austenitic (AFA) steel was explored through a transmission electron microscopy analysis and a small angle neutron scattering experiment. The samples were aged at 700 °C for up to 504 h. Particles of NbC, M{sub 23}C{sub 6} and Ni{sub 3}Al-type L1{sub 2} were observed in the early stage of ageing. Metastable L1{sub 2} particles were formed both in grain interior and along grain boundary. M{sub 23}C{sub 6} carbides precipitated along grain boundary accompanied with precipitation of L1{sub 2} particles. After ageing for longer than 48 h, particles of B2-NiAl and Laves-Fe{sub 2}Nb were newly formed. We suggest the possibility of phase transition from L1{sub 2} to B2 with increase in ageing time. Finally, this study examined the change of mechanical properties during ageing through a Gleeble hot tension test and a Vickers hardness test, and then the relationship between precipitation behavior and mechanical properties was carefully investigated and discussed in terms of precipitation behavior.

High temperature oxidation behavior of austenitic stainless steel AISI 304 in steam of nanofluids contain nanoparticle ZrO2

Energy Technology Data Exchange (ETDEWEB)

Prajitno, Djoko Hadi, E-mail: djokohp@batan.go.id; Syarif, Dani Gustaman, E-mail: djokohp@batan.go.id [Research Center for Nuclear Materials and Radiometry, Jl. Tamansari 71, Bandung 40132 (Indonesia)

2014-03-24

The objective of this study is to evaluate high temperature oxidation behavior of austenitic stainless steel SS 304 in steam of nanofluids contain nanoparticle ZrO{sub 2}. The oxidation was performed at high temperatures ranging from 600 to 800°C. The oxidation time was 60 minutes. After oxidation the surface of the samples was analyzed by different methods including, optical microscope, scanning electron microscope (SEM) and X-ray diffraction (XRD). X-ray diffraction examination show that the oxide scale formed during oxidation of stainless steel AISI 304 alloys is dominated by iron oxide, Fe{sub 2}O{sub 3}. Minor element such as Cr{sub 2}O{sub 3} is also appeared in the diffraction pattern. Characterization by optical microscope showed that cross section microstructure of stainless steel changed after oxidized with the oxide scale on the surface stainless steels. SEM and x-ray diffraction examination show that the oxide of ZrO{sub 2} appeared on the surface of stainless steel. Kinetic rate of oxidation of austenite stainless steel AISI 304 showed that increasing oxidation temperature and time will increase oxidation rate.

Five-parameter crystallographic characteristics of the interfaces formed during ferrite to austenite transformation in a duplex stainless steel

Science.gov (United States)

Haghdadi, N.; Cizek, P.; Hodgson, P. D.; Tari, V.; Rohrer, G. S.; Beladi, H.

2018-05-01

The crystallography of interfaces in a duplex stainless steel having an equiaxed microstructure produced through the ferrite to austenite diffusive phase transformation has been studied. The five-parameter interface character distribution revealed a high anisotropy in habit planes for the austenite-ferrite and austenite-austenite interfaces for different lattice misorientations. The austenite and ferrite habit planes largely terminated on (1 1 1) and (1 1 0) planes, respectively, for the austenite-ferrite interfaces associated with Kurdjumov-Sachs (K-S) and Nishiyama-Wasserman (N-W) orientation relationships. This was mostly attributed to the crystallographic preference associated with the phase transformation. For the austenite-ferrite interfaces with orientation relationships which are neither K-S nor N-W, both austenite and ferrite habit planes had (1 1 1) orientations. Σ3 twin boundaries comprised the majority of austenite-austenite interfaces, mostly showing a pure twist character and terminating on (1 1 1) planes due to the minimum energy configuration. The second highest populated austenite-austenite boundary was Σ9, which tended to have grain boundary planes in the tilt zone due to the geometrical constraints. Furthermore, the intervariant crystallographic plane distribution associated with the K-S orientation relationship displayed a general tendency for the austenite habit planes to terminate with the (1 1 1) orientation, mainly due to the crystallographic preference associated with the phase transformation.

Cracking behavior of thermally aged and irradiated CF-8 cast austenitic stainless steel

Energy Technology Data Exchange (ETDEWEB)

Chen, Y., E-mail: Yiren_Chen@anl.gov [Argonne National Laboratory, 9700 S. Cass Ave, Argonne, IL 60439 (United States); Alexandreanu, B.; Chen, W.-Y.; Natesan, K. [Argonne National Laboratory, 9700 S. Cass Ave, Argonne, IL 60439 (United States); Li, Z.; Yang, Y. [University of Florida, Gainesville, FL 32611 (United States); Rao, A.S. [US Nuclear Regulatory Commission, 11545 Rockville Pike, Rockville, MD 20852 (United States)

2015-11-15

To assess the combined effect of thermal aging and neutron irradiation on the cracking behavior of CF-8 cast austenitic stainless steel, crack growth rate (CGR) and fracture toughness J-R curve tests were carried out on compact-tension specimens in high-purity water with low dissolved oxygen. Both unaged and thermally aged specimens were irradiated at ∼320 °C to 0.08 dpa. Thermal aging at 400 °C for 10,000 h apparently had no effect on the corrosion fatigue and stress corrosion cracking behavior in the test environment. The cracking susceptibility of CF-8 was not elevated significantly by neutron irradiation at 0.08 dpa. Transgranular cleavage-like cracking was the main fracture mode during the CGR tests, and a brittle morphology of delta ferrite was often seen on the fracture surfaces at the end of CGR tests. The fracture toughness J-R curve tests showed that both thermal aging and neutron irradiation can induce significant embrittlement. The loss of fracture toughness due to neutron irradiation was more pronounced in the unaged than aged specimens. After neutron irradiation, the fracture toughness values of the unaged and aged specimens were reduced to a similar level. G-phase precipitates were observed in the aged and irradiated specimens with or without prior aging. The similar microstructural changes resulting from thermal aging and irradiation suggest a common microstructural mechanism of inducing embrittlement in CF-8.

New type of M23C6 carbide precipitation in an austenitic stainless steel containing niobium

International Nuclear Information System (INIS)

Terao, Nobuzo; Sasmal, B.

1981-01-01

An electron microscopic study has been made of precipitation in an austenitic stainless steel, 16Cr-16Ni-0.8Nb-1.8Mo-0.06C. Attention has been focused on structural changes which take place during long ageing treatments, extended up to 14.4 Ms (4000 h). In addition to the wellknown chromium rich M 23 C 6 carbides, which appear, together with NbC, from the beginning of the precipitation treatment at 1073 K, a new plate-like morphology of M 23 C 6 carbide precipitation was observed after long ageing treatments. These M 23 C 6 carbide plates were formed on (110) planes in regions near pre-existing undissolved NbC particles and their edges were bounded by (111) planes of the fcc alloy matrix. It is suggested that this unexpected process might be favoured by the stresses produced around the undissolved NbC particles. (author)

Universality of isothermal fluid spheres in Lovelock gravity

Science.gov (United States)

Dadhich, Naresh; Hansraj, Sudan; Maharaj, Sunil D.

2016-02-01

We show universality of isothermal fluid spheres in pure Lovelock gravity where the equation of motion has only one N th order term coming from the corresponding Lovelock polynomial action of degree N . Isothermality is characterized by the equation of state, p =α ρ and the property, ρ ˜1 /r2 N . Then the solution describing isothermal spheres, which exist only for the pure Lovelock equation, is of the same form for the general Lovelock degree N in all dimensions d ≥2 N +2 . We further prove that the necessary and sufficient condition for the isothermal sphere is that its metric is conformal to the massless global monopole or the solid angle deficit metric, and this feature is also universal.

Aging behaviour of 25Cr-17Mn high nitrogen duplex stainless steel

OpenAIRE

Machado, I. F.; Padilha, A. F.

2000-01-01

The precipitation behaviour of a nickel free stainless steel containing 25% chromium, 17% manganese and 0.54% nitrogen, with duplex ferritic-austenitic microstructure, was studied using several complementary techniques of microstructural analysis after aging heat treatments between 600 and 1 000 degrees C for periods of lime between 15 and 6 000 min. During aging heat treatments, ferrite was decomposed into sigma phase and austenite by a eutectoid reaction, like in the Fe-Cr-Ni duplex stainle...

Extended X-ray absorption fine structure investigation of nitrogen stabilized expanded austenite

DEFF Research Database (Denmark)

Oddershede, Jette; Christiansen, Thomas; Ståhl, Kenny

2010-01-01

As-delivered austenitic stainless steel and nitrogen stabilized expanded austenite, both fully nitrided and denitrided (in H2), were investigated with Cr, Fe and Ni extended X-ray absorption fine structure. The data shows pronounced short-range ordering of Cr and N. For the denitrided specimen...

Effects of Aging and W Addition on the Corrosion Resistance and Mechanical Properties of Fe-Cr-Mn-N Stainless Steels

International Nuclear Information System (INIS)

Jeon, Yu Taek; Joo, Uk Hyon; Park, Yong Soo; Kim, Young Sik

2000-01-01

The characteristics of the mechanical properties and sensitization behaviors in Fe-Cr-Mn stainless steels by W addition and aging treatment were studied. Yield strength, tensile strength, elongation and impact energy decreased, and hardness increased slightly by aging treatment. W-containing alloys showed especially a larger degree of brittle characteristics due to the hard chi(χ) phase formed from the decomposition of ferrite. Carbides precipitated in grain boundary had a bad effect on impact energy rather than on strength and hardness. Ni addition suppressed the formation of ferrite and resulted in some improvement of mechanical properties. Anodic polarization tests showed that the corrosion resistance of aged alloys decreased by the formation of carbides and secondary austenite. It was observed that W addition made no improvement of the pitting potential and passive current density of aged alloys in the HCI solution. But Ni and W decreased critical current density in the sulfuric acid and made easier formation of passive film, contributing to corrosion resistance. From the results of EPR (Electrochemical Potentiokinetic Reactivation). DOS (Degree of Sensitization) increased with aging time and carbides and ferrite were preferentially attacked. It was observed that Ni delayed the sensitization. It can be concluded from the previous results that the selective dissolution of ferrite is due to the ferrite decomposition to chi (χ) phase and secondary austenite. In the secondary austenite. Cr and W which are known to improve the corrosion resistance were depleted. Therefore, it seems that ferrite phase became sensitive to corrosion

Fracture toughness of irradiated wrought and cast austenitic stainless steels in BWR environment

International Nuclear Information System (INIS)

Chopra, O.K.; Gruber, E.E.; Shack, W.J.

2007-01-01

Experimental data are presented on the fracture toughness of wrought and cast austenitic stainless steels (SSs) that were irradiated to a fluence of ∼ 1.5 x 10 21 n/cm 2 (E > 1 MeV) * (∼ 2.3 dpa) at 296-305 o C. To evaluate the possible effects of test environment and crack morphology on the fracture toughness of these steels, all tests were conducted in normal-water-chemistry boiling water reactor (BWR) environments at ∼ 289 o C. Companion tests were also conducted in air on the same material for comparison. The fracture toughness J-R curves for SS weld heat-affected-zone materials in BWR water were found to be comparable to those in air. However, the results of tests on sensitized Type 304 SS and thermally aged cast CF-8M steel suggested a possible effect of water environment. The available fracture toughness data on irradiated austenitic SSs were reviewed to assess the potential for radiation embrittlement of reactor-core internal components. The synergistic effects of thermal and radiation embrittlement of cast austenitic SS internal components are also discussed. (author)

Aging behavior and mechanical properties of maraging steels in the presence of submicrocrystalline Laves phase particles

International Nuclear Information System (INIS)

Mahmoudi, A.; Ghavidel, M.R. Zamanzad; Nedjad, S. Hossein; Heidarzadeh, A.; Ahmadabadi, M. Nili

2011-01-01

Cold rolling and annealing of homogenized Fe-Ni-Mn-Mo-Ti-Cr maraging steels resulted in the formation of submicrocrystalline Fe 2 (Mo,Ti) Laves phase particles. Optical and scanning electron microscopy, X-ray diffraction, tensile and hardness tests were used to study the microstructure, aging behavior and mechanical properties of the annealed steels. The annealed microstructures showed age hardenability during subsequent isothermal aging at 753 K. Ultrahigh fracture stress but poor tensile ductility was obtained after substantial age hardening in the specimens with 2% and 4% chromium. Increasing chromium addition up to 6% toughened the aged microstructure at the expense of the fracture stress by increasing the volume fraction of retained austenite. The Laves phase particles acted as crack nucleation sites during tensile deformation. - Highlights: → Laves phases dispersed in a BCC iron matrix by annealing of cold rolled samples. → The samples showed age hardenability during subsequent isothermal aging at 753 K. → Ultrahigh fracture stress but poor ductility was obtained after age hardening. → Increasing chromium addition toughened the aged microstructure. → Laves phase particles acting as crack nucleation sites during tensile deformation.

Damping Capacity of High Manganese Austenitic Stainless Steel with a Two Phase Mixed Structure of Martensite and Austenite

International Nuclear Information System (INIS)

Hwang, Tae Hyun; Kang, Chang-Yong

2013-01-01

The damping capacity of high manganese austenitic stainless steel with a two phase mixed structure of deformation-induced martensite and reversed austenite was studied. Reversed austenite with an ultra-fine grain size of less than 0.2 μm was obtained by reversion treatment. The two phase structure of deformation-induced martensite and reversed austenite was obtained by annealing treatment at a range of 500-700 °C and various times in cold rolled high manganese austenitic stainless steel. The damping capacity increased with an increasing annealing temperature and time. In high manganese stainless steel with the two phase mixed structure of martensite and austenite, the damping capacity decreased with an increasing volume fraction of deformation-induced martensite. Thus, the damping capacity was strongly affected by deformation-induced martensite. The results confirmed that austenitic stainless steel with a good combination of strength and damping capacity was obtained from the two phase mixed structure of austenite and martensite.

Microstructural features of dissimilar welds between 316LN austenitic stainless steel and alloy 800

International Nuclear Information System (INIS)

Sireesha, M.; Sundaresan, S.

2000-01-01

For joining type 316LN austenitic stainless steel to modified 9Cr-1Mo steel for power plant application, a trimetallic configuration using an insert piece (such as alloy 800) of intermediate thermal coefficient of expansion (CTE) has been sometimes suggested for bridging the wide gap in CTE between the two steels. Two joints are thus involved and this paper is concerned with the weld between 316LN and alloy 800. These welds were produced using three types of filler materials: austenitic stainless steels corresponding to 316,16Cr-8Ni-2Mo, and the nickel-base Inconel 182 1 . The weld fusion zones and the interfaces with the base materials were characterised in detail using light and transmission electron microscopy. The 316 and Inconel 182 weld metals solidified dendritically, while the 16-8-2(16%Cr-8%Ni-2%Mo) weld metal showed a predominantly cellular substructure. The Inconel weld metal contained a large number of inclusions when deposited from flux-coated electrodes, but was relatively inclusion-free under inert gas-shielded welding. Long-term elevated-temperature aging of the weld metals resulted in embrittling sigma phase precipitation in the austenitic stainless steel weld metals, but the nickel-base welds showed no visible precipitation, demonstrating their superior metallurgical stability for high-temperature service. (orig.)

Understanding and modelling of the aniso-thermal cyclic mechanical behaviour of the AISI 316LN austenitic stainless steel

International Nuclear Information System (INIS)

Gentet, D.

2009-11-01

The main subject of this report consists in proposing a mechanical model of the viscoplastic behaviour of an austenitic stainless steel under isothermal and aniso-thermal low cycle fatigue loadings at high temperatures (550-900 K). In this domain, numerous phenomena linked to dynamic strain ageing (DSA) and to dipolar dislocation structure formation may appear. Isothermal and aniso-thermal low cycle fatigue tension-compression tests were performed in order to verify some aspects about the effect of temperature on the mechanical behaviour. The study of the hysteresis loops and the observation of dislocation structures carried on transmission electron microscopy establish two different DSA mechanisms during isothermal tests. The effect of temperature history is shown for for particular temperature sequences. It is demonstrated that the stress amplitude increase when the sample is submitted to cycles at 'high temperature' is linked to the second mechanism of DSA. It comes from the increase of short range interaction between dislocations (chromium segregation), but it is also the consequence of the lack of dipolar structure annihilation at low temperature. From the experimental analysis of DSA mechanisms and dipolar restoration, a macroscopic aniso-thermal model is developed using physical internal variables (densities of dislocations). The equations of a polycrystalline model are rewritten with the aim of getting a simple multi-scale approach which can be used on finite elements analysis software. Between 550 and 873 K, the simulation results are in good accordance with the macroscopic and microscopic observations of low cycle fatigue, relaxation, and 2D-ratchetting tests. (author)

Design of Wear-Resistant Austenitic Steels for Selective Laser Melting

Science.gov (United States)

Lemke, J. N.; Casati, R.; Lecis, N.; Andrianopoli, C.; Varone, A.; Montanari, R.; Vedani, M.

2018-03-01

Type 316L stainless steel feedstock powder was modified by alloying with powders containing carbide/boride-forming elements to create improved wear-resistant austenitic alloys that can be readily processed by Selective Laser Melting. Fe-based alloys with high C, B, V, and Nb contents were thus produced, resulting in a microstructure that consisted of austenitic grains and a significant amount of hard carbides and borides. Heat treatments were performed to modify the carbide distribution and morphology. Optimal hard-phase spheroidization was achieved by annealing the proposed alloys at 1150 °C for 1 hour followed by water quenching. The total increase in hardness of samples containing 20 pct of C/B-rich alloy powder was of 82.7 pct while the wear resistance could be increased by a factor of 6.

Effect of nitrate on corrosion of austenitic stainless steel in boiling nitric acid solution containing chromium ions

International Nuclear Information System (INIS)

Hasegawa, Satoshi; Kim, Seong-Yun; Ebina, Tetsunari; Ito, Tatsuya; Nagano, Nobumichi; Hitomi, Keitaro; Ishii, Keizo; Tokuda, Haruaki

2016-01-01

The oxidation behavior of chromium and the corrosion behavior of austenitic stainless steel in boiling nitric acid solution containing highly concentrated nitrates were investigated using UV-visible spectroscopic measurements, Raman spectral measurements, immersion tests, and potentiodynamic polarization measurements. The oxidation rate measurement of chromium from Cr(III) to Cr(VI) was performed by 1 M boiling nitric acid solution containing each highly concentrated nitrates: Al(NO_3)_3, Nd(NO_3)_3, Ca(NO_3)_2, Mg(NO_3)_2, and NaNO_3 as a simulant of uranium nitrate in uranium concentrator in reprocessing plants. As a result, the rate of chromium oxidation was different depending on the added nitrates even at the same nitric acid concentration. In addition, the oxidation rate of chromium was increased with increasing the calculated partial pressure of nitric acid in consideration of the hydration of cation of nitrates. Furthermore, the corrosion rate of type 310 stainless steel was accelerated by the solution having a high chromium oxidation rate containing nitrates. These results indicated that the acceleration of the corrosion rate in the solutions depending on the oxidation rate of chromium, and the rate is affected by the salt-effect of nitrates. (author)

On abnormal decomposition of supercooled austenite in carbon and alloy steels

International Nuclear Information System (INIS)

Parusov, V.V.; Dolzhenkov, I.I.; Podobedov, L.V.; Vakulenko, I.A.

1980-01-01

Residual stresses which appear as a result of thermal cycling in the temperature range of 300-700 deg C are investigated in an austenitic class steel (03Kh18N11) to ground the assumption on the effect of plastic deformation, appearing due to thermal stresses, on the mechanism of supercooled austenite decomposition. The determination of residual stresses is carried out with the help of X-ray diffraction analysis. It is established that the deformation brings about an increase in density of dislocation the interaction of which leads to the formation of a typical austenite substructure which conditions the proceeding of the eutectoid transformation according to an abnormal mechanism. It is noted, that the grain pearlite formation due to plastic and microplastic deformation of supercooled austenite induced by thermal stresses should be taken into account when developing steel heat treatment shedules [ru

Kinetic of martensitic transformations induced by hydrogen in the austenite

International Nuclear Information System (INIS)

Oliveira, Sergio P. de; Saavedra, A.; Miranda, P.E.V. de

1986-01-01

The X-ray diffractometry technique was used, with an automatic data acquisition system to determine the kinetics of hydrogen induced martensitic phase transformations in an AISI 304 austenitic stainless steel type, used in nuclear power plants. Hydrogenation was performed cathodically in a 1N sulfuric acid solution, containing 100 mg/l of arsenic trioxide, at 50 0 C, during 2 hours and with a current density of 200 A/m 2 . It was found that the microstructure of the steel plays a role on the generation of hydrogen induced martensitic phases and surface micro cracks. Both kinetics were slower on a pre-cold rolled steel. (Author) [pt

The kinetic of mass loss of grades A and B of melted TNT by isothermal and non-isothermal gravimetric methods

Directory of Open Access Journals (Sweden)

Hamid Reza Pouretedal

2018-04-01

Full Text Available The kinetic and activation energy of mass loss of two grades of melted TNT explosive, grade A and grade B, with freezing points of 80.57 and 78.15 °C, respectively, were studied by isothermal and non-isothermal gravimetric methods. In isothermal method, the mass loss of samples in containers of glass and aluminum was followed in temperatures of 80, 90 and 100 °C. The kinetic of the mass loss of the samples in the aluminum container was higher than the kinetic of it in the glass container that can be related to the effects of heat transfer and catalytic of aluminum metal. Also, the presence of impurities in grade B was due to increasing of kinetic of mass loss of it versus grade A. The non-isothermal curves were obtained in range of 30–330 °C at heating rates of 10, 15 and 20 °C⋅min−1. The TG/DTG data were used for determination of activation energy (Ea of mass loss of TNT samples upon degradation by using Ozawa, Kissinger, Ozawa-Flynn-Wall (OFW and Kissinger-Akahira-Sunose (KAS methods as model free methods. The activation energies of grades of A and B of TNT was obtained 99–120 and 66–70 kJ mol−1, respectively. The lower values of activation energy of the degradation reaction of grade B confirm the effect of impurities in the kinetics of mass loss of this grade. Keywords: TNT, Isothermal, Non-isothermal, Kinetic, Mass loss

Effect of 4-(N,N-diethylamino)benzaldehyde thiosemicarbazone on the corrosion of aged 18 Ni 250 grade maraging steel in phosphoric acid solution

International Nuclear Information System (INIS)

Poornima, T.; Nayak, Jagannath; Nityananda Shetty, A.

2011-01-01

Highlights: → DEABT as corrosion inhibitor for maraging steel in phosphoric acid. → Inhibition efficiency increases with increase in inhibitor concentration. → Inhibition efficiency decreases with increase in temperature. → Adsorption obeys Langmuir adsorption isotherm. - Abstract: 4-(N,N-diethylamino)benzaldehyde thiosemicarbazone (DEABT) was studied for its corrosion inhibition property on the corrosion of aged 18 Ni 250 grade maraging steel in 0.67 M phosphoric acid at 30-50 deg. C by potentiodynamic polarization, EIS and weight loss techniques. Inhibition efficiency of DEABT was found to increase with the increase in DEABT concentration and decrease with the increase in temperature. The activation energy E a and other thermodynamic parameters (ΔG ads 0 , ΔH ads 0 , ΔS ads 0 ) have been evaluated and discussed. The adsorption of DEABT on aged maraging steel surface obeys the Langmuir adsorption isotherm model and the inhibitor showed mixed type inhibition behavior.

Retained Austenite in SAE 52100 Steel Post Magnetic Processing and Heat Treatment

Energy Technology Data Exchange (ETDEWEB)

Pappas, Nathaniel R [ORNL; Watkins, Thomas R [ORNL; Cavin, Odis Burl [ORNL; Jaramillo, Roger A [ORNL; Ludtka, Gerard Michael [ORNL

2007-01-01

Steel is an iron-carbon alloy that contains up to 2% carbon by weight. Understanding which phases of iron and carbon form as a function of temperature and percent carbon is important in order to process/manufacture steel with desired properties. Austenite is the face center cubic (fcc) phase of iron that exists between 912 and 1394 C. When hot steel is rapidly quenched in a medium (typically oil or water), austenite transforms into martensite. The goal of the study is to determine the effect of applying a magnetic field on the amount of retained austenite present at room temperature after quenching. Samples of SAE 52100 steel were heat treated then subjected to a magnetic field of varying strength and time, while samples of SAE 1045 steel were heat treated then subjected to a magnetic field of varying strength for a fixed time while being tempered. X-ray diffraction was used to collect quantitative data corresponding to the amount of each phase present post processing. The percentage of retained austenite was then calculated using the American Society of Testing and Materials standard for determining the amount of retained austenite for randomly oriented samples and was plotted as a function of magnetic field intensity, magnetic field apply time, and magnetic field wait time after quenching to determine what relationships exist with the amount of retained austenite present. In the SAE 52100 steel samples, stronger field strengths resulted in lower percentages of retained austenite for fixed apply times. The results were inconclusive when applying a fixed magnetic field strength for varying amounts of time. When applying a magnetic field after waiting a specific amount of time after quenching, the analyses indicate that shorter wait times result in less retained austenite. The SAE 1045 results were inconclusive. The samples showed no retained austenite regardless of magnetic field strength, indicating that tempering removed the retained austenite. It is apparent

Construction of isotherms in solvent extraction of copper

Directory of Open Access Journals (Sweden)

Cvetkovski Vladimir B.

2009-01-01

Full Text Available The aim of this work is construction of equilibrium isotherms in solvent extraction. Technological parameters have been predicted for treatment of mine water by solvent extraction and electrowining. Two stages of extractions and one stage of stripping have been predicted for copper recovery by analyzing the equilibrium isotherms. The process was performed on mine water with 2,5 g/dm3 Cu2+, 3 g/dm Fe2+, pH 1,8, using 9 vol% LIX 984N in kerosene (organic solvent, with 95 and 98% stages efficiencies, respectively. This course produced an advanced electrolyte solution, suitable for electrowining and cathodic copper recovery, containing 51 g/dm3 Cu2+ and 160g/dm3 H2SO4 from a 30 g/dm3 Cu and 190 g/dm3 H2SO4.

Phase stability of high manganese austenitic steels for cryogenic applications

CERN Document Server

Couturier, K

2000-01-01

The aim of this work is to study the austenitic stability against a' martensitic transformation of three non-magnetic austenitic steels : a new stainless steel X2CrMnNiMoN 19-12-11-1 grade, a traditional X8CrMnNiN 19-11-6 grade and a high manganese X8MnCrNi 28-7-1 grade. Measurements of relative magnetic susceptibility at room temperature are performed on strained tensile specimens at 4.2 K. A special extensometer for high precision strain measurements at low temperature has been developed at CERN to test specimens up to various levels of plastic strain. Moreover, the high precision strain recording of the extensometer enables a detailed study of the serrated yield phenomena associated with 4.2 K tensile testing and their influence on the evolution of magnetic susceptibility. The results show that high Mn contents increase the stability of the austenitic structure against a' martensitic transformation, while keeping high strength at cryogenic temperature. Moreover, proper elaboration through primary and possi...

In Situ Study of Phase Transformations during Non-Isothermal Tempering of Bainitic and Martensitic Microstructures

Directory of Open Access Journals (Sweden)

S. Hesamodin Talebi

2017-09-01

Full Text Available Phase transformations during non-isothermal tempering of bainitic or martensitic microstructures obtained after quenching of a medium-carbon low-alloy steel was studied. The microstructures correspond to different locations of an as-quenched large-sized forged ingot used as a die material in the automotive industry. High-resolution dilatometry experiments were conducted to simulate the heat treatment process, as well as to investigate different phenomena occurring during non-isothermal tempering. The microstructures were characterized using optical and scanning electron microscopy. Dilatometry analyses demonstrated that tempering behavior varied significantly from bainitic to martensitic microstructures. Retained austenite, which exists between bainitic ferrite sheaves, decomposes to lower bainite causing a remarkable volume increase. It was found that this decomposition finishes below 386 °C. By contrast, martensite tempering was accompanied with a volume decrease due to the decomposition of medium-carbon martensite to low carbon martensite and carbides.

Weldability of newly developed austenitic alloy for cryogenic service

International Nuclear Information System (INIS)

Ogawa, T.; Koseki, T.

1986-01-01

The testing reported in this paper involved typical steels of the new grades such as STEEL-A (0.025C-14Ni-25Cr-0.35N), STEEL-B (0.04C-23Mn-13Cr-0.22N) and STEEL-C (0.20C-25Mn-5Cr), and commercial steels of Type 300 series. Weldments were made mainly using the GTAW, SMAW and SAW processes with experimental and commercial filler metals. Strength and toughness of weldments were examined at 77 K (-321 0 F) and 4 K. The strengthening of material through the addition of nitrogen was far greater in the weld metal that in the base metal at cryogenic temperature. In fact, 0.2% proof stress of weld metals bearging 0.20% to 0.40% nitrogen at 77 K exhibited a higher value by 60 to 150 MPa (8,740 to 21,760 psi) than that of the base metal. Impact absorbed energy of weld metals at 77 K decreased rapidly with nitrogen content, 60-90 J at 0.20%N to 20-50J at 0.35% N. Rather high impact absorbed energy was obtained when the weld metal solidified as primary austenitic phase, resulting in fully austenitic microstructure or austenite-eutectic ferrite mixture at ambient temperature. In addition, oxide inclusions, the number of which strongly depends on welding processes, were detrimental to toughness of weld metals at cryogenic temperature

Interfacial Reaction and IMC Growth of an Ultrasonically Soldered Cu/SAC305/Cu Structure during Isothermal Aging

Directory of Open Access Journals (Sweden)

Yulong Li

2018-01-01

Full Text Available In order to accelerate the growth of interfacial intermetallic compound (IMC layers in a soldering structure, Cu/SAC305/Cu was first ultrasonically spot soldered and then subjected to isothermal aging. Relatively short vibration times, i.e., 400 ms and 800 ms, were used for the ultrasonic soldering. The isothermal aging was conducted at 150 °C for 0, 120, 240, and 360 h. The evolution of microstructure, the IMC layer growth mechanism during aging, and the shear strength of the joints after aging were systemically investigated. Results showed the following. (i Formation of intermetallic compounds was accelerated by ultrasonic cavitation and streaming effects, the thickness of the interfacial Cu6Sn5 layer increased with aging time, and a thin Cu3Sn layer was identified after aging for 360 h. (ii The growth of the interfacial IMC layer of the ultrasonically soldered Cu/SAC305/Cu joints followed a linear function of the square root of the aging time, revealing a diffusion-controlled mechanism. (iii The tensile shear strength of the joint decreased to a small extent with increasing aging time, owing to the combined effects of IMC grain coarsening and the increase of the interfacial IMC. (iv Finally, although the fracture surfaces and failure locations of the joint soldered with 400 ms and 800 ms vibration times show similar characteristics, they are influenced by the aging time.

Oxidation resistant high creep strength austenitic stainless steel

Science.gov (United States)

Brady, Michael P.; Pint, Bruce A.; Liu, Chain-Tsuan; Maziasz, Philip J.; Yamamoto, Yukinori; Lu, Zhao P.

2010-06-29

An austenitic stainless steel displaying high temperature oxidation and creep resistance has a composition that includes in weight percent 15 to 21 Ni, 10 to 15 Cr, 2 to 3.5 Al, 0.1 to 1 Nb, and 0.05 to 0.15 C, and that is free of or has very low levels of N, Ti and V. The alloy forms an external continuous alumina protective scale to provide a high oxidation resistance at temperatures of 700 to 800.degree. C. and forms NbC nanocarbides and a stable essentially single phase fcc austenitic matrix microstructure to give high strength and high creep resistance at these temperatures.

Hot deforming effect on the isothermal transformation of a steel for hot working schedules; Efeito da deformacao a quente sobre a transformacao isotermica de um aco para trabalho a quente

Energy Technology Data Exchange (ETDEWEB)

Mendonca Lima, Ricardo Fonseca de; Nogueira, Marcos Alexandre Stuart [Acos Villares SA, Rio de Janeiro, RJ (Brazil)

1989-12-31

The effect of hot deformation of austenite on its isothermal deformation at 645 deg C and on the final grain size, obtained after hardening, has been investigated. The deformation was given to compression with different degrees of reduction of the material. (author) 18 refs., 13 figs., 1 tab.

Effects of cooling rate, austenitizing temperature and austenite deformation on the transformation behavior of high-strength boron steel

International Nuclear Information System (INIS)

Mun, Dong Jun; Shin, Eun Joo; Choi, Young Won; Lee, Jae Sang; Koo, Yang Mo

2012-01-01

Highlights: ► Non-equilibrium segregation of B in steel depends strongly on the cooling rate. ► A higher austenitization temperature reduced the B hardenability effect. ► An increase in B concentration at γ grain boundaries accelerates the B precipitation. ► The loss of B hardenability effect is due to intragranular borocarbide precipitation. ► The controlled cooling after hot deformation increased the B hardenability effect. - Abstract: The phase transformation behavior of high-strength boron steel was studied considering the segregation and precipitation behavior of boron (B). The effects of cooling rate, austenitizing temperature and austenite deformation on the transformation behavior of B-bearing steel as compared with B-free steel were investigated by using dilatometry, microstructural observations and analysis of B distribution. The effects of these variables on hardenability were discussed in terms of non-equilibrium segregation mechanism and precipitation behavior of B. The retardation of austenite-to-ferrite transformation by B addition depends strongly on cooling rate (CR); this is mainly due to the phenomenon of non-equilibrium grain boundary segregation of B. The hardenability effect of B-bearing steel decreased at higher austenitizing temperature due to the precipitation of borocarbide along austenite grain boundaries. Analysis of B distribution by second ion mass spectroscopy confirmed that the grain boundary segregation of B occurred at low austenitizing temperature of 900 °C, whereas B precipitates were observed along austenite grain boundaries at high austenitizing temperature of 1200 °C. The significant increase in B concentration at austenite grain boundaries due to grain coarsening and a non-equilibrium segregation mechanism may lead to the B precipitation. In contrast, solute B segregated to austenite grain boundaries during cooling after heavy deformation became more stable because the increase in boundary area by grain

Effect of bainitic isothermal transformation plus Q&P process on the microstructure and mechanical properties of 0.2C bainitic steel

Energy Technology Data Exchange (ETDEWEB)

Huang, Yuyin; Li, Qiangguo; Huang, Xuefei; Huang, Weigang, E-mail: huangwg56@163.com

2016-12-15

A novel bainitic isothermal transformation plus quenching and partitioning (B-QP) process was developed for a 0.2C-1.5Si-1.8Mn bainitic steel. The microstructure and mechanical properties of the steel treated by different heat treatment process were investigated. The results show that the B{sub 3}-QP (the subscript ‘3’ indicates the isothermal holding of 3 min for the bainitic transformation) samples exhibit a multiphase microstructure containing carbide-free bainite, martensite, film-like retained austenite. The microstructure is much finer than that of the Q&T samples with full martensite and the B{sub 30}-QP samples with a bainite microstructure. Although the Q&T sample has the highest tensile strength (1455 MPa), the ductility and the product of strength and elongation (PSE) are lower. In contrast, the B{sub 3}-QP and B{sub 30}-QP samples exhibit better ductility and higher PSE values of 26.3 GPa% and 28.2 GPa%, respectively. Furthermore, the B{sub 3}-QP sample exhibits maximum impact toughness value of 121 Jcm{sup −2}, which is about 20% and 55% higher than those of Q&T sample (101 J cm{sup −2}) and B{sub 30}-QP sample (78 J cm{sup −2}) respectively.

Influence of Thermal Aging on Tensile and Low Cycle Fatigue Behavior of Type 316LN Austenitic Stainless Steel Weld Joint

Science.gov (United States)

Suresh Kumar, T.; Nagesha, A.; Ganesh Kumar, J.; Parameswaran, P.; Sandhya, R.

2018-05-01

Influence of short-term thermal aging on the low-cycle fatigue (LCF) behavior of 316LN austenitic stainless steel weld joint with 0.07 wt pct N has been investigated. Prior thermal exposure was found to improve the fatigue life compared with the as-welded condition. Besides, the treatment also imparted a softening effect on the weld metal, leading to an increase in the ductility of the weld joint which had a bearing on the cyclic stress response. The degree of cyclic hardening was seen to increase after aging. Automated ball-indentation (ABI) technique was employed toward understanding the mechanical properties of individual zones across the weld joint. It was observed that the base metal takes most of the applied cyclic strain during LCF deformation in the as-welded condition. In the aged condition, however, the weld also participates in the cyclic deformation. The beneficial effect of thermal aging on cyclic life is attributed to a reduction in the severity of the metallurgical notch leading to a restoration of ductility of the weld region. The transformation of δ-ferrite to σ-phase during the aging treatment was found to influence the location of crack initiation. Fatigue cracks were found to initiate in the base metal region of the joint in most of the testing conditions. However, embrittlement in the weld metal caused a shift in the point of crack initiation with increasing strain amplitude under LCF.

Prediction of long-term precipitate evolution in austenitic heat-resistant steels

Energy Technology Data Exchange (ETDEWEB)

Shim, Jae-Hyeok; Jung, Woo-Sang; Cho, Young Whan [Korea Institute of Science and Technology, Seoul (Korea, Republic of). Materials/Devices Div.; Kozeschnik, Ernst [Vienna Univ. of Technology (Austria). Inst. of Materials Science and Technology

2010-07-01

Numerical prediction of the long-term precipitate evolution in five different austenitic heat-resistant stainless steels, NF709, Super304H, Sanicro25, CF8C-PLUS and HTUPS has been carried out. MX and M{sub 23}C{sub 6} are predicted to remain as major precipitates during long-term aging in these steels. The addition of 3 wt% Cu produces very fine Cu-rich precipitates during aging in Super304H and Sanicro25. It is found that the amount of Z phase start to increase remarkably between 1,000 and 10,000 hours of aging at the expense of MX precipitates in the steels containing a high nitrogen content. However, the growth rate of Z phase is relatively slow and its average size reaches at most a few tens of nanometers after 100,000 hours of aging at 700 C, compared with 9-12% Cr ferritic/martensitic heat-resistant steels. The predicted precipitation sequence and precipitate size during aging are in general agreement with experimental observations. (orig.)

Corrosion of silicon-containing austenitic stainless steels under trans-passive conditions

International Nuclear Information System (INIS)

Stolarz, Jacek

1989-01-01

This research thesis addresses austenitic stainless steels which are used in installations for the chemical treatment of nuclear fuels, and are there in contact with nitric acid solutions the oxidising character of which generally promotes metal passivity. However, if this nitric environment becomes too oxidising, these steels may face severe corrosion problems. More particularly, this thesis addresses the study of intergranular corrosion, and aims at analysing various aspects of the corrosion of these austenitic stainless steels in trans-passive conditions. The author aims at determining and distinguishing the contributions due to silicon and those related to the presence of other impurities and addition elements by comparing the behaviours of industrial grade steels and high purity alloys in rigorously controlled electrochemical conditions. Another objective is to study the influence of the intergranular structure on silicon segregation by means of an attack technique in trans-passive conditions. After a report of a bibliographical study on the addressed topics and a presentation of the studied materials and implemented experimental techniques, the author reports the study of steel behaviour with respect to generalised dissolution in trans-passive conditions, as well in the nitric environment as in a sulphuric acid solution at imposed potential. Localised intragranular corrosion phenomena are discussed. A trans-passive intragranular corrosion model is proposed, and its possibilities in the analysis of intergranular segregation analysis are discussed. Experimental results of trans-passive intergranular corrosion of stainless steels are presented and interpreted by using the McLean segregation model. The influence of steel composition and of experimental conditions is discussed, as well as the role of grain boundary structure in the corrosion process [fr

Sandblasting induced stress release and enhanced adhesion strength of diamond films deposited on austenite stainless steel

Science.gov (United States)

Li, Xiao; Ye, Jiansong; Zhang, Hangcheng; Feng, Tao; Chen, Jianqing; Hu, Xiaojun

2017-08-01

We firstly used sandblasting to treat austenite stainless steel and then deposited a Cr/CrN interlayer by close field unbalanced magnetron sputtering on it. After that, diamond films were prepared on the interlayer. It is found that the sandblasting process induces phase transition from austenite to martensite in the surface region of the stainless steel, which decreases thermal stress in diamond films due to lower thermal expansion coefficient of martensite phase compared with that of austenite phase. The sandblasting also makes stainless steel's surface rough and the Cr/CrN interlayer film inherits the rough surface. This decreases the carburization extent of the interlayer, increases nucleation density and modifies the stress distribution. Due to lower residual stress and small extent of the interlayer's carburization, the diamond film on sandblast treated austenite stainless steel shows enhanced adhesion strength.

Effect of Heat Treatment on the Microstructure and Mechanical Properties of Nitrogen-Alloyed High-Mn Austenitic Hot Work Die Steel

Directory of Open Access Journals (Sweden)

Yi Zhang

2017-03-01

Full Text Available In view of the requirements for mechanical properties and service life above 650 °C, a high-Mn austenitic hot work die steel, instead of traditional martensitic hot work die steel such as H13, was developed in the present study. The effect of heat treatment on the microstructure and mechanical properties of the newly developed work die steel was studied. The results show that the microstructure of the high-Mn as-cast electroslag remelting (ESR ingot is composed of γ-Fe, V(C,N, and Mo2C. V(C,N is an irregular multilateral strip or slice shape with severe angles. Most eutectic Mo2C carbides are lamellar fish-skeleton-like, except for a few that are rod-shaped. With increasing solid solution time and temperature, the increased hardness caused by solid solution strengthening exceeds the effect of decreased hardness caused by grain size growth, but this trend is reversed later. As a result, the hardness of specimens after various solid solution heat treatments increases first and then decreases. The optimal combination of hardness and austenitic grain size can be obtained by soaking for 2 h at 1170 °C. The maximum Rockwell hardness (HRC is 47.24 HRC, and the corresponding austenite average grain size is 58.4 μm. When the solid solution time is 3 h at 1230 °C, bimodality presented in the histogram of the austenite grain size as a result of further progress in secondary recrystallization. Compared with the single-stage aging, the maximum impact energy of the specimen after two-stage aging heat treatment was reached at 16.2 J and increased by 29.6%, while the hardness decreased by 1–2 HRC. After two-stage aging heat treatment, the hardness of steel reached the requirements of superior grade H13, and the maximum impact energy was 19.6% higher than that of superior grade H13, as specified in NADCA#207-2003.

Austenitic Reversion of Cryo-rolled Ti-Stabilized Austenitic Stainless Steel: High-Resolution EBSD Investigation

Science.gov (United States)

Tiamiyu, A. A.; Odeshi, A. G.; Szpunar, J. A.

2018-02-01

In this study, AISI 321 austenitic stainless steel (ASS) was cryo-rolled and subsequently annealed at 650 and 800 °C to reverse BCC α'-martensite to FCC γ-austenite. The texture evolution associated with the reversion at the selected temperatures was investigated using high-resolution EBSD. After the reversion, TiC precipitates were observed to be more stable in 650 °C-annealed specimens than those reversed at 800 °C. {110} texture was mainly developed in specimens subjected to both annealing temperatures. However, specimens reversed at 650 °C have stronger texture than those annealed at 800 °C, even at the higher annealing time. The strong intensity of {110} texture component is attributed to the ability of AISI 321 ASS to memorize the crystallographic orientation of the deformed austenite, a phenomenon termed texture memory. The development of weaker texture in 800 °C-annealed specimens is attributed to the residual strain relief in grains, dissolution of grain boundary precipitates, and an increase in atomic migration along the grain boundaries. Based on the observed features of the reversed austenite grains and estimation from an existing model, it is suspected that the austenite reversion at 650 and 800 °C undergone diffusional and martensitic shear reversion, respectively.

Hot deformation effect on the kinetics of austenite transformation under continuous cooling conditions

International Nuclear Information System (INIS)

Bernshtejn, M.L.; Zajmovskij, V.A.; Kisteh, N.V.; Samedov, O.V.; Faldin, S.A.

1979-01-01

The effect of hot deformation on the kinetics of austenite transformations in the commercial 4040Kh 40KhN, and 40KhNMA steels on continuous cooling was studied. The transformations were studied using a dilatometer of a special design which permits a specimen to be fixed quickly in holders after hot deformation. It is stated that in hot-deformed austenite the pearlite transformation proceeds at higher temperatures and in a narrower temperature range. Austenite deformation provides an opportunity to obtain a more fine ferrite-pearlite structure and ensures a uniform distribution of a structurally free ferrite in the steel bulk. The effect of hot deformation on the structure of ferrite decomposition products in the 40KhN and 40KhNMA steels is more complicated, which is connected with a substantial change in the kinetics of pearlite and intermediate transformations

Carbide Precipitation in 2.25 Cr-1 Mo Bainitic Steel: Effect of Heating and Isothermal Tempering Conditions

Science.gov (United States)

Dépinoy, Sylvain; Toffolon-Masclet, Caroline; Urvoy, Stéphane; Roubaud, Justine; Marini, Bernard; Roch, François; Kozeschnik, Ernst; Gourgues-Lorenzon, Anne-Françoise

2017-05-01

The effect of the tempering heat treatment, including heating prior to the isothermal step, on carbide precipitation has been determined in a 2.25 Cr-1 Mo bainitic steel for thick-walled applications. The carbides were identified using their amount of metallic elements, morphology, nucleation sites, and diffraction patterns. The evolution of carbide phase fraction, morphology, and composition was investigated using transmission electron microscopy, X-ray diffraction, as well as thermodynamic calculations. Upon heating, retained austenite into the as-quenched material decomposes into ferrite and cementite. M7C3 carbides then nucleate at the interface between the cementite and the matrix, triggering the dissolution of cementite. M2C carbides precipitate separately within the bainitic laths during slow heating. M23C6 carbides precipitate at the interfaces (lath boundaries or prior austenite grain boundaries) and grow by attracting nearby chromium atoms, which results in the dissolution of M7C3 and, depending on the temperature, coarsening, or dissolution of M2C carbides, respectively.

Microstructural study of thermally aged duplex stainless steel deformation and fracture modes

International Nuclear Information System (INIS)

Verhaeghe, B.

1996-01-01

The aim of this work is to study the micro mechanisms of deformation and rupture of an austeno ferritic stainless steel (Z 3 CND 22-10 M) with 33 % of ferrite. It is studied after ageing 1 000 h at 400 deg. C and 8 000 h at 350 deg. C and compared to the 'as received' state. During ageing the ferritic phase undergoes microstructural evolutions which affects its properties. The two ageing treatments lead to roughly the same level of embrittlement. Microstructural characterisation shows that both phases percolate and exhibit orientation relationships close to Kurdjumov-Sachs ones. Mechanical properties of the steel were characterised for different ageing treatments at room temperature and at 320 deg. C. The interface is particularly strong and ensures the load transfer to ferrite even if this phase contains cleavage cracks. Moreover the interface does not oppose slip transmission which is instead controlled by localised glide in the ferritic phase. If activated slip systems of austenite are common with ferrite, slip transmission from austenite to ferrite indeed occurs through the=e interface. If they are not common, dislocations cross-slip back into the austenite. At 320 deg. C cross-slip occurs even far from the interface. Damage starts by nucleation in ferrite of cleavage cracks which propagate between austenite islands. Crack propagation is controlled by stretching of austenite ligaments. The material breaks by ductile tearing of austenite islands when the crack eventually percolates in the ferritic phase. The ductility of the material can be correctly describer using a simple model that takes into account the tearing-off the ductile-phase. (author)

Evaluation of welds on a ferritic-austenitic stainless steel

International Nuclear Information System (INIS)

Pleva, J.; Johansson, B.

1984-01-01

Five different welding methods for the ferritic-austenitic steel 22Cr6Ni3MoN have been evaluated on mill welded heavy wall pipes. The corrosion resistance of the weld joints has been tested both in standard tests and in special environments, related to certain oil and gas wells. The tests were conclusive in that a welding procedure with the addition of sufficient amounts of filler metal should be employed. TIG welds without or with marginal filler addition showed poor resistance to pitting, and to boiling nitric acid. Contents of main alloying elements in ferrite and austenite phases have been measured and causes of corrosion attack in welds are discussed

The effect of cooling rate and austenite grain size on the austenite to ferrite transformation temperature and different ferrite morphologies in microalloyed steels

International Nuclear Information System (INIS)

Esmailian, M.

2010-01-01

The effect of different austenite grain size and different cooling rates on the austenite to ferrite transformation temperature and different ferrite morphologies in one Nb-microalloyed high strength low alloy steel has been investigated. Three different austenite grain sizes were selected and cooled at two different cooling rates for obtaining austenite to ferrite transformation temperature. Moreover, samples with specific austenite grain size have been quenched, partially, for investigation on the microstructural evolution. In order to assess the influence of austenite grain size on the ferrite transformation temperature, a temperature differences method is established and found to be a good way for detection of austenite to ferrite, pearlite and sometimes other ferrite morphologies transformation temperatures. The results obtained in this way show that increasing of austenite grain size and cooling rate has a significant influence on decreasing of the ferrite transformation temperature. Micrographs of different ferrite morphologies show that at high temperatures, where diffusion rates are higher, grain boundary ferrite nucleates. As the temperature is lowered and the driving force for ferrite formation increases, intragranular sites inside the austenite grains become operative as nucleation sites and suppress the grain boundary ferrite growth. The results indicate that increasing the austenite grain size increases the rate and volume fraction of intragranular ferrite in two different cooling rates. Moreover, by increasing of cooling rate, the austenite to ferrite transformation temperature decreases and volume fraction of intragranular ferrite increases.

Hot working effect on austenite transformations in structural steel in continuous cooling

International Nuclear Information System (INIS)

Zajmovskij, V.A.; Kisteh, N.V.; Samedov, O.V.

1979-01-01

Austenite transformations in 40, 40Kh, 40KhN and 40KhNMA steels under hot working at 900 deg C with 20% reduction degree and continuous cooling with 1,7-16 0 /s are investigated. Changing of cooling rate in various ways affects the temperature range of austenite transformation in pearlite and bainite regions. Regulating the cooling rate after hot working one can essentially change the impact strength and steel ductility as a result of high temperature thermomechanical treatment effect

Thermal-aging evaluation of on site aged cast duplex stainless steel

International Nuclear Information System (INIS)

Yamada, Takuyo; Fujii, Katsuhiko; Aoki, Masanori; Arioka, Koji

2013-01-01

In this study, thermal-aging evaluation has been performed using service aged elbow pipe in PWR plant, aged at 320degC for 196,500h. As a result, micro Vickers hardness of ferrite in service material (SCS14A), HV(0.025) was 616∼630. Since micro Vickers hardness of un-aged ferrite phase is about HV(0.025)=300 in commercial SCS14A, the increasing of ferrite hardness during aging was 300. Cr-rich and Fe-rich regions were observed in the ferrite phase using Atom-probe analysis. In addition, Ni, Si and Mo clustering were also observed in the ferrite phase. So the ferrite phase was hardened caused by these micro-structural changes. Micro Vickers hardness of austenite phase, HV(0.025) was 155∼180. Since micro Vickers hardness of un-aged austenite phase is about HV(0.025)=180∼200, and no micro-structural change was observed in the austenite phase, so on change was observed in the austenite phase during aging. To compare the micro Vickers hardness of ferrite in service and accelerated materials using activation energy, Q=100 kJ/mol, the ferrite hardness of in service material was very low rather than predictive line. This seems the activation energy was too conservative. (author)

Understanding aging in containment cooling systems

International Nuclear Information System (INIS)

Lofaro, R.J.

1993-01-01

A study has been performed to assess the effects of aging in nuclear power plant containment cooling systems. Failure records from national databases, as well as plant specific data were reviewed and analyzed to identify aging characteristics for this system. The predominant aging mechanisms were determined, along with the most frequently failed components and their associated failure modes. This paper discusses the aging mechanisms present in the containment spray system and the containment fan cooler system, which are two systems used to provide the containment cooling function. The failure modes, along with the relative frequency of each is also discussed

Low temperature sensitization of austenitic stainless steel: an ageing effect during BWR service

International Nuclear Information System (INIS)

Shah, B.K.; Sinha, A.K.; Rastogi, P.K.; Kulkarni, P.G.

1994-01-01

Sensitization in austenitic stainless steel refers to chromium carbide precipitation at the grain boundaries with concomitant depletion of chromium below 12% near grain boundaries. This makes the material susceptible to either intergranular corrosion (IGC) or intergranular stress corrosion cracking (IGSCC). This effect is predominant whenever austenitic stainless steel is subjected to thermal exposure in the temperature range 723-1073K either during welding or during heat treatment. Low temperature sensitization (LTS) refers to sensitization at temperature below the typical range of sensitization i.e. 723-1073K. A prerequisite for LTS phenomenon is reported to be the presence of chromium carbide nuclei at the grain boundaries which can grow during boiling water reactor service even at a relatively lower temperature of around 560K. LTS can lead to failure of BWR pipe due to IGSCC. The paper reviews the phenomenological and mechanistic aspects of LTS. Studies carried out regarding effect of prior cold work on LTS are reported. Summary of the studies reported in literature to examine the occurrence of LTS during BWR service has also been included. (author). 10 refs., 3 figs

Determination of the concentration dependent diffusion coefficient of nitrogen in expanded austenite

DEFF Research Database (Denmark)

Christiansen, Thomas; Somers, Marcel A. J.

2008-01-01

The concentration dependent diffusion coefficient of nitrogen in expanded austenite was determined from of the rate of retracting nitrogen from thin initially N-saturated coupons. Nitrogen saturated homogeneous foils of expanded austenite were obtained by nitriding AISI 304 and AISI 316 in pure...... in the composition range where nitrogen can be extracted by hydrogen gas at the diffusion temperature. Numerical simulation of the denitriding experiments shows that the thus determined concentration dependent diffusion coefficients are an accurate approximation of the actual diffusivity of nitrogen in expanded...... ammonia at 693 K and 718 K. Denitriding experiments were performed by equilibrating the foils with a successively lower nitrogen activity, as imposed by a gas mixture of ammonia and hydrogen. The concentration dependent diffusion coefficient of nitrogen in expanded austenite was approximated...

Nondestructive characterization of austenitic stainless steels

International Nuclear Information System (INIS)

Jayakumar, T.; Kumar, Anish

2010-01-01

The paper presents an overview of the non-destructive methodologies developed at the authors' laboratory for characterization of various microstructural features, residual stresses and corrosion in austenitic stainless steels. Various non-destructive evaluation (NDE) parameters such as ultrasonic velocity, ultrasonic attenuation, spectral analysis of the ultrasonic signals, magnetic hysteresis parameters and eddy current amplitude have been used for characterization of grain size, precipitation behaviour, texture, recrystallization, thermomechanical processing, degree of sensitization, formation of martensite from metastable austenite, assessment of residual stresses, degree of sensitization and propensity for intergranular corrosion in different austenitic steels. (author)

Behaviour and damage of aged austenitic-ferritic steels: a micro-mechanical approach

International Nuclear Information System (INIS)

Bugat, St.

2000-12-01

The austenitic-ferritic steels are used in the PWR primary cooling system. At the running temperature (320 C), they are submitted to a slow aging, which leads to the embrittlement of the ferritic phase. This embrittlement leads to a decrease of the mechanical properties, in particular of the crack resistance of the austenitic-ferritic steels. The damage and rupture of the austenitic-ferritic steels have been approached at the ENSMP by the works of P. Joly (1992) and of L. Devilliers-Guerville (1998). These works have allowed to reveal a damage heterogeneity which induces a strong dispersion on the ductilities and the toughnesses as well as on the scale effects. Modeling including the damage growth kinetics measured experimentally, have allowed to verify these effects. Nevertheless, they do not consider the two-phase character of the material and do not include a physical model of the cleavage cracks growth which appear in the embrittled ferrite. In this study, is proposed a description of the material allowing to treat these aspects while authorizing the structure calculation. In a first part, the material is studied. The use of the ESBD allows to specify the complex morphology of these steels and crystal orientation relations between the two phases. Moreover, it is shown that the two phases keep the same crystal orientation in the zones, called bicrystals, whose size varies between 500 μm and 1 mm. The study of the sliding lines, coupled to the ESBD, allows to specify too the deformation modes of the two phases. At last, tensile and tensile-compression tests at various deformation range are carried out to characterize the macroscopic mechanical behaviour of these materials. Then, a micro-mechanical modeling of the material behaviour is proposed. This one takes into account the three scales identified at the preceding chapter. The first scale, corresponding to the laths is described as a monocrystal whose behaviour includes both an isotropic and a kinematic strain

Deformation-Induced Dissolution and Precipitation of Nitrides in Austenite and Ferrite of a High-Nitrogen Stainless Steel

Science.gov (United States)

Shabashov, V. A.; Makarov, A. V.; Kozlov, K. A.; Sagaradze, V. V.; Zamatovskii, A. E.; Volkova, E. G.; Luchko, S. N.

2018-02-01

Methods of Mössbauer spectroscopy and electron microscopy have been used to study the effect of the severe plastic deformation by high pressure torsion in Bridgman anvils on the dissolution and precipitation of chromium nitrides in the austenitic and ferritic structure of an Fe71.2Cr22.7Mn1.3N4.8 high-nitrogen steel. It has been found that an alternative process of dynamic aging with the formation of secondary nitrides affects the kinetics of the dissolution of chromium nitrides. The dynamic aging of ferrite is activated with an increase in the deformation temperature from 80 to 573 K.

The effect of thermoplastic treatment regimes on the microplastic strain of nitrogen-containing steel Kh21G10N7MBF

International Nuclear Information System (INIS)

Bannykh, O.A.; Blinov, V.M.; Kostina, M.V.; Grachev, S.V.; Mal'tseva, L.A.

2005-01-01

A study is made into the influence of a percentage reduction during cold rolling and subsequent holdings at heat on development of microplastic deformation when bending sheet specimens of stainless austenitic high-nitrogen steel Kh21G10N7MBF. It is revealed that a maximum value of apparent limit of elasticity (∼1800 MPa) is attained due to plastic deformation by rolling at 20 Deg C with a total percentage reduction of 60 % and subsequent aging at 500 Deg C for 1-4 h [ru

Hydrogen-Induced Delayed Cracking in TRIP-Aided Lean-Alloyed Ferritic-Austenitic Stainless Steels

Directory of Open Access Journals (Sweden)

Suvi Papula

2017-06-01

Full Text Available Susceptibility of three lean-alloyed ferritic-austenitic stainless steels to hydrogen-induced delayed cracking was examined, concentrating on internal hydrogen contained in the materials after production operations. The aim was to study the role of strain-induced austenite to martensite transformation in the delayed cracking susceptibility. According to the conducted deep drawing tests and constant load tensile testing, the studied materials seem not to be particularly susceptible to delayed cracking. Delayed cracks were only occasionally initiated in two of the materials at high local stress levels. However, if a delayed crack initiated in a highly stressed location, strain-induced martensite transformation decreased the crack arrest tendency of the austenite phase in a duplex microstructure. According to electron microscopy examination and electron backscattering diffraction analysis, the fracture mode was predominantly cleavage, and cracks propagated along the body-centered cubic (BCC phases ferrite and α’-martensite. The BCC crystal structure enables fast diffusion of hydrogen to the crack tip area. No delayed cracking was observed in the stainless steel that had high austenite stability. Thus, it can be concluded that the presence of α’-martensite increases the hydrogen-induced cracking susceptibility.

The tensile properties of austenitic steel weld metals

International Nuclear Information System (INIS)

Wood, D.S.

1985-01-01

Elevated temperature tensile data on Mo containing and Mo free austenitic weld metals have been collected from French, German and UK sources and the results analysed. In the as welded condition the proof strength is significantly higher than that of wrought material and Mo containing weld metal is stronger than Mo free weld metal. The differences in UTS values are not so marked, and on average at temperatures above 400 0 the weld metal UTS is slightly lower than that of wrought material. The ductility of weld metal is significantly lower than that for wrought material. 7 refs, 2 tables, 20 figs

The nucleation of austenite in ferritic ductile cast iron

International Nuclear Information System (INIS)

Chou, J.M.; Hon, M.H.; Lee, J.L.

1992-01-01

Austempered ductile cast iron has recently been receiving increasing attention because of its excellent combination of strength and ductility. Since the austenitization process has a significant influence on the mechanical properties of austempered ductile cast iron, several investigations on the nucleation sites of austenite and diffusion paths of carbon from spheroidal graphite have been reported in ferritic ductile cast iron. However, agreement on this subject has not ben reached. The purpose of this paper is to study the preferential nucleation sites of austenite during austenitization at two austenitizing temperatures in ferritic ductile cast iron. An attempt was made to understand the reasons which give rise to preferential austenite nucleation sites. The carbon diffusion paths from spheroidal graphite were also investigated

Self-stabilization of untransformed austenite by hydrostatic pressure via martensitic transformation

International Nuclear Information System (INIS)

Nakada, Nobuo; Ishibashi, Yuji; Tsuchiyama, Toshihiro; Takaki, Setsuo

2016-01-01

For improving the understanding of austenite stability in steel, hydrostatic pressure in untransformed austenite that is generated via martensitic transformation was evaluated from macro- and micro-viewpoints, and its effect on austenite stability was investigated in a Fe-27%Ni austenitic alloy. X-ray diffractometry revealed that the lattice parameter of untransformed austenite is continuously decreased via martensitic transformation only when martensite becomes the dominant phase in the microstructure. This suggests that the untransformed austenite is isotropically compressed by the surrounding martensite grains, i.e., hydrostatic pressure is generated in untransformed austenite dynamically at a later stage of martensitic transformation. On the other hand, microscopic strain mapping using the electron backscatter diffraction technique indicated that a finer untransformed austenite grain has a higher hydrostatic pressure, while a high density of dislocations is also introduced in untransformed austenite near the austenite/martensite interface because of lattice-invariant shear characterized by non-thermoelastic martensitic transformation. Furthermore, it was experimentally demonstrated that the hydrostatic pressure stabilizes the untransformed austenite; however, the austenite stabilization effect alone is not large enough to fully explain a large gap between martensite start and finish temperatures in steel.

Simulation of competitive Cu precipitation in steel during non-isothermal aging

International Nuclear Information System (INIS)

Yang, J.B.; Yamashita, T.; Sano, N.; Enomoto, M.

2008-01-01

A numerical model has been developed to simulate Cu precipitation in dilute bcc Fe-Cu alloys during non-isothermal aging taking into account competitive nucleation at grain boundaries, dislocations and in the matrix, and structural transformation of Cu particles that occurs during growth. The temporal evolution of number density, mean particle size and size distribution during continuous cooling is simulated and is compared with experimental observations under transmission electron microscope and three-dimensional atom probe field ion microscope. With decreasing temperature the growth and coarsening rates diminishes rapidly whereas nucleation continues to occur down to lower temperatures due to the decrease in the activation energy of nucleation and thus, distributions of fine particles can be obtained relatively easily after cooling. Precipitation and dissolution during continuous heating are simulated and are compared with experimental observations in the literature

Plastic deformation and fracture behaviors of nitrogen-alloyed austenitic stainless steels

International Nuclear Information System (INIS)

Wang Songtao; Yang Ke; Shan Yiyin; Li Laifeng

2008-01-01

The plastic deformation and fracture behaviors of two nitrogen-alloyed austenitic stainless steels, 316LN and a high nitrogen steel (Fe-Cr-Mn-0.66% N), were investigated by tensile test and Charpy impact test in a temperature range from 77 to 293 K. The Fe-Cr-Mn-N steel showed ductile-to-brittle transition (DBT) behavior, but not for the 316LN steel. X-ray diffraction (XRD) confirmed that the strain-induced martensite occurred in the 316LN steel, but no such transformation in the Fe-Cr-Mn-N steel. Tensile tests showed that the temperature dependences of the yield strength for the two steels were almost the same. The ultimate tensile strength of the Fe-Cr-Mn-N steel displayed less significant temperature dependence than that of the 316LN steel. The strain-hardening exponent increased for the 316LN steel, but decreased for the Fe-Cr-Mn-N steel, with decreasing temperature. Based on the experimental results and the analyses, a modified scheme was proposed to explain the fracture behaviors of austenitic stainless steels

Effect of isothermal aging on the microstructure and properties of as-cast Mg-Gd-Y-Zr alloy

Energy Technology Data Exchange (ETDEWEB)

Liang Shuquan [School of Material Science and Engineering, Central South University, Changsha 410083 (China); Guan Dikai, E-mail: gdk199@126.com [School of Material Science and Engineering, Central South University, Changsha 410083 (China); Tan Xiaoping; Chen Liang; Tang Yan [School of Material Science and Engineering, Central South University, Changsha 410083 (China)

2011-01-25

Research highlights: {yields} The improvement of the hardness of the peak-aged alloys at 200 deg. C, 225 deg. C and 250 deg. C is mainly ascribed to the presence of the {beta}' phase. {yields} The alloy peak-aged at 200 deg. C displays the highest hardness owing to the existence of a great many {beta}' precipitates with a quite small size and uniform distribution in the matrix. {yields} The corrosion rates of the peak-aged samples increase as the isothermal aging temperature rise. The {beta}' precipitates are larger and appear to be more active as galvanic cathodes for the alloy peak-aged at the higher aging temperatures. {yields} Therefore, in our paper, optimal mechanical properties and good corrosion resistance in 5% NaCl solutions are obtained simultaneously when the alloy is aged at 200 deg. C for 120 h. - Abstract: The microstructure of Mg-7Gd-3Y-0.4Zr (wt.%) alloy during isothermal aging at 200 deg. C, 225 deg. C and 250 deg. C was investigated using optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray diffraction. The mechanical properties of the peak-aged materials were evaluated by using Vickers hardness values, and their corrosion resistance was studied by using immersion tests, salt spray tests and electrochemical measurements in 5% NaCl solutions (wt.%). The results show that owing to the existence of a great many {beta}' precipitates with a quite small size and uniform distribution in the matrix, optimal mechanical properties and good corrosion resistance in 5% NaCl solutions are obtained when the alloy is aged at 200 deg. C for 120 h. The potentiodynamic polarization curves show that the corrosion current densities of the cathodic hydrogen evolution on the alloy peak-aged at 200 deg. C is lower than those for specimens of the alloy aged at 225 deg. C and 250 deg. C, which agrees fairly well with the microstructures of the alloys.

Expanded austenite, crystallography and residual stress

DEFF Research Database (Denmark)

Christiansen, Thomas; Hummelshøj, Thomas Strabo; Somers, Marcel A. J.

2010-01-01

The identity of expanded austenite as developing during low temperature nitriding and/or carburising of austenitic stainless steel has been under debate since the very first observation of this phase. In the present article, recent results obtained with (a) homogeneous samples of various uniform ...

Expanded austenite; crystallography and residual stress

DEFF Research Database (Denmark)

Christiansen, Thomas; Hummelshøj, Thomas Strabo; Somers, Marcel A. J.

2009-01-01

The identity of expanded austenite as developing during low temperature nitriding and/or carburizing of austenitic stainless steel has been under debate since the very first observation of this phase. In the present article recent results obtained with i) homogeneous samples of various uniform co...

Some data of second sequence non standard austenitic ingot, A2

International Nuclear Information System (INIS)

Nurdin Effendi; Aziz K Jahja; Bandriana; Wisnu Ari Adi

2012-01-01

Synthesis of second sequence austenite stainless steel named A2 using extracted minerals from Indonesian mines has been carried out. The starting materials for austenite alloy consist of granular ferro scrap, nickel, ferro-chrome, ferro-manganese, and ferro-silicon. The second sequence composition differs from the former first sequence. This A2 sequence contained more nickel, meanwhile titanium element had not been added explicitly to it, and just been found from raw materials contents or impurities, as well as carbon content in the alloy. However before the actual alloying work started, the first important step was to carry out the determination of the fractional amount of each starting material necessary to form an austenite stainless steel alloy as specified. Once the component fraction of each base alloy-element was determined, the raw materials are weighed on the mini-balance. After the fractional quantities of each constituent have been computed, an appropriate amount of these base materials are weighed separately on the micro scale. The raw materials were then placed in the induction foundry furnace, which was operated by an electromagnetic inductive-thermal system. The foundry furnace system performs the stirring of the molten materials automatically. The homogenized molten metals were poured down into sand casting prepared in advance. Some of the austenite stainless steel were normalized at 600°C for 6 hours. The average density is 7.8 g cm -1 and the average hardness value of 'normalized' austenite stainless-steels is in the range of 460 on the Vickers scale. The microstructure observation concludes that an extensive portion of the sample's structure is dendritic and the surface turns out to be homogenous. X-ray diffraction analysis shows that the material belongs to the fcc crystallographic system, which fits in with the austenite class of the alloy. The experimental fractional elemental composition data acquired by OES method turn out to

Fracture of Fe--Cr--Mn austenitic steel

International Nuclear Information System (INIS)

Caskey, G.R. Jr.

1979-01-01

Tensile tests of Tenelon (U.S. Steel), a nitrogen-strengthened iron-base alloy containing 18% chromium and 15% manganese, demonsterated that cleavage fracture can occur in some austenitic steels and is promoted by the presence of hydrogen. Tensile failure of Tenelon at 78 0 K occurred with no detectable necking at low strain levels. The fracture surface contained cleavage facets that lay along coherent twin boundaries oriented transversely to the tensile axis. Charging gaseous hydrogen at 679 MPa pressure and 650 0 K had no significant effect on the mechanical behavior or fracture mode at 78 0 K, but raised the ductile-to-brittle transition temperature from less than 200 0 K to about 250 0 K

Cryogenic deformation microstructures of 32Mn-7Cr-1Mo-0.3N austenitic steels

International Nuclear Information System (INIS)

Fu Ruidong; Qiu Liang; Wang Tiansheng; Wang Cunyu; Zheng Yangzeng

2005-01-01

The cryogenic deformation microstructures of impact and tensile specimens of 32Mn-7Cr-1Mo-0.3N austenitic steel were investigated using light microscopy and transmission electron microscopy. The results show that the deformation microstructures of the impact specimens are mainly composed of stacking faults, network dislocation, slip bands, and a few mechanical twins and ε-martensite. These microstructures cross with each other in a crystal angle. The deformation microstructures of the tensile specimens consist only of massive slip bands, in which a few mechanical twins and ε-martenite are located. Because of the larger plastic deformation the slip band traces become bent. All the deformation microstructures are formed on the {111} planes and along the orientation

Effect of austempering temperature and time on mechanical properties of SAE 9260 steel

Science.gov (United States)

Dalwatkar, Ranjit; Prabhu, N.; Singh, R. K. P.

2018-04-01

This work describes the effect of austempering heat treatment on microstrcuture and mechanical properties of SAE 9260 steel. Steel samples, austenitized at 900 °C for one hour, were isothermally heat treated in the temperature range 300,325 and 350 °C for different times. Microstructural characterization was carried out using optical and scanning electron microscopes. The microstructure of the austempered samples consisted of bainitic ferrite and retained austenite. The volume fraction of retained austenite was determined using X-ray diffraction. Isothermal heat treatment at 350 °C for 20 min, resulted in a retained austenite content of around 38% in the microstructure. Increase in isothermal transformation temperature led to an increase in the fraction of retained austenite. Also, good combination of strength and ductility was obtained in the samples with increased amounts of retained austenite.

Diagnostic experimental results on the hydrogen embrittlement of austenitic steels

Energy Technology Data Exchange (ETDEWEB)

Gavriljuk, V.G.; Shivanyuk, V.N.; Foct, J

2003-03-14

Three main available hypotheses of hydrogen embrittlement are analysed in relation to austenitic steels based on the studies of the hydrogen effect on the interatomic bonds, phase transformations and microplastic behaviour. It is shown that hydrogen increases the concentration of free electrons, i.e. enhances the metallic character of atomic interactions, although such a decrease in the interatomic bonding cannot be a reason for brittleness and rather assists an increased plasticity. The hypothesis of the critical role of the hydrogen-induced {epsilon} martensite was tested in the experiment with the hydrogen-charged Si-containing austenitic steel. Both the fraction of the {epsilon} martensite and resistance to hydrogen embrittlement were increased due to Si alloying, which is at variance with the pseudo-hydride hypothesis. The hydrogen-caused early start of the microplastic deformation and an increased mobility of dislocations, which are usually not observed in the common mechanical tests, are revealed by the measurements of the strain-dependent internal friction, which is consistent with the hypothesis of the hydrogen-enhanced localised plasticity. An influence of alloying elements on the enthalpy E{sub H} of hydrogen migration in austenitic steels is studied using the temperature-dependent internal friction and a correlation is found between the values of E{sub H} and hydrogen-caused decrease in plasticity. A mechanism for the transition from the hydrogen-caused microplasticity to the apparent macrobrittle fracture is proposed based on the similarity of the fracture of hydrogenated austenitic steels to that of high nitrogen steels.

Adsorption isotherm studies of chromium (VI) from aqueous solutions using sol-gel hydrotalcite-like compounds

Energy Technology Data Exchange (ETDEWEB)

Ramos-Ramirez, Esthela, E-mail: ramosre@quijote.ugto.mx [Centro de Investigaciones en Quimica Inorganica de la Universidad de Guanajuato, Noria Alta s/n, Col. Noria Alta, C.P. 36050, Guanajuato, Gto. (Mexico); Gutierrez Ortega, Norma L.; Conteras Soto, Cesar A. [Centro de Investigaciones en Quimica Inorganica de la Universidad de Guanajuato, Noria Alta s/n, Col. Noria Alta, C.P. 36050, Guanajuato, Gto. (Mexico); Instituto Nacional de Investigaciones Nucleares, Carretera Mexico-Toluca s/n, km 36.5, La Marquesa, Coyoacan Mexico, C.P. 52750 (Mexico); Olguin Gutierrez, Maria T. [Instituto Nacional de Investigaciones Nucleares, Carretera Mexico-Toluca s/n, km 36.5, La Marquesa, Coyoacan Mexico, C.P. 52750 (Mexico)

2009-12-30

In under-developed countries, industries such as paint and pigment manufacturing, leather tanning, chrome plating and textile processing, usually discharge effluents containing Cr(VI) and Cr(III) into municipal sanitary sewers. It has been reported that Cr(VI) acts as a powerful epithelial irritant and as a human carcinogen. In the present work, hydrotalcite-like compounds with a Mg/Al ratio = 2 were synthesized by the sol-gel method. The hydrotalcite-like compounds and their corresponding thermally treated products were characterized by powder X-ray diffraction, infrared spectroscopy and N{sub 2} adsorption. The hydrotalcite-like compounds and the heated solids were used as adsorbents for Cr(VI) in aqueous solutions. Adsorption isotherm studies of Cr(VI) from aqueous solution are described. The adsorbent capacity was determined using the Langmuir, Freundlich and Dubinin-Radushkevich adsorption isotherm models. The Cr(VI) adsorption isotherm data fit best to the Langmuir isotherm model. The maximum Cr(VI) uptake by hydrotalcite and the heated solids was determined using the Langmuir equation and was found to range between 26 and 29 mg Cr(VI)/g adsorbent.

Adsorption isotherm studies of chromium (VI) from aqueous solutions using sol-gel hydrotalcite-like compounds

International Nuclear Information System (INIS)

Ramos-Ramirez, Esthela; Gutierrez Ortega, Norma L.; Conteras Soto, Cesar A.; Olguin Gutierrez, Maria T.

2009-01-01

In under-developed countries, industries such as paint and pigment manufacturing, leather tanning, chrome plating and textile processing, usually discharge effluents containing Cr(VI) and Cr(III) into municipal sanitary sewers. It has been reported that Cr(VI) acts as a powerful epithelial irritant and as a human carcinogen. In the present work, hydrotalcite-like compounds with a Mg/Al ratio = 2 were synthesized by the sol-gel method. The hydrotalcite-like compounds and their corresponding thermally treated products were characterized by powder X-ray diffraction, infrared spectroscopy and N 2 adsorption. The hydrotalcite-like compounds and the heated solids were used as adsorbents for Cr(VI) in aqueous solutions. Adsorption isotherm studies of Cr(VI) from aqueous solution are described. The adsorbent capacity was determined using the Langmuir, Freundlich and Dubinin-Radushkevich adsorption isotherm models. The Cr(VI) adsorption isotherm data fit best to the Langmuir isotherm model. The maximum Cr(VI) uptake by hydrotalcite and the heated solids was determined using the Langmuir equation and was found to range between 26 and 29 mg Cr(VI)/g adsorbent.

Adsorption isotherm studies of chromium (VI) from aqueous solutions using sol-gel hydrotalcite-like compounds.

Science.gov (United States)

Ramos-Ramírez, Esthela; Ortega, Norma L Gutiérrez; Soto, Cesar A Contreras; Gutiérrez, Maria T Olguín

2009-12-30

In under-developed countries, industries such as paint and pigment manufacturing, leather tanning, chrome plating and textile processing, usually discharge effluents containing Cr(VI) and Cr(III) into municipal sanitary sewers. It has been reported that Cr(VI) acts as a powerful epithelial irritant and as a human carcinogen. In the present work, hydrotalcite-like compounds with a Mg/Al ratio=2 were synthesized by the sol-gel method. The hydrotalcite-like compounds and their corresponding thermally treated products were characterized by powder X-ray diffraction, infrared spectroscopy and N(2) adsorption. The hydrotalcite-like compounds and the heated solids were used as adsorbents for Cr(VI) in aqueous solutions. Adsorption isotherm studies of Cr(VI) from aqueous solution are described. The adsorbent capacity was determined using the Langmuir, Freundlich and Dubinin-Radushkevich adsorption isotherm models. The Cr(VI) adsorption isotherm data fit best to the Langmuir isotherm model. The maximum Cr(VI) uptake by hydrotalcite and the heated solids was determined using the Langmuir equation and was found to range between 26 and 29 mg Cr(VI)/g adsorbent.

Effects of Ce Addition and Isothermal Aging on the Elevated Temperature Tensile Properties of Mechanically Alloyed Al-Ti Alloys

Energy Technology Data Exchange (ETDEWEB)

Kim, JunKi; Oh, YoungMin; Kim, YongDeog; Kim, SeonJin [Hanyang Univ., Seoul (Korea, Republic of); Kim, ByungChul [KOREA ATOMIC RESEARCH INSTITUTE, TAEJON (Korea, Republic of)

1997-05-01

The room and elevated temperature tensile strength of mechanically alloyed Al-8wt%. Ti alloy increased by substituting Ce for Ti up to 25at.%. However, further substitution of Ce for Ti decreased the tensile strength. It was considered to be due to the decrease of volume fraction of Ce contained dispersoid. In the meantime, the decrease of tensile strength due to the isothermal aging was effectively reduced by the addition of Ce at 400 deg. C but not 510 deg. C. The activation energies for the deformation of Al-80wt.%(Ti+Ce)alloys measured at the temperature between 300 deg. C{approx}510 deg. C were about 1.3{approx}1.9 times higher than that for pure Al self-diffusion(142 kJ/mole). Thus, it was considered that the elevated temperature deformation of Al-8wt.%(Ti+Ce)alloys was governed by Orowan mechanism (author). 9 refs. 6 figs.

Nanostructured Bainite-Austenite Steel for Armours Construction

Directory of Open Access Journals (Sweden)

Burian W.

2014-10-01

Full Text Available Nanostructured bainite-austenite steels are applied in the armours construction due to their excellent combination of strength and ductility which enables to lower the armour weight and to improve the protection efficiency. Mechanical properties of the bainite-austenite steels can be controlled in the wide range by chemical composition and heat treatment. In the paper the results of investigation comprising measuring of quasi - static mechanical properties, dynamic yield stress and firing tests of bainite-austenite steel NANOS-BA® are presented. Reported results show that the investigated bainite-austenite steel can be used for constructing add-on armour and that the armour fulfils requirements of protection level 2 of STANAG 4569. Obtained reduction in weight of the tested NANOS-BA® plates in comparison with the present solutions is about 30%.

Impact Strength of Austenitic and Ferritic-Austenitic Cr-Ni Stainless Cast Steel in -40 and +20°C Temperature

Directory of Open Access Journals (Sweden)

Kalandyk B.

2014-10-01

Full Text Available Studies described in this paper relate to common grades of cast corrosion resistant Cr-Ni steel with different matrix. The test materials were subjected to heat treatment, which consisted in the solution annealing at 1060°C followed by cooling in water. The conducted investigations, besides the microstructural characteristics of selected cast steel grades, included the evaluation of hardness, toughness (at a temperature of -40 and +20oC and type of fracture obtained after breaking the specimens on a Charpy impact testing machine. Based on the results of the measured volume fraction of ferrite, it has been found that the content of this phase in cast austenitic steel is 1.9%, while in the two-phase ferritic-austenitic grades it ranges from 50 to 58%. It has been demonstrated that within the scope of conducted studies, the cast steel of an austenitic structure is characterised by higher impact strength than the two-phase ferritic-austenitic (F-A grade. The changing appearance of the fractures of the specimens reflected the impact strength values obtained in the tested materials. Fractures of the cast austenitic Cr-Ni steel obtained in these studies were of a ductile character, while fractures of the cast ferritic-austenitic grade were mostly of a mixed character with the predominance of brittle phase and well visible cleavage planes.

The difference in thermal and mechanical stabilities of austenite between carbon- and nitrogen-added metastable austenitic stainless steels

International Nuclear Information System (INIS)

Masumura, Takuro; Nakada, Nobuo; Tsuchiyama, Toshihiro; Takaki, Setsuo; Koyano, Tamotsu; Adachi, Kazuhiko

2015-01-01

In order to evaluate the effects of carbon and nitrogen addition on the stability of austenite, athermal and deformation-induced α′-martensitic transformation behaviors were investigated using type 304-metastable austenitic stainless steels containing 0.1 mass% carbon or nitrogen. The difference in the development of the deformation microstructure in particular is discussed in terms of the stacking-fault energy (SFE). Since carbon-added steel has a lower SFE than that of nitrogen-added steel, deformation twins and ε-martensite were preferentially formed in the carbon-added steel, whereas a dislocation cell structure developed in the nitrogen-added steel. Crystallographic analysis using the electron backscatter diffraction method revealed that the difference in the deformation microstructure has a significant influence on the growth behavior of deformation-induced α′-martensite, that is, the interface of the deformation twins and ε-martensite suppresses the growth of α′-martensite, whereas dislocation cell boundaries are not effective. As a result, the mechanical stability of carbon-added steel is slightly higher than that of nitrogen-added steel, although the thermal stabilization effect of carbon is much lower than that of nitrogen

General and Localized corrosion of Austenitic and Borated Stainless Steels in Simulated Concentrated Ground Waters

International Nuclear Information System (INIS)

Fix, D.; Estill, J.; Wong, L.; Rebak, R.

2004-01-01

Boron containing stainless steels are used in the nuclear industry for applications such as spent fuel storage, control rods and shielding. It was of interest to compare the corrosion resistance of three borated stainless steels with standard austenitic alloy materials such as type 304 and 316 stainless steels. Tests were conducted in three simulated concentrated ground waters at 90 C. Results show that the borated stainless were less resistant to corrosion than the witness austenitic materials. An acidic concentrated ground water was more aggressive than an alkaline concentrated ground water

Effects of niobium additions on the structure, depth, and austenite grain size of the case of carburized 0.07% C steels

Science.gov (United States)

Islam, M. A.; Bepari, M. M. A.

1996-10-01

Carbon (0.07%) steel samples containing about 0.04% Nb singly and in combination with nitrogen were carburized in a natural Titas gas atmosphere at a temperature of 1223 K (950 °C) and a pressure of about 0.10 MPa for 1/2 to 4 h, followed by slow cooling in the furnace. Their microstructures were studied by optical microscopy. The austenite grain size of the case and the case depths were determined on baseline samples of low-carbon steels and also on niobium and (Nb + N) microalloyed steel samples. It was found that, when compared to the baseline steel, niobium alone or in combination with nitrogen decreased the thickness of cementite network near the surface of the carburized case of the steels. However, niobium in combination with nitrogen was more effective than niobium in reducing the thickness of cementite network. Niobium with or without nitrogen inhibited the formation of Widmanstätten cementite plates at grain boundaries and within the grains near the surface in the hypereutectoid zone of the case. It was also revealed that, when compared to the baseline steel, niobium decreased the case depth of the carburized steels, but that niobium with nitrogen is more effective than niobium alone in reducing the case depth. Niobium as niobium carbide (NbC) and niobium in the presence of nitrogen as niobium carbonitride, [Nb(C,N)] particles refined the austenite grain size of the carburized case, but Nb(C,N) was more effective than NbC in inhibiting austenite grain growth.

Nitrogen-containing steels and thermomechanical treatment

International Nuclear Information System (INIS)

Kaputkina, L.; Prokoshkina, V.G.; Svyazhin, G.

2004-01-01

The strengthening of nitrogen-containing corrosion-resistant steels resulting from alloying and thermomechanical treatment have been investigated using X-ray diffraction analysis, light microscopy, hardness measurements and tensile testing. Combined data have been obtained for nitrogen interaction with alloying elements , peculiarities of deformed structure and short-range of nitrogen-containing steels of various structural classes. The higher nitrogen and total alloying element contents, the higher deformation strengthening. Prospects of use the steels with not high nitrogen content and methods of their thermomechanical strengthening are shown. High temperature thermomechanical treatment (HTMT) is very effective for obtaining high and thermally stable constructional strength of nitrogen-containing steels of all classes. The HTMT is most effective if used in a combination with dispersion hardening for aging steels or in the case of mechanically unstable austenitic steels. (author)

Low-activation Mn-Cr austenitic stainless steel with further reduced content of long-lived radioactive elements

Energy Technology Data Exchange (ETDEWEB)

Onozuka, M.; Saida, T.; Hirai, S. [Mitsubishi Heavy Ind. Ltd., Yokohama (Japan); Kusuhashi, M.; Sato, I.; Hatakeyama, T. [The Japan Steel Works Ltd., Chatsu-machi 4, Muroran 051-8505 (Japan)

1998-06-01

Low-activation austenitic stainless steel based on Mn-Cr non-magnetic steels has been developed. The alloying elements of long-life activation, such as Ni, Mo and Co, were eliminated and substituted with Mn along with an addition of N. A Mn-Cr austenitic stainless steel, 24.5Mn-13.5Cr-0.02C-0.2N, has been developed successfully. Examined material properties, including mechanical, thermal and magnetic properties, as well as weldability and characteristics of corrosion resistance, are presented. It was found that the alloy has excellent material properties virtually equivalent to those of 316SS. In this study, the applicability of the Schaeffler, DeLong and Hull constitution diagrams for the stainless steels with low Ni and high Mn contents was also examined. The boundary conditions distinguishing the single austenite phase from the others have been identified for the Mn-Cr steels. (orig.) 22 refs.

Low-activation Mn Cr austenitic stainless steel with further reduced content of long-lived radioactive elements

Science.gov (United States)

Onozuka, Masanori; Saida, Tomikane; Hirai, Shouzou; Kusuhashi, Mikio; Sato, Ikuo; Hatakeyama, Tsuyoshi

1998-06-01

Low-activation austenitic stainless steel based on Mn-Cr non-magnetic steels has been developed. The alloying elements of long-life activation, such as Ni, Mo and Co, were eliminated and substituted with Mn along with an addition of N. A Mn-Cr austenitic stainless steel, 24.5Mn-13.5Cr-0.02C-0.2N, has been developed successfully. Examined material properties, including mechanical, thermal and magnetic properties, as well as weldability and characteristics of corrosion resistance, are presented. It was found that the alloy has excellent material properties virtually equivalent to those of 316SS. In this study, the applicability of the Schaeffler, DeLong and Hull constitution diagrams for the stainless steels with low Ni and high Mn contents was also examined. The boundary conditions distinguishing the single austenite phase from the others have been identified for the Mn-Cr steels.

Catalytic properties of Thallium-containing mesoporous silicas

Directory of Open Access Journals (Sweden)

A. Baradji

2017-02-01

Full Text Available The benzylation of benzene by benzyl chloride over a series of Thallium-containing mesoporous silicas with different Tl contents has been investigated. These materials (Tl-HMS-n have been characterized by chemical analysis, N2 adsorption/desorption isotherm and X-ray diffraction (XRD. The mesoporous Thallium-containing materials showed both high activity and high selectivity for the benzylation of benzene. More interesting is the observation that these catalysts are always active and selective for large molecules like naphthenic compounds such as methoxynaphthalene.

Lattice expansion of carbon-stabilized expanded austenite

DEFF Research Database (Denmark)

Hummelshøj, Thomas Strabo; Christiansen, Thomas; Somers, Marcel A. J.

2010-01-01

The lattice parameter of expanded austenite was determined as a function of the content of interstitially dissolved carbon in homogeneous, carburized thin stainless steel foils. For the first time this expansion of the face-centered cubic lattice is determined on unstrained austenite. It is found...

Study on isothermal precision forging process of rare earth intensifying magnesium alloy

International Nuclear Information System (INIS)

Shan, Debin; Xu, Wenchen; Han, Xiuzhu; Huang, Xiaolei

2012-01-01

A three dimensional rigid-plastic finite element model is established to simulate the isothermal precision forging process of the magnesium alloy bracket based on DEFORM 3D in order to analyze the material flow rule and determine the forging process scheme. Some problems such as underfilling and too large forging pressure are predicted and resolved through optimizing the shapes of the billet successfully. Compared to the initial microstructure, the isothermal-forged microstructure of the alloy refines obviously and amounts of secondary phases precipitate on the matrix during isothermal forging process. In subsequent ageing process, large quantities of secondary phases precipitate from α-Mg matrix with increasing ageing time. The optimal comprehensive mechanical properties of the alloy have been obtained after aged at 473 K, 63 h with the ultimate tensile strength, tensile yield strength and elongation 380 MPa, 243 MPa and 4.07% respectively, which shows good potential for application of isothermal forging process of rare earth intensifying magnesium alloy.

Austenitic stainless steel weld inspection

International Nuclear Information System (INIS)

Mech, S.J.; Emmons, J.S.; Michaels, T.E.

1978-01-01

Analytical techniques applied to ultrasonic waveforms obtained from inspection of austenitic stainless steel welds are described. Experimental results obtained from a variety of geometric and defect reflectors are presented. Specifically, frequency analyses parameters, such as simple moments of the power spectrum, cross-correlation techniques, and adaptive learning network analysis, all represent improvements over conventional time domain analysis of ultrasonic waveforms. Results for each of these methods are presented, and the overall inspection difficulties of austenitic stainless steel welds are discussed

Defining the Post-Machined Sub-surface in Austenitic Stainless Steels

Science.gov (United States)

Srinivasan, N.; Sunil Kumar, B.; Kain, V.; Birbilis, N.; Joshi, S. S.; Sivaprasad, P. V.; Chai, G.; Durgaprasad, A.; Bhattacharya, S.; Samajdar, I.

2018-06-01

Austenitic stainless steels grades, with differences in chemistry, stacking fault energy, and thermal conductivity, were subjected to vertical milling. Anodic potentiodynamic polarization was able to differentiate (with machining speed/strain rate) between different post-machined sub-surfaces in SS 316L and Alloy A (a Cu containing austenitic stainless steel: Sanicroe 28™), but not in SS 304L. However, such differences (in the post-machined sub-surfaces) were revealed in surface roughness, sub-surface residual stresses and misorientations, and in the relative presence of sub-surface Cr2O3 films. It was shown, quantitatively, that higher machining speed reduced surface roughness and also reduced the effective depths of the affected sub-surface layers. A qualitative explanation on the sub-surface microstructural developments was provided based on the temperature-dependent thermal conductivity values. The results herein represent a mechanistic understanding to rationalize the corrosion performance of widely adopted engineering alloys.

Defining the Post-Machined Sub-surface in Austenitic Stainless Steels

Science.gov (United States)

Srinivasan, N.; Sunil Kumar, B.; Kain, V.; Birbilis, N.; Joshi, S. S.; Sivaprasad, P. V.; Chai, G.; Durgaprasad, A.; Bhattacharya, S.; Samajdar, I.

2018-04-01

Austenitic stainless steels grades, with differences in chemistry, stacking fault energy, and thermal conductivity, were subjected to vertical milling. Anodic potentiodynamic polarization was able to differentiate (with machining speed/strain rate) between different post-machined sub-surfaces in SS 316L and Alloy A (a Cu containing austenitic stainless steel: Sanicroe 28™), but not in SS 304L. However, such differences (in the post-machined sub-surfaces) were revealed in surface roughness, sub-surface residual stresses and misorientations, and in the relative presence of sub-surface Cr2O3 films. It was shown, quantitatively, that higher machining speed reduced surface roughness and also reduced the effective depths of the affected sub-surface layers. A qualitative explanation on the sub-surface microstructural developments was provided based on the temperature-dependent thermal conductivity values. The results herein represent a mechanistic understanding to rationalize the corrosion performance of widely adopted engineering alloys.

Investigation on the crystallography of the transformation products of reverted austenite in intercritically reheated coarse grained heat affected zone

International Nuclear Information System (INIS)

You, Yang; Shang, Chengjia; Chen, Liang; Subramanian, Sundaresa

2013-01-01

Highlights: ► Area of reverted austenite is traced out by crystallographic information. ► Bainite and martensite regions were confirmed within it. ► The martensite region is considered as the blocky MA particles. ► Martensite region has high deformation to initiate fracture. ► More uniform transformation of the reverted austenite is good for toughness. -- Abstract: In present study the intercritically reheated coarse grained heat affected zone (ICCGHAZ) showing the worst impact toughness in the heat affected zone of multi-pass welding was simulated by Gleeble-1500, and its microstructure was investigated in detail by means of scanning electron microscope (SEM) and electron backscattering diffraction (EBSD). With the crystallographic information from EBSD scanning the area of a single reverted austenite grain which formed during the thermal cycles of second pass simulation was traced out. Within it two regions with different characteristic both in morphology and crystallography were found out, showing an un-uniform transformation of the reverted austenite. The region I is a bainitic region containing larger bainitic ferrite grains, while the region II is made up of several clusters containing tiny grains. Based on the crystallographic information each cluster was determined as martensite island thereby should be considered as blocky Martensite/Austenite constituent (M/A), which is hard phase and harmful for toughness. Analysis on the level of deformation shows that the region II is much higher deformed than the region I, indicating there is high stress concentration within the region II. The possible influence of the region I and the region II on fracture is discussed under the early proposed M/A’s fracture-initiating mechanisms. It suggests that the main cause of the toughness reduction is the un-uniform transformation of the reverted austenite, and the toughness performance of the ICCGHAZ could be improved if the transformation of the reverted

Effect of Morphological Differences on the Cold Formability of an Isothermally Heat-Treated Advanced High-Strength Steel

Science.gov (United States)

Weißensteiner, Irmgard; Suppan, Clemens; Hebesberger, Thomas; Winkelhofer, Florian; Clemens, Helmut; Maier-Kiener, Verena

2018-04-01

Steel sheets of Fe-0.2C-2Mn-0.2Si-0.03Ti-0.003B (m%) for the automotive industry were isothermally heat-treated, comprising austenitizing and subsequent isothermal annealing at temperatures between 300°C and 500°C. As a consequence, microstructures ranging from granular bainite over lower bainite to auto-tempered and untempered martensite were obtained. In tensile, hole expansion and bending tests, the performances in different forming conditions were compared and the changes of microstructure and texture were studied by complementary electron backscatter diffraction (EBSD) analyses. Samples with granular bainitic microstructures exhibited high total elongations but lower hole expansion ratios; in subsequent EBSD and texture analyses, evidence for inhomogeneous deformation was found. In contrast, the lath-like bainitic/martensitic microstructure showed higher strength and lower elongation to fracture. This results in a reduced bendability, but also in a high tolerance against damage induced by the shearing of edges, and, thus, allows homogeneous deformation to higher strains in the hole expansion test.

(AJST) ADSORPTION ISOTHERME DE L'ACIDE ACÉTIQUE PAR ...

African Journals Online (AJOL)

opiyo

ont été étudiées à partir des isothermes d'adsorption de l'acide acétique à 30° et ... has resulted in the determination of the two types of adsorption isotherms : the Freundlich and .... zinc 60 % pendant 6 heures n'améliore pas suffisamment le.

Solidification behavior of austenitic stainless steel filler metals

International Nuclear Information System (INIS)

David, S.A.; Goodwin, G.M.; Braski, D.N.

1980-02-01

Thermal analysis and interrupted solidification experiments on selected austenitic stainless steel filler metals provided an understanding of the solidification behavior of austenitic stainless steel welds. The sequences of phase separations found were for type 308 stainless steel filler metal, L + L + delta + L + delta + γ → γ + delta, and for type 310 stainless steel filler metal, L → L + γ → γ. In type 308 stainless steel filler metal, ferrite at room temperature was identified as either the untransformed primary delta-ferrite formed during the initial stages of solidification or the residual ferrite after Widmanstaetten austenite precipitation. Microprobe and scanning transmission electron microscope microanalyses revealed that solute extensively redistributes during the transformation of primary delta-ferrite to austenite, leading to enrichment and stabilization of ferrite by chromium. The type 310 stainless steel filler metal investigated solidifies by the primary crystallization of austenite, with the transformation going to completion at the solidus temperature. In our samples residual ferrite resulting from solute segregation was absent at the intercellular or interdendritic regions

Low-temperature creep of austenitic stainless steels

Science.gov (United States)

Reed, R. P.; Walsh, R. P.

2017-09-01

Plastic deformation under constant load (creep) in austenitic stainless steels has been measured at temperatures ranging from 4 K to room temperature. Low-temperature creep data taken from past and unreported austenitic stainless steel studies are analyzed and reviewed. Creep at cryogenic temperatures of common austenitic steels, such as AISI 304, 310 316, and nitrogen-strengthened steels, such as 304HN and 3116LN, are included. Analyses suggests that logarithmic creep (creep strain dependent on the log of test time) best describe austenitic stainless steel behavior in the secondary creep stage and that the slope of creep strain versus log time is dependent on the applied stress/yield strength ratio. The role of cold work, strain-induced martensitic transformations, and stacking fault energy on low-temperature creep behavior is discussed. The engineering significance of creep on cryogenic structures is discussed in terms of the total creep strain under constant load over their operational lifetime at allowable stress levels.

Transformation in austenitic stainless steel sheet under different loading directions

NARCIS (Netherlands)

van den Boogaard, Antonius H.; Krauer, J.; Hora, P.

2011-01-01

The stress-strain relation for austenitic stainless steels is based on 2 main contributions: work hardening and a phase transformation from austenite to martensite. The transformation is highly temperature dependent. In most models for phase transformation from austenite to martensite, the stress

Transformation in Austenitic Stainless Steel Sheet under Different Loading Directions

NARCIS (Netherlands)

van den Boogaard, Antonius H.; Krauer, J.; Hora, P.

2011-01-01

The stress-strain relation for austenitic stainless steels is based on 2 main contributions: work hardening and a phase transformation from austenite to martensite. The transformation is highly temperature dependent. In most models for phase transformation from austenite to martensite, the stress

Phase transformations of under-cooled austenite of new bainitic materials for scissors crossovers

Directory of Open Access Journals (Sweden)

J. Pacyna

2008-07-01

Full Text Available The paper contains CCT diagrams presenting a transformation kinetics of under-cooled austenite from two new bainitic cast steels which the scissors crossovers for heavy-duty railway tracks (min. 230kN/axle at the speed up to 200 km/h are made of. The cooling ranges of UIC60 type railway tracks plot on the CCT diagrams indicate that there is a 100% bainitic structure in the scissors crossovers made of these cast steels as well, but mainly it would be a favourable for cracking resistance lower bainite. The achievable hardness of scissors crossovers made of new materials make it possible to use high–temperature tempering resulting in obtaining of good crack resistance. However one should provide a good quality of castings made.

Effects of isothermal heat treatment on nanostructured bainite morphology and microstructures in laser cladded coatings

International Nuclear Information System (INIS)

Guo, Yanbing; Feng, Kai; Lu, Fenggui; Zhang, Ke; Li, Zhuguo; Hosseini, Seyed Reza Elmi; Wang, Min

2015-01-01

Highlights: • Nanobainitic coatings under 200, 250 and 300 °C heat treatments are fabricated. • The size of bainite sheaves increased with the isothermal temperature increasing. • Textured and chaotic distributions are observed in 200 and 300 °C microstructures. • The evolution model of nanobainite morphology is established and analyzed. • The bainitic ferrite of 200 °C heat treatment has a true thickness of 45 nm. - Abstract: Laser cladding and subsequent isothermal heat treatments have been used to fabricate nanostructured bainitic coatings. XRD has been used to determine the kinetics of bainitic transformation process. OM, SEM and TEM have been used to characterize the morphology and microstructures at different stages of transformation. The results showed that at the initial stage of bainitic transformation, the bainite sheaves are short and thin at a relatively low transformation temperature. The fully transformed bainitic microstructure obtained at a relatively high temperature present a textured morphology. The chaotic growth orientations of the sheaves and the island like of the retained austenite have been observed at the low transformation temperature. A simple model has been established to describe the microstructures and the bainite sheaves growth evolutions during the isothermal holding at the different transformed temperatures. The morphology and distribution of the bainite in the coatings were analyzed by using the nucleation and growth rate of bainitic transformation theories, which is consisted with the experiment results.

Effects of isothermal heat treatment on nanostructured bainite morphology and microstructures in laser cladded coatings

Energy Technology Data Exchange (ETDEWEB)

Guo, Yanbing [Shanghai Key Lab of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Feng, Kai; Lu, Fenggui; Zhang, Ke [Shanghai Key Lab of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); State Key Laboratory of Metal Matrix Composite, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Li, Zhuguo, E-mail: lizg@sjtu.edu.cn [Shanghai Key Lab of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Hosseini, Seyed Reza Elmi [Shanghai Key Lab of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Wang, Min [Shanghai Key Lab of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); State Key Laboratory of Metal Matrix Composite, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China)

2015-12-01

Highlights: • Nanobainitic coatings under 200, 250 and 300 °C heat treatments are fabricated. • The size of bainite sheaves increased with the isothermal temperature increasing. • Textured and chaotic distributions are observed in 200 and 300 °C microstructures. • The evolution model of nanobainite morphology is established and analyzed. • The bainitic ferrite of 200 °C heat treatment has a true thickness of 45 nm. - Abstract: Laser cladding and subsequent isothermal heat treatments have been used to fabricate nanostructured bainitic coatings. XRD has been used to determine the kinetics of bainitic transformation process. OM, SEM and TEM have been used to characterize the morphology and microstructures at different stages of transformation. The results showed that at the initial stage of bainitic transformation, the bainite sheaves are short and thin at a relatively low transformation temperature. The fully transformed bainitic microstructure obtained at a relatively high temperature present a textured morphology. The chaotic growth orientations of the sheaves and the island like of the retained austenite have been observed at the low transformation temperature. A simple model has been established to describe the microstructures and the bainite sheaves growth evolutions during the isothermal holding at the different transformed temperatures. The morphology and distribution of the bainite in the coatings were analyzed by using the nucleation and growth rate of bainitic transformation theories, which is consisted with the experiment results.

Effect of microalloying elements (Nb, V and Ti) on the hot flow behavior of high-Mn austenitic twinning induced plasticity (TWIP) steel

International Nuclear Information System (INIS)

Reyes-Calderón, F.; Mejía, I.; Boulaajaj, A.; Cabrera, J.M.

2013-01-01

This research work studies the effect of microalloying elements such as Nb, V and Ti on the hot flow behavior of high-Mn austenitic TWIP steel. For this purpose, isothermal uniaxial hot compression tests were carried out at three temperatures (900, 1000 and 1100 °C) and four constant strain rates (10 −1 , 10 −2 , 10 −3 and 10 −4 s −1 ). Experimental results revealed that hot flow curves of microalloyed TWIP steels show single peak curves for all test conditions. Results are discussed in terms of the peak stress (σ p ) and peak strain (ε p ) and its dependence on the strain rate (ε) and temperature. The addition of microalloying elements such as Nb, V and Ti in TWIP steels generates a slight increase in the σ p value, and Ti microalloyed TWIP steel exhibits the highest σ p value. Hot deformed microstructures were analyzed by the Electron Back-Scattering Diffraction Technique (EBSD). The most important results of the austenitic recrystallized grain refinement were obtained for V and Ti microalloyed TWIP steels.

Crystallography of lath martensite and stabilization of retained austenite

International Nuclear Information System (INIS)

Sarikaya, M.

1982-10-01

TEM was used to study the morphology and crystallography of lath martensite in low and medium carbon steels in the as-quenched and 200 0 C tempered conditions. The steels have microduplex structures of dislocated lath martensite and continuous thin films of retained austenite at the lath interfaces. Stacks of laths form the packets which are derived from different [111] variants of the same austenite grain. The residual parent austenite enables microdiffraction experiments with small electron beam spot sizes for the orientation relationships (OR) between austenite and martensite. All three most commonly observed ORs, namely Kurdjumov-Sachs, Nishiyama-Wassermann, and Greninger-Troiano, operate within the same sample

Crystallography of lath martensite and stabilization of retained austenite

Energy Technology Data Exchange (ETDEWEB)

Sarikaya. M.

1982-10-01

TEM was used to study the morphology and crystallography of lath martensite in low and medium carbon steels in the as-quenched and 200/sup 0/C tempered conditions. The steels have microduplex structures of dislocated lath martensite and continuous thin films of retained austenite at the lath interfaces. Stacks of laths form the packets which are derived from different (111) variants of the same austenite grain. The residual parent austenite enables microdiffraction experiments with small electron beam spot sizes for the orientation relationships (OR) between austenite and martensite. All three most commonly observed ORs, namely Kurdjumov-Sachs, Nishiyama-Wassermann, and Greninger-Troiano, operate within the same sample.

Local approach: fracture at high temperature in an austenitic stainless steel submitted to thermomechanical loadings. Calculations and experimental validations

International Nuclear Information System (INIS)

Poquillon, D.

1997-10-01

Usually, for the integrity assessment of defective components, well established rules are used: global approach to fracture. A more fundamental way to deal with these problems is based on the local approach to fracture. In this study, we choose this way and we perform numerical simulations of intergranular crack initiation and intergranular crack propagation. This type of damage can be find in components of fast breeder reactors in 316 L austenitic stainless steel which operate at high temperatures. This study deals with methods coupling partly the behaviour and the damage for crack growth in specimens submitted to various thermomechanical loadings. A new numerical method based on finite element computations and a damage model relying on quantitative observations of grain boundary damage is proposed. Numerical results of crack initiation and growth are compared with a number of experimental data obtained in previous studies. Creep and creep-fatigue crack growth are studied. Various specimen geometries are considered: compact Tension Specimens and axisymmetric notched bars tested under isothermal (600 deg C) conditions and tubular structures containing a circumferential notch tested under thermal shock. Adaptative re-meshing technique and/or node release technique are used and compared. In order to broaden our knowledge on stress triaxiality effects on creep intergranular damage, new experiments are defined and conducted on sharply notched tubular specimens in torsion. These isothermal (600 deg C) Mode II creep tests reveal severe intergranular damage and creep crack initiation. Calculated damage fields at the crack tip are compared with the experimental observations. The good agreement between calculations and experimental data shows the damage criterion used can improve the accuracy of life prediction of components submitted to intergranular creep damage. (author)

On the S-phase formation and the balanced plasma nitriding of austenitic-ferritic super duplex stainless steel

Science.gov (United States)

de Oliveira, Willian R.; Kurelo, Bruna C. E. S.; Ditzel, Dair G.; Serbena, Francisco C.; Foerster, Carlos E.; de Souza, Gelson B.

2018-03-01

The different physical responses of austenite (γ) and ferrite (α) iron structures upon nitriding result in technical challenges to the uniform modification of α-γ materials, as the super duplex stainless steel (SDSS). The effects of voltage (7-10 kV), frequency and pulse width on the nitrogen plasma immersion ion implantation of SDSS (α ∼ 56%, γ ∼ 44%) were investigated, correlated with structural, morphological and mechanical analyses. By controlling the treatment power, temperatures ranged from 292 °C to 401 °C. Despite the overall increase in hardness for any of the employed parameters (from ∼6 GPa to ∼15 GPa), the structure of individual grains was strikingly dissimilar at the same temperatures, depending on the energetic conditions of implantation. Modified-α grains containing iron nitrides (ε-Fe2-3N, γ‧ -Fe4N) presented intense brittleness, whereas the expanded phase γN (S-phase) laid principally in modified-γ grains, exhibiting ductile-like deformation features and thicker layers. The γN was the dominant phase in both α-γ grains at ∼401 °C, providing them with balanced structure and mechanical behavior. These phenomena corroborate with γN as mediator of the process, through a mechanism involving the nitrogen-promoted ferrite to austenite conversion and nitrides dissolution at high temperatures. An approximately linear correlation of the γN content with respect to the ion energy per pulse was demonstrated, which properly embodies limiting effects to the treatment. This can be a parameter for the α-γ steel surface modification, consisting in a better adjustment to obtain more precise control along with temperature.

Fatigue damage evolution of cold-worked austenitic nickel-free high-nitrogen steel X13CrMnMoN18-14-3 (1.4452)

Energy Technology Data Exchange (ETDEWEB)

Tikhovskiy, I.; Weiss, S.; Fischer, A. [Univ. of Duisburg-Essen, Materials Science and Engineering II, Duisburg (Germany)

2004-07-01

Due to the fact that the risk of Ni-allergies becomes more and more important for modern therapies, the necessity of Ni-free implant materials becomes increasingly important. Beside Co- and Ti-base alloys Ni-free high-nitrogen steels may offer an attractive alternative. The present work presents the austenitic high-nitrogen and nickel-free steel X13CrMnMoN18-14-3, (Material No.: 1.4452) after 20% cold-working. In addition this material was deformed under axial cyclic total strain controlled fatigue tests at room temperature. The development of dislocation structure due to different loading amplitudes was compared to none cyclically deformed material. The good mechanical und fatigue properties of these austenitic high-nitrogen steels as well as the better tribological, chemical and biological properties compared to CrNiMo-steels qualify these steels as a promising alternative in medical applications. (orig.)

Strength of "Light" Ferritic and Austenitic Steels Based on the Fe - Mn - Al - C System

Science.gov (United States)

Kaputkina, L. M.; Svyazhin, A. G.; Smarygina, I. V.; Kindop, V. E.

2017-01-01

The phase composition, the hardness, the mechanical properties at room temperature, and the resistance to hot (950 - 1000°C) and warm (550°C) deformation are studied for cast deformable "light" ferritic and austenitic steels of the Fe - (12 - 25)% Mn - (0 - 15)% Al - (0 - 2)% C system alloyed additionally with about 5% Ni. The high-aluminum high-manganese low-carbon and carbonless ferritic steels at a temperature of about 0.5 T melt have a specific strength close to that of the austenitic steels and may be used as weldable scale-resistant and wear-resistant materials. The high-carbon Fe - (20 - 24)% Mn - (5 - 9)% Al - 5% Ni - 1.5% C austenitic steels may be applied as light high-strength materials operating at cryogenic temperatures after a solution treatment and as scale- and heat-resistant materials in an aged condition.

The negative effect of Zr addition on the high temperature strength in alumina-forming austenitic stainless steels

International Nuclear Information System (INIS)

Moon, Joonoh; Jang, Min-Ho; Kang, Jun-Yun; Lee, Tae-Ho

2014-01-01

The effect of a Zr addition on the precipitation behavior and mechanical properties in Nb-containing alumina-forming austenitic (AFA) stainless steels was investigated using tensile tests, scanning electron microscopy (SEM), and scanning transmission electron microscopy (STEM) analysis. The TEM observation showed that a Zr addition led to the formation of a (Nb,Zr)(C,N) complex particle, which coarsened the Nb-rich carbonitride. Tensile tests were performed at an elevated temperature (700 °C), and both the tensile and yield strengths decreased with a Zr addition. This unexpected result of a Zr addition was due to the reduction of the precipitation strengthening by particle coarsening. - Highlights: • The effect of Zr on high temperature strength in AFA steel containing Nb was studied. • Both the tensile and yield strengths of an AFA steel decreased with Zr-addition. • This is due to the reduction of precipitation strengthening by particle coarsening. • Nb(C,N) and (Nb,Zr)(C,N) particles were precipitated in an AFA and Zr-added AFA steel. • The size of (Nb,Zr)(C,N) particle is much bigger than that of Nb(C,N) particle

Isothermal and hygrothermal agings of hybrid glass fiber/carbon fiber composite

Science.gov (United States)

Barjasteh, Ehsan

anhydride/epoxy network used in composite-reinforced conductor cables was investigated to determine the extent of thermal oxidative (surface effect) and non-oxidative (bulk effect) degradation. Thermal oxidation tests were performed in air-circulating and vacuum ovens at 180°C and 200ºC (the maximum emergency temperature for ACCC conductors). The extent of oxidation during aging was determined by monitoring the thickness of the oxidized layer. Results showed that the oxidized layer thickness did not increase monotonically as a function of exposure time, and even decreased for a limited period of time. A phenomenological reaction-diffusion model was implemented to predict the thickness of oxidized layer, and the calculated results were compared with measurements for aging times up to 10,000 hours. The accuracy of the reaction-diffusion-based thickness values for the isothermally aged epoxy specimen was affected by the permeability properties of the oxidized material, and to a lesser extent by the degree of oxidation. The diffusivity varied because of changes in the density of the oxidized layer, the macro-void content, crack formation, and the molecular structures. To investigate the effects on diffusivity, the morphology of the oxidized layer and the void content was monitored over time. In addition, the density of the oxidized specimens was calculated by direct measurements of volume and weight during exposure. An empirically based volume-loss model was developed to predict the changes in volume of the specimen as a function of aging times and hence to predict the effects on the oxidized layer thickness. Volume-loss measurements provide an indication of material degradation by demonstrating a direct measurement of shrinkage rates and insight into crack initiation, as opposed to typical weight-loss measurements that provide no insight into material failure. Thermal oxidation of a unidirectional carbon-fiber/glass-fiber hybrid composite was also investigated in this study

On superplasticity of corrosion resistant ferritic-austenitic chromium-nickel steels

Energy Technology Data Exchange (ETDEWEB)

Surovtsev, A P; Sukhanov, V E

1988-01-01

The deformability of corrosion resistant chromium-nickel ferritic austenitic steel type O8Kh22N6T under tension, upsetting and torsion in the 600-1200 deg C temperature range is studied. For the deformation rate of the order of 10/sup -3/ s/sup -1/ the effect of superelasticity reveals itself at 850 deg C in the process of ferrite dynamic polymerization, in the 925-950 deg C range, at initial stages of dynamic recrystallization - the dynamic polygonization controlled by chromium carbide dissolving in steel and maximum at 1050 deg C in the process of development of austenite dynamic recrystallization with grain refinement with F/A ratio equalling 1. After upsetting in the elasticity mode at 1050 deg C the impact strength of the above steel is maximum.

Reversed austenite in 0Cr13Ni4Mo martensitic stainless steels

Energy Technology Data Exchange (ETDEWEB)

Song, Y.Y., E-mail: songyuanyuan@imr.ac.cn [Institute of Metal Research, Chinese Academy of Science, Shenyang 110016 (China); Li, X.Y.; Rong, L.J.; Li, Y.Y. [Institute of Metal Research, Chinese Academy of Science, Shenyang 110016 (China); Nagai, T. [National Institute for Materials Science, Sengen 1-2-1, Tsukuba 305-0047 (Japan)

2014-01-15

The austenite reversion process and the distribution of carbon and other alloying elements during tempering in 0Cr13Ni4Mo martensitic stainless steel have been investigated by in-situ high temperature X-ray diffraction (XRD) and scanning transmission electron microscopy (STEM). The microstructure of the reversed austenite was characterized using transmission electron microscopy (TEM). The results revealed that the amount of the reversed austenite formed at high temperature increased with the holding time. Direct experimental evidence supported carbon partitioning to carbides and Ni to the reversed austenite. The reversed austenite almost always nucleated in contact with lath boundary M{sub 23}C{sub 6} carbides during tempering and the diffusion of Ni promoted its growth. The Ni enrichment and the ultrafine size of the reversed austenite were considered to be the main factors that accounted for the stability of the reversed austenite. - Highlights: • The amount of the reversed austenite formed at high temperature increases with the holding time. • STEM results directly show that carbon is mainly partitioned into the carbides and Ni into the reversed austenite. • The Ni enrichment and the ultrafine size are the main factors leading to the stabilization of the reversed austenite.

Internal hydrogen-induced subcritical crack growth in austenitic stainless steels

Science.gov (United States)

Huang, J. H.; Altstetter, C. J.

1991-11-01

The effects of small amounts of dissolved hydrogen on crack propagation were determined for two austenitic stainless steel alloys, AISI 301 and 310S. In order to have a uniform distribution of hydrogen in the alloys, they were cathodically charged at high temperature in a molten salt electrolyte. Sustained load tests were performed on fatigue precracked specimens in air at 0 ‡C, 25 ‡C, and 50 ‡C with hydrogen contents up to 41 wt ppm. The electrical potential drop method with optical calibration was used to continuously monitor the crack position. Log crack velocity vs stress intensity curves had definite thresholds for subcritical crack growth (SCG), but stage II was not always clearly delineated. In the unstable austenitic steel, AISI 301, the threshold stress intensity decreased with increasing hydrogen content or increasing temperature, but beyond about 10 wt ppm, it became insensitive to hydrogen concentration. At higher concentrations, stage II became less distinct. In the stable stainless steel, subcritical crack growth was observed only for a specimen containing 41 wt ppm hydrogen. Fractographic features were correlated with stress intensity, hydrogen content, and temperature. The fracture mode changed with temperature and hydrogen content. For unstable austenitic steel, low temperature and high hydrogen content favored intergranular fracture while microvoid coalescence dominated at a low hydrogen content. The interpretation of these phenomena is based on the tendency for stress-induced phase transformation, the different hydrogen diffusivity and solubility in ferrite and austenite, and outgassing from the crack tip. After comparing the embrittlement due to internal hydrogen with that in external hydrogen, it is concluded that the critical hydrogen distribution for the onset of subcritical crack growth is reached at a location that is very near the crack tip.

Effects of nitrogen on corrosion of stainless steels in a liquid sodium environment

International Nuclear Information System (INIS)

Suzuki, Tadashi; Mutoh, Isao

1990-01-01

The corrosion of ferritic stainless steels using sodium at 650degC in a maximum isothermal region contained in a non-isothermal sodium loop constructed of a Type 316 stainless steel has been examined. Also, previous results on corrosion of austenitic stainless steels in sodium at 700degC in the same loop have been reproduced. The selective dissolution and absorption of nickel, the selective dissolution of chromium, and the resultant increase in iron in the surface of stainless steels in the loop mainly determine the corrosion loss of the stainless steel specimens. The austenitic steels hardly decarburize, but denitride. The ferritic steels decarburize and denitride and the denitriding is more remarkable than the decarburizing. The vanadium and niobium, carbide and nitride formers, in the ferritic steels inhibit the decarburizing to some extent, but barely inhibit the denitriding. The nitrogen in the steels rapidly diffuses to the grain boundaries, and rapidly dissolves into sodium, which will lower surface energy of the steels to enhance the dissolution of other elements. The dissolved N in sodium would then be transported to the free surface of the sodium adjacent to the argon cover gas of sodium and easily be released into the cover gas. This mechanism would cause the rapid dissolution of nitrogen into sodium and the enhancement of the corrosion rate of the steels containing nitrogen. (orig.)

Microstructural evolution during aging at 800 °C and its effect on the magnetic behavior of UNS S32304 lean duplex stainless steel

International Nuclear Information System (INIS)

Dille, J.; Areiza, M.C.L.; Tavares, S.S.M.; Pereira, G.R.; De Almeida, L.H.; Rebello, J.M.A.

2017-01-01

Duplex stainless steels are high strength and corrosion resistant alloys extensively used in chemical and petrochemical industries. However, exposition to temperatures in the range 300–1000 °C leads to precipitation of different phases having a detrimental effect on the mechanical properties and on the corrosion resistance of the alloy. In this work, the microstructural evolution during aging of a UNS S32304 lean duplex stainless steel was investigated by scanning electron microscopy, transmission electron microscopy and magnetic force microscopy. Formation of secondary austenite as well as Cr_2N and Cr_2_3C_6 precipitation and, consequently, a decrease of ferrite volume fraction were observed. EDX analysis indicated that secondary austenite is depleted in chromium which is detrimental to the corrosion resistance of the alloy. A variation of magnetic properties and Eddy current measurement parameters during aging was simultaneously detected and can be explained by the decrease of ferrite volume content. Therefore, Eddy current non-destructive testing can be successfully applied to detect the formation of deleterious phases during aging. - Highlights: • Aging of UNS S32304 lean duplex stainless steel at 800 °C is investigated. • STEM reveals formation of Cr-depleted secondary austenite and precipitation of Cr_2_3C_6 and Cr_2N. • Microstructural transformation occurs only during the first 30 min of aging. • Microstructural evolution during aging is correlated to magnetic properties evolution. • Eddy current testing permits to survey the formation of deleterious secondary austenite.

Isothermal relaxation current and microstructure changes of thermally aged polyester films impregnated by epoxy resin

Science.gov (United States)

Jiang, Xiongwei; Sun, Potao; Peng, Qingjun; Sima, Wenxia

2018-01-01

In this study, to understand the effect of thermal aging on polymer films degradation, specimens of polyester films impregnated by epoxy resin with different thermal aging temperatures (80 and 130 °C) and aging times (500, 1600, 2400 and 3000 h) are prepared, then charge de-trapping properties of specimens are investigated via the isothermal relaxation current (IRC) measurement, the distributions of trap level and its corresponding density are obtained based on the modified IRC model. It is found that the deep trap density increases remarkably at the beginning of thermal aging (before 1600 h), but it decreases obviously as the aging degree increases. At elevated aging temperature and, in particular considering the presence of air gap between two-layer insulation, the peak densities of deep traps decrease more significant in the late period of aging. It can be concluded that it is the released energy from de-trapping process leads to the fast degradation of insulation. Moreover, after thermal aging, the microstructure changes of crystallinity and molecular structures are analyzed via the x-ray diffraction experiment and Fourier transform infrared spectrometer. The results indicate that the variation of the deep trap density is closely linked with the changes of microstructure, a larger interface of crystalline/amorphous phase, more defects and broken chains caused by thermal aging form higher deep trap density stored in the samples.

Fatigue behavior of welded austenitic stainless steel in different environments

Directory of Open Access Journals (Sweden)

D.S. Yawas

2014-01-01

Full Text Available The fatigue behavior of welded austenitic stainless steel in 0.5 M hydrochloric acid and wet steam corrosive media has been investigated. The immersion time in the corrosive media was 30 days to simulate the effect on stainless steel structures/equipment in offshore and food processing applications and thereafter annealing heat treatment was carried out on the samples. The findings from the fatigue tests show that seawater specimens have a lower fatigue stress of 0.5 × 10−5 N/mm2 for the heat treated sample and 0.1 × 10−5 N/mm2 for the unheat-treated sample compared to the corresponding hydrochloric acid and steam samples. The post-welding heat treatment was found to increase the mechanical properties of the austenitic stainless steel especially tensile strength but it reduces the transformation and thermal stresses of the samples. These findings were further corroborated by the microstructural examination of the stainless steel specimen.

The influence of grain size on the strain-induced martensite formation in tensile straining of an austenitic 15Cr–9Mn–Ni–Cu stainless steel

International Nuclear Information System (INIS)

Kisko, A.; Misra, R.D.K.; Talonen, J.; Karjalainen, L.P.

2013-01-01

In order to improve understanding on the behavior of ultrafine-grained austenitic stainless steels during deformation, the influence of the austenite grain size and microstructure on the strain-induced martensite transformation was investigated in an austenitic 15Cr–9Mn–Ni–Cu (Type 204Cu) stainless steel. By different reversion treatments of the 60% cold-rolled sheet, varying grain sizes from ultrafine (0.5 μm), micron-scale (1.5 μm), fine (4 μm) to coarse (18 μm) were obtained. Some microstructures also contained a mixture of ultrafine or micron-scale and coarse initially cold-worked austenite grains. Samples were tested in tensile loading and deformation structures were analyzed after 2%, 10% and 20% engineering strains by means of martensite content measurements, scanning electron microscope together with a electron backscatter diffraction device and transmission electron microscope. The results showed that the martensite nucleation sites and the rate of transformation vary. In ultrafine grains strain-induced α′-martensite nucleates at grain boundaries and twins, whereas in coarser grains as well as in coarse-grained retained austenite, α′-martensite formation occurs at shear bands, sometimes via ε-martensite. The transformation rate of strain-induced α′-martensite decreases with decreasing grain size to 1.5 μm. However, the rate is fastest in the microstructure containing a mixture of ultrafine and retained cold-worked austenite grains. There the ultrafine grains transform quite readily to martensite similarly as the coarse retained austenite grains, where the previous cold-worked microstructure is still partly remaining

Ageing management of CANDUtm concrete containment buildings

International Nuclear Information System (INIS)

Philipose, K.E.; Gregor, F.E.

2009-01-01

The containment system in a Nuclear Power Plant (NPP) provides the final physical barrier against release of radioactive materials to the external environment. Even though there are different physical configurations to meet this fundamental safety function in various reactor types, a common feature is the use of a thick-walled concrete structure as part of the containment system commonly referred to as 'Concrete Containment Building'. In order for the concrete containment buildings to continue to provide the required safety function, it has to maintain its structural integrity. As well, its leak rates under test pressures must be maintained below acceptable limits. As some of the containment buildings of the CANDU nuclear power plants are approaching their fourth decade of successful operation, questions regarding the impact of ageing on their ultimate useful service life emerge. Ageing Management has become the tool for addressing those questions. In this paper, the ageing and ageing management of the CANDU concrete containments are discussed, including the specific programs being implemented to monitor and trend the ageing conditions. Specifically, the usefulness of the embedded strain gauges as a tool for the assessment of the condition of the containment concrete structure is discussed. Some of the operational and test data accumulated over the last 30 years have been evaluated and trended to provide some results and conclusions regarding the satisfactory long-term behaviour of the concrete containment buildings. (authors)

Sensitization behaviour of modified 316N and 316L stainless steel weld metals after complex annealing and stress relieving cycles

International Nuclear Information System (INIS)

Parvathavarthini, N.; Dayal, R.K.; Khatak, H.S.; Shankar, V.; Shanmugam, V.

2006-01-01

Sensitization behaviour of austenitic stainless steel weld metals prepared using indigenously developed modified 316N (C = 0.05%; N = 0.12%) and 316L (C = 0.02%; N = 0.07%) electrodes was studied. Detailed optical and scanning electron microscopic examination was carried out to understand the microstructural changes occurring in the weld metal during isothermal exposure at various temperatures ranging from 500 deg. C to 850 deg. C (773-1123 K). Based on these studies the mechanism of sensitization in the austenite-ferrite weld metal has been explained. Time-temperature-sensitization (TTS) diagrams were established using ASTM A262 Practice E test. From the TTS diagrams, critical cooling rate (CCR) above which there is no risk of sensitization was calculated for both materials. The heating/cooling rates to be followed for avoiding sensitization during heat treatment cycles consisting of solution-annealing and stress-relieving in fabrication of welded components of AISI 316LN stainless steel (SS) were estimated taking into account the soaking time and the number of times the component undergoes thermal excursions in the sensitization regime. The results were validated by performing controlled heating and cooling heat treatment trials on welded specimens

Methodic recommendations on ultrasonic testing of pipeline austenitic butt joints

International Nuclear Information System (INIS)

Grebennik, V.S.; Lantukh, V.M.; Tajts, M.Z.; Ermolov, I.N.; Volkov, A.S.; Vyatskov, I.A.; Kesler, N.A.; Shchedrin, I.F.

1989-01-01

Recommendations for the application of ultrasonic testing of austenitic welded joints of the Du 500 pipelines with the walls 32-34 mm thick made of steel Kh18N10T are developed. The optimal values of the main parameters of ultrasonic testing are determined experimentally. Principles of calculation of the optimal parameters are considered. 1 ref.; 4 figs

Corrosion behavior in high heat input welded heat-affected zone of Ni-free high-nitrogen Fe–18Cr–10Mn–N austenitic stainless steel

International Nuclear Information System (INIS)

Moon, Joonoh; Ha, Heon-Young; Lee, Tae-Ho

2013-01-01

The pitting corrosion and interphase corrosion behaviors in high heat input welded heat-affected zone (HAZ) of a metastable high-nitrogen Fe–18Cr–10Mn–N austenitic stainless steel were explored through electrochemical tests. The HAZs were simulated using Gleeble simulator with high heat input welding condition of 300 kJ/cm and the peak temperature of the HAZs was changed from 1200 °C to 1350 °C, aiming to examine the effect of δ-ferrite formation on corrosion behavior. The electrochemical test results show that both pitting corrosion resistance and interphase corrosion resistance were seriously deteriorated by δ-ferrite formation in the HAZ and their aspects were different with increasing δ-ferrite fraction. The pitting corrosion resistance was decreased by the formation of Cr-depleted zone along δ-ferrite/austenite (γ) interphase resulting from δ-ferrite formation; however it didn't depend on δ-ferrite fraction. The interphase corrosion resistance depends on the total amount of Cr-depleted zone as well as ferrite area and thus continuously decreased with increasing δ-ferrite fraction. The different effects of δ-ferrite fraction on pitting corrosion and interphase corrosion were carefully discussed in terms of alloying elements partitioning in the HAZ based on thermodynamic consideration. - Highlights: • Corrosion behavior in the weld HAZ of high-nitrogen austenitic alloy was studied. • Cr 2 N particle was not precipitated in high heat input welded HAZ of tested alloy. • Pitting corrosion and interphase corrosion show a different behavior. • Pitting corrosion resistance was affected by whether or not δ-ferrite forms. • Interphase corrosion resistance was affected by the total amount of δ-ferrite

Microstructural evolution of a 2.25Cr - 1 Mo steel during austenitization and temper: austenite grain growth, carbide precipitation sequence and effects on mechanical properties

International Nuclear Information System (INIS)

Depinoy, Sylvain

2015-01-01

This work aims at optimizing tensile and toughness properties of a 2.25Cr - 1Mo steel by controlling its microstructure through heat treatments. To this aim, phase transformations during austenitization, quenching and tempering have to be understood. Quantitative microstructural analyses were performed by means of SEM, TEM and XRD to characterize and model metallurgical evolution of the steel at each step of the heat treatment. The evolution of austenite during the austenitization stage, and its influence on the resulting as-quenched microstructure were thoroughly investigated. Austenite grain growth was modelled in order to understand its mechanisms, including the limited growth phenomenon observed at lower temperatures. The effect of austenitization conditions on further decomposition of austenite and on mechanical properties after quenching + tempering was experimentally determined. An optimal austenitization condition was selected and applied to study the tempering stage. Carbide precipitation was studied for various tempering temperatures and amounts of time. M3C carbides precipitate first, followed by M2C and M7C3; M23C6 are the equilibrium carbides. The influence of carbide precipitation on mechanical properties was studied. Tensile properties are closely linked to the tempering conditions in the range investigated, while impact toughness remains stable. (author) [fr

Effect of Nb Addition to Ti-Bearing Super Martensitic Stainless Steel on Control of Austenite Grain Size and Strengthening

Science.gov (United States)

Ma, Xiaoping; Langelier, Brian; Gault, Baptiste; Subramanian, Sundaresa

2017-05-01

The role of Nb in normalized and tempered Ti-bearing 13Cr5Ni2Mo super martensitic stainless steel is investigated through in-depth characterization of the bimodal chemistry and size of Nb-rich precipitates/atomic clusters and Nb in solid solution. Transmission electron microscopy and atom probe tomography are used to analyze the samples and clarify precipitates/atom cluster interactions with dislocations and austenite grain boundaries. The effect of 0.1 wt pct Nb addition on the promotion of (Ti, Nb)N-Nb(C,N) composite precipitates, as well as the retention of Nb in solution after cooling to room temperature, are analyzed quantitatively. (Ti, Nb)N-Nb(C,N) composite precipitates with average diameters of approximately 24 ± 8 nm resulting from epitaxial growth of Nb(C,N) on pre-existing (Ti,Nb)N particles, with inter-particle spacing on the order of 205 ± 68 nm, are found to be associated with mean austenite grain size of 28 ± 10 µm in the sample normalized at 1323 K (1050 °C). The calculated Zener limiting austenite grain size of 38 ± 13 µm is in agreement with the experimentally observed austenite grain size distribution. 0.08 wt pct Nb is retained in the as-normalized condition, which is able to promote Nb(C, N) atomic clusters at dislocations during tempering at 873 K (600 °C) for 2 hours, and increases the yield strength by 160 MPa, which is predicted to be close to maximum increase in strengthening effect. Retention of solute Nb before tempering also leads to it preferentially combing with C and N to form Nb(C, N) atom clusters, which suppresses the occurrence of Cr- and Mo-rich carbides during tempering.

High Nb, Ta, and Al creep- and oxidation-resistant austenitic stainless steel

Science.gov (United States)

Brady, Michael P [Oak Ridge, TN; Santella, Michael L [Knoxville, TN; Yamamoto, Yukinori [Oak Ridge, TN; Liu, Chain-tsuan [Oak Ridge, TN

2010-07-13

An austenitic stainless steel HTUPS alloy includes, in weight percent: 15 to 30 Ni; 10 to 15 Cr; 2 to 5 Al; 0.6 to 5 total of at least one of Nb and Ta; no more than 0.3 of combined Ti+V; up to 3 Mo; up to 3 Co; up to 1 W; up to 0.5 Cu; up to 4 Mn; up to 1 Si; 0.05 to 0.15 C; up to 0.15 B; up to 0.05 P; up to 1 total of at least one of Y, La, Ce, Hf, and Zr; less than 0.05 N; and base Fe, wherein the weight percent Fe is greater than the weight percent Ni wherein said alloy forms an external continuous scale comprising alumina, nanometer scale sized particles distributed throughout the microstructure, said particles comprising at least one composition selected from the group consisting of NbC and TaC, and a stable essentially single phase fcc austenitic matrix microstructure, said austenitic matrix being essentially delta-ferrite-free and essentially BCC-phase-free.

Ageing of forged superaustenitic stainless steel: Precipitate phases and mechanical properties

Energy Technology Data Exchange (ETDEWEB)

Anburaj, J., E-mail: janburaj@gmail.com [Department of Metallurgical Engineering, PSG College of Technology, Coimbatore 641 004 (India); Nazirudeen, S.S. Mohamed; Narayanan, R.; Anandavel, B.; Chandrasekar, A. [Department of Metallurgical Engineering, PSG College of Technology, Coimbatore 641 004 (India)

2012-02-15

Highlights: Black-Right-Pointing-Pointer Solutionizing of 1250 Degree-Sign C and ageing of 500-1000 Degree-Sign C was done for hot forged SASS. Black-Right-Pointing-Pointer Strength and toughness increased by 25% on hot forged than the cast SASS. Black-Right-Pointing-Pointer Amounts of precipitates after ageing were evaluated by thermo-calc. Black-Right-Pointing-Pointer Sigma forms from chi at 900 Degree-Sign C and contains constant Cr and Mo contents, unlike chi. Black-Right-Pointing-Pointer Sigma is incoherent, contains high Mo and causes low toughness at 900 Degree-Sign C. - Abstract: Cast superaustenitic stainless steel (SASS), of composition 19 wt% Cr, 20 wt% Ni, 7.5 wt% Mo and 0.37 wt% N, is hot forged at 1200 Degree-Sign C. The forging was then solutionized at 1250 Degree-Sign C and aged for 1 h and 10 h at different temperatures in the range of 500-1000 Degree-Sign C. Effect of these treatments on (i) hardness and (ii) fracture toughness based on impact energy is reported. Chi is formed from low temperatures up to 800 Degree-Sign C, and sigma at temperatures above 900 Degree-Sign C. A model is proposed to illustrate the dissolution of chi and sigma in austenite at elevated temperatures. Compared with chi, sigma contains more Mo. Toughness decreased with increasing amounts of chi and sigma precipitates. However, in the temperature range of 850-950 Degree-Sign C, low toughness was observed for relatively a short ageing time, although virtually the volume of sigma phase is very low. This is attributed to the presence of incoherent sigma in austenite matrix. Fractographs of the impact-tested samples indicated an increased tendency for brittle fracture with increasing ageing temperatures (increase in sigma content). Thermodynamic calculations substantiated (i) EDS results of composition of secondary phases present in the aged SASS and (ii) the proposed model. From these studies it is concluded that sigma is enriched in Mo at 900 Degree-Sign C and can be as

Microstructural development during the quenching and partitioning process in a newly designed low-carbon steel

Energy Technology Data Exchange (ETDEWEB)

Santofimia, M.J., E-mail: m.j.santofimianavarro@tudelft.nl [Materials Innovation Institute (M2i), Mekelweg 2, 2628 CD Delft (Netherlands); Department of Materials Science and Engineering, Delft University of Technology, Mekelweg 2, 2628 CD Delft (Netherlands); Zhao, L. [Materials Innovation Institute (M2i), Mekelweg 2, 2628 CD Delft (Netherlands); Department of Materials Science and Engineering, Delft University of Technology, Mekelweg 2, 2628 CD Delft (Netherlands); Petrov, R. [Department of Metallurgy and Materials Science, Ghent University, Technologiepark 903, 9052 Ghent (Belgium); Department of Materials Science and Engineering, Delft University of Technology, Mekelweg 2, 2628 CD Delft (Netherlands); Kwakernaak, C.; Sloof, W.G.; Sietsma, J. [Department of Materials Science and Engineering, Delft University of Technology, Mekelweg 2, 2628 CD Delft (Netherlands)

2011-09-15

This paper presents a detailed characterization of the microstructural development of a new quenching and partitioning (Q and P) steel. Q and P treatments, starting from full austenitization, were applied to the developed steel, leading to microstructures containing volume fractions of retained austenite of up to 0.15. The austenite was distributed as films in between the martensite laths. Analysis demonstrates that, in this material, stabilization of austenite can be achieved at significantly shorter time scales via the Q and P route than is possible via a bainitic isothermal holding. The results showed that the thermal stabilization of austenite during the partitioning step is not necessarily accompanied by a significant expansion of the material. This implies that the process of carbon partitioning from martensite to austenite occurs across low-mobility martensite-austenite interfaces. The amount of martensite formed during the first quench has been quantified. Unlike martensite formed in the final quench, this martensite was found to be tempered during partitioning. Measured volume fractions of retained austenite after different treatments were compared with simulations using model descriptions for carbon partitioning from martensite to austenite. Simulation results confirmed that the carbon partitioning takes place at low-mobility martensite-austenite interfaces.

Kinetics analysis of two-stage austenitization in supermartensitic stainless steel

DEFF Research Database (Denmark)

Nießen, Frank; Villa, Matteo; Hald, John

2017-01-01

The martensite-to-austenite transformation in X4CrNiMo16-5-1 supermartensitic stainless steel was followed in-situ during isochronal heating at 2, 6 and 18 K min−1 applying energy-dispersive synchrotron X-ray diffraction at the BESSY II facility. Austenitization occurred in two stages, separated...... that the austenitization kinetics is governed by Ni-diffusion and that slow transformation kinetics separating the two stages is caused by soft impingement in the martensite phase. Increasing the lath width in the kinetics model had a similar effect on the austenitization kinetics as increasing the heating-rate....

Dissolution mechanism of austenitic stainless steels in lead-bismuth eutectic at 500 deg. C

International Nuclear Information System (INIS)

Roy, M.

2012-01-01

In the framework of the future nuclear power plants studies, lead-bismuth eutectic (LBE) is foreseen as a coolant in the primary or the secondary circuit in three nuclear systems. The use of this liquid alloy induces corrosion issues for structural steels. In liquid lead alloys, steels can undergo two corrosion phenomena: dissolution or oxidation depending on the temperature and the dissolved oxygen content in LBE. The goal of this study is to identify the dissolution mechanisms of austenitic steels in LBE at 500 deg. C. Four Fe-Cr-Ni model austenitic steels, the 316L steel and five other industrial steels were corroded in LBE up to, respectively, 3000, 6000 and 200 h. The dissolution mechanism is identical for all steels: it starts by a preferential dissolution of chromium and nickel. This dissolution leads to the formation of a ferritic corrosion layer penetrated by LBE and containing between 5 and 10 at% of chromium and almost no nickel. This study demonstrates that dissolutions of nickel and chromium are linked. Otherwise, the corrosion kinetics is linear whatever the tested austenitic steel. The controlling steps of the austenitic steels' corrosion rates have been identified. Natural convection in the LBE bath leads to the formation of a diffusion boundary layer at the steel surface. Chromium diffusion in this diffusion boundary layer seems to control the corrosion rates of the model and industrial austenitic steels except the 316L steel. Indeed, the corrosion rate of the 316L steel is controlled by an interfacial reaction which is either the simultaneous dissolution of nickel and chromium in Ni, Cr compounds or the nickel and chromium dissolution catalyzed by the dissolved oxygen in LBE. This study has permitted to highlight the major role of chromium on the corrosion mechanisms and the corrosion rates of austenitic steels: the corrosion rate increases when chromium activity increases. Finally, the impact of the dissolved oxygen and the minor alloying

Fracture analysis procedure for cast austenitic stainless steel pipe with an axial crack

International Nuclear Information System (INIS)

Kamaya, Masayuki

2012-01-01

Since the ductility of cast austenitic stainless steel pipes decreases due to thermal aging embrittlement after long term operation, not only plastic collapse failure but also unstable ductile crack propagation (elastic-plastic failure) should be taken into account for the structural integrity assessment of cracked pipes. In the fitness-for-service code of the Japan Society of Mechanical Engineers (JSME), Z-factor is used to incorporate the reduction in failure load due to elastic-plastic failure. However, the JSME code does not provide the Z-factor for axial cracks. In this study, Z-factor for axial cracks in aged cast austenitic stainless steel pipes was derived. Then, a comparison was made for the elastic-plastic failure load obtained from different analysis procedures. It was shown that the obtained Z-factor could derive reasonable elastic-plastic failure loads, although the failure loads were more conservative than those obtained by the two-parameter method. (author)

Isothermal calorimetry on enzymatic biodiesel production

DEFF Research Database (Denmark)

Fjerbæk, Lene

2008-01-01

information about effects taking place when using lipases immobilized on an inert carrier for transesterification of a triglyceride and an alcohol as for biodiesel production. The biodiesel is produced by rapeseed oil and methanol as well as ethanol and a commercial biocatalyst Novozym 435 from Novozymes...... containing a Candida Antarctica B lipase immobilized on an acrylic resin. The reaction investigated is characterized by immiscible liquids (oil, methanol, glycerol and biodiesel) and enzymes imm. on an inert carrier during reaction, which allows several effects to take place that during normal reaction...... conditions can not be elucidated. These effects have been observed with isothermal calorimetry bringing forth new information about the reaction of enzymes catalyzing transesterification. Enzymatic biodiesel production has until now not been investigated with isothermal microcalorimetry, but the results...

Microstructural evolution during aging at 800 °C and its effect on the magnetic behavior of UNS S32304 lean duplex stainless steel

Energy Technology Data Exchange (ETDEWEB)

Dille, J., E-mail: jdille@metalmat.ufrj.br [Metallurgical and Materials Engineering, COPPE - Federal University of Rio de Janeiro Cidade Universitária, Centro de Tecnologia, Bloco F, CEP 21941-914 Rio de Janeiro (Brazil); Areiza, M.C.L. [Laboratory of Nondestructive Testing, Corrosion and Welding, Department of Metallurgical and Materials Engineering, Federal University of Rio of Janeiro, CEP 21941-596 (Brazil); Tavares, S.S.M. [Universidade Federal Fluminense – Departamento de Engenharia Mecânica, Rua Passo da Pátria, 156, CEP 24210-240 Niterói (Brazil); Pereira, G.R.; De Almeida, L.H.; Rebello, J.M.A. [Metallurgical and Materials Engineering, COPPE - Federal University of Rio de Janeiro Cidade Universitária, Centro de Tecnologia, Bloco F, CEP 21941-914 Rio de Janeiro (Brazil)

2017-03-15

Duplex stainless steels are high strength and corrosion resistant alloys extensively used in chemical and petrochemical industries. However, exposition to temperatures in the range 300–1000 °C leads to precipitation of different phases having a detrimental effect on the mechanical properties and on the corrosion resistance of the alloy. In this work, the microstructural evolution during aging of a UNS S32304 lean duplex stainless steel was investigated by scanning electron microscopy, transmission electron microscopy and magnetic force microscopy. Formation of secondary austenite as well as Cr{sub 2}N and Cr{sub 23}C{sub 6} precipitation and, consequently, a decrease of ferrite volume fraction were observed. EDX analysis indicated that secondary austenite is depleted in chromium which is detrimental to the corrosion resistance of the alloy. A variation of magnetic properties and Eddy current measurement parameters during aging was simultaneously detected and can be explained by the decrease of ferrite volume content. Therefore, Eddy current non-destructive testing can be successfully applied to detect the formation of deleterious phases during aging. - Highlights: • Aging of UNS S32304 lean duplex stainless steel at 800 °C is investigated. • STEM reveals formation of Cr-depleted secondary austenite and precipitation of Cr{sub 23}C{sub 6} and Cr{sub 2}N. • Microstructural transformation occurs only during the first 30 min of aging. • Microstructural evolution during aging is correlated to magnetic properties evolution. • Eddy current testing permits to survey the formation of deleterious secondary austenite.

Reversed austenite for enhancing ductility of martensitic stainless steel

Science.gov (United States)

Dieck, S.; Rosemann, P.; Kromm, A.; Halle, T.

2017-03-01

The novel heat treatment concept, “quenching and partitioning” (Q&P) has been developed for high strength steels with enhanced formability. This heat treatment involves quenching of austenite to a temperature between martensite start and finish, to receive a several amount of retained austenite. During the subsequent annealing treatment, the so called partitioning, the retained austenite is stabilized due to carbon diffusion, which results in enhanced formability and strength regarding strain induced austenite to martensite transformation. In this study a Q&P heat treatment was applied to a Fe-0.45C-0.65Mn-0.34Si-13.95Cr stainless martensite. Thereby the initial quench end temperature and the partitioning time were varied to characterize their influence on microstructural evolution. The microstructural changes were analysed by dilatometer measurements, X-ray diffraction and scanning electron microscopy, including electron back-scatter diffraction. Compression testing was made to examine the mechanical behaviour. It was found that an increasing partitioning time up to 30 min leads to an enhanced formability without loss in strength due to a higher amount of stabilized retained and reversed austenite as well as precipitation hardening.

Strain hardening of cold-rolled lean-alloyed metastable ferritic-austenitic stainless steels

Energy Technology Data Exchange (ETDEWEB)

Papula, Suvi [Aalto University School of Engineering, Department of Mechanical Engineering, P.O. Box 14200, FI-00076 Aalto (Finland); Anttila, Severi [Centre for Advanced Steels Research, University of Oulu, P.O. Box 4200, 90014 Oulu (Finland); Talonen, Juho [Outokumpu Oyj, P.O. Box 245, FI-00181 Helsinki (Finland); Sarikka, Teemu; Virkkunen, Iikka; Hänninen, Hannu [Aalto University School of Engineering, Department of Mechanical Engineering, P.O. Box 14200, FI-00076 Aalto (Finland)

2016-11-20

Mechanical properties and strain hardening of two pilot-scale lean-alloyed ferritic-austenitic stainless steels having metastable austenite phase, present at 0.50 and 0.30 volume fractions, have been studied by means of tensile testing and nanoindentation. These ferritic-austenitic stainless steels have high strain-hardening capacity, due to the metastable austenite phase, which leads to an improved uniform elongation and higher tensile strength in comparison with most commercial lean duplex stainless steels. According to the results, even as low as 0.30 volume fraction of austenite seems efficient for achieving nearly 40% elongation. The austenite phase is initially the harder phase, and exhibits more strain hardening than the ferrite phase. The rate of strain hardening and the evolution of the martensite phase were found to depend on the loading direction: both are higher when strained in the rolling direction as compared to the transverse direction. Based on the mechanical testing, characterization of the microstructure by optical/electron microscopy, magnetic balance measurements and EBSD texture analysis, this anisotropy in mechanical properties of the cold-rolled metastable ferritic-austenitic stainless steels can be explained by the elongated dual-phase microstructure, fiber reinforcement effect of the harder austenite phase and the presence and interplay of rolling textures in the two phases.

Grain boundary precipitation in an austenitic stainless steel

International Nuclear Information System (INIS)

Jones, A.R.; Howell, P.R.; Ralph, B.

The precipitation of second phase particles of niobium carbide in an austenitic stainless steel is shown to be considerably influenced by the degree of deformation introduced prior to the ageing treatment. Sites for the nucleation of second phase particles are identified and the importance of one type of nucleation site, extrinsic dislocations, to the evolution of the final boundary precipitate distributions is emphasized. Further, it is shown that the presence of a grain boundary can effect precipitation processes for some considerable distance into the matrix on either side of the boundary. (author)

Constitutive modeling of metastable austenitic stainless steel (CD-rom)

NARCIS (Netherlands)

Perdahcioglu, Emin Semih; Geijselaers, Hubertus J.M.; Huetink, Han; Boisse, P.

2008-01-01

A stress-update algorithm is developed for austenitic metastable steels which undergo phase evolution during deformation. The material initially comprises only the soft and ductile austenite phase which due to the phenomenon of mechanically induced martensitic transformation, transforms completely

Microstructural evolution and strain hardening behavior of the cold-drawn austenitic stainless steels

International Nuclear Information System (INIS)

Choi, Jeom Yong; Jin, Won

1998-01-01

The strain induced α ' -martensite formation and the strain hardening behavior of metastable austenitic stainless steel during cold drawing have been investigated. The strain induced α ' -martensite nucleates mainly at the intersection of the mechanical twins rather than ε-martensite. It could be explained by the increase of stacking fault energy which arises from the heat generated during high speed drawing and, for AISI 304/Cu, the additional effect of Cu additions. The strain hardening behavior of austenitic stainless steel is strongly related to the microstructural evolution accompanied by strain induced α ' -martensite. The work hardening rates of cold-drawn 304 increased with increasing interstitial element(C,N) contents which affect the strength of the strain induced α ' -martensite

Lathlike upper bainite in a silicon steel

International Nuclear Information System (INIS)

Liu Cheng; Zhao Zhenbo; Bhole, S.D.

2006-01-01

The morphology and mechanical properties of upper bainite formed isothermally at 400 deg. C for different holding times in a 1.83 wt.% silicon steel have been investigated by optical metallograph, X-ray diffraction and transmission electron microscopy (TEM). In the early stage of upper bainitic transformation, lathlike bainite whose individual lath ferrite is separated by the thin film type of retained austenite is obtained. As the isothermal holding times are increased, the blocky region consisting of retained austenite and martensite is also found. The stability of retained austenite in lathlike upper bainite is studied in relation to the isothermal treatment times, and the heat treatment conditions. The results show that an optimum combination of strength and ductility is attributed to the formation of bainitic ferrite (BF) and a large amount of thin film carbon-enriched retained austenite in the upper bainite

Capability of austenitic steel to withstand cyclic deformations during service at elevated temperatures

International Nuclear Information System (INIS)

Etienne, C.F.; Dortland, W.; Zeedijk, H.B.

1975-01-01

Safe design for structures with steels for elevated temperatures necessitates screening these materials on the basis of objective criteria for ductility, besides screening them on elevated temperature strength. Because creep and fatigue damage may occur during operation, the ductility of a steel after a long operation time is more important than the ductility in the as delivered condition. Results of an investigation into the ductility of austenitic Cr--Ni-steels are described. In order to determine the capability of the steels to withstand cyclic plastic deformations in the aged condition, various aging treatments were applied before determining the ductility in low-cycle fatigue testing. Correlating the ductility with the sizes of the carbide precipitates made it possible to predict the ductility behavior during long service times. This led to the conclusion that for an austenitic steel with a high thermal stability (17.5 percent Cr--11 percent Ni) the ductility can decrease considerably during service at elevated temperature. Nevertheless it is expected that the remaining ductility of such steels in aged condition will be amply sufficient to withstand the cyclic deformations that occur during normal service

Microstructural evolution in deformed austenitic TWinning Induced Plasticity steels

NARCIS (Netherlands)

Van Tol, R.T.

2014-01-01

This thesis studies the effect of plastic deformation on the stability of the austenitic microstructure against martensitic transformation and diffusional decomposition and its role in the phenomenon of delayed fracture in austenitic manganese (Mn)-based TWinning Induced Plasticity (TWIP) steels.

Intergranular corrosion behavior associated with delta-ferrite transformation of Ti-modified Super304H austenitic stainless steel

International Nuclear Information System (INIS)

Bai, Guanshun; Lu, Shanping; Li, Dianzhong; Li, Yiyi

2015-01-01

Highlights: • Relationship between delta-ferrite transformation and IGC behavior was evaluated by DL-EPR test quantitatively. • The IGC site at austenite/ferrite grain boundary changes with aging time at 650 °C. • A higher fraction of delta-ferrite with poor stability increases the IGC sensitisation. • Self-healing of IGC was mainly induced by the Cr diffusion from primary austenite rather than the delta-ferrite. - Abstract: A double loop electrochemical potentiokinetic reactivation (DL-EPR) test was conducted to investigate the relationship between the evolution of delta-ferrite and the intergranular corrosion (IGC) of Ti-modified Super304H, which was aged at 650 °C for 4–500 h. Scanning electron microscopy and transmission electron microscopy were adopted to analyze the evolution of delta-ferrite. The results indicated that a higher fraction of delta-ferrite with poor stability increased the IGC sensitisation of Ti-modified Super304H. Moreover, the self-healing of the sensitisation of Ti-modified Super304H occurred after 48 h due to the diffusion of chromium atoms mainly from the adjacent primary austenite rather than the delta-ferrite

Compatibility of graphite with a martensitic-ferritic steel, an austenitic stainless steel and a Ni-base alloy up to 1250 C

International Nuclear Information System (INIS)

Hofmann, P.

1994-08-01

To study the chemical interactions between graphite and a martensitic-ferritic steel (1.4914), an austenitic stainless steel (1.4919; AISI 316), and a Ni-base alloy (Hastelloy X) isothermal reaction experiments were performed in the temperature range between 900 and 1250 C. At higher temperatures a rapid and complete liquefaction of the components occurred as a result of eutectic interactions. The chemical interactions are diffusion-controlled processes and can be described by parabolic rate laws. The reaction behavior of the two steels is very similar. The chemical interactions of the steels with graphite are much faster above 1100 C than those for the Ni-base alloy. Below 1000 C the effect is opposite. (orig.) [de

Neutron depolarisation study of the austenite grain size in TRIP steels

International Nuclear Information System (INIS)

Dijk, N.H. van; Zhao, L.; Rekveldt, M.Th.; Fredrikze, H.; Tegus, O.; Brueck, E.; Sietsma, J.; Zwaag, S. van der

2004-01-01

We have performed combined neutron depolarisation and magnetisation measurements in order to obtain an in situ determination of the average grain size and volume fraction of the retained austenite phase in TRIP steels. The average grain size of the retained austenite was found to decrease for an increase in austenite volume fraction at two different annealing temperatures

Decomposition kinetics of expanded austenite with high nitrogen contents

DEFF Research Database (Denmark)

Christiansen, Thomas; Somers, Marcel A. J.

2006-01-01

This paper addresses the decomposition kinetics of synthesized homogeneous expanded austenite formed by gaseous nitriding of stainless steel AISI 304L and AISI 316L with nitrogen contents up to 38 at.% nitrogen. Isochronal annealing experiments were carried out in both inert (N2) and reducing (H2......) atmospheres. Differential thermal analysis (DTA) and thermogravimetry were applied for identification of the decomposition reactions and X-ray diffraction analysis was applied for phase analysis. CrN precipitated upon annealing; the activation energies are 187 kJ/mol and 128 kJ/mol for AISI 316L and AISI 304L...

Optimized chemical composition, working and heat treatment condition for resistance to irradiation assisted stress corrosion cracking of cold worked 316 and high-chromium austenitic stainless steel

International Nuclear Information System (INIS)

Yonezawa, Toshio; Iwamura, Toshihiko; Fujimoto, Koji; Ajiki, Kazuhide

2000-01-01

The authors have reported that the primary water stress corrosion cracking (PWSCC) in baffle former bolts made of austenitic stainless steels for PWR after long-term operation is caused by irradiation-induced grain boundary segregation. The resistance to PWSCC of simulated austenitic stainless steels whose chemical compositions are simulated to the grain boundary chemical composition of 316 stainless steel after irradiation increased with decrease of the silicon content, increases of the chromium content, and precipitation of M 23 C 6 carbides at the grain boundaries. In order to develop resistance to irradiation assisted stress corrosion cracking in austenitic stainless steels, optimized chemical compositions and heat treatment conditions for 316CW and high-chromium austenitic stainless steels for PWR baffle former bolts were investigated. For 316CW stainless steel, ultra-low-impurities and high-chromium content are beneficial. About 20% cold working before aging and after solution treatment has also been recommended to recover sensitization and make M 23 C 6 carbides coherent with the matrix at the grain boundaries. Heating at 700 to 725degC for 20 to 50 h was selected as a suitable aging procedure. Cold working of 5 to 10% after aging produced the required mechanical properties. The optimized composition of the high-chromium austenitic stainless steel contents 30% chromium, 30% nickel, and ultra-low impurity levels. This composition also reduces the difference between its thermal expansion coefficient and that of 304 stainless steel for baffle plates. Aging at 700 to 725degC for longer than 40 h and cold working of 10 to 15% after aging were selected to meet mechanical property specifications. (author)

Fundamental flow and fracture analysis of prime candidate alloy (PCA) for path a (austenitics)

International Nuclear Information System (INIS)

Lucas, G.E.; Jayakumar, M.; Maziasz, P.J.

1982-01-01

Room temperature microhardness tests have been performed on samples of Prime Candidate Alloy (PCA) for the austenitics (Path A) subjected to various thermomechanical treatments (TMT). The TMTs have effected various microstructures, which have been well characterized by optical metallography and TEM. For comparison, microhardness tests have been performed on samples of N-lot, DO heat and MFE 316 stainless steel with similar TMTs. The results indicate that the TMTs investigated can significantly alter the microhardness of the PCA in a manner which is consistent with microstructural changes. Moreover, while PCA had the lowest microhardness of the four alloys types after cold working, its microhardness increased while the others decreased to comparable values after aging for 2 h at 750 0 C

Radiation damage of austenitic stainless steels and zirconium alloys; Pregled radijacionog ostecenja austenitnih nerdjajucih celika i legura cirkonijuma

Energy Technology Data Exchange (ETDEWEB)

Stefanovic, V [Institute of Nuclear Sciences Boris Kidric, Vinca, Beograd (Yugoslavia)

1965-11-15

This review contains analyses of available data concerning texture deformations and radiation damage of zirconium and zircaloy-2; radiation damage, influence of neutron radiation on the mechanical properties of austenitic, ferritic and other types of stainless steels.

Generalized isothermic lattices

International Nuclear Information System (INIS)

Doliwa, Adam

2007-01-01

We study multi-dimensional quadrilateral lattices satisfying simultaneously two integrable constraints: a quadratic constraint and the projective Moutard constraint. When the lattice is two dimensional and the quadric under consideration is the Moebius sphere one obtains, after the stereographic projection, the discrete isothermic surfaces defined by Bobenko and Pinkall by an algebraic constraint imposed on the (complex) cross-ratio of the circular lattice. We derive the analogous condition for our generalized isothermic lattices using Steiner's projective structure of conics, and we present basic geometric constructions which encode integrability of the lattice. In particular, we introduce the Darboux transformation of the generalized isothermic lattice and we derive the corresponding Bianchi permutability principle. Finally, we study two-dimensional generalized isothermic lattices, in particular geometry of their initial boundary value problem

Copper precipitation behavior and mechanical properties of Cu-bearing 316L austenitic stainless steel: A comprehensive cross-correlation study

International Nuclear Information System (INIS)

Xi, Tong; Babar Shahzad, M.; Xu, Dake; Zhao, Jinlong; Yang, Chunguang; Qi, Min; Yang, Ke

2016-01-01

The effect of precipitation hardening on mechanical properties and coarsening behavior of Cu-rich precipitates in a Cu-bearing 316L austenite stainless steel after aging at 700 °C for different time were systematically investigated. The variations of morphology and composition of Cu-rich precipitates as a function of aging time were respectively characterized by electrical resistivity, atom probe tomography (APT) and transmission electron microscopy (TEM). It was found that both hardness and mechanical strength increased to peak value within short aging time, and remained nearly unchanged with prolonged aging time. The TEM observation confirmed a coherent interface between Cu-rich precipitates and austenite matrix, while high number densities of spheroidal Cu-rich precipitates were observed in all aged samples. APT analyses confirmed virtually 100% Cu core composition of Cu-rich precipitates, whereas the average radius was slightly increased from 1.38±0.46 nm to 2.39±0.81 nm with increasing the aging time. The relatively slow growth and coarsening behavior of Cu-rich precipitates was largely attributed to the slower diffusion kinetics of Cu, low interfacial energy and high strain energy of Cu-rich precipitates in the austenite matrix, and was well predicted by the Lifshitz-Slyozov-Wagner theory. The slow increase in average radius of Cu-rich precipitates was consistent with the modest change in hardness and yield strength with extended aging. In addition, the precipitation strengthening effects of Cu-rich precipitates were quantitatively evaluated and analyzed. These cumulative results and analyses could provide a solid foundation for much wider applications of Cu-bearing stainless steels.

Copper precipitation behavior and mechanical properties of Cu-bearing 316L austenitic stainless steel: A comprehensive cross-correlation study

Energy Technology Data Exchange (ETDEWEB)

Xi, Tong [Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024 (China); Babar Shahzad, M.; Xu, Dake; Zhao, Jinlong [Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); Yang, Chunguang, E-mail: cgyang@imr.ac.cn [Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); Qi, Min [School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024 (China); Yang, Ke, E-mail: kyang@imr.ac.cn [Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China)

2016-10-15

The effect of precipitation hardening on mechanical properties and coarsening behavior of Cu-rich precipitates in a Cu-bearing 316L austenite stainless steel after aging at 700 °C for different time were systematically investigated. The variations of morphology and composition of Cu-rich precipitates as a function of aging time were respectively characterized by electrical resistivity, atom probe tomography (APT) and transmission electron microscopy (TEM). It was found that both hardness and mechanical strength increased to peak value within short aging time, and remained nearly unchanged with prolonged aging time. The TEM observation confirmed a coherent interface between Cu-rich precipitates and austenite matrix, while high number densities of spheroidal Cu-rich precipitates were observed in all aged samples. APT analyses confirmed virtually 100% Cu core composition of Cu-rich precipitates, whereas the average radius was slightly increased from 1.38±0.46 nm to 2.39±0.81 nm with increasing the aging time. The relatively slow growth and coarsening behavior of Cu-rich precipitates was largely attributed to the slower diffusion kinetics of Cu, low interfacial energy and high strain energy of Cu-rich precipitates in the austenite matrix, and was well predicted by the Lifshitz-Slyozov-Wagner theory. The slow increase in average radius of Cu-rich precipitates was consistent with the modest change in hardness and yield strength with extended aging. In addition, the precipitation strengthening effects of Cu-rich precipitates were quantitatively evaluated and analyzed. These cumulative results and analyses could provide a solid foundation for much wider applications of Cu-bearing stainless steels.

Isothermal vapour-liquid equilibrium data for the binary systems of (CHF3 or C2F6) and n-heptane

International Nuclear Information System (INIS)

Williams-Wynn, Mark D.; Naidoo, Paramespri; Ramjugernath, Deresh

2016-01-01

Highlights: • Isothermal static-analytic and static-synthetic phase equilibrium measurements. • Binary VLE data for (CHF3 or C 2 F 6 ) + n-heptane. • Thermodynamic models were fitted to the experimental data. • Critical locus estimation for the systems. - Abstract: Isothermal vapour-liquid equilibrium (VLE) values for two binary systems; trifluoromethane and n-heptane at temperatures between T = (272.9 and 313.2) K, and hexafluoroethane and n-heptane at temperatures between T = (293.0 and 313.2) K were measured with a static-analytic apparatus. Bubble pressures at temperatures between T = (293.0 and 313.2) K, at several compositions, were also measured with a variable-volume static-synthetic apparatus. Vapour-liquid-liquid equilibrium (VLLE) was found to occur for certain isotherms for both of the systems. The PR EOS, with the Mathias-Copeman (MC) alpha function, combined with either the classical mixing rule or the Wong-Sandler (WS) mixing rule was used to correlate the experimental results. Either the NRTL or the UNIQUAC activity coefficient model was used within the WS mixing rule. The indirect extended scaling laws of Ungerer et al. were used to extrapolate critical loci from the experimental coexistence data, and the calculation procedure of Heidemann and Khalil was employed to calculate the mixture critical locus curves at temperatures close to the refrigerant critical temperatures. At lower temperatures on the mixture critical curve, gas-liquid critical points occurred, whereas, at higher temperatures, the critical points occurred along a liquid-liquid locus curve. The two systems were categorised according to the van Konynenburg and Scott classification.

Mechanical Stabilisation for Bainitic Reaction in a Fe-Mn-Si-C Bainitic Steel

OpenAIRE

Yang , J.; Huang , C.; Hsieh , W.; Chiou , C.

1995-01-01

In this work, the effects of different amounts (5, 10, 20, 40%) of compressive deformation of austenite on the isothermal transformation of bainite in a Fe-Mn-Si-C alloy steel have been investigated. It is found that the prior deformation of austenite retards significantly the bainitic transformation. At the same isothermal transformation temperature, as the amount of prior deformation is higher, the quantity of bainite (which can be obtained after the isothermal transformation is completed) ...

Grain-to-Grain Variations in NbC Particle Size Distributions in an Austenitic Stainless Steel

DEFF Research Database (Denmark)

Barlow, Claire; Ralph, B.; Silverman, B.

1979-01-01

Quantitative information has been obtained concerning the size distributions of NbC precipitate particles in different grains in a deformed and aged austenitic stainless steel specimen. The precipitate size distributions obtained differ from one grain to another. The average disparity measured be...

Characterization of microstructures in austenitic stainless steels by ultrasonics

International Nuclear Information System (INIS)

Raj, Baldev; Palanichamy, P.; Jayakumar, T.; Kumar, Anish; Vasudevan, M.; Shankar, P.

2000-01-01

Recently, many nondestructive techniques have been considered for microstructural characterization of materials to enable in-situ component assessment for pre-service quality and in-service performance. Ultrasonic parameters have been used for estimation of average grain size, evaluation of recrystallization after cold working, and characterization of Cr2N precipitation during thermal aging in different grades of austenitic stainless steels. Ultrasonic first back wall echo signals were obtained from several specimens of AISI type 316 stainless steel with different grain sizes. Shift in the spectral peak frequency and the change in the full width at half maximum of the autopower spectrum of the first back wall echo are correlated with the grain size in the range 30-150 microns. The advantages of this method are: (i) independence of variation in couplant conditions (ii), applicable even to highly attenuating materials, (iii) direct correlation of the ultrasonic parameters with yield strength and (iv) suitability for shop-floor applications. Recrystallization behavior (temperature range 973-1173 K and time durations 0.5-1000 h) of cold worked titanium modified 316 stainless steel (D9) has been characterized using ultrasonic velocity measurements. A velocity parameter derived using a combination of shear and longitudinal wave velocities is correlated with the degree of recrystallization. These velocity measurement could also identify onset, progress and completion of recrystallization more accurately as compared to hardness and strength measurements. Ultrasonic velocity measurements were performed in thermally aged (at 1123 K for 10 to 2000 h) nuclear grade 316 LN stainless steel. Change in velocity due to thermal aging treatment could be used to reveal the formation of (i) Cr-N clusters associated with high lattice strains, (ii) coherent Cr2N precipitation, (iii) loss of coherency and (iv) growth of incoherent Cr2N precipitates. Microstructural characterization by

Maraging-350 steel: Following the aging through diffractometric, magnetic and hyperfine analysis

Energy Technology Data Exchange (ETDEWEB)

Nunes, G.C.S. [Universidade Estadual de Maringá, Departamento de Física, Av. Colombo, 5790, PR, 87.020-900 Brazil (Brazil); Sarvezuk, P.W.C. [Universidade Tecnológica Federal do Paraná, Campo Mourão, PR (Brazil); Alves, T.J.B.; Biondo, V.; Ivashita, F.F. [Universidade Estadual de Maringá, Departamento de Física, Av. Colombo, 5790, PR, 87.020-900 Brazil (Brazil); Paesano, A., E-mail: paesano@wnet.com.br [Universidade Estadual de Maringá, Departamento de Física, Av. Colombo, 5790, PR, 87.020-900 Brazil (Brazil)

2017-01-01

Plates of solution annealed Maraging-350 steel were submitted to aging under an inert atmosphere, varying the time and temperature. The aged samples were characterized by X-ray diffraction and Mössbauer spectroscopy. The results revealed that the aging treatments induced the reversion of austenite, in amounts that vary with the time and the temperature of the heat treatment. The lattice parameters of the martensite and austenite phases, as well as their hyperfine parameters, were obtained at all aging conditions. No intermetallic compounds were identified in any of the aged samples, but a poorly crystallized phase fraction, the consequence of an incomplete martensite ⇒ austenite reversion transformation, was observed for some samples. The tetragonal distortion from cubic symmetry presented by the martensite in the solution annealed steel was not eliminated after aging. - Highlights: • We report a fine characterization of aged Maraging-350 steel. • Martensite shows a crystallographic distortion from the cubic symmetry. • Reverted austenite is present in amounts that depend on the aging conditions. • Properties measured are key information for a proper control of the steel aging.

Diffraction study of the retained austenite content in TRIP steels

Energy Technology Data Exchange (ETDEWEB)

Gnaeupel-Herold, T., E-mail: tg-h@nist.gov [NIST Center for Neuron Research, 100 Bureau Dr., Gaithersburg MD 20899-6102 (United States); University of Maryland, Department of Material Science and Engineering., College Park MD 20742-2142 (United States); Creuziger, A., E-mail: adam.creuziger@nist.gov [NIST Metallurgy Division, 100 Bureau Dr., Gaithersburg MD 20899-8553 (United States); Kent State University, Kent, OH 44242 (United States)

2011-04-25

Research highlights: {yields} Novel orientation averaging scheme for retained austenite content measurement. {yields} assumption of random grain orientation generally not justified. {yields} Averaging scheme allows to disregard texture. {yields} unlike Rietveld method, averaging method does not orientation density function. {yields} Two independent (hkl) are necessary for retained austenite content. - Abstract: The results of a study of using neutron diffraction for determining the retained austenite content of TRIP steels are presented. The study covers a wide area of materials, deformation modes (uniaxial, biaxial and plane strain), strains, and the retained austenite content as a result of these variables. It was determined using basic principles of statistics that a minimum of two reflections (hkl) for each phase is necessary to calculate a phase mass fraction and the associated standard deviation. Texture from processing the steel is the largest source of uncertainty. Through the method of complete orientation averaging described in this paper, the texture effect and with it the standard deviation of the austenite mass fraction can be substantially reduced, regardless of the type or severity of the texture.

Evaluation of Microstructure and Mechanical Properties in Dissimilar Austenitic/Super Duplex Stainless Steel Joint

Science.gov (United States)

Rahmani, Mehdi; Eghlimi, Abbas; Shamanian, Morteza

2014-10-01

To study the effect of chemical composition on microstructural features and mechanical properties of dissimilar joints between super duplex and austenitic stainless steels, welding was attempted by gas tungsten arc welding process with a super duplex (ER2594) and an austenitic (ER309LMo) stainless steel filler metal. While the austenitic weld metal had vermicular delta ferrite within austenitic matrix, super duplex stainless steel was mainly comprised of allotriomorphic grain boundary and Widmanstätten side plate austenite morphologies in the ferrite matrix. Also the heat-affected zone of austenitic base metal comprised of large austenite grains with little amounts of ferrite, whereas a coarse-grained ferritic region was observed in the heat-affected zone of super duplex base metal. Although both welded joints showed acceptable mechanical properties, the hardness and impact strength of the weld metal produced using super duplex filler metal were found to be better than that obtained by austenitic filler metal.

Effect of flue gas composition on deposit induced high temperature corrosion under laboratory conditions mimicking biomass firing. Part II: Exposures in SO2 containing atmospheres

DEFF Research Database (Denmark)

Okoro, Sunday Chukwudi; Kiamehr, Saeed; Montgomery, Melanie

2017-01-01

SO2. Scanning electron microscopy (SEM), energy dispersive X-rayspectroscopy (EDS) and X-ray diffraction (XRD) techniques werecomplimentarily applied to characterize the resulting corrosion products. Apartially molten K2SO4-layer formed on KCl coated specimens, and corrosionresulted in localized......In biomass fired power plants, the fast corrosion of superheaters is facilitatedby the presence of corrosive flue gas species, for example, SO2, which arereleased during combustion. To understand the role of the gas species on thecorrosion process, comparative laboratory exposures of deposit (KCl......)-coatedand deposit-free austenitic stainless steel (TP 347H FG) samples to gas mixturescontaining SO2 was carried out, under conditions relevant to biomass-firing.Exposures were conducted isothermally at 560 8C for 72 h, in oxidizingsulphidizing,and oxidizing-sulphidizing-chlorinating gas mixtures containing60 ppmv...

The Effects of Alloy Chemistry on Localized Corrosion of Austenitic Stainless Steels

Science.gov (United States)

Sapiro, David O.

This study investigated localized corrosion behavior of austenitic stainless steels under stressed and unstressed conditions, as well as corrosion of metallic thin films. While austenitic stainless steels are widely used in corrosive environments, they are vulnerable to pitting and stress corrosion cracking (SCC), particularly in chloride-containing environments. The corrosion resistance of austenitic stainless steels is closely tied to the alloying elements chromium, nickel, and molybdenum. Polarization curves were measured for five commercially available austenitic stainless steels of varying chromium, nickel, and molybdenum content in 3.5 wt.% and 25 wt.% NaCl solutions. The alloys were also tested in tension at slow strain rates in air and in a chloride environment under different polarization conditions to explore the relationship between the extent of pitting corrosion and SCC over a range of alloy content and environment. The influence of alloy composition on corrosion resistance was found to be consistent with the pitting resistance equivalent number (PREN) under some conditions, but there were also conditions under which the model did not hold for certain commercial alloy compositions. Monotonic loading was used to generate SCC in in 300 series stainless steels, and it was possible to control the failure mode through adjusting environmental and polarization conditions. Metallic thin film systems of thickness 10-200 nm are being investigated for use as corrosion sensors and protective coatings, however the corrosion properties of ferrous thin films have not been widely studied. The effects of film thickness and substrate conductivity were examined using potentiodynamic polarization and scanning vibrating electrode technique (SVET) on iron thin films. Thicker films undergo more corrosion than thinner films in the same environment, though the corrosion mechanism is the same. Conductive substrates encourage general corrosion, similar to that of bulk iron

Sorption Isotherm of Southern Yellow Pine—High Density Polyethylene Composites

Directory of Open Access Journals (Sweden)

Feihong Liu

2015-01-01

Full Text Available Temperature and relative humidity (RH are two major external factors, which affect equilibrium moisture content (EMC of wood-plastic composites (WPCs. In this study, the effect of different durability treatments on sorption and desorption isotherms of southern yellow pine (SYP-high density polyethylene (HDPE composites was investigated. All samples were equilibriumed at 20 °C and various RHs including 16%, 33%, 45%, 66%, 75%, 85%, 93%, and100%. EMCs obtained from desorption and absorption for different WPC samples were compared with Nelson’s sorption isotherm model predictions using the same temperature and humidity conditions. The results indicated that the amount of moisture absorbed increased with the increases in RH at 20 °C. All samples showed sorption hysteresis at a fixed RH. Small difference between EMC data of WPC samples containing different amount of ultraviolet (UV stabilizers were observed. Similar results were observed among the samples containing different amount of zinc borate (ZB. The experimental data of EMCs at various RHs fit to the Nelson’s sorption isotherm model well. The Nelson’s model can be used to predicate EMCs of WPCs under different RH environmental conditions.

Microstructural study of thermally aged duplex stainless steel deformation and fracture modes; Etude microstructurale des modes de deformation et de rupture d`un acier austenoferritique vieilli thermiquement

Energy Technology Data Exchange (ETDEWEB)

Verhaeghe, B. [Institut national polytechnique, 38 - Grenoble (France)

1996-12-31

The aim of this work is to study the micro mechanisms of deformation and rupture of an austeno ferritic stainless steel (Z 3 CND 22-10 M) with 33 % of ferrite. It is studied after ageing 1 000 h at 400 deg. C and 8 000 h at 350 deg. C and compared to the `as received` state. During ageing the ferritic phase undergoes microstructural evolutions which affects its properties. The two ageing treatments lead to roughly the same level of embrittlement. Microstructural characterisation shows that both phases percolate and exhibit orientation relationships close to Kurdjumov-Sachs ones. Mechanical properties of the steel were characterised for different ageing treatments at room temperature and at 320 deg. C. The interface is particularly strong and ensures the load transfer to ferrite even if this phase contains cleavage cracks. Moreover the interface does not oppose slip transmission which is instead controlled by localised glide in the ferritic phase. If activated slip systems of austenite are common with ferrite, slip transmission from austenite to ferrite indeed occurs through the=e interface. If they are not common, dislocations cross-slip back into the austenite. At 320 deg. C cross-slip occurs even far from the interface. Damage starts by nucleation in ferrite of cleavage cracks which propagate between austenite islands. Crack propagation is controlled by stretching of austenite ligaments. The material breaks by ductile tearing of austenite islands when the crack eventually percolates in the ferritic phase. The ductility of the material can be correctly describer using a simple model that takes into account the tearing-off the ductile-phase. (author). 153 refs.

Chemically Induced Phase Transformation in Austenite by Focused Ion Beam

Science.gov (United States)

Basa, Adina; Thaulow, Christian; Barnoush, Afrooz

2014-03-01

A highly stable austenite phase in a super duplex stainless steel was subjected to a combination of different gallium ion doses at different acceleration voltages. It was shown that contrary to what is expected, an austenite to ferrite phase transformation occurred within the focused ion beam (FIB) milled regions. Chemical analysis of the FIB milled region proved that the gallium implantation preceded the FIB milling. High resolution electron backscatter diffraction analysis also showed that the phase transformation was not followed by the typical shear and plastic deformation expected from the martensitic transformation. On the basis of these observations, it was concluded that the change in the chemical composition of the austenite and the local increase in gallium, which is a ferrite stabilizer, results in the local selective transformation of austenite to ferrite.

Sensitiaztion of austenitic stainless steels and its significance as regards stress-corrosion cracking of BWR pipe systems

International Nuclear Information System (INIS)

Roberts, W.; Otterberg, R.

1984-05-01

A critical literature evaluation dealing with sensitization of austenitic stainless steels and its importance in the context of intergranular stress-corrosion cracking (IGSCC) in high-temperature, oxygenated water is presented. The factors influencing the degree of sensitization are discussed, principally for type-304 stainless steels, both as regards sensitization arising as a result of isothermal holding within the critical temperature range and weld sensitization. The phenomenon of low-temperature sensitization is described and its potential significance under BWR operating conditions speculated upon. The principal features of and mechanisms controlling IGSCC of sensitized 304 steels in BWR-type environments are reviewed and some thoughts are given to the relevance of laboratory SCC testing in predicting the occurrence of cracking in actual BWR systems. Finally various countermeasures against IGSCC in existing and projected reactors are presented and discussed. (Author)

Simulation of the Growth of Austenite from As-Quenched Martensite in Medium Mn Steels

Science.gov (United States)

Huyan, Fei; Yan, Jia-Yi; Höglund, Lars; Ågren, John; Borgenstam, Annika

2018-04-01

As part of an ongoing development of third-generation advanced high-strength steels with acceptable cost, austenite reversion treatment of medium Mn steels becomes attractive because it can give rise to a microstructure of fine mixture of ferrite and austenite, leading to both high strength and large elongation. The growth of austenite during intercritical annealing is crucial for the final properties, primarily because it determines the fraction, composition, and phase stability of austenite. In the present work, the growth of austenite from as-quenched lath martensite in medium Mn steels has been simulated using the DICTRA software package. Cementite is added into the simulations based on experimental observations. Two types of systems (cells) are used, representing, respectively, (1) austenite and cementite forming apart from each other, and (2) austenite forming on the cementite/martensite interface. An interfacial dissipation energy has also been added to take into account a finite interface mobility. The simulations using the first type of setup with an addition of interfacial dissipation energy are able to reproduce the observed austenite growth in medium Mn steels reasonably well.

OPTIMIZATION OF SURFACE ROUGHNESS OF AISI 304 AUSTENITIC STAINLESS STEEL IN DRY TURNING OPERATION USING TAGUCHI DESIGN METHOD

Directory of Open Access Journals (Sweden)

D. PHILIP SELVARAJ

2010-09-01

Full Text Available The present work is concentrated with the dry turning of AISI 304 Austenitic Stainless Steel (ASS. This paper presents the influence of cutting parameters like cutting speed, feed rate and depth of cut on the surface roughness of austenitic stainless steel during dry turning. A plan of experiments based on Taguchi’s technique has been used to acquire the data. An orthogonal array, the signal to noise (S/N ratio and the analysis of variance (ANOVA are employed to investigate the cutting characteristics of AISI 304 austenitic stainless steel bars using TiC and TiCN coated tungsten carbide cutting tool. Finally the confirmation tests that have been carried out to compare the predicted values with the experimental values confirm its effectiveness in the analysis of surface roughness.

The role of nitrogen in improving pitting corrosion resistance of high-alloy austenitic and duplex stainless steel welds

International Nuclear Information System (INIS)

Vilpas, M.; Haenninen, H.

1999-01-01

The effects of nitrogen alloyed shielding gas on weld nitrogen content and pitting corrosion resistance of super austenitic (6%Mo) and super duplex stainless steels have been studied with special emphasis on microsegregation behaviour of Cr, Mo and N. The measurements performed with the 6%Mo steel indicate that all these elements segregate interdendritically in the fully austenitic weld metal. With nitrogen addition to the shielding gas the enrichment of nitrogen to the interdendritic regions is more pronounced than to the dendrite cores due to which the pitting corrosion resistance of the dendrite cores increases only marginally. In the super duplex steel welds nitrogen enriches in austenite increasing its pitting corrosion resistance more effectively. In these welds the pitting corrosion resistance of the ferrite phase remains lower. (orig.)

Synergistic enhancing effect of N+C alloying on cyclic deformation behaviors in austenitic steel

Energy Technology Data Exchange (ETDEWEB)

Kang, J. [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); Zhang, F.C., E-mail: zfc@ysu.edu.cn [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); Long, X.Y. [State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); Yang, Z.N. [National Engineering Research Center for Equipment and Technology of Cold Strip Rolling, Yanshan University, Qinhuangdao 066004 (China)

2014-07-29

Cyclic plastic and elastic strain controlled deformation behaviors of Mn18Cr7 austenitic steel with N0.6C0.3 synergistic enhancing alloying have been investigated using tension-compression low cycle fatigue and three-point bending high cycle fatigue testing. Results of cyclic deformation characteristic and fatigue damage mechanism have been compared to that in Mn12C1.2 steel. Mn18Cr7N0.6C0.3 steel always shows cyclic softening caused by enhanced planar sliding due to the interaction between N+C and the substitutional atoms as well as the dislocation, which is totally different from cyclic hardening in Mn12C1.2 steel caused by the interaction between C members of C–Mn couples with the dislocation. Enhanced effective stress is obtained due to the solid solution strengthening effect caused by the short range order at low strain amplitude while this effect does not work at high strain amplitude. Internal stress contributes most to the cyclic softening with the increase of strain amplitudes. Significant planar slip characteristic can be observed resulting from low stacking fault energy and high short range order effects in Mn18Cr7N0.6C0.3 steel and finally the parallel or intersecting thin sheets with dislocation tangles separated by dislocation free sheets are obtained with the prolonged cycles under cyclic elastic or plastic strain controlled fatigue testing. There exist amounts of small cracks on the surface of the Mn18Cr7N0.6C0.3 steel because fatigue crack initiation is promoted by the cyclic plastic strain localization. However, the zigzag configuration of the cracks reveals that the fatigue crack propagation is highly inhibited by the planar slip characteristic, which eventually improves the fatigue life.

Reformed austenite transformation during fatigue crack propagation of 13%Cr-4%Ni stainless steel

Energy Technology Data Exchange (ETDEWEB)

Thibault, Denis, E-mail: thibault.denis@ireq.ca [Institut de recherche d' Hydro-Quebec (IREQ), 1800, boul. Lionel-Boulet, Varennes, Quebec, J3X 1S1 (Canada); Bocher, Philippe, E-mail: philippe.bocher@etsmtl.ca [Ecole de technologie superieure, 1100, rue Notre-Dame Ouest, Montreal, Quebec, H3C 1K3 (Canada); Thomas, Marc, E-mail: marc.thomas@etsmtl.ca [Ecole de technologie superieure, 1100, rue Notre-Dame Ouest, Montreal, Quebec, H3C 1K3 (Canada); Lanteigne, Jacques, E-mail: lanteigne.jacques@ireq.ca [Institut de recherche d' Hydro-Quebec (IREQ), 1800, boul. Lionel-Boulet, Varennes, Quebec, J3X 1S1 (Canada); Hovington, Pierre, E-mail: hovington.pierre@ireq.ca [Institut de recherche d' Hydro-Quebec (IREQ), 1800, boul. Lionel-Boulet, Varennes, Quebec, J3X 1S1 (Canada); Robichaud, Patrice, E-mail: patrice.robichaud@riotinto.com [Centre de recherche et de developpement Arvida (CRDA), 1955, boul. Mellon, Jonquiere, Quebec, G7S 4K8 (Canada)

2011-08-15

Highlights: {yields} Reformed austenite in 13%Cr-4%Ni stainless steel transforms during fatigue crack growth. {yields} Low cycle fatigue tests showed that this transformation to martensite is gradual. {yields} XRD spectrums obtained on the fracture surface and have been correlated to LCF results. - Abstract: In the as-quenched state, 13%Cr-4%Ni martensitic stainless steels are essentially 100% martensitic. However, a certain amount of austenite is formed during the tempering of this alloy. This reformed austenite is thermally stable at room temperature but can transform to martensite under stress. This transformation is known to happen during impact testing but it has never been established if it occurs during fatigue crack propagation. This study presents the results of X-ray diffraction measurements of reformed austenite before and after crack growth testing. It has been found that reformed austenite does transform to martensite at the crack tip and that this transformation occurs even at a low stress intensity factor. Low-cycle fatigue tests were conducted to verify austenite transformation under cyclic straining. It was found that reformed austenite transforms only partially during the first strain reversal but that essentially all austenite has disappeared after 100 cycles. The relation between austenite transformation under low-cycle fatigue and its transformation during crack growth is also discussed.

Reformed austenite transformation during fatigue crack propagation of 13%Cr-4%Ni stainless steel

International Nuclear Information System (INIS)

Thibault, Denis; Bocher, Philippe; Thomas, Marc; Lanteigne, Jacques; Hovington, Pierre; Robichaud, Patrice

2011-01-01

Highlights: → Reformed austenite in 13%Cr-4%Ni stainless steel transforms during fatigue crack growth. → Low cycle fatigue tests showed that this transformation to martensite is gradual. → XRD spectrums obtained on the fracture surface and have been correlated to LCF results. - Abstract: In the as-quenched state, 13%Cr-4%Ni martensitic stainless steels are essentially 100% martensitic. However, a certain amount of austenite is formed during the tempering of this alloy. This reformed austenite is thermally stable at room temperature but can transform to martensite under stress. This transformation is known to happen during impact testing but it has never been established if it occurs during fatigue crack propagation. This study presents the results of X-ray diffraction measurements of reformed austenite before and after crack growth testing. It has been found that reformed austenite does transform to martensite at the crack tip and that this transformation occurs even at a low stress intensity factor. Low-cycle fatigue tests were conducted to verify austenite transformation under cyclic straining. It was found that reformed austenite transforms only partially during the first strain reversal but that essentially all austenite has disappeared after 100 cycles. The relation between austenite transformation under low-cycle fatigue and its transformation during crack growth is also discussed.

Comparison of the corrosion behavior of austenitic and ferritic/martensitic steels exposed to static liquid Pb Bi at 450 and 550 °C

Science.gov (United States)

Kurata, Y.; Futakawa, M.; Saito, S.

2005-08-01

Static corrosion tests of various steels were conducted in oxygen-saturated liquid Pb-Bi eutectic at 450 °C and 550 °C for 3000 h to study the effects of temperature and alloying elements on corrosion behavior in liquid Pb-Bi. Corrosion depth decreases at 450 °C with increasing Cr content in steels regardless of ferritic/martensitic steels or austenitic steels. Appreciable dissolution of Ni and Cr does not occur in the three austenitic steels at 450 °C. Corrosion depth of ferritic/martensitic steels also decreases at 550 °C with increasing Cr content in steels whereas corrosion depth of austenitic steels, JPCA and 316SS becomes larger due to ferritization caused by dissolution of Ni at 550 °C than that of ferritic/martensitic steels. An austenitic stainless steel containing about 5%Si exhibits fine corrosion resistance at 550 °C because the protective Si oxide film is formed and prevents dissolution of Ni and Cr.

Comparison of the corrosion behavior of austenitic and ferritic/martensitic steels exposed to static liquid Pb-Bi at 450 and 550 deg. C

International Nuclear Information System (INIS)

Kurata, Y.; Futakawa, M.; Saito, S.

2005-01-01

Static corrosion tests of various steels were conducted in oxygen-saturated liquid Pb-Bi eutectic at 450 deg. C and 550 deg. C for 3000 h to study the effects of temperature and alloying elements on corrosion behavior in liquid Pb-Bi. Corrosion depth decreases at 450 deg. C with increasing Cr content in steels regardless of ferritic/martensitic steels or austenitic steels. Appreciable dissolution of Ni and Cr does not occur in the three austenitic steels at 450 deg. C. Corrosion depth of ferritic/martensitic steels also decreases at 550 deg. C with increasing Cr content in steels whereas corrosion depth of austenitic steels, JPCA and 316SS becomes larger due to ferritization caused by dissolution of Ni at 550 deg. C than that of ferritic/martensitic steels. An austenitic stainless steel containing about 5%Si exhibits fine corrosion resistance at 550 deg. C because the protective Si oxide film is formed and prevents dissolution of Ni and Cr

Forecasting of mechanical - and structural behavior of 316 austenitic stainless steels by deformation charts

International Nuclear Information System (INIS)

Monteiro, S.N.

1980-01-01

The utilization of deformation charts applied to AISI 316 austenitic stainless steel with the purpose of foreseeing its behavior associated with structural and mechanical phenomena, is evaluated. The ocurrence of phenomena such as dynamic aging, martensite transformation, static aging, failure at creep curve, cells, subgrains and boundary slips is discussed in the different regions of the chart. A practical example of the charts' utilization for components of fast reactors is finally presented. (Author) [pt

Model-free method for isothermal and non-isothermal decomposition kinetics analysis of PET sample

International Nuclear Information System (INIS)

Saha, B.; Maiti, A.K.; Ghoshal, A.K.

2006-01-01

Pyrolysis, one possible alternative to recover valuable products from waste plastics, has recently been the subject of renewed interest. In the present study, the isoconversion methods, i.e., Vyazovkin model-free approach is applied to study non-isothermal decomposition kinetics of waste PET samples using various temperature integral approximations such as Coats and Redfern, Gorbachev, and Agrawal and Sivasubramanian approximation and direct integration (recursive adaptive Simpson quadrature scheme) to analyze the decomposition kinetics. The results show that activation energy (E α ) is a weak but increasing function of conversion (α) in case of non-isothermal decomposition and strong and decreasing function of conversion in case of isothermal decomposition. This indicates possible existence of nucleation, nuclei growth and gas diffusion mechanism during non-isothermal pyrolysis and nucleation and gas diffusion mechanism during isothermal pyrolysis. Optimum E α dependencies on α obtained for non-isothermal data showed similar nature for all the types of temperature integral approximations

Assessment of the integrity of ferritic-austenitic dissimilar weld joints of different grades of Cr-Mo ferritic steels

Energy Technology Data Exchange (ETDEWEB)

Laha, K.; Chandravathi, K.S.; Parameswaran, P.; Goyal, Sunil; Mathew, M.D. [Indira Gandhi Centre for Atomic Research, Kalpakkam (India). Metallurgy and Materials Group

2010-07-01

Integrity of the 2.25 Cr-1Mo / Alloy 800, 9Cr-1Mo / Alloy 800 and 9Cr-1Mo-VNb / Alloy 800 ferritic-austenitic dissimilar joints, fusion welded employing Inconel 182 electrode, has been assessed under creep conditions at 823 K. The dissimilar weld joints displayed lower creep rupture strength than their respective ferritic steel base metals. The strength reduction was more for 2.25Cr-1Mo steel joint and least for 9Cr-1Mo steel joint. The failure location in the joints was found to shift from the ferritic steel base metal to the intercritical region of heat-affected zone (HAZ) in ferritic steel (type IV cracking) with decrease in stress. At still lower stresses the failure occurred at the ferritic / austenitic weld interface. Localized creep deformation and cavitation in the soft intercritical HAZ induced type IV failure whereas creep cavitation at the weld interface particles induced ferritic / austenitic interface cracking due to high creep strength mismatch across it. Micromechanisms of type IV failure and interface cracking in the ferritic / austenitic joints and different susceptibility to failure for different grades of ferritic steels are discussed based on microstructural investigation, mechanical testing and finite element analysis. (Note from indexer: paper contains many typographical errors.)

Resistance to pitting corrosion in ferritic and austenitic/ferritic steels

International Nuclear Information System (INIS)

De Bouvier, O.

1995-01-01

Stainless steel tubes carrying raw water are potentially vulnerable to pitting corrosion. With a view to minimizing the corrosion risk in the river-water-cooled condensers at PWR power plant, a study was conducted to determine initiation conditions and incubation durations for pitting corrosion in stagnant water. As a result, condenser tubes in Z2 CI 18 (439) or Z2 CT 18-10 (304L) steels were phased out in favour of Z2 CND 16-32 (316L) stainless steel. The same question can be yield for other applications and especially for all types of exchangers for use in electrical applications. This study sought to assess alternative methods for estimating pitting corrosion, and to check the results of these methods against the actual behaviour of studied steels. The study covered ferritic steels (439, 444, 290Mo), austenitic steel (316L) and austenitic/ferritic steels (Uranus 35N, 45N, 47N, 52N). Two approaches were adopted: laboratory tests to compare pitting corrosion risks on different materials, and tests for characterizing the behaviour of steels exposed to river water. The study begins with a laboratory tests that yield an arbitrary parameter for quantifying pitting corrosion resistance. One method involves measuring the pitting temperature in an aggressive ferric chloride solution. Other methods measure the pitting potential, either statistically (Multipit method) or deterministically (polarization curve). We then go on to discuss tests under simulated life-like conditions, involving repeated immersions in water from the Seine. (author). 9 refs., 13 figs, 9 tabs

Effect of ferrite on the precipitation of σ phase in cast austenitic stainless steel used for primary coolant pipes of nuclear power plants

Energy Technology Data Exchange (ETDEWEB)

Wang, Yongqiang; Li, Na, E-mail: wangyongqiang1124@163.com [State Key Laboratory for Advanced Metals and Materials, University of Science and Technology, Beijing (China)

2017-11-15

The effect of ferrite phase on the precipitation of σ phase in a Z3CN20.09M cast austenitic stainless steel (CASS) used for primary coolant pipes of pressurized water reactor (PWR) nuclear power plants was investigated by using isothermal heat-treatment, optical microscopy (OM), transmission electron microscopy (TEM) and electron probe microanalysis (EPMA) techniques. The influence of different morphologies and volume fractions of ferrite in the σ phase formation mechanism was discussed. The amount of σ phase precipitated in all specimens with different microstructures increased with increasing of aging time, however, the precipitation rate is significant different. The formation of σ phase in specimens with the coarsest ferrite and the dispersively smallest ferrite is slowest. The lowest level Cr content in ferrite and fewest α/γ interfaces in specimen are the main reasons for the slowest σ precipitation due to they are unfavorable for the kinetics and thermodynamics of phase transformation respectively. By contraries, the fastest formation of σ phase takes place in specimens with narrow and long ferrite due to the most α/γ interfaces and higher Cr content in ferrite which are beneficial for preferential nucleation and formation thermodynamics of σ phase. (author)

Modelling of degradation processes in creep resistant steels through accelerated creep tests after long-term isothermal ageing

Energy Technology Data Exchange (ETDEWEB)

Sklenicka, V.; Kucharova, K.; Svoboda, M.; Kroupa, A.; Kloc, L. [Academy of Sciences of the Czech Republic, Brno (Czech Republic). Inst. of Physics of Materials; Cmakal, J. [UJP PRAHA a.s., Praha-Zbraslav (Czech Republic)

2010-07-01

Creep behaviour and degradation of creep properties of creep resistant materials are phenomena of major practical relevance, often limiting the lives of components and structures designed to operate for long periods under stress at elevated and/or high temperatures. Since life expectancy is, in reality, based on the ability of the material to retain its high-temperature creep strength for the projected designed life, methods of creep properties assessment based on microstructural evolution in the material during creep rather than simple parametric extrapolation of short-term creep tests are necessary. In this paper we will try to further clarify the creep-strength degradation of selected advanced creep resistant steels. In order to accelerate some microstructural changes and thus to simulate degradation processes in long-term service, isothermal ageing at 650 C for 10 000 h was applied to P91 and P23 steels in their as-received states. The accelerated tensile creep tests were performed at temperature 600 C in argon atmosphere on all steels both in the as-received state and after long-term isothermal ageing, in an effort to obtain a more complete description of the role of microstructural stability in high temperature creep of these steels. Creep tests were followed by microstructural investigations by means of both transmission and scanning electron microscopy and by the thermodynamic calculations. The applicability of the accelerated creep tests was verified by the theoretical modelling of the phase equilibria at different temperatures. It is suggested that under restructed oxidation due to argon atmosphere microstructural instability is the main detrimental process in the long-term degradation of the creep rupture strength of these steels. (orig.)

Microstructure and mechanical properties of annealed SUS 304H austenitic stainless steel with copper

Energy Technology Data Exchange (ETDEWEB)

Sen, Indrani [Department of Materials Engineering, Indian Institute of Science, Bangalore 560012 (India); Amankwah, E. [Department of Materials Engineering, Indian Institute of Science, Bangalore 560012 (India); Department of Materials Science, African University of Science and Technology, Abuja (Nigeria); Kumar, N.S. [Department of Materials Engineering, Indian Institute of Science, Bangalore 560012 (India); Fleury, E. [Center for High Temperature Energy Materials, Korea Institute of Science and Technology, Seoul 136-791 (Korea, Republic of); Oh-ishi, K.; Hono, K. [National Institute for Materials Science, 1-2-1 Sengen, Tsukuba 305-0047 (Japan); Ramamurty, U., E-mail: ramu@materials.iisc.ernet.in [Department of Materials Engineering, Indian Institute of Science, Bangalore 560012 (India)

2011-05-25

Research highlights: {yields} SUS 304H austenitic stainless steel containing 3 wt.% Cu was annealed at 700 deg. C for up to 100 h. {yields} Microstructure and mechanical properties of annealed alloys are examined. {yields} Nano-sized Cu-rich precipitation upon annealing. {yields} Strength of the alloy remains invariant with annealing whereas ductility improves. {yields} Fatigue crack growth threshold of 3 wt.% Cu added alloy increases with annealing. - Abstract: An experimental investigation into the effect of Cu on the mechanical properties of 0 and 3 wt.% Cu added SUS 304H austenitic stainless steel upon annealing at 700 deg. C for up to 100 h was conducted. Optical microscopy reveals grain coarsening in both the alloys upon annealing. Observations by transmission electron microscopy revealed the precipitation of nanometer-sized spherical Cu particles distributed within the austenitic grains and the presence of carbides at the dislocations. Both the yield and ultimate tensile strengths of the alloys were found to remain invariant with annealing. Tensile ductility and the threshold stress intensity factor range for fatigue crack growth for 3 wt.% Cu added alloy increase with annealing. These are attributed to the grain coarsening with annealing. In all, the addition of Cu to SUS 304H does not affect the mechanical performance adversely while improving creep resistance.

Nitrogen-containing superlow-carbon austenitic steel 02Kh25N22AM2

Science.gov (United States)

Fe'ldgandler, É. G.; Svistunova, T. V.; Savkina, L. Ya.; Lapshina, O. B.

1996-02-01

At present the equipment for manufacturing carbamide mineral fertilizers is produced from domestic steel 03Kh17N14M3 having "carbamide quality." Imported equipment also used in the industry is produced from steel of the 25-22-2 (Cr -Ni-Mo) type shipped by various firms, namely, 2RE69 (Sandvik, Sweden), 254SFER (Avesta, Sweden), 2522LCN (VDM, Germany), DM 1.4466 (Germany), and X2CrNiMo 25-22-2 (Dalmine, Italy). The imported steels are used because in some units steel 03Khl7Nl4M3 does not provide the requisite corrosion resistance in an intensified process of carbamide manufacturing. We currently possess domestic high-alloyed steel for producing new and repairing imported equipment operating under the severe conditions of carbamide synthesis. The present paper concerns the structure, mechanical properties, and corrosion resistance of industrially produced steel 02Kh25N22AM2 (ChS-108) and the recommended range of its application.

Austenite reversion in low-carbon martensitic stainless steels – a CALPHAD-assisted review

DEFF Research Database (Denmark)

Niessen, Frank

2018-01-01

Low-carbon martensitic stainless steels with 11.5–16 wt-% Cr and martensite upon inter-critical annealing. The review treats...... the mechanisms governing the formation and stabilisation of reverted austenite and is assisted by the computation of phase equilibria. Literature data on Cr and Ni concentrations of the reverted austenite/martensite dual-phase microstructure are assessed with respect to predicted concentrations. Reasonable...... agreement was found for concentrations in martensite. Systematic excess of Cr in austenite of approx. 2 wt-% relative to calculations was suspected to originate from the growth of M23C6 with a coherent interface to austenite. Within large scatter, measured values of Ni in austenite were on average 2 wt...

Effect of Austenitic and Austeno-Ferritic Electrodes on 2205 Duplex and 316L Austenitic Stainless Steel Dissimilar Welds

Science.gov (United States)

Verma, Jagesvar; Taiwade, Ravindra V.

2016-11-01

This study addresses the effect of different types of austenitic and austeno-ferritic electrodes (E309L, E309LMo and E2209) on the relationship between weldability, microstructure, mechanical properties and corrosion resistance of shielded metal arc welded duplex/austenitic (2205/316L) stainless steel dissimilar joints using the combined techniques of optical, scanning electron microscope, energy-dispersive spectrometer and electrochemical. The results indicated that the change in electrode composition led to microstructural variations in the welds with the development of different complex phases such as vermicular ferrite, lathy ferrite, widmanstatten and intragranular austenite. Mechanical properties of welded joints were diverged based on compositions and solidification modes; it was observed that ferritic mode solidified weld dominated property wise. However, the pitting corrosion resistance of all welds showed different behavior in chloride solution; moreover, weld with E2209 was superior, whereas E309L exhibited lower resistance. Higher degree of sensitization was observed in E2209 weld, while lesser in E309L weld. Optimum ferrite content was achieved in all welds.

Crystallization kinetics of the Cu50Zr50 metallic glass under isothermal conditions

International Nuclear Information System (INIS)

Gao, Qian; Jian, Zengyun; Xu, Junfeng; Zhu, Man; Chang, Fange; Han, Amin

2016-01-01

Amorphous structure of the melt-spun Cu 50 Zr 50 amorphous alloy ribbons were confirmed by X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HR-TEM). Isothermal crystallization kinetics of these alloy ribbons were investigated using differential scanning calorimetry (DSC). Besides, Arrhenius and Johnson-Mehl-Avrami (JMA) equations were utilized to obtain the isothermal crystallization kinetic parameters. As shown in the results, the local activation energy E α decreases by a large margin at the crystallized volume fraction α<0.1, which proves that crystallization process is increasingly easy. In addition, the local activation energy E α is basically constant at 0.1<α<0.9. Therefore, it turns out that the unchanged barrier is overcome in the crystallization process. Finally, E α rapidly decreases at 0.9<α<1, implying that crystallization becomes easier and easier to proceed. Nucleation activation energy E nucleation is greater than growth activation energy E growth , so nucleation is harder than growth in isothermal process. In terms of the local Avrami exponent n(α), it ranges 1.1–7.4, revealing that isothermal crystallization mechanism is interface-controlled one- two- or three-dimensional growth with different nucleation rates. - Graphical abstract: The local Avrami exponent n(α), it ranges 1.1–7.4, revealing that isothermal crystallization mechanism is interface-controlled one- two- or three-dimensional growth with different nucleation rates. - Highlights: • Isothermal crystallization kinetics of Cu 50 Zr 50 metallic glass was investigated. • The relationship between the local activation energy E α and the crystallized volume fraction α were determined. • The nucleation activation energy E nucleation and grain growth activation energy E growth were obtained. • The local Avrami exponent n(α) was calculated in isothermal model.

Quality of austenite chrome-nickel steel made by gas-oxygen refining

International Nuclear Information System (INIS)

Fel'dgandler, Eh.G.; Levin, F.L.; Moshkevich, E.A.; Shifrin, Eh.V.; Movshovich, V.S.; Pargamonov, E.A.

1991-01-01

Properties and structure were investigated of austenitic 03Kh18N11 and 08KhN10T steels melted at gas oxygen refining aggregates. It was established that mechanical and corrosion properties of rolling of such steels were in agreement with standard properties of metal of open melting. Sheet 08Kh18N10T steel has the level of strength and plasticity regulated for 12Kh18N10T steel. As steel of 08Kh18N10T holds the complex of high mechanical and corrosion properties, 08Kh18N10T is recommended to be replace by 12Kh18N10T with the aim of decrease of titanium usage and increase of process efficiency

Effect of shot peening on metastable austenitic stainless steels

Energy Technology Data Exchange (ETDEWEB)

Fargas, G., E-mail: gemma.fargas@upc.edu [CIEFMA - Departament de Ciència dels Materials i Enginyeria Metallúrgica, Universitat Politècnica de Catalunya, 08028 Barcelona (Spain); CRnE, Centre de Recerca en Nanoenginyeria, Universitat Politècnica de Catalunya, 08028 Barcelona (Spain); Roa, J.J.; Mateo, A. [CIEFMA - Departament de Ciència dels Materials i Enginyeria Metallúrgica, Universitat Politècnica de Catalunya, 08028 Barcelona (Spain); CRnE, Centre de Recerca en Nanoenginyeria, Universitat Politècnica de Catalunya, 08028 Barcelona (Spain)

2015-08-12

In this work, shot peening was performed in a metastable austenitic stainless steel EN 1.4318 (AISI 301LN) in order to evaluate its effect on austenite to martensite phase transformation and also the influence on the fatigue limit. Two different steel conditions were considered: annealed, i.e., with a fully austenitic microstructure, and cold rolled, consisting of a mixture of austenite and martensite. X-ray diffraction, electron back-scattered diffraction and focus ion beam, as well as nanoindentation techniques, were used to elucidate deformation mechanisms activated during shot peening and correlate with fatigue response. Results pointed out that extensive plastic deformation and phase transformation developed in annealed specimens as a consequence of shot peening. However, the increase of roughness and the generation of microcracks led to a limited fatigue limit improvement. In contrast, shot peened cold rolled specimens exhibited enhanced fatigue limit. In the latter case, the main factor that determined the influence on the fatigue response was the distance from the injector, followed successively by the exit speed of the shots and the coverage factor.

Study of interactions between liquid lead-lithium alloy and austenitic and martensitic steels

International Nuclear Information System (INIS)

Simon, N.

1992-06-01

In the framework of Fusion Technology, the behaviour of structural materials in presence of liquid alloy Pb17Li is investigated. First, the diffusion coefficients of Fe and Cr have been determined at 500 deg C. Then mass transfer experiments in Pb17Li have been conducted in an anisothermal container with pure metals (Fe, Cr, Ni), Fe-Cr steels and austenitic steels. These experiments showed a very high loss of Nickel, which is an accordance with its high solubility, and Cr showed mass-losses one order of magnitude higher than for pure iron, as the diffusion coefficient of Cr is three orders of magnitude higher than for pure Fe. The corrosion rate of binary Fe-Cr and pure Fe are identical. In austenitic steels, the gamma lattice allows a higher mass-transfer of Cr than the alpha lattice, the presence of Cr slows downs the dissolution of Ni, and the porosity of corrosion layers results of losses of Cr and Ni. Finally, a review of our results and those of other laboratories allowed an identification of the corrosion limiting step. In the case of 1.4914 martensitic steel it is the diffusion of Fe in Pb17Li, while in the case of 316L austenitic steel it is the diffusion of Cr in Pb17Li

Nanoscale microstructural characterization of a nanobainitic steel

Energy Technology Data Exchange (ETDEWEB)

Timokhina, I.B., E-mail: ilana.timokhina@eng.monash.edu.au [Centre for Material and Fibre Innovation, Deakin University, Victoria 3216 (Australia); Beladi, H. [Centre for Material and Fibre Innovation, Deakin University, Victoria 3216 (Australia); Xiong, X.Y. [Monash Centre for Electron Microscopy, Monash University, Victoria 3800 (Australia); Adachi, Y. [National Institute for Materials Science, 1-2-1 Sengen, Tsukuba 305-0047 (Japan); Hodgson, P.D. [Centre for Material and Fibre Innovation, Deakin University, Victoria 3216 (Australia)

2011-08-15

A 0.79 C-1.5 Si-1.98 Mn-0.98 Cr-0.24 Mo-1.06 Al-1.58 Co (wt.%) steel was isothermally heat treated at 200 deg. C for 10 days and 350 deg. C for 1 day to form a nanoscale bainitic microstructure consisting of nanobainitic ferrite laths with high dislocation density and retained austenite films. The microstructures of the samples were characterized by transmission electron microscopy and atom probe tomography. Despite the formation of nanoscale bainite with a high volume fraction of retained austenite in both steels, the ductility of both steels was surprisingly low. It is believed that this was associated with the formation of carbon-depleted retained austenite after isothermal transformation at 200 deg. C due to the formation of high number of Fe-C clusters and particles in the bainitic ferrite laths and carbon-enriched austenite after isothermal transformation at 350 deg. C.

Transformation of austenite to duplex austenite-ferrite assembly in annealed stainless steel 316L consolidated by laser melting

Energy Technology Data Exchange (ETDEWEB)

Saeidi, K.; Gao, X. [Department of Materials and Environmental Chemistry, Arrhenius Laboratory, Stockholm University, S-106 91 Stockholm (Sweden); Lofaj, F. [Institute of Materials Research of the Slovak Academy of Sciences, Watsonova 47, Košice (Slovakia); Faculty of Materials Science and Technology in Trnava, Slovak University of Technology in Bratislava, 916 24 Trnava (Slovakia); Kvetková, L. [Institute of Materials Research of the Slovak Academy of Sciences, Watsonova 47, Košice (Slovakia); Shen, Z.J. [Department of Materials and Environmental Chemistry, Arrhenius Laboratory, Stockholm University, S-106 91 Stockholm (Sweden)

2015-06-05

Highlights: • Mechanical properties, phase and microstructure stability of laser melted steel was studied. • Duplex austenite-ferrite assembly with improved mechanical properties was formed. • Dissolution of Mo in the steel matrix resulted in ferrite stabilization and stress relief. • Enhanced mechanical properties were achieved compared to conventionally casted and annealed steel. - Abstract: Laser melting (LM), with a focused Nd:YAG laser beam, was used to form solid bodies from 316L austenite stainless steel powder and the laser melted samples were heat treated at various temperatures. The phase changes in heat treated samples were characterized using X-ray diffraction (XRD). Samples heat treated at 800 °C and 900 °C remained single austenite while in samples heat treated at 1100 °C and 1400 °C a dual austenite-ferrite phase assembly was formed. The ferrite formation was further verified by electron back scattering diffraction (EBSD) and selective area diffraction (SAD). Microstructural changes were studied by scanning and transmission electron microscopy (SEM, TEM). In samples heat treated up to 900 °C, coalescence of the cellular-sub grains was noticed, whereas in sample heat treated at and above 1100 °C the formation of ferrite phase was observed. The correlation between the microstructure/phase assembly and the measured strength/microhardness were investigated, which indicated that the tensile strength of the laser melted material was significantly higher than that of the conventional 316L steel even after heat treatment whereas caution has to be taken when laser melted material will be exposed to an application temperature above 900 °C.

Recrystallization induced plasticity in austenite and ferrite

International Nuclear Information System (INIS)

Huang Mingxin; Pineau, André; Bouaziz, Olivier; Vu, Trong-Dai

2012-01-01

Highlights: ► Plasticity can be induced by recrystallization in austenite and ferrite. ► Strain rate is proportional to recrystallization kinetics. ► Overall atomic flux selects a preferential direction may be the origin. - Abstract: New experimental evidences are provided to demonstrate that plastic strain can be induced by recrystallization in austenite and ferrite under an applied stress much smaller than their yield stresses. Such Recrystallization Induced Plasticity (RIP) phenomenon occurs because the overall atomic flux during recrystallization follows a preferential direction imposed by the applied stress.

Carburization of austenitic and ferritic alloys in hydrocarbon environments at high temperature

Directory of Open Access Journals (Sweden)

Serna, A.

2003-12-01

Full Text Available The technical and industrial aspects of high temperature corrosion of materials exposed to a variety of aggressive environments have significant importance. These environments include combustion product gases and hydrocarbon gases with low oxygen potentials and high carbon potentials. In the refinery and petrochemical industries, austenitic and ferritic alloys are usually used for tubes in fired furnaces. The temperature range for exposure of austenitic alloys is 800-1100 °C, and for ferritic alloys 500-700 °C, with carbon activities a_c > 1 in many cases. In both applications, the carburization process involves carbon (coke deposition on the inner diameter, carbon absorption at the metal surface, diffusion of carbon inside the alloy, and precipitation and transformation of carbides to a depth increasing with service. The overall kinetics of the internal carburization are approximately parabolic, controlled by carbon diffusion and carbide precipitation. Ferritic alloys exhibit gross but uniform carburization while non-uniform intragranular and grain-boundary carburization is observed in austenitic alloys.

La corrosión a alta temperatura, tal como la carburación de materiales expuestos a una amplia variedad de ambientes agresivos, tiene especial importancia desde el punto de vista técnico e industrial. Estos ambientes incluyen productos de combustión, gases e hidrocarburos con bajo potencial de oxígeno y alto potencial de carbono. En las industrias de refinación y petroquímica, las aleaciones austeníticas y ferríticas se utilizan en tuberías de hornos. El rango de temperatura de exposición para aleaciones austeníticas está entre 800-1.100°C y para aleaciones ferríticas está entre 500-700°C, con actividades de carbono a_c>1 en algunos casos. En tuberías con ambas aleaciones, el proceso de carburación incluye deposición de carbón (coque en el diámetro interno, absorción de carbono en la superficie

Deformation behavior of austenitic stainless steel at deep cryogenic temperatures

Science.gov (United States)

Han, Wentuo; Liu, Yuchen; Wan, Farong; Liu, Pingping; Yi, Xiaoou; Zhan, Qian; Morrall, Daniel; Ohnuki, Somei

2018-06-01

The nonmagnetic austenite steels are the jacket materials for low-temperature superconductors of fusion reactors. The present work provides evidences that austenites transform to magnetic martensite when deformation with a high-strain is imposed at 77 K and 4.2 K. The 4.2 K test is characterized by serrated yielding that is related to the specific motion of dislocations and phase transformations. The in-situ transmission electron microscope (TEM) observations in nanoscale reveal that austenites achieve deformation by twinning under low-strain conditions at deep cryogenic temperatures. The generations of twins, martensitic transformations, and serrated yielding are in order of increasing difficulty.

Extended x-ray absorption fine structure investigation of annealed carbon expanded austenite

DEFF Research Database (Denmark)

Oddershede, Jette; Christiansen, Thomas L.; Somers, Marcel A. J.

2012-01-01

-carburized in a temperature regime around 470°C. The surface zone is converted into carbon expanded austenite; the high interstitial content of carbon dissolved in the surface results in highly favorable materials properties. In the present article the local atomic environment of (annealed) carbon expanded austenite...... austenite and Hägg carbide, Ξ-M5C2. EXAFS showed that the Cr atoms were mainly present in environments similar to the carbides Hägg Ξ-M5C2 and M23C6. The environments of the Fe and Ni atoms were concluded to be largely metallic austenite. Light optical micrograph of stainless steel AISI 316 gas...

Austenite Formation from Martensite in a 13Cr6Ni2Mo Supermartensitic Stainless Steel

NARCIS (Netherlands)

Bojack, A.; Zhao, L.; Morris, P.F.; Sietsma, J.

2016-01-01

The influence of austenitization treatment of a 13Cr6Ni2Mo supermartensitic stainless steel (X2CrNiMoV13-5-2) on austenite formation during reheating and on the fraction of austenite retained after tempering treatment is measured and analyzed. The results show the formation of austenite in two

Loop-mediated isothermal amplification (LAMP) based detection of ...

African Journals Online (AJOL)

SAM

2014-05-07

May 7, 2014 ... 2 months for growing in a culture. Therefore, to control .... The LAMP reaction is carried out in a 25 µL reaction mixture containing ..... J. Fish Dis. 32(6):491-497. Goto M, Honda E, Ogura A, Nomoto A, Hanaki K (2009). Colorimetric detection of loop-mediated isothermal amplification reaction by using hydroxy ...

Numerical and experimental study of long term creep damage in austenitic stainless steels

International Nuclear Information System (INIS)

Cui, Yiting

2015-01-01

The creep fracture of 316L(N) austenitic stainless steels has been studied both experimentally and theoretically for temperatures from 525 C up to 700 C and lifetimes up to nineteen years. For short term creep, failure is due to necking. Experimental lifetimes are bounded by the lower and upper bound predictions provided by a necking model and taking into account scatter in input parameters. This model leads to fair predictions of lifetimes up to a few thousand hours at very high temperature. Based on FEG-SEM observations, the transition observed in the failure curves is due to intergranular cavitation. The Riedel modeling of cavity growth by vacancy diffusion along grain boundaries coupled with continuous nucleation is carried out. Lifetimes are predicted fairly well using this model for long term creep failure whatever the considered austenitic stainless steel (316L(N), 304H, 316H, 321H) and the applied temperature (525 C - 700 C). Taking into account low and high stress regimes of Norton-power law, the Riedel model allows us to predict the creep lifetimes up to 25 years which differ from experimental data by less than a factor 3. The effect of the heterogeneity of the microstructure on grain boundary stress concentrations and cavity nucleation is simulated by the finite element method (Cast3M software). It aims to determine the distribution of grain boundary normal stress fields around precipitates depending on time and temperature. The features of the precipitates and the creep behavior of the austenitic matrix are both taking into account. (author) [fr

On the capability of austenitic steel to withstand cyclic deformations during service at elevated temperatures

International Nuclear Information System (INIS)

Etienne, C.F.; Dortland, W.; Zeedijk, H.B.

1975-01-01

Safe design for structures with steels for elevated temperatures necessitates screening these materials on the basis of objective criteria for ductility, besides screening them on elevated temperature strength. Because creep and fatigue damage may occur during operation, the ductility of a steel after a long operation time is more important than the ductility in the as delivered condition. This paper describes results of an investigation into the ductility of some austenitic Cr-Ni-steels. In order to determine the capability of the steels to withstand cyclic plastic deformation in the aged condition, various ageing treatments were applied before determining the ductility in low-cycle fatigue testing. Correlating the ductility with the sizes of the carbide precipitates made it possible to predict the ductility behaviour during long service times. This led to the conclusion that for an austenitic steel with a high thermal stability (17.5 per cent Cr-11 per cent Ni) the ductility can decrease considerably during service at elevated temperature. Nevertheless it is expected that the remaining ductility of such steels in aged condition will be amply sufficient to withstand the cyclic deformations that occur during normal service. (author)

The mechanical stability of retained austenite in low-alloyed TRIP steel under shear loading

Energy Technology Data Exchange (ETDEWEB)

Blondé, R., E-mail: r.j.p.blonde@tudelft.nl [Fundamental Aspects of Materials and Energy, Faculty of Applied Sciences, Delft University of Technology, Mekelweg 15, 2629 JB Delft (Netherlands); Materials Innovation Institute, Mekelweg 2, 2628 CD Delft (Netherlands); Jimenez-Melero, E., E-mail: enrique.jimenez-melero@manchester.ac.uk [Dalton Cumbrian Facility, The University of Manchester, Westlakes Science and Technology Park, Moor Row, Cumbria CA24 3HA (United Kingdom); Zhao, L., E-mail: lie.zhao@tudelft.nl [Materials Innovation Institute, Mekelweg 2, 2628 CD Delft (Netherlands); Department of Materials Science and Engineering, Delft University of Technology, Mekelweg 2, 2628 CD Delft (Netherlands); Schell, N., E-mail: norbert.schell@hzg.de [Institute of Materials Research, Helmholtz-Zentrum Geesthacht, Max Planck Strasse 1, 21502 Geesthacht (Germany); Brück, E., E-mail: e.h.bruck@tudelft.nl [Fundamental Aspects of Materials and Energy, Faculty of Applied Sciences, Delft University of Technology, Mekelweg 15, 2629 JB Delft (Netherlands); Zwaag, S. van der, E-mail: s.vanderzwaag@tudelft.nl [Novel Aerospace Materials Group, Faculty of Aerospace Engineering, Delft University of Technology, Kluyverweg 1, 2629 HS Delft (Netherlands); Dijk, N.H. van, E-mail: n.h.vandijk@tudelft.nl [Fundamental Aspects of Materials and Energy, Faculty of Applied Sciences, Delft University of Technology, Mekelweg 15, 2629 JB Delft (Netherlands)

2014-01-31

The microstructure evolution during shear loading of a low-alloyed TRIP steel with different amounts of the metastable austenite phase and its equivalent DP grade has been studied by in-situ high-energy X-ray diffraction. A detailed powder diffraction analysis has been performed to probe the austenite-to-martensite transformation by characterizing simultaneously the evolution of the austenite phase fraction and its carbon concentration, the load partitioning between the austenite and the ferritic matrix and the texture evolution of the constituent phases. Our results show that for shear deformation the TRIP effect extends over a significantly wider deformation range than for simple uniaxial loading. A clear increase in average carbon content during the mechanically-induced transformation indicates that austenite grains with a low carbon concentration are least stable during shear loading. The observed texture evolution indicates that under shear loading the orientation dependence of the austenite stability is relatively weak, while it has previously been found that under tensile load the {110}〈001〉 component transforms preferentially. The mechanical stability of retained austenite in TRIP steel is found to be a complex interplay between the interstitial carbon concentration in the austenite, the grain orientation and the load partitioning.

Diffractometry of expanded austenite using synchrotron radiation

International Nuclear Information System (INIS)

Fewell, M.P.; Priest, J.M.; Collins, G.A.; Short, K.T.

2000-01-01

Full text: The question of the structure of the nitrogen-rich surface layer produced in the nitriding of austenitic stainless steel has been controversial for some time. Diffractometry using conventional x-ray sources is routinely carried out on this material. The result universally seen shows an ostensibly f.c.c. lattice with a larger lattice parameter than that of the underlying austenite. The difficulty with this interpretation lies in the 200 reflection, which lies at slightly lower Bragg angle than expected on the basis of the 111, 220 and 311 reflections. This behaviour is seen in all work known to us, regardless of the grade of austenitic stainless steel or the details of the nitriding technique. It has been explained as due to a mixed f.c.c. phase with different grains having different lattice constants, or as due to a tetragonal distortion of the lattice or an f.c.c lattice with a high frequency of stacking faults, or as indicating a triclinic lattice with a unit cell having all sides equal and two angles equal

A review of hot cracking in austenitic stainless steel weldments

International Nuclear Information System (INIS)

Shankar, V.; Gill, T.P.S.; Mannan, S.L.; Rodriguez, P.

1991-01-01

The occurrence of hot cracking in austenitic stainless steel weldments is discussed with respect to its origin and metallurgical contributory factors. Of the three types of hot cracking, namely solidification cracking, liquation and ductility dip cracking, solidification cracking occurs in the interdendritic regions in weld metal while liquation and ductility dip cracking occur intergranularly in the heat-affected zone (HAZ). Segregation of impurity and minor elements such as sulphur, phosphorous, silicon, niobium, boron etc to form low melting eutectic phases has been found to be the major cause of hot cracking. Control of HAZ cracking requires minimisation of impurity elements in the base metal. In stabilized stainless steels containing niobium, higher amounts of delta-ferrite have been found necessary to prevent cracking than in unstabilized compositions. Titanium compounds have been found to cause liquation cracking in maraging steels and titanium containing stainless steels and superalloys. In nitrogen added stainless steels, cracking resistance decreases when the solidification mode changes to primary austenitic due to nitrogen addition. A review of the test methods to evaluate hot cracking behaviour showed that several external restraint and semi-self-restraint tests are available. The finger Test, WRC Fissure Bend Test, the PVR test and the Varestraint Test are described along with typical test results. Hot ductility testing to reveal HAZ cracking tendency during welding is described, which is of particular importance to stabilized stainless steels. Based on the literature, recommendations are made for welding stabilized and nitrogen added steels, indicating areas of further work. (author). 81 refs., 30 figs., 1 tab

Effects of Strain Rate and Temperature on the Mechanical Properties of Medium Manganese Steels

Energy Technology Data Exchange (ETDEWEB)

Rana, Radhakanta [Colorado School of Mines, Golden, CO (United States); Matlock, David K [Colorado School of Mines, Golden, CO (United States); Speer, John G [Colorado School of Mines, Golden, CO (United States); De Moor, Emmanuel [Colorado School of Mines, Golden, CO (United States)

2016-11-16

The effects of temperature (-60 to 100 °C) and strain rate (0.002 to 0.2 s-1) on the properties of Al-alloyed 7 and 10 wt-% Mn steels containing 34.8 and 57.3 vol-% austenite respectively were evaluated by tensile tests in isothermal liquid baths. The tensile strengths of both medium Mn steels increased with a decrease in temperature owing to the decreased austenite stability with a decrease in temperature. At lower temperatures the strength of the 10MnAl steel was highest, a consequence of the higher strain hardening rate caused by more austenite transformation to martensite with deformation. The resulting properties are assessed with a consideration of the effects of strain rate and deformation on adiabatic heating which was observed to be as high as 95o C.

Assessment of microstructure stability of cold worked Ti-modified austenitic stainless steel during aging using ultrasonic velocity measurements and correlation with mechanical properties

International Nuclear Information System (INIS)

Vasudevan, M.; Palanichamy, P.

2003-01-01

As ultrasonic velocity is sensitive to the changes in texture, it is a more reliable technique than mechanical property measurements for assessment of microstructural stability (recrystallization behaviour) of cold worked alloy where recrystallization is coupled with precipitation. Hence ultrasonic velocity measurements have been employed for studying the influence of Ti/C ratio on the microstructural stability of cold worked Ti-modified austenitic stainless steel during isochronal aging. In this alloy precipitation of TiC is known to retard recovery and recrystallization. The variation in ultrasonic velocity with aging temperature exhibited a three stage behaviour at all three frequencies employed (2, 10 and 20 MHz) and correlated well with the microstructural changes. Based on the microstructural investigations, the three stages have been identified to be recovery, progress of recrystallization and completion of recrystallization. There was one to one correspondence between the variation in the hardness, strength values and the variation in the ultrasonic velocity values as a function of aging temperature in assessing the microstructural changes, except when the interaction between the TiC precipitation and recrystallization is stronger

On the role of interlath retained austenite in the deformation of lath martensite

International Nuclear Information System (INIS)

Maresca, F; Kouznetsova, V G; Geers, M G D

2014-01-01

Literature presents extensive experimental evidence of large deformation and ductile fracture behaviour of lath martensite in martensitic and multi-phase high strength steels under quasi-static, uniaxial loading conditions. The physical origin of this apparent ductile behaviour of martensite is not clear, since martensite generally provides a high material strength. The presence of thin films of interlath retained austenite may trigger the observed apparent martensite ductility. The present contribution investigates the role played by interlath retained austenite on the mechanics of lath martensite by means of crystal plasticity simulations. It is shown that independently from the interlath retained austenite volume fraction and the exact lath morphology, localized shearing along the lath habit plane occurs as long as there are enough carriers for plasticity. The austenite film acts like a ‘greasy’ plane on which the stiffer laths can slide. The shearing mechanism is not a mere consequence of the lower flow stress in the austenitic phase, but it is largely due to the orientation relationship between the retained austenite face centred cubic lattice and the body centred cubic lath crystals. (paper)

Aging management and life extension - Containment aging study

International Nuclear Information System (INIS)

Tai, Tom M.; Deng, Daniel

2004-01-01

Bechtel is currently completing an aging study on a concrete containment structure. The target plant is a two-unit PWR plant with a generating capacity of about 850 MWe from each unit. Both units are less than 20 years old. The total electrical energy output from this plant site accounts for more than 50% of the utility's baseload operation. Although no utility in the United States has made a decision to submit a license renewal application, some have begun to investigate the feasibility of developing an life cycle management (LCM) program for a strategy to operate their plants efficiently, to investigate the financial benefit and safety implications of license renewal to operate their nuclear power plants beyond their current licensed periods, and to prepare a program plan for plant decommissioning. The LCM program includes economic, environmental, regulatory and technical aspects of continuing plant operations beyond the current license period. The Electric Power Research Institute (EPRI) has been supportive to assist utilities and owners groups in their research and development efforts to develop the technical requirements and the issues associated with important to license renewal structures. The focus of this paper is on the technical issues related to the evaluation of the material condition of the containment structure with respect to aging and the effective management of that aging. (author)

Fe-15Ni-13Cr austenitic stainless steels for fission and fusion reactor applications. II. Effects of minor elements on precipitate phase stability during thermal aging

International Nuclear Information System (INIS)

Lee, E.H.; Mansur, L.K.

2000-01-01

The precipitate phase stability in Fe-15Ni-13Cr base austenitic alloys was investigated as a function of minor alloying additions after thermally aging at 600 deg. C and 675 deg. C for times ranging from 24 h to one year. Seven major precipitate phases were found in aged specimens, including M 23 C 6 , Laves, Eta (η), TiO, NbC, MC, and M 2 P. The types and amounts of precipitate phases varied with alloying element additions, aging temperature, and aging time. By analyzing the composition of each individual particle, it was possible to determine the essential constituent elements for each phase. From this information, a strategy to promote or suppress certain precipitate phases was developed. Among the seven phases, the most desirable precipitate phases were considered to be MC and M 2 P, because these particles form on a fine scale with a high number density and, therefore, can serve as effective gas atom trap sites under irradiation

Derivation of tensile flow characteristics for austenitic materials from instrumented indentation technique

International Nuclear Information System (INIS)

Lee, K-W; Kim, K-H; Kim, J-Y; Kwon, D

2008-01-01

In this study, a method for deriving the tensile flow characteristics of austenitic materials from an instrumented indentation technique is presented along with its experimental verification. We proposed a modified algorithm for austenitic materials that takes their hardening behaviour into account. First, the true strain based on sine function instead of tangent function was adapted. It was proved that the sine function shows constant degrees of hardening which is a main characteristic of the hardening of austenitic materials. Second, a simple and linear constitutive equation was newly suggested to optimize indentation flow curves. The modified approach was experimentally verified by comparing tensile properties of five austenitic materials from uniaxial tensile test and instrumented indentation tests

Structure and phase composition of titanium nitride coating on austenitic steel

International Nuclear Information System (INIS)

Dubovitskaya, N.V.; Kolenchenko, L.D.; Larikov, L.N.

1989-01-01

Structure and phase composition of titanium nitride coating deposited on 08Kh18N10T steel substrate using ''Bulat'' device are studied. Use of complex investigation methods permitted despite small coating thickness (1μm) to aquire information on hardness, porosity, to study phase composition in all coating thickness. The surface layer (∼0.1 μm) consists of ε-Ti 2 N, TiN 0.6 , TiC 0.35 , that is formed with carbon participation from oil vacuum. In more deeper layers beside ε-Ti 2 N TiC 0.14 N 0.77 is present. Effect of carbon diffusion from substrate to forming coating is stated. Gradient of element concentrations in the substrate-coating interface causes recrystallization of austenite

Alumina-Forming Austenitic Stainless Steels Strengthened by Laves Phase and MC Carbide Precipitates

Science.gov (United States)

Yamamoto, Y.; Brady, M. P.; Lu, Z. P.; Liu, C. T.; Takeyama, M.; Maziasz, P. J.; Pint, B. A.

2007-11-01

Creep strengthening of Al-modified austenitic stainless steels by MC carbides or Fe2Nb Laves phase was explored. Fe-20Cr-15Ni-(0-8)Al and Fe-15Cr-20Ni-5Al base alloys (at. pct) with small additions of Nb, Mo, W, Ti, V, C, and B were cast, thermally-processed, and aged. On exposure from 650 °C to 800 °C in air and in air with 10 pct water vapor, the alloys exhibited continuous protective Al2O3 scale formation at an Al level of only 5 at. pct (2.4 wt pct). Matrices of the Fe-20Cr-15Ni-5Al base alloys consisted of γ (fcc) + α (bcc) dual phase due to the strong α-Fe stabilizing effect of the Al addition and exhibited poor creep resistance. However, adjustment of composition to the Fe-15Cr-20Ni-5Al base resulted in alloys that were single-phase γ-Fe and still capable of alumina scale formation. Alloys that relied solely on Fe2Nb Laves phase precipitates for strengthening exhibited relatively low creep resistance, while alloys that also contained MC carbide precipitates exhibited creep resistance comparable to that of commercially available heat-resistant austenitic stainless steels. Phase equilibria studies indicated that NbC precipitates in combination with Fe2Nb were of limited benefit to creep resistance due to the solution limit of NbC within the γ-Fe matrix of the alloys studied. However, when combined with other MC-type strengtheners, such as V4C3 or TiC, higher levels of creep resistance were obtained.

Highly corrosive and high strength Cr-Mn series austenite sintered steel, method of manufacturing the same and the usage

International Nuclear Information System (INIS)

Arai, Masahiko; Hirano, Tatsumi; Aono, Yasuhisa; Kato, Takahiko; Kondo, Yasuo; Inagaki, Masatoshi

1998-01-01

The steel of the present invention comprises a highly corrosive and high strength Cr-Mn series austenite sintered steel containing up to 0.1% of C, up to 1% of Si, up to 0.4% of N, from 9 to 25% of (Mn + Ni) within a range of more than 2% and up to 15% of Mn and from 14 to 20% of Cr, and it has an average crystal grain size of 1μm or less and comprises at least 90 vol% of an austenite phase. In addition, the alloy is incorporated with one or more elements of up to 3% of Mo, 1.0% of Ti, up to 2.0% of Zr and up to 1.0% of Nb in an amount of up to 2.0% in total of Ti, Zr and Nb. When these materials are used under the circumstance where materials are generally deteriorated in grain boundaries, since they are excellent in corrosion resistance and strength, remarkable effects can be attained in the improvement of the safety and the reliability of products. In addition, they are applied not only to a reactor core but also to a water-cooled circumstance and a circumstance where hydrogen exists, thereby capable of exhibiting remarkable effects. (T.M.)

Use of overlapped reflection for determining the retained austenite by X-ray diffraction

International Nuclear Information System (INIS)

Garin, J.L.; Gonzalez, C.F.

1988-01-01

Retainec austenite in high-carbon steels has been determined by means of new computation techniques applied to the processing of X-ray diffraction data. Instead of using the traditional procedure based on the weak (200) reflections of martensite and austenite, intensity measurements of the overlapped (110) peak of martensite and (111) peak of austenite were performed. The separation of the peaks was based on a Pearson VII function, which is capable of describing all diffraction profiles. The accuracy of integrated intensities was then improved with the beneficial effects of higher precision in the calculation of the amount of retained austenite. (author) [pt

Phase transformation system of austenitic stainless steels obtained by permanent compressive strain

Energy Technology Data Exchange (ETDEWEB)

Okayasu, Mitsuhiro, E-mail: mitsuhiro.okayasu@utoronto.ca; Tomida, Sai

2017-01-27

In order to understand more completely the formation of strain-induced martensite, phase structures were investigated both before and after plastic deformation, using austenitic stainless steels of various chemical compositions (carbon C=0.007–0.04 mass% and molybdenum Mo=0–2.10 mass%) and varying pre-strain levels (0–30%). Although the stainless steels consisted mainly of γ austenite, two martensite structures were generated following plastic deformation, comprising ε and α′ martensite. The martensitic structures were obtained in the twin deformation and slip bands. The severity of martensite formation (ε and α′) increased with increasing C content. It was found that α′ martensite was formed mainly in austenitic stainless steel lacking Mo, whereas a high Mo content led to a strong ε martensite structure, i.e. a weak α′ martensite. The formation of α′ martensite occurred from γ austenite via ε martensite, and was related to the slip deformation. Molybdenum in austenitic stainless steel had high slip resistance (or weak stress-induced martensite transformation), because of the stacking fault energy of the stainless steel affecting the austenite stability. This resulted in the creation of weak α′ martensite. Models of the martensitic transformations γ (fcc)→ε (hcp)→α′ (bcc) were proposed on both the microscopic and nanoscopic scales. The α′ martensite content of austenitic stainless steel led to high tensile strength; conversely, ε martensite had a weak effect on the mechanical strength. The influence of martensitic formation on the mechanical properties was evaluated quantitatively by statistical analysis.

Dualism of precipitation morphology in high strength low alloy steel

International Nuclear Information System (INIS)

Chih-Yuan, Chen; Chien-Chon, Chen; Jer-Ren, Yang

2015-01-01

While the role of microalloying elements on precipitation strengthening in ferrite matrix during austenite/ferrite transformation is quite clear, some uncertainty still exists concerning the variability of the microhardness distribution of ferrite grains in the isothermal holding condition. The objective of the present study was to clarify the intrinsic characteristics of carbide precipitation morphology in the ferrite matrix under different processing temperatures and times and to correlate it with austenite decomposition kinetics to elucidate why a large microhardness distribution occurs at low isothermal holding temperature. Better understanding of carbide precipitation behavior can help researchers to determine the root cause of variation in microhardness distribution, which would allow metallurgists to produce high quality steels. Measurement with a Vickers hardness indenter revealed that, in specimens isothermally held at 625 °C, the range of Vickers hardness distribution was 240–420 after 5 min of isothermal holding, and 270–340 after 60 min. For specimens isothermally held at 725 °C, the range of Vickers hardness distribution was 200–330 for 5 min of isothermal holding, and 200–250 for 60 min. Therefore, the average microhardness decreased with the isothermal holding temperature and time, and a larger range of distribution occurred with short isothermal holding times. Transmission electron microscopy (TEM) images showed that interface precipitation and random precipitation can occur within the same ferrite grain. The reason is that the austenite decomposition rate varies with transformation temperature and time. An excessively fast austenite/ferrite interface movement velocity, which usually happens in small ferrite grains, would cause these ferrite grains with microalloying elements to exceed their solubility. Furthermore, these microalloying elements will be precipitated randomly after isothermal holding at longer times. Consequently, a large

Dualism of precipitation morphology in high strength low alloy steel

Energy Technology Data Exchange (ETDEWEB)

Chih-Yuan, Chen, E-mail: chen6563@gmail.com [Department of Energy Engineering, National United University, Miaoli 36003, Taiwan (China); Department of Materials Science and Engineering, National Taiwan University, Taipei 10617, Taiwan (China); Chien-Chon, Chen [Department of Energy Engineering, National United University, Miaoli 36003, Taiwan (China); Jer-Ren, Yang, E-mail: jryang@ntu.edu.tw [Department of Materials Science and Engineering, National Taiwan University, Taipei 10617, Taiwan (China)

2015-02-25

While the role of microalloying elements on precipitation strengthening in ferrite matrix during austenite/ferrite transformation is quite clear, some uncertainty still exists concerning the variability of the microhardness distribution of ferrite grains in the isothermal holding condition. The objective of the present study was to clarify the intrinsic characteristics of carbide precipitation morphology in the ferrite matrix under different processing temperatures and times and to correlate it with austenite decomposition kinetics to elucidate why a large microhardness distribution occurs at low isothermal holding temperature. Better understanding of carbide precipitation behavior can help researchers to determine the root cause of variation in microhardness distribution, which would allow metallurgists to produce high quality steels. Measurement with a Vickers hardness indenter revealed that, in specimens isothermally held at 625 °C, the range of Vickers hardness distribution was 240–420 after 5 min of isothermal holding, and 270–340 after 60 min. For specimens isothermally held at 725 °C, the range of Vickers hardness distribution was 200–330 for 5 min of isothermal holding, and 200–250 for 60 min. Therefore, the average microhardness decreased with the isothermal holding temperature and time, and a larger range of distribution occurred with short isothermal holding times. Transmission electron microscopy (TEM) images showed that interface precipitation and random precipitation can occur within the same ferrite grain. The reason is that the austenite decomposition rate varies with transformation temperature and time. An excessively fast austenite/ferrite interface movement velocity, which usually happens in small ferrite grains, would cause these ferrite grains with microalloying elements to exceed their solubility. Furthermore, these microalloying elements will be precipitated randomly after isothermal holding at longer times. Consequently, a large

A new effect of retained austenite on ductility enhancement in high strength bainitic steel

Energy Technology Data Exchange (ETDEWEB)

Wang Ying; Zhang Ke; Guo Zhenghong; Chen Nailu [School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Rong Yonghua, E-mail: yhrong@sjtu.edu.cn [School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China)

2012-08-30

Highlights: Black-Right-Pointing-Pointer A new DARA effect in the bainitic steel is proposed. Black-Right-Pointing-Pointer The conditions of DARA effect are proposed. Black-Right-Pointing-Pointer The mechanism of retained austenite on ductility enhancement is clarified. - Abstract: A designed high strength bainitic steel with considerable amount of retained austenite is presented in order to study the effect of retained austenite on the ductility enhancement in bainitic steels. Transformation induced plasticity (TRIP) effect is verified by both X-ray diffraction (XRD) measurement of retained austenite fraction in various deformation stages and transmission electron microscopy observation of the deformed twin-type martensite. Results from XRD line profile analysis reveal that the average dislocation density in bainite during the deformation is lower than that before deformation, and such a phenomenon can be explained by a new effect, dislocations absorption by retained austenite (DARA) effect, based on our previous investigation of martensitic steels. DARA effect availably enhances the compatibility of deformation ability of bainite with retained austenite. In view of microstructure similarity of bainitic steels with martensitic steels, the conditions of DARA effect are proposed. The effects of retained austenite on the ductility enhancement in bainitic steels are clarified.

Low ductility creep failure in austenitic weld metals

International Nuclear Information System (INIS)

Thomas, R.G.

Creep tests have been carried out for times of up to approx. 22,000 hrs on three austenitic weld metals of nominal composition 17Cr-8Ni-2Mo, 19Cr-12Ni-3Mo+Nb and 17Cr-10Ni-2Mo. The two former deposits were designed to produce delta-ferrite contents in the range 3-9% while the latter was designed to be fully austenitic. The common feature of all three weld metals was that they all gave very low strains at failure, typically approx. 1%. The microstructures of the failed creep specimens have been studied using optical and electron microscopy and the precipitate structures related to the occurrence of low creep strains. Creep deformation and fracture mechanisms in austenitic materials in general have been reviewed and this has been used as a basis for discussion of the observations of the present work. Finally, some of the factors that can be controlled to improve long-term creep ductility have been appraised

Effect of ageing on the microstructural stability of cold-worked titanium-modified 15Cr-15Ni-2.5Mo austenitic stainless steel

International Nuclear Information System (INIS)

Venkadesan, S.; Bhaduri, A.K.; Rodriguez, P.; Padmanabhan, K.A.

1992-01-01

A titanium-modified 15Cr-15Ni-2.5Mo austenitic stainless steel conforming to ASTM A 771 (UNS S 38660), commercially called Alloy D9, is being indigenously developed for application as material for the fuel clad and the hexagonal wrapper for fuel subassemblies of the Prototype Fast Breeder Reactor. As this material would be used in the cold-worked condition and would be subjected to prolonged exposure to elevated service temperatures, the effect of ageing on the microstructural stability was studied as a function of the amount of cold work. The material was given 2.5-30% prior cold work and then aged at temperatures in the range 923 to 1173 K for times ranging from 0.25 to 1000 h. Hardness measurements made before and after ageing were correlated with the Larson-Miller parameter to determine the highest stable prior cold-work level. Optical microscopy was used to study the microstructural changes. The influence of prolonged exposure for two and three years at the operating temperatures of clad and wrapper, on the elevated temperature tensile properties of a 20% prior cold-worked Alloy D9 was also studied through accelerated ageing treatments based on the present parametric approach. (orig.)

Effect of Long-Term Thermal Exposures on Microstructure and Impression Creep in 304HCu Grade Austenitic Stainless Steel

Science.gov (United States)

Dash, Manmath Kumar; Karthikeyan, T.; Mythili, R.; Vijayanand, V. D.; Saroja, S.

2017-10-01

This paper presents the results of microstructural evolution and mechanical properties in 304H Cu grade austenite stainless (SS 304HCu) during long-term exposure at high temperatures. The predicted phase composition as a function of temperature obtained using JMatPro® software was confirmed in conjunction with the microstructural evolution characterized by scanning and transmission electron microscopy. Microstructures revealed primary Nb(C,N), M23C6 precipitates at γ-grain boundaries, fine secondary Nb(C,N) intragranular carbides, and a uniform precipitation of <40-nm-sized spherical Cu-rich phase after thermal aging for 10,000 hours at 903 K (630 °C). The impression creep rate at 300 MPa increased by a factor of 20 between 873 K and 923 K (600 °C and 650 °C). The creep rate at 903 K (630 °C) was found to moderately reduce with aging time, signifying the role of Cu-rich phase in improving the creep resistance. The deformation zones and the recrystallization behavior of the plastic zone in creep tested specimen was assessed using Electron backscatter diffraction technique.

Structure-property relationships for n-alkyl-isocyanate-containing polymers

Science.gov (United States)

Aronson, Carl Lawrence

-NMR spectra of PBCHIC revealed perturbations to the helical polymer backbone structure. The wide angle x-ray diffraction pattern for the n-hexyl isocyanate containing polymers was found to be a function of DC electric field strength applied during isothermal crystallization from solution. The PHIC, backbone was protonated on a small percentage of monomer units by reaction with BF3 and H2O with no detectable chain scission but a loss of lyotropic liquid crystallinity. Methyl-N-(1,1-dimetboxyperfluroro- n-heptyl)carbamate was isolated from the reaction of perfluoro- n-heptyl isocyanate with excess methanol. 2,5-Dioxahexyl isocyanate and 2,5,8-trioxanonyl isocyanate were synthesized.

Effect of Isothermal Aging on the Long-Term Reliability of Fine-Pitch Sn-Ag-Cu and Sn-Ag Solder Interconnects With and Without Board-Side Ni Surface Finish

Science.gov (United States)

Lee, Tae-Kyu; Duh, Jeng-Gong

2014-11-01

The combined effects on long-term reliability of isothermal aging and chemically balanced or unbalanced surface finish have been investigated for fine-pitch ball grid array packages with Sn-3.0Ag-0.5Cu (SAC305) (wt.%) and Sn-3.5Ag (SnAg) (wt.%) solder ball interconnects. Two different printed circuit board surface finishes were selected to compare the effects of chemically balanced and unbalanced structure interconnects with and without board-side Ni surface finish. NiAu/solder/Cu and NiAu/solder/NiAu interconnects were isothermally aged and thermally cycled to evaluate long-term thermal fatigue reliability. Weibull plots of the combined effects of each aging condition and each surface finish revealed lifetime for NiAu/SAC305/Cu was reduced by approximately 40% by aging at 150°C; less degradation was observed for NiAu/SAC305/NiAu. Further reduction of characteristic life-cycle number was observed for NiAu/SnAg/NiAu joints. Microstructure was studied, focusing on its evolution near the board and package-side interfaces. Different mechanisms of aging were apparent under the different joint configurations. Their effects on the fatigue life of solder joints are discussed.

A study of the carbon distribution in retained austenite

International Nuclear Information System (INIS)

Scott, C.P.; Drillet, J.

2007-01-01

Cold-rolled and annealed transformation-induced plasticity (TRIP) steels were overaged to modify the carbon concentrations (C γ ) in retained austenite. Experimental C γ values were directly obtained by electron energy loss spectroscopy and compared with data derived from X-ray diffraction measurements of the austenite lattice parameter (a γ ). In this way, we evaluated the different expressions available in the literature relating C γ to a γ

Simulation of radiation induced segregation and PWSCC susceptibility for austenitic stainless steels

Energy Technology Data Exchange (ETDEWEB)

Fujimoto Koji; Yonezawa, Toshio; Iwamura, Toshihiko [Mitsubishi Heavy Industries Ltd., Takasago, Hyogo (Japan). Takasago R and D Center; Ajiki, Kazuhide [Mitsubishi Heavy Industries Ltd., Kobe (Japan). Kobe Shipyard and Machinery Works; Urata, Sigeru [General Office of Nuclear and Fossil Power Production, Kansai Electric Power Co., Inc., Osaka (Japan)

2000-08-01

Recently, irradiation assisted stress corrosion cracking (IASCC) of austenitic stainless steels for core internal components materials become a subject of discussion in light water reactors (LWRs). IASCC has not been found in Pressurized Water Reactors (PWRs). However, the authors have investigated on the possibility of IASCC of austenitic stainless steels for core internal materials so as to be able to estimate the degradation of PWR plants up to the end of their lifetime. In this study, in order to verify the hypothetical that the IASCC in PWRs shall be caused by the primary water stress corrosion cracking (PWSCC) as a result of radiation induced segregation (RIS) at grain boundaries, the authors simulated RIS at grain boundaries of austenitic stainless steels based on previous study and estimated RIS tendency after long time operation. And the authors melted the test alloys whose bulk compositions simulated the grain boundary compositions of irradiated austenitic stainless steels and made clear chromium-nickel-silicon compositions for PWSCC susceptibility area in austenitic alloys by slow strain rate tensile (SSRT) test. (author)

Simulation of radiation induced segregation and PWSCC susceptibility for austenitic stainless steels

International Nuclear Information System (INIS)

Fujimoto Koji; Yonezawa, Toshio; Iwamura, Toshihiko

2000-01-01

Recently, irradiation assisted stress corrosion cracking (IASCC) of austenitic stainless steels for core internal components materials become a subject of discussion in light water reactors (LWRs). IASCC has not been found in Pressurized Water Reactors (PWRs). However, the authors have investigated on the possibility of IASCC of austenitic stainless steels for core internal materials so as to be able to estimate the degradation of PWR plants up to the end of their lifetime. In this study, in order to verify the hypothetical that the IASCC in PWRs shall be caused by the primary water stress corrosion cracking (PWSCC) as a result of radiation induced segregation (RIS) at grain boundaries, the authors simulated RIS at grain boundaries of austenitic stainless steels based on previous study and estimated RIS tendency after long time operation. And the authors melted the test alloys whose bulk compositions simulated the grain boundary compositions of irradiated austenitic stainless steels and made clear chromium-nickel-silicon compositions for PWSCC susceptibility area in austenitic alloys by slow strain rate tensile (SSRT) test. (author)

On the measurement of austenite in supermartensitic stainless steel by X-ray diffraction

Energy Technology Data Exchange (ETDEWEB)

Tolchard, Julian Richard, E-mail: tolchard@material.ntnu.no [Department of Materials Science and Engineering, Norwegian University of Science and Technology, Trondheim (Norway); Sømme, Astri; Solberg, Jan Ketil [Department of Materials Science and Engineering, Norwegian University of Science and Technology, Trondheim (Norway); Solheim, Karl Gunnar [Statoil, Stavanger (Norway)

2015-01-15

Sections of a 13Cr supermartensitic stainless steel were investigated to determine the optimum sample preparation for measurement of the austenite content by X-ray diffraction. The surface of several samples was mechanically ground or polished using media of grit sizes in the range 1–120 μm. The strained surface layer was afterwards removed stepwise by electropolishing, and the austenite content measured at each step. It was found that any level of mechanical grinding or polishing results in a reduction of the measured austenite fraction relative to the true bulk value, and that coarser grinding media impart greater damage and greater reduction in the measured austenite content. The results thus highlight the importance of the electropolishing step in preparation of such samples, but suggest that the American Society for Testing and Materials standard E975-03 substantially overestimates the amount of material which needs to be removed to recover the true “bulk” content. - Highlights: • Quantitative Rietveld analysis of austenite/martensite ratio in supermartensitic stainless steels • Critical evaluation of sample preparation for residual austenite measurements by X-ray diffraction • Highlighting of the importance of electropolishing as a final preparation step.

Evaluation of High Temperature Corrosion Resistance of Finned Tubes Made of Austenitic Steel And Nickel Alloys

Directory of Open Access Journals (Sweden)

Turowska A.

2016-06-01

Full Text Available The purpose of the paper was to evaluate the resistance to high temperature corrosion of laser welded joints of finned tubes made of austenitic steel (304,304H and nickel alloys (Inconel 600, Inconel 625. The scope of the paper covered the performance of corrosion resistance tests in the atmosphere of simulated exhaust gases of the following chemical composition: 0.2% HCl, 0.08% SO2, 9.0% O2 and N2 in the temperature of 800°C for 1000 hours. One found out that both tubes made of austenitic steel and those made of nickel alloy displayed good resistance to corrosion and could be applied in the energy industry.

Effect of small addition of Cr on stability of retained austenite in high carbon steel

Energy Technology Data Exchange (ETDEWEB)

Hossain, Rumana; Pahlevani, Farshid, E-mail: f.pahlevani@unsw.edu.au; Sahajwalla, Veena

2017-03-15

High carbon steels with dual phase structures of martensite and austenite have considerable potential for industrial application in high abrasion environments due to their hardness, strength and relatively low cost. To design cost effective high carbon steels with superior properties, it is crucial to identify the effect of Chromium (Cr) on the stability of retained austenite (RA) and to fully understand its effect on solid-state phase transition. This study addresses this important knowledge gap. Using standard compression tests on bulk material, quantitative X-ray diffraction analysis, nano-indentation on individual austenitic grains, transmission electron microscopy and electron backscatter diffraction–based orientation microscopy techniques, the authors investigated the effect of Cr on the microstructure, transformation behaviour and mechanical stability of retained austenite in high carbon steel, with varying Cr contents. The results revealed that increasing the Cr %, altered the morphology of the RA and increased its stability, consequently, increasing the critical pressure for martensitic transformation. This study has critically addressed the elastoplastic behaviour of retained austenite – and provides a deep understanding of the effect of small additions of Cr on the metastable austenite of high carbon steel from the macro- to nano-level. Consequently, it paves the way for new applications for high carbon low alloy steels. - Highlights: • Effect of small addition of Cr on metastable austenite of high carbon steel from the macro- to nano-level • A multi-scale study of elastoplastic behaviour of retained austenite in high carbon steel • The mechanical stability of retained austenite during plastic deformation increased with increasing Cr content • Effect of grain boundary misorientation angle on hardness of individual retained austenite grains in high carbon steel.

Inter granular stress corrosion cracking of Ignalina NPP austenitic piping of outside diameter 325 mm

International Nuclear Information System (INIS)

Nedzinskas, L.; Klimasauskas, A.

2003-01-01

The Inter Granular Stress Corrosion Cracking (IGSCC) of Ignalina NPP main circulation circuit piping, produced from austenitic stainless steel is presented covering current performances and further 'Ageing Management' related actions and plans as well as experience (lessons learned) on solving IGSCC phenomenon, which is currently under investigations and no yet comprehensive answer how to avoid it. (author)

Longitudinal wave ultrasonic inspection of austenitic weldments

International Nuclear Information System (INIS)

Gray, B.S.; Hudgell, R.J.; Seed, H.

1980-01-01

Successful volumetric inspection of LMFBR primary circuits, and also much of the secondary circuit, is dependent on the availability of satisfactory examination procedures for austenitic welds. Application of conventional ultrasonic techniques is hampered by the anisotropic, textured structure of the weld metal and this paper describes development work on the use of longitudinal wave techniques. In addition to confirming the dominant effects of the weld structure on ultrasound propagation some results are given of studies utilising deliberately induced defects in Manual Metal Arc Welds in 50 mm plate together with preliminary work on the inspection of narrow austenitic welds fabricated by automatic processes. (author)

Effect of multiple austenitizing treatments on HT-9 steels

International Nuclear Information System (INIS)

Emigh, R.A.

1985-12-01

The effect of multiple austenitizing treatments on the toughness of an Fe-12Cr-1.0Mo-0.5W-0.3V (HT-9) steel was studied. The resulting microstructures were characterized by their mechanical properties, precipitated carbide distribution, and fracture surface appearance. It was proposed that multiple transformations would refine the martensite structure and improve toughness. Optical and scanning electron microscopic observations revealed that the martensite packet structure was somewhat refined by a second austenite transformation. Transmission electron microscopy studies of carbon extraction replicas showed that this multiple step treatment had eliminated grain boundary carbide films seen in single treated specimens on prior austenite grain boundaries. The 0.2% yield strength, tensile strength, and elongation were relatively unchanged, but the toughness measured by fatigue pre-cracked Charpy impact tests increased for the multiple step specimens

Demonstrating the Effect of Precipitation on the Mechanical Stability of Fine-Grained Austenite in Reversion-Treated 301LN Stainless Steel

Directory of Open Access Journals (Sweden)

Antti Järvenpää

2017-09-01

Full Text Available According to recent investigations, a huge difference exists in the mechanical stability of austenite between the grain-refined structure states obtained in reversion annealing at 800–700 °C or at 900 °C, in a 301LN type austenitic stainless steel. Precipitation of chromium nitride occurring at these lower temperatures has been argued to be the factor reducing the stability. To prove this argument, a fine-grained, very stable austenitic structure was created at 900 °C in 1 s, and subsequently annealed at lower temperatures between 850 and 750 °C, up to 1000 s. It was found that the subsequent annealing at 750 and 800 °C resulted in prominent gradual decrease of the mechanical stability under tensile straining, detectable after 10 s annealing duration and continued until 1000 s. Only minimal grain growth occurred, which decreased the stability very marginally. The degree of the stability drop followed the predicted kinetics of the Cr2N precipitation with regards as its dependence on annealing duration and temperature. Further, the tensile yield strength of the fine-grained structure increased slightly due to the annealing. The presence of nano-sized Cr2N particles was verified after 1000 s holding at 750 °C. These observations and predictions yield firm evidence for the imperative contribution of precipitation to the highly reduced mechanical stability of grain-refined austenite in this steel.

Container for shipping dangerous material

International Nuclear Information System (INIS)

Blum, P.T.

1987-01-01

This container for shipping dangerous material is made by a cylindrical casing of austenitic stainless steel with rounded ends and walls of uniform thickness with welded joins, a tubular metal shock absorber fixed over each end of the casing, removable lugs fixed to the casing, optionally retainers for the material within the casing [fr

Influence of Thermal Aging on Primary Water Stress Corrosion Cracking of Cast Duplex Stainless Steels

International Nuclear Information System (INIS)

Yamada, T.; Totsuka, N.; Nakajima, N.; Arioka, K.; Negishi, K.

2002-01-01

In order to evaluate the SCC (stress corrosion cracking) susceptibility of cast duplex stainless steels which are used for the main coolant piping material of pressurized water reactors (PWRs), the slow strain rate test (SSRT) and the constant load test (CLT) were performed in simulated PWR primary water at 360 C. The main coolant piping materials contain ferrite phase with ranging from 8 to 23 % and its mechanical properties are affected by long time thermal aging. The 23% ferrite material was prepared for test as the maximum ferrite content of main coolant pipes in Japanese PWRs. The brittle fracture in the non-aged materials after SSRT is mainly caused by quasi-cleavage fracture in austenitic phase. On the other hand, a mixture of quasi-cleavage fracture in austenite and ferrite phases was observed on long time aged material. Also on CLT, (2 times σ y ), after 3,000 hours exposure, microcracks were observed on the surface of non-aged and aged for 10,000 hours at 400 C materials. The crack initiation site of CLT is similar to that of SSRT. The SCC susceptibility of the materials increases with aging time. It is suggested that the ferrite hardening with aging affect SCC susceptibility of cast duplex stainless steels. (authors)

Ultrasonic inspection of austenitic welds

Energy Technology Data Exchange (ETDEWEB)

Tomlinson, J R; Wagg, A R; Whittle, M J [N.D.T. Applications Centre, CEGB, Manchester (United Kingdom)

1980-11-01

The metallurgical structure of austenitic welds is described and contrasted with that found in ferritic welds. It is shown that this structure imparts a marked elastic anisotropy in the ultrasonic propagation parameters. Measurements of variations in the apparent attenuation of sound and deviations in the beam direction are described. The measurements are interpreted in terms of the measured velocity anisotropy. Two applications of the fundamental work are described. In the first it is shown how, by using short pulse compression wave probes, and with major modification of the welding procedure, a stainless steel fillet weld in an AGR boiler can be inspected. In the second application, alternative designs of a transition butt weld have been compared for ease of ultrasonic inspection. The effects of two different welding processes on such an inspection are described. Finally, the paper examines the prospects for future development of inspection and defect-sizing techniques for austenitic welds. (author)

Isothermal Martensite Formation

DEFF Research Database (Denmark)

Villa, Matteo

Isothermal (i.e. time dependent) martensite formation in steel was first observed in the 40ies of the XXth century and is still treated as an anomaly in the description of martensite formation which is considered as a-thermal (i.e. independent of time). Recently, the clarification of the mechanism...... of lattice strains provided fundamental information on the state of stress in the material and clarified the role of the strain energy on martensite formation. Electron backscatter diffraction revealed that the microstructure of the material and the morphology of martensite were independent on the cooling...... leading to isothermal kinetics acquired new practical relevance because of the identification of isothermal martensite formation as the most likely process responsible for enhanced performances of sub-zero Celsius treated high carbon steel products. In the present work, different iron based alloys...

Theoretical and experimental study of carburisation and decarburisation of a meta-stable austenitic steel

Directory of Open Access Journals (Sweden)

Charles West

2005-12-01

Full Text Available Metastable austenitic stainless steels are known to undergo a partial transformation of austenite to martensite as a consequence of plastic deformation. In the case of cyclic loading, a certain level of plastic strain must be exceeded, and phase formation takes place after an incubation period, during which the necessary amount of plastic deformation is accumulated. The susceptibility of the austenitic phase to deformation-induced martensite formation is strongly affected by the temperature of loading and the stability of austenite, which itself depends on the chemical composition. A key element in this regard is carbon which stabilizes the austenitic phase. It is shown in this study that the carbon concentration can be analysed systematically and reproducible by means of annealing treatments, if the parameters of these treatments are carefully defined on the basis of advanced theoretical thermodynamic and kinetic considerations. First results on the effect of carbon concentration and temperature of fatigue testing on the austenite/martensite transformation are presented, in order to illustrate the significance of these parameters on the martensite formation rate.

The effects of retained austenite on dry sliding wear behavior of carburized steels

Energy Technology Data Exchange (ETDEWEB)

Kim, Hyung-Jun [Research Inst. of Industrial Science and Technology, Steel Products Dept., Pohang (Korea, Republic of); Kweon, Young-Gak [Research Inst. of Industrial Science and Technology, Steel Products Dept., Pohang (Korea, Republic of)

1996-04-01

Ring-on-square tests on two kinds of low-alloy carburized steel which were AISI 8620 and 4140 were carried out to study the dry sliding wear behavior. The influence of different retained austenite level of 6% to 40% was evaluated while trying to eliminate other factors. Test results show that the effects of grain size and carburized steel species are negligible in dry sliding wear behavior. While the influence of retained austenite is negligible at 20 kg load condition, wear resistance is decreased at 40 kg load condition as the retained austenite level is increased from 6% to 30%. However, wear resistance is again increased above about 30% of retained austenite level at 40 kg load condition. (orig.)

Interaction between recrystallization and strain-induced precipitation in a high Nb- and N-bearing austenitic stainless steel: Influence of the interpass time

Energy Technology Data Exchange (ETDEWEB)

Silva, M.B.R., E-mail: marianabdrs@gmail.com [Department of Materials Engineering, UFSCar, Via Washington Luis, Km 235, 13565-905 São Carlos, SP (Brazil); Gallego, J. [Department of Mechanical Engineering, UNESP, Avenida Brasil, 56, 15385-000 Ilha Solteira, SP (Brazil); Cabrera, J.M. [Department of Materials Science and Metallurgical Engineering, Polytechnic University of Catalunya, Avenida Diagonal 647, 08028 Barcelona (Spain); Fundacio CTM Centre Tecnologic, Plaza de la Ciencia 2, 08243 Manresa (Spain); Balancin, O. [Department of Materials Engineering, UFSCar, Via Washington Luis, Km 235, 13565-905 São Carlos, SP (Brazil); Jorge, A.M., E-mail: moreira@dema.ufscar.br [Department of Materials Engineering, UFSCar, Via Washington Luis, Km 235, 13565-905 São Carlos, SP (Brazil)

2015-06-18

In this work, we studied the influence of the interpass time (20 and 5 s) on the interaction between recrystallization and strain-induced precipitation occurring during multiple passes' deformations under continuous cooling conditions in a high niobium- and nitrogen-bearing austenitic stainless steel (ISO 5832-9). The correlation between microstructure evolution and hot mechanical properties was performed by physical simulation using hot torsion tests. The microstructure evolution was analyzed by optical microscopy, transmission electron microscopy and electron back scattered diffraction (EBSD). This technique indicated that dynamic recrystallization occurred at the first passes promoting an excellent grain refinement. On the other hand, shorter interpass time (5 s) allowed higher volume fraction of smallest precipitates than larger interpass time (20 s). After soaking, only TiNbN precipitates were found, whereas, Z-phase (CrNbN) and NbN were formed during thermomechanical processing. Particles with sizes between 20 and 50 nm were effective to pin grain boundaries and dislocations.

SIMS analysis of deuterium absorption and diffusion in austenitic Fe-Mn-C steels

International Nuclear Information System (INIS)

Dieudonne, T.; Chene, J.; Marchetti, L.; Jomard, F.; Wery, M.; Allely, C.; Cugy, P.; Scott, C.P.

2012-01-01

Austenitic Fe-Mn-C steels are Ultra High Strength Steels which may be used for the production of deep drawn automotive parts containing extremely high residual stress and strain levels. In consequence, hydrogen absorption occurring during the corrosion process in aqueous environments may enhance the sensitivity of these steels to different kinds of hydrogen-induced damage, in particular Stress Corrosion Cracking (SCC). In order to predict and prevent SCC, it is important to study the behaviour of hydrogen in these austenitic steels exposed to aqueous environments and in particular the dependence on the alloy chemistry and microstructure. SIMS profiles of deuterium introduced by cathodic charging in selected specimens were used to characterize the diffusion of hydrogen in these steels. This allowed to be studied the role of chemical composition and microstructure on the kinetics of H absorption at room temperature. The competition between bulk matrix diffusion and short-circuit diffusion phenomena along grain boundaries was investigated. The results show a strong dependence of H diffusion and distribution on the alloy chemistry and grain size. (authors)

Effect of Nb and Cu on the high temperature creep properties of a high Mn–N austenitic stainless steel

International Nuclear Information System (INIS)

Lee, Kyu-Ho; Suh, Jin-Yoo; Huh, Joo-Youl; Park, Dae-Bum; Hong, Sung-Min; Shim, Jae-Hyeok; Jung, Woo-Sang

2013-01-01

The effect of Nb and Cu addition on the creep properties of a high Mn–N austenitic stainless steel was investigated at 600 and 650 °C. In the original high Mn–N steel, which was initially precipitate-free, the precipitation of M 23 C 6 (M = Cr, Fe) and Cr 2 N took place mostly on grain boudaries during creep deformation. On the other hand, the minor addition of Nb resulted in high number density of Z-phases (CrNbN) and MX (M = Nb; X = C, N) carbonitrides inside grains by combining with a high content of N, while suppressing the formation of Cr 2 N. The addition of Cu gave rise to the independent precipitation of nanometer-sized metallic Cu particles. The combination of the different precipitate-forming mechanisms associated with Z-phase, MX and Cu-rich precipitates turned out to improve the creep-resistance significantly. The thermodynamics and kinetics of the precipitation were discussed using thermo-kinetic simulations. - Highlights: • The creep rupture life was improved by Nb and Cu addition. • The creep resistance of the steel A2 in this study was comparable to that of TP347HFG. • The size of Z-phase and MX carbonitride did not change significantly after creep test. • The nanometer sized Cu-rich precipitate was observed after creep. • The predicted size of precipitates by MatCalc agreed well with measured size

Precipitation evolution in a Ti-free and Ti-containing stainless maraging steel

International Nuclear Information System (INIS)

Schober, M.; Schnitzer, R.; Leitner, H.

2009-01-01

Stainless maraging steels have a Cr content higher than 12 wt% and show a excellent combination of high strength and ductility, which make them attractive for use in machinery fields and aircraft applications. The massive increase of strength during ageing treatment of maraging steels is related to a precipitation sequence of various nm-scaled intermetallic phases. The peak hardness especially in Ti-containing maraging steels can be reached after short-time ageing at temperatures around 500 o C. However, precipitation reactions in different stainless maraging steels are not fully understood, especially the evolution from clustering over growing to coarsening. In the present work a commercial maraging steel and a Ti-containing model alloy are investigated and compared to each other. The steels were isothermally heat treated at 525 o C for a range of times. Special emphasis was laid on the correlation of hardness to the formation and presence of different kinds of precipitates. The isothermal aged samples were investigated by using two advanced three-dimensional energy compensated atom probes (LEAP TM and 3DAP TM ) both in voltage mode and in laser mode. The atom probe data were correlated to standard hardness measurements. The results show that the partial substitution of Al by Ti results in a different precipitation behaviour. While the Ti-free maraging steel exhibit only one type of precipitate, the Ti-containing grade shows a change in the type of precipitates during ageing. However, this change leads to an accelerated coarsening and thus to a faster drop in hardness.

Precipitation evolution in a Ti-free and Ti-containing stainless maraging steel.

Science.gov (United States)

Schober, M; Schnitzer, R; Leitner, H

2009-04-01

Stainless maraging steels have a Cr content higher than 12wt% and show a excellent combination of high strength and ductility, which make them attractive for use in machinery fields and aircraft applications. The massive increase of strength during ageing treatment of maraging steels is related to a precipitation sequence of various nm-scaled intermetallic phases. The peak hardness especially in Ti-containing maraging steels can be reached after short-time ageing at temperatures around 500 degrees C. However, precipitation reactions in different stainless maraging steels are not fully understood, especially the evolution from clustering over growing to coarsening. In the present work a commercial maraging steel and a Ti-containing model alloy are investigated and compared to each other. The steels were isothermally heat treated at 525 degrees C for a range of times. Special emphasis was laid on the correlation of hardness to the formation and presence of different kinds of precipitates. The isothermal aged samples were investigated by using two advanced three-dimensional energy compensated atom probes (LEAP and 3DAP) both in voltage mode and in laser mode. The atom probe data were correlated to standard hardness measurements. The results show that the partial substitution of Al by Ti results in a different precipitation behaviour. While the Ti-free maraging steel exhibit only one type of precipitate, the Ti-containing grade shows a change in the type of precipitates during ageing. However, this change leads to an accelerated coarsening and thus to a faster drop in hardness.

Comparison of high temperature steam oxidation behavior of Zircaloy-4 versus austenitic and ferritic steels under light water reactor safety aspects

International Nuclear Information System (INIS)

Leistikow, S.; Schanz, G.; Zurek, Z.

1985-12-01

A comparative study of the oxidation behavior of Zy-4 versus steel No. 1.4914 and steel No. 1.4970 was performed in high temperature steam. Reactor typical tube sections of all three materials were exposed on both sides to superheated steam at temperatures ranging from 600 to 1300 0 C for up to 6 h. The specimens were evaluated by gravimetry, metallography, and other methods. The results are presented in terms of weight gain, corresponding metal (wall) penetration and consumption as function of time and temperature. Concerning the corrosion resistance the ranking position of Zy-4 was between the austenitic and the ferritic steel. Because of the chosen wall dimensions Zy-4 and the austenitic steel behaved similarly in that the faster oxidation of the thicker Zy-4 cladding consumed the total wall thickness in a time equivalent to the slower oxidation of the thinner austenitic steel cladding. The ferritic steel cladding however was faster consumed because of the lower oxidation resistance and the thinner wall thickness compared to the austenitic steel. So besides oxide scale formation, oxygen diffusion into the bulk of the metal forming various oxygen-containing phases were evaluated - also in respect to their influence on mechanical cladding properties and the dimensional changes. (orig./HP) [de

Analysis of creep effective stress in austenitic heat resistant steel

International Nuclear Information System (INIS)

Park, In Duck; Nam, Ki Woo

2002-01-01

This paper describes the comparison of calculated effective stress with experimental one in austenitic heat resistant steels, STS310J1TB and STS310S with and without a small amount of Nb and N. Based on a solute atoms diffusion model, contribution from soluble nitrogen to the high-temperature strength was numerically examined for austenitic heat-resisting Fe-Cr-Ni-N(STS310J1TB) and Fe-Cr-Ni(STS310S) alloys. The solute atmosphere dragging stress of dislocation was calculated in optional dislocation velocity of STS310J1TB and STS310S at 650 degree C, 675 degree C and 700 degree C. As a result of the numerical calculation, the solute atmosphere dragging stress of STS310J1TB was about 50 times larger than that of STS310S. When the temperature became high, the maximum value of solute atmosphere dragging stress was small and the velocity of moving dislocation was fast. From the relationship between the dislocation rate and the solute atmosphere dragging stress, the relation of both was proportional and the inclination is about 1 in the level with low velocity of moving dislocation. From above results, the mechanism of dislocation movement in STS310J1TB was the solute atmosphere dragging stress. The solute atmosphere dragging stress, which was calculated from the numerical calculation was close to the effect stress in stress relaxation tests

Effect of the low temperature ion nitriding on the wear and corrosion resistance of 316L austenitic stainless steel biomaterials

International Nuclear Information System (INIS)

Sudjatmoko; Bambang Siswanto; Wirjoadi; Lely Susita RM

2012-01-01

In the present study has been completed done the ion nitriding process and characterization of the 316L SS samples. The ion nitriding process has been conducted on the samples for nitriding temperature variation of 350, 400, 450, 500, and 550 °C, the optimum nitrogen gas pressure of 1.8 mbar and optimum nitriding time of 3 hours. The micro-structure, elemental composition and the phase structure of the nitride layer formed on the surface of samples were observed using the techniques of SEM-EDAX and XRD, respectively. It is known that a thin layer of iron nitrides has been formed on the surface of the samples. Iron nitride layer has a phase structure including ε-Fe_2_-_3N, γ'-Fe_4N, CrN, Cr_2N and expanded austenite γN. The characterization results of the wear resistance of the 316L SS samples showed an increasing of about 2.6 times the wear resistance of standard samples after nitriding temperature of 350 °C. From the corrosion test by using the Hanks solution was obtained 29.87 mpy corrosion rate or the increasing of corrosion resistance of about 137%. Thus it can be seen that by using ion nitriding technique the iron nitride layer has been formed on the surface of the 316L SS samples, and they have an excellent properties of wear resistance and corrosion resistance, which were caused especially due to the formation of an expanded austenite γN. Properties of the high hardness and has the good corrosion resistance, especially due to the formation of iron nitride and expanded austenite phases γN at low temperature nitriding process. (author)

Tailoring plasticity of austenitic stainless steels for nuclear applications: Review of mechanisms controlling plasticity of austenitic steels below 400 °C

Energy Technology Data Exchange (ETDEWEB)

Meric de Bellefon, G., E-mail: mericdebelle@wisc.edu [University of Wisconsin-Madison (United States); Duysen, J.C. van [EDF R& D (France); University of Tennessee-Knoxville (United States); Unité Matériaux et Transformation (UMET) CNRS, Université de Lille (France)

2016-07-15

AISI 304 and 316 austenitic stainless steels were invented in the early 1900s and are still trusted by materials and mechanical engineers in numerous sectors because of their good combination of strength, ductility, and corrosion resistance, and thanks to decades of experience and data. This article is part of an effort focusing on tailoring the plasticity of both types of steels to nuclear applications. It provides a synthetic and comprehensive review of the plasticity mechanisms in austenitic steels during tensile tests below 400 °C. In particular, formation of twins, extended stacking faults, and martensite, as well as irradiation effects and grain rotation are discussed in details. - Highlights: • This article is part of an effort to tailor the plasticity of 304L and 316L steels for nuclear applications. • It reviews mechanisms controlling plasticity of austenitic steels during tensile tests. • Formation of twins, extended stacking faults, and martensite, grain rotation, and irradiation effects are discussed.

Irradiation-Assisted Stress Corrosion Cracking of Austenitic Stainless Steels in BWR Environments

International Nuclear Information System (INIS)

Chen, Y.; Chopra, O. K.; Gruber, Eugene E.; Shack, William J.

2010-01-01

The internal components of light water reactors are exposed to high-energy neutron irradiation and high-temperature reactor coolant. The exposure to neutron irradiation increases the susceptibility of austenitic stainless steels (SSs) to stress corrosion cracking (SCC) because of the elevated corrosion potential of the reactor coolant and the introduction of new embrittlement mechanisms through radiation damage. Various nonsensitized SSs and nickel alloys have been found to be prone to intergranular cracking after extended neutron exposure. Such cracks have been seen in a number of internal components in boiling water reactors (BWRs). The elevated susceptibility to SCC in irradiated materials, commonly referred to as irradiation-assisted stress corrosion cracking (IASCC), is a complex phenomenon that involves simultaneous actions of irradiation, stress, and corrosion. In recent years, as nuclear power plants have aged and irradiation dose increased, IASCC has become an increasingly important issue. Post-irradiation crack growth rate and fracture toughness tests have been performed to provide data and technical support for the NRC to address various issues related to aging degradation of reactor-core internal structures and components. This report summarizes the results of the last group of tests on compact tension specimens from the Halden-II irradiation. The IASCC susceptibility of austenitic SSs and heat-affected-zone (HAZ) materials sectioned from submerged arc and shielded metal arc welds was evaluated by conducting crack growth rate and fracture toughness tests in a simulated BWR environment. The fracture and cracking behavior of HAZ materials, thermally sensitized SSs and grain-boundary engineered SSs was investigated at several doses (3 dpa). These latest results were combined with previous results from Halden-I and II irradiations to analyze the effects of neutron dose, water chemistry, alloy compositions, and welding and processing conditions on IASCC. The

The Stellar IMF from Isothermal MHD Turbulence

Science.gov (United States)

Haugbølle, Troels; Padoan, Paolo; Nordlund, Åke

2018-02-01

We address the turbulent fragmentation scenario for the origin of the stellar initial mass function (IMF), using a large set of numerical simulations of randomly driven supersonic MHD turbulence. The turbulent fragmentation model successfully predicts the main features of the observed stellar IMF assuming an isothermal equation of state without any stellar feedback. As a test of the model, we focus on the case of a magnetized isothermal gas, neglecting stellar feedback, while pursuing a large dynamic range in both space and timescales covering the full spectrum of stellar masses from brown dwarfs to massive stars. Our simulations represent a generic 4 pc region within a typical Galactic molecular cloud, with a mass of 3000 M ⊙ and an rms velocity 10 times the isothermal sound speed and 5 times the average Alfvén velocity, in agreement with observations. We achieve a maximum resolution of 50 au and a maximum duration of star formation of 4.0 Myr, forming up to a thousand sink particles whose mass distribution closely matches the observed stellar IMF. A large set of medium-size simulations is used to test the sink particle algorithm, while larger simulations are used to test the numerical convergence of the IMF and the dependence of the IMF turnover on physical parameters predicted by the turbulent fragmentation model. We find a clear trend toward numerical convergence and strong support for the model predictions, including the initial time evolution of the IMF. We conclude that the physics of isothermal MHD turbulence is sufficient to explain the origin of the IMF.

Aging characteristics of containment building and sensitivity on ultimate pressure capacity

International Nuclear Information System (INIS)

Seo, Jeong Moon; Choun, Young Sun; Choi, In Kil; Ha, Jae Joo

1998-03-01

For the reliable safety assessment of the containment building, structural and material conditions can be investigated in detail and pertinent assessment technologies have to be established. Also, an understanding on the aging-related degradations for the construction materials is required to predict long-term structural safety of the containment building. For the development of reliable aging prediction models, an extensive data base system related to aging properties of the containment building has to be prepared. The objectives of this research are to develop aging models representing long-term degradation of materials and a structural performance assessment program for containment building considering aging-related degradation. According to the results of sensitivity analysis, as the mechanical properties of the constituent materials degrade, the ultimate pressure capacity of containment building may decrease and severe damage may occur around the mid-level of the containment wall. (author). 28 refs., 11 tabs., 36 figs

Consideration of the environmental effects on fatigue behavior of austenitic components. Calculation methods and practical application

International Nuclear Information System (INIS)

Seichter, Johannes; Reese, Sven H.; Klucke, Dietmar

2012-01-01

During the last years environmental effects on the fatigue behavior of nuclear power plant components has worldwide been discussed controversial with respect to the transferability of laboratory data on real components. A publication from Argonne National Laboratory on experimental results concerning environmental effects (air and LWR coolant) on fatigue of austenitic steels included a proposal on calculation methods concerning the lifetime reduction due to environmental effects. This calculation method, i.e. multiplication of the usage factor by a F(en), has been included into the ASME Code, Section III, Division I, as Code Case N-792 (fatigue evaluations including environmental effects). The presented contribution evaluates the practical application of this calculation procedure and demonstrates the determination of the usage factor of an austenitic component under environmental exposure.

Microstructure evolution of Fe-based nanostructured bainite coating by laser cladding

International Nuclear Information System (INIS)

Guo, Yanbing; Li, Zhuguo; Yao, Chengwu; Zhang, Ke; Lu, Fenggui; Feng, Kai; Huang, Jian; Wang, Min; Wu, Yixiong

2014-01-01

Highlights: • The laser cladding and isothermal holding are used to fabricate nanobainite coating. • Fine prior austenite is obtained to accelerate the bainite transformation. • Low transformation temperature results in fine bainite ferrite and film austenite. • Retained austenite volume fraction in bainite coating is determined by XRD. • Evolution of carbon content in austenite and ferrite is analyzed. - Abstract: A Fe-based coating with nano-scale bainitic microstructure was fabricated using laser cladding and subsequent isothermal heat treatment. The microstructure of the coating was observed and analyzed using optical microscope (OM), field-emission scanning electron microscope (FE-SEM), transmission electron microscope (TEM) and X-ray diffraction (XRD). The results showed that nanostructured bainitic ferrite and carbon-enriched retained austenite distributed uniformly in the coating. Blocky retained austenite was confined to the prior austenite grain boundaries resulting from the elements segregation. The bainitic microstructure obtained at 250 °C had a finer scale compared with that obtained at 300 °C. The volume fraction of austenite increased with increasing transformation temperature for the fully transformed bainitic coating. The bainitic transformation was accelerated as a result of the fine prior austenite generated during the laser cladding. The evolution of the carbon contents in bainitic ferrite and retained austenite revealed the diffusionless mechanism of the bainitic transformation

n-Type Azaacenes Containing B←N Units.

Science.gov (United States)

Min, Yang; Dou, Chuandong; Tian, Hongkun; Geng, Yanhou; Liu, Jun; Wang, Lixiang

2018-02-12

We disclose a novel strategy to design n-type acenes through the introduction of boron-nitrogen coordination bonds (B←N). We synthesized two azaacenes composed of two B←N units and six/eight linearly annelated rings. The B←N unit significantly perturbed the electronic structures of the azaacenes: Unique LUMOs delocalized over the entire acene skeletons and decreased aromaticity of the B←N-adjacent rings. Most importantly, these B←N-containing azaacenes exhibited low-lying LUMO energy levels and high electron affinities, thus leading to n-type character. The solution-processed organic field-effect transistor based on one such azaacene exhibited unipolar n-type characteristics with an electron mobility of 0.21 cm 2  V -1  s -1 . © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Study of Ferrite During Refinement of Prior Austenite Grains in Microalloyed Steel Continuous Casting

Science.gov (United States)

Liu, Jiang; Wen, Guanghua; Tang, Ping

2017-12-01

The formation of coarse prior austenite grain is a key factor to promote transverse crack, and the susceptibility to the transverse crack can be reduced by refining the austenite grain size. In the present study, the high-temperature confocal laser scanning microscope (CLSM) was used to simulate two types of double phase-transformation technologies. The distribution and morphology of ferrites under different cooling conditions were analyzed, and the effects of ferrite distribution and morphology on the double phase-transformation technologies were explored to obtain the suitable double phase-change technology for the continuous casting process. The results indicate that, under the thermal cycle TH0 [the specimens were cooled down to 913 K (640 °C) at a cooling rate of 5.0 K/s (5.0 °C/s)], the width of prior austenite grain boundaries was thick, and the dislocation density at grain boundaries was high. It had strong inhibition effect on crack propagation; under the thermal cycle TH1 [the specimens were cooled down to 1073 K (800 °C) at a cooling rate of 5.0 K/s (5.0 °C/s) and then to 913 K (640 °C) at a cooling rate of 1.0 K/s (1.0 °C/s)], the width of prior austenite grain boundary was thin, and the dislocation density at grain boundaries was low. It was beneficial to crack propagation. After the first phase change, the developed film-like ferrite along the austenite grain boundaries improved the nucleation conditions of new austenitic grains and removed the inhibition effect of the prior austenite grain boundaries on the austenite grain size.

Isothermal and non-isothermal conditions of isotope separation by chemical exchange method

International Nuclear Information System (INIS)

Khoroshilov, A.V.; Andreev, B.M.; Katalnikov, S.G.

1992-01-01

The published data about the effect of temperature on thermodynamic and mass transfer parameters of isotope separation by the chemical exchange method were used to examine the influence of iso- and non-isothermal conditions on the effectiveness of the separation process. It has been shown that simultaneous fulfillment of several optimization criteria is impossible in optimization of the isothermal process. If the limitation that temperature must be constant in the whole range of concentrational changes for an isolated isotope is removed, then it is possible to solve the problem of optimization with simultaneous fulfillment of several optimization criteria. When the separation process is carried out with non-isothermal conditions, that is, in temperature cascade, then the maximum concentration change takes place at every theoretical separation plate, and whole cascade is characterised by maximum throughput, minimum height and volume, and minimum cost for the stream reflux. From the results of our study, it was concluded that in the optimum temperature cascade, the cost of production of unity quantity of isotope can be decreased at least by a factor of two as compared with the optimal isothermal version of the separation process. (author)

Isothermal α″ formation in β metastable titanium alloys

International Nuclear Information System (INIS)

Aeby-Gautier, E.; Settefrati, A.; Bruneseaux, F.; Appolaire, B.; Denand, B.; Dehmas, M.; Geandier, G.; Boulet, P.

2013-01-01

Highlights: ► Isothermal kinetics of orthorhombic α″ formation is characterized by HEXRD. ► Cell parameters of parent and product phases are obtained. ► Partitioning of solutes during the transformation and the ageing is discussed. -- Abstract: Thanks to time resolved high energy X-ray diffraction, isothermal decomposition of β metastable phase was studied, directly after solution treatment in the β temperature range, for temperatures ranging from 300 to 450 °C for two beta metastable alloys (Ti 17 and Ti 5553). The formation of an orthorhombic α″ phase is clearly identified at the beginning of the transformation whatever the alloy studied. If transformation occurs at the higher temperature an evolution of α″ is observed toward the hexagonal α phase. The phase amounts and the mean cell parameters of each phase were quantified by the Rietveld refinement method. The obtained cell parameters evolutions and the orthorhombicity of α″ are discussed. Moreover, the orthorhombicity of α″ compared to that obtained for stress induced martensite may indicate a slight partitioning of solutes in isothermal α″

Isothermal α″ formation in β metastable titanium alloys

Energy Technology Data Exchange (ETDEWEB)

Aeby-Gautier, E., E-mail: Elisabeth.Gautier@mines.inpl-nancy.fr [Institut Jean Lamour, UMR CNRS Nancy Université, UPVM 7198, Nancy (France); Settefrati, A. [Institut Jean Lamour, UMR CNRS Nancy Université, UPVM 7198, Nancy (France); Airbus Operations, Materials and Processes, Toulouse (France); Bruneseaux, F. [Institut Jean Lamour, UMR CNRS Nancy Université, UPVM 7198, Nancy (France); Appolaire, B. [Laboratoire d’Etudes des Microstructures ONERA – CNRS Chatillon (France); Denand, B.; Dehmas, M.; Geandier, G.; Boulet, P. [Institut Jean Lamour, UMR CNRS Nancy Université, UPVM 7198, Nancy (France)

2013-11-15

Highlights: ► Isothermal kinetics of orthorhombic α″ formation is characterized by HEXRD. ► Cell parameters of parent and product phases are obtained. ► Partitioning of solutes during the transformation and the ageing is discussed. -- Abstract: Thanks to time resolved high energy X-ray diffraction, isothermal decomposition of β metastable phase was studied, directly after solution treatment in the β temperature range, for temperatures ranging from 300 to 450 °C for two beta metastable alloys (Ti 17 and Ti 5553). The formation of an orthorhombic α″ phase is clearly identified at the beginning of the transformation whatever the alloy studied. If transformation occurs at the higher temperature an evolution of α″ is observed toward the hexagonal α phase. The phase amounts and the mean cell parameters of each phase were quantified by the Rietveld refinement method. The obtained cell parameters evolutions and the orthorhombicity of α″ are discussed. Moreover, the orthorhombicity of α″ compared to that obtained for stress induced martensite may indicate a slight partitioning of solutes in isothermal α″.

Isothermal and non-isothermal cure of a tri-functional epoxy resin (TGAP): A stochastic TMDSC study

International Nuclear Information System (INIS)

Hutchinson, John M.; Shiravand, Fatemeh; Calventus, Yolanda; Fraga, Iria

2012-01-01

Highlights: ► First evaluation of T g of tri-functional epoxy resin TGAP by DSC. ► Clearly shows advantages of TOPEM for isothermal and non-isothermal cure analysis. ► Evidence of highly non-linear enthalpy relaxation in partially cured TGAP system. - Abstract: The isothermal cure of a highly reactive tri-functional epoxy resin, tri-glycidyl para-amino phenol (TGAP), with diamino diphenyl sulphone (DDS), at two different cure temperatures T c has been studied by both conventional differential scanning calorimetry (DSC) and by a stochastic temperature modulated DSC technique, TOPEM. From a series of isothermal cure experiments for increasing cure times, the glass transition temperature T g as a function of isothermal cure time is determined by conventional DSC from a second (non-isothermal) scan, and the vitrification time t v is obtained as the time at which T g = T c . In parallel, TOPEM experiments at the same T c lead directly to the determination of t v from the sigmoidal change in the quasi-static heat capacity. It is not possible to identify the glass transition temperature of the fully cured system, T g∞ , in a third scan by conventional DSC. In contrast, with TOPEM a second (non-isothermal) scan at 2 K/min after the isothermal cure gives rise to three separate transitions: devitrification of the partially cured and vitrified material; almost immediate vitrification as the T g of the system again rises; finally another devitrification, at a temperature approximating closely to T g∞ . Thus with TOPEM it is possible to obtain a calorimetric measure of the glass transition temperature of this fully cured system.

Elaboration of data and documents intended to complement and expand the German series of nuclear engineering codes. 3. Technical report. Non-destructive testing of austenitic welds and claddings

International Nuclear Information System (INIS)

Waidele, H.

1997-01-01

This 3. technical report presents a literature study on non-destructive testing of austenitic welds and claddings. NDT of claddings was the subject of a previous BMU project report SR 2024, so that this report contains only an update covering the latest developments in this subject area, and NDT of austenitic welds is the major subject of the report in hand. The literature study shows that improvements of ultrasonic test results for austenitic welds are expected to be achieved soon as a result of application of novel testing methods, advanced signal processing algorithms, and reduced anisotropy of austenitic welds due to specific welding techniques. Enhanced information is expected to be achieved from radiography tests through improvements available now, such as digitization of conventional radiographs combined with computer-assisted evaluation methods. As to the inspection of components with wall thickness up to 10 mm, low-frequency methods or eddy current methods will increasingly be applied in future as complementing methods supplying additional information. (orig./CB) [de

Retained austenite thermal stability in a nanostructured bainitic steel

International Nuclear Information System (INIS)

Avishan, Behzad; Garcia-Mateo, Carlos; Yazdani, Sasan; Caballero, Francisca G.

2013-01-01

The unique microstructure of nanostructured bainite consists of very slender bainitic ferrite plates and high carbon retained austenite films. As a consequence, the reported properties are opening a wide range of different commercial uses. However, bainitic transformation follows the T 0 criteria, i.e. the incomplete reaction phenomena, which means that the microstructure is not thermodynamically stable because the bainitic transformation stops well before austenite reaches an equilibrium carbon level. This article aims to study the different microstructural changes taking place when nanostructured bainite is destabilized by austempering for times well in excess of that strictly necessary to end the transformation. Results indicate that while bainitic ferrite seems unaware of the extended heat treatment, retained austenite exhibits a more receptive behavior to it. - Highlights: • Nanostructured bainitic steel is not thermodynamically stable. • Extensive austempering in these microstructures has not been reported before. • Precipitation of cementite particles is unavoidable at longer austempering times. • TEM, FEG-SEM and XRD analysis were used for microstructural characterization

Retained austenite thermal stability in a nanostructured bainitic steel

Energy Technology Data Exchange (ETDEWEB)

Avishan, Behzad, E-mail: b_avishan@sut.ac.ir [Faculty of Materials Engineering, Sahand University of Technology, Tabriz (Iran, Islamic Republic of); Garcia-Mateo, Carlos, E-mail: cgm@cenim.csic.es [Department of Physical Metallurgy, National Centre for Metallurgical Research (CENIM-CSIC), MATERALIA Research Group, Avda. Gregorio del Amo, 8, 28040, Madrid (Spain); Yazdani, Sasan, E-mail: yazdani@sut.ac.ir [Faculty of Materials Engineering, Sahand University of Technology, Tabriz (Iran, Islamic Republic of); Caballero, Francisca G., E-mail: fgc@cenim.csic.es [Department of Physical Metallurgy, National Centre for Metallurgical Research (CENIM-CSIC), MATERALIA Research Group, Avda. Gregorio del Amo, 8, 28040, Madrid (Spain)

2013-07-15

The unique microstructure of nanostructured bainite consists of very slender bainitic ferrite plates and high carbon retained austenite films. As a consequence, the reported properties are opening a wide range of different commercial uses. However, bainitic transformation follows the T{sub 0} criteria, i.e. the incomplete reaction phenomena, which means that the microstructure is not thermodynamically stable because the bainitic transformation stops well before austenite reaches an equilibrium carbon level. This article aims to study the different microstructural changes taking place when nanostructured bainite is destabilized by austempering for times well in excess of that strictly necessary to end the transformation. Results indicate that while bainitic ferrite seems unaware of the extended heat treatment, retained austenite exhibits a more receptive behavior to it. - Highlights: • Nanostructured bainitic steel is not thermodynamically stable. • Extensive austempering in these microstructures has not been reported before. • Precipitation of cementite particles is unavoidable at longer austempering times. • TEM, FEG-SEM and XRD analysis were used for microstructural characterization.

Phase composition and saturated liquid properties in binary and ternary systems containing carbon dioxide, n-decane, and n-tetradecane

International Nuclear Information System (INIS)

Kariznovi, Mohammad; Nourozieh, Hossein; Abedi, Jalal

2013-01-01

Highlights: ► Binary and ternary systems of (carbon dioxide + n-decane + n-tetradecane) at 323.2 K. ► Isothermal phase properties measurements over wide range of pressure (1 to 6) MPa. ► Experimental measurements, density, viscosity, and composition, using a designed PVT apparatus. ► The experimental data were correlated using two equations of state. ► The interaction parameters and the volume shift values from the experimental data on the binary pairs. - Abstract: Experimental phase equilibrium data have been measured for the binary and ternary systems containing (carbon dioxide, n-decane, and n-tetradecane) at 323.2 K over the pressure range (1 to 6) MPa using a designed PVT apparatus. The measurements presented in this paper were undertaken to determine liquid phase composition and liquid saturated properties (density and viscosity) when a liquid hydrocarbon (n-decane, n-tetradecane, and their mixtures) was saturated with carbon dioxide. The generated data for compositions and densities were correlated with the Soave–Redlich–Kwong (SRK) and Peng–Robinson (PR) equations of state (EOS). The adjustment of binary interaction parameters and volume translation technique has been employed to correlate the experimental compositions and densities. The adjusted binary parameters from the data of binary pairs (carbon dioxide + n-decane) and (carbon dioxide + n-tetradecane) were used to correlate the generated ternary data. The calculated ternary compositions were found to be in good agreement with the experimental data using the binary parameters from the data of binary pairs for both EOSs. The results for the density of saturated liquid phase indicated that the volume translation should be applied to all components in the binary and ternary systems to describe accurately the saturated liquid densities for mixtures.

Effect of Heat Treatment on the Microstructure and Hardness of 17Cr-0.17N-0.43C-1.7 Mo Martensitic Stainless Steel

Science.gov (United States)

Krishna, S. Chenna; Gangwar, Narendra Kumar; Jha, Abhay K.; Pant, Bhanu; George, Koshy M.

2015-04-01

The microstructure and hardness of a nitrogen-containing martensitic stainless steel were investigated as a function of heat treatment using optical microscopy, electron microscopy, amount of retained austenite, and hardness measurement. The steel was subjected to three heat treatments: hardening, cryo treatment, and tempering. The hardness of the steel in different heat-treated conditions ranged within 446-620 HV. The constituents of microstructure in hardened condition were lath martensite, retained austenite, M23C6, M7C3, MC carbides, and M(C,N) carbonitrides. Upon tempering at 500 °C, two new phases have precipitated: fine spherical Mo2C carbides and needle-shaped Cr2N particles.

Wearing Quality of Austenitic, Duplex Cast Steel, Gray and Spheroidal Graphite Iron

Directory of Open Access Journals (Sweden)

S. Pietrowski

2012-04-01

Full Text Available The current work presents the research results of abrasion wear and adhesive wear at rubbing and liquid friction of new austenitic, austenitic-ferritic (“duplex” cast steel and gray cast iron EN-GJL-250, spheroidal graphite iron EN-GJS-600-3, pearlitic with ledeburitic carbides and spheroidal graphite iron with ledeburitic carbides with a microstructure of the metal matrix: pearlitic, upper bainite, mixture of upper and lower bainite, martensitic with austenite, pearlitic-martensitic-bainitic-ausferritic obtained in the raw state. The wearing quality test was carried out on a specially designed and made bench. Resistance to abrasion wear was tested using sand paper P40. Resistance to adhesive wear was tested in interaction with steel C55 normalized, hardened and sulfonitrided. The liquid friction was obtained using CASTROL oil. It was stated that austenitic cast steel and “duplex” are characterized by a similar value of abrasion wear and adhesive wear at rubbing friction. The smallest decrease in mass was shown by the cast steel in interaction with the sulfonitrided steel C55. Austenitic cast steel and “duplex��� in different combinations of friction pairs have a higher wear quality than gray cast iron EN-GJL- 250 and spheroidal graphite iron EN-GJS-600-3. Austenitic cast steel and “duplex” are characterized by a lower wearing quality than the spheroidal graphite iron with bainitic-martensitic microstructure. In the adhesive wear test using CASTROL oil the tested cast steels and cast irons showed a small mass decrease within the range of 1÷2 mg.

The effect of aging on the critical current density in superconducting Nb-Ti-Zr alloys

International Nuclear Information System (INIS)

Ishida, Fumihiko; Doi, Toshio

1979-01-01

The effect of aging temperature, cold-reduction prior to aging, O 2 content and composition on the variation in the critical current density, J sub(c), by isothermal aging was investigated in heavily cold-worked Nb-Ti-Zr alloys on the Nb-Ti side. The results are summarized as follows: (1) When these alloys are aged isothermally at temperatures from 350 to 500 0 C, J sub(c) increases initially, reaches a maximum value and then decreases. Increase in J sub(c) of three orders of magnitude is possible as a result of aging. (2) The maximum value of J sub(c) on the isothermal aging curve becomes higher at a lower aging temperature, at a less cold-reduction prior to aging or with a higher O 2 content. (3) The J sub(c) of aged alloy becomes a maximum in composition containing 35 at%Nb, 60 to 65 at%Ti and less than 5 at%Zr. (4) The maximum value of J sub(c) was obtained for Nb-60.0 at%Ti-5.0 at%Zr alloy containing 1200 wt ppm O 2 , aged at 350 0 C for 330 h after 98.44% cold-reduction. The values of J sub(c) at 4.2 K were 2.4 x 10 9 A/m 2 at 5.0 T, 1.1 x 10 9 A/m 2 at 7.0 T and 3.0 x 10 8 A/m 2 at 9.0 T, respectively. The upper critical field of this specimen was 11.3 T at 4.2 K and its critical temperature was 8.6 K. (author)

Fatigue Properties of Aged Mod. 9Cr-1Mo

International Nuclear Information System (INIS)

Kim, Dae Whan; Kim, Sung Ho; Lee, Chan Bock

2007-01-01

Ferritic/Martensitic steel has a good mechanical properties and a lower thermal expansion coefficient than austenitic stainless steel. Mechanical property of Mod. 9Cr-1Mo steel is less than austenitic stainless steel at high temperature. High temperature mechanical properties are affected by precipitation for Mod. 9Cr-1Mo. FMS steel is used for long time at high temperature and the effect of aging on mechanical properties is very important. In this study, low cycle fatigue properties with aging were investigated

Weld repair issues in thick section austenitic pipework

International Nuclear Information System (INIS)

Goodwin, S.J.; Price, A.T.

1989-03-01

Thick section austenitic Type 316 Stainless steel, in the solution treated condition, has been used in Central Electricity Generating Board plant in the United Kingdom for some three decades and has given good service. Repair and replacement of this material after long term service is becoming a requirement and is complicated by the precipitation hardening and sensitisation of the materials. This paper summarises the compositional, microstructural and ageing characteristics of the wrought material and weld metals and the consequences for materials properties. Post weld heat treatment options are outlined and sensitisation to stress corrosion cracking is discussed. Finally, some examples of cracking that has occurred in plant after long term operation are given and weld repair research requirements are noted. (author)

Corrosion of austenitic stainless steel

Energy Technology Data Exchange (ETDEWEB)

Silva, M C.M. [Instituto Nacional de Tecnologia, Rio de Janeiro (Brazil)

1977-01-01

Types of corrosion observed in a heat exchanger pipe and on a support of still of molasses fermented wort, both in austenitic stainless steel, are focused. Not only are the causes which might have had any kind of influence on them examined, but also the measures adopted in order to avoid and lessen its occurence.

Isochronal and isothermal crystallization kinetics of amorphous Fe-based alloys

International Nuclear Information System (INIS)

Zhang, J.T.; Wang, W.M.; Ma, H.J.; Li, G.H.; Li, R.; Zhang, Z.H.

2010-01-01

Using the differential scanning calorimetry (DSC), the isochronal and isothermal crystallization kinetics of amorphous Fe 61 Co 9-x Zr 8 Mo 5 W x B 17 (x = 0 and 2) ribbons was investigated by the Kissinger equation and by the Kolmogorov-Johnson-Mehl-Avrami and Ranganathan-Heimendahl equations, respectively. The results show that tungsten can improve the activation energy E 1 K for the first crystallization in the isochronal annealing process and activation energy E n for the nucleation in the isothermal annealing process, which can be ascribed to the dissolution of tungsten in the amorphous phase. Meanwhile, tungsten can decrease the activation energy E 2 K for the second crystallization in the isochronal annealing process and growth activation energy E g in the isothermal annealing process, which is possibly associated with the formation of W-rich compound after the early nucleation process.

A systematic study of the isothermal crystallization of the mono-alcohol n-butanol monitored by dielectric spectroscopy

DEFF Research Database (Denmark)

Jensen, Mikkel Hartmann; Hecksher, Tina; Niss, Kristine

2015-01-01

Isothermal crystallization of the mono-hydroxyl alcohol n-butanol was studied with dielectric spectroscopy in real time. The crystallization was carried out using two different sample cells at 15 temperatures between 120 K and 134 K. Crystallization is characterized by a decrease of the dielectric...... intensity. In addition, a shift in relaxation times to shorter times was observed during the crystallization process for all studied temperatures. The two different sample environments induced quite different crystallization behaviors, consistent and reproducible over all studied temperatures...... that a microscopic interpretation of crystallization measurements requires multiple probes, sample cells, and protocols....

Rapid nickel diffusion in cold-worked type 316 austenitic steel at 360-500 C

Energy Technology Data Exchange (ETDEWEB)

Arioka, Koji [Institute of Nuclear Safety Systems, Inc., Mihama (Japan); Iijima, Yoshiaki [Tohoku Univ., Sendai (Japan). Dept. of Materials Science; Miyamoto, Tomoki [Kobe Material Testing Laboratory Co. Ltd., Harima (Japan)

2017-10-15

The diffusion coefficient of nickel in cold-worked Type 316 austenitic steel was determined by the diffusion couple method in the temperature range between 360 and 500 C. A diffusion couple was prepared by electroless nickel plating on the surface of a 20 % cold-worked Type 316 austenitic steel specimen. The growth in width of the interdiffusion zone was proportional to the square root of diffusion time until 14 055 h. The diffusion coefficient of nickel (D{sub Ni}) in cold-worked Type 316 austenitic steel was determined by extrapolating the concentration-dependent interdiffusion coefficient to 11 at.% of nickel. The value of D{sub Ni} at 360 C was about 5 000 times higher than the lattice diffusion coefficient of nickel in Type 316 austenitic steel. The determined activation energy 117 kJ mol{sup -1} was 46.6 % of the activation energy 251 kJ mol{sup -1} for the lattice diffusion of nickel in Type 316 austenitic steel.

Isothermal transitions of a thermosetting system

Science.gov (United States)

Gillham, J. K.; Benci, J. A.; Noshay, A.

1974-01-01

A study of the curing reactions of a cycloaliphatic epoxy resin/anhydride system by torsional braid analysis showed the existence of two critical isothermal temperatures - namely, the maximum glass transition temperature of the thermoset system and the glass transition temperature of the material at its gel point. Two rheologically active kinetic transitions occur during isothermal cure which correspond to gelation and vitrification. Three types of isothermal behavior occur. Methods for determining the time to gel and the time to vitrify, and also the two above-mentioned critical isothermal temperatures, have been developed. The time to gel obeyed the Arrhenius relationship, whereas the time to vitrify passed through a minimum. Application of these results to thermosetting systems in general is discussed in terms of the influence of molecular structure on the values of the critical isothermal temperatures.

Phase Transformation of Metastable Austenite in Steel during Nano indentation

International Nuclear Information System (INIS)

Ahn, Taehong; Lee, Sung Bo; Han, Heung Nam; Park, Kyungtae

2013-01-01

These can produce geometrical softening accompanied by a sudden displacement excursion during load-controlled nanoindentation, which referred to in the literature as a pop-in. In this study, phase transformation of metastable austenite to stress-induced ε martensite which causes pop-ins during nanoindentation of steel will be reported and discussed. This study investigated the relationship between pop-in behavior of austenite in the early stage of nanoindentation and formation of ε martensite based on microstructural analyses. The load-displacement curve obtained from nanoindentation revealed stepwise pop-ins in the early stage of plastic deformation. From analyses of high resolution TEM images, a cluster of banded structure under the indent turned out a juxtaposition of (111) planes of γ austenite and (0001) planes of ε martensite. The calculation of displacement along indentation axis for (111) slip system by formation of ε martensite showed that geometrical softening can also occur by ε martensite formation when considering that the stress-induced ε martensite transformation is the predominant deformation mode in the early stage of plastic deformation and its monopartial nature as well. These microstructural investigations strongly suggest that the pop-in behavior in the early stage of plastic deformation of austenite is closely related to the formation of ε martensite

Phase Transformation of Metastable Austenite in Steel during Nano indentation

Energy Technology Data Exchange (ETDEWEB)

Ahn, Taehong [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of); Lee, Sung Bo; Han, Heung Nam [Seoul National Univ., Seoul (Korea, Republic of); Park, Kyungtae [Hanbat National Univ., Daejeon (Korea, Republic of)

2013-05-15

These can produce geometrical softening accompanied by a sudden displacement excursion during load-controlled nanoindentation, which referred to in the literature as a pop-in. In this study, phase transformation of metastable austenite to stress-induced ε martensite which causes pop-ins during nanoindentation of steel will be reported and discussed. This study investigated the relationship between pop-in behavior of austenite in the early stage of nanoindentation and formation of ε martensite based on microstructural analyses. The load-displacement curve obtained from nanoindentation revealed stepwise pop-ins in the early stage of plastic deformation. From analyses of high resolution TEM images, a cluster of banded structure under the indent turned out a juxtaposition of (111) planes of γ austenite and (0001) planes of ε martensite. The calculation of displacement along indentation axis for (111) slip system by formation of ε martensite showed that geometrical softening can also occur by ε martensite formation when considering that the stress-induced ε martensite transformation is the predominant deformation mode in the early stage of plastic deformation and its monopartial nature as well. These microstructural investigations strongly suggest that the pop-in behavior in the early stage of plastic deformation of austenite is closely related to the formation of ε martensite.

Modification of the Strength Anisotropy in an Austenitic ODS Steel

International Nuclear Information System (INIS)

Kim, T. K.; Jang, J.; Kim, S. H.; Lee, C. B.; Bae, C. S.; Kim, D. H.

2007-01-01

Among many candidate alloys for Gen IV reactors, the oxide dispersion strengthened (ODS) alloy is widely considered as a good candidate material for the in-reactor component, like cladding tube. The ODS alloy is well known due to its good high temperature strength, and excellent irradiation resistance. For the previous two decades in the nuclear community, the ODS alloy developments have been mostly focused on the ferritic martensitic (F-M) steel-based ones. On the other hand, the austenitic stainless steels (e.g. 316L or 316LN) have been used as a structural material due to its good high temperature strength and a good compatibility with a media. However, the austenitic stainless steel showed unfavorable characteristics in the dimensional stability under neutron irradiation and cracking behavior with the media. It is thus expected that the austenitic ODS steels restrain the dimension stability under neutron irradiation. However, the ODS alloys usually reveal the anisotropic characteristic in mechanical strength in the hoop and longitudinal directions, which is attributed to the grain morphology strongly developed parallel to the rolling direction with a high aspect ratio. This study focuses on a modification of the strength anisotropy of an austenitic ODS alloy by a recrystallization heat treatment

Room temperature isotherms for Mo and Ni

International Nuclear Information System (INIS)

Masse, J.L.

1986-11-01

Isotherms at room temperature for Mo and Ni are proposed. They are of three types: BIRCH, KEANE and BORN-MIE. The adjustable constants appearing in these isotherms have been determined from experimental quantities at zero pressure. An evaluation of the limit of (δB T /δP) T as P #-> # ∞, where B T is the isothermal bulk modulus, has been also used. These three isotherms obtained for Mo and Ni are compared with isotherms derived from shock-wave data according to the PRIETO's model. There is a good agreement between these and these derived from shock-wave data. The three isotherms proposed for Mo and Ni can be considered as valid until pressures of several B To , where B To is the bulk modulus B T at P = o [fr

Isothermal microcalorimetry for antifungal susceptibility testing of Mucorales, Fusarium spp., and Scedosporium spp.

NARCIS (Netherlands)

Furustrand Tafin, U.; Meis, J.F.G.M.; Trampuz, A.

2012-01-01

We evaluated isothermal microcalorimetry for real-time susceptibility testing of non-Aspergillus molds. MIC and minimal effective concentration (MEC) values of Mucorales (n = 4), Fusarium spp. (n = 4), and Scedosporium spp. (n = 4) were determined by microbroth dilution according to the Clinical

Application of Moessbauer effect in the study of austenite retained in low carbon steel

International Nuclear Information System (INIS)

Azevedo, A.L.T. de; Silva, E.G. da

1979-01-01

Moessbauer effect measurements of two samples of low carbon alloy having micro-structure of granular bainite type and martensite type have been done. The concentration of the retained austenite in both samples was determined by Moessbauer effect and x-rays there, being agreement for the higher austenite content sample. Concentration of carbon in the MA (Martensite - Austenite) constituents of bainite is also ditermined, the results being in agreement with metallographic considerations. Carbon enrichments are shown as responsible by the stabilization of the austenite in the granular bainite. Spectra of both samples present three magnetic configurations for α-iron with medium magnetic fields iqual to 335, 307 and 280 KOe. (A.R.H.) [pt

Austenitic stainless steels with cryogenic resistance

International Nuclear Information System (INIS)

Tarata, Daniela Florentina

1999-01-01

The most used austenitic stainless steels are alloyed with chromium and nickel and have a reduced carbon content, usually lower than 0.1 % what ensures corresponding properties for processing by plastic deformation at welding, corrosion resistance in aggressive environment and toughness at low temperatures. Steels of this kind alloyed with manganese are also used to reduce the nickel content. By alloying with manganese which is a gammageneous element one ensures the stability of austenites. Being cheaper these steels may be used extensively for components and equipment used in cryogenics field. The best results were obtained with steels of second group, AMnNi, in which the designed chemical composition was achieved, i.e. the partial replacement of nickel by manganese ensured the toughness at cryogenic temperatures. If these steels are supplementary alloyed, their strength properties may increase to the detriment of plasticity and toughness, although the cryogenic character is preserved

Synergistic Computational and Microstructural Design of Next- Generation High-Temperature Austenitic Stainless Steels

Energy Technology Data Exchange (ETDEWEB)

Karaman, Ibrahim [Texas A& M Engineering Experiment Station, College Station, TX (United States); Arroyave, Raymundo [Texas A& M Engineering Experiment Station, College Station, TX (United States)

2015-07-31

The purpose of this project was to: 1) study deformation twinning, its evolution, thermal stability, and the contribution on mechanical response of the new advanced stainless steels, especially at elevated temperatures; 2) study alumina-scale formation on the surface, as an alternative for conventional chromium oxide, that shows better oxidation resistance, through alloy design; and 3) design new generation of high temperature stainless steels that form alumina scale and have thermally stable nano-twins. The work involved few baseline alloys for investigating the twin formation under tensile loading, thermal stability of these twins, and the role of deformation twins on the mechanical response of the alloys. These baseline alloys included Hadfield Steel (Fe-13Mn-1C), 316, 316L and 316N stainless steels. Another baseline alloy was studied for alumina-scale formation investigations. Hadfield steel showed twinning but undesired second phases formed at higher temperatures. 316N stainless steel did not show signs of deformation twinning. Conventional 316 stainless steel demonstrated extensive deformation twinning at room temperature. Investigations on this alloy, both in single crystalline and polycrystalline forms, showed that deformation twins evolve in a hierarchical manner, consisting of micron–sized bundles of nano-twins. The width of nano-twins stays almost constant as the extent of strain increases, but the width and number of the bundles increase with increasing strain. A systematic thermomechanical cycling study showed that the twins were stable at temperatures as high as 900°C, after the dislocations are annealed out. Using such cycles, volume fraction of the thermally stable deformation twins were increased up to 40% in 316 stainless steel. Using computational thermodynamics and kinetics calculations, we designed two generations of advanced austenitic stainless steels. In the first generation, Alloy 1, which had been proposed as an alumina

Tuberculosis Biomarker Extraction and Isothermal Amplification in an Integrated Diagnostic Device.

Directory of Open Access Journals (Sweden)

Amy Creecy

Full Text Available In this study, we integrated magnetic bead-based sample preparation and isothermal loop mediated amplification (LAMP of TB in a single tube. Surrogate sputum samples produced by the Program for Appropriate Technology in Health containing inactivated TB bacteria were used to test the diagnostic. In order to test the sample preparation method, samples were lysed, and DNA was manually extracted and eluted into water in the tube. In a thermal cycler, LAMP amplified TB DNA from 103 TB cells/mL of sputum at 53.5 ± 3.3 minutes, 104 cells/mL at 46.3 ± 2.2 minutes, and 105 cells/mL at 41.6 ± 1.9 minutes. Negative control samples did not amplify. Next, sample preparation was combined with in-tubing isothermal LAMP amplification by replacing the water elution chamber with a LAMP reaction chamber. In this intermediate configuration, LAMP amplified 103 cells/mL at 74 ± 10 minutes, 104 cells/mL at 60 ± 9 minutes, and 105 TB cells/mL of sputum at 54 ± 9 minutes. Two of three negative controls did not amplify; one amplified at 100 minutes. In the semi-automated system, DNA was eluted directly into an isothermal reaction solution containing the faster OptiGene DNA polymerase. The low surrogate sputum concentration, 103 TB cells/mL, amplified at 52.8 ± 3.3 minutes, 104 cells/mL at 45.4 ± 11.3 minutes, and 105 cells/mL at 31.8 ± 2.9 minutes. TB negative samples amplified at 66.4 ± 7.4 minutes. This study demonstrated the feasibility of a single tube design for integrating sample preparation and isothermal amplification, which with further development could be useful for point-of-care applications, particularly in a low-resource setting.

Effect of partial oxygen pressure on physicochemical properties of Kh18N10T steel at isothermal oxidation

International Nuclear Information System (INIS)

Alekseev, V.N.; Oshe, E.K.; Fokin, M.N.; Bogdanova, S.V.; Loskutov, A.I.

1990-01-01

Auger-electron spectroscopy, photoelectric polarization, conductometry methods have been used to analyze chemical and defect composition of surface oxide layers, formed on stainless steel Kh18N10T in vacuum (10 -9 - 10 -2 torr) and at temperatures 593-673 K. The boundary conditions of manifestation of extermal behaviour of the dependence of the surface oxide growth rate at isothermal oxidation of this steel are determined. The relation between passivation properties of the surface oxide and the magnitude of the edge angle of the surface wetting with molten tin is revealed

Aging of steel containments and liners in nuclear power plants

International Nuclear Information System (INIS)

Naus, D.J.; Oland, C.B.; Ellingwood, B.; Norris, W.E.

1998-02-01

Aging of the containment pressure boundary in light water reactor plants is being addressed to understand the significant factors relating occurrence of corrosion efficacy of inspection and structural capacity reduction of steel containments and liners of concrete containments. and to make recommendations on use of risk models in regulatory decisions. Current regulatory in-service inspection requirements are reviewed and a summary of containment related degradation experience is presented. Current and emerging nondestructive examination techniques and a degradation assessment methodology for characterizing and quantifying the amount of damage present are described. Quantitative tools for condition assessment of aging structures using time dependent structural reliability analysis methods are summarized. Such methods provide a framework for addressing the uncertainties attendant to aging in the decision process. Results of this research provide a means for establishing current and estimating future structural capacity margins of containments, and to address the significance of incidences of reported containment degradation

Corrosion behaviour of austenitic stainless steel, nickel-base alloy and its weldments in aqueous LiBr solutions

Energy Technology Data Exchange (ETDEWEB)

Blasco-Tamarit, E.; Igual-Munoz, A.; Garcia Anton, J.; Garcia-Garcia, D. [Departamento de Ingenieria Quimica y Nuclear. E.T.S.I.Industriales, Universidad Politecnica de Valencia, P.O. Box 22012 E-46071 Valencia (Spain)

2004-07-01

With the advances in materials production new alloys have been developed, such as High- Alloy Austenitic Stainless Steels and Nickel-base alloys, with high corrosion resistance. These new alloys are finding applications in Lithium Bromide absorption refrigeration systems, because LiBr is a corrosive medium which can cause serious corrosion problems, in spite of its favourable properties as absorbent. The objective of the present work was to study the corrosion resistance of a highly alloyed austenitic stainless steel (UNS N08031) used as base metal, a Nickel-base alloy (UNS N06059) used as its corresponding filler metal, and the weld metal obtained by the Gas Tungsten Arc Welding (GTAW) procedure. The materials have been tested in different LiBr solutions (400 g/l, 700 g/l, 850 g/l and a commercial 850 g/l LiBr heavy brine containing Lithium Chromate as corrosion inhibitor), at 25 deg. C. Open Circuit Potential tests and potentiodynamic anodic polarization curves have been carried out to obtain information about the general electrochemical behaviour of the materials. The polarization curves of all the alloys tested were typical of passivable materials. Pitting corrosion susceptibility has been evaluated by means of cyclic potentiodynamic curves, which provide parameters to analyse re-passivation properties. The galvanic corrosion generated by the electrical contact between the welded and the base material has been estimated from the polarization diagrams according to the Mixed Potential Method. Samples have been etched to study the microstructure by Scanning Electron Microscopy (SEM). The results demonstrate that the pitting resistance of all these materials increases as the LiBr concentration decreases. In general, the presence of chromate tended to shift the pitting potential to more positive values than those obtained in the 850 g/l LiBr solution. (authors)

Isothermal and non-isothermal cure of a tri-functional epoxy resin (TGAP): a stochastic TMDSC study

OpenAIRE

Hutchinson, John M.; Shiravand, Fatemeh; Calventus Solé, Yolanda; Fraga Rivas, Iria

2012-01-01

The isothermal cure of a highly reactive tri-functional epoxy resin, tri-glycidyl para-amino phenol (TGAP), with diamino diphenyl sulphone (DDS), at two different cure temperatures Tc has been studied by both conventional differential scanning calorimetry (DSC) and by a stochastic temperature modulated DSC technique, TOPEM. From a series of isothermal cure experiments for increasing cure times, the glass transition temperature Tg as a function of isothermal cure time is determined by co...

Survey of degradation modes of candidate materials for high-level radioactive-waste disposal containers

International Nuclear Information System (INIS)

Bullen, D.B.; Gdowski, G.E.

1988-08-01

Three copper-based alloys and three iron- to nickel-based austenitic alloys are being considered as possible materials for fabrication of high-level radioactive-waste disposal containers. The waste will include spent fuel assemblies from reactors as well as high-level waste in borosilicate glass and will be sent to the prospective site at Yucca Mountain, Nevada, for disposal. The copper-based alloy materials are CDA 102 (oxygen-free copper), CDA 613 (Cu-7Al), and CDA 715 (Cu-30Ni). The austenitic materials are Types 304L and 316L stainless steels and Alloy 825. The waste-package containers must maintain substantially complete containment for at least 300 yr and perhaps as long as 1000 yr, and they must be retrievable from the disposal site during the first 50 yr after emplacement. The containers will be exposed to high temperatures and high gamma radiation fields from the decay of high-level waste. This volume surveys the available data on the phase stability of both groups of candidate alloys. The austenitic alloys are reviewed in terms of the physical metallurgy of the iron-chromium-nickel system, martensite transformations, carbide formation, and intermetallic-phase precipitation. The copper-based alloys are reviewed in terms of their phase equilibria and the possibility of precipitation of the minor alloying constituents. For the austenitic materials, the ranking based on phase stability is: Alloy 825 (best), Type 316L stainless steel, and then Type 304L stainless steel (worst). For the copper-based materials, the ranking is: CDA 102 (oxygen-free copper) (best), and then both CDA 715 and CDA 613. 75 refs., 24 figs., 6 tabs

Tailoring plasticity of austenitic stainless steels for nuclear applications: Review of mechanisms controlling plasticity of austenitic steels below 400 °C

Science.gov (United States)

Meric de Bellefon, G.; van Duysen, J. C.

2016-07-01

AISI 304 and 316 austenitic stainless steels were invented in the early 1900s and are still trusted by materials and mechanical engineers in numerous sectors because of their good combination of strength, ductility, and corrosion resistance, and thanks to decades of experience and data. This article is part of an effort focusing on tailoring the plasticity of both types of steels to nuclear applications. It provides a synthetic and comprehensive review of the plasticity mechanisms in austenitic steels during tensile tests below 400 °C. In particular, formation of twins, extended stacking faults, and martensite, as well as irradiation effects and grain rotation are discussed in details.

Influence of pre-treatments on the desorption isotherm ...

African Journals Online (AJOL)

Influence of pre-treatments on the desorption isotherm characteristics of plaintain. P-N T Johnson. Full Text: EMAIL FULL TEXT EMAIL FULL TEXT · DOWNLOAD FULL TEXT DOWNLOAD FULL TEXT · http://dx.doi.org/10.4314/gjs.v39i1.15851 · AJOL African Journals Online. HOW TO USE AJOL... for Researchers · for ...

Precipitation model in microalloyed steels both isothermal and continuous cooling conditions

International Nuclear Information System (INIS)

Medina, S. F.; Quispe, A.; Gomez, M.

2015-01-01

Niobium and vanadium precipitates (nitrides and carbides) can inhibit the static recrystallization of austenite but this does not happen for Ti, which form nitrides at high temperatures. RPTT diagrams show the interaction between recrystallization and precipitation allowing study the strain induced precipitation kinetics and precipitate coarsening. Based on Dutta and Sellars expression for the start of strain-induced precipitation in microalloyed steels, a new model has been constructed which takes into account the influence of variables such as microalloying element percentages, strain, temperature, strain rate and grain size. Recrystallization- Precipitation-Time-Temperature (RPTT) diagrams have been plotted thanks to a new experimental study carried out by means of hot torsion tests on approximately twenty microalloyed steels with different Nb, V and Ti contents. Mathematical analysis of the results recommends the modification of some parameters such as the supersaturation ratio (ks) and constant B, which is no longer a constant but a function of ks. The expressions are now more consistent and predict the Precipitation-Time-Temperature (PTT) curves with remarkable accuracy. The model for strain-induced precipitation kinetics is completed by means of Avramis equation. Finally, the model constructed in isothermal testing conditions, it has been converted to continuous cooling conditions in order to apply it in hot rolling. (Author)

Influence of low-temperature nitriding on the strain-induced martensite and laser-quenched austenite in a magnetic encoder made from 304L stainless steel

Science.gov (United States)

Leskovšek, Vojteh; Godec, Matjaž; Kogej, Peter

2016-01-01

We have investigated the possibility of producing a magnetic encoder by an innovative process. Instead of turning grooves in the encoder bar for precise positioning, we incorporated the information in 304L stainless steel by transforming the austenite to martensite after bar extrusion in liquid nitrogen and marking it with a laser, which caused a local transformation of martensite back into austenite. 304L has an excellent corrosion resistance, but a low hardness and poor wear resistance, which limits its range of applications. However, nitriding is a very promising way to enhance the mechanical and magnetic properties. After low-temperature nitriding at 400 °C it is clear that both ε- and α′-martensite are present in the deformed microstructure, indicating the simultaneous stress-induced and strain-induced transformations of the austenite. The effects of a laser surface treatment and the consequent appearance of a non-magnetic phase due to the α′ → γ transformation were investigated. The EDS maps show a high concentration of nitrogen in the alternating hard surface layers of γN and α′N (expanded austenite and martensite), but no significantly higher concentration of chromium or iron was detected. The high surface hardness of this nitride layer will lead to steels and encoders with better wear and corrosion resistance. PMID:27492862

Assessment of Retained Austenite in AISI D2 Tool Steel Using Magnetic Hysteresis and Barkhausen Noise Parameters

Science.gov (United States)

Kahrobaee, Saeed; Kashefi, Mehrdad

2015-03-01

Inaccurate heat treatment process could result in excessive amount of retained austenite, which degrades the mechanical properties, like strength, wear resistance, and hardness of cold work tool steel parts. Thus, to control the mechanical properties, quantitative measurement of the retained austenite is a critical step in optimizing the heat-treating parameters. X-ray diffraction method is the most frequently used technique for this purpose. This technique is, however, destructive and time consuming. Furthermore, it is not applicable to 100% quality inspection of industrial parts. In the present paper, the influence of austenitizing temperature on the retained austenite content and hardness of AISI D2 tool steel has been studied. Additionally, nondestructive magnetic hysteresis parameters of the samples including coercivity, magnetic saturation, and maximum differential permeability as well as their magnetic Barkhausen noise features (RMS peak voltage and peak position) have been investigated. The results revealed direct relations between magnetic saturation, differential permeability, and MBN peak amplitude with increasing austenitizing temperature due to the retained austenite formation. Besides, both parameters of coercivity and peak position had an inverse correlation with the retained austenite fraction.

Reduced-activation austenitic stainless steels: The Fe--Mn--Cr--C system

International Nuclear Information System (INIS)

Klueh, R.L.; Maziasz, P.J.

1988-01-01

Nickel-free manganese-stabilized steels are being developed for fusion-reactor applications. As the first part of this effort, the austenite-stable region in the Fe--Mn--Cr--C system was determined. Results indicated that the Schaeffler diagram developed for Fe--Ni--Cr--C alloys cannot be used to predict the constituents expected for high-manganese steels. This is true because manganese is not as strong an austenite stabilizer relative to δ-ferrite formation as predicted by the diagram, but it is a stronger austenite stabilizer relative to martensite than predicted. Therefore, the austenite-stable region for Ne--Mn--Cr--C alloys occurs at lower chromium and hugher combinations of manganese and carbon than predicted by the Schaeffler diagram. Development of a manganese-stabilized stainless steel should be possible in the composition range of 20 to 25% Mn, 10 to 15% Cr, and 0.01 to 0.25%C. Tensile behavior of an Fe--20%Mn--12%Cr--0.25%C alloy was determined. The strength and ductility of this possible base composition was comparable to type 316 stainless steel in both the solution-annealed and cold-worked condition

Anelastic mechanical loss spectrometry of hydrogen in austenitic stainless steels

International Nuclear Information System (INIS)

Yagodzinskyy, Y.; Andronova, E.; Ivanchenko, M.; Haenninen, H.

2009-01-01

Atomic distribution of hydrogen, its elemental diffusion jumps and its interaction with dislocations in a number of austenitic stainless steels are studied with anelastic mechanical loss (AML) spectrometry in combination with the hydrogen thermal desorption method. Austenitic stainless steels of different chemical composition, namely, AISI 310, AISI 201, and AISI 301LN, as well as LDX 2101 duplex stainless steel are studied to clarify the role of different alloying elements on the hydrogen behavior. Activation analyses of the hydrogen Snoek-like peaks are performed with their decomposition to sets of Gaussian components. Fine structure of the composite hydrogen peaks is analyzed under the assumption that each component corresponds to diffusion transfer of hydrogen between octahedral positions with certain atomic compositions of the nearest neighbouring lattice sites. An additional component originating from hydrogen-dislocation interaction is considered. Binding energies for hydrogen-dislocation interaction are also estimated for the studied austenitic stainless steels.

Isochronal and isothermal crystallization kinetics of amorphous Fe-based alloys

Energy Technology Data Exchange (ETDEWEB)

Zhang, J.T. [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan 250061 (China); Wang, W.M., E-mail: weiminw@sdu.edu.cn [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan 250061 (China); Key Lab of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); Ma, H.J.; Li, G.H.; Li, R.; Zhang, Z.H. [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan 250061 (China)

2010-06-10

Using the differential scanning calorimetry (DSC), the isochronal and isothermal crystallization kinetics of amorphous Fe{sub 61}Co{sub 9-x}Zr{sub 8}Mo{sub 5}W{sub x}B{sub 17} (x = 0 and 2) ribbons was investigated by the Kissinger equation and by the Kolmogorov-Johnson-Mehl-Avrami and Ranganathan-Heimendahl equations, respectively. The results show that tungsten can improve the activation energy E{sub 1}{sup K} for the first crystallization in the isochronal annealing process and activation energy E{sub n} for the nucleation in the isothermal annealing process, which can be ascribed to the dissolution of tungsten in the amorphous phase. Meanwhile, tungsten can decrease the activation energy E{sub 2}{sup K} for the second crystallization in the isochronal annealing process and growth activation energy E{sub g} in the isothermal annealing process, which is possibly associated with the formation of W-rich compound after the early nucleation process.

Study on the crystallographic orientation relationship and formation mechanism of reversed austenite in economical Cr12 super martensitic stainless steel

International Nuclear Information System (INIS)

Ye, Dong; Li, Shaohong; Li, Jun; Jiang, Wen; Su, Jie; Zhao, Kunyu

2015-01-01

Effect of carbides and crystallographic orientation relationship on the formation mechanism of reversed austenite of economical Cr12 super martensitic stainless steel (SMSS) has been investigated mainly by transmission electron microscopy (TEM) and electron backscatter diffraction (EBSD). The results indicate that the M_2_3C_6 precipitation and the formation of the reversed austenite have the interaction effect during tempering process in SMSS. The reversed austenite forms intensively at the sub-block boundary and the lath boundary within a misorientation range of 0–60°. M_2_3C_6 has the same crystallographic orientation relationship with reversed austenite. There are two different kinds of formation modes for reversed austenite. One is a nondiffusional shear reversion; the other is a diffusion transformation. Both are strictly limited by crystallographic orientation relationship. The austenite variants are limited to two kinds within one packet and five kinds within one prior austenite grain. - Highlights: • Reversed austenite forms at martensite boundaries with misorientation of 0–60° • M_2_3C_6 precipitation and reversed austenite formation have the interaction effect. • Two austenite variants with different orientations can be formed inside a packet. • Two reversed austenite formation modes: shear reversion; diffusion transformation

Study on the crystallographic orientation relationship and formation mechanism of reversed austenite in economical Cr12 super martensitic stainless steel

Energy Technology Data Exchange (ETDEWEB)

Ye, Dong; Li, Shaohong; Li, Jun; Jiang, Wen [Faculty of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093 (China); Su, Jie [Institute for Structural Materials, Central Iron and Steel Research Institute, Beijing 100081 (China); Zhao, Kunyu, E-mail: kyzhaoy@sina.com [Faculty of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093 (China)

2015-11-15

Effect of carbides and crystallographic orientation relationship on the formation mechanism of reversed austenite of economical Cr12 super martensitic stainless steel (SMSS) has been investigated mainly by transmission electron microscopy (TEM) and electron backscatter diffraction (EBSD). The results indicate that the M{sub 23}C{sub 6} precipitation and the formation of the reversed austenite have the interaction effect during tempering process in SMSS. The reversed austenite forms intensively at the sub-block boundary and the lath boundary within a misorientation range of 0–60°. M{sub 23}C{sub 6} has the same crystallographic orientation relationship with reversed austenite. There are two different kinds of formation modes for reversed austenite. One is a nondiffusional shear reversion; the other is a diffusion transformation. Both are strictly limited by crystallographic orientation relationship. The austenite variants are limited to two kinds within one packet and five kinds within one prior austenite grain. - Highlights: • Reversed austenite forms at martensite boundaries with misorientation of 0–60° • M{sub 23}C{sub 6} precipitation and reversed austenite formation have the interaction effect. • Two austenite variants with different orientations can be formed inside a packet. • Two reversed austenite formation modes: shear reversion; diffusion transformation.

Effect of alloying elements on solidification of primary austenite in Ni-Mn-Cu cast iron

Directory of Open Access Journals (Sweden)

A. Janus

2011-04-01

Full Text Available Within the research, determined were direction and intensity of alloying elements influence on solidification way (directional orvolumetric of primary austenite dendrites in hypoeutectic austenitic cast iron Ni-Mn-Cu. 50 cast shafts dia. 20 mm were analysed.Chemical composition of the alloy was as follows: 1.7 to 3.3 % C, 1.4 to 3.1 % Si, 2.8 to 9.9 % Ni, 0.4 to 7.7 % Mn, 0 to 4.6 % Cu, 0.14 to0.16 % P and 0.03 to 0.04 % S. The discriminant analysis revealed that carbon influences solidification of primary austenite dendrites most intensively. It clearly increases the tendency to volumetric solidification. Influence of the other elements is much weaker. This means that the solidification way of primary austenite dendrites in hypoeutectic austenitic cast iron Ni-Mn-Cu does not differ from that in an unalloyed cast iron.

Production and several properties of single crystal austenitic stainless steels

International Nuclear Information System (INIS)

Okamoto, Kazutaka; Yoshinari, Akira; Kaneda, Junya; Aono, Yasuhisa; Kato, Takahiko

1998-01-01

The single crystal austenitic stainless steels Type 316L and 304L were grown in order to improve the resistance to stress corrosion cracking (SCC) using a unidirectional solidification method which can provide the large size single crystals. The mechanical properties and the chemical properties were examined. The orientation and temperature dependence of tensile properties of the single crystals were measured. The yield stress of the single crystal steels are lower than those of the conventional polycrystal steels because of the grain boundary strength cannot be expected in the single crystal steels. The tensile properties of the single crystal austenitic stainless steel Type 316L depend strongly on the orientation. The tensile strength in orientation are about 200 MPa higher than those in the and orientations. The microstructure of the single crystal consists of a mixture of the continuous γ-austenitic single crystal matrix and the δ-ferrite phase so that the effects of the γ/δ boundaries on the chemical properties were studied. The effects of the δ-ferrite phases and the γ/δ boundaries on the resistance to SCC were examined by the creviced bent beam test (CBB test). No crack is observed in all the CBB test specimens of the single crystals, even at the γ/δ boundaries. The behavior of the radiation induced segregation (RIS) at the γ/δ boundaries in the single crystal austenitic stainless steel Type 316L was evaluated by the electron irradiation test in the high voltage electron microscope (HVEM). The depletion of oversized solute chromium at the γ/δ boundary in the single crystal austenitic stainless steel Type 316L is remarkably lower than that at the grain boundary in the polycrystalline-type 316L. (author)

Carburization behavior of AISI 316LN austenitic stainless steel - Experimental studies and modeling

Energy Technology Data Exchange (ETDEWEB)

Sudha, C. [Physical Metallurgy Division, Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102, Tamilnadu (India); Sivai Bharasi, N. [Corrosion Science and Technology Division, Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102, Tamilnadu (India); Anand, R. [Physical Metallurgy Division, Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102, Tamilnadu (India); Shaikh, H., E-mail: hasan@igcar.gov.i [Corrosion Science and Technology Division, Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102, Tamilnadu (India); Dayal, R.K. [Corrosion Science and Technology Division, Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102, Tamilnadu (India); Vijayalakshmi, M. [Physical Metallurgy Division, Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102, Tamilnadu (India)

2010-07-31

AISI type 316LN austenitic stainless steel was exposed to flowing sodium at 798 K for 16,000 h in the bi-metallic (BIM) sodium loop. A modified surface layer of 10 {mu}m width having a ferrite structure was detected from X-ray diffraction and electron micro probe based analysis. Beneath the modified surface layer a carburized zone of 60 {mu}m width was identified which was found to consist of M{sub 23}C{sub 6} carbides. A mathematical model based on finite difference technique was developed to predict the carburization profiles in sodium exposed austenitic stainless steel. In the computation, effect of only chromium on carbon diffusion was considered. Amount of carbon remaining in solution was determined from the solubility parameter. The predicted profile showed a reasonably good match with the experimental profile. Calculations were extended to simulate the thickness of the carburized layer after exposure to sodium for a period of 40 years. Attempt was also made to predict the carburization profiles based on equilibrium calculations using Dictra and Thermocalc which contain both thermodynamic and kinetic databases for the system under consideration.

Evolución microestructural del acero austenítico al manganeso sometido a tratamiento térmico de temple y revenido Microstructural evolution of manganese austenitic steel submitted to thermal treatments of quenching and tempering

Directory of Open Access Journals (Sweden)

Óscar Fabián Higuera Cobos

2010-07-01

Full Text Available En el presente trabajo de investigación se evaluaron los cambios microestructurales en aceros austeníticos al manganeso con 9 y 13% Mn en presencia de cromo (1.4 - 2.0% . Se evaluó el ciclo térmico de temple y revenido sobre la estabilidad de la fase austenita y la presencia de compuestos de segunda fase como carburos de hierro y cromo del tipo (Fe, Mn3C y (Fe, Cr7C3. La temperatura de austenización fue de 1050 °C, con un tiempo de sostenimiento de 1 hora y el medio de enfriamiento agua. Los tratamientos de revenido se efectuaron en un rango de 200 a 800 °C con intervalos de 200 °C y tiempo de permanencia 2 horas. Para este análisis el material se sometió a pruebas de caracterización tales como: microscopia electrónica de barrido (SEM-EDS, espectrometría de emisión óptica y difracción de rayos X, en estado de suministro y bonificado.In this study the microstructural changes in manganese austenitic steel with 9 and 13% Mn in presence of chromium with (1,4-2,0% was evaluated, thermal cycles of quenching and tempering in order to evaluate the influence of kinetic of cooling on the stability of the phase austenite and the presence of composed of second phase like iron and chromium carbides of type (Fe, Mn3C and (Fe, Cr7C3. were also evaluated. The temperature of austenitizing was of 1050 °C, with a time of support of 1 hour and means of cooling water. The tempering treatments took place in a rank of 200 to 800 °C with intervals of 200 °C and dwell time 2 hours. The material was evaluated by electronic microscopy of sweeping (SEM-EDS, spectrometry of optical emission and X-ray diffraction, in state as cast and heat treating.

Modeling of austenite to ferrite transformation

Indian Academy of Sciences (India)

395–398. c Indian Academy of Sciences. Modeling of austenite to ferrite transformation. MOHSEN KAZEMINEZHAD. ∗. Department of Materials Science and Engineering, Sharif University of Technology, Azadi Avenue, Tehran, Iran. MS received 17 January 2011; revised 9 July 2011. Abstract. In this research, an algorithm ...

Development of a lean duplex stainless steel

Energy Technology Data Exchange (ETDEWEB)

Liljas, M.; Johansson, P.; Liu Hui-Ping; Olsson, C.O.A. [Avesta Research Centre, Avesta (Sweden). Outokumpu Stainless

2008-06-15

The classic series of duplex stainless steels shows very high corrosion resistance and can be used for very demanding applications. A new lean duplex steel, LDX 2101 {sup registered} (EN 1.4162, UNS S32101), has been developed with corrosion resistance on a par with standard austenitic grades. Application areas include: structural components, chemical industry, tanks and containers. The steel was designed to have equal amounts of ferrite and austenite in annealed condition and with an austenite that is stable against strain-induced martensite. Thanks to its high nitrogen content, the steel has a fast austenite reformation when subjected to thermal cycling, e.g. welding. Unlike conventional duplex grades, the formation of intermetallic phase is very sluggish, although precipitation of nitrides and carbides has a certain impact on material properties after exposure in the temperature range 600 to 800 C. The precipitation behaviour after different isothermal treatments is described and its influence on different product properties is shown. A good agreement was found between impact toughness and corrosion resistance for a wide range of thermal treatments. (orig.)

Study of irradiation damage structures in austenitic stainless steels

Energy Technology Data Exchange (ETDEWEB)

Hamada, Shozo [Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan). Tokai Research Establishment

1997-08-01

The irradiation damage microstructures in austenitic stainless steels, which have been proposed to be a candidate of structural materials of a fusion reactor, under ions and neutrons irradiation have been studied. In ion irradiation experiments, cross-sectional observation of the depth distribution of damage formed due to ion irradiation became available. Comparison and discussion between experimental results with TEM and the calculated ones in the depth profiles of irradiation damage microstructures. Further, dual-phase stainless steels, consisted of ferritic/austenitic phases, showed irradiation-induced/enhanced precipitation during ion irradiation. High Flux Isotope Reactor with high neutron fluxes was employed in neutron-irradiation experiments. Swelling of 316 steel showed irradiation temperature dependence and this had strong correlation with phase instability under heavy damage level. Swelling resistance of Ti-modified austenitic stainless steel, which has good swelling resistance, decreased during high damage level. This might be caused by the instability of Ti-carbide particles. The preparation method to reduce higher radioactivity of neutron-irradiated TEM specimen was developed. (author). 176 refs.

Study of irradiation damage structures in austenitic stainless steels

International Nuclear Information System (INIS)

Hamada, Shozo

1997-08-01

The irradiation damage microstructures in austenitic stainless steels, which have been proposed to be a candidate of structural materials of a fusion reactor, under ions and neutrons irradiation have been studied. In ion irradiation experiments, cross-sectional observation of the depth distribution of damage formed due to ion irradiation became available. Comparison and discussion between experimental results with TEM and the calculated ones in the depth profiles of irradiation damage microstructures. Further, dual-phase stainless steels, consisted of ferritic/austenitic phases, showed irradiation-induced/enhanced precipitation during ion irradiation. High Flux Isotope Reactor with high neutron fluxes was employed in neutron-irradiation experiments. Swelling of 316 steel showed irradiation temperature dependence and this had strong correlation with phase instability under heavy damage level. Swelling resistance of Ti-modified austenitic stainless steel, which has good swelling resistance, decreased during high damage level. This might be caused by the instability of Ti-carbide particles. The preparation method to reduce higher radioactivity of neutron-irradiated TEM specimen was developed. (author). 176 refs

Cryogenic properties of austenitic stainless steels for superconducting magnet

International Nuclear Information System (INIS)

Nohara, K.; Kato, T.; Ono, Y.; Sasaki, T.; Suzuki, S.

1983-01-01

The present study examines the magnetic and mechanical properties of a variety of austenitic stainless steels and high maganese steel which are candidate materials for the superconducting magnet attached to high energy particle accelerators. The effect of a specified heat treatment for the precipitation of intermetallic compound Nb3Sn to be used as superconductor on ductility and toughness are especially examined. It is found that nitrogen-strengthened austenitic stainless steels have high strength and good ductility and toughness, but that these are destroyed by precipitation treatment. The poor ductility and toughness after precipitation are caused by a weakening of the grain boundaries due to the agglomerated chromium carbide percipitates. The addition of vanadium suppresses this effect by refining the grain. Austenitic steels are found to have low magnetic permeabilities and Neel temperatures, and show serrated flow in traction test due to strained martensitic transformation. High manganese steel has extremely low permeability, a Neel temperature about room temperature, and has a serrated flow in traction test due to adiabatic deformation at liquid helium temperature

Effects of aging in containment spray injection system of PWR reactor containment

International Nuclear Information System (INIS)

Borges, Diogo da S.; Lava, Deise D.; Affonso, Renato R.W.; Guimaraes, Antonio C.F.; Moreira, Maria de L.

2014-01-01

This paper presents a contribution to the study of the components aging process in commercial plants of Pressurized Water Reactors (PWR). The analysis is done by applying the method of Fault trees, Monte Carlo Method and Fussell-Vesely Importance Measurement. The study on the aging of nuclear plants, is related to economic factors involved directly with the extent of their operational life, and also provides important data on issues of safety. The most recent case involving the process of extending the life of a PWR plant can be seen in Angra 1 Nuclear Power Plant by investing $ 27 million in the installation of a new reactor cover. The corrective action generated an extension of the useful life of Angra 1 estimated in twenty years, and a great savings compared to the cost of building a new plant and the decommissioning of the first, if it had reached the operation time out 40 years. The extension of the lifetime of a nuclear power plant must be accompanied by special attention from the most sensitive components of the systems to the aging process. After the application of the methodology (aging analysis of Containment Spray Injection System (CSIS)) proposed in this paper, it can be seen that increasing the probability of failure of each component, due to the aging process, generate an increased general unavailability of the system that contains these basic components. The final results obtained were as expected and can contribute to the maintenance policy, preventing premature aging in nuclear power systems

TEM studies of plasma nitrided austenitic stainless steel.

Science.gov (United States)

Stróz, D; Psoda, M

2010-03-01

Cross-sectional transmission electron microscopy and X-ray phase analysis were used to study the structure of a layer formed during nitriding the AISI 316L stainless steel at temperature 440 degrees C. It was found that the applied treatment led to the formation of 6-microm-thick layer of the S-phase. There is no evidence of CrN precipitation. The X-ray diffraction experiments proved that the occurred austenite lattice expansion - due to nitrogen atoms - depended on the crystallographic direction. The cross-sectional transmission electron microscopy studies showed that the layer consisted of a single cubic phase that contained a lot of defects such as dislocations, stacking faults, slip bands and twins. The high-resolution electron microscopy observations were applied to study the defect formation due to the nitriding process. It was shown that the presence of great number of stacking faults leads to formation of nanotwins. Weak, forbidden {100} reflections were still another characteristic feature of the S-phase. These were not detected in the X-ray spectra of the phase. Basing on the high-resolution electron microscopy studies it can be suggested that the short-range ordering of the nitrogen atoms in the octahedral sites inside the f.c.c. matrix lattice takes place and gives rise to appearance of these spots. It is suggested that the cubic lattice undergoes not only expansion but also slight rombohedral distortion that explains differences in the lattice expansion for different crystallographic directions.

Evolution of secondary phases in 0.17C-16Cr-11Mn-0.43N austenitic stainless steel at 800 and 850°C: Thermodynamic modeling of phase equilibria and experimental kinetic studies

Directory of Open Access Journals (Sweden)

Čička R.

2012-01-01

Full Text Available The precipitation of secondary phases was investigated in the 0.17C-16Cr-11Mn-0.43N austenitic stainless steel during annealing at 800 and 850°C for times between 5 min and 100 h. Light microscopy, transmission electron microscopy, energy dispersive X-ray spectroscopy, scanning electron microscopy, and differential thermal analysis were used in experiments. Thermodynamic calculations were done by the ThermoCalc database software package. Cr2N and M23C6 were considered to be stable phases at the annealing temperatures. Cells consisting of alternating Cr2N and austenite lamellae were observed in the steel microstructure after sufficiently long annealing. The metastable chi phase was also found in all the annealed samples. After 100 h of annealing the equilibrium sigma started to precipitate. The thermodynamically predicted M6C was not confirmed experimentally in any of the annealed samples. DTA analysis showed the initial precipitation stage was followed by the phase dissolution. For the investigated steel the computational thermodynamics can be used only for qualitative interpretation of the experimental results as the measured endothermal peaks were found to be shifted of about 50 ÷ 70°C related to the computed results.

Determination of local carbon content in austenite during intercritical annealing of dual phase steels by PEELS analysis

International Nuclear Information System (INIS)

Garcia-Junceda, A.; Caballero, F.G.; Capdevila, C.; Garcia de Andres, C.

2007-01-01

Parallel electron energy loss spectroscopy has allowed to analyse and quantify local variations in the carbon concentration of austenite islands transformed during the intercritical annealing treatment of commercial dual-phase steels. These changes in the carbon content of different austenite regions are responsible for the different volume fractions of tempered martensite, martensite and retained austenite obtained after intercritical annealing and overaging treatment. This technique reveals how carbon distribution in austenite evolves as the transformation process advances

Isotherm, kinetic, and thermodynamic study of ciprofloxacin sorption on sediments.

Science.gov (United States)

Mutavdžić Pavlović, Dragana; Ćurković, Lidija; Grčić, Ivana; Šimić, Iva; Župan, Josip

2017-04-01

In this study, equilibrium isotherms, kinetics and thermodynamics of ciprofloxacin on seven sediments in a batch sorption process were examined. The effects of contact time, initial ciprofloxacin concentration, temperature and ionic strength on the sorption process were studied. The K d parameter from linear sorption model was determined by linear regression analysis, while the Freundlich and Dubinin-Radushkevich (D-R) sorption models were applied to describe the equilibrium isotherms by linear and nonlinear methods. The estimated K d values varied from 171 to 37,347 mL/g. The obtained values of E (free energy estimated from D-R isotherm model) were between 3.51 and 8.64 kJ/mol, which indicated a physical nature of ciprofloxacin sorption on studied sediments. According to obtained n values as measure of intensity of sorption estimate from Freundlich isotherm model (from 0.69 to 1.442), ciprofloxacin sorption on sediments can be categorized from poor to moderately difficult sorption characteristics. Kinetics data were best fitted by the pseudo-second-order model (R 2  > 0.999). Thermodynamic parameters including the Gibbs free energy (ΔG°), enthalpy (ΔH°) and entropy (ΔS°) were calculated to estimate the nature of ciprofloxacin sorption. Results suggested that sorption on sediments was a spontaneous exothermic process.

Dissolution and oxidation behaviour of various austenitic steels and Ni rich alloys in lead-bismuth eutectic at 520 °C

Energy Technology Data Exchange (ETDEWEB)

Roy, Marion, E-mail: marion.roy@cea.fr [CEA, DEN, DPC, SCCME, Laboratoire d’Etude de la Corrosion Non Aqueuse, F-91191 Gif-sur-Yvette (France); Martinelli, Laure, E-mail: laure.martinelli@cea.fr [CEA, DEN, DPC, SCCME, Laboratoire d’Etude de la Corrosion Non Aqueuse, F-91191 Gif-sur-Yvette (France); Ginestar, Kevin, E-mail: kevin.ginestar@cea.fr [CEA, DEN, DPC, SCCME, Laboratoire d’Etude de la Corrosion Non Aqueuse, F-91191 Gif-sur-Yvette (France); Favergeon, Jérôme, E-mail: jerome.favergeon@utc.fr [Laboratoire Roberval, UMR 7337, Université de Technologie de Compiègne, Centre de Recherche de Royallieu, CS 60319, 60203 Compiègne Cedex (France); Moulin, Gérard [Laboratoire Roberval, UMR 7337, Université de Technologie de Compiègne, Centre de Recherche de Royallieu, CS 60319, 60203 Compiègne Cedex (France)

2016-01-15

Ten austenitic steels and Ni rich alloys were tested in static lead-bismuth eutectic (LBE) at 520 °C in order to obtain a selection of austenitic steels having promising corrosion behaviour in LBE. A test of 1850 h was carried out with a dissolved oxygen concentration between 10{sup −9} and 5 10{sup −4} g kg{sup −1}. The combination of thermodynamic of the studied system and literature results leads to the determination of an expression of the dissolved oxygen content in LBE as a function of temperature: RT(K)ln[O](wt%) = −57584/T(K) −55.876T(K) + 254546 (R is the gas constant in J mol{sup −1} K{sup −1}). This relation can be considered as a threshold of oxygen content above which only oxidation is observed on the AISI 316L and AISI 304L austenitic alloys in static LBE between 400 °C and 600 °C. The oxygen content during the test leads to both dissolution and oxidation of the samples during the first 190 h and leads to pure oxidation for the rest of the test. Results of mixed oxidation and dissolution test showed that only four types of corrosion behaviour were observed: usual austenitic steels and Ni rich alloys behaviour including the reference alloy 17Cr-12Ni-2.5Mo (AISI 316LN), the 20Cr-31Ni alloy one, the Si containing alloy one and the Al containing alloy one. According to the proposed criteria of oxidation and dissolution kinetics, silicon rich alloys and aluminum rich alloy presented a promising corrosion behaviour. - Highlights: • 10 austenitic steels and Ni rich alloys were tested in LBE at 520 °C with dissolved oxygen content between 10{sup -9} and 5 10{sup -4} wt%. • It is shown that only thermodynamics cannot explain the Ni rich alloys corrosion behaviour in LBE. • The role of oxygen on corrosion behaviour in LBE was highlighted. • An equilibrium line was defined above which only oxidation has occurred on 316L: RTln[O](wt%) = -57584/T(K)-55.876T(K)+254546. • 18Cr-15Ni-3.7Si, 21Cr-11Ni-1.6Si and 14Cr-25Ni-3.5Al

Intergranular Corrosion Behavior of Low-Nickel and 304 Austenitic Stainless Steels

Science.gov (United States)

Bansod, Ankur V.; Patil, Awanikumar P.; Moon, Abhijeet P.; Khobragade, Nilay N.

2016-09-01

Intergranular corrosion (IGC) susceptibility for Cr-Mn austenitic stainless steel and 304 austenitic stainless steel (ASS) was estimated using electrochemical techniques. Optical and SEM microscopy studies were carried out to investigate the nature of IGC at 700 °C with increasing time (15, 30, 60, 180, 360, 720, 1440 min) according to ASTM standard 262 A. Quantitative analysis was performed to estimate the degree of sensitization (DOS) using double loop electrochemical potentiokinetic reactivation (DLEPR) and EIS technique. DLEPR results indicated that with the increase in thermal aging duration, DOS becomes more severe for both types of stainless steel. The DOS for Cr-Mn ASS was found to be higher (65.12% for 1440 min) than that of the AISI 304 ASS (23% for 1440 min). The higher degree of sensitization resulted in lowering of electrical charge capacitance resistance. Chronoamperometry studies were carried out at a passive potential of 0.4 V versus SCE and was observed to have a higher anodic dissolution of the passive film of Cr-Mn ASS. EDS studies show the formation of chromium carbide precipitates in the vicinity of the grain boundary. The higher Mn content was also observed for Cr-Mn ASS at the grain boundary.

Cinéticas de transformación de fases a 850 ºC de aceros inoxidables dúplex clásicos (2205 y 2507 y de uno nuevo de bajo contenido en níquel y alto en manganeso (DBNi

Directory of Open Access Journals (Sweden)

Rodríguez, M. P.

2004-04-01

Full Text Available Austenitic-ferritic stainless steels are formed by ferrite and austenite in a variable proportion between 30 % and 70 %. Their chemical composition conditions the ageing processes that can happen during heat treatments, where phases that hardens and brittles the material can be generated. Evolution of a new duplex stainless steel with lower nickel and higher nitrogen and manganese content maintained at 1123 K (critical precipitation temperature up to 8 hours compared to classical ones (2205 and 2507 is presented. The study, done by magnetic measurements, XRD, optical and scanning electron microscopy and microanalysis, revealed a roughly similar behaviour for the three steels. The new one presents a higher initial stability, probably due to the high nitrogen and manganese contents; however, it also produces the higher final transformation due to the higher initial ferrite. A fine comparative analysis was done to correctly identify any phase; an accurate microanalysis in every generated phase was performed. All the steels tested are initially made on ferrite and austenite. After the ageing treatment, 8 hours at 1123 K, in the 2205 duplex steel a strong precipitation of sigma phase is observed, austenite and some of the original ferrite are also present; ferrite completely transforms in the 2507 duplex and austenite, sigma, secondary austenite and chromium nitride can be found; regarding the new duplex steel DBNi, austenite, ferrite, sigma, chi and chromium nitrides are detected.

Los aceros dúplex austeno-ferríticos están constituidos por ferrita y austenita en proporciones variables del 30 % al 70 %. Su composición química condiciona los procesos de envejecimiento que sufren durante los tratamientos térmicos, cuando se generan fases que endurecen y fragilizan el material. Este trabajo estudia la evolución de un nuevo inoxidable dúplex con bajo contenido en níquel y alto en nitrógeno y manganeso a 1123 K (temperatura crítica de

Residual stress studies of austenitic and ferritic steels

International Nuclear Information System (INIS)

Chrenko, R.M.

1978-01-01

Residual studies have been made on austenitic and ferritic steels of the types used as structural materials. The residual stress results presented here will include residual stress measurements in the heat-affected zone on butt welded Type 304 stainless steel pipes, and the stresses induced in Type 304 austenitic stainless steel and Type A508 ferritic steel by several surface preparations. Such surface preparation procedures as machining and grinding can induce large directionality effects in the residual stresses determined by X-ray techniques and some typical data will be presented. A brief description is given of the mobile X-ray residual stress apparatus used to obtain most of the data in these studies. (author)

The Effect of Ultrafast Heating on Cold-Rolled Low Carbon Steel: Formation and Decomposition of Austenite

Directory of Open Access Journals (Sweden)

Felipe Manuel Castro Cerda

2016-12-01

Full Text Available The effect of heating rate on the formation and decomposition of austenite was investigated on cold-rolled low carbon steel. Experiments were performed at two heating rates, 150 °C/s and 1500 °C/s, respectively. The microstructures were characterized by means of scanning electron microscopy (SEM and electron backscattered diffraction (EBSD. Experimental evidence of nucleation of austenite in α/θ, as well as in α/α boundaries is analyzed from the thermodynamic point of view. The increase in the heating rates from 150 °C/s to 1500 °C/s has an impact on the morphology of austenite in the intercritical range. The effect of heating rate on the austenite formation mechanism is analyzed combining thermodynamic calculations and experimental data. The results provide indirect evidence of a transition in the mechanism of austenite formation, from carbon diffusion control to interface control mode. The resulting microstructure after the application of ultrafast heating rates is complex and consists of a mixture of ferrite with different morphologies, undissolved cementite, martensite, and retained austenite.