The properties and transport phenomena in oxide films on iron, nickel, chromium and their alloys in aqueous environments

International Nuclear Information System (INIS)

Laitinen, T.; Bojinov, M.; Betova, I.; Maekelae, K.; Saario, T.

1999-01-01

The construction materials used in coolant systems in nuclear power plants become covered with oxide films as a result of exposure to the aqueous environment. The susceptibility of the materials to different forms of corrosion, as well as the extent of the incorporation of radioactive species on the surfaces of the primary circuit, are greatly influenced by the physical and chemical properties of these oxide films. The composition and characteristics of the oxide films in turn depend on the applied water chemistry. This work was undertaken in order to collect and evaluate the present views on the structure and behaviour of oxide films formed on iron- and nickel-based materials in aqueous environments. This survey should serve to recognise the areas in which more understanding and research effort is needed. The review begins with a discussion on the bulk oxides of iron, nickel and chromium, as well as their mixed oxides. In addition to bulk oxides, the structure and properties of oxide films forming on pure iron, nickel and chromium and on iron- and nickel-based engineering alloys are considered. General approaches to model the structure and growth of oxide films on metals are discussed in detail. The specific features of the oxide structures, properties and growth at high temperatures are presented with special focus on the relevance of existing models. Finally, the role of oxide films in localised corrosion, oxide breakdown pitting. Stress corrosion cracking and related phenomena is considered. The films formed on the surfaces of iron- and nickel-based alloys in high-temperature aqueous environments generally comprise two layers, i.e. the so-called duplex structure. The inner part is normally enriched in chromium and has a more compact structure, while the outer part is enriched in iron and has a cracked or porous structure. The information collected clearly indicates the effect of the chemical environment on the properties of oxide films growing on metal surfaces

The properties and transport phenomena in oxide films on iron, nickel, chromium and their alloys in aqueous environments

Energy Technology Data Exchange (ETDEWEB)

Laitinen, T.; Bojinov, M.; Betova, I.; Maekelae, K.; Saario, T. [VTT Manufacturing Technology, Espoo (Finland)

1999-01-01

The construction materials used in coolant systems in nuclear power plants become covered with oxide films as a result of exposure to the aqueous environment. The susceptibility of the materials to different forms of corrosion, as well as the extent of the incorporation of radioactive species on the surfaces of the primary circuit, are greatly influenced by the physical and chemical properties of these oxide films. The composition and characteristics of the oxide films in turn depend on the applied water chemistry. This work was undertaken in order to collect and evaluate the present views on the structure and behaviour of oxide films formed on iron- and nickel-based materials in aqueous environments. This survey should serve to recognise the areas in which more understanding and research effort is needed. The review begins with a discussion on the bulk oxides of iron, nickel and chromium, as well as their mixed oxides. In addition to bulk oxides, the structure and properties of oxide films forming on pure iron, nickel and chromium and on iron- and nickel-based engineering alloys are considered. General approaches to model the structure and growth of oxide films on metals are discussed in detail. The specific features of the oxide structures, properties and growth at high temperatures are presented with special focus on the relevance of existing models. Finally, the role of oxide films in localised corrosion, oxide breakdown pitting. Stress corrosion cracking and related phenomena is considered. The films formed on the surfaces of iron- and nickel-based alloys in high-temperature aqueous environments generally comprise two layers, i.e. the so-called duplex structure. The inner part is normally enriched in chromium and has a more compact structure, while the outer part is enriched in iron and has a cracked or porous structure. The information collected clearly indicates the effect of the chemical environment on the properties of oxide films growing on metal surfaces

A Neutron Elastic Scattering Study of Chromium, Iron and Nickel in the Energy Region 1.77 to 2.76 MeV

Energy Technology Data Exchange (ETDEWEB)

Holmqvist, B; Johansson, S G; Lodin, G; Wiedling, T [AB Atomenergi, Nyko eping (Sweden); Salama, M [Reactor and Neutron Physics Dept., Atomic Energy Es tablishment, Cairo (Egypt)

1970-07-01

Elastic neutron scattering measurements have been performed on the natural elements chromium, iron and nickel. Angular distributions were recorded in the interval 20 to 160 deg at several energies in the region 1.77 to 2.76 MeV. The experimental data were analysed in terms of the optical model, applying a spherical nuclear potential.

The Properties Of And Transport Phenomena In Oxide Films On Iron, Nickel, Chromium And Their Alloys In Aqueous Environments

International Nuclear Information System (INIS)

Saario, T.; Laitinen, T.; Maekelae, K.; Bojinov, M.; Betova, I.

1998-07-01

The construction materials used in coolant systems in nuclear power plants become covered with oxide films as a result of exposure to the aqueous environment. The susceptibility of the materials to different forms of corrosion, as well as the extent of the incorporation of radioactive species on the surfaces of the primary circuit, are greatly influenced by the physical and chemical properties of these oxide films. The composition and characteristics of the oxide films in turn depend on the applied water chemistry. This work was undertaken in order to collect and evaluate the present views on the structure and behaviour of oxide films formed on iron- and nickel-based materials in aqueous environments. This survey should serve to recognise the areas in which more understanding and research effort is needed. The review begins with a discussion on the bulk oxides of iron, nickel and chromium, as well as their mixed oxides. In addition to bulk oxides, the structure and properties of oxide films forming on pure iron, nickel and chromium and on iron- and nickel-based engineering alloys are considered. General approaches to model the structure and growth of oxide films on metals are discussed in detail. The specific features of the oxide structures, properties and growth at high temperatures are presented with special focus on the relevance of existing models. Finally, the role of oxide films in localised corrosion, oxide breakdown, pitting, stress corrosion cracking and related phenomena is considered. The films formed on the surfaces of iron- and nickel-based alloys in high-temperature aqueous environments generally comprise two layers, i.e. the so-called duplex structure. The inner part is normally enriched in chromium and has a more dense structure, while the outer part is enriched in iron and has a cracked or porous structure. The information collected clearly indicates the effect of the chemical environment on the properties of oxide films growing on metal surfaces

40 CFR Appendix Xii to Part 266 - Nickel or Chromium-Bearing Materials that may be Processed in Exempt Nickel-Chromium Recovery...

Science.gov (United States)

2010-07-01

... 40 Protection of Environment 26 2010-07-01 2010-07-01 false Nickel or Chromium-Bearing Materials that may be Processed in Exempt Nickel-Chromium Recovery Furnaces XII Appendix XII to Part 266... FACILITIES Pt. 266, App. XII Appendix XII to Part 266—Nickel or Chromium-Bearing Materials that may be...

Observed transitions in n = 2 ground configurations of copper, nickel, iron, chromium and germanium in tokamak discharges

International Nuclear Information System (INIS)

Hinnov, E.; Suckewer, S.; Cohen, S.; Sato, K.

1981-11-01

A number of spectrum lines of highly ionized copper, nickel, iron, chromium, and germanium have been observed and the corresponding transitions identified. The element under study is introduced into the discharge of the PLT Tokamak by means of rapid ablation by a laser pulse. The ionization state is generally distinguishable from the time behavior of the emitted light. New identifications of transitions are based on predicted wavelengths (from isoelectronic extrapolation and other data) and on approximate expected intensities. All the transitions pertain to the ground configurations of the respective ions, which are the only states strongly populated at tokamak plasma conditions. These lines are expected to be useful for spectroscopic plasma diagnostics in the 1-3 keV temperature range, and they provide direct measurement of intersystem energy separations from chromium through copper in the oxygen, nitrogen, and carbon isoelectronic sequences

Specification for corrosion-resisting chromium and chromium-nickel steel welding rods and bare electrodes - approved 1969

International Nuclear Information System (INIS)

Anon.

1975-01-01

This specification covers corrosion-resisting chromium and chromium-nickel steel welding rods for use with the atomic hydrogen and gas-tungsten-arc welding processes and bare electrodes for use with the submerged arc and gas metal-arc welding processes. These welding rods and electrodes include those alloy steels designated as corrosion- or heat-resisting chromium and chromium-nickel steels, in which chromium exceeds 4% and nickel does not exceed 50%

Biomonitoring for iron, manganese, chromium, aluminum, nickel and cadmium in workers exposed to welding fume: a preliminary study

Directory of Open Access Journals (Sweden)

Mulyana

2015-05-01

Full Text Available The control of exposure to welding fumes is increasing importance in promoting a healthy, safe and productive work environment. This study is a case-control design, random study was conducted among welder (56 subjects and non welder (39 subjects with more than 1 years experience in the same job task in an automotive parts manufactory within the industrial area at Cikarang in 2013. All subjects were completed physical examination, informed consent and questionnaire. Blood heavy metals were determined by Inductively-Coupled Plasma Mass Spectrometry (ICP-MS. Whole blood iron, manganese, chromium and lead in welder were higher than non-welder, but not different for aluminum, nickel and cadmium. In welder, chromium and manganese correlated with smoking status, cadmium correlated with age and smoking status. In multivariate analysis, wholeblood cadmium correlates with age and smoking status.

Crystallization and structure of chromium cast iron with addition of Mo and Ni

International Nuclear Information System (INIS)

Pietrowski, S.

1998-01-01

The aim of the presented paper is to show the results of examination of the crystallization process using the method of thermal-derivative analysis (ATD) and the structure examination of chromium cast iron, chromium molybdenum c. i. and chromium molybdenum nickel c.i. It was found that molybdenum in amount over 2 wt % causes the crystallization of eutectic carbides M 23 C 6 and M 6 C. The M 23 C 6 carbide crystallizes upon the crystallization of eutectic carbides M 3 C and M 7 C 3 . It is shown that ATD method facilitates both interpretation and control of the crystallization as well as formation of the cast iron structure at the solid state. (author)

Measurement of (n,/alpha/) cross sections of chromium, iron, and nickel in the 5- to 10-MeV neutron energy range

International Nuclear Information System (INIS)

Paulsen, A.; Liskien, H.; Arnotte, F.; Widera, R.

1981-01-01

A measuring program has been carried out at the Van de Graaff accelerator facility of the Central Bureau for Nuclear Measurements for the determination of (n,/alpha/) cross sections on the main constituents of fast reactor structural materials, namely the elements chromium, iron, and nickel. Results obtained in the energy range from 5 to 10 Mev are presented in terms of laboratory angle-differential cross sections, relative Legendre polynomial coefficients of angular distributions, angle-integrated cross sections, and average alpha energies. 13 refs

Monitoring of occupational exposure in manufacturing of stainless steel constructions. Part I: Chromium, iron, manganese, molybdenum, nickel and vanadium in the workplace air of stainless steel welders.

Science.gov (United States)

Kucera, J; Bencko, V; Pápayová, A; Saligová, D; Tejral, J; Borská, L

2001-11-01

Exposure to workplace airborne pollutants was examined in a group of 20 workers dealing mainly with welding, polishing, drilling and assembling of stainless steel constructions. Airborne particulate matter (APM) collected using both personal and stationary samplers was analyzed by instrumental neutron activation analysis (INAA). Quality assurance procedures of both sampling and analytical stages are described. Of the elements determined, results are presented for chromium, iron, manganese, molybdenum, nickel and vanadium. The median values of element concentrations exceeded the maximum admissible limits for workplace pollutants only for chromium, while for nickel the limit was exceeded in several individual cases. Sampling of hair, nails, blood, urine and saliva to be used for biological monitoring of the exposed and control groups is also described.

Calculated electronic structure of chromium surfaces and chromium monolayers on iron

International Nuclear Information System (INIS)

Victora, R.H.; Falicov, L.M.

1985-01-01

A self-consistent calculation of the magnetic and electronic properties of the chromium (100) and (110) surfaces and of a chromium monolayer on the (100) and (110) iron surfaces is presented. It is found that (i) the (100) chromium surface is ferromagnetic with a greatly enhanced spin polarization (3.00 electrons); (ii) a substantial enhancement of the spin imbalance exists several (>5) layers into the bulk; (iii) the (110) chromium surface is antiferromagnetic with a large (2.31) spin imbalance; (iv) the (100) chromium monolayer on ferromagnetic iron is ferromagnetic, with a huge spin imbalance (3.63), and aligned antiferromagnetically with respect to the bulk iron; (v) the (110) chromium monolayer on ferromagnetic iron is also ferromagnetic, with a spin imbalance of 2.25 and antiferromagnetically aligned to the iron. The spin imbalance of chromium on iron (100) is possibly the largest of any transition-metal system

On the rational alloying of structural chromium-nickel steels

International Nuclear Information System (INIS)

Astaf'ev, A.A.

1982-01-01

A study was made on the influence of chromium nickel, phosphorus on the critical brittleness temperature of Cr-Ni-Mo-V structural steels. It is shown that the critical brittleness temperature of these steels increases at chromium content more over than 2% and nickel content more than 2% in the result of carbide transformations during tempering. Increase of nickel content in Cr-Ni-Mo-V-steels strengthens the tendency to embrittlement during slow cooling, from tempering temperature owing to development of process of phosphorus grain-boundary segregation. Two mentioned mechanisms of embrittlement determine principles of rational steel alloying. The extreme dependence of the critical brittleness temperature on chromium and nickel content, which enables to choose the optimum composition of Cr-Ni-Mo-V-steels, was established

The determination of copper and nickel in iron- and chromium-bearing materials by a pressed-powder technique and x-ray-fluorescence spectrometry

International Nuclear Information System (INIS)

Balaes, A.M.E.; Dixon, K.

1984-01-01

A method was developed that is suitable for the determination of copper and nickel in ores such as those from the Merensky and UG-2 Reefs. The sample was ground finely and diluted with river sand so that matrix variations were avoided as much as possible. After the addition of a wax-polystyrene binder, the material was pelletized. The matrix effects of iron and chromium, and the effects of their mutual interferences on the determination of copper and nickel, were then investigated. Equations were derived for the corrected copper and nickel Kα intensities, and were applied to the analyses of head, concentrate, middling, and tailing samples. Comparative values obtained by atomic-absorption spectrophotometry were found to be in reasonable agreement with the X-ray values; the average deviation was +0,3 per cent for copper and -1,6 per cent for nickel relative to the AAS values. The limits of detection of the method for copper and nickel are 31 and 40μg/g respectively; the limit of determination for copper is 92μg/g and for nickel is 119μg/g. The relative standard deviation at 900 and 2400μg of copper and nickel per gram is 0,02

Study of the polarization for Incoloy 800 and for the stainless stell AISI 304 in mixtures of Iron, Nickel and Chromium Chlorides

International Nuclear Information System (INIS)

Travalloni, A.M.; Sathler, L.; Mattos, O.R.

1985-01-01

Polarization curves for the Incoloy 800 and for the stainless stell AISI 304 were obtained with static and rotational electrodes. The electrolytes employed showed growing concentrations of mixtures as Iron, Nickel and Chromium Chlorides their proportion being the same as the content of these elements in the respective alloys. The alloys under investigation exhibited a continuous transition behaviour from the passive to the active-passive and to the active conditions. Also, the pH was found the main parameter controlling the anodic behaviour of the alloy. (Author) [pt

Specification for corrosion-resisting chromium and chromium-nickel steel bare and composite metal cored and stranded arc welding electrodes and welding rods

International Nuclear Information System (INIS)

Anon.

1983-01-01

This specification prescribes requirements for corrosion or heat resisting chromium and chromium-nickel steel electrodes and welding rods. These electrodes and welding rods are normally used for arc welding and include those alloy steels designated as corrosion or heat-resisting chromium and chromium-nickel steels, in which chromium exceeds 4.0 percent and nickel does not exceed 50.0 percent

Method for electrodeposition of nickel--chromium alloys and coating of uranium

International Nuclear Information System (INIS)

Stromatt, R.W.; Lundquist, J.R.

1975-01-01

High-quality electrodeposits of nickel-chromium binary alloys in which the percentage of chromium is controlled can be obtained by the addition of a complexing agent such as ethylenediaminetetraacetic disodium salt to the plating solution. The nickel-chromium alloys were found to provide an excellent hydrogen barrier for the protection of uranium fuel elements. (U.S.)

Genotoxic Effects Due to Exposure to Chromium and Nickel Among Electroplating Workers.

Science.gov (United States)

El Safty, Amal Mohamed Kamal; Samir, Aisha Mohamed; Mekkawy, Mona Kamal; Fouad, Marwa Mohamed

Using chromium and nickel for electroplating is important in many industries. This process induces variable adverse health effects among exposed workers. The aim of this study is to detect the genotoxic effects of combined exposure to chromium and nickel among electroplating workers. This study was conducted on 41 male workers occupationally exposed to chromium and nickel in the electroplating section of a factory compared to 41 male nonexposed individuals, where full history and clinical examination were performed. Laboratory investigations included measurement of serum chromium, nickel, 8-hydroxydeoxyguanosine (8-OHdG), and micronuclei were measured in buccal cells. In exposed workers, serum chromium ranged from 0.09 to 7.20 µg/L, serum nickel ranged from 1.20 to 28.00 µg/L, serum 8-OHdG ranged from 1.09 to12.60 ng/mL, and these results were statistically significantly increased compared to nonexposed group ( P electroplating industry are at risk of significant cytogenetic damage.

Exposure to nickel, chromium, or cadmium causes distinct changes in the gene expression patterns of a rat liver derived cell line.

Directory of Open Access Journals (Sweden)

Matthew G Permenter

Full Text Available Many heavy metals, including nickel (Ni, cadmium (Cd, and chromium (Cr are toxic industrial chemicals with an exposure risk in both occupational and environmental settings that may cause harmful outcomes. While these substances are known to produce adverse health effects leading to disease or health problems, the detailed mechanisms remain unclear. To elucidate the processes involved in the toxicity of nickel, cadmium, and chromium at the molecular level and to perform a comparative analysis, H4-II-E-C3 rat liver-derived cell lines were treated with soluble salts of each metal using concentrations derived from viability assays, and gene expression patterns were determined with DNA microarrays. We identified both common and unique biological responses to exposure to the three metals. Nickel, cadmium, chromium all induced oxidative stress with both similar and unique genes and pathways responding to this stress. Although all three metals are known to be genotoxic, evidence for DNA damage in our study only exists in response to chromium. Nickel induced a hypoxic response as well as inducing genes involved in chromatin structure, perhaps by replacing iron in key proteins. Cadmium distinctly perturbed genes related to endoplasmic reticulum stress and invoked the unfolded protein response leading to apoptosis. With these studies, we have completed the first gene expression comparative analysis of nickel, cadmium, and chromium in H4-II-E-C3 cells.

Effect of nickel and chromium exposure on buccal cells of electroplaters.

Science.gov (United States)

Qayyum, Saba; Ara, Anjum; Usmani, Jawed Ahmad

2012-02-01

The electroplating industry commonly involves the use of nickel and chromium. An assessment of the genotoxic effects of these metals can be carried out by micronucleus (MN) test in buccal cells. Other nuclear anomalies (NA) observed in buccal cells viz., karyorrhexis, pyknosis and karyolysis are also the indicators of genotoxicity. The current study aims at determining the extent of genotoxic damage in relation to the duration of exposure to nickel and hexavalent chromium via micronuclei induction and other nuclear anomalies. The present investigation included 150 subjects of which 50 individuals with no history of nickel/chromium exposure (Group I) were taken as control, 50 electroplaters exposed to nickel and hexavalent chromium for duration of less than 10 years (Group II) and 50 electroplaters exposed for ≥10 years (Group III) were included. Slides of buccal cells were prepared and the frequency of MN (‰) and NA (‰) were calculated. ANOVA was applied to test significance. Results were considered significant at p exposure increased. Plasma nickel and chromium levels were also determined which showed a positive correlation with frequency MN and other nuclear abnormalities (p < 0.01).

Bioaccumulation of chromium and nickel in the tissues of Barb us ...

African Journals Online (AJOL)

1996-04-25

Apr 25, 1996 ... S, marequensis suggested no serious chromium or nickel pollution in the study area. "To \\~hom . ... The toxicity of chromium and nickel to fish, as individual elements, is ..... its fitness for human consumption). One should also ...

Chromium, Nickel and Zinc Levels from Canned and Non-Canned ...

African Journals Online (AJOL)

Heavy metals (Chromium, Nickel and Zinc) were determined from both canned and non-canned beverages sold in Samaru, Zaria, Kaduna State, Nigeria. Concentration of Chromium was found to range from 0.528 - 1.509mg/L for canned and 0.176 - 1.358mg/L for non-canned beverages, Nickel concentration was found to ...

Nickel-chromium-silicon brazing filler metal

Science.gov (United States)

Martini, Angelo J.; Gourley, Bruce R.

1976-01-01

A brazing filler metal containing, by weight percent, 23-35% chromium, 9-12% silicon, a maximum of 0.15% carbon, and the remainder nickel. The maximum amount of elements other than those noted above is 1.00%.

Investigation of alternative phosphating treatments for nickel and hexavalent chromium elimination

International Nuclear Information System (INIS)

Jazbinsek, Luiz Antonio Rossi

2014-01-01

The phosphating processes are widely used in industry as surface treatments for metals, especially for low thickness plates, improving the adhesion between the metallic surface and the paint coating, and increasing the durability of paint systems against corrosion attacks. The tricationic phosphates containing zinc, nickel and manganese are commonly applied on steel. There is much discussion about the replacement of nickel by another element in order to have an environmentally friendly phosphating process. Niobium as a replacement for nickel has been evaluated. The most significant environmental impacts of phosphating processes are related to the presence of nickel and hexavalent chromium used in the process, this last as a passivation treatment. Nickel and hexavalent chromium are harmful to human and environment leading to contamination of water and soil. In the present study phosphate layers containing zinc, manganese and niobium have been evaluated and characterized on galvanized steel, and the results were compared with phosphates containing zinc, manganese and nickel, or a bicationic phosphate layer with zinc and manganese. Although the use of hexavalent chromium is not recommended worldwide, it is still used in processes for sealing the porosity of phosphate layers. This element is carcinogenic and has been associated with various diseases. Due to the passivation characteristics of niobium, this study also evaluated the tricationic bath containing niobium ammonium oxalate as a passivation treatment. The results showed that it could act as a replacement for the hexavalent chromium. The results of the present study showed that formulations containing niobium are potential replacements for hexavalent chromium and similar corrosion protection was obtained for the phosphate containing nickel or that with niobium. The morphology observed by scanning electron microscopy, gravimetric tests, porosity and adhesion evaluation results indicated that the phosphate

Stainless Steel Leaches Nickel and Chromium into Foods During Cooking

OpenAIRE

Kamerud, Kristin L.; Hobbie, Kevin A.; Anderson, Kim A.

2013-01-01

Toxicological studies show that oral doses of nickel and chromium can cause cutaneous adverse reactions such as dermatitis. Additional dietary sources, such as leaching from stainless steel cookware during food preparation, are not well characterized. This study examined stainless steel grades, cooking time, repetitive cooking cycles, and multiple types of tomato sauces for their effects on nickel and chromium leaching. Trials included three types of stainless steels and a stainless steel sau...

Separation of valence forms of chromium(III) and chromium(VI) by coprecipitation with iron(III) hydroxide

International Nuclear Information System (INIS)

Nazirmadov, B.; Khamidov, B.O.; Egorova, L.A.

1989-01-01

The sorption of 9.62·10 -5 M of Cr (III) and Cr (VI) with iron hydroxide in 1 M potassium nitrate and potassium chloride was investigated in relation to the pH of the medium. Experimental data on the sorption of chromium(III) and chromium(VI) with iron(III) hydroxide made it possible to determine the region of practically complete concentration of Cr (III) and Cr (VI) (pH = 3-6.5). The results from spectrophotometric investigations, calculated data on the distribution of the hydroxocationic forms of chromium(III) and the anions of chromium(IV), and their sorption by iron-(III) hydroxide made it possible to characterize the sorbability of the cationic and anionic forms of chromium in various degrees of oxidation. On this basis a method was developed for the separation of chromium(III) and chromium(VI) by coprecipitation on iron(III) hydroxide and their separation from the iron(III) hydroxide support

Kinetics of chromium (VI) reduction by ferrous iron

International Nuclear Information System (INIS)

Batchelor, B.; Schlautman, M.; Hwang, I.; Wang, R.

1998-09-01

Chromium is a primary inorganic contaminant of concern at the Pantex Plant. Chromium concentrations have been found to be two orders of magnitude higher than the drinking water standards, particularly in certain wells in the perched aquifer below Zone 12. In situ reduction of a mobile form of chromium, Cr(VI) to an immobile form, Cr(III), was examined as a viable option to active soil restoration. Successfully immobilizing chromium in the vadose zone as Cr(III) will reduce the amount of chromium that reaches the groundwater table. The results from the solution experiments indicated that chromium was rapidly and stoichiometrically reduced by Fe(II) in solution. Also, the slurry experiments showed that the aquifer solids removed Fe(II) from solution, but a portion of the iron removed remained available for reaction with Cr(VI), but at a slower rate. A model to predict different amounts of iron pseudo-components was developed, which allowed prediction of iron amounts required to reduce chromium under in situ conditions

Biodegradation of nickel and chromium from space maintainers: An in vitro study

Directory of Open Access Journals (Sweden)

Bhaskar V

2010-03-01

Full Text Available Band materials are often used in the practice of pediatric dentistry. Nickel and Chromium are the main ingredients of these materials. The potential health hazards of nickel and chromium and their compounds have been the focus of attention for more than 100 years. It has established that these metals could cause hypersensitivity. The study was undertaken to analyze in vitro biodegradation of space maintainers made out of stainless steel band materials from manufacturers Dentaurum and Unitek. The leaching effect simulating the use of one, two, three, and four space maintainers in clinical practice was studied by keeping the respective number of space maintainers in the artificial saliva incubating at 37°C and analyzing for nickel and chromium release after 1,7,14,21 and 28 days using atomic absorption spectrophotometer. Results showed that there was measurable release of both nickel and chromium which reached maximum level at the end of 7 days which was statistically significant (P < 0.05 and was very much below the dietary average intake even for four bands used and was not capable of causing any toxicity.

Chromium, Nickel and Zinc Induced Histopathological Alterations in ...

African Journals Online (AJOL)

Michael Horsfall

fish, Labeo rohita to chlorides of chromium, nickel and zinc for 30 days. However ... toxicants such as salts of heavy metals, acids, organic matter ... nutritional supply becomes excessive. ... action), petrochemicals, and fertilizers and in steam.

Influence of Chromium and Molybdenum on the Corrosion of Nickel Based Alloys

International Nuclear Information System (INIS)

Hayes, J R; Gray, J; Szmodis, A W; Orme, C A

2005-01-01

The addition of chromium and molybdenum to nickel creates alloys with exceptional corrosion resistance in a diverse range of environments. This study examines the complementary roles of Cr and Mo in Ni alloy passivation. Four nickel alloys with varying amounts of chromium and molybdenum were studied in 1 molar salt solutions over a broad pH range. The passive corrosion and breakdown behavior of the alloys suggests that chromium is the primary element influencing general corrosion resistance. The breakdown potential was nearly independent of molybdenum content, while the repassivation potential is strongly dependant on the molybdenum content. This indicates that chromium plays a strong role in maintaining the passivity of the alloy, while molybdenum acts to stabilize the passive film after a localized breakdown event

Separation of valent forms of chromium (3) and chromium (6) by coprecipitation with iron (3) hydroxide

International Nuclear Information System (INIS)

Nazirmadov, B.; Khamidov, B.O.; Egorova, L.A.

1988-01-01

Soption 9.62x10 -5 mol/l of 51 Cr radioactive isotope in oxidation states 3 and 6 by iron(3) hydroxide in 1 mol/l of KNO 3 and KCl depending on pH medium is investigated. The region of practically total concentration of Cr(3) and Cr(6 + ) (pH=3-6.5) is determined. The results of spectrophotometric investigations, calculational data on distribution of hydroxocation forms of chromium (3) and of chromium (6) anions and sorption by iron (3) hydroxide permit to characterize sorption of chromium forms in different stages of oxidation. The methods of chromium (3) and chromium (6) separation by coprecipitation of iron (3) hydroxide and their precipitation from it is developed on the above foundation

Dietary chromium and nickel enhance UV-carcinogenesis in skin of hairless mice

International Nuclear Information System (INIS)

Uddin, Ahmed N.; Burns, Fredric J.; Rossman, Toby G.; Chen, Haobin; Kluz, Thomas; Costa, Max

2007-01-01

The skin cancer enhancing effect of chromium (in male mice) and nickel in UVR-irradiated female Skh1 mice was investigated. The dietary vitamin E and selenomethionine were tested for prevention of chromium-enhanced skin carcinogenesis. The mice were exposed to UVR (1.0 kJ/m 2 3x weekly) for 26 weeks either alone, or combined with 2.5 or 5.0 ppm potassium chromate, or with 20, 100 or 500 ppm nickel chloride in drinking water. Vitamin E or selenomethionine was added to the lab chow for 29 weeks beginning 3 weeks before the start of UVR exposure. Both chromium and nickel significantly increased the UVR-induced skin cancer yield in mice. In male Skh1 mice, UVR alone induced 1.9 ± 0.4 cancers/mouse, and 2.5 or 5.0 ppm potassium chromate added to drinking water increased the yields to 5.9 ± 0.8 and 8.6 ± 0.9 cancers/mouse, respectively. In female Skh1 mice, UVR alone induced 1.7 ± 0.4 cancers/mouse, and the addition of 20, 100 or 500 ppm nickel chloride increased the yields to 2.8 ± 0.9, 5.6 ± 0.7 and 4.2 ± 1.0 cancers/mouse, respectively. Neither vitamin E nor selenomethionine reduced the cancer yield enhancement by chromium. These results confirm that chromium and nickel, while not good skin carcinogens per se, are enhancers of UVR-induced skin cancers in Skh1 mice. Data also suggest that the enhancement of UVR-induced skin cancers by chromate may not be oxidatively mediated since the antioxidant vitamin E as well as selenomethionine, found to prevent arsenite-enhanced skin carcinogenesis, failed to suppress enhancement by chromate

Analysis of molybdenum, chromium, vanadium and iron by polarographic techniques

International Nuclear Information System (INIS)

Al-Zand, T.K.

1986-01-01

The application of direct current Tast polarograph, differential pulse polarography and phase-selective alternative current Tast polarography to the problem of determining molybdenum, chromium, vanadium and iron in various supporting electrolytes is reported. The effect of the supporting electrolyte on the wave/peak potential and sensitivity of the metal ion have been examined. The polarographic methods were applied for simultaneous determination of chromium (3)/chromium (6), vanadium (4), vanadium (5) and iron (2)/iron (3) in different supporting electrolytes

Chromium effect on the Young modulus and thermoelastic coefficient of elinvars

International Nuclear Information System (INIS)

Sazykina, A.V.; Khomenko, O.A.

1976-01-01

The effect was studied of thermal and thermal-mechanical treatment upon the elastic modules and its temperature coefficient in iron-nickel Elinvars with different chromium contents (from 0 to 6.7%). It has been shown that doping with chromium results in an increase in the modulus of elasticity of Elinvars after hardening. The elastic modulus of alloys containing no chromium increases after a cold plastic deformation (drawing), whereas that of chromous Elinvars decreases upon such a treatment. It has been established that the elastic modulus of hardened and cold drawn after hardening Elinvars increases upon ageing. An increase in chromium content in iron-nickel Elinvars reduces the effect of the temperature of ageing upon the thermoelastic coefficient during the usual heat treatment and the thermalmechanical treatment and lowers its sensitivity to the influence of an external magnetic field [ru

Crystallization and structure of chromium cast iron with addition of Mo and Ni; Krystalizacja i struktura zeliwa chromowego z dodatkami Mo i Ni

Energy Technology Data Exchange (ETDEWEB)

Pietrowski, S. [Instytut Inzynierii Materialowej i Technik Bezwiorowych, Politechnika Lodzka, Lodz (Poland)

1998-12-31

The aim of the presented paper is to show the results of examination of the crystallization process using the method of thermal-derivative analysis (ATD) and the structure examination of chromium cast iron, chromium molybdenum c. i. and chromium molybdenum nickel c.i. It was found that molybdenum in amount over 2 wt % causes the crystallization of eutectic carbides M{sub 23}C{sub 6} and M{sub 6}C. The M{sub 23}C{sub 6} carbide crystallizes upon the crystallization of eutectic carbides M{sub 3}C and M{sub 7}C{sub 3}. It is shown that ATD method facilitates both interpretation and control of the crystallization as well as formation of the cast iron structure at the solid state. (author) 14 refs, 16 figs, 5 tabs

Comparison of chromium and nickel uptake of plants grown in different soils

Energy Technology Data Exchange (ETDEWEB)

Vago, I. [University of Agriculture, Faculty of Agronomy, H-4015 Debrecen, P.O. Box 36 (Hungary); Gyoeri, Z. [University of Agriculture, Faculty of Agronomy, H-4015 Debrecen, P.O. Box 36 (Hungary); Loch, J. [University of Agriculture, Faculty of Agronomy, H-4015 Debrecen, P.O. Box 36 (Hungary)

1996-03-01

The chromium and nickel uptake of ryegrass has been examined in pot experiments in extremely different soils, poor sandy and fertile black chernozem. The effect of calcium carbonate doses and nitrogen supply on heavy metal uptake of the plant has been studied for chromium and nickel loadings (0-100 mg/kg Cr{sup 3+} or Ni{sup 2+}) applied as inorganic salts. The ability to uptake Cr{sup 3+} and Ni{sup 2+} differs significantly and is highly affected by the characteristics of soils, and depends on the metal investigated. The heavy metal uptake of the plant differs significantly in acid, colloid deficient sandy soils; while artificial chromium contamination did not modify the dry-matter production in the pots in either soil, a large quantity of nickel reduced the yields significantly. Nitrogen application did not change significantly the uptake of heavy metals. Lime application reduced the Ni{sup 2+} uptake of plants considerably, especially in sandy soil. In case of a calcium carbonate addition the dry-matter production of the plant was not affected by nickel. In chernozem soil the effect of lime application - i.e., the reduction of nickel uptake - was of a lesser degree. The significantly lesser Cr{sup 3+} uptake was further limited by a calcium carbonate application for both soils studied. A graphic presentation of these effects is given. (orig.). With 3 figs., 3 tabs.

[The effect of hydrogen peroxide on the electrochemical corrosion properties and metal ions release of nickel-chromium dental alloys].

Science.gov (United States)

Wang, Jue; Qiao, Guang-yan

2013-04-01

To investigate the effect of hydrogen peroxide on the electrochemical corrosion and metal ions release of nickel-chromium dental alloys. The corrosion resistance of nickel-chromium dental alloys was compared by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization curve (PD) methods in artificial saliva after immersed in different concentrations of hydrogen peroxide for 112 h. The metal ions released from nickel-chromium dental alloys to the artificial saliva were detected after electrochemical measurements using inductively coupled plasma mass spectrometry (ICP-MS). The data was statistically analyzed by analysis of variance (ANOVA) using SPSS 13.0 software package. The electrochemical experiment showed that the sequence of polarization resistance in equivalent circuit (Rct), corrosion potential (Ecorr), pitting breakdown potential (Eb), and the difference between Ecorr and Eb representing the "pseudo-passivation" (δE) of nickel-chromium alloys in artificial saliva was 30% alloys to the artificial saliva, and the order of the concentrations of metal ions was 0% corrosion resistance of nickel-chromium dental alloys decrease after immersed in different concentrations of hydrogen peroxide for 112 h. Nickel-chromium dental alloys are more prone to corrosion in the artificial saliva with the concentration of hydrogen peroxide increased, and more metal ions are released in the artificial saliva.

Nickel - iron battery. Nikkel - jern batteri

Energy Technology Data Exchange (ETDEWEB)

Petersen, H. A.

1989-03-15

A newer type of nickel-iron battery, (SAFT 6v 230 Ah monobloc), which could possibly be used in relation to electrically driven light road vehicles, was tested. The same test methods used for lead batteries were utilized and results compared favourably with those reached during other testings carried out, abroad, on a SAFT nickle-iron battery and a SAB-NIFE nickel-iron battery. Description (in English) of the latter-named tests are included in the publication as is also a presentation of the SAFT battery. Testing showed that this type of battery did not last as long as had been expected, but the density of energy and effect was superior to lead batteries. However energy efficiency was rather poor in comparison to lead batteries and it was concluded that nickel-iron batteries are not suitable for stationary systems where recharging under a constant voltage is necessary. (AB).

Swelling of austenitic iron-nickelchromium ternary alloys during fast neutron irradiation

International Nuclear Information System (INIS)

Garner, F.A.; Brager, H.R.

1984-01-01

Swelling data are now available for 15 iron-nickel-chromium ternary alloys irradiated to exposures as high as 110 displacements per atom (dpa) in Experimental Breeder Reactor-II (EBR-II) between 400 and 650 0 C. These data confirm trends observed at lower exposure levels and extend the generality of earlier conclusions to cover a broader range of composition and temperature. It appears that all austenitic iron-nickel-chromium ternary alloys eventually approach an intrinsic swelling rate of about1%/dpa over a range of temperature even wider than studied in this experiment. The duration of the transient regime that precedes the attainment of this rate is quite sensitive to nickel and chromium content, however. At nickel and chromium levels typical of 300 series steels, swelling does not saturate at engineering-relevant levels. However, there appears to be a tendency toward saturation that increases with declining temperature, increasing nickel and decreasing chromium levels. Comparisons of these results are made with those of similar studies conducted with charged particles. Conclusions are then drawn concerning the validity of charged particle simulation studies to determine the compositional and temperature dependence of swelling

Improvement in mechanical properties of chromium-nickel sintered compacts by repeated rolling and annealing; Kuromu nickel shoketsuzai no kurikaeshi atsuen shodon ni yoru kikaiteki seishitsu no kaizen

Energy Technology Data Exchange (ETDEWEB)

Harada, Y. [Toyohashi University of Technology, Aichi (Japan); Omori, M. [Hiroshima-Denki Institute of Technology, Hiroshima (Japan); Ando, H. [Nippon Steel Glass Co. Ltd., Tokyo (Japan); Matsui, H. [Tadano Ltd., Kagawa (Japan); Okita, T. [Honda R and D Co. Ltd., Tokyo (Japan)

1998-09-20

Chromium-nickel sintered compacts containing 50 and 80 mass%Cr were tried to improve their mechanical properties by means of a thermo-mechanical treatment, i.e., repeated rolling and annealing. Specimens from the as-sintered compacts showed no ductility at room temperature and small ductility at temperatures higher than 1000 K because of poor alloying of nickel with chromium. Tensile properties of the sheets repeatedly rolled with the intermediate annealing at 1173 K were very similar to those of the as-sintered specimen. While the sheets rolled with the annealing at 1573 K were excellently improved in their strength and ductility due to the considerable interdiffusion of chromium and nickel. The intermediate temperature embrittlement, that is, the ductility minimum well observed around 1000 K in a chromium-nickel alloy appeared also in the sheets rolled with the annealing at 1573 K. 15 refs., 13 figs., 1 tab.

Stainless steel leaches nickel and chromium into foods during cooking.

Science.gov (United States)

Kamerud, Kristin L; Hobbie, Kevin A; Anderson, Kim A

2013-10-02

Toxicological studies show that oral doses of nickel and chromium can cause cutaneous adverse reactions such as dermatitis. Additional dietary sources, such as leaching from stainless steel cookware during food preparation, are not well characterized. This study examined stainless steel grades, cooking time, repetitive cooking cycles, and multiple types of tomato sauces for their effects on nickel and chromium leaching. Trials included three types of stainless steels and a stainless steel saucepan, cooking times of 2-20 h, 10 consecutive cooking cycles, and four commercial tomato sauces. After a simulated cooking process, samples were analyzed by ICP-MS for Ni and Cr. After 6 h of cooking, Ni and Cr concentrations in tomato sauce increased up to 26- and 7-fold, respectively, depending on the grade of stainless steel. Longer cooking durations resulted in additional increases in metal leaching, where Ni concentrations increased 34-fold and Cr increased approximately 35-fold from sauces cooked without stainless steel. Cooking with new stainless steel resulted in the largest increases. Metal leaching decreases with sequential cooking cycles and stabilized after the sixth cooking cycle, although significant metal contributions to foods were still observed. The tenth cooking cycle resulted in an average of 88 μg of Ni and 86 μg of Cr leached per 126 g serving of tomato sauce. Stainless steel cookware can be an overlooked source of nickel and chromium, where the contribution is dependent on stainless steel grade, cooking time, and cookware usage.

Stainless Steel Leaches Nickel and Chromium into Foods During Cooking

Science.gov (United States)

Kamerud, Kristin L.; Hobbie, Kevin A.; Anderson, Kim A.

2014-01-01

Toxicological studies show that oral doses of nickel and chromium can cause cutaneous adverse reactions such as dermatitis. Additional dietary sources, such as leaching from stainless steel cookware during food preparation, are not well characterized. This study examined stainless steel grades, cooking time, repetitive cooking cycles, and multiple types of tomato sauces for their effects on nickel and chromium leaching. Trials included three types of stainless steels and a stainless steel saucepan; cooking times of 2 to 20 hours, ten consecutive cooking cycles, and four commercial tomato sauces. After a simulated cooking process, samples were analyzed by ICP-MS for Ni and Cr. After six hours of cooking, Ni and Cr concentrations in tomato sauce increased up to 26- and 7-fold respectively, depending on the grade of stainless steel. Longer cooking durations resulted in additional increases in metal leaching, where Ni concentrations increased 34 fold and Cr increased approximately 35 fold from sauces cooked without stainless steel. Cooking with new stainless steel resulted in the largest increases. Metal leaching decreases with sequential cooking cycles and stabilized after the sixth cooking cycle, though significant metal contributions to foods were still observed. The tenth cooking cycle, resulted in an average of 88 μg of Ni and 86 μg of Cr leached per 126 g serving of tomato sauce. Stainless steel cookware can be an overlooked source of nickel and chromium, where the contribution is dependent on stainless steel grade, cooking time, and cookware usage. PMID:23984718

Biosorption characteristics of copper (II), chromium (III), nickel (II), and lead (II) from aqueous solutions by Chara sp. and Cladophora sp.

Science.gov (United States)

Elmaci, Ayşe; Yonar, Taner; Ozengin, Nihan

2007-09-01

The aim of this research was to expose individual removals of copper, chromium, nickel, and lead from aqueous solutions via biosorption using nonliving algae species, Chara sp. and Cladophora sp. Optimum pH values for biosorption of copper (II), chromium (III), nickel (II), and lead (II) from aqueous solutions were determined to be 6, 7, 7, and 3 for Cladophora sp. and 5, 3, 5, and 4 for Chara sp. respectively. Maximum adsorption capacities of Chara sp. [10.54 for chromium (III) and 61.72 for lead (II)] and Cladophora sp. [6.59 for chromium (III) and 16.75 and 23.25 for lead (II)] for chromium (III) and lead (II) are similar. On the other hand, copper (II) and nickel (II) biosorption capacity of Cladophora sp. [14.28 for copper (II) and 16.75 for nickel (II)] is greater than Chara sp. [6.506 for copper (II) and 11.76 for nickel (II)]. Significantly high correlation coefficients indicated for the Langmuir adsorption isotherm models can be used to describe the equilibrium behavior of copper, chromium, nickel, and lead adsorption onto Cladophora sp. and Chara sp.

Evaluation of Beryllium, Total Chromium and Nickel in the Surface Contaminant Layer Available for Dermal Exposure After Abrasive Blasting in a Shipyard

Science.gov (United States)

2013-04-24

workers are potentially exposed to metals including cadmium, chromium, beryllium, iron, lead, nickel, tin, zinc and copper (43). 2 Potential worker...identified in the breathing zone air samples at Portsmouth NSY, coal slag was the abrasive in use. Within Portsmouth NSY, there are two main areas...where coal slag is used for blasting: the dry docks for blasting of submarines and in Building 286. Building 286 is a large bay room building where

Advanced STEM/EDX investigation on an oxide scale thermally grown on a high-chromium iron–nickel alloy under very low oxygen partial pressure

International Nuclear Information System (INIS)

Latu-Romain, L.; Madi, Y.; Mathieu, S.; Robaut, F.; Petit, J.-P.; Wouters, Y.

2015-01-01

Highlights: • A scale grown on a high-chromium iron–nickel alloy under low oxygen partial pressure was studied. • STEM-EDX maps at high resolution on a transversal thin lamella have been conducted. • The real complexity of the oxide layer has been highlighted. • These results explain the elevated number of semiconducting contributions. - Abstract: A thermal oxide scale has been grown on a high-chromium iron-nickel alloy under very low oxygen partial pressure (1050 °C, 10"−"1"0 Pa). In this paper, a special attention has been paid to morphological and chemical characterizations of the scale by scanning transmission electron microscopy and energy dispersive X-ray analysis at high resolution on a cross-section thin lamella beforehand prepared by using a combined focused ion beam/scanning electron microscope instrument. The complexity of the oxide layer is highlighted, and the correlation between the present results and the ones of a photoelectrochemical study is discussed.

Nickel decreases cellular iron level and converts cytosolic aconitase to iron-regulatory protein 1 in A549 cells

International Nuclear Information System (INIS)

Chen Haobin; Davidson, Todd; Singleton, Steven; Garrick, Michael D.; Costa, Max

2005-01-01

Nickel (Ni) compounds are well-established carcinogens and are known to initiate a hypoxic response in cells via the stabilization and transactivation of hypoxia-inducible factor-1 alpha (HIF-1α). This change may be the consequence of nickel's interference with the function of several Fe(II)-dependent enzymes. In this study, the effects of soluble nickel exposure on cellular iron homeostasis were investigated. Nickel treatment decreased both mitochondrial and cytosolic aconitase (c-aconitase) activity in A549 cells. Cytosolic aconitase was converted to iron-regulatory protein 1, a form critical for the regulation of cellular iron homeostasis. The increased activity of iron-regulatory protein 1 after nickel exposure stabilized and increased transferrin receptor (Tfr) mRNA and antagonized the iron-induced ferritin light chain protein synthesis. The decrease of aconitase activity after nickel treatment reflected neither direct interference with aconitase function nor obstruction of [4Fe-4S] cluster reconstitution by nickel. Exposure of A549 cells to soluble nickel decreased total cellular iron by about 40%, a decrease that likely caused the observed decrease in aconitase activity and the increase of iron-regulatory protein 1 activity. Iron treatment reversed the effect of nickel on cytosolic aconitase and iron-regulatory protein 1. To assess the mechanism for the observed effects, human embryonic kidney (HEK) cells over expressing divalent metal transporter-1 (DMT1) were compared to A549 cells expressing only endogenous transporters for inhibition of iron uptake by nickel. The inhibition data suggest that nickel can enter via DMT1 and compete with iron for entry into the cell. This disturbance of cellular iron homeostasis by nickel may have a great impact on the ability of the cell to regulate a variety of cell functions, as well as create a state of hypoxia in cells under normal oxygen tension. These effects may be very important in how nickel exerts phenotypic

The GENIALL process for generation of nickel-iron alloys from nickel ores or mattes

International Nuclear Information System (INIS)

Diaz, G.; Frias, C.; Palma, J.

2001-01-01

A new process, called GENIALL (acronym of Generation of Nickel Alloys), for nickel recovery as ferronickel alloys from ores or mattes without previous smelting is presented in this paper. Its core technology is a new electrolytic concept, the ROSEL cell, for electrowinning of nickel-iron alloys from concentrated chloride solutions. In the GENIALL Process the substitution of iron-based solid wastes as jarosite, goethite or hematite, by saleable ferronickel plates provides both economic and environmental attractiveness. Another advantage is that no associated sulfuric acid plant is required. The process starts with leaching of the raw material (ores or mattes) with a solution of ferric chloride. The leachate liquor is purified by conventional methods like cementation or solvent extraction, to remove impurities or separate by-products like copper and cobalt. The purified solution, that contains a mixture of ferrous and nickel chlorides is fed to the cathodic compartment of the electrowinning cell, where nickel and ferrous ions are reduced together to form an alloy. Simultaneously, ferrous chloride is oxidized to ferric chloride in the anodic compartment, from where it is recycled to the leaching stage. The new electrolytic equipment has been developed and scaled up from laboratory to pilot prototypes with commercial size electrodes of 1 m 2 . Process operating conditions have been established in continuous runs at bench and pilot plant scale. The technology has shown a remarkable capacity to produce nickel-iron alloys of a wide range of compositions, from 10% to 80% nickel, just by adjusting the operating parameters. This emerging technology could be implemented in many processes in which iron and other non-ferrous metals are harmful impurities to be removed, or valuable metals to be recovered as a marketable iron alloy. Other potential applications of this technology are regeneration of spent etching liquors, and iron removal from aqueous effluents. (author)

Electrodeposited tungsten-nickel-boron: A replacement for hexavalent chromium

International Nuclear Information System (INIS)

Steffani, C.; Meltzer, M.

1995-04-01

Chromium, deposited from acidic solutions of its hexavalent ion, has been the rule for wear resistant, corrosion resistant coatings for many years. Although chromium coatings are durable, the plating process generates air emissions, effluent rinse waters, and process solutions that are toxic, suspected carcinogens, and a risk to human health and the environment. Tungsten-nickel-boron (W-Ni-B) alloy deposition is a potential substitute for hexavalent chrome. It has excellent wear, corrosion, and mechanical properties and also may be less of an environmental risk. This study examines the electroplating process and deposit properties of W-Ni-B and compares them with those of hexavalent chrome

Influence of Chemical Composition on Rupture Properties at 1200 Degrees F. of Forged Chromium-Cobalt-Nickel-Iron Base Alloys in Solution-Treated and Aged Condition

Science.gov (United States)

Reynolds, E E; Freeman, J W; White, A E

1951-01-01

The influence of systematic variations of chemical composition on rupture properties at 1200 degrees F. was determined for 62 modifications of a basic alloy containing 20 percent chromium, 20 percent nickel, 20 percent cobalt, 3 percent molybdenum, 2 percent tungsten, 1 percent columbium, 0.15 percent carbon, 1.7 percent manganese, 0.5 percent silicon, 0.12 percent nitrogen and the balance iron. These modifications included individual variations of each of 10 elements present and simultaneous variations of molybdenum, tungsten, and columbium. Laboratory induction furnace heats were hot-forged to round bar stock, solution-treated at 2200 degrees F., and aged at 1400 degrees F. The melting and fabrication conditions were carefully controlled in order to minimize all variable effects on properties except chemical composition. Information is presented which indicates that melting and hot-working conditions play an important role in high-temperature properties of alloys of the type investigated.

Methods to Develop Inhalation Cancer Risk Estimates for Chromium and Nickel Compounds

Science.gov (United States)

This document summarizes the approaches and rationale for the technical and scientific considerations used to derive inhalation cancer risks for emissions of chromium and nickel compounds from electric utility steam generating units.

PARTITIONING OF THE REFRACTORY METALS, NICKEL AND CHROMIUM, IN COMBUSTION SYSTEMS

Science.gov (United States)

The partitioning of nickel (Ni) and Chromium (Cr) in combustion systems was investigated theoretically and experimentally. In comparison to other volatile and semi-volatile metals, both Ni and Cr are usually considered to be refractory (non-volatile). Theoretical predictions ba...

Theromdynamics of carbon in nickel-based multicomponent solid solutions

International Nuclear Information System (INIS)

Bradley, D.J.

1978-04-01

The activity coefficient of carbon in nickel, nickel-titanium, nickel-titanium-chromium, nickel-titanium-molybdenum and nickel-titanium-molybdenum-chromium alloys has been measured at 900, 1100 and 1215 0 C. The results indicate that carbon obeys Henry's Law over the range studied (0 to 2 at. percent). The literature for the nickel-carbon and iron-carbon systems are reviewed and corrected. For the activity of carbon in iron as a function of composition, a new relationship based on re-evaluation of the thermodynamics of the CO/CO 2 equilibrium is proposed. Calculations using this relationship reproduce the data to within 2.5 percent, but the accuracy of the calibrating standards used by many investigators to analyze for carbon is at best 5 percent. This explains the lack of agreement between the many precise sets of data. The values of the activity coefficient of carbon in the various solid solutions are used to calculate a set of parameters for the Kohler-Kaufman equation. The calculations indicate that binary interaction energies are not sufficient to describe the thermodynamics of carbon in some of the nickel-based solid solutions. The results of previous workers for carbon in nickel-iron alloys are completely described by inclusion of ternary terms in the Kohler-Kaufman equation. Most of the carbon solid solution at high temperatures in nickel and nickel-titantium alloys precipitates from solution on quenching in water. The precipitate is composed of very small particles (greater than 2.5 nm) of elemental carbon. The results of some preliminary thermomigration experiments are discussed and recommendations for further work are presented

[The effect of epigallocatechin gallate (EGCG) on the surface properties of nickel-chromium dental casting alloys after electrochemical corrosion].

Science.gov (United States)

Qiao, Guang-yan; Zhang, Li-xia; Wang, Jue; Shen, Qing-ping; Su, Jian-sheng

2014-08-01

To investigate the effect of epigallocatechin gallate (EGCG) on the surface properties of nickel-chromium dental alloys after electrochemical corrosion. The surface morphology and surface structure of nickel-chromium dental alloys were examined by stereomicroscope and scanning electron microscopy before and after electrochemical tests in 0 g/L and 1.0 g/L EGCG artificial saliva. The surface element component and chemical states of nickel-chromium dental alloys were analyzed by X-ray photoelectron spectrograph after electrochemical tests in 0 g/L and 1.0 g/L EGCG artificial saliva. More serious corrosion happened on the surface of nickel-chromium alloy in 1.0 g/L EGCG artificial saliva than in 0 g/L EGCG. The diameters of corrosion pits were smaller, and the dendrite structure of the alloy surface was not affected in 0 g/L EGCG. While the diameters of corrosion pits were larger, the dendritic interval of the alloy surface began to merge, and the dendrite structure was fuzzy in 1.0 g/L EGCG. In addition, the O, Ni, Cr, Be, C and Mo elements were detected on the surface of nickel-chromium alloys after sputtered for 120 s in 0 g/L EGCG and 1.0 g/L EGCG artificial saliva after electrochemical corrosion, and the surface oxides were mainly NiO and Cr(2)O(3). Compared with 0 g/L EGCG artificial saliva, the content of O, NiO and Cr(2)O(3) were lower in 1.0 g/L EGCG. The results of surface morphology and the corrosion products both show that the corrosion resistance of nickel-chromium alloys become worse and the oxide content of corrosion products on the surface reduce in 1.0 g/L EGCG artificial saliva.

Estimation of Release of Nickel and Chromium by Indian Made Orthodontic Appliance in Saliva.

Science.gov (United States)

Parashar, Sandeep; Maurya, Rajkumar; Gupta, Ankur; Hegde, Chatura; Anand, Neelima

2015-09-01

With increasing use of Indian made orthodontic materials, need was felt to know nickel and chromium release from these material. This study was conducted on simulated appliances consisting of brackets (022″Roth, Modern orthodontics, Ludhiana, India), from second premolar to central incisor, buccal tube and 0.019×0.025- inch SS arch wires secured with SS ligatures. Immersion was done in artificial saliva. Samples were analysed to using Atomic Absorption Photospectrometer (GVC ScientificEquipment Pvt. Ltd Australia) at AES Laboratories (P) Ltd., Noida India on 1(st), 7(th), 14(th) and 28(th) day. SPSS (ver 17, Inc., Chicago, Illinois, USA) was used toperform the statistical analysis. Descriptive statistics i.e. median and 25 and75 percentiles were used. Peak nickel release was on 7(th) day and subsequently declined over 14(th) and 28(th) day. The peak level of chromium concentration was on 14(th) day, which declined thereafter. Average daily release of nickel and chromium over a period of one month was 97.368 μg/day and 47.664 μg/day respectively. The estimated release rates were approximately 32% and 16% of the reported average daily dietary.

Corrosion of chromium, nickel, titanium and steels in solutions of sodium and ammonium thiosulfates

International Nuclear Information System (INIS)

Grebenshchikova, S.V.; Kochergin, V.P.; Doronina, I.V.

1983-01-01

Results of gravimetric determinatiion of average rate of chromium, nickel, titatnium and steels 12Kh18N10T and VSt.3 corrosion rate in solutions 50 mass.% (NH 4 ) 2 S 2 O 3 and Na 2 S 2 O 3 in the air and nitrogen atmosphere at 333 K have been generalized. Anodic polarization curves are recorded and stationary potentials of metals and steels under the conditions are measured. It is shown that in (NH 4 ) 2 S 2 O 3 solution the rate of metal and steels corrosion is higher than in Na 2 S 2 O 3 solution indepenent of the nature of gaseous medium contacting with solution. In the series Ni → VSt.3 → 12Kh18N10T → VT1 → chromium in (NH 4 ) 2 S 2 O 3 and Na 2 S 2 O 3 solutions at 333 K corrosion resistance increases. Chromium, titanium and chromium-nickel steel 12Kh18N10T possess a high corrosion resistance

Reduction Expansion Synthesis of Chromium and Nickel Metal Coatings

Science.gov (United States)

2017-06-01

Garth V. Hobson Chair, Department of Mechanical and Aerospace Engineering iv THIS PAGE INTENTIONALLY LEFT BLANK v ABSTRACT This thesis represents a...chromium and nickel coatings,” Plating and Surface Finishing, vol. 92, no. 4, pp. 42–48, Apr. 2005. [43] S. I. Sandler, Chemical and Engineering ...NAVAL POSTGRADUATE SCHOOL MONTEREY, CALIFORNIA THESIS Approved for public release. Distribution is unlimited. REDUCTION EXPANSION SYNTHESIS OF

Transpassive dissolution of alloy 625, chromium, nickel, and molybdenum in high-temperature solutions containing hydrochloric acid and oxygen

International Nuclear Information System (INIS)

Kritzer, P.; Boukis, N.; Dinjus, E.

2000-01-01

Coupons of nickel, molybdenum, chromium, and the nickel-based Alloy 625 (UNS 06625) were corroded in strongly oxidizing hydrochloric acid (HCl) solutions at 350 C and a pressure (p) of 24 MPa, with reaction times between 0.75 h and 50 h. For Alloy 625, the effect of surface roughness also was investigated. Nickel and molybdenum showed strong material loss after only 5 h of reaction as a result of the instability of the solid oxides formed under experimental conditions. The attack on chromium started at the grain boundaries. At longer reaction times, thick, spalling oxide layers formed on the surface. The attack on Alloy 625 also started at the grain boundaries and at inclusions leading to the formation of small pits. On polished surfaces, the growth of these pits occurred faster than on nonpolished surfaces, but fewer pits grew. Corrosion products formed at the surface consisted of oxygen and chromium. On isolated spots, nickel- and chlorine-containing products also were found

Effect of nickel and iron co-exposure on human lung cells

International Nuclear Information System (INIS)

Salnikow, Konstantin; Li Xiaomei; Lippmann, Morton

2004-01-01

Exposure to ambient air particulate matter (PM) is associated with increased mortality and morbidity in susceptible populations. The epidemiological data also suggest a relationship between PM air pollution and impairment of cardiopulmonary function. The mechanisms that may be responsible for these effects are not fully understood and are likely related to perturbations of cellular and molecular functions. One type of PM, residual oil fly ash (ROFA), is of particular interest. ROFA does not contain much organic material, but does contain relatively high quantities of transition metals, predominantly nickel, vanadium, and iron, as well as black carbon and sulfates. In this study, we investigated the effect of two metals (iron and nickel) on the induction of 'hypoxia-like' stress and the production of interleukins (ILs) in minimally transformed human airway epithelial cells (1HAEo - ). We found that exposure to soluble nickel sulfate results in the induction of hypoxia-inducible genes and IL-8 production by the 1HAEo - cells. The simultaneous addition of iron in either ferric or ferrous form and nickel completely inhibited IL-8 production and had no effect on 'hypoxia-like' stress caused by nickel, suggesting the existence of two different pathways for the induction 'hypoxia-like' stress and IL-8 production. The effect of nickel was not related to the blocking of iron entry into cells since the level of intracellular iron was not affected by co-exposure with nickel. The obtained data indicate that nickel can induce different signaling pathways with or without interference with iron metabolism. Our observations suggest that in some cases the excess of iron in PM can cancel the effects of nickel

Comparison of evaluated data for chromium-52, iron-56 and nickel-58 - International Evaluation Co-operation Volume 1

International Nuclear Information System (INIS)

Fu, C.Y.; Larson, Duane C.; Hetrick, David M.; Vonach, Herbert; Maino, G.; Menapace, Enzo; Mengoni, I.; Asami, T.; Chiba, Satoshi; Shibata, Keiichi Kanagawa; Iijima, S.; Yamamuro, N.; Kopecky, J.

1992-01-01

A Working Party on International Evaluation Co-operation was established under the sponsorship of the OECD/NEA Nuclear Science Committee (NSC) to promote the exchange of information on nuclear data evaluations, validation, and related topics. Its aim is also to provide a framework for co-operative activities between members of the major nuclear data evaluation projects. This includes the possible exchange of scientists in order to encourage co-operation. Requirements for experimental data resulting from this activity are compiled. The Working Party determines common criteria for evaluated nuclear data files with a view to assessing and improving the quality and completeness of evaluated data. The Parties to the project are: ENDF (United States), JEFF/EFF (NEA Data Bank Member countries), and JENDL (Japan). Co-operation with evaluation projects of non-OECD countries are organised through the Nuclear Data Section of the International Atomic Energy Agency (IAEA). This report is issued by a Subgroup investigating discrepancies in different evaluations of the major structural materials. The isotopes selected are Chromium-52, Iron-56 and Nickel-58. Graphical overlay comparisons between cross-sections, and also energy-angle correlated particle distributions, in different evaluated libraries was performed. Benefits from these comparisons include information useful for improving structural material evaluations in individual data libraries, for assessing differences associated with present-day evaluation techniques and for development of techniques for graphical representation of the energy-angle correlated data

High temperature dissolution of chromium substituted nickel ferrite in nitrilotriacetic acid medium

Energy Technology Data Exchange (ETDEWEB)

Sathyaseelan, V.S.; Chandramohan, P.; Velmurugan, S., E-mail: svelu@igcar.gov.in

2016-12-01

High temperature (HT) dissolution of chromium substituted nickel ferrite was carried out with relevance to the decontamination of nuclear reactors by way of chemical dissolution of contaminated corrosion product oxides present on stainless steel coolant circuit surfaces. Chromium substituted nickel ferrites of composition, NiFe{sub (2−x)}Cr{sub x}O{sub 4} (x ≤ 1), was synthetically prepared and characterized. HT dissolution of these oxides was carried out in nitrilotriacetic acid medium at 160 °C. Dissolution was remarkably increased at 160 °C when compared to at 85 °C in a reducing decontamination formulation. Complete dissolution could be achieved for the oxides with chromium content 0 and 0.2. Increasing the chromium content brought about a marked reduction in the dissolution rate. About 40 fold decrease in rate of dissolution was observed when chromium was increased from 0 to 1. The rate of dissolution was not very significantly reduced in the presence of N{sub 2}H{sub 4}. Dissolution of oxide was found to be stoichiometric. - Highlights: • Dissolution of NiFe{sub (2−x)}Cr{sub x}O{sub 4} was remarkably increased at 160 °C in NTA medium. • The dissolution was significantly decreasing with the increase in Cr content in the oxide. • Dissolution rate is dependent on the lability of metal-oxo bonds. • The rate of dissolution was not significantly reduced in the presence of N{sub 2}H{sub 4.} • NTA at high temperature is effective for decontamination of stainless steel surfaces.

Contribution to the study of the electrodeposition of iron-nickel alloys

International Nuclear Information System (INIS)

Valignat, J.

1968-01-01

Using a coulometric technique based upon the anodic intentiostatic dissolution, we studied the potentiostatic, deposition of nickel, iron and nickel iron alloys. We have shown that the minimum of the curve I = f (t) (deposition current versus time) is probably due to the transitory blocking of the surface by hydrogen and that the syn-crystallisation of nickel and iron is responsible for the anomalous co-deposition of these two elements. (author) [fr

Quantitative Assessment of Serum Nickel and Chromium Levels in Orthodontic Patients: An in vitro Study

Directory of Open Access Journals (Sweden)

Rohan Rai

2011-01-01

Results : Results obtained indicated that although nickel level in the serum was significant initially in the samples when compared to the controls, there was a gradual decrease of serum nickel level when the appliance was present for a longer duration. However, serum chromium levels showed no significant changes with time.

Comparison of chromium-51 and iron-59 for estimating erythrocyte survival in the cat

International Nuclear Information System (INIS)

Liddle, C.G.; Putnam, J.P.; Berman, E.; Fisher, H.; Ostby, J.

1984-01-01

Erythrocyte survival studies were conducted on eight normal, healthy, 1-year-old male specific-pathogen-free cats using both chromium-51 and iron-59 simultaneously. The chromium-51 procedure gave a half-life value of 11.1 +/- 0.9 days. This was considerably lower than would be expected on the basis of the experimentally determined iron-59 erythrocyte survival time of 51.2 +/- 14.9 days. The results of this study indicated that there was considerable loss of the chromium-51 label in the cat other than that from senescence alone. An analysis of the chromium-51 disappearance curve indicated that there were two exponential disappearance rates for the chromium-51 label and, in the absence of cell death, approximately 67% of the label was lost with a rate constant of 0.02 per day and 33% was lost with a rate constant of 0.1 per day. An equation is presented which models the loss of chromium-51 label which could be used to calculate erythrocyte survival from a chromium-51 disappearance curve. Blood volume measurements, hemograms, bone marrow differential results, and iron kinetic values also were determined and the results presented. While a reasonable approximation of the erythrocyte life span could be made by correcting the chromium-51 values for losses other than senescence, the iron-59 procedure would be the preferred method in cats

Thermodynamic studies of chromium adsorption on iron species generated by electrocoagulation

Energy Technology Data Exchange (ETDEWEB)

Parga, J.R.; Vazquez, V.; Gonzalez, G.; Cisneros, M.M. [Metallurgy and Materials Science Department, Institute Technology of Saltillo (Mexico)

2010-10-15

The protection of the global environment and in particular, the provision of a sustainable source of clean water is a necessity for human survival. Specifically, large quantities of chromium containing compounds are being discharged into the environment. This study has been carried out to determine the feasibility of chromium adsorption on iron species by an Electrocoagulation (EC) process using the Langmuir Isotherm. The full potential of EC with air injection as an alternative wastewater treatment technique to remove chromium from well water shows more than 99 % removal without the addition of any chemical reagents. In this study, X-Ray Diffraction, Scanning Electron Microscopy, Moessbauer Spectroscopy and Fourier Transform Infrared Spectroscopy are used to characterize the solid products that reveal the expected crystalline iron oxides, i.e., lepidocrocite, magnetite, gohetite, and iron oxide. (Abstract Copyright [2010], Wiley Periodicals, Inc.)

Heavy metal pollution among autoworkers. II. Cadmium, chromium, copper, manganese, and nickel

Energy Technology Data Exchange (ETDEWEB)

Clausen, J.; Rastogi, S.C.

1977-08-01

Garages and auto-repair workshops may be polluted with other heavy metals besides lead. Blood of autoworkers with high lead content was analyzed for cadmium, chromium, copper, manganese, nickel, ALAD activity and carboxyhaemoglobin level. Cadmium and copper levels in blood of autoworkers were comparable with those of the control subjects while chromium and nickel levels were significantly higher (P < 0.01 for both metals), and scattered raised values of manganese were found. There was no significant mutual correlation between levels of various heavy metals determined in whole blood. High copper levels were slightly related to decreasing ALAD activity (P < 0.1). Nineteen percent of autoworkers were found to have an abnormally high blood level of carboxyhemoglobin. The amount of particulate heavy metal in autoworkshop air was not related to biochemical abnormalities found in the autoworkers. Various sources of pollution of these heavy metals in autoworkshops are discussed.

Arsenic, chromium, copper, iron, manganese, lead, selenium and ...

African Journals Online (AJOL)

Arsenic, chromium, copper, iron, manganese, lead, selenium and zinc in the tissues of the largemouth yellowfish, Labeobarbus kimberleyensis (Gilchrist and Thompson, 1913), from the Vaal Dam, South Africa, and associated consumption risks.

Forgings made of austenitic chromium-nickel steels for the low temperature range

International Nuclear Information System (INIS)

Gruendler, O.; Schwarz, W.; Koren, M.

1981-01-01

The authors discuss the low temperature application of austenitic chromium-nickel steels for energy production and process techniques. Material requirements are presented, and the behaviour, mechanical and physical properties of such steels are discussed. The manufacture of forgings is considered and test results presented. (Auth.)

Forgings made of austenitic chromium-nickel steels for the low temperature range

Energy Technology Data Exchange (ETDEWEB)

Gruendler, O.; Schwarz, W.; Koren, M. (Vereinigte Edelstahlwerke A.G. (VEW), Kapfenberg (Austria))

1981-09-01

The authors discuss the low temperature application of austenitic chromium-nickel steels for energy production and process techniques. Material requirements are presented, and the behaviour, mechanical and physical properties of such steels are discussed. The manufacture of forgings is considered and test results presented.

Reduction of Hexavalent Chromium Using L-Cysteine Capped Nickel Nanocatalysts

Directory of Open Access Journals (Sweden)

Razium Ali Soomro

2013-06-01

Full Text Available The aim of this study was to reduce the highly toxic hexavalent chromium Cr(VI into less toxic chromium Cr(III species by using nickel nanoparticles (Ni NPs as catalysts in order to provide safety to the aqueous environment. In the first phase Ni NPs were synthesized in ethylene glycol and capped with l-cysteine by a modified microwave irradiation method using NaOH as the accelerator. The formed Ni NPs were characterized by various techniques such as UV-Visible spectroscopy, Fourier Transform Infra-red (FTIR spectroscopy and Scanning Electron Microscopy (SEM. In the second phase the formed Ni NPs were immobilized on glass surfaces and employed as catalyst for the reduction of Cr(VI ions. According to observations, 99% reduction of Cr(VI ions was achieved in the presence of 0.5 mg of Ni NPs catalyst in just five minutes as compared to nickel powder that showed only 16% reduction in 15 minutes. The study has a great impact on the aqueous pollution control of Cr(VI especially caused by the discharge of waste water from several industries utilizing Cr(VI containing salt as one of the essential gradients.

An in vitro comparison of nickel and chromium release from brackets

Directory of Open Access Journals (Sweden)

Ana Cristina Soares Santos Haddad

2009-12-01

Full Text Available This study aimed at comparing amounts of nickel (Ni and chromium (Cr released from brackets from different manufacturers in simulated oral environments. 280 brackets were equally divided into 7 groups according to manufacturer. 6 groups of brackets were stainless steel, and 1 group of brackets was made of a cobalt-chromium alloy with low Ni content (0.5%. International standard ISO 10271/2001 was applied to provide test methods. Each bracket was immersed in 0.5 ml of synthetic saliva (SS or artificial plaque fluid (PF over a period of 28 days at 37ºC. Solutions were replaced every 7 days, and were analyzed by spectrometry. The Kruskal-Wallis test was applied. Amounts of Ni release in SS (µg L-1 per week varied between groups from "bellow detection limits" to 694, and from 49 to 5,948.5 in PF. The group of brackets made of cobalt-chromium alloy, with the least nickel content, did not release the least amounts of Ni. Amounts of Cr detected in SS and in PF (µg L-1 per week were from 1 to 10.4 and from 50.5 to 8,225, respectively. It was therefore concluded that brackets from different manufacturers present different corrosion behavior. Further studies are necessary to determine clinical implications of the findings.

Comparison of nickel and chromium ions released from stainless steel and NiTi wires after immersion in Oral B®, Orthokin® and artificial saliva.

Science.gov (United States)

Jamilian, Abdolreza; Moghaddas, Omid; Toopchi, Shabnam; Perillo, Letizia

2014-07-01

Oral environment of the mouth is a suitable place for biodegradation of alloys used in orthodontic wires. The toxicity of these alloys namely nickel and chromium has concerned the researchers about the release of these ions from orthodontic wires and brackets. The aim of this study was to measure the levels of nickel and chromium ions released from 0.018" stainless steel (SS) and NiTi wires after immersion in three solutions. One hundred and forty-four round NiTi and 144 round SS archwires with the diameters of 0.018" were immersed in Oral B®, Orthokin® and artificial saliva. The amounts of nickel and chromium ions released were measured after 1, 6, 24 hours and 7 days. Two way repeated ANOVA showed that the amount of chromium and nickel significantly increased in all solutions during all time intervals (p nickel ions were released more in NiTi wire in all solutions compared with SS wire. The lowest increase rate was also seen in artificial saliva. There is general consensus in literature that even very little amounts of nickel and chromium are dangerous for human body specially when absorbed orally; therefore, knowing the precise amount of these ions released from different wires when immersed in different mouthwashes is of high priority.

Lung cancer mortality in nickel/chromium platers, 1946-95

OpenAIRE

Sorahan, T.; Burges, D. C.; Hamilton, L.; Harrington, J. M.

1998-01-01

OBJECTIVES: To investigate mortality from lung cancer in nickel/chromium platers. METHODS: The mortality experience of a cohort of 1762 chrome workers (812 men, 950 women) from a large electroplating and light engineering plant in the Midlands, United Kingdom, was investigated for the period 1946-95. All subjects were first employed in chrome work at the plant during the period 1946-75, and had at least six months employment in jobs associated with exposure to chromic acid mist (hexaval...

Cavitation erosion of chromium-manganese and chromium-cobalt coatings processed by laser beam

International Nuclear Information System (INIS)

Giren, B.G.; Szkodo, M.

2002-01-01

In this work the cavitation erosion of chromium-manganese and chromium-cobalt clads were tested, each of them for three cases: (1) without additional processing; (2) after laser heating of the solid state and (3) after laser remelting of the material. Armco iron, carbon steel 45 and chromium-nickel steel 0H18N9T were used as substrates. C.W. CO 2 laser with a beam power of 1000 W was used as a source of radiation. The investigated samples were subjected to cavitation impingement in a rotating disk facility. The results indicate that laser processing of the thick, electrode deposited coatings by laser beam leads in some cases to an increase of their cavitation resistance. Strong dependence of the coatings performance on the substrate, both for the laser processed or unprocessed parts of the materials was also discovered. (author)

Electrochemical removal of hexavalent chromium from wastewater using Platinum-Iron/Iron-carbon nanotubes and bipolar Electrodes

Directory of Open Access Journals (Sweden)

Hoshyar Hossini

2015-01-01

Full Text Available Background: In recent decades, electrocoagulation (EC has engrossed much attention as an environmental-friendly and effectiveness process. In addition, the EC process is a potential suitable way for treatment of wastewater with concern to costs and environment. The object of this study was electrochemical evaluation of chromium removal from industrial wastewater using Platinum and carbon nanotubes electrodes. Materials and Methods: The effect of key variables including pH (3–9, hexavalent chromium concentration (50–300 mg/l, supporting electrolyte (NaCl, KCl, Na2CO3 and KNO3 and its dosage, Oxidation-Reduction variations, sludge generation rate and current density (2–20 mA/cm2 was determined. Results: Based on experimental data, optimum conditions were determined in 20, 120 min, pH 3, NaCl 0.5% and 100 mg/L initial concentration of chromium. Conclusions: Removal of hexavalent chromium from the wastewater could be successfully performanced using Platinum-Iron/Iron-carbon nanotubes and bipolar Electrodes.

Nickel-iron spherules from aouelloul glass

Science.gov (United States)

Chao, E.C.T.; Dwornik, E.J.; Merrill, C.W.

1966-01-01

Nickel-iron spherules, ranging from less than 0.2 to 50 microns in diameter and containing 1.7 to 9.0 percent Ni by weight, occur in glass associated with the Aouelloul crater. They occur in discrete bands of siliceous glass enriched in dissolved iron. Their discovery is significant tangible evidence that both crater and glass originated from terrestrial impact.

X-ray diffraction on nanoparticles chromium and nickel oxides obtained by gelatin using synchrotron radiation

International Nuclear Information System (INIS)

Menezes, Alan Silva de; Medeiros, Angela Maria de Lemos; Miranda, Marcus Aurelio Ribeiro; Almeida, Juliana Marcela Abraao; Remedios, Claudio Marcio Rocha; Silva, Lindomar R.D. da; Gouveia, S.T.; Sasaki, Jose Marcos; Jardim, P.M.

2003-01-01

Full text: Cr 2 O 3 nanoparticles has many applications like green pigments, wear resistance, and coating materials for thermal protection. Several methods to produce chromium oxide nanoparticles have already been studied, gas condensation, laser induced pyrolysis, microwave plasma, sol-gel and gamma radiation methods. Many applications for this kind of material can be provide concerning the particle size. For instance, particle size approximately of 200 nm are preferable as pigment due to its opacity and below 50 nm can be used as transparent pigment. In this work we have demonstrated that chromium and nickel oxide nanoparticles can be prepared by gelatin method. X-Ray diffraction (XRD) show that mean particle size for chromium oxide of 15-150 nm and nickel oxide of 90 nm were obtained for several temperature of sintering. The X-Ray powder diffraction pattern were performed using Synchrotron Radiation X-Ray source at XRD1 beamline in National Laboratory of Light Synchrotron (LNLS). (author)

Nickel and chromium ion release from stainless steel bracket on immersion various types of mouthwashes

Science.gov (United States)

Mihardjanti, M.; Ismah, N.; Purwanegara, M. K.

2017-08-01

The stainless steel bracket is widely used in orthodontics because of its mechanical properties, strength, and good biocompatibility. However, under certain conditions, it can be susceptible to corrosion. Studies have reported that the release of nickel and chromium ions because of corrosion can cause allergic reactions in some individuals and are mutagenic. The condition of the oral environment can lead to corrosion, and one factor that can alter the oral environment is mouthwash. The aim of this study was to measure the nickel and chromium ions released from stainless steel brackets when immersed in mouthwash and aquadest. The objects consisted of four groups of 17 maxillary premolar brackets with .022 slots. Each group was immersed in a different mouthwash and aquadest and incubated at 37 °C for 30 days. After 30 days of immersion, the released ions were measured using the ICP-MS (Inductively Coupled Plasma-Mass Spectrometer). For statistical analysis, both the Kruskal-Wallis and Mann-Whitney tests were used. The results showed differences among the four groups in the nickel ions released (p < 0.05) and the chromium ions released (p < 0.5). In conclusion, the ions released as a result of mouthwash immersion have a small value that is below the limit of daily intake recommended by the World Health Organization.

Bioaccessibility, bioavailability and toxicity of commercially relevant iron- and chromium-based particles: in vitro studies with an inhalation perspective

Directory of Open Access Journals (Sweden)

Hedberg Yolanda

2010-09-01

Full Text Available Abstract Background Production of ferrochromium alloys (FeCr, master alloys for stainless steel manufacture, involves casting and crushing processes where particles inevitably become airborne and potentially inhaled. The aim of this study was to assess potential health hazards induced by inhalation of different well-characterized iron- and chromium-based particles, i.e. ferrochromium (FeCr, ferrosiliconchromium (FeSiCr, stainless steel (316L, iron (Fe, chromium (Cr, and chromium(IIIoxide (Cr2O3, in different size fractions using in vitro methods. This was done by assessing the extent and speciation of released metals in synthetic biological medium and by analyzing particle reactivity and toxicity towards cultured human lung cells (A549. Results The amount of released metals normalized to the particle surface area increased with decreasing particle size for all alloy particles, whereas the opposite situation was valid for particles of the pure metals. These effects were evident in artificial lysosomal fluid (ALF of pH 4.5 containing complexing agents, but not in neutral or weakly alkaline biological media. Chromium, iron and nickel were released to very low extent from all alloy particles, and from particles of Cr due to the presence of a Cr(III-rich protective surface oxide. Released elements were neither proportional to the bulk nor to the surface composition after the investigated 168 hours of exposure. Due to a surface oxide with less protective properties, significantly more iron was released from pure iron particles compared with the alloys. Cr was predominantly released as Cr(III from all particles investigated and was strongly complexed by organic species of ALF. Cr2O3 particles showed hemolytic activity, but none of the alloy particles did. Fine-sized particles of stainless steel caused however DNA damage, measured with the comet assay after 4 h exposure. None of the particles revealed any significant cytotoxicity in terms of cell death

Selective recovery of nickel over iron from a nickel-iron solution using microbial sulfate reduction in a gas-lift bioreactor

NARCIS (Netherlands)

Bijmans, M.F.M.; Helvoort, van P.J.; Dar, S.; Dopson, M.; Lens, P.N.L.; Buisman, C.J.N.

2009-01-01

Process streams with high concentrations of metals and sulfate are characteristic for the mining and metallurgical industries. This study aims to selectively recover nickel from a nickel-iron-containing solution at pH 5.0 using a single stage bioreactor that simultaneously combines low pH sulfate

Release of nickel and chromium ions from orthodontic wires following the use of teeth whitening mouthwashes

Directory of Open Access Journals (Sweden)

AmirHossein Mirhashemi

2018-02-01

Full Text Available Abstract Background Corrosion resistance is an important requirement for orthodontic appliances. Nickel and chromium may be released from orthodontic wires and can cause allergic reactions and cytotoxicity when patients use various mouthwashes to whiten their teeth. Our study aimed to assess the release of nickel and chromium ions from nickel titanium (NiTi and stainless steel (SS orthodontic wires following the use of four common mouthwashes available on the market. Methods This in vitro, experimental study was conducted on 120 orthodontic appliances for one maxillary quadrant including five brackets, one band and half of the required length of SS, and NiTi wires. The samples were immersed in Oral B, Oral B 3D White Luxe, Listerine, and Listerine Advance White for 1, 6, 24, and 168 h. The samples immersed in distilled water served as the control group. Atomic absorption spectroscopy served to quantify the amount of released ions. Results Nickel ions were released from both wires at all time-points; the highest amount was in Listerine and the lowest in Oral B mouthwashes. The remaining two solutions were in-between this range. The process of release of chromium from the SS wire was the same as that of nickel. However, the release trend in NiTi wires was not uniform. Conclusions Listerine caused the highest release of ions. Listerine Advance White, Oral B 3D White Luxe, and distilled water were the same in terms of ion release. Oral B showed the lowest amount of ion release.

Release of nickel and chromium ions in the saliva of patients with fixed orthodontic appliance: An in-vivo study.

Science.gov (United States)

Dwivedi, Anoop; Tikku, Tripti; Khanna, Rohit; Maurya, Rana Pratap; Verma, Geeta; Murthy, R C

2015-01-01

Various components of fixed orthodontic appliances are continuously interacting with saliva and other fluids in the mouth releasing various metal ions including nickel and chromium that can cause damaging effects if their concentration exceeds above the toxic dose. To determine and compare the level of nickel and chromium in the saliva of patients undergoing fixed orthodontic treatment at different time periods. The sample of saliva of 13 patients was taken at different time periods that is: Group 1 (before appliance placement), Group II, III, and IV (after 1-week, 1-month, and 3 months of appliance placement respectively). The fixed appliance comprised of brackets, bands, buccal tubes, lingual sheath, transpalatal arch and wires composed of Ni-Ti and stainless steel. The level of ions was determined using graphite furnace atomic absorption spectro-photometry. The data thus obtained were statistically analyzed using SPSS Statistical Analysis Software (Version 15.0). Level of nickel and chromium in saliva was highest in Group II and lowest in Groups I for both the ions. On comparison among different Groups, it was statistically significant for all the groups (<0.001) except between Group III and Group IV. The release of nickel and chromium was maximum at 1-week and then the level gradually declined. These values were well below the toxic dose of these ions. The results should be viewed with caution in subjects with Ni hypersensitivity.

Iron -chromium alloys and free surfaces: from ab initio calculations to thermodynamic modeling

International Nuclear Information System (INIS)

Levesque, M.

2010-11-01

Ferritic steels possibly strengthened by oxide dispersion are candidates as structural materials for generation IV and fusion nuclear reactors. Their use is limited by incomplete knowledge of the iron-chromium phase diagram at low temperatures and of the phenomena inducing preferential segregation of one element at grain boundaries or at surfaces. In this context, this work contributes to the multi-scale study of the model iron-chromium alloy and their free surfaces by numerical simulations. This study begins with ab initio calculations of properties related to the mixture of atoms of iron and chromium. We highlight complex dependency of the magnetic moments of the chromium atoms on their local chemical environment. Surface properties are also proving sensitive to magnetism. This is the case of impurity segregation of chromium in iron and of their interactions near the surface. In a second step, we construct a simple energy model for high numerical efficiency. It is based on pair interactions on a rigid lattice to which are given local chemical environment and temperature dependencies. With this model, we reproduce the ab initio results at zero temperature and experimental results at high temperature. We also deduce the solubility limits at all intermediate temperatures with mean field approximations that we compare to Monte Carlo simulations. The last step of our work is to introduce free surfaces in our model. We then study the effect of ab initio calculated bulk and surface properties on surface segregation.Finally, we calculate segregation isotherms. We therefore propose an evolution model of surface composition of iron-chromium alloys as a function of bulk composition. which are given local chemical environment and temperature dependencies. With this model, we reproduce the ab initio results at zero temperature and experimental results at high temperature. We also deduce the solubility limits at all intermediate temperatures with mean field approximations that

Void swelling in fast reactor irradiated high purity binary iron-chromium alloys

International Nuclear Information System (INIS)

Little, E.A.; Stow, D.A.

The void swelling characteristics of a series of high purity binary iron-chromium alloys containing 0 - 615 0 C. The void swelling behaviour can be qualitatively rationalized in terms of point defect trapping and precipitation processes involving chromium atoms

Human biomonitoring of chromium and nickel from an experimental exposure to manual metal arc welding fumes of low and high alloyed steel.

Science.gov (United States)

Bertram, Jens; Brand, Peter; Schettgen, Thomas; Lenz, Klaus; Purrio, Ellwyn; Reisgen, Uwe; Kraus, Thomas

2015-05-01

The uptake and elimination of metals from welding fumes is currently not fully understood. In the Aachen Workplace Simulation Laboratory (AWSL) it is possible to investigate the impact of welding fumes on human subjects under controlled exposure conditions. In this study, the uptake and elimination of chromium or chromium (VI) respectively as well as nickel was studied in subjects after exposure to the emissions of a manual metal arc welding process using low or high alloyed steel. In this present study 12 healthy male non-smokers, who never worked as welders before, were exposed for 6h to welding fumes of a manual metal arc welding process. In a three-fold crossover study design, subjects were exposed in randomized order to either clean air, emissions from welding low alloyed steel, and emissions from welding high alloyed steel. Particle mass concentration of the exposure aerosol was 2.5mg m(-3). The content of chromium and nickel in the air was determined by analysing air filter samples on a high emission scenario. Urine analysis for chromium and nickel was performed before and after exposure using methods of human biomonitoring. There were significantly elevated chromium levels after exposure to welding fumes from high alloyed steel compared to urinary chromium levels before exposure to high alloyed welding fumes, as well as compared to the other exposure scenarios. The mean values increased from 0.27 µg l(-1) to 18.62 µg l(-1). The results were in good agreement with already existing correlations between external and internal exposure (German exposure equivalent for carcinogenic working materials EKA). The variability of urinary chromium levels was high. For urinary nickel no significant changes could be detected at all. Six-hour exposure to 2.5mg m(-3) high alloyed manual metal arc welding fumes lead to elevated urinary chromium levels far higher (7.11-34.16 µg l(-1)) than the German biological exposure reference value (BAR) of 0.6 µg l(-1) directly after

On superplasticity of corrosion resistant ferritic-austenitic chromium-nickel steels

Energy Technology Data Exchange (ETDEWEB)

Surovtsev, A P; Sukhanov, V E

1988-01-01

The deformability of corrosion resistant chromium-nickel ferritic austenitic steel type O8Kh22N6T under tension, upsetting and torsion in the 600-1200 deg C temperature range is studied. For the deformation rate of the order of 10/sup -3/ s/sup -1/ the effect of superelasticity reveals itself at 850 deg C in the process of ferrite dynamic polymerization, in the 925-950 deg C range, at initial stages of dynamic recrystallization - the dynamic polygonization controlled by chromium carbide dissolving in steel and maximum at 1050 deg C in the process of development of austenite dynamic recrystallization with grain refinement with F/A ratio equalling 1. After upsetting in the elasticity mode at 1050 deg C the impact strength of the above steel is maximum.

Techniques for Achieving Zero Stress in Thin Films of Iridium, Chromium, and Nickel

Science.gov (United States)

Broadway, David M.; O'Dell, Stephen L.; Ramsey, Brian D.; Weimer, Jeffrey

2015-01-01

We examine techniques for achieving zero intrinsic stress in thin films of iridium, chromium, and nickel deposited by magnetron sputter deposition. The intrinsic stress is further correlated to the microstructural features and physical properties such as surface roughness and optical density at a scale appropriate to soft X-ray wavelengths. The examination of the stress in these materials is motivated by efforts to advance the optical performance of light-weight X-ray space telescopes into the regime of sub-arcsecond resolution through various deposition techniques that rely on control of the film stress to values within 10-100 MPa. A characteristic feature of the intrinsic stress behavior in chromium and nickel is their sensitivity to the magnitude and sign of the intrinsic stress with argon gas pressure and deposition rate, including the existence of a critical argon process pressure that results in zero film stress which scales linearly with the atomic mass of the sputtered species. While the effect of stress reversal with argon pressure has been previously reported by Hoffman and others for nickel and chromium, we report this effect for iridium. In addition to stress reversal, we identify zero stress in the optical functioning iridium layer shortly after island coalescence for low process pressures at a film thickness of approximately 35nm. The measurement of the low values of stress during deposition was achieved with the aid of a sensitive in-situ instrument capable of a minimum detectable level of stress, assuming a 35nm thick film, in the range of 0.40-6.0 MPa for oriented crystalline silicon substrate thicknesses of 70-280 microns, respectively.

Arsenic, chromium, copper, iron, manganese, lead, selenium and ...

African Journals Online (AJOL)

2014-05-20

May 20, 2014 ... Arsenic, chromium, copper, iron, manganese, lead, selenium and zinc in the ... and sediment were collected and trace element concentrations were measured with an ICP-MS. ..... Clay minerals are known to have high sorption affinities ..... sediment/water quality interaction with particular reference to the.

Hydrogenation of carbon to methane in reduced sponge iron, chromium, and ferrochromium

Energy Technology Data Exchange (ETDEWEB)

Qayyum, M A; Reeve, D A

1976-01-01

Hydrogenation of excess carbon to methane in reduced sponge iron, chromium and ferrochromium under isothermal and temperature-programmed conditions indicates that it is possible to control the residual carbon content of the metallized products which may be an advantage if further processing of the products is contemplated. Hydrogenation starts above 800/sup 0/C and a shrinking-core kinetic model fits the experimental data. The mean apparent activation energy for the hydrogenation of residual carbon to methane in sponge iron, chromium and ferrochromium is 21 kcal/mole.

High chromium nickel base alloys hot cracking susceptibility

International Nuclear Information System (INIS)

Tirand, G.; Primault, C.; Robin, V.

2014-01-01

High Chromium nickel based alloys (FM52) have a higher ductility dip cracking sensitivity. New filler material with higher niobium and molybdenum content are developed to decrease the hot crack formation. The behavior of these materials is studied by coupling microstructural analyses and hot cracking test, PVR test. The metallurgical analyses illustrate an Nb and Mo enrichment of the inter-dendritic spaces of the new materials. A niobium high content (FM52MSS) induces the formation of primary carbide at the end of solidification. The PVR test reveal a solidification crack sensitivity of the new materials, and a lowest ductility dip cracking sensitivity for the filler material 52MSS. (authors)

Iron-based amorphous alloys and methods of synthesizing iron-based amorphous alloys

Science.gov (United States)

Saw, Cheng Kiong; Bauer, William A.; Choi, Jor-Shan; Day, Dan; Farmer, Joseph C.

2016-05-03

A method according to one embodiment includes combining an amorphous iron-based alloy and at least one metal selected from a group consisting of molybdenum, chromium, tungsten, boron, gadolinium, nickel phosphorous, yttrium, and alloys thereof to form a mixture, wherein the at least one metal is present in the mixture from about 5 atomic percent (at %) to about 55 at %; and ball milling the mixture at least until an amorphous alloy of the iron-based alloy and the at least one metal is formed. Several amorphous iron-based metal alloys are also presented, including corrosion-resistant amorphous iron-based metal alloys and radiation-shielding amorphous iron-based metal alloys.

Spectrophotometric determination of zirconium in nickel-base alloys with Arsenazo III after separation by froth flotation

International Nuclear Information System (INIS)

Sekine, K.; Onishi, H.

1977-01-01

0.02-0.1% of zirconium can be determined in nickel alloys by spectrophotometry with Arsenazo III after its separation from the sample solution by means of froth flotation using Arsenazo III and Zephiramine. Nickel, chromium and iron do not interfere. Analysis of standard alloys yielded a standard deviation of 2.2%. (orig.) [de

In vitro and in vivo corrosion evaluation of nickel-chromium- and copper-aluminum-based alloys.

Science.gov (United States)

Benatti, O F; Miranda, W G; Muench, A

2000-09-01

The low resistance to corrosion is the major problem related to the use of copper-aluminum alloys. This in vitro and in vivo study evaluated the corrosion of 2 copper-aluminum alloys (Cu-Al and Cu-Al-Zn) compared with a nickel-chromium alloy. For the in vitro test, specimens were immersed in the following 3 corrosion solutions: artificial saliva, 0.9% sodium chloride, and 1.0% sodium sulfide. For the in vivo test, specimens were embedded in complete dentures, so that one surface was left exposed. The 3 testing sites were (1) close to the oral mucosa (partial self-cleaning site), (2) surface exposed to the oral cavity (self-cleaning site), and (3) specimen bottom surface exposed to the saliva by means of a tunnel-shaped perforation (non-self-cleaning site). Almost no corrosion occurred with the nickel-chromium alloy, for either the in vitro or in vivo test. On the other hand, the 2 copper-aluminum-based alloys exhibited high corrosion in the sulfide solution. These same alloys also underwent high corrosion in non-self-cleaning sites for the in vivo test, although minimal attack was observed in self-cleaning sites. The nickel-chromium alloy presented high resistance to corrosion. Both copper-aluminum alloys showed considerable corrosion in the sulfide solution and clinically in the non-self-cleaning site. However, in self-cleaning sites these 2 alloys did not show substantial corrosion.

Microplasma synthesis on aluminum with additions of iron and nickel soluble complexes in electrolyte

Energy Technology Data Exchange (ETDEWEB)

Rogov, A.B., E-mail: alex-lab@bk.ru [Nikolaev Institute of Inorganic Chemistry. 3, Acad. Lavrentiev Ave, Novosibirsk, 630090 (Russian Federation); Mironov, I.V.; Terleeva, O.P.; Slonova, A.I. [Nikolaev Institute of Inorganic Chemistry. 3, Acad. Lavrentiev Ave, Novosibirsk, 630090 (Russian Federation)

2012-10-01

Highlights: Black-Right-Pointing-Pointer Alkaline homogeneous electrolyte with transition metals complexes. Black-Right-Pointing-Pointer Coatings contain metallic iron, nickel and their oxides in alumina-silica matrix. Black-Right-Pointing-Pointer Effect of Fe/Ni ratio on coatings properties and process characteristics. - Abstract: The microplasma synthesis of coatings containing iron and nickel from homogeneous electrolytes has been studied. For stabilization of transition metals in solution, it is proposed to use chelation. It was found that the synthesis of coatings using alternating current leads to the formation of metallic iron and nickel particles in addition to oxide phases. The iron and nickel complexes concentrations ratio in the electrolyte correlates with the coatings composition. Obtained coatings have been studied by scanning electron microscopy with X-ray microanalyser and by X-ray diffraction with Cu and Mo radiation. The metal content in the coating was determined spectrophotometrically from the absorption of iron thiocyanate complexes and nickel dimethylglyoxime complex.

Investigation of alternative phosphating treatments for nickel and hexavalent chromium elimination; Investigacao de tratamentos alternativos de fosfatizacao para eliminacao do niquel e cromo hexavalente

Energy Technology Data Exchange (ETDEWEB)

Jazbinsek, Luiz Antonio Rossi

2014-07-01

The phosphating processes are widely used in industry as surface treatments for metals, especially for low thickness plates, improving the adhesion between the metallic surface and the paint coating, and increasing the durability of paint systems against corrosion attacks. The tricationic phosphates containing zinc, nickel and manganese are commonly applied on steel. There is much discussion about the replacement of nickel by another element in order to have an environmentally friendly phosphating process. Niobium as a replacement for nickel has been evaluated. The most significant environmental impacts of phosphating processes are related to the presence of nickel and hexavalent chromium used in the process, this last as a passivation treatment. Nickel and hexavalent chromium are harmful to human and environment leading to contamination of water and soil. In the present study phosphate layers containing zinc, manganese and niobium have been evaluated and characterized on galvanized steel, and the results were compared with phosphates containing zinc, manganese and nickel, or a bicationic phosphate layer with zinc and manganese. Although the use of hexavalent chromium is not recommended worldwide, it is still used in processes for sealing the porosity of phosphate layers. This element is carcinogenic and has been associated with various diseases. Due to the passivation characteristics of niobium, this study also evaluated the tricationic bath containing niobium ammonium oxalate as a passivation treatment. The results showed that it could act as a replacement for the hexavalent chromium. The results of the present study showed that formulations containing niobium are potential replacements for hexavalent chromium and similar corrosion protection was obtained for the phosphate containing nickel or that with niobium. The morphology observed by scanning electron microscopy, gravimetric tests, porosity and adhesion evaluation results indicated that the phosphate

Determination of chromium, cobalt and nickel in tissue samples by radiochemical activation analysis

International Nuclear Information System (INIS)

Reisell, A.; Lakomaa, E.L.

1983-03-01

A radiochemical neutron activation analysis method for the determination of chromium, cobalt and nickel in tissue samples. A radiochemical neutron activation analysis method for the determination of chromium, cobalt and nickel has been developed. The destruction device used consisted of a combined wet-ashing-distillation and ion-exchange system. Six samples could be treated at the same time. The samples were wet-ashed with H*L2SO*L4-H*L2O*L2 mixture. Volatile elements were distilled as bromide compounds with HBr*H-. The distillation residue in 8M HCl was passed through hydrated antimony pentoxide (HAP) in order to remove disturbing *H2*H4Na-activity and through a Dowex 2 x 8 column so as to retain *H6*H0Co (formed from *H5*H8Ni). Chromium was elutriated from the column and precipitated as Cr(OH)*L3 for the removal of disturbing *H3*H2P-activity. The standards and samples were treated in a similar manner each so that the yield determination is not necessarily needed. The yields by tracer experiments were (43 +- 5) % for Cr, (93 +- 4) % for Co and (88 +- 14) % for Ni. The precision and accuracy of the method were studied by using reference materials of the National Bureau of Standards (NBS) and the International Atomic Energy Agency (IAEA)

Determination of macro nickel, vanadium and iron in crude oil and residues by derivative spectrophotometry

International Nuclear Information System (INIS)

Liu, W.; Wang, L.; Li, X.

1992-01-01

In this paper, a new method with derivative spectrophotometry and 2-(5-bromo-2-pyridylazo)-5-diethylaminophenol as the chromogenic reagent in buffer solution of different pH developed for determining micro amounts of nickel. Vanadium and iron in crude oil and residues is reported. Forth-, Second- and Third-, Fourth-order derivative spectrophotometry were applied to determine nickel, nickel and vanadium, nickel and iron in crude oil and residues, respectively. The derivative maximums chosen for the measurement were at 556 nm for nickel, 540 nm and 643 nm for nickel and vanadium, 524 nm and 604 nm for nickel and iron. Beer's law is valid for the range 1.0 x 10 -6 to 2.5 x 10 -5 M

Abrasion Resistance of as-Cast High-Chromium Cast Iron

Directory of Open Access Journals (Sweden)

Pokusová Marcela

2014-12-01

Full Text Available High chromium cast irons are widely used as abrasion resistant materials. Their properties and wear resistance depend on carbides and on the nature of the matrix supporting these carbides. The paper presents test results of irons which contain (in wt.% 18-22 Cr and 2-5 C, and is alloyed by 1.7 Mo + 5 Ni + 2 Mn to improve the toughness. Tests showed as-cast irons with mostly austenitic matrix achieved hardness 36-53 HRC but their relative abrasion-resistance was higher than the tool steel STN 19436 heat treated on hardness 60 HRC.

Corrosion resistance of nickel alloys with chromium and silicon to the red fuming nitric acid

International Nuclear Information System (INIS)

Gurvich, L.Ya.; Zhirnov, A.D.

1994-01-01

Corrosion and electrochemical behaviour of binary Ni-Cr, Ni-Si nickel and ternary Ni-Cr-Si alloys in the red fuming nitric acid (RFNA) (8-% of HNO 3 +20% of N 2 O 4 ) is studied. It is shown that nickel alloying with chromium improves its corrosion resistance to the red fuming nitric acid. Nickel alloying with silicon in quantities of up to 5 % reduces, and up to 10%-increases abruptly the corrosion resistance with subsequent decrease of the latter after the further increase of concentration. Ni-15% of Cr alloy alloying with silicon increases monotonously the corrosion resistance. 10 refs., 7 figs., 3 tabs

Contribution to the study of the electrodeposition of iron-nickel alloys; Contribution a l'etude du depot electrolytique des alliages fer-nickel

Energy Technology Data Exchange (ETDEWEB)

Valignat, J [Commissariat a l' Energie Atomique, Grenoble (France). Centre d' Etudes Nucleaires

1967-12-01

Using a coulometric technique based upon the anodic intentiostatic dissolution, we studied the potentiostatic, deposition of nickel, iron and nickel iron alloys. We have shown that the minimum of the curve I = f (t) (deposition current versus time) is probably due to the transitory blocking of the surface by hydrogen and that the syn-crystallisation of nickel and iron is responsible for the anomalous co-deposition of these two elements. (author) [French] En employant une methode coulometrique par dissolution anodique intensipstatique, nous avons etudie le depot potentiostatique du nickel, du fer et des alliages fer-nickel. Nous avons pu montrer que le minimum de la courbe I = f (t) enregistree au cours du depot est du probablement au blocage momentane de la surface par l'hydrogene et que la syncristallisation du fer et du nickel est responsable de l'anomalie du depot simultane de ces deux elements. (auteur)

Transmission electron microscope study of fusion-environment radiation damage in iron and iron-chromium alloys

International Nuclear Information System (INIS)

Horton, L.L.S.

1982-07-01

A transmission electron microscopy study of radiation damage microstructures in iron and iron-chromium alloys has been performed. This study consisted of both qualitative and quantitative characterization of the dislocation and cavity microstructures, including determination of vacancy/interstitial character and Burgers vectors for dislocation loops and analysis of the cavity morphology. The effects of irradiation temperature, fluence, helium implantation, and chromium content were investigated. Neutron irradiation (iron specimens, 1 dpa, 455 to 1000 K) and triple-beam ion irradiation (Fe-10% Cr specimens, 10 dpa, 725 to 950 K; Fe-10% Cr specimens, 850 K, 0.3 to 100 dpa; and Fe, Fe-5% Cr, Fe-10% Cr specimens, 850 K, 10 dpa) were employed. In the triple-beam ion irradiation procedure, simultaneous bombardment with 4 MeV Fe ++ ions and energetic He + and D 2 + ions was used to simulate the fusion environment (10 at. ppM He/dpa and 41 at. ppM D/dpa). In addition, single-beam 4 MeV Fe ++ ion irradiations of Fe-10% Cr both with and without pre-injection of helium and deuterium were performed

The temperature gradient on section of casting in process of primary crystallization of chromium cast iron

Directory of Open Access Journals (Sweden)

A. Studnicki

2008-08-01

Full Text Available The methodology of defining in article was introduced the temperature gradient in process of primary crystallization during cooling the casting from chromium cast iron on basis of measurements of thermal field in test DTA-K3. Insert also the preliminary results of investigations of influence temperature gradient on structure of studied wear resistance chromium cast iron.

Chromium, Nickel and Manganese in the Groundwater Resources of Asadabad Plain, Iran

Directory of Open Access Journals (Sweden)

Azadeh Ghobadi

2017-01-01

Full Text Available Background & Aims of the Study: Heavy metals are one of the most important environmental pollutants which agricultural and industrial activities and urban development increased their entry rate to the underground resources. This study aimed to investigate the concentration of chromium, nickel and manganese in groundwater resources in Asadabad plain. Materials & Methods: Sampling of groundwater done in 2015 autumn. In this study, according to the Cochran’s sample size formula, tote formula, totally 60 samples of groundwater of Asadabad plain were collected from 20 wells and after preparation stage with atomic device, elements concentration of samples is read. To analysis of data SPSS 19 with significant level of 0.50 is used. Results: The concentration average of Chromium, Nickel and Manganese equal to 0.044¬ ±0.016, 70.42±10.83 and 2.64±0.83 ppb. The comparison results of the concentration average of elements based on WHO and ISIRI standard shows the concentration average of elements is lower than standard level. Conclusions: Currently the groundwater resources of Asadabad plain are not polluted with heavy metals, but long-term excessive use of agricultural inputs and construction of polluting industries can cause a threat to groundwater resources in this area.

Assessment of Changes in Nickel and Chromium Levels in the Gingival Crevicular Fluid during Fixed Orthodontic Treatment.

Science.gov (United States)

Bhasin, Vinny; Pustake, Swati J; Joshi, Viprat; Tiwari, Anil; Bhasin, Meenakshi; Punia, Ramandeep S

2017-08-01

Various components of appliances used in fixed orthodontic treatment are fabricated from materials that are highly resistant in nature and have high strength and biocompatibility. Corrosion of materials occurs inside the oral cavity due to numerous environmental or oral factors that act on them. These factors include temperature, pH variation, salivary conditions, mechanical loads, microbiological and enzymatic activity, and various food components. Gingival crevicular fluid (GCF) is the material obtained from the gingival sulcus and might act as a potential source for various biomarkers in the orthodontic setup because inflammatory-induced response is directly related to orthodontic forces in GCF. In the light of above-mentioned data, we planned this study to assess and evaluate the changes occurring in nickel and chromium levels in the GCF during fixed orthodontic treatment. This study included assessment of 30 patients who underwent fixed orthodontic treatment. Three samples were taken from the GCF of the patients giving a total of 90 samples. The samples were collected at the following time intervals: At baseline (pretreatment time), 1 month after the start of orthodontic treatment, and at 6 months after the commencement of orthodontic treatment. Cellulose strips were used for isolation of the tooth region. For GCF collection, a standardized cellulose acetate absorbent strip was used. Placement of the strips was done in the sulcus for 60 seconds for the collection of the samples. Refrigeration of the specimen bottles was done for a minimum of 7 days and was then sent to a laboratory where specimens were transferred for atomic absorption spectrophotometry. All the results were analyzed by Statistical Package for the Social Sciences software. At 1 month, the mean value of nickel and chromium in GCF was found to be 4.5 and 4.9 ug/gm of GCF respectively. While comparing the mean nickel levels between 1 and 6 months and between baseline and 6 months, significant

Temperature dependent quasiparticle renormalization in nickel and iron

Energy Technology Data Exchange (ETDEWEB)

Ovsyannikov, Ruslan; Thirupathaiah, Setti; Sanchez-Barriga, Jaime; Fink, Joerg; Duerr, Hermann [Helmholtz Zentrum Berlin, BESSY II, Albert-Einstein-Strasse 15, D-12489 Berlin (Germany)

2010-07-01

One of the fundamental consequences of electron correlation effects is that the bare particles in solids become 'dressed' with an excitation cloud resulting in quasiparticles. Such a quasiparticle will carry the same spin and charge as the original particle, but will have a renormalized mass and a finite lifetime. The properties of many-body interactions are described with a complex function called self energy which is directly accessible to modern high-resolution angle resolved photoemission spectroscopy (ARPES). Ferromagnetic metals like nickel or iron offers the exciting possibility to study the spin dependence of quasiparticle coupling to bosonic modes. Utilizing the exchange split band structure as an intrinsic 'spin detector' it is possible to distinguish between electron-phonon and electron-magnon coupling phenomena. In this contribution we will report a systematic investigation of the k- and temperature dependence of the electron-boson coupling in nickel and iron metals as well as discuss origin of earlier observed anomalous lifetime broadening of majority spin states of nickel at Fermi level.

Compaction study of particulate iron-chromium matrix composite reinforced with alumina

International Nuclear Information System (INIS)

Saidatulakmar Shamsuddin; Shamsul Baharin Jamaludin; Zuhailawati Hussain; Zainal Arifin Ahmad

2007-01-01

Recently, a sharper focus on cost reduction in producing advanced composites systems has increased and leads to an interest in ferrous matrix composite which is cheaper compared to Cobalt, Nickel and their alloys that are scarce, expensive and their dust is especially harmful. In the present investigation, Fe-Cr-Al 2 O 3 composite was prepared using conventional powder metallurgy technique; mixing, compaction and sintering. Consolidation of particulate materials is dependent on the compaction process. As load is increased, the number of contacting asperities increases and they flatten and grow to form a planar contact surface. These asperities eventually merge to form bonding surfaces between particles. This paper focused on finding the optimum compaction parameter in a uniaxial pressing. Six different pressure were studied; (250, 375, 500, 625, 750 and 875)MPa. experimental results show that the optimum compaction parameter is 750 MPa that produced highest linear shrinkage, highest bulk density, lowest porosity and highest hardness value. Every sample has formed binary alloy of Fe-Cr alloy, confirmed by XRD and alumina are homogeneously distributed in the Fe-Cr matrix revealed by optical micrograph and SEM. from EDX, the composites consist of iron, chromium and alumina. (author)

Effects of fixed orthodontic treatment on nickel and chromium levels in gingival crevicular fluid as a novel systemic biomarker of trace elements: A longitudinal study.

Science.gov (United States)

Amini, Fariborz; Shariati, Mahsa; Sobouti, Farhad; Rakhshan, Vahid

2016-05-01

Nickel and chromium might induce hypersensitivity. Therefore, they are of interest to orthodontists. Gingival crevicular fluid (GCF) is highly relevant to orthodontic treatments and might reflect systemic changes associated with the inflammatory response induced by orthodontic forces. Therefore, it might also be used to show metal ion changes. Nevertheless, baseline metal levels of GCF are unknown, and the effect of orthodontic treatment on GCF metal levels has not been investigated. The aim of this study was to assess the levels of nickel and chromium in GCF. Based on a pilot study, the sample size was predetermined as 24 × 3 measurements to obtain test powers above 90%. Nickel and chromium concentrations were measured before treatment and 1 month and 6 months later in 12 female and 12 male patients who had fixed orthodontic appliances using atomic absorption spectrophotometry. The gingival index was also evaluated in each session. The effects of treatment on GCF ions were analyzed using repeated-measures analysis of variance and Friedman tests (α = 0.05, β ≤0.01). The gingival index worsened over time (chi-square test, P <0.001). The mean nickel levels were 3.894 ± 1.442, 5.913 ± 2.735, and 19.810 ± 8.452 μg per gram, respectively, at baseline, month 1, and month 6. Chromium concentrations were 1.978 ± 0.721, 4.135 ± 1.591, and 13.760 ± 3.555 μg per gram, respectively. Compared with the baseline, nickel increased by 150% and 510%, respectively, in the first and sixth months (Friedman, P <0.0001), and chromium increased by 200% and 700%, respectively (analysis of variance, P <0.0001). Six months of fixed orthodontic treatment might intensify the levels of nickel and chromium in the GCF as well as gingival inflammation. Copyright © 2016 American Association of Orthodontists. Published by Elsevier Inc. All rights reserved.

Experimental exposure of healthy subjects with emissions from a gas metal arc welding process--part II: biomonitoring of chromium and nickel.

Science.gov (United States)

Gube, Monika; Brand, Peter; Schettgen, Thomas; Bertram, Jens; Gerards, Kerstin; Reisgen, Uwe; Kraus, Thomas

2013-01-01

The objective of this study was to investigate whether there is a relationship between the external exposure dose of chromium and nickel caused by a metal active gas welding process with a solid high-alloyed steel welding wire and inner exposure of subjects. In order to perform welding fume exposure under controlled and standardized conditions, the investigations were conducted in the "Aachen Workplace Simulation Laboratory". To perform biological monitoring of chromium and nickel, blood and urine samples of 12 healthy male non-smokers who never worked as welders were collected before and after a 6-h exposure to ambient air (0 mg/m(3)) and to welding fumes of a metal active gas welding process once with a concentration of the welding fume of 1 mg/m(3) and once with a concentration of 2.5 mg/m(3). Although the internal exposure to chromium and nickel in this study was comparatively low, the subjects showed significantly increased concentrations of these metals in urine after exposure to welding fume compared to the values at baseline. Moreover, the observed increase was significantly dose dependent for both of the substances. For the biological monitoring of chromium and nickel in urine of subjects exposed to welding fumes, a dependency on exposure dose was seen under standardized conditions after a single exposure over a period of 6 h. Thus, this study contributes to a better understanding of the relationship between ambient and biological exposures from welding fumes and provides a good basis for evaluating future biological threshold values for these metals in welding occupation.

Transmission electron microscope study of fusion-environment radiation damage in iron and iron-chromium alloys

Energy Technology Data Exchange (ETDEWEB)

Horton, L.L.S.

1982-07-01

A transmission electron microscopy study of radiation damage microstructures in iron and iron-chromium alloys has been performed. This study consisted of both qualitative and quantitative characterization of the dislocation and cavity microstructures, including determination of vacancy/interstitial character and Burgers vectors for dislocation loops and analysis of the cavity morphology. The effects of irradiation temperature, fluence, helium implantation, and chromium content were investigated. Neutron irradiation (iron specimens, 1 dpa, 455 to 1000 K) and triple-beam ion irradiation (Fe-10% Cr specimens, 10 dpa, 725 to 950 K; Fe-10% Cr specimens, 850 K, 0.3 to 100 dpa; and Fe, Fe-5% Cr, Fe-10% Cr specimens, 850 K, 10 dpa) were employed. In the triple-beam ion irradiation procedure, simultaneous bombardment with 4 MeV Fe/sup + +/ ions and energetic He/sup +/ and D/sub 2//sup +/ ions was used to simulate the fusion environment (10 at. ppM He/dpa and 41 at. ppM D/dpa). In addition, single-beam 4 MeV Fe/sup + +/ ion irradiations of Fe-10% Cr both with and without pre-injection of helium and deuterium were performed.

Synthesis of uniform-sized bimetallic iron-nickel phosphide nanorods

International Nuclear Information System (INIS)

Yoon, Ki Youl; Jang, Youngjin; Park, Jongnam; Hwang, Yosun; Koo, Bonil; Park, Je-Geun; Hyeon, Taeghwan

2008-01-01

We synthesized uniform-sized nanorods of iron-nickel phosphides from the thermal decomposition of metal-phosphine complexes. Uniform-sized (Fe x Ni 1-x ) 2 P nanorods (0≤x≤1) of various compositions were synthesized by thermal decomposition of Ni-trioctylphosphine (TOP) complex and Fe-TOP complex. By measuring magnetic properties, we found that blocking temperature and coercive field depend on Ni content in the nanorods. Both parameters were more sensitive to doping compared with bulk samples. - Graphical abstract: We synthesized uniform-sized nanorods of iron-nickel phosphides from thermal decomposition of metal-phosphine complexes. The magnetic studies showed that blocking temperature and coercive field depend on Ni content in the nanorods

Study of solubility of akaline earth metals in liquid iron and in alloys on its base

International Nuclear Information System (INIS)

Ageev, Yu.A.; Archugov, S.A.

1985-01-01

Solubility of magnesium, calcium, strontium and barium in liquid iron and its alloys with aluminium, silicon, nickel, chromium and carbon at 1600 deg C has been measured. Interaction parameters taking account of the effect of added elements on alkaline earth metal solubility in liquid iron have been estimated

Adsorption studies of water on copper, nickel, and iron: assessment of the polarization model

International Nuclear Information System (INIS)

Lee, S.; Staehle, R.W.

1997-01-01

In the atmospheric corrosion of copper, nickel, and iron, the adsorption of water affects the corrosion rates. Knowledge of water adsorption and metal oxyhydroxide formation is important in understanding the atmospheric corrosion process. The purposes of the present research were (i) to measure the adsorption of water on metal surfaces as a function of temperature and relative humidity (RH) and (ii) to assess Bradley's polarization model of adsorption. In the present research, the quartz-crystal microbalance (QCM) technique was used to measure the mass changes of copper, nickel, and iron at 0 to 100% relative humidity and 7 to 90 C under nitrogen and air environments. Less water was adsorbed on copper, nickel, and iron which form oxides than on gold. The amount of water adsorption was similar on copper, nickel, and iron under N 2 and air carrier gases. Functional relationship was first proposed as a way to include dipole/induced dipole interactions between the adsorbents and water layers. (orig.)

Standard Test Methods for Detecting Susceptibility to Intergranular Corrosion in Wrought, Nickel-Rich, Chromium-Bearing Alloys

CERN Document Server

American Society for Testing and Materials. Philadelphia

2008-01-01

1.1 These test methods cover two tests as follows: 1.1.1 Method A, Ferric Sulfate-Sulfuric Acid Test (Sections 3-10, inclusive)—This test method describes the procedure for conducting the boiling ferric sulfate—50 % sulfuric acid test which measures the susceptibility of certain nickel-rich, chromium-bearing alloys to intergranular corrosion (see Terminology G 15), which may be encountered in certain service environments. The uniform corrosion rate obtained by this test method, which is a function of minor variations in alloy composition, may easily mask the intergranular corrosion components of the overall corrosion rate on alloys N10276, N06022, N06059, and N06455. 1.1.2 Method B, Mixed Acid-Oxidizing Salt Test (Sections 11-18, inclusive)—This test method describes the procedure for conducting a boiling 23 % sulfuric + 1.2 % hydrochloric + 1 % ferric chloride + 1 % cupric chloride test which measures the susceptibility of certain nickel-rich, chromium-bearing alloys to display a step function increa...

Direct analysis of plutonium metal for gallium, iron, and nickel by energy dispersive x-ray spectrometry

International Nuclear Information System (INIS)

Bramlet, H.L.; Doyle, J.H.

1981-01-01

An x-ray secondary target method for routine determination of gallium, iron, and nickel in plutonium metal is described that has significant advantages over wet chemical analysis. Coupons requiring minimal preparation for analysis are produced as a breakaway tab on the plutonium ingot. All three elements are determined on the same coupon. Gallium is determined using an arsenic secondary target followed by iron and nickel using a zinc target. The analysis times are 5 minutes for gallium and 15 minutes for the combined iron and nickel. The method of analysis was evaluated in the range of from 0.5 to 1.5% gallium. Iron was investigated over the range of 67 to 3000 ppM and nickel from 64 to 110 ppM

Austenitic stainless steel alloys with high nickel contents in high temperature liquid metal systems

International Nuclear Information System (INIS)

Konvicka, H.R.; Schwarz, N.F.

1981-01-01

Fe-Cr-Ni base alloys (nickel content: from 15 to 70 wt%, Chromium content: 15 wt%, iron: balance) together with stainless steel (W.Nr. 1.4981) have been exposed to flowing liquid sodium at 730 0 C in four intervals up to a cumulative exposure time of 1500 hours. Weight change data and the results of post-exposition microcharacterization of specimens are reported. The corrosion rates increase with increasing nickel content and tend to become constant after longer exposure times for each alloy. The corrosion rate of stainless steel is considerably reduced due to the presence of the base alloys. Different kinetics of nickel poor (up to 35% nickel) and nickel rich (> 50% nickel) alloys and nickel transport from nickel rich to nickel poor material is observed. (orig.)

Effect of Low Nickel Dopant on Torque Transducer Response Function in High-Chromium Content ESR Stainless Tool Steels

Science.gov (United States)

Wiewel, Joseph L.; Hecox, Bryan G.; Orris, Jason T.; Boley, Mark S.

2007-03-01

The change in magnetoelastic torque transducer response was investigated as a low nickel content (up to 0.2%) is alloyed into an ESR (Electro-Slag-Refining) stainless tool steel with a chromium content of around 13%, which our previous studies have proven to be the ideal level of chromium content for optimal transducer performance. Two separate hollow steel 3/4-inch diameter shafts were prepared from ESR 416 and ESR 420 steel, respectively, the first having no nickel content and the second having 0.2% nickel content. The heat treatment of these steels consisted of a hardening process conducted in a helium atmosphere at 1038^oC, followed by an annealing at 871^oC for 5h and a 15^oC cool down rate. Prior and subsequent to the heat treatment processes, the circumferential and axial magnetic hysteresis properties of the samples were measured and their external field signals were mapped over the magnetically polarized regions both with and without applied shear stress up to 2500 psi on the samples. It was found that the effect of the low nickel dopant was to improve torque transducer sensitivity and linearity, but heat treatment worsened the performance of both samples.

Phosphorus effect on structure and physical properties of iron-nickel alloys

International Nuclear Information System (INIS)

Berseneva, F.N.; Kalinin, V.M.; Rybalko, O.F.

1982-01-01

The structure and properties of iron-nickel alloys (30-50 % Ni) containing from 0.02 to 0.5 wt. % P have been investigated. It has been found that phosphorus solubility in iron-nickel alloys at most purified from impurities exceeds limiting solubility values usually observed for commercial alloys. Phosphide eutectics precipitation over the grain boundaries of studied alloys occurs but with phosphorus content equal 0.45 wt. %. The 0.4 wt. % P addition in invar alloys increases saturation magnetization and the Curie point and leads to a more homogeneous structure

Heterogeneous kinetics of the reduction of chromium (VI) by elemental iron

International Nuclear Information System (INIS)

Fiuza, Antonio; Silva, Aurora; Carvalho, Goreti; Fuente, Antonio V. de la; Delerue-Matos, Cristina

2010-01-01

Zero valent iron (ZVI) has been extensively used as a reactive medium for the reduction of Cr(VI) to Cr(III) in reactive permeable barriers. The kinetic rate depends strongly on the superficial oxidation of the iron particles used and the preliminary washing of ZVI increases the rate. The reaction has been primarily modelled using a pseudo-first-order kinetics which is inappropriate for a heterogeneous reaction. We assumed a shrinking particle type model where the kinetic rate is proportional to the available iron surface area, to the initial volume of solution and to the chromium concentration raised to a power α which is the order of the chemical reaction occurring at surface. We assumed α = 2/3 based on the likeness to the shrinking particle models with spherical symmetry. Kinetics studies were performed in order to evaluate the suitability of this approach. The influence of the following parameters was experimentally studied: initial available surface area, chromium concentration, temperature and pH. The assumed order for the reaction was confirmed. In addition, the rate constant was calculated from data obtained in different operating conditions. Digital pictures of iron balls were periodically taken and the image treatment allowed for establishing the time evolution of their size distribution.

Effects of surface finishing conditions on the biocompatibility of a nickel-chromium dental casting alloy.

LENUS (Irish Health Repository)

McGinley, Emma Louise

2011-07-01

To assess the effects of surface finishing condition (polished or alumina particle air abraded) on the biocompatibility of direct and indirect exposure to a nickel-chromium (Ni-Cr) d.Sign®10 dental casting alloy on oral keratinocytes. Biocompatibility was performed by assessing cellular viability and morphology, metabolic activity, cellular toxicity and presence of inflammatory cytokine markers.

Iron and silicon effect on the phase composition of nickel-beryllium bronzes

International Nuclear Information System (INIS)

Zakharov, A.M.; Zakharov, M.V.; Ajvaz'yan, N.G.

1977-01-01

In order to specify phase composition and strengthening heat treatment conditions for nickel beryllium bronzes that are promising electrode materials for welding of high strength steels and nickel-base superalloys, the primary section of the quinternary Cu-Ni-Be-Fe-S system was studied at constant nickel and beryllium concentration and varying silicon and iron concentration (max. 4% of every element). The study was made using the metallographic and x-ray phase techniques, determination of alloy solidus temperature, and exessphase microhardness testing. Silicon additions are shown to decrease abruptly and those of iron, in contrast, somewhat to raise the solidus temperature of ternary Cu + 2% Ni + 0.3% Be alloy. When added concurrently, iron compensates for the damaging silicon effect on the solidus temperature of Cu-Ni-Be alloys. The excess phases formed can be used as strengthening agents of Cu-Ni-Be-Si-Fe alloys during quenching and subsequent aging

Associations of neonatal lead, cadmium, chromium and nickel co-exposure with DNA oxidative damage in an electronic waste recycling town

International Nuclear Information System (INIS)

Ni, Wenqing; Huang, Yue; Wang, Xiaoling; Zhang, Jingwen; Wu, Kusheng

2014-01-01

Objective: This study aimed to evaluate the effects of toxic heavy metal co-exposure on DNA oxidative damage in neonates from a primitive e-waste recycling region, Guiyu town, China. Methods: Our participants included 201 pregnant women: 126 from Guiyu town and 75 from Jinping district of Shantou city, where no e-waste recycling and dismantling activities existed. Structured interview questionnaires were administered to the pregnant women and umbilical cord blood (UCB) samples were collected after delivery. The UCB concentrations of lead, cadmium, chromium, and nickel were analyzed by graphite furnace atomic absorption spectrometry (GFAAS). Levels of UCB plasma 8-hydroxydeoxyguanosine (8-OHdG, a DNA oxidative damage biomarker) were determined by enzyme-linked immunosorbent assay. Results: Our results suggested that UCB lead and cadmium concentrations in neonates of Guiyu were significantly higher than those of Jinping (lead: median 110.45 ng/mL vs. 57.31 ng/mL; cadmium: median 2.50 ng/mL vs. 0.33 ng/mL, both P < 0.001). Parents' residence in Guiyu, and parents' work related to e-waste recycling were the risk factors associated with neonate's UCB lead and cadmium levels. No significant difference of UCB plasma 8-OHdG levels was found between Guiyu and the control area. After adjusting for potential confounders, cord plasma 8-OHdG concentrations (ng/mL) were positively associated with blood cadmium (β = 0.126 ng/mL, 95% CI: 0.055 to 0.198 ng/mL), chromium (β = 0.086 ng/mL, 95% CI: 0.014 to 0.158 ng/mL) and nickel (β = 0.215 ng/mL, 95% CI: 0.113 to 0.317 ng/mL) concentrations. Conclusions: The primitive e-waste recycling and dismantling activities may contribute to the elevated umbilical cord blood toxic heavy metal levels in neonates born in Guiyu. Exposures to cadmium, chromium and nickel were associated with increased oxidative DNA damage in neonates. - Highlights: • DNA oxidative damage levels (8-OHdG) in neonates from Guiyu were assessed. • Neonatal lead

Associations of neonatal lead, cadmium, chromium and nickel co-exposure with DNA oxidative damage in an electronic waste recycling town

Energy Technology Data Exchange (ETDEWEB)

Ni, Wenqing; Huang, Yue; Wang, Xiaoling; Zhang, Jingwen; Wu, Kusheng, E-mail: kswu@stu.edu.cn

2014-02-01

Objective: This study aimed to evaluate the effects of toxic heavy metal co-exposure on DNA oxidative damage in neonates from a primitive e-waste recycling region, Guiyu town, China. Methods: Our participants included 201 pregnant women: 126 from Guiyu town and 75 from Jinping district of Shantou city, where no e-waste recycling and dismantling activities existed. Structured interview questionnaires were administered to the pregnant women and umbilical cord blood (UCB) samples were collected after delivery. The UCB concentrations of lead, cadmium, chromium, and nickel were analyzed by graphite furnace atomic absorption spectrometry (GFAAS). Levels of UCB plasma 8-hydroxydeoxyguanosine (8-OHdG, a DNA oxidative damage biomarker) were determined by enzyme-linked immunosorbent assay. Results: Our results suggested that UCB lead and cadmium concentrations in neonates of Guiyu were significantly higher than those of Jinping (lead: median 110.45 ng/mL vs. 57.31 ng/mL; cadmium: median 2.50 ng/mL vs. 0.33 ng/mL, both P < 0.001). Parents' residence in Guiyu, and parents' work related to e-waste recycling were the risk factors associated with neonate's UCB lead and cadmium levels. No significant difference of UCB plasma 8-OHdG levels was found between Guiyu and the control area. After adjusting for potential confounders, cord plasma 8-OHdG concentrations (ng/mL) were positively associated with blood cadmium (β = 0.126 ng/mL, 95% CI: 0.055 to 0.198 ng/mL), chromium (β = 0.086 ng/mL, 95% CI: 0.014 to 0.158 ng/mL) and nickel (β = 0.215 ng/mL, 95% CI: 0.113 to 0.317 ng/mL) concentrations. Conclusions: The primitive e-waste recycling and dismantling activities may contribute to the elevated umbilical cord blood toxic heavy metal levels in neonates born in Guiyu. Exposures to cadmium, chromium and nickel were associated with increased oxidative DNA damage in neonates. - Highlights: • DNA oxidative damage levels (8-OHdG) in neonates from Guiyu were assessed. �

TO SELECTION OF TECHNOLOGICAL SCHEME OF SOFTENING HEAT TREATMENT FOR HIGH CHROMIUM CAST IRON

Directory of Open Access Journals (Sweden)

V. G. Efremenko

2014-03-01

Full Text Available Purpose. High chromium cast irons with austenitic matrix have low machinability. The aim of work is search of new energy-saving modes of preliminary softening heat treatment enhancing the machinability of castings by forming an optimum microstructure. Methodology. Metallographic analysis, hardness testing and machinability testing are applied. Findings. It was found out that high temperature annealing with continuous cooling yields to martensite-austenite matrix in cast iron 270Х15Г2Н1MPhT, which abruptly affects the machinability of cast iron. Significant improvement of machinability is achieved by forming of structure "ferrite + granular carbides" and by decline of hardness to 37-39 HRC in the case of two-stage isothermal annealing in the subcritical temperature range or by the use of quenching and tempering (two-step or cyclic. Originality. It was found that the formation of the optimal structure of the matrix and achievement of desired hardness level needed for improving machinability of high chromium cast iron containing 3 % austenite-forming elements, can be obtained: 1 due to pearlite original austenite followed by spherodization eutectoid carbides, and 2 by getting predominantly martensite structure followed by the decay of martensite and carbides coagulation at high-temperature tempering. Practical value. The new energy-saving schemes of softening heat treatment to ensure the growth of machinability of high chromium cast iron, alloyed by higher quantity of austenite forming elements, are proposed.

Aluminium alloys containing iron and nickel

International Nuclear Information System (INIS)

Coriou, H.; Fournier, R.; Grall, L.; Hure, J.; Herenguel, J.; Lelong, P.

1958-01-01

The first part of this report addresses mechanism, kinetics and structure factors of aluminium alloys containing iron and nickel in water and high temperature steam. The studied alloys contain from 0.3 to 0.7 per cent of iron, and 0.2 to 1.0 per cent of nickel. Corrosion resistance and corrosion structure have been studied. The experimental installation, process and samples are presented. Corrosion structures in water at 350 C are identified and discussed (structure of corrosion products, structure of metal-oxide interface), and then in steam at different temperatures (350-395 C). Corrosion kinetics is experimentally studied (weight variation in time) in water at 350 C and in steam at different temperatures. Reactions occurring at over-heated steam (more than 400 C) are studied, and the case of welded alloys is also addressed. The second part addresses the metallurgical mechanism and processes influencing aluminium alloy resistance to corrosion by high temperature water as it appeared that separated phases protect the solid solution through a neighbourhood action. In order to avoid deep local corrosions, it seems necessary to multiply protective phases in an as uniform as possible way. Some processes enabling this result are described. They belong to conventional metallurgy or to powder metallurgy (with sintering and extrusion)

TEM characterisation of stress corrosion cracks in nickel based alloys: effect of chromium content and chemistry of environment

International Nuclear Information System (INIS)

Delabrouille, F.

2004-11-01

Stress corrosion cracking (SCC) is a damaging mode of alloys used in pressurized water reactors, particularly of nickel based alloys constituting the vapour generator tubes. Cracks appear on both primary and secondary sides of the tubes, and more frequently in locations where the environment is not well defined. SCC sensitivity of nickel based alloys depends of their chromium content, which lead to the replacement of alloy 600 (15 % Cr) by alloy 690 (30 % Cr) but this phenomenon is not yet very well understood. The goal of this thesis is two fold: i) observe the effect of chromium content on corrosion and ii) characterize the effect of environment on the damaging process of GV tubes. For this purpose, one industrial tube and several synthetic alloys - with controlled chromium content - have been studied. Various characterisation techniques were used to study the corrosion products on the surface and within the SCC cracks: SIMS; TEM - FEG: thin foil preparation, HAADF, EELS, EDX. The effect of chromium content and surface preparation on the generalised corrosion was evidenced for synthetic alloys. Moreover, we observed the penetration of oxygen along triple junctions of grain boundaries few micrometers under the free surface. SCC tests show the positive effect of chromium for contents varying from 5 to 30 % wt. Plastic deformation induces a modification of the structure, and thus of the protective character, of the internal chromium rich oxide layer. SCC cracks which developed in different chemical environments were characterised by TEM. The oxides which are formed within the cracks are different from what is observed on the free surface, which reveals a modification of medium and electrochemical conditions in the crack. Finally we were able to evidence some structural characteristics of the corrosion products (in the cracks and on the surface) which turn to be a signature of the chemical environment. (author)

Assessment of corrosion resistance of cast cobalt- and nickel-chromium dental alloys in acidic environments.

Science.gov (United States)

Mercieca, Sven; Caligari Conti, Malcolm; Buhagiar, Joseph; Camilleri, Josette

2018-01-01

The aim of this study was to compare the degradation resistance of nickel-chromium (Ni-Cr) and cobalt-chromium (Co-Cr) alloys used as a base material for partial dentures in contact with saliva. Wiron® 99 and Wironit Extra-Hard® were selected as representative casting alloys for Ni-Cr and Co-Cr alloys, respectively. The alloys were tested in contact with deionized water, artificial saliva and acidified artificial saliva. Material characterization was performed by X-ray diffractometry (XRD) and microhardness and nanohardness testing. The corrosion properties of the materials were then analyzed using open circuit potential analysis and potentiodynamic analysis. Alloy leaching in solution was assessed by inductively coupled plasma mass spectrometry techniques. Co-Cr alloy was more stable than the Ni-Cr alloy in all solutions tested. Leaching of nickel and corrosion attack was higher in Ni-Cr alloy in artificial saliva compared with the acidified saliva. The corrosion resistance of the Co-Cr alloy was seen to be superior to that of the Ni-Cr alloy, with the former exhibiting a lower corrosion current in all test solutions. Microstructural topographical changes were observed for Ni-Cr alloy in contact with artificial saliva. The Ni-Cr alloy exhibited microstructural changes and lower corrosion resistance in artificial saliva. The acidic changes did not enhance the alloy degradation. Ni-Cr alloys are unstable in solution and leach nickel. Co-Cr alloys should be preferred for clinical use.

Leaching behavior of lanthanum, nickel and iron from spent catalyst using inorganic acids

Science.gov (United States)

Astuti, W.; Prilitasari, N. M.; Iskandar, Y.; Bratakusuma, D.; Petrus, H. T. B. M.

2018-01-01

Highly technological applications of rare earth metals (REs) and scarcity of supply have become an incentive torecover the REs from various resources, which include high grade and low grade ores, as well as recycledwaste materials. Spent hydrocracking catalyst contain lanthanum and a variety of valuable metals such as nickel and iron. This study investigated the recovery of lanthanum, nickel and iron from spent hydrocracking catalyst by leaching using various inorganic acid (sulfuric acid, hydrochloric acid, and nitric acid). The effect of acid concentration, type of acid and leaching temperature was conducted to study the leaching behavior of each valuable metal from spent-catalyst. It has been shown that it is possible to recover more than 90% of lanthanum, however the leaching efficiency of nickel and iron in this process was very low. It can be concluded that the leaching process is selective for lanthanum recovery from hydrocracking spent-catalyst.

Measurement of iron, magnesium and chromium concentrations in the saliva of the patients undergoing fixed orthodontic treatment

Directory of Open Access Journals (Sweden)

Valiollah Arash

2012-09-01

Full Text Available Introduction: Stainless steel alloy used in orthodontics has elements such as iron - magnesium and chromium , which may be released due to corrosion in the mouth . The aim of this study was to evaluate the changes of these elements in the saliva of patients undergoing fixed orthodontic treatment. Methods: In a clinical study with simple non- random sampling , 1ml saliva of 11 patients (7 females and 4 males who needed fixed orthodontic treatment and had no restorations or crowns were collected. During the fixed orthodontic treatment at successive times ( a day, a week, a month , two months and six months , 1 ml of saliva was collected and evaluated for the amount of iron ( spectrophotometry, chromium ( atomic absorption, and magnesium ( spectrophotometry . Bracket , band and wire used in all patients were stainless steel alloy and were manufactured by Dentaurum Company. After sample collection , the data analysis was performed with " Azeri- 5" and "10SPSS" software and repeated measures test. Results: The mean concentration of iron 66.326±0.541, chromium 0.483±0.324 and magnesium 0.552±293 decreased during the study but these results were not statistical y significant (p>0.05. Conclusions: Iron , chromium and magnesium concentration do not exceed the standard limits in saliva during orthodontic treatment.

Carbon-encapsulated nickel-iron nanoparticles supported on nickel foam as a catalyst electrode for urea electrolysis

International Nuclear Information System (INIS)

Wu, Mao-Sung; Jao, Chi-Yu; Chuang, Farn-Yih; Chen, Fang-Yi

2017-01-01

Highlights: • Electrochemical process can purify the urea-rich wastewater, producing hydrogen gas. • Carbon-encapsulated nickel iron nanoparticles (CE-NiFe) are prepared by pyrolysis. • An ultra-thin layer of CE-NiFe nanoparticles is attached to the 3D Ni foam. • CE-NiFe nanoparticles escalate both the urea electrolysis and hydrogen evolution. - Abstract: A cyanide-bridged bimetallic coordination polymer, nickel hexacyanoferrate, could be pyrolyzed to form carbon-encapsulated nickel-iron (CE-NiFe) nanoparticles. The formation of nitrogen-doped spherical carbon shell with ordered mesoporous structure prevented the structural damage of catalyst cores and allowed the migration and diffusion of electrolyte into the hollow carbon spheres. An ultra-thin layer of CE-NiFe nanoparticles could be tightly attached to the three-dimensional macroporous nickel foam (NF) by electrophoretic deposition. The CE-NiFe nanoparticles could lower the onset potential and increase the current density in anodic urea electrolysis and cathodic hydrogen production as compared with bare NF. Macroporous NF substrate was very useful for the urea electrolysis and hydrogen production, which allowed for fast transport of electron, electrolyte, and gas products. The superior electrocatalytic ability of CE-NiFe/NF electrode in urea oxidation and water reduction made it favorable for versatile applications such as water treatment, hydrogen generation, and fuel cells.

Emission flame spectrophotometry of chromium, cobalt, nickel trace amounts

International Nuclear Information System (INIS)

Prudnikov, Y.D.; Shapkina, Y.S.

1976-01-01

Chromium, cobalt, and nickel were determined in a flame spectrophotometer with a dual diffraction monochromator, DFS-12, in a high-temperature nitrogen-acetylene flame. The effect of ionization and the elements in the oxidizing flame was small. The lower limit of detection for the three elements is 1x10 -2 to 1 x10 -3 μg/ml, and the high selectivity of the analysis permits determining down to 10 -4 % Cr and Ni and to 10 -3 % Co. These elements may be determined in rocks and minerals from solutions prepared for analysis for alkali and alkali-earth elements. The possibilities of emission flame spectrophotometry are as great as those of atomic-absorption analysis, and it may be used for determining Cr, Co, and Ni in rocks and minerals, especially pure substances, metals, and other materials

Effect of Titanium Inoculation on Tribological Properties of High Chromium Cast Iron

Directory of Open Access Journals (Sweden)

Siekaniec D.

2017-12-01

Full Text Available The present investigation focuses on the study of the influence of titanium inoculation on tribological properties of High Chromium Cast Iron. Studies of tribological properties of High Chromium Cast Iron, in particularly the wear resistance are important because of the special application of this material. High Chromium Cast Iron is widely used for parts that require high wear resistance for example the slurry pumps, brick dies, several pieces of mine drilling equipment, rock machining equipment, and similar ones. Presented research described the effects of various amounts of Fe-Ti as an inoculant for wear resistance. The results of wear resistance were collated with microstructural analysis. The melts were conducted in industrial conditions. The inoculation was carried out on the stream of liquid metal. The following amount of inoculants have been used; 0.17% Fe-Ti, 0.33% Fe-Ti and 0.66% Fe-Ti. The tests were performed on the machine type MAN. The assessment of wear resistance was made on the basis of the weight loss. The experimental results indicate that inoculation improve the wear resistance. In every sample after inoculation the wear resistance was at least 20% higher than the reference sample. The best result, thus the smallest wear loss was achieved for inoculation by 0.66% Fe-Ti. There is the correlation between the changing in microstructure and wear resistance. With greater amount of titanium the microstructure is finer. More fine carbides do not crumbling so quickly from the matrix, improving the wear resistance.

A mathematical model for the iron/chromium redox battery

Science.gov (United States)

Fedkiw, P. S.; Watts, R. W.

1984-01-01

A mathematical model has been developed to describe the isothermal operation of a single anode-separator-cathode unit cell in a redox-flow battery and has been applied to the NASA iron/chromium system. The model, based on porous electrode theory, incorporates redox kinetics, mass transfer, and ohmic effects as well as the parasitic hydrogen reaction which occurs in the chromium electrode. A numerical parameter study was carried out to predict cell performance to aid in the rational design, scale-up, and operation of the flow battery. The calculations demonstrate: (1) an optimum electrode thickness and electrolyte flow rate exist; (2) the amount of hydrogen evolved and, hence, cycle faradaic efficiency, can be affected by cell geometry, flow rate, and charging procedure; (3) countercurrent flow results in enhanced cell performance over cocurrent flow; and (4) elevated temperature operation enhances cell performance.

Influence of iron doping on tetravalent nickel content in catalytic oxygen evolving films

Energy Technology Data Exchange (ETDEWEB)

Li, Nancy; Bediako, D. Kwabena; Hadt, Ryan G.; Hayes, Dugan; Kempa, Thomas J.; von Cube, Felix; Bell, David C.; Chen, Lin X.; Nocera, Daniel G.

2017-01-30

Iron doping of nickel oxide films results in enhanced activity for promoting the oxygen evolution reaction (OER). Whereas this enhanced activity has been ascribed to a unique iron site within the nickel oxide matrix, we show here that Fe doping influences the Ni valency. The percent of Fe3+ doping promotes the formation of formal Ni4+, which in turn directly correlates with an enhanced activity of the catalyst in promoting OER. The role of Fe3+ is consistent with its behavior as a superior Lewis acid.

A study of the levels of vanadium, cadmium, chromium and iron in ...

African Journals Online (AJOL)

Background: There is conflicting information on the adverse health effects of photocopier toner powder on operators.This study aims to determine the possible nephrotoxic effects of some commercially available photocopier toners and the levels of selected heavy metals (vanadium, cadmium, chromium and iron) for ...

Μetal Uptake by Sunflower (Helianthus annuus) Irrigated with Water Polluted with Chromium and Nickel.

Science.gov (United States)

Stoikou, Vasiliki; Andrianos, Vangelis; Stasinos, Sotiris; Kostakis, Marios G; Attiti, Sofia; Thomaidis, Nikolaos S; Zabetakis, Ioannis

2017-07-17

The water aquifers of the regions of Asopos River in Viotia and Messapia in Evia (Greece) have been contaminated with hexavalent chromium (Cr (VI)) and bivalent nickel (Ni (II)). Given that these areas are the two biggest tuber producing regions of Greece, in our previous work, the cross-contamination of the food chain with these two heavy metals was quantified. In the present study, the potential of sunflower ( Helianthus annuus ) cultivation in these regions is evaluated. The scope of our study was to investigate the uptake of chromium and nickel by sunflower, in a greenhouse experiment. The study included two cultivation periods of plants in six irrigation lines with different levels of Cr (VI) and Ni (II) ranging from 0 μg/L (control) to 10,000 μg/L. In all plant parts, statistically significant increased levels of Cr (VI) and Ni (II) were found when compared to control ones. Also, a positive correlation, both for Cr and Ni, between levels of heavy metals in irrigation water and plants was observed. Following European Food Safety Authority recommendations, the obtained oil was evaluated as safe for consumption, therefore, sunflower cultivation could be a valid bioremediation solution for the Asopos and Messapia regions.

Technology for producing synthetic cast iron for nuclear power station parts

International Nuclear Information System (INIS)

Blozhko, N.K.; Kurochkin, V.S.; Narkevich, E.A.; Nikitin, L.A.; Petrov, L.A.

1984-01-01

A technology was developed and implemented for producing grades SCh-30 through SCh-40 synthetic cast iron in industrial-frequency induction melting furnaces. Alternative innoculations with ferrosilicon and silicocalcium and alloying with chrome and nickel were studied. The mechanical properties and structure of cast irons produced by various technological methods were studied. The research showed that the sector's plants, equipped with industrial-frequency induction furnaces, can produce high-quality synthetic cast irons containing flake graphite for nuclear-power-station casting, without the use of expensive innoculants. Careful observance of the melting and innoculating technologies makes it possible to produce SCh 40 cast iron, without cementite inclusions, by innoculating with FS 75 ferrosilicon in the amount of 0.7% of the total melt weight. Using an innoculant mixture of 0.2% FS 75 and 0.5% SK 30 and low alloying with nickel and chromium, the cast-iron strength can be increased to 440-450 MPa, although the danger of cementite inclusions increase

Theoretical Modelling of Immobilization of Cadmium and Nickel in Soil Using Iron Nanoparticles

Directory of Open Access Journals (Sweden)

Vaidotas Danila

2017-09-01

Full Text Available Immobilization using zero valent using iron nanoparticles is a soil remediation technology that reduces concentrations of dissolved contaminants in soil solution. Immobilization of heavy metals in soil can be achieved through heavy metals adsorption and surface complexation reactions. These processes result in adsorption of heavy metals from solution phase and thus reducing their mobility in soil. Theoretical modelling of heavy metals, namely, cadmium and nickel, adsorption using zero valent iron nanoparticles was conducted using Visual MINTEQ. Adsorption of cadmium and nickel from soil solutions were modelled separately and when these metals were dissolved together. Results have showed that iron nanoparticles can be successfully applied as an effective adsorbent for cadmium and nickel removal from soil solution by producing insoluble compounds. After conducting the modelling of dependences of Cd+2 and Ni+2 ions adsorption on soil solution pH using iron nanoparticles, it was found that increasing pH of solution results in the increase of these ions adsorption. Adsorption of cadmium reached approximately 100% when pH ≥ 8.0, and adsorption of nickel reached approximately 100% when pH ≥ 7.0. During the modelling, it was found that adsorption of heavy metals Cd and Ni mostly occur, when one heavy metal ion is chemically adsorbed on two sorption sites. During the adsorption modelling, when Cd+2 and Ni+2 ions were dissolved together in acidic phase, it was found that adsorption is slightly lower than modelling adsorption of these metals separately. It was influenced by the competition of Cd+2 and Ni+2 ions for sorption sites on the surface of iron nanoparticles.

Research, development, and demonstration of nickel-iron batteries for electric vehicle propulsion. Annual report, 1980

Energy Technology Data Exchange (ETDEWEB)

1981-03-01

The objective of the Eagle-Picher nickel-iron battery program is to develop a nickel-iron battery for use in the propulsion of electric and electric-hybrid vehicles. To date, the program has concentrated on the characterization, fabrication and testing of the required electrodes, the fabrication and testing of full-scale cells, and finally, the fabrication and testing of full-scale (270 AH) six (6) volt modules. Electrodes of the final configuration have now exceeded 1880 cycles and are showing minimal capacity decline. Full-scale cells have presently exceeded 600 cycles and are tracking the individual electrode tests almost identically. Six volt module tests have exceeded 500 cycles, with a specific energy of 48 Wh/kg. Results to date indicate the nickel-iron battery is beginning to demonstrate the performance required for electric vehicle propulsion.

Three-body abrasive wear behaviour of metastable spheroidal carbide cast irons with different chromium contents

Energy Technology Data Exchange (ETDEWEB)

Efremenko, Vasily; Pastukhova, Tatiana; Chabak, Yuliia; Efremenko, Alexey [Pryazovskyi State Technical Univ., Mariupol (Ukraine); Shimizu, Kazumichi; Kusumoto, Kenta [Muroran Institute of Technology, Hokkaido (Japan); Brykov, Michail [Zaporozhye National Technical Univ., Zaporozhye (Ukraine)

2018-02-15

The effect of heat treatment and chromium contents (up to 9.1 wt.%) on the wear resistance of spheroidal carbide cast iron (9.5 wt.% V) was studied using optical and scanning electron microscopy, X-ray diffractometry, dilatometry and three-body abrasive testing. It was found that quenching from 760 C and 920 C improved the alloys' wear resistance compared to the as-cast state due to the formation of metastable austenite transforming into martensite under abrasion. The wear characteristics of alloys studied are 1.6 - 2.3 times higher than that of reference cast iron (12 wt.% V) having stable austenitic matrix. Chromium addition decreases surface damage due to the formation of M{sub 7}C{sub 3} carbides, while it reduces wear resistance owing to austenite stabilization to abrasion-induced martensite transformation. The superposition of these factors results in decreasing the alloys' wear behaviour with chromium content increase.

Pelepasan ion nikel dan kromium kawat Australia dan stainless steel dalam saliva buatan (The release of nickel and chromium ions from Australian wire and stainless steel in artificial saliva)

OpenAIRE

Nolista Indah Rasyid; Pinandi Sri Pudyani; JCP Heryumani

2014-01-01

Background: Fixed orthodontic treatment needs several types of wire to produce biomechanical force to move teeth. The use orthodontic wire within the mouth interacts with saliva, causing the release of nickel and chromium ions. Purpose: The study was aimed to examine the effect of immersion time in artificial saliva between special type of Australian wire and stainless steel on the release of nickel and chromium ions. Methods: Thirty special type Australian wires and 30 stainless steel wires ...

Anodic behaviours, dissolution and passivation of iron-nickel alloys in sulphuric environment. Influence of friction

International Nuclear Information System (INIS)

Ponthiaux, Pierre

1990-01-01

This research thesis reports the study of anodic dissolution and passivation of iron-nickel alloys (10, 20 and 31 pc nickel) in a sulphuric environment, with or without friction, by using anodic polarization curves. Without friction, the three alloys have a similar behaviour as pure iron. The analysis reveals different dissolution and passivation mechanisms with pure iron, and highlights the influence of nickel content on corresponding kinetics. The influence of cyclic plane-on-plane friction has been studied for the 31 pc nickel alloy which has an unsteady austenitic structure. Fretting results in some modifications of polarization curves. These modifications are analysed with respect to fretting parameters (relative speed of antagonist surfaces, contact pressure). They reveal the specific influence of the following phenomena: material strain hardening, martensitic transformation induced by strain hardening, partial destruction of adsorbates and/or of the passive film. Modifications of polarization curves give also information on the evolution of friction characteristics with respect to speed (a phenomenon of lubrication by the electrolyte occurs) [fr

Biosorption phenomena of chromium, copper, iron and zink by dispersed bacterial extracellular polymeric substance

International Nuclear Information System (INIS)

Zainus Salimin; Endang Nuraeni; Mirawaty

2015-01-01

Heavy metals removing is generally performed using chemical coagulant that generates the chemical pollutant, so it is necessary to replace it by another alternative material as the Extracellular Polymeric Substance (EPS) resulting from the extraction of bacteria. The EPS contains the negatively functional groups (RCOOH, ROPO 3 H, ROPO 3 Na, ROSO 3 H, ROSO 3 Na, etc) as the cation sorbent and the positively functional groups (ROH, RC(NH 2 )HCOOH, etc) as the anion sorbent. The EPS absorbs the ion pollutants, then EPS containing the loaded metals be settled by gravitation. The utilization of EPS for removing of chromium, copper, iron, and zink was performed for biosorption phenomena study. Two hundred mg of EPS is mixed with 300 ml of the liquid waste having the pH of 2,4 containing 3,06 ppm of chromium; 4,83 ppm of copper; 1,6 ppm of iron and 15,07 ppm of zink. The solution is then agitated on 150 rpm and the pH of 7. The separated water supernatant is then sampled every 2 hours for its analysis of metals content. The experiment is repeated again for the solution pH of 4 and 8. The results of experiment indicates that the EPS composition are 11% of polysaccharides, 77% of protein, and 11% of fat ,and EPS contains the chemical bounding of C-H, OH, NH, and C=O. Indicating that EPS contains RCOOH, ROH and (RC(NH 2 )HCOOH. The best condition for metals biosorption is pH 8, and on the 6 hours of process time, the metal concentration on the water supernatant for chromium, copper, iron and zinc are 0,99 ppm; 0,51 ppm; 0,17 ppm; and 4,61 ppm respectively. Its selectivities are Fe 3+ > Cr 3+ >Cu 2+ >Fe 2+ >Zn 2+ , on the 6 hours of process time the location of cations functional groups was filled by the cations of Cr 3+ ,Cu 2+ , dan Fe 2+ . The cation of Zn 2+ enters to that location on the end of period so on the 6 hours of process time its concentration of 4,61 ppm not conforms to its concentration of regulation value of 2 ppm. On the process time of 6 hours the removing

The determination of iron, chromium, titanium, and tungsten by x-ray-fluorescence spectrometry

International Nuclear Information System (INIS)

Austen, C.E.

1977-01-01

An accurate and precise method is described for the determination of iron and chromium in chromite, iron and titanium in ilmenite, and tungsten in tungsten ores. Samples are prepared for analysis by fusion with sodium peroxide or sodium tetraborate and leaching of the melt in a solution of tartaric or hydrochloric acid. Matrix correction and calibration are achieved by means of the single-standard calibration method with reference solutions prepared from compounds of the elements determined

Experience in melting of high-quality chromium-nickel-molybdenum steel in oxygen converter

Energy Technology Data Exchange (ETDEWEB)

Kosoi, L F; Yaburov, S I; Shul' kin, M L; Vedernikov, G G; Bragin, E D; Filork' yan, B K

1978-10-01

Technology of melting high-quality medium-carbon constructional chromium-nickel-molybdenum steel has been developed and tested in 130-t converters. The technology envisages metal refinement in a casting laddle using synthetic lime-aluminous slag and argon blowing, as well as liquid ferroallys (master alloys) for steel deoxidation and alloying. Due to a smaller content of sulfur, phosphorus, arsenic and sulphide inclusions, and to a smaller grain size (N 11-12), the steel, produced according to this technology possesses higher plastic properties and impact strength than conventional open-hearth furnace metal after heat treatment for the same strength.

Systematic Review of Chromium and Nickel Exposure During Pregnancy and Impact on Child Outcomes.

Science.gov (United States)

McDermott, Suzanne; Salzberg, Deborah C; Anderson, Anna Paige; Shaw, Timothy; Lead, Jamie

2015-01-01

Some forms of chromium (Cr) and nickel (Ni) are toxic, especially with chronic elevated exposure, and certain forms such as hexavalent chromium or nickel carbonyl were labeled as carcinogens. Since both metals are naturally occurring, and used in industrial processes, individuals may be exposed through ingestion of contaminated food or water, inhalation, or dermal contact. This study focused on the impact of toxic forms of Cr and Ni during pregnancy and outcomes in newborn and young children. A systematic literature review following "The Navigation Guide" was applied, and 16 reports that satisfied the inclusion criteria were scored. Six papers studied birth weight, prematurity, or gestational age: one found an association between Ni and small for gestational age, while another linked Ni with low birth weight; however, four reported no marked associations. Of six studies that examined birth defects, three found no significant associations; one noted an association between Ni and neural tube defects; one showed an association between Ni and structural birth defects; and one reported a weak effect for Cr exposure and musculoskeletal defects. In the remaining four studies, weak associations were found for hexavalent Cr and neuroblastoma, Ni and autism spectrum disorder, Cr and Ni and DNA damage, and Cr and lymphocyte damage. Among the studies that were rated as good for execution and reliability, there was weak evidence of an association between Ni and autism spectrum disorder and small for gestational age, but no significant association between Cr and a child outcome.

Monitoring of occupational exposure in manufacturing of stainless steel constructions. Part I: Chromium, iron, manganese, molybdenum, nickel and vanadium in the workplace air of stainless steel welders

International Nuclear Information System (INIS)

Kucera, J.; Hnatowicz, V.; Bencko, V.; Papayova, A.; Saligova, D.; Tejral, J.; Borska, L.

2000-01-01

Exposure to workplace airborne pollutants was examined in a group of 20 workers dealing mainly with welding, polishing, drilling and assembling of stainless steel constructions. Monitoring of airborne particulate matter (ARM) was performed using both personal and stationary samplers. For the personal full-shift monitoring, a SKC 224 PCRX-4 constant flow rate pump was used which was connected to a sampling head with mixed cellulose matched-weight filters having a diameter of 32 mm and a 0.8 μm pore size. The constant flow rate amounted to 2 L min -1 . For the stationary sampling, the ''Gent'' stacked filter unit PM10 sampler was used, operating at a flow rate of 16 L min -1 . It collects particles having an equivalent aerodynamic diameter (EAD) of less than 10,um in the separate ''coarse'' (2-10 μm EAD) and ''fine'' (< 2 μm EAD) size fractions on two sequential polycarbonate (Costar, Nuclepore) filters with a 47 mm diameter. The filters of both types were analyzed by instrumental neutron activation analysis (INAA). Of the elements determined, results for chromium, iron, manganese, molybdenum, nickel and vanadium are presented. Procedures for quality assurance of both sampling and analytical stages are described. Sampling of biological material for elemental analysis (hair, nails, urine and blood and/or serum) of exposed and control persons in contamination-free conditions was also performed. In addition, saliva samples were collected for studying immunological and genotoxicity aspects of occupational exposure. (author)

GROUND WATER REMEDIATION OF CHROMIUM USING ZERO-VALENT IRON IN A PERMEABLE REACTIVE BARRIER

Science.gov (United States)

A series of laboratory experiments were performed to elucidate the chromium transformation and precipitation reactions caused by the corrosion of zero-valent iron in water-based systems. Reaction rates were determined for chromate reduction in the presence of different types of ...

Effects of fixed orthodontic treatment using conventional (two-piece) versus metal injection moulding brackets on hair nickel and chromium levels: a double-blind randomized clinical trial.

Science.gov (United States)

Khaneh Masjedi, Mashallah; Haghighat Jahromi, Nima; Niknam, Ozra; Hormozi, Elham; Rakhshan, Vahid

2017-02-01

Although nickel and chromium are known as allergen and cytotoxic orthodontic metals, very few and controversial studies have assessed the effect of orthodontic treatment on their systemic levels especially those reflected by their best biomarker of exposure, hair. Additionally, metal injection moulding (MIM) brackets are not studied, and there is no study on systemic ion changes following their usage. In this double-blind randomized clinical trial, scalp hair samples of 24 female and 22 male fixed orthodontic patients [as two groups of conventional (two-piece) versus MIM brackets, n = 23×2] were collected before treatment and 6 months later. Randomization was carried out using a computer-generated random number table. The patients, laboratory expert, and author responsible for analyses were blinded of the bracket allocations. Hair nickel and chromium levels were measured using atomic absorption spectrophotometry. The effects of treatment, bracket types, gender, and age on hair ions were analysed statistically (α = 0.05, β ≤ 0.02). In both groups combined (n = 46), nickel increased from 0.1600±0.0890 µg/g dry hair mass (pre-treatment) to 0.3199±0.1706 (6th month). Chromium increased from 0.1657±0.0884 to 0.3066±0.1362 µg/g. Both of these increases were significant (paired t-test, P = 0.0000). Bracket types, age, and gender had no significant influence on ion levels (P > 0.05). ANCOVA indicated different patterns of chromium increases in different genders (P = 0.033) and ages (P = 0.056). Sample size determination should have accounted for the grouping as well. Hair nickel and chromium levels might increase about 185-200% after 6 months. They might not be affected by bracket types. Gender and age might not influence the baseline or 6th-month levels of both metals. Gender might however interact with orthodontic treatment, only in the case of chromium. The research is registered offline (thesis) and online (IR.AJUMS.REC.1394.516). The protocol was pre

Structure and growth of oxide on iron-chromium alloys

International Nuclear Information System (INIS)

Cox, M.G.C.; McEnaney, B.; Scott, V.D.

1974-01-01

Several oxides form during the initial stages of oxidation of iron-chromium alloys at 400 to 600 0 C in CO 2 -1%CO gas. The nature of the oxidation product depends upon crystallographic orientation and composition of the substrate, and can be explained by considering the maximum solubility of chromium in different oxide phases together with interfacial and strain energy factors. Kinetics of oxidation together with micrographic observations indicate that, as oxidation proceeds spinel oxide M 3 O 4 nucleates at sites on the substrate surface associated with asperities. The spinel nuclei grow laterally and vertically until they coalesce and the scale subsequently thickens according to a parabolic rate law. The duplex structure of scales is interpreted in terms of an outward diffusion of cations together with simultaneous growth of an inner layer in the space created by this outward movement. Scale porosity provides a route for gas-phase transport of oxidant to support the growth of the inner layer. Regularly spaced lamellar voids which may form in the inner layer are believed to be associated with a cyclic vacancy condensation process. Enrichment of the inner layer in chromium is explained by analysis of the possible diffusion path networks in close-packed oxides. Some comments are made concerning possible practical applications of these data. (author)

Noncentral forces and lattice vibration in transition metals. Alpha-iron, chromium, and tungsten

Energy Technology Data Exchange (ETDEWEB)

Singh, V P; Kharoo, H L; Kumar, M; Hemkar, M P [Allahabad Univ. (India). Dept. of Physics

1976-03-11

The elastic-force model proposed in a previous paper has been considered to compute the phonon dispersion relations for lattice waves propagating along the principal symmetry directions of ..cap alpha..-iron, chromium and tungsten. The model, however, takes into account the central forces together with the Clark, Gazis and Wallis type angular forces and the effect of electron-iron interaction on the lattice vibration as outlined by Krebs. The theoretical results are found to be quite satisfactory and compare well with recent neutron scattering data.

Adverse effects of nickel in transosseous wires and surgical implants: literature review.

Science.gov (United States)

Nwashindi, A; Dim, E M

2014-01-01

Transosseous wires used in the management of fractures are stainless steel alloys which contain nickel 14.5%, chromium 17.6%, iron 62.5% and molybdenum 2.8%. Gradual disintegration of the transosseous wires release nickel into the blood leading to increase nickel concentration in the blood. Nickel has been found to have some adverse systemic effects on the body. The aim of this paper is to discuss the sources of Nickel in the body as well as the systemic adverse effects of Nickel as a degradation product of stainless steel surgical implants. A study of pertinent literature on nickel as a content of stainless steel alloy used in implant surgery was done, taking note also of other sources of nickel in the body, the toxicokinetics of nickel and the related adverse effects of this metal and its compound in humans. As outcome,the sources of human exposure to nickel,distribution and metabolism of nickel in the body, host responseto stainless steel wires and the adverse effects of nickel in the body are presented. It may be necessary to discourage the use of wires or implants containing nickel in the management of fractures.The need for removal of these implants after they have served their purposes is emphasized.

Theoretical study of the correlation between magnetism and the properties of defects in iron, chromium and their alloys

International Nuclear Information System (INIS)

Soulairol, R.

2011-09-01

This PhD thesis is devoted to the study of the correlation between the magnetism and the properties of defects in 3d metals, mainly iron- and chromium-based systems, which are used in many technological applications, such as the new-generation nuclear reactors. This work is based on two complementary approaches: the Density Functional Theory (DFT) and a Tight Binding model (TB). We begin this study by the properties of pure materials such as chromium and α-iron. For the first one, we observe that the presence of a spin density wave (SDW) induces an anisotropy in the formation of point defects as well as the migration of vacancies. For the second, the solution energy of various 3d impurities depends on two terms: a chemical contribution mainly linked to the difference between the number of d electrons of iron and solute, and a magnetic contribution that reveals to be predominant in Fe-Cr. In the following parts, we tackle the correlation between magnetism and extended defects. We show in particular that the existence of magnetic frustrations near Fe/Cr interfaces can lead to the creation of non collinear magnetic structures. It also influences the energetic stability of these interfaces. We have noticed, in agreement with experimental findings, the presence of SDW near Fe/Cr interfaces, which is able to decrease those magnetic frustrations at the interface. We have also studied the magnetic structure of iron or chromium clusters embedded in an Fe-Cr alloy. We have finally shown, in the last part of this work, how the TB approach was able to account for the energetic and magnetic properties of defects not only in pure iron or chromium, but also in Fe-Cr alloys. (author)

Experimental patch testing with chromium-coated materials

DEFF Research Database (Denmark)

Bregnbak, David; Thyssen, Jacob P; Jellesen, Morten Stendahl

2017-01-01

Chromium coatings on metal alloys can be decorative, and prevent corrosion and metal ion release. We recently showed that handling of a chromium-containing disc resulted in chromium deposition on the skin. To examine patch test reactivity to chromium-coated discs. We included 15 patients: 10...... chromium-allergic patients, and 5 patients without chromium allergy. All were patch tested with potassium dichromate, cobalt chloride, nickel sulfate, and nine different metallic discs. The chromium-allergic patients were also patch tested with serial dilutions of potassium dichromate. Positive...

THE EFFECT OF IRON ION TO THE REMOVAL OF NICKEL ION FROM ELECTROPLATING WASTEWATER USING DOUBLE CHAMBER ELECTRODEPOSITION CELL (DCEC REACTOR

Directory of Open Access Journals (Sweden)

Djaenudin Djaenudin

2017-05-01

Full Text Available Modern society demands industrial technology advances to produce products that have high durability and long utilization lives. Materials made from ferrous metal become a solution to meet these industry needs. Ferrous metal is corrosive and it requires more care to support the performance. Electroplating or metal coating applied to iron or nickel solves this problem. In the production process, the usage of nickel is only 30%-40% and the remaining 60-70% is wasted through effluent. Nickel is a toxic heavy metal that can cause cancer. The purpose of this study is to evaluate the effect of iron concentration on nickel metal removal in electroplating wastewater using an insulated electrolytic reactor double chamber electrodeposition cell (DCEC. The result of this study shows that any ratio variation of iron concentration to nickel gives varying impacts on nickel removal efficiency, electric current efficiency, and specific energy. On the fourth variation, the iron ratio of 1.29% removed 83.1% nickel (the highest removal efficiency at the cost of 20.687 kWh / kg specific energy. The number is extremely high for energy needs. On the other hand, the variation of iron ratio of 1.73% consumpting only 15.067 kWh / kg, the lowest specific energy needs, resulted in the lowest removal efficiency of 63.6%.

Mineralogical issues in long-term corrosion of iron and iron-nickel alloys

International Nuclear Information System (INIS)

VanOrden, A.C.; McNeil, M.B.

1988-01-01

Prediction of very long term corrosion behavior of buried objects in general requires taking into account that the corrosion processes themselves after the local conditions. Recent work has analyzed corrosion processes in terms of trajectories on Pourbaix diagrams and appears to offer the prospect for using short-term corrosion tests to project corrosion behavior over very long periods. Two different classes of materials are considered here: essentially pure iron, which is an analogue to the carbon steel design overpacks for the salt and basalt sites (on which work has been suspended at present, and iron-nickel alloys, which are the best analogues available for some of the alloys being considered on the tuff site. There are a number of sources of data on corrosion of iron over archaeological times; the data used in this paper are from the recent National Bureau of Standards work on Roman iron nails for Inchtuthill in Scotland, which can be dated fairly precisely to about 70 A.D. and whose method of production is understood. The only available source of natural-analogue data on Fe-Ni alloys is the corrosion of meteorites

Evaluation of effect of recasting of nickel-chromium alloy on its castability using different investment materials: An in vitro study

Directory of Open Access Journals (Sweden)

Abhinav Sharma

2016-01-01

Conclusions: Within the limitations of the study, it was concluded that there was no significant difference found in castability of different percentage combinations of new and once casted alloy using two investment materials. The addition of new alloy during recasting to maintain the castability of nickel-chromium alloy may therefore not be required.

Thermodynamic properties of compounds of Na2O with the oxides of chromium, nickel, and iron

International Nuclear Information System (INIS)

Shaiu, B.J.

1976-10-01

Results of emf measurements on Na 2 O solid electrolytes in binary compounds with Cr 2 O 3 , FeO, and NiO are presented along with thermodynamic properties of these compounds. It was found that reliable thermodynamic data for compounds of NaCrO 2 , Na 2 FeO 2 , NaFeO 2 , Na 2 NiO 2 , and NaNiO 2 at 500 to 800 0 can be obtained by using emf measurements with solid electrolyte cells. The pretreatment of heating the cells in a vacuum of 10 -2 torr at 500 0 C or above for about 12 hours causes the emf dependence on temperature to be very small. The measurements were carried out over the temperature range in which no phase transformations occurred, the ΔC/sub p/ for the compounds involved was reasonably considered as approximately zero. Linear emf-temperature plots were therefore expected for these cells and the equation of ΔG 0 /sub f/ was indeed valid for constant values of ΔH 0 /sub f/ and ΔS 0 /sub f/. The formation of compound NaCrO 2 is thermodynamically favorable in a sodium loop made of austenic stainless steels. The critical oxygen concentration for the formation of NaCrO 2 shows that it is stable in liquid sodium in temperature range from 400 to 1100 0 C and Cr 2 O 3 does not exist with the double oxide in liquid sodium. The existence temperature for (Na 2 O) 2 .FeO in equilibrium with oxygen saturated liquid sodium is 693 0 K or above, for Na 2 FeO 2 it is 1141 0 K or above and for NaFeO 2 it is greater than or equal to 1173 0 K. The double oxides of nickel with sodium oxide are much less stable than the iron double oxides and do therefore not exist in liquid sodium. The nickel in austenitic stainless steel shows the least attack by oxygen saturated liquid sodium

Effect of iron and chromium on the graphitization behaviour of sulfur-containing carbon

International Nuclear Information System (INIS)

Tyumentsev, V.A.; Belenkov, E.A.; Saunina, S.I.; Podkopaev, S.A.; Shvejkin, G.P.

1998-01-01

Process of transition of carbonaceous material, containing structurally incorporated sulfur, into graphite and impact of iron and chromium additions are studied. It is established that carbonaceous material, containing more than 1.5 mass % S and also 1.5 mass % Cr 2 O 3 is heterogeneous after thermal treatment at 1300-1600 deg C. It consists of large and sufficiency complete areas of coherent scattering having graphite structure and ultra-dispersed matrix. The number of graphite crystals formed in the presence of dispersed iron within this temperature range, decreases by two times [ru

Quantitative analysis of chromium concentration in nickel based alloys by laser induced breakdown spectroscopy at atmospheric pressure using a nanosecond ultraviolet Nd:YAG laser

International Nuclear Information System (INIS)

Gupta, G.P.; Suri, B.M.; Verma, A.; Sundararaman, M.; Unnikrishnan, V.K.; Alti, K.; Kartha, V.B.; Santhosh, C.

2010-01-01

Laser-induced breakdown spectroscopy (LIBS) has been well recognized as a simple, fast and direct analytical technique of elemental analysis of multi-element materials by a number of research groups all over the world. It is based on the focusing of a high-power pulsed laser beam with a power density > 100 MW/cm 2 onto a sample surface followed by optical emission spectroscopy of the plasma produced over the surface. In the present work, they have carried out the quantitative analysis of chromium in nickel-based-alloys using laser-induced breakdown spectroscopy (LIBS) in air at atmospheric pressure. In the present work the quantitative analysis of chromium in nickel-based-alloys using laser-induced break-down spectroscopy (LIBS) in air at atmospheric pressure has been carried out

Nickel speciation in several serpentine (ultramafic) topsoils via bulk synchrotron-based techniques

Energy Technology Data Exchange (ETDEWEB)

Siebecker, Matthew G.; Chaney, Rufus L.; Sparks, Donald L.

2017-07-01

Serpentine soils have elevated concentrations of trace metals including nickel, cobalt, and chromium compared to non-serpentine soils. Identifying the nickel bearing minerals allows for prediction of potential mobility of nickel. Synchrotron-based techniques can identify the solid-phase chemical forms of nickel with minimal sample treatment. Element concentrations are known to vary among soil particle sizes in serpentine soils. Sonication is a useful method to physically disperse sand, silt and clay particles in soils. Synchrotron-based techniques and sonication were employed to identify nickel species in discrete particle size fractions in several serpentine (ultramafic) topsoils to better understand solid-phase nickel geochemistry. Nickel commonly resided in primary serpentine parent material such as layered-phyllosilicate and chain-inosilicate minerals and was associated with iron oxides. In the clay fractions, nickel was associated with iron oxides and primary serpentine minerals, such as lizardite. Linear combination fitting (LCF) was used to characterize nickel species. Total metal concentration did not correlate with nickel speciation and is not an indicator of the major nickel species in the soil. Differences in soil texture were related to different nickel speciation for several particle size fractionated samples. A discussion on LCF illustrates the importance of choosing standards based not only on statistical methods such as Target Transformation but also on sample mineralogy and particle size. Results from the F-test (Hamilton test), which is an underutilized tool in the literature for LCF in soils, highlight its usefulness to determine the appropriate number of standards to for LCF. EXAFS shell fitting illustrates that destructive interference commonly found for light and heavy elements in layered double hydroxides and in phyllosilicates also can occur in inosilicate minerals, causing similar structural features and leading to false positive results in

Effect of molybdenum, vanadium, boron on mechanical properties of high chromium white cast iron in as-cast condition

Science.gov (United States)

Nurjaman, F.; Sumardi, S.; Shofi, A.; Aryati, M.; Suharno, B.

2016-02-01

In this experiment, the effect of the addition carbide forming elements on high chromium white cast iron, such as molybdenum, vanadium and boron on its mechanical properties and microstructure was investigated. The high chromium white cast iron was produced by casting process and formed in 50 mm size of grinding balls with several compositions. Characterization of these grinding balls was conducted by using some testing methods, such as: chemical and microstructure analysis, hardness, and impact test. From the results, the addition of molybdenum, vanadium, and boron on high chromium white cast iron provided a significant improvement on its hardness, but reduced its toughness. Molybdenum induced fully austenitic matrix and Mo2C formation among eutectic M7C3 carbide. Vanadium was dissolved in the matrix and carbide. While boron was played a role to form fine eutectic carbide. Grinding balls with 1.89 C-13.1 Cr-1.32 Mo-1.36 V-0.00051 B in as-cast condition had the highest hardness, which was caused by finer structure of eutectic carbide, needle like structure (upper bainite) matrix, and martensite on its carbide boundary.

Enhanced aerobic degradation of 4-chlorophenol with iron-nickel nanoparticles

Energy Technology Data Exchange (ETDEWEB)

Shen, Wenjuan; Mu, Yi; Wang, Bingning; Ai, Zhihui, E-mail: jennifer.ai@mail.ccnu.edu.cn; Zhang, Lizhi

2017-01-30

Highlights: • Bimetallic iron-nickel nanoparticles possessed an enhanced performance on aerobic degradation of 4-CP. • Hydroxyl radicals were the major active species contributed to aerobic 4-CP degradation with nZVI. • Superoxide radicals predominated the 4-CP degradation in the nZVIN/Air process. • The 4-CP degradation pathways were dependent on the generated superoxide radicals in the nZVIN/Air process. - Abstract: In this study, we demonstrate that the bimetallic iron-nickel nanoparticles (nZVIN) possessed an enhanced performance in comparison with nanoscale zero-valent iron (nZVI) on aerobic degradation of 4-chlorophenol (4-CP). The 4-CP degradation rate constant in the aerobic nZVIN process (nZVIN/Air) was 5 times that in the classic nZVI counterpart system (nZVI/Air). Both reactive oxygen species measurement and inhibition experimental results suggested that hydroxyl radicals were the major active species contributed to aerobic 4-CP degradation with nZVI, on contrast, superoxide radicals predominated the 4-CP degradation in the nZVIN/Air process. High performance liquid chromatography and gas chromatography-mass spectrometer analysis indicated the intermediates of the nZVI/Air system were p-benzoquinone and hydroquinone, which were resulted from the bond cleavage between the chlorine and carbon atom in the benzene ring by hydroxyl radicals. However, the primary intermediates of 4-CP found in the nZVIN/Air system were phenol via the direct dechlorination by superoxide radicals, accompanying with the formation of chloride ions. On the base of experimental results, a superoxide radicals mediated enhancing mechanism was proposed for the aerobic degradation of 4-CP in the nZVIN/Air system. This study provides new insight into the role of bimetallic nickel on enhancing removal of organic pollutants with nZVI.

Contact eczema and tumors caused by chromium, nickel and their compounds. An evaluation of occupational diseases approved from 1978 until 1984

Energy Technology Data Exchange (ETDEWEB)

Wardenbach, P.; Henter, A.; Kollmeier, H.

1989-07-01

The majority of the approved occupational diseases caused by chromium, nickel and their compounds are contact eczema. Only in chemical workers contact eczema and tumors of the respiratory tract are recognized with a comparable frequency. Within the textile and leather branche no contact exzema were caused by chromium. It is conceivable that technology changes and/or substitution of sensitizing chromium compounds in tanning entailed a considerable decrease of this disease. Quantitative data of exposures, which caused the recently observed tumors of the respiratory tract, are not available. From recently published workplace measurements it can be deduced that at the corresponding workplaces even nowadays the heaviest exposures exist. As the formerly established MAK values are nearly identical with the current TRK values a reevaluation of the latter should be performed. (orig.).

Suitability of Nickel Chromium Wire Cutters as Deployable Release Mechanisms on CubeSats in Low Earth Orbit

OpenAIRE

Gardiner, James

2015-01-01

This paper investigates the suitability of a nickel chromium wire cutter (NCWC) for use on the GASPACS (Get Away Special Passive Attitude Control Satellite) Mission. It is intended that when activated the NCWC will cut through a restraining wire and thereby release the stored energy of the deployable AeroBoom. Flight worthiness is based on favorable performance during functional testing to address known issues with the NCWC, such as wire burn through and cutting issues. In-depth testing discu...

Accumulation and distribution of iron, cadmium, lead and nickel in cucumber plants grown in hydroponics containing two different chelated iron supplies.

Science.gov (United States)

Csog, Árpád; Mihucz, Victor G; Tatár, Eniko; Fodor, Ferenc; Virág, István; Majdik, Cornelia; Záray, Gyula

2011-07-01

Cucumber plants grown in hydroponics containing 10 μM Cd(II), Ni(II) and Pb(II), and iron supplied as Fe(III) EDTA or Fe(III) citrate in identical concentrations, were investigated by total-reflection X-ray fluorescence spectrometry with special emphasis on the determination of iron accumulation and distribution within the different plant compartments (root, stem, cotyledon and leaves). The extent of Cd, Ni and Pb accumulation and distribution were also determined. Generally, iron and heavy-metal contaminant accumulation was higher when Fe(III) citrate was used. The accumulation of nickel and lead was higher by about 20% and 100%, respectively, if the iron supply was Fe(III) citrate. The accumulation of Cd was similar. In the case of Fe(III) citrate, the total amounts of Fe taken up were similar in the control and heavy-metal-treated plants (27-31 μmol/plant). Further, the amounts of iron transported from the root towards the shoot of the control, lead- and nickel-contaminated plants were independent of the iron(III) form. Although Fe mobility could be characterized as being low, its distribution within the shoot was not significantly affected by the heavy metals investigated. Copyright © 2011 Elsevier GmbH. All rights reserved.

Kinetics of passivation of a nickel-base alloy in high temperature water

Energy Technology Data Exchange (ETDEWEB)

Machet, A. [Laboratoire de Physico-Chimie des Surfaces, CNRS-ENSCP (UMR 7045), Ecole Nationale Superieure de Chimie de Paris, Universite Pierre et Marie Curie, F-75231 Paris cedex 05 (France)]|[Framatome ANP, Tour AREVA, F-92084 Paris-la-Defense (France); Galtayries, A.; Zanna, S.; Marcus, P. [Laboratoire de Physico-Chimie des Surfaces, CNRS-ENSCP (UMR 7045), Ecole Nationale Superieure de Chimie de Paris, Universite Pierre et Marie Curie, F-75231 Paris cedex 05 (France); Jolivet, P.; Scott, P. [Framatome ANP, Tour AREVA, F-92084 Paris-la-Defense (France); Foucault, M.; Combrade, P. [Framatome ANP, Centre Technique, F-71205 Le Creusot (France)

2004-07-01

The kinetics of passivation and the composition of the surface oxide layer, in high temperature and high pressure water, of a nickel-chromium-iron alloy (Alloy 600) have been investigated by X-ray Photoelectron Spectroscopy (XPS). The samples have been exposed for short (0.4 - 8.2 min) and longer (0 - 400 hours) time periods to high temperature (325 deg. C) and high pressure water (containing boron and lithium) under controlled hydrogen pressure. The experiments were performed in two types of autoclaves: a novel autoclave dedicated to short time periods and a classic static autoclave for the longer exposures. In the initial stage of passivation, a continuous ultra-thin layer of chromium oxide (Cr{sub 2}O{sub 3}) is rapidly formed on the surface with an external layer of chromium hydroxide. For longer times of passivation, the oxide layer is in a duplex form with an internal chromium oxide layer and an external layer of nickel hydroxide. The growth of the internal Cr{sub 2}O{sub 3} oxide layer has been fitted by three classical models (parabolic, logarithmic and inverse logarithmic laws) for the short passivation times, and the growth curves have been extrapolated to longer passivation periods. The comparison with the experimental results reveals that the kinetics of passivation of Alloy 600 in high temperature and high pressure water, for passivation times up to 400 hours, is well fitted by a logarithmic growth law. (authors)

Kinetics of passivation of a nickel-base alloy in high temperature water

International Nuclear Information System (INIS)

Machet, A.; Galtayries, A.; Zanna, S.; Marcus, P.; Jolivet, P.; Scott, P.; Foucault, M.; Combrade, P.

2004-01-01

The kinetics of passivation and the composition of the surface oxide layer, in high temperature and high pressure water, of a nickel-chromium-iron alloy (Alloy 600) have been investigated by X-ray Photoelectron Spectroscopy (XPS). The samples have been exposed for short (0.4 - 8.2 min) and longer (0 - 400 hours) time periods to high temperature (325 deg. C) and high pressure water (containing boron and lithium) under controlled hydrogen pressure. The experiments were performed in two types of autoclaves: a novel autoclave dedicated to short time periods and a classic static autoclave for the longer exposures. In the initial stage of passivation, a continuous ultra-thin layer of chromium oxide (Cr 2 O 3 ) is rapidly formed on the surface with an external layer of chromium hydroxide. For longer times of passivation, the oxide layer is in a duplex form with an internal chromium oxide layer and an external layer of nickel hydroxide. The growth of the internal Cr 2 O 3 oxide layer has been fitted by three classical models (parabolic, logarithmic and inverse logarithmic laws) for the short passivation times, and the growth curves have been extrapolated to longer passivation periods. The comparison with the experimental results reveals that the kinetics of passivation of Alloy 600 in high temperature and high pressure water, for passivation times up to 400 hours, is well fitted by a logarithmic growth law. (authors)

Corrosion Characterization in Nickel Plated 110 ksi Low Alloy Steel and Incoloy 925: An Experimental Case Study

Science.gov (United States)

Thomas, Kiran; Vincent, S.; Barbadikar, Dipika; Kumar, Shresh; Anwar, Rebin; Fernandes, Nevil

2018-04-01

Incoloy 925 is an age hardenable Nickel-Iron-Chromium alloy with the addition of Molybdenum, Copper, Titanium and Aluminium used in many applications in oil and gas industry. Nickel alloys are preferred mostly in corrosive environments where there is high concentration of H2S, CO2, chlorides and free Sulphur as sufficient nickel content provides protection against chloride-ion stress-corrosion cracking. But unfortunately, Nickel alloys are very expensive. Plating an alloy steel part with nickel would cost much lesser than a part make of nickel alloy for large quantities. A brief study will be carried out to compare the performance of nickel plated alloy steel with that of an Incoloy 925 part by conducting corrosion tests. Tests will be carried out using different coating thicknesses of Nickel on low alloy steel in 0.1 M NaCl solution and results will be verified. From the test results we can confirm that Nickel plated low alloy steel is found to exhibit fairly good corrosion in comparison with Incoloy 925 and thus can be an excellent candidate to replace Incoloy materials.

Aluminium alloys containing iron and nickel; Alliages d'aluminium contenant du fer et du nickel

Energy Technology Data Exchange (ETDEWEB)

Coriou, H.; Fournier, R.; Grall, L.; Hure, J. [Commissariat a l' Energie atomique, Centre d' Etudes Nucleaires de Saclay, Departement de Metallurgie et de Chimie Appliquee (France); Herenguel, J.; Lelong, P. [Centre de Recherches d' Antony, des Trefileries et Laminoirs du Havre (France)

1958-07-01

The first part of this report addresses mechanism, kinetics and structure factors of aluminium alloys containing iron and nickel in water and high temperature steam. The studied alloys contain from 0.3 to 0.7 per cent of iron, and 0.2 to 1.0 per cent of nickel. Corrosion resistance and corrosion structure have been studied. The experimental installation, process and samples are presented. Corrosion structures in water at 350 C are identified and discussed (structure of corrosion products, structure of metal-oxide interface), and then in steam at different temperatures (350-395 C). Corrosion kinetics is experimentally studied (weight variation in time) in water at 350 C and in steam at different temperatures. Reactions occurring at over-heated steam (more than 400 C) are studied, and the case of welded alloys is also addressed. The second part addresses the metallurgical mechanism and processes influencing aluminium alloy resistance to corrosion by high temperature water as it appeared that separated phases protect the solid solution through a neighbourhood action. In order to avoid deep local corrosions, it seems necessary to multiply protective phases in an as uniform as possible way. Some processes enabling this result are described. They belong to conventional metallurgy or to powder metallurgy (with sintering and extrusion)

Reliability and validity of expert assessment based on airborne and urinary measures of nickel and chromium exposure in the electroplating industry

Science.gov (United States)

Chen, Yu-Cheng; Coble, Joseph B; Deziel, Nicole C.; Ji, Bu-Tian; Xue, Shouzheng; Lu, Wei; Stewart, Patricia A; Friesen, Melissa C

2014-01-01

The reliability and validity of six experts’ exposure ratings were evaluated for 64 nickel-exposed and 72 chromium-exposed workers from six Shanghai electroplating plants based on airborne and urinary nickel and chromium measurements. Three industrial hygienists and three occupational physicians independently ranked the exposure intensity of each metal on an ordinal scale (1–4) for each worker's job in two rounds: the first round was based on responses to an occupational history questionnaire and the second round also included responses to an electroplating industry-specific questionnaire. Spearman correlation (rs) was used to compare each rating's validity to its corresponding subject-specific arithmetic mean of four airborne or four urinary measurements. Reliability was moderately-high (weighted kappa range=0.60–0.64). Validity was poor to moderate (rs= -0.37–0.46) for both airborne and urinary concentrations of both metals. For airborne nickel concentrations, validity differed by plant. For dichotomized metrics, sensitivity and specificity were higher based on urinary measurements (47–78%) than airborne measurements (16–50%). Few patterns were observed by metal, assessment round, or expert type. These results suggest that, for electroplating exposures, experts can achieve moderately-high agreement and (reasonably) distinguish between low and high exposures when reviewing responses to in-depth questionnaires used in population-based case-control studies. PMID:24736099

Reliability and validity of expert assessment based on airborne and urinary measures of nickel and chromium exposure in the electroplating industry.

Science.gov (United States)

Chen, Yu-Cheng; Coble, Joseph B; Deziel, Nicole C; Ji, Bu-Tian; Xue, Shouzheng; Lu, Wei; Stewart, Patricia A; Friesen, Melissa C

2014-11-01

The reliability and validity of six experts' exposure ratings were evaluated for 64 nickel-exposed and 72 chromium-exposed workers from six Shanghai electroplating plants based on airborne and urinary nickel and chromium measurements. Three industrial hygienists and three occupational physicians independently ranked the exposure intensity of each metal on an ordinal scale (1-4) for each worker's job in two rounds: the first round was based on responses to an occupational history questionnaire and the second round also included responses to an electroplating industry-specific questionnaire. The Spearman correlation (r(s)) was used to compare each rating's validity to its corresponding subject-specific arithmetic mean of four airborne or four urinary measurements. Reliability was moderately high (weighted kappa range=0.60-0.64). Validity was poor to moderate (r(s)=-0.37-0.46) for both airborne and urinary concentrations of both metals. For airborne nickel concentrations, validity differed by plant. For dichotomized metrics, sensitivity and specificity were higher based on urinary measurements (47-78%) than airborne measurements (16-50%). Few patterns were observed by metal, assessment round, or expert type. These results suggest that, for electroplating exposures, experts can achieve moderately high agreement and (reasonably) distinguish between low and high exposures when reviewing responses to in-depth questionnaires used in population-based case-control studies.

Electrical and magnetic behavior of iron doped nickel titanate (Fe{sup 3+}/NiTiO{sub 3}) magnetic nanoparticles

Energy Technology Data Exchange (ETDEWEB)

Lenin, Nayagam; Karthik, Arumugam; Sridharpanday, Mathu; Selvam, Mohanraj; Srither, Saturappan Ravisekaran; Arunmetha, Sundarmoorthy; Paramasivam, Palanisamy; Rajendran, Venkatachalam, E-mail: veerajendran@gmail.com

2016-01-01

Iron doped nickel titanate (Fe{sup 3+}/NiTiO{sub 3}) ferromagnetic nanoparticles with different concentrations of Fe (0.2, 0.4, and 0.6 mol) were synthesized using precipitation route with precursor source such as nickel nitrate and iron nitrate solutions. The prepared magnetic nanopowders were investigated through X-ray diffraction (XRD), Fourier transform infrared, scanning electron microscope, X-ray fluorescence, Brunauer–Emmett–Teller, vibrating sample magnetometer, and electrochemical impedance spectroscopy to explore the structural, ferromagnetic, and dielectric properties. The obtained XRD pattern shows formation of iron doped nickel titanate in orthorhombic structure. The crystallite size ranges from 57 to 21 nm and specific surface area ranges from 11 to 137 m{sup 2} g{sup −1}. The hysteresis loops of nanomagnetic materials show ferromagnetic behavior with higher magnitude of coercivity (H{sub c}) 867–462 Oe. The impedance analysis of ferromagnetic materials explores the ferro-dielectric behavior with enhanced properties of Fe{sup 3+}/NiTiO{sub 3} nanoparticles at higher Fe content. - Highlights: • Iron doped nickel titanate magnetic nanoparticles. • Ferromagnetic magnetism behavior with higher magnitude of coercivity. • Dielectric behavior of ferromagnetic nanoparticles with increase of Fe content.

Effect of Microstructures on Working Properties of Nickel-Manganese-Copper Cast Iron

Directory of Open Access Journals (Sweden)

Daniel Medyński

2018-05-01

Full Text Available In the paper, the effects, on basic usable properties (abrasive wear and corrosion resistance, of solidification (acc. to the stable and non-stable equilibrium system and transformations occurring in the matrix during the cooling of castings of Ni-Mn-Cu cast iron were determined. Abrasive wear resistance was mainly determined by the types and arrangements of high-carbon phases (indicated by eutectic saturation degree, and the kinds of matrices (indicated by the nickel equivalent value, calculated from chemical composition. The highest abrasive wear resistance was found for white cast iron, with the highest degree of austenite to martensite transformation occurring in its matrix. Irrespective of solidification, a decrease of the equivalent value below a limit value resulted in increased austenite transformation, and thus, to a significant rise in hardness and abrasive wear resistance for the castings. At the same time, corrosion resistance of the alloy was slightly reduced. The examinations showed that corrosion resistance of Ni-Mn-Cu cast iron is, too a much lesser degree, decided by the means of solidification of the castings, rather than transformations occurring in the matrix, as controlled by nickel equivalent value (especially elements with high electrochemical potential.

Chromium(VI) release from leather and metals can be detected with a diphenylcarbazide spot test

DEFF Research Database (Denmark)

Bregnbak, David; Johansen, Jeanne D.; Jellesen, Morten Stendahl

2015-01-01

Along with chromium, nickel and cobalt are the clinically most important metal allergens. However, unlike for nickel and cobalt, there is no validated colorimetric spot test that detects chromium. Such a test could help both clinicians and their patients with chromium dermatitis to identify culprit...... exposures. To evaluate the use of diphenylcarbazide (DPC) as a spot test reagent for the identification of chromium(VI) release. A colorimetric chromium(VI) spot test based on DPC was prepared and used on different items from small market surveys. The DPC spot test was able to identify chromium(VI) release...

Evaluation of some emitted elements from selected small industries in Khartoum state

International Nuclear Information System (INIS)

Elboraie, Mahir Zein Elabdeen

1999-08-01

Employing x-ray fluorescence spectrometry, levels of calcium, chromium, iron, cobalt, nickel, copper, zinc and lead in the indoor aerosol environment of nile painting company, battery charging shop, Khartoum university printing press, Mirghany workshop, Burri power station and Sudanese mint company industries were measured. In the Nile painting company site, calcium, cobalt, nickel and lead exhibited high levels of concentration, whilst chromium, and copper displayed relatively high values with respect to their levels in the control site (Tutti Island). Iron exhibited a level nearly identical to that measured at the control site. No emission of zinc was monitored. In Battery Charging Shop site, Iron and lead, displayed the highest levels recorded, and calcium, chromium, copper, exhibited concentrations relatively high than the corresponding levels in the control site. Cobalt, nickel, and zinc have not been detected. The same trending was found in Khartoum University Printing Press site, with the exception that the level of iron is relatively high with respect to that of control site. In Mirghany Workshop site, calcium, iron, nickel, and zinc measured the highest values. Chromium, copper, and lead measured relatively high values with respect to their concentrations in the control site. No emission of cobalt was monitored. The average concentrations of calcium, iron, copper, and lead in Burri Power Station were nearly the same with that control site. Chromium, cobalt, nickel, and zinc, however, were not detected. In the indoor aerosol of Sudanese Mint Company site, cobalt, nickel, copper, and zinc, measured the highest values, whilst calcium, iron, chromium, and lead, displayed relatively high values with respect to their concentrations in the control site. The average concentrations of the elements under study in the indoor and outdoor aerosols of Sudanese Mint Company do not correlate to each other, but the outdoor measurements nearly resemble to those of the

Cyclic Oxidation and Hot Corrosion Behavior of Nickel-Iron-Based Superalloy

Science.gov (United States)

Chellaganesh, D.; Adam Khan, M.; Winowlin Jappes, J. T.; Sathiyanarayanan, S.

2018-01-01

The high temperature oxidation and hot corrosion behavior of nickel-iron-based superalloy are studied at 900 ° and 1000 °C. The significant role of alloying elements with respect to the exposed medium is studied in detail. The mass change per unit area was catastrophic for the samples exposed at 1000 °C and gradual increase in mass change was observed at 900 °C for both the environments. The exposed samples were further investigated with SEM, EDS and XRD analysis to study the metallurgical characteristics. The surface morphology has expressed the in situ nature of the alloy and its affinity toward the environment. The EDS and XRD analysis has evidently proved the presence of protective oxides formation on prolonged exposure at elevated temperature. The predominant oxide formed during the exposure at high temperature has a major contribution toward the protection of the samples. The nickel-iron-based superalloy is less prone to oxidation and hot corrosion when compared to the existing alloy in gas turbine engine simulating marine environment.

A compact and low cost laser induced breakdown spectroscopic system: Application for simultaneous determination of chromium and nickel in steel using multivariate calibration

Energy Technology Data Exchange (ETDEWEB)

Barbieri Gonzaga, Fabiano [Chemical Metrology Division, National Institute of Metrology, Quality and Technology, Av. N. S. das Gracas, 50, Xerem, 25250-020, Duque de Caxias, RJ (Brazil); Pasquini, Celio, E-mail: pasquini@iqm.unicamp.br [Institute of Chemistry, State University of Campinas, POB 6154, 13083-970, Campinas, SP (Brazil)

2012-03-15

This work describes a compact and low cost analyzer for laser induced breakdown spectroscopy (LIBS) based on a diode pumped passively Q-switched Nd:LSB microchip laser and a conventional Czerny-Turner spectrograph (spectral range from about 250 to 390 nm) containing a non-intensified, non-gated and non-cooled 1024 pixel linear sensor array. The new LIBS instrument was applied for analyzing steel samples containing chromium and nickel in the concentration range from about 5 to 26% w/w (certified reference materials), integrating the emitted radiation for 40 s under continuous application of laser pulses at 2 kHz for each acquired spectrum (integration of about 80,000 plasmas). The emission data from about 356 to 362 nm and 340 to 354 nm were employed for the construction of two Partial Least Squares (PLS) calibration models for determination of chromium and nickel, respectively. The average relative errors of prediction of chromium and nickel concentrations were 3.7 and 6.7%, respectively, which are similar to or lower than those obtained using higher cost LIBS analyzers. The results have shown that multivariate calibration can help to overcome the decreasing instrumental performance associated with the low cost equipment. - Highlights: Black-Right-Pointing-Pointer Low cost laser induced breakdown spectroscopy instrumentation. Black-Right-Pointing-Pointer Microchip laser based LIBS system. Black-Right-Pointing-Pointer Standard non-intensified, non-gated, non-cooled detector for LIBS system. Black-Right-Pointing-Pointer Improvement of results from a low cost LIBS system using multivariate calibration. Black-Right-Pointing-Pointer Cr and Ni determination in steel by a low cost LIBS system.

Effect of nickel monolayer deposition on the structural and electronic properties of the low miller indices of (bcc) iron : A DFT study

NARCIS (Netherlands)

Kwawu, Caroline; Tia, Richard; Adei, Evans; Dzade, Nelson Y.; Catlow, Richard; de Leeuw, Nora H.

2017-01-01

Metal clusters of both iron (Fe) and nickel (Ni) have been found in nature as active electro-catalytic sites, for example in the enzyme carbon mono-oxide dehydrogenase found in autotrophic organisms. Thus, surface modification of iron with nickel could improve the surface work function to enhance

Surface passivity largely governs the bioaccessibility of nickel-based powder particles at human exposure conditions.

Science.gov (United States)

Hedberg, Yolanda S; Herting, Gunilla; Latvala, Siiri; Elihn, Karine; Karlsson, Hanna L; Odnevall Wallinder, Inger

2016-11-01

The European chemical framework REACH requires that hazards and risks posed by chemicals, including alloys and metals, are identified and proven safe for humans and the environment. Therefore, differences in bioaccessibility in terms of released metals in synthetic biological fluids (different pH (1.5-7.4) and composition) that are relevant for different human exposure routes (inhalation, ingestion, and dermal contact) have been assessed for powder particles of an alloy containing high levels of nickel (Inconel 718, 57 wt% nickel). This powder is compared with the bioaccessibility of two nickel-containing stainless steel powders (AISI 316L, 10-12% nickel) and with powders representing their main pure alloy constituents: two nickel metal powders (100% nickel), two iron metal powders and two chromium metal powders. X-ray photoelectron spectroscopy, microscopy, light scattering, and nitrogen absorption were employed for the particle and surface oxide characterization. Atomic absorption spectroscopy was used to quantify released amounts of metals in solution. Cytotoxicity (Alamar blue assay) and DNA damage (comet assay) of the Inconel powder were assessed following exposure of the human lung cell line A549, as well as its ability to generate reactive oxygen species (DCFH-DA assay). Despite its high nickel content, the Inconel alloy powder did not release any significant amounts of metals and did not induce any toxic response. It is concluded, that this is related to the high surface passivity of the Inconel powder governed by its chromium-rich surface oxide. Read-across from the pure metal constituents is hence not recommended either for this or any other passive alloy. Copyright © 2016 The Author(s). Published by Elsevier Inc. All rights reserved.

Iron-nickel alloys as canister material for radioactive waste disposal in underground repositories

International Nuclear Information System (INIS)

Apps, J.A.

1982-01-01

Canisters containing high-level radioactive waste must retain their integrity in an underground waste repository for at least one thousand years after burial (Nuclear Regulatory Commission, 1981). Since no direct means of verifying canister integrity is plausible over such a long period, indirect methods must be chosen. A persuasive approach is to examine the natural environment and find a suitable material which is thermodynamically compatible with the host rock under the environmental conditions with the host rock under the environmental conditions expected in a waste repository. Several candidates have been proposed, among them being iron-nickel alloys that are known to occur naturally in altered ultramafic rocks. The following review of stability relations among iron-nickel alloys below 350 0 C is the initial phase of a more detailed evaluation of these alloys as suitable canister materials

Thermodynamic Properties of Chromium Adsorption by Sediments ...

African Journals Online (AJOL)

MBI

2013-06-19

Jun 19, 2013 ... The adsorption of Chromium from aqueous solution using river Watari sediment as an adsorbent was modeled. The influence of initial ... number of metals, including chromium, copper, nickel and zinc. The ion ... through filter paper to determine the concentration ... liquid and solid phases were separated by.

Nickel extraction from nickel matte

Science.gov (United States)

Subagja, R.

2018-01-01

In present work, the results of research activities to make nickel metal from nickel matte are presented. The research activities were covering a) nickel matte characterization using Inductively Couple plasma (ICP), Electron Probe Micro Analyzer (EPMA) and X-Ray Diffraction (XRD), b) nickel matte dissolution process to dissolve nickel from nickel matte into the spent electrolyte solutions that contains hydrochloric acid, c) purification of nickel chloride leach solution by copper cementation process to remove copper using nickel matte, selective precipitation process to remove iron, solvent extraction using Tri normal octyl amine to separate cobalt from nickel chloride solutions and d) Nickel electro winning process to precipitate nickel into the cathode surface from purified nickel chloride solution by using direct current. The research activities created 99, 72 % pure nickel metal as the final product of the process.

Solidification structure and abrasion resistance of high chromium white irons

Science.gov (United States)

Doğan, Ö. N.; Hawk, J. A.; Laird, G.

1997-06-01

Superior abrasive wear resistance, combined with relatively low production costs, makes high Cr white cast irons (WCIs) particularly attractive for applications in the grinding, milling, and pumping apparatus used to process hard materials. Hypoeutectic, eutectic, and hypereutectic cast iron compositions, containing either 15 or 26 wt pct chromium, were studied with respect to the macrostructural transitions of the castings, solidification paths, and resulting microstructures when poured with varying superheats. Completely equiaxed macrostructures were produced in thick section castings with slightly hypereutectic compositions. High-stress abrasive wear tests were then performed on the various alloys to examine the influence of both macrostructure and microstructure on wear resistance. Results indicated that the alloys with a primarily austenitic matrix had a higher abrasion resistance than similar alloys with a pearlitic/bainitic matrix. Improvement in abrasion resistance was partially attributed to the ability of the austenite to transform to martensite at the wear surface during the abrasion process.

Polymeric precursors method for obtaining pigments based on Inorganic oxides of chromium and iron deposited on TiO2

International Nuclear Information System (INIS)

Silva, Everlania M. da; Galvao, Sheila B.; Paskocimas, C.A.

2011-01-01

The case study was the use of chromium oxides and iron, as a precursor in the synthesis of inorganic pigments. The synthesis was based on the dissolution of citric acid as a complexing agent, addition of metal oxides, such as ion chromophores; polymerization with ethylene glycol and doping with titanium oxide. Going through pre-calcination, breakdown, calcination at different temperatures (700, 900 and 1100 deg C resulting in pigments: green for pigment and chromium deposited on TiO2, orange for iron on TiO2. The thermal analysis (TG and DTA), evaluated their thermal decompositions, the XRD revealed the formation of crystalline phases such as iron titanate and chrome titanate; SEM showed the formation of hexagonal particles for both oxides. Under the different analysis, one can see the potential stability of pigments and powders, can be proposed its use as pigments in polymers. (author)

Influence of nickel and nitrogen on the structure workability and mechanical properties of weld-deposited high-chromium metal

International Nuclear Information System (INIS)

Krasavchikov, V.A.; Solov'eva, L.I.

1984-01-01

Results are presented of investigation into the effect of austenite-forming elements (nitrogen and nickel) on the structure, mechanical properties and workability durina weld deposition and on the hardness after heat treatment of the Kh32N8M2 alloy forming the sigma-phase. Nitrogen is stated to produce a stronger effect on the improvement of the workability at a minimum decrease in the hardness of the alloy being investigated. Changes in the mechanical properties and workability of the alloy are shown to take place at the expense of changes in the structural components, the austenite quantity in the structure as well as its arrangement and form being the determining factors. The effect of nickel- and nitrogen content on the sigma-phase formation is less noticeable as compared with their effect on austenization. It should be taken into account that in case of nickel and nitrogen alloying an essential part of nitrogen is bound in chromium nitrides, that is why a decrease in the alloy hardness under heat treatment is less noticeable with growing nitrogen concentration

Separation and Precipitation of Nickel from Acidic Sulfate Leaching Solution of Molybdenum-Nickel Black Shale by Potassium Nickel Sulfate Hexahydrate Crystallization

Science.gov (United States)

Deng, Zhigan; Wei, Chang; Fan, Gang; Li, Xingbin; Li, Minting; Li, Cunxiong

2018-02-01

Nickel was separated and precipitated with potassium nickel sulfate hexahydrate [K2Ni(SO4)2·6H2O] from acidic sulfate solution, a leach solution from molybdenum-nickel black shale. The effects of the potassium sulfate (K2SO4) concentration, crystallization temperature, solution pH, and crystallization time on nickel(II) recovery and iron(III) precipitation were investigated, revealing that nickel and iron were separated effectively. The optimum parameters were K2SO4 concentration of 200 g/L, crystallization temperature of 10°C, solution pH of 0.5, and crystallization time of 24 h. Under these conditions, 97.6% nickel(II) was recovered as K2Ni(SO4)2·6H2O crystals while only 2.0% of the total iron(III) was precipitated. After recrystallization, 98.4% pure K2Ni(SO4)2·6H2O crystals were obtained in the solids. The mother liquor was purified by hydrolysis-precipitation followed by cooling, and more than 99.0% K2SO4 could be crystallized. A process flowsheet was developed to separate iron(III) and nickel(II) from acidic-sulfate solution.

Kinetic study of the isotopic exchange of Na+ and Zn2+ ions on iron and chromium titanates

International Nuclear Information System (INIS)

Zakaria, E.S.; Ali, I.M.; Aly, H.F.

2004-01-01

Iron(III) (FeTi) and chromium (III) titanates (CrTi) were prepared as cation exchange materials in a granular form. The rate of the isotopic exchange of Na + /*Na + and Zn 2+ /*Zn 2+ between aqueous solution and iron(III) and chromium(III) titanates in Na + or Zn 2+ form has been carried out radiometrically in the 25-60 deg C temperature range. The exchange rate is controlled by a particle diffusion mechanism and experimental and theoretical approaches have been used to obtain the rate of diffusion through the spherical particles of the exchangers. The values of self diffusion (D-bar) of Na + and Zn 2+ ions were measured at different operation conditions, particle size, reaction temperatures and drying temperatures of the matrix. The values of kinetic and thermodynamic parameters were calculated and their significance discussed. (author)

Heat capacity of iron, aluminum, and chromium vanadates at high temperatures

Energy Technology Data Exchange (ETDEWEB)

Cheshnitskii, S.M.; Fotiev, A.A.; Ignashin, V.P.; Kesler, Y.A.

1985-09-01

The thermodynamic characteristics of compounds participating in the processing of vanadium-containing raw materials have not been sufficiently investigated. In this paper the authors report on measurements of the heat capacities of the compounds FeVO/sub 4/, CrVO/sub 4/, AIVO/sub 4/, Fe/sub 2/V/sub 4/O/sub 13/ and FeCr(VO/sub 4/)/sub 2/ at high temperatures. The obtained experimental data on the high-temperature heat capacity of iron, aluminum, and chromium vanadates makes it possible to calculate the thermodynamic functions of these compounds at high temperatures.

Cast thermally stable high temperature nickel-base alloys and casting made therefrom

International Nuclear Information System (INIS)

Acuncius, D.A.; Herchenroeder, R.B.; Kirchner, R.W.; Silence, W.L.

1977-01-01

A cast thermally stable high temperature nickel-base alloy characterized by superior oxidation resistance, sustainable hot strength and retention of ductility on aging is provided by maintaining the alloy chemistry within the composition molybdenum 13.7% to 15.5%; chromium 14.7% to 16.5%; carbon up to 0.1%, lanthanum in an effective amount to provide oxidation resistance up to 0.08%; boron up to 0.015%; manganese 0.3% to 1.0%; silicon 0.2% to 0.8%; cobalt up to 2.0%; iron up to 3.0%; tungsten up to 1.0%; copper up to 0.4%; phosphorous up to 0.02%; sulfur up to 0.015%; aluminum 0.1% to 0.5% and the balance nickel while maintaining the Nv number less than 2.31

Corrosion behavior of self-ligating and conventional metal brackets

Directory of Open Access Journals (Sweden)

Lúcio Henrique Esmeraldo Gurgel Maia

2014-04-01

Full Text Available Objective: To test the null hypothesis that the aging process in self-ligating brackets is not higher than in conventional brackets. Methods: Twenty-five conventional (GN-3M/Unitek; GE-GAC; VE-Aditek and 25 self-ligating (SCs-3M/Unitek; INs-GAC; ECs-Aditek metal brackets from three manufacturers (n = 150 were submitted to aging process in 0.9% NaCl solution at a constant temperature of 37 ± 1ºC for 21 days. The content of nickel, chromium and iron ions in the solution collected at intervals of 7, 14 and 21 days was quantified by atomic absorption spectrophotometry. After the aging process, the brackets were analyzed by scanning electron microscopy (SEM under 22X and 1,000X magnifications. Results: Comparison of metal release in self-ligating and conventional brackets from the same manufacturer proved that the SCs group released more nickel (p < 0.05 than the GN group after 7 and 14 days, but less chromium (p < 0.05 after 14 days and less iron (p < 0.05 at the three experimental time intervals. The INs group released less iron (p < 0.05 than the GE group after 7 days and less nickel, chromium and iron (p < 0.05 after 14 and 21 days. The ECs group released more nickel, chromium and iron (p < 0.05 than the VE group after 14 days, but released less nickel and chromium (p < 0.05 after 7 days and less chromium and iron (p < 0.05 after 21 days. The SEM analysis revealed alterations on surface topography of conventional and self-ligating brackets. Conclusions: The aging process in self-ligating brackets was not greater than in conventional brackets from the same manufacturer. The null hypothesis was accepted.

Performance enhancement of iron-chromium redox flow batteries by employing interdigitated flow fields

Science.gov (United States)

Zeng, Y. K.; Zhou, X. L.; Zeng, L.; Yan, X. H.; Zhao, T. S.

2016-09-01

The catalyst for the negative electrode of iron-chromium redox flow batteries (ICRFBs) is commonly prepared by adding a small amount of Bi3+ ions in the electrolyte and synchronously electrodepositing metallic particles onto the electrode surface at the beginning of charge process. Achieving a uniform catalyst distribution in the porous electrode, which is closely related to the flow field design, is critically important to improve the ICRFB performance. In this work, the effects of flow field designs on catalyst electrodeposition and battery performance are investigated. It is found that compared to the serpentine flow field (SFF) design, the interdigitated flow field (IFF) forces the electrolyte through the porous electrode between the neighboring channels and enhances species transport during the processes of both the catalyst electrodeposition and iron/chromium redox reactions, thus enabling a more uniform catalyst distribution and higher mass transport limitation. It is further demonstrated that the energy efficiency of the ICRFB with the IFF reaches 80.7% at a high current density (320 mA cm-2), which is 8.2% higher than that of the ICRFB with the SFF. With such a high performance and intrinsically low-cost active materials, the ICRFB with the IFF offers a great promise for large-scale energy storage.

Studies on neutron irradiation effects of iron alloys and nickel-base heat resistant alloys

International Nuclear Information System (INIS)

Watanabe, Katsutoshi

1987-09-01

The present paper describes the results of neutron irradiation effects on iron alloys and nickel-base heat resistant alloys. As for the iron alloys, irradiation hardening and embrittlement were investigated using internal friction measurement, electron microscopy and tensile testings. The role of alloying elements was also investigated to understand the irradiation behavior of iron alloys. The essential factors affecting irradiation hardening and embrittlement were thus clarified. On the other hand, postirradiation tensile and creep properties were measured of Hastelloy X alloy. Irradiation behavior at elevated temperatures is discussed. (author)

Effects of fixed orthodontic treatment using conventional versus metal-injection molding brackets on salivary nickel and chromium levels: a double-blind randomized clinical trial.

Science.gov (United States)

Amini, Fariborz; Harandi, Saghar; Mollaei, Mobina; Rakhshan, Vahid

2015-10-01

Despite the importance of nickel and chromium release from orthodontic brackets, there are no in vivo or in vitro studies on this issue in the case of metal-injection molding (MIM) brackets. Saliva samples were collected from 30 orthodontic patients divided randomly into two groups of conventional and MIM brackets, before treatment and 2 months later. Approved attendees with odd and even numbers were, respectively, assigned to the control and treatment groups. For blinding, the patients were not informed of their bracket types, and the saliva samples were coded. Nickel and chromium levels were determined using atomic absorption spectrophotometry. Data were analysed using repeated-measures two-way analysis of covariance, independent-samples t-test, chi-squared, Spearman and point-biserial correlation coefficients, Mann-Whitney, and Wilcoxon tests (α = 0.05). Mean nickel level increased from 7.87±8.14 (pre-treatment) to 12.57±9.96 (2nd month) in the control group, and from 8.62±9.85 (pre-treatment) to 8.86±6.42 µg/l in the MIM group. Both of these increases were significant (Wilcoxon P 0.1). The differences between both ions' levels measured in the 60th day in both bracket groups were not significant (Mann-Whitney P > 0.05). The extents of changes over time were not significantly different between the bracket types (Mann-Whitney P > 0.05). The sample size was not predetermined based on power calculations. The spectrophotometer was limited to detecting chromium concentrations above 0.25 µg/l. Ion discharge from brackets might continuously change. The current in vivo methods are unable to take such fluctuations into account. Nickel might increase in patients undergoing treatment with both bracket types, although the rate of increase might be greater in patients under treatment with conventional brackets. Using MIM brackets might reduce salivary chromium for a trivial but generalizable amount. Still, ion levels leached from conventional versus MIM brackets might

Lung cancer mortality in nickel/chromium platers, 1946-95.

Science.gov (United States)

Sorahan, T; Burges, D C; Hamilton, L; Harrington, J M

1998-04-01

To investigate mortality from lung cancer in nickel/chromium platers. The mortality experience of a cohort of 1762 chrome workers (812 men, 950 women) from a large electroplating and light engineering plant in the Midlands, United Kingdom, was investigated for the period 1946-95. All subjects were first employed in chrome work at the plant during the period 1946-75, and had at least six months employment in jobs associated with exposure to chromic acid mist (hexavalent chromium). Detailed job histories were abstracted from original company personnel records and individual cumulative durations of employment in three types of chrome work were derived as time dependent variables (chrome bath work, other chrome work, any chrome work). Two analytical approaches were used--indirect standardisation and Poisson regression. Based on mortalities for the general population of England and Wales, male workers with some period of chrome bath work had higher lung cancer mortalities (observed deaths 40, expected deaths 25.41, standardised mortality ratio (SMR) 157, 95% confidence interval (95% CI) 113 to 214, p chrome workers (observed 9, expected 13.70, SMR 66, 95% CI 30 to 125). Similar findings were shown for female workers (chrome bath workers: observed 15, expected 8.57, SMR 175, 95% CI 98 to 289, p = 0.06; other chrome workers: observed 1, expected 4.37, SMR 23, 95% CI 1 to 127). Poisson regression was used to investigate risks of lung cancer relative to four categories of cumulative duration of chrome bath work and four categories of cumulative duration of other chrome work (none, or = 5 y). After adjusting for sex, age, calendar period, year of starting chrome work, period from first chrome work, and employment status (still employed v left employment), there was a significant positive trend (p chrome bath work and risks of mortality for lung cancer. Relative to a risk of unity for those chrome workers without any period of chrome bath work, risks were 2.83 (95% CI 1.47 to

Calculation of cross sections of discrete γ rays production in the (n,n'γ) reaction on chromium and nickel with neutron energy up to 10MeV

International Nuclear Information System (INIS)

Duchemin, B.

1975-01-01

Cross-sections for the production of de-excitation γ rays following inelastic neutron scattering have been calculated, using the statistical model, and are given for natural chromium and nickel for neutron incident energy up to 10MeV [fr

Carbon deposition on nickel ferrites and nickel-magnetite surfaces

International Nuclear Information System (INIS)

Allen, G.C.; Jutson, J.A.

1988-06-01

Carbon deposition on Commercial Advanced Gas-Cooled Reactor (CAGR) fuel cladding and heat exchanger surfaces lowers heat transfer efficiency and increases fuel pin temperatures. Several types of deposit have been identified including both thin dense layers and also low density columnar deposits with filamentary or convoluted laminar structure. The low-density types are often associated with particles containing iron, nickel or manganese. To identify the role of nickel in the deposition process surfaces composed of nickel-iron spinels or metallic nickel/magnetite mixtures have been exposed to γ radiation in a gas environment simulating that in the reactor. Examination of these surfaces by Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM) have shown that while metallic nickel (Ni(O)) catalyses the formation of filamentary low density carbon deposits, the presence of divalent nickel (Ni(II)) sites in spinel type oxides is associated only with dense deposits. (author)

Fundamental data: Solubility of nickel and oxygen and diffusivity of iron and oxygen in molten LBE

International Nuclear Information System (INIS)

Abella, J.; Verdaguer, A.; Colominas, S.; Ginestar, K.; Martinelli, L.

2011-01-01

Experiments for determining nickel solubility limit and iron diffusion coefficient are presented and their results are discussed. Nickel solubility limit is determined by two methods: ex situ by solid sampling followed by ICP-AES analysis and in situ by Laser Induced Breakdown Spectroscopy and their results are compared. The iron diffusion coefficient is obtained using the technique of rotating specimen dissolution. Also a method to determine the oxygen solubility and diffusivity in LBE is developed and results at 460, 500 and 540 deg. C are presented. It is based on the following electrochemical cell: O 2 (reference mixture), Pt //YSZ//O 2 (LBE) which can work as an oxygen sensor or as a coulometric pump.

Study of the quenching and subsequent return to room temperature of uranium-chromium, uranium-iron, and uranium-molybdenum alloys containing only small amounts of the alloying element

International Nuclear Information System (INIS)

Delaplace, J.

1960-09-01

By means of an apparatus which makes possible thermal pre-treatments in vacuo, quenching carried out in a high purity argon atmosphere, and simultaneous recording of time temperature cooling and thermal contraction curves, the author has examined the transformations which occur in uranium-chromium, uranium-iron and uranium-molybdenum alloys during their quenching and subsequent return to room temperature. For uranium-chromium and uranium-iron alloys, the temperature at which the γ → β transformation starts varies very little with the rate of cooling. For uranium-molybdenum alloys containing 2,8 atom per cent of Mo, this temperature is lowered by 120 deg. C for a cooling rate of 500 deg. C/mn. The temperature at which the β → α transformation starts is lowered by 170 deg. C for a cooling rate of 500 deg. C/mn in the case of uranium-chromium alloy containing 0,37 atom per cent of Cr. The temperature is little affected in the case of uranium-iron alloys. The addition of chromium or iron makes it possible to conserve the form β at ordinary temperatures after quenching from the β and γ regions. The β phase is particularly unstable and changes into needles of the α form even at room temperatures according to an autocatalytic transformation law similar to the austenitic-martensitic transformation law in the case of iron. The β phase obtained by quenching from the β phase region is more stable than that obtained by quenching from the γ region. Chromium is a more effective stabiliser of the β phase than is iron. Unfortunately it causes serious surface cracking. The β → α transformation in uranium-chromium alloys has been followed at room temperature by means of micro-cinematography. The author has not observed the direct γ → α transformation in uranium-molybdenum alloys containing 2,8 per cent of molybdenum even for cooling rates of up to 2000 deg. C/s. He has however observed the formation of several martensitic structures. (author) [fr

Chemical vapor deposition of aluminide coatings on iron, nickel and superalloys

International Nuclear Information System (INIS)

John, John T.; De, P.K.; Dubey, Vivekanand; Srinivasa, Raman

2009-08-01

Aluminide coatings are a class of intermetallic coatings applied on nickel and cobalt base superalloys and steels to protect them from different forms of environmental degradation at high temperatures. In this report a CVD system that can produce the aluminide coatings on iron, nickel and nickel base alloys has been described and the result of chemical vapor deposition of aluminide coatings on iron specimens, their characterization, and property evaluation have been presented. The CVD system consists of an AlCl 3 bath, a stainless steel retort as a hot-wall reacto, cold traps and vacuum system. Aluminium chloride vapor was carried in a stream of hydrogen gas at a flow rate of 150 SCCM (standard cubic centimeter per minute) into the CVD reactor maintained in the temperature range of 1173 - 1373 K and at a pressure of 1.33 kPa (10 Torr). Aluminum deposition takes place from aluminium subchlorides produced by reaction between AlCl 3 and pure aluminum kept in the CVD reactor. The aluminum diffuses into the iron samples and iron aluminide phases are formed at the surface. The coatings were shining bright and showed good adherence to the substrate. The coatings consisted of FeAl phase over a wide range of experimental conditions. The growth kinetics of the coating followed a parabolic rate law and the mean activation energy was 212 ±16 kJ/mol. Optical microscopic studies on the transverse section of the coating showed that the aluminide coating on iron consisted of two layers. The top layer had a thickness in the range of 20-50 μm, and the under layer had thickness ranging from 35 to 250 μm depending on coating temperature in two hours. The thickness of the aluminide layer increased with coating duration and temperature. Electron microprobe studies (EPMA) showed that the aluminum concentration decreased steadily as distance from the surface increased. TEM studies showed that the outer most layer had a B2 order (of the FeAl phase), which extended even into the under

Nickel-base alloys having a low coefficient of thermal expansion

International Nuclear Information System (INIS)

Baldwin, J.F.; Maxwell, D.H.

1975-01-01

Alloy compositions consisting predominantly of nickel, chromium, molybdenum, carbon, and boron are disclosed. The alloys possess a duplex structure consisting of a nickel--chromium--molybdenum matrix and a semi-continuous network of refractory carbides and borides. A combination of desirable properties is provided by these alloys, including elevated temperature strength, resistance to oxidation and hot corrosion, and a very low coefficient of thermal expansion

Study of cast and thermo-mechanically strengthened chromium-nickel nitrogen-containing steel

International Nuclear Information System (INIS)

Prokoshkina, V.G.; Kaputkina, L.M.; Svyazhin, A.G.

2000-01-01

The effect of nitrogen on the structure and strength of corrosion-resistant chromium-nickel steels after thermal and thermomechanical treatment is studied. The 06Kh15N7AD and 07Kh15N7DAMB steels alloying by nitrogen was accomplished through the basic composition steels remelting in the molecular nitrogen atmosphere under the pressure of 0.1-2.5 MPa. The 02Kh15N5DAF and 05Kh15N5DAM steels ingots were obtained through melting in a plasma furnace under the nitrogen pressure of 0.4MPA. The high-temperature thermomechanical treatment (HTMT) was performed by rolling with preliminary blanks heating up to 1050 deg C and the rolling end temperature not below 950 deg C. It is shown, that the HTMT of the nitrogen-containing steels makes it possible to obtain strength characteristics by 1.5 times exceeding the properties of traditionally applicable corrosion-resistant steels, whereby sufficiently high plasticity of the nitrogen-containing steel is retained [ru

A comparative study of all-vanadium and iron-chromium redox flow batteries for large-scale energy storage

Science.gov (United States)

Zeng, Y. K.; Zhao, T. S.; An, L.; Zhou, X. L.; Wei, L.

2015-12-01

The promise of redox flow batteries (RFBs) utilizing soluble redox couples, such as all vanadium ions as well as iron and chromium ions, is becoming increasingly recognized for large-scale energy storage of renewables such as wind and solar, owing to their unique advantages including scalability, intrinsic safety, and long cycle life. An ongoing question associated with these two RFBs is determining whether the vanadium redox flow battery (VRFB) or iron-chromium redox flow battery (ICRFB) is more suitable and competitive for large-scale energy storage. To address this concern, a comparative study has been conducted for the two types of battery based on their charge-discharge performance, cycle performance, and capital cost. It is found that: i) the two batteries have similar energy efficiencies at high current densities; ii) the ICRFB exhibits a higher capacity decay rate than does the VRFB; and iii) the ICRFB is much less expensive in capital costs when operated at high power densities or at large capacities.

Mortality study of nickel platers with special reference to cancers of the stomach and lung, 1945-93.

OpenAIRE

Pang, D; Burges, D C; Sorahan, T

1996-01-01

OBJECTIVES: To re-examine mortality patterns in a cohort of nickel platers with no history of chromium plating. METHODS: All 284 men first employed by the company in 1945-75 with a minimum employment of three months in the nickel plating department were identified. Workers who had worked in the chromium plating or nickel/chromium plating departments were excluded. Standardised mortality ratios (SMRs), P values, and 95% confidence intervals were calculated. Poisson regression was used to carry...

Electrochemical activity of iron in acid treated bentonite and influence of added nickel

Energy Technology Data Exchange (ETDEWEB)

Mudrinić, T., E-mail: tihana@nanosys.ihtm.bg.ac.rs [University of Belgrade-Institute of Chemistry, Technology and Metallurgy, Center for Catalysis and Chemical Engineering, Njegoševa 12, 11000 Belgrade (Serbia); Mojović, Z.; Milutinović-Nikolić, A. [University of Belgrade-Institute of Chemistry, Technology and Metallurgy, Center for Catalysis and Chemical Engineering, Njegoševa 12, 11000 Belgrade (Serbia); Mojović, M. [University of Belgrade, Faculty of Physical Chemistry, Studenski trg 12-16, 11000 Belgrade (Serbia); Žunić, M. [University of Belgrade-Institute of Chemistry, Technology and Metallurgy, Center for Catalysis and Chemical Engineering, Njegoševa 12, 11000 Belgrade (Serbia); Vukelić, N. [University of Belgrade, Faculty of Physical Chemistry, Studenski trg 12-16, 11000 Belgrade (Serbia); Jovanović, D. [University of Belgrade-Institute of Chemistry, Technology and Metallurgy, Center for Catalysis and Chemical Engineering, Njegoševa 12, 11000 Belgrade (Serbia)

2015-10-30

Highlights: • Mild acid treatment followed by incorporation of nickel was performed on bentonite. • Modified bentonites based electrodes were tested in H{sub 2}SO{sub 4} by cyclic voltammetry. • Acid treatment increased current response of electroactive iron within smectite. • Incorporation of Ni improved reversibility of Fe{sup 2+}/Fe{sup 3+} oxidation/reduction process. - Abstract: Bentonite originated from Mečji Do, Serbia, was submitted to acid treatment at 70 °C for 30 min, while only the concentration of applied HCl varied. The obtained acid treated samples were used to modify glassy carbon (GC) electrode. The effect of applied acid treatment on the electrochemical behavior of GC electrodes modified with these materials was investigated. Furthermore, the effect of the introduction of nickel into acid treated samples was studied. The incorporation of nickel into acid treated bentonite was achieved by either ion exchange or impregnation/decomposition method. The obtained samples were characterized using the following methods: inductively coupled plasma (ICP), X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy and electron spin resonance (ESR) spectroscopy. The electrochemical behavior of these samples was tested by cyclic voltammetry in 0.1 mol dm{sup −3} H{sub 2}SO{sub 4} solution. The ICP, FTIR and ESR results exhibited a slight decrease of iron content in the acid treated samples. XRD and FTIR results confirmed that the conditions applied for the acid treatment were mild enough for the smectite structure to be preserved. The electrocatalytic test showed that the current response of Fe{sup 2+}/Fe{sup 3+} oxidation/reduction process increased on the GC electrodes separately modified with each of the acid treated samples in comparison with current obtained on the GC electrode modified with untreated sample. These results indicated that applied acid treatment probably increased the accessibility of the electroactive iron within

Early stages of oxidation of ion-implanted nickel at high temperature

International Nuclear Information System (INIS)

Peide, Z.; Grant, W.A.; Procter, R.P.M.

1981-01-01

The early stages of oxidation of nickel implanted with nickel, chromium, or lithium ions in oxygen at 1100 0 C have been studied using various electron-optical techniques. The unimplanted metal develops initially a fine-grained, convoluted scale having a ridged, cellular structure. Subsequently, the oxide grains increase in size significantly and oxidation becomes predominantly controlled by diffusion of Ni /sup 2+/ ions across a compact, columnar scale. Implantation of the surface with nickel ions has no significant effect on the initial oxidation behavior. However, after implantation with chromium or lithium ions, the development of the NiO scale is, in the early stages of oxidation, suppressed by formation of NiCr 2 O 4 or LiO 2 nodules, respectively. Subsequently, the implanted species are incorporated into the steady-state NiO scale where they dope the oxide and thus influence the diffusion rate of Ni /sup 2+/ ions through it. As would be predicted, the steady-state oxidation rate of chromium-implanted nickel is increased while that of lithium- implanted nickel is decreased compared with that of the unimplanted metal

Associations of neonatal lead, cadmium, chromium and nickel co-exposure with DNA oxidative damage in an electronic waste recycling town.

Science.gov (United States)

Ni, Wenqing; Huang, Yue; Wang, Xiaoling; Zhang, Jingwen; Wu, Kusheng

2014-02-15

This study aimed to evaluate the effects of toxic heavy metal co-exposure on DNA oxidative damage in neonates from a primitive e-waste recycling region, Guiyu town, China. Our participants included 201 pregnant women: 126 from Guiyu town and 75 from Jinping district of Shantou city, where no e-waste recycling and dismantling activities existed. Structured interview questionnaires were administered to the pregnant women and umbilical cord blood (UCB) samples were collected after delivery. The UCB concentrations of lead, cadmium, chromium, and nickel were analyzed by graphite furnace atomic absorption spectrometry (GFAAS). Levels of UCB plasma 8-hydroxydeoxyguanosine (8-OHdG, a DNA oxidative damage biomarker) were determined by enzyme-linked immunosorbent assay. Our results suggested that UCB lead and cadmium concentrations in neonates of Guiyu were significantly higher than those of Jinping (lead: median 110.45 ng/mL vs. 57.31 ng/mL; cadmium: median 2.50 ng/mL vs. 0.33 ng/mL, both Pnickel (β=0.215 ng/mL, 95% CI: 0.113 to 0.317 ng/mL) concentrations. The primitive e-waste recycling and dismantling activities may contribute to the elevated umbilical cord blood toxic heavy metal levels in neonates born in Guiyu. Exposures to cadmium, chromium and nickel were associated with increased oxidative DNA damage in neonates. Copyright © 2013 Elsevier B.V. All rights reserved.

Reducing elution in anion exchange chromatography as a pretreatment of colorimetry of chromium(VI) and vanadium(V)

International Nuclear Information System (INIS)

Shigetomi, Yasumasa; Hatamoto, Takeji; Nagoshi, Kimie; Yamashige, Takashi.

1976-01-01

In order to increase the selectivity of the colorimetry of chromium and vanadium, the separation by means of anion exchange chromatography was tested. The column, phi 0.8x5.0 cm packing (50--100 mesh) Dowex 1x4 anion exchange resin was used for the separation of chromium. The solution containing chromium (VI), zinc(II), cadmium(II), iron(III) and reducing organic substances contained in industrial waste water was introduced into the column and then the substances other than chromium(VI) were removed by washing the column with distilled water. Finally chromium(VI) was reduced to chromium(III) by hydroxylamine in the eluent and eluted. The concentration of sulfuric acid and hydroxylamine in the eluent were 0.1 mol/l and 0.001 mol/l respectively. For analyzing chromium(III) in the mixture of chromium(VI) and chromium(III), after removal of chromium(VI) it should be oxidized to chromium(VI) anion with the oxidant, e.g., sodium peroxide or hydrogen peroxide, before introducing it into the column. In terms of the pretreatment by using the acetate form resin column, chromium (VI) and chromium(III) can be determined separately in the solution whose concentration ranges from 0.05 ppm to 0.5 ppm despite the presence of contaminants, which interfere with the colorimetric determination of chromium(VI) using diphenylcarbonohydrazide, in the original solution. The separation of vanadium(V) in the solution containing copper(II), cobalt(II) and etc. was made using the mixed solution of hydrochloric acid (2 mol/l) and hydroxylamine (0.2 mol/l) similarly to chromium(VI). In terms of the similar pretreatment vanadium could be determined precisely as far as 0.1 ppm by the colorimetry using 4-(2-pyridylazo) resorcinol despite the presence of copper(II), cobalt(II), nickel(II) and etc in the original solution. (auth.)

Mortality study of nickel platers with special reference to cancers of the stomach and lung, 1945-93.

Science.gov (United States)

Pang, D; Burges, D C; Sorahan, T

1996-10-01

To re-examine mortality patterns in a cohort of nickel platers with no history of chromium plating. All 284 men first employed by the company in 1945-75 with a minimum employment of three months in the nickel plating department were identified. Workers who had worked in the chromium plating or nickel/chromium plating departments were excluded. Standardised mortality ratios (SMRs), P values, and 95% confidence intervals were calculated. Poisson regression was used to carry out statistical modelling of mortalities within the cohort (internal standard). Four variables were considered to have the potential to influence mortality within the cohort: attained age (age at follow up or age at death), year of starting nickel work, period of follow up (measured from the first period of work with nickel exposure), and duration of exposure to nickel. The only significant difference between observed and expected numbers, when investigated by site of cancer and by broad non-cancer groupings, was that for stomach cancer (observed eight, expected 2.49, SMR 322). The study provides only weak evidence that nickel plating is associated with an excess risk of stomach cancer. This cohort of nickel platers does not seem to have experienced any discernible risk of occupational lung cancer. Other studies of nickel platers rather than nickel/chromium platers would be useful.

Carbothermic Reduction of Nickeliferous Laterite Ores for Nickel Pig Iron Production in China: A Review

Science.gov (United States)

Rao, Mingjun; Li, Guanghui; Jiang, Tao; Luo, Jun; Zhang, Yuanbo; Fan, Xiaohui

2013-11-01

Both the consumption and production of crude stainless steel in China rank first in the world. In 2011, the nickel production in China amounted to 446 kilotons, with the proportion of electrolytic nickel and nickel pig iron (NPI) registering 41.5% and 56.5%, respectively. NPI is a low-cost feedstock for stainless steel production when used as a substitute for electrolytic nickel. The existing commercial NPI production processes such as blast furnace smelting, rotary kiln-electric furnace smelting, and Krupp-Renn (Nipon Yakin Oheyama) processes are discussed. As low-temperature (below 1300°C) reduction of nickeliferous laterite ores followed by magnetic separation could provide an alternative avenue without smelting at high temperature (~1500°C) for producing ferronickel with low cost, the fundamentals and recent developments of the low-temperature reduction of nickeliferous laterite ores are reviewed.

Moessbauer study of nickel containing 0.5% iron between room temperature and the Curie point

International Nuclear Information System (INIS)

Longworth, G.; Cranshaw, T.E.

1983-01-01

The Moessbauer measurements of the temperature variation of the spectra for nickel containing 0.5% iron by Hirsch have been repeated for a similar sample. No evidence was found for the magnetic first order transition postulated by Hirsch. (orig.)

Chromium fate in constructed wetlands treating tannery wastewaters.

Science.gov (United States)

Dotro, Gabriela; Palazolo, Paul; Larsen, Daniel

2009-06-01

Nine experimental wetlands were built to determine chromium partitioning inside systems treating tannery wastewaters. Results showed 5-day biochemical oxygen demand and chromium removals of 95 to 99% and 90 to 99%, respectively. The majority of chromium was found in association with media (96 to 98%), followed by effluents (2.9 to 3.9%), and the least was found in plant parts (0.1%). Chemical speciation modeling of solutions and scanning electron microscope analysis suggest two potential chromium removal mechanisms--sorption/coprecipitation with iron hydroxides or oxyhydroxides and biomass sorption. The release of the majority of chromium in the iron- and organic-bound phases during sequential extractions supports the proposed dominant removal mechanisms. The use of a mixture of peat and gravel resulted in lower removal efficiencies and stronger partitioning in organic phases during sequential extractions. Chromium was efficiently removed by wetlands, retained through chemical and biological processes. Future research will focus on further exploring removal mechanisms and proposing management strategies for the chromium-containing wetland media.

PROTECTIVE LAYERS OF IRON AND NICKEL ALUMINIDES ON STEEL

Directory of Open Access Journals (Sweden)

Milena Voděrová

2013-07-01

Full Text Available Intermediary phases Ni-Al and Fe-Al are promising materials due to their superior properties such as hardness and good resistance against oxidation at high temperatures. Moreover, Fe-Al phases are resistant in sulphur - containing atmospheres. Because of these characteristics, the above mentioned intermetallic phases seem to be prospective for the use in many technical applications such as energetics, chemical or automotive industry in a form of a bulk material or coatings. Presently, the protective aluminide layer is usually prepared by thermal spraying. Nevertheless, this method is not suitable for complex-shaped components. Therefore, the aim of this work was to find an alternative way to prepare layers consisting of nickel or iron aluminides by other technique than thermal spraying. At first, carbon steel samples were coated using galvanic or electroless nickel plating. Coated samples were subsequently submerged into molten aluminium at various temperatures and process durations. The influence of the temperature and duration on the intermetallic phase growth was studied by scanning electron and light microscopy. Thickness and microhardness of the intermetallic layer was also measured.

PROTECTIVE LAYERS OF IRON AND NICKEL ALUMINIDES ON STEEL

Directory of Open Access Journals (Sweden)

Milena Voderova

2013-05-01

Full Text Available Intermediary phases Ni-Al and Fe-Al are promising materials due to their superior properties such as hardness and good resistance against oxidation at high temperatures. Moreover, Fe-Al phases are resistant in sulphur - containing atmospheres. Because of these characteristics, the above mentioned intermetallic phases seem to be prospective for the use in many technical applications such as energetics, chemical or automotive industry in a form of a bulk material or coatings. Presently, the protective aluminide layer is usually prepared by thermal spraying. Nevertheless, this method is not suitable for complex-shaped components. Therefore, the aim of this work was to find an alternative way to prepare layers consisting of nickel or iron aluminides by other technique than thermal spraying. At first, carbon steel samples were coated using galvanic or electroless nickel plating. Coated samples were subsequently submerged into molten aluminium at various temperatures and process durations. The influence of the temperature and duration on the intermetallic phase growth was studied by scanning electron and light microscopy. Thickness and microhardness of the intermetallic layer was also measured.

Scattering of polarized protons by yttrium, iron and nickel nuclei

International Nuclear Information System (INIS)

Melssen, J.P.M.G.

1978-01-01

Results are presented of scattering experiments performed on yttrium and some iron and nickel isotopes with polarized proton beams at energies around 20 MeV. The angular distributions of the differential cross sections and analyzing powers have been measured and comparison of these with predictions from theoretical models has led to information about excited nuclear states like spin, parity and details of the wavefunctions. The DWBA has been mostly used to describe the reaction at the bombarding energies and for the target nuclei investigated. (C.F.)

Enthalpy of formation of vanadates of iron, chromium, and aluminum

Energy Technology Data Exchange (ETDEWEB)

Kesler, Y.A.; Cheshnitskii, S.M.; Fotiev, A.A.; Tret' yakov, Y.D.

1985-09-01

The study of vanadates of iron, aluminum and chromium is of importance for the analysis of the functioning of catalysts of organic synthesis reactions and for the study of vanadium corrosion of structural materials. Of principal interest, however, are the processes in the treatment of vanadium-containing metallurgical slags and waste from thermal power plants, in which these compounds play a major role. At the same time, the thermochemical properties of these substances, which are necessary for creating the physicochemical foundations of industrially important processes, have not been investigated sufficiently. The authors therefore undertake here a study of the compounds FeVO/sub 4/, AIVO/sub 4/, CrVO/sub 4/ and FeCr(VO/sub 4/)/sub 2/, to determine their enthalpies of formation.

Effect of vibration frequency on microstructure and performance of high chromium cast iron prepared by lost foam casting

Directory of Open Access Journals (Sweden)

Wen-qi Zou

2016-07-01

Full Text Available In the present research, high chromium cast irons (HCCIs were prepared using the lost foam casting (LFC process. To improve the wear resistance of the high chromium cast irons (HCCIs, mechanical vibration was employed during the solidification of the HCCIs. The effects of vibration frequency on the microstructure and performance of the HCCIs under as-cast, as-quenched and as-tempered conditions were investigated. The results indicated that the microstructures of the LFC-produced HCCIs were refined due to the introduction of mechanical vibration, and the hardness was improved compared to that of the alloy without vibration. However, only a slight improvement in hardness was found in spite of the increase of vibration frequency. In contrast, the impact toughness of the as-tempered HCCIs increased with an increase in the vibration frequency. In addition, the wear resistance of the HCCIs was improved as a result of the introduction of vibration and increased with an increase in the vibration frequency.

TECHNOLOGIES OF DOPING OF CAST IRON THROUGH THE SLAG PHASE WITH USING OF THE SPENT NICKEL- AND COPPER-CONTAINING CATALYSTS

Directory of Open Access Journals (Sweden)

I. B. Provorova

2015-01-01

Full Text Available We have defined the regularities of the doping of cast iron through the slag phase of nickel and copper due to the waste catalysts using a carbonaceous reducing agent. We have justified the need to use the cast iron chips as a seed in the composition of the slag mixture. We have defined the dependence of the degree of extraction of nickel or copper from spent catalyst on the amount of the catalyst, on the basicity of the slag mixture, on the temperature and time of melting.

Effects of chloride, sulfate and natural organic matter (NOM) on the accumulation and release of trace-level inorganic contaminants from corroding iron.

Science.gov (United States)

Peng, Ching-Yu; Ferguson, John F; Korshin, Gregory V

2013-09-15

This study examined effects of varying levels of anions (chloride and sulfate) and natural organic matter (NOM) on iron release from and accumulation of inorganic contaminants in corrosion scales formed on iron coupons exposed to drinking water. Changes of concentrations of sulfate and chloride were observed to affect iron release and, in lesser extent, the retention of representative inorganic contaminants (vanadium, chromium, nickel, copper, zinc, arsenic, cadmium, lead and uranium); but, effects of NOM were more pronounced. DOC concentration of 1 mg/L caused iron release to increase, with average soluble and total iron concentrations being four and two times, respectively, higher than those in the absence of NOM. In the presence of NOM, the retention of inorganic contaminants by corrosion scales was reduced. This was especially prominent for lead, vanadium, chromium and copper whose retention by the scales decreased from >80% in the absence of NOM to chloride levels. Modeling indicated that the observed effects were associated with the formation of metal-NOM complexes and effects of NOM on the sorption of the inorganic contaminants on solid phases that are typical for iron corrosion in drinking water. Copyright © 2013 Elsevier Ltd. All rights reserved.

Predicting chromium (VI) adsorption rate in the treatment of liquid ...

African Journals Online (AJOL)

Administrator

The adsorption rate of chromium (VI) on commercial activated carbon during the ... time and initial chromium (VI) ion concentration. .... model, the separation factor r, according to Calvo et al (2001) cited .... Lead (II) and nickel (II) adsorption kinetics .... heavy metal by Talaromyces helicus: a trained fungus for copper and.

Plasma Spraying and Characterization of Chromium Carbide-Nickel Chromium Coatings

Czech Academy of Sciences Publication Activity Database

Ctibor, Pavel; Prantnerová, M.

2016-01-01

Roč. 9, č. 4 (2016), s. 281-290, č. článku PCCC-2016-09-16-339. ISSN 2008-2134 Institutional support: RVO:61389021 Keywords : Plasma spraying * Chromium carbide * Slurry abrasion * Dry rubber wheel test * Friction * Microhardness Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass http://www.pccc.icrc.ac.ir/?xid=0113010121000001804&id=976

4-META opaque resin--a new resin strongly adhesive to nickel-chromium alloy.

Science.gov (United States)

Tanaka, T; Nagata, K; Takeyama, M; Atsuta, M; Nakabayashi, N; Masuhara, E

1981-09-01

1) A new adhesive opaque resin containing a reactive monomer, 4-methacryloxy-ethyl trimellitate anhydride (4-META), was prepared, and its application to thermosetting acrylic resin veneer crowns was studied. 2) The 4-META opaque resin was applied to a variety of nickel-chromium dental alloy specimens which had undergone different treatment, and endurance tests were conducted to evaluate the durability of adhesion. 3) Stable adhesion against water penetration was achieved with metal surfaces first etched with HCl and then oxidized with HNO3. A bond strength of 250 kg/cm2 was maintained even after immersion in water at 37 degrees C for 30 wk or at 80 degrees C for ten wk. Furthermore, this value did not decrease even after the specimens were subjected to 500 thermal cycles. 4) The 4-META opaque resin studied can eliminate the necessity for retention devices on metal castings. 5) The smooth 4-META opaque resin should have no adverse effects on gingivae.

Selective phenol methylation to 2,6-dimethylphenol in a fluidized bed of iron-chromium mixed oxide catalyst with o-cresol circulation.

Science.gov (United States)

Zukowski, Witold; Berkowicz, Gabriela; Baron, Jerzy; Kandefer, Stanisław; Jamanek, Dariusz; Szarlik, Stefan; Wielgosz, Zbigniew; Zielecka, Maria

2014-01-01

2,6-dimethylphenol (2,6-DMP) is a product of phenol methylation, especially important for the plastics industry. The process of phenol methylation in the gas phase is strongly exothermic. In order to ensure good temperature equalization in the catalyst bed, the process was carried out using a catalyst in the form of a fluidized bed - in particular, the commercial iron-chromium catalyst TZC-3/1. Synthesis of 2,6-dimethylphenol from phenol and methanol in fluidized bed of iron-chromium catalyst was carried out and the fluidization of the catalyst was examined. Stable state of fluidized bed of iron-chromium catalyst was achieved. The measured velocities allowed to determine the minimum flow of reactants, ensuring introduction of the catalyst bed in the reactor into the state of fluidization. Due to a high content of o-cresol in products of 2,6-dimethylphenol synthesis, circulation in the technological node was proposed. A series of syntheses with variable amount of o-cresol in the feedstock allowed to determine the parameters of stationary states. A stable work of technological node with o-cresol circulation is possible in the temperature range of350-380°C, and o-cresolin/phenolin molar ratio of more than 0.48. Synthesis of 2,6-DMP over the iron-chromium catalyst is characterized by more than 90% degree of phenol conversion. Moreover, the O-alkylation did not occur (which was confirmed by GC-MS analysis). By applying o-cresol circulation in the 2,6-DMP process, selectivity of more than 85% degree of 2,6-DMP was achieved. The participation levels of by-products: 2,4-DMP and 2,4,6-TMP were low. In the optimal conditions based on the highest yield of 2,6-DMP achieved in the technological node applying o-cresol circulation, there are 2%mol. of 2,4-DMP and 6%mol. of 2,4,6-TMP in the final mixture, whereas 2,4,6-TMP can be useful as a chain stopper and polymer's molar mass regulator during the polymerization of 2,6-DMP.

TEM characterisation of stress corrosion cracks in nickel based alloys: effect of chromium content and chemistry of environment; Caracterisation par MET de fissures de corrosion sous contrainte d'alliages a base de nickel: influence de la teneur en chrome et de la chimie du milieu

Energy Technology Data Exchange (ETDEWEB)

Delabrouille, F

2004-11-15

Stress corrosion cracking (SCC) is a damaging mode of alloys used in pressurized water reactors, particularly of nickel based alloys constituting the vapour generator tubes. Cracks appear on both primary and secondary sides of the tubes, and more frequently in locations where the environment is not well defined. SCC sensitivity of nickel based alloys depends of their chromium content, which lead to the replacement of alloy 600 (15 % Cr) by alloy 690 (30 % Cr) but this phenomenon is not yet very well understood. The goal of this thesis is two fold: i) observe the effect of chromium content on corrosion and ii) characterize the effect of environment on the damaging process of GV tubes. For this purpose, one industrial tube and several synthetic alloys - with controlled chromium content - have been studied. Various characterisation techniques were used to study the corrosion products on the surface and within the SCC cracks: SIMS; TEM - FEG: thin foil preparation, HAADF, EELS, EDX. The effect of chromium content and surface preparation on the generalised corrosion was evidenced for synthetic alloys. Moreover, we observed the penetration of oxygen along triple junctions of grain boundaries few micrometers under the free surface. SCC tests show the positive effect of chromium for contents varying from 5 to 30 % wt. Plastic deformation induces a modification of the structure, and thus of the protective character, of the internal chromium rich oxide layer. SCC cracks which developed in different chemical environments were characterised by TEM. The oxides which are formed within the cracks are different from what is observed on the free surface, which reveals a modification of medium and electrochemical conditions in the crack. Finally we were able to evidence some structural characteristics of the corrosion products (in the cracks and on the surface) which turn to be a signature of the chemical environment. (author)

Plants sensitivity on nickel under different conditions of iron or calcium concentration in the nutrient medium

Directory of Open Access Journals (Sweden)

Renata Matraszek

2013-12-01

Full Text Available The sensitivity of six vegetable plants on nickel at early stages of their growth was investigated by index of tolerance. Besides the possibility of nickel fitostabilization by additional application of iron or calcium was tested. The experiment was conducted on Petri dishes. Different concentrations of nickel (0; 0,03; 0,06mM Ni as nickel sulphate, iron (0,05; O,OlmM Fe as Fe2+ citrate and calcium (0,50; 0,75; lmM Ca as calcium carbonate were added. Taking into consideration the sensitivity, investigated vegetables can be ordered in the following way: Cucurbita pepo conv. giromontiina L.>Lactuca sativa L.>Sinapis alba L.>Spinacia oleracea L.=Zea mays var. saccharata Kcke.>Phaseolus vulgaris L. Positive, statistically significant effect ofnickel fitostabilization (0,03 or 0,06mM Ni on elongative growth by the iron application (0,10mM Fe was shown for Zea mays var. saccharata Kcke independently of Ni concentration in the nutrient medium as well as for Sinapis alba L. and Phaseolus vulgaris L. in 0,06mM Ni. Addition as much as 0,75mM Ca in the presence 0,03mM Ni had positive result on Sinapis alba L and Phaseolus vulgaris L. seedlings as well as on Zea mays var. saccharata Kcke and Lactuca sativa L. roots and Cucurbita pepo convar. giromontiina L. shoots. Addition of 0,75mM Ca in the presence 0,06mM Ni promoted elongative growth of Zea mays var. saccharata Kcke seedlings. Application lmM Ca resulted in the promotion of elongative growth of Zea mays var. saccharata Kcke. roots (0,03mM Ni as well as Spinacia oleracea L. roots (0,06mM Ni.

An electron-microscope study of alpha to gamma transformation in an iron-nickel alloy

Science.gov (United States)

Lobodyuk, V. A.; Khandros, L. G.; Fedas, N. P.

1980-01-01

Procedures used to study the alpha to gamma conversion in thin foils of an iron alloy with 32% nickel concentration and initial martensite conversion temperature of -60 C are described. Photomicrographs show deformation twinning as well as changes in samples after they were heated. Reverse conversion is discussed and results are examined.

Heavy metal toxicity and iron chlorosis

Energy Technology Data Exchange (ETDEWEB)

DeKock, P C

1956-01-01

The toxicity of copper, nickel, cobalt, zinc, chromium, and manganese to mustard was studied in water culture, utilizing either the ionic form or the EDTA chelate of the metal in the presence of either ferric chloride or ferric EDTA. In presence of ferric chloride the activity of the metals in producing chlorosis was as given above, i.e. in the order of stability of their chelates. In the presence of ferric versenate, toxicity of the ionic metal was much reduced. The metal chelates gave very little indication of toxicity with either form of iron. It was found that the ratio of total phosphorus to total iron was higher in chlorotic plants than in green plants, irrespective of which metal was causing the toxicity. Copper could be demonstrated in the phloem cells of the root using biscyclohexanone-oxalydihydrazone as histochemical reagent. It is postulated that transport of iron probably takes place in the phloem as an active process. It would appear that as a major part of the iron in plant cells is attached to nucleo- or phospho-proteins, the heavy metals must be similarly attached to phospho-proteins.

The electrochemistry of chromium, chromium-boron and chromium-phosphorus alloys

International Nuclear Information System (INIS)

Moffat, T.P.; Ruf, R.R.; Latanision, R.M.

1987-01-01

It is fairly well established that chromium-metalloid interactions represent the key to understanding the remarkable corrosion behavior of TM-Cr-M glasses; (Fe, Ni, Co,...)-Cr-(P, Si, C, S). The character and kinetics of passive film growth on the glasses are being studied ni order to assess the role of the film former, chromium, and the metalloids in the passivation process. A series of thin film microcrystalline chromium, Cr-B and Cr-P binary alloys have been fabricated by physical vapor deposition techniques. Vacuum melted conventionally processed chromium has also been studied. Examination of these materials in lM H/sub 2/SO/sub 4/ and lM HCl by voltammetry, potentiostatic and impedance techniques yields the following conclusion: 1. Pure chromium with a grain size varying from < 400 A to 0.5 mm exhibits no well defined differences in electrochemical behavior in lM H/sub 2/SO/sub 4/. 2. The tremendous corrosion resistance of Cr-B alloys has been confirmed. 3. The beneficial effects observed for boron alloyed with chromium may be considered surprising in view of the neutral/negative influence of alloying boron with iron, i.e. Fe/sub 80/B/sub 20/. 4. The interaction of the electrochemistry of the metalloid constituent with that of the transition base element determines the corrosion behavior. 5. Preliminary work with Cr-P alloys indicates that certain compositions exhibit promising properties - certain films were found to be intact after two days of immersion in concentrated HCl. Further work is in progress

Electrochemical reduction of nickel ions from dilute solutions

NARCIS (Netherlands)

Njau, K.N.; Janssen, L.J.J.

1995-01-01

Electrochemical reduction of nickel ions in dilute solution using a divided GBC-cell is of interest for purification of waste waters. A typical solution to be treated is the effluent from steel etching processes which contain low quantities of nickel, chromate and chromium ions. Reduction of

Diffusion of Nickel into Ferritic Steel Interconnects of Solid Oxide Fuel/Electrolysis Stacks

DEFF Research Database (Denmark)

Molin, Sebastian; Chen, Ming; Bowen, Jacob R.

2013-01-01

diffusion of nickel from the Ni/YSZ electrode or the contact layer into the interconnect plate. Such diffusion can cause austenization of the ferritic structure and could possibly alter corrosion properties of the steel. Whereas this process has already been recognized by SOFC stack developers, only...... a limited number of studies have been devoted to the phenomenon. Here, diffusion of Ni into ferritic Crofer 22 APU steel is studied in a wet hydrogen atmosphere after 250 hours of exposure at 800 °C using Ni-plated (~ 10 micron thick coatings) sheet steel samples as a model system. Even after...... this relatively short time all the metallic nickel in the coating has reacted and formed solid solutions with iron and chromium. Diffusion of Ni into the steel causes formation of the austenite FCC phase. The microstructure and composition of the oxide scale formed on the sample surface after 250 hours is similar...

Segregation and precipitation in iron-chromium alloys during thermal ageing and irradiation

International Nuclear Information System (INIS)

Senninger, O.

2013-01-01

Iron-Chromium alloys have a peculiar thermodynamic and diffusion behavior which is due to their magnetic properties. The alloy decomposition under thermal ageing has been studied in this thesis. An atomistic kinetic model has been performed in this aim in which we have modeled in details the chemical species thermodynamic and diffusion properties. In particular, the evolution of elements diffusion properties which the ferro-paramagnetic transition has been introduced in the model. Simulated decompositions have been compared with experiments for a large range of concentrations and temperatures. A good agreement between simulations and experiments was observed and these comparisons have highlighted the ferro to paramagnetic transition key role in the concentrated alloys kinetic decomposition. This study has also evidenced that the elements diffusion at phases interfaces is responsible for the alloy decomposition kinetic in long lasting.We have also started a study of the alloy radiation induced segregation. For that purpose, atomistic kinetic model has been performed modeling defects migration through a perfect planar sink. It have been shown, I agreement with former studies, that chromium tends to segregate in the vicinity of sinks at low temperatures and deplete at high temperature. (author) [fr

Chemoorganotrophic Bioleaching of Olivine for Nickel Recovery

Directory of Open Access Journals (Sweden)

Yi Wai Chiang

2014-06-01

Full Text Available Bioleaching of olivine, a natural nickel-containing magnesium-iron-silicate, was conducted by applying chemoorganotrophic bacteria and fungi. The tested fungus, Aspergillus niger, leached substantially more nickel from olivine than the tested bacterium, Paenibacillus mucilaginosus. Aspergillus niger also outperformed two other fungal species: Humicola grisae and Penicillium chrysogenum. Contrary to traditional acid leaching, the microorganisms leached nickel preferentially over magnesium and iron. An average selectivity factor of 2.2 was achieved for nickel compared to iron. The impact of ultrasonic conditioning on bioleaching was also tested, and it was found to substantially increase nickel extraction by A. niger. This is credited to an enhancement in the fungal growth rate, to the promotion of particle degradation, and to the detachment of the stagnant biofilm around the particles. Furthermore, ultrasonic conditioning enhanced the selectivity of A. niger for nickel over iron to a value of 3.5. Pre-carbonating the olivine mineral, to enhance mineral liberation and change metal speciation, was also attempted, but did not result in improvement as a consequence of the mild pH of chemoorganotrophic bioleaching.

Physical models of corrosion of iron and nickel in liquid sodium

International Nuclear Information System (INIS)

Skyrme, G.

1975-11-01

The possible physical models for the corrosion of iron and nickel in liquid sodium loops are considered. The models are assessed in the light of available experimental evidence, in particular the magnitude of the corrosion rate and the velocity, downstream, temperature and oxygen effects. Currently recommended solubility values are used throughout. It is shown that the simple model based on these recommended values, which assumes that the dissolved metals are in equilibrium throughout the loop, overestimates the corrosion rate by three orders of magnitude. (author)

Nickel--chromium strain gages for cryogenic stress analysis of superconducting structures in high magnetic fields

International Nuclear Information System (INIS)

Freynik, H.S. Jr.; Roach, D.R.; Deis, D.W.; Hirzel, D.G.

1977-01-01

Evaluation and calibration measurements were performed on commercial nickel-chromium metal-foil strain gages in a high-magnetic-field (12 T), liquid-helium (4.2 K) environment. The purpose was to fully characterize strain gages for use at cryogenic temperatures in high magnetic fields. In this study, the magnetoresistance of a number of strain gages was measured in three orthogonal directions at mechanical strain levels to 8900 μm/m. As a result, a unique calibration curve was defined for magnetoresistance strain errors that is independent of strain level and field direction to 12 T at 4.2 K. A current strain-gage application is the measurement of superconductor mechanical properties. These gages will soon be used in the stress analysis of superconducting fusion magnets during cooldown from ambient temperatures and during operation at 4.2 K with magnetic fields to 12 T

Intracellular chromium localization and cell physiological response in the unicellular alga Micrasterias

Energy Technology Data Exchange (ETDEWEB)

Volland, Stefanie, E-mail: Stefanie.Volland@stud.sbg.ac.at [Plant Physiology Division, Cell Biology Department, University of Salzburg, Hellbrunnerstr 34, 5020 Salzburg (Austria); Luetz, Cornelius, E-mail: cornelius.luetz@uibk.ac.at [Institute of Botany, University of Innsbruck, Sternwartestrasse 15, 6020 Innsbruck (Austria); Michalke, Bernhard, E-mail: bernhard.michalke@helmholtz-muenchen.de [Helmholtz Zentrum Muenchen, German Research Centre for Environmental Health, Institute of Ecological Chemistry, Ingolstaedter Landstrasse 1, 85764 Neuherberg (Germany); Luetz-Meindl, Ursula, E-mail: ursula.luetz-meindl@sbg.ac.at [Plant Physiology Division, Cell Biology Department, University of Salzburg, Hellbrunnerstr 34, 5020 Salzburg (Austria)

2012-03-15

Various contaminants like metals and heavy metals are constantly released into the environment by anthropogenic activities. The heavy metal chromium has a wide industrial use and exists in two stable oxidation states: trivalent and hexavalent. Chromium can cause harm to cell metabolism and development, when it is taken up by plants instead of necessary micronutrients such as for example iron. The uptake of Cr VI into plant cells has been reported to be an active process via carriers of essential anions, while the cation Cr III seems to be taken up inactively. Micrasterias denticulata, an unicellular green alga of the family Desmidiaceae is a well-studied cell biological model organism. Cr III and VI had inhibiting effects on its cell development, while cell division rates were only impaired by Cr VI. Transmission electron microscopy (TEM) revealed ultrastructural changes such as increased vacuolization, condensed cytoplasm and dark precipitations in the cell wall after 3 weeks of Cr VI treatment. Electron energy loss spectroscopy (EELS) and electron spectroscopic imaging (ESI) were applied to measure intracellular chromium distribution. Chromium was only detected after 3 weeks of 10 {mu}M Cr VI treatment in electron dense precipitations found in bag-like structures along the inner side of the cell walls together with iron and elevated levels of oxygen, pointing toward an accumulation respectively extrusion of chromium in form of an iron-oxygen compound. Atomic emission spectroscopy (EMS) revealed that Micrasterias cells are able to accumulate considerable amounts of chromium and iron. During chromium treatment the Cr:Fe ratio shifted in favor of chromium, which implied that chromium may be taken up instead of iron. Significant and rapid increase of ROS production within the first 5 min of treatment confirms an active Cr VI uptake. SOD and CAT activity after Cr VI treatment did not show a response, while the glutathione pool determined by immuno-TEM decreased

Palmtop EPMA by electric battery

International Nuclear Information System (INIS)

Imashuku, Susumu; Imanishi, Akira; Kawai, Jun

2012-01-01

The measurement pressure of a palmtop electron probe X-ray microanalyzer (EPMA) we previously reported was reduced using stainless steel vacuum flanges for the chamber instead of a borosilicate glass tube. The improved palmtop EPMA could reach the measurement pressure of 1 Pa in 5 minutes. The time was more than twice shorter than that to reach the measurement pressure of 5 Pa with the palmtop EPMA we previously reported. Titanium, copper K lines and silver Lα line were observed during 90 seconds measurement in addition to chromium, iron, and nickel K lines when titanium, copper, and silver plates were placed on the carbon sample stage. Chromium, iron, and nickel K lines came from stainless steel, and copper K lines came from copper rod and copper plate placed on the sample stage. The improved palmtop EPMA can analyze metals except for chromium, iron, nickel, and small amount of copper in 90 seconds.

TEM characterisation of stress corrosion cracks in nickel based alloys: effect of chromium content and chemistry of environment; Caracterisation par MET de fissures de corrosion sous contrainte d'alliages a base de nickel: influence de la teneur en chrome et de la chimie du milieu

Energy Technology Data Exchange (ETDEWEB)

Delabrouille, F

2004-11-15

Stress corrosion cracking (SCC) is a damaging mode of alloys used in pressurized water reactors, particularly of nickel based alloys constituting the vapour generator tubes. Cracks appear on both primary and secondary sides of the tubes, and more frequently in locations where the environment is not well defined. SCC sensitivity of nickel based alloys depends of their chromium content, which lead to the replacement of alloy 600 (15 % Cr) by alloy 690 (30 % Cr) but this phenomenon is not yet very well understood. The goal of this thesis is two fold: i) observe the effect of chromium content on corrosion and ii) characterize the effect of environment on the damaging process of GV tubes. For this purpose, one industrial tube and several synthetic alloys - with controlled chromium content - have been studied. Various characterisation techniques were used to study the corrosion products on the surface and within the SCC cracks: SIMS; TEM - FEG: thin foil preparation, HAADF, EELS, EDX. The effect of chromium content and surface preparation on the generalised corrosion was evidenced for synthetic alloys. Moreover, we observed the penetration of oxygen along triple junctions of grain boundaries few micrometers under the free surface. SCC tests show the positive effect of chromium for contents varying from 5 to 30 % wt. Plastic deformation induces a modification of the structure, and thus of the protective character, of the internal chromium rich oxide layer. SCC cracks which developed in different chemical environments were characterised by TEM. The oxides which are formed within the cracks are different from what is observed on the free surface, which reveals a modification of medium and electrochemical conditions in the crack. Finally we were able to evidence some structural characteristics of the corrosion products (in the cracks and on the surface) which turn to be a signature of the chemical environment. (author)

76 FR 49450 - Stainless Steel Sheet and Strip in Coils From Germany, Italy, and Mexico: Revocation of...

Science.gov (United States)

2011-08-10

... products of a thickness of 4.75 mm or more), (4) flat wire (i.e., cold-rolled sections, with a prepared..., by weight, 36 percent nickel, 18 percent chromium, and 46 percent iron, and is most notable for its... contains, by weight, 11 to 13 percent chromium, and 7 to 10 percent nickel. Carbon, manganese, silicon and...

Method of fabricating thin-walled articles of tungsten-nickel-iron alloy

Science.gov (United States)

Hovis, Jr., Victor M.; Northcutt, Jr., Walter G.

1982-01-01

The present invention relates to a method for fabricating thin-walled high-density structures oftungsten-nickel-iron alloys. A powdered blend of the selected alloy constituents is plasma sprayed onto a mandrel having the desired article configuration. The sprayed deposit is removed from the mandrel and subjected to liquid phase sintering to provide the alloyed structure. The formation of the thin-walled structure by plasma spraying significantly reduces shrinkage, and cracking while increasing physical properties of the structure over that obtainable by employing previously known powder metallurgical procedures.

Experimental patch testing with chromium-coated materials.

Science.gov (United States)

Bregnbak, David; Thyssen, Jacob P; Jellesen, Morten S; Zachariae, Claus; Johansen, Jeanne D

2017-06-01

Chromium coatings on metal alloys can be decorative, and prevent corrosion and metal ion release. We recently showed that handling of a chromium-containing disc resulted in chromium deposition on the skin. To examine patch test reactivity to chromium-coated discs. We included 15 patients: 10 chromium-allergic patients, and 5 patients without chromium allergy. All were patch tested with potassium dichromate, cobalt chloride, nickel sulfate, and nine different metallic discs. The chromium-allergic patients were also patch tested with serial dilutions of potassium dichromate. Positive/weaker reactions were observed to disc B (1 of 10), disc C (1 of 10), and disc D, disc E, and disc I (4 of 10 each). As no controls reacted to any of the discs, the weak reactions indicate allergic reactions. Positive patch test reactions to 1770 ppm chromium(VI) in the serial dilutions of potassium dichromate were observed in 7 of 10 patients. When the case group was narrowed down to include only the patients with a current positive patch test reaction to potassium dichromate, elicitation of dermatitis by both chromium(III) and chromium(VI) discs was observed in 4 of 7 of patients. Many of the patients reacted to both chromium(III) and chromium(VI) surfaces. Our results indicate that both chromium(VI) and chromium(III) pose a risk to chromium-allergic patients. © 2017 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

Stress corrosion crack tip microstructure in nickel-based alloys

International Nuclear Information System (INIS)

Shei, S.A.; Yang, W.J.

1994-04-01

Stress corrosion cracking behavior of several nickel-base alloys in high temperature caustic environments has been evaluated. The crack tip and fracture surfaces were examined using Auger/ESCA and Analytical Electron Microscopy (AEM) to determine the near crack tip microstructure and microchemistry. Results showed formation of chromium-rich oxides at or near the crack tip and nickel-rich de-alloying layers away from the crack tip. The stress corrosion resistance of different nickel-base alloys in caustic may be explained by the preferential oxidation and dissolution of different alloying elements at the crack tip. Alloy 600 (UNS N06600) shows good general corrosion and intergranular attack resistance in caustic because of its high nickel content. Thermally treated Alloy 690 (UNS N06690) and Alloy 600 provide good stress corrosion cracking resistance because of high chromium contents along grain boundaries. Alloy 625 (UNS N06625) does not show as good stress corrosion cracking resistance as Alloy 690 or Alloy 600 because of its high molybdenum content

Research, development, and demonstration of nickel-iron batteries for electric vehicle propulsion. Annual report for 1980

Energy Technology Data Exchange (ETDEWEB)

1981-03-01

The FY 1980 program continued to involve full-size, prototype cell, module and battery fabrication and evaluation, aimed at advancing the technical capabilities of the nickel-iron battery, while simultaneously reducing its potential cost in materials and process areas. Improved Electroprecipitation Process (EPP) nickel electrodes of design thickness (2.5 mm) are now being prepared that display stable capacities of 23 to 25 Ah for the C/3 drain rate at 200+ test cycles. Iron electrodes of the composite-type are delivering 24 Ah at the target thickness (1.0 mm). Iron electrodes are displaying capacity stability for > 1000 test cycles in continuing 3 plate cell tests. Finished cells have delivered 57 to 61 Wh/kg at C/3, and have demonstrated cyclic stability to 500+ cycles at 80% depth of discharge profiles at Westinghouse. A 6-cell module that demonstrated 239 Ah, 1735 Wh, 48 Wh/kg at the C/3 drain rate has also been evaluated at the National Battery Test Laboratory, ANL. It operated for 327 test cycles, to a level of 161 Ah at the C/3 rate, before being removed from test. Reduction in nickel electrode swelling (and concurrent stack starvation), to improve cycling, continues to be an area of major effort to reach the final battery cycle life objectives. Pasted nickel electrodes continue to show promise for meeting the life objectives while, simultaneously, providing a low manufacturing cost. Refinements have occurred in the areas of cell hardware, module manifolding and cell interconnections. These improvements have been incorporated into the construction and testing of the cells and modules for this program. Temperature tests at 0/sup 0/C were performed on a 6-cell module and showed a decrease in capacity of only 25% in Ah and .29% in Wh as compared to 25/sup 0/C performance. Additional tests are planned to demonstrate performance at -15/sup 0/C and 40/sup 0/C.

Effect of chromium and phosphorus on the physical properties of iron and titanium-based amorphous metallic alloy films

Science.gov (United States)

Distefano, S.; Rameshan, R.; Fitzgerald, D. J.

1991-01-01

Amorphous iron and titanium-based alloys containing various amounts of chromium, phosphorus, and boron exhibit high corrosion resistance. Some physical properties of Fe and Ti-based metallic alloy films deposited on a glass substrate by a dc-magnetron sputtering technique are reported. The films were characterized using differential scanning calorimetry, stress analysis, SEM, XRD, SIMS, electron microprobe, and potentiodynamic polarization techniques.

High density tungsten-nickel-iron-cobalt alloys having improved hardness and method for making same

International Nuclear Information System (INIS)

Penrice, T.W.; Bost, J.

1988-01-01

This patent describes the process of making high density alloy containing about 85 to 98 weight percent tungsten and the balance of the alloy being essentially a binder of nickel, iron and cobalt, and wherein the cobalt is present in an amount within the range of about 5 to 47.5 weight percent of the binder, comprising: blending powders of the tungsten, nickel, iron and cobalt into a homogeneous composition, compacting the homogeneous composition into a shaped article, heating the shaped article to a temperature and for a time sufficient to sinter the article, subjecting the sintered article to a temperature sufficient to enable the intermetallic phase formed at the matrix to tungsten interface to diffuse into the gamma austenitic phase whereby the alpha tungsten/gamma austenite boundaries are essentially free of such intermetallic phase, quenching the article, and swaging the article to a reduction in area of about 5 to 40 percent, the article having improved mechanical properties, including improved tensile strength and hardness while maintaining suitable ductility for subsequent working thereof

Synthesis and characterization of ceramic pigments based on oxides of chromium and iron, on TiO2

International Nuclear Information System (INIS)

Silva, E.M. da; Galvao, S.B.; Paskocimas, C.A.

2011-01-01

This work used oxides of chromium and iron, as precursors of the synthesis of ceramic pigments. The synthesis is based on the dissolution of citric acid as a complexing agent, addition of metal oxides, such as ion chromophores; polymerization with ethylene glycol and doping with titanium oxide. Passing through pre-calcination, breakdown, calcination at different temperatures (900 and 1100 ° C), resulting in pigments: green for pigment chrome deposited on TiO 2 and orange for iron on TiO 2 . Noticing an increase in the opacity with increasing temperature. The thermal analysis (TG and DTA), evaluated their thermal behavior, the XRD revealed the formation of crystalline phases as Iron Titanate and Chrome Titanate; SEM showed the formation of hexagonal particles for both oxides. Thus, the synthesized oxides were within the requirements for application as ceramic pigments. (author)

Heat exchanger tubing materials for CANDU nuclear generating stations

International Nuclear Information System (INIS)

Taylor, G.F.

1977-07-01

The performance of steam generator tubing (nickel-chromium-iron alloy in NPD and nickel-copper alloy in Douglas Point and Pickering generating stations) has been outstanding and no corrosion-induced failures have occurred. The primary coolant will be allowed to boil in the 600 MW (electrical) CANDU-PHW reactors. An iron-nickel-chromium alloy has been selected for the steam generator tubing because it will result in lower radiation fields than the alloys used before. It is also more resistant than nickel-chromium-iron alloy to stress corrosion cracking in the high purity water of the primary circuit, an unlikely but conceivable hazard associated with higher operating temperatures. Austenitic alloy and ferritic-austenitic stainless steel tubing have been selected for the moderator coolers in CANDU reactors being designed and under construction. These materials will reduce the radiation fields around the moderator circuit while retaining the good resistance to corrosion in service water that has characterized the copper-nickel alloys now in use. Brass and bronze tubes in feedwater heaters and condensers have given satisfactory service but do, however, complicate corrosion control in the steam cycle and, to reduce the transport of corrosion products from the feedtrain to the steam generator, stainless steel is preferred for feedwater heaters and stainlss steel or titanium for condensers. (author)

Enhancement in the Tribological and Mechanical Properties of Electroless Nickel-Nanodiamond Coatings Plated on Iron

Directory of Open Access Journals (Sweden)

Z. Karaguiozova

2017-12-01

Full Text Available A technology to improve the tribological and mechanical surface properties of iron alloys is developed based on the electroless nickel plating. The technology combines sol-gel and electroless deposition technique. Novel nanocomposite coatings are obtained consisting of Nickel-phosphorus-nanodiamond (Ni-P-ND. The ND sol is added directly to the electroless Ni-P solution. A suitable surfactant is added to achieve well-dispersed ND particles in the electroless solution to facilitate their embodiment and equal distribution in the coating. Substrates of steel 17CrNiMo6 and spheroidal graphite cast irons are used for the manufacture of the iron alloys specimens. The surface morphology and microstructure observation performed by scanning electron microscopy (SEM and optical metallography confirms the influence of ND particles on the coating structure. The structural phase investigation by X Ray analysis indicates a transformation of the amorphous phase to a crystalline one such as Ni, Ni3P after coatings' heat treatment. The microhardness investigation by Knoop Method and wear resistance measurement in accordance with the Polish Standard PN-83/H-04302 of Ni-P and Ni-P-ND composite coatings are evaluated and compared with each other. The increase in the value of hardness and wear resistance of Ni-P composite coatings in the presence of ND particles and after heat treatment is obtained.

The impact of engineered cobalt, iron, nickel and silver nanoparticles on soil bacterial diversity under field conditions

International Nuclear Information System (INIS)

Shah, Vishal; Collins, Daniel; Shah, Shreya; Walker, Virginia K

2014-01-01

Our understanding of how engineered nanoparticles (NPs) migrate through soil and affect microbial communities is scarce. In the current study we examined how metal NPs, including those from the iron triad (iron, cobalt and nickel), moved through pots of soil maintained under winter field conditions for 50 days, when mesophilic bacteria may not be dividing. Based on total metal analysis, cobalt and nickel were localized in the top layer of soil, even after exposure to high precipitation and freeze–thaw cycles. In contrast, a bimodal distribution of silver was observed. Due to high endogenous levels of iron, the migration pattern of these NPs could not be determined. Pyrosequence analysis of the bacterial communities revealed that there was no significant engineered NP-mediated decline in microbial richness. However, analysis of individual genera showed that Sphingomonas and Lysobacter were represented by fewer sequences in horizons containing elevated metal levels whereas there was an increase in the numbers of Flavobacterium and Niastella. Collectively, the results indicate that along with the differential migration behavior of NPs in the soil matrix, their impact on soil bacterial diversity appears to be dependent on environmental parameters. (paper)

Effects of carbon and molybdenum on the microstructures of high chromium white cast irons

International Nuclear Information System (INIS)

Sinatora, Amilton; Ambrosio Filho, Francisco; Goldenstein, Helio; Fuoco, Ricardo; Albertin, Eduardo; Mei, Paulo Roberto

1992-01-01

The effects of 3 levels of carbon and 1.5% Mo addition on the solidification structures of a 15% chromium white cast iron were studied. The volume fraction of primary austenite and of eutectic carbides, as well as the number of carbide particles per unit length and the mean secondary dendrite arm spacing were measured. By means of thermal analysis, thermal arrest corresponding to the formation of the primary austenite and of the eutectic were determined. The increase in the carbon content and the addition of Mo led to lowering of the thermal arrests and to coarsening of the particles. (author)

Effect of carbon and silicon on nitrogen solubility in liquid chromium and iron-chromium alloys

International Nuclear Information System (INIS)

Khyakkinen, V.I.; Bezobrazov, S.V.

1986-01-01

The study is aimed at specifying the role of carbon and silicon in high-chromium melts nitridation processes. It is shown that in high-chromium melts of the Cr-Fe-C system the nitrogen solubility is reduced with the growth of carbon content and in the chromium concentration range of 70-100% at 1873 K and P N 2 =0.1 MPa it is described by the lg[%N] Cr-Fe-C =lg[%N] cr-fe -0.098[%C] equation. While decreasing the temperature the nitrogen solubility in alloys is increased. Silicon essentially decreases the nitrogen solubility in liquid chromium. For the 0-10% silicon concentration range the relation between the equilibrium content of nitrogen and silicon at 1873 K and P N 2 =0.1 MPa is described by the straight line equation [%N] Cr-Si =6.1-0.338 [%Si

Energy of the Isolated Metastable Iron-Nickel FCC Nanocluster with a Carbon Atom in the Tetragonal Interstice.

Science.gov (United States)

Bondarenko, Natalya V; Nedolya, Anatoliy V

2017-12-01

The energy of the isolated iron-nickel nanocluster was calculated by molecular mechanics method using Lennard-Jones potential. The cluster included a carbon atom that drifted from an inside octahedral interstice to a tetrahedral interstice in [Formula: see text] direction and after that in direction to the surface. In addition, one of 14 iron atoms was replaced by a nickel atom, the position of which was changing during simulation.The energy of the nanocluster was estimated at the different interatomic distances. As a result of simulation, the optimal interatomic distances of Fe-Ni-C nanocluster was chosen for the simulation, in which height of the potential barrier was maximal and face-centered cubic (FCC) nanocluster was the most stable.It is shown that there were three main positions of a nickel atom that significantly affected nanocluster's energy.The calculation results indicated that position of the carbon atom in the octahedral interstice was more energetically favorable than tetrahedral interstice in the case of FCC nanocluster. On the other side, the potential barrier was smaller in the direction [Formula: see text] than in the direction .This indicates that there are two ways for carbon atom to drift to the surface of the nanocluster.

Hydrogen-water deuterium exchange over metal oxide promoted nickel catalysts

Energy Technology Data Exchange (ETDEWEB)

Sagert, N H; Shaw-Wood, P E; Pouteau, R M.L. [Atomic Energy of Canada Ltd., Pinawa, Manitoba. Whiteshell Nuclear Research Establishment

1975-11-01

Specific rates have been measured for hydrogen-water deuterium isotope exchange over unsupported nickel promoted with about 20% of various metal oxides. The oxides used were Cr/sub 2/O/sub 3/, MoO/sub 2/, MnO, WO/sub 2/-WO/sub 3/, and UO/sub 2/. Nickel surface areas, which are required to measure the specific rates, were determined by hydrogen chemisorption. Specific rates were measured as a function of temperature in the range 353 to 573 K and as a function of the partial pressure of hydrogen and water over a 10-fold range of partial pressure. The molybdenum and tungsten oxides gave the highest specific rates, and manganese and uranium oxides the lowest. Chromium oxide was intermediate, although it gave the highest rate per gram of catalyst. The orders with respect to hydrogen and water over molybdenum oxide and tungsten oxide promoted nickel were consistent with a mechanism in which nickel oxide is formed from the reaction of water with the catalyst, and then is reduced by hydrogen. Over manganese and uranium oxide promoted catalysts, these orders are consistent with a mechanism in which adsorbed water exchanges with chemisorbed hydrogen atoms on the nickel surface. Chromium oxide is intermediate. It was noted that those oxides which favored the nickel oxide route had electronic work functions closest to those of metallic nickel and nickel oxide.

Intracellular chromium localization and cell physiological response in the unicellular alga Micrasterias

Science.gov (United States)

Volland, Stefanie; Lütz, Cornelius; Michalke, Bernhard; Lütz-Meindl, Ursula

2012-01-01

Various contaminants like metals and heavy metals are constantly released into the environment by anthropogenic activities. The heavy metal chromium has a wide industrial use and exists in two stable oxidation states: trivalent and hexavalent. Chromium can cause harm to cell metabolism and development, when it is taken up by plants instead of necessary micronutrients such as for example iron. The uptake of Cr VI into plant cells has been reported to be an active process via carriers of essential anions, while the cation Cr III seems to be taken up inactively. Micrasterias denticulata, an unicellular green alga of the family Desmidiaceae is a well-studied cell biological model organism. Cr III and VI had inhibiting effects on its cell development, while cell division rates were only impaired by Cr VI. Transmission electron microscopy (TEM) revealed ultrastructural changes such as increased vacuolization, condensed cytoplasm and dark precipitations in the cell wall after 3 weeks of Cr VI treatment. Electron energy loss spectroscopy (EELS) and electron spectroscopic imaging (ESI) were applied to measure intracellular chromium distribution. Chromium was only detected after 3 weeks of 10 μM Cr VI treatment in electron dense precipitations found in bag-like structures along the inner side of the cell walls together with iron and elevated levels of oxygen, pointing toward an accumulation respectively extrusion of chromium in form of an iron–oxygen compound. Atomic emission spectroscopy (EMS) revealed that Micrasterias cells are able to accumulate considerable amounts of chromium and iron. During chromium treatment the Cr:Fe ratio shifted in favor of chromium, which implied that chromium may be taken up instead of iron. Significant and rapid increase of ROS production within the first 5 min of treatment confirms an active Cr VI uptake. SOD and CAT activity after Cr VI treatment did not show a response, while the glutathione pool determined by immuno-TEM decreased

Intracellular chromium localization and cell physiological response in the unicellular alga Micrasterias

International Nuclear Information System (INIS)

Volland, Stefanie; Lütz, Cornelius; Michalke, Bernhard; Lütz-Meindl, Ursula

2012-01-01

Various contaminants like metals and heavy metals are constantly released into the environment by anthropogenic activities. The heavy metal chromium has a wide industrial use and exists in two stable oxidation states: trivalent and hexavalent. Chromium can cause harm to cell metabolism and development, when it is taken up by plants instead of necessary micronutrients such as for example iron. The uptake of Cr VI into plant cells has been reported to be an active process via carriers of essential anions, while the cation Cr III seems to be taken up inactively. Micrasterias denticulata, an unicellular green alga of the family Desmidiaceae is a well-studied cell biological model organism. Cr III and VI had inhibiting effects on its cell development, while cell division rates were only impaired by Cr VI. Transmission electron microscopy (TEM) revealed ultrastructural changes such as increased vacuolization, condensed cytoplasm and dark precipitations in the cell wall after 3 weeks of Cr VI treatment. Electron energy loss spectroscopy (EELS) and electron spectroscopic imaging (ESI) were applied to measure intracellular chromium distribution. Chromium was only detected after 3 weeks of 10 μM Cr VI treatment in electron dense precipitations found in bag-like structures along the inner side of the cell walls together with iron and elevated levels of oxygen, pointing toward an accumulation respectively extrusion of chromium in form of an iron–oxygen compound. Atomic emission spectroscopy (EMS) revealed that Micrasterias cells are able to accumulate considerable amounts of chromium and iron. During chromium treatment the Cr:Fe ratio shifted in favor of chromium, which implied that chromium may be taken up instead of iron. Significant and rapid increase of ROS production within the first 5 min of treatment confirms an active Cr VI uptake. SOD and CAT activity after Cr VI treatment did not show a response, while the glutathione pool determined by immuno-TEM decreased

Concentrations of the genotoxic metals, chromium and nickel, in whales, tar balls, oil slicks, and released oil from the gulf of Mexico in the immediate aftermath of the deepwater horizon oil crisis: is genotoxic metal exposure part of the deepwater horizon legacy?

Science.gov (United States)

Wise, John Pierce; Wise, James T F; Wise, Catherine F; Wise, Sandra S; Gianios, Christy; Xie, Hong; Thompson, W Douglas; Perkins, Christopher; Falank, Carolyne; Wise, John Pierce

2014-01-01

Concern regarding the Deepwater Horizon oil crisis has largely focused on oil and dispersants while the threat of genotoxic metals in the oil has gone largely overlooked. Genotoxic metals, such as chromium and nickel, damage DNA and bioaccumulate in organisms, resulting in persistent exposures. We found chromium and nickel concentrations ranged from 0.24 to 8.46 ppm in crude oil from the riser, oil from slicks on surface waters and tar balls from Gulf of Mexico beaches. We found nickel concentrations ranged from 1.7 to 94.6 ppm wet weight with a mean of 15.9 ± 3.5 ppm and chromium concentrations ranged from 2.0 to 73.6 ppm wet weight with a mean of 12.8 ± 2.6 ppm in tissue collected from Gulf of Mexico whales in the wake of the crisis. Mean tissue concentrations were significantly higher than those found in whales collected around the world prior to the spill. Given the capacity of these metals to damage DNA, their presence in the oil, and their elevated concentrations in whales, we suggest that metal exposure is an important understudied concern for the Deepwater Horizon oil disaster.

Chromium(VI) release from leather and metals can be detected with a diphenylcarbazide spot test.

Science.gov (United States)

Bregnbak, David; Johansen, Jeanne D; Jellesen, Morten S; Zachariae, Claus; Thyssen, Jacob P

2015-11-01

Along with chromium, nickel and cobalt are the clinically most important metal allergens. However, unlike for nickel and cobalt, there is no validated colorimetric spot test that detects chromium. Such a test could help both clinicians and their patients with chromium dermatitis to identify culprit exposures. To evaluate the use of diphenylcarbazide (DPC) as a spot test reagent for the identification of chromium(VI) release. A colorimetric chromium(VI) spot test based on DPC was prepared and used on different items from small market surveys. The DPC spot test was able to identify chromium(VI) release at 0.5 ppm without interference from other pure metals, alloys, or leather. A market survey using the test showed no chromium(VI) release from work tools (0/100). However, chromium(VI) release from metal screws (7/60), one earring (1/50), leather shoes (4/100) and leather gloves (6/11) was observed. We found no false-positive test reactions. Confirmatory testing was performed with X-ray fluorescence (XRF) and spectrophotometrically on extraction fluids. The use of DPC as a colorimetric spot test reagent appears to be a good and valid test method for detecting the release of chromium(VI) ions from leather and metal articles. The spot test has the potential to become a valuable screening tool. © 2015 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

High-solid mesophilic methane fermentation of food waste with an emphasis on Iron, Cobalt, and Nickel requirements.

Science.gov (United States)

Qiang, Hong; Lang, Dong-Li; Li, Yu-You

2012-01-01

The effect of trace metals on the mesophilic methane fermentation of high-solid food waste was investigated using both batch and continuous experiments. The continuous experiment was conducted by using a CSTR-type reactor with three run. During the first run, the HRT of the reactor was stepwise decreased from 100 days to 30 days. From operation day 50, the reactor efficiency deteriorated due to the lack of trace metals. The batch experiment showed that iron, cobalt, and nickel combinations had a significant effect on food waste. According to the results of the batch experiment, a combination of iron, cobalt, and nickel was added into the CSTR reactor by two different methods at run II, and III. Based on experimental results and theoretical calculations, the most suitable values of Fe/COD, Co/COD, and Ni/COD in the substrate were identified as 200, 6.0, and 5.7 mg/kg COD, respectively. Copyright © 2011 Elsevier Ltd. All rights reserved.

Liquid-Liquid Extraction and Determination of Trace Elements in Iron Minerals by Atomic Absorption Spectrometry

International Nuclear Information System (INIS)

Taseska, Milena; Stafilov, Trajche; Makreski, Petre; Jacimovic, Radojko; Jovanovski, Gligor

2006-01-01

Various trace elements (cadmium, chromium, cobalt, nickel, manganese) in some iron minerals were determined by flame (FAAS) and electrothermal atomic absorption spectrometry (ETAAS). The studied minerals were chalcopyrite (CuFeS 2 ), hematite (Fe 2 O 3 ) and pyrite (FeS 2 ). To avoid the interference of iron, a method for liquid-liquid extraction of iron and determination of investigated elements in the inorganic phase was proposed. Iron was extracted by diisopropyl ether in hydrochloride acid solution and the extraction method was optimized. Some parameters were obtained to be significantly important: Fe mass in the sample should not exceed 0.3 g, the optimal concentration of HCI should be 7.8 mol 1 -1 and ratio of the inorganic and organic phase should be 1: 1. The procedure was verified by the method of standard additions and by its applications to reference standard samples. The investigated minerals originate from various mines in the Republic of Macedonia. (Author)

Positive muon diffusion in iron and nickel pressure dependence

CERN Document Server

Butz, T; Dufresne, J F; Hartmann, O; Karlsson, E; Lindgren, B; Longobardi, R; Norlin, L O; Pezzetti, J P; Yaouanc, A

1980-01-01

The hyperfine field B/sub hf/ at positive muon ( mu /sup +/) in iron and nickel was previously found. Exhibits marked deviations from the bulk magnetization as a function of temperature. For substitutional impurities in Fe and Ni matrices the volume dependence of B/sub hf/ has been considered as a possible reason for such deviations. Therefore the authors have measured at CERN the local magnetic field at mu /sup +/, B/sub mu /, in high purity polycrystalline Fe and Ni samples at room temperature and at pressures up to 7 kbar by the positive muon spin rotation ( mu /sup +/ SR) technique. To their knowledge, this is the first mu /sup +/SR experiment performed under hydrostatic pressure. The authors observe a linear pressure dependence for both samples but slopes are of opposite signs. (12 refs).

Investigations on the binary systems of boron with chromium, columbium, nickel, and thorium, including a discussion of the Phase TiB in the titanium-boron system

Energy Technology Data Exchange (ETDEWEB)

Andersson, L H; Kiessling, R

1950-01-01

Investigations on the binary systems chromium-, columbium-, nickel-, and thorium-boron are reported. The titanium-boron system is discussed, and it is shown that the phase TiB, previously assumed to have zincblende structure, probably has a face-centered titanium lattice with boron in the octahedral interstices. In the chromium-boron system, the structure of the eta phase has been determined. It has the composition Cr/sub 3/B/sub 4/ and is isomorphous with Ta/sub 3/B/sub 4/ and Mn/sub 3/B/sub 4/. Some data for the delta phase are also given. For the columbium-boron system, a phase analysis has been carried out. The structures of three of the intermediary phases, CbB, Cb/sub 3/B/sub 2/, and CbB/sub 2/ (with extended homogeneity range), have been determined. They are isomorphous with corresponding phases of the tantalum-boron system. A brief phase analysis of the nickel-boron system showed the existence of a phase with lower boron content than Ni/sub 2/B, which has not been previously reported. In the thorium-boron system a new phase, probably with a complicated structure, was found with a boron content of about 50 at. %.

Thermal neutron capture cross section of chromium, vanadium, titanium and nickel isotopes

International Nuclear Information System (INIS)

Venturini, L.; Pecequilo, B.R.S.

1990-04-01

The thermal neutron cross section of chromium, vanadium, titanium and nickel can be determined by measuring the pair spectrum of prompt gamma-rays emitted targets of these elements are irradiated by a thermal neutron beam. Such measurements were carried out by irradiating the natural element mixed with a nitrogen standard (melamine) in the tangential beam hole of the IEA-R1 research reactor. The pair spectrometer efficiency calibration curve in the 1.5 to 11 MeV energy range was performed with a melamine plus ammonium chloride mixed target. The cross section was calculated for the most prominent gamma transitions of each isotope, using nitrogen as standard and averaged over the obtained values. The resulting mean cross sections are as follows: (13.4 ± 0.7)b for 50 Cr, (0.79 ± 0,02)b for 52 Cr, (18.1 ± 0,7)b for 53 Cr, (4.9 ± 0.2)b for 51 V, (8.4 ± 0.1)b for 48 Ti, (4.41 ± 0.08)b 58 Ni, (2.54 ± 0.07)b for 60 Ni, (15.2 ± 0.5)b for 62 Ni and (1.6 ± 0.1) for 64 Ni. (author) [pt

Impacts of iron and steelmaking facilities on soil quality.

Science.gov (United States)

Strezov, Vladimir; Chaudhary, Chandrakant

2017-12-01

Iron and steel are highly important materials used in a wide range of products with important contribution to the economic development. The processes for making iron and steel are energy intensive and known to contribute to local pollution. Deposition of the metals may also have adverse impacts on soil quality, which requires detailed assessment. The aim of this study was to investigate the impacts of iron and steelmaking facilities on the local soil quality. Soil samples were collected in the vicinity of two steelmaking sites in Australia, one based on blast furnace steelmaking operation, while the second site was based on electric arc furnace steel recycling. The soil samples were compared to a background site where no industrial impact is expected. The soil collected near industrial facilities contained larger toxic metal contents, however this concentration for all priority metals was within the Australian National Environmental Protection Measure guidelines for the acceptable recreational soil quality. When compared to the international soil quality guidelines, some of the soils collected near the industrial sites, particularly near the blast furnace operated steelmaking, exceeded the arsenic, iron and manganese (according to United States Environmental Protection Agency guidelines) and chromium, copper and nickel concentrations (according to the Canadian guidelines). The work further provided a novel environmental assessment model taking into consideration the environmental and health impacts of each element. The environmental assessment revealed most significant contribution of manganese, followed by titanium, zinc, chromium and lead. Titanium was the second most important contributor to the soil quality, however this metal is currently not included in any of the international soil quality guidelines. Copyright © 2017 Elsevier Ltd. All rights reserved.

Effect of pulp density and particle size on indirect bioleaching of Pomalaa nickel laterite using metabolic citric acid

Science.gov (United States)

Petrus, H. B. T. M.; Wanta, K. C.; Setiawan, H.; Perdana, I.; Astuti, W.

2018-01-01

Nickel laterite ore contains oxide of iron, aluminum or both with nickel, cobalt and chromium which can be leached out using hydrometallurgical process. For the purpose of meeting the world’s increasing demand of nickel, there is a need to invent environmentally friendly process to efficiently leach nickel. This experiment used nickel laterite ore obtained from Pomalaa, South Sulawesi. The leaching agent is metabolic citric acid produced by Aspergillus niger under optimum condition. Leaching process was done in three-necked flask in atmospheric temperature and constant stirring speed of 200 rpm. The variable examined in the experiment was pulp density and particle size of nickel laterite ore. Samples were taken at 3, 7, 10, 14, and 17 minutes and then filtered and diluted to be analyzed using ICP-AES. The result of the experiment showed the maximum recovery of metals increase with the decrease of the pulp density. The maximum recovery for varying pulp density were at 5% solid/liquid ratio and the recovery were Ni at 1.63%, Al at 0.47%, Fe at 0.23% and Mg at 1.09%. The effect of particle size on leaching process showed that the leaching process follows the shrinking core model. The maximum recovery of metals at particle size were at 100-120 mesh with Ni at 1.37%, Fe at 0.10%, Al at 0.72% and Mg at 0.62%.

Comparison of low cycle fatigue of ductile cast irons with different matrix alloyed with nickel

Czech Academy of Sciences Publication Activity Database

Petrenec, Martin; Tesařová, H.; Beran, Přemysl; Šmíd, Miroslav; Roupcová, Pavla

2010-01-01

Roč. 2, č. 1 (2010), s. 2307-2316 E-ISSN 1877-7058. [ Fatigue 2010. Praha, 06.06.2010-11.06.2010] R&D Projects: GA ČR GAP108/10/2371 Institutional research plan: CEZ:AV0Z20410507; CEZ:AV0Z10480505 Keywords : Low cycle fatigue * ferritic ductile cast iron * ADI * nickel alloying * neutron diffraction Subject RIV: JL - Materials Fatigue , Friction Mechanics

Superhydrophobic surface fabricated on iron substrate by black chromium electrodeposition and its corrosion resistance property

Energy Technology Data Exchange (ETDEWEB)

Zhang, Bo [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008, Qinghai (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Key Lab of Comprehensive and Highly Efficient Utilization of Salt Lake Resource, Chinese Academy of Science, Xining 810008, Qinghai (China); Feng, Haitao [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008, Qinghai (China); Key Lab of Comprehensive and Highly Efficient Utilization of Salt Lake Resource, Chinese Academy of Science, Xining 810008, Qinghai (China); Lin, Feng [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008, Qinghai (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Wang, Yabin [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008, Qinghai (China); Key Lab of Comprehensive and Highly Efficient Utilization of Salt Lake Resource, Chinese Academy of Science, Xining 810008, Qinghai (China); Wang, Liping [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008, Qinghai (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Dong, Yaping [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008, Qinghai (China); Key Lab of Comprehensive and Highly Efficient Utilization of Salt Lake Resource, Chinese Academy of Science, Xining 810008, Qinghai (China); Li, Wu, E-mail: liwu2016@126.com [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008, Qinghai (China); Key Lab of Comprehensive and Highly Efficient Utilization of Salt Lake Resource, Chinese Academy of Science, Xining 810008, Qinghai (China)

2016-08-15

Highlights: • Superhydrophobic surface was fabricated by black chromium electrodeposition and stearic acid modification. • The reaction process is simple, and of low cost, and no special instrument or environment is needed. • The obtained superhydrophobic surface presents good water repellency, and performs well at corrosion resistance. - Abstract: The fabrication of superhydrophobic surface on iron substrate is carried out through 20 min black chromium electrodeposition, followed by immersing in 0.05 M ethanolic stearic acid solution for 12 h. The resultant superhydrophobic complex film is characterized by scanning electron microscope (SEM), disperse Spectrometer (EDS), atomic force microscope (AFM), water contact angle (CA), sliding angle (SA) and X-ray photoelectron spectroscope (XPS), and its corrosion resistance property is measured with cyclic voltammetry (CV), linear polarization and electrochemical impedance spectroscopy (EIS). The results show that the fabricated superhydrophobic film has excellent water repellency (CA, 158.8°; SA, 2.1°) and significantly high corrosion resistance (1.31 × 10{sup 6} Ω cm{sup −2}) and excellent corrosion protection efficiency (99.94%).

Recovery Of Nickel From Spent Nickel-Cadmium Batteries Using A Direct Reduction Process

Directory of Open Access Journals (Sweden)

Shin D.J.

2015-06-01

Full Text Available Most nickel is produced as Ferro-Nickel through a smelting process from Ni-bearing ore. However, these days, there have been some problems in nickel production due to exhaustion and the low-grade of Ni-bearing ore. Moreover, the smelting process results in a large amount of wastewater, slag and environmental risk. Therefore, in this research, spent Ni-Cd batteries were used as a base material instead of Ni-bearing ore for the recovery of Fe-Ni alloy through a direct reduction process. Spent Ni-Cd batteries contain 24wt% Ni, 18.5wt% Cd, 12.1% C and 27.5wt% polymers such as KOH. For pre-treatment, Cd was vaporized at 1024K. In order to evaluate the reduction conditions of nickel oxide and iron oxide, pre-treated spent Ni-Cd batteries were experimented on under various temperatures, gas-atmospheres and crucible materials. By a series of process, alloys containing 75 wt% Ni and 20 wt% Fe were produced. From the results, the reduction mechanism of nickel oxide and iron oxide were investigated.

THE INFLUENCE OF CHEMICAL COMPOSITION OF HIGH-CHROMIUM CAST IRONS ON THE MACHINABILITY

Directory of Open Access Journals (Sweden)

V. V. Netrebko

2016-02-01

Full Text Available Purpose. This research is aimed to obtain the regression dependence of the machinability on the chemical composition of pig iron (C, Cr, Mn and Ni in cast state. Methodology. The method of active experiment planning was used to build a mathematical model. Cast irons of composition 1.09…3.91 % С; 11.43…25.57 % Cr; 0.6…5.4 % Mn; 0.19…3.01 % Ni were studied. Cutting tools with plates 10х10 mm out of ВК8 according to State Standard 19051-80 were used for turning. Cutting modes: cutting depth – 0.8 mm, longitudinal feed – 0.15 mm/rot., spindle’s rotation frequency during turning – 200…360 rot./min. Lubricating and cooling liquids were not applied. Evaluation of iron workability was produced by determining the linear tool flank wear per unit length of the cutting path. Findings. Mathematically probabilistic equation of the regression dependence of the cutting tool’s wear on the C, Cr, Mn and Ni content in the machined cast iron were obtained. It was established that with the increase of Cr content in the cast iron to 14.8 % the cutting tool’s wear decreased as a result of formation of carbide eutectic which destroyed the doped ledeburite continuous frame. Further increase of chromium content promoted appearing of chromic carbides with high microhardness which considerably increased the tool’s wear. The conducted research shown that the minimum cutting tool’s wear 0,18 mkm/m was observed during the machining of cast iron containing: 1.09 % C, 14.8 % Cr, 2.3 % Mn and 1.2 % Ni; and the maximum wear is 48,96 mkm/m – when the content was: 3.91 % C, 11.43 % Cr, 5.4 % Mn and 0.19 % Ni. The tool’s wear reached 47.61 mkm/m during the treatment of cast iron containing 3.91 % C, 25.57 % Cr, 5.4 % Mn and 0.19 % Ni. Originality. Mathematically probabilistic model of the dependence of the cutting tool’s wear on the C, Cr, Mn and Ni content in the machined cast iron has been elaborated by the author. Practical value. The model

Radiation-enhanced diffusion in nickel-10.6% chromium alloys

International Nuclear Information System (INIS)

Gieb, M.

1995-01-01

Results of investigations of the diffusion rate of nickel-10.6% chromium alloys after plastic deformation, after quenching from 700 C and from 1030 C, and during irradiation with 18 MeV protons and 1.85 MeV electrons are reported. The diffusion rate is measured by means of the electrical resistivity which increases with increasing degree of short range order. It was found that the characteristic temperature below which short range order develops is T t =550 C. Below about 400 C the atomic mobilities of the component atoms of the alloy are so small that no further increase in the degree of short range order is found in due laboratory times. The activation energy for self-diffusion was determined after quenching from 700 C to Q SD =2.88 eV. For the migration activation energy of vacancies a value of E M 1V =1.18 eV was obtained after quenching from 1030 C. For the migration activation energies of interstitials and vacancies values of E M 1I =1.04 eV and E M 1V =1.16 eV are derived from results of measurements of radiation enhanced diffusion, respectively. These values decrease with increasing high energy particle flux. The characteristic temperature for interstitial cluster formation is T t =300 C. Above this temperature radiation-induced interstitials and vacancies annihilate mainly by pair recombination. Below this temperature interstitials also annihilate at sinks which are formed during irradiation so that the concentration of vacancies increases with irradiation time. Their migration activation energy is approximately obtained in a straight-forward way from the experimental data. Above about 380 C the radiation enhanced diffusion rate is surprisingly much smaller than the thermal diffusion rate. The quasi-dynamic vacancy concentration built up during irradiation is much smaller than the thermal vacancy concentration. (orig.)

Seal welded cast iron nuclear waste container

International Nuclear Information System (INIS)

Filippi, A.M.; Sprecace, R.P.

1987-01-01

An article of manufacture is described comprising a cast iron container having an opening at one end and a cast iron plug; a first nickel-carbon alloy fusion weldable insert surrounding the opening and metallurgically bonded to the cast iron container at the one end of the container; a second nickel-carbon alloy insert metallurgically bonded to the cast iron plug located within the opening and surrounded by the first insert the inserts being jointed by a fusion bond in the opening without heating the cast iron container to an austenite formation temperature thereby sealing the interior of the container from the exterior ambient outside the opening; the nickel-carbon alloy containing about 2 to 5 w% carbon; and both the nickel-carbon alloy insert and the cast iron container have a microstructure containing a graphite phase

REMOVAL OF HEXAVALENT CHROMIUM FROM DRINKING WATER

Directory of Open Access Journals (Sweden)

A. R. Asgari ، F. Vaezi ، S. Nasseri ، O. Dördelmann ، A. H. Mahvi ، E. Dehghani Fard

2008-10-01

Full Text Available Removal of chromium can be accomplished by various methods but none of them is cost-effective in meeting drinking water standards. For this study, granular ferric hydroxide was used as adsorbent for removal of hexavalent chromium. Besides, the effects of changing contact time, pH and concentrations of competitive anions were determined for different amounts of granular ferric hydroxide. It was found that granular ferric hydroxide has a high capacity for adsorption of hexavalent chromium from water at pH≤7 and in 90 min contact time. Maximum adsorption capacity was determined to be 0.788 mg Cr+6/g granular ferric hydroxide. Although relatively good adsorption of sulfate and chloride had been specified in this study, the interfering effects of these two anions had not been detected in concentrations of 200 and 400 mg/L. The absorbability of hexavalent chromium by granular ferric hydroxide could be expressed by Freundlich isotherm with R2>0.968. However, the disadvantage was that the iron concentration in water was increased by the granular ferric hydroxide. Nevertheless, granular ferric hydroxide is a promising adsorbent for chromium removal, even in the presence of other interfering compounds, because granular ferric hydroxide treatment can easily be accomplished and removal of excess iron is a simple practice for conventional water treatment plants. Thus, this method could be regarded as a safe and convenient solution to the problem of chromium-polluted water resources.

Method for determining the hardness of strain hardening articles of tungsten-nickel-iron alloy

International Nuclear Information System (INIS)

Wallace, S.A.

1984-01-01

The present invention is directed to a rapid nondestructive method for determining the extent of strain hardening in an article of tungsten-nickel-iron alloy. The method comprises saturating the article with a magnetic field from a permanent magnet, measuring the magnetic flux emanating from the article, comparing the measurements of the magnetic flux emanating from the article with measured magnetic fluxes from similarly shaped standards of the alloy with known amounts of strain hardening to determine the hardness

The secret behind the success of doping nickel oxyhydroxide with iron.

Science.gov (United States)

Fidelsky, Vicky; Toroker, Maytal Caspary

2017-03-15

Discovering better catalysts for water splitting is the holy grail of the renewable energy field. One of the most successful water oxidation catalysts is nickel oxyhydroxide (NiOOH), which is chemically active only as a result of doping with Fe. In order to shed light on how Fe improves efficiency, we perform Density Functional Theory +U (DFT+U) calculations of water oxidation reaction intermediates of Fe substitutional doped NiOOH. The results are analyzed while considering the presence of vacancies that we use as probes to test the effect of adding charge to the surface. We find that the smaller electronegativity of the Fe dopant relative to Ni allows the dopant to have several possible oxidation states with less energy penalty. As a result, the presence of vacancies which alters local oxidation states does not affect the low overpotential of Fe-doped NiOOH. We conclude that the secret to the success of doping NiOOH with iron is the ability of iron to easily change oxidation states, which is critical during the chemical reaction of water oxidation.

Determination of trace amounts of lead, arsenic, nickel and cobalt in high-purity iron oxide pigment by inductively coupled plasma atomic emission spectrometry after iron matrix removal with extractant-contained resin

International Nuclear Information System (INIS)

Xu Yuyu; Zhou Jianfeng; Wang Guoxin; Zhou Jinfan; Tao Guanhong

2007-01-01

Inductively coupled plasma atomic emission spectrometry (ICP-AES) was applied to the determination of lead, arsenic, nickel and cobalt in high-purity iron oxide pigment. Samples were dissolved with hydrochloric acid and hydrogen peroxide. The digest was passed through a column, which was packed with a polymer resin containing a neutral organophosphorus extractant, tri-n-butylphosphate. Iron was sorbed selectively on the resin and the analytes of interest passed through the column, allowing the effective separation of them from the iron matrix. Conditions of separation were optimized. The detection limits (3σ) in solution were 10, 40, 7 and 5 μg L -1 , and in pigment were 0.2, 0.8, 0.14 and 0.1 mg kg -1 for lead, arsenic, cobalt and nickel, respectively. The recoveries ranged from 95% to 107% when sample digests were spiked with 5 μg of the analytes of interest, and relative standard deviations (n = 6) were 1.5-17.6% for the determination of the spiked samples. The method was successfully applied to the determination of trace amounts of these elements in high-purity iron oxide pigment samples

Nickel base alloys

International Nuclear Information System (INIS)

Gibson, R.C.; Korenko, M.K.

1980-01-01

Nickel based alloy, the characteristic of which is that it mainly includes in percentages by weight: 57-63 Ni, 7-18 Cr, 10-20 Fe, 4-6 Mo, 1-2 Nb, 0.2-0.8 Si, 0.01-0.05 Zr, 1.0-2.5 Ti, 1.0-2.5 Al, 0.02-0.06 C and 0.002-0.015 B. The aim is to create new nickel-chromium alloys, hardened in a solid solution and by precipitation, that are stable, exhibit reduced swelling and resistant to plastic deformation inside the reactor. These alloys of the gamma prime type have improved mechanical strengthm swelling resistance, structural stability and welding properties compared with Inconel 625 [fr

Pelepasan ion nikel dan kromium kawat Australia dan stainless steel dalam saliva buatan (The release of nickel and chromium ions from Australian wire and stainless steel in artificial saliva

Directory of Open Access Journals (Sweden)

Nolista Indah Rasyid

2014-09-01

Full Text Available Background: Fixed orthodontic treatment needs several types of wire to produce biomechanical force to move teeth. The use orthodontic wire within the mouth interacts with saliva, causing the release of nickel and chromium ions. Purpose: The study was aimed to examine the effect of immersion time in artificial saliva between special type of Australian wire and stainless steel on the release of nickel and chromium ions. Methods: Thirty special type Australian wires and 30 stainless steel wires were used in this study, each of which weighed 0.12 grams. The wires were immersed for 1, 7, 28, 35, 42, and 49 days in artificial saliva with a normal pH. The release of ions in saliva was examined using Atomic Absorption spectrophotometry. Results: The result indicated that the release of nickel ions on special type of Australian wire was larger than that on stainless steel wire (p<0.005, there were differences in the release of the amount of nickel ions on special type of Australia in different immersion time, and there was a correlation between the types of wire and immersion time. Nickel ions released from the special type of Australian wire detected on the 7th day of immersion and reached its peak on the 35th day, while from stainless steel wire were detected on the 49th day of immersion. The released of chromium ions from the special type of Australian wire and stainless steel wire were not detected until the 49th day of immersion. Conclusion: The release of nickel ions were highest on the 35th day of immersion in special type of Australian wire and they were detected on the 49th day in stainless steel wire. The release of chromium ions were not detected until 49th day of immersion in special type of Australian and stainless steel wire.Latar belakang: Perawatan ortodonti cekat memerlukan beberapa macam kawat untuk menghasilkan kekuatan biomekanika yang sesuai dalam menggerakkan gigi. Pemakaian kawat ortodonti di dalam mulut dapat bereaksi dengan

Zero-valent iron particles embedded on the mesoporous silica–carbon for chromium (VI) removal from aqueous solution

Energy Technology Data Exchange (ETDEWEB)

Xiong, Kun, E-mail: kunxiong312@gmail.com; Gao, Yuan [Chongqing Technology and Business University, Engineering Research Center for Waste Oil Recovery Technology and Equipment of Ministry of Education, Chongqing Key Laboratory of Catalysis & Environmental New Materials (China); Zhou, Lin [Chengdu Radio and TV University (China); Zhang, Xianming [Chongqing Technology and Business University, Engineering Research Center for Waste Oil Recovery Technology and Equipment of Ministry of Education, Chongqing Key Laboratory of Catalysis & Environmental New Materials (China)

2016-09-15

Nanoscale zero-valent iron (nZVI) particles were embedded on the walls of mesoporous silica–carbon (MSC) under the conditions of high-temperature carbonization and reduction and used to remove chromium (VI) from aqueous solution. The structure and textural properties of nZVI–MSC were characterized by the powder X-ray diffraction, transmission electron microscopy and N{sub 2} adsorption and desorption. The results show that nZVI–MSC has highly ordered mesoporous structure and large surface area, indistinguishable with that of MSC. Compared with the support MSC and iron particles supported on the activated carbon (nZVI/AC), nZVI–MSC exhibited much higher Cr(VI) removal efficiency with about 98 %. The removal process obeys a pseudo first-order model. Such excellent performance of nZVI–MSC could be ascribed to the large surface and iron particles embedded on the walls of the MSC, forming an intimate contact with the MSC. It is proposed that this feature might create certain micro-electrode on the interface of iron particles and MSC, which prevented the formation of metal oxide on the surface and provided fresh Fe surface for Cr(VI) removal.

Delamination wear mechanism in gray cast irons

International Nuclear Information System (INIS)

Salehi, M.

2000-01-01

An investigation of the friction and sliding wear of gray cast iron against chromium plated cast irons was carried out on a newly constructed reciprocating friction and wear tester. The tests were the first to be done on the test rig under dry conditions and at the speed of 170 cm/min, and variable loads of 20-260 N for a duration of 15 min. to 3 hours. The gray cast iron surfaces worn by a process of plastic deformation at the subsurface, crack nucleation, and crack growth leading to formation of plate like debris and therefore the delamination theory applies. No evidence of adhesion was observed. This could be due to formation of oxides on the wear surface which prevent adhesion. channel type chromium plating ''picked'' up cast iron from the counter-body surfaces by mechanically trapping cast iron debris on and within the cracks. The removal of the plated chromium left a pitted surface on the cast iron

Stress corrosion cracking of Alloy 600 in primary water of PWR: study of chromium diffusion

International Nuclear Information System (INIS)

Chetroiu, Bogdan-Adrian

2015-01-01

Alloy 600 (Ni-15%Cr-10%Fe) is known to be susceptible to Stress Corrosion Cracking (SCC) in primary water of Pressurized Water Reactors (PWR). Recent studies have shown that chromium diffusion is a controlling rate step in the comprehension of SCC mechanism. In order to improve the understanding and the modelling of SCC of Alloy 600 in PWR primary medium the aim of this study was to collect data on kinetics diffusion of chromium. Volume and grain boundary diffusion of chromium in pure nickel and Alloy 600 (mono and poly-crystals) has been measured in the temperature range 678 K to 1060 K by using Secondary Ions Mass Spectroscopy (SIMS) and Glow Discharge-Optical Spectrometry (GD-OES) techniques. A particular emphasis has been dedicated to the influence of plastic deformation on chromium diffusion in nickel single crystals (orientated <101>) for different metallurgical states. The experimental tests were carried out in order to compare the chromium diffusion coefficients in free lattice (not deformed), in pre-hardening specimens (4% and 20%) and in dynamic deformed tensile specimens at 773 K. It has been found that chromium diffusivity measured in dynamic plastic deformed creep specimens were six orders of magnitude greater than those obtained in not deformed or pre-hardening specimens. The enhancement of chromium diffusivity can be attributed to the presence of moving dislocations generated during plastic deformation. (author)

Diffusion of alloying elements in liquid nickel

International Nuclear Information System (INIS)

Ershov, G.S.; Majboroda, V.P.; Permyakova, T.V.

1990-01-01

Values of diffusion coefficients for chromium, vanadium, zinc, silicon, tin, antimony, lead and zirconium in liquid nickel are determined within 1500-1700 deg C temperature range using annular gap technique. The data obtained are explained concerning microheterogeneous structure of metallic melts

Phase equilibria analysis in chromium-nickel steel

International Nuclear Information System (INIS)

Gurevich, Yu.G.; Frage, N.R.; Dudorova, T.A.

1982-01-01

Comparison of calculation results of nitrogen solubility in liquid multicomponent iron alloys containing essential concentrations of alloying transition metals is conducted. Nitrogen solubility has been calculated by the interaction parameters of the first order, by the interaction parameters of the first and second orders by the Schurmann-Kunze method; by the formula [% N]=[% N]sub(Fe)(Asub(Fe)/Asub(m)(1-1/6 μsub(j=3)sup(m)epsilonsub(N)sup(j)xsub(j))sup(6), where Asub(Fe) - mass of iron mol; Asub(m) - mass of alloy mol; xsub(j) - mol ratio of j-element; epsilonsub(N)sup(j) - Wagner parameter of interaction for nitrogen in iron base alloys. The calculation data have been compared with the experimental values of nitrogen solubility in iron alloys at 1600 deg C. Advantages of calculation by the formula in respect to other calculation methods of nitrogen solubility in iron base alloys are clarified. Approximately pointed out is the region of compositions for which accountancy of interaction parameters of the second and third orders is necessary

Research, development, and demonstration of nickel-iron batteries for electric vehicle propulsion. Annual report, 1979

Energy Technology Data Exchange (ETDEWEB)

1980-06-01

The program has progressed to the stage of evaluating full-sized (220 Ah) cells, multicell modules, and 22 kWh batteries. Nickel electrodes that display stable capacities of up to 24 Ah/plate (at C/3 drain rate) at design thickness (2.5 mm) in tests at 200/sup +/ test cycles. Iron electrodes of the composite-type are also delivering 24 Ah/plate (at C/3) at target thickness (1.0 mm). Iron plates are displaying capacity stability for 300/sup +/ test cycles in continuing 3 plate cell tests. Best finished cells are delivering 57 to 63 Wh/kg at C/3, based on cell weights of the finished cells, and in the actual designed cell volume. 6-cell module (6-1) performance has demonstrated 239 Ah, 1735 Wh, 53 WH/kg at the C/3 drain rate. This module is now being evaluated at the National Battery Test Laboratory. The 2 x 4 battery has been constructed, tested, and delivered for engineering test and evaluation. The battery delivered 22.5 kWh, as required (199 Ah discharge at 113 V-bar) at the C/3 drain rate. The battery has performed satisfactorily under dynamometer and constant current drain tests. Some cell problems, related to construction, necessitated changing 3 modules, but the battery is now ready for further testing. Reduction in nickel plate swelling (and concurrent stack electrolyte starvation), to improve cycling, is one area of major effort to reach the final battery objectives. Pasted nickel electrodes are showing promise in initial full-size cell tests and will continue to be evaluated in finished cells, along with other technology advancements. 30 figures, 14 tables.

Preparation of nickel-coated titanium carbide particulates and their use in the production of reinforced iron matrix composites

International Nuclear Information System (INIS)

Yi, Danqing; Yu, Pengchao; Hu, Bin; Liu, Huiqun; Wang, Bin; Jiang, Yong

2013-01-01

Highlights: • Ni-coated TiC composite powders were prepared by electroless plating. • Iron-based composites reinforced by TiC particles was prepared by HIP. • Mechanical and wear properties were improved with the addition of Ni-coated TiC. • The nickel coating promotes the formation and growth of sintering neck. - Abstract: Ni-coated titanium carbide (TiC) composite powders were prepared by electroless plating (EP). Further, using hot isostatic pressing (HIP), iron matrix composites reinforced with 4 wt% Ni-coated TiC particulates with relative density close to 100% were prepared. The microstructure and phase composition of the Ni-coated powders and the composites were analyzed using X-ray diffraction, scanning electron microscopy, and energy dispersive X-ray spectroscopy. The results showed that the TiC particles were distributed uniformly in the matrix and were free of segregation or coarsening. Compared to the TiC particles without Ni coating, the reinforced iron-based composites containing the Ni-coated particles showed higher relative densities and better mechanical properties. The density, hardness, tensile strength, and elongation were enhanced to 99.98%, 243 HV, 565 MPa, and 11.7%, respectively in composites containing Ni-coated TiC particles from 99.70%, 210 HV, 514 MPa, and 10.3%, respectively in composites that were prepared using particles without Ni coating. In addition, the mass losses in the composites containing the Ni-coated particles were reduced by 32–75% in the abrasive wear test with various vertical loads. We propose that the nickel coatings on the particulates had a beneficial effect on the microstructure and properties of the reinforced iron-based composites is due to promotion of neck formation and growth between TiC and iron powders during sintering, which enhanced the density of the sintered compact and the bonding strength between the TiC particles and the iron matrix

Effect of cold working on the stress corrosion cracking resistance of nickel-chromium-iron alloys

International Nuclear Information System (INIS)

Yonezawa, T.; Onimura, K.

1987-01-01

In order to grasp the stress corrosion cracking resistance of cold worked nickel base alloys in PWR primary water, the effect of cold working on the stress corrosion cracking resistance of alloys 600, X-750 and 690, in high temperature water, have been studied. Stress corrosion cracking tests were conducted at 360 0 C (633K) in a simulated PWR primary water for about 12,000 hours (43.2Ms). From the test results, it is concluded that the stress corrosion cracking resistance in the cold worked Alloy 600 at the same applied stress level increases with an increase in cold working ratio, and the cold worked alloys of thermally treated 690 and X-750 have excellent stress corrosion cracking resistance. (Author)

Microstructure and wear resistance of high chromium cast iron containing niobium

Directory of Open Access Journals (Sweden)

Zhang Zhiguo

2014-05-01

Full Text Available In the paper, the effect of niobium addition on the microstructure, mechanical properties and wear resistance of high chromium cast iron has been studied. The results show that the microstructure of the heat-treated alloys is composed of M7C3 and M23C6 types primary carbide, eutectic carbide, secondary carbide and a matrix of martensite and retained austenite. NbC particles appear both inside and on the edge of the primary carbides. The hardness of the studied alloys maintains around 66 HRC, not significantly affected by the Nb content within the selected range of 0.48%-0.74%. The impact toughness of the alloys increases with increasing niobium content. The wear resistance of the specimens presents little variation in spite of the increase of Nb content under a light load of 40 N. However, when heavier loads of 70 and 100 N are applied, the wear resistance increases with increasing Nb content.

Snapshot of cobalt, chromium and nickel exposure in dental technicians.

Science.gov (United States)

Kettelarij, Jolinde; Nilsson, Sara; Midander, Klara; Lidén, Carola; Julander, Anneli

2016-12-01

It is not fully understood where and how people are exposed to sensitizing metals. Much can be learnt from studying occupational settings where metals are handled. To quantify cobalt (Co), chromium (Cr) and nickel (Ni) exposure on the skin and in the air, and urine levels, in dental technicians working with tools and alloys that may result in skin and respiratory exposure. The metal skin dose was quantified with acid wipe sampling in dental technicians (n = 13). Air exposure was monitored by personal air sampling. Spot urine samples were collected for 24 h. Metals were analysed with inductively coupled plasma mass spectrometry. Before work, Co was detected on the skin of 10 participants (0.00025-0.0039 µg/cm 2 ), and Cr (0.00051-0.011 µg/cm 2 ) and Ni (0.0062-0.15 µg/cm 2 ) on the skin of all participants. After a 2-h period without hand washing, CoCr-exposed participants had more Co on the skin (p = 0.004) than non-CoCr-exposed participants. Co was found in 10 air samples (0.22-155 µg/m 3 ), Cr in nine (0.43-71 µg/m 3 ), and Ni in four (0.48-3.7 µg/m 3 ). Metal urine concentrations were considered to be normal. Dental technicians were exposed to Co, Cr and Ni on the skin and through the air, which was not reflected in the urine concentrations in this study. Cobalt skin doses may potentially elicit allergic contact dermatitis and cause sensitization. © 2016 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

Corrosion of nickel and stainless steels in concentrated lithium hydroxide solutions

International Nuclear Information System (INIS)

Graydon, J.W.; Kirk, D.W.

1990-06-01

The corrosion behaviour of four alloys in 3 and 5 mol/L lithium hydroxide solutions under a hydrogen atmosphere at 95 degrees C was investigated. Corrosion of Nickel 200 and the stainless steels 316, 316L, and E-Brite 26-1 was assessed in two sets of immersion tests lasting 10 and 136 days. Corrosion rates were determined by weight loss, susceptibility to stress corrosion cracking was evaluated using U-bends, and the details of the corrosion process were studied on specimens with a mirror finish using light and electron microscopy, x-ray spectrometry and mapping, and x-ray diffraction. The long term corrosion rates were low for all alloys ( 2 , β-LiFeO 2 , and a very iron-rich β-LiFe 5 0 8 . The passivating layer on the nickel was Ni(OH) 2 . The underlying metal corroded evenly except for the 316 stainless steels. These showed a uniform intergranular corrosion with minor drop-out of smaller grains likely because of segregation of impurities to the grain boundaries. The walls of these intergranular crevices were covered with a passivating layer of chromium oxide. (8 figs., 5 tabs., 11 refs.)

Research, development, and demonstration of nickel-iron batteries for electric vehicle propulsion. Annual report, 1978

Energy Technology Data Exchange (ETDEWEB)

1979-10-01

The objective of this program is to develop a nickel-iron battery suitable for use in electric vehicles. Ultimately, it is expected that a number of these batteries will be demonstrated under the Electric and Hybrid Vehicle Act of 1976. The report presents the technical approach and a summary of the progress that was achieved under the contract. Work began 1 May 1978. The report covers the period through September 1978. (TFD)

Stabilization and solidification of chromium-contaminated soil

Energy Technology Data Exchange (ETDEWEB)

Cherne, C.A.; Thomson, B.M. [Univ. of New Mexico, Albuquerque, NM (United States). Civil Engineering Dept.; Conway, R. [Sandia National Labs., Albuquerque, NM (United States)

1997-11-01

Chromium-contaminated soil is a common environmental problem in the United States as a result of numerous industrial processes involving chromium. Hexavalent chromium [Cr(VI)] is the species of most concern because of its toxicity and mobility in groundwater. One method of diminishing the environmental impact of chromium is to reduce it to a trivalent oxidation state [Cr(III)], in which it is relatively insoluble and nontoxic. This study investigated a stabilization and solidification process to minimize the chromium concentration in the Toxicity Characteristic Leaching Procedure (TCLP) extract and to produce a solidified waste form with a compressive strength in the range of 150 to 300 pounds per square inch (psi). To minimize the chromium in the TCLP extract, the chromium had to be reduced to the trivalent oxidation state. The average used in this study was an alluvium contaminated with chromic and sulfuric acid solutions. The chromium concentration in the in the in situ soil was 1212 milligrams per kilogram (mg/kg) total chromium and 275 mg/kg Cr(VI). The effectiveness of iron, ferrous sulfate to reduce Cr(VI) was tested in batch experiments.

Stabilization and solidification of chromium-contaminated soil

International Nuclear Information System (INIS)

Cherne, C.A.; Thomson, B.M.

1997-11-01

Chromium-contaminated soil is a common environmental problem in the United States as a result of numerous industrial processes involving chromium. Hexavalent chromium [Cr(VI)] is the species of most concern because of its toxicity and mobility in groundwater. One method of diminishing the environmental impact of chromium is to reduce it to a trivalent oxidation state [Cr(III)], in which it is relatively insoluble and nontoxic. This study investigated a stabilization and solidification process to minimize the chromium concentration in the Toxicity Characteristic Leaching Procedure (TCLP) extract and to produce a solidified waste form with a compressive strength in the range of 150 to 300 pounds per square inch (psi). To minimize the chromium in the TCLP extract, the chromium had to be reduced to the trivalent oxidation state. The average used in this study was an alluvium contaminated with chromic and sulfuric acid solutions. The chromium concentration in the in the in situ soil was 1212 milligrams per kilogram (mg/kg) total chromium and 275 mg/kg Cr(VI). The effectiveness of iron, ferrous sulfate to reduce Cr(VI) was tested in batch experiments

Impurities determination of uranium metal flame spectrophotometry and atomic absorption spectrophotometry

International Nuclear Information System (INIS)

Rukihati.

1978-01-01

The atomic absorption flame spectrophotometry has been applied to the determination of chromium, copper, iron, lead, manganese and nickel in the metal of uranium. The first step to be done is to dissolve the uranium sample in nitric acid and then the uranium is extracted by a tributylphosphate-carbon tetrachloride solution. The aqueous phase which contains the chromium, copper, iron, lead, manganese and nickel is aspirated into an airacetylene flame. The results of this method are compared with the results of emission spectrographic method. It is found that this technique is competative to other methods in the sense that it is quite fast and accurate. (author)

Chromium, Nickel and Zinc Levels from Canned and Non-Canned ...

African Journals Online (AJOL)

DR. AMINU

2013-06-01

Jun 1, 2013 ... Water soluble nickel salts do not readily enter cell. Therefore, these compounds are generally not carcinogenic in animals and, to a large extent, have not been considered potent human carcinogens, although recent studies have suggested an increase in cancer in nickel refinery areas where exposure to ...

Amendment of arsenic and chromium polluted soil from wood preservation by iron residues from water treatment

DEFF Research Database (Denmark)

Nielsen, Sanne Skov; Petersen, L. R.; Kjeldsen, Peter

2011-01-01

An iron-rich water treatment residue (WTR) consisting mainly of ferrihydrite was used for immobilization of arsenic and chromium in a soil contaminated by wood preservatives. A leaching batch experiment was conducted using two soils, a highly contaminated soil (1033mgkg−1 As and 371mgkg−1 Cr....... Pore water was extracted during 3years from the amended soil and a control site. Pore water arsenic concentrations in the amended soil were more than two orders of magnitude lower than in the control for the upper samplers. An increased release of arsenic was observed during winter in both fields...

Bioavailability of nickel in man: effects of foods and chemically-defined dietary constituents on the absorption of inorganic nickel.

Science.gov (United States)

Solomons, N W; Viteri, F; Shuler, T R; Nielsen, F H

1982-01-01

By serial determination of the change in plasma nickel concentration following a standard dose of 22.4 mg of nickel sulfate hexahydrate containing 5 mg of elemental nickel, the bioavailability of nickel was estimated in human subjects. Plasma nickel concentration was stable in the fasting state and after an unlabeled test meal, but after the standard dose of nickel in water was elevated 48.8, 73.0, 80.0, and 53.3 microgram/1, respectively, at hours 1, 2, 3, and 4. Plasma nickel did not rise above fasting levels when 5 mg of nickel was added to two standard meals: a typical Guatemalan meal and a North American breakfast. When 5 mg of nickel was added to five beverages-whole cow milk, coffee, tea, orange juice, and Coca Cola-the rise in plasma nickel was significantly suppressed with all but Coca Cola. Response to nickel also was suppressed in the presence of 1 g of ascorbic acid. Phytic acid in a 2:1 molar ratio with nickel, however, did not affect the rise in plasma nickel. The chelate of iron and ethylenediaminetetraacetate, NaFeEDTA, an iron-fortifying agent suggested for application in Central America, slightly but not significantly depressed plasma nickel rise at 2 hours, whereas disodium EDTA depressed plasma nickel levels significantly below the fasting nickel curve at 3 and 4 hours postdose. These studies suggest that the differential responses of inorganic nickel to distinct foods, beverages, and chemically-defined dietary constituents could be important to human nutrition.

Hot corrosion studies on nickel-based alloys containing silicon

International Nuclear Information System (INIS)

Kerr, T.W.; Simkovich, G.

1976-01-01

Alloys of Ni--Cr, Ni--Si and Ni--Cr--Si were oxidized and ''hot corroded'' in pure oxygen at 1000 0 C. In the oxidation experiments it was found that small amounts of either chromium or silicon in nickel increased the oxidation rates in comparison to pure nickel in accord with Wagner's parabolic oxidation theory. At high concentrations of the alloying elements the oxidation rates decreased due to the formation of oxide phases other than nickel oxide in the scale. Hot corrosion experiments were conducted on both binary and ternary alloys by oxidizing samples coated with 1.0 mg/cm 2 of Na 2 SO 4 in oxygen at 1000 0 C. In general it was found that high chromium and high silicon alloys displayed excellent resistance to the hot corrosion process gaining or losing less than 0.5 mg/cm 2 in 1800 min at temperature. Microprobe and x-ray diffraction studies of the alloy and the scale indicate that amorphous SiO 2 probably formed to aid in retarding both the oxidation and the hot corrosion process

Straining electrode behavior and corrosion resistance of nickel base alloys in high temperature acidic solution

International Nuclear Information System (INIS)

Yamanaka, Kazuo

1992-01-01

Repassivation behavior and IGA resistance of nickel base alloys containing 0∼30 wt% chromium was investigated in high temperature acid sulfate solution. (1) The repassivation rate was increased with increasing chromium content. And so the amounts of charge caused by the metal dissolution were decreased with increasing chromium content. (2) Mill-annealed Alloy 600 suffered IGA at low pH environment below about 3.5 at the fixed potentials above the corrosion potential in 10%Na 2 SO 4 +H 2 SO 4 solution at 598K. On the other hand, thermally-treated Alloy 690 was hard to occur IGA at low pH environments which mill-annealed Alloy 600 occurred IGA. (3) It was considered that the reason, why nickel base alloys containing high chromium content such as Alloy 690 (60%Ni-30%Cr-10%Fe) had high IGA/SCC resistance in high temperature acidic solution containing sulfate ion, is due to both the promotion of the repassivation and the suppression of the film dissolution by the formation of the dense chromium oxide film

Jewellery

DEFF Research Database (Denmark)

Hamann, Dathan; Thyssen, Jacob P; Hamann, Carsten R

2015-01-01

and lead release by the use of artificial sweat immersion and plasma optical emission spectroscopy. RESULTS: Eighteen elements were detected. The 10 most frequently occurring were, in order of frequency, copper, iron, zinc, nickel, silver, chromium, tin, manganese, lead, and cobalt. Release of nickel...

Dermatite de contato por metais: prevalência de sensibilização ao níquel, cobalto e cromo Metal contact dermatitis: prevalence of sensitization to nickel, cobalt and chromium

Directory of Open Access Journals (Sweden)

Ida Duarte

2005-04-01

Full Text Available FUNDAMENTOS: Dermatite de contato (DC por metais é dermatose comum em diversos grupos populacionais. OBJETIVOS: Caracterizar o grupo com DC ao níquel, cromo e cobalto na população estudada, determinar a prevalência da sensibilização aos mesmos, verificar as combinações de testes positivos e comparar com a literatura. CASUÍSTICAS E MÉTODOS: Foram realizados testes epicutâneos em 1.208 pacientes com hipótese diagnóstica de DC. Selecionaram-se aqueles com testes positivos aos metais. RESULTADOS: Obtiveram-se 404 pacientes (33,5% da amostra com pelo menos um teste positivo ao níquel e/ou cobalto e/ou cromo. Foram 487 testes positivos a metais, correspondendo a 48% de todos os testes positivos. A maioria dos pacientes era do sexo feminino (72%, de cor branca (54%, com idade entre 40 e 49 anos (25% empregada na área de limpeza (59%. Dos 404, 329 (81,5% foram positivos a apenas um tipo de metal, sendo 60% com teste positivo ao níquel, 13% ao cromo e 8,5% ao cobalto. Cerca de 18,5% apresentaram testes positivos a dois ou três metais, sendo a associação níquel/cobalto a mais comum. CONCLUSÕES: A sensibilização aos metais foi de 48%, entre os testes positivos e ocorreu principalmente em mulheres da cor branca, na faixa etária de 40 a 49 anos e sem correlação ocupacional. A maioria apresentou sensibilização a apenas um metal. Esses dados são semelhantes aos de outros trabalhos já publicados.BACKGROUND: Metal contact dermatitis (nickel, cobalt and chromium is a common dermatosis among several population groups. OBJECTIVE: To describe the individuals with metal contact dermatitis in the group studied, to determine the prevalence of skin sensitization by nickel, cobalt and chromium, to verify the positive test combinations among these three substances and to compare our results with the literature. PATIENTS AND METHODS: Patch test was performed in 1208 patients with a presumptive diagnosis of contact dermatitis. Those with

Use of radionuclides in the study of iron metabolism in iron deficient states

International Nuclear Information System (INIS)

Anatkov, A.; Karakostov, K.; Iliev, Z.; Dimitrov, L.

1977-01-01

A study of erythropoiesis in iron deficient anemias by simultaneous labelling with the radionuclides iron 59 and chromium 51 revealed accelerated iron circuit, higher percentage of daily hemolysis, severely reduced or even absent labile reserves, decreased volume of packed red cells with no decrease of blood volume. Adequate iron 59 utilization was observed after administration of large doses of iron (500 mg) in the treatment of iron deficient anemias. (author)

Nitrogen solubility in nickel base multicomponent melts

International Nuclear Information System (INIS)

Bol'shov, L.A.; Stomakhin, A.Ya.; Sokolov, V.M.; Teterin, V.G.

1984-01-01

Applicability of various methods for calculation of nitrogen solubility in high-alloyed nickel base alloys, containing Cr, Fe, W, Mo, Ti, Nb, has been estimated. A possibility is shown to use the formUla, derived for the calculation of nitrogen solubility in iron on the basis of statistical theory for a grid model of solution which does not require limitations for the content of a solvent component. The calculation method has been used for nickel alloys, with the concentration of solvent, iron, being accepted equal to zero, and employing parameters of nitrogen interaction as determined for iron-base alloys

Determination of Pb (Lead, Cd (Cadmium, Cr (Chromium, Cu (Copper, and Ni (Nickel in Chinese tea with high-resolution continuum source graphite furnace atomic absorption spectrometry

Directory of Open Access Journals (Sweden)

Wen-Si Zhong

2016-01-01

Full Text Available The contents of lead, cadmium, chromium, copper, and nickel were determined in 25 tea samples from China, including green, yellow, white, oolong, black, Pu'er, and jasmine tea products, using high-resolution continuum source graphite furnace atomic absorption spectrometry. The methods used for sample preparation, digestion, and quantificational analysis were established, generating satisfactory analytical precisions (represented by relative standard deviations ranging from 0.6% to 2.5% and recoveries (98.91–101.32%. The lead contents in tea leaves were 0.48–10.57 mg/kg, and 80% of these values were below the maximum values stated by the guidelines in China. The contents of cadmium and chromium ranged from 0.01 mg/kg to 0.39 mg/kg and from 0.27 mg/kg to 2.45 mg/kg, respectively, remaining in compliance with the limits stipulated by China's Ministry of Agriculture. The copper contents were 7.73–63.71 mg/kg; only 64% of these values complied with the standards stipulated by the Ministry of Agriculture. The nickel contents ranged from 2.70 mg/kg to 13.41 mg/kg. Consequently, more attention must be paid to the risks of heavy metal contamination in tea. The quantitative method established in this work lays a foundation for preventing heavy metal toxicity in human from drinking tea and will help establish regulations to control the contents of heavy metals in tea.

A study on the corrosion and erosion behavior of electroless nickel and TiAlN/ZrN duplex coatings on ductile iron

Energy Technology Data Exchange (ETDEWEB)

Lin, Chung-Kwei [School of Dental Technology, Taipei Medical University, Taipei 110, Taiwan (China); Hsu, Cheng-Hsun, E-mail: chhsu@ttu.edu.tw [Department of Materials Engineering, Tatung University, Taipei 104, Taiwan (China); College of Oral Medicine, Taipei Medical University, Taipei 110, Taiwan (China); Cheng, Yin-Hwa [Department of Materials Engineering, Tatung University, Taipei 104, Taiwan (China); Ou, Keng-Liang [College of Oral Medicine, Taipei Medical University, Taipei 110, Taiwan (China); Department of Mechanical Engineering, National Central University, Taoyuan 320, Taiwan (China); Lee, Sheng-Long [Research Center for Biomedical Devices and Prototyping Production, Taipei Medical University, Taipei 110, Taiwan (China)

2015-01-01

Highlights: • Electroless nickel was used as an interlayer for TiAlZrN-coated ductile iron. • The duplex coatings evidently improved corrosion resistance of ductile iron. • The duplex coated ductile iron showed a good erosion resistance. - Abstract: This study utilized electroless nickel (EN) and cathodic arc evaporation (CAE) technologies to deposit protective coatings onto ductile iron. Polarization corrosion tests were performed in 3.5 wt.% sodium chloride, and also erosion tests were carried out by using Al{sub 2}O{sub 3} particles (∼177 μm in size and Mohr 7 scale) of about 5 g. Surface morphologies of the corroded and eroded specimens were observed separately. To further understand the coating effects on both the corrosive and erosive behavior of ductile iron, coating structure, morphology, and adhesion were analyzed using X-ray diffractormeter, scanning electron microscopy, and Rockwell-C indenter, respectively. The results showed that the EN exhibited an amorphous structure while the CAE-TiAlN/ZrN coating was a multilayered nanocrystalline. When the TiAlN/ZrN coated specimen with EN interlayer could effectively increase the adhesion strength between the CAE coating and substrate. Consequently, the combination of TiAlN/ZrN and EN delivered a better performance than did the monolithic EN or TiAlN/ZrN for both corrosion and erosion protection.

A study on the corrosion and erosion behavior of electroless nickel and TiAlN/ZrN duplex coatings on ductile iron

International Nuclear Information System (INIS)

Lin, Chung-Kwei; Hsu, Cheng-Hsun; Cheng, Yin-Hwa; Ou, Keng-Liang; Lee, Sheng-Long

2015-01-01

Highlights: • Electroless nickel was used as an interlayer for TiAlZrN-coated ductile iron. • The duplex coatings evidently improved corrosion resistance of ductile iron. • The duplex coated ductile iron showed a good erosion resistance. - Abstract: This study utilized electroless nickel (EN) and cathodic arc evaporation (CAE) technologies to deposit protective coatings onto ductile iron. Polarization corrosion tests were performed in 3.5 wt.% sodium chloride, and also erosion tests were carried out by using Al 2 O 3 particles (∼177 μm in size and Mohr 7 scale) of about 5 g. Surface morphologies of the corroded and eroded specimens were observed separately. To further understand the coating effects on both the corrosive and erosive behavior of ductile iron, coating structure, morphology, and adhesion were analyzed using X-ray diffractormeter, scanning electron microscopy, and Rockwell-C indenter, respectively. The results showed that the EN exhibited an amorphous structure while the CAE-TiAlN/ZrN coating was a multilayered nanocrystalline. When the TiAlN/ZrN coated specimen with EN interlayer could effectively increase the adhesion strength between the CAE coating and substrate. Consequently, the combination of TiAlN/ZrN and EN delivered a better performance than did the monolithic EN or TiAlN/ZrN for both corrosion and erosion protection

The release of nickel and other trace elements from electric kettles and coffee machines

DEFF Research Database (Denmark)

Berg, T.; Petersen, Annette; Pedersen, Gitte Alsing

2000-01-01

was improved. Two of these ten kettles still released more than 50 mu g/l nickel to water under the test conditions. These two kettles, however, were subsequently withdrawn from the market. Coffee machines tested similarly did not release aluminium, lead, chromium or nickel in quantities of any significance....

Design of a rotary reactor for chemical-looping combustion. Part 2: Comparison of copper-, nickel-, and iron-based oxygen carriers

KAUST Repository

Zhao, Zhenlong

2014-04-01

Chemical-looping combustion (CLC) is a novel and promising option for several applications including carbon capture (CC), fuel reforming, H 2 generation, etc. Previous studies demonstrated the feasibility of performing CLC in a novel rotary design with micro-channel structures. Part 1 of this series studied the fundamentals of the reactor design and proposed a comprehensive design procedure, enabling a systematic methodology of designing and evaluating the rotary CLC reactor with different OCs and operating conditions. This paper presents the application of the methodology to the designs with three commonly used OCs, i.e., copper, nickel, and iron. The physical properties and the reactivities of the three OCs are compared at operating conditions suitable for the rotary CLC. Nickel has the highest reduction rate, but relatively slow oxidation reactivity while the iron reduction rate is most sensitive to the fuel concentration. The design parameters and the operating conditions for the three OCs are selected, following the strategies proposed in Part 1, and the performances are evaluated using a one-dimensional plug-flow model developed previously. The simulations show that for all OCs, complete fuel conversion and high carbon separation efficiency can be achieved at periodic stationary state with reasonable operational stabilities. The nickel-based design includes the smallest dimensions because of its fast reduction rate. The operation of nickel case is mainly limited to the slow oxidation rate, and hence a relatively large share of air sector is used. The iron-based design has the largest size, due to its slow reduction reactivity near the exit or in the fuel purge sector where the fuel concentration is low. The gas flow temperature increases monotonically for all the cases, and is mainly determined by the solid temperature. In the periodic state, the local temperature variation is within 40 K and the thermal distortion is limited. The design of the rotary CLC is

Embrittlement of nickel-, cobalt-, and iron-base superalloys by exposure to hydrogen

Science.gov (United States)

Gray, H. R.

1975-01-01

Five nickel-base alloys (Inconel 718, Udimet 700, Rene 41, Hastelloy X, and TD-NiCr), one cobalt-base alloy (L-605), and an iron-base alloy (A-286) were exposed in hydrogen at 0.1 MN/sq m (15 psi) at several temperatures in the range from 430 to 980 C for as long as 1000 hours. These alloys were embrittled to varying degrees by such exposures in hydrogen. Embrittlement was found to be: (1) sensitive to strain rate, (2) reversible, (3) caused by large concentrations of absorbed hydrogen, and (4) not associated with any detectable microstructural changes in the alloys. These observations are consistent with a mechanism of internal reversible hydrogen embrittlement.

Gum karaya (Sterculia urens) stabilized zero-valent iron nanoparticles: characterization and applications for the removal of chromium and volatile organic pollutants from water

Czech Academy of Sciences Publication Activity Database

Vinod, V.T.P.; Waclawek, S.; Senan, Ch.; Kupčík, Jaroslav; Pešková, K.; Černík, M.; Somashekarappa, H. M.

2017-01-01

Roč. 7, č. 23 (2017), s. 13997-14009 ISSN 2046-2069 R&D Projects: GA MŠk(CZ) LM2015073 Institutional support: RVO:61388980 Keywords : nanoscale zerovalent iron * ray photoelectron-spectroscopy * groundwater remediation * hexavalent chromium * xanthan gum * guar gum * waste-water Subject RIV: CA - Inorganic Chemistry OBOR OECD: Inorganic and nuclear chemistry Impact factor: 3.108, year: 2016

Microwave acid-digestion method for determination of nickel, pro-oxidants and other heavy metals in different brands of banaspati ghee

International Nuclear Information System (INIS)

Latif, A.; Khan, F.; Noor, S.; Amin-ur-Rehman

2009-01-01

Samples of different brands of banaspati ghee (Hydrogenated vegetable oil) were procured from local market in Peshawar. Nickel, Pro-oxidants and other heavy metals in these samples were determined by microwave acid digestion method and were analyzed by atomic absorption spectrometry to evaluate the value of different brands of banaspati ghee found in the local Peshawar market. Microwave acid digestion program was developed to give reliable estimates for metals in small sample (0.5g) of banaspati ghee. It reduced the external contamination and required small quantities of acid, improving the detection-limits and overall accuracy of the analytical method. Iron and copper concentrations were found in ranges of (0.44-4.64 ppm), (0.072 - 0.38 ppm), respectively. Nickel ranged (0.098 - 0.24 ppm), while the concentrations of chromium, cadmium, lead, manganese and zinc ranged (0. 035 - 0. 15ppm), (0.022 - 0. 16ppm), (0.025 - 0.095ppm), (0.029 - 0.12 ppm) and (0.019 - 0.13 ppm), respectively.(author)

Estimation of changes in nickel and chromium content in nickel-titanium and stainless steel orthodontic wires used during orthodontic treatment: An analytical and scanning electron microscopic study

Directory of Open Access Journals (Sweden)

Vandana Kararia

2015-01-01

Full Text Available Introduction: The biocompatibility of orthodontic dental alloys has been investigated over the past 20 years, but the results have been inconclusive. The study compares standard 3 M Unitek nickel-titanium (NiTi and stainless steel archwires with locally available JJ orthodontics wires. Scanning electron microscope (SEM study of surface changes and complexometric titration to study compositional change was performed. Materials and Methods: Ten archwires each of group 1-3 M 0.016" NiTi, group 2-JJ 0.016" NiTi, group 3-3 M 0.019" FNx010.025" SS and group 4-JJ SS contributed a 10 mm piece of wire for analysis prior to insertion in the patient and 6 weeks post insertion. SEM images were recorded at Χ2000, Χ4000 and Χ6000 magnification. The same samples were subjected to complexiometric titration using ethylenediaminetetraacetic acid to gauge the actual change in the composition. Observations and Results: The SEM images of all the archwires showed marked changes with deep scratches and grooves and dark pitting corrosion areas post intraoral use. 3M wires showed an uniform criss-cross pattern in as received wires indicating a coating which was absent after intraoral use. There was a significant release of Nickel and Chromium from both group 3 and 4. Group 2 wires released ions significantly more than group 1 (P = 0.0. Conclusion: Extensive and stringent trials are required before certifying any product to be used in Orthodontics.

Comparative Studies of the Speciation Patterns of Nickel and ...

African Journals Online (AJOL)

Results of speciation stdies of nickel and chromium in wastewater, surface and groundwater systems using flame atomic absorption spectrometry (FAAS), graphite furnace atomic absorption spectrometry (GFAAS) and differential pulse adsorptive cathodic stripping voltammetry (DPAdCSV) are presented. Dimethylglyoxime ...

Selected Test Results from the Encell Technology Nickel Iron Battery

Energy Technology Data Exchange (ETDEWEB)

Ferreira, Summer Kamal Rhodes [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States). Advanced Power Sources R& D; Baca, Wes Edmund [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States). Advanced Power Sources R& D; Avedikian, Kristan [Encell Technology, Alachua, FL (United States)

2014-09-01

The performance of the Encell Nickel Iron (NiFe) battery was measured. Tests included capacity, capacity as a function of rate, capacity as a function of temperature, charge retention (28-day), efficiency, accelerated life projection, and water refill evaluation. The goal of this work was to evaluate the general performance of the Encell NiFe battery technology for stationary applications and demonstrate the chemistry's capabilities in extreme conditions. Test results have indicated that the Encell NiFe battery technology can provide power levels up to the 6C discharge rate, ampere-hour efficiency above 70%. In summary, the Encell batteries have met performance metrics established by the manufacturer. Long-term cycle tests are not included in this report. A cycle test at elevated temperature was run, funded by the manufacturer, which Encell uses to predict long-term cycling performance, and which passed their prescribed metrics.

Relationship between equivalent chromium content and irradiation-induced swelling in 316 stainless steel

International Nuclear Information System (INIS)

Bates, J.F.; Guthrie, G.L.

1974-12-01

A correlation is noted between equivalent chromium content and resistance to irradiation induced swelling in various 316 stainless steel specimens which have slightly different chemical compositions. Several examples are cited where an increased concentration of an α-stabilizing minor constituent results in decreased swelling. It is shown that the relative swelling resistance of alloys having the same carbon and equivalent nickel contents is higher for those alloys with the higher equivalent chromium content

Ductile tungsten-nickel-alloy and method for manufacturing same

Science.gov (United States)

Ludwig, Robert L.

1978-01-01

The tensile elongation of a tungsten-nickel-iron alloy containing essentially 95 weight percent reprocessed tungsten, 3.5 weight percent nickel, and 1.5 weight percent iron is increased from a value of less than about 1 percent up to about 23 percent by the addition of less than 0.5 weight percent of a reactive metal consisting of niobium and zirconium.

48 CFR 252.225-7009 - Restriction on Acquisition of Certain Articles Containing Specialty Metals.

Science.gov (United States)

2010-10-01

... metal (by mass). (ii) If two metals are specified in the name (e.g., nickel-iron alloy), those metals..., billet, wire, slab, plate, or sheet, and in the grade appropriate for the production of— (i) A finished... of the following elements: Aluminum, chromium, cobalt, molybdenum, nickel, niobium (columbium...

Self-powered neutron flux detector assembly

International Nuclear Information System (INIS)

Allan, C.J.; McIntyre, I.L.

1980-01-01

A self-powered neutron flux detector has both the central emitter electrode and its surrounding collector electrode made of inconel 600. The lead cables may also be made of inconel. Other nickel alloys, or iron, nickel, titamium, chromium, zirconium or their alloys may also be used for the electrodes

Determination of concentration factors for Chromium cesium, iron and cobalt in corvine and shrimp in the vicinities of Almirante Alvaro Alberto Nuclear Power Plant

International Nuclear Information System (INIS)

Kamel, L.N.

1988-01-01

In order to verify if the concentration factors for dose calculations in critical population recommended by the International Atomic Energy (IAEA), on the Safety Series 57, are in agreement with local factors, studies were carried out at Piraquara de Dentro bay, a region in the vicinities of the Almirante Alvaro Alberto Nuclear Power Plant (CNAAA). Chromium, caesium, iron and cobalt concentration factors for corvine and shrimp were determined using the activation analysis method by neutrons, taking into account the same behaviour between radioactive and stable from the same physicochemical form. This study has evidenced that: The local values of cesium, iron and cobalt concentration factors for corvine (fish) are in the same order of magnitude of the IAEA recommended values; The chromium, caesium and cobalt concentration factor values determined for shrimp for Piraquara de Dentro bay are in the same order of magnitude or smaller than those proposed by IAEA, while the concentration factor value for ion is one order of magnitude higher than the IAEA recommended value. (author) [pt

Extraction of nickel from Ramu laterite by sulphation roasting-water leaching

Science.gov (United States)

Wang, Weiwei; Du, Shangchao; Liu, Guo; Tang, Jianwen; Lu, Yeda; Lv, Dong

2017-08-01

Recovery of nickel from a PNG nickel laterite with high content of iron by a sulphation roasting-water leaching has been studied. The influences of sulfuric acid/ore ratio, temperature of roasting and water on recovery efficiency were investigated. The effective separation of nickel over the co-existed elements including iron was achieved by the process with mixing, curing, roasting and leaching stages. Near 100% of nickel was leached from the roasted laterite by water at 80°C in an atmospheric air, while co-leaching of about 2% of iron, under the optimal pre-treatment conditions with the ratio of acid: ore around 0.45:1 and the roasting temperature about 650°C. The advantages and disadvantages of sulphation atmospheric leaching are compared with pressure acid leaching with engineering consideration.

Reactivity of iron-rich phyllosilicates with uranium and chromium through redox transition zones

International Nuclear Information System (INIS)

Burgos, William D.

2016-01-01

This project performed thermodynamic, kinetic, and mineral structural studies on the reactivity of phyllosilicate Fe(II/III) with metal-reducing bacteria, and with two important poly-valent DOE contaminants (chromium and uranium) that show high mobility in their oxidized state. We focused on Fe-bearing phyllosilicates because these are important components of the reactive, fines fraction of Hanford, Oak Ridge, and Idaho National Laboratory sediments. Iron-bearing phyllosilicates strongly influence the redox state and mobility of Cr and U because of their limited hydraulic conductivity, high specific surface area, and redox reactivity. This was a collaborative project between Penn State (W.D. Burgos - PI), Miami University (H. Dong - Co-PI), and Argonne National Laboratory (K. Kemner and M. Boyanov - Co-PIs). Penn State and Miami University were funded together but separately from ANL. This report summarizes research findings and publications produced by Penn State and Miami University.

Reactivity of iron-rich phyllosilicates with uranium and chromium through redox transition zones

Energy Technology Data Exchange (ETDEWEB)

Burgos, William D. [Pennsylvania State Univ., University Park, PA (United States)

2016-09-01

This project performed thermodynamic, kinetic, and mineral structural studies on the reactivity of phyllosilicate Fe(II/III) with metal-reducing bacteria, and with two important poly-valent DOE contaminants (chromium and uranium) that show high mobility in their oxidized state. We focused on Fe-bearing phyllosilicates because these are important components of the reactive, fines fraction of Hanford, Oak Ridge, and Idaho National Laboratory sediments. Iron-bearing phyllosilicates strongly influence the redox state and mobility of Cr and U because of their limited hydraulic conductivity, high specific surface area, and redox reactivity. This was a collaborative project between Penn State (W.D. Burgos – PI), Miami University (H. Dong – Co-PI), and Argonne National Laboratory (K. Kemner and M. Boyanov – Co-PIs). Penn State and Miami University were funded together but separately from ANL. This report summarizes research findings and publications produced by Penn State and Miami University.

Nanomagnetic domains of chromium deposited on vertically-aligned carbon nanotubes

International Nuclear Information System (INIS)

Wright, Andrew C.; Faulkner, Michael K.; Harris, Robert C.; Goddard, Alex; Abbott, Andrew P.

2012-01-01

The drive to create ever smaller magnetic memory devices has led to the development of new nanomagnetic domains on surfaces. This paper reports the development of nano-chromium magnetic domains obtained using electrodeposition on vertically aligned carbon nanofibers arrays. Attempts to achieve this using conventional aqueous solutions were unsuccessful even after thin nickel underlayers were applied. The use of a novel electrolyte, a deep eutectic solvent, made from choline chloride: chromium (III) chloride enabled highly conformal overcoatings of chromium on individual bare carbon nanotubes to be obtained. Very high aspect ratio metal microstructures could be obtained by this novel technology. Magnetic imaging of the coated nanoarrays showed there to be clear magnetic character to the coating when the thin coatings were applied but this disappeared when the deposits were thicker and more contiguous. - Highlights: ► Nanoscale chromium deposited from non-aqueous electrolyte shows magnetic behavior. ► Vertically aligned carbon nanotubes conformally coated with chromium metal. ► Ionic liquid electrolyte superior to chromic acid for plating high aspect ratio structures.

Nanomagnetic domains of chromium deposited on vertically-aligned carbon nanotubes

Energy Technology Data Exchange (ETDEWEB)

Wright, Andrew C., E-mail: a.wright@glyndwr.ac.uk [Advanced Materials Research Laboratory, Materials Science Research Center, Glyndwr University, Wrexham LL11 2AW (United Kingdom); Faulkner, Michael K., E-mail: m.faulkner@manchester.ac.uk [Manchester Materials Science Centre, University of Manchester, Grosvenor Street, Manchester M13 9PL (United Kingdom); Harris, Robert C.; Goddard, Alex; Abbott, Andrew P., E-mail: apa1@le.ac.uk [Department of Chemistry, University of Leicester, Leicester LE1 7RH (United Kingdom)

2012-12-15

The drive to create ever smaller magnetic memory devices has led to the development of new nanomagnetic domains on surfaces. This paper reports the development of nano-chromium magnetic domains obtained using electrodeposition on vertically aligned carbon nanofibers arrays. Attempts to achieve this using conventional aqueous solutions were unsuccessful even after thin nickel underlayers were applied. The use of a novel electrolyte, a deep eutectic solvent, made from choline chloride: chromium (III) chloride enabled highly conformal overcoatings of chromium on individual bare carbon nanotubes to be obtained. Very high aspect ratio metal microstructures could be obtained by this novel technology. Magnetic imaging of the coated nanoarrays showed there to be clear magnetic character to the coating when the thin coatings were applied but this disappeared when the deposits were thicker and more contiguous. - Highlights: Black-Right-Pointing-Pointer Nanoscale chromium deposited from non-aqueous electrolyte shows magnetic behavior. Black-Right-Pointing-Pointer Vertically aligned carbon nanotubes conformally coated with chromium metal. Black-Right-Pointing-Pointer Ionic liquid electrolyte superior to chromic acid for plating high aspect ratio structures.

Cytokine detection for the diagnosis of chromium allergy*

Science.gov (United States)

Martins, Luis Eduardo Agner Machado; dos Reis, Vitor Manoel Silva

2013-01-01

BACKGROUND Patch testing remains the gold standard method for the identification of the etiologic agent of allergic contact dermatitis. However, it is a subjective, time-consuming exam whose technique demands special care and which presents some contraindications, which hamper its use. In a recent study, we showed that the proliferation assay can suitably replace patch testing for the diagnosis of chromium allergy, which had been previously demonstrated only for nickel allergy. In this study, we try to refine the method by reducing the incubation period of cultures for lymphocyte proliferation assays in response to chromium. OBJECTIVE Develop an alternative or complementary diagnostic test for chromium allergic contact dermatitis. METHODS We compared the production of 9 cytokines (IFN-γ, IL-2, IL-4, IL-5, IL-10, IL-12, IL-13, IL-17 and RANTES) between 18 chromium-allergic patients and 19 controls. RESULTS Chromium increased the production of IFN-y, IL-5, IL-2 and IL-13 in allergic patients, but only IL-2 and especially IL-13 helped discriminate allergic patients from controls. The sensitivity, specificity and accuracy found with IL-13 were about 80%. CONCLUSIONS IL-13 and IL-2 detection may be used to diagnose chromium allergy in 2-day cultures. However, in general, the 6-day cultures seem to be superior for this purpose. PMID:24173176

Levels of some Trace Metals in Macroalgae from the Red Sea in Egypt

International Nuclear Information System (INIS)

Aboul-Naga, Wafiqa Mohamed

2005-01-01

The concentrations of iron (Fe), Zinc (Zn), manganese (Mn), Copper (Cu), chromium (Cr), nickel (Ni), and cobalt (Co) in ten macroalgae species from the Red Sea coastal water varied widely and also the trend of abundance of each metal also differed from one group to another. Concentration factors varied among species for iron (Fe) copper (Cu) manganese (Mn), but with iron (Fe) showing generally high concentration factors. Highly significant (P<0.05) relationships were found between manganese (Mn) and Nickel (Ni), and, Zinc (Zn) and copper (Cu). Moreover, moderate correlations were observed between manganese (Mn) and iron (Fe) and chromium (Cr), indicating that manganese (Mn) is the most accumulated metal in the macro algae of the Red Sea. In spite of the level of trace metals in the macro algae of the Red Sea. In spite of the level of trace metals in the macro algae, dominance is moderate relative to other sea areas subjected to intensive pollution. That is, the results indicated a nonpolluted environment. (author)

Estimation of differences in trace element composition of Bulgarian summer fruits using ICP-MS

Directory of Open Access Journals (Sweden)

G. Toncheva

2016-06-01

Full Text Available Abstract. The content of potentially essential and toxic elements: chromium, manganese, iron, copper, nickel, cadmium and arsenic in Bulgarian fruits such as aronia, morello, cherry, raspberry, nectarine peach, apple type „akane” and pear type „early gold” were investigated. By using the ICP-MS we found that -1 -1 -1 raspberry has the highest content of iron (4635.9 ± 53.2 μg kg , manganese (5690.9 ± 31.7 μg kg and chromium (150.2 ± 2.5 μg kg , while the richest in -1 copper is the nectarine (887.5 ± 31.19 μg kg . The content of toxic elements (nickel, cadmium and arsenic is in amount significantly below the permissible standards. Single ANOVA and subsequent Dunkan's test were used to define the fruit and to estimate the significance of chemical elements. The test for multidirectional comparisons indicated that for five of the investigated seven elements: iron, copper, nickel, cadmium, and arsenic the fruits are statistically distinguishable According to hierarchical cluster analysis the fruits are into one cluster.

Corrosion resistance of metals and alloys in molten alkalies

International Nuclear Information System (INIS)

Zarubitskij, O.G.; Dmitruk, B.F.; Minets, L.A.

1979-01-01

Literature data on the corrosion of non-ferrous and noble metals, iron and steels in the molten alkalis and mixtures of their base are presented. It is shown that zirconium, niobium and tantalum are characterized by high corrosion stability in the molten NaOH. Additions of NaOH and KOH to the alkali chloride melts result in a 1000 time decrease of zirconium corrosion rate at 850 deg. The data testify to the characteristic passivating properties of OH - ions; Mo and W do not possess an ability to selfpassivation in hydroxide melts. Corrosion resistance of carbon and chromium-nickel steels in hydroxide melts depends considerably on the temperature, electrolyte composition and atmosphere over them. At the temperatures up to 600 deg C chromium-nickel steel is corrosion resistant in the molten alkali only in the inert atmosphere. Corrosion rate of chromium-nickel alloy is the lower the less chromium and the more nickel it contains. For the small installations the 4Kh18N25S2 and Kh23N28M3D3T steels can be recommended

Effect of citric acid and EDTA on chromium and nickel uptake and translocation by Datura innoxia

International Nuclear Information System (INIS)

Jean, Liliane; Bordas, Francois; Gautier-Moussard, Cecile; Vernay, Philippe; Hitmi, Adnane; Bollinger, Jean-Claude

2008-01-01

EDTA and citric acid were tested to solubilize metals and enhance their uptake by Datura innoxia, chosen because of its ability to accumulate and tolerate metals. Two application modes were used on an industrial soil contaminated mainly by Cr and Ni. The results showed that citric acid was the most effective at increasing the uptake of Cr and EDTA for Ni. These results are consistent with the effectiveness of both chelants in solubilizing metals from the soil. The translocation factor (TF) of Ni was 1.6- and 6.7-fold higher than the control, respectively, for one and two applications of 1 mmol kg -1 EDTA. After two applications of 5 and 10 mmol kg -1 citric acid, the TF of Cr increased 2- and 3.5-fold relative to the control. Whatever the concentration, the application of EDTA modified the plant physiology significantly. For citric acid this was only observed with the highest dose (10 mmol kg -1 ). - Chelant effectiveness in increasing chromium and nickel uptake by Datura innoxia is the result of the increase in translocation versus negative effect on plant physiology

Changes of surface structure of Ni, W and chromium-nickel steel Cr18Ni10 irradiated by high fluences of krypton ions with high energies

International Nuclear Information System (INIS)

Didyk, A.Yu.; Semina, V.K.; Khalil, A.; Suvorov, A.L.; Stepanov, A.Eh.; Cheblukov, Yu.N.

1999-01-01

The surfaces of W single crystal, Ni polycrystal and chromium-nickel steel, irradiated by Kr ions with energy 305 and 245 MeV up to the fluences 2*10 15 and 3*10 15 ion/cm 2 , were studied by means of scanning electron microscopy. The evaporation coefficients of material surfaces were estimated on the base of changes of surface relief. The values of these coefficients turned out much more than ones predicted by the inelastic sputtering model. The method of 'step' was offered and realized for the more correct estimations evaporation coefficient on the Ni example. The phenomenological model explaining the observed phenomena is introduced

Remediation of hexavalent chromium spiked soil by using synthesized iron sulfide particles.

Science.gov (United States)

Li, Yujie; Wang, Wanyu; Zhou, Liqiang; Liu, Yuanyuan; Mirza, Zakaria A; Lin, Xiang

2017-02-01

Carboxymethyl cellulose (CMC) stabilized microscale iron sulfide (FeS) particles were synthesized and applied to remediate hexavalent chromium (Cr(VI)) spiked soil. The effects of parameters including dosage of FeS particles, soil moisture, and natural organic matter (NOM) in soil were investigated with comparison to iron sulfate (FeSO 4 ). The results show that the stabilized FeS particles can reduce Cr(VI) and immobilize Cr in soil quickly and efficiently. The soil moisture ranging from 40% to 70% and NOM in soil had no significant effects on Cr(VI) remediation by FeS particles. When molar ratio of FeS to Cr(VI) was 1.5:1, about 98% of Cr(VI) in soil was reduced by FeS particles in 3 d and Cr(VI) concentration decreased from 1407 mg kg -1 to 16 mg kg -1 . The total Cr and Cr(VI) in Toxicity Characteristic Leaching Procedure (TCLP) leachate were reduced by 98.4% and 99.4%, respectively. In FeS particles-treated soil, the exchangeable Cr fraction was mainly converted to Fe-Mn oxides bound fraction because of the precipitation of Cr(III)-Fe(III) hydroxides. The physiologically based extraction test (PBET) bioaccessibility of Cr was decreased from 58.67% to 6.98%. Compared to FeSO 4 , the high Cr(VI) removal and Cr immobilization efficiency makes prepared FeS particles a great potential in field application of Cr(VI) contaminated soil remediation. Copyright © 2016 Elsevier Ltd. All rights reserved.

Chromium metal organic frameworks and synthesis of metal organic frameworks

Science.gov (United States)

Zhou, Hong-Cai; Liu, Tian-Fu; Lian, Xizhen; Zou, Lanfang; Feng, Dawei

2018-04-24

The present invention relates to monocrystalline metal organic frameworks comprising chromium ions and carboxylate ligands and the use of the same, for example their use for storing a gas. The invention also relates to methods for preparing metal organic frameworks comprising chromium, titanium or iron ions and carboxylate ligands. The methods of the invention allow such metal organic frameworks to be prepared in monocrystalline or polycrystalline forms.

High temperature corrosion behaviour of a new Ni-30Fe-10Ar-Cr-alloy

International Nuclear Information System (INIS)

Kloewer, J.; Sauthoff, G.

1997-01-01

The high temperature corrosion behaviour of a new duplex nickel-base alloy containing about 30 mass% iron, 10 mass% aluminium and 8 mass% chromium was determined in both air and hot process gases containing methane/hydrogen, sulphur dioxide and hydrogen sulphide, respectively. It was found that the corrosion resistance against carburisation, sulphidation and oxidation was excellent due to the formation of a dense, protective alumina scale. The adherence of the alumina scale was increased by an addition of 0.1 mass% hafnium. The concentration of chromium was found to have a remarkable impact on the oxidation and high temperature corrosion resistance. Alloys without chromium showed increased corrosion rates in both air and sulphur-containing gas atmospheres due to the initial formation of nickel oxides. In sulphidising SO 2 -and H 2 S- containing gases at least 4 mass% chromium are required to stabilise the formation of alumina and to prevent the formation of nickel/sulphur compounds. (orig.)

Material composition and nuclear data libraries' influence on nickel-chromium alloys activation evaluation: a comparison with decay heat experiments

CERN Document Server

Cepraga, D G

2000-01-01

The paper presents the activation analyses on Inconel-600 nickel-chromium alloy. Three activation data libraries, namely the EAF-4.1, the EAF-97 and the FENDL/A-2, and the FENDL/D-2 decay data library, have been used to perform the calculation with the European activation code ANITA-4/M. The neutron flux distribution into the material samples was provided by JAERI as results of 3D Monte-Carlo MCNP transport code experiment simulation. A comparison with integral decay heat measurement performed at the Fusion Neutronics Source (FNS), JAERI, Tokai, Japan, is used to validate the computational approach. The calculation results are given and discussed. The impact of the material composition, including impurities, on the decay heat of samples irradiated in fusion-like neutron spectra is assessed and discussed. The discrepancies calculations-experiments are within the experimental errors, that is between 6% and 10%, except for the short cooling times (less than 40 min after the end of irradiation). To improve calcul...

Removal of trace metal contaminants from potable water by electrocoagulation

Science.gov (United States)

Heffron, Joe; Marhefke, Matt; Mayer, Brooke K.

2016-06-01

This study investigated the effects of four operational and environmental variables on the removal of trace metal contaminants from drinking water by electrocoagulation (EC). Removal efficiencies for five metals (arsenic, cadmium, chromium, lead and nickel) were compared under varying combinations of electrode material, post-treatment, water composition and pH. Iron electrodes out-performed aluminum electrodes in removing chromium and arsenic. At pH 6.5, aluminum electrodes were slightly more effective at removing nickel and cadmium, while at pH 8.5, iron electrodes were more effective for these metals. Regardless of electrode, cadmium and nickel removal efficiencies were higher at pH 8.5 than at pH 6.5. Post-EC treatment using membrane filtration (0.45 μm) enhanced contaminant removal for all metals but nickel. With the exception of lead, all metals exhibited poorer removal efficiencies as the ionic strength of the background electrolyte increased, particularly in the very high-solids synthetic groundwaters. Residual aluminum concentrations were lowest at pH 6.5, while iron residuals were lowest in low ionic strength waters. Both aluminum and iron residuals required post-treatment filtration to meet drinking water standards. EC with post-treatment filtration appears to effectively remove trace metal contaminants to potable water standards, but both reactor and source water parameters critically impact removal efficiency.

Depositing Nickel-based Hardfacing to Join Carbon Steel and Cast Iron

Directory of Open Access Journals (Sweden)

Tomás Fernández-Columbié

2016-10-01

Full Text Available The objective of this investigation is to determine the micro-structural behavior of a joint between cast iron and carbon steel by depositing a nickel-based substrate in the carbon steel. The filler was added through Shielded Metal Arc Welding using Castec 3099 (UTP 8 electrodes while the base materials were joined through Gas Tungsten Arc Welding with ER 70S – A1 bare electrodes. The Schaeffler diagram was used to analyze the chemical composition of the resulting weld beads. The results of the analysis performed on the welded area and the heat influence zone indicated the formation of acicular structures near the welded line when Castec 3099 electrodes are used and the formation of skeletal ferrite on the heat influence zone during the application of this welding process. An austenitic mixture is formed when ER 70S – A1 electrodes are used.

Investigation on steam oxidation behaviour of TP347H FG Part I Exposure at 256 bar

DEFF Research Database (Denmark)

Jianmin, J; Montgomery, Melanie; Larsen, OH

2005-01-01

with the aforementioned steel in coal-fired boilers and this paper focuses on the steam oxidation behaviour for specimens tested at various metal temperatures for exposure times of 7700, 23000 and 30000 hours as investigated by light optical and scanning electron microscopy. The oxide present on the specimens is a duplex......The stainless steel TP347H FG is a candidate material for the final stage tubing of superheater and reheater sections of ultra supercritical boilers operated at steam temperatures up to 620C in the mild corrosion environments of coal-firing. A series of field tests has been conducted...... oxide, where the outer layer consists of two sub-layers, an iron oxide layer and an iron-nickel oxide layer; the inner layer is chromium rich chromium-iron-nickel oxide. Microstructure examination showed that for all these samples the varying grain size of subsurface metal affected the oxide thickness...

Study of matrix effect in determination of metals in re-refined basic oils by energy dispersive X-ray fluorescence - EDX; Estudo do efeito de matriz na determinação de metais em óleos básicos rerrefinados por fluorescência de raios-X por energia dispersiva

Energy Technology Data Exchange (ETDEWEB)

Melo, Maristela L. S., E-mail: mlsilva@anp.gov.br [Agência Nacional do Petróleo, Gás Natural e Biocombustíveis (ANP), Brasília, DF (Brazil); Souza, Jurandir R. de [Universidade de Brasília (UnB), Brasília, DF (Brazil). Instituto de Química

2015-06-15

In this article, the results of the study of the matrix effect in the determination of metals calcium, chromium, iron, nickel, copper, zinc, molybdenum, cadmium, barium and lead in base oil using Energy Dispersive X-Ray Fluorescence (EDX) are presented. Sensitivities obtained for each calibration curve were evaluated where calcium, chromium, copper, cadmium, barium and lead had the lowest sensitivities. In the case of cadmium, this parameter was lagging and the studies were not carried forward. The curves of the other metals in different base oils were evaluated for linearity. The elements chromium, copper, molybdenum and lead showed linearity problems in some cases. Therefore, curves in different base oils showed distinct mathematical behavior where the matrix effect was confirmed. The other curves were evaluated and existence of the matrix effect attributed to interference of C / H ratio was confirmed in the quantification of all elements. Metals iron, nickel and zinc exhibited the highest sensitivity and determination coefficients, showing that the method has application potential. (author)

Synthesis and Characterization of Mixed Iron-Manganese Oxide Nanoparticles and Their Application for Efficient Nickel Ion Removal from Aqueous Samples

Science.gov (United States)

Serra, Antonio; Monteduro, Anna Grazia; Padmanabhan, Sanosh Kunjalukkal; Licciulli, Antonio; Bonfrate, Valentina; Salvatore, Luca; Calcagnile, Lucio

2017-01-01

Mixed iron-manganese oxide nanoparticles, synthesized by a simple procedure, were used to remove nickel ion from aqueous solutions. Nanostructures, prepared by using different weight percents of manganese, were characterized by transmission electron microscopy, selected area diffraction, X-ray diffraction, Raman spectroscopy, and vibrating sample magnetometry. Adsorption/desorption isotherm curves demonstrated that manganese inclusions enhance the specific surface area three times and the pores volume ten times. This feature was crucial to decontaminate both aqueous samples and food extracts from nickel ion. Efficient removal of Ni2+ was highlighted by the well-known dimethylglyoxime test and by ICP-MS analysis and the possibility of regenerating the nanostructure was obtained by a washing treatment in disodium ethylenediaminetetraacetate solution. PMID:28804670

Long-life fatigue test results for two nickel-base structural alloys

International Nuclear Information System (INIS)

Mowbray, D.F.; Giaquinto, E.V.; Mehringer, F.J.

1978-11-01

The results are reported of fatigue tests on two nickel--base alloys, hot-cold-worked and stress-relieved nickel--chrome--iron Alloy 600 and mill-annealed nickel--chrome--moly--iron Alloy 625 in which S-N data were obtained in the life range of 10 6 to 10 10 cycles. The tests were conducted in air at 600 0 F, in the reversed membrane loading mode, at a frequency of approx. 1850 Hz. An electromagnetic, closed loop servo-controlled machine was built to perform the tests. A description of the machine is given

Use of thermogravimetry and thermodynamic calculations for specifying chromium diffusion occurring in alloys containing chromium carbides during high temperature oxidation

International Nuclear Information System (INIS)

Berthod, Patrice; Conrath, Elodie

2015-01-01

The chromium diffusion is of great importance for the high temperature oxidation behaviour of the chromium-rich carbides-strengthened superalloys. These ones contain high chromium quantities for allowing them well resisting hot corrosion by constituting and maintaining a continuous external scale of chromia. Knowing how chromium can diffuse in such alloys is thus very useful for predicting the sustainability of their chromia-forming behaviour. Since Cr diffusion occurs through the external part of the alloy already affected by the previous steps of oxidation (decarburized subsurface) it is more judicious to specify this diffusion during the oxidation process itself. This was successfully carried out in this work in the case of a model chromia-forming nickel-based alloy containing chromium carbides, Ni(bal.)–25Cr–0.5C (in wt.%). This was done by specifying, using real-time thermogravimetry, the mass gain kinetic due to oxidation, and by combining it with the post-mortem determination of the Cr concentration profiles in subsurface. The values of D Cr thus obtained for 1000, 1050 and 1100 °C in the alloy subsurface are consistent with the values obtained in earlier works for similar alloy's chemical compositions. - Highlights: • A Ni25Cr0.50C alloy was oxidized at high temperature in a thermo-balance. • The mass gain files were analysed to specify the Cr 2 O 3 volatilization constant K v . • Concentration profiles were acquired to specify the chromium gradient. • The diffusion coefficient of chromium through the subsurface was deduced. • The obtained diffusion coefficient is consistent with values previously obtained.

Effect of leaching on heavy metals concentration of soil in some ...

African Journals Online (AJOL)

Administrator

chemical manufacturing, painting and coating, mining, extractive metallurgy, nuclear and other .... The concentration of cadmium, cobalt, chromium, copper, iron, lead, manganese, nickel, tin and zinc from seven locations on each dumpsites at ...

Size-separated particle fractions of stainless steel welding fume particles - A multi-analytical characterization focusing on surface oxide speciation and release of hexavalent chromium.

Science.gov (United States)

Mei, N; Belleville, L; Cha, Y; Olofsson, U; Odnevall Wallinder, I; Persson, K-A; Hedberg, Y S

2018-01-15

Welding fume of stainless steels is potentially health hazardous. The aim of this study was to investigate the manganese (Mn) and chromium (Cr) speciation of welding fume particles and their extent of metal release relevant for an inhalation scenario, as a function of particle size, welding method (manual metal arc welding, metal arc welding using an active shielding gas), different electrodes (solid wires and flux-cored wires) and shielding gases, and base alloy (austenitic AISI 304L and duplex stainless steel LDX2101). Metal release investigations were performed in phosphate buffered saline (PBS), pH 7.3, 37°, 24h. The particles were characterized by means of microscopic, spectroscopic, and electroanalytical methods. Cr was predominantly released from particles of the welding fume when exposed in PBS [3-96% of the total amount of Cr, of which up to 70% as Cr(VI)], followed by Mn, nickel, and iron. Duplex stainless steel welded with a flux-cored wire generated a welding fume that released most Cr(VI). Nano-sized particles released a significantly higher amount of nickel compared with micron-sized particle fractions. The welding fume did not contain any solitary known chromate compounds, but multi-elemental highly oxidized oxide(s) (iron, Cr, and Mn, possibly bismuth and silicon). Copyright © 2017 The Authors. Published by Elsevier B.V. All rights reserved.

Nickel detoxification and plant growth promotion by multi metal resistant plant growth promoting Rhizobium species RL9.

Science.gov (United States)

Wani, Parvaze Ahmad; Khan, Mohammad Saghir

2013-07-01

Pollution of the biosphere by heavy metals is a global threat that has accelerated dramatically since the beginning of industrial revolution. The aim of the study is to check the resistance of RL9 towards the metals and to observe the effect of Rhizobium species on growth, pigment content, protein and nickel uptake by lentil in the presence and absence of nickel. The multi metal tolerant and plant growth promoting Rhizobium strain RL9 was isolated from the nodules of lentil. The strain not only tolerated nickel but was also tolerant o cadmium, chromium, nickel, lead, zinc and copper. The strain tolerated nickel 500 μg/mL, cadmium 300 μg/mL, chromium 400 μg/mL, lead 1,400 μg/mL, zinc 1,000 μg/mL and copper 300 μg/mL, produced good amount of indole acetic acid and was also positive for siderophore, hydrogen cyanide and ammonia. The strain RL9 was further assessed with increasing concentrations of nickel when lentil was used as a test crop. The strain RL9 significantly increased growth, nodulation, chlorophyll, leghaemoglobin, nitrogen content, seed protein and seed yield compared to plants grown in the absence of bioinoculant but amended with nickel The strain RL9 decreased uptake of nickel in lentil compared to plants grown in the absence of bio-inoculant. Due to these intrinsic abilities strain RL9 could be utilized for growth promotion as well as for the remediation of nickel in nickel contaminated soil.

A Novel Nonelectrolytic Process for Chromium and Nickel Coating

Science.gov (United States)

2015-06-01

chromium (CrVI) has been regarded as the “ gold standard” against corrosion in military applications for decades [2]. Its uses range from electronics to...silver or gold . Furthermore, these researchers discovered that for centuries, the metal plating industry was dominated by mercury-based coating...generation of metal and metal alloy particles, including nanoparticles, from a physical mixture of metal nitrate, oxide or hydroxide species and urea. This

Heavy metals content in the stem bark of Detarium microcarpum ...

African Journals Online (AJOL)

Ehianeta Teddy

2013-03-13

Mar 13, 2013 ... nickel, chromium and aluminum standards respectively (Momodu and Anyakora ... there are clues pointing at the interaction of manganese with iron ... Phytoremediation of Uranium-Contaminated Soils: role of organic acids in ...

Relationship between the level of zinc, lead, cadmium, nickel and chromium in hair of people with diabetes

Directory of Open Access Journals (Sweden)

Tadayon F.

2014-07-01

Full Text Available It has long been believed that some metals possess many adverse health effects. Recently, certain elements have been identified as essential trace elements that play an important role in the genesis and progression of several diseases. Some toxic metals have also been shown to be elevated in biological samples of diabetes mellitus patients. The status of trace elements in diabetes patients is also influenced by their diet, drugs administered and, to a large extent, by environmental factors. Pollutants due to the presence of toxic metals in environment not only enter the body by breading, water, and foodstuff accumulates in hair, but they could be adsorbed directly on the hair from environment. The aim of present study was to investigate the relationship between the level of zinc, lead, cadmium, nickel and chromium in hair samples of diabetic women from Tehran (Iran. The study population consisted of 100 women between 30 to 70 years of age from Tehran. The hair samples were washed with 1% (w/v (DDTC, 0.1M HCL and deionized water. Afterwards, the hair sample dried in oven at 70° C for 5 hours and then digested the next day. Dry ashing digestion procedure was carried out. The concentration of elements was measured by means of an atomic absorption spectrophotometer. The statistical analysis confirmed that mean concentrations of lead and nickel did not differ significantly from the control group. The results of this study showed that the mean values of Cr and Zn were significantly decreased in scalp hair samples of diabetic patients as compared to control subjects. Hair Cd level was significantly higher in type 2 diabetic patients. Values of Pearson correlation coefficient showed positive correlation between these elements.

Process for recovering uranium

Science.gov (United States)

MacWood, G. E.; Wilder, C. D.; Altman, D.

1959-03-24

A process useful in recovering uranium from deposits on stainless steel liner surfaces of calutrons is presented. The deposit is removed from the stainless steel surface by washing with aqueous nitric acid. The solution obtained containing uranium, chromium, nickel, copper, and iron is treated with an excess of ammonium hydroxide to precipitnte the uranium, iron, and chromium and convert the nickel and copper to soluble ammonio complexions. The precipitated material is removed, dried and treated with carbon tetrachloride at an elevated temperature of about 500 to 600 deg C to form a vapor mixture of UCl/ sub 4/, UCl/sub 5/, FeCl/sub 3/, and CrCl/sub 4/. The UCl/sub 4/ is separated from this vapor mixture by selective fractional condensation at a temperature of about 500 to 400 deg C.

Effect of Nickel Equivalent on Austenite Transition Ratio in Ni-Mn-Cu Cast Iron

Directory of Open Access Journals (Sweden)

Janus A.

2013-06-01

Full Text Available Determined was quantitative effect of nickel equivalent value on austenite decomposition degree during cooling-down castings of Ni-Mn- Cu cast iron. Chemical composition of the alloy was 1.8 to 5.0 % C, 1.3 to 3.0 % Si, 3.1 to 7.7 % Ni, 0.4 to 6.3 % Mn, 0.1 to 4.9 % Cu, 0.14 to 0.16 % P and 0.03 to 0.04 % S. Analysed were castings with representative wall thickness 10, 15 and 20 mm. Scope of the examination comprised chemical analysis (including WDS, microscopic observations (optical and scanning microscopy, image analyser, as well as Brinell hardness and HV microhardness measurements of structural components.

Studies on physicochemical properties of pure and iron substituted chromium niobates, Cr{sub 1−x}Fe{sub x}NbO{sub 4} (x = 0, 0.2, 0.4, 0.6)

Energy Technology Data Exchange (ETDEWEB)

Sree Rama Murthy, A.; Gnanasekar, K.I. [Materials Chemistry and Metal Fuel Cycle Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India); Govindaraj, R. [Materials Science Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India); Jayaraman, V., E-mail: vjram@igcar.gov.in [Materials Chemistry and Metal Fuel Cycle Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India); Umarji, A.M. [Materials Research Centre, Indian Institute of Science, Bangalore 560012 (India)

2017-03-15

Highlights: • Systematic increase in unit cell volume on iron substitution. • Similar mechanism of electronic conduction in these compositions. • Decrease in quadrupole splitting with increasing iron content in Mössbauer spectra. • Iron and chromium exhibited multiple valences, as identified from X-ray photoelectron spectra. - Abstract: Pristine and iron substituted chromium niobates (Cr{sub 1−x}Fe{sub x}NbO{sub 4} with x = 0, 0.2, 0.4 and 0.6) are prepared by solid-state synthesis and phase characterised by X-ray diffraction. Microstructure is determined using scanning electron microscope and micro-chemical analysis is performed by energy dispersive X-ray analysis (EDX). The current-voltage characteristics are studied in the temperature range of 423–723 K. The electrical conductivity of sintered pellets is measured by impedance spectroscopy. Temperature dependent magnetization studies are performed using vibrating sample magnetometer (VSM) and room temperature Bohr magneton number is calculated from the magnetic susceptibility data. The conductivity is passed through a minimum at x = 0.2 in Cr{sub 1−x}Fe{sub x}NbO{sub 4} for x = 0–0.6. X-ray photoelectron spectroscopic studies revealed the surface non-stoichiometry in these compositions.

The corrosion of austenitic steel in flowing high-temperature water

International Nuclear Information System (INIS)

Asmundis, C. de; Weisgerber, P.; Mazzocchi, N.; Plog, C.

1981-01-01

This work represents an attempt to obtain data on the corrosion product formation, including corrosion products which are released to the water, of austenitic steel. AISI 316 or DIN Werkstoff No. 14401. The oxidation experiments were carried out in a small laboratory test loop, which was designed for this study. In the stainless water system considered during an oxidation time of 1800 h at 300 0 C, five zones of differing composition developed. 1. The base metal (for comparison) Fe/Cr/Ni = 67/20/13. 2. The metal at the metal/oxide interface nickel enriched, chromium and iron decreased Fe/Cr/Ni = 64/19/17. 3. The inner oxide chromium enriched and iron and nickel decreased Fe/Cr/Ni = 53/32/14. 4. The outer oxide iron enriched, chromium decreased Fe/Cr/Ni = 70/17/13. 5. The corrosion products released to the water, in total, i.e. particulate and dispersed matter, a Fe/Cr/Ni ratio rather close to that base metal: Fe/Cr/Ni = 68/19/13. (80% particulate: Fe/Cr/Ni = 72/23/5, 20% dispersed: Fe/Cr/Ni = 55/1/44)

Iron (III Ion Sensor Based on the Seedless Grown ZnO Nanorods in 3 Dimensions Using Nickel Foam Substrate

Directory of Open Access Journals (Sweden)

Mazhar Ali Abbasi

2013-01-01

Full Text Available In the present work, the seedless, highly aligned and vertical ZnO nanorods in 3 dimensions (3D were grown on the nickel foam substrate. The seedless grown ZnO nanorods were characterised by field emission scanning electron microscopy (FESEM, high resolution transmission electron microscopy (HRTEM, and X-ray diffraction (XRD techniques. The characterised seedless ZnO nanorods in 3D on nickel foam were highly dense, perpendicular to substrate, grown along the (002 crystal plane, and also composed of single crystal. In addition to this, these seedless ZnO nanorods were functionalized with trans-dinitro-dibenzo-18-6 crown ether, a selective iron (III ion ionophore, along with other components of membrane composition such as polyvinyl chloride (PVC, 2-nitopentylphenyl ether as plasticizer (NPPE, and tetrabutyl ammonium tetraphenylborate (TBATPB as conductivity increaser. The sensor electrode has shown high linearity with a wide range of detection of iron (III ion concentrations from 0.005 mM to 100 mM. The low limit of detection of the proposed ion selective electrode was found to be 0.001 mM. The proposed sensor also described high storage stability, selectivity, reproducibility, and repeatability and a quick response time of less than 10 s.

Investigation of some trace elements in drinking water: Nuba Mountains Section, Sudan

International Nuclear Information System (INIS)

Elgorashe, R.E.E.

2008-09-01

This study was conducted to assess the extent of pollution in the drinking water from various sources at the area of the Nuba Mountains, Sudan. 42 samples were collected from hand pump stations, water yard (diesel machine) stations and surface water (lake) stations.These waters were analyzed using atomic absorption spectrophotometer. The concentrations of iron, nickel, copper, manganese, magnesium, zinc and chromium were determined using flame atomic spectroscopy, while the concentrations of cadmium and lead were determined by furnace atomic spectroscopy. The mean concentrations of iron, nickel, lead, copper, manganese, magnesium, zinc and chromium in water samples collected from hand pump stations were 1.901, 0.010, 0.1310, 0.0070, 0.0410, 20.35, 0.558 and 0.0430 mg/L respectively. And in samples collected from water yard stations were found to be 0.871, 0.013, 0.438, 0.209, 0.128, 28.41, 0.103 and 0.032 mg/L for iron, nickel, lead, copper, manganese, magnesium, zinc and chromium respectively. And in samples collected from surface water station were found to be 13.74, 0.023, 0.015, 0.017, 0.118, 7.008, 0.042 and 0.0002 mg/L for iron, nickel, lead, copper, manganese, magnesium, zinc and chromium respectively. The concentrations of cadmium were found below detection of limits. Mean concentrations of elements from different sources were compared using the Kruskal - wallis method. This study showed that there are significant different between mean concentrations for these elements. The spear man correlation method was identified between elements. Correlation study shows that there is a significant positive correlation between iron and chromium. Comparison between those data and the specific criterion specifies drinking water by the World Health Organization (WHO) showed that the concentrations of Pb are exceeding the maximum permissible levels in eighteen stations. Violations of drinking water limits were observed also for the elements Mn in six stations and Cr in

Investigation of some trace elements in drinking water: Nuba Mountains Section, Sudan

Energy Technology Data Exchange (ETDEWEB)

Elgorashe, R E.E. [Coordination Council of Sudan Atomic Energy Commission, Sudan Academy of Sciences, Khartoum (Sudan)

2008-09-15

This study was conducted to assess the extent of pollution in the drinking water from various sources at the area of the Nuba Mountains, Sudan. 42 samples were collected from hand pump stations, water yard (diesel machine) stations and surface water (lake) stations.These waters were analyzed using atomic absorption spectrophotometer. The concentrations of iron, nickel, copper, manganese, magnesium, zinc and chromium were determined using flame atomic spectroscopy, while the concentrations of cadmium and lead were determined by furnace atomic spectroscopy. The mean concentrations of iron, nickel, lead, copper, manganese, magnesium, zinc and chromium in water samples collected from hand pump stations were 1.901, 0.010, 0.1310, 0.0070, 0.0410, 20.35, 0.558 and 0.0430 mg/L respectively. And in samples collected from water yard stations were found to be 0.871, 0.013, 0.438, 0.209, 0.128, 28.41, 0.103 and 0.032 mg/L for iron, nickel, lead, copper, manganese, magnesium, zinc and chromium respectively. And in samples collected from surface water station were found to be 13.74, 0.023, 0.015, 0.017, 0.118, 7.008, 0.042 and 0.0002 mg/L for iron, nickel, lead, copper, manganese, magnesium, zinc and chromium respectively. The concentrations of cadmium were found below detection of limits. Mean concentrations of elements from different sources were compared using the Kruskal - wallis method. This study showed that there are significant different between mean concentrations for these elements. The spear man correlation method was identified between elements. Correlation study shows that there is a significant positive correlation between iron and chromium. Comparison between those data and the specific criterion specifies drinking water by the World Health Organization (WHO) showed that the concentrations of Pb are exceeding the maximum permissible levels in eighteen stations. Violations of drinking water limits were observed also for the elements Mn in six stations and Cr in

African leafy vegetables consumed by households in the Limpopo ...

African Journals Online (AJOL)

pureed green leafy vegetables was shown to have a beneficial effect ..... was regarded as very nutritious; “having it is just like having meat”. ...... chromium, copper, iodine, iron, manganese, molybdenum, nickel, silicon, vanadium, and zinc.

ORIGINAL ARTICLES

African Journals Online (AJOL)

deficiency in children and the relative risks of associated health problems, applied to revised burden of disease estimates for. South Africa in the ..... Vitamin K, Arsenic, Boron, Chromium, Copper, Iodine, Iron, Manganese, Molybdenum,. Nickel ...

Synthesis and Characterization of Mixed Iron-Manganese Oxide Nanoparticles and Their Application for Efficient Nickel Ion Removal from Aqueous Samples

Directory of Open Access Journals (Sweden)

Alessandro Buccolieri

2017-01-01

Full Text Available Mixed iron-manganese oxide nanoparticles, synthesized by a simple procedure, were used to remove nickel ion from aqueous solutions. Nanostructures, prepared by using different weight percents of manganese, were characterized by transmission electron microscopy, selected area diffraction, X-ray diffraction, Raman spectroscopy, and vibrating sample magnetometry. Adsorption/desorption isotherm curves demonstrated that manganese inclusions enhance the specific surface area three times and the pores volume ten times. This feature was crucial to decontaminate both aqueous samples and food extracts from nickel ion. Efficient removal of Ni2+ was highlighted by the well-known dimethylglyoxime test and by ICP-MS analysis and the possibility of regenerating the nanostructure was obtained by a washing treatment in disodium ethylenediaminetetraacetate solution.

Prevalence of contact allergy to metals in the European general population with a focus on nickel sulfate and piercings: The EDEN Fragrance Study.

Science.gov (United States)

Schuttelaar, Marie L A; Ofenloch, Robert F; Bruze, Magnus; Cazzaniga, Simone; Elsner, Peter; Gonçalo, Margarida; Naldi, Luigi; Svensson, Åke; Diepgen, Thomas L

2018-04-10

Studies on sensitization to metals in the general population are scarce. To determine the prevalence of sensitization to metals in the general population, and factors associated with nickel sensitization. In 5 European countries (The Netherlands, Germany, Italy, Portugal and Sweden), a random sample (N = 3119) from the general population (aged 18-74 years) was patch tested and interviewed by use of a questionnaire on exposure to metals, piercing, and jewellery. Overall, the age-standardized prevalences of sensitization to nickel, cobalt and chromium were, respectively, 14.5%, 2.1%, and 0.8%. The highest prevalence of nickel sensitization was seen in Portugal (18.5%) and the lowest (8.3%) in Sweden. The prevalence of cobalt sensitization varied between 3.8% (The Netherlands) and 0.9% (Italy), and the prevalence of chromium sensitization varied between 1.3% (Portugal) and 0.2% (Sweden). Significant associations were observed between nickel allergy and female sex (odds ratio [OR] 5.19; 95% confidence interval [95%CI]: 3.99-6.74), past piercing use (OR 3.86; 95%CI: 2.85-5.24), and currently having ≥3 piercings (OR 5.58; 95%CI: 4.02-7.76). The prevalence of sensitization to metals in the European general population was high, mostly because of nickel. The lowest prevalence of contact allergy to nickel and chromium observed in Sweden supports the effectiveness of long-standing regulation. © 2018 The Authors. Contact Dermatitis published by John Wiley & Sons Ltd.

Dissolution studies on Nickel ferrite in dilute chemical decontamination formulations

Energy Technology Data Exchange (ETDEWEB)

Ranganathan, S. [New Brunswick Univ., Fredericton, NB (Canada). Dept. of Chemical Engineering; Srinivasan, M.P. [Bhabha Atomic Research Centre (BARC) (India). Water and Steam Chemistry Laboratory; Raghavan, P.S. [Madras Christian College, Chennai (India); Narasimhan, S.V. [Bhabha Atomic Research Centre, Bombay (India); Gopalan, R. [Madras Christian College, Chennai (India). Department of Chemistry

2004-09-01

Nickel ferrite is one of the important corrosion products in the pipeline surfaces of water-cooled nuclear reactors. The dissolution of the nickel ferrite by chelating agents is very sensitive to the nature of the chelant, the nature of the reductant used in the formulation and the temperature at which the dissolution studies are performed. The dissolution is mainly controlled by the reductive dissolution of the ferrite particles, but complexing agents also play a significant role in the dissolution process. This study deals with the leaching of iron and nickel from nickel ferrite prepared by the solid-state method. The dissolution studies are performed in pyridine-2,6-dicarboxylic acid (PDCA), nitrilotriacetic acid (NTA), and ethylenediaminetetraacetic acid (EDTA) formulations containing organic reductants like ascorbic acid and low oxidation state transition metal ion reductants like Fe(II)-L (where L = PDCA, NTA, EDTA) at 85 C. The dissolution of nickel ferrite in PDCA, NTA and EDTA formulations is influenced by the presence of reductants in the formulations. The addition of Fe(II)-L in the formulation greatly enhances the dissolution of nickel ferrite. The preferential leaching of nickel over iron during the dissolution of nickel ferrite was observed in all the formulations. (orig.)

Dissolution studies on Nickel ferrite in dilute chemical decontamination formulations

International Nuclear Information System (INIS)

Ranganathan, S.; Narasimhan, S.V.; Gopalan, R.

2004-01-01

Nickel ferrite is one of the important corrosion products in the pipeline surfaces of water-cooled nuclear reactors. The dissolution of the nickel ferrite by chelating agents is very sensitive to the nature of the chelant, the nature of the reductant used in the formulation and the temperature at which the dissolution studies are performed. The dissolution is mainly controlled by the reductive dissolution of the ferrite particles, but complexing agents also play a significant role in the dissolution process. This study deals with the leaching of iron and nickel from nickel ferrite prepared by the solid-state method. The dissolution studies are performed in pyridine-2,6-dicarboxylic acid (PDCA), nitrilotriacetic acid (NTA), and ethylenediaminetetraacetic acid (EDTA) formulations containing organic reductants like ascorbic acid and low oxidation state transition metal ion reductants like Fe(II)-L (where L = PDCA, NTA, EDTA) at 85 C. The dissolution of nickel ferrite in PDCA, NTA and EDTA formulations is influenced by the presence of reductants in the formulations. The addition of Fe(II)-L in the formulation greatly enhances the dissolution of nickel ferrite. The preferential leaching of nickel over iron during the dissolution of nickel ferrite was observed in all the formulations. (orig.)

Solubility of nickel-cadmium ferrite in acids

International Nuclear Information System (INIS)

Vol'ski, V.; Vol'ska, Eh.; Politan'ska, U.

1977-01-01

The solubility of a solid solution of nickel-cadmium ferrite containing an excess of ferric oxide, (CdO)sub(0.5), (NiO)sub(0.5) and (Fe 2 O 3 )sub(1.5), in hydrochloric and nitric acids at 20, 40 and 60 deg C, was determined colorimetrically and chelatometrically, as well as by studying the x-ray diffraction patterns of the preparations prior to dissolution and their residues after dissolution. It is shown that cadmium passes into the solution faster than iron and nickel; after 800 hours, the solution contains 40% of iron ions and more than 80% of cadmium ions. The kinetics of ferrite dissolution is studied

Assessment of chromium, nickel, cobalt and zinc in edible flesh of ...

African Journals Online (AJOL)

ADOWIE PERE

melanotheron) are two of the highly consumed fish species in Bodo River. .... American diet as 60-90µg per day (i.e. estimated daily intake). ... estimated daily intake (EDI) for chromium in a North .... Trace Element Concentrations in Freshwater.

Influence of Nickel Addition on Properties of Secondary AlSi7Mg0.3 Alloy

Directory of Open Access Journals (Sweden)

Richtárech L.

2015-06-01

Full Text Available This paper deals with influence on segregation of iron based phases on the secondary alloy AlSi7Mg0.3 microstructure by nickel. Iron is the most common and harmful impurity in aluminum casting alloys and has long been associated with an increase of casting defects. In generally, iron is associated with the formation of Fe-rich intermetallic phases. It is impossible to remove iron from melt by standard operations. Some elements eliminates iron by changing iron intermetallic phase morphology, decreasing its extent and by improving alloy properties. Realization of experiments and results of analysis show new view on solubility of iron based phases during melt preparation with higher iron content and influence of nickel as iron corrector of iron based phases.

Effects of alloying elements on nodular and uniform corrosion resistance of zirconium-based alloys

International Nuclear Information System (INIS)

Abe, Katsuhiro

1992-01-01

The effects of alloying and impurity elements (tin, iron, chromium, nickel, niobium, tantalum, oxygen, aluminum, carbon, nitrogen, silicon, and phosphorus) on the nodular and uniform corrosion resistance of zirconium-based alloys were studied. The improving effect of iron, nickel and niobium in nodular corrosion resistance were observed. The uniform corrosion resistance was also improved by nickel, niobium and tantalum. The effects of impurity elements, nitrogen, aluminum and phosphorus were negligibly small but increasing the silicon content seemed to improve slightly the uniform corrosion resistance. Hydrogen pick-up fraction were not changed by alloying and impurity elements except nickel. Nickel addition increased remarkably hydrogen pick-up fraction. Although the composition of secondary precipitates changed with contents of alloying elements, the correlation of composition of secondary precipitates to corrosion resistance was not observed. (author)

Evaluation and comparison of shear bond strength of porcelain to a beryllium-free alloy of nickel-chromium, nickel and beryllium free alloy of cobalt-chromium, and titanium: An in vitro study

Directory of Open Access Journals (Sweden)

Ananya Singh

2017-01-01

Conclusion: It could be concluded that newer nickel and beryllium free Co-Cr alloys and titanium alloys with improved strength to weight ratio could prove to be good alternatives to the conventional nickel-based alloys when biocompatibility was a concern.

Microsegregation observed in Fe-35.5Ni-7.5Cr irradiated in EBR-II

International Nuclear Information System (INIS)

Brager, H.R.; Garner, F.A.

1984-01-01

At 593 0 C one alloy, Fe-35.5Ni-7.5Cr, which was particularly resistant to swelling in EBR-II, increased in density 0.9% at 7.6 x 10 22 n/cm 2 (E > 0.1 MeV). Examination by energy dispersive x-ray analysis revealed that substantial oscillations occur in the nickel content of the alloy, varying from 25 to 53% about the nominal level of 35.5%. These oscillations exhibit a period of approx.200 nm. Regions enriched in nickel are depleted in chromium and iron, and the reverse is true in regions of low nickel content. This spinodal-like process produces a net densification and also appears to eventually destroy the swelling resistance of the alloy. Once voids form in the nickel-poor chromium-rich regions, further segregation of nickel to void surfaces is expected to accelerate the loss of swelling resistance

Bioleaching of a complex nickel–iron concentrate by mesophile bacteria.

OpenAIRE

Santos, Luciano Rodrigo Gomes; Barbosa, Alexandre Ferraz; Souza, Adelson Dias de; Leão, Versiane Albis

2006-01-01

This work investigates the bioleaching of a complex nickel–iron concentrate (pentlandite, pyrrhotite, and minor amounts of chalcopyrite) using acidophile iron-oxidizing bacteria. It aims to improve the understanding of the mechanism of bacterial action on nickel sulphide bioleaching. The effects of the external addition of Fe(II) and the mineralogical assembly on the extraction of nickel are evaluated. A high nickel extraction (around 70%) can be achieved in batch experiments. Moreover, the e...

Study of alumina-trichite reinforcement of a nickel-based matric by means of powder metallurgy

Science.gov (United States)

Walder, A.; Hivert, A.

1982-01-01

Research was conducted on reinforcing nickel based matrices with alumina trichites by using powder metallurgy. Alumina trichites previously coated with nickel are magnetically aligned. The felt obtained is then sintered under a light pressure at a temperature just below the melting point of nickel. The halogenated atmosphere technique makes it possible to incorporate a large number of additive elements such as chromium, titanium, zirconium, tantalum, niobium, aluminum, etc. It does not appear that going from laboratory scale to a semi-industrial scale in production would create any major problems.

The suppression of dissolution for alloy 690 in high temperature and high pressure water with chromium ion implantation

International Nuclear Information System (INIS)

Shibata, Toshio; Fujimoto, Shinji; Ohtani, Saburou; Watanabe, Masanori; Hirao, Kyozo; Okumoto, Masaru; Shibaike, Hiroyuki.

1994-01-01

As the material of heat exchanger tubes for PWRs, the nickel alloys such as alloy 690 and alloy 600 have been used, but 58 Ni and 60 Co contained as an impurity elute in primary cooling water, and are radioactivated, in this way, they become the cause of radiation exposure. By increasing chromium concentration, the corrosion resistance of nickel alloys is improved, and for modern heat exchangers, the alloy 690, of which the chromium content is increased up to 30%, has been adopted, and excellent results have been obtained. In this research, aiming at the further reduction of radiation exposure, by increasing the chromium concentration in surface layer using ion implantation technology, the change of the corrosion behavior of alloy 690 in high temperature, high pressure water was investigated. The chemical composition of the alloy 690 used, and the making of plate specimens are shown. The polarization behavior of alloy 690 in 0.1 mol/l sulfuric acid deaerated at normal temperature is reported, and the effect of suppressing dissolution was remarkable in the specimens with much implantation. The electrochemical behavior of alloy 690 in simulated cooling water was investigated. Immobile case has high chromium content and is thin. (K.I.)

Magnetism of iron and nickel from rotationally invariant Hirsch-Fye quantum Monte Carlo calculations

Science.gov (United States)

Belozerov, A. S.; Leonov, I.; Anisimov, V. I.

2013-03-01

We present a rotationally invariant Hirsch-Fye quantum Monte Carlo algorithm in which the spin rotational invariance of Hund's exchange is approximated by averaging over all possible directions of the spin quantization axis. We employ this technique to perform benchmark calculations for the two- and three-band Hubbard models on the infinite-dimensional Bethe lattice. Our results agree quantitatively well with those obtained using the continuous-time quantum Monte Carlo method with rotationally invariant Coulomb interaction. The proposed approach is employed to compute the electronic and magnetic properties of paramagnetic α iron and nickel. The obtained Curie temperatures agree well with experiment. Our results indicate that the magnetic transition temperature is significantly overestimated by using the density-density type of Coulomb interaction.

Box-Behnken experimental design for chromium(VI) ions removal by bacterial cellulose-magnetite composites.

Science.gov (United States)

Stoica-Guzun, Anicuta; Stroescu, Marta; Jinga, Sorin Ion; Mihalache, Nicoleta; Botez, Adriana; Matei, Cristian; Berger, Daniela; Damian, Celina Maria; Ionita, Valentin

2016-10-01

In this study bacterial cellulose-magnetite composites were synthesised for the removal of chromium(VI) from aqueous solutions. Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), thermogravimetric analysis and X-ray Photoelectron Spectroscopy (XPS) were used to characterize the bacterial cellulose-magnetite composites and to reveal the uniform dispersion of nanomagnetite in the BC matrix. Magnetic properties were also measured to confirm the magnetite immobilization on bacterial cellulose membrane. The effects of initial Cr(VI) concentration, solution pH and solid/liquid ratio upon chromium removal were examined using the statistical Box-Behnken Design. Because of the possibility of magnetite dissolution during chromium(VI) adsorption, the degree of iron leaching was also analysed in the same conditions as Cr(VI) adsorption. From the factors affecting chromium(VI) adsorption the most important was solution pH. The highest Cr(VI) removal efficiency was observed at pH 4, accompanied by the lowest iron leaching in the solution. The adsorption experiments also indicated that the adsorption process of chromium(VI) is well described by Freundlich adsorption model. Our results proved that the BC-magnetite composites could be used for an efficient removal of chromium(VI) from diluted solutions with a minimum magnetite dissolution during operation. Copyright © 2016 Elsevier B.V. All rights reserved.

The effect of heat treatment on structure and properties of hard metals on a tungsten carbide basis with iron-nickel-binders

International Nuclear Information System (INIS)

Chaporova, I.N.; Kudryavtseva, V.I.; Sapronova, Z.N.; Sychkova, L.V.

1980-06-01

In the present paper the effect of storage and quenching on structure and properties of WC(Fe,Ni)-hardmetals was investigated. Starting materials were powders of tungsten carbide, iron and nickel, commonly used for the hard metal production. WC(Fe,Ni)-specimens (Fe: Ni = 80:20, 85:15) with 8, 11, 80, 85, 89 and 92 percent by weight were produced for the investigation. (orig.) [de

Evaluation of chromite ore and the optimum methods for industrial extraction of chromium

International Nuclear Information System (INIS)

Salih, Bakheit Mustafa Mohamed

1999-10-01

Samples of chromite ore, collected from Gam and Cheikay mining area (Ingaessana Hills) in east Sudan, were analysed to assess the chromium content. Analysis were carried out using atomic absorption spectroscopy (AAS) to estimate the contents of chromium, iron, calcium and magnesium. X-ray florescence (XRF) was used to evaluate the levels of chromium, iron and calcium in the ore. Volumetric analysis was performed to assess chromium and iron, whilest gravimetric analysis was employed to measure the amounts of calcium, magnesium, aluminum and silicon present in the ore. The results are in a good agreement except iron oxide, which displayed a significantly different value when measured by x-ray fluorescence. The data obtained exhibited similarity in almost all cases, when compared with local and global researches, reports and literature. The study has revealed the average contents of Cr 2 O 3 , FeO, CaO, MgO, Al 2 O 3 , and SiO 2 as 40.66, 11.96, 11.94, 0.36, 16.94, 11.45% respectively. MnO and NiO were detected in trace amounts, the corresponding levels in the ore being 72 and 27 ppm. The average chromium content in extracted potassium dichromate measured by using AAS, XRF, and volumetric methods was found to be 31.7%. The highest grade reached by individual technique being 33.10%. The extraction with sodium peroxide is the optimum method for preparation of potassium dichromate. X-ray diffraction analysis, has showed that the d spaces and intensities of prepared potassium dichromate are isostructural with the corresponding ones of standard potassium dichromate. This suggests that the composition of the two samples is identical. Chromite samples were analysed using gamma ray spectroscopy in order to estimate the levels of radioactive elements present. It was found that the concentrations of 232 Th and 40 K range from 7.62 to 10.98 Bq/kg and 47.38 to 56.28 Bq/kg respectively

Trace element studies in urolithiasis; preliminary investigation on mixed calcium oxalate-struvite urinary calculi

International Nuclear Information System (INIS)

Syed, A.M.; Qadiruddin, M.; Shirin, K.; Manser, W.W.T.

1999-01-01

In this study the levels of the trace elements copper , zinc, lead, iron, aluminum, nickel, chromium along with magnesium, sodium and potassium were estimated in fifteen mixed calcium oxalate-struvite (CaOx/STR) urinary stones. The mean values of the combined results were, copper 4.24, zinc 1302, zinc 1302.10, lead 23.25, iron 36.83,nickel 0.69, chromium 1.93, magnesium 4530441, sodium 54.13 and potassium 5.93 ng mg/sup -1/. It was observed that zinc, aluminum and potassium levels were higher than in calcium oxalate(CaOx) calculi 0.05>P>0.02 and potassium levels were higher than in mixed calcium oxalate-hydroxy appetite (CaOx/APA) calculi, P<0.01. A combination of all the results was also compared with similar data from South Africa, Turkey, Austria, India, U.S.A and Japan. (author)

Thermodynamic properties of chromium bearing slags and minerals. A review

Energy Technology Data Exchange (ETDEWEB)

Xiao Yanping; Holappa, L.

1996-12-31

In this report, the thermodynamic properties of chromium bearing slags and minerals were reviewed based on the available information in the literature. It includes the analysing methods for oxidation state of chromium in slags, oxidation state of chromium and activities of chromium oxides in slags and minerals. The phase diagrams of chromium oxide systems and chromium distributions between slag and metal phases are also covered ill this review. Concerning the analysing methods, it was found that most of the available approaches are limited to iron free slag systems and the sample preparation is very sensitive to the analysing results. In silicate slags under reducing atmosphere, divalent and trivalent chromium co-exist in the slags. It is agreed that the fraction of divalent chromium to total chromium increases with higher temperature, lower slag basicity and oxygen potential. For the slags under oxidising atmosphere, trivalent, pentavalent and hexavalent states were reported to be stable. The activities of CrO and CrO{sub 1.5} were concluded to have positive deviation from ideal solution. Slag basicity has a positive effect and temperature has a negative effect on the activities of chromium oxides. The phase diagrams of the Cr-O, binary, and ternary chromium containing oxide systems have been examined systematically. The analysis shows that the data on the quaternary and quinary systems are insufficient, and require further investigation. The most important features of the chromium containing silicate slags are the large miscibility gaps and the stability of the chromite spinel. (orig.) (76 refs.)

Structural investigations of amorphised iron and nickel by high-fluence metalloid ion implantation

International Nuclear Information System (INIS)

Rauschenbach, B.; Otto, G.; Hohmuth, K.; Heera, V.

1987-01-01

Boron, phosphorus and arsenic ions have been implanted into evaporated iron and nickel thin films at room temperature, and the implantation-induced microstructure has been investigated by high-voltage electron microscopy and transmission high energy electron diffraction. The metal films were implanted with ions to a constant dose of 1 x 10 17 and 5 x 10 17 ions/cm 2 respectively at energy of 50 keV. An amorphous layer was produced by boron and phosphorus ion implantation. Information on the atomic structure of the amorphous layers was obtained from the elastically diffracted electron intensity. On the basis of the correct scattering curves, the total interference function and the pair correlation function were determined. Finally, the atomic arrangement of the implantation-induced amorphous layers is discussed and structure produced by ion irradiation is compared with amorphous structures formed with other techniques. (author)

Corrosion behaviour of high chromium ferritic stainless steels

International Nuclear Information System (INIS)

Kiesheyer, H.; Lennartz, G.; Brandis, H.

1976-01-01

Ferritic steels developed for seawater desalination and containing 20 to 28% chromium, up to 5% Mo and additions of nickel and copper have been tested with respect to their corrosion behaviour, in particular in chloride containing media. The materials in the sensibilized state were tested for intercrystalline corrosion susceptibility in the Strauss-, Streicher-, nitric acid hydrofluoric acid- and Huey-Tests. No intercrystalline corrosion was encountered in the case of the steels with 28% Cr and 2% Mo. The resistance to pitting was assessed on the basis of rupture potentials determined by potentiokinetic tests. The resistance of the steels with 20% Cr and 5% Mo or 28% Cr and 2% Mo is superior to that of the molybdenum containing austenitic types. Addition of nickel yields a significant increase in crevice corrosion resistance; the same applies to resistance in sulfuric acid. In boiling seawater all the materials tested are resistant to stress corrosion cracking. No sign of any type of corrosion was found on nickel containing steels after about 6,000 hours exposure to boiling 50% seawater brine even under salt deposits. (orig.) [de

Equations for nickel-chromium wire heaters of column transfer lines in gas chromatographic-electroantennographic detection (GC-EAD).

Science.gov (United States)

Byers, John A

2004-05-30

Heating of chromatographic columns, transfer lines, and other devices is often required in neuroscience research. For example, volatile compounds passing through a capillary column of a gas chromatograph (GC) can be split, with half exiting the instrument through a heated transfer line to an insect antenna or olfactory sensillum for electroantennographic detector (GC-EAD) recordings. The heated transfer line is used to prevent condensation of various chemicals in the capillary that would otherwise occur at room temperature. Construction of such a transfer line heater is described using (80/20%) nickel-chromium heating wire wrapped in a helical coil and powered by a 120/220 V ac rheostat. Algorithms were developed in a computer program to estimate the voltage at which a rheostat should be set to obtain the desired heater temperature for a specific coil. The coil attributes (radius, width, number of loops, or length of each loop) are input by the user, as well as AWG size of heating wire and desired heater temperature. The program calculates total length of wire in the helix, resistance of the wire, amperage used, and the voltage to set the rheostat. A discussion of semiochemical isolation methods using the GC-EAD and bioassays is presented.

Boron solubility in Fe-Cr-B cast irons

International Nuclear Information System (INIS)

Guo Changqing; Kelly, P.M.

2003-01-01

Boron solubility in the as-cast and solution treated martensite of Fe-Cr-B cast irons, containing approximately 1.35 wt.% of boron, 12 wt.% of chromium, as well as other alloying elements, has been investigated using conventional microanalysis. The significant microstructural variations after tempering at 750 deg. C for 0.5-4 h, compared with the original as-cast and solution treated microstructures, indicated that the matrix consisted of boron and carbon supersaturated solid solutions. The boron solubility detected by electron microprobe was between 0.185-0.515 wt.% for the as-cast martensite and 0.015-0.0589 wt.% for the solution treated martensite, much higher than the accepted value of 0.005 wt.% in pure iron. These remarkable increases are thought to be associated with some metallic alloying element addition, such as chromium, vanadium and molybdenum, which have atomic diameters larger than iron, and expand the iron lattice to sufficiently allow boron atoms to occupy the interstitial sites in iron lattice

In-situ Lead Removal by Iron Nano Particles Coated with Nickel

Directory of Open Access Journals (Sweden)

Mohammadreza Fadaei-tehrani

2016-01-01

Full Text Available This study investigates the potential of nano-zero-valent iron particles coated with nickel in the removal of lead (Pb2+ from porous media. For this purpose, the nano-particles were initially synthesized and later stablilized using the strach biopolymer prior to conducting batch and continuous experiments. The results of the batch experiments revealed that the reaction kinetics fitted well with the pseudo-first-order adsorption model and that the reaction rate ranged from 0.001 to 0.035 g/mg/min depending on solution pH and the molar ratio of Fe/Pb. Continuous experiments showed that lead remediation was mostly influenced not only by seepage velocity but also by the quantity and freshness of nZVI as well as the grain type of the porous media. Maximum Pb2+ removal rates obtained in the batch and lab models were 95% and 80%, respectively. Based on the present study, S-nZVI may be suggested as an efficient agent for in-situ remediation of groundwater contaminated with lead.

Column leaching of chromium and nickel from a contaminated soil using EDTA and citric acid

International Nuclear Information System (INIS)

Jean-Soro, Liliane; Bordas, François; Bollinger, Jean-Claude

2012-01-01

This study investigates the column leaching of a soil contaminated mainly with Cr and Ni by using two chelants: citric acid (biodegradable) and EDTA (non-biodegradable) followed with water rinse. The chelants lead to Cr and Ni leaching, in addition to major elements (Ca, Fe, Mg, Al, Mn and Zn) showing the dissolution of soil mineral constituents. EDTA leaches more major elements and Ni than citric acid related to the respective stability of metal–chelant complexes; citric acid leaches more Cr than EDTA, certainly because of a substitution reaction with Cr(VI). In the case of alternating chelant/water applications, leaching occurs during the chelant applications, but also during water applications. In the case of chelant/water applications followed by continuous water application, both Cr and Ni leach over time. This increased mobility could be due to the residual chelant present in soil as well as to the dissolution/mobilization of mineral or organic soil fractions. - Highlights: ► Column leaching of an industrial soil contaminated with chromium and nickel. ► Citric acid or EDTA were used alternatively or followed with water rinse. ► Chelants lead to Cr and Ni leaching and the dissolution of soil mineral constituents. ► Leaching of these two metals proceeds continuously during water rinse. ► Chelants deeply impacted Cr and Ni mobility. - Citric acid or EDTA application deeply impact Cr and Ni mobility during column leaching of a contaminated soil.

Open Burn/Open Detonation (OBOD) Area Management Using Lime For Explosives Transformation And Metals Immobilization

Science.gov (United States)

2012-01-01

Arsenic Ca Calcium Cd Cadmium Co Cobalt Cr Chromium Cu Copper Fe Iron Mo Molybdenum ERDC/EL TR-12-4 xii Ni Nickel Pb Lead Sb... phytoremediation , reactive barriers, etc.) exist for treatment after the explosive constituents have entered the groundwater or surface water. However, no...Explosives (1,3-dinitrobenzene and nitrobenzene), perchlorate, and inor- ganics ( arsenic , copper, nickel, selenium and zinc) were detected in pre- vious

Filler metal alloy for welding cast nickel aluminide alloys

Science.gov (United States)

Santella, M.L.; Sikka, V.K.

1998-03-10

A filler metal alloy used as a filler for welding cast nickel aluminide alloys contains from about 15 to about 17 wt. % chromium, from about 4 to about 5 wt. % aluminum, equal to or less than about 1.5 wt. % molybdenum, from about 1 to about 4.5 wt. % zirconium, equal to or less than about 0.01 wt. % yttrium, equal to or less than about 0.01 wt. % boron and the balance nickel. The filler metal alloy is made by melting and casting techniques such as are melting the components of the filler metal alloy and cast in copper chill molds. 3 figs.

Radiative properties of stellar envelopes: Comparison of asteroseismic results to opacity calculations and measurements for iron and nickel

International Nuclear Information System (INIS)

Turck-Chieze, S.; Gilles, D.; Le Pennec, M.; Blenski, T.; Thais, F.; Bastiani-Ceccotti, S.; Blancard, C.; Caillaud, T.; Cosse, P.; Faussurier, G.; Gilleron, F.; Pain, J.C.; Reverdin, C.; Silvert, V.; Villette, B.; Busquet, M.; Colgan, J.; Guzik, J.; Kilcrease, D.P.; Magee, N.H.; Delahaye, F.; Zeippen, C.J.; Ducreta, J.E.; Fontes, C.J.; Harris, J.W.; Loisel, G.

2013-01-01

The international OPAC consortium consists of astrophysicists, plasma physicists and experimentalists who examine opacity calculations used in stellar physics that appear questionable and perform new calculations and laser experiments to understand the differences and improve the calculations. We report on iron and nickel opacities for envelopes of stars from 2 to 14 M and deliver our first conclusions concerning the reliability of the used calculations by illustrating the importance of the configuration interaction and of the completeness of the calculations for temperatures around 15-27 eV. (authors)

Principles for prevention of toxic effects from metals

DEFF Research Database (Denmark)

Landrigan, Philip J.; Kotelchuk, David; Grandjean, Philippe

2007-01-01

of the Toxic Effects of Metals Aluminum Antimony Arsenic Barium Beryllium Bismuth Cadmium Chromium Cobalt Copper Gallium and Semiconductor Compounds Germanium Indium Iron Lead Manganese Mercury Molybdenum Nickel Palladium Platinum Selenium Silver Tellurium Thallium Tin Titanium Tungsten Uranium Vanadium Zinc...

Seasonal study on Bothriocephalus as indicator of metal pollution in ...

African Journals Online (AJOL)

... vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, arsenic, selenium, molybdenum, cadmium, tin, antimony, tellurium, barium, mercury, thallium, lead and uranium) were determined with an ICP-MS. Bioconcentration of metals (selenium, mercury, and lead during autumn; copper, zinc, selenium, cadmium, ...

Carbon, chromium and molybdenum contents

International Nuclear Information System (INIS)

Sinatora, A; Goldenstein, H.; Mei, P.R.; Albertin, E.; Fuoco, R.; Mariotto, C.L.

1992-01-01

This work describes solidification experiments on white cast iron, with 15 and 20% of chromium, 2.3, 3.0 and 3.6 % of carbon and 0.0, 1.5 and 2.5 % of molybdenum in test de samples with 30 mm diameter. Measurements were performed on the austenite and eutectic formation arrests, the number of the eutectic carbide particles relative to the total and the eutectic volumes, and the volume fraction of the primary austenite

Interlaboratory comparison survey of the determination of chromium, manganese, iron, titanium in dust and arsenic, cadmium, cobalt and chromium in urine

International Nuclear Information System (INIS)

Christensen, Jytte Molin

2000-01-01

This report describes an intercomparison survey based on the Danish External Quality Assessment Scheme (DEQAS). The study was carried out in 1998 for 10 laboratories in a research project on assessment of levels and health effects of airborne particulate matter in mining, metal refining and metal working industries using nuclear and related analytical techniques. The project was co-ordinated by the IAEA. Eight laboratories measured chromium (Cr), manganese (Mn), iron (Fe) and titanium (Ti) in welding fume dust loaded on filters. Six laboratories measured arsenic (As), four laboratories measured cadmium (Cd), five laboratories measured cobalt (Co) and four laboratories measured chromium (Cr) in urine. The target values of the quality control materials were traceable to certified reference materials with respect to Cr in welding fume and As, Cd, Co and Cr in urine. For Mn, Fe and Ti in welding fume the target values were established based on values from reference laboratories and consensus values from several DEQAS rounds. For evaluating the analytical performance the z-score and E n number were calculated as recommended in ISO 45. The judgement of laboratories according to the performance scores revealed that few laboratories could maintain an ideal z-score below 3 and an ideal E n number below 1. Nearly all participants had a high precision in the reported results. This is a good basis for improvements. The deviations from the target values appear to be systematic, because the deviations for Mn, Fe, Ti in welding dust as well as for As, Cd, Co and Cr in urine were a linear function of the target values (ISO 5725 evaluation). The cause for this bias is unknown at present and might not be the same for all participants. It is necessary to look further into the cause for this bias. Therefore, validation of the methodologies and regularly use of certified reference materials are highly recommended. (author)

Removal of trace metal contaminants from potable water by electrocoagulation

OpenAIRE

Heffron, Joe; Marhefke, Matt; Mayer, Brooke K.

2016-01-01

This study investigated the effects of four operational and environmental variables on the removal of trace metal contaminants from drinking water by electrocoagulation (EC). Removal efficiencies for five metals (arsenic, cadmium, chromium, lead and nickel) were compared under varying combinations of electrode material, post-treatment, water composition and pH. Iron electrodes out-performed aluminum electrodes in removing chromium and arsenic. At pH 6.5, aluminum electrodes were slightly more...

Study of the influence of temperature and time on the electroplating nickel layer in Inconel 718 strips used in spacer grid of Pressurized Water Cooled nuclear reactors (PWR)

Energy Technology Data Exchange (ETDEWEB)

Rezende, Renato; Abati, Amanda; Verne, Júlio; Panossian, Zehbour, E-mail: amanda.abati@marinha.mil.br, E-mail: jvernegropp@gmail.com, E-mail: renato.rezende@marinha.mil.br, E-mail: zep@ipt.br [Centro Tecnológico da Marinha em São Paulo (CTMSP), São Paulo, SP (Brazil). Laboratório de Desenvolvimento e Instrumentação de Combustível Nuclear; Instituto de Pesquisas Tecnológicas (IPT), São Paulo, SP (Brazil)

2017-07-01

The Inconel 718 (UNS N07718: Ni-{sup 19}Cr-{sup 18}Fe-{sup 5}Nb-3 Mo) is a precipitation hardenable nickel alloy that has good corrosion resistance and high mechanical strength. These strips are used for assembling the spacer grid of fuel element of pressurized water cooled nuclear reactors (PWR). The spacer grid is a structural component of fundamental importance in fuel elements of PWR reactors, maintaining the position and necessary spacing of the fuel rods within the arrangement of the fuel element. The spacer grid is formed by joining the points of intersection of the strips, by a joint process called brazing. For this process, these strips are stamped and plated with a thin layer of nickel by means of electroplating in order to protect against oxidation and allow a better flowability and wettability of the addition metal in the strips during brazing. Oxidation at the surface of the base material harms wettability and inhibits spreading of the liquid addition metal on the substrate surface during the brazing process. The use of coatings such as nickel plating is used to ensure such conditions. The results showed that there is a process of diffusion de some chemical elements such as chromium, iron, titanium and aluminum from the substrate to the nickel layer and nickel from the layer to the substrate. These chemical elements are responsible for the oxidation at the surface of the strip. (author)

Relative SHG measurements of metal thin films: Gold, silver, aluminum, cobalt, chromium, germanium, nickel, antimony, titanium, titanium nitride, tungsten, zinc, silicon and indium tin oxide

Directory of Open Access Journals (Sweden)

Franklin Che

Full Text Available We have experimentally measured the surface second-harmonic generation (SHG of sputtered gold, silver, aluminum, zinc, tungsten, copper, titanium, cobalt, nickel, chromium, germanium, antimony, titanium nitride, silicon and indium tin oxide thin films. The second-harmonic response was measured in reflection using a 150 fs p-polarized laser pulse at 1561 nm. We present a clear comparison of the SHG intensity of these films relative to each other. Our measured relative intensities compare favorably with the relative intensities of metals with published data. We also report for the first time to our knowledge the surface SHG intensity of tungsten and antimony relative to that of well known metallic thin films such as gold and silver. Keywords: Surface second-harmonic generation, Nonlinear optics, Metal thin films

Crystallization characteristics of iron-rich glass ceramics prepared from nickel slag and blast furnace slag

Science.gov (United States)

Wang, Zhong-Jie; Ni, Wen; Li, Ke-Qing; Huang, Xiao-Yan; Zhu, Li-Ping

2011-08-01

The crystallization process of iron-rich glass-ceramics prepared from the mixture of nickel slag (NS) and blast furnace slag (BFS) with a small amount of quartz sand was investigated. A modified melting method which was more energy-saving than the traditional methods was used to control the crystallization process. The results show that the iron-rich system has much lower melting temperature, glass transition temperature ( T g), and glass crystallization temperature ( T c), which can result in a further energy-saving process. The results also show that the system has a quick but controllable crystallization process with its peak crystallization temperature at 918°C. The crystallization of augite crystals begins from the edge of the sample and invades into the whole sample. The crystallization process can be completed in a few minutes. A distinct boundary between the crystallized part and the non-crystallized part exists during the process. In the non-crystallized part showing a black colour, some sphere-shaped augite crystals already exist in the glass matrix before samples are heated to T c. In the crystallized part showing a khaki colour, a compact structure is formed by augite crystals.

Study of thermodynamic properties of binary and ternary liquid alloys of aluminium with the elements iron, cobalt, nickel and oxygen; Etude des proprietes thermodynamiques des alliages liquides binaires et ternaires de l'aluminium avec les elements fer, cobalt, nickel et l'oxygene

Energy Technology Data Exchange (ETDEWEB)

Vachet, F [CEA Vallee du Rhone, 26-Pierrelatte (France)

1966-07-01

The present work deals with the thermodynamic study of aluminium liquid alloys with the metals iron, cobalt and nickel. The experiments carried out lead to the activity, at 1600 deg C, of aluminium in the (Al, Fe), (Al, Co), (Al, Ni) liquid alloys. The experimental method used consists in studying the partition of aluminium between the liquid immiscible phases made up with the pairs of metals (Fe, Ag), (Co, Ag), (Ni, Ag). The informations so obtained are used for drawing the isothermal equilibrium phases diagrams sections of (Al, Fe, Ag), (Al, Co, Ag), (Al, Ni, Ag) systems. The study of the partition of silver between lead and aluminium joined with the determinations of several authors allows us to determine the aluminium activity, analytically presented, in the metal M (iron cobalt and nickel). The Wagner's interaction parameters of aluminium in metal M are determined. The results obtained as the equilibrium phases diagrams of (Al, M) systems allow to compare the thermodynamic properties of the Al Fe system in liquid and solid states and to estimate the enthalpies of melting of the AlCo and AlNi intermetallic compounds. The activity, at 1600 deg C, of aluminium in (Al, Fe, Co), (Al, Fe, Ni), (Al, Co, Ni) liquid alloys is estimated through thermodynamic properties of binary components systems by application of several methods leading to results in good agreement. The study of aluminium-oxygen interactions in the liquid metallic solvants M allows us to propose an explanation for the shape of the deoxidation equilibrium line of iron, cobalt and nickel by aluminium and to compare the de-oxidizing power of aluminium toward iron, cobalt and nickel oxides. (author) [French] Le travail presente se rapporte a l'etude thermodynamique des alliages liquides de l'aluminium avec les metaux fer, cobalt et nickel. Les experiences effectuees ont pour but de determiner l'activite, a 1600 C, de l'aluminium dans les alliages liquides (Al, Fe), (Al, Co), (Al, Ni). La methode

Alloys of nickel-iron and nickel-silicon do not swell under fast neutron irradiation

International Nuclear Information System (INIS)

Silvestre, G.; Silvent, A.; Regnard, C.; Sainfort, G.

1975-01-01

This research is concerned with the effect of fast-neutron irradiation on the swelling of nickel and nickel alloys. Ni-Fe (0-60at%Fe) and Ni-Si (0-8at%Si) were studied, and the fluences were in the range 10 20 -4.3x10 22 n/cm 2 . In dilute alloys, the added elements are dissolved and reduce swelling, silicon being particularly effective. In more concentrated alloys, irradiation of Ni-Fe and Ni-Si alloys brings about the formation of plate-shaped precipitates of Ni 3 X and these alloys do not swell. (Auth.)

Determination of the diffusion coefficients of iron and chromium in Pb17Li at 500 deg C

International Nuclear Information System (INIS)

Simon, N.; Flament, T.; Terlain, A.

1992-01-01

The diffusion of the dissolved metallic species in a liquid metal towards the boundary layer is one of the elementary steps of the overall mass transfer process induced by thermal gradient. This phenomenon is very probably the limiting step in the mass transfer of martensitic Fe-Cr steels in the presence of Pb17Li liquid eutectic alloy. For estimating diffusion flux, the diffusion coefficients of iron and chromium in Pb17Li are needed but are not known. Consequently these data have been determined in CEA laboratory by measuring metal loss of cylindrical specimens after rotation at 500 deg C in Pb17Li for several hours and applying the first Fick diffusion law in the boundary layer whose the thickness has been previously determined by EISENBERG. After a description of the experimental device, the results are presented and discussed

Evaluation of heavy metals (Cr, Fe, Ni, Cu, Zn, Cd, Pb and Hg) in water, sediments and water lily (Eichornia crassipes) from Jose Antonio Alzate dam; Evaluacion de metales pesados Cr, Fe, Ni, Cu, Zn, Cd, Pb y Hg en agua, sedimento y lirio acuatico (Eichhornia crassipes) de la Presa Jose Antonio Alzate, Estado de Mexico

Energy Technology Data Exchange (ETDEWEB)

Avila P, P

1996-12-31

Water, sediments and water lily (Eichornia crassipes) from the Jose Antonio Alzate Dam were analyzed in order to determine concentrations of chromium, iron, nickel, copper, zinc, cadmium, lead and mercury. Mercury, lead, chromium and iron were found in concentrations above permissible limits in water, and in high concentrations in sediments. Cadmium, nickel, copper and zinc never were found in concentrations above permissible limits in water. The highest concentrations of heavy metals in water lily were found in the root. Accumulation factors decreased in the following order: Zn> Cr> Fe> Ni> Cu> Pb> Hg and Cd. Statistical differences ({alpha} < 0.5) between the collection samples dates was observed. High correlations between metals concentrations in superficial water, sediment and water hyacinth were also observed. These correlations could indicate that the heavy metals studied here, are originated from a natural source such as sediments or from an industrial source. (Author).

Investigation of mangrove macroalgae as biomonitors of estuarine metal contamination

Energy Technology Data Exchange (ETDEWEB)

Melville, Felicity [Department of Environmental Sciences/Institute of Water and Environmental Resource Management, University of Technology, Sydney, PO Box 123, Broadway NSW 2007 (Australia)], E-mail: f.melville@cqu.edu.au; Pulkownik, Alex [Department of Environmental Sciences/Institute of Water and Environmental Resource Management, University of Technology, Sydney, PO Box 123, Broadway NSW 2007 (Australia)

2007-11-15

This study examined the potential use of macroalgae epiphytic on mangrove aerial roots as biomonitors of estuarine contamination. The metal concentrations of macroalgae were investigated in four estuaries in the vicinity of Sydney, Australia, and compared to water and sediment metal concentrations over three seasonal surveys. Macroalgal metal concentrations (copper, zinc, cadmium, chromium, lead, nickel, manganese and iron) appeared to be more associated with sediment metal concentrations than water concentrations, suggesting they may be useful biomonitors of estuarine sediment contamination. Algae in the more contaminated estuaries generally contained higher metal concentrations. However, concentrations of iron, nickel and manganese appeared to be similar in the algae despite the varying sediment concentrations, while accumulation of copper, zinc, lead and chromium appeared to be associated with ambient environmental concentrations. The uptake of metals also varied among the different species, suggesting that algal parameters, such as morphology, may also influence metal uptake and accumulation.

Evaluation of heavy metals (Cr, Fe, Ni, Cu, Zn, Cd, Pb and Hg) in water, sediments and water lily (Eichornia crassipes) from Jose Antonio Alzate dam

International Nuclear Information System (INIS)

Avila P, P.

1995-01-01

Water, sediments and water lily (Eichornia crassipes) from the Jose Antonio Alzate Dam were analyzed in order to determine concentrations of chromium, iron, nickel, copper, zinc, cadmium, lead and mercury. Mercury, lead, chromium and iron were found in concentrations above permissible limits in water, and in high concentrations in sediments. Cadmium, nickel, copper and zinc never were found in concentrations above permissible limits in water. The highest concentrations of heavy metals in water lily were found in the root. Accumulation factors decreased in the following order: Zn> Cr> Fe> Ni> Cu> Pb> Hg and Cd. Statistical differences (α < 0.5) between the collection samples dates was observed. High correlations between metals concentrations in superficial water, sediment and water hyacinth were also observed. These correlations could indicate that the heavy metals studied here, are originated from a natural source such as sediments or from an industrial source. (Author)

Residues of chromium, nickel, cadmium and lead in Rook Corvus frugilegus eggshells from urban and rural areas of Poland.

Science.gov (United States)

Orłowski, Grzegorz; Kasprzykowski, Zbigniew; Dobicki, Wojciech; Pokorny, Przemysław; Wuczyński, Andrzej; Polechoński, Ryszard; Mazgajski, Tomasz D

2014-08-15

We examined the concentrations of chromium (Cr), nickel (Ni), cadmium (Cd) and lead (Pb) in Rook Corvus frugilegus eggshells from 43 rookeries situated in rural and urban areas of western (=intensive agriculture) and eastern (=extensive agriculture) Poland. We found small ranges in the overall level of Cr (the difference between the extreme values was 1.8-fold; range of concentrations=5.21-9.40 Cr ppm), Ni (3.5-fold; 1.15-4.07 Ni ppm), and Cd (2.6-fold; 0.34-0.91 Cd ppm), whereas concentrations of Pb varied markedly, i.e. 6.7-fold between extreme values (1.71-11.53 Pb ppm). Eggshell levels of these four elements did not differ between rural rookeries from western and eastern Poland, but eggshells from rookeries in large/industrial cities had significantly higher concentrations of Cr, Ni and Pb than those from small towns and villages. Our study suggests that female Rooks exhibited an apparent variation in the intensity of trace metal bioaccumulation in their eggshells, that rapid site-dependent bioaccumulation of Cu, Cr, Ni and Pb occurs as a result of the pollution gradient (ruralsoil environment. Copyright © 2014 Elsevier B.V. All rights reserved.

Quantitative analysis of nickel in zirconium and zircaloy

International Nuclear Information System (INIS)

Rastoix, M.

1957-01-01

A rapid spectrophotometric has been developed for determination of 10 to 1000 ppm of Ni in zirconium and zircaloy using dimethylglyoxime. Iron, copper, tin and chromium, do not interfere at the concentration usually present in zirconium and its alloys. (author) [fr

Solubility of nickel ferrite (NiFe2O4) from 100 to 200 deg. C

International Nuclear Information System (INIS)

Bellefleur, Alexandre; Bachet, Martin; Benezeth, Pascale; Schott, Jacques

2012-09-01

The solubility of nickel ferrite was measured in a Hydrogen-Electrode Concentration Cell (HECC) at temperatures of 100 deg. C, 150 deg. C and 200 deg. C and pH between 4 and 5.25. The experimental solution was composed of HCl and NaCl (0.1 mol.L -1 ). Based on other studies ([1,2]), pure nickel ferrite was experimentally synthesized by calcination of a mixture of hematite Fe 2 O 3 and bunsenite NiO in molten salts at 1000 deg. C for 15 hours in air. The so obtained powder was fully characterized. The Hydrogen-Electrode Concentration cell has been described in [3]. It allowed us to run solubility experiments up to 250 deg. C with an in-situ pH measurement. To avoid reduction of the solid phase to metallic nickel, a hydrogen/argon mixture was used instead of pure hydrogen. Consequently, the equilibration time for the electrodes was longer than with pure hydrogen. Eight samples were taken on a 70 days period. After the experiments, the powder showed no significant XRD evidence of Ni (II) reduction. Nickel concentration was measured by atomic absorption spectroscopy and iron concentration was measured by UV spectroscopy. The protocol has been designed to be able to measure both dissolved Fe (II) and total iron. The nickel solubility of nickel ferrite was slightly lower than the solubility of nickel oxide in close experimental conditions [3]. Dissolved iron was mainly ferrous and the solution was under-saturated relative to both hematite and magnetite. The nickel/iron ratio indicated a non-stoichiometric dissolution. The solubility measurements were compared with equilibrium calculations using the MULTEQ database. [1] Hayashi et al (1980) J. Materials Sci. 15, 1491-1497. [2] Ziemniak et al (2007) J. Physics and Chem. of Solids. 68,10-21. [3] EPRI Report 1003155 (2002). (authors)

Electrical Resistivity of Chromium, Cobalt, Iron, and Nickel.

Science.gov (United States)

1982-06-01

set 43), which appeared to have a change of slope at � K. At temperatures above the Curie temperature, the data of Seydel and Fucke (871 (data...of Seydel and Fucke [871 (data set 42) agree to within ±1%. In addition, their data for the solid phase at the melting point agree to within ±1.5% of...of Seydel and Fucke (87] (data set 205) which were obtained by a pulse-heated exploding wire technique show that the linear dependence is applicable

Composition tunable cobalt–nickel and cobalt–iron alloy nanoparticles below 10 nm synthesized using acetonated cobalt carbonyl

International Nuclear Information System (INIS)

Schooneveld, Matti M. van; Campos-Cuerva, Carlos; Pet, Jeroen; Meeldijk, Johannes D.; Rijssel, Jos van; Meijerink, Andries; Erné, Ben H.; Groot, Frank M. F. de

2012-01-01

A general organometallic route has been developed to synthesize Co x Ni 1−x and Co x Fe 1−x alloy nanoparticles with a fully tunable composition and a size of 4–10 nm with high yield. In contrast to previously reported synthesis methods using dicobalt octacarbonyl (Co 2 (CO) 8 ), here the cobalt–cobalt bond in the carbonyl complex is first broken with anhydrous acetone. The acetonated compound, in the presence of iron carbonyl or nickel acetylacetonate, is necessary to obtain small composition tunable alloys. This new route and insights will provide guidelines for the wet-chemical synthesis of yet unmade bimetallic alloy nanoparticles.

Rapid nickel diffusion in cold-worked carbon steel at 320-450 °C

Science.gov (United States)

Arioka, Koji; Iijima, Yoshiaki; Miyamoto, Tomoki

2015-11-01

The diffusion coefficient of nickel in cold-worked carbon steel was determined with the diffusion couple method in the temperature range between 320 and 450 °C. Diffusion couple was prepared by electro-less nickel plating on the surface of a 20% cold-worked carbon steel. The growth in width of the interdiffusion zone was proportional to the square root of diffusion time to 12,000 h. The diffusion coefficient (DNi) of nickel in cold-worked carbon steel was determined by extrapolating the concentration-dependent interdiffusion coefficient to 0% of nickel. The temperature dependence of DNi is expressed by DNi = (4.5 + 5.7/-2.5) × 10-11 exp (-146 ± 4 kJ mol-1/RT) m2s-1. The value of DNi at 320 °C is four orders of magnitude higher than the lattice diffusion coefficient of nickel in iron. The activation energy 146 kJ mol-1 is 54% of the activation energy 270.4 kJ mol-1 for lattice diffusion of nickel in the ferromagnetic state iron.

Structural, optical and dielectric properties of pure and chromium (Cr) doped nickel oxide nanoparticles

Science.gov (United States)

Gupta, Jhalak; Ahmed, Arham S.

2018-05-01

The pure and Cr doped nickel oxide (NiO) nanoparticles have been synthesized by cost effective co-precipitation method having nickel nitrate as initial precursor. The synthesized samples were characterized by X-Ray diffraction (XRD), UV-Visible Spectroscopy(UV-Vis) and LCR meter for structural, optical and dielectric properties respectively. The crystallite size of pure nickel oxide nanoparticles characterized by XRD using Debye Scherer's formula was found to be 21.7nm and the same decreases on increasing Cr concentration whereas optical and dielectric properties were analyzed by UV-Vis and LCR meter respectively. The energy band gaps were determined by UV-Vis using Tauc relation.

Levels of heavy metals in Gubi dam water Bauchi, Nigeria | Wufem ...

African Journals Online (AJOL)

Global Journal of Environmental Sciences ... The average concentrations of iron, manganese, nickel, zinc, cobalt, chromium and cadmium were generally highest in filtrate water, whereas the concentrations of copper and lead were always highest in the suspended materials which indicate the dominant role played by ...

Biological recovery of metals, sulfur and water in the mining and metallurgical industry

NARCIS (Netherlands)

Weijma, J.; Copini, C.F.M.; Buisman, C.J.N.; Schultz, C.E.

2002-01-01

Metals of particular interest in acid mine drainage and industrial wastewaters include copper, zinc, cadmium, arsenic, manganese, aluminum, lead, nickel, silver, mercury, chromium, uranium and iron, in a concentration that can range from 106 to 102 g/l. The composition of such wastewater reflects

Segregation effects and phase developments during solidification of alloy 625

DEFF Research Database (Denmark)

Højerslev, Christian; Tiedje, Niels Skat; Hald, John

2006-01-01

contained gamma-phase, Laves phase and, if carbon was dissolved in the liquid, niobium rich carbides formed. Molybdenum and niobium showed strong tendencies to segregate. Their segregation was balanced by inverse segregation of nickel and iron. The chromium concentration remained almost constant in gamma...

Heavy metals burden of Keenjhar Lake, District Thatta, Sindh, Pakistan

African Journals Online (AJOL)

Detection of heavy metals (HMs) content from Keenjhar Lake water was carried out monthly from January to December, 2003. Zinc, chromium, copper, iron, manganese, nickel and cadmium were analyzed by dual mode of analytical methods flame atomic absorption spectrometry and electrothermal atomic absorption ...

Toxic elements and speciation in seafood samples from different contaminated sites in Europe

NARCIS (Netherlands)

Maulvault, A.L.; Anacleto, P.; Barbosa, V.; Sloth, J.J.; Rasmussen, R.; Tediosi, A.; Fernandez-Tejedor, M.; Heuvel, F.H.M.; Kotterman, M.J.J.; Marques, A.

2015-01-01

The presence of cadmium (Cd), lead (Pb), mercury (THg), methylmercury (MeHg), arsenic (TAs), inorganic arsenic (iAs), cobalt (Co), copper (Cu), zinc (Zn), nickel (Ni), chromium (Cr) and iron (Fe) was investigated in seafood collected from European marine ecosystems subjected to strong anthropogenic

Low-temperature CVD of iron, cobalt, and nickel nitride thin films from bis[di(tert-butyl)amido]metal(II) precursors and ammonia

International Nuclear Information System (INIS)

Cloud, Andrew N.; Abelson, John R.; Davis, Luke M.; Girolami, Gregory S.

2014-01-01

Thin films of late transition metal nitrides (where the metal is iron, cobalt, or nickel) are grown by low-pressure metalorganic chemical vapor deposition from bis[di(tert-butyl)amido]metal(II) precursors and ammonia. These metal nitrides are known to have useful mechanical and magnetic properties, but there are few thin film growth techniques to produce them based on a single precursor family. The authors report the deposition of metal nitride thin films below 300 °C from three recently synthesized M[N(t-Bu) 2 ] 2 precursors, where M = Fe, Co, and Ni, with growth onset as low as room temperature. Metal-rich phases are obtained with constant nitrogen content from growth onset to 200 °C over a range of feedstock partial pressures. Carbon contamination in the films is minimal for iron and cobalt nitride, but similar to the nitrogen concentration for nickel nitride. X-ray photoelectron spectroscopy indicates that the incorporated nitrogen is present as metal nitride, even for films grown at the reaction onset temperature. Deposition rates of up to 18 nm/min are observed. The film morphologies, growth rates, and compositions are consistent with a gas-phase transamination reaction that produces precursor species with high sticking coefficients and low surface mobilities

Physical models of mass transport of iron and nickel in liquid sodium systems

International Nuclear Information System (INIS)

Davies, B.S.J.; Polley, M.V.; Skyrme, G.

1975-12-01

Experimental observations on corrosion of pure iron and nickel specimens in non-isothermal loops containing flowing sodium have been used to derive values of the concentration of dissolved material at the entrance to the test section and diffusion coefficients of the test material in sodium. The former values differ from the saturation value by only 10 -3 ppm, which is small compared to currently recommended solubility values. The phenomenon cannot be explained in terms of circulating particles. Two other possible explanations are also dismissed. The diffusion coefficient values are consistent with the corroding species being atoms, or molecules containing a few atoms. It is also shown that the observations are better explained in terms of boundary layer controlled mass transfer, rather than a surface controlled process. A computer model based on an alternative solubility relationship is shown to produce results which describe well the observed variation of corrosion rate with oxygen concentration, sodium velocity and downstream position. (author)

Criticality of iron and its principal alloying elements.

Science.gov (United States)

Nuss, Philip; Harper, E M; Nassar, N T; Reck, Barbara K; Graedel, T E

2014-04-01

Because modern technology depends on reliable supplies of a wide variety of materials and because of increasing concern about those supplies, a comprehensive methodology was created to quantify the degree of criticality of the metals of the periodic table. In this paper, we apply this methodology to iron and several of its main alloying elements (i.e., vanadium, chromium, manganese, and niobium). These elements represent the basic metals of any industrial society and are vital for national security and economic well-being. Assessments relating to the dimensions of criticality - supply risk, vulnerability to supply restriction, and environmental implications - for 2008 are made on the global level and for the United States. Evaluations of each of the multiple indicators are presented, with aggregate results plotted in "criticality space", together with Monte Carlo simulation-derived "uncertainty cloud" estimates. Iron has the lowest supply risk, primarily because of its widespread geological occurrence. Vanadium displays the highest cradle-to-gate environmental implications, followed by niobium, chromium, manganese, and iron. Chromium and manganese, both essential in steel making, display the highest vulnerability to supply restriction, largely because substitution or substitution at equal performance is not possible for all end-uses. From a comprehensive perspective, we regard the overall criticality as low for iron and modest for the alloying elements we evaluated.

Microwave absorption properties of the core/shell-type iron and nickel nanoparticles

Science.gov (United States)

Lu, B.; Dong, X. L.; Huang, H.; Zhang, X. F.; Zhu, X. G.; Lei, J. P.; Sun, J. P.

Iron (Fe) and nickel (Ni) nanoparticles were prepared by the DC arc-discharge method in a mixture of hydrogen and argon gases, using bulk metals as the raw materials. The microstructure of core/shell (metal/metal oxide) in nanoparticle formed after in situ passivation process. The complex electromagnetic parameters (permittivity ɛ=ɛr'+iɛr″ and permeability μ=μr'+iμr″) of the paraffin-mixed nanocomposite samples (paraffin:nanoparticles=1:1 in mass ratio) were measured in the frequency range of 2-18 GHz. The polarization mechanisms of the space charge and dipole coexist in both the Fe and Ni nanoparticles. The orientational polarization is a particular polarization for Fe nanoparticles and brings a relatively higher dielectric loss. Natural resonance is the main reason for magnetic loss and the corresponding frequencies are 11.6 and 5.2 GHz for the Fe and Ni nanoparticles, respectively. The paraffin composite with Fe nanoparticles provided excellent microwave absorption properties (reflection loss <-20 dB) in the range 6.8-16.6 GHz over the absorber thickness of 1.1-2.3 mm.

TEM investigations on the effect of chromium content and of stress relief treatment on precipitation in Alloy 82

International Nuclear Information System (INIS)

Sennour, M.; Chaumun, E.; Crépin, J.; Duhamel, C.; Gaslain, F.; Guerre, C.; Curières, I. de

2013-01-01

Highlights: •Slight change of the Cr content does not affect the microstructure of the butt welds. •Stress relief thermal treatment leads to the intergranular precipitation of Cr 23 C 6 . •The Cr 23 C 6 carbides are supposed to improve the SCC resistance of the butt welds. -- Abstract: Nickel-base alloys are widely used in nuclear Pressurized Water Reactors (PWRs). Most of them have been found susceptible to Stress Corrosion Cracking (SCC) in nominal PWR primary water. The time to initiation depends on the material and is longer for weld metals than for Alloy 600. This study will focus on Alloy 82, which is used in Dissimilar Metal Welds (DMWs). In service, DMWs are either in the as-welded state or have undergone a stress relief treatment. Previous SCC studies showed that the heat treatment reduces significantly the SCC susceptibility of the weld. In this context, this study focuses on the microstructure characterization of the weld in the as-welded state and in the heat-treated state. As chromium content is also a key factor for the SCC susceptibility, welds with low chromium content and medium chromium content were studied. The lower SCC susceptibility of the heat-treated welds was attributed to intergranular Cr 23 C 6 resulting from a combined effect of heat treatment and chromium and carbon contents. These intergranular carbides could explain the better behavior of Alloy 82, compared to other nickel-base alloys

Backfill barriers: the use of engineered barriers based on geologic materials to assure isolation of radioactive wastes in a repository. [Nickel-iron alloys

Energy Technology Data Exchange (ETDEWEB)

Apps, J.A.; Cook, N.G.W.

1981-06-01

A preliminary assessment is made to show that canisters fabricated of nickel-iron alloys, and surrounded by a suitable backfill, may produce an engineered barrier where the canister material is thermodynamically stable with respect to its environment. As similar conditions exist in nature, the performance of such systems as barriers to isolate radionuclides can be predicted over very long periods, of the order of 10/sup 6/ years.

Economical characteristics of base types of minerals. 1. Metallic minerals

International Nuclear Information System (INIS)

Khasanov, A.Kh.

1990-01-01

Metallic minerals is raw materials base of black and colour metallurgy. In this article of book author describes the group of black metals (iron, manganese, chromium), group of tempers (titanium, vanadium, nickel, cobalt, molybdenum, tungsten), colour metals (copper, lead, zinc, aluminium, tin, mercury, antimony, bismuth) and etc.

Relation between the degree of lung pollution by air pollution and heavy metals

Energy Technology Data Exchange (ETDEWEB)

Kawai, H; Endo, R; Takemoto, K

1975-04-01

Human and dog lungs were analyzed for 13 kinds of heavy metals. The human lungs (all of Tokyo citizens) showed a broad range of dust sedimentation, some correlation between the degree of pollution and the amount of cadmium, nickel, and chromium only, and conspicuous individual differences seemingly due to occupation. No correlation was found between the amount of pulmonary metals, and age, or sex. In dog lungs there was no correlation between the local pollution and the amount of iron, copper, zinc, cobalt, and cadmium. Cadmium, nickel, lead, and chromium showed a correlation between local air pollution in human lungs. In dogs obtained in Korea, Ni and Cr were higher than in dog lungs obtained in Jinsen.

Anodic characteristics and stress corrosion cracking behavior of nickel rich alloys in bicarbonate and buffer solutions

International Nuclear Information System (INIS)

Zadorozne, Natalia S.; Giordano, Mabel C.; Ares, Alicia E.; Carranza, Ricardo M.; Rebak, Raul B.

2016-01-01

Highlights: • We investigate which element in alloy C-22 may be responsible for the cracking susceptibility of the high nickel alloy. • Six nickel based alloys with different amount of Cr and Mo were selected for the electrochemical tests and response to SSRT. • Polarization tests showed that an anodic peak appear in the passive region in Cr containing alloys. • Cracking of Ni alloys in carbonate solutions seem to be a consequence of the instability of the passivating chromium oxide. • Alloys containing both Cr and Mo have the highest susceptibility. - Abstract: The aim of this work is to investigate which alloying element in C-22 is responsible for the cracking susceptibility of the alloy in bicarbonate and two buffer solutions (tungstate and borate). Six nickel based alloys, with different amount of chromium (Cr) and molybdenum (Mo) were tested using electrochemical methods and slow strain rate tests (SSRT) at 90 °C. All Cr containing alloys had transgranular cracking at high anodic potential; however, C-22 containing high Cr and high Mo was the most susceptible alloy to cracking. Bicarbonate was the most aggressive of three tested environments of similar pH.

Bottom concentrations Determination of particle material in suspension in Medellin City

International Nuclear Information System (INIS)

Echeverri Londono, Carlos Alberto

2000-01-01

The aim of this work is at achieving a better understanding of background concentrations of particle materials in suspension (pst) in Medellin. This will allow certain actions and programs for watching and controlling air pollution in this city. Metals analyzed in particle material were: calcium, chromium, copper, iron, magnesium, nickel and lead. Chromium and nickel were not detected in any station and lead was detected in one station only. It is observed that all metals have a large dispersion, excepting total iron in La America and magnesium in point 2 at Belencito, which demonstrates the high temporal variability of these metals in these places. also It is observed that metals do not have a homogenous variation in their breathable fraction (encountered in pm-10) in relation to the total metals (encountered in PST) which is indication of the different sources contribution to the metals concentration and, in general, of PST and PM - 10

Improvement of solvents for chemical decontamination: nickel ferrites removal

International Nuclear Information System (INIS)

Figueroa, Carlos A.; Morando, Pedro J.; Blesa, Miguel A.

1999-01-01

Carboxylic acids are usually included in commercial solvents for the chemical cleaning and decontamination of metal surfaces from the oxide layers grown and/or deposited from high temperature water by corrosive process. In particular oxalic acid is included in second path of AP-Citrox method. However, in some cases, their use shows low efficiency. This fact is attributed to the special passivity of the mixed oxides as nickel ferrites. This work reports a kinetic study of dissolution of a synthetic nickel ferrite (NiFe 2 O 4 ) confronted with simple oxides (NiO and Fe 2 O 3 ) in mineral acids and oxalic acid. The dissolution factor and reaction rate were determined in several conditions (reactive concentrations, pH and added ferrous ions). Experimental data of dissolution (with and without Fe(II) added) show a congruent kinetic regime. Pure nickel oxide (NiO) is rather resistant to the attack by oxalic acid solutions, and ferrous ions do not accelerate dissolution. In fact, nickel oxide dissolves better by oxidative attack that takes advantage of the higher lability of Ni 3+ . It may be concluded that oxalic acid operates to dissolve iron, and the ensuing disruption of the solid framework accelerates the release of nickel. Our results point to use more reactive solvents in iron from mixed oxides and to the possibility of using one stage decontamination method. (author)

Mechanical-thermal synthesis of chromium carbides

International Nuclear Information System (INIS)

Cintho, Osvaldo Mitsuyuki; Favilla, Eliane Aparecida Peixoto; Capocchi, Jose Deodoro Trani

2007-01-01

The present investigation deals with the synthesis of chromium carbides (Cr 3 C 2 and Cr 7 C 3 ), starting from metallic chromium (obtained from the reduction of Cr 2 O 3 with Al) and carbon (graphite). The synthesis was carried out via high energy milling, followed by heat-treating of pellets made of different milled mixtures at 800 o C, for 2 h, under an atmosphere of argon. A SPEX CertPrep 8000 Mixer/Mill was used for milling under argon atmosphere. A tool steel vat and two 12.7 mm diameter chromium steel balls were used. The raw materials used and the products were characterized by differential thermal analysis, thermo gravimetric analysis, X-ray diffraction, electronic microscopy and X-ray fluorescence chemical analysis. The following variables were investigated: the quantity of carbon in the mixture, the milling time and the milling power. Mechanical activation of the reactant mixture depends upon the milling power ratio used for processing. The energy liberated by the reduction of the chromium oxide with aluminium exhibits a maximum for milling power ratio between 5:1 and 7.5:1. Self-propagating reaction occurred for all heat-treated samples whatever the carbon content of the sample and the milling power ratio used. Bearing carbon samples exhibited hollow shell structures after the reaction. The level of iron contamination of the milled samples was kept below 0.3% Fe. The self-propagated reaction caused high temperatures inside the samples as it may be seen by the occurrence of spherules, dendrites and whiskers. The carbon content determines the type of chromium carbide formed

Studies on heavy metal contamination in Godavari river basin

Science.gov (United States)

Hussain, Jakir; Husain, Ikbal; Arif, Mohammed; Gupta, Nidhi

2017-12-01

Surface water samples from Godavari river basin was analyzed quantitatively for the concentration of eight heavy metals such as arsenic, cadmium, chromium, copper, iron, lead, nickel and zinc using atomic absorption spectrophotometer. The analyzed data revealed that iron and zinc metals were found to be the most abundant metals in the river Godavari and its tributaries. Iron (Fe) recorded the highest, while cadmium (Cd) had the least concentration. Arsenic, cadmium, chromium, iron and zinc metals are within the acceptable limit of BIS (Bureau of Indian Standards (BIS) 1050 (2012) Specification for drinking water, pp 1-5). The analysis of Godavari river and its tributary's water samples reveals that the water is contaminated at selected points which are not suitable for drinking. Nickel and Copper concentration is above acceptable limit and other metal concentration is within the acceptable limit. Comprehensive study of the results reveals that out of 18 water quality stations monitored, water samples collected at 7 water quality stations are found to be within the permissible limit for all purposes. While Rajegaon, Tekra, Nandgaon, P. G. Bridge, Bhatpalli, Kumhari, Pauni, Hivra, Ashti, Bamini, and Jagda stations were beyond the desirable limit due to presence of copper and nickel metals. The contents of copper metal ions were higher at some water quality stations on Wunna river (Nandgaon); Wardha river (Hivra) and Wainganga river (Kumhari, Pauni, Ashti) during Feb. 2012, while nickel concentration during Feb. 2012, June 2012, March 2013 and Aug. 2013 at some water quality stations on rivers Bagh, Indravati, Pranhita, Wunna, Penganga, Peddavagu, Wainganga and Wardha. It can be concluded that rapid population growth and industrialization have brought about resource degradation and a decline in environmental quality.

Synthesis and Ligand Non-Innocence of Thiolate-Ligated (N4S) Iron(II) and Nickel(II) Bis(imino)pyridine Complexes

Science.gov (United States)

Widger, Leland R.; Jiang, Yunbo; Siegler, Maxime; Kumar, Devesh; Latifi, Reza; de Visser, Sam P.; Jameson, Guy N.L.; Goldberg, David P.

2013-01-01

The known iron(II) complex [FeII(LN3S)(OTf)] (1) was used as starting material to prepare the new biomimetic (N4S(thiolate)) iron(II) complexes [FeII(LN3S)(py)](OTf) (2) and [FeII(LN3S)(DMAP)](OTf) (3), where LN3S is a tetradentate bis(imino)pyridine (BIP) derivative with a covalently tethered phenylthiolate donor. These complexes were characterized by X-ray crystallography, UV-vis, 1H NMR, and Mössbauer spectroscopy, as well as electrochemistry. A nickel(II) analogue, [NiII(LN3S)](BF4) (5), was also synthesized and characterized by structural and spectroscopic methods. Cyclic voltammetric studies showed 1 – 3 and 5 undergo a single reduction process with E1/2 between −0.9 to −1.2 V versus Fc+/Fc. Treatment of 3 with 0.5% Na/Hg amalgam gave the mono-reduced complex [Fe(LN3S)(DMAP)]0 (4), which was characterized by X-ray crystallography, UV-vis, EPR (g = [2.155, 2.057, 2.038]) and Mössbauer (δ = 0.33 mm s−1; ΔEQ = 2.04 mm s−1) spectroscopies. Computational methods (DFT) were employed to model complexes 3 – 5. The combined experimental and computational studies show that 1 – 3 are 5-coordinate, high-spin (S = 2) FeII complexes, whereas 4 is best described as a 5-coordinate, intermediate-spin (S = 1) FeII complex antiferromagnetically coupled to a ligand radical. This unique electronic configuration leads to an overall doublet spin (Stotal = ½) ground state. Complexes 2 and 3 are shown to react with O2 to give S-oxygenated products, as previously reported for 1. In contrast, the mono-reduced 4 appears to react with O2 to give a mixture of S- and Fe-oxygenates. The nickel(II) complex 5 does not react with O2, and even when the mono-reduced nickel complex is produced, it appears to undergo only outer-sphere oxidation with O2. PMID:23992096

Polymeric precursors method for obtaining pigments based on Inorganic oxides of chromium and iron deposited on TiO{sub 2}; Metodo dos precursores polimericos para obtencao de pigmentos inorganicos a base de oxidos de cromo e de ferro, depositados sobre TiO{sub 2}

Energy Technology Data Exchange (ETDEWEB)

NONE

2011-07-01

The case study was the use of chromium oxides and iron, as a precursor in the synthesis of inorganic pigments. The synthesis was based on the dissolution of citric acid as a complexing agent, addition of metal oxides, such as ion chromophores; polymerization with ethylene glycol and doping with titanium oxide. Going through pre-calcination, breakdown, calcination at different temperatures (700, 900 and 1100 deg C resulting in pigments: green for pigment and chromium deposited on TiO2, orange for iron on TiO2. The thermal analysis (TG and DTA), evaluated their thermal decompositions, the XRD revealed the formation of crystalline phases such as iron titanate and chrome titanate; SEM showed the formation of hexagonal particles for both oxides. Under the different analysis, one can see the potential stability of pigments and powders, can be proposed its use as pigments in polymers. (author)

Chromium depletion on the surface of nickel based alloys

International Nuclear Information System (INIS)

Dille, E.R.; McDonald, J.L.; Berry, P.

1988-01-01

Successful selection of corrosion resistant materials for flue gas desuflurization applications is tricky business at best. Most simulated, accelerated, concentrated corrosion tests try to rank materials to known corrosive condition. If you check the actual data, occasionally you find anomalies such as highly corrosion resistant materials performing below what was expected, while the rest of the group is performing normally. In the field the authors have observed similar results with few acceptable explanations. Recently the authors have found numerous cases of Ni/Cr/Mo alloys with a surface analysis below the ASTM specified range for the element chromium. These surface analysis have been done with a portable X-ray Fluorescent Instrument with the initial results confirmed by an independent laboratory

Persistent pollution of Warta river catchment with chromium: case study from central Poland

Science.gov (United States)

Hermanski, S.; Lukaczynski, I.; Nikiel, G.; Mizera, J.; Dulinski, M.; Kania, J.; Rozanski, K.; Szklarczyk, T.; Wachniew, P.; Witczak, S.; Zurek, A.

2012-04-01

Upper reaches of the Warta river, the third largest river in Poland, are located in a densely populated and industrialized area, with presence of heavy industry going back to the second half of the XIX century. Industrial activities include iron smelters in towns of Częstochowa and Zawiercie, large chemical plants (Rudniki and Aniolow) producing predominantly chromium compounds, paper and textile industry, as well as large number of small enterprises specialized in metal coatings (nickel and chromium). Until the 1960s all the industrial and municipal effluents in the region were discharged into the Warta river and its tributaries. Solid wastes were dumped on the surface, mostly without appropriate cover and isolation. This resulted in progressive contamination of surface waters and groundwater with heavy metals, mostly chromium. The upper reaches of the Warta river are located on top of upper Jurassic Major Groundwater Basin (MGWB 326 which is one of four most important groundwater reservoirs in Poland. Almost all potable water demands in the area (ca. 340,000 inhabitants, 800 factories and enterprises) are covered by MGWB 326 (50 deep wells with the average extraction rate of 57,000 m3/d). As the MGWB 326 is mostly phreatic, it has been recognized since long time that persistent pollution of the upper catchment of the Warta river with heavy metals may pose serious thread to quality of this important groundwater resource. In this presentation we summarize the work carried out to date, focused on characterization of the extent and understanding of the mechanisms of pollution of surface water, sediments and groundwater in MGWB 326 with chromium. Historical monitoring data of the levels of chromium in the Warta river and its tributaries are presented, supplemented by the results of measurements of Cr loads in Warta over-bank deposits and Cr levels in groundwater production wells in the area. Three conceptual models of spreading of chromium in the catchment of Warta

DETERMINATION OF METAL IONS RELEASED BY STAINLESS ...

African Journals Online (AJOL)

The amounts of cobalt, iron, manganese, nickel and chromium ions released from new and reused stainless steel arch bar used for maxillomandibular fixation was determined in Hank's solutions of different hydrogen and chloride ions concentrations, whole blood serum and phosphate buffered saline (PBS) in vitro, over a ...

Analysis of corrosions-products in tissue samples near surgical implants by means of LAMMA (Laser Microprobe Mass Analyzer) and ICP-MS (Inductively Coupled Plasma Mass Spectrometer)

International Nuclear Information System (INIS)

Schlagenhaufen, C.

1996-08-01

In this work corrosion products of surgical implants in tissue samples were identified. For the characterization of the corrosion products the LAMMA 500 (Laser Microprobe Mass Analyzer) was used. Additional analysis were made with the ICP-MS (Inductively Coupled Plasma Mass Spectrometer) to determine the concentration of chromium, cobalt, nickel, and molybdenum in the tissues. In the first part several synthetic chromium- and molybdenum compounds were investigated with LAMMA. With the anionic mass spectra of the chromium-compounds it is possible to the oxidation state of chromium. The mass spectra of the synthetic compounds were used to identify, the compounds in the corrosion products. In the second part thin sections prepared from the tissue samples from the surrounding of the implants were analyzed. Several embedding and cutting methods were tested. Histological staining methods and LAMMA spectra were used to characterize the deposits in the tissue. Three different deposits were found in the tissue. In all tissues metal splinters from the implant were found. In most of the tissues iron-rich deposits were found, that were identified as iron-phosphate. As definitive corrosion products of the implant mixtures of chromium(III)phosphate, calcium molybdate, calcium phosphate and chromium(III) molybdate were identified. The ICP-MS results show in comparison to normal values, very high concentrations for chromium, nickel, cobalt and molybdenum. These results support the conclusions based on LAMMA results. The results of these investigations clearly indicate, that stainless steel implants, are not corrosion-resistant in the body. Relatively high amounts of the constituents, of the implant dissolved, and are deposited as solid compounds in the tissue next to the implant. (author)

Discontinuous precipitation in a nickel-free high nitrogen austenitic stainless steel on solution nitriding

DEFF Research Database (Denmark)

Mohammadzadeh, Roghayeh; Akbari, Alireza; Grumsen, Flemming Bjerg

2017-01-01