Structural and functional intermetallics - an overview

International Nuclear Information System (INIS)

Varin, R.A.

2000-01-01

This overview presents the current status of the research and development of both structural and functional intermetallics. On the one hand, the discussion is focused on commercialization and existing industrial applications of intermetallics. Within this frame the applications of titanium aluminides (TiAl) for turbocharger rotors and exhaust valves in automotive industry are being discussed. Advances in the applications of TiAl alloys for the next generation of turbine blades in aerospace/aircraft segment are also presented. The entire spectrum of nickel and iron aluminide alloys developed commercially by the Oak Ridge national Laboratory (USA) and the examples of their application in various segments of industry are thoroughly discussed. Some inroads made in the application of directionally solidified (DS) multiphase niobium silicides (Nb 3 Si+Nb 5 Si 3 ) in situ intermetallic composites with the goal of pushing the service temperature envelope of turbine blades to ∼ 1200-1300 o C are also discussed. On the other hand, various topics in basic or curiosity driven research of titanium aluminides and trialuminides, iron aluminides and high temperature structural silicides are discussed. Some very recent findings on the improvements in fracture toughness and strength of titanium trialuminides and magnetic behaviour of unconventionally cold - worked iron aluminides are highlighted. The topic of functional intermetallics is limited to the systems must suitable for hydrogen storage applications. A perspective on the directions of future research and development of intermetallics is also provided. (author)

Zirconium intermetallics and hydrogen uptake during corrosion

International Nuclear Information System (INIS)

Cox, B.

1987-04-01

The routes by which hydrogen can enter zirconium alloys containing second phase particles during corrosion are discussed. Both direct diffusion through the bulk of the oxide film, and migration through second phase particles that intersect the surface are considered. An examination of results for hydrogen uptake by zirconium alloys during the early stages of oxidation, when the oxide film is still coherent, suggests that for Zr, Zr-1%Cu and Zr-1%Fe the hydrogen enters by diffusing through the bulk ZrO 2 film, whereas for the Zircaloys the primary migration route may be through the intermetallics. The steps in the latter process are discussed and the evidence available on the properties of the intermetallics collated. A comparison of these data with results for hydrogen uptake by two series of ternary alloys (Zr-1%Nb - 1%X, Zr-1%Cu - 1%X) suggests that high hydrogen uptakes often correlate with intermetallics with high hydrogen solubilities and vice versa. The properties of Zr(Fe/Cr) 2+x intermetallics are examined in an attempt to understand the behaviour of the Zircaloys, and it is concluded that present data establishing composition and unit cell dimensions for such intermetallic particles are not of sufficient accuracy to permit a correlation

Persistent local chemical bonds in intermetallic phase formation

Energy Technology Data Exchange (ETDEWEB)

Bai, Yanwen [Key Laboratory for Liquid–Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan 250061 (China); Bian, Xiufang, E-mail: xfbian@sdu.edu.cn [Key Laboratory for Liquid–Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan 250061 (China); Qin, Xubo [Key Laboratory for Liquid–Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan 250061 (China); Zhang, Shuo; Huang, Yuying [Shanghai Synchrotron Radiation Facilities, Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201204 (China)

2014-05-01

We found a direct evidence for the existence of the local chemical Bi–In bonds in the BiIn{sub 2} melt. These bonds are strong and prevail, dominating the structure evolution of the intermetallic clusters. From the local structure of the melt-quenched BiIn{sub 2} ribbon, the chemical Bi–In bonds strengthen compared with those in the equilibrium solidified alloy. The chemical bonds in BiIn{sub 2} melt retain to solid during a rapid quenching process. The results suggest that the intermetallic clusters in the melt evolve into the as-quenched intermetallic phase, and the intermetallic phase originates from the chemical bonds between unlike atoms in the melt. The chemical bonds preserve the chemical ordered clusters and dominate the clusters evolution.

Intermetallic alloys: Deformation, mechanical and fracture behaviour

International Nuclear Information System (INIS)

Dogan, B.

1988-01-01

The state of the art in intermetallic alloys development with particular emphasis on deformation, mechanical and fracture behaviour is documented. This review paper is prepared to lay the ground stones for a future work on mechanical property characterization and fracture behaviour of intermetallic alloys at GKSS. (orig.)

Charge and spin density in s-stable rare earth intermetallic compounds

International Nuclear Information System (INIS)

Graaf, H. de.

1982-01-01

This thesis deals with a study of the electronic structure of rare earth intermetallic compounds, in particular the electronic charge and spin density distribution. These are closely related to the properties of the rare earth ions, which carry the partly filled 4f shell. In chapter 1 a survey of the theory of hyperfine interaction as far as it has a bearing on the Moessbauer effect of 155 Gd and 151 Eu is given. Also some details of the Moessbauer spectra, which have practical importance are discussed. In chapter 2 the experimental set-up is described. Special attention is paid to the gamma radiation source and gamma detection requirements. In chapter 3 the author introduces the theoretical framework which will be used to interpret the measurements. In chapter 4 the results of the 155 Gd Moessbauer measurements are presented. Also it is discussed how the result can be understood in terms of the charge and spin density in rare earth intermetallic compounds. In order to lend support to the picture emerging from the previous chapter, in chapter 5 the conduction electron band structure of some representative Gd intermetallics is computed with an approximate semi-empirical LCAO method. The results are compared with those from chapter 4. Finally, in chapter 6, the 151 Eu resonance is used to investigate the temperature dependence of the hyperfine field and line width in the Eu intermetallic compounds Eu 2 Mg 17 and EuMg 5 . (Auth.)

Low-Temperature Synthesis Routes to Intermetallic Superconductors

Energy Technology Data Exchange (ETDEWEB)

Schaak, Raymond E

2008-01-08

Over the past few years, our group has gained expertise at developing low-temperature solution-based synthetic pathways to complex nanoscale solids, with particular emphasis on nanocrystalline intermetallic compounds. Our synthetic capabilities are providing tools to reproducibly generate intermetallic nanostructures with simultaneous control over crystal structure, composition, and morphology. This DOE-funded project aims to expand these capabilities to intermetallic superconductors. This could represent an important addition to the tools that are available for the synthesis and processing of intermetallic superconductors, which traditionally utilize high-temperature, high-pressure, thin film, or gas-phase vacuum deposition methods. Our current knowledge of intermetallic superconductors suggests that significant enhancements could result from the inherent benefits of low-temperature solution synthesis, e.g. metastable phase formation, control over nanoscale morphology to facilitate size-dependent property studies, robust and inexpensive processability, low-temperature annealing and consolidation, and impurity incorporation (for doping, stoichiometry control, flux pinning, and improving the critical fields). Our focus is on understanding the superconducting properties as a function of synthetic route, crystal structure, crystallite size, and morphology, and developing the synthetic tools necessary to accomplish this. This research program can currently be divided into two classes of superconducting materials: intermetallics (transition metal/post transition metal) and metal carbides/borides. Both involve the development and exploitation of low-temperature synthesis routes followed by detailed characterization of structures and properties, with the goal of understanding how the synthetic pathways influence key superconducting properties of selected target materials. Because of the low-temperature methods used to synthesize them and the nanocrystalline morphologies

Microstructure and tribological properties of Ti–Cu intermetallic compound coating

International Nuclear Information System (INIS)

Guo, Chun; Zhou, Jiansong; Yu, Youjun; Wang, Lingqian; Zhou, Huidi; Chen, Jianmin

2012-01-01

Highlights: ► Ti–Cu coating has been synthesized on pure Ti substrate by laser cladding. ► Microstructure and tribological properties of Ti–Cu coating were analyzed. ► The prepared Ti–Cu intermetallic compound coating has excellent wear resistance. -- Abstract: Ti–Cu intermetallic compound coating has been in situ synthesized successfully on pure Ti substrate by laser cladding using copper powder as the precursor. It has been found that the prepared coating mainly contains of TiCu, TiCu 3 , Ti 3 Cu, and Ti phases. The transmission electron microscopy results conform further the existence of Ti–Cu intermetallic compound in the fabricated coating. Tribological properties of the prepared Ti–Cu intermetallic compound coating were systematically evaluated. It was found that normal loads and sliding speeds have a strong influence on the friction coefficient and wear rate of Ti–Cu intermetallic compound coating. Namely, the friction coefficient of the Ti–Cu intermetallic compound coating decreased with increasing normal load and sliding speed. The wear rate of the Ti–Cu intermetallic compound coating decreased rapidly with increasing sliding speed, while the wear rate increased as the normal load increased.

Mechanical properties of aluminium matrix composites reinforced with intermetallics

International Nuclear Information System (INIS)

Torres, B.; Garcia-Escorial, A.; Ibanez, J.; Lieblich, M.

2001-01-01

In this work 2124 aluminium matrix composites reinforced with Ni 3 Al, NiAl, MoSi 2 and Cr 3 Si intermetallic powder particles have been investigated. For comparison purposes, un reinforced 2124 and reinforced with SiC have also been studied. In all cases, the same powder metallurgy route was used, i. e. the 2124 alloy was obtained by rapid solidification and the intermetallic particles by self-propagating high-temperature synthesis (SHS). The matrix and the intermetallics were mechanically blended, cold compacted and finally hot extruded. Tensile tests were carried out in T1 and T4 treatments. Results indicate that mechanical properties depend strongly on the tendency to form new phases at the matrix-intermetallic interface during processing and/or further thermal treatments. The materials which present better properties are those that present less reaction between matrix and intermetallic reinforcement, i. e. MoSi 2 and SiC reinforced composites. (Author) 9 refs

Containerless automated processing of intermetallic compounds and composites

Science.gov (United States)

Johnson, D. R.; Joslin, S. M.; Reviere, R. D.; Oliver, B. F.; Noebe, R. D.

1993-01-01

An automated containerless processing system has been developed to directionally solidify high temperature materials, intermetallic compounds, and intermetallic/metallic composites. The system incorporates a wide range of ultra-high purity chemical processing conditions. The utilization of image processing for automated control negates the need for temperature measurements for process control. The list of recent systems that have been processed includes Cr, Mo, Mn, Nb, Ni, Ti, V, and Zr containing aluminides. Possible uses of the system, process control approaches, and properties and structures of recently processed intermetallics are reviewed.

Intermetallics: past, present and future

Directory of Open Access Journals (Sweden)

Morris, D. G.

2005-12-01

Full Text Available Intermetallics have seen extensive world-wide attention over the past decades. For the most part these studies have examined multi-phase aluminide based alloys, because of their high stiffness, combined with reasonable strength and ductility, good structural stability and oxidation resistance, and attempted to improve current Ni-base superalloys, Ti-base alloys, or Fe-base stainless steels for structural aerospace applications. The current status of development and application of such materials is briefly reviewed. Future developments are taking intermetallics from the realm of "improved high-temperature but low-ductility metallic alloys" into the realm of "improved aggressive-environment, high-toughness ceramic-like alloys". Such evolution will be outlined.

Durante los últimos décadas ha habido un desarrollo de los intermetálicos, sobre todo por aplicaciones estructurales a alta temperatura en aplicaciones aeroespaciales, donde, por su rigidez alta, en combinación con una resistencia mecánica y ductilidad razonable, su buena estabilidad estructural y resistencia a la oxidación, han sido vistos como versiones avanzadas y mejoradas de las aleaciones metálicas como, por ejemplo, las superaleaciones a base de nitrógeno y las aleaciones de titanio. Se discute el desarrollo importante durante las últimas décadas, y también los nuevos desarrollos probables durante los próximos años. Se podrían ver los intermetálicos como versiones mejoradas de los cerámicos.

Rare earth intermetallic compounds produced by a reduction-diffusion process

International Nuclear Information System (INIS)

Cech, R.E.

1975-01-01

A reduction-diffusion process is given for producing novel rare earth intermetallic compounds, such as cobalt--rare earth intermetallic compounds, especially compounds useful in preparing permanent magnets. A particulate mixture of rare earth metal halide, cobalt and calcium hydride is heated to effect reduction of the rare earth metal halide and to diffuse the resulting rare earth metal into the cobalt to form the intermetallic compound

The influence of the surface distribution of Al6(MnFe) intermetallic on the electrochemical response of AA5083 aluminium alloy in NaCl solutions

International Nuclear Information System (INIS)

Bethencourt, M.; Botana, F.J.; Calvino, J.J.; Perez, J.; Rodriguez, M.A.; Marcos, M.

1998-01-01

In this paper the behaviour against pitting corrosion of different samples of AA5083 aluminium alloy has been studied. A correlation between the microstructure of the samples and their susceptibility to pitting has been established. Metallographic analysis combined with SEM and EDS techniques have allowed us to detect three intermetallic compounds in the samples. The particle size distribution and surface density of each intermetallic phase have been evaluated for the three AA5083 alloy samples coming from different suppliers. Significant differences in the microstructure of the three samples have been found. Full immersion test carried out in 3.5% aerated aqueous solutions showed that pitting starts at the locations of the Al 6 (MnFe) intermetallic particles. As a consequence of this, the samples with higher Al 6 (MnFe) content showed a higher pit density on its surface. The results of cyclic polarisation tests showed also a good correlation with the microstructural parameters. (orig.)

Electronic and magnetic properties of intermetallic compound YCo5

International Nuclear Information System (INIS)

Zhang, G.W.; Feng, Y.P.; Ong, C.K.

1998-01-01

The electronic and magnetic properties of the intermetallic compound YCo 5 have been studied using density functional theory with the local spin density approximation. The calculated magnetic moments of Y, Co(2c) and Co(3g) are -0.61, 1.68 and 2.04 μ B , respectively, and the total magnetic moment is about 8.87 μ B per formula unit, which agrees well with the previous experimental results. The dependence of the magnetic moments of Y, Co(2c) and Co(3g) on the lattice spacing has been investigated. The local electronic structure of Y, Co(2c) and Co(3g) are discussed in detail. The local magnetic susceptibilities of Y, Co(2c) and Co(3g) are calculated. Based on our results, YCo 5 was found to have characteristic of a strong ferromagnet. (orig.)

Microstructure and tribological properties of TiAg intermetallic compound coating

International Nuclear Information System (INIS)

Guo Chun; Chen Jianmin; Zhou Jiansong; Zhao Jierong; Wang Linqian; Yu Youjun; Zhou Huidi

2011-01-01

TiAg intermetallic compound coating has been in situ synthesized successfully on pure Ti substrate by laser cladding using Ag powder as the precursor. It has been found that the prepared coating mainly comprised TiAg and Ti phases. The high resolution transmission electron microscopy results further conform the existence of TiAg intermetallic compound in the prepared coating. The magnified high resolution transmission electron microscopy images shown that the laser cladding coating contains TiAg nanocrystalline with the size of about 4 nm. Tribological properties of the prepared TiAg intermetallic compound coating were systematically evaluated. It was found that the friction coefficient and wear rate was closely related to the normal load and sliding speed, i.e., the friction coefficient of the prepared TiAg intermetallic compound coating decreased with increasing normal load and sliding speed. The wear rate of the TiAg intermetallic compound coating decreased rapidly with increasing sliding speed, while the wear rate increased as the normal load increased.

Microstructure and tribological properties of TiAg intermetallic compound coating

Energy Technology Data Exchange (ETDEWEB)

Guo Chun [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000 (China); Graduate University of Chinese Academy of Sciences, Beijing 100039 (China); Chen Jianmin, E-mail: chenjm@lzb.ac.cn [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000 (China); Zhou Jiansong [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000 (China); Zhao Jierong; Wang Linqian; Yu Youjun [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000 (China); Graduate University of Chinese Academy of Sciences, Beijing 100039 (China); Zhou Huidi [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000 (China)

2011-10-01

TiAg intermetallic compound coating has been in situ synthesized successfully on pure Ti substrate by laser cladding using Ag powder as the precursor. It has been found that the prepared coating mainly comprised TiAg and Ti phases. The high resolution transmission electron microscopy results further conform the existence of TiAg intermetallic compound in the prepared coating. The magnified high resolution transmission electron microscopy images shown that the laser cladding coating contains TiAg nanocrystalline with the size of about 4 nm. Tribological properties of the prepared TiAg intermetallic compound coating were systematically evaluated. It was found that the friction coefficient and wear rate was closely related to the normal load and sliding speed, i.e., the friction coefficient of the prepared TiAg intermetallic compound coating decreased with increasing normal load and sliding speed. The wear rate of the TiAg intermetallic compound coating decreased rapidly with increasing sliding speed, while the wear rate increased as the normal load increased.

Rare earth-ruthenium-magnesium intermetallics

Energy Technology Data Exchange (ETDEWEB)

Stein, Sebastian; Kersting, Marcel; Heletta, Lukas; Poettgen, Rainer [Muenster Univ. (Germany). Inst. fuer Anorganische und Analytische Chemie

2017-07-01

Eight new intermetallic rare earth-ruthenium-magnesium compounds have been synthesized from the elements in sealed niobium ampoules using different annealing sequences in muffle furnaces. The compounds have been characterized by powder and single crystal X-ray diffraction. Sm{sub 9.2}Ru{sub 6}Mg{sub 17.8} (a=939.6(2), c=1779(1) pm), Gd{sub 11}Ru{sub 6}Mg{sub 16} (a=951.9(2), c=1756.8(8) pm), and Tb{sub 10.5}Ru{sub 6}Mg{sub 16.5} (a=942.5(1), c=1758.3(4) pm) crystallize with the tetragonal Nd{sub 9.34}Ru{sub 6}Mg{sub 17.66} type structure, space group I4/mmm. This structure exhibits a complex condensation pattern of square-prisms and square-antiprisms around the magnesium and ruthenium atoms, respectively. Y{sub 2}RuMg{sub 2} (a=344.0(1), c=2019(1) pm) and Tb{sub 2}RuMg{sub 2} (a=341.43(6), c=2054.2(7) pm) adopt the Er{sub 2}RuMg{sub 2} structure and Tm{sub 3}Ru{sub 2}Mg (a=337.72(9), c=1129.8(4) pm) is isotypic with Sc{sub 3}Ru{sub 2}Mg. Tm{sub 3}Ru{sub 2}Mg{sub 2} (a=337.35(9), c=2671(1) pm) and Lu{sub 3}Ru{sub 2}Mg{sub 2} (a=335.83(5), c=2652.2(5) pm) are the first ternary ordered variants of the Ti{sub 3}Cu{sub 4} type, space group I4/mmm. These five compounds belong to a large family of intermetallics which are completely ordered superstructures of the bcc subcell. The group-subgroup scheme for Lu{sub 3}Ru{sub 2}Mg{sub 2} is presented. The common structural motif of all three structure types are ruthenium-centered rare earth cubes reminicent of the CsCl type. Magnetic susceptibility measurements of Y{sub 2}RuMg{sub 2} and Lu{sub 3}Ru{sub 2}Mg{sub 2} samples revealed Pauli paramagnetism of the conduction electrons.

Phase transformations in intermetallic phases in zirconium alloys

Energy Technology Data Exchange (ETDEWEB)

Filippov, V. P., E-mail: vpfilippov@mephi.ru [National Research Nuclear University MEPhI (Moscow Engineering Physics Institute) (Russian Federation); Kirichenko, V. G. [Kharkiv National Karazin University (Ukraine); Salomasov, V. A. [National Research Nuclear University MEPhI (Moscow Engineering Physics Institute) (Russian Federation); Khasanov, A. M. [University of North Carolina – Asheville, Chemistry Department (United States)

2017-11-15

Phase change was analyzed in intermetallic compounds of zirconium alloys (Zr – 1.03 at.% Fe; Zr – 0.51 at.% Fe; Zr – 0.51 at.% Fe – M(M = Nb, Sn). Mössbauer spectroscopy on {sup 57}Fe nuclei in backscattering geometry with the registration of the internal conversion electrons and XRD were used. Four types of iron bearing intermetallic compounds with Nb were detected. A relationship was found between the growth process of intermetallic inclusions and segregation of these phases. The growth kinetics of inclusions possibly is not controlled by bulk diffusion, and a lower value of the iron atom’s activation energy of migration can be attributed to the existence of enhanced diffusion paths and interface boundaries.

Laves intermetallics in stainless steel-zirconium alloys

International Nuclear Information System (INIS)

Abraham, D.P.; McDeavitt, S.M.; Richardson, J.W. Jr.

1997-01-01

Laves intermetallics have a significant effect on properties of metal waste forms being developed at Argonne National Laboratory. These waste forms are stainless steel-zirconium alloys that will contain radioactive metal isotopes isolated from spent nuclear fuel by electrometallurgical treatment. The baseline waste form composition for stainless steel-clad fuels is stainless steel-15 wt.% zirconium (SS-15Zr). This article presents results of neutron diffraction measurements, heat-treatment studies and mechanical testing on SS-15Zr alloys. The Laves intermetallics in these alloys, labeled Zr(Fe,Cr,Ni) 2+x , have both C36 and C15 crystal structures. A fraction of these intermetallics transform into (Fe,Cr,Ni) 23 Zr 6 during high-temperature annealing; the authors have proposed a mechanism for this transformation. The SS-15Zr alloys show virtually no elongation in uniaxial tension, but exhibit good strength and ductility in compression tests. This article also presents neutron diffraction and microstructural data for a stainless steel-42 wt.% zirconium (SS-42Zr) alloy

Diffusion mechanisms in intermetallic compounds

Energy Technology Data Exchange (ETDEWEB)

Larikov, L N [ANU, Inst. Metallofiziki, Kiev (Ukraine)

1992-08-01

Recent research aimed at the identification of the principal mechanisms of diffusion in intermetallics is reviewed. In particular, attention is given to the effect of the type of interatomic bond on the contribution of different mechanisms to diffusion in ordered metallic compounds. Results of an analysis of experimental determinations of diffusion coefficients D(A) and D(B) in binary intermetallics (CuZn, Cu3Sn, AuCd, AgZn, AgMg, InSb, GaSb, AlSb, Fe3Al, FeAl, FeAl3, Ni3Al, Ni3Nb, FeSn, FeSn2, Ni3Sn2, Ni3Sn4, Co3Sn2, CoSn, CoSn2, and CoGa) are presented, and it is shown that the D(A)/D(B) ratio differs substantially for different diffusion mechanisms. 60 refs.

Growth of intermetallics between Sn/Ni/Cu, Sn/Ag/Cu and Sn/Cu layered structures

International Nuclear Information System (INIS)

Horváth, Barbara; Illés, Balázs; Shinohara, Tadashi

2014-01-01

Intermetallic growth mechanisms and rates are investigated in Sn/Ni/Cu, Sn/Ag/Cu and Sn/Cu layer systems. An 8–10 μm thick Sn surface finish layer was electroplated onto a Cu substrate with a 1.5–2 μm thick Ni or Ag barrier layer. In order to induce intermetallic layer growth, the samples were aged in elevated temperatures: 50 °C and 125 °C. Intermetallic layer growth was checked by focused ion beam–scanning ion microscope. The microstructures and chemical compositions of the intermetallic layers were observed with a transmission electron microscope. It has been found that Ni barrier layers can effectively block the development of Cu 6 Sn 5 intermetallics. The intermetallic growth characteristics in the Sn/Cu and Sn/Ni/Cu systems are very similar. The intermetallic layer grows towards the Sn layer and forms a discrete layer. Differences were observed only in the growth gradients and surface roughness of the intermetallic layer which may explain the different tin whiskering properties. It was observed that the intermetallic layer growth mechanisms are completely different in the Ag barrier layers compared to the Ni layers. In the case of Sn/Ag/Cu systems, the Sn and Cu diffused through the Ag layer, formed Cu 6 Sn 5 intermetallics mainly at the Sn/Ag interface and consumed the Ag barrier layer. - Highlights: • Intermetallic growth was characterised in Sn/Ni/Cu, Sn/Ag/Cu and Sn/Cu layer systems. • Intermetallic growth rates and roughness are similar in the Sn/Cu and Sn/Ni/Cu systems. • Sn/Ni/Cu system contains the following intermetallic layer structure Sn–Ni3Sn4–Ni3Sn2–Ni3Sn–Ni. • In the case of Sn/Ag/Cu systems the Sn and Cu diffusion consumes the Ag barrier layer. • When Cu reaches the Sn/Ag interface a large amount of Cu 6 Sn 5 forms above the Ag layer

Superplastic ceramics and intermetallics and their potential applications

International Nuclear Information System (INIS)

Wadsworth, J.; Nieh, T.G.

1994-11-01

Recent advances in the basic understanding of superplasticity and superplastic forming of ceramics and intermetallics are reviewed. Fine-grained superplastic ceramics, including yttria-stabilized tetragonal zirconia polycrystal, Y- or MgO-doped Al 2 O 3 Hydroxyapatite, β-spodumene glass ceramics, Al 2 0 3 -YTZP two-phase composites, SiC-Si 3 N 4 and Fe-Fe 3 C composites, are discussed. Superplasticity in the nickel-base (e.g., Ni 3 Al and Ni 3 Si) and titanium-base intermetallics (TiAl and T1 3 Al), is described. Deformation mechanisms as well as microstructural requirements and effects such as grain size, grain growth, and grain-boundary phases, on the superplastic deformation behavior am addressed. Factors that control the superplastic tensile elongation of ceramics are discussed. Superplastic forming, and particularly biaxial gas-pressure forming, of several ceramics and intermetallics are presented with comments on the likelihood of commercial application

Stability of ZrBe17, and NiBe intermetallics during intermediate temperature oxidation

International Nuclear Information System (INIS)

Chou, T.C.; Nieh, T.G.; Wadsworth, J.

1992-01-01

This paper reports that since the finding of MoSi 2 pest by Fitzer in 1955, a number of intermetallic compounds, e.g., ZrBe 13 , WSi 2 , and NiAl have also been reported to exhibit similar behavior during oxidation in air. For example, Lewis reported that catastrophic failure (total disintegration into powders) occurred in ZrBe 13 when oxidized at 700 degrees C in air. X-ray diffraction analyses revealed that the powders were composed of BeO, ZrO 2 (cubic), Zr 2 Be 17 , and unreacted ZrBe 13 . Regardless of numerous cited incidents of pest in intermetallics, fundamental understanding of pest is very limited. Recently, MoSi 2 pest has been studied in a great detail and fundamental insights to the mechanism of pest have been established. It is found that both single- and ply- crystalline MoSi 2 are susceptible to pest, which leads to the disintegration of test samples into powder consisting of MoO 3 whiskers, SiP 2 clusters, and residual MoSi 2 crystals. Pest is also noted to associate with substantial volume expansion of the samples. Most important, the occurrence of pest is contingent upon the formation of blisters, resulting from volume expansion by oxidation and the evaporation of MoO 3 on the surfaces and grain boundary interfaces

Microstructure and tribological properties of TiCu2Al intermetallic compound coating

International Nuclear Information System (INIS)

Guo Chun; Zhou Jiansong; Zhao Jierong; Wang Linqian; Yu Youjun; Chen Jianmin; Zhou Huidi

2011-01-01

TiCu 2 Al ternary intermetallic compound coating has been in situ synthesized successfully on pure Ti substrate by laser cladding. Tribological properties of the prepared TiCu 2 Al intermetallic compound coating were systematically evaluated. It was found that the friction coefficient and wear rate was closely related to the normal load and sliding speed, i.e., the friction coefficient of the prepared TiCu 2 Al intermetallic compound coating decreased with increasing normal load and sliding speed. The wear rate of the TiCu 2 Al intermetallic compound coating decreased rapidly with increasing sliding speed, while the wear rate first increased and then decreased at normal load from 5 to 15 N.

Electron-Poor Polar Intermetallics: Complex Structures, Novel Clusters, and Intriguing Bonding with Pronounced Electron Delocalization.

Science.gov (United States)

Lin, Qisheng; Miller, Gordon J

2018-01-16

Intermetallic compounds represent an extensive pool of candidates for energy related applications stemming from magnetic, electric, optic, caloric, and catalytic properties. The discovery of novel intermetallic compounds can enhance understanding of the chemical principles that govern structural stability and chemical bonding as well as finding new applications. Valence electron-poor polar intermetallics with valence electron concentrations (VECs) between 2.0 and 3.0 e - /atom show a plethora of unprecedented and fascinating structural motifs and bonding features. Therefore, establishing simple structure-bonding-property relationships is especially challenging for this compound class because commonly accepted valence electron counting rules are inappropriate. During our efforts to find quasicrystals and crystalline approximants by valence electron tuning near 2.0 e - /atom, we observed that compositions close to those of quasicrystals are exceptional sources for unprecedented valence electron-poor polar intermetallics, e.g., Ca 4 Au 10 In 3 containing (Au 10 In 3 ) wavy layers, Li 14.7 Mg 36.8 Cu 21.5 Ga 66 adopting a type IV clathrate framework, and Sc 4 Mg x Cu 15-x Ga 7.5 that is incommensurately modulated. In particular, exploratory syntheses of AAu 3 T (A = Ca, Sr, Ba and T = Ge, Sn) phases led to interesting bonding features for Au, such as columns, layers, and lonsdaleite-type tetrahedral frameworks. Overall, the breadth of Au-rich polar intermetallics originates, in part, from significant relativistics effect on the valence electrons of Au, effects which result in greater 6s/5d orbital mixing, a small effective metallic radius, and an enhanced Mulliken electronegativity, all leading to ultimate enhanced binding with nearly all metals including itself. Two other successful strategies to mine electron-poor polar intermetallics include lithiation and "cation-rich" phases. Along these lines, we have studied lithiated Zn-rich compounds in which structural

X-ray and magnetic studies on intermetallic phases of the type CaCu5 using noble metals and strontium

International Nuclear Information System (INIS)

Heumann, T.; Birnschein, R.R.

1976-01-01

The intermetallic phases SrAu 5 , SrAg 5 and SrPd 5 and their binary part systems with the specific noble metals as well as the pseudobinary series SrAu 5 -SrPd 5 and SrAg 5 -SrPd 5 are dealt with within the framework of this lecture. The noble metals gold, silver and palladium form AB 5 phases with strontium which cristallize in CaCu 5 structure. The atomic susceptibilities of the part systems Ag-SrAg 5 and Au-SrAu 5 as a function of the Sr concentration, of the part system Pd-SrPd 5 as a function of the temperature and the Sr concentration, of Au-Pd as a function of the Pd concentration, of the series SrAu 5 -SrPd 5 as a function of the SrPd 5 concentration, of the series SrAg 5 -SrPd 5 as function of the SrPd 5 concentration, the electrical resistance of Ag-SrAg 5 and Au-SrAu 5 as function of the Sr concentration, the lattice constants of the series SrAu 5 -SrPd 5 as a function of the SrPd 5 concentration, as well as the number of effective magnetones in the system Au-Pd as a function of the Pd concentration, were measured and evaluated. (orig./LH) [de

The intermetallic ThRh5: microstructure and enthalpy increments

International Nuclear Information System (INIS)

Banerjee, Aparna; Joshi, A.R.; Kaity, Santu; Mishra, R.; Roy, S.B.

2013-01-01

Actinide intermetallics are one of the most interesting and important series of compounds. Thermochemistry of these compounds play significant role in understand the nature of bonding in alloys and nuclear fuel performance. In the present paper we report synthesis and characterization of thorium based intermetallic compound ThRh 5 (s) by SEM/EDX technique. The mechanical properties and enthalpy increment as a function of temperature of the alloy has been measured. (author)

Intermetallics structures, properties, and statistics

CERN Document Server

Steurer, Walter

2016-01-01

The focus of this book is clearly on the statistics, topology, and geometry of crystal structures and crystal structure types. This allows one to uncover important structural relationships and to illustrate the relative simplicity of most of the general structural building principles. It also allows one to show that a large variety of actual structures can be related to a rather small number of aristotypes. It is important that this book is readable and beneficial in the one way or another for everyone interested in intermetallic phases, from graduate students to experts in solid-state chemistry/physics/materials science. For that purpose it avoids using an enigmatic abstract terminology for the classification of structures. The focus on the statistical analysis of structures and structure types should be seen as an attempt to draw the background of the big picture of intermetallics, and to point to the white spots in it, which could be worthwhile exploring. This book was not planned as a textbook; rather, it...

Microstructure and tribological properties of TiCu{sub 2}Al intermetallic compound coating

Energy Technology Data Exchange (ETDEWEB)

Guo Chun, E-mail: guochun@licp.cas.cn [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000 (China); Graduate University of Chinese Academy of Sciences, Beijing 100039 (China); Zhou Jiansong [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000 (China); Zhao Jierong; Wang Linqian; Yu Youjun [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000 (China); Graduate University of Chinese Academy of Sciences, Beijing 100039 (China); Chen Jianmin; Zhou Huidi [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000 (China)

2011-04-15

TiCu{sub 2}Al ternary intermetallic compound coating has been in situ synthesized successfully on pure Ti substrate by laser cladding. Tribological properties of the prepared TiCu{sub 2}Al intermetallic compound coating were systematically evaluated. It was found that the friction coefficient and wear rate was closely related to the normal load and sliding speed, i.e., the friction coefficient of the prepared TiCu{sub 2}Al intermetallic compound coating decreased with increasing normal load and sliding speed. The wear rate of the TiCu{sub 2}Al intermetallic compound coating decreased rapidly with increasing sliding speed, while the wear rate first increased and then decreased at normal load from 5 to 15 N.

Production of nanograined intermetallics using high-pressure torsion

Energy Technology Data Exchange (ETDEWEB)

Alhamidi, Ali; Edalati, Kaveh; Horita, Zenji, E-mail: horita@zaiko.kyushu-u.ac.jp [Department of Materials Science and Engineering, Faculty of Engineering, Kyushu University, Fukuoka (Japan)

2013-11-01

Formation of intermetallics is generally feasible at high temperatures when the lattice diffusion is fast enough to form the ordered phases. This study shows that nanograined intermetallics are formed at a low temperature as 573 K in Al- 25 mol% Ni, Al- 50 mol.% Ni and Al- 50 mol% Ti powder mixtures through powder consolidation using high-pressure torsion (HPT). For the three compositions, the hardness gradually increases with straining but saturates to the levels as high as 550-920 Hv. In addition to the high hardness, the TiAl material exhibits high yield strength as {approx}3 GPa with good ductility as {approx}23%, when they are examined by micropillar compression tests. X-ray diffraction analysis and high-resolution transmission electron microscopy reveal that the significant increase in hardness and strength is due to the formation of nanograined intermetallics such as Al{sub 3}Ni, Al{sub 3}Ni{sub 2}, TiAl{sub 3}, TiAl{sub 2} and TiAl with average grain sizes of 20-40 nm (author)

Studies about interaction of hydrogen isotopes with metals and intermetallic compounds

International Nuclear Information System (INIS)

Vasut, F.; Anisoara, P.; Zamfirache, M.

2003-01-01

Hydrogen is a non-toxic but highly inflammable gas. Compared to other inflammable gases, its range of inflammability in air is much broader (4-74.5%) but it also vaporizes much more easily. Handling of hydrogen in form of hydrides enhances safety. The interaction of hydrogen with metals and intermetallic compounds is a major field within physical chemistry. Using hydride-forming metals and intermetallic compounds, for example, recovery, purification and storage of heavy isotopes in tritium containing system can solve many problems arising in the nuclear-fuel cycle. The paper presents the thermodynamics and the kinetics between hydrogen and metal or intermetallic compounds. (author)

Multi-component intermetallic electrodes for lithium batteries

Science.gov (United States)

Thackeray, Michael M; Trahey, Lynn; Vaughey, John T

2015-03-10

Multi-component intermetallic negative electrodes prepared by electrochemical deposition for non-aqueous lithium cells and batteries are disclosed. More specifically, the invention relates to composite intermetallic electrodes comprising two or more compounds containing metallic or metaloid elements, at least one element of which can react with lithium to form binary, ternary, quaternary or higher order compounds, these compounds being in combination with one or more other metals that are essentially inactive toward lithium and act predominantly, but not necessarily exclusively, to the electronic conductivity of, and as current collection agent for, the electrode. The invention relates more specifically to negative electrode materials that provide an operating potential between 0.05 and 2.0 V vs. metallic lithium.

Thermodynamics and kinetics of the formation of rare earth intermetallics

International Nuclear Information System (INIS)

Deodhar, S.S.

1975-01-01

Heats of reaction of rare earth intermetallics with iron, cobalt and nickel were determined using Differential Thermal Analysis technique. The intermetallic compounds studied were of MgCu 2 type Laves phases and the rare earth elements studied were praseodymium, gadolinium, dyprosium and erbium. The reactions were exothermic and the heats of reaction were generally high. They varied from the low of -2.5 kcal/g mole for Fe 2 Gd to the high of -35.3 kcal/g mole for Ni 2 Er. The magnitudes of heats of reaction were always greater for the intermetallics of heavy rare earth elements. The rare earth intermetallics studied were either ferromagnetic or antiferromagnetic. The variations in the magnetic moments and the heats of reaction with respect to the atomic number of the rare earth elements followed certain trends. The similarities were observed in the trends of two properties. Electronic configuration for the MgCu 2 type rare earth intermetallics is proposed using Engel--Brewer correlation for metallic structures and the structural features of the Laves phase compounds. Kinetics of the reactions between the rare earth elements and iron, cobalt, and nickel was studied. The rate of reaction was diffusion controlled in each case. The Valensi--Carter equation for the diffusion mechanism satisfactorily described the kinetic behavior. The magnitudes of activation energies and frequency factors were determined. The reactions can be characterized by their reaction temperatures since they always begin at definite temperatures. It was observed that the reaction began at a higher temperature if the activation energy for the reaction was high

Electrochemical properties of the passive film on bulk Zr–Fe–Cr intermetallic fabricated by spark plasma sintering

Energy Technology Data Exchange (ETDEWEB)

Bai, Yakui [School of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China); Ling, Yunhan, E-mail: yhling@mail.tsinghua.edu.cn [School of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China); Lai, Wensheng [School of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China); Xing, Shupei; Ma, Wen [School of Materials Science and Engineering, Inner Mongolia University of Technology, Huhhot 010051 (China)

2016-12-01

Highlights: • SPS was employed to prepare Zr-based intermetallics which were commonly existed in zircaloy. • Zr-based intermetallics act as cathode when they embedded in zirconium matrix. • The passive films on surface of intermetallics behaved as n-type semiconductors. • Carrier concentration of Zr(Fe{sub 3}Cr){sub 2} was much lower than that of other intermetallics. - Abstract: Although Zr-based second phase particles (SPPs) are important factors influencing corrosion resistance of zircaloy cladding materials, the corrosion behavior of SPPs has not been investigated by means of electrochemical method so far. In order to clarify the role of SPPs commonly existed in zircaloy, bulk Zr-based intermetallics were firstly fabricated by spark plasma sintering (SPS) at temperatures 1373 K and an applied pressure of 60 MPa in this work. Both the natural passive film on surface and oxidation behavior of intermetallic has been investigated in this work. X-ray diffraction (XRD) pattern showed that as-prepared intermetallic of crystal structure belongs to Laves phase with AB{sub 2} type. Electrochemical measurement of passive film on surface of bulk Zr-based intermetallic exhibited significant difference with that of zirconium. Potentiodynamic measurements results revealed that intermetallic exhibited higher corrosion potential and lower corrosion current density than that of pure zirconium, implying that Zr-based second phase will act as cathode when they are included in zirconium matrix. Meanwhile, significant improvement of Zr–Fe–Cr intermetallic on the water chemistry corrosion resistance was demonstrated comparing with Zr–Fe and Zr–Cr binary intermetallics.

Effects of iron on intermetallic compound formation in scandium modified Al–Si–Mg Alloys

Energy Technology Data Exchange (ETDEWEB)

Patakham, Ussadawut [National Metal and Materials Technology Center, National Science and Technology Development Agency, 114 Thailand Science Park, Klong Nueng, Klong Luang, Pathumthani 12120 (Thailand); Limmaneevichitr, Chaowalit, E-mail: chaowalit.lim@mail.kmutt.ac.th [Production Engineering Department, Faculty of Engineering, King Mongkut’s University of Technology Thonburi, 126 Pracha-Utid Rd., Bangmod, Tungkhru, Bangkok 10140 (Thailand)

2014-12-15

Highlights: • Iron reduces the modification effects of scandium in Al–Si–Mg alloys. • Morphologies of Sc-rich intermetallic phases vary with Fe and Sc contents and the cooling rates. • Sc neutralizes effects of Fe by changing Fe-rich intermetallic phases from platelets to more cubic. - Abstract: In general, iron has a strong tendency to dissolve in molten aluminum. Iron has very low solid solubility in aluminum–silicon casting alloys, so it will form intermetallic compounds that cause detrimental effects on mechanical properties. In this work, the effects of iron on intermetallic compound formations in scandium modified Al–Si–Mg alloys were studied. There were two levels of iron addition (0.2 and 0.4 wt.%) and two levels of scandium addition (0.2 and 0.4 wt.%). We found that the effects of scandium modification decreased with increasing iron addition. The morphologies of the complex intermetallic compounds were characterized by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and electron backscatter diffraction (EBSD) techniques. It was found that scandium changes the morphology of Fe-rich intermetallic compounds from β-phase (plate-like) to α-phase, which reduces the harmful effects of β-phase.

Atomic interaction of the MEAM type for the study of intermetallics in the Al–U alloy

International Nuclear Information System (INIS)

Pascuet, M.I.; Fernández, J.R.

2015-01-01

Interaction for both pure Al and Al–U alloys of the MEAM type are developed. The obtained Al interatomic potential assures its compatibility with the details of the framework presently adopted. The Al–U interaction fits various properties of the Al_2U, Al_3U and Al_4U intermetallics. The potential verifies the stability of the intermetallic structures in a temperature range compatible with that observed in the phase diagram, and also takes into account the greater stability of these structures relative to others that are competitive in energy. The intermetallics are characterized by calculating elastic and thermal properties and point defect parameters. Molecular dynamics simulations show a growth of the Al_3U intermetallic in the Al/U interface in agreement with experimental evidence. - Highlights: • Potential parameters for Al and Al–U systems are obtained. • Intermetallics are characterized by calculating elastic and thermal properties. • Point defect diffusivities are calculated for the three intermetallics. • Growth of the Al_3U intermetallic is shown to occur in the Al/U interface as in the real alloy.

Preparation of Ti3Al intermetallic compound by spark plasma sintering

Science.gov (United States)

Ito, Tsutomu; Fukui, Takahiro

2018-04-01

Sintered compacts of single phase Ti3Al intermetallic compound, which have excellent potential as refractory materials, were prepared by spark plasma sintering (SPS). A raw powder of Ti3Al intermetallic compound with an average powder diameter of 176 ± 56 μm was used in this study; this large powder diameter is disadvantageous for sintering because of the small surface area. The samples were prepared at sintering temperatures (Ts) of 1088, 1203, and 1323 K, sintering stresses (σs) of 16, 32, and 48 MPa, and a sintering time (ts) of 10 min. The calculated relative densities based on the apparent density of Ti3Al provided by the supplier were approximately 100% under all sintering conditions. From the experimental results, it was evident that SPS is an effective technique for dense sintering of Ti3Al intermetallic compounds in a short time interval. In this report, the sintering characteristics of Ti3Al intermetallic compacts are briefly discussed and compared with those of pure titanium compacts.

Surfaces of Intermetallics: Quasicrystals and Beyond

Energy Technology Data Exchange (ETDEWEB)

Yuen, Chad [Iowa State Univ., Ames, IA (United States)

2012-01-01

The goal of this work is to characterize surfaces of intermetallics, including quasicrystals. In this work, surface characterization is primarily focused on composition and structure using X-ray photoelectron spectroscopy (XPS) and scanning tunneling microscopy (STM) performed under ultrahigh vacuum (UHV) conditions.

Study on the Mechanical Properties and Corrosion Behaviors of Fe-(20, 45) wt%Gd Intermetallics

Energy Technology Data Exchange (ETDEWEB)

Kang, Bo Kyeong; Baik, Youl; Choi, Yong [Dankook University, Chungnam (Korea, Republic of); Moon, Byung Moon [Korea Institute of Industrial Technology, Incheon (Korea, Republic of)

2017-02-15

Fe-(20, 45 wt%) Gd intermetallics were vacuum arc melted as the mother alloy of a neutron shielding and absorbing material. The structure of the cast Fe-20 wt%Gd intermetallics had primary dendrites with a short width of about 2 μm, which became coarse with increasing Gd content. The final compositions of the Fe-20 wt%Gd and Fe-45 wt%Gd intermetallics determined by Rietveld refinement were mainly Fe{sub 3}Gd with 26.6 at%Fe{sub 2}Gd, and Fe{sub 3}Gd with various intermetallics like 13.9 at%Fe{sub 2}Gd, 7.3 at%Fe{sub 9}Gd and 3.9 at%Fe{sub 17}Gd{sub 2}, respectively. The micro-hardnesses, yield strength, ultimate compressive strength and elongation of the Fe-20 wt%Gd intermetallics were 629±12 Hv, 753 MPa, 785 MPa and 4%, respectively, and those of the Fe-45 wt%Gd intermetallics were 741±13 Hv, 772 MPa, 823 MPa and 3%. Passivity was not present in artificial sea water at room temperature. The corrosion potentials and the corrosion rates of the Fe-20 wt%Gd and Fe-45 wt%Gd intermetallics were –624 mV{sub SHE}, 2.771 mA/cm{sup 2} , and –804 mV{sub SHE}, 3.397 mA/cm{sup 2} , respectively. The corroded surface of the Fe-Gd intermetallics contained corrosion products like gadolinium with iron, which detached to leave a trail of pits.

The chemical phenol extraction of intermetallic particles from casting AlSi5Cu1Mg alloy.

Science.gov (United States)

Mrówka-Nowotnik, G; Sieniawski, J; Nowotnik, A

2010-03-01

This paper presents a chemical extraction technique for determination of intermetallic phases formed in the casting AlSi5Cu1Mg aluminium alloy. Commercial aluminium alloys contain a wide range of intermetallic particles that are formed during casting, homogenization and thermomechanical processing. During solidification, particles of intermetallics are dispersed in interdendritic spaces as fine primary phases. Coarse intermetallic compounds that are formed in this aluminium alloy are characterized by unique atomic arrangement (crystallographic structure), morphology, stability, physical and mechanical properties. The volume fraction, chemistry and morphology of the intermetallics significantly affect properties and material behaviour during thermomechanical processing. Therefore, accurate determination of intermetallics is essential to understand and control microstructural evolution in Al alloys. Thus, in this paper it is shown that chemical phenol extraction method can be applied for precise qualitative evaluation. The results of optical light microscopy LOM, scanning electron microscopy SEM and X-ray diffraction XRD analysis reveal that as-cast AlSi5Cu1Mg alloy contains a wide range of intermetallic phases such as Al(4)Fe, gamma- Al(3)FeSi, alpha-Al(8)Fe(2)Si, beta-Al(5)FeSi, Al(12)FeMnSi.

Atomic interaction of the MEAM type for the study of intermetallics in the Al–U alloy

Energy Technology Data Exchange (ETDEWEB)

Pascuet, M.I. [CONICET, Avda. Rivadavia 1917, 1033 Buenos Aires (Argentina); Fernández, J.R., E-mail: julrfern@cnea.gov.ar [CONICET, Avda. Rivadavia 1917, 1033 Buenos Aires (Argentina); CAC-CNEA, Avda. Gral Paz 1499, 1650 Buenos Aires (Argentina); UNSAM, Avda. Gral Paz 1499, 1650 Buenos Aires (Argentina)

2015-12-15

Interaction for both pure Al and Al–U alloys of the MEAM type are developed. The obtained Al interatomic potential assures its compatibility with the details of the framework presently adopted. The Al–U interaction fits various properties of the Al{sub 2}U, Al{sub 3}U and Al{sub 4}U intermetallics. The potential verifies the stability of the intermetallic structures in a temperature range compatible with that observed in the phase diagram, and also takes into account the greater stability of these structures relative to others that are competitive in energy. The intermetallics are characterized by calculating elastic and thermal properties and point defect parameters. Molecular dynamics simulations show a growth of the Al{sub 3}U intermetallic in the Al/U interface in agreement with experimental evidence. - Highlights: • Potential parameters for Al and Al–U systems are obtained. • Intermetallics are characterized by calculating elastic and thermal properties. • Point defect diffusivities are calculated for the three intermetallics. • Growth of the Al{sub 3}U intermetallic is shown to occur in the Al/U interface as in the real alloy.

A survey of combustible metals, thermites, and intermetallics for pyrotechnic applications

Energy Technology Data Exchange (ETDEWEB)

Fischer, S.H.; Grubelich, M.C.

1996-08-01

Thermite mixtures, intermetallic reactants, and metal fuels have long been used in pyrotechnics. Advantages include high energy density, impact insensitivity, high combustion temperature, and a wide range of gas production. They generally exhibit high temperature stability and possess insensitive ignition properties. This paper reviews the applications, benefits, and characteristics of thermite mixtures, intermetallic reactants, and metal fuels. 50 refs, tables.

Complex magnetic behaviour and evidence of a superspin glass state in the binary intermetallic compound Er5Pd2

Science.gov (United States)

Sharma, Mohit K.; Yadav, Kavita; Mukherjee, K.

2018-05-01

The binary intermetallic compound Er5Pd2 has been investigated using dc and ac magnetic susceptibilities, magnetic memory effect, isothermal magnetization, non-linear dc susceptibility, heat capacity and magnetocaloric effect studies. Interestingly, even though the compound does not show geometrical frustration it undergoes glassy magnetic phase transition below 17.2 K. Investigation of dc magnetization and heat capacity data divulged absence of long-ranged magnetic ordering. Through the magnetic memory effect, time dependent magnetization and ac susceptibility studies it was revealed that the compound undergoes glass-like freezing below 17.2 K. Analysis of frequency dependence of this transition temperature through scaling and Arrhenius law; along with the Mydosh parameter indicate, that the dynamics in Er5Pd2 are due to the presence of strongly interacting superspins rather than individual spins. This phase transition was further investigated by non-linear dc susceptibility and was characterized by static critical exponents γ and δ. Our results indicate that this compound shows the signature of superspin glass at low temperature. Additionally, both conventional and inverse magnetocaloric effect was observed with a large value of magnetic entropy change and relative cooling power. Our results suggest that Er5Pd2 can be classified as a superspin glass system with large magnetocaloric effect.

The behavior of intermetallic compounds at large plastic strains

International Nuclear Information System (INIS)

Gray, G.T.; Embury, J.D.

1993-01-01

This paper contains a summary of a broad study of intermetallics which includes the following materials, Ni 3 Al, Ti-48Al-1V, Ti-24Al-11Nb, Ti-48Al-2Cr-2Nb, and Ti-24.5 Al-10.5Nb-1.5Mo. Much effort has been devoted to the study of ordered materials at modes plastic strains and the problem of premature failure. However by utilizing stress states other than simple tension it is possible to study the deformation of intermetallic compounds up to large plastic strains and to consider the behavior of these materials in the regime where stresses approach the theoretical stress. The current work outlines studies of the work hardening rate of a number of titanium and nickel-based intermetallic compounds deformed in compression. Attention is given to the structural basis of the sustained work hardening. The large strain plasticity of these materials is summarized in a series of diagrams. Fracture in these materials in compression occurs via catastrophic shear at stresses of the order of E/80 (where E is the elastic modulus)

The role of intermetallic precipitates in Ti-62222S

Energy Technology Data Exchange (ETDEWEB)

Evans, D J [US Air Force Mater. Directorate Wright Lab., Wright Patterson AFB, OH (United States); Broderick, T F [US Air Force Mater. Directorate Wright Lab., Wright Patterson AFB, OH (United States); Woodhouse, J B [UES Inc, Dayton, OH (United States); Hoenigman, J R [Wright State Univ., Dayton, OH (United States). Research Inst.

1996-08-15

Samples of Ti-62222-0.23wt.%Si were heat treated and aged at temperatures ranging from 1150 F to 1500 F with the view of effecting selective precipitation of {alpha}{sub 2} precipitates and silicides (i.e. Ti{sub x}Zr{sub 5-x}Si{sub 3}). The effect of these intermetallic precipitates on the mechanical properties and fracture morphology was assessed via three separate microstructural conditions: Ti-62222S with {alpha}{sub 2} precipitates, Ti-62222S with {alpha}{sub 2} and silicide precipitates, and Ti-62222S with silicide precipitates. Both types of intermetallic precipitate appear to lower the fracture toughness, however {alpha}{sub 2} promotes intergranular fracture while silicides lead to transgranular failure and dimpling. The combined presence of the {alpha}{sub 2} and silicides leads to mixed mode failure. Further, since {alpha}{sub 2} is present in the {alpha} phase and silicides precipitate out in the {beta} phase, it appears that the effect of each of these intermetallics in Ti-62222S is additive rather than synergistic. (orig.)

MD study of primary damage in L10 TiAl structural intermetallics

International Nuclear Information System (INIS)

Voskoboinikov, Roman E.

2013-01-01

Computer modelling by molecular dynamics has been applied to study the radiation damage created in collision cascades in L1 0 TiAl intermetallic compound. Either Al or Ti primary knock-on atoms (PKA) with energy 5 keV ⩽ E PKA ⩽ 20 keV were introduced in the intermetallic crystals at temperatures ranging from 100 K to 900 K. At least 24 different cascade for each (E PKA , T, PKA type) set were modelled in order to simulate a random spatial and temporal distribution of PKAs and provide statistical reliability of the results. The total yield of more than 760 simulated cascades is the largest yet reported for this binary intermetallic material. A comprehensive treatment of the modelling results has been carried out. The number of Frenkel pairs, fraction of Al and Ti vacancies, self-interstitial atoms and anti-sites as a function of (E PKA , T, PKA type) has been established. Preferred formation of Al self-interstitial atoms has been detected in L1 0 TiAl structural intermetallics exposed to irradiation

High temperature oxidation behavior of TiAl-based intermetallics

International Nuclear Information System (INIS)

Stroosnijder, M.F.; Sunderkoetter, J.D.; Haanappel, V.A.C.

1996-01-01

TiAl-based intermetallic compounds have attracted considerable interest as structural materials for high-temperature applications due to their low density and substantial mechanical strength at high temperatures. However, one major drawback hindering industrial application arises from the insufficient oxidation resistance at temperatures beyond 700 C. In the present contribution some general aspects of high temperature oxidation of TiAl-based intermetallics will be presented. This will be followed by a discussion of the influence of alloying elements, in particular niobium, and of the effect of nitrogen in the oxidizing environment on the high temperature oxidation behavior of such materials

Valence instabilities in cerium intermetallics

International Nuclear Information System (INIS)

Dijkman, W.H.

1982-01-01

The primary purpose of this investigation was to study the magnetic behaviour of cerium in intermetallic compounds, that show an IV behaviour, e.g. CeSn 3 . In the progress of the investigations, it became of interest to study the effect of changes in the lattice of the IV compound by substituting La or Y for Ce, thus constituting the Cesub(1-x)Lasub(x)Sn 3 and Cesub(1-x)Ysub(x)Sn 3 quasibinary systems. A second purpose was to examine the possibility of introducing instabilities in the valency of a trivalent intermetallic cerium compound: CeIn 3 , also by La and Y-substitutions in the lattice. Measurements on the resulting Cesub(1-x)Lasub(x)In 3 and Cesub(1-x)Ysub(x)In 3 quasibinaries are described. A third purpose was to study the (gradual) transition from a trivalent cerium compound into an IV cerium compound. This was done by examining the magnetic properties of the CeInsub(x)Snsub(3-x) and CePbsub(x)Snsub(3-x) systems. Finally a new possibility was investigated: that of the occurrence of IV behaviour in CeSi 2 , CeSi, and in CeGa 2 . (Auth.)

Calorimetric study of the intermetallic compounds UAl2 and PuAl2

International Nuclear Information System (INIS)

Trainor, R.J.; Brodsky, M.B.; Knapp, G.S.

1975-01-01

Results of low temperature specific heat measurements are presented on the strongly paramagnetic intermetallic compounds UAl 2 and PuAl 2 in the temperature intervals 0.9 to 20 0 K, respectively. These compounds are characterized by very narrow 5f bands near the Fermi energy. The low-temperature properties of UAl 2 and PuAl 2 are dominated by long lived spin fluctuations within these narrow bands. In UAl 2 a nearly field-independent T 3 logT contribution dominates the specific heat below 10 0 K, consistent with the predictions of ferromagnetic spin-fluctuation theory. The specific heat, static susceptibility, and electrical resistivity are mutually consistent with T/sub sf/ = 25 +- 10 0 K, where T/sub sf/ is the characteristic spin-fluctuation temperature of the system. Below 20 0 K, the specific heat of PuAl 2 contains a very large linear term, C greater than or approximately equal to 260T (mJ/mole- 0 K), which is approximately four times the magnitude of the measured susceptibility, when both quantities are expressed in the same units. The specific heat of PuAl 2 exhibits no anomalous behavior below 10 0 K, where a resistivity anomaly has been previously obser []ed. The properties of PuAl 2 are qualitatively discussed in terms of antiferromagnetic spin fluctuations. (auth)

Microstructure Characterization and Wear-Resistant Properties Evaluation of an Intermetallic Composite in Ni–Mo–Si System

Directory of Open Access Journals (Sweden)

Boyuan Huang

2017-02-01

Full Text Available Intermetallic compounds have been studied for their potential application as structural wear materials or coatings on engineering steels. In the present work, a newly designed intermetallic composite in a Ni–Mo–Si system was fabricated by arc-melting process with commercially pure metal powders as starting materials. The chemical composition of this intermetallic composite is 45Ni–40Mo–15Si (at %, selected according to the ternary alloy diagram. The microstructure was characterized using optical microscopy (OM, scanning electron microscopy (SEM, X-ray diffraction (XRD, and energy dispersive spectroscopy (EDS, and the wear-resistant properties at room temperature were evaluated under different wear test conditions. Microstructure characterization showed that the composite has a dense and uniform microstructure. XRD results showed that the intermetallic composite is constituted by a binary intermetallic compound NiMo and a ternary Mo2Ni3Si metal silicide phase. Wear test results indicated that the intermetallic composite has an excellent wear-resistance at room-temperature, which is attributed to the high hardness and strong atomic bonding of constituent phases NiMo and Mo2Ni3Si.

The nucleation and growth of intermetallic Al-Pt phases

International Nuclear Information System (INIS)

Kovacs, A.; Barna, P.B.; Labar, J. l.

2002-01-01

The nucleation and growth of intermetallic Al-Pt phases on amorphous carbon was investigated by half shadow technique in co-deposited thin films. In such experimental condition, the composition of the deposited films varied in the range of Al x Pt 1-x (0≤x≤0.6). The coexistence of Al 5 Pt, Al 2 Pt, Al 3 Pt 2 intermetallic phases have been found in the whole range with varying ratio. Vapour depositions were performed in an UHV system. The Al and Pt components were evaporated simultaneously onto amorphous carbon layer supported by TEM micro-grids. Deposition rates were controlled separately by quartz crystal monitors. Substrate temperature during deposition was 350 grad C. A special evaporation arrangement made possible to create a half shadow area on the substrate in which the quantity one of the components increased from zero to the wanted composition of the sample. The composition of the zones was determined by energy dispersive X-ray spectroscopy (EDS) in TEM. The intermetallic phases developed in the sample were investigated by analytical TEM (Philips CM20) and high resolution TEM (JEOL 3010 UHR). The electron diffraction patterns have been evaluated by ProcessDiffraction program. (Authors)

First principles study of halogens adsorption on intermetallic surfaces

International Nuclear Information System (INIS)

Zhu, Quanxi; Wang, Shao-qing

2016-01-01

Graphical abstract: - Highlights: • The linear relation between adsorbates induced work function change and dipole moment change also exists for intermetallic surfaces. • It is just a common linear relationship rather than a directly proportion. • A new weight parameter β is proposed to describe different factors effect on work function shift. - Abstract: Halides are often present at electrochemical environment, they can directly influence the electrode potential or zero charge potential through the induced work-function change. In this work, we focused in particular on the halogen-induced work function change as a function of the coverage of fluorine, chlorine, bromine and iodine on Al_2Au and Al_2Pt (110) surfaces. Results show that the real relation between work function change and dipole moment change for halogens adsorption on intermetallic surfaces is just a common linear relationship rather than a directly proportion. Besides, the different slopes between fitted lines and the theoretical slope employed in pure metal surfaces demonstrating that the halogens adsorption on intermetallic surfaces are more complicated. We also present a weight parameter β to describe different factors effect on work function shift and finally qualify which factor dominates the shift direction.

Low temperature and surfactant-free synthesis of Pd2Sn intermetallic nanoparticles for ethanol electro-oxidation

International Nuclear Information System (INIS)

Wang, Congmin; Wu, Yurong; Wang, Xin; Zou, Liangliang; Zou, Zhiqing; Yang, Hui

2016-01-01

Many intermetallic compounds have a predictable structure, interesting electronic effects, and useful catalytic properties. In this work, a low temperature, surfactant-free, and one-pot method is used to synthesize carbon supported Pd 2 Sn intermetallic nanoparticles. The superlattice of the product was then characterized using X-ray diffraction and transmission electron microscopy. These synthesized intermetallic nanoparticles were found to exhibit a higher activity and stability for electrocatalysis of the ethanol oxidation reaction in an alkaline media than has been achieved using a traditional Pd/C catalyst, which could be attributed to the structural and compositional stabilities of ordered Pd 2 Sn intermetallic nanoparticles.

Influence of intermetallic growth on the mechanical properties of Zn–Sn–Cu–Bi/Cu solder joints

Energy Technology Data Exchange (ETDEWEB)

Xing, Fei; Yao, Jia; Liang, Jingwei; Qiu, Xiaoming, E-mail: qiuxm13@163.com

2015-11-15

The formation of intermetallic reaction layers and their influence on shear strength and fractography was investigated between the Zn–Sn–Cu–Bi (ZSCB) and Cu substrate during the liquid state reaction at 450 °C after 10–90 s. Results showed that reliable solder joints could be obtained at 450 °C after 15–30 s of wetting, accompanied by the creation of scallop ε-CuZn{sub 5}, flat γ-Cu{sub 5}Zn{sub 8} and β-CuZn intermetallic layers in ZSCB/Cu interface. However, with excess increase of soldering time, a transient intermetallic ε-CuZn{sub 4} phase was nuclear and grew at ε-CuZn{sub 5}/γ-Cu{sub 5}Zn{sub 8} interface, which apparently deteriorated the shear strength of solder joints from 76.5 MPa to 51.6 MPa. The sensitivity of the fracture proportion was gradually transformed from monotonic ε-CuZn{sub 5} to the mixture of ε-CuZn{sub 4} and ε-CuZn{sub 5} intermetallic cleavage. Furthermore, the growth mechanism of ε-CuZn{sub 4} intermetallic phase at the ZSCB/Cu interface was discussed. - Highlights: • There are four interfacial intermetallic layers formed at the Zn–Sn–Cu–Bi/Cu interface. • The growth mechanism of ε-CuZn{sub 4} intermetallic phase was discussed. • The wetting time of Zn–Sn–Cu–Bi solder in contact with Cu substrate is a key parameter.

Structure data of elements and intermetallic phases. SubVol. B. Sulfides, selenides, tellurides. Pt. 1. Ag-Al-Cd-S. Cu-Te-Yb

Energy Technology Data Exchange (ETDEWEB)

Hellwege, K H; Hellwege, A M [eds.; Eisenmann, B; Schaefer, H

1986-01-01

Volume III/14 'Structure data of elements and intermetallic phases' is a supplement to and extension of Volume III/6. Since the publication of III/6 in 1971 (considering original papers up to 1967), the amount of new information for these substances has increased rapidly. Therefore the data had to be divided into several parts. The first part, III/14b1, is presented herewith. In Volume III/6, simple sulfides, selenides and tellurides were treated together with the intermetallic phases. The data are compiled in the same way as in III/6: for each substance the space group, lattice constants, their dependence on temperature and pressure, and other information is listed in the tables. In several cases, mostly for solid solutions, diagrams are given which are added in a separate chapter. Original papers containing a complete structure analysis are referred to in the tables. (orig./GSCH).

Hydrogenations of alloys and intermetallic compounds of magnesium

International Nuclear Information System (INIS)

Gavra, Z.

1981-08-01

A kinetic and thermodynamic study of the hydrogenation of alloys and intermetallic compounds of magnesium is presented. It was established that the addition of elements of the IIIA group (Al, Ga, In) to magnesium catalyses its hydrogenation. This is explained by the mechanism of diffusion of magnesium cation vacancies. The hydride Mg 2 NiH 4 was characterized by thermal analysis, x-ray diffraction and NMR measurements. The possibility of forming pseudo-binary compounds of Mg 2 Ni by the substitution of nickel or magnesium was examined. The hydrogenation of the inter-metallic compounds of the Mg-Al system was investigated. It was found that the addition of indium and nickel affected the hydrogenation kinetics. A preliminary study of the hydrogenation of various binary and ternary alloys of magnesium was carried out. (Author)

Magnetocaloric effect in rare-earth intermetallics: Recent trends

Indian Academy of Sciences (India)

... intermetallic hydrides, manganite oxides, Ni–Mn–Sb-type shape memory ... With the help of temperature-dependent heat capacity information in various applied .... for relative cooling power and a wide working temperature range of about ...

Studies of hydrogen absorption and desorption processes in advanced intermetallic hydrides

Energy Technology Data Exchange (ETDEWEB)

Sato, Masashi

2005-07-01

This work is a part of the research program performed in the Department of Energy Systems, Institute for Energy Technology (Kjeller, Norway), which is focused on the development of the advanced hydrogen storage materials. The activities are aimed on studies of the mechanisms of hydrogen interactions with intermetallic alloys with focus on establishing an interrelation between the crystal structure, thermodynamics and kinetics of the processes in the metal-hydrogen systems, on the one hand, and hydrogen storage properties (capacity, rates of desorption, hysteresis). Many of the materials under investigation have potential to be applied in applications, whereas some already have been commercialised in the world market. A number of metals take up considerable amounts of hydrogen and form chemical compounds with H, metal hydrides. Unfortunately, binary hydrides are either very stable (e.g. for the rare earth metals [RE], Zr, Ti, Mg: metal R) or are formed at very high applied pressures of hydrogen gas (e.g. for the transition metals, Ni, Co, Fe, etc.: Metal T). However, hydrogenation process becomes easily reversible at very convenient from practical point of view conditions, around room temperature and at H2 pressures below 1 MPa for the two-component intermetallic alloys R{sub x}T{sub y}. This raised and maintains further interest to the intermetallic hydrides as solid H storage materials. Materials science research of this thesis is focused on studies of the reasons staying behind the beneficial effect of two non-transition elements M(i.e., In and Sn) contributing to the formation of the ternary intermetallic alloys R{sub x}T{sub y}M{sub 2}., on the hydrogen storage behaviours. Particular focus is on two aspects where the remarkable improvement of ordinary metal hydrides is achieved via introduction of In and Sn: a) Increase of the volume density of stored hydrogen in solid materials to the record high level. b) Improvement of the kinetics of hydrogen charge and

Theoretical energy release of thermites, intermetallics, and combustible metals

Energy Technology Data Exchange (ETDEWEB)

Fischer, S.H.; Grubelich, M.C.

1998-06-01

Thermite (metal oxide) mixtures, intermetallic reactants, and metal fuels have long been used in pyrotechnic applications. Advantages of these systems typically include high energy density, impact insensitivity, high combustion temperature, and a wide range of gas production. They generally exhibit high temperature stability, and possess insensitive ignition properties. In this paper, the authors review the applications, benefits, and characteristics of thermite mixtures, intermetallic reactants, and metal fuels. Calculated values for reactant density, heat of reaction (per unit mass and per unit volume), and reaction temperature (without and with consideration of phase changes and the variation of specific heat values) are tabulated. These data are ranked in several ways, according to density, heat of reaction, reaction temperature, and gas production.

First principles electronic and thermal properties of some AlRE intermetallics

Science.gov (United States)

Srivastava, Vipul; Sanyal, Sankar P.; Rajagopalan, M.

2008-10-01

A study on structural and electronic properties of non-magnetic cubic B 2-type AlRE (RE=Sc, Y, La, Ce, Pr and Lu) intermetallics has been done theoretically. The self-consistent tight binding linear muffin tin orbital method is used to describe the electronic properties of these intermetallics at ambient and at high pressure. These compounds show metallic behavior under ambient conditions. The variation of density of states under compression indicates some possibility of structural phase transformation in AlLa, AlCe and AlPr. Thermal properties like Debye temperature and Grüneisen constant are calculated at T=0 K and at ambient pressure within the Debye-Grüneisen model and compared with the others’ theoretical results. Our results are in good agreement. We have also performed a pressure-induced variation of Debye temperature and have found a decrease in Debye temperature around 40 kbar in AlRE (RE=La, Ce, Pr) intermetallics.

First principles electronic and thermal properties of some AlRE intermetallics

Energy Technology Data Exchange (ETDEWEB)

Srivastava, Vipul [Department of Physics, Barkatullah University, Hoshangabad Road, Bhopal, Madhya Pradesh 462 026 (India)], E-mail: vips73@yahoo.com; Sanyal, Sankar P. [Department of Physics, Barkatullah University, Hoshangabad Road, Bhopal, Madhya Pradesh 462 026 (India); Rajagopalan, M. [Department of Physics, Anna University, Chennai-600 025 (India)

2008-10-01

A study on structural and electronic properties of non-magnetic cubic B{sub 2}-type AlRE (RE=Sc, Y, La, Ce, Pr and Lu) intermetallics has been done theoretically. The self-consistent tight binding linear muffin tin orbital method is used to describe the electronic properties of these intermetallics at ambient and at high pressure. These compounds show metallic behavior under ambient conditions. The variation of density of states under compression indicates some possibility of structural phase transformation in AlLa, AlCe and AlPr. Thermal properties like Debye temperature and Grueneisen constant are calculated at T=0 K and at ambient pressure within the Debye-Grueneisen model and compared with the others' theoretical results. Our results are in good agreement. We have also performed a pressure-induced variation of Debye temperature and have found a decrease in Debye temperature around 40 kbar in AlRE (RE=La, Ce, Pr) intermetallics.

First principles electronic and thermal properties of some AlRE intermetallics

International Nuclear Information System (INIS)

Srivastava, Vipul; Sanyal, Sankar P.; Rajagopalan, M.

2008-01-01

A study on structural and electronic properties of non-magnetic cubic B 2 -type AlRE (RE=Sc, Y, La, Ce, Pr and Lu) intermetallics has been done theoretically. The self-consistent tight binding linear muffin tin orbital method is used to describe the electronic properties of these intermetallics at ambient and at high pressure. These compounds show metallic behavior under ambient conditions. The variation of density of states under compression indicates some possibility of structural phase transformation in AlLa, AlCe and AlPr. Thermal properties like Debye temperature and Grueneisen constant are calculated at T=0 K and at ambient pressure within the Debye-Grueneisen model and compared with the others' theoretical results. Our results are in good agreement. We have also performed a pressure-induced variation of Debye temperature and have found a decrease in Debye temperature around 40 kbar in AlRE (RE=La, Ce, Pr) intermetallics

Strong, ductile, and thermally stable Cu-based metal-intermetallic nanostructured composites.

Science.gov (United States)

Dusoe, Keith J; Vijayan, Sriram; Bissell, Thomas R; Chen, Jie; Morley, Jack E; Valencia, Leopolodo; Dongare, Avinash M; Aindow, Mark; Lee, Seok-Woo

2017-01-09

Bulk metallic glasses (BMGs) and nanocrystalline metals (NMs) have been extensively investigated due to their superior strengths and elastic limits. Despite these excellent mechanical properties, low ductility at room temperature and poor microstructural stability at elevated temperatures often limit their practical applications. Thus, there is a need for a metallic material system that can overcome these performance limits of BMGs and NMs. Here, we present novel Cu-based metal-intermetallic nanostructured composites (MINCs), which exhibit high ultimate compressive strengths (over 2 GPa), high compressive failure strain (over 20%), and superior microstructural stability even at temperatures above the glass transition temperature of Cu-based BMGs. Rapid solidification produces a unique ultra-fine microstructure that contains a large volume fraction of Cu 5 Zr superlattice intermetallic compound; this contributes to the high strength and superior thermal stability. Mechanical and microstructural characterizations reveal that substantial accumulation of phase boundary sliding at metal/intermetallic interfaces accounts for the extensive ductility observed.

Intermetallic matrix composites; Proceedings of the MRS Symposium, San Francisco, CA, Apr. 18-20, 1990

International Nuclear Information System (INIS)

Anton, D.L.; Martin, P.L.; Miracle, D.B.; Mcmeeking, R.

1990-01-01

The present volume on intermetallic matrix composites discusses the modeling, processing, microstructure/property relationships, and compatibility of intermetallic matrix composites. Attention is given to models for the strength of ductile matrix composites, innovative processing techniques for intermetallic matrix composites, ductile phase toughening of brittle intermetallics, and reactive synthesis of NbAl3 matrix composites. Topics addressed include solidification processing of NbCr2 alloys, Ta and Nb reinforced MoSi2, the microstructure and mechanical behavior of Ni3Al-matrix composites, and ductile-phase toughening of Cr3Si with chromium. Also discussed are dislocation morphologies in TiB2/NiAl, the development of highly impact resistant NiAl matrix composites, the effect of notches on the fatigue life of the SCS-6Ti3Al composite, and the chemical stability of fiber-metal matrix composites

Atom probe tomography of intermetallic phases and interfaces formed in dissimilar joining between Al alloys and steel

International Nuclear Information System (INIS)

Lemmens, B.; Springer, H.; Duarte, M.J.; De Graeve, I.; De Strycker, J.; Raabe, D.; Verbeken, K.

2016-01-01

While Si additions to Al are widely used to reduce the thickness of the brittle intermetallic seam formed at the interface during joining of Al alloys to steel, the underlying mechanisms are not clarified yet. The developed approach for the site specific atom probe tomography analysis revealed Si enrichments at grain and phase boundaries between the θ (Fe 4 Al 13 ) and η (Fe 2 Al 5 ) phase, up to about ten times that of the concentration in Al. The increase in Si concentration could play an important role for the growth kinetics of the intermetallic phases formed for example in hot-dip aluminizing of steel. - Highlights: •Si additions to Al reduce thickness of intermetallic seam in joining with steel. •Approach developed for the site specific APT analysis of the intermetallic seam •Si enrichment at grain and phase boundaries possibly affects growth of intermetallics.

Reaction kinetics of the formation of intermetallic Fe – Zn during hot - dip galvanizing of steel

Directory of Open Access Journals (Sweden)

P. Pokorny

2016-01-01

Full Text Available This review article mainly describes the composition of intermetallic Fe - Zn, i.e. zeta (ζ, delta (δ1k + δ1p, gamma1 (Γ1 and gamma (Γ on galvanized steel during low temperature galvanization (t ~ 450 °C. It gives detailed the formation, growth of individual phases during galvanization and their interaction. In terms of the kinetics, the formation of the coating is defined by a parabolic kinetic equation of the growth of different intermetallic phases under ideal conditions. From the available literature the rate constants of the formation of individual intermetallic phases and also for the total coating are cited. The composition of the intermetallic phases, iron content, crystal structure, and group symmetry in which the surface of galvanized steel forms.

Toughening and creep in multiphase intermetallics through ...

Indian Academy of Sciences (India)

It has however often been the case that the process of ductilisation or toughening has also led to a decrease in high temperature properties, especially creep. In this paper we describe approaches to the ductilisation of two different classes of intermetallic alloys through alloying to introduce beneficial, second phase effects.

Large positive magnetoresistance in intermetallic compound NdCo2Si2

Science.gov (United States)

Roy Chowdhury, R.; Dhara, S.; Das, I.; Bandyopadhyay, B.; Rawat, R.

2018-04-01

The magnetic, magneto-transport and magnetocaloric properties of antiferromagnetic intermetallic compound NdCo2Si2 (TN = 32K) have been studied. The compound yields a positive magnetoresistance (MR) of about ∼ 123 % at ∼ 5K in 8 T magnetic field. The MR value is significantly large vis - a - vis earlier reports of large MR in intermetallic compounds, and possibly associated with the changes in magnetic structure of the compound. The large MR value can be explained in terms of field induced pseudo-gaps on Fermi surface.

Abrasive wear of intermetallics

International Nuclear Information System (INIS)

Hawk, J.A.; Alman, D.E.; Wilson, R.D.

1995-01-01

The US Bureau of Mines is investigating the wear behavior of a variety of advanced materials. Among the many materials under evaluation are intermetallic alloys based on the compounds: Fe 3 Al, Ti 3 Al, TiAl, Al 3 Ti, NiAl and MoSi 2 . The high hardness, high modulus, low density, and superior environmental stability of these compounds make them attractive for wear materials. This paper reports on the abrasive wear of alloys and composites based on the above compounds. The abrasive wear behavior of these alloys and composites are compared to other engineering materials used in wear applications

Mechanical and oxidation properties of some B2 rare earth–magnesium intermetallic

Energy Technology Data Exchange (ETDEWEB)

Stumphy, Brad [Iowa State Univ., Ames, IA (United States)

2006-12-15

The remainder of Chapter 1 provides background information on three main topics. First is a discussion about the basic structure and composition of binary B2 intermetallic compounds. Second, the mechanical properties of intermetallics are examined, starting with the cause for the typically inherent brittleness observed in B2 intermetallics. A number of B2 compounds have been found to possess an abnormal level of ductility compared to other intermetallics in this class, including a handful of other rare earth–non-rare earth (RM) B2 line compounds, and these findings are also discussed. Finally, oxidation studies of rare earth metals, focusing on yttrium and cerium, as well as magnesium and some B2 materials are discussed. Chapter 2 is an in-depth look into certain aspects of the laboratory work done during this study. The many challenges and difficulties encountered required that a variety of laboratory techniques be attempted in the making, processing, and testing of these two intermetallic materials. The results and ensuing discussion for the mechanical testing that was performed are found in Chapter 3. Tensile and compression testing results for YMg are shown first, followed by those for CeMg. Some samples were made using electrical discharge machining (EDM) while others were polished into the desired shape. A scanning electron microscope (SEM) was utilized to inspect surfaces of the tensile and compression samples. Hardness values and attempts to determine fracture toughness are also recorded before beginning the discussion. Chapter 4 follows the same basic format for the oxidation study portion of the research. Oxidation curves for CeMg are followed by a qualitative chemical analysis using energy dispersive spectroscopy (EDS). The YMg oxidation curves are shown next followed by an x-ray diffraction (XRD) analysis of the oxidation process for this material and a discussion of the results. Chapter 5 is a summary of the research performed in the mechanical and

EFFECT OF INTERMETALLIC PHASES ON CORROSION BEHAVIOR AND MECHANICAL PROPERTIES OF DUPLEX STAINLESS STEEL AND SUPER-DUPLEX STAINLESS STEEL

Directory of Open Access Journals (Sweden)

Prabhu Paulraj

2015-08-01

Full Text Available Duplex Stainless Steels (DSS and Super Duplex Stainless Steel (SDSS have excellent integration of mechanical and corrosion properties. However, the formation of intermetallic phases is a major problem in their usage. The mechanical and corrosion properties are deteriorated due to the presence of intermetallic phases. These phases are induced during welding, prolonged exposure to high temperatures, and improper heat treatments. The main emphasis of this review article is on intermetallic phases and their effects on corrosion and mechanical properties. First the effect of various alloying elements on DSS and SDSS has been discussed followed by formation of various intermetallic phases. The intermetallic phases affect impact toughness and corrosion resistance significantly. Their deleterious effect on weldments has also been reviewed.

Pressure-induced phenomena in U intermetallics

Czech Academy of Sciences Publication Activity Database

Sechovský, V.; Honda, F.; Prokeš, K.; Syshchenko, O.; Andreev, Alexander V.; Kamarád, Jiří

2003-01-01

Roč. 34, č. 2 (2003), s. 1377-1386 ISSN 0587-4254. [International Conference on Strongly Correlated Electron Systems (SCES 02). Cracow, 10.07.2002-13.07.2002] R&D Projects: GA ČR GA202/02/0739 Institutional research plan: CEZ:AV0Z1010914; CEZ:MSM 113200002 Keywords : pressure effect * intermetallics Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.752, year: 2003

Corrosion Study and Intermetallics Formation in Gold and Copper Wire Bonding in Microelectronics Packaging

Directory of Open Access Journals (Sweden)

Christopher Breach

2013-07-01

Full Text Available A comparison study on the reliability of gold (Au and copper (Cu wire bonding is conducted to determine their corrosion and oxidation behavior in different environmental conditions. The corrosion and oxidation behaviors of Au and Cu wire bonding are determined through soaking in sodium chloride (NaCl solution and high temperature storage (HTS at 175 °C, 200 °C and 225 °C. Galvanic corrosion is more intense in Cu wire bonding as compared to Au wire bonding in NaCl solution due to the minimal formation of intermetallics in the former. At all three HTS annealing temperatures, the rate of Cu-Al intermetallic formation is found to be three to five times slower than Au-Al intermetallics. The faster intermetallic growth rate and lower activation energy found in this work for both Au/Al and Cu/Al as compared to literature could be due to the thicker Al pad metallization which removed the rate-determining step in previous studies due to deficit in Al material.

Chemistry and Properties of Complex Intermetallics from Metallic Fluxes

Energy Technology Data Exchange (ETDEWEB)

Kanatzidis, Mercouri G. [Northwestern Univ., Evanston, IL (United States)

2015-03-28

This project investigated the reaction chemistry and synthesis of new intermetallic materials with complex compositions and structures using metallic fluxes as solvents. It was found that the metallic fluxes offer several key advantages in facilitating the formation and crystal growth of new materials. The fluxes mostly explored were liquid aluminum, gallium and indium. The main purpose of this project was to exploit the potential of metallic fluxes as high temperature solvent for materials discovery in the broad class of intermetallics. This work opened new paths to compound formation. We discovered many new Si (or Ge)-based compounds with novel structures, bonding and physicochemical properties. We created new insights about the reaction chemistry that is responsible for stabilizing the new materials. We also studied the structural and compositional relationships to understand their properties. We investigated the use of Group-13 metals Al, Ga and In as solvents and have generated a wide variety of new results including several new ternary and quaternary materials with fascinating structures and properties as well as new insights as to how these systems are stabilized in the fluxes. The project focused on reactions of metals from the rare earth element family in combination with transition metals with Si and Ge. For example molten gallium has serves both as a reactive and non-reactive solvent in the preparation and crystallization of intermetallics in the system RE/M/Ga/Ge(Si). Molten indium behaves similarly in that it too is an excellent reaction medium, but it gives compounds that are different from those obtained from gallium. Some of the new phase identified in the aluminide class are complex phases and may be present in many advanced Al-matrix alloys. Such phases play a key role in determining (either beneficially or detrimentally) the mechanical properties of advanced Al-matrix alloys. This project enhanced our basic knowledge of the solid state chemistry

Composites having an intermetallic containing matrix

International Nuclear Information System (INIS)

Nagle, D.C.; Brupbacher, J.M.; Christodoulou, L.

1990-01-01

This paper describes a composite material. It comprises: a dispersion of in-situ precipitated second phase particles selected from the group consisting of borides, carbides, nitrides, and sulfides, in an intermetallic containing matrix selected from the group consisting of the aluminides, silicides, and beryllides of nickel, copper, titanium, cobalt, iron, platinum, gold, silver, niobium, tantalum, zinc, molybdenum, hafnium, tin, tungsten, lithium, magnesium, thorium, chromium, vanadium, zirconium, and manganese

Single crystal growth of europium and ytterbium based intermetallic ...

Indian Academy of Sciences (India)

The difference between an intermetallic compound and a regular metal (e.g., ... intriguing properties, there have not been any reports of thorough investigations of .... scanning electron microscope (SEM) equipped with an energy dispersive ...

Intermetallic compounds of Ni and Ga as catalysts for the synthesis of methanol

DEFF Research Database (Denmark)

Sharafutdinov, Irek; Elkjær, Christian Fink; de Carvalho, Hudson Wallace Pereira

2014-01-01

In this work, we present a detailed study of the formation of supported intermetallic Ni–Ga catalysts for CO2 hydrogenation to methanol. The bimetallic phase is formed during a temperature-programmed reduction of the metal nitrates. By utilizing a combination of characterization techniques......, in particular in situ and ex situ X-ray diffraction, in situ X-ray absorption spectroscopy, transmission electron microscopy combined with electron energy loss spectroscopy and X-ray fluorescence, we have studied the formation of intermetallic Ni–Ga catalysts of two compositions: NiGa and Ni5Ga3. These methods...... demonstrate that the catalysts with the desired intermetallic phase and composition are formed upon reduction in hydrogen and enable us to propose a mechanism of the Ni–Ga nanoparticles formation. By studying the effect of calcination prior to catalyst reduction, we show that the reactivity depends...

3D study of intermetallics and their effect on the corrosion morphology of rheocast aluminium alloy

International Nuclear Information System (INIS)

Mingo, B.; Arrabal, R.; Pardo, A.; Matykina, E.; Skeldon, P.

2016-01-01

In the present study, the effect of heat treatment T6.1 on the microstructure and corrosion behaviour of rheocast aluminium alloy A356 is investigated on the basis of 2D/3D characterization techniques and electrochemical and SKPFM measurements. Heat treatment strengthens the α-Al matrix, modifies the intermetallic particles and spheroidizes eutectic Si. These changes do not modify significantly the corrosion behaviour of the alloy. 3D SEM-Tomography clearly shows that the corrosion advances in the shape of narrow paths between closely spaced intermetallics without a major influence of eutectic Si. - Highlights: • T6.1 spheroidizes Si, strengthens the matrix and modifies the intermetallics. • Electrochemical behaviour of untreated and heat-treated alloys is similar. • 3D SEM-Tomography provides additional information on the corrosion morphology. • Corrosion advances as paths between intermetallics with little influence of Si.

An Investigation of the Microstructure of an Intermetallic Layer in Welding Aluminum Alloys to Steel by MIG Process.

Science.gov (United States)

Nguyen, Quoc Manh; Huang, Shyh-Chour

2015-12-02

Butt joints of A5052 aluminum alloy and SS400 steel, with a new type of chamfered edge, are welded by means of metal inert gas welding and ER4043 Al-Si filler metal. The microhardness and microstructure of the joint are investigated. An intermetallic layer is found on the surface of the welding seam and SS400 steel sheet. The hardness of the intermetallic layer is examined using the Vickers hardness test. The average hardness values at the Intermetallic (IMC) layer zone and without the IMC layer zone were higher than that of the welding wire ER4043. The tensile strength test showed a fracture at the intermetallic layer when the tensile strength is 225.9 MPa. The tensile value test indicated the average of welds was equivalent to the 85% tensile strength of the A5052 aluminum alloy. The thickness of the intermetallic layers is non-uniform at different positions with the ranges from 1.95 to 5 μm. The quality of the butt joint is better if the intermetallic layer is minimized. The Si crystals which appeared at the welding seam, indicating that this element participated actively during the welding process, also contributed to the IMC layer's formation.

Structural and Electronic Investigations of Complex Intermetallic Compounds

Energy Technology Data Exchange (ETDEWEB)

Ko, Hyunjin [Iowa State Univ., Ames, IA (United States)

2008-01-01

In solid state chemistry, numerous investigations have been attempted to address the relationships between chemical structure and physical properties. Such questions include: (1) How can we understand the driving forces of the atomic arrangements in complex solids that exhibit interesting chemical and physical properties? (2) How do different elements distribute themselves in a solid-state structure? (3) Can we develop a chemical understanding to predict the effects of valence electron concentration on the structures and magnetic ordering of systems by both experimental and theoretical means? Although these issues are relevant to various compound classes, intermetallic compounds are especially interesting and well suited for a joint experimental and theoretical effort. For intermetallic compounds, the questions listed above are difficult to answer since many of the constituent atoms simply do not crystallize in the same manner as in their separate, elemental structures. Also, theoretical studies suggest that the energy differences between various structural alternatives are small. For example, Al and Ga both belong in the same group on the Periodic Table of Elements and share many similar chemical properties. Al crystallizes in the fcc lattice with 4 atoms per unit cell and Ga crystallizes in an orthorhombic unit cell lattice with 8 atoms per unit cell, which are both fairly simple structures (Figure 1). However, when combined with Mn, which itself has a very complex cubic crystal structure with 58 atoms per unit cell, the resulting intermetallic compounds crystallize in a completely different fashion. At the 1:1 stoichiometry, MnAl forms a very simple tetragonal lattice with two atoms per primitive unit cell, while MnGa crystallizes in a complicated rhombohedral unit cell with 26 atoms within the primitive unit cell. The mechanisms influencing the arrangements of atoms in numerous crystal structures have been studied theoretically by calculating electronic

Vacancies and atomic processes in intermetallics - From crystals to quasicrystals and bulk metallic glasses

Energy Technology Data Exchange (ETDEWEB)

Schaefer, Hans-Eckhardt [Institute of Theoretical and Applied Physics, Stuttgart University, Pfaffenwaldring 57, 70569 Stuttgart (Germany); Baier, Falko [Voith Turbo Comp., Alexanderstr. 2, 89552 Heidenheim (Germany); Mueller, Markus A. [GFT Technologies A. G., Filderhauptstr. 142, 70599 Stuttgart (Germany); Reichle, Klaus J. [Philipp-Matthaeus-Hahn School, Jakob-Beutter-Str. 15, 72336 Balingen (Germany); Reimann, Klaus [NXP Semiconductors, Central Research and Development, High Tech Campus 4, 5656 AE Eindhoven (Netherlands); Rempel, Andrey A. [Institute of Solid State Chemistry, Russian Academy of Sciences, Ul. Pervomaiskaya 91, 620041 Ekaterinburg (Russian Federation); Sato, Kiminori [Tokyo Gakugei University, Nukuikita 4-1-1, Koganei, Tokyo 184-8501 (Japan); Ye, Feng [State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, 30 Xue Yuan Road, Beijing 100083 (China); Zhang, Xiangyi [Yanshan University, Qinhuangdao 066004 (China); Sprengel, Wolfgang [Institute of Materials Physics, Graz University of Technology, Petersgasse 16, 8010 Graz (Austria)

2011-10-15

A review is given on atomic vacancies in intermetallic compounds. The intermetallic compounds cover crystalline, quasicrystalline, and bulk metallic glass (BMG) structures. Vacancies can be specifically characterized by their positron lifetimes, by the coincident measurement of the Doppler broadening of the two quanta emitted by positron-electron annihilation, or by time-differential dilatometry. By these techniques, high concentrations and low mobilities of thermal vacancies were found in open-structured B2 intermetallics such as FeAl or NiAl, whereas the concentrations of vacancies are low and their mobilities high in close-packed structure as, e.g., L1{sub 2}-Ni{sub 3}Al. The activation volumes of vacancy formation and migration are determined by high-pressure experiments. The favorable sublattice for vacancy formation is found to be the majority sublattice in Fe{sub 61}Al{sub 39} and in MoSi{sub 2}. In the icosahedral quasicrystal Al{sub 70}Pd{sub 21}Mn{sub 9} the thermal vacancy concentration is low, whereas in the BMG Zr{sub 57}Cu{sub 15.4}Ni{sub 12.6}Nb{sub 3}Al{sub 10} thermal vacancies are found in high concentrations with low mobilities. This may determine the basic mechanisms of the glass transition. Making use of the experimentally determined vacancy data, the main features of atomic diffusion studies in crystalline intermetallics, in quasicrystals, and in BMGs can be understood. Manfred Faehnle and his group have substantially contributed to the theoretical understanding of vacancies and diffusion mechanisms in intermetallics. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

Structural plasticity: how intermetallics deform themselves in response to chemical pressure, and the complex structures that result.

Science.gov (United States)

Berns, Veronica M; Fredrickson, Daniel C

2014-10-06

Interfaces between periodic domains play a crucial role in the properties of metallic materials, as is vividly illustrated by the way in which the familiar malleability of many metals arises from the formation and migration of dislocations. In complex intermetallics, such interfaces can occur as an integral part of the ground-state crystal structure, rather than as defects, resulting in such marvels as the NaCd2 structure (whose giant cubic unit cell contains more than 1000 atoms). However, the sources of the periodic interfaces in intermetallics remain mysterious, unlike the dislocations in simple metals, which can be associated with the exertion of physical stresses. In this Article, we propose and explore the concept of structural plasticity, the hypothesis that interfaces in complex intermetallic structures similarly result from stresses, but ones that are inherent in a defect-free parent structure, rather than being externally applied. Using DFT-chemical pressure analysis, we show how the complex structures of Ca2Ag7 (Yb2Ag7 type), Ca14Cd51 (Gd14Ag51 type), and the 1/1 Tsai-type quasicrystal approximant CaCd6 (YCd6 type) can all be traced to large negative pressures around the Ca atoms of a common progenitor structure, the CaCu5 type with its simple hexagonal 6-atom unit cell. Two structural paths are found by which the compounds provide relief to the Ca atoms' negative pressures: a Ca-rich pathway, where lower coordination numbers are achieved through defects eliminating transition metal (TM) atoms from the structure; and a TM-rich path, along which the addition of spacer Cd atoms provides the Ca coordination environments greater independence from each other as they contract. The common origins of these structures in the presence of stresses within a single parent structure highlights the diverse paths by which intermetallics can cope with competing interactions, and the role that structural plasticity may play in navigating this diversity.

Oxygen stabilized rare-earth iron intermetallic compounds

International Nuclear Information System (INIS)

Dariel, M.P.; Malekzadeh, M.; Pickus, M.R.

1975-10-01

A new, oxygen-stabilized intermetallic compound was identified in sintered, pre-alloyed rare-earth iron powder samples. Its composition corresponds to formula R 12 Fe 32 O 2 and its crystal structure belongs to space group Im3m. The presence of these compounds was observed, so far, in several R--Fe--O systems, with R = Gd, Tb, Dy, Ho, Er, and Y

Development of intermetallic coatings for fusion power applications

International Nuclear Information System (INIS)

Park, J.H.; Domenico, T.; Dragel, G.; Clark, R.

1994-03-01

In the design of liquid-metal cooling systems, corrosion resistance of structural materials and magnetohydrodynamic (MHD) force and its subsequent influence on thermal hydraulics and corrosion are major concerns. The objective of this study is to develop stable corrosion-resistant electrical insulator coatings at the liquid-metal/structural-material interface, with emphasis on electrically insulating coatings that prevent adverse MHD-generated currents from passing through the structural walls. Vanadium and V-base alloys are potential materials for structural applications in a fusion reactor. Insulator coatings inside the tubing are required when the system is cooled by liquid metals. Various intermetallic films were produced on V, V-t, and V-20 Ti, V-5Cr-t and V-15Cr-t, and Ti, and Types 304 and 316 stainless steel. The intermetallic layers were developed by exposure of the materials to liquid lithium of 3--5 at.% and containing dissolved metallic solutes at temperatures of 416--880 degrees C. Subsequently, electrical insulator coatings were produced by reaction of the reactive layers with dissolved nitrogen in liquid lithium or by air oxidation under controlled conditions at 600--1000 degrees C. These reactions converted the intermetallic layers to electrically insulating oxide/nitride or oxy-nitride layers. This coating method could be applied to a commercial product. The liquid metal can be used over and over because only the solutes are consumed within the liquid metal. The technique can be applied to various shapes because the coating is formed by liquid-phase reaction. This paper will discuss initial results on the nature of the coatings and their in-situ electrical resistivity characteristics in liquid lithium at high temperatures

Effect of Sr and solidification conditions on characteristics of intermetallic in Al-Si 319 industrial alloys

International Nuclear Information System (INIS)

Espinoza-Cuadra, J.; Gallegos-Acevedo, P.; Mancha-Molinar, H.; Picado, A.

2010-01-01

An experimental study was carried out to determine the effect of strontium (Sr) on the characteristic of intermetallic phases, particularly the Al 5 FeSi phase which present morphology of platelets or needle-like. The results showed that within the range of variables studied, the modification process caused the disappearance of the needles and only occur the precipitation of phase α (chinese script-like). Refinement of the intermetallic phases occurs in conjunction with the refinement in grain size. Both parameters depend strongly on local cooling rate (T), temperature gradient (G) and apparent rate of solidification front (V). In the case of equiaxed structures the refinement of grain size and intermetallic occurs with increasing local cooling rate and temperature gradient and decrease the apparent rate of solidification front. In the case of columnar structures, refinement of grains and intermetallic requires the increase in values of the three variables indicated. Moreover, the addition of Sr resulted in the modification of silicon eutectic, as noted in others research works.

Nanoscale grain growth behaviour of CoAl intermetallic synthesized ...

Indian Academy of Sciences (India)

Grain growth behaviour of the nanocrystalline CoAl intermetallic compound synthesized by mechanical alloying has been studied by isothermal annealing at different temperatures and durations. X-ray diffraction method was employed to investigate structural evolutions during mechanical alloying and annealing processes.

Nanoscale grain growth behaviour of CoAl intermetallic synthesized ...

Indian Academy of Sciences (India)

Administrator

Abstract. Grain growth behaviour of the nanocrystalline CoAl intermetallic compound synthesized by mechanical alloying has been studied by isothermal annealing at different temperatures and durations. X-ray diffraction method was employed to investigate structural evolutions during mechanical alloying and anneal-.

Thermal, structural, and magnetic studies of metals and intermetallic compounds. Final report

International Nuclear Information System (INIS)

Wallace, W.E.; Craig, R.S.; Rao, V.U.S.

1976-01-01

The powerful magnetism of certain intermetallics, e.g., SmCo 5 , has been established to originate with the powerful magnetic anisotropy of SmCo 5 , not its large magnetization. The anisotropy is, in turn, a crystal field effect. The crystal field interaction has been elucidated by the method of quantum mechanics. Studies of the systems RFe 2 , RFe 3 , RCo 3 , and R 2 Co 7 (R = a rare earth, Y or Th) reveals them to be important for hydrogen storage. In addition, important effects associated with hydrogenation of metals have been found--great enhancement of magnetization of certain systems (e.g., ErFe 2 ) and substantial increase in superconducting transition temperatures (e.g., Zr/sub .5/H/sub .5/V 2 ). Results of studies suggest that the surfaces of rare earth intermetallics are atypical. The spectrum of properties exhibited by the rare earth intermetallics suggests their utility in the efficient capture and storage of solar energy and the use of it for powering a vehicle. These aspects of the systems warrant further attention

A new method to estimate the atomic volume of ternary intermetallic compounds

International Nuclear Information System (INIS)

Pani, M.; Merlo, F.

2011-01-01

The atomic volume of an A x B y C z ternary intermetallic compound can be calculated starting from volumes of some proper A-B, A-C and B-C binary phases. The three methods by Colinet, Muggianu and Kohler, originally used to estimate thermodynamic quantities, and a new method here proposed, were tested to derive volume data in eight systems containing 91 ternary phases with the known structure. The comparison between experimental and calculated volume values shows the best agreement both for the Kohler method and for the new proposed procedure. -- Graphical abstract: Synopsys: the volume of a ternary intermetallic compound can be calculated starting from volumes of some binary phases, selected by the methods of Colinet, Muggianu, Kohler and a new method proposed here. The so obtained values are compared with the experimental ones for eight ternary systems. Display Omitted Research highlights: → The application of some thermodinamic methods to a crystallochemical problem. → The prevision of the average atomic volume of ternary intermetallic phases. → The proposal of a new procedure to select the proper starting set of binary phases.

Modification of NiAl intermetallic coatings processed by PTA with chromium carbides

International Nuclear Information System (INIS)

Yano, Diogo Henrique Sepel; Brunetti, Cristiano; Pintaude, Giuseppe; Oliveira, Ana Sofia Climaco Monteiro d'

2010-01-01

Equipment that operate under high-temperatures can be protected with NiAl intermetallic coatings mainly because of their metallurgical stability. This study as it evaluates the effect of chromium carbide added to Ni-Al intermetallic coatings processed by PTA. Three Ni-Al-Cr23C6 powder mixtures with different carbide fractions (15, 30 and 45 wt%) and another without carbides were deposited by PTA on an AISI 304 stainless steel plate, using two different current intensities (100 and 150A). Coatings were evaluated regarding the presence of welding defects, and resultant microstructures were characterized by X-ray diffraction and scanning electron microscopy. Vickers microhardness and EDS chemical composition were also determined. NiAl and Cr_7C_3 development was confirmed by X-ray diffraction analysis. A combination of NiAl/Cr-Fe-Ni phases was identified. The hardness was strongly related to the formed phases and their amounts. Besides presenting advances toward the development of coatings which can withstand severe operation conditions, the present study shows that PTA hardfacing is able to produce reinforced intermetallic coatings for high-temperature applications. (author)

EFFECT OF INTERMETALLIC PHASES ON CORROSION BEHAVIOR AND MECHANICAL PROPERTIES OF DUPLEX STAINLESS STEEL AND SUPER-DUPLEX STAINLESS STEEL

OpenAIRE

Prabhu Paulraj; Rajnish Garg

2015-01-01

Duplex Stainless Steels (DSS) and Super Duplex Stainless Steel (SDSS) have excellent integration of mechanical and corrosion properties. However, the formation of intermetallic phases is a major problem in their usage. The mechanical and corrosion properties are deteriorated due to the presence of intermetallic phases. These phases are induced during welding, prolonged exposure to high temperatures, and improper heat treatments. The main emphasis of this review article is on intermetallic pha...

Magnetic and electronic properties of some actinide intermetallic compounds

International Nuclear Information System (INIS)

Yaar, Ilan

1992-06-01

The electronic structure and magnetic properties of the light actinide intermetallic compounds are often related to interplay between localized and itinerant (band like) behavior of the 5f- electrons. In the present work, the properties of some actinide, mainly Np, intermetallic compounds were studied by Mossbauer effect, ac and dc susceptibility, X-ray and Neutron diffraction techniques. 1. NpX 2 (X=Ga,Si) - Both compounds order ferromagnetically at TC=55(2) and 48(2) K respectively. A comparison of our data with the results for other NpX 2 (X=Al,As,Sb,Tl) compounds indicates that NpGa 2 is a highly localized 5f electron system, whereas in NpSi 2 the 5f electrons are partially delocalized. The magnetic properties of NpX 2 compounds can neither be consistently explained within the conventional crystal electric field picture (CEF) nor by takink into account hybridization dressing of local spin density models. 2. NpX 3 (X=Ga,Si,In,Al) in the cubic AuCu 3 (Pm3m) crystallographic structure - From the Mossbauer isomer shift (IS) data we argue that the Np ion in the NpX 3 family is close to the formal 3+ (5I 4 ) charge state. The magnetic moment of the Np in NpSi 3 is totally suppressed whereas in NpGa 3 and NpAl 3 a localized (narrow band) moment is established. However, in NpIn 3 at 4.2 K, a modulated magnetic moment (0-1.5μB) is observed. Comparing the magnetic behavior of the NpX 3 family (X=Si,Ge,Ga, Al,In and Sn), we find an impressive variation of the magnetic properties, from temperature independent paramagnetism (TIP), localized and modulated ordered moments, to the formation of a concentrated Kondo lattice. Hybridization of 5f electrons with ligand electrons appears to play a crucial role in establishing these magnetic properties. However, at present a consistent theoretical picture can not be drawn. 3. XFe 4 Al 8 (X=Ho,Np,U) spin galss (SG) systems in the ThMn 12 (I 4 /mmm) crystallographic structure - Localized and itinerant behaviour of the f electrons

Microstructure and Tribological Properties of Mo–40Ni–13Si Multiphase Intermetallic Alloy

Science.gov (United States)

Song, Chunyan; Wang, Shuhuan; Gui, Yongliang; Cheng, Zihao; Ni, Guolong

2016-01-01

Intermetallic compounds are increasingly being expected to be utilized in tribological environments, but to date their implementation is hindered by insufficient ductility at low and medium temperatures. This paper presents a novel multiphase intermetallic alloy with the chemical composition of Mo–40Ni–13Si (at %). Microstructure characterization reveals that a certain amount of ductile Mo phases formed during the solidification process of a ternary Mo–Ni–Si molten alloy, which is beneficial to the improvement of ductility of intermetallic alloys. Tribological properties of the designed alloy—including wear resistance, friction coefficient, and metallic tribological compatibility—were evaluated under dry sliding wear test conditions at room temperature. Results suggest that the multiphase alloy possesses an excellent tribological property, which is attributed to unique microstructural features and thereby a good combination in hardness and ductility. The corresponding wear mechanism is explained by observing the worn surface, subsurface, and wear debris of the alloy, which was found to be soft abrasive wear. PMID:28774106

Microstructure and Tribological Properties of Mo-40Ni-13Si Multiphase Intermetallic Alloy.

Science.gov (United States)

Song, Chunyan; Wang, Shuhuan; Gui, Yongliang; Cheng, Zihao; Ni, Guolong

2016-12-06

Intermetallic compounds are increasingly being expected to be utilized in tribological environments, but to date their implementation is hindered by insufficient ductility at low and medium temperatures. This paper presents a novel multiphase intermetallic alloy with the chemical composition of Mo-40Ni-13Si (at %). Microstructure characterization reveals that a certain amount of ductile Mo phases formed during the solidification process of a ternary Mo-Ni-Si molten alloy, which is beneficial to the improvement of ductility of intermetallic alloys. Tribological properties of the designed alloy-including wear resistance, friction coefficient, and metallic tribological compatibility-were evaluated under dry sliding wear test conditions at room temperature. Results suggest that the multiphase alloy possesses an excellent tribological property, which is attributed to unique microstructural features and thereby a good combination in hardness and ductility. The corresponding wear mechanism is explained by observing the worn surface, subsurface, and wear debris of the alloy, which was found to be soft abrasive wear.

Microstructure and Tribological Properties of Mo–40Ni–13Si Multiphase Intermetallic Alloy

Directory of Open Access Journals (Sweden)

Chunyan Song

2016-12-01

Full Text Available Intermetallic compounds are increasingly being expected to be utilized in tribological environments, but to date their implementation is hindered by insufficient ductility at low and medium temperatures. This paper presents a novel multiphase intermetallic alloy with the chemical composition of Mo–40Ni–13Si (at %. Microstructure characterization reveals that a certain amount of ductile Mo phases formed during the solidification process of a ternary Mo–Ni–Si molten alloy, which is beneficial to the improvement of ductility of intermetallic alloys. Tribological properties of the designed alloy—including wear resistance, friction coefficient, and metallic tribological compatibility—were evaluated under dry sliding wear test conditions at room temperature. Results suggest that the multiphase alloy possesses an excellent tribological property, which is attributed to unique microstructural features and thereby a good combination in hardness and ductility. The corresponding wear mechanism is explained by observing the worn surface, subsurface, and wear debris of the alloy, which was found to be soft abrasive wear.

Environmental embrittlement of intermetallic compounds in Fe-Al alloys

Institute of Scientific and Technical Information of China (English)

张建民; 张瑞林; S.H.YU; 余瑞璜

1996-01-01

First,it is proposed that hydrogen atoms occupy the interstitial sites in Fe3Al and FeAl.Then the environmental embrittlement of intermetallic compounds in Fe-Al alloys is studied in the light of calculated valence electron structures and bond energy of Fe3Al and FeAl containing hydrogen atoms.From the analyses it is found that the states of metal atoms will change,in which more lattice electrons will become covalent electrons to bond with hydrogen atoms when the atomic hydrogen diffuses into the intermetallic compounds in Fe-Al alloys,which will result in the decrease of local metallicity in Fe3Al and FeAl.Meanwhile,it is found that the crystal will easily cleave since solute hydrogen bonds with metal atoms and severely anisotropic bonds form.As a conclusion,these factors result in the environmental embrittlement of Fe3Al and FeAl.

X-ray diffraction and high resolution transmission electron microscopy characterization of intermetallics formed in Fe/Ti nanometer-scale multilayers during thermal annealing

International Nuclear Information System (INIS)

Wu, Z.L.; Peng, T.X.; Cao, B.S.; Lei, M.K.

2009-01-01

Intermetallics formation in the Fe/Ti nanometer-scale multilayers magnetron-sputtering deposited on Si(100) substrate during thermal annealing at 623-873 K was investigated by using small and wide angle X-ray diffraction and cross-sectional high-resolution transmission electron microscopy. The Fe/Ti nanometer-scale multilayers were constructed with bilayer thickness of 16.2 nm and the sublayer thickness ratio of 1:1. At the annealing temperature of 623 K, intermetallics FeTi were formed by nucleation at the triple joins of α-Fe(Ti)/α-Ti interface and α-Ti grain boundary with an orientational correlation of FeTi(110)//α-Ti(100) and FeTi[001]//α-Ti[001] to adjacent α-Ti grains. The lateral growth of intermetallics FeTi which is dependent on the diffusion path of Ti led to a coalescence into an intermetallic layer. With an increase in the annealing temperature, intermetallics Fe 2 Ti were formed between the intermetallics FeTi and the excess Fe due to the limitation of Fe and Ti atomic concentrations, resulting in the coexistence of intermetallics FeTi and Fe 2 Ti. It was found that the low energy interface as well as the dominant diffusion path constrained the nucleation and growth of intermetallics during interfacial reaction in the nanometer-scale metallic multilayers.

Results on powder injection molding of Ni[sub 3]Al and application to other intermetallic compositions

Energy Technology Data Exchange (ETDEWEB)

Cooper, R.M.

1992-01-01

Net forming processes are under development to allow affordable production of intermetallic components. Powder injection molding (PIM) mav be employed for the production of complex-shaped intermetallic geometries. Proper choice of powder parameters and processing conditions can lead to the formation of fullv dense structures through pressure-less sintering. In this study, Ni[sub 3]Al with 0.04 wt.-% boron has been successfully injection molded and sintered to full density. A yield strength of 340 MPa, ultimate tensile strength (UTS) of 591 MPa, and 8% elongation were attained for injection molded and sintered tensile bars. Powder characteristics and sintering behavior are given for the nickel aluminide employed in this study to highlight the powder attributes needed for injection molding. Molding parameters, debinding and sintering schedules, along, with mechanical properties are presented to indicate the viability of PIM for intermetallics. This approach based on the understanding of key powder characteristics and use of the reactive synthesis powder process mav be extended to the successful injection molding of other intermetallic systems.

Results on powder injection molding of Ni{sub 3}Al and application to other intermetallic compositions

Energy Technology Data Exchange (ETDEWEB)

Cooper, R.M.

1992-12-31

Net forming processes are under development to allow affordable production of intermetallic components. Powder injection molding (PIM) mav be employed for the production of complex-shaped intermetallic geometries. Proper choice of powder parameters and processing conditions can lead to the formation of fullv dense structures through pressure-less sintering. In this study, Ni{sub 3}Al with 0.04 wt.-% boron has been successfully injection molded and sintered to full density. A yield strength of 340 MPa, ultimate tensile strength (UTS) of 591 MPa, and 8% elongation were attained for injection molded and sintered tensile bars. Powder characteristics and sintering behavior are given for the nickel aluminide employed in this study to highlight the powder attributes needed for injection molding. Molding parameters, debinding and sintering schedules, along, with mechanical properties are presented to indicate the viability of PIM for intermetallics. This approach based on the understanding of key powder characteristics and use of the reactive synthesis powder process mav be extended to the successful injection molding of other intermetallic systems.

Micromechanisms of fracture and fatigue in Ti3Al based and TiAl based intermetallics

International Nuclear Information System (INIS)

James, A.W.; Chave, R.A.; Hippsley, C.A.; Bowen, P.

1993-01-01

Micromechanisms of fracture and fatigue crack growth resistance in specific Ti 3 Al based and TiAl based intermetallics are reviewed. Effects of test temperature, environment and microstructure on crack growth resistance are considered in detail for several Ti 3 Al and Ti'Al based intermetallic systems under development. The implications of these studies for the structural reliability of these materials is also addressed briefly. (orig.)

Al/Ni metal intermetallic composite produced by accumulative roll bonding and reaction annealing

International Nuclear Information System (INIS)

Mozaffari, A.; Hosseini, M.; Manesh, H. Danesh

2011-01-01

Highlights: → Al/Ni metallic composites produced by accumulative roll bonding were heat treated at different temperatures and periods, to investigate the effect of reaction annealing on the structure and mechanical properties. → Based on the annealing conditions, various intermetallic phases were formed. The structure and composition of the composites were detected by SEM and XRD techniques. → The strength of the initial metallic composite can be improved due to the formation of the hard intermetallic phases, by the heat treatment process. - Abstract: In this research, Al/Ni multilayers composites were produced by accumulative roll bonding and then annealed at different temperatures and durations. The structure and mechanical properties of the fabricated metal intermetallic composites (MICs) were investigated. Scanning electron microscopy and X-ray diffraction analyses were used to evaluate the structure and composition of the composite. The Al 3 Ni intermetallic phase is formed in the Al/Ni interface of the samples annealed at 300 and 400 deg. C. When the temperature increased to 500 deg. C, the Al 3 Ni 2 phase was formed in the composite structure and grew, while the Al 3 Ni and Al phases were simultaneously dissociated. At these conditions, the strength of MIC reached the highest content and was enhanced by increasing time. At 600 deg. C, the AlNi phase was formed and the mechanical properties of MIC were intensively degraded due to the formation of structural porosities.

High-pressure structural stability of the ductile intermetallic ...

Indian Academy of Sciences (India)

Administrator

Murnaghan equation of state fit to the pressure, volume data yielded a bulk modulus of 67∙6 GPa with the pressure derivative of bulk modulus fixed at 4. Keywords. Intermetallics; X-ray ... ners of the unit cell cube occupied by the 'M' element and cube centre occupied by the 'R' element. Although some ductility has been ...

The μ3 model of acids and bases: extending the Lewis theory to intermetallics.

Science.gov (United States)

Stacey, Timothy E; Fredrickson, Daniel C

2012-04-02

A central challenge in the design of new metallic materials is the elucidation of the chemical factors underlying the structures of intermetallic compounds. Analogies to molecular bonding phenomena, such as the Zintl concept, have proven very productive in approaching this goal. In this Article, we extend a foundational concept of molecular chemistry to intermetallics: the Lewis theory of acids and bases. The connection is developed through the method of moments, as applied to DFT-calibrated Hückel calculations. We begin by illustrating that the third and fourth moments (μ(3) and μ(4)) of the electronic density of states (DOS) distribution tune the properties of a pseudogap. μ(3) controls the balance of states above and below the DOS minimum, with μ(4) then determining the minimum's depth. In this way, μ(3) predicts an ideal occupancy for the DOS distribution. The μ(3)-ideal electron count is used to forge a link between the reactivity of transition metals toward intermetallic phase formation, and that of Lewis acids and bases toward adduct formation. This is accomplished through a moments-based definition of acidity which classifies systems that are electron-poor relative to the μ(3)-ideal as μ(3)-acidic, and those that are electron-rich as μ(3)-basic. The reaction of μ(3) acids and bases, whether in the formation of a Lewis acid/base adduct or an intermetallic phase, tends to neutralize the μ(3) acidity or basicity of the reactants. This μ(3)-neutralization is traced to the influence of electronegativity differences at heteroatomic contacts on the projected DOS curves of the atoms involved. The role of μ(3)-acid/base interactions in intermetallic phases is demonstrated through the examination of 23 binary phases forming between 3d metals, the stability range of the CsCl type, and structural trends within the Ti-Ni system.

Intermetallic Growth and Interfacial Properties of the Grain Refiners in Al Alloys

Science.gov (United States)

Li, Chunmei; Cheng, Nanpu; Chen, Zhiqian; Xie, Zhongjing; Hui, Liangliang

2018-01-01

Al3TM(TM = Ti, Zr, Hf, Sc) particles acting as effective grain refiners for Al alloys have been receiving extensive attention these days. In order to judge their nucleation behaviors, first-principles calculations are used to investigate their intermetallic and interfacial properties. Based on energy analysis, Al3Zr and Al3Sc are more suitable for use as grain refiners than the other two intermetallic compounds. Interfacial properties show that Al/Al3TM(TM = Ti, Zr, Hf, Sc) interfaces in I-ter interfacial mode exhibit better interface wetting effects due to larger Griffith rupture work and a smaller interface energy. Among these, Al/Al3Sc achieves the lowest interfacial energy, which shows that Sc atoms should get priority for occupying interfacial sites. Additionally, Sc-doped Al/Al3(Zr, Sc) interfacial properties show that Sc can effectively improve the Al/Al3(Zr, Sc) binding strength with the Al matrix. By combining the characteristics of interfaces with the properties of intermetallics, the core-shell structure with Al3Zr-core or Al3Zr(Sc1-1)-core encircled with an Sc-rich shell forms. PMID:29677155

Elemental analysis of the Al-Fe intermetallic prepared by fast solidification

International Nuclear Information System (INIS)

Sandoval J, R.A.; Lopez M, J.; Ramirez T, J.J.; Aspiazu F, J.; Villasenor S, P.

2003-01-01

Applying the PIXE technique samples of the Al-Fe intermetallic prepared by fast solidification, obtained starting from Al recycled were analyzed. The concentrations of the found elements are given. (Author)

Discontinuously reinforced intermetallic matrix composites via XD synthesis. [exothermal dispersion

Science.gov (United States)

Kumar, K. S.; Whittenberger, J. D.

1992-01-01

A review is given of recent results obtained for discontinuously reinforced intermetallic matrix composites produced using the XD process. Intermetallic matrices investigated include NiAl, multiphase NiAl + Ni2AlTi, CoAl, near-gamma titanium aluminides, and Ll2 trialuminides containing minor amounts of second phase. Such mechanical properties as low and high temperature strength, compressive and tensile creep, elastic modulus, ambient ductility, and fracture toughness are discussed as functions of reinforcement size, shape, and volume fraction. Microstructures before and after deformation are examined and correlated with measured properties. An observation of interest in many of the systems examined is 'dispersion weakening' at high temperatures and high strain rates. This behavior is not specific to the XD process; rather similar observations have been reported in other discontinuous composites. Proposed mechanisms for this behavior are presented.

Structure and mechanical properties of parts obtained by selective laser melting of metal powder based on intermetallic compounds Ni3Al

Science.gov (United States)

Smelov, V. G.; Sotov, A. V.; Agapovichev, A. V.; Nosova, E. A.

2018-03-01

The structure and mechanical properties of samples are obtained from metal powder based on intermetallic compound by selective laser melting. The chemical analysis of the raw material and static tensile test of specimens were made. Change in the samples’ structure and mechanical properties after homogenization during four and twenty-four hours were investigated. A small-sized combustion chamber of a gas turbine engine was performed by the selective laser melting method. The print combustion chamber was subjected to the gas-dynamic test in a certain temperature and time range.

Magnetic properties of RNi5-xCux intermetallics

International Nuclear Information System (INIS)

Kuchin, A.G.; Ermolenko, A.S.; Kulikov, Yu.A.; Khrabrov, V.I.; Rosenfeld, E.V.; Makarova, G.M.; Lapina, T.P.; Belozerov, Ye.V.

2006-01-01

The magnetic properties have been studied for the series of RNi 5-x Cu x intermetallics with R=Y, La, Ce, Pr, Nd, Sm, Gd, Tb, Dy, Ho, Er, Tm, Lu; x= 5-x Cu x but GdNi 5-x Cu x . These results are explained in the frame of band magnetism, random local crystal field, and domain wall pinning theories

Digestive ripening facilitated atomic diffusion at nanosize regime: Case of AuIn{sub 2} and Ag{sub 3}In intermetallic nanoparticles

Energy Technology Data Exchange (ETDEWEB)

Arora, Neha [Department of Inorganic and Physical Chemistry, Indian Institute of Science, Bangalore 560 012 (India); Jagirdar, Balaji R., E-mail: jagirdar@ipc.iisc.ernet.in [Department of Inorganic and Physical Chemistry, Indian Institute of Science, Bangalore 560 012 (India); Klabunde, Kenneth J. [Department of Chemistry, Kansas State University, Manhattan, KS 66506 (United States)

2014-10-15

Highlights: • A digestive ripening facilitated interatomic diffusion process is presented. • Nearly monodisperse AuIn{sub 2} and Ag{sub 3}In intermetallic nanoparticles were synthesized. • Optimization of reaction temperature facilitates interatomic transfer. • Presence of excess ligand plays a crucial role in the digestive ripening process. - Abstract: Monodisperse colloidal gold–indium (AuIn{sub 2}) intermetallic nanoparticles have been synthesized from Au and In colloids using the digestive ripening process. Formation of the intermetallic proceeds via digestive ripening facilitated atomic diffusion of Au and In atoms from the Au and In nanoparticles followed simultaneously by their growth in the solution. Optimization of the reaction temperature was found to be crucial for the formation of AuIn{sub 2} intermetallic from gold and indium nanoparticles. Transmission electron microscopy revealed the presence of nearly monodisperse nanoparticles of Au and AuIn{sub 2} with particle size distribution of 3.7 ± 1.0 nm and 5.0 ± 1.6 nm, respectively. UV–visible spectral studies brought out the absence of SPR band in pure AuIn{sub 2} intermetallic nanoparticles. Optical study and electron microscopy, in combination with powder X-ray diffraction established phase pure AuIn{sub 2} intermetallic nanoparticles unambiguously. The potential of such an unprecedented approach has been further exploited in the synthesis of Ag{sub 3}In intermetallic nanoparticles with the dimension of less than 10 nm.

Processing, Microstructure and Creep Behavior of Mo-Si-B-Based Intermetallic Alloys for Very High Temperature Structural Applications

Energy Technology Data Exchange (ETDEWEB)

Vijay Vasudevan

2008-03-31

This research project is concerned with developing a fundamental understanding of the effects of processing and microstructure on the creep behavior of refractory intermetallic alloys based on the Mo-Si-B system. In the first part of this project, the compression creep behavior of a Mo-8.9Si-7.71B (in at.%) alloy, at 1100 and 1200 C was studied, whereas in the second part of the project, the constant strain rate compression behavior at 1200, 1300 and 1400 C of a nominally Mo-20Si-10B (in at.%) alloy, processed such as to yield five different {alpha}-Mo volume fractions ranging from 5 to 46%, was studied. In order to determine the deformation and damage mechanisms and rationalize the creep/high temperature deformation data and parameters, the microstructure of both undeformed and deformed samples was characterized in detail using x-ray diffraction, scanning electron microscopy (SEM) with back scattered electron imaging (BSE) and energy dispersive x-ray spectroscopy (EDS), electron back scattered diffraction (EBSD)/orientation electron microscopy in the SEM and transmission electron microscopy (TEM). The microstructure of both alloys was three-phase, being composed of {alpha}-Mo, Mo{sub 3}Si and T2-Mo{sub 5}SiB{sub 2} phases. The values of stress exponents and activation energies, and their dependence on microstructure were determined. The data suggested the operation of both dislocation as well as diffusional mechanisms, depending on alloy, test temperature, stress level and microstructure. Microstructural observations of post-crept/deformed samples indicated the presence of many voids in the {alpha}-Mo grains and few cracks in the intermetallic particles and along their interfaces with the {alpha}-Mo matrix. TEM observations revealed the presence of recrystallized {alpha}-Mo grains and sub-grain boundaries composed of dislocation arrays within the grains (in Mo-8.9Si-7.71B) or fine sub-grains with a high density of b = 1/2<111> dislocations (in Mo-20Si-10B), which

Sn and Ti influences on intermetallic phases damage in hot dip galvanizing

Directory of Open Access Journals (Sweden)

V. Di Cocco

2012-10-01

Full Text Available Protection against metallic materials corrosion is one of the most important means to reduce both maintenance costs and environmental impact. In the last years new studies on chemical baths compositions and fluxes have been performed in order to improve processes, corrosion resistance and mechanical behavior of Zn based coatings. Chemical bath composition is often improved by the Sn addition which increases the fluidity of the melt. Ti addition makes the coatings to change color under appropriate heat treatment. In this work a comparative microstructural analysis, in Zn-Sn and Zn-Ti coatings, is performed to evaluate intermetallic phases formation kinetics and the influence of intermetallic microstructure on coating damage under constant bending deformation.

Thermochemical investigations on intermetallic UMe3 compounds (Me=Ru,Rh,Pd)

International Nuclear Information System (INIS)

Wijbenga, G.

1981-10-01

The subject of this thesis is the determination of the thermodynamic properties of the intermetallic compounds of uranium with the light platinum metals, ruthenium, rhodium and palladium. These intermetallics are formed as very stable compounds during fission in nuclear fuel by the reaction of the fission products Ru, Rh and Pd with the matrix. Methods for the preparation of URu 3 , URh 3 and UPd 3 , experiments showing the chemical reactivities of these compounds, and studies of the stoichiometry of hexagonal UPd 3 by X-ray diffraction of solubility experiments of UN and palladium in UPd 3 , are described. Thermodynamic properties of the UMe 3 compounds have been obtained using several experimental thermodynamic techniques: fluorine bomb calorimetry, low-temperature cryogenic calorimetry, high-temperature drop calorimetry and EMF measurements of reversible cells. (Auth.)

Effect of Mn and Fe on the Formation of Fe- and Mn-Rich Intermetallics in Al–5Mg–Mn Alloys Solidified Under Near-Rapid Cooling

Directory of Open Access Journals (Sweden)

Yulin Liu

2016-01-01

Full Text Available Mn was an important alloying element used in Al–Mg–Mn alloys. However, it had to be limited to a low level (<1.0 wt % to avoid the formation of coarse intermetallics. In order to take full advantage of the benefits of Mn, research was carried out to investigate the possibility of increasing the content of Mn by studying the effect of cooling rate on the formation of Fe- and Mn-rich intermetallics at different content levels of Mn and Fe. The results indicated that in Al–5Mg–Mn alloy with low Fe content (<0.1 wt %, intermetallic Al6(Fe,Mn was small in size and amount. With increasing Mn content, intermetallic Al6(Fe,Mn increased, but in limited amount. In high-Fe-containing Al–5Mg–Mn alloys (0.5 wt % Fe, intermetallic Al6(Fe,Mn became the dominant phase, even in the alloy with low Mn content (0.39 wt %. Cooling rate played a critical role in the refinement of the intermetallics. Under near-rapid cooling, intermetallic Al6(Fe,Mn was extremely refined. Even in the high Mn and/or high-Fe-containing alloys, it still demonstrated fine Chinese script structures. However, once the alloy composition passed beyond the eutectic point, the primary intermetallic Al6(Fe,Mn phase displayed extremely coarse platelet-like morphology. Increasing the content of Fe caused intermetallic Al6(Fe,Mn to become the primary phase at a lower Mn content.

Lattice and magnetic anisotropies in uranium intermetallic compounds

DEFF Research Database (Denmark)

Havela, L.; Mašková, S.; Adamska, A.

2013-01-01

Examples of UNiAlD and UCoGe illustrate that the soft crystallographic direction coincides quite generally with the shortest U-U links in U intermetallics. Added to existing experimental evidence on U compounds it leads to a simple rule, that the easy magnetization direction and the soft crystall...... crystallographic direction (in the sense of highest compressibility under hydrostatic pressure) must be mutually orthogonal....

Antiferromagnetism, structural instability and frustration in intermetallic AFe4X2 systems

Science.gov (United States)

Rosner, Helge; Bergmann, Christoph; Weber, Katharina; Kraft, Inga; Mufti, N.; Klauss, Hans-Henning; Dellmann, T.; Woike, T.; Geibel, Christoph

2013-03-01

Magnetic systems with reduced dimensionality or frustration attract strong interest because these features lead to an increase of quantum fluctuations and often result in unusual properties. Here, we present a detailed study of the magnetic, thermodynamic, and structural properties of the intermetallic AFe4X2 compounds (A=Sc,Y,Lu,Zr; X=Si,Ge) crystallizing in the ZrFe4Si2 structure type. Our results evidence that these compounds cover the whole regime from frustrated AFM order up to an AFM quantum critical point. Susceptibility χ(T), specific heat, resistivity, and T-dependent XRD measurements were performed on polycrystalline samples. In all compounds we observed a Curie-Weiss behavior in χ(T) at high T indicating a paramagnetic moment of about 3μB/Fe. Magnetic and structural transitions as previously reported for YFe4Ge2 occur in all compounds with trivalent A. However, transition temperatures, nature of the transition as well as the relation between structural and magnetic transitions change significantly with the A element. Low TN's and large θCW /TN ratios confirm the relevance of frustration. The results are analyzed and discussed with respect to electronic, structural and magnetic instabilities applying DFT calculations. Financial support from the DFG (GRK 1621) is acknowledged

Theoretical Energy Release of Thermites, Intermetallics, and Combustible Metals

Energy Technology Data Exchange (ETDEWEB)

Fischer, S.H.; Grubelich, M.C.

1999-05-14

Thermite mixtures, intermetallic reactants, and metal fuels have long been used in pyrotechnic applications. Advantages of these systems typically include high energy density, high combustion temperature, and a wide range of gas production. They generally exhibit high temperature stability and possess insensitive ignition properties. For the specific applications of humanitarian demining and disposal of unexploded ordnance, these pyrotechnic formulations offer additional benefits. The combination of high thermal input with low brisance can be used to neutralize the energetic materials in mines and other ordnance without the "explosive" high-blast-pressure events that can cause extensive collateral damage to personnel, facilities, and the environment. In this paper, we review the applications, benefits, and characteristics of thermite mixtures, intermetallic reactants, and metal fuels. Calculated values for reactant density, heat of reaction (per unit mass and per unit volume), and reaction temperature (without and with consideration of phase changes and the variation of specific heat values) are tabulated. These data are ranked in several ways, according to density, heat of reaction, reaction temperature, and gas production.

Pitting Corrosion of Ni3(Si,Ti Intermetallic Compound at Various Chloride Concentrations

Directory of Open Access Journals (Sweden)

Gadang Priyotomo

2013-10-01

Full Text Available The pitting corrosion of Ni3(Si,Ti intermetallic compound was investigated as function of chloride concentration by using electrochemical method and scanning electron microscope in sodium chloride solutions at 293 K.  In addition, the pitting corrosion of type C276 alloy was also studied under the same experimental condition for comparison.  The pitting potential obtained for the intermetallic compound decreased with increasing chloride concentration.  The specific pitting potential and pitting potential of Ni3(Si,Ti were lower than those of C276 alloy, which means that the pitting corrosion resistance of C276 alloy was higher than that of Ni3(Si,Ti.

Intermetallic alloys - overview on new materials developments for structural applications in West Germany

International Nuclear Information System (INIS)

Sauthoff, G.

1990-01-01

As a result of recent research on intermetallics for high-temperature applications several alloy systems which are based on intermetallics are regarded as promising for new materials developments, and respective developments have been initiated in West Germany. The present work is aimed a lightweight materials on one hand and at high-temperature high-strength materials on the other hand. The overview surveys the work in West Germany on γ-TiAl, Ti 5 Si 3 -based alloys, Mg 2 Si-Al, NiAl-Cr, Al 3 Nb-NiAl and Laves phase-based alloys, and the mechanical properties - strength, ductility and/or toughness - are described. (orig.) [de

Real structure and selected properties of the superconducting intermetallic compound V3Si

International Nuclear Information System (INIS)

Kleinstueck, K.; Kraemer, U.; Paufler, P.; Ullrich, H.J.

1980-01-01

Plasticity and electro-plastic effects have been detected at temperatures above 1200 0 C in the intermetallic compound V 3 Si which can not plastically be deformed under normal conditions. The mechanisms of plastic deformation were elucidated. The critical temperature and the critical current density could be altered by plastic deformation. It was found that the mechanisms of plastic deformation as well as the alteration of the critical parameters are dependent on the chemical composition of the intermetallic compound within the range of homogeneity. For measuring such alterations Kossel's interference method was used. Intense plastic deformation of crystals resulted in an influence on the martensite transformation

Synthesis, growth, and studies (crystal chemistry, magnetic chemistry) of actinide-based intermetallic compounds and alloys with a 1.1.1 stoichiometry

International Nuclear Information System (INIS)

Kergadallan, Yann

1993-01-01

The first part of this research thesis reports the study of the synthesis and reactivity of intermetallic compounds with a 1.1.1 stoichiometry. It presents the thermal properties of 1.1.1 compounds: general presentation of physical transitions, and of solid solutions and formation heat, application to actinides (reactivity analysis from phase diagrams, techniques of crystal synthesis and crystal growth. It describes experimental techniques: synthesis, determination of fusion temperature by dilatometry, methods used for crystal growth, characterisation techniques (metallography, X ray diffraction on powders, dilatometry). It discusses the obtained results in terms of characterisation of synthesised samples, of crystal growth, and of measurements of fusion temperature. The second part addresses crystal chemistry studies: structure of compounds with a 1.1.1 stoichiometry (Laves structures, Zr, Ti and Pu compounds), techniques of analysis by X-ray diffraction (on powders and on single crystals), result interpretation (UNiX compounds, AnTAl compounds with T being a metal from group VIII, AnTGa compounds, AnNiGe compounds, distance comparison, structure modifications under pressure). The third part concerns physical issues. The author addresses the following topics: physical properties of intermetallic 1.1.1 compounds (magnetism of yttrium phases, behaviour of uranium-based Laves phases, analysis of pseudo-binary diagrams, physical characteristics of uranium-based 1.1.1 compounds, predictions of physical measurements), analysis techniques (Moessbauer spectroscopy, SQUID for Superconducting Quantum Interference Device), and result interpretation

A phase-field model for non-equilibrium solidification of intermetallics

International Nuclear Information System (INIS)

Assadi, H.

2007-01-01

Intermetallics may exhibit unique solidification behaviour-including slow growth kinetics, anomalous partitioning and formation of unusual growth morphologies-because of departure from local equilibrium. A phase-field model is developed and used to illustrate these non-equilibrium effects in solidification of a prototype B2 intermetallic phase. The model takes sublattice compositions as primary field variables, from which chemical long-range order is derived. The diffusive reactions between the two sublattices, and those between each sublattice and the liquid phase are taken as 'internal' kinetic processes, which take place within control volumes of the system. The model can thus capture solute and disorder trapping effects, which are consistent-over a wide range of the solid/liquid interface thickness-with the predictions of the sharp-interface theory of solute and disorder trapping. The present model can also take account of solid-state ordering and thus illustrate the effects of chemical ordering on microstructure formation and crystal growth kinetics

Landslide susceptibility mapping for a part of North Anatolian Fault Zone (Northeast Turkey) using logistic regression model

Science.gov (United States)

Demir, Gökhan; aytekin, mustafa; banu ikizler, sabriye; angın, zekai

2013-04-01

The North Anatolian Fault is know as one of the most active and destructive fault zone which produced many earthquakes with high magnitudes. Along this fault zone, the morphology and the lithological features are prone to landsliding. However, many earthquake induced landslides were recorded by several studies along this fault zone, and these landslides caused both injuiries and live losts. Therefore, a detailed landslide susceptibility assessment for this area is indispancable. In this context, a landslide susceptibility assessment for the 1445 km2 area in the Kelkit River valley a part of North Anatolian Fault zone (Eastern Black Sea region of Turkey) was intended with this study, and the results of this study are summarized here. For this purpose, geographical information system (GIS) and a bivariate statistical model were used. Initially, Landslide inventory maps are prepared by using landslide data determined by field surveys and landslide data taken from General Directorate of Mineral Research and Exploration. The landslide conditioning factors are considered to be lithology, slope gradient, slope aspect, topographical elevation, distance to streams, distance to roads and distance to faults, drainage density and fault density. ArcGIS package was used to manipulate and analyze all the collected data Logistic regression method was applied to create a landslide susceptibility map. Landslide susceptibility maps were divided into five susceptibility regions such as very low, low, moderate, high and very high. The result of the analysis was verified using the inventoried landslide locations and compared with the produced probability model. For this purpose, Area Under Curvature (AUC) approach was applied, and a AUC value was obtained. Based on this AUC value, the obtained landslide susceptibility map was concluded as satisfactory. Keywords: North Anatolian Fault Zone, Landslide susceptibility map, Geographical Information Systems, Logistic Regression Analysis.

Novel Nanocrystalline Intermetallic Coatings for Metal Alloys in Coal-fired Environments

Energy Technology Data Exchange (ETDEWEB)

Z. Zak Fang; H. Y. Sohn

2009-08-31

Intermetallic coatings (iron aluminide and nickel aluminide) were prepared by a novel reaction process. In the process, the aluminide coating is formed by an in-situ reaction between the aluminum powder fed through a plasma transferred arc (PTA) torch and the metal substrate (steel or Ni-base alloy). Subjected to the high temperature within an argon plasma zone, aluminum powder and the surface of the substrate melt and react to form the aluminide coatings. The prepared coatings were found to be aluminide phases that are porosity-free and metallurgically bonded to the substrate. The coatings also exhibit excellent high-temperature corrosion resistance under the conditions which simulate the steam-side and fire-side environments in coal-fired boilers. It is expected that the principle demonstrated in this process can be applied to the preparation of other intermetallic and alloy coatings.

Application of mechanical alloying to synthesis of intermetallic phases based alloys

International Nuclear Information System (INIS)

Dymek, S.

2001-01-01

Mechanical alloying is the process of synthesis of powder materials during milling in high energetic mills, usually ball mills. The central event in mechanical alloying is the ball-powder-ball collision. Powder particles are trapped between the colliding balls during milling and undergo deformation and/or fracture. Fractured parts are cold welded. The continued fracture and cold welding results in a uniform size and chemical composition of powder particles. The main applications of mechanical alloying are: processing of ODS alloys, syntheses of intermetallic phases, synthesis of nonequilibrium structures (amorphous alloys, extended solid solutions, nanocrystalline, quasi crystals) and magnetic materials. The present paper deals with application of mechanical alloying to synthesis Ni A l base intermetallic phases as well as phases from the Nb-Al binary system. The alloy were processed from elemental powders. The course of milling was monitored by scanning electron microscopy and X-ray diffraction. After milling, the collected powders were sieved by 45 μm grid and hot pressed (Nb alloys and NiAl) or hot extruded (NiAl). The resulting material was fully dense and exhibited fine grain (< 1 μm) and uniform distribution of oxide dispersoid. The consolidated material was compression and creep tested. The mechanical properties of mechanically alloys were superior to properties of their cast counterparts both in the room and elevated temperatures. Higher strength of mechanically alloyed materials results from their fine grains and from the presence of dispersoid. At elevated temperatures, the Nb-Al alloys have higher compression strength than NiAl-based alloys processed at the same conditions. The minimum creep rates of mechanically alloyed Nb alloys are an order of magnitude lower than analogously processed NiAl-base alloys. (author)

Intermetallic superconductors - The state of development in 1991

International Nuclear Information System (INIS)

Forsyth, E.

1991-01-01

The commercial fabrication of intermetallic superconductors has reached a high degree of maturity in the past thirty years. The only significant, commercial requirement for superconducting wire is the construction of magnetic resonance imaging (MRI) devices for medical diagnosis. In addition to this demand there are one-time projects such as a high energy particle accelerators which often need considerable quantities of superconducting material over the few years of construction. R and D projects also provide a fluctuating market for superconducting materials, in the past the projects have included power apparatus such as generators, motors, energy storage and transmission cables, and magnets for experimental fusion reactors. Superconducting magnetically levitated trains have undergone full scale trials in Japan and Germany. This is by no means a comprehensive list of all the possible applications. Virtually all the devices requiring a magnetic field to be produced by superconducting windings have used NbTi wire, but a few experimental Nb 3 Sn high field magnets have been constructed. In the case of these materials commercial vendors can provide a high degree of quality assurance on such characteristics as critical current, coupling effects and mechanical tolerances. This paper discusses the market for intermetallic and ceramic superconductors, their fabrication properties, applications, and cost

Investigations on Ce- and Yb-based intermetallic compounds

International Nuclear Information System (INIS)

Elenbaas, R.A.

1980-01-01

The author describes investigations on a number of cerium- and ytterbium-based intermetallic compounds and alloys, yielding a lot of experimental results which could not always be put in a quantitative picture. All experimental data are consistent with a single-ion behaviour, where the 4f state is more or less modified by the conduction electrons. In the investigated systems several different features of the magnetism of cerium atoms in metals were studied. (Auth.)

The Effects of Grain Refinement and Rare Earth Intermetallics on Mechanical Properties of As-Cast and Wrought Magnesium Alloys

Science.gov (United States)

Pourbahari, Bita; Mirzadeh, Hamed; Emamy, Massoud

2018-03-01

The effects of rare earth intermetallics and grain refinement by alloying and hot extrusion on the mechanical properties of Mg-Gd-Al-Zn alloys have been studied to elucidate some useful ways to enhance the mechanical properties of magnesium alloys. It was revealed that aluminum as an alloying element is a much better grain refining agent compared with gadolinium, but the simultaneous presence of Al and Gd can refine the as-cast grain size more efficiently. The presence of fine and widely dispersed rare earth intermetallics was found to be favorable to achieve finer recrystallized grains during hot deformation by extrusion. The presence of coarse dendritic structure in the GZ61 alloy, grain boundary eutectic containing Mg17Al12 phase in the AZ61 alloy, and rare earth intermetallics with unfavorable morphology in the Mg-4Gd-2Al-1Zn alloy was found to be detrimental to mechanical properties of the alloy in the as-cast condition. As a result, the microstructural refinement induced by hot extrusion process resulted in a significant enhancement in strength and ductility of the alloys. The presence of intermetallic compounds in the extruded Mg-4Gd-2Al-1Zn and Mg-2Gd-4Al-1Zn alloys deteriorated tensile properties, which was related to the fact that such intermetallic compounds act as stress risers and microvoid initiation sites.

Mechanism of forming interfacial intermetallic compounds at interface for solid state diffusion bonding of dissimilar materials

International Nuclear Information System (INIS)

He, P.; Liu, D.

2006-01-01

The formation of brittle intermetallic compounds at the interfaces of diffusion bonds is the main cause which leads to poor bond strength. Therefore, it is very important to study and establish the formation and growth model of intermetallic compounds at the interfaces for the control process of diffusion bonding. In this paper, according to the diffusion kinetics and the thermodynamics, the principle of formation of intermetallic compounds at interfaces in the multi-component diffusion couple, the flux-energy principle, is put forward. In the light of diffusion theory, the formation capacity of the phase at the interfaces is determined by specific properties of the composition in the diffusion couple and the composition ratio of the formed phase is in agreement with the diffusion flux. In accordance with the flux-energy principle, the microstructure of the Ni/TC4 interface is Ni/TiNi 3 /TiNi/Ti 2 Ni/TC4, the microstructure of the TC4/00Cr18Ni9Ti interface is 00Cr18Ni9Ti/TiFe 2 /TiFe/Ti 2 Fe/TC4, and the microstructure of the TiAl/40Cr interface is 40Cr/TiC/Ti 3 Al + FeAl + FeAl 2 /TiAl. Multi-intermetallic compounds with the equivalent flux-energy can be formed at the interfaces at the same time

NiTi intermetallic surface coatings by laser metal deposition for improving wear properties of Ti-6Al-4V substrates

CSIR Research Space (South Africa)

Mokgalaka, MN

2014-03-01

Full Text Available The NiTi intermetallic possesses a number of good properties, such as high wear, oxidation, and corrosion resistance. This paper focuses on the deposition of NiTi intermetallic coatings on Ti6Al4V substrate by laser melting of Ti and Ni elemental...

Effect of Mn and Fe on the Formation of Fe- and Mn-Rich Intermetallics in Al–5Mg–Mn Alloys Solidified Under Near-Rapid Cooling

Science.gov (United States)

Liu, Yulin; Huang, Gaoren; Sun, Yimeng; Zhang, Li; Huang, Zhenwei; Wang, Jijie; Liu, Chunzhong

2016-01-01

Mn was an important alloying element used in Al–Mg–Mn alloys. However, it had to be limited to a low level (Al–5Mg–Mn alloy with low Fe content (Al6(Fe,Mn) was small in size and amount. With increasing Mn content, intermetallic Al6(Fe,Mn) increased, but in limited amount. In high-Fe-containing Al–5Mg–Mn alloys (0.5 wt % Fe), intermetallic Al6(Fe,Mn) became the dominant phase, even in the alloy with low Mn content (0.39 wt %). Cooling rate played a critical role in the refinement of the intermetallics. Under near-rapid cooling, intermetallic Al6(Fe,Mn) was extremely refined. Even in the high Mn and/or high-Fe-containing alloys, it still demonstrated fine Chinese script structures. However, once the alloy composition passed beyond the eutectic point, the primary intermetallic Al6(Fe,Mn) phase displayed extremely coarse platelet-like morphology. Increasing the content of Fe caused intermetallic Al6(Fe,Mn) to become the primary phase at a lower Mn content. PMID:28787888

Effect of Mn and Fe on the Formation of Fe- and Mn-Rich Intermetallics in Al-5Mg-Mn Alloys Solidified Under Near-Rapid Cooling.

Science.gov (United States)

Liu, Yulin; Huang, Gaoren; Sun, Yimeng; Zhang, Li; Huang, Zhenwei; Wang, Jijie; Liu, Chunzhong

2016-01-29

Mn was an important alloying element used in Al-Mg-Mn alloys. However, it had to be limited to a low level (Al-5Mg-Mn alloy with low Fe content (Al₆(Fe,Mn) was small in size and amount. With increasing Mn content, intermetallic Al₆(Fe,Mn) increased, but in limited amount. In high-Fe-containing Al-5Mg-Mn alloys (0.5 wt % Fe), intermetallic Al₆(Fe,Mn) became the dominant phase, even in the alloy with low Mn content (0.39 wt %). Cooling rate played a critical role in the refinement of the intermetallics. Under near-rapid cooling, intermetallic Al₆(Fe,Mn) was extremely refined. Even in the high Mn and/or high-Fe-containing alloys, it still demonstrated fine Chinese script structures. However, once the alloy composition passed beyond the eutectic point, the primary intermetallic Al₆(Fe,Mn) phase displayed extremely coarse platelet-like morphology. Increasing the content of Fe caused intermetallic Al₆(Fe,Mn) to become the primary phase at a lower Mn content.

Limitation of critical current density by intermetallic formation in fine filament Nb-Ti superconductors

International Nuclear Information System (INIS)

Larbalestier, D.C.; Chengren, L.; Starch, W.; Lee, P.J.

1985-01-01

Two experiments have been performed to investigate the role that the intermetallic reaction between the copper matrix and the Nb-Ti filaments plays in limiting the critical current density (J/sub c/) of Nb 45.6 wt% Ti composites. The first experiment involved composites which were industrially extruded. It was found that as the number of heat treatments increased, the J/sub c/ declined, the resistive transition broadened and the filaments sausaged. The filament sausaging was initiated by intermetallic particles at the filament matrix interface. A series of many heat treatment procedures were then applied to composites fabricated in the authors own laboratories without extrusion. Very high J/sub c/ values were obtained at filament sizes of 20 μm. When the same heat treatment procedures were applied to 4 - 5 μm conductors, extensive sausaging and degraded J/sub c/ values resulted. This degradation was also found to be due to the formation of Cu-Nb-Ti intermetallic compounds. It is concluded that a reliable filament diffusion barrier technology is necessary to permit full flexibility in the heat treatment of 2 - 5 μ filament Nb-Ti composites

Limitation of critical current density by intermetallic formation in fine filament Nb-Ti superconductors

International Nuclear Information System (INIS)

Larbalestier, D.C.; Chengren, Li; Lee, P.J.; Starch, W.

1985-01-01

Two experiments have been performed to investigate the role that the intermetallic reaction between the copper matrix and the Nb-Ti filaments plays in limiting the critical current density (J /SUB c/ ) of Nb 46.5 wt% Ti composites. The first experiment involved composites which were industrially extruded. It was found that as the number of heat treatments increased, the J /SUB c/ declined, the resistive transition broadened and the filaments sausaged. The filament sausaging was initiated by intermetallic particles at the filament matrix interface. A series of many heat treatment procedures were then applied to composites fabricated in our own laboratories without extrusion. Very high J /SUB c/ values were obtained at filament sizes of 20 μm. When the same heat treatment procedures were applied to 4 - 5 μm conductors, extensive sausaging and degraded J /SUB c/ values resulted. This degradation was also found to be due to the formation of Cu-Nb-Ti intermetallic compounds. It is concluded that a reliable filament diffusion barrier technology is necessary to permit full flexibility in the heat treatment of 2 - 5 μm filament Nb-Ti composites

First principles study of electronic, elastic and thermal properties of lutetium intermetallics

International Nuclear Information System (INIS)

Pagare, Gitanjali; Chouhan, Sunil Singh; Soni, Pooja; Sanyal, S.P.; Rajagopalan, M.

2011-01-01

In the present work, the electronic, elastic and thermal properties of lutetium intermetallics LuX have been studied theoretically by using first principles calculations based on density functional theory (DFT) with the generalized gradient approximation (GCA)

Effect of intermetallic phases on the anodic oxidation and corrosion of 5A06 aluminum alloy

Science.gov (United States)

Li, Song-mei; Li, Ying-dong; Zhang, You; Liu, Jian-hua; Yu, Mei

2015-02-01

Intermetallic phases were found to influence the anodic oxidation and corrosion behavior of 5A06 aluminum alloy. Scattered intermetallic particles were examined by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) after pretreatment. The anodic film was investigated by transmission electron microscopy (TEM), and its corrosion resistance was analyzed by electrochemical impedance spectroscopy (EIS) and Tafel polarization in NaCl solution. The results show that the size of Al-Fe-Mg-Mn particles gradually decreases with the iron content. During anodizing, these intermetallic particles are gradually dissolved, leading to the complex porosity in the anodic film beneath the particles. After anodizing, the residual particles are mainly silicon-containing phases, which are embedded in the anodic film. Electrochemical measurements indicate that the porous anodic film layer is easily penetrated, and the barrier plays a dominant role in the overall protection. Meanwhile, self-healing behavior is observed during the long immersion time.

First principle study on generalized-stacking-fault energy surfaces of B2-AlRE intermetallic compounds

Science.gov (United States)

Li, Shaorong; Wang, Shaofeng; Wang, Rui

2011-12-01

First-principles calculations are used to predict the generalized-stacking-fault energy (GSFE) surfaces of AlRE intermetallics. The calculations employ the projector augmented-wave (PAW) method within the generalized gradient approximation (GGA) using the density functional theory (DFT). GSFE curves along {1 1 0} direction, {1 1 0} direction and {1 1 0} direction have been calculated. The fitted GSFE surfaces have been obtained from the Fourier series based on the translational symmetry. In order to illuminate the reasonable of our computational accuracy, we have compared our theoretical results of B2 intermetallics YCu with the previous calculated results. The unstable-stacking-fault energy (γus) on the {1 1 0} plane has the laws of AlPr, and directions. For the antiphase boundary (APB) energy, that of AlSc is the lowest in the calculated AlRE intermetallics. So the superdislocation with the Burgers vector along direction of AlSc will easily split into two superpartials.

Development of melting and casting process for Nb-Al intermetallic compounds and mechanical properties

International Nuclear Information System (INIS)

Kamata, Kinya; Degawa, Toru; Nagashima, Yoshinori

1993-01-01

The shaping methods of Nb-Al intermetallic compounds, especially melting and casting, have considerably different characteristics as compared with those for other metals and alloys. The authors have investigated melting and casting processes for Nb-Al compounds to develop precision casting processes for these intermetallics. Fundamental properties of Nb-Al compound castings have been also investigated for high temperature structural use in this work. An advanced Induction Skull Melting (ISM) furnace has been developed and the advantages of ISM have been recognized as a result of this study. The mechanical properties, such as hardness and compression strength, are dependent upon the Al content in Nb-Al binary compounds

Electronic structure and phase stability during martensitic transformation in Al-doped ZrCu intermetallics

International Nuclear Information System (INIS)

Qiu Feng; Shen Ping; Liu Tao; Lin Qiaoli; Jiang Qichuan

2010-01-01

Martensitic transformation, phase stability and electronic structure of Al-doped ZrCu intermetallics were investigated by experiments and first-principles calculations using the pseudopotentials plane wave method. The formation energy calculations indicate that the stability of the ZrCu phase increases with the increasing Al content. Al plays a decisive role in controlling the formation and microstructures of the martensite phases in Zr-Cu-Al alloys. The total energy difference between ZrCu (B2) austenite and ZrCu martensite plays an important role in the martensitic transformation. The phase stability is dependent on its electronic structure. The densities of states (DOS) of the intermetallics were discussed in detail.

A Self-Propagating Foaming Process of Porous Al-Ni Intermetallics Assisted by Combustion Reactions

Directory of Open Access Journals (Sweden)

Makoto Kobashi

2009-12-01

Full Text Available The self-propagating foaming process of porous Al-Ni intermetallics was investigated. Aluminum and nickel powders were blended, and titanium and boron carbide powders were added as reactive exothermic agents. The blended powder was extruded to make a rod-shape precursor. Only one end of the rod precursor was heated to ignite the reaction. The reaction propagated spontaneously throughout the precursor. Pore formation took place at the same time as the reaction occurred. Adding the exothermic agent was effective to increase the porosity. Preheating the precursor before the ignition was also very effective to produce porous Al-Ni intermetallics with high porosity.

Effects of ductile phase volume fraction on the mechanical properties of Ti-Al3Ti metal-intermetallic laminate (MIL) composites

International Nuclear Information System (INIS)

Price, Richard D.; Jiang Fengchun; Kulin, Robb M.; Vecchio, Kenneth S.

2011-01-01

Research highlights: → Residual Al improves the mechanical properties of Ti-Al 3 Ti MIL composites. → Residual Al can eliminate intermetallic centerline delaminations in MILs. → Low levels of residual Al increase fracture toughness in MIL composites. → MIL stiffness, strength, and fracture toughness can be optimized at low Al levels. - Abstract: Metal-intermetallic laminate (MIL) composites consisting of alternating layers of Ti, Al, and the intermetallic Al 3 Ti have been fabricated by reactive foil sintering in open air. Six initially identical stacks of alternating Ti-3Al-2.5 V and 1100-Al foils were processed for different lengths of time, yielding specimens with different metal and intermetallic volume fractions. Their mechanical properties have been investigated with an emphasis on the effect of residual Al at the intermetallic centerline on composite strength and fracture toughness, as well as fracture and failure modes. Samples were cut from each composite plate (in layer orientations parallel and perpendicular to the intended load direction) for mechanical testing in compression and four-point bending under quasi-static and high-rate loading conditions. Examination of the damaged specimens and their fracture surfaces by optical and scanning electron microscopy was performed to establish a correlation between the failure mechanisms present, composite strength, and microstructure. Results indicated that regardless of loading direction, cracks always initiated in the intermetallic region, rarely at the centerline, and crack propagation and failure were heavily influenced by the thickness of the residual aluminum layers. There is an ideal residual aluminum volume fraction that represents the amount of ductile reinforcement that maximizes the combined properties of strength, toughness and stiffness.

Thermal Expansion of Ni3Al Intermetallic Compound: Experiment and Simulation

International Nuclear Information System (INIS)

Wang Hai-Peng; Lü Peng; Zhou Kai; Wei Bing-Bo

2016-01-01

The thermal expansion of Ni 3 Al intermetallic compound is determined by a thermal dilatometer and simulated by the molecular dynamics method. The results of the linear thermal expansion coefficients are presented from 200 K up to the maximum temperature of 1600 K. The single phase of Ni 3 Al intermetallic compound is confirmed by x-ray diffraction together with DSC melting and solidification peaks, from which the solidus and the liquidus temperatures are obtained to be 1660 and 1695 K, respectively. The measured linear thermal expansion coefficient increases from 1.5 × 10 −5 to 2.7 × 10 −5 K −1 in the experimental temperature range, in good agreement with the data obtained by the molecular dynamics simulation, just a slight difference from the temperature dependence coefficient. Furthermore, the atomic structure and position are presented to reveal the atom distribution change during thermal expansion of Ni 3 Al compound. (paper)

Ceramic-intermetallic composites produced by mechanical alloying and spark plasma sintering

CERN Document Server

Cabanas-Moreno, J G; Martínez-Sanchez, R; Delgado-Gutierrez, O; Palacios-Gomez, J; Umemoto, M

1998-01-01

Nano-and microcomposites of intermetallic (Co/sub 3/Ti, AlCo/sub 2 /Ti) and ceramic (TiN, Ti(C, N), Al/sub 2/O/sub 3/) phases have been produced by spark plasma sintering (SPS) of powders resulting from mechanical alloying of Al-Co-Ti elemental powder mixtures. The mechanically alloyed powders consisted of mixtures of nanocrystalline and amorphous phases which, on sintering, transformed into complex microstructures of the intermetallic and ceramic phases. For Al contents lower than about 30 at% in the original powder mixtures, the use of SPS led to porosities of 1-2% in the sintered compacts and hardness values as high as ~1700 kg/mm/sup 2/; in these cases, the composite matrix was TiN and Ti(C, N), with the Al/sub 2/O/sub 3/ phase found as finely dispersed particles in the matrix and the Co /sub 3/Ti and AlCo/sub 2/Ti phases as interdispersed grains. (19 refs).

Intermetallics Synthesis in the Fe–Al System via Layer by Layer 3D Laser Cladding

Directory of Open Access Journals (Sweden)

Floran Missemer

2013-10-01

Full Text Available Intermetallide phase formation was studied in a powdered Fe–Al system under layer by layer laser cladding with the aim of fabricating the gradient of properties by means of changing the Fe–Al concentration ratio in the powder mixture from layer to layer. The relationships between the laser cladding parameters and the intermetallic phase structures in the consecutively cladded layers were determined. In order to study the structure formation an optical microscopy, X-ray diffraction analysis, measurement of microhardness, scanning electron microscopy (SEM with energy dispersive X-ray (EDX spectroscopy analysis were used after the laser synthesis of intermetallic compounds.

Effect of Iron-Containing Intermetallic Particles on the Corrosion Behaviour of Aluminium

DEFF Research Database (Denmark)

Ambat, Rajan

2006-01-01

The effect of heat treatment on the corrosion behaviour of binary Al-Fe alloys containing iron at levels between 0.04 and 0.42 wt.% was investigated by electrochemical measurements in both acidic and alkaline chloride solutions. Comparing solution heat-treated and quenched materials with samples...... with {100} facets, and are observed to contain numerous intermetallic particles. Fine facetted filaments also radiate out from the periphery of pits. The results demonstrate that the corrosion of "pure" 99.96% Al is thus dominated by the role of iron, which is the main impurity, and its electrochemical...... that had been subsequently annealed to promote precipitation of Al3Fe intermetallic particles, it was found that annealing increases both the cathodic and anodic reactivity. The increased cathodic reactivity is believed to be directly related to the increased available surface area of the iron...

Role of intermetallics on the mechanical fatigue behavior of Cu–Al ball bond interfaces

Energy Technology Data Exchange (ETDEWEB)

Lassnig, A., E-mail: alice.lassnig@univie.ac.at [University of Vienna, Faculty of Physics, Physics of Nanostructured Materials, Boltzmanngasse 5, 1090 Wien (Austria); Pelzer, R. [Infineon Technologies Austria AG, Siemensstrae 2, 9500 Villach (Austria); Gammer, C. [University of Vienna, Faculty of Physics, Physics of Nanostructured Materials, Boltzmanngasse 5, 1090 Wien (Austria); National Center for Electron Microscopy, Molecular Foundry, Lawrence Berkeley National Laboratory, Berkeley, CA 94720 (United States); Khatibi, G. [Vienna University of Technology, Institute of Chemical Technology and Analytics, Getreidemarkt 9, 1060 Wien (Austria)

2015-10-15

The mechanical fatigue behavior of Cu–Al interfaces occurring in thermosonic ball bonds –typically used in microelectronic packages for automotive applications – is investigated by means of a specially designed fatigue test technique. Fully reversed cyclic shear stresses are induced at the bond interface, leading to subsequent fatigue lift off failure and revealing the weakest site of the bond. A special focus is set on the role of interfacial intermetallic compounds (IMC) on the fatigue performance of such interfaces. Therefore fatigue life curves were obtained for three representative microstructural states: The as-bonded state is compared to two annealed states at 200 °C for 200 h and at 200 °C for 2000 h respectively. In the moderately annealed state two IMC layers (Al{sub 2}Cu, Al{sub 4}Cu{sub 9}) could be identified, whereas in the highly aged state the original pad metallization was almost entirely consumed and AlCu is formed as a third IMC. Finally, the crack path is traced back as a function of interfacial microstructure by means of electron microscopy techniques. Whereas conventional static shear tests reveal no significant decrease of the bond shear force with increased IMC formation the fatigue tests prove a clear degradation in the cyclic mechanical performance. It can be concluded that during cycling the crack deflects easily into the formed intermetallics, leading to early failure of the ball bonds due to their brittle nature. - Highlights: • High cycle fatigue of various miniaturized Cu–Al interfaces is investigated. • Interfacial intermetallic compounds consist of Al2Cu, AlCu and Al4Cu9. • Static shear strength shows minor dependency on interfacial phase formation. • Fatigue tests prove significant degradation with intermetallic compound evolution. • Fatigue fracture surface analysis reveal microstructure dependent crack path.

Role of intermetallics on the mechanical fatigue behavior of Cu–Al ball bond interfaces

International Nuclear Information System (INIS)

Lassnig, A.; Pelzer, R.; Gammer, C.; Khatibi, G.

2015-01-01

The mechanical fatigue behavior of Cu–Al interfaces occurring in thermosonic ball bonds –typically used in microelectronic packages for automotive applications – is investigated by means of a specially designed fatigue test technique. Fully reversed cyclic shear stresses are induced at the bond interface, leading to subsequent fatigue lift off failure and revealing the weakest site of the bond. A special focus is set on the role of interfacial intermetallic compounds (IMC) on the fatigue performance of such interfaces. Therefore fatigue life curves were obtained for three representative microstructural states: The as-bonded state is compared to two annealed states at 200 °C for 200 h and at 200 °C for 2000 h respectively. In the moderately annealed state two IMC layers (Al 2 Cu, Al 4 Cu 9 ) could be identified, whereas in the highly aged state the original pad metallization was almost entirely consumed and AlCu is formed as a third IMC. Finally, the crack path is traced back as a function of interfacial microstructure by means of electron microscopy techniques. Whereas conventional static shear tests reveal no significant decrease of the bond shear force with increased IMC formation the fatigue tests prove a clear degradation in the cyclic mechanical performance. It can be concluded that during cycling the crack deflects easily into the formed intermetallics, leading to early failure of the ball bonds due to their brittle nature. - Highlights: • High cycle fatigue of various miniaturized Cu–Al interfaces is investigated. • Interfacial intermetallic compounds consist of Al2Cu, AlCu and Al4Cu9. • Static shear strength shows minor dependency on interfacial phase formation. • Fatigue tests prove significant degradation with intermetallic compound evolution. • Fatigue fracture surface analysis reveal microstructure dependent crack path

Gas-Solid Reaction Route toward the Production of Intermetallics from Their Corresponding Oxide Mixtures

Directory of Open Access Journals (Sweden)

Hesham Ahmed

2016-08-01

Full Text Available Near-net shape forming of metallic components from metallic powders produced in situ from reduction of corresponding pure metal oxides has not been explored to a large extent. Such a process can be probably termed in short as the “Reduction-Sintering” process. This methodology can be especially effective in producing components containing refractory metals. Additionally, in situ production of metallic powder from complex oxides containing more than one metallic element may result in in situ alloying during reduction, possibly at lower temperatures. With this motivation, in situ reduction of complex oxides mixtures containing more than one metallic element has been investigated intensively over a period of years in the department of materials science, KTH, Sweden. This review highlights the most important features of that investigation. The investigation includes not only synthesis of intermetallics and refractory metals using the gas solid reaction route but also study the reaction kinetics and mechanism. Environmentally friendly gases like H2, CH4 and N2 were used for simultaneous reduction, carburization and nitridation, respectively. Different techniques have been utilized. A thermogravimetric analyzer was used to accurately control the process conditions and obtain reaction kinetics. The fluidized bed technique has been utilized to study the possibility of bulk production of intermetallics compared to milligrams in TGA. Carburization and nitridation of nascent formed intermetallics were successfully carried out. A novel method based on material thermal property was explored to track the reaction progress and estimate the reaction kinetics. This method implies the dynamic measure of thermal diffusivity using laser flash method. These efforts end up with a successful preparation of nanograined intermetallics like Fe-Mo and Ni-W. In addition, it ends up with simultaneous reduction and synthesis of Ni-WN and Ni-WC from their oxide mixtures

The corrosion behavior of the T1 (Al2CuLi) intermetallic compound in aqueous environments

Science.gov (United States)

Buchheit, R. G.; Stoner, G. E.

1989-01-01

The intermetallic compound T1 (Al2CuLi) is suspected to play an important role in the localized corrosion at subgrain boundaries in Al-Li-Cu alloys. The intermetallic was synthesized for characterization of its corrosion behavior. Experiments performed included open circuit potential measurements, potentiodynamic polarization, and corrosion rate vs. pH in solutions whose pH was varied over the range of 3 to 11. Subgrain boundary pitting and continuous subgrain boundary corrosion are discussed in terms of the data obtained. Evidence suggesting the dealloying of copper from this compound is also presented.

Plutonium microstructures. Part 1

International Nuclear Information System (INIS)

Cramer, E.M.; Bergin, J.B.

1981-09-01

This report is the first of three parts in which Los Alamos and Lawrence Livermore National Laboratory metallographers exhibit a consolidated set of illustrations of inclusions that are seen in plutonium metal as a consequence of inherent and tramp impurities, alloy additions, and thermal or mechanical treatments. This part includes illustrations of nonmetallic and intermetallic inclusions characteristic of major impurity elements as an aid to identifying unknowns. It also describes historical aspects of the increased purity of laboratory plutonium samples, and it gives the composition of the etchant solutions and describes the etching procedure used in the preparation of each illustrated sample. 25 figures

Effects of filling material and laser power on the formation of intermetallic compounds during laser-assisted friction stir butt welding of steel and aluminum alloys

Science.gov (United States)

Fei, Xinjiang; Jin, Xiangzhong; Peng, Nanxiang; Ye, Ying; Wu, Sigen; Dai, Houfu

2016-11-01

In this paper, two kinds of materials, Ni and Zn, are selected as filling material during laser-assisted friction stir butt welding of Q235 steel and 6061-T6 aluminum alloy, and their influences on the formation of intermetallic compounds on the steel/aluminum interface of the joints were first studied. SEM was used to analyze the profile of the intermetallic compound layer and the fractography of tensile fracture surfaces. In addition, EDS was applied to investigate the types of the intermetallic compounds. The results indicate that a thin iron-abundant intermetallic compound layer forms and ductile fracture mode occurs when Ni is added, but a thick aluminum-abundant intermetallic compound layer generates and brittle fracture mode occurs when Zn is added. So the tensile strength of the welds with Ni as filling material is greater than that with Zn as filling material. Besides, the effect of laser power on the formation of intermetallic compound layer when Ni is added was investigated. The preheated temperature field produced by laser beam in the cross section of workpiece was calculated, and the tensile strength of the joints at different laser powers was tested. Results show that only when suitable laser power is adopted, can suitable preheating temperature of the steel reach, then can thin intermetallic compound layer form and high tensile strength of the joints reach. Either excessive or insufficient laser power will reduce the tensile strength of the joints.

The role of intermetallic phases in the corrosion of magnesium-rare earth alloys

Energy Technology Data Exchange (ETDEWEB)

Silva Campos, Maria del Rosario

2016-07-25

A new concept to develop a RE based Mg alloy with improved corrosion resistance was followed in the current work. Based on subsequent characterisation steps to eliminate less suitable RE elements the best microstructure for improved corrosion resistance was identified. At first, the corrosion properties of selected RE elements were determined. Based on these results RE elements that have a potential to enhance the corrosion resistance of Mg-RE alloys were selected. Two aspects of RE elements were important for the selection: the electrochemical properties and the solid solubility in Mg. If the solubility limit of RE elements in the Mg matrix is exceeded, they form intermetallic phases with Mg. By performing galvanic coupling measurements the compatibility between Mg matrix and intermetallic phases were estimated. At that point three binary Mg-RE alloys systems remained (Mg-Ce, Mg-La, and Mg-Gd). To evaluate the influence of composition (amount of intermetallic phases) on the corrosion behaviour, four concentrations were cast with 1, 5, 10 and 15 wt. % of RE. Ce and La have a lower solid solubility in Mg matrix generating higher volume fraction of the secondary phases, thus higher dissolution rates in the binary Mg-RE alloys. While Gd with higher solid solubility shows a different behaviour. Additions of up to 10 wt. % Gd resulted in similar behaviour compared to 1 wt. % Gd addition. The most promising results were obtained for the Mg-Gd system with 10 wt. % Gd. Thus, the microstructure of this alloy was further modified by heat treatments to understand the influence of microstructural changes on corrosion behaviour. A ternary element was used to attempt further optimisation of the corrosion performance. Additions of Al, Zn, Ga and Y did not show any improvement in the corrosion resistance of Mg10Gd. This is due to increasing volume fractions of critical more noble phases and the microstructure dominated by eutectic phase formation. Thus galvanic effects became much

The role of intermetallic phases in the corrosion of magnesium-rare earth alloys

International Nuclear Information System (INIS)

Silva Campos, Maria del Rosario

2016-01-01

A new concept to develop a RE based Mg alloy with improved corrosion resistance was followed in the current work. Based on subsequent characterisation steps to eliminate less suitable RE elements the best microstructure for improved corrosion resistance was identified. At first, the corrosion properties of selected RE elements were determined. Based on these results RE elements that have a potential to enhance the corrosion resistance of Mg-RE alloys were selected. Two aspects of RE elements were important for the selection: the electrochemical properties and the solid solubility in Mg. If the solubility limit of RE elements in the Mg matrix is exceeded, they form intermetallic phases with Mg. By performing galvanic coupling measurements the compatibility between Mg matrix and intermetallic phases were estimated. At that point three binary Mg-RE alloys systems remained (Mg-Ce, Mg-La, and Mg-Gd). To evaluate the influence of composition (amount of intermetallic phases) on the corrosion behaviour, four concentrations were cast with 1, 5, 10 and 15 wt. % of RE. Ce and La have a lower solid solubility in Mg matrix generating higher volume fraction of the secondary phases, thus higher dissolution rates in the binary Mg-RE alloys. While Gd with higher solid solubility shows a different behaviour. Additions of up to 10 wt. % Gd resulted in similar behaviour compared to 1 wt. % Gd addition. The most promising results were obtained for the Mg-Gd system with 10 wt. % Gd. Thus, the microstructure of this alloy was further modified by heat treatments to understand the influence of microstructural changes on corrosion behaviour. A ternary element was used to attempt further optimisation of the corrosion performance. Additions of Al, Zn, Ga and Y did not show any improvement in the corrosion resistance of Mg10Gd. This is due to increasing volume fractions of critical more noble phases and the microstructure dominated by eutectic phase formation. Thus galvanic effects became much

Preparation of Fe-Al Intermetallic / TiC-Al2O3 Ceramic Composites from Ilmenite by SHS

Institute of Scientific and Technical Information of China (English)

无

2007-01-01

Fe-Al intermetallic/TiC-Al2O3 ceramic composites were successfully prepared by self-propagating high-temperature synthesis (SHS) from natural ilmenite, aluminium and carbon as the raw materials. The effects of carbon sources, preheating time and heat treatment temperature on synthesis process and products were investigated in detail, and the reaction process of the FeTiO3-Al-C system was also discussed.It is shown that the temperature and velocity of the combustion wave are higher when graphite is used as the carbon source, which can reflect the effect of the carbon source structure on the combustion synthesis;Prolonging the preheating time or heat treatment temperature is beneficial to the formation of the ordered intermetallics; The temperature and velocity of the combustion wave arc improved, but the disordered alloys are difficult to eliminate with the preheating time prolonged. The compound powders mainly containing ordered Fe3Al intermetallic can be prepared through heat treatment at 750 ℃.

New intermetallic compounds Ln(Ag, AL)4 (Ln-Y, Gd, Tb, Dy) and their structure

International Nuclear Information System (INIS)

Kuz'ma, Yu.B.; Stel'makhovich, B.M.

1990-01-01

By the methods of X-ray analysis crystal structure of compounds Ln(Ag,Al) 4 , where Ln-Y, Gd, Tb, Dy, posessing rhombic structure, is determined. The intermetallics have been prepared for the first time. Ways of atom distribution and their coordinates in DyAg 0.55 Al 3.45 structure (a=0.4296(1), b=04179(1), c=0.9995(3), R=0.093) are specified. Other compounds are formed in case of LnAgAl 3 compositions. Interatomic distances in Dy(Ag,Al) 4 structure are considered. A supposition is made on the formation in Ln-Ag-Al systems of a greater number of intermetallic compounds

Influence of annealing time and temperature on the Fe3Al intermetallic alloys microstructure modification

Directory of Open Access Journals (Sweden)

K. Garbala

2011-04-01

Full Text Available There is an industry interesting in intermetallic alloys in recent years. There are widely possibilities to adopt this kind of materials for structural units. More expensive materials can be replaced by them. A property which limits their wider application is the low plasticity at environment and elevated temperatures. In paper the results of the thermal microstructure modification are shown. To this end, the influence of annealing time and temperature on the intermetallic phase Fe3Al grain size was investigated. The impact of these factors on micro-hardness was examined as well. It was found that these operations cause the grain size reduction and the micro-hardness decrease.

Multiscale modeling of the influence of Fe content in a Al-Si-Cu alloy on the size distribution of intermetallic phases and micropores

International Nuclear Information System (INIS)

Wang Junsheng; Lee, Peter D.; Li Mei; Allison, John

2010-01-01

A multiscale model was developed to simulate the formation of Fe-rich intermetallics and pores in quaternary Al-Si-Cu-Fe alloys. At the microscale, the multicomponent diffusion equations were solved for multiphase (liquid-solid-gas) materials via a finite difference framework to predict microstructure formation. A fast and robust decentered plate algorithm was developed to simulate the strong anisotropy of the solid/liquid interfacial energy for the Fe-rich intermetallic phase. The growth of porosity was controlled by local pressure drop due to solidification and interactions with surrounding solid phases, in addition to hydrogen diffusion. The microscale model was implemented as a subroutine in a commercial finite element package, producing a coupled multiscale model. This allows the influence of varying casting conditions on the Fe-rich intermetallics, the pores, and their interactions to be predicted. Synchrotron x-ray tomography experiments were performed to validate the model by comparing the three-dimensional morphology and size distribution of Fe-rich intermetallics as a function of Fe content. Large platelike Fe-rich β intermetallics were successfully simulated by the multiscale model and their influence on pore size distribution in shape castings was predicted as a function of casting conditions.

Microstructure and tribological properties of NiMo/Mo2Ni3Si intermetallic 'in-situ' composites

International Nuclear Information System (INIS)

Gui Yongliang; Song Chunyan; Yang Li; Qin Xiaoling

2011-01-01

Research highlights: → Wear resistant NiMo/Mo 2 Ni 3 Si intermetallic 'in-situ' composites was fabricated successfully with Mo-Ni-Si powder blends as the starting materials. Microstructure of the NiMo/Mo 2 Ni 3 Si composites consists of Mo 2 Ni 3 Si primary dendrites, binary intermetallic phase NiMo and small amount of Ni/NiMo eutectics structure. The NiMo/Mo 2 Ni 3 Si composites exhibited high hardness and outstanding tribological properties under room-temperature dry-sliding wear test conditions which were attributed to the covalent-dominant strong atomic bonds and excellent combination of strength and ductility and toughness. - Abstract: Wear resistant NiMo/Mo 2 Ni 3 Si intermetallic 'in-situ' composites with a microstructure of ternary metal silicide Mo 2 Ni 3 Si primary dendritic, the long strip-like NiMo intermetallic phase, and a small amount of Ni/NiMo eutectics structure were designed and fabricated using molybdenum, nickel and silicon elemental powders. Friction and wear properties of NiMo/Mo 2 Ni 3 Si composites were evaluated under different contact load at room-temperature dry-sliding wear test conditions. Microstructure, worn surface morphologies and subsurface microstructure were characterized by OM, XRD, SEM and EDS. Results indicate that NiMo/Mo 2 Ni 3 Si composites have low fiction coefficient, excellent wear resistance and sluggish wear-load dependence. The dominant wear mechanisms of NiMo/Mo 2 Ni 3 Si composites are soft abrasion and slightly superficial oxidative wear.

Landslide susceptibility zonation in part of Tehri reservoir region

Indian Academy of Sciences (India)

Fuzzy logic; landslide susceptibility; frequency ratio. ... zones using landslide frequency ratio and fuzzy logic in GIS environment is presented for Tehri ... Temporal remote sensing data was used to prepare important landslide causative factor ...

The equiatomic intermetallics REPtCd (RE = La, Ce, Pr, Nd, Eu) and magnetic properties of CeAuCd

Energy Technology Data Exchange (ETDEWEB)

Johnscher, Michael; Niehaus, Oliver; Poettgen, Rainer [Muenster Univ. (Germany). Inst. fuer Anorganische und Analytische Chemie; Tappe, Frank [Hochschule Hamm-Lippstadt, Hamm (Germany)

2015-06-01

The cadmium intermetallics REPtCd (RE = La, Ce, Pr, Nd, Eu) and CeAuCd were synthesized by induction-melting of the elements in sealed niobium ampoules followed by annealing in muffle furnaces. The samples were characterized by powder X-ray diffraction. The structures of CePtCd (ZrNiAl type, P anti 62m, a = 763.8(6), c = 409.1(4) pm, wR2 = 0.0195, 298 F{sup 2} values, 14 variables) and EuPtCd (TiNiSi type, Pnma, a = 741.3(2), b = 436.4(1), c = 858.0(4) pm, wR2 = 0.0385, 440 F{sup 2} values, 20 variables) were refined from single-crystal data. The REPtCd structures exhibit three-dimensional networks of corner- and edge-sharing Cd rate at Pt{sub 2/6}Pt{sub 2/3} and Cd rate at Pt{sub 4/4} tetrahedra, which leave cages for the rare earth atoms. Temperature-dependent magnetic susceptibility data of CeAuCd reveal a paramagnetic to antiferromagnetic phase transition at T{sub N} = 3.7(5) K.

The equiatomic intermetallics REPtCd (RE = La, Ce, Pr, Nd, Eu) and magnetic properties of CeAuCd

International Nuclear Information System (INIS)

Johnscher, Michael; Niehaus, Oliver; Poettgen, Rainer

2015-01-01

The cadmium intermetallics REPtCd (RE = La, Ce, Pr, Nd, Eu) and CeAuCd were synthesized by induction-melting of the elements in sealed niobium ampoules followed by annealing in muffle furnaces. The samples were characterized by powder X-ray diffraction. The structures of CePtCd (ZrNiAl type, P anti 62m, a = 763.8(6), c = 409.1(4) pm, wR2 = 0.0195, 298 F 2 values, 14 variables) and EuPtCd (TiNiSi type, Pnma, a = 741.3(2), b = 436.4(1), c = 858.0(4) pm, wR2 = 0.0385, 440 F 2 values, 20 variables) were refined from single-crystal data. The REPtCd structures exhibit three-dimensional networks of corner- and edge-sharing Cd rate at Pt 2/6 Pt 2/3 and Cd rate at Pt 4/4 tetrahedra, which leave cages for the rare earth atoms. Temperature-dependent magnetic susceptibility data of CeAuCd reveal a paramagnetic to antiferromagnetic phase transition at T N = 3.7(5) K.

Pressure effect on magnetic and magnetotransport properties of intermetallic and colossal magnetoresistance oxide compounds

International Nuclear Information System (INIS)

Arnold, Z; Ibarra, M R; Algarabel, P A; Marquina, C; Teresa, Jose MarIa de; Morellon, L; Blasco, J; Magen, C; Prokhnenko, O; Kamarad, J; Ritter, C

2005-01-01

The joint power of neutron diffraction and pressure techniques allows us to characterize under unique conditions the nature and different role of basic interactions in solids. We have covered a broad phenomenology in archetypical compounds: intermetallics and magnetic oxides. We have selected compounds in which the effect of moderate pressure is able to modify the electronic structure and bond angles that in turn are in the bases of magnetic and structural transitions. Complex magnetic and structural phase diagrams are reported for compounds with magnetic (Tb 1-X Y X Mn 2 ) and structural (RE 5 Si 4-X Ge X ) instabilities. Pressure-induced change of the magnetic structure in (R 2 Fe 17 ) intermetallics and the effect on the colossal magnetoresistance manganites are described

Vanadium Influence on Iron Based Intermetallic Phases in AlSi6Cu4 Alloy

Directory of Open Access Journals (Sweden)

Bolibruchová D.

2014-10-01

Full Text Available Negative effect of iron in Al-Si alloys mostly refers with iron based intermetallic phases, especially Al5FeSi phases. These phases are present in platelet-like forms, which sharp edges are considered as main cracks initiators and also as contributors of porosity formation. In recent times, addition of some elements, for example Mn, Co, Cr, Ni, V, is used to reduce influence of iron. Influence of vanadium in aluminium AlSi6Cu4 alloy with intentionally increased iron content is presented in this article. Vanadium amount has been graduated and chemical composition of alloy has been analysed by spectral analysis. Vanadium influence on microstructural changes was evaluated by microstructural analysis and some of intermetallic particles were reviewed by EDX analysis.

The behaviour of the lande factor and effective exchange parameter in a group of Pr intermetallics observed through reduced level scheme models

International Nuclear Information System (INIS)

Ranke, P.J. von; Caldas, A.; Palermo, L.

1993-01-01

The present work constitutes a portion of a continuing series of studies dealing with models, in which we retain only the two lowest levels of the crystal field splitting scheme of rare-earth ion in rare-earth intermetallics. In these reduced level scheme models, the crystal field and the magnetic Hamiltonians are represented in matrix notation. These two matrices constitute the model Hamiltonian proposed in this paper, from which we derive the magnetic state equations of interest for this work. Putting into these equations a group of adequate experimental data found in the literature for a particular rare-earth intermetallic we obtain the Lande factor and effective exchange parameter related to this rare-earth intermetallic. This study will be applied to a group of Pr intermetallics, in cubic symmetry, in which the ground level may be a non-magnetic singlet level or a non-magnetic doublet level. In both cases, the first excited level is a triplet one. (orig.)

Magnetic anisotropy in intermetallic compounds containing both uranium and 3d-metal

Czech Academy of Sciences Publication Activity Database

Andreev, Alexander V.; Tereshina, Evgeniya; Gorbunov, Denis; Šantavá, Eva; Šebek, Josef; Žáček, Martin; Homma, Y.; Shiokawa, Y.; Satoh, I.; Yamamura, Y.; Komatsubara, T.; Watanabe, K.; Koyama, K.

2013-01-01

Roč. 114, č. 9 (2013), s. 727-733 ISSN 0031-918X R&D Projects: GA ČR GAP204/12/0150 Institutional support: RVO:68378271 Keywords : uranium intermetallics * magnetic anisotropy * ferromagnetism Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.605, year: 2013

Landslide susceptibility zonation in part of Tehri reservoir region ...

Indian Academy of Sciences (India)

Validation of the model was performed by using cumulative ..... thrusts, folds and joints of varying shape and size ...... Lee S, Choi J and Min K 2002 Landslide susceptibility analy- ... cross-validation in three test areas using a frequency.

X-Ray Diffraction of Intermetallic Compounds: A Physical Chemistry Laboratory Experiment

Science.gov (United States)

Varberg, Thomas D.; Skakuj, Kacper

2015-01-01

Here we describe an experiment for the undergraduate physical chemistry laboratory in which students synthesize the intermetallic compounds AlNi and AlNi3 and study them by X-ray diffractometry. The compounds are synthesized in a simple one-step reaction occurring in the solid state. Powder X-ray diffractograms are recorded for the two compounds…

Homogeneous (Cu, Ni)6Sn5 intermetallic compound joints rapidly formed in asymmetrical Ni/Sn/Cu system using ultrasound-induced transient liquid phase soldering process.

Science.gov (United States)

Li, Z L; Dong, H J; Song, X G; Zhao, H Y; Tian, H; Liu, J H; Feng, J C; Yan, J C

2018-04-01

Homogeneous (Cu, Ni) 6 Sn 5 intermetallic compound (IMC) joints were rapidly formed in asymmetrical Ni/Sn/Cu system by an ultrasound-induced transient liquid phase (TLP) soldering process. In the traditional TLP soldering process, the intermetallic joints formed in Ni/Sn/Cu system consisted of major (Cu, Ni) 6 Sn 5 and minor Cu 3 Sn IMCs, and the grain morphology of (Cu, Ni) 6 Sn 5 IMCs subsequently exhibited fine rounded, needlelike and coarse rounded shapes from the Ni side to the Cu side, which was highly in accordance with the Ni concentration gradient across the joints. However, in the ultrasound-induced TLP soldering process, the intermetallic joints formed in Ni/Sn/Cu system only consisted of the (Cu, Ni) 6 Sn 5 IMCs which exhibited an uniform grain morphology of rounded shape with a remarkably narrowed Ni concentration gradient. The ultrasound-induced homogeneous intermetallic joints exhibited higher shear strength (61.6 MPa) than the traditional heterogeneous intermetallic joints (49.8 MPa). Copyright © 2017 Elsevier B.V. All rights reserved.

Implementation of landslide susceptibility maps in Lower Austria as part of risk governance

Science.gov (United States)

Bell, Rainer; Petschko, Helene; Bauer, Christian; Glade, Thomas; Granica, Klaus; Heiss, Gerhard; Leopold, Philip; Pomaroli, Gilbert; Proske, Herwig; Schweigl, Joachim

2013-04-01

Landslides frequently cause damage to agricultural land and infrastructure in Lower Austria - a province of Austria. Also settlements and people are threatened by landslides. To reduce landslide risks and to prevent the establishment of new settlements in highly landslide prone areas, the project "MoNOE" (Method development for landslide susceptibility modeling in Lower Austria) was set up by the provincial government. The main aim of the project is the development of methods to model rock fall and slide susceptibility for an area of approx. 15,900 km2 and to implement the resulting susceptibility maps into the spatial planning strategies of the state. Right from the beginning of the project a close cooperation between the involved scientists and the stakeholders from the Geological Survey of Lower Austria and the Department of Spatial Planning and Regional Policy of Lower Austria was established to ensure that method development and final susceptibility maps meet exactly the needs and demands of the stakeholders. This posed huge challenges, together with its realization in the large study area and a (heterogeneous) complex geological situation,. Limitations were given by restricted data availability (e.g. for geology or landslide inventories) in such a large study area. Rock fall susceptibility was modeled by a combined approach of determining rock fall release areas by empirical slope thresholds (dependent on geology) followed by empirical run-out modeling. Slide susceptibility was modeled based on the statistical approaches of weights of evidence (WofE) and generalized additive models (GAM) by two different research groups. Huge efforts were spent on the validation of all susceptibility models. In a later stage of the project we found that the best scientific maps are not necessarily the best maps to be implemented in spatial planning strategies. Thus, in close cooperation with the stakeholders, decisions had to be taken to find the best resolution of the maps

Quantitative assessment of intermetallic phase precipitation in a super duplex stainless steel weld metal using automatic image analysis

Energy Technology Data Exchange (ETDEWEB)

Gregori, A. [AB Sandvik Steel, Sandviken (Sweden). R and D Centre; Nilsson, J.-O. [AB Sandvik Steel, R and D Centre, Sandviken (Sweden); Bonollo, F. [Univ. di Padova, DTGSI, Vicenza (Italy)

1999-07-01

The microstructure of weld metal of the type 25%Cr-10%Ni-4%Mo-0.28%N in both as-welded and isothermally heat treated (temperature range: 700-1050 C: time range: 10s-72h) conditions has been investigated. Multipass welding was performed in Ar+2%N{sub 2} atmosphere using GTAW. By means of the electron diffraction technique. {sigma}-phase and {chi}-phase were detected and investigated. {chi}-phase precipitated more readily than {sigma}-phase and was found to be a precursor to {sigma}-phase by providing suitable nucleation sites. Quantitative image analysis of ferrite and intermetallic phases was performed as well as manual point counting (ISO 9042). Automatic image analysis was found to be more accurate. The results were used to assess the TTT-diagram with respect to intermetallic phase formation. On the basis of these results a CCT-diagram was computed, considering the intermetallic phase formation described by an Avrami type equation and adopting the additivity rule. (orig.)

Anisotropic behavior and complex colinear magnetic structures of cerium and actinide intermetallics

International Nuclear Information System (INIS)

Cooper, B.R.

1977-01-01

A review is given of the experimental situation and degree of theoretical understanding for the occurrence of complex colinear magnetic structures in cerium and actinide intermetallics of NaCl structure. In doing this, emphasis is on the qualitative nature of the anisotropic effects necessary to understand the behavior. With this in mind we focus on the I to IA magnetic structure transition, and indeed more simply, on the occurrence of the IA magnetic structure which appears for CeBi, UAs, and some of the mixed uranium monopnictide-monochalcogenides. We show how the experimental observations involving properties related to the IA magnetic structure indicate important qualitative features of the physical mechanism involved. Through discussion of the possible analogue to the situation in UO 2 , the idea is introduced that magnetoelastic effects involving internal rearrangement modes may play a key role in the occurrence of the IA structure. Internal rearrangement modes are modes where one ionic species remains at its site in the undistorted crystal structure, and the other species is displaced from its position in the undistorted structure. We show that in a very natural way one can anticipate the possible occurrence of an internal rearrangement mode having a four-layer, periodic displacement sequence for planes for one species in the NaCl structure crystals, while the other species remains undisplaced. The presence of such a static lattice mode is susceptible to direct experimental observation. (author)

Joining thick section aluminum to steel with suppressed FeAl intermetallic formation via friction stir dovetailing

Energy Technology Data Exchange (ETDEWEB)

Reza-E-Rabby, Md.; Ross, Kenneth; Overman, Nicole R.; Olszta, Matthew J.; McDonnell, Martin; Whalen, Scott A.

2018-04-01

A new solid-phase technique called friction stir dovetailing (FSD) has been developed for joining thick section aluminum to steel. In FSD, mechanical interlocks are formed at the aluminum-steel interface and are reinforced by metallurgical bonds where intermetallic growth has been uniquely suppressed. Lap shear testing shows superior strength and extension at failure compared to popular friction stir approaches where metallurgical bonding is the only joining mechanism. High resolution microscopy revealed the presence of a 40-70 nm interlayer having a composition of 76.4 at% Al, 18.4 at% Fe, and 5.2 at% Si, suggestive of limited FeAl3 intermetallic formation.

Characterization of intermetallics in aluminum to zinc coated interstitial free steel joining by pulsed MIG brazing for automotive application

Energy Technology Data Exchange (ETDEWEB)

Basak, Sushovan, E-mail: sushovanbasak@gmail.com [Metallurgical and Material Engineering Department, Jadavpur University, Kolkata–700032 (India); Das, Hrishikesh, E-mail: hrishichem@gmail.com [Metallurgical and Material Engineering Department, Jadavpur University, Kolkata–700032 (India); Pal, Tapan Kumar, E-mail: tkpal.ju@gmail.com [Metallurgical and Material Engineering Department, Jadavpur University, Kolkata–700032 (India); Shome, Mahadev, E-mail: mshome@tatasteel.com [Material Characterization & Joining Group, R & D, Tata Steel, Jamshedpur–831007 (India)

2016-02-15

In order to meet the demand for lighter and more fuel efficient vehicles, a significant attempt is currently being focused toward the substitution of aluminum for steel in the car body structure. It generates vital challenge with respect to the methods of joining to be used for fabrication. However, the conventional fusion joining has its own difficulty owing to formation of the brittle intermetallic phases. In this present study AA6061-T6 of 2 mm and HIF-GA steel sheet of 1 mm thick are metal inert gas (MIG) brazed with 0.8 mm Al–5Si filler wire under three different heat inputs. The effect of the heat inputs on bead geometry, microstructure and joint properties of MIG brazed Al-steel joints were exclusively studied and characterized by X-ray diffraction, field emission scanning electron microscopy (FESEM), electron probe micro analyzer (EPMA) and high resolution transmission electron microscopy (HRTEM) assisted X-ray spectroscopy (EDS) and selective area diffraction pattern. Finally microstructures were correlated with the performance of the joint. Diffusion induced intermetallic thickness measured by FESEM image and concentration profile agreed well with the numerically calculated one. HRTEM assisted EDS study was used to identify the large size FeAl{sub 3} and small size Fe{sub 2}Al{sub 5} type intermetallic compounds at the interface. The growth of these two phases in A2 (heat input: 182 J mm{sup −1}) is attributed to the slower cooling rate with higher diffusion time (~ 61 s) along the interface in comparison to the same for A1 (heat input: 155 J mm{sup −1}) with faster cooling rate and shorter diffusion time (~ 24 s). The joint efficiency as high as 65% of steel base metal is achieved for A2 which is the optimized parameter in the present study. - Highlights: • AA 6061 and HIF-GA could be successfully joined by MIG brazing. • Intermetallics are exclusively studied and characterized by XRD, FESEM and EPMA. • Intermetallic formation by diffusion is

Intermetallic Al-, Fe-, Co- and Ni-Based Thermal Barrier Coatings Prepared by Cold Spray for Applications on Low Heat Rejection Diesel Engines

Science.gov (United States)

Leshchinsky, E.; Sobiesiak, A.; Maev, R.

2018-02-01

Conventional thermal barrier coating (TBC) systems consist of a duplex structure with a metallic bond coat and a ceramic heat insulating topcoat. They possess the desired low thermal conductivity, but at the same time they are very brittle and sensitive to thermal shock and thermal cycling due to the inherently low coefficient of thermal expansion. Recent research activities are focused on the developing of multilayer TBC structures obtained using cold spraying and following annealing. Aluminum intermetallics have demonstrated thermal and mechanical properties that allow them to be used as the alternative TBC materials, while the intermetallic layers can be additionally optimized to achieve superior thermal physical properties. One example is the six layer TBC structure in which cold sprayed Al-based intermetallics are synthesized by annealing in nitrogen atmosphere. These multilayer coating systems demonstrated an improved thermal fatigue capability as compared to conventional ceramic TBC. The microstructures and properties of the coatings were characterized by SEM, EDS and mechanical tests to define the TBC material properties and intermetallic formation mechanisms.

Thermomechanical processing of plasma sprayed intermetallic sheets

Science.gov (United States)

Hajaligol, Mohammad R.; Scorey, Clive; Sikka, Vinod K.; Deevi, Seetharama C.; Fleischhauer, Grier; Lilly, Jr., A. Clifton; German, Randall M.

2001-01-01

A powder metallurgical process of preparing a sheet from a powder having an intermetallic alloy composition such as an iron, nickel or titanium aluminide. The sheet can be manufactured into electrical resistance heating elements having improved room temperature ductility, electrical resistivity, cyclic fatigue resistance, high temperature oxidation resistance, low and high temperature strength, and/or resistance to high temperature sagging. The iron aluminide has an entirely ferritic microstructure which is free of austenite and can include, in weight %, 4 to 32% Al, and optional additions such as .ltoreq.1% Cr, .gtoreq.0.05% Zr .ltoreq.2% Ti, .ltoreq.2% Mo, .ltoreq.1% Ni, .ltoreq.0.75% C, .ltoreq.0.1% B, .ltoreq.1% submicron oxide particles and/or electrically insulating or electrically conductive covalent ceramic particles, .ltoreq.1% rare earth metal, and/or .ltoreq.3% Cu. The process includes forming a non-densified metal sheet by consolidating a powder having an intermetallic alloy composition such as by roll compaction, tape casting or plasma spraying, forming a cold rolled sheet by cold rolling the non-densified metal sheet so as to increase the density and reduce the thickness thereof and annealing the cold rolled sheet. The powder can be a water, polymer or gas atomized powder which is subjecting to sieving and/or blending with a binder prior to the consolidation step. After the consolidation step, the sheet can be partially sintered. The cold rolling and/or annealing steps can be repeated to achieve the desired sheet thickness and properties. The annealing can be carried out in a vacuum furnace with a vacuum or inert atmosphere. During final annealing, the cold rolled sheet recrystallizes to an average grain size of about 10 to 30 .mu.m. Final stress relief annealing can be carried out in the B2 phase temperature range.

The role of zinc on the chemistry of complex intermetallic compounds

Energy Technology Data Exchange (ETDEWEB)

Xie, Weiwei [Iowa State Univ., Ames, IA (United States)

2014-01-01

Combining experiments and electronic structure theory provides the framework to design and discover new families of complex intermetallic phases and to understand factors that stabilize both new and known phases. Using solid state synthesis and multiple structural determinations, ferromagnetic β-Mn type Co_8+xZn_12–x was analyzed for their crystal and electronic structures.

Intermetallic and electrical insulator coatings on high-temperature alloys in liquid-lithium environments

International Nuclear Information System (INIS)

Park, J.H.

1994-06-01

In the design of liquid-metal cooling systems for fusion-reactor blanket, applications, the corrosion resistance of structural materials and the magnetohydrodynamic (MHD) force and its subsequent influence on thermal hydraulics and corrosion are major concerns. When the system is cooled by liquid metals, insulator coatings are required on piping surfaces in contact with the coolant. The objective of this study is to develop stable corrosion-resistant electrical insulator coatings at the liquid-metal/structural-material interface, with emphasis on electrically insulating coatings that prevent adverse MHD-generated currents from passing through the structural wall, and Be-V intermetallic coatings for first-wall components that face the plasma. Vanadium and V-base alloys are leading candidate materials for structural applications in a fusion reactor. Various intermetallic films were produced on V-alloys and on Types 304 and 316 stainless steel. The intermetallic layers were developed by exposure of the materials to liquid Li containing 2 at temperatures of 500--1030 degree C. CaO electrical insulator coatings were produced by reaction of the oxygen-rich layer with <5 at. % Ca dissolved in liquid Li at 400--700 degree C. The reaction converted the oxygen-rich layer to an electrically insulating film. This coating method is applicable to reactor components because the liquid metal can be used over and over; only the solute within the liquid metal is consumed. This paper will discuss initial results on the nature of the coatings and their in-situ electrical resistivity characteristics in liquid Li at high temperatures

Plasticity enhancement mechanisms in refractory metals and intermetallics

International Nuclear Information System (INIS)

Gibala, R.; Chang, H.; Czarnik, C.M.; Edwards, K.M.; Misra, A.

1993-01-01

Plasticity enhancement associated with surface films and precipitates or dispersoids in bcc refractory metals is operative in ordered intermetallic compounds. Some results are given for NiAl and MoSi 2 -based materials. The monotonic and cyclic plasticity of NiAl at room temperature can be enhanced by surface films. Ductile second phases also enhance the plasticity of NiAl. MoSi 2 exhibits similar effects of surface films and dispersoids, but primarily at elevated temperatures. The plasticity enhancement is associated with enhanced dislocation generation from constrained deformation at the film-substrate or precipitate/dispersoid-matrix interface of the composite systems

NMR and domain wall mobility in intermetallic compounds

International Nuclear Information System (INIS)

Guimaraes, A.P.; Sampaio, L.C.; Cunha, S.F.; Alves, K.M.B.

1991-01-01

The technique of pulsed NMR can be used to study the distribution of hyperfine fields in a magnetic matrix. The dynamics of the domain walls are relevant to the generation of NMR signals. In the present study on the (R x Y 1-x ) Fe 2 intermetallic compounds, the reduction in the signals is associated to increased propagation fields. This indicates that a smaller domain wall mobility is at the origin of these effects. NMR spectra in this system show the importance of direct and indirect (i.e., mediated by Fe atoms) terms in the transferred hyperfine field. (author)

Fe-Zn intermetallic phases prepared by diffusion annealing and spark-plasma sintering

Czech Academy of Sciences Publication Activity Database

Pokorný, P.; Cinert, Jakub; Pala, Zdeněk

2016-01-01

Roč. 50, č. 2 (2016), s. 253-256 ISSN 1580-2949 R&D Projects: GA ČR GB14-36566G Institutional support: RVO:61389021 Keywords : Fe-Zn intermetallics * spark-plasma sintering * diffusion annealing * phase composition * hardness Subject RIV: JK - Corrosion ; Surface Treatment of Materials Impact factor: 0.436, year: 2016

Mechanical properties of intermetallics formed during thermal aging of Cu-Al ball bonds

NARCIS (Netherlands)

Kouters, M.H.M.; Gubbels, G.H.M.; O'Halloran, O.; Rongen, R.; Weltevreden, E.R.

2011-01-01

In high power automotive electronics copper wire bonding is regarded as most promising alternative for gold wire bonding in 1st level interconnects and therefore subjected to severe functional requirements. In the Cu-Al ball bond interface the growth of intermetallic compounds may deteriorate the

The shock Hugoniot of the intermetallic alloy Ti-46.5Al-2Nb-2Cr

International Nuclear Information System (INIS)

Millett, Jeremy; Gray, George T. Rusty III; Bourne, Neil

2000-01-01

Plate impact experiments were conducted on a γ-titanium aluminide (TiAl) based ordered intermetallic alloy. Stress measurements were recorded using manganin stress gauges supported on the back of TiAl targets using polymethylmethacrylate windows. The Hugoniot in stress-particle velocity space for this TiAl alloy was deduced using impedance matching techniques. The results in this study are compared to the known Hugoniot data of the common alpha-beta engineering Ti-based alloy Ti-6Al-4V. The results of the current study on the intermetallic alloy TiAl support that TiAl possesses a significantly higher stress for a given particle velocity than the two-phase Ti-6Al-4V alloy. (c) 2000 American Institute of Physics

Electronic structure and properties of rare earth and actinide intermetallics

International Nuclear Information System (INIS)

Kirchmayr, H.R.

1984-01-01

There are 188 contributions, experimental and theoretical, a few on rare earth and actinide elements but mostly on rare earth and actinide intermetallic compounds and alloys. The properties dealt with include 1) crystal structure, 2) magnetic properties and magnetic structure, 3) magnetic phase transformations and valence fluctuations, 4) electrical properties and superconductivity and their temperature, pressure and magnetic field dependence. A few papers deal with crystal growth and novel measuring methods. (G.Q.)

Effects of surface polishing and annealing on the optical conductivity of intermetallic compounds

CERN Document Server

Rhee, J Y

1999-01-01

The optical conductivity spectra of several intermetallic compounds were measured by spectroscopic ellipsometry. Three spectra were measured for each compound; just after the sample was mechanically polished, at high temperature, and after the sample was annealed at 110 .deg. C for at least one day and cooled to room temperature. An equiatomic FeTi alloy showed the typical effects of annealing after mechanical polishing of surface. The spectrum after annealing had a larger magnitude and sharper structures than the spectrum before annealing. We also observed shifts of peaks in the spectrum. A relatively low-temperature annealing gave rise to unexpectedly substantial effects, and the effects were explained by recrystallization and/or a disorder -> order transition of the surface of the sample which was damaged and, hence, became highly disordered by mechanical polishing. Similar effects were also observed when the sample temperature was lowered. The observed changes upon annealing could partly be explained by p...

Stability of molybdenum nanoparticles in Sn-3.8Ag-0.7Cu solder during multiple reflow and their influence on interfacial intermetallic compounds

Energy Technology Data Exchange (ETDEWEB)

Haseeb, A.S.M.A., E-mail: haseeb@um.edu.my; Arafat, M.M., E-mail: arafat_mahmood@yahoo.com; Johan, Mohd Rafie, E-mail: mrafiej@um.edu.my

2012-02-15

This work investigates the effects of molybdenum nanoparticles on the growth of interfacial intermetallic compound between Sn-3.8Ag-0.7Cu solder and copper substrate during multiple reflow. Molybdenum nanoparticles were mixed with Sn-3.8Ag-0.7Cu solder paste by manual mixing. Solder samples were reflowed on a copper substrate in a 250 Degree-Sign C reflow oven up to six times. The molybdenum content of the bulk solder was determined by inductive coupled plasma-optical emission spectrometry. It is found that upon the addition of molybdenum nanoparticles to Sn-3.8Ag-0.7Cu solder, the interfacial intermetallic compound thickness and scallop diameter decreases under all reflow conditions. Molybdenum nanoparticles do not appear to dissolve or react with the solder. They tend to adsorb preferentially at the interface between solder and the intermetallic compound scallops. It is suggested that molybdenum nanoparticles impart their influence on the interfacial intermetallic compound as discrete particles. The intact, discrete nanoparticles, by absorbing preferentially at the interface, hinder the diffusion flux of the substrate and thereby suppress the intermetallic compound growth. - Highlights: Black-Right-Pointing-Pointer Mo nanoparticles do not dissolve or react with the SAC solder during reflow. Black-Right-Pointing-Pointer Addition of Mo nanoparticles results smaller IMC thickness and scallop diameter. Black-Right-Pointing-Pointer Mo nanoparticles influence the interfacial IMC through discrete particle effect.

Evolution of Fe based intermetallic phases in Al–Si hypoeutectic casting alloys: Influence of the Si and Fe concentrations, and solidification rate

International Nuclear Information System (INIS)

Gorny, Anton; Manickaraj, Jeyakumar; Cai, Zhonghou; Shankar, Sumanth

2013-01-01

Highlights: •Anomalous evolution of Fe based intermetallic phases in Al–Si–Fe alloys. •XRF coupled with nano-diffraction to confirm the nano-size Fe intermetallic phases. •Crystallography of the θ-Al 13 Fe 4 , τ 5 -Al 8 Fe 2 Si and τ 6 -Al 9 Fe 2 Si 2 phases. •Peritectic reactions involving the Fe intermetallic phases in Al–Si–Fe alloys. -- Abstract: Al–Si–Fe hypoeutectic cast alloy system is very complex and reported to produce numerous Fe based intermetallic phases in conjunction with Al and Si. This publication will address the anomalies of phase evolution in the Al–Si–Fe hypoeutectic casting alloy system; the anomaly lies in the peculiarities in the evolution and nature of the intermetallic phases when compared to the thermodynamic phase diagram predictions and past publications of the same. The influence of the following parameters, in various combinations, on the evolution and nature of the intermetallic phases were analyzed and reported: concentration of Si between 2 and 12.6 wt%, Fe between 0.05 and 0.5 wt% and solidification rates of 0.1, 1, 5 and 50 K s −1 . Two intermetallic phases are observed to evolve in these alloys under these solidification conditions: the τ 5 -Al 8 SiFe 2 and τ 6 -Al 9 Fe 2 Si 2 . The τ 5 -Al 8 SiFe 2 phase evolves at all levels of the parameters during solidification and subsequently transforms into the τ 6 -Al 9 Fe 2 Si 2 through a peritectic reaction when promoted by certain combinations of solidification parameters such as higher Fe level, lower Si level and slower solidification rates. Further, it is also hypothesized from experimental evidences that the θ-Al 13 Fe 4 binary phase precludes the evolution of the τ 5 during solidification and subsequently transforms into the τ 6 phase during solidification. These observations are anomalous to the publications as prior art and simulation predictions of thermodynamic phase diagrams of these alloys, wherein, only one intermetallic phases in the �

Ab Initio Studies of Shock-Induced Chemical Reactions of Inter-Metallics

Science.gov (United States)

Zaharieva, Roussislava; Hanagud, Sathya

2009-06-01

Shock-induced and shock assisted chemical reactions of intermetallic mixtures are studied by many researchers, using both experimental and theoretical techniques. The theoretical studies are primarily at continuum scales. The model frameworks include mixture theories and meso-scale models of grains of porous mixtures. The reaction models vary from equilibrium thermodynamic model to several non-equilibrium thermodynamic models. The shock-effects are primarily studied using appropriate conservation equations and numerical techniques to integrate the equations. All these models require material constants from experiments and estimates of transition states. Thus, the objective of this paper is to present studies based on ab initio techniques. The ab inito studies, to date, use ab inito molecular dynamics. This paper presents a study that uses shock pressures, and associated temperatures as starting variables. Then intermetallic mixtures are modeled as slabs. The required shock stresses are created by straining the lattice. Then, ab initio binding energy calculations are used to examine the stability of the reactions. Binding energies are obtained for different strain components super imposed on uniform compression and finite temperatures. Then, vibrational frequencies and nudge elastic band techniques are used to study reactivity and transition states. Examples include Ni and Al.

Mining for elastic constants of intermetallics from the charge density landscape

Energy Technology Data Exchange (ETDEWEB)

Kong, Chang Sun; Broderick, Scott R. [Department of Materials Science and Engineering, Iowa State University, Ames, IA 50011 (United States); Jones, Travis E. [Molecular Theory Group, Colorado School of Mines, Golden, CO 80401 (United States); Loyola, Claudia [Department of Materials Science and Engineering, Iowa State University, Ames, IA 50011 (United States); Eberhart, Mark E. [Molecular Theory Group, Colorado School of Mines, Golden, CO 80401 (United States); Rajan, Krishna, E-mail: krajan@iastate.edu [Department of Materials Science and Engineering, Iowa State University, Ames, IA 50011 (United States)

2015-02-01

There is a significant challenge in designing new materials for targeted properties based on their electronic structure. While in principle this goal can be met using knowledge of the electron charge density, the relationships between the density and properties are largely unknown. To help overcome this problem we develop a quantitative structure–property relationship (QSPR) between the charge density and the elastic constants for B2 intermetallics. Using a combination of informatics techniques for screening all the potentially relevant charge density descriptors, we find that C{sub 11} and C{sub 44} are determined solely from the magnitude of the charge density at its critical points, while C{sub 12} is determined by the shape of the charge density at its critical points. From this reduced charge density selection space, we develop models for predicting the elastic constants of an expanded number of intermetallic systems, which we then use to predict the mechanical stability of new systems. Having reduced the descriptors necessary for modeling elastic constants, statistical learning approaches may then be used to predict the reduced knowledge-based required as a function of the constituent characteristics.

Fracture and fatigue considerations in the development of ductile-phase reinforced intermetallic-matrix composites

International Nuclear Information System (INIS)

Venkateswara Rao, K.T.; Ritchie, R.O.

1994-01-01

The salient microstructural factors influencing fracture and fatigue-crack growth resistance of ductile-particle reinforced intermetallic-matrix composites at ambient temperature are reviewed through examples from the Nb/MoSi 2 , TiNb/TiAl, Nb/TiAl and Nb/Nb 3 Al systems; specific emphasis is placed on properties and morphology of the reinforcement and its interfacial properties with the matrix. It is shown that composites must be fabricated with a high aspect ratio ductile-reinforcement morphology in order to promote crack-particle interception and resultant crack bridging for improved fracture and fatigue properties. Concurrently, however, the ductile phases have contrasting effects on crack growth under monotonic vs. cyclic loading suggesting that composite microstructures tailored for optimal toughness may not necessarily yield optimal fatigue resistance. Perspectives for the future development of damage-tolerant intermetallic-composite microstructures are discussed

Discovery of Intermetallic Compounds from Traditional to Machine-Learning Approaches.

Science.gov (United States)

Oliynyk, Anton O; Mar, Arthur

2018-01-16

Intermetallic compounds are bestowed by diverse compositions, complex structures, and useful properties for many materials applications. How metallic elements react to form these compounds and what structures they adopt remain challenging questions that defy predictability. Traditional approaches offer some rational strategies to prepare specific classes of intermetallics, such as targeting members within a modular homologous series, manipulating building blocks to assemble new structures, and filling interstitial sites to create stuffed variants. Because these strategies rely on precedent, they cannot foresee surprising results, by definition. Exploratory synthesis, whether through systematic phase diagram investigations or serendipity, is still essential for expanding our knowledge base. Eventually, the relationships may become too complex for the pattern recognition skills to be reliably or practically performed by humans. Complementing these traditional approaches, new machine-learning approaches may be a viable alternative for materials discovery, not only among intermetallics but also more generally to other chemical compounds. In this Account, we survey our own efforts to discover new intermetallic compounds, encompassing gallides, germanides, phosphides, arsenides, and others. We apply various machine-learning methods (such as support vector machine and random forest algorithms) to confront two significant questions in solid state chemistry. First, what crystal structures are adopted by a compound given an arbitrary composition? Initial efforts have focused on binary equiatomic phases AB, ternary equiatomic phases ABC, and full Heusler phases AB 2 C. Our analysis emphasizes the use of real experimental data and places special value on confirming predictions through experiment. Chemical descriptors are carefully chosen through a rigorous procedure called cluster resolution feature selection. Predictions for crystal structures are quantified by evaluating

Self-irradiation damage to the local structure of plutonium and plutonium intermetallics

Energy Technology Data Exchange (ETDEWEB)

Booth, C. H.; Jiang Yu; Medling, S. A. [Chemical Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, California 94720 (United States); Wang, D. L. [Nuclear Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, California 94720 (United States); Costello, A. L.; Schwartz, D. S.; Mitchell, J. N.; Tobash, P. H. [Materials Science and Technology Division, Los Alamos National Laboratory, Los Alamos, New Mexico 87545 (United States); Bauer, E. D. [Materials Physics and Applications Division, Los Alamos National Laboratory, Los Alamos, New Mexico 87545 (United States); McCall, S. K.; Wall, M. A.; Allen, P. G. [Condensed Matter and Materials Division, Lawrence Livermore National Laboratory, Livermore, California 94550 (United States)

2013-03-07

The effect of self-irradiation damage on the local structure of {delta}-Pu, PuAl{sub 2}, PuGa{sub 3}, and other Pu intermetallics has been determined for samples stored at room temperature using the extended x-ray absorption fine-structure (EXAFS) technique. These measurements indicate that the intermetallic samples damage at a similar rate as indicated in previous studies of PuCoGa{sub 5}. In contrast, {delta}-Pu data indicate a much slower damage accumulation rate. To explore the effect of storage temperature and possible room temperature annealing effects, we also collected EXAFS data on a {delta}-Pu sample that was held at less than 32 K for a two month period. This sample damaged much more quickly. In addition, the measurable damage was annealed out at above only 135 K. Data from samples of {delta}-Pu with different Ga concentrations and results on all samples collected from different absorption edges are also reported. These results are discussed in terms of the vibrational properties of the materials and the role of Ga in {delta}-Pu as a network former.

Isothermal analysis of intermetallic MmNi5-xAlx in air decomposition processes

International Nuclear Information System (INIS)

Obregon, S.A.; Andrade Gamboa, J.J.; Esquivel, M.R.

2012-01-01

In this paper, it is analyzed the behavior of the degree of reaction as function of time α (t) of a sample of MmNi 4.3 Al 0.7 (Mm mischmetal = La 0.25 Ce 0.52 Nd 0.17 Pr 0.06 ) at different temperatures. The curves were obtained by isothermal calorimetric techniques. As a result of this study, it was observed that the kinetics of intermetallic can be separated into two main stages. At temperatures below 350 o C, the first stage is the oxidation of Mm and Al. At temperatures over 400 o C, the oxidation of Ni is also produced parallel to the above mentioned reactions. But the kinetics of the last one is at least three orders of magnitude slower. It was also observed that no thermal event occurs below 180 o C. It indicates that the intermetallic do not react at temperatures below this temperature value (author)

Plutonium microstructures. Part 2. Binary and ternary alloys

International Nuclear Information System (INIS)

Cramer, E.M.; Bergin, J.B.

1983-12-01

This report is the second of three parts that exhibit illustrations of inclusions in plutonium metal from inherent and tramp impurities, of intermetallic and nonmetallic constituents from alloy additions, and of the effects of thermal and mechanical treatments. This part includes illustrations of the microstructures in binary cast alloys and a few selected ternary alloys that result from measured additions of diluent elements, and of the microconstituents that are characteristic of phase fields in extended alloy systems. Microhardness data are given and the etchant used in the preparation of each sample is described

Corrosion behavior of Fe3Al intermetallics with addition of lithium, cerium and nickel in 2.5 % SO2+N2 at 900 degree centigrade

International Nuclear Information System (INIS)

Luna-Ramirez, A.; Porcayo-Calderon, J.; Martinez-Villafane, A.; Gonzalez-Rodriguez, J. G.; Chaon-Nava, J. G.

2012-01-01

The corrosion behavior of Fe 3 Al-type intermetallic alloys with addition of 1 at. % cerium, lithium and nickel at high temperature has been studied. The various alloys were exposed to an environment composed of 2.5 % SO 2 +N 2 at 900 degree centigrade for 48 h. For all the intermetallic tested, the corrosion kinetics showed a parabolic behavior. The alloy, which showed less corrosion rate, was the Fe3AlNi alloy, being Fe 3 AlCeLi the alloy with the highest corrosion rate. For the various alloys, energy dispersive X-ray spectroscopy analysis, EDS, on the developed scale only detected aluminum, oxygen, and traces of iron and cerium, suggesting the formation of alumina as main component. The intermetallic alloys showed oxide cracking and spalling. The intermetallic chemical composition played an important role in defining the oxide scale morphology and the extent of damage. (Author) 39 refs.

Catalytic Hydrogenation of Levulinic Acid in Water into g-Valerolactone over Bulk Structure of Inexpensive Intermetallic Ni-Sn Alloy Catalysts

Directory of Open Access Journals (Sweden)

Rodiansono Rodiansono

2015-07-01

Full Text Available A bulk structure of inexpensive intermetallic nickel-tin (Ni-Sn alloys catalysts demonstrated highly selective in the hydrogenation of levulinic acid in water into g-valerolactone. The intermetallic Ni-Sn catalysts were synthesized via a very simple thermochemical method from non-organometallic precursor at low temperature followed by hydrogen treatment at 673 K for 90 min. The molar ratio of nickel salt and tin salt was varied to obtain the corresponding Ni/Sn ratio of 4.0, 3.0, 2.0, 1.5, and 0.75. The formation of Ni-Sn alloy species was mainly depended on the composition and temperature of H2 treatment. Intermetallics Ni-Sn that contain Ni3Sn, Ni3Sn2, and Ni3Sn4 alloy phases are known to be effective heterogeneous catalysts for levulinic acid hydrogenation giving very excellence g-valerolactone yield of >99% at 433 K, initial H2 pressure of 4.0 MPa within 6 h. The effective hydrogenation was obtained in H2O without the formation of by-product. Intermetallic Ni-Sn(1.5 that contains Ni3Sn2 alloy species demonstrated very stable and reusable catalyst without any significant loss of its selectivity. © 2015 BCREC UNDIP. All rights reserved. Received: 26th February 2015; Revised: 16th April 2015; Accepted: 22nd April 2015  How to Cite: Rodiansono, R., Astuti, M.D., Ghofur, A., Sembiring, K.C. (2015. Catalytic Hydrogenation of Levulinic Acid in Water into g-Valerolactone over Bulk Structure of Inexpensive Intermetallic Ni-Sn Alloy Catalysts. Bulletin of Chemical Reaction Engineering & Catalysis, 10 (2: 192-200. (doi:10.9767/bcrec.10.2.8284.192-200Permalink/DOI: http://dx.doi.org/10.9767/bcrec.10.2.8284.192-200  

Two stages of Kondo effect and competition between RKKY and Kondo in Gd-based intermetallic compound

International Nuclear Information System (INIS)

Vaezzadeh, Mehdi; Yazdani, Ahmad; Vaezzadeh, Majid; Daneshmand, Gissoo; Kanzeghi, Ali

2006-01-01

The magnetic behavior of Gd-based intermetallic compound (Gd 2 Al (1-x) Au x ) in the form of the powder and needle, is investigated. All the samples are an orthorhombic crystal structure. Only the compound with x=0.4 shows the Kondo effect (other compounds have a normal behavior). Although, for the compound in the form of powder, with x=0.4, the susceptibility measurement χ(T) shows two different stages. Moreover for (T>T K2 ) a fall of the value of χ(T) is observable, which indicates a weak presence of ferromagnetic phase. About the two stages of Kondo effect, we observe at the first (T K1 ) an increase of χ(T) and in the second stage (T K2 ) a new remarkable decrease of χ(T) (T K1 >T K2 ). For the sample in the form of needles, the first stage is observable only under high magnetic field. This first stage could be corresponds to a narrow resonance between Kondo cloud and itinerant electron. The second stage, which is remarkably visible for the sample in the form of the powder, can be attribute to a complete polarization of Kondo cloud. Observation of these two Kondo stages could be due to the weak presence of RKKY contribution

Formation of intermetallic phases in AlSi7Fe1 alloy processed under microgravity and forced fluid flow conditions and their influence on the permeability

Science.gov (United States)

Steinbach, S.; Ratke, L.; Zimmermann, G.; Budenkova, O.

2016-03-01

Ternary Al-6.5wt.%Si-0.93wt.%Fe alloy samples were directionally solidified on-board of the International Space Station ISS in the ESA payload Materials Science Laboratory (MSL) equipped with Low Gradient Furnace (LGF) under both purely diffusive and stimulated convective conditions induced by a rotating magnetic field. Using different analysis techniques the shape and distribution of the intermetallic phase β-Al5SiFe in the dendritic microstructure was investigated, to study the influence of solidification velocity and fluid flow on the size and spatial arrangement of intermetallics. Deep etching as well as 3-dimensional computer tomography measurements characterized the size and the shape of β-Al5SiFe platelets: Diffusive growth results in a rather homogeneous distribution of intermetallic phases, whereas forced flow promotes an increase in the amount and the size of β-Al5SiFe platelets in the centre region of the samples. The β-Al5SiFe intermetallics can form not only simple platelets, but also be curved, branched, crossed, interacting with dendrites and porosity located. This leads to formation of large and complex groups of Fe-rich intermetallics, which reduce the melt flow between dendrites leading to lower permeability of the mushy zone and might significantly decrease feeding ability in castings.

Negative thermal expansion induced by intermetallic charge transfer.

Science.gov (United States)

Azuma, Masaki; Oka, Kengo; Nabetani, Koichiro

2015-06-01

Suppression of thermal expansion is of great importance for industry. Negative thermal expansion (NTE) materials which shrink on heating and expand on cooling are therefore attracting keen attention. Here we provide a brief overview of NTE induced by intermetallic charge transfer in A-site ordered double perovskites SaCu 3 Fe 4 O 12 and LaCu 3 Fe 4- x Mn x O 12 , as well as in Bi or Ni substituted BiNiO 3 . The last compound shows a colossal dilatometric linear thermal expansion coefficient exceeding -70 × 10 -6 K -1 near room temperature, in the temperature range which can be controlled by substitution.

Intermetallic compound development for the 21st century

International Nuclear Information System (INIS)

Munroe, P.R.

2000-01-01

lntermetallic compounds have been vigorously researched for the past twenty years. As a result of these studies the fundamental behaviour of a number of transition metal aluminides and suicides is now well understood, and a number of alloys with commercially acceptable properties have been developed. Future challenges for these alloys, for example Ni 3 AI, TiAI and Fe 3 AI, are focused on the development of large-scale production routes. However, there remain a number of other intermetallic compounds, such as Laves phases, which exhibit some promising properties, but little is presently known about their intrinsic behaviour. For compounds such as these more fundamental studies are required

Study of Intermetallic Nanostructures for Light-Water Reactors

Energy Technology Data Exchange (ETDEWEB)

Jensen, Niels Grobech [Univ. of California, Davis, CA (United States); Asta, Mark D. [Univ. of California, Berkeley, CA (United States); Hosemann, Peter [Univ. of California, Berkeley, CA (United States); Maloy, Stuart [Los Alamos National Lab. (LANL), Los Alamos, NM (United States)

2015-09-30

High temperature mechanical measurements were conducted to study the effect of the dynamic precipitation process of PH 13-8 Mo maraging steel. Yield stress, ultimate tensile strength, total elongation, hardness, strain rate sensitivity and activation volume were evaluated as a function of the temperature. The dynamic changes in the mechanical properties at different temperatures were evaluated and a balance between precipitation hardening and annealed softening is discussed. A comparison between hardness and yield stress and ultimate tensile strength over a temperature range from 300 to 600 °C is made. The behavior of the strain rate sensitivity was correlated with the intermetallic precipitates formed during the experiments.

An application of Pettifor structure maps for the identification of pseudo-binary quasicrystalline intermetallics

International Nuclear Information System (INIS)

Ranganathan, S.; Inoue, A.

2006-01-01

Quasicrystal-forming ability is considered from the viewpoint of Pettifor maps, where a single phenomenological coordinate, the Mendeleev number, captures the bonding characteristics of elements in forming intermetallics. By considering the largest sized atom as the most important constituent, it is shown that most known ternary and quaternary quasicrystals can be treated as pseudo-binary intermetallics. This also results in a classification of quasicrystals into four structural classes based on the nature of the bond orbital - s, p, d or f - of the large atom with four associated related crystal structures. A colour scheme is introduced to indicate preferences for two types of sites. We propose a new classification of quasicrystals as centred on Li, Mg, Al, Ga, Ca, Sc, Y, Ti, Zr, Hf and rare earth elements, as they are the largest atoms in the constituent quasicrystals in contrast to the conventional classification based on majority species

An application of Pettifor structure maps for the identification of pseudo-binary quasicrystalline intermetallics

Energy Technology Data Exchange (ETDEWEB)

Ranganathan, S. [Department of Metallurgy, Indian Institute of Science, CV Raman Avenue, Bangalore 560012, Karnataka (India) and Institute for Materials Research, Tohoku University, Sendai 9808577 (Japan)]. E-mail: rangu@met.iisc.ernet.in; Inoue, A. [Institute for Materials Research, Tohoku University, Sendai 9808577 (Japan)

2006-08-15

Quasicrystal-forming ability is considered from the viewpoint of Pettifor maps, where a single phenomenological coordinate, the Mendeleev number, captures the bonding characteristics of elements in forming intermetallics. By considering the largest sized atom as the most important constituent, it is shown that most known ternary and quaternary quasicrystals can be treated as pseudo-binary intermetallics. This also results in a classification of quasicrystals into four structural classes based on the nature of the bond orbital - s, p, d or f - of the large atom with four associated related crystal structures. A colour scheme is introduced to indicate preferences for two types of sites. We propose a new classification of quasicrystals as centred on Li, Mg, Al, Ga, Ca, Sc, Y, Ti, Zr, Hf and rare earth elements, as they are the largest atoms in the constituent quasicrystals in contrast to the conventional classification based on majority species.

Evolution of Fe based intermetallic phases in Al–Si hypoeutectic casting alloys: Influence of the Si and Fe concentrations, and solidification rate

Energy Technology Data Exchange (ETDEWEB)

Gorny, Anton; Manickaraj, Jeyakumar [Light Metal Casting Research Centre (LMCRC), Department of Mechanical Engineering, McMaster University, 1280 Main Street W, Hamilton, ON, Canada L8S 4L7 (Canada); Cai, Zhonghou [Advanced Photon Source, Argonne National Laboratory, 9700 South Cass Avenue, Argonne, IL 60439 (United States); Shankar, Sumanth, E-mail: shankar@mcmaster.ca [Light Metal Casting Research Centre (LMCRC), Department of Mechanical Engineering, McMaster University, 1280 Main Street W, Hamilton, ON, Canada L8S 4L7 (Canada)

2013-11-15

Highlights: •Anomalous evolution of Fe based intermetallic phases in Al–Si–Fe alloys. •XRF coupled with nano-diffraction to confirm the nano-size Fe intermetallic phases. •Crystallography of the θ-Al{sub 13}Fe{sub 4}, τ{sub 5}-Al{sub 8}Fe{sub 2}Si and τ{sub 6}-Al{sub 9}Fe{sub 2}Si{sub 2} phases. •Peritectic reactions involving the Fe intermetallic phases in Al–Si–Fe alloys. -- Abstract: Al–Si–Fe hypoeutectic cast alloy system is very complex and reported to produce numerous Fe based intermetallic phases in conjunction with Al and Si. This publication will address the anomalies of phase evolution in the Al–Si–Fe hypoeutectic casting alloy system; the anomaly lies in the peculiarities in the evolution and nature of the intermetallic phases when compared to the thermodynamic phase diagram predictions and past publications of the same. The influence of the following parameters, in various combinations, on the evolution and nature of the intermetallic phases were analyzed and reported: concentration of Si between 2 and 12.6 wt%, Fe between 0.05 and 0.5 wt% and solidification rates of 0.1, 1, 5 and 50 K s{sup −1}. Two intermetallic phases are observed to evolve in these alloys under these solidification conditions: the τ{sub 5}-Al{sub 8}SiFe{sub 2} and τ{sub 6}-Al{sub 9}Fe{sub 2}Si{sub 2}. The τ{sub 5}-Al{sub 8}SiFe{sub 2} phase evolves at all levels of the parameters during solidification and subsequently transforms into the τ{sub 6}-Al{sub 9}Fe{sub 2}Si{sub 2} through a peritectic reaction when promoted by certain combinations of solidification parameters such as higher Fe level, lower Si level and slower solidification rates. Further, it is also hypothesized from experimental evidences that the θ-Al{sub 13}Fe{sub 4} binary phase precludes the evolution of the τ{sub 5} during solidification and subsequently transforms into the τ{sub 6} phase during solidification. These observations are anomalous to the publications as prior art and

The Effect of CuSn Intermetallics on the Interstrand Contact Resistance in Superconducting Cables for the Large Hadron Collider (LHC)

CERN Document Server

Scheuerlein, C; Jacob, P; Leroy, D; Oberli, L R; Taborelli, M

2005-01-01

The LHC superconducting cables are submitted to a 200°C heat-treatment in air in order to increase the resistance between the crossing strands (RC) within the cable. During this treatment the as-applied Sn-Ag alloy strand coating is transformed into a CuSn intermetallic compound layer. The microstructure, the surface topography and the surface chemistry of the non-reacted and reacted coatings have been characterised by different techniques, notably focused ion beam (FIB), transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDS) and X-ray photoelectron spectroscopy (XPS). Based on the results obtained by these techniques the different influences that the intermetallics have on RC are discussed. The desired RC is obtained only when a continuous Cu3Sn layer is formed, i.e. a sufficient wetting of the Cu substrate by the tinning alloy is crucial. Among other effects the formation of the comparatively hard intermetallics roughens the surface and, thus, reduces the true contact area and i...

Pressure effect on magnetic and magnetotransport properties of intermetallic and colossal magnetoresistance oxide compounds

Czech Academy of Sciences Publication Activity Database

Arnold, Zdeněk; Ibarra, M. R.; Algarabel, P. A.; Marquina, C.; De Teresa, J. M.; Morellon, L.; Blasco, J.; Magen, C.; Prokhnenko, Olexandr; Kamarád, Jiří; Ritter, C.

2005-01-01

Roč. 17, - (2005), S3035-S3055 ISSN 0953-8984 Institutional research plan: CEZ:AV0Z10100521 Keywords : pressure effect * intermetallic compounds * magnetic properties * magnetic phase transitions * magnetotransport properties * oxides Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.145, year: 2005

Ultrafast and Highly Reversible Sodium Storage in Zinc-Antimony Intermetallic Nanomaterials

Energy Technology Data Exchange (ETDEWEB)

Nie, Anmin [Univ. of Illinois, Chicago, IL (United States). Mechanical and Industrial Engineering Department; Gan, Li-yong [Southwest Jiaotong University, Chengdu, Sichuan, (China). Key Laboratory of Advanced Technology of Materials; Cheng, Yingchun [Nanjing Univ. of Technology (China). Institute of Advanced Materials (IAM); Tao, Xinyong [Zhejiang Univ. of Technology, Hangzhou (China). College of Materials Science and Engineering; Yuan, Yifei [Argonne National Lab. (ANL), Argonne, IL (United States). Chemical Sciences and Engineering Division; Sharifi-Asl, Soroosh [Univ. of Illinois, Chicago, IL (United States). Mechanical and Industrial Engineering Department; He, Kun [Univ. of Illinois, Chicago, IL (United States). Mechanical and Industrial Engineering Department; Asayesh-Ardakani, Hasti [Univ. of Illinois, Chicago, IL (United States). Mechanical and Industrial Engineering Department; Vasiraju, Venkata [Texas A& M Univ., College Station, TX (United States). Artie McFerrin Department of Chemical Engineering; Lu, Jun [Argonne National Lab. (ANL), Argonne, IL (United States). Chemical Sciences and Engineering Division; Mashayek, Farzad [Univ. of Illinois, Chicago, IL (United States). Mechanical and Industrial Engineering Department; Klie, Robert [Univ. of Illinois, Chicago, IL (United States). Department of Physics; Vaddiraju, Sreeram [Texas A& M Univ., College Station, TX (United States). Artie McFerrin Department of Chemical Engineering; Schwingenschlögl, Udo [King Abdullah Univ. of Science and Technology, Thuwal (Saudi Arabia); Shahbazian-Yassar, Reza [Univ. of Illinois, Chicago, IL (United States). Mechanical and Industrial Engineering Department

2015-12-17

The progress on sodium-ion battery technology faces many grand challenges, one of which is the considerably lower rate of sodium insertion/deinsertion in electrode materials due to the larger size of sodium (Na) ions and complicated redox reactions compared to the lithium-ion systems. Here, it is demonstrated that sodium ions can be reversibly stored in Zn-Sb intermetallic nanowires at speeds that can exceed 295 nm s^-1. Remarkably, these values are one to three orders of magnitude higher than the sodiation rate of other nanowires electrochemically tested with in situ transmission electron micro­scopy. It is found that the nanowires display about 161% volume expansion after the first sodiation and then cycle with an 83% reversible volume expansion. Despite their massive expansion, the nanowires can be cycled without any cracking or facture during the ultrafast sodiation/desodiation process. Additionally, most of the phases involved in the sodiation/desodiation process possess high electrical conductivity. More specifically, the NaZnSb exhibits a layered structure, which provides channels for fast Na⁺ diffusion. This observation indicates that Zn-Sb intermetallic nanomaterials offer great promise as high rate and good cycling stability anodic materials for the next generation of sodium-ion batteries.

Rapid Solidification of Sn-Cu-Al Alloys for High-Reliability, Lead-Free Solder: Part II. Intermetallic Coarsening Behavior of Rapidly Solidified Solders After Multiple Reflows

Science.gov (United States)

Reeve, Kathlene N.; Choquette, Stephanie M.; Anderson, Iver E.; Handwerker, Carol A.

2016-12-01

Controlling the size, dispersion, and stability of intermetallic compounds in lead-free solder alloys is vital to creating reliable solder joints regardless of how many times the solder joints are melted and resolidified (reflowed) during circuit board assembly. In this article, the coarsening behavior of Cu x Al y and Cu6Sn5 in two Sn-Cu-Al alloys, a Sn-2.59Cu-0.43Al at. pct alloy produced via drip atomization and a Sn-5.39Cu-1.69Al at. pct alloy produced via melt spinning at a 5-m/s wheel speed, was characterized after multiple (1-5) reflow cycles via differential scanning calorimetry between the temperatures of 293 K and 523 K (20 °C and 250 °C). Little-to-no coarsening of the Cu x Al y particles was observed for either composition; however, clustering of Cu x Al y particles was observed. For Cu6Sn5 particle growth, a bimodal size distribution was observed for the drip atomized alloy, with large, faceted growth of Cu6Sn5 observed, while in the melt spun alloy, Cu6Sn5 particles displayed no significant increase in the average particle size, with irregularly shaped, nonfaceted Cu6Sn5 particles observed after reflow, which is consistent with shapes observed in the as-solidified alloys. The link between original alloy composition, reflow undercooling, and subsequent intermetallic coarsening behavior was discussed by using calculated solidification paths. The reflowed microstructures suggested that the heteroepitaxial relationship previously observed between the Cu x Al y and the Cu6Sn5 was maintained for both alloys.

Heat resistance of Fe-Al intermetallics in the context of selected heat-resistant and hihg-temperature creep resistant steels

Directory of Open Access Journals (Sweden)

P. Baranowski

2009-04-01

Full Text Available Results are hereby presented of heat-resistance tests of two Fe3Al and FeAl intermetallic phase-based alloys in the context of St41k-typeboiler steel and 50H21G9N4 high-temperature creep resistant steel. It has been ascertained that heat resistance of the 50H21G9N4 steeland of the Fe3Al and FeAl intermetallic phase-based alloys significantly exceeds that of the boiler steel tested in the air atmosphere and the atmosphere of a flue gas with CO, CO2, SiO2 content alike. Improvement of these properties depends of exposure conditions. The largest differences have been observed when the tests were carried out in temperature 1023 K and in the flue gas atmosphere. The differences have been more and more noticeable as the exposition duration extended. A tendency has been also recorded of smaller mass decrements of the Fe3Al and FeAl intermetallic phase-based alloys as compared to the 50H21G9N4 steel.

Structure evolution of multilayer materials of heat-resistant intermetallic compounds under the influence of temperature in the process of diffusion welding under pressure and their mechanical properties

Energy Technology Data Exchange (ETDEWEB)

Korzhov, Valeriy P.; Karpov, Michael I.; Prokhorov, Dmitriy V. [Institute of Solid State Physics, Russian Academy of Sciences, Chernogolovka (Russian Federation)

2013-07-01

Multilayer materials of high-resistant intermetallic compounds of some transition metals with aluminum and silicon were obtained by diffusion welding of packages, collected from a large number of the respective foils, such as niobium and aluminum. Materials of intermetallics with silicon were obtained by the welding of packages built from metal foils with Si-coating. The change in the structure according to the temperature of the welding was studied, and the high-temperature bending strength was determined. Key words: multilayer composite, high-resistant material, intermetallic compound, diffusion welding, package rolling, layered structure, bending strength.

Spontaneous growth of whiskers on RE-bearing intermetallic compounds of Sn-RE, In-RE, and Pb-RE

International Nuclear Information System (INIS)

Liu Meng; Xian Aiping

2009-01-01

A phenomenon of the whiskers growth on the bulk rare earth (RE)-intermetallic compounds of NdSn 3 , NdIn 3 , and LaPb 3 is reported. The whiskers formed spontaneously on all of the RE-intermetallic compounds after exposed to room ambience (21-28 deg. C/20-56% RH, relative humidity) for several days. Among the samples, the propensity of whisker growth for NdSn 3 is the strongest, on which the tin whiskers were flourishing and covered all of the surfaces after exposed to room ambience for 22 days; while LaPb 3 is the secondary and NdIn 3 is the last one. Observed by SEM, the whiskers were exhibited as different morphology, size, and number density. The XRD analysis confirms the existence of RE(OH) 3 after whiskers formed, also, the weight gain curve of the samples exposed to room ambience supports that a spontaneous chemical reaction of the RE-intermetallic compounds with water in room ambience takes place. In discussion, it is proposed that the fresh metal atoms released by the chemical reaction could be causative to result in nucleation and spontaneous growth of the whiskers, while the anisotropy of crystal structure could be a reason to understand the difference of the whisker growth behaviors between Sn and Pb.

Intermetallic precipitation in rare earth-treated A413.1 alloy. A metallographic study

International Nuclear Information System (INIS)

Samuel, Agnes M.; Samuel, Fawzy H.

2018-01-01

The present study was performed mainly on A413.1 alloy. Measured amounts of La, Ce or La+Ce, Ti and Sr were added to the molten alloy in the form of master alloys. Samples sectioned from castings obtained from thermal analysis experiments were used for preparing samples for metallographic examination. The results show that addition of rare earth (RE) metals to Al-Si alloys increased the α-Al nucleation temperature and depressed the Al-Si eutectic formation temperature, thereby increasing the solidification range. Depending upon the alloying elements/additives, a large number of RE-based intermetallics could be formed: Al 4 (Ce,La), Al 13 (Ce,La) 2 Cu 3 , Al 7 (Cu,Fe) 6 (Ce,La) 6 Si 2 , Al 4 La, Al 2 La 5 Si 2 , Al 2 Ce 5 Si 2 , Al 2 (Ce,La) 5 Si 2 . Under an electron microscope, these phases appear in backscatter imaging mode in the form of thin grayish-white platelets on the dark gray Al matrix. The average thickness of these platelets is about 1.5 μm. When the alloy is grain refined with Ti-based master alloys, precipitation of a gray phase in the form of sludge is observed: Al 12 La 3 Ti 2 , or Al 12 (Ce,La) 3 Ti 2 . Regardless the alloy composition, the RE/Al ratios remain constant in each type of intermetallic. Rare earth metals have a strong affinity to react with Sr (resulting in partial modification of the eutectic Si particles) as well as some transition elements, in particular Ti and Cu. Iron has a very low affinity for interaction with RE metals. It is only confined to Fe-based intermetallics.

Intermetallic precipitation in rare earth-treated A413.1 alloy. A metallographic study

Energy Technology Data Exchange (ETDEWEB)

Samuel, Agnes M.; Samuel, Fawzy H. [Univ. du Quebec a Chicoutimi (Canada). Dept. des Sciences Appliquees; Doty, Herbert W. [General Motors, Pontiac, MI (United States). Materials Engineering; Valtierra, Salvador [Nemak, S.A., Garza Garcia (Mexico)

2018-02-15

The present study was performed mainly on A413.1 alloy. Measured amounts of La, Ce or La+Ce, Ti and Sr were added to the molten alloy in the form of master alloys. Samples sectioned from castings obtained from thermal analysis experiments were used for preparing samples for metallographic examination. The results show that addition of rare earth (RE) metals to Al-Si alloys increased the α-Al nucleation temperature and depressed the Al-Si eutectic formation temperature, thereby increasing the solidification range. Depending upon the alloying elements/additives, a large number of RE-based intermetallics could be formed: Al{sub 4}(Ce,La), Al{sub 13}(Ce,La){sub 2}Cu{sub 3}, Al{sub 7}(Cu,Fe){sub 6}(Ce,La){sub 6}Si{sub 2}, Al{sub 4}La, Al{sub 2}La{sub 5}Si{sub 2}, Al{sub 2}Ce{sub 5}Si{sub 2}, Al{sub 2}(Ce,La){sub 5}Si{sub 2}. Under an electron microscope, these phases appear in backscatter imaging mode in the form of thin grayish-white platelets on the dark gray Al matrix. The average thickness of these platelets is about 1.5 μm. When the alloy is grain refined with Ti-based master alloys, precipitation of a gray phase in the form of sludge is observed: Al{sub 12}La{sub 3}Ti{sub 2}, or Al{sub 12}(Ce,La){sub 3}Ti{sub 2}. Regardless the alloy composition, the RE/Al ratios remain constant in each type of intermetallic. Rare earth metals have a strong affinity to react with Sr (resulting in partial modification of the eutectic Si particles) as well as some transition elements, in particular Ti and Cu. Iron has a very low affinity for interaction with RE metals. It is only confined to Fe-based intermetallics.

Electromagnetic generation of volume waves in RFe2 intermetallics

International Nuclear Information System (INIS)

Il'yasov, R.S.; Borovkova, M.A.

1996-01-01

Experimental results are presented on the phenomenon of electromagneto-acoustic transformation of longitudinal and cross waves in RFe 2 intermetallics. It is shown that in the range from the room temperature to Curie point the generation of ultrasound occurs only at the expense of one-ion anisotropic magnetostriction. In the vicinity of Curie point the contribution of isotropic magnetostriction of paraprocess is not observed. The quantitative interpretation is given to temperature and field dependences of electromagneto-acoustic transformation parameters. A noticeable temperature hysteresis of the above-mentioned transformation is revealed in ErFe 2 near the point of compensation. 7 refs.; 5 figs

Oxidation behavior of niobium aluminide intermetallics protected by aluminide and silicide diffusion coatings

International Nuclear Information System (INIS)

Li, Y.; Soboyejo, W.; Rapp, R.A.

1999-01-01

The isothermal and cyclic oxidation behavior of a new class of damage-tolerant niobium aluminide (Nb 3 Al-xTi-yCr) intermetallics is studied between 650 C and 850 C. Protective diffusion coatings were deposited by pack cementation to achieve the siliciding or aluminizing of substrates with or without intervening Mo or Ni layers, respectively. The compositions and microstructures of the resulting coatings and oxidized surfaces were characterized. The isothermal and cyclic oxidation kinetics indicate that uncoated Nb-40Ti-15Al-based intermetallics may be used up to ∼750 C. Alloying with Cr improves the isothermal oxidation resistance between 650 C and 850 C. The most significant improvement in oxidation resistance is achieved by the aluminization of electroplated Ni interlayers. The results suggest that the high-temperature limit of niobium aluminide-based alloys may be increased to 800 C to 850 C by aluminide-based diffusion coatings on ductile Ni interlayers. Indentation fracture experiments also indicate that the ductile nickel interlayers are resistant to crack propagation in multilayered aluminide-based coatings

High temperature cyclic oxidation of Ti-Al based intermetallic in static laboratory air

International Nuclear Information System (INIS)

Astuty Amrin; Esah Hamzah; Nurfashahidayu Mohd Badri; Hafida Hamzah

2007-01-01

The objective of this study is to investigate the oxidation behaviour of binary γ-Ti Al based intermetallics with composition (at%) of 45A, 48Al and 50 Al, and ternary alloys of Ti-48Al containing 2Cr and 4Cr. Thermal cyclic oxidation was conducted discontinuously at temperatures of 700 degree Celsius and 900 degree Celsius in static laboratory air. Optical microscopy, Scanning Electron Microscopy (SEM), Energy Dispersive X-ray Analysis (EDX) and X-ray diffraction (XRD) techniques were employed for the analysis. SEM examination of cross-sectional samples using secondary electron and line-scan analysis after exposure at 700 degree Celsius showed that non-adherent oxides scales formed due to the spallation caused by cyclic condition. For exposure to 900 degree Celsius, only binary alloys exhibited breakaway oxidation whereas the oxide scales formed on the ternary alloys were well-adhered on the substrate alloy. Overall, exposure at 900 degree Celsius resulted in thicker and harder oxide scales and addition of Cr seems to improve oxidation resistance of Ti-Al based intermetallics at higher temperature. (author)

Diffusion in substitutionally disordered B2 intermetallics

International Nuclear Information System (INIS)

Belova, I.V.; Murch, G.E.

2002-01-01

In this paper, a comprehensive diffusion kinetics theory is formulated to describe seamlessly tracer and chemical diffusion in antistructurally disordered B2 intermetallics showing positive and negative deviations from stoichiometry. The theory is based around unit processes consisting of six-jump cycles that can be assisted by intrinsic and extrinsic antistructural atoms of either atomic species. The Ising alloy model is used to illustrate the formalism, but the formalism can be adapted to other models. Expressions are developed for the tracer diffusion coefficients, the phenomenological coefficients, the intrinsic diffusion coefficients, the interdiffusion coefficient and the various correlation factor components. Results for the tracer and collective correlation factors and the vacancy wind factor (in interdiffusion) are in excellent agreement with results from Monte Carlo computer simulations based around single vacancy jumps. (author)

PAC and μSr investigations of light interstitial diffusion in intermetallic hydrides

International Nuclear Information System (INIS)

Boyer, P.; Baudry, A.

1988-01-01

Specific aspects of the Perturbed Angular Correlation (PAC) of gamma rays concerning its application to the study of atomic diffusion in solids are presented. PAC results recently obtained on the 181 Ta probe in several crystalline and amorphous phases of Zr 2 Ni hydrides are briefly summarized. Preliminary μSR results relative to these intermetallic hydrides are presented and compared to the PAC data

Electronic Structure of GdCuGe Intermetallic Compound

Science.gov (United States)

Lukoyanov, A. V.; Knyazev, Yu. V.; Kuz'min, Yu. I.

2018-04-01

The electronic structure of GdCuGe intermetallic compound has been studied. Spin-polarized energy spectrum calculations have been performed by the band method with allowance for strong electron correlations in the 4 f-shell of gadolinium ions. Antiferromagnetic ordering of GdCuGe at low temperatures has been obtained in a theoretical calculation, with the value of the effective magnetic moment of gadolinium ions reproduced in fair agreement with experimental data. The electronic density of states has been analyzed. An optical conductivity spectrum has been calculated for GdCuGe; it reveals specific features that are analogous to the ones discovered previously in the GdCuSi compound with a similar hexagonal structure.

Formation of Ni-Ti intermetallics during reactive sintering at 500-650 degrees C

Czech Academy of Sciences Publication Activity Database

Novák, P.; Pokorný, P.; Vojtěch, V.; Knaislová, A.; Školáková, A.; Čapek, J.; Karlík, M.; Kopeček, Jaromír

2015-01-01

Roč. 155, Apr (2015), s. 113-121 ISSN 0254-0584 R&D Projects: GA ČR(CZ) GA14-03044S Institutional support: RVO:68378271 Keywords : intermetallic compounds * powder metallurgy * electron microscopy * microstructure Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 2.101, year: 2015

Effects of surface polishing and annealing on the optical conductivity of intermetallic compounds

International Nuclear Information System (INIS)

Rhee, Joo Yull

1999-01-01

The optical conductivity spectra of several intermetallic compounds were measured by spectroscopic ellipsometry. Three spectra were measured for each compound; just after the sample was mechanically polished, at high temperature, and after the sample was annealed at 110 .deg. C for at least one day and cooled to room temperature. An equiatomic FeTi alloy showed the typical effects of annealing after mechanical polishing of surface. The spectrum after annealing had a larger magnitude and sharper structures than the spectrum before annealing. We also observed shifts of peaks in the spectrum. A relatively low-temperature annealing gave rise to unexpectedly substantial effects, and the effects were explained by recrystallization and/or a disorder → order transition of the surface of the sample which was damaged and, hence, became highly disordered by mechanical polishing. Similar effects were also observed when the sample temperature was lowered. The observed changes upon annealing could partly be explained by presumption that the recrystallization would be realized in such a way that the average atomic spacing would be reduced

Spark plasma sintering of titanium aluminide intermetallics and its composites

Science.gov (United States)

Aldoshan, Abdelhakim Ahmed

Titanium aluminide intermetallics are a distinct class of engineering materials having unique properties over conventional titanium alloys. gamma-TiAl compound possesses competitive physical and mechanical properties at elevated temperature applications compared to Ni-based superalloys. gamma-TiAl composite materials exhibit high melting point, low density, high strength and excellent corrosion resistance. Spark plasma sintering (SPS) is one of the powder metallurgy techniques where powder mixture undergoes simultaneous application of uniaxial pressure and pulsed direct current. Unlike other sintering techniques such as hot iso-static pressing and hot pressing, SPS compacts the materials in shorter time (< 10 min) with a lower temperature and leads to highly dense products. Reactive synthesis of titanium aluminide intermetallics is carried out using SPS. Reactive sintering takes place between liquid aluminum and solid titanium. In this work, reactive sintering through SPS was used to fabricate fully densified gamma-TiAl and titanium aluminide composites starting from elemental powders at different sintering temperatures. It was observed that sintering temperature played significant role in the densification of titanium aluminide composites. gamma-TiAl was the predominate phase at different temperatures. The effect of increasing sintering temperature on microhardness, microstructure, yield strength and wear behavior of titanium aluminide was studied. Addition of graphene nanoplatelets to titanium aluminide matrix resulted in change in microhardness. In Ti-Al-graphene composites, a noticeable decrease in coefficient of friction was observed due to the influence of self-lubrication caused by graphene.

Ground state searches in fcc intermetallics

International Nuclear Information System (INIS)

Wolverton, C.; de Fontaine, D.; Ceder, G.; Dreysse, H.

1991-12-01

A cluster expansion is used to predict the fcc ground states, i.e., the stable phases at zero Kelvin as a function of composition, for alloy systems. The intermetallic structures are not assumed, but derived regorously by minimizing the configurational energy subject to linear constraints. This ground state search includes pair and multiplet interactions which spatially extend to fourth nearest neighbor. A large number of these concentration-independent interactions are computed by the method of direct configurational averaging using a linearized-muffin-tin orbital Hamiltonian cast into tight binding form (TB-LMTO). The interactions, derived without the use of any adjustable or experimentally obtained parameters, are compared to those calculated via the generalized perturbation method extention of the coherent potential approximation within the context of a KKR Hamiltonian (KKR-CPA-GPM). Agreement with the KKR-CPA-GPM results is quite excellent, as is the comparison of the ground state results with the fcc-based portions of the experimentally-determined phase diagrams under consideration

Phase stability, electronic, elastic and thermodynamic properties of Al-RE intermetallics in Mg-Al-RE alloy: A first principles study

Directory of Open Access Journals (Sweden)

H.L. Chen

2015-09-01

Full Text Available Electronic structure and elastic properties of Al2Y, Al3Y, Al2Gd and Al3Gd phases were investigated by means of first-principles calculations from CASTEP program based on density functional theory (DFT. The ground state energy and elastic constants of each phase were calculated, the formation enthalpy (ΔH, bulk modulus (B, shear modulus (G, Young's modulus (E, Poisson's ratio (ν and anisotropic coefficient (A were derived. The formation enthalpy shows that Al2RE is more stable than Al3RE, and Al-Y intermetallics have stronger phase stability than Al-Gd intermetallics. The calculated mechanical properties indicate that all these four intermetallics are strong and hard brittle phases, it may lead to the similar performance when deforming due to their similar elastic constants. The total and partial electron density of states (DOS, Mulliken population and metallicity were calculated to analyze the electron structure and bonding characteristics of the phases. Finally, phonon calculation was conducted, and the thermodynamic properties were obtained and further discussed.

Synthesis and Characterization of Nanocrystalline Ni50Al50-xMox (X=0-5 Intermetallic Compound During Mechanical Alloying Process

Directory of Open Access Journals (Sweden)

A. Khajesarvi

2015-07-01

Full Text Available In the present study, nanocrystalline Ni50Al50-xMox (X = 0, 0.5, 1, 2.5, 5 intermetallic compound was produced through mechanical alloying of nickel, aluminum, and molybdenum powders. AlNi compounds with good and attractive properties such as high melting point, high strength to weight ratio and high corrosion resistance especially at high temperatures have attracted the attention of many researchers. Powders produced from milling were analyzed using scanning electron microscopy (SEM and X-ray diffractometry (XRD. The results showed that intermetallic compound of NiAl formed at different stage of milling operation. It was concluded that at first disordered solid solution of (Ni,Al was formed then it converted into ordered intermetallic compound of NiAl. With increasing the atomic percent of molybdenum, average grain size decreased from 3 to 0.5 μm. Parameter lattice and lattice strain increased with increasing the atomic percent of molybdenum, while the crystal structure became finer up to 10 nm. Also, maximum microhardness was obtained for NiAl49Mo1 alloy.

Characterization of intermetallic compounds in Cu-Al ball bonds: layer growth, mechanical properties and oxidation

NARCIS (Netherlands)

Kouters, M.H.M.; Gubbels, G.H.M.; O'Halloran, O.; Rongen, R.

2011-01-01

In high power automotive electronics copper wire bonding is regarded as most promising alternative for gold wire bonding in 1 st level interconnects and therefore subjected to severe functional requirements. In the Cu-Al ball bond interface the growth of intermetallic compounds may deteriorate the

Two stages of Kondo effect and competition between RKKY and Kondo in Gd-based intermetallic compound

Energy Technology Data Exchange (ETDEWEB)

Vaezzadeh, Mehdi [Department of Physics, K.N.Toosi University of Technology, P.O. Box 15875-4416, Tehran (Iran, Islamic Republic of)]. E-mail: mehdi@kntu.ac.ir; Yazdani, Ahmad [Tarbiat Modares University, P.O. Box 14155-4838, Tehran (Iran, Islamic Republic of); Vaezzadeh, Majid [Department of Physics, K.N.Toosi University of Technology, P.O. Box 15875-4416, Tehran (Iran, Islamic Republic of); Daneshmand, Gissoo [Department of Physics, K.N.Toosi University of Technology, P.O. Box 15875-4416, Tehran (Iran, Islamic Republic of); Kanzeghi, Ali [Department of Physics, K.N.Toosi University of Technology, P.O. Box 15875-4416, Tehran (Iran, Islamic Republic of)

2006-05-01

The magnetic behavior of Gd-based intermetallic compound (Gd{sub 2}Al{sub (1-x)}Au{sub x}) in the form of the powder and needle, is investigated. All the samples are an orthorhombic crystal structure. Only the compound with x=0.4 shows the Kondo effect (other compounds have a normal behavior). Although, for the compound in the form of powder, with x=0.4, the susceptibility measurement {chi}(T) shows two different stages. Moreover for (T>T{sub K2}) a fall of the value of {chi}(T) is observable, which indicates a weak presence of ferromagnetic phase. About the two stages of Kondo effect, we observe at the first (T{sub K1}) an increase of {chi}(T) and in the second stage (T{sub K2}) a new remarkable decrease of {chi}(T) (T{sub K1}>T{sub K2}). For the sample in the form of needles, the first stage is observable only under high magnetic field. This first stage could be corresponds to a narrow resonance between Kondo cloud and itinerant electron. The second stage, which is remarkably visible for the sample in the form of the powder, can be attribute to a complete polarization of Kondo cloud. Observation of these two Kondo stages could be due to the weak presence of RKKY contribution.

Ni.sub.3 Al-based intermetallic alloys having improved strength above 850.degree. C.

Science.gov (United States)

Liu, Chain T.

2000-01-01

Intermetallic alloys composed essentially of: 15.5% to 17.0% Al, 3.5% to 5.5% Mo, 4% to 8% Cr, 0.04% to 0.2% Zr, 0.04% to 1.5% B, balance Ni, are characterized by melting points above 1200.degree. C. and superior strengths at temperatures above 1000.degree. C.

Spontaneous growth of whiskers on RE-bearing intermetallic compounds of Sn-RE, In-RE, and Pb-RE

Energy Technology Data Exchange (ETDEWEB)

Liu Meng [Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Science, 72 Wenhua Road, Shenyang 110016 (China); Xian Aiping, E-mail: ap.xian@imr.ac.c [Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Science, 72 Wenhua Road, Shenyang 110016 (China)

2009-11-03

A phenomenon of the whiskers growth on the bulk rare earth (RE)-intermetallic compounds of NdSn{sub 3}, NdIn{sub 3}, and LaPb{sub 3} is reported. The whiskers formed spontaneously on all of the RE-intermetallic compounds after exposed to room ambience (21-28 deg. C/20-56% RH, relative humidity) for several days. Among the samples, the propensity of whisker growth for NdSn{sub 3} is the strongest, on which the tin whiskers were flourishing and covered all of the surfaces after exposed to room ambience for 22 days; while LaPb{sub 3} is the secondary and NdIn{sub 3} is the last one. Observed by SEM, the whiskers were exhibited as different morphology, size, and number density. The XRD analysis confirms the existence of RE(OH){sub 3} after whiskers formed, also, the weight gain curve of the samples exposed to room ambience supports that a spontaneous chemical reaction of the RE-intermetallic compounds with water in room ambience takes place. In discussion, it is proposed that the fresh metal atoms released by the chemical reaction could be causative to result in nucleation and spontaneous growth of the whiskers, while the anisotropy of crystal structure could be a reason to understand the difference of the whisker growth behaviors between Sn and Pb.

Effect of grain refiner on intermetallic phase formation in directional solidification of 6xxx series wrought Al alloys

Energy Technology Data Exchange (ETDEWEB)

Sha, G.; O' Reilly, K.; Cantor, B. [Oxford Univ. (United Kingdom). Centre for Adv. Mat. and Composites; Hamerton, R.; Worth, J.

2000-07-01

The effect of a grain refiner on the formation of intermetallic phases in a directionally solidified (Bridgman grown) model 6xxx series wrought Al alloy has been investigated using X-ray diffractometry (XRD), transmission electron microscopy (TEM) and differential scanning calorimetry (DSC). A base alloy with and without Al-Ti-B grain refiner was directionally solidified in a Bridgman furnace at growth velocities in the range of 5-120 mm/min. In both cases, the Fe-containing intermetallic phases present were found to be mainly {alpha}-AlFeSi and {beta}-AlFeSi. However, in the alloy with grain refiner solidified at 5mm/min, Al{sub 13}Fe{sub 4} was also observed. Quantitative XRD results indicated that the addition of Al-Ti-B grain refiner has a strong influence on the relative quantities of intermetallic phases forming during solidification at different growth velocities, which was also confirmed by TEM observations. TEM observations also show that depending on where the {beta}-AlFeSi particles solidified e.g. grain boundaries or triple grain junctions, the size and morphology of the particles may change dramatically. TiB{sub 2} particles were observed to nucleate {beta}-AlFeSi at low and high growth velocities in the 6xxx series Al alloys. (orig.)

Mechanical alloying of TiFe intermetallic for hydrogen storage

International Nuclear Information System (INIS)

Vega, L.E.R.; Leiva, D.R.; Silva, W.B.; Ishikawa, T.T.; Botta, W.J.; Leal Neto, R.M.

2016-01-01

Elementary powders of Ti and Fe in the stoichiometric ratio 50:50 were submitted to mechanical alloying for 2, 6, 10 and 20 h in a planetary ball mill. The synthesis of TiFe intermetallic with high yield was achieved for all milling times. The structural characterization of the samples revealed the trend of the particles to form agglomerates and the formation of cracks. H-absorption capacities of 0,74; 0,90; 0,97 and 0,95 wt. % (at room temperature and 20 bar of H2) were obtained for processing times of 2, 6, 10 and 20 h, respectively, without using a thermal activation process after milling. (author)

Shaping optimal zinc coating on the surface of high-quality ductile iron casting. Part II – Technological formula and value of diffusion coefficient

Directory of Open Access Journals (Sweden)

Kopyciński D.

2017-03-01

Full Text Available The completed research presented in the first part of the article has allowed linking the manufacturing technology of ductile iron castings with the process of hot dip galvanizing. On the basis of these data simulations were carried out to examine the behaviour of zinc diffusion coefficient D in the galvanized coating. The adopted model of zinc coating growth helped to explain the cases of excessive growth of the intermetallic phases in this type of coating. The paper analyzes covered the relationship between the roughness and phase composition of the top layer of product and the thickness and kinetics of zinc coating growth referred to individual sub-layers of the intermetallic phases.Roughness and phase composition in the surface layer of product were next related to the diffusion coefficient D examined in respective sublayers of the intermetallic phases.

Nucleation and growth of intermetallic precipitates in Zircaloy-2 and zircaloy-4 and correlation to nodular corrosion behavior

International Nuclear Information System (INIS)

Maussner, G.; Steinberg, E.; Tenckhoff, E.

1987-01-01

One of the fundamental aspects in the history of the development of zirconium alloys for nuclear applications is the corrosion behavior under in-pile conditions. In boiling-water reactors (BWRs) and pressurized-water reactors (PWRs) the zirconium alloys Zircaloy-2 and Zircaloy-4 are the most commonly used materials, permitting attainment of a very high level of integrity and reliability. Nevertheless, efforts are required to optimize these well-established alloys with regard to their resistance to nodular corrosion, where improvements will give long-term advantages in fuel integrity and fuel economy. Phenomenological studies allow correlation of the nodular corrosion behavior with the morphological appearance of precipitated intermetallic phases in the microstructures of Zry-2 and Zry-4. To understand the fundamental processes of precipitation, particle nucleation-and-growth studies were made with Zry-2 and Zry-4 in different fabrication dimensions and with variations in β-quenching rates followed by isothermal and isochronical heat treatments. The microstructural characteristics of the precipitates were investigated by optical and transmission-electron microscopy. The macroscopic behavior was studied by electrical-resistivity measurements and hardness measurements. The nodular-corrosion susceptibility was determined by weight-gain and nodule distribution measurements after a 500 0 C laboratory-autoclave test

FIB-SEM investigation of trapped intermetallic particles in anodic oxide films on AA1050 aluminium

DEFF Research Database (Denmark)

Jariyaboon, Manthana; Møller, Per; Dunin-Borkowski, Rafal E.

2011-01-01

-containing intermetallic particles incorporated into the anodic oxide films on industrially pure aluminium (AA1050, 99.5 per cent) has been investigated. AA1050 aluminium was anodized in a 100?ml/l sulphuric acid bath with an applied voltage of 14?V at 20°C ±2°C for 10 or 120?min. The anodic film subsequently was analyzed......Purpose - The purpose of this investigation is to understand the structure of trapped intermetallics particles and localized composition changes in the anodized anodic oxide film on AA1050 aluminium substrates. Design/methodology/approach - The morphology and composition of Fe......-shaped particles were embedded in the anodic oxide film as a thin strip structure and located near the top surface of the film, whereas the round-shaped particles were trapped in the film with a spherical structure, but partially dissolved and were located throughout the thickness of the anodic film. The Fe...

A theoretical search for intermetallic compounds and solution phases in the binary system Sn/Zn

Energy Technology Data Exchange (ETDEWEB)

Appen, Joerg von; Dronskowski, Richard; Hack, Klaus

2004-10-06

The binary system Sn/Zn was theoretically investigated by a classical thermodynamic analysis (CALPHAD approach) and by density-functional total-energy calculations on the basis of the LDA/GGA, plane waves/muffin-tin orbitals, and supercell geometries. In harmony with experimental data, both methods agree in that there is only very small solubility between the elements and no formation of a stable intermetallic phase over the entire compositional range. For the hypothetical composition Sn{sub 2}Zn, a total of 30 different crystal structures was quantum-mechanically optimized, and the chemical bondings of Sn{sub 2}Zn adopting the CaF{sub 2} and HgBr{sub 2} structures were analyzed in detail; generally, the more ionic structure types are better suited for the Sn{sub 2}Zn composition than typical intermetallic ones. Theoretical enthalphy-pressure diagrams were generated to explore high-pressure compound formation, and the observed transition pressures between the {alpha}, {beta} and {gamma} allotropes of tin were correctly reproduced by electronic structure theory.

Effect of intermetallic precipitation on the properties of multi passed duplex stainless steel weldment

Energy Technology Data Exchange (ETDEWEB)

Bae, Seong Han [Technology research institute, Ulsan (Korea, Republic of); Lee, Hae Woo [Dong-A University, Busan (Korea, Republic of)

2014-01-15

This study investigated the effect of the aging time of weldment of 24Cr-3.5Mo duplex stainless steel on the microstructure and corrosion behavior. After performing FCAW, we carried out heat treatments at varying times at 850 ℃ and performed observation of microstructure, potentio dynamic test, SEM-EDS analysis, and X-ray diffraction analysis. As the aging time increased, the fraction of δ-ferrite decreased sharply, but the fraction of γ slightly increased. The σ phase was generated at a non-metallic inclusion along the grain boundaries of δ-ferrite and γ, while the χ phase was generated in the structure of δ-ferrite. As the intermetallic compounds increased, the critical pitting potential fell sharply, and PREN of the surrounding structure decreased by 5 due to precipitation of the σ phase in 3.5% NaCl at 60 ℃. Pitting occurred intensively under a multi-pass line which relatively had more intermetallic compounds, and the precipitation of the σ phase caused the formation of Cr carbide.

Effect of intermetallic precipitation on the properties of multi passed duplex stainless steel weldment

International Nuclear Information System (INIS)

Bae, Seong Han; Lee, Hae Woo

2014-01-01

This study investigated the effect of the aging time of weldment of 24Cr-3.5Mo duplex stainless steel on the microstructure and corrosion behavior. After performing FCAW, we carried out heat treatments at varying times at 850 ℃ and performed observation of microstructure, potentio dynamic test, SEM-EDS analysis, and X-ray diffraction analysis. As the aging time increased, the fraction of δ-ferrite decreased sharply, but the fraction of γ slightly increased. The σ phase was generated at a non-metallic inclusion along the grain boundaries of δ-ferrite and γ, while the χ phase was generated in the structure of δ-ferrite. As the intermetallic compounds increased, the critical pitting potential fell sharply, and PREN of the surrounding structure decreased by 5 due to precipitation of the σ phase in 3.5% NaCl at 60 ℃. Pitting occurred intensively under a multi-pass line which relatively had more intermetallic compounds, and the precipitation of the σ phase caused the formation of Cr carbide.

Control of interfacial intermetallic compounds in Fe–Al joining by Zn addition

Energy Technology Data Exchange (ETDEWEB)

Yang, J. [Key Laboratory of Robot and Welding Automation of Jiangxi Province, School of Mechanical and Electrical Engineering, Nanchang University, Nanchang, Jiangxi 330031 (China); Center for Advanced Materials Joining, University of Waterloo, Waterloo, Ontario, Canada N2L 3G1 (Canada); Li, Y.L., E-mail: liyulong1112ster@gmail.com [Key Laboratory of Robot and Welding Automation of Jiangxi Province, School of Mechanical and Electrical Engineering, Nanchang University, Nanchang, Jiangxi 330031 (China); Zhang, H. [Key Laboratory of Robot and Welding Automation of Jiangxi Province, School of Mechanical and Electrical Engineering, Nanchang University, Nanchang, Jiangxi 330031 (China); Guo, W. [Center for Advanced Materials Joining, University of Waterloo, Waterloo, Ontario, Canada N2L 3G1 (Canada); School of Mechanical Engineering and Automation, Beijing University of Aeronautics and Astronautics, Beijing 100191 (China); Zhou, Y. [Center for Advanced Materials Joining, University of Waterloo, Waterloo, Ontario, Canada N2L 3G1 (Canada)

2015-10-01

By Zn addition to the fusion zone, the interfacial intermetallic compounds (IMCs) of laser Al/steel joint changed from layered Fe{sub 2}Al{sub 5} and needle-like FeAl{sub 3} to layered Fe{sub 2}Al{sub 5−x}Zn{sub x} and dispersed FeZn{sub 10} with minor Al-rich amorphous phase. This resulted in an improvement in the joint strength and the change of failure mode.

< c >-component plastic displacements in different microstructures of TiAl-base intermetallics

Czech Academy of Sciences Publication Activity Database

Orlová, Alena; Kuchařová, Květa; Dlouhý, Antonín

2008-01-01

Roč. 483, Sp.Iss.SI (2008), s. 109-112 ISSN 0921-5093. [International Conference on the Strength of Materials /14./. Xian, 04.06.2006-09.06.2006] R&D Projects: GA AV ČR(CZ) 1QS200410502; GA MŠk OC 522.100 Institutional research plan: CEZ:AV0Z20410507 Keywords : intermetallics * creep * transmission electron microscopy * titanium aluminides Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.806, year: 2008

Study of the structure and development of the set of reference materials of composition and structure of heat resisting nickel and intermetallic alloys

Directory of Open Access Journals (Sweden)

E. B. Chabina

2016-01-01

Full Text Available Relevance of research: There are two sizes (several microns and nanodimensional of strengthening j'-phase in single-crystal heat resisting nickel and intermetallic alloys, used for making blades of modern gas turbine engines (GTD. For in-depth study of structural and phase condition of such alloys not only qualitative description of created structure is necessary, but quantitative analysis of alloy components geometrical characteristics. Purpose of the work: Development of reference material sets of heat resisting nickel and intermetallic alloy composition and structure. Research methods: To address the measurement problem of control of structural and geometrical characteristics of single-crystal heat resisting and intermetallic alloys by analytical microscopy and X-ray diffraction analysis the research was carried out using certified measurement techniques on facilities, entered in the Register of Measurement Means of the Russian Federation. The research was carried out on microsections, foils and plates, cut in the plane {100}. Results: It is established that key parameters, defining the properties of these alloys are particle size of strengthening j' -phase, the layer thickness of j-phase between them and parameters of phases lattice. Metrological requirements for reference materials of composition and structure of heat resisting nickel and intermetallic alloys are formulated. The necessary and sufficient reference material set providing the possibility to determine the composition and structure parameters of single-crystal heat resisting nickel and intermetallic alloys is defined. The developed RM sets are certified as in-plant reference materials. Conclusion: The reference materials can be used for graduation of spectral equipment when conducting element analysis of specified class alloys; for calibration of means of measuring alloy structure parameters; for measurement of alloys phases lattice parameters; for structure reference pictures

Hot Corrosion Behavior of Ti-48Al and Ti-48Al-2Cr Intermetallic Alloys Produced by Electric Current Activated Sintering

Science.gov (United States)

Garip, Y.; Ozdemir, O.

2018-06-01

In this study, Ti-48Al and Ti-48Al-2Cr (at. pct) intermetallic alloys were produced by electric current activated sintering (ECAS). In order to characterize the phase formation and microstructures of these alloys, scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), and X-ray diffraction (XRD) analysis were used. The XRD result shows that the intermetallic alloys are composed of γ-TiAl and α 2-Ti3Al phases. The microstructure is dense with a low amount of porosity. The hot corrosion behavior of intermetallic alloys was carried out in a salt mixture of 25 wt pct K2SO4 and 75 wt pct Na2SO4 at 700 °C for 180 hours. The morphology of corroded surfaces was observed by SEM-EDS and XRD. Corrosion phases were identified as TiO2 and Al2O3. Well-adhering oxide scale was detected on the corroded sample surface at the end of 180 hours, and no spallation was observed. In addition, a parabolic curve was obtained at the weight change rate vs time.

Hot Corrosion Behavior of Ti-48Al and Ti-48Al-2Cr Intermetallic Alloys Produced by Electric Current Activated Sintering

Science.gov (United States)

Garip, Y.; Ozdemir, O.

2018-03-01

In this study, Ti-48Al and Ti-48Al-2Cr (at. pct) intermetallic alloys were produced by electric current activated sintering (ECAS). In order to characterize the phase formation and microstructures of these alloys, scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), and X-ray diffraction (XRD) analysis were used. The XRD result shows that the intermetallic alloys are composed of γ-TiAl and α 2-Ti3Al phases. The microstructure is dense with a low amount of porosity. The hot corrosion behavior of intermetallic alloys was carried out in a salt mixture of 25 wt pct K2SO4 and 75 wt pct Na2SO4 at 700 °C for 180 hours. The morphology of corroded surfaces was observed by SEM-EDS and XRD. Corrosion phases were identified as TiO2 and Al2O3. Well-adhering oxide scale was detected on the corroded sample surface at the end of 180 hours, and no spallation was observed. In addition, a parabolic curve was obtained at the weight change rate vs time.

Microstructure and high-temperature oxidation resistance of TiN/Ti3Al intermetallic matrix composite coatings on Ti6Al4V alloy surface by laser cladding

Science.gov (United States)

Zhang, Xiaowei; Liu, Hongxi; Wang, Chuanqi; Zeng, Weihua; Jiang, Yehua

2010-11-01

A high-temperature oxidation resistant TiN embedded in Ti3Al intermetallic matrix composite coating was fabricated on titanium alloy Ti6Al4V surface by 6kW transverse-flow CO2 laser apparatus. The composition, morphology and microstructure of the laser clad TiN/Ti3Al intermetallic matrix composite coating were characterized by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy dispersive spectrometer (EDS). In order to evaluate the high-temperature oxidation resistance of the composite coatings and the titanium alloy substrate, isothermal oxidation test was performed in a conventional high-temperature resistance furnace at 600°C and 800°C respectively. The result shows that the laser clad intermetallic composite coating has a rapidly solidified fine microstructure consisting of TiN primary phase (granular-like, flake-like, and dendrites), and uniformly distributed in the Ti3Al matrix. It indicates that a physical and chemical reaction between the Ti powder and AlN powder occurred completely under the laser irradiation. In addition, the microhardness of the TiN/Ti3Al intermetallic matrix composite coating is 844HV0.2, 3.4 times higher than that of the titanium alloy substrate. The high-temperature oxidation resistance test reveals that TiN/Ti3Al intermetallic matrix composite coating results in the better modification of high-temperature oxidation behavior than the titanium substrate. The excellent high-temperature oxidation resistance of the laser cladding layer is attributed to the formation of the reinforced phase TiN and Al2O3, TiO2 hybrid oxide. Therefore, the laser cladding TiN/Ti3Al intermetallic matrix composite coating is anticipated to be a promising oxidation resistance surface modification technique for Ti6Al4V alloy.

Influence of the ion implantation on the nanoscale intermetallic phases formation in Ni-Ti system

International Nuclear Information System (INIS)

Kalashnikov, M.P.; Kurzina, I.A.; Bozhko, I.A.; Kozlov, E.V.; Fortuna, S.V.; Sivin, D.O.; Stepanov, I.B.; Sharkeev, Yu.P.

2005-01-01

Full text: The ion implantation at a high intensity mode is an effective method for modification of the surface properties of metals and alloys. Improvement of mechanical and tribological properties of irradiated materials using the high intensity implantation is connected with an element composition and microstructure modification of the surface and subsurface layers. One shows a great interest in intermetallic phase's synthesis by ion implantation, because of unique physical-mechanical properties of the intermetallic compounds. The influence of the irradiation conditions on the structural state and surface properties of implanted materials is not clear enough. The study of the factors influencing on the formation of the surface ion - alloyed layers of metal targets having the high tribological and mechanical properties by high intensity ion implantation is actual. The aim of the present work is a study of the microstructure, phase composition, physical and mechanical properties of the ion-alloyed Ni surfaces formed at high intensity implantation of Ti ions. The implantation Ti ions into Ni samples at high intensity mode was realized using ion source 'Raduga - 5'. The implantation Ti ions into Ni was carried out at accelerating voltage 20 kV for 2 h. The regimes were differed in the samples temperature (580 - 700 K), the distance from the ion implanted samples to the ion source (0.43-0.93 m) and the dose of irradiated ions (0.3·10 18 -2.9·10 18 ion/cm -2 ). The element composition of the implanted samples was analyzed by the electron spectroscopy. The structural-phase state of the Ni ion-modified layers was investigated by the transmission electron microscopy and X-ray diffraction methods. Additionally, the investigation of mechanical and tribological properties of the implanted Ni samples was carried out. It was established that the maximum thickness of the ion-alloyed nickel layers at high intensity mode allows forming the nanoscale intermetallic phases (Ni

Chemical Frustration. A Design Principle for the Discovery of New Complex Alloy and Intermetallic Phases, Final Report

Energy Technology Data Exchange (ETDEWEB)

Fredrickson, Daniel C [Univ. of Wisconsin, Madison, WI (United States)

2015-06-23

Final technical report for "Chemical Frustration: A Design Principle for the Discovery of New Complex Alloy and Intermetallic Phases" funded by the Office of Science through the Materials Chemistry Program of the Office of Basic Energy Sciences.

Preliminary soil-slip susceptibility maps, southwestern California

Science.gov (United States)

Morton, Douglas M.; Alvarez, Rachel M.; Campbell, Russell H.; Digital preparation by Bovard, Kelly R.; Brown, D.T.; Corriea, K.M.; Lesser, J.N.

2003-01-01

This group of maps shows relative susceptibility of hill slopes to the initiation sites of rainfall-triggered soil slip-debris flows in southwestern California. As such, the maps offer a partial answer to one part of the three parts necessary to predict the soil-slip/debris-flow process. A complete prediction of the process would include assessments of “where”, “when”, and “how big”. These maps empirically show part of the “where” of prediction (i.e., relative susceptibility to sites of initiation of the soil slips) but do not attempt to show the extent of run out of the resultant debris flows. Some information pertinent to “when” the process might begin is developed. “When” is determined mostly by dynamic factors such as rainfall rate and duration, for which local variations are not amenable to long-term prediction. “When” information is not provided on the maps but is described later in this narrative. The prediction of “how big” is addressed indirectly by restricting the maps to a single type of landslide process—soil slip-debris flows. The susceptibility maps were created through an iterative process from two kinds of information. First, locations of sites of past soil slips were obtained from inventory maps of past events. Aerial photographs, taken during six rainy seasons that produced abundant soil slips, were used as the basis for soil slip-debris flow inventory. Second, digital elevation models (DEM) of the areas that were inventoried were used to analyze the spatial characteristics of soil slip locations. These data were supplemented by observations made on the ground. Certain physical attributes of the locations of the soil-slip debris flows were found to be important and others were not. The most important attribute was the mapped bedrock formation at the site of initiation of the soil slip. However, because the soil slips occur in surficial materials overlying the bedrocks units, the bedrock formation can only serve as

Characterization of intermetallic compounds in Cu-Al ball bonds: thermo-mechanical properties, interface delamination and corrosion

NARCIS (Netherlands)

Gubbels, G.H.M.; Kouters, M.H.M.; Dos Santos Ferreira, O.

2012-01-01

In high power automotive electronics copper wire bonding is regarded as the most promising alternative for gold wire bonding in 1st level interconnects. In the Cu-Al ball bond interface the growth of intermetallic compounds can deteriorate the electrical and mechanical properties of the

Effect of Flux onto Intermetallic Compound Formation and Growth

Directory of Open Access Journals (Sweden)

Idris Siti Rabiatull Aisha

2016-01-01

Full Text Available In this study, the effect of different composition of no-clean flux onto intermetallic compound (IMC formation and growth was investigated. The solder joint between Sn-3Ag-0.5Cu solder alloy and printed circuit board (PCB was made through reflow soldering. They were further aged at 125°C and 150°C for up to 1000 hours. Results showed that fluxes significantly affect the IMC thickness and growth. In addition, during aging, the scallop and columnar morphology of IMC changed to a more planar type for both type of flux during isothermal aging. It was observed that the growth behavior of IMC was closely related to initial soldering condition.

Interface-related deformation phenomena in intermetallic γ-titanium aluminides

International Nuclear Information System (INIS)

Appel, F.; Wagner, R.

1993-01-01

The development of titanium aluminides towards higher ductility concentrates on Ti-rich alloys which are composed of the intermetallic phases γ(TiAl) and α 2 (Ti 3 Al). The two phases form a lamellar microstructure with various types of interfaces. The deformation behaviour of these materials was investigated by compression tests, which were performed for different orientations of the interfacial boundaries with respect to the sample axis. With regard to the mechanical properties the structure of the interfaces and the micromechanisms of deformation were studied by conventional and high resolution electron microscopy. Accordingly, the interfacial boundaries impede the propagation of slip across the lamellae, leading to an athermal contribution to the flow stress. (orig.)

Interface-related deformation phenomena in intermetallic γ-titanium aluminides

Science.gov (United States)

Appel, F.; Wagner, R.

1993-01-01

The development of titanium aluminides towards higher ductility concentrates on Ti-rich alloys which are composed of the intermetallic phases γ(TiAl) and α2(Ti3Al). The two phases form a lamellar microstructure with various types of interfaces. The deformation behaviour of these materials was investigated by compression tests, which were performed for different orientations of the interfacial boundaries with respect to the sample axis. With regard to the mechanical properties the structure of the interfaces and the micromechanisms of deformation were studied by conventional and high resolution electron microscopy. Accordingly, the interfacial boundaries impede the propagation of slip across the lamellae, leading to an athermal contribution to the flow stress.

Microstructure and electrochemical characterization of laser melt-deposited Ti2Ni3Si/NiTi intermetallic alloys

International Nuclear Information System (INIS)

Dong Lixin; Wang Huaming

2008-01-01

Corrosion and wear resistant Ti 2 Ni 3 Si/NiTi intermetallic alloys with Ti 2 Ni 3 Si as the reinforcing phase and the ductile NiTi as the toughening phase were designed and fabricated by the laser melt-deposition manufacturing process. Electrochemical behavior of the alloys was investigated using potentiodynamic polarization testing and electrochemical impedance spectroscopy in an NaOH solution. The results showed that the alloys have outstanding corrosion resistance due to the formation of a protective passive surface film of Ni(OH) 2 as well as the high chemical stability and strong inter-atomic bonds inherent to Ti 2 Ni 3 Si and NiTi intermetallics. The Ti 2 Ni 3 Si content has a significant influence on the microstructure of the alloys but only a slight effect on electrochemical corrosion properties

Nanoporous alumina formed by self-organized two-step anodization of Ni3Al intermetallic alloy in citric acid

International Nuclear Information System (INIS)

Stępniowski, Wojciech J.; Cieślak, Grzegorz; Norek, Małgorzata; Karczewski, Krzysztof; Michalska-Domańska, Marta; Zasada, Dariusz; Polkowski, Wojciech; Jóźwik, Paweł; Bojar, Zbigniew

2013-01-01

Highlights: ► Anodic porous alumina was formed by Ni 3 Al intermetallic alloy anodization. ► The anodizations were conducted in 0.3 M citric acid. ► Nanopores geometry depends on anodizing voltage. ► No barrier layer was formed during anodization. - Abstract: Formation of the nanoporous alumina on the surface of Ni 3 Al intermetallic alloy has been studied in details and compared with anodization of aluminum. Successful self-organized anodization of this alloy was performed in 0.3 M citric acid at voltages ranging from 2.0 to 12.0 V using a typical two-electrode cell. Current density records revealed different mechanism of the porous oxide growth when compared to the mechanism pertinent for the anodization of aluminum. Electrochemical impedance spectroscopy experiments confirmed the differences in anodic oxide growth. Surface and cross-sections of the Ni 3 Al intermetallic alloy with anodic oxide were observed with field-emission scanning electron microscope and characterized with appropriate software. Nanoporous oxide growth rate was estimated from cross-sectional FE-SEM images. The lowest growth rate of 0.14 μm/h was found for the anodization at 0 °C and 2.0 V. The highest one – 2.29 μm/h – was noticed for 10.0 V and 30 °C. Pore diameter was ranging from 18.9 nm (2.0 V, 0 °C) to 32.0 nm (12.0 V, 0 °C). Interpore distance of the nanoporous alumina was ranging from 56.6 nm (2.0 V, 0 °C) to 177.9 nm (12.0 V, 30 °C). Pore density (number of pore occupying given area) was decreasing with anodizing voltage increase from 394.5 pores/μm 2 (2.0 V, 0 °C) to 94.9 pores/μm 2 (12.0 V, 0 °C). All the geometrical features of the anodic alumina formed by two-step self-organized anodization of Ni 3 Al intermetallic alloy are depending on the operating conditions.

Multifunctional phenomena in rare-earth intermetallic compounds with a laves phase structure: giant magnetostriction and magnetocaloric effect

Czech Academy of Sciences Publication Activity Database

Tereshina, I.; Cwik, J.; Tereshina, Evgeniya; Politova, G.; Burkhanov, G.; Chzhan, V.; Ilyushin, A.; Miller, M.; Zaleski, A.; Nenkov, K.; Schultz, L.

2014-01-01

Roč. 50, č. 11 (2014), s. 2504604 ISSN 0018-9464 Institutional support: RVO:68378271 Keywords : giant magnetostriction * Laves phase structure * magnetic anisotropy * magnetocaloric effect * rare-earth intermetallic Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.386, year: 2014

Characterization of oxidation products on a ZrFe2-type laves intermetallic exposed to 200degreeC steam

International Nuclear Information System (INIS)

Abraham, D. P.; Dietz, N.; Finnegan, N.

2000-01-01

The release of radioactive elements from the stainless steel-15 wt% zirconium (SS-15Zr) metal waste form will be governed by the corrosion behavior of ZrFe 2 -type intermetallics phases present in the alloy. In this article, oxidation products that formed on a ZrFe 2 -type intermetallic sample exposed to 200 C steam were characterized by Auger Electron Spectroscopy (AES) and Transmission Electron Microscopy (TEM). The data revealed two oxide layers on the sample surface: an outer crystalline iron-oxide layer and an inner amorphous zirconium-rich layer believed to be zirconium oxide. Thermodynamic considerations indicate that the zirconium-rich layer formed first. The iron-oxide layer appears to have resulted from the diffusion of iron through the zirconium-rich layer to the oxide-vapor interface

Microwave-assisted combustion synthesis of NiAl intermetallics in a single mode applicator: Modeling and optimisation

International Nuclear Information System (INIS)

Poli, G.; Sola, R.; Veronesi, P.

2006-01-01

The microwave-assisted combustion synthesis of NiAl intermetallics in a single mode applicator has been simulated numerically and performed with the aim of achieving the highest yields, energy efficiency and process reproducibility. The electromagnetic field modeling of the microwave system allowed to chose the proper experimental set-up and the materials more suitable for the application, minimising the reflected power and the risks of arcing. In all the experimental conditions tested, conversions of 3-5 g 1:1 atomic ratio Ni and Al powder compacts into NiAl ranged from 98.7% to 100%, requiring from 30 to 180 s with power from 500 to 1500 W. The optimisation procedure allowed to determine and quantify the effects of the main process variables on the ignition time, the NiAl yields and the specific energy consumption, leading to a fast, reproducible and cost-effective process of microwave-assisted combustion synthesis of NiAl intermetallics

Reaction of intermetallic compounds of the ScT composition (T=Ag, Cu, Zn, Ni) with hydrogen

International Nuclear Information System (INIS)

Shilkin, S.P.; Volkova, L.S.; Tarasov, B.P.

1995-01-01

Reaction of intermetallic compounds of ScT composition (T=Ag, Cu, Zn, Ni), crystallized in CsCl structural type, with hydrogen at 0.2-10 MPa pressure and 293-673 K temperature is studied by chemical, x-ray phase and complex thermogravimetry analysis methods. It is shown that under such conditions hydrogen absorption by ScAg and ScCu is accompanied by the decay of their source matrices into scandium dihydride and metal silver and copper respectively. For ScZn a fine-dispersion mixture of scandium dihydride with zinc and hydride phase of a new zinc-containing intermetallic compound appears to be the finite reaction product. In case of ScNi a hydride phase of ScNiH 2.6 composition is produced, which is crystallized in a rhombic syngony with the lattice periods: a=0.5281±0.0007, b=0.7393±0.0009 and c=0.3327±0.0004 nm. 9 refs.; 2 tabs

Irregular Homogeneity Domains in Ternary Intermetallic Systems

Directory of Open Access Journals (Sweden)

Jean-Marc Joubert

2015-12-01

Full Text Available Ternary intermetallic A–B–C systems sometimes have unexpected behaviors. The present paper examines situations in which there is a tendency to simultaneously form the compounds ABx, ACx and BCx with the same crystal structure. This causes irregular shapes of the phase homogeneity domains and, from a structural point of view, a complete reversal of site occupancies for the B atom when crossing the homogeneity domain. This work reviews previous studies done in the systems Fe–Nb–Zr, Hf–Mo–Re, Hf–Re–W, Mo–Re–Zr, Re–W–Zr, Cr–Mn–Si, Cr–Mo–Re, and Mo–Ni–Re, and involving the topologically close-packed Laves, χ and σ phases. These systems have been studied using ternary isothermal section determination, DFT calculations, site occupancy measurement using joint X-ray, and neutron diffraction Rietveld refinement. Conclusions are drawn concerning this phenomenon. The paper also reports new experimental or calculated data on Co–Cr–Re and Fe–Nb–Zr systems.

Four-branched compounds coupled Si and iron-rich intermetallics in near eutectic Al-Si alloys

International Nuclear Information System (INIS)

Wu, Yuying; Liu, Xiangfa; Jiang, Binggang; Bian, Xiufang

2007-01-01

Many four-branched compounds coupled Si and iron-rich intermetallics were observed in near eutectic Al-Si alloy modified with Al-P master alloy. Such four-branched compounds have never been reported before, but in our case it seems to be commonly observed. In this work the growth characterization of the four-branched compounds are scrutinized with a JXA-8800 electron microprobe (EPMA). More deep study of the formation of four-branched compounds is performed by SEM and TEM analysis. The characterization of the four-branched compounds is that of a primary silicon in the center with four iron-rich intermetallics around. Experimental results also show that the precipitation of primary silicon is the key factor for the formation of four-branched compounds. And WHS-theory explains the growth mechanism of the four-branched compounds. In detail, subsequent twinning within the primary silicon provides four-fold coordination sites on the surface, and then the α-Al(Fe,Mn)-Si phase nucleates on the surface of the primary silicon

Fabrication of FeAl Intermetallic Foams by Tartaric Acid-Assisted Self-Propagating High-Temperature Synthesis

Directory of Open Access Journals (Sweden)

Krzysztof Karczewski

2018-04-01

Full Text Available Iron aluminides are intermetallics with interesting applications in porous form thanks to their mechanical and corrosion resistance properties. However, making porous forms of these materials is not easy due to their high melting points. We formed FeAl foams by elemental iron and aluminum powders sintering with tartaric acid additive. Tartaric acid worked as an in situ gas-releasing agent during the self-propagating high-temperature synthesis of FeAl intermetallic alloy, which was confirmed by X-ray diffraction measurements. The porosity of the formed foams was up to 36 ± 4%. In the core of the sample, the average equivalent circle diameter was found to be 47 ± 20 µm, while on the surface, it was 35 ± 16 µm; thus, the spread of the pore size was smaller than reported previously. To investigate functional applications of the formed FeAl foam, the pressure drop of air during penetration of the foam was examined. It was found that increased porosity of the material increased the flow of the air through the metallic foam.

States and properties of metallic systems at a threshold breakdown of the through holes under power laser action (part 2. Susceptibility

Directory of Open Access Journals (Sweden)

Kalashnikov E.

2016-01-01

Full Text Available Threshold breakdown of the through holes by power laser radiation of metallic foils is considered as response of metallic system to laser radiation. Binding experimentally determined response to the absolute temperature scale allows to determine the value of the imaginary part of the generalized susceptibility depending on temperature, the critical temperature of the transition “liquid metal - gas”, states of the electronic subsystems at this temperature, and the reflectance coefficient values.

Iron Intermetallic Phases in the Alloy Based on Al-Si-Mg by Applying Manganese

Directory of Open Access Journals (Sweden)

Podprocká R.

2017-09-01

Full Text Available Manganese is an effective element used for the modification of needle intermetallic phases in Al-Si alloy. These particles seriously degrade mechanical characteristics of the alloy and promote the formation of porosity. By adding manganese the particles are being excluded in more compact shape of “Chinese script” or skeletal form, which are less initiative to cracks as Al5FeSi phase. In the present article, AlSi7Mg0.3 aluminium foundry alloy with several manganese content were studied. The alloy was controlled pollution for achieve higher iron content (about 0.7 wt. % Fe. The manganese were added in amount of 0.2 wt. %, 0.6 wt. %, 1.0 wt. % and 1.4 wt. %. The influence of the alloying element on the process of crystallization of intermetallic phases were compared to microstructural observations. The results indicate that increasing manganese content (> 0.2 wt. % Mn lead to increase the temperature of solidification iron rich phase (TAl5FeSi and reduction this particles. The temperature of nucleation Al-Si eutectic increase with higher manganese content also. At adding 1.4 wt. % Mn grain refinement and skeleton particles were observed.

Study and development of NiAl intermetallic coating on hypo-eutectoid steel using highly activated composite granules of the Ni-Al system

Energy Technology Data Exchange (ETDEWEB)

Shahzad, Aamir; Zadorozhnyy, Vladislav Yu.; Pavlov, Mikhail D.; Semenov, Dmitri V.; Kaloshkin, Sergey D. [National Univ. of Science and Technology (MISIS), Moscow (Russian Federation)

2018-01-15

NiAl intermetallic coating thickness of about 50 μm was fabricated on hypo-eutectoid steel by mechanical alloying using pre-activated Ni-Al composite granules as coating material. First, Ni and Al powders were mixed with the composition of Ni-50 at.% Al and mechanically activated in a planetary ball mill, until the composite granules of this powder mixture, having maximum activity (9 cm sec{sup -1}), were formed after 120 min of milling at 200 rpm. The composite granules were then taken out from the planetary ball mill just before the critical time, i. e. the time at which these granules synthesize and convert to an intermetallic NiAl compound. The highly activated composite granules of Ni-Al were then put into the vial of a vibratory ball mill with the substrate on top of the chamber. After mechanical alloying for 60 min in the vibratory ball mill, the composite granules were synthesized fully and heat was produced during the synthesis which helped producing a thick and strong adhesive coating of NiAl intermetallic on the steel substrate. The main advantage of this technique is that not only is time saved but also there is no need for any post mechanical alloying process such as annealing or laser treatment etc. to get homogeneous, strongly bonded intermetallic coatings. X-ray diffraction analysis clearly indicates the formation of NiAl phase. Micro-hardness of the coating and substrate was also measured. The cross-sectional microstructure of the composite granules and the final coating were studied by scanning electron microscopy.

Investigations of intermetallic alloy hydriding mechanisms. Annual progress report, May 1 1979-April 30, 1980

International Nuclear Information System (INIS)

Livesay, B.R.; Larsen, J.W.

1980-05-01

Investigations are being conducted on mechanisms involved with the hydrogen-metal interactions which control the absorption and desorption processes in intermetallic compounds. The status of the following investigations is reported: modeling of hydride formation; microbalance investigations; microstructure investigations; flexure experiments; resistivity experiments; and nuclear backscattering measurements. These investigations concern fundamental hydrogen interaction mechanisms involved in storage alloys

Insecticide susceptibility status and major detoxifying enzymes' activity in Aedes albopictus (Skuse), vector of dengue and chikungunya in Northern part of West Bengal, India.

Science.gov (United States)

Bharati, Minu; Saha, Dhiraj

2017-06-01

Mosquitoes belonging to Aedes genus, Aedes aegypti and Aedes albopictus transmit many globally important arboviruses including Dengue (DENV) and Chikungunya (CHIKV). Vector control with the use of insecticide remains the suitable method of choice to stop the transmission of these diseases. However, vector control throughout the world is failing to achieve its target results because of the worldwide development of insecticide resistance in mosquitoes. To assess the insecticide susceptibility status of Aedes albopictus from northern part of West Bengal, the susceptibility of eight different Aedes albopictus populations were tested against a commonly used larvicide (temephos) and some adulticides (malathion, deltamethrin and lambda cyhalothrin) along with the major insecticide detoxifying enzymes' activity in them. Through this study, it was revealed that most of the populations were found susceptible to temephos except Nagrakata (NGK) and Siliguri (SLG), which showed both a higher resistance ratio (RR 99 ) and a lower susceptibility, thereby reflecting the development of resistance against temephos in them. However, all tested adulticides caused 100% mortality in all the population implying their potency in control of this mosquito in this region of India. Through the study of carboxylesterase activity, it was revealed that the NGK population showed a 9.6 fold higher level of activity than susceptible population. The same population also showed a lower level of susceptibility and a higher resistance ratio (RR 99 ), indicating a clear correlation between susceptibility to temephos and carboxylesterase enzymes' activity in this population. This preliminary data reflects that the NGK population is showing a trend towards resistance development and with time, there is possibility that this resistance phenomenon will spread to other populations. With the recurrence of dengue and chikungunya, this data on insecticide susceptibility status of Aedes albopictus could help the

Magnetic-field induced phase transitions in intermetallic rare-earth ferrimagnets with a compensation point

Czech Academy of Sciences Publication Activity Database

Sabdenov, Ch.K.; Davydova, M.D.; Zvezdin, K.A.; Gorbunov, Denis; Tereshina, I. S.; Andreev, Alexander V.; Zvezdin, A. K.

2017-01-01

Roč. 43, č. 5 (2017), s. 551-558 ISSN 1063-777X R&D Projects: GA ČR GA16-03593S Institutional support: RVO:68378271 Keywords : rare-earth intermetallics * phase diagram * field-induced transition * magnetic anisotropy * high magnetic fields Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 0.804, year: 2016

The Role of Second Phase Intermetallic Particles on the Spall Failure of 5083 Aluminum

Science.gov (United States)

2016-12-01

Bradley Survice Engineering Company, Aberdeen, MD A reprint from Journal of Dynamic Behavior of Materials. 2016;2:476–483...Army Research Laboratory, Aberdeen Proving Ground, Aberdeen, MD, USA 2 Survice Engineering Company, Aberdeen Proving Ground, Aberdeen, MD, USA 123 J...2016) 2:476–483 479 123 ligaments between cracks and a second phase intermetallic particle (identified by black arrow) above the crack with an average

Development of New Cryocooler Regenerator Materials-Ductile Intermetallic Compounds

International Nuclear Information System (INIS)

Gschneidner, K.A.; Pecharsky, A.O.; Pecharsky, V.K.

2004-01-01

The volumetric heat capacities of a number of binary and ternary Er- and Tm-based intermetallic compounds, which exhibited substantial ductilities, were measured from ∼3 to ∼350 K. They have the RM stoichiometry (where R = Er or Tm, and M is a main group or transition metal) and crystallize in the CsCl-type structure. The heat capacities of the Tm-based compounds are in general larger than the corresponding Er-based materials. Many of them have heat capacities which are significantly larger than those of the low temperature ( 2 , Er 3 Ni and ErNi. Utilization of the new materials as regenerators in the various cryocoolers should improve the performance of these refrigeration units for cooling below 15 K

Microstructural evolution of Ni40Zr60 alloy during early stage of mechanical alloying of intermetallic compounds NiZr2 and Ni11Zr9

International Nuclear Information System (INIS)

Lee Peeyew; Koch, C.C.

1994-01-01

The microstructural change of Ni 40 Zr 60 alloy during mechanical alloying of mixtures of the intermetallic compounds NiZr 2 and Ni 11 Zr 9 has been studied by transmission electron microscopy. A specific ''cauliflower'' phase was formed during early stage of mechanical alloying process. It is suggested that the solid state reaction between intermetallic compounds NiZr 2 and Ni 11 Zr 9 is not the only origin for the formation of the ''cauliflower'' phase. ((orig.))

Vacuum brazing of TiAl48Cr2Nb2 casting alloys based on TiAl (γ intermetallic compound

Directory of Open Access Journals (Sweden)

Z. Mirski

2010-01-01

Full Text Available A growing interest in modern engineering materials characterised by increasingly better operational parameters combined with a necessity to obtain joints of such materials representing good operation properties create important research and technological problems of today. These issues include also titanium joints or joints of titanium alloys based on intermetallic compounds. Brazing is one of the basic and sometimes even the only available welding method used for joining the aforesaid materials in production of various systems, heat exchangers and, in case of titanium alloys based on intermetallic compounds, turbine elements and space shuttle plating etc. This article presents the basic physical and chemical properties as well as the brazability of alloys based on intermetallic compounds. The work also describes the principle and mechanisms of diffusion-brazed joint formation as well as reveals the results of metallographic and strength tests involving diffusion-welded joints of TiAl48Cr3Nb2 casting alloy based on TiAl (γ phase with the use of sandwich-type layers of silver-based parent metal (grade B- Ag72Cu-780 (AG 401 and copper (grade CF032A. Structural examination was performed by means of light microscopy, scanning electron microscope (SEM and energy dispersion spectrometer (EDS. Furthermore, the article reveals the results of shear strength tests involving the aforementioned joints.

antimicrobial susceptibility pattern of Salmonella species

African Journals Online (AJOL)

user

GLOBAL JOURNAL OF COMMUNITY MEDICINE VOL. 2 NO. 1 & 2 2009: 5 - ... This study is a review of the contemporary antimicrobial susceptibility pattern of. Salmonella species. ... south-east Asia, parts of Latin America, the. Caribbean, and ...

The intermetallic bonding between a ring carrier and aluminum piston alloy

Directory of Open Access Journals (Sweden)

Manasijevic, Srećko

2015-09-01

Full Text Available This paper presents the results of investigating the formation of intermetallic bond between a ring carrier and aluminum piston alloy. The ring carrier is made of austenitic cast iron (Ni-Resist in order to increase the wear resistance of the first ring groove and applied in highly loaded diesel engines. Metallographic examination of the quality of alfin bond was done. A metallographic investigation using an optical microscope in combination with the SEM/EDS analysis of the quality of the intermetallic bonding layer was done. The test results show that can be made successfully as well as the formation of metal connection (alfin bond between the ring carrier and aluminum piston alloy.El artículo presenta los resultados de la investigación sobre la formación de una unión intermetálica entre el portasegmento y la aleación de aluminio del pistón. El portasegmento es una fundición de hierro austenítico (Ni-Resist con el fin de aumentar la resistencia al desgaste de la unión Al-fin del primer segmento y se utiliza en motores diésel altamente cargados. Se realizó un examen metalográfico de la unión intermetálica, mediante un microscopio óptico en combinación con SEM/EDS. Los satisfactorios resultados obtenidos muestran la formación de contacto metálico (unión Al-fin del primer segmento entre el portasegmento y la aleación de aluminio del pistón.

Intermetallic Alloys as CO Electroreduction Catalysts-Role of Isolated Active Sites

DEFF Research Database (Denmark)

Karamad, Mohammadreza; Tripkovic, Vladimir; Rossmeisl, Jan

2014-01-01

One of the main challenges associated with the electrochemical CO or CO2 reduction is poor selectivity toward energetically rich products. In order to promote selectivity toward hydrocarbons and alcohols, most notably, the hydrogen evolution reaction (HER) should be suppressed. To achieve this goal...... potentially selective intermetallic surfaces on which CO can be reduced to methanol at potentials comparable to or even slightly positive than those for CO/CO2 reduction to methane on Cu. Common features shared by most of the selective alloys are single TM sites. The role of single sites is to block parasitic...... HER and thereby promote CO reduction....

Thermodynamic data for uranium and thorium intermetallic compounds: A historical perspective

International Nuclear Information System (INIS)

Alcock, C.B.

1989-01-01

The development of quantitative information concerning the stabilities of uranium and thorium intermetallic compounds since the publication of Rough and Bauer's phase diagram compilation are reviewed. During this era a number of high temperature measurement techniques have been developed, from gas/solid equilibration to mass spectrometry and from high temperature calorimetry to solid state electrochemistry, and the growth of quantitative information has run parallel to this evolution. The amount of experimental effort now appears to be declining, and the task presently of major importance is to integrate and rationalize the quantitative information, an effort which will undoubtedly lead to new experimental initiatives. (orig.)

Influence of Filler Alloy Composition and Process Parameters on the Intermetallic Layer Thickness in Single-Sided Cold Metal Transfer Welding of Aluminum-Steel Blanks

Science.gov (United States)

Silvayeh, Zahra; Vallant, Rudolf; Sommitsch, Christof; Götzinger, Bruno; Karner, Werner; Hartmann, Matthias

2017-11-01

Hybrid components made of aluminum alloys and high-strength steels are typically used in automotive lightweight applications. Dissimilar joining of these materials is quite challenging; however, it is mandatory in order to produce multimaterial car body structures. Since especially welding of tailored blanks is of utmost interest, single-sided Cold Metal Transfer butt welding of thin sheets of aluminum alloy EN AW 6014 T4 and galvanized dual-phase steel HCT 450 X + ZE 75/75 was experimentally investigated in this study. The influence of different filler alloy compositions and welding process parameters on the thickness of the intermetallic layer, which forms between the weld seam and the steel sheet, was studied. The microstructures of the weld seam and of the intermetallic layer were characterized using conventional optical light microscopy and scanning electron microscopy. The results reveal that increasing the heat input and decreasing the cooling intensity tend to increase the layer thickness. The silicon content of the filler alloy has the strongest influence on the thickness of the intermetallic layer, whereas the magnesium and scandium contents of the filler alloy influence the cracking tendency. The layer thickness is not uniform and shows spatial variations along the bonding interface. The thinnest intermetallic layer (mean thickness < 4 µm) is obtained using the silicon-rich filler Al-3Si-1Mn, but the layer is more than twice as thick when different low-silicon fillers are used.

Investigation of passivity and its breakdown on Fe3Al–Si and Fe3Al–Ge intermetallics in chloride-containing solution

International Nuclear Information System (INIS)

Rosalbino, F.; Carlini, R.; Parodi, R.; Zanicchi, G.; Scavino, G.

2014-01-01

Highlights: • Passivity and its breakdown on Fe 3 Al–Si and Fe 3 Al–Ge iron aluminides was investigated. • Investigation was performed in borate buffer solution with and without 100 mM KCl. • Polarization, potentiostatic transients and impedance measurements have been employed. • Results have been compared with those obtained on Fe 3 Al intermetallic. • Si and Ge improve the resistance to localized corrosion of Fe 3 Al. - Abstract: The passivity and passivity breakdown of Fe 3 Al–Si and Fe 3 Al–Ge iron aluminides were studied in borate buffer solution (pH 8.4) in the absence and presence of 100 mM KCl, performing potentiodynamic polarization, potentiostatic transients and electrochemical impedance spectroscopy (EIS) measurements complemented with scanning electron microscopy (SEM). In the absence of chloride ions Si and Ge exercise a beneficial role in the passivating characteristics of Fe 3 Al intermetallic. Addition of Si or Ge significantly modifies the electrochemical response of iron aluminide Fe 3 Al resulting in a more stable passive film. In the presence of chloride ions all the intermetallic compounds experience localized corrosion (pitting). However, Si and Ge alloying additions increase the breakdown potential and the extent of passivation domain, indicating improved resistance to initiation of pitting corrosion. Furthermore, EIS measurements performed at the breakdown state evidenced higher R ct and lower depression angle values for Fe 3 Al–Si and Fe 3 Al–Ge iron aluminides compared to Fe 3 Al intermetallic, confirming their better localized corrosion behavior. The improved resistance to pitting corrosion results from the enhanced protective function of passive film due to the presence of Si or Ge that inhibit pit initiation by hindering the adsorption of Cl − ions at the metal surface

Femtosecond laser ablation and nanoparticle formation in intermetallic NiAl

Energy Technology Data Exchange (ETDEWEB)

Jorgensen, David J., E-mail: davidjjorgensen@engr.ucsb.edu; Titus, Michael S.; Pollock, Tresa M.

2015-10-30

Highlights: • The single-pulse fs laser ablation threshold of NiAl is 83 mJ/cm{sup 2}. • The transition between low- and high-fluence ablation regimes is 2.8 J/cm{sup 2}. • A bimodal size distribution of nanoparticles is formed with fs laser ablation. • Smaller nanoparticles are enriched in Al during pulsed fs laser ablation. • The target surface is depleted in Al during pulsed fs laser ablation. - Abstract: The ablation behavior of a stoichiometric intermetallic compound β-NiAl subjected to femtosecond laser pulsing in air has been investigated. The single-pulse ablation threshold for NiAl was determined to be 83 ± 4 mJ/cm{sup 2} and the transition to the high-fluence ablation regime occurred at 2.8 ± 0.3 J/cm{sup 2}. Two sizes of nanoparticles consisting of Al, NiAl, Ni{sub 3}Al and NiO were formed and ejected from the target during high-fluence ablation. Chemical analysis revealed that smaller nanoparticles (1–30 nm) tended to be rich in Al while larger nanoparticles (>100 nm) were lean in Al. Ablation in the low-fluence regime maintained this trend. Redeposited material and nanoparticles remaining on the surface after a single 3.7 J/cm{sup 2} pulse, one hundred 1.7 J/cm{sup 2} pulses, or one thousand 250 mJ/cm{sup 2} pulses were enriched in Al relative to the bulk target composition. Further, the surface of the irradiated high-fluence region was depleted in Al indicating that the fs laser ablation removal rate of the intermetallic constituents in this regime does not scale with the individual pure element ablation thresholds.

Computer simulations of disordering and amorphization kinetics in intermetallic compounds

International Nuclear Information System (INIS)

Spaczer, M.; Victoria, M.

1995-01-01

Molecular dynamics computer simulations on three intermetallic compounds, Cu 3 Au, Ni 3 Al and NiAl, have been performed to investigate the kinetics of the disordering and amorphization processes. These systems were chosen because reliable embedded atom potentials were developed for the constituent species and their alloys, and also because extended experimental results are available for them. Previous simulations of collision cascades with 5 keV Cu and Ni primary knock-out atom (PKA) showed a significant difference between the evolution of the short range order (SRO) and the crystalline order (CO) parameters in all of the intermetallics: a complete loss of the crystalline structure and only partial chemical disorder in the core of the cascade [T. Diaz de la Rubia et al., Phys. Rev. B 47 (1993) 11483; M. Spaczer et al., Phys. Rev. B 50 (1994) 13204]. The present paper deals with the simulation of the amorphization process in NiAl by 5 and 15 keV Ni PKAs. The kinetic energy of the atoms in the simulated systems was removed on different time scales to mimic strong or weak coupling between electrons and phonons. No evidence of amorphization was found at the end of the cascades created by the 5 keV recoils. However, the 15 keV PKA events showed that (i) in the no-coupling case the system evolved to a highly disordered state, (ii) an amorphous region with about 100 non-lattice atoms was found in the case of weak coupling, (iii) the locally melted and recrystallized region collapsed to a small dislocation loop when medium coupling was used and (iv) a highly ordered state resulted in the case of strong coupling. (orig.)

Effect of ternary alloying elements on microstructure and mechanical property of Nb-Si based refractory intermetallic alloy

International Nuclear Information System (INIS)

Kim, W.Y.; Kim, H.S.; Kim, S.K.; Ra, T.Y.; Kim, M.S.

2005-01-01

Microstructure and mechanical property at room temperature and at 1773 K of Nb-Si based refractory intermetallic alloys were investigated in terms of compression and fracture toughness test. Mo and V were chosen as ternary alloying elements because of their high melting points, atomic sizes smaller than Nb. Both ternary alloying elements were found to have a significant role in modifying the microstructure from dispersed structure to eutectic-like structure in Nb solid solution/Nb 5 Si 3 intermetallic composites. The 0.2% offset yield strength at room temperature increased with increasing content of ternary elements in Nb solid solution and volume fraction of Nb 5 Si 3 . At 1773 K, Mo addition has a positive role in increasing the yield strength. On the other hand, V addition has a role in decreasing the yield strength. The fracture toughness of ternary alloys was superior to binary alloys. Details will be discussed in correlation with ternary alloying, volume fraction of constituent phase, and the microstructure. (orig.)

Mictomagnetic, ferromagnetic, and antiferromagnetic transitions in La(FexAl1–x)13 intermetallic compounds

NARCIS (Netherlands)

Palstra, T.T.M.; Nieuwenhuys, G.J.; Mydosh, J.A.; Buschow, K.H.J.

1985-01-01

Cubic La(FexAl1–x)13 intermetallic compounds can be stabilized with iron concentration x between 0.46 and 0.92 in the NaZn13-type structure (D23) with Fm3c (Oh6) space-group symmetry. Here the Fe-Fe coordination number can increase up to 12. At low x values, a mictomagnetic regime occurs with

Advanced ordered intermetallic alloy deployment

Energy Technology Data Exchange (ETDEWEB)

Liu, C.T.; Maziasz, P.J.; Easton, D.S. [Oak Ridge National Lab., TN (United States)

1997-04-01

The need for high-strength, high-temperature, and light-weight materials for structural applications has generated a great deal of interest in ordered intermetallic alloys, particularly in {gamma}-based titanium aluminides {gamma}-based TiAl alloys offer an attractive mix of low density ({approximately}4g/cm{sup 3}), good creep resistance, and high-temperature strength and oxidation resistance. For rotating or high-speed components. TiAl also has a high damping coefficient which minimizes vibrations and noise. These alloys generally contain two phases. {alpha}{sub 2} (DO{sub 19} structure) and {gamma} (L 1{sub 0}), at temperatures below 1120{degrees}C, the euticoid temperature. The mechanical properties of TiAl-based alloys are sensitive to both alloy compositions and microstructure. Depending on heat-treatment and thermomechanical processing, microstructures with near equiaxed {gamma}, a duplex structure (a mix of the {gamma} and {alpha}{sub 2} phases) can be developed in TiAl alloys containing 45 to 50 at. % Al. The major concern for structural use of TiAl alloys is their low ductility and poor fracture resistance at ambient temperatures. The purpose of this project is to improve the fracture toughness of TiAl-based alloys by controlling alloy composition, microstructure and thermomechanical treatment. This work is expected to lead to the development of TiAl alloys with significantly improved fracture toughness and tensile ductility for structural use.

Rare-earth transition-metal intermetallics: Structure-bonding-property relationships

Energy Technology Data Exchange (ETDEWEB)

Han, M. K. [Iowa State Univ., Ames, IA (United States)

2006-01-01

The explorations of rare-earth, transition metal intermetallics have resulted in the synthesis and characterization, and electronic structure investigation, as well as understanding the structure-bonding property relationships. The work has presented the following results: (1) Understanding the relationship between compositions and properties in LaFe_13-xSi_x system: A detailed structural and theoretical investigation provided the understanding of the role of a third element on stabilizing the structure and controlling the transformation of cubic NaZn{sub 13}-type structures to the tetragonal derivative, as well as the relationship between the structures and properties. (2) Synthesis of new ternary rare-earth iron silicides Re_2-xFe₄Si_14-y and proposed superstructure: This compound offers complex structural challenges such as fractional occupancies and their ordering in superstructure. (3) Electronic structure calculation of FeSi₂: This shows that the metal-semiconductor phase transition depends on the structure. The mechanism of band gap opening is described in terms of bonding and structural distortion. This result shows that the electronic structure calculations are an essential tool for understanding the relationship between structure and chemical bonding in these compounds. (4) Synthesis of new ternary rare-earth Zinc aluminides Tb₃Zn_3.6Al_7.4: Partially ordered structure of Tb₃Zn_3.6Al_7.4 compound provides new insights into the formation, composition and structure of rare-earth transition-metal intermetallics. Electronic structure calculations attribute the observed composition to optimizing metal-metal bonding in the electronegative (Zn, Al) framework, while the specific ordering is strongly influenced by specific orbital interactions. (5) Synthesis of new structure type of Zn₃₉(Cr_xAl_1-x)₈₁

Rare-Earth Transition-Metal Intermetallics: Structure-bonding-Property Relationships

Energy Technology Data Exchange (ETDEWEB)

Han, Mi-Kyung [Iowa State Univ., Ames, IA (United States)

2006-01-01

Our explorations of rare-earth, transition metal intermetallics have resulted in the synthesis and characterization, and electronic structure investigation, as well as understanding the structure-bonding-property relationships. Our work has presented the following results: (1) Understanding the relationship between compositions and properties in LaFe_13-xSi_x system: A detailed structural and theoretical investigation provided the understanding of the role of a third element on stabilizing the structure and controlling the transformation of cubic NaZn₁₃-type structures to the tetragonal derivative, as well as the relationship between the structures and properties. (2) Synthesis of new ternary rare-earth iron silicides RE_2-xFe₄Si_14-y and proposed superstructure: This compound offers complex structural challenges such as fractional occupancies and their ordering in superstructure. (3) Electronic structure calculation of FeSi₂: This shows that the metal-semiconductor phase transition depends on the structure. The mechanism of band gap opening is described in terms of bonding and structural distortion. This result shows that the electronic structure calculations are an essential tool for understanding the relationship between structure and chemical bonding in these compounds. (4) Synthesis of new ternary rare-earth Zinc aluminides Tb₃Zn_3.6Al_7.4: Partially ordered structure of Tb_3.6Zn_13-xAl_7.4 compound provides new insights into the formation, composition and structure of rare-earth transition-metal intermetallics. Electronic structure calculations attribute the observed composition to optimizing metal-metal bonding in the electronegative (Zn, Al) framework, while the specific ordering is strongly influenced by specific orbital interactions. (5) Synthesis of new structure type of Zn₃₉(Cr_xAl_1-x

Synthesis of Fe-Al-Ti Based Intermetallics with the Use of Laser Engineered Net Shaping (LENS

Directory of Open Access Journals (Sweden)

Monika Kwiatkowska

2015-04-01

Full Text Available The Laser Engineered Net Shaping (LENS technique was combined with direct synthesis to fabricate L21-ordered Fe-Al-Ti based intermetallic alloys. It was found that ternary Fe-Al-Ti alloys can be synthesized using the LENS technique from a feedstock composed of a pre-alloyed Fe-Al powder and elemental Ti powder. The obtained average compositions of the ternary alloys after the laser deposition and subsequent annealing were quite close to the nominal compositions, but the distributions of the elements in the annealed samples recorded over a large area were inhomogeneous. No traces of pure Ti were observed in the deposited alloys. Macroscopic cracking and porosity were observed in all investigated alloys. The amount of porosity in the samples was less than 1.2 vol. %. It seems that the porosity originates from the porous pre-alloyed Fe-Al powders. Single-phase (L21, two-phase (L21-C14 and multiphase (L21-A2-C14 Fe-Al-Ti intermetallic alloys were obtained from the direct laser synthesis and annealing process. The most prominent feature of the ternary Fe-Al-Ti intermetallics synthesized by the LENS method is their fine-grained structure. The grain size is in the range of 3–5 μm, indicating grain refinement effect through the highly rapid cooling of the LENS process. The Fe-Al-Ti alloys synthesized by LENS and annealed at 1000 °C in the single-phase B2 region were prone to an essential grain growth. In contrast, the alloys annealed at 1000 °C in the two-phase L21-C14 region exhibited almost constant grain size values after the high-temperature annealing.

Effects of elastic anisotropy on mechanical behavior of intermetallic compounds

International Nuclear Information System (INIS)

Yoo, M.H.

1991-01-01

Fundamental aspects of the deformation and fracture behavior of ordered intermetallic compounds are examined within the framework of linear anisotropic elasticity theory of dislocations and cracks. The orientation dependence and the tension/compression asymmetry of yield stress are explained in terms of the anisotropic coupling effect of non-glide stresses to the glide strain. The anomalous yield behavior is related to the disparity (edge/screw) of dislocation mobility and the critical stress required for the dislocation multiplication mechanism of Frank-Read type. The slip-twin conjugate relationship, extensive faulting, and pseudo-twinning (martensitic transformation) at a crack tip can be enhanced also by the anisotropic coupling effect, which may lead to transformation toughening of shear type

Properties of vacancies type defects in intermetallic compounds of the Al-Mo system

International Nuclear Information System (INIS)

Pascuet, M.I; Fernandez, J.R; Monti, A.M

2006-01-01

There are five intermetallic compounds in the Al-Mo system that are stable at low temperatures. Of these, the richest phases in some of the two components are the compounds Al 12 Mo and AlMo 3 , whose Pearson symbols are cI26 and cP8, respectively. In both structures, the atoms of the minority component occupy positions bcc and each one of them is surrounded by 12 atoms first neighbors of the other component. These 13 atoms form icosahedron shaped units or heaps. Unlike what occurs in Al 12 Mo, the AlMo 3 heaps are superposed by sharing atoms from the majority component. The neighboring environment of the majority component is mixed but differs considerably in one or another intermetallic. In each structure, the sites occupied by any given species are crystallographically equivalent, that is, they can self generate from one of the positions and from the crystalline structure's elements of symmetry. This work studies the energy of vacancies and antisites in both compounds and the atomic-jump processes to vacant sites. Computer simulation techniques were used based on minimizing the system's energy. Many-body embedded-atom potentials were used to represent the atomic interactions. The potential mixture used resulted in an adjustment to the crystalline structure of the AlMo 3 phase at low temperatures and to its formation energy (cw)

X-ray diffraction study of the phase purity, order and texture of ductile B2 intermetallics

Energy Technology Data Exchange (ETDEWEB)

Mulay, R.P.; Wollmershauser, J.A.; Heisel, M.A. [Materials Science and Engineering, University of Virginia, Charlottesville, VA 22904-4745 (United States); Bei, H. [Oak Ridge National Laboratory, Material Science and Technology Division, Oak Ridge, TN 37831 (United States); Russell, A.M. [Iowa State University, Department of Materials Science and Engineering, Ames, IA 50011 (United States); Agnew, S.R., E-mail: sra4p@virginia.edu [Materials Science and Engineering, University of Virginia, Charlottesville, VA 22904-4745 (United States)

2010-04-15

Representatives (AgY, CuY, AgEr, CuDy, MgY and MgCe) of the newly discovered family of ductile stoichiometric B2 intermetallic (metal-rare-earth element, MR) compounds were characterized by X-ray diffraction, to determine if their anomalous ductility is related to an exceptional level of phase purity, lack of chemical ordering or a strong crystallographic texture. Brittle NiAl served as an anti-type in this study. We found that all of the rare-earth compounds, except MgY, have a significant volume fraction ({approx}5-20 vol.%) of second phases (M{sub 2}R intermetallics and R{sub 2}O{sub 3} oxides), which has not been reported in previous studies of these materials. The most ductile of observed MR compounds, AgY, is highly ordered. A moderate texture was observed in AgY, which may explain its higher ductility (using polycrystal modeling) as compared to other MR compounds. However, the intrinsic polycrystalline ductility of these compounds in the randomly textured state (like that observed in CuY) still has no specific, definitive explanation.

X-ray diffraction study of the phase purity, order and texture of ductile B2 intermetallics

International Nuclear Information System (INIS)

Mulay, R.P.; Wollmershauser, J.A.; Heisel, M.A.; Bei, H.; Russell, A.M.; Agnew, S.R.

2010-01-01

Representatives (AgY, CuY, AgEr, CuDy, MgY and MgCe) of the newly discovered family of ductile stoichiometric B2 intermetallic (metal-rare-earth element, MR) compounds were characterized by X-ray diffraction, to determine if their anomalous ductility is related to an exceptional level of phase purity, lack of chemical ordering or a strong crystallographic texture. Brittle NiAl served as an anti-type in this study. We found that all of the rare-earth compounds, except MgY, have a significant volume fraction (∼5-20 vol.%) of second phases (M 2 R intermetallics and R 2 O 3 oxides), which has not been reported in previous studies of these materials. The most ductile of observed MR compounds, AgY, is highly ordered. A moderate texture was observed in AgY, which may explain its higher ductility (using polycrystal modeling) as compared to other MR compounds. However, the intrinsic polycrystalline ductility of these compounds in the randomly textured state (like that observed in CuY) still has no specific, definitive explanation.

Determination of the enthalpy of formation of Ni-Al intermetallic compounds using differential scanning calorimetry technique

International Nuclear Information System (INIS)

Kubaski, Evaldo Toniolo; Capocchi, Jose Deodoro Trani; Cintho, Osvaldo Mitsuyuki

2010-01-01

The compositions Ni20Al80, Ni25Al75, Ni40Al60, Ni50Al50, Ni60Al40 and Ni75Al25 (at. %) were heated in a calibrated thermal analysis equipment. All runs were conducted at a heating rate of 10 deg C/min under a dynamic argon atmosphere. Each composition was heated until the completion of the corresponding exothermic reaction responsible for intermetallic compound formation, and, also heated to 1480 deg C. The products obtained were characterized using X ray diffraction in order to identify the intermetallic compounds that were synthesized. Moreover, the results were evaluated using variance analysis. As a result, enthalpies of formation of Ni 2 Al 3 and Ni 3 Al compounds were determined by means of this methodology. Experimental values were 167 kJ/mol and 93 kJ/mol for Ni 2 Al 3 and Ni 3 Al, respectively. The former is 18% lower than the value found on literature, while the latter is 6% greater. (author)

A spin echo study of A15 intermetallic compounds

International Nuclear Information System (INIS)

Schoep, G.K.

1976-01-01

This thesis mainly concerns the measurement of spin-lattice relaxation times in intermetallic compounds of the bcc lattice structure, having the formula V 3 X (C = Pt, Ir, Os, Pd, Rh, Ni, Co, Au). When, in a spin echo experiment, a two-pulse sequence was applied, several quadrupolar echoes were observed. Special attention is given to the 'forbidden' echoes (absol.(Δm')GT1) in V 3 Au and V 3 Co. In relation to the V 3 X compounds, several characteristics are discussed including temperature dependence and concentration dependence of spin relaxation times, superconductivity and the importance of d-state electrons in determination of the spin relaxation times. Finally, the above characteristics were determined for 6 different samples of the vanadium-gold alloy, V 3 Au, specifically

Platinum Iron Intermetallic Nanoparticles Supported on Carbon Formed In Situ by High-Pressure Pyrolysis for Efficient Oxygen Reduction

DEFF Research Database (Denmark)

Hu, Yang; Jensen, Jens Oluf; Zhang, Wei

2016-01-01

Carbon-supported PtFe alloy catalysts are synthesized by the one-step, high-temperature pyrolysis of Pt, Fe, and C precursors. As a result of the high temperature, the formed PtFe nanoparticles possess highly ordered, face-centered tetragonal, intermetallic structures with a mean size of ≈11.8 nm....... At 0.9 V versus the reversible hydrogen electrode, the PtFe nanoparticles show a 6.8 times higher specific activity than the reference Pt/C catalyst towards the oxygen reduction reaction (ORR) as well as excellent stability, most likely because of the durable intermetallic structure and the preleaching...... treatment of the catalyst. During these preliminary syntheses, we found that a portion of the PtFe nanoparticles is buried in the in situ formed carbon phase, which limits Pt utilization in the catalyst and results in a mass-specific activity equivalent to the commercial Pt/C catalyst. Moreover...

Tracing crystal-field splittings in the rare-earth-based intermetallic CeIrIn5

Science.gov (United States)

Chen, Q. Y.; Wen, C. H. P.; Yao, Q.; Huang, K.; Ding, Z. F.; Shu, L.; Niu, X. H.; Zhang, Y.; Lai, X. C.; Huang, Y. B.; Zhang, G. B.; Kirchner, S.; Feng, D. L.

2018-02-01

Crystal electric field states in rare earth intermetallics show an intricate entanglement with the many-body physics that occurs in these systems and that is known to lead to a plethora of electronic phases. Here we attempt to trace different contributions to the crystal electric field (CEF) splittings in CeIrIn5, a heavy-fermion compound and member of the Ce M In5 (M = Co, Rh, Ir) family. To this end, we utilize high-resolution resonant angle-resolved photoemission spectroscopy (ARPES) and present a spectroscopic study of the electronic structure of this unconventional superconductor over a wide temperature range. As a result, we show how ARPES can be used in combination with thermodynamic measurements or neutron scattering to disentangle different contributions to the CEF splitting in rare earth intermetallics. We also find that the hybridization is stronger in CeIrIn5 than CeCoIn5 and the effects of the hybridization on the Fermi volume increase is much smaller than predicted. By providing experimental evidence for 4 f7/2 1 splittings which, in CeIrIn5, split the octet into four doublets, we clearly demonstrate the many-body origin of the so-called 4 f7/2 1 state.

STrategically Acquired Gradient Echo (STAGE) imaging, part I: Creating enhanced T1 contrast and standardized susceptibility weighted imaging and quantitative susceptibility mapping.

Science.gov (United States)

Chen, Yongsheng; Liu, Saifeng; Wang, Yu; Kang, Yan; Haacke, E Mark

2018-02-01

To provide whole brain grey matter (GM) to white matter (WM) contrast enhanced T1W (T1WE) images, multi-echo quantitative susceptibility mapping (QSM), proton density (PD) weighted images, T1 maps, PD maps, susceptibility weighted imaging (SWI), and R2* maps with minimal misregistration in scanning times creating enhanced GM/WM contrast (the T1WE). The proposed T1WE image was created from a combination of the proton density weighted (6°, PDW) and T1W (24°) images and corrected for RF transmit field variations. Prior to the QSM calculation, a multi-echo phase unwrapping strategy was implemented using the unwrapped short echo to unwrap the longer echo to speed up computation. R2* maps were used to mask deep grey matter and veins during the iterative QSM calculation. A weighted-average sum of susceptibility maps was generated to increase the signal-to-noise ratio (SNR) and the contrast-to-noise ratio (CNR). The proposed T1WE image has a significantly improved CNR both for WM to deep GM and WM to cortical GM compared to the acquired T1W image (the first echo of 24° scan) and the T1MPRAGE image. The weighted-average susceptibility maps have 80±26%, 55±22%, 108±33% SNR increases across the ten subjects compared to the single echo result of 17.5ms for the putamen, caudate nucleus, and globus pallidus, respectively. STAGE imaging offers the potential to create a standardized brain imaging protocol providing four pieces of quantitative tissue property information and multiple types of qualitative information in just 5min. Published by Elsevier Inc.

The effect of graphene on the intermetallic and joint strength of Sn-3.5Ag lead-free solder

Science.gov (United States)

Mayappan, R.; Salleh, A.; Andas, J.

2017-09-01

Solder has been widely used in electronic industry as interconnection for electronic packaging. European Union and Japan have restricted the use of Sn-Pb solder as it contains lead which can harmful to human health and environment. Due to this, many researches have been done in order to find a suitable replacement for the lead solder. Although many lead-free solders are available, the Sn-3.5Ag solder with the addition of graphene seem to be a suitable candidate. In this study, a 0.07 wt% graphene nanosheet was added into the Sn-3.5Ag solder and this composite solder was prepared under powder metallurgy method. The solder was reacted with copper substrate at 250 °C for one minute. For joint strength analysis, two copper strips were soldered together. The solder joint was aged at temperature 100 °C for 500 hours. Scanning Electron Microscope (SEM) was used to observe the interfacial reaction and Instron machine was used to determine the joint strength. Cu6Sn5 intermetallic layer was formed at the interface between the Cu substrate and the solders. Composite solder showed the retardation of the intermetallic growth compared to the plain solder. The thickness value of the intermetallic was used to calculate the growth rate the IMC. The graphene nanosheets added solder has lower growth rate which is 3.86 × 10-15 cm2/s compared to the plain solder 7.15 × 10-15 cm2/s. Shear strength analysis show that the composite solder has higher joint compared to the plain solder.

Extended spectrum of antibiotic susceptibility for tuberculosis, Djibouti.

Science.gov (United States)

Bouzid, Fériel; Astier, Hélène; Osman, Djaltou Aboubaker; Javelle, Emilie; Hassan, Mohamed Osman; Simon, Fabrice; Garnotel, Eric; Drancourt, Michel

2018-02-01

In the Horn of Africa, there is a high prevalence of tuberculosis that is reported to be partly driven by multidrug-resistant (MDR) Mycobacterium tuberculosis strictu sensu strains. We conducted a prospective study to investigate M. tuberculosis complex species causing tuberculosis in Djibouti, and their in vitro susceptibility to standard anti-tuberculous antibiotics in addition to clofazimine, minocycline, chloramphenicol and sulfadiazine. Among the 118 mycobacteria isolates from 118 successive patients with suspected pulmonary tuberculosis, 111 strains of M. tuberculosis, five Mycobacterium canettii, one 'Mycobacterium simulans' and one Mycobacterium kansasii were identified. Drug-susceptibility tests performed on the first 78 isolates yielded nine MDR M. tuberculosis isolates. All isolates were fully susceptible to clofazimine, minocycline and chloramphenicol, and 75 of 78 isolates were susceptible to sulfadiazine. In the Horn of Africa, patients with confirmed pulmonary tuberculosis caused by an in vitro susceptible strain may benefit from anti-leprosy drugs, sulfamides and phenicol antibiotics. Copyright © 2017 Elsevier B.V. and International Society of Chemotherapy. All rights reserved.

Measurement of complex RF susceptibility using a series Q-meter

International Nuclear Information System (INIS)

Kisselev, Yu.F.; Dulya, C.M.; Niinikoski, T.O.

1995-01-01

In this paper we have for the first time derived closed form expressions for the nuclear magnetic susceptibility in terms of the series Q-meter output voltage. We discuss the corrections involved in determining nuclear polarization from NMR signals by using the deuteron and proton spin systems as examples. Deuteron signals are shown to exhibit a false asymmetry, while proton signals have substantial shape distortions. Moreover, for the first time the importance of making a phase correction is demonstrated. We conclude that the series Q-meter with real part detection is not sufficient to produce an output voltage from which the nuclear susceptibility can be determined. An additional phase-sensitive detector is proposed for obtaining the imaginary part of the signal required for unambiguous extraction of the complex RF susceptibility. ((orig.))

Description of structure of Fe-Zn intermetalic compounds present in hot-dip galvanized coatings on steel

Directory of Open Access Journals (Sweden)

P. Pokorny

2015-10-01

Full Text Available The article is describing formation, composition, morphology and crystallographic characteristics of intermetalic compounds Fe - Zn present in the coating formed during the process of low-temperature hot-dip galvanizing of carbon steels. In mutual confrontation we introduce older bibliography and results of latest modern researches based on combination of most precise analytical methods.

Ultrafast and Highly Reversible Sodium Storage in Zinc-Antimony Intermetallic Nanomaterials

KAUST Repository

Nie, Anmin

2015-12-17

The progress on sodium-ion battery technology faces many grand challenges, one of which is the considerably lower rate of sodium insertion/deinsertion in electrode materials due to the larger size of sodium (Na) ions and complicated redox reactions compared to the lithium-ion systems. Here, it is demonstrated that sodium ions can be reversibly stored in Zn-Sb intermetallic nanowires at speeds that can exceed 295 nm s-1. Remarkably, these values are one to three orders of magnitude higher than the sodiation rate of other nanowires electrochemically tested with in situ transmission electron microscopy. It is found that the nanowires display about 161% volume expansion after the first sodiation and then cycle with an 83% reversible volume expansion. Despite their massive expansion, the nanowires can be cycled without any cracking or facture during the ultrafast sodiation/desodiation process. In addition, most of the phases involved in the sodiation/desodiation process possess high electrical conductivity. More specifically, the NaZnSb exhibits a layered structure, which provides channels for fast Na+ diffusion. This observation indicates that Zn-Sb intermetallic nanomaterials offer great promise as high rate and good cycling stability anodic materials for the next generation of sodium-ion batteries. Sodium ions can be stored in Zn4 Sb3 nanowires with a speed of 295.5 nm/s, which is one to three orders of magnitude higher than that of other nanowires electrochemically tested by the same method. Despite their massive expansion, the nanowires can be cycled dozens of times without any internal fracture during the ultrafast sodiation/desodiation process. © 2015 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

The possibility to use TiAl intermetallics for high temperature applications

International Nuclear Information System (INIS)

Molotkov, A.V.

1993-01-01

Titanium aluminide TiAl is the promising heat resisting structural material with operation temperature up to 850-900 deg C. This intermetallic compound is characterized by low density and high specific values of elasticity moduli and heat resistance properties in wide temperature range, as compared to known heat resisting titanium, iron and nickel base alloys. Test batch of pressed blades was manufactured of TiAl with the use of powder technology. Results of testing showed, that endurance strength of blades exceeded by 30% the strength, required for operation. The calculations showed, that the use of such blades in gas-turbine cagines could provide 30-40% decrease of mass of compressor blading

Elemental analysis of the Al-Fe intermetallic prepared by fast solidification; Analisis elemental del intermetalico Al-Fe preparado por solidificacion rapida

Energy Technology Data Exchange (ETDEWEB)

Sandoval J, R.A.; Lopez M, J.; Ramirez T, J.J.; Aspiazu F, J.; Villasenor S, P. [ININ, 52045 Ocoyoacac, Estado de Mexico (Mexico)

2003-07-01

Applying the PIXE technique samples of the Al-Fe intermetallic prepared by fast solidification, obtained starting from Al recycled were analyzed. The concentrations of the found elements are given. (Author)

FY 1992 Report on the survey results. Surveys on trends of research and development of advanced materials for severe environments (Intermetallic compounds); 1992 nendo chotaikankyosei senshin zairyo no kenkyu kaihatsu (kinzokukan kagobutsu) ni kakawaru kenkyu doko chosa

Energy Technology Data Exchange (ETDEWEB)

NONE

1993-03-01

The trends of the ongoing researches on intermetallic compounds are surveyed through interviews and inquiries, in order to evaluate the results of the projects and research and development of the advanced materials for severe environments, and also to survey the research trends. The survey results are pigeonholed into 4 general categories; (1) research trends in the USA, UK and Germany, (2) notable topics of recent progress in intermetallic research and development, (3) evaluation of the projects, and (4) lists of the results of the researches on the Al-Ti and Al-Nb intermetallic compounds. The ongoing projects include those for intermetallic compounds of high specific strength and of high melting point, the former being represented by Al-Ti compounds and the latter by Al-Nb compounds, for aircraft and space development purposes. The projects are evaluated, viewed from materials and purposes/targets pursued by the projects, R and D organizations, and degree of attention the projects are attracting. The intermetallic compounds are extensively studied and attracting attention in various countries, but possibilities of achieving the set targets are rather pessimistic. (NEDO)

Identification of intermetallic phases in a eutectic Al-Si casting alloy using electron backscatter diffraction pattern analysis

International Nuclear Information System (INIS)

Kral, M.V.; McIntyre, H.R.; Smillie, M.J.

2004-01-01

Intermetallic phases in sand cast eutectic Al-Si alloys were characterized using a combination of SEM, EDS and EBSD pattern analysis. Chinese script α-phase particles were consistent with cubic Al 19 (Fe,Mn) 5 Si 2 . Plate-shaped β-phase particles were consistent with tetragonal Al 3 (Fe,Mn)Si 2

The corrosion resistance of HVOF sprayed coatings with intermetallic phases in aggressive environments

OpenAIRE

B. Formanek; J. Cizner; B. Szczucka-Lasota; R. Przeliorz

2006-01-01

Purpose: The cyclic corrosion behavior of coatings with intermetallic matrix ( FeAl, NiAl and FeAl-TiAl) was investigated in aggressive gases.Design/methodology/approach: The composite coatings strengthened by a fine dispersive Al2O3 and other ceramic phases were thermally sprayed by HVOF method in Jet Kote 2 system. A kinetics test was carried out by periodic method for exposure times of up to 500 hours. Mass changes of the studied coatings during the corrosion test are presented. The surfac...

Development of Ion-Plasma Coatings for Protecting Intermetallic Refractory Alloys VKNA-1V and VKNA-25 in the Temperature Range of 1200 - 1250°C

Science.gov (United States)

Budinovskii, S. A.; Matveev, P. V.; Smirnov, A. A.

2017-05-01

Multilayer heat-resistant ion-plasma coatings for protecting the parts of the hot duct of gas-turbine engines produced from refractory nickel alloys based on VKNA intermetallics from high-temperature oxidation are considered. Coatings of the Ni - Cr - Al (Ta, Re, Hf, Y) + Al - Ni - Y systems are tested for high-temperature strength at 1200 and 1250°C. Metallographic and microscopic x-ray spectrum analyses of the structure and composition of the coatings in the initial condition and after the testing are performed. The effect of protective coatings of the Ni - Cr - Al - Hf + Al - Ni - Y systems on the long-term strength of alloys VKNA-1V and VKNA-25 at 1200°C is studied.

Theory of Valence Transitions in Ytterbium and Europium Intermetallics

International Nuclear Information System (INIS)

Zlatic, V.; Freericks, J.K.

2001-01-01

The exact solution of the multi-component Falicov-Kimball model in infinite-dimensions is presented and used to discuss a new fixed point of valence fluctuating intermetallics with Yb and Eu ions. In these compounds, temperature, external magnetic field, pressure, or chemical pressure induce a transition between a metallic state with the f-ions in a mixed-valent (non-magnetic) configuration and a semi-metallic state with the f-ions in an integral-valence (paramagnetic) configuration. The zero-field transition occurs at the temperature T V , while the zero-temperature transition sets in at the critical field H c . We present the thermodynamic and dynamic properties of the model for an arbitrary concentration of d- and f -electrons. For large U, we find a MI transition, triggered by the temperature or field- induced change in the f-occupancy. (author)

2. Intermetallic compounds with lanthanides

International Nuclear Information System (INIS)

Elemans, J.B.A.A.

1975-01-01

Theoretical considerations are given concerning the structures of intermetallic compounds of the lanthanides and thorium (R) on the one hand, and with Fe, Co or Ni (M) on the other. They all derive from the parent composition RM 5 with the CaCu 5 hexagonal structure. This consists of alternate layers in which the M atoms are distinguished as M 1 and M 2 . The other compounds whose structures are studied are obtained by systematic replacement of R by M, or vice versa. In the first type, every third R is replaced by two M's yielding R 2 M 17 compounds. The substitution may be truly random or structured in two ways: so that either the hexagonal structure is maintained or that it is converted into a rhombihedral one. In the second type, one M (in a M 1 position) out of every five is replaced by one R, giving rise to RM 2 compounds which form Laves phases. In the third type, the M 1 's are replaced by R's, resulting in compounds RM 3 . In the fourth type, every third M is replaced by R, yielding R 2 M 7 compounds. With M = Co and R a light lanthanide, the compounds are ferromagnets; with R yttrium, thorium, or a heavy lanthanide, they are ferrimagnets. The preparation of the compounds in an arc-melting apparatus under an Ar-atmosphere followed by annealing is described

Nanoporous alumina formed by self-organized two-step anodization of Ni{sub 3}Al intermetallic alloy in citric acid

Energy Technology Data Exchange (ETDEWEB)

Stepniowski, Wojciech J., E-mail: wstepniowski@wat.edu.pl [Department of Advanced Materials and Technology, Faculty of New Technologies and Chemistry, Military University of Technology, Kaliskiego 2 Str., 00-908 Warszawa (Poland); Cieslak, Grzegorz; Norek, Malgorzata; Karczewski, Krzysztof; Michalska-Domanska, Marta; Zasada, Dariusz; Polkowski, Wojciech; Jozwik, Pawel; Bojar, Zbigniew [Department of Advanced Materials and Technology, Faculty of New Technologies and Chemistry, Military University of Technology, Kaliskiego 2 Str., 00-908 Warszawa (Poland)

2013-01-01

Highlights: Black-Right-Pointing-Pointer Anodic porous alumina was formed by Ni{sub 3}Al intermetallic alloy anodization. Black-Right-Pointing-Pointer The anodizations were conducted in 0.3 M citric acid. Black-Right-Pointing-Pointer Nanopores geometry depends on anodizing voltage. Black-Right-Pointing-Pointer No barrier layer was formed during anodization. - Abstract: Formation of the nanoporous alumina on the surface of Ni{sub 3}Al intermetallic alloy has been studied in details and compared with anodization of aluminum. Successful self-organized anodization of this alloy was performed in 0.3 M citric acid at voltages ranging from 2.0 to 12.0 V using a typical two-electrode cell. Current density records revealed different mechanism of the porous oxide growth when compared to the mechanism pertinent for the anodization of aluminum. Electrochemical impedance spectroscopy experiments confirmed the differences in anodic oxide growth. Surface and cross-sections of the Ni{sub 3}Al intermetallic alloy with anodic oxide were observed with field-emission scanning electron microscope and characterized with appropriate software. Nanoporous oxide growth rate was estimated from cross-sectional FE-SEM images. The lowest growth rate of 0.14 {mu}m/h was found for the anodization at 0 Degree-Sign C and 2.0 V. The highest one - 2.29 {mu}m/h - was noticed for 10.0 V and 30 Degree-Sign C. Pore diameter was ranging from 18.9 nm (2.0 V, 0 Degree-Sign C) to 32.0 nm (12.0 V, 0 Degree-Sign C). Interpore distance of the nanoporous alumina was ranging from 56.6 nm (2.0 V, 0 Degree-Sign C) to 177.9 nm (12.0 V, 30 Degree-Sign C). Pore density (number of pore occupying given area) was decreasing with anodizing voltage increase from 394.5 pores/{mu}m{sup 2} (2.0 V, 0 Degree-Sign C) to 94.9 pores/{mu}m{sup 2} (12.0 V, 0 Degree-Sign C). All the geometrical features of the anodic alumina formed by two-step self-organized anodization of Ni{sub 3}Al intermetallic alloy are depending on the

On ternary intermetallic aurides. CaAu{sub 2}Al{sub 2}, SrAu{sub 2-x}Al{sub 2+x} and Ba{sub 3}Au{sub 5+x}Al{sub 6-x}

Energy Technology Data Exchange (ETDEWEB)

Stegemann, Frank [Institut fuer Anorganische und Analytische Chemie, Westfaelische Wilhelms-Universitaet Muenster (Germany); Benndorf, Christopher [Institut fuer Anorganische und Analytische Chemie, Westfaelische Wilhelms-Universitaet Muenster (Germany); Institut fuer Physikalische Chemie, Westfaelische Wilhelms-Universitaet Muenster (Germany); Institut fuer Mineralogie, Kristallographie und Materialwissenschaften, Universitaet Leipzig (Germany); Zhang, Yuemei; Fokwa, Boniface P.T. [Department of Chemistry, University of California, Riverside, CA (United States); Bartsch, Manfred; Zacharias, Helmut [Physikalisches Institut, Westfaelische Wilhelms-Universitaet Muenster (Germany); Eckert, Hellmut [Institut fuer Physikalische Chemie, Westfaelische Wilhelms-Universitaet Muenster (Germany); Instituto de Fisica de Sao Carlos, Universidade de Sao Paulo, Sao Carlos, SP (Brazil); Janka, Oliver [Institut fuer Anorganische und Analytische Chemie, Westfaelische Wilhelms-Universitaet Muenster (Germany); Institut fuer Chemie, Carl von Ossietzky Universitaet Oldenburg (Germany)

2017-11-17

The intermetallic compound CaAu{sub 2}Al{sub 2}, and the members of the solid solutions SrAu{sub 2-x}Al{sub 2+x} (0 ≤ x ≤ 0.33) and Ba{sub 3}Au{sub 5+x}Al{sub 6-x} (x = 0, 0.14, 0.49) were synthesized from the elements in sealed tantalum ampoules. The Ca compound crystallizes with the orthorhombic ThRu{sub 2}P{sub 2} type structure, whereas the targeted SrAu{sub 2}Al{sub 2} was found to form a solid solution according to SrAu{sub 2-x}Al{sub 2+x}. For the Ba system no ''BaAu{sub 2}Al{sub 2}'' was found, however, Ba{sub 3}Au{sub 5+x}Al{sub 6-x} was discovered to crystallize in the monoclinic space group C2/c with its own structure type. The samples were investigated by powder X-ray diffraction and their crystal structures were refined on the basis of single-crystal X-ray diffraction data. All compounds were characterized furthermore by susceptibility measurements. The crystallographic aluminum sites of CaAu{sub 2}Al{sub 2} and Ba{sub 3}Au{sub 5}Al{sub 6} can be differentiated by {sup 27}Al solid state NMR spectra on the basis of their different electric field gradients, in agreement with theoretical calculations. The electron transfer from the alkaline earth metals and the aluminum atoms onto the gold atoms was investigated by X-ray photoelectron spectroscopy (XPS) classifying these intermetallics as aurides, in full agreement with the calculated Bader charges. (copyright 2017 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

Computer simulation of disordering kinetics in irradiated A3B intermetallic compounds

International Nuclear Information System (INIS)

Spaczer, M.; Caro, A.; Victoria, M.; De la Rubia, T.

1994-01-01

Molecular dynamics computer simulations of collision cascades on intermetallic Ni 3 Al, Cu 3 Au and NiAl have been performed to study the nature of the disordering processes in the cascade. The evolution of the crystalline and chemical order parameters show different time scales. To understand these features we study the liquid phase of these three alloys and present simulation results concerning the dynamical melting of small samples, examining the relaxation time and saturation value of the chemical short range order, SRO. A theoretical model for the time evolution of the SRO is given. ((orig.))

INVESTIGATING THE fFORMATION OF INTERMETALLIC COMPOUNDS AND THE VARIATION OF BOND STRENGTH BETWEEN Al-Cu LAYERS AFTER ANNEALING IN PRESENCE OF NICKEL BETWEEN LAYERS

Directory of Open Access Journals (Sweden)

A. Shabani

2016-06-01

Full Text Available In the present study, the effect of post-rolling annealing heat treatment on the formation of intermetallic compounds between Al-Cu strips, in the presence of nickel coating on the Cu strips, was investigated. In addition, the effect of post-rolling annealing and intermetallic compounds on the bond strength of Al-Cu strips was evaluated. In order to prepare samples, Cu strips were coated with nickel by electroplating process. After surface preparing, Cu strips were placed between two Al strips and roll bonded. This method is used for producing Al-Ni-Cu composites. Then the samples were annealed at 773K for 2 h. The formation of intermetallic compounds was studied using energy dispersive spectroscopy (EDS and X-ray diffraction (XRD. Also, in order to investigate bond strength of Al-Cu after post-rolling annealing heat treatment, samples were produced using nickel powder and nickel coating. Then bond strength of strips was investigated using peeling test. The results revealed that by post-rolling annealing of layers, the bond strength between Al-Cu strips decreases dramatically.

Low temperature AC susceptibility of UCoGe crystal

Czech Academy of Sciences Publication Activity Database

Prokleška, J.; Pospíšil, J.; Vejpravová Poltierová, J.; Sechovský, V.; Šebek, Josef

2010-01-01

Roč. 200, č. 1 (2010), 012161/1-012161/4 ISSN 1742-6588. [International Conference on Magnetism - ICM 2009. Karlsruhe, 26.07.2009-31.07.2009] Institutional research plan: CEZ:AV0Z10100520 Keywords : magnetism * uranium * intermetallics Subject RIV: BM - Solid Matter Physics ; Magnetism

Susceptibility of ternary aluminum alloys to cracking during solidification

International Nuclear Information System (INIS)

Liu, Jiangwei; Kou, Sindo

2017-01-01

The crack susceptibility map of a ternary Al alloy system provides useful information about which alloy compositions are most susceptible to cracking and thus should be avoided by using a filler metal with a significantly different composition. In the present study the crack susceptibility maps of ternary Al alloy systems were calculated based on the maximum |dT/d(f S ) 1/2 | as an index for the crack susceptibility, where T is temperature and f S fraction solid. Due to the complexity associated with ternary alloy solidification, commercial thermodynamic software Pandat and Al database PanAluminum, instead of analytical equations, were used to calculate f S as a function of T and hence the maximum |dT/d(f S ) 1/2 | for ternary Al-Mg-Si, Al-Cu-Mg and Al-Cu-Si alloy systems. A crack susceptibility map covering 121 alloy compositions was constructed for each of the three ternary alloy systems at each of the following three levels of back diffusion: no back diffusion, back diffusion under a 100 °C/s cooling rate, and back diffusion under 20° C/s. The location of the region of high crack susceptibility, which is the most important part of the map, was shown in each of the nine calculated maps. These locations were compared with those observed in crack susceptibility tests by previous investigators. With back diffusion considered, either under 20 or 100 °C/s, the agreement between the calculated and observed maps was good especially for Al-Mg-Si and Al-Cu-Mg. Thus, the maximum |dT/d(f S ) 1/2 | can be used as a crack susceptibility index to construct crack susceptibility maps for ternary Al alloys and to evaluate the effect of back diffusion on their crack susceptibility. - Graphical abstract: The crack susceptibility map of a ternary alloy system indicates the composition range most susceptible to cracking, which should be avoided in welding or casting. The crack susceptibility maps of ternary Al alloy systems Al-Mg-Si, Al-Cu-Mg and Al-Cu-Si were calculated based

Magnetic susceptibility of molecular carbon: nanotubes and fullerite

Energy Technology Data Exchange (ETDEWEB)

Ramirez, A P; Haddon, R C; Zhou, O; Fleming, R M; Zhang, J; McClure, S M; Smalley, R E [AT T Bell Laboratories, Murray Hill, NJ (United States)

1994-07-01

Elemental carbon can be synthesized in a variety of geometrical forms, from three-dimensional extended structures (diamond) to finite molecules (C[sub 60] fullerite). Results are presented here on the magnetic susceptibility of the least well-understood members of this family, nanotubes and C[sub 60] fullerite. (1) Nanotubes represent the cylindrical form of carbon, intermediate between graphite and fullerite. They are found to have significantly larger orientation-averaged susceptibility, on a per carbon basis, than any other form of elemental carbon. This susceptibility implies an average band structure among nanotubes similar to that of graphite. (2) High-resolution magnetic susceptibility data on C[sub 60] fullerite near the molecular orientational-ordering transition at 259 K show a sharp jump corresponding to 2.5 centimeter-gram-second parts per million per mole of C[sub 60]. This jump directly demonstrates the effect of an intermolecular cooperative transition on an intramolecular electronic property, where the susceptibility jump may be ascribed to a change in the shape of the molecule due to lattice forces.

Void formation and its impact on Cu−Sn intermetallic compound formation

International Nuclear Information System (INIS)

Ross, Glenn; Vuorinen, Vesa; Paulasto-Kröckel, Mervi

2016-01-01

Void formation in the Cu−Sn system has been identified as a major reliability issue with small volume electronic interconnects. Voids form during the interdiffusion of electrochemically deposited Cu and Sn, with varying magnitude and density. Electroplating parameters include the electrolytic chemistry composition and the electroplating current density, all of which appear to effect the voiding characteristics of the Cu−Sn system. In addition, interfacial voiding affects the growth kinetics of the Cu_3Sn and Cu_6Sn_5 intermetallic compounds of the Cu−Sn system. The aim here is to present voiding data as a function of electroplating chemistry and current density over a duration (up to 72 h) of isothermal annealing at 423 K (150 °C). Voiding data includes the average interfacial void size and average void density. Voids sizes grew proportionally as a function of thermal annealing time, whereas the void density grew initially very quickly but tended to saturate at a fixed density. A morphological evolution analysis called the physicochemical approach is utilised to understand the processes that occur when a voided Cu/Cu_3Sn interface causes changes to the IMC phase growth. The method is used to simulate the intermetallic thickness growths' response to interfacial voiding. The Cu/Cu_3Sn interface acts as a Cu diffusion barrier disrupting the diffusion of Cu. This resulted in a reduction in the Cu_3Sn thickness and an accelerated growth rate of Cu_6Sn_5. - Highlights: • Average void size is proportional linearly to thermal annealing time. • Average void density grows initially very rapidly followed by saturation. • Voids located close to the Cu/Cu_3Sn interface affect IMC growth rates. • Voids act as a diffusion barrier inhibiting Cu diffusion towards Sn. • Voids located at the interface cause Cu_3Sn to be consumed by Cu_6Sn_5.

Codeformation processing of mechanically-dissimilar metal/intermetallic composites

Science.gov (United States)

Marte, Judson Sloan

A systematic and scientific approach has been applied to the study of codeformation processing. A series of composites having mechanically-dissimilar phases were developed in which the high temperature flow behavior of the reinforcement material could be varied independent of the matrix. This was accomplished through the use of a series of intermetallic matrix composites (IMCs) as discontinuous reinforcements in an otherwise conventional metal matrix composite. The IMCs are produced using an in-situ reaction synthesis technique, called the XD(TM) process. The temperature of the exothermic synthesis reaction, called the adiabatic temperature, has been calculated and shown to increase with increasing volume percentage of TiB2 reinforcement. Further, this temperature has been shown to effect the size and spacing of the TiB2, microstructural features which are often used in discontinuous composite strength models. Study of the high temperature flow behavior of the components of the metal/IMC composite is critical to the development of an understanding of codeformation. A series of compression tests performed at 1000° to 1200°C and strain-rates of 10-3 and 10-4 sec-1. Peak flow stresses were used to evaluate the influence of material properties and process conditions. These data were incorporated into phenomenologically-based constitutive equations that have been used to predict the flow behavior. It has been determined that plastic deformation of the IMCs occurs readily, and is largely TiB2 independent, at temperatures approaching the melting point of the intermetallic matrices. Ti-6Al-4V/IMC powder blends were extruded at high temperatures to achieve commensurately deformed microstructures. The results of codeformation processing were analyzed in terms of the plastic strain of the IMC particulates. IMC particle deformation was shown to increase with increasing IMC particle size, volume percentage of IMC, extrusion temperature, homologous temperature, extrusion

Significance of grain boundaries and stacking faults on hydrogen storage properties of Mg2Ni intermetallics processed by high-pressure torsion

International Nuclear Information System (INIS)

Hongo, Toshifumi; Edalati, Kaveh; Arita, Makoto; Matsuda, Junko; Akiba, Etsuo; Horita, Zenji

2015-01-01

Mg 2 Ni intermetallics are processed using three different routes to produce three different microstructural features: annealing at high temperature for coarse grain formation, severe plastic deformation through high-pressure torsion (HPT) for nanograin formation, and HPT processing followed by annealing for the introduction of stacking faults. It is found that both grain boundaries and stacking faults are significantly effective to activate the Mg 2 Ni intermetallics for hydrogen storage at 423 K (150 °C). The hydrogenation kinetics is also considerably enhanced by the introduction of large fractions of grain boundaries and stacking faults while the hydrogenation thermodynamics remains unchanged. This study shows that, similar to grain boundaries and cracks, stacking faults can act as quick pathways for the transportation of hydrogen in the hydrogen storage materials

Post-heat treatment of arc-sprayed coating prepared by the wires combination of Mg-cathode and Al-anode to form protective intermetallic layers

International Nuclear Information System (INIS)

Xu Rongzheng; Song Gang

2011-01-01

A Mg-Al intermetallic compounds coating was prepared on the surface of Mg-steel lap joint by arc-sprayed Al-Mg composite coating (Mg-cathode and Al-anode) and its post-heat treatment (PHT). The effect of PHT temperature on the phase transition, microstructure and mechanical properties of the coating was investigated by X-ray diffraction, scanning electron microscope, energy dispersive X-ray spectroscopy, optical microscope and microhardness test. The result shows that the intermetallic compounds layer that is mainly composed of Al 3 Mg 2 and Mg 17 Al 12 is formed by the self-diffusion reaction of Mg and Al splats in the coating after PHT for 4 h at 430 deg. C.

Diffusion in intermetallic compounds studied using short-lived radioisotopes

CERN Multimedia

Diffusion – the long range movement of atoms – plays an important role in materials processing and in determining suitable applications for materials. Conventional radiotracer methods for measuring diffusion can determine readily how distributions of radioactive probe atoms in samples evolve under varying experimental conditions. It is possible to obtain limited information about atomic jump rates and pathways from these measurements; however, it is desirable to make more direct observations of the atomic jumps by using experimental methods that are sensitive to atomic scale processes. One such method is time-differential perturbed $\\gamma$–$\\gamma$-angular correlation spectroscopy (PAC). Two series of PAC experiments using $^{111m}$Cd are proposed to contribute to fundamental understanding of diffusion in intermetallic compounds. The goal of the first is to determine the dominant vacancy species in several Li$_{2}$-structured compounds and see if the previously observed change in diffusion mechanism th...

A tem investigation on intermetallic particles in zircaloy-2

International Nuclear Information System (INIS)

Sudarminto, Harini Sosiati; Kuwano, Noriyuki; Oki, Kensuke

1996-01-01

Tem investigation were conducted on the heat treated zircaloy-2 having the composition of Zr containing 1.6% Sn, 0.2% Fe, 0.1% Cr and 0.05% Ni (%wt) in order tostudy the characteristics of intermetallic particles related to the microstructural basis on the corrosion effect. Forged zircaloy-2 was annealed in the β-phase at 1050 C degrees for various isothermally in the α-phase region at 650 and 750 C degrees, followed by water quenching. The size precipates, the lower became their number. By increasing the annealing temperature, the growth of precipitates formed in this zircaloy-2 were of the Zr(Cr,Fe) 2 and Zr 2 (Fe,Cr,Ni) types. These kinds of precipitates and the ratios of Fe/Cr were independent of size and shape of precipitates and annealing time and temperature. (author), 16 refs, 2 tabs, 5 figs

A five year study on the susceptibility of isolates from various parts of ...

African Journals Online (AJOL)

STORAGESEVER

2008-10-06

Oct 6, 2008 ... faecalis 200, Enterobacter aerogenes 175, Acinetobacter baumannii 150, Proteus vulgaris 110,. Providencia stuartii 101, Streptococcus pneumoniae 16, Citrobacter freundii 51. The isolates varied widely in their susceptibility pattern. Almost all the isolates were about 100% resistant to cloxacillin,.

Phase transition of intermetallic TbPt at high temperature and high pressure

Science.gov (United States)

Qin, Fei; Wu, Xiang; Yang, Ke; Qin, Shan

2018-04-01

Here we present synchrotron-based x-ray diffraction experiments combined with diamond anvil cell and laser heating techniques on the intermetallic rare earth compound TbPt (Pnma and Z  =  4) up to 32.5 GPa and ~1800 K. The lattice parameters of TbPt exhibit continuous compression behavior up to 18.2 GPa without any evidence of phase transformation. Pressure-volume data were fitted to a third-order Birch-Murnaghan equation of state with V 0  =  175.5(2) Å3, {{K}{{T0}}}   =  110(5) GPa and K{{T0}}\\prime   =  3.8(7). TbPt exhibits anisotropic compression with β a   >  β b   >  β c and the ratio of axial compressibility is 2.50:1.26:1.00. A new monoclinic phase of TbPt assigned to the Pc or P2/c space group was observed at 32.5 GPa after laser heating at ~1800 K. This new phase is stable at high pressure and presented a quenchable property on decompression to ambient conditions. The pressure-volume relationship is well described by the second-order Birch-Murnaghan equation of state, which yields V 0  =  672(4) Å3, {{K}{{T0}}}   =  123(6) GPa, which is about ~14% more compressible than the orthorhombic TbPt. Our results provide more information on the structure and elastic property view, and thus a better understanding of the physical properties related to magnetic structure in some intermetallic rare earth alloys.

Intermetallic Pd ₃ Pb nanowire networks boost ethanol oxidation and oxygen reduction reactions with significantly improved methanol tolerance

Energy Technology Data Exchange (ETDEWEB)

Shi, Qiurong [School of Mechanical and Materials Engineering; Washington State University; Pullman; USA; Zhu, Chengzhou [School of Mechanical and Materials Engineering; Washington State University; Pullman; USA; Key Laboratory of Pesticide and Chemical Biology; Bi, Cuixia [Institute of Crystal Materials; Shandong University; Jinan 250100; P. R. China; Xia, Haibing [Institute of Crystal Materials; Shandong University; Jinan 250100; P. R. China; Engelhard, Mark H. [Environmental Molecular Sciences Laboratory; Pacific Northwest National Laboratory; Richland; USA; Du, Dan [School of Mechanical and Materials Engineering; Washington State University; Pullman; USA; Key Laboratory of Pesticide and Chemical Biology; Lin, Yuehe [School of Mechanical and Materials Engineering; Washington State University; Pullman; USA

2017-01-01

Intermetallic nanocrystals are currently receiving extensive attention due to their well-defined crystal structures, highly ordered atomic distribution and superior structural stability that endow them with optimized catalytic activities, stabilities and high selectivity for use as electrocatalysts for fuel cells.

Titanium as an intermetallic phase stabilizer and its effect on the mechanical and thermal properties of Al-Si-Mg-Cu-Ti alloy

Energy Technology Data Exchange (ETDEWEB)

Choi, Se-Weon [Korea Institute of Industrial Technology, 6 Cheomdan-gwagiro 208 beon-gil, Buk-gu, Gwangju 500-480 (Korea, Republic of); Cho, Hoon-Sung [School of Materials Science and Engineering, Chonnam National University, 77 Yongbong-ro, Buk-gu, Gwangju 500-757 (Korea, Republic of); Kumai, Shinji [Department of Metallurgy and Ceramics Science, Tokyo Institute of Technology, S8-10, 2-12-1 O-okayama, Meguro-ku, Tokyo 152-8552 (Japan)

2016-12-15

The effect of precipitation of intermetallics on the mechanical and thermal properties of Al-6.5Si-0.44Mg-0.9Cu-(Ti) alloys (in wt%) during various artificial aging treatments was studied using a universal testing machine and a laser flash apparatus. The solution treatment of the alloy samples was conducted at 535 °C for 6 h, followed by quenching in warm water. The solution-treated samples were artificially aged for 5 h at different temperatures ranging from 170 °C to 220 °C. After the artificial aging treatment, the Al-6.5Si-0.44Mg-0.9Cu alloy (the Ti-free alloy) had a lower ultimate tensile strength (UTS) than the Al-6.5Si-0.44Mg-0.9Cu-0.2Ti alloy. The UTS response of the alloys was enhanced by the addition of Ti, with the maximum UTS showing an increase from 348 MPa for the Ti-free alloy to 363 MPa for that containing 0.2 wt% Ti, aged at 180 °C. The Ti-free alloy had a higher thermal diffusivity than the Ti-containing alloy over all temperature ranges. Upon increasing the temperature from 180 °C to 220 °C, the room temperature thermal diffusivities increased because the solute concentration in the α-Al matrix rapidly decreased. In particular, the thermal diffusivity increased significantly between 200 °C and 400 °C. This temperature range matched the range of intermetallic phase precipitation as confirmed by differential scanning calorimetry and measurement of the coefficient of thermal expansion. During the artificial aging treatment, the intermetallic phases precipitated and grew rapidly. These reactions induced a reduction of the solute atoms in the solid solution, thus producing a more significant reduction in the thermal diffusivity. As the temperature was increased to above 400 °C, the formation of intermetallic phases ceased, and the thermal diffusivity showed a steady value, regardless of the aging temperature.

Tigecycline in-vitro susceptibility and antibiotics fitness forgram-negative pathogens

International Nuclear Information System (INIS)

Arya, Subhash C.; Agarwal, N.

2008-01-01

Objective was to determine the tigecycline in-vitro susceptibility ofnaive gram-negative pathogens from serious infections in Delhi, India. DuringJuly to October 2007 investigations were carried out to determine thetigecycline in vitro susceptibility of 50 consecutive gram-negative pathogensfrom serious infections at the Sant Parmanand Hospital, Delhi, India. Minimumtigecycline inhibitory concentrations were determined employing the E testmethod (AB Biodisk). Twenty-four percent of isolates were found to betigecycline resistant or partly susceptible. Susceptibility of the isolateswere lower than meropenem but similar to piperacillin-tazobactum,amoxicillin-clavulanic acid and amikacin. Tigecycline resistance wasprevalent in the gram-negative isolates from serious infections prior to itsmarketing in India. The choice of any recently marketed antibiotic for apilot treatment against serious gram-negative infections should not beautomatic. In the initial phase of its marketing, it should be evaluated inparallel with the antibiotics with excellent local susceptibility profiles.(author)

A diffraction based study of the deformation mechanisms in anomalously ductile B2 intermetallics

Science.gov (United States)

Mulay, Rupalee Prashant

For many decades, the brittle nature of most intermetallic compounds (e.g. NiAl) has been the limiting factor in their practical application. Many B2 (CsCl prototypical structure) intermetallics are known to exhibit slip on the {110} slip mode, which provides only 3 independent slip systems and, hence, is unable to satisfy the von Mises (a.k.a. Taylor) criterion for polycrystalline ductility. As a result, inherent polycrystalline ductility is unexpected. Recent discovery of a number of ductile B2 intermetallics has raised questions about possible violation of the von Mises criterion by these alloys. These ductile intermetallic compounds are MR (metal (M) combined with a rare earth metal or group IV refractory metal (R)) alloys and are stoichiometric, ordered compounds. Single crystal slip trace analyses have only identified the presence of {011} or {010} slip systems. More than 100 other B2 MR compounds are known to exist and many of them have already been shown to be ductile (e.g., CuY, AgY, CuDy, CoZr, CoTi, etc.). Furthermore, these alloys exhibit a large Bauschinger effect. The present work uses several diffraction based techniques including electron back scattered diffraction (EBSD), X-ray diffraction (XRD) and in-situ neutron diffraction; in conjunction with scanning electron microscopy (SEM), transmission electron microscopy (TEM), mechanical testing, and crystal plasticity modeling, to elucidate the reason for ductility in select B2 alloys, explore the spread of this ductility over the B2 family, and understand the Bauschinger effect in these alloys. Several possible explanations (e.g., slip of dislocations, strong texture, phase transformations and twinning) for the anomalous ductility were explored. An X-ray diffraction based analysis ruled out texture, phase purity and departure from order as explanations for the anomalous ductility in MR alloys. In-situ neutron diffraction and post deformation SEM, EBSD, and TEM were unable to detect any evidence for

Electrochemical preparation of Al–Sm intermetallic compound whisker in LiCl–KCl Eutectic Melts

International Nuclear Information System (INIS)

Ji, De−Bin; Yan, Yong−De; Zhang, Mi−Lin; Li, Xing; Jing, Xiao−Yan; Han, Wei; Xue, Yun; Zhang, Zhi−Jian; Hartmann, Thomas

2015-01-01

Highlights: • The reduction process of Sm(III) was investigated in LiCl–KCl melt on an aluminum electrode at 773 K. • Al–Sm alloy with different phase structure (Al 2 Sm and Al 3 Sm) was prepared by potentiostatic electrolysis on an aluminum electrode with the change of electrolytic potentials and time in LiCl–KCl–SmCl 3 melts. • Al − Sm alloy containing whiskers (Al 4 Sm) was obtained by potentiostatic electrolysis (−2.10 V) on an aluminum electrode for 7 hours with the change of electrolytic temperature and cooling rate in LiCl–KCl–SmCl 3 (16.5 wt. %) melts. The results from micro–hardness test and potentiodynamic polarization test show the micro hardness and corrosion property are remarkably improved with the help of Al–Sm intermetallic compound whiskers. - Abstract: This work presents the electrochemical study of Sm(III) on an aluminum electrode in LiCl–KCl melts at 773 K by different electrochemical methods. Three electrochemical signals in cyclic voltammetry, square wave voltammetry, open circuit chronopotentiometry, and cathode polarization curve are attributed to different kinds of Al–Sm intermetallic compounds, Al 2 Sm, Al 3 Sm, and Al 4 Sm, respectively. Al–Sm alloy with different phase structure (Al 2 Sm and Al 3 Sm) could be obtained by the potentiostatic electrolysis with the change of electrolytic potentials and time. Al–Sm alloy containing whiskers (Al 4 Sm) was obtained by potentiostatic electrolysis (−2.10 V) on an aluminum electrode for 7 hours with the change of electrolytic temperature and cooling rate in LiCl–KCl–SmCl 3 (16.5 wt. %) melts. The XRD and SEM&EDS were employed to investigate the phase composition and microstructure of Al–Sm alloy. SEM analysis shows that lots of needle−like precipitates formed in Al–Sm alloy, and their ratios of length to diameter are found to be greater than 10 to 1. The TEM and electron diffraction pattern were performed to investigate the crystal structure of the

B2 intermetallic compounds of Zr. New class of the shape memory alloys

International Nuclear Information System (INIS)

Koval, Yu.N.; Delaey, L.; Jang, W.Y.

1995-01-01

It is known that the B2 equiatomic intermetallic compounds of Zr (ZrCo-based) undergo a martensitic transformation (MT) with wide temperature hysteresis. It was found that the MT is accompanied by the perfect shape memory effect (SME) for ZrCu and ZrRh. In this report we represent the results of structural analysis, electrical resistivity, calorimetric and SME measurements for ZrCu- and ZrCo-based compounds. Interrelation between structural, thermodynamical parameters of MT and SME in this alloys will be described. The shape memory aspects of this potential alloys for the application at high temperatures will be discussed. (orig.)

Magnetization and specific heat study of metamagnetism in Lu.sub.2./sub.Fe.sub.17./sub.-based intermetallic compounds

Czech Academy of Sciences Publication Activity Database

Tereshina, Evgeniya; Andreev, Alexander V.

2010-01-01

Roč. 18, č. 6 (2010), 1205-1210 ISSN 0966-9795 R&D Projects: GA ČR GA202/09/0339 Institutional research plan: CEZ:AV0Z10100520 Keywords : rare-earth intermetallics * magnetic properties * single crystal growth Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.327, year: 2010

Production of low oxygen contamination orthorhombic Ti-Al-Nb intermetallic foil

International Nuclear Information System (INIS)

Gill, S.C.; Peters, J.A.; Blatter, P.; Jaquet, J.C.; Morris, M.A.

1996-01-01

Aerospace industries continue the search for high performance materials, and recent years have seen rapid developments being made in the capabilities of Ti-Al based intermetallic alloys. Interest in these alloys is caused by their attractive combination of strength and density, but major drawbacks include brittleness at low temperature and sensitivity to interstitial contamination. Development of a relatively new class of alloys was stimulated in 1988 by the discovery of Banerjee et al. of a Ti-Al-Nb orthorhombic (O) phase based on the Ti 2 AlNb composition. Some important applications for these alloys require the use of foil ( 2 phase and leads to material embrittlement. ELIT (Extra Low Interstitial Transfer) pack-rolling, developed by Sulzer Innotec, offers a technique to avoid oxygen contamination

Influence of Al grain boundaries segregations and La-doping on embrittlement of intermetallic NiAl

Energy Technology Data Exchange (ETDEWEB)

Kovalev, Anatoly I., E-mail: a_kovalev@sprg.ru; Wainstein, Dmitry L.; Rashkovskiy, Alexander Yu.

2015-11-01

Highlights: • We investigated Al grain boundaries segregations in ordered pure and La-doped NiAl. • Structural segregation of Al decreases critical strain for brittle cracks nucleation. • La alloying sharply improves plasticity of NiAl intermetallic. • Metallicity of interatomic bonds on grain boundaries increases at La alloying. • We have experimentally measured by EELFS that La atoms are located in Al sublattice. - Abstract: The microscopic nature of intergranular fracture of NiAl was experimentally investigated by the set of electron spectroscopy techniques. The paper demonstrates that embrittlement of NiAl intermetallic compound is caused by ordering of atomic structure that leads to formation of structural aluminum segregations at grain boundaries (GB). Such segregations contain high number of brittle covalent interatomic bonds. The alloying by La increases the ductility of material avoiding Al GB enrichment and disordering GB atomic structure. The influence of La alloying on NiAl mechanical properties was investigated. GB chemical composition, atomic and electronic structure transformations after La doping were investigated by AES, XPS and EELFS techniques. To qualify the interatomic bonds metallicity the Fermi level (E{sub F}) position and electrons density (n{sub eff}) in conduction band were determined in both undoped and doped NiAl. Basing on experimental results the physical model of GB brittleness formation was proposed.

Influence of gas detonation spraying conditions on the quality of Fe-Al intermetallic protective coatings

Directory of Open Access Journals (Sweden)

Senderowski C.

2007-01-01

Full Text Available The aim of this paper is to present generalized research results and analyses of the quality of coatings produced with self decomposing Fe-Al intermetallic powders deposited on 1045 steel in the gas detonation spraying (GDS. A number of GDS experiments has been carried out with significantly changed operational spraying parameters (the volume of the fuel gas, carrier gas, distance and the frequency of spraying which define the process energy level directly influencing the quality of the coating. On the basis of the initial results the choice of the process parameters has been made to obtain the most advantageous set of geometrical and physical-mechanical properties of the coating material and substrate. The quality of the coatings was considered by taking into account the grain morphology, chemical content, phase inhomogeneity, cohesive porosity, as well as adhesive porosity in the substrate coating joint. The coating roughness was also considered. It was found that all GDS coatings produced are built with lamellar splats which result from the GDS process transformed (changed plasticity and geometry powder particles forming the deposit. The result of the GDS spraying parameters optimization is the lack of signs of melting of the material (even in microareas while the geometry of the deposited grains is considerably changed. This phenomenon has been considered as a proof of high plasticity of the GDS formed Fe-Al intermetallic coatings.

Behavior of palladium and its impact on intermetallic growth in palladium-coated Cu wire bonding

International Nuclear Information System (INIS)

Xu Hui; Qin, Ivy; Clauberg, Horst; Chylak, Bob; Acoff, Viola L.

2013-01-01

This paper describes the behavior of palladium in palladium-coated Cu (PdCu) wire bonding and its impact on bond reliability by utilizing transmission electron microscopy (TEM). A Pd layer approximately 80 nm thick, which is coated on the surface of Cu wire, dissolves into the Cu matrix during ball formation (under N 2 gas protection) when the wire tip is melted to form a ball. As a result of dissolving the very thin Pd layer into the ball, Pd is almost undetectable along the entire bond interface between the ball and the Al pad. The behavior of Pd during thermal aging in air, however, is different for central and peripheral interfaces. At the central interface, less than 5 at.% Pd is present after 168 h aging at 175 °C. At the periphery, however, Pd diffuses back and congregates, reaching a level of ∼12 at.% after 24 h, and a Pd-rich (Cu,Pd) 9 Al 4 layer (>40 at.% Pd) forms after 168 h. Pd acts substitutionally in Cu 9 Al 4 but cannot penetrate into the CuAl 2 or CuAl. By comparison of intermetallic thickness and interfacial morphology between PdCu and bare Cu wire bonds, it is concluded that the presence of Pd reduces intermetallic growth rate, and is associated with numerous nanovoids in PdCu bonds.

Low-temperature thermal expansion of metastable intermetallic Fe-Cr phases

International Nuclear Information System (INIS)

Gorbunoff, A.; Levin, A.A.; Meyer, D.C.

2009-01-01

The thermal expansion coefficients (TEC) of metastable disordered intermetallic Fe-Cr phases formed in thin Fe-Cr alloy films prepared by an extremely non-equilibrium method of the pulsed laser deposition are studied. The lattice parameters of the alloys calculated from the low-temperature wide-angle X-ray diffraction (WAXRD) patterns show linear temperature dependencies in the temperature range 143-293 K and a deviation from the linearity at lower temperatures. The linear thermal expansion coefficients determined from the slopes of the linear portions of the temperature-lattice parameter dependencies differ significantly from phase to phase and from the values expected for the body-centered cubic (b.c.c.) Fe 1-x Cr x solid solutions. Strain-crystallite size analysis of the samples is performed. Predictions about the Debye temperature and the mechanical properties of the alloys are made.

The system analysis of temperature and melting enthalpy of intermetallic compounds of antimony-lanthanoids system of Sb Ln, Sb2Ln composition

International Nuclear Information System (INIS)

Badalova, M.A.; Chamanova, M.; Dodkhoev, E.S.; Badalov, A.; Abdusalyamova, M.N.

2015-01-01

Present article is devoted to system analysis of temperature and melting enthalpy of intermetallic compounds of antimony-lanthanoids system of Sb Ln, Sb 2 Ln composition. The melting enthalpy was estimated. The temperature value was determined.

Amorphous phase formation in intermetallic Mg2Ni alloy synthesized by ethanol wet milling

International Nuclear Information System (INIS)

Wang, H.-W.; Chyou, S.-D.; Wang, S.-H.; Yang, M.-W.; Hsu, C.-Y.; Tien, H.-C.; Huang, N.-N.

2009-01-01

The hydriding/dehydriding properties of an intermetallic Mg 2 Ni alloy synthesized by wet ball milling in ethanol have been investigated. The appearance of the particle surface after different milling methods is one obvious difference. The alloyed powders prepared by either dry milling or wet milling under ethanol were characterized for phase content by X-ray diffractometer (XRD). The results show that two broad diffuse peaks, which are an ionic-organic-Mg amorphous material, appear in addition to the nickel element peaks. This unexpected amorphous phase has the special hydrogen absorbing/desorbing features.

School connectedness and susceptibility to smoking among adolescents in Canada.

Science.gov (United States)

Azagba, Sunday; Asbridge, Mark

2013-08-01

Smoking susceptibility in early adolescence is strongly predictive of subsequent smoking behavior in youth. As such, smoking susceptibility represents a key modifiable factor in reducing the onset of smoking in young people. A growing literature has documented a number of factors that influence susceptibility to smoking; however, there is limited amount of research examining associations of susceptibility to smoking and school connectedness. The current study examines whether school connectedness has an independent protective effect on smoking susceptibility among younger adolescents. A nationally representative sample of 12,894 Canadian students in grades 6-8 (11-14 years old), surveyed as part of the 2010-2011 Youth Smoking Survey, was analyzed. Multilevel logistic regression models examined unadjusted and adjusted associations between school connectedness and smoking susceptibility. The impacts of other covariates on smoking susceptibility were also explored. Approximately 29% of never-smokers students in grades 6-8 in Canada were susceptible to future smoking. Logistic regression analysis, controlling for standard covariates, found that school connectedness had strong protective effects on smoking susceptibility (odds ratio [OR] 0.91, 95% CI 0.89-0.94). The finding that school connectedness is protective of smoking susceptibility, together with previous research, provides further evidence that improving school conditions that promote school connectedness could reduce risky behavior in adolescents. While prevention efforts should be directed at youth of all ages, particular attention must be paid to younger adolescents in the formative period of 11-14 years of age.

Valence behavior of Eu-ions in intermetallic compound Ce{sub 0.5}Eu{sub 0.5}Pd{sub 3}B{sub 0.5}

Energy Technology Data Exchange (ETDEWEB)

Pandey, Abhishek, E-mail: apandey@ameslab.gov [Experimental Condensed Matter Physics Division, Saha Institute of Nuclear Physics, 1/AF, Bidhannagar, Kolkata 700064 (India); S.N. Bose National Centre for Basic Sciences, Block-JD, Sector-III, Salt Lake, Kolkata 700098 (India); Mazumdar, Chandan, E-mail: chandan.mazumdar@saha.ac.in [S.N. Bose National Centre for Basic Sciences, Block-JD, Sector-III, Salt Lake, Kolkata 700098 (India); Ranganathan, R. [S.N. Bose National Centre for Basic Sciences, Block-JD, Sector-III, Salt Lake, Kolkata 700098 (India); Raghavendra Reddy, V.; Gupta, Ajay [UGC-DAE Consortium for Scientific Research, University Campus, Khandawa Road, Indore (India)

2011-12-15

We have studied the valence behavior of rare-earth ions, in particular Eu-ions, in a cubic intermetallic compound Ce{sub 0.5}Eu{sub 0.5}Pd{sub 3}B{sub 0.5} which is a homogeneous solid solution of two mixed-valent compounds CePd{sub 3} and EuPd{sub 3}B. Results of {sup 151}Eu Moessbauer spectroscopic measurements show that two different valence states, i.e., divalent- and trivalent-like states of Eu-ions exist in the compound. The possible reason for the observed heterogeneous valency vis-a-vis the variation in the chemical environment and the number of nearest-neighbor B atoms surrounding the Eu-ions has been discussed. Our results demonstrate that B incorporation in such Eu-based cubic intermetallic compounds leads to a situation where heterogeneous-valence state of Eu-ions is an energetically favorable ground state. - Highlights: > Intermetallic compound Ce{sub 0.5}Eu{sub 0.5}Pd{sub 3}B{sub 0.5} crystallizes in a single phase. > Eu-ions in Ce{sub 0.5}Eu{sub 0.5}Pd{sub 3}B{sub 0.5} are charge-ordered compared to +2.3 valency in Ce{sub 0.5}Eu{sub 0.5}Pd{sub 3}. > B incorporation makes charge-ordered state of Eu-ions energetically more favorable. > Nearest-neighbor chemical environment affects the Eu valency.

Spin polarization in rare earth intermetallic compounds

International Nuclear Information System (INIS)

Steenwijk, F.J. van

1976-01-01

In this thesis the results of Moessbauer experiments performed on a series of intermetallic compounds of europium and gadolinium are reported. For each of these compounds the magnetic hyperfine field, the electric field gradient at the nuclear site and the isomer shift were determined. For most of the compounds the magnetic ordering temperature was also measured. For some of the europium compounds (e.g. EuAu 5 , EuAg 5 , and EuCu 5 ) it could be derived from the measurements that the easy direction of magnetization falls along the crystallographic c-axis. In a number of compounds (e.g. EuCu 5 , EuZn 5 , EuAu 2 and GdCu 5 ), the various contributions to the magnetic hyperfine field were disentangled by the investigation of suitable pseudobinary compounds that are dilute in Eu. The neighbour contribution Hsub(N) and the paramagnetic Curie temperature thetasub(p) were compared with each other in terms of the RKKY model for EuCu 5 and GdCu 5 . Since the correspondence was found to be poor it was concluded that the magnetic behaviour in these compounds cannot be described by a simple free electron picture as is the basis for the RKKY model

A statistical-thermodynamic model for ordering phenomena in thin film intermetallic structures

International Nuclear Information System (INIS)

Semenova, Olga; Krachler, Regina

2008-01-01

Ordering phenomena in bcc (110) binary thin film intermetallics are studied by a statistical-thermodynamic model. The system is modeled by an Ising approach that includes only nearest-neighbor chemical interactions and is solved in a mean-field approximation. Vacancies and anti-structure atoms are considered on both sublattices. The model describes long-range ordering and simultaneously short-range ordering in the thin film. It is applied to NiAl thin films with B2 structure. Vacancy concentrations, thermodynamic activity profiles and the virtual critical temperature of order-disorder as a function of film composition and thickness are presented. The results point to an important role of vacancies in near-stoichiometric and Ni-rich NiAl thin films

Sodium borohydride hydrolysis in the presence of intermetallic compound LaNi5

International Nuclear Information System (INIS)

Korobov, I.I.; Mozgina, N.G.

1992-01-01

Kinetics of catalytic hydrolysis of sodium borohydride in the 1 mol/l solution of caustic sodium within the range of 298-318 K in presence of LaNi 5 intermetallic compound is studied. It is established that the reaction has zero order by NaBH 4 and the first one by LaNi 5 . The apparent activation energy of NaBH 4 catalytic hydrolysis in presence of LaNi 5 , calculated on the basis of temperature dependence of reaction velocity, is constant within the temperature range under investigation and constitutes 56$+-$1.5 kJ/mol. Recombination of surface hydrogen on LaNi 5 in molecular one is limiting stage determining NaBH 4 hydrolysis rate

Influence of severe plastic deformation on intermetallic particles in Mg-12wt.%Zn alloy investigated using transmission electron microscopy

Czech Academy of Sciences Publication Activity Database

Němec, Martin; Gärtnerová, Viera; Jäger, Aleš

2016-01-01

Roč. 119, Sep (2016), 129-136 ISSN 1044-5803 R&D Projects: GA ČR GBP108/12/G043 Institutional support: RVO:68378271 Keywords : Mg-Zn * severe plastic deformation * equal channel angular pressing * transmission electron microscopy * microstructure * intermetallic particles Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.714, year: 2016

Kinetics of intermetallic phase formation at the interface of Sn-Ag-Cu-X (X = Bi, In) solders with Cu substrate

International Nuclear Information System (INIS)

Hodulova, Erika; Palcut, Marian; Lechovic, Emil; Simekova, Beata; Ulrich, Koloman

2011-01-01

Highlights: → In substitutes Sn in intermetallic compounds formed at the Cu-solder interface. → Bi and In decrease the parabolic rate constant of Cu 3 Sn layer growth. → In increases the parabolic rate constant of Cu 6 Sn 5 layer growth. → High In concentrations should be avoided since they may lead to a pre-mature solder joint degradation. - Abstract: The effects of Bi and In additions on intermetallic phase formation in lead-free solder joints of Sn-3.7Ag-0.7Cu; Sn-1.0Ag-0.5Cu-1.0Bi and Sn-1.5Ag-0.7Cu-9.5In (composition given in weight %) with copper substrate are studied. Soldering of copper plate was conducted at 250 deg. C for 5 s. The joints were subsequently aged at temperatures of 130-170 deg. C for 2-16 days in a convection oven. The aged interfaces were analyzed by optical microscopy and energy dispersive X-ray spectroscopy (EDX) microanalysis. Two intermetallic layers are observed at the interface - Cu 3 Sn and Cu 6 Sn 5 . Cu 6 Sn 5 is formed during soldering. Cu 3 Sn is formed during solid state ageing. Bi and In decrease the growth rate of Cu 3 Sn since they appear to inhibit tin diffusion through the grain boundaries. Furthermore, indium was found to produce a new phase - Cu 6 (Sn,In) 5 instead of Cu 6 Sn 5 , with a higher rate constant. The mechanism of the Cu 6 (Sn,In) 5 layer growth is discussed and the conclusions for the optimal solder chemical composition are presented.

Void formation and its impact on Cu−Sn intermetallic compound formation

Energy Technology Data Exchange (ETDEWEB)

Ross, Glenn, E-mail: Glenn.Ross@aalto.fi; Vuorinen, Vesa; Paulasto-Kröckel, Mervi

2016-08-25

Void formation in the Cu−Sn system has been identified as a major reliability issue with small volume electronic interconnects. Voids form during the interdiffusion of electrochemically deposited Cu and Sn, with varying magnitude and density. Electroplating parameters include the electrolytic chemistry composition and the electroplating current density, all of which appear to effect the voiding characteristics of the Cu−Sn system. In addition, interfacial voiding affects the growth kinetics of the Cu{sub 3}Sn and Cu{sub 6}Sn{sub 5} intermetallic compounds of the Cu−Sn system. The aim here is to present voiding data as a function of electroplating chemistry and current density over a duration (up to 72 h) of isothermal annealing at 423 K (150 °C). Voiding data includes the average interfacial void size and average void density. Voids sizes grew proportionally as a function of thermal annealing time, whereas the void density grew initially very quickly but tended to saturate at a fixed density. A morphological evolution analysis called the physicochemical approach is utilised to understand the processes that occur when a voided Cu/Cu{sub 3}Sn interface causes changes to the IMC phase growth. The method is used to simulate the intermetallic thickness growths' response to interfacial voiding. The Cu/Cu{sub 3}Sn interface acts as a Cu diffusion barrier disrupting the diffusion of Cu. This resulted in a reduction in the Cu{sub 3}Sn thickness and an accelerated growth rate of Cu{sub 6}Sn{sub 5}. - Highlights: • Average void size is proportional linearly to thermal annealing time. • Average void density grows initially very rapidly followed by saturation. • Voids located close to the Cu/Cu{sub 3}Sn interface affect IMC growth rates. • Voids act as a diffusion barrier inhibiting Cu diffusion towards Sn. • Voids located at the interface cause Cu{sub 3}Sn to be consumed by Cu{sub 6}Sn{sub 5}.

Magnetic phase transitions in R2Fe17 compounds under pressure

International Nuclear Information System (INIS)

Arnold, Z.; Kamarad, J.

1994-01-01

The effect of the pressure up to 1.4 GPa on the Curie temperature T c in the R 2 Fe 17 intermetallics with R = Nd, Er and Y was measured using a low field susceptibility technique. The identical character of the temperature dependence of susceptibility χ(T) of the R 2 Fe 17 intermetallics observed at ambient pressure (sharp step-like drop at T c ) is preserved at high pressures only in the case of Nd 2 Fe 17 . Pronounced broadening and splitting of the sharp drop of χ(T) was observed in Er 2 Fe 17 and Y 2 Fe 17 respectively. The initial pressure slopes of dTc/dp are large and negative for all studied compounds, having nearly the same values (dTc/dp = -36K/GPa for Nd 2 Fe 17 compound). The results are discussed from the point of view of the sensitivity of T c on the crystal structure, the number of nearest neighbors of Fe atoms and the possible effect of disordered structures in the R 2 Fe 17 intermetallics

NMR measurements in milled GdCo2 and GdFe2 intermetallic compounds

International Nuclear Information System (INIS)

Tribuzy, C.V.B.; Guimaraes, A.P.; Biondo, A.; Larica, C.; Alves, K.M.B.

1998-12-01

We have used the nuclear magnetic resonance technique to study the magnetic and structural properties of the Gd-Co and Gd-Fe metallic systems, starting with the C15 laves phase intermetallic compounds, and submitting them to a high energy milling process. This leads to the amorphization of the samples, as determined by the X-ray diffraction spectra. For the Gd-Co system the NMR study used the 59 Co nucleus; in the Gd-Fe system, 155,157 Gd and 57 Fe were used. Both systems showed segregation of the pure elements, after a few hours of milling. In the Gd-Co system, a single line, of increasing width, was observed in the 59 Co spectrum. In the Gd-Fe system, the 155 Gd and 157 Gd resonances show three lines, arising from electrical quadrupole interaction. With increasing milling time, the lines broaden, and extra lines appear attributed to a cubic phase of Gd; this interpretation is supported by the X-ray analysis of the samples. The 57 Fe NMR spectrum of this system also informs on the direction of magnetization of the samples in the early stages of milling. From 1 h to 7 h of milling, a spectrum of α-Fe was observed. The study of the NMR line intensity as a function of radio frequency (r.f.) power in Gd Co 2 suggests the existence of regions of the samples with different degrees of disorder. We have observed the persistence of NMR signals from the original intermetallic compounds in the samples with up to 10 h and 7 h of milling, respectively, for Gd Co 2 and Gd Fe 2 . (author)

Magneto-caloric effect in the pseudo-binary intermetallic YPrFe{sub 17} compound

Energy Technology Data Exchange (ETDEWEB)

Alvarez, Pablo [Departamento de Fisica, Universidad de Oviedo, Calvo Sotelo, s/n, 33007 Oviedo (Spain); Gorria, Pedro, E-mail: pgorria@uniovi.es [Departamento de Fisica, Universidad de Oviedo, Calvo Sotelo, s/n, 33007 Oviedo (Spain); Sanchez Llamazares, Jose L. [Division de Materiales Avanzados, Instituto Potosino de Investigacion Cientifica y Tecnologica, Camino a la presa San Jose 2055, CP 78216, San Luis Potosi (Mexico); Perez, Maria J. [Departamento de Fisica, Universidad de Oviedo, Calvo Sotelo, s/n, 33007 Oviedo (Spain); Franco, Victorino [Departamento de Fisica de la Materia Condensada, ICMSE-CSIC, Universidad de Sevilla, P.O. Box 1065, 41080 Sevilla (Spain); Reiffers, Marian; Kovac, Jozef [Institute of Experimental Physics, Watsonova 47, SK-04001 Kosice (Slovakia); Puente-Orench, Ines [Institute Laue Langevin, 6 rue Jules Horowitz, 38042 Grenoble (France); Blanco, Jesus A. [Departamento de Fisica, Universidad de Oviedo, Calvo Sotelo, s/n, 33007 Oviedo (Spain)

2011-12-15

Highlights: Black-Right-Pointing-Pointer YPrFe{sub 17} exhibits a broad {Delta}S{sub M}(T) associated with the ferro-to-paramagnetic phase transition (T{sub C} Almost-Equal-To 290 K). Black-Right-Pointing-Pointer We obtain |{Delta}S{sub M}| Almost-Equal-To 2.3 J kg{sup -1} K{sup -1} and RCP Almost-Equal-To 100 J kg{sup -1}for a magnetic field change of 1.5 T. Black-Right-Pointing-Pointer A single master curve for {Delta}S{sub M} is found when compared with other isostructural R{sub 2}Fe{sub 17} binary alloys. - Abstract: We have synthesized the intermetallic YPrFe{sub 17} compound by arc-melting. X-ray and neutron powder diffraction show that the crystal structure is rhombohedral with R3{sup Macron }m space group (Th{sub 2}Zn{sub 17}-type). The investigated compound exhibits a broad isothermal magnetic entropy change {Delta}S{sub M}(T) associated with the ferro-to-paramagnetic phase transition (T{sub C} Almost-Equal-To 290 K). The |{Delta}S{sub M}| ( Almost-Equal-To 2.3 J kg{sup -1} K{sup -1}) and the relative cooling power ( Almost-Equal-To 100 J kg{sup -1}) have been calculated for applied magnetic field changes up to 1.5 T. A single master curve for {Delta}S{sub M} under different values of the magnetic field change can be obtained by a rescaling of the temperature axis. The results are compared and discussed in terms of the magneto-caloric effect in the isostructural R{sub 2}Fe{sub 17} (R = Y, Pr and Nd) binary intermetallic alloys.

Synthesis of nano intermetallic Nb{sub 3}Sn by mechanical alloying and annealing at low temperature

Energy Technology Data Exchange (ETDEWEB)

López, M., E-mail: marlope@udec.cl [Department of Materials Engineering, Universidad de Concepción, Edmundo Larenas 270, Concepción (Chile); Jiménez, J.A. [Department of Physical Metallurgy, Centro Nacional de Investigaciones Metalúrgicas, C.S.I.C., Av. Gregorio del Amo 8, 28040 Madrid (Spain); Ramam, K.; Mangalaraja, R.V. [Department of Materials Engineering, Universidad de Concepción, Edmundo Larenas 270, Concepción (Chile)

2014-11-05

Highlights: • Intermetallic Nb{sub 3}Sn nano grains were synthesized by powder metallurgy route. • Structure analysis was studied using a multiphase Rietveld refinement fit. • The presence of Nb{sub 3}Sn 86% and NbO 8% was identified. • More tin content in the equilibrium Nb–Sn diagram was obtained. • Magnetic properties show Nb{sub 3}Sn powders are soft super paramagnetic materials. - Abstract: In this study, intermetallic Nb{sub 3}Sn of nanometer-sized grains was synthesized by powder metallurgy route. Elemental powders of Nb and Sn in the stoichiometric proportions were mechanically alloyed for 3 h in a high-energy mill under a protective atmosphere of argon. X-ray diffraction patterns of milled powders confirmed the formation of a Nb(Sn) solid solution evidenced by the presence of Nb peaks only, which are shifted to higher angles. Rietveld refinements used to analyze this XRD pattern indicated a better fit when a tetragonal structure with the space group I4/mmm is used instead the Nb cubic lattice with space group Im−3m. Size-strain analysis from line-broadening of peak profiles by using “double-Voigt” approaches showed that the broadening is due to both a small crystallite size (around 6 nm) and microstrains. Subsequent heat treatment of the Nb(Sn) powder mixture was required for the formation of the Nb{sub 3}Sn ordered phase. X-ray diffraction patterns obtained after a thermal treatment at 700 °C for 1 h were fitted using a multiphase Rietveld refinement. Although the resulting powders are composed mainly by Nb{sub 3}Sn (up to 87 weight%), certain amount of other intermetallic phases like Nb{sub 6}Sn{sub 5}, NbSn{sub 2} and Nb and Sn oxides were also determined. In agreement with the Rietveld refinement analysis, microprobe analysis also revealed that changes in chemical composition at different sites of powder particles are preserved even after annealing at 700 °C. Magnetic properties measured at 300 K on resulted Nb{sub 3}Sn powders

Intermetallic compounds in 3D integrated circuits technology: a brief review.

Science.gov (United States)

Annuar, Syahira; Mahmoodian, Reza; Hamdi, Mohd; Tu, King-Ning

2017-01-01

The high performance and downsizing technology of three-dimensional integrated circuits (3D-ICs) for mobile consumer electronic products have gained much attention in the microelectronics industry. This has been driven by the utilization of chip stacking by through-Si-via and solder microbumps. Pb-free solder microbumps are intended to replace conventional Pb-containing solder joints due to the rising awareness of environmental preservation. The use of low-volume solder microbumps has led to crucial constraints that cause several reliability issues, including excessive intermetallic compounds (IMCs) formation and solder microbump embrittlement due to IMCs growth. This article reviews technologies related to 3D-ICs, IMCs formation mechanisms and reliability issues concerning IMCs with Pb-free solder microbumps. Finally, future outlook on the potential growth of research in this area is discussed.

Intermetallic compounds in 3D integrated circuits technology: a brief review

Science.gov (United States)

Annuar, Syahira; Mahmoodian, Reza; Hamdi, Mohd; Tu, King-Ning

2017-12-01

The high performance and downsizing technology of three-dimensional integrated circuits (3D-ICs) for mobile consumer electronic products have gained much attention in the microelectronics industry. This has been driven by the utilization of chip stacking by through-Si-via and solder microbumps. Pb-free solder microbumps are intended to replace conventional Pb-containing solder joints due to the rising awareness of environmental preservation. The use of low-volume solder microbumps has led to crucial constraints that cause several reliability issues, including excessive intermetallic compounds (IMCs) formation and solder microbump embrittlement due to IMCs growth. This article reviews technologies related to 3D-ICs, IMCs formation mechanisms and reliability issues concerning IMCs with Pb-free solder microbumps. Finally, future outlook on the potential growth of research in this area is discussed.

Advertising literacy and children’s susceptibility to advertising

OpenAIRE

Rozendaal, E.

2011-01-01

This dissertation covers two areas of research that expand our knowledge on children’s advertising literacy (i.e., advertising-related knowledge). The first part addresses the development of children’s advertising literacy into adult-like levels. The second part focuses on the role of advertising literacy in reducing children’s susceptibility to advertising effects. In doing so, this dissertation not only deepens the existing theoretical and empirical insights on children’s advertising litera...

Effect of Co on Si and Fe-containing intermetallic compounds (IMCs) in Al–20Si–5Fe alloys

International Nuclear Information System (INIS)

Fatih Kilicaslan, M.; Yilmaz, Fikret; Hong, Soon-Jik; Uzun, Orhan

2012-01-01

The effects of cobalt addition on microstructure and mechanical properties of Al–20Si–5Fe–XCo (X=0, 1, 3, and 5) alloys were reported in this study. The alloys were produced by both conventional sand casting and melt-spinning at 20 m/s disk velocity. Microstructures of the samples were investigated using X-ray diffractometry (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Vickers micro-hardness tester was used for hardness measurements. Results showed that Co addition can alter morphology of Fe-bearing intermetallic compounds (IMCs) from long rod/needle-like structures to short rod-like ones, and lead to a more homogenous distribution in the microstructure. Addition of 5 wt% Co leads to a decrease in average size of the primary silicon phases in as-cast Al–Si alloys. In melt-spun alloys, with the addition of Co, the microstructure became finer and more homogenously distributed, while thickness of the featureless zone has seen great increase. The optimum Fe to Co ratio was found to be 1 for suppressing the undesirable effect of Fe-bearing acicular/needle-like intermetallic compounds.

Effect of Co on Si and Fe-containing intermetallic compounds (IMCs) in Al-20Si-5Fe alloys

Energy Technology Data Exchange (ETDEWEB)

Fatih Kilicaslan, M. [Department of Physics, Faculty of Art and Science, Kastamonu University, Kastamonu (Turkey); Yilmaz, Fikret [Department of Physics, Faculty of Art and Science, Gaziosmanpasa University, Tokat (Turkey); Hong, Soon-Jik, E-mail: hongsj@kongju.ac.kr [Division of Advanced Materials Engineering, Institute for Rare Metals, Kongju National University, Cheonan 331717 (Korea, Republic of); Uzun, Orhan, E-mail: orhan.uzun@gop.edu.tr [Department of Physics, Faculty of Art and Science, Gaziosmanpasa University, Tokat (Turkey)

2012-10-30

The effects of cobalt addition on microstructure and mechanical properties of Al-20Si-5Fe-XCo (X=0, 1, 3, and 5) alloys were reported in this study. The alloys were produced by both conventional sand casting and melt-spinning at 20 m/s disk velocity. Microstructures of the samples were investigated using X-ray diffractometry (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Vickers micro-hardness tester was used for hardness measurements. Results showed that Co addition can alter morphology of Fe-bearing intermetallic compounds (IMCs) from long rod/needle-like structures to short rod-like ones, and lead to a more homogenous distribution in the microstructure. Addition of 5 wt% Co leads to a decrease in average size of the primary silicon phases in as-cast Al-Si alloys. In melt-spun alloys, with the addition of Co, the microstructure became finer and more homogenously distributed, while thickness of the featureless zone has seen great increase. The optimum Fe to Co ratio was found to be 1 for suppressing the undesirable effect of Fe-bearing acicular/needle-like intermetallic compounds.

Surface improvement and biocompatibility of TiAl{sub 24}Nb{sub 10} intermetallic alloy using rf plasma nitriding

Energy Technology Data Exchange (ETDEWEB)

Abd El-Rahman, A.M. [Physics Department, Faculty of Science, Sohag University (Egypt)], E-mail: ahmedphys96@hotmail.com; Maitz, M.F. [Institut fuer Ionenstrahlphysik und Materialforschung, Forschungszentrum Dresden Rossendorf (Germany); Kassem, M.A. [Department of Materials and Metals Engineering, Faculty of Petroleum and Mining Engineering, Suez Canal University (Egypt); El-Hossary, F.M. [Physics Department, Faculty of Science, Sohag University (Egypt); Prokert, F.; Reuther, H.; Pham, M.T.; Richter, E. [Institut fuer Ionenstrahlphysik und Materialforschung, Forschungszentrum Dresden Rossendorf (Germany)

2007-09-30

The present work describes the surface improvement and biocompatibility of TiAl{sub 24}Nb{sub 10} intermetallic alloy using rf plasma nitriding. The nitriding process was carried out at different plasma power from 400 W to 650 W where the other plasma conditions were fixed. Grazing incidence X-ray diffractometry (GIXRD), Auger electron spectroscopy (AES), tribometer and a nanohardness tester were employed to characterize the nitrided layer. Further potentiodynamic polarization method was used to describe the corrosion behavior of the un-nitrided and nitrided alloy. It has been found that the Vickers hardness (HV) and corrosion resistance values of the nitrided layers increase with increasing plasma power while the wear rates of the nitrided layers reduce by two orders of magnitude as compared to those of the un-nitrided layer. This improvement in surface properties of the intermetallic alloy is due to formation of a thin modified layer which is composed of titanium nitride in the alloy surface. Moreover, all modified layers were tested for their sustainability as a biocompatible material. Concerning the application area of biocompatibility, the present treated alloy show good surface properties especially for the nitrided alloy at low plasma power of 400 W.

The formation of intermetallic compounds during interdiffusion of Mg–Al/Mg–Ce diffusion couples

International Nuclear Information System (INIS)

Dai, Jiahong; Jiang, Bin; Li, Xin; Yang, Qingshan; Dong, Hanwu; Xia, Xiangsheng; Pan, Fusheng

2015-01-01

Graphical abstract: Al–Ce intermetallic compounds (IMCs) formed in Mg–Al/Mg–Ce diffusion couples. During the whole diffusion process, Al was the dominant diffusing species, and it substituted for Mg atoms of the Mg–Ce substrate. Five Al–Ce IMCs of Al 4 Ce, Al 11 Ce 3 , Al 3 Ce, Al 2 Ce, and AlCe were formed via the reaction of Al and Ce. - Highlights: • Al–Ce IMCs formation in the Mg–Al/Mg–Ce diffusion couples was studied. • Formation of Al 4 Ce as the first phase was rationalized using the Gibbs free energy. • The activation energy for the growth of the diffusion reaction zones was 36.6 kJ/mol. - Abstract: The formation of Al–Ce intermetallic compounds (IMCs) during interdiffusion of Mg–Al/Mg–Ce diffusion couples prepared by solid–liquid contact method was investigated at 623 K, 648 K and 673 K for 24 h, 48 h and 72 h, respectively. During the whole diffusion process, Al was the dominant diffusing species, and it substituted for Mg of the Mg–Ce substrate. Five Al–Ce IMCs of Al 4 Ce, Al 11 Ce 3 , Al 3 Ce, Al 2 Ce and AlCe were formed via the reaction of Al and Ce. The formation of Al 4 Ce as the first kind of IMC was rationalized on the basis of an effective Gibbs free energy model. The activation energy for the growth of the total diffusion reaction layer was 36.6 kJ/mol

Susceptibility-Weighted Imaging and Quantitative Susceptibility Mapping in the Brain

Science.gov (United States)

Liu, Chunlei; Li, Wei; Tong, Karen A.; Yeom, Kristen W.; Kuzminski, Samuel

2015-01-01

Susceptibility-weighted imaging (SWI) is a magnetic resonance imaging (MRI) technique that enhances image contrast by using the susceptibility differences between tissues. It is created by combining both magnitude and phase in the gradient echo data. SWI is sensitive to both paramagnetic and diamagnetic substances which generate different phase shift in MRI data. SWI images can be displayed as a minimum intensity projection that provides high resolution delineation of the cerebral venous architecture, a feature that is not available in other MRI techniques. As such, SWI has been widely applied to diagnose various venous abnormalities. SWI is especially sensitive to deoxygenated blood and intracranial mineral deposition and, for that reason, has been applied to image various pathologies including intracranial hemorrhage, traumatic brain injury, stroke, neoplasm, and multiple sclerosis. SWI, however, does not provide quantitative measures of magnetic susceptibility. This limitation is currently being addressed with the development of quantitative susceptibility mapping (QSM) and susceptibility tensor imaging (STI). While QSM treats susceptibility as isotropic, STI treats susceptibility as generally anisotropic characterized by a tensor quantity. This article reviews the basic principles of SWI, its clinical and research applications, the mechanisms governing brain susceptibility properties, and its practical implementation, with a focus on brain imaging. PMID:25270052

Susceptibility-weighted imaging and quantitative susceptibility mapping in the brain.

Science.gov (United States)

Liu, Chunlei; Li, Wei; Tong, Karen A; Yeom, Kristen W; Kuzminski, Samuel

2015-07-01

Susceptibility-weighted imaging (SWI) is a magnetic resonance imaging (MRI) technique that enhances image contrast by using the susceptibility differences between tissues. It is created by combining both magnitude and phase in the gradient echo data. SWI is sensitive to both paramagnetic and diamagnetic substances which generate different phase shift in MRI data. SWI images can be displayed as a minimum intensity projection that provides high resolution delineation of the cerebral venous architecture, a feature that is not available in other MRI techniques. As such, SWI has been widely applied to diagnose various venous abnormalities. SWI is especially sensitive to deoxygenated blood and intracranial mineral deposition and, for that reason, has been applied to image various pathologies including intracranial hemorrhage, traumatic brain injury, stroke, neoplasm, and multiple sclerosis. SWI, however, does not provide quantitative measures of magnetic susceptibility. This limitation is currently being addressed with the development of quantitative susceptibility mapping (QSM) and susceptibility tensor imaging (STI). While QSM treats susceptibility as isotropic, STI treats susceptibility as generally anisotropic characterized by a tensor quantity. This article reviews the basic principles of SWI, its clinical and research applications, the mechanisms governing brain susceptibility properties, and its practical implementation, with a focus on brain imaging. © 2014 Wiley Periodicals, Inc.

Microstructural and Material Quality Effects on Rolling Contact Fatigue of Highly Elastic Intermetallic Ball Bearings

Science.gov (United States)

DellaCorte, Christopher; Howard, S. Adam; Thomas, Fransua; Stanford, Malcolm K.

2016-01-01

Rolling element bearings made from highly-elastic intermetallic materials (HIM)s, such as 60NiTi, are under development for applications that require superior corrosion and shock resistance. Compared to steel, intermetallics have been shown to have much lower rolling contact fatigue (RCF) stress capability in simplified 3-ball on rod (ASTM STP 771) fatigue tests. In the 3-ball tests, poor material quality and microstructural flaws negatively affect fatigue life but such relationships have not been established for full-scale 60NiTi bearings. In this paper, 3-ball-on-rod fatigue behavior of two quality grades of 60NiTi are compared to the fatigue life of full-scale 50mm bore ball bearings made from the same materials. 60NiTi RCF rods with material or microstructural flaws suffered from infant mortality failures at all tested stress levels while high quality 60NiTi rods exhibited no failures at lower stress levels. Similarly, tests of full-scale bearings made from flawed materials exhibited early surface fatigue and through crack type failures while bearings made from high quality material did not fail even in long-term tests. Though the full-scale bearing test data is yet preliminary, the results suggest that the simplified RCF test is a good qualitative predictor of bearing performance. These results provide guidance for materials development and to establish minimum quality levels required for successful bearing operation and life.

Effects of metallic nanoparticle doped flux on the interfacial intermetallic compounds between lead-free solder ball and copper substrate

International Nuclear Information System (INIS)

Sujan, G.K.; Haseeb, A.S.M.A.; Afifi, A.B.M.

2014-01-01

Lead free solders currently in use are prone to develop thick interfacial intermetallic compound layers with rough morphology which are detrimental to the long term solder joint reliability. A novel method has been developed to control the morphology and growth of intermetallic compound layers between lead-free Sn–3.0Ag–0.5Cu solder ball and copper substrate by doping a water soluble flux with metallic nanoparticles. Four types of metallic nanoparticles (nickel, cobalt, molybdenum and titanium) were used to investigate their effects on the wetting behavior and interfacial microstructural evaluations after reflow. Nanoparticles were dispersed manually with a water soluble flux and the resulting nanoparticle doped flux was placed on copper substrate. Lead-free Sn–3.0Ag–0.5Cu solder balls of diameter 0.45 mm were placed on top of the flux and were reflowed at a peak temperature of 240 °C for 45 s. Angle of contact, wetting area and interfacial microstructure were studied by optical microscopy, field emission scanning electron microscopy and energy-dispersive X-ray spectroscopy. It was observed that the angle of contact increased and wetting area decreased with the addition of cobalt, molybdenum and titanium nanoparticles to flux. On the other hand, wettability improved with the addition of nickel nanoparticles. Cross-sectional micrographs revealed that both nickel and cobalt nanoparticle doping transformed the morphology of Cu 6 Sn 5 from a typical scallop type to a planer one and reduced the intermetallic compound thickness under optimum condition. These effects were suggested to be related to in-situ interfacial alloying at the interface during reflow. The minimum amount of nanoparticles required to produce the planer morphology was found to be 0.1 wt.% for both nickel and cobalt. Molybdenum and titanium nanoparticles neither appear to undergo alloying during reflow nor have any influence at the solder/substrate interfacial reaction. Thus, doping of flux

Effects of metallic nanoparticle doped flux on the interfacial intermetallic compounds between lead-free solder ball and copper substrate

Energy Technology Data Exchange (ETDEWEB)

Sujan, G.K., E-mail: sgkumer@gmail.com; Haseeb, A.S.M.A., E-mail: haseeb@um.edu.my; Afifi, A.B.M., E-mail: amalina@um.edu.my

2014-11-15

Lead free solders currently in use are prone to develop thick interfacial intermetallic compound layers with rough morphology which are detrimental to the long term solder joint reliability. A novel method has been developed to control the morphology and growth of intermetallic compound layers between lead-free Sn–3.0Ag–0.5Cu solder ball and copper substrate by doping a water soluble flux with metallic nanoparticles. Four types of metallic nanoparticles (nickel, cobalt, molybdenum and titanium) were used to investigate their effects on the wetting behavior and interfacial microstructural evaluations after reflow. Nanoparticles were dispersed manually with a water soluble flux and the resulting nanoparticle doped flux was placed on copper substrate. Lead-free Sn–3.0Ag–0.5Cu solder balls of diameter 0.45 mm were placed on top of the flux and were reflowed at a peak temperature of 240 °C for 45 s. Angle of contact, wetting area and interfacial microstructure were studied by optical microscopy, field emission scanning electron microscopy and energy-dispersive X-ray spectroscopy. It was observed that the angle of contact increased and wetting area decreased with the addition of cobalt, molybdenum and titanium nanoparticles to flux. On the other hand, wettability improved with the addition of nickel nanoparticles. Cross-sectional micrographs revealed that both nickel and cobalt nanoparticle doping transformed the morphology of Cu{sub 6}Sn{sub 5} from a typical scallop type to a planer one and reduced the intermetallic compound thickness under optimum condition. These effects were suggested to be related to in-situ interfacial alloying at the interface during reflow. The minimum amount of nanoparticles required to produce the planer morphology was found to be 0.1 wt.% for both nickel and cobalt. Molybdenum and titanium nanoparticles neither appear to undergo alloying during reflow nor have any influence at the solder/substrate interfacial reaction. Thus, doping

Investigation of odd-order nonlinear susceptibilities in atomic vapors

Energy Technology Data Exchange (ETDEWEB)

Yan, Yaqi [Key Laboratory for Physical Electronics and Devices of the Ministry of Education, Xi’an Jiaotong University, Xi’an 710049 (China); Shaanxi Key Laboratory of Information Photonic Technique, Xi’an Jiaotong University, Xi’an 710049 (China); Teaching and Research Section of Maths and Physics, Guangzhou Commanding Academy of Chinese People’s Armed Police Force, Guangzhou, 510440 (China); Wu, Zhenkun; Si, Jinhai; Yan, Lihe; Zhang, Yiqi; Yuan, Chenzhi; Sun, Jia [Key Laboratory for Physical Electronics and Devices of the Ministry of Education, Xi’an Jiaotong University, Xi’an 710049 (China); Shaanxi Key Laboratory of Information Photonic Technique, Xi’an Jiaotong University, Xi’an 710049 (China); Zhang, Yanpeng, E-mail: ypzhang@mail.xjtu.edu.cn [Key Laboratory for Physical Electronics and Devices of the Ministry of Education, Xi’an Jiaotong University, Xi’an 710049 (China); Shaanxi Key Laboratory of Information Photonic Technique, Xi’an Jiaotong University, Xi’an 710049 (China)

2013-06-15

We theoretically deduce the macroscopic symmetry constraints for arbitrary odd-order nonlinear susceptibilities in homogeneous media including atomic vapors for the first time. After theoretically calculating the expressions using a semiclassical method, we demonstrate that the expressions for third- and fifth-order nonlinear susceptibilities for undressed and dressed four- and six-wave mixing (FWM and SWM) in atomic vapors satisfy the macroscopic symmetry constraints. We experimentally demonstrate consistence between the macroscopic symmetry constraints and the semiclassical expressions for atomic vapors by observing polarization control of FWM and SWM processes. The experimental results are in reasonable agreement with our theoretical calculations. -- Highlights: •The macroscopic symmetry constraints are deduced for homogeneous media including atomic vapors. •We demonstrate that odd-order nonlinear susceptibilities satisfy the constraints. •We experimentally demonstrate the deduction in part.

Analysis of significance of environmental factors in landslide susceptibility modeling: Case study Jemma drainage network, Ethiopia

Directory of Open Access Journals (Sweden)

Vít Maca

2017-06-01

Full Text Available Aim of the paper is to describe methodology for calculating significance of environmental factors in landslide susceptibility modeling and present result of selected one. As a study area part of a Jemma basin in Ethiopian Highland is used. This locality is highly affected by mass movement processes. In the first part all major factors and their influence are described briefly. Majority of the work focuses on research of other methodologies used in susceptibility models and design of own methodology. This method is unlike most of the methods used completely objective, therefore it is not possible to intervene in the results. In article all inputs and outputs of the method are described as well as all stages of calculations. Results are illustrated on specific examples. In study area most important factor for landslide susceptibility is slope, on the other hand least important is land cover. At the end of article landslide susceptibility map is created. Part of the article is discussion of results and possible improvements of the methodology.

Process for the manufacture of a superconductor with an intermetallic compound

International Nuclear Information System (INIS)

Wilhelm, M.

1980-01-01

A superconductor with a superconducting intermetallic compound consisting of at least two elements can be manufactured by producing a conductor preproduct with a first component containing one element of the compound and a second component consisting of a carrier metal and the remaining element or elements of the alloy containing the compound, and by heat treating the conductor preproduct, so that the compound is formed by the reaction of the element of the first compound with the remaining element or elements of the second compound. In such a superconductor, one tries to increase the effective current density and critical current. The invention states that the heat treatment should be carried out in a hydrogen atmosphere. Superconductors produced by this process can be used for superconductor devices whose magnetic fields have a flux density above 10 Tesla. (orig.) [de

Effects of Nb content on the Zr2Fe intermetallic stability

International Nuclear Information System (INIS)

Ramos, C.; Saragovi, C.; Granovsky, M.; Arias, D.

2003-01-01

With the aim of studying the stability range of the Zr 2 Fe intermetallic when adding Nb, the range of existence of the cubic ternary phase (λ 1 ) and the corresponding two-phase field between them, four samples were analyzed, each one containing 35 at.% Fe and different at.% Nb: 0.5, 4 10 and 15. Optical and scanning electron metallographies, X-ray diffraction, microprobe analysis and Moessbauer spectroscopy were performed to determine and characterize the phases present in the samples. Results show that the Zr 2 Fe compound accepts up to nearly 0.5 at.% Nb in solution, since the Zr 2 Fe+λ 1 region is stable in the (0.5-3.5) at.% Nb range. To summarize these results an 800 deg. C section of the ternary Zr-Nb-Fe diagram, in the studied zone, was proposed

Contribution to the study of magnetic properties of rare-earth iron intermetallic compounds

International Nuclear Information System (INIS)

Morariu, M.

1976-01-01

The intermetallic binary compounds Ysub(x)Fesub(y)(YFe 2 ,YFe 3 ,Y 6 Fe 23 ,Y 2 Fe 17 ), RFe 2 (R=Gd,Tb,Dy,Ho,Er and Tm) and the intermetallic pseudobinary compounds (Gdsub(x)Ysub(1-x))Fe 2 and Dy(Fesub(x)Nisub(1-x)) 3 were studied, using magnetic measurements and Moessbauer spectroscopy, in order to obtain information on their magnetic behaviour. The different models which describe magnetic interactions in rare-earths with 3d transition element compounds are reviewed. The magnetic hyperfine field Hsub(n) at the Fe 57 nucleus, measured by Moessbauer spectroscopy, depends on the atom position in the lattice, being sensitive to magnetic interactions with neighbouring atoms. The mean value of the magnetic hyperfine field, average Hsub(n) is proportional to the mean magnetic moment of the iron atom: average Hsub(n)/average μsub(Fe) approximately 150 kOe. The comparative study of the temperature dependence of average Hsub(n) and average μsub(Fe) values shows that this relation is valid for the whole range of magnetic ordering (T>Tsub(c)). The mean magnetic hyperfine fields at the Fe 57 nucleus in RFe 2 compounds depend on the rare-earth partner and vary approximative linearly with the Gennes factor. The spin reorientation diagram for the (Gdsub(x)Ysub(1-x))Fe 2 system is obtained. All results on Moessbauer spectroscopy are in good agreement with the magnetic measurements. The magnetic behaviour of iron atoms is justified using a model in which the most electrons are in a narrow band, so they could be considered localized, and the magnetic interactions between these atoms take place through a fraction (<5%) of 3d itinerant electrons. (author)

The possibility of the mixed valence state in the uranium intermetallic compounds: UCoGa5, U2Ru2Sn and U2RuGa8

International Nuclear Information System (INIS)

Troc, Robert

2007-01-01

The mixed valence (MV) phenomenon has been observed so far in a large number of various compounds but containing only lanthanides. These properties are usually associated with the mixing of the localised f-state and the band states. The usual valence state for magnetic uranium intermetallics is the trivalent state 5f 3 or hybridised 5f 2 6d 1 , both are nearly degenerate in energy and can compete for a stability of the compound. In some cases a gain in an energy minimum may be achieved by very fast fluctuating between these two states with a time of 10 -14 s, which does not allow to yield the ordered state even if the exchange interactions (favourite the U-U distances) would be able for that. The latter cases seem to concern the described here intermetallics: one ternary compound based on Co, UCoGa 5 , and the two uranium ternary compounds based on Ru, namely U 2 Ru 2 Sn and U 2 RuGa 8 which all crystallize in a tetragonal unit cell. All these compounds show a maximum in their temperature dependences of the magnetic susceptibility measured along and perpendicular to the c-axis. Such a behaviour, which is reminiscent of a number of Ce (Sm, Eu) and Yb compounds for which χ(T) has in the past been considered by Sales and Wohlleben (SW) by applying their ICF model or by Lawrance et al. following their scaling procedure. It turned out that these phenomenological models can also be applied to the considered here two Ru-based uranium ternaries from which some reliable energy parameters could be found. In order to further support the mixing valence scenario for the first such cases in uranium compounds presented here, the transport and thermodynamic properties are also discussed. However, some of the most important results confirming the MV state, e.g., in U 2 RuGa 8 , has recently been achieved from the inelastic neutron scattering performed in the Rutherford Appleton Laboratory on the ISIS facility. From these measurements a characteristic gap of 60 meV has been

Effect of Si on Fe-rich intermetallic formation and mechanical properties of heat-treated Al–Cu–Mn–Fe alloys

Science.gov (United States)

Zhao, Yuliang; Zhang, Weiwen; Yang, Chao; Zhang, Datong; Wang, Zhi

2018-04-01

The effect of Si on Fe-rich intermetallics formation and mechanical properties of heat-treated squeeze cast Al-5.0Cu-0.6Mn-0.7Fe alloy was investigated. Our results show that increasing Si content promotes the formation of Al15(FeMn)3(SiCu)2 (${\\alpha}$-Fe), and varying the morphology of T (Al20Cu3Mn2) where the size decreases and the amount increases. The major reason is that Si promotes heterogeneous nucleation of the intermetallics leading to finer precipitates. Si addition significantly enhances ultimate tensile strength and yield strength of the alloys. The strengthening effect is mainly owing to the dispersoid strengthening by increasing volume fraction of T phase and less harmful ${\\alpha}$-Fe with a compact structure, which make the cracks more difficult to initiate and propagation during tensile test. The squeeze cast Al-5.0Cu-0.6Mn-0.7Fe alloy with 1.1% Si shows significantly improved mechanical properties than the alloy without Si addition, which has tensile strength of 386 MPa, yield strength of 280 MPa and elongation of 8.6%.

X-ray nano-diffraction study of Sr intermetallic phase during solidification of Al-Si hypoeutectic alloy

Energy Technology Data Exchange (ETDEWEB)

Manickaraj, Jeyakumar; Gorny, Anton; Shankar, Sumanth, E-mail: shankar@mcmaster.ca [Light Metal Casting Research Centre (LMCRC), Department of Mechanical Engineering, McMaster University, 1280 Main Street W, Hamilton, Ontario L8S 4L7 (Canada); Cai, Zhonghou [Advanced Photon Source, Argonne National Laboratory, 9700 South Cass Avenue, Argonne, Illinois 60439 (United States)

2014-02-17

The evolution of strontium (Sr) containing intermetallic phase in the eutectic reaction of Sr-modified Al-Si hypoeutectic alloy was studied with high energy synchrotron beam source for nano-diffraction experiments and x-ray fluorescence elemental mapping. Contrary to popular belief, Sr does not seem to interfere with the Twin Plane Re-entrant Edge (TPRE) growth mechanism of eutectic Si, but evolves as the Al{sub 2}Si{sub 2}Sr phase during the eutectic reaction at the boundary between the eutectic Si and Al grains.

The influence of interparticle correlations and self-assembly on the dynamic initial magnetic susceptibility spectra of ferrofluids

International Nuclear Information System (INIS)

Ivanov, A.O.; Kantorovich, S.S.; Elfimova, E.A.; Zverev, V.S.; Sindt, J.O.; Camp, P.J.

2017-01-01

Using computer simulations and a mean-field theoretical approach, we study how the growth in dipolar interparticle correlations manifests itself in the frequency-dependent initial magnetic susceptibility of a ferrofluid. Our recently developed theory gives the correct single-particle Debye-theory results in the low-concentration, non-interacting regime; and it yields the exact leading-order contributions from interparticle correlations. The susceptibility spectra are analysed in terms of the low-frequency behaviours of the real and imaginary parts, and the position of the peak in the imaginary part. By comparing the theoretical predictions to the results from Brownian dynamics simulations, it is possible to identify the conditions where correlations are important, but where self-assembly has not developed. We also provide a qualitative explanation for the behaviour of spectra beyond the mean-field limit. - Highlights: • The interparticle interaction influences the dynamic susceptibility spectra of magnetic fluids. • The imaginary part maximum shifts to lower frequencies due to the dipolar interparticle interaction. • Chain formation should influence the susceptibility spectrum by shifting the absorption peak to lower frequencies.

The influence of interparticle correlations and self-assembly on the dynamic initial magnetic susceptibility spectra of ferrofluids

Energy Technology Data Exchange (ETDEWEB)

Ivanov, A.O., E-mail: alexey.ivanov@urfu.ru [Institute of Mathematics and Computer Sciences, Ural Federal University, Lenin Avenue 51, 620000 Ekaterinburg (Russian Federation); Kantorovich, S.S. [Institute of Mathematics and Computer Sciences, Ural Federal University, Lenin Avenue 51, 620000 Ekaterinburg (Russian Federation); Faculty of Physics, University of Vienna, Sensengasse 8, 1090 Vienna (Austria); Elfimova, E.A.; Zverev, V.S. [Institute of Mathematics and Computer Sciences, Ural Federal University, Lenin Avenue 51, 620000 Ekaterinburg (Russian Federation); Sindt, J.O. [School of Chemistry, University of Edinburgh, David Brewster Road, Edinburgh EH9 3FJ, Scotland (United Kingdom); Camp, P.J. [Institute of Mathematics and Computer Sciences, Ural Federal University, Lenin Avenue 51, 620000 Ekaterinburg (Russian Federation); School of Chemistry, University of Edinburgh, David Brewster Road, Edinburgh EH9 3FJ, Scotland (United Kingdom)

2017-06-01

Using computer simulations and a mean-field theoretical approach, we study how the growth in dipolar interparticle correlations manifests itself in the frequency-dependent initial magnetic susceptibility of a ferrofluid. Our recently developed theory gives the correct single-particle Debye-theory results in the low-concentration, non-interacting regime; and it yields the exact leading-order contributions from interparticle correlations. The susceptibility spectra are analysed in terms of the low-frequency behaviours of the real and imaginary parts, and the position of the peak in the imaginary part. By comparing the theoretical predictions to the results from Brownian dynamics simulations, it is possible to identify the conditions where correlations are important, but where self-assembly has not developed. We also provide a qualitative explanation for the behaviour of spectra beyond the mean-field limit. - Highlights: • The interparticle interaction influences the dynamic susceptibility spectra of magnetic fluids. • The imaginary part maximum shifts to lower frequencies due to the dipolar interparticle interaction. • Chain formation should influence the susceptibility spectrum by shifting the absorption peak to lower frequencies.

New ternary intermetallics, based magnesium, for hydrogen storage

International Nuclear Information System (INIS)

Roquefere, J.G.

2009-05-01

The use of fossil fuels (non-renewable energy) is responsible for increasing the concentration of greenhouse gases in the atmosphere. Among the considered alternatives, hydrogen is seen as the most attractive energy vector. The storage in intermetallics makes it possible to obtain mass and volume capacities (e.g. 140 g/L) higher than those obtained by liquid form or under pressure (respectively 71 and 40 g/L). We have synthesised Mg and Rare Earth based compounds (RE = Y, Ce and Gd), derived from the cubic Laves phases AB2. Their physical and chemical properties have been studied (hydrogenation, electrochemistry, magnetism,...). The conditions of sorption (P and T) are particularly favorable (i.e. absorption at room temperature and atmospheric pressure). Besides, to improve the sorption kinetics of metallic magnesium, the compounds developed previously were used as catalysts. Thus, GdMgNi4 was milled with magnesium and the speeds of absorption and desorption of the mixture are found higher than those obtained for the composites Mg+Ni or Mg+V, which are reference systems. A theoretical approach (DFT) was used to model the electronic structure of the ternary compounds (i.e. REMgNi4) and thus to predict or confirm the experimental results. (authors)

Hydrogen-Induced Phase Transformation and Microstructure Evolution for Ti-6Al-4V Parts Produced by Electron Beam Melting

Directory of Open Access Journals (Sweden)

Natalia Pushilina

2018-04-01

Full Text Available In this paper, phase transitions and microstructure evolution in titanium Ti-6Al-4V alloy parts produced by electron beam melting (EBM under hydrogenation was investigated. Hydrogenation was carried out at the temperature of 650 °C to the absolute hydrogen concentrations in the samples of 0.29, 0.58, and 0.90 wt. %. Comparative analysis of microstructure changes in Ti-6Al-4V alloy parts was performed using scanning electron microscopy (SEM, transmission electron microscopy (TEM, and X-ray diffraction (XRD. Furthermore, in-situ XRD was used to investigate the phase transitions in the samples during hydrogenation. The structure of Ti-6Al-4V parts produced by EBM is represented by the α phase plates with the transverse length of 0.2 μm, the β phase both in the form of plates and globular grains, and metastable α″ and ω phases. Hydrogenation to the concentration of 0.29 wt. % leads to the formation of intermetallic Ti3Al phase. The dimensions of intermetallic Ti3Al plates and their volume fraction increase significantly with hydrogen concentration up to 0.58 wt. % along with precipitation of nano-sized crystals of titanium δ hydrides. Individual Ti3Al plates decay into nanocrystals with increasing hydrogen concentration up to 0.9 wt. % accompanied by the increase of proportion and size of hydride plates. Hardness of EBM Ti-6Al-4V alloy decreases with hydrogen content.

Preparation, microstructural evolution and properties of Ni–Zr intermetallic/Zr–Si ceramic reinforced composite coatings on zirconium alloy by laser cladding

Energy Technology Data Exchange (ETDEWEB)

Liu, Kun; Li, Yajiang, E-mail: yajli@sdu.edu.cn; Wang, Juan; Ma, Qunshuang; Li, Jishuai; Li, Xinyue

2015-10-25

NiZr{sub 2}–ZrSi–Zr{sub 5}(Si{sub x}Ni{sub 1−x}){sub 4}-ZrC intermetallic/ceramic reinforced composite coatings were in situ synthesized by laser cladding the pre-placed Ni–Cr–B–Si powder on zirconium substrate. Microstructure and phase constituents were investigated by X-ray diffraction (XRD), optical microscope (OM), scanning electron microscope (SEM) and energy dispersive spectroscopy (EDS). Microhardness tester and block-on-ring wear tester were employed to measure the hardness distribution and wear resistance of the intermetallic/ceramic reinforced composite coating. Results indicated that the multiphase of reinforcements includes Ni–Zr intermetallic compounds (e.g., NiZr and NiZr{sub 2}) and Zr–Si(C) ceramic phases (e.g., ZiSi, Zr{sub 5}Si{sub 4} and ZrC). Ni–Si clusters transforming to Zr–Si–Ni clusters at high temperature facilitated the forming of Zr{sub 5}(Si{sub x}Ni{sub 1−x}){sub 4} and during the growth of Zr{sub 5}(Si{sub x}Ni{sub 1−x}){sub 4}, the consumption of Zr atoms at the lateral interface of liquid/Zr{sub 5}(Si{sub x}Ni{sub 1−x}){sub 4} resulted into developing Zr-poor zone near Zr{sub 5}(Si{sub x}Ni{sub 1−x}){sub 4}. The microhardness and wear resistance of the coating were significantly improved by various reinforced phases in comparison to zirconium substrate. - Highlights: • NiZr{sub 2}–ZrSi–Zr{sub 5}(Si{sub x}Ni{sub 1−x}){sub 4}-ZrC compostie coating was in-situ synthesized. • Ni–Si clusters transforming resulted into developing Zr-poor zone near Zr{sub 5}(Si{sub x}Ni{sub 1−x}){sub 4}. • Reinforced phases significantly improve wear resistance of the coating.

Influence of severe plastic deformation on intermetallic particles in Mg-12 wt.%Zn alloy investigated using transmission electron microscopy

International Nuclear Information System (INIS)

Němec, M.; Gärtnerová, V.; Jäger, A.

2016-01-01

The in-depth microstructural characterization of intermetallic particles in an Mg-12 wt.%Zn binary alloy subjected to a severe plastic deformation is presented. The alloy was processed by four passes via equal channel angular pressing with an applied back pressure at a gradually decreasing temperature and analyzed using transmission electron microscopy techniques to observe the influence of processing on intermetallic particles. The results are compared with the initial state of the material prior to severe plastic deformation. The microstructural evolution of the α-Mg matrix and the Mg 21 Zn 25 , Mg 51 Zn 20 and MgZn 2 was analyzed using bright field imaging, selected area electron diffraction, high-resolution transmission electron microscopy and high-angle annular dark field imaging in scanning mode. The plastic deformation process influenced the α-Mg matrix and each type of intermetallic particle. The α-Mg matrix consisted of two types of areas. The first type of area had a highly deformed structure, and the second type of area had a partially recrystallized structure with an average grain size of approximately 250 nm. The Mg 21 Zn 25 microparticles exhibited distinct forms in the α-Mg matrix that were characterized as a single-crystalline form, a nano-crystalline form and a broken up form. No evidence of Mg 51 Zn 20 nanoparticles within the α-Mg matrix was found in the microstructure, which indicates their dissolution or phase transformation during the deformation process. MgZn 2 nanoparticles exhibited different behavior in both types of α-Mg matrix. Two orientation relationships toward the highly deformed α-Mg matrix were observed; however, there was no relationship toward the partially recrystallized α-Mg matrix. Additionally, the growth of the MgZn 2 nanoparticles was different in the two types of α-Mg matrix. The Mg 51 Zn 20 nanoparticles inside Mg 21 Zn 25 microparticles exhibited a distinct behavior within the single-crystalline or nano

Stereo and scanning electron microscopy of in-shell Brazil nut (Bertholletia excelsa H.B.K.): part two-surface sound nut fungi spoilage susceptibility.

Science.gov (United States)

Scussel, Vildes M; Manfio, Daniel; Savi, Geovana D; Moecke, Elisa H S

2014-11-01

This work reports the in-shell Brazil nut spoilage susceptible morpho-histological characteristics and fungi infection (shell, edible part, and brown skin) through stereo and scanning electron microscopies (SEM). The following characteristics related to shell (a) morphology-that allow fungi and insects' entrance to inner nut, and (b) histology-that allow humidity absorption, improving environment conditions for living organisms development, were identified. (a.1) locule in testae-the nut navel, which is a cavity formed during nut detaching from pods (located at 1.0 to 2.0/4th of the shell B&C nut faces linkage). It allows the nut brown skin (between shell and edible part) first contact to the external environment, through the (a.2) nut channel-the locule prolongation path, which has the water/nutrients cambium function for their transport and distribution to the inner seed (while still on the tree/pod). Both, locule followed by the channel, are the main natural entrance of living organisms (fungi and insects), including moisture to the inner seed structures. In addition, the (a.3) nut shell surface-which has a crinkled and uneven surface morphology-allows water absorption, thus adding to the deterioration processes too. The main shell histological characteristic, which also allows water absorption (thus improving environment conditions for fungi proliferation), is the (b.1) cell wall porosity-the multilayered wall and porous rich cells that compose the shell faces double tissue layers and the (b.2) soft tissue-the mix of tissues 2 faces corner/linkage. This work also shows in details the SEM nut spoilage susceptible features highly fungi infected with hyphae and reproductive structures distribution. © 2014 Institute of Food Technologists®

Assessing rockfall susceptibility in steep and overhanging slopes using three-dimensional analysis of failure mechanisms

Science.gov (United States)

Matasci, Battista; Stock, Greg M.; Jaboyedoff, Michael; Carrea, Dario; Collins, Brian D.; Guérin, Antoine; Matasci, G.; Ravanel, L.

2018-01-01

Rockfalls strongly influence the evolution of steep rocky landscapes and represent a significant hazard in mountainous areas. Defining the most probable future rockfall source areas is of primary importance for both geomorphological investigations and hazard assessment. Thus, a need exists to understand which areas of a steep cliff are more likely to be affected by a rockfall. An important analytical gap exists between regional rockfall susceptibility studies and block-specific geomechanical calculations. Here we present methods for quantifying rockfall susceptibility at the cliff scale, which is suitable for sub-regional hazard assessment (hundreds to thousands of square meters). Our methods use three-dimensional point clouds acquired by terrestrial laser scanning to quantify the fracture patterns and compute failure mechanisms for planar, wedge, and toppling failures on vertical and overhanging rock walls. As a part of this work, we developed a rockfall susceptibility index for each type of failure mechanism according to the interaction between the discontinuities and the local cliff orientation. The susceptibility for slope parallel exfoliation-type failures, which are generally hard to identify, is partly captured by planar and toppling susceptibility indexes. We tested the methods for detecting the most susceptible rockfall source areas on two famously steep landscapes, Yosemite Valley (California, USA) and the Drus in the Mont-Blanc massif (France). Our rockfall susceptibility models show good correspondence with active rockfall sources. The methods offer new tools for investigating rockfall hazard and improving our understanding of rockfall processes.

Magnetic susceptibility and relation to initial 87Sr/86Sr for granitoids of the central Sierra Nevada, California

Science.gov (United States)

Bateman, P.C.; Dodge, F.C.W.; Kistler, R.W.

1991-01-01

Measurement of the magnetic susceptibility of more than 6000 samples of granitic rock from the Mariposa 1?? by 2?? quadrangle, which crosses the central part of the Sierra Nevada batholith between 37?? and 38??N latitude, shows that magnetic susceptibility values are above 10-2 SI units in the east and central parts of the batholith and drop abruptly to less than 10-3 SI units in the western foothills. In a narrow transitional zone, intermediate values (10-3 to 10-2) prevail. Magnetic susceptibility appears to decrease slightly westward within the zones of both high and low values. Magnetic susceptibility in plutonic rocks is chiefly a function of the abundance of magnetite, which depends, in turn, on the total iron content of the rocks and their oxidation ratio. Correlations of magnetic susceptibility with initial 87Sr/86Sr suggest that oxidation ratios have been inherited from the source regions for the magmas from which the rocks crystallized. Reduction of Fe3+ to Fe2+ by organic carbon or other reducing substances may also have affected magnetic susceptibility. -from Authors

Magnetism of a sigma-phase Fe{sub 60}V{sub 40} alloy: Magnetic susceptibilities and magnetocaloric effect studies

Energy Technology Data Exchange (ETDEWEB)

Bałanda, Maria [Institute of Nuclear Physics, Polish Academy of Science, PL-31-342 Kraków (Poland); Dubiel, Stanisław M., E-mail: Stanislaw.Dubiel@fis.agh.edu.pl [AGH University of Science and Technology, Faculty of Physics and Applied Computer Science, PL-30-059 Kraków (Poland); Pełka, Robert [Institute of Nuclear Physics, Polish Academy of Science, PL-31-342 Kraków (Poland)

2017-06-15

Highlights: • Sigma-phase Fe{sub 60}V{sub 40} alloy was studied by means of AC and DC magnetic susceptibilities. • Re-entrant character of the magnetism has been evidenced. • Curie temperature was found as ∼169 K and the spin-freezing temperature as ∼164 K. • Critical exponents β = 0.6, γ = 1.0 and Δ = 1.6 were determined. • Magnetocaloric effect was investigated. - Abstract: Magnetic properties of a sigma-phase Fe{sub 60}V{sub 40} intermetallic compound were studied by means of ac and dc magnetic susceptibility and magnetocaloric effect measurements. The compound is a soft magnet yet it was found to behave like a re-entrant spin-glass system. The magnetic ordering temperature was found to be T{sub C} ≈ 170 K, while the spin-freezing temperature was ∼164 K. Its relative shift per decade of ac frequency was 0.002, a value smaller than that typical of canonical spin-glasses. Magnetic entropy change, ΔS, in the vicinity of T{sub C} was determined for magnetic field, H, ranging between 5 and 50 kOe. Analysis of ΔS in terms of the power law yielded the critical exponent, n, vs. temperature with the minimum value of 0.75 at T{sub C}, while from the analysis of a relative shift of the maximum value of ΔS with the field a critical exponent Δ = 1.7 was obtained. Based on scaling laws relationships values of other two exponents viz. β = 0.6 and γ = 1 were determined.

Thermal stress effects in intermetallic matrix composites

Science.gov (United States)

Wright, P. K.; Sensmeier, M. D.; Kupperman, D. S.; Wadley, H. N. G.

1993-01-01

Intermetallic matrix composites develop residual stresses from the large thermal expansion mismatch (delta-alpha) between the fibers and matrix. This work was undertaken to: establish improved techniques to measure these thermal stresses in IMC's; determine residual stresses in a variety of IMC systems by experiments and modeling; and, determine the effect of residual stresses on selected mechanical properties of an IMC. X ray diffraction (XRD), neutron diffraction (ND), synchrotron XRD (SXRD), and ultrasonics (US) techniques for measuring thermal stresses in IMC were examined and ND was selected as the most promising technique. ND was demonstrated on a variety of IMC systems encompassing Ti- and Ni-base matrices, SiC, W, and Al2O3 fibers, and different fiber fractions (Vf). Experimental results on these systems agreed with predictions of a concentric cylinder model. In SiC/Ti-base systems, little yielding was found and stresses were controlled primarily by delta-alpha and Vf. In Ni-base matrix systems, yield strength of the matrix and Vf controlled stress levels. The longitudinal residual stresses in SCS-6/Ti-24Al-llNb composite were modified by thermomechanical processing. Increasing residual stress decreased ultimate tensile strength in agreement with model predictions. Fiber pushout strength showed an unexpected inverse correlation with residual stress. In-plane shear yield strength showed no dependence on residual stress. Higher levels of residual tension led to higher fatigue crack growth rates, as suggested by matrix mean stress effects.

Genome-wide association studies on HIV susceptibility, pathogenesis and pharmacogenomics

NARCIS (Netherlands)

van Manen, Daniëlle; van 't Wout, Angélique B.; Schuitemaker, Hanneke

2012-01-01

Susceptibility to HIV-1 and the clinical course after infection show a substantial heterogeneity between individuals. Part of this variability can be attributed to host genetic variation. Initial candidate gene studies have revealed interesting host factors that influence HIV infection, replication

Magnetic propertiesof Lu.sub.2./sub.Fe.sub.16./sub.X (X = Fe, Ni, Cr, Si) intermetallics under high hydrostatic pressure

Czech Academy of Sciences Publication Activity Database

Kamarád, Jiří; Andreev, Alexander V.; Machátová, Zuzana; Arnold, Zdeněk

408-412, - (2006), s. 151-154 ISSN 0925-8388 R&D Projects: GA ČR(CZ) GA202/02/0739; GA MŠk(CZ) ME 495 Institutional research plan: CEZ:AV0Z10100521 Keywords : intermetallic compounds * Lu 2 Fe 17 * magnetic properties * high pressure Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.250, year: 2006

Predicting the stability of ternary intermetallics with density functional theory and machine learning

Science.gov (United States)

Schmidt, Jonathan; Chen, Liming; Botti, Silvana; Marques, Miguel A. L.

2018-06-01

We use a combination of machine learning techniques and high-throughput density-functional theory calculations to explore ternary compounds with the AB2C2 composition. We chose the two most common intermetallic prototypes for this composition, namely, the tI10-CeAl2Ga2 and the tP10-FeMo2B2 structures. Our results suggest that there may be ˜10 times more stable compounds in these phases than previously known. These are mostly metallic and non-magnetic. While the use of machine learning reduces the overall calculation cost by around 75%, some limitations of its predictive power still exist, in particular, for compounds involving the second-row of the periodic table or magnetic elements.

Lattice disorder in strongly correlated lanthanide and actinide intermetallics

International Nuclear Information System (INIS)

Booth, C.H.; Bauer, E.D.; Maple, M.B.; Lawrence, J.M.; Kwei, G.H.; Sarrao, J.L.

2001-01-01

Lanthanide and actinide intermetallic compounds display a wide range of correlated-electron behavior, including ferromagnetism, antiferromagnetism, nonmagnetic (Kondo) ground states, and so-called 'non-Fermi liquid' (NFL) behavior. The interaction between f electrons and the conduction band is a dominant factor in determining the ground state of a given system. However, lattice disorder can create a distribution of interactions, generating unusual physical properties. These properties may include NFL behavior in many materials. In addition, lattice disorder can cause deviations from standard Kondo behavior that is less severe than NFL behavior. A review of the lattice disorder mechanism within a tight-binding model is presented, along with measurements of the YbBCu 4 and UPd x Cu 5-x systems, demonstrating the applicability of the model. These measurements indicate that while the YbBCu 4 system appears to be well ordered, both site interchange and continuous bond-length disorder occur in the UPd x Cu 5-x series. Nevertheless, the measured bond-length disorder in UPdCu 4 does not appear to be enough to explain the NFL properties simply with the Kondo disorder model. (au)

Magnetic susceptibility of functional groups

International Nuclear Information System (INIS)

Herr, T.; Ferraro, M.B.; Contreras, R.H.

1990-01-01

Proceeding with a series of works where new criteria are applied to the the calculation of the contribution of molecular fragments to certain properties, results are presented for a group of 1-X-benzenes and 1-X-naphtalenes for the magnetic susceptibility constant. Both the diamagnetic and paramagnetic parts are taken into account. To reduce the problems associated with the Gauge dependence originated in the approximations made, Gauge independent atomic orbitals (GIAO) orbitals are used in the atomic orbital basis. Results are discussed in terms of functional groups. (Author). 17 refs., 1 fig., 3 tabs

Thermal expansion and thermal diffusivity properties of Co-Si solid solutions and intermetallic compounds

International Nuclear Information System (INIS)

Ruan, Ying; Li, Liuhui; Gu, Qianqian; Zhou, Kai; Yan, Na; Wei, Bingbo

2016-01-01

Highlights: • Length change difference between rapidly and slowly solidified Co-Si alloy occurs at high temperature. • Generally CTE increases with an increasing Si content. • The thermal diffusion abilities are CoSi 2 > Co 95 Si 5 > Co 90 Si 10 > Co 2 Si > CoSi if T exceeds 565 K. • All the CTE and thermal diffusivity variations with T satisfy linear or polynomial relations. - Abstract: The thermal expansion of Co-Si solid solutions and intermetallic compounds was measured via dilatometric method, compared with the results of first-principles calculations, and their thermal diffusivities were investigated using laser flash method. The length changes of rapidly solidified Co-Si alloys are larger than those of slowly solidified alloys when temperature increases to around 1000 K due to the more competitive atom motion. The coefficient of thermal expansion (α) of Co-Si alloy increases with an increasing Si content, except that the coefficient of thermal expansion of Co 95 Si 5 influenced by both metastable structure and allotropic transformation is lower than that of Co 90 Si 10 at a higher temperature. The thermal expansion abilities of Co-Si intermetallic compounds satisfy the relationship of Co 2 Si > CoSi > CoSi 2 , and the differences of the coefficients of thermal expansion between them increase with the rise of temperature. The thermal diffusivity of CoSi 2 is evidently larger than the values of other Co-Si alloys. If temperature exceeds 565 K, their thermal diffusion abilities are CoSi 2 > Co 95 Si 5 > Co 90 Si 10 > Co 2 Si > CoSi. All the coefficient of thermal expansion and thermal diffusivity variations with temperature satisfy linear or polynomial relations.

Preparation and characterization of the Li(17)Pb(83) eutectic alloy and the LiPb intermetallic compound

International Nuclear Information System (INIS)

Jauch, U.; Karcher, V.; Schulz, B.

1986-01-01

Li(17)Pb(83) and LiPb were prepared from the pure elements in amounts of several hundred grams. The resolidified samples were characterized by melting points (eutectic temperature), chemical analysis and metallography. Using differential thermal analysis the heats of fusion were determined and the behaviour of the intermetallic phase LiPb in vacuum and high purified He was studied. The results from these investigations were applied to characterize Li(17)Pb(83) prepared in high amounts for technical application as a potential liquid breeder material. (orig.)

Crack resistance behaviour of an intermetallic Ti-Al-Si-Nb alloy at room temperature

International Nuclear Information System (INIS)

Wittkowsky, B.U.; Pfuff, M.J.

1996-01-01

The room temperature crack growth behaviour of a Ti-Al-Si-Nb alloy consisting of the two intermetallic phases (Ti, Nb) 3 (Al, Si) and (Ti, Nb) 5 (Si, Al) 3 is investigated in the present paper. The material exhibits a heterogeneous disordered microstructure and fails in a brittle manner. Crack growth is associated with a pronounced crack resistance behaviour. For a sample of nominally identical specimens the R-curves scatter around a mean curve with a standard deviation which remains roughly constant as the crack grows. A natural extension of the bundle model introduced in a previous paper is used to simulate R-curves and their scatter is in reasonably good agreement with the experimental findings. (orig.)

The creep properties of a low alloy ferritic steel containing an intermetallic precipitate dispersion

International Nuclear Information System (INIS)

Batte, A.D.; Murphy, M.C.; Edmonds, D.V.

1976-01-01

A good combination of creep rupture ductility and strength together with excellent long term thermal stability, has been obtained from a dispersion of intermetallic Laves phase precipitate in a non-transforming ferritic low alloy steel. The steel is without many of the problems currently associated with the heat affected zone microstructures of low alloy transformable ferritic steels, and can be used as a weld metal. Following suitable development to optimize the composition and heat treatment, such alloys may provide a useful range of weldable creep resistant steels for steam turbine and other high temperature applications. They would offer the unique possibility of easily achievable microstructural uniformity, giving good long term strength and ductility across the entire welded joint

Experimental formation enthalpies for intermetallic phases and other inorganic compounds

Science.gov (United States)

Kim, George; Meschel, S. V.; Nash, Philip; Chen, Wei

2017-01-01

The standard enthalpy of formation of a compound is the energy associated with the reaction to form the compound from its component elements. The standard enthalpy of formation is a fundamental thermodynamic property that determines its phase stability, which can be coupled with other thermodynamic data to calculate phase diagrams. Calorimetry provides the only direct method by which the standard enthalpy of formation is experimentally measured. However, the measurement is often a time and energy intensive process. We present a dataset of enthalpies of formation measured by high-temperature calorimetry. The phases measured in this dataset include intermetallic compounds with transition metal and rare-earth elements, metal borides, metal carbides, and metallic silicides. These measurements were collected from over 50 years of calorimetric experiments. The dataset contains 1,276 entries on experimental enthalpy of formation values and structural information. Most of the entries are for binary compounds but ternary and quaternary compounds are being added as they become available. The dataset also contains predictions of enthalpy of formation from first-principles calculations for comparison. PMID:29064466

The complex ac susceptibility of superconducting Y-Ba-CuO thin film and bulk samples

International Nuclear Information System (INIS)

Lobotka, P.; Goemoery, F.

1988-01-01

Complex ac susceptibility measurements as function of temperature on Y-Ba-CuO superconductors are reported. A strong dependence of the susceptibility curves on the ac field magnitude and little influence of the superimposed dc field are observed on both, thin film and bulk samples. The susceptibilities of these materials are frequency independent in the range 30 to 7200 Hz what demonstrates the negligible role of eddy currents. A second peak in the imaginary part of susceptibility is observed in the bulk sample at higher levels of ac field. This implies the existence of another component in the sample with higher T c and lower losses. (author)

Size and surface AREA analysis of some metallic and intermetallic powders

International Nuclear Information System (INIS)

Elmasry, M.A.A.; Elsayed, A.A.; Abadir, M.F.

1988-01-01

The powder characterization of three intermetallic compounds ( Cr B, B 4 c and S ib 4 ) and three metallic powders (Fe, Co, and Ni) has been performed. This included the determination of powder density, chemical analysis, impurity analysis, shape factor, particle size analysis and specific surface area. The particle size analysis for the six powders was carried out using three techniques, namely; the 0-23, the microtrac and the fisher sub sieve and size. It was found that the analysis of the two powders and deviates from the log-normal probability distribution and the deviation was corrected. The specific surface area of the powders was measured using the high speed surface area analysis (BET method), and it was also calculated from surface area analysis findings, the BET technique was found to give the highest specific surface area values, and was attributed to the inclusion of internal porosity in the measurement. 8 fig., 10 tab

Susceptibility of Aeromonas Hydophila Isolates to Antimicrobial Drugs

Directory of Open Access Journals (Sweden)

Igor Stojanov

2010-05-01

Full Text Available Aeromonas hydrophila is a microorganism widely distributed in nature: in water, soil, food. It is also part of the normal bacterial flora of many animals. As an opportune microorganism it is a secondary biological agent that contributes to the occurrence of a fish disease and its deterioration. Frequently, its presence is an indication of bad zoohygiene and zootechnical conditions in fish ponds. Reduced quality and quantity of feed, mechanical injuries, parasitosis, seasonal oscillation in temperature present some of the factors that produce favorable conditions for bacterial proliferation of aeromonas in fish ponds, so clinical symptoms of the disease occur. Aeromonas is almost always present in clinical isolates and may be unjustly accused for bad health of fish. Antibiotic therapy is applied even when the clinical findings are clear, what certainly effects the susceptibility to chemotherapeutics. The subject of our work was bacteriological examination of the material obtained from the carps with the observed skin changes and the carps without these changes. Also, antimicrobial susceptibility of Aeromonas hydrophila was tested. The aim of this research was to determined the presence of Aeromonas hydrophilia in the carp ponds and to test antibiotic susceptibility. The material consisted of the samples from the fish ponds where the carps were with and without changed skin. The method the isolation of Aeromonas hydrophila was used. The diffusion disk technique was used for testing antibiotic susceptibility. The isolates were tested for their susceptibility to Florephenikol, Flumequine, Olaqindox and Oxitetracycline. The obtained results point that antimicrobial susceptibility was the same regardless of the origin of the samples, i.e. the resistance was the same for both groups of samples (the strains isolated from the fish with skin changes and the strains from fish without changes on skin. The strains were highly resistant: 35% were resistant to

One-pot solvothermal synthesis of ordered intermetallic Pt2In3 as stable and efficient electrocatalyst towards direct alcohol fuel cell application

Science.gov (United States)

Jana, Rajkumar; Peter, Sebastian C.

2016-10-01

Ordered intermetallic Pt2In3 nanoparticles have been synthesized by superhydride reduction of K2PtCl4 and InCl3.xH2O precursors using facile, one-pot solvothermal method. We report surfactant free solvothermal synthesis of a novel ordered Pt2In3 intermetallic nanoparticles for the first time. The structure and morphology of the catalyst has been confirmed by powder X-ray diffraction, transmission electron microscopy, field emission scanning electron microscopy, energy-dispersive spectrometry and X-ray photoelectron spectroscopy. The electrocatalytic properties of the catalysts have been investigated by cyclic voltammetry and chronoamperometry. The as prepared Pt2In3 catalyst exhibit far superior electrocatalytic activity and stability towards alcohol oxidation over commercial Pt/C. The specific activity of as synthesized catalyst was found to be 3.2 and 2.3 times higher than commercial Pt/C for methanol and ethanol oxidation, respectively. This improved activity and durability of the Pt2In3 nanoparticles can make the catalyst an ideal catalyst candidate for direct alcohol fuel cell.

Advancement of Compositional and Microstructural Design of Intermetallic γ-TiAl Based Alloys Determined by Atom Probe Tomography

Science.gov (United States)

Klein, Thomas; Clemens, Helmut; Mayer, Svea

2016-01-01

Advanced intermetallic alloys based on the γ-TiAl phase have become widely regarded as most promising candidates to replace heavier Ni-base superalloys as materials for high-temperature structural components, due to their facilitating properties of high creep and oxidation resistance in combination with a low density. Particularly, recently developed alloying concepts based on a β-solidification pathway, such as the so-called TNM alloy, which are already incorporated in aircraft engines, have emerged offering the advantage of being processible using near-conventional methods and the option to attain balanced mechanical properties via subsequent heat-treatment. Development trends for the improvement of alloying concepts, especially dealing with issues regarding alloying element distribution, nano-scale phase characterization, phase stability, and phase formation mechanisms demand the utilization of high-resolution techniques, mainly due to the multi-phase nature of advanced TiAl alloys. Atom probe tomography (APT) offers unique possibilities of characterizing chemical compositions with a high spatial resolution and has, therefore, been widely used in recent years with the aim of understanding the materials constitution and appearing basic phenomena on the atomic scale and applying these findings to alloy development. This review, thus, aims at summarizing scientific works regarding the application of atom probe tomography towards the understanding and further development of intermetallic TiAl alloys. PMID:28773880

In-situ synthesized Ni–Zr intermetallic/ceramic reinforced composite coatings on zirconium substrate by high power diode laser

Energy Technology Data Exchange (ETDEWEB)

Liu, Kun; Li, Yajiang, E-mail: yajli@sdu.edu.cn; Wang, Juan; Ma, Qunshuang

2015-03-05

Highlights: • In-situ synthesized Ni–Zr intermetallics/ceramic reinforced composite coatings. • Si enrichment and Ni replacing site of Si both resulted in forming Zr{sub 5}(Si{sub x}Ni{sub 1−x}){sub 4.} • Microstructure and forming of ZrB{sub 2} depended on affinity of elements and Si/B ratio. - Abstract: Ni–Zr intermetallic/ceramic reinforced composite coatings were in-situ synthesized by laser cladding series of Ni–Cr–B–Si powders on zirconium substrate. Microstructure, phase constituents and microhardness of coatings were investigated by means of optical microscope (OM), scanning electron microscope (SEM), energy dispersive spectrometer (EDS), X-ray diffraction (XRD) and microsclemeter. Results indicated that coatings with metallurgical bonding to substrate consisted of cellular NiZr matrix and massive reinforcements including NiZr{sub 2}, Zr{sub 5}(Si{sub x}Ni{sub 1−x}){sub 4} and ZrB{sub 2}. Morphologies of reinforcements were mainly dominated by temperature gradient and cooling rate from surface to bottom of the coating produced by same powder. In different coatings, microstructure and forming of ZrB{sub 2} mainly depended on affinity of elements and Si/B ratio in different powders. In addition, the mean microhardness of coatings up to 1200–1300 HV{sub 0.2} is nearly 7 times higher than that of R60702 zirconium substrate.

Fast diffusion in the intermetallics Ni3Sb and Fe3Si: a neutron scattering study

International Nuclear Information System (INIS)

Randl, O.G.

1994-02-01

We present the results of neutron scattering experiments designed to elucidate the reason for the extraordinarily fast majority component diffusion in two intermetallic alloys of DO 3 structure, Fe 3 Si and Ni 3 Sb: We have performed diffraction measurements in order to determine the crystal structure and the state of order of both alloys as a function of composition and temperature. The results on Fe 3 Si essentially confirm the classical phase diagram: The alloys of a composition between 16 and 25 at % Si are DO 3 -ordered at room temperature and disorder at high temperatures. The high-temperature phase Ni 3 Sb also crystallizes in the DO 3 structure. Vacancies are created in one Ni sublattice at Sb contents beyond 25 at %. In a second step the diffusion mechanism in Ni 3 Sb has been studied by means of quasielastic neutron scattering. The results are reconcileable with a very simple NN jump model between the two different Ni sublattices. Finally, the lattice dynamics of Fe 3 Si and Ni 3 Sb has been studied by inelastic neutron scattering in dependence of temperature (both alloys) and alloy composition (Fe 3 Si only). The results on Fe 3 Si indicate clearly that phonon enhancement is not the main reason for fast diffusion in this alloy. In Ni 3 Sb no typical signs of phonon-enhanced diffusion have been found either. As a conclusion, fast diffusion in DO 3 intermetallics is explained by extraordinarily high vacancy concentrations (several atomic percent) in the majority component sublattices. (author)

The effect of crystal structure stability on the mobility of gas bubbles in intermetallic uranium compounds

International Nuclear Information System (INIS)

Rest, J.; Hofman, G.L.; Birtcher, R.C.

1988-01-01

Irradiation experiments with certain low-enrichment, high-density, uranium-base intermetallic alloys that are candidate reactor fuel materials, such as U 3 Si and U 6 Fe, have revealed extraordinarily large voids at low and medium fuel burnup. This phenomenon of breakaway swelling does not occur in other fuel types, such as U 3 Si 2 and UAl 3 , where a distribution of relatively small and stable fission gas bubbles forms. In situ transmission electron microscope observations of ion radiation-induced rapid swelling of intermetallic materials are consistent with growth by plastic flow. Large radiation enhancement of plastic flow in amorphous materials has been observed in several independent experiments and is thought to be a general materials phenomenon. The basis for a microscopic theory of fission gas bubble behavior in irradiated amorphous compounds has been formulated. The assumption underlying the overall theory is that the evolution of the porosity from that observed in the crystalline material to that observed in irradiated amorphous U 3 Si as a function of fluence is due to a softening of the irradiated amorphous material. Bubble growth in the low-viscosity material has been approximated by an effective enhanced diffusivity. Mechanisms are included for the radiation-induced softening of the amorphous material, and for a relation between gas atom mobilities and radiation-induced (defect-generated) changes in the material. Results of the analysis indicate that the observed rapid swelling in U 3 Si arises directly from enhanced bubble migration and coalescence due to plastic flow. 34 refs., 11 figs

Microstructural and Material Quality Effects on Rolling Contact Fatigue of Highly Elastic Intermetallic NiTi Ball Bearings

Science.gov (United States)

Dellacorte, Christopher; Howard, S. Adam; Thomas, Fransua; Stanford, Malcolm K.

2017-01-01

Rolling element bearings made from highly-elastic intermetallic materials (HIM)s, such as 60NiTi, are under development for applications that require superior corrosion and shock resistance. Compared to steel, intermetallics have been shown to have much lower rolling contact fatigue (RCF) stress capability in simplified 3-ball on rod (ASTM STP 771) fatigue tests. In the 3-ball tests, poor material quality and microstructural flaws negatively affect fatigue life but such relationships have not been established for full-scale 60NiTi bearings. In this paper, 3-ball-on-rod fatigue behavior of two quality grades of 60NiTi are compared to the fatigue life of full-scale 50mm bore ball bearings made from the same materials. 60NiTi RCF rods with material or microstructural flaws suffered from infant mortality failures at all tested stress levels while high quality 60NiTi rods exhibited no failures at lower stress levels. Similarly, tests of full-scale bearings made from flawed materials exhibited early surface fatigue and through crack type failures while bearings made from high quality material did not fail even in long-term tests. Though the full-scale bearing test data is yet preliminary, the results suggest that the simplified RCF test is a good qualitative predictor of bearing performance. These results provide guidance for materials development and to establish minimum quality levels required for successful bearing operation and life.

A Neurogenetics Approach to Defining Differential Susceptibility to Institutional Care

Science.gov (United States)

Brett, Zoe H.; Sheridan, Margaret; Humphreys, Kate; Smyke, Anna; Gleason, Mary Margaret; Fox, Nathan; Zeanah, Charles; Nelson, Charles; Drury, Stacy

2015-01-01

An individual's neurodevelopmental and cognitive sequelae to negative early experiences may, in part, be explained by genetic susceptibility. We examined whether extreme differences in the early caregiving environment, defined as exposure to severe psychosocial deprivation associated with institutional care compared to normative rearing,…

Intermetallic GaPd₂ Nanoparticles on SiO₂ for Low-Pressure CO₂ Hydrogenation to Methanol

DEFF Research Database (Denmark)

Fiordaliso, Elisabetta Maria; Sharafutdinov, Irek; Carvalho, Hudson W. P.

2015-01-01

A nanodispersed intermetallic GaPd2/SiO2 catalyst is prepared by simple impregnation of industrially relevant high-surface-area SiO2 with Pd and Ga nitrates, followed by drying, calcination, and reduction in hydrogen. The catalyst is tested for CO2 hydrogenation to methanol at ambient pressure, r...

Ab-initio thermodynamic and elastic properties of AlNi and AlNi3 intermetallic compounds

Science.gov (United States)

Yalameha, Shahram; Vaez, Aminollah

2018-04-01

In this paper, thermodynamic and elastic properties of the AlNi and AlNi3 were investigated using density functional theory (DFT). The full-potential linearized augmented plane-wave (APW) in the framework of the generalized gradient approximation as used as implemented in the Wien2k package. The temperature dependence of thermal expansion coefficient, bulk modulus and heat capacity in a wide range of temperature (0-1600 K) were investigated. The calculated elastic properties of the compounds show that both intermetallic compounds of AlNi and AlNi3 have surprisingly negative Poisson’s ratio (NPR). The results were compared with other experimental and computational data.

Corrosion behavior of Fe3Al intermetallics with addition of lithium, cerium and nickel in 2.5 % SO2+N2 at 900 °C

Directory of Open Access Journals (Sweden)

González-Rodríguez, J. G.

2012-12-01

Full Text Available The corrosion behavior of Fe3Al-type intermetallic alloys with addition of 1 at. % cerium, lithium and nickel at high temperature has been studied. The various alloys were exposed to an environment composed of 2.5 % SO2+N2 at 900 °C for 48 h. For all the intermetallic tested, the corrosion kinetics showed a parabolic behavior. The alloy, which showed less corrosion rate, was the Fe3AlNi alloy, being Fe3AlCeLi the alloy with the highest corrosion rate. For the various alloys, energy dispersive X-ray spectroscopy analysis, EDS, on the developed scale only detected aluminum, oxygen, and traces of iron and cerium, suggesting the formation of alumina as main component. The intermetallic alloys showed oxide cracking and spalling. The intermetallic chemical composition played an important role in defining the oxide scale morphology and the extent of damage.Se estudió el comportamiento a la corrosión a alta temperatura de intermetálicos tipo Fe3Al con adición de 1at. % de cerio, litio y níquel. Las diferentes aleaciones fueron expuestas bajo un ambiente compuesto de 2,5 % SO2+N2 a 900 °C durante 48 h. Para todos los intermetálicos ensayados, la cinética de corrosión presentó un comportamiento parabólico. La aleación que mostró la menor velocidad de corrosión fue el intermetálico Fe3AlNi, siendo el intermetálico Fe3AlCeLi el de mayor velocidad de corrosión. Los análisis mediante espectroscopía de dispersión de rayos X, EDS, sobre la costra formada identificaron únicamente aluminio, oxígeno y trazas de hierro y cerio, lo que sugiere la formación de alúmina como el componente principal. Los intermetálicos mostraron agrietamiento y desprendimiento de la costra de óxido. La composición química de los intermetálicos tuvo un papel importante en la definición de la morfología del óxido formado y el grado de daño.

Lanthanum hexaboride as advanced structural refiner/getter in TiAl-based refractory intermetallics

Energy Technology Data Exchange (ETDEWEB)

Kartavykh, A.V., E-mail: karta@korolev-net.ru [Technological Institute for Superhard and Novel Carbon Materials (TISNCM), 7a Centralnaya str., 142190 Troitsk, Moscow (Russian Federation); National University of Science and Technology “MISIS”, Leninsky pr. 4, 119049 Moscow (Russian Federation); Asnis, E.A.; Piskun, N.V.; Statkevich, I.I. [The E.O. Paton Electric Welding Institute, 11 Bozhenko str., 03680 Kyiv (Ukraine); Gorshenkov, M.V.; Tcherdyntsev, V.V. [National University of Science and Technology “MISIS”, Leninsky pr. 4, 119049 Moscow (Russian Federation)

2014-03-05

Highlights: • Fist application of LaB{sub 6} additive in TiAl-based intermetallics casting. • Pilot synthesis/casting and study of selected TiAl(Nb,Cr,Zr)B,La alloys set. • Dual effect observed: phase structure refinement and oxygen impurity removal. • Co-precipitation of TiB and La{sub 2}O{sub 3} in melt: 2LaB{sub 6} + 12Ti + 3O → 12TiB↓ + La{sub 2}O{sub 3}↓. • Features of structure refinement and oxygen gettering mechanisms reported. -- Abstract: The work is aimed at the study of the formation and refinement of microstructure appearing in the solidifying refractory TiAl-based intermetallics being inoculated with precise boron addition. The novelty of research consists in test application of lanthanum hexaboride (LaB{sub 6}) ligature within semi-continuous electron beam casting process of selected alloys. Two ingots with nominal compositions Ti–44Al–5Nb–2Cr–1.5Zr–0.4B–0.07La and Ti–44Al–5Nb–1Cr–1.5Zr–1B–0.17La (at.%) have been synthesized and cast along with the reference alloy Ti–44Al–5Nb–3Cr–1.5Zr. Their comparative examination suggests (i) essential microstructural phase refinement effect coupled with (ii) threefold/fourfold decrease of background content of undesirable residual oxygen impurity in both alloys containing LaB{sub 6}. This advanced dual activity (i–ii) of LaB{sub 6} is explained by its complete dissolution, dissociation and following re-precipitation of effective Ti-based monoboride nucleants of orthorhombic B27 structure, those being accompanied by strong internal gettering of dissolved oxygen from the melt and from boride-inoculated solid α{sub 2}-Ti{sub 3}Al phase with liberated elemental lanthanum. The phase composition and structure of cast alloys; state and characterization of newly precipitated TiB boride; features of La{sub 2}O{sub 3} micro/nano-dimensional precipitation and oxygen gettering mechanism are reported and discussed.

Fracture toughness of ordered intermetallic compounds exhibiting limited ductility and mechanical properties of ion-irradiated polycrystalline NiAl. Final report, July 1, 1986 - June 30, 1997

International Nuclear Information System (INIS)

Ardell, A.J.

1997-09-01

The focus of the research performed under the auspices of this grant changed several times during the lifetime of the project. The initial activity was an investigation of irradiation-induced amorphization of ordered intermetallic compounds, using energetic protons as the bombarding species. Two significant events stimulated a change of direction: (1) the proton accelerating facility that the authors had been using at the California State University at Los Angeles became unavailable late in 1988 because of a personnel matter involving the only individual capable of operating the machine; (2) they learned that disordering and amorphization of intermetallic compounds produced interesting effects on their mechanical properties. Loss of access t the local accelerator prompted a collaboration with Dr. Droa Pedraza of the Oak Ridge National Laboratory (ORNL), enabling access to the accelerator at ORNL. The influence of disordering and amorphization on mechanical properties ultimately stimulated the development of a miniaturized disk-bend testing (MDBT) facility, the intent of which was to provide semiquantitative and even quantitative measures of the mechanical behavior of ion-irradiated ordered intermetallic alloys. The second phase of the project involved the perfection and usage of the MDBT, and involved exploratory experiments on unirradiated materials like amorphous alloy ribbons and brittle grain boundaries in Ni 3 Al. This report is a brief summary of the research highlights of the project, organized according to the activity that was emphasized at the time

Magnetic measurements under pressure

Czech Academy of Sciences Publication Activity Database

Zentková, M.; Arnold, Zdeněk; Mihalik, M.; Mihalik, M.; Zentko, A.; Kamarád, Jiří; Mitróová, Z.; Mat`aš, S.

2006-01-01

Roč. 57, 8/S (2006), s. 29-32 ISSN 1335-3632 Institutional research plan: CEZ:AV0Z10100521 Keywords : hydrostatic pressure * Prussian blue analogues * AC susceptibility * intermetallic compound * ferromagnetism * errimagnetism Subject RIV: BM - Solid Matter Physics ; Magnetism

Microstructure and high temperature oxidation resistance of in-situ synthesized TiN/Ti_3Al intermetallic composite coatings on Ti6Al4V alloy by laser cladding process

International Nuclear Information System (INIS)

Liu, Hongxi; Zhang, Xiaowei; Jiang, Yehua; Zhou, Rong

2016-01-01

High temperature anti-oxidation TiN/Ti_3Al intermetallic composite coatings were fabricated with the powder and AlN powder on Ti6Al4V titanium alloy surface by 6 kW transverse-flow CO_2 laser apparatus. The chemical composition, morphology and microstructure of the TiN/Ti_3Al composite coatings were characterized by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy dispersive spectrometer (EDS). In order to evaluate the high temperature oxidation resistance of TiN/Ti_3Al coating, the isothermal oxidation test was performed in a high temperature resistance furnace at 600 °C and 800 °C, respectively. The result shows that the composite coating has a rapidly solidified fine microstructure consisting of TiN primary phase (granular-like, flake-like or dendrites), with an even distribution in Ti_3Al matrix. It indicates that a physical and chemical reaction between Ti powder and AlN powder has completely occurred under the laser irradiation condition. In addition, the microhardness of the TiN/Ti3Al intermetallic composite coating is 3.4 times higher than that of the Ti6Al4V alloy substrate and reaches 844 HV_0_._2. The high temperature oxidation behavior test reveals that the high temperature oxidation resistance of TiN/Ti_3Al composite coating is much better than that of titanium alloy substrate. The excellent high temperature oxidation resistance of TiN/Ti_3Al intermetallic composite coating is attributed to the formation of reinforced phases TiN, Al_2O_3 and TiO_2. The laser cladding TiN/Ti_3Al intermetallic composite coating is anticipated to be a promising high temperature oxidation resistance coating for Ti6Al4V alloy. - Highlights: • In-situ TiN/Ti_3Al composite coating was synthesized on Ti6Al4V alloy by laser cladding. • The influence of Ti and AlN molar ratio on the microstructure of the coating was studied. • The TiN/Ti_3Al intermetallic coating is mainly composed of α-Ti, TiN and Ti_3Al phases. • The

Immunogenetics and genetic susceptibility in the pathogenesis of autoimmune hepatitis

Directory of Open Access Journals (Sweden)

Das Anup K

2014-11-01

Full Text Available vAutoimmune hepatitis is a progressive liver disease. Its pathogenesis is unclear, but needs a ‘trigger’ to initiate the disease in a genetically susceptible person. The susceptibility is partly related to MHCII class genes, and more so with human leukocyte antigen (HLA. Several mechanisms have been proposed which, however, cannot fully explain the immunologic findings in autoimmune hepatitis. The susceptibility to any autoimmune disease is determined by several factors where genetic and immunological alterations, along with, environmental factor are active. MHCII antigens as a marker for AIH, or a predictor of treatment response and prognosis has been investigated. Since MHCII antigens show significant ethnic heterogeneity, mutations in MHCII may merely act as only precursors of the surface markers of immune cells, which can be of significance, because the changes in HLA and MHC are missing in certain populations. One such marker is the CTLA-4 (CD152 gene mutation, reported in the phenotypes representing susceptibility to AIH. Other candidate genes of cytokines, TNF, TGF-beta1 etc, have also been investigated but with unvalidated results. Paediatric AIH show differences in genetic susceptibility. Genetic susceptibility or resistance to AIH may be associated with polypeptides in DRB1 with certain amino-acid sequences. Understanding which genes are implicated in genesis and/or disease progression will obviously help to identify key pathways in AIH and provide better insights into its pathogenesis. But studies to identify responsible genes are complex because of the complex trait of AIH.

Radiation-induced amorphization of intermetallic compounds: A molecular-dynamics study of CuTi and Cu4Ti3

International Nuclear Information System (INIS)

Lam, N.Q.; Okamoto, P.R.; Sabochick, M.J.

1991-06-01

In the present paper, important results of our recent computer simulation of radiation-induced amorphization in the ordered compounds CuTi and Cu 4 Ti 3 are summarized. The energetic, structural, thermodynamic and mechanical responses of these intermetallics during chemical disordering, point-defect production and heating were simulated, using molecular dynamics and embedded-atom potentials. From the atomistic details obtained, the critical role of radiation-induced structural disorder in driving the crystalline-to-amorphous phase transformation is discussed. 25 refs., 4 figs

Magnesium-rich intermetallics RE3RuMg7 (RE = Y, Nd, Dy, Ho). Rows of condensed Ru rate at RE6/2 octahedra in magnesium matrices

International Nuclear Information System (INIS)

Kersting, Marcel; Rodewald, Ute C.; Schwickert, Christian; Poettgen, Rainer

2013-01-01

The magnesium-rich intermetallic phases RE 3 RuMg 7 (RE = Y, Nd, Dy, Ho) have been synthesized from the elements in sealed niobium ampoules and subsequently characterized by powder X-ray diffraction. The structure of the dysprosium compound was refined on the basis of single-crystal X-ray diffractometer data: Ti 6 Sn 5 type, P6 3 /mmc, a = 1019.1(2), c = 606.76(9) pm, wR2 = 0.0159, 439 F 2 values, 19 variables. The Mg3 site shows a small degree of Mg3/Dy mixing, leading to the composition Dy 3.03 RuMg 6.97 for the investigated crystal. The striking structural motifs in the Dy 3 RuMg 7 structure are rows of face-sharing Ru rate at Dy 6 octahedra and corner-sharing Mg2 rate at Mg 8 Dy 4 icosahedra. The rows of octahedra form a hexagonal rod-packing, and each rod is enrolled by six rows of the condensed icosahedra. Temperature-dependent magnetic susceptibility measurements of Dy 3 RuMg 7 show Curie-Weiss behavior with an experimental magnetic moment of 10.66(1) μ B per Dy atom. Antiferromagnetic ordering is detected at T N = 27.5(5) K. The 5 K isotherm shows a metamagnetic transition at a critical field of H C = 40 kOe. (orig.)

The nuclear quadrupole interaction of {sup 181}Ta in the intermetallic compound Hf{sub 2}Rh

Energy Technology Data Exchange (ETDEWEB)

Ivanovic, N.; Koicki, S.; Cekic, B.; Manasijevic, M.; Koteski, V.; Marjanovic, D. [Institute of Nuclear Sciences VINCA, Laboratory for Nuclear and Plasma Physics, PO Box 522, Belgrade (Yugoslavia)

1999-01-11

The time differential perturbed angular correlation technique has been used to measure the electric field gradient at {sup 181}Ta impurities in the intermetallic compound Hf{sub 2}Rh. The results of the measurements show the presence of two independent quadrupole interactions. At room temperature the interaction frequencies are {omega}{sub Q1} = 58 Mrad s{sup -1} and {omega}{sub Q2} = 239 Mrad s{sup -1}. The electric field gradient V{sub 22}, the corresponding asymmetry parameter {eta} and the distribution parameter {delta} exhibit a pronounced temperature dependence from 78 to 1223 K. (author)

On the valence state of Yb and Ce in transition metal intermetallic compounds

International Nuclear Information System (INIS)

Boer, F.R. de; Dijkman, W.H.; Mattens, W.C.M.

1979-01-01

In the pure state Yb is a divalent metal, similar to Ca; in alloys it can become trivalent like the majority of the rare earth metals. Using a value of 38 kJ (mol Yb) -1 for the energy difference between divalent and trivalent Yb metal and using model calculations for the heat of formation of intermetallic compounds, the authors are able to account for the existing information on the valence state of Yb in transition metal compounds. A similar analysis of compounds of Ce with transition metals shows that a model in which the 4f electron is treated as a core electron, i.e. being absent in the tetravalent modification of Ce and present as a fully localized electron in trivalent Ce, does not apply. (Auth.)

Microstructural and wear characteristics of cobalt free, nickel base intermetallic alloy deposited by laser cladding

International Nuclear Information System (INIS)

Awasthi, Reena; Kumar, Santosh; Viswanadham, C.S.; Srivastava, D.; Dey, G.K.; Limaye, P.K.

2011-01-01

This paper describes the microstructural and wear characteristics of Ni base intermetallic hardfacing alloy (Tribaloy-700) deposited on stainless steel-316 L substrate by laser cladding technique. Cobalt base hardfacing alloys have been most commonly used hardfacing alloys for application involving wear, corrosion and high temperature resistance. However, the high cost and scarcity of cobalt led to the development of cobalt free hardfacing alloys. Further, in the nuclear industry, the use of cobalt base alloys is limited due to the induced activity of long lived radioisotope 60 Co formed. These difficulties led to the development of various nickel and iron base alloys to replace cobalt base hardfacing alloys. In the present study Ni base intermetallic alloy, free of Cobalt was deposited on stainless steel- 316 L substrate by laser cladding technique. Traditionally, welding and thermal spraying are the most commonly employed hardfacing techniques. Laser cladding has been explored for the deposition of less diluted and fusion-bonded Nickel base clad layer on stainless steel substrate with a low heat input. The laser cladding parameters (Laser power density: 200 W/mm 2 , scanning speed: 430 mm/min, and powder feed rate: 14 gm/min) resulted in defect free clad with minimal dilution of the substrate. The microstructure of the clad layer was examined by Optical microscopy, Scanning electron microscopy, with energy dispersive spectroscopy. The phase analysis was performed by X-ray diffraction technique. The clad layer exhibited sharp substrate/clad interface in the order of planar, cellular, and dendritic from the interface upwards. Dilution of clad with Fe from substrate was very low passing from ∼ 15% at the interface (∼ 40 μm) to ∼ 6% in the clad layer. The clad layer was characterized by the presence of hexagonal closed packed (hcp, MgZn 2 type) intermetallic Laves phase dispersed in the eutectic of Laves and face centered cubic (fcc) gamma solid solution. The

Fabrication, interfacial characterization and mechanical properties of continuous Al{sub 2}O{sub 3} ceramic fiber reinforced Ti/Al{sub 3}Ti metal-intermetallic laminated (CCFR-MIL) composite

Energy Technology Data Exchange (ETDEWEB)

Han, Yuqiang; Lin, Chunfa; Han, Xiaoxiao; Chang, Yunpeng; Guo, Chunhuan, E-mail: guochunhuan@hrbeu.edu.cn; Jiang, Fengchun, E-mail: fengchunjiang@hrbeu.edu.cn

2017-03-14

Continuous Al{sub 2}O{sub 3} ceramic fiber reinforced Ti/Al{sub 3}Ti metal-intermetallic laminated (CCFR-MIL) composite was fabricated using a vacuum hot pressing (VHP) sintering method and followed by hot isostatic pressing (HIP). The microstructure characteristics of the interfaces between Ti and Al{sub 3}Ti, as well as Al{sub 2}O{sub 3} fiber and Al{sub 3}Ti intermetallic were analyzed by scanning electron microscopy (SEM). Elemental distribution in the interfacial reaction zones were quantitatively examined by energy-dispersive spectroscopy (EDS). The phases in the composite were identified by X-ray diffractometer (XRD). The mechanical properties of the CCFR-MIL composite were measured using compression and tensile tests under quasi-static strain rate. The experimental results indicated that the residual Al was found in Al{sub 3}Ti intermetallic layer of CCFR-MIL composite. The interfacial reactions occurred during HIP and the reaction products were determined to be Al{sub 2}Ti, TiSi{sub 2}, TiO{sub 2} and Al{sub 2}SiO{sub 5} phases. Compared to Ti/Al{sub 3}Ti MIL composite without fiber reinforcement, both the strength and failure strain of CCFR-MIL composite under both compressive and tensile stress states increased due to the contribution of the continuous ceramic Al{sub 2}O{sub 3} fiber.

Effects of Nb content on the Zr{sub 2}Fe intermetallic stability

Energy Technology Data Exchange (ETDEWEB)

Ramos, C. E-mail: ciramos@cnea.gov.ar; Saragovi, C.; Granovsky, M.; Arias, D

2003-02-01

With the aim of studying the stability range of the Zr{sub 2}Fe intermetallic when adding Nb, the range of existence of the cubic ternary phase ({lambda}{sub 1}) and the corresponding two-phase field between them, four samples were analyzed, each one containing 35 at.% Fe and different at.% Nb: 0.5, 4 10 and 15. Optical and scanning electron metallographies, X-ray diffraction, microprobe analysis and Moessbauer spectroscopy were performed to determine and characterize the phases present in the samples. Results show that the Zr{sub 2}Fe compound accepts up to nearly 0.5 at.% Nb in solution, since the Zr{sub 2}Fe+{lambda}{sub 1} region is stable in the (0.5-3.5) at.% Nb range. To summarize these results an 800 deg. C section of the ternary Zr-Nb-Fe diagram, in the studied zone, was proposed.

Hydrogen in intermetallic phases: the system titanium--nickel--hydrogen. Wasserstoff in intermetallischen phasen am beispiel des systems titan-nickel-wasserftoff

Energy Technology Data Exchange (ETDEWEB)

Buchner, H.; Gutjahr, M. A.; Beccu, K. D.; Saeufferer, H.

1972-07-01

The intermetallic phases Ti/sub 2/-Ni (E9/sub 3/-type) and TiNi (B2-type) are able to absorb great amounts of hydrogen interstitially. The E9/sub 3/-structure forms four isotypic hydrogen phases, the lattice parameters of which increase with increasing hydrogen contents (..delta..d/sub max/ = 5.3%). The stoichiometric formulas are: Ti/sub 2/NiH/sub 0/./sub 5/; Ti/sub 2/NiH; Ti/sub 2/NiH/sub 2/; Ti/sub 2/NiH/sub 2/./sub 5/. The lattice parameter of the B2-structure increases from 3.01 A to 3.10 A (..delta..d = 3%), thus forming the stoichiometric TiNiH phase. The TiNiH structure possesses an eight-fold superlattice having a B2 type cell. The positions of hydrogen in the two intermetallic phases Ti/sub 2/Ni and TiNi are discussed from the geometrical point of view. Neutron diffraction diagrams verify these positions for only two hydrogen phases (Ti/sub 2/NiH/sub 0/./sub 5/; Ti/sub 2/NiH). Because of extreme experimental difficulties, the exact hydrogen positions in the phases Ti/sub 2/NiH/sub 2/; Ti/sub 2/NiH/sub 2/./sub 5/; TiNiH are still unknown.

Fracture toughness of intermetallics using a micro-mechanical probe

International Nuclear Information System (INIS)

Gerberich, W.W.; Venkataraman, S.K.; Hoehn, J.W.; Marsh, P.G.

1993-01-01

A novel technique for determining the fracture toughness of brittle intermetallics is presented, wherein very small samples are used and multiple tests are easily conducted on a flat polished surface. The fracture toughness of single crystal NiAl and polycrystalline Al 3 Sc are evaluated with this continuous microscratch technique at scratch rates ranging from 0.5 to greater than 100 μm s - . For comparison, small compact tension samples of (100) NiAl are evaluated at applied stress intensity rates ranging from 1.5 to 5,400 MPa-m 1/2 s -1 . Good comparison of microscratch toughness to compact tension K Ic values are obtained in this study for (001) NiAl, 10.6 vs. 10.0 MPa-m 1/2 , from the literature for (001) , 13.5 vs. 12.2 MPa-m 1/2 , and from the literature for polycrystalline Al 3 Sc, 3.5 vs. 3.1 MPa-m 1/2 . Also, the fracture toughness of both NiAl and Al 3 Sc are found to be strongly dependent on strain rate at room temperature with toughness dropping by an order of magnitude over a decade increase in rate. Possible reasons and implications to improving low temperature brittleness are discussed

Shock response of Ni/Al reactive inter-metallic composites

Science.gov (United States)

Cherukara, Mathew; Germann, Timothy; Kober, Edward; Strachan, Alejandro

2014-03-01

Intermolecular reactive composites find diverse applications in defense, microelectronics and medicine, where strong, localized sources of heat are required. Motivated by experimental work which has shown that high-energy ball milling can significantly improve the reactivity as well as the ease of ignition of Ni/Al inter-metallic composites, we present large scale (~41 million atom) molecular dynamics simulations of shock-induced chemistry in porous, polycrystalline, lamellar Ni/Al nano-composites, which are designed to capture the microstructure that is obtained post milling. Shock propagation in these porous, lamellar materials is observed to be extremely diffuse, leading to substantial inhomogeneity in the local stress states of the material. We describe the importance of pores as sites of initiation, where local temperatures can rise to several thousands of degrees, and chemical mixing is accelerated by vortex formation and jetting in the pore. We also follow the evolution of the chemistry after the shock passage by allowing the sample to ``cook'' under the shock induced pressures and temperatures for up to 0.5 ns. Multiple ``tendril-like'' reaction fronts, born in the cauldron of the pores, propagate rapidly through the sample, consuming it within a nanosecond. US Defense Threat Reduction Agency, Contract No. HDTRA1-10-1-0119.

[Zn(NH3)4][PtCl6] and [Cd(NH3)4][PtCl6] as precursors for intermetallic compounds PtZn and PtCd

International Nuclear Information System (INIS)

Zadesenets, A.V.; Venediktov, A.B.; Shubin, Yu.V.; Korenev, S.V.

2007-01-01

Double complex salts (tetraamminezinc and tetraamminecadmium hexachloroplatinates) have been synthesized. Their thermal properties have been studied, as well as the products of their degradation in hydrogen and helium atmospheres. Optimal thermolysis schedules have been determined. Thermolysis under hydrogen yields intermetallic compounds PtZn and PtCd [ru

Optimization of Causative Factors for Landslide Susceptibility Evaluation Using Remote Sensing and GIS Data in Parts of Niigata, Japan.

Directory of Open Access Journals (Sweden)

Jie Dou

Full Text Available This paper assesses the potentiality of certainty factor models (CF for the best suitable causative factors extraction for landslide susceptibility mapping in the Sado Island, Niigata Prefecture, Japan. To test the applicability of CF, a landslide inventory map provided by National Research Institute for Earth Science and Disaster Prevention (NIED was split into two subsets: (i 70% of the landslides in the inventory to be used for building the CF based model; (ii 30% of the landslides to be used for the validation purpose. A spatial database with fifteen landslide causative factors was then constructed by processing ALOS satellite images, aerial photos, topographical and geological maps. CF model was then applied to select the best subset from the fifteen factors. Using all fifteen factors and the best subset factors, landslide susceptibility maps were produced using statistical index (SI and logistic regression (LR models. The susceptibility maps were validated and compared using landslide locations in the validation data. The prediction performance of two susceptibility maps was estimated using the Receiver Operating Characteristics (ROC. The result shows that the area under the ROC curve (AUC for the LR model (AUC = 0.817 is slightly higher than those obtained from the SI model (AUC = 0.801. Further, it is noted that the SI and LR models using the best subset outperform the models using the fifteen original factors. Therefore, we conclude that the optimized factor model using CF is more accurate in predicting landslide susceptibility and obtaining a more homogeneous classification map. Our findings acknowledge that in the mountainous regions suffering from data scarcity, it is possible to select key factors related to landslide occurrence based on the CF models in a GIS platform. Hence, the development of a scenario for future planning of risk mitigation is achieved in an efficient manner.

Optimization of Causative Factors for Landslide Susceptibility Evaluation Using Remote Sensing and GIS Data in Parts of Niigata, Japan.

Science.gov (United States)

Dou, Jie; Tien Bui, Dieu; Yunus, Ali P; Jia, Kun; Song, Xuan; Revhaug, Inge; Xia, Huan; Zhu, Zhongfan

2015-01-01

This paper assesses the potentiality of certainty factor models (CF) for the best suitable causative factors extraction for landslide susceptibility mapping in the Sado Island, Niigata Prefecture, Japan. To test the applicability of CF, a landslide inventory map provided by National Research Institute for Earth Science and Disaster Prevention (NIED) was split into two subsets: (i) 70% of the landslides in the inventory to be used for building the CF based model; (ii) 30% of the landslides to be used for the validation purpose. A spatial database with fifteen landslide causative factors was then constructed by processing ALOS satellite images, aerial photos, topographical and geological maps. CF model was then applied to select the best subset from the fifteen factors. Using all fifteen factors and the best subset factors, landslide susceptibility maps were produced using statistical index (SI) and logistic regression (LR) models. The susceptibility maps were validated and compared using landslide locations in the validation data. The prediction performance of two susceptibility maps was estimated using the Receiver Operating Characteristics (ROC). The result shows that the area under the ROC curve (AUC) for the LR model (AUC = 0.817) is slightly higher than those obtained from the SI model (AUC = 0.801). Further, it is noted that the SI and LR models using the best subset outperform the models using the fifteen original factors. Therefore, we conclude that the optimized factor model using CF is more accurate in predicting landslide susceptibility and obtaining a more homogeneous classification map. Our findings acknowledge that in the mountainous regions suffering from data scarcity, it is possible to select key factors related to landslide occurrence based on the CF models in a GIS platform. Hence, the development of a scenario for future planning of risk mitigation is achieved in an efficient manner.

Evaluation of precipitates used in strainer head loss testing: Part II. Precipitates by in situ aluminum alloy corrosion

International Nuclear Information System (INIS)

Bahn, Chi Bum; Kasza, Ken E.; Shack, William J.; Natesan, Ken; Klein, Paul

2011-01-01

Graphical abstract: Display Omitted Research highlights: → Sump strainer head loss testing to evaluate chemical effects. → Aluminum hydroxide precipitates by in situ Al alloy corrosion caused head loss. → Intermetallic particles released from Al alloy can also cause significant head loss. → When evaluating Al effect on head loss, intermetallics should be considered. - Abstract: Vertical loop head loss tests were performed with 6061 and 1100 aluminum (Al) alloy plates immersed in borated solution at pH = 9.3 at room temperature and 60 o C. The results suggest that the potential for corrosion of an Al alloy to result in increased head loss across a glass fiber bed may depend on its microstructure, i.e., the size distribution and number density of intermetallic particles that are present in Al matrix and FeSiAl ternary compounds, as well as its Al release rate. Per unit mass of Al removed from solution, the WCAP-16530 aluminum hydroxide (Al(OH) 3 ) surrogate was more effective in increasing head loss than the Al(OH) 3 precipitates formed in situ by corrosion of Al alloy. However, in choosing a representative amount of surrogate for plant specific testing, consideration should be given to the potential for additional head losses due to intermetallic particles and the apparent reduction in the effective solubility of Al(OH) 3 when intermetallic particles are present.

Pressure induced helimagnetism in Fe-based (Y.sub.2./sub.Fe.sub.17./sub., Lu.sub.2./sub.Fe.sub.17./sub.) intermetallic compounds

Czech Academy of Sciences Publication Activity Database

Kamarád, Jiří; Prokhnenko, Olexandr; Prokeš, K.; Arnold, Zdeněk; Andreev, Alexander V.

2007-01-01

Roč. 310, - (2007), s. 1801-1803 ISSN 0304-8853 R&D Projects: GA ČR GA202/06/0178 Institutional research plan: CEZ:AV0Z10100521 Keywords : magnetic structure * Fe-base intermetallics * Y 2 Fe 17 * pressure effects Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.704, year: 2007

Melt impregnation as a post processing treatment for performance enhancement in high capacity 3D microporous tin-copper-nickel intermetallic anode for Li-ion battery supported by electrodeposited nickel scaffold: A structural study

Science.gov (United States)

Sengupta, Srijan; Patra, Arghya; Mitra, Arijit; Jena, Sambedan; Das, Karabi; Majumder, Subhasish Basu; Das, Siddhartha

2018-05-01

This paper communicates stabilization of a Sn anode by impregnating it within the porous framework of a Ni-scaffold. The impregnation is carried out by electrodeposition Sn on Ni-foam followed by heating at 300 °C for 1 h. The Ni-foam was also electrodeposited on a Cu foil prior to deposition of Sn. The melting step leads to the formation of Nisbnd Sn and Cusbnd Sn intermetallics within pores of the Ni-scaffold. Snsbnd Cu/Ni intermetallics lithiate following the active-inactive strategy in which the inactive Cu/Ni buffers the volume expansion while Sn lithiates. Furthermore, this entire process takes place within Ni-scaffold which resists material pulverization and delamination and provide better electronic pathway for charge transfer. This active-inactive Sn:Snsbnd Cu/Ni intermetallic within a protected Ni-scaffold assembly results in 100th cycle discharge capacity of 587.9 mA h/g at a rate of 500 mA/g (0.5 C), and superior rate capability delivering 463 mAh/g at a rate of 2 A/g (2 C) while retaining structural integrity as compared to pure Sn electrodeposited (without heat-treatment) on the nickel scaffold.

Susceptibility to eating disorders among collegiate female student-athletes.

Science.gov (United States)

McLester, Cherilyn N; Hardin, Robin; Hoppe, Stephanie

2014-01-01

Research has suggested that the prevalence of young women with eating disorders (EDs) is increasing, but determining the exact prevalence of EDs within the female student-athlete (FS-A) population is difficult. Looking at certain traits may help us to identify their level of susceptibility to developing an ED. To determine the susceptibility of FS-As to EDs in relation to self-concept, including self-esteem and body image. Cross-sectional study. Athletic training and health centers at National Collegiate Athletic Association Division I, II, and III institutions via e-mail questionnaire correspondence. A total of 439 FS-As from 17 participating institutions completed the questionnaires. The sample was primarily white (83.1%) and underclass (61.8%). The questionnaire consisted of 4 parts: 3 subscales of the Eating Disorder Inventory-2, the Rosenberg Self-Esteem Scale, the Body Cathexis Scale, and demographic items. A total of 6.8% of FS-As were susceptible to anorexia and 1.8% were susceptible to bulimia. The majority of FS-As (61%) reported normal self-esteem levels, whereas 29.4% had high self-esteem. Overall, 64.5% were satisfied and 23% were very satisfied with their body image. These results are generally positive in that they suggest FS-As have high levels of self-concept and are at low risk to develop EDs. However, these findings do not mean that all concerns should be dismissed. Although more than 90% of the respondents were not susceptible to an ED, there are still FS-As who may be. Athletic departments should evaluate their FS-As' levels of self-concept so that their susceptibility to EDs can be addressed. The emotional aspect of health care should be included in providing holistic care for student-athletes. Athletic trainers often are the primary health care providers for FS-As, so they should be made aware of this concern.

Reliable and cost effective design of intermetallic Ni2Si nanowires and direct characterization of its mechanical properties

OpenAIRE

Seung Zeon Han; Joonhee Kang; Sung-Dae Kim; Si-Young Choi; Hyung Giun Kim; Jehyun Lee; Kwangho Kim; Sung Hwan Lim; Byungchan Han

2015-01-01

We report that a single crystal Ni2Si nanowire (NW) of intermetallic compound can be reliably designed using simple three-step processes: casting a ternary Cu-Ni-Si alloy, nucleate and growth of Ni2Si NWs as embedded in the alloy matrix via designing discontinuous precipitation (DP) of Ni2Si nanoparticles and thermal aging, and finally chemical etching to decouple the Ni2Si NWs from the alloy matrix. By direct application of uniaxial tensile tests to the Ni2Si NW we characterize its mechanica...

Improving of Corrosion Resistance of Aluminum Alloys by Removing Intermetallic Compound

International Nuclear Information System (INIS)

Seri, Osami

2008-01-01

It is well known that iron is one of the most common impurity elements sound in aluminum and its alloys. Iron in the aluminum forms an intermetallic compounds such as FeAl 3 . The FeAl 3 particles on the aluminum surface are one of the most detrimental phases to the corrosion process and anodizing procedure for aluminum and its alloys. Trial and error surface treatment will be carried out to find the preferential and effective removal of FeAl 3 particles on the surfaces without dissolution of aluminum matrix around the particles. One of the preferable surface treatments for the aim of getting FeAl 3 free surface was an electrochemical treatment such as cathodic current density of -2 kAm -2 in a 20-30 mass% HNO 3 solution for the period of 300s. The corrosion characteristics of aluminum surface with FeAl 3 free particles are examined in a 0.1 kmol/m 3 NaCl solution. It is found that aluminum with free FeAl 3 particles shows higher corrosion resistance than aluminum with FeAl 3 particles

Mechanical Behavior and Fracture Properties of NiAl Intermetallic Alloy with Different Copper Contents

Directory of Open Access Journals (Sweden)

Tao-Hsing Chen

2016-03-01

Full Text Available The deformation behavior and fracture characteristics of NiAl intermetallic alloy containing 5~7 at% Cu are investigated at room temperature under strain rates ranging from 1 × 10−3 to 5 × 103 s−1. It is shown that the copper contents and strain rate both have a significant effect on the mechanical behavior of the NiAl alloy. Specifically, the flow stress increases with an increasing copper content and strain rate. Moreover, the ductility also improves as the copper content increases. The change in the mechanical response and fracture behavior of the NiAl alloy given a higher copper content is thought to be the result of the precipitation of β-phase (Ni,CuAl and γ'-phase (Ni,Cu3Al in the NiAl matrix.

Penicillin-susceptible Staphylococcus aureus: susceptibility testing, resistance rates and outcome of infection.

Science.gov (United States)

Hagstrand Aldman, Malin; Skovby, Annette; I Påhlman, Lisa

2017-06-01

Staphylococcus aureus (SA) is an important human pathogen that causes both superficial and invasive infections. Penicillin is now rarely used in the treatment of SA infections due to widespread resistance and a concern about the accuracy of existing methods for penicillin susceptibility testing. The aims of the present study were to determine the frequency of penicillin-susceptible SA isolates from blood and wound cultures in Lund, Sweden, and to evaluate methods for penicillin testing in SA. We also wanted to investigate if penicillin-susceptible isolates are associated with higher mortality. Hundred blood culture isolates collected 2008/2009, 140 blood culture isolates from 2014/2015, and 141 superficial wound culture strains from 2015 were examined. Penicillin susceptibility was tested with disk diffusion according to EUCAST guidelines, and results were confirmed with a cloverleaf assay and PCR amplification of the BlaZ gene. Patient data for all bacteraemia cases were extracted from medical records. The disk diffusion method with assessment of both zone size and zone edge appearance had high accuracy in our study. About 57% of bacteraemia isolates from 2008/2009 were sensitive to penicillin compared to 29% in 2014/2015 (p penicillin susceptible. There was no difference in co-morbidity or mortality rates between patients with penicillin resistant and penicillin sensitive SA bacteraemia. Disk-diffusion is a simple and reliable method to detect penicillin resistance in SA, and susceptibility rates are significant. Penicillin has many theoretical advantages and should be considered in the treatment of SA bacteraemia when susceptible.

The Role of Abcb5 Alleles in Susceptibility to Haloperidol-Induced Toxicity in Mice and Humans

Science.gov (United States)

Zheng, Ming; Zhang, Haili; Dill, David L.; Clark, J. David; Tu, Susan; Yablonovitch, Arielle L.; Tan, Meng How; Zhang, Rui; Rujescu, Dan; Wu, Manhong; Tessarollo, Lino; Vieira, Wilfred; Gottesman, Michael M.; Deng, Suhua; Eberlin, Livia S.; Zare, Richard N.; Billard, Jean-Martin; Gillet, Jean-Pierre; Li, Jin Billy; Peltz, Gary

2015-01-01

Background We know very little about the genetic factors affecting susceptibility to drug-induced central nervous system (CNS) toxicities, and this has limited our ability to optimally utilize existing drugs or to develop new drugs for CNS disorders. For example, haloperidol is a potent dopamine antagonist that is used to treat psychotic disorders, but 50% of treated patients develop characteristic extrapyramidal symptoms caused by haloperidol-induced toxicity (HIT), which limits its clinical utility. We do not have any information about the genetic factors affecting this drug-induced toxicity. HIT in humans is directly mirrored in a murine genetic model, where inbred mouse strains are differentially susceptible to HIT. Therefore, we genetically analyzed this murine model and performed a translational human genetic association study. Methods and Findings A whole genome SNP database and computational genetic mapping were used to analyze the murine genetic model of HIT. Guided by the mouse genetic analysis, we demonstrate that genetic variation within an ABC-drug efflux transporter (Abcb5) affected susceptibility to HIT. In situ hybridization results reveal that Abcb5 is expressed in brain capillaries, and by cerebellar Purkinje cells. We also analyzed chromosome substitution strains, imaged haloperidol abundance in brain tissue sections and directly measured haloperidol (and its metabolite) levels in brain, and characterized Abcb5 knockout mice. Our results demonstrate that Abcb5 is part of the blood-brain barrier; it affects susceptibility to HIT by altering the brain concentration of haloperidol. Moreover, a genetic association study in a haloperidol-treated human cohort indicates that human ABCB5 alleles had a time-dependent effect on susceptibility to individual and combined measures of HIT. Abcb5 alleles are pharmacogenetic factors that affect susceptibility to HIT, but it is likely that additional pharmacogenetic susceptibility factors will be discovered

The role of Abcb5 alleles in susceptibility to haloperidol-induced toxicity in mice and humans.

KAUST Repository

Zheng, Ming

2015-02-03

We know very little about the genetic factors affecting susceptibility to drug-induced central nervous system (CNS) toxicities, and this has limited our ability to optimally utilize existing drugs or to develop new drugs for CNS disorders. For example, haloperidol is a potent dopamine antagonist that is used to treat psychotic disorders, but 50% of treated patients develop characteristic extrapyramidal symptoms caused by haloperidol-induced toxicity (HIT), which limits its clinical utility. We do not have any information about the genetic factors affecting this drug-induced toxicity. HIT in humans is directly mirrored in a murine genetic model, where inbred mouse strains are differentially susceptible to HIT. Therefore, we genetically analyzed this murine model and performed a translational human genetic association study.A whole genome SNP database and computational genetic mapping were used to analyze the murine genetic model of HIT. Guided by the mouse genetic analysis, we demonstrate that genetic variation within an ABC-drug efflux transporter (Abcb5) affected susceptibility to HIT. In situ hybridization results reveal that Abcb5 is expressed in brain capillaries, and by cerebellar Purkinje cells. We also analyzed chromosome substitution strains, imaged haloperidol abundance in brain tissue sections and directly measured haloperidol (and its metabolite) levels in brain, and characterized Abcb5 knockout mice. Our results demonstrate that Abcb5 is part of the blood-brain barrier; it affects susceptibility to HIT by altering the brain concentration of haloperidol. Moreover, a genetic association study in a haloperidol-treated human cohort indicates that human ABCB5 alleles had a time-dependent effect on susceptibility to individual and combined measures of HIT. Abcb5 alleles are pharmacogenetic factors that affect susceptibility to HIT, but it is likely that additional pharmacogenetic susceptibility factors will be discovered.ABCB5 alleles alter susceptibility to

A highly active PtCu3 intermetallic core-shell, multilayered Pt-skin, carbon embedded electrocatalyst produced by a scale-up sol-gel synthesis.

Science.gov (United States)

Bele, M; Jovanovič, P; Pavlišič, A; Jozinović, B; Zorko, M; Rečnik, A; Chernyshova, E; Hočevar, S; Hodnik, N; Gaberšček, M

2014-11-07

We present a novel, scaled-up sol-gel synthesis which enables one to produce 20 g batches of highly active and stable carbon supported PtCu3 nanoparticles as cathode materials for low temperature fuel cell application. We confirm the presence of an ordered intermetallic phase underneath a multilayered Pt-skin together with firm embedment of nanoparticles in the carbon matrix.

Nodal infection in Markovian susceptible-infected-susceptible and susceptible-infected-removed epidemics on networks are non-negatively correlated.

Science.gov (United States)

Cator, E; Van Mieghem, P

2014-05-01

By invoking the famous Fortuin, Kasteleyn, and Ginibre (FKG) inequality, we prove the conjecture that the correlation of infection at the same time between any pair of nodes in a network cannot be negative for (exact) Markovian susceptible-infected-susceptible (SIS) and susceptible-infected-removed (SIR) epidemics on networks. The truth of the conjecture establishes that the N-intertwined mean-field approximation (NIMFA) upper bounds the infection probability in any graph so that network design based on NIMFA always leads to safe protections against malware spread. However, when the infection or/and curing are not Poisson processes, the infection correlation between two nodes can be negative.

Nodal infection in Markovian susceptible-infected-susceptible and susceptible-infected-removed epidemics on networks are non-negatively correlated

Science.gov (United States)

Cator, E.; Van Mieghem, P.

2014-05-01

By invoking the famous Fortuin, Kasteleyn, and Ginibre (FKG) inequality, we prove the conjecture that the correlation of infection at the same time between any pair of nodes in a network cannot be negative for (exact) Markovian susceptible-infected-susceptible (SIS) and susceptible-infected-removed (SIR) epidemics on networks. The truth of the conjecture establishes that the N-intertwined mean-field approximation (NIMFA) upper bounds the infection probability in any graph so that network design based on NIMFA always leads to safe protections against malware spread. However, when the infection or/and curing are not Poisson processes, the infection correlation between two nodes can be negative.

Synthesis, Characterization and Properties of Nanoparticles of Intermetallic Compounds

Energy Technology Data Exchange (ETDEWEB)

DiSalvo, Francis J. [Cornell Univ., Ithaca, NY (United States)

2015-03-12

The research program from 2010 to the end of the grant focused on understanding the factors important to the synthesis of single phase intermetallic nano-particles (NPs), their size, crystalline order, surface properties and electrochemical activity. The synthetic method developed is a co-reduction of mixtures of single metal precursors by strong, soluble reducing agents in a non-protic solvent, tetrahydrofuran (THF). With some exceptions, the particles obtained by room temperature reduction are random alloys that need to be annealed at modest temperatures (200 to 600 °C) in order to develop an ordered structure. To avoid significant particle size growth and agglomeration, the particles must be protected by surface coatings. We developed a novel method of coating the metal nanoparticles with KCl, a by-product of the reduction reaction if the proper reducing agents are employed. In that case, a composite product containing individual metal nanoparticles in a KCl matrix is obtained. The composite can be heated to at least 600 °C without significant agglomeration or growth in particle size. Washing the annealed product in the presence of catalyst supports in ethylene glycol removes the KCl and deposits the particles on the support. Six publications present the method and its application to producing and studying new catalyst/support combinations for fuel cell applications. Three publications concern the use of related methods to explore new lithium-sulfur battery concepts.

Computer simulations of disordering kinetics in irradiated intermetallic compounds

International Nuclear Information System (INIS)

Spaczer, M.; Caro, A.; Victoria, M.; Diaz de la Rubia, T.

1994-01-01

Molecular-dynamics computer simulations of collision cascades in intermetallic Cu 3 Au, Ni 3 Al, and NiAl have been performed to study the nature of the disordering processes in the collision cascade. The choice of these systems was suggested by the quite accurate description of the thermodynamic properties obtained using embedded-atom-type potentials. Since melting occurs in the core of the cascades, interesting effects appear as a result of the superposition of the loss (and subsequent recovery) of the crystalline order and the evolution of the chemical order, both processes being developed on different time scales. In our previous simulations on Ni 3 Al and Cu 3 Au [T. Diaz de la Rubia, A. Caro, and M. Spaczer, Phys. Rev. B 47, 11 483 (1993)] we found a significant difference between the time evolution of the chemical short-range order (SRO) and the crystalline order in the cascade core for both alloys, namely the complete loss of the crystalline structure but only partial chemical disordering. Recent computer simulations in NiAl show the same phenomena. To understand these features we study the liquid phase of these three alloys and present simulation results concerning the dynamical melting of small samples, examining the atomic mobility, the relaxation time, and the saturation value of the chemical short-range order. An analytic model for the time evolution of the SRO is given

Intermetallic bonds and midgap interface states at epitaxial Al/GaAs(001) junctions

International Nuclear Information System (INIS)

Maxisch, T.; Baldereschi, A.; Binggeli, N.

2003-03-01

Using first-principles pseudopotential calculations, we have investigated the nature of the electronic states with energies within the semiconductor bandgap of abrupt, defect-free As-terminated Al/GaAs(001) junctions. While bonding-/antibonding-like semiconductor evanescent states occur near the valence-/conduction-band edges, the semiconductor midgap region is characterized by a new type of electronic states, not accounted for by commonly accepted models. These states, which correspond to intermetallic bonds between the outermost Ga cations of the semiconductor and Al atoms of the metal, occur near the Fermi energy. They are localized at the interface and are located around the J-point of the Brillouin zone. These new interface states derive from an interaction between localized states of the Al(001) surface and bulk GaAs conduction band states, mediated by localized states of the unreconstructed As-terminated GaAs(001) surface. (author)

Formation and transformation of binary intermetallic phases in high purity Al-Fe alloys

International Nuclear Information System (INIS)

Griger, A.; Stefaniay, V.; Kovacs-Csetenyi, E.; Turmezey, T.

1990-01-01

The solid solubility of iron in aluminium is very low (<0.04%), (all compositions are given in w%) therefore most of the iron content appears as intermetallic phases in combination with aluminium and other elements. The amount of iron does not exceed the level of the eutectic concentration in the commercial aluminium alloys, however the non-desired effect of these primary phases of large size must be taken into consideration. In the case of rapid solidification (RS) the eutectic point shifts to higher values of iron content. The eutectic has a very fine structure and the primary phases formed at high cooling rates have also very low particle size. Because of it, for the sake of improvement of the thermo-mechanical properties of the RS aluminium alloys the quantity of iron can be increased up to 8-10%. Above this concentration the favourable properties do not develop while the elongation decreases

Microstructure and high temperature oxidation resistance of in-situ synthesized TiN/Ti{sub 3}Al intermetallic composite coatings on Ti6Al4V alloy by laser cladding process

Energy Technology Data Exchange (ETDEWEB)

Liu, Hongxi, E-mail: piiiliuhx@sina.com; Zhang, Xiaowei; Jiang, Yehua; Zhou, Rong

2016-06-15

High temperature anti-oxidation TiN/Ti{sub 3}Al intermetallic composite coatings were fabricated with the powder and AlN powder on Ti6Al4V titanium alloy surface by 6 kW transverse-flow CO{sub 2} laser apparatus. The chemical composition, morphology and microstructure of the TiN/Ti{sub 3}Al composite coatings were characterized by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy dispersive spectrometer (EDS). In order to evaluate the high temperature oxidation resistance of TiN/Ti{sub 3}Al coating, the isothermal oxidation test was performed in a high temperature resistance furnace at 600 °C and 800 °C, respectively. The result shows that the composite coating has a rapidly solidified fine microstructure consisting of TiN primary phase (granular-like, flake-like or dendrites), with an even distribution in Ti{sub 3}Al matrix. It indicates that a physical and chemical reaction between Ti powder and AlN powder has completely occurred under the laser irradiation condition. In addition, the microhardness of the TiN/Ti3Al intermetallic composite coating is 3.4 times higher than that of the Ti6Al4V alloy substrate and reaches 844 HV{sub 0.2}. The high temperature oxidation behavior test reveals that the high temperature oxidation resistance of TiN/Ti{sub 3}Al composite coating is much better than that of titanium alloy substrate. The excellent high temperature oxidation resistance of TiN/Ti{sub 3}Al intermetallic composite coating is attributed to the formation of reinforced phases TiN, Al{sub 2}O{sub 3} and TiO{sub 2}. The laser cladding TiN/Ti{sub 3}Al intermetallic composite coating is anticipated to be a promising high temperature oxidation resistance coating for Ti6Al4V alloy. - Highlights: • In-situ TiN/Ti{sub 3}Al composite coating was synthesized on Ti6Al4V alloy by laser cladding. • The influence of Ti and AlN molar ratio on the microstructure of the coating was studied. • The TiN/Ti{sub 3}Al intermetallic

Critical current density measurement of thin films by AC susceptibility based on the penetration parameter h

DEFF Research Database (Denmark)

Li, Xiao-Fen; Grivel, Jean-Claude; Abrahamsen, Asger B.

2012-01-01

We have numerically proved that the dependence of AC susceptibility χ of a E(J) power law superconducting thin disc on many parameters can be reduced to one penetration parameter h, with E the electric field and J the current density. Based on this result, we propose a way of measuring the critical...... current density Jc of superconducting thin films by AC susceptibility. Compared with the normally used method based on the peak of the imaginary part, our method uses a much larger range of the AC susceptibility curve, thus allowing determination of the temperature (T) dependence of Jc from a normally...

Superconducting Nb{sub 3}Sn intermetallics made by electrochemical reduction of Nb{sub 2}O{sub 5}-SnO{sub 2} oxides

Energy Technology Data Exchange (ETDEWEB)

Glowacki, B A; Fray, D J; Yan, X-Y; Chen, G

2003-05-01

The article is focused on low temperature superconducting Nb{sub 3}Sn material manufactured by novel electrodeoxidizing method developed in Cambridge whereby the range of alloys and intermetallics are produced cheaply making potential superconducting wires more cost effective. The process of direct electrochemical reduction of Nb{sub 2}O{sub 5}-SnO{sub 2} mixtures and in situ formation of the Nb{sub 3}Sn is discussed in details.

Microstructure and properties of Ti-Al intermetallic/Al2O3 layers produced on Ti6Al2Mo2Cr titanium alloy by PACVD method

Science.gov (United States)

Sitek, R.; Bolek, T.; Mizera, J.

2018-04-01

The paper presents investigation of microstructure and corrosion resistance of the multi-component surface layers built of intermetallic phases of the Ti-Al system and an outer Al2O3 ceramic sub-layer. The layers were produced on a two phase (α + β) Ti6Al2Mo2Cr titanium alloy using the PACVD method with the participation of trimethylaluminum vapors. The layers are characterized by a high surface hardness and good corrosion, better than that of these materials in the starting state. In order to find the correlation between their structure and properties, the layers were subjected to examinations using optical microscopy, X-ray diffraction analysis (XRD), surface analysis by XPS, scanning electron microscopy (SEM), and analyses of the chemical composition (EDS). The properties examined included: the corrosion resistance and the hydrogen absorptiveness. Moreover growth of the Al2O3 ceramic layer and its influence on the residual stress distribution was simulated using finite element method [FEM]. The results showed that the produced layer has amorphous-nano-crystalline structure, improved corrosion resistance and reduces the permeability of hydrogen as compared with the base material of Ti6Al2Mo2Cr -titanium alloy.

Ab initio study of the structural, electronic, elastic and thermal properties of RMn{sub 2}Ge{sub 2} (R = Ca, Nd and Y) intermetallic compounds

Energy Technology Data Exchange (ETDEWEB)

Miloud Abid, O.; Yakoubi, A. [Laboratoire d’Etudes des Matériaux et Instrumentations Expérimentales, Université Djilali Liabes de Sidi Bel-Abbes, 22000 (Algeria); Tadjer, A. [Modeling and Simulation in Materials Science Laboratory, Physics Department, University of Sidi Bel-Abbes, Sidi Bel-Abbes (Algeria); Khenata, R., E-mail: khenata_rabah@yahoo.fr [Laboratoire de Physique Quantique de la Modélisation Mathématique (LPQ3M), Université de Mascara, 29000 (Algeria); Ahmed, R. [Department of Physics, Faculty of Science, Universiti Teknologi Malaysia, UTM Skudai, 81310 Johor (Malaysia); Murtaza, G. [Materials Modeling Laboratory, Department of Physics, Islamia College University, Peshawar (Pakistan); Bin Omran, S. [Department of Physics and Astronomy, College of Science, King Saud University, P.O. Box 2455, Riyadh 11451 (Saudi Arabia); Azam, Sikander [New Technologies – Research Center, University of West Bohemia, Univerzitni 8, 306 14 Pilsen (Czech Republic)

2014-12-15

Highlights: • The calculated structural parameters of RMn{sub 2}Ge{sub 2} (R = Ca, Nd and Y) compounds are found in good agreement with the experimental data. • The structural and band structure calculation reveals that these compounds are ferromagnetic brittle metals. • The elastic and thermodynamic properties for the herein studied compounds are investigated for the first time. - Abstract: Intermetallic RMn{sub 2}Ge{sub 2} ternary compounds have attracted considerable attention from researchers in recent years because they show strong indications for novel magnetic characteristics and they have the potential to reveal the mechanism of superlattices. The study of the paramagnetic, ferromagnetic and antiferromagnetic phases affirms the strong dependence to the distance between atomic species in these compounds. In this study, we investigated the structural, elastic, electronic and thermodynamic properties of the intermetallic RMn{sub 2}Ge{sub 2} (R = Ca, Nd and Y) compounds. To carry out this study, we used the full potential (FP) linearized (L) augmented plane wave plus local orbitals (APW + lo), a scheme of calculations developed within the frame work of density functional theory (DFT). To incorporate the exchange correlation (XC) energy and corresponding potential into the total energy calculations, local density approximation (LDA) parameterized by Perdew and Wang is taken into account. Analysis of the density of states (DOS) profile illustrates the conducting nature of these intermetallic compounds; with a predominantly contribution from the R and Mn-d states. At ambient conditions, calculations for elastic constants (C{sub 11}, C{sub 12}, C{sub 13}, C{sub 44}, C{sub 33} and C{sub 66}) are also performed, which point to their brittle character. In addition, the quasi harmonic Debye model was used to predict the thermal properties, together with relative expansion coefficients and heat capacity.

Solid-state transformation of Fe-rich intermetallic phases in Al–5.0Cu–0.6Mn squeeze cast alloy with variable Fe contents during solution heat treatment

International Nuclear Information System (INIS)

Lin, Bo; Zhang, Weiwen; Zhao, Yuliang; Li, Yuanyuan

2015-01-01

The Al–5.0 wt.% Cu–0.6 wt.% Mn alloys with a variable Fe content were prepared by squeeze casting. Optical microscopy (OM), Deep etching technique, scanning electron microscopy(SEM), X-ray diffraction (XRD) and transmission electron microscopy (TEM) were used to examine the solid-state transformation of Fe-rich intermetallics during the solution heat treatment. The results showed that the Chinese script-like α-Fe, Al 6 (FeMn) and needle-like Al 3 (FeMn) phases transform to a new Cu-rich β-Fe (Al 7 Cu 2 (FeMn)) phase during solution heat treatment. The possible reaction and overall transformation kinetics of the solid-state phase transformation for the Fe-rich intermetallics were investigated. - Graphical abstract: Display Omitted - Highlights: • The α-Fe, Al 6 (FeMn) and Al 3 (FeMn) phases change to the β-Fe phases. • Possible reactions of Fe phases during solution heat treatment are discussed. • The overall fractional transformation rate follows an Avrami curve

Communicating Zika Risk: Using Metaphor to Increase Perceived Risk Susceptibility.

Science.gov (United States)

Lu, Hang; Schuldt, Jonathon P

2018-02-27

Effectively communicating the risks associated with emerging zoonotic diseases remains an important challenge. Drawing on research into the psychological effects of metaphoric framing, we explore the conditions under which exposure to the "nation as a body" metaphor influences perceived risk susceptibility, behavioral intentions, and policy support in the context of Zika virus. In a between-subjects experiment, 354 U.S. adults were randomly assigned to one of four experimental conditions as part of a 2 (severity message: high vs. low) × 2 (U.S. framing: metaphoric vs. literal) design. Results revealed an interaction effect such that metaphoric (vs. literal) framing increased perceived risk susceptibility in the high-severity condition only. Further analyses revealed that perceived risk susceptibility and negative affect mediated the path between the two-way interaction and policy support and behavioral intentions regarding Zika prevention. Overall, these findings complement prior work on the influence of metaphoric framing on risk perceptions, while offering practical insights for risk communicators seeking to communicate about Zika and other zoonotic diseases. © 2018 Society for Risk Analysis.

Nonlinear electromagnetic susceptibilities of unmagnetized plasmas

International Nuclear Information System (INIS)

Yoon, Peter H.

2005-01-01

Fully electromagnetic nonlinear susceptibilities of unmagnetized plasmas are analyzed in detail. Concrete expressions of the second-order nonlinear susceptibility are found in various forms in the literature, usually in connection with the discussions of various three-wave decay processes, but the third-order susceptibilities are rarely discussed. The second-order susceptibility is pertinent to nonlinear wave-wave interactions (i.e., the decay/coalescence), whereas the third-order susceptibilities affect nonlinear wave-particle interactions (i.e., the induced scattering). In the present article useful approximate analytical expressions of these nonlinear susceptibilities that can be readily utilized in various situations are derived

Crystal structure and electrical resistivity studies of Gd(Fe1-x Cox)2 intermetallics

International Nuclear Information System (INIS)

Onak, M.; Guzdek, P.; Stoch, P.; Chmist, J.; Bednarski, M.; Panta, A.; Pszczola, J.

2007-01-01

From X-ray analysis (295 K) it was found that the cubic, MgCu 2 -type, Fd3m crystal structure appears across the Gd(Fe 1-x Co x ) 2 series. Electrical resistivity measurements for the Gd(Fe 1-x Co x ) 2 intermetallics were performed in a wide temperature region and the parameters characterizing the resistivity dependence on temperature and composition were determined. The differential of the electrical resistivity against temperature was used to estimate Curie temperatures. The Curie temperature versus x, high and moderately increasing in the iron-rich area, rapidly drops in the cobalt-rich region. The obtained results are compared with the data known for the Dy(Fe 1-x Co x ) 2 series. The Curie temperature is related to both the number of 3d electrons and the de Gennes factor

Crystal Growth and Characterization of MT2Si2 Ternary Intermetallics (M = U, RE and T = 3d, 4d, 5d Transition Metals)

NARCIS (Netherlands)

Menovsky, A.A.; Moleman, A.C.; Snel, G.E.; Gortenmulder, T.J.; Palstra, T.T.M.

1986-01-01

Bulk single crystals of the ternary intermetallic compounds UT2Si2 (T = Ni, Pd, Pt and Ru), LaT2Si2 (T = Pd and Rh) and LuPd2Si2 have been grown from the melt with a modified “tri-arc” Czochralski method. The as-grown crystals were characterized by X-ray, microprobe and chemical analyses. The

Formation of abrasion-resistant coatings of the AlSiFe{sub x}Mny intermetallic compound type on the AISI 304L alloy

Energy Technology Data Exchange (ETDEWEB)

Martinez-Peralez, L. G.; Flores-Valdes, A.; Salinas-Rodriguez, A.; Ochoa-Palacios, R. M.; Toscano-giles, J. A.; Torres-Torres, J.

2016-05-01

The α-Al{sub 9}FeMnSi and α-Al{sub 9}FeMn{sub 2}Si intermetallics formed by reactive sintering of Al, Si, Mn, Fe, Cr and Ni powders have been used in AISI 304L steels to enhance microhardness. Processing variables of the reactive sintering treatment were temperature (600, 650, 700, 750 and 800 degree centigrade), pressure (5, 10 y 20 MPa) and holding time (3600, 5400 y 7200 seconds). Experimental results show that temperature is the most important variable affecting the substrate/coating formation, while pressure does not appear to have a significant effect. The results show the optimum conditions of the reactive sintering that favor the substrate/coating formation are 800 degree centigrade, 20 MPa and 7200 seconds. Under these conditions, the reaction zone between the substrate and coating is more compacted and well-adhered, with a microhardness of 1300 Vickers. The results of SEM and X-Ray diffraction confirmed the formation of β-Al{sub 9}FeMnSi and β-Al{sub 9}FeMn{sub 2}Si intermetallics in the substrate/coating interface as well as the presence of Cr and Ni, indicating diffusion of these two elements from the substrate to the interface. (Author)

Antibiotic susceptibility profiles for mastitis treatment.

Science.gov (United States)

Hinckley, L S; Benson, R H; Post, J E; DeCloux, J C

1985-10-01

Susceptibility tests were performed on milk samples representing prevalent mastitis infections in certain herds. Susceptibility patterns of the same bacterial species from several mastitis infections in the same herd were consistent. The herd antibiotic susceptibility profiles were used as a basis for selecting antibiotics for treatment of all such mastitis cases in that herd. A high degree of correlation was seen between the susceptibility test results and treatment results. Susceptibility patterns of the same bacterial species from mastitis infections in different herds varied greatly, which indicated that any one antibiotic would not work equally well against the same bacterial infection in every herd. Therefore, treatment should be selected on the basis of susceptibility test results. When both Streptococcus and Staphylococcus mastitis occurred in the same herd, the susceptibility patterns for the 2 bacterial species varied widely. Therefore, for herds that experienced both streptococcal and staphylococcal mastitis, antibiotics to which both bacterial species were susceptible were used for treatment.

Susceptibility to Eating Disorders Among Collegiate Female Student–Athletes

Science.gov (United States)

McLester, Cherilyn N.; Hardin, Robin; Hoppe, Stephanie

2014-01-01

Context: Research has suggested that the prevalence of young women with eating disorders (EDs) is increasing, but determining the exact prevalence of EDs within the female student–athlete (FS-A) population is difficult. Looking at certain traits may help us to identify their level of susceptibility to developing an ED. Objective: To determine the susceptibility of FS-As to EDs in relation to self-concept, including self-esteem and body image. Design: Cross-sectional study. Setting: Athletic training and health centers at National Collegiate Athletic Association Division I, II, and III institutions via e-mail questionnaire correspondence. Patients or Other Participants: A total of 439 FS-As from 17 participating institutions completed the questionnaires. The sample was primarily white (83.1%) and underclass (61.8%). Main Outcome Measure(s): The questionnaire consisted of 4 parts: 3 subscales of the Eating Disorder Inventory-2, the Rosenberg Self-Esteem Scale, the Body Cathexis Scale, and demographic items. Results: A total of 6.8% of FS-As were susceptible to anorexia and 1.8% were susceptible to bulimia. The majority of FS-As (61%) reported normal self-esteem levels, whereas 29.4% had high self-esteem. Overall, 64.5% were satisfied and 23% were very satisfied with their body image. Conclusions: These results are generally positive in that they suggest FS-As have high levels of self-concept and are at low risk to develop EDs. However, these findings do not mean that all concerns should be dismissed. Although more than 90% of the respondents were not susceptible to an ED, there are still FS-As who may be. Athletic departments should evaluate their FS-As' levels of self-concept so that their susceptibility to EDs can be addressed. The emotional aspect of health care should be included in providing holistic care for student–athletes. Athletic trainers often are the primary health care providers for FS-As, so they should be made aware of this concern. PMID:24762233

Manifestation of a neuro-fuzzy model to produce landslide susceptibility map using remote sensing data derived parameters

Science.gov (United States)

Pradhan, Biswajeet; Lee, Saro; Buchroithner, Manfred

Landslides are the most common natural hazards in Malaysia. Preparation of landslide suscep-tibility maps is important for engineering geologists and geomorphologists. However, due to complex nature of landslides, producing a reliable susceptibility map is not easy. In this study, a new attempt is tried to produce landslide susceptibility map of a part of Cameron Valley of Malaysia. This paper develops an adaptive neuro-fuzzy inference system (ANFIS) based on a geographic information system (GIS) environment for landslide susceptibility mapping. To ob-tain the neuro-fuzzy relations for producing the landslide susceptibility map, landslide locations were identified from interpretation of aerial photographs and high resolution satellite images, field surveys and historical inventory reports. Landslide conditioning factors such as slope, plan curvature, distance to drainage lines, soil texture, lithology, and distance to lineament were extracted from topographic, soil, and lineament maps. Landslide susceptible areas were analyzed by the ANFIS model and mapped using the conditioning factors. Furthermore, we applied various membership functions (MFs) and fuzzy relations to produce landslide suscep-tibility maps. The prediction performance of the susceptibility map is checked by considering actual landslides in the study area. Results show that, triangular, trapezoidal, and polynomial MFs were the best individual MFs for modelling landslide susceptibility maps (86

Improving of Corrosion Resistance of Aluminum Alloys by Removing Intermetallic Compound

Energy Technology Data Exchange (ETDEWEB)

Seri, Osami [Muroran it., Hokkaido (Japan)

2008-06-15

It is well known that iron is one of the most common impurity elements sound in aluminum and its alloys. Iron in the aluminum forms an intermetallic compounds such as FeAl{sub 3}. The FeAl{sub 3} particles on the aluminum surface are one of the most detrimental phases to the corrosion process and anodizing procedure for aluminum and its alloys. Trial and error surface treatment will be carried out to find the preferential and effective removal of FeAl{sub 3} particles on the surfaces without dissolution of aluminum matrix around the particles. One of the preferable surface treatments for the aim of getting FeAl{sub 3} free surface was an electrochemical treatment such as cathodic current density of -2 kAm{sup -2} in a 20-30 mass% HNO{sub 3} solution for the period of 300s. The corrosion characteristics of aluminum surface with FeAl{sub 3} free particles are examined in a 0.1 kmol/m{sup 3} NaCl solution. It is found that aluminum with free FeAl{sub 3} particles shows higher corrosion resistance than aluminum with FeAl{sub 3} particles.

Effect on strength of ternary alloying additions in L12 intermetallics

International Nuclear Information System (INIS)

Wu Yuanpang.

1991-01-01

The thermodynamic properties of {111} antiphase boundaries (APBs) as well as the site preference of ternary additions in an A 3 B intermetallic with L1 2 structure are studied, using a thermodynamic model. A survey of the results from a variety of ternary alloying additions to Ni 3 Al has shown that there is a conflict in the actual role which solid solution strengthening plays in the athermal increment of yield strength. For instance, a good quantitative agreement with linear concentration law is observed only in alloys with stoichiometric compositions but not in the general case of non-stoichiometric alloys. In the light of the possibility that micro-segregation could explain the experimental discrepancy, the author extends the binary solid solution strengthening theory to the ternary system in an L1 2 structure for the four real systems of Ni-Al-Si, Ni-Al-Ti, Ni-Al-Hf, and Ni-Al-V. It is found that ternary site preference plays an important role in the ternary solid solution strengthening theory with L1 2 structure. Good quantitative agreement was found between the calculated and experimentally measured strength for both stoichiometric and nonstoichiometric alloys

Intermetallic phases in the iron-rich region of the Zr-Fe phase diagram

International Nuclear Information System (INIS)

Granovsky, M.S.; Arias, D.

1996-01-01

Intermetallic phases in the Fe-rich region of the Zr-Fe system are studied by X-ray diffraction and optical and electron microscopy. The chemical composition of each phase has been quantitatively measured in a electron microprobe. The stable phases found in this region are ZrFe 2 , Zr 6 Fe 23 and (αFe). ZrFe 2 is identified as a cubic Laves type phase (C15) and the ZrFe 2 /ZrFe 2 +Zr 6 Fe 23 boundary composition is 73±1 at.% Fe. Zr 6 Fe 23 is a cubic phase of the Th 6 Mn 23 type and its composition is 80.0±1.5 at.% Fe. The eutectic L↔Zr 6 Fe 23 +τ-Fe transformation temperature and composition are 1325 C and 91±1 at.% Fe, respectively. The solubility of Zr in τ-Fe at 1012 C is 500±50 appm and 1000±100 appm close to the eutectic temperature. (orig.)

Moessbauer Study of the Ball Milling Disordering Process of FeAl Intermetallic Compounds

International Nuclear Information System (INIS)

Oleszak, Dariusz; Bruna, Pere; Crespo, Daniel; Pradell, Trinitat

2005-01-01

Structural changes during ball milling of ordered Fe50Al50 intermetallic compounds were studied. X-Ray diffraction allowed the computation of a Long Range Order parameter (LRO) which dropped to zero after a short milling time. The initial B2 ordered structure gradually transforms into a disordered BCC structure, with a final crystallite size of about 25 nm. Moessbauer spectroscopy was used for obtaining a Chemical Short Range Order parameter (CSRO). Using a semiempirical n-body noncentral potential a model of the partially disordered B2 structure was built allowing computing the distribution of Quadrupole Splitting during the disordering process. Comparison between experimental and simulated Moessbauer spectra shows a maximum of disorder in the system for 5h milling, related to the highest value of the lattice spacing and the broader quadrupole hyperfine distribution. However, after milling for times longer than 5h, there is a change on the behavior of the experimental data that cannot be explained by the simple disordering process

Effect of iodine on the corrosion of Au-Al wire bonds

DEFF Research Database (Denmark)

Verdingovas, Vadimas; Müller, Lutz; Jellesen, Morten Stendahl

2015-01-01

Corrosion study was performed on Au-Al wire bonds, thin layers of sputter deposited Au and Al, and Au-Al intermetallic nuggets. The test environment was iodine-vapour in air (1. mg/L) at 85 °C with varying relative humidity, and 500 mg/L of KI in water. GDOES, XRD, SEM EDS, wire bond shear......, and electrochemical testing were used to characterize the samples. Failures of Au-Al wire bonds were found to be primarily attributed to the corrosion of Al via formation of Al iodides and consequent formation of Al oxides and/or hydroxides. Most susceptible to corrosion are Al metallization and Al rich intermetallic...

First-principles screening of structural properties of intermetallic compounds on martensitic transformation

Science.gov (United States)

Lee, Joohwi; Ikeda, Yuji; Tanaka, Isao

2017-11-01

Martensitic transformation with good structural compatibility between parent and martensitic phases are required for shape memory alloys (SMAs) in terms of functional stability. In this study, first-principles-based materials screening is systematically performed to investigate the intermetallic compounds with the martensitic phases by focusing on energetic and dynamical stabilities as well as structural compatibility with the parent phase. The B2, D03, and L21 crystal structures are considered as the parent phases, and the 2H and 6M structures are considered as the martensitic phases. In total, 3384 binary and 3243 ternary alloys with stoichiometric composition ratios are investigated. It is found that 187 alloys survive after the screening. Some of the surviving alloys are constituted by the chemical elements already widely used in SMAs, but other various metallic elements are also found in the surviving alloys. The energetic stability of the surviving alloys is further analyzed by comparison with the data in Materials Project Database (MPD) to examine the alloys whose martensitic structures may cause further phase separation or transition to the other structures.

Personality traits as potential susceptibility markers : Differential susceptibility to support among parents

NARCIS (Netherlands)

Slagt, M.; Dubas, J.S.; Denissen, J.J.A.; Deković, M.; van Aken, M.A.G.

2015-01-01

In this study, we examined whether parents are differentially susceptible to support from their spouse and adolescent child depending on their personality traits, and whether differences in susceptibility to support among parents, in turn, are linked to the quality of support parents give to their

Ac susceptibility of a Bi-2223/Ag tape in a perpendicular field

International Nuclear Information System (INIS)

Savvides, N.; Mueller, K.-H.

1999-01-01

Full text: We report experimental measurements and theoretical calculations of the real ( X ') and imaginary or loss ( X '') parts of the ac susceptibility as a function of temperature T = 4 - 130 K, frequency ω/2π = 5 Hz - 5 kHz and ac magnetic field amplitude μ 0 H m = 0.02 - 7 mT for of a monofilament silver-sheathed Bi-2223 tape. The susceptibilities consist of a hysteretic component due to ac loss ( Xsc '') in the superconductor core and an eddy current component due to eddy current loss ( Xed '') in the silver sheath. At high temperatures the low frequency limit is used to calculate the hysteretic and eddy current susceptibilities while at low temperatures the susceptibility is found to be due to eddy currents flowing along the edges of the tape. The measured loss at low frequencies (< 50 Hz) and high temperatures is dominated by the hysteresis loss which varies with amplitude but is essentially independent of frequency. At higher frequencies the eddy current loss of the silver sheath becomes dominant and it increases dramatically with frequency at both low and high temperatures

Methodology for calculating the thickness free of sigma phase in duplex stainless steels large section parts during hiperquenching; Metodologia para el calculo de espesores limite libres de fase sigma durante el hipertemple en piezas de aceros duplex de gran seccion

Energy Technology Data Exchange (ETDEWEB)

Jimbert, P.; Guraya, T.; Torregary, A.; Bravo, P.

2013-06-01

To achieve the mechanical properties and corrosion resistance desired by duplex stainless steels used by the petrochemical and nuclear industry, parts are subjected to a hiperquenching heat treatment from about 1050 degree centigrade. This avoids the risk of intermetallic precipitation which drastically reduces the properties of these materials. However with increasing depth to which the deposits are present, the thicknesses for such pipes have been increased, resulting in higher levels of demand on all its manufacturing process, including the heat treatment. To avoid the precipitation of intermetallic phases such as sigma phase it is necessary to know the cooling profile in the center of the work piece and for this purpose to know the value of the Surface Heat Transfer Coefficient (h) is essential. This coefficient changes during the hiperquenching and its value is determined experimentally as it depends on several process parameters. Studies reveal that its value is stabilized within a few seconds. We can then assume that to know the cooling profile in the center of large sections it is only necessary to know the stabilized value of h. However, all the studies found in the literature are referred to diameters smaller than 100 mm. This paper has developed a methodology to predict the precipitation of intermetallic phases in duplex stainless steel parts with large thicknesses in industrial facilities from the calculation of h. This methodology allows us to calculate the cooling profiles without wasting any work piece using one or more sensorized patterns with thermocouples and a subsequent simulation with ANSYS. (Author)

Intermetallic Nickel-Titanium Alloys for Oil-Lubricated Bearing Applications

Science.gov (United States)

DellaCorte, C.; Pepper, S. V.; Noebe, R.; Hull, D. R.; Glennon, G.

2009-01-01

An intermetallic nickel-titanium alloy, NITINOL 60 (60NiTi), containing 60 wt% nickel and 40 wt% titanium, is shown to be a promising candidate material for oil-lubricated rolling and sliding contact applications such as bearings and gears. NiTi alloys are well known and normally exploited for their shape memory behavior. When properly processed, however, NITINOL 60 exhibits excellent dimensional stability and useful structural properties. Processed via high temperature, high-pressure powder metallurgy techniques or other means, NITINOL 60 offers a broad combination of physical properties that make it unique among bearing materials. NITINOL 60 is hard, electrically conductive, highly corrosion resistant, less dense than steel, readily machined prior to final heat treatment, nongalling and nonmagnetic. No other bearing alloy, metallic or ceramic encompasses all of these attributes. Further, NITINOL 60 has shown remarkable tribological performance when compared to other aerospace bearing alloys under oil-lubricated conditions. Spiral orbit tribometer (SOT) tests were conducted in vacuum using NITINOL 60 balls loaded between rotating 440C stainless steel disks, lubricated with synthetic hydrocarbon oil. Under conditions considered representative of precision bearings, the performance (life and friction) equaled or exceeded that observed with silicon nitride or titanium carbide coated 440C bearing balls. Based upon this preliminary data, it appears that NITINOL 60, despite its high titanium content, is a promising candidate alloy for advanced mechanical systems requiring superior and intrinsic corrosion resistance, electrical conductivity and nonmagnetic behavior under lubricated contacting conditions.

Sub-4 nm PtZn Intermetallic Nanoparticles for Enhanced Mass and Specific Activities in Catalytic Electrooxidation Reaction

International Nuclear Information System (INIS)

Qi, Zhiyuan

2017-01-01

Atomically ordered intermetallic nanoparticles (iNPs) have sparked considerable interest in fuel cell applications by virtue of their exceptional electronic and structural properties. However, the synthesis of small iNPs in a controllable manner remains a formidable challenge because of the high temperature generally required in the formation of intermetallic phases. Here in this paper we report a general method for the synthesis of PtZn iNPs (3.2 ± 0.4 nm) on multiwalled carbon nanotubes (MWNT) via a facile and capping agent free strategy using a sacrificial mesoporous silica (mSiO 2 ) shell. The as-prepared PtZn iNPs exhibited ca. 10 times higher mass activity in both acidic and basic solution toward the methanol oxidation reaction (MOR) compared to larger PtZn iNPs synthesized on MWNT without the mSiO 2 shell. Density functional theory (DFT) calculations predict that PtZn systems go through a “non-CO” pathway for MOR because of the stabilization of the OH* intermediate by Zn atoms, while a pure Pt system forms highly stable COH* and CO* intermediates, leading to catalyst deactivation. Experimental studies on the origin of the backward oxidation peak of MOR coincide well with DFT predictions. Moreover, the calculations demonstrate that MOR on smaller PtZn iNPs is energetically more favorable than larger iNPs, due to their high density of corner sites and lower-lying energetic pathway. Therefore, smaller PtZn iNPs not only increase the number but also enhance the activity of the active sites in MOR compared with larger ones. This work opens a new avenue for the synthesis of small iNPs with more undercoordinated and enhanced active sites for fuel cell applications.

Electronic and optical properties of RESn{sub 3} (RE=Pr & Nd) intermetallics: A first principles study

Energy Technology Data Exchange (ETDEWEB)

Pagare, G., E-mail: gita-pagare@yahoo.co.in [Department of Physics, Government M. L. B. Girls P. G. Autonomous College, Bhopal-462002 (India); Abraham, Jisha A. [Department of Physics, Government M. L. B. Girls P. G. Autonomous College, Bhopal-462002 (India); Department of Physics, National Defence Academy, Pune-411023 (India); Sanyal, S. P. [Department of Physics, Barkatullah University, Bhopal-462026 (India)

2015-06-24

A theoretical study of structural, electronic and optical properties of RESn{sub 3} (RE = Pr & Nd) intermetallics have been investigated systematically using first principles density functional theory. The calculations are carried out within the PBE-GGA and LSDA for the exchange correlation potential. The ground state properties such as lattice parameter (a{sub 0}), bulk modulus (B) and its pressure derivative (B′) are calculated and the calculated lattice parameters show well agreement with the experimental results. We first time predict elastic constants for these compounds. From energy dispersion curves, it is found that these compounds are metallic in nature. The linear optical response of these compounds are also studied and the higher value of static dielectric constant shows the possibility to use them as good dielectric materials.

A simple route to Cu{sub x}Sn{sub (100−x)} intermetallic nanoparticle catalyst for ultra-phenol hydroxylation

Energy Technology Data Exchange (ETDEWEB)

Pithakratanayothin, Sakollapath [The Petroleum and Petrochemical College and Center of Excellence on Petrochemical and Materials Technology, Chulalongkorn University, Bangkok 10330 (Thailand); Tongsri, Ruangdaj [Powder Metallurgy Research and Development Unit - PM-RDU, National Metal and Materials Technology Center, Pathum Thani 12120 (Thailand); Chaisuwan, Thanyalak [The Petroleum and Petrochemical College and Center of Excellence on Petrochemical and Materials Technology, Chulalongkorn University, Bangkok 10330 (Thailand); Wongkasemjit, Sujitra, E-mail: dsujitra@chula.ac.th [The Petroleum and Petrochemical College and Center of Excellence on Petrochemical and Materials Technology, Chulalongkorn University, Bangkok 10330 (Thailand)

2016-09-15

A practical methodology and novel, economical materials were proposed to successfully prepare nanoparticle catalysts for phenol hydroxylation. The preparation was carried out via mechanical alloying (MA) of Cu{sub x}Sn{sub (100−x)} powder mixtures (where x = 30, 50, 70, and 100%wt). The mechanical alloyed nanoparticles were characterized using various techniques. X-ray diffraction patterns indicated that η-Cu{sub 6}Sn{sub 5}, ε-Cu{sub 3}Sn, and CuSn phases could be formed in the mechanical alloyed Cu{sub x}Sn{sub (100−x)} materials. Transmission electron micrographs and selected area electron diffraction patterns confirmed the presence of η-Cu{sub 6}Sn{sub 5}, ε-Cu{sub 3}Sn, and CuSn phases. Activity of the catalysts, using the optimal conditions of 70 °C reaction temperature for 1 h, 50 mg of Cu{sub 0.5}Sn{sub 0.5}, and 1:3 phenol:H{sub 2}O{sub 2} ratio, provided more than 98% conversion with 70% catechol (CAT) and 29% hydroquinone (HQ). Experimental results suggested that the presence of the ε-Cu{sub 3}Sn phase gave higher activity while Sn reduced benzoquinone (BQ) to HQ. The catalyst maintained its stability with no structural collapse for more than 24 h. - Highlights: • Cu{sub x}Sn{sub y} intermetallic as a catalyst was successfully synthesized via mechanical alloying. • Cu{sub x}Sn{sub y} intermetallics promoted impressive phenol hydroxylation. • 98% conversion was achieved with high selectivity of catechol.

Molecular dynamics simulations of radiation damage in D019 Ti3Al intermetallic compound

International Nuclear Information System (INIS)

Voskoboinikov, Roman E.

2013-01-01

Molecular dynamics (MD) has been applied to simulate the radiation damage created in displacement cascades in D0 19 Ti 3 Al structural intermetallics. Collision cascades formed by the recoil of either Al or Ti primary knock-on atoms (PKA) with energy E PKA = 5, 10, 15 or 20 keV were considered in Ti 3 Al single crystals at T = 100, 300, 600 and 900 K. At least 24 different cascades for each (E PKA , T, PKA type) set were simulated. A comprehensive treatment of the modelling results has been carried out. We have evaluated the number of Frenkel pairs, fraction of Al and Ti vacancies, self-interstitial atoms and anti-sites as a function of (E PKA ,T, PKA type). Preferred formation of both Al vacancies and self-interstitial atoms in D0 19 Ti 3 Al exposed to irradiation has been detected

Electronic structure, elasticity, bonding features and mechanical behaviour of zinc intermetallics: A DFT study

Energy Technology Data Exchange (ETDEWEB)

Fatima, Bushra, E-mail: bushrafatima25@gmail.com; Acharya, Nikita; Sanyal, Sankar P. [Department of Physics, Barkatullah University, Bhopal, 462026 (India)

2016-05-06

The structural stability, electronic structure, elastic and mechanical properties of TiZn and ZrZn intermetallics have been studied using ab-initio full potential linearized augmented plane wave (FP-LAPW) method within generalized gradient approximation for exchange and correlation potentials. The various structural parameters, such as lattice constant (a{sub 0}), bulk modulus (B), and its pressure derivative (B’) are analysed and compared. The investigation of elastic constants affirm that both TiZn and ZrZn are elastically stable in CsCl (B{sub 2} phase) structure. The electronic structures have been analysed quantitatively from the band structure which reveals the metallic nature of these compounds. To better illustrate the nature of bonding and charge transfer, we have also studied the Fermi surfaces. The three well known criterion of ductility namely Pugh’s rule, Cauchy’s pressure and Frantsevich rule elucidate the ductile nature of these compounds.

Structural, electronic and elastic properties of RERu{sub 2} (RE=Pr and Nd) Laves phase intermetallic compounds

Energy Technology Data Exchange (ETDEWEB)

Shrivastava, Deepika, E-mail: deepika89shrivastava@gmail.com; Sanyal, Sankar P. [Department of Physics, Barkatullah university, Bhopal, 462026 (India)

2016-05-06

We have performed the first-principles calculations to study the structural, electronic and elastic properties of RERu{sub 2} (RE = Pr and Nd) Laves phase intermetallic compounds using full-potential linearized augmented plane wave (FP-LAPW) method based on density functional theory (DFT) within the generalized gradient approximation (GGA) for exchange and correlation potential. The optimized lattices constant are in reasonable agreement with available experimental data. The electronic properties are analyzed in terms of band structures, total and partial density of states, which confirm their metallic character. The calculated elastic constants infer that these compounds are mechanically stable in C15 (MgCu{sub 2} type) structure and found to be ductile in nature.

Susceptibility Tensor Imaging (STI) of the Brain

Science.gov (United States)

Li, Wei; Liu, Chunlei; Duong, Timothy Q.; van Zijl, Peter C.M.; Li, Xu

2016-01-01

Susceptibility tensor imaging (STI) is a recently developed MRI technique that allows quantitative determination of orientation-independent magnetic susceptibility parameters from the dependence of gradient echo signal phase on the orientation of biological tissues with respect to the main magnetic field. By modeling the magnetic susceptibility of each voxel as a symmetric rank-2 tensor, individual magnetic susceptibility tensor elements as well as the mean magnetic susceptibility (MMS) and magnetic susceptibility anisotropy (MSA) can be determined for brain tissues that would still show orientation dependence after conventional scalar-based quantitative susceptibility mapping (QSM) to remove such dependence. Similar to diffusion tensor imaging (DTI), STI allows mapping of brain white matter fiber orientations and reconstruction of 3D white matter pathways using the principal eigenvectors of the susceptibility tensor. In contrast to diffusion anisotropy, the main determinant factor of susceptibility anisotropy in brain white matter is myelin. Another unique feature of susceptibility anisotropy of white matter is its sensitivity to gadolinium-based contrast agents. Mechanistically, MRI-observed susceptibility anisotropy is mainly attributed to the highly ordered lipid molecules in myelin sheath. STI provides a consistent interpretation of the dependence of phase and susceptibility on orientation at multiple scales. This article reviews the key experimental findings and physical theories that led to the development of STI, its practical implementations, and its applications for brain research. PMID:27120169

Personality Traits and Susceptibility to Behavioral Biases among a Sample of Polish Stock Market Investors

Directory of Open Access Journals (Sweden)

Rzeszutek Marcin

2015-09-01

Full Text Available The aim of this paper is to investigate whether susceptibility to selected behavioral biases (overconfidence, mental accounting and sunk-cost fallacy is correlated with the Eysenck’s [1978] personality traits (impulsivity, venturesomeness, and empathy. This study was conducted on a sample of 90 retail investors frequently investing on the Warsaw Stock Exchange. Participants filled out a survey made up of two parts: 1 three situational exercises, which assessed susceptibility to behavioral biases and 2 an Impulsiveness Questionnaire, which measures impulsivity, venturesomeness, and empathy. The results demonstrated the relationship between venturesomeness and susceptibility to all behavioral biases explored in this study. We find that higher level of venturesomeness was linked with a lower probability of all behavioral biases included in this study.

Landslide susceptibility mapping using a neuro-fuzzy

Science.gov (United States)

Lee, S.; Choi, J.; Oh, H.

2009-12-01

This paper develops and applied an adaptive neuro-fuzzy inference system (ANFIS) based on a geographic information system (GIS) environment using landslide-related factors and location for landslide susceptibility mapping. A neuro-fuzzy system is based on a fuzzy system that is trained by a learning algorithm derived from the neural network theory. The learning procedure operates on local information, and causes only local modifications in the underlying fuzzy system. The study area, Boun, suffered much damage following heavy rain in 1998 and was selected as a suitable site for the evaluation of the frequency and distribution of landslides. Boun is located in the central part of Korea. Landslide-related factors such as slope, soil texture, wood type, lithology, and density of lineament were extracted from topographic, soil, forest, and lineament maps. Landslide locations were identified from interpretation of aerial photographs and field surveys. Landslide-susceptible areas were analyzed by the ANFIS method and mapped using occurrence factors. In particular, we applied various membership functions (MFs) and analysis results were verified using the landslide location data. The predictive maps using triangular, trapezoidal, and polynomial MFs were the best individual MFs for modeling landslide susceptibility maps (84.96% accuracy), proving that ANFIS could be very effective in modeling landslide susceptibility mapping. Various MFs were used in this study, and after verification, the difference in accuracy according to the MFs was small, between 84.81% and 84.96%. The difference was just 0.15% and therefore the choice of MFs was not important in the study. Also, compared with the likelihood ratio model, which showed 84.94%, the accuracy was similar. Thus, the ANFIS could be applied to other study areas with different data and other study methods such as cross-validation. The developed ANFIS learns the if-then rules between landslide-related factors and landslide

Phase equilibria of Al3(Ti,V,Zr) intermetallic system

International Nuclear Information System (INIS)

Park, S.I.; Han, S.Z.; Choi, S.K.; Lee, H.M.

1996-01-01

Trialuminides such as DO 22 -structured Al 3 Ti are promising candidates as potential materials for elevated temperature applications because of their attractive high temperature strength and excellent oxidation resistance along with their low density. However, in the tetragonal structure, slip systems are restricted due to low symmetry and the primary deformation mode is twinning. And, therefore, monolithic trialuminide compounds have been very impractical to be used as structural materials. When transition elements such as Ti, V and Zr which constitute trialuminides are alloyed in aluminum, they have low solubilities and low diffusion coefficients in the Al matrix. If precipitated as trialuminide intermetallics, they maintain a small lattice mismatch with the Al matrix, which reduces the interfacial energy between matrix and precipitates. As a result, these precipitates would have a large coarsening resistance in the matrix. As most of the previous works have been concentrated on the microstructural stability and mechanical properties, thermochemical properties will be treated in this work. In this study, phase equilibria and diagrams of Al 3 (Ti,V,Zr) systems will be experimentally determined and then thermodynamically analyzed with a hope to extend to the Al-Al 3 (Ti,V,Zr) composite system. This approach will then be used as a guide for alloy design of Al-Al 3 (Ti,V,Zr) composite system

Susceptibility tensor imaging (STI) of the brain.

Science.gov (United States)

Li, Wei; Liu, Chunlei; Duong, Timothy Q; van Zijl, Peter C M; Li, Xu

2017-04-01

Susceptibility tensor imaging (STI) is a recently developed MRI technique that allows quantitative determination of orientation-independent magnetic susceptibility parameters from the dependence of gradient echo signal phase on the orientation of biological tissues with respect to the main magnetic field. By modeling the magnetic susceptibility of each voxel as a symmetric rank-2 tensor, individual magnetic susceptibility tensor elements as well as the mean magnetic susceptibility and magnetic susceptibility anisotropy can be determined for brain tissues that would still show orientation dependence after conventional scalar-based quantitative susceptibility mapping to remove such dependence. Similar to diffusion tensor imaging, STI allows mapping of brain white matter fiber orientations and reconstruction of 3D white matter pathways using the principal eigenvectors of the susceptibility tensor. In contrast to diffusion anisotropy, the main determinant factor of the susceptibility anisotropy in brain white matter is myelin. Another unique feature of the susceptibility anisotropy of white matter is its sensitivity to gadolinium-based contrast agents. Mechanistically, MRI-observed susceptibility anisotropy is mainly attributed to the highly ordered lipid molecules in the myelin sheath. STI provides a consistent interpretation of the dependence of phase and susceptibility on orientation at multiple scales. This article reviews the key experimental findings and physical theories that led to the development of STI, its practical implementations, and its applications for brain research. Copyright © 2016 John Wiley & Sons, Ltd. Copyright © 2016 John Wiley & Sons, Ltd.

Advances in processing of NiAl intermetallic alloys and composites for high temperature aerospace applications

Science.gov (United States)

Bochenek, Kamil; Basista, Michal

2015-11-01

Over the last few decades intermetallic compounds such as NiAl have been considered as potential high temperature structural materials for aerospace industry. A large number of investigations have been reported describing complex fabrication routes, introducing various reinforcing/alloying elements along with theoretical analyses. These research works were mainly focused on the overcoming of main disadvantage of nickel aluminides that still restricts their application range, i.e. brittleness at room temperature. In this paper we present an overview of research on NiAl processing and indicate methods that are promising in solving the low fracture toughness issue at room temperature. Other material properties relevant for high temperature applications are also addressed. The analysis is primarily done from the perspective of NiAl application in aero engines in temperature regimes from room up to the operating temperature (over 1150 °C) of turbine blades.

FP-LAPW study of structural, electronic, elastic, mechanical and thermal properties of AlFe intermetallic

Energy Technology Data Exchange (ETDEWEB)

Jain, Ekta, E-mail: jainekta05@gmail.com [Department of Physics, Government M. L. B. Girls P. G. Autonomous College, Bhopal-462002 (India); Pagare, Gitanjali, E-mail: gita-pagare@yahoo.co.in [Department of Physics, Sarojini Naidu Government Girls P. G. Autonomous College, Bhopal-462016 (India); Sanyal, S. P., E-mail: sps.physicsbu@gmail.com [Department of Physics, Barkatullah University, Bhopal-462026 (India)

2016-05-06

The structural, electronic, elastic, mechanical and thermal properties of AlFe intermetallic compound in B{sub 2}-type (CsCl) structure have been investigated using first-principles calculations. The exchange-correlation term was treated within generalized gradient approximation. Ground state properties i.e. lattice constants (a{sub 0}), bulk modulus (B) and first-order pressure derivative of bulk modulus (B’) are presented. The density of states are derived which show the metallic character of present compound. Our results for C{sub 11}, C{sub 12} and C{sub 44} agree well with previous theoretical data. Using Pugh’s criteria (B/G{sub H} < 1.75), brittle character of AlFe is satisfied. In addition shear modulus (G{sub H}), Young’s modulus (E), sound wave velocities and Debye temperature (θ{sub D}) have also been estimated.

Solid-state transformation of Fe-rich intermetallic phases in Al–5.0Cu–0.6Mn squeeze cast alloy with variable Fe contents during solution heat treatment

Energy Technology Data Exchange (ETDEWEB)

Lin, Bo [School of Mechanical and Automotive Engineering, South China University of Technology, Guangzhou 510640 (China); School of Mechanical Engineering, Gui Zhou University, Guiyang 550000 (China); Zhang, Weiwen, E-mail: mewzhang@scut.edu.cn [School of Mechanical and Automotive Engineering, South China University of Technology, Guangzhou 510640 (China); Zhao, Yuliang; Li, Yuanyuan [School of Mechanical and Automotive Engineering, South China University of Technology, Guangzhou 510640 (China)

2015-06-15

The Al–5.0 wt.% Cu–0.6 wt.% Mn alloys with a variable Fe content were prepared by squeeze casting. Optical microscopy (OM), Deep etching technique, scanning electron microscopy(SEM), X-ray diffraction (XRD) and transmission electron microscopy (TEM) were used to examine the solid-state transformation of Fe-rich intermetallics during the solution heat treatment. The results showed that the Chinese script-like α-Fe, Al{sub 6}(FeMn) and needle-like Al{sub 3}(FeMn) phases transform to a new Cu-rich β-Fe (Al{sub 7}Cu{sub 2}(FeMn)) phase during solution heat treatment. The possible reaction and overall transformation kinetics of the solid-state phase transformation for the Fe-rich intermetallics were investigated. - Graphical abstract: Display Omitted - Highlights: • The α-Fe, Al{sub 6}(FeMn) and Al{sub 3}(FeMn) phases change to the β-Fe phases. • Possible reactions of Fe phases during solution heat treatment are discussed. • The overall fractional transformation rate follows an Avrami curve.

Inhibition of the formation of intermetallic compounds in aluminum-steel welded joints by friction stir welding

Directory of Open Access Journals (Sweden)

Torres López, Edwar A.

2015-12-01

Full Text Available Formation of deleterious phases during welding of aluminum and steel is a challenge of the welding processes, for decades. Friction Stir Welding (FSW has been used in an attempt to reduce formation of intermetallic compounds trough reducing the heat input. In this research, dissimilar joint of 6063-T5 aluminum alloy and AISI-SAE 1020 steel were welded using this technique. The temperature of welded joints was measured during the process. The interface of the welded joints was characterized using optical microscopy, scanning and transmission electron microscopy. Additionally, composition measurements were carried out by X-EDS and DRX. The experimental results revealed that the maximum temperature on the joint studied is less than 360 °C. The microstructural characterization in the aluminum-steel interface showed the absence of intermetallic compounds, which is a condition attributed to the use of welding with low thermal input parameters.La unión de juntas aluminio-acero, sin la formación de fases deletéreas del tipo FexAly, ha sido, por décadas, un desafío para los procesos de soldadura. La soldadura por fricción-agitación ha sido empleada para intentar reducir el aporte térmico y evitar la formación de compuestos intermetálicos. Usando esta técnica fueron soldadas juntas disimilares de aluminio 6063-T5 y acero AISI-SAE 1020. La soldadura fue acompañada de medidas de temperatura durante su ejecución. La interfase de las juntas soldadas fue caracterizada utilizando microscopía óptica, electrónica de barrido y electrónica de transmisión. Adicionalmente fueron realizadas medidas puntuales X-EDS y DRX. Los resultados experimentales revelan que la temperatura máxima en la junta es inferior a 360 °C. La caracterización microestructural en la interfase aluminio-acero demostró la ausencia de compuestos intermetálicos, condición atribuida al uso de parámetros de soldadura con bajo aporte térmico.

A landslide susceptibility map of Africa

Science.gov (United States)

Broeckx, Jente; Vanmaercke, Matthias; Duchateau, Rica; Poesen, Jean

2017-04-01

Studies on landslide risks and fatalities indicate that landslides are a global threat to humans, infrastructure and the environment, certainly in Africa. Nonetheless our understanding of the spatial patterns of landslides and rockfalls on this continent is very limited. Also in global landslide susceptibility maps, Africa is mostly underrepresented in the inventories used to construct these maps. As a result, predicted landslide susceptibilities remain subject to very large uncertainties. This research aims to produce a first continent-wide landslide susceptibility map for Africa, calibrated with a well-distributed landslide dataset. As a first step, we compiled all available landslide inventories for Africa. This data was supplemented by additional landslide mapping with Google Earth in underrepresented regions. This way, we compiled 60 landslide inventories from the literature (ca. 11000 landslides) and an additional 6500 landslides through mapping in Google Earth (including 1500 rockfalls). Various environmental variables such as slope, lithology, soil characteristics, land use, precipitation and seismic activity, were investigated for their significance in explaining the observed spatial patterns of landslides. To account for potential mapping biases in our dataset, we used Monte Carlo simulations that selected different subsets of mapped landslides, tested the significance of the considered environmental variables and evaluated the performance of the fitted multiple logistic regression model against another subset of mapped landslides. Based on these analyses, we constructed two landslide susceptibility maps for Africa: one for all landslide types and one excluding rockfalls. In both maps, topography, lithology and seismic activity were the most significant variables. The latter factor may be surprising, given the overall limited degree of seismicity in Africa. However, its significance indicates that frequent seismic events may serve as in important

The effect of high-temperature treatment on the formation of nanoscale intermetallic compounds of transition metals in Al-Cu-Mn-Zr alloy

Science.gov (United States)

Monastyrska, Tetiana O.; Berezina, Alla L.; Labur, Tetiana M.; Molebny, Oleh A.; Kotko, Andrii V.

2018-02-01

The precipitation of intermetallic compounds of transition metals during aging of the Al-5.8%Cu-0.3%Mn-0.1%Zr alloy has been studied using DSC, resistometry, X-ray and transmission electron microscopy. In these age hardenable alloys, the nanoscale metastable Θ″ and Θ' phases of the Al2Cu compound are the main strengthening phases, which are formed at low temperature aging of T stresses, etc.) on the aging with the precipitation of strengthening phases has been investigated.

Bipolar disorder: idioms of susceptibility and disease and the role of 'genes' in illness explanations.

Science.gov (United States)

Baart, Ingrid; Widdershoven, Guy

2013-11-01

This qualitative study explores (1) how members of the Dutch Association for People with Bipolar Disorder explain the affliction of bipolar disorder; (2) the relationship between genetic, environmental and personal factors in these explanations and (3) the relationship between illness explanations, self-management and identity. A total of 40 participants took part in seven different focus group discussions. The results demonstrate that there are two different explanatory idioms, each one centred around an opposing concept, that is, susceptibility and disease. Individuals who construct explanations around the concept of 'disease' attach more importance to 'genes and chemicals' than to environmental components in the onset of the disorder, whereas individuals adhering to the central concept of 'susceptibility' tend to do this much less. Compared with individuals using the 'susceptibility' idiom, those who use a 'disease' idiom tend to observe fewer possibilities for self-management and are less inclined to construct normalcy through a quest for personal growth. Stories of suffering seem more integral to the 'disease' idiom than to the 'susceptibility' idiom. The 'disease' idiom seems less integrated in a contemporary surveillance psychiatric discourse than the 'susceptibility' idiom; however, both vocabularies can offer normative constraints.

Electride and superconductivity behaviors in Mn5Si3-type intermetallics

Science.gov (United States)

Zhang, Yaoqing; Wang, Bosen; Xiao, Zewen; Lu, Yangfan; Kamiya, Toshio; Uwatoko, Yoshiya; Kageyama, Hiroshi; Hosono, Hideo

2017-08-01

Electrides are unique in the sense that they contain localized anionic electrons in the interstitial regions. Yet they exist with a diversity of chemical compositions, especially under extreme conditions, implying generalized underlying principles for their existence. What is rarely observed is the combination of electride state and superconductivity within the same material, but such behavior would open up a new category of superconductors. Here, we report a hexagonal Nb5Ir3 phase of Mn5Si3-type structure that falls into this category and extends the electride concept into intermetallics. The confined electrons in the one-dimensional cavities are reflected by the characteristic channel bands in the electronic structure. Filling these free spaces with foreign oxygen atoms serves to engineer the band topology and increase the superconducting transition temperature to 10.5 K in Nb5Ir3O. Specific heat analysis indicates the appearance of low-lying phonons and two-gap s-wave superconductivity. Strong electron-phonon coupling is revealed to be the pairing glue with an anomalously large ratio between the superconducting gap Δ0 and Tc, 2Δ0/kBTc = 6.12. The general rule governing the formation of electrides concerns the structural stability against the cation filling/extraction in the channel site.

Intermetallic Compound Growth and Stress Development in Al-Cu Diffusion Couple

Science.gov (United States)

Mishler, M.; Ouvarov-Bancalero, V.; Chae, Seung H.; Nguyen, Luu; Kim, Choong-Un

2018-01-01

This paper reports experimental observations evidencing that the intermetallic compound phase interfaced with Cu in the Al-Cu diffusion couple is most likely α2-Cu3Al phase, not γ-Cu9Al4 phase as previously assumed, and that its growth to a critical thickness may result in interface failure by stress-driven fracture. These conclusions are made based on an interdiffusion study of a diffusion couple made of a thick Cu plate coated with ˜ 2- μm-thick Al thin film. The interface microstructure and lattice parameter were characterized using scanning electron microscopy and x-ray diffraction analysis. Specimens aged at temperature between 623 K (350°C) and 723 K (450°C) for various hours produced consistent results supporting the main conclusions. It is found that disordered α2-Cu3Al phase grows in a similar manner to solid-state epitaxy, probably owing to its structural similarity to the Cu lattice. The increase in the interface strain that accompanies the α2-Cu3Al phase growth ultimately leads to interface fracture proceeding from crack initiation and growth along the interface. This mechanism provides the most consistent explanation for interface failures observed in other studies.

Physical properties of the GaPd2 intermetallic catalyst in bulk and nanoparticle morphology

DEFF Research Database (Denmark)

Wencka, M.; Schwerin, J.; Klanjšek, M.

2015-01-01

Intermetallic compound GaPd2 is a highly selective catalyst material for the semi-hydrogenation of acetylene. We have determined anisotropic electronic, thermal and magnetic properties of a GaPd2 monocrystal along three orthogonal orthorhombic directions of the structure. By using 69Ga and 71Ga NMR...... properties of the GaPd2 phase on going from the bulk material to the nanoparticles morphology, we have synthesized GaPd2/SiO2 supported nanoparticles and determined their electronic DOS at εF from the 71Ga NMR spin-lattice relaxation rate. The electronic DOS of the GaPd2 was also studied theoretically from...... spectroscopy, we have determined the electric-field-gradient tensor at the Ga site in the unit cell and the Knight shift, which yields the electronic density of states (DOS) at the Fermi energy εF. The DOS at εF was determined independently also from the specific heat. To see the change of electronic...

Highly stable carbon coated Mg2Si intermetallic nanoparticles for lithium-ion battery anode

Science.gov (United States)

Tamirat, Andebet Gedamu; Hou, Mengyan; Liu, Yao; Bin, Duan; Sun, Yunhe; Fan, Long; Wang, Yonggang; Xia, Yongyao

2018-04-01

Silicon is an ideal candidate anode material for Li-ion batteries (LIBs). However, it suffers from rapid capacity fading due to large volume expansion upon lithium insertion. Herein, we design and fabricate highly stable carbon coated porous Mg2Si intermetallic anode material using facile mechano-thermal technique followed by carbon coating using thermal vapour deposition (TVD), toluene as carbon source. The electrode exhibits an excellent first reversible capacity of 726 mAh g-1 at a rate of 100 mA g-1. More importantly, the electrode demonstrates high rate capability (380 mAh g-1 at high rate of 2 A g-1) as well as high cycle stability, with capacity retentions of 65% over 500 cycles. These improvements are attributable to both Mg supporting medium and the uniform carbon coating, which can effectively increase the conductivity and electronic contact of the active material and protects large volume alterations during the electrochemical cycling process.

Anisotropic magnetic properties of Dy{sub 6}Cr{sub 4}Al{sub 43} single crystal

Energy Technology Data Exchange (ETDEWEB)

Maurya, Arvind, E-mail: arvindmaurya@tifr.res.in; Thamizhavel, A., E-mail: arvindmaurya@tifr.res.in; Dhar, S. K., E-mail: arvindmaurya@tifr.res.in [Department of Condensed Matter Physics and Material Science, Tata Institute of Fundamental Research, Mumbai-400005 (India)

2014-04-24

We have studied the anisotropic magnetic behavior of the rare earth intermetallic compound Dy{sub 6}Cr{sub 4}Al{sub 43}. This compound crystallizes in the hexagonal symmetry and orders ferromagnetically at 8.3 K as confirmed by the magnetic susceptibility and heat capacity measurements. A significant anisotropy in the magnetization is observed between the c axis and the ab-plane. The easy axis liesin theab-plane at low temperatures; however it orients itselfalong the c-axis above 170 K as inferred from the susceptibility data.

An investigation of the fatigue and fracture behavior of a Nb-12Al-44Ti-1.5Mo intermetallic alloy

International Nuclear Information System (INIS)

Soboyejo, W.O.; Dipasquale, J.; Ye, F.; Mercer, C.

1999-01-01

This article presents the results of a study of the fatigue and fracture behavior of a damage-tolerant Nb-12Al-44Ti-1.5Mo alloy. This partially ordered B2 + orthorhombic intermetallic alloy is shown to have attractive combinations of room-temperature ductility (11 to 14 pct), fracture toughness (60 to 92 MPa√m), and comparable fatigue crack growth resistance to IN718, Ti-6Al-4V, and pure Nb at room temperature. The studies show that tensile deformation in the Nb-12Al-44Ti-1.5Mo alloy involves localized plastic deformation (microplasticity via slip-band formation) which initiates at stress levels that are significantly below the uniaxial yield stress (∼9.6 pct of the 0.2 pct offset yield strength (YS)). The onset of bulk yielding is shown to correspond to the spread of microplasticity completely across the gage sections of the tensile specimen. Fatigue crack initiation is also postulated to occur by the accumulation of microplasticity (coarsening of slip bands). Subsequent fatigue crack growth then occurs by the unzipping of cracks along slip bands that form ahead of the dominant crack tip. The proposed mechanism of fatigue crack growth is analogous to the unzipping crack growth mechanism that was suggested originally by Neumann for crack growth in single-crystal copper. Slower near-threshold fatigue crack growth rates at 750 C are attributed to the shielding effects of oxide-induced crack closure. The fatigue and fracture behavior are also compared to those of pure Nb and emerging high-temperature niobium-based intermetallics