WorldWideScience

Sample records for irradiated solid beryllium

  1. Fracture toughness of irradiated beryllium

    International Nuclear Information System (INIS)

    Beeston, J.M.

    1978-01-01

    The fracture toughness of nuclear grade hot-pressed beryllium upon irradiation to fluences of 3.5 to 5.0 x 10 21 n/cm 2 , E greater than 1 MeV, was determined. Procedures and data relating to a round-robin test contributing to a standard ASTM method for unirradiated beryllium are discussed in connection with the testing of irradiated specimens. A porous grade of beryllium was also irradiated and tested, thereby enabling some discrimination between the models for describing the fracture toughness behavior of porous beryllium. The fracture toughness of unirradiated 2 percent BeO nuclear grade beryllium was 12.0 MPa m/sup 1 / 2 /, which was reduced 60 percent upon irradiation at 339 K and testing at 295 K. The fracture toughness of a porous grade of beryllium was 13.1 MPa m/sup 1 / 2 /, which was reduced 68 percent upon irradiation and testing at the same conditions. Reasons for the reduction in fracture toughness upon irradiation are discussed

  2. Mechanical properties of irradiated beryllium

    International Nuclear Information System (INIS)

    Beeston, J.M.; Longhurst, G.R.; Wallace, R.S.

    1992-01-01

    Beryllium is planned for use as a neutron multiplier in the tritium breeding blanket of the International Thermonuclear Experimental Reactor (ITER). After fabricating samples of beryllium at densities varying from 80 to 100% of the theoretical density, we conducted a series of experiments to measure the effect of neutron irradiation on mechanical properties, especially strength and ductility. Samples were irradiated in the Advanced Test Reactor (ATR) to a neutron fluence of 2.6 x 10 25 n/m 2 (E > MeV) at an irradiation temperature of 75deg C. These samples were subsequently compression-tested at room temperature, and the results were compared with similar tests on unirradiated specimens. We found that the irradiation increased the strength by approximately four times and reduced the ductility to approximately one fourth. Failure was generally ductile, but the 80% dense irradiated samples failed in brittle fracture with significant generation of fine particles and release of small quantities of tritium. (orig.)

  3. Mechanical properties of irradiated beryllium

    Science.gov (United States)

    Beeston, J. M.; Longhurst, G. R.; Wallace, R. S.; Abeln, S. P.

    1992-10-01

    Beryllium is planned for use as a neutron multiplier in the tritium breeding blanket of the International Thermonuclear Experimental Reactor (ITER). After fabricating samples of beryllium at densities varying from 80 to 100% of the theoretical density, we conducted a series of experiments to measure the effect of neutron irradiation on mechanical properties, especially strength and ductility. Samples were irradiated in the Advanced Test Reactor (ATR) to a neutron fluence of 2.6 × 10 25 n/m 2 ( E > 1 MeV) at an irradiation temperature of 75°C. These samples were subsequently compression-tested at room temperature, and the results were compared with similar tests on unirradiated specimens. We found that the irradiation increased the strength by approximately four times and reduced the ductility to approximately one fourth. Failure was generally ductile, but the 80% dense irradiated samples failed in brittle fracture with significant generation of fine particles and release of small quantities of tritium.

  4. Mechanical properties of irradiated beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Beeston, J.M.; Longhurst, G.R.; Wallace, R.S. (EG and G Idaho, Inc., Idaho Falls, ID (United States). Idaho National Engineering Lab.); Abeln, S.P. (EG and G Rocky Flats, Inc., Golden, CO (United States))

    1992-10-01

    Beryllium is planned for use as a neutron multiplier in the tritium breeding blanket of the International Thermonuclear Experimental Reactor (ITER). After fabricating samples of beryllium at densities varying from 80 to 100% of the theoretical density, we conducted a series of experiments to measure the effect of neutron irradiation on mechanical properties, especially strength and ductility. Samples were irradiated in the Advanced Test Reactor (ATR) to a neutron fluence of 2.6 x 10[sup 25] n/m[sup 2] (E > MeV) at an irradiation temperature of 75deg C. These samples were subsequently compression-tested at room temperature, and the results were compared with similar tests on unirradiated specimens. We found that the irradiation increased the strength by approximately four times and reduced the ductility to approximately one fourth. Failure was generally ductile, but the 80% dense irradiated samples failed in brittle fracture with significant generation of fine particles and release of small quantities of tritium. (orig.).

  5. Tritium release from neutron irradiated beryllium pebbles

    Energy Technology Data Exchange (ETDEWEB)

    Scaffidi-Argentina, F.; Werle, H. [Forschungszentrum Karlsruhe GmbH Technik und Umwelt (Germany). Inst. fuer Neutronenphysik und Reactortechnik

    1998-01-01

    One of the most important open issues related to beryllium for fusion applications refers to the kinetics of the tritium release as a function of neutron fluence and temperature. The EXOTIC-7 as well as the `Beryllium` experiments carried out in the HFR reactor in Petten are considered as the most detailed and significant tests for investigating the beryllium response under neutron irradiation. This paper reviews the present status of beryllium post-irradiation examinations performed at the Forschungszentrum Karlsruhe with samples from the above mentioned irradiation experiments, trying to elucidate the tritium release controlling processes. In agreement with previous studies it has been found that release starts at about 500-550degC and achieves a maximum at about 700-750degC. The observed release at about 500-550degC is probably due to tritium escaping from chemical traps, while the maximum release at about 700-750degC is due to tritium escaping from physical traps. The consequences of a direct contact between beryllium and ceramics during irradiation, causing tritium implanting in a surface layer of beryllium up to a depth of about 40 mm and leading to an additional inventory which is usually several times larger than the neutron-produced one, are also presented and the effects on the tritium release are discussed. (author)

  6. Mechanical performance of irradiated beryllium pebbles

    Energy Technology Data Exchange (ETDEWEB)

    Scaffidi-Argentina, F.; Dalle-Donne, M.; Werle, H. [Forschungszentrum Karlsruhe GmbH Technik und Umwelt (Germany). Inst. fuer Neutronenphysik und Reaktortechnik

    1998-01-01

    For the Helium Cooled Pebble Bed (HCPB) Blanket, which is one of the two reference concepts studied within the European Fusion Technology Programme, the neutron multiplier consists of a mixed bed of about 2 and 0.1-0.2 mm diameter beryllium pebbles. Beryllium has no structural function in the blanket, however microstructural and mechanical properties are important, as they might influence the material behavior under neutron irradiation. The EXOTIC-7 as well as the `Beryllium` experiments carried out in the HFR reactor in Petten are considered as the most detailed and significant tests for investigating it. This paper reviews the present status of beryllium post-irradiation examinations performed at the Forschungszentrum Karlsruhe with samples from these irradiation experiments, emphasizing the effects of irradiation of essential material properties and trying to elucidate the processes controlling the property changes. The microstructure, the porosity distribution, the impurity content, the behavior under compression loads and the compatibility of the beryllium pebbles with lithium orthosilicate (Li{sub 4}SiO{sub 4}) during the in-pile irradiation are presented and critically discussed. Qualitative information on ductility and creep obtained by hardness-type measurements are also supplied. (author)

  7. ESR investigations of gamma irradiated beryllium ceramics

    International Nuclear Information System (INIS)

    Ryabikin, Yu.A.; Polyakov, A.I.; Petukhov, Yu.V.; Bitenbaev, M.I.; Zashkvara, O.V.

    2000-01-01

    In this report the result of ESR- investigation of kinetics of radiation paramagnetic defects accumulated in beryllium ceramics under gamma irradiation are presented. The data on quantum yield and destruction rate constants of these defects under ionizing irradiation are obtained. (orig.)

  8. ESR investigations of gamma irradiated beryllium ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Ryabikin, Yu A; Polyakov, A I; Petukhov, Yu V; Bitenbaev, M I; Zashkvara, O V [Physical-Technical Inst., Almaty (Kazakhstan)

    2000-04-01

    In this report the result of ESR- investigation of kinetics of radiation paramagnetic defects accumulated in beryllium ceramics under gamma irradiation are presented. The data on quantum yield and destruction rate constants of these defects under ionizing irradiation are obtained. (orig.)

  9. Neutron irradiation behavior of ITER candidate beryllium grades

    Energy Technology Data Exchange (ETDEWEB)

    Kupriyanov, I.B.; Gorokhov, V.A.; Nikolaev, G.N. [A.A.Bochvar All-Russia Scientific Research Inst. of Inorganic Materials (VNIINM), Moscow (Russian Federation); Melder, R.R.; Ostrovsky, Z.E.

    1998-01-01

    Beryllium is one of the main candidate materials both for the neutron multiplier in a solid breeding blanket and for the plasma facing components. That is why its behaviour under the typical for fusion reactor loading, in particular, under the neutron irradiation is of a great importance. This paper presents mechanical properties, swelling and microstructure of six beryllium grades (DshG-200, TR-30, TshG-56, TRR, TE-30, TIP-30) fabricated by VNIINM, Russia and also one - (S-65) fabricated by Brush Wellman, USA. The average grain size of the beryllium grades varied from 8 to 25 {mu}m, beryllium oxide content was 0.8-3.2 wt. %, initial tensile strength was 250-680 MPa. All the samples were irradiated in active zone of SM-3 reactor up to the fast neutron fluence (5.5-6.2) {center_dot} 10{sup 21} cm{sup -2} (2.7-3.0 dpa, helium content up to 1150 appm), E > 0.1 MeV at two temperature ranges: T{sub 1} = 130-180degC and T{sub 2} = 650-700degC. After irradiation at 130-180degC no changes in samples dimensions were revealed. After irradiation at 650-700degC swelling of the materials was found to be in the range 0.1-2.1 %. Beryllium grades TR-30 and TRR, having the smallest grain size and highest beryllium oxide content, demonstrated minimal swelling, which was no more than 0.1 % at 650-700degC and fluence 5.5 {center_dot} 10{sup 21} cm{sup -2}. Tensile and compression test results and microstructure parameters measured before and after irradiation are also presented. (author)

  10. New facility for post irradiation examination of neutron irradiated beryllium

    International Nuclear Information System (INIS)

    Ishitsuka, Etsuo; Kawamura, Hiroshi

    1995-01-01

    Beryllium is expected as a neutron multiplier and plasma facing materials in the fusion reactor, and the neutron irradiation data on properties of beryllium up to 800 degrees C need for the engineering design. The acquisition of data on the tritium behavior, swelling, thermal and mechanical properties are first priority in ITER design. Facility for the post irradiation examination of neutron irradiated beryllium was constructed in the hot laboratory of Japan Materials Testing Reactor to get the engineering design data mentioned above. This facility consist of the four glove boxes, dry air supplier, tritium monitoring and removal system, storage box of neutron irradiated samples. Beryllium handling are restricted by the amount of tritium;7.4 GBq/day and 60 Co;7.4 MBq/day

  11. Thermophysical properties of solid and liquid beryllium

    International Nuclear Information System (INIS)

    Boivineau, M.; Arles, L.; Vermeulen, J.M.; Thevenin, Th.

    1993-01-01

    A submillisecond resistive heating technique under high pressure (0.12 GPa) has been used to measure selected thermophysical properties of both solid and liquid beryllium. Data have been obtained between room temperature and 2900 K. Results on enthalpy, volume expansion, electrical resistivity, and sound velocity measurements are presented

  12. Critical parameters controlling irradiation swelling in beryllium

    International Nuclear Information System (INIS)

    Dubinko, V.I.

    1995-01-01

    Radiation effects in beryllium can hardly be explained within a framework of the conventional theory based on the bias concept due to elastic interaction difference (EID) between vacancies and self-interstitial atoms (SIAs) since beryllium belongs to hexagonal close-packed metals where diffusion has been shown to be anisotropic. Diffusional anisotropy difference (DAD) between point defects changes the cavity bias for their absorption and leads to dependence of the dislocation bias on the distribution of dislocations over crystallographic directions. On the other hand, the elastic interaction between point defects and cavities gives rise to the size and gas pressure dependencies of the cavity bias, resulting in new critical quantities for bubble-void transition effects at low temperature irradiation. In the present paper, we develop the concept of the critical parameters controlling irradiation swelling with account of both DAD and EID, and take care of thermal effects as well since they are of major importance for beryllium which has an anomalously low self-diffusion activation energy. Experimental data on beryllium swelling are analyzed on the basis of the present theory. (orig.)

  13. Behavior of beryllium pebbles under irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Dalle-Donne, M.; Scaffidi-Argentina, F. [Forschungszentrum Karlsruhe GmbH Technik und Umwelt (Germany). Inst. fuer Neutronenphysik und Reactortechnik; Baldwin, D.L.; Gelles, D.S.; Greenwood, L.R.; Kawamura, H.; Oliver, B.M.

    1998-01-01

    Beryllium pebbles are being considered in fusion reactor blanket designs as neutron multiplier. An example is the European `Helium Cooled Pebble Bed Blanket.` Several forms of beryllium pebbles are commercially available but little is known about these forms in response to fast neutron irradiation. Commercially available beryllium pebbles have been irradiated to approximately 1.3 x 10{sup 22} n/cm{sup 2} (E>1 MeV) at 390degC. Pebbles 1-mm in diameter manufactured by Brush Wellman, USA and by Nippon Gaishi Company, Japan, and 3-mm pebbles manufactured by Brush Wellman were included. All were irradiated in the below-core area of the Experimental Breeder Reactor-II in Idaho Falls, USA, in molybdenum alloy capsules containing helium. Post-irradiation results are presented on density change measurements, tritium release by assay, stepped-temperature anneal, and thermal ramp desorption tests, and helium release by assay and stepped-temperature anneal measurements, for Be pebbles from two manufacturing methods, and with two specimen diameters. The experimental results on density change and tritium and helium release are compared with the predictions of the code ANFIBE. (author)

  14. Interaction of hydrogen and its isotopes with irradiated beryllium

    International Nuclear Information System (INIS)

    Tazhibaeva, I.L.; Shestakov, V.P.; Klepikov, A.Kh.; Pomanenko, O.G.; Chikhraj, E.V.; Kenzhin, E.A.; Zverev, V.V.; Kolbanenkov, A.N.

    2000-01-01

    In the article the results of experiments on hydrogen and its isotopes accumulation and gas-release from irradiated beryllium are presented. The irradiation was conducted at different media and temperatures in the RA and IVG.1M reactors. The measurements were carried out by thermal desorption method. Hydrogen release from beryllium samples saturated at different conditions were calculated. Dependence of hydrogen confinement character in beryllium from grain orientation in the sample, temperature and irradiation rate was revealed

  15. Electron microscope study of irradiated beryllium oxide

    International Nuclear Information System (INIS)

    Bisson, A.A.

    1965-06-01

    The beryllium oxide is studied first by fractography, before and after irradiation, using sintered samples. The fractures are examined under different aspects. The higher density sintered samples, with transgranular fractures are the most interesting for a microscopic study. It is possible to mark the difference between the 'pores' left by the sintering process and the 'bubbles' of gases that can be produced by former thermal treatments. After irradiation, the grain boundaries are very much weakened. By annealing, it is possible to observe the evolution of the gases produced by the reaction (n, 2n) and (n. α) and gathered on the grain boundaries. The irradiated beryllium oxide is afterwards studied by transmission. For that, a simple method has been used: little chips of the crushed material are examined. Clusters of point defects produced by neutrons are thus detected in crystals irradiated at the three following doses: 6 x 10 19 , 9 x 10 19 and 2 x 10 20 n f cm -2 at a temperature below 100 deg. C. For the irradiation at 6 x 10 19 n f cm -2 , the defects are merely visible, but at 2 x l0 20 n f cm -2 the crystals an crowded with clusters and the Kikuchi lines have disappeared from the micro-diffraction diagrams. The evolution of the clusters into dislocation loops is studied by a series of annealings. The activation energy (0,37 eV) calculated from the annealing curves suggests that it must be interstitials that condense into dislocation loops. Samples irradiated at high temperatures (650, 900 and 1100 deg. C) are also studied. In those specimens the size of the loops is not the same as the equilibrium size obtained after out of pile annealing at the same temperature. Those former loops are more specifically studied and their Burgers vector is determined by micro-diffraction. (author) [fr

  16. Study on neutron irradiation behavior of beryllium as neutron multiplier

    Energy Technology Data Exchange (ETDEWEB)

    Ishitsuka, Etsuo [Japan Atomic Energy Research Inst., Oarai, Ibaraki (Japan). Oarai Research Establishment

    1998-03-01

    More than 300 tons beryllium is expected to be used as a neutron multiplier in ITER, and study on the neutron irradiation behavior of beryllium as the neutron multiplier with Japan Materials Testing Reactor (JMTR) were performed to get the engineering data for fusion blanket design. This study started as the study on the tritium behavior in beryllium neutron reflector in order to make clear the generation mechanism on tritium of JMTR primary coolant since 1985. These experiences were handed over to beryllium studies for fusion study, and overall studies such as production technology of beryllium pebbles, irradiation behavior evaluation and reprocessing technology have been started since 1990. In this presentation, study on the neutron irradiation behavior of beryllium as the neutron multiplier with JMTR was reviewed from the point of tritium release, thermal properties, mechanical properties and reprocessing technology. (author)

  17. Steam-chemical reactivity for irradiated beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Anderl, R.A.; McCarthy, K.A.; Oates, M.A.; Petti, D.A.; Pawelko, R.J.; Smolik, G.R. [Idaho National Engineering and Environmental Lab., Idaho Falls, ID (United States)

    1998-01-01

    This paper reports the results of an experimental investigation to determine the influence of neutron irradiation effects and annealing on the chemical reactivity of beryllium exposed to steam. The work entailed measurements of the H{sub 2} generation rates for unirradiated and irradiated Be and for irradiated Be that had been previously annealed at different temperatures ranging from 450degC to 1200degC. H{sub 2} generation rates were similar for irradiated and unirradiated Be in steam-chemical reactivity experiments at temperatures between 450degC and 600degC. For irradiated Be exposed to steam at 700degC, the chemical reactivity accelerated rapidly and the specimen experienced a temperature excursion. Enhanced chemical reactivity at temperatures between 400degC and 600degC was observed for irradiated Be annealed at temperatures of 700degC and higher. This reactivity enhancement could be accounted for by the increased specific surface area resulting from development of a surface-connected porosity in the irradiated-annealed Be. (author)

  18. Physical properties of beryllium oxide - Irradiation effects

    International Nuclear Information System (INIS)

    Elston, J.; Caillat, R.

    1958-01-01

    This work has been carried out in view of determining several physical properties of hot-pressed beryllium oxide under various conditions and the change of these properties after irradiation. Special attention has been paid on to the measurement of the thermal conductivity coefficient and thermal diffusivity coefficient. Several designs for the measurement of the thermal conductivity coefficient have been achieved. They permit its determination between 50 and 300 deg. C, between 400 and 800 deg. C. Some measurements have been made above 1000 deg. C. In order to measure the thermal diffusivity coefficient, we heat a perfectly flat surface of a sample in such a way that the heat flux is modulated (amplitude and frequency being adjustable). The thermal diffusivity coefficient is deduced from the variations of temperature observed on several spots. Tensile strength; compressive strength; expansion coefficient; sound velocity and crystal parameters have been also measured. Some of the measurements have been carried out after neutron irradiation. Some data have been obtained on the change of the properties of beryllium oxide depending on the integrated neutron flux. (author) [fr

  19. Irradiation effects on aluminium and beryllium

    International Nuclear Information System (INIS)

    Bieth, M.

    1992-01-01

    ductility of 1.6%. Besides, due to the effects of embrittlement and swelling induced by irradiation, the HFR beryllium reflector elements had to be replaced after more than 25 years of operation. Operational and practical experiences with these reflector elements are commented, as well as main engineering features of the new reflector elements: upper-end fittings of both filler element and insert in stainless steel, no radially drilled holes and no roll pins

  20. European Fusion Programme. ITER task T23: Beryllium characterisation. Progress report. Tensile tests on neutron irradiated and reference beryllium

    International Nuclear Information System (INIS)

    Moons, F.

    1996-02-01

    As part of the European Technology Fusion Programme, the irradiation embrittlement characteristics of the more ductile and isotopic grades of beryllium manufactured by Brush Wellman has been investigated using modern powder production and consolidation techniques . This study was initiated in support of the development and evaluation of beryllium as a neutron multiplier for the solid breeder blanket design concepts proposed for a DEMO fusion power reactor. Four different species of beryllium: S-200 F (vacuum hot pressed, 1.2 wt% BeO), S-200FH (hot isostatic pressed, 0.9 wt% BeO), S-65 (vacuum hot pressed, 0.6 wt% BeO), S-65H (hot isostatic pressed, 0.5 wt% BeO) have been compared. Three batches of the beryllium have been investigated, a neutron batch, a thermal control batch and a reference batch. Neutron irradiation has been performed at temperatures between 175 and 605 degrees Celsius up to a neutron fluence of 2.1 10 25 n.m -2 (E> 1 MeV) or 750 appm He. The results of the tensile tests are summarized

  1. Proton irradiation effects on beryllium – A macroscopic assessment

    Energy Technology Data Exchange (ETDEWEB)

    Simos, Nikolaos, E-mail: simos@bnl.gov [Nuclear Sciences & Technology Department, Brookhaven National Laboratory, Upton, NY, 11973 (United States); Elbakhshwan, Mohamed [Nuclear Sciences & Technology Department, Brookhaven National Laboratory, Upton, NY, 11973 (United States); Zhong, Zhong [Photon Sciences, NSLS II, Brookhaven National Laboratory, Upton, NY, 11973 (United States); Camino, Fernando [Center for Functional Nanomaterials, Brookhaven National Laboratory, Upton, NY, 11973 (United States)

    2016-10-15

    Beryllium, due to its excellent neutron multiplication and moderation properties, in conjunction with its good thermal properties, is under consideration for use as plasma facing material in fusion reactors and as a very effective neutron reflector in fission reactors. While it is characterized by unique combination of structural, chemical, atomic number, and neutron absorption cross section it suffers, however, from irradiation generated transmutation gases such as helium and tritium which exhibit low solubility leading to supersaturation of the Be matrix and tend to precipitate into bubbles that coalesce and induce swelling and embrittlement thus degrading the metal and limiting its lifetime. Utilization of beryllium as a pion production low-Z target in high power proton accelerators has been sought both for its low Z and good thermal properties in an effort to mitigate thermos-mechanical shock that is expected to be induced under the multi-MW power demand. To assess irradiation-induced changes in the thermal and mechanical properties of Beryllium, a study focusing on proton irradiation damage effects has been undertaken using 200 MeV protons from the Brookhaven National Laboratory Linac and followed by a multi-faceted post-irradiation analysis that included the thermal and volumetric stability of irradiated beryllium, the stress-strain behavior and its ductility loss as a function of proton fluence and the effects of proton irradiation on the microstructure using synchrotron X-ray diffraction. The mimicking of high temperature irradiation of Beryllium via high temperature annealing schemes has been conducted as part of the post-irradiation study. This paper focuses on the thermal stability and mechanical property changes of the proton irradiated beryllium and presents results of the macroscopic property changes of Beryllium deduced from thermal and mechanical tests.

  2. Impurities effect on the swelling of neutron irradiated beryllium

    International Nuclear Information System (INIS)

    Donne, M.D.; Scaffidi-Argentina, F.

    1995-01-01

    An important factor controlling the swelling behaviour of fast neutron irradiated beryllium is the impurity content which can strongly affect both the surface tension and the creep strength of this material. Being the volume swelling of the old beryllium (early sixties) systematically higher than that of the more modem one (end of the seventies), a sensitivity analysis with the aid of the computer code ANFIBE (ANalysis of Fusion Irradiated BEryllium) to investigate the effect of these material properties on the swelling behaviour of neutron irradiated beryllium has been performed. Two sets of experimental data have been selected: the first one named Western refers to quite recently produced Western beryllium, whilst the second one, named Russian refers to relatively old (early sixties) Russian beryllium containing a higher impurity rate than the Western one. The results obtained with the ANFIBE Code were assessed by comparison with experimental data and the used material properties were compared with the data available in the literature. Good agreement between calculated and measured values has been found

  3. Ab Initio Simulation Beryllium in Solid Molecular Hydrogen: Elastic Constant

    Science.gov (United States)

    Guerrero, Carlo L.; Perlado, Jose M.

    2016-03-01

    In systems of inertial confinement fusion targets Deuterium-Tritium are manufactured with a solid layer, it must have specific properties to increase the efficiency of ignition. Currently there have been some proposals to model the phases of hydrogen isotopes and hence their high pressure, but these works do not allow explaining some of the structures present at the solid phase change effect of increased pressure. By means of simulation with first principles methods and Quantum Molecular Dynamics, we compare the structural difference of solid molecular hydrogen pure and solid molecular hydrogen with beryllium, watching beryllium inclusion in solid hydrogen matrix, we obtain several differences in mechanical properties, in particular elastic constants. For C11 the difference between hydrogen and hydrogen with beryllium is 37.56%. This may produce a non-uniform initial compression and decreased efficiency of ignition.

  4. High dose neutron irradiation damage in beryllium as blanket material

    Energy Technology Data Exchange (ETDEWEB)

    Chakin, V.P. E-mail: fae@niiar.ru; Kazakov, V.A.; Teykovtsev, A.A.; Pimenov, V.V.; Shimansky, G.A.; Ostrovsky, Z.E.; Suslov, D.N.; Latypov, R.N.; Belozerov, S.V.; Kupriyanov, I.B. E-mail: vniinm.400@g23.relkom.ru

    2001-11-01

    The paper presents the investigation results of beryllium products that operated in the SM and BOR-60 reactors up to neutron doses of 2.8x10{sup 22} and 8.0x10{sup 22} cm{sup -2} (E>1 MeV), respectively. The calculated and experimental data are given on helium and tritium accumulation, swelling, micro-hardness and thermal conductivity. The microstructural investigation results of irradiated beryllium are also presented. It is shown that the rate of helium and tritium accumulation in beryllium in the SM and BOR-60 reactors is high enough, which is of interest from the viewpoint of modeling the working conditions of the DEMO fusion reactor. Swelling of beryllium at irradiation temperature of 70-150 deg. C and neutron fluence of 2.8x10{sup 22} cm{sup -2} (E>1 MeV) makes up 0.8-1.5%, at 400 deg. C and fluence of 8x10{sup 22} cm{sup -2} (E>1 MeV)-3.2-5.0%. Irradiation hardening and decrease of thermal conductivity strongly depend on the irradiation temperature and are more significant at reduced temperatures. All results presented in the paper were analyzed with due account of the supposed working parameters of the DEMO fusion reactor blanket.

  5. High dose neutron irradiation damage in beryllium as blanket material

    International Nuclear Information System (INIS)

    Chakin, V.P.; Kazakov, V.A.; Teykovtsev, A.A.; Pimenov, V.V.; Shimansky, G.A.; Ostrovsky, Z.E.; Suslov, D.N.; Latypov, R.N.; Belozerov, S.V.; Kupriyanov, I.B.

    2001-01-01

    The paper presents the investigation results of beryllium products that operated in the SM and BOR-60 reactors up to neutron doses of 2.8x10 22 and 8.0x10 22 cm -2 (E>1 MeV), respectively. The calculated and experimental data are given on helium and tritium accumulation, swelling, micro-hardness and thermal conductivity. The microstructural investigation results of irradiated beryllium are also presented. It is shown that the rate of helium and tritium accumulation in beryllium in the SM and BOR-60 reactors is high enough, which is of interest from the viewpoint of modeling the working conditions of the DEMO fusion reactor. Swelling of beryllium at irradiation temperature of 70-150 deg. C and neutron fluence of 2.8x10 22 cm -2 (E>1 MeV) makes up 0.8-1.5%, at 400 deg. C and fluence of 8x10 22 cm -2 (E>1 MeV)-3.2-5.0%. Irradiation hardening and decrease of thermal conductivity strongly depend on the irradiation temperature and are more significant at reduced temperatures. All results presented in the paper were analyzed with due account of the supposed working parameters of the DEMO fusion reactor blanket

  6. Tensile and fracture toughness test results of neutron irradiated beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Chaouadi, R.; Moons, F.; Puzzolante, J.L. [Centre d`Etude de l`Energie Nucleaire, Mol (Belgium)

    1998-01-01

    Tensile and fracture toughness test results of four Beryllium grades are reported here. The flow and fracture properties are investigated by using small size tensile and round compact tension specimens. Irradiation was performed at the BR2 material testing reactor which allows various temperature and irradiation conditions. The fast neutron fluence (>1 MeV) ranges between 0.65 and 2.45 10{sup 21} n/cm{sup 2}. In the meantime, un-irradiated specimens were aged at the irradiation temperatures to separate if any the effect of temperature from irradiation damage. Test results are analyzed and discussed, in particular in terms of the effects of material grade, test temperature, thermal ageing and neutron irradiation. (author)

  7. Beryllium

    Science.gov (United States)

    Foley, Nora K.; Jaskula, Brian W.; Piatak, Nadine M.; Schulte, Ruth F.; Schulz, Klaus J.; DeYoung,, John H.; Seal, Robert R.; Bradley, Dwight C.

    2017-12-19

    Beryllium is a mineral commodity that is used in a variety of industries to make products that are essential for the smooth functioning of a modern society. Two minerals, bertrandite (which is supplied domestically) and beryl (which is currently supplied solely by imports), are necessary to ensure a stable supply of high-purity beryllium metal, alloys, and metal-matrix composites and beryllium oxide ceramics. Although bertrandite is the source mineral for more than 90 percent of the beryllium produced globally, industrial beryl is critical for the production of the very high purity beryllium metal needed for some strategic applications. The current sole domestic source of beryllium is bertrandite ore from the Spor Mountain deposit in Utah; beryl is imported mainly from Brazil, China, Madagascar, Mozambique, and Portugal. High-purity beryllium metal is classified as a strategic and critical material by the Strategic Materials Protection Board of the U.S. Department of Defense because it is used in products that are vital to national security. Beryllium is maintained in the U.S. stockpile of strategic materials in the form of hot-pressed beryllium metal powder.Because of its unique chemical properties, beryllium is indispensable for many important industrial products used in the aerospace, computer, defense, medical, nuclear, and telecommunications industries. For example, high-performance alloys of beryllium are used in many specialized, high-technology electronics applications, as they are energy efficient and can be used to fabricate miniaturized components. Beryllium-copper alloys are used as contacts and connectors, switches, relays, and shielding for everything from cell phones to thermostats, and beryllium-nickel alloys excel in producing wear-resistant and shape-retaining high-temperature springs. Beryllium metal composites, which combine the fabrication ability of aluminum with the thermal conductivity and highly elastic modulus of beryllium, are ideal for

  8. Beryllium

    International Nuclear Information System (INIS)

    1988-01-01

    In this data sheet the occurrence, ore processing, chemical and physical properties and the uses of beryllium and its alloys is presented. The hazards involved in the use of beryllium and its compounds in the laboratory are discussed with particular reference to its toxicity, carcinogenicity, handling, storage, disposal, fire prevention and the principal health hazards. Further reading is suggested. (UK)

  9. Microstructure and mechanical properties of neutron irradiated beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Ishitsuka, E.; Kawamura, H. [Japan Atomic Energy Research Inst., Oarai, Ibaraki (Japan). Oarai Research Establishment; Terai, T.; Tanaka, S.

    1998-01-01

    Microstructure and mechanical properties of the neutron irradiated beryllium with total fast neutron fluences of 1.3 - 4.3 x 10{sup 21} n/cm{sup 2} (E>1 MeV) at 327 - 616degC were studied. Swelling increased by high irradiation temperature, high fluence, and by the small grain size and high impurity. Obvious decreasing of the fracture stress was observed in the bending test and in small grain specimens which had many helium bubbles on the grain boundary. Decreasing of the fracture stress for small grain specimens was presumably caused by crack propagation on the grain boundaries which weekend by helium bubbles. (author)

  10. Beryllium

    International Nuclear Information System (INIS)

    Hansen, N.B.

    1980-01-01

    A method for determination of beryllium in minerals and rocks is described. The method comprises microanalysis and trace analysis. Because of the toxidity of beryllium the method is designed for determination of a hitherto unknown small amount, 1-10 nanogram Be. With the optimal amount for determination, 3 ng Be, the relative error of the method is 10%. The description includes an inventory of chemicals and apparatus, also an example of application of the method on the mineral epididymite. In brief, the sample is melted with sodium carbonate and sodium tetra borate; when required the sample in advance is fumed with hydrogen fluoride and sulphuric acid to evaporate silica. The residuum is dissolved in water and hydrogen chloride, upon which the solution is made to volume. In the Ring oven interfering compounds are masked with EDTA. Beryllium is settled with chrome azurol and ammonia. Beryllium is identified and evaluated in comparison with previously produced standards. (author)

  11. Beryllium

    International Nuclear Information System (INIS)

    Hansen, N.B.

    1979-01-01

    A method for determination of beryllium in minerals and rocks is described. The method comprises microanalysis and trace analysis. Because of the toxidity of beryllium the method is designed for determination of a hitherto unknown small amount, 1-10 nanogram Be. With the optimal amount for determination, 3 ng Be, the relative error of the method is 10%. The description includes an inventory of chemicals and apparatus, also an example of application of the method on the mineral epididymite. In brief, the sample is melted with sodium carbonate and sodium tetra borate; when required the sample in advance is fumed with hydrogen fluoride and sulphuric acid to evaporate silica. The residuum is dissolved in water and hydrogen chloride, upon which the solution is made to volume. In the Ring oven interfering compounds are masked with EDTA. Beryllium is settled with chrome azurol and ammonia. Beryllium is identified and evaluated in comparison with previously produced standards. (author)

  12. Mechanical compression tests of beryllium pebbles after neutron irradiation up to 3000 appm helium production

    Energy Technology Data Exchange (ETDEWEB)

    Chakin, V., E-mail: vladimir.chakin@kit.edu [Karlsruhe Institute of Technology, Institite for Applied Materials, Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Rolli, R.; Moeslang, A. [Karlsruhe Institute of Technology, Institite for Applied Materials, Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Zmitko, M. [The European Joint Undertaking for ITER and the Development of Fusion Energy, c/Josep Pla, no. 2, Torres Diagonal Litoral, Edificio B3, 08019 Barcelona (Spain)

    2015-04-15

    Highlights: • Compression tests of highly neutron irradiated beryllium pebbles have been performed. • Irradiation hardening of beryllium pebbles decreases the steady-state strain-rates. • The steady-state strain-rates of irradiated beryllium pebbles exceed their swelling rates. - Abstract: Results: of mechanical compression tests of irradiated and non-irradiated beryllium pebbles with diameters of 1 and 2 mm are presented. The neutron irradiation was performed in the HFR in Petten, The Netherlands at 686–968 K up to 1890–2950 appm helium production. The irradiation at 686 and 753 K cause irradiation hardening due to the gas bubble formation in beryllium. The irradiation-induced hardening leads to decrease of steady-state strain-rates of irradiated beryllium pebbles compared to non-irradiated ones. In contrary, after irradiation at higher temperatures of 861 and 968 K, the steady-state strain-rates of the pebbles increase because annealing of irradiation defects and softening of the material take place. It was shown that the steady-state strain-rates of irradiated beryllium pebbles always exceed their swelling rates.

  13. Influence of neutron irradiation on the tritium retention in beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Rolli, R.; Ruebel, S.; Werle, H. [Forschungszentrum Karlsruhe, Inst. fuer Neutronenphysik und Reaktortechnik, Karlsruhe (Germany); Wu, C.H.

    1998-01-01

    Carbon-based materials and beryllium are the candidates for protective layers on the components of fusion reactors facing plasma. In contact with D-T plasma, these materials absorb tritium, and it is anticipated that tritium retention increases with the neutron damage due to neutron-induced traps. Because of the poor data base for beryllium, the work was concentrated on it. Tritium was loaded into the samples from stagnant T{sub 2}/H{sub 2} atmosphere, and afterwards, the quantity of the loaded tritium was determined by purged thermal annealing. The specification of the samples is shown. The samples were analyzed by SEM before and after irradiation. The loading and the annealing equipments are contained in two different glove boxes with N{sub 2} inert atmosphere. The methods of loading and annealing are explained. The separation of neutron-produced and loaded tritium and the determination of loaded tritium in irradiated samples are reported. Also the determination of loaded tritium in unirradiated samples is reported. It is evident that irradiated samples contained much more loaded tritium than unirradiated samples. The main results of this investigation are summarized in the table. (K.I.)

  14. The effect of helium generation and irradiation temperature on tritium release from neutron irradiated beryllium

    International Nuclear Information System (INIS)

    Kupriyanov, I.B.; Gorokhov, V.A.; Vlasov, V.V.; Kovalev, A.M.; Chakin, V.P.

    2004-01-01

    The effect of neutron irradiation condition on tritium release from beryllium is described in this paper. Beryllium samples were irradiated in the SM reactor with neutron fluence (E > 0.1 MeV) of (0.37-2.0) x 10 22 cm -2 at 70-100degC and 650-700degC. Mass-spectrometer technique was used in out of tritium release experiments during stepped-temperature anneal within a temperature range from 250 to 1300degC. The total amount of helium accumulated in irradiated beryllium samples varied from 521 appm to 3061 appm. The first signs of tritium release were detected at temperature of 406-553degC. It was shown that irradiation temperature and helium generation level significantly affect the tritium release. A fraction of 44 - 74 % of tritium content in samples irradiated at low temperature (70 - 100degC) is release from beryllium at an annealing temperature below 800degC, whereas for samples after high temperature irradiation (650 - 700 degC) tritium release did not exceed 14 %. Majority of tritium (∼68%) is released within a temperature range from 800 to 920 degC. The increase of helium generation from 521 appm to 3061 appm results in lowering the temperature of maximal tritium release rate and the upper temperature of tritium release from beryllium by 100-130degC and 200-240degC, correspondingly. On the basis of data obtained, the diffusion coefficients of tritium in beryllium were calculated. (author)

  15. Tritium and helium behavior in irradiated beryllium

    International Nuclear Information System (INIS)

    Billone, M.C.; Lin, C.C.; Baldwin, D.L.

    1990-11-01

    Large quantities of Be (> 100 metric tons) are planned for use in the ITER blanket design to enhance tritium breeding and to act as a thermal barrier between coolant and breeder. Tritium retention/release and He-induced swelling are important issues in blanket design. The data base on tritium and helium behavior in Be is reviewed. New data on tritium retention/release and He bubble growth are presented for Be irradiated to 5 x 10 22 n(E > 1 MeV)/cm 2 at ∼75 degree C and postirradiation-annealed for 700 hours at 500 degree C. A model (diffusion/desorption) is proposed and tested against the data base to determine tritium diffusivity and the desorption rate constant. Similarly a model for He-induced swelling is developed and tested against the data base. The dependence of tritium retention and release on He content and impurities (e.g. BeO) is also explored. 11 refs., 6 figs

  16. Post irradiation characterization of beryllium and beryllides after high temperature irradiation up to 3000 appm helium production in HIDOBE-01

    Energy Technology Data Exchange (ETDEWEB)

    Fedorov, A.V., E-mail: fedorov@nrg.eu [Nuclear Research and Consultancy Group, Westerduinweg 3, Postbus 25, Petten, 1755 ZG (Netherlands); Til, S. van; Stijkel, M.P. [Nuclear Research and Consultancy Group, Westerduinweg 3, Postbus 25, Petten, 1755 ZG (Netherlands); Nakamichi, M. [Japan Atomic Energy Agency, Rokkasho (Japan); Zmitko, M. [The European Joint Undertaking for ITER and the Development of Fusion Energy, c/ Josep Pla, n° 2, Torres Diagonal Litoral, Edificio B3, Barcelona 08019 (Spain)

    2016-01-15

    Titanium beryllides are considered as advanced candidate material for neutron multiplier for the helium cooled pebble bed (HCPB) and/or the water cooled ceramic breeder (WCCB) breeder blankets. In the HIDOBE-01 (HIgh DOse irradiation of BEryllium) experiment, beryllium and beryllide pellets with 5 at% and 7 at% Ti are irradiated at four different target temperatures (T{sub irr}): 425 °C, 525 °C, 650 °C and 750 °C up to the dose corresponding to 3000 appm He production in beryllium. The pellets were supplied by JAEA. During post irradiation examinations the critical properties of volumetric swelling and tritium retention were studied. Both titanium beryllide grades show significantly less swelling than the beryllium grade, with the difference increasing with the irradiation temperature. The irradiation induced swelling was studied by using direct dimensions. Both beryllide grades showed much less swelling as compare to the reference beryllium grade. Densities of the grades were studied by Archimedean immersion and by He-pycnometry, giving indications of porosity formation. While both beryllide grades show no significant reduction in density at all irradiation temperatures, the beryllium density falls steeply at higher T{sub irr}. Finally, the tritium release and retention were studied by temperature programmed desorption (TPD). Beryllium shows the same strong tritium retention as earlier observed in studies on beryllium pebbles, while the tritium inventory of the beryllides is significantly less, already at the lowest T{sub irr} of 425 °C.

  17. Thermal conductivity of beryllium under low temperature high dose neutron irradiation

    International Nuclear Information System (INIS)

    Chakin, V.P.; Latypov, R.N.; Suslov, D.N.; Kupriyanov, I.B.

    2004-01-01

    Thermal conductivity of compact beryllium of several Russian grades such as TE-400, TE-56, TE-30, TIP and DIP differing in the production technology, grain size and impurity content has been investigated. The thermal diffusivity of beryllium was measured on the disks in the initial and irradiated conditions using the pulse method in the range from room temperature to 200degC. The thermal conductivity was calculated using the table values for the beryllium thermal capacity. The specimens and beryllium neutron source fragments were irradiation in the SM reactor at 70degC and 200degC to a neutron fluence of (0.5-11.4)·10 22 cm -2 (E>0.1 MeV) and in the BOR-60 reactor at 400degC to 16·10 22 cm -2 (E>0.1MeV), respectively. The low-temperature irradiation leads to the drop decrease of the beryllium thermal conductivity and the effect depends on the irradiation parameters. The paper analyses the effect of irradiation parameters (temperature, neutron fluence), measurement temperature and structural factors on beryllium conductivity. The experiments have revealed that the short time post-irradiation annealing at high temperature results in partial reduction of the thermal conductivity of irradiated beryllium. (author)

  18. HEINBE; the calculation program for helium production in beryllium under neutron irradiation

    International Nuclear Information System (INIS)

    Shimakawa, Satoshi; Ishitsuka, Etsuo; Sato, Minoru

    1992-11-01

    HEINBE is a program on personal computer for calculating helium production in beryllium under neutron irradiation. The program can also calculate the tritium production in beryllium. Considering many nuclear reactions and their multi-step reactions, helium and tritium productions in beryllium materials irradiated at fusion reactor or fission reactor may be calculated with high accuracy. The calculation method, user's manual, calculated examples and comparison with experimental data were described. This report also describes a neutronics simulation method to generate additional data on swelling of beryllium, 3,000-15,000 appm helium range, for end-of-life of the proposed design for fusion blanket of the ITER. The calculation results indicate that helium production for beryllium sample doped lithium by 50 days irradiation in the fission reactor, such as the JMTR, could be achieved to 2,000-8,000 appm. (author)

  19. Electron microscope study of irradiated beryllium oxide; Etude au microscope electronique de l'oxyde de beryllium irradie

    Energy Technology Data Exchange (ETDEWEB)

    Bisson, A A [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

    1965-06-01

    The beryllium oxide is studied first by fractography, before and after irradiation, using sintered samples. The fractures are examined under different aspects. The higher density sintered samples, with transgranular fractures are the most interesting for a microscopic study. It is possible to mark the difference between the 'pores' left by the sintering process and the 'bubbles' of gases that can be produced by former thermal treatments. After irradiation, the grain boundaries are very much weakened. By annealing, it is possible to observe the evolution of the gases produced by the reaction (n, 2n) and (n. {alpha}) and gathered on the grain boundaries. The irradiated beryllium oxide is afterwards studied by transmission. For that, a simple method has been used: little chips of the crushed material are examined. Clusters of point defects produced by neutrons are thus detected in crystals irradiated at the three following doses: 6 x 10{sup 19}, 9 x 10{sup 19} and 2 x 10{sup 20} n{sub f} cm{sup -2} at a temperature below 100 deg. C. For the irradiation at 6 x 10{sup 19} n{sub f} cm{sup -2}, the defects are merely visible, but at 2 x l0{sup 20} n{sub f} cm{sup -2} the crystals an crowded with clusters and the Kikuchi lines have disappeared from the micro-diffraction diagrams. The evolution of the clusters into dislocation loops is studied by a series of annealings. The activation energy (0,37 eV) calculated from the annealing curves suggests that it must be interstitials that condense into dislocation loops. Samples irradiated at high temperatures (650, 900 and 1100 deg. C) are also studied. In those specimens the size of the loops is not the same as the equilibrium size obtained after out of pile annealing at the same temperature. Those former loops are more specifically studied and their Burgers vector is determined by micro-diffraction. (author) [French] L'oxyde de beryllium est d'abord etudie, par une methode fractographique, avant et apres irradiation, en

  20. Beryllium irradiation embrittlement test programme. Material and specimen specification, manufacture and qualification

    International Nuclear Information System (INIS)

    Harries, D.R.; Dalle Donne, M.

    1996-06-01

    The report presents the specification, manufacture and qualification of the beryllium specimens to be irradiated in the BR2 reactor in Mol to investigate the effect of the neutron irradiation on the embrittlement as a function of temperature and beryllium oxide content. This work was been performed in the framework of the Nuclear Fusion Project of the Forschungszentrum Karlsruhe and is supported by the European Union within the European Fusion Technology Program. (orig.)

  1. Tritium and helium retention and release from irradiated beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Anderl, R.A.; Longhurst, G.R.; Oates, M.A.; Pawelko, R.J. [Idaho National Engineering and Environmental Lab., Idaho Falls, ID (United States)

    1998-01-01

    This paper reports the results of an experimental effort to anneal irradiated beryllium specimens and characterize them for steam-chemical reactivity experiments. Fully-dense, consolidated powder metallurgy Be cylinders, irradiated in the EBR-II to a fast neutron (>0.1 MeV) fluence of {approx}6 x 10{sup 22} n/cm{sup 2}, were annealed at temperatures from 450degC to 1200degC. The releases of tritium and helium were measured during the heat-up phase and during the high-temperature anneals. These experiments revealed that, at 600degC and below, there was insignificant gas release. Tritium release at 700degC exhibited a delayed increase in the release rate, while the specimen was at 700degC. For anneal temperatures of 800degC and higher, tritium and helium release was concurrent and the release behavior was characterized by gas-burst peaks. Essentially all of the tritium and helium was released at temperatures of 1000degC and higher, whereas about 1/10 of the tritium was released during the anneals at 700degC and 800degC. Measurements were made to determine the bulk density, porosity and specific surface area for each specimen before and after annealing. These measurements indicated that annealing caused the irradiated Be to swell, by as much as 14% at 700degC and 56% at 1200degC. Kr gas adsorption measurements for samples annealed at 1000degC and 1200degC determined specific surface areas between 0.04 m{sup 2}/g and 0.1 m{sup 2}/g for these annealed specimens. The tritium and helium gas release measurements and the specific surface area measurements indicated that annealing of irradiated Be caused a porosity network to evolve and become surface-connected to relieve internal gas pressure. (author)

  2. Tritium release and retention properties of highly neutron-irradiated beryllium pebbles from HIDOBE-01 experiment

    Energy Technology Data Exchange (ETDEWEB)

    Chakin, V., E-mail: vladimir.chakin@kit.edu [Karlsruhe Institute of Technology, Institute for Applied Materials, Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Rolli, R.; Moeslang, A.; Klimenkov, M.; Kolb, M.; Vladimirov, P.; Kurinskiy, P.; Schneider, H.-C. [Karlsruhe Institute of Technology, Institute for Applied Materials, Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Til, S. van; Magielsen, A.J. [Nuclear Research and Consultancy Group, Westerduinweg 3, Postbus 25, 1755 ZG Petten (Netherlands); Zmitko, M. [The European Joint Undertaking for ITER and the Development of Fusion Energy, c/Josep Pla, no. 2, Torres Diagonal Litoral, Edificio B3, 08019 Barcelona (Spain)

    2013-11-15

    The current helium cooled pebble bed (HCPB) tritium breeding blanket concept for fusion reactors includes a bed of 1 mm diameter beryllium pebbles to act as a neutron multiplier. Beryllium pebbles, fabricated by the rotating electrode method, were neutron irradiated in the HFR in Petten within the HIDOBE-01 experiment. This study presents tritium release and retention properties and data on microstructure evolution of beryllium pebbles irradiated at 630, 740, 873, 948 K up to a damage dose of 18 dpa, corresponding to a helium accumulation of about 3000 appm. The measured cumulative released activity from the beryllium pebbles irradiated at 948 K was found to be significantly lower than the calculated value. After irradiation at 873 and 948 K scanning electron microscopy (SEM) and transmission electron microscopy (TEM) analyses revealed large pores or bubbles in the bulk and oxide films with a thickness of up to 8 μm at the surface of the beryllium pebbles. The radiation-enhanced diffusion of tritium and the formation of open porosity networks accelerate the tritium release from the beryllium pebbles during the high-flux neutron irradiation.

  3. Nuclear irradiation parameters of beryllium under fusion, fission and IFMIF irradiation conditions

    International Nuclear Information System (INIS)

    Fischer, U.; Chen, Y.; Leichtle, D.; Simakov, S.; Moeslang, A.; Vladimirov, P.

    2004-01-01

    A computational analysis is presented of the nuclear irradiation parameters for Beryllium under irradiation in typical neutron environments of fission and fusion reactors, and of the presently designed intense fusion neutron source IFMIF. The analysis shows that dpa and Tritium production rates at fusion relevant levels can be achieved with existing high flux fission reactors while the achievable Helium production is too low. The resulting He-Tritium and He/dpa ratios do not meet typical fusion irradiation conditions. Irradiation simulations in the medium flux test modules of the IFMIF neutron source facility were shown to be more suitable to match fusion typical irradiation conditions. To achieve sufficiently high production rates it is suggested to remove the creep-fatigue testing machine together with the W spectra shifter plate and move the tritium release module upstream towards the high flux test module. (author)

  4. On use of beryllium in fusion reactors: Resources, impurities and necessity of detritiation after irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Kolbasov, B.N., E-mail: b.kolbasov@yandex.ru; Khripunov, V.I., E-mail: Khripunov_VI@nrcki.ru; Biryukov, A.Yu.

    2016-11-01

    Highlights: • Potential needs in Be for fusion power engineering may exceed Be resources. • Be recycling after its operation in a fusion power plant (FPP) seems inevitable. • U impurity in Be seriously impairs environmental properties of fusion power plants. • Upon burial of irradiated Be the main problems are caused by U and {sup 3}H impurities. • Clearance of Be extracted from a FPP is impossible due to U impurity. - Abstract: Worldwide identified resources of beryllium somewhat exceed 80 000 t. Beryllium production in all the countries of the world in 2012 was about 230 t. At the same time, some conceptual designs of fusion power reactors envisage utilization of several hundred tons of this metal. Therefore return of beryllium into the production cycle (recycling) will be necessary. The beryllium ore from some main deposits has uranium content inadmissible for fusion reactors. This fact raises a question on the need to develop and apply an economically acceptable technology for beryllium purification from the uranium. Practically any technological procedure with beryllium used in fusion reactors requires its detritiation. A study of tritium and helium release from irradiated beryllium at different temperatures and rates of temperature increase was performed at Kurchatov Institute.

  5. Irradiation effects in beryllium exposed to high energy protons of the NuMI neutrino source

    Energy Technology Data Exchange (ETDEWEB)

    Kuksenko, V., E-mail: viacheslav.kuksenko@materials.ox.ac.uk [University of Oxford, Oxford (United Kingdom); Ammigan, K.; Hartsell, B. [Fermi National Accelerator Laboratory, Batavia (United States); Densham, C. [Rutherford Appleton Laboratory, Didcot (United Kingdom); Hurh, P. [Fermi National Accelerator Laboratory, Batavia (United States); Roberts, S. [University of Oxford, Oxford (United Kingdom)

    2017-07-15

    A beryllium primary vacuum-to-air beam ‘window’ of the 'Neutrinos at the Main Injector' (NuMI) beamline at Fermi National Accelerator Laboratory (Fermilab), Batavia, Illinois, USA, has been irradiated by 120 GeV protons over 7 years, with a maximum integrated fluence at the window centre of 2.06 10{sup 22} p/cm{sup 2} corresponding to a radiation damage level of 0.48 dpa. The proton beam is pulsed at 0.5 Hz leading to an instantaneous temperature rise of 40 °C per pulse. The window is cooled by natural convection and is estimated to operate at an average of around 50 °C. The microstructure of this irradiated material was investigated by SEM/EBSD and Atom Probe Tomography, and compared to that of unirradiated regions of the beam window and that of stock material of the same PF-60 grade. Microstructural investigations revealed a highly inhomogeneous distribution of impurity elements in both unirradiated and irradiated conditions. Impurities were mainly localised in precipitates, and as segregations at grain boundary and dislocation lines. Low levels of Fe, Cu, Ni, C and O were also found to be homogeneously distributed in the beryllium matrix. In the irradiated materials, up to 440 appm of Li, derived from transmutation of beryllium was homogeneously distributed in solution in the beryllium matrix.

  6. Tritium release from beryllium pebbles after high temperature irradiation up to 3000 appm He in the HIDOBE-01 experiment

    Energy Technology Data Exchange (ETDEWEB)

    Til, S. van, E-mail: vantil@nrg.eu [Nuclear Research and Consultancy Group, Westerduinweg 3, Postbus 25, 1755 ZG Petten (Netherlands); Fedorov, A.V.; Stijkel, M.P.; Cobussen, H.L.; Mutnuru, R.K.; Idsert, P. van der [Nuclear Research and Consultancy Group, Westerduinweg 3, Postbus 25, 1755 ZG Petten (Netherlands); Zmitko, M. [The European Joint Undertaking for ITER and The Development of Fusion Energy, c/ Josep Pla, no. 2, Torres Diagonal Litoral, Edificio B3, 08019 Barcelona (Spain)

    2013-11-15

    In the HIDOBE (HIgh DOse irradiation of BEryllium) irradiation program, various grades of constrained and unconstrained beryllium pebbles, beryllium pellets and titanium-beryllide samples are irradiated in the High Flux Reactor (HFR) in Petten at four different temperatures (between 698 K and 1023 K) for 649 days [1]. The first of two HIDOBE irradiation experiments, HIDOBE-01, was completed after achieving a DEMO relevant helium production level of 3000 appm and the samples are retrieved for postirradiation examination (PIE). This work shows preliminary results of the out-of-pile tritium release analysis performed on different grades of irradiated beryllium pebbles (different in size). Relationships between irradiation temperature, tritium inventory and microstructural evolution have been observed by light microscopy and scanning electron microscopy.

  7. Analysis of Beryllium Having Irradiated at the RSG-GAS Core using ORIGEN2 Code

    International Nuclear Information System (INIS)

    Jaja Sukmana; Jonnie AK; S-Suwarto; Irwan

    2012-01-01

    Analysis of activation products generated by irradiated beryllium at the RSG-GAS core has been done using ORIGEN2 code. By assuming that irradiation is 176 days, neutron flux average of 2.30e+14 n/cm 2 s, radioisotopes rose from activated Be are tritium, lithium, beryllium, carbon, magnesium, aluminum, silicon, argon, calcium, scandium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, silver, and lead. The highest activity after 100 days of irradiation demonstrated by Be-10 (7.99 E-03 Curie), H-3 (2.97 E-03 Curie), Cr-51, Fe-55 and Co-60. Radioactivity generated getting smaller when irradiation time are long. From this analysis it can be conclude that radioactivity was caused by impurities present in Be such as Mn-54, Fe-59, Zn-65, and Li-6. (author)

  8. Desorption of tritium and helium from high dose neutron irradiated beryllium

    Science.gov (United States)

    Kupriyanov, I. B.; Nikolaev, G. N.; Vlasov, V. V.; Kovalev, A. M.; Chakin, V. P.

    2007-08-01

    The effect of high dose neutron irradiation on tritium and helium desorption in beryllium is described. Beryllium samples were irradiated in the SM and BOR-60 reactors to a neutron fluences ( E > 0.1 MeV) of (5-16) × 10 22 cm -2 at 70-100 °C and 380-420 °C. A mass-spectrometry technique was used in out of pile tritium release experiments during stepped annealing in the 250-1300 °C temperature range. The total amount of helium accumulated in irradiated beryllium samples varied from 6000 to 7200 appm. The first signs of tritium and helium release were detected at temperature of 312-445 °C and 500-740 °C, respectively. It is shown that most tritium (˜82%) from sample irradiated at 70-100 °C releases in temperature range of 312-700 °C before the beginning of helium release (740 °C). In the case of beryllium sample irradiated at 380-420 °C, tritium release starts at a higher temperature ( Ts > Tann = 445 °C) and most of the tritium (˜99.8%) is released concurrently with helium which could be considered as evidence of co-existence of partial amounts of tritium and helium in common bubbles. Both the Be samples differ little in the upper temperatures of gas release: 745 and 775 °C for tritium; 1140 and 1160 °C for helium. Swelling of beryllium starts to play a key role in accelerating tritium release at Tann > 600 °C and in helium release - at Tann > 750 °C.

  9. Physical properties of beryllium oxide - Irradiation effects; Proprietes physiques et caracteristiques mecaniques de l'oxyde de beryllium fritte - Effet de l'irradiation et guerison

    Energy Technology Data Exchange (ETDEWEB)

    Elston, J; Caillat, R [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

    1958-07-01

    This work has been carried out in view of determining several physical properties of hot-pressed beryllium oxide under various conditions and the change of these properties after irradiation. Special attention has been paid on to the measurement of the thermal conductivity coefficient and thermal diffusivity coefficient. Several designs for the measurement of the thermal conductivity coefficient have been achieved. They permit its determination between 50 and 300 deg. C, between 400 and 800 deg. C. Some measurements have been made above 1000 deg. C. In order to measure the thermal diffusivity coefficient, we heat a perfectly flat surface of a sample in such a way that the heat flux is modulated (amplitude and frequency being adjustable). The thermal diffusivity coefficient is deduced from the variations of temperature observed on several spots. Tensile strength; compressive strength; expansion coefficient; sound velocity and crystal parameters have been also measured. Some of the measurements have been carried out after neutron irradiation. Some data have been obtained on the change of the properties of beryllium oxide depending on the integrated neutron flux. (author)Fren. [French] L'objet de cette etude est la determination de plusieurs proprietes physiques de l'oxyde de beryllium fritte sous charge dans differentes conditions et l'evolution de ces proprietes apres irradiation. Une attention particuliere a ete portee sur la mesure de la conductibilite et de la diffusivite thermiques. Differents montages ont ete realises pour mesurer la conductibilite thermique. Ils permettent la determination entre 50 et 300 deg. C, entre 400 et 800 deg. C; quelques mesures ont ete faites au-dessus de 1000 deg. C. Pour la mesure du coefficient de diffusivite thermique, on realise une attaque thermique, de frequence et d'amplitude reglables d'une face parfaitement plane d'un echantillon d'oxyde de beryllium. Les variations de temperature sont ovees en plusieurs points, on en

  10. Semi-solid metal forming of beryllium-reinforced aluminum alloys

    International Nuclear Information System (INIS)

    Haws, W.; Lane, L.; Marder, J.; Nicholas, N.

    1995-01-01

    A Powder Metallurgy (PM) based, Semi-Solid Metal (SSM) forming process has been developed to produce low cost near-net shapes of beryllium-reinforced aluminum alloys. Beryllium acts as a reinforcing additive to the aluminum, in which there is nearly no mutual solid solubility. The modulus of elasticity of the alloy dramatically increases, while the density and thermal expansion coefficient decrease with increasing beryllium content. The material is suitable for complex thermal management and vibration resistance applications, as well as for airborne components which are density and stiffness sensitive. The forming process involves heating a blank of the material to a temperature at which the aluminum is semi-solid and the beryllium is solid. The semi-solid blank is then injected without turbulence into a permanent mold. High quality, near net shape components can be produced which are functionally superior to those produced by other permanent mold processes. Dimensional accuracy is equivalent to or better than that obtained in high pressure die casting. Cost effectiveness is the primary advantage of this technique compared to other forming processes. The advantages and limitations of the process are described. Physical and mechanical property data are presented, as well as directions for future investigation

  11. Solid state bonding of beryllium to copper and vanadium

    International Nuclear Information System (INIS)

    Floyd, D.R.; Liby, A.L.; Weaver, W.

    1993-01-01

    The intent of this effort was to demonstrate that ingot metallurgy (IM) beryllium (Be) can be bonded to dissimilar metals such as copper (Cu) or vanadium (V) at low temperatures by using silver (Ag) as a bonding aid. It is hoped that success at the coupon stage will stimulate more extensive studies of the mechanical and thermal integrity of such joints, leading ultimately to use of this technology to fabricate first wall structures for ITER. (orig.)

  12. Beryllium and lithium resource requirements for solid blanket designs for fusion reactors

    International Nuclear Information System (INIS)

    Powell, J.R.

    1975-01-01

    The lithium and beryllium requirements are analyzed for an economy of 10 6 MW(e) CTR 3 capacity using solid blanket fusion reactors. The total lithium inventory in fusion reactors is only approximately 0.2 percent of projected U. S. resources. The lithium inventory in the fusion reactors is almost entirely 6 Li, which must be extracted from natural lithium. Approximately 5 percent of natural lithium can be extracted as 6 Li. Thus the total feed of natural lithium required is approximately 20 times that actually used in fusion reactors, or approximately 4 percent of U. S. resources. Almost all of this feed is returned to the U. S. resource base after 6 Li is extracted, however. The beryllium requirements are on the order of 10 percent of projected U. S. resources. Further, the present cost of lithium and the cost of beryllium extraction could both be increased tenfold with only minor effects on CTR capital cost. Such an increase should substantially multiply the economically recoverable resources of lithium and beryllium. It is concluded that there are no lithium or beryllium resource limitations preventing large-scale implementation of solid blanket fusion reactors. (U.S.)

  13. Study of the microstructure of neutron irradiated beryllium for the validation of the ANFIBE code

    International Nuclear Information System (INIS)

    Rabaglino, E.; Ferrero, C.; Reimann, J.; Ronchi, C.; Schulenberg, T.

    2002-01-01

    The behaviour of beryllium under fast neutron irradiation is a key issue of the helium cooled pebble bed tritium breeding blanket, due to the production of large quantities of helium and of a non-negligible amount of tritium. To optimise the design, a reliable prediction of swelling due to helium bubbles and of tritium inventory during normal and off-normal operation of a fusion power reactor is needed. The ANFIBE code (ANalysis of Fusion Irradiated BEryllium) is being developed to meet this need. The code has to be applied in a range of irradiation conditions where no experimental data are available, therefore a detailed gas kinetics model, and a specific and particularly careful validation strategy are needed. The validation procedure of the first version of the code was based on macroscopic data of swelling and tritium release. This approach is, however, incomplete, since a verification of the microscopic behaviour of the gas in the metal is necessary to obtain a reliable description of swelling. This paper discusses a general strategy for a thorough validation of the gas kinetics models in ANFIBE. The microstructure characterisation of weakly irradiated beryllium pebbles, with different visual examination techniques, is then presented as an example of the application of this strategy. In particular, the advantage of developing 3D techniques, such as X-ray microtomography, is demonstrated

  14. Studies on the irradiated solids

    International Nuclear Information System (INIS)

    Lesueur, D.

    1988-01-01

    The 1988 progress report of the Irradiated Solids laboratory (Polytechnic School, France), is presented. The Laboratory activities concern the investigations on disordered solids (chemical or structural disorder). The disorder itself, its effects on the material physical properties and the particle-matter interactions, are investigated. The research works are performed in the following fields: solid state physics, irradiation and stoechiometric defects, and nuclear materials. The scientific reviews, the congress communications and the thesis are listed [fr

  15. Irradiated Beryllium Disposal Workshop, Idaho Falls, ID, May 29-30, 2002

    Energy Technology Data Exchange (ETDEWEB)

    Longhurst, Glen Reed; Anderson, Gail; Mullen, Carlan K; West, William Howard

    2002-07-01

    In 2001, while performing routine radioactive decay heat rate calculations for beryllium reflector blocks for the Advanced Test Reactor (ATR), it became evident that there may be sufficient concentrations of transuranic isotopes to require classification of this irradiated beryllium as transuranic waste. Measurements on samples from ATR reflector blocks and further calculations confirmed that for reflector blocks and outer shim control cylinders now in the ATR canal, transuranic activities are about five times the threshold for classification. That situation implies that there is no apparent disposal pathway for this material. The problem is not unique to the ATR. The High Flux Isotope Reactor at Oak Ridge National Laboratory, the Missouri University Research Reactor at Columbia, Missouri and other reactors abroad must also deal with this issue. A workshop was held in Idaho Falls Idaho on May 29-30, 2002 to acquaint stakeholders with these findings and consider a path forward in resolving the issues attendant to disposition of irradiated material. Among the findings from this workshop were (1) there is a real potential for the US to be dependent on foreign sources for metallic beryllium within about a decade; (2) there is a need for a national policy on beryllium utilization and disposition and for a beryllium coordinating committee to be assembled to provide guidance on that policy; (3) it appears it will be difficult to dispose of this material at the Waste Isolation Pilot Plant (WIPP) near Carlsbad, New Mexico due to issues of Defense classification, facility radioactivity inventory limits, and transportation to WIPP; (4) there is a need for a funded DOE program to seek resolution of these issues including research on processing techniques that may make this waste acceptable in an existing disposal pathway or allow for its recycle.

  16. High-temperature annealing of proton irradiated beryllium – A dilatometry-based study

    Energy Technology Data Exchange (ETDEWEB)

    Simos, Nikolaos, E-mail: simos@bnl.gov [Brookhaven National Laboratory, Upton, NY, 11973 (United States); Elbakhshwan, Mohamed; Zhong, Zhong; Ghose, Sanjit [Brookhaven National Laboratory, Upton, NY, 11973 (United States); Savkliyildiz, Ilyas [Rutgers University (United States)

    2016-08-15

    S−200 F grade beryllium has been irradiated with 160 MeV protons up to 1.2 10{sup 20} cm{sup −2} peak fluence and irradiation temperatures in the range of 100–200 °C. To address the effect of proton irradiation on dimensional stability, an important parameter in its consideration in fusion reactor applications, and to simulate high temperature irradiation conditions, multi-stage annealing using high precision dilatometry to temperatures up to 740 °C were conducted in air. X-ray diffraction studies were also performed to compliment the macroscopic thermal study and offer a microscopic view of the irradiation effects on the crystal lattice. The primary objective was to qualify the competing dimensional change processes occurring at elevated temperatures namely manufacturing defect annealing, lattice parameter recovery, transmutation {sup 4}He and {sup 3}H diffusion and swelling and oxidation kinetics. Further, quantification of the effect of irradiation dose and annealing temperature and duration on dimensional changes is sought. The study revealed the presence of manufacturing porosity in the beryllium grade, the oxidation acceleration effect of irradiation including the discontinuous character of oxidation advancement, the effect of annealing duration on the recovery of lattice parameters recovery and the triggering temperature for transmutation gas diffusion leading to swelling.

  17. Assessment of irradiation effects on beryllium reflector and heavy water tank of JRR-3M

    Energy Technology Data Exchange (ETDEWEB)

    Murayama, Yoji; Kakehuda, Kazuhiro [Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan). Tokai Research Establishment

    1998-10-01

    The JRR-3M, a swimming pool type research reactor with beryllium and heavy water reflectors, has been operated since 1990. Since the beryllium reflectors are close to fuel and receive high fast neutron fluence in a relatively short time, they may be subject to change their dimensions by swelling due mostly to entrapped helium gaseous. This may bend the reflectors to the outside and narrow gaps between the reflectors and the fuel elements. The gaps have been measured with an ultrasonic thickness gage in an annual inspection. The results in 1996 show that the maximum of expansion in the diametral directions was 0.6 mm against 1.6 mm of a managed value for replacement of the reflector. A heavy water tank of the JRR-3M is made of aluminum alloy A5052. Surveillance tests of the alloy have been conducted to evaluate irradiation effects of the heavy water tank. Five sets of specimens of the alloy have been irradiated in the beryllium reflectors where fast neutron flux is higher than that in the heavy water tank. In 1994, one set of specimens had been unloaded and carried out the post-irradiation tests. The results show that the heavy water tank preserved satisfactory mechanical properties. (author)

  18. Composite beryllium-ceramics breeder pin elements for a gas cooled solid blanket

    International Nuclear Information System (INIS)

    Carre, F.; Chevreau, G.; Gervaise, F.; Proust, E.

    1986-06-01

    Helium coolant have main advantages compared to water for solid blankets. But limitations exist too and the development of attractive helium cooled blankets based on breeder pin assemblies has been essentially made possible by the derivation from recent CEA neutronic studies of an optimized composite beryllium/ceramics breeder arrangement. Description of the proposed toroidal blanket layout for Net is made together with the analysis of its main performance. Merits of the considered composite Be/ceramics breeder elements are discussed

  19. Design and fabrication of a dead weight equipment to perform creep measurements on highly irradiated beryllium specimens

    International Nuclear Information System (INIS)

    Scibetta, M.; Pellettieri, A.; Wouters, P.; Leenaerts, A.; Verpoucke, G.

    2005-01-01

    Beryllium is an important material to be used in the blanket of fusion reactors. It acts as a neutron multiplier that allows tritium production. In order to use this material effectively, some data on creep and swelling behaviour are needed. This paper describes preliminary microstructural investigations and the qualification of a creep set-up that will be used to measure creep of highly irradiated beryllium from the BR2 research reactor matrix. (Author)

  20. Gas bubble network formation in irradiated beryllium pebbles monitored by X-Ray micro-tomography

    Energy Technology Data Exchange (ETDEWEB)

    Bolier, E; Ferrero, C. [Forschungszentrum Karlsruhe, Zimer 203, Gebaeude 451, Abteilung HVT-TL (Germany); Moslang, A. [Forschungszentrum Karlsruhe GmbH, FZK, Karlsruhe (Germany); Pieritz, R.A. [CNRS, Lab. de Glaciologie et Geophysique de l' Environnement, 38 - Saint Martin d' Heres (France)

    2007-07-01

    Full text of publication follows: The efficient and safe operation of helium cooled ceramic breeder blankets requires among others an efficient tritium release during operation at blanket relevant temperatures. In the past out-of-pile thermal desorption studies on low temperature neutron irradiated beryllium have shown that tritium and helium release peaks occur together. This phenomenon can be interpreted in terms of growth and coalescence of helium bubbles and tritium that either is trapped inside the helium bubbles in form of T{sub 2} molecules or in their strain field. With increasing temperature the bubble density and size at grain interfaces increase together with the probability of interconnected porosities and channel formation to the outer surface, leading to simultaneous helium and tritium release peaks in TDS. For a reliable prediction of gas release up to end-of-life conditions at blanket relevant temperatures, knowledge of the dynamics of bubble growth and coalescence as well as the 3D distribution of bubble network formation is indispensable. Such data could also be used to experimentally validate any future model predictions of tritium and helium release rates. A high resolution computer aided micro-tomography (CMT) setup has been developed at the European Synchrotron Radiation Facility which allowed reconstructing 3-D images of beryllium pebbles without damaging them. By postprocessing the data a 3D rendering of inner surfaces and of interconnected channel networks can be obtained, thus allowing the identification of open porosities in neutron irradiated and tempered beryllium pebbles. In our case Beryllium pebbles of 2 mm diameter had been neutron irradiated in the 'Beryllium' experiment at 770 K with 1.24 x 10{sup 25} nxm{sup -2} resulting in 480 appm He and 12 appm Tritium. After annealing at 1500 K CMT was performed on the pebbles with 4.9 and 1.4 {mu}m voxel resolution, respectively, followed by morphological and topological post

  1. Recent progress in the modelling of helium and tritium behaviour in irradiated beryllium pebbles

    International Nuclear Information System (INIS)

    Rabaglino, E.; Ronchi, C.; Cardella, A.

    2003-01-01

    One of the key issues of the European Helium Cooled Pebble Bed blanket is the behaviour under irradiation of beryllium pebbles, which have the function of neutron multiplier. An intense production of helium occurs in-pile, as well as a non negligible generation of tritium. Helium bubbles induce swelling and a high tritium inventory is a safety issue. Extensive studies for a better understanding, characterisation and modelling of the behaviour of helium and tritium in irradiated beryllium pebbles are being carried out, with the final aim to enable a reliable prediction of gas release and swelling in the full range of operating and accidental conditions of a Fusion Power Reactor. The general strategy consists in integrating studies on macroscopic phenomena (gas release) with the characterisation of corresponding microscopic diffusion phenomena (bubble kinetics) and the assessment of some fundamental diffusion parameter for the models (gas atomic diffusion coefficients). The present work gives a summary of the latest achievements in this context. By an inverse analysis of experimental out-of-pile gas release from weakly irradiated pebbles, coupled to the study of the characteristics of bubble population, it has been possible to assess the thermal diffusion coefficients of helium and tritium in and to improve and validate the classical model of gas precipitation into bubbles inside the grain. The improvement of the description of gas atomic diffusion and precipitation is the first step to enable a more reliable prediction of gas release

  2. Features micro plastic deformation auxetic beryllium irradiated with high-energy electrons

    International Nuclear Information System (INIS)

    Rarans'kij, M.D.; Olyijnich-Lisyuk, A.V.; Tashchuk, O.Yu.

    2016-01-01

    By low-frequency internal friction (LFIF) (1...3 Hz) method, the study of the behavior of the dynamic modulus of torsion (Gef) and by mathematical modeling of dislocation motion studied micro plastic deformation in naturally aged and irradiated with high-energy (18 MeV) electrons auxetic beryllium. With increasing doses of radiation found an increase in IF and speed of movement of dislocations in 2-3 times. Installed stage character micro strain auxetic Be. By mathematical modeling showed that in the irradiated material the deformation occurs due to the accelerated movement of the twin dislocations in the early stages, and anomalous dynamic deceleration of complete dislocations with an increase in the degree of deformation in the second stage. It is shown that theoretically estimated values are in good agreement with the experimentally determined.

  3. Analysis of influence of fast neutron fluence irradiated to Beryllium element of The RSG-GAS reactor

    International Nuclear Information System (INIS)

    Sri Kuntjoro

    2010-01-01

    Analysis of influence fast neutron fluence irradiated to the RSG-GAS beryllium reflector have been done. Methods of analysis was carried out by measuring fluxes neutron in beryllium element and block position that function as reflector.The calculation done for determination it is there any influence of neutron as long as beryllium in the core. Besides that, visualization done to make sure it there is any deformation at beryllium as effect of irradiation. Fluxes and fluences of beryllium element measurement result in 200 kW reactor power are 2.30E+07 n/cm 2 .sec and 4.19E+17 n/cm 2 in position E-2, 3.70E+07 n/cm 2 s and 6.74E+17 n/cm 2 in position J-8, 2.19E+12 n/cm 2 s and 3.99E+22 n/cm 2 in position. Measurement results in the position B-3 are 2.12E+12 n/cm 2 s and 3.86E+22 n/cm 2 in position G-10 respectively. Other result are fluxes and fluence in beryllium block, those are 5,02E+07 n/cm 2 s and 9,15E+17 n/cm 2 in position (5-6), and 2,32E+07 n/cm 2 s and 4,23E+17 n/cm 2 in position (C-D). Deformation (L/L) results for beryllium element are 1,12E-08 in position E-2, 1,84E-08 in position J-8, 1,60E-03 in position B-3, and 1,55E-03 in position G-10. In beryllium block deformation results are 2,52E-08 in position (5-6) and 1,13E-08 in position (C-D). Those results are shown unseen deformation in beryllium element and beryllium block and demonstrably by visual observation in reactor hot cell. (author)

  4. Investigation of anisotropy in EPR spectra of radiation defects in irradiated beryllium ceramics

    International Nuclear Information System (INIS)

    Polyakov, A.I.; Ryabikin, Yu.A.; Zashkvara, O. V.; Bitenbaev, M.I.; Petukhov, Yu. V.

    2004-01-01

    Full text: In this work results of analysis of anisotropy and hyperfine structure in EPR spectra of paramagnetic defects in irradiated samples of beryllium ceramics are presented. To explain peculiarities in a shape and parameters of the EPR spectrum hyperfine structure in beryllium ceramics, we have analyzed several versions of model representations for the radiation-induced paramagnetic defects uniformly distributed in a sample as well as for cluster defects which hyperfine structure is determined by interactions between electrons and nuclei of impurity atoms (S=1/2) and which are characterized by anisotropy in the g factors. Calculations of a shape of the uniformly widened EPR spectra are carried out by the model of random interactions between electron spins. The EPR spectra, widened at the expense of anisotropy in the g factors, are calculated by the following equation: g(Δ)=[2(ω-ω 0 )+α] -1/2 , where ω 0 =γH 0 , α is the quantify proportional to the anisotropy shift. To describe wings of spectral lines, where the equation doesn't work, we use the Gaussian function. To determine the frequency of precession of electron spins packages with local concentration N loc , the following expression is used: ω=ω 0 +1/2α(3cos 2 θ-1), where θ is an angle between the symmetry axis and the direction of the external magnetic field. It is shown that the best agreement between the calculated and experimental EPR spectra is observed with the following computational model: paramagnetic radiation defects are distributed uniformly over a ceramics sample, and the g factors of its EPR spectra have the anisotropy typical for dipole-dipole interaction in powder samples. By results of the data we obtained, it's clear that in future we'll need in more detailed information than that published in scientific journals about formation of the paramagnetic defect EPR spectra structure in beryllium oxides and ceramics at the expense of resonance line hyperfine splitting on atoms of

  5. Investigation of anisotropy in EPR spectra of radiation defects in irradiated beryllium ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Polyakov, A I; Ryabikin, Yu A; Zashkvara, O V; Bitenbaev, M I; Petukhov, Yu V [Inst. of Physics and Technology, Almaty (Kazakhstan)

    2004-07-01

    Full text: In this work results of analysis of anisotropy and hyperfine structure in EPR spectra of paramagnetic defects in irradiated samples of beryllium ceramics are presented. To explain peculiarities in a shape and parameters of the EPR spectrum hyperfine structure in beryllium ceramics, we have analyzed several versions of model representations for the radiation-induced paramagnetic defects uniformly distributed in a sample as well as for cluster defects which hyperfine structure is determined by interactions between electrons and nuclei of impurity atoms (S=1/2) and which are characterized by anisotropy in the g factors. Calculations of a shape of the uniformly widened EPR spectra are carried out by the model of random interactions between electron spins. The EPR spectra, widened at the expense of anisotropy in the g factors, are calculated by the following equation: g({delta})=[2({omega}-{omega}{sub 0})+{alpha}]{sup -1/2}, where {omega}{sub 0}={gamma}H{sub 0}, {alpha} is the quantify proportional to the anisotropy shift. To describe wings of spectral lines, where the equation doesn't work, we use the Gaussian function. To determine the frequency of precession of electron spins packages with local concentration N{sub loc}, the following expression is used: {omega}={omega}{sub 0}+1/2{alpha}(3cos{sup 2}{theta}-1), where {theta} is an angle between the symmetry axis and the direction of the external magnetic field. It is shown that the best agreement between the calculated and experimental EPR spectra is observed with the following computational model: paramagnetic radiation defects are distributed uniformly over a ceramics sample, and the g factors of its EPR spectra have the anisotropy typical for dipole-dipole interaction in powder samples. By results of the data we obtained, it's clear that in future we'll need in more detailed information than that published in scientific journals about formation of the paramagnetic defect EPR spectra structure in

  6. The effect of helium, radiation damage and irradiation temperature on the mechanical properties of beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Fabritsiev, S.A. [D.V. Efremov Scientific Research Inst., St. Petersburg (Russian Federation); Pokrovsky, A.S.

    1998-01-01

    In this work different RF beryllium grades were irradiated in the BOR-60 reactor to a dose of {approx}5-10 dpa at irradiation temperatures 350, 420, 500, 800degC. Irradiation at temperatures of 350-400degC is shown to result in Be hardening due to the accumulation of radiation defect complexes. Hardening is accompanied with a sharp drop in plasticity at T{sub test} {<=} 300degC. A strong anisotropy in plasticity has been found at a mechanical testing temperature of 400degC and this parameter may be preferable when the samples are cut crosswise to the pressing direction. High-temperature irradiation (T{sub irr} = 780degC) gives rise to large helium pores over the grain boundaries and smaller pores in the grain body. Fracture is brittle and intercrystallite at T{sub test} {>=} 600degC. Helium embrittlement is accompanied as well with a drop in the Be strength properties. (author)

  7. Tritium release from EXOTIC-7 orthosilicate pebbles. Effect of burnup and contact with beryllium during irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Scaffidi-Argentina, F; Werle, H [Forschungszentrum Karlsruhe GmbH Technik und Umwelt (Germany). Inst. fuer Neutronenphysik und Reaktortechnik

    1998-03-01

    EXOTIC-7 was the first in-pile test with {sup 6}Li-enriched (50%) lithium orthosilicate (Li{sub 4}SiO{sub 4}) pebbles and with DEMO representative Li-burnup. Post irradiation examinations of the Li{sub 4}SiO{sub 4} have been performed at the Forschungszentrum Karlsruhe (FZK), mainly to investigate the tritium release kinetics as well as the effect of Li-burnup and/or contact with beryllium during irradiation. The release rate of Li{sub 4}SiO{sub 4} from pure Li{sub 4}SiO{sub 4} bed of capsule 28.1-1 is characterized by a broad main peak at about 400degC and by a smaller peak at about 800degC, and that from the mixed beds of capsule 28.2 and 26.2-1 shows again these two peaks, but most of the tritium is now released from the 800degC peak. This shift of release from low to high temperature may be due to the higher Li-burnup and/or due to contact with Be during irradiation. Due to the very difficult interpretation of the in-situ tritium release data, residence times have been estimated on the basis of the out-of-pile tests. The residence time for Li{sub 4}SiO{sub 4} from caps. 28.1-1 irradiated at 10% Li-burnup agrees quite well with that of the same material irradiated at Li-burnup lower than 3% in the EXOTIC-6 experiment. In spite of the observed shift in the release peaks from low to high temperature, also the residence time for Li{sub 4}SiO{sub 4} from caps. 26.2-1 irradiated at 13% Li-burnup agrees quite well with the data from EXOTIC-6 experiment. On the other hand, the residence time for Li{sub 4}SiO{sub 4} from caps. 28.2 (Li-burnup 18%) is about a factor 1.7-3.8 higher than that for caps. 26.2-1. Based on these data on can conclude that up to 13% Li-burnup neither the contact with beryllium nor the Li-burnup have a detrimental effect on the tritium release of Li{sub 4}SiO{sub 4} pebbles, but at 18% Li-burnup the residence time is increased by about a factor three. (J.P.N.)

  8. Beryllium technology workshop, Clearwater Beach, Florida, November 20, 1991

    International Nuclear Information System (INIS)

    Longhurst, G.R.

    1991-12-01

    This report discusses the following topics: beryllium in the ITER blanket; mechanical testing of irradiated beryllium; tritium release measurements on irradiated beryllium; beryllium needs for plasma-facing components; thermal conductivity of plasma sprayed beryllium; beryllium research at the INEL; Japanese beryllium research activities for in-pile mockup tests on ITER; a study of beryllium bonding of copper alloy; new production technologies; thermophysical properties of a new ingot metallurgy beryllium product line; implications of beryllium:steam interactions in fusion reactors; and a test program for irradiation embrittlement of beryllium at JET

  9. Beryllium technology workshop, Clearwater Beach, Florida, November 20, 1991

    Energy Technology Data Exchange (ETDEWEB)

    Longhurst, G.R.

    1991-12-01

    This report discusses the following topics: beryllium in the ITER blanket; mechanical testing of irradiated beryllium; tritium release measurements on irradiated beryllium; beryllium needs for plasma-facing components; thermal conductivity of plasma sprayed beryllium; beryllium research at the INEL; Japanese beryllium research activities for in-pile mockup tests on ITER; a study of beryllium bonding of copper alloy; new production technologies; thermophysical properties of a new ingot metallurgy beryllium product line; implications of beryllium:steam interactions in fusion reactors; and a test program for irradiation embrittlement of beryllium at JET.

  10. Comparison of compression properties and swelling of beryllium irradiated at various temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Beeston, J.M.; Miller, L.G.; Wood, E.L. Jr.; Moir, R.W.

    1983-01-01

    A beryllium cylinder irradiated in Experimental Breeder Reactor (EBR-II) for four years at 700 to 760 K to a neutron fluence of 8.13 x 10/sup 22/ n/cm/sup 2/ (total) or 1 x 10/sup 22/ n/cm/sup 2/ (E > 1 MeV) was cut into samples and tested. Yield strength and plastic strain was determined in compression tests at 300, 723, 823 K and after annealing at 1173 K for one hour. The immersion density and helium content were measured on samples. An equation for swelling was derived from the data by regression analysis. The microstructure showed agglomeration of helium in voids or bubbles at the grain boundaries.

  11. Reducing beryllium content in mixed bed solid-type breeder blankets

    Energy Technology Data Exchange (ETDEWEB)

    Shimwell, J., E-mail: mail@jshimwell.com [Department of Physics and Astronomy, University of Sheffield, Hicks Building, Hounsfield Road, Sheffield S3 7RH (United Kingdom); Lilley, S.; Morgan, L.; Packer, L.; Kovari, M.; Zheng, S. [Culham Centre for Fusion Energy, Culham Science Centre, Abingdon, Oxfordshire OX14 3DB (United Kingdom); McMillan, J. [Department of Physics and Astronomy, University of Sheffield, Hicks Building, Hounsfield Road, Sheffield S3 7RH (United Kingdom)

    2016-11-01

    Highlights: • The ratio of breeder ceramic to neutron multiplier of breeder blankets was varied linearly with depth. • Blankets with varying composition were found to perform better than uniform composition breeder blankets. • It was also possible to reduce the amount of beryllium required by the blanket. - Abstract: Beryllium (Be) is a precious resource with many high value uses, the low energy threshold (n,2n) reaction makes Be an excellent neutron multiplier for use in fusion breeder blankets. Estimates of Be requirements and available resources suggest that this could represent a major supply difficulty for solid-type blanket concepts. Reducing the quantity of Be required by breeder blankets would help to alleviate the problem to some extent. In addition, it is important that the reduction in the Be quantity does not diminish the blanket's performance in key aspects such as the tritium breeding ratio (TBR), energy multiplication and peak nuclear heating. Mixed pebble bed designs allow for the multiplier fraction to be varied throughout the blanket. This neutronics study used MCNP 6 to investigate linear variations of the multiplier fraction in relation to blanket depth, in order to better utilise the important multiplying Be(n,2n) and breeding reactions. Blankets with a uniform multiplier fraction showed little scope for reduction in Be mass. Blankets with varying multiplier fractions were able to simultaneously use 10% less Be, increase the energy amplification by 1%, reduce the peak heating by 7% and maintaining a sufficient TBR when compared to the performance achievable using a uniform composition.

  12. Investigation of high purity beryllium for the International Thermonuclear Experimental Reactor (ITER), Task 002. Final report

    International Nuclear Information System (INIS)

    Vagin, S.P.

    1995-05-01

    The report includes a description of experimental abilities of Solid Structure Research Laboratory of IAE NNC RK, a results of microstructural characterization of A-4 grade polycrystal Beryllium produced at the Ulba metal plant and a technical project-for irradiation experiments. Technical project contains a detailed description of five proposed experiments, clearing behavior of Beryllium materials under the influence of irradiation, temperature, helium and hydrogen accumulation. Complex irradiation jobs, microstructural investigations and mechanical tests are planned in the framework of these experiments

  13. Tritium and helium release from beryllium pebbles neutron-irradiated up to 230appm tritium and 3000appm helium

    Directory of Open Access Journals (Sweden)

    Vladimir Chakin

    2016-12-01

    Full Text Available Study of tritium and helium release from beryllium pebbles with diameters of 0.5 and 1mm after high-dose neutron irradiation at temperatures of 686–968K was performed. The release rate always has a single peak, and the peak temperatures at heating rates of 0.017K/s and 0.117K/s lie in the range of 1100–1350K for both tritium and helium release. The total tritium release from 1mm pebbles decreases considerably by increasing the irradiation temperature. The total tritium release from 0.5mm pebbles is less than that from 1mm pebbles and remains constant regardless of the irradiation temperature. At high irradiation temperatures, open channels are formed which contribute to the enhanced tritium release.

  14. Solid state bonding of beryllium-copper for an ITER first wall application

    Energy Technology Data Exchange (ETDEWEB)

    Odegard, B.C. Jr.; Cadden, C.H. [Sandia National Labs., Livermore, CA (United States)

    1998-01-01

    Several different joint assemblies were evaluated in support of a manufacturing technology for diffusion bonding a beryllium armor tile to a copper alloy heat sink for fusion reactor applications. Because beryllium reacts with all but a few elements to form intermetallic compounds, this study considered several different surface treatments as a means of both inhibiting these reactions and promoting a good diffusion bond between the two substrates. All diffusion bonded assemblies used aluminum or an aluminum-beryllium composite (AlBeMet-150) as the interfacial material in contact with beryllium. In most cases, explosive bonding was utilized as a technique for joining the copper alloy heat sink to an aluminum or AlBeMet-150 substrate, which was subsequently diffusion bonded to an aluminum coated beryllium tile. In this approach, a 250 {mu}m thick titanium foil was used as a diffusion barrier between the copper and aluminum to prevent the formation of Cu-Al intermetallic phases. In all cases, a hot isostatic pressing (HIP) furnace was used in conjunction with canned assemblies in order to minimize oxidation and apply sufficient pressure on the assembly for excellent metal-to-metal contact and subsequent bonding. Several different processing schedules were evaluated during the course of this study; bonded assemblies were produced that failed outside the bond area indicating a 100% joint efficiency. (author)

  15. Solid state bonding of beryllium-copper for an ITER first wall application

    International Nuclear Information System (INIS)

    Odegard, B.C. Jr.; Cadden, C.H.

    1998-02-01

    Several different joint assemblies were evaluated in support of a manufacturing technology for diffusion bonding a beryllium armor tile to a copper alloy heat sink for fusion reactor applications. Because beryllium reacts with all but a few elements to form intermetallic compounds, this study considered several different surface treatments as a means of both inhibiting these reactions and promoting a good diffusion bond between the two substrates. A diffusion bonded assemblies used aluminum or an aluminum-beryllium composite (AlBeMet-150) as the interfacial material in contact with beryllium. In most cases, explosive bonding was utilized as a technique for joining the copper alloy heat sink to an aluminum or AlBeMet-150 substrate, which was subsequently diffusion bonded to an aluminum coated beryllium tile. In this approach, a 250 microm thick titanium foil was used as a diffusion barrier between the copper and aluminum to prevent the formation of Cu-Al intermetallic phases. In all cases, a hot isostatic pressing (HIP) furnace was used in conjunction with canned assemblies in order to minimize oxidation and apply sufficient pressure on the assembly for excellent metal-to-metal contact and subsequent bonding. Several different processing schedules were evaluated during the course of this study; bonded assemblies were produced that failed outside the bond area indicating a 100% joint efficiency

  16. On kinetics of paramagnetic radiation defects accumulation in beryllium ceramics

    International Nuclear Information System (INIS)

    Polyakov, A.I.; Ryabikin, Yu.A.; Zashkvara, O.V.; Bitenbaev, M.I.; Petykhov, Yu.V.

    1999-01-01

    Results of paramagnetic radiation defects concentration dependence study in beryllium ceramics from gamma-irradiation dose ( 60 Co) within interval 0-100 Mrem are cited. Obtained dose dependence has form of accumulation curve with saturation typical of for majority of solids (crystals, different polymers, organic substances and others) , in which under irradiation occur not only formation of paramagnetic radiation defects, but its destruction due to recombination and interaction with radiation fields. Analysis of accumulation curve by the method of distant asymptotics allows to determine that observed in gamma-irradiated beryllium ceramics double line of electron spin resonance is forming of two types of paramagnetic radiation defects. It was defined, that sum paramagnetic characteristics of beryllium ceramics within 1-100 Mrad gamma- irradiation dose field change insignificantly and define from first type of paramagnetic radiation defects

  17. The laboratory of irradiated solids

    International Nuclear Information System (INIS)

    1988-01-01

    After a brief recall of results obtained these last twenty years researches in progress are described. Are studied: Solid state physics, particle-matter interactions, crystal defects, nuclear materials. A list of main projects is given [fr

  18. The 1989 progress report: Irradiated solids

    International Nuclear Information System (INIS)

    Novion, C. de.

    1989-01-01

    The 1989 activity report of the laboratory of Irradiated Solids of the Polytechnic School (France) is presented. Investigations on disordered solids are the main field of research. Disorder and its consequences on the physical properties of materials are studied. Some of the most important results are: the experimental demonstration of the creation of defects by electron excitation in iron; the precipitation induced by the irradiation of high temperature electrons; the demonstration of an additional trapping of magnetic flux lines and the increase of the critical current in the YBa2Cu307 superconducting oxyde [fr

  19. Research of flaw assessment methods for beryllium reflector elements

    International Nuclear Information System (INIS)

    Shibata, Akira; Ito, Masayasu; Takemoto, Noriyuki; Tanimoto, Masataka; Tsuchiya, Kunihiko; Nakatsuka, Masafumi; Ohara, Hiroshi; Kodama, Mitsuhiro

    2012-02-01

    Reflector elements made from metal beryllium is widely used as neutron reflectors to increase neutron flux in test reactors. When beryllium reflector elements are irradiated by neutron, bending of reflector elements caused by swelling occurs, and beryllium reflector elements must be replaced in several years. In this report, literature search and investigation for non-destructive inspection of Beryllium and experiments for Preliminary inspection to establish post irradiation examination method for research of characteristics of metal beryllium under neutron irradiation were reported. (author)

  20. Continuum emission from irradiated solid deuterium

    DEFF Research Database (Denmark)

    Forrest, J.A.; Brooks, R.L.; Hunt, J.L.

    1992-01-01

    A new emission feature from the spectrum of irradiated solid deuterium has been observed in the very near-infrared spectral region. Experiments from three laboratories, using different excitation conditions, have confirmed the observation. Comparison of the timing and temperature dependence...... of the spectral feature to the information previously available from electron spin resonance studies of solid deuterium, points to atomic association as the underlying cause. We shall show the connection of this emission to the occurrence of thermal spikes and optical flashes, previously observed in solid...

  1. Synthesis, solid-state structure, and bonding analysis of a homoleptic beryllium azide

    International Nuclear Information System (INIS)

    Naglav, Dominik; Tobey, Briac; Lyhs, Benjamin; Roemer, Beate; Blaeser, Dieter; Woelper, Christoph; Jansen, Georg; Schulz, Stephan

    2017-01-01

    [Ph 4 P] 2 [Be(N 3 ) 4 ] (1) and [PNP] 2 [Be(N 3 ) 4 ] (2; PNP=Ph 3 PNPPh 3 ) were synthesized by reacting Be(N 3 ) 2 with [Ph 4 P]N 3 and [PNP]N 3 . Compound 1 represents the first structurally characterized homoleptic beryllium azide. The electronic structure and bonding situation in the tetraazidoberyllate dianion [Be(N 3 ) 4 ] 2- were investigated by quantum-chemical calculations (NPA, ELF, LOL). (copyright 2017 Wiley-VCH Verlag GmbH and Co. KGaA, Weinheim)

  2. Synthesis, Solid-State Structure, and Bonding Analysis of a Homoleptic Beryllium Azide.

    Science.gov (United States)

    Naglav, Dominik; Tobey, Briac; Lyhs, Benjamin; Römer, Beate; Bläser, Dieter; Wölper, Christoph; Jansen, Georg; Schulz, Stephan

    2017-07-10

    [Ph 4 P] 2 [Be(N 3 ) 4 ] (1) and [PNP] 2 [Be(N 3 ) 4 ] (2; PNP=Ph 3 PNPPh 3 ) were synthesized by reacting Be(N 3 ) 2 with [Ph 4 P]N 3 and [PNP]N 3 . Compound 1 represents the first structurally characterized homoleptic beryllium azide. The electronic structure and bonding situation in the tetraazidoberyllate dianion [Be(N 3 ) 4 ] 2- were investigated by quantum-chemical calculations (NPA, ELF, LOL). © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  3. High resolution studies by Secondary Ion Mass Spectrometry of the spatial distribution of tritium in neutron irradiated beryllium pebbles

    International Nuclear Information System (INIS)

    Rabaglino, E.; Tamborini, G.; Hiernaut, J.-P.; Betti, M.

    2006-01-01

    A key issue of beryllium as a neutron multiplier in the blanket of future fusion reactors is tritium retention. Models are under development in order to predict tritium release kinetics in the typical operating conditions of the material in the blanket: the absence of experimental data in this range imposes an extrapolation of the models, therefore a detailed characterization and understanding of microscopic diffusion phenomena related to macroscopic tritium release is necessary. It has been recently shown, that the availability of evidence on such phenomena at a scale of 1 micron down to tens of nanometers enables a relevant progress in the effectiveness of model validation: therefore the need for applying and developing advanced analytical techniques based on mass spectrometry at this scale. A study of tritium spatial distribution in neutron irradiated beryllium pebbles (2 mm diameter, 480 appm 4 He, 7 appm 3 H) by means of Secondary Ion Mass Spectrometry (SIMS) is presented. Samples in different conditions (non-irradiated, at end of irradiation and at different temperatures during thermal ramp annealing) are examined by an oxygen ion primary beam with a spatial resolution of 1 micron along a diameter. The sample preparation is optimized in order to enable a quantitative comparison among the different conditions. Under an oxygen ion beam tritium is detected in the irradiated samples in a molecular form (3H 2 ), with a continuous distribution inside the grains, which suggests the presence of small clusters in agreement with TEM analyses, and in the form of peaks at grain boundaries, corresponding to large grain boundary bubbles. The evolving of molecular tritium distribution measured by SIMS during a typical thermal ramp release experiment shows precisely tritium diffusion from the centre of the grain to grain boundaries as the temperature increases: at the same time the remaining intragranular tritium inventory, given by the integral of the distribution

  4. Beryllium production using beryllium fluoride

    International Nuclear Information System (INIS)

    Hubler, Carlos Henrique

    1993-01-01

    This work presents the beryllium production by thermal decomposition of the ammonium beryllium fluoride, followed by magnesium reduction, obtained in the small pilot plant of the Brazilian National Nuclear Energy Commission - Nuclear Engineering Institute

  5. Synthesis, solid-state structure, and bonding analysis of a homoleptic beryllium azide

    Energy Technology Data Exchange (ETDEWEB)

    Naglav, Dominik; Tobey, Briac; Lyhs, Benjamin; Roemer, Beate; Blaeser, Dieter; Woelper, Christoph; Jansen, Georg; Schulz, Stephan [Faculty of Chemistry and Center for Nanointegration Duisburg-Essen (Cenide), Duisburg-Essen Univ., Essen (Germany)

    2017-07-10

    [Ph{sub 4}P]{sub 2}[Be(N{sub 3}){sub 4}] (1) and [PNP]{sub 2}[Be(N{sub 3}){sub 4}] (2; PNP=Ph{sub 3}PNPPh{sub 3}) were synthesized by reacting Be(N{sub 3}){sub 2} with [Ph{sub 4}P]N{sub 3} and [PNP]N{sub 3}. Compound 1 represents the first structurally characterized homoleptic beryllium azide. The electronic structure and bonding situation in the tetraazidoberyllate dianion [Be(N{sub 3}){sub 4}]{sup 2-} were investigated by quantum-chemical calculations (NPA, ELF, LOL). (copyright 2017 Wiley-VCH Verlag GmbH and Co. KGaA, Weinheim)

  6. Status of beryllium R and D in Japan

    International Nuclear Information System (INIS)

    Kawamura, H.; Ishida, K.

    2004-01-01

    Recently, several R and D program of beryllium for fusion are being promoted in Japan and community of beryllium study is growing up. In the R and D area of beryllium for solid breeding blanket, major subjects are beryllide application for prototype reactor, lifetime evaluation of neutron multiplier, impurity effect of beryllium and recycling of irradiated beryllium. Especially, the study of beryllide application has significant progress in these two years. The basic properties such as tritium inventory, oxidation behavior, steam interaction for stoichiometric Be 12 Ti fabricated by HIP (Hot Isostatic Pressing) have been studied and some advantages against beryllium were made clear. For manufacturing technology development, phase diagram and ductility improvement have been studied. And, Be 12 Ti pebbles with the improved microstructure were successfully fabricated by Rotating Electrode Process. In order to enhance the R and D activities, the R and D network consisted of industries, universities and laboratories in all Japan have been organized. Many collaboration and information exchange strongly promotes the R and D and some projects for commercial application have been launched form these activities. Also international collaborative project such as IEA and ISTC have been launched or planned. Recent result of R and D in Japan is described on this paper. (author)

  7. European DEMO BOT Solid Breeder Blanket: the concept based on the use of cooling plates and beds of beryllium and Li4SiO4 pebbles

    International Nuclear Information System (INIS)

    Dalle Donne, M.; Fischer, U.; Norajitra, P.; Reimann, G.; Reiser, H.

    1995-01-01

    The paper presents an important modification of the European DEMO BOT Solid Breeder Blanket. The new design uses cooling plates rather than tubes. This allows a considerable simplification of the blanket and the separation of the beryllium from the Li 4 SiO 4 pebbles. The neutronic, thermohydraulic and tritium performance of the new design is quite good and equivalent to that of the previous one. (orig.)

  8. Specific features of reactor or cyclotron {alpha}-particles irradiated beryllium microstructure

    Energy Technology Data Exchange (ETDEWEB)

    Khomutov, A M [A.A.Bochvar All-Russia Research Inst. of Inorganic Materials (VNIINM), Moscow (Russian Federation); Gromov, B F; Karabanov, V N [and others

    1998-01-01

    Studies were carried out into microstructure changes accompanying helium swelling of Be reactor neutron irradiated at 450degC or {alpha}-particles implanted in cyclotron to reach the same volume accumulation of He (6-8 ncm{sup 3} He/cm{sup 3} Be). The microstructures of reactor irradiated and implanted samples were compared after vacuum anneal at 600-800degC up to 50h. The irradiated samples revealed the etchability along the grain boundaries in zones formed by adequately large equilibrium helium pores. The width of the zones increased with the annealing time and after 50h reached 30{mu}. Depleted areas 2-3{mu} dia were observed in some regions of near grain boundary zones. The roles of grain boundaries and manufacturing pores as vacancies` sources and helium sinks are considered. (author)

  9. Beryllium allergy

    International Nuclear Information System (INIS)

    Schoenherr, S.; Pevny, I.

    1989-12-01

    Beryllium is not only a high potent allergen, but also a fotoallergen and can provoke contact allergic reactions, fotoallergic reactions, granulomatous skin reactions, pulmonary granulomatous diseases and sometimes even systemic diseases. The authors present 9 own cases of a patch test positive beryllium allergy, 7 patients with relevant allergy and 5 patients with an allergic contact stomatitis. (author)

  10. Preliminary proposal for a beryllium technology program for fusion applications

    International Nuclear Information System (INIS)

    1985-02-01

    The program was designed to provide the answers to the critical issues of beryllium technology needed in fusion blanket designs. The four tasks are as follows: (1) Beryllium property measurements needed for fusion data base. (2) Beryllium stress relaxation and creep measurements for lifetime modelling calculations. (3) Simplified recycle technique development for irradiated beryllium. (4) Beryllium neutron multiplier measurements using manganese bath absolute calibration techniques

  11. Influence of nickel and beryllium content on swelling behavior of copper irradiated with fast neutrons

    Energy Technology Data Exchange (ETDEWEB)

    Singh, B.N.; Garner, F.A.; Edwards, D.J. [Pacific Northwest National Lab., Richland, WA (United States); Evans, J.H.

    1996-10-01

    In the 1970`s, the effects of nickel content on the evolution of dislocation microstructures and the formation and growth of voids in Cu-Ni alloys were studied using 1 MeV electrons in a high voltage electron microscope. The swelling rate was found to decrease rapidly with increasing nickel content. The decrease in the swelling rate was associated with a decreasing void growth rate with increasing nickel content at irradiation temperatures up to 450{degrees}C. At 500{degrees}C, both void size and swelling rate were found to peak at 1 and 2% Ni, respectively, and then to decrease rapidly with increasing nickel content. However, recent work has demonstrated that the swelling behavior of Cu-5%Ni irradiated with fission neutrons is very similar for that of pure copper. The present experiments were designed to investigate this apparent discrepancy.

  12. Research of beryllium safety issues

    International Nuclear Information System (INIS)

    Longhurst, G.R.; Anderl, R.A.; Dolan, T.J.; Hankins, M.R.; Pawelko, R.J.

    1993-01-01

    Beryllium has been identified as a leading contender for the plasma-facing material in ITER. Its use has some obvious advantages, but there are also a number of safety concerns associated with it. The Idaho National Engineering Laboratory (INEL) has undertaken a number of studies to help resolve some of these issues. One issue is the response of beryllium to neutron irradiation. We have tested samples irradiated in the Advanced Test Reactor (ATR) and are currently preparing to make measurements of the change in mechanical properties of beryllium samples irradiated at elevated temperatures in the Fast Flux Test Facility (FFTF) and the Experimental Breeder Reactor II (EBR-II) at the INEL. Mechanical tests will be conducted at the irradiation temperatures of 375-550 C. Other experiments address permeation and retention of implanted tritium in plasma-sprayed beryllium. In one test the porosity of the material allowed 0.12% of implanted ions and 0.17% of atoms from background gas pressure to pass through the foil with essentially no delay. For comparison, similar tests on fully dense hot-rolled, vacuum melted or sintered powder foils of high purity beryllium showed only 0.001% of implanting ions to pass through the foil, and then only after a delay of several hours. None of the molecular gas appeared to permeate these latter targets. An implication is that plasma-sprayed beryllium may substantially enhance recycling of tritium to the plasma provided it is affixed to a relatively impermeable substrate. (orig.)

  13. Alternative method of portable irradiation of manganese sulphate solution by an plutonium-beryllium source for manganese sulphate bath efficiency measurements

    International Nuclear Information System (INIS)

    Silva, Fellipe Souza da; Martins, Marcelo Marques; Pereira, Walsan Wagner

    2016-01-01

    This study intends to create an alternative irradiation system from a Plutonium-Beryllium source for manganese sulphate solution using the Monte Carlo code. Thus seeking to eliminate the issue of institutes that do not have reactors or particle accelerators in its infrastructure, in order to optimize and provide independence for them to carry out efficiency measurements of MnSO_4 solution in their own locality. The Monte Carlo simulations defined the technical features of this new system so that the solution reaches the maximum neutron capture by manganese in solution. (author)

  14. LITHIUM-BERYLLIUM-BORON ISOTOPIC COMPOSITIONS IN METEORITIC HIBONITE: IMPLICATIONS FOR ORIGIN OF 10Be AND EARLY SOLAR SYSTEM IRRADIATION

    International Nuclear Information System (INIS)

    Liu, Ming-Chang; Nittler, Larry R.; Alexander, Conel M. O'D.; Lee, Typhoon

    2010-01-01

    NanoSIMS isotopic measurements of Li, Be, and B in individual hibonite grains extracted from the Murchison meteorite revealed that 10 B excesses correlate with the 9 Be/ 11 B ratios in 26 Al-free PLAty hibonite Crystals. From these data, an initial 10 Be/ 9 Be = (5.5 ± 1.6) x 10 -4 (2σ) and 10 B/ 11 B = 0.2508 ± 0.0015 can be inferred. On the other hand, chondritic boron isotopic compositions were found in 26 Al-bearing Spinel-HIBonite spherules, most likely due to contamination with normal boron. No 7 Li excesses due to 7 Be decay were observed. When combined with previously reported data, the new data yield the best defined 10 Be/ 9 Be = (5.3 ± 1.0) x 10 -4 (2σ) and 10 B/ 11 B = 0.2513 ± 0.0012 for PLACs. A comparison of this value and the best constrained 10 Be/ 9 Be = (8.8 ± 0.6) x 10 -4 in CV Ca-Al-rich inclusions supports a heterogeneous distribution of 10 Be and its protosolar irradiation origin. We consider two possible irradiation scenarios that could potentially lead to the observed Li-Be-B isotopic compositions in PLACs. Although in situ irradiation of solids with hibonite chemistry seems to provide the simplest explanation, more high quality data will be needed for quantitatively constraining the irradiation history.

  15. Beryllium electrodeposition on aluminium cathode from chloride melts

    International Nuclear Information System (INIS)

    Nichkov, I.F.; Novikov, E.A.; Serebryakov, G.A.; Kanashin, Yu.P.; Sardyko, G.N.

    1980-01-01

    Cathodic processes during beryllium deposition on liquid and solid aluminium cathodes are investigated. Mixture of sodium, potassium and beryllium chloride melts served as an lectrolyte. Beryllium ion discharge at the expense of alloy formation takes place at more positive potentials than on an indifferent cathode at low current densities ( in the case of liquid aluminium cathode). Metallographic analysis and measurements of microhardness have shown, that the cathodic product includes two phases: beryllium solid solution in aluminium and metallic beryllium. It is concluded, that aluminium-beryllium alloys with high cathodic yield by current can be obtained by the electrolytic method

  16. On kinetics of paramagnetic radiation defects accumulation in beryllium ceramics; O kinetike nakopleniya paramagnitnykh radiatsionnykh defektov v berillievykh keramikakh

    Energy Technology Data Exchange (ETDEWEB)

    Polyakov, A I; Ryabikin, Yu A; Zashkvara, O V; Bitenbaev, M I; Petykhov, Yu V [Fiziko-Tekhnicheskij Inst., Almaty (Kazakhstan); Inst. Atomnoj Ehnergii, Kurchatov (Kazakhstan)

    1999-07-01

    Results of paramagnetic radiation defects concentration dependence study in beryllium ceramics from gamma-irradiation dose ({sup 60}Co) within interval 0-100 Mrem are cited. Obtained dose dependence has form of accumulation curve with saturation typical of for majority of solids (crystals, different polymers, organic substances and others) , in which under irradiation occur not only formation of paramagnetic radiation defects, but its destruction due to recombination and interaction with radiation fields. Analysis of accumulation curve by the method of distant asymptotics allows to determine that observed in gamma-irradiated beryllium ceramics double line of electron spin resonance is forming of two types of paramagnetic radiation defects. It was defined, that sum paramagnetic characteristics of beryllium ceramics within 1-100 Mrad gamma- irradiation dose field change insignificantly and define from first type of paramagnetic radiation defects.

  17. Sandis irradiator for dried sewage solids. Final safety analysis report

    International Nuclear Information System (INIS)

    Morris, M.

    1980-07-01

    Analyses of the hazards associated with the operation of the Sandia irradiator for dried sewage solids, as well as methods and design considerations to minimize these hazards, are presented in accordance with DOE directives

  18. Recommended design correlations for S-65 beryllium

    International Nuclear Information System (INIS)

    Billone, M.C.

    1995-01-01

    The properties of tritium and helium behavior in irradiated beryllium are reviewed, along with the thermal-mechanical properties needed for ITER design analysis. Correlations are developed to describe the performance of beryllium in a fusion reactor environment. While this paper focuses on the use of beryllium as a plasma-facing component (PFC) material, the correlations presented here can also be used to describe the performance of beryllium as a neutron multiplier for a tritium breeding blanket. The performance properties for beryllium are subdivided into two categories: properties which do not change with irradiation damage to the bulk of the material; and properties which are degraded by neutron irradiation. The irradiation-independent properties described within are: thermal conductivity, specific heat capacity, thermal expansion, and elastic constants. Irradiation-dependent properties include: yield strength, ultimate tensile strength, plastic tangent modulus, uniform and total tensile elongation, thermal and irradiation-induced creep strength, He-induced swelling and tritium retention/release. The approach taken in developing properties correlations is to describe the behavior of dense, pressed S-65 beryllium -- the material chosen for ITER PFC application -- as a function of temperature. As there are essentially no data on the performance of porous and/or irradiated S-65 beryllium, the degradation of properties with as-fabricated porosity and irradiation are determined from the broad data base on S-200F, as well as other types and grades, and applied to S-65 beryllium by scaling factors. The resulting correlations can be used for Be produced by vacuum hot pressing (VHP) and cold-pressing (CP)/sintering(S)/hot-isostatic-pressing (HIP). The performance of plasma-sprayed beryllium is discussed but not quantified

  19. Beryllium poisonings

    International Nuclear Information System (INIS)

    Alibert, S.

    1959-03-01

    This note reports a bibliographical study of beryllium toxicity. Thus, this bibliographical review addresses and outlines aspects and issues like aetiology, cases of acute poisoning (cutaneous manifestations, pulmonary manifestations), chronic poisoning (cutaneous, pulmonary and bone manifestations), excretion and localisation, and prognosis

  20. Belgian research on fusion beryllium waste

    International Nuclear Information System (INIS)

    Druyts, F.; Mallants, D.; Sillen, X.; Iseghem, P. Van

    2004-01-01

    Future fusion power plants will generate important quantities of neutron irradiated beryllium. Although recycling is the preferred management option for this waste, this may not be technically feasible for all of the beryllium, because of its radiological characteristics. Therefore, at SCK·CEN, we initiated a research programme aimed at studying aspects of the disposal of fusion beryllium, including waste characterisation, waste acceptance criteria, conditioning methods, and performance assessment. One of the main issues to be resolved is the development of fusion-specific waste acceptance criteria for surface or deep geological disposal, in particular with regard to the tritium content. In case disposal is the only solution, critical nuclides can be immobilised by conditioning the waste. As a first approach to immobilising beryllium waste, we investigated the vitrification of beryllium. Corrosion tests were performed on both metallic and vitrified beryllium to provide source data for performance assessment. Finally, a first step in performance assessment was undertaken. (author)

  1. Some aspects of beryllium disposal in Kazakhstan

    International Nuclear Information System (INIS)

    Shestakov, V.; Chikhray, Y.; Shakhvorostov, Yr.

    2004-01-01

    Historically in Kazakhstan all disposals of used beryllium and beryllium wasted materials were stored and recycled at JSC ''Ulba Metallurgical Plant''. Since Ulba Metallurgical Plant (beside beryllium and tantalum production) is one of the world largest complex producers of fuel for nuclear power plants as well it has possibilities, technologies and experience in processing toxic and radioactive wastes related with those productions. At present time only one operating Kazakhstan research reactors (EWG1M in Kurchatov) contains beryllium made core. The results of current examination of that core allow using it without replacement long time yet (at least for next five-ten years). Nevertheless the problem how to utilize such irradiated beryllium becomes actual issue for Kazakhstan even today. Since Kazakhstan is the member of ITER/DEMO Reactors Projects and is permanently considered as possible provider of huge amount of beryllium for those reactors so that is the reason for starting studies of possibilities of large scale processing/recycling of such disposed irradiated beryllium. It is clear that the Ulba Metallurgical Plant is considered as the best site for it in Kazakhstan. The draft plan how to organize experimental studies of irradiated beryllium disposals in Kazakhstan involving National Nuclear Center, National University (Almaty), JSC ''Ulba Metallurgical Plant'' (Ust-Kamenogorsk) would be presented in this paper as well as proposals to arrange international collaboration in that field through ISTC (International Science Technology Center, Moscow). (author)

  2. Production behavior of irradiation defects in solid breeder materials

    Energy Technology Data Exchange (ETDEWEB)

    Moriyama, Hirotake; Moritani, Kimikazu [Kyoto Univ. (Japan)

    1998-03-01

    The irradiation effects in solid breeder materials are important for the performance assessment of fusion reactor blanket systems. For a clearer understanding of such effects, we have studied the production behavior of irradiation defects in some lithium ceramics by an in-situ luminescence measurement technique under ion beam irradiation. The luminescence spectra were measured at different temperatures, and the temperature-transient behaviors of luminescence intensity were also measured. The production mechanisms of irradiation defects were discussed on the basis of the observations. (author)

  3. Neutron Dosimetry and Irradiation of Solids; Dosimetrie des neutrons et irradiation des solides

    Energy Technology Data Exchange (ETDEWEB)

    Perriot, G; Schmitt, A P [Commissariat a l' Energie Atomique. Centre d' Etudes Nucleaires de Saclay, 91 - Gif-sur-Yvette (France)

    1962-07-01

    Results of work at C.E.A. from 1958 to 1960 are reviewed. The possibilities offered by classical dosimetry methods are discussed. The tests which led to the utilization, for fast neutron dosimetry, of resistivity variations induced in solid W by such neutrons are described. Experimental W irradiation results led to a definition of neutron efficiency which describes the relations between neutron energy and their effects on materials. Possibilities offered by detectors which make use of radiation damage and are sensitive to neutrons at keV energies were explored. In other work, the principal French reactors were classified according to their ability to produce damage in materials such as W. (authors) [French] Dans ce rapport on a presente les resultats essentiels de travaux qui ont ete effectues de 1958 a 1980 par des chercheurs du CEA issus de differents services. En meme temps qu'une revue des possibilites offertes a l'epoque par les methodes classiques de dosimetrie (utilisation des detecteurs par activation), on a decrit les essais qui devaient permettre d'utiliser, a la dosimetrie les neutrons rapides, les variations de resistivite qu'ils creent dans un corps solide (tungstene). L'irradiation du tungstene a montre l'importance qu'il y avait a definir 'l'efficacite' des neutrons, c'est-a-dire leur aptitude plus ou moins grande, selon leur energie, a creer des defauts dans les materiaux. L'efficacite d'un emplacement d'irradiation se trouvant liee au spectre neutronique, on a vu les difficultes qu'il y avait a utiliser les detecteurs par activation des qu'on n'avait plus affaire a un spectre en 1/E ou de fission et on a pu entrevoir les possibilites offertes par les detecteurs utilisant la creation des defauts qui repondent a tous les neutrons d'energies, superieures a quelques keV. Enfin, on a classe les principaux types de Piles Francaises selon leur aptitude a creer plus ou moins rapidement des dommages dans des materiaux comme le tungstene. (auteur)

  4. The design of a multisource americium-beryllium (Am-Be) neutron irradiation facility using MCNP for the neutronic performance calculation.

    Science.gov (United States)

    Sogbadji, R B M; Abrefah, R G; Nyarko, B J B; Akaho, E H K; Odoi, H C; Attakorah-Birinkorang, S

    2014-08-01

    The americium-beryllium neutron irradiation facility at the National Nuclear Research Institute (NNRI), Ghana, was re-designed with four 20 Ci sources using Monte Carlo N-Particle (MCNP) code to investigate the maximum amount of flux that is produced by the combined sources. The results were compared with a single source Am-Be irradiation facility. The main objective was to enable us to harness the maximum amount of flux for the optimization of neutron activation analysis and to enable smaller sample sized samples to be irradiated. Using MCNP for the design construction and neutronic performance calculation, it was realized that the single-source Am-Be design produced a thermal neutron flux of (1.8±0.0007)×10(6) n/cm(2)s and the four-source Am-Be design produced a thermal neutron flux of (5.4±0.0007)×10(6) n/cm(2)s which is a factor of 3.5 fold increase compared to the single-source Am-Be design. The criticality effective, k(eff), of the single-source and the four-source Am-Be designs were found to be 0.00115±0.0008 and 0.00143±0.0008, respectively. Copyright © 2014 Elsevier Ltd. All rights reserved.

  5. Experimental and theoretical study of solid solution stability under irradiation

    International Nuclear Information System (INIS)

    Cauvin, Richard.

    1981-08-01

    The behavior of dilute alloys (Al-Zn, Al-Ag, Al-Si, Al-Ge and Al-Mg) under 1 MeV electron irradiation has been studied in a high voltage electron microscope. A phenomenon of homogeneous precipitation induced by irradiation in undersaturated solid solutions (Al-Zn, Al-Ag and Al-Si) has been discovered; the observed precipitates are either coherent or incoherent, but never associated with point defect sinks. The solubility limit is a function of irradiation temperature and flux; but, under irradiation, it does not behave as a true thermal solubility limit (without irradiation). The existing theories (kinetic or strictly thermodynamic) do not account for this phenomenon. It is shown that the irreversibility of the mutual recombination between trapped vacancies and mixed interstitials is the driving force of this homogeneous precipitation. Using a dilute solid solution model, we show that, under irradiation, the homogeneous stationary state, stable from a strictly thermodynamic point of view, can be unstable when the recombination reaction is taken into account. The solubility limit under irradiation is calculated with a nucleation-growth model taking account for this effect; it is proportional to the thermal solubility limit without irradiation. This model explains all the experimental observations [fr

  6. Method for welding beryllium

    Science.gov (United States)

    Dixon, R.D.; Smith, F.M.; O`Leary, R.F.

    1997-04-01

    A method is provided for joining beryllium pieces which comprises: depositing aluminum alloy on at least one beryllium surface; contacting that beryllium surface with at least one other beryllium surface; and welding the aluminum alloy coated beryllium surfaces together. The aluminum alloy may be deposited on the beryllium using gas metal arc welding. The aluminum alloy coated beryllium surfaces may be subjected to elevated temperatures and pressures to reduce porosity before welding the pieces together. The aluminum alloy coated beryllium surfaces may be machined into a desired welding joint configuration before welding. The beryllium may be an alloy of beryllium or a beryllium compound. The aluminum alloy may comprise aluminum and silicon. 9 figs.

  7. Method for welding beryllium

    International Nuclear Information System (INIS)

    Dixon, R.D.; Smith, F.M.; O'Leary, R.F.

    1997-01-01

    A method is provided for joining beryllium pieces which comprises: depositing aluminum alloy on at least one beryllium surface; contacting that beryllium surface with at least one other beryllium surface; and welding the aluminum alloy coated beryllium surfaces together. The aluminum alloy may be deposited on the beryllium using gas metal arc welding. The aluminum alloy coated beryllium surfaces may be subjected to elevated temperatures and pressures to reduce porosity before welding the pieces together. The aluminum alloy coated beryllium surfaces may be machined into a desired welding joint configuration before welding. The beryllium may be an alloy of beryllium or a beryllium compound. The aluminum alloy may comprise aluminum and silicon. 9 figs

  8. Problems of the heat transfer during the irradiation of solids

    International Nuclear Information System (INIS)

    Jahn, G.

    1981-03-01

    This report deals with the thermal problems during the irradiation of solids. Analytical and constructive solutions are outlined by some examples. Two cases are looked at: 1) the samples and the equipment are warmed up during irradiation. Thus they have to be cooled which yields a negative heat flux direction. 2) The samples shall have a suitable temperature higher than room temperature. Thus they have to be heated which yields a positive heat flux direction. (BHO)

  9. Beryllium for fusion application - recent results

    International Nuclear Information System (INIS)

    Khomutov, A.; Barabash, V.; Chakin, V.; Chernov, V.; Davydov, D.; Gorokhov, V.; Kawamura, H.; Kolbasov, B.; Kupriyanov, I.; Longhurst, G.; Scaffidi-Argentina, F.; Shestakov, V.

    2002-01-01

    The main issues for the application of beryllium in fusion reactors are analyzed taking into account the latest results since the ICFRM-9 (Colorado, USA, October 1999) and presented at 5th IEA Be Workshop (10-12 October 2001, Moscow Russia). Considerable progress has been made recently in understanding the problems connected with the selection of the beryllium grades for different applications, characterization of the beryllium at relevant operational conditions (irradiation effects, thermal fatigue, etc.), and development of required manufacturing technologies. The key remaining problems related to the application of beryllium as an armour in near-term fusion reactors (e.g. ITER) are discussed. The features of the application of beryllium and beryllides as a neutron multiplier in the breeder blanket for power reactors (e.g. DEMO) in pebble-bed form are described

  10. Beryllium for fusion application - recent results

    Science.gov (United States)

    Khomutov, A.; Barabash, V.; Chakin, V.; Chernov, V.; Davydov, D.; Gorokhov, V.; Kawamura, H.; Kolbasov, B.; Kupriyanov, I.; Longhurst, G.; Scaffidi-Argentina, F.; Shestakov, V.

    2002-12-01

    The main issues for the application of beryllium in fusion reactors are analyzed taking into account the latest results since the ICFRM-9 (Colorado, USA, October 1999) and presented at 5th IEA Be Workshop (10-12 October 2001, Moscow Russia). Considerable progress has been made recently in understanding the problems connected with the selection of the beryllium grades for different applications, characterization of the beryllium at relevant operational conditions (irradiation effects, thermal fatigue, etc.), and development of required manufacturing technologies. The key remaining problems related to the application of beryllium as an armour in near-term fusion reactors (e.g. ITER) are discussed. The features of the application of beryllium and beryllides as a neutron multiplier in the breeder blanket for power reactors (e.g. DEMO) in pebble-bed form are described.

  11. Anisotropic dewetting of ion irradiated solid films

    Energy Technology Data Exchange (ETDEWEB)

    Repetto, L., E-mail: luca.repetto@unige.it [Dipartimento di fisica, Università di Genova, Via Dodecaneso 33, 16146 Genova (Italy); Šetina Batič, B. [Inštitut Za Kovinske Materiale in Tehnologije, Lepi pot 11, 1000 Ljubljana (Slovenia); Firpo, G.; Piano, E.; Valbusa, U. [Dipartimento di fisica, Università di Genova, Via Dodecaneso 33, 16146 Genova (Italy)

    2013-11-15

    Experiments of irradiation with 30 keV Ga ions were conducted on ultrathin chromium films on rippled silicon substrates. The evolution of their surface morphology, as detected by real time scanning electron microscopy, shows an apparent differential sputtering yield for regions of positive and negative curvature which is in contrast with the standard theory for curvature depending sputtering yield. In particular, at the end of the irradiation process, chromium wires are left in the valleys of the substrate. This result was explained in terms of local melting caused by the ion impact and of a process of dewetting under the concurring actions of surface tension and Van der Waals forces while ion sputtering is active. The interpretation of the reported experimental results are fully supported by numeric simulations implementing the same continuum model used to explain ion induced spinodal dewetting. This hierarchical self-organization process breaks the symmetry of previously demonstrated ion induced dewetting, making possible to create new structures by using the same fundamental effects.

  12. Dosimetry report for the Sandia irradiator for dried sewage solids

    International Nuclear Information System (INIS)

    Greene, R.T.; McFarland, E.W.; Dickson, H.W.

    1981-06-01

    Gamma dose measurements were made at the Sandia Irradiator for Dried Sewage Solids. Passive plastic, chemical, and thermoluminescent dosimeters were exposed in the facility under conditions designed to simulate typical plant operation. Absolute dose and dose distribution information were obtained in air, water, compost, fruit, and sewage sludge

  13. Experiments on tritium behavior in beryllium, (1)

    International Nuclear Information System (INIS)

    Kawamura, Hiroshi; Ishizuka, Etsuo; Matsumoto, Mikio; Inada, Seiji; Sezaki, Katsuji; Saito, Minoru; Kato, Mineo.

    1989-06-01

    In JMTR, it was observed that the tritium concentration of the primary coolant increases with the reactor operation at 50 MW. As one of the tritium generation sources, we paid attention to a neutron reflector made of beryllium because the tritium generation rate in the beryllium is bigger than other components in the reactor core. On the other hand, the irradiation test of blanket materials (i.e. tritium breeding materials and neutron multipling materials) are planned for development of the fusion reactor in JMTR and the beryllium will be also irradiated as a neutron multiplier with tritium breeding materials. Therefore, as the irradiated specimens, we used a hot-pressed beryllium disk fabricated by the same method as the neutron reflector or the neutron multiplier and conducted the irradiation tests in JMTR. The purpose of these tests are to clarify the tritium behavior in the hot-pressed beryllium. In this paper, from a viewpoint of the fabrication of capsules for neutron irradiation, the specifications of the irradiated specimens and capsules are summarized. Additionally, the results on the puncture test of the container of the irradiation specimens are described. (author)

  14. Dried, irradiated sewage solids as supplemental feed for cattle

    International Nuclear Information System (INIS)

    Smith, G.S.; Kiesling, H.E.; Ray, E.E.; Orcasberro, R.; Trujillo, P.; Herbel, C.H.; Sivinski, J.S.

    1980-01-01

    Sewage solids were collected as 'primary settled solids' and then dried and gamma-irradiated (using 60 Co or 177 Cs) to absorbed dosage of about one magarad to minimize viable parasites and pathogenic organisms. Nutrient composition and bioassays suggested prospective usage as supplemental feed for ruminants. In a large-scale experiment, beef cows grazing poor-quality rangeland forage during late gestation-early lactation were given either no supplemental feed or cottonseed meal or experimental supplement comprised of 62% sewage solids. Supplements were provided for 13 weeks until rangeland forage quality improved seasonably. Supplemental cottenseed meal for cows improved weaning weights of calves by about 11% over unsupplemented controls; whereas, supplement with 62% sewage solids improved calf weaning weights by about 7%. Hazards or risks to animals or to human health appear to be slight when sewage solids of this type are fed as supplemental feeds to cattle in production programs of this type. (Auth.)

  15. Experiments on tritium behavior in beryllium, (2)

    International Nuclear Information System (INIS)

    Ishitsuka, Etsuo; Kawamura, Hiroshi; Nakata, Hirokatsu; Sugai, Hiroyuki; Tanase, Masakazu.

    1990-02-01

    Beryllium has been used as the neutron reflector of material testing reactor and as the neutron multiplier for the fusion reactor lately. To study the tritium behavior in beryllium, we conducted the experiments, i.e., tritium release by recoil or diffusion by using the hot-pressed beryllium which had been produced both tritium and helium by neutron irradiation. From our experiments, we found that (1) amount of tritium production per one cycle irradiation (lasting 22 days) of JMTR is 10 mCi/g, (2) amount of tritium per surface area of hot-pressed beryllium released by recoil is 4 μCi/cm 2 , (3) diffusion coefficient of tritium in a temperature range of 800 ∼1180degC can be expressed with the following equation; D = 8.7 x 10 4 exp(-2.9x10 5 /R/T) cm 2 /s. (author)

  16. THE IDAHO NATIONAL LABORATORY BERYLLIUM TECHNOLOGY UPDATE

    International Nuclear Information System (INIS)

    Glen R. Longhurst

    2007-01-01

    A Beryllium Technology Update meeting was held at the Idaho National Laboratory on July 18, 2007. Participants came from the U.S., Japan, and Russia. There were two main objectives of this meeting. One was a discussion of current technologies for beryllium in fission reactors, particularly the Advanced Test Reactor and the Japan Materials Test Reactor, and prospects for material availability in the coming years. The second objective of the meeting was a discussion of a project of the International Science and Technology Center regarding treatment of irradiated beryllium for disposal. This paper highlights discussions held during that meeting and major conclusions reached

  17. Surface roughness statistics and temperature step stress effects for D-T solid layers equilibrated inside a 2 mm beryllium torus

    International Nuclear Information System (INIS)

    Sheliak, J.D.; Hoffer, J.K.

    1998-01-01

    Solid D-T layers are equilibrated inside a 2 mm diameter beryllium toroidal cell at temperatures ranging from 19.0 K to 19.6 K, using the beta-layering process. The experimental runs consists of multiple cycles of rapid- or slow-freezing of the initially liquid D-T charge, followed by a lengthy period of beta-layering equilibration, terminated by melting the layer. The temperature was changed in discrete steps at the end of some equilibration cycles in an attempt to simulate actual ICF target conditions. High-precision images of the D-T solid-vapor interface were analyzed to yield the surface roughness σ mns as a sum of modal contributions. Results show an overage σ mns of 1.3 ± 0.3 microm for layers equilibrated at 19.0 K and show an inverse dependence of σ mns on equilibration temperature up to 19.525 K. Inducing sudden temperature perturbations lowered σ mns to 1.0 ± 0.05 microm

  18. Fluorimetric method for determination of Beryllium

    International Nuclear Information System (INIS)

    Sparacino, N.; Sabbioneda, S.

    1996-10-01

    The old fluorimetric method for the determination of Beryllium, based essentially on the fluorescence of the Beryllium-Morine complex in a strongly alkaline solution, is still competitive and stands the comparison with more modern methods or at least three reasons: in the presence of solid or gaseous samples (powders), the times necessary to finalize an analytic determination are comparable since the stage of the process which lasts the longest is the mineralization of the solid particles containing Beryllium, the cost of a good fluorimeter is by far Inferior to the cost, e. g., of an Emission Spectrophotometer provided with ICP torch and magnets for exploiting the Zeeman effect and of an Atomic absorption Spectrophotometer provided with Graphite furnace; it is possible to determine, fluorimetrically, rather small Beryllium levels (about 30 ng of Beryllium/sample), this potentiality is more than sufficient to guarantee the respect of all the work safety and hygiene rules now in force. The study which is the subject of this publication is designed to the analysis procedure which allows one to reach good results in the determination of Beryllium, chiefly through the control and measurement of the interference effect due to the presence of some metals which might accompany the environmental samples of workshops and laboratories where Beryllium is handled, either at the pure state or in its alloys. The results obtained satisfactorily point out the merits and limits of this analytic procedure

  19. High performance liquid chromatographic separation of beryllium from some transition metals produced in high energy proton irradiations of medium mass elements: measurement of (p,7Be) cross sections

    International Nuclear Information System (INIS)

    Fassbender, M.; Spellerberg, S.; Qaim, S.M.

    1996-01-01

    A high performance liquid chromatographic (HPLC) method was developed for the separation of 7 Be formed in high energy proton irradiation of medium mass elements like Fe, Cu etc. The bulk of the target material was removed in a preseparation step. Thereafter beryllium was obtained in a high purity within a few minutes elution time using a mixture of 5 mM citric acid and 1.0 mM pyridinedicarboxylic acid as eluent and a SYKAM KO2 analytical cation-exchange column. The effect of Be-carrier on the quality of separation was investigated. The quality of separation deteriorated with the increasing Be-carrier column loading. A certain amount of Be-carrier was, however, necessary in order to quantitate the results. By using low Be-carrier amounts (∝100 μg) and determining the elution yield via a conductometric method, it was possible to obtain quantitative separation results. Besides the analytical column, a semi-preparative column was also used, and the Be separation yield determined gravimetrically. The cross sections for the (p, 7 Be) process on Cu obtained using the two separation columns (analytical and semipreparative) and the two separation yield determination methods agreed within 15%. (orig.)

  20. Status of material development for lifetime expansion of beryllium reflector

    Energy Technology Data Exchange (ETDEWEB)

    Dorn, C [Materion Brush Beryllium and Composites, California (United States); Tsuchiya, Kunihiko; Kawamura, Hiroshi [Japan Atomic Energy Agency, Oarai Research and Development Center, Oarai, Ibaraki (Japan); Hatano, Y [Univ. of Toyama, Toyama (Japan); Chakrov, P [INP-KNNC, Almaty (Kazakhstan); Kodama, M [Nippon Nuclear Fuel Development Co., Ltd., Oarai, Ibaraki (Japan)

    2012-03-15

    Beryllium has been used as the reflector element material in the reactor, specifically S-200F structural grade beryllium manufactured by Materion Brush Beryllium and Composites (former, Brush Wellman Inc.). As a part of the reactor upgrade, the Japan Atomic Energy Agency (JAEA) also has carried out the cooperation experiments to extend the operating lifetime of the beryllium reflector elements. It will first be necessary to determine which of the material's physical, mechanical and chemical properties will be the most influential on that choice. The irradiation testing plans to evaluate the various beryllium grades are also briefly considered and prepared. In this paper, material selection, irradiation test plan and PEI development for lifetime expansion of beryllium are described for material testing reactors. (author)

  1. Solid malignant neoplasms after childhood irradiation: decrease of the relative risk with time after irradiation

    International Nuclear Information System (INIS)

    Vathaire, F. de; Shamsaldin, A.; Grimaud, E.; Campbell, S.; Guerra, M.; Raquin, M.; Hardiman, C.; Jan, P.; Rumeau, N.; Diallo, I.; Nicolazic, G.; Lamon, A.; Oberlin, O.; Cervens, C. de; Suarez, A.; Meresse, V.; Eschwege, F.; Sancho-Garnier, H.; Chavaudra, J.; Lermerle, J.; Bessa, E.; Bell, J.; Hawkins, M.; Schlienger, J.Y.; Panis, X.; Lagrande, J.L.; Gaboriaud, G.; Zucker, J.M.; Daly-Schveitzer, N.

    1995-01-01

    The pattern of the temporal distribution of solid cancer incidence after irradiation in childhood is not well known, although, its importance in radioprotection is well known. We studied a cohort of 1 055 children from 8 European cancer centres, who received radiotherapy between 1942 and 1985 for a first cancer in childhood. After a mean follow-up of 19 years, 26 children developed a solid second malignant neoplasm (SMN), as compared to 5.6 expected from general population rates. Both the excess relative risk and the excess of absolute risk of solid SMN were higher among children who were younger at time of the irradiation. After reaching a maximum 15 to 20 years after irradiation, the excess relative risk of SMN decreased with time after irradiation, when controlling for age at irradiation and sex. The analysis of the risk of thyroid, brain and breast cancer together, as a function of the dose averaged on these 3 organs lead to similar results. (authors). 16 refs., 8 tabs., 2 figs

  2. Combined BC/MD approach to the evaluation of damage from fast neutrons and its implementation for beryllium irradiation in a fusion reactor

    Science.gov (United States)

    Borodin, V. A.; Vladimirov, P. V.

    2017-12-01

    The determination of primary damage production efficiency in metals irradiated with fast neutrons is a complex problem. Typically, the majority of atoms are displaced from their lattice positions not by neutrons themselves, but by energetic primary recoils, that can produce both single Frenkel pairs and dense localized cascades. Though a number of codes are available for the calculation of displacement damage from fast ions, they commonly use binary collision (BC) approximation, which is unreliable for dense cascades and thus tend to overestimate the number of created displacements. In order to amend the radiation damage predictions, this work suggests a combined approach, where the BC approximation is used for counting single Frenkel pairs only, whereas the secondary recoils able to produce localized dense cascades are stored for later processing, but not followed explicitly. The displacement production in dense cascades is then determined independently from molecular dynamics (MD) simulations. Combining contributions from different calculations, one gets the total number of displacements created by particular neutron spectrum. The approach is applied here to the case of beryllium irradiation in a fusion reactor. Using a relevant calculated energy spectrum of primary knocked-on atoms (PKAs), it is demonstrated that more than a half of the primary point defects (˜150/PKA) is produced by low-energy recoils in the form of single Frenkel pairs. The contribution to the damage from the dense cascades as predicted using the mixed BC/MD scheme, i.e. ˜110/PKA, is remarkably lower than the value deduced from uncorrected SRIM calculations (˜145/PKA), so that in the studied case SRIM tends to overpredict the total primary damage level.

  3. Chronic Beryllium Disease

    Science.gov (United States)

    ... who are exposed to beryllium will not experience health effects. Studies have shown that on average, 1 – 6 percent of exposed workers develop beryllium sensitization, although the rates can be ...

  4. Thermal Properties of Beryllium Metal

    International Nuclear Information System (INIS)

    Cho, Tae Won; Baek, Je Kyun; Jeong, Gwan Yoon; Kim, Ji Hyeon; Sohn, Dong Seong

    2013-01-01

    It is known that the presence of as-fabricated porosity largely affect thermal conductivity of beryllium. Therefore, in this paper we will suggest a new thermal conductivity equation which consider volume fraction and discuss how this can be applied to irradiation induced degradation of thermal conductivity later. This study was performed to develop a new correlation of thermal conductivity of Beryllium. Although there are many factors like BeO contents, impurity level, grain size, and porosity, we assumed porosity will be the dominant factor for thermal conductivity. Therefore, a new correlation which consider volume fraction by applying Maxwell-Eucken equation is developed and this is consistent to some degrees. However, increasing impurity level and decreasing grain size will decrease thermal conductivity. Therefore, we need to consider their effects although we assume BeO contents, impurity, and grain size do not make noticeable effects in the future. Furthermore, thermal conductivity degradation by neutron irradiation should be considered afterward. There are two main factors for the thermal conductivity degradation: the one is defects formed by neutron collisions and the other is helium generated by transmutation of Be. It is known that they make a considerable degradation of conductivity. Beryllium is known there are considerable volume increases by helium accumulation. Therefore, we anticipate our suggested model can be applicable if it has been developed furthermore considering irradiation induced swelling

  5. Report of a technical evaluation panel on the use of beryllium for ITER plasma facing material and blanket breeder material

    Energy Technology Data Exchange (ETDEWEB)

    Ulrickson, M.A. [ed.] [Sandia National Labs., Albuquerque, NM (United States); Manly, W.D. [Oak Ridge National Lab., TN (United States); Dombrowski, D.E. [Brush Wellman, Inc., Cleveland, OH (United States)] [and others

    1995-08-01

    Beryllium because of its low atomic number and high thermal conductivity, is a candidate for both ITER first wall and divertor surfaces. This study addresses the following: why beryllium; design requirements for the ITER divertor; beryllium supply and unirradiated physical/mechanical property database; effects of irradiation on beryllium properties; tritium issues; beryllium health and safety; beryllium-coolant interactions and safety; thermal and mechanical tests; plasma erosion of beryllium; recommended beryllium grades for ITER plasma facing components; proposed manufacturing methods to produce beryllium parts for ITER; emerging beryllium materials; proposed inspection and maintenance techniques for beryllium components and coatings; time table and costs; and the importance of integrating materials and manufacturing personnel with designers.

  6. Report of a technical evaluation panel on the use of beryllium for ITER plasma facing material and blanket breeder material

    International Nuclear Information System (INIS)

    Ulrickson, M.A.; Manly, W.D.; Dombrowski, D.E.

    1995-08-01

    Beryllium because of its low atomic number and high thermal conductivity, is a candidate for both ITER first wall and divertor surfaces. This study addresses the following: why beryllium; design requirements for the ITER divertor; beryllium supply and unirradiated physical/mechanical property database; effects of irradiation on beryllium properties; tritium issues; beryllium health and safety; beryllium-coolant interactions and safety; thermal and mechanical tests; plasma erosion of beryllium; recommended beryllium grades for ITER plasma facing components; proposed manufacturing methods to produce beryllium parts for ITER; emerging beryllium materials; proposed inspection and maintenance techniques for beryllium components and coatings; time table and costs; and the importance of integrating materials and manufacturing personnel with designers

  7. Experimental study of swelling of irradiated solid methane during annealing

    International Nuclear Information System (INIS)

    Shabalin, E.; Fedorov, A.; Kulagin, E.; Kulikov, S.; Melikhov, V.; Shabalin, D.

    2008-01-01

    Solid methane, notwithstanding its poor radiation properties, is still widely in use at pulsed neutron sources. One of the specific problems is radiolytic hydrogen gas pressure on the walls of a methane chamber during annealing of methane. Results of experimental study of this phenomenon under fast neutron irradiation with the help of a specially made low temperature irradiation rig at the IBR-2 pulsed reactor are presented. Peak pressure on the wall of the experimental capsule during heating of a sample irradiated at 23-35 K appeared to have a maximum of 27 bar at the absorbed dose 20 MGy, and then falls down with higher doses. Pressure always reached its peak value within the temperature range 72-79 K. Generally, three phases of methane swelling during heating can be distinguished, each characterized by proper rate and intensity. Results of this study were accounted for in design of the solid methane moderator of the second target station of the ISIS facility (England)

  8. Laser fabrication of beryllium components

    International Nuclear Information System (INIS)

    Hanafee, J.E.; Ramos, T.J.

    1995-08-01

    Working with the beryllium industry on commercial applications and using prototype parts, the authors have found that the use of lasers provides a high-speed, low-cost method of cutting beryllium metal, beryllium alloys, and beryllium-beryllium oxide composites. In addition, they have developed laser welding processes for commercial structural grades of beryllium that do not need a filler metal; i.e., autogenous welds were made in commercial structural grades of beryllium by using lasers

  9. The Effect Of Beryllium Interaction With Fast Neutrons On the Reactivity Of ETRR-2 Research Reactor

    International Nuclear Information System (INIS)

    Aziz, M.; El Messiry, A.M.

    2000-01-01

    The effect of beryllium interactions with fast neutrons is studied for Etrr 2 research reactors. Isotope build up inside beryllium blocks is calculated under different irradiation times. a new model for the Etrr 2 research reactor is designed using MCNP code to calculate the reactivity and flux change of the reactor due to beryllium poison

  10. Beryllium chemistry and processing

    CERN Document Server

    Walsh, Kenneth A

    2009-01-01

    This book introduces beryllium; its history, its chemical, mechanical, and physical properties including nuclear properties. The 29 chapters include the mineralogy of beryllium and the preferred global sources of ore bodies. The identification and specifics of the industrial metallurgical processes used to form oxide from the ore and then metal from the oxide are thoroughly described. The special features of beryllium chemistry are introduced, including analytical chemical practices. Beryllium compounds of industrial interest are identified and discussed. Alloying, casting, powder processing, forming, metal removal, joining and other manufacturing processes are covered. The effect of composition and process on the mechanical and physical properties of beryllium alloys assists the reader in material selection. The physical metallurgy chapter brings conformity between chemical and physical metallurgical processing of beryllium, metal, alloys, and compounds. The environmental degradation of beryllium and its all...

  11. Beryllium. Evaluation of beryllium hydroxide industrial processes. Pt. 3

    International Nuclear Information System (INIS)

    Lires, O.A.; Delfino, C.A.; Botbol, J.

    1991-01-01

    This work continues the 'Beryllium' series. It is a historical review of different industrial processes of beryllium hydroxide obtention from beryllium ores. Flowsheats and operative parameters of five plants are provided. These plants (Degussa, Brush Beryllium Co., Beryllium Corp., Murex Ltd., SAPPI) were selected as representative samples of diverse commercial processes in different countries. (Author) [es

  12. Sewage Solids Irradiator Transportation System (SSITS) cask: preliminary design description

    International Nuclear Information System (INIS)

    Eakes, R.G.; Kempka, S.N.; Lamoreaux, G.H.; Sutherland, S.H.

    1983-02-01

    The preliminary design of the Sewage Solids Irradiator Transportation System (SSITS) Cask is presented in this document. The SSITS cask is to be used for the transport of radioactive cesium chloride and strontium fluoride capsules which are of use in irradiators or as heat sources. The SSITS cask is approximately 1.4 m in diameter, 1.3 m high, weighs roughly 9 t, provides 33 cm of steel shielding, and can dissipate up to 5.2 kW of decay heat. The cask design criteria are identified and a description of the cask design and operation is provided. Detailed analyses of the design were performed to demonstrate licensability of the cask by the Nuclear Regulatory Commission (NRC). Results of the analyses indicate that the preliminary design is in compliance with the pertinent regulatory requirements for licensing of a radioactive material transportation container

  13. Experimental studies and modeling of processes of hydrogen isotopes interaction with beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Tazhibaeva, I.L.; Chikhray, Y.V.; Romanenko, O.G.; Klepikov, A.Kh.; Shestakov, V.P.; Kulsartov, T.V. [Science Research Inst. of Experimental and Theoretical Physics of Kazakh State Univ., Almaty (Kazakhstan); Kenzhin, E.A.

    1998-01-01

    The objective of this work was to clarify the surface beryllium oxide influence on hydrogen-beryllium interaction characteristics. Analysis of experimental data and modeling of processes of hydrogen isotopes accumulation, diffusion and release from neutron irradiated beryllium was used to achieve this purpose as well as the investigations of the changes of beryllium surface element composition being treated by H{sup +} and Ar{sup +} plasma glowing discharge. (author)

  14. Dried, irradiated sewage solids as supplemental feed for cattle

    Energy Technology Data Exchange (ETDEWEB)

    Smith, G.S.; Kiesling, H.E.; Ray, E.E.; Orcasberro, R.; Trujillo, P.; Herbel, C.H.

    1979-01-01

    Sewage solids were collected as primary settled solids and then dried and gamma-irradiated (using /sup 60/Co or /sup 137/Cs) to absorbed dosage of about one megarad to minimize viable parasites and pathogenic organisms. Nutrient composition and bioassays with rumen microbes suggested prospective usage as supplemental feed for ruminants. Short-term experiments with sheep and then with cattle further suggested that usage of nutrients could be beneficial and that accumulation of heavy metals was not excessive. A longer-term feeding trial with cattle fed sewage solids as 20% of diet for 68 days demonstrated that tissue uptake of elements such as Cu, Fe and Pb was measurably increased, but not sufficient to exceed ranges considered normal. Likewise, of 22 refractory organic compounds having toxicological interest, only a few were detectible in adipose tissue and none of these exceeded levels that have been reported in tissues from cattle produced conventionally. In a large-scale experiment, beef cows grazing poor-quality rangeland forage during late gestation-early lactation were given either no spplemental feed or cottonseed meal or experimental supplement comprised of 62% sewage solids. Supplements were provided for 13 weeks until rangeland forage quality improved seasonably. Supplemental cottonseed meal for cows improved weaning weights of calves by about 11% over unsupplemented controls; whereas, supplement with 62% sewage solids improved calf weaning weights by about 7%. Hazards or risks to animals or to human health appear to be slight when sewage solids of this type are fed as supplemental feeds to cattle in production programs of this type.

  15. (Beryllium). Internal Report No. 137, Jan. 15, 1958; Le beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Mouret, P; Rigaud, A

    1959-07-01

    After a brief summary of the physical and chemical properties of beryllium, the various chemical treatments which can be applied to beryllium minerals either directly or after a physical enrichment are discussed. These various treatments give either the hydroxide or beryllium salts, from which either beryllium oxide or metallic beryllium can easily be obtained. The purification, analysis and uses of beryllium are also briefly discussed. (author)

  16. Beryllium R and D for fusion applications

    International Nuclear Information System (INIS)

    Scaffidi-Argentina, F.; Longhurst, G.R.; Shestakov, V.; Kawamura, H.

    2000-01-01

    Beryllium is one of the primary candidates as both plasma-facing material (PFM) and neutron multiplier in the next-step fusion reactors. Both sintered-product blocks and pebbles are considered in fusion reactor designs. Beryllium evaporated on carbon tiles has also been used in Joint European Torus (JET) and may be considered for other designs. Future efforts are directed toward the pebble form of beryllium. Research and evaluations of data are underway to determine the most attractive material processing approaches in terms of fabrication cost and quality; technical issues associated with heat transfer; thermal, mechanical and irradiation stability; safety and tritium release. Beryllium plasma-facing components will require periodic repair or replacement, therefore disposal or recycling of activated and tritiated beryllium will also be a concern. Beryllium as a component of the molten salt, Flibe is also being considered in novel approaches to the plasma-structure interface. This paper deals with the main issues related to the use of Be in a fusion reactor as both neutron multiplier and first wall material. These issues include potential reactions with steam during accidents and the health and environmental aspects of its use, reprocessing and reuse, or disposal

  17. Beryllium R and D for fusion applications

    Energy Technology Data Exchange (ETDEWEB)

    Scaffidi-Argentina, F. E-mail: francesco.scaffidi@iket.fzk.de; Longhurst, G.R.; Shestakov, V.; Kawamura, H

    2000-11-01

    Beryllium is one of the primary candidates as both plasma-facing material (PFM) and neutron multiplier in the next-step fusion reactors. Both sintered-product blocks and pebbles are considered in fusion reactor designs. Beryllium evaporated on carbon tiles has also been used in Joint European Torus (JET) and may be considered for other designs. Future efforts are directed toward the pebble form of beryllium. Research and evaluations of data are underway to determine the most attractive material processing approaches in terms of fabrication cost and quality; technical issues associated with heat transfer; thermal, mechanical and irradiation stability; safety and tritium release. Beryllium plasma-facing components will require periodic repair or replacement, therefore disposal or recycling of activated and tritiated beryllium will also be a concern. Beryllium as a component of the molten salt, Flibe is also being considered in novel approaches to the plasma-structure interface. This paper deals with the main issues related to the use of Be in a fusion reactor as both neutron multiplier and first wall material. These issues include potential reactions with steam during accidents and the health and environmental aspects of its use, reprocessing and reuse, or disposal.

  18. Elastic wave from fast heavy ion irradiation on solids

    CERN Document Server

    Kambara, T; Kanai, Y; Kojima, T M; Nanai, Y; Yoneda, A; Yamazaki, Y

    2002-01-01

    To study the time-dependent mechanical effects of fast heavy ion irradiations, we have irradiated various solids by a short-bunch beam of 95 MeV/u Ar ions and observed elastic waves generated in the bulk. The irradiated targets were square-shaped plates of poly-crystals of metals (Al and Cu), invar alloy, ceramic (Al sub 2 O sub 3), fused silica (SiO sub 2) and single crystals of KC1 and LiF with a thickness of 10 mm. The beam was incident perpendicular to the surface and all ions were stopped in the target. Two piezo-electric ultrasonic sensors were attached to the surface of the target and detected the elastic waves. The elastic waveforms as well as the time structure and intensity of the beam bunch were recorded for each shot of a beam bunch. The sensor placed opposite to the beam spot recorded a clear waveform of the longitudinal wave across the material, except for the invar and fused silica targets. From its propagation time along with the sound velocity and the thickness of the target, the depth of the...

  19. Effect of transient heating loads on beryllium

    International Nuclear Information System (INIS)

    Kupriyanov, Igor B.; Porezanov, Nicolay P.; Nikolaev, Georgyi N.; Kurbatova, Liudmila A.; Podkovyrov, Vyacheslav L.; Muzichenko, Anatoliy D.; Zhitlukhin, Anatoliy M.; Khimchenko, Leonid N.; Gervash, Alexander A.

    2014-01-01

    Highlights: • We study the effect of transient plasma loads on beryllium erosion and surface microstructure. • Beryllium targets were irradiated by plasma streams with energy of 0.5–1 MJ/m 2 at ∼250 °C. • Under plasma loads 0.5–1 MJ/m 2 cracking of beryllium surface is rather slight. • Under 0.5 MJ/m 2 the mass loss of Be is no more than 0.2 g/m 2 shot and decreasing with shots number. • Under 1 MJ/m 2 maximum mass loss of beryllium was 3.7 g/m 2 shot and decreasing with shots number. - Abstract: Beryllium will be used as a plasma facing material for ITER first wall. It is expected that erosion of beryllium under transient plasma loads such as the edge-localized modes (ELMs) and disruptions will mainly determine a lifetime of ITER first wall. The results of recent experiments with the Russian beryllium of TGP-56FW ITER grade on QSPA-Be plasma gun facility are presented. The Be/CuCrZr mock-ups were exposed to upto 100 shots by deuterium plasma streams with pulse duration of 0.5 ms at ∼250 °C and average heat loads of 0.5 and 1 MJ/m 2 . Experiments were performed at 250 °C. The evolution of surface microstructure and cracks morphology as well as beryllium mass loss are investigated under erosion process

  20. Extractive metallurgy of the beryllium

    International Nuclear Information System (INIS)

    Alonso, Neusa; Capocchi, Jose Deodoro Trani

    1995-01-01

    A bibliographic review is performed on the beryllium extractive metallurgy. The work describes the main type of ores and processes applied to the metallic beryllium production, beryllium oxide production using fluoride, sulfide and direct chlorination. The thermodynamic consideration are made on beryllium reduction processes, discussing the viability of the beryllium oxide and hallide reduction processes. Under the technological viewpoint, the Cu-Be alloys main production processes are discussed, and the main toxicity problems related with beryllium are mentioned

  1. Thermogravimetric analysis of the beryllium/steam reaction

    Energy Technology Data Exchange (ETDEWEB)

    Druyts, Frank E-mail: fdruyts@sckcen.be; Iseghem, Pierre van

    2000-11-01

    In view of the safety assessment of new fusion reactor designs, kinetic data are needed on the beryllium/steam reaction. Therefore, thermogravimetric analysis was used to determine the reactivity of beryllium in steam as a function of temperature, irradiation history and porosity of the samples. To this purpose, reference unirradiated S-200 VHP beryllium samples were compared with specimens irradiated in the BR2 reactor up to fast neutron fluences (E>1 MeV) of respectively 1.6x10{sup 21} n cm{sup -2} (resulting in a helium content of 300 appm He and a theoretical density of 99.9%) and 4x10{sup 22} n cm{sup -2} (21000 appm He, 97.2% theoretical density). Kinetics were parabolic for all tested beryllium types at 600 deg. C. At 700 deg. C, kinetics were parabolic for the unirradiated and irradiated 99.9% dense beryllium, and accelerating/linear for the irradiated 97.2% material. At 800 deg. C, all samples showed accelerating/linear behaviour. There was no influence of porosity on the reaction rate of beryllium in steam within the limited investigated density range, except at 700 deg. C, where the measured reaction rate for the irradiated 97.2% dense samples is an order of magnitude higher than for the irradiated 99.9% dense specimens.

  2. 5. IEA International workshop on beryllium technology for fusion. Book of abstracts

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    2001-07-01

    The collection includes the abstracts of reports presented to the 5-th IEA international workshop on beryllium technology for fusion. The themes of reports are as follows: status of beryllium technology for fusion in Russia; manufacturing and testing of Be armoured first wall mock-up for ITER; development of the process of diffusion welding of metals stainless steel-copper-beryllium into a single composite; some features of beryllium-laser beam interaction; the effect of irradiation dose on tritium and helium release from neutron irradiated beryllium; thermal properties of neutron irradiated Be{sub 12}Ti. The results of investigating the mechanical properties variation and swelling of beryllium under high temperature neutron irradiation are presented.

  3. 5. IEA International workshop on beryllium technology for fusion. Book of abstracts

    International Nuclear Information System (INIS)

    2001-01-01

    The collection includes the abstracts of reports presented to the 5-th IEA international workshop on beryllium technology for fusion. The themes of reports are as follows: status of beryllium technology for fusion in Russia; manufacturing and testing of Be armoured first wall mock-up for ITER; development of the process of diffusion welding of metals stainless steel-copper-beryllium into a single composite; some features of beryllium-laser beam interaction; the effect of irradiation dose on tritium and helium release from neutron irradiated beryllium; thermal properties of neutron irradiated Be 12 Ti. The results of investigating the mechanical properties variation and swelling of beryllium under high temperature neutron irradiation are presented [ru

  4. Tritium behavior in ITER beryllium

    International Nuclear Information System (INIS)

    Longhurst, G.R.

    1990-10-01

    The beryllium neutron multiplier in the ITER breeding blanket will generate tritium through transmutations. That tritium constitutes a safety hazard. Experiments evaluating tritium storage and release mechanisms have shown that most of the tritium comes out in a burst during thermal ramping. A small fraction of retained tritium is released by thermally activated processes. Analysis of recent experimental data shows that most of the tritium resides in helium bubbles. That tritium is released when the bubbles undergo swelling sufficient to develop porosity that connects with the surface. That appears to occur when swelling reaches about 10--15%. Other tritium appears to be stored chemically at oxide inclusions, probably as Be(OT) 2 . That component is released by thermal activation. There is considerable variation in published values for tritium diffusion through the beryllium and solubility in it. Data from experiments using highly irradiated beryllium from the Idaho National Engineering Laboratory showed diffusivity generally in line with the most commonly accepted values for fully dense material. Lower density material, planned for use in the ITER blanket may have very short diffusion times because of the open structure. The beryllium multiplier of the ITER breeding blanket was analyzed for tritium release characteristics using temperature and helium production figures at the midplane generated in support of the ITER Summer Workshop, 1990 in Garching. Ordinary operation, either in Physics or Technology phases, should not result in the release of tritium trapped in the helium bubbles. Temperature excursions above 600 degree C result in large-scale release of that tritium. 29 refs., 10 figs., 3 tabs

  5. Behavior of solid fission products in irradiated fuel

    International Nuclear Information System (INIS)

    Song, Ung Sup; Jung, Yang Hong; Kim, Hee Moon; Yoo, Byun Gok; Kim, Do Sik; Choo, Yong Sun; Hong, Kwon Pyo

    2004-01-01

    Many fission products are generated by fission events in UO 2 fuel under irradiation in nuclear reactor. Concentration of each fission product is changed by conditions of neutron energy spectrum, fissile material, critical thermal power, irradiation period and cooling time. Volatile materials such as Cs and I, the fission products, degrade nuclear fuel rod by the decrease of thermal conductivity in pellet and the stress corrosion cracking in cladding. Metal fission products (white inclusion) make pellet be swelled and decrease volume of pellet by densification. It seems that metal fission products are filled in the pore in pellet and placed between UO 2 lattices as interstitial. In addition, metal oxide state may change structural lattice volume. Considering behavior of fission products mentioned above, concentration of them is important. Fission products could be classified as bellows; solid solution in matrix : Sr, Zr, Nb, Y, La, Ce, Pr, Nd, Pm, Sm - metal precipitates : Mo, Tc, Ru, Rh, Pd, Ag, Cd, In, Sb, Te - oxide precipitates : Ba, Zr, Nb, Mo, (Rb, Cs, Te) - volatile and gases : Kr, Xe, Br, I, (Rb, Cs, Te)

  6. Postirradiation examination of beryllium pebbles

    International Nuclear Information System (INIS)

    Gelles, D.S.

    1998-01-01

    Postirradiation examinations of COBRA-1A beryllium pebbles irradiated in the EBR-II fast reactor at neutron fluences which generated 2700--3700 appm helium have been performed. Measurements included density change, optical microscopy, scanning electron microscopy, and transmission electron microscopy. The major change in microstructure is development of unusually shaped helium bubbles forming as highly non-equiaxed thin platelet-like cavities on the basal plane. Measurement of the swelling due to cavity formation was in good agreement with density change measurements

  7. Status of beryllium study for fusion in RF

    International Nuclear Information System (INIS)

    Khomutov, A.M.; Kupriyanov, I.B.; Markushkin, Yu.E.; Gervash, A.; Kolbasov, B.N.

    2004-01-01

    The main directions of research activities in the field of beryllium application science and technology carried out in Russia during 2001-2003 have been reviewed. The main results of these investigations have been highlighted. First wall and port-limier. The investigation on the actively cooled components with beryllium cladding is under progress objecting on the clarification of their ultimate thermo cycling capabilities. The study of behavior of bulk beryllium and the boundary region of the contact with the cooling structure under the intensive thermo cycling loading and neutron irradiation have been the object of consideration in particular. The works on the optimization and modification of industrial fabrication processes for commercial scaled production of beryllium tile were also under way. The influence of neutron irradiation. The new experimental data on the nuclear properties of several Russian beryllium grades has been obtained. The samples have been subjected to the high neutron dozes. The influence of low temperature (70-200degree C) neutron irradiation on the thermal conductivity has been examined in particular. The interrelations of the helium inventory and temperature of neutron irradiation with tritium release out of irradiated beryllium samples have been analyzed. The beryllium associated safety questions. The experiments on the modeling of normal working conditions and conditions imitating the plasma disruption events in ITER performance scenario have been continued. The new experimental information on the coefficient of pulverization of beryllium and the accumulation of deuterium in beryllium under the action of proton beam has been collected. The dependence of the reaction rate constant for the beryllium oxidation by the water vapor for different conditions has been analyzed. The compact, porous and powder beryllium samples have been tested at the wide range of temperature, pressure and duration of reaction with water vapor. The calculating

  8. METHOD OF BRAZING BERYLLIUM

    Science.gov (United States)

    Hanks, G.S.; Keil, R.W.

    1963-05-21

    A process is described for brazing beryllium metal parts by coating the beryllium with silver (65- 75 wt%)-aluminum alloy using a lithium fluoride (50 wt%)-lithium chloride flux, and heating the coated joint to a temperature of about 700 un. Concent 85% C for about 10 minutes. (AEC)

  9. Preparation of beryllium hydride

    International Nuclear Information System (INIS)

    Roberts, C.B.

    1975-01-01

    A process is described for preparing beryllium hydride by the direct reaction of beryllium borohydride and aluminum hydride trimethylamine adduct. Volatile by-products and unreacted reactants are readily removed from the product mass by sublimation and/or evaporation. (U.S.)

  10. Structural changes of organic solids caused by irradiation: raman study at very low temperatures

    International Nuclear Information System (INIS)

    Hase, Hirotomo; Ishioka, Kunie; Miyatake, Yoko.

    1995-01-01

    In this paper we first describe a simple liquid helium cryostat and a device of making and mounting organic solid samples. We then present the Raman spectra for irradiated ethanol crystal that were obtained by using the new cryostat and demonstrate how the Raman method is useful for getting insight into structural changes of organic solids caused by irradiation. (J.P.N.)

  11. Thermal Effects Induced by Laser Irradiation of Solids

    International Nuclear Information System (INIS)

    Galovic, S.

    2004-01-01

    A part of incident energy is absorbed within the irradiated sample when a solid is exposed to the influence of laser radiation, to more general electromagnetic radiation within the wide range of wavelengths (from microwaves, to infrared radiation to X-rays), or to the energy of particle beams (electronic, protonic, or ionic). The absorption process signifies a highly selective excitation of the electronic state of atoms or molecules, followed by thermal and non-thermal de-excitation processes. Non-radiation de-excitation-relaxation processes induce direct sample heating. In addition, a great number of non-thermal processes (e.g., photoluminescence, photochemistry, photovoltage) may also induce heat generation as a secondary process. This method of producing heat is called the photothermal effect.The photothermal effect and subsequent propagation of thermal waves on the surface and in the volume of the solid absorbing the exciting beam may produce the following: variations in the temperature on the surfaces of the sample; deformation and displacement of surfaces; secondary infrared radiation (photothermal radiation); the formation of the gradient of the refractivity index; changes in coefficients of reflection and absorbtion; the generation of sound (photoacoustic generation), etc. These phenomena may be used in the investigation and measurement of various material properties since the profile and magnitude of the generated signal depend upon the nature of material absorbing radiation. A series of non-destructive spectroscopic, microscopic and defectoscopic detecting techniques, called photothermal methods, is developed on the basis of the above-mentioned phenomena.This paper outlines the interaction between the intensity modulated laser beam and solids, and presents a mathematical model of generated thermal sources. Generalized models for a photothermal response of optically excited materials have been obtained, including thermal memory influence on the propagation

  12. Recovery of uranium from an irradiated solid target after removal of molybdenum-99 produced from the irradiated target

    Science.gov (United States)

    Reilly, Sean Douglas; May, Iain; Copping, Roy; Dale, Gregory Edward

    2017-10-17

    A process for minimizing waste and maximizing utilization of uranium involves recovering uranium from an irradiated solid target after separating the medical isotope product, molybdenum-99, produced from the irradiated target. The process includes irradiating a solid target comprising uranium to produce fission products comprising molybdenum-99, and thereafter dissolving the target and conditioning the solution to prepare an aqueous nitric acid solution containing irradiated uranium. The acidic solution is then contacted with a solid sorbent whereby molybdenum-99 remains adsorbed to the sorbent for subsequent recovery. The uranium passes through the sorbent. The concentrations of acid and uranium are then adjusted to concentrations suitable for crystallization of uranyl nitrate hydrates. After inducing the crystallization, the uranyl nitrate hydrates are separated from a supernatant. The process results in the purification of uranyl nitrate hydrates from fission products and other contaminants. The uranium is therefore available for reuse, storage, or disposal.

  13. Experience of beryllium blocks operation in the SM and MIR nuclear reactors useful for fusion

    International Nuclear Information System (INIS)

    Chakin, V.P.; Melder, R.R.; Belozerov, S.V.

    2004-01-01

    The results are presented concerning the examinations of state of beryllium blocks after the completion of their operation in the SM and MIR reactors. Both cracks and more significant mechanical damages are revealed in the irradiated beryllium blocks. Under neutron irradiation of beryllium radiation degradation of its physical and mechanical properties occurs. It shows itself in embrittlement, decrease of brittle strength level as well in worsening of thermal conductivity that leads to increase of thermal stresses into beryllium block. Under irradiation it takes place damage of beryllium microstructure, in particular, formation of radiation defects occurs in the form of dislocation loops and great amount of helium atoms. Optimization of beryllium radioactive waste storage is related to their preliminary surface and volumetric decontamination. (author)

  14. Corrosion of beryllium

    International Nuclear Information System (INIS)

    Mueller, J.J.; Adolphson, D.R.

    1987-01-01

    The corrosion behavior of beryllium in aqueous and elevated-temperature oxidizing environments has been extensively studied for early-intended use of beryllium in nuclear reactors and in jet and rocket propulsion systems. Since that time, beryllium has been used as a structural material in les corrosive environments. Its primary applications include gyro systems, mirror and reentry vehicle structures, and aircraft brakes. Only a small amount of information has been published that is directly related to the evaluation of beryllium for service in the less severe or normal atmospheric environments associated with these applications. Despite the lack of published data on the corrosion of beryllium in atmospheric environments, much can be deduced about its corrosion behavior from studies of aqueous corrosion and the experiences of fabricators and users in applying, handling, processing, storing, and shipping beryllium components. The methods of corrosion protection implemented to resist water and high-temperature gaseous environments provide useful information on methods that can be applied to protect beryllium for service in future long-term structural applications

  15. Beryllium poisonings; Les intoxications par le beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Alibert, S.

    1959-03-15

    This note reports a bibliographical study of beryllium toxicity. Thus, this bibliographical review addresses and outlines aspects and issues like aetiology, cases of acute poisoning (cutaneous manifestations, pulmonary manifestations), chronic poisoning (cutaneous, pulmonary and bone manifestations), excretion and localisation, and prognosis.

  16. Study beryllium microplastic deformation

    International Nuclear Information System (INIS)

    Papirov, I.I.; Ivantsov, V.I.; Nikolaenko, A.A.; Shokurov, V.S.; Tuzov, Yu.V.

    2015-01-01

    Microplastic flow characteristics systematically studied for different varieties beryllium. In isostatically pressed beryllium it decreased with increasing particle size of the powder, increasing temperature and increasing the pressing metal purity. High initial values of the limit microelasticity and microflow in some cases are due a high level of internal stresses of thermal origin and over time it can relax slowly. During long-term storage of beryllium materials with high initial resistance values microplastic deformation microflow limit and microflow stress markedly reduced, due mainly to the relaxation of thermal microstrain

  17. Preparation of beryllium hydride

    International Nuclear Information System (INIS)

    Lowrance, B.R.

    1975-01-01

    A process is described for the preparation of beryllium hydride which comprises pyrolyzing, while in solution in a solvent inert under the reaction conditions, with respect to reactants and products and at a temperature in the range of about 100 0 to about 200 0 C, sufficient to result in the formation of beryllium hydride, a di-t-alkyl beryllium etherate wherein each tertiary alkyl radical contains from 4 to 20 carbon atoms. The pyrolysis is carried out under an atmosphere inert under the reaction conditions, with respect to reactants and products. (U.S.)

  18. Thermodynamic Calculation of the Distribution Coefficient Between the Liquid and Solid Phases of an Element in Dilute Solution in a Metal: Application to the Purification of Beryllium; Calcul Thermodynamique du Coefficient de Distribution Entre Phases Liquide et Solide d'un Element en Presence d'Autres Constituants en Solution Diluee dans un Metal: Application a la Purification du Beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Desre, P. [Ecole Nationale Superieure d' Electrochimie et d' Electrometallurgie (France); Schaub, B. [Centre d' Etudes Nucleaires de Grenoble (France); Bonnier, I. E. [Ecole Nationale Superieure d' Electrochimie et d' Electrometallurgie, Grenoble (France)

    1966-01-15

    The authors calculate the distribution coefficient {Gamma}{sub i} between the liquid and solid phases of an element i in the presence of other elements j in a solvent M ({Gamma}{sub i} = x'{sub i}/x{sub i}, where x'{sub i} and x{sub i} are the atomic fractions of i in the solid and liquid phases respectively) from the thermodynamic properties of binary systems of the type (i, M), (j, M) and (i, j). They show that the interaction of all the elements present may, under certain conditions, strongly affect the value of the coefficient {Gamma}{sub i}. This effect is pronounced if the following condition is fulfilled: {gamma}{sup {infinity}}{sub i(M)}, {gamma}{sup {infinity}}{sub j(M)} > {gamma}{sup {infinity}}{sub ij} where {gamma}{sup {infinity}}{sub i(M)}, {gamma}{sup {infinity}}{sub j(M)} and {gamma}{sup {infinity}}{sub ij} are limiting activity coefficients of the constituents i and j in the (i, M) (j, M) and (i, j) liquid state systems. It is a simple matter to deduce from this condition an application to the purification of metals by the zone-melting method; the condition enables one to choose an element j which is added deliberately to a metal in order to facilitate the elimination-of an element i (subsequent elimination of the element j being also, of course, a simple matter). For example, the authors were able to confirm that the addition of aluminium to beryllium enables one to improve the elimination of iron during the purification of the beryllium by the zone-melting technique, the aluminium acting as a carrier. (author) [French] Les auteurs calculent le coefficient de distribution Greek-Capital-Letter-Gamma {sub i} entre phases liquide et solide d'un element i en presence d'autres elements j dans un solvant M ( Greek-Capital-Letter-Gamma {sub i} = x'{sub i}/x{sub i}, x'{sub i} et x{sub i} representant respectivement les fractions atomiques de i dans les phases solide et liquide), a partir des proprietes thermodynamiques des systemes binaires de type: (i, M

  19. Beryllium and copper-beryllium alloys; Beryllium und Kupfer-Beryllium-Legierungen

    Energy Technology Data Exchange (ETDEWEB)

    Nagel, Nikolaus [Materion Brush GmbH, Stuttgart (Germany). Operation and Quality/EH and S

    2017-02-15

    The light metal beryllium is a comparatively rare element, which today is primarily derived from bertrandite. It is mainly used as pure metal or in the form of copper-beryllium alloys, e.g., in automotive industry, aerospace, and electrical components. The wide range of applications is mainly attributed to the extremely high rigidity/density ratio. An overview of the history of the metal, its production, and recycling as well as the properties of CuBe alloys are given.

  20. The immunotoxicity of beryllium

    International Nuclear Information System (INIS)

    Reeves, A.L.

    1983-01-01

    In the disease berylliosis, granulomatous hypersensitivity is the specific immune response to tissue contact with a poorly soluble particle of beryllium compound, mediated through the accumulation and proliferation of reticuloendothelial cells. A review is given of the work accomplished since the 1950's and particularly since the 1970's to elucidate the nature and consequences of this response to beryllium and its compounds. (U.K.)

  1. Preparation of beryllium hydride

    International Nuclear Information System (INIS)

    Bergeron, C.R.; Baker, R.W.

    1975-01-01

    Beryllium hydride of high bulk density, suitable for use as a component of high-energy fuels, is prepared by the pyrolysis, in solution in an inert solvent, of a ditertiary-alkyl beryllium. An agitator introduces mechanical energy into the reaction system, during the pyrolysis, at the rate of 0.002 to 0.30 horsepower per gallon of reaction mixture. (U.S.)

  2. Studies on rate equations for defects in irradiated solids using the local analysis method

    International Nuclear Information System (INIS)

    Carvalho e Camargo, M.U. de.

    1983-10-01

    The void formation and swelling phenomenon in material for nuclear reactors structures, mainly for fast reactors, has been studied by several authors. A simple calculation covering the basic instance of radiation damage in irradiated solid solution, using the local analysis in rate theory is presented here. A simple description of pratical and fundamental interest for the complex problem of solid solution under irradiation is given. (Author) [pt

  3. Movement of liquid beryllium during melt events in JET with ITER-like wall

    International Nuclear Information System (INIS)

    Sergienko, G; Huber, A; Brezinsek, S; Coenen, J W; Mertens, Ph; Philipps, V; Samm, U; Arnoux, G; Matthews, G F; Nunes, I; Riccardo, V; Sirinelli, A; Devaux, S

    2014-01-01

    The ITER-like wall recently installed in JET comprises solid beryllium limiters and a combination of bulk tungsten and tungsten-coated carbon fibre composite divertor tiles without active cooling. During a beryllium power handling qualification experiment performed in limiter configuration with 5 MW neutral beam injection input power, accidental beryllium melt events, melt layer motion and splashing were observed locally on a few beryllium limiters in the plasma contact areas. The Lorentz force is responsible for the observed melt layer movement. To move liquid beryllium against the gravity force, the current flowing from the plasma perpendicularly to the limiter surface must be higher than 6 kA m −2 . The thermo-emission current at the melting point of beryllium is much lower. The upward motion of the liquid beryllium against gravity can be due to a combination of the Lorentz force from the secondary electron emission and plasma pressure force. (paper)

  4. Ion beam assisted deposition of metal-coatings on beryllium

    International Nuclear Information System (INIS)

    Tashlykov, I.S.; Tul'ev, V.V.

    2015-01-01

    Thin films were applied on beryllium substrates on the basis of metals (Cr, Ti, Cu and W) with method of the ion-assisted deposition in vacuum. Me/Be structures were prepared using 20 kV ions irradiation during deposition on beryllium neutral fraction generated from vacuum arc plasma. Rutherford back scattering and computer simulation RUMP code were applied to investigate the composition of the modified beryllium surface. Researches showed that the superficial structure is formed on beryllium by thickness ~ 50-60 nm. The covering composition includes atoms of the deposited metal (0.5-3.3 at. %), atoms of technological impurity carbon (0.8-1.8 at. %) and oxygen (6.3-9.9 at. %), atoms of beryllium from the substrate. Ion assisted deposition of metals on beryllium substrate is accompanied by radiation enhanced diffusion of metals, oxygen atoms in the substrate, out diffusion of beryllium, carbon atoms in the deposited coating and sputtering film-forming ions assists. (authors)

  5. Neutron induced displacement damage in beryllium in the blanket of a (d,t)-fusion reactor

    International Nuclear Information System (INIS)

    Hermanutz, D.

    1995-09-01

    Beryllium is a favoured candidate for a neutron multiplier in solid breeder blankets of fusion reactors. This is mainly due to its low (n, 2n)-reaction threshold and because of its good thermal and mechanical properties. Its behaviour under intense neutron irradiation, however, is a crucial issue for its use in future fusion reactors. Displacement damage in beryllium so far has been calculated both with data related and methodological deficiencies. First of all, there is a need to have accurate cross-section data in order to obtain reliable spectra of primary knock-on atoms (PKA's). Furthermore, there are principal restrictions of the NRT-model in general used to calculate secondary displacements initiated by PKA's. The underlying theory of damage-energy (part of kinetic energy of PKA transferred elastically to matrix atoms) according to Lindhard is strictly valid only for medium and heavy mass ions with moderate energies in targets of the same element. In this work improved damage cross-sections and displacement rates (dpa/s) in beryllium have been calculated based on cross-section data from ENDF/B-VI (with a significantly improved (n, 2n)-evaluation) and on an appropriate treatment of damage-energy that is suitable for fusion relevant damage of light mass materials. ''This work has been performed in the framework of the Nuclear Fusion Project of the Forschungszentrum Karlsruhe and is supported by the European Communities within the European Fusion Technology Program''. (orig.)

  6. Assessment of the feasibility and advantages of beryllium recycling

    International Nuclear Information System (INIS)

    Druyts, F.; Braet, J.; Ooms, L.

    2006-01-01

    This paper proposes a generic route for the recycling of beryllium from fusion reactors, based on critical issues associated with beryllium pebbles after their service life in the HCPB breeding blanket. These critical issues are the high tritium inventory, the presence of long-lived radionuclides (among which transuranics due to traces of uranium in the base metal), and the chemical toxicity of beryllium. On the basis of the chemical and radiochemical characteristics of the neutron irradiated beryllium pebbles, we describe a possible recycling route. The first step is the detritiation of the material. This can be achieved by heating the pebbles to 800 o C under an argon flow. The argon gas avoids oxidation of the beryllium, and at the proposed temperature the tritium inventory is readily released from the pebbles. In a second step, the released tritium can be oxidised on a copper oxide bed to produce tritiated water, which is consistent with the current international strategy to convert all kinds of tritiated waste into tritiated water, which can subsequently be treated in a water detritiation plant. Removal of radionuclides from the beryllium pebbles may be achieved by several types of chloride processes. The first step is to pass chlorine gas (in an argon flow) over the pebbles, thus yielding volatile BeCl 2 . This beryllium chloride can then be purified by fractional distillation. As a small fraction of the beryllium chloride contains the long-lived 10 Be isotope, 10BeCl 2 has to be separated from 9BeCl 2 , which could be achieved by centrifugal techniques. The product can then be reduced to obtain high-purity metallic beryllium. Two candidate reduction methods were identified: fused salt electrolysis and thermal decomposition. Both these methods require laboratory parametric studies to maximise the yield and achieve a high purity metal, before either process can be upgraded to a larger scale. The eventual product of the chloride reduction process must be a high

  7. Effect of gamma irradiation on cefotaxime in the solid state

    Energy Technology Data Exchange (ETDEWEB)

    Zegota, H.; Koprowski, M.; Zegota, A. [Technical Univ., Lodz (Poland). Inst. of Applied Radiation Chemistry

    1995-02-01

    The effect of {gamma}-irradiation on cefotaxime, a member of the third generation of cephalosporins, has been investigated by using different spectroscopic, chromatographic and microbiological analytical methods. Cefotaxime sodium salt was irradiated in dry state in the range of sterilization doses from 5.85 to 46.8 kGy. According to the results obtained, the degree of cefotaxime alterations was lower than 1%, even for the higher radiation dose used. Trace amounts of antibiotic radiolysis products have been found by HPLC. The microbiological assay carried out using E. coli test strain reveal that the activity of irradiated cefotaxime did not decrease. (author).

  8. Sintering of beryllium oxide

    International Nuclear Information System (INIS)

    Caillat, R.; Pointud, R.

    1955-01-01

    This study had for origin to find a process permitting to manufacture bricks of beryllium oxide of pure nuclear grade, with a density as elevated as possible and with standardized shape. The sintering under load was the technique kept for the manufacture of the bricks. Because of the important toxicity of the beryllium oxide, the general features for the preliminary study of the sintering, have been determined while using alumina. The obtained results will be able to act as general indication for ulterior studies with sintering under load. (M.B.) [fr

  9. A low temperature cryostat with a refrigerator for studying electron irradiation effects on solids

    International Nuclear Information System (INIS)

    Oka, Takashi; Yoshida, Toshio; Kitagawa, Michiharu; Yanai, Masayoshi

    1976-01-01

    A low temperature cryostat with a small cryogenic refrigerator is described which is convenient for studying irradiation effects of the energetic electrons on solids. It allows a sample to be kept about 12 K without irradiation and 15 K under the irradiation at a heating rate of 1.5 w. The sample temperature can be changed up to room temperature by adjusting the power of an attached heater and the pressure of a compressor for the refrigerator. The optical and electrical properties of the sample can be measured under and after irradiation. (auth.)

  10. Stability of cefuroxime following gamma-irradiation in the solid state

    International Nuclear Information System (INIS)

    Zegota, Henryk; Koprowski, Marek; Zegota, Alicja

    1994-01-01

    The effect of γ-irradiation on cefuroxime, a member of the second generation of cephalosporins, has been assessed by different spectroscopic, HPLC, chemical and microbiological analytical methods. According to the results obtained, the chemical changes in irradiated cefuroxime have relatively low yield. The microbiological assay carried out using Bacillus subtilis test strain reveal that the activity of irradiated cefuroxime did not decrease even for radiation doses as high as 85 kGy. The remarkable radiation stability of cefuroxime irradiated in the solid state supports its suitability for radiation sterilization. (author)

  11. Stability of cefuroxime following gamma-irradiation in the solid state

    Energy Technology Data Exchange (ETDEWEB)

    Zegota, Henryk; Koprowski, Marek; Zegota, Alicja (Politechnika Lodzka, Lodz (Poland). Katedra Chemii Radiacyjnej)

    1994-04-01

    The effect of [gamma]-irradiation on cefuroxime, a member of the second generation of cephalosporins, has been assessed by different spectroscopic, HPLC, chemical and microbiological analytical methods. According to the results obtained, the chemical changes in irradiated cefuroxime have relatively low yield. The microbiological assay carried out using Bacillus subtilis test strain reveal that the activity of irradiated cefuroxime did not decrease even for radiation doses as high as 85 kGy. The remarkable radiation stability of cefuroxime irradiated in the solid state supports its suitability for radiation sterilization. (author).

  12. Reduction of surface erosion caused by helium blistering in sintered beryllium and sintered aluminum powder

    International Nuclear Information System (INIS)

    Das, S.K.; Kaminsky, M.

    1976-01-01

    Studies have been conducted to find materials with microstructures which minimize the formation of blisters. A promising class of materials appears to be sintered metal powder with small average grain sizes and low atomic number Z. Studies of the surface erosion of sintered aluminum powder (SAP 895) and of aluminum held at 400 0 C due to blistering by 100 keV helium ions have been conducted and the results are compared to those obtained earlier for room temperature irradiation. A significant reduction of the erosion rate in SAP 895 in comparison to annealed aluminum and SAP 930 is observed. In addition results on the blistering of sintered beryllium powder (type I) irradiated at room temperature and 600 0 C by 100 keV helium ions are given. These results will be compared with those reported recently for vacuum cast beryllium foil and a foil of sintered beryllium powder (type II) which was fabricated differently, than type I. For room temperature irradiation only a few blisters could be observed in sintered beryllium powder type I and type II and they are smaller in size and in number than in vacuum cast beryllium. For irradiation at 600 0 C large scale exfoliation of blisters was observed for vacuum cast beryllium but much less exfoliation was seen for sintered beryllium powder, type I, and type II. The results show a reduction in erosion rate cast beryllium, for both room temperature and 600 0 C

  13. Workshop on beryllium for fusion applications. Proceedings. IEA Implementing Agreement for a Programme of Research and Development on Fusion Materials

    International Nuclear Information System (INIS)

    Dalle Donne, M.

    1993-12-01

    As shown by recent developments beryllium has become one of the most important materials in the development of fusion reactors. It is practically the only neutron multiplier available for blankets with ceramic breeder materials and can be used with liquid metal breeders as well. It is one of the most likely materials to be used on the surface of the first walls and of the divertor. The neutron irradiation behavior of beryllium in a fusion reactor is not well know. Beryllium was extensively irradiated about 25-40 years ago and has been used since then in material testing reactors as reflector. In the meantime, however, beryllium has been improved quite considerably. Today it is possible to obtain commercially beryllium which is much more isotropic and contains smaller ammounts of oxide. There are already indications that these new kinds of beryllium behave better under irradiation. (orig.)

  14. Measurement and calculation of neutron leakage spectra from slab samples of beryllium, gallium and tungsten irradiated with 14.8 MeV neutrons

    Science.gov (United States)

    Nie, Y. B.; Ruan, X. C.; Ren, J.; Zhang, S.; Han, R.; Bao, J.; Huang, H. X.; Ding, Y. Y.; Wu, H. C.; Liu, P.; Zhou, Z. Y.

    2017-09-01

    In order to make benchmark validation of the nuclear data for gallium (Ga), tungsten (W) and beryllium (Be) in existing modern evaluated nuclear data files, neutron leakage spectra in the range from 0.8 to 15 MeV from slab samples were measured by time-of-flight technique with a BC501 scintillation detector. The measurements were performed at China Institute of Atomic Energy (CIAE) using a D-T neutron source. The thicknesses of the slabs were 0.5 to 2.5 mean free path for 14.8 MeV neutrons, and the measured angles were chosen to be 60∘ and 120∘. The measured spectra were compared with those calculated by the continuous energy Monte-Carlo transport code MCNP, using the data from the CENDL-3.1, ENDF/B-VII.1 and JENDL-4.0 nuclear data files, the comparison between the experimental and calculated results show that: The results from all three libraries significantly underestimate the cross section in energy range of 10-13 MeV for Ga; For W, the calculated spectra using data from CENDL-3.1 and JENDL-4.0 libraries show larger discrepancies with the measured ones, especially around 8.5-13.5 MeV; and for Be, all the libraries led to underestimation below 3 MeV at 120∘.

  15. Measurement and calculation of radiation fields of the Sandia irradiator for dried sewage solids

    International Nuclear Information System (INIS)

    Morris, M.E.

    1981-03-01

    The radiation field of the Sandia Irradiator for Dried Sewage Solids was measured. The results of the measurement are given in this report. In addition, theoretical calculations of the fields are given and then compared with the measured values. Elementary models of the radiation source geometry and irradiated product are found to be adequate and thus allow us to duplicate (through calculation) the important features of the measured fields

  16. Dried gamma-irradiated sewage solids use on calcareous soils: crop yields and heavy metals uptake

    International Nuclear Information System (INIS)

    McCaslin, B.D.; Sivinski, J.S.

    1980-01-01

    The fertilizer values of gamma-irradiated digested sewage solids (RDSS) and gamma-irradiated undigested sewage solids (RUSS) have been examined on calcareous soils. Previously published data from Sandia Laboratories have shown that approximately 1 mega-rad of gamma-irradiation effectively destroys pathogenic bacteria, parasites and plant seeds in dried sewage solids. Greenhouse experiments directly comparing gamma-irradiated and non-irradiated undigested and digested dried sewage solids as fertilizers indicate little or no effect of 1 mega-rad gamma radiation treatment on plant yield or plant-nutrient uptake and demonstrated considerable benefit from using sewage solids on calcareous soils. Plant response to undigested sewage solids was considerably greater than to digested sewage solids when applied at levels that were isonitrogenous. The calcareous soils in New Mexico typically range in pH from 7.5 to 9.0, limiting the plant-availability of many elements, especially heavy metals. Soils irrigated with sewage-effluent for 40 years demonstrated beneficial use of supplied plant-nutrients with no apparent increase in plant-uptake of heavy metals. RDSS applied to a calcareous soil low in plant-available iron increased plant growth in the greenhouse considerably more than treatments with equal amounts of nitrogen, phosphorus and iron applied as common fertilizer materials. Plant tissue concentrations of Fe, Zn, Mn and Cu showed that RDSS was a good source of these nutrients. Results also indicated that the total soluble salt concentration of the RDSS was the factor most limiting plant growth. Chromium, Cd, Ni and Pd plant-tissue concentrations were apparently not increased by RDSS treatments. (Auth.)

  17. Thermal effects on beryllium mirrors

    International Nuclear Information System (INIS)

    Weinswig, S.

    1989-01-01

    Beryllium is probably the most frequently used material for spaceborne system scan mirrors. Beryllium's properties include lightweightedness, high Young's modulus, high stiffness value, high resonance value. As an optical surface, beryllium is usually nickel plated in order to produce a higher quality surface. This process leads to the beryllium mirror acting like a bimetallic device. The mirror's deformation due to the bimetallic property can possibly degrade the performance of the associated optical system. As large space borne systems are designed and as temperature considerations become more crucial in the instruments, the concern about temporal deformation of the scan mirrors becomes a prime consideration. Therefore, two sets of tests have been conducted in order to ascertain the thermal effects on nickel plated beryllium mirrors. These tests are categorized. The purpose of this paper is to present the values of the bimetallic effect on typical nickel plated beryllium mirrors

  18. Irradiation of solid Walker carcino-sarcomas after synchronisation with hydroxyurea

    International Nuclear Information System (INIS)

    Wayss, K.; Mattern, J.; Volm, M.

    1980-01-01

    Sprague-Dawley rats with solid Walker carcino-sarcomas were synchronized with hydroxyurea (HU; 6 x 50 mg and 1 x 300 mg HU/kg body weight) and then irradiated at different time points ( 60 Co). The synchronized tumors showed a significant delay of growth when irradiation was applied in the late G1 phase, at the transition G1/S and in the early S phase. The remaining phases of the cell cycle, especially the S phase showed the same sensitivity as the non-synchronized controls. Improvement of therapy by irradiation after HU application was largely due to the synchronization of tumor cells. Only the increased therapeutic effect of irradiation shortly after application of HU can be explained also by combination of both HU and irradiation. (orig.) 891 MG/orig. 892 MKO [de

  19. X-ray diffraction studies of neutron irradiated beryllium oxide; Etude par diffraction des rayons X de glucine irradiee aux neutrons

    Energy Technology Data Exchange (ETDEWEB)

    Belbeoch, B; Rodot, J; Roulliay, M [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

    1966-07-01

    X-ray diagrams of neutron irradiated sintered BeO (E > 1 MeV) can be classified into 3 types depending on the value of the c/a ratio, independently of the characteristics of the sinters, (hot pressed or cold pressed, material, variable density and grain size, pure BeO or BeO with additions). The anisotropic expansion of the BeO lattice caused by irradiation depends not only on the dose of irradiation, but also on the intergranular stresses of the samples. The sintered samples which resist most satisfactorily to irradiation consist of cold pressed high density and small grain size material for which the c/a ratio varies little with increasing dosage. The single crystal diagrams show the same classification as the polycrystalline material in respect with the c/a ratio. Furthermore, in addition to the Bragg reflections, X-ray diffusions are observed; the distribution of the defects is no longer isotropic; a description is given in particular of the scattering which occurs when 1.625 < c/a < 1.645. It appears that the defects start to congregate and cause pronounced distortion of the lattice. The defects are stabilized in the form of large aggregates only when a later irradiation stage is reached. (author) [French] Les diagrammes de rayons X obtenus a l'aide d'echantillons frittes de BeO irradies aux neutrons (E > 1 MeV) peuvent etre classes en trois types qui dependent de la valeur du rapport c/a, quelles que soient les caracteristiques du fritte (fritte sous charge ou fritte naturel, densite et taille de grains variables, BeO pur ou avec additions). La dilatation anisotrope de la maille de BeO observee par irradiation ne depend pas seulement de la dose recue, mais aussi des etats de contraintes intergranulaires des echantillons; ainsi les frittes qui resistent le mieux sous irradiation sont les frittes naturels a forte densite et a petits grains pour lesquels le rapport c/a varie peu en fonction de la dose d'irradiation. Les diagrammes de monocristaux presentent la

  20. Beryllium. Its minerals. Pt. 1

    International Nuclear Information System (INIS)

    Lires, O.A.; Delfino, C.A.; Botbol, J.

    1990-01-01

    With this work a series of reports begins, under the generic name 'Beryllium', related to several aspects of beryllium technology. The target is to update, with critical sense, current bibliographic material in order to be used in further applications. Some of the most important beryllium ores, the Argentine emplacement of their deposits and world occurrence are described. Argentine and world production, resources and reserves are indicated here as well. (Author) [es

  1. Beryllium Metal Supply Options

    Science.gov (United States)

    1989-01-01

    Carcinogen Assessment Group (U.S. Environmental Protec- tion Agency, 1987). The National Institute of Occupational Safety and Health is currently examining...Epidemiology of beryllium intox- ication. Arch. Ind. Hyg. Occup . Med. 4:123-151. U. S. Environmental Protection Agency 1987. Health Assessment Document...1957 to 1961. He rejoined the Bureau of Mines in 1961 as the aluminum and bauxite commcdity specialist. In 1973 he became chief of the Division of

  2. Beryllium and zirconium

    International Nuclear Information System (INIS)

    Salesse, Marc

    1959-01-01

    Pure beryllium and zirconium, both isolated at about the same date but more than a century ago remained practically unused for eighty years. Fifteen years ago they were released from this state of inactivity by atomic energy, which made them into current metal a with an annual production which runs into tens of tons for the one and thousands for the other. The reasons for this promotion promise well for the future of the two metals, which moreover will probably find additional uses in other branches of industry. The attraction of beryllium and zirconium for atomic energy is easily explained. The curve of figure 1 gives the price per gram of uranium-235 as a function of enrichment: this price increases by about a factor of 3 on passing from natural uranium (0, 7 percent 235 U) to almost pure uranium-235. Because of their tow capture cross-section beryllium and zirconium make it possible, or at least easier, to use natural uranium and they thus enjoy an advantage the extent of which must be calculated for each reactor or fuel element project, but which is generally considerable. It will be seen later that this advantage should be based on figures which are even more favourable that would appear from the simple ratio 3 of the price of pure uranium- 235 contained in natural uranium. Reprint of a paper published in 'Industries Atomiques' - n. 1-2, 1959

  3. Characterization of shocked beryllium

    Directory of Open Access Journals (Sweden)

    Papin P.A.

    2012-08-01

    Full Text Available While numerous studies have investigated the low-strain-rate constitutive response of beryllium, the combined influence of high strain rate and temperature on the mechanical behavior and microstructure of beryllium has received limited attention over the last 40 years. In the current work, high strain rate tests were conducted using both explosive drive and a gas gun to accelerate the material. Prior studies have focused on tensile loading behavior, or limited conditions of dynamic strain rate and/or temperature. Two constitutive strength (plasticity models, the Preston-Tonks-Wallace (PTW and Mechanical Threshold Stress (MTS models, were calibrated using common quasi-static and Hopkinson bar data. However, simulations with the two models give noticeably different results when compared with the measured experimental wave profiles. The experimental results indicate that, even if fractured by the initial shock loading, the Be remains sufficiently intact to support a shear stress following partial release and subsequent shock re-loading. Additional “arrested” drive shots were designed and tested to minimize the reflected tensile pulse in the sample. These tests were done to both validate the model and to put large shock induced compressive loads into the beryllium sample.

  4. Preparation by irradiation of a solid support for enzyme immunoassay

    International Nuclear Information System (INIS)

    Kumakura, M.; Kaetsu, I.

    1984-01-01

    Reagents (immobilized anti-α-fetoprotein discs) having a porous structure were prepared for enzyme immunoassay of α-fetoprotein by radiation polymerization at low temperatures. Discs were attached to sticks for easy handling. The activity (determined by absorbance at 492 nm) of the discs varied with the hydrophilic properties and size of the discs. The discs are sufficiently sensitive and precise for enzyme immunoassay of α-fetoprotein. Anti-AFP dissolved in PBS solution was mixed with a monomer solution of hydroxyethyl methacrylate and hydroxypropyl methacrylate. The mixture was frozen to -78 0 C and gamma irradiated. (Auth.)

  5. Effects of irradiation on four solid breeder materials

    International Nuclear Information System (INIS)

    Hollenberg, G.W.

    1984-01-01

    The tritium breeding material with the highest lithium atom density, Li 2 O has been observed to incur significant swelling (>4%) under fast reactor irradiation. Such swelling, if unrestrained leads to either unacceptable, induced-strains in adjacent structural material or undesirable design compromises. Fortunately, however, Li 2 O deforms at low temperatures so that swelling strains may be internally accommodated. Laboratory dilational creep experiments were conducted on unirraciated Li 2 O between 500 and 700 0 C in order to provide data for structural analysis of in-reactor experiments and blanket design studies. A densification model agreed with most of the available data. 15 refs

  6. Modelisation and distribution of neutron flux in radium-beryllium source (226Ra-Be)

    Science.gov (United States)

    Didi, Abdessamad; Dadouch, Ahmed; Jai, Otman

    2017-09-01

    Using the Monte Carlo N-Particle code (MCNP-6), to analyze the thermal, epithermal and fast neutron fluxes, of 3 millicuries of radium-beryllium, for determine the qualitative and quantitative of many materials, using method of neutron activation analysis. Radium-beryllium source of neutron is established to practical work and research in nuclear field. The main objective of this work was to enable us harness the profile flux of radium-beryllium irradiation, this theoretical study permits to discuss the design of the optimal irradiation and performance for increased the facility research and education of nuclear physics.

  7. Fabrication of lithium ceramic pellets, rings and single crystals for irradiation in BEATRIX-II

    International Nuclear Information System (INIS)

    Slagle, O.D.; Noda, K.; Takahashi, T.

    1989-04-01

    BEATRIX-II is an IEA sponsored experiment of lithium ceramic solid breeder materials in the FFTF/MOTA. Li 2 O solid pellets and annular ring specimens were fabricated for in-situ tritium release tests. In addition, a series of single crystal and polycrystalline lithium ceramic samples were fabricated to determine the irradiation behavior and beryllium compatibility. 6 refs., 10 figs., 4 tabs

  8. TEM study of impurity segregations in beryllium pebbles

    Energy Technology Data Exchange (ETDEWEB)

    Klimenkov, M., E-mail: michael.klimenkov@kit.edu [Institute for Applied Materials – Applied Materials Physics, Karlsruhe Institute of Technology, Hermann-von-Helmholz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Chakin, V.; Moeslang, A. [Institute for Applied Materials – Applied Materials Physics, Karlsruhe Institute of Technology, Hermann-von-Helmholz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Rolli, R. [Institute for Applied Materials – Materials and Biomechanics, Karlsruhe Institute of Technology, Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany)

    2014-12-15

    Beryllium is planned to be used as a neutron multiplier in the Helium-cooled Pebble Bed European concept of a breeding blanket of demonstration power reactor DEMO. In order to evaluate the irradiation performance, individual pebbles and constrained pebble beds were neutron-irradiated at temperatures typical of fusion blankets. Beryllium pebbles 1 mm in diameter produced by the rotating electrode method were subjected to a TEM study before and after irradiation at High Flux Reactor, Petten, Netherlands at 861 K. The grain size varied in a wide range from sub-micron size up to several tens of micrometers, which indicated formation bimodal grain size distribution. Based on the application of combined electron energy loss spectroscopy and energy dispersive X-ray spectroscopy methods, we suggest that impurity precipitates play an important role in controlling the mechanical properties of beryllium. The impurity elements were present in beryllium at a sub-percent concentration form beryllide particles of a complex (Fe/Al/Mn/Cr)B composition. These particles are often ordered along dislocations lines, forming several micron-long chains. It can be suggested that fracture surfaces often extended along these chains in irradiated material.

  9. A low temperature cryostat with a refrigerator for studying electron-irradiation effects on solids, 2

    International Nuclear Information System (INIS)

    Oka, Takashi; Yoshida, Toshio; Shono, Yoshihiko

    1978-01-01

    A convenient cryostat with a small cryogenic refrigerator for studying electron-irradiation effects on solids is reported. The lowest temperature at the sample room is about 10 K or less. In a temperature region below 80 K, the sample temperature can be controlled within 0.05 K. (auth.)

  10. A possible anti-proliferative and anti-metastatic effect of irradiated riboflavin in solid tumours

    NARCIS (Netherlands)

    de Souza Queiroz, Karla Cristiana; Zambuzzi, Willian Fernando; de Souza, Ana Carolina Santos; da Silva, Rodrigo Augusto; Machado, Daisy; Justo, Giselle Zenker; Carvalho, Hernandes F.; Peppelenbosch, Maikel P.; Ferreira, Carmen Verissima

    2007-01-01

    Riboflavin is a potent photosensitizer as well as part of the vitamin B complex. Recently we demonstrated that the products generated by irradiation of riboflavin have potential as anti-leukaemic therapy. The possible action, however, of the riboflavin photoproducts in solid cancers has not been

  11. Photon emission from irradiated solids: Proceedings of the Werner Brandt workshop on penetration phenomena

    International Nuclear Information System (INIS)

    1986-11-01

    The workshop was concerned with photon emission from irradiated solids and the present record of the proceedings consists of material solicited from each participant. The results range from detailed and complete manuscripts to skeletal remnants of Vugraph transparencies. Individual papers have been cataloged separately

  12. Fine interstitial clusters as recombinators in decomposing solid solutions under irradiation

    International Nuclear Information System (INIS)

    Trushin, Yu.V.

    1991-01-01

    Behaviour of interstitial clusters and their roll in processes of radiation swelling of metals are described. It is shown that occurrence of coherent advanced precipitations during decomposition of solid solutions under irradiation leads to matrix supersaturation over interstitial atoms. This enhances recombination of unlike defects due to vacancy precipitation on fine interstitial clusters. Evaluation of cluster sizes was conducted

  13. Improved calculation of displacements per atom cross section in solids by gamma and electron irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Piñera, Ibrahin, E-mail: ipinera@ceaden.edu.cu [Centro de Aplicaciones Tecnológicas y Desarrollo Nuclear, CEADEN, 30 St. 502, Playa 11300, Havana (Cuba); Cruz, Carlos M.; Leyva, Antonio; Abreu, Yamiel; Cabal, Ana E. [Centro de Aplicaciones Tecnológicas y Desarrollo Nuclear, CEADEN, 30 St. 502, Playa 11300, Havana (Cuba); Espen, Piet Van; Remortel, Nick Van [University of Antwerp, CGB, Groenenborgerlaan 171, 2020 Antwerpen (Belgium)

    2014-11-15

    Highlights: • We present a calculation procedure for dpa cross section in solids under irradiation. • Improvement about 10–90% for the gamma irradiation induced dpa cross section. • Improvement about 5–50% for the electron irradiation induced dpa cross section. • More precise results (20–70%) for thin samples irradiated with electrons. - Abstract: Several authors had estimated the displacements per atom cross sections under different approximations and models, including most of the main gamma- and electron-material interaction processes. These previous works used numerical approximation formulas which are applicable for limited energy ranges. We proposed the Monte Carlo assisted Classical Method (MCCM), which relates the established theories about atom displacements to the electron and positron secondary fluence distributions calculated from the Monte Carlo simulation. In this study the MCCM procedure is adapted in order to estimate the displacements per atom cross sections for gamma and electron irradiation. The results obtained through this procedure are compared with previous theoretical calculations. An improvement in about 10–90% for the gamma irradiation induced dpa cross section is observed in our results on regard to the previous evaluations for the studied incident energies. On the other hand, the dpa cross section values produced by irradiation with electrons are improved by our calculations in about 5–50% when compared with the theoretical approximations. When thin samples are irradiated with electrons, more precise results are obtained through the MCCM (in about 20–70%) with respect to the previous studies.

  14. Beryllium. Beryllium oxide, obtention and properties. Pt.4

    International Nuclear Information System (INIS)

    Lires, O.A.; Delfino, C.A.; Botbol, J.

    1991-01-01

    As a continuation of the 'Beryllium' series this work reviews several methods of high purity beryllia production. Diverse methods of obtention and purification from different beryllium compounds are described. Some chemical, mechanical and electrical properties related with beryllia obtention methods are summarized. (Author) [es

  15. Proceedings of the third IEA international workshop on beryllium technology for fusion

    International Nuclear Information System (INIS)

    Kawamura, Hiroshi; Okamoto, Makoto

    1998-01-01

    This report is the Proceedings of the Third International Energy Agency International Workshop on Beryllium Technology for Fusion. The workshop was held on October 22-24, 1997, at the Sangyou Kaikan in Mito City with 68 participants who attended from the Europe, the Russian Federation, the Kazakstan, the United States and Japan. The topics for papers were arranged into 9 sessions; beryllium applications for ITER, production and characterization, chemical compatibility and corrosion, forming and joining, plasma/tritium interactions, beryllium coating, first wall applications, neutron irradiation effects, health and safety. To utilize beryllium in the pebble type blanket, a series of discussions were intensified in multiple view points such as the swelling, He/T release from beryllium pebble irradiated up to high He content, effective thermal conductivity, tritium permeation and coating, and fabrication cost, and so on. As the plasma facing material, life time of beryllium and coated beryllium, dust and particle production, joining, waste treatment, mechanical properties and deformation by swelling were discussed as important issues. Especially, it was recognized throughout the discussions that the comparative study by the different researchers should be carried out to establish the reliability of the data reported in the workshop and in others. To enhance the comparative study, the world wide collaboration for the relative evaluation of the beryllium was proposed by the International Organization Committee and the proposal was approved by all of the participants. The 45 of the presented papers are indexed individually. (J.P.N.)

  16. Plasma spraying of beryllium and beryllium-aluminum-silver alloys

    International Nuclear Information System (INIS)

    Castro, R.G.; Stanek, P.W.; Elliott, K.E.; Jacobson, L.A.

    1994-01-01

    A preliminary investigation on plasma-spraying of beryllium and a beryllium-aluminum-4% silver alloy was done at the Los Alamos National Laboratory's Beryllium Atomization and Thermal Spray Facility (BATSF). Spherical Be and Be-Al-4%Ag powders, which were produced by centrifugal atomization, were used as feedstock material for plasma-spraying. The spherical morphology of the powders allowed for better feeding of fine (<38 μm) powders into the plasma-spray torch. The difference in the as-deposited densities and deposit efficiencies of the two plasma-sprayed powders will be discussed along with the effect of processing parameters on the as-deposited microstructure of the Be-Al-4%Ag. This investigation represents ongoing research to develop and characterize plasma-spraying of beryllium and beryllium-aluminum alloys for magnetic fusion and aerospace applications

  17. Plasma spraying of beryllium and beryllium-aluminum-silver alloys

    International Nuclear Information System (INIS)

    Castro, R.G.; Stanek, P.W.; Elliott, K.E.; Jacobson, L.A.

    1993-01-01

    A preliminary investigation on plasma-spraying of beryllium and a beryllium-aluminum 4% silver alloy was done at the Los Alamos National Laboratory's Beryllium Atomization and Thermal Spray Facility (BATSF). Spherical Be and Be-Al-4%Ag powders, which were produced by centrifugal atomization, were used as feedstock material for plasma-spraying. The spherical morphology of the powders allowed for better feeding of fine (<38 μm) powders into the plasma-spray torch. The difference in the as-deposited densities and deposit efficiencies of the two plasma-sprayed powders will be discussed along with the effect of processing parameters on the as-deposited microstructure of the Be-Al-4%Ag. This investigation represents ongoing research to develop and characterize plasma-spraying of beryllium and beryllium-aluminum alloys for magnetic fusion and aerospace applications

  18. Computer codes for simulating atomic-displacement cascades in solids subject to irradiation

    International Nuclear Information System (INIS)

    Asaoka, Takumi; Taji, Yukichi; Tsutsui, Tsuneo; Nakagawa, Masayuki; Nishida, Takahiko

    1979-03-01

    In order to study atomic displacement cascades originating from primary knock-on atoms in solids subject to incident radiation, the simulation code CASCADE/CLUSTER is adapted for use on FACOM/230-75 computer system. In addition, the code is modified so as to plot the defect patterns in crystalline solids. As other simulation code of the cascade process, MARLOWE is also available for use on the FACOM system. To deal with the thermal annealing of point defects produced in the cascade process, the code DAIQUIRI developed originally for body-centered cubic crystals is modified to be applicable also for face-centered cubic lattices. By combining CASCADE/CLUSTER and DAIQUIRI, we then prepared a computer code system CASCSRB to deal with heavy irradiation or saturation damage state of solids at normal temperature. Furthermore, a code system for the simulation of heavy irradiations CASCMARL is available, in which MARLOWE code is substituted for CASCADE in the CASCSRB system. (author)

  19. Measurements of beryllium sputtering yields at JET

    Science.gov (United States)

    Jet-Efda Contributors Stamp, M. F.; Krieger, K.; Brezinsek, S.

    2011-08-01

    The lifetime of the beryllium first wall in ITER will depend on erosion and redeposition processes. The physical sputtering yields for beryllium (both deuterium on beryllium (Be) and Be on Be) are of crucial importance since they drive the erosion process. Literature values of experimental sputtering yields show an order of magnitude variation so predictive modelling of ITER wall lifetimes has large uncertainty. We have reviewed the old beryllium yield experiments on JET and used current beryllium atomic data to produce revised beryllium sputtering yields. These experimental measurements have been compared with a simple physical sputtering model based on TRIM.SP beryllium yield data. Fair agreement is seen for beryllium yields from a clean beryllium limiter. However the yield on a beryllium divertor tile (with C/Be co-deposits) shows poor agreement at low electron temperatures indicating that the effect of the higher sputtering threshold for beryllium carbide is important.

  20. Technical Basis for PNNL Beryllium Inventory

    Energy Technology Data Exchange (ETDEWEB)

    Johnson, Michelle Lynn

    2014-07-09

    The Department of Energy (DOE) issued Title 10 of the Code of Federal Regulations Part 850, “Chronic Beryllium Disease Prevention Program” (the Beryllium Rule) in 1999 and required full compliance by no later than January 7, 2002. The Beryllium Rule requires the development of a baseline beryllium inventory of the locations of beryllium operations and other locations of potential beryllium contamination at DOE facilities. The baseline beryllium inventory is also required to identify workers exposed or potentially exposed to beryllium at those locations. Prior to DOE issuing 10 CFR 850, Pacific Northwest Nuclear Laboratory (PNNL) had documented the beryllium characterization and worker exposure potential for multiple facilities in compliance with DOE’s 1997 Notice 440.1, “Interim Chronic Beryllium Disease.” After DOE’s issuance of 10 CFR 850, PNNL developed an implementation plan to be compliant by 2002. In 2014, an internal self-assessment (ITS #E-00748) of PNNL’s Chronic Beryllium Disease Prevention Program (CBDPP) identified several deficiencies. One deficiency is that the technical basis for establishing the baseline beryllium inventory when the Beryllium Rule was implemented was either not documented or not retrievable. In addition, the beryllium inventory itself had not been adequately documented and maintained since PNNL established its own CBDPP, separate from Hanford Site’s program. This document reconstructs PNNL’s baseline beryllium inventory as it would have existed when it achieved compliance with the Beryllium Rule in 2001 and provides the technical basis for the baseline beryllium inventory.

  1. Beryllium for first wall, limiter and divertor - a literature survey

    International Nuclear Information System (INIS)

    Schuster, A.; Smid, I.; Kny, E.

    1994-01-01

    A survey of the topical literature on beryllium as material for plasma interactive components in future fusion devices is given. The radiation damage which can be expected as a result of the neutron irradiation from ignited tokamak plasma is discussed. The response to high heat fluxes and simulation experiments in different test facilities are referred. Another focus will be on the material properties literature data, on joining techniques and on compatibility with other materials. The performance of a beryllium coated first wall at JET is reported. Some relevant literature on other candidate materials for plasma interactive components shall be considered

  2. Response and recovery kinetics of a solid tumour after irradiation

    International Nuclear Information System (INIS)

    Rowley, R.; Hopkins, H.A.; Ritenour, E.R.; Looney, W.B.

    1980-01-01

    The effects of local tumour radiation over the dose range 7.5-30 Gy on the growth and cell kinetics of rat hepatoma H-4-II-E have been investigated. A plot of growth delays against log surviving fraction was linear below a fraction of 0.03, but failed to extrapolate to the origin. Following a single dose of 15 Gy to the tumour, DNA-precursor incorporation, labelling and mitotic indices were depressed for 7 days. Tumour cellularity, measured as DNA/g tumour was reduced and the rate of increase of total clonogenic cells slower than after complete tumour recovery. From Day 7 to Day 9 all indices of proliferation recovered to about control levels, clonogenic cell numbers increased more rapidly and tumour cellularity was restored. Repopulation of the tumour therefore appeared to take place mainly after Day 7. Incorporation of [ 3 H]-TdR into tumour DNA reached twice the control values on Day 9. The rate of tumour growth accelerated after the initial decrease, and maximum tumour growth rate was also twice the control values on Day 13. Accelerated growth rates in irradiated tumours, above those of control tumours, occurred 10-16 days after treatment. The effectiveness of sequential therapy may therefore be improved if given during this period of accelerated tumour growth. (author)

  3. Method for fabricating beryllium structures

    Science.gov (United States)

    Hovis, Jr., Victor M.; Northcutt, Jr., Walter G.

    1977-01-01

    Thin-walled beryllium structures are prepared by plasma spraying a mixture of beryllium powder and about 2500 to 4000 ppm silicon powder onto a suitable substrate, removing the plasma-sprayed body from the substrate and placing it in a sizing die having a coefficient of thermal expansion similar to that of the beryllium, exposing the plasma-sprayed body to a moist atmosphere, outgassing the plasma-sprayed body, and then sintering the plasma-sprayed body in an inert atmosphere to form a dense, low-porosity beryllium structure of the desired thin-wall configuration. The addition of the silicon and the exposure of the plasma-sprayed body to the moist atmosphere greatly facilitate the preparation of the beryllium structure while minimizing the heretofore deleterious problems due to grain growth and grain orientation.

  4. Neutron irradiation characteristic tests of oxygen sensors using zirconia solid electrolyte

    International Nuclear Information System (INIS)

    Hiura, Nobuo; Endou, Yasuichi; Yamaura, Takayuki; Niimi, Motoji; Hoshiya, Taiji; Saito, Junichi; Souzawa, Shizuo; Ooka, Norikazu; Kobiyama, Mamoru.

    1997-03-01

    In the Department of JMTR of Japan Atomic Energy Research Institute (JAERI), the in-situ measuring technique of oxygen potential has been being developed to study the chemical behavior of high burn-up fuel base-irradiated in the Light Water Reactor. In this test for development of the technique, oxygen sensors using zirconia solid electrolyte stabilized by MgO, CaO and Y 2 O 3 , named MSZ, CSZ and YSZ, respectively, were irradiated by neutrons in the Japan Materials Testing Reactor (JMTR) of JAERI and the characteristics of electromotive force of these sensors under and after irradiation were discussed. From the experimental results, the electromotive force of YSZ sample under irradiation decreased with an increase in irradiation fluence within a range of neutron fluence (E>1 MeV) up to 1 x 10 23 m -2 . The electromotive force of MSZ sensor irradiated with neutron fluences (E>1 MeV) up to 9 x 10 21 m -2 was almost equal to the theoretical value of the electromotive force. It was shown that after irradiation, a decrease in the electromotive force of CSZ sensor was smaller than those of MSZ and YSZ sensors, although the electromotive forces of MSZ, CSZ and YSZ sensors were smaller than the theoretical value. (author)

  5. Doped beryllium lanthanate crystals

    International Nuclear Information System (INIS)

    1974-01-01

    Monocrystals of doped beryllium lanthanate, Be 2 Lasub(2-2x)Zsub(2x)O 5 --where Z may be any rare earth, but preferably neodymium, and x may have values between 0.001 and 0.2, but preferably between 0.007 and 0.015-- are recommended as laser hosts. They are softer and may be grown at a lower temperature than Y 3 A1 5 O 12 :Nd (YAG:Nd). Their chemical composition and preparation are described. An example of an optically pumped laser apparatus with this type of monocrystal as laser host is presented

  6. SAFARI-1 research reactor beryllium reflector element replacement, management and relocation

    Energy Technology Data Exchange (ETDEWEB)

    Kock, Marisa De; Vlok, Jwh; Steynberg, B J [South Africa Atomic Energy Corporation (Necsa) (South Africa)

    2012-03-15

    The beryllium (Be) reflector elements of the SAFARI-1 Research Reactor were replaced in October 2011 as part of the Ageing Management Programme of the reactor. After more than three million MWh of operation over a period of 47 years, core reloading became more difficult due to the geometric deformation of the beryllium reflector elements. During the replacement of the reflector elements, criticality and reactivity worth experiments were performed and found to compare favorably with calculated values. A Beryllium Management Programme was established at SAFARI-1 to identify and apply effective and appropriate actions and practices for managing the ageing of the new beryllium reflector elements. This will provide timely detection and mitigation of ageing mechanisms relevant to beryllium reflector elements, supporting the life extension of these elements. These actions and practices include monitoring of the tritium levels in the primary water, calculating and measuring the fluxes within the beryllium reflector positions, measuring the straightness of the elements to track geometric deformation and visually inspecting the reflector elements for crack formation. Acceptance criteria indicating the end of life of the elements were established. These criteria take into account the smallest gap that could exist between elements, sudden changes in the tritium levels and formation of cracks. All the data obtained through the Beryllium Management Programme are recorded in a database. Additional benefits gained through a Beryllium Management Programme are the availability of a complete irradiation history of the beryllium reflector elements at any point in time and the establishment of a knowledge base to assists in the understanding of the behavior of the beryllium reflector elements in an irradiation environment. Straightness baseline measurements of the new beryllium reflector elements were performed with a beryllium straightness measurement tool, designed at SAFARI-1. The

  7. SAFARI-1 research reactor beryllium reflector element replacement, management and relocation

    International Nuclear Information System (INIS)

    Kock, Marisa De; Vlok, Jwh; Steynberg, B.J.

    2012-01-01

    The beryllium (Be) reflector elements of the SAFARI-1 Research Reactor were replaced in October 2011 as part of the Ageing Management Programme of the reactor. After more than three million MWh of operation over a period of 47 years, core reloading became more difficult due to the geometric deformation of the beryllium reflector elements. During the replacement of the reflector elements, criticality and reactivity worth experiments were performed and found to compare favorably with calculated values. A Beryllium Management Programme was established at SAFARI-1 to identify and apply effective and appropriate actions and practices for managing the ageing of the new beryllium reflector elements. This will provide timely detection and mitigation of ageing mechanisms relevant to beryllium reflector elements, supporting the life extension of these elements. These actions and practices include monitoring of the tritium levels in the primary water, calculating and measuring the fluxes within the beryllium reflector positions, measuring the straightness of the elements to track geometric deformation and visually inspecting the reflector elements for crack formation. Acceptance criteria indicating the end of life of the elements were established. These criteria take into account the smallest gap that could exist between elements, sudden changes in the tritium levels and formation of cracks. All the data obtained through the Beryllium Management Programme are recorded in a database. Additional benefits gained through a Beryllium Management Programme are the availability of a complete irradiation history of the beryllium reflector elements at any point in time and the establishment of a knowledge base to assists in the understanding of the behavior of the beryllium reflector elements in an irradiation environment. Straightness baseline measurements of the new beryllium reflector elements were performed with a beryllium straightness measurement tool, designed at SAFARI-1. The

  8. Erosion of beryllium under ITER – Relevant transient plasma loads

    International Nuclear Information System (INIS)

    Kupriyanov, I.B.; Nikolaev, G.N.; Kurbatova, L.A.; Porezanov, N.P.; Podkovyrov, V.L.; Muzichenko, A.D.; Zhitlukhin, A.M.; Gervash, A.A.; Safronov, V.M.

    2015-01-01

    Highlights: • We study the erosion, mass loss/gain and surface structure evolution of Be/CuCrZr mock-ups, armored with beryllium of TGP-56FW grade after irradiation by deuterium plasma heat load of 0.5 MJ/m 2 at 250 °C and 500 °C. • Beryllium mass loss/erosion under plasma heat load at 250 °C is rather small (no more than 0.2 g/m 2 shot and 0.11 μm/shot, correspondingly, after 40 shots) and tends to decrease with increasing number of shots. • Beryllium mass loss/erosion under plasma heat load at 500 °C is much higher (∼2.3 g/m 2 shot and 1.2 μm/shot, correspondingly, after 10 shot) and tends to decrease with increasing the number of shots (∼0.26 g/m 2 pulse and 0.14 μm/shot, correspondingly, after 100 shot). • Beryllium erosion value derived from the measurements of profile of irradiated surface is much higher than erosion value derived from mass loss data. - Abstract: Beryllium will be used as a armor material for the ITER first wall. It is expected that erosion of beryllium under transient plasma loads such as the edge-localized modes (ELMs) and disruptions will mainly determine a lifetime of the ITER first wall. This paper presents the results of recent experiments with the Russian beryllium of TGP-56FW ITER grade on QSPA-Be plasma gun facility. The Be/CuCrZr mock-ups were exposed to up to 100 shots by deuterium plasma streams (5 cm in diameter) with pulse duration of 0.5 ms and heat loads range of 0.2–0.5 MJ/m 2 at different temperature of beryllium tiles. The temperature of Be tiles has been maintained about 250 and 500 °C during the experiments. After 10, 40 and 100 shots, the beryllium mass loss/gain under erosion process were investigated as well as evolution of surface microstructure and cracks morphology

  9. Erosion of beryllium under ITER – Relevant transient plasma loads

    Energy Technology Data Exchange (ETDEWEB)

    Kupriyanov, I.B., E-mail: igkupr@gmail.com [A.A. Bochvar High Technology Research Institute of Inorganic Materials, Rogova St. 5a, 123060 Moscow (Russian Federation); Nikolaev, G.N.; Kurbatova, L.A.; Porezanov, N.P. [A.A. Bochvar High Technology Research Institute of Inorganic Materials, Rogova St. 5a, 123060 Moscow (Russian Federation); Podkovyrov, V.L.; Muzichenko, A.D.; Zhitlukhin, A.M. [TRINITI, Troitsk, Moscow reg. (Russian Federation); Gervash, A.A. [Efremov Research Institute, S-Peterburg (Russian Federation); Safronov, V.M. [Project Center of ITER, Moscow (Russian Federation)

    2015-08-15

    Highlights: • We study the erosion, mass loss/gain and surface structure evolution of Be/CuCrZr mock-ups, armored with beryllium of TGP-56FW grade after irradiation by deuterium plasma heat load of 0.5 MJ/m{sup 2} at 250 °C and 500 °C. • Beryllium mass loss/erosion under plasma heat load at 250 °C is rather small (no more than 0.2 g/m{sup 2} shot and 0.11 μm/shot, correspondingly, after 40 shots) and tends to decrease with increasing number of shots. • Beryllium mass loss/erosion under plasma heat load at 500 °C is much higher (∼2.3 g/m{sup 2} shot and 1.2 μm/shot, correspondingly, after 10 shot) and tends to decrease with increasing the number of shots (∼0.26 g/m{sup 2} pulse and 0.14 μm/shot, correspondingly, after 100 shot). • Beryllium erosion value derived from the measurements of profile of irradiated surface is much higher than erosion value derived from mass loss data. - Abstract: Beryllium will be used as a armor material for the ITER first wall. It is expected that erosion of beryllium under transient plasma loads such as the edge-localized modes (ELMs) and disruptions will mainly determine a lifetime of the ITER first wall. This paper presents the results of recent experiments with the Russian beryllium of TGP-56FW ITER grade on QSPA-Be plasma gun facility. The Be/CuCrZr mock-ups were exposed to up to 100 shots by deuterium plasma streams (5 cm in diameter) with pulse duration of 0.5 ms and heat loads range of 0.2–0.5 MJ/m{sup 2} at different temperature of beryllium tiles. The temperature of Be tiles has been maintained about 250 and 500 °C during the experiments. After 10, 40 and 100 shots, the beryllium mass loss/gain under erosion process were investigated as well as evolution of surface microstructure and cracks morphology.

  10. EPR of gamma irradiated solid sucrose and UV spectra of its solution. An attempt for calibration of solid state/EPR dosimetry

    International Nuclear Information System (INIS)

    Yordanov, N.D.; Karakirova, Y.

    2007-01-01

    A simple new approach for independent calibration of solid state/EPR (SS/EPR) dosimetry system is reported. It is based on the fact that: (i) gamma-irradiation of solid sucrose (sugar) induces stable EPR detectable free radicals accompanied by UV detectable brown colour stable in the solid state and in solution; (ii) both the EPR intensity of gamma-irradiated solid sucrose and its solution UV absorbance linearly depend on the absorbed dose high energy radiation and may be independently used for dosimetric purpose; (iii) UV spectrometers are calibrated. The correlation between EPR response and absorbed dose radiation of solid sucrose and UV absorption of its solutions is used in the present communication for calibration purpose. The procedure of sucrose extraction from sucrose-paraffin dosimeters is described. The calibration procedure may be applied to any other (alanine, self-calibrated, etc.) SS/EPR dosimeters, simultaneously irradiated with sucrose

  11. Thermal fatigue of beryllium

    International Nuclear Information System (INIS)

    Deksnis, E.; Ciric, D.; Falter, H.

    1995-01-01

    Thermal fatigue life of S65c beryllium castellated to a geometry 6 x 6 x (8-10)mm deep has been tested for steady heat fluxes of 3 MW/m 2 to 5 MW/m 2 and under pulsed heat fluxes (10-20 MW/m 2 ) for which the time averaged heat flux is 5 MW/m 2 . These tests were carried out in the JET neutral beam test facility A test sequence with peak surface temperatures ≤ 600 degrees C produced no visible fatigue cracks. In the second series of tests, with T max ≤ 750 degrees C evidence for fatigue appeared after a minimum of 1350 stress cycles. These fatigue data are discussed in view of the observed lack of thermal fatigue in JET plasma operations with beryllium PFC. JET experience with S65b and S65c is reviewed; recent operations with Φ = 25 MW/m 2 and sustained melting/resolidification are also presented. The need for a failure criterion for finite element analyses of Be PFC lifetimes is discussed

  12. Corrosion of beryllium oxide

    International Nuclear Information System (INIS)

    Elston, J.; Caillat, R.

    1958-01-01

    Data are reported on the volatilization rate of beryllium oxide in moist air depending on temperature and water vapour concentration. They are concerned with powder samples or sintered shapes of various densities. For sintered samples, the volatilization rate is very low under the following conditions: - temperature: 1300 deg. C, - water vapour concentration in moist air: 25 g/m 3 , - flow rate: 12 I/hour corresponding to a speed of 40 m/hour on the surface of the sample. For calcinated powders (1300 deg. C), grain growth has been observed under a stream of moist air at 1100 deg. C. For instance, grain size changes from 0,5 to at least 2 microns after 500 hours of exposure at this temperature. Furthermore, results data are reported on corrosion of sintered beryllium oxide in pressurized water. At 250 deg. C, under a pressure of 40 kg/cm 2 water is very slightly corrosive; however, internal strains are revealed. Finally, some features on the corrosion in liquid sodium are exposed. (author) [fr

  13. Irradiation specifically sensitises solid tumour cell lines to TRAIL mediated apoptosis

    International Nuclear Information System (INIS)

    Marini, Patrizia; Schmid, Angelika; Jendrossek, Verena; Faltin, Heidrun; Daniel, Peter T; Budach, Wilfried; Belka, Claus

    2005-01-01

    TRAIL (tumor necrosis factor related apoptosis inducing ligand) is an apoptosis inducing ligand with high specificity for malignant cell systems. Combined treatment modalities using TRAIL and cytotoxic drugs revealed highly additive effects in different tumour cell lines. Little is known about the efficacy and underlying mechanistic effects of a combined therapy using TRAIL and ionising radiation in solid tumour cell systems. Additionally, little is known about the effect of TRAIL combined with radiation on normal tissues. Tumour cell systems derived from breast- (MDA MB231), lung- (NCI H460) colorectal- (Colo 205, HCT-15) and head and neck cancer (FaDu, SCC-4) were treated with a combination of TRAIL and irradiation using two different time schedules. Normal tissue cultures from breast, prostate, renal and bronchial epithelia, small muscle cells, endothelial cells, hepatocytes and fibroblasts were tested accordingly. Apoptosis was determined by fluorescence microscopy and western blot determination of PARP processing. Upregulation of death receptors was quantified by flow cytometry. The combined treatment of TRAIL with irradiation strongly increased apoptosis induction in all treated tumour cell lines compared to treatment with TRAIL or irradiation alone. The synergistic effect was most prominent after sequential application of TRAIL after irradiation. Upregulation of TRAIL receptor DR5 after irradiation was observed in four of six tumour cell lines but did not correlate to tumour cell sensitisation to TRAIL. TRAIL did not show toxicity in normal tissue cell systems. In addition, pre-irradiation did not sensitise all nine tested human normal tissue cell cultures to TRAIL. Based on the in vitro data, TRAIL represents a very promising candidate for combination with radiotherapy. Sequential application of ionising radiation followed by TRAIL is associated with an synergistic induction of cell death in a large panel of solid tumour cell lines. However, TRAIL receptor

  14. The INEL beryllium multiplication experiment

    International Nuclear Information System (INIS)

    Smith, J.R.; King, J.J.

    1991-03-01

    The experiment to measure the multiplication of 14-MeV neutrons in bulk beryllium has been completed. The experiment consists of determining the ratio of 56 Mn activities induced in a large manganese bath by a central 14-MeV neutron source, with and without a beryllium sample surrounding the source. In the manganese bath method a neutron source is placed at the center of a totally-absorbing aqueous solution of MnSo 4 . The capture of neutrons by Mn produces a 56 Mn activity proportional to the emission rate of the source. As applied to the measurement of the multiplication of 14- MeV neutrons in bulk beryllium, the neutron source is a tritium target placed at the end of the drift tube of a small deuteron accelerator. Surrounding the source is a sample chamber. When the sample chamber is empty, the neutrons go directly to the surrounding MnSO 4 solution, and produce a 56 Mn activity proportional to the neutron emission rate. When the chamber contains a beryllium sample, the neutrons first enter the beryllium and multiply through the (n,2n) process. Neutrons escaping from the beryllium enter the bath and produce a 56 Mn activity proportional to the neutron emission rate multiplied by the effective value of the multiplication in bulk beryllium. The ratio of the activities with and without the sample present is proportional to the multiplication value. Detailed calculations of the multiplication and all the systematic effects were made with the Monte Carlo program MCNP, utilizing both the Young and Stewart and the ENDF/B-VI evaluations for beryllium. Both data sets produce multiplication values that are in excellent agreement with the measurements for both raw and corrected values of the multiplication. We conclude that there is not real discrepancy between experimental and calculated values for the multiplication of neutrons in bulk beryllium. 12 figs., 11 tabs., 18 refs

  15. Offshoots from beryllium development programme

    International Nuclear Information System (INIS)

    Sharma, B.P.; Sinha, P.K.

    1995-01-01

    The paper briefly presents extraction and processing of beryllium metal as practiced in the beryllium facilities at Turbhe, New Bombay. These facilities have been set up to meet the indigenous requirements of the metal in space and nuclear science programmes. As offshoot of this beryllium development programme has been the development of a number of pyro and powder metallurgical equipment. Indigenous development of these pieces of equipment has been a professionally rewarding experience. Efforts are now on to promote these equipment for industrial use. (author). 6 refs., 6 figs., 2 tabs

  16. Small interstitial clusters as opposite defect recombinators in decomposing solid solutions under irradiation

    International Nuclear Information System (INIS)

    Orlov, A.N.; Trushin, Yu.V.

    1988-01-01

    An attempt was made to make allowance for the role of binary and ternary interstitials in the kinetics of radiation point defects both in the presence and in the absence of coherent preseparation. It is shown that in solid solutions, decomposing under irradiation, recombination with binary and ternary interstitials proceeds more quickly than directly, and this difference is more pronounced (from 2 up to 20 time growth) due to defect flow for preseparation at the stage of coherent preseparation formation

  17. Alternative method of portable irradiation of manganese sulphate solution by an plutonium-beryllium source for manganese sulphate bath efficiency measurements; Metodo alternativo de irradiacao portatil da solucao de sulfato de manganes por uma fonte de plutonio-berilio para medicoes de eficiencia do banho de sulfato de manganes

    Energy Technology Data Exchange (ETDEWEB)

    Silva, Fellipe Souza da; Martins, Marcelo Marques; Pereira, Walsan Wagner, E-mail: fellipess@ird.gov.br [Instituto de Radioprotecao e Dosimetria (IRD/CNEN-RJ), Rio de Janeiro, RJ (Brazil)

    2016-07-01

    This study intends to create an alternative irradiation system from a Plutonium-Beryllium source for manganese sulphate solution using the Monte Carlo code. Thus seeking to eliminate the issue of institutes that do not have reactors or particle accelerators in its infrastructure, in order to optimize and provide independence for them to carry out efficiency measurements of MnSO{sub 4} solution in their own locality. The Monte Carlo simulations defined the technical features of this new system so that the solution reaches the maximum neutron capture by manganese in solution. (author)

  18. Status of EC solid breeder blanket designs and R and D for demo fusion reactors

    International Nuclear Information System (INIS)

    Proust, E.; Anzidei, L.; Moons, F.

    1994-01-01

    Within the European Community Fusion Technology Program two solid breeder blankets for a DEMO reactor are being developed. The two blankets have various features in common: helium as coolant and as tritium purge gas, the martensitic steel MANET as structural material and beryllium as neutron multiplier. The configurations of the two blankets are however different: in the B.I.T. (Breeder Inside Tube) concept the breeder materials are LiAlO 2 or Li 2 ZrO 3 in the form of annular pellets contained in tubes surrounded by beryllium blocks, the coolant helium being outside the tubes, whereas in the B.O.T. (Breeder out of Tube) the breeder and multiplier material are Li 4 SiO 4 and beryllium pebbles forming a mixed bed placed outside the tubes containing the coolant helium. The main critical issues for both blankets are the behavior of the breeder ceramics and of beryllium under irradiation and the tritium control. Other issues are the low temperature irradiation induced embrittlement of MANET, the mechanical effects caused by major plasma disruptions, and safety and reliability. The R and D work concentrate on these issues. The development of martensitic steels including MANET is part of a separate program. Breeder ceramics and beryllium irradiations have been so far performed for conditions which do not cover the peak values injected in the DEMO blankets. Further irradiations in thermal reactors and in fast reactors, especially for beryllium, are required. An effective tritium control requires the development of permeation barriers and/or of methods of oxidation of the tritium in the main helium cooling systems. First promising results have been obtained also in field of mechanical effects from plasma disruptions and safety and reliability, however further work is required in the reliability field and to validate the codes for the calculations of the plasma disruption effects. (authors). 8 figs., 2 tabs., 53 refs

  19. Formation of fine solid particles from aqueous solutions of sodium chloropalladate by gamma-ray irradiation

    International Nuclear Information System (INIS)

    Hatada, Motoyoshi; Fujita, Iwao; Korekawa, Kei-ichi.

    1994-10-01

    Studies have been carried out on the radiation chemical formation of palladium fine particles in argon saturated aqueous solutions of sodium chloropalladate without organic stabilizer. The solutions were irradiated with gamma-rays from a cobalt gamma-ray source and the irradiated solutions were subjected to the dynamic light scattering analysis for the particle diameter measurements, and to the UV-visible optical absorption spectroscopy for the measurements of turbidity (absorption at 700 nm) and remaining chloropalladate ion concentrations in the solution. In the solution of pH = 1.95 by HCl, the turbidity increased after the irradiation and then decreased with time. The concentration of remaining palladate ion in the solution decreased by the irradiation, but it gradually increased with time after the irradiation. These phenomena were qualitatively explained by the reaction scheme in that a precursor to the solid particles still exists in the solution after the irradiation was terminated, and that intermediates including the precursor reacted with chloride ion to re-form chloropalladate ions. The average diameter of the particles after the irradiation was ca. 20 nm and it increased with time to 40 nm at 2.75 kGy, and to 80 nm at 8.25 kGy absorption of radiation. The solution of pH = 0.65 by HCl was found to give lower yields of particles than those observed for the solution of pH = 1.95, and to give the particles of diameters about 150-200 nm. In the solution containing HClO 4 instead of HCl, palladium particles were also formed by the irradiation, whereas no backward reaction after the irradiation was observed due to the low concentration of chloride ion in the solution. The average diameter of the particles after the irradiation was about 300 nm and increased with time after the irradiation to a final values which was found to depend on pH of the solution and dose. (author)

  20. The fourth international energy agency international workshop on beryllium technology for fusion

    International Nuclear Information System (INIS)

    Scaffidi-Argentina, F.; Longhurst, G.R.

    2000-01-01

    The main objective of the workshop was to support the advancement of the international development of fusion power through communication and dissemination of information on progress made in beryllium technology. This has been accomplished through presentation of original research on issues of current interest to the fusion beryllium community. The workshop was divided into ten technical sessions that addressed the following general topics: production and characterization, health and safety, forming and joining, chemical compatibility, thermal-mechanical properties, pebble bed behavior, high-heat-flux performance, irradiation effects, plasma-tritium interaction, and molten beryllium-bearing salts

  1. The fourth international energy agency international workshop on beryllium technology for fusion

    Energy Technology Data Exchange (ETDEWEB)

    Scaffidi-Argentina, F.; Longhurst, G.R.

    2000-05-01

    The main objective of the workshop was to support the advancement of the international development of fusion power through communication and dissemination of information on progress made in beryllium technology. This has been accomplished through presentation of original research on issues of current interest to the fusion beryllium community. The workshop was divided into ten technical sessions that addressed the following general topics: production and characterization, health and safety, forming and joining, chemical compatibility, thermal-mechanical properties, pebble bed behavior, high-heat-flux performance, irradiation effects, plasma-tritium interaction, and molten beryllium-bearing salts.

  2. Thermodynamic pathways to melting, ablation, and solidification in absorbing solids under pulsed laser irradiation

    International Nuclear Information System (INIS)

    Lorazo, Patrick; Lewis, Laurent J.; Meunier, Michel

    2006-01-01

    The thermodynamic pathways involved in laser irradiation of absorbing solids are investigated in silicon for pulse durations of 500 fs and 100 ps. This is achieved by accounting for carrier and atom dynamics within a combined Monte Carlo and molecular-dynamics scheme and simultaneously tracking the time evolution of the irradiated material in ρ-T-P space. Our simulations reveal thermal changes in long-range order and state of aggregation driven, in most cases, by nonequilibrium states of rapidly heated or promptly cooled matter. Under femtosecond irradiation near the ablation threshold, the system is originally pulled to a near-critical state following rapid ( -12 s) disordering of the mechanically unstable crystal and isochoric heating of the resulting metallic liquid. The latter is then adiabatically cooled to the liquid-vapor regime where phase explosion of the subcritical, superheated melt is initiated by a direct conversion of translational, mechanical energy into surface energy on a ∼10 -12 -10 -11 s time scale. At higher fluences, matter removal involves, instead, the fragmentation of an initially homogeneous fluid subjected to large strain rates upon rapid, supercritical expansion in vacuum. Under picosecond irradiation, homogeneous and, at later times, heterogeneous melting of the superheated solid are followed by nonisochoric heating of the molten metal. In this case, the subcritical liquid material is subsequently cooled onto the binodal by thermal conduction and explosive boiling does not take place; as a result, ablation is associated with a ''trivial'' fragmentation process, i.e., the relatively slow expansion and dissociation into liquid droplets of supercritical matter near thermodynamic equilibrium. This implies a liquid-vapor equilibration time of ∼10 -11 -10 -10 s and heating along the binodal under nanosecond irradiation. Solidification of the nonablated, supercooled molten material is eventually observed on a ∼10 -11 -10 -9 s time scale

  3. Beryllium R and D for blanket application

    Energy Technology Data Exchange (ETDEWEB)

    Dalle Donne, M.; Scaffidi-Argentina, F. [Forschungszentrum Karlsruhe GmbH Technik und Umwelt (Germany). Inst. fuer Neutronenphysik und Reaktortechnik; Longhurst, G.R. [Idaho National Engineering Lab., Idaho Falls (United States); Kawamura, H. [Japan Atomic Energy Research Inst., Oarai, Ibaraki (Japan). Oarai Research Establishment

    1998-10-01

    The paper describes the main problems and the R and D for the beryllium to be used as neutron multiplier in blankets. As the four ITER partners propose to use beryllium in the form of pebbles for their DEMO relevant blankets (only the Russians consider the porous beryllium option as an alternative) and the ITER breeding blanket will use beryllium pebbles as well, the paper is mainly based on beryllium pebbles. Also the work on the chemical reactivity of fully dense and porous beryllium in contact with water steam is described, due to the safety importance of this point. (orig.) 29 refs.

  4. Beryllium R and D for blanket application

    International Nuclear Information System (INIS)

    Dalle Donne, M.; Scaffidi-Argentina, F.; Kawamura, H.

    1998-01-01

    The paper describes the main problems and the R and D for the beryllium to be used as neutron multiplier in blankets. As the four ITER partners propose to use beryllium in the form of pebbles for their DEMO relevant blankets (only the Russians consider the porous beryllium option as an alternative) and the ITER breeding blanket will use beryllium pebbles as well, the paper is mainly based on beryllium pebbles. Also the work on the chemical reactivity of fully dense and porous beryllium in contact with water steam is described, due to the safety importance of this point. (orig.)

  5. Beryllium R&D for blanket application

    Science.gov (United States)

    Donne, M. Dalle; Longhurst, G. R.; Kawamura, H.; Scaffidi-Argentina, F.

    1998-10-01

    The paper describes the main problems and the R&D for the beryllium to be used as neutron multiplier in blankets. As the four ITER partners propose to use beryllium in the form of pebbles for their DEMO relevant blankets (only the Russians consider the porous beryllium option as an alternative) and the ITER breeding blanket will use beryllium pebbles as well, the paper is mainly based on beryllium pebbles. Also the work on the chemical reactivity of fully dense and porous beryllium in contact with water steam is described, due to the safety importance of this point.

  6. Is the Spencer-Attix cavity equation applicable for solid-state detectors irradiated in megavoltage electron beams?

    International Nuclear Information System (INIS)

    Mobit, P.N.; Sandison, G.A.; Calgary Univ., AB

    2001-01-01

    The applicability of the Spencer-Attix cavity equation in determining absorbed doses in water using solid state detectors irradiated by megavoltage electron beams have been examined. The calculations were performed using the EGSnrc Monte Carlo code. This work is an extension of a recently published article examining the perturbation of dose by solid state detectors in megavoltage electron beams. (orig.)

  7. Ion beam irradiation as a tool to improve the ionic conductivity in solid polymer electrolyte systems

    Energy Technology Data Exchange (ETDEWEB)

    Manjunatha, H., E-mail: h-manjunath@blr.amrita.edu; Kumaraswamy, G. N. [Department of Physics, Amrita Vishwa Vidyapeetham, Bengaluru-560 035 (India); Damle, R. [Department of Physics, Bangalore University, Bengaluru-560 056 (India)

    2016-05-06

    Solid polymer electrolytes (SPEs) have potential applications in solid state electronic and energy devices. The optimum conductivity of SPEs required for such applications is about 10{sup −1} – 10{sup −3} Scm{sup −1}, which is hard to achieve in these systems. It is observed that ionic conductivity of SPEs continuously increase with increasing concentration of inorganic salt in the host polymer. However, there is a critical concentration of the salt beyond which the conductivity of SPEs decreases due to the formation of ion pairs. In the present study, solid polymer thin films based on poly (ethylene oxide) (PEO) complexed with NaBr salt with different concentrations have been prepared and the concentration at which ion pair formation occurs in PEO{sub x}NaBr is identified. The microstructure of the SPE with highest ionic conductivity is modified by irradiating it with low energy O{sup +1} ion (100 keV) of different fluencies. It is observed that the ionic conductivity of irradiated SPEs increases by one order in magnitude. The increase in ionic conductivity may be attributed to the enhanced segmental motion of the polymer chains due to radiation induced micro structural modification.

  8. Enhanced mass transfer during solid-liquid extraction of gamma-irradiated red beetroot

    International Nuclear Information System (INIS)

    Nayak, Chetan A.; Chethana, S.; Rastogi, N.K.; Raghavarao, K.S.M.S.

    2006-01-01

    The exposure to gamma-irradiation pretreatment increases cell wall permeabilization, resulting in loss of turgor pressure, which led to the increase of extractability of betanin from red beetroot. The degree of extraction of betanin was investigated using gamma irradiation as a pretreatment prior to the solid-liquid extraction process and compared with control beetroot samples. The beetroot subjected to different doses of gamma irradiation (2.5, 5.0, 7.5, 10.0 kGy) and control was dipped in an acetic acid medium (1% v/v) to extract the betanin. The diffusion coefficients for betanin as well as ionic component were estimated considering Fickian diffusion. The results indicated an increase in the diffusion coefficient of betanin (0.302x10 -9 -0.463x10 -9 m 2 /s) and ionic component (0.248x10 -9 -0.453x10 -9 m 2 /s) as the dose rate increased (from 2.5 to 10.0 kGy). The degradation constant was found to increase (0.050-0.079 min -1 ) with an increase gamma-irradiation doses (2.5-10.0 kGy), indicating lower stability of the betanin as compared to control sample at 65 deg. C

  9. Safe waste management practices in beryllium facilities

    International Nuclear Information System (INIS)

    Bhat, P.N.; Soundararajan, S.; Sharma, D.N.

    2012-01-01

    Beryllium, an element with the atomic symbol Be, atomic number 4, has very high stiffness to weight ratio and low density. It has good electrical conductive properties with low coefficient of thermal expansion. These properties make the metal beryllium very useful in varied technological endeavours, However, beryllium is recognised as one of the most toxic metals. Revelation of toxic effects of beryllium resulted in institution of stringent health and safety practices in beryllium handling facilities. The waste generated in such facilities may contain traces of beryllium. Any such waste should be treated as toxic waste and suitable safe waste management practices should be adopted. By instituting appropriate waste management practice and through a meticulously incorporated safety measures and continuous surveillance exercised in such facilities, total safety can be ensured. This paper broadly discusses health hazards posed by beryllium and safe methods of management of beryllium bearing wastes. (author)

  10. Contribution to the study of the uranium-carbon-beryllium ternary system

    International Nuclear Information System (INIS)

    Vaugoyeau, H.

    1969-01-01

    The isothermal section at 1000 deg. C of the uranium-carbon- beryllium system has been determined, and the quasi linear character of the sections UC-UBe 13 , UC-Be 2 C and Be 2 C-UBe 13 has been shown. The very low solubility of beryllium in uranium monocarbide has also been evidenced; quenching experiments have thus allowed the study of the limits of the solid solution UC 1+x Be y up to 1900 deg. C. (author) [fr

  11. The nature of beryllium disease

    International Nuclear Information System (INIS)

    Williams, W.J.

    1977-01-01

    The increasing use of beryllium in modern industry poses a continuing health hazard with a real risk of producing incapacitating disease and even death. Beryllium and its salts are very toxic, even in small doses and may produce lesions in any organ. The majority of cases follow inhalation and may cause either acute or chronic lung disease. Acute pulmonary disease is a form of chemical pneumonitis while the chronic disease is characterised by the production of granulomas and fibrosis. The skin may be affected with the finding of dermatitis, acute or chronic ulceration. Other organs commonly involved include the liver and kidneys. The pathology of beryllium disease is not specific and diagnosis depends on satisfying the following criteria - history of exposure, consistent clinical, radiographic and pathological finding, presence of beryllium in tissue/fluid and evidence of hypersensitivity. Recent development of 'in vitro' tests of hypersensitivity may prove of value in both diagnosis and prevention of disease. Beryllium disease responds to steroid therapy but the only sure treatment is avoidance of exposure. (author)

  12. Microstructural study of hydrogen-implanted beryllium

    International Nuclear Information System (INIS)

    Vagin, S.P.; Chakrov, P.V.; Utkelbayev, B.D.

    1998-01-01

    Hot pressed beryllium (TGP-56) was implanted by 650 keV H + ions to a dose of 6.7 x 10 16 cm -2 at a temperature below 50 C. TEM examinations were performed both at as-irradiated specimens and after post-irradiation annealings at 400-600 C for 15 min. After irradiation, a high density of ''black dot'' defects with a size of about 5 nm is observed in the straggling zone, some of which are resolved as small dislocation loops. During post-irradiation annealing, growth of dislocation loops and oriented gas-filled bubbles are observed in the damaged zone. The bubbles are strongly elongated along the left angle 0001 right angle direction, and their sidelong facts lie along {1-100} planes. These facets have a regular ''toothed'' surface with ''tooth'' facets on {1-100} planes. The size of the ''teeth'' increases with annealing temperature, as well as the total volume of bubbles, with their length growing faster than their width. (orig.)

  13. [Novel irradiation techniques in the treatment of solid tumours. Radiotherapy for metastases].

    Science.gov (United States)

    Mayer, Arpád; Póti, Zsuzsa

    2014-02-23

    Novel developments in percutaneous radiotherapy, such as positron emission tomography/computed tomography, adaptive radiation planning, intensity modulation radiotherapy and intensity modulated arc therapy (RapidArc), as well as the newer generation of image control (cone-beam computed tomography) and image guided radiotherapy ensure increased dosages of planning target volume and clinical target volume of solid tumours without damaging surrounding tissues and providing maximal protection. By raising the dosages of planned target volume and clinical target volume, these novel technical developments have created new indications in the treatment of solid tumours. With the aid of the cone-beam computed tomography and image guided radiotherapy the organ metastasis (lung, liver, spinal cord) and the primary tumour can be treated safety and effectively. Hypofractionation, dose escalation and the use of stereotactic devices can probably decrease radiation damage. The authors review the most common forms of evidence-based fractionation schemes used in irradiation therapy.

  14. The accumulation of disorder, subject to saturation and sputter limitation, in ion irradiated solids

    International Nuclear Information System (INIS)

    Carter, G.; Webb, R.; Collins, R.

    1978-01-01

    The depth distribution of disorder and the depth integrated disorder produced by ion irradiation of solids is analysed theoretically as a function of increasing ion fluence when disorder saturation processes operate at all depths and the solid surface is continuously uniformly eroded by sputtering. The resulting defining equations are evaluated numerically for a Gaussian approximation to the disorder depth function with parameters appropriate to low, equal and high projectile:substrate mass ratio conditions, for several values of sputtering coefficient and effective atom displacement energy. It is shown that the form, if not the magnitude, of the integrated disorder/projectile fluence function is only weakly dependent upon these parameters. More meaningful comparison with depth resolved disorder functions is, however, possible and such a comparison is made for 100 keV Sb projectiles on a Si substrate. (author)

  15. Beryllium-beryllium oxide filter difference spectrometer

    International Nuclear Information System (INIS)

    Goldstone, J.A.; Eckert, J.; Taylor, A.D.; Wood, E.J.

    1982-06-01

    A successful experimental program has been initiated on the filter difference spectrometer. The instrument is most appropriate for energy transfers from about 50 to 600 MeV when moderate energy resolution is sufficient and a high count rate of importance. The difference technique is well enough understood so that peak positions, line widths and integrated intensities can be determined from fairly complex spectra. Several improvements to the instrument are in progress. An important change will be cooling of the sections which is expected to give approximately a factor of two increase in signal. The solid angle subtended by the detector banks will also be increased by a factor of 1.7 without significant degradation in resolution. With these improvements, much smaller samples can be examined in cases where material is unavailable in larger quantities, as well as samples with much small scattering cross sections. The major improvement will come when the proton storage ring becomes operational in 1985. A total increase of approximately 100 in neutrons detected will allow much more difficult experiments to be performed on this instrument with still a fast turnover rate

  16. Hydrogen transport behavior of beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Anderl, R.A.; Hankins, M.R.; Longhurst, G.R.; Pawelko, R.J. (Idaho National Engineering Lab., EG and G Idaho, Inc., Idaho Falls, ID (United States)); Macaulay-Newcombe, R.G. (Dept. of Engineering Physics, Univ. Hamilton, ON (Canada))

    1992-12-01

    Beryllium is being evaluated for use as a plasma-facing material in the International Thermonuclear Experimental Reactor (ITER). One concern in the evaluation is the retention and permeation of tritium implanted into the plasma-facing surface. We performed laboratory-scale studies to investigate mechanisms that influence hydrogen transport and retention in beryllium foil specimens of rolled powder metallurgy product and rolled ingot cast beryllium. Specimen characterization was accomplished using scanning electron microscopy. Auger electron spectroscopy, and Rutherford backscattering spectrometry (RBS) techniques. Hydrogen transport was investigated using ion-beam permeation experiments and nuclear reaction analysis (NRA). Results indicate that trapping plays a significant role in permeation, re-emission, and retention, and that surface processes at both upstream and downstream surfaces are also important. (orig.).

  17. High-strength beryllium block

    International Nuclear Information System (INIS)

    Pinto, N.P.; Keith, G.H.

    1977-01-01

    Beryllium billets hot isopressed using fine powder of high purity have exceptionally attractive properties; average tensile ultimate, 0.2% offset yield strength and elongation are 590 MPa, 430 MPa and 4.0% respectively. Properties are attributed to the fine grain size (about 4.0 μm average diameter) and the relatively low levels of BeO present as fine, well-dispersed particles. Dynamic properties, e.g., fracture toughness, are similar to those of standard grade, high-purity beryllium. The modulus of beryllium is retained to very high stress levels, and the microyield stress or precision elastic limit is higher than for other grades, including instrument grades. Limited data for billets made from normal-purity fine powders show similar room temperature properties. (author)

  18. Cascade diffusion theory of sink capture fluctuations during irradiation of a solid

    International Nuclear Information System (INIS)

    Mansur, L.K.; Brailsford, A.D.; Coghlan, W.A.

    1985-01-01

    Fluctuations in the number of defects captured by sinks in an irradiated solid, that arise because of the stochastic nature of collision cascade events, are analyzed. Two types of sinks are considered, cavities (or voids) and dislocations. The importance of the physical size of the sink is emphasized, as also is the magnitude of the fluctuations in defect capture relative to the behavior of its statistical mean. In particular, it is shown that the ratio of the variance to the mean, for either a cavity or a dislocation segment, decreases rapidly as overall steady state is approached. Further analytical and computational aspects of a shell model that we introduced earlier are analyzed. The relationship of this model to a truly random system is established, and additional calculations are presented to exemplify some of the features predicted by the mathematical analysis. Importance functions describing the spatial origins of the point defects contributing to the average concentration and flux are described. The probabilities of special types of cascade coincidences are developed. The application of the present formalism to the problems of void nucleation, and dislocation climb over localized obstacles, in irradiated solids is indicated

  19. Cause of pitting in beryllium

    International Nuclear Information System (INIS)

    Kershaw, R.P.

    1982-01-01

    Light microscopy, bare-film radiography, secondary ion mass spectroscopy, electron microprobe and physical testing were used to examine beryllium specimens exhibiting a stratified, pitted, pattern after chemical milling. The objective was to find the cause of this pattern. Specimens were found to have voids in excess of density specification allowances. These voids are attributed, at least in part, to the sublimation of beryllium fluoride during the vacuum hot pressing operation. The origin of the pattern is attributed to these voids and etching out of fines and associated impurities. Hot isostatic pressing with a subsequent heat treatment close residual porosity and dispersed impurities enough to correct the problem

  20. Bioenvironmental Engineering Guide to Beryllium

    Science.gov (United States)

    2017-07-26

    Dermal contact with beryllium can result in dermatitis resembling first- or second-degree burns and skin granulomas [7]. Beryllium dust, fume...minute short-term exposure limit (STEL) of 2.0 µg/m3 [§1910.1024(c)(2) & §1926.1124(c)(2)], and added provisions to prevent skin contact [§1910.1024(b...document you want more information, contact the Environmental, Safety, and Occupational Health (ESOH) Service Center at DSN 798-3764, 1-888-232-ESOH (3764

  1. Status of the European R and D on beryllium as multiplier material for breeder blankets

    International Nuclear Information System (INIS)

    Moeslang, A.; Boccaccini, L.V.; Rabaglino, E.; Piazza, G.; Cardella, A.; Sannen, L.; Scibetta, M.; Laan, J. van der; Hegeman, J.B.J.W.

    2004-01-01

    Within the international fusion community a variety of breeding blanket concepts are being considered, ranging from more conservative concepts to higher-risk concepts for fusion power reactors. In Europe, the Helium Cooled Pebble Bed (HCPB) blanket is one of the two reference concepts which will also be tested as Test Blanket Module (TBM) in ITER. In addition to the R and D for structural parts of the HCPB blanket, a considerable effort is devoted to the production and qualification of ceramic breeder and neutron multiplier (beryllium or beryllide) pebble beds. Since in the HCPB blanket pebbles made of lithium ceramics are foreseen, a high volume fraction of beryllium as a neutron multiplier to Li-based ceramic of about 4: l is needed. The typical loading conditions for beryllium are, with a neutron wall load of ∼12.5 MWa/m 2 and in ∼5 years lifetime: T min ∼300degC, T max ∼600-900degC, displacement damage ∼80 dpa, peak 4 He production ∼26000 appm and peak 3 H production ∼700 appm at the End-Of-Life. The behaviour of beryllium under irradiation is considered to be a key issue of the HCPB blanket, because of swelling due to helium bubbles and tritium retention. A large R and D programme on beryllium has been implemented in Europe, aimed at characterising and predicting the material behaviour before and under irradiation. An overview on experimental and modelling activities performed during the past 2 years is given with typical results on non-irradiated and irradiated Beryllium materials and pebble beds and the relevance of major results on future beryllium R and D is addressed. (author)

  2. In-pile thermocycling testing and post-test analysis of beryllium divertor mockups

    Energy Technology Data Exchange (ETDEWEB)

    Giniatulin, R.; Mazul, I. [Efremov Inst., St. Petersburg (Russian Federation); Melder, R.; Pokrovsky, A.; Sandakov, V.; Shiuchkin, A.

    1998-01-01

    The main damaging factors which impact the ITER divertor components are neutron irradiation, cyclic surface heat loads and hydrogen environment. One of the important questions in divertor mockups development is the reliability of beryllium/copper joints and the beryllium resistance under neutron irradiation and thermal cycling. This work presents the experiment, where neutron irradiation and thermocyclic heat loads were applied simultaneously for two beryllium/copper divertor mockups in a nuclear reactor channel to simulate divertor operational conditions. Two mockups with different beryllium grades were mounted facing each other with the tantalum heater placed between them. This device was installed in the active zone of the nuclear reactor SM-2 (Dimitrovgrad, Russia) and the tantalum block was heated by neutron irradiation up to a high temperature. The main part of the heat flux from the tantalum surface was transported to the beryllium surface through hydrogen, as a result the heat flux loaded two mockups simultaneously. The mockups were cooled by reactor water. The device was lowered to the active zone so as to obtain the heating regime and to provide cooling lifted. This experiment was performed under the following conditions: tantalum heater temperature - 1950degC; hydrogen environment -1000 Pa; surface heat flux density -3.2 MW/m{sup 2}; number of thermal cycles (lowering and lifting) -101; load time in each cycle - 200-5000 s; dwell time (no heat flux, no neutrons) - 300-2000 s; cooling water parameters: v - 1 m/s, Tin - 50degC, Pin - 5 MPa; neutron fluence -2.5 x 10{sup 20} cm{sup -2} ({approx}8 years of ITER divertor operation from the start up). The metallographic analysis was performed after experiment to investigate the beryllium and beryllium/copper joint structures, the results are presented in the paper. (author)

  3. Defense programs beryllium good practice guide

    International Nuclear Information System (INIS)

    Herr, M.

    1997-07-01

    Within the DOE, it has recently become apparent that some contractor employees who have worked (or are currently working) with and around beryllium have developed chronic beryllium disease (CBD), an occupational granulomatous lung disorder. Respiratory exposure to aerosolized beryllium, in susceptible individuals, causes an immunological reaction that can result in granulomatous scarring of the lung parenchyma, shortness of breath, cough, fatigue, weight loss, and, ultimately, respiratory failure. Beryllium disease was originally identified in the 1940s, largely in the fluorescent light industry. In 1950, the Atomic Energy Commission (AEC) introduced strict exposure standards that generally curtailed both the acute and chronic forms of the disease. Beginning in 1984, with the identification of a CBD case in a DOE contractor worker, there was increased scrutiny of both industrial hygiene practices and individuals in this workforce. To date, over 100 additional cases of beryllium-specific sensitization and/or CBD have been identified. Thus, a disease previously thought to be largely eliminated by the adoption of permissible exposure standards 45 years ago is still a health risk in certain workforces. This good practice guide forms the basis of an acceptable program for controlling workplace exposure to beryllium. It provides (1) Guidance for minimizing worker exposure to beryllium in Defense Programs facilities during all phases of beryllium-related work, including the decontamination and decommissioning (D ampersand D) of facilities. (2) Recommended controls to be applied to the handling of metallic beryllium and beryllium alloys, beryllium oxide, and other beryllium compounds. (3) Recommendations for medical monitoring and surveillance of workers exposed (or potentially exposed) to beryllium, based on the best current understanding of beryllium disease and medical diagnostic tests available. (4) Site-specific safety procedures for all processes of beryllium that is

  4. Solid solutions of gadolinium doped zinc oxide nanorods by combined microwave-ultrasonic irradiation assisted crystallization

    Science.gov (United States)

    Kiani, Armin; Dastafkan, Kamran; Obeydavi, Ali; Rahimi, Mohammad

    2017-12-01

    Nanocrystalline solid solutions consisting of un-doped and gadolinium doped zinc oxide nanorods were fabricated by a modified sol-gel process utilizing combined ultrasonic-microwave irradiations. Polyvinylpyrrolidone, diethylene glycol, and triethylenetetramine respectively as capping, structure directing, and complexing agents were used under ultrasound dynamic aging and microwave heating to obtain crystalline nanorods. Crystalline phase monitoring, lattice parameters and variation, morphology and shape, elemental analysis, functional groups, reducibility, and the oxidation state of emerged species were examined by PXRD, FESEM, TEM, EDX, FTIR, micro Raman, H2-TPR, and EPR techniques. Results have verified that irradiation mechanism of gelation and crystallization reduces the reaction time, augments the crystal quality, and formation of hexagonal close pack structure of Wurtzite morphology. Besides, dissolution of gadolinium within host lattice involves lattice deformation, unit cell distortion, and angular position variation. Structure related shape and growth along with compositional purity were observed through microscopic and spectroscopic surveys. Furthermore, TPR and EPR studies elucidated more detailed behavior upon exposure to the exerted irradiations and subsequent air-annealing including the formed oxidation states and electron trapping centers, presence of gadolinium, zinc, and oxygen disarrays and defects, as well as alteration in the host unit cell via gadolinium addition.

  5. Effect of radiation quality on radical formation in ion-irradiated solid alanine

    Energy Technology Data Exchange (ETDEWEB)

    Koizumi, Hitoshi; Ichikawa, Tsuneki; Yoshida, Hiroshi [Hokkaido Univ., Sapporo (Japan); Namba, Hideki; Taguchi, Mitsumasa; Kojima, Takuji

    1997-03-01

    Radical formation in solid alanine irradiated with H{sup +} and He{sup +} ions of 0.5-3.0 MeV and with heavy ions of hundreds of MeV was examined by the ESR method. Radical yield is constant below a critical fluence, and the yield decreases above the fluence. The critical fluence for the H{sup +} and He{sup +} ions is about 10{sup 12} ions cm{sup -2}, while the critical fluence for the heavy ions is 10{sup 10}-10{sup 11} ions cm{sup -2}. G-value of the radical formation (radicals per 100 eV absorbed dose) is obtained from the constant yield at the low fluences. The G-value depends on the radiation quality. This dependence is ascribed to the difference of local dose in the ion tracks. The fluence-yield curves were simulated with a model assuming cylindrical shape of ion tracks and dose-yield relationship for {gamma}-irradiation. This model well explains the fluence-yield curves for the ion irradiations. (author)

  6. Inhalation hazards from machining beryllium metal

    International Nuclear Information System (INIS)

    Hoover, M.D.; Finch, G.L.; Mewhinney, J.A.; Eidson, A.F.

    1987-01-01

    Beryllium metal has special nuclear and structural properties that make it useful for applications in fission and fusion reactor designs. Unfortunately, concerns for its toxicity have made designers wary of using beryllium metal. The work being reported here was undertaken to characterize the aerosols produced by two very common operations performed during preparation or modification of components for use in reactor systems: sawing and milling of beryllium metal. The study also covered beryllium metal alloys to allow comparison. Information from this study is to enable better assessments of the risk of using beryllium metal in reactor designs

  7. Paramagnetic centers in ternary coordinated oxygen in beryllium aluminosilicate glasses

    International Nuclear Information System (INIS)

    Blaginina, L.A.; Zatsepin, A.F.; Dmitriev, I.A.

    1988-01-01

    Glasses of the composition 3BeO-Al 2 O 3 -6SiO 2 containing a homogenizing additive of MgF 2 were synthesized. The ESR spectra of x-ray and gamma irradiated specimens were determined. A complex ESR spectrum arose in the original glass. The ESR spectrum of the gamma-irradiated polycrystalline Be 2 SiO 4 glass was almost identical to the crystallized glass. It was shown that the presence of beryllium atoms in the composition of silicate glasses created the conditions for the formation of structural fragments with ternary coordinated oxygen

  8. Optimization of beryllium for fusion blanket applications

    International Nuclear Information System (INIS)

    Billone, M.C.

    1993-01-01

    The primary function of beryllium in a fusion reactor blanket is neutron multiplication to enhance tritium breeding. However, because heat, tritium and helium will be generated in and/or transported through beryllium and because the beryllium is in contact with other blanket materials, the thermal, mechanical, tritium/helium and compatibility properties of beryllium are important in blanket design. In particular, tritium retention during normal operation and release during overheating events are safety concerns. Accommodating beryllium thermal expansion and helium-induced swelling are important issues in ensuring adequate lifetime of the structural components adjacent to the beryllium. Likewise, chemical/metallurgical interactions between beryllium and structural components need to be considered in lifetime analysis. Under accident conditions the chemical interaction between beryllium and coolant and breeding materials may also become important. The performance of beryllium in fusion blanket applications depends on fabrication variables and operational parameters. First the properties database is reviewed to determine the state of knowledge of beryllium performance as a function of these variables. Several design calculations are then performed to indicate ranges of fabrication and operation variables that lead to optimum beryllium performance. Finally, areas for database expansion and improvement are highlighted based on the properties survey and the design sensitivity studies

  9. Reactivity test between beryllium and copper

    International Nuclear Information System (INIS)

    Kawamura, H.; Kato, M.

    1995-01-01

    Beryllium has been expected for using as plasma facing material on ITER. And, copper alloy has been proposed as heat sink material behind plasma facing components. Therefore, both materials must be joined. However, the elementary process of reaction between beryllium and copper alloy does not clear in detail. For example, other authors reported that beryllium reacted with copper at high temperature, but it was not obvious about the generation of reaction products and increasing of the reaction layer. In the present work, from this point, for clarifying the elementary process of reaction between beryllium and copper, the out-of-pile compatibility tests were conducted with diffusion couples of beryllium and copper which were inserted in the capsule filled with high purity helium gas (6N). Annealing temperatures were 300, 400, 500, 600 and 700 degrees C, and annealing periods were 100, 300 and 1000h. Beryllium specimens were hot pressed beryllium, and copper specimens were OFC (Oxygen Free Copper)

  10. Galvanic corrosion of beryllium welds

    International Nuclear Information System (INIS)

    Hill, M.A.; Butt, D.P.; Lillard, R.S.

    1997-01-01

    Beryllium is difficult to weld because it is highly susceptible to cracking. The most commonly used filler metal in beryllium welds is Al-12 wt.% Si. Beryllium has been successfully welded using Al-Si filler metal with more than 30 wt.% Al. This filler creates an aluminum-rich fusion zone with a low melting point that tends to backfill cracks. Drawbacks to adding a filler metal include a reduction in service temperature, a lowering of the tensile strength of the weld, and the possibility for galvanic corrosion to occur at the weld. To evaluate the degree of interaction between Be and Al-Si in an actual weld, sections from a mock beryllium weldment were exposed to 0.1 M Cl - solution. Results indicate that the galvanic couple between Be and the Al-Si weld material results in the cathodic protection of the weld and of the anodic dissolution of the bulk Be material. While the cathodic protection of Al is generally inefficient, the high anodic dissolution rate of the bulk Be during pitting corrosion combined with the insulating properties of the Be oxide afford some protection of the Al-Si weld material. Although dissolution of the Be precipitate in the weld material does occur, no corrosion of the Al-Si matrix was observed

  11. Worker Environment Beryllium Characterization Study

    International Nuclear Information System (INIS)

    2009-01-01

    This report summarizes the conclusion of regular monitoring of occupied buildings at the Nevada Test Site and North Las Vegas facility to determine the extent of beryllium (Be) contamination in accordance with Judgment of Needs 6 of the August 14, 2003, 'Minnema Report.'

  12. Worker Environment Beryllium Characterization Study

    Energy Technology Data Exchange (ETDEWEB)

    NSTec Environment, Safety, Health & Quality

    2009-12-28

    This report summarizes the conclusion of regular monitoring of occupied buildings at the Nevada Test Site and North Las Vegas facility to determine the extent of beryllium (Be) contamination in accordance with Judgment of Needs 6 of the August 14, 2003, “Minnema Report.”

  13. Multiscale modelling of hydrogen behaviour on beryllium (0001 surface

    Directory of Open Access Journals (Sweden)

    Ch. Stihl

    2016-12-01

    Full Text Available Beryllium is proposed to be a neutron multiplier and plasma facing material in future fusion devices. Therefore, it is crucial to acquire an understanding of the microscopic mechanisms of tritium accumulation and release as a result of transmutation processes that Be undergoes under neutron irradiation. A multiscale simulation of ad- and desorption of hydrogen isotopes on the beryllium (0001 surface is developed. It consists of ab initio calculations of certain H adsorption configurations, a suitable cluster expansion approximating the energies of arbitrary configurations, and a kinetic Monte Carlo method for dynamic simulations of adsorption and desorption. The processes implemented in the kinetic Monte Carlo simulation are deduced from further ab initio calculations comprising both, static relaxation as well as molecular dynamics runs. The simulation is used to reproduce experimental data and the results are compared and discussed. Based on the observed results, proposals for a refined model are made.

  14. Protection of a protein against irradiation-induced degradation by additives in the solid state

    International Nuclear Information System (INIS)

    Shalaev, E.; Reddy, R.; Kimball, R.N.; Weinschenk, M.F.; Guinn, M.; Margulis, L.

    2003-01-01

    The impact of ionizing radiation on a globular protein (porcine somatotropin, pST) in the solid state was studied using rate of dissolution, high-performance liquid chromatography, and Electron spin resonance (ESR) in the presence of different additives. o-Vanillin stabilized pST against irradiation-induced degradation whereas effects of trolox and isopropyl alcohol were less significant. Stabilization effect of o-vanillin has been related to the energy transfer from pST molecules to the additive which was facilitated by formation of covalent bonds between o-vanillin and pST molecules. Anticorrelation between the level of free radicals and chemical degradation (i.e. degradation increased with decrease in a free radical level) was observed in the presence of o-vanillin

  15. OVERVIEW OF BERYLLIUM SAMPLING AND ANALYSIS

    Energy Technology Data Exchange (ETDEWEB)

    Brisson, M

    2009-04-01

    Because of its unique properties as a lightweight metal with high tensile strength, beryllium is widely used in applications including cell phones, golf clubs, aerospace, and nuclear weapons. Beryllium is also encountered in industries such as aluminium manufacturing, and in environmental remediation projects. Workplace exposure to beryllium particulates is a growing concern, as exposure to minute quantities of anthropogenic forms of beryllium may lead to sensitization and to chronic beryllium disease, which can be fatal and for which no cure is currently known. Furthermore, there is no known exposure-response relationship with which to establish a 'safe' maximum level of beryllium exposure. As a result, the current trend is toward ever lower occupational exposure limits, which in turn make exposure assessment, both in terms of sampling and analysis, more challenging. The problems are exacerbated by difficulties in sample preparation for refractory forms of beryllium, such as beryllium oxide, and by indications that some beryllium forms may be more toxic than others. This chapter provides an overview of sources and uses of beryllium, health risks, and occupational exposure limits. It also provides a general overview of sampling, analysis, and data evaluation issues that will be explored in greater depth in the remaining chapters. The goal of this book is to provide a comprehensive resource to aid personnel in a wide variety of disciplines in selecting sampling and analysis methods that will facilitate informed decision-making in workplace and environmental settings.

  16. Mechanisms of hydrogen retention in metallic beryllium and beryllium oxide and properties of ion-induced beryllium nitride

    International Nuclear Information System (INIS)

    Oberkofler, Martin

    2011-01-01

    In the framework of this thesis laboratory experiments on atomically clean beryllium surfaces were performed. They aim at a basic understanding of the mechanisms occurring upon interaction of a fusion plasma with a beryllium first wall. The retention and the temperature dependent release of implanted deuterium ions are investigated. An atomistic description is developed through simulations and through the comparison with calculations based on density functional theory. The results of these investigations are compared to the behaviour of hydrogen upon implantation into thermally grown beryllium oxide layers. Furthermore, beryllium nitride is produced by implantation of nitrogen into metallic beryllium and its properties are investigated. The results are interpreted with regard to the use of beryllium in a fusion reactor. (orig.)

  17. The Status of Beryllium Research for Fusion in the United States

    International Nuclear Information System (INIS)

    Glen R. Longhurst

    2003-01-01

    Use of beryllium in fusion reactors has been considered for neutron multiplication in breeding blankets and as an oxygen getter for plasma-facing surfaces. Previous beryllium research for fusion in the United States included issues of interest to fission (swelling and changes in mechanical and thermal properties) as well as interactions with plasmas and hydrogen isotopes and methods of fabrication. When the United States formally withdrew its participation in the International Thermonuclear Experimental Reactor (ITER) program, much of this effort was terminated. The focus in the U.S. has been mainly on toxic effects of beryllium and on industrial hygiene and health-related issues. Work continued at the INEEL and elsewhere on beryllium-containing molten salts. This activity is part of the JUPITER II Agreement. Plasma spray of ITER first wall samples at Los Alamos National Laboratory has been performed under the European Fusion Development Agreement. Effects of irradiation on beryllium structure are being studied at Oak Ridge National Laboratory. Numerical and phenomenological models are being developed and applied to better understand important processes and to assist with design. Presently, studies are underway at the University of California Los Angeles to investigate thermo-mechanical characteristics of beryllium pebble beds, similar to research being carried out at Forschungszentrum Karlsruhe and elsewhere. Additional work, not funded by the fusion program, has dealt with issues of disposal, and recycling

  18. Investigation of the mechanism of interaction of Lithium 6 ions on Beryllium 9

    International Nuclear Information System (INIS)

    Coste, Mireille

    1962-01-01

    The objective of this research on the interaction of Lithium 6 and Beryllium 9 ions is to obtain new indications on the mode of interaction of these heavy ions, and on the configuration of target nuclei and projectile nuclei. In a first part, the author presents and describes the experimental conditions which comprise a Van de Graaff accelerator, a source, a stripper, and a target. He reports the study of α particles emitted by the reaction between the Lithium and Beryllium ions: description of the experimental installation (irradiation chamber and method), presentation and interpretation of experimental results. In the next part, he reports the study of Lithium 7 and Beryllium 10 nuclides emitted by disintegration of Beryllium 11: description of experimental conditions, variations of cross sections, variation of the cross section rate, and interpretation. The author then addresses the study of the intervention of the mode of interaction by 15 N compound nucleus in the reactions between lithium and beryllium ions: study of intensities of the different spectrum lines, measurement of the Doppler effect produced of the 479 keV line, interpretation of results. In conclusion, the author analyses the mechanism of interaction between lithium and beryllium ions, and discusses different theories: the Newns and Glendenning theories, and the Leigh theory

  19. The status of beryllium research for fusion in the United States

    International Nuclear Information System (INIS)

    Longhurst, G.R.; Snead, L.L.; Abou-Sena, A.A.

    2004-01-01

    Use of beryllium in fusion reactor has been considered for neutron multiplication in breeding blankets an as an oxygen getter for plasma - facing surface. Previous beryllium research for fusion in the United States included issues of interest to fission (swelling an changes in mechanical and thermal properties) as well as interactions with plasmas and hydrogen isotopes and methods of fabrication. When the United States formally withdrew its participation in the International Experimental Reactor (ITER) program, much of this effort was terminated. The focus in the U.S. has been mainly on toxic effects of beryllium and on industrial hygiene and health-related issues. Work continued at the INEEL (Idaho National Engineering and Environmental Laboratory) and elsewhere on beryllium-containing molten salts. This activity is part of the JUPITER II Agreement. Plasma spray of ITER first wall samples at Los Alamos National Laboratory has been performed under the European Fusion Development Agreement. Effects of irradiation on beryllium structure are being studied at Oak Ridge National Laboratory. Numerical and phenomenological models are being developed and applied at the University of California Los Angels to investigate thermo-mechanical characteristics of beryllium pebble beds, similar to research being carried out at Forschungszentrum Karlsruhe and elsewhere. Additional work, not funded by the fusion program, has dealt with issues of disposal, and recycling. (author)

  20. A diethylhydroxylaminate based mixed lithium/beryllium aggregate

    Energy Technology Data Exchange (ETDEWEB)

    Berger, Raphael J.F. [Paris-Lodron Universitaet Salzburg (Austria). Fachbereich fuer Materialwissenschaften und Physik; Jana, Surajit [Asansol Girls College, West-Bengal (India). Dept. of Chemistry; Froehlich, Roland [Muenster Univ. (Germany). Organisch-Chemisches Inst.; Mitzel, Norbert W. [Bielefeld Univ. (Germany). Anorganische Chemie und Strukturchemie

    2015-07-01

    A mixed lithium/beryllium diethylhydroxylaminate compound containing {sup n}butyl beryllium units of total molecular composition {sup n}Be(ONEt{sub 2}){sub 2} [(LiONEt{sub 2}){sup 2} {sup n}BuBeONEt{sub 2}]{sub 2} (1) was isolated from a reaction mixture of {sup n}butyl lithium, N,N-diethylhydroxylamine and BeCl{sub 2} in diethylether/thf. The crystal structure of 1 has been determined by X-ray diffraction. The aggregate is composed of two ladder-type subunits connected in a beryllium-centered distorted tetrahedron of four oxygen atoms. Only the lithium atoms are engaged in coordination with the nitrogen donor atoms. The DFT calculations support the positional occupation determined for Li and Be in the crystal structure. The DFT and the solid-state structure are in excellent agreement, indicating only weak intermolecular interactions in the solid state. Structural details of metal atom coordination are discussed.

  1. Defense programs beryllium good practice guide

    Energy Technology Data Exchange (ETDEWEB)

    Herr, M.

    1997-07-01

    Within the DOE, it has recently become apparent that some contractor employees who have worked (or are currently working) with and around beryllium have developed chronic beryllium disease (CBD), an occupational granulomatous lung disorder. Respiratory exposure to aerosolized beryllium, in susceptible individuals, causes an immunological reaction that can result in granulomatous scarring of the lung parenchyma, shortness of breath, cough, fatigue, weight loss, and, ultimately, respiratory failure. Beryllium disease was originally identified in the 1940s, largely in the fluorescent light industry. In 1950, the Atomic Energy Commission (AEC) introduced strict exposure standards that generally curtailed both the acute and chronic forms of the disease. Beginning in 1984, with the identification of a CBD case in a DOE contractor worker, there was increased scrutiny of both industrial hygiene practices and individuals in this workforce. To date, over 100 additional cases of beryllium-specific sensitization and/or CBD have been identified. Thus, a disease previously thought to be largely eliminated by the adoption of permissible exposure standards 45 years ago is still a health risk in certain workforces. This good practice guide forms the basis of an acceptable program for controlling workplace exposure to beryllium. It provides (1) Guidance for minimizing worker exposure to beryllium in Defense Programs facilities during all phases of beryllium-related work, including the decontamination and decommissioning (D&D) of facilities. (2) Recommended controls to be applied to the handling of metallic beryllium and beryllium alloys, beryllium oxide, and other beryllium compounds. (3) Recommendations for medical monitoring and surveillance of workers exposed (or potentially exposed) to beryllium, based on the best current understanding of beryllium disease and medical diagnostic tests available. (4) Site-specific safety procedures for all processes of beryllium that is likely to

  2. Irradiation and accretion of solids in space based on observations of lunar rocks and grains

    International Nuclear Information System (INIS)

    Lal, D.

    1977-01-01

    Clues to a wide range of questions relating to the origin and evolution of the solar system and dynamic physical and electromagnetic processes occurring concurrently and in the past in our galaxy have been provided by a study of the lunar samples. This information is deduced from a variety of complementary physical and chemical evidence. In this presentation greatest emphasis is laid on information based on effects arising from interactions of low energy cosmic rays with lunar surface materials. The present discussions concern the nature of experimental data to date and implications thereof to the charged particle environment of the Moon, ancient magnetic fields and the nature of time scales involved in the irradiation and accretion of solids in space, based on lunar regolith dynamics. It becomes clear that there does not yet exist any consensus on the absolute values of charged particle or the meteorite fluxes, and also about the details of the evolution of the lunar regolith. The complex history of evolution of lunar material is slowly being understood and it is hoped that a great deal of quantitative information will soon be available which will in turn allow discussion of evolution of solid bodies in the solar system. (author)

  3. Beryllium minerals - demand strong for miniaturisation

    International Nuclear Information System (INIS)

    Griffiths, J.

    1985-01-01

    Beryllium is an essential constituent of over 40 minerals of which two are exploited commercially. Beryl is largely produced in the USSR and China and bertrandite in the U.S.A. Phenacite, from Canada, is also under investigation. The largest extraction plant for the recovery of beryllium in the western world is in Utah, U.S.A. and the company also produces beryllium oxide used in the manufacture of ceramics widely used in the electronics industry and for refractory articles. Beryllium-copper alloys in strip, rod and tube form are produced in the U.S.A., Germany and the U.K. Beryllium ceramics are important because of their high thermal conductivity, electrical insulation, strength and rigidity. The alloys, used as electric connectors, microswitch contacts are important for their high suitability for miniaturisation. The future growth potential for the beryllium industry is in the automotive industries in Europe and Japan. (U.K.)

  4. Method for hot pressing beryllium oxide articles

    Science.gov (United States)

    Ballard, Ambrose H.; Godfrey, Jr., Thomas G.; Mowery, Erb H.

    1988-01-01

    The hot pressing of beryllium oxide powder into high density compacts with little or no density gradients is achieved by employing a homogeneous blend of beryllium oxide powder with a lithium oxide sintering agent. The lithium oxide sintering agent is uniformly dispersed throughout the beryllium oxide powder by mixing lithium hydroxide in an aqueous solution with beryllium oxide powder. The lithium hydroxide is converted in situ to lithium carbonate by contacting or flooding the beryllium oxide-lithium hydroxide blend with a stream of carbon dioxide. The lithium carbonate is converted to lithium oxide while remaining fixed to the beryllium oxide particles during the hot pressing step to assure uniform density throughout the compact.

  5. Dependence of secondary ion emission current on the composition of beryllium-nickel alloys

    International Nuclear Information System (INIS)

    Pistryak, V.M.; Kozlov, V.F.; Tikhinskij, G.F.; Fogel', Ya.M.

    1976-01-01

    The dependence is studied of the secondary ions emission current on the composition of beryllium-nickel alloys. It is established that appearance of intermetallide phases in the Be-Ni alloys has no effect on the linear character of the secondary ions Ni + and Be + of emission current. The phase transformation from the solid solution to the compound Ni 5 Be 21 with a change in the alloys concentration is fixed by appearance of the secondary ion NiBe + emission. The limited solubility of nickel in solid beryllium at a temperature close to room temperature is determined to be equal to 1.3+-0.27 at%

  6. MEASUREMENTS OF THE PROPERTIES OF BERYLLIUM FOIL

    International Nuclear Information System (INIS)

    ZHAO, Y.; WANG, H.

    2000-01-01

    The electrical conductivity of beryllium at radio frequency (800 MHz) and liquid nitrogen temperature were investigated and measured. This summary addresses a collection of beryllium properties in the literature, an analysis of the anomalous skin effect, the test model, the experimental setup and improvements, MAFIA simulations, the measurement results and data analyses. The final results show that the conductivity of beryllium is not as good as indicated by the handbook, yet very close to copper at liquid nitrogen temperature

  7. New audio applications of beryllium metal

    International Nuclear Information System (INIS)

    Sato, M.

    1977-01-01

    The major applications of beryllium metal in the field of audio appliances are for the vibrating cones for the two types of speakers 'TWITTER' for high range sound and 'SQUAWKER' for mid range sound, and also for beryllium cantilever tube assembled in stereo cartridge. These new applications are based on the characteristic property of beryllium having high ratio of modulus of elasticity to specific gravity. The production of these audio parts is described, and the audio response is shown. (author)

  8. Thermal expansion of beryllium oxide

    International Nuclear Information System (INIS)

    Solodukhin, A.V.; Kruzhalov, A.V.; Mazurenko, V.G.; Maslov, V.A.; Medvedev, V.A.; Polupanova, T.I.

    1987-01-01

    Precise measurements of temperature dependence of the coefficient of linear expansion in the 22-320 K temperature range on beryllium oxide monocrystals are conducted. A model of thermal expansion is suggested; the range of temperature dependence minimum of the coefficient of thermal expansion is well described within the frames of this model. The results of the experiment may be used for investigation of thermal stresses in crystals

  9. Intoxication experiments with beryllium sulphate

    International Nuclear Information System (INIS)

    Bucurescu, I.; Stan, T.

    1990-01-01

    The changes in the particular number of animals in two groups of 40 rats each subjected to intoxication experiments with beryllium sulphate was investigated. The two investigations had very different characteristics. In the case of chronic intoxication there was a marked lethality over given time intervals. In the case of subacute intoxication the number of animals decreased with time. It was found empirically that this change can be described by an exponential relationship which lends itself to statistical interpretation. (author)

  10. Thermodynamic properties of beryllium hydroxide

    International Nuclear Information System (INIS)

    Baur, A.; Lecocq, A.

    1964-01-01

    The study of the hydro-thermal decomposition of beryllium hydroxide has made it possible to determine the free energy of formation and the entropy. The results obtained are in good agreement with the theoretical values calculated from the solubility product of this substance. They give furthermore the possibility of acquiring a better understanding of the BeO-H 2 O-Be (OH) 2 system between 20 and 1500 C. (authors) [fr

  11. (Beryllium). Internal Report No. 137, Jan. 15, 1958

    International Nuclear Information System (INIS)

    Mouret, P.; Rigaud, A.

    1959-01-01

    After a brief summary of the physical and chemical properties of beryllium, the various chemical treatments which can be applied to beryllium minerals either directly or after a physical enrichment are discussed. These various treatments give either the hydroxide or beryllium salts, from which either beryllium oxide or metallic beryllium can easily be obtained. The purification, analysis and uses of beryllium are also briefly discussed. (author)

  12. Beryllium dust generation resulting from plasma bombardment

    International Nuclear Information System (INIS)

    Doerner, R.; Mays, C.

    1997-01-01

    The beryllium dust resulting from erosion of beryllium samples subjected to plasma bombardment has been measured in PISCES-B. Loose surface dust was found to be uniformly distributed throughout the device and accounts for 3% of the eroded material. A size distribution measurement of the loose surface dust shows an increasing number of particles with decreasing diameter. Beryllium coatings on surfaces with a line of sight view of the target interaction region account for an additional 33% of the eroded beryllium material. Flaking of these surface layers is observed and is thought to play a significant role in dust generation inside the vacuum vessel. (orig.)

  13. Microplasticity in hot-pressed beryllium

    International Nuclear Information System (INIS)

    Plane, D.C.; Bonfield, W.

    1977-01-01

    Closed hysteresis loops measured in the microstrain region of hot pressed, commercially pure, polycrystalline beryllium are correlated with a dislocation - impurity atom, energy dissipating mechanism. (author)

  14. Beryllium thin films for resistor applications

    Science.gov (United States)

    Fiet, O.

    1972-01-01

    Beryllium thin films have a protective oxidation resistant property at high temperature and high recrystallization temperature. However, the experimental film has very low temperature coefficient of resistance.

  15. Determination of inorganic beryllium species in the particulate matter of emissions and working areas

    Energy Technology Data Exchange (ETDEWEB)

    Profumo, A.; Spini, G.; Cucca, L.; Pesavento, M. [Dipartimento di Chimica Gen., Pavia (Italy)

    2002-07-01

    A sequential extraction procedure for separating and determining Be(0), soluble Be(II) inorganic compounds, BeO and beryllium silicates in samples, such as particulate matter of emissions and working areas, has been developed. The proposed procedure has been tested on synthetic samples prepared with the inorganic beryllium compounds, in the presence of atmospherical particulate matter sampled in a laboratory, previously checked for the absence of beryllium. The speciation was then repeated on a sample of fly ash deriving from a solid waste incinerator and on a reference material (Coal Fly ash SRM 1633a, by NIST), followed by an evaluation of matrix spiking and recovery analyses. Performing multiple analyses of the spiked samples assessed the repeatability of the procedure. Quantitative determinations have been made by inductively coupled plasma optical emission spectrometry (ICP-OES) and electrothermal atomic absorption spectrometry (ETAAS). The possible interferences of the most common ions have been investigated. The selective sequential extractions allow one to separate and to determine different inorganic beryllium species, to which a different toxicity and therefore, a different risk are related: it is the case for example of metallic beryllium and beryllium oxide.

  16. The occurrence of recruitment supported from the finding of an increase in radiosensitivity of quiescent cells in solid tumors after fractionated irradiation with X-rays

    International Nuclear Information System (INIS)

    Masunaga, Shinichiro; Ono, Koji; Kinashi, Yuko; Suzuki, Minoru; Akaboshi, Mitsuhiko

    1998-01-01

    We examined the behavior of quiescent cells in solid tumors irradiated twice at various intervals with X-rays, using our recently developed method for selectively detecting the response of quiescent cells in solid tumors. To determine the labeling indices of tumors at the second irradiation, each mouse group included mice that were continuously administered BrdU until just before the second irradiation using mini-osmotic pumps which had been implanted before the first irradiation. Radiosensitivity of total tumor cells at the second irradiation decreased in proportion to the increase in interval time. However, radiosensitivity of quiescent cells was raised with increase in the interval time. In addition, the labeling index at the second irradiation was higher than that at the first irradiation. These findings supported the occurrence of recruitment from quiescent to proliferating state during fractionated irradiation. (author)

  17. Long-Range Electron Effects upon Irradiation of Molecular Solids and Polymers

    International Nuclear Information System (INIS)

    Feldman, V.I.

    2006-01-01

    Long-range electron effects are responsible for specific localization and selectivity of the radiation-induced chemical transformations occurring in molecular solids and polymers, when the classic diffusion mobility is essentially restricted. In particullar, understanding of the effects of this kind may be of key significance for establishing new ways to control the radiation sensitivity of macromolecules and organized polymeric systems, nanomaterials and biopolymers. This talk will present an overview of model studies of the long-range electron effects with the characteristic scale from several angstroms to ten nanometers. The following aspects of the problem will be analyzed: (1) Positive hole delocalization in ionized molecules. This phenomenon has been demonstrated experimentally and confirmed by quantum chemical calculations for a number of various-type molecules (alkanes, conjugated polyenes, bifunctional compounds). The effective delocalization length was found to be up to 2 nm (or even larger). The role of this effect in site-selective radiation chemistry will be discussed in the frame of concepts of distributed reactivity and 'switching' between delocalized and localized states. (2) Trap-to-trap positive hole and electron migration between isolated molecules or functional groups. The characteristic distance for this process was estimated to be 2 to 4 nm. Special impact will be made on the possible role of this process in selection of specific isomers or conformers upon irradiation of complex systems and macromolecules. (3) The effects of long-range scavenging of low-energy secondary electrons in polymers and organized polymeric systems. As revealed by model experiments, the radius of electron capture in solid polymers may be in the range of 1 to 10 nm. Possible implications of scavenging effects for controlling the radiation chemistry of polymers and organized polymeric systems will be considered

  18. Some structural characteristics of gamma-irradiated pure and Li2O-doped NiO solids

    International Nuclear Information System (INIS)

    Ramadan, A.A.; Dessouki, A.M.

    1989-01-01

    The induced structural changes, due to Li 2 O-doping (2.5 mol%) and γ-irradiation (10-80 Mrad), of NiO were investigated by XRD analyses. The results obtained revealed that lithium-doping resulted in a significant increase in the internal strain and a decrease in lattice parameter. These changes were explained in terms of creation of Ni 3+ ions in the doped solids. γ-Irradiation of pure and doped solids effected a decrease in both crystallite size and microstrain upon subjecting to doses of 20 and 30 Mrad. Higher doses induced an increase in both parameters in the case of pure NiO and a further decrease in case of the doped solid. These results were attributed to splitting of the large strained crystallites and to an activated sintering of the small strained ones. γ-Irradiation effected also an increase in the lattice parameters of pure and doped solids due to removal of some excess oxygen with subsequent decrease in the concentration of Ni 3+ ions. (author)

  19. Beryllium and growth. II. The effect of beryllium on plant growth

    Energy Technology Data Exchange (ETDEWEB)

    Hoagland, M B

    1952-01-01

    Experiments were undertaken to determine whether beryllium could replace magnesium in a growing organism. This was stimulated by the several known growth effects of beryllium in animals and by the fact that beryllium apparently competes with magnesium for animal alkaline phosphatases. The following findings are noted: (1) beryllium can reduce the magnesium requirement of plants by some 60% within a certain range of magnesium deficiency. (2) The residual obligatory magnesium requirements is probably accounted for by chlorophyll since beryllium appears to have no primary effect on chlorophyll or chlorophyll production. (3) The pH of the nutrient solution is critical: at acid pH's, beryllium is highly toxic, and growth increase due to beryllium only appears at initial pH's above 11.2, although this initial pH rapidly falls to neutrality during the experimental period. 22 references, 4 figures, 1 table.

  20. Criteria for formation of low-frequency sound under wide-aperture repetitively pulsed laser irradiation of solids

    International Nuclear Information System (INIS)

    Tishchenko, V N; Posukh, V G; Gulidov, A I; Zapryagaev, V I; Pavlov, A A; Boyarintsev, Ye L; Golubev, M P; Kavun, I N; Melekhov, A V; Golobokova, L S; Miroshnichenko, I B; Pavlov, Al A; Shmakov, A S

    2011-01-01

    The criteria for merging shock waves formed by optical breakdowns on the surface of solids have been investigated. Targets made of different materials were successively irradiated by two CO 2 -laser pulses with energies up to 200 J and a duration of ∼1 μs. It is shown that the criteria under consideration can be applied to different targets and irradiation regimes and make it possible to calculate the parameters of repetitively pulsed laser radiation that are necessary to generate low-frequency sound and ultrasound in air.

  1. Beryllium in aircraft brakes - a summary

    International Nuclear Information System (INIS)

    Zenczak, S.

    1977-01-01

    Beryllium has been in use in aircraft brakes for ten years. During the original design phases of the several aircraft programs using beryllium a number of problems requiring solution confronted the designers. In actual service the solution to these problems performed much better than had been anticipated. A summary is presented. (author)

  2. ICT diagnostic method of beryllium welding quality

    International Nuclear Information System (INIS)

    Sun Lingxia; Wei Kentang; Ye Yunchang

    2002-01-01

    To avoid the interference of high density material for the quality assay of beryllium welding line, a slice by slice scanning method was proposed based upon the research results of the Industrial Computerized Tomography (ICT) diagnostics for weld penetration, weld width, off-centered deviation and weld defects of beryllium-ring welding seam with high density material inside

  3. Investigation of beryllium/steam interaction

    Energy Technology Data Exchange (ETDEWEB)

    Chekhonadskikh, A.M.; Vurim, A.D.; Vasilyev, Yu.S.; Pivovarov, O.S. [Inst. of Atomic Energy National Nuclear Center of the Republic of Kazakstan Semipalatinsk (Kazakhstan); Shestakov, V.P.; Tazhibayeva, I.L.

    1998-01-01

    In this report program on investigations of beryllium emissivity and transient processes on overheated beryllium surface attacked by water steam to be carried out in IAE NNC RK within Task S81 TT 2096-07-16 FR. The experimental facility design is elaborated in this Report. (author)

  4. Modeling of hydrogen interactions with beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Longhurst, G.R. [Lockheed Martin Idaho Technologies Co., Idaho Falls, ID (United States)

    1998-01-01

    In this paper, improved mathematical models are developed for hydrogen interactions with beryllium. This includes the saturation effect observed for high-flux implantation of ions from plasmas and retention of tritium produced from neutronic transmutations in beryllium. Use of the models developed is justified by showing how they can replicated experimental data using the TMAP4 tritium transport code. (author)

  5. Managing health effects of beryllium exposure

    National Research Council Canada - National Science Library

    Committee on Beryllium Alloy Exposures; Committee on Toxicology; National Research Council; Division on Earth and Life Studies; National Research Council

    2008-01-01

    ... to its occurrence in exposed people. Despite reduced workplace exposure, chronic beryllium disease continues to occur. In addition, beryllium has been classified as a likely human carcinogen by several agencies, such as the International Agency for Research on Cancer, the National Toxicology Program, and the U.S. Environmental Protection Agency. Thos...

  6. Structure investigations of some beryllium materials

    Energy Technology Data Exchange (ETDEWEB)

    Faeldt, I; Lagerberg, G

    1960-05-15

    Metallographic structure, microhardness and texture have been studied on various types of beryllium metal including hot pressed powder, a rolled strip and an extruded tube It was found that beryllium exhibits its highest hardness in directions perpendicular to the basal plane. Good ideas of the prevailing textures were obtained with an ordinary X-ray diffractometer.

  7. Structure investigations of some beryllium materials

    International Nuclear Information System (INIS)

    Faeldt, I.; Lagerberg, G.

    1960-05-01

    Metallographic structure, microhardness and texture have been studied on various types of beryllium metal including hot pressed powder, a rolled strip and an extruded tube It was found that beryllium exhibits its highest hardness in directions perpendicular to the basal plane. Good ideas of the prevailing textures were obtained with an ordinary X-ray diffractometer

  8. Surface composition variation and high-vacuum performance of DLC/ILs solid-liquid lubricating coatings: Influence of space irradiation

    International Nuclear Information System (INIS)

    Liu Xiufang; Wang Liping; Pu Jibin; Xue Qunji

    2012-01-01

    In this paper, we fabricated a DLC/ionic liquid (DLC/ILs) solid-liquid lubricating coating and investigated the effect of atomic oxygen (AO), ultraviolet (UV), proton and electron irradiations on composition, structure, morphology and tribological properties of the DLC/ILs solid-liquid lubricating coatings. A ground-based simulation facility was employed to carry out the irradiation experiments. X-ray photoelectron spectroscope (XPS), Raman spectra, and Fourier Transform Infrared Spectroscopy (FTIR) were used to analyzed the structure and composition changes of DLC film and IL lubricant before and after irradiations. The tribological behavior of the DLC/ILs solid-liquid lubricating coating before and after irradiations was investigated by a vacuum tribometer with the pressure of 10 -5 Pa. The experimental results revealed that irradiations induced the structural changes, including oxidation, bond break and crosslinking reactions of DLC film and IL lubricant. The damage of proton and AO irradiations to lubricating materials were the most serious, and UV irradiation was the slightest. After irradiations, the friction coefficient of the solid-liquid lubricating coatings decreased (except for AO irradiation), but the disc wear rate increased compared with non-irradiation coatings.

  9. The status of beryllium technology for fusion

    Energy Technology Data Exchange (ETDEWEB)

    Scaffidi-Argentina, F.; Longhurst, G.R. E-mail: gx1@inel.gov; Shestakov, V.; Kawamura, H

    2000-12-01

    Beryllium was used for a number of years in the Joint European Torus (JET), and it is planned to be used extensively on the lower heat-flux surfaces of the reduced technical objective/reduced cost international thermonuclear experimental reactor (RTO/RC ITER). It has been included in various forms in a number of tritium breeding blanket designs. There are technical advantages but also a number of safety issues associated with the use of beryllium. Research in a variety of technical areas in recent years has revealed interesting issues concerning the use of beryllium in fusion. Progress in this research has been presented at a series of International Workshops on Beryllium Technology for Fusion. The most recent workshop was held in Karlsruhe, Germany on 15-17 September 1999. In this paper, a summary of findings presented there and their implications for the use of beryllium in the development of fusion reactors are presented.

  10. The status of beryllium technology for fusion

    International Nuclear Information System (INIS)

    Scaffidi-Argentina, F.; Longhurst, G.R.; Shestakov, V.; Kawamura, H.

    2000-01-01

    Beryllium was used for a number of years in the Joint European Torus (JET), and it is planned to be used extensively on the lower heat-flux surfaces of the reduced technical objective/reduced cost international thermonuclear experimental reactor (RTO/RC ITER). It has been included in various forms in a number of tritium breeding blanket designs. There are technical advantages but also a number of safety issues associated with the use of beryllium. Research in a variety of technical areas in recent years has revealed interesting issues concerning the use of beryllium in fusion. Progress in this research has been presented at a series of International Workshops on Beryllium Technology for Fusion. The most recent workshop was held in Karlsruhe, Germany on 15-17 September 1999. In this paper, a summary of findings presented there and their implications for the use of beryllium in the development of fusion reactors are presented

  11. BERYLLIUM MEASUREMENT IN COMMERCIALLY AVAILABLE WET WIPES

    Energy Technology Data Exchange (ETDEWEB)

    Youmans-Mcdonald, L.

    2011-02-18

    Analysis for beryllium by fluorescence is now an established method which is used in many government-run laboratories and commercial facilities. This study investigates the use of this technique using commercially available wet wipes. The fluorescence method is widely documented and has been approved as a standard test method by ASTM International and the National Institute for Occupational Safety and Health (NIOSH). The procedure involves dissolution of samples in aqueous ammonium bifluoride solution and then adding a small aliquot to a basic hydroxybenzoquinoline sulfonate fluorescent dye (Berylliant{trademark} Inc. Detection Solution Part No. CH-2) , and measuring the fluorescence. This method is specific to beryllium. This work explores the use of three different commercial wipes spiked with beryllium, as beryllium acetate or as beryllium oxide and subsequent analysis by optical fluorescence. The effect of possible interfering metals such as Fe, Ti and Pu in the wipe medium is also examined.

  12. Beryllium Measurement In Commercially Available Wet Wipes

    International Nuclear Information System (INIS)

    Youmans-Mcdonald, L.

    2011-01-01

    Analysis for beryllium by fluorescence is now an established method which is used in many government-run laboratories and commercial facilities. This study investigates the use of this technique using commercially available wet wipes. The fluorescence method is widely documented and has been approved as a standard test method by ASTM International and the National Institute for Occupational Safety and Health (NIOSH). The procedure involves dissolution of samples in aqueous ammonium bifluoride solution and then adding a small aliquot to a basic hydroxybenzoquinoline sulfonate fluorescent dye (Berylliant(trademark) Inc. Detection Solution Part No. CH-2) , and measuring the fluorescence. This method is specific to beryllium. This work explores the use of three different commercial wipes spiked with beryllium, as beryllium acetate or as beryllium oxide and subsequent analysis by optical fluorescence. The effect of possible interfering metals such as Fe, Ti and Pu in the wipe medium is also examined.

  13. Assessment of LANL beryllium waste management documentation

    International Nuclear Information System (INIS)

    Danna, J.G.; Jennrich, E.A.; Lund, D.M.; Davis, K.D.; Hoevemeyer, S.S.

    1991-04-01

    The objective of this report is to determine present status of the preparation and implementation of the various high priority documents required to properly manage the beryllium waste generated at the Laboratory. The documents being assessed are: Waste Acceptance Criteria, Waste Characterization Plan, Waste Certification Plan, Waste Acceptance Procedures, Waste Characterization Procedures, Waste Certification Procedures, Waste Training Procedures and Waste Recordkeeping Procedures. Beryllium is regulated (as a dust) under 40 CFR 261.33 as ''Discarded commercial chemical products, off specification species, container residues and spill residues thereof.'' Beryllium is also identified in the 3rd thirds ruling of June 1, 1990 as being restricted from land disposal (as a dust). The beryllium waste generated at the Laboratory is handled separately because beryllium has been identified as a highly toxic carcinogenic material

  14. Beryllium coating on Inconel tiles

    International Nuclear Information System (INIS)

    Bailescu, V.; Burcea, G.; Lungu, C.P.; Mustata, I.; Lungu, A.M.; Rubel, M.; Coad, J.P.; Matthews, G.; Pedrick, L.; Handley, R.

    2007-01-01

    Full text of publication follows: The Joint European Torus (JET) is a large experimental nuclear fusion device. Its aim is to confine and study the behaviour of plasma in conditions and dimensions approaching those required for a fusion reactor. The plasma is created in the toroidal shaped vacuum vessel of the machine in which it is confined by magnetic fields. In preparation for ITER a new ITER-like Wall (ILW) will be installed on Joint European Torus (JET), a wall not having any carbon facing the plasma [1]. In places Inconel tiles are to be installed, these tiles shall be coated with Beryllium. MEdC represented by the National Institute for Laser, Plasma and Radiation Physics, Magurele, Bucharest and in direct cooperation with Nuclear Fuel Plant Pitesti started to coat Inconel tiles with 8 μm of Beryllium in accordance with the requirements of technical specification and fit for installation in the JET machine. This contribution provides an overview of the principles of manufacturing processes using thermal evaporation method in vacuum and the properties of the prepared coatings. The optimization of the manufacturing process (layer thickness, structure and purity) has been carried out on Inconel substrates (polished and sand blasted) The results of the optimization process and analysis (SEM, TEM, XRD, Auger, RBS, AFM) of the coatings will be presented. Reference [1] Takeshi Hirai, H. Maier, M. Rubel, Ph. Mertens, R. Neu, O. Neubauer, E. Gauthier, J. Likonen, C. Lungu, G. Maddaluno, G. F. Matthews, R. Mitteau, G. Piazza, V. Philipps, B. Riccardi, C. Ruset, I. Uytdenhouwen, R and D on full tungsten divertor and beryllium wall for JET TIER-like Wall Project, 24. Symposium on Fusion Technology - 11-15 September 2006 -Warsaw, Poland. (authors)

  15. Irradiated ignition over solid materials in reduce pressure environment: Fire safety issue in man-made enclosure system

    Science.gov (United States)

    Nakamura, N.; Aoki, A.

    Effects of ambient pressure and oxygen yield on irradiated ignition characteristics over solid combustibles have been studied experimentally Aim of the present study is to elucidate the flammability and chance of fire in depressurized enclosure system and give ideas for the fire safety and fire fighting strategies in such environment Thin cellulosic paper is considered as the solid combustible since cellulose is one of major organic compounds and flammables in the nature Applied atmosphere consists of inert gas either CO2 or N2 and oxygen and various mixture ratios are of concerned Total ambient pressure level is varied from 0 1MPa standard atmospheric pressure to 0 02MPa Ignition is initiated by external thermal flux exposed into the solid surface as a model of unexpected thermal input to initiate the localized fire Thermal degradation of the solid induces combustible gaseous products e g CO H2 or other low class of HCs and the gas mixes with ambient oxygen to form the combustible mixture over the solid Heat transfer from the hot irradiated surface into the mixture accelerates the local exothermic reaction in the gas phase and finally thermal runaway ignition is achieved Ignition event is recorded by high-speed digital video camera to analyze the ignition characteristics Flammable map in partial pressure of oxygen Pox and total ambient pressure Pt plane is made to reveal the fire hazard in depressurized environment Results show that wider flammable range is obtained depending on the imposed ambient

  16. Frequency Distribution of Second Solid Cancer Locations in Relation to the Irradiated Volume Among 115 Patients Treated for Childhood Cancer

    International Nuclear Information System (INIS)

    Diallo, Ibrahima; Haddy, Nadia; Adjadj, Elisabeth; Samand, Akhtar; Quiniou, Eric; Chavaudra, Jean; Alziar, Iannis; Perret, Nathalie; Guerin, Sylvie; Lefkopoulos, Dimitri; Vathaire, Florent de

    2009-01-01

    Purpose: To provide better estimates of the frequency distribution of second malignant neoplasm (SMN) sites in relation to previous irradiated volumes, and better estimates of the doses delivered to these sites during radiotherapy (RT) of the first malignant neoplasm (FMN). Methods and Materials: The study focused on 115 patients who developed a solid SMN among a cohort of 4581 individuals. The homemade software package Dos E G was used to estimate the radiation doses delivered to SMN sites during RT of the FMN. Three-dimensional geometry was used to evaluate the distances between the irradiated volume, for RT delivered to each FMN, and the site of the subsequent SMN. Results: The spatial distribution of SMN relative to the irradiated volumes in our cohort was as follows: 12% in the central area of the irradiated volume, which corresponds to the planning target volume (PTV), 66% in the beam-bordering region (i.e., the area surrounding the PTV), and 22% in regions located more than 5 cm from the irradiated volume. At the SMN site, all dose levels ranging from almost zero to >75 Gy were represented. A peak SMN frequency of approximately 31% was identified in volumes that received <2.5 Gy. Conclusion: A greater volume of tissues receives low or intermediate doses in regions bordering the irradiated volume with modern multiple-beam RT arrangements. These results should be considered for risk-benefit evaluations of RT.

  17. The benchmark experiment on slab beryllium with D–T neutrons for validation of evaluated nuclear data

    Energy Technology Data Exchange (ETDEWEB)

    Nie, Y., E-mail: nieyb@ciae.ac.cn [Science and Technology on Nuclear Data Laboratory, China Institute of Atomic Energy, Beijing 102413 (China); Ren, J.; Ruan, X.; Bao, J. [Science and Technology on Nuclear Data Laboratory, China Institute of Atomic Energy, Beijing 102413 (China); Han, R. [Institute of Modern Physics, Chinese Academy of Sciences, Lanzhou 730000 (China); Zhang, S. [Institute of Modern Physics, Chinese Academy of Sciences, Lanzhou 730000 (China); Inner Mongolia University for the Nationalities, Inner Mongolia, Tongliao 028000 (China); Huang, H.; Li, X. [Science and Technology on Nuclear Data Laboratory, China Institute of Atomic Energy, Beijing 102413 (China); Ding, Y. [Science and Technology on Nuclear Data Laboratory, China Institute of Atomic Energy, Beijing 102413 (China); School of Nuclear Science and Technology, Lanzhou University, Lanzhou 730000 (China); Wu, H.; Liu, P.; Zhou, Z. [Science and Technology on Nuclear Data Laboratory, China Institute of Atomic Energy, Beijing 102413 (China)

    2016-04-15

    Highlights: • Evaluated data for beryllium are validated by a high precision benchmark experiment. • Leakage neutron spectra from pure beryllium slab are measured at 61° and 121° using time-of-flight method. • The experimental results are compared with the MCNP-4B calculations with the evaluated data from different libraries. - Abstract: Beryllium is the most favored neutron multiplier candidate for solid breeder blankets of future fusion power reactors. However, beryllium nuclear data are differently presented in modern nuclear data evaluations. In order to validate the evaluated nuclear data on beryllium, in the present study, a benchmark experiment has been performed at China Institution of Atomic Energy (CIAE). Neutron leakage spectra from pure beryllium slab samples were measured at 61° and 121° using time-of-flight method. The experimental results were compared with the calculated ones by MCNP-4B simulation, using the evaluated data of beryllium from the CENDL-3.1, ENDF/B-VII.1 and JENDL-4.0 libraries. From the comparison between the measured and the calculated spectra, it was found that the calculation results based on CENDL-3.1 caused overestimation in the energy range from about 3–12 MeV at 61°, while at 121°, all the libraries led to underestimation below 3 MeV.

  18. The benchmark experiment on slab beryllium with D–T neutrons for validation of evaluated nuclear data

    International Nuclear Information System (INIS)

    Nie, Y.; Ren, J.; Ruan, X.; Bao, J.; Han, R.; Zhang, S.; Huang, H.; Li, X.; Ding, Y.; Wu, H.; Liu, P.; Zhou, Z.

    2016-01-01

    Highlights: • Evaluated data for beryllium are validated by a high precision benchmark experiment. • Leakage neutron spectra from pure beryllium slab are measured at 61° and 121° using time-of-flight method. • The experimental results are compared with the MCNP-4B calculations with the evaluated data from different libraries. - Abstract: Beryllium is the most favored neutron multiplier candidate for solid breeder blankets of future fusion power reactors. However, beryllium nuclear data are differently presented in modern nuclear data evaluations. In order to validate the evaluated nuclear data on beryllium, in the present study, a benchmark experiment has been performed at China Institution of Atomic Energy (CIAE). Neutron leakage spectra from pure beryllium slab samples were measured at 61° and 121° using time-of-flight method. The experimental results were compared with the calculated ones by MCNP-4B simulation, using the evaluated data of beryllium from the CENDL-3.1, ENDF/B-VII.1 and JENDL-4.0 libraries. From the comparison between the measured and the calculated spectra, it was found that the calculation results based on CENDL-3.1 caused overestimation in the energy range from about 3–12 MeV at 61°, while at 121°, all the libraries led to underestimation below 3 MeV.

  19. Aspects of land application of sewage solids and gamma-irradiated dried sewage solids on calcareous soils

    International Nuclear Information System (INIS)

    McCaslin, B.D.; O'Connor, G.A.; Sivinski, J.S.

    1980-01-01

    One of the cheapest and generally most convenient methods of disposing of sewage sludge is by land application. The greatest risks of land application are potential contamination of the environment by heavy metals, other toxicants, and pathogens. Irradiation of sewage sludge has been shown to have little or no effect on sludge elements available to plants, and can remove the potential pathogen problem. Work at New Mexico State University has shown that, with little risk, gamma-irradiated sewage sludge can be used to great advantage for crop production, especially on highly calcareous soils low in heavy metals essential for plant growth

  20. Technical issues for beryllium use in fusion blanket applications

    International Nuclear Information System (INIS)

    McCarville, T.J.; Berwald, D.H.; Wolfer, W.; Fulton, F.J.; Lee, J.D.; Maninger, R.C.; Moir, R.W.; Beeston, J.M.; Miller, L.G.

    1985-01-01

    Beryllium is an excellent non-fissioning neutron multiplier for fusion breeder and fusion electric blanket applications. This report is a compilation of information related to the use of beryllium with primary emphasis on the fusion breeder application. Beryllium resources, production, fabrication, properties, radiation damage and activation are discussed. A new theoretical model for beryllium swelling is presented

  1. Production of beryllium oxide of nuclear purity from beryl

    Energy Technology Data Exchange (ETDEWEB)

    Copat, A; Sood, S P

    1984-01-01

    Production of beryllium oxide from beryl by the fluoride process was optimized in this study. Optimum results were obtained using a mixture of sodium hexafluorsilicate and sodium hexafluorferrate as flux and calcinating at 740/sup 0/C for 2 hours. The beryllium concentrate produced was further purified by crystallization as beryllium sulfate to obtain nuclear grade beryllium oxide

  2. Production of beryllium oxide of nuclear purity from beryl

    International Nuclear Information System (INIS)

    Copat, A.; Sood, S.P.

    1983-01-01

    Production of beryllium oxide from beryl by the fluoride process was optimized in this study. Optimum results were obtained using a mixture of sodium hexafluorsilicate and sodium hexafluorferrate as flux and calcinating at 740 0 C for 2 hours. The beryllium concentrate produced was further purified by crystallization as beryllium sulfate to obtain nuclear grade beryllium oxide (Author) [pt

  3. Experimental results of beryllium exposed to intense high energy proton beam pulses

    CERN Document Server

    Ammigan, K; Hurh, P; Zwaska, R; Butcher, M; Guinchard, M; Calviani, M; Losito, R; Roberts, S; Kuksenko, V; Atherton, A; Caretta, O; Davenne, T; Densham, C; Fitton, M; Loveridge, J; O'Dell, J

    2017-01-01

    Beryllium is extensively used in various accelerator beam lines and target facilities as a material for beam windows, and to a lesser extent, as secondary particle production targets. With increasing beam intensities of future accelerator facilities, it is critical to understand the response of beryllium under extreme conditions to reliably operate these components as well as avoid compromising particle production efficiency by limiting beam parameters. As a result, an exploratory experiment at CERN’s HiRadMat facility was carried out to take advantage of the test facility’s tunable high intensity proton beam to probe and investigate the damage mechanisms of several beryllium grades. The test matrix consisted of multiple arrays of thin discs of varying thicknesses as well as cylinders, each exposed to increasing beam intensities. This paper outlines the experimental measurements, as well as findings from Post-Irradiation-Examination (PIE) work where different imaging techniques were used to analyze and co...

  4. Examination of Beryllium Under Intense High Energy Proton Beam at CERN's HiRadMat Facility

    CERN Document Server

    Ammigan, K.; Hurh, P.; Zwaska, R.; Atherton, A.; Caretta, O.; Davenne,T.; Densham, C.; Fitton, M.; Loveridge, P.; O'Dell, J.; Roberts, S.; Kuksenko, V.; Butcher, M.; Calviani, M.; Guinchard, M.; Losito, R.

    2017-01-01

    Beryllium is extensively used in various accelerator beam lines and target facilities as material for beam win- dows, and to a lesser extent, as secondary particle produc- tion targets. With increasing beam intensities of future ac- celerator facilities, it is critical to understand the response of beryllium under extreme conditions to avoid compro- mising particle production efficiency by limiting beam pa- rameters. As a result, the planned experiment at CERN’s HiRadMat facility will take advantage of the test facility’s tunable high intensity proton beam to probe and investigate the damage mechanisms of several grades of beryllium. The test matrix will consist of multiple arrays of thin discs of varying thicknesses as well as cylinders, each exposed to increasing beam intensities. Online instrumentations will acquire real time temperature, strain, and vibration data of the cylinders, while Post-Irradiation-Examination (PIE) of the discs will exploit advanced microstructural characteri- zation and imagin...

  5. Examination of Beryllium Under Intense High Energy Proton Beam at CERN's HiRadMat Facility

    CERN Document Server

    Ammigan, K; Hurh, P; Zwaska, R; Atherton, A; Caretta, O; Davenne, t; Densham, C; Fitton, M; Loveridge, P; O'Dell, J; Roberts, S; Kuksenko, v; Butcher, M; Calviani, M; Guinchard, M; Losito, R

    2015-01-01

    Beryllium is extensively used in various accelerator beam lines and target facilities as material for beam win- dows, and to a lesser extent, as secondary particle produc- tion targets. With increasing beam intensities of future ac- celerator facilities, it is critical to understand the response of beryllium under extreme conditions to avoid compro- mising particle production efficiency by limiting beam pa- rameters. As a result, the planned experiment at CERN’s HiRadMat facility will take advantage of the test facility’s tunable high intensity proton beam to probe and investigate the damage mechanisms of several grades of beryllium. The test matrix will consist of multiple arrays of thin discs of varying thicknesses as well as cylinders, each exposed to increasing beam intensities. Online instrumentations will acquire real time temperature, strain, and vibration data of the cylinders, while Post-Irradiation-Examination (PIE) of the discs will exploit advanced microstructural characteri- zation and imagin...

  6. Analytical solutions for thermal transient profile in solid target irradiated with low energy and high beam current protons

    International Nuclear Information System (INIS)

    Oliveira, Henrique B. de; Brazao, Nei G.; Sciani, Valdir

    2009-01-01

    There were obtained analytical solutions for thermal transient in solid targets, used in short half-life radioisotopes production, when irradiated with low energy and high beam current protons, in the cyclotron accelerator Cyclone 30 of the Institute for Energy and Nuclear Research (IPEN/CNEN-SP). The beam spatial profile was considered constant and the time depended heat distribution equation was resolved for a continuous particles flow entering the target. The problem was divided into two stages: a general solution was proposed which is the sum of two functions, the first one related to the thermal equilibrium situation and the second one related to a time dependent function that was determinate by the setting of the contour conditions and the initial conditions imposed by the real problem. By that one got an analytic function for a complete description of the heat transport phenomenon inside the targets. There were used both, numerical and symbolic computation methods, to obtain temperature maps and thermal gradients and the results showed an excellent agreement when compared with purely numerical models. The results were compared with obtained data from Gallium-67 and Thallium-201 irradiation routines conducted by the IPEN Cyclotrons accelerators center, showing excellent agreement. The objective of this paper is to develop solid targets irradiation systems (metals and oxides) so that one can operate with high levels of current beam, minimizing the irradiation time and maximizing the final returns. (author)

  7. Inherent structure features of beryllium and their influence on the performance polycrystalline metal under different conditions

    Energy Technology Data Exchange (ETDEWEB)

    Khomutov, A.M.; Mikhailov, V.S.; Pronin, V.N.; Pakhomov, Ya.D. [State Scientific Center of Russian Federation `A.A. Bochvar All-Russia Research Inst. of Inorganic Materials (VNIINM)`, Moscow (Russian Federation)

    1998-01-01

    The anisotropy of physical properties of beryllium single crystals resulting from covalent bonds in crystal lattice leads to significant residual thermal microstresses (RTM) in the polycrystalline metal. It is demonstrated experimentally that there is a simple linear dependence between the magnitude of RTM and the ultimate tensile strength. The factors controlling RTM are analysed and in the framework of powder metallurgy process the technological methods of producing beryllium with the needed properties are recommended. Primarily it is necessary to control the quantity and extent of dispersity of intergranular oxide inclusions and mean grain size in combination with the high degree of macro- and microhomogenity of the structure. The requirements to beryllium microstructure for different operating conditions including neutron fluxes and transient temperature fields are formulated. In the framework of the concept under development one can explain formerly not fully understandable effects, which are characteristic of polycrystalline beryllium such as unexpected Petch-Stro curve, the role of twinning etc., and predict new ones. In particular, it can be possible to expect the growth of ductility of high strength beryllium grades as neutron irradiated. (author)

  8. Technical session 4: Health and safety issues. Working environment control in beryllium handling area

    International Nuclear Information System (INIS)

    Yonehara, K.; Natori, Y.; Tatenuma, K.; Nakamichi, Masaru

    2016-01-01

    Beryllium (Be) and its intermetallic compound (beryllide) are recommended from Japan as the most promising solid neutron multiplier for nuclear fusion power plant. The shape as the neutron multiplier is small sphere (pebble), and the mass production technology of it must be developed urgently. Beryllium is the substance regulated by the law of Ordinance on Prevention of Hazards Due to Specified the Chemical Substances Control. We'll report on a way of the operational environmental management to make a safe Be handling area for the Be handling researchers and workers. (author)

  9. Beryllium and growth. III. The effect of beryllium on plant phosphatase

    Energy Technology Data Exchange (ETDEWEB)

    Hoagland, M B

    1952-01-01

    The purpose of the investigations was to correlate the apparent ability of beryllium to substitute for magnesium in plant growth with a specific biochemical effect of the metal. Through association with earlier work on beryllium inhibition of animal alkaline phosphatase, a study was made of the effect of beryllium and other metals upon the activity of a phosphatase derived from tomato leaves. Although only indirect evidence is available that this enzyme system was magnesium-activated, beryllium was found to inhibit reversibly the splitting of GP and ATP. Other metals were also found to be inhibitory but the ATP-ase inhibition - and especially the ratio of P split from GP to P split from ATP - was higher for beryllium than for any other metal studied. The significance of this finding in relation to energy metabolism, growth, and beryllium toxicity is discussed. 12 references, 5 figures, 2 tables.

  10. Spectrographic measurement of beryllium in the atmosphere; Dosage spectrographique du beryllium dans l'atmosphere

    Energy Technology Data Exchange (ETDEWEB)

    Artaud, J; Cittanova, J [Commissariat a l' Energie Atomique, Service d' Analyses et Recherches Chimiques Appliquees, Saclay (France). Centre d' Etudes Nucleaires; Crehange, G; Frequelin, S [Commissariat a l' Energie Atomique, Dir. des Applications Militaires, Service Chimie, Saclay (France). Centre d' Etudes Nucleaires; Baudin, G [Commissariat a l' Energie Atomique, Grenoble (France). Centre d' Etudes Nucleaires

    1961-07-01

    We describe here a method for the spectrographic determination of beryllium on filters which is valid for amounts varying between 0,01 and 30 {mu}g of beryllium and which is independent of the nature of the beryllium compound involved. This is a flux method (graphite-lithium carbonate mixture), the excitation being by a direct current arc. (author) [French] Nous decrivons ici, une methode de dosage spectrographique de beryllium sur filtre, valable pour des teneurs comprises entre 0,01 et 30 {mu}g de beryllium et independante de la nature du compose de beryllium a doser. C'est une methode de 'flux' (melange graphite-carbonate de lithium) l'excitation etant un arc a courant continu. (auteur)

  11. Solid-phase photocatalytic degradation of polystyrene plastic with goethite modified by boron under UV-vis light irradiation

    International Nuclear Information System (INIS)

    Liu Guanglong; Zhu Duanwei; Zhou Wenbing; Liao Shuijiao; Cui Jingzhen; Wu Kang; Hamilton, David

    2010-01-01

    A novel photodegradable polyethylene-boron-goethite (PE-B-goethite) composite film was prepared by embedding the boron-doped goethite into the commercial polyethylene. The goethite catalyst was modified by boron in order to improve its photocatalytic efficiency under the ultraviolet and visible light irradiation. Solid-phase photocatalytic degradation of the PE-B-goethite composite film was carried out in an ambient air at room temperature under ultraviolet and visible light irradiation. The properties of composite films were compared with those of the pure PE films and the PE-goethite composite films through performing weight loss monitoring, scanning electron microscope (SEM) analysis, FT-IR spectroscopy and X-ray photoelectron spectroscopy (XPS). The photo-induced degradation of PE-B-goethite composite films was higher than that of the pure PE films and the PE-goethite composite films under the UV-irradiation, while there has been little change under the visible light irradiation. The weight loss of the PE-B-goethite (0.4 wt.%) composite film reached 12.6% under the UV-irradiation for 300 h. The photocatalytic degradation mechanism of the composite films was briefly discussed.

  12. Metallurgical viewpoints on the brittleness of beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Lagerberg, G

    1960-02-15

    At present the development and use of beryllium metal for structural applications is severely hampered by its brittleness. Reasons for this lack of ductility are reviewed in discussing the deformation behaviour of beryllium in relation to other hexagonal metals. The ease of fracturing in beryllium is assumed to be a consequence of a limited number of deformation modes in combination with high deformation resistance. Models for the nucleation of fracture are suggested. The relation of ductility to elastic constants as well as to grain size, texture and alloying additions is discussed.

  13. Metallurgical viewpoints on the brittleness of beryllium

    International Nuclear Information System (INIS)

    Lagerberg, G.

    1960-02-01

    At present the development and use of beryllium metal for structural applications is severely hampered by its brittleness. Reasons for this lack of ductility are reviewed in discussing the deformation behaviour of beryllium in relation to other hexagonal metals. The ease of fracturing in beryllium is assumed to be a consequence of a limited number of deformation modes in combination with high deformation resistance. Models for the nucleation of fracture are suggested. The relation of ductility to elastic constants as well as to grain size, texture and alloying additions is discussed

  14. Beryllium health effects in the era of the beryllium lymphocyte proliferation test.

    Science.gov (United States)

    Maier, L A

    2001-05-01

    The beryllium lymphocyte proliferation test (BeLPT) has revolutionized our approach to the diagnosis, screening, and surveillance of beryllium health effects. Based on the development of a beryllium-specific cell-mediated immune response, the BeLPT has allowed us to define early health effects of beryllium, including beryllium sensitization (BeS), and chronic beryllium disease (CBD) at a subclinical stage. The use of this test as a screening tool has improved our understanding of these health effects. From a number of studies it is apparent that BeS precedes CBD and develops after as little as 9 weeks of beryllium exposure. CBD occurs within 3 months and up to 30 years after initial beryllium exposure. Exposure-response variables have been associated with BeS/CBD, including work as a machinist, chemical or metallurgical operator, laboratory technician, work in ceramics or beryllium metal production, and years of beryllium exposure. Recent studies have found BeS and CBD in workplaces in which the majority of exposures were below the 2 microg/m3 OSHA time-weighted average (TWA). Ideally, the BeLPT would be used in surveillance aimed at defining other risk-related processes, determining exposure variables which predict BeS and CBD, and defining the exposure level below which beryllium health effects do not occur. Unfortunately, the BeLPT can result in false negative tests and still requires an invasive procedure, a bronchoscopy, for the definitive diagnosis of CBD. Thus, research is needed to establish new tests to be used alone or in conjunction with the BeLPT to improve our ability to detect early beryllium health effects.

  15. Sublethal effects of tritium on aquatic systems, effects of low-level chronic irradiation on embryonic development, effects of beryllium and lithium on aquatic systems, and teratogenic effects of low-level magnetic fields

    International Nuclear Information System (INIS)

    Strand, J.A.; Roesijadi, G.; Emery, R.M.

    1978-01-01

    It is conceivable, and possible, that with increasing applications of nuclear energy, greater quantities of potentially harmful radionuclides will be released to the environment. This may be particularly true for advanced reactor designs such as the fusion reactor where radionuclides, principally tritium, may be expected to escape from the plant both in gaseous and liquid effluents in quantities significantly greater than for present PWR or BWR designs. Foreseeing such contingencies, the research programs described herein are in response to the need to measure the potential radiation effects of tritium releases on individuals, and ultimately populations and biotic communities. As a first approach, our efforts are directed to determine effects of low-level chronic exposures on developing embryo and larval stages, clearly the most radiosensitive. The anticipated increase in the release of beryllium and lithium from mining, refining, and fabrication of materials used during construction of fusion reactors has also caused concern as to potential adverse effects on the environment. Accordingly, FY-78 fusion related research will include efforts to study the metabolism of each metal in the living organism, and to determine at what levels toxicity may be expected. Fusion related research will also include preliminary experiments on the effects of low-level magnetic fields. It is conceivable that magnetic fields of 70 to 450 gauss will be encountered by attendant personnel working in the transport and hot cell areas of fusion reactors. Also, those personnel assigned to the areas immediately surrounding the reactor may be exposed

  16. Thermal cycling tests on Li4SiO4 and beryllium pebbles

    International Nuclear Information System (INIS)

    Dalle Donne, M.; Norajitra, P.; Weisenburger, A.

    1995-01-01

    The European B.O.T. Demo-relevant solid breeder blanket is based on the use of beds of beryllium and Li 4 SiO 4 pebbles. Particularly dangerous for the pebble integrity are the rapid temperature changes which could occur, for instance, by a sudden blanket power shut-down. A series of thermal cycle tests have been performed for various beds of beryllium and Li 4 SiO 4 pebbles. No breaking was observed in the beryllium pebbles, however the Li 4 SiO 4 pebbles broke by temperature rates of change of about -50 C/sec independently on pebbles size and lithium enrichment. This value is considerably higher than the peak temperature rates of change expected in the blanket. (orig.)

  17. Irradiation effect on leaching behavior and form of heavy metals in fly ash of municipal solid waste incinerator

    International Nuclear Information System (INIS)

    Nam, Sangchul; Namkoong, Wan

    2012-01-01

    Highlights: ► No research has been done to examine effect of electron beam irradiation on leaching behavior of heavy metals in fly ash. ► Electron beam irradiation on fly ash had significant effect on heavy metal leaching. ► Leaching potential of heavy metals in fly ash differed among metal species tested (Pb, Zn, Cu). ► Metal forms in the ash were analyzed to explain the difference. ► The difference could be explained by metal form change. - Abstract: Fly ash from a municipal solid waste incinerator (MSWI) is commonly classified as hazardous waste. High-energy electron beam irradiation systems have gained popularity recently as a clean and promising technology to remove environmental pollutants. Irradiation effects on leaching behavior and form of heavy metals in MSWI fly ash have not been investigated in any significant detail. An electron beam accelerator was used in this research. Electron beam irradiation on fly ash significantly increased the leaching potential of heavy metals from fly ash. The amount of absorbed dose and the metal species affected leaching behavior. When electron beam irradiation intensity increased gradually up to 210 kGy, concentration of Pb and Zn in the leachate increased linearly as absorbed dose increased, while that of Cu underwent no significant change. Concentration of Pb and Zn in the leachate increased up to 15.5% (10.7 mg/kg), and 35.6% (9.6 mg/kg) respectively. However, only 4.8% (0.3 mg/kg) increase was observed in the case of Cu. The results imply that irradiation has significant effect on the leaching behavior of heavy metals in fly ash, and the effect is quite different among the metal species tested in this study. A commonly used sequential extraction analysis which can classify a metal species into five forms was conducted to examine any change in metal form in the irradiated fly ash. Notable change in metal form in fly ash was observed when fly ash was irradiated. Change in Pb form was much greater than that of

  18. Combined aging of beryllium bronze

    International Nuclear Information System (INIS)

    Duraev, P.P.; Kaplun, Yu.A.; Pastukhova, Zh.P.; Rakhshtadt, A.G.

    1986-01-01

    This article evaluates the possibility of increasing the resistance of beryllium bronze to small plastic deformations as a result of the application of stepped aging under stress. Low-temperature aging under conditions of bending under a stress of about 100 MPa was applied to alloy BrBNT1, 9Mg at 150, 180, and 210 0 C, high-temperature aging at 300 and 340 0 C under stress and without stress. As a result of applying stepped aging under stress, the elastic limit of the alloy BrBNT1, 9Mg was raised to 900 MPa. Stepped aging under stress has a substantial effect on the relaxation stability of the alloy. The procedure suggested in the article for aging may be used efficiently for treating elastic elements made of other brands of bronze as well

  19. Analysis of a beryllium-copper diffusion joint after HHF test

    International Nuclear Information System (INIS)

    Guiniatouline, R.N.; Mazul, I.V.; Gorodetsky, A.E.; Zalavutdinov, R.Kh.; Rybakov, S.Yu.; Savenko, V.I.

    1996-01-01

    The development of beryllium-copper joints which can withstand relevant ITER divertor conditions is one of the important tasks at the present time. One of the main problems associated with these joints is the intermetallic layers. The strength and life of these joints significantly depend on the width and contents of the intermetallic layers. The objective of this work is to study the diffusion joint of TGP-56 beryllium to OFHC copper after thermal response and thermocyclic tests with a beryllium-copper mock-up. The HHF test was performed on the e-beam facility (EBTS, SNLA). The following methods were used for analysis: roentgenographic analysis, X-ray spectrum analysis and fracture analysis. During the investigation the following studies were undertaken: the analysis of the diffusion boundary layer, which was obtained at the cross-section of one of the tiles, the analysis of the debonded surfaces of several beryllium tiles and corresponding copper parts and the analysis of the upper surface of one of the tiles after HHF tests. The joint roentgenographic and element analyses revealed the following phases in the diffusion zone: Cu 2 Be (∝170 μm), CuBe (∝30 μm), CuBe 2 (∝1 μm) and a solid solution of copper in beryllium. The phases Cu 2 Be, CuBe and the solid solution of copper in beryllium were detected by the quantitative microanalysis and the phases CuBe, CuBe 2 and CuBe, by the roentgenographic analysis. The fracture (origin) is located in the central part of the tiles. This crack was caused by residual stresses and thermal fatigue testing. This analysis provides important data on the joint quality and may be used for all types of joints used for ITER applications. (orig.)

  20. The adhesive bonding of beryllium structural components

    International Nuclear Information System (INIS)

    Fullerton-Batten, R.C.

    1977-01-01

    Where service conditions permit, adhesive bonding is a highly recommendable, reliable means of joining beryllium structural parts. Several important programs have successfully used adhesive bonding for joining structural and non-structural beryllium components. Adhesive bonding minimizes stress concentrations associated with other joining techniques and considerably improves fatigue resistance. In addition, no degradation of base metal properties occur. In many instances, structural joints can be fabricated more cheaply by adhesive bonding or in combination with adhesive bonding than by any other method used alone. An evaluation program on structural adhesive bonding of beryllium sheet components is described. A suitable surface pretreatment for beryllium adherends prior to bonding is given. Tensile shear strength and fatigue properties of FM 1000 and FM 123-5 adhesive bonded joints are reviewed and compared with data obtained from riveted joints of similar geometry. (author)

  1. Chronic Beryllium Disease Prevention Program Report

    Energy Technology Data Exchange (ETDEWEB)

    Lee, S

    2012-03-29

    This document describes how Lawrence Livermore National Laboratory (LLNL) meets the requirements and management practices of federal regulation 10 CFR 850, 'Chronic Beryllium Disease Prevention Program (CBDPP).' This revision of the LLNL CBDPP incorporates clarification and editorial changes based on lessons learned from employee discussions, observations and reviews of Department of Energy (DOE) Complex and commercial industry beryllium (Be) safety programs. The information is used to strengthen beryllium safety practices at LLNL, particularly in the areas of: (1) Management of small parts and components; and (2) Communication of program status to employees. Future changes to LLNL beryllium activities and on-going operating experience will be incorporated into the program as described in Section S, 'Performance Feedback.'

  2. Beryllium-aluminum alloys for investment castings

    International Nuclear Information System (INIS)

    Nachtrab, W.T.; Levoy, N.

    1997-01-01

    Beryllium-aluminum alloys containing greater than 60 wt % beryllium are very favorable materials for applications requiring light weight and high stiffness. However, when produced by traditional powder metallurgical methods, these alloys are expensive and have limited applications. To reduce the cost of making beryllium-aluminum components, Nuclear Metals Inc. (NMI) and Lockheed Martin Electronics and Missiles have recently developed a family of patented beryllium-aluminum alloys that can be investment cast. Designated Beralcast, the alloys can achieve substantial weight savings because of their high specific strength and stiffness. In some cases, weight has been reduced by up to 50% over aluminum investment casting. Beralcast is now being used to make thin wall precision investment castings for several advanced aerospace applications, such as the RAH-66 Comanche helicopter and F-22 jet fighter. This article discusses alloy compositions, properties, casting method, and the effects of cobalt additions on strength

  3. Criteria to average out the chemical shift anisotropy in solid-state NMR when irradiated with BABA I, BABA II, and C7 radiofrequency pulse sequences.

    Science.gov (United States)

    Stephane Mananga, Eugene

    2013-01-01

    Floquet-Magnus expansion is used to study the effect of chemical shift anisotropy in solid-state NMR of rotating solids. The chemical shift interaction is irradiated with two types of radiofrequency pulse sequences: BABA and C7. The criteria for the chemical shift anisotropy to be averaged out in each rotor period are obtained. Copyright © 2013 Elsevier Inc. All rights reserved.

  4. Beryllium concentration in pharyngeal tonsils in children

    Directory of Open Access Journals (Sweden)

    Ewa Nogaj

    2014-06-01

    Full Text Available Power plant dust is believed to be the main source of the increased presence of the element beryllium in the environment which has been detected in the atmospheric air, surface waters, groundwater, soil, food, and cigarette smoke. In humans, beryllium absorption occurs mainly via the respiratory system. The pharyngeal tonsils are located on the roof of the nasopharynx and are in direct contact with dust particles in inhaled air. As a result, the concentration levels of beryllium in the pharyngeal tonsils are likely to be a good indicator of concentration levels in the air. The presented study had two primary aims: to investigate the beryllium concentration in pharyngeal tonsils in children living in southern Poland, and the appropriate reference range for this element in children’s pharyngeal tonsils. Pharyngeal tonsils were extracted from a total of 379 children (age 2–17 years, mean 6.2 ± 2.7 years living in southern Poland. Tonsil samples were mineralized in a closed cycle in a pressure mineralizer PDS 6, using 65% spectrally pure nitric acid. Beryllium concentration was determined using the ICP-AES method with a Perkin Elmer Optima 5300DVTM. The software Statistica v. 9 was used for the statistical analysis. It was found that girls had a significantly greater beryllium concentration in their pharyngeal tonsils than boys. Beryllium concentration varies greatly, mostly according to the place of residence. Based on the study results, the reference value for beryllium in pharyngeal tonsils of children is recommended to be determined at 0.02–0.04 µg/g.

  5. Vacuum hot-pressed beryllium and TiC dispersion strengthened tungsten alloy developments for ITER and future fusion reactors

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Xiang, E-mail: xliu@swip.ac.cn [Southwestern Institute of Physics, P.O. Box 432, Chengdu 610041, Sichuan (China); Chen, Jiming; Lian, Youyun; Wu, Jihong; Xu, Zengyu; Zhang, Nianman; Wang, Quanming; Duan, Xuro [Southwestern Institute of Physics, P.O. Box 432, Chengdu 610041, Sichuan (China); Wang, Zhanhong; Zhong, Jinming [Northwest Rare Metal Material Research Institute, CNMC, Ningxia Orient Group Co. Ltd.,No.119 Yejin Road, Shizuishan City, Ningxia,753000 (China)

    2013-11-15

    Beryllium and tungsten have been selected as the plasma facing materials of the ITER first wall (FW) and divertor chamber, respectively. China, as a participant in ITER, will share the manufacturing tasks of ITER first-wall mockups with the European Union and Russia. Therefore ITER-grade beryllium has been developed in China and a kind of vacuum hot-pressed (VHP) beryllium, CN-G01, was characterized for both physical, and thermo-mechanical properties and high heat flux performance, which indicated an equivalent performance to U.S. grade S-65C beryllium, a reference grade beryllium of ITER. Consequently CN-G01 beryllium has been accepted as the armor material of ITER-FW blankets. In addition, a modification of tungsten by TiC dispersion strengthening was investigated and a W–TiC alloy with TiC content of 0.1 wt.% has been developed. Both surface hardness and recrystallization measurements indicate its re-crystallization temperature approximately at 1773 K. Deuterium retention and thermal desorption behaviors of pure tungsten and the TiC alloy were also measured by deuterium ion irradiation of 1.7 keV energy to the fluence of 0.5–5 × 10{sup 18} D/cm{sup 2}; a main desorption peak at around 573 K was found and no significant difference was observed between pure tungsten and the tungsten alloy. Further characterization of the tungsten alloy is in progress.

  6. On the modeling of irradiation-induced homogeneous precipitation in proton-bombarded Ni-Si solid solutions

    Science.gov (United States)

    Lam, Nghi Q.; Janghorban, K.; Ardell, A. J.

    1981-10-01

    Irradiation-induced solute redistribution leading to precipitation of coherent γ' particles in undersaturated Ni-based solid solutions containing 6 and 8 at.% Si during 400-keV proton bombardment was modeled, based on the concept of solute segregation in concentrated alloys under spatially-dependent defect production conditions. The combined effects of (i) an extremely large difference between the defect production rates in the peak-damage and mid-range regions during irradiation and (ii) a preferential coupling between the interstitial and solute fluxes generate a net transient flux of Si atoms into the mid-range region, which is much larger than the solute flux out of this location. As a result, the Si concentration exceeds the solubility limit and homogeneous precipitation of the γ' phase occurs in this particular region of the irradiated samples. The spatial, compositional and temperature dependences of irradiation-induced homogeneous precipitation derived from the present theoretical calculations are in good qualitative agreement with experimental observations

  7. Pressure measurements and an analytical model for laser-generated shock waves in solids at low irradiance

    CERN Document Server

    Romain, J P; Dayma, G; Boustie, M; Resseguier, T D; Combis, P

    2002-01-01

    Low amplitude shock waves (from 1 to 300 bar) have been generated in gold layers deposited on a quartz substrate, by laser pulses at an incident fluence from 0.4 to 4.0 J cm sup - sup 2. The quartz was used as a pressure gauge for recording the induced shock profile. At a fluence <1.4 J cm sup - sup 2 , the shock pressure does not exceed 10 bar and the shock front is followed by a tension peak typical of an absorption in solid state. An analytical model of the compression-tension process has been developed, accounting for shock pressure and shock profile evolution as a function of irradiation conditions and material properties. From this model a mechanical interpretation is given to previous observations of spalling of the irradiated target surface.

  8. Pressure measurements and an analytical model for laser-generated shock waves in solids at low irradiance

    Energy Technology Data Exchange (ETDEWEB)

    Romain, J P [Laboratoire de Combustion et de Detonique, ENSMA, BP 40109, 86961 Futuroscope-Chasseneuil (France); Bonneau, F [Departement de Physique Theorique et Appliquee CEA/DAM Ile de France, BP 12, 91680 Bruyeres le Chatel (France); Dayma, G [Laboratoire de Combustion et de Detonique, ENSMA, BP 40109, 86961 Futuroscope-Chasseneuil (France); Boustie, M [Laboratoire de Combustion et de Detonique, ENSMA, BP 40109, 86961 Futuroscope-Chasseneuil (France); Resseguier, T de [Laboratoire de Combustion et de Detonique, ENSMA, BP 40109, 86961 Futuroscope-Chasseneuil (France); Combis, P [Departement de Physique Theorique et Appliquee CEA/DAM Ile de France, BP 12, 91680 Bruyeres le Chatel (France)

    2002-11-11

    Low amplitude shock waves (from 1 to 300 bar) have been generated in gold layers deposited on a quartz substrate, by laser pulses at an incident fluence from 0.4 to 4.0 J cm{sup -2}. The quartz was used as a pressure gauge for recording the induced shock profile. At a fluence <1.4 J cm{sup -2}, the shock pressure does not exceed 10 bar and the shock front is followed by a tension peak typical of an absorption in solid state. An analytical model of the compression-tension process has been developed, accounting for shock pressure and shock profile evolution as a function of irradiation conditions and material properties. From this model a mechanical interpretation is given to previous observations of spalling of the irradiated target surface.

  9. Pressure measurements and an analytical model for laser-generated shock waves in solids at low irradiance

    International Nuclear Information System (INIS)

    Romain, J P; Bonneau, F; Dayma, G; Boustie, M; Resseguier, T de; Combis, P

    2002-01-01

    Low amplitude shock waves (from 1 to 300 bar) have been generated in gold layers deposited on a quartz substrate, by laser pulses at an incident fluence from 0.4 to 4.0 J cm -2 . The quartz was used as a pressure gauge for recording the induced shock profile. At a fluence -2 , the shock pressure does not exceed 10 bar and the shock front is followed by a tension peak typical of an absorption in solid state. An analytical model of the compression-tension process has been developed, accounting for shock pressure and shock profile evolution as a function of irradiation conditions and material properties. From this model a mechanical interpretation is given to previous observations of spalling of the irradiated target surface

  10. Detection of beryllium treatment of natural sapphires by NRA

    Energy Technology Data Exchange (ETDEWEB)

    Gutierrez, P.C., E-mail: carolina.gutierrez@uam.e [Centro de Micro-Analisis de Materiales (CMAM), Universidad Autonoma de Madrid, Campus de Cantoblanco, 28049 Madrid (Spain); Ynsa, M.-D.; Climent-Font, A. [Centro de Micro-Analisis de Materiales (CMAM), Universidad Autonoma de Madrid, Campus de Cantoblanco, 28049 Madrid (Spain); Dpto. Fisica Aplicada C-12, Universidad Autonoma de Madrid, Campus de Cantoblanco, 28049 Madrid (Spain); Calligaro, T. [Centre de Recherche et de Restauration des musees de France C2RMF, CNRS-UMR171, 14 quai Francois Mitterrand, 75001 Paris (France)

    2010-06-15

    Since the 1990's, artificial treatment of natural sapphires (Al{sub 2}O{sub 3} crystals coloured by impurities) by diffusion of beryllium at high temperature has become a growing practice. This process permits to enhance the colour of these gemstones, and thus to increase their value. Detection of such a treatment - diffusion of tens of {mu}g/g of beryllium in Al{sub 2}O{sub 3} crystals - is usually achieved using high sensitivity techniques like laser-ablation inductively coupled plasma mass spectrometry (LA-ICP/MS) or laser-induced breakdown spectrometry (LIBS) which are unfortunately micro-destructive (leaving 50-100-{mu}m diameter craters on the gems). The simple and non-destructive alternative method proposed in this work is based on the nuclear reaction {sup 9}Be({alpha}, n{gamma}){sup 12}C with an external helium ion beam impinging on the gem directly placed in air. The 4439 keV prompt {gamma}-ray tagging Be atoms are detected with a high efficiency bismuth germanate scintillator. Beam dose is monitored using the 2235 keV prompt {gamma}-ray produced during irradiation by the aluminium of the sapphire matrix through the {sup 27}Al({alpha}, p{gamma}){sup 30}Si nuclear reaction. The method is tested on a series of Be-treated sapphires previously analyzed by LA-ICP/MS to determine the optimal conditions to obtain a peak to background appropriate to reach the required {mu}g/g sensitivity. Using a 2.8-MeV external He beam and a beam dose of 200 {mu}C, beryllium concentrations from 5 to 16 {mu}g/g have been measured in the samples, with a detection limit of 1 {mu}g/g.

  11. Sanitary-hygienic and ecological aspects of beryllium production

    Energy Technology Data Exchange (ETDEWEB)

    Dvinskykh, E.M.; Savchuk, V.V.; Sidorov, V.L.; Slobodin, D.B.; Tuzov, Y.V. [Ulba Metallurgical Plant, Ust-Kamenogorsk (Kazakhstan)

    1998-01-01

    The Report describes An organization of sanitary-hygienic and ecological control of beryllium production at Ulba metallurgical plant. It involves: (1) the consideration of main methods for protection of beryllium production personnel from unhealthy effect of beryllium, (2) main kinds of filters, used in gas purification systems at different process areas, (3) data on beryllium monitoring in water, soil, on equipment. This Report also outlines problems connected with designing devices for a rapid analysis of beryllium in air as well as problems of beryllium production on ecological situation in the town. (author)

  12. Beryllium satellite thrust cone design, manufacture and test

    International Nuclear Information System (INIS)

    Schneiter, H.; Chandler, D.

    1977-01-01

    Pre-formed beryllium sheet material has been used in the design, manufacturing and test of a satellite thrust cone structure. Adhesive bonding was used for attachment of aluminium flanges and conical segment lap strips. Difficulties in beryllium structure design such as incompatibilities with aluminium and handling problems are discussed. Testing to optimize beryllium-beryllium and beryllium-aluminium adhesive bonds is described. The completed thrust cone assembly has been subjected to static load testing and the results are presented. A summary of the relative merits of the use of beryllium in satellite structures is given with recommendations for future users. (author)

  13. Beryllium-rich intermediate phases in beryllium alloys

    International Nuclear Information System (INIS)

    Raynor, G.V.

    1977-01-01

    The results of a survey of the factors affecting the formation of phases of stoichiometry MBe 5 , M 2 Be 17 , MBe 12 and MBe 13 are presented. Using published information it is shown that the structures adopted at the higher Be:M ratios involve different characteristics from those adopted at lower Be:M ratios. In the ThMn 12 and NaZn 13 structures adopted in the former case dsub(M-Be) > (rsub(M) + rsub(Be)), (where the atomic radii refer to coordination number 12) and the dsub(Be-Be) distances are contracted. In the CaCu 5 structure adopted at composition MBe 5 , dsub(M-Be) < (rsub(M) + rsub(Be)) and interactions between unlike atoms are significant. The structural characteristics, occurrence, and the stabilities of these phases, and of the others mentioned above, are discussed in terms of atomic radius ratios, the position of the M component in the periodic table, and the value of the univalent ionic radius of the M component, taken as a measure of the extension in space of the hard incompressible ionic core. Though the compound-forming characteristics of beryllium are largely dictated by its small atomic diameter, other factors such as the nature of the bonding which can be exerted by the partner atoms are also significant. In particular, the proportions of the volumes of the atoms which are occupied by the hard incompressible ionic cores assume importance. (author)

  14. Thermomechanical testing of beryllium for the JET/ISX-B beryllium limiter experiment

    International Nuclear Information System (INIS)

    Watson, R.D.; Smith, M.F.; Whitley, J.B.; McDonald, J.M.

    1984-01-01

    Materials testing of S-65-B beryllium has been conducted in support of the beryllium limiter experiment on the ISX-B tokamak. The S-65-B grade of hot-pressed beryllium was chosen over S-200-E because of its superior strength and ductility at elevated temperatures. The testing has included measurement of tensile and yield strength, ductility, Young's Modulus, thermal conductivity, and specific heat from 50 0 C to 700 0 C. Thermal fatigue testing of a 2.5 cm beryllium cube was conducted using an electron beam to apply a heat flux of 2.5 kw/cm 2 for 0.3 second pulses for 1500 cycles. Results from the tests are compared to elastic-plastic finite element stress calculations. The testing indicates that the ISX-B beryllium limiter should survive the tokamak environment without serious structural failure, although some surface cracking is expected to occur. (author)

  15. Proceedings of the sixth IEA international workshop on beryllium technology for fusion

    Energy Technology Data Exchange (ETDEWEB)

    Kawamura, Hiroshi [Japan Atomic Energy Research Inst., Kashiwa, Chiba (Japan); Tanaka, Satoru [Tokyo Univ., Tokyo (Japan); Ishitsuka, Etsuo [Japan Atomic Energy Research Inst., Oarai, Ibaraki (Japan). Oarai Research Establishment

    2004-03-01

    This report is the Proceedings of the Sixth International Energy Agency International Workshop on Beryllium Technology for Fusion. The workshop was held on December 2-5, 2003, at SEAGAIA in Miyazaki City, Japan with 69 participants who attended from Europe, the Russian Federation, Kazakhstan, Ukraine, China, the United States and Japan. The topics for papers were arranged into nine sessions; Status of beryllium study, Plasma and tritium interactions, ITER oriented issues, Neutron irradiation effects, Beryllide application, Disposal and recycling, Molten salt, Health and safety issues and Panel discussion. In the Panel discussion, the international collaboration for three topics, i.e., Neutron irradiation effects, Beryllide application, Recycling and Disposal, were discussed, and necessary items for the international collaboration were proposed. The 46 of the presented papers are indexed individually. (J.P.N.)

  16. Deuterium trapping in ion implanted and co-deposited beryllium oxide layers

    International Nuclear Information System (INIS)

    Markin, A.V.; Gorodetsky, A.E.; Zakharov, A.P.; Wu, C.H.

    2000-01-01

    Deuterium trapping in beryllium oxide films irradiated with 400 eV D ions has been studied by thermal desorption spectroscopy (TDS). It has been found that for thermally grown BeO films implanted in the range 300 - 900 K the total deuterium retention doesn't depend whereas TDS spectra do markedly on irradiation temperature. For R.T. implantation the deuterium is released in a wide range from 500 to 1100 K. At implantation above 600 K the main portion of retained deuterium is released in a single peak centered at about 1000 K. The similar TDS peak is measured for D/BeO co-deposited layer. In addition we correlate our implantation data on BeO with the relevant data on beryllium metal and carbon. The interrelations between deuterium retention and microstructure are discussed. (orig.)

  17. Status of the beryllium replacement project

    Energy Technology Data Exchange (ETDEWEB)

    Dimayuga, I. [Atomic Energy of Canada, Chalk River, Ontario (Canada); Corcoran, E. [Royal Military College of Canada, Kingston, Ontario (Canada); Daniels, T. [Ontario Power Generation, Pickering, Ontario (Canada); Harmsen, J. [Cameco Fuel Manufacturing Inc., Port Hope, Ontario (Canada); Lu, E. [Bruce Power, Tiverton, Ontario (Canada); Onderwater, T.; Palleck, S. [General Electric- Hitachi, Wilmington, North Carolina (United States); Pant, A. [Cameco Fuel Manufacturing Inc., Port Hope, Ontario (Canada)

    2013-07-01

    Currently, beryllium (Be) is used as the filler metal for brazing appendages on the sheaths of CANDU® fuel elements. Because of its toxicity, occupational exposure limits for Be are being reduced to very low levels, resulting in significant challenges to CANDU® fuel fabricators. The CANDU® Owners Group (COG) initiated a test program to identify a filler material to replace Be and confirm that the brazed joints meet the established technical requirements for CANDU® fuel. Together with eliminating health risks associated with the use of Be, the industry needs to be assured that continuation of fuel supply remains unaffected and that fuel fabrication processes continue to comply with health and safety standards. A literature survey of studies on brazing and joining of Zircaloy identified potential filler materials that can meet or exceed existing design requirements of the brazed joint, including the required mechanical, microstructural, corrosion resistance, and irradiation properties equivalent to those obtained with Be as braze material. Candidate materials were evaluated against several criteria, including manufacturability, melting point, wettability, mechanical properties, corrosion resistance, effect on neutron economy, potential activation products, and interaction with fuel channels and other related disciplines. This exercise resulted in a list of promising candidate materials that were recommended for the first phase of testing. These materials include stainless steel (304 or 316), Al-Si, Ni-P, and Zr-Mn alloys. To allow a CANDU® utility have sufficient confidence in considering implementation of a different braze filler material, a Be Replacement Test Program, involving out-reactor and in-reactor tests, is being undertaken as a collaborative endeavour by the Canadian nuclear industry. The out-reactor tests consist of: a constructability assessment to determine the material’s suitability with current fuel manufacturing methods; evaluation of

  18. Radiobiologic significance of apoptosis and micronucleation in quiescent cells within solid tumors following γ-ray irradiation

    International Nuclear Information System (INIS)

    Masunaga, Shin-ichiro; Ono, Koji; Suzuki, Minoru; Kinashi, Yuko; Takagaki, Masao

    2001-01-01

    Purpose: To determine the frequency of apoptosis in quiescent (Q) cells within solid tumors following γ-ray irradiation, using four different tumor cell lines. In addition, to assess the significance of detecting apoptosis in these cell lines. Methods and Materials: C3H/He mice bearing SCC VII or FM3A tumors, Balb/c mice bearing EMT6/KU tumors, and C57BL mice bearing EL4 tumors received 5-bromo-2'-deoxyuridine (BrdU) continuously for 5 days via implanted mini-osmotic pumps to label all proliferating (P) cells. The mice then received γ-ray irradiation at a dose of 4-25 Gy while alive or after tumor clamping. Immediately after irradiation, the tumors were excised, minced, and trypsinized. The tumor cell suspensions thus obtained were incubated with cytochalasin-B (a cytokinesis blocker), and the micronucleus (MN) frequency in cells without BrdU labeling (=Q cells) was determined using immunofluorescence staining for BrdU. Meanwhile, 6 hours after irradiation, tumor cell suspensions obtained in the same manner were fixed. The apoptosis frequency in Q cells was also determined with immunofluorescence staining for BrdU. The MN and apoptosis frequency in total (P+Q) tumor cells were determined from the tumors that were not pretreated with BrdU. Results: In total cells, SCC VII, FM3A, and EMT6/KU cells showed reasonable relationships between MN frequency and surviving fraction (SF). However, fewer micronuclei were induced in EL4 cells than the other cell lines. In contrast, a comparatively close relationship between apoptosis frequency and SF was found in total cells of EL4 cell line. Less apoptosis was observed in the other cell lines. Quiescent tumor cells exhibited significantly lower values of MN and apoptosis frequency probably due to their large hypoxic fraction, similar to total tumor cells on clamped irradiation. Conclusion: γ-ray irradiation induced MN formation in SCC VII, FM3A, and EMT6/KU tumor cells, and the apoptosis was marked in EL4 cells compared with

  19. Beryllium. Health hazards and their control. Pt. 2

    International Nuclear Information System (INIS)

    Lires, O.A.; Delfino, C.A.; Botbol, J.

    1991-01-01

    In this work (continuation of 'Beryllium' series) health hazards, toxic effects, limits of permissible atmospheric contamination and safe exposure to beryllium are described. Guidelines to the design, control operations and hygienic precautions of the working facilities are given. (Author) [es

  20. 75 FR 80734 - Chronic Beryllium Disease Prevention Program

    Science.gov (United States)

    2010-12-23

    ... are used in nuclear weapons as nuclear reactor moderators or reflectors and as nuclear reactor fuel...), grinding, and machine tooling of parts. Inhalation of beryllium particles may cause chronic beryllium...

  1. A wide temperature range irradiation cryostat for reasearch on solid state targets

    Energy Technology Data Exchange (ETDEWEB)

    Reeve, Scott; Dutz, Hartmut; Goertz, Stefan; Runkel, Stefan; Voge, Thomas [Physikalisches Institut, Universitaet Bonn (Germany)

    2012-07-01

    To qualitatively improve the data obtained in asymmetry measurements of scattering experiments the figure of merit (FOM) plays a major role and can reduce the data acquisition time when a certain precision in the measurement is needed. One of the defining factors for the improvement of the polarised experiment lies in the target choice and preparation, in particular the method employed to introduce the paramagnetic defects for the use of dynamic nuclear polarisation (DNP). To this end the Polarized Target Group in Bonn has developed a wide range temperature cryostat for the irradiation of potential target materials in which materials can be irradiated to varying doses at specified temperatures. The stable irradiation temperature of the materials can be controlled to within {+-}1 K over a range of 90 K

  2. Single-laboratory evaluation of SW-846 Methods 7090/7091 determination of beryllium by flame and furnace atomic absorption spectrophotometry. Summary report January-August 1987

    International Nuclear Information System (INIS)

    Hodge, V.F.; Darby, D.A.; Thompson, W.E.; Jones, C.L.

    1988-02-01

    The results of a single-laboratory study of the Determination of Beryllium by Flame and Furnace Atomic Absorption Spectrophotometry, are described. The study examined the application of these two powerful beryllium detection methods to the analysis of selected liquid and solid samples after digestion by appropriate SW-846 methods. Method performance data including detection limits, optimum concentration ranges (linearity), spike recoveries, interferences, precision, accuracy, and optimum operating parameters are presented and discussed

  3. A simple model for the microstructural evolution of solids under irradiation

    International Nuclear Information System (INIS)

    Valentin, P.P.; Martin, G.

    1982-01-01

    The coupled evolutions of the void and dislocation populations in crystals under high-temperature irradiation are studied by a simple heuristic theoretical approach: rate equations are used for describing both defect concentrations and microstructural variables, and the trajectories of the point representative of the microstructure in the appropriate state space are studied. Qualitatively different microstructural evolutions are found depending on the irradiation flux and temperature. Non-trivial behaviours are revealed such as: transient swelling, effect of cold work on the incubation dose for swelling, large dose divergence of evolutions which looked similar at low dose (which should result in large swelling heterogeneities) and radiation-enhanced sintering. (author)

  4. Effect of machining damage on tensile properties of beryllium

    International Nuclear Information System (INIS)

    Hanafee, J.E.

    1976-01-01

    It is well established that damage introduced at the surface of beryllium during machining operations can lower its mechanical properties. Tensile tests were conducted to illustrate this on beryllium presently being used for parts in the W79 program and similar to the new powder-processed beryllium specified for production (tentative specification MEL 76-001319). The objective of this study is to quantitatively illuminate the importance of controlling machining damage in this particular grade of powder-processed beryllium

  5. Experimental simulation of irradiation effects on thermomechanical behaviour of UO2 fuel: Impact of solid and gaseous fission products

    International Nuclear Information System (INIS)

    Balland, J.

    2007-12-01

    Predictive simulation of thermomechanical behaviour of nuclear fuel has to take into account irradiation effects. Fission Products (FP) can modify the thermomechanical behaviour of UO 2 . During this thesis, differentiation was made between fission products which create a solid solution with UO 2 and gaseous products, generating pressurized bubbles. SIMFUELS containing gadolinium oxide and pressurized argon bubbles were manufactured, respectively by conventional process and by Gas Pressure Sintering. Brittle and ductile behaviour of UO 2 was investigated, under experimental conditions representative of Pellet-Cladding Interaction (PCI), respectively with 3 points bending tests and compressive creep tests. Investigation of brittle behaviour of UO 2 showed that fracture is mainly controlled by natural defects, like porosities, acting like starting points for cracks propagation. Addition of simulates fission products increase the brittle-to-ductile transition temperature of UO 2 , up to 400-500 C regarding FP in solid solution, and up to 200 C for gaseous products. Fission products although reduce fracture stresses, by a factor between 1.5 and 4, respectively for gas bubbles and solid solutions. Decrease of fracture stress is linked to an increase of microstructural defects due the solid solution and to pressurized bubbles located at grain boundaries. Pellets were tested under compressive solicitation at high temperatures. Experimental results of creep tests are well represented by Norton laws. Creep controlling mechanisms are evidenced by microstructural analysis performed on pellets at different strains. On the basis of calculations made for fuels having the same microstructures than the SIMFUELs, a creep factor is determined. It revealed a strong hardening effect of the solid solution, due to the fact that the added elements anchor the dislocations, whereas pressurized bubbles showed a coupling between hardening and softening effects. (author)

  6. Occupational and non-occupational allergic contact dermatitis from beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Vilaplana, J; Romaguera, C; Grimalt, F [Allergy Department, Dermatological Service Hospital Clinico, Barcelona (Spain)

    1992-01-01

    There are various references to sensitization to beryllium in the literature. Since introducing a patch testing series for patients with suspected sensitization to metals, we have found 3 cases of sensitization to beryllium. Of these 3 cases, we regard the first 2 as having relevant sensitization. Beryllium chloride (1% pet.) was positive in 3 patients and negative in 150 controls. (au).

  7. Occupational and non-occupational allergic contact dermatitis from beryllium

    International Nuclear Information System (INIS)

    Vilaplana, J.; Romaguera, C.; Grimalt, F.

    1992-01-01

    There are various references to sensitization to beryllium in the literature. Since introducing a patch testing series for patients with suspected sensitization to metals, we have found 3 cases of sensitization to beryllium. Of these 3 cases, we regard the first 2 as having relevant sensitization. Beryllium chloride (1% pet.) was positive in 3 patients and negative in 150 controls. (au)

  8. The kinetics of formation and transformation of silver atoms on solid surfaces subjected to ionizing irradiation

    International Nuclear Information System (INIS)

    Popovich, G.M.

    1988-01-01

    The paper discusses the results obtained in ESR-assisted studies of the kinetics of formation and transformation of silver atoms generated by γ-irradiation of silver-containing carriers. Three types of dependences have been established: (1) extreme; (2) saturation curves and (3) step-like. All the kinetic curves display, after a definite period of time, stable concentrations of adsorbed silver atoms per unit of the surface at a given temperature. Depending on the temperature of the experiment, the composition and nature of the carrier, the number of adsorbed silver ions, the irradiation dose and conditions of the experiment, a stable concentration of silver atoms at a given temperature may be equal to, higher or lower than the number of silver atoms measured immediately after γ-irradiation at a temperature of liquid nitrogen. A kinetic scheme is proposed to explain the obtained curves. The model suggests that the silver atoms adsorbed on the surface, as well as those formed after γ-irradiation, are bonded to the surface by various energies, which are related to heterogeneity of the carrier surface. (author)

  9. Determinations of the temperature of terminal solid solubility in dissolution and precipitation of hydrogen/deuterium in irradiated Zircaloy-4

    Energy Technology Data Exchange (ETDEWEB)

    Vizcaino, P [CNEA-CONICET, Centro Atomico Ezeiza (Argentina)

    2012-07-01

    The proposed plan is an approach to the metallurgical consequences of the high neutron fluencies (10''2''2 n/cm''2) on the hydrogen behavior in zirconium based alloys, based on the significance of the microstructural behavior of the high burn up fuel claddings during the dry storage period. The studies are focused on Zircaloy-4, concerning to two processes: Neutron irradiation damage; Hydrogen pick up. The Zircaloy-4 was taken from cooling channels of the PHWR Atucha 1. These components remained more than 10 years in service, reaching neutron fluencies up to 10''2''2 n/cm''2. In the last recent years, measurements of the hydride dissolution temperatures have shown that hydrogen solubility is affected by the neutron irradiation, increasing it respect to the unirradiated Zircaloy solubility. In addition, in this material the amorphization/dissolution of the second phase particles (SPPs) was observed, being proposed an interaction between the hydrogen atoms, the SPPs and the irradiation defects as a possible explanation of the observed behavior. For the present case, attention will be focused on the hydride precipitation process, since it is strongly related with delay hydrogen cracking initiation, a problem of direct concern for the dry storage. The goal of the present proposal is to make an approach to the source of the observed effect, applying several specific techniques as differential scanning calorimetry (DSC), high resolution x-ray diffraction and transmission electron microscopy. The objectives can be divided as follows: Determination of the temperatures of terminal solid solubility in dissolution (TTSSd) and in precipitation (TTSSp) in high fluency irradiated Zircaloy-4, reproducing the temperatures at which the Zircaloy fuel claddings remain during dry storage by an annealing program during the DSC experiments; Observations by optical and transmission electron microscopy of the hydride distribution before (as received material) and after high temperature

  10. Beryllium phonon spectrum from cold neutron measurements

    International Nuclear Information System (INIS)

    Bulat, I.A.

    1979-01-01

    The inelastic coherent scattering of neutrons with the initial energy E 0 =4.65 MeV on the spectrometer according to the time of flight is studied in polycrystalline beryllium. The measurements are made for the scattering angles THETA=15, 30, 45, 60, 75 and 90 deg at 293 K. The phonon spectrum of beryllium, i-e. g(w) is reestablished from the experimental data. The data obtained are compared with the data of model calculations. It is pointed out that the phonon spectrum of beryllium has a bit excessive state density in the energy range from 10 to 30 MeV. It is caused by the insufficient statistical accuracy of the experiment at low energy transfer

  11. Spectrographic determination of impurities in beryllium oxide

    International Nuclear Information System (INIS)

    Paula Reino, L.C. de; Lordello, A.R.; Pereira, A.S.A.

    1986-03-01

    A method for the spectrographic determination of Al, B, Cd, Co, Cu, Cr, Fe, Mg, NaNi, Si and Zn in nuclear grade beryllium oxide has been developed. The determination of Co, Al, Na and Zn is besed upon a carrier distillation technique. Better results were obtained with 2% Ga 2 O 3 as carrier in beryllium oxide. For the elements B, Cd, Cu, Fe, Cr, Mg, Ni and Si the sample is loaded in a Scribner-Mullin shallow cup electrode, covered with graphite powder and excited in DC arc. The relative standard deviation values for different elements are in the range of 10 to 20%. The method fulfills requirements of precision and sensitivity for specification analysis of nuclear grade beryllium oxide.(Author) [pt

  12. On two possible mechanisms of metallic island remotion from solid surface at heavy multicharged ion irradiation

    International Nuclear Information System (INIS)

    Vorob'eva, I.V.; Geguzin, Ya.E.; Monastyrenko, V.E.

    1986-01-01

    Two mechanisms of energy transfer from a moving ion to a metallic island film on a solid surface are described. A particular case when the energy transfer quantity is enough to remove an island from the solid surface breaking adhesion bond is considered. One mechanism is 'shaking off', another one is a 'jumping up' mechanism. The essence of the first mechanism is that an ion bombarding the surface excites a cylindrical shock wave with a front that can 'shake off' islands from the solid surface along the ion trajectory when it reaches the surface. An island is heated in pulsed mode, and during thermal expansion it should push off the substrate, and so it jumps up. The pure case of such mechanism is observed when an ion transverses an island and transfers energy to the latter one that is defined by the quantity of ion energy losses in the island

  13. Electron-beam-irradiation-induced crystallization of amorphous solid phase change materials

    Science.gov (United States)

    Zhou, Dong; Wu, Liangcai; Wen, Lin; Ma, Liya; Zhang, Xingyao; Li, Yudong; Guo, Qi; Song, Zhitang

    2018-04-01

    The electron-beam-irradiation-induced crystallization of phase change materials in a nano sized area was studied by in situ transmission electron microscopy and selected area electron diffraction. Amorphous phase change materials changed to a polycrystalline state after being irradiated with a 200 kV electron beam for a long time. The results indicate that the crystallization temperature strongly depends on the difference in the heteronuclear bond enthalpy of the phase change materials. The selected area electron diffraction patterns reveal that Ge2Sb2Te5 is a nucleation-dominated material, when Si2Sb2Te3 and Ti0.5Sb2Te3 are growth-dominated materials.

  14. The analysis of beryllium-copper diffusion joint after HHF test

    International Nuclear Information System (INIS)

    Guiniatouline, R.N.; Mazul, I.V.; Rubkin, S.Y.

    1995-01-01

    The development of beryllium-copper joints which can withstand to relevant ITER divertor conditions is one of the important tasks at present time. One of the main problem for beryllium-copperjoints, is the inter-metallic layers, the strength and life time of joints significantly depends from the width and contents of the intermetallic layers. The objective of this work is to study the diffusion joint of TGP-56 beryllium to OFHC copper after thermal response and thermocyclic tests with beryllium-copper mockup. The BEY test were performed at e-beam facility (EBTS, SNLA). The following methods were used for analyses: the roentgenographic analysis; X-ray spectrum analysis; the fracture graphic analysis. During the investigation the followed studies were done: the analysis of diffusion boundary Be-Cu, which was obtained at the crossection of one of the tiles, the analysis of the debonded surfaces of a few beryllium tiles and corresponding copper parts; the analysis of upper surface of one of the tiles after HHF tests. The results of this work have showed that: the joint roentgenographic and elements analyses indicated the following phases in the diffusion zone: Cu 2 Be (∼170 μm), CuBe (∼30μm), CuBe 2 (∼1 μm) and solid solution of copper in beryllium. The phases Cu 2 Be, CuBe and solid solution of copper in beryllium were indicated using quantitative microanalysis and phases CuBe, CuBe 2 , Cu, Be - by roentgenographic analysis; the source of fracture (initial crack) is located in the central part of the tiles, the crack caused by the influence of residual stresses during cooling of a mock-up after fabrication and developed under the conditions of slow elastic-plastic growing during the process of thermal fatigue testing. The analysis gives the important data about joint's quality and also may be used for any type of joints and its comparison for ITER applications

  15. A comparative study on the effective thermal conductivity of a single size beryllium pebble bed

    International Nuclear Information System (INIS)

    Abou-Sena, A.; Ying, A.; Abdou, M.

    2004-01-01

    Solid breeder blankets generally use beryllium-helium pebble beds to ensure sufficient tritium breeding. The data of the effective thermal conductivity, k eff , of beryllium pebble beds is important to the design of fusion blankets. It serves as a database for benchmarking the models of pebble beds. The objective of this paper is to review and compare the available data (obtained by several studies) of the effective thermal conductivity of beryllium pebble beds in order to address the current status of these data. Two comparisons are presented: one for the data of k eff versus bed mean temperature and the second one for the data of k eff versus external applied pressures. The data (k eff versus bed temperature) reported by Enoeda et al., Dalle Donne et al., and UCLA, have a similar particle size and packing fraction. Despite their similarity, the standard deviation values of their data are around 32%. Also, the data of the effective thermal conductivity as a function of mechanical pressure have standard deviation values of ∼50%. From the presented comparisons, significant discrepancies among the available data of k eff of the beryllium pebble beds were observed. These discrepancies may be attributed to the apparent differences among available studies, such as experiment technique, packing fraction, particle characteristics, bed dimensions, and temperature range and gradient across the bed. (author)

  16. European DEMO BOT solid breeder blanket

    International Nuclear Information System (INIS)

    Dalle Donne, M.

    1994-11-01

    The BOT (Breeder Outside Tube) Solid Breeder Blanket for a fusion DEMO reactor is presented. This is one of the four blanket concepts under development in the frame of the European fusion technology program with the aim to select in 1995 the two most promising ones for further development. In the paper the reference blanket design and external loops are described as well as the results of the theoretical and experimental work in the fields of neutronics, thermohydraulics, mechanical stresses, tritium control and extraction, development and irradiation of the ceramic breeder material, beryllium development, ferromagnetic forces caused by disruptions, safety and reliability. An outlook is given on the remaining open questions and on the required R and D program. (orig.) [de

  17. Preliminary results for explosion bonding of beryllium to copper

    International Nuclear Information System (INIS)

    Butler, D.J.; Dombrowski, D.E.

    1995-01-01

    This program was undertaken to determine if explosive bonding is a viable technique for joining beryllium to copper substrates. The effort was a cursory attempt at trying to solve some of the problems associated with explosive bonding beryllium and should not be considered a comprehensive research effort. There are two issues that this program addressed. Can beryllium be explosive bonded to copper substrates and can the bonding take place without shattering the beryllium? Thirteen different explosive bonding iterations were completed using various thicknesses of beryllium that were manufactured with three different techniques

  18. Growth of second phase particles in a copper--beryllium alloy. Final technical report

    International Nuclear Information System (INIS)

    Bunch, R.; Wells, R.; Mukherjee, A.K.

    1977-01-01

    Growth of second phase particles from a solid solution of copper-beryllium was studied to determine this alloy's suitability for acoustic emission testing. Optical and Scanning Electron microscopes were used to study the microstructure. Micro and macro hardness tests were also performed. A hardness curve for aging at 550 0 F was determined. Microscopic examination revealed the presence of large inclusions which make this alloy unsuitable for the acoustic tests envisioned

  19. 2-D simulation of hohlraum targets for HIDIF: gold vs. beryllium converters

    International Nuclear Information System (INIS)

    Honrubia, J.J.; Meyer-ter-Vehn, J.

    2000-01-01

    Two cylindrical hohlraum targets for heavy-ion-fusion are compared from the point of view of total ion-energy required to ignite a specified capsule. Target a, a simple bare gold cylindrical cavity behaves much more efficiently than Target b, the former one internally cladded with solid beryllium where convenient, to ensure ion energy conversion to X-rays mainly in this cladding. A discussion of the problem is provided. (authors)

  20. Beryllium research on FFHR molten salt blanket

    International Nuclear Information System (INIS)

    Terai, T.; Tanaka, S.; Sze, D.-K.

    2000-01-01

    Force-free helical reactor, FFHR, is a demo-relevant heliotron-type D-T fusion reactor based on the great amount of R and D results obtained in the LHD project. Since 1993, collaboration works have made great progress in design studies of FFHR with standing on the major advantage of current-less steady operation with no dangerous plasma disruptions. There are two types of reference designs, FFHR-1 and FFHR-2, where molten Flibe (LiF-BeF2) is utilized as tritium breeder and coolant. In this paper, we present the outline of FFHR blanket design and some related R and D topics focusing on Be utilization. Beryllium is used as a neutron multiplier in the design and Be pebbles are placed in the front part of the tritium breeding zone. In a Flibe blanket, HF (TF) generated due to nuclear transmutation will be a problem because of its corrosive property. Though nickel-based alloys are thought to be intact in such a corrosive environment, FFHR blanket design does not adopt the alloys because of their induced radioactivity. The present candidate materials for the structure are low-activated ferritic steel (JLF-1), V-4Cr-4Ti, etc. They are capable to be corroded by HF in the operation condition, and Be is expected to work as a reducing agent in the system as well. Whether Be pebbles placed in a Flibe flow can work well or not is a very important matter. From this point, Be solubility in Flibe, reaction rate of the Redox reaction with TF in the liquid and on the surface of Be pebbles under irradiation, flowing behavior of Flibe through a Be pebble bed, etc. should be investigated. In 1997, in order to establish more practical and new data bases for advanced design works, we started a collaboration work of R and D on blanket engineering, where the Be research above mentioned is included. Preliminary dipping-test of Be sheets and in-situ tritium release experiment from Flibe with Be sheets have got started. (orig.)

  1. Determination of radiation-induced hydrocarbons in processed food and complex lipid matrices. A new solid phase extraction (SPE) method for detection of irradiated components in food

    International Nuclear Information System (INIS)

    Hartmann, M.; Ammon, J.; Berg, H.

    1997-01-01

    Detection of irradiated components in processed food with complex lipid matrices can be affected by two problems. First, the processed food may contain only a small amount of the irradiated component, and the radiation-induced hydrocarbons may be diluted throughout the lipid matrix of the whole food. Second, in complex lipid matrices, the detection of prior irradiation is often disturbed by fat-associated compounds. In these cases, common solid phase extraction (SPE) Florisil clean-up alone is inadequate in the detection of prior irradiation. Subsequent SPE argentation chromatography of the Florisil eluate allows the measurement of small amounts of irradiated lipid-containing ingredients in processed food as well as the detection of prior irradiation in complex lipid matrices such as paprika and chilli. SPE argetation chromatography is the first method available for the selective enrichment of radiation-specific hydrocarbons from even complex lipid matrices, thus enabling the detection of irradiation does as low as 0.025 kGy. Furthermore, by using radiation-induced hydrocarbons in the detection of prior irradiation of paprika and chilli powder, a second independent method, the first being measurement of thermoluminescence, is available for the analysis of these matrices. Such analysis could be achieved by using this highly sensitive, cheap and easy to perform combined SPE Florisil/argentation chromatography method, without the need for sophisticated techniques like SFE-GC/MS or LC-GC/MS, so that highly sensitive detection of prior irradiation colud be performed in almost every laboratory

  2. Consideration of the 'Burp' phenomenon in solid methane accounting for nonuniform distribution of irradiation defects

    International Nuclear Information System (INIS)

    Shabalin, E. P.

    1997-09-01

    This paper focuses on an optional model of radical recombination in solid methane, apart from conventional theory. It shares the common property of two-order reactions, but accounts for local nonuniformitites of the objects involved (such as radical concentration, the track nature of energy deposition, and others). Accounting for local nonuniformity provides absolutely different results for the time dependence of the space-averaged concentration of radicals, both for the processes of their storage and 'burping', compared to the common approach; it also brings new conditions for the thermal instability of the methane slug under irradiation and gives a better understanding of most of the strange features of burp performances.

  3. Effect of solid phase on the selectivity of alkyl radical formation by gamma-irradiation of branched alkanes

    International Nuclear Information System (INIS)

    Koizumi, Hitoshi; Hashino, Masatoshi; Ichikawa, Tsuneki; Yoshida, Hiroshi

    1992-01-01

    ESR and electron spin echo measurements of alkyl radicals generated by γ-irradiation of glassy and crystalline branched alkanes C 10 ∼ C 13 have been carried out to elucidate the effect of molecular structure and solid phase on the selectivity of alkyl radical formation. Alkyl radicals generated and stabilized at 77 K in the glassy alkanes are secondary penultimate radicals. Tertiary radicals and secondary radicals other than the penultimate one are not generated either by hydrogen abstraction or from ionized or excited molecules. In the crystalline alkanes, however, a small amount of secondary internal radicals are generated in addition to the predominant formation of the secondary penultimate radicals. It is concluded that the detachment of C-H hydrogen preferentially takes place at the location where the motion of carbon atoms assisting the detachment of the C-H hydrogen easily occurs. (author)

  4. Development of beryllium bonds for plasma-facing components

    International Nuclear Information System (INIS)

    Franconi, E.; Ceccotti, G.C.; Magnoli, L.

    1992-01-01

    This study concerns the techniques of bonding beryllium to both structural material (AISI 316 SS) and heat sink material (copper and DS-copper) plates, and the characterization of the bonding material obtained. Conventional bonding techniques for joining Be to SS and copper using brazing alloys were first investigated. The best result was obtained using a silver-copper eutetic alloy as a brazing alloy. However, the high-temperature capability of the materials prepared by this method is limited by the performance of brazing alloys at the operating temperature. To avoid this problem, we are developing a joining process known as solid-state reaction bonding that improves the capability at the operating temperature. (orig.)

  5. Status of beryllium development for fusion applications

    International Nuclear Information System (INIS)

    Billone, M.C.; Donne, M.D.; Macaulay-Newcombe, R.G.

    1994-05-01

    Beryllium is a leading candidate material for the neutron multiplier of tritium breeding blankets and the plasma facing component of first wall and divertor systems. Depending on the application, the fabrication methods proposed include hot-pressing, hot-isostatic-pressing, cold isostatic pressing/sintering, rotary electrode processing and plasma spraying. Product forms include blocks, tubes, pebbles, tiles and coatings. While, in general, beryllium is not a leading structural material candidate, its mechanical performance, as well its performance with regard to sputtering, heat transport, tritium retention/release, helium-induced swelling and chemical compatibility, is an important consideration in first-wall/blanket design. Differential expansion within the beryllium causes internal stresses which may result in cracking, thereby affecting the heat transport and barrier performance of the material. Overall deformation can result in loading of neighboring structural material. Thus, in assessing the performance of beryllium for fusion applications, it is important to have a good database in all of these performance areas, as well as a set of properties correlations and models for the purpose of interpolation/extrapolation

  6. Method of beryllium implantation in germanium substrate

    International Nuclear Information System (INIS)

    Kagawa, S.; Baba, Y.; Kaneda, T.; Shirai, T.

    1983-01-01

    A semiconductor device is disclosed, as well as a method for manufacturing it in which ions of beryllium are implanted into a germanium substrate to form a layer containing p-type impurity material. There after the substrate is heated at a temperature in the range of 400 0 C. to 700 0 C. to diffuse the beryllium ions into the substrate so that the concentration of beryllium at the surface of the impurity layer is in the order of 10 17 cm- 3 or more. In one embodiment, a p-type channel stopper is formed locally in a p-type germanium substrate and an n-type active layer is formed in a region surrounded by, and isolated from, the channel stopper region. In another embodiment, a relatively shallow p-type active layer is formed at one part of an n-type germanium substrate and p-type guard ring regions are formed surrounding, and partly overlapping said p-type active layer. In a further embodiment, a p-type island region is formed at one part of an n-type germanium substrate, and an n-type region is formed within said p-type region. In these embodiments, the p-type channel stopper region, p-type guard ring regions and the p-type island region are all formed by implanting ions of beryllium into the germanium substrate

  7. Beryllium, a material of great promise

    International Nuclear Information System (INIS)

    Le Fauconnier, J.P.; Nomine, A.M.

    1992-01-01

    Beryllium is one of the lightest metals. It also owns an outstanding combination of physical, mechanical and nuclear properties which gives it a favorable position, compared to more usual materials, in various fields of applications. Constant technological advancements in the elaboration and working up have induced a significant improvement of its ductility and a reduction of the production costs. (Author). 12 refs., 7 figs

  8. Role of ultrasonic irradiation on transesterification of palm oil using calcium oxide as a solid base catalyst

    International Nuclear Information System (INIS)

    Poosumas, Jutipong; Ngaosuwan, Kanokwan; Quitain, Armando T.; Assabumrungrat, Suttichai

    2016-01-01

    Highlights: • Transesterification of palm oil using a circulated continuous flow ultrasonic reactor. • Heterogeneous system using CaO as catalyst. • Effects of ultrasonic frequency and power, and catalyst reusability were considered. • A single high frequency and high intensity irradiation is favorable for heterogeneous system. - Abstract: Biodiesel production from transesterification of palm oil using a circulated continuous flow ultrasonic reactor was investigated. Transesterification was carried out at 60 °C, 1 atm and a methanol-to-oil molar ratio of 9:1. The highest reaction rate was achieved at the catalyst loading of 2 wt%, and biodiesel yield constantly increased until transesterification equilibrium (about 80%) was reached. A higher ultrasonic frequency (50 kHz) promoted the heterogeneously catalyzed transesterification of refined palm oil, because the three-phase system (packed solid catalyst, methanol and oil) required more spatial distribution by ultrasonic irradiation. Moreover, the highest ultrasonic power also provided highest transesterification rate and biodiesel yield due to cavitation activity enhancement. Reusability of calcium oxide catalysts was also investigated, and results showed that this can be reused to provide high biodiesel yield for at least three operations with slight decrease in the rate of reaction due to counter balance effect of organic compounds deposition on the catalyst surface. The results from this study can be a basis for scaling up of the process to industrial scale.

  9. Potential exposures and risks from beryllium-containing products.

    Science.gov (United States)

    Willis, Henry H; Florig, H Keith

    2002-10-01

    Beryllium is the strongest of the lightweight metals. Used primarily in military applications prior to the end of the Cold War, beryllium is finding new applications in many commercial products, including computers, telecommunication equipment, and consumer and automotive electronics. The use of beryllium in nondefense consumer applications is of concern because beryllium is toxic. Inhalation of beryllium dust or vapor causes a chronic lung disease in some individuals at concentrations as low as 0.01 microg/m3 in air. As beryllium enters wider commerce, it is prudent to ask what risks this might present to the general public and to workers downstream of the beryllium materials industry. We address this question by evaluating the potential for beryllium exposure from the manufacturing, use, recycle, and disposal of beryllium-containing products. Combining a market study with a qualitative exposure analysis, we determine which beryllium applications and life cycle phases have the largest exposure potential. Our analysis suggests that use and maintenance of the most common types of beryllium-containing products do not result in any obvious exposures of concern, and that maintenance activities result in greater exposures than product use. Product disposal has potential to present significant individual risks, but uncertainties concerning current and future routes of product disposal make it difficult to be definitive. Overall, additional exposure and dose-response data are needed to evaluate both the health significance of many exposure scenarios, and the adequacy of existing regulations to protect workers and the public. Although public exposures to beryllium and public awareness and concern regarding beryllium risks are currently low, beryllium risks have psychometric qualities that may lead to rapidly heightened public concern.

  10. Mono-energetic ions emission by nanosecond laser solid target irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Muoio, A., E-mail: Annamaria.Muoio@lns.infn.it [Istituto Nazionale di Fisica Nucleare – Laboratori Nazionali del Sud, Via S. Sofia 62, 95123 Catania (Italy); Dipartimento di Fisica e Scienze della Terra, Università degli Studi di Messina, Viale F.S. D’Alcontres 31, 98166 Messina (Italy); Tudisco, S. [Istituto Nazionale di Fisica Nucleare – Laboratori Nazionali del Sud, Via S. Sofia 62, 95123 Catania (Italy); Altana, C. [Istituto Nazionale di Fisica Nucleare – Laboratori Nazionali del Sud, Via S. Sofia 62, 95123 Catania (Italy); Dipartimento di Fisica e Astronomia, Università degli Studi di Catania, Via S. Sofia 64, 95123 Catania (Italy); Lanzalone, G. [Istituto Nazionale di Fisica Nucleare – Laboratori Nazionali del Sud, Via S. Sofia 62, 95123 Catania (Italy); Università degli Studi di Enna “Kore”, Via delle Olimpiadi, 94100 Enna (Italy); Mascali, D.; Cirrone, G.A.P.; Schillaci, F. [Istituto Nazionale di Fisica Nucleare – Laboratori Nazionali del Sud, Via S. Sofia 62, 95123 Catania (Italy); Trifirò, A. [Dipartimento di Fisica e Scienze della Terra, Università degli Studi di Messina, Viale F.S. D’Alcontres 31, 98166 Messina (Italy); Sezione INFN, Catania (Italy)

    2016-09-01

    An experimental campaign aiming to investigate the acceleration mechanisms through laser–matter interaction in nanosecond domain has been carried out at the LENS (Laser Energy for Nuclear Science) laboratory of INFN-LNS, Catania. Pure Al targets were irradiated by 6 ns laser pulses at different pumping energies, up to 2 J. Advanced diagnostics tools were used to characterize the plasma plume and ion production. We show the preliminary results of this experimental campaign, and especially the ones showing the production of multicharged ions having very narrow energy spreads.

  11. Tensometrical properties of volumetric crystals of germanium-silicon solid solutions irradiated by fast electrons

    International Nuclear Information System (INIS)

    Abbasov, Sh.M.

    2002-01-01

    Full Text: In the present work the tensometrical properties of Ge1-xSix solid solution monocrystal contended of up to 15 at. % Si were investigated. The radiation-proof strain gauges of researched crystals were made. For this purpose the site was cutted out from a sample, perpendicularly or in parallel of a crystal axes. After polishing the samples had thickness of 30-40 microns, and length of 2 mm

  12. Status of Irradiation technology development in JMTR

    International Nuclear Information System (INIS)

    Inaba, Y.; Inoue, S.; Izumo, H.; Kitagishi, S.; Tsuchiya, K.; Saito, T.; Ishitsuka, E.

    2008-01-01

    Irradiation Engineering Section of the Neutron Irradiation and Testing Reactor Center was organized to development the new irradiation technology for the application at JMTR re operation. The new irradiation engineering building was remodeled from the old RI development building, and was started to use from the end of September, 2008. Advanced in situ instrumentation technology (high temperature multi paired thermocouple, ceramic sensor, application of optical measurement), 99M o production technology by new Mo solution irradiation method, recycling technology on used beryllium reflector, and so on are planned as the development of new irradiation technologies. The development will be also important for the education and training programs through the development of young generation in not only Japan but also Asian counties. In this report, as the status of the development the new irradiation technology, new irradiation engineering building, high temperature multi paired thermocouple, experiences of optical measurement, recycling technology on used beryllium reflector are introduced

  13. Status of irradiation technology development in JMTR

    International Nuclear Information System (INIS)

    Inaba, Y.; Inoue, S.; Izumo, H.; Kitagishi, S.; Tsuchiya, K.; Saito, T.; Ishitsuka, E.

    2008-01-01

    Irradiation Engineering Section of the Neutron Irradiation and Testing Reactor Centre was organised to development the new irradiation technology for the application at JMTR re-operation. The new irradiation engineering building was remoulded from the old RI development building, and was started to use from the end of September, 2008. Advanced in-situ instrumentation technology(high temperature multi-paired thermocouple, ceramic sensor,application of optical measurement), 99 Mo production technology by new Mo solution irradiation method,recycling technology on used beryllium reflector, and so on are planned as the development of new irradiation technologies. The development will be also important for the education and training programs through the development of young generation in not only Japan but also Asian countries. In this report, as the status of the development the new irradiation technology, new irradiation engineering building, high temperature multi-paired thermocouple, experiences of optical measurement, recycling technology on used beryllium reflector are introduced

  14. First-principles and classical molecular dynamics study of threshold displacement energy in beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Vladimirov, P.V. [Institute for Applied Materials – Applied Materials Physics, Karlsruhe Institute of Technology, P.O. Box 3640, 76021 Karlsruhe (Germany); Borodin, V.A., E-mail: Borodin_VA@nrcki.ru [National Research Center “Kurchatov Institute”, 123182 Moscow (Russian Federation); NRNU MEPhI, 115409 Moscow (Russian Federation)

    2017-02-15

    Highlights: • Beryllium is a functional material of future fusion reactors. • The threshold displacement energy by fast particles is studied. • Classical and first principles simulations are used. - Abstract: Beryllium selected as a neutron multiplier material for the tritium breeding blanket of fusion reactor should withstand high doses of fast neutron irradiation. The damage produced by irradiation is usually evaluated assuming that the number of atomic displacements to the threshold displacement energy, E{sub d}, which is considered as an intrinsic material parameter. In this work the value of E{sub d} for hcp beryllium is estimated simultaneously from classical and first-principles molecular dynamics simulations. Quite similar quantitative pictures of defect production are observed in both simulation types, though the predicted displacement threshold values seem to be approximately two times higher in the first-principles approach. We expect that, after more detailed first-principles investigations, this approach can be used for scaling the damage prediction predictions by classical molecular dynamics, opening a way for more consistent calculations of displacement damage in materials.

  15. Dried gamma-irradiated sewage solids use on calcareous soils: crop yeilds and heavy metals uptake

    International Nuclear Information System (INIS)

    McCaslin, B.D.; Sivinski, J.S.

    1979-01-01

    Experiments designed to examine gamma-radiation effects on extractable and plant-available sludge elements and to examine the response of crops to sludge applications on two typical, calcareous soils in New Mexico are summarized. Information has been given indicating that the radiation process of reducing pathogens in sewage products being developed by Sandia Laboratories, does not significantly increase the chemical extractability and plant uptake of a broad range of nutrients and heavy metals. However, radiation treatment greatly facilitates handling sewage for experimentation, because pathogen contamination precautions are eliminated and weed seeds killed. Studies on the effects of sludge irradiation on plant nutrient uptake revealed no concentration increases, agreeing with results presented herein. Sewage products may have special potential for use on calcareous soils, such as in New Mexico. For instance, in New Mexico the lack of potassium in sewage products is not a problem and the naturally high pH of New Mexico soil greatly reduces plant availability of many problem heavy metals. Dramatic increases in yield are typified by the greenhouse and field results presented herein, especially for the known micronutrient deficient soils of New Mexico. Results indicate that sewage sludge is an excellent Zn and Fe fertilizer. More research needs to be done before the economics of sludge application can be calculated and more field information is needed before irradiated sewage products are used indiscriminately

  16. Enzyme activity and allosteric characteristics of gamma-irradiated solid aspartate transcarbamylase

    International Nuclear Information System (INIS)

    Bigler, W.N.; Tolbert, B.M.

    1977-01-01

    Aspartate transcarbamylase purified from E. coli was lyophilized, irradiated in vacuo with γ radiation from a cesium-137 source, redissolved in buffer under a nitrogen atmosphere, and assayed for enzyme activity. Lyophilized and redissolved enzyme had normal catalytic and allosteric kinetic characteristics. The average D 37 observed with saturating substrate, 25 mM aspartate, was 4.1 Mrad. With less than saturating substrate, 5 mM aspartate, the activity increases from zero to 1.6 Mrad and then decreases with a D 37 of 7.2 Mrad. Inclusion of 1 mM CTP, an allosteric inhibitor, in the 5 mM aspartate assays results in a more pronounced maximum in the activity curve occurring at slightly higher dose, 2.2 Mrad. Inhibitability by CTP has a D 37 of 2.3 Mrad with doses below the activity maximum. Enzyme lyophilized in the presence of 1 mM CTP has a D 37 of 2.9 Mrad. ATCase activity changes caused by irradiation of lyophylized bacteria were qualitatively like the changes observed in the detailed studies with the purified enzyme. Apparent radiation sensitivities of ATCase in lyophilized bacteria were observed to vary with the technique used to disrupt the resuspended bacteria

  17. Dried gamma-irradiated sewage solids use on calcareous soils: crop yeilds and heavy metals uptake

    Energy Technology Data Exchange (ETDEWEB)

    McCaslin, B.D.; Sivinski, J.S.

    1979-01-01

    Experiments designed to examine gamma-radiation effects on extractable and plant-available sludge elements and to examine the response of crops to sludge applications on two typical, calcareous soils in New Mexico are summarized. Information has been given indicating that the radiation process of reducing pathogens in sewage products being developed by Sandia Laboratories, does not significantly increase the chemical extractability and plant uptake of a broad range of nutrients and heavy metals. However, radiation treatment greatly facilitates handling sewage for experimentation, because pathogen contamination precautions are eliminated and weed seeds killed. Studies on the effects of sludge irradiation on plant nutrient uptake revealed no concentration increases, agreeing with results presented herein. Sewage products may have special potential for use on calcareous soils, such as in New Mexico. For instance, in New Mexico the lack of potassium in sewage products is not a problem and the naturally high pH of New Mexico soil greatly reduces plant availability of many problem heavy metals. Dramatic increases in yield are typified by the greenhouse and field results presented herein, especially for the known micronutrient deficient soils of New Mexico. Results indicate that sewage sludge is an excellent Zn and Fe fertilizer. More research needs to be done before the economics of sludge application can be calculated and more field information is needed before irradiated sewage products are used indiscriminately. (ERB)

  18. Status of beryllium development for fusion applications

    International Nuclear Information System (INIS)

    Billone, M.C.; Macaulay-Newcombe, R.G.

    1995-01-01

    Beryllium is a leading candidate material for the neutron multiplier of tritium breeding blankets and the plasma-facing component of first-wall and divertor systems. Depending on the application, the fabrication methods proposed include hot-pressing, hot-isostatic-pressing, cold-isostatic-pressing/sintering, rotary electrode processing and plasma spraying. Product forms include blocks, tubes, pebbles, tiles and coatings. While, in general, beryllium is not a leading structural material candidate, its mechanical performance, as well as its performance with regard to sputtering, heat transport, tritium retention/release, helium-induced swelling and chemical compatibility, is an important consideration in first-wall/blanket design. Differential expansion within the beryllium causes internal stresses which may result in cracking, thereby affecting the heat transport and barrier performance of the material. Overall deformation can result in loading of neighboring structural material. Thus, in assessing the performance of beryllium for fusion applications, it is important to have a good database in all of these performance areas, as well as a set of properties correlations and models for the purpose of interpolation/extrapolation.In this current work, the range of anticipated fusion operating conditions is reviewed. The thermal, mechanical, chemical compatibility, tritium retention/release, and helium retention/swelling databases are then reviewed for fabrication methods and fusion operating conditions of interest. Properties correlations and uncertainty ranges are also discussed. In the case of the more complex phenomena of tritium retention/release and helium-induced swelling, fundamental mechanisms and models are reviewed in more detail. Areas in which additional data are needed are highlighted, along with some trends which suggest ways of optimizing the performance of beryllium for fusion applications. (orig.)

  19. Interfacial properties of HIP joint between beryllium and reduced activation ferritic/martensitic steel

    International Nuclear Information System (INIS)

    Hirose, T.; Ogiwara, H.; Enoeda, M.; Akiba, M.

    2007-01-01

    Full text of publication follows: ITER test blanket module is the most important components to validate energy production and fuel breeding process for future demonstration reactor. Reduced activation ferritic / martensitic steel is recognized as a promising structural material for breeding blanket systems. And Beryllium must be used as plasma facing materials for ITER in vessel components. In this work, interfacial properties of beryllium/reduced activation ferritic/martensitic steel (RAF/Ms) joint were investigated for a first wall of ITER test blanket module (TBM). The starting materials were ITER grade Beryllium, S65C and a Japanese RAF/M, F82H. The joint was produced by solid state hot isostatic pressing (HIP) method. Chromium layer with the thickness of 1 μm and 10 μm were formed by plasma vapor deposition on the beryllium surface as a diffusion barrier. The HIP was carried out at 1023 K and 1233 K which are determined by standard normalizing and tempering temperature of F82H. The joint made at 1233 K was followed by tempering at 1033 K. The bonding interface was characterized by electron probe microanalysis (EPMA). The bonding strength was also investigated by isometric four point bending tests at ambient temperature. EPMA showed chromium layer effectively worked as a diffusion barrier at 1023 K. However, the beryllium rich layer was formed in F82H after HIP at 1233 K followed by tempering. Bending tests revealed that thin chromium layer and low temperature HIP is preferable. The high temperature HIP introduce brittle BeFe inter metallic compounds along bonding interface. On the other hand, joint with thick chromium layer suffer from brittleness of chromium itself. (authors)

  20. Interfacial properties of HIP joint between beryllium and reduced activation ferritic/martensitic steel

    Energy Technology Data Exchange (ETDEWEB)

    Hirose, T. [Blanket Engineering Group, Japan Atomic Energy Agency, Naka, Ibaraki (Japan); Ogiwara, H. [Japan Atomic Energy Agency, Tokai-mura, Naga-gun, Ibaraki-ken (Japan); Enoeda, M. [Naka Fusion Research Establishment, J.A.E.R.I., Japan Atomic Energy Research Institute, Naka-gun, Ibaraki-ken (Japan); Akiba, M. [Naka Fusion Institute, Japan Atomic Energy Agency, Naka, Ibaraki (Japan)

    2007-07-01

    Full text of publication follows: ITER test blanket module is the most important components to validate energy production and fuel breeding process for future demonstration reactor. Reduced activation ferritic / martensitic steel is recognized as a promising structural material for breeding blanket systems. And Beryllium must be used as plasma facing materials for ITER in vessel components. In this work, interfacial properties of beryllium/reduced activation ferritic/martensitic steel (RAF/Ms) joint were investigated for a first wall of ITER test blanket module (TBM). The starting materials were ITER grade Beryllium, S65C and a Japanese RAF/M, F82H. The joint was produced by solid state hot isostatic pressing (HIP) method. Chromium layer with the thickness of 1 {mu}m and 10 {mu}m were formed by plasma vapor deposition on the beryllium surface as a diffusion barrier. The HIP was carried out at 1023 K and 1233 K which are determined by standard normalizing and tempering temperature of F82H. The joint made at 1233 K was followed by tempering at 1033 K. The bonding interface was characterized by electron probe microanalysis (EPMA). The bonding strength was also investigated by isometric four point bending tests at ambient temperature. EPMA showed chromium layer effectively worked as a diffusion barrier at 1023 K. However, the beryllium rich layer was formed in F82H after HIP at 1233 K followed by tempering. Bending tests revealed that thin chromium layer and low temperature HIP is preferable. The high temperature HIP introduce brittle BeFe inter metallic compounds along bonding interface. On the other hand, joint with thick chromium layer suffer from brittleness of chromium itself. (authors)

  1. Neutron irradiation effects on plasma facing materials

    Science.gov (United States)

    Barabash, V.; Federici, G.; Rödig, M.; Snead, L. L.; Wu, C. H.

    2000-12-01

    This paper reviews the effects of neutron irradiation on thermal and mechanical properties and bulk tritium retention of armour materials (beryllium, tungsten and carbon). For each material, the main properties affected by neutron irradiation are described and the specific tests of neutron irradiated armour materials under thermal shock and disruption conditions are summarized. Based on current knowledge, the expected thermal and structural performance of neutron irradiated armour materials in the ITER plasma facing components are analysed.

  2. Neutron irradiation effects on plasma facing materials

    International Nuclear Information System (INIS)

    Barabash, V.; Federici, G.; Roedig, M.; Snead, L.L.; Wu, C.H.

    2000-01-01

    This paper reviews the effects of neutron irradiation on thermal and mechanical properties and bulk tritium retention of armour materials (beryllium, tungsten and carbon). For each material, the main properties affected by neutron irradiation are described and the specific tests of neutron irradiated armour materials under thermal shock and disruption conditions are summarized. Based on current knowledge, the expected thermal and structural performance of neutron irradiated armour materials in the ITER plasma facing components are analysed

  3. Tensile properties of neutron irradiated solid HIP 316L(N). ITER Task T214, NET deliverable GB6 ECN-5

    International Nuclear Information System (INIS)

    Van Osch, E.V.; Tjoa, G.L.; Boskeljon, J.; Van Hoepen, J.

    1998-05-01

    The tensile properties of neutron irradiated Hot Isostatically Pressed (HIP) joints of type 316L(N) stainless steel (heat PM-130) have been measured. Cylindrical tensile test specimens of 4 mm diameter were irradiated in the High Flux Reactor (HFR) in Petten, The Netherlands, simulating the first wall conditions by a combination of high displacement damage with proportional amounts of helium. The solid HIP specimens were irradiated up to a target dose level of 5 dpa at a temperature of 550K. The damage levels realized range from 3.0 to 4.1 dpa, with helium contents up to 38 appm. Post irradiation testing temperatures ranged from 300 to 700K. The report contains the experimental conditions and summarises the results, which are given in terms of engineering stresses and strains and reduction of area. The main conclusions are that the unirradiated solid-HIP material is very soft, assumingly due to the relatively large grain size. Neutron irradiation induces both hardening and reduction of ductility, similar to the behaviour of 316L(N) plate. No failures related to debonding were observed for the tests of the unirradiated samples, however one of eight tested irradiated specimens fractured in the HIP joint, showing a flat fracture surface and a low reduction of area. 6 refs

  4. Investigation of a 0.52 eV absorption band of n-type Ge1-xSix solid solutions irradiated with fast electrons at 77 K

    International Nuclear Information System (INIS)

    Abbasov, Sh.M.; Allakhverdiev, K.R.; Agaverdieva, G.T.; Bakhyshov, N.A.; Nagiev, A.I.

    1987-01-01

    Solid solutions belonging to the Ge 1-x Si x system are among the promising semiconductor materials. There is no published information on the absorption band in the region of 0.52 eV in Ge 1-x Si x solid solutions irradiated with fast electrons. The authors determined the infrared absorption spectra, impurity photoconductivity, and Hall effect of n-type Ge 1-x Si x solid solutions doped with antimony. These solid solutions were irradiated at 77 K with 5 MeV electrons in doses up to 2 x 10 17 cm -2 . This irradiation was carried out by a method described in Ref. 3

  5. Solid targets and irradiation facilities for production of diagnostic and therapeutic radionuclides at the Debrecen cyclotron

    International Nuclear Information System (INIS)

    Tarkanyi, F.; Ando, L.; Szucs, Z.; Mahunka, I.; Kovacs, Z.

    2000-01-01

    The MGC-20E (NIIEFA, Leningrad, USSR) variable energy compact cyclotron (k=20) was installed in ATOMKI (Debrecen, Hungary) in 1985. Protons, deuterons, 3 He- and α-particles can be accelerated with currents up to 300 μA for internal irradiation and up to 50 μA for external beams. The establishment of the Cyclotron Laboratory was partly supported by the International Atomic Energy Agency. The application of the cyclotron is multipurpose: basic nuclear research, application of activation technique for analytical and wear studies, application of intense fast neutron source for agro-biological, bio-medical application and for radiation damage test of electronic components, and finally radioisotope production for medical diagnostics and for other scientific and applied fields. The cyclotron laboratory has six target rooms, a radiochemistry laboratory and a medical unit equipped with PET

  6. Tailor-made dimensions of diblock copolymer truncated micelles on a solid by UV irradiation.

    Science.gov (United States)

    Liou, Jiun-You; Sun, Ya-Sen

    2015-09-28

    We investigated the structural evolution of truncated micelles in ultrathin films of polystyrene-block-poly(2-vinylpyridine), PS-b-P2VP, of monolayer thickness on bare silicon substrates (SiOx/Si) upon UV irradiation in air- (UVIA) and nitrogen-rich (UVIN) environments. The structural evolution of micelles upon UV irradiation was monitored using GISAXS measurements in situ, while the surface morphology was probed using atomic force microscopy ex situ and the chemical composition using X-ray photoelectron spectroscopy (XPS). This work provides clear evidence for the interpretation of the relationship between the structural evolution and photochemical reactions in PS-b-P2VP truncated micelles upon UVIA and UVIN. Under UVIA treatment, photolysis and cross-linking reactions coexisted within the micelles; photolysis occurred mainly at the top of the micelles, whereas cross-linking occurred preferentially at the bottom. The shape and size of UVIA-treated truncated micelles were controlled predominantly by oxidative photolysis reactions, which depended on the concentration gradient of free radicals and oxygen along the micelle height. Because of an interplay between photolysis and photo-crosslinking, the scattering length densities (SLD) of PS and P2VP remained constant. In contrast, UVIN treatments enhanced the contrast in SLD between the PS shell and the P2VP core as cross-linking dominated over photolysis in the presence of nitrogen. The enhancement of the SLD contrast was due to the various degrees of cross-linking under UVIN for the PS and P2VP blocks.

  7. Safety handling of beryllium for fusion technology R and D

    International Nuclear Information System (INIS)

    Yoshida, Hiroshi; Okamoto, Makoto; Terai, Takayuki; Odawara, Osamu; Ashibe, Kusuo; Ohara, Atsushi.

    1992-07-01

    Feasibility of beryllium use as a blanket neutron multiplier, first wall and plasma facing material has been studied for the D-T burning experiment reactors such as ITER. Various experimental work of beryllium and its compounds will be performed under the conditions of high temperature and high energy particle exposure simulating fusion reactor conditions. Beryllium is known as a hazardous substance and its handling has been carefully controlled by various health and safe guidances and/or regulations in many countries. Japanese regulations for hazardous substance provide various guidelines on beryllium for the protection of industrial workers and environment. This report was prepared for the safe handling of beryllium in a laboratory scale experiments for fusion technology R and D such as blanket development. Major items in this report are; (1) Brief review of guidances and regulations in USA, UK and Japan. (2) Safe handling and administration manuals at beryllium facilities in INEL, LANL and JET. (3) Conceptual design study of beryllium handling facility for small to mid-scale blanket R and D. (4) Data on beryllium toxicity, example of clinical diagnosis of beryllium disease, and environmental occurence of beryllium. (5) Personnel protection tools of Japanese Industrial Standard for hazardous substance. (author) 61 refs

  8. Control of beryllium powder at a DOE facility

    International Nuclear Information System (INIS)

    Langner, G.C.; Creek, K.L.; Castro, R.G.

    1997-01-01

    Beryllium is contained in a number of domestic and national defense items. Although many items might contain beryllium in some manner, few people need worry about the adverse effects caused by exposure to beryllium because it is the inhalable form of beryllium that is most toxic. Chronic beryllium disease (CBD), a granulomas and fibrotic lung disease with long latency, can be developed after inhalation exposures to beryllium. It is a progressive, debilitating lung disease. Its occurrence in those exposed to beryllium has been difficult to predict because some people seem to react to low concentration exposures whereas others do not react to high concentration exposures. Onset of the disease frequently occurs between 15 to 20 years after exposure begins. Some people develop the disease after many years of low concentration exposures but others do not develop CBD even though beryllium is shown to be present in lungs and urine. Conclusions based on these experiences are that their is some immunological dependence of developing CBD in about 3--4% of the exposed population, but the exact mechanism involved has not yet been identified. Acute beryllium disease can occur after a single exposure to a concentration of greater than 0.100 mg/m3 (inhalation exposure); it is characterized by the development of chemical pneumoconiosis, a respiratory disease. The acute effect of skin contact is a dermatitis characterized by itching and reddened, elevated, or fluid-accumulated lesions which appear particularly on the exposed surfaces of the body, especially the face, neck, arms, and hands. Small particles of beryllium that enter breaks in the skin can lead to the development of granulomas and/or open sores that do not heal until the beryllium has been removed. Our interest is only airborne beryllium, which is found in areas that machine or produce beryllium

  9. Solid organic residues produced by irradiation of hydrocarbon-containing H2O and H2O/NH3 ices - Infrared spectroscopy and astronomical implications

    International Nuclear Information System (INIS)

    Khare, B.N.; Thompson, W.R.; Murray, B.G.J.P.T.; Chyba, C.F.; Sagan, C.

    1989-01-01

    Plasma-discharge irradiations were conducted for the methane clathrate expected in outer solar system satellites and cometary nuclei; also irradiated were ices prepared from other combinations of H 2 O with CH 4 , C 2 H 6 , or C 2 H 2 . Upon evaporation of the yellowish-to-tan irradiated ices, it is found that a colored solid film adheres to the walls of the reaction vessel at room temperature. These organic films are found to exhibit IR band identifiable with alkane, aldehide, alcohol, and perhaps alkene, as well as substituted aromatic functional groups. These spectra are compared with previous studies of UV- or photon-irradiated nonclathrated hydrocarbon-containing ices. 73 refs

  10. Problems of saturation of the excitation and creation of irreversible changes in solid after laser irradiation

    International Nuclear Information System (INIS)

    Sakhnyuk, L.A.; Trokhimchuck, P.P.

    2009-01-01

    The problem of modeling of processes of the irreversible interaction light and solid is discussed. This problem is connected with the processes of the saturation the excitation of respective scattering centers. The possible cascades of these processes are analyzed. The correlation between nonequilibrium and irreversible phenomena are analyzed. Two-dimensional sphalerite lattice of InSb was used for the kinetic modeling of the hierarchic processes of saturation of the excitation respective chemical bonds. The cascade characteristics of these processes were estimated for the cylindrical form of 'zone of energy scattering' of photon. The comparative analyses these results with results, which were received with the help straight method and method the spherical form of 'zone of energy scattering' of photon, is represented too. The good concordance of experimental and theoretical data was received. (authors)

  11. A Monte Carlo based development of a cavity theory for solid state detectors irradiated in electron beams

    International Nuclear Information System (INIS)

    Mobit, P.

    2002-01-01

    Recent Monte Carlo simulations have shown that the assumption in the small cavity theory (and the extension of the small cavity theory by Spencer-Attix) that the cavity does not perturb the electron fluence is seriously flawed. For depths beyond d max not only is there a significant difference between the energy spectra in the medium and in the solid cavity materials but there is also a significant difference in the number of low-energy electrons which cannot travel across the solid cavity and hence deposit their dose in it (i.e. stopper electrons whose residual range is less than the cavity thickness). The number of these low-energy electrons that are not able to travel across the solid state cavity increases with depth and effective thickness of the detector. This also invalidates the assumption in the small cavity theory that most of the dose deposited in a small cavity is delivered by crossers. Based on Monte Carlo simulations, a new cavity theory for solid state detectors irradiated in electron beams has been proposed as: D med (p)=D det (p) x s S-A med.det x gamma(p) e x S T , where D med (p) is the dose to the medium at point, p, D det (p) is the average detector dose to the same point, s S-A med.det is the Spencer-Attix mass collision stopping power ratio of the medium to the detector material, gamma(p) e is the electron fluence perturbation correction factor and S T is a stopper-to-crosser correction factor to correct for the dependence of the stopper-to-crosser ratio on depth and the effective cavity size. Monte Carlo simulations have been computed for all the terms in this equation. The new cavity theory has been tested against the Spencer-Attix cavity equation as the small cavity limiting case and also Monte Carlo simulations. The agreement between this new cavity theory and Monte Carlo simulations is within 0.3%. (author)

  12. Irradiation cryostat for LiH and LiD polarized solid targets

    International Nuclear Information System (INIS)

    Goertz, S.

    1991-01-01

    Scattering experiments with polarized nucleon targets are an important tool to understand the nuclear spin structure. Pion photoproduction experiments on polarized protrons and neutrons as well as measurements of the neutron and deuteron formfactors will be performed at ELSA. 7 LiH and 6 LiD seem to be attractive target materials for these experiments, because they offer high proton and deuteron polarisation, respectively. Expecially 6 LiD has further very important advantages compared to the common deuteron target materials as d-Butanol and ND 3 . This work describes the mechanism of DNP (Dynamic Nuclear Polarization) in LiH and LiD and gives a view on the nature of the so-called paramagnetic impurities in these materials. In order to maximize the nuclear polarization, the production of these radicals have to take place under well defined temperature conditions. Therefore the first version of an irradiation cryostat was built and tested in regard to its cooling power and temperature adjustment. (orig.)

  13. Solid-phase photocatalytic degradation of polyethylene-goethite composite film under UV-light irradiation

    International Nuclear Information System (INIS)

    Liu, G.L.; Zhu, D.W.; Liao, S.J.; Ren, L.Y.; Cui, J.Z.; Zhou, W.B.

    2009-01-01

    A novel photodegradable polyethylene-goethite (PE-goethite) composite film was prepared by embedding the goethite into the commercial polyethylene. The degradation of PE-goethite composite films was investigated under ultraviolet light irradiation. The photodegradation activity of the PE plastic was determined by monitoring its weight loss, scanning electron microscopic (SEM) analysis and FT-IR spectroscopy. The weight of PE-goethite (1 wt%) sample steadily decreased and led to the total 16% reduction in 300 h under UV-light intensity for 1 mW/cm 2 . Through SEM observation there were some cavities around the goethite powder in the composite films, but there were few changes except some surface chalking phenomenon in pure PE film. The degradation rate could be controlled by changing the concentration of goethite particles in PE plastic. The degradation of composite plastic initiated on PE-goethite interface and then extended into polymer matrix induced by the diffusion of the reactive oxygen species generated on goethite particle surface. The photocatalytic degradation mechanism of the composite films was briefly discussed.

  14. Fractionated half body irradiation for palliation of multiple symptomatic bone metastases from solid tumors

    Energy Technology Data Exchange (ETDEWEB)

    Sekiguchi, Kenji; Hayashi, Shinya; Sunagawa, Yoshimitsu; Sougawa, Mitsuharu; Nakazawa, Masanori; Yamashita, Takashi (Japanese Foundation for Cancer Research, Tokyo (Japan). Hospital)

    1992-06-01

    This was a phase I-II nonrandomized study that explored the toxicity and response of fractionated half-body irradiation (F-HBI) in patients with multiple symptomatic osseous metastases. The patients had no premedication and received 10 Gy in 5 fractions with a dose rate of 15 cGy/min. At the Cancer Institute Hospital, 9 patients were treated by this technique (1 upper and lower F-HBI, 6 upper F-HBI, 2 lower F-HBI). All patients were female and had adenocarcinomas (8 breast and 1 lung). Adverse effects were myelosuppression, vomiting and partial alopecia. But hematologic toxicity was treated with blood transfusion or G-CSF. All toxicity was transient, and no pneumonitis nor radiation-related deaths occurred. When given as palliation, F-HBI was found to relieve pain in 80% of the patients. In 10% of the patients the pain relief was complete. The mean time to achieve pain relief in responders after F-HBI was 9 days. The pain relief was long-lasting and continued without need of reirradiation for 40% of the remaining patient's life. This treatment modality appears to be well tolerated and effective in patients with multiple symptomatic osseous metastases. The optimal indications, dose and fractionation for F-HBI should be further explored in randomized trials. (author).

  15. Toxicokinetics of beryllium following inhalation of beryllium oxide by Beagle dogs. III

    International Nuclear Information System (INIS)

    Finch, G.L.; Haley, P.J.; Hoover, M.D.; Mewhinney, J.A.; Bice, D.E.; Eidson, A.F.

    1988-01-01

    Young adult Beagle dogs inhaled radiolabeled beryllium oxide aerosols ( 7 BeO) prepared at either 500 deg. or 1000 deg. C to achieve one of two initial lung burdens (ILBs) of BeO. After exposure, animals were monitored by whole body counting for 7 Be, and excreta, clinical, and radiographic data were collected. One group of dogs was assigned for serial sacrifice for quantitation of beryllium clearance from lung, translocation to other organs, and histopathologic analysis of lung and lymph nodes. A second group of dogs was subjected to periodic bronchopulmonary lavage for analysis of lymphocyte responsiveness to beryllium. These latter dogs were subsequently re-exposed to the high ILB level of BeO prepared t 500 deg. C. ILBs following the second exposure were higher than that after the first exposure (74 vs. 42 μg BeO/kg, respectively). Except for one dog that exhibited enhanced beryllium retention after the second exposure, patterns of whole body clearance were similar to those observed after the initial exposures to the 500 deg. C-BeO. Analysis of lymphocyte responsiveness to beryllium in the second group of dogs is continuing. (author)

  16. Toxicokinetics of beryllium following inhalation of beryllium oxide by Beagle dogs. III

    Energy Technology Data Exchange (ETDEWEB)

    Finch, G L; Haley, P J; Hoover, M D; Mewhinney, J A; Bice, D E; Eidson, A F

    1988-12-01

    Young adult Beagle dogs inhaled radiolabeled beryllium oxide aerosols ({sup 7}BeO) prepared at either 500 deg. or 1000 deg. C to achieve one of two initial lung burdens (ILBs) of BeO. After exposure, animals were monitored by whole body counting for {sup 7}Be, and excreta, clinical, and radiographic data were collected. One group of dogs was assigned for serial sacrifice for quantitation of beryllium clearance from lung, translocation to other organs, and histopathologic analysis of lung and lymph nodes. A second group of dogs was subjected to periodic bronchopulmonary lavage for analysis of lymphocyte responsiveness to beryllium. These latter dogs were subsequently re-exposed to the high ILB level of BeO prepared t 500 deg. C. ILBs following the second exposure were higher than that after the first exposure (74 vs. 42 {mu}g BeO/kg, respectively). Except for one dog that exhibited enhanced beryllium retention after the second exposure, patterns of whole body clearance were similar to those observed after the initial exposures to the 500 deg. C-BeO. Analysis of lymphocyte responsiveness to beryllium in the second group of dogs is continuing. (author)

  17. Characterization of plasma sprayed beryllium ITER first wall mockups

    Energy Technology Data Exchange (ETDEWEB)

    Castro, R.G.; Vaidya, R.U.; Hollis, K.J. [Los Alamos National Lab., NM (United States). Material Science and Technology Div.

    1998-01-01

    ITER first wall beryllium mockups, which were fabricated by vacuum plasma spraying the beryllium armor, have survived 3000 thermal fatigue cycles at 1 MW/m{sup 2} without damage during high heat flux testing at the Plasma Materials Test Facility at Sandia National Laboratory in New Mexico. The thermal and mechanical properties of the plasma sprayed beryllium armor have been characterized. Results are reported on the chemical composition of the beryllium armor in the as-deposited condition, the through thickness and normal to the through thickness thermal conductivity and thermal expansion, the four-point bend flexure strength and edge-notch fracture toughness of the beryllium armor, the bond strength between the beryllium armor and the underlying heat sink material, and ultrasonic C-scans of the Be/heat sink interface. (author)

  18. Characterization of Plasma Sprayed Beryllium ITER First Wall Mockups

    International Nuclear Information System (INIS)

    Castro, Richard G.; Vaidya, Rajendra U.; Hollis, Kendall J.

    1997-10-01

    ITER first wall beryllium mockups, which were fabricated by vacuum plasma spraying the beryllium armor, have survived 3000 thermal fatigue cycles at 1 MW/sq m without damage during high heat flux testing at the Plasma Materials Test Facility at Sandia National Laboratory in New Mexico. The thermal and mechanical properties of the plasma sprayed beryllium armor have been characterized. Results are reported on the chemical composition of the beryllium armor in the as-deposited condition, the through thickness and normal to the through thickness thermal conductivity and thermal expansion, the four-point bend flexure strength and edge-notch fracture toughness of the beryllium armor, the bond strength between the beryllium armor and the underlying heat sink material, and ultrasonic C-scans of the Be/heat sink interface

  19. Mechanisms of hydrogen retention in metallic beryllium and beryllium oxide and properties of ion-induced beryllium nitride; Rueckhaltemechanismen fuer Wasserstoff in metallischem Beryllium und Berylliumoxid sowie Eigenschaften von ioneninduziertem Berylliumnitrid

    Energy Technology Data Exchange (ETDEWEB)

    Oberkofler, Martin

    2011-09-22

    In the framework of this thesis laboratory experiments on atomically clean beryllium surfaces were performed. They aim at a basic understanding of the mechanisms occurring upon interaction of a fusion plasma with a beryllium first wall. The retention and the temperature dependent release of implanted deuterium ions are investigated. An atomistic description is developed through simulations and through the comparison with calculations based on density functional theory. The results of these investigations are compared to the behaviour of hydrogen upon implantation into thermally grown beryllium oxide layers. Furthermore, beryllium nitride is produced by implantation of nitrogen into metallic beryllium and its properties are investigated. The results are interpreted with regard to the use of beryllium in a fusion reactor. (orig.)

  20. Production and Magnetic Field Confinement of Laser-Irradiated Solid Particle Plasmas

    Energy Technology Data Exchange (ETDEWEB)

    Haught, A. F.; Polk, D. H.; Fader, W. J. [United Aircraft Research Laboratories East Hartford, CT (United States)

    1969-01-15

    The focused high-intensity beam from a Q-spoiled laser has been used to form a high-temperature, high-density plasma from a single 10-20 micron radius solid particle of lithium hydride which is electrically suspended in a vacuum environment free of all material supports. Time-resolved charge collection measurements of the freely expanding plasma have shown that a high degree of ionization of the 10{sup 15} atoms in the lithium hydride particle can be achieved and that the plasma produced is essentially spherically symmetric in density over the full 4 {pi} solid angle. Time-of-flight studies of the plasma expansion have shown that average electron and ion energies exceeding 200 electron volts are obtained and that the plasma expansion rate, like the plasma density, is spherically symmetric. No charge separation or separation of the lithium and hydrogen ions is observed in the expanding plasma. Numerical calculations of the plasma formation and expansion have been made using a one-dimensional spherical hydrodynamic model and, on the basis of the results obtained, an integrated similarity model has been developed for calculations of the plasma time history and energy over the range of conditions employed in the experiments. These calculations, which include the effects of laser pulse time history, fraction of the incident beam occupied by the expanding plasma, radial density and velocity gradients within the plasma, and spatial distribution of the incident laser energy, give results for the plasma radial density distribution, velocity profile, and plasma energy in good agreement with those determined experimentally over the full range of the present measurements. Measurements have been carried out to examine the interaction of these laser -produced plasmas with mirror, cusp, and minimum-B magnetic fields. Experiments with mirror and minimum-B magnetic fields up to 8 kC show that plasmas with densities of 10{sup 12} -10{sup 13} cm{sup -3} are confined for times of 5

  1. Measuring device for bending of beryllium reflector

    International Nuclear Information System (INIS)

    Nishida, Seiri; Sakamoto, Naoki.

    1994-01-01

    The device of the present invention can measure bending of a beryllium reflector formed in a reactor core of a nuclear reactor by a relatively easy operation. Namely, a sensor portion comprises a long-support that can be inserted to a fuel element-insertion hole disposed in the reactor and a plurality of distance sensors disposed in a longitudinal direction of the support. A supersonic wave sensor which is advantageous in the heat resistance, the size and the accuracy and can conduct measurement in water relatively easily is used as the distance sensors. However, other sensors, instead of the sensor described above, may also be used. The plurality of distance sensors detect the bending amount of the beryllium reflector in the longitudinal direction by such an easy operation of inserting such a sensor portion to the fuel element-insertion hole upon exchange of fuel elements. (I.S.)

  2. Premelting hcp to bcc Transition in Beryllium

    Science.gov (United States)

    Lu, Y.; Sun, T.; Zhang, Ping; Zhang, P.; Zhang, D.-B.; Wentzcovitch, R. M.

    2017-04-01

    Beryllium (Be) is an important material with wide applications ranging from aerospace components to x-ray equipment. Yet a precise understanding of its phase diagram remains elusive. We have investigated the phase stability of Be using a recently developed hybrid free energy computation method that accounts for anharmonic effects by invoking phonon quasiparticles. We find that the hcp → bcc transition occurs near the melting curve at 0 materials.

  3. Analysis of surface contaminants on beryllium windows

    International Nuclear Information System (INIS)

    Gmur, N.F.

    1986-12-01

    It is known that various crystalline and liquid compounds form on the downstream surfaces of beryllium windows exposed to air. It is also known that the integrity of such windows may be compromised resulting in leaks through the window. The purpose of this report is to document the occurrences described as they pertain to the NSLS and to analyze, where possible, the various substances formed

  4. Preparation and properties of beryllium diphosphide

    International Nuclear Information System (INIS)

    Brice, J.F.; Gerardin, R.; Zanne, M.; Gleitzer, C.; Aubry, J.

    1975-01-01

    The compound BeP 2 can be obtained by direct action of phosphor on beryllium metal at 800-1000 0 C, and by removal of arsenic with phosphor in the diarsenide BeAs 2 . BeP 2 is a non hygroscopic brown-red powder. The X rays diffraction provide evidence for a quadratic cell with a = 7.08 A and c = 15.06 A. The atomic stacking is diamond type

  5. Separation of actinides from irradiated An–Zr based fuel by electrorefining on solid aluminium cathodes in molten LiCl–KCl

    Energy Technology Data Exchange (ETDEWEB)

    Souček, P., E-mail: Pavel.Soucek@ec.europa.eu [European Commission, Joint Research Centre (JRC), Institute for Transuranium Elements (ITU), Postfach 2340, 76125 Karlsruhe (Germany); Murakami, T. [Central Research Institute of Electric Power Industry (CRIEPI), Komae-shi, Tokyo 201-8511 (Japan); Claux, B.; Meier, R.; Malmbeck, R. [European Commission, Joint Research Centre (JRC), Institute for Transuranium Elements (ITU), Postfach 2340, 76125 Karlsruhe (Germany); Tsukada, T. [Central Research Institute of Electric Power Industry (CRIEPI), Komae-shi, Tokyo 201-8511 (Japan); Glatz, J.-P. [European Commission, Joint Research Centre (JRC), Institute for Transuranium Elements (ITU), Postfach 2340, 76125 Karlsruhe (Germany)

    2015-04-15

    Highlights: • Electrorefining process in molten LiCl-KCl using solid Al electrodes was demonstrated. • High separation factors of actinides over lanthanides were achieved. • Efficient recovery of actinides from irradiated nuclear fuel was achieved. • Uniform, dense and well adhered deposits were obtained and characterised. • Kinetic parameters of actinide–aluminium alloy formation were evaluated. - Abstract: An electrorefining process for metallic spent nuclear fuel treatment is being investigated in ITU. Solid aluminium cathodes are used for homogeneous recovery of all actinides within the process carried out in molten LiCl–KCl eutectic salt at a temperature of 500 °C. As the selectivity, efficiency and performance of solid Al has been already shown using un-irradiated An–Zr alloy based test fuels, the present work was focused on laboratory-scale demonstration of the process using irradiated METAPHIX-1 fuel composed of U{sub 67}–Pu{sub 19}–Zr{sub 10}–MA{sub 2}–RE{sub 2} (wt.%, MA = Np, Am, Cm, RE = Nd, Ce, Gd, Y). Different electrorefining techniques, conditions and cathode geometries were used during the experiment yielding evaluation of separation factors, kinetic parameters of actinide–aluminium alloy formation, process efficiency and macro-structure characterisation of the deposits. The results confirmed an excellent separation and very high efficiency of the electrorefining process using solid Al cathodes.

  6. Low cycle fatigue properties of neutron irradiated solid HIP 316L(N). ITER Task T214, NET deliverable GB6 ECN-5

    International Nuclear Information System (INIS)

    Rensman, J.; Van Osch, E.V.; Tjoa, G.L.; Boskeljon, J.; Van Hoepen, J.

    1998-05-01

    The Low Cycle Fatigue (LCF) properties of neutron irradiated Hot Isostatically Pressed (HIP) joints of type 316L(N) stainless steel (heat PM-130) have been measured, as well as the LCF properties of reference 316L(N)-ERHII. Cylindrical LCF test specimens of 3 mm diameter were irradiated in the High Flux Reactor (HFR) in Petten, The Netherlands, simulating the first wall conditions of future fusion reactors by a combination of high displacement damage with proportional amounts of helium. The solid HIP specimens were irradiated up to a target dose level of 5 dpa at a temperature of 550K. The damage levels realised range from 3.0 to 4.4 dpa, with helium contents up to 41 appm. Testing temperature was equal to the irradiation temperature: 550K. The report contains the experimental conditions and summarises the results, which are given in terms of first cycle stress, the peak stress, the number of cycles where the peak stress is reached, the stress at half life and the plastic strain at half life, and the total number of cycles to failure, N f . The main conclusions are that the unirradiated solid-HIP materials has the same LCF properties as unirradiated 316L(N)-ERHII plate material. The neutron irradiation induces both hardening and reduction of fatigue life. The bond does not seem to have any effect on the fatigue properties for the unirradiated solid HIP 316L(N), whereas a combined effect of irradiation and the bond cannot be established. No failures related to debonding of the joint were observed for the tests. 7 refs

  7. Permeation behavior of deuterium implanted into beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Nakamura, Hirofumi; Hayashi, Takumi; O' hira, Shigeru; Nishi, Masataka [Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan). Tokai Research Establishment

    2001-09-01

    Study on Implantation Driven Permeation (IDP) behavior of deuterium through pure beryllium was investigated as a part of the research to predict the tritium permeation through the first wall components ITER (International Thermonuclear Experimental Reactor). The permeation experiments were carried out with two beryllium specimens, one was an unannealed specimen and the other was that annealed at 1173 K. The permeation flux was measured as a function of specimen temperature and incident ion flux. Surface analysis of specimen was also carried out after the permeation experiment. Permeation was observed only with the annealed specimen and no significant permeation was observed with unannealed specimen under the present experimental condition (maximum temperature: 685 K, detection limit: 1x10{sup 13} D atoms/m{sup 2}s). It could be attributed that the intrinsic lattice defects, which act as diffusion preventing site, decreased with the specimen annealing. Based on the result of steady and transient permeation behavior and surface analysis, it was estimated that the deuterium permeation implanted into annealed beryllium was controlled by surface recombination due to the oxide layer on the surface of the permeated side. (author)

  8. Dynamic behaviour of S200F beryllium

    International Nuclear Information System (INIS)

    Montoya, Dominique

    1991-01-01

    Compression tests have been made on a large scale of strain, strain rate (up to 2000 s -1 ) and temperature (between 20 C and 300 C). From these experiences, we have calculated a constitutive model for beryllium S200F, which can be used by computer codes. Its formulation is not far from Steinberg, Cochran and Guinan's. But in our case, the influences of temperature and strain rate appear clearly within the expression. To validate our equation, we have used it in a computer code. Its extrapolation for higher strain rates is in good agreement with experiments such as Taylor impact tests or plate impact tests (strain rates greater than 10 4 s -1 ). With micrography, we could settle a link between the main strain mode within the material, and the variation of one parameter of the model. Beside the constitutive model, we have shown that shock loaded beryllium behaves in two different ways. If the strain rate is lower than 5.10 6 s -1 , then it is proportional to the squared shock pressure. Beyond, it is a linear function of shock pressure to the power of four. By a spall study on beryllium, we have confirmed that it is excessively fragile. Its fracture is sudden, at a strength near 1 GPa. (author) [fr

  9. Quantitative method of determining beryllium or a compound thereof in a sample

    Science.gov (United States)

    McCleskey, T. Mark; Ehler, Deborah S.; John, Kevin D.; Burrell, Anthony K.; Collis, Gavin E.; Minogue, Edel M.; Warner, Benjamin P.

    2010-08-24

    A method of determining beryllium or a beryllium compound thereof in a sample, includes providing a sample suspected of comprising beryllium or a compound thereof, extracting beryllium or a compound thereof from the sample by dissolving in a solution, adding a fluorescent indicator to the solution to thereby bind any beryllium or a compound thereof to the fluorescent indicator, and determining the presence or amount of any beryllium or a compound thereof in the sample by measuring fluorescence.

  10. The Cryogenic Properties of Several Aluminum-Beryllium Alloys and a Beryllium Oxide Material

    Science.gov (United States)

    Gamwell, Wayne R.; McGill, Preston B.

    2003-01-01

    Performance related mechanical properties for two aluminum-beryllium (Al-Be) alloys and one beryllium-oxide (BeO) material were developed at cryogenic temperatures. Basic mechanical properties (Le., ultimate tensile strength, yield strength, percent elongation, and elastic modulus were obtained for the aluminum-beryllium alloy, AlBeMetl62 at cryogenic [-195.5"C (-320 F) and -252.8"C (-423"F)I temperatures. Basic mechanical properties for the Be0 material were obtained at cyrogenic [- 252.8"C (-423"F)] temperatures. Fracture properties were obtained for the investment cast alloy Beralcast 363 at cryogenic [-252.8"C (-423"F)] temperatures. The AlBeMetl62 material was extruded, the Be0 material was hot isostatic pressing (HIP) consolidated, and the Beralcast 363 material was investment cast.

  11. The Rocky Flats Environmental Technology Site beryllium characterization project

    International Nuclear Information System (INIS)

    Morrell, D.M.; Miller, J.R.; Allen, D.F.

    1999-01-01

    A site beryllium characterization project was completed at the Rocky Flats Environmental Technology Site (RFETS) in 1997. Information from historical reviews, previous sampling surveys, and a new sampling survey were used to establish a more comprehensive understanding of the locations and levels of beryllium contamination in 35 buildings. A feature of the sampling strategy was to test if process knowledge was a good predictor of where beryllium contamination could be found. Results revealed that this technique was effective at identifying where surface contamination levels might exceed the RFETS smear control level but that it was not effective in identifying where low concentrations of beryllium might be found

  12. Formation of cellular structure in beryllium at plastic working

    International Nuclear Information System (INIS)

    Papirov, I.I.; Nikolaenko, A.A.; Shokurov, V.S.; Pikalov, A.I.

    2013-01-01

    Conditions of cellular structure formation are investigated at various kinds of deformation and heat treatment of beryllium ingots. It is shown that the cellular structure plays the important role in formation of complex of physical mechanical properties of beryllium. Influence of impurity, various conditions of deformation (temperature, squeezing degree) and heat treatments on substructure, texture and mechanical properties of metal is investigated. Optimum conditions of rolling and heat treatments of beryllium are defined. The way of sign-variable cyclic deformation of beryllium ingots is offered for reception quasi-isotropic fine-grained metal. Physical-mechanical properties of ultra fine-grained metal are studied

  13. The influence of thermal treatment and irradiation on specific resistance of (SnSe)1-x - (PrSe)x solid solutions

    International Nuclear Information System (INIS)

    Huseynov, J.I.; Murguzov, M.I.; Ismayilov, Sh.S.; Jafarov, T.A.

    2014-01-01

    Full text: It was studied some kinetic coefficients in cluding specific resistance of (SnSe) 1 -x - (PrSe) x solid solutions as well. Special interest was caused by composetions of above mentioned system for which the influence of irradiation and thermal treatment following this irradiation was explored. By its electric characteristics praseodymium monoselenide belongs to metals because a metallic link is formed among cation atoms in PrSe, at the expense of cohich praseodymium atoms possess an oxidation degree equalling to 3+

  14. Thermal conductivities for sintered and sphere-pac Li2O and γ-LiAlO2 solid breeders with and without irradiation effects

    International Nuclear Information System (INIS)

    Liu, Y.Y.; Tam, S.W.

    1984-07-01

    Thermal conductivities (k, k/sub eff/) have been estimated for sintered and sphere-pac Li 2 O and γ-LiAlO 2 with and without neutron irradiation effects. The estimation is based on (1) data from unirradiated UO 2 , Li 2 O, and γ-LiAlO 2 ; (2) data from irradiated dielectric insulator materials; and (3) relatively simple physical models. Comparison of model predictions with limited ex- and in-reactor data found reasonable agreement, thus lending credence for their use in design applications. The impact of thermal conductivities on tritium breeding and power generation in fusion solid-breeder blankets is briefly highlighted

  15. Dynamics and structure of self-generated magnetics fields on solids following high contrast, high intensity laser irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Albertazzi, B. [LULI, École Polytechnique, CNRS, CEA, UPMC, 91128 Palaiseau (France); INRS-EMT, 1650 bd L. Boulet, J3X1S2, Varennes, Québec (Canada); Graduate School of Engineering, University of Osaka, Suita, Osaka 565-087 (Japan); Chen, S. N.; Fuchs, J., E-mail: julien.fuchs@polytechnique.fr [LULI, École Polytechnique, CNRS, CEA, UPMC, 91128 Palaiseau (France); Institute of Applied Physics, 46 Ulyanov Street, 603950 Nizhny Novgorod (Russian Federation); Antici, P. [INRS-EMT, 1650 bd L. Boulet, J3X1S2, Varennes, Québec (Canada); Dept. SBAI, Universita di Roma “La Sapienza,” Via A. Scarpa 14, 00161 Rome (Italy); Böker, J.; Swantusch, M.; Willi, O. [Institut für Laser-und Plasmaphysik, Heinrich-Heine-Universität, Düsseldorf (Germany); Borghesi, M. [School of Mathematics and Physics, The Queen' s University, Belfast (United Kingdom); Breil, J.; Feugeas, J. L.; Nicolaï, Ph.; Tikhonchuk, V. T.; D' Humières, E. [CELIA, University of Bordeaux - CNRS - CEA, 33405 Talence (France); Dervieux, V.; Nakatsutsumi, M.; Romagnagni, L. [LULI, École Polytechnique, CNRS, CEA, UPMC, 91128 Palaiseau (France); Lancia, L. [Dept. SBAI, Universita di Roma “La Sapienza,” Via A. Scarpa 14, 00161 Rome (Italy); Shepherd, R. [LLNL, East Av., Livermore, California 94550 (United States); Sentoku, Y. [Department of Physics, University of Nevada, Reno, Nevada 89557-0058 (United States); Starodubtsev, M. [Institute of Applied Physics, 46 Ulyanov Street, 603950 Nizhny Novgorod (Russian Federation); and others

    2015-12-15

    The dynamics of self-generated magnetic B-fields produced following the interaction of a high contrast, high intensity (I > 10{sup 19 }W cm{sup −2}) laser beam with thin (3 μm thick) solid (Al or Au) targets is investigated experimentally and numerically. Two main sources drive the growth of B-fields on the target surfaces. B-fields are first driven by laser-generated hot electron currents that relax over ∼10–20 ps. Over longer timescales, the hydrodynamic expansion of the bulk of the target into vacuum also generates B-field induced by non-collinear gradients of density and temperature. The laser irradiation of the target front side strongly localizes the energy deposition at the target front, in contrast to the target rear side, which is heated by fast electrons over a much larger area. This induces an asymmetry in the hydrodynamic expansion between the front and rear target surfaces, and consequently the associated B-fields are found strongly asymmetric. The sole long-lasting (>30 ps) B-fields are the ones growing on the target front surface, where they remain of extremely high strength (∼8–10 MG). These B-fields have been recently put by us in practical use for focusing laser-accelerated protons [B. Albertazzi et al., Rev. Sci. Instrum. 86, 043502 (2015)]; here we analyze in detail their dynamics and structure.

  16. Pomegranate peels: A novel ago-residue for tannate production by gamma irradiated aspergillus versicolor under solid state fermentation

    International Nuclear Information System (INIS)

    Khalaf, M.A.; Khalaf, S.A.

    2005-01-01

    Pomegranate peels were tested as a substrate for the production of tannate and gallic acid (GA) under solid state fermentation (SSF) using Aspergillus versicolor-g3B (highly potent gamma irradiated tannate producer isolate). The fungal strain was grown on the substrate without any pre-treatment. Different parameters for maximum production of tannate by this strain under SSF method were optimized. The maximum tannate yield (12.45μg-1ds) and GA (94%) were obtained when SSF was carried out at ph 5.0, 30 degree C, 60% initial substrate moisture, 20% inoculum size, 3% tannic acid and 1% ammonium nitrate as additional carbon and nitrogen sources, after 96 h of fermentation. The crude tannate from this isolate showed ph and temperature optima of 5.0 and 50 degree C, respectively. Also, the enzyme was stable in a broad ph range of 3-8 for 24 h and was also heat stable as it retained 65% activity at 70 degree C after 1 hour

  17. Corrosion of beryllium oxide; Corrosion de l'oxyde de beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Elston, J; Caillat, R [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

    1958-07-01

    Data are reported on the volatilization rate of beryllium oxide in moist air depending on temperature and water vapour concentration. They are concerned with powder samples or sintered shapes of various densities. For sintered samples, the volatilization rate is very low under the following conditions: - temperature: 1300 deg. C, - water vapour concentration in moist air: 25 g/m{sup 3}, - flow rate: 12 I/hour corresponding to a speed of 40 m/hour on the surface of the sample. For calcinated powders (1300 deg. C), grain growth has been observed under a stream of moist air at 1100 deg. C. For instance, grain size changes from 0,5 to at least 2 microns after 500 hours of exposure at this temperature. Furthermore, results data are reported on corrosion of sintered beryllium oxide in pressurized water. At 250 deg. C, under a pressure of 40 kg/cm{sup 2} water is very slightly corrosive; however, internal strains are revealed. Finally, some features on the corrosion in liquid sodium are exposed. (author)Fren. [French] La volatilisation de l'oxyde de beryllium dans l'air humide est etudiee en fonction de la temperature pour differentes teneurs de vapeur d'eau. Les essais decrits portent sur de l'oxyde de beryllium en poudre ou sur des echantillons d'oxyde de beryllium fritte de differentes densites. Avec un debit d'air de 12 I/h contenant 25 g de vapeur par m{sup 3} correspondant a une vitesse de 40 m/h sur la surface de l'echantillon, la volatilisation des frittes a 1300 deg. C reste tres faible. Sur de la poudre d'oxyde de beryllium calcinee initialement a 1300 deg. C, on observe un grossissement de la taille des grains sous l'influence de l'air humide a 1100 deg. C. Par exemple, elle passe de 0,5 a au moins 2 microns apres 500 heures d'exposition a cette temperature. On donne d'autre part les resultats d'une etude de la corrosion de frittes d'oxyde de beryllium par l'eau, en autoclave. A 250 deg. C, sous une pression de 40 kg/cm{sup 2}, l'action de l'eau reste tres

  18. Compatibility behavior of beryllium with LiAlO2 and Li2ZrO3 ceramics, with 316L and 1.4914 steels in Sibelius

    International Nuclear Information System (INIS)

    Flament, T.; Roux, N.; Abassin, J.J.; Briec, M.; Cruz, D.; Schuster, I.

    1991-01-01

    The compatibility under irradiation of beryllium with Li 2 O, LiAlO 2 , Li 4 SiO 4 and Li 2 ZrO 3 ceramics and with 316L and 1.4914 steels was investigated in SIBELIUS. The irradiation was performed in the SILOE reactor at 550 deg C for 1690 hours in He + 0.1%H 2 purge pas. Examinations of the LiAlO 2 /Be and Li 2 ZrO 3 /Be couples show a weak oxidation of beryllium and the presence of cavities near the interface with ceramics. Examinations of the 316L/Be and 1.4914/Be couples show the formation of an oxide layer on all beryllium and steel surfaces suggesting that corrosion arises from a species (most likely T 2 O and/or H 2 O) present in the environmental atmosphere. Post-irradiation annealing tests of beryllium indicate that the major part of helium is released during irradiation whereas the major part of tritium is released above 700 deg C

  19. Experimental results of beryllium exposed to intense high energy proton beam pulses

    Energy Technology Data Exchange (ETDEWEB)

    Ammigan, K. [Fermilab; Hartsell, B. [Fermilab; Hurh, P. [Fermilab; Zwaska, R. [Fermilab; Butcher, M. [CERN; Guinchard, M. [CERN; Calviani, M. [CERN; Losito, R. [CERN; Roberts, S. [Culham Lab; Kuksenko, V. [Oxford U.; Atherton, A. [Rutherford; Caretta, O. [Rutherford; Davenne, T. [Rutherford; Densham, C. [Rutherford; Fitton, M. [Rutherford; Loveridge, J. [Rutherford; O' Dell, J. [Rutherford

    2017-02-10

    Beryllium is extensively used in various accelerator beam lines and target facilities as a material for beam windows, and to a lesser extent, as secondary particle production targets. With increasing beam intensities of future accelerator facilities, it is critical to understand the response of beryllium under extreme conditions to reliably operate these components as well as avoid compromising particle production efficiency by limiting beam parameters. As a result, an exploratory experiment at CERN’s HiRadMat facility was carried out to take advantage of the test facility’s tunable high intensity proton beam to probe and investigate the damage mechanisms of several beryllium grades. The test matrix consisted of multiple arrays of thin discs of varying thicknesses as well as cylinders, each exposed to increasing beam intensities. This paper outlines the experimental measurements, as well as findings from Post-Irradiation-Examination (PIE) work where different imaging techniques were used to analyze and compare surface evolution and microstructural response of the test matrix specimens.

  20. Progress in production and characterization of RF beryllium for ITER fist wall

    International Nuclear Information System (INIS)

    Kupriyanov, I.B.; Nikolaev, G.N.; Khomutov, A.M.; Gervash, A.; Romanov, P.V.

    2007-01-01

    Full text of publication follows: Beryllium was chosen as the armor material for the Fist Wall and Port Limiter of ITER. As results of ITER EDA activities the reference beryllium grade S-65C (USA, Brush Wellman) and the DshG-200 grade (RF, Bochvar Institute) were selected as materials for armor of ITER FW. The main criterion of a choice of given grades was their highest resistance against High Heat Flux loading shown by results of thermal fatigue/shock test experiments carried out earlier in SNL (USA) and FZ Juelich (Germany). Recently in RF the new Be grade TGP-56FW has been proposed, which is a modified analogue of DshG-200 grade with improved properties, and also a low-waste manufacturing process for production of Be tiles for armor of ITER FW has been developed. In comparison with DshG-200 grade the main advantage of TGP-56FW grade consists in higher level of strength properties and plasticity as well as higher uniformity of physical-mechanical properties in transverse and longitudinal directions relatively pressing axis. In this paper the results of RF R and D activities in production and characterization of TGP- 56FW beryllium grade for FW armor are presented. The results of HHF tests (thermal fatigue/disruption simulation) on TSEFEY-M testing facility for full-scale beryllium tiles produced from TGP-56FW grade are also reported. A new in-pile integrated test experiment for Be mock-ups that combines thermal cycling (2x10 4 cycles at 0.5 MW/m 2 ) and neutron irradiation (about 0.6 dpa) is discussed.(authors)

  1. Failure analysis of beryllium tile assembles following high heat flux testing for the ITER program

    International Nuclear Information System (INIS)

    Odegard, B.C. Jr.; Cadden, C. H.; Yang, N. Y. C.

    2000-01-01

    The following document describes the processing, testing and post-test analysis of two Be-Cu assemblies that have successfully met the heat load requirements for the first wall and dome sections for the ITER (International Thermonuclear Experimental Reactor) fusion reactor. Several different joint assemblies were evaluated in support of a manufacturing technology investigation aimed at diffusion bonding or brazing a beryllium armor tile to a copper alloy heat sink for fusion reactor applications. Judicious selection of materials and coatings for these assemblies was essential to eliminate or minimize interactions with the highly reactive beryllium armor material. A thin titanium layer was used as a diffusion barrier to isolate the copper heat sink from the beryllium armor. To reduce residual stresses produced by differences in the expansion coefficients between the beryllium and copper, a compliant layer of aluminum or aluminum-beryllium (AlBeMet-150) was used. Aluminum was chosen because it does not chemically react with, and exhibits limited volubility in, beryllium. Two bonding processes were used to produce the assemblies. The primary process was a diffusion bonding technique. In this case, undesirable metallurgical reactions were minimized by keeping the materials in a solid state throughout the fabrication cycle. The other process employed an aluminum-silicon layer as a brazing filler material. In both cases, a hot isostatic press (HIP) furnace was used in conjunction with vacuum-canned assemblies in order to minimize oxidation and provide sufficient pressure on the assemblies for full metal-to-metal contact and subsequent bonding. The two final assemblies were subjected to a suite of tests including: tensile tests and electron and optical metallography. Finally, high heat flux testing was conducted at the electron beam testing system (EBTS) at Sandia National Laboratories, New Mexico. Here, test mockups were fabricated and subjected to normal heat loads to

  2. Ação promotora do berílio em catalisadores da síntese do estireno Promotor action of beryllium in catalysts for styrene production

    Directory of Open Access Journals (Sweden)

    Mário Nilo Mendes Barbosa

    1997-10-01

    Full Text Available The catalytic dehydrogenation of ethylbenzene in presence of steam is the main commercial route to produce styrene. The industrial catalysts are potassium- and chromia-doped hematite which show low surface areas leading to bad performance and short life. In order to develop catalysts with high areas, the effect of beryllium on the textural properties and on the catalytic performance of this iron oxide was studied. The influence of the amount of the dopant, the starting material and the calcination temperature were also studied. In sample preparations, iron and beryllium salts (nitrate or sulfate were hydrolyzed with ammonia and then calcinated. The experiments followed a factorial design with two variables in two levels (Fe/Be= 3 and 7; calcination temperature= 500 and 700ºC. Solids without any dopant were also prepared. Samples were characterized by elemental analysis, infrared spectroscopy, surface area and porosity measurements, X-ray diffraction, DSC and TG. The catalysts were tested in a microreactor at 524ºC and 1 atm, by using a mole ratio of steam/ ethylbenzene=10. The selectivity was measured by monitoring styrene, benzene and toluene formation. It was found that the effect of beryllium on the characteristics of hematite and on its catalytic performance depends on the starting material and on the amount of dopant. Surface areas increased due to the dopant as well as the nature of the precursor; samples produced by beryllium sulfate showed higher areas. Beryllium-doped solids showed a higher catalytic activity when compared to pure hematite, but no significant influence of the anion of starting material was noted. It can be concluded that beryllium acts as both textural and structural promoter. Samples with Fe/Be= 3, heated at 500ºC, lead to the highest conversion and were the most selective. However, catalysts prepared from beryllium sulfate are the most promising to ethylbenzene dehydrogenation due to their high surface area which

  3. Deuterium/hydrogen isotope exchange on beryllium and beryllium nitride; Deuterium/Wasserstoff-Isotopenaustausch an Beryllium und Berylliumnitrid

    Energy Technology Data Exchange (ETDEWEB)

    Dollase, Petra; Eichler, Michael; Koeppen, Martin; Dittmar, Timo; Linsmeier, Christian [Forschungszentrum Juelich GmbH, Institut fuer Energie- und Klimaforschung - Plasmaphysik (Germany)

    2016-07-01

    In the fusion experiments JET and ITER, the first wall is made up of beryllium. The use of nitrogen is discussed for radiative cooling in the divertor. This can react with the surface of the first wall to form beryllium nitride (Be{sub 3}N{sub 2}). The hydrogen isotopes deuterium and tritium, which react in the fusion reaction to helium and a neutron, are used as fuel. Since the magnetic confinement of the plasma is not perfect, deuterium and tritium ions are also found on the beryllium wall and can accumulate there. This should be avoided due to the radioactivity of tritium. Therefore the isotope exchange with deuterium is investigated to regenerate the first wall. We investigate the isotopic exchange of deuterium and protium in order to have not to work with radioactive tritium. The ion bombardment is simulated with an ion source. With voltages up to a maximum of 5 kV, deuterium and protic hydrogen ions are implanted in polycrystalline Be and Be{sub 3}N{sub 2}. The samples are then analyzed in situ using X-ray photoelectron spectroscopy (XPS) and thermal desorption spectroscopy (TDS). Subsequently, samples prepared under the same conditions are characterized ex-situ by means of nuclear reaction analysis (NRA). [German] In den Fusionsexperimenten JET und ITER besteht die erste Wand im Hauptraum aus Beryllium (Be). Zur Strahlungskuehlung im Divertor wird der Einsatz von Stickstoff diskutiert. Dieser kann mit der Oberflaeche der ersten Wand zu Berylliumnitrid (Be{sub 3}N{sub 2}) reagieren. Als Brennstoff werden die Wasserstoffisotope Deuterium und Tritium eingesetzt, die in der Fusionsreaktion zu Helium und einem Neutron reagieren. Da der magnetische Einschluss des Plasmas nicht perfekt ist, treffen auch Deuterium- und Tritiumionen auf die Berylliumwand auf und koennen sich dort anreichern. Das soll aufgrund der Radioaktivitaet von Tritium unbedingt vermieden werden. Daher wird zur Regenerierung der ersten Wand der Isotopenaustausch mit Deuterium untersucht. Wir

  4. Szilard-Chalmers effect in solid H I O{sub 4}. 2 H{sub 2} O by neutron irradiation (source-reactor)

    Energy Technology Data Exchange (ETDEWEB)

    Takriti, S [radiochemistry laboratory, syrian atomic energy commission P.O. Box 6091 Damascus, (Syrian Arab Republic)

    1995-10-01

    The Szilard-Chalmers effect in solid periodic acid was investigated. In order to study the initial distribution of {sup 128I} o{sub 4} as a function of neutron flux, samples were irradiated utilizing both neutron source ({sup 241} Am-Be), the manual vertical irradiation channel and the thermal column of ET-R R-1 research reactor in Egypt. The initial retention reached a maximum of 40% after 120 minutes at 5.5 x 10 {sup 8} n s{sup -1} cm {sup -2}. The data was analysed using first order reaction. As a result, the activation Ko= 2.82 x 10 {sup 11} (S{sup -1}), respectively. Kinetics comparison of the dehydration and irradiation reactions for this solid showed disorder in the crystallographic form. Such disorder may be the result of dehydration or irradiation reactions, where the loss of water molecule will lead to formation of vacancies which, in turn, are responsible for the distribution process. 6 figs., 1 tab.

  5. The impact of transient thermal loads on beryllium as plasma facing material

    Energy Technology Data Exchange (ETDEWEB)

    Spilker, Benjamin Christof

    2017-01-24

    microstructural integrity in the transition region involves the risk of a macroscopic delamination of armour material, which reduces the lifetime of afflicted first wall panels. Overall, it was found that the yield strength and ultimate tensile strength of beryllium represent two key parameters that strongly influence its performance under transient thermal loading. Both quantities decrease as a function of the base temperature. Therefore, a lower base temperature (tested down to room temperature) is favourable for the performance of the beryllium armour tiles in ITER. The generated results indicate that the plastic deformation and the cracking of beryllium do not pose a threat to the operation of ITER, if the heat flux factors of the transient thermal pulses remain at 9 MW m{sup -2} s{sup 0.5} or below. This conclusion was drawn from the fact that the thermally induced damage saturated after 10{sup 5} pulses and did not significantly change for up to 10{sup 7} pulses. However, the performed experiments did not include the effects of plasma exposure and neutron irradiation of beryllium, though these loading conditions will be present in ITER in addition to the evaluated transient thermal loads. Further experiments with sequential and simultaneous plasma/thermal/neutron loading are proposed to investigate the synergistic effects of the different loading types and to evaluate possible shifts of the threshold values that were determined within this work.

  6. The impact of transient thermal loads on beryllium as plasma facing material

    International Nuclear Information System (INIS)

    Spilker, Benjamin Christof

    2017-01-01

    microstructural integrity in the transition region involves the risk of a macroscopic delamination of armour material, which reduces the lifetime of afflicted first wall panels. Overall, it was found that the yield strength and ultimate tensile strength of beryllium represent two key parameters that strongly influence its performance under transient thermal loading. Both quantities decrease as a function of the base temperature. Therefore, a lower base temperature (tested down to room temperature) is favourable for the performance of the beryllium armour tiles in ITER. The generated results indicate that the plastic deformation and the cracking of beryllium do not pose a threat to the operation of ITER, if the heat flux factors of the transient thermal pulses remain at 9 MW m"-"2 s"0"."5 or below. This conclusion was drawn from the fact that the thermally induced damage saturated after 10"5 pulses and did not significantly change for up to 10"7 pulses. However, the performed experiments did not include the effects of plasma exposure and neutron irradiation of beryllium, though these loading conditions will be present in ITER in addition to the evaluated transient thermal loads. Further experiments with sequential and simultaneous plasma/thermal/neutron loading are proposed to investigate the synergistic effects of the different loading types and to evaluate possible shifts of the threshold values that were determined within this work.

  7. Sintering of beryllium oxide; Frittage de l'oxyde de beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Caillat, R; Pointud, R [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

    1955-07-01

    This study had for origin to find a process permitting to manufacture bricks of beryllium oxide of pure nuclear grade, with a density as elevated as possible and with standardized shape. The sintering under load was the technique kept for the manufacture of the bricks. Because of the important toxicity of the beryllium oxide, the general features for the preliminary study of the sintering, have been determined while using alumina. The obtained results will be able to act as general indication for ulterior studies with sintering under load. (M.B.) [French] Cette etude a eu pour origine la recherche d'un procede permettant de fabriquer industriellement des briques d'oxyde de beryllium nucleaireraent pures, de densite aussi elevee que possible et de forme standardisee. Le frittage sous charge fut la technique retenue pour la fabrication des briques. En raison de la grande toxicite de l'oxyde de beryllium, les caracteristiques generales du frittage, pour l'etude preliminaire, ont ete determine en utilisant de l'alumine. Les resultats obtenus pourront servir d'indication generale pour des etudes ulterieurs avec frittage sous charge. (M.B.)

  8. Beryllium-stimulated neopterin as a diagnostic adjunct in chronic beryllium disease.

    Science.gov (United States)

    Maier, Lisa A; Kittle, Lori A; Mroz, Margaret M; Newman, Lee S

    2003-06-01

    The diagnosis of chronic beryllium disease (CBD) relies on the beryllium lymphocyte proliferation test (BeLPT) to demonstrate a Be specific immune response. This test has improved early diagnosis, but cannot discriminate beryllium sensitization (BeS) from CBD. We previously found high neopterin levels in CBD patients' serum and questioned whether Be-stimulated neopterin production by peripheral blood cells in vitro might be useful in the diagnosis of CBD. CBD, BeS, Be exposed workers without disease (Be-exp) normal controls and sarcoidosis subjects were enrolled. Peripheral blood mononuclear cells (PBMN) were cultured in the presence and absence of beryllium sulfate. Neopterin levels were determined from cell supernatants by enzyme linked immunosorbent assay (ELISA). Clinical evaluation of CBD subjects included chest radiography, pulmonary function testing, exercise testing, and the BeLPT. CBD patients produced higher levels of neopterin in both unstimulated and Be-stimulated conditions compared to all other subjects (P workplace screening. Copyright 2003 Wiley-Liss, Inc.

  9. Implanted deuterium retention and release in carbon-coated beryllium

    International Nuclear Information System (INIS)

    Anderl, R.A.; Longhurst, G.R.; Pawelko, R.J.; Oates, M.A.

    1997-01-01

    Deuterium implantation experiments have been conducted on samples of clean and carbon-coated beryllium. These studies entailed preparation and characterization of beryllium samples coated with carbon thicknesses of 100, 500, and 1000 angstrom. Heat treatment of a beryllium sample coated with carbon to a thickness of approximately 100 angstrom revealed that exposure to a temperature of 400 degrees C under high vacuum conditions was sufficient to cause substantial diffusion of beryllium through the carbon layer, resulting in more beryllium than carbon at the surface. Comparable concentrations of carbon and beryllium were observed in the bulk of the coating layer. Higher than expected oxygen levels were observed throughout the coating layer as well. Samples were exposed to deuterium implantation followed by thermal desorption without exposure to air. Differences were observed in deuterium retention and postimplantation release behavior in the carbon-coated samples as compared with bare samples. For comparable implantation conditions (sample temperature of 400 degrees C and an incident deuterium flux of approximately 6 X 10 19 D/m 2 sec), the quantity of deuterium retained in the bare sample was less than that retained in the carbon-coated samples. Further, the release of the deuterium took place at lower temperatures for the bare beryllium surfaces than for carbon-coated beryllium samples. 4 refs., 8 figs., 1 tab

  10. Implanted Deuterium Retention and Release in Carbon-Coated Beryllium

    Science.gov (United States)

    Anderl, R. A.; Longhurst, G. R.; Pawelko, R. J.; Oates, M. A.

    1997-06-01

    Deuterium implantation experiments have been conducted on samples of clean and carbon-coated beryllium. These studies entailed preparation and characterization of beryllium samples coated with carbon thicknesses of 100, 500, and 1000 Å. Heat treatment of a beryllium sample coated with carbon to a thickness of approximately 100 Å revealed that exposure to a temperature of 400°C under high vacuum conditions was sufficient to cause substantial diffusion of beryllium through the carbon layer, resulting in more beryllium than carbon at the surface. Comparable concentrations of carbon and beryllium were observed in the bulk of the coating layer. Higher than expected oxygen levels were observed throughout the coating layer as well. Samples were exposed to deuterium implantation followed by thermal desorption without exposure to air. Differences were observed in deuterium retention and postimplantation release behavior in the carbon-coated samples as compared with bare samples. For comparable implantation conditions (sample temperature of 400°C and an incident deuterium flux of approximately 6 × 1019 D/m2-s), the quantity of deuterium retained in the bare sample was less than that retained in the carbon-coated samples. Further, the release of the deuterium took place at lower temperatures for the bare beryllium surfaces than for carbon-coated beryllium samples.

  11. 10 CFR 850.20 - Baseline beryllium inventory.

    Science.gov (United States)

    2010-01-01

    ... 10 Energy 4 2010-01-01 2010-01-01 false Baseline beryllium inventory. 850.20 Section 850.20 Energy... Baseline beryllium inventory. (a) The responsible employer must develop a baseline inventory of the... inventory, the responsible employer must: (1) Review current and historical records; (2) Interview workers...

  12. Atlas of hot isostatic beryllium powder pressing diagrams

    International Nuclear Information System (INIS)

    Stoev, P.I.; Papirov, I.I.; Tikhinskij, G.F.; Vasil'ev, A.A.

    1995-01-01

    Diagrams of hot isotopic pressing (HIP) of beryllium powder with different grain size in a wide range of pressing parameters are built by mathematical modeling methods. The HIP diagrams presented are divided into 3 groups: parametric dependencies D=f(P,T); technological HIP diagrams; compacting mechanisms. The created data bank permits to optimise beryllium powder HIP with changing parameters. 4 refs., 23 figs

  13. Reactivity effects due to beryllium poisoning of BR2

    International Nuclear Information System (INIS)

    Kalcheva, S.; Ponsard, B.; Koonen, E.

    2004-01-01

    This paper illustrates the impact of the poisoning of the beryllium reflector on reactivity variations of the Belgian MTR BR2 in SCK.CEN. Detailed calculations by MCNP-4C of reactivity effects caused by strong neutron absorbers 3 He and 6 Li during reactor operation history are presented. The importance of beryllium poisoning for the accuracy of reactivity predictions is discussed. (authors)

  14. Progress report of preliminary studies of beryllium toxicity

    Energy Technology Data Exchange (ETDEWEB)

    Hodge, H.C.

    1947-09-01

    This document was prepared in connection with a symposium of beryllium poisoning held at the Saranac Laboratories and describes progress made and a research program aimed at characterizing the toxicity of beryllium. Seven individual papers in this document are separately indexed and cataloged for the database.

  15. Joining of beryllium by braze welding technique: preliminary results

    Energy Technology Data Exchange (ETDEWEB)

    Banaim, P.; Abramov, E. [Ben-Gurion Univ. of the Negev, Beersheba (Israel); Zalkind, S.; Eden, S.

    1998-01-01

    Within the framework of some applications, there is a need to join beryllium parts to each other. Gas Tungsten Arc Braze Welds were made in beryllium using 0.3 mm commercially Aluminum (1100) shim preplaced at the joint. The welds exhibited a tendency to form microcracks in the Fusion Zone and Heat Affected Zone. All the microcracks were backfilled with Aluminum. (author)

  16. Laser welding of a beryllium/tantalum collimator

    International Nuclear Information System (INIS)

    Lingenfelter, A.C.; Anglin, C.D.

    1985-01-01

    This report describes the methods utilized in the fabrication of a collimator from 0.001 inch thick beryllium and tantalum foil. The laser welding process proved to be an acceptable method for joining the beryllium in a standing edge joint configuration

  17. Protection of air in premises and environment against beryllium aerosols

    Energy Technology Data Exchange (ETDEWEB)

    Bitkolov, N.Z.; Vishnevsky, E.P.; Krupkin, A.V. [Research Inst. of Industrial and Marine Medicine, St. Petersburg (Russian Federation)

    1998-01-01

    First and foremost, the danger of beryllium aerosols concerns a possibility of their inhalation. The situation is aggravated with high biological activity of the beryllium in a human lung. The small allowable beryllium aerosols` concentration in air poses a rather complex and expensive problem of the pollution prevention and clearing up of air. The delivery and transportation of beryllium aerosols from sites of their formation are defined by the circuit of ventilation, that forms aerodynamics of air flows in premises, and aerodynamic links between premises. The causes of aerosols release in air of premises from hoods, isolated and hermetically sealed vessels can be vibrations, as well as pulses of temperature and pressure. Furthermore, it is possible the redispersion of aerosols from dirty surfaces. The effective protection of air against beryllium aerosols at industrial plants is provided by a complex of hygienic measures: from individual means of breath protection up to collective means of the prevention of air pollution. (J.P.N.)

  18. Hydrodynamic instabilities in beryllium targets for the National Ignition Facility

    Energy Technology Data Exchange (ETDEWEB)

    Yi, S. A., E-mail: austinyi@lanl.gov; Simakov, A. N.; Wilson, D. C.; Olson, R. E.; Kline, J. L.; Batha, S. H. [Los Alamos National Laboratory, P.O. Box 1663, Los Alamos, New Mexico 87545 (United States); Clark, D. S.; Hammel, B. A.; Milovich, J. L.; Salmonson, J. D.; Kozioziemski, B. J. [Lawrence Livermore National Laboratory, P.O. Box 808, Livermore, California 94551 (United States)

    2014-09-15

    Beryllium ablators offer higher ablation velocity, rate, and pressure than their carbon-based counterparts, with the potential to increase the probability of achieving ignition at the National Ignition Facility (NIF) [E. I. Moses et al., Phys. Plasmas 16, 041006 (2009)]. We present here a detailed hydrodynamic stability analysis of low (NIF Revision 6.1) and high adiabat NIF beryllium target designs. Our targets are optimized to fully utilize the advantages of beryllium in order to suppress the growth of hydrodynamic instabilities. This results in an implosion that resists breakup of the capsule, and simultaneously minimizes the amount of ablator material mixed into the fuel. We quantify the improvement in stability of beryllium targets relative to plastic ones, and show that a low adiabat beryllium capsule can be at least as stable at the ablation front as a high adiabat plastic target.

  19. Preparation and characterization of beryllium doped organic plasma polymer coatings

    International Nuclear Information System (INIS)

    Brusasco, R.; Letts, S.; Miller, P.; Saculla, M.; Cook, R.

    1995-01-01

    We report the formation of beryllium doped plasma polymerized coatings derived from a helical resonator deposition apparatus, using diethylberyllium as the organometaric source. These coatings had an appearance not unlike plain plasma polymer and were relatively stable to ambient exposure. The coatings were characterized by Inductively Coupled Plasma Mass Spectrometry and X-Ray Photoelectron Spectroscopy. Coating rates approaching 0.7 μm hr -1 were obtained with a beryllium-to-carbon ratio of 1:1.3. There is also a significant oxygen presence in the coating as well which is attributed to oxidation upon exposure of the coating to air. The XPS data show only one peak for beryllium with the preponderance of the XPS data suggesting that the beryllium exists as BeO. Diethylberyllium was found to be inadequate as a source for beryllium doped plasma polymer, due to thermal decomposition and low vapor recovery rates

  20. Reaction-diffusion modeling of hydrogen in beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Wensing, Mirko; Matveev, Dmitry; Linsmeier, Christian [Forschungszentrum Juelich GmbH, Institut fuer Energie- und Klimaforschung - Plasmaphysik (Germany)

    2016-07-01

    Beryllium will be used as first-wall material for the future fusion reactor ITER as well as in the breeding blanket of DEMO. In both cases it is important to understand the mechanisms of hydrogen retention in beryllium. In earlier experiments with beryllium low-energy binding states of hydrogen were observed by thermal desorption spectroscopy (TDS) which are not yet well understood. Two candidates for these states are considered: beryllium-hydride phases within the bulk and surface effects. The retention of deuterium in beryllium is studied by a reaction rate approach using a coupled reaction diffusion system (CRDS)-model relying on ab initio data from density functional theory calculations (DFT). In this contribution we try to assess the influence of surface recombination.

  1. Fracture toughness of neutron irradiated solid and powder HIP 316L(N). ITER Task 214, NET deliverable GB6 ECN-5

    International Nuclear Information System (INIS)

    Rensman, J.; Van den Broek, F.P.; Jong, M.; Van Osch, E.V.

    1998-04-01

    The fracture toughness properties of unirradiated and neutron irradiated type 316L(N) stainless steel plate (European Reference Heat ERHII), conventional 316L(N) solid HIP joints (heat PM-130), and 316L(N)-1G powder HIP material have been measured. Compact tension specimens with a thickness of 12 and 5 mm were irradiated in the High Flux Reactor (HFR) in Petten, The Netherlands, simulating the fusion reactor's first wall conditions by a combination of high displacement damage with proportional amounts of helium. The solid HIP (or HIP-bonded) CT-specimens were irradiated in two separate experiments: SIWAS-6 with 1.3 to 2.3 dpa (1.7 dpa av.) at 353 K, and CHARIOT-3 with 2.7 to 3.1 dpa (2.9 dpa av.) at 600 K. The plate material and powder HIP CT-specimens were irradiated in one experiment only, SIWAS-6. The helium content is up to 20 appm for the 2.9 dpa (av.) dose level. Testing temperatures of 353K and 573K have been used for the fracture toughness experiments. The report contains the experimental conditions and summarises the results, which are given in terms of J-resistance curve fits. The main conclusions are that all three materials have very high toughness in the unirradiated state with little difference between them; the solid HIP has the highest toughness, the powder HIP lowest. The toughness of all three materials is reduced significantly by irradiation, the reduction is the least for the plate material and the highest for the powder HIP material. However, many, but not all, of the solid HIP CT specimens showed debonding of the joint during testing. The machined notch of the CT specimens was not exactly on the joint interface, which could lead to unjustified interpretation of the measured values as being the toughness of the joint, the toughness of the joint being probably much lower. The reduction by irradiation of the fracture toughness of the powder HIP material is clearly larger than for plate material, which is confirmed by the observed early initiation

  2. ZIRCONIUM-TITANIUM-BERYLLIUM BRAZING ALLOY

    Science.gov (United States)

    Gilliland, R.G.; Patriarca, P.; Slaughter, G.M.; Williams, L.C.

    1962-06-12

    A new and improved ternary alloy is described which is of particular utility in braze-bonding parts made of a refractory metal selected from Group IV, V, and VI of the periodic table and alloys containing said metal as a predominating alloying ingredient. The brazing alloy contains, by weight, 40 to 50 per cent zirconium, 40 to 50 per cent titanium, and the balance beryllium in amounts ranging from 1 to 20 per cent, said alloy having a melting point in the range 950 to 1400 deg C. (AEC)

  3. Moessbauer study of iron diffusion in beryllium

    International Nuclear Information System (INIS)

    Sepiol, B.; Ruebenbauer, K.; Miczko, B.; Birchall, T.

    1991-01-01

    The broadening of the 14.41 keV Moessbauer line of 57 Fe dure to diffusion of iron atoms in polycrystalline beryllium has been investigated in the temperature range 1123 to 1423 K. The observed broadenings obey the Arrhenius law with activation energy 1.66(10) eV, i.e., lower than that obtained from the corresponding polycrystalline tracer data. The variations of the resonant fraction, second order Doppler shift and quadrupole splitting versus temperature are reported. An average diffusion coefficient has been calculated from the obtained broadenings and compared with the tracer results. (orig.)

  4. Investigations of the ternary system beryllium-carbon-tungsten and analyses of beryllium on carbon surfaces

    International Nuclear Information System (INIS)

    Kost, Florian

    2009-01-01

    Beryllium, carbon and tungsten are planned to be used as first wall materials in the future fusion reactor ITER. The aim of this work is a characterization of mixed material formation induced by thermal load. To this end, model systems (layers) were prepared and investigated, which give insight into the basic physical and chemical concepts. Before investigating ternary systems, the first step was to analyze the binary systems Be/C and Be/W (bottom-up approach), where the differences between the substrates PG (pyrolytic graphite) and HOPG (highly oriented pyrolytic graphite) were of special interest. Particularly X-ray photoelectron spectroscopy (XPS), low energy ion scattering (ISS) and Rutherford backscattering spectroscopy (RBS) were used as analysis methods. Beryllium evaporated on carbon shows an island growth mode, whereas a closed layer can be assumed for layer thicknesses above 0.7 nm. Annealing of the Be/C system induces Be 2 C island formation for T≥770 K. At high temperatures (T≥1170 K), beryllium carbide dissociates, resulting in (metallic) beryllium desorption. For HOPG, carbide formation starts at higher temperatures compared to PG. Activation energies for the diffusion processes were determined by analyzing the decreasing beryllium amount versus annealing time. Surface morphologies were characterized using angle-resolved XPS (ARXPS) and atomic force microscopy (AFM). Experiments were performed to study processes in the Be/W system in the temperature range from 570 to 1270 K. Be 2 W formation starts at 670 K, a complete loss of Be 2 W is observed at 1170 K due to dissociation (and subsequent beryllium desorption). Regarding ternary systems, particularly Be/C/W and C/Be/W were investigated, attaching importance to layer thickness (reservoir) variations. At room temperature, Be 2 C, W 2 C, WC and Be 2 W formation at the respective interfaces was observed. Further Be 2 C is forming with increasing annealing temperatures. Depending on the layer

  5. Microstructure Analysis on Beryllium Reflector Blocks of Research Reactors

    Energy Technology Data Exchange (ETDEWEB)

    Kang, Suk Hoon; Jang, Jin Sung; Jeong, Yong Hwan; Han, Chang Hee; Jung, Yang Il; Kim, Tae Kyu [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of); Choi, Yong Seok; Oh, Kyu Hwan [Seoul National University, Seoul (Korea, Republic of)

    2012-05-15

    A pure beryllium has a very low mass absorption coefficient: it has been used as the reflector element material in research reactors. The lifetime of beryllium reflector elements usually determined by the swelling: the swelling leads to dimensional change in the reflector frame, which results in bending or cracking of the parts. The mechanical interference in between parts should be avoided; the anisotropy of beryllium also needs to be considered. A beryllium has hexagonal close-pack (HCP) crystal structure, which is inherently anisotropic. It has virtually no ductility in one direction. There are two main aspects in the manufacturing of beryllium which will affect its isotropy, and those are the powder morphology and the consolidation process. Powder metallurgy permits the material to be produced in isotropic and fine-grained form, which overcomes the crystal structure problem by distributing loads in low ductility oriented grains to high ductility oriented grains. There are three representative consolidating methods to make beryllium reflector blocks. Traditionally, most powder-derived grades of beryllium have been consolidated by vacuum hot-pressing (VHP). A column of loose beryllium powder is compacted under vacuum by the pressure of the opposed upper and lower punches, bringing the billet to final density. The VHP process is directional in nature: it contributes to the anisotropy of the material properties. Another consolidating method for beryllium powder is hot isostatic pressing (HIPing), which will enhance its isotropy. During HIPing, The argon gas exerts pressure uniformly in all directions on the can containing the beryllium powder. The HIP process is effective to improve the isotropy of the resulting material as well as refinement of grain sizes. The last consolidating method is hot extrusion (HE). A roughly close packed beryllium is subjected to severe plastic defomation, the grains are refined and the tensile strength is enhanced. Since the material

  6. Copper-beryllium alloys for technical applications

    International Nuclear Information System (INIS)

    Heller, W.

    1976-01-01

    Data of physical properties are compiled for the most commonly used copper-beryllium alloys (CuBe 2, CuBe 1.7, CuCoBe, and CuCoAgBe), with emphasis on their temperature dependence and their variation with particular annealing and hardening treatments. The purpose is to provide a reference source and to indicate the versatility of these materials with respect to other copper alloys and to pure copper. The special features of CuBe alloys include high mechanical strength with reasonably high electrical conductivity, as well as good wear and corrosion resistance. For example, CuBe 2 has a yield strength of up to 1200 N/mm 2 , about three times that of pure copper, whilst the electrical conductivity of CuCoBe can be as high as 28 MS/m, nearly half that of pure copper. Typical applications are springs and electrical contacts. The importance of a proper heat treatment is discussed in some detail, notably the metallurgy and effects of low-temperature annealing (precipitation-hardening). A chapter on manufacturing processes covers machining, brazing, welding, and cleaning. This is followed by some remarks on safety precautions against beryllium poisoning. CuBe alloys are commercially available in the form of wires, strips, rods, and bars. Typical dimensions, specifications, a brief cost estimate, and addresses of suppliers are listed. (Author)

  7. Development of all-beryllium riveted structures

    International Nuclear Information System (INIS)

    Floyd, D.R.; Leslie, W.W.; Miley, D.V.; Nokes, R.W.

    1976-01-01

    Results are presented of a development program aimed at making a full-scale, all-beryllium frustrum by riveted assembly methods. Included are descriptions of the sheet-metal fabrication practices and assembly plans. Results of extensive mechanical testing of both ingot- and powder-source beryllium products that are presented include tensile, notch-tensile, bearing, and shear tests. Although the full-size structure has not been built, examples are given of several conical and cylindrical structures that were made. The largest of these is a 20-in. diameter, 15-in. long cylinder that was roll-formed from one 0.050-in. thick ingot sheet and assembled with 60 countersunk rivets. Tensile testing of riveted flat coupons is also reported as is bulge testing of riveted cylindrical shells. A cost comparison of riveted deep-drawn and powder-source cylinders is made. Results show that when strength and dimensional tolerance requirements are not severe, a riveted assembly approach is warranted. 33 figures, 8 tables

  8. Charge-density study of crystalline beryllium

    Energy Technology Data Exchange (ETDEWEB)

    Stewart, R F [Carnegie-Mellon Univ., Pittsburgh, Pa. (USA). Dept. of Chemistry

    1977-01-01

    The X-ray structure factors for crystalline beryllium measured by Brown (Phil. Mag. (1972), 26, 1377) have been analyzed with multipole deformation functions for charge-density information. Single exponential radial functions were used for the valence charge density. A valence monopole plus the three harmonics, P/sup 3//sub 5/(cos theta) sin 3phi, P/sub 6/(cos theta) and P/sup 3//sub 7/(cos theta) sin 3phi, provide a least-squares fit to the data with Rsub(w)=0.0081. The superposition of these density functions describes a bonding charge density between Be atoms along the c axis through the tetrahedral vacancy. The results reported here are in qualitative agreement with a recent pseudo-potential calculation of metallic beryllium. The final residuals in the analysis are largest at high sin theta/lambda values. This suggests that core charge deformation is present and/or anharmonic motion of the nuclei is appreciable.

  9. Beryllium(II), manganese(II) and uranyl(VI)-salicylamide complexes

    Energy Technology Data Exchange (ETDEWEB)

    Maurya, P L; Agarwala, B V; Dey, A K [Allahabad Univ. (India)

    1977-01-01

    The preparation, composition, general properties and i.r. absorption spectra of the solid chelates formed by salicylamide with beryllium(II), manganese(II) and uranyl(VI) are described. The complexes have been synthesized by refluxing a mixture of ethanolic solutions of the reactants (metal:ligand :: 1:2) for several hours in the presence of alkali. Attempts to isolate the complexes by the interaction of ethanolic solutions of the metal salts and the ligand in the absence of alkali did not succeed.

  10. Control of molten salt corrosion of reduced activation steel for fusion applications by metallic beryllium

    International Nuclear Information System (INIS)

    Calderoni, P.; Sharpe, P.; Nishimura, H.; Terai, T.

    2007-01-01

    Full text of publication follows: In 2001 the INL started a research program as a part of the 2. Japan/US Program on Irradiation Tests for Fusion Energy Research (JUPITER-II collaboration) aimed at the characterization of the 2LiF-BeF2 (Flibe) molten salt as a breeder and coolant material for fusion applications. A key objective of the work was to demonstrate chemical compatibility between Flibe and potential fusion structural materials once suitable fluoride potential control methods are established. A series of tests performed at INL demonstrated that this can be achieved by contacting the salt with metallic beryllium, and the results have been published in recent years. A further step was to expose two specimens of low activation ferritic/martensitic steel 9Cr-2W JLF-1 to static corrosion tests that include an active corrosion agent (hydrofluoric gas) and fluoride potential control (metallic Be) at 530 C, and the results of the tests are presented in this paper. The specimen and a beryllium rod were simultaneously immersed in the molten salt through gas tight fittings mounted on risers extending from the top lid of the test vessel; the beryllium rod was extracted after 5 hours, while the sample was left in the salt for 250 hours during which salt samples were withdrawn from the melt at fixed intervals. A diagnostic system based on the measurement of reacting HF through on-line titration was coupled with the analysis of metallic components in the salt samples that were dissolved and analyzed using inductively coupled plasma atomic emission spectroscopy (ICP-AES). Impurity levels of oxygen, nitrogen and carbon were determined from pieces of the solidified melt using Leco analytical systems. The results confirmed the expected correlation of the HF recovery with the concentration of metallic elements dissolved in the salt because of specimen corrosion. The metals concentration falls below the detectable limit when the beryllium rod is inserted and increases when the

  11. Beryllium-copper reactivity in an ITER joining environment

    International Nuclear Information System (INIS)

    Odegard, B.C.; Cadden, C.H.; Yang, N.Y.C.

    1998-01-01

    Beryllium-copper reactivity was studied using test parameters being considered for use in the ITER reactor. In this application, beryllium-copper tiles are produced using a low-temperature copper-copper diffusion bonding technique. Beryllium is joined to copper by first plating the beryllium with copper followed by diffusion bonding the electrodeposited (ED) copper to a wrought copper alloy (CuNiBe) at 450 C, 1-3 h using a hot isostatic press (HIP). In this bonded assembly, beryllium is the armor material and the CuNiBe alloy is the heat sink material. Interface temperatures in service are not expected to exceed 350 C. For this study, an ED copper-beryllium interface was subjected to diffusion bonding temperatures and times to study the reaction products. Beryllium-copper assemblies were subjected to 350, 450 and 550 C for times up to 200 h. Both BeCu and Be 2 Cu intermetallic phases were detected using scanning electron microscopy and quantitative microprobe analysis. Growth rates were determined experimentally for each phase and activation energies for formation were calculated. The activation energies were 66 mol and 62 kJ mol -1 for the BeCu and Be 2 Cu, respectively. Tensile bars were produced from assemblies consisting of coated beryllium (both sides) sandwiched between two blocks of Hycon-3. Tensile tests were conducted to evaluate the influence of these intermetallics on the bond strength. Failure occurred at the beryllium-copper interface at fracture strengths greater than 300 MPa for the room-temperature tests. (orig.)

  12. Primary and aggregate color centers in proton irradiated LiF crystals and thin films for luminescent solid state detectors

    International Nuclear Information System (INIS)

    Piccinini, M; Ambrosini, F; Ampollini, A; Bonfigli, F; Libera, S; Picardi, L; Ronsivalle, C; Vincenti, M A; Montereali, R M

    2015-01-01

    Proton beams of 3 MeV energy, produced by the injector of a linear accelerator for proton therapy, were used to irradiate at room temperature lithium fluoride crystals and polycrystalline thin films grown by thermal evaporation. The irradiation fluence range was 10 11 -10 15 protons/cm 2 . The proton irradiation induced the stable formation of primary and aggregate color centers. Their formation was investigated by optical absorption and photoluminescence spectroscopy. The F 2 and F 3 + photoluminescence intensities, carefully measured in LiF crystals and thin films, show linear behaviours up to different maximum values of the irradiation fluence, after which a quenching is observed, depending on the nature of the samples (crystals and films). The Principal Component Analysis, applied to the absorption spectra of colored crystals, allowed to clearly identify the formation of more complex aggregate defects in samples irradiated at highest fluences. (paper)

  13. Primary and aggregate color centers in proton irradiated LiF crystals and thin films for luminescent solid state detectors

    Science.gov (United States)

    Piccinini, M.; Ambrosini, F.; Ampollini, A.; Bonfigli, F.; Libera, S.; Picardi, L.; Ronsivalle, C.; Vincenti, M. A.; Montereali, R. M.

    2015-04-01

    Proton beams of 3 MeV energy, produced by the injector of a linear accelerator for proton therapy, were used to irradiate at room temperature lithium fluoride crystals and polycrystalline thin films grown by thermal evaporation. The irradiation fluence range was 1011-1015 protons/cm2. The proton irradiation induced the stable formation of primary and aggregate color centers. Their formation was investigated by optical absorption and photoluminescence spectroscopy. The F2 and F3+ photoluminescence intensities, carefully measured in LiF crystals and thin films, show linear behaviours up to different maximum values of the irradiation fluence, after which a quenching is observed, depending on the nature of the samples (crystals and films). The Principal Component Analysis, applied to the absorption spectra of colored crystals, allowed to clearly identify the formation of more complex aggregate defects in samples irradiated at highest fluences.

  14. Fiber optical dose rate measurement based on the luminescence of beryllium oxide

    Directory of Open Access Journals (Sweden)

    Teichmann Tobias

    2018-01-01

    Full Text Available This work presents a fiber optical dose rate measurement system based on the radioluminescence and optically stimulated luminescence of beryllium oxide. The system consists of a small, radiation sensitive probe which is coupled to a light detection unit with a long and flexible light guide. Exposing the beryllium oxide probe to ionizing radiation results in the emission of light with an intensity which is proportional to the dose rate. Additionally, optically stimulated luminescence can be used to obtain dose and dose rate information during irradiation or retrospectively. The system is capable of real time dose rate measurements in fields of high dose rates and dose rate gradients and in complex, narrow geometries. This enables the application for radiation protection measurements as well as for quality control in radiotherapy. One inherent drawback of fiber optical dosimetry systems is the generation of Cherenkov radiation and luminescence in the light guide itself when it is exposed to ionizing radiation. This so called “stem” effect leads to an additional signal which introduces a deviation in the dose rate measurement and reduces the spatial resolution of the system, hence it has to be removed. The current system uses temporal discrimination of the effect for radioluminescence measurements in pulsed radiation fields and modulated optically stimulated luminescence for continuous irradiation conditions. This work gives an overview of the major results and discusses new-found obstacles of the applied methods of stem discrimination.

  15. Historical perspectives on the uses and health risks of beryllium

    International Nuclear Information System (INIS)

    Preuss, O.P.

    1985-01-01

    Unawareness of the health risks of beryllium resulted in a decade of unmitigated exposure of several thousand workers and numerous cases of beryllium disease in employees and nearby residents. Subsequent adoption of exposure limits and their implementation with effective technical controls reduced the occurrence of new cases, which were mainly due to accidental exposures, to a minimum. The fact that continuously growing production and consumption did not alter this trend demonstrates the effectiveness of the present threshold limit value. It shows that the potential health hazard can be well contained and that beryllium can be produced and fabricated without undue risk to employees or the general public

  16. Analysis of surface contaminants on beryllium and aluminum windows

    International Nuclear Information System (INIS)

    Gmur, N.F.

    1987-06-01

    An effort has been made to document the types of contamination which form on beryllium window surfaces due to interaction with a synchrotron radiation beam. Beryllium windows contaminated in a variety of ways (exposure to water and air) exhibited surface powders, gels, crystals and liquid droplets. These contaminants were analyzed by electron diffraction, electron energy loss spectroscopy, energy dispersive x-ray spectroscopy and wet chemical methods. Materials found on window surfaces include beryllium oxide, amorphous carbon, cuprous oxide, metallic copper and nitric acid. Aluminum window surface contaminants were also examined

  17. About kinetics of paramagnetic radiation malformations in beryllium ceramics

    International Nuclear Information System (INIS)

    Polyakov, A.I.; Ryabinkin, Yu.A.; Zashkvara, O.V.; Bitenbaev, M.I.; Petukhov, Yu.V.

    1999-01-01

    This paper [1] specifies that γ-radiation of the beryllium-oxide-based ceramics results in development of paramagnetic radiation malformations emerging the ESR spectrum in form of doublet with the splitting rate of oestrasid Δ∼1.6 and g-factor of 2.008. This report presents evaluation outcomes of dependence of paramagnetic radiation malformations concentration in beryllium ceramics on gamma-radiation dose ( 60 Co) within the range of 0-100 Mrad. Total paramagnetic parameters of beryllium ceramics in the range 0-100 Mrad of gamma-radiation dose varied slightly, and were specified by the first type of paramagnetic radiation malformations

  18. Evaluation of the hazard associated with fabricating beryllium copper alloys

    International Nuclear Information System (INIS)

    Senn, T.J.

    1977-01-01

    Beryllium-copper alloys should be considered toxic materials and proper controls must be used when they are machined, heated, or otherwise fabricated. Air samples should be taken for each type of fabrication to determine the worker's exposure and the effectiveness of the controls in use. It has been shown that aerosols containing beryllium are generated during the four methods of fabrication tested, and that these aerosols can be reduced through local exhaust to undetectable levels. Considering the acute, chronic and possibly carcinogenic effects of exposure to beryllium, effective controls should be required because they are feasible both technologically and economically. The health hazards and control measures are reviewed

  19. Effect of molecular weight on radiation chemical degradation yield of chain scission of γ-irradiated chitosan in solid state and in aqueous solution

    International Nuclear Information System (INIS)

    Tahtat, Djamel; Mahlous, Mohamed; Benamer, Samah; Nacer Khodja, Assia; Larbi Youcef, Souad

    2012-01-01

    Chitosan A 1 , A 2 and A 3 with molecular weight of 471, 207 and 100 kDa respectively, produced from squid pen chitin was degraded by gamma rays in the solid state and in aqueous solution with various doses in air at ambient temperature. Effect of molecular weight on radiation chemical degradation yield of chain scission and degradation rate constants of γ-irradiated chitosan in solid state and in aqueous solution was investigated. The radiation chemical degradation yield G (s) and degradation rate values were calculated. The molecular weight changes were monitored by capillary viscometry method and the chemical structure changes were followed by UV analysis. The results showed that, the degradation of chitosan was faster in solution, than in solid state. The values of G (s) in solid state and in aqueous solution were respectively 1.1×10 −8 mol/J and 0.074×10 −7 mol/J for A 1 , 4.42×10 −8 mol/J and 0.28×10 −7 mol/J for A 2 and 6.08×10 −8 mol/J and 0.38×10 −7 mol/J for A 3 . Degradation rate constants values ranged from 0.41×10 −5 to 2.1×10 −5 kGy −1 in solid state, whereas in solution they ranged from 13×10 −5 to 68×10 −5 kGy −1 . The chitosan A 3 was more sensitive to radiolysis than A 1 and A 2 . The chain scission yield, G (s) and degradation rate constants seems to be greatly influenced by the initial molecular weight of the chitosan. Structural changes in irradiated chitosan are revealed by the apparition of absorption peaks at 261 and 295 nm, which could be attributed to the formation of carbonyl groups. In both conditions the peak intensity was higher in chitosan A 3 than in A 1 and A 2 , the oxidative products decreased with increasing molecular weight of chitosan. - Highlights: ► We investigated the effects of MW on G (s) value of γ-irradiated chitosan in solid and aqueous state. ► Chitosan with low molecular weight was more sensitive to radiolysis than high molecular weight. ► G (s) value and degradation rate

  20. Preparation of a sinterable beryllium oxide through decomposition of beryllium hydroxide (1963)

    International Nuclear Information System (INIS)

    Bernier, M.

    1963-01-01

    In the course of the present study, we have attempted to precise the factors which among the ones effective in the course of the preparation of the beryllium hydroxide and oxide and during the sintering have an influence on the final result: the density and homogeneity of the sintered body. Of the several varieties of hydroxides precipitated from a sulfate solution the β-hydroxide only is always contaminated with beryllium sulfate and cannot be purified even by thorough washing. We noticed that those varieties of the hydroxide (gel, α, β) have different decomposition rates; this behaviour is used to identify and even to dose the different species in (α, β) mixtures. The various hydroxides transmit to the resulting oxides the shape they had when precipitated. Accordingly the history of the oxide is revealed by its behaviour during its fabrication and sintering. By comparing the results of the sintering operation with the various measurements performed on the oxide powders we are led to the conclusion that an oxide obtained from beryllium hydroxide is sinterable under vacuum if the following conditions are fulfilled: the particle size must lie between 0.1 and 0.2 μ and the BeSO 4 content of the powder must be less than 0.25 per cent wt (expressed as SO 3 /BeO). The best fitting is obtained with the oxide issued from an α-hydroxide precipitated as very small aggregates and with a low sulfur-content. We have observed that this is also the case for the oxide obtained by direct calcination of beryllium sulfate. (author) [fr

  1. Novel plasma source for safe beryllium spectral line studies in the presence of beryllium dust

    Science.gov (United States)

    Stankov, B. D.; Vinić, M.; Gavrilović Božović, M. R.; Ivković, M.

    2018-05-01

    Plasma source for beryllium spectral line studies in the presence of beryllium dust particles was realised. The guideline during construction was to prevent exposure to formed dust, considering the toxicity of beryllium. Plasma source characterization through determination of optimal working conditions is described. The necessary conditions for Be spectral line appearance and optimal conditions for line shape measurements are found. It is proven experimentally that under these conditions dust appears coincidently with the second current maximum. The electron density measured after discharge current maximum is determined from the peak separation of the hydrogen Balmer beta spectral line, and the electron temperature is determined from the ratios of the relative intensities of Be spectral lines emitted from successive ionized stages of atoms. Maximum values of electron density and temperature are measured to be 9.3 × 1022 m-3 and 16 800 K, respectively. Construction details and testing of the BeO discharge tube in comparison with SiO2 and Al2O3 discharge tubes are also presented in this paper.

  2. Effect of neutron irradiation on etching, optical and structural properties of microscopic glass slide used as a solid state nuclear track detector

    International Nuclear Information System (INIS)

    Singh, Surinder; Kaur Sandhu, Amanpreet; Prasher, Sangeeta; Prakash Pandey, Om

    2007-01-01

    Microscopic glass slides are soda-lime glasses which are readily available and are easy to manufacture with low production cost. The application of these glasses as nuclear track detector will help us to make use of these glasses as solid-state nuclear track detector. The present paper describes the variation in the etching, optical and structural properties of the soda-lime microscopic glass slides due to neutron irradiation of different fluences. The color transformation and an increase in the optical absorption with neutron irradiation are observed. Both the bulk and track etch rates are found to increase with neutron fluence, thus showing a similar dependence on neutron fluence, but the sensitivity remains almost constant

  3. Synthesis and characterization of CdSe/ZnS core-shell quantum dots immobilized on solid substrates through laser irradiation

    International Nuclear Information System (INIS)

    Gyoergy, E.; Perez del Pino, A.; Roqueta, J.; Ballesteros, B.; Miguel, A.S.; Maycock, C.; Oliva, A.G.

    2012-01-01

    CdSe/ZnS core-shell quantum dots (QDs) have been immobilized onto solid substrates by matrix assisted pulsed laser evaporation (MAPLE). An UV KrF* (λ = 248 nm, τ FWHM ≅ 25 ns) excimer laser source was used for irradiations of the composite MAPLE targets. The targets were prepared by the dispersion of the CdSe/ZnS QDs in a solvent with high absorption at the incident laser radiation. The dependence of the surface morphology, crystalline structure, chemical composition, and functional properties of the laser transferred CdSe/ZnS QDs on the processing conditions as incident laser fluence value and ambient atmosphere inside the irradiation chamber was investigated. The possible physical mechanisms implied in the laser ablation process were identified. (Copyright copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  4. Synthesis and characterization of CdSe/ZnS core-shell quantum dots immobilized on solid substrates through laser irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Gyoergy, E. [Centre d' Investigacions en Nanociencia i Nanotecnologia, Institut Catala de Nanotecnologia, Consejo Superior de Investigaciones Cientificas (CIN2, ICN-CSIC), Bellaterra (Spain); National Institute for Lasers, Plasma and Radiation Physics, Bucharest (Romania); Perez del Pino, A. [Instituto de Ciencia de Materiales de Barcelona, Consejo Superior de Investigaciones Cientificas (ICMAB, CSIC), Bellaterra (Spain); Roqueta, J.; Ballesteros, B. [Centre d' Investigacions en Nanociencia i Nanotecnologia, Institut Catala de Nanotecnologia, Consejo Superior de Investigaciones Cientificas (CIN2, ICN-CSIC), Bellaterra (Spain); Miguel, A.S.; Maycock, C.; Oliva, A.G. [Instituto de Tecnologia Quimica e Biologica, Universidade Nova de Lisboa (ITQB-UNL), Oeiras (Portugal)

    2012-11-15

    CdSe/ZnS core-shell quantum dots (QDs) have been immobilized onto solid substrates by matrix assisted pulsed laser evaporation (MAPLE). An UV KrF* ({lambda} = 248 nm, {tau}{sub FWHM} {approx_equal} 25 ns) excimer laser source was used for irradiations of the composite MAPLE targets. The targets were prepared by the dispersion of the CdSe/ZnS QDs in a solvent with high absorption at the incident laser radiation. The dependence of the surface morphology, crystalline structure, chemical composition, and functional properties of the laser transferred CdSe/ZnS QDs on the processing conditions as incident laser fluence value and ambient atmosphere inside the irradiation chamber was investigated. The possible physical mechanisms implied in the laser ablation process were identified. (Copyright copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  5. optimization of process parameters for lovastatin production under solid-state fermentation from ground corn cobs by gamma irradiated aspergillus tamarri isolate

    International Nuclear Information System (INIS)

    Mattar, Z.A.; Khalaf, M.A.; Meleigy, S.A.

    2010-01-01

    rapid screening method is demonstrated for isolating lovastatin overproducing strains of gamma irradiated aspergillus tamarri. the screening methodology, based on the activity of lovastatin against the yeast candida albicans. among 24 gamma irradiated isolates of a. tamarri, the isolate G-8 was selected as best producer for lovastatin. solid state fermentation (SSF)was evaluated to produce lovastatin by a. tamarri G-8 isolate using ground corn cobs as substrate. monofactorial experiments were adopted to optimize the fermentation conditions. various crucial parameters such as particle size, moisture content, ph, temperature, inoculum size and incubation time were derived. corn cobs of particle size 0.4 mm having moisture level of 60 % and ph 5 gave the highest yield of lovastatin (12.4 mg/gram dry substrate) when inoculated with a. tamarri G-8 at inoculum size 10 % and 28 degree C for 8 days.

  6. Report on antimony-beryllium neutron sources examined after 7.45 effective full power years in the Dodewaard BWR

    International Nuclear Information System (INIS)

    Engen, W.R. van; Ainsworth, A.

    1984-01-01

    A source of neutrons is required to check instrumentation in the Dodewaard BWR after each shut-down. The longest shut-down is the annual refuelling shut-down when the reactor is routinely out for several weeks. Thus the isotopic neutron source needs to have a radioactive half-life which is sufficiently longer than several weeks. An appropriate source is antimony-124/ beryllium which has a half-life of 60.9 days. In this source 1.7 MeV gamma rays emitted by antimony-124 bombard the beryllium target material and produce neutrons. A report on the sources falls under the headings: design considerations (active insert; encapsulation (general considerations; chemical considerations; single or double encapsulation; radium-226 emanating source)); source production; post irradiation examination results (visual examination; eddy current tests); conclusions. (U.K.)

  7. Real-time monitoring of airborne beryllium, at OSHA limit levels, by time-resolved laser-induced breakdown spectroscopy

    International Nuclear Information System (INIS)

    Radziemski, L.J.; Loree, T.R.; Cremers, D.A.

    1982-01-01

    Real-time detection of beryllium particulate is being investigated by the new technique of laser-induced breakdown spectroscopy. For beryllium detection we monitor the 313.1-nm feature of once ionized beryllium (Be II). Numerous publications describe the technique, our beryllium results, and other applications. Here we summarize the important points and describe our experiments with beryllium

  8. Status of the solid breeder materials database

    International Nuclear Information System (INIS)

    Billone, M.C.; Dienst, W.; Lorenzetto, P.; Noda, K.; Roux, N.

    1995-01-01

    The databases for solid breeder ceramics (Li 2 O, Li 4 SiO 4 , Li 2 ZrO 3 , and LiAlO 2 ) and beryllium multiplier material were critically reviewed and evaluated as part of the ITER/CDA design effort (1988-1990). The results have been documented in a detailed technical report. Emphasis was placed on the physical, thermal, mechanical, chemical stability/compatibility, tritium retention/release, and radiation stability properties which are needed to assess the performance of these materials in a fusion reactor environment. Materials properties correlations were selected for use in design analysis, and ranges for input parameters (e.g., temperature, porosity, etc.) were established. Also, areas for future research and development in blanket materials technology were highlighted and prioritized. For Li 2 O, the most significant increase in the database has come in the area of tritium retention as a function of operating temperature and purge flow composition. The database for postirradiation inventory from purged in-reactor samples has increased from four points to 20 points. These new data have allowed an improvement in understanding and modeling, as well as better interpretation of the results of laboratory annealing studies on unirradiated and irradiated material. In the case of Li 2 ZrO 3 , relatively little data were available on the sensitivity of the mechanical properties of this ternary ceramic to microstructure and moisture content. The increase in the database for this material has allowed not only better characterization of its properties, but also optimization of fabrication parameters to improve its performance. Some additional data are also available for the other two ternary ceramics to aid in the characterization of their performance. In particular, the thermal performance of these materials, as well as beryllium, in packed-bed form has been measured and characterized

  9. Investigation of the ion beryllium surface interaction

    International Nuclear Information System (INIS)

    Guseva, M.I.; Birukov, A.Yu.; Gureev, V.M.

    1995-01-01

    The self -sputtering yield of the Be was measured. The energy dependence of the Be self-sputtering yield agrees well with that calculated by W. Eckstein et. al. Below 770 K the self-sputtering yield is temperature independent; at T irr .> 870 K it increases sharply. Hot-pressed samples at 370 K were implanted with monoenergetic 5 keV hydrogen ions and with a stationary plasma (flux power ∼ 5 MW/m 2 ). The investigation of hydrogen behavior in beryllium shows that at low doses hydrogen is solved, but at doses ≥ 5x10 22 m -2 the bubbles and channels are formed. It results in hydrogen profile shift to the surface and decrease of its concentration. The sputtering results in further concentration decrease at doses > 10 25 m -2

  10. Polarizabilities of the beryllium clock transition

    International Nuclear Information System (INIS)

    Mitroy, J.

    2010-01-01

    The polarizabilities of the three lowest states of the beryllium atom are determined from a large basis configuration interaction calculation. The polarizabilities of the 2s 2 1 S e ground state (37.73a 0 3 ) and the 2s2p 3 P 0 o metastable state (39.04a 0 3 ) are found to be very similar in size and magnitude. This leads to an anomalously small blackbody radiation shift at 300 K of -0.018(4) Hz for the 2s 2 1 S e -2s2p 3 P 0 o clock transition. Magic wavelengths for simultaneous trapping of the ground and metastable states are also computed.

  11. Primordial beryllium as a big bang calorimeter.

    Science.gov (United States)

    Pospelov, Maxim; Pradler, Josef

    2011-03-25

    Many models of new physics including variants of supersymmetry predict metastable long-lived particles that can decay during or after primordial nucleosynthesis, releasing significant amounts of nonthermal energy. The hadronic energy injection in these decays leads to the formation of ⁹Be via the chain of nonequilibrium transformations: Energy(h)→T, ³He→⁶He, ⁶Li→⁹Be. We calculate the efficiency of this transformation and show that if the injection happens at cosmic times of a few hours the release of O(10 MeV) per baryon can be sufficient for obtaining a sizable ⁹Be abundance. The absence of a plateau structure in the ⁹Be/H abundance down to a O(10⁻¹⁴) level allows one to use beryllium as a robust constraint on new physics models with decaying or annihilating particles.

  12. Advances in beryllium powder consolidation simulations

    International Nuclear Information System (INIS)

    Reardon, B.J.

    1998-01-01

    A fuzzy logic based multiobjective genetic algorithm (GA) is introduced and the algorithm is used to optimize micromechanical densification modeling parameters for warm isopressed beryllium powder, HIPed copper powder and CIPed/sintered and HIPed tantalum powder. In addition to optimizing the main model parameters using the experimental data points as objective functions, the GA provides a quantitative measure of the sensitivity of the model to each parameter, estimates the mean particle size of the powder, and determines the smoothing factors for the transition between stage 1 and stage 2 densification. While the GA does not provide a sensitivity analysis in the strictest sense, and is highly stochastic in nature, this method is reliable and reproducible in optimizing parameters given any size data set and determining the impact on the model of slight variations in each parameter

  13. Electron-beam fusion welding of beryllium

    International Nuclear Information System (INIS)

    Campbell, R.P.; Dixon, R.D.; Liby, A.L.

    1978-01-01

    Ingot-sheet beryllium (Be) having three different chemistries and three different thicknesses was fusion-welded by the electron-beam process. Several different preheats were used to obtain 100% penetration and crack-free welds. Cracking susceptability was found to be related to aluminum (Al) content; the higher Al-content material was most susceptable. However, adequate preheat allowed full penetration and crack-free welds to be made in all materials tested. The effect of a post-weld heat treatment on the mechanical properties of these compositions was also determined. The heat treatment produced no significant effect on the ultimate tensile strength. However, the yield strength was decreased and the ductility was increased. These changes are attributed to the formation of AlFeBe 4 and FeBe 11

  14. Preparation of selenium coatings onto beryllium foils

    International Nuclear Information System (INIS)

    Erikson, E.D.; Tassano, P.L.; Reiss, R.H.; Griggs, G.E.

    1984-09-01

    A technique for preparing selenium films onto 50.8 microns thick beryllium foils is described. The selenium was deposited in vacuum from a resistance heated evaporation source. Profilometry measurements of the coatings indicate deposit thicknesses of 5.5, 12.9, 37.5, 49.8 and 74.5 microns. The control of deposition rate and of coating thickness was facilitated using a commercially available closed-loop programmable thin film controller. The x-ray transmission of the coated substrates was measured using a tritiated zirconium source. The transmissivities of the film/substrate combination are presented for the range of energies from 4 to 20 keV. 15 references, 3 figures

  15. Physical nature of structural and phase transformations in Cu-Al α solid solutions upon low-temperature irradiation and subsequent annealing

    Science.gov (United States)

    Petrenko, P. V.; Kulish, N. P.; Mel'nikova, N. A.; Grabovskii, Yu. E.

    2013-12-01

    Methods of X-ray diffraction analysis and measurements of residual resistivity have been used to study effects of electron irradiation in the temperature range of 250-330 K on the structural and phase state of the Cu-15 at % Al solid solution. The results obtained are explained by the presence in the Cu-Al alloys of an inhomogeneous short-range order of two types, i.e., low-temperature, α2 type; and high-temperature, γ2 type.

  16. Mitigation of solid waste and reuse of effluent from paint and varnish automotive and industrial treated by irradiation at electron beam accelerator

    International Nuclear Information System (INIS)

    Nascimento, Fernando C.; Ribeiro, Marcia A.; Duarte, Celina Lopes; Minamidani, Pedro T.; Guzella, Catia C.

    2011-01-01

    One of the most representative industrial segments is the polymeric coatings for house paint, automotive, industrial, marine, maintenance, and repainting markets. The general consumption of paint market in 2010 was 438,364 10 3 gallons of paint, in Brazil. However, when produce paints and varnishes, various kinds of solid wastes and liquid effluent are generated. The present research focus on the effluent from resins, water base paint and paint for electrophoresis, automotive industry, and general industrial coatings. The goal of this study is to use ionizing radiation to destroy the pollutants allowing the use of part of effluent as reuse water, and the rest discarded within the specified requirements. Actual industrial effluent samples were irradiated at Electron beam Accelerator applying absorbed doses of 10 kGy, 30 kGy and 50 kGy. The results, in this preliminary stage, showed a reduction of organic compounds and suspended solids. (author)

  17. Experimental Set-up for Irradiation of Solid H2 and D2 with Charged Particles of keV Energies

    DEFF Research Database (Denmark)

    Sørensen, H.

    1976-01-01

    crystal film thickness monitor. The target plate, which can be heated so that films are removable by evaporation, may be used both as a calorimeter and as a beam current collector. Methods for measurement of secondary electron emission coefficients were developed, and preliminary measurements were made...... with electrons and hydrogen ions. For electron bombardment, the secondary electron emission coefficient of solid deuterium was much smaller than one. It was shown possible to use the set-up to study beam desorption of very thin films. Furthermore the set-up could be used for measuring the energy......An experimental facility was built where films of solid deuterium (and hydrogen) may be made with known thickness and irradiated with pulsed beams of electrons (up to 3 keV) and light ions (up to 10 keV). Films are made on a target plate held at 2.5–3 K. Film growth rate is calibrated with a quartz...

  18. Deuterium permeation and diffusion in high-purity beryllium

    International Nuclear Information System (INIS)

    Abramov, E.; Riehm, M.P.; Thompson, D.A.; Smeltzer, W.W.

    1990-01-01

    The permeation rate of deuterium through high-purity beryllium membranes was measured using the gas-driven permeation technique. The time-dependent and the steady-state deuterium flux data were analyzed and the effective diffusivities of the samples were determined. Using multilayer permeation theory the effects of surface oxide were eliminated and the diffusion coefficients of the bulk beryllium determined. The diffusion parameters obtained for the extra-grade beryllium samples (99.8%) are D 0 =6.7x10 -9 m 2 /s and E D =28.4 kJ/mol. For the high-grade beryllium samples (99%) the parameters are D 0 =8.0x10 -9 m 2 /s and E D =35.1 kJ/mol. (orig.)

  19. Deuterium permeation and diffusion in high purity beryllium

    International Nuclear Information System (INIS)

    Abramov, E.

    1990-05-01

    The permeation rate of deuterium through high-purity beryllium membranes was measured using the gas-driven permeation technique. The time-dependent and the steady-state deuterium flux data were analyzed and the effective diffusivities of the samples were determined. A multilayer permeation theory was used in order to eliminate the surface oxide effects and the diffusion coefficients of the bulk beryllium were determined. The diffusion parameters obtained for the extra-grade beryllium samples (99.8%) are D 0 = 6.7 x 10 -9 [m 2 /s] and E D = 28.4 [KJ/mol]; and for the high-grade beryllium samples (99%) the parameters are D 0 = 8.0 x 10 -9 [m 2 /s] and E D = 35.1 [KJ/mol

  20. Spectrochemical determination of beryllium and lithium in stream sediments

    International Nuclear Information System (INIS)

    Gallimore, D.L.; Hues, A.D.; Palmer, B.A.; Cox, L.E.; Simi, O.R.; Bieniewski, T.M.; Steinhaus, D.W.

    1979-11-01

    A spectrochemical method was developed to analyze 200 or more samples of stream sediments per day for beryllium and lithium. One part of ground stream sediment is mixed with two parts graphite-SiO 2 buffer, packed into a graphite electrode, and excited in a direct-current arc. The resulting emission goes to a 3.4-m, direct-reading, Ebert spectrograph. A desk-top computer system is used to record and process the signals, and to report the beryllium and lithium concentrations. The limits of detection are 0.2 μg/g for beryllium and 0.5 μg/g for lithium. For analyses of prepared reference materials, the relative standard deviations were 16% for determining 0.2 to 100 μg/g of beryllium and 15% for determining 0.5 to 500 μg/g of lithium. A correction is made for vanadium interference

  1. Electropolishing or chemical milling of beryllium to remove machining defects

    International Nuclear Information System (INIS)

    Helms, J.R.

    1975-12-01

    The techniques of electropolishing and chemical milling to remove machine damage from beryllium are compared. Both techniques are found to be effective; chemical milling is recommended because it is easier to use and control

  2. Beryllium brazing considerations in CANDU fuel bundle manufacture

    International Nuclear Information System (INIS)

    Harmsen, J.; Pant, A.; Lewis, B.J.; Thompson, W.T.

    2010-01-01

    'Full text:' Appendages of CANDU fuel bundle elements are currently joined to zircaloy sheaths by vacuum beryllium brazing. Ongoing environmental and workplace concerns about beryllium combined with the continuous efforts by Cameco Fuel Manufacturing in its improvement process, initiated this study to find a substitute for pure beryllium. The presentation will review the necessary functionality of brazing alloy components and short list a series of alloys with the potential to duplicate the performance of pure beryllium. Modifications to current manufacturing processes based on in-plant testing will be discussed in relation to the use of these alloys. The presentation will conclude with a summary of the progress to date and further testing expected to be necessary.

  3. Health effects of beryllium exposure: a literature review

    National Research Council Canada - National Science Library

    Committee on Beryllium Alloy Exposures, Committee on Toxicology, National Research Council

    2007-01-01

    Beryllium is an important metal that is used in a number of industries-including the defense, aerospace, automotive, medical, and electronics industries-because of its exceptional strength, stability...

  4. Phosphorus-containing azo compounds as analytical reagents for beryllium

    International Nuclear Information System (INIS)

    Lisenko, N.F.; Dolzhnikova, E.N.; Petrova, G.S.; Tsvetkov, E.N.; Vsesoyuznyj Nauchno-Issledovatel'skij Inst. Khimicheskikh Reaktivov i Osobo Chistykh Veshchestv, Moscow; AN SSSR, Moscow. Inst. Ehlementoorganicheskikh Soedinenij)

    1979-01-01

    The interaction of beryllium with six new azocompounds based on chromotropic or R-acids and o-aminophenyl-phenylphosphonic acids is studied. A sharp difference in the detection limit for beryllium by the two groups of compounds is found. Azoderivatives based on chromotropic acid are promising agent for beryllium due to sufficiently high selectivity. The introduction of the methyl-group into the o-position of the phosphorus-containing group improves the analytical properties of agents. Techniques are developed for the determination of beryllium in bronze, sewage water and in an artificial mixture using a sodium salt of 1.8-dioxi-2 [2' - (oxi- (o-methylphenyl)-phosphenyl)-phenilazo]-naphtalene-3.6-disulfoacid

  5. Beryllium armour produced by evaporation-condensation technique

    International Nuclear Information System (INIS)

    Anisimov, A.; Frolov, V.; Moszherin, S.; Pepekin, G.; Pirogov, A.; Komarov, V.; Mazul, I.

    1997-01-01

    Beryllium, as armour material for ITER plasma facing components, has a limited erosion lifetime. In order to repair the surface of eroded tiles in-situ, Be-deposition technologies are under consideration. One of them uses the physical vapour deposition of beryllium on copper or beryllium substrate produced by a hot Be-target placed in the vicinity of this substrate. Three different options for using this technology for ITER Be-armour application are considered. The first option is the repair in-situ of eroded Be-tiles. The second option suggests the use of this technology to provide the joining of Be to Cu-substrate. The third option assumes the use of evaporated-condensed beryllium as a bulk tile material bonded to copper substrate by conventional joining (Brazing et al.) techniques. The first results and prospects of these approaches are presented below. (orig.)

  6. Data Needs for Erosion and Tritium Retention in Beryllium Surfaces

    International Nuclear Information System (INIS)

    Braams, B.J.

    2011-07-01

    A Consultants' Meeting was held at IAEA Headquarters 30-31 May 2011 with the aim to provide advice about the scope and aims of a planned IAEA coordinated research project on erosion and tritium retention in beryllium plasma-facing materials and about other activities of the A+M Data Unit in the area of plasma interaction with beryllium surfaces. The present report contains the proceedings, recommendations and conclusions of that Consultants' Meeting. (author)

  7. The beryllium production at Ulba metallurgical plant (Ust-Kamenogrsk, Kazakhstan)

    Energy Technology Data Exchange (ETDEWEB)

    Dvinskykh, E.M.; Savchuk, V.V.; Tuzov, Y.V. [Ulba Metallurgical Plant (Zavod), Ust-Kamenogorsk, Abay prospect 102 (Kazakhstan)

    1998-01-01

    The Report includes data on beryllium production of Ulba metallurgical plant, located in Ust-Kamenogorsk (Kazakhstan). Beryllium production is showed to have extended technological opportunities in manufacturing semi-products (beryllium ingots, master alloys, metallic beryllium powders, beryllium oxide) and in production of structural beryllium and its parts. Ulba metallurgical plant owns a unique technology of beryllium vacuum distillation, which allows to produce reactor grades of beryllium with a low content of metallic impurities. At present Ulba plant does not depend on raw materials suppliers. The quantity of stored raw materials and semi-products will allow to provide a 25-years work of beryllium production at a full capacity. The plant has a satisfactory experience in solving ecological problems, which could be useful in ITER program. (author)

  8. All-proportional solid-solution Rh–Pd–Pt alloy nanoparticles by femtosecond laser irradiation of aqueous solution with surfactant

    Energy Technology Data Exchange (ETDEWEB)

    Sarker, Md. Samiul Islam, E-mail: samiul-phy@ru.ac.bd; Nakamura, Takahiro; Sato, Shunichi [Tohoku University, Institute of Multidisciplinary Research for Advanced Materials (Japan)

    2015-06-15

    Formation of Rh–Pd–Pt solid-solution alloy nanoparticles (NPs) by femtosecond laser irradiation of aqueous solution in the presence of polyvinylpyrrolidone (PVP) or citrate as a stabilizer was studied. It was found that the addition of surfactant (PVP or citrate) significantly contributed to reduce the mean size of the particles to 3 nm for PVP and 10 nm for citrate, which was much smaller than that of the particles fabricated without any surfactants (20 nm), and improved the dispersion state as well as the colloidal stability. The solid-solution formation of the Rh–Pd–Pt alloy NPs was confirmed by the XRD results that the diffraction pattern was a single peak, which was found between the positions corresponding to each pure Rh, Pd, and Pt NPs. Moreover, all the elements were homogeneously distributed in every particle by STEM-EDS elemental mapping, strongly indicating the formation of homogeneous solid-solution alloy. Although the Rh–Pd–Pt alloy NPs fabricated with PVP was found to be Pt rich by EDS observation, the composition of NPs fabricated with citrate almost exactly preserved the feeding ratio of ions in the mixed solution. To our best knowledge, these results demonstrated for the first time, the formation of all-proportional solid-solution Rh–Pd–Pt alloy NPs with well size control.

  9. Exposure and genetics increase risk of beryllium sensitisation and chronic beryllium disease in the nuclear weapons industry.

    Science.gov (United States)

    Van Dyke, Michael V; Martyny, John W; Mroz, Margaret M; Silveira, Lori J; Strand, Matt; Cragle, Donna L; Tankersley, William G; Wells, Susan M; Newman, Lee S; Maier, Lisa A

    2011-11-01

    Beryllium sensitisation (BeS) and chronic beryllium disease (CBD) are caused by exposure to beryllium with susceptibility affected by at least one well-studied genetic host factor, a glutamic acid residue at position 69 (E69) of the HLA-DPβ chain (DPβE69). However, the nature of the relationship between exposure and carriage of the DPβE69 genotype has not been well studied. The goal of this study was to determine the relationship between DPβE69 and exposure in BeS and CBD. Current and former workers (n=181) from a US nuclear weapons production facility, the Y-12 National Security Complex (Oak Ridge, Tennessee, USA), were enrolled in a case-control study including 35 individuals with BeS and 19 with CBD. HLA-DPB1 genotypes were determined by PCR-SSP. Beryllium exposures were assessed through worker interviews and industrial hygiene assessment of work tasks. After removing the confounding effect of potential beryllium exposure at another facility, multivariate models showed a sixfold (OR 6.06, 95% CI 1.96 to 18.7) increased odds for BeS and CBD combined among DPβE69 carriers and a fourfold (OR 3.98, 95% CI 1.43 to 11.0) increased odds for those exposed over an assigned lifetime-weighted average exposure of 0.1 μg/m(3). Those with both risk factors had higher increased odds (OR 24.1, 95% CI 4.77 to 122). DPβE69 carriage and high exposure to beryllium appear to contribute individually to the development of BeS and CBD. Among workers at a beryllium-using facility, the magnitude of risk associated with either elevated beryllium exposure or carriage of DPβE69 alone appears to be similar.

  10. Beryllium data base for in-pile mockup test on blanket of fusion reactor, (1)

    Energy Technology Data Exchange (ETDEWEB)

    Kawamura, Hiroshi; Ishitsuka, Etsuo (Japan Atomic Energy Research Inst., Oarai, Ibaraki (Japan). Oarai Research Establishment); Sakamoto, Naoki; Kato, Masakazu; Takatsu, Hideyuki.

    1992-11-01

    Beryllium has been used in the fusion blanket designs with ceramic breeder as a neutron multiplier to increase the net tritium breeding ratio (TBR). The properties of beryllium, that is physical properties, chemical properties, thermal properties, mechanical properties, nuclear properties, radiation effects, etc. are necessary for the fusion blanket design. However, the properties of beryllium have not been arranged for the fusion blanket design. Therefore, it is indispensable to check and examine the material data of beryllium reported previously. This paper is the first one of the series of papers on beryllium data base, which summarizes the reported material data of beryllium. (author).

  11. In Quest of the Alanine R3 Radical: Multivariate EPR Spectral Analyses of X-Irradiated Alanine in the Solid State.

    Science.gov (United States)

    Jåstad, Eirik O; Torheim, Turid; Villeneuve, Kathleen M; Kvaal, Knut; Hole, Eli O; Sagstuen, Einar; Malinen, Eirik; Futsaether, Cecilia M

    2017-09-28

    The amino acid l-α-alanine is the most commonly used material for solid-state electron paramagnetic resonance (EPR) dosimetry, due to the formation of highly stable radicals upon irradiation, with yields proportional to the radiation dose. Two major alanine radical components designated R1 and R2 have previously been uniquely characterized from EPR and electron-nuclear double resonance (ENDOR) studies as well as from quantum chemical calculations. There is also convincing experimental evidence of a third minor radical component R3, and a tentative radical structure has been suggested, even though no well-defined spectral signature has been observed experimentally. In the present study, temperature dependent EPR spectra of X-ray irradiated polycrystalline alanine were analyzed using five multivariate methods in further attempts to understand the composite nature of the alanine dosimeter EPR spectrum. Principal component analysis (PCA), maximum likelihood common factor analysis (MLCFA), independent component analysis (ICA), self-modeling mixture analysis (SMA), and multivariate curve resolution (MCR) were used to extract pure radical spectra and their fractional contributions from the experimental EPR spectra. All methods yielded spectral estimates resembling the established R1 spectrum. Furthermore, SMA and MCR consistently predicted both the established R2 spectrum and the shape of the R3 spectrum. The predicted shape of the R3 spectrum corresponded well with the proposed tentative spectrum derived from spectrum simulations. Thus, results from two independent multivariate data analysis techniques strongly support the previous evidence that three radicals are indeed present in irradiated alanine samples.

  12. Study of gamma irradiation effects on the etching and optical properties of CR-39 solid state nuclear track detector and its application to uranium assay in soil samples

    International Nuclear Information System (INIS)

    Amol Mhatre; Kalsi, P.C.

    2011-01-01

    The gamma irradiation effects in the dose range of 2.5-43.0 Mrad on the etching and optical characteristics of CR-39 solid state nuclear track detector (SSNTD) have been studied by using etching and UV-Visible spectroscopic techniques. From the measured bulk etch rates at different temperatures, the activation energies for bulk etching at different doses have also been determined. It is seen that the bulk etch rates increase and the activation energies for bulk etching decrease with the increase in gamma dose. The optical band gaps of the unirradiated and the gamma -irradiated detectors determined from the UV-Visible spectra were found to decrease with the increase in gamma dose. These results have been explained on the basis of scission of the detector due to gamma irradiation. The present studies can be used for the estimation of gamma dose in the range of 2.5-43.0 Mrad and can also be used for estimating track registration efficiency in the presence of gamma dose. The CR-39 detector has also been applied for the assay of uranium in some soil samples of Jammu city. (author)

  13. Deposition of radiation energy in solids as visualized by the distribution, structure and properties of alkyl radicals in γ-irradiated n-alkane single crystals

    International Nuclear Information System (INIS)

    Gillbro, T.; Lund, A.

    1976-01-01

    This paper summarizes results obtained earlier from ESR studies of γ-irradiated n-alkane single crystals. It also contains some new experimental results that serve to give a more complete picture of the deposition of radiation energy in solid alkanes. The experiments performed with solid n-alkanes have thus far provided structural data that permit the nature and even the conformation of alkyl radicals to be clearly understood. Two types of radical exist namely, one where the unpaired electron is located next to the end methyl group and one with the unpaired electron in the interior of the chain. The first type has a conformation which differs from that of the undamaged molecule. Microwave saturation data show that there is a difference in relaxation properties of these radicals which can be understood in terms of a difference in mobility. Relative yield measurements give the distribution of isomeric alkyl, the result differing from that obtained using product analysis in liquids. For protiated n-alkanes n-alkyl is lacking and the 2-alkyl concentration is higher than expected. For deuterated n-alkanes the ESR spectrum is mainly that of radicals with the unpaired electron located in the interior of the carbon chain. This isotope effect is again contrary to observations in liquid n-alkanes. The broad lines observed in protiated alkanes irradiated at 77 K and deuterated alkanes irradiated at 4.2 K are not believed to arise from strong spin-spin interactions. They are thought instead to arise from distorted crystal and radical structures relating to the damaged regions of the crystals. (Auth.)

  14. Development of intergranular thermal residual stresses in beryllium during cooling from processing temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Brown, D.W. [Los Alamos National Laboratory, Los Alamos, NM 87545 (United States)], E-mail: dbrown@lanl.gov; Sisneros, T.A.; Clausen, B.; Abeln, S.; Bourke, M.A.M.; Smith, B.G.; Steinzig, M.L.; Tome, C.N.; Vogel, S.C. [Los Alamos National Laboratory, Los Alamos, NM 87545 (United States)

    2009-02-15

    The intergranular thermal residual stresses in texture-free solid polycrystalline beryllium were determined by comparison of crystallographic lattice parameters in solid and powder samples measured by neutron diffraction during cooling from 800 deg. C. The internal stresses are not significantly different from zero >575 deg. C and increase nearly linearly <525 deg. C. At room temperature, the c axis of an average grain is under {approx}200 MPa of compressive internal stress, and the a axis is under 100 MPa of tensile stress. For comparison, the stresses have also been calculated using an Eshelby-type polycrystalline model. The measurements and calculations agree very well when temperature dependence of elastic constants is accounted for, and no plastic relaxation is allowed in the model.

  15. A study on irradiation damage of solid 5'-dTMP implanted by low energy N+ ion beam

    International Nuclear Information System (INIS)

    Shao Chunlin; Yu Zengliang

    1995-01-01

    The yields of inorganic phosphate and base released from 5'-dTMP irradiated by 30 keV N + ion beam were investigated. The fluence effects of these yields and the influence with 0.1 mol/L NaOH treatment on them were presented. It was shown that the alkali treatment would not only increase the yield of inorganic phosphate, but also damage and then split base released from the irradiated 5'-dTMP. When the irradiated samples were treated with 0.1 mol/L NaOH immediately, the yield of inorganic phosphate was increased by a factor of 1.7 and the concentration of base decreased to half of that in the sample's water solution. Furthermore, the yield of inorganic phosphate would increase by a factor of 2.8 after 40 min of alkali treatment. Irradiation effects of ion beam were mainly direct ones and had a higher value of G(P i ), greater than 0.44 molecule/100 eV

  16. Beryllium reflectors for research reactors. Review and preliminary finite element analysis

    Energy Technology Data Exchange (ETDEWEB)

    Bejarano, Pablo S; Cocco, Roxana G., E-mail: rcocco@invap.com.ar [INVAP S.E., Rio Negro (Argentina)

    2012-03-15

    Beryllium is used in numerous research reactors to moderate neutron energy and to reflect neutrons back into the core, thus intensifying the thermal neutron flux. However, beryllium is degraded by radiation damage, as a result of both displacement and transmutation. Displacement damage leads to point defect clustering, irradiation hardening and embrittlement. Transmutation produces helium, which results in high levels of gas and swelling, even at low temperatures. A brief state-of-the-art review on the use of reflector assemblies reveals that each user has adopted a different method for overcoming problems related to swelling: strengthening, cracking and distortion. In the present work a preliminary study about the geometry influence on the reflector assembly behavior was performed by a Finite Element Analysis (FEA). A simplified study was made varying its geometry in height, thickness and width. The results showed that the most influencing parameter in avoiding distortion due to swelling is firstly the reflector's assembly height, H; secondly its thickness, L, and lastly its angle/width, {theta}. These results contribute to the understanding of distortion behavior and the stresses generated in a simple geometry Be bar subjected to radiation, which can be a useful tool for mechanical design of more complex components. (author)

  17. Green synthesis of 3,4-dihydropyrimidinones using nano Fe3O4@meglumine sulfonic acid as a new efficient solid acid catalyst under microwave irradiation

    Directory of Open Access Journals (Sweden)

    Leila Moradi

    2018-01-01

    Full Text Available Design, synthesis and characterization of nano Fe3O4@meglumine sulfonic acid as a new solid acid catalyst for the simple and green one pot multicomponent synthesis of 3,4-dihydropyrimidin-2(1H-ones/thiones was studied. New solid acid catalyst was prepared through a clean and simple protocol and characterized using FTIR, VSM, TGA, SEM, elemental analysis (CHN and XRD techniques. Heterogenization of homogeneous catalyst as a green approach is a useful method for enhancing the efficiency of catalyst. Presented study was a new method for attachment of homogeneous highly soluble catalyst (meglumine sulfate to the magnetite nanoparticle surfaces for preparing a heterogeneous and effective catalyst. Obtained heterogeneous and reusable solid acid catalyst has high performance in the synthesis of Biginelli compounds. The reaction was performed under microwave irradiation as a rapid and green condition. Easy work up as well as excellent yield (90–98% of products in short reaction times (40–200 s and reusable catalyst are the main advantages of presented procedure. Reaction products were characterized in details using physical and chemical techniques such as melting point, 1H NMR, 13C NMR and FTIR.

  18. Vapor pressure and thermodynamics of beryllium carbide

    International Nuclear Information System (INIS)

    Rinehart, G.H.; Behrens, R.G.

    1980-01-01

    The vapor pressure of beryllium carbide has been measured over the temperature range 1388 to 1763 K using Knudsen-effusion mass spectrometry. Vaporization occurs incongruently according to the reaction Be 2 C(s) = 2Be(g) + C(s). The equilibrium vapor pressure above the mixture of Be 2 C and C over the experimental temperature range is (R/J K -1 mol -1 )ln(p/Pa) = -(3.610 +- 0.009) x 10 5 (K/T) + (221.43 +- 1.06). The third-law enthalpy change for the above reaction obtained from the present vapor pressures is ΔH 0 (298.15 K) = (740.5 +- 0.1) kJ mol -1 . The corresponding second-law result is ΔH 0 (298.15 K) = (732.0 +- 1.8) kJ mol -1 . The enthalpy of formation for Be 2 C(s) calculated from the present third-law vaporization enthalpy and the enthalpy of formation of Be(g) is ΔH 0 sub(f)(298.15 K) = -(92.5 +- 15.7) kJ mol -1 . (author)

  19. Beryllium application in ITER plasma facing components

    International Nuclear Information System (INIS)

    Raffray, A.R.; Federici, G.; Barabash, V.; Cardella, A.; Jakeman, R.; Ioki, K.; Janeschitz, G.; Parker, R.; Tivey, R.; Pacher, H.D.; Wu, C.H.; Bartels, H.W.

    1997-01-01

    Beryllium is a candidate armour material for the in-vessel components of the International Thermonuclear Experimental Reactor (ITER), namely the primary first wall, the limiter, the baffle and the divertor. However, a number of issues arising from the performance requirements of the ITER plasma facing components (PFCs) must be addressed to better assess the attractiveness of Be as armour for these different components. These issues include heat loading limits arising from temperature and stress constraints under steady state conditions, armour lifetime including the effects of sputtering erosion as well as vaporisation and loss of melt during disruption events, tritium retention and permeation, and chemical hazards, in particular with respect to potential Be/steam reaction. Other issues such as fabrication and the possibility of in-situ repair are not performance-dependent but have an important impact on the overall assessment of Be as PFC armour. This paper describes the present view on Be application for ITER PFCs. The key issues are discussed including an assessment of the current level of understanding based on analysis and experimental data; and on-going activities as part of the ITER EDA R and D program are highlighted. (orig.)

  20. The unusual properties of beryllium surfaces

    International Nuclear Information System (INIS)

    Stumpf, R.; Hannon, J.B.

    1994-01-01

    Be is a ''marginal metal.'' The stable phase, hcp-Be, has a low Fermi-level density of states and very anisotropic structural and elastic properties, similar to a semiconductor's. At the Be(0001) surface, surface states drastically increase the Fermi-level density of states. The different nature of bonding in bulk-Be and at the Be(0001) surface explains the large outward relaxation. The presence of surface states causes large surface core-level shifts by inducing a higher electrostatic potential in the surface layers and by improving the screening at the surface. The authors experimental and theoretical investigations of atomic vibrations at the Be(0001) surface demonstrate clearly that Be screening of atomic motion by the surface states makes the surface phonon dispersion fundamentally different from that of the bulk. Properties of Be(0001) are so different from those of the bulk that the surface can be considered a new ''phase'' of beryllium with unique electronic and structural characteristics. For comparison they also study Be(11 bar 20), a very open surface without important surface states. Be(11 bar 20) is the only clean s-p metal surface known to reconstruct (1 x 3 missing row reconstruction)