  1. Comparative study in the induced corrosion by sulfate reducing microorganisms, in a stainless steel 304L sensitized and a carbon steel API X65; Estudio comparativo de la corrosion inducida por microorganismos sulfatorreductores, en un acero inoxidable 304L sensibilizado y un acero al carbono API X65

    Energy Technology Data Exchange (ETDEWEB)

    Diaz S, A.; Gonzalez F, E.; Arganis J, C.; Luna C, P.; Carapia M, L. [ININ, Carretera Mexico-Toluca Km. 36.5, 52045 Estado de Mexico (Mexico)]. e-mail: ads@nuclear.inin.mx

    2004-07-01

    In spite of the operational experience related with the presence of the phenomenon of microbiological corrosion (MIC) in industrial components, it was not but until the decade of the 80 s when the nuclear industry recognized its influence in some systems of Nuclear Generating Power plants. At the moment, diverse studies that have tried to explain the generation mechanism of this phenomenon exist; however, they are even important queries that to solve, especially those related with the particularities of the affected metallic substrates. Presently work, the electrochemical behavior of samples of stainless steel AISI 304L sensitized is evaluated and the carbon steel APIX65, before the action of sulfate reducing microorganisms low the same experimental conditions; found that for the APIX65 the presence of this type of bacteria promoted the formation of a stable biofilm that allowed the maintenance of the microorganisms that damaged the material in isolated places where stings were generated; while in the AISI 304L, it was not detected damage associated to the inoculated media. The techniques of Resistance to the Polarization and Tafel Extrapolation, allowed the calculation of the speed of uniform corrosion, parameter that doesn't seem to be influenced by the presence of the microorganisms; while that noise electrochemical it distinguished in real time, the effect of the sulfate reducing in the steel APIX65. (Author)

  2. Propagation of crevices in stainless steel AISI304L in conditions of hydrogen chemistry (HWC); Propagacion de grietas en acero inoxidable AISI304L en condiciones de quimica de hidrogeno (HWC)

    Energy Technology Data Exchange (ETDEWEB)

    Diaz S, A.; Fuentes C, P.; Merino C, F. [ININ, 52750 Ocoyoacac, Estado de Mexico (Mexico); Castano M, V. [IFA-UNAM, Juriquilla, Queretaro (Mexico)]. e-mail: ads@nuclear.inin.mx

    2006-07-01

    Crevice growth velocities in samples of AISI 304L stainless steel thermally welded and sensitized were obtained by the Rising displacement method or of growing displacement. It was used a recirculation circuit in where the operation conditions of a BWR type reactor were simulated (temperature of 288 C and a pressure of 8 MPa) with the chemistry modified by the addition of hydrogen with and without the addition of impurities of a powerful oxidizer like the Cu{sup ++} ion. CT pre cracked specimens were used and each rehearsal stayed to one constant displacement velocity of 1 x 10{sup -9} m/s (3.6 {mu}m/hr), making a continuous pursuit of the advance of the crack by the electric potential drop technique. To the end of the rehearsal it was carried out the fractographic analysis of the propagation surfaces. The values of the growth velocities obtained by this methodology went similar to the opposing ones under normal conditions of operation; while the fractographic analysis show the cracks propagation in trans and intergranular ways, evidencing the complexity of the regulator mechanisms of the one IGSCC even under controlled ambient conditions or with mitigation methodologies like the alternative hydrogen chemistry. (Author)

  3. Characterization of welding of AISI 304l stainless steel similar to the core encircling of a BWR reactor; Caracterizacion de soldaduras de acero inoxidable AISI 304L similares a las de la envolvente del nucleo de un reactor BWR

    Energy Technology Data Exchange (ETDEWEB)

    Gachuz M, M.E.; Palacios P, F.; Robles P, E.F. [ININ, 52045 Ocoyoacac, Estado de Mexico (Mexico)

    2003-07-01

    Plates of austenitic stainless steel AISI 304l of 0.0381 m thickness were welded by means of the SMAW process according to that recommended in the Section 9 of the ASME Code, so that it was reproduced the welding process used to assemble the encircling of the core of a BWR/5 reactor similar to that of the Laguna Verde Nucleo electric plant, there being generated the necessary documentation for the qualification of the one welding procedure and of the welder. They were characterized so much the one base metal, as the welding cord by means of metallographic techniques, scanning electron microscopy, X-ray diffraction, mechanical essays and fracture mechanics. From the obtained results it highlights the presence of an area affected by the heat of up to 1.5 mm of wide and a value of fracture tenacity (J{sub IC}) to ambient temperature for the base metal of 528 KJ/m{sup 2}, which is diminished by the presence of the welding and by the increment in the temperature of the one essay. Also it was carried out an fractographic analysis of the fracture zone generated by the tenacity essays, what evidence a ductile fracture. The experimental values of resistance and tenacity are important for the study of the structural integrity of the encircling one of the core. (Author)

  4. Crack propagation in stainless steel AISI 304L in Hydrogen Chemistry conditions (HWC); Propagacion de Grietas en Acero Inoxidable AISI 304L en Condiciones de Quimica de Hidrogeno (HWC)

    Energy Technology Data Exchange (ETDEWEB)

    Diaz S, A.; Fuentes C, P.; Merino C, F. [ININ, Carretera Mexico -Toluca s/n, La Marquesa, Ocoyoacac, Mexico (Mexico); Castano M, V. [Instituto de Fisica Aplicada, UNAM, Km 15.5 Carretera Queretaro-San Luis Potosi, Juriquilla, Queretaro (Mexico)]. e-mail: ads@nuclear.inin.mx

    2006-07-01

    Velocities of crack growth in samples type CT pre cracking of stainless steel AISI 304l solder and sensitized thermally its were obtained by the Rising Displacement method or of growing displacement. It was used a recirculation circuit that simulates the operation conditions of a BWR type reactor (temperature of 280 C and a pressure of 8 MPa) with the chemistry modified by the addition of hydrogen with and without the addition of impurities of a powerful oxidizer like the Cu{sup +} ion. In each essay stayed a displacement velocity was constant of 1x10{sup -9} m/s, making a continuous pursuit of the advance of the crack by the electric potential drop technique. Contrary to the idea of mitigation of the crack propagation velocity by effect of the addition of the hydrogen in the system, the values of the growth velocities obtained by this methodology went similar to the opposing ones under normal operation conditions. To the finish of the rehearsal one carries out the fractographic analysis of the propagation surfaces, which showed cracks growth in trans and intergranular way, evidencing the complexity of the regulator mechanisms of the IGSCC like in mitigation conditions as the alternative Hydrogen Chemistry. (Author)

  5. Microestrutura de uma Solda Dissimilar entre o Aço Inoxidável Ferrítico AISI 410S e o Aço Inoxidável Austenítico AISI 304L Soldado pelo Processo FSW

    Directory of Open Access Journals (Sweden)

    Tathiane Caminha Andrade

    2015-12-01

    Full Text Available Resumo O presente trabalho visa investigar a microestrutura formada na soldagem dissimilar entre chapas de aços inoxidáveis ferríticos AISI 410S e aços inoxidáveis austeníticos AISI 304L pelo processo friction stir welding. A soldagem foi realizada com o ajuste dos seguintes parâmetros: rotação 450 rpm; velocidade de soldagem de 1,0 mm/s; e força axial 40 kN. O aço AISI 410S foi posicionado no lado de avanço enquanto que o aço AISI 304L foi posicionado no lado de retrocesso. A análise consistiu de preparação metalográfica e caracterização microestrutural por microscopia ótica e microscopia eletrônica de varredura. Para o aço AISI 410S foi observada a formação de martensita associada com ferrita na zona de mistura (ZM, zona termomecanicamente afetada (ZTMA e na zona afetada pelo calor (ZAC. As características do processo de soldagem FSW resultaram num refino de grão para o aço inoxidável ferrítico, posicionado no lado de avanço, tanto na ZM quanto nas ZTMA e ZAC. O mesmo comportamento não foi observado para o lado austenítico.

  6. Zirconium oxide deposits (ZrO{sub 2}) and titanium oxide (TiO{sub 2}) on 304l stainless steel; Depositos de oxido de circonio (ZrO{sub 2}) y oxido de titanio (TiO{sub 2}) sobre acero inoxidable 304L

    Energy Technology Data Exchange (ETDEWEB)

    Davila N, M. L.

    2015-07-01

    This research project aims to carry out the surface and electrochemical characterization to obtain the optimum conditions of the hydrothermal deposits of zirconium oxide ZrO{sub 2} (baddeleyite) and titanium oxide TiO{sub 2} (anatase and rutile phases) on 304l stainless steel, simulating an inhibiting protective layer. 304l steel specimens were cut, pre-oxidized in water at a temperature of 288 degrees Celsius and 8 MPa, similar to those of a typical BWR conditions. From the titanium oxide anatase crystalline phase, the rutile phase was obtained by a heat treatment at 1000 degrees Celsius. The Sigma-Aldrich pre-oxidized powders and steel 304l were characterized using techniques of X-ray diffraction, scanning electron microscopy, X-ray dispersive energy, chemical mapping and Raman spectrometry. The pre-oxidized steel has two oxide layers, an inner layer with nano metric crystals and another outer of larger crystals to 1μm, with the formation of hematite and magnetite, this predominating. The surface that contacted the sample holder has larger crystals. Hydrothermal deposits were carry out from suspensions of 10, 100 and 1000 ppm, of the crystal phases of anatase, rutile and baddeleyite, on the pre-oxidized steel at a temperature of 150 degrees Celsius for 2 and 7 days, samples were analyzed by X-ray diffraction, scanning electron microscopy, X-ray dispersive energy, Raman spectrometry and Tafel polarization. The suspension to 1000 ppm for 7 days coated surface most; the baddeleyite deposit is noticed more homogeneous than anatase and rutile. The deposit is favored when hematite and magnetite crystals are larger. The chemical mapping on deposits show that even after being immersed in water to 288 degrees Celsius during 30 days, the deposits are still present although a loss is observed. A reference electrode was assembled to conduct electrochemical tests of Tafel able to withstand a temperature of 288 degrees Celsius and pressure of 8 MPa. The baddeleyite deposit

  7. Superficial and electrochemical study of stainless steel 304l with an inhibitory protective coating (TiO{sub 2} and ZrO{sub 2}); Estudio superficial y electroquimico de acero inoxidable 304L con una capa protectora inhibidora (TiO{sub 2} y ZrO{sub 2})

    Energy Technology Data Exchange (ETDEWEB)

    Davila N, M. L.; Contreras R, A.; Arganis J, C. R., E-mail: aida.contreras@inin.gob.mx [ININ, Carretera Mexico-Toluca s/n, 52750 Ocoyoacac, Estado de Mexico (Mexico)

    2014-10-15

    The degradation mechanisms in the boiling water reactors (BWR) have been an alert focus for owners, especially the cracking by stress corrosion cracking (SCC), therefore different techniques have been studied to inhibit this problem inside which is the water injection of hydrogen feeding (HWC, Hydrogen Water Chemistry), together with the noble metals injection (NMCA, Nobel Metal Chemical Addition) and the ceramic materials injection that form an inhibitory protective coating (Ipc). In this work the Ipc was simulated, for which were carried out hydro-thermals deposits starting from suspensions of 1000 ppm of zirconium oxide in its crystalline phase baddeleyite and titanium oxides in its anatase and rutile phases, on test tubes of stainless steel 304l previously rusty under simulated conditions of pressure and temperature of a BWR (288 C and 8 MPa). The superficial characterization was realized by scanning electron microscopy, energy-dispersive of X-ray and X-ray diffraction. The capacity to mitigate the corrosion was studied with the electrochemical technique of Tafel polarization (288 C and 8 MPa). The steel presents the formation of two oxide coatings formed by magnetite and hematite. The baddeleyite presents a deposit more thick and homogeneous it also presents the most negative electrochemical potential of corrosion, what indicates that it has the bigger capacity to mitigate the SCC. (Author)

  8. Phosphate coating on stainless steel 304 sensitized;Recubrimiento fosfatado sobre acero inoxidable 304 sensibilizado

    Energy Technology Data Exchange (ETDEWEB)

    Cruz V, J. P. [IPN, Centro de Investigacion en Ciencia Aplicada y Tecnologia Avanzada, Unidad Altamira, Km. 14.5 Carretera Tampico-Puerto Industrial Altamira, 89600 Altamira, Tamaulipas (Mexico); Vite T, J. [ININ, Carretera Mexico-Toluca s/n, Ocoyoacac 52750, Estado de Mexico (Mexico); Castillo S, M.; Vite T, M., E-mail: jpcruz@ipn.m [IPN, Escuela Superior de Ingenieria Mecanica y Electrica, Seccion de Estudios de Posgrado e Investigacion, Unidad Profesional -Adolfo Lopez Mateos-, Zacatenco, 07738 Mexico, D. F. (Mexico)

    2009-07-01

    The stainless steel 304 can be sensitized when welding processes are applied, that causes the precipitation of chromium carbide in the grain limits, being promoted in this way the formation of galvanic cells and consequently the corrosion process. Using a phosphate coating is possible to retard the physiochemical damages that can to happen in the corrosion process. The stainless steel 304 substrate sensitized it is phosphate to base of Zn-Mn, in a immersion cell very hot. During the process was considered optimization values, for the characterization equipment of X-rays diffraction and scanning electron microscopy was used. The XRD technique confirmed the presence of the phases of manganese phosphate, zinc phosphate, as well as the phase of the stainless steel 304. When increasing the temperature from 60 to 90 C in the immersion process a homogeneous coating is obtained. (Author)

  9. Forging evaluaion of 304L stainless steel

    International Nuclear Information System (INIS)

    Packard, C.L.; Edstrom, C.M.

    1979-01-01

    The objective of this project was to evaluate and characterize the effects of various forging parameters on the metallographic structure and mechanical properties of 304L stainless steel forgings. Upset and die forgings were produced by hammer and Dynapak forging with forging temperatures ranging from 760 to 1145 0 C, upset reductions ranging from 20 to 60%, and annealing times ranging from 0 to 25 minutes at 843 0 C. The carbide precipitation behavior observed was found to be a function of forging temperature and annealing time. Higher forging temperatures were beneficial in avoiding continuous carbide precipitation and annealing at 843 0 C promoted increased carbide precipitation. The yield strength of the unannealed forgings decreased with increasing forging temperature and, with the exception of the 1145 0 C upset forgings, was significantly lowered by annealing

  10. Acoustic emission from hydrogen saturated Type 304L stainless steel

    International Nuclear Information System (INIS)

    Caskey, G.R. Jr.

    1978-01-01

    Acoustic emission is attributed to energy release within a material body by localized plastic deformation or failure processes. The elastic stress waves may come from slip band formation, mechanical twinning, martensite transformation, or crack propagation. Each of these processes has slightly different acoustic characteristics allowing for easy identification. Acoustic emission was monitored during tensile tests of Type 304L austenitic stainless steel to explore the applicability of the technique to hydrogen-assisted fracture

  11. Modeling of residual stress state in turning of 304L

    International Nuclear Information System (INIS)

    Valiorgue, F.; Rech, J.; Bergheau, J.M.

    2010-01-01

    Research presented in this paper aims to link machining parameters to residual stress state and helps understanding mechanisms responsible of machined surface properties modifications. The first presented works are based on an experimental campaign. They reproduce the finishing turning operation of 304L and allow observing the residual stress state evolution at the work piece surface and for an affected depth of 0.2 mm for such processes. Then, the finishing turning operation is simulated numerically in order to realize the same sensitivity study to cutting parameters. This simulation is based on an hybrid approach mixing experimental data and numerical simulation. This method allows getting round the classical difficulties of turning simulation by applying equivalent thermo mechanical loadings onto the work piece surface without modeling the material separation phenomena. Moreover the numerical model uses an hardening law taking into account dynamic recrystallization phenomena. (authors)

  12. Constant extension rate testing of Type 304L stainless steel in simulated waste tank environments

    International Nuclear Information System (INIS)

    Wiersma, B.J.

    1992-01-01

    New tanks for storage of low level radioactive wastes will be constructed at the Savannah River Site (SRS) of AISI Type 304L stainless steel (304L). The presence of chlorides and fluorides in the wastes may induce Stress Corrosion Cracking (SCC) in 304L. Constant Extension Rate Tests (CERT) were performed to determine the susceptibility of 304L to SCC in simulated wastes. In five of the six tests conducted thus far 304L was not susceptible to SCC in the simulated waste environments. Conflicting results were obtained in the final test and will be resolved by further tests. For comparison purposes the CERT tests were also performed with A537 carbon steel, a material similar to that utilized for the existing nuclear waste storage tanks at SRS

  13. Evolution of microstructure in laser welding of SS304L

    International Nuclear Information System (INIS)

    Kumar, Santosh; Kushwaha, R.P.; Viswanadham, C.S.; Dey, G.K.

    2009-01-01

    Laser welding is an important joining process and its application in industries is growing rapidly. One can produce laser welds over a wide range of process parameters and this offers very good opportunity for producing microstructure of different morphology and scales in the weldment. Weld beads have been produced on 5 mm thick plates of SS304L using CW Nd-YAG laser. Laser power was varied in 200 W to 1000 W range and welding speed was varied in 100 mm/mm to 1000 mm/mm. This resulted in weld beads of different morphology. Microstructure of the weld beads was examined on the cross-section as well as in the axial direction using optical microscopy and Transmission Electron Microscopy (TEM) to study evolution of the microstructure in the weldment. Microstructure was cellular and cellular-dendritic with grains growing from the fusion line towards the centerline. In the central region, cellular growth along the welding direction was observed. The cell size was found to increase with increasing laser power and decreasing welding speed. The findings are presented in this paper. (author)

  14. Simulation of Friction Stir Processing in 304L Stainless Steel

    Directory of Open Access Journals (Sweden)

    Miles M.P.

    2016-01-01

    Full Text Available A major dilemma facing the nuclear industry is repair or replacement of stainless steel reactor components that have been exposed to neutron irradiation. When conventional fusion welding is used for weld repair, the high temperatures and thermal stresses inherent in the process enhance the growth of helium bubbles, causing intergranular cracking in the heat-affected zone (HAZ. Friction stir processing (FSP has potential as a weld repair technique for irradiated stainless steel, because it operates at much lower temperatures than fusion welding, and is therefore less likely to cause cracking in the HAZ. Numerical simulation of the FSP process in 304L stainless steel was performed using an Eulerian finite element approach. Model input required flow stresses for the large range of strain rates and temperatures inherent in the FSP process. Temperature predictions in three locations adjacent to the stir zone were accurate to within 4% of experimentally measure values. Prediction of recrystallized grain size at a location about 6mm behind the tool center was less accurate, because the empirical model employed for the prediction did not account for grain growth that occurred after deformation in the experiment was halted.

  15. Weld solidification cracking in 304 to 304L stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Hochanadel, Patrick W [Los Alamos National Laboratory; Lienert, Thomas J [Los Alamos National Laboratory; Martinez, Jesse N [Los Alamos National Laboratory; Martinez, Raymond J [Los Alamos National Laboratory; Johnson, Matthew Q [Los Alamos National Laboratory

    2010-01-01

    A series of annulus welds were made between 304 and 304L stainless steel coaxial tubes using both pulsed laser beam welding (LBW) and pulsed gas tungsten arc welding (GTAW). In this application, a change in process from pulsed LBW to pulsed gas tungsten arc welding was proposed to limit the possibility of weld solidification cracking since weldability diagrams developed for GTAW display a greater range of compositions that are not crack susceptible relative to those developed for pulsed LBW. Contrary to the predictions of the GTAW weldability diagram, cracking was found. This result was rationalized in terms of the more rapid solidification rate of the pulsed gas tungsten arc welds. In addition, for the pulsed LBW conditions, the material compositions were predicted to be, by themselves, 'weldable' according to the pulsed LBW weldability diagram. However, the composition range along the tie line connecting the two compositions passed through the crack susceptible range. Microstructurally, the primary solidification mode (PSM) of the material processed with higher power LBW was determined to be austenite (A), while solidification mode of the materials processed with lower power LBW apparently exhibited a dual PSM of both austenite (A) and ferrite-austenite (FA) within the same weld. The materials processed by pulsed GT A W showed mostly primary austenite solidification, with some regions of either primary austenite-second phase ferrite (AF) solidification or primary ferrite-second phase austenite (FA) solidification. This work demonstrates that variations in crack susceptibility may be realized when welding different heats of 'weldable' materials together, and that slight variations in processing can also contribute to crack susceptibility.

  16. Passivity and passivity breakdown of 304L stainless steel in hot and concentrated nitric acid

    International Nuclear Information System (INIS)

    Gillard-Tcharkhtchi, Elsa

    2014-01-01

    The objective of this study is to characterize the oxidation behavior of 304L stainless steel (SS) in representative conditions of spent nuclear fuel reprocessing, i.e. in hot and concentrated nitric acid. In these conditions the SS electrochemical potential is in the passive domain and its corrosion rate is low. However when the media becomes more aggressive, the potential may be shifted towards the trans-passive domain characterized with a high corrosion rate. Passivity and passivity breakdown in the trans-passive domain are of a major interest for the industry. So as to characterize these phenomenons, this work was undertaken with the following representative conditions: a 304L SS from an industrial sheet was studied, the media was hot and concentrated HNO 3 , long term tests were performed. First, the surface of an immersed 304L SS was characterized with several complementary techniques from the micro to the nanometer scale. Then oxidation kinetics was studied in the passive and in the trans-passive domain. The oxidation behavior was studied thanks to weight loss determination and surface analysis. Finally, oxidation evolution as a function of the potential was studied from the passive to the trans-passive domain. In particular, this allowed us to obtain the anodic curve of 304L SS in hot and concentrated and to define precisely the 304L SS limits of in such conditions. (author) [fr

  17. Microstructure and mechanical properties of 304L steel fabricated by arc additive manufacturing

    Directory of Open Access Journals (Sweden)

    Ji Lei

    2017-01-01

    Full Text Available For 304L large structural parts used in nuclear power, it is hard and costly to fabricate and machine traditionally. Wire arc additive manufacturing (WAAM has low cost and high material utilization, which provides an efficient way to fabricate the large structural parts. So in this study, WAAM is used to fabricate the parts of 304L stainless steel. Through the tensile test and metallographic analysis, the mechanical properties and microstructure of the 304L stainless steel fabricated by WAAM were explored. The results indicate that with the layers depositing, the cooling rate becomes slower, the dendrites become thicker and the morphology becomes more stable. Due to the existence of dendrites, the grain boundary strengthening effect is different between the transverse direction and longitudinal direction, and resulting in anisotropy of mechanical properties. However, the mechanical properties of the parts correspond to the forged piece, which lays the foundation for future applications.

  18. Long-Term Effects of Temperature Exposure on SLM 304L Stainless Steel

    Science.gov (United States)

    Amine, Tarak; Kriewall, Caitlin S.; Newkirk, Joseph W.

    2018-03-01

    Austenitic stainless steel is extensively used in industries that operate at elevated temperatures. This work investigates the high-temperature microstructure stability as well as elevated-temperature properties of 304L stainless steel fabricated using the selective laser melting (SLM) process. Significant microstructural changes were seen after a 400°C aging process for as little as 25 h. This dramatic change in microstructure would not be expected based on the ferrite decomposition studied in conventional 304L materials. The as-built additively manufactured alloy has much faster kinetic response to heat treatment at 400°C. An investigation of the structures which occur, the kinetics of the various transformations, and the mechanical properties is presented. The impact of this on the application of SLM 304L is discussed.

  19. Effect of Temperature on the Fracture Toughness of Hot Isostatically Pressed 304L Stainless Steel

    Science.gov (United States)

    Cooper, A. J.; Brayshaw, W. J.; Sherry, A. H.

    2018-03-01

    Herein, we have performed J- Resistance multi-specimen fracture toughness testing of hot isostatically pressed (HIP'd) and forged 304L austenitic stainless steel, tested at elevated (300 °C) and cryogenic (- 140 °C) temperatures. The work highlights that although both materials fail in a pure ductile fashion, stainless steel manufactured by HIP displays a marked reduction in fracture toughness, defined using J 0.2BL, when compared to equivalently graded forged 304L, which is relatively constant across the tested temperature range.

  20. Effect of Temperature on the Fracture Toughness of Hot Isostatically Pressed 304L Stainless Steel

    OpenAIRE

    Cooper, Adam J.; Sherry, Andrew

    2018-01-01

    Herein, we have performed J-Resistance multi-specimen fracture toughness testing of hot isostatically pressed (HIP’d) and forged 304L austenitic stainless steel, tested at elevated (300 °C) and cryogenic (− 140 °C) temperatures. The work highlights that although both materials fail in a pure ductile fashion, stainless steel manufactured by HIP displays a marked reduction in fracture toughness, defined using J0.2BL, when compared to equivalently graded forged 304L, which is relatively constant...

  1. Martensitic transformation in 304L and 316L types stainless steels cathodically hydrogen charged

    International Nuclear Information System (INIS)

    Minkovitz, E.; Eliezer, D.

    1984-01-01

    This paper reports a TEM study on the role of phase transitions at the crack tip in 304L and 316L types stainless steels cathodically hydrogen charged in the absence of any eternally applied forces. The possible role of α prime and epsilon martensite phases in the fracture mechanism is discussed

  2. Dynamic compressive response of wrought and additive manufactured 304L stainless steels

    Directory of Open Access Journals (Sweden)

    Nishida Erik

    2015-01-01

    Full Text Available Additive manufacturing (AM technology has been developed to fabricate metal components that include complex prototype fabrication, small lot production, precision repair or feature addition, and tooling. However, the mechanical response of the AM materials is a concern to meet requirements for specific applications. Differences between AM materials as compared to wrought materials might be expected, due to possible differences in porosity (voids, grain size, and residual stress levels. When the AM materials are designed for impact applications, the dynamic mechanical properties in both compression and tension need to be fully characterized and understood for reliable designs. In this study, a 304L stainless steel was manufactured with AM technology. For comparison purposes, both the AM and wrought 304L stainless steels were dynamically characterized in compression Kolsky bar techniques. They dynamic compressive stress-strain curves were obtained and the strain rate effects were determined for both the AM and wrought 304L stainless steels. A comprehensive comparison of dynamic compressive response between the AM and wrought 304L stainless steels was performed. SAND2015-0993 C.

  3. Multitechnique characterisation of 304L surface states oxidised at high temperature in steam and air atmospheres

    Energy Technology Data Exchange (ETDEWEB)

    Mamede, Anne-Sophie, E-mail: anne-sophie.mamede@ensc-lille.fr [University Lille, CNRS, ENSCL, Centrale Lille, University Artois, UMR 8181 – UCCS – Unité de Catalyse et Chimie du Solide, F-59000 Lille (France); Nuns, Nicolas, E-mail: nicolas.nuns@univ-lille1.fr [University Lille, CNRS, ENSCL, Centrale Lille, University Artois, UMR 8181 – UCCS – Unité de Catalyse et Chimie du Solide, F-59000 Lille (France); Cristol, Anne-Lise, E-mail: anne-lise.cristol@ec-lille.fr [University Lille, CNRS, Centrale Lille, Arts et Métiers Paris Tech, FRE 3723 – LML – Laboratoire de Mécanique de Lille, F-59000 Lille (France); Cantrel, Laurent, E-mail: laurent.cantrel@irsn.fr [Institut de Radioprotection et de Sûreté Nucléaire, PSN-RES, Cadarache, Saint Paul lez Durance, 13115 (France); Laboratoire de Recherche Commun IRSN-CNRS-Lille 1: «Cinétique Chimique, Combustion, Réactivité» (C3R), Cadarache, Saint Paul lez Durance, 13115 (France); Souvi, Sidi, E-mail: sidi.souvi@irsn.fr [Institut de Radioprotection et de Sûreté Nucléaire, PSN-RES, Cadarache, Saint Paul lez Durance, 13115 (France); Laboratoire de Recherche Commun IRSN-CNRS-Lille 1: «Cinétique Chimique, Combustion, Réactivité» (C3R), Cadarache, Saint Paul lez Durance, 13115 (France); and others

    2016-04-30

    Graphical abstract: - Highlights: • Mutitechnique characterisation of oxidised 304L. • Oxidation at high temperature under steam and air conditions of 304L stainless steel. • Chromium and manganese oxides formed in the outer layer. • Oxide profiles differ in air or steam atmosphere. - Abstract: In case of a severe accident occurring in a nuclear reactor, surfaces of the reactor coolant system (RCS), made of stainless steel (304L) rich in Cr (>10%) and Ni (8–12%), are oxidised. Fission products (FPs) are released from melt fuel and flow through the RCS. A part of them is deposited onto surfaces either by vapour condensation or by aerosol deposition mechanisms. To be able to understand the nature of interactions between these FPs and the RCS surfaces, a preliminary step is to characterize the RSC surface states in steam and air atmosphere at high temperatures. Pieces of 304L stainless steel have been treated in a flow reactor at two different temperatures (750 °C and 950 °C) for two different exposition times (24 h and 72 h). After surfaces analysing by a unique combination of surface analysis techniques (XPS, ToF-SIMS and LEIS), for 304L, the results show a deep oxide scale with multi layers and the outer layer is composed of chromium and manganese oxides. Oxide profiles differ in air or steam atmosphere. Fe{sub 2}O{sub 3} oxide is observed but in minor proportion and in all cases no nickel is detected near the surface. Results obtained are discussed and compared with the literature data.

  4. Influencia de la adición de cobre y de bronce sobre las propiedades de los aceros inoxidables austeníticos sinterizados

    Directory of Open Access Journals (Sweden)

    Velasco, F.

    1997-04-01

    Full Text Available The effect that, on AISI 316L and 304L stainless steels alloyed with copper and bronze in different percentages up to a maximun of 20 % wt, produce both the alloying content and the sintering temperature over physical and mechanical properties and over the microstructure of sintered stainless steels are studied. Alloying with copper and bronze improves the density of sintered steels at the two sintering temperatures used. Copper and bronze promote liquid phase sintering (transitory or permanent, that activates sintering process. Tensile strength of stainless steel is highly improved for higher alloying contents. Moreover, tensile strength presents greater values alloying with bronze than with copper.

    Partiendo de los aceros inoxidables AISI 316L y 304L a los que se añadió cobre y bronce en diferentes porcentajes hasta el 20 % en peso, se estudia el efecto que la cantidad de aleante y la temperatura de sinterización tienen sobre las propiedades físicas y mecánicas y sobre la microestructura de los aceros inoxidables sinterizados. La aleación con cobre y con bronce aumenta la densidad de los aceros sinterizados para las dos temperaturas de sinterización utilizadas. El cobre y el bronce provocan la aparición de fase líquida (transitoria o permanente que activa el proceso de sinterización. La resistencia a la tracción del acero inoxidable experimenta un fuerte incremento para los contenidos más elevados de aleante. Además, la resistencia a la tracción alcanza mayores valores para la aleación con bronce que con cobre.

  5. Estudio de la resistencia a la corrosión por picadura de aceros inoxidables austeníticos: influencia de la adición de manganeso en solución sólida

    OpenAIRE

    José Wilmar Calderón-Hernández; Lara Beatriz Braga Luz; Duberney Hincapie-Ladino; Neusa Alonso-Falleiros

    2015-01-01

    Este documento presenta los resultados de una investigación sobre la influencia del Mn en solución sólida sobre la resistencia a la corrosión por picadura de dos aceros inoxidables austeníticos, uno denominado 17Cr6Mn5Ni y un acero comercial UNS S304L utilizado como material de referencia. Fueron usadas soluciones electrolíticas de 0,6M NaCl en tres diferentes condiciones de concentración de oxígeno (solución desaireada, naturalmente aireada y aireada artificialment...

  6. Corrosion and microstructural aspects of dissimilar joints of titanium and type 304L stainless steel

    International Nuclear Information System (INIS)

    Mudali, U. Kamachi.; Ananda Rao, B.M.; Shanmugam, K.; Natarajan, R.; Raj, Baldev

    2003-01-01

    To link titanium and zirconium metal based (Ti, Zr-2, Ti-5%Ta, Ti-5%Ta-1.8Nb) dissolver vessels containing highly radioactive and concentrated corrosive nitric acid solution to other nuclear fuel reprocessing plant components made of AISI type 304L stainless steel (SS), high integrity and corrosion resistant dissimilar joints between them are necessary. Fusion welding processes produce secondary precipitates which dissolve in nitric acid, and hence solid-state processes are proposed. In this work, various dissimilar joining processes available for producing titanium-304L SS joints with adequate strength, ductility and corrosion resistance for this critical application are highlighted. Developmental efforts made at IGCAR, Kalpakkam are outlined. The possible methods and the microstructural-metallurgical properties of the joints along with corrosion results obtained with three phase (liquid, vapour, condensate) corrosion testing are discussed. Based on the results, dissimilar joint produced by the explosive joining process was adopted for plant application

  7. Martensitic Transformation in Ultrafine-Grained Stainless Steel AISI 304L Under Monotonic and Cyclic Loading

    Directory of Open Access Journals (Sweden)

    Heinz Werner Höppel

    2012-02-01

    Full Text Available The monotonic and cyclic deformation behavior of ultrafine-grained metastable austenitic steel AISI 304L, produced by severe plastic deformation, was investigated. Under monotonic loading, the martensitic phase transformation in the ultrafine-grained state is strongly favored. Under cyclic loading, the martensitic transformation behavior is similar to the coarse-grained condition, but the cyclic stress response is three times larger for the ultrafine-grained condition.

  8. Intergranular stress corrosion cracking of ion irradiated 304L stainless steel in PWR environment

    International Nuclear Information System (INIS)

    Gupta, Jyoti

    2016-01-01

    IASCC is irradiation - assisted enhancement of intergranular stress corrosion cracking susceptibility of austenitic stainless steel. It is a complex degrading phenomenon which can have a significant influence on maintenance time and cost of PWRs' core internals and hence, is an issue of concern. Recent studies have proposed using ion irradiation (to be specific, proton irradiation) as an alternative of neutron irradiation to improve the current understanding of the mechanism. The objective of this study was to investigate the cracking susceptibility of irradiated SA 304L and factors contributing to cracking, using two different ion irradiations; iron and proton irradiations. Both resulted in generation of point defects in the microstructure and thereby causing hardening of the SA 304L. Material (unirradiated and iron irradiated) showed no susceptibility to intergranular cracking on subjection to SSRT with a strain rate of 5 * 10 -8 s -1 up to 4 % plastic strain in inert environment. But, irradiation (iron and proton) was found to increase intergranular cracking severity of material on subjection to SSRT in simulated PWR primary water environment at 340 C. Correlation between the cracking susceptibility and degree of localization was studied. Impact of iron irradiation on bulk oxidation of SA 304L was studied as well by conducting an oxidation test for 360 h in simulated PWR environment at 340 C. The findings of this study indicate that the intergranular cracking of 304L stainless steel in PWR environment can be studied using Fe irradiation despite its small penetration depth in material. Furthermore, it has been shown that the cracking was similar in both iron and proton irradiated samples despite different degrees of localization. Lastly, on establishing iron irradiation as a successful tool, it was used to study the impact of surface finish and strain paths on intergranular cracking susceptibility of the material. (author) [fr

  9. Evaluation of Mechanical Properties and Fatigue Behavior of STS 304L due to Plastic Working

    Energy Technology Data Exchange (ETDEWEB)

    Shim, Hyun-Bo [Yeungnam Univ., Daegu (Korea, Republic of); Kim, Young-Kyun [KOGAS Research Institute, Seoul (Korea, Republic of); Suh, Chang-Min [Kyungpook Nat’l Univ., Daegu (Korea, Republic of)

    2017-07-15

    The purpose of this study is to investigate the influence of the cold reduction rate and an ultrasonic fatigue test (UFT) on the fatigue behaviors of STS 304L. The tensile strength, yield strength, hardness value and fatigue limit in the UFT fatigue test linearly increased as thickness decreased from 1.5 mm to 1.1 mm, as the cold reduction rate of STS 304L increased. As a result of the UFT fatigue test (R = -1) of four specimens, the fatigue limit of the S-N curve formed a knee point in the region of 10{sup 6}, and the 2nd fatigue limit caused by giga cycle fatigue did not appeared. In the case of t = 1.1 mm, the highest fatigue limit was 345 MPa, which was 64.3% higher than the original material (t = 1.5 mm). As a result of the UFT fatigue test of STS 304L, many small surface cracks occurred, grown, coalesced while tearing.

  10. Corrosion testing of type 304L stainless steel in tuff groundwater environments

    International Nuclear Information System (INIS)

    Westerman, R.E.; Pitman, S.G.; Haberman, J.H.

    1987-11-01

    The stress-corrosion cracking (SCC) resistance of Type 304L stainless steel (SS) to elevated temperatures in tuff rock and tuff groundwater environments was determined under irradiated and nonirradiated conditions using U-bend specimens and slow-strain-rate tests. The steel was tested both in the solution-annealed condition and after sensitization heat treatments. The material was found to be susceptible to SCC in both the solution-annealed and solution-annealed-and-sensitized conditions when exposed to an irradiated crushed tuff rock environment containing air and water vapor at 90 0 C. A similar exposure at 50 0 C did not result in failure after a 25-month test duration. Specimens of sensitized 304 SS conditioned with a variety of sensitization heat treatments resisted failure during a test of 1-year duration in which a nonirradiated environment of tuff rock and groundwater held at 200 0 C was allowed to boil to dryness on a cyclical basis. All specimens of sensitized 304 SS exposed to this environment failed. Slow-strain-rate studies were performed on 304L, 304, and 316L SS specimens. The 304L SS was tested in J-13 well water at 150 0 C, and the 316L SS at 95 0 C. Neither material showed evidence of SCC in these tests. Sensitized 304 SS did exhibit SCC in J-13 well water in tests conducted at 150 0 C. 12 refs., 27 figs., 13 tabs

  11. Assessment and comparison of oxides grown on 304l ods steel and 304l ss in water environment in supercritical conditions

    International Nuclear Information System (INIS)

    Mihalache, M.; Dinu, A.; Fulger, M.; Zhou, Z.; Mihalache, M.

    2013-01-01

    In order to fulfil superior cladding for new reactor generation G IV, the austenitic 3 04 L stainless steel was improved by oxide dispersion strengthening (ODS), using two nano-oxides: titanium and yttrium oxides. The behaviour of the new material resulted, 304 ODS, in water at supercritical temperature of about 550 O C and 25 MPa pressure, was considered. The oxidation kinetics by weigh gain measurements for both materials have been estimated and compared. The weight gain of ODS samples is higher than basic austenitic steel up to 1320 hours. The oxides developed on the ODS samples in SCPW are layered and more uniform than in 304 L SS. The protectively character of oxide films was estimated by different techniques. The morphology of oxide surface, the layering and chemical formula of oxides films were investigated by scanning electron microscopy (SEM), Energy Dispersion X-Ray Spectrometry (EDS), electrochemical impedance spectrometry (EIS) and by Small Angle X-ray Diffraction (SAXD). 1. (authors)

  12. Preparation of high-performance ultrafine-grained AISI 304L stainless steel under high temperature and pressure

    Directory of Open Access Journals (Sweden)

    Peng Wang

    2016-08-01

    Full Text Available Bulk ultra-fine grained (UFG AISI 304L stainless steel with excellent mechanical properties was prepared by a high-temperature and high-pressure (HTHP method using nanocrystalline AISI 304L stainless steel powders obtained from ball milling. Samples were sintered in high-pressure conditions using the highest martensite content of AISI 304L stainless steel powders milled for 25 h. Analyses of phase composition and grain size were accomplished by X-ray diffraction and Rietveld refinement. By comparing the reverse martensite transformation under vacuum and HTHP treat, we consider that pressure can effectively promote the change in the process of transformation. Compared with the solid-solution-treated 304L, the hardness and yield strength of the samples sintered under HTHP are considerably higher. This method of preparation of UFG bulk stainless steel may be widely popularised and used to obtain UFG metallic materials with good comprehensive performance.

  13. Irradiation-induced creep in 316 and 304L stainless steels

    International Nuclear Information System (INIS)

    Walters, L.C.; McVay, G.L.; Hudman, G.D.

    1977-01-01

    Recent results are presented from the in-reactor creep experiments that are being conducted by Argonne National Laboratory. The experiments consist of four subassemblies that contain helium-pressurized as well as unstressed capsules of 316 and 304L stainless steels in several metallurgical conditions. Experiments are being irradiated in row 7 of the EBR-II sodium-cooled fast breeder reactor. Three of the subassemblies are being irradiated at temperatures near 400 0 C, and the fourth subassembly is being irradiated at a temperature of 550 0 C. Creep and swelling strains were determined by profilometer measurements on the full length of the capsules after each irradiation cycle. The accumulated neutron dose on the 304L capsules at 385 0 C was 45 dpa; on the 316 capsules at 400 0 C, 40 dpa; and on the 316 capsules at 550 0 C, 25 dpa. It was found that the in-reactor creep rates were linearly dependent on hoop stress, with the exception being capsules of 316 stainless steel that had been given long-term carbide aging treatment and then irradiated at 550 0 C. Those capsules exhibited much higher creep and swelling rates than their unaged counterparts. For the metallurgical conditions where significant swelling was observed (solution-annealed 304L and aged 316 stainless steels), it was found that the in-reactor creep rates were readily fit to a model that related the creep rates to accumulated swelling. Additionally, it was found that the stress-normalized creep rate for 20%-cold-worked 316 stainless steel at a temperature of 550 0 C was 1.6 times that observed at 400 0 C

  14. Behaviour under fatigue of AISI 304-L stainless steel welded joints

    International Nuclear Information System (INIS)

    Scal, M.W.; Joia, C.J.B.M.; Sousa e Silva, A.S. de

    1979-01-01

    The fatigue behaviour at room temperature of AISI-304-L stainless steel welded joints obtained by two distinct welding methods was studied. The results obtained were compared to those characteristic of the base metal. The welded joint fatigue samples were rectified in order to eliminate the effect of the welded seam geometry. It was concluded that the mechanisms of fatigue crack start in this case is commanded by the austenitic matrix, there being no influence of the delta ferrite rate and distribution present at the melted zone. (Author) [pt

  15. Comparative study of the microbiological corrosion among an AISI 304L and an API X65

    International Nuclear Information System (INIS)

    Diaz S, A.; Arganis J, C.; Luna C, P.; Carapia M, L.; Gonzalez F, E.

    2004-01-01

    Metallic samples of AISI 304L sensitized and API X65, were subjected to the action of an inoculated media with reductive sulphate microorganisms (SBR), carrying out electrochemical evaluations by means of the techniques of Polarization Resistance (RP), Tafel extrapolation (ET) and Electrochemical Noise (RE). The generated information was complemented with the analysis and diagnostic of the present damage in the surfaces exposed in both metals. The used electrochemical techniques allow to determine the corrosion velocities associated to each system, establishing that the uniform corrosion is not affected by the effect of the microorganisms; however, electrochemical noise, evidenced the formation of stings associated to the presence of bacteria. (Author)

  16. Fatigue of welded joint in a stainless steel AISI 304 L

    International Nuclear Information System (INIS)

    Kuromoto, N.K.; Guimaraes, A.S.; Miranda, P.E.V. de

    1986-01-01

    The flexion fatigue behavior for the base metal and welded joint of an AISI 304 L stainless steel type, used in the Angra-1 reactor, was determined. An automatic welding process was used with improved procedures in order to assure better welding metallurgy. Fatigue tests samples reinforcements were done to allow the evaluation of metallurgical variables, specially the role played by delta ferrite. The resulting welded joint showed better fatigue life than the base metal. Delta ferrite was found to play an important role on the initiation and propagation processes of the fatigue cracks. (Author) [pt

  17. Swelling of AISI 304L in response to simultaneous variations in stress and displacement rate

    International Nuclear Information System (INIS)

    Porter, D.L.; Garner, F.A.

    1984-01-01

    The duration of the transient regime of neutron-induced swelling in annealed AISI 304L at 400 0 C is sensitive to both stress and displacement rate variations. The simultaneous application of both variables exerts a synergistic effect on the transient regime. The duration of this regime cannot be reduced below a required intrinsic exposure of approx. 10 dpa, however, which has been found to be characteristic of all Fe-Ni-Cr austenitic alloys. This is four times larger than that currently assumed in the stress-affected swelling equation for 20% cold-worked AISI 316

  18. Moessbauer spectroscopy and X-ray diffraction study of 304 L stainless steel thin films

    International Nuclear Information System (INIS)

    Boubeker, B.; Eymery, J.P.; Goudeau, P.; Sayouty, E.H.

    1994-01-01

    304 L stainless steel films (SS) were elaborated using an ion-beam sputtering technique. The target material was a sheet of commercial grade 304 L SS. The starting material was first analysed by both conversion electron Moessbauer spectroscopy (CEMS) and X-ray diffraction. The nonmagnetic state and f.c.c. structure of this material were confirmed. The films were deposited on various substrates with thicknesses in the 175-800 nm range. The films are found to have both b.c.c. structure and ferromagnetic character. X-ray diffraction technique was also used in order to determine the residual stresses developed during the deposition process. The second stage of the work is devoted to the evolution of the film structure as a function of annealing treatments. So isochronal and isothermal kinetics at temperatures higher than 913 K have allowed to follow the alpha --> gamma phase transformation using X-ray diffraction and CEMS technique.The X-ray diffractograms reveal the existence of both b.c.c. and f.c.c. phases. Similar results can be deduced from Moessbauer spectra due to the single line coming from the non-magnetic phase and the sextet coming from the ferromagnetic phase. In addition the CEMS spectra reveal that the ferromagnetic component is split into two parts which indicates the existence of two iron sites. 1 fig., 4 refs.(author)

  19. Effect of H2O2 on the corrosion behavior of 304L stainless steel

    International Nuclear Information System (INIS)

    Song, Taek Ho

    1994-02-01

    In connection with the safe storage of high level nuclear waste, effect of H 2 O 2 on the corrosion behavior of 304L stainless steel was examined. Open circuit potentials and polarization curves were measured with and without H 2 O 2 . The experimental results show that H 2 O 2 increased corrosion potential and decreased pitting potential. The passive range, therefore, decreased as H 2 O 2 concentration increased, indicating that pitting resistance was decreased by the existence of H 2 O 2 in the electrolyte. These effects of H 2 O 2 on corrosion of 304L stainless steel are considered to be similar to those of γ-irradiation. To compare the effects of H 2 O 2 with those of O 2 , cathodic and anodic polarization curves were made in three types of electrolyte such as aerated, deaerated, and stirred electrolyte. The experimental results show that the effects of H 2 O 2 on the corrosion behavior were very similar to those of O 2 such as increase of corrosion potential, decrease of pitting resistance, and increase of repassivation potential. Further, H 2 O 2 played much greater role in controlling cathodic reaction rate in neutral water environment. In acid and alkaline media, potential shifts by H 2 O 2 were restricted by the large current density of proton reduction and by the le Chatelier's principle respectively

  20. Effect of H2O2 on the corrosion behavior of 304L stainless steel

    International Nuclear Information System (INIS)

    Song, Taek Hoh; Kim, In Sub; Noh, Sung Kee

    1995-01-01

    In connection with the safe storage of high level nuclear waste, effect of H 2 O 2 on the corrosion behavior of 304L stainless steel was examined. Open circuit potentials and polarization curves were measured with and without H 2 O 2 . The experimental results show that H 2 O 2 increased corrosion potential and decreased pitting potential. The passive range, therefore, decreased as H 2 O 2 concentration increased, indicating that pitting resistance was decreased by the existence of H 2 O 2 in the electrolyte. These effects of H 2 O 2 on corrosion of 304L stainless steel are considered to be similar to those of γ-irradiation. To compare the effects of H 2 O 2 with those of O 2 , cathodic and anodic polarization curves were made in three types of electrolyte such as aerated, deaerated, and stirred electrolyte. The experimental results show that the effects of H 2 O 2 on the corrosion behavior were very similar to those of O 2 such as increase of corrosion potential, decrease of pitting resistance, and increase of repassivation potential. In acid and alkaline media, the corrosion potential shifts by H 2 O 2 were restricted by the large current density of proton reduction and by the le Chatelier's principle respectively. 13 figs., 1 tabs., 17 refs. (Author)

  1. Effect of Prior Deformation on Welding Microstructure of Steel 304L

    Directory of Open Access Journals (Sweden)

    WU Luo-fei

    2017-01-01

    Full Text Available This subject was raised by an automotive company.Based on the welding design on the curved surface,the effect of prior deformation on the weld structure was studied.Metal active-gas welding was used on the T-joint and pre-deformed plates of austenitic stainless steel 304L to find the proper welding parameters and observe the effect of prior deformation on the microstructure.The proper parameters acquired are:the speed of the torch is 4mm/s,the speed of delivery of welding wire is 2.5m/min and the voltage is 17V.In the T-joint and pre-deformed joint,the weld toes are in the zone with strain of 0% and 30%.In the pre-deformed welding specimen,it was observed that the fusion zone and partially melted zone are narrowed,carbide precipitation and ferrites are found less.In all,the microstructure in the pre-deformed weld joints on 304L is more uniform.

  2. Carburization behavior under the pits induced by metal dusting in 304L and 347 stainless steels

    Energy Technology Data Exchange (ETDEWEB)

    Chang, Chia-Hao [Department of Materials Engineering and Science, National Cheng Kung University, Tainan 701, Taiwan (China); Tsai, Wen-Ta, E-mail: wttsai@mail.ncku.edu.tw [Department of Materials Engineering and Science, National Cheng Kung University, Tainan 701, Taiwan (China)

    2009-08-15

    The metal dusting behavior of Type 304L and 347 stainless steels (SSs) in a flowing mixed CO/H{sub 2}/H{sub 2}O gas stream at 600 deg. C was investigated. After exposure in a 35% CO + 60% H{sub 2} + 5% H{sub 2}O gas for 500 h, large pits were formed on both steel surfaces. The aspect ratio of the pits formed in 304L SS was higher than that of the pits formed in 347 SS. The microstructures and chemical compositions of the reaction products and those of the substrate under the pits were examined by using a scanning electron microscope (SEM) combined with an energy dispersive spectrometer (EDS). A Cr-depleted zone containing voids was formed on the outer surface just beneath the pit. Massive matrix carburization and intergranular carbide precipitation were seen for both steels. The experimental results showed that niobium (Nb) could delay the ingress of carbon and retard the metal dusting reaction.

  3. The effect of cysteine on the corrosion of 304L stainless steel in sulphuric acid

    International Nuclear Information System (INIS)

    Silva, A.B.; Agostinho, S.M.L.; Barcia, O.E.; Cordeiro, G.G.O.; D'Elia, E.

    2006-01-01

    The effect of cysteine on the corrosion of 304L stainless steel in 1 mol l -1 H 2 SO 4 was studied using open-circuit potential measurements, anodic polarization curves, electrochemical impedance spectroscopy (EIS) and scanning electron microscopy (SEM). All the electrochemical measurements obtained in the presence of low cysteine concentration (10 -6 -10 -5 mol l -1 ) presented the same behaviour as those obtained in the absence of cysteine, a passivated steel surface. However, for higher cysteine concentrations (10 -4 -10 -2 mol l -1 ), a different behaviour was observed: the corrosion potential stabilized at a more negative value; an active region was observed in the anodic polarization curves and the electrochemical impedance diagrams showed an inductive loop at lower frequencies and a much lower polarization resistance. These results show that the presence of cysteine at high concentration turns the surface of 304L stainless steel electrochemically active, probably dissolving the passivation layer and promoting the stainless steel anodic dissolution. SEM experiments performed after immersion experiments at corrosion potential were in good agreement with the electrochemical results

  4. Dependence of corrosion properties of AISI 304L stainless steel on the austenite grain size

    Energy Technology Data Exchange (ETDEWEB)

    Sabooni, Soheil; Rashtchi, Hamed; Eslami, Abdoulmajid; Karimzadeh, Fathallah; Enayati, Mohammad Hossein; Raeissi, Keyvan; Imani, Reihane Faghih [Isfahan Univ. of Technology, Isfahan (Iran, Islamic Republic of). Dept. of Materials Engineering; Ngan, Alfonso Hing Wan [The Univ. of Hong Kong (China). Dept. of Mechanical Engineering

    2017-07-15

    The corrosion resistance of austenitic stainless steels is known to be hampered by the loss of chromium available for passive surface layer formation as a result of chromium carbide precipitation at austenite grain boundaries during annealing treatments. Although high-temperature annealing can promote carbide dissolution leading to better corrosion resistance, grain coarsening also results, which would lead to poorer mechanical properties. Processing methods to achieve both good corrosion resistance and mechanical properties are thus highly desirable for austenitic stainless steels. In the present study, we show that the corrosion resistance of AISI 304L stainless steel can be improved by grain refinement into the ultrafine-grained regime. Specifically, samples with different austenite grain sizes in the range of 0.65-12 μm were studied by potentiodynamic polarization and electrochemical impedance spectroscopy tests in a 3.5 wt.% NaCl solution. All samples showed a typical passive behavior with similar corrosion potential, but the corrosion current density decreased significantly with decreasing grain size. The results show that the sample with the finest grain size had the best corrosion resistance due to a higher resistance of the passive layer to pitting attacks. This study indicates that grain refinement which improves mechanical properties can also significantly improve the corrosion resistance of AISI 304L stainless steel.

  5. Behavior of stressed and unstressed 304L specimens in tuff repository environmental conditions

    International Nuclear Information System (INIS)

    Juhas, M.C.; McCright, R.D.; Garrison, R.E.

    1984-11-01

    This paper presents preliminary results of an investigation of the behavior of candidate barrier material for high-level nuclear waste storage, Type 304L stainless steel, in tuff repository environmental conditions. Tuff is a densely welded, devitrified, igneous rock common to the proposed repository site at Yucca Mountain, Nevada. The results discussed include: irradiation corrosion tests, U-bend irradiation corrosion tests, slow strain rate tests, and bent beam stress corrosion tests. Results indicate that Type 304L stainless steel shows excellent resistance to general, localized, and stress corrosion under the environmental and microstructural conditions tested so far. The environmental test conditions are 50 to 100 0 C J-13 well water (non-saline, near neutral pH, and oxic in nature) and saturated steam at 100 0 C. Microstructural conditions include solution annealed and long furnace heat treatments to provoke a sensitized structure. However, this particular type of stainless steel may be susceptible to long-term, low-temperature sensitization because of the combination of expected time at elevated temperature and residual stress in the container after emplacement in the repository. Other grades of austenitic stainless steels are reported to be more resistant to low-temperature sensitization. Future work will therefore include more extensive testing of these grades. 15 references, 5 figures, 7 tables

  6. Analysis of martensitic transformation and residual tension in an 304L stainless steel; Analise da transformacao martensitica e tensao residual em um aco inoxidavel 304L

    Energy Technology Data Exchange (ETDEWEB)

    Alves, Juciane Maria

    2014-07-01

    The relationship between plastic deformation and the strain induced phase transformation, that provides a practical route to the development of new engineering materials with excellent mechanical properties, characterize the TRIP effect 'Transformation Induced Plasticity'. Among the stainless steels, the metastable 304 L austenitic steel is susceptible to transformation of austenite-martensite phase from tensile tests at room temperature by increments of plastic deformation. It is of great technological and scientific interest the knowledge of the evolution of phase transformation and residual stress from different levels and rates of plastic deformation imposed to the material. It is also important to evaluate the interference of metallographic preparation in quantitative analyzes of this steel. The main techniques used in this study consisted of X-rays diffraction and Ferritoscopy for the quantitation phase, and XRD to residual stress analysis also. As observed, the phase transformation quantification has not suffered significant influence of the metallographic preparation and evolved from increments of plastic deformation due to different stop charges and strain rates, leading to a further strengthening of the austenite matrix. The evaluation of residual stress resulting from the martensitic transformation was susceptible to the metallographic preparation and increased its value on comparison to sample without metallographic preparation. It was also observed that the residual stress decreased with the increase of the fraction of transformed martensite. (author)

  7. Tests on mechanical behavior of 304 L stainless steel under constant stress associated with cyclic strain

    International Nuclear Information System (INIS)

    Lebey, J.; Roche, R.

    1979-01-01

    Mechanical analyses of structures, to be efficient, must incorporate materials behavior data. Among the mechanisms liable to cause collapse, progressive distortion (or ratcheting) has been the subject of only a few basic experiments, most of the investigations being theoretical. In order to get meaningful results to characterize materials behavior, an experimental study on ratcheting of austenitic steels has been undertaken at the C.E.A. This paper gives the first results of tests at room temperature on thin tubes of 304L steel submitted to an axial constant stress (primary stress) to which is added a cyclic shearing strain (secondary stress). The tests cover a large combination of the two loading modes. The main results consist of curves of cumulative iso-deformation in the primary and secondary stress field (Bree type diagrams). Results are given for plastic deformations ranging from 0.1 to 2.5% up to N=100 cycles

  8. Corrosion of type 304L stainless steel in boiling dilute neptunium nitrate solution

    International Nuclear Information System (INIS)

    Motooka, Takafumi; Kiuchi, Kiyoshi

    2003-01-01

    Corrosion of type 304L stainless steel in nitric acid solution containing neptunium was studied under immersion and heat-transfer condition. Corrosion rates of stainless steel were obtained by the weight loss measurement and the quantitative analysis of metallic ions dissolved in solution. The surface morphology was observed by scanning electron microscopy. The corrosion acceleration mechanism was investigated by polarization measurement and spectrophotometry. The corrosion rate in boiling 9M nitric acid was accelerated by addition of neptunium. The corrosion of stainless steel was promoted under heat-transfer condition compared to immersion condition. In polarization measurements, the cathodic current was increased by addition of neptunium. Spectrophotometric measurements showed the oxidization of neptunium in boiling nitric acid. It was suggested that the accelerated corrosion in nitric acid solution containing neptunium was caused by re-oxidation of neptunium. (author)

  9. Fatigue behaviour of 304L steel welded structures: influence of residual stresses and surface mechanical finishing

    International Nuclear Information System (INIS)

    Magnier-Monin, L.

    2007-12-01

    This study focuses on the influence of residual stresses and surface mechanical finishing on lifetime of stainless steel 304L welded structures. Residual stresses are determined on specific specimens of three types: base-metal, as-welded and ground-welded specimens. Each type is submitted to fatigue tests in order to assess the influence of these parameters on the lifetime, and to determine their evolution. The experiments show that an important surface stress concentration is located in the weld root of as-welded structures, which has a negative effect on the fatigue life. The grinding operation generates high-level surface residual stresses but the lifetime is higher thanks to the reduction of the notch effect. The fatigue test results are compared to the nuclear industry best-fit S-N curves. This enables the determination of correction factors related to fatigue test results of polished specimens, and to assess the lifetime of structures. (author)

  10. Stress Corrosion Cracking Susceptibility of 304L Substrate and 308L Weld Metal Exposed to a Salt Spray

    Directory of Open Access Journals (Sweden)

    Chia-Hao Hsu

    2017-02-01

    Full Text Available 304 stainless steels (SS were considered as the materials for a dry storage canister. In this study, ER (Electrode Rod 308L was utilized as the filler metal for the groove and overlay welds of a 304L stainless steel substrate, which was prepared via a gas tungsten arc-welding process in multiple passes. The electron backscatter diffraction (EBSD map was used to identify the inherent microstructures in distinct specimens. U-bend and weight-loss tests were conducted by testing the 304L substrates and welds in a salt spray containing 5 wt % NaCl at 80 °C to evaluate their susceptibility to stress corrosion cracking (SCC. Generally, the weight loss of the ER 308L deposit was higher than that of the 304L substrate in a salt spray in the same sample-prepared condition. The dissolution of the skeletal structure in the fusion zone (FZ was responsible for a greater weight loss of the 308L deposit, especially for the cold-rolled and sensitized specimen. Cold rolling was detrimental and sensitization after cold rolling was very harmful to the SCC resistance of the 304L substrate and 308L deposit. Overall, the SCC susceptibility of each specimen was correlated with its weight loss in each group.

  11. An Assessment of the Ductile Fracture Behavior of Hot Isostatically Pressed and Forged 304L Stainless Steel

    Science.gov (United States)

    Cooper, A. J.; Smith, R. J.; Sherry, A. H.

    2017-05-01

    Type 300 austenitic stainless steel manufactured by hot isostatic pressing (HIP) has recently been shown to exhibit subtly different fracture behavior from that of equivalent graded forged steel, whereby the oxygen remaining in the component after HIP manifests itself in the austenite matrix as nonmetallic oxide inclusions. These inclusions facilitate fracture by acting as nucleation sites for the initiation, growth, and coalescence of microvoids in the plastically deforming austenite matrix. Here, we perform analyses based on the Rice-Tracey (RT) void growth model, supported by instrumented Charpy and J-integral fracture toughness testing at ambient temperature, to characterize the degree of void growth ahead of both a V-notch and crack in 304L stainless steel. We show that the hot isostatically pressed (HIP'd) 304L steel exhibits a lower critical void growth at the onset of fracture than that observed in forged 304L steel, which ultimately results in HIP'd steel exhibiting lower fracture toughness at initiation and impact toughness. Although the reduction in toughness of HIP'd steel is not detrimental to its use, due to the steel's sufficiently high toughness, the study does indicate that HIP'd and forged 304L steel behave as subtly different materials at a microstructural level with respect to their fracture behavior.

  12. Effect of pre-hardening on the lifetime of type 304L austenitic stainless steels

    International Nuclear Information System (INIS)

    Kpodekon, C.

    2010-01-01

    This study deals with the effect of the loading history on the cyclic behavior and the fatigue life of two kinds (THYSSEN and CLI) of 304L stainless steel at room temperature. The experiments have been performed using two specimens' categories. The first one (virgin) has been submitted to only classical fatigue tests while in the second category, prior to the fatigue test, the specimen is subjected to a pre-hardening process under either monotonic or cyclic strain control. Cyclic softening followed by cyclic hardening are observed for the virgin specimens while only cyclic softening is exhibited by the pre-hardened specimens. The obtained results show that fatigue life is strongly influenced by the pre-hardening: it seems beneficial under stress control but detrimental under strain control, even in the presence of a compressive mean stress. The results are discussed regarding the cyclic evolution of the elastic modulus as well as the isotropic and kinematic parts of the strain hardening, and strain energy density per cycle, in different configurations: with or without prehardening,stress or strain control. (author)

  13. Low cycle fatigue: high cycle fatigue damage accumulation in a 304L austenitic stainless steel

    International Nuclear Information System (INIS)

    Lehericy, Y.

    2007-05-01

    The aim of this study was to evaluate the consequences of a Low Cycle Fatigue pre-damage on the subsequent fatigue limit of a 304L stainless steel. The effects of hardening and severe roughness (grinding) have also been investigated. In a first set of tests, the evolution of the surface damage induced by the different LCF pre-cycling was characterized. This has permitted to identify mechanisms and kinetics of damage in the plastic domain for different surface conditions. Then, pre-damaged samples were tested in the High Cycle Fatigue domain in order to establish the fatigue limits associated with each level of pre-damage. Results evidence that, in the case of polished samples, an important number of cycles is required to initiate surface cracks ant then to affect the fatigue limit of the material but, in the case of ground samples, a few number of cycles is sufficient to initiate cracks and to critically decrease the fatigue limit. The fatigue limit of pre-damaged samples can be estimated using the stress intensity factor threshold. Moreover, this detrimental effect of severe surface conditions is enhanced when fatigue tests are performed under a positive mean stress (author)

  14. Deposition and characterization of noble metal onto surfaces of 304l stainless steel

    International Nuclear Information System (INIS)

    Contreras R, A.; Arganis J, C. R.; Aguilar T, J. A.; Medina A, A. L.

    2010-10-01

    Noble metal chemical addition (NMCA) plus hydrogen water chemistry is an industry-wide accepted approach for potential intergranular stress corrosion cracking mitigation of BWR internals components. NMCA is a method of applying noble metal onto BWR internals surfaces using reactor water as the transport medium that causes the deposition of noble metal from the liquid onto surfaces. In this work different platinum concentration solutions were deposited onto pre-oxidized surfaces of 304l steel at 180 C during 48 hr in an autoclave. In order to simulate the zinc water conditions, deposits of Zn and Pt-Zn were also carried out. The solutions used to obtain the deposits were: sodium hexahydroxyplatinate (IV), zinc nitrate hydrate and zinc oxide. The deposits obtained were characterized by scanning electron microscopy and X-ray diffraction. Finally, the electrochemical corrosion potential of pre-oxidized samples with Pt deposit were obtained and compared with the electrochemical corrosion potential of only pre-oxidized samples. (Author)

  15. Superior radiation-resistant nanoengineered austenitic 304L stainless steel for applications in extreme radiation environments.

    Science.gov (United States)

    Sun, C; Zheng, S; Wei, C C; Wu, Y; Shao, L; Yang, Y; Hartwig, K T; Maloy, S A; Zinkle, S J; Allen, T R; Wang, H; Zhang, X

    2015-01-15

    Nuclear energy provides more than 10% of electrical power internationally, and the increasing engagement of nuclear energy is essential to meet the rapid worldwide increase in energy demand. A paramount challenge in the development of advanced nuclear reactors is the discovery of advanced structural materials that can endure extreme environments, such as severe neutron irradiation damage at high temperatures. It has been known for decades that high dose radiation can introduce significant void swelling accompanied by precipitation in austenitic stainless steel (SS). Here we report, however, that through nanoengineering, ultra-fine grained (UFG) 304 L SS with an average grain size of ~100 nm, can withstand Fe ion irradiation at 500 °C to 80 displacements-per-atom (dpa) with moderate grain coarsening. Compared to coarse grained (CG) counterparts, swelling resistance of UFG SS is improved by nearly an order of magnitude and swelling rate is reduced by a factor of 5. M(23)C(6) precipitates, abundant in irradiated CG SS, are largely absent in UFG SS. This study provides a nanoengineering approach to design and discover radiation tolerant metallic materials for applications in extreme radiation environments.

  16. Some aspects of thermomechanical fatigue of AISI 304L stainless steel: Part I. creep- fatigue damage

    Science.gov (United States)

    Zauter, R.; Christ, H. J.; Mughrabi, H.

    1994-02-01

    Thermomechanical fatigue (TMF) tests on the austenitic stainless steel AISI 304L have been conducted under “true≓ plastic-strain control in vacuum. This report considers the damage oc-curring during TMF loading. It is shown how the temperature interval and the phasing (in-phase, out-of-phase) determine the mechanical response and the lifetime of the specimens. If creep-fatigue interaction takes place during in-phase cycling, the damage occurs inside the ma-terial, leading to intergranular cracks which reduce the lifetime considerably. Out-of-phase cy-cling inhibits creep-induced damage, and no lifetime reduction occurs, even if the material is exposed periodically to temperatures in the creep regime. A formula is proposed which allows prediction of the failure mode, depending on whether creep-fatigue damage occurs or not. At a given strain rate, the formula is able to estimate the temperature of transition between pure fatigue and creep-fatigue damage.

  17. Effect of surface grinding on chloride induced SCC of 304L

    Energy Technology Data Exchange (ETDEWEB)

    Zhou, Nian, E-mail: nzh@du.se [Department of Material Science, Dalarna University, SE-79188 Falun (Sweden); KTH, SE-10044 Stockholm (Sweden); Pettersson, Rachel [KTH, SE-10044 Stockholm (Sweden); Jernkontoret, SE-11187 Stockholm (Sweden); Lin Peng, Ru [Department of Management and Engineering, Linköping University, SE-58183 Linköping (Sweden); Schönning, Mikael [Corrosion Department, Avesta Research Centre – Outokumpu Stainless AB, SE-774 22 Avesta (Sweden)

    2016-03-21

    The effect of surface grinding on the stress corrosion cracking (SCC) behavior of 304L austenitic stainless steel in boiling magnesium chloride has been investigated. SCC tests were conducted both without external loading and with varied levels of four-point bend loading for as-delivered material and for specimens which had been ground parallel or perpendicular to the loading direction. Residual stresses due to the grinding operation were measured using the X-ray diffraction technique. In addition, surface stress measurements under applied load were performed before exposure to evaluate the deviation between actual applied loading and calculated values according to ASTM G39. Micro-cracks initiated by a high level of tensile residual stress in the surface layer were observed for all the ground specimens but not those in the as-delivered condition. Grinding along the loading direction increased the susceptibility to chloride induced SCC; while grinding perpendicular to the loading direction improved SCC resistance. Surface tensile residual stresses were largely relieved after the initiation of cracks.

  18. Analysis of martensitic transformation and residual tension in an 304L stainless steel

    International Nuclear Information System (INIS)

    Alves, Juciane Maria

    2014-01-01

    The relationship between plastic deformation and the strain induced phase transformation, that provides a practical route to the development of new engineering materials with excellent mechanical properties, characterize the TRIP effect 'Transformation Induced Plasticity'. Among the stainless steels, the metastable 304 L austenitic steel is susceptible to transformation of austenite-martensite phase from tensile tests at room temperature by increments of plastic deformation. It is of great technological and scientific interest the knowledge of the evolution of phase transformation and residual stress from different levels and rates of plastic deformation imposed to the material. It is also important to evaluate the interference of metallographic preparation in quantitative analyzes of this steel. The main techniques used in this study consisted of X-rays diffraction and Ferritoscopy for the quantitation phase, and XRD to residual stress analysis also. As observed, the phase transformation quantification has not suffered significant influence of the metallographic preparation and evolved from increments of plastic deformation due to different stop charges and strain rates, leading to a further strengthening of the austenite matrix. The evaluation of residual stress resulting from the martensitic transformation was susceptible to the metallographic preparation and increased its value on comparison to sample without metallographic preparation. It was also observed that the residual stress decreased with the increase of the fraction of transformed martensite. (author)

  19. High temperature oxidation behavior of AISI 304L stainless steel—Effect of surface working operations

    International Nuclear Information System (INIS)

    Ghosh, Swati; Kumar, M. Kiran; Kain, Vivekanand

    2013-01-01

    Highlights: ► Surface working resulted in thinner oxide on the surface. ► Oxides on machined/ground surfaces richer in Cr, higher in specific resistivity. ► Additional ionic transport process at the metal-oxide for ground sample established. ► Presence of fragmented grains and martensite influenced oxide nature/morphology. - Abstract: The oxidation behavior of grade 304L stainless steel (SS) subjected to different surface finishing (machining and grinding) operations was followed in situ by contact electric resistance (CER) and electrochemical impedance spectroscopy (EIS) measurements using controlled distance electrochemistry (CDE) technique in high purity water (conductivity −1 ) at 300 °C and 10 MPa in an autoclave connected to a recirculation loop system. The results highlight the distinct differences in the oxidation behavior of surface worked material as compared to solution annealed material in terms of specific resistivity and low frequency Warburg impedance. The resultant oxide layer was characterized for (a) elemental analyses by glow discharge optical emission spectroscopy (GDOES) and (b) morphology by scanning electron microscopy (SEM). Oxide layers with higher specific resistivity and chromium content were formed in case of machined and ground conditions. Presence of an additional ionic transport process has also been identified for the ground condition at the metal/oxide interface. These differences in electrochemical properties and distinct morphological features of the oxide layer as a result of surface working were attributed to the prevalence of heavily fragmented grain structure and presence of martensite.

  20. Solid state crack repair by friction stir processing in 304L stainless steel

    Institute of Scientific and Technical Information of China (English)

    C.Gunter; M.P.Miles; F.C.Liu; T.W Nelson

    2018-01-01

    Friction stir processing (FSP) was investigated as a method of repairing cracks in 12mm thick 304L stainless steel plate.Healing feasibility was demonstrated by processing a tapered crack using a PCBN/WRe tool with a 25 mm diameter shoulder and a pin length of 6.4 mm.The experiment showed that it was possible to heal a crack that begins narrow and then progressively grows up to a width of 2 mm.Bead on plate experiments were used to find the best parameters for creating a consolidated stir zone with the least amount of hardness difference compared to the base metal.Grain refinement in some specimens resulted in much higher stir zone hardness,compared to base metal.A plot of grain size versus microhardness showed a very strong inverse correlation between grain size and hardness,as expected from the HallPetch relationship.Corrosion testing was carried out in order to evaluate the effect of FSP on potential sensitization of the stir zone.After 1000h of intermittent immersion in 3.5% saline solution at room temperature it was found that no corrosion products formed on the base material controls or on any of the friction stir processed specimens.

  1. Deformation and failure response of 304L stainless steel SMAW joint under dynamic shear loading

    International Nuclear Information System (INIS)

    Lee, Woei-Shyan; Cheng, J.-I.; Lin, C.-F.

    2004-01-01

    The dynamic shear deformation behavior and fracture characteristics of 304L stainless steel shielded metal arc welding (SMAW) joint are studied experimentally with regard to the relations between mechanical properties and strain rate. Thin-wall tubular specimens are deformed at room temperature under strain rates in the range of 8 x 10 2 to 2.8 x 10 3 s -1 using a torsional split-Hopkinson bar. The results indicate that the strain rate has a significant influence on the mechanical properties and fracture response of the tested SMAW joints. It is found that the flow stress, total shear strain to failure, work hardening rate and strain rate sensitivity all increase with increasing strain rate, but that the activation volume decreases. The observed dynamic shear deformation behavior is modeled using the Kobayashi-Dodd constitutive law, and it is shown that the predicted results are in good agreement with the experimental data. Fractographic analysis using scanning electron microscopy reveals that the tested specimens all fracture within their fusion zones, and that the primary failure mechanism is one of the extensive localized shearing. The fracture surfaces are characterized by the presence of many dimples. A higher strain rate tends to reduce the size of the dimples and to increase their density. The observed fracture features are closely related to the preceding flow behavior

  2. Investigation of high temperature corrosion behavior on 304L austenite stainless steel in corrosive environments

    Energy Technology Data Exchange (ETDEWEB)

    Sahri, M. I.; Othman, N. K.; Samsu, Z.; Daud, A. R. [School of Applied Physics, Faculty of Science and Technology, Universiti Kebangsaan Malaysia, 43600 UKM Bangi Selangor (Malaysia)

    2014-09-03

    In this work, 304L stainless steel samples were exposed at 700 °C for 10hrs in different corrosive environments; dry oxygen, molten salt, and molten salt + dry oxygen. The corrosion behavior of samples was analyzed using weight change measurement technique, optical microscope (OM) and Scanning Electron Microscope (SEM) equipped with Energy Dispersive X-ray (EDX). The existence phases of corroded sample were determined using X-ray Diffraction (XRD). The lowest corrosion rate was recorded in dry oxygen while the highest was in molten salt + dry oxygen environments with the value of 0.0062 mg/cm{sup 2} and −13.5225 mg/cm{sup 2} respectively. The surface morphology of sample in presence of salt mixture showed scale spallation. Oxide scales of Fe{sub 3}O{sub 4}, Fe{sub 2}O{sub 3} were the main phases developed and detected by XRD technique. Cr{sub 2}O{sub 3} was not developed in every sample as protective layers but chromate-rich oxide was developed. The cross-section analysis found the oxide scales were in porous, thick and non-adherent that would not an effective barrier to prevent from further degradation of alloy. EDX analysis also showed the Cr-element was low compared to Fe-element at the oxide scale region.

  3. Effect of martensitic transformation on springback behavior of 304L austenitic stainless steel

    Science.gov (United States)

    Fathi, H.; Mohammadian Semnani, H. R.; Emadoddin, E.; Sadeghi, B. Mohammad

    2017-09-01

    The present paper studies the effect of martensitic transformation on the springback behavior of 304L austenitic stainless steel. Martensite volume fraction was determined at the bent portion under various strain rates after bending test. Martensitic transformation has a significant effect on the springback behavior of this material. The findings of this study indicated that the amount of springback was reduced under a situation of low strain rate, while a higher amount of springback was obtained with a higher strain rate. The reason for this phenomenon is that higher work hardening occurs during the forming process with the low strain rate due to the higher martensite volume fraction, therefore the formability of the sheet is enhanced and it leads to a decreased amount of springback after the bending test. Dependency of the springback on the martensite volume fraction and strain rate was expressed as formulas from the results of the experimental tests and simulation method. Bending tests were simulated using LS-DYNA software and utilizing MAT_TRIP to determine the martensite volume fraction and strain under various strain rates. Experimental result reveals good agreement with the simulation method.

  4. Biaxial fatigue tests and crack paths for AISI 304L stainless steel

    Directory of Open Access Journals (Sweden)

    V. Chaves

    2014-10-01

    Full Text Available AISI 304L stainless steel specimens have been tested in fatigue. The tests were axial, torsional and in-phase biaxial, all of them under load control and R=-1. The S-N curves were built following the ASTM E739 standard and the method of maximum likelihood proposed by Bettinelli. The fatigue limits of the biaxial tests were represented in axes σ-τ. The elliptical quadrant, appropriate for ductile materials, and the elliptical arc, appropriate for fragile materials, were included in the graph. The experimental values were better fitted with an elliptical quadrant, despite the ratio between the pure torsion and tension fatigue limits, τFL/σFL, is 0.91, close to 1, which is a typical value for fragile materials. The crack direction along the surface has been analyzed by using a microscope, with especial attention to the crack initiation zones. The crack direction during the Stage I has been compared with theoretical models.

  5. Propagation of crevices in stainless steel AISI304L in conditions of hydrogen chemistry (HWC)

    International Nuclear Information System (INIS)

    Diaz S, A.; Fuentes C, P.; Merino C, F.; Castano M, V.

    2006-01-01

    Crevice growth velocities in samples of AISI 304L stainless steel thermally welded and sensitized were obtained by the Rising displacement method or of growing displacement. It was used a recirculation circuit in where the operation conditions of a BWR type reactor were simulated (temperature of 288 C and a pressure of 8 MPa) with the chemistry modified by the addition of hydrogen with and without the addition of impurities of a powerful oxidizer like the Cu ++ ion. CT pre cracked specimens were used and each rehearsal stayed to one constant displacement velocity of 1 x 10 -9 m/s (3.6 μm/hr), making a continuous pursuit of the advance of the crack by the electric potential drop technique. To the end of the rehearsal it was carried out the fractographic analysis of the propagation surfaces. The values of the growth velocities obtained by this methodology went similar to the opposing ones under normal conditions of operation; while the fractographic analysis show the cracks propagation in trans and intergranular ways, evidencing the complexity of the regulator mechanisms of the one IGSCC even under controlled ambient conditions or with mitigation methodologies like the alternative hydrogen chemistry. (Author)

  6. Crack propagation in stainless steel AISI 304L in Hydrogen Chemistry conditions (HWC)

    International Nuclear Information System (INIS)

    Diaz S, A.; Fuentes C, P.; Merino C, F.; Castano M, V.

    2006-01-01

    Velocities of crack growth in samples type CT pre cracking of stainless steel AISI 304l solder and sensitized thermally its were obtained by the Rising Displacement method or of growing displacement. It was used a recirculation circuit that simulates the operation conditions of a BWR type reactor (temperature of 280 C and a pressure of 8 MPa) with the chemistry modified by the addition of hydrogen with and without the addition of impurities of a powerful oxidizer like the Cu + ion. In each essay stayed a displacement velocity was constant of 1x10 -9 m/s, making a continuous pursuit of the advance of the crack by the electric potential drop technique. Contrary to the idea of mitigation of the crack propagation velocity by effect of the addition of the hydrogen in the system, the values of the growth velocities obtained by this methodology went similar to the opposing ones under normal operation conditions. To the finish of the rehearsal one carries out the fractographic analysis of the propagation surfaces, which showed cracks growth in trans and intergranular way, evidencing the complexity of the regulator mechanisms of the IGSCC like in mitigation conditions as the alternative Hydrogen Chemistry. (Author)

  7. Dislocation structure evolution in 304L stainless steel and weld joint during cyclic plastic deformation

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Hao; Jing, Hongyang; Zhao, Lei; Han, Yongdian; Lv, Xiaoqing [School of Materials Science and Engineering, Tianjin University, Tianjin 300072 (China); Tianjin Key Laboratory of Advanced Joining Technology, Tianjin 300072 (China); Xu, Lianyong, E-mail: xulianyong@tju.edu.cn [School of Materials Science and Engineering, Tianjin University, Tianjin 300072 (China); Tianjin Key Laboratory of Advanced Joining Technology, Tianjin 300072 (China)

    2017-04-06

    Dislocation structures and their evolution of 304L stainless steel and weld metal made with ER308L stainless steel welding wire subjected to uniaxial symmetric strain-controlled loading and stress-controlled ratcheting loading were observed by transmission electron microscopy (TEM). The correlation between the cyclic response and the dislocation structure has been studied. The experiment results show that the cyclic behaviour of base metal and weld metal are different. The cyclic behaviour of the base metal consists of primary hardening, slight softening and secondary hardening, while the weld metal shows a short hardening within several cycles followed by the cyclic softening behaviour. The microscopic observations indicate that in base metal, the dislocation structures evolve from low density patterns to those with higher dislocation density during both strain cycling and ratcheting deformation. However, the dislocation structures of weld metal change oppositely form initial complicated structures to simple patterns and the dislocation density gradually decrease. The dislocation evolution presented during the strain cycling and ratcheting deformation is summarized, which can qualitatively explain the cyclic behaviour and the uniaxial ratcheting behaviour of two materials. Moreover, the dislocation evolution in the two types of tests is compared, which shows that the mean stress has an effect on the rate of dislocation evolution during the cyclic loading.

  8. Effect of surface grinding on chloride induced SCC of 304L

    International Nuclear Information System (INIS)

    Zhou, Nian; Pettersson, Rachel; Lin Peng, Ru; Schönning, Mikael

    2016-01-01

    The effect of surface grinding on the stress corrosion cracking (SCC) behavior of 304L austenitic stainless steel in boiling magnesium chloride has been investigated. SCC tests were conducted both without external loading and with varied levels of four-point bend loading for as-delivered material and for specimens which had been ground parallel or perpendicular to the loading direction. Residual stresses due to the grinding operation were measured using the X-ray diffraction technique. In addition, surface stress measurements under applied load were performed before exposure to evaluate the deviation between actual applied loading and calculated values according to ASTM G39. Micro-cracks initiated by a high level of tensile residual stress in the surface layer were observed for all the ground specimens but not those in the as-delivered condition. Grinding along the loading direction increased the susceptibility to chloride induced SCC; while grinding perpendicular to the loading direction improved SCC resistance. Surface tensile residual stresses were largely relieved after the initiation of cracks.

  9. Establishing precursor events for stress corrosion cracking initiation in type 304L stainless steel

    International Nuclear Information System (INIS)

    Khan, M.U.F.; Raja, V.S.; Roychowdhury, S.; Kain, V.

    2015-01-01

    The present study attempts to establish slip band emergence, due to localized deformation, as a precursor event for SCC initiation in type 304L SS. The unidirectional tensile loading was used for straining flat tensile specimen, less than 10% strain, in air, 0.5 M NaCl + 0.5 M H 2 SO 4 and boiling water reactor (BWR) simulated environment (288 C. degrees, 10 MPa). The surface features were characterized using optical microscopy, scanning electron microscopy (including electron backscattered diffraction-EBSD) and atomic force microscopy. The study shows that with increase in strain level, during unidirectional slow strain rate test (SSRT), average slip band height increases in air and the attack on slip lines occurs in acidified chloride environment. In BWR simulated environment, preferential oxidation on slip lines and initiation of a few cracks on some of the slip lines are observed. Based on the observation, the study suggests slip bands, formed due to localized deformation, to act as a precursor for SCC initiation. (authors)

  10. Microstructure and mechanical properties of friction welded AISI 1040/AISI 304L steels before and after electrochemical corrosion

    Energy Technology Data Exchange (ETDEWEB)

    Sarsilmaz, Furkan [Firat Univ., Elazig (Turkey). Dept. of Mechatronics Engineering; Kirik, Ihsan [Batman Univ. (Turkey); Ozdemir, Niyazi [Firat Univ., Elazig (Turkey)

    2018-03-01

    The aim of the present study is to investigate the effect of welding parameters both on the electrochemical corrosion behavior and tensile strength of pre- and post-electrochemical corrosion of friction welded dissimilar steels. The microstructural changes of AISI 1040/AISI 304L friction welded couples and also parent materials were analyzed by using scanning electron microscopy. The electrochemical behaviors of AISI1040/AISI304L joints were comparatively investigated by potentiodynamic polarization curve test and by electrochemical impedance spectra. Moreover, tensile strength experiments were carried out determining the behavior of friction welded joints of pre- and post-electrochemical corrosion and results indicated that the maximum tensile test value of the dissimilar welded pre-electrochemical corrosion was higher than those of post-electrochemical corrosion and was also very close to AISI 1040 parent material value.

  11. Multi-scale analysis of behavior and fatigue life of 304L stainless under cyclic loading with pre-hardening

    International Nuclear Information System (INIS)

    Belattar, A.

    2013-01-01

    This study investigates the effects of loading history on the cyclic stress-strain curve and fatigue behavior of 304L stainless steel at room temperature. Tension-compression tests were performed on the same specimen under controlled strain, using several loading sequences of increasing or decreasing amplitude. The results showed that fatigue life is significantly reduced by the previous loading history. A previously developed method for determining the effect of prehardening was evaluated. Microstructural analyses were also performed; the microstructures after pre-loading and their evolution during the fatigue cycles were characterized by TEM. The results of these analyses improve our understanding of the macroscopic properties of 304L stainless steel and can help us identify the causes of failure and lifetime reduction. (author)

  12. L2 Milestone 5433: Characterization of Dynamic Behavior of AM and Conventionally Processed Stainless Steel (316L and 304L)

    Energy Technology Data Exchange (ETDEWEB)

    Gray, George Thompson [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Livescu, Veronica [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Rigg, P. A. [Washington State Univ., Pullman, WA (United States). Inst. for Shock Physics; Trujillo, Carl Patrick [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Cady, Carl McElhinney [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Chen, Shuh-Rong [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Carpenter, John S. [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Lienert, Thomas J. [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Fensin, Saryu Jindal [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Knapp, Cameron M. [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Beal, Roberta Ann [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Morrow, Benjamin [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Dippo, Olivia F. [Univ. of California, San Diego, CA (United States); Jones, David Robert [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Martinez, Daniel Tito [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Valdez, James Anthony [Los Alamos National Lab. (LANL), Los Alamos, NM (United States)

    2016-09-26

    For additive manufacturing (AM) of metallic materials, the certification and qualification paradigm needs to evolve as there currently exists no broadly accepted “ASTM- or DIN-type” additive manufacturing certified process or AM-material produced specifications. Accordingly, design, manufacture, and thereafter implementation and insertion of AM materials to meet engineering applications requires detailed quantification of the constitutive (strength and damage) properties of these evolving materials, across the spectrum of metallic AM methods, in comparison/contrast to conventionally-manufactured metals and alloys. This report summarizes the 316L SS research results and presents initial results of the follow-on study of 304L SS. For the AM-316L SS investigation, cylindrical samples of 316L SS were produced using a LENS MR-7 laser additive manufacturing system from Optomec (Albuquerque, NM) equipped with a 1kW Yb-fiber laser. The microstructure of the AM-316L SS was characterized in both the “as-built” Additively Manufactured state and following a heat-treatment designed to obtain full recrystallization to facilitate comparison with annealed wrought 316L SS. The dynamic shock-loading-induced damage evolution and failure response of all three 316L SS materials was quantified using flyer-plate impact driven spallation experiments at peak stresses of 4.5 and 6.35 GPa. The results of these studies are reported in detail in the first section of the report. Publication of the 316L SS results in an archival journal is planned. Following on from the 316L SS completed work, initial results on a study of AM 304L SS are in progress and presented herein. Preliminary results on the structure/dynamic spallation property behavior of AM-304L SS fabricated using both the directed-energy LENS and an EOS powder-bed AM techniques in comparison to wrought 304L SS is detailed in this Level 2 Milestone report.

  13. STUDY AND ANALYSIS OF THE EFFECT OF WELDING PROCESS ON DISTORTION WITH 304L STAINLESS STEEL WELD JOINTS

    OpenAIRE

    Dhananjay Kumar*, Dharamvir mangal

    2017-01-01

    The effect of welding process on the distortion with 304L stainless steel 12thk weld joints made by TIG (tungsten inert gas) and SMAW (Shielded metal arc welding) welding process involving different type joint configuration have been studied. The joint configurations employed were double V-groove edge preparation for double side SMAW welding and square – butt preparation for double side TIG welding. All weld joints passed by radiographic. Distortion measurements were carried out using height ...

  14. Cladding of aluminum on AISI 304L stainless steel by cold roll bonding: Mechanism, microstructure, and mechanical properties

    Energy Technology Data Exchange (ETDEWEB)

    Akramifard, H.R., E-mail: akrami.1367@ut.ac.ir [School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, P.O. Box 11155-4563, Tehran (Iran, Islamic Republic of); Mirzadeh, H., E-mail: hmirzadeh@ut.ac.ir [School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, P.O. Box 11155-4563, Tehran (Iran, Islamic Republic of); Advanced Metalforming and Thermomechanical Processing Laboratory, School of Metallurgy and Materials Engineering, University of Tehran, Tehran (Iran, Islamic Republic of); Parsa, M.H., E-mail: mhparsa@ut.ac.ir [School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, P.O. Box 11155-4563, Tehran (Iran, Islamic Republic of); Center of Excellence for High Performance Materials, School of Metallurgy and Materials Engineering, University of Tehran, Tehran (Iran, Islamic Republic of); Advanced Metalforming and Thermomechanical Processing Laboratory, School of Metallurgy and Materials Engineering, University of Tehran, Tehran (Iran, Islamic Republic of)

    2014-09-08

    The AA1050 aluminum alloy and AISI 304L stainless steel sheets were stacked together to fabricate Al/304L/Al clad sheet composites by the cold roll bonding process, which was performed at temperatures of ∼100 and 23 °C to produce austenitic and austenitic–martensitic microstructures in the AISI 304L counterpart, respectively. The peel test results showed that the threshold reduction required to make a suitable bond at room temperature is below 10%, which is significantly lower than the required reduction for cold roll bonding of Al sheets. The tearing of the Al sheet during the peel test signified that the bond strength of the roll bonded sheets by only 38% reduction has reached the strength of Al, which is a key advantage of the developed sheets. The extrusion of Al through the surface cracks and settling inside the 304L surface valleys due to strong affinity between Al and Fe was found to be the bonding mechanism. Subsequently, the interface and tensile behaviors of three-layered clad sheets after soaking at 200–600 °C for 1 h were investigated to characterize the effect of annealing treatment on the formation and thickening of intermetallic compound layer and the resultant mechanical properties. Field emission scanning electron microscopy, X-ray diffraction, and optical microscopy techniques revealed that an intermediate layer composed mainly of Al{sub 13}Fe{sub 4}, FeC and Al{sub 8}SiC{sub 7} forms during annealing at 500–600 °C. A significant drop in tensile stress–strain curves after the maximum point (UTS) was correlated to the interface debonding. It was found that the formation of intermediate layer by post heat treatment deteriorates the bond quality and encourages the debonding process. Moreover, the existence of strain-induced martensite in clad sheets was found to play a key role in the enhancement of tensile strength.

  15. Experimental investigation of Ti–6Al–4V titanium alloy and 304L stainless steel friction welded with copper interlayer

    Directory of Open Access Journals (Sweden)

    R. Kumar

    2015-03-01

    Full Text Available The basic principle of friction welding is intermetallic bonding at the stage of super plasticity attained with self-generating heat due to friction and finishing at upset pressure. Now the dissimilar metal joints are especially popular in defense, aerospace, automobile, bio-medical, refinery and nuclear engineerings. In friction welding, some special alloys with dual phase are not joined successfully due to poor bonding strength. The alloy surfaces after bonding also have metallurgical changes in the line of interfacing. The reported research work in this area is scanty. Although the sound weld zone of direct bonding between Ti–6Al–4V and SS304L was obtained though many trials, the joint was not successful. In this paper, the friction welding characteristics between Ti–6Al–4V and SS304L into which pure oxygen free copper (OFC was introduced as interlayer were investigated. Box–Behnken design was used to minimize the number of experiments to be performed. The weld joint was analyzed for its mechanical strength. The highest tensile strength between Ti–6Al–4V and SS304L between which pure copper was used as insert metal was acquired. Micro-structural analysis and elemental analysis were carried out by EDS, and the formation of intermetallic compound at the interface was identified by XRD analysis.

  16. Notch Effect on Tensile Deformation Behavior of 304L and 316L Steels in Liquid Helium and Hydrogen

    International Nuclear Information System (INIS)

    Shibata, K.; Fujii, H.

    2004-01-01

    Tensile tests of type 304L and 316L steels were carried out using round bar specimens with a notch in liquid helium, hydrogen, liquid nitrogen and at ambient temperature. The obtained tensile strengths were compared with the tensile strengths of smooth specimens. For smooth specimens, tensile strength increased with a decrease in temperature and the strengths in liquid helium and hydrogen show similar values in both steels. For notched specimen of 304L steel, tensile strength (including fracture strength) increased noticeably from ambient to liquid nitrogen temperature but showed a large decrease in liquid helium and hydrogen. In liquid hydrogen and helium, the tensile strength is a little lower in liquid hydrogen than in liquid helium and both strengths are lower than tensile strengths of smooth specimens. For notched specimen of 316L steel, an increase in tensile strength from ambient to liquid nitrogen temperature was not so large and a decrease from liquid nitrogen to liquid hydrogen was small. The tensile strengths in liquid helium and hydrogen were nearly same and higher than those of smooth specimens. Different behavior of serration was observed between liquid helium and hydrogen, and between 304L and 316L steels. The reasons for these differences were discussed using computer simulation

  17. Effect of sensitization on the mechanical properties of type 304 L stainless steel

    International Nuclear Information System (INIS)

    Vargas Mendoza, L.F.

    1990-01-01

    The sensitization is a corrosion cause that it has studied broadly in the austenitic steels; however its relations don't knowed very well, into the sensitization and the steel's mechanical properties. Wherefore, the objectives of this work was to study the mechanical properties, in tension of austenitic steel with different levels of sensitization. The material utilized was a 304 L steel of standard composition AISI. The samples were sensitized at 450, 650 and 850 Centigrade degree, by short expositions, following by a temper in water. After this treatment, the tension test tubes were carried to rupture at low deformation velocity. The sensitization was evaluated by the method of Akashi EPR cyclic polarization. The sensitization distribution was analyzed by optical metallography in color and the fracture surface were studied by sweeping electronic microscopy. The distribution and length of the carbides were the factor that control the mechanic behavior of materials. At 450 Centigrade, the border of the grain its founded free of carbides, also for the longest times of exposition, but the particles are presented as fine precipitates in the grain interior, with this is increased the mechanical properties by the internal interactions of hardness or oldness types. At 650 Centigrade the frontiers show a dense distribution of fine carbides. These precipitates are interacting with the borders grain, increasing lightly the mechanical properties of steel. At 850 Centigrade, were formed discontinued carbides that not affect the mechanical behavior, but whether the fracture; the resistance is reduced and the ductility is increased although to impose the thermic effect of treatment. (Author)

  18. Corrosion study of stainless steel SS304L in molten molybdates

    Energy Technology Data Exchange (ETDEWEB)

    Usami, T., E-mail: tusami@criepi.denken.or.jp [Central Research Institute of Electric Power Industry, Iwadokita2-11-1, Komae-shi, Tokyo 201-8511 (Japan); Uruga, K.; Tsukada, T. [Central Research Institute of Electric Power Industry, Iwadokita2-11-1, Komae-shi, Tokyo 201-8511 (Japan); Miura, Y.; Komamine, S.; Ochi, E. [Japan Nuclear Fuel Limited, 4-108, Aza Okitsuke, Oaza Obuchi, Rokkasho-mura, Kamikita-gun, Aomori 039-3212 (Japan)

    2016-04-01

    Depending on operating conditions of the vitrification process of high-level liquid waste, molten salt mainly composed of sodium and molybdenum can be generated, and poured into stainless steel canisters. In this work, the possible reaction between the molten molybdate and stainless steel was investigated using multi-component molybdate and simple Na{sub 2}MoO{sub 4} – MoO{sub 3} molybdate. In the experiments using multi-component molybdates, no significant reaction is observed between the mixed molybdates and the stainless steel specimens at 700 °C in 4 h. The reaction rate of the stainless steel with the multi-component molybdate increases in proportion to exp(-1/T). The depth of the most reacted area is about 300 μm even at 1000 °C, and was much smaller than the 6 mm thickness of the canister. In the simple Na{sub 2}MoO{sub 4} – MoO{sub 3} molybdate, the reaction rate was proportional to the MoO{sub 3} concentration. The essence of the reaction is oxidation of metals by Mo{sup 6+} - > Mo{sup 4+}. Part of the reaction product mainly composed of Fe is dissolved into the molybdate, while the other part mainly composed of Cr sloughs and forms a banded layer. - Highlights: • The reaction yield of SS304L with molten molybdate was negligible at 700 °C in 4 h. • The corrosion rate increased in proportion to exp (-1/T). • The corrosion rate was proportional to MoO{sub 3} concentration in Na{sub 2}MoO{sub 4}–MoO{sub 3} mixture. • The essence of the reaction was oxidation of metals by Mo{sup 6+} –> Mo{sup 4+}.

  19. Comparative study of the microbiological corrosion among an AISI 304L and an API X65; Estudio comparativo de la corrosion microbiologica entre un AISI 304L y un API X65

    Energy Technology Data Exchange (ETDEWEB)

    Diaz S, A.; Arganis J, C.; Luna C, P.; Carapia M, L. [ININ, 52045 Ocoyoacac, Estado de Mexico (Mexico); Gonzalez F, E. [ITT, Toluca, Estado de Mexico (Mexico)

    2004-07-01

    Metallic samples of AISI 304L sensitized and API X65, were subjected to the action of an inoculated media with reductive sulphate microorganisms (SBR), carrying out electrochemical evaluations by means of the techniques of Polarization Resistance (RP), Tafel extrapolation (ET) and Electrochemical Noise (RE). The generated information was complemented with the analysis and diagnostic of the present damage in the surfaces exposed in both metals. The used electrochemical techniques allow to determine the corrosion velocities associated to each system, establishing that the uniform corrosion is not affected by the effect of the microorganisms; however, electrochemical noise, evidenced the formation of stings associated to the presence of bacteria. (Author)

  20. Corrosion behavior of mild steel and SS 304L in presence of dissolved nickel under aerated and deaerated conditions

    Directory of Open Access Journals (Sweden)

    Mohd Mobin

    2011-12-01

    Full Text Available In dual purpose water/power co-generation plants, the presence of high concentration of Cu and Ni in the re-circulating brine/condensate as a result of condenser tubes corrosion has been attributed as one of the several causes of corrosion damage of flash chamber materials and water touched parts of the boilers. The present investigation deals with the effect of dissolved nickel in the concentration range of 10 ppb to 100 ppm on the corrosion behavior of mild steel and SS 304L in two aqueous medium namely, distilled water and artificial seawater. The effect of pH, dissolved oxygen and flow condition of aqueous medium on the corrosion behavior was also monitored. The experimental techniques include immersion test and electrochemical tests which include free corrosion potential measurements and potentiodynamic polarization measurements. The corrosion rate of mild steel and SS 304L under different experimental conditions was determined by weight loss method and spectrophotometric determination of iron ion entered into the test solution during the period of immersion. The pH of the test solution was also monitored during the entire period of immersion. The left over nickel ions present in the test solution after completion of immersion was also estimated using Atomic Absorption Spectrophotometer. The surface morphology of the corroded steel surface was also examined using scanning electron microscopy (SEM. The results of the studies show that SS 304L largely remains unaffected in both distilled water and artificial seawater under different experimental conditions. However, the effect of nickel on the corrosion behavior of mild steel is quite pronounced and follows interesting trends.

  1. The effect of electrode vertex angle on automatic tungsten-inert-gas welds for stainless steel 304L plates

    International Nuclear Information System (INIS)

    Maarek, V.; Sharir, Y.; Stern, A.

    1980-03-01

    The effect of electrode vertex angle on penetration depth and weld bead width, in automatic tungsten-inert-gas (TIG) dcsp bead-on-plate welding with different currents, has been studied for stainless steel 304L plates 1.5 mm and 8 mm thick. It has been found that for thin plates, wider and deeper welds are obtained when using sharper electrodes while, for thick plates, narrower and deeper welds are produced when blunt electrodes (vertex angle 180 deg) are used. An explanation of the results, based on a literature survey, is included

  2. Improvement of pitting corrosion resistance of AISI 304L stainless steel by nano-pulsed laser surface melting

    International Nuclear Information System (INIS)

    Pacquentin, W.; Blanc, C.; Caron, N.; Thro, P.Y.; Cheniere, A.; Tabarant, M.; Moutiers, G.; Miserque, F.; Plouzennec, H.; Oltra, R.

    2013-01-01

    The stainless steel 304L is widely used, however, in particular conditions, it may be sensitive to pitting corrosion. Nano-pulsed laser surface melting is a surface treatment which allows improving the corrosion resistance of this steel. This treatment consists in focusing a laser beam on the surface of the material, involving its quite immediately melting through a few microns depth, then an ultra-fast solidification occurs with cooling rate about 1011 K/s. The laser parameters control the modifications of the physico-chemical properties. In particular, we studied the influence of the impacts overlap of an ytterbium laser-fiber on the corrosion resistance of a 304L stainless steel in conditions of an aerated and agitated solution of NaCl (concentration of 30 g/L). We obtained an increase of the pitting potential of 220 mV, highlighting an improvement of the corrosion resistance. The study of the chemical and structural modifications is not enough to explain the improvement of the corrosion resistance. Other phenomena must be taken into account, as the quality of the oxide layer, in terms of physico-chemical and mechanical properties. (authors)

  3. Corrosion of high Ni-Cr alloys and Type 304L stainless steel in HNO3-HF

    International Nuclear Information System (INIS)

    Ondrejcin, R.S.; McLaughlin, B.D.

    1980-04-01

    Nineteen alloys were evaluated as possible materials of construction for steam heating coils, the dissolver vessel, and the off-gas system of proposed facilities to process thorium and uranium fuels. Commercially available alloys were found that are satisfactory for all applications. With thorium fuel, which requires HNO 3 -HF for dissolution, the best alloy for service at 130 0 C when complexing agents for fluoride are used is Inconel 690; with no complexing agents at 130 0 C, Inconel 671 is best. At 95 0 C, six other alloys tested would be adequate: Haynes 25, Ferralium, Inconel 625, Type 304L stainless steel, Incoloy 825, and Haynes 20 (in order of decreasing preference); based on composition, six untested alloys would also be adequate. The ions most effective in reducing fluoride corrosion were the complexing agents Zr 4+ and Th 4+ ; Al 3+ was less effective. With uranium fuel, modestly priced Type 304L stainless steel is adequate. Corrosion will be most severe in HNO 3 -HF used occasionally for flushing and in solutions of HNO 3 and corrosion products (ferric and dichromate ions). HF corrosion can be minimized by complexing the fluoride ion and by passivation of the steel with strong nitric acid. Corrosion caused by corrosion products can be minimized by operating at lower temperatures

  4. The application of an internal state variable model to the viscoplastic behavior of irradiated ASTM 304L stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    McAnulty, Michael J., E-mail: mcanulmj@id.doe.gov [Department of Energy, 1955 Fremont Avenue, Idaho Falls, ID 83402 (United States); Potirniche, Gabriel P. [Mechanical Engineering Department, University of Idaho, Moscow, ID 83844 (United States); Tokuhiro, Akira [Mechanical Engineering Department, University of Idaho, Idaho Falls, ID 83402 (United States)

    2012-09-15

    Highlights: Black-Right-Pointing-Pointer An internal state variable approach is used to predict the plastic behavior of irradiated metals. Black-Right-Pointing-Pointer The model predicts uniaxial tensile test data for irradiated 304L stainless steel. Black-Right-Pointing-Pointer The model is implemented as a user-defined material subroutine in the finite element code ABAQUS. Black-Right-Pointing-Pointer Results are compared for the unirradiated and irradiated specimens loaded in uniaxial tension. - Abstract: Neutron irradiation of metals results in decreased fracture toughness, decreased ductility, increased yield strength and increased ductile-to-brittle transition temperature. Designers use the most limiting material properties throughout the reactor vessel lifetime to determine acceptable safety margins. To reduce analysis conservatism, a new model is proposed based on an internal state variable approach for the plastic behavior of unirradiated ductile materials to support its use for analyzing irradiated materials. The proposed modeling addresses low temperature irradiation of 304L stainless steel, and predicts uniaxial tensile test data of irradiated experimental specimens. The model was implemented as a user-defined material subroutine (UMAT) in the finite element software ABAQUS. Results are compared between the unirradiated and irradiated specimens subjected to tension tests.

  5. Effect of SiC particle impact nano-texturing on tribological performance of 304L stainless steel

    Science.gov (United States)

    Lorenzo-Martin, C.; Ajayi, O. O.

    2014-10-01

    Topographical features on sliding contact surfaces are known to have a significant impact on friction and wear. Indeed, various forms of surface texturing are being used to improve and/or control the tribological performance of sliding surfaces. In this paper, the effect of random surface texturing produced by a mechanical impact process is studied for friction and wear behavior of 304L stainless steel (SS) under dry and marginal oil lubrication. The surface processing was applied to 304L SS flat specimens and tested under reciprocating ball-on-flat sliding contact, with a 440C stainless steel ball. Under dry contact, the impact textured surface exhibited two order of magnitude lower wear than the isotropically ground surface of the same material. After 1500 s of sliding and wearing through of the processed surface layer following occurring of scuffing, the impact textured surface underwent a transition in wear and friction behavior. Under marginal oil lubrication, however, no such transition occurred, and the wear for the impact textured surface was consistently two orders of magnitude lower than that for the ground material. Mechanisms for the tribological performance enhancement are proposed.

  6. The role of martensitic transformation on bimodal grain structure in ultrafine grained AISI 304L stainless steel

    International Nuclear Information System (INIS)

    Sabooni, S.; Karimzadeh, F.; Enayati, M.H.; Ngan, A.H.W.

    2015-01-01

    In the present study, metastable AISI 304L austenitic stainless steel samples were subjected to different cold rolling reductions from 70% to 93%, followed by annealing at 700 °C for 300 min to form ultrafine grained (UFG) austenite with different grain structures. Transmission electron microscopy (TEM) and nanoindentation were used to characterize the martensitic transformation, in order to relate it to the bimodal distribution of the austenite grain size after subsequent annealing. The results showed that the martensite morphology changed from lath type in the 60% rolled sample to a mixture of lath and dislocation-cell types in the higher rolling reductions. Calculation of the Gibbs free energy change during the reversion treatment showed that the reversion mechanism is shear controlled at the annealing temperature and so the morphology of the reverted austenite is completely dependent on the morphology of the deformation induced martensite. It was found that the austenite had a bimodal grain size distribution in the 80% rolled and annealed state and this is related to the existence of different types of martensite. Increasing the rolling reduction to 93% followed by annealing caused changing of the grain structure to a monomodal like structure, which was mostly covered with small grains of around 300 nm. The existence of bimodal austenite grain size in the 80% rolled and annealed 304L stainless steel led to the improvement of ductility while maintaining a high tensile strength in comparison with the 93% rolled and annealed sample

  7. Tensile Stress-Strain Results for 304L and 316L Stainless-Steel Plate at Temperature

    International Nuclear Information System (INIS)

    R. K. Blandford; D. K. Morton; S. D. Snow; T. E. Rahl

    2007-01-01

    The Idaho National Laboratory (INL) is conducting moderate strain rate (10 to 200 per second) research on stainless steel materials in support of the Department of Energy's (DOE) National Spent Nuclear Fuel Program (NSNFP). For this research, strain rate effects are characterized by comparison to quasi-static tensile test results. Considerable tensile testing has been conducted resulting in the generation of a large amount of basic material data expressed as engineering and true stress-strain curves. The purpose of this paper is to present the results of quasi-static tensile testing of 304/304L and 316/316L stainless steels in order to add to the existing data pool for these materials and make the data more readily available to other researchers, engineers, and interested parties. Standard tensile testing of round specimens in accordance with ASTM procedure A 370-03a were conducted on 304L and 316L stainless-steel plate materials at temperatures ranging from -20 F to 600 F. Two plate thicknesses, eight material heats, and both base and weld metal were tested. Material yield strength, Young's modulus, ultimate strength, ultimate strain, failure strength and failure strain were determined, engineering and true stress-strain curves to failure were developed, and comparisons to ASME Code minimums were made. The procedures used during testing and the typical results obtained are described in this paper

  8. Effect of welding process, type of electrode and electrode core diameter on the tensile property of 304L austenitic stainless steel

    Directory of Open Access Journals (Sweden)

    Akinlabi OYETUNJI

    2014-11-01

    Full Text Available The effect of welding process, type of electrode and electrode core diameter on the tensile property of AISI 304L Austenitic Stainless Steel (ASS was studied. The tensile strength property of ASS welded samples was evaluated. Prepared samples of the ASS were welded under these three various variables. Tensile test was then carried out on the welded samples. It was found that the reduction in ultimate tensile strength (UTS of the butt joint samples increases with increase in core diameter of the electrode. Also, the best electrode for welding 304L ASS is 308L stainless steel-core electrode of 3.2 mm core diameter. It is recommended that the findings of this work can be applied in the chemical, food and oil industries where 304L ASS are predominantly used.

  9. Zirconium oxide deposits (ZrO2) and titanium oxide (TiO2) on 304l stainless steel

    International Nuclear Information System (INIS)

    Davila N, M. L.

    2015-01-01

    This research project aims to carry out the surface and electrochemical characterization to obtain the optimum conditions of the hydrothermal deposits of zirconium oxide ZrO 2 (baddeleyite) and titanium oxide TiO 2 (anatase and rutile phases) on 304l stainless steel, simulating an inhibiting protective layer. 304l steel specimens were cut, pre-oxidized in water at a temperature of 288 degrees Celsius and 8 MPa, similar to those of a typical BWR conditions. From the titanium oxide anatase crystalline phase, the rutile phase was obtained by a heat treatment at 1000 degrees Celsius. The Sigma-Aldrich pre-oxidized powders and steel 304l were characterized using techniques of X-ray diffraction, scanning electron microscopy, X-ray dispersive energy, chemical mapping and Raman spectrometry. The pre-oxidized steel has two oxide layers, an inner layer with nano metric crystals and another outer of larger crystals to 1μm, with the formation of hematite and magnetite, this predominating. The surface that contacted the sample holder has larger crystals. Hydrothermal deposits were carry out from suspensions of 10, 100 and 1000 ppm, of the crystal phases of anatase, rutile and baddeleyite, on the pre-oxidized steel at a temperature of 150 degrees Celsius for 2 and 7 days, samples were analyzed by X-ray diffraction, scanning electron microscopy, X-ray dispersive energy, Raman spectrometry and Tafel polarization. The suspension to 1000 ppm for 7 days coated surface most; the baddeleyite deposit is noticed more homogeneous than anatase and rutile. The deposit is favored when hematite and magnetite crystals are larger. The chemical mapping on deposits show that even after being immersed in water to 288 degrees Celsius during 30 days, the deposits are still present although a loss is observed. A reference electrode was assembled to conduct electrochemical tests of Tafel able to withstand a temperature of 288 degrees Celsius and pressure of 8 MPa. The baddeleyite deposit presented

  10. Surface decontamination of Type 304L stainless steel with electrolytically generated hydrogen: Design and operation of the electrolyzer

    International Nuclear Information System (INIS)

    Bellanger, G.

    1993-01-01

    The surface of tritiated Type 304L stainless steel is decontaminated by isotopic exchange with the hydrogen generated in an electrolyzer. This steel had previously been exposed to tritium in a tritium gas facility for several years. The electrolyzer for the decontamination uses a conducting solid polymer electrolyte made of a Nafion membrane. The cathode where the hydrogen is formed is nickel deposited on one of the polymer surfaces. This cathode is placed next to the region of the steel to be decontaminated. The decontamination involves, essentially, the tritiated oxide layers of which the initial radioactivity is ∼ 5 kBq/cm 2 . After treatment for 1 h, the decontamination factor is 8. 9 refs., 16 figs., 2 tabs

  11. Relationship between oxide film structures and corrosion resistance of SUS 304 L stainless steel in high temperature pure water

    International Nuclear Information System (INIS)

    Yamanaka, Kazuo; Matsuda, Yasushi.

    1990-01-01

    The effect of various oxidation conditions on metal release of SUS304L stainless steels in deaerated pure water at 488 K was investigated. The behavior of metal release was also discussed in relation to the surface films which were formed by various oxidation treatments. The results obtained are as follows: (1) The oxidation treatment in high purity argon gas at high temperatures for short time such as 1273 K - 2 min (120S) was effective to decrease the metal dissolution, and the oxide films primarily consisted of spinel type double oxide layer containing high concentration of Mn and Cr. (2) The oxidation treatments in non-deaerated pure water at 561 K for 24∼336 h (86.4∼1209.6 ks) were furthermore effective to decrease the metal dissolution. (3) It may be concluded that the key factors controlling the metal release are thickness, structure and compactness together with compositions of surface oxide films. (author)

  12. In situ AFM study of pitting corrosion and corrosion under strain on a 304L stainless steel

    International Nuclear Information System (INIS)

    Martin, F.A.; Cousty, J.; Masson, J-L.; Bataillon, C.

    2004-01-01

    Our study is centred on surface localised corrosion under strain of a standard stainless steel (304L). The interest we take in these corrosion phenomena is led by the general misunderstanding of its primary initiation steps. The goal of this study is to determine precisely the relationships between local geometrical defects (grain boundaries, dislocation lines, etc) or chemical defects (inclusions) with the preferential sites of corrosion on the strained material. By combining three techniques at the same time: Atomic Force Microscopy, an electrochemical cell and a traction plate, we can observe in situ the effect of localised stress and deformation on the sample surface exposed to a corrosive solution. We managed to build an original set-up compatible with all the requirements of these three different techniques. Furthermore, we prepared the surface of our sample as flat as possible to decrease at maximum the topographical noise in order to observe the smallest defect on the surface. By using a colloidal suspension of SiO 2 , we obtained surfaces with a typical corrugation (RMS) of about 1 A for areas of at least 1 μm 2 . Our experimental study has been organised in two primary investigations: - In situ study of the morphology evolution of the surface under a corrosive chloride solution (borate buffer with NaCl salt). The influence of time, NaCl concentration, and potential was investigated; - In situ exploration of a 304L strained surface. It revealed the first stages of the surface plastic evolutions like activation of sliding dislocations, materialized by parallel steps of about 2 nm high in the same grain. The secondary sliding plane systems were also noticeable for higher deformation rates. Recent results concerning in situ AFM observation of corroded surfaces under strain in a chloride media will be presented. (authors)

  13. Effect of H{sub 2}O{sub 2} on the corrosion behavior of 304L stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Song, Taek Ho

    1994-02-15

    In connection with the safe storage of high level nuclear waste, effect of H{sub 2}O{sub 2} on the corrosion behavior of 304L stainless steel was examined. Open circuit potentials and polarization curves were measured with and without H{sub 2}O{sub 2}. The experimental results show that H{sub 2}O{sub 2} increased corrosion potential and decreased pitting potential. The passive range, therefore, decreased as H{sub 2}O{sub 2} concentration increased, indicating that pitting resistance was decreased by the existence of H{sub 2}O{sub 2} in the electrolyte. These effects of H{sub 2}O{sub 2} on corrosion of 304L stainless steel are considered to be similar to those of γ-irradiation. To compare the effects of H{sub 2}O{sub 2} with those of O{sub 2}, cathodic and anodic polarization curves were made in three types of electrolyte such as aerated, deaerated, and stirred electrolyte. The experimental results show that the effects of H{sub 2}O{sub 2} on the corrosion behavior were very similar to those of O{sub 2} such as increase of corrosion potential, decrease of pitting resistance, and increase of repassivation potential. Further, H{sub 2}O{sub 2} played much greater role in controlling cathodic reaction rate in neutral water environment. In acid and alkaline media, potential shifts by H{sub 2}O{sub 2} were restricted by the large current density of proton reduction and by the le Chatelier's principle respectively.

  14. Effect of H{sub 2}O{sub 2} on the corrosion behavior of 304L stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Song, Taek Hoh; Kim, In Sub [Korea Advanced Institute of Science and Technology, Taejon (Korea, Republic of); Noh, Sung Kee [Korea Atomic Energy Research Institute, Taejon (Korea, Republic of)

    1995-08-01

    In connection with the safe storage of high level nuclear waste, effect of H{sub 2}O{sub 2} on the corrosion behavior of 304L stainless steel was examined. Open circuit potentials and polarization curves were measured with and without H{sub 2}O{sub 2}. The experimental results show that H{sub 2}O{sub 2} increased corrosion potential and decreased pitting potential. The passive range, therefore, decreased as H{sub 2}O{sub 2} concentration increased, indicating that pitting resistance was decreased by the existence of H{sub 2}O{sub 2} in the electrolyte. These effects of H{sub 2}O{sub 2} on corrosion of 304L stainless steel are considered to be similar to those of {gamma}-irradiation. To compare the effects of H{sub 2}O{sub 2} with those of O{sub 2}, cathodic and anodic polarization curves were made in three types of electrolyte such as aerated, deaerated, and stirred electrolyte. The experimental results show that the effects of H{sub 2}O{sub 2} on the corrosion behavior were very similar to those of O{sub 2} such as increase of corrosion potential, decrease of pitting resistance, and increase of repassivation potential. In acid and alkaline media, the corrosion potential shifts by H{sub 2}O{sub 2} were restricted by the large current density of proton reduction and by the le Chatelier`s principle respectively. 13 figs., 1 tabs., 17 refs. (Author).

  15. In situ AFM study of pitting corrosion and corrosion under strain on a 304L stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Martin, F.A. [CEA de Saclay, DRECAM/SPCSI, 91191 Gif-sur-Yvette cedex (France); Cousty, J.; Masson, J-L. [CEA de Saclay, DRECAM/SPCSI, 91191 Gif-sur-Yvette cedex (France); Bataillon, C. [CEA de Saclay, DEN/DPC/LECA, 91191 Gif-sur-Yvette cedex (France)

    2004-07-01

    Our study is centred on surface localised corrosion under strain of a standard stainless steel (304L). The interest we take in these corrosion phenomena is led by the general misunderstanding of its primary initiation steps. The goal of this study is to determine precisely the relationships between local geometrical defects (grain boundaries, dislocation lines, etc) or chemical defects (inclusions) with the preferential sites of corrosion on the strained material. By combining three techniques at the same time: Atomic Force Microscopy, an electrochemical cell and a traction plate, we can observe in situ the effect of localised stress and deformation on the sample surface exposed to a corrosive solution. We managed to build an original set-up compatible with all the requirements of these three different techniques. Furthermore, we prepared the surface of our sample as flat as possible to decrease at maximum the topographical noise in order to observe the smallest defect on the surface. By using a colloidal suspension of SiO{sub 2}, we obtained surfaces with a typical corrugation (RMS) of about 1 A for areas of at least 1 {mu}m{sup 2}. Our experimental study has been organised in two primary investigations: - In situ study of the morphology evolution of the surface under a corrosive chloride solution (borate buffer with NaCl salt). The influence of time, NaCl concentration, and potential was investigated; - In situ exploration of a 304L strained surface. It revealed the first stages of the surface plastic evolutions like activation of sliding dislocations, materialized by parallel steps of about 2 nm high in the same grain. The secondary sliding plane systems were also noticeable for higher deformation rates. Recent results concerning in situ AFM observation of corroded surfaces under strain in a chloride media will be presented. (authors)

  16. Influence of surface finish on the high cycle fatigue behavior of a 304L austenitic stainless steel

    International Nuclear Information System (INIS)

    Petitjean, S.

    2003-06-01

    This work has dealt with the influence of surface finish on the high cycle fatigue behavior of a 304L. The role played by roughness, surface hardening and residual stresses has been particularly described. First part of this study has consisted of the production of several surface finishes. These latter were obtained by turning, grinding, mechanical polishing and sandblasting. The obtained surfaces were then characterised in terms of roughness, hardening, microstructure and residual stresses. Fatigue tests were finally conducted under various stress ratios or mean stresses at two temperatures (25 C and 300 C). Results clearly evidenced an effect of the surface integrity on the fatigue resistance of the 304L. This influence is nevertheless more pronounced at ambient temperature and for a positive mean stress. For all explored testing conditions, the lowest endurance limit was obtained for ground specimens whereas polished samples exhibited the best fatigue strength. Results also cleared out a detrimental influence of a positive mean stress in the case of specimens having surface defaults of a great acuity. The study of the relative effect of each of the surface parameter, under a positive stress ratio and at the ambient temperature, showed that roughness profile and surface hardening are the two more influential factors. The role of the residual stresses remains negligible due to their rapid relaxation during the application of the first cycles of fatigue. The estimation of the initiation and propagation periods showed that mechanisms differed as a function of the applied stress ratio. Crack propagation is governed by the parameter DK at a positive stress ratio and by Dep/2 in the case of tension-compression tests. (author)

  17. Distinguishing effect of buffing vs. grinding, milling and turning operations on the chloride induced SCC susceptibility of 304L austenitic stainless steel

    International Nuclear Information System (INIS)

    Kumar, Pandu Sunil; Acharyya, Swati Ghosh; Rao, S.V. Ramana; Kapoor, Komal

    2017-01-01

    The study compares the effect of different surface working operations like grinding, milling, turning and buffing on the Cl – induced stress corrosion cracking (SCC) susceptibility of austenitic 304L stainless steel (SS) in a chloride environment. SS 304L was subjected to four different surface working operations namely grinding, milling, turning and buffing. The residual stress distribution of the surface as a result of machining was measured by X-ray diffraction. The Cl – induced SCC susceptibility of the different surface worked samples were determined by testing in boiling magnesium chloride as per ASTM G36 for 3 h, 9 h and 72 h. The surface and cross section of the samples both pre and post exposure to the corrosive medium was characterized using optical microscopy, scanning electron microscopy (SEM). The study revealed that grinding, milling and turning operations resulted in high tensile residual stresses on the surface together with the high density of deformation bands making these surfaces highly susceptible to Cl – induced SCC. On the other hand buffing produces compressive residual stresses on the surface with minimal plastic strain, making it more resistance to Cl – induced SCC. The study highlights that the conventional machining operations on 304L SS surfaces should be invariably followed by buffing operation to make the surfaces more resistance to SCC. - Highlights: • Grinding, milling and turning lead to tensile residual stresses and plastic strain. • Buffing leads to compressive residual stresses on the surface and minimal strain. • Grinding, milling and turning make 304L SS surface susceptible to SCC. • Buffed 304L SS surface is immune to SCC. • Grinding, milling, and turning operations should be followed by buffing operation.

  18. Distinguishing effect of buffing vs. grinding, milling and turning operations on the chloride induced SCC susceptibility of 304L austenitic stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, Pandu Sunil [School of Engineering Sciences and Technology, University of Hyderabad, Hyderabad 500046 (India); Acharyya, Swati Ghosh, E-mail: swati364@gmail.com [School of Engineering Sciences and Technology, University of Hyderabad, Hyderabad 500046 (India); Rao, S.V. Ramana; Kapoor, Komal [Nuclear Fuel Complex, Department of Atomic Energy, Government of India, Hyderabad 500062 (India)

    2017-02-27

    The study compares the effect of different surface working operations like grinding, milling, turning and buffing on the Cl{sup –} induced stress corrosion cracking (SCC) susceptibility of austenitic 304L stainless steel (SS) in a chloride environment. SS 304L was subjected to four different surface working operations namely grinding, milling, turning and buffing. The residual stress distribution of the surface as a result of machining was measured by X-ray diffraction. The Cl{sup –} induced SCC susceptibility of the different surface worked samples were determined by testing in boiling magnesium chloride as per ASTM G36 for 3 h, 9 h and 72 h. The surface and cross section of the samples both pre and post exposure to the corrosive medium was characterized using optical microscopy, scanning electron microscopy (SEM). The study revealed that grinding, milling and turning operations resulted in high tensile residual stresses on the surface together with the high density of deformation bands making these surfaces highly susceptible to Cl{sup –} induced SCC. On the other hand buffing produces compressive residual stresses on the surface with minimal plastic strain, making it more resistance to Cl{sup –} induced SCC. The study highlights that the conventional machining operations on 304L SS surfaces should be invariably followed by buffing operation to make the surfaces more resistance to SCC. - Highlights: • Grinding, milling and turning lead to tensile residual stresses and plastic strain. • Buffing leads to compressive residual stresses on the surface and minimal strain. • Grinding, milling and turning make 304L SS surface susceptible to SCC. • Buffed 304L SS surface is immune to SCC. • Grinding, milling, and turning operations should be followed by buffing operation.

  19. Teste de tuberculinização em caprinos (Capra hircus experimentalmente sensibilizados Tuberculin test in experimentally sensitized goats (Capra hircus

    Directory of Open Access Journals (Sweden)

    Paulo Eduardo Gomes da Silva

    2006-06-01

    Full Text Available Foram estabelecidos critérios de interpretação do teste de tuberculinização aplicado ao diagnóstico da tuberculose em grupos de caprinos experimentalmente sensibilizados. Dos 30 animais utilizados, dez foram sensibilizados com Mycobacterium avium - amostra D4 (grupo A e dez com Mycobacterium bovis - amostra AN5 (grupo B. Dez caprinos não foram sensibilizados e constituíram o grupo controle (grupo C. No teste cervical simples, realizado com tuberculina bovina (M. bovis e lido às 72 horas pós-tuberculinização (p.t., as reações positivas foram aquelas em que houve aumento da espessura da dobra de pele igual ou superior a 3,9mm; reações inconclusivas, quando situadas entre 1,8 e 3,8mm, e negativas quando iguais ou menores que 1,7mm. A análise dos resultados do teste cervical comparativo, realizado com o M. avium e M. bovis e lido às 72 horas p.t., indicou reação positiva quando o aumento da espessura da dobra da pele induzida pela tuberculina bovina superou a reação à aviária em pelo menos 2,5mm; reação inconclusiva quando a diferença entre a reação à tuberculina bovina e à tuberculina aviária ficou situada entre 1,9 e 2,4mm; e negativa quando a reação bovina ultrapassou a aviária em até 1,8mm. Às 96 horas após a injeção da tuberculina, foi efetuada a avaliação histológica do local das reações tuberculínicas colhendo-se amostras de pele de cinco caprinos dos grupos A e B e de quatro animais do grupo controle; os resultados confirmaram a presença, nos grupos sensibilizados, de infiltrado inflamatório, constituído, preferencialmente, por células mononucleares.The tuberculin skin test was established with the aim to be applied in the diagnosis of tuberculosis in experimentally sensitized goats. Thirty goats were alocated into three groups with ten animals each. The animals in group A were sensitized with Mycobacterium avium sample D4; group B with Mycobacterium bovis sample AN5; and group C (control was

  20. Low cycle fatigue: high cycle fatigue damage accumulation in a 304L austenitic stainless steel; Endommagement et cumul de dommage en fatigue dans le domaine de l'endurance limitee d'un acier inoxydable austenitique 304L

    Energy Technology Data Exchange (ETDEWEB)

    Lehericy, Y

    2007-05-15

    The aim of this study was to evaluate the consequences of a Low Cycle Fatigue pre-damage on the subsequent fatigue limit of a 304L stainless steel. The effects of hardening and severe roughness (grinding) have also been investigated. In a first set of tests, the evolution of the surface damage induced by the different LCF pre-cycling was characterized. This has permitted to identify mechanisms and kinetics of damage in the plastic domain for different surface conditions. Then, pre-damaged samples were tested in the High Cycle Fatigue domain in order to establish the fatigue limits associated with each level of pre-damage. Results evidence that, in the case of polished samples, an important number of cycles is required to initiate surface cracks ant then to affect the fatigue limit of the material but, in the case of ground samples, a few number of cycles is sufficient to initiate cracks and to critically decrease the fatigue limit. The fatigue limit of pre-damaged samples can be estimated using the stress intensity factor threshold. Moreover, this detrimental effect of severe surface conditions is enhanced when fatigue tests are performed under a positive mean stress (author)

  1. Nanosecond laser surface modification of AISI 304L stainless steel: Influence the beam overlap on pitting corrosion resistance

    International Nuclear Information System (INIS)

    Pacquentin, Wilfried; Caron, Nadège; Oltra, Roland

    2014-01-01

    Surface modifications of AISI 304L stainless steel by laser surface melting (LSM) were investigated using a nanosecond pulsed laser-fibre doped by ytterbium at different overlaps. The objective was to study the change in the corrosion properties induced by the treatment of the outer-surface of the stainless steel without modification of the bulk material. Different analytical techniques such as scanning electron microscopy (SEM), X-ray diffraction (XRD), and glow discharge optical emission spectrometry (GDOES) were used to characterize the laser-melted surface. The corrosion resistance was evaluated in a chloride solution at room temperature by electrochemical tests. The results showed that the crystallographic structure, the chemical composition, the properties of the induced oxide layer and consequently the pitting corrosion resistance strongly depend on the overlap rate. The most efficient laser parameters led to an increase of the pitting potential by more than 300 mV, corresponding to a quite important improvement of the corrosion resistance. This latter was correlated to chromium enrichment (47 wt.%) at the surface of the stainless steel and the induced absence of martensite and ferrite phases. However, these structural and chemical modifications were not sufficient to explain the change in corrosion behaviour: defects and adhesion of the surface oxide layer must have been taken into consideration.

  2. Standard test method for electrochemical reactivation (EPR) for detecting sensitization of AISI type 304 and 304L stainless steels

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    1994-01-01

    1.1 This test method covers a laboratory procedure for conducting an electrochemical reactivation (EPR) test on AISI Type 304 and 304L (UNS No. S30400 and S30403, respectively) stainless steels. This test method can provide a nondestructive means of quantifying the degree of sensitization in these steels (1, 2, 3). This test method has found wide acceptance in studies of the effects of sensitization on intergranular corrosion and intergranular stress corrosion cracking behavior (see Terminology G15). The EPR technique has been successfully used to evaluate other stainless steels and nickel base alloys (4), but the test conditions and evaluation criteria used were modified in each case from those cited in this test method. 1.2 The values stated in SI units are to be regarded as the standard. The inch-pound units given in parentheses are for information only. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this...

  3. Functionally graded material of 304L stainless steel and inconel 625 fabricated by directed energy deposition: Characterization and thermodynamic modeling

    International Nuclear Information System (INIS)

    Carroll, Beth E.; Otis, Richard A.; Borgonia, John Paul; Suh, Jong-ook; Dillon, R. Peter; Shapiro, Andrew A.; Hofmann, Douglas C.; Liu, Zi-Kui; Beese, Allison M.

    2016-01-01

    Many engineering applications, particularly in extreme environments, require components with properties that vary with location in the part. Functionally graded materials (FGMs), which possess gradients in properties such as hardness or density, are a potential solution to address these requirements. The laser-based additive manufacturing process of directed energy deposition (DED) can be used to fabricate metallic parts with a gradient in composition by adjusting the volume fraction of metallic powders delivered to the melt pool as a function of position. As this is a fusion process, secondary phases may develop in the gradient zone during solidification that can result in undesirable properties in the part. This work describes experimental and thermodynamic studies of a component built from 304L stainless steel incrementally graded to Inconel 625. The microstructure, chemistry, phase composition, and microhardness as a function of position were characterized by microscopy, energy dispersive spectroscopy, X-ray diffraction, and microindentation. Particles of secondary phases were found in small amounts within cracks in the gradient zone. These were ascertained to consist of transition metal carbides by experimental results and thermodynamic calculations. The study provides a combined experimental and thermodynamic computational modeling approach toward the fabrication and evaluation of a functionally graded material made by DED additive manufacturing.

  4. Martensite phase reversion-induced nano/ ultrafine grained AISI 304L stainless steel with magnificent mechanical properties

    Directory of Open Access Journals (Sweden)

    Mohammad Shirdel

    2015-06-01

    Full Text Available Austenitic stainless steels are extensively used in various applications requiring good corrosion resistance and formability. In the current study, the formation of nano/ ultrafine grained austenitic microstructure in a microalloyed AISI 304L stainless steel was investigated by the advanced thermomechanical process of reversion of strain-induced martensite. For this purpose, samples were subjected to heavy cold rolling to produce a nearly complete martensitic structure. Subsequently, a wide range of annealing temperatures (600 to 800°C and times (1 to 240 min were employed to assess the reversion behavior and to find the best annealing condition for the production of the nano/ultrafine grained austenitic microstructure. Microstructural characterizations have been performed using X-ray diffraction (XRD, scanning electron microscopy (SEM, and magnetic measurement, whereas the mechanical properties were assessed by tensile and hardness tests. After thermomechanical treatment, a very fine austenitic structure was obtained, which was composed of nano sized grains of ~ 85 nm in an ultrafine grained matrix with an average grain size of 480 nm. This microstructure exhibited superior mechanical properties: high tensile strength of about 1280 MPa with a desirable elongation of about 41%, which can pave the way for the application of these sheets in the automotive industry.

  5. Characterization of welding of AISI 304l stainless steel similar to the core encircling of a BWR reactor

    International Nuclear Information System (INIS)

    Gachuz M, M.E.; Palacios P, F.; Robles P, E.F.

    2003-01-01

    Plates of austenitic stainless steel AISI 304l of 0.0381 m thickness were welded by means of the SMAW process according to that recommended in the Section 9 of the ASME Code, so that it was reproduced the welding process used to assemble the encircling of the core of a BWR/5 reactor similar to that of the Laguna Verde Nucleo electric plant, there being generated the necessary documentation for the qualification of the one welding procedure and of the welder. They were characterized so much the one base metal, as the welding cord by means of metallographic techniques, scanning electron microscopy, X-ray diffraction, mechanical essays and fracture mechanics. From the obtained results it highlights the presence of an area affected by the heat of up to 1.5 mm of wide and a value of fracture tenacity (J IC ) to ambient temperature for the base metal of 528 KJ/m 2 , which is diminished by the presence of the welding and by the increment in the temperature of the one essay. Also it was carried out an fractographic analysis of the fracture zone generated by the tenacity essays, what evidence a ductile fracture. The experimental values of resistance and tenacity are important for the study of the structural integrity of the encircling one of the core. (Author)

  6. Soldadura de recargue con aceros inoxidables dúplex

    OpenAIRE

    Zappa, Sebastián; Martínez, Juan; Svoboda, Hernán Gabriel; Surian, Estela

    2016-01-01

    Los aceros inoxidables dúplex se caracterizan por poseer una estructura dual constituida por ferrita y austenita en iguales proporciones. Poseen una combinación de buenas propiedades mecánicas y resistencia a la corrosión, que dependen de la composición química y de la relación entre las fases mencionadas. Son ampliamente utilizados en las industrias de procesos químicos y, fundamentalmente, del petróleo y gas. La soldadura de recargue, es utilizada en las industrias de fabricación y reparaci...

  7. Effect of strain-path on stress corrosion cracking of AISI 304L stainless steel in PWR primary environment at 360 deg. C

    International Nuclear Information System (INIS)

    Couvant, T.; Vaillant, F.; Boursier, JM.; Delafosse, D.

    2004-01-01

    Austenitic stainless steels (ASS) are widespread in primary and auxiliary circuits of PWR. Moreover, some components suffer stress corrosion cracking (SCC) under neutron irradiation. This degradation could be the result of the increase of hardness or the modification of chemical composition at the grain boundary by irradiation. In order to avoid complex and costly corrosion facilities, the effects of irradiation on the material are commonly simulated by applying a cold work on non-irradiated material prior to stress corrosion cracking tests. Slow strain rate tests were conducted on an austenitic stainless steel (SS) AISI 304L in PWR environment (360 deg. C). Particular attention was directed towards pre-straining effects on crack growth rate (CGR) and crack growth path (CGP). Results have demonstrated that the susceptibility of 304L to SCC in high-temperature hydrogenated water was enhanced by pre-straining. It seemed that IGSCC was enhanced by complex strain paths. (authors)

  8. Effect of Low-Temperature Sensitization on the Corrosion Behavior of AISI Type 304L SS Weld Metal in Simulated Groundwater

    Science.gov (United States)

    Suresh, Girija; Nandakumar, T.; Viswanath, A.

    2018-05-01

    The manuscript presents the investigations carried out on the effect of low-temperature sensitization (LTS) of 304L SS weld metal on its corrosion behavior in simulated groundwater, for its application as a canister material for long-term storage of nuclear vitrified high-level waste in geological repositories. AISI type 304L SS weld pad was fabricated by multipass gas tungsten arc welding process using 308L SS filler wire. The as-welded specimens were subsequently subjected to carbide nucleation and further to LTS at 500 °C for 11 days to simulate a temperature of 300 °C for 100-year life of the canister in geological repositories. Delta ferrite ( δ-ferrite) content of the 304L SS weld metal substantially decreased on carbide nucleation treatment and further only a marginal decrease occurred on LTS treatment. The microstructure of the as-welded consisted of δ-ferrite as a minor phase distributed in austenite matrix. The δ-ferrite appeared fragmented in the carbide-nucleated and LTS-treated weld metal. The degree of sensitization measured by double-loop electrochemical potentokinetic reactivation method indicated an increase in carbide nucleation treatment when compared to the as-welded specimens, and further increase occurred on LTS treatment. Potentiodynamic anodic polarization investigations in simulated groundwater indicated a substantial decrease in the localized corrosion resistance of the carbide-nucleated and LTS 304L SS weld metals, when compared to the as-welded specimens. Post-experimental micrographs indicated pitting as the primary mode of attack in the as-welded, while pitting and intergranular corrosion (IGC) occurred in the carbide-nucleated weld metal. LTS-treated weld metal predominantly underwent IGC attack. The decrease in the localized corrosion resistance of the weld metal after LTS treatment was found to have a direct correlation with the degree of sensitization and the weld microstructure. The results are detailed in the manuscript.

  9. Effect of Low-Temperature Sensitization on the Corrosion Behavior of AISI Type 304L SS Weld Metal in Simulated Groundwater

    Science.gov (United States)

    Suresh, Girija; Nandakumar, T.; Viswanath, A.

    2018-04-01

    The manuscript presents the investigations carried out on the effect of low-temperature sensitization (LTS) of 304L SS weld metal on its corrosion behavior in simulated groundwater, for its application as a canister material for long-term storage of nuclear vitrified high-level waste in geological repositories. AISI type 304L SS weld pad was fabricated by multipass gas tungsten arc welding process using 308L SS filler wire. The as-welded specimens were subsequently subjected to carbide nucleation and further to LTS at 500 °C for 11 days to simulate a temperature of 300 °C for 100-year life of the canister in geological repositories. Delta ferrite (δ-ferrite) content of the 304L SS weld metal substantially decreased on carbide nucleation treatment and further only a marginal decrease occurred on LTS treatment. The microstructure of the as-welded consisted of δ-ferrite as a minor phase distributed in austenite matrix. The δ-ferrite appeared fragmented in the carbide-nucleated and LTS-treated weld metal. The degree of sensitization measured by double-loop electrochemical potentokinetic reactivation method indicated an increase in carbide nucleation treatment when compared to the as-welded specimens, and further increase occurred on LTS treatment. Potentiodynamic anodic polarization investigations in simulated groundwater indicated a substantial decrease in the localized corrosion resistance of the carbide-nucleated and LTS 304L SS weld metals, when compared to the as-welded specimens. Post-experimental micrographs indicated pitting as the primary mode of attack in the as-welded, while pitting and intergranular corrosion (IGC) occurred in the carbide-nucleated weld metal. LTS-treated weld metal predominantly underwent IGC attack. The decrease in the localized corrosion resistance of the weld metal after LTS treatment was found to have a direct correlation with the degree of sensitization and the weld microstructure. The results are detailed in the manuscript.

  10. Environmental effect on cracking of an 304L austenitic stainless steels in PWR primary environment under cyclic loading

    International Nuclear Information System (INIS)

    Huin, N.

    2013-01-01

    The present study was undertaken in order to get further insights on cracking mechanisms in a 304L stainless steel. More precisely, a first objective of this study was to evaluate the effect of various cold working conditions on the cyclic stress-strain behavior and the fatigue life in air and in PWR primary environment. In air a prior hardening was found to reduce the fatigue life in the LCF regime but not in primary environment. In both environments, the fatigue limit of the hardened materials was increased after cold working.The second objective addresses the effect of the air and the PWR primary environments on the cracking mechanisms (initiation and propagation) in the annealed material in the LCF regime. More precisely, the kinetics of crack initiation and micro crack propagation were evaluated with a multi scale microscopic approach in air and in primary environment. In PWR primary environment, during the first cycles, preferential oxidation occurs along emerging dissociated dislocation and each cycle generates a new C-rich/Fe-rich oxide layer. Then, during cycling, the microstructure evolves from stacking fault into micro twinning and preferential oxidation occurs by continuous shearing and dissolution of the passive film. Beyond a certain crack depth (≤3 μm), the crack starts to propagate with a direction close to a 90 degrees angle from the surface. The crack continues its propagation by successive generation of shear bands and fatigue striations at each cycle up to failure. The role of corrosion hydrogen on these processes is finally discussed. (author)

  11. Modelling of cyclic plasticity for austenitic stainless steels 304L, 316L, 316L(N)-IG

    Energy Technology Data Exchange (ETDEWEB)

    Dalla Palma, Mauro, E-mail: mauro.dallapalma@igi.cnr.it

    2016-11-01

    Highlights: • Stress-strain amplitudes of cyclic stress strain curves defined by design codes are provided as reference data. • A macroinstruction simulating cyclic plasticity and producing hardening parameters of constitutive models is developed. • Hardening parameters of the nonlinear Chaboche model are provided for stainless steels 316l-N, 316L, 304L at different temperatures. • Ratcheting is simulated by using the produced hardening parameters. - Abstract: The integrity assessment of structures subjected to cyclic loading must be verified with regard to cyclic type damage including time-independent fatigue and progressive deformation or ratcheting. Cyclic damage is verified simulating the material elastic-plastic loop and looking at the accumulated net plastic strain during each cycle at all points of the structure subjected to the complete time history of loadings. This work deals with the development of a numerical model producing the Chaboche hardening parameters starting from stress-strain data produced by testing of materials. Then, the total plastic strain can be simulated using the Chaboche inelastic constitutive model requested for finite element analyses. This is particularly demanding for pressure vessels, pressurised piping, boilers, and mechanical components of nuclear installations made of stainless steels. A design optimisation by iterative analyses is developed to approach the stress-strain test data with the Chaboche model. The parameters treated as design variables are the Chaboche parameters and the objective function to be minimised is a combination of the deviations from test data. The optimiser calls a macroinstruction simulating cyclic loading of a sample for different material temperatures. The numerical model can be used to produce hardening parameters of materials for inelastic finite element verifications of structures with complex joints like elbows subjected to a combination of steady sustained and cyclic loads.

  12. Effect of heat input on the microstructure, residual stresses and corrosion resistance of 304L austenitic stainless steel weldments

    Energy Technology Data Exchange (ETDEWEB)

    Unnikrishnan, Rahul, E-mail: rahulunnikrishnannair@gmail.com [Department of Metallurgical and Materials Engineering, Visvesvaraya National Institute of Technology (VNIT), South Ambazari Road, Nagpur 440010, Maharashtra (India); Idury, K.S.N. Satish, E-mail: satishidury@gmail.com [Department of Metallurgical and Materials Engineering, Visvesvaraya National Institute of Technology (VNIT), South Ambazari Road, Nagpur 440010, Maharashtra (India); Ismail, T.P., E-mail: tpisma@gmail.com [Department of Metallurgical and Materials Engineering, Visvesvaraya National Institute of Technology (VNIT), South Ambazari Road, Nagpur 440010, Maharashtra (India); Bhadauria, Alok, E-mail: alokbhadauria1@gmail.com [Department of Metallurgical and Materials Engineering, Visvesvaraya National Institute of Technology (VNIT), South Ambazari Road, Nagpur 440010, Maharashtra (India); Shekhawat, S.K., E-mail: satishshekhawat@gmail.com [Department of Metallurgical Engineering and Materials Science, Indian Institute of Technology Bombay (IITB), Powai, Mumbai 400076, Maharashtra (India); Khatirkar, Rajesh K., E-mail: rajesh.khatirkar@gmail.com [Department of Metallurgical and Materials Engineering, Visvesvaraya National Institute of Technology (VNIT), South Ambazari Road, Nagpur 440010, Maharashtra (India); Sapate, Sanjay G., E-mail: sgsapate@yahoo.com [Department of Metallurgical and Materials Engineering, Visvesvaraya National Institute of Technology (VNIT), South Ambazari Road, Nagpur 440010, Maharashtra (India)

    2014-07-01

    Austenitic stainless steels are widely used in high performance pressure vessels, nuclear, chemical, process and medical industry due to their very good corrosion resistance and superior mechanical properties. However, austenitic stainless steels are prone to sensitization when subjected to higher temperatures (673 K to 1173 K) during the manufacturing process (e.g. welding) and/or certain applications (e.g. pressure vessels). During sensitization, chromium in the matrix precipitates out as carbides and intermetallic compounds (sigma, chi and Laves phases) decreasing the corrosion resistance and mechanical properties. In the present investigation, 304L austenitic stainless steel was subjected to different heat inputs by shielded metal arc welding process using a standard 308L electrode. The microstructural developments were characterized by using optical microscopy and electron backscattered diffraction, while the residual stresses were measured by X-ray diffraction using the sin{sup 2}ψ method. It was observed that even at the highest heat input, shielded metal arc welding process does not result in significant precipitation of carbides or intermetallic phases. The ferrite content and grain size increased with increase in heat input. The grain size variation in the fusion zone/heat affected zone was not effectively captured by optical microscopy. This study shows that electron backscattered diffraction is necessary to bring out changes in the grain size quantitatively in the fusion zone/heat affected zone as it can consider twin boundaries as a part of grain in the calculation of grain size. The residual stresses were compressive in nature for the lowest heat input, while they were tensile at the highest heat input near the weld bead. The significant feature of the welded region and the base metal was the presence of a very strong texture. The texture in the heat affected zone was almost random. - Highlights: • Effect of heat input on microstructure, residual

  13. Effect of microstructure and chemical composition on localized corrosion resistance of a AISI 304L stainless steel after nanopulsed-laser surface melting

    International Nuclear Information System (INIS)

    Pacquentin, W.; Caron, N.; Oltra, R.

    2015-01-01

    Highlights: • Laser surface melting treatments require neither additional feedstock nor contact. • By affecting 1 μm, the pitting potential of laser treated 304L increases by 500 mV. • Surface modification of laser treated sample observed by TEM. • The physico-chemical properties of the surface are correlated to overlap rate. • AISI 304L pitting corrosion resistance strongly depends of overlap rate. - Abstract: Changes induced in the surface properties of AISI 304L stainless steel when it is treated with a nanopulsed ytterbium-doped fiber laser were investigated to determine the microscale distribution of its physico-chemical properties. A Gaussian energy distribution was created with a radius of 71 μm (1/e 2 ) at the focal point. Local investigations were carried out using transmission electron microscopy to consider the effect of overlapping individual laser impacts. The results obtained reveal that laser surface melting leads to changes in the crystallographic structure of the steel through the formation of a δ-ferritic phase. It also results in the creation of an oxide layer that increases the corrosion resistance of the steel, with the chemical composition, structure and thickness of this layer being dependent on the overlap percentage and the position along the beam radius. Measurement of the localized corrosion resistance in a 30 g L −1 NaCl solution using polarization curves found that optimal laser treatment conditions can led to an increase in the breakdown potential of more than 500 mV, which corresponds to a significant improvement in corrosion resistance.

  14. Evaluation at 290 degrees Celsius and 8 MPa of the anticorrosion properties of hydrothermal ceramic nano deposits on preoxidized 304l Ss

    Energy Technology Data Exchange (ETDEWEB)

    Lopez G, N.; Marin A, M.; Medina A, A. L. [ININ, Carretera Mexico-Toluca s/n, 52750 Ocoyoacac, Estado de Mexico (Mexico); Galicia A, G., E-mail: natali_log@hotmail.com [Universidad Veracruzana, Instituto de Ingenieria, Av. Juan Pablo II s/n, Fracc. Costa Verde, 94294 Boca del Rio, Veracruz (Mexico)

    2017-09-15

    In the present paper, we present the electrochemical evaluation carried out under reductive conditions (molar ratio H{sub 2}:O{sub 2} >5), at 290 degrees Celsius and 8 MPa, of preoxidized 304l Ss with hydrothermal deposits of nanoparticles of TiO{sub 2} and ZrO{sub 2}. The anticorrosion properties of the deposits were studied by Electrochemical Impedance Spectroscopy (EIS) and Linear Polarization Resistance (LPR). After electrochemical tests, the samples were characterized by X-Ray Diffraction (XRD) and Scanning Electron Microscopy (Sem). It was found by EIS that both, ZrO{sub 2} and TiO{sub 2} produce an increase in the charge transfer resistance (R{sub CT}) of preoxidized 304l Ss. At the same time, by LPR we observed that the studied ceramic nano deposits decrease the corrosion rate (Cr) and corrosion current density (i{sub corr}), however, in most of the cases the Electrochemical Corrosion Potential (Ecp) is slightly higher in the presence of the ceramic nano deposits that the one of preoxidized 304l Ss. After holding time at 290 degrees Celsius, when the impedance (Z) increases, the capacitance increases also, which is attributed to a surface increase due to the roughness of the oxide formed at this temperature under a reductive environment. The observed electrochemical behavior has a dependence on the homogeneity and thickness of the deposits, as has been corroborated by Sem and XRD. The best electrochemical results are obtained when two conditions are fulfilled: The bigger the effective coated area and the lower the deposit thickness. (Author)

  15. Influence of Size on the Microstructure and Mechanical Properties of an AISI 304L Stainless Steel—A Comparison between Bulk and Fibers

    Directory of Open Access Journals (Sweden)

    Francisco J. Baldenebro-Lopez

    2015-01-01

    Full Text Available In this work, the mechanical properties and microstructural features of an AISI 304L stainless steel in two presentations, bulk and fibers, were systematically studied in order to establish the relationship among microstructure, mechanical properties, manufacturing process and effect on sample size. The microstructure was analyzed by XRD, SEM and TEM techniques. The strength, Young’s modulus and elongation of the samples were determined by tensile tests, while the hardness was measured by Vickers microhardness and nanoindentation tests. The materials have been observed to possess different mechanical and microstructural properties, which are compared and discussed.

  16. Study of interaction of fatigue damage and ratcheting. Effect of a tensile primary load on torsion fatigue resistance of stainless steel 304 L at ambient temperature

    International Nuclear Information System (INIS)

    Hakem, N.S.

    1987-01-01

    Effect of ratcheting on fatigue resistance of a stainless steel 304 L, used for reactor vessels, is studied experimentally. Lifetime of samples is reduced if a static constant tensile load (primary loading) is superimposed to cyclic torsion deformations (secondary loading). An equivalent deformation concept is developed to express a criterion of fatigue rupture under primary loading. No effect is noted on the curve of cyclic strain hardening. This fatigue analysis gives no information on cumulated axial deformation. Progressive elongation, observed during testing, is dependent of primary and secondary loading. Rupture is produced by fatigue because cumulated axial deformation is limited ( 4 cycles at rupture cumulated deformation is [fr

  17. Oligo-cyclic damage and behaviour of a 304 L austenitic stainless steel according to environment (vacuum, air, PWR primary water) at 300 C

    International Nuclear Information System (INIS)

    De Baglion, L.

    2011-01-01

    Nowadays, for nuclear power plants licensing or operating life extensions, various safety authorities require the consideration of the primary water environment effect on the fatigue life of Pressurized Water Reactor (PWR) components. Thus, this work focused on the study of low cycle fatigue damage kinetics and mechanisms, of a type 304L austenitic stainless steel. Several parameters effects such as temperature, strain rate or strain amplitude were investigated in air as in PWR water. Thanks to targeted in-vacuum tests, the intrinsic influence of these parameters and environments on the fatigue behaviour of the material was studied. It appears that compared with vacuum, air is already an active environment which is responsible for a strong decrease in fatigue lifetime of this steel, especially at 300 C and low strain amplitude. The PWR water coolant environment is more active than air and leads to increased damage kinetics, without any modifications of the initiation sites or propagation modes. Moreover, the decreased fatigue life in PWR water is essentially attributed to an enhancement of both initiation and micropropagation of 'short cracks'. Finally, the deleterious influence of low strain rates on the 304L austenitic stainless steel fatigue lifetime was observed in PWR water environment, in air and also in vacuum without any environmental effects. This intrinsic strain rate effect is attributed to the occurrence of the Dynamic Strain Aging phenomenon which is responsible for a change in deformation modes and for an enhancement of cracks initiation. (author)

  18. Processing of fine grained AISI 304L austenitic stainless steel by cold rolling and high-temperature short-term annealing

    Science.gov (United States)

    Naghizadeh, Meysam; Mirzadeh, Hamed

    2018-05-01

    An advanced thermomechanical process based on the formation and reversion of deformation-induced martensite was used to refine the grain size and enhance the hardness of an AISI 304L austenitic stainless steel. Both low and high reversion annealing temperatures and also the repetition of the whole thermomechanical cycle were considered. While a microstructure with average austenite grain size of a few micrometers was achieved based on cold rolling and high-temperature short-term annealing, an extreme grain refinement up to submicrometer regime was obtained by cold rolling followed by low-temperature long-term annealing. However, the required annealing time was found to be much longer, which negates its appropriateness for industrial production. While a magnificent grain refinement was achieved by one pass of the high-temperature thermomechanical process, the reduction in grain size was negligible by the repetition of the whole cycle. It was found that the hardness of the thermomechanically processed material is much higher than that of the as-received material. The results of the present work were shown to be compatible with the general trend of grain size dependence of hardness for AISI 304L stainless steel based on the Hall-Petch relationship. The results were also discussed based on the X-ray evaluation of dislocation density by modified Williamson-Hall plots.

  19. Influence of low-temperature nitriding on the strain-induced martensite and laser-quenched austenite in a magnetic encoder made from 304L stainless steel

    Science.gov (United States)

    Leskovšek, Vojteh; Godec, Matjaž; Kogej, Peter

    2016-01-01

    We have investigated the possibility of producing a magnetic encoder by an innovative process. Instead of turning grooves in the encoder bar for precise positioning, we incorporated the information in 304L stainless steel by transforming the austenite to martensite after bar extrusion in liquid nitrogen and marking it with a laser, which caused a local transformation of martensite back into austenite. 304L has an excellent corrosion resistance, but a low hardness and poor wear resistance, which limits its range of applications. However, nitriding is a very promising way to enhance the mechanical and magnetic properties. After low-temperature nitriding at 400 °C it is clear that both ε- and α′-martensite are present in the deformed microstructure, indicating the simultaneous stress-induced and strain-induced transformations of the austenite. The effects of a laser surface treatment and the consequent appearance of a non-magnetic phase due to the α′ → γ transformation were investigated. The EDS maps show a high concentration of nitrogen in the alternating hard surface layers of γN and α′N (expanded austenite and martensite), but no significantly higher concentration of chromium or iron was detected. The high surface hardness of this nitride layer will lead to steels and encoders with better wear and corrosion resistance. PMID:27492862

  20. Comparative study in the induced corrosion by sulfate reducing microorganisms, in a stainless steel 304L sensitized and a carbon steel API X65

    International Nuclear Information System (INIS)

    Diaz S, A.; Gonzalez F, E.; Arganis J, C.; Luna C, P.; Carapia M, L.

    2004-01-01

    In spite of the operational experience related with the presence of the phenomenon of microbiological corrosion (MIC) in industrial components, it was not but until the decade of the 80 s when the nuclear industry recognized its influence in some systems of Nuclear Generating Power plants. At the moment, diverse studies that have tried to explain the generation mechanism of this phenomenon exist; however, they are even important queries that to solve, especially those related with the particularities of the affected metallic substrates. Presently work, the electrochemical behavior of samples of stainless steel AISI 304L sensitized is evaluated and the carbon steel APIX65, before the action of sulfate reducing microorganisms low the same experimental conditions; found that for the APIX65 the presence of this type of bacteria promoted the formation of a stable biofilm that allowed the maintenance of the microorganisms that damaged the material in isolated places where stings were generated; while in the AISI 304L, it was not detected damage associated to the inoculated media. The techniques of Resistance to the Polarization and Tafel Extrapolation, allowed the calculation of the speed of uniform corrosion, parameter that doesn't seem to be influenced by the presence of the microorganisms; while that noise electrochemical it distinguished in real time, the effect of the sulfate reducing in the steel APIX65. (Author)

  1. Gas tungsten arc welding and friction stir welding of ultrafine grained AISI 304L stainless steel: Microstructural and mechanical behavior characterization

    Energy Technology Data Exchange (ETDEWEB)

    Sabooni, S., E-mail: s.sabooni@ma.iut.ac.ir [Department of Materials Engineering, Isfahan University of Technology, 84156-83111 Isfahan (Iran, Islamic Republic of); Karimzadeh, F.; Enayati, M.H. [Department of Materials Engineering, Isfahan University of Technology, 84156-83111 Isfahan (Iran, Islamic Republic of); Ngan, A.H.W. [Department of Mechanical Engineering, The University of Hong Kong, Pokfulam Road, Hong Kong (China); Jabbari, H. [Department of Materials Engineering, Isfahan University of Technology, 84156-83111 Isfahan (Iran, Islamic Republic of)

    2015-11-15

    In the present study, an ultrafine grained (UFG) AISI 304L stainless steel with the average grain size of 650 nm was successfully welded by both gas tungsten arc welding (GTAW) and friction stir welding (FSW). GTAW was applied without any filler metal. FSW was also performed at a constant rotational speed of 630 rpm and different welding speeds from 20 to 80 mm/min. Microstructural characterization was carried out by High Resolution Scanning Electron Microscopy (HRSEM) with Electron Backscattered Diffraction (EBSD) and Transmission Electron Microscopy (TEM). Nanoindentation, microhardness measurements and tensile tests were also performed to study the mechanical properties of the base metal and weldments. The results showed that the solidification mode in the GTAW welded sample is FA (ferrite–austenite) type with the microstructure consisting of an austenite matrix embedded with lath type and skeletal type ferrite. The nugget zone microstructure in the FSW welded samples consisted of equiaxed dynamically recrystallized austenite grains with some amount of elongated delta ferrite. Sigma phase precipitates were formed in the region ahead the rotating tool during the heating cycle of FSW, which were finally fragmented into nanometric particles and distributed in the weld nugget. Also there is a high possibility that the existing delta ferrite in the microstructure rapidly transforms into sigma phase particles during the short thermal cycle of FSW. These suggest that high strain and deformation during FSW can promote sigma phase formation. The final austenite grain size in the nugget zone was found to decrease with increasing Zener–Hollomon parameter, which was obtained quantitatively by measuring the peak temperature, calculating the strain rate during FSW and exact examination of hot deformation activation energy by considering the actual grain size before the occurrence of dynamic recrystallization. Mechanical properties observations showed that the welding

  2. Simulation and experimental comparison of the thermo-mechanical history and 3D microstructure evolution of 304L stainless steel tubes manufactured using LENS

    Science.gov (United States)

    Johnson, Kyle L.; Rodgers, Theron M.; Underwood, Olivia D.; Madison, Jonathan D.; Ford, Kurtis R.; Whetten, Shaun R.; Dagel, Daryl J.; Bishop, Joseph E.

    2017-12-01

    Additive manufacturing enables the production of previously unachievable designs in conjunction with time and cost savings. However, spatially and temporally fluctuating thermal histories can lead to residual stress states and microstructural variations that challenge conventional assumptions used to predict part performance. Numerical simulations offer a viable way to explore the root causes of these characteristics, and can provide insight into methods of controlling them. Here, the thermal history of a 304L stainless steel cylinder produced using the Laser Engineered Net Shape process is simulated using finite element analysis (FEA). The resultant thermal history is coupled to both a solid mechanics FEA simulation to predict residual stress and a kinetic Monte Carlo model to predict the three-dimensional grain structure evolution. Experimental EBSD measurements of grain structure and in-process infrared thermal data are compared to the predictions.

  3. Response to annealing and reirradiation of AISI 304L stainless steel following initial high-dose neutron irradiation in EBR-II

    International Nuclear Information System (INIS)

    Porter, D.L.; McVay, G.L.; Walters, L.C.

    1980-01-01

    The object of this study was to measure the stability of irradiation-induced microstructure upon annealing and, by selectively annealing out some of these features and reirradiating the material, it was expected that information could be gained concerning the role of microstructural changes in the void swelling process. Transmission electron microscopic examinations of isochronally annealed (200 to 1050 0 C) AISI 304L stainless steel, which had been irradiated at approximately 415 0 C to a fast (E > 0.1 MeV) neutron fluence of approximately 5.1 x 10 26 n/m 2 , verified that the two-stage hardness recovery with temperatures was related to a low temperature annealing of dislocation structures and a higher temperature annealing of voids and solute redistribution

  4. Impact of Defects in Powder Feedstock Materials on Microstructure of 304L and 316L Stainless Steel Produced by Additive Manufacturing

    Science.gov (United States)

    Morrow, Benjamin M.; Lienert, Thomas J.; Knapp, Cameron M.; Sutton, Jacob O.; Brand, Michael J.; Pacheco, Robin M.; Livescu, Veronica; Carpenter, John S.; Gray, George T.

    2018-05-01

    Recent work in both 304L and 316L stainless steel produced by additive manufacturing (AM) has shown that in addition to the unique, characteristic microstructures formed during the process, a fine dispersion of sub-micron particles, with a chemistry different from either the powder feedstock or the expected final material, are evident in the final microstructure. Such fine-scale features can only be resolved using transmission electron microscopy (TEM) or similar techniques. The present work uses electron microscopy to study both the initial powder feedstock and microstructures in final AM parts. Special attention is paid to the chemistry and origin of these nanoscale particles in several different metal alloys, and their impact on the final build. Comparisons to traditional, wrought material will be made.

  5. Measurement of carbon activity in sodium by Fe-Mn 20% alloy, and by strainless austenitic steel 304L and 316L

    International Nuclear Information System (INIS)

    Oberlin, C.; Saint Paul, P.; Baque, P.; Champeix, L.

    1980-01-01

    Precise knowledge of carbon activity in sodium used as coolant in fast breeder reactors, is essential for continuous survey of carburization-decarburization processes. Carbon activity can be periodically surveyed by measuring the carbon concentration or by hot trap like metal alloy strip placed in sodium loop. In fact, in equilibrium, activity of carbon in sodium is equal to the activity in metal alloy. Thus if the relation between concentration of carbon and it activity in the alloy is known, it is possible to estimate the activity of carbon in sodium. Materials to be used should have high solubility in carbon at the needed temperature. They should quickly attain equilibrium with sodium and they should not contain impurities that can affect the results. Materials chosen according to these criteria were Fe-Mn 20%, stainless austenitic steel AISI 304L and 316L

  6. Effect of martensitic phase transformation on the hardening behavior and texture evolution in a 304L stainless steel under compression at liquid nitrogen temperature

    Energy Technology Data Exchange (ETDEWEB)

    Cakmak, Ercan [Department of Materials Science and Engineering, The University of Tennessee, Knoxville, TN 37996 (United States); Vogel, Sven C. [Los Alamos Neutron Science Center, Los Alamos National Laboratory, Los Alamos, NM 87545 (United States); Choo, Hahn, E-mail: hchoo@utk.edu [Department of Materials Science and Engineering, The University of Tennessee, Knoxville, TN 37996 (United States)

    2014-01-01

    The martensitic phase transformation behavior and its relations with the macroscopic hardening rate and the evolutions in the crystallographic texture of the constituent phases were studied for a 304L stainless steel that exhibits the transformation induced plasticity (TRIP) phenomenon. Time-of-flight neutron diffraction was used to measure the evolutions of phase fractions and texture in terms of pole figures as a function of the applied compressive strain at the liquid nitrogen temperature (77 K). The phase transformation analyses show that the hcp-martensite phase fraction reaches a significant level of about 22 wt% at 15% applied strain and remains constant. The bcc-martensite phase fraction increases continuously with the deformation that correlates well with the macroscopic hardening behavior. Furthermore, the texture analyses show that transformation has dominant effect on the bcc-martensite texture evolution with little influence from subsequent plastic deformation at current testing conditions.

  7. Effect of martensitic phase transformation on the hardening behavior and texture evolution in a 304L stainless steel under compression at liquid nitrogen temperature

    International Nuclear Information System (INIS)

    Cakmak, Ercan; Vogel, Sven C.; Choo, Hahn

    2014-01-01

    The martensitic phase transformation behavior and its relations with the macroscopic hardening rate and the evolutions in the crystallographic texture of the constituent phases were studied for a 304L stainless steel that exhibits the transformation induced plasticity (TRIP) phenomenon. Time-of-flight neutron diffraction was used to measure the evolutions of phase fractions and texture in terms of pole figures as a function of the applied compressive strain at the liquid nitrogen temperature (77 K). The phase transformation analyses show that the hcp-martensite phase fraction reaches a significant level of about 22 wt% at 15% applied strain and remains constant. The bcc-martensite phase fraction increases continuously with the deformation that correlates well with the macroscopic hardening behavior. Furthermore, the texture analyses show that transformation has dominant effect on the bcc-martensite texture evolution with little influence from subsequent plastic deformation at current testing conditions

  8. Simulation and experimental comparison of the thermo-mechanical history and 3D microstructure evolution of 304L stainless steel tubes manufactured using LENS

    Science.gov (United States)

    Johnson, Kyle L.; Rodgers, Theron M.; Underwood, Olivia D.; Madison, Jonathan D.; Ford, Kurtis R.; Whetten, Shaun R.; Dagel, Daryl J.; Bishop, Joseph E.

    2018-05-01

    Additive manufacturing enables the production of previously unachievable designs in conjunction with time and cost savings. However, spatially and temporally fluctuating thermal histories can lead to residual stress states and microstructural variations that challenge conventional assumptions used to predict part performance. Numerical simulations offer a viable way to explore the root causes of these characteristics, and can provide insight into methods of controlling them. Here, the thermal history of a 304L stainless steel cylinder produced using the Laser Engineered Net Shape process is simulated using finite element analysis (FEA). The resultant thermal history is coupled to both a solid mechanics FEA simulation to predict residual stress and a kinetic Monte Carlo model to predict the three-dimensional grain structure evolution. Experimental EBSD measurements of grain structure and in-process infrared thermal data are compared to the predictions.

  9. Influence of substrate bias voltage on the properties of TiO{sub 2} deposited by radio-frequency magnetron sputtering on 304L for biomaterials applications

    Energy Technology Data Exchange (ETDEWEB)

    Bait, L. [Division Milieux Ionisés et Lasers, Centre de Développement des Technologies Avancées, CDTA,Cité du 20 aout 1956, Baba Hassen, BP n°. 17, Alger (Algeria); Azzouz, L. [Université de Amar Telidji, Laghouat (Algeria); Madaoui, N. [Division Milieux Ionisés et Lasers, Centre de Développement des Technologies Avancées, CDTA,Cité du 20 aout 1956, Baba Hassen, BP n°. 17, Alger (Algeria); Saoula, N., E-mail: nsaoula@cdta.dz [Division Milieux Ionisés et Lasers, Centre de Développement des Technologies Avancées, CDTA,Cité du 20 aout 1956, Baba Hassen, BP n°. 17, Alger (Algeria)

    2017-02-15

    Highlights: • TiO{sub 2} films were deposited on stainless steel 304L RF magnetron sputtering at different substrate bias. • The hardness of TiO{sub 2} coated 304L are higher than those obtained for uncoated substrate. • TiO{sub 2} films provide good protection for stainless steel against corrosion in Ringer solution. - Abstract: The aim of this paper is to investigate the effect of the substrate bias, varied from 0 to −100 V, on the structure and properties of the TiO{sub 2} thin films for biomaterials applications. The TiO{sub 2} films were grown onto 304L stainless steel substrate using radio-frequency (rf) magnetron sputtering from a pure titanium target in Ar-O{sub 2} gas mixture. The variation of substrate bias voltage from 0 to −100 V produces variations of structure and mechanical properties of the films. The deposited films were characterized by X-rays diffraction, nanoindentation and potentiodynamic polarization. Also, the friction and wear properties of TiO{sub 2} films sliding against alumina ball in air were investigated. Experimental results showed that the thickness increases for non-biased substrate voltage to Vs = −100 V from 820 nm to 1936 nm respectively. The roughness is in the range of 50 nm and 14 nm. XRD results show that all structures of the films are crystalline and changed with varying the bias voltage. The anatase phase is predominant in the low negative bias range (0–50 V). The hardness significantly increased from 2.2 to 6.4 GPa when the bias voltage was increased from 0 to 75 V and then slightly decrease to 5.1 GPa as further increased to 100 V. At the same time, the results indicate that TiO{sub 2} films deposited at −100 V exhibited better wear resistance compared to the other samples, i.e. the minimum wear rates and the lower coefficient of friction of 0.16. In order to simulate natural biological conditions, physiological serum (pH = 6.3), thermostatically controlled at 37 °C, was used as the electrolyte for the

  10. Influence of substrate bias voltage on the properties of TiO2 deposited by radio-frequency magnetron sputtering on 304L for biomaterials applications

    International Nuclear Information System (INIS)

    Bait, L.; Azzouz, L.; Madaoui, N.; Saoula, N.

    2017-01-01

    Highlights: • TiO 2 films were deposited on stainless steel 304L RF magnetron sputtering at different substrate bias. • The hardness of TiO 2 coated 304L are higher than those obtained for uncoated substrate. • TiO 2 films provide good protection for stainless steel against corrosion in Ringer solution. - Abstract: The aim of this paper is to investigate the effect of the substrate bias, varied from 0 to −100 V, on the structure and properties of the TiO 2 thin films for biomaterials applications. The TiO 2 films were grown onto 304L stainless steel substrate using radio-frequency (rf) magnetron sputtering from a pure titanium target in Ar-O 2 gas mixture. The variation of substrate bias voltage from 0 to −100 V produces variations of structure and mechanical properties of the films. The deposited films were characterized by X-rays diffraction, nanoindentation and potentiodynamic polarization. Also, the friction and wear properties of TiO 2 films sliding against alumina ball in air were investigated. Experimental results showed that the thickness increases for non-biased substrate voltage to Vs = −100 V from 820 nm to 1936 nm respectively. The roughness is in the range of 50 nm and 14 nm. XRD results show that all structures of the films are crystalline and changed with varying the bias voltage. The anatase phase is predominant in the low negative bias range (0–50 V). The hardness significantly increased from 2.2 to 6.4 GPa when the bias voltage was increased from 0 to 75 V and then slightly decrease to 5.1 GPa as further increased to 100 V. At the same time, the results indicate that TiO 2 films deposited at −100 V exhibited better wear resistance compared to the other samples, i.e. the minimum wear rates and the lower coefficient of friction of 0.16. In order to simulate natural biological conditions, physiological serum (pH = 6.3), thermostatically controlled at 37 °C, was used as the electrolyte for the study of the electrochemical properties

  11. Studies on mechanical properties, microstructure and fracture morphology details of laser beam welded thick SS304L plates for fusion reactor applications

    Energy Technology Data Exchange (ETDEWEB)

    Buddu, Ramesh Kumar, E-mail: buddu@ipr.res.in [Fusion Reactor Materials Development and Characterization Division, Institute for Plasma Research, Bhat, Gandhinagar 382428 (India); Chauhan, N.; Raole, P.M. [Fusion Reactor Materials Development and Characterization Division, Institute for Plasma Research, Bhat, Gandhinagar 382428 (India); Natu, Harshad [Magod Laser Machining Pvt. Ltd, Jigani, Bengaluru 560105 (India)

    2015-06-15

    Highlights: • CO{sub 2} laser welding of 8 mm thick SS304L plates has been carried out and full penetration welds fabricated and characterized for mechanical properties and microstructure details. • Welded samples have shown tensile properties comparable to base indicating good weld quality joints. • Impact fracture tests of weld zone and heat affected zone samples have shown poor toughness compared to the base metal. • SEM analysis of fracture samples of tensile and impact specimens indicated the complex microstructure features in weld zone and combined ductile and brittle fracture features. • Combined features of dendrite and cellular structures are observed in weld microstructures with narrow HAZ and delta ferrite is found in the welds and further confirmed by higher Ferrite Number data. - Abstract: Austenitic stainless steel is widely used structural material for the fabrication of the fusion reactor components. Laser welding is high power density process which offers several advantages over the other conventional processes like Tungsten Inert Gas welding. The features like low distortion, narrow heat affected zone, deep penetration in single pass, good mechanical properties are some of the advantages of laser welding process. The laser weld process parameters optimization has several challenges in terms of overcoming the weld defects like voids due to lack of penetration over depth, undercuts and porosity. The present paper reports the studies carried out with CO{sub 2} laser welding of 8 mm thick austenitic stainless steel SS304L plates and their characterization of mechanical properties, microstructure and fracture morphology details. The weld process parameter optimization towards defect free welds with full penetration welding has been carried out. The welded samples have shown tensile properties comparable to base metal, bend tests are successfully passed. The hardness measurements have shown slightly higher for weld zone compared to base metal

  12. Studies on mechanical properties, microstructure and fracture morphology details of laser beam welded thick SS304L plates for fusion reactor applications

    International Nuclear Information System (INIS)

    Buddu, Ramesh Kumar; Chauhan, N.; Raole, P.M.; Natu, Harshad

    2015-01-01

    Highlights: • CO 2 laser welding of 8 mm thick SS304L plates has been carried out and full penetration welds fabricated and characterized for mechanical properties and microstructure details. • Welded samples have shown tensile properties comparable to base indicating good weld quality joints. • Impact fracture tests of weld zone and heat affected zone samples have shown poor toughness compared to the base metal. • SEM analysis of fracture samples of tensile and impact specimens indicated the complex microstructure features in weld zone and combined ductile and brittle fracture features. • Combined features of dendrite and cellular structures are observed in weld microstructures with narrow HAZ and delta ferrite is found in the welds and further confirmed by higher Ferrite Number data. - Abstract: Austenitic stainless steel is widely used structural material for the fabrication of the fusion reactor components. Laser welding is high power density process which offers several advantages over the other conventional processes like Tungsten Inert Gas welding. The features like low distortion, narrow heat affected zone, deep penetration in single pass, good mechanical properties are some of the advantages of laser welding process. The laser weld process parameters optimization has several challenges in terms of overcoming the weld defects like voids due to lack of penetration over depth, undercuts and porosity. The present paper reports the studies carried out with CO 2 laser welding of 8 mm thick austenitic stainless steel SS304L plates and their characterization of mechanical properties, microstructure and fracture morphology details. The weld process parameter optimization towards defect free welds with full penetration welding has been carried out. The welded samples have shown tensile properties comparable to base metal, bend tests are successfully passed. The hardness measurements have shown slightly higher for weld zone compared to base metal and the

  13. Characterization and study of mechanical and tribological properties on titanium di oxide (TiO2) coated 304L stainless steel

    Science.gov (United States)

    Ghanaraja, S.; Ali, Syed Imran; Ravikumar, K. S.; Likith, P.

    2018-04-01

    In the present investigation Atmospheric Plasma Spraying (APS) method is selected for coating the materials on 304L Stainless Steel as a substrate material, also called as substrate of Thermal Barrier Coating (TBC) system developed in the present work. Commercially available Ni-Cr metal powder is selected for bond coat and TiO2 powder is selected for Top Coat. The thickness of bond coat is taken as 75 µm where as the top coat thickness is varied as 100 µm, 200 µm and 300 µm. In plasma sprayed coating more attention is given to obtain uniform thickness on the given substrate. The various surface texture parameters of each sample is tested, morphology and coating thickness of above TBC system are studied with the help of SEM and X-Ray Diffraction for phase analysis. Micro-hardness of each layer of coating is measured by using Vicker's diamond indentation and the abrasive wear resistance of each system has been investigated through Pin-on-disc test, at room temperature by using wear and friction tribometer. The coating system possesses good wear resistance and can be used in various applications.

  14. An Investigation into Stress Corrosion Cracking of Dissimilar Metal Welds with 304L Stainless Steel and Alloy 82 in High Temperature Pure Water

    Science.gov (United States)

    Yeh, Tsung-Kuang; Huang, Guan-Ru; Tsai, Chuen-Horng; Wang, Mei-Ya

    For a better understanding toward stress corrosion cracking (SCC) in dissimilar metal welds with 304L stainless steel and Alloy 82, the SCC growth behavior in the transition regions of weld joints was investigated via slow strain rate tensile (SSRT) tests in 280 oC pure water with a dissolve oxygen level of 300 ppb. Prior to the SSRT tests, samples with dissimilar metal welds were prepared and underwent various pretreatments, including post-weld heat treatment (PWHT), shot peening, solution annealing, and mechanical grinding. In addition to the SSRT tests, measurements of degree of sensitization and micro-hardness on the transition regions of the metal welds were also conducted. According to the test results, the samples having undergone PWHTs exhibited relatively high degrees of sensitization. Distinct decreases in hardness were observed in the heat-affected zones of the base metals in all samples. Furthermore, the fracture planes of all samples after the SSRT tests were located at the stainless steel sides and were in parallel with the fusion lines. Among the treating conditions investigated in this study, a PWHT would pose a detrimental effect on the samples in the aspects of mechanical property and degree of SCC. Solution annealing would lead to the greatest improvement in ductility and SCC retardation, and shot peening would provide the treated samples with a positive improvement in ductility and corrosion retardation, but not to a great extent.

  15. In situ neutron diffraction study of grain-orientation-dependent phase transformation in 304L stainless steel at a cryogenic temperature

    International Nuclear Information System (INIS)

    Tao Kaixiang; Wall, James J.; Li, Hongqi; Brown, Donald W.; Vogel, Sven C.; Choo, Hahn

    2006-01-01

    In situ time-of-flight neutron diffraction was performed to investigate the martensitic phase transformation during quasistatic uniaxial compression testing of 304L stainless steel at 300 and 203 K. In situ neutron diffraction enabled the bulk measurement of intensity evolution for various hkl atomic planes during the austenite (fcc) to martensite (hcp and bcc) phase transformation. Based on the neutron diffraction patterns, the martensite phases were observed from the very beginning of the plastic deformation at 203 K. However, at 300 K, no newly formed martensite, except a small amount of preexisting hcp phase, was observed throughout the test. From the changes in the relative intensities of individual hkl atomic planes, the grain-orientation-dependent phase transformation was investigated. The preferred orientation of the newly formed martensite grains was also investigated for the sample deformed at 203 K using neutron diffraction. The results reveal the orientation relationships between the austenite and the newly formed martensites. The fcc grain family diffracting with (200) plane normal parallel to the loading axis is favored for the fcc to bcc transformation and the bcc (200) plane normals are primarily aligned along the loading direction. For the fcc to hcp transformation, the fcc grains with (111) plane normals at an angle in between about 10 deg. and 50 deg. to the loading direction are favored

  16. Superficial and electrochemical study of stainless steel 304l with an inhibitory protective coating (TiO2 and ZrO2)

    International Nuclear Information System (INIS)

    Davila N, M. L.; Contreras R, A.; Arganis J, C. R.

    2014-10-01

    The degradation mechanisms in the boiling water reactors (BWR) have been an alert focus for owners, especially the cracking by stress corrosion cracking (SCC), therefore different techniques have been studied to inhibit this problem inside which is the water injection of hydrogen feeding (HWC, Hydrogen Water Chemistry), together with the noble metals injection (NMCA, Nobel Metal Chemical Addition) and the ceramic materials injection that form an inhibitory protective coating (Ipc). In this work the Ipc was simulated, for which were carried out hydro-thermals deposits starting from suspensions of 1000 ppm of zirconium oxide in its crystalline phase baddeleyite and titanium oxides in its anatase and rutile phases, on test tubes of stainless steel 304l previously rusty under simulated conditions of pressure and temperature of a BWR (288 C and 8 MPa). The superficial characterization was realized by scanning electron microscopy, energy-dispersive of X-ray and X-ray diffraction. The capacity to mitigate the corrosion was studied with the electrochemical technique of Tafel polarization (288 C and 8 MPa). The steel presents the formation of two oxide coatings formed by magnetite and hematite. The baddeleyite presents a deposit more thick and homogeneous it also presents the most negative electrochemical potential of corrosion, what indicates that it has the bigger capacity to mitigate the SCC. (Author)

  17. On the ability of some cyclic plasticity models to predict the evolution of stored energy in a type 304L stainless steel submitted to high cycle fatigue

    International Nuclear Information System (INIS)

    Vincent, L.

    2008-01-01

    Fatigue analyses of materials are generally based on a so-called stabilized cycle, on which plastic strain amplitude, plastic energy, maximum shear stress and so on are determined. The part of plastic energy which is dissipated in heat cannot be used to accumulate damage and it should be worthwhile extracting only the part of plastic energy which is stored in material microstructure in order to build a consistent damage model. In this paper, some cyclic plasticity models including a polycrystalline model are reformulated in the thermodynamic framework in order to test their capacity to predict both the stress-strain behaviour and the partition of plastic energy for a high cycle fatigue test on a type 304L stainless steel. For an equivalent description of stress-strain loops, the number of kinematic hardening variables chosen in a model may qualitatively alter the prediction of plastic energy partition due to the modification of the isotropic hardening variable. Measurements of the specimen temperature increase due to plastic dissipation is therefore proposed as a convenient complementary experimental data to identify the constitutive equation of the isotropic hardening variable of a cyclic plasticity model. (author)

  18. Thermal fatigue of a 304L austenitic stainless steel: simulation of the initiation and of the propagation of the short cracks in isothermal and aniso-thermal fatigue

    International Nuclear Information System (INIS)

    Haddar, N.

    2003-04-01

    The elbow pipes of thermal plants cooling systems are submitted to thermal variations of short range and of variable frequency. These variations bound to temperature changes of the fluids present a risk of cracks and leakages. In order to solve this problem, EDF has started the 'CRECO RNE 808' plan: 'thermal fatigue of 304L austenitic stainless steels' to study experimentally on a volume part, the initiation and the beginning of the propagation of cracks in thermal fatigue on austenitic stainless steels. The aim of this study is more particularly to compare the behaviour and the damage of the material in mechanic-thermal fatigue (cycling in temperature and cycling in deformation) and in isothermal fatigue (the utmost conditions have been determined by EDF for the metal: Tmax = 165 degrees C and Tmin = 90 degrees C; the frequency of the thermal variations can reach a Hertz). A lot of experimental results are given. A model of lifetime is introduced and validated. (O.M.)

  19. Formation of abrasion-resistant coatings of the AlSiFe{sub x}Mny intermetallic compound type on the AISI 304L alloy

    Energy Technology Data Exchange (ETDEWEB)

    Martinez-Peralez, L. G.; Flores-Valdes, A.; Salinas-Rodriguez, A.; Ochoa-Palacios, R. M.; Toscano-giles, J. A.; Torres-Torres, J.

    2016-05-01

    The α-Al{sub 9}FeMnSi and α-Al{sub 9}FeMn{sub 2}Si intermetallics formed by reactive sintering of Al, Si, Mn, Fe, Cr and Ni powders have been used in AISI 304L steels to enhance microhardness. Processing variables of the reactive sintering treatment were temperature (600, 650, 700, 750 and 800 degree centigrade), pressure (5, 10 y 20 MPa) and holding time (3600, 5400 y 7200 seconds). Experimental results show that temperature is the most important variable affecting the substrate/coating formation, while pressure does not appear to have a significant effect. The results show the optimum conditions of the reactive sintering that favor the substrate/coating formation are 800 degree centigrade, 20 MPa and 7200 seconds. Under these conditions, the reaction zone between the substrate and coating is more compacted and well-adhered, with a microhardness of 1300 Vickers. The results of SEM and X-Ray diffraction confirmed the formation of β-Al{sub 9}FeMnSi and β-Al{sub 9}FeMn{sub 2}Si intermetallics in the substrate/coating interface as well as the presence of Cr and Ni, indicating diffusion of these two elements from the substrate to the interface. (Author)

  20. Transformaciones Microestructurales en Soldaduras Disímiles de Acero Inoxidable Austenítico con Acero Inoxidable Ferrítico

    Directory of Open Access Journals (Sweden)

    Sara María Aguilar-Sierra

    2015-03-01

    Full Text Available En este trabajo se estudian los fenómenos metalúrgicos que ocurren en la soldadura SMAW de un acero inoxidable ferrítico AISI 430 con un acero inoxidable austenítico AISI 316L. Para el estudio se utilizaron dos tipos de electrodos: austenítico AWS E309L y dúplex AWS E2209-16, ambos con un diámetro de 3,2 mm. Las uniones soldadas se realizaron con un solo pase y se variaron simultáneamente la corriente y la velocidad de soldadura; las condiciones fueron 49 A y 2,4 mm.s–1como valores bajos y 107 A y 4,3 mm.s–1como valores altos. Se evaluó la influencia del tipo de electrodo y de los parámetros de soldadura en la evolución microestructural de las zonas afectadas por el calor y de las zonas de fusión, encontrando diferencias en la morfología y cantidad de ferrita delta para todas las condiciones estudiadas. Se evidenció crecimiento y refinación de grano ferrítico y formación de martensita en la zona afectada por el calor del metal base ferrítico. Se evaluó también la resistencia a la tensión hallando similitudes en todas las soldaduras.

  1. Formation of abrasion-resistant coatings of the AlSiFexMny intermetallic compound type on the AISI 304L alloy

    Directory of Open Access Journals (Sweden)

    Martínez-Perales, Laura G.

    2016-03-01

    Full Text Available The α-Al9FeMnSi and β-Al9FeMn2Si intermetallics formed by reactive sintering of Al, Si, Mn, Fe, Cr and Ni powders have been used in AISI 304L steels to enhance microhardness. Processing variables of the reactive sintering treatment were temperature (600, 650, 700, 750 and 800 °C, pressure (5, 10 y 20 MPa and holding time (3600, 5400 y 7200 seconds. Experimental results show that temperature is the most important variable affecting the substrate/coating formation, while pressure does not appear to have a significant effect. The results show the optimum conditions of the reactive sintering that favor the substrate/coating formation are 800 °C, 20 MPa and 7200 seconds. Under these conditions, the reaction zone between the substrate and coating is more compacted and well-adhered, with a microhardness of 1300 Vickers. The results of SEM and X-Ray diffraction confirmed the formation of α-Al9FeMnSi and β-Al9FeMn2Si intermetallics in the substrate/coating interface as well as the presence of Cr and Ni, indicating diffusion of these two elements from the substrate to the interface.Los intermetálicos α-Al9FeMnSi y β-Al9FeMn2Si formados por sinterización reactiva de polvos Al, Si, Mn, Fe, Cr, Ni se han utilizado en aceros AISI 304L para mejorar la microdureza. Las variables de procesamiento de sinterización reactiva fueron temperatura (600, 650, 700, 750, y 800 °C, presión (5, 10 y 20 MPa y el tiempo de retención (3600, 5400 7200 segundos. Los resultados experimentales muestran que la temperatura es la variable más importante que afecta a la formación del sustrato/recubrimiento, mientras que la presión no parece tener un efecto significativo una influencia significativa. Los resultados muestran las condiciones óptimas de la sinterización reactiva que favorecen la formación del sustrato/recubrimiento a 800 °C, 20 MPa y 7200 segundos. En estas condiciones, la zona de reacción entre el sustrato y el recubrimiento es más compacta y bien

  2. Study on the Effect of Laser Welding Parameters on the Microstructure and Mechanical Properties of Ultrafine Grained 304L Stainless Steel

    Directory of Open Access Journals (Sweden)

    Reihane Nafar Dehsorkhi

    2016-12-01

    Full Text Available In the present study, an ultrafine grained (UFG 304L stainless steel with the average grain size of 300 nm was produced by a combination of cold rolling and annealing. Weldability of the UFG sample was studied by Nd: YAG laser welding under different welding conditions. Taguchi experimental design was used to optimize the effect of frequency, welding time, laser current and laser pulse duration on the resultant microstructure and mechanical properties. X-ray Diffraction (XRD, Optical Microscope (OM, Scanning Electron Microscope (SEM, Transmission Electron Microscope (TEM, microhardness measurements and tension tests were conducted to characterize the sample after thermomechanical processing and laser welding. The results showed that the ultrafine grained steel had the yield strength of 1000 Mpa and the total elongation of 48%, which were almost three times higher than those of the as-received sample. The microstructure of the weld zone was shown to be a mixture of austenite and delta ferrite. The microhardness of the optimized welded sample (315 HV0.5 was found to be close to the UFG base metal (350 HV. It was also observed that the hardness of the heat affected zone (HAZ was  lower than that of the weld zone, which was related to the HAZ grain growth during laser welding. The results of optimization also showed that the welding time was the most important parameter affecting the weld strength. Overall, the study showed that laser welding could be an appropriate and alternative welding technique for the joining of UFG steels.

  3. Estudio de la corrosión producida en aceros inoxidables 304 en procesos de soldadura

    Directory of Open Access Journals (Sweden)

    G. Terán

    2004-01-01

    Full Text Available En este trabajo de investigación se analizan las probetas de aceros inoxidables 304 que después de haber sido soldadas mediante los procesos de soldadura SMAW, GMAW y GTAW, se sometieron a un ambiente corrosivo propio de las condiciones de trabajo. Se estudió la microestructura del cordón de soldadura utilizando microscopía electrónica de barrido (SEM, la interfase entre el material base y el de aporte se estudió utilizando un microscopio óptico y analizador de imágenes.

  4. Influence of substrate bias voltage on the properties of TiO2 deposited by radio-frequency magnetron sputtering on 304L for biomaterials applications

    Science.gov (United States)

    Bait, L.; Azzouz, L.; Madaoui, N.; Saoula, N.

    2017-02-01

    The aim of this paper is to investigate the effect of the substrate bias, varied from 0 to -100 V, on the structure and properties of the TiO2 thin films for biomaterials applications. The TiO2 films were grown onto 304L stainless steel substrate using radio-frequency (rf) magnetron sputtering from a pure titanium target in Ar-O2 gas mixture. The variation of substrate bias voltage from 0 to -100 V produces variations of structure and mechanical properties of the films. The deposited films were characterized by X-rays diffraction, nanoindentation and potentiodynamic polarization. Also, the friction and wear properties of TiO2 films sliding against alumina ball in air were investigated. Experimental results showed that the thickness increases for non-biased substrate voltage to Vs = -100 V from 820 nm to 1936 nm respectively. The roughness is in the range of 50 nm and 14 nm. XRD results show that all structures of the films are crystalline and changed with varying the bias voltage. The anatase phase is predominant in the low negative bias range (0-50 V). The hardness significantly increased from 2.2 to 6.4 GPa when the bias voltage was increased from 0 to 75 V and then slightly decrease to 5.1 GPa as further increased to 100 V. At the same time, the results indicate that TiO2 films deposited at -100 V exhibited better wear resistance compared to the other samples, i.e. the minimum wear rates and the lower coefficient of friction of 0.16. In order to simulate natural biological conditions, physiological serum (pH = 6.3), thermostatically controlled at 37 °C, was used as the electrolyte for the study of the electrochemical properties. Comparison between the corrosion resistance of the uncoated and coated samples showed a reduction in corrosion current density for coated samples compared to the uncoated one. The best corrosion current density of the film deposited at -75 V was 5.9 nA/cm2, which is about 11 times less than that of the uncoated steel 68.3 nA/cm2). The

  5. Initiation and growth of thermal fatigue crack networks in an AISI 304 L type austenitic stainless steel (X2 CrNi18-09)

    International Nuclear Information System (INIS)

    Maillot, V.

    2004-01-01

    We studied the behaviour of a 304 L type austenitic stainless steel submitted to thermal fatigue. Using the SPLASH equipment of CEA/SRMA we tested parallelepipedal specimens on two sides: the specimens are continuously heated by Joule effect, while two opposites faces are cyclically. cooled by a mixed spray of distilled water and compressed air. This device allows the reproduction and the study of crack networks similar to those observed in nuclear power plants, on the inner side of circuits fatigued by mixed pressurized water flows at different temperatures. The crack initiation and the network constitution at the surface were observed under different thermal conditions (Tmax = 320 deg C, ΔT between 125 and 200 deg C). The experiment produced a stress gradient in the specimen, and due to this gradient, the in-depth growth of the cracks finally stopped. The obtained crack networks were studied quantitatively by image analysis, and different parameters were studied: at the surface during the cycling, and post mortem by step-by-step layer removal by grinding. The maximal depth obtained experimentally, 2.5 mm, is relatively coherent with the finite element modelling of the SPLASH test, in which compressive stresses appear at a depth of 2 mm. Some of the crack networks obtained by thermal fatigue were also tested in isothermal fatigue crack growth under 4-point bending, at imposed load. The mechanisms of the crack selection, and the appearance of the dominating crack are described. Compared to the propagation of a single crack, the crack networks delay the propagation, depending on the severity of the crack competition for domination. The dominating crack can be at the network periphery, in that case it is not as shielded by its neighbours as a crack located in the center of the network. It can also be a straight crack surrounded by more sinuous neighbours. Indeed, on sinuous cracks, the loading is not the same all along the crack path, leading to some morphological

  6. Investigation of high temperature phase stability, thermal properties and evaluation of metallurgical compatibility with 304L stainless steel, of indigenously developed ferroboron alternate shielding material for fast reactor applications

    Energy Technology Data Exchange (ETDEWEB)

    Rai, Arun Kumar [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam, 603102 (India); Raju, S., E-mail: sraju@igcar.gov.in [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam, 603102 (India); Jeya Ganesh, B. [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam, 603102 (India); Panneerselvam, G. [Chemistry Group, Indira Gandhi Centre for Atomic Research, Kalpakkam, 603102 (India); Vijayalakshmi, M.; Jayakumar, T. [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam, 603102 (India); Raj, Baldev [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam, 603102 (India); Chemistry Group, Indira Gandhi Centre for Atomic Research, Kalpakkam, 603102 (India)

    2011-08-15

    Highlights: > High temperature phase stability and metallurgical compatibility of indigenous Ferro boron alloy (17 wt.%) with 304L SS have been evaluated using calorimetry, metallography and X-ray diffraction. > Fe-B is stable upto 1227 deg. C without any phase transformation. > In combination with SS 304L, it develops an eutectic reaction at 1198 deg. C. > High temperature metallurgical interaction between Ferroboron and 304L SS clad has been simulated for temperatures 550-800 deg. C for reaction times up to 5000 h, using diffusion couple. > Clad penetration depth with time follows a paraobolic rate law. - Abstract: Towards the cause of serving economic power production through fast reactors, it is necessary to bring in functionally more efficient and innovative design options, which also includes exploration of cheaper material alternatives, wherever possible. In this regard, the feasibility of using a commercial grade ferroboron alloy as potential alternate shielding material in the outer subassemblies of future Indian fast reactors has been recently investigated from shielding physics point of view. The present study explores in detail the high temperature thermal stability and the metallurgical compatibility of Fe-15.4B-0.3C-0.89Si-0.17Al-0.006S-0.004P-0.003O (wt.%) alloy with SS 304L material. In addition, the high temperature specific heat and lattice thermal expansion characteristics of this alloy have also been investigated as a part of the present comprehensive characterisation program. The Fe-15 wt.%B alloy is constituted of principally of two boride phases, namely tetragonal Fe{sub 2}B and orthorhombic FeB phases, which in addition to boron also contains some amount of C and Si dissolved in solid solution form. This Fe-B alloy undergoes a series of phase transformation as a function of increasing temperature; the major ones among them are the dissolution of Fe{sub 2}B-lower boride in the matrix through a eutectic type reaction, which results in the

  7. Thermal fatigue of a 304L austenitic stainless steel: simulation of the initiation and of the propagation of the short cracks in isothermal and aniso-thermal fatigue; Fatigue thermique d'un acier inoxydable austenitique 304L: simulation de l'amorcage et de la croissance des fissures courtes en fatigue isotherme et anisotherme

    Energy Technology Data Exchange (ETDEWEB)

    Haddar, N

    2003-04-01

    The elbow pipes of thermal plants cooling systems are submitted to thermal variations of short range and of variable frequency. These variations bound to temperature changes of the fluids present a risk of cracks and leakages. In order to solve this problem, EDF has started the 'CRECO RNE 808' plan: 'thermal fatigue of 304L austenitic stainless steels' to study experimentally on a volume part, the initiation and the beginning of the propagation of cracks in thermal fatigue on austenitic stainless steels. The aim of this study is more particularly to compare the behaviour and the damage of the material in mechanic-thermal fatigue (cycling in temperature and cycling in deformation) and in isothermal fatigue (the utmost conditions have been determined by EDF for the metal: Tmax = 165 degrees C and Tmin = 90 degrees C; the frequency of the thermal variations can reach a Hertz). A lot of experimental results are given. A model of lifetime is introduced and validated. (O.M.)

  8. Behavior to the fracture of an AISI 304 stainless steel sensitized in BWR reactor conditions (288 degrees Centigrade and 80 Kg/cm{sup 2}); Comportamiento a la fractura de un acero inoxidable AISI 304 sensibilizado en condiciones de reactor BWR (288 grados Centigrados y 80 Kg/cm{sup 2})

    Energy Technology Data Exchange (ETDEWEB)

    Hernandez C, R.; Diaz S, A.; Garcia R, R.; Aguilar T, A.; Gachuz M, M.; Arganis J, C.; Merino C, J. [Instituto Nacional de Investigaciones Nucleares, A.P. 18-1027, 11801 Mexico D.F. (Mexico)

    1999-07-01

    It is a knew fact that ductility of a lot of structural alloys can be deteriorated by the environment effect which are exposed, and that their consequent embrittlement can put in doubt the safety of their functioning; such is the case of austenitic stainless steels used in internal components of the BWR type reactors which not only is subjected to the effect combined of the aggressive environment which surround it (pressure, temperature, corrosion potential, conductivity medium, local state of efforts, etc.), but also to the action of present neutron radiation, manifesting microstructural changes which are reflected in the augmentation of its susceptibility to the intergranular cracking, phenomena generally known as IASCC ''Irradiation Assisted Stress Corrosion Cracking''. Once appeared the cracking in the material, the useful life of a component is limited by the rapidity to growth of these cracking, making necessary evaluations which can to predict its behavior, therefore the present work shows the preliminary results for determining the behavior to the fracture of an AISI 304 stainless steel sensitized, in a dynamic recirculation circuit which allows to simulate the operation conditions of a BWR reactor (288 Centigrade and 80 kg/cm{sup 2}). (Author)

  9. Correlation of radiation-induced changes in microstructure/microchemistry, density and thermo-electric power of type 304L and 316 stainless steels irradiated in the Phénix reactor

    Energy Technology Data Exchange (ETDEWEB)

    Renault Laborne, Alexandra, E-mail: alexandra.renault@cea.fr [CEA, DEN, SRMA, F-91191 Gif-sur-Yvette (France); Gavoille, Pierre [CEA, DEN, SEMI, F-91191 Gif-sur-Yvette (France); Malaplate, Joël [CEA, DEN, SRMA, F-91191 Gif-sur-Yvette (France); Pokor, Cédric [EDF R& D, MMC, Site des Renardières, F-77818 Morêt-sur-Loing cedex (France); Tanguy, Benoît [CEA, DEN, SEMI, F-91191 Gif-sur-Yvette (France)

    2015-05-15

    Annealed specimens of type 304L and 316 stainless steel and cold-worked 316 specimens were irradiated in the Phénix reactor in the temperature range 381–394 °C and to different damage doses up to 39 dpa. The microstructure and microchemistry of both 304L and 316 have been examined using the combination of the different techniques of TEM to establish the void swelling and precipitation behavior under neutron irradiation. TEM observations are compared with results of measurements of immersion density and thermo-electric power obtained on the same irradiated stainless steels. The similarities and differences in their behavior on different scales are used to understand the factors in terms of the chemical composition and metallurgical state of steels, affecting the precipitation under irradiation and the swelling behavior. Irradiation induces the formation of some precipitate phases (e.g., M{sub 6}C and M{sub 23}C{sub 6}-type carbides, and γ’- and G-phases), Frank loops and cavities. According to the metallurgical state and chemical composition of the steel, the amount of each type of radiation-induced defects is not the same, affecting their density and thermo-electric power.

  10. Correlation of radiation-induced changes in microstructure/microchemistry, density and thermo-electric power of type 304L and 316 stainless steels irradiated in the Phénix reactor

    Science.gov (United States)

    Renault Laborne, Alexandra; Gavoille, Pierre; Malaplate, Joël; Pokor, Cédric; Tanguy, Benoît

    2015-05-01

    Annealed specimens of type 304L and 316 stainless steel and cold-worked 316 specimens were irradiated in the Phénix reactor in the temperature range 381-394 °C and to different damage doses up to 39 dpa. The microstructure and microchemistry of both 304L and 316 have been examined using the combination of the different techniques of TEM to establish the void swelling and precipitation behavior under neutron irradiation. TEM observations are compared with results of measurements of immersion density and thermo-electric power obtained on the same irradiated stainless steels. The similarities and differences in their behavior on different scales are used to understand the factors in terms of the chemical composition and metallurgical state of steels, affecting the precipitation under irradiation and the swelling behavior. Irradiation induces the formation of some precipitate phases (e.g., M6C and M23C6-type carbides, and γ'- and G-phases), Frank loops and cavities. According to the metallurgical state and chemical composition of the steel, the amount of each type of radiation-induced defects is not the same, affecting their density and thermo-electric power.

  11. Correlation of radiation-induced changes in microstructure/microchemistry, density and thermo-electric power of type 304L and 316 stainless steels irradiated in the Phénix reactor

    International Nuclear Information System (INIS)

    Renault Laborne, Alexandra; Gavoille, Pierre; Malaplate, Joël; Pokor, Cédric; Tanguy, Benoît

    2015-01-01

    Annealed specimens of type 304L and 316 stainless steel and cold-worked 316 specimens were irradiated in the Phénix reactor in the temperature range 381–394 °C and to different damage doses up to 39 dpa. The microstructure and microchemistry of both 304L and 316 have been examined using the combination of the different techniques of TEM to establish the void swelling and precipitation behavior under neutron irradiation. TEM observations are compared with results of measurements of immersion density and thermo-electric power obtained on the same irradiated stainless steels. The similarities and differences in their behavior on different scales are used to understand the factors in terms of the chemical composition and metallurgical state of steels, affecting the precipitation under irradiation and the swelling behavior. Irradiation induces the formation of some precipitate phases (e.g., M 6 C and M 23 C 6 -type carbides, and γ’- and G-phases), Frank loops and cavities. According to the metallurgical state and chemical composition of the steel, the amount of each type of radiation-induced defects is not the same, affecting their density and thermo-electric power

  12. AES depth profiles in Mo-coated 304L stainless steel achieved by RF-magnetron sputtering and influence of Mo on the corrosion in 3.5% NaCl solution

    Energy Technology Data Exchange (ETDEWEB)

    Saidi, D. [Département de métallurgie, Division de Technologie du Combustible, Centre de Recherche Nucléaire de Draria CRND, BP. 43 Draria, Alger (Algeria); Zaid, B., E-mail: zaidbachir@yahoo.com [Département de métallurgie, Division de Technologie du Combustible, Centre de Recherche Nucléaire de Draria CRND, BP. 43 Draria, Alger (Algeria); Souami, N. [Centre de Recherche Nucléaire d’Alger CRNA, 2 Bd. Frantz Fanon, Alger (Algeria); Saoula, N. [Division des Milieux Ionisés et Lasers, Centre de Développement des Technologies Avancées CDTA, Cité du 20 août 1956, Baba Hassan, BP n 17, Alger (Algeria); Siad, M. [Centre de Recherche Nucléaire d’Alger CRNA, 2 Bd. Frantz Fanon, Alger (Algeria); Si Ahmed, A. [Im2np, UMR 7334 CNRS, Aix-Marseille Université, 13397 Marseille Cedex 20 (France); Biberian, J.P. [CINaM, UMR 7525 CNRS, Aix Marseille Université, 13288 Marseille Cedex 9 (France)

    2015-10-05

    Highlights: • Mo coating of 304L stainless steel is achieved via RF-magnetron sputtering. • The AES depth profiles before and after annealing in air (at 973 K) are analyzed. • The corrosions in NaCl solution of bare and Mo-coated samples are compared. • Mo-coated steels exhibit better corrosion behaviors. • The positive action of Mo oxide via its semi-conducting properties is deduced. - Abstract: Molybdenum-coated 304L stainless steel samples, fabricated by RF-magnetron sputtering, are characterized by Auger Electron Spectroscopy (AES) before and after annealing in air at 973 K. The electrochemical parameters of bare and coated materials, in NaCl 3.5% water solution at 298 K, are derived from the potentiodynamic polarization curves. The corrosion current of Mo-coated samples (before and after annealing) is significantly lower than that of its bare counterpart. The information gained from the AES depth profiles leads us to infer that the positive action of molybdenum on the corrosion behavior may be attributed to the changes induced by the semi-conducting properties of Mo oxide in the passive film.

  13. El refractario en la fabricación de acero inoxidable

    Directory of Open Access Journals (Sweden)

    Ferrer, F. J.

    2006-10-01

    Full Text Available The influence of the steelmaking process on the quality and the performance of refractory materials used on stainless steel production was described. The most important technical and design parameters of the processing units were explained and related with the slag chemical composition and the qualities of the refractories used.

    Se describe la influencia del proceso siderúrgico sobre el tipo y rendimiento del material refractario utilizado en la producción de acero inoxidable. Tras describir las distintas unidades implicadas en el proceso metalúrgico se hace especial énfasis en la importancia que ejercen el diseño de las distintas unidades y el tipo y control de la escoria sobre la calidad del tipo de refractario a utilizar.

  14. Initiation and growth of thermal fatigue crack networks in an AISI 304 L type austenitic stainless steel (X2 CrNi18-09); Amorcage et propagation de reseaux de fissures de fatigue thermique dans un acier inoxydable austenitique de type X2 CrNi18-09 (AISI 304 L)

    Energy Technology Data Exchange (ETDEWEB)

    Maillot, V

    2004-07-01

    We studied the behaviour of a 304 L type austenitic stainless steel submitted to thermal fatigue. Using the SPLASH equipment of CEA/SRMA we tested parallelepipedal specimens on two sides: the specimens are continuously heated by Joule effect, while two opposites faces are cyclically. cooled by a mixed spray of distilled water and compressed air. This device allows the reproduction and the study of crack networks similar to those observed in nuclear power plants, on the inner side of circuits fatigued by mixed pressurized water flows at different temperatures. The crack initiation and the network constitution at the surface were observed under different thermal conditions (Tmax = 320 deg C, {delta}T between 125 and 200 deg C). The experiment produced a stress gradient in the specimen, and due to this gradient, the in-depth growth of the cracks finally stopped. The obtained crack networks were studied quantitatively by image analysis, and different parameters were studied: at the surface during the cycling, and post mortem by step-by-step layer removal by grinding. The maximal depth obtained experimentally, 2.5 mm, is relatively coherent with the finite element modelling of the SPLASH test, in which compressive stresses appear at a depth of 2 mm. Some of the crack networks obtained by thermal fatigue were also tested in isothermal fatigue crack growth under 4-point bending, at imposed load. The mechanisms of the crack selection, and the appearance of the dominating crack are described. Compared to the propagation of a single crack, the crack networks delay the propagation, depending on the severity of the crack competition for domination. The dominating crack can be at the network periphery, in that case it is not as shielded by its neighbours as a crack located in the center of the network. It can also be a straight crack surrounded by more sinuous neighbours. Indeed, on sinuous cracks, the loading is not the same all along the crack path, leading to some

  15. Efectos gammágenos del cobre en los aceros inoxidables 18Cr8Ni

    Directory of Open Access Journals (Sweden)

    Botella, J.

    1997-10-01

    Full Text Available From a series of 22 typical 18Cr8Ni stainless steel 40 kg ingots, with copper variable concentrations from 0.6 to 3.0 weight %, δ-ferrite is measured with a ferrite-meter device, calculating a nickel equivalent of 0.27 for copper. Some differences between the 8-ferrite and that on calculated by DeLong -excluding the copper γ-gene action- have been found because of different solidification and cooling regimes in ingot and weld cases.

    A partir de una serie de 22 lingotes de 40 kg de aceros inoxidables típicos 18Cr8Ni, con concentraciones variables de cobre entre 0,6 y 3,0 % en masa, se mide la ferrita δ mediante un medidor de ferrita y se deduce para el cobre un equivalente en níquel de 0,27, a la vez que se establecen ciertas diferencias entre los contenidos de ferrita δ medida y la deducida según DeLong -excluida la acción gammágena del cobre- por el hecho de solidificar en lingotes en vez de la típica solidificación de soldaduras.

  16. Caracterización termomecánica de aceros inoxidables austeníticos AISI-304

    OpenAIRE

    El Wahabi, Mohammed

    2003-01-01

    El control de la microestructura necesita la optimización de las condiciones del conformado en caliente. La recristalización dinámica es el fenómeno protagonista durante un proceso termomecánico, por lo que tiene un interés industrial, permitiendo mejorar las propiedades mecánicas de los aceros inoxidables mediante el afinamiento de grano, y al mismo tiempo aumentar la resistencia a la fragilización y a la corrosión. El objetivo principal de este trabajo es estudiar el comportamiento termomec...

  17. Fabricación aditiva mediante sinterizado láser de polvos de acero inoxidable martensítico AISI 420

    OpenAIRE

    Vega Nava, Sergio

    2014-01-01

    Busqueda de los parámetros de fabricación adecuados y los tratamientos térmicos a realizar, con el fin de alcanzar durezas de 50 HRC y una adecuada porosidad, en el acero inoxidable AISI 420 obtenido mediante sinterizado láser.

  18. Losas de concreto reforzadas con acero inoxidable de desecho Reinforced concrete slabs with stainless steel waste

    Directory of Open Access Journals (Sweden)

    Jorge Alberto Pérez González

    2008-08-01

    Full Text Available Se muestran los resultados de un programa experimental que explora la reutilización de materiales de desecho industrial (específicamente láminas de acero inoxidable producto de la acuñación de moneda como refuerzo en losas de concreto. Para ello se elaboraron 23 especímenes tipo viga-losa a escala natural con dicho refuerzo a fin de determinar su comportamiento en términos de resistencia, ductilidad y formas de falla; el análisis experimental de modelos ensayados con diferentes cantidades de refuerzo muestra que en algunos casos, bajo ciertas condiciones de cuantías y colocación del mismo, es posible alcanzar capacidades de carga y formas de falla similares a las de especímenes de control con refuerzo tradicional. En base a estos resultados se concluye en la factibilidad de utilizar el material arriba descrito como refuerzo alternativo en elementos estructurales de concreto, tratando de encontrar alternativas más económicas en la construcción de vivienda popular.The results from an experimental program that explores the use of industrial waste materials (specifically sheets of stainless steel that result of the currency coinage as reinforcement for concrete slabs are presented. Twenty three full size beam-deck specimens were built in order to measure resistance, ductility and failure modes; the experimental analysis in models with reinforcement in different quantities shows that in some cases, under certain quantities and location, it is possible to reach similar load capacities and failure modes as specimens with traditional reinforcement. Based on these results, it is concluded the feasibility of using the material described above as alternative reinforcement in structural concrete elements, as an economic option in the construction of social housing.

  19. Comportamiento frente a la corrosión de los aceros inoxidables AISI 430L P/M

    Directory of Open Access Journals (Sweden)

    Corpas, F. A.

    2004-04-01

    Full Text Available In this paper we have studied the resistance to corrosion of the 430L ferritic stainless steels, manufactured by powder metallurgy. We have compared the behaviour of the different series of 430L stainless steels sintered, tempered and annealing, in different corrosive environments. Finally, the microstructure of the steels was determined by means of scanning electron microscopy. The better resistance to corrosion are produced in the steel annealing to 300ºC and 600ºC.

    En este trabajo hemos estudiado la resistencia a la corrosión que presentan los aceros inoxidables ferríticos 430L fabricados por procedimientos pulvimetalúrgicos. Hemos evaluado y comparado distintas series de aceros inoxidables 430L sinterizados, templados y madurados a diferentes temperaturas en atmósfera de nitrógeno, introduciéndolos en varios medios corrosivos de distinta naturaleza. Por último, se determinó la microestructura, mediante microscopía electrónica de barrido. Los mejores valores de resistencia a la corrosión se encuentran para los aceros tratados a 300ºC y 600ºC.

  20. Análisis de soldabilidad de aceros inoxidables con aceros de medio y bajo carbono por SMAW

    Directory of Open Access Journals (Sweden)

    José Luddey Marulanda Arevalo

    2013-12-01

    Full Text Available Se presenta un estudio de la soldabilidad de aceros inoxidables austeníticos AISI 304 y AISI 316 con aceros de bajo y medio carbono AISI 1020 – AISI 1045, empleando como materiales de aporte los electrodos EutecTrode® 52 NG, 54 NG y 57 NG, mediante el proceso de arco eléctrico con electrodo revestido (SMAW. Para analizar la soldabilidad de estos electrodos cuando se realiza la unión de aceros inoxidables con aceros al carbono, se practicaron pruebas metalográficas y ensayos mecánicos de dureza, doblez y tracción, con el fin de observar el comportamiento tanto de la zona afectada térmicamente como del cordón de soldadura, a partir del cambio en las propiedades mecánicas y metalúrgicas en las diferentes regiones de las uniones soldadas. Durante el proceso de soldadura se siguió una especificación del procedimiento de soldadura (WPS, para que los resultados fueran repetibles, minimizando los problemas de agrietamiento en caliente, agrietamiento en frío, formación de fase sigma y precipitación de carburos.

  1. In situ micro Raman spectroscopy for characterization of oxide film formed on the new surface and for measurements of the stress of oxide film formed on 304L stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Kai, A.; Takegoshi, M.; Shoji, T. [Fracture Research Inst., Tohoku Univ., Sendai (Japan)

    2004-07-01

    Environmentally assisted cracking (EAC) consists of two distinct events viz., i) crack initiation and ii) crack propagation. On a smooth surface, the EAC initiates by the rupture or by the degradation of the surface film due to the combined action of stress and an electrochemical reaction of the materials with the environment. The mechanical properties of the surface oxide films are also important considerations when determining the susceptibility to EAC. In this research, Micro Raman Spectroscopy (MRS) was applied for in-situ oxides characterization and for in-situ measurements of the stress in oxide film formed on the surface of 304L stainless steel during the scratching electrode and the slow strain rate test (SSRT), respectively. The passive oxide film growth formed on the bare surface was continuously monitored by MRS as a function of time. For stress measurements, Cr{sub 2}O{sub 3} was focused on and raman shift at Cr{sub 2}O{sub 3} peak of Raman spectrum was measured continuously. The strain rate was 8.2 x 10{sup -7}/sec. In the initial stage of SSRT, the Raman shift of surface film decreased gradually with strain. At 5% strain, the Raman shift of surface film increased rapidly to around the initial value of Raman shift. It is considered that the surface film was ruptured at this time. At 5% strain, the shift value of Raman peak of Cr{sub 2}O{sub 3} reached to 5 cm{sup -1}. This value (5 cm{sup -1}) corresponds to 1.2 GPa which value of tensile stress is calculated from reference data. These characteristics of oxide film will be implemented into the theoretical formulation of EAC and their implication to EAC growth rate will be discussed. (orig.)

  2. Efecto de la biopelícula en la corrosión de aceros inoxidables

    Directory of Open Access Journals (Sweden)

    Bethencourt, M.

    2010-02-01

    Full Text Available In this work, the influence of the biofilms in the corrosion process of different alloys of stainless steel was studied in two sampling points in a wastewater treatment plant during 4 years. The physicochemical microenvironment within the biofilms was characterized through O2, H2S and pH microelectrodes. Corrosion rates were quantified from the number, diameter and depth of pits. The results show a remarkable development of the biofilm and a significantly greater number of pits in the grit removal channel than in the sludge recirculation channel. Based on the characteristics of the water phase and microelectrode measurements, our results suggest that biofilms induced corrosion throughout 3 mechanisms: creation of differential aeration cells, areas with different pH and areas having high sulphide production which may react with metal ions.

    En este trabajo se ha estudiado la influencia de las biopelículas en los procesos de corrosión de diferentes aleaciones de acero inoxidable, situadas durante 4 años en dos puntos de una estación depuradora de aguas residuales. Se caracterizó el microambiente físico-químico en el interior de las biopelículas mediante microelectrodos de O2, H2S y pH, y se cuantificaron las tasas de corrosión a partir del número, diámetro y profundidad de picadura. Los resultados obtenidos muestran un desarrollo más notable de las biopelículas y un número de picaduras significativamente mayor en el canal de salida de desbastes que en el canal de recirculación de fangos. Con base en las características del agua sobrenadante y en las medidas realizadas con microelectrodos, se sugiere que la biopelícula induce la corrosión a través de tres posibles mecanismos: creación de celdas de aireación diferencial, zonas con diferente pH y zonas con elevada producción de sulfuro capaz de reaccionar con iones metálicos.

  3. Propiedades mecánicas de las uniones por láser de aceros inoxidables dúplex

    Directory of Open Access Journals (Sweden)

    Amigó, V.

    2005-04-01

    Full Text Available The welded joints of stainless steels always present problems for the microstructural modifications that occur in the heat affected zone. Particularly, duplex stainless steels present very important changes when the weld pool solidifies forming fundamentally ferritic structures with some austenite in grain boundaries. These microstructural modifications, and those which occur in the HAZ, justify the mechanical properties of the joint and mainly those of plasticity, being all of them influenced by the processing conditions. In this work the influence of the laser welding speed on the tensile behaviour of duplex stainless steel welded joints is presented. The microstructure of the obtained seams and of the heat affected zone will be evaluated by means of optic and scanning electron microscopy. Also, different microhardness profiles have been obtained to evaluate the modifications in the mechanical properties both in the seam and the zone of thermal affection.

    Las uniones soldadas de aceros inoxidables siempre presentan problemas por las modificaciones microestructurales que suceden en la zona afectada por el calor. Particularmente, los aceros inoxidables dúplex presentan cambios microestructurales muy importantes al solidificar el cordón y formar estructuras, fundamentalmente ferríticas, con formación de austenita en borde de grano. Estas modificaciones microestructurales, junto a las que suceden en la ZAC, son las que justifican las propiedades mecánicas de la unión y fundamentalmente las de plasticidad. Y todo ello en función de las condiciones de procesado. En este trabajo se presenta la influencia de la velocidad de soldeo en las propiedades a tracción de uniones soldadas por láser de chapas de acero inoxidables dúplex. La microestructura de los cordones obtenidos y de la zona afectada por el calor se ha evaluado mediante microscopía óptica y electrónica de barrido, y se han obtenido diferentes perfiles de microdureza que

  4. Oxidación en vapor de agua del acero inoxidable aisi 317 a 700 y 750ºc

    OpenAIRE

    MARULANDA AREVALO, JOSE LUDDEY; REMOLINA MILLAN, ADULJAY; BARON, JAIRO ALBERO

    2013-01-01

    Se realizó la oxidación del acero inoxidable austenítico AISI SAE 317, a temperaturas de 700 y 750ºC, en un ambiente con 100% vapor de agua, para evaluar su comportamiento a la corrosión. Se realizaron curvas de ganancia de masa y las películas de óxidos se analizaron por medio de Microscopia Electrónica de Barrido (SEM) y difracción de rayos X (DRX), para observar cómo se forman las capas de óxidos y discutir el posible mecanismo de oxidación en vapor de agua. Se encontró que el mecanismo de...

  5. OXIDACIÓN EN VAPOR DE AGUA DEL ACERO INOXIDABLE AISI 317 A 700 Y 750ºC

    OpenAIRE

    José Luddey Marulanda Arevalo; Aduljay Remolina Millan; Jairo Alberto Barón

    2013-01-01

    Se realizó la oxidación del acero inoxidable austenítico AISI SAE 317, a temperaturas de 700 y 750ºC, en un ambiente con 100% vapor de agua, para evaluar su comportamiento a la corrosión. Se realizaron curvas de ganancia de masa y las películas de óxidos se analizaron por medio de Microscopia Electrónica de Barrido (SEM) y difracción de rayos X (DRX), para observar cómo se forman las capas de óxidos y discutir el posible mecanismo de oxidación en vapor de agua. Se encontró que el mecanismo de...

  6. Tratamiento térmico del acero inoxidable ferrítico AISI 430L sinterizado en atmósfera de N2-H2

    Directory of Open Access Journals (Sweden)

    Ruiz-Prieto, J. M.

    2005-12-01

    Full Text Available In this Work the influence of sintering AISI 430L stainless steel in N2-H2 atmosphere on its properties and microstructure have been studied. The presence of nitrogen in the sintering atmosphere leads to complex nitrides formation the AISI 430L sintered steel microstructure. A subsequent heat treatment was applied to modify this microstructure in order to improve the mechanical properties and corrosion resistance of these ferritic stainless steels.Los aceros inoxidables ferríticos, son aceros que contienen esencialmente cromo (12-30 % junto con níquel y molibdeno en cantidades que, en general, no sobrepasan el 1 % y, en ocasiones, se les adicionan otros elementos como son el aluminio, silicio, titanio o niobio. En el presente trabajo de investigación se ha evaluado la influencia del nitrógeno presente en la atmósfera de sinterización sobre la microestructura y propiedades del acero inoxidable ferrítico AISI 430L. Además, se ha realizado un tratamiento térmico posterior de hipertemple y maduración con el objeto de incrementar las propiedades mecánicas y a corrosión de este acero inoxidable, mediante la modificación microestructural de los nitruros complejos de hierro y cromo precipitados durante la etapa de sinterización.

  7. Evaluación del grado de sensibilización en el acero inoxidable AISI

    Directory of Open Access Journals (Sweden)

    González, O.

    2003-12-01

    Full Text Available Austenitic stainless steel, when heat-treated at 550-850 °C, became susceptible to intergranular corrosion in acids. This phenomenon, know as sensitization, it is result from the precipitation of chrome carbides in the grain boundary, making these areas less resistant to corrosion. Two different electrochemical reactivation tests are compared with a destructive test and related to the classification of its respective microstructures. It was established a quantitative methodology to evaluate the degree of sensitization in AISI 304 and also to compare the correspondence of the results with the data of the automatic and portable EPR device for non-destructive field measurement of the degree of sensitization. The used electrochemical techniques were the EPR (Electrochemical Potentiokinetic Reactivation or single loop test and the PRP (Pasivation Reactivation Potentiokinetic or double loop test. The destructive test used was boiling, 120 h ferric sulfate-50 % sulfuric acid, according to the standard practices ASTM A-262 practices B. The classifications of each structures were according to the standard practices ASTM A-262 practices B.

    El acero inoxidable austenítico, cuando se calienta en un rango de temperatura entre 550 y 850 °C es susceptible a corrosión intergranular en ácidos. Este fenómeno, conocido como sensibilización, es resultado de la precipitación de carburos de cromo en el límite de grano, haciendo esas áreas menos resistentes a la corrosión. Se comparan dos pruebas diferentes de reactivación electroquímica con una prueba destructiva, relacionándolas con su respectiva microestructura. Se estableció una metodología cuantitativa para evaluar el grado de sensibilización del acero AISI 304 y se comparó con los datos generados de una herramienta no destructiva de campo, automática y portátil, para medir el grado de sensibilización. Las técnicas electroquímicas usadas fueron: la EPR (Reactivación electroqu

  8. Desarrollo de los procesos de moldeo por inyección y extrusión de polvos para la obtención de piezas de aceros inoxidables dúplex y ferríticos

    OpenAIRE

    Sotomayor Lozano, María Eugenia

    2011-01-01

    En la presente Tesis Doctoral se ha desarrollado el proceso de moldeo por inyección de polvos (pIM) para la obtención de piezas de acero inoxidable dúplex con aplicaciones en ortodoncia. Por otro lado, se ha desarrollado el proceso de moldeo por extrusión de polvos (PEM) para la obtención de láminas y tubos porosos de acero inoxidable ferrítico con aplicaciones en pilas de combustible de óxido sólido (SOFCs). En primer lugar, se prepararon y caracterizaron térmica y reológicamente las mezclas...

  9. Influence of surface conditions on fatigue strength through the numerical simulation of microstructure; Etude par simulation numerique de la microstructure de l'influence de l'etat de surface sur la resistance a la fatigue d'un acier 304L

    Energy Technology Data Exchange (ETDEWEB)

    Le Pecheur, A.; Clavel, M.; Rey, C.; Bompard, P. [Laboratoire MSSMat, UMR 8579 CNRS, Ecole Centrale Paris (France); Le Pecheur, A.; Curtit, F.; Stephan, J.M. [Departement MMC, EDF RD, Site des Renardieres (France)

    2010-11-15

    A thermal fatigue test (INTHERPOL) was developed by EDF in order to study the initiation of cracks. These tests are carried out on tubular specimens under various thermal loadings and surface finish qualities in order to give an account of these parameters on crack initiation. The main topic of this study is to test the sensitivity of different fatigue criteria to surface conditions using a micro/macro modelling approach. Therefore a 304L polycrystalline aggregate, used for cyclic plasticity based FE modelling, have been considered as a Representative Volume Element located at the surface and subsurface of the test tube. This aggregate has been cyclically strained according to the results issued from FE simulation of INTHERPOL thermal fatigue experiment. Different surface parameters have been numerically simulated: effects of local microstructure and of grains orientation, effects of machining: metallurgical prehardening, residual stress gradient, and surface roughness. Three different fatigue criteria (Manson Coffin, Fatemi Socie and dissipated energy types), previously fitted at a macro-scale for thermal fatigue of 304L, have been computed at a meso scale, in order to show the surface 'hot spots' features and test the sensitivity of these three criteria to different surface conditions. Results show that grain orientation and neighbouring play an important role on the location of hot spots, and also that the positive effect of pre-straining and the negative effect of roughness on fatigue life are not all similarly predicted by these different fatigue criteria. (authors)

  10. Correlaciones entre la microestructura y la atenuación sonora en un acero inoxidable martensítico

    Directory of Open Access Journals (Sweden)

    Daniel Ramírez C.

    2004-01-01

    Full Text Available En este trabajo se exploró la relación entre la microestructura de un acero inoxidable martensítico y las variaciones en el sonido producido por un instrumento metalófono construido con dicho material. Para lograr este propósito, se hicieron copias de una de las placas de un glockenspiel y éstas fueron sometidas a diferentes tratamientos térmicos. Se construyeron montajes que permitieron producir sonidos mediante la excitación por percusión o electromagnética de las placas y se desarrollaron procedimientos para el análisis de las señales adquiridas usando programas de que permitían un análisis automático de la información. A partir de los resultados fue posible establecer correlaciones entre la microestructura obtenida con los diferentes tratamientos térmicos y características de los sonidos tales como la envolvente de atenuación y frecuencias predominantes.

  11. Análise microestrutural e tenacidade ao impacto da ZAC do aço inoxidável ferrítico com 11%Cr

    Directory of Open Access Journals (Sweden)

    Temístocles de Sousa Luz

    2013-09-01

    Full Text Available O aço inoxidável ferrítico possibilita, em função de suas características, o uso em diversos campos da engenharia. Dentre esses é possível citar a industria do petróleo e gás, de celulose açucareira, de transporte, entre outras. Atualmente, o desenvolvimento de novas ligas para a substituição dos aços ao carbono no que se refere ao setor de transporte de carga, levou muitos fabricantes a adotarem a liga ferrítica com base de cromo entre 11% e 12%, implementando a tal situação, uma maior vida util. A utilização dessa nova classe de aço inoxidável ferrítico gera uma demanda no que tange à pesquisas das soldas desses aços. Neste trabalho, buscou-se analisar a região soldada de um aço inoxidável ferrítico experimental contendo 11% de cromo, realizando para tal um estudo de sua microestrutura, e tenacidade ao impacto do metal de base e da zona afetada pelo calor (ZAC. A avaliação mostrou bons resultados nas propriedades mecânicas medidas nas duas regiões analisadas. Entretanto, verificou-se uma perda acentuada da tenacidade ao impacto na ZAC em relação ao metal de base.

  12. Evaluación de la adherencia del biofilm sobre salivaderas dentales de acero inoxidable, cerámica y opalina

    OpenAIRE

    Butler, Teresa Adela

    2009-01-01

    El objetivo principal de esta investigación fue estudiar el desarrollo de la biopelícula depositada sobre las salivaderas dentales de tres materiales diferentes (acero inoxidable, cerámica y opalina), de equipos odontológicos correspondientes a dos zonas diferentes del casco urbano de la ciudad de La Plata (Z1 y Z2). Para ello se realizaron 38 cortes de salivaderas dentales de los tres materiales, de cada zona En primer lugar se realizó el análisis de la microbiota planctónica y sé...

  13. Estudio comparativo de la cavidad de acceso radicular en conductos curvos con limas de níquel-titanio y taladros de acero inoxidable

    OpenAIRE

    Oncins Rodríguez, J.; Pumarola Suñé, José; Canalda Sahli, Carlos

    2005-01-01

    El propósito de este estudio fue comparar la cantidad de dentina radicular removida y evaluar el mantenimiento de la forma del conducto tras la instrumentación de los dos tercios coronarios radiculares, utilizando instrumentos de acero inoxidable (taladros de Gates Glidden) y de níqueltitanio (limas GT Flare y limas Orifice Shaper). Un total de 42 dientes humanos extraídos con conductos radiculares curvos fueron divididos en tres grupos. Los conductos se instrumentaron mecánicamente usando ta...

  14. Estudio de la calidad de recubrimientos de hidroxiapatita sobre acero inoxidable implantable aplicados mediante proyección térmica con plasma

    OpenAIRE

    Bernal Gaona, Sandra Paola

    2013-01-01

    El objetivo de este trabajo de investigación se basó en el estudio de los parámetros del proceso de deposición de recubrimientos de hidroxiapatita sobre substratos de acero inoxidable implantable mediante el proceso de proyección térmica con plasma atmosférico, que pueden afectar de forma significativa la calidad de los recubrimientos, en cuanto a su cristalinidad y adherencia al substrato. Como parámetros a evaluar se tomaron el tamaño de grano de la hidroxiapatita, el espesor...

  15. Corrosión a alta temperatura de acero al carbono y acero inoxidable austenítico en atmósferas contaminadas por CO2

    OpenAIRE

    Proy Pérez, Manuel

    2014-01-01

    Los efectos a veces catastróficos producidos por los procesos de corrosión a alta temperatura en atmósferas contaminadas por agentes agresivos, poseen la suficiente relevancia para ser objeto de estudio en los próximos años, debido a que en muchas ocasiones no están definidos claramente. Los aceros al carbono y los inoxidables austeníticos son materiales potencialmente utilizables en condiciones de elevada temperatura gracias a su excelente relación entre sus propiedades est...

  16. Comportamiento al desgaste por deslizamiento en aceros inoxidables: ferrítico, austenítico, dúplex y martensítico.

    OpenAIRE

    Renedo Rouco, Jordi

    2010-01-01

    En este proyecto se estudia el comportamiento al desgaste por deslizamiento de cuatro aceros representativos de las cuatro grandes familias de aceros inoxidables: ferrítico (AISI 446), austenítico (AISI 316), dúplex (AISI 2205) y martensítico (AISI 420). Para cada uno de ellos se han realizado: caracterización metalográfica, determinación de dureza, densidad y rugosidad, y ensayos de tribología mediante la técnica de bola sobre disco. Esta técnica consiste en deslizar una bola ...

  17. Formación de maclas durante el enfriamiento en aceros inoxidables superferríticos envejecidos

    Directory of Open Access Journals (Sweden)

    Salán, M. N.

    2005-12-01

    Full Text Available Superferritic stainless steels show a BCC structure free of austenite at any temperature. Intermediate ageing temperatures, close to 475 °C, induce a-chromium content modulation and only after long periods of time, it is possible to detect chromium rich α' phase, which is responsible for embrittlement (475 °C embrittlement. In this work, ageing thermal treatments at intermediate temperatures in the superferritic stainless steel DIN 1.4575, have allowed to relate the associated hardness increase with time and temperature by means of a relationship that is compatible with a thermally activated process. After quenching from ageing temperature, twinning formation has been observed, and the extent of twinning is proportional to the increase in hardness, showing in this way that twinning density is proportional to embrittlement level.

    Los aceros inoxidables superferríticos se caracterizan por su estructura cúbica centrada, libre de austenita a cualquier temperatura. Sometidos a temperaturas intermedias, próximas a 475 °C, revelan una modulación del contenido en Cr de la red. Después de tiempos prolongados se forma fase α', fragilizante y rica en cromo, fenómeno conocido como fragilización a 475 °C. En este trabajo, los tratamientos de envejecimiento realizados a temperaturas intermedias para un superferrítico DIN 1.4575 han permitido relacionar el incremento de dureza asociado a éstos con el tiempo de tratamiento, mediante una expresión coherente con un proceso térmicamente activado. Por otra parte, se ha detectado la presencia de maclas en el acero envejecido y templado en agua, siendo proporcional su densidad al grado de endurecimiento provocado por el tratamiento.

  18. Caracterización y propiedades mecánicas a alta temperatura de un acero inoxidable dúplex

    Directory of Open Access Journals (Sweden)

    Jiménez, J. A.

    1998-05-01

    Full Text Available The microstructure and mechanical behavior at high temperature of a thermomechanical processed duplex stainless steel have been studied. Recrystalization of the material takes place during heating to test temperature, and a microstructure consisting of islands of austenitic grains of about 10-15 μm in size included in a more or less continuous matrix of ferrite is observed. Tensile tests at temperatures above 1,000°C and at low strain rates show a stress exponent of about 2 and elongations to failure up to 290 %. These values suggest that deformation is controlled by a grain boundary sliding mechanism, which causes a decrease in the size of the islands during deformation. Finally, an activation energy for plastic deformation of 167 kJ/mol was observed that was related to the activation energy for grain boundary diffusion of iron.

    Se ha estudiado la microestructura y el comportamiento mecánico a alta temperatura de un acero inoxidable dúplex procesado termomecánicamente. Durante el calentamiento a la temperatura de ensayo, el material recristaliza y se obtiene una microestructura de granos austeníticos de tamaños comprendidos entre 10 y 15 μm agrupados en islas incluidas en una matriz más o menos continua de ferrita. Ensayos de tracción a temperaturas superiores a 1.000°C y bajas velocidades de deformación muestran un exponente de la tensión igual a 2 y alargamientos a rotura de hasta 290 %. Estos valores permiten asociar el mecanismo de deformación al deslizamiento de fronteras de grano, el cual determina la desaparición progresiva de las islas de granos austeníticos durante la deformación. Finalmente, se encontró un valor de 167 kJ/mol para la energía de activación de la deformación plástica, la cual se relacionó con la energía de autodifusión del hierro a lo largo de las fronteras de grano.

  19. Vida a la fatiga de juntas soldadas del acero inoxidable AISI 316L obtenidas mediante el proceso GMAW

    Directory of Open Access Journals (Sweden)

    Puchi-Cabrera, E. S.

    2007-06-01

    Full Text Available An investigation has been conducted in order to determine the effect of both the metallic transfer mode (pulsed arc or short circuit and the O2 content in the Ar/O2 gas mixture, of the gas-metal arc welding process (GMAW, on the fatigue life under uniaxial conditions of welded joints of 316L stainless steel. It has been concluded that the mixture of the protective gases employed in the process could have an important influence on the fatigue life of the welded joints of such steel in two different ways. Firstly, through the modification of the radius of curvature at the joint between the welding toe and the base metal and, secondly, through a more pronounced degree of oxidation of the alloying elements induced by a higher O2 content in the mixture. As far as the metallic transfer mode is concerned, it has been determined that the welded joints obtained under a pulsed arc mode show a greater fatigue life in comparison with the joints obtained under short circuit for both gas mixtures.

    Se ha llevado a cabo una investigación con la finalidad de determinar el efecto, tanto del modo de transferencia metálica (arco pulsado o cortocircuito como del contenido de O2 en la mezcla de gases protectores Ar/O2, del proceso de soldadura a tope mediante arco metálico con protección gaseosa (GMAW, sobre la vida a la fatiga en condiciones uniaxiales de juntas soldadas del acero inoxidable AISI 316L. Dicho trabajo ha permitido concluir que la composición de la mezcla de gases protectores del proceso GMAW pudiera tener una influencia importante en la vida a la fatiga de las juntas soldadas de dicho material, a través de dos formas distintas: primero, mediante la modificación del radio de curvatura entre la raíz del cordón de soldadura y el metal base y, en segundo lugar, a través del mayor grado de oxidación de los elementos de aleación. En cuanto al modo de transferencia metálica, se determinó que las juntas soldadas mediante arco pulsado

  20. Influencia de la microestructura en el comportamiento a fatiga de aceros inoxidables austeníticos con alto contenido en molibdeno

    Directory of Open Access Journals (Sweden)

    Oñoro, J.

    2006-02-01

    Full Text Available Austenitic stainless steels with molybdenum present high mechanical properties and corrosion resistance to aggressive environments. These steels have been used to tank and vessel components for high corrosive liquids as phosphoric, nitric and sulphuric acids. These materials with low carbon and nitrogen addition have been proposed candidates as structural materials for the international thermonuclear experimental reactor (ITER in-vessel components. Molybdenum addition in austenitic stainless steel improves mechanical and corrosion properties, but with it can produce the presence of nitrogen microstructure modifications by presence or precipitation of second phases. This paper summarises the fatigue and corrosion fatigue behaviour of two 317LN stainless steels with different microstructure. Fully austenitic steel microstructure show better fatigue, corrosion fatigue resistance and better ductility than austenitic steel with delta ferrite microstructure, mainly at low stresses.

    Los aceros inoxidables austeníticos con elevados contenidos en molibdeno presentan alta resistencia mecánica y resistencia a los medios corrosivos. Se utilizan en la construcción de depósitos y recipientes para el almacenamiento y transporte de líquidos altamente corrosivos, tales como ácido fosfórico, nítrico o sulfúrico. Estos materiales con bajo carbono y adiciones de nitrógeno han sido propuestos como candidatos para materiales estructurales en la fabricación de la vasija del reactor experimental termonuclear internacional (ITER. La adición de molibdeno mejora las propiedades frente a la corrosión de los aceros inoxidables austeníticos. Sin embargo, este aumento del contenido en molibdeno, junto con la presencia de nitrógeno, puede producir modificaciones microestructurales, por la aparición de fases precipitadas o segundas fases. En este trabajo, se analiza el comportamiento la fatiga y corrosión-fatiga de dos aceros inoxidables austen

  1. Soldagem por Difusão de Aços Inoxidáveis para Fabricação de Trocadores de Calor Compactos

    Directory of Open Access Journals (Sweden)

    Marcus Vinícius Volponi Mortean

    2016-03-01

    Full Text Available Resumo A união de materiais diferentes ou componentes com geometrias complexas muitas vezes requer processos de uniões especiais, como por exemplo, uma fonte de energia de alta densidade como laser ou feixe de elétrons para soldagem por fusão ou mesmo um processo de soldagem no estado sólido. Em particular, este trabalho descreve os experimentos recentes da aplicação da soldagem por difusão no estado sólido (SDES para diferentes tipos de aços inoxidáveis: austenítico AISI 316L, duplex UNS 31803 e superduplex UNS 327250. A soldagem por difusão foi realizada sob alto vácuo a 1050 °C, durante 60 minutos, empregando uma pressão uniaxial de 18-35 MPa. A qualidade da união foi avaliada por microscopia óptica e testes mecânicos. Os resultados preliminares indicam a necessidade de otimização dos parâmetros de processo para os aços duplex e superduplex. Os resultados positivos alcançados no presente trabalho permitiram a fabricação de protótipos de trocadores de calor compacto em aço inoxidável, utilizando o novo método de fabricação, desenvolvido por LABTUCAL / UFSC, através do qual o processo de corte a jato de água é aplicado para confeccionar com precisão os canais do núcleo do permutador de calor.

  2. Efecto de la Composición Química del Metal de Aporte y del Calor Aportado Sobre la Microestructura y las Propiedades Mecánicas de Juntas Soldadas de Aceros Inoxidables Dúplex

    Directory of Open Access Journals (Sweden)

    Sebastián Zappa

    Full Text Available Resumen Los aceros inoxidables dúplex poseen una microestructura dual (ferrita y austenita con contenidos aproximadamente iguales y se caracterizan por tener buena soldabilidad, buenas propiedades mecánicas y una alta resistencia a la corrosión generalizada y localizada. Gracias a estas características, estos aceros son los principales materiales a emplear en cañerías con altas exigencias, ampliamente utilizados en varias industrias, principalmente la petroquímica. Dichas propiedades están controladas por la composición química, el equilibrio microestructural y la ausencia de compuestos intermetálicos. El objetivo de este trabajo fue estudiar la influencia de la composición química del metal de aporte y el calor aportado sobre la microestructura y las propiedades mecánicas en juntas soldadas de cañerías de acero inoxidable dúplex. El metal base utilizado fue un acero inoxidable dúplex UNS S31803 de 8” de diámetro y 8,18 mm de espesor y los metales de aporte fueron dos alambres tubulares que depositan aceros inoxidables dúplex y lean dúplex (AWS A5.22: E2209T1-1 y E2209T1-G, mediante el proceso de soldadura semi-automático bajo protección gaseosa, soldados con alto y bajo calor aportado. De cada probeta se extrajeron muestras donde se determinó la composición química, se realizó la caracterización microestructural y se determinaron las propiedades mecánicas (dureza, tracción y Charpy-V.

  3. Deposición electroforética de una porcelana dental sobre acero inoxidable austenítico 304

    Directory of Open Access Journals (Sweden)

    Vargas, G.

    2003-02-01

    Full Text Available An alternative technique for the production of dental restorations with porcelain, is the electrophoretic deposition (EPD. In this work, deposits of dental porcelain on stainless steel were obtained by EPD using water, ethanol and isopropanol as suspension mediums. The effect of the porcelain concentration, the intensity of the electric field and the suspension medium on the quantity of deposited mass were studied. All the tests were carried out at constant voltage, using a deposition time of 3 min. The particle size of the dental porcelain was in the range between 1.5 and 2.3 μm in the suspension. The results showed that the porcelain in the aqueous medium presented the major deposition velocity, in comparison with both ethanol and isopropanol. However, due to low the low suspension stability and hydrolysis of the water problems, the best coating finishes were obtained with ethanol. These results were obtained applying voltages between 70 and 150 V, for a deposition time of 3 min. Using isopropanol heterogeneous deposits were obtained due to the low suspension stability and to electrochemical reactions problems in the working electrodes, resulted from the high voltages application.

    Una técnica alternativa para la fabricación de restauraciones dentales con porcelana, es la deposición electroforética (EPD. En este trabajo depósitos de porcelana dental sobre acero inoxidable fueron obtenidos por EPD utilizando como medios de suspensión: agua, etanol e isopropanol. Se estudió el efecto de la concentración de porcelana, de la intensidad del campo eléctrico y del medio de suspensión sobre la cantidad de masa depositada. Todas las pruebas fueron realizadas a voltaje constante, utilizando un tiempo de deposición de 3 min. La porcelana dental utilizada presentó un intervalo de tamaño de partícula entre 1,5 y 2,3 μm. Los resultados mostraron que la porcelana en el medio acuoso presentó la mayor velocidad de deposición, en

  4. Estudio de la influencia microbiológica en la corrosión de latones (UNS C68700, UNS C443 y acero inoxidable AISI 316;

    Directory of Open Access Journals (Sweden)

    Ohanian, Mauricio

    2014-06-01

    Full Text Available Microorganisms may play an important role in the corrosion process and generate conditions which affect the rate and/or the mechanism of deterioration. They become visible by the formation of biofilms: clusters of microorganisms and extracellular polymers. These biofilms affect not only the durability of the material, but also reduce the heat transfer. The present work studied the growth of aerobic and anaerobic heterotrophic microorganisms and sulfate reducing bacteria on aluminum brass (UNS C68700, admiralty brass (UNS C443 and stainless steel AISI 316 in exposure experiments held in the Bay of Montevideo (Uruguay. The influence of the biofilm growth on the corrosion behavior was studied by electrochemical techniques: polarization curves and Electrochemical Impedance Spectroscopy (EIS. The selection of the most suitable material for the exposure conditions is discussed and hypotheses of the corrosion mechanism are presented. Although stainless steel AISI 316 presented the lowest corrosion rate it showed localized deterioration.Los microorganismos influyen de manera significativa en el proceso corrosivo y generan condiciones que afectan la velocidad y/o el mecanismo de deterioro. Su presencia se manifiesta por la formación de bio-películas: conglomerados de bacterias y polímeros extracelulares. Dichas bio-películas afectan la durabilidad del material, la velocidad de flujo y la transferencia de calor. En el presente trabajo se evalúa el crecimiento de microorganismos heterótrofos aerobios, heterótrofos anaerobios y bacterias sulfato-reductoras sobre latón aluminio (UNS C68700, latón almirantazgo (UNS C443 y acero inoxidable AISI 316. Asimismo, se estudia la influencia del crecimiento de la bio-película sobre el comportamiento corrosivo mediante técnicas electroquímicas: curvas de polarización y espectroscopia de impedancia electroquímica. Las exposiciones se realizan en la Bahía de Montevideo, estuario del Río de la Plata

  5. Estudio de corrosión galvánica en pares latón/acero inoxidable y latón/fundición de hierro

    Directory of Open Access Journals (Sweden)

    Ohanian, M.

    2011-08-01

    Full Text Available Corrosion attack in heat exchanger systems is a topic of main interest for the maintenance in each industrial plant. These are multigalvanic systems with particular geometric and fluidodynamic complexity. Corrosive damages include zinc selective dealeation in copper alloys. In order to explain zinc dealeation attack, this paper deals with laboratory scale testing, characterization and interactions between two copper and zinc alloys (Yellow brass –UNS C268– and Admiralty brass –UNS C443– compared to AISI 316 stainless steel and cast iron. The tests were performed at 20 °C in 1.5 % NaCl and 1.5 % Na2SO4 solutions, pH 8 and each material was characterized by potentiodynamic sweeps. The couples are analyzed by studying transient galvanic currents. We conclude about the cause of the analyzed pathology, brass protection potential ranges and its coupling compatibility with other metals.

    El ataque por corrosión en los sistemas intercambiadores de calor constituye un problema para el mantenimiento de cualquier planta industrial. Se trata de sistemas multigalvánicos con particular complejidad geométrica y fluidodinámica. Las patologías corrosivas incluyen el fenómeno de dealeación selectiva de cinc en las aleaciones de cobre. A fin de explicar un caso particular de ataque por decinficación (deterioro en placa de intercambiador de calor de tubos de inoxidable, el presente trabajo aborda en ensayos a escala de laboratorio, la caracterización e interacciones entre dos aleaciones de cobre y cinc, (Yellow brass –UNS C268– y Admiralty brass –UNS C443–, respecto a acero inoxidable AISI 316 y fundición gris de hierro. Los ensayos se realizan a 20 °C en disoluciones de NaCl 1,5 % y Na2SO4 1,5 % y pH 8. Se caracterizan electroquímicamente las aleaciones y materiales involucrados mediante barridos potenciodinámicos. Los pares galvánicos formados se analizan mediante el

  6. Influência da temperatura interpasse nas propriedades do aço inoxidável duplex durante a soldagem pelo processo a arco submerso

    Directory of Open Access Journals (Sweden)

    Tatiana Resende Alvarez

    2014-06-01

    Full Text Available Os aços inoxidáveis duplex (AID são materiais que apresentam elevada resistência à corrosão com altos valores de resistência mecânica motivando sua utilização em diversos componentes de processo na indústria offshore. No entanto, existem grandes desafios na soldagem destes materiais em termos de produtividade e qualidade da junta produzida, tendo em vista sua ampla utilização desde componentes de pequenas espessuras, tais como umbilicais, até de grandes espessuras, como tubulações de linhas de injeção de água salgada. No que concerne a tubulações de espessuras pequenas é empregado satisfatoriamente o processo de soldagem Gas Tungsten Arc Welding (GTAW conhecido como TIG. No que diz a respeito a tubulações de paredes espessas foi implementado, recentemente, o processo automático de soldagem por arco submerso (SAW na linha de pré-montagem de tubulações, aumentando consideravelmente a produtividade das juntas produzidas. No entanto, existe uma grande demanda de tempo para a realização de um novo passe de solda, em virtude da máxima temperatura interpasse exigida ser inferior a 150ºC. Portanto, o presente trabalho apresenta os resultados da caracterização e avaliação da resistência à corrosão de uma junta soldada correspondente a uma tubulação de aço inoxidável duplex (AID UNS S31803 de 21,4 mm de espessura de parede soldada pelos processos de soldagem MIG (GMAW na raiz e arco submerso (SAW no enchimento e acabamento, empregando-se temperaturas interpasses entre 150 e 290ºC. Os resultados da caracterização das propriedades mecânicas, composição química e resistência à corrosão em diversas regiões da junta soldada foram comparadas com os obtidos para o metal de base (MB da tubulação, assim como com os valores mínimos exigidos pelas normas de projeto. Deste modo, o presente trabalho permite avaliar a influência da temperatura interpasse nas propriedades da junta em decorrência de um poss

  7. CATALIZADOR ESTRUCTURADO DE Pt/Al2O3 SOBRE UNA ESPUMA DE ACERO INOXIDABLE (AISI 314 PARA LA OXIDACIÓN DE CO

    Directory of Open Access Journals (Sweden)

    Juan P. Bortolozzi

    2011-01-01

    Full Text Available Se obtuvo un catalizador estructurado por recubrimiento de Pt/Al2O3 sobre las paredes de una espuma de acero inoxidable AISI 314. Para estabilizar térmicamente e incrementar la rugosidad de la superficie de la espuma original se realizó un tratamiento a 900°C por 2 h. El soporte, Al2O3, y el metal activo, Pt, se incorporaron por inmersión. Las técnicas de caracterización aplicadas, XRD, LRS y SEM-EDX, permiten concluir que el tratamiento térmico previo indujo la formación de óxido de cromo y de las espinelas Mn1+xCr2-xO4-x y FeCr2O4 como fases principales en las paredes del sustrato. El espesor de la capa formada es cercano a 1 μm y los cristales producidos tienen forma octaédrica. El cubrimiento de alúmina presentó en general una apariencia homogénea, sin interacción con los óxidos formados durante el tratamiento. El Pt se distribuyó de manera uniforme, resultando un catalizador muy activo para la reacción test elegida: oxidación de monóxido de carbono.

  8. Influencia de la soldadura sobre la rotura por tensiones en tubos de acero inoxidable austenitico del tipo 18-11NB(TP347

    Directory of Open Access Journals (Sweden)

    Gutiérrez de Saiz-Solabarria, S.

    2000-06-01

    Full Text Available This work has been undertaken to study the stress cracking failure in various 18Cr11Ni [TP347 (18-11Nb, TP 321 (18-11 Ti, TP304 (18-11 and TP316 (18-11-2] types austenitic stainless steel tubes. The material used was produced hot-rolling at 76,2 mm φ (3"φ x 2,54 mm (1/10" thickness. The study was carried out at 593ºC and applied stress of 50 Ton/in2.

    Se estudia el efecto de la soldadura sobre la rotura por tensiones en tubos de acero inoxidable austenítico estabilizado con Nb o Ti de los tipos 18-11Nb (TP 347 y 18-11Ti (TP 321 así como sin estabilizar del tipo 18-11 (TP 304 y con Mo del tipo 18-11-2 (TP 316. Los tubos, en todos los casos, son de dimensiones 76,2 mm (3” φ x 2,54 mm (1/10” de espesor y la tensión aplicada (σ de 10 Ton/in2, para una temperatura de servicio de 593ºC.

  9. Corrosión en caliente de un acero inoxidable 304h para calderas en presencia de sales fundidas de vanadatos y sulfatos

    Directory of Open Access Journals (Sweden)

    Sonia Rincón

    2003-01-01

    Full Text Available El presente trabajo busca indagar y establecer el tipo de mecanismo de daño que sufre el acero inoxidable 304H en contacto con depósitos de sal fundida, junto con un estudio preliminar de la cinética de la corrosión. Para ello, se analizarán los depósitos fundidos, la composición química de éstos y se medirá la pérdida de material luego de ser sometido a períodos continuos de ataque, con el uso de la técnica gravimétrica en crisol. Con esto se pretende conocer las variables que influyen directamente sobre el deterioro del acero 304H, para en un futuro, adoptar medidas predictivas y/o preventivas que incrementen su vida útil, aumentando de ésta manera la eficiencia de las calderas y disminuyendo el tiempo entre paradas programadas.

  10. Nitrocarburación mediante el proceso TENIFER QDQ de aceros inoxidables austeníticos estabilizados : caracterización química y estudio de su comportamiento frente al desgaste y la corrosión

    OpenAIRE

    Bellas Muiño, Leonardo

    2016-01-01

    [Resumen]La nitrocarburación en baño de sales se utiliza para mejorar las propiedades tribológicas de los aceros inoxidables. Sin embargo, la aparición de carburos y nitruros de elementos de aleación en la capa externa puede tener efectos contraproducentes para su resistencia a la corrosión. Por este motivo, el proceso TENIFER®QPQ introduce una etapa de oxidación a altas temperaturas con objeto de formar una capa de magnetita (Fe3O4) que incrementa la resistencia a la corrosión...

  11. Estudio de electrodeposición de cobre sobre electrodos porosos de grafito y acero inoxidable vía SEM-DRX y análisis de imagen

    OpenAIRE

    Constanzo-R., Robinson; Pagliero-N., Antonio; Vergara-G., Froilán

    2014-01-01

    El objetivo de este trabajo fue realizar un análisis cualitativo de la distribución de un electrodepósito de cobre en el interior de electrodos porosos (EP) de acero inoxidable y carbono grafito. Para ello, se realizaron pruebas de electrodepositación de cobre a nivel de laboratorio, con un posterior análisis de cortes de muestras de acero y grafito vía Microscopía Estereoscópica, Microscopía SEM-DRX y Análisis de Imagen, los cuales mostraron que el cobre no se deposita en forma uniforme al i...

  12. Efecto de las variables del procedimiento de soldadura sobre las propiedades mecánicas y la resistencia a la corrosión en depósitos de soldadura de aceros inoxidables supermartensíticos

    OpenAIRE

    Zappa, Sebastián

    2011-01-01

    La soldadura de los aceros inoxidables martensíticos ha presentado ciertas dificultades y el uso de tratamientos térmicos es normalmente obligatorio. Las razones son diferentes para cada grado de acero, pero en general, es común obtener alta dureza y baja tenacidad en la zona afectada por el calor. Este hecho está asociado con la estructura martensítica en sí misma y el contenido de carbono. Una posible solución a este problema y para alcanzar determinadas propiedades en condición como soldad...

  13. Separación selectiva de hierro y cromo de las lejías agotadas del decapado de acero inoxidable

    Directory of Open Access Journals (Sweden)

    Gálvez, J. L.

    2005-12-01

    Full Text Available Stainless steel spent pickling baths are very complex solutions of metals and acids (HNO3 and HF and are a very important environmental concern. Several processes have been developed for acid recovery (free and bounded acid with techniques like acid retardation, solvent extraction, evaporation and dialysis diffusion. In these processes, metallic content is precipitated and treated for its disposal. We have developed a process that permits the separation of metals by means of a selective precipitation, induced by adding free fluoride. Iron (Fe and chromium (Cr precipitate as pentafluorides and nitrogennickel (Ni remains in solution. After this stage, complex fluorides can be hydrolized with alkali to give iron and chromium hydroxides, releasing fluoride in solution

    Los baños ácidos agotados del decapado de acero inoxidable son disoluciones muy complejas debido al alto contenido de metales y ácidos (HNO3 y HF, por lo que constituyen un grave problema medioambiental. Existen tratamientos comerciales para la recuperación del ácido (libre o complejado que se basan en técnicas de retardo ácido, extracción con disolventes, evaporación o membranas. En estos procesos el contenido metálico es precipitado y tratado como un residuo. El grupo de investigación formado por los autores del presente trabajo ha desarrollado un procedimiento que permite el aprovechamiento de dichos metales mediante su recuperación selectiva con una técnica de precipitación modificada inducida por fluoruro libre. Se consigue la precipitación de hierro (Fe y cromo (Cr como pentafluoruros (pH 3-4,5 dejando el níquel en disolución. Posteriormente, los fluoruros complejos son hidrolizados con álcali dando lugar a hidróxidos de hierro y cromo, mientras que el fluoruro es redisuelto.

  14. Caracterización de una nueva membrana cerámica de microfiltración con soporte de tejido en acero inoxidable flexible

    Directory of Open Access Journals (Sweden)

    Palacio, L.

    1999-04-01

    Full Text Available In this work we present the characterization of a ceramic flexible membrane, made by SynthesechemieⓇ, with a nominal pore size of 0.45 μm. This membrane consists in an α-alúmina porous support which has an embedded stainless steel metallic network, onto what a selective layer of titanium dioxide has been deposited. Membrane characterization has been realized with the aid of several techniques as: atomic force microscopy (AFM, air-liquid displacemente porosimetry and mercury porosimetry. Each tecnique giving information on different aspects: surface characteristics, bulk pores and active pores. Although the total pore size distribution is rather broad, the active pores (those opened to flux present a narrow distribution with a mean pore size very close to the manufacturer nominal value.

    En este trabajo se ha abordado la caracterización de una membrana cerámica de microfiltración flexible, fabricada por SynthesechemieⓇ con tamaño de poro nominal de 0.45 μm. Ésta consiste en un soporte poroso de α-alúmina que posee un armazón formado por una red metálica de acero inoxidable sobre el cual existe una capa selectiva de óxido de titanio. La caracterización de la membrana ha sido realizada con diversas técnicas como: microscopia de fuerza atómica (AFM, porometría de desplazamiento aire-líquido y porosimetría de mercurio. Cada técnica da información sobre aspectos diferentes: superficie, poros totales y poros activos. Si bien la distribución total de tamaños de poro es bastante ancha, los poros activos (abiertos al flujo presentan una distribución de tamaños estrecha con un valor medio muy próximo al nominal.

  15. Recubrimientos de aluminio-silicio realizados por deposición química de vapor en lecho fluidizado sobre el acero inoxidable AISI 316

    Directory of Open Access Journals (Sweden)

    José Luddey Marulanda Arevalo

    2013-12-01

    Full Text Available Los recubrimientos de aluminio-silicio fueron depositados sobre el acero inoxidable AISI 316 mediante deposición química de vapor en lecho fluidizado (CVD-FBR, en el rango de temperaturas de 540 a 560 ºC, utilizando un lecho formado por 2,5 g de silicio y 7,5 g de aluminio en polvo, y 90 g de lecho inerte (Alúmina, el cual se hizo fluidizar con Ar. Como gases activadores se usó una mezcla de HCl/H2, en relaciones de 1/10 a 1/16. Además, se varió el tiempo de deposición de los recubrimientos de 45 minutos a 1.5 horas, con una relación en volumen de 50% de gases activos y 50% de gases neutros. Se realizó una simulación termodinámica con la ayuda del programa informático Thermocalc, para obtener información de la posible composición y cantidad de material depositado, para las condiciones seleccionadas. En los recubrimientos se encuentran FeAl2Si, Fe2Al5 y FeAl2. Los recubrimientos aluminio-silicio fueron tratados térmicamente, para mejorar sus propiedades mecánicas y su comportamiento frente a la oxidación, por la interdifusión de los elementos de aleación, ya que el tratamiento térmico hace que el aluminio difunda hacia el substrato, y el hierro difunda hacia la superficie del recubrimiento, logrando la transformación de los compuestos anteriores en FeAl, Al2FeSi, Cr3Si, AlCrFe y AlFeNi.

  16. Influencia del material de aporte en la resistencia a corrosión por picadura en uniones soldadas de un acero inoxidable dúplex 2205

    Directory of Open Access Journals (Sweden)

    Múnez, C. J.

    2007-08-01

    Full Text Available In this work, it has been studied the pitting corrosion resistance of welding duplex stainless steel 2205. Unions were made by GMAW process with different fillers: duplex ER 2209 and two austenitic (ER 316LSi and ER 308LSi. The microstructure obtained with the duplex ER 2209 filler is similar to the duplex 2205 base material, but the unions produced with the austenitic fillers cause a decrease of the phases relation a/g. To evaluate the influence of the filler on the weld, the pitting corrosion resistance was determined by electrochemical critical pitting temperature test (TCP and the mechanical properties by the hardness. The phases imbalance produced for the dissimilar fillers bring out a variation of the pitting corrosion resistance and the mechanical properties.

    En este trabajo se ha estudiado la resistencia a la corrosión localizada por picadura, de soldaduras realizadas sobre un acero inoxidable dúplex 2205. Se hicieron uniones mediante el proceso GMAW, utilizando como material de aporte un hilo dúplex ER 2209 y dos austeníticos ER 316LSi y ER 308LSi. Metalúrgicamente, se observa como para el hilo ER 2209 las microestructuras que se obtienen son similares a la del dúplex 2205, mientras que en las uniones con hilo austenítico, pueden verse microestructuras muy diferentes en las que la relación de fases a/g disminuye. Al evaluar la resistencia a la corrosión por picadura, mediante la Temperatura Crítica de Picadura (TCP, se comprobó como el desequilibrio entre las fases, generado por el aporte, provoca la variación en la resistencia a la corrosión localizada por picadura. También, se estudió la variación en las propiedades mecánicas del material mediante ensayos de dureza.

  17. Some pitfalls in welding of duplex stainless steels Algumas armadilhas na soldagem de aços inoxidáveis duplex

    Directory of Open Access Journals (Sweden)

    Demian J. Kotecki

    2010-12-01

    Full Text Available Duplex stainless steels (DSS, including super duplex stainless steels {SDSS} have proven to be very useful engineering materials, albeit with somewhat different welding requirements than those of the more familiar austenitic stainless steels. Despite a generally good track record in welding of duplex stainless steels, certain pitfalls have been encountered with enough frequency that they deserve review. Inappropriate base metal specification often leads to unsuitable heat affected zone (HAZ properties. Autogenous fusion zones are also of concern. This issue centers around nitrogen limits. The most frequently encountered is applying the UNS S31803 composition for 2205 DSS, instead of the S32205 composition. Inappropriate welding heat input arises most frequently with SDSS. While 0.5 to 1.5 kJ/mm is a normal heat input recommendation for SDSS, either a root pass or many small beads towards the low end of this heat input range tends to result in precipitation and/or secondary austenite formation in weld metal subjected to repeated thermal cycles from multiple weld passes. Inappropriate PWHT occurs when the enhanced nickel filler metals (typically 9% Ni are used. DSS are not normally given PWHT, but extensive forming of heads, for example, or repair welding of castings, may require a postweld anneal. Specifications such as ASTM A790 and A890 call for annealing at 1040ºC minimum, and the fabricator tends to use temperatures close to that minimum. However, the enhanced nickel filler metals require higher temperatures to dissolve sigma phase that forms during heating to the annealing temperature.Aços inoxidáveis duplex (AID, incluindo os aços super duplex, AISD provaram ser materiais de engenharia muito úteis, embora com requerimentos de soldagem em alguma medida diferentes daqueles dos aços inoxidáveis austeníticos mais usuais. Apesar do histórico geralmente bom dos aços inoxidáveis duplex quanto a soldagem, algumas dificuldades têm sido

  18. Análisis de la resistencia a la corrosión de barras corrugadas de acero inoxidable en medios acuosos que simulan el hormigón

    Directory of Open Access Journals (Sweden)

    Belzunce, F. J.

    2004-04-01

    Full Text Available The corrosion behaviour of stainless steel reinforced bars used in civil engineering was studied. Different electrochemical tests were performed using several stainless steel bars (austenitic and duplex, hot and cold rolled, in the presence of a solution, which simulates the contact with salt contaminated concrete. The corrosion rates were determined and also their behaviour against localized corrosion (pitting.

    Se ha realizado un estudio sobre la resistencia a la corrosión de barras corrugadas de acero inoxidable utilizadas en construcción civil para armar el hormigón. Con este objeto se han realizado diferentes ensayos electroquímicos en presencia de un medio acuoso básico, que simula el contacto con hormigón contaminado con sal, y se ha determinado la velocidad de corrosión y la resistencia a la formación de picaduras de diferentes calidades de aceros inoxidables (austeníticos y dúplex, tanto conformadas en caliente como en frío.

  19. Decapado de un acero inoxidable austenítico mediante mezclas ecológicas basadas en H2O2 - H2SO4 - iones F-

    Directory of Open Access Journals (Sweden)

    Narváez, L.

    2013-04-01

    Full Text Available This study reports the pickling of 316L stainless steel using mixtures of hydrogen peroxide (H2O2, sulphuric acid (H2SO4 and fluoride ions as hydrofluoric acid (HF, sodium fluoride (NaF and potassium fluoride (KF. The decomposition of H2O2 in the mixtures was assessed at different temperatures 25 °C to 60 °C, with ferric ion contents from 0 to 40 g/l. According to the results obtained, were established the optimal condition pickling at 20 g/l of ferric ions, 25 °C and p-toluensulphonic acid as stabilizer of H2O2. The HF pickling mixture was the only capable to remove totally the oxide layer from the 316L stainless steel after 300 s. The fluoride salts pickling mixtures only remove partially the oxide layer (20 to 40 % aprox. after 300 s. When the pickling time was increased until 1200 s, the removal percentages were around to 80 %.En este estudio se presenta el decapado del acero inoxidable austenítico 316L utilizando mezclas de peróxido de hidrógeno (H2O2/ácido sulfúrico (H2SO4/iones fluoruro; los iones fluoruro provienen del ácido fluorhídrico (HF, fluoruro de sodio (NaF y fluoruro de potasio (KF. La estabilidad del H2O2 fue valorada modificando las concentraciones del ión férrico de 0 a 40 g/l y las temperaturas de 25 °C a 60 °C en las mezclas decapantes. Se establecieron las condiciones óptimas de decapado utilizando 20 g/l de iones férrico a 25 °C empleando el ácido p-toluensulfónico como estabilizante del H2O2. La mezcla que contenía HF fue la única capaz de eliminar completamente los óxidos superficiales del acero a tiempos de 300 s. Las mezclas a base de sales fluoradas eliminaron parcialmente los óxidos (20 y 40 % aprox. en 300 s. Al incrementar el tiempo de decapado hasta 1200 s se obtuvieron porcentajes de eliminación alrededor de un 80 %.

  20. Efecto del contenido de azufre y del grado de desoxidación sobre la ductilidad en caliente de aceros inoxidables austeníticos resulfurados en estado de solidificación

    Directory of Open Access Journals (Sweden)

    Botella, J.

    1998-05-01

    Full Text Available The manufacture of free machining austenitic stainless steels features a specific drawback derived from their high sulphur content, which is needed for generating, into the austenitic matrix, inclusions to optimize the different machining operations. However, sulphur has a harmful effect on hot workability. This paper deals with assessing the effect of sulphur content and deoxidation level on the hot ductility of resulphurized austenitic stainless steels in as cast condition. Hot tensile tests were conducted on a Gleeble machine, at temperatures between 1,150 and 1,250°C, studying a ductility factor as a function of sulphur content, deoxidation degree, as well as type, size and distribution of sulfides. Results point out the harmful effect of increasing sulphur and oxygen contents on the hot workability of resulphurized austenitic stainless steels, and the need to control carefully the level of oxides of these steels.

    La fabricación de aceros inoxidables austeníticos de alta maquinabilidad presenta una problemática específica derivada de su elevado contenido de azufre; elemento necesario para generar en la matriz austenítica inclusiones que faciliten las diferentes operaciones de mecanizado, pero perjudicial en cuanto al deterioro que produce en la deformabilidad en caliente. Este artículo describe el estudio realizado para evaluar el efecto del contenido de azufre y el grado de desoxidación sobre la ductilidad en caliente de aceros inoxidables austeníticos resulfurados, partiendo de una estructura de solidificación (as cast condition. Se realizaron ensayos de tracción en un sistema Gleeble, a temperaturas entre 1.150 y 1.250°C, analizándose el parámetro de ductilidad en función del contenido de azufre, nivel de desoxidación, y del tipo, tamaño y distribución de los sulfuros presentes. Los resultados ponen de manifiesto el efecto perjudicial de los contenidos de azufre y oxígeno sobre la deformabilidad en

  1. Análisis experimental del desgaste entre UHMWPE y acero inoxidable 316l empleados en la manufactura de prótesis coxofemorales

    Directory of Open Access Journals (Sweden)

    Ricardo Gustavo Rodríguez Cañizo

    2010-07-01

    Full Text Available Título en inglés: Experimental wear analysis of UHMWPE and stainless 316l used in the manufacturing of coxofemoral prosthesis. Resumen La causa más común de falla en prótesis coxofemorales es el aflojamiento entre los componentes que conforman el sistema, de manera específica la copa acetabular y la cabeza femoral. En esta investigación se presenta un análisis tribológico del desgaste en los componentes mencionados, ya que cuando las superficies en contacto se desgastan, la funcionalidad mecánica del sistema se compromete, debido al cambio de geometría de los mismos, dando como resultado un juego mecánico entre la copa y la cabeza. Los materiales considerados en este estudio son el polietileno de ultra elevado peso molecular (UHMWPE, por sus siglas en inglés para la copa acetabular, y acero inoxidable 316L para la cabeza femoral. Esta combinación de materiales representa hoy en día la recomendación más usual por parte de los cirujanos para pacientes de la tercera edad. La tasa anual de desgaste se determinó de manera experimental y se cuantificó la cantidad de material desprendido durante el contacto. Se establecieron las condiciones de carga de forma analítica, considerando las que actúan sobre la cabeza femoral a lo largo del área de desgaste durante la marcha humana. Posteriormente, se realizó el análisis experimental de desgaste utilizando una máquina tribológica de configuración perno-sobre-disco (pin-on-disk, diseñada de manera específica para este estudio. Las pruebas para determinar la pérdida volumétrica de los componentes se realizaron bajo tres condiciones de operación: en seco, lubricada con agua destilada y lubricada con suero bovino. El marco experimental considerado consistió en pernos de UHMWPE sobre discos de acero inoxidable 316L simulando el desgaste equivalente a diez años de uso de la prótesis. Finalmente, de los resultados obtenidos se puede establecer que el desgaste y la cantidad de part

  2. Caracterización mecánica de recubrimientos de aluminio por CVD-FBR sobre aceros inoxidables y resistencia a la oxidación en vapor de agua

    OpenAIRE

    Diego Pérez-Muñoz; José Luddey Marulanda-Arévalo; Juan Manuel Meza-Meza

    2015-01-01

    Los recubrimientos de aluminio depositados sobre el acero inoxidable austenítico AISI 317 por Deposición Química de Vapor en Lecho Fluidizado (CVD-FBR) presentan a altas temperaturas una reducción de la velocidad de corrosión de más de 80 veces. Se realizó la caracterización mecánica de los recubrimientos por medio de microdureza, nanoindentación, para conocer cómo se vieron afectas las propiedades mecánicas (en especial la dureza y el módulo de Young) del recubrimiento y del sustrato luego d...

  3. Resistência à corrosão de aços inoxidáveis em solução sintética de condensado de álcool combustível

    OpenAIRE

    Menezes, Marcela Rabelo

    2010-01-01

    A necessidade de atender as exigências impostas por órgãos ambientais no que se refere à emissão de poluentes gasosos e à demanda dos consumidores por veículos mais econômicos e mais duráveis, principalmente no que diz respeito à maior resistência à corrosão, tem promovido pesquisas para a substituição de materiais tradicionais nos sistemas de exaustão de veículos procurando atingir um custo-benefício favorável. Nesse contexto estão inseridos os aços inoxidáveis que têm elevadas resistência m...

  4. Optimización topológica y fabricación aditiva de un soporte aeronáutico mediante sinterizado láser de acero inoxidable 15-5PH

    OpenAIRE

    Marchal Montes, Álvaro

    2016-01-01

    El objetivo de este trabajó será la aplicación de la optimización topológica a un soporte usado en el sector aeronáutico para reducir su masa que posteriormente se fabricará mediante fabricación aditiva con tecnología DMLS (Direct Metal Laser Sintering) en acero inoxidable 15-5PH. Para llegar a una buena optimización topológica será necesario estudiar todos los caminos de optimización posibles hasta llegar a una correcta mediante softwares adecuados además de adaptarla a la fabricación ad...

  5. Influência do nitrogênio adicionado por SHTPN na resistência à erosão por cavitação do aço inoxidável martensítico

    OpenAIRE

    Maftoum, Ricardo de Almeida

    2013-01-01

    Muitos estudos são realizados para melhorar a resistência à erosão por cavitação dos aços. Entre estes estudos, está a utilização de aços inoxidáveis enriquecidos com nitrogênio na superfície. O presente trabalho estudou o uso da técnica SHTPN (Solution Heat Treatment after Plasma Nitriding), que consiste em duas etapas. Primeiro utiliza-se a nitretação a plasma, para inserir o nitrogênio no material. Na sequência realiza-se o tratamento térmico de solubilização, para que o nitrogênio fique e...

  6. PROTECCIÓN CONTRA LA CORROSIÓN EN SALES FUNDIDAS DE UN ACERO HOT ROLLED, EN EL RANGO DE TEMPERATURAS DE 400 ºC-600 ºC, RECUBIERTO POR ROCIADO TÉRMICO CON ACERO INOXIDABLE 312

    Directory of Open Access Journals (Sweden)

    JOSE LUDDEY MARULANDA

    2009-01-01

    Full Text Available Se evaluó la corrosión por sales fundidas mediante la técnica gravimétrica en un acero de bajo carbono tipo hot rolled, rociado térmicamente con una aleación de acero inoxidable tipo 312, con el equipo Rototec, en una mezcla de sal 20% Na2SO4 - 80% V2O5, entre 400ºC - 600ºC, durante tiempos de 1-7-22 horas. Los resultados mostraron una moderada protección de la capa rociada térmicamente y se presentó alta degradación en el recubrimiento a 600ºC. Se concluyó que la velocidad de corrosión aumenta con la temperatura y disminuye con el tiempo de exposición.

  7. Oxidación en vapor de agua a 700 ºC y 750 ºC del acero inoxidable AISI 317 recubierto con aluminio por CVD-FBR.

    OpenAIRE

    Jose L. Marulanda; Saul I. Castañeda; Aduljay Remolina

    2014-01-01

    Se realizó la oxidación del acero inoxidable austenítico AISI 317 recubierto con aluminio por deposición química de vapor en lecho fluidizado, a temperaturas de 700 °C y 750ºC, en un ambiente con 100% vapor de agua, para evaluar su comportamiento. Se realizaron curvas de ganancia de masa y las películas de óxidos se analizaron por medio de SEM y difracción de rayos X, para observar la morfología de los óxidos. Se realizó la simulación termodinámica del proceso de oxidación en vapor de agua de...

  8. Um novo fio de aço inoxidável para aplicações ortodônticas A new stainless steel wire for orthodontic purposes

    Directory of Open Access Journals (Sweden)

    André Itman Filho

    2011-08-01

    Full Text Available OBJETIVO: desenvolver uma metodologia para fabricação de fios ortodônticos de aço inoxidável austeno-ferrítico SEW 410 Nr. 14517 por meio dos processos convencionais de laminação e trefilação. MÉTODOS: o aço austeno-ferrítico foi elaborado em um forno elétrico de indução. A qualidade dos fios foi avaliada por ensaios de tração e medidas de microdureza. A ductilidade e a manuseabilidade foram analisadas por meio da confecção de componentes ortodônticos. RESULTADOS E CONCLUSÕES: os valores encontrados mostraram que os fios de aço inoxidável austeno-ferrítico atenderam às normas BS 3507:1976 e ISO 5832-1, e apresentaram ótima ductilidade para confecção de componentes ortodônticos com dobras complexas.OBJECTIVE: To develop a method to manufacture austenitic-ferritic stainless steel orthodontic wires (SEW 410 Nr. 14517 using conventional rolling and wiredrawing processes. METHODS: Austenitic-ferritic steel was produced in an induction furnace. Traction trials and microhardness measurements were used to evaluate wire quality. Orthodontic parts were fabricated to assess ductility and malleability. RESULTS AND CONCLUSIONS: Austenitic-ferritic stainless steel wires meet the BS 3507:1976 and ISO 5832-1 norms and have excellent ductility for the fabrication of orthodontic parts with complex folds.

  9. Influencia de la fase sigma en la laminación en frío de los aceros inoxidables dúplex

    Directory of Open Access Journals (Sweden)

    Fargas, G.

    2004-04-01

    Full Text Available One of the steps in the industrial rolling process of duplex stainless steels is the annealing heat treatment after hot rolling. If this annealing is performed in a temperature range that favours the precipitation of intermetallic phases, the mechanical properties can be modified considerably. The formation of these precipitates has a detrimental effect on the DSS ductility and toughness, so it will be a drawback for further cold rolling. In the present investigation, the effect of the sigma phase during cold rolling of a duplex stainless steel type EN 1.4462 has been studied. To simulate this process, compression tests up to a thickness reduction similar to that performed at industrial level have been done. The testing samples were studied by optical microscopy, SEM (scanning electronic microscopy and TEM (transmission electronic microscopy. Afterwards, some of the annealing conditions were selected in order to carry out cold rolling, using a laboratory scale machine, with the aim to observe if they offered a similar behaviour as that experienced in the compression tests. The results show that only the annealing condition at 975ºC during 10 minutes allows to produce sheets without rolling defects.

    Una de las etapas en el proceso de fabricación industrial de los aceros inoxidables dúplex laminados es el tratamiento térmico de recocido posterior a la laminación en caliente. Si dicho recocido se efectúa en un rango de temperaturas que favorezca la formación de fases intermetálicas, las propiedades mecánicas del material pueden modificarse notablemente. La presencia en la microestructura bifásica de dichos precipitados provoca efectos muy perjudiciales sobre la ductilidad y la tenacidad del material, pudiendo llegar a hacer inviable la posterior etapa de laminación en frío. En el presente trabajo se ha estudiado el efecto sobre el proceso de laminación en frío de la presencia de fase sigma en un acero dúplex tipo E.N. 1

  10. Stainless-Steel-Gadolinium Alloys; Alliages Acier Inoxydable-Gadolinium; Splavy iz nerzhaveyushchej stali i gadoliniya; Aleaciones de Acero Inoxidable-Gadolinio

    Energy Technology Data Exchange (ETDEWEB)

    Copeland, M.; Kato, H. [Albany Metallurgy Research Center, Bureau Of Mines, United States Department of the Interior, Albany, OR (United States)

    1964-06-15

    mineures ont une grande influence sur les structures resultant de traitements equilibrants et sur les possibilites de transformation des aciers. Lorsque le gadolinium est melange a de l 'acier au chrome et au nickel, deux phases mineures, Fe{sub 9}Gd et Ni{sub 7}Gd, fondent a 1080 Degree-Sign C, ce qui impose une limite superieure aux temperatures de traitement a chaud et de transformation. Les auteurs ont pu facilement transformer des alliages comprenant jusqu'a 5 Degree-Sign Io en poids de gadolinium et determiner leurs caracteristiques mecaniques et leur resistance a la corrosion. Ils n'ont observe aucun changement dans les caracteristiques mecaniques de l'acier ou sa resistance a la corrosion par l'eau chaude, lorsqu'ils lui ont ajoute'jusqu'a 3% en poids de gadolinium. En raison des limites imposees aux temperatures de transformation des aciers au chrome et au nickel par le point de fusion des phases mineures, les auteurs ont etudie les effets du gadolinium sur des aciers au chrome. Ils ont releve une seule phase mineure qui fond a 1320 Degree-Sign C en etudiant l 'isoplethe du gadolinium a 10% en poids dans l 'alliage chrome-fer-gadolinium. Cette propriete permettrait d'equilibrer et de transformer ces aciers au gadolinium aux temperatures auxquelles on opere normalement. (author) [Spanish] En vista de la excelente resistencia a la corrosion de los aceros inoxidables y del interes que presenta el gadolinio como veneno nuclear, se han estudiado aleaciones de esos dos metales. El gadolinio fue aleado con aceros inoxidables de tipo AISI-304 y al cromo, y se estudiaron las relaciones de fase, la facilidad de trabajo y las propiedades de estas aleaciones. Se observo que en las aleaciones que contienen bajos porcentajes de gadolinio, los puntos de fusion de las fases menores ejercen un efecto muy marcado sobre las estructuras resultantes de los tratamientos de equilibracion y sobre la facilidad de trabajo de los afceros. Cuando se alea el gadolinio con acerce al cromo

  11. Soldabilidad del acero inoxidable austenitico

    Directory of Open Access Journals (Sweden)

    Pedro Pablo Torres-Medina

    2002-01-01

    Full Text Available This work involves welding stainless steel AISI 321H applying technical specifications according to welding standards, know the properties and phenomena that occur in the base metal and select the appropriate input material to ensure good quality of the process.

  12. Soldagem de um aço inoxidável ferrítico com o processo A-TIG Ferritic stainless steel welding with the A-TIG process

    Directory of Open Access Journals (Sweden)

    Alessandra Gois Luciano de Azevedo

    2009-03-01

    Full Text Available O processo de soldagem TIG com fluxo (processo A-TIG apresenta como principal vantagem a possibilidade de se obter uma maior penetração do cordão de solda empregando os mesmos parâmetros de soldagem do processo TIG convencional. Diversos estudos mostram a influência dos fluxos ativos sobre as características geométricas das soldas em aços inoxidáveis austeníticos, porém pouco se sabe sobre a influência deste processo nas características geométricas e metalúrgicas de cordões de solda em aços inoxidáveis ferríticos. Neste trabalho são aplicados diferentes tipos de fluxo na soldagem de aço inoxidável ferrítico com o objetivo de verificar possíveis influências no perfil do cordão de solda, no seu aspecto visual, na microestrutura, na dureza da zona fundida e na resistência ao impacto (ensaio Charpy. As soldagens "bead-on-plate" foram realizadas sem metal de adição. Foram utilizados seis tipos de fluxo, sendo um óxido elaborado em laboratório (TiO2 e cinco fluxos comerciais. Os resultados mostraram que a utilização do fluxo permite um aumento na penetração com mudanças significativas no aspecto do cordão de solda. Verificou-se ainda que a microestrutura e a dureza do cordão de solda do aço estudado não foram afetadas pelo tipo de fluxo utilizado, com a microestrutura analisada em microscópio óptico. O aço em estudo mostrou um alto grau de fragilidade à temperatura ambiente.The A-TIG welding process presents as main advantage the possibility of increase in the penetration depth using the same parameters as conventional TIG welding. Many researchers show the influence of the active flux on the weld geometry in austenitic stainless steel, however little it is known of the influence of this process in the weld fillet shape and metallurgic characteristics of the weld fillet in ferritic stainless steel. In this work different types of flux are applied with the objective to verify possible influences on the weld

  13. Estudio de la viabilidad de fabricación de un sistema codo (fundición inoxidable ferrítica, GX 260 Cr27-tubo composite (Incolloy 800 HT+Stal 2465 solidario por fusión

    Directory of Open Access Journals (Sweden)

    Gutiérrez de Solabarría, S.

    1995-10-01

    Full Text Available Flying ashes captured by ciclones in the experimental plant for combustion in pressure fluid bed, in Escatrón Power Plant (Zaragoza, Spain, circulate through the gas cleaning system and are evacuated by means of pneumatic transport. The temperature of these ashes is aprox. 800 °C and the relative pressure is up to 8 negative bars relating the outdoor pressure of the transport pipe. The configuration of the pneumatic transport lines is Incolloy 800 HT quality composite tubes lined with Stal 2465 in straight stretches. Regarding direction changes, ferritic stainless casting, quality GX 260 Cr 27 elbows are used. The aim of this work is to study the possibility of manufacturing a solidary system by means of melting between the ferritic stainless casting elbow and the composite pipe.

    Las cenizas volantes captadas por ciclones en la planta experimental de combustión en lecho fluido a presión, de la central térmica de Escatrón (Zaragoza, circulan por el sistema de depuración de gases y son evacuadas mediante transporte neumático. Estas cenizas se encuentran a una temperatura aproximada de 800 °C y a una presión relativa de hasta 8 bares negativos con respecto a la presión en el exterior de la tubería de transporte. Para configurar las líneas de transporte neumático, se utilizan en los tramos rectos tubos composite de calidad Incolloy 800 HT recubiertos interiormente de material Stal 2465. Para los cambios de dirección, se utilizan codos de fundición inoxidable ferrítica de calidad GX 260 Cr 27. El objetivo del presente trabajo es estudiar la viabilidad de fabricación de un sistema solidario por fusión entre el codo de fundición inoxidable ferrítica y la tubería composite.

  14. Simulación del efecto de la irradiación mediante el trabajado en frío y los tratamientos térmicos en dos aceros inoxidables austeníticos

    Directory of Open Access Journals (Sweden)

    de Diego, G.

    1998-10-01

    Full Text Available In the present study, annealed type 304 SS was cold worked and heat treated to simúlate irradiation hardening, ductility loss and grain boundary segregation. Constant Extension Rate Tensile (CERT tests were conducted to reproduce Irradiation Assisted Stress Corrosion Cracking (IASCC in BWR (Boiling Water Reactor environment.

    En este trabajo se simulan los efectos que produce la irradiación, pérdida de ductilidad y segregación de impurezas en borde de grano, mediante trabajado en frío y posterior tratamiento térmico, para aceros inoxidables austeníticos AISI 304. Mediante ensayos de velocidad de extensión constante y en medios similares a los de los reactores de agua en ebullición se intenta relacionar la susceptibilidad a la corrosión bajo tensión con la susceptibilidad a la corrosión asistida por irradiación.

  15. Soldadura TIG de los aceros inoxidables dúplex del tipo 22-05 (Uranus 45N y Avesta. Estudio de la microestructura y de las propiedades mecánicas

    Directory of Open Access Journals (Sweden)

    Gómez de Salazar, J. M.

    1998-05-01

    Full Text Available TIG welding of two different duplex stainless steels is carried out. Arc-discharge on base-material plates by means of the TIG technique without filler metal and varying the energetic conditions (E.N.A. has been performed, A comparative study concerning the microstructural evolution as well as mechanical properties is carried out, The relation between hardness profiles, the microstructural variations and the ferrita δ concentration is established. Further, the above mentioned properties are related to the E.N.A. for each welded joint.

    Se estudia la soldadura TIG de dos aceros inoxidables dúplex. Para ello, se ha descargado un arco sobre las chapas de material base mediante la técnica TIG, sin aportación de material y variando las E.N.A. Se realiza un estudio comparativo de la evolución microestructural, así como de las propiedades mecánicas. Se establece la relación entre los perfiles de dureza obtenidos y la variación microestructural y de la concentración de ferrita δ, así como estas propiedades con el E.N.A, de cada cordón.

  16. Caracterización mecánica de recubrimientos de aluminio por CVD-FBR sobre aceros inoxidables y resistencia a la oxidación en vapor de agua

    Directory of Open Access Journals (Sweden)

    Diego Pérez-Muñoz

    2015-09-01

    Full Text Available Los recubrimientos de aluminio depositados sobre el acero inoxidable austenítico AISI 317 por Deposición Química de Vapor en Lecho Fluidizado (CVD-FBR presentan a altas temperaturas una reducción de la velocidad de corrosión de más de 80 veces. Se realizó la caracterización mecánica de los recubrimientos por medio de microdureza, nanoindentación, para conocer cómo se vieron afectas las propiedades mecánicas (en especial la dureza y el módulo de Young del recubrimiento y del sustrato luego de ser sometidos a la oxidación a alta temperatura. También se hicieron análisis por medio de Microscopia Electrónica de Barrido (MEB, para observar los cambios microestructurales, y de Microscopia de Fuerza Atómica (MFA, para observar cómo varía la topografía y el gradiente de rugosidad en función de la distancia recorrida por la punta del cantiléver durante los barridos.

  17. Electrodos austeníticos inoxidables semisintéticos para la soldadura manual por arco eléctrico: Una variante económica para las pequeñas y medianas empresas (PIME. // Semi-synthetic austenitics stainless steel electrodes for shielded metal arc welding: A

    Directory of Open Access Journals (Sweden)

    A. Paz Iglesias

    2002-09-01

    Full Text Available En el presente trabajo se brinda una valoración económica para la producción de electrodos austeníticos inoxidables tiposE308L, E309, E312 y E316L en las pequeñas y medianas empresas (PIME. Lo significativo de la presente valoración esque se brindan los resultados obtenidos al fabricar los electrodos de forma semisintética; es decir, utilizando un solo tipo dealambre inoxidable (308L y añadiendo las ferroaleaciones necesarias en el revestimiento. Los resultados que se muestranestán basados en las experiencias de investigación, producción y comercialización de una planta con capacidad para 200toneladas al año, a la cual le es muy difícil insertarse en el mercado utilizando los mismos procedimientos tecnológicos yfinancieros de una gran empresa con grandes capitales y recursos.Palabras claves: Electrodos austeníticos inoxidables, electrodos sintéticos, ferroaleaciones, electrodossemisintéticos, electrodos convencionales, metal depositado.___________________________________________________________________Abstract.This paper offers an economic valuation for the production of stainless electrodes type E308L, E309, E312 and E316L,for small and middle companies (PIME. The significant part of the present valuation gives the results obtained in theproduction of semi-synthetic electrodes; using just one type of stainless wire (308L and adding the ferroalloys neededin the coat. The results shown are based on investigation experiences, production and trading of companies with acapacity for 200 T/year, so it is very difficult to enter in the market using the same technological procedures of a bigcompany with higher capital and financial resources.Key words: Nonrusting austenistic electrodes, sintetic electrodes, semisintetic electrodes, iron alloy,conventional electrodes, metal deposition.

  18. Evaluación del comportamiento estructural y de resistencia a la corrosión de armaduras de acero inoxidable austenítico AISI 304 y dúplex AISI 2304 embebidas en morteros de cemento Pórtland

    Directory of Open Access Journals (Sweden)

    Medina, E.

    2012-12-01

    Full Text Available The mechanical and structural behaviour of two stainless steels reinforcements, with grades austenitic EN 1.4301 (AISI 304 and duplex EN 1.4362 (AISI 2304 have been studied, and compared with the conventional carbon steel B500SD rebar. The study was conducted at three levels: at rebar level, at section level and at structural element level. The different mechanical properties of stainless steel directly influence the behaviour at section level and structural element level. The study of the corrosion behaviour of the two stainless steels has been performed by electrochemical measurements, monitoring the corrosion potential and the lineal polarization resistance (LPR, of reinforcements embedded in ordinary Portland cement (OPC mortar specimens contaminated with different amount of chloride over one year time exposure. Both stainless steels specimens embedded in OPC mortar remain in the passive state for all the chloride concentration range studied after one year exposure.

    Se ha evaluado el comportamiento mecánico y estructural de dos aceros inoxidables corrugados, el austenítico EN 1.4301 (AISI 304 y el dúplex EN 1.4362 (AISI 2304, y se han comparado con el tradicional acero al carbono B500SD. El estudio se ha realizado en tres niveles: a nivel de barra, de sección y de pieza. Las diferentes características mecánicas de los aceros inoxidables condicionan el comportamiento a nivel de sección y de pieza estructural. El estudio del comportamiento frente a la corrosión de los dos aceros inoxidables se ha realizado mediante mediciones electroquímicas monitorizando el potencial de corrosión y la resistencia de polarización de armaduras embebidas en probetas de mortero contaminado con diferentes concentraciones de cloruros durante un tiempo de exposición de un año. Ambos aceros inoxidables permanecen en estado pasivo en las probetas para todos los contenidos de cloruros.

  19. Desarrollo de un modelo matemático de diferencias finitas para el análisis del campo de temperaturas en la soldadura por arco de chapas finas de acero inoxidable

    Directory of Open Access Journals (Sweden)

    Miguel, V.

    2010-12-01

    Full Text Available This work develops a finite difference method to evaluate the temperature field in the heat affected zone in butt welding applied to AISI 304 stainless steel thin sheet by GTAWprocess. A computer program has been developed and implemented by Visual Basic for Applications (VBA in MS-Excel spreadsheet. The results that are obtained using the numerical application foresee the thermal behaviour of arc welding processes. An experimental methodology has been developed to validate the mathematical model that allows to measure the temperature in several points close to the weld bead. The methodology is applied to a stainless steel sheet with a thickness lower than 3 mm, although may be used for other steels and welding processes as MIG/MAG and SMAW. The data which has been obtained from the experimental procedure have been used to validate the results that have been calculated by the finite differences numerical method. The mathematical model adjustment has been carried out taking into account the experimental results. The differences found between the experimental and theoretical approaches are due to the convection and radiation heat losses, which have not been considered in the simulation model.With this simple model, the designer will be able to calculate the thermal cycles that take place in the process as well as to predict the temperature field in the proximity of the weld bead.

    En este trabajo se desarrolla un método de diferencias finitas para calcular el campo de temperaturas en la zona afectada por el calor en la soldadura de dos chapas de acero inoxidable AISI 304, soldadas mediante el procedimiento GTAW. Se ha desarrollado un programa informático implementado en libros de cálculo MS-Excel con Visual Basic para Aplicaciones (VBA. Los experimentos modelizados a través de la aplicación numérica predicen el comportamiento térmico de un procedimiento de soldadura. Para la validación del modelo matemático se ha desarrollado un

  20. Resistencia a la oxidación de aleaciones Ni-Cr-Al plaqueadas por láser sobre aceros al carbono e inoxidables austeníticos

    Directory of Open Access Journals (Sweden)

    de Damborenea, J.

    1995-04-01

    Full Text Available Laser surface cladding has been carried out by means of a 5 kW CO2 continuous wave laser on both a mild and a stainless steel. A powder injection technique has been used to deliver a Ni-Cr-Al alloy onto the steel molten pool. After processing, samples were analyzed by optical and scanning electron microscopy in order to know the microstructure and composition of present phases. High temperature corrosion resistance tests were done in an oxidant environment at temperatures of 950 °C. Phase transformations and corrosion behaviour are discussed. A general conclusion is the suitability of these alloys to bear oxidation due to the formation of protective oxide layers on their surface.

    Se realiza un estudio sobre la obtención de recubrimientos de superficie mediante un láser continuo de CO2 de 5 kW de potencia de salida. Mediante la técnica de inyección de partículas, se realizaron plaqueados en superficie de Ni-Cr-Al sobre un acero suave y otro inoxidable de tipo 316. Tras el procesado, se estudió la microestructura de las probetas obtenidas. Posteriormente, se procedió a su ensayo en atmósfera oxidante a 950 °C, observándose la evolución de la microestructura, la formación de las capas de óxido y la cinética del proceso. Como conclusión general, destaca, independientemente de la base sobre la que se obtienen los recubrimientos, la gran resistencia del material a la oxidación, seguramente debida a la formación de capas de alúmina que actúan como barreras frente al ataque del oxidante.

  1. Oxidación en vapor de agua a 700 ºC y 750 ºC del acero inoxidable AISI 317 recubierto con aluminio por CVD-FBR.

    Directory of Open Access Journals (Sweden)

    Jose L. Marulanda

    2014-01-01

    Full Text Available Se realizó la oxidación del acero inoxidable austenítico AISI 317 recubierto con aluminio por deposición química de vapor en lecho fluidizado, a temperaturas de 700 °C y 750ºC, en un ambiente con 100% vapor de agua, para evaluar su comportamiento. Se realizaron curvas de ganancia de masa y las películas de óxidos se analizaron por medio de SEM y difracción de rayos X, para observar la morfología de los óxidos. Se realizó la simulación termodinámica del proceso de oxidación en vapor de agua de los substratos para conocer las posibles fases sólidas y gaseosas que se podrían formar, en presencia de una ambiente con 100% vapor de agua y una atmosfera de presión. La forma de ataque a 750 ºC es similar a 700 ºC, aunque la velocidad de oxidación es mayor, ya que la difusión de los elementos de aleación y las reacciones de oxidación son más rápidas. Los recubrimientos de aluminio tienen una buena resistencia a la oxidación en vapor de agua, ya que forman una capa superficial de Al 2 O 3 , que es compacta y adherente, la cual protege al substrato del ataque corrosivo.

  2. Resistência à corrosão de junta dissimilar soldada pelo processo TIG composta pelos aços inoxidáveis AISI 316L e AISI 444

    Directory of Open Access Journals (Sweden)

    Luis Henrique Guilherme

    2014-03-01

    Full Text Available O aço inoxidável AISI 444 tornou-se uma opção para substituir a liga AISI 316L devido ao seu menor custo e satisfatória resistência à corrosão. Entretanto, o uso da liga AISI 444 no feixe tubular de trocadores de calor acarreta na soldagem de uma junta dissimilar. O presente estudo teve por objetivo avaliar a resistência à corrosão da junta tubo-espelho soldada pelo processo TIG composta pelas ligas AISI 316L e AISI 444. A manufatura das amostras consistiu em replicar o projeto da junta tubo-espelho de trocadores de calor. Realizou-se em juntas soldadas ensaios de sensitização, perda de massa por imersão desde a temperatura ambiente até 90 ºC, e ensaios eletroquímicos de polarização potenciodinâmica nos eletrólitos 0,5 mol/L de HCl e 0,5 mol/L de H2SO4. Os resultados mostraram que a junta dissimilar sofreu corrosão galvânica com maior degradação na zona afetada pelo calor (ZAC do tubo AISI 444. Porém, os mecanismos de corrosão localizada (pite e intergranular demonstraram ser mais ativos para a liga AISI 316L. Conclui-se que a junta dissimilar apresentou melhor resistência à corrosão do que a junta soldada composta unicamente pela liga AISI 316L em temperaturas de até 70 ºC, conforme as condições observadas neste trabalho.

  3. Efecto de la velocidad y ángulo de impacto en la resistencia a corrosión - erosión de aceros inoxidables recubiertos con TiN

    Directory of Open Access Journals (Sweden)

    José Ricardo Cano Rodas

    2004-01-01

    Full Text Available Fueron estudiados los mecanismos de degradación superficial en aceros inoxidables austenítico AISI 304 y martensítico AISI 420, con y sin recubrimiento cerámico de TiN, aplicado mediante técnica de deposición física de vapor PVD por arco pulsado, sometidos a erosión (solución de agua destilada con 30% en peso de partículas de sílice, corrosión (solución ½ M H2SO4 + 3.5% NaCl y efectos sinérgicos corrosión - erosión. Fue construido un dispositivo para realizar los ensayos descritos con la posibilidad de variar la velocidad y el ángulo medio de impacto de las partículas sobre la superficie de las muestras. Marcas características fueron observadas en las superficies desgastadas, siendo la condición de ángulo rasante la de mayor efecto nocivo tanto para las superficies desnudas como para las recubiertas con TiN. El nivel de deterioro superficial aumentó con la velocidad de impacto, al tiempo que se evidenció la importancia de la adherencia de las películas protectoras al substrato para la obtención de una buena resistencia a corrosiónerosión. La sinergia corrosión-erosión presentó, en algunas ocasiones, un efecto positivo para la superficie, ya que el impacto de las partículas duras causó intensa deformación plástica pero no consiguió remover material de la superficie.

  4. Adesão de linhagem selvagem de Streptococcus thermophilus em superfície de aço inoxidável e efeitos da higienização na sua remoção Adhesion of a wild strain of Streptococcus thermophilus onto stainless steel surfaces and the effects of cleaning and sanification on its removal

    Directory of Open Access Journals (Sweden)

    Ana Lourdes Neves GÂNDARA

    2000-04-01

    Full Text Available Linhagem selvagem de Streptococcus thermophilus isolada de leite pasteurizado foi avaliada em modelo experimental quanto a adesão em superfície de aço inoxidável e comportamento frente à limpeza e sanificação. Em leite, a adesão do microrganismo em aço inoxidável foi estudada em 6h de contato a 45°C sob agitação e uma higienização com detergentes alcalino e ácido seguida de sanificação foi utilizada para avaliação do comportamento das células aderidas frente à higienização. Esse microrganismo aderiu a essa superfície produzindo uma carga de 10(4UFC/cm². Após a limpeza alcalina não foram detectadas células aderidas; em seguida a limpeza ácida 6 UFC/cm² ainda foram detectadas. A sanificação com hipoclorito de sódio, após a limpeza, foi suficiente para reduzir a carga de S. thermophilus selvagem aderida ao aço inoxidável. O modelo experimental mostrou-se adequado para o estudo, indicando que a cultura selvagem de Streptococcus thermophilus é produtora de biofilme em superfície de aço inoxidável. A limpeza da superfície de aço inoxidável por detergência alcalina remove mais que 99,9% das células aderidas. Pequenos números de células remanescentes são removidos na detergência ácida o que demonstra a necessidade das diferentes etapas e tipos de detergentes para a eficiência da limpeza. Melhores resultados na remoção desse biofilme são alcançadas com detergência alcalina seguida de detergência ácida e mais eficientemente quando se utiliza uma sanificação complementar com hipoclorito de sódio.A wild strain of Streptococcus thermophilus isolated from pasteurized milk was evaluated using an experimental model with respect to its adhesion onto stainless steel surfaces and its behaviour when submitted to cleansing and sanification. In milk, the adhesion of the microorganism on to stainless steel surfaces was studied after 6 hours of contact at 45°C with agitation, and after a cleansing process

  5. Formação de biofilme por Pseudomonas aeruginosa sobre aço inoxidável em contato com leite e seu controle por óleos essenciais

    Directory of Open Access Journals (Sweden)

    Nádia Nara BATISTA

    2014-01-01

    Full Text Available Objetivo: Avaliar a ação bacteriostática e bactericida de diferentes óleos essenciais sobre células planctônicas de Pseudomonas aeruginosa ATCC 27853, bem como verificar a ação sanitizante, dos óleos essenciais que apresentarem a menor Concentração Mínima Inibitória (CMI, sobre o biofilme formado por esta espécie, Material e Métodos: A ação bacteriostática foi realizada por meio da determinação das CMIs dos óleos de Zingiber officinale, Eugenia caryophyllus, Elettaria cardamomum, Citrus limon e Citrus reticulata v, tangerine, O tempo de morte bacteriana foi determinado utilizando-se as CMIs de cada óleo essencial submetidos a diferentes tempos de contato, O biofilme de P, aeruginosa foi desenvolvido em cupons de aço inoxidável AISI 304 dispostos em placa de Petri contendo leite tratado por Ultra Alta Temperatura (UAT, sendo incubado sob agitação de 70 rpm, a 37 °C/96 horas, Células aderidas foram removidas através de swabs e enumeradas por contagem em placas após submissão a diferentes tratamentos, Resultados: Todos os óleos essenciais apresentaram efeito bacteriostático, se destacando Z, officinale, E, caryophyllus e E, cardamomum, por apresentarem menor CMI, O tempo de morte de P, aeruginosa foi de 10 minutos quando utilizadas soluções a base de E, cardamomum e E, caryophyllus, No entanto, quando testados em biofilme, apenas E, caryophyllus eliminou as células bacterianas viáveis de P, aeruginosa, Conclusão: E, caryophyllus é uma nova alternativa para o controle do biofilme de P, aeruginosa na indústria de alimentos, pois, além de sua alta atividade antimicrobiana, é um composto natural, o que atende as exigências do mercado consumidor.

  6. Estudio de corrosión bajo tensión en los aceros inoxidables 17-4PH y 17-7PH en presencia de NaCl y NaOH (20 % a 90 °C

    Directory of Open Access Journals (Sweden)

    Gaona-Tiburcio, Citlalli

    2000-04-01

    Full Text Available One of the problems that affects to the electric industry is the not programmed stoppages in the power plants, due to the failure of any main component: boiler, turbine and generator. In the turbine, the combined action of a corrosive agent (humid polluted vapor and a mechanical effort generally will result in Stress Corrosion Cracking (SCC. In this work the SCC susceptibility of the precipitation hardening stainless steels 17-4PH and 17- 7PH, thoroughly used in steam turbine blades of power stations is analyzed. The specimens were tested in the presence of NaCl and NaOH (20 % to 90 °C and different pH. The CERT test (Constant Extension Rate Test was used, at 10-6 s-1 supplementing it with electrochemical noise; the aim was to identify the conditions of maximum susceptibility and the performance of the studied materials. The fractographic analysis revealed ductile and brittle fracture. Intergranular crackings, characteristic of the anodic dissolution mechanism of the material was observed. Nevertheless, the main mechanism responsible the failure was hydrogen embrittlement.

    Uno de los problemas que afecta a la industria eléctrica es el de los paros no programados en las plantas generadoras de electricidad, debidos al fallo de algún componente principal: caldera, turbina y generador. En la turbina, la acción combinada de un agente corrosivo (vapor húmedo contaminado y un esfuerzo mecánico, generalmente provocará corrosión bajo tensión (CBT. En este trabajo se analiza la susceptibilidad a la CBT de los aceros inoxidables, endurecibles por precipitación, 17-4PH y 17-7PH, ampliamente usados en alabes de turbina de vapor de centrales termoeléctricas. Las muestras se ensayaron en presencia de NaCl y NaOH (20 % a 90 °C, y distintos valores de pH. Se empleó el ensayo CERT (Constant Extensión Rate Test, a velocidades de 10-6 s-1, complementándolo con ruido electroquímico, buscando

  7. PROPIEDADES MECÁNICAS DE PELÍCULAS HÍBRIDAS (ORGÁNICO-INORGÁNICO SOBRE ACERO INOXIDABLE 304 Mechanical Properties of Hybrid Films (Organic-Inorganic on Stainless Steel 304

    Directory of Open Access Journals (Sweden)

    Jorge H. Bautista-Ruiz

    2011-12-01

    Full Text Available This article shows the creation of ceramic films of the SiO2-TiO2 Organic Polymer hybrid system from Tetraethyl-Orthosilicate (Si (OC2H54 and Titanium Tetrabutoxide (Ti(OBu4 synthesized through the sol-gel method in several volumetric concentrations of precursors. This hybrid system was deposited on AISI 304 stainless steel substrates through the dip-coating technique. Feasibility for obtaining hybrid and homogeneous coatings on this type of substrate and evaluating the surface properties was studies. For such a purpose, the coating microhardness and adhesion were studies. Additionally, the film surface was characterized through the SEM (Scanning Electron Microscopy. The study concluded that characteristics of films change in function of the volumetric amount of precursors used for creating films.Este trabajo muestra la conformación de películas cerámicas del sistema híbrido SiO2-TiO2-Polímero Orgánico, a partir de tetraetil-ortosilicato (Si (OC2H54, y tetra-butoxido de titanio (Ti(OBu4 y sintetizado por el método sol-gel en diferentes concentraciones volumétricas de los precursores. Este sistema híbrido se depositó sobre sustratos de acero inoxidable AISI 304 mediante la técnica de inmersión (dip-coating. Se estudió la viabilidad de obtener recubrimientos híbridos homogéneos sobre este tipo de sustrato y evaluar las propiedades superficiales. Para tal efecto, se estudió microdureza y adhesión del recubrimiento. Adicionalmente, se caracterizó la superficie de las películas por microscopía electrónica de barrido (MEB. Del estudio se concluye que las características de las películas cambian en función de la cantidad volumétrica de los precursores utilizados en la conformación de las mismas.

  8. Aplicación del ensayo miniatura de embutido para la evaluación de la tenacidad a temperaturas criogénicas de aceros inoxidables austeníticos envejecidos isotérmicamente

    Directory of Open Access Journals (Sweden)

    Saucedo-Muñoz, M. L.

    2003-10-01

    Full Text Available Two types of austenitic stainless steels JJl and JNl were isothermally aged at temperatures from 873 to 1173 K for 10 to 1000 min in order to study the microstructural evolution and its effect on fracture toughness at cryogenic temperatures. The Charpy V-Notch (CVN and Small-Punch (SPTesting methods were conducted at 77 K to evaluate the toughness of both solution treated and aged specimens. The fracture energy at 77 K determined for both methods showed a significant decrease with aging time for both steels. A linear correlation between the fracture energies of both methods was found. The intergranular precipitation of carbides and nitrides was responsible for the fracture toughness deterioration. The scanning electron microscope fractographs showed an intergranular brittle fracture and its fraction also increased with aging time and temperature. The presence of a more abundant intergranular precipitation resulted in a more rapid decrease in fracture toughness with aging time in JNl steel due to its higher content of C and N, compared to that of JJl steel.

    Dos tipos de aceros inoxidables austeníticos, JJl y JNl, se envejecieron isotérmicamente a temperaturas entre 873 y 1.173 K por tiempos de 10 a 1.000 min, para estudiar la evolución microestructural y su efecto sobre la tenacidad a la fractura a temperaturas criogénicas. Los métodos de ensayo de impacto Charpy y el ensayo miniatura de embutido se llevaron a cabo a 77 K para evaluar la tenacidad de las muestras tratadas térmicamente. La energía de fractura determinada por ambos métodos mostró una disminución con el tiempo de envejecido para ambos aceros. Se encontró una relación lineal entre ambos valores de energía. La precipitación intergranular de carburos y nitruros fue la responsable de la pérdida de la tenacidad en las muestras envejecidas. La fractografía indicó que la fractura intergranular se incrementa con la temperatura y el tiempo de envejecido. La presencia

  9. Caracterização química e metalográfica dos aços inoxidáveis de implantes removidos de pacientes Chemical and metallographic characterization of stainless steel in implants removed from patients

    Directory of Open Access Journals (Sweden)

    Elison da Fonseca e Silva

    2011-01-01

    Full Text Available OBJETIVO: Este trabalho estudou a composição química e metalográfica (microestrutura, tamanho de grão, teor de inclusões de aços inoxidáveis austeníticos, desenvolvidos para aplicações como biomateriais, utilizados na fabricação de implantes ortopédicos. MÉTODO: Foram analisados doze implantes removidos de pacientes afetados por quadro inflamatório. As análises químicas foram desenvolvidas pelas técnicas Espectrometria de Emissão Ótica e Microanálise por Dispersão de Energia (EDS e o tamanho de grão foi determinado por microscopia ótica e Microscopia Eletrônica de Varredura (MEV conforme norma ASTM E 1382 97. RESULTADOS: Observou-se que, todos os implantes apresentavam tamanho de grão superior ao recomendado pela norma, constatou-se também a presença de ferrita delta em dez dos doze implantes removidos, que de acordo com a norma ASTM F138-92 não deveriam ser percebidas microscopicamente com um aumento de 100 vezes. CONCLUSÕES: Em oito casos existe forte indicação de que as inflamações foram desencadeadas pela corrosão por pite. Nivel de Evidência III, Revisão sistemática de Estudos .OBJECTIVE: This study examines the chemical and metallographic composition (microstructure, grain size, inclusion content of austenitic stainless steel developed as biomaterials for used in the manufacture of orthopedic implants. METHOD: An analysis was carried out of twelve implants removed from patients affected by inflammation. Chemical analyses were carried out using Optical Emission Spectrometry and Energy Dispersive Microanalysis (EDS, and the grain size was determined by optical microscopy and scanning electron microscopy (SEM according to ASTM Standard E 1382 97. RESULTS: It was observed that all the implants had a larger grain size than is recommended by the Standard. The presence of delta ferrite was also observed in ten of the twelve implants removed, which according to ASTM Standard F138-92, should not be perceived

  10. Desenvolvimento da ferrita delta na solda e ZTA resultante de soldagem plasma pulsada em um aço inoxidável supermartensítico Delta-ferrite development in weld and HAZ produced by pulsed plasma arc welding in a supermartensitic stainless steel

    Directory of Open Access Journals (Sweden)

    Sérgio L. Henke

    2013-03-01

    Full Text Available A ferrita delta é considerada uma fase indesejável na microestrutura dos aços inoxidáveis martensíticos haja vista a mesma poder influenciar no desempenho da resistência à fadiga, tenacidade e corrosão sob-tensão. Sendo assim, o objetivo deste trabalho foi investigar o efeito da soldagem plasma pulsada sobre a distribuição e quantidade de ferrita delta em um aço inoxidável supermartensítico. Para tal foram obtidos cordões por meio de fusão superficial sobre uma amostra de aço inoxidável supermartensítico de alta liga utilizando corrente pulsada e convencional. Em seguida foi efetuada a caracterização microestrutural, em especial da ferrita delta, via análises metalográficas por meio de microscopia óptica e eletrônica de varredura . Os experimentos revelaram que, para o mesmo aporte térmico, a pulsação de corrente promoveu a formação de ferrita delta na forma de bandas ao longo do cordão de solda e redução significativa desta fase na ZTA quando comparada à soldagem convencional.The objective of this study was to investigate the effect of pulsed plasma welding on the distribution and amount of delta ferrite which is considered an undesirable phase in a supermartensitic stainless steel. For such weld beads have been obtained by melting the surface of a sample of a high-alloy supermartensitic stainless steel using pulsed and conventional current. Microstructural characterization, especially of delta ferrite, was performed by metallographic analysis by means of optical microscopy and scanning electron microscopy. The experiments showed that for the same heat input, pulsed current promoted the formation of delta ferrite in the form of bands along the weld bead and caused a significant reduction of this phase in HAZ as compared to conventional welding.

  11. Stress corrosion (Astm G30-90 standard) in 08x18H10T stainless steel of nuclear fuel storage pool in WWER reactors; Corrosion bajo esfuerzo (Norma ASTM G30-90) en acero inoxidable 08x18H10T de piscinas de almacenamiento de combustible nuclear en reactores V.V.E.R

    Energy Technology Data Exchange (ETDEWEB)

    Herrera, V.; Zamora R, L. [Centro de Estudios Aplicados al Desarrollo Nuclear (Cuba)

    1997-07-01

    At the water storage of the irradiated nuclear fuel has been an important factor in its management. The actual pools have its walls covered with inoxidable steel and heat exchangers to dissipate the residual heat from fuel. It is essential to control the water purity to eliminate those conditions which aid to the corrosion process in fuel and at related components. The steel used in this research was obtained from an austenitic inoxidizable steel standardized with titanium 08x18H10T (Type 321) similar to one of the two steel coatings used to cover walls and the pools floor. the test consisted in the specimen deformation through an U ply according to the Astm G30-90 standard. The exposition of the deformed specimen it was realized in simulated conditions to the chemical regime used in pools. (Author)

  12. Fricção em braquetes gerada por fios de aço inoxidável, superelásticos com IonGuard e sem IonGuard Friction force on brackets generated by stainless steel wire and superelastic wires with and without IonGuard

    Directory of Open Access Journals (Sweden)

    Luiz Carlos Campos Braga

    2011-08-01

    Full Text Available OBJETIVO: o objetivo deste estudo foi verificar a fricção no braquete (Roth, Composite, 10.17.005, 3,2mm, largura 0,022" x 0,030", Torque -2° e angulação +13°, Morelli®, Brasil, utilizando fios ortodônticos retangulares de 0,019" x 0,025" de aço inoxidável (Morelli®, Brasil e de níquel-titânio superelásticos Bioforce com IonGuard e sem IonGuard (Bioforce, GAC®, EUA. MÉTODOS: foram utilizados 24 conjuntos braquetes/segmento de fio, divididos em 3 grupos de acordo com o fio. Cada conjunto braquete/segmento de fio foi testado 3 vezes e obtida uma média. Os ensaios foram realizados em máquina universal de ensaios EMIC DL2000®. Os dados foram submetidos à Análise de Variância com significância de 95%. RESULTADOS: o fio retangular Bioforce com IonGuard apresentou fricção significativamente menor que o Bioforce sem IonGuard, porém sem diferença do fio de aço inoxidável. Entretanto, o coeficiente de variação dos fios Bioforce com e sem IonGuard foi menor que o do fio de aço inoxidável. CONCLUSÃO: os fios retangulares de 0,019" x 0,025" Bioforce com IonGuard apresentam menor fricção que o fio Bioforce sem IonGuard, sem diferença para o fio de aço inoxidável.OBJECTIVE: The aim of this study was to evaluate the friction forces on brackets (Roth, Composite, 10.17.005, 3.2 mm, width 0.022" x 0.030 ", Torque -2° and angulation +13°, Morelli®, Brazil, with stainless steel orthodontic rectangular wire (Morelli®, Brazil and nickel titanium superelastic Bioforce wires with and without IonGuard (Bioforce, GAC®, USA. MATERIAL AND METHODS: Twenty-four brackets/wire segment combinations were used, distributed into three groups according to the orthodontic wire. Each bracket/wire segment combination was tested three times. The tests were performed in a universal testing machine Emic DL2000®. The data was submitted to ANOVA one way followed by Tukey's post hoc test (p<0.05. RESULTS: The rectangular orthodontic Bioforce wire

  13. Avaliação da soldagem multipasse de chapas espessas de aços inoxidáveis lean duplex UNS S32304 soldadas pelos processos SMAW, GMAW e FCAW: parte 1: propriedades mecânicas Evaluation of multipass welding of thick lean duplex stainless steel UNS S32304 plates welded by SMAW, GMAW and FCAW: part 1: Mechanical Properties

    Directory of Open Access Journals (Sweden)

    Ronaldo Cardoso Junior

    2012-12-01

    Full Text Available Os aços inoxidáveis duplex (AID vêm se apresentando como uma excelente alternativa para aplicações em que alta resistência à corrosão e alta resistência mecânica são requeridas. Contudo, os AID, incluindo os aços inoxidáveis lean duplex, apresentam soldabilidade inferior em relação aos aços inoxidáveis austeníticos. Nesse sentido, esse trabalho tem como objetivo a avaliação da soldagem multipasse de chapas 22 mm de espessura da liga inoxidável lean duplex UNS S32304, utilizando-se os processo SMAW, GMAW e FCAW e consumíveis com dois tipos de composição química, 22%Cr9%Ni3%Mo e 23%Cr7%Ni, totalizando seis experimentos. Foram empregados chanfros em V com 60º e suporte cerâmico para soldagem do passe de raiz, sendo que o aporte térmico foi mantido praticamente constante em 1,6 kJ.mm-1. Determinou-se os tempos de soldagem e a seqüência de passes, objetivando uma análise de produtividade, em seguida as juntas soldadas foram submetidas à END por raios x. Foram extraídos corpos de prova para ensaios de tração, dobramento, Charpy a -30 ºC e microdureza. A produtividade dos processos semi-automáticos se mostrou pelo menos 63 % maior que a do processo SMAW, enquanto o processo FCAW se mostrou de 6 a 18% mais rápido que o GMAW. Foram encontradas descontinuidades (porosidade consideradas aceitáveis segundo ASME B31.3 em alguns dos experimentos, que não influenciaram negativamente os resultados mecânicos, os quais se apresentaram acima requerimento do metal de base e especificado por normas de fabricação.The duplex stainless steels (DSS's have been placed as an excellent alternative for applications where high corrosion resistance and high mechanical strength are required. However, DSS's, including the lean duplex, present lower weldability than the austenitic stainless steels. Thus, this study aims to evaluate the multipass welding of 22 mm plates of lean duplex stainless steel alloy UNS S32304, using the process

  14. Brasagem dos aços inoxidáveis duplex 'baixa liga' UNS S32101, UNS S32304 e superduplex UNS S32750 com metal de adição AWS A5.3 tipo BNi-7 (Ni-Cr-P

    Directory of Open Access Journals (Sweden)

    Dany Michell Andrade Centeno

    2013-12-01

    Full Text Available Os aços inoxidáveis duplex, devido à sua resistência à corrosão, têm uma grande aplicação em diversos segmentos industriais, onde a resistência à corrosão é uma propriedade requerida. Por terem resistência mecânica superior aos aços inoxidáveis ferríticos e austeníticos convencionais, podem produzir equipamentos mais leves. Quando ciclados termicamente, estes aços podem ter suas propriedades alteradas, principalmente quando se emprega processos de junção, como a brasagem, e quando ocorre o desbalanceamento da fração volumétrica ferrita/austenita. O objetivo deste trabalho é caracterizar a brasagem de aços inoxidáveis duplex 'baixa liga' e superduplex, verificando o efeito da folga e do tempo de brasagem na formação de intermetálicos contínuos no interior da junta brasada. Neste trabalho foram brasados, em forno continuo com atmosfera de hidrogênio, corpos-de-prova de aço inoxidável duplex UNS S32101, UNS S32304 e UNS S32750 com a adição para brasagem BNi-7 (Ni-Cr-P, na temperatura de 1100ºC, por tempos de 12 min e 32 min, utilizando-se folgas das juntas de 0,0 e 0,3 mm, seguidos de resfriamento em forno. Os corpos de prova foram caracterizados utilizando-se microscópio óptico, microscópio eletrônico de varredura com EDS e difração de raios X. Os resultados mostraram que a melhor condição para a brasagem em forno empregado foi a brasagem com a folga de 0,0 mm. Ambas as folgas apresentaram microestruturas variadas, porém a folga de 0,0 mm mostrou a presença de uma fase contínua CFC (cúbica de face centrada, rica em níquel, que é denominada, frequentemente, de γ-Ni. Para folgas de 0,3 mm, forma-se uma região eutética contínua no centro da junta, que pode prejudicar as propriedades mecânicas da mesma. Esta região é composta de fases intermetálicas ricas em fósforo. Foram observadas precipitações de fase sigma no metal de base no AID UNS S35750, nas condições de brasagem estudadas.

  15. Efecto de los ciclos térmicos sobre la ZAT de una soldadura multipasos de un acero inoxidable superdúplex SAF 2507 Effect of thermal cycles on the HAZ of a stainless steel multipass weld of superduplex SAF 2507

    Directory of Open Access Journals (Sweden)

    D. Villalobos

    2010-09-01

    Full Text Available Los ciclos térmicos de una soldadura multipasos que experimenta un acero inoxidable superdúplex SAF 2507, pueden promover la precipitación de fases secundarias reduciendo significativamente las propiedades mecánicas y la resistencia a la corrosión. Debido a su aplicación en la industria petroquímica, el estudio de las aleaciones superdúplex es de suma importancia para predecir su comportamiento en servicio cuando están involucrados procesos de soldadura por arco eléctrico. En este trabajo, se estudia el cambio microestructural de la zona afectada térmicamente correspondiente al primer cordón depositado de una unión multipasos de acero inoxidable superdúplex SAF 2507 mediante el proceso GTAW y bajo tres temperaturas de interpasos. Los resultados muestran que la temperatura de interpasos tiene una influencia sobre la precipitación de fase sigma en la zona afectada térmicamente del primer cordón depositado.Thermal cycles experienced by a superduplex stainless steel SAF 2507 when is welded, can promote the precipitation of secondary phases which decrease the mechanical properties as well as the corrosion resistance. Due to the application of the duplex alloys in the petrochemical industry, the study of these alloys has become very important in order to predict its service behavior. The aim of this work is to study the microstructural changes in the superduplex stainless steel weld joint after applying the GTAW process under three interpass temperatures after the deposition of every single pass. The results showed that slow cooling rates promoted by the deposition of the subsecuent passes and the higher interpass temperature, promote the precipitation of sigma phase in the HAZ while rapid cooling rates promoted by the lower interpass temperature do not promote the sigma phase precipitation.

  16. Efeito da energia de soldagem sobre a microestrutura e propriedades mecânicas da zona afetada pelo calor de juntas de aço inoxidável duplex Effect of the welding heat input on the microstructure and mechanical properties of the heat affected zone of multipass welded joints of duplex stainless steel

    Directory of Open Access Journals (Sweden)

    Everton Barbosa Nunes

    2011-09-01

    Full Text Available O objetivo deste trabalho é analisar a influência da energia de soldagem na zona afetada pelo calor (ZAC, de juntas soldadas do aço inoxidável duplex UNS S31803. Foram realizadas soldagens com eletrodo revestido AWS E2209-17 em junta tipo V de Aço Inoxidável Duplex UNS S31803, com dois níveis de energia (15 e 20 kJ/cm. A condição soldada com energia mais elevada apresentou uma ZAC mais extensa e microestrutura mais grosseira nos passes de acabamento. No entanto, nos passes de enchimento e de raiz, as ZAC's destas regiões foram mais refinadas e menos extensa. Em relação à microdureza, a condição soldada com energia de 15 kJ/cm apresentou níveis menores. Em relação à tenacidade, não foi verificada diferença significativa nos resultados.The aim this work is to evaluate the influence of multipass welding heat input on the microstructure and mechanical properties of the heat affected zone (HAZ of UNS S31803 duplex stainless steel multipass welded joints. The shielded metal arc welding process using as filler metal the AWS E2209-17 covered electrode were employed had been carried through V joint groove UNS S31803 DSS, so that two levels of energy (15 and 20 kJ/cm had been used in this experiment. The condition welded with higher energy higher a HAZ extensive and coarser microstructure in the finishing passes. On the other hand, in the wadding passes and root pass, the HAZ this region was more refined and less extensive. In respect of microhardness, the condition welded with energy of 15 kJ/cm got lower levels. In relation to toughness, it was not observed significant differences.

  17. Multi-cracking in uniaxial and biaxial fatigue of 304L stainless steel

    International Nuclear Information System (INIS)

    Rupil, J.

    2012-01-01

    When a mechanical part is subjected to a repeated mechanical stress, it may be damaged after a number of cycles by several cracks initiation and propagation of a main crack. This is the phenomenon of fatigue damage. The thesis deals specifically with possible damage to some components of nuclear plants due to thermal fatigue. Unlike conventional mechanical fatigue damage where a main crack breaks the part, the thermal fatigue damage usually results in the appearance of a surface crack network. Two aspects are discussed in the thesis. The first is the experimental study of fatigue multiple cracking stage also called multi-cracking. Two mechanical test campaigns with multi-cracking detection by digital image correlation were conducted. These campaigns involve uniaxial and equi-biaxial mechanical loads in tension/compression without mean stress. This work allows to monitor and to observe the evolution of different networks of cracks through mechanical solicitations. The second is the numerical simulation of the phenomenon of fatigue damage. Several types of model are used (stochastic, probabilistic, cohesive finite elements). The experimental results have led to identify a multiple crack initiation law in fatigue which is faced with the numerical results. This comparison shows the relevance of the use of an analytical probabilistic model to find statistical results on the density of cracks that can be initiated with thermal and mechanical fatigue loadings. (author) [fr

  18. Four nondestructive electrochemical tests for detecting sensitization in type 304 and 304L stainless steels

    International Nuclear Information System (INIS)

    Majidi, A.P.; Streicher, A.

    1986-01-01

    Three different electrochemical reactivation tests are compared with etch structures produced in the electrolytic oxalic acid etch test. These nondestructive tests are needed to evaluate welded stainless steel pipes and other plant equipment for susceptibility to intergranular attack. Sensitization associated with precipitates of chromium carbides at grain boundaries can make these materials subject to intergranular attack in acids and, in particular, to intergranular stress corrosion cracking in high-temperature (289 0 C) water on boiling water nuclear reactor power plants. In the first of the two older reactivation tests, sensitization is detected by the electrical charge generated during reactivation. In the second, it is measured by the ratio of maximum currents generated by a prior anodic loop and the reactivation loop. A third, simpler reactivation method based on a measurement of the maximum current generated during reactivation is proposed. If the objective of the field tests, which are to be carried out with portable equipment, is to distinguish between nonsensitized and sensitized material, this can be accomplished most simply, most rapidly, and at lowest cost by an evaluation of oxalic acid etch structures

  19. Adsorption of Pu(IV) Polymer onto 304L Stainless Steel

    International Nuclear Information System (INIS)

    Bronikowski, M.G.

    1999-01-01

    'The report, Technical Basis for Safe Operations with Pu-239 Polymer in NMS and S Operating Facilities (F and H Areas), (WSRC-TR-99-00008) was issued in an effort to upgrade the Authorization Basis (AB) for H Area facilities relative to nuclear criticality. At the time, insufficient data were found in the literature to quantify the adsorption of Pu polymer onto the surfaces of stainless steel tanks. Additional experimental or literature information on the adsorption of Pu(IV) polymer and its removal was deemed necessary to support the H Area AB. The results obtained are also applicable to processing in F Area facilities.Additional literature sources suggest that adsorption on the tank walls should not be a safety concern. The sources show that the amount of Pu polymer that adsorbs from a solution comes to a limiting amount in 5 to 7 days after which no additional Pu is adsorbed. Adsorption increases with Pu concentration and decreases with acid concentration. The adsorbed amounts are small varying from 0.5 mg/cm2 for a 0.5 g/l Pu / 0.5M HNO3 solution to 11 mg/cm2 for a 1-3 g/l Pu / 0.1M HNO3 solution. Additionally, acid concentrations greater than 0.1M will remove a percentage of adsorbed Pu.The experimental results have generally confirmed much of what has been reported in the literature. Specifically, adsorption onto stainless steel was found to increase with increased Pu concentration, and decreased acid concentration. The amount adsorbed was found to come to a limiting amount after 5 to 7 days. Pu adsorbed as polymer was found to be harder to remove than if it was adsorbed as Pu(IV). The amount of Pu adsorbed as polymer was found to be almost an order of magnitude more than that from a similar concentration Pu(IV) solution. Unlike the literature, only a slight increase in adsorption values was found when the steel surface was removed, dried, and replaced in the Pu solution. The amount of Pu as polymer which would adsorb onto the surface of a 14,000L tank was estimated to be less than 10 grams and thus was not a safety concern.'

  20. Influence of martensitic phase in abrasion behaviour of stainless steel 304 L

    International Nuclear Information System (INIS)

    Ruzzante, J.; Alvarez, P.; Hey, A.; Gestido, G.D.; Vosen, J.H.; Fernandez, H.A.

    1986-01-01

    Abrasion behaviour is studied in commercial stainless steels of different class compositions by standard. The work achieved guieds in structural analysis of superficial coat formed and its relation with abrasion variables, load and velocity. The abrasion is made in an equipment LF WK of high velocity with friction powers, abrasion velocity and temperature variation registered on the tested piece. The abrasion zone is studied with scanning electron microscope (SEM). The deformed superficial zone nature is studied relationing its microstructure with profile corresponding of microhardness. (C.M.C.T.R.) [pt

  1. Kinetics modelling of the concentrated nitric acid reduction on 304L stainless steel

    International Nuclear Information System (INIS)

    Benoit, Marie

    2016-01-01

    In France, the spent nuclear fuel reprocessing involves the use of nitric acid at various concentrations and temperatures. The corrosiveness of these nitric mixtures leads to the use of corrosion resistant materials such as austenitic stainless steels (SS), which naturally forms a protective oxide layer under those conditions. The goal of this work is to study the influence of the passive layer on the mechanism and kinetics of concentrated nitric acid reduction reaction (NRR). We firstly focused on a single step in the reduction reaction (Fe(III)/Fe(II) couple in acidic solution) on passivated zirconium with different oxide layer thicknesses. The electrochemical impedance spectroscopy can lead to estimate the semiconducting properties of the film: the space charge capacitance (from the Mott-Schottky equation) allowed to estimate the number of charge carriers in the oxide. We experimentally compare the NRR on gold (on which no passive layer is formed) and SS, respectively. The chemical composition (chromium enrichment) and thickness of the SS passive layer are characterized by electrochemical impedance spectroscopy (EIS) and X-ray photoelectron spectroscopy (XPS), and the mechanism and kinetics of NRR are studied by chrono-amperometry and EIS. On gold electrode, two mechanisms occur successively as a function of cathodic overpotential. at lower over potentials (0.85≤E/SHE≤1.15 V) we propose that NRR follows the Vetter's mechanism, whereas at higher over potentials (0.65≤E/ESH≤ 0.85 V), Schmid's mechanism may occur. On SS, the presence of the passive layer slows down the NRR by a factor 10"4. Moreover, depending on the experimental conditions (4 M to 8 M, 40 C to 100 C) Schmid's mechanism may occur or not in the potential range investigated. Finally, based on the EIS results, we propose a quantitative modelling of the NRR mechanism on stainless steel electrodes. (author) [fr

  2. Corrosion Testing of 304L SS 3013 Inner Container and Teardrop Samples

    Energy Technology Data Exchange (ETDEWEB)

    Tokash, Justin Charles [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Hill, Mary Ann [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Lillard, Scott [Univ. of Akron, OH (United States); Joyce, Stephen Anthony [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Tegtmeier, Eric Lee [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Berg, John M. [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Veirs, Douglas Kirk [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Worl, Laura Ann [Los Alamos National Lab. (LANL), Los Alamos, NM (United States)

    2017-06-27

    The Department of Energy (DOE) 3013 Standard specifies a minimum of two containers to be used for the storage of plutonium-bearing materials containing at least 30 wt.% plutonium and uranium. Three nested containers are typically used, the outer, inner, and convenience containers, shown in Figure 1. Both the outer and inner containers are sealed with a weld while the innermost convenience container must not be sealed. Lifetime of the containers is expected to be fifty years. The containers are fabricated of austenitic stainless steels (SS) due to their high corrosion resistance. Potential failure mechanisms of the storage containers have been examined by Kolman and Lillard et al.

  3. Avaliação do coeficiente de atrito de braquetes metálicos e estéticos com fios de aço inoxidável e beta-titânio Evaluation of the friction coefficient of metal and esthetic brackets with stainless steel and beta-titanium wires

    Directory of Open Access Journals (Sweden)

    Cristine Pritsch Braga

    2004-12-01

    Full Text Available Um fator importante que define a eficácia dos aparelhos ortodônticos fixos é o atrito existente entre as superfícies de fios e braquetes. Assim, este estudo teve como objetivo investigar o coeficiente de atrito estático entre fios de aço inoxidável e beta-titânio (TP Orthodontics e braquetes de aço inoxidável (Dynalock® - Unitek, braquetes estéticos com slot de aço inoxidável (Clarity® - Unitek e estéticos convencionais (Allure® - GAC. Para tanto, construiu-se um equipamento no Departamento de Engenharia Mecânica e Mecatrônica da PUCRS. Antes de serem iniciados os testes, foi quantificado o erro de método e constatou-se que não houve interferência significante (p>0,05 do fator operador nas medições. Então, pôde-se calcular o valor do coeficiente de atrito, obtido pela divisão da força de atrito pela carga normal. O método estatístico utilizado neste estudo foi Análise de Variância (ANOVA e teste de Comparações Múltiplas (Tukey. Constatou-se que: 1 a combinação com menor coeficiente de atrito foi composta pelo fio de aço inoxidável e braquete Dynalock® e a que apresentou maior coeficiente foi a do braquete Allure® com o fio de beta-titânio; 2 o fio de beta-titânio apresentou coeficiente de atrito significativamente maior do que o fio de aço inoxidável; 3 o braquete Dynalock® não apresentou diferenças significativas em relação ao coeficiente de atrito do braquete Clarity® quando o fio utilizado foi de beta-titânio. No entanto, quando o fio testado foi de aço inoxidável, apresentou coeficiente de atrito significativamente menor. O braquete Clarity® apresentou coeficiente de atrito significativamente menor do que o braquete Allure®.An important factor that defines the effectiveness of the appliances is the friction between the surfaces of wires and brackets. Thus, that study was developed in order to investigate the static friction coefficient between stainless steel and beta-titanium wires (TP

  4. Relaciones cuantitativas entre los contenidos de azufre y de sulfuros en los aceros inoxidables tipo AISI 303: influencia de la composición química de los sulfuros

    Directory of Open Access Journals (Sweden)

    Botella, J.

    1999-06-01

    Full Text Available The work has been done with ten AISI 303 stainless steel rods which have similar chemical compositions, except for sulphur which varies between 0.25 and 0.36%. These steels are studied by Scanning Electron Microscopy (SEM and Energy Dispersive X-Ray Spectrometry (EDX. The sulphides are chemically microanalysed and the occupied volume determined by automatic image analysis. It can be inferred that the chemical composition of sulphides in AISI 303 steels is variable to some extent even though the steel chemistry is almost invariable. This could mean that solidification conditions and thermomechanical transformations are able to affect resulting in variations of sulphide compositions. Quantitative relations between sulphur and sulphide contents are established and the influence of sulphide chemical compositions on those relations is studied. The experimental results are compared with those obtained from theoretical calculations. A good approach is obtained when the difference between chemical compositions of real sulphides and the theoretical one, MnS, is taken into account.

    Se trabaja con una serie de diez redondos de aceros inoxidables tipo AISI 303 de composiciones químicas prácticamente iguales a excepción del azufre que varía entre 0,25 y 0,36%. Se examinan los aceros mediante Microscopía Electrónica de Barrido (MEB y Espectrometría de Dispersión de Energías de Rayos X (EDX acoplada al MEB, analizándose químicamente los sulfuros y determinando, mediante análisis automático de imágenes, los volúmenes ocupados por los sulfuros. Parece deducible que la composición química de los sulfuros en el AISI 303 puede ser discretamente variable aún siendo prácticamente invariable la composición química del acero. Ello podría significar que las condiciones de solidificación y las transformaciones termomecánicas pueden influir, dando como resultado variaciones en la composición química de los sulfuros. Se establecen

  5. A força de atrito em braquetes plásticos e de aço inoxidável com a utilização de quatro diferentes tipos de amarração Frictional forces in stainless steel and plastic brackets using four types of wire ligation

    Directory of Open Access Journals (Sweden)

    Vanessa Nínia Correia Lima

    2010-04-01

    Full Text Available OBJETIVO: a finalidade deste estudo in vitro foi avaliar e comparar a resistência friccional em braquetes de aço inoxidável e de policarbonato compósito amarrados com fio metálico e elastômeros. MÉTODOS: foram utilizados quatro braquetes de aço inoxidável e quatro de policarbonato compósito (PC para pré-molares levados à máquina universal de ensaio mecânico para a tração de um segmento de fio de aço inoxidável 0,019" x 0,025" na velocidade de 0,5mm/min, com 8mm de deslocamento total. A forma de amarração variou entre as seguintes possibilidades: amarração metálica com pinça de Steiner, metálica com pinça Mathieu, elastômero da marca Morelli e elastômero da marca TP Orthodontics. RESULTADOS E CONCLUSÕES: os módulos elastoméricos geraram mais atrito do que os metálicos e a amarração com pinça Mathieu provocou menor atrito quando comparada a todas as situações avaliadas. Os braquetes de PC geraram menor atrito do que os metálicos, porém, na escolha do material a ser utilizado na clínica, outras variáveis - tais como a resistência ao cisalhamento e à fratura, a estabilidade de cor e a aderência por microrganismos - devem ser consideradas.OBJECTIVE: This in vitro study evaluated and compared the frictional resistance of stainless steel and polycarbonate (PC composite brackets tied with metal wire and elastomeric ligation. METHODS: Four stainless steel and four polycarbonate composite brackets for premolars were placed in a universal testing machine for the traction of a piece of 0.019 x 0.025-in wire at 0.5 mm/min and total displacement of 8 mm. Ligations were performed according to the following alternatives: metal ligation with Steiner tying pliers; metal ligation using Mathieu tying pliers; Morelli™ elastomeric ligation; and TP Orthodontics™ elastomeric ligation. RESULTS AND CONCLUSIONS: Elastomeric modules generated more friction than the metal ligations, and the ligation with the Mathieu tying

  6. Formation of biofilms by Staphylococcus aureus on stainless steel and glass surfaces and its resistance to some selected chemical sanitizers Formação de biofilme por Staphylococcus aureus na superfície de aço inoxidável e vidro e sua resistência a alguns sanificantes químicos

    Directory of Open Access Journals (Sweden)

    Simone Cristina Marques

    2007-09-01

    Full Text Available The objectives of this work were to verify the capability of Staphylococcus aureus of forming bio-film on stainless steel and glass surfaces; to evaluate the efficiency of sodium dichloroisocyanurate, hydrogen peroxide and peracetic acid in inactivating Staphylococcus aureus cells adhered onto these surfaces; and to visualize biofilm development by scanning electron microscopy before and after sanitizer treatment. The surfaces studied consisted of 10x20mm chips immersed in Petri dishes containing BHI broth inoculated with S. aureus ATCC 25923. Biofilm formation was observed after 15-day incubation, when the cells were removed using the swab technique, followed by Baird Parker agar plating. Also, the efficiency of the chemical sanitizers on the chip surfaces was tested and the non-removed cells were counted on the Baird-Parker agar. After biofilm formation and use of sanitizers, the chips were respectively observed by scanning electronic microscopy following a pre-existing protocol. The obtained results showed biofilm formation on both surfaces, with bacterial count in the order of 10(7 CFU/cm² on and 10(8 CFU/cm² on stainless steel and glass surfaces, respectively. Peracetic acid was the most efficient in removing adhered cells, presenting 5.26 and 4.5 decimal reduction for adhered cells on stainless steel and glass surfaces, respectively.Os objetivos deste trabalho foram verificar a capacidade de Staphylococcus aureus formar biofilme nas superfícies de aço inoxidável e vidro, avaliar a eficiência do dicloroisocianurato de sódio, peróxido de hidrogênio e ácido peracético na inativação de células de S. aureus aderidas e visualização por microscopia eletrônica de varredura, o desenvolvimento antes e depois do tratamento das superfícies com os sanificantes. As superfícies foram cupons 10x200mm imersos em placas de Petri contendo caldo BHI inoculado com cultura de Staphylococcus aureus ATCC 25923. A formação de biofilme foi

  7. Avaliação da suscetibilidade à corrosão sob tensão da ZAC do aço inoxidável AISI 316L em ambiente de reator nuclear PWR Stress corrosion cracking of stainless steel AISI 316L HAZ in PWR Nuclear reactor environment

    Directory of Open Access Journals (Sweden)

    Mônica Maria de Abreu Mendonça Schvartzman

    2009-09-01

    Full Text Available Aços carbono de baixa liga e aços inoxidáveis são amplamente utilizados nos circuitos primários de reatores nucleares do tipo PWR (Pressurized Water Reactor. Ligas de níquel são empregadas na soldagem destes materiais devido a características como elevadas resistências mecânica e à corrosão, coeficiente de expansão térmica adequado, etc. Nos últimos 30 anos, a corrosão sob tensão (CST tem sido observada principalmente nas regiões das soldas entre materiais dissimilares existentes nestes reatores. Este trabalho teve como objetivo avaliar, por comparação, a suscetibilidade à corrosão sob tensão da zona afetada pelo calor (ZAC do aço inoxidável austenítico AISI 316L quando submetida a um ambiente similar ao do circuito primário de um reator nuclear PWR nas temperaturas de 303ºC e 325ºC. Para esta avaliação empregou-se o ensaio de taxa de deformação lenta - SSRT (Slow Strain Rate Test. Os resultados indicaram que a CST é ativada termicamente e que a 325ºC pode-se observar a presença mais significativa de fratura frágil decorrente do processo de corrosão sob tensão.In pressurized water reactors (PWRs, low alloy carbon steels and stainless steel are widely used in the primary water circuits. In most cases, Ni alloys are used to joint these materials and form dissimilar welds. These alloys are known to accommodate the differences in composition and thermal expansion of the two materials. Stress corrosion cracking of metals and alloys is caused by synergistic effects of environment, material condition and stress. Over the last thirty years, CST has been observed in dissimilar metal welds. This study presents a comparative work between the CST in the HAZ (Heat Affected Zone of the AISI 316L in two different temperatures (303ºC and 325ºC. The susceptibility to stress corrosion cracking was assessed using the slow strain rate tensile (SSRT test. The results of the SSRT tests indicated that CST is a thermally

  8. Estudio in vitro de la citotoxicidad y genotoxicidad de los productos liberados del acero inoxidable 316L con recubrimientos cerámicos bioactivos Cytotoxic and genotoxic study of in Vitro released products of stainless Steel 316l with bioactive ceramic Coatings

    Directory of Open Access Journals (Sweden)

    María Elena Márquez Fernández

    2007-03-01

    Full Text Available El acero inoxidable AISI 316L es el biomaterial mas utilizado para la fabricación de implantes temporales, pero presenta limitaciones para implantes permanentes debido a la liberación de iones metálicos hacia los tejidos circundantes, produciendo especies reactivas de oxígeno (ERO y daño en ADN, factores que aumentan el riesgo de aparición de tumores locales y fallas mecánicas del implante. Una estrategia utilizada para disminuir la liberación de iones es la modificación superficial de los implantes metálicos por medio de recubrimientos inorgánicos, cerámicos o vítreos, aplicados por el método sol-gel, el cual presenta una serie de ventajas comparativas con otras técnicas de deposición, como buena adherencia, aplicación sencilla, mínimos problemas de secado, bajas temperaturas de densificación y posibilidad de agregar partículas y/o grupos orgánicos que mejoran la adherencia celular al implante aumentando su biocompatibilidad. En el presente trabajo se evaluaron los efectos citotóxico por medio de la técnica MTT, y genotóxico por electroforesis en gel de células individuales (Ensayo Cometa, sobre células de la línea celular CHO, de los productos liberados en medio MEM por el acero inoxidable 316L sin recubrir, recubierto con una monocapa de vidrio de sílice (MC, o con doble capa que contiene partículas bioactivas de hidroxiapatita (HA, vidrio (V o vitrocerámico (VC, después de un periodo de 30 días. Los resultados muestran que a los 30 días de envejecimiento en medio MEM no se encuentra ningún efecto citotóxico, pero se encontró efecto genotóxico en las probetas de A y MC que no representa un peligro inminente a sistemas celulares. The stainless steel AISI 316L is the must used biomaterial for the making of temporal prosthesis, but it presents severe limitations for permanent implants due to the generation and migration of metallic ions to the surrounding peripheral tissues, which produces oxygen reactive

  9. Influência da velocidade de circulação do leite na adesão de Pseudomonas aeruginosa sobre aço inoxidável The speed of milk circulation influences the adhesion of Pseudomonas aeruginosa on stainless steel

    Directory of Open Access Journals (Sweden)

    Hamilton Mendes de Figueiredo

    2009-09-01

    Full Text Available A influência da velocidade de circulação do leite na adesão bacteriana de Pseudomonas aeruginosa foi avaliada em teste de uso simulado por meio de um modelo de circuito de processamento de leite. O circuito é composto por uma tubulação de aço inoxidável AISI 304, com 1,9 cm de diâmetro e 5,8 m de comprimento, além de um tanque de 25 L, utilizado como reservatório do produto e das soluções sanitizantes. O reservatório foi acoplado a uma bomba centrífuga de ½ HP, para impulsionar o alimento ou soluções de higienização pelo sistema equipado com cupons de prova em aço inoxidável nas formas cilíndrica, cotovelo 90º e T. As velocidades de circulação foram de 0,5, 1,0 e 1,5 m.s-1, correspondentes a fluxo turbulento com número de Reynolds de 14.000, 28.000 e 42.000, respectivamente. Quando se utilizou velocidade de 0,5 m.s-1, permaneceram aderidas à superfície 10,7% das células. Já nas velocidades e 1,0 e 1,5 m.s-1 as porcentagens de adesão foram de 5,36 e 4,9%, respectivamente, o que demonstra uma menor remoção de células aderidas à medida que o fluxo diminui, permitindo assim que mais células permaneçam aderidas na linha de produção, o que pode favorecer a formação de biofilmes.The influence of the flow milk circulation in the bacterial adhesion of Pseudomonas aeruginosa was evaluated by simulation tests through a circuit model of milk processing. The circuit is composed of a tubulation of stainless steel AISI 304, with 1.9 cm of diameter, 5.8 m of length and a tank of 25 L used as the reservoir of the product and sanitizer solutions. The reservoir was coupled to a centrifugal bomb of ½ HP to impel the food or sanitizer solutions for the system equipped with 90º and T cylindrical stainless steel specimens. The speed of circulation values were 0.5, 1.0 and 1.5 m.s-1, corresponding to turbulent flow with number of Reynolds 14.000, 28.000 and 42.000, respectively. When flow of 0.5 m.s-1 was used 10.7% the

  10. Formação de biofilme em aço inoxidável por Aeromonas hydrophila e Staphylococcus aureus usando leite e diferentes condições de cultivo Biofilm formation by Aeromonas hydrophila and Staphylococcus aureus on stainless steel using milk and different conditions of cultivation

    Directory of Open Access Journals (Sweden)

    Cleube Andrade Boari

    2009-12-01

    Full Text Available O objetivo desta pesquisa consistiu em avaliar a formação de biofilme em aço inoxidável por Aeromonas hydrophila e Staphylococcus aureus usando leite e diferentes condições de cultivo. As variáveis em estudo consistem no cultivo monoespécie e combinado, dos referidos microrganismos e nas temperaturas de 4, 7 e 18 °C. Recipientes contendo 1000 mL de leite, densidade populacional de 10(5 UFC.mL-1 de cada microrganismo e 10 cupons de aço inoxidável (10 × 20 mm foram lacrados e armazenados, sob agitação de 60 rpm, por um período de 10 dias. As análises ocorreram a cada 48 horas. Células sésseis de A.hydrophila e S. aureus foram enumeradas através do plaqueamento seletivo em ágar m-Aeromonas selective e Baird-Parker, respectivamente. Estudos sobre o tempo de geração, enumeração de células planctônicas e observação dos cupons através da microscopia eletrônica de varredura foram conduzidos. S. aureus, em monocultivo, formou biofilme a 18 °C e a 7 °C. Para 4 °C, foi observado um processo de adesão. A presença de A. hydrophila reduziu o desempenho de S. aureus. Nesta condição de cultivo multiespécie houve formação de biofilme a 18 °C. A. hydrophila, tanto em monocultivo quanto em presença de S. aureus, formou biofilme em todas as condições pesquisadas.The aim of this research was to verify the capability of biofilm formation on stainless steel by Aeromonas hydrophila and Staphylococcus aureus using milk and different conditions of cultivation. The variables consisted in mono and multi-species cultivation of these microorganisms and in the temperatures of 4, 7 and 18 °C. Containers containing 1000 mL of milk, population density of 10(5 CFU.mL-1 of each microorganism, and ten suspended chips of stainless steel AISI 304 (10 × 20 mm were used to seal up and storage, under 60 rpm of agitation for 10 days. The analyses were conducted every 48 hours. Sessile cells of A. hydrophila and S. aureus and were enumerated

  11. Efeito da amarração em Ortodontia, com ligaduras elastoméricas e de aço inoxidável, na saúde periodontal Effects of orthodontic ligation-using elastomeric and stainless steel ligatures-on periodontal health

    Directory of Open Access Journals (Sweden)

    Clotilde Freitas Rodrigues

    2011-02-01

    Full Text Available OBJETIVO: o presente estudo avaliou clinicamente as condições periodontais de um grupo teste e um grupo controle utilizando-se os seguintes três sistemas de indexação periodontal: índice de biofilme, índice de sangramento e profundidade de sondagem. MÉTODOS: o grupo teste foi composto por 20 indivíduos com média etária de 13,5 anos, submetido ao tratamento ortodôntico fixo, que recebeu duas formas de ligaduras: a elastomérica e a de aço inoxidável. Os resultados foram comparados entre si e com um grupo controle, sem tratamento ortodôntico, composto de 15 indivíduos com média etária de 15,3 anos. As mensurações foram realizadas previamente ao tratamento ortodôntico (T1 e seis meses após a colocação do aparelho ortodôntico fixo (T2; e, no grupo controle, após seis meses da mensuração inicial (T2. Ambos os grupos foram orientados quanto à higiene bucal, segundo a técnica de Bass, antes do início do tratamento. RESULTADOS E CONCLUSÕES: os resultados das análises das faces dentárias demonstraram um aumento estatisticamente significativo nos índices de biofilme (P=0,000, sangramento gengival (P=0,000 e profundidade de sondagem (P=0,000, quando T1 e T2 e os grupos foram comparados; entretanto, não foram encontradas diferenças estatisticamente significativas entre as ligaduras elastoméricas e de aço inoxidável na avaliação desses índices periodontais.OBJECTIVE: This study aimed to conduct a clinical evaluation of the periodontal conditions of a test group and a control group using three periodontal indexing systems, namely: dental biofilm index (DBI, bleeding index (BI and pocket probing depth (PPD. METHODS: The test group consisted of 20 subjects with a mean age of 13.5 years undergoing fixed orthodontic treatment involving the use of two types of ligature: elastomeric ligature (EL and stainless steel ligature (SSL. The results were compared with a control group without prior orthodontic treatment, comprising

  12. Estudo do processo de fabricação de tubos flexíveis de aço inoxidável duplex UNS 32304 utilizados na indústria de petróleo e gás Study of the manufacturing process of UNS 32304 flexible pipes for the oil and gas industry

    Directory of Open Access Journals (Sweden)

    Ida Paula Gusmão de Oliveira

    2013-03-01

    Full Text Available A principal característica dos aços inoxidáveis duplex é o equilíbrio entre as fases austenita e ferrita, que garantem ao material melhores índices de resistências à corrosão e mecânica. No entanto, durante o processo de soldagem, ocorrem modificações estruturais, principalmente no balanço destas fases. Este desbalanceamento, em função dos níveis de solicitações mecânicas, pode levar tais regiões soldadas ao colapso. No intuito de minimizar o desequilíbrio das fases na região soldada, diversas técnicas são utilizadas, tais como inserção de metal de adição com elementos austenitizantes, uso de gás de proteção com nitrogênio ou, em outros casos, controle pós soldagem. Buscou-se identificar o verdadeiro efeito dos parâmetros de soldagem e do tratamento térmico especificado pela literatura em situações de campo. Através de uma avaliação temporal, observando uma linha de produção de tubulação flexível de aço inoxidável duplex UNS 32304 durante três anos, utilizando-se de procedimentos convencionais de soldagem com e sem a utilização de tratamento térmico foram observadas as falhas por fratura na zona termicamente afetada (ZTA. Foi utilizado um indutor localizado para o tratamento térmico, gerando um intenso fluxo de calor que promoveu temperaturas da ordem de 1000 ºC a altíssimas taxas de subida e descida, conforme estabelecem algumas literaturas.The main characteristic of duplex stainless steels is the balance between ferrite and austenite phases, wich ensures to such material the best levels of corrosion and mechanical resistance. However, during the welding process, structural modifications occur, especially with regard to the balance of these phases. This imbalance, depending on the levels of mechanical stress, may lead welded regions to collapse. In order to minimize the imbalance of the phases in the welded steel, several techniques are used, such as the insertion of filler metal with

  13. Characterization of gold and nickel coating on AISI 304 stainless steel for use in the fabrication of current collector plates for fuel cells; Caracterizacion de recubrimientos de oro y niquel realizados sobre acero inoxidable AISI 304 para su empleo en la fabricacion de placas colectoras de corriente para celdas de combustible

    Energy Technology Data Exchange (ETDEWEB)

    Flores Hernandez, J. Roberto [Instituto de Investigaciones Electricas, Cuernavaca, Morelos (Mexico)] e-mail: jrflores@iie.org.mx; Aguilar Gama, M. Tulio [UNAM. Facultad de Quimica, Mexico D.F. (Mexico); Cano Castillo, Ulises; Albarran, Lorena [Instituto de Investigaciones Electricas, Cuernavaca, Morelos (Mexico); Olvera, J. Carlos; Orozco, German [CIDETEQ, Pedro Escobedo, Queretaro (Mexico)

    2009-09-15

    Among the different components that compose fuel cell technology (MEA, bipolar plates, seals, etc.) current collector plates play an important role in the good performance of fuel cells, since they collect all of the current generated and distribute it to the external circuit. Therefore, the most important properties that the current collector plates should have are excellent conductivity and good resistance to the corrosive conditions present in the fuel cell. This document presents results obtained during the nickel and gold electrodeposition process on AISI 304 stainless steel and the morphology and thickness of each coating, their adhesion, hardness and conductivity values. Finally, results obtained during some of the electrochemical tests performed on the coatings are shown. [Spanish] De los diferentes componentes que integran la tecnologia de celdas de combustible (MEA's, placas bipolares, sellos, etc.), las placas colectoras de corriente tienen un importante rol en el buen desempeno de la celdas de combustibles, ya que en estas placas se colecta toda la corriente generada y se distribuye al circuito externo. Debido a esto, las propiedades mas importantes que deben tener las placas colectaras de corriente son: excelente conductividad y buena resistencia a las condiciones corrosivas presentes en la celda de combustible. En este documento se presentan los resultados obtenidos en el proceso de electrodeposicion de niquel y oro sobre acero inoxidable AISI 304, asi como la morfologia y el espesor de cada recubrimiento, sus valores de adherencia, dureza y conductividad. Finalmente se muestran tambien los resultados obtenidos de algunas pruebas electroquimicas a los que fueron sometidos los recubrimientos.

  14. Efeito do Pré-aquecimento e de Único e Múltiplos Passes no Grau de Porosidade, Oxidação e Microdureza de um Revestimento de Aço Inoxidável Duplex Depositado por Aspersão Térmica Chama Arame

    Directory of Open Access Journals (Sweden)

    Valdir Celestino da Silva

    Full Text Available Resumo: Este trabalho tem como objetivo estudar o efeito do pré-aquecimento e de único e múltiplos passes no grau de porosidade, oxidação e microdureza no processo de revestimento obtido por aspersão térmica chama arame. A oxidação ao ar de partículas aspergidas após ancoragem afeta o desempenho para o aço inoxidável duplex AF2209 depositado por aspersão térmica chama arame em substrato de aço estrutural pré-aquecido com maçarico à diferentes temperaturas. O percentual de óxidos e poros foram medidos e quantificados por microscopia óptica com auxilio de software de análise de imagem. Imagens por MEV e a dureza Vickers dos óxidos e panquecas indicam que a oxidação aumenta com o pré-aquecimento e com a deposição de múltiplos passes. Os resultados indicam que maiores pré-aquecimentos e a deposição de múltiplos passes reduzem a fragmentação das partículas, mas aumenta a quantidade de óxidos. Observa-se também que o reaquecimento da camada reduz a microdureza Vickers média dos óxidos e panquecas da condição de único passe para a condição de múltiplos passes.

  15. Avaliação do campo de tensões residuais por difração de raios - X utilizando o método do sen²ψ em revestimentos metálicos do aço inoxidável E308-L

    Directory of Open Access Journals (Sweden)

    Raphael. H. F. Melo

    2013-03-01

    Full Text Available A aplicação por soldagem de revestimentos metálicos de aços e ligas nobres resistentes à corrosão é uma alternativa bastante razoável economicamente frente à fabricação de componentes maciços nestas ligas. Entretanto há uma carência de informações sobre as alterações mecânico/metalúrgicas causadas pelos ciclos térmicos de soldagem quando da aplicação destes revestimentos, principalmente sobre a influência sobre o nível de tensões residuais , que é mister no entendimento do fenômeno da corrosão assistida por tensão. O objetivo deste trabalho foi avaliar o nível de tensões residuais superficiais em revestimentos do aço inoxidável AWS E308-L T-1 aplicados pelo processo de soldagem ao Arco Elétrico com Arame Tubular sobre chapas do aço ASTM A36. As medições das tensões residuais foram realizadas por um difratômetro portátil de raios - X na superfície dos revestimentos e os principais resultados obtidos foram que a natureza das tensões residuais na superfície dos revestimentos sempre se apresentou compressivas e não observou-se uma linearidade da magnitude das tensões residuais em função da energia de soldagem.

  16. Efeitos dos fios de nivelamento de níquel-titânio e de aço inoxidável na posição dos incisivos inferiores Effects of nickel-titanium and stainless steel leveling wires on the position of mandibular incisors

    Directory of Open Access Journals (Sweden)

    Ricardo Moresca

    2011-10-01

    Full Text Available OBJETIVO: estudar os efeitos do nivelamento realizado com fios de NiTi termoativado e de aço inoxidável, avaliando-se as possíveis alterações na posição dos incisivos inferiores, em casos com extrações, correlacionando com o tempo de tratamento. MÉTODOS: a amostra foi composta de 36 indivíduos, de ambos os sexos, leucodermas brasileiros, com idade média inicial de 15 anos e 5 meses, portadores de más oclusões de Classes I e II, distribuídos em dois grupos. No Grupo 1 (n=17, o nivelamento foi realizado com a sequência 1, utilizando-se três fios - 0,016" e 0,019"x0,025" de NiTi termoativado, e 0,019"x0,025" de aço inoxidável. No Grupo 2 (n=19, foi testada a sequência 2, na qual foram utilizados apenas fios de aço inoxidável (0,014"; 0,016"; 0,018"; 0,020" e 0,019"x0,025" com torque passivo nos incisivos inferiores. Os dados foram coletados utilizando-se o método cefalométrico computadorizado e comparados pelo teste t de Student com o nível de significância de 5%. RESULTADOS: no Grupo 1, os incisivos inferiores inclinaram-se para lingual, com movimento significativo apenas da coroa (1,6mm. No Grupo 2, os incisivos inferiores permaneceram estáveis. Não houve alteração vertical em nenhum dos grupos. CONCLUSÕES: a sequência 2 proporcionou um melhor controle dos incisivos inferiores, não alterando suas posições iniciais, enquanto a sequência 1 permitiu a expressão do torque da prescrição utilizada, levando a uma inclinação lingual desses dentes. O tempo de tratamento foi menor utilizando-se a sequência 1. As variações biomecânicas estudadas apresentaram vantagens e desvantagens que devem ser conhecidas e ponderadas pelo ortodontista no planejamento do caso.OBJECTIVE: To study the effects of the leveling phase performed with heat activated NiTi and stainless steel archwires evaluating the possible changes in lower incisors position in extraction cases, as well as its correlation with treatment time. METHODS

  17. Optimum thickness evaluation of ZrO2 coating on type 304L stainless steel for corrosion protection

    International Nuclear Information System (INIS)

    Garg, Nidhi; Bera, Santanu; Velmurugan, S.; Tripathi, V.S.; Karki, Vijay

    2015-01-01

    Nano-crystalline ZrO 2 coatings of different thickness have been grown on pre-oxidized stainless steel (SS) surface by hydrothermal method in an autoclave. Thickness of the coating has been enhanced by repeating the deposition process several times using same precursor concentration. Several cycles of the deposition process lead to the increase of the coating thickness from 200 nm to ∼1 μm after the fourth round of deposition. The samples after different rounds of the coating have been extensively characterized by SEM-EDS technique to find the surface topography, coating thickness and composition. Corrosion resistance properties of the plain SS, pre-oxidized SS and all the ZrO 2 coated samples were studied by potentiodynamic polarization technique and electrochemical impedance spectroscopy (EIS). Corrosion current densities (I corr /cm 2 ) of the coated samples are found to reduce significantly with the increase in thickness. After a certain critical thickness, the corrosion resistance properties found to deteriorate due to the formation of coating defects caused by lattice strain. The coating was found to be continuous but porous after the first cycle but porosity of zirconia coating have been reduced drastically after the second cycle itself. EIS analysis confirms that the zirconia coated samples show insulating, barrier like characteristics in terms of high charge transfer resistance after the second cycle of zirconia deposition. The role of pre-oxidized surface composition and the interface between the pre-oxidized surface and the coating has been discussed in details by showing the depth distribution of Zr in the coating. (author)

  18. An Assessment of the Ductile Fracture Behaviour of Hot Isostatically Pressed and Forged 304L Stainless Steel

    OpenAIRE

    Cooper, Adam; Smith, R. J.; Sherry, Andrew

    2017-01-01

    Type 300 austenitic stainless steel manufactured by hot isostatic pressing (HIP) has recently been shown to exhibit subtly different fracture behavior from that of equivalent graded forged steel, whereby the oxygen remaining in the component after HIP manifests itself in the austenite matrix as nonmetallic oxide inclusions. These inclusions facilitate fracture by acting as nucleation sites for the initiation, growth, and coalescence of microvoids in the plastically deforming austenite matrix....

  19. Incremental elongation or ratchetting - Experimental tests and practical method of analysis (on stainless steel 304L and 306L)

    International Nuclear Information System (INIS)

    Cousseran, Pierre; Lebey, Jacques; Roche, Roland; Clement, Gerard; Moulin, Didier.

    1980-12-01

    Ratchetting, or incremental elongation can be considered as a creep enhancement when cyclic deformations are added to a primary constant load. Under examination, it appears that theoretical models proposed till now do not fit correctly the actual behavior of materials. From experimental tests results performed in Saclay, a simplified method for prevention of ratcheting is proposed. A validation was made by using experimental data from various sources [fr

  20. Caracterização e avaliação da resistência à corrosão na soldagem de tubulação de aço inoxidável duplex UNS S31803 pelo processo a arco submerso Characterization and evaluation of corrosion resistance of welded joint of duplex stainless steel pipe UNS S31803 by submerged arc process

    Directory of Open Access Journals (Sweden)

    Juan Manuel Pardal

    2011-12-01

    Full Text Available O presente trabalho apresenta os resultados da caracterização e avaliação da resistência à corrosão de uma junta soldada correspondente a uma tubulação de aço inoxidável duplex (AID UNS S31803 de 35 mm de espessura de parede soldada pelos processos de soldagem TIG (GTAW na raiz e arco submerso (SAW no enchimento e acabamento. Foram empregados como consumíveis de soldagem metais de adição de liga 25Cr-9Ni-4Mo (% em peso. Os resultados da caracterização das propriedades mecânicas, composição química e resistência à corrosão em diversas regiões da junta soldada foram comparados com os obtidos para o metal de base da tubulação, assim como com os valores mínimos exigidos pelas normas de projeto. Os resultados obtidos demonstram claramente a possibilidade da implementação do processo SAW na pré fabricação de tubulações de paredes espessas de AID, tendo em vista os resultados das propriedades analisadas e a grande demanda na construção e montagem de tubulações desta família de aço inoxidáveis na indústria offshore.This work presents the mechanical properties, microstructural and corrosion resistance evaluation of a welded joint of duplex stainless steel (DSS pipe with 35 mm wall thickness. The joint was welded by gas tungsten arc welding (GTAW process in the root passes and submerged arc welding (SAW in the filling and cap passes using filler metals with composition 25Cr-9Ni-4Mo (%wt.. The results of mechanical properties, chemical composition and corrosion resistance characterization in different regions of the welded joint were compared to the base metal and to the specifications required by the standards applied in the project. The main focus of this work was to show the successful utilization of SAW process in the welding of thick wall pipes of DSS. The application of high productivity process such as SAW has a crescent demand in offshore industry.

  1. Análise da resistência à corrosão por pite em soldas de reparo pelo processo TIG em aço inoxidável superduplex UNS S32750 Analysis of pitting corrosion resistance in welding repair by GTAW procedure in a superduplex stainless steel UNS S32750

    Directory of Open Access Journals (Sweden)

    Juliana Primo Basílio de Souza

    2011-06-01

    Full Text Available Atualmente, os aços inoxidáveis superduplex (AISD estão sendo muito empregados no Brasil em setores industriais tais como petroquímico, energético, naval e plataformas offshore, tendo vasta aplicação em vasos de pressão em processos críticos, trocadores de calor, reatores, tubulações, umbilicais, digestores, bombas e naqueles componentes onde a produtividade contínua é essencial e o custo não é a maior limitação. No entanto, durante processos de fabricação e montagem, assim como na vida em serviço destes componentes de processo pode existir a necessidade eventual de efetuar soldagens de reparo. Deste modo, o presente trabalho, visa avaliar a microestrutura e os valores de resistência à corrosão por pites na zona termicamente afetada (ZTA e metal de solda do AISD UNS S32750 durante a simulação de um processo de reparo mediante a utilização do processo de soldagem TIG (GTAW. Os resultados obtidos permitem estabelecer diretrizes para a realização de procedimentos de soldagem de reparo em AISD.Currently superduplex stainless steels (SDSS are being extensively employed in the petrochemical, power generation, naval and offshore industries. The uses of these materials are: pressure vessels for critical processes, heat exchangers, reactors, pipes, umbilicals, digesters, pumps and other facilities where continuous use is essential and cost is not the main limitation. However, during fabrication and assembly, or as consequence of service, repair welding operations may be necessary. Thus, in this study a simulation of welding repair by GTAW process was performed in a SDSS UNS S32750. The objective of this work was to evaluate the microstructure and the values of critical pitting resistance (CPT in the weld metal, heat affected zone and base metal. The results obtained allows the determination of welding procedures and recommendations useful to the welding repair of SDSS.

  2. Chemical sanitizers to control biofilms formed by two Pseudomonas species on stainless steel surface Sanificantes químicos no controle de biofilmes formados por duas espécies de Pseudomonas em superfície de aço inoxidável

    Directory of Open Access Journals (Sweden)

    Danila Soares Caixeta

    2012-03-01

    Full Text Available The biofilm formation of Pseudomonas aeruginosa and Pseudomonas fluorescens on AISI 304 stainless steel in the presence of reconstituted skim milk under different temperatures was conducted, and the potential of three chemical sanitizers in removing the mono-species biofilms formed was compared. Pseudomonas aeruginosa cultivated in skim milk at 28 °C presented better growth rate (10.4 log CFU.mL-1 when compared with 3.7 and 4.2 log CFU.mL-1 for P. aeruginosa and P. fluorescens cultivated at 7 °C, respectively. Pseudomonas aeruginosa formed biofilm when cultivated at 28 °C. However, only the adhesion of P. aeruginosa and P. fluorescens was observed when incubated at 7 °C. The sodium dichloroisocyanurate was the most efficient sanitizer in the reduction of the adhered P. aeruginosa cells at 7 and 28 °C and those on the biofilm, respectively. The hydrogen peroxide was more effective in the reduction of adhered cells of P. fluorescens at 7 °C.A capacidade de adesão e formação de biofilme por Pseudomonas aeruginosa e Pseudomonas fluorescens em aço inoxidável AISI 304, na presença de leite desnatado resconstituído sobre diferentes temperaturas foi conduzido e o potencial de três sanificantes químicos na remoção de biofilmes monoespécies foi comparado. Pseudomonas aeruginosa cultivada em leite desnatado a 28 °C apresentou melhor crescimento (10,4 log UFC.mL-1 quando comparado com 3,7 and 4,2 log UFC.mL-1 para P. aeruginosa e P. fluorescens cultivadas a 7 °C, respectivamente. Pseudomonas aeruginosa formou biofilme quando cultivada a 28 °C. Contudo foi observado somente adesão de P. aeruginosa e P. fluorescens quando incubada a 7 °C. O dicloroisocianurato de sódio foi o sanificante mais eficiente na redução de células aderidas e em biofilme de P. aeruginosa a 7 e 28 °C, respectivamente. O peróxido de hidrogênio foi o mais eficiente na redução de células aderidas de P. fluorescens a 7 °C.

  3. Estudio de la susceptibilidad de un acero inoxidable austenítico estabilizado con niobio al dañado por tensocorrosión en medio H2S (SSC y corrosión intergranular (IGC en otros medios agresivos

    Directory of Open Access Journals (Sweden)

    Gutiérrez de Saiz-Solabarría, S.

    1998-05-01

    Full Text Available Behavior to hydrogen damage caused by stress corrosion in a H2S medium (SSC and to intergranular corrosion (IGC in different mediums, such as oxalic acid (C2H2O4-2H20, iron sulphate-50 % sulfuric acid [Fe2(SO43-50 % H2SO4], nitric acid (HNO3, copper sulphate-16 % sulfuric acid (CuSO4-5H2O-16 % H2SO4 and cooper sulphate-50 % sulfuric acid (CuSO4-5H2O-50 % H2SO4, is studied in an AISI 347 austenitic stainless steel stabilized with 0.61 mass % Nb and hot rolled to a seamless pipe with 273.1 mm in diameter and 18.2 mm in thickness.

    Se estudia el comportamiento de un acero inoxidable austenítico del tipo AISI 347 estabilizado con un 0,61 % en masa de Nb, laminado en caliente para producir una tubería sin soldadura de 273,1 mm de diámetro y 18,2 mm de espesor, frente al dañado por hidrógeno generado por tensocorrosión en medio H2S (SSC y frente a la corrosión intergranular (IGC en diferentes medios agresivos tales como ácido oxálico (C2H2O4∙2H2O, sulfato de hierro-50% ácido sulfúrico [Fe2 (SO43-50 % H2SO4], ácido nítrico (HNO3, sulfato de cobre-16% ácido sulfúrico (CuSO4-5H2O-16 % H2SO4 y sulfato de cobre-50 % ácido sulfúrico (CuSO4-5H2O-50 % H2SO4, respectivamente.

  4. Corrosion behavior of powder metallurgical stainless steels in urban and marine environments

    Directory of Open Access Journals (Sweden)

    Bautista, A.

    2006-06-01

    Full Text Available This work studies the development of corrosive attack on sintered components manufactured from AISI 316L and AISI 304L powders. The stainless steels were sintered in vacuum and in nitrogen-base atmosphere at 1,120 and 1,250 ºC, and their corrosion resistance was then analyzed by electrochemical techniques and by atmospheric corrosion testing (two years at urban and marine test sites. Images are shown of the morphology of the attack on the surface of the stainless steels and the development of this attack in the interior of the material.

    Este trabajo estudia el desarrollo del proceso corrosivo en componentes sinterizados fabricados a partir de polvos de AISI 316L y AISI 304L. Los aceros inoxidables fueron sinterizados en vacío y en atmósfera base nitrógeno a 1.120 y 1.250 ºC y, su resistencia a corrosión se ha analizado mediante técnicas electroquímicas y mediante ensayos de corrosión atmosférica (dos años en ambientes urbano y marino. Se muestran imágenes de la morfología del ataque en la superficie de los aceros inoxidables y del desarrollo de este ataque en el interior del material.

  5. Cinéticas de transformación de fases a 850 ºC de aceros inoxidables dúplex clásicos (2205 y 2507 y de uno nuevo de bajo contenido en níquel y alto en manganeso (DBNi

    Directory of Open Access Journals (Sweden)

    Rodríguez, M. P.

    2004-04-01

    Full Text Available Austenitic-ferritic stainless steels are formed by ferrite and austenite in a variable proportion between 30 % and 70 %. Their chemical composition conditions the ageing processes that can happen during heat treatments, where phases that hardens and brittles the material can be generated. Evolution of a new duplex stainless steel with lower nickel and higher nitrogen and manganese content maintained at 1123 K (critical precipitation temperature up to 8 hours compared to classical ones (2205 and 2507 is presented. The study, done by magnetic measurements, XRD, optical and scanning electron microscopy and microanalysis, revealed a roughly similar behaviour for the three steels. The new one presents a higher initial stability, probably due to the high nitrogen and manganese contents; however, it also produces the higher final transformation due to the higher initial ferrite. A fine comparative analysis was done to correctly identify any phase; an accurate microanalysis in every generated phase was performed. All the steels tested are initially made on ferrite and austenite. After the ageing treatment, 8 hours at 1123 K, in the 2205 duplex steel a strong precipitation of sigma phase is observed, austenite and some of the original ferrite are also present; ferrite completely transforms in the 2507 duplex and austenite, sigma, secondary austenite and chromium nitride can be found; regarding the new duplex steel DBNi, austenite, ferrite, sigma, chi and chromium nitrides are detected.

    Los aceros dúplex austeno-ferríticos están constituidos por ferrita y austenita en proporciones variables del 30 % al 70 %. Su composición química condiciona los procesos de envejecimiento que sufren durante los tratamientos térmicos, cuando se generan fases que endurecen y fragilizan el material. Este trabajo estudia la evolución de un nuevo inoxidable dúplex con bajo contenido en níquel y alto en nitrógeno y manganeso a 1123 K (temperatura crítica de

  6. Avaliação da proporção de fases em juntas soldadas de tubulações de aço inoxidável duplex mediante aplicação de ensaios não destrutivos Evaluation of phases proportions in welded joints of duplex stainless steel by non-destructive testing

    Directory of Open Access Journals (Sweden)

    Guttemberg Chagas de Souza

    2013-06-01

    Full Text Available Os aços inoxidáveis Duplex (AID aliam uma excelente resistência à corrosão com elevada resistência mecânica devido à fina microestrutura bifásica composta por quantidades similares de ferrita (δ e austenita (γ. Portanto, estas ligas são utilizados em tubulações e equipamentos industriais onde se requer elevada relação resistência/peso, especialmente em empreendimentos de construção e montagem off-shore. Entretanto, as condições operacionais, na soldagem de campo, podem promover um significativo desbalanço microestrutural destas fases, resultando em decréscimo das propriedades mencionadas. A inspeção com o ferritoscópio é uma avaliação normalmente utilizada nestas atividades. Durante a avaliação com esta técnica pode ocorrer a rejeição da junta soldada quando o metal de solda se encontra com valores de ferrita fora das faixas estabelecidas pelas especificações de projeto. Assim, torna-se importante a análise destas juntas, com outras técnicas complementares, tal como a utilização das réplicas metalográficas. Este fato motivou a avaliação da proporção de fases em spools de AID de espessuras relativamente finas, soldados no campo, comparando-se as técnicas não destrutivas descritas. Os resultados denotam valores semelhantes, contudo o resultado pode ser influenciado pela forma e condições superficiais da junta soldada.Duplex stainless steels are high strength and corrosion resistant alloys, whose properties are devoted to the fine microstructure composed by similar amounts of ferrite and austenite and also to the high concentrations of Cr, Mo and N in solid solution. Not for coincidence, duplex steels are extensively used in chemical and petrochemical industries. However, welding operations conditions can promote the unbalance of the ferrite/austenite proportions mainly in the welding metal, with decrease of the properties mentioned. For this reason, non destructive measurements of ferrite content

  7. Estudo da soldagem de tubos de aço inoxidável duplex e superduplex na posição 5G Study of the welding of duplex and superduplex stainless steel pipes in the 5G position

    Directory of Open Access Journals (Sweden)

    Pedro Ivo Guimarães de Vasconcellos

    2010-09-01

    Full Text Available Os aços inoxidáveis duplex e superduplex possuem uma microestrutura austeno-ferrítica com fração média de cada fase de cerca 50%. A microestrutura duplex é responsável pelas excelentes propriedades mecânicas, especialmente o limite de escoamento e a tenacidade, e pela elevada resistência a corrosão por pites e sob tensão em meios contendo cloretos. A soldagem destes aços é frequentemente uma operação crítica. Neste trabalho, um tubo de superduplex SAF 2207 foi soldado pelo processo TIG (GTAW no passe de raiz e eletrodo revestido (SMAW nos passes de enchimento, e um tubo de duplex SAF 2205 foi todo soldado pelo processo GTAW. A microestrutura do metal base, zona afetada termicamente (ZTA e metal de solda foi caracterizada e quantificada. As propriedades de tenacidade, resistência a corrosão e composição química foram avaliadas e correlacionadas. Os valores de tenacidade ao impacto Charpy-V foram considerados adequados. Não foi observada a precipitação de intermetálicos, carbonetos e nitretos. O melhor resultado no teste de corrosão da junta soldada de aço inox superduplex, comparado ao duplex, foi atribuído ao baixo teor de ferrita delta na solda e ZTA, e composição química da solda enriquecida em Cr, Mo, W e N.The duplex and superduplex stainless steels have an austenitic-ferritic microstructure with an average fraction of each phase of approximately 50%. This duplex microstructure is responsible for the excellent mechanical properties, specially the yield strength and toughness, and for the improved pitting and stress corrosion cracking resistance in chloride environments. Welding of these steels is often a critical operation. In this work, a superduplex stainless steel SAF 2507 pipe was welded by the GTAW process in the root pass and by SMAW process on filler passes, and one pipe of duplex SAF 2205 was entirely welded by the GTAW process. The microstructure of the base metal, heat affected zone (HAZ and weld

  8. Influência da energia de soldagem na microestrutura e na microdureza de revestimentos de aço inoxidável duplex Influence of the heat input on the microstructure and microhardness of weld overlay of duplex stainless steel

    Directory of Open Access Journals (Sweden)

    Everton Barbosa Nunes

    2012-06-01

    Full Text Available Aços inoxidáveis duplex (AID são caracterizados por apresentar interessante boas propriedades mecânicas e resistência à corrosão, possuindo um vasto campo de aplicação na indústria química e petroquímica. Geralmente, os reparos dos equipamentos ou estruturas são realizados por soldagem, sendo importante a seleção de parâmetros. É de suma importância a obtenção do teor adequado de ferrita no metal de solda, sendo que a variação da energia de soldagem pode influenciar de forma direta no percentual de ferrita. Logo, o objetivo deste trabalho é avaliar a influência da variação da energia de soldagem na microestrutura e na microdureza do metal de solda do AID. Foram realizadas soldagens de revestimento com sobreposição de duas camadas sobre o aço estrutural ASTM A516 Gr.60, utilizando eletrodo revestido AWS E2209-17. Três níveis de energia (15, 20 e 24 kJ/cm foram empregados, variando-se a corrente e a velocidade de soldagem. Foi verificado que para os níveis de energia empregados não houve diferença significativa no percentual de ferrita, porém o primeiro cordão depositado apresentou maior teor de austenita em relação aos demais cordões. De forma geral, foi verificado que o primeiro cordão depositado obteve níveis maiores de microdureza. Todas as condições apresentaram microdurezas abaixo do valor crítico.Duplex stainless steels (DSS are characterized by the presentation of an interesting combination of good mechanical properties and corrosion resistance, having a wide application in chemical and petrochemical industry. Generally, the manufacture and repair of any industrial equipment involve welding operations, even though it is very important to evaluate the influence of welding parameters. It is very important to obtain appropriate ferrite content in the weld metal, so that the variation of heat input can influence on the ferrite content directly. Therefore, the aim this work is to evaluate the

  9. Estudo dos efeitos da restrição na microestrutura, microdureza e tenacidade em juntas soldadas em aço inoxidável duplex Study of restriction effects on mMicrostructure, microhardness and toughness in welded joints of duplex stainless steel

    Directory of Open Access Journals (Sweden)

    Everton Barbosa Nunes

    2011-06-01

    Full Text Available Os aços inoxidáveis duplex (AID apresentam em sua microestrutura ferrita e austenita, de modo a aliar boas propriedades mecânicas e resistência à corrosão. Estes materiais possuem grande aplicação na indústria petroquímica, sendo o UNS S31803 um dos mais conhecidos. Existem poucos trabalhos referentes ao estudo da influência da restrição na soldagem da junta na formação de Widmanstätten. Logo, este trabalho tem como objetivo analisar a influência da restrição no balanceamento de fases, na morfologia da austenita, na microdureza e na tenacidade da Zona Afetada pelo Calor (ZAC e da Zona Fundida (ZF. Foram realizadas soldagens em juntas tipo V utilizando eletrodo revestido AWS E2209-17com dois níveis de energia: 15 kJ/cm e 20 kJ/cm, com e sem restrição. De maneira geral, houve maior quantidade de ferrita nos passes de acabamento em relação aos passes de enchimento e de raiz. Foram observadas maiores quantidades de Widmanstätten nas condições soldadas com restrição. A ZAC apresentou uma microestrutura mais grosseira nos passes de acabamento. No entanto, não foram observadas diferenças significativas nas microestruturas quando comparadas as condições com e sem restrição. As condições que apresentaram maior quantidade de Widmanstätten obtiveram menores níveis de microdureza. Não foram observadas diferenças na energia absorvida na ZAC e ZF.Duplex stainless steels present ferrite and austenite in their microstructure in order to join good mechanical properties and corrosion resistance. These materials are very used in petrochemical industry, being the DSS UNS S31803 one of the most commercially known. There were not much published literature to study the influence of the precipitation of Widmanstätten austenite in joins with some restriction. This work has as objective to analyze the influence of the restriction in the phase balance of austenite and ferrite, in the morphology of the austenite, in the

  10. Ganho de peso de novilhas mestiças submetidas ou não à esterilização pela introdução intrauterina de esferas inoxidáveis e ao uso ou não de modificador orgânico Weight gain of crossbred heifers submitted or not to sterilization by intrauterine stainless globes introduction and submitted or not to organic modifier use

    Directory of Open Access Journals (Sweden)

    M.G. Abba

    2010-04-01

    Full Text Available Avaliou-se o ganho de peso de novilhas mestiças, 1/4 Simental e 3/4 Nelore, empregando-se o método experimental de esterilização, que consiste na introdução intrauterina de esferas inoxidáveis. Foram utilizadas 100 novilhas nulíparas, destinadas ao abate, com idades entre 12 e 24 meses e com média de peso de 275kg. Todos os animais receberam o mesmo manejo alimentar, em sistema de pastejo em Brachiaria brizantha, com água e sal mineral ad libitum, e pesagens a intervalos de 28 dias, obedecido o jejum prévio de 16 horas. Os animais foram distribuídos aleatoriamente em quatro grupos (G experimentais: G1 - composto por 25 novilhas testemunhas; G2 - por 25 novilhas esterilizadas e aplicação de um modificador orgânico; G3 - por 25 novilhas esterilizadas; e G4 - por 25 novilhas não esterilizadas e aplicação de um modificador orgânico. Foram introduzidas 12 esferas de aço inoxidável, previamente esterilizadas, no útero de cada novilha. Houve maior ganho de peso total e diário entre os animais do G2, 140,50kg e 0,578g/dia vs 108,58kg e 0,447g/dia (G1, 103,73kg e 0,427g/dia (G3, 102,68kg e 0,423g/dia (G4, respectivamente. Esta técnica pode ser recomendada aos criadores.The weight gain in 1/4 Simental and 3/4 Nelore crossbred heifers was evaluated using an experimental method of castration, which consisted of stainless globes intra-uterine introduction. A total of 100 nulliparous heifers, destined to slaughter, aging from 12 to 24-months old and averaging 275kg were used. The animals were randomly distributed in four experimental groups: G1: control; G2: sterilized heifers plus application of organic modifier; G3: sterilized heifers; and G4: non sterilized heifers plus application of organic modifier. It was concluded that G2 showed higher weight gain - 140,50kg and 0,578g/day vs 108,58kg and 0,447g/day (G1, 103,73kg and 0,427g/day (G3, 102,68kg and 0,423g/day (G4. The sterilized heifers plus application of organic modifier is a

  11. Development of UO{sub 2}-Stainless Steel Fuel Plates Containing 30-50 Vol. % Oxide; Fabrication de plaques de combustible en acier inoxydable-UO{sub 2} contenant 30 a 40% d'oxyde (en volume); Razrabotka toplivnykh ehlementov iz nerzhaveyushchej stali i UO{sub 2}, soderzhashchikh 30 - 50 OB.% okisi; Elaboracion de placas de combustible de acero inoxidable UO{sub 2} conteniendo 30 a 40% de oxido (en volumen)

    Energy Technology Data Exchange (ETDEWEB)

    Lloyd, H. [Atomic Energy Research Establishment, Harwell (United Kingdom)

    1963-11-15

    lesquelles les particules de UO{sub 2} sont reparties uniformement dans la matrice en acier inoxydable, ainsi que le procede de revetement des plaques de combustible par rechargement a chaud. On a etudie des operations de laminage comprenant des deformations allant de 40% a 90%, a des temperatures allant jusqu'a 1300{sup o}C pour determiner les conditions optimums de production des noyaux de densite elevee et pour realiser une bonne cohesion entre les elements constitutifs des plaques, la fissuration des particules de UO{sub 2} etant reduite au minimum. L'auteui decrit la fabrication de grandes plaques de combustible composees de plaques a plusieurs noyaux, liees ensemble par laminage a chaud. L'auteur donne des indications sur les proprietes mecaniques de cermets UO{sub 2}-Inox contenant 30, 40 et 50% de UO{sub 2}(en volume), fabriques comme on l'a indique plus haut et essayes bruts de laminage et recuits a diverses temperatures allant jusqu'a 700{sup o}C. Il a utilise a cet effet des echantillons preleves les uns perpendiculairement, les autres parallelement au sens du laminage. Il examine en outre l'influence de la taille des particules de UO{sub 2} et de l'uniformite de leur repartition sur les proprietes mecaniques. Il a determine egalement les forces de liaison entre le noyau et la gaine pour des cermets similaires dans la meme gamme de temperatures. Le memoire contient encore les resultats d'essais de cyclage thermique entre 50 et 800{sup o}C entrepris pour determiner les effets de ce cyclage sur la structure du cermet et la stabilite de la liaison, apres 100, 500 et 1000 cycles. (author) [Spanish] La memoria expone los recientes progresos en lo relativo a la elaboracion de elementos combustibles del tipo de UO{sub 2} y acero inoxidable en placas, que contienen hasta 50% de UO{sub 2} en volumen. Describe la preparacion de particulas esfericas de UO{sub 2} sinterizado, de elevada densidad, de granulome tria comprendida entre 100 y 500, y la compactacion y sinterizacion

  12. Strain-Annealing Based Grain Boundary Engineering to Evaluate its Sole Implication on Intergranular Corrosion in Extra-Low Carbon Type 304L Austenitic Stainless Steel

    Science.gov (United States)

    Pradhan, S. K.; Bhuyan, P.; Kaithwas, C.; Mandal, Sumantra

    2018-07-01

    Strain-annealing based thermo-mechanical processing has been performed to promote grain boundary engineering (GBE) in an extra-low carbon type austenitic stainless steel without altering the grain size and residual strain to evaluate its sole influence on intergranular corrosion. Single-step processing comprising low pre-strain ( 5 and 10 pct) followed by annealing at 1273 K for 1 hour have resulted in a large fraction of Σ3 n boundaries and significant disruption in random high-angle grain boundaries (RHAGBs) connectivity. This is due to the occurrence of prolific multiple twinning in these specimens as confirmed by their large twin-related domain and twin-related grain size ratio. Among the iterative processing, the schedule comprising two cycles of 10 and 5 pct deformation followed by annealing at 1173 K for 1 hour has yielded the optimum GBE microstructure with the grain size and residual strain akin to the as-received condition. The specimens subjected to the higher number of iterations failed to realize GBE microstructures due to the occurrence of partial recrystallization. Owing to the optimum grain boundary character distribution, the GBE specimen has exhibited remarkable resistance against sensitization and intergranular corrosion as compared to the as-received condition. Furthermore, the lower depth of percolation in the GBE specimen is due to the significant disruption of RHAGBs connectivity as confirmed from its large twin-related domain and lower fractal dimension.

  13. Investigations On Crack Propagation Under Cyclical Isothermal And Thermo-mechanical Loadings For A Type 304-L Stainless Steel Used For Pressurized Water Reactor

    Directory of Open Access Journals (Sweden)

    Gourdin Cédric

    2018-01-01

    Full Text Available The integrity of structures exhibiting flaws in Pressurized Water Reactor (PWR has to be assessed to meet safety criteria. This paper deals with crack-propagation under cyclic thermo-mechanical loadings, as encountered in class I austenitic pipes of PWR’s. To have a conservative and reliable assessment of the crack propagation due to the in-service loading, various codes and standards use simplified method. For example, the RSE-M Code introduces a plastic correction depending on the proportion of the mechanical loading. An improvement of the current method requires additional investigations. Moreover, components loaded with transient or thermal fluctuations are not really in loadcontrolled conditions. To this end, a device called PROFATH was designed. The specimen is a pre-cracked thick-walled tube undergoing a set of thermal cycles and loaded with a static mechanical force. During the first part of the thermal cycle, a high frequency induction coil heats the external wall of the tube. Then, the heating system stops and the specimen is cooled down by running water inside the tube. Finite element calculations show that only a region half-way along the tube should be heated to ensure adequate structural effect. In the heated zone, the machining of a sharp circumferential groove ensures the propagation of a unique crack. An electro-mechanical jack controls the level of the mechanical static load. Tests have been carried out, and these tests allow having an evaluation of the pertinence of the correction proposed by the RSE-M Code for a significant plasticity.

  14. Study of oxide film formed in a pre cracked CT specimen of AISI 304L during a rising displacement test in 288 C water

    International Nuclear Information System (INIS)

    Diaz S, A.; Castano M, V.

    2007-01-01

    A study of oxide film formed inside pre cracked CT specimens during a rising displacement test in high temperature water (288 C) was performed in this study, The environmental conditions used during the experiments were similar to these found in Boiling Water Reactors (BWR): Normal Water Condition (NWC - 200 ppb O 2 ) and Hydrogen Water Chemistry (HWC - 125 ppb H2). The oxide films formed were analyzed by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). In both cases the oxide film consisted of two layers identified as magnetite. In the case of HWC the results agree with previous reports that mention magnetite as a stable phase in reducing conditions. However the stable phase in oxidant conditions is hematite and this work shows the presence of magnetite crystals in the narrow crack of CT specimens in spite of the oxidant environmental condition. This situation confirms that inside the pre-cracked CT specimens the environmental conditions were different from the oxidant bulk, and probably a poor oxygen access and stagnant conditions within the narrow crack promoted a localized reducing environment that permitted the magnetite formation. Is evident that the crack growth studies should consider the conditions inside crack because they are significantly different. (Author)

  15. Influência da refusão por plasma na microestrutura de um revestimento Fe-Mn-Cr-Si depositado por aspersão térmica arco elétrico sobre aço inoxidável ASTM A743-CA6NM Influence of plasma remelting on the microstructure of Fe-Mn-Cr-Si arc thermal spray coating deposited on ASTM A743-CA6NM stainless steel

    Directory of Open Access Journals (Sweden)

    Anderson Geraldo Marenda Pukasiewicz

    2012-03-01

    Full Text Available ASTM A743-CA6NM é um aço inoxidável martensítico muito utilizado na fabricação de turbinas hidráulicas devido a sua elevada tenacidade, entretanto apresenta restrições com relação à regiões recuperadas por soldagem. Diferentes técnicas de deposição tem sido aplicadas com o intuito de reduzir ou eliminar a tensão residual. A deposição de revestimentos resistentes a cavitação é outra forma importante de aumentar a vida útil destes componentes. O objetivo deste trabalho é avaliar a influência do tipo e intensidade de corrente de refusão por plasma na microestrutura, composição química e microdureza de um revestimento Fe-Mn-Cr-Si resistente a cavitação depositado por aspersão térmica arco elétrico sobre aço ASTMA743-CA6NM. Observou-se que a adoção de menores valores de corrente média, assim como a utilização de corrente pulsada reduziram a formação de ferrita δ e a espessura final da ZTA, possibilitando a formação do revestimento com menores alterações na microestrutura do metal base. Verificou-se que a microestrutura e microdureza dos revestimentos refundidos não se mostraram muito sensível a variações na diluição do metal base. A utilização de corrente contínua promoveu um alinhamento da estrutura dendrítica no sentido da movimentação da tocha, entretanto este comportamento não foi observado em revestimentos refundidos com corrente pulsada.ASTM A743-CA6NM martensitic stainless steel have been used in hydraulic turbines manufacturing, but show some restrictions in welded recovered areas. Different techniques have been applied in order to reduce or eliminate residual stress, with life increase. The deposition of cavitation resistant coatings is another important way to increase the service life of these components. The objective of this study is evaluate the influence of type and intensity of plasma remelting current on the microstructure, chemical composition and microhardness of the Fe

  16. Obtainment of TiO{sub 2} powders solar cells photo electrodes dye sensitized; Obtencao de pos de TiO{sub 2} para fotoeletrodos de celulas solares sensibilizados por corante

    Energy Technology Data Exchange (ETDEWEB)

    Forbeck, Guilherme; Folgueras, Marilena V., E-mail: guilhermeforbeck@hotmail.com [Universidade do Estado de Santa Catarina (PGCE/UDESC), SC (Brazil). Programa de Pos Graduacao em Ciencia e Engenharia de Materiais; Chinelatto, Adilson L. [Universidade Estadual de Ponta Grossa (UEPG), PR (Brazil). Programa de Mestrado em Engenharia e Ciencia dos Materiais

    2012-07-01

    Titanium dioxide in its polymorphic anatase phase, presents interesting properties for solar cells photo electrodes dye sensitized such as the forbidden energy band, high refractive index and high constant dielectric. In this study, powders of nanometric titanium dioxide were produced with predominantly the anatase phase and high surface area. We used the sol-gel method, and titanium tetraisopropoxide as a precursor, which was hydrolyzed in nitric acid solution. The obtained powder was heated to 450 ° C, varying the time for each lot (0, 20 or 120 minutes). The powders were characterized by X-ray diffraction, atomic force microscopy and surface area analysis. For all lots nanosized crystallites predominated. It was observed that in the batch with 120min heating an increase rutile content. The TiO{sub 2} with 20min heating showed high surface area, greater than that of TiO{sub 2} as taken reference.

  17. Clearance patterns for 111In-oxide particles deposited in specific airways of beagle dogs

    International Nuclear Information System (INIS)

    Snipes, M.B.; Muggenburg, B.A.; Griffith, W.C.; Guilmette, R.A.

    1994-01-01

    The International Commission on Radiological Protection (ICRP) has incorporated long-term retention of radioactive particles in conducting airways into its newly approved respiratory tract dosimetry model. This model is purported to provide a better basis for assessing risk associated with human inhalation exposures to radioactive particles. However, applying the new model requires an understanding of particle retention patterns in conducting airways of the lung. Studies are being conducted at ITRI to quantify long-term retention patterns for particles deposited at specific sites in conducting airways of Beagle dogs. The dog was selected as a model because long-term retention and clearance patterns for particles deposited in the lungs of dogs and humans are similar

  18. Efecto de las sales fundidas en la termofluencia del acero inoxidable tipo 304

    Directory of Open Access Journals (Sweden)

    González-Rodríguez, G.

    1995-06-01

    Full Text Available Problems caused by both hot corrosion and creep type-damage occurring on superheater and reheater tubes of power plants using heavy oil as fuel shorten their design lives. The acceleration of hot corrosion attack of boilers is caused by the presence of fuel ash deposits containing mainly vanadium, sodium and sulphur, in the form of Na2SO4 y V2O5 and V2O5 which form low melting point compounds. In addition to this, the tubes are exposed to the action of both high stresses and high temperatures, producing the so called creep damage. In this work, creep rupture tests were carried out in the temperature range of 620 to 660 °C in static air and in corrosive environments. The corrosive environments included 100 % Na2SO4, 100 % V2O5 and a 80 % V2O5 + 20 % Na2SO4 mixture.

    Los problemas causados tanto por la corrosión por sales fundidas, así como por la termofluencia en los tubos de los sobrecalentadores y recalentadores de una planta de potencia que usa combustibles fósiles, reducen su vida prevista en diseño. La aceleración de la corrosión por sales fundidas es causada por la presencia de cenizas que contienen principalmente vanadio, sodio y azufre en la forma de Na2SO4 y V2O5, los cuales forman mezclas con eutécticos de bajo punto de fusión. Adicionalmente, los tubos están expuestos a la acción de altos esfuerzos y altas temperaturas, lo cual propicia la termofluencia del material. En este trabajo, se han realizado ensayos de termofluencia hasta la rotura en aire y en ambientes corrosivos en el rango de temperaturas de 620 a 660 °C. Los ambientes corrosivos fueron 100 % Na2SO4, 100 % V2O5, y una mezcla 20 % Na2SO4-80 % V2O5.

  19. Evaluación electroquímica de soldaduras en tubos capilares de acero inoxidable

    Directory of Open Access Journals (Sweden)

    Javier E. Rodríguez-Yáñez

    2014-02-01

    Full Text Available La recuperación de capilares de acero 316L utilizados en pozos geotérmicos neutros, por medio de soldadura orbital autógena, se evalúa desde el punto de vista de su resistencia a la corrosión en las condiciones de utilización, mediante técnicas electroquímicas básicas. En el pretratamiento se encuentra que es más conveniente realizar un decapado químico previo a la soldadura por 5 minutos. Mientras que posteriormente a la soldadura, la aplicación de tratamiento térmico de reducción de tensiones no se justifica desde el punto de vista de la resistencia a la corrosión. También se plantea la comparación de los capilares soldados respecto a capilares nuevos y usados, teniendo los capilares soldados un comportamiento intermedio entre ambos.

  20. Thermal fatigue loading for a type 304-L stainless steel used for pressure water reactor: investigations on the effect of a nearly perfect biaxial loading, and on the cumulative fatigue life

    International Nuclear Information System (INIS)

    Fissolo, A.; Gourdin, C.; Bouin, P.; Perez, G.

    2010-01-01

    Fatigue-life curves are used in order to estimate crack-initiation, and also to prevent water leakage on Pressure Water Reactor pipes. Such curves are built exclusively from push-pull tests performed under constant and uniaxial strain or stress-amplitude. However, thermal fatigue corresponds to a nearly perfect biaxial stress state and severe loading fluctuations are observed in operating conditions. In this frame, these two aspects have been successively investigated in this paper: In order to investigate on potential difference between thermal fatigue and mechanical fatigue, tests have been carried out at CEA using thermal fatigue devices. They show that for an identical level of strain-amplitude, the number of cycles required to achieve crack-initiation is significantly lower under thermal fatigue. This enhanced damage results probably from a perfect biaxial state under thermal fatigue. In this frame, application of the multiaxial Zamrik's criterion seems to be very promising. In order to investigate on cumulative damage effect in fatigue, multi-level strain controlled fatigue tests have been performed. Experimental results show that linear Miner's rule is not verified. A loading sequence effect is clearly evidenced. The double linear damage rule ('DLDR') improves significantly predictions of fatigue-life. (authors)

  1. Resistencia a la corrosión localizada de juntas soldadas en un acero inoxidable duplex saf 2205

    OpenAIRE

    LEÓN, JOSÉ B; ARIAS, RAFAEL; SÁNCHEZ, ABBY; SUÁREZ, MARIBEL; QUINTERO, AMADO

    2008-01-01

    La corrosión por picadura es uno de los mecanismos de falla más frecuentes que se presentan en la industria química, petrolera y petroquímica. El hecho de que metales o aleaciones metálicas estén expuestos a ambientes agresivos inducen a fenómenos de corrosión como la «corrosión por picadura». El conocimiento de cómo se originan y la detección temprana de este mecanismo se traducen en ahorros económicos considerables debido a que se evitaría la interrupción momentánea de operaciones de una ac...

  2. Comportamiento frente a la corrosión de los aceros inoxidables AISI 430L P/M

    OpenAIRE

    Corpas, F. A.; Iglesias, F. J.; Ruiz, J. M.; Codina, S.; Ruiz, J. M.; García, V.

    2004-01-01

    In this paper we have studied the resistance to corrosion of the 430L ferritic stainless steels, manufactured by powder metallurgy. We have compared the behaviour of the different series of 430L stainless steels sintered, tempered and annealing, in different corrosive environments. Finally, the microstructure of the steels was determined by means of scanning electron microscopy. The better resistance to corrosion are produced in the steel annealing to 300ºC and 600ºC.

    En es...

  3. Formación de fase sigma en uniones soldadas de acero inoxidable súper dúplex fundido

    Directory of Open Access Journals (Sweden)

    Garin, J. L.

    2011-08-01

    Full Text Available This paper decribes the microstructural characteristics of weldments of cast super duplex stainless steel (J93404, being subjected to annealing processes to induce formation of sigma-phase at high temperatures. The influence of heating time at 1073 K, 1123 K and 1173 K upon precipitation of sigma in the heat affected zone, base metal and fusion zone of the weldments was analyzed. The experimental results revealed the formation of this intermetallic compound throughout decomposition of the ferritic phase into austenite and sigma. At earlier stages of the transformation the phase rapidly nucleates and growth along the ferrite-austenite grain boundaries, and then massively advances towards the bulk of the ferritic zone with greater effectiveness as temperature increases. The formation of sigma-phase in all weldments resembles the Johnson-Mehl-Avrami’s mechanism stated for nucleation and growth.

    El presente trabajo describe las características microestructurales de uniones soldadas de acero súper dúplex fundido (J93404, al ser sometidas a procesos de recocido para inducir la formación de fase sigma a altas temperaturas. Se analizó la influencia del tiempo de calentamiento a 1.073 K, 1.123 K y 1.173 K sobre la precipitación de fase sigma en la zona afectada térmicamente, metal base y zona de fusión de los conjuntos soldados. Los resultados experimentales evidenciaron la formación de este compuesto intermetálico por descomposición de la fase ferrítica en austenita y sigma. Al comienzo de la transformación la fase nuclea y crece rápidamente en los bordes de grano austenita-ferrita, extendiéndose luego masivamente hacia el seno de la zona ferrítica, con mayor efectividad en términos del aumento de la temperatura de proceso. La formación de sigma en todas las uniones soldadas obedece a un mecanismo de nucleación y crecimiento del tipo Jonson-Mehl-Avrami.

  4. Influence of microstructure on the microbial corrosión behaviour of stainless steels

    Directory of Open Access Journals (Sweden)

    Moreno, Diego Alejandro

    2000-08-01

    (EDX. En cada estado microestructural estudiado se han observado diferentes comportamientos en relación con su resistencia a la corrosión microbiana. Los aceros inoxidables austeníticos sensibilizados fueron más afectados por la presencia de aniones agresivos y los valores del potencial de picadura (Ep fueron más catódicos que en estado de recepción. Así mismo, se produce un incremento de la corrosión por la acción sinérgica entre los aniones cloruros y los sulfuros biogénicos. Se ha encontrado, en uno de los ensayos de biocorrosión, picaduras en el acero inoxidable martensítico del tipo UNS S42000. Se correlaciona la morfología observada en las picaduras con la composición química, la microestructura y el electrólito.

  5. Influencia de la microestructura en el comportamiento a fatiga de aceros inoxidables austeníticos con alto contenido en molibdeno

    OpenAIRE

    Oñoro, J.; Gamboa, R.; Ranninger, C.

    2006-01-01

    Austenitic stainless steels with molybdenum present high mechanical properties and corrosion resistance to aggressive environments. These steels have been used to tank and vessel components for high corrosive liquids as phosphoric, nitric and sulphuric acids. These materials with low carbon and nitrogen addition have been proposed candidates as structural materials for the international thermonuclear experimental reactor (ITER) in-vessel components. Molybdenum addition in austenitic stainless...

  6. Comparación entre los diagramas TTS obtenidos mediante los ensayos normalizados Huey y Strauss modificado para el acero inoxidable AISI 304

    Directory of Open Access Journals (Sweden)

    Otero, E.

    1996-04-01

    Full Text Available This work presents a comparison of Temperature-Time-Sensitization TTS diagrams obtained by Huey and modified Strauss standard, for detecting susceptibility to intergranular attack. The difference between these tests is the use of a strong or a slightly smooth oxidizing electrolyte. The diagrams obtained are different and if a sample tested by modified Strauss is sensitized, then it will be sensitized in the Huey test, but the contrary is not always true. This difference is because a sensitized sample has to have a continuous band lacking in chromium along the grain boundary in order to be sensitized in the modified Strauss test. This condition is not necessary in the Huey test.

    Se comparan los diagramas Temperatura-Tiempo-Sensibilización TTS, obtenidos mediante los ensayos normalizados de corrosión intergranular Huey y Strauss modificado, que, respectivamente, utilizan electrólitos fuerte y suavemente oxidantes, mostrándose que los diagramas obtenidos son diferentes. Si una muestra evaluada mediante el ensayo Strauss modificado se encuentra sensibilizada, entonces lo estará también en el ensayo Huey, pero no necesariamente ocurrirá lo contrario; esta diferencia se asocia a la necesidad de la existencia de una zona continua empobrecida en cromo a lo largo del límite de grano para que el material se sensibilice con respecto al ensayo Strauss modificado, condición innecesaria para el caso del ensayo Huey.

  7. Electrocoagulation applied to the decontamination of stainless steel parts contaminated with uranium; Electrocoagulacion aplicada a la descontaminacion de piezas de acero inoxidable contaminadas con uranio

    Energy Technology Data Exchange (ETDEWEB)

    Pujol P, A. A.; Monroy G, F. [ININ, Carretera Mexico-Toluca s/n, 52750 Ocoyoacac, Estado de Mexico (Mexico); Bustos B, E., E-mail: apujol@cideteq.mx [Centro de Investigacion y Desarrollo Tecnologico en Electroquimica, S. C., Parque Sanfandila s/n, Pedro Escobedo, 76703 Santiago de Queretaro, Qro. (Mexico)

    2017-09-15

    The decontamination of non-compact able radioactive waste, such as tools and equipment, has the purpose of removing surface radioactive waste from waste, in order to reduce its volume to be conditioned and stored. The application of treatment techniques based on electrochemistry, such as electro-coagulation (Ec) in the decontamination of waste or non-compact able radioactive materials of stainless steel containing uranium, was studied in the present work and its technical feasibility was evaluated. For this, tests were carried out, first with stainless steel plates coated with WO{sub 3}, to simulate a fixed contamination and to determine the best conditions of tungsten removal by Ec as: ph, support electrolyte, cell potential, type of counter electrode material and distance between the anode/cathode electrodes. In addition, different arrangements of configurations were tested for a rectangular acrylic cell and for a circular configuration cell, using flat plate electrodes and cylindrical electrodes to perform the removal process of the contaminant with the best conditions. In the case of the Ec, the mechanism that occurs is an electrodisolution of the iron plate, with the release of oxygen at the anode and detachment of the WO{sub 3} layer, all the material passing to the solution with the formation of iron hydroxides. Subsequently, from the best experimental conditions to remove WO{sub 3}, UO{sub 2} (NO{sub 3}) {sub 2} was used as radioactive contaminant to evaluate the feasibility of the decontamination process. Removal efficiencies of 90% uranium were obtained in 1 hour, ph = 1, using a molar solution of H{sub 2}SO{sub 4} as support electrolyte and potential of 2.4 V. Finally, after testing the different electrochemical cell (Ec) arrays at the laboratory level, radioactive decontamination of real pieces contaminated with U-238 was performed using the circular configuration arrangement under the best experimental conditions previously determined. (Author)

  8. “MEDICION DE PARAMETROS GENERADORES DE ESFUERZOS RESIDUALES DURANTE EL PROCESO DE SOLDADURA DE ACERO INOXIDABLE AUSTENITICO AISI 304L”.

    OpenAIRE

    García López, Christian Jesus

    2012-01-01

    En la actualidad los procesos de soldadura por arco eléctrico se han convertido en la técnica por excelencia para la unión del acero y sus aleaciones. Se puede mencionar que la importancia de la soldadura, es tal, que sin ella no serían posibles muchos de los productos y servicios que cotidianamente son consumidos o requeridos por las sociedades contemporáneas actuales. Cada vez con mayor longitud y diámetro se instalan líneas de tubería para la distribución y conducción de tod...

  9. Structure and properties of the Stainless steel AISI 316 nitrided with microwave plasma; Estructura y propiedades del acero inoxidable AISI 316 nitrurado con plasmas de microondas

    Energy Technology Data Exchange (ETDEWEB)

    Becerril R, F

    1999-07-01

    In this work were presented the results obtained by nitridation on stainless steel AISI 316 using a plasma generated through a microwave discharge with an external magnetic field using several moistures hydrogen / nitrogen to form a plasma. The purpose of nitridation was to increase the surface hardness of stainless steel through a phase formation knew as {gamma}N which has been reported that produces such effect without affect the corrosion resistance proper of this material. (Author)

  10. Waste water treatment of slaughterhouse through water treatment plants of stainless steel; Tratamiento de aguas residuales de mataderos mediante depuradoras compactas modulares de acero inoxidable

    Energy Technology Data Exchange (ETDEWEB)

    BaNales Sirvent, P.

    1997-06-01

    The object of this project was to develop an integral waste water treatment concept, based on compact module made of stainless steel, with a combination that allows to get performances according to given requirements stablished in the Community Directive 91/271/CEE (1991). The industrial pilot tests have been made in a slaughterhouse with a capacity of 20 tons per day. (Author)

  11. Intergranular stress corrosion in soldered joints of stainless steel 304.; Corrosion intergranular bajo esfuerzo en uniones soldadas de acero inoxidable 304

    Energy Technology Data Exchange (ETDEWEB)

    Zamora R, L [Instituto Nacional de Investigaciones Nucleares, Mexico City (Mexico)

    1994-12-31

    The intergranular stress cracking of welded joints of austenitic stainless steel, AISI 304, is a serious problem in BWR type reactors. It is associated with the simultaneous presence of three factors; stress, a critical media and sensibilization (DOS). EPR technique was used in order to verify the sensibilization degree in the base metal, and the zone affected by heat and welding material. The characterization of material was done. The objective of this work is the study of microstructure and the evaluation of EPR technique used for the determination of DOS in a welded plate of austenitic stainless steel AISI 304. (Author).

  12. Laser desensitization of austenitic stainless steel weld AHZ. Desensibilizacion con Laser de la zona afectada por el calor (ZAC) en aceros inoxidables austeniticos

    Energy Technology Data Exchange (ETDEWEB)

    Lee, C.H.; Kim, K.C.; Chang, R.W. (Welding Research Center Research Institute of Industrial Science and Technology, Pohang (Korea, Republic of))

    1994-01-01

    This paper addressed the fundamental understanding of sensitization phenomena in the weld HAZ of austenitic stainless steel and a method of desensitization utilizing LASER, without degradation of other corrosion resistance (pitting resistance). Sensitization in the weld HAZ was due to a formation of CR depleted zone along grain boundaries and twin boundaries by precipitation of Cr[sub 2]3C[sub 6] which contains 70-80% Cr and a small amount of Fe having a cubic-cubic relationship with the austenite matrix. Common morphologies of carbides were found to be of bar and globular shapes. As the holding time increased, carbides with coarsened globular (iodomorph) and dendrite shapes were also found. However, there was no significant variation in the composition of carbides and width of the Cr depleted zone with morphology. Laser desensitization could be obtained with a proper choice of the beam power and travel speed under a constant beam size. As long as the beam density reached a critical amount, carbides and Cr depleted zone completed zone completely disappeared. The critical travel speed increased with higher beam power, but was constant regardless of the original degree of sensitization. Pitting resistance of the LASER desensitized base metal and HAZ appeared to be far superior to that found in the sensitized condition. The protection potential in the hysteresis loop test was very sensitive to the degree of sensitization, revealing that the protection potential was dependent upon the propagation of the pits through the Cr depleted grain boundaries. (Author) 10 refs.

  13. Analysis of the passive layer developed on stainless steels implanted with chromium; Analisis de las peliculas pasivas generadas en aceros inoxidables implantados con cromo

    Energy Technology Data Exchange (ETDEWEB)

    Abreu, C. M.; Cristobal, M. J.; Novoa, X. R.; Pena, G.; Perez, M. C.

    2004-07-01

    This work studies the effect of chromium implantation on the development of passive layers generated electrochemically in alkaline medium over two stainless steels. The XPS analyses show that the layers generated on the implanted steels present less thickness together with similar composition compared to the unimplanted steels layers. However, SEM micrographs show that the layers grown on implanted steels present more defects and less adherence that the films on unimplanted steels. These changes together with the results obtained by Cyclic Voltammetry suggest an oxide structure modification, lattice structure or crystallinity state. (Author) 6 refs.

  14. Low temperature plasma carburizing of AISI 316L austenitic stainless steel and AISI F51 duplex stainless steel Cementação sob plasma à baixa temperatura do aço inoxidável austenítico AISI 316L e do aço inoxidável duplex AISI F51

    OpenAIRE

    Carlos Eduardo Pinedo; André Paulo Tschiptschin

    2013-01-01

    In this work an austenitic AISI 316L and a duplex AISI F51 (EN 1.4462) stainless steel were DC-Plasma carburized at 480ºC, using CH4 as carbon carrier gas. For the austenitic AISI 316L stainless steel, low temperature plasma carburizing induced a strong carbon supersaturation in the austenitic lattice and the formation of carbon expanded austenite (γC) without any precipitation of carbides. The hardness of the carburized AISI 316L steel reached a maximum of 1000 HV due to ∼13 at% c...

  15. Oxidation behavior of 304 stainless steel exposed to steam at high temperature

    Energy Technology Data Exchange (ETDEWEB)

    Jeong, H.; Ryu, J. R.; Park, G. H. [Kyunghee Univ., Yongin (Korea, Republic of); Yoo, T. G. [FNC Technology, Seoul (Korea, Republic of)

    2003-10-01

    An experiment was conducted on 304 stainless steel(SUS304L) at the LOCA(Lost of Coolant Accident) requirement temperature, 800 .deg. C to 1100 deg. C. SUS304L was used as clothing material and structural frame of LWR. Oxidation behavior of SUS304L by temperature and time was examined after the mechanical and chemical polishing of SUS304L plate. After oxidation, change in weight showed a linear pattern for the first 20 minutes and a parabolic pattern afterwards. Then, fine structure and oxidation layer of SUS304L plate were observed through OM photographing and oxidation characteristics of SUS304L were found through hardness measurement by depth of each plate and XRD(X-Ray Diffraction) photographing.

  16. Development of a Novel Approach for Fatigue Life Prediction of Structural Materials

    Science.gov (United States)

    2008-12-01

    Mughrabi, H., 1989, "Plasticity-Induced Martensitic Transformation of AISI 304L Stainless Steel ," Mat Sci Eng A114, pp. LI 1-LI 6. [26] Krupp, U...four structural materials: aluminum 7075T651 alloy, stainless steel AL6-XN, stainless steel 304L, and Aerospace Steel 4340. It was confirmed that...four structural materials: aluminum 7075T651 alloy, stainless steel AL6-XN, stainless steel 304L, and Aerospace Steel 4340. Fatigue and cyclic

  17. Effect of Adenine Concentration on the Corrosion Inhibition of Aisi ...

    African Journals Online (AJOL)

    This gave a surface coverage of 0.8956 and corrosion penetration rate of 0.022132mm/yr. Hence, the best adenine concentration for the corrosion inhibition of alloys 304L in 1.0M sulphuric acid solution to obtain optimum inhibition efficiency is 0.011M. Keywords: Corrosion, AISI 304L Steel, Inhibition efficiency, Degree of ...

  18. Characterization of stainless steel through Scanning Electron Microscopy, nitrided in the process of implantation of immersed ions in plasma; Caracterizacion de acero inoxidable mediante Microscopia Electronica de Barrido nitrurado en el proceso de implantacion de iones inmersos en plasmas

    Energy Technology Data Exchange (ETDEWEB)

    Moreno S, H

    2003-07-01

    The present project carries out the investigation of the nitridation of the austenitic stainless steel schedule 304, applying the novel technology of installation of nitrogen ions in immersed materials in plasma (Plll), by means of which they modify those properties of the surface of the steel. The obtained results by means of tests of Vickers microhardness, shows that the hardness was increment from 266 to 740 HV (microhardness units). It was determined by means of scanning electron microscopy, the one semiquantitative chemical analysis of the elements that constitute the austenitic stainless steel schedule 304; the obtained results, show to the nitrogen like an element of their composition in the pieces where carried out to end the PIII technology. The parameters of the plasma with which carried out the technology Plll, were monitored and determined by means of electric probes, and with which it was determined that the density of particles is stable in the interval of 1x10{sup -1} at 3x10{sup -1}Torr, and it is where better results of hardness were obtained. That reported in this work, they are the first results obtained when applying the technology Plll in Mexico, and with base in these, it is even necessary to investigate and to deepen until to dominate the process and to be in possibilities of proposing it to be carried out and exploited in an industrial way. (Author)

  19. Influence of the chemical composition, heat and surface treatment in the biofouling of austenitic stainless steels; Influencia de la composicion quimica, del tratamiento termico y del acabado supreficial en el bioensuciamiento de aceros inoxidables austeniticos

    Energy Technology Data Exchange (ETDEWEB)

    Sarro, M. I.; Aleman, O.; Moreno, D. A.; Roso, M.; Ranninger, C.

    2004-07-01

    The main objective of this study was to analyse the biofouling processes in the kinds of stainless steels used normally in industry (UNS S30400, UNS S30403 and UNS S31600), with different surface treatments after grinding and polishing. The study was developed using two microscopy techniques. Scanning Electron Microscopy (SEM) was used to evaluate the microorganisms distribution in the materials, and Epi fluorescence Microscopy was used to evaluate the viability of cells in the biofilm. The results revealed the influence of the material, heat treatment, surface treatment and roughness in the biofouling processes in the stainless steel assays. (Author) 33 refs.

  20. Construção e aplicação de eletrodo de aço inoxidável UNS S31254 como eletrodo indicador em titulações condutimétricas

    Directory of Open Access Journals (Sweden)

    Terra Lúcia Helena

    2003-01-01

    Full Text Available UNS S31254 SS electrodes have been built to substitute platinum in conductimetric titrations. The electrodes were tested in both acid-basic titration (chloridric acid and sodium hydroxide and precipitation titration (sodium chloride and argentum nitrate as titrant. The practical application was exemplified from conductimetric tritations of HF fraction three-quarters HNO3 mixtures used in metalurgical industry to passivate stainless steels. The results were compared with those obtained using commercial platinum electrodes. The equivalent volumes obtained were comparable within 3% experimental error. Its application depends on the nature of electrolyte. These results have shown that stainless steel, less expensive than platinum (about three order of magnitude, can substitute platinum electrodes in routine analyses and didactic laboratories.

  1. Circumferential welding applied for inox steel super duplex UNS S32750 using the process MIG using CMT® control; Soldagem circunferencial do aço inoxidável super duplex UNS S32750 pelo processo MIG com controle CMT®

    Energy Technology Data Exchange (ETDEWEB)

    Invernizzi, Bruno Pizol

    2017-07-01

    This study carried out circumferential welding experiments in UNS S32750 Super Duplex Stainless Steel tubes using diameters of 19,05 mm and 48,20 mm. Welds were performed using various welding parameters on a MIG machine with Cold Metal Transfer® CMT control. The weld joints were evaluated by visual and dimensional inspection in addition to the Vickers microhardness and traction tests, as well as the microstructural analysis in conjunction with phase precipitation analysis, which was performed according to practice A of ASTM A923, and corrosion test in accordance with practice A of ASTM G48 in conjunction with ASTM A923. The results indicated that welds performed in pipes with a diameter of 19.05 mm showed a weld joint with unacceptable dimensions according to the standard, this condition being attributed the use of a high wire diameter for the welding conditions used. Welding performed for pipes with a diameter of 48.20 mm showed a lack of penetration under the conditions employed when welded by the conventional CMT® process. In the case of the use of CMT® combined with pulsed arc, under conditions that generated greater heat input during welding, this resulted in total penetration of the joint and adequate surface finish. The results indicated that welding using the CMT® process combined with pulsed arc, under the conditions (parameters) employed generated good surface finish, combined mechanical properties, meeting standards requirements, as well as a balanced microstructure and high resistance to corrosion. (author)

  2. Recubrimiento de Stellite 6 sobre acero inoxidable realizado con láser de CO2 para válvulas de escape de motores diesel

    Directory of Open Access Journals (Sweden)

    Cadenas, M.

    2002-12-01

    Full Text Available To reduce the recovery or the replacement costs of diesel engine exhaust valves, they are manufactured with an economic base material, and a coating which is deposited on the seat valve in order to reach high hardness and good impact, corrosion and high temperature wear resistance (>550 °C and without lubrication. In this work, appropriate laser cladding parameters have been determined to obtain Stellite 6 coatings over AISI 304 steel (as plane test specimens and SAE EV8 steel (as valves substrates. One and two superimposed tracks were deposited on the seat valves, and modifying the laser power as a function of the rotated angle at the beginning and the end of the circular tracks, pores and cracks have been minimized and the thickness of the track were made uniform. Hardness, dilution and final microstructure of the different coatings have been analysed. A 10 % dilution and 550 HV in the tracks over plane test specimens was observed, while valves with one track showed 25 % and 430 HV respectively. With two superimposed tracks the hardness was up to 470 HV in the upper track.

    Para abaratar el coste de recuperación o sustitución de válvulas de escape en motores diesel, estas se fabrican con un material base económico, recubriéndose el asiento de la válvula con otro material al que se exigirá elevada dureza y buena resistencia al impacto, a la corrosión y al desgaste erosivo en caliente (>550 °C y sin lubricación. Partiendo de esta idea, en el presente trabajo se han determinado los parámetros adecuados para realizar, mediante la técnica de plaqueado láser, un recubrimiento con Stellite 6, sobre sustratos de acero AISI 304 (probetas planas y SAE EV8 (válvulas reales. Sobre las válvulas, se depositaron uno y dos cordones superpuestos, se minimizó la presencia de poros y grietas, modificando el grado de solape inicial y final de los cordones circulares y la potencia en función del ángulo girado. Así, se consiguieron cordones de espesor uniforme. Tras los tratamientos, se estudiaron la dureza, dilución y microestructura final de los distintos recubrimientos, observándose, en los cordones sobre probetas planas, diluciones del 10 % y durezas de 550 HV, mientras que, en las válvulas con un cordón, eran del 25 % y 430 HV, respectivamente. Con dos cordones superpuestos, la dureza llegaba a 470 HV en el cordón superior.

  3. Applications of the essay at slow deformation velocity in pipes of stainless steel AISI-304; Aplicaciones del ensayo a velocidad de deformacion lenta en tuberias de acero inoxidable AISI-304

    Energy Technology Data Exchange (ETDEWEB)

    Zamora R, L.; Mora R, T. De la [ININ, 52045 Ocoyoacac, Estado de Mexico (Mexico)

    2004-07-01

    Nowadays is carried out research related with the degradation mechanisms of structures, systems and/or components in the nuclear power plants, since many of the involved processes are those responsible for the dependability of these, of the integrity of the components and of the aspects of safety. The purpose of this work, was to determine the grade of susceptibility to the corrosion of a pipe of Austenitic stainless steel AISI 304, in a solution of Na CI (3.5%) to the temperatures of 60 and 90 C, in two different thermal treatments - 1. - Sensitive 650 C by 4 hours and cooled in water. 2. Solubilized to 1050 C by 1 hour and cooled in water.

  4. Microbiologically influenced corrosion evaluation on brass (UNS C68700, UNS C443) and AISI 316 stainless steel; Estudio de la influencia microbiologica en la corrosion de latones (UNS C68700, UNS C443) y acero inoxidable AISI 316

    Energy Technology Data Exchange (ETDEWEB)

    Ohanian, M.; Diaz, V.; Corengia, M.; Russi, P.; Pianzzola, M. J.; Menes, R. J.

    2014-10-01

    Microorganisms may play an important role in the corrosion process and generate conditions which affect the rate and/or the mechanism of deterioration. They become visible by the formation of bio films: clusters of microorganisms and extracellular polymers. These bio films affect not only the durability of the material, but also reduce the heat transfer. The present work studied the growth of aerobic and anaerobic heterotrophic microorganisms and sulfate reducing bacteria on aluminum brass (Uns C.a.), admiralty brass (Uns C.a.) and stainless steel Asi 316 in exposure experiments held in the Bay of Montevideo (Uruguay). The influence of the biofilm growth on the corrosion behavior was studied by electrochemical techniques: polarization curves and Electrochemical Impedance Spectroscopy (Ei). The selection of the most suitable material for the exposure conditions is discussed and hypotheses of the corrosion mechanism are presented. Although stainless steel Asi 316 presented the lowest corrosion rate it showed localized deterioration. (Author)

  5. Efecto del contenido de azufre y del grado de desoxidación sobre la ductilidad en caliente de aceros inoxidables austeníticos resulfurados en estado de solidificación

    OpenAIRE

    Botella, J.; Sánchez, R.

    1998-01-01

    The manufacture of free machining austenitic stainless steels features a specific drawback derived from their high sulphur content, which is needed for generating, into the austenitic matrix, inclusions to optimize the different machining operations. However, sulphur has a harmful effect on hot workability. This paper deals with assessing the effect of sulphur content and deoxidation level on the hot ductility of resulphurized austenitic stainless steels in as cast condition. Hot tensile test...

  6. Relaciones cuantitativas entre los contenidos de azufre y de sulfuros en los aceros inoxidables tipo AISI 303: influencia de la composición química de los sulfuros

    OpenAIRE

    Botella, J.; Merino, C.; Heredia, M. A.; Almagro, J.

    1999-01-01

    The work has been done with ten AISI 303 stainless steel rods which have similar chemical compositions, except for sulphur which varies between 0.25 and 0.36%. These steels are studied by Scanning Electron Microscopy (SEM) and Energy Dispersive X-Ray Spectrometry (EDX). The sulphides are chemically microanalysed and the occupied volume determined by automatic image analysis. It can be inferred that the chemical composition of sulphides in AISI 303 steels is variable to some extent even though...

  7. T.I.G. Welding of stainless steel. Numerical modelling for temperatures calculation in the Haz; Soldadura T.I.G. de acero inoxidable. Modelo numerico para el calculo de temperaturas en la ZAT

    Energy Technology Data Exchange (ETDEWEB)

    Martinez-Conesa, E. J.; Estrems-Amestoy, M.; Miguel-Eguia, V.; Garrido-Hernandez, A.; Guillen-Martinez, J. A.

    2010-07-01

    In this work, a numerical method for calculating the temperature field into the heat affected zone for butt welded joints is presented. The method has been developed for sheet welding and takes into account a bidimensional heat flow. It has built a computer program by MS-Excel books and Visual Basic for Applications (VBA). The model has been applied to the TIG process of AISI 304 stainless steel 2mm thickness sheet. The welding process has been considered without input materials. The numerical method may be used to help the designers to predict the temperature distribution in welded joints. (Author) 12 refs.

  8. INFLUENCIA DE LA NITRURACIÓN POR PLASMA SOBRE EL COMPORTAMIENTO A LA CORROSIÓN Y LA ADHESIÓN DE RECUBRIMIENTOS DLC SOBRE ACERO INOXIDABLE AISI 420

    Directory of Open Access Journals (Sweden)

    Jorge N. Pecina

    2016-01-01

    Full Text Available En este trabajo se estudió el comportamiento a la corrosió n y la adhesión de dos rec ubrimientos DLC (“Diamond Like Carbon ” , “Soft” y “Hard”, depositados por PACVD (“Plasma Assisted Chemical Vapour Deposition” sobre acero AISI 420, templado y revenido y /o nitrurado por plasma . Se analizaron por espectroscopía Raman y midió dureza en superficie. Se observó la microestructura por OM y SEM. Se realizaron pruebas de adhesión con indentación Rockwell C . S e practicaron ensayos de Niebla Salina e inmersión en HCl . Los DLC “ Soft ” presentaron una dureza de 5 00 HV y un espesor de 2 0 μm , mientras que los “ Hard ” tuvieron 1400 HV y 2 ,5 μm. Ambos recubrimientos presentaron bajo coeficiente de fricción y buena adhesión sobre el sustrato nitrurado . También presentaron buena resistencia a la corrosión atmosférica. En HCl el DLC retardó la degradación que se presentó rápidamente en las muestras sin recubrir.

  9. Ionic implantation by plasma in titanium and stainless steels used in prosthesis and medical instruments; Implantacion ionica por plasma en titanio y aceros inoxidables usados en protesis e instrumental medico

    Energy Technology Data Exchange (ETDEWEB)

    Munoz C, A. E. [ININ, 52750 La Marquesa, Estado de Mexico (Mexico)

    2008-07-01

    A study of a process known as plasma immersion ion implantation (PIII) of nitrogen at low voltages (< 4 kV) into three kind of samples: 1) austenitic stainless AISI 316-L steel plates, 2) ferritic stainless AISI 434 steel-based dentistry drills and 3) commercially pure titanium (CPTi) disks. On the case of CPTi the study was conducted in nitrogen- oxygen calibrated mixtures: 90% N-10% O, 80% N-20% O, 70% N-30% O and in 99.5% pure oxygen and 99.9% pure nitrogen. The PIII process was carried out by using a direct current plasma source controlled both in voltage and current, a negative voltage pulse modulator, a stainless AISI 304 steel vacuum chamber and a rod of the same material, horizontally located in the upper region of the chamber, which plays the role of anode in the plasma discharge. The purpose of the nitriding is forming a relatively thick layer on the surface of the steel specimens in order to enhance their both microhardness and general corrosion performances, desirable in medical applications. This layer contains interstitial nitrogen atoms ({approx}24% at.) which gives place to a deformed lattice (expanded phase) of the steel. Vickers microhardness and potentiodynamic tests (the latter in agreement to the norm ASTM G-61-89) confirm an increase of microhardness up to three times and a decrease of general corrosion rate in one order of magnitude. The nitriding of de dentistry drills is aimed at inhibiting the pitting corrosion produced by the asepsis process which results in pit nucleations, their propagation and consequent fractures when being under cyclic stress (fatigue). Scanning electron microscope micrographs reveal the risks involved in surpassing the critical treatment simple temperature of 450 C as the PIII process itself induces pitting. On its part, cyclic (ASTM G-61) potentiodynamic tests indicate an excellent pitting corrosion resistance of the samples treated under 450 C. In turn, the treatment of CPTi was meant to develop oxidized and/or nitrided replacement layers of high biocompatibility in the form of rutile phase titanium oxide, which favours the bony-integration, along with enhanced wear resistance layers of improved microhardness. The superficial treatments of titanium largely succeed in these purposes both as for microhardness and for most parameters of the biological environment corrosion (simulated in a Hanks solution), surpassing the performance of conventional prosthetic metals, as reported in the current literature, including the Co-Cr-Mo alloy as to its wear resistance. (Author)

  10. Nondestructive metallographic control for the determination of the degree of sensitivity to intragranular corrosion of austenitic stainless steels; Control metalografico no destructivo para determinar el grado de sensibilidad a la corrosion intergranular de aceros inoxidables austeniticos

    Energy Technology Data Exchange (ETDEWEB)

    Diaz S, A; Juarez G, F [Instituto Nacional de Investigaciones Nucleares, Mexico City (Mexico)

    1994-12-31

    The relationship between: microstructure-heat treatment, microstructure-mechanical properties, microstructure-corrosion resistance make that the study of the microstructure of metals and alloys be a powerful tool either in technical-scientific research as in the control of materials. The destructive nature of metallographic analysis create a serious limitation in the case of control methods for failures in the service. The `Tampon` Method make possible the polishing `In situ` of the majority of metals and alloys of industrial use, and the method of nitrocellulose replica allows the obtention of an accurate copy of the metallographic structure which can be observed by transparency or reflection. The purpose of this work is to show in a general way, the fundamental principles of the technique for the obtention of replicas, as well as the countless benefits of its utilization in the national industry. (Author).

  11. Evaluación de la fuerza de doblado y de fricción en el conformado de chapa de acero inoxidable AISI 304 DDQ mediante ensayos de doblado en condiciones multiaxiales de embutición

    Directory of Open Access Journals (Sweden)

    Coello, J.

    2012-08-01

    Full Text Available Die radius is a critical area from the viewpoint of friction in forming processes. Moreover the sheet, that has been previously deformed in flange area, suffers bending and unbending stresses. Then, die-sheet contact in die radius must be especially considered in order to guarantee the suitable lubrication conditions. In the present work, a test method is carried out for evaluating an AISI 304 DDQ steel under similar conditions to those existing in the die radius area and that, usually, are not really reproduced in traditional bending under tensions tests. Deformation under pure shear condition, the bending and the radius angle have been established as variables of the tests. Results allow to obtain the apparent pressure sheet-bending tool, that increases with bending angle and decreases with tool radius. This last variable is the most significant while the bending angle has lesser influence. Although experimental results present some concordances with values obtained by analytical methods, some corrections must be considered in them in order to improve the theoretical values.

    El radio de entrada a la matriz se considera una de las zonas críticas en los procesos de conformado de chapa mediante embutición profunda. El análisis de la fuerza de fricción y de doblado existentes resulta importante para predecir el comportamiento de la chapa en dicha zona, así como para garantizar una lubricación adecuada a las condiciones de procesado. En el presente trabajo, se aplica un método de ensayo que evalúa las acciones en el proceso de doblado del acero AISI 304 DDQ bajo condiciones similares a las que sufre el material en los procesos de embutición y que no son reproducidas por los clásicos ensayos de doblado bajo tensión. Se establecen como variables la deformación experimentada previamente por el material en condiciones típicas de cortante puro, “pure shear”, el ángulo de doblado y el radio de doblado. Los resultados obtenidos permiten establecer la presión de contacto herramienta-chapa, creciente con el ángulo de doblado y decreciente con el radio. Aunque dichos resultados guardan tendencias similares a los obtenidos de forma analítica, aconsejan introducir correcciones con el fin de conseguir mayor grado de concordancia del método analítico.

  12. Avaliação da resistência à corrosão de implantes em aços inoxidáveis ISO 5832-9 e F138 removidos de pacientes

    Directory of Open Access Journals (Sweden)

    Elison da Fonseca e Silva

    2012-01-01

    Full Text Available This work has compared the surfaces of two different steel samples used as orthopedical implants, classified as ASTM F138 and ISO5832-9, through optical emission spectroscopy, by means of SEM and EDS. The samples (implants were also submitted to potentiodynamic cyclic polarization in Ringer lactate and NaCl 0.9 M L-1 solutions; ISO5832-9 sample did not show any kind of localized corrosion, but in the case of F138 steel was observed a pit localized corrosion in both solutions. In Ringer lactate solution it was observed a loss of about 63% for nickel and 26% for iron for F138 stell, compared to the initial composition.

  13. Study of cyclic oxidation for stainless steels AISI 309 T 253 M A, with low additions of cerium; Estudio de la oxidacion ciclica de los aceros inoxidables AISI 309 T 253 MA, con pequenas adiciones de Cerio

    Energy Technology Data Exchange (ETDEWEB)

    Velazquez F, G.L.; Martinez, M.; Ruiz, A. [Universidad Nacional Experimental Politecnica (UNEXPO) - Vicerrectorado de Puerto Ordaz, Centro de Estudios de Corrosion. Puerto Ordaz. venezuela (Venezuela)

    1998-12-31

    It has been detected that the addition of small amounts (<1%) of the so called `reactive elements` such as Cerium to Fe-Cr alloys that was utilized in oxidating environment at high temperatures improving its resistance to oxidation under isothermal and cyclic conditions. In this work, it was evaluated the behavior under cyclic oxidation conditions for an austenitic stainless steel at chromium-nickel (253MA) with cerium addition, and comparing it with the AISI 310S austenitic stainless steel. The cyclic oxidation essays consist of five cycles by 24 hours each one, following of a cooling in air until ambient temperature from the temperatures of 850, 900 and 950 Centigrade, registering the gain mass of the specimen at end of each cycle. In order to this were prepared samples with dimensions of 20 mm. x 10 mm. x 1 mm. Later to the oxidation essays was evaluated the morphology of the corrosion products layer by scanning electron microscopy. The present phases were identified by X-ray diffraction and by chemical microanalysis by Dispersive energy (EDAX). The results obtained show that the steel with cerium addition, presents a higher adherence and resistance to the spalling noting that the cerium promotes the casting anchor of the oxides layer to matrix and by reducing the grain size of the layer improving its plasticity. Additionally the cerium promotes the preferential oxidation of the forming elements of protective layers like the chromium. (Author)

  14. Effect of biofilm in the corrosion of austenitic stainless steels in wastewater treatment plants; Efecto de la biopelicula en la corrosion de aceros inoxidables austeniticos en estaciones depuradoras de aguas residuales

    Energy Technology Data Exchange (ETDEWEB)

    Bethencourt, M.; Garcia de Lomas, J.; Corzo, A.; Villahermosa, D.; Matres, V.

    2010-07-01

    In this work, the influence of the biofilm in the corrosion process of different alloys of stainless steel was studied in two sampling points in a wastewater treatment plant during 4 years. The physicochemical microenvironment within the biofilm was characterized through O{sub 2}, H{sub 2}S and pH microelectrodes. Corrosion rates were quantified from the number, diameter and depth of pits. The results show a remarkable development of the biofilm and a significantly greater number of pits in the grit removal channel than in the sludge recirculation channel. Based on the characteristics of the water phase and microelectrode measurements, our results suggest that biofilm induced corrosion throughout 3 mechanisms: creation of differential aeration cells, areas with different pH and areas having high sulphide production which may react with metal ions. (Author) 54 refs.

  15. Oxidación en vapor de agua del acero inoxidable AISI 316 recubierto con Al-Si por deposición química de vapor en lecho fluidizado

    Directory of Open Access Journals (Sweden)

    José Luddey Marulanda Arevalo

    2014-06-01

    Full Text Available Stainless steel AISI 316 was coated with aluminum-silicon by Chemical Vapor Deposition in Fluidized Bed Reactor (CVD-FBR to 540°C and subsequently heat treated to improve its mechanical properties and its behavior against oxidation, by inter diffusion of the alloying elements. Later, oxidation was performed austenitic stainless steel aluminum-silicon coated at temperatures of 700 and 750°C, in an environment with 100% steam, to evaluate their performance. Mass gain graphs were made and oxide films were analyzed by SEM and X-ray diffraction to observe the morphology of the oxides. Thermodynamic simulation was carried out during oxidation in water vapor of the substrates for possible solid phases which could be formed. The form of attack at 750°C is similar to 700°C, although the rate of oxidation is increased, because the diffusion of the alloying elements and the oxidation reactions are faster. These coatings have good resistance to oxidation in water vapor and forming an alumina surface layer which protects the substrate from corrosion attack.

  16. Effects of nitrogen and pulsed mean welding current in AISI 316 austenitic stainless steel solidification cracks; Efecto del nitrogeno y la corriente media pulsada de soldadura en la formacion de grietas de solidificacion en aceros inoxidables AISI 316L

    Energy Technology Data Exchange (ETDEWEB)

    Trevisan, R. E.; Braga, E.; Fals, H. C.

    2002-07-01

    An analysis of the influence of nitrogen concentration in the weld zone and the pulsed mean welding current in the solidification crack formation is presented in this paper. The AISI 316L austenitic stainless steel was employed as the metal base. The welding was done using CC+ pulsed flux cored are welding process and AWS E316L wire type. The tests were conducted using CO{sub 2} shielding gas with four different nitrogen levels (0,5; 10 and 15%) in order to induce different nitrogen weld metal concentrations. The pulsed mean welding current was varied in three levels and the. Transvarestraint tangential strain test was fixed of 5%. The results showed that the solidification cracking decreased as the pulsed mean welding current increase. It was also verified that an increase of the weld zone nitrogen level was associated with a decrease in both the total length of solidification crack and the amount of {delta} ferrite. (AUthor) 20 refs.

  17. Apical displacement produced by rotary nickel-titanium instruments and stainless steel files Deslocamento apical produzido por instrumentos de níquel-titânio acionados a motor e limas de aço inoxidável

    Directory of Open Access Journals (Sweden)

    José Roberto Vanni

    2004-03-01

    Full Text Available The aim of this study was to evaluate the apical displacement produced by different rotary nickel-titanium instruments, testing the hypothesis that rotary systems with nickel-titanium instruments produce lower mean values of apical displacement than stainless steel hand instruments. A total of 100 maxillary permanent first molars were selected for the study. The mesiobuccal roots were sectioned at the top cervical third and embedded in blocks of self-curing resin. The specimens were randomly divided into 5 groups and the root canals were prepared using the following nickel-titanium instruments: Group 1 - Quantec system 2000 (Analytic Endodontics, Mexico; Group 2 - Pro-File T.0.04 (Dentsply/Maillefer, Switzerland; Group 3 - Pro-File Series 29 T.0.04 (Dentsply Tulsa, Switzerland; Group 4 - Pow-R T.0.02 (Moyco-Union Broach, USA. Specimens in Group 5 were prepared using stainless steel hand instruments Flexofile (Dentsply/Maillefer, Switzerland. All root canals were previously submitted to cervical preparation using Orifice Shaper instruments #1, 2, 3 and 4 (Dentsply/Maillefer, Switzerland. After odontometry, the remaining root canal was shaped employing increasingly larger instruments, so that the final instrument corresponded to Quantec #9, Pro-File Series 29 #6, and #35 for the other groups. Specimens in Groups 1 to 4 were prepared using an electric handpiece with 16:1 reduction at 350 rpm. The specimens in Group 5 were manually prepared. Apical displacement was measured and recorded by means of radiographic superimposition on a specific desk. Statistical analysis (ANOVA of the results revealed that all groups presented apical displacements. Considering only the nickel-titanium instruments, Group 4 showed the lowest mean value while Groups 2 and 3 produced the highest mean apical displacement values (pO objetivo deste trabalho foi avaliar o deslocamento apical produzido por diferentes instrumentos de níquel-titânio acionadas a motor testando a hipótese de que os sistemas rotatórios que usam instrumentos de níquel-titânio produzem valores médios de deslocamento apical menores que as limas manuais de aço inox. Foram utilizados 100 primeiros molares permanentes superiores, cujas raízes mesiovestibulares foram separadas e incluídas em blocos de resina autopolimerizável. Os corpos de prova foram divididos aleatoriamente em 5 grupos e os canais radiculares preparados com instrumentos de níquel-titânio: Grupo 1 - sistema Quantec 2000 (Analytic Endodontics, México; Grupo 2 - Pro-File T.0.04 (Dentsply/Maillefer, Suíça; Grupo 3 - Pro-File Série 29 T.0.04 (Dentsply Tulsa, Suíça; Grupo 4 - Pow-R T.0.02 (Moyco-Union Broach, EUA; e Grupo 5 (limas manuais - limas manuais de aço inox Flexofile (Dentsply/Maillefer, Suíça. Todos os canais mesiovestibulares foram submetidos a um preparo cervical prévio utilizando-se instrumentos Orifice Shaper números 1, 2, 3 e 4 (Dentsply/Maillefer, Suíça. Realizada a odontometria, o restante do canal radicular foi modelado a partir dos instrumentos do menor para o maior calibre de tal ordem que o instrumento final de preparo correspondeu ao número 9 para o Quantec, número 06 para o Pro-File Série 29 e o número 35 para os demais grupos. Nos grupos de 1 a 4 foi utilizado motor elétrico com contra-ângulo de redução de 16:1 numa velocidade de 350 rpm. No grupo 5 o preparo foi realizado manualmente. A análise dos resultados (ANOVA, obtidos pela sobreposição radiográfica numa plataforma especifica, demonstraram que todos os grupos apresentaram deslocamentos apicais, sendo que o menor valor médio foi verificado no grupo 4 e os maiores valores médios foram observados nos grupos 2 e 3 (p<0,001.

  18. Effect of the microstructure on the sensibilization to intergranular corrosion of a 24. 7 Cr7. 4Ni duplex stainless steel. Efecto de la microestructura en la sensibilizacion a la corrosion inoxidable duplex 24, 7Cr7,Ni

    Energy Technology Data Exchange (ETDEWEB)

    Otero, E; Pardo, A; Merino, C; Hierro, P; Perez, F J

    1993-01-01

    The influence of microstructure on the resistance to intergranular corrosion of a 24.4Cr7.4Ni is studied. The results are discussed both in terms of the Huey experiment as well as of the sweeping corresponding to the experimental conditions under which the experiments have been performed. Author (11 refs.)

  19. Corrosion of high purity Fe-Cr-Ni alloys in 13 N boiling nitric acid

    International Nuclear Information System (INIS)

    Ohta, Joji; Mayuzumi, Masami; Kusanagi, Hideo; Takaku, Hiroshi

    1998-01-01

    Corrosion in boiling nitric acid was investigated for high purity Fe-18%Cr-12%Ni alloys and type 304L stainless steels (SS). Owing to very low impurity concentration, the solution treated high purity alloys show almost no intergranular corrosion while the type 304L SS show severe intergranular corrosion. Both in the high purity alloys and type 304L SS, aging treatments ranging from 873 K to 1073 K for 1 h enhance intergranular corrosion. During the aging treatments, impurities should be segregated to the grain boundaries. The corrosion behaviors were discussed from a standpoint of impurity segregation to grain boundaries. This study is of importance for purex reprocessing of spent fuels

  20. Teste intradérmico com proteínas recombinantes de Mycobacterium bovis como antígenos em Cavia porcellus

    Directory of Open Access Journals (Sweden)

    Elaine S.P. Melo

    2014-10-01

    Full Text Available O teste intradérmico para o diagnóstico da tuberculose bovina utiliza derivados proteicos purificados (PPD de Mycobacterium bovis que são capazes de induzir reações de hipersensibilidade em animais infectados. No entanto, apresenta baixa especificidade devido à ocorrência de reações cruzadas com outras micobactérias. Neste sentido, o objetivo desse trabalho foi produzir proteínas recombinantes (ESAT-6, PE13, PE5 e ESX-1 de Mycobacterium bovis e avaliá-las como antígenos em teste intradérmico utilizando Cavia porcellus como modelo, e verificar se as condições empregadas na purificação (nativa ou desnaturante interferem no desempenho antigênico dessas proteínas. As proteínas foram testadas em Cavia porcellus previamente sensibilizados com cepa M. bovis AN5 inativada, individualmente (160 µg ou combinadas na forma de um coquetel (40 µg cada. O coquetel de proteínas induziu reações de hipersensibilidade nos animais sensibilizados significativamente superiores (p=0,002 as observadas nos animais não sensibilizados, possibilitando diferenciação. No entanto, as proteínas isoladamente não foram capazes de promover essa diferenciação. As condições de solubilização e purificação influenciaram o desempenho antigênico da proteína ESAT-6, pois, quando produzida em condição desnaturante desencadeou reações inespecíficas nos animais não sensibilizados, enquanto que aquela produzida em condições nativas e aplicada em concentrações de 6, 12, 24 e 48µg induziu reações significativas apenas nos animais sensibilizados, confirmando o seu potencial como antígeno.

  1. Viabilidad de nuevos materiales frente a materiales convencionales en la construcción de pantalanes

    OpenAIRE

    Marín Gallego, Enric

    2012-01-01

    Este proyecto estudia la viabilidad de nuevos materiales estructurales, tales como los materiales compuestos, comparándolos con materiales convencionales como el acero, el acero inoxidable o el hormigón.

  2. Carbohydrate metabolism in Bacillus subtilis

    International Nuclear Information System (INIS)

    Riedel, K.

    1980-01-01

    The glucose metabolism via the glycolytic pathway as well as via the oxidative and inoxidative hexose monophosphate pathways in Bacillus subtilis was studied applying 1- 14 C- and 6- 14 C-glucose, respectively, and determining labelled CO 2 and RNA. A method for calculating the catabolic pathways was developed. In nonproliferating cultures glucose is catabolized to 62% via the glycolytic pathway, to 20% via the oxidative, and to 18% via the inoxidative pathway

  3. Fixation of Simulated Highly Radioactive Wastes in Glassy Solids; Fixation de Dechets Simules de Haute Activite dans des Soudes Vitreux; 0424 0418 041a 0421 0410 0426 0418 042f 0418 041c 0418 0422 0418 0420 041e 0412 0410 041d 041d 042b 0425 0420 0410 0414 0418 041e 0410 041a 0422 0418 0412 041d 042b 0425 041e 0422 0425 041e 0414 041e 0412 0412 042b 0421 041e 041a 041e 0419 0410 041a 0422 0418 0412 041d 041e 0421 0422 0418 0421 0422 0415 041a 041b 041e 041e 0411 0420 0410 0417 041d 042b 041c 0418 0422 0412 0415 0420 0414 042b 041c 0418 0412 0415 0429 0415 0421 0422 0412 0410 041c 0418 ; Fijacion de Desechos Simulados de Elevada Radiactividad en Solidos Vitreos

    Energy Technology Data Exchange (ETDEWEB)

    Clark, W. E.; Godbee, H. W. [Oak Ridge National Laboratory, Oak Ridge, TN (United States)

    1963-02-15

    entre 5,07 W/cm. Degree-Sign C a 160 Degree-Sign C et 7,73 W/cm. Degree-Sign C a 565 Degree-Sign C, c'est-a-dire qu'elle est 10 fois superieure a celle de la masse calcinee sans additifs. La volatilite du ruthenium a ete maintenue a moins de 10% par addition de phosphite. Le recipient de calcination-fixation peut etre construit en acier inoxydable. Pratiquement toute la corrosion interne se produit au cours de la periode relativement breve (2 a 6 h) au cours de laquelle les derniers residus d'acier et d'eau sont chasses a la temperature maximum. La formation de verre fondu a augmente la corrosion de l'acier inoxydable 304L de 0,12 a 1,05 mm par mois, pour un cycle d'evaporation-fixation de 24 heures, dans le cas des dechets du procede TBP-25 et de 0,20 a 3,5 mm par mois dans celui des dechets Purex. Si l'on travaille a plus de 900 Degree-Sign C sur des dechets Purex en presence de fondants, une corrosion localisee extremement grave risque de se produire. (author) [Spanish] En el Oak Ridge National Laboratory se procura perfeccionar metodos para incorporar desechos de elevada radiactividad a vidrios insolubles de gran densidad, que contengan todos los componentes radiactivos en la fraccion solida. Los experimentos con desechos simulados de los procesos TBP-25 (aluminio, HNO{sub 3}), Purex y Darex (acero inoxidable, HNOj) demuestran que tales metodos son tecnicamente factibles. Los solidos densos, de estructura nucrocristalina pueden ser tan aceptables como los vidrios verdaderos; su mayor conductividad termica compensa hasta cierto punto el aumento de superficie con respecto a la de los vidrios verdaderos. Con los mencionados tipos de desechos se prepararon en el laboratorio vidrios al fosfato y al borofosfato. La volatilidad del cesio se limito al 0,1 por ciento, aproximadamente, debido al arrastre mecanico y la volatilidad del rutenio se rebajo a menos de 0,5%, agregando fosfito o hipofosfito a la mezcla. Entre los otros aditivos figuran el PbO, el Ca(OH){sub 2}, el Na

  4. Nelson Maculan Filho: cientista e educador

    Directory of Open Access Journals (Sweden)

    Ribeiro Celso Carneiro

    2003-01-01

    Full Text Available Este texto é um pequeno e merecido tributo ao Professor Nelson Maculan Filho por ocasião do seu 60masculine aniversário, em reconhecimento às suas grandes contribuições à Universidade brasileira. Como amigos, colaboradores e ex-alunos, ficamos sensibilizados e honrados com o convite feito pelo Professor Jayme Luiz Szwarcfiter para escrever este artigo. Carpe diem, querido amigo Maculan!

  5. Corrosion testing of a degraded moderator: L-Area Tuff Tanks

    International Nuclear Information System (INIS)

    Mickalonis, J.I.

    2000-01-01

    Based on test results, storage of the degraded moderator in 55-gallon 304L drums (0.065 inches thick) would not cause failure by general corrosion for up to 5 plus years storage. Acidic degraded moderator was temporarily stored in Tuff Tanks located in L-area. The moderator characteristics included a D 2 O content of 5.02--5.33%, a pH of 1.25--1.31, a conductivity of 29,300--31,200 m mhos/cm, tritium activity of 114--141 m Ci/mL, and levels of approximately 6,000 ppm for chloride and 500 ppm for chromium. The compatibility of the degraded with AISI Type 304L stainless steel (304L) was investigated in this study. Following ASTM standard practice, coupon immersion tests were conducted in both treated and untreated moderator. Treatment included the addition of either a 40 wt % NaOH solution, distilled water to serially dilute the chloride, or concentrated nitric acid to increase the nitrate concentration. Type 304L stainless steel exposed to the Tuff Tank moderator was found from these tests to: have a general corrosion rate of less than 5 mils per year (mpy) for 304L plate, which bounds that of the 304L storage drum, passivate at chloride concentrations up to 5,000 ppm for 304L sheet, resist corrosion for nitrate/chloride ratios ranging from 0.1 to 1,000, and be susceptible to crevice corrosion. Based on these test results, storage of the degraded moderator in 55-gallon 304L drums (0.065 inch thick) would not cause failure by general corrosion for up to 5+ years storage. The chloride concentration, [Cl], in the degraded moderator has been measured up to 6000 ppm. The potential or risk for aggressive localized attack of 304L increases with [Cl] concentration. A qualitative range is as follows: [Cl minus ] minus ] minus ] < 600 ppm, reasonable resistance, medium risk. The degraded moderator should be treated to reduce the chloride concentration to reduce the potential for localized corrosion and the risk for a leakage failure of the drum. A good practice would be to

  6. Assessment of industrial wastes in mortar layers deposited on stainless steel sheets of sinks Avaliação de resíduos industriais em camadas de argamassas depositadas sobre chapas de aço inoxidável de pias

    Directory of Open Access Journals (Sweden)

    E. Gemelli

    2004-12-01

    Full Text Available This work deals with the properties of alternative mortars destined to strengthen metal sheets of sinks. The performance of these mortars was compared to that of a basic mortar made of cement, sand, and water, named standard mortar (SM. One of these mortars, named alternative mortar 2 (AM2, and composed of cement, textile residue, polyurethane, polypropylene fibers and water, was developed recently to replace the current one, named alternative mortar 1 (AM1, composed of cement, sand, polystyrene, polypropylene fibers and water. These mortars were manufactured and aged in a room in atmospheric environment for 7, 14, 28, 60 and 90 days, either with or without initial drying in a furnace. After cure of 90 days the flexion strength stress of the SM, AM1 and AM2 mortars was 5.21, 3.84, and 1.42 MPa, respectively. The SM and AM1 mortars were constituted of C-S-H phases, Ca(OH2, SiO2, AFm and AFt (monossulphate/ettringite phases. The AM2 mortar presented, apart from the compounds mentioned above, CaCO3. This compound is from the textile residue that is composed essentially of CaCO3 and Ca(OH2. The reduction in flexion strength of AM1 mortar, compared to SM mortar, is caused by the polystyrene whereas the lowering mechanical strength of the AM2 is due to both polyurethane and textile residue. Even so, its mechanical strength is acceptable because the flexion strength stress required for the industrial application is 1.0 MPa.O objetivo desse trabalho foi estudar as propriedades de argamassas alternativas usadas para reforço de chapas metálicas de pias de cozinha. O desempenho dessas argamassas foi comparado com aquele de uma argamassa básica feita de cimento, areia e água, denominada argamassa padrão (SM. Uma dessas argamassas, denominada argamassa alternativa 2 (AM2, composta de cimento, resíduo, poliuretano, fibras de polipropileno e água, foi desenvolvida recentemente para substituir a atual, chamada argamassa alternativa 1 (AM1, composta de cimento, areia, poliestireno, fibras de polipropileno e água. Essas argamassas foram produzidas e envelhecidas em um quarto à temperatura atmosférica por 7, 14, 28, 60 e 90 dias com ou sem secagem inicial em estufa. Após 90 dias de cura a tensão de resistência à flexão das argamassas SM, AM1 e AM2 foi, respectivamente, de 5,21, 3,84 e 1,42 MPa. Nas argamassas SM e AM1 foram encontradas as fases C-S-H, Ca(OH2, SiO2, AFm e AFt (monossulfato/etringita. A argamassa AM2 apresentou, além das fases mencionadas acima, CaCO3. Este composto é proveniente do resíduo têxtil que é composto essencialmente de CaCO3 e Ca(OH2. A diminuição da resistência à flexão da argamassa AM1, comparada com a argamassa SM, é provocada pela presença de poliestireno enquanto que a diminuição da resistência mecânica da argamassa AM2 é devido à presença de poliuretano e resíduo têxtil. Contudo, a resistência mecânica à flexão da argamassa A2 se mantém acima do mínimo exigido pela aplicação industrial (1 MPa.

  7. Electrochemical noise transient analysis for 316 and Duplex 2205 stainless steels in NaCl and FeCl; Analisis de los transitorios de ruido electroquimico para aceros inoxidables 316 Y - DUPLEX 2205 en NaCl Y FeCl

    Energy Technology Data Exchange (ETDEWEB)

    Almeraya-Calderaon, F.; Estupinan, F.; Zambrano, P.; Martinez-Villafane, A.; Borunda, A.; Colas, R.; Gaona-Tiburcio, C.

    2012-11-01

    This work shows the results obtained from electrochemical noise measurements for different materials exhibiting pitting corrosion. The transients presented in the potential and current time, correlates with the scanning electron microscopy (SEM) surface analysis. Electrochemical measurements were made at different exposure times to obtain the correlation. The materials used were stainless steel austenitic 316 and duplex 2205, immersed in ferric chloride (FeCl3) and sodium chloride (NaCl) electrolytes. SEM analysis shows that the transients observed in the time series, really correspond to the activity of pit nucleation developed over the surface of the electrodes. (Author) 31 refs.

  8. Industrial Ultrasonic Inspection of Stainless-Steel Claddings for the EL4 Reactor; Controle Industriel par Ultrasons des Gaines en Acier Inoxydable du Reacteur EL4; Promyshlennyj kontrol' obolochechnykh trub iz nerzhaveyushchej stali reaktora dlya EL4 s pomoshch'yu ul'trazvukovogo metoda; Metodos Ultrasonicos para Control Industrial de las Vainas de Acero Inoxidable del Reactor EL4

    Energy Technology Data Exchange (ETDEWEB)

    Prot, A. C.; Foulquoer, H. E.; Peyrot, J. P. [Centre d' Etudes Nucleaires de Saclay (France)

    1965-09-15

    Improved reactor performance requires the use of accurately fabricated and carefully inspected components. One inspection relates to the quality of the cladding tubes, whose mechanical reliability is essential for economic reactor operation. The choice and development of a method is a difficult matter and the authors explain the main factors involved. Once the choice has been made and the method has been developed in the laboratory, two new problems arise: Adaptation to meet industrial requirements; and The need to reconcile the quality standards attainable with the manufacturing process at any given stage and the somewhat arbitrarily defined specifications for the finished product. In practice, this involves a statistical study of batches of tubes from various sources and their classification in relation to more or less strict thresholds. The number of tubes which have to be inspected is much larger than originally expected. This has led to the design of an automatic inspection device geared both to the output rates involved and to the requirements of the type of inspection adopted; the latter are generally mechanical and impose particularly careful product fabrication. These various characteristics are now embodied in a device whose capacity can already easily meet the requirements of a fuel-element production line. The potentialities of the device are closely dependent on the characteristics of the inspection equipment used, especially the performances of the electronic part of ultrasonic inspection instruments and of the transducers. This study shows that standard equipment is not very suitable and that immediate thought should be given to special instruments for this type of inspection. (author) [French] L'accroissement des performances des reacteurs necessite l'utilisation de materiaux finement elabores et soigneusement controles. L'un des aspects de ce controle est celui de la qualite des tubes de gainage utilises, dont la tenue mecanique est un facteur essentiel de rentabilite du reacteur. Il s'avere que le choix de la methode a utiliser et a mettre au point est delicat; le memoire en donne les elements essentiels. Ce choix etant fait, apres mise au point en laboratoire, deux nouveaux problemes se posent: - la transposition dans le domaine industriel; - la necessite de tenir compte de la qualite permise, a un instant determine, par les procedes de fabrication, en relation avec les normes de reception definies de maniere plus ou moins arbitraire. Ceci se traduit en fait par la necessite d'une etude statistique sur des lots de tubes de diverses provenances, et leur classement par rapport a des seuils plus ou moins severes. On verra que le nombre de tubes a controler est tres superieur a celui prevu initialement. Cela conduit a l'etude d'une machine de controle automatique, capable de satisfaire a la fois les exigences de cadence et celles propres au type de controle choisi: ces dernieres sont generalement d'ordre mecanique et necessitent une construction particulierement soignee. L'ensemble de ces considerations a conduit a concevoir une machine dont la cadence peut des maintenant couvrir sans difficulte les besoins d'une chaihe de fabrication d'elements combustibles. Les possibilites de cette machine sont etroitement liees aux caracteristiques du materiel de controle choisi, en particulier aux performances de l'electronique des appareils de controle par ultrasons et a celles des traducteurs utilises. Il resulte d'ailleurs de cette etude que le materiel standard ne repond que tres imparfaitement au probleme et que l'on doit envisager des maintenant un appareillage particulier pour ce type de controle. (author) [Spanish] Las mayores exigencias a que se someten los reactores obligan a utilizar materiales elaborados y controlados con sumo cuidado. Un aspecto de tal control se refiere a la calidad de las vainas empleadas, cuyas propiedades mecanicas ejercen una influencia decisiva sobre la rentabilidad del reactor. La eleccion del metodo a utilizar representa un proceso delicado, cuyas consideraciones fundamentales se exponen en el presente trabajo. Una vez elegido el metodo y puesto a punto en el laboratorio, surgen dos nuevos problemas: Transposicion a escala industrial. Necesidad de tener siempre presente la calidad que puede alcanzarse en la industria, en relacion con normas de aceptacion definidas de manera mas o menos arbitraria. En la practica, ello obliga a realizar un estudio estadistico sobre partidas de tubos de diversos origenes y clasificarlos teniendo en cuenta umbrales de aceptacion de distintos grados de severidad. Como se ve en el trabajo, el numero de tubos a controlar es muy superior al previsto inicialmente. Este hecho indujo a estudiar una maquina de control automatico, capaz de satisfacer al mismo tiempo las exigencias de la cantidad y las propias del tipo de control seleccionado; estas ultimas son por lo general de orden mecanico y requieren una construccion especialmente esmerada. El conjunto de estas consideraciones llevo a concebir una maquina capaz de satisfacer sin dificultad las necesidades de una cadena de fabricacion'de elementos combustibles. Las posibilidades de esta maquina estan estrechamente ligadas a las caracteristicas del material descontrol escogido, sobre todo al rendimiento de los circuitos electronicos correspondientes a los aparatos de control por metodos ultrasonicos y al de los transductores utilizados. Se deduce del presente estudio, por otra parte, que el material corriente no responde al problema sino de manera muy imperfecta, y que se debe encarar desde ya el proyecto de un aparato especial para este tipo de control. (author) [Russian] Uluchshenie rabochih harakteristik reaktorov trebuet primenenija tshhatel'no razrabotannyh i strogo kontroliruemyh materialov. Odnim iz aspektov jetogo kontrolja javljaetsja kachestvo ispol'zuemyh pokrytij dlja trub, mehanicheskoe sostojanie kotoryh predstavljaet soboj sushhestvennyj faktor rentabel'nosti reaktorov. Podtverzhdaetsja, chto vybor metoda, kotoryj sleduet primenjat' i razrabatyvat', javljaetsja trudnym. Privodjatsja osnovnye momenty. Posle togo, kak v rezul'tate laboratornyh rabot sdelan vybor, voznikajut dve novye problemy: D) vnedrenie v promyshlennost' neobhodimost' ucheta dopustimogo kachestva v opredelennyj moment metodami izgotovlenija v svjazi s ustanovlennymi bolee ili menee proizvol'nym obrazom normami dlja priema. Jeto, v dejstvitel'nosti, obuslavlivaetsja neobhodimost'ju v statisticheskom issledovanii komplektov trub razlichnogo izgotovlenija i ih klassifikacii po otnosheniju k bolee ili menee strogim normam. Vidno, chto kolichestvo podlezhashhih kontrolju trub znachitel'no prevyshaet pervonachal'no namechennoe. Jeto vedet k izucheniju avtomaticheskogo kontrol'nogo mehanizma, sposobnogo udovletvorit' odnovremenno i trebovanijam tempa, i trebovanijam, vytekajushhim iz vybrannogo tipa kontrolja: poslednie obychno svodjatsja k mehanicheskomu kontrolju i nuzhdajutsja v osobenno tshhatel'no razrabotannoj konstrukcii. Sovokupnost' jetih soobrazhenij privela k razrabotke ustrojstva, temp raboty kotorogo uzhe sejchas mozhet bez truda pokryt' potrebnosti vsego cikla proizvodstva toplivnyh jelementov. Vozmozhnosti jetogo ustrojstva tesno svjazany s harakteristikami podobrannogo oborudovanija navedenija i kontrolja, v osobennosti so svojstvami jelektroniki priborov kontrolja po ul'trazvuku i so svojstvami ispol'zuemyh preobrazovatelej. K tomu zhe iz jetogo issledovanija javstvuet, chto standartnoe oborudovanie daleko ne sootvetstvuet probleme i chto uzhe sejchas sleduet predusmotret' osoboe ustrojstvo dlja dannogo tipa kontrolja. (author)

  9. A mathematical approach based on finite differences method for analyzing the temperature field in arc welding of stainless steel thin sheets; Desarrollo de un modelo matematico de diferencias finitas para el analisis del campo de temperaturas en la soldadura por arco de chapas finas de acero inoxidable

    Energy Technology Data Exchange (ETDEWEB)

    Martinez-Conesa, E.J.; Estrems, M.; Miguel, V.

    2010-07-01

    This work develops a finite difference method to evaluate the temperature field in the heat affected zone in butt welding applied to AISI 304 stainless steel thin sheet by GTAW process. A computer program has been developed and implemented by Visual Basic for Applications (VBA) in MS-Excel spreadsheet. The results that are obtained using the numerical application foresee the thermal behaviour of arc welding processes. An experimental methodology has been developed to validate the mathematical model that allows to measure the temperature in several points close to the weld bead. The methodology is applied to a stainless steel sheet with a thickness lower than 3 mm, although may be used for other steels and welding processes as MIG/MAG and SMAW. The data which has been obtained from the experimental procedure have been used to validate the results that have been calculated by the finite differences numerical method. The mathematical model adjustment has been carried out taking into account the experimental results. The differences found between the experimental and theoretical approaches are due to the convection and radiation heat losses, which have not been considered in the simulation model.With this simple model, the designer will be able to calculate the thermal cycles that take place in the process as well as to predict the temperature field in the proximity of the weld bead. (Author). 18 refs.

  10. Modificações na angulação coronária após implante de suporte vascular bioabsorvível e de stents de cromo-cobalto e aço inoxidável

    OpenAIRE

    Silva, Mateus Veloso e; Costa Jr., J. Ribamar; Abizaid, Alexandre; Staico, Rodolfo; Taiguara, Danillo; Borghi Jr., Tarcísio Campostrini; Costa, Ricardo; Chamié, Daniel; Sousa, Amanda G. M. R.; Sousa, J. Eduardo

    2013-01-01

    INTRODUÇÃO: A conformabilidade do stent, definida como a adaptação da prótese à forma natural do vaso, é a principal responsável pelas alterações geométricas produzidas após o implante do dispositivo, sendo influenciada pelo material e pelo desenho do stent. Ela pode ser aferida medindo-se as modificações da curvatura e a angulação do segmento tratado após o implante do stent. O objetivo deste estudo foi comparar as mudanças na angulação coronária após implante do suporte vascular bioabsorvív...

  11. Nitretação por plasma em baixa temperatura dos aços inoxidáveis martensíticos : estudo da influência da composição química do aço na cinética de tratamento

    OpenAIRE

    Ferreira, Lauro Mariano

    2015-01-01

    Orientador: Prof. Dr. Rodrigo Perito Cardoso Co-orientador: Prof. Dr. Silvio Francisco Brunatto Dissertação (mestrado) - Universidade Federal do Paraná, Setor de Tecnologia, Programa de Pós-Graduação em Engenharia e Ciência dos Materiais - PIPE. Defesa: Curitiba, 13/04/2015 Inclui referências : f. 86-90 Área de concentração: Engenharia e ciência de materiais Resumo: A crescente aplicação dos tratamentos termoquímicos assistidos por plasma no âmbito industrial motivou o desenvol...

  12. Susceptibility to stress corrosion in stainless steels type AISI 321 and 12X18H10T used in PWR type reactors (WWER); Susceptibilidad a la corrosion bajo esfuerzo de barras de acero inoxidable AISI 321 y 12X18H10T en ambientes utilizados en reactores VVER

    Energy Technology Data Exchange (ETDEWEB)

    Matadamas C, N

    1996-12-31

    Titanium stabilized stainless steels have been utilized in sovietic pressurized water reactors (VVER) for avoid the susceptibility to Intergranular Corrosion (IGC) present in other austenitic stainless steels. However the Intergranular Corrosion resistance of this kind of materials has been questioned because of Intergranular Stress Corrosion Cracking failures (IGSCC) have been reported. This paper study the electrochemical behavior of the AISI 321 stainless steel in a H{sub 3}BO{sub 3} Solution contaminated with chlorides and its susceptibility to Intergranular Corrosion.Electrochemical prediction diagrams of the stainless steels AISI 321 and 12X18H10T (sovietic) sensitized (600 Centigrade, 3 h.) were compared. Cylindrical and conical samples were used in Slow Strain Rate Tests (SSRT), to determine the susceptibility to Stress Corrosion Cracking (SCC) in AISI 321 and 12X18H10T stainless steels. The results obtained showed that the temperature of the solution is a very important factor to detect this susceptibility. Fractography studies on the fracture surfaces of the samples obtained in the SSRT at high temperature were realized. Corrosion velocities of both AISI 321 and 12X18H10T stainless steels were determined using conical samples in the CERT system at high temperature. E.D.A.X. analysis was employed in both AISI 321 and 12X18H10T stainless steels in order to explain the degree of sensitization. (Author).

  13. Friction and bending forces evaluation of AISI 304 DDQ steel sheet forming by bending tests under deep-drawing multiaxial stresses; Evaluacion de la fuerza de doblado y de friccion en el conformado de chapa de acero inoxidable AISI 304 DDQ mediante ensayos de doblado en condiciones multiaxiales de embuticion

    Energy Technology Data Exchange (ETDEWEB)

    Coello, J.; Miguel, V.; Ferrer, C.; Calatayud, A.; Martinez, A.

    2012-11-01

    Die radius is a critical area from the viewpoint of friction in forming processes. Moreover the sheet, that has been previously deformed in flange area, suffers bending and unbending stresses. Then, die-sheet contact in die radius must be especially considered in order to guarantee the suitable lubrication conditions. In the present work, a test method is carried out for evaluating an AISI 304 DDQ steel under similar conditions to those existing in the die radius area and that, usually, are not really reproduced in traditional bending under tensions tests. Deformation under pure shear condition, the bending and the radius angle have been established as variables of the tests. Results allow to obtain the apparent pressure sheet-bending tool, that increases with bending angle and decreases with tool radius. This last variable is the most significant while the bending angle has lesser influence. Although experimental results present some concordances with values obtained by analytical methods, some corrections must be considered in them in order to improve the theoretical values. (Author) 18 refs.

  14. Evaluation of structural behaviour and corrosion resistant of austenitic AISI 304 and duplex AISI 2304 stainless steel reinforcements embedded in ordinary Portland cement mortars; Evaluacion del comportamiento estructural y de resistencia a la corrosion de armaduras de acero inoxidable austenitico AISI 304 y duplex AISI 2304 embebidas en morteros de cemento Portland

    Energy Technology Data Exchange (ETDEWEB)

    Medina, E.; Cobo, A.; Bastidas, D. M.

    2012-07-01

    The mechanical and structural behaviour of two stainless steels reinforcements, with grades austenitic EN 1.4301 (AISI 304) and duplex EN 1.4362 (AISI 2304) have been studied, and compared with the conventional carbon steel B500SD rebar. The study was conducted at three levels: at rebar level, at section level and at structural element level. The different mechanical properties of stainless steel directly influence the behaviour at section level and structural element level. The study of the corrosion behaviour of the two stainless steels has been performed by electrochemical measurements, monitoring the corrosion potential and the lineal polarization resistance (LPR), of reinforcements embedded in ordinary Portland cement (OPC) mortar specimens contaminated with different amount of chloride over one year time exposure. Both stainless steels specimens embedded in OPC mortar remain in the passive state for all the chloride concentration range studied after one year exposure. (Author) 26 refs.

  15. Solubility of Oxygen in Liquid Sodium and the Interpretation of Predictions for the Corrosion Rate of Stainless Steels in Liquid Sodium; Solubilidad del oxigeno en sodio liquido e interpretacion de predicciones de la velocidad de corrosion de los aceros inoxidables en sodio liquido

    Energy Technology Data Exchange (ETDEWEB)

    Claxton, K T

    1979-07-01

    A statistical analysis of all oxygen in sodium solubility data has been made. The results indicate a real difference. between levels of oxygen reported by UK und US workers. Analysis using sub-sets of culled data to derive a compromise solubility function are considered less than adequate. It is considered preferable and more realistic to distinguish data sub-sets by the analytical technique employed. The vacuum distillation method yields results differing amongst them selves by up to a factor of five at cold trap temperatures of relevance to fast reactor operation. The vanadium wire and electrochemical cell techniques give the lowest solubility values. (Author) 51 refs.

  16. Spring back evaluation by bending under tension tests in conditions of multiaxial stresses corresponding to deep drawing processes. Application to AISI 304 DDQ stainless steel sheet; Evaluacion del springback mediante ensayos de doblado bajo tension en condiciones de multiaxialidad tipicas de los procesos de embuticion profunda. Aplicacion a chapa de acero inoxidable AISI 304 DDQ

    Energy Technology Data Exchange (ETDEWEB)

    Miguel, V.; Coello, J.; Martinez, A.; Calatayud, A.

    2013-09-01

    In this paper, a methodology has been developed for evaluating the spring back of AISI 304 DDQ stainless steel sheet based on a bending under tension test. The main difference of the methodology herein carried out is that tests are made under the multiaxial stresses state that take place in deep drawing processes. This affects to the level of stress value in the test and to the hardening state of the sheet. Springback evaluation has been done in two different areas. Bending area has been evaluated from elastic recovery ratio defined as the ratio between the bending radius after and before bending. Bending and unbending extreme has been studied from the measured curvature radius in this area and taking into account the geometric equivalence of the test with the drawing cups process. Results found allow to state that drawing ratio or deformation ratio have a negligible influence on the springback into the range of values experimented here. Bending radius has hardly influence as well while bending angle is the most significant variable. The results obtained are compared to those measured in deep-drawn cups, finding a great agreement. (Author)

  17. Creep-rupture-test on the stainless steel X6crni1811 (Din 1.494.8) in the frame of the Extrapolation-Program. (Part III); Ensayos de fluencia lenta en el acero inoxidable X6 Cr Ni 1811 (1.4948) en el marco del Programa Extrapolacion

    Energy Technology Data Exchange (ETDEWEB)

    Solano, R; Schirra, M; Rivas, M de la; Barroso, S; Seith, B

    1982-07-01

    The austenitic stainless steel X6crni1811 (Din 1.4948) used as a structure material for the German Fast Breeder Reactor SNR 300 was creep tested in a temperature range of 550-650 degree centigree material condition as well as welded material condition. The main point of this program (Extrapolation-Program) lies in the knowledge of the creep-rupture-strength and creep-behaviour up to 3 x 10{sup 4} hours higher temperatures in order to extrapolated up to {>=}10{sup 5} hours for operating temperatures. In order to study the stress dependency of the minimum creep rate additional tests were carried out of 550 degree centigree - 750 degree centigree. The present report describes the state in the running program with test-times of 23.000 hours and results from tests up to 55.000 hours belonging to other parallel programs are taken into account. Besides the creep-rupture behaviour it is also made a study of ductility between 550 and 750 degree centigree. Extensive metallographic examinations have been made to study the fracture behaviour and changes in structure. (Author)

  18. Proposed Testing to Assess the Accuracy of Glass-To-Metal Seal Stress Analyses.

    Energy Technology Data Exchange (ETDEWEB)

    Chambers, Robert S.; Emery, John M; Tandon, Rajan; Antoun, Bonnie R.; Stavig, Mark E.; Newton, Clay S.; Gibson, Cory S; Bencoe, Denise N.

    2014-09-01

    The material characterization tests conducted on 304L VAR stainless steel and Schott 8061 glass have provided higher fidelity data for calibration of material models used in Glass - T o - Metal (GTM) seal analyses. Specifically, a Thermo - Multi - Linear Elastic Plastic ( thermo - MLEP) material model has be en defined for S S304L and the Simplified Potential Energy Clock nonlinear visc oelastic model has been calibrated for the S8061 glass. To assess the accuracy of finite element stress analyses of GTM seals, a suite of tests are proposed to provide data for comparison to mo del predictions.

  19. Outgassing rates before, during and after bake-out for various vacuum and first wall candidate materials of a large tokamak device

    International Nuclear Information System (INIS)

    Yoshikawa, H.; Gomay, J.; Sugiyama, Y.; Mizuno, M.; Komiya, S.; Tazima, T.

    1977-01-01

    Outgassing rates of vacuum wall candidate materials; stainless steel SS-304L and YUS-170, Inconel-625 and Hastelloy-X, and first wall materials; molybdenum, pyrolytic graphite and silicon carbide are measured before, during and after a bake-out at 500 0 C. The outgassing rate from the inside wall of the cylinder made of each material is estimated from the pressure difference between before and after a calibrated orifice. The ultimate outgassing rates of SS-304L and pyrolytic graphite, and YUS-170 Inconel-625, Hastelloy-X and molybdenum are the orders of 10 -10 and 10 -11 Pa.l.s -1 cm -2 , respectively

  20. Decomposition kinetics of expanded austenite with high nitrogen contents

    DEFF Research Database (Denmark)

    Christiansen, Thomas; Somers, Marcel A. J.

    2006-01-01

    This paper addresses the decomposition kinetics of synthesized homogeneous expanded austenite formed by gaseous nitriding of stainless steel AISI 304L and AISI 316L with nitrogen contents up to 38 at.% nitrogen. Isochronal annealing experiments were carried out in both inert (N2) and reducing (H2......) atmospheres. Differential thermal analysis (DTA) and thermogravimetry were applied for identification of the decomposition reactions and X-ray diffraction analysis was applied for phase analysis. CrN precipitated upon annealing; the activation energies are 187 kJ/mol and 128 kJ/mol for AISI 316L and AISI 304L...

  1. Chemistry research and development. Progress report, July 1977--May 1978

    International Nuclear Information System (INIS)

    Miner, F.J.

    1979-01-01

    Studies were continued to determine the compatibility of non-nuclear weapons metals with various production processing materials. The corrosion resistance of 304L stainless steel in mixed acid environment was tested. Intergranular corrosion tests were performed on welded 21-6-9 and 304L stainless steels. A laboratory scale fast fluidized bed incineration system was installed and operating techniques developed. A new uranium chip burning process is being developed. Component development, pilot plant development, and instrumentation and statistical systems development are briefly discussed

  2. EFICACIA DE LA PREPARACIÓN BIOMECÁNICA DE CONDUCTOS RADICULARES EN EL CRECIMIENTO MICROBIOLÓGICO EN PIEZAS DENTARIAS ANTERIORES CON NECROSIS PULPAR EN PACIENTES DE LA CLÍNICA ODONTOLÓGICA UANCV. JULIACA, PUNO. 2013

    OpenAIRE

    TAPIA CONDORI, RILDO PAÚL

    2015-01-01

    RESULTADOS TABLAS DE INFORMACIÓN GENERAL TABLAS QUE RESPONDEN A LOS OBJETIVOS MICROBIOLOGÍA ENDODÓNTICA VÍAS MICROBIANAS DE ACCESO TÚBULOS DENTINARIOS CAVIDAD ABIERTA MEMBRANA PERIODONTAL REQUERIMIENTOS PARA UN PATÓGENO ENDODÓNTICO POTENCIAL DE OXIDO-REDUCCIÓN ANTAGÓNICOS INTERMICROBIANOS NECROSIS PULPAR TIPOS DE NECROSIS PREPARACIÓN BIOMECÁNICA EN PIEZAS CON NECROSIS PULPAR INSTRUMENTOS CONVENCIONALES DE ACERO INOXIDABLE CARACTERÍSTICAS DE LAS LIMAS K DE ACERO INOXIDABLE PROPIEDADES FÍSICAS ...

  3. Relationship between mechanical and surface properties of a stainless steels duplex UNS S31803 (45N) nitriding at high temperature

    OpenAIRE

    Mesa Grajales, Dairo Hernán; Garzón Ospina, Carlos Mario; Tschiptschin, André Paulo

    2008-01-01

    Se estudió la relación entre dureza, resistencia a la cavitación (en sus primeras etapas), y la textura cristalográfica de un acero inoxidable duplex (UNS S31803 llamado de 45N), transformado en inoxidable austenítico por tratamiento térmoquímico de nitruración gaseosa a alta temperatura. Usando la técnica de difracción de electrones retroproyectados (Electron Backscattering Diffraction - EBSD), fue posible generar un patrón de textura del material (mapa EBSD), el cual se utilizó pa...

  4. Investigation of hot cracking in deep penetration electron beam welds

    Energy Technology Data Exchange (ETDEWEB)

    Thorvaldson, W.G.

    1978-06-10

    A defect in a deep penetration electron beam weld of 304L stainless steel to 21-6-9 stainless steel has been identified as a centerline hot crack. The study discussed in this report was made to define and to eliminate the cause of cracking.

  5. Author Details

    African Journals Online (AJOL)

    Boudebane, S. Vol 18 (2008) - Articles Influence de la fatigue thermique et des chocs thermiques sur la tenue au frottement et à l'usure d'un revêtement en acier inoxydable austénitique 304L Abstract PDF. ISSN: 2352-9717. AJOL African Journals Online. HOW TO USE AJOL... for Researchers · for Librarians · for Authors ...

  6. Corrosion Of Stainless Steel With A Laser Bar Code In A Saline Solution

    OpenAIRE

    Domingues S.R.; Proenca M.B.; Ierardi M.C.F.; Freire C.M.A.

    1996-01-01

    The corrosion of stainless steel AISI 304 L plates marked by laser beam fusion is studied. The electrochemical experiments are carried out in 3.5% NaCl water solution. Electrochemical curves are obtained by potentiodynamic method. Sample surfaces are also examined by scanning electron microscopy. The changes of corrosion resistance after laser treatment are insignificant.

  7. In-reactor precipitation and ferritic transformation in neutron-irradiated stainless steels

    International Nuclear Information System (INIS)

    Porter, D.L.; Wood, E.L.

    1979-01-01

    Ferritic transformation (γ→α) was observed in type 304L, 20% cold-worked AISI 316, and solution-annealed AISI 316 stainless steels when subjected to fast neutron irradiation. Each material demonstrated an increasing propensity for transformation with increasing irradiation temperature between 40 and 550 0 C. Irradiation-induced segregation of Ni solute to precipitates was found not to be a controlling factor in the transformation kinetics in 304L. Similar composition data from 316 materials demonstrates a much greater dependence of matrix Ni depletion by precipitation reactions during neutron irradiation. The 316 data establishes a strong link between such depletion and the observed γ→α transformation. Moreover, the lack of correlation between precipitate-related Ni depletion and the γ→α transformation in 304L can be related to the fact that irradiation-induced voids nucleate very quickly in 304L steel during irradiation. These voids present competing sites for Ni segregation through a defect drag mechanism, and hence Ni segregates to voids rather than to precipitates, as evidenced by observed stable γ shells around voids in areas of complete transformation. (Auth.)

  8. Application of a non-dynamometric method to the measurement of the coefficient of static friction in cold and hot water between stainless steel and two alloys of zirconium

    International Nuclear Information System (INIS)

    D'Agraives, B.C.; Toornvliet, J.

    1977-01-01

    A method is proposed to perform comparative measurements of the coefficient of friction, either in cold water (25 0 C) or in hot pressurized water (240 0 C). For the purpose, a pin-on-disc tribometer, working with no force transducer, in which the coefficient of friction μ is measured through an angle 0, and given by μ=K sin 0 is used. The method is presently applied to the determination of the incipient friction along a distance of few millimetres. At low speed (1 mm/s) and with light contacts loads (from 50 to 150 g), two different friction mechanisms are observed for the following couples of materials; Zircalloy 2/304L stainless steel, Zirconium Niobium 2.5/304L stainless steel, 304L stainless steel/304L stainless steel. The first mechanism, which is observed essentially in cold conditions, is characterized by a regular sliding since friction starts, whereas the second appears mostly in hot conditions and shows peaks of friction with irregular and scattered values of μ. These two mechanisms seem to be related to intermetallic affinity of the mating materials, and also to the existence of preoxydized surface layers, and, to a large extent, to the change in the water viscosity. In such conditions, it appears that it is not possible to replace friction experiments in hot water by easier experiments in cold water

  9. Cooper coatings on stainless steel by laser cladding

    International Nuclear Information System (INIS)

    Reis, M.; Estanislau, S.; Cabral, A.; Pecas, P.; Gouveia, H.

    1998-01-01

    Copper laser cladding was performed on AISI 304L stainless steel. Some process parameters like process speed and focal point were analysed and it was established its influence on the quality of the coating. Simple track coating were achieved with good aspect, good adherence and good surface finishing. Therefore a reference basis for further developments related to industrial application, was created. (Author) 14 refs

  10. Containment of Nitric Acid Solutions of Plutonium-238

    International Nuclear Information System (INIS)

    Reimus, M.A.H.; Silver, G.L.; Pansoy-Hjelvik, L.; Ramsey, K.

    1999-01-01

    The corrosion of various metals that could be used to contain nitric acid solutions of Pu-238 has been studied. Tantalum and tantalum/2.5% tungsten resisted the test solvent better than 304L stainless steel and several INCONEL alloys. The solvent used to imitate nitric acid solutions of Pu-238 contained 70% nitric acid, hydrofluoric acid, and ammonium hexanitratocerate

  11. In-reactor precipitation and ferritic transformation in neutron--irradiated stainless steels

    International Nuclear Information System (INIS)

    Porter, D.L.; Wood, E.L.

    1978-01-01

    Ferritic transformation (γ → α) was observed in Type 304L, 20% cold-worked AISI 316, and solution-annealed AISI 316 stainless steels subjected to fast neutron irradiation. Each material demonstrated an increasing propensity for transformation with increasing irradiation temperature between 400 and 550 0 C. Irradiation-induced segregation of Ni solute to precipitates was found not to influence the transformation kinetics in 304L. Similar composition data from 316 materials demonstrates a much greater temperature dependence of precipitation reactions in the process of matrix Ni depletion during neutron irradiation. The 316 data establishes a strong link between such depletion and the observed γ → α transformation. Moreover, the lack of correlation between precipitate-related Ni depletion and the γ → α transformation in 304L can be related to the fact that irradiation-induced voids nucleate very quickly in 304L steel during irradiation. These voids present preferential sites for Ni segregation through a defect trapping mechanism, and hence Ni segregates to voids rather than to precipitates, as evidenced by observed stable γ shells around voids in areas of complete transformation

  12. A temperature dependent slip factor based thermal model for friction

    Indian Academy of Sciences (India)

    This paper proposes a new slip factor based three-dimensional thermal model to predict the temperature distribution during friction stir welding of 304L stainless steel plates. The proposed model employs temperature and radius dependent heat source to study the thermal cycle, temperature distribution, power required, the ...

  13. Improvement in reliability and accuracy of heater tube eddy current testing by integration with an appropriate destructive test

    International Nuclear Information System (INIS)

    Giovanelli, F.; Gabiccini, S.; Tarli, R.; Motta, P.

    1988-01-01

    A specially developed destructive test is described showing how the reliability and accuracy of a non-destructive technique can be improved if it is suitably accompanied by an appropriate destructive test. The experiment was carried out on samples of AISI 304L tubes from the low-pressure (LP) preheaters of a BWR 900 MW nuclear plant. (author)

  14. EXPERIMENTAL PREDICTION AND OPTIMIZATION OF MATERIAL ...

    African Journals Online (AJOL)

    It investigates the influence of machining process parameters such as cutting speed, feed rate and depth of cut on the material removal rate (output parameter) during hard turning of AISI 304L austenitic stainless steel (0.03 wt. % C (max)). A total of 27 experiments were conducted using a MORISEIKI SL-253B CNC machine ...

  15. Irradiation effects on reactor structural materials. Semiannual progress report, March 1975--July 1975

    International Nuclear Information System (INIS)

    Claudson, T.T.

    1975-12-01

    Mechanical properties and irradiation effects are reported by Aerojet, ANL, AI, GE, HEDL, NRL, ORNL, PNL, and Univ. of Cincinnati for: Type 304, 304L, and 316 stainless steels; Inconel 718; nickel; Ni alloys; V alloys; Mo; Nb; and Nb--1 Zr

  16. Feasibility of a novel approach for fast, economical determination of radiation damage in nuclear reactor cores

    International Nuclear Information System (INIS)

    Was, G.S.

    1993-01-01

    Progress was made in the following areas: radioinduced segregation (modeling and experiment), deformation of irradiated microstructures, stress corrosion cracking of irradiated microstructures, and development of an apparatus to determine the role of deformation on the radiation microstructure in-situ. Materials used were based on Ni-Cr-Fe and 304L

  17. The diagnostic value of 111In-oxine or 99mTc-sulphur-colloid-labelled leucocytes in patients with inflammation of bones and hip endoprothesis

    International Nuclear Information System (INIS)

    Kostadinowa, I.; Dontschev, M.; Dojtschinov, A.; Kynev, W.; Kowatschewa, S.

    1990-01-01

    Scintigraphy with leukocytes, labelled with 99m Tc sulphur colloid or 111 In-oxide, in 41 patients with suspected inflammation in endoprothetic hip joints (n=23) or infectious complications after femoral fracture (n=18) has shown to be a highly specific and useful tool in orthopaedic routine diagnosis. (orig.) [de

  18. An experience with in-service fabrication and inspection of austenitic stainless steel piping in high temperature sodium system

    Energy Technology Data Exchange (ETDEWEB)

    Ravi, S., E-mail: sravi@igcar.gov.in; Laha, K.; Sakthy, S.; Mathew, M.D.; Bhaduri, A.K.

    2015-04-01

    Highlights: • Procedure for changing 304L SS pipe to 316L SS in sodium loop has been established. • Hot leg made of 304L SS was isolated from existing cold leg made of 316LN SS. • Innovative welding was used in joining the new 316L SS pipe with existing 316LN SS. • The old components of 304L SS piping have been integrated with the new piping. - Abstract: A creep testing facility along with dynamic sodium loop was installed at Indira Gandhi Centre for Atomic Research, Kalpakkam, India to assess the creep behavior of fast reactor structural materials in flowing sodium. Type 304L austenitic stainless steel was used in the low cross section piping of hot-leg whereas 316LN austenitic stainless steel in the high cross section cold-leg of the sodium loop. The intended service life of the sodium loop was 10 years. The loop has performed successfully in the stipulated time period. To enhance its life time, it has been decided to replace the 304L piping with 316L piping in the hot-leg. There were more than 300 welding joints involved in the integration of cold-leg with the new 316L hot-leg. Continuous argon gas flow was maintained in the loop during welding to avoid contamination of sodium residue with air. Several innovative welding procedures have been adopted for joining the new hot-leg with the existing cold-leg in the presence of sodium residue adopting TIG welding technique. The joints were inspected for 100% X-ray radiography and qualified by performing tensile tests. The components used in the discarded hot-leg were retrieved, cleaned and integrated in the renovated loop. A method of cleaning component of sodium residue has been established. This paper highlights the in-service fabrication and inspection of the renovation.

  19. Utilização do subproduto da recuperação metálica de escórias de aços inoxidáveis na síntese de pigmentos cerâmicos; caracterização da matéria-prima By-product utilization of metallic recovering of stainless steel slags in the ceramic pigments synthesis; raw material characterization

    Directory of Open Access Journals (Sweden)

    V. P. Della

    2005-06-01

    Full Text Available O processo de recuperação metálica em escórias de aciaria - resíduo gerado em grande quantidade no processo de refino do ferro-gusa para obtenção do aço - que visa a recuperação de metais nobres, gera uma massa de óxidos que pode ser utilizada como fonte precursora na síntese do pigmento cerâmico verde vitória. Verde vitória é o nome dado ao pigmento cerâmico à base de cálcio, cromo e silício (Ca3Cr2Si3O12 que a elevadas temperaturas desenvolve a estrutura cristalina uvarovita responsável pela estabilização da cor verde característica. Este subproduto apresenta características constitucionais favoráveis à obtenção deste pigmento mediante o ajuste da composição química através da adição de óxidos puros. A combinação de técnicas de análise microestrutural, térmica e química foi utilizada nesta caracterização inicial.The metallic recovering process of steel industry slags - waste produced in a big amount by the process of pig iron refining for steel obtainment, which aims the recovering of noble metals, produces a oxide mass that can be used as a precursor source for the synthesis of the Victory Green ceramic pigment. Victory Green is the name of the ceramic pigment based on calcium, chromium and silicon (Ca3Cr2Si3O12 , and that develops the uvarovite crystalline structure in high temperatures, responsible for the stabilization of characteristic green color. This by-product presents favorable constitutional characteristics to the obtainment of this pigment by adjusting the chemical composition through additions of pure oxides. The combination of techniques of microstructural, thermal and chemical analysis was used in this initial characterization.

  20. Dissimilar welding in nuclear reactors: review of the main aspects related to dissimilar welding of carbon steel and stainless steel with addition of nickel alloys; Soldas dissimilares em reatores nucleares: revisão dos principais aspectos relacionados à soldagem dissimilar de aço carbono e aço inoxidável com adição de ligas de níquel

    Energy Technology Data Exchange (ETDEWEB)

    Ribeiro, Vladimir Soler

    2015-07-01

    This work presents a review of the literature about Stress Corrosion Cracking, which is one of the main damage mechanisms that affect PWR and BWR type nuclear reactor. It deals with issues related to one of the sources of the problem, which are the trative residual stress caused by the thermal cycle of welding. It also addressed measurement techniques of residual stresses, with emphasis on technique the center hole drilling. It is shown that, once found the problem, there are means to mitigate the damage, which allow prolonging the life of the component. (author)

  1. Cobre antimicrobiano contra patógenos intrahospitalarios en Perú

    Directory of Open Access Journals (Sweden)

    Edwin Neciosup

    2015-01-01

    Full Text Available Introducción: Las infecciones intrahospitalarias (IIH constituyen un problema de salud pública que generan grandes gastos por parte de los gobiernos, debido a que los patógenos causantes de IIH presentan resistencia a fármacos y generan una mayor permanencia de los pacientes, pues la infraestructura hospitalaria constituye un reservorio favorable para los patógenos. Las superficies de cobre surgen como opción sanitaria y efectiva para controlar el crecimiento y propagación de estos patógenos. Objetivos: Evaluar la actividad bactericida de las superficies de cobre contra los principales bacterias patógenas causantes de IIH (Escherichia coli, Pseudomonas aeruginosa y Staphylococcus aureus. Diseño: Estudio experimental con muestreo no probabilístico. Lugar: Hospital Regional Docente las Mercedes (HRDLM y Hospital Provincial Docente Belén (HPDB, Lambayeque, Perú. Materiales: Nueve cepas bacterianas, 3 de E. coli , 3 de P. aeruginosa y 3 de S. aureus; superficies metálicas (1 cm² de cobre y acero inoxidable (control . Intervenciones: Las 9 cepas bacterianas fueron proporcionadas por los hospitales HRDLM (4 cepas y HPDB (5 cepas. Los análisis de ANOVA y de Tukey fueron aplicados para evaluar la actividad bactericida de las superficies de cobre y acero inoxidable contra las 9 cepas causantes de IIH, usando los programas estadísticos Minitab y Sigmaplot, respectivamente. Principales medidas de resultados: Diferencias en el crecimiento bacteriano sobre superficies de cobre o acero inoxidable, con respecto al tiempo de exposición. Resultados: Las 9 cepas -3 de P. aeruginosa, 3 de E. coli y 3 de S. aureus - expuestas a superficies de cobre fueron eliminadas en 10, 15 y 60 minutos, respectivamente. La carga bacteriana de las células expuestas en superficies de acero inoxidable permaneció constante y viable por periodos mayores a 60 minutos. Además, las superficies de cobre eliminaron más rápido a las bacterias Gram negativas (P

  2. Survey of degradation modes of candidate materials for high-level radioactive-waste disposal containers

    Energy Technology Data Exchange (ETDEWEB)

    Strum, M.J.; Weiss, H.; Farmer, J.C. (Lawrence Livermore National Lab., CA (USA)); Bullen, D.B. (Science and Engineering Associates, Inc., Pleasanton, CA (USA))

    1988-06-01

    This volume surveys the effects of welding on the degradation modes of three austenitic alloys: Types 304L and 316L stainless steels and Alloy 825. These materials are candidates for the fabrication of containers for the long-term storage of high-level nuclear waste. The metallurgical characteristics of fusion welds are reviewed here and related to potential degradation modes of the containers. Three specific areas are discussed in depth: (1) decreased resistance to corrosion in the forms of preferential corrosion, sensitization, and susceptibility to stress corrosion cracking, (2) hot cracking in the heat-affected zone and the weld zone, and (3) formation of intermetallic phases. The austenitic alloys are ranked as follows in terms of overall weldability: Alloy 825 (best) > Type 316L stainless steel > Type 304L stainless steel (worst). 108 refs., 31 figs., 7 tabs.

  3. Survey of degradation modes of candidate materials for high-level radioactive-waste disposal containers

    International Nuclear Information System (INIS)

    Strum, M.J.; Weiss, H.; Farmer, J.C.; Bullen, D.B.

    1988-06-01

    This volume surveys the effects of welding on the degradation modes of three austenitic alloys: Types 304L and 316L stainless steels and Alloy 825. These materials are candidates for the fabrication of containers for the long-term storage of high-level nuclear waste. The metallurgical characteristics of fusion welds are reviewed here and related to potential degradation modes of the containers. Three specific areas are discussed in depth: (1) decreased resistance to corrosion in the forms of preferential corrosion, sensitization, and susceptibility to stress corrosion cracking, (2) hot cracking in the heat-affected zone and the weld zone, and (3) formation of intermetallic phases. The austenitic alloys are ranked as follows in terms of overall weldability: Alloy 825 (best) > Type 316L stainless steel > Type 304L stainless steel (worst). 108 refs., 31 figs., 7 tabs

  4. High temperature coatings from post processing Fe-based chips and Ni-based alloys as a solution for critical raw materials

    Science.gov (United States)

    Dudziak, T.; Olbrycht, A.; Polkowska, A.; Boron, L.; Skierski, P.; Wypych, A.; Ambroziak, A.; Krezel, A.

    2018-03-01

    Due to shortage of natural resources worldwide, it is a need to develop innovative technologies, to save natural resources and secure Critical Raw Materials (CRM). On the other hand, these new technologies should move forward materials engineering in order to develop better materials for extreme conditions. One way to develop new materials is to use post processing chips of austenitic steels (i.e. 304L stainless steel: 18/10 Cr/Ni) and other materials such as Ni-based alloy with high Cr content. In this work, the results of the preliminary study on the High Velocity Oxy Fuel (HVOF) coatings developed from 304L stainless steel chips and Haynes® 282® Ni- based alloys are shown. The study obeys development of the powder for HVOF technology. The produced coatings were exposed at high temperature at 500 and 700 °C for 100 and 300 hours respectively to assess corrosion behaviour.

  5. Evaluation of commercially available decontamination chemicals

    International Nuclear Information System (INIS)

    Shurte, E.A.; Rankin, W.N.

    1988-01-01

    The effectiveness of commercially available decontamination solutions was compared with the effectiveness of 10% oxalic acid in controlled laboratory tests. Type 304L stainless steel and Inconel 625 specimens were used. Contamination was sludge from Savannah River Plant (SRP) high level waste tanks. Measured amounts of contamination were placed on each specimen. They were then heated to bond the contamination to the surface and cleaned according to the manufacturer's directions. The effectiveness of the product was determined by monitoring specimens before and after cleaning. Four of the 16 solutions evaluated removed all the contamination from Type 304L stainless steel. Inconel 625 was more difficult to decontaminate. Further tests are planned with the chemicals that were most effective in this test. 4 refs., 6 tabs

  6. Corrosion studies on materials of construction for spent nuclear fuel reprocessing plant equipment

    International Nuclear Information System (INIS)

    Kamachi Mudali, U.; Dayal, R.K.; Gnanamoorthy, J.B.

    1993-01-01

    Corrosion studies on specimens of commercial Type 304L stainless steel (SS), nuclear grade type 304L SS, extra low-carbon nitric acid grade (NAG) Uranus-16 SS, NAG Uranus-65 SS, Ti, Ti-5% Ta, Ti-0.25% Pd, Zircaloy-2, weldments of Ti and of Ti-5% Ta, and surface-modified (thermally oxidised and anodised) Ti were carried out to assess their corrosion resistance in nitric acid medium. The results indicated that Zircaloy-2, Ti-5% Ta, Uranus-16 SS and Uranus-65 SS have excellent corrosion resistance in boiling nitric acid solution. Specimens of Zircaloy-2, Ti-5% Ta and thermally-oxidised Ti showed excellent corrosion resistance also in a simulated uranium-containing reprocessing medium in a concentrated nitric acid solution. SEM and XRD analyses were carried out on the tested specimens to examine the scale morphology and phases present on the surface. (orig.)

  7. Corrosion Study Using Electrochemical Impedance Spectroscopy

    Science.gov (United States)

    Farooq, Muhammad Umar

    2003-01-01

    Corrosion is a common phenomenon. It is the destructive result of chemical reaction between a metal or metal alloy and its environment. Stainless steel tubing is used at Kennedy Space Center for various supply lines which service the orbiter. The launch pads are also made of stainless steel. The environment at the launch site has very high chloride content due to the proximity to the Atlantic Ocean. Also, during a launch, the exhaust products in the solid rocket boosters include concentrated hydrogen chloride. The purpose of this project was to study various alloys by Electrochemical Impedance Spectroscopy in corrosive environments similar to the launch sites. This report includes data and analysis of the measurements for 304L, 254SMO and AL-6XN in primarily neutral 3.55% NaCl. One set of data for 304L in neutral 3.55%NaCl + 0.1N HCl is also included.

  8. Corrosion test plan to guide canister material selection and design for a tuff repository

    International Nuclear Information System (INIS)

    McCright, R.D.; van Konynenburg, R.A.; Ballou, L.B.

    1983-11-01

    Corrosion rates and the mode of corrosion attack form a most important basis for selection of canister materials and design of a nuclear waste package. Type 304L stainless steel was selected as the reference material for canister fabrication because of its generally excellent corrosion resistance in water, steam and air. However, 304L may be susceptible to localized and stress-assisted forms of corrosion under certain conditions. Alternative alloys are also investigated; these alloys were chosen because of their improved resistance to these forms of corrosion. The fabrication and welding processes, as well as the glass pouring operation for defense and commercial high-level wastes, may influence the susceptibility of the canister to localized and stress forms of corrosion. 12 references, 2 figures, 4 tables

  9. Corrosion of stainless steels in the condensate emitted from cooled exhaust gases

    International Nuclear Information System (INIS)

    Krol, S.

    2004-01-01

    The research of stainless steels 316L and 304L exposed to the water condensate forming in cooled exhausted gases and containing the aggressive sulfate and chloride ions was presented in this article. It was assumed, that after 200 days and nights of their exposition to the condensate significant losses of steel 316L created with speed of 1,6 mm/yearly were taking place. Such a tremendous speed of corrosion has come from a porous layer construction, containing beside magnetite and spinels also chlorides and sulfates. The presence of about 2% of molybdenum in steel due to the bonding of sulfur near the phase border with the metallic base reduced profoundly the corrosion effects; while the exposed at the same time and under the same conditions steel without molybdenum of type 304L was corroding with the speed of nearly 13 mm/yearly. (author)

  10. Correlation between Fatigue Crack Growth Behavior and Fracture Surface Roughness on Cold-Rolled Austenitic Stainless Steels in Gaseous Hydrogen

    Directory of Open Access Journals (Sweden)

    Tai-Cheng Chen

    2018-03-01

    Full Text Available Austenitic stainless steels are often considered candidate materials for use in hydrogen-containing environments because of their low hydrogen embrittlement susceptibility. In this study, the fatigue crack growth behavior of the solution-annealed and cold-rolled 301, 304L, and 310S austenitic stainless steels was characterized in 0.2 MPa gaseous hydrogen to evaluate the hydrogen-assisted fatigue crack growth and correlate the fatigue crack growth rates with the fracture feature or fracture surface roughness. Regardless of the testing conditions, higher fracture surface roughness could be obtained in a higher stress intensity factor (∆K range and for the counterpart cold-rolled specimen in hydrogen. The accelerated fatigue crack growth of 301 and 304L in hydrogen was accompanied by high fracture surface roughness and was associated with strain-induced martensitic transformation in the plastic zone ahead of the fatigue crack tip.

  11. Evaluation of commercially available decontamination chemicals

    International Nuclear Information System (INIS)

    Shurte, E.A.

    1988-01-01

    The effectiveness of commercially available decontamination solutions was compared with the effectiveness of 10% oxalic acid in controlled lab. tests. Type 304L stainless steel and Inconel 625 specimens were used. Contamination was sludge from Savannah River Plant (SRP) high level waste tanks. Measured amounts of contamination were placed on each specimen. They were then heated to bond the contamination to the surface and cleaned according to the manufacturer's directions. The effectiveness of the produce was determined by monitoring specimens before and after cleaning. Four of the 16 solutions evaluated removed all the contamination from Type 304L stainless steel. Inconel 625 was more difficult to decontaminate. Further tests are planned with the chemicals that were most effective in this test

  12. Corrosion of ferrous alloys in nitrogen contaminated liquid lithium

    International Nuclear Information System (INIS)

    Olson, D.L.; Bradley, W.L.

    1976-01-01

    Liquid lithium penetration of 304L stainless steel and Armco iron grain boundaries has been studied. The penetration kinetics for the 304L stainless steel was found to be diffusion controlled. The measured temperature dependent delay time has been associated with the initial formation of the corrosion product at the grain boundary. Nitrogen in the stainless steel or the liquid lithium has been found to accelerate the rate of attack without changing the apparent activation energy. Grain boundary grooving of Armco iron in liquid lithium indicates that the controlling mass transport is also through a corrosion product present as a surface film. Stresses as small as 12 MPa have been found to give rise to a fifty-fold increase in the rate of penetration of Armco iron by liquid lithium

  13. Utensílios para alimentos e implicações nutricionais

    Directory of Open Access Journals (Sweden)

    QUINTAES Késia Diego

    2000-01-01

    Full Text Available Há grande variedade de materiais empregados na confecção de utensílios para os alimentos: barro, ferro, vidro, cerâmica, inox, pedra, alumínio e outros. Cerca de 43% de panelas vendidas atualmente nos Estados Unidos são de aço inoxidável. Outra parcela da população utiliza utensílios de alumínio. Este artigo visa especular a contribuição nutricional de utensílios usados na preparação de alimentos e feitos de três diferentes materiais (alumínio, ferro e aço inoxidável, através de revisão de literatura científica.

  14. Safety analysis report on the ''Paducah Tiger'' protective overpack for 10-ton cylinders of uranium hexafluoride. Supplement 1

    International Nuclear Information System (INIS)

    Stitt, D.H.

    1977-01-01

    This supplement details design changes made to the ''Paducah Tiger'' since the issue date of the SAR, June 16, 1976. A 3 / 8 -inch thick, 304L stainless steel plate has been added on the valve end of existing and future overpacks to provide increased puncture resistance and the overpack cavity has been modified to preclude incorrect loading of the type 48X cylinder. Temperature profiles of the ''Paducah Tiger'' during the 30-minute fire test are included

  15. Reduction of Friction of Metals Using Laser-Induced Periodic Surface Nanostructures

    OpenAIRE

    Zhuo Wang; Quanzhong Zhao; Chengwei Wang

    2015-01-01

    We report on the effect of femtosecond-laser-induced periodic surface structures (LIPSS) on the tribological properties of stainless steel. Uniform periodic nanostructures were produced on AISI 304L (American Iron and Steel Institute steel grade) steel surfaces using an 800-nm femtosecond laser. The spatial periods of LIPSS measured by field emission scanning electron microscopy ranged from 530 to 570 nm. The tribological properties of smooth and textured surfaces with periodic nanostructures...

  16. Propagation of cracks by stress corrosion in conditions of BWR type reactor

    International Nuclear Information System (INIS)

    Merino C, F.J.; Fuentes C, P.

    2004-01-01

    In this work, the obtained results when applying the Hydrogen Chemistry to a test tube type Compact Tension (CT), built in austenitic stainless steel 304l, simulating the conditions to those that it operates a Boiling Water Reactor (BWR), temperature 288 C and pressure of 8 MPa are presented. With the application of this water chemistry, seeks to be proven the diminution of the crack propagation speed. (Author)

  17. Proceedings of the International Congress (12th), Corrosion Control for Low-Cost Reliability, Held in Houston, Texas on September 19 -24, 1993. Volume 3B. Corrosion: Specific Issues

    Science.gov (United States)

    1993-09-24

    de Quimica Pura y Aplicada, Monterrey N.L., 1990. No. 47. 3.- 8. Valdez, G. Guerra, J. Sampedro, N. Rosas. CORROSION, Vol. 2, No. 3, 1991, pp. 11-15...AISI 304L AND 316L STAINLESS STEELS PREPARED BY POWDER METALLURGY. E. Otero Departamento de Ciencia de Materiales Facultad de Ciencias Quimicas ...Madrid, Spain. V. Utrilla Departamento de Ciencia de Materiales Facultad de Ciencias Quimicas Universidad Complutense 28040-Madrid, Spain. E. Sfienz

  18. Stress corrosion cracking of candidate materials for nuclear waste containers

    International Nuclear Information System (INIS)

    Maiya, P.S.; Shack, W.J.; Kassner, T.F.

    1989-09-01

    Types 304L and 316L stainless steel (SS), Incoloy 825, Cu, Cu-30%Ni, and Cu-7%Al have been selected as candidate materials for the containment of high-level nuclear waste at the proposed Yucca Mountain Site in Nevada. The susceptibility of these materials to stress corrosion cracking has been investigated by slow-strain-rate tests (SSRTs) in water which simulates that from well J-13 (J-13 water) and is representative of the groundwater present at the Yucca Mountain site. The SSRTs were performed on specimens exposed to simulated J-13 water at 93 degree C and at a strain rate 10 -7 s -1 under crevice conditions and at a strain rate of 10 -8 s -1 under both crevice and noncrevice conditions. All the tests were interrupted after nominal elongation strains of 1--4%. Examination by scanning electron microscopy showed some crack initiation in virtually all specimens. Optical microscopy of metallographically prepared transverse sections of Type 304L SS suggests that the crack depths are small (<10 μm). Preliminary results suggest that a lower strain rate increases the severity of cracking of Types 304L and 316L SS, Incoloy 825, and Cu but has virtually no effect on Cu-30%Ni and Cu-7%Al. Differences in susceptibility to cracking were evaluated in terms of a stress ratio, which is defined as the ratio of the increase in stress after local yielding in the environment to the corresponding stress increase in an identical test in air, both computed at the same strain. On the basis of this stress ratio, the ranking of materials in order of increasing resistance to cracking is: Types 304L SS < 316L SS < Incoloy 825 congruent Cu-30%Ni < Cu congruent Cu-7%Al. 9 refs., 12 figs., 7 tabs

  19. Reassessment of the swelling behavior of AISI 304 stainless steel

    International Nuclear Information System (INIS)

    Garner, F.A.; Porter, D.L.

    1982-03-01

    Published swelling data derived from EBR-II irradiations of AISI 304 and 304L have been reanalyzed in light of insights gained from irradiation of AISI 316 and Fe-15Cr-25Ni. The primary influence of temperature, displacement rate and compositional variations in the 300 series stainless steels lies in the duration of the transient regime of swelling and not in the steady-state or constant swelling rate regime

  20. Racheting - experimental tests and practical method of analysis

    International Nuclear Information System (INIS)

    Cousseran, P.; Lebey, J.; Moulin, D.; Roche, R.; Clement, G.

    1980-09-01

    Ratcheting is the acceleration of deformation, under controlled load, due to imposed cyclic deformations. Attention is given to the increase of creep elongation in presence of cyclic deformations, such as thermal straining. Tests on stainless steel-304L and 316L are described. The aim of this paper is to bring a contribution for the establishment of a conservative design rule, with a wide field of application and an easy mode of utilization

  1. Thermophysical properties of stainless steels

    International Nuclear Information System (INIS)

    Kim, C.S.

    1975-09-01

    Recommended values of the thermodynamic and transport properties of stainless steels Type 304L and Type 316L are given for temperatures from 300 to 3000 0 K. The properties in the solid region were obtained by extrapolating available experimental data to the melting range, while appropriate correlations were used to estimate the properties in the liquid region. The properties evaluated include the enthalpy, entropy, specific heat, vapor pressure, density, thermal expansion coefficient, thermal conductivity, thermal diffusivity, and viscosity. (9 fig, 11 tables)

  2. Characterization of Residual Stress as a Function of Friction Stir Welding Parameters in ODS Steel MA956

    Science.gov (United States)

    2013-06-01

    dispersion strengthened - Eurofer steel ,” J. Nucl. Mater., vol. 416 , pp. 2229, Sep 1, 2011. [10] H. J. K. Lemmen and K. J. Sudmeijer, I, “Laser beam...Reynolds and W. Tang, “Structure, properties, and residual stress of 304L stainless steel friction stir welds,” Scr. Mater., vol. 48, pp. 12891294...OF RESIDUAL STRESS AS A FUNCTION OF FRICTION STIR WELDING PARAMETERS IN ODS STEEL MA956 by Martin S. Bennett June 2013 Thesis Advisor

  3. Design of a pressurized water loop heated by electric resistances

    International Nuclear Information System (INIS)

    Ribeiro, S.V.G.

    1981-01-01

    A pressurized water loop design is presented. Its operating pressure is 420 psi and we seek to simulate qualitatively some thermo-hydraulic phenomena of PWR reactors. The primary circuit simulator consists basically of two elements: 1)the test section housing 16 electric resistences dissipating a total power of 100 Kw; 2)the loop built of SCH40S 304L steel piping, consisting of the pump, a heat exchanger and the pressurizer. (Author) [pt

  4. Recent Developments in Assessing Microstructure-Sensitive Early Stage Fatigue of Polycrystals (Postprint)

    Science.gov (United States)

    2014-04-01

    can strongly affect formation of fatigue cracks. El Bartali et al. [7] quantified plastic strain at the grain scale in a duplex stainless steel and mea...finite ele- ment models for 304L stainless steel using EBSD measurements ta- ken on successive slices of microstructure through the thickness. Their work...inclusions in martensitic gear steel in the context of 3D polycrystal plasticity and nonlocal FIPs. Coupled effects of inclusion fracture/debonding and

  5. Oxide Evolution in ODS Steel Resulting From Friction Stir Welding

    Science.gov (United States)

    2014-06-01

    the SZ on both the AS and RS of 304L stainless steel , from [16]. ...........................................12  Figure 7.  Past research conditions...being done on void swelling and embrittlement effects. Reduced activation ferritic/ martensitic (RAFM) steels and oxide dispersion strengthened (ODS...growth by grain boundary pinning at higher temperatures. Another type of ODS steel is 9-Cr martensitic steel , which is not considered in this research

  6. Preliminary cleaning tests on candidate materials for APS beamline and front end UHV components

    International Nuclear Information System (INIS)

    Nielsen, R.; Kuzay, T.M.

    1992-01-01

    Comparative cleaning tests have been done on four candidate materials for use in APS beamline and front-end vacuum components. These materials are 304 SS, 304L SS, OFHC copper, and Glidcop* (Cu-Al 2 O 3 )- Samples of each material were prepared and cleaned using two different methods. After cleaning, the sample surfaces were analyzed using ESCA (Electron Spectography for Chemical Analysis). Uncleaned samples were used as a reference. The cleaning methods and surface analysis results are further discussed

  7. Hot-wall corrosion testing of simulated high level nuclear waste

    International Nuclear Information System (INIS)

    Chandler, G.T.; Zapp, P.E.; Mickalonis, J.I.

    1995-01-01

    Three materials of construction for steam tubes used in the evaporation of high level radioactive waste were tested under heat flux conditions, referred to as hot-wall tests. The materials were type 304L stainless steel alloy C276, and alloy G3. Non-radioactive acidic and alkaline salt solutions containing halides and mercury simulated different high level waste solutions stored or processed at the United States Department of Energy's Savannah River Site. Alloy C276 was also tested for corrosion susceptibility under steady-state conditions. The nickel-based alloys C276 and G3 exhibited excellent corrosion resistance under the conditions studied. Alloy C276 was not susceptible to localized corrosion and had a corrosion rate of 0.01 mpy (0.25 μm/y) when exposed to acidic waste sludge and precipitate slurry at a hot-wall temperature of 150 degrees C. Type 304L was susceptible to localized corrosion under the same conditions. Alloy G3 had a corrosion rate of 0.1 mpy (2.5 μm/y) when exposed to caustic high level waste evaporator solution at a hot-wall temperature of 220 degrees C compared to 1.1 mpy (28.0 μ/y) for type 304L. Under extreme caustic conditions (45 weight percent sodium hydroxide) G3 had a corrosion rate of 0.1 mpy (2.5 μm/y) at a hot-wall temperature of 180 degrees C while type 304L had a high corrosion rate of 69.4 mpy (1.8 mm/y)

  8. Test plan for Series 3 NNWSI spent fuel leaching/dissolution tests

    International Nuclear Information System (INIS)

    Wilson, C.N.

    1986-04-01

    The Series 3 tests will differ from the Series 2 tests in that the Series 3 tests will be run at 85 0 C (J-13 water) in sealed 304 stainless steel (SS) test vessels. The current NNWSI reference spent fuel container material is 304L SS. The candidate NNWSI repository horizon is above the water table, and 95 0 C (boiling temperature at the repository elevation) is the maximum liquid water temperature expected to contact spent fuel in the repository

  9. Propagation of cracks by stress corrosion in conditions of BWR type reactor; Propagacion de grietas por corrosion bajo esfuerzo en condiciones de reactor de agua en ebullicion (BWR)

    Energy Technology Data Exchange (ETDEWEB)

    Merino C, F.J. [ININ, 52045 Estado de Mexico (Mexico); Fuentes C, P. [ITT, Metepec, Estado de Mexico (Mexico)]. E-mail: fjmc@nuclear.inin.mx

    2004-07-01

    In this work, the obtained results when applying the Hydrogen Chemistry to a test tube type Compact Tension (CT), built in austenitic stainless steel 304l, simulating the conditions to those that it operates a Boiling Water Reactor (BWR), temperature 288 C and pressure of 8 MPa are presented. With the application of this water chemistry, seeks to be proven the diminution of the crack propagation speed. (Author)

  10. Proceedings of the Conference on the Design of Experiments in Army Research, Development, and Testing (22nd) Held at Harry Diamond Laboratories, Adelphi, Maryland on 20-22 October 1976

    Science.gov (United States)

    1977-06-01

    complicated model. These models and their percentages of the total data are given in Table 1. Due to the biological and psychological differencea among...These test. have had broad based applioations in education and psychological research and to some exttnt in military testing and evaltealion of new...prediction 304 L.L boud o S t alevel of approximately 70 per cent. One can therefore be fairly confident the test will show at least 1600 reliable life. On

  11. Diseño y evaluación de un procedimiento on-line para la biorremediación de aguas radiactivas en centrales nucleares

    OpenAIRE

    Belinchón Vergara, Julio Angel

    2016-01-01

    Recientemente se ha demostrado la existencia de microorganismos en las piscinas de almacenamiento de combustible nuclear gastado en las centrales nucleares utilizando técnicas convencionales de cultivo en el laboratorio. Estudios posteriores han puesto de manifiesto que los microorganismos presentes eran capaces de colonizar las paredes de acero inoxidable de las piscinas formando biopelículas. Adicionalmente se ha observado la capacidad de estas biopelículas de retener radionúclidos, lo que ...

  12. Characterization of Friction Welded Titanium Alloy and Stainless Steel with a Novel Interlayer Geometry

    Science.gov (United States)

    Kumar, R.; Balasubramanian, M.

    The main purpose of the current research work is to identify and investigate a novel method of holding an intermediate metal and to evaluate its metallurgical and mechanical properties. Copper was used as an interlayer material for the welding of this dissimilar Ti-6Al-4V (Ti alloy) and 304L stainless steel (SS). The study shows that the input parameters and surface geometry played a very significant role in producing a good quality joints with minimum heat affected zone and metal loss. A sound weld was achieved between Ti-6Al-4V and SS304L, on the basis of the earlier experiments conducted by the authors in their laboratory, by using copper rod as intermediate metal. Box-Behnken method was used for performing a minimum number of experiments for the study. In the present study, Ti-6Al-4V alloy and SS304L were joined by a novel method of holding the interlayer and new surface geometry for the interlayer. Initially, the drop test was used for determining the quality of the fabricated joint and, subsequently, non-destructive techniques like radiography and C-scan were used. Further optical micrograph, SEM-EDS, hardness and tensile test were done for understanding the performance of the joint.

  13. Oxide layer stability in lead-bismuth at high temperature

    Science.gov (United States)

    Martín, F. J.; Soler, L.; Hernández, F.; Gómez-Briceño, D.

    2004-11-01

    Materials protection by 'in situ' oxidation has been studied in stagnant lead-bismuth, with different oxygen levels (H 2/H 2O ratios of 0.3 and 0.03), at temperatures from 535 °C to 600 °C and times from 100 to 3000 h. The materials tested were the martensitic steels F82Hmod, EM10 and T91 and the austenitic stainless steels, AISI 316L and AISI 304L. The results obtained point to the existence of an apparent threshold temperature above which corrosion occurs and the formation of a protective and stable oxide layer is not possible. This threshold temperature depends on material composition, oxygen concentration in the liquid lead-bismuth and time. The threshold temperature is higher for the austenitic steels, especially for the AISI 304L, and it increases with the oxygen concentration in the lead-bismuth. The oxide layer formed disappear with time and, after 3000 h all the materials, except AISI 304L, suffer corrosion, more severe for the martensitic steels and at the highest temperature tested.

  14. Impact Testing of Stainless Steel Materials

    International Nuclear Information System (INIS)

    R. K. Blandford; D. K. Morton; T. E. Rahl; S. D. Snow

    2005-01-01

    Stainless steels are used for the construction of numerous spent nuclear fuel or radioactive material containers that may be subjected to high strains and moderate strain rates (10 to 200 per second) during accidental drop events. Mechanical characteristics of these materials under dynamic (impact) loads in the strain rate range of concern are not well documented. The goal of the work presented in this paper was to improve understanding of moderate strain rate phenomena on these materials. Utilizing a drop-weight impact test machine and relatively large test specimens (1/2-inch thick), initial test efforts focused on the tensile behavior of specific stainless steel materials during impact loading. Impact tests of 304L and 316L stainless steel test specimens at two different strain rates, 25 per second (304L and 316L material) and 50 per second (304L material) were performed for comparison to their quasi-static tensile test properties. Elevated strain rate stress-strain curves for the two materials were determined using the impact test machine and a ''total impact energy'' approach. This approach considered the deformation energy required to strain the specimens at a given strain rate. The material data developed was then utilized in analytical simulations to validate the final elevated stress-strain curves. The procedures used during testing and the results obtained are described in this paper

  15. Ceramic/Metal Composites with Positive Temperature Dependence of Thermal Conductivity

    International Nuclear Information System (INIS)

    Li Jianhui; Yu Qi; Sun Wei; Zhang Rui; Wang Ke; Li Jingfeng; Ichigozaki, Daisuke

    2013-01-01

    Most materials show decreasing thermal conductivity with increasing temperature, but an opposite temperature dependence of thermal conductivity is required for some industrial applications. The present work was conducted with a motivation to develop composite materials with a positive temperature dependence of thermal conductivity. ZrO 2 / stainless steel powders (304L) composite, with 3% stearic acid, was prepared by normal sintering under the protecting of Ar after mixing by mechanical ball milling technique. With the 304L content increasing from 10% to 20%, the thermal conductivity values increased. For all samples, the thermal conductivity in the temperature range of room temperature to 700 °C decreased with temperature below 300 °C, and then began to increase. The increasing thermal conductivity of the composites (within the high temperature range was attributed to the difference of the thermal conductivity and thermal expansion coefficient between ZrO 2 ceramic and 304L stainless steel powders. Two simple models were also used to estimate the thermal conductivity of the composites, which were in good agreement with the experiment results.

  16. Stress corrosion cracking susceptibilities of various stainless steels in high temperature water

    International Nuclear Information System (INIS)

    Shoji, Saburo; Ohnaka, Noriyuki; Kikuchi, Eiji; Minato, Akira; Tanno, Kazuo.

    1980-01-01

    The intergranular stress corrosion cracking (IGSCC) behaviors of several austenitic stainless steels in high temperature water were evaluated using three types of SCC tests, i.e., single U-bend test in chloride containing water, uniaxial constant load and constant extension rate tests (CERT) in pure water. The steels used were SUS 304, 304L, 316, 316L, 321 and 347 and several heats of them to examine heat to heat variations. The three test methods gave the same relative ranking of the steels. The CERT is the most sensitive method to detect the relative IGSCC susceptibilities. The CERT result for relative ranking from poor to good is: SUS 304 - 0.07% C, 304 - 0.06% C, 304L - 0.028% C, 316 - 0.07% C. The IGSCC susceptibilities of SUS 304L - 0.020% C, 316L - 0.023% C, 321 and 347 were not detected. These test results suggest that the use of the low carbon, molybdenum bearing, or stabilized austenitic stainless steel is beneficial for eliminating the IGSCC problem in boiling water reactor environment. (author)

  17. Microstructure and Deformation Response of TRIP-Steel Syntactic Foams to Quasi-Static and Dynamic Compressive Loads

    Science.gov (United States)

    Ehinger, David; Weise, Jörg; Baumeister, Joachim; Funk, Alexander; Krüger, Lutz; Martin, Ulrich

    2018-01-01

    The implementation of hollow S60HS glass microspheres and Fillite 106 cenospheres in a martensitically transformable AISI 304L stainless steel matrix was realized by means of metal injection molding of feedstock with varying fractions of the filler material. The so-called TRIP-steel syntactic foams were studied with respect to their behavior under quasi-static compression and dynamic impact loading. The interplay between matrix material behavior and foam structure was discussed in relation to the findings of micro-structural investigations, electron back scatter diffraction EBSD phase analyses and magnetic measurements. During processing, the cenospheres remained relatively stable retaining their shape while the glass microspheres underwent disintegration associated with the formation of pre-cracked irregular inclusions. Consequently, the AISI 304L/Fillite 106 syntactic foams exhibited a higher compression stress level and energy absorption capability as compared to the S60HS-containing variants. The α′ -martensite kinetic of the steel matrix was significantly influenced by material composition, strain rate and arising deformation temperature. The highest ferromagnetic α′-martensite phase fraction was detected for the AISI 304L/S60HS batches and the lowest for the TRIP-steel bulk material. Quasi-adiabatic sample heating, a gradual decrease in strain rate and an enhanced degree of damage controlled the mechanical deformation response of the studied syntactic foams under dynamic impact loading. PMID:29695107

  18. Role of twinning and transformation in hydrogen embrittlement of austenitic stainless steels

    International Nuclear Information System (INIS)

    Caskey, G.R. Jr.

    1977-01-01

    Internal hydrogen embrittlement may be viewed as an extreme form of environmental embrittlement that arises following prolonged exposure to a source of hydrogen. Smooth bar tensile specimens of three stainless steels saturated with deuterium (approximately 200 mol D 2 /m 3 ) were pulled to failure in air at 200 to 400 0 K or in liquid nitrogen at 78 0 K. In Type 304L stainless steel and Tenelon ductility losses are a maximum around 200 to 273 0 K; Type 310 stainless steel is not embrittled at this hydrogen concentration. A distinct change in fracture mode accompanies hydrogen embrittlement, with fracture proceeding along coherent boundaries of pre-existing annealing twins. This fracture path is observed in Tenelon at 78 0 K even when hydrogen is absent. There is also a change in fracture appearance in specimens with no prior exposure to hydrogen if they are pulled to failure in high-pressure hydrogen. The fracture path is not identifiable, however. Magnetic response measurements and changes in the stress-strain curves show that hydrogen suppresses formation of strain-induced α'-martensite at 198 0 K in both Type 304L stainless steel and Tenelon, but there is little effect in Type 304L stainless at 273 0 K

  19. Active Waste Materials Corrosion and Decontamination Tests

    International Nuclear Information System (INIS)

    Danielson, M.J.; Elmore, M.R.; Pitman, S.G.

    2000-01-01

    Stainless steel alloys, 304L and 316L, were corrosion tested in representative radioactive samples of three actual Hanford tank waste solutions (Tanks AW-101, C-104, AN-107). Both the 304L and 316L exhibited good corrosion performance when immersed in boiling waste solutions. The maximum general corrosion rate was 0.015 mm/y (0.60 mils per year). Generally, the 304L had a slightly higher rate than the 316L. No localized attack was observed after 122 days of testing in the liquid phase, liquid/vapor phase, or vapor phase. Radioactive plate-out decontamination tests indicated that a 24-hour exposure to 1 und M HNO 3 could remove about 99% of the radioactive components in the metal film when exposed to the C-104 and AN-107 solutions. The decontamination results are less certain for the AW-101 solution, since the initial contamination readings exceeded the capacity of the meter used for this test

  20. Thoria/thoria-urania dissolution studies for reprocessing application

    International Nuclear Information System (INIS)

    Srinivas, C.; Yalmali, Vrunda; Pente, A.S.; Wattal, P.K.; Misra, S.D.

    2012-06-01

    Thoria dissolution is normally conducted in 13M nitric acid in the presence of 0.03M sodium fluoride or HF as catalyst and 0.1M aluminium nitrate for mitigation of fluoride related corrosion of SS 304L dissolver vessel. Addition of aluminium nitrate in such high concentrations has undesirable consequences in the downstream high level radioactive liquid waste vitrification process at 900-1000 degC. Besides, because of the highly corrosive nature of fluoride ion, lowering its concentration in the dissolution reaction is advantageous in reducing the corrosion of dissolver and other downstream equipments. The present work was done with twin objectives of avoiding aluminium nitrate addition and lowering the fluoride ion concentration during dissolution reaction. High temperature sintered thoria and thoria-4 weight% urania dissolution reactions were investigated in the absence of aluminium nitrate and at reduced fluoride concentrations. Corrosion rates of SS 304L zircaloy in various dissolvent mixtures were studied by weight loss method. These studies clearly showed that aluminium nitrate addition for control of fluoride related corrosion of SS 304L can be avoided when zircaloy-clad thoria/thoria-urania pellets are dissolved. Dissolved zirconium ion was observed to be as effective as aluminium ion. Moreover, dissolution could be achieved with reasonable reaction rates at reduced fluoride concentration of 0.005-0.01M instead of 0.03M by changing the method of addition of the fluoride catalyst. (author)

  1. A comparison of tensile, fracture and fatigue mechanical behaviour of structural reinforcing bars made with different steels

    Directory of Open Access Journals (Sweden)

    Rodríguez, C.

    2013-09-01

    Full Text Available The use of austenitic stainless steels as rebar is an option increasingly used in reinforced concrete structures exposed to aggressive environments and especially those that have to work in marine environments. The same is true for duplex stainless steel rebars, although nowadays they have a lower use, mainly due to the fact that their inclusion in the reinforced concrete standards was delayed 10 years compared to austenitic stainless steel ones, and consequently their in-service behavior is not as well known. A study of the mechanical properties, including fracture toughness, fatigue behaviour and corrosion resistance in saline alkaline environments of austenitic (AISI 304LN and 316LN and duplex (D2205 stainless steel reinforcing bars was performed in this work. Bars made on a high ductility carbon steel (B500SD that are normally used to reinforce concrete were also characterized and used as a comparison. Stainless steel reinforcing bars show mechanical properties at least similar but usually higher than one of the best carbon steel re-bars (B500SD, along with a significantly higher ductility and, of course, much better corrosion behaviour in saline alkaline environments.El uso de aceros inoxidables austeníticos como armaduras de refuerzo es una opción cada vez más utilizada en estructuras de hormigón armado expuestas a ambientes agresivos y especialmente en las que han de trabajar en ambientes marinos. Lo mismo cabe decir de las armaduras de acero inoxidable dúplex, si bien su uso es menor, debido sobre todo a que su inclusión en la normativa aplicable al armado de hormigón se retrasó 10 años con respecto a los inoxidables austeníticos y, consecuentemente, su comportamiento en servicio es menos conocido. En este trabajo se analiza el comportamiento mecánico, incluyendo fractura y fatiga, así como la resistencia a la corrosión en medios que simulan un hormigón contaminado de cloruros, de armaduras fabricadas tanto con

  2. Inmunidad humoral y trasplante renal posibilidades terapéuticas

    Directory of Open Access Journals (Sweden)

    P. Jacqueline Pefaur, Dra.

    2010-03-01

    Por otra parte y basado en el exitoso tratamiento del RAH, se ha planteado mejorar las expectativas de llegar a realizar un trasplante a los pacientes sensibilizados. Esto es posible conseguir aplicando protocolos de desensibilización que se basan en la utilización de las mismas drogas para tratar RAH, consiguiendo ampliar las posibilidades de trasplante. El éxito de éstas es relativo al tipo de protocolos y a la intensidad de la sensibilización. La sobrevida del injerto en esta situación es plausible en la gran mayoría de los casos, sin embargo existe riesgo de presentar rechazo agudo humoral, y más complejo aún es el hecho que la sobrevida a largo plazo de los injertos sigue siendo todavía desconocida.

  3. Prevalencia de la población de riesgo para anorexia nerviosa en el alumnado de Educación secundaria obligatoria de la provincia de Jaén. Especial atención al uso excesivo

    OpenAIRE

    Rodríguez Marín, Inmaculada; Zagalaz Sánchez, Dra. María Luisa; Martínez López, Dr. Emilio J.

    2005-01-01

    La anorexia nerviosa es un trastorno de la conducta alimentaria que en los últimos años ha sensibilizado a la opinión pública y empieza a hacerlo con la política educativa. Actualmente se reconoce y acepta la naturaleza multicausal de la anorexia nerviosa. Es por ello que la tesis doctoral realizada conexiona la psicología con la educación, y más concretamente con la Educación Física, dado el interés que la práctica de ejercicio físico para perder peso presenta entre el alumnado de educación ...

  4. Composição química e aspecto superficial do slot de braquetes metálicos Elemental composition and superficial aspect of metallic brackets slot

    Directory of Open Access Journals (Sweden)

    Tatiana Féres Assad-Loss

    2008-06-01

    Full Text Available OBJETIVO: avaliar a composição química e rugosidade do fundo do slot de 90 braquetes metálicos divididos em 9 grupos: grupo 1- aço inoxidável (Equilibrium 2 - Dentaurum; grupo 2 - titânio (Equilibrium ti - Dentaurum; grupo 3- cromo-cobalto (Topic- Dentaurum; grupo 4 - aço inoxidável (Standard -TP Orthodontics; grupo 5 - aço inoxidável (Serie light - American Orthodontics; grupo 6 - aço inoxidável (Kirium Line - Abzil Lancer; grupo 7 - aço inoxidável livre de níquel (Monobloc - Morelli; grupo 8 - aço inoxidável (Convencional- Morelli e grupo 9 - aço inoxidável livre de níquel (Monobloc Golden - Morelli. METODOLOGIA: a composição química foi analisada pela Espectroscopia de Energia Dispersiva. A avaliação qualitativa do fundo do slot foi realizada através do MEV classificada de 0 a 8, correspondente às características da superfície. RESULTADOS: composição química - grupo 1 = titânio puro; grupo 9 = recoberto por nitreto de titânio em 99,48%; grupo 3 = cromo-cobalto; grupo 8 = aço inoxidável livre de níquel. Os demais grupos são compostos de aço inoxidável. Avaliação da superfície - grupo 1 = valor 2 (superfície mais polida; grupos 2, 5 e 7 = valor 3 (aspecto de polimento; grupos 3, 8 e 9 = valor 6 (menor polimento; grupo 4 = valor 6,5 (maior rugosidade e o grupo 6 = valor 5 (características intermediárias de polimento. CONCLUSÕES: os braquetes metálicos são compostos de diferentes ligas e estão disponíveis com baixo conteúdo ou ausência de níquel. Os braquetes de titânio apresentaram polimento semelhante aos de aço inoxidável, porém os recobertos por nitreto de titânio e os de cromo-cobalto mostraram superfície mais irregular ou menos polida.AIM: To evaluate the elemental composition and the slot roughness of 90 metallic brackets divided into 9 groups: group 1 - stainless steel (Equilibrium 2 - Dentaurum; group 2 - titanium (Equilibrium ti - Dentaurum; group 3 - chromium-cobalt (Topic

  5. Contribution to the study of physico-chemical properties of surfaces modified by laser treatment. Application to the enhancement of localized corrosion resistance of stainless steels

    International Nuclear Information System (INIS)

    Pacquentin, W.

    2011-01-01

    Metallic materials are more and more used in severe conditions with particularly strong request for improving their behavior in aggressive environment and especially over long periods. The objective of this PhD work is to estimate the potentiality of a laser surface melting treatment on the improvement of the stainless steel 304L corrosion resistance, surface treatments by laser can be revisited on the basis of a recent change in the laser technology. In the frame of this work, a nano-pulsed laser fiber was chosen: it allows the treated surface to be melted for few microns in depth, followed by an ultra-fast solidification occurring with cooling rates up to 1011 K/s. The combination of these processes leads to the elimination of the surface defects, the formation (trapping) of metastable phases, the segregation of chemical elements and the growth of a new oxide layer which properties are governed by the laser parameters. To correlate these latter to the electrochemical reactivity of the surface, the influence of two laser parameters on the physico-chemical properties of the surface was studied: the laser power and the overlap of the laser impacts. To support this approach, the pitting corrosion resistance of the samples was determined by standard electrochemical tests. For specific laser parameters, the pitting potential of a 304L stainless steel was increased by more than 500 mV corresponding to an important enhancement in localized corrosion resistance in chloride environment. The interdependence of the different phenomena resulting from the laser treatment lead to a quite complex prioritization of their role on the sensibility of the 304L. However, it was demonstrated that the nature of the thermal oxide formed during the laser surface melting and the induced defects are first-order parameters for the initiation of pits. (author) [fr

  6. Self-ion emulation of high dose neutron irradiated microstructure in stainless steels

    Science.gov (United States)

    Jiao, Z.; Michalicka, J.; Was, G. S.

    2018-04-01

    Solution-annealed 304L stainless steel (SS) was irradiated to 130 dpa at 380 °C, and to 15 dpa at 500 °C and 600 °C, and cold-worked 316 SS (CW 316 SS) was irradiated to 130 dpa at 380 °C using 5 MeV Fe++/Ni++ to produce microstructures and radiation-induced segregation (RIS) for comparison with that from neutron irradiation at 320 °C to 46 dpa in the BOR60 reactor. For the 304L SS alloy, self-ion irradiation at 380 °C produced a dislocation loop microstructure that was comparable to that by neutron irradiation. No voids were observed in either the 380 °C self-ion irradiation or the neutron irradiation conditions. Irradiation at 600 °C produced the best match to radiation-induced segregation of Cr and Ni with the neutron irradiation, consistent with the prediction of a large temperature shift by Mansur's invariant relations for RIS. For the CW 316 SS alloy irradiated to 130 dpa at 380 °C, both the irradiated microstructure (dislocation loops, precipitates and voids) and RIS reasonably matched the neutron-irradiated sample. The smaller temperature shift for RIS in CW 316 SS was likely due to the high sink (dislocation) density induced by the cold work. A single self-ion irradiation condition at a dose rate ∼1000× that in reactor does not match both dislocation loops and RIS in solution-annealed 304L SS. However, a single irradiation temperature produced a reasonable match with both the dislocation/precipitate microstructure and RIS in CW 316 SS, indicating that sink density is a critical factor in determining the temperature shift for self-ion irradiations.

  7. Attenuation of shock waves in copper and stainless steel

    International Nuclear Information System (INIS)

    Harvey, W.B.

    1986-06-01

    By using shock pins, data were gathered on the trajectories of shock waves in stainless steel (SS-304L) and oxygen-free-high-conductivity copper (OFHC-Cu). Shock pressures were generated in these materials by impacting the appropriate target with thin (approx.1.5 mm) flying plates. The flying plates in these experiments were accelerated to high velocities (approx.4 km/s) by high explosives. Six experiments were conducted, three using SS-304L as the target material and three experiments using OFHC-Cu as the target material. Peak shock pressures generated in the steel experiments were approximately 109, 130, and 147 GPa and in the copper experiments, the peak shock pressures were approximately 111, 132, and 143 GPa. In each experiment, an attenuation of the shock wave by a following release wave was clearly observed. An extensive effort using two characteristic codes (described in this work) to theoretically calculate the attenuation of the shock waves was made. The efficacy of several different constitutive equations to successfully model the experiments was studied by comparing the calculated shock trajectories to the experimental data. Based on such comparisons, the conclusion can be drawn that OFHC-Cu enters a melt phase at about 130 GPa on the principal Hugoniot. There was no sign of phase changes in the stainless-steel experiments. In order to match the observed attenuation of the shock waves in the SS-304L experiments, it was necessary to include strength effects in the calculations. It was found that the values for the parameters in the strength equations were dependent on the equation of state used in the modeling of the experiments. 66 refs., 194 figs., 77 tabs

  8. Survey of degradation modes of candidate materials for high-level radioactive-waste disposal containers

    Energy Technology Data Exchange (ETDEWEB)

    Farmer, J.C.; Van Konynenburg, R.A.; McCright, R.D. (Lawrence Livermore National Lab., CA (USA)); Bullen, D.B. (Science and Engineering Associates, Inc., Pleasanton, CA (USA))

    1988-04-01

    Three iron- to nickel-based austenitic alloys (Types 304L and 316L stainless steels and Alloy 825) are being considered as candidate materials for the fabrication of high-level radioactive-waste containers. Waste will include fuel assemblies from reactors as well as high-level waste in borosilicate glass forms, and will be sent to the prospective repository at Yucca Mountain, Nevada. The decay of radionuclides in the repository will result in the generation of substantial heat and in fluences of gamma radiation. Container materials may undergo any of several modes of degradation in this environment, including atmospheric oxidation; uniform aqueous phase corrosion; pitting; crevice corrosion; sensitization and intergranular stress corrosion cracking (IGSCC); and transgranular stress corrosion cracking (TGSCC). This report is an analysis of data relevant to the pitting, crevice corrosion, and stress corrosion cracking (SCC) of the three austenitic candidate alloys. The candidates are compared in terms of their susceptibilities to these forms of corrosion. Although all three candidates have demonstrated pitting and crevice corrosion in chloride-containing environments, Alloy 825 has the greatest resistance to these types of localized corrosion (LC); such resistance is important because pits can penetrate the metal and serve as crack initiation sites. Both Types 304L and 316L stainless steels are susceptible to SCC in acidic chloride media. In contrast, SCC has not been documented in Alloy 825 under comparable conditions. Gamma radiation has been found to enhance SCC in Types 304 and 304L stainless steels, but it has no detectable effect on the resistance of Alloy 825 to SCC. Furthermore, while the effects of microbiologically induced corrosion have been observed for 300-series stainless steels, nickel-based alloys such as Alloy 825 seem to be immune to such problems. 211 refs., 49 figs., 10 tabs.

  9. Survey of degradation modes of candidate materials for high-level radioactive-waste disposal containers

    International Nuclear Information System (INIS)

    Farmer, J.C.; Van Konynenburg, R.A.; McCright, R.D.; Bullen, D.B.

    1988-04-01

    Three iron- to nickel-based austenitic alloys (Types 304L and 316L stainless steels and Alloy 825) are being considered as candidate materials for the fabrication of high-level radioactive-waste containers. Waste will include fuel assemblies from reactors as well as high-level waste in borosilicate glass forms, and will be sent to the prospective repository at Yucca Mountain, Nevada. The decay of radionuclides in the repository will result in the generation of substantial heat and in fluences of gamma radiation. Container materials may undergo any of several modes of degradation in this environment, including atmospheric oxidation; uniform aqueous phase corrosion; pitting; crevice corrosion; sensitization and intergranular stress corrosion cracking (IGSCC); and transgranular stress corrosion cracking (TGSCC). This report is an analysis of data relevant to the pitting, crevice corrosion, and stress corrosion cracking (SCC) of the three austenitic candidate alloys. The candidates are compared in terms of their susceptibilities to these forms of corrosion. Although all three candidates have demonstrated pitting and crevice corrosion in chloride-containing environments, Alloy 825 has the greatest resistance to these types of localized corrosion (LC); such resistance is important because pits can penetrate the metal and serve as crack initiation sites. Both Types 304L and 316L stainless steels are susceptible to SCC in acidic chloride media. In contrast, SCC has not been documented in Alloy 825 under comparable conditions. Gamma radiation has been found to enhance SCC in Types 304 and 304L stainless steels, but it has no detectable effect on the resistance of Alloy 825 to SCC. Furthermore, while the effects of microbiologically induced corrosion have been observed for 300-series stainless steels, nickel-based alloys such as Alloy 825 seem to be immune to such problems. 211 refs., 49 figs., 10 tabs

  10. Attenuation of shock waves in copper and stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Harvey, W.B.

    1986-06-01

    By using shock pins, data were gathered on the trajectories of shock waves in stainless steel (SS-304L) and oxygen-free-high-conductivity copper (OFHC-Cu). Shock pressures were generated in these materials by impacting the appropriate target with thin (approx.1.5 mm) flying plates. The flying plates in these experiments were accelerated to high velocities (approx.4 km/s) by high explosives. Six experiments were conducted, three using SS-304L as the target material and three experiments using OFHC-Cu as the target material. Peak shock pressures generated in the steel experiments were approximately 109, 130, and 147 GPa and in the copper experiments, the peak shock pressures were approximately 111, 132, and 143 GPa. In each experiment, an attenuation of the shock wave by a following release wave was clearly observed. An extensive effort using two characteristic codes (described in this work) to theoretically calculate the attenuation of the shock waves was made. The efficacy of several different constitutive equations to successfully model the experiments was studied by comparing the calculated shock trajectories to the experimental data. Based on such comparisons, the conclusion can be drawn that OFHC-Cu enters a melt phase at about 130 GPa on the principal Hugoniot. There was no sign of phase changes in the stainless-steel experiments. In order to match the observed attenuation of the shock waves in the SS-304L experiments, it was necessary to include strength effects in the calculations. It was found that the values for the parameters in the strength equations were dependent on the equation of state used in the modeling of the experiments. 66 refs., 194 figs., 77 tabs.

  11. Compatibility testing of vitrified waste forms

    International Nuclear Information System (INIS)

    Rankin, W.N.

    1978-01-01

    The compatibility of vitrified radioactive waste with candidate canister materials will be evaluated with both cast and in-can melted vitrified waste. Both real and simulated sludges will be used. In addition, the compatibility of these materials with salt from a possible final storage location will be determined. Cast vitrified waste will be tested with ASTM A 333 and ASTM A 516 low-carbon steels and Type 304L stainless steel at 100, 600 and 800 0 C. Cast vitrified waste that has been devitrified by heat treatment will be tested at 100 0 C. Two types of test specimens will be used with either simulated or real sludges: (1) unsealed capsules made of pieces of mill-finished pipe into which vitrified waste is cast, and (2) sealed capsules containing a small container of vitrified waste identical to the ones in the unsealed capsule. In-can melted vitrified waste will be tested with synthetic sludge only and with ASTM A 333 and ASTM A 516 low-carbon steels, Type 304L stainless steel and Inconel 600. Two types of tests will be carried out: (1) melting vitrified waste in miniature metal canisters and (2) exposure of small (carefully measured) metal coupons to molten glass. The air oxidation rates of candidate canister materials will be determined, and specimens will also be exposed to salt from Drill Hole AEC-8 in Carlsbad, New Mexico. Sealed capsules containing an ASTM A 516 low-carbon steel or Type 304L stainless steel specimen partially embedded in a small block of salt will be heated

  12. Dermatitis de contacto por prótesis ortopédicas Contact dermatitis for orthopaedic prostheses

    Directory of Open Access Journals (Sweden)

    C.A. Danielo

    2007-09-01

    Full Text Available Diversas aleaciones son utilizadas en la fabricación de prótesis ortopédicas (ej: titanio, vitalio, etc, dentro de las cuales la más utilizada es la de acero inoxidable. El níquel, parte importante de esta aleación, es capaz de liberarse y provocar sensibilización, desencadenando reacciones cutáneas locales y sistémicas. De los materiales que componen la aleación para formar acero inoxidable, el níquel es el que más frecuentemente se ve implicado en reacciones cutáneas por sensibilidad, en tanto que otros como el cromo y cobalto, la posibilidad de pérdida de material a partir de la prótesis es discutida. Presentamos el caso de una paciente con dermatitis alérgica al níquel con lesiones generalizadas, que aparecieron luego del implante de prótesis ortopédicas de acero inoxidable, dando positivo para níquel sulfato en las pruebas epicutáneas.Several alloys are used in the manufacture of orthopaedics prostheses (ie: titanium, vitalium. Stainless steel is the most frequently used among them. Nickel is an important component of this alloy and may release and provoke sensitivity. Arising local and systemic cutaneous reactions. Nickel is the material composing stainless steel that ordinary is implicated in cutaneous reactions of sensitivity; the role of chrome or cobalt is still uncertain. Our patient is a woman affected of nickel contact dermatitis, with generalized reactions that appear after an implant of a stainless steel orthopaedic prosthesis. Epicutaneous tests were performed, confirming a strong sensitivity to nickel sulphate.

  13. Deposition and characterization of zirconium nitride (ZrN) thin films by reactive magnetron sputtering with linear gas ion source and bias voltage

    Energy Technology Data Exchange (ETDEWEB)

    Kavitha, A.; Kannan, R. [Department of Physics, University College of Engineering, Anna University, Dindugal-624622 (India); Subramanian, N. Sankara [Department of Physics, Thiagarajar College of Engineering, Madurai -625015, Tamilnadu (India); Loganathan, S. [Ion Plating, Titan Industries Ltd., Hosur - 635126, Tamilnadu (India)

    2014-04-24

    Zirconium nitride thin films have been prepared on stainless steel substrate (304L grade) by reactive cylindrical magnetron sputtering method with Gas Ion Source (GIS) and bias voltage using optimized coating parameters. The structure and surface morphologies of the ZrN films were characterized using X-ray diffraction, atomic microscopy and scanning electron microscopy. The adhesion property of ZrN thin film has been increased due to the GIS. The coating exhibits better adhesion strength up to 10 N whereas the ZrN thin film with bias voltage exhibits adhesion up to 500 mN.

  14. Optimization of process parameters in welding of dissimilar steels using robot TIG welding

    Science.gov (United States)

    Navaneeswar Reddy, G.; VenkataRamana, M.

    2018-03-01

    Robot TIG welding is a modern technique used for joining two work pieces with high precision. Design of Experiments is used to conduct experiments by varying weld parameters like current, wire feed and travelling speed. The welding parameters play important role in joining of dissimilar stainless steel SS 304L and SS430. In this work, influences of welding parameter on Robot TIG Welded specimens are investigated using Response Surface Methodology. The Micro Vickers hardness tests of the weldments are measured. The process parameters are optimized to maximize the hardness of the weldments.

  15. J-controlled crack growth as an indicator of hydrogen-stainless steel compatibility

    International Nuclear Information System (INIS)

    Dietrich, M.R.; Caskey, G.R. Jr.; Donovan, J.A.

    1980-01-01

    The J-integral was evaluated as a parameter to characterize fracture of stainless steels and as a measure of hydrogen damage. C-shaped specimens of type 304L, 316, and 21-6-9 stainless steels were tested in high pressure helium and hydrogen. The critical force for crack initiation (Jm), and tearing resistance (dJ/da) were decreased by hydrogen in all three alloys. The J-integral appears useful as a measure of hydrogen compatibility because it is sensitive to both test environment and microstructure

  16. Properties of concentrated plutonium nitrate solutions

    International Nuclear Information System (INIS)

    Gray, J.H.; Swanson, J.L.

    1978-01-01

    Selected properties were measured for solutions containing about 500 and 700 g/l plutonium (IV) in 4--5M nitric acid: density, viscosity, vapor pressure, boiling point, radiolytic gas (H 2 ) evolution rates, and corrosion rate on Ti and 304L stainless steel. Pu solubility was determined to be 550 to 800 g/l in 2.5 to 7M HNO 3 at ambient temperature and 820 to 860 g/l in 3M HNO 3 at 50 0 C

  17. Influence of dynamic material properties on the design criteria of containment structures for fast breeder reactors

    International Nuclear Information System (INIS)

    Albertini, C.; Montagnani, M.

    1978-01-01

    Effects of defects in materials, created by welding processes and irradiation, are examined taking into account the influence of strain-rate. Materials examined are austenitic stainless steels, such as AISI 316 L and H, AISI 304 L. The influence of such parameters on the flow curves of these materials requires the introduction of additional safety coefficients in calculating the response of dynamically loaded structures such as the pressure vessel in the case of an accident. Furthermore the effects of dynamic multi-axial loading and wave propagation should be taken into account in the safety analysis. Running experiments in dynamic biaxial loading conditions are introduced. (author)

  18. Aluminum and Other Coatings for the Passivation of Tritium Storage Vessels

    Energy Technology Data Exchange (ETDEWEB)

    Spencer, W. [Savannah River Site (SRS), Aiken, SC (United States). Savannah River National Lab. (SRNL); Korinko, P. [Savannah River Site (SRS), Aiken, SC (United States). Savannah River National Lab. (SRNL)

    2016-11-16

    Using a highly sensitive residual gas analyzer, the off-gassing of hydrogen, water, and hydrocarbons from surface-treated storage vessels containing deuterium was measured. The experimental storage vessels were compared to a low-off-gassing, electro-polished 304L canister. Alternative vessels were made out of aluminum, or were coatings on 304L steel. Coatings included powder pack aluminide, electro-plated aluminum, powder pack chromide, dense electro-plated chromium, copper plated, and copper plated with 25 and 50 percent nano-diamond. Vessels were loaded with low pressure deuterium to observe exchange with protium or hydrogen as observed with formation of HD and HDO. Off gas of D2O or possible CD4 was observed at mass 20. The main off-gas in all of the studies was H2. The studies indicated that coatings required significant post-coating treatment to reduce off-gas and enhance the permeation barrier from gases likely added during the coating process. Dense packed aluminum coatings needed heating to drive off water. Electro-plated aluminum, chromium and copper coatings appeared to trap hydrogen from the plating process. Nano-diamond appeared to enhance the exchange rate with hydrogen off gas, and its coating process trapped significant amounts of hydrogen. Aluminum caused more protium exchange than chromium-treated surfaces. Aluminum coatings released more water, but pure aluminum vessels released small amounts of hydrogen, little water, and generally performed well. Chromium coating had residual hydrogen that was difficult to totally outgas but otherwise gave low residuals for water and hydrocarbons. Our studies indicated that simple coating of as received 304L metal will not adequately block hydrogen. The base vessel needs to be carefully out-gassed before applying a coating, and the coating process will likely add additional hydrogen that must be removed. Initial simple bake-out and leak checks up to 350° C for a few hours was

  19. Formation of M23C6-type precipitates and chromium-depleted zones in austenite stainless steel

    International Nuclear Information System (INIS)

    Kaneko, Kenji; Fukunaga, Tatsuya; Yamada, Kazuhiro; Nakada, Nobuo; Kikuchi, Masao; Saghi, Zineb; Barnard, Jon S.; Midgley, Paul A.

    2011-01-01

    Graphical abstract: Precipitate formation during the in situ annealing experiment at 650 o C. -- Formation of M 23 C 6 carbides and chromium-depleted zones in commercially available type 304L stainless steel were investigated by in situ transmission electron microscopy and analytical transmission electron microscopy. It was found that each individual small M 23 C 6 carbide starts to grow with a clear orientation relationship with the matrix, and film-like carbide was subsequently observed at the interfaces with asymmetric Cr-depleted zones. From these experimental results, a model describing the precipitation of M 23 C 6 and the formation of the Cr-depleted zone was proposed.

  20. Study and characterization of noble metal deposits on similar rusty surfaces to those of the reactor U-1 type BWR of nuclear power station of Laguna Verde; Estudio y caracterizacion de depositos de metales nobles sobre superficies oxidadas similares a las del reactor de la Central de Laguna Verde (CNLV) U1 del tipo BWR

    Energy Technology Data Exchange (ETDEWEB)

    Flores S, V. H.

    2011-07-01

    In the present investigation work, were determined the parameters to simulate the conditions of internal oxidation reactor circulation pipes of the nuclear power plant of Laguna Verde in Veracruz. We used 304l stainless steel cylinders with two faces prepared with abrasive paper of No. 600, with the finality to obtain similar surface to the internal circulation piping nuclear reactor. Oxides was formed within an autoclave (Autoclave MEX-02 unit B), which is a device that simulates the working conditions of the nuclear reactor, but without radiation generated by the fission reaction within the reactor. The oxidation conditions were a temperature of 280 C and pressure of 8 MPa, similar conditions to the reactor operating in nuclear power plant of Laguna Verde in Veracruz, Mexico (BWR conditions), with an average conductivity of 4.58 ms / cm and 2352 ppb oxygen to simulate normal water chemistry NWC. Were obtained deposits of noble metal oxides formed on 304l stainless steel samples, in a 250 ml autoclave at a temperature range of 180 to 200 C. The elements that were used to deposit platinum-rhodium (Pt-Rh) with aqueous Na{sub 2}Pt (OH){sub 6} and Na{sub 3}Rh (NO{sub 2}){sub 6}, Silver (Ag) with an aqueous solution of AgNO{sub 3}, zirconium (Zr) with aqueous Zr O (NO{sub 3}) and ZrO{sub 2}, and zinc (Zn) in aqueous solution of Zn (NO{sub 3}){sub 2} under conditions of normal water chemistry. Also there was the oxidation of 304l stainless steel specimens in normal water chemistry with a solution of Zinc (Zn) (NWC + Zn). Oxidation of the specimens in water chemistry with a solution of zinc (Zn + NWC) was prepared in two ways: within the MEX-02 autoclave unit A in a solution of zinc and a flask at constant temperature in zinc solution. The oxides formed and deposits were characterized by scanning electron microscopy, energy dispersive X-ray analysis, elemental field analysis and X-ray diffraction. By other hand was evaluated the electrochemical behavior of the oxides

  1. Experimental tests on ratchet of structural elements diagrams for primary tension and secondary twist

    International Nuclear Information System (INIS)

    Lebey, J.; Roche, R.L.; Cousseran, P.

    1980-05-01

    Design by analysis of pressure vessels is not complete without an appraisal of failure by progressive distortion or stress ratchet. Ratchet tests under constant axial stress associated with cyclic torsion deformation have been carried out on 304 L and 316 L thin tubular specimens, at room temperature. Results are given in the form of iso-deformation curves ranging from 0.1% to 2.5%, in the field definite by the primary and secondary stress intensities (Bree's diagram type). The use of an effective primary stress is proposed, as a practical way, to assess the elongation due to the ratchet effect

  2. High-level waste canister envelope study: structural analysis

    International Nuclear Information System (INIS)

    1977-11-01

    The structural integrity of waste canisters, fabricated from standard weight Type 304L stainless steel pipe, was analyzed for sizes ranging from 8 to 24 in. diameter and 10 to 16 feet long under normal, abnormal, and improbable life cycle loading conditions. The canisters are assumed to be filled with vitrified high-level nuclear waste, stored temporarily at a fuel reprocessing plant, and then transported for storage in an underground salt bed or other geologic storage. In each of the three impact conditions studies, the resulting impact force is far greater than the elastic limit capacity of the material. Recommendations are made for further study

  3. Electrochemical Impedance Spectroscopy Of Metal Alloys

    Science.gov (United States)

    Macdowell, L. G.; Calle, L. M.

    1993-01-01

    Report describes use of electrochemical impedance spectroscopy (EIS) to investigate resistances of 19 alloys to corrosion under conditions similar to those of corrosive, chloride-laden seaside environment of Space Transportation System launch site. Alloys investigated: Hastelloy C-4, C-22, C-276, and B-2; Inconel(R) 600, 625, and 825; Inco(R) G-3; Monel 400; Zirconium 702; Stainless Steel 304L, 304LN, 316L, 317L, and 904L; 20Cb-3; 7Mo+N; ES2205; and Ferralium 255. Results suggest electrochemical impedance spectroscopy used to predict corrosion performances of metal alloys.

  4. Magnetic permeability of stainless steel for use in accelerator beam transport systems

    International Nuclear Information System (INIS)

    Wilson, N.G.; Bunch, P.

    1991-01-01

    High-vacuum beam transport tubes are being designed for use in an accelerator under development at Los Alamos. In areas such as weld-heat-affected zones, the tubes will require localized magnetic permeability of less than 1.02. Seven austenitic stainless steel candidates, 304L, 310, 316L, 317LN, 20Cb-3, Nitronic 33, and Nitronic 40, have been evaluated to determine their permeability in cold-worked, annealed, and weld-affected zones. 310 and 20Cb-3 showed permeability after welding of less than 1.01. 1 ref., 1 fig., 1 tab

  5. Fabrication and loading of long-term stress corrosion cracking surveillance specimens for the Dresden 1 decontamination program

    International Nuclear Information System (INIS)

    Walker, W.L.

    1979-10-01

    Stress-corrosion cracking test specimens were prepared for Dow Nuclear Services for insertion in the Dresden 1 reactor during the chemical decontamination of the primary system, and for subsequent exposure under operating conditions when the station returns to service. The specimens consist of pressurized tubes fabricated from Type-304 and -304L stainless steel, Inconel 600, Incoloy 800, and Zircaloy 2. In addition, constant radius bent-beam specimens of 3/4 hard Type-410 stainless steel were also included. All specimens were stressed to, or slightly above, their respective 0.2% offset yield strengths at the temperatures of interest

  6. Failures of austenitic stainless steel components during storage: Case studies

    International Nuclear Information System (INIS)

    Shah, B.K.; Rastogi, P.K.; Sinha, A.K.; Kulkarni, P.G.

    1993-01-01

    Three studies of failures of austenitic stainless steel components during storage are described. In all cases, stress corrosion cracking was the failure mode by the action of residual stress alone. However, the source of residual stress was different for each case. Case 1 was the failure of a sample tube header for a pressurized heavy water reactor (PHWR). In Case 2, a heat exchanger shell failed during a hydrotest in a fertilizer plant. Cases concerned the cracking of type 304L plates used for spent fuel pool lining of a nuclear power station

  7. Magnetic susceptibility and magnetization studies of some commercial austenitic stainless steels

    International Nuclear Information System (INIS)

    Collings, E.W.

    1979-01-01

    Results of magnetic susceptibility measurements using the Curie magnetic force technique are reported for six AISI 300-series alloys 310S, 304, 304L, 304N, 316, 316L as well as AWS 330 weld metal and Inconel 625. The temperature ranged from 5 to 416 0 K. Magnetization measurements over the temperature range 3 to 297 0 K, performed using a vibrating-sample magnetometer, are also reported. Alloy compositions and sample preparation procedures are discussed and numerical results of the study are presented. Magnetic characteristics of the four principal types of austenitic stainless steels studied are summarized

  8. Controlled chloride cracking of austenitic stainless steel tube samples

    OpenAIRE

    Raseroka, M.S.; Pistorius, P.C.

    2009-01-01

    An experimental rig has been constructed to produce chloride stress corrosion cracks in Type 304L stainless steel tube samples. The samples are to be used to test possible in situ repair methods in future work. The factor which influences the time to failure most strongly is the sample temperature; the distribution of cracks within the sample is affected by local temperature variations and by the position of the water line. Low-frequency oscillations in stress, caused by the on-off temperatur...

  9. Tribocorrosion wear of austenitic and martensitic steels

    Directory of Open Access Journals (Sweden)

    G. Rozing

    2016-07-01

    Full Text Available This paper explores the impact of tribocorrosion wear caused by an aggressive acidic media. Tests were conducted on samples made of stainless steel AISI 316L, 304L and 440C. Austenitic steels were tested in their nitrided state and martensitic in quenched and tempered and then induction hardened state. Electrochemical corrosion resistance testing and analysis of the microstructure and hardness in the cross section was carried out on samples of selected steels. To test the possibility of applying surface modification of selected materials in conditions of use, tests were conducted on samples/parts in a worm press for final pressing.

  10. Hydrogen Absorption Induced Slow Crack Growth in Austenitic Stainless Steels for Petrochemical Pressure Vessel Industries

    Directory of Open Access Journals (Sweden)

    Ronnie Rusli

    2011-05-01

    Full Text Available Type 304Land type 309 austenitic stainless steels were tested either by exposed to gaseous hydrogen or undergoing polarized cathodic charging. Slow crack growth by straining was observed in type 304L, and the formation of α‘ martensite was indicated to be precursor for such cracking. Gross plastic deformation was observed at the tip of the notch, and a single crack grew slowly from this region in a direction approximately perpendicular to the tensile axis. Martensite formation is not a necessary condition for hydrogen embrittlement in the austenitic phase.

  11. Hydrogen permeation through metallic foils

    International Nuclear Information System (INIS)

    Bernardi, M.I.B.; Rodrigues, J.A.

    1987-01-01

    The process of electrolytic permeation of hydrogen through metallic foils is studied. A double electrolytic cell, in glass, in which the two compartments of reaction are separated by a metallic foil to be studied, was built. As direct result, the hydrogen diffusion coefficient in the metal is obtained. The hydrogen diffusion coefficients in the palladium and, in austenitic stainless steels 304 and 304 L, used in the Angra-1 reactor, were obtained. Samples of stainless steels with and without welding, were used. (Author) [pt

  12. Joining uranium to steel

    International Nuclear Information System (INIS)

    Perkins, M.A.

    1976-05-01

    A method has been devised which will allow the joining of uranium to steel by fusion welding through the use of an intermediate material. Uranium-0.5 titanium was joined to AISI 304L stainless steel by using a vanadium insert. Also, a method is now available for selecting possible filler metals when two entirely dissimilar metals need to be joined. This method allows a quantitative ranking to be made of the possible filler metals and thus the most likely candidate can be selected

  13. Underwater laser cutting of metal structures

    Energy Technology Data Exchange (ETDEWEB)

    Alfille, J.P.; Prunele, D. de [CEA Centre d`Etudes de Saclay, 91 - Gif-sur-Yvette (France). Direction des Technologies Avancees; Pilot, G. [CEA Centre d`Etudes de Fontenay-aux-Roses, 92 (France). Dept. de Protection de l`Environnement et des Installations; Fredrick, P.; Ramaswami, V.S.; Muys, P. [Radius Engineering, Gent (Belgium)

    1994-12-31

    Cutting tests were carried out on stainless steel (304L) in air and under 7 meters of water (application to reactor pools), using CO{sub 2} and YAG lasers; results concerned cutting speed, quality of cut, cutting thickness. By-products of sectioning operations using a CO{sub 2} laser were studied: dross, aerosols, suspended particles in water, gas analysis, chemical analysis of the aerosols. Same measurements are currently being taken in the case of the YAG laser with beam transported via optical fiber. (from author). 16 figs., 2 tabs., 3 refs.

  14. New pulsed YAG laser performances in cutting thick metallic materials for nuclear applications

    International Nuclear Information System (INIS)

    Alfille, J.P.; Prunele, D. de; Pilot, G.

    1996-01-01

    The purpose of this study was to evaluate the capacities of the pulsed YAG laser thick cutting on metallic material and to compare with the CO 2 laser capacities. Stainless steel (304L) cutting tests were made in air and underwater using CO 2 and YAG lasers. A performance assessment was made for each laser and the wastes produced in the cutting operation were measured and the gases and the aerosols analyzed. The results show that the pulsed YAG laser is high performance tool for thick cutting and particularly attractive for nuclear applications

  15. Study and characterization of noble metal deposits on similar rusty surfaces to those of the reactor U-1 type BWR of nuclear power station of Laguna Verde

    International Nuclear Information System (INIS)

    Flores S, V. H.

    2011-01-01

    In the present investigation work, were determined the parameters to simulate the conditions of internal oxidation reactor circulation pipes of the nuclear power plant of Laguna Verde in Veracruz. We used 304l stainless steel cylinders with two faces prepared with abrasive paper of No. 600, with the finality to obtain similar surface to the internal circulation piping nuclear reactor. Oxides was formed within an autoclave (Autoclave MEX-02 unit B), which is a device that simulates the working conditions of the nuclear reactor, but without radiation generated by the fission reaction within the reactor. The oxidation conditions were a temperature of 280 C and pressure of 8 MPa, similar conditions to the reactor operating in nuclear power plant of Laguna Verde in Veracruz, Mexico (BWR conditions), with an average conductivity of 4.58 ms / cm and 2352 ppb oxygen to simulate normal water chemistry NWC. Were obtained deposits of noble metal oxides formed on 304l stainless steel samples, in a 250 ml autoclave at a temperature range of 180 to 200 C. The elements that were used to deposit platinum-rhodium (Pt-Rh) with aqueous Na 2 Pt (OH) 6 and Na 3 Rh (NO 2 ) 6 , Silver (Ag) with an aqueous solution of AgNO 3 , zirconium (Zr) with aqueous Zr O (NO 3 ) and ZrO 2 , and zinc (Zn) in aqueous solution of Zn (NO 3 ) 2 under conditions of normal water chemistry. Also there was the oxidation of 304l stainless steel specimens in normal water chemistry with a solution of Zinc (Zn) (NWC + Zn). Oxidation of the specimens in water chemistry with a solution of zinc (Zn + NWC) was prepared in two ways: within the MEX-02 autoclave unit A in a solution of zinc and a flask at constant temperature in zinc solution. The oxides formed and deposits were characterized by scanning electron microscopy, energy dispersive X-ray analysis, elemental field analysis and X-ray diffraction. By other hand was evaluated the electrochemical behavior of the oxides formed on the surface of 304l stainless steel

  16. On the effectiveness of surface severe plastic deformation by shot peening at cryogenic temperature

    Science.gov (United States)

    Novelli, M.; Fundenberger, J.-J.; Bocher, P.; Grosdidier, T.

    2016-12-01

    The effect of cryogenic temperature (CT) on the graded microstructures obtained by severe shot peening using surface mechanical attrition treatment (SMAT) was investigated for two austenitic steels that used different mechanisms for assisting plastic deformation. For the metastable 304L steel, the depth of the hardened region increases because CT promotes the formation of strain induced martensite. Comparatively, for the 310S steel that remained austenitic, the size of the subsurface affected region decreases because of the improved strength of the material at CT but the fine twinned nanostructures results in significant top surface hardening.

  17. Yucca Mountain project container fabrication, closure and non-destructive evaluation development activities

    International Nuclear Information System (INIS)

    Russell, E.W.; Nelson, T.A.

    1989-06-01

    In this presentation, container fabrication, closure, and non-destructive evaluation (NDE) process development activities are described. All of these activities are interrelated, and will contribute to the metal barrier selection activity. The plan is to use a corrosion-resistant material in the form of a cylinder with a wall thickness of ∼1cm (2cm for pure copper.) The materials under consideration include the three austenitic alloys: stainless steel-304L, stainless steel-316L and alloy 825, as well as the three copper alloys: CDA 102, CDA 613, and CDA 715. This document reviews the recommended procedures and processes for fabricating, closing and evaluating each of the candidate materials

  18. Underwater laser cutting of metal structures

    International Nuclear Information System (INIS)

    Alfille, J.P.; Prunele, D. de

    1994-01-01

    Cutting tests were carried out on stainless steel (304L) in air and under 7 meters of water (application to reactor pools), using CO 2 and YAG lasers; results concerned cutting speed, quality of cut, cutting thickness. By-products of sectioning operations using a CO 2 laser were studied: dross, aerosols, suspended particles in water, gas analysis, chemical analysis of the aerosols. Same measurements are currently being taken in the case of the YAG laser with beam transported via optical fiber. (from author). 16 figs., 2 tabs., 3 refs

  19. Local strain in front of cracks in the case of creep fatigue

    International Nuclear Information System (INIS)

    Rie Kyongtschong; Olfe, J.

    1993-01-01

    In-situ measurements of strain fields in front of cracks were performed for high temperature Low Cycle Fatigue (LCF) with different hold times by means of a grid method. The tests were carried out on the austenitic stainless steel 304 L and the ferritic steel X22 CrMoV 12 1. Simultaneous observation of crack growth leads to a correlation between crack growth and local strain. The interaction of creep and fatigue related to strain concentration at the crackk tip and crack growth was discussed. A model is proposed which is based on the formation of cavities on grain boundaries. (orig.) [de

  20. A multi-level code for metallurgical effects in metal-forming processes

    Energy Technology Data Exchange (ETDEWEB)

    Taylor, P.A.; Silling, S.A. [Sandia National Labs., Albuquerque, NM (United States). Computational Physics and Mechanics Dept.; Hughes, D.A.; Bammann, D.J.; Chiesa, M.L. [Sandia National Labs., Livermore, CA (United States)

    1997-08-01

    The authors present the final report on a Laboratory-Directed Research and Development (LDRD) project, A Multi-level Code for Metallurgical Effects in metal-Forming Processes, performed during the fiscal years 1995 and 1996. The project focused on the development of new modeling capabilities for simulating forging and extrusion processes that typically display phenomenology occurring on two different length scales. In support of model fitting and code validation, ring compression and extrusion experiments were performed on 304L stainless steel, a material of interest in DOE nuclear weapons applications.

  1. Note on a simple test method for estimaing J/sub Ic/

    International Nuclear Information System (INIS)

    Whipple, T.A.; McHenry, H.I.

    1980-01-01

    Fracture toughness testing is generally a time-consuming and expensive procedure; therefore, there has been a significant amount of effort directed toward developing an inexpensive and rapid method of estimating the fracture toughness of materials. In this paper, a simple method for estimating J/sub Ic/ through the use of small, notched, bend bars is evaluated. The test only involves the measurement of the energy necessary to fracture the sample. Initial tests on Fe-18Cr-3Ni-13Mn and 304L stainless steel at 76 and 4 0 K have yielded results consistent with other fracture toughness tests, for materials in the low- to medium-toughness range

  2. The Decontamination Technique for Metal by Using Pressured Solid of CO2

    International Nuclear Information System (INIS)

    Sutoto

    1998-01-01

    The decontamination of radioactive deposited in the stainless steel 304l type has been done. The radiation exposure was reduced from 460 to 200 mrem/h. For the supporting of the processes, the compressed air 12 bar was flue in blaster. The various of treatment are blasting time between 15 to 60 seconds. Result of the experiment is decontamination factor (DF) = 0,22 and the consumption of dry ice is 10 kgs needed. The secondary waste generated as aerosol were treated by HEPA Filter

  3. Study of the experimental parameters associated to the determination of residual macro stresses in stainless steel tubes, through x-ray diffraction method

    International Nuclear Information System (INIS)

    Guimaraes, L.R.

    1990-01-01

    The basic principles related to the determination of residual macro stresses by X-rays diffractometry are present, whereas different techniques associated with the respective experimental errors are discussed. The residual stresses in two 304 L stainless steel tubes were measured using three models of diffractometers, Rigaku SG-8, Jeol JDX-11PA and Rigaku Strainflex. The measured values of stresses as well as the reproducibilities are examined. The suitability of peak location method, by fitting three data points to the parabolic function, is discussed through values of position and intensity obtained by two of the above diffractometers. (author)

  4. Study of the experimental parameters associated to the determination of residual macro stresses in stainless steel tubes through x-rays diffraction method

    International Nuclear Information System (INIS)

    Guimaraes, L.R.

    1990-01-01

    The basic principles related to the determination of residual macro stresses by X-rays diffractometry are present, whereas different techniques associated with the respective experimental errors are discussed. The residual stresses in two 304 L stainless steel tubes were measured using three models of diffractometers, Rigaku SG-8, Jeol JDX-11PA and Rigaku Strainflex. The measured values of stresses as well as the reproducibilities are examined. The suitability of peak location method, by fitting three data points to the parabolic function, is discussed through values of position and intensity obtained by two of the above diffractometers. (author)

  5. Examples of expert methodology. B : met cases in nuclear power plants

    International Nuclear Information System (INIS)

    Gras, J.M.

    1994-01-01

    In spite of especially severe quality controls of materials, stress corrosion is the most important problem met during PWR type reactors operating. Examples of corrosion (except stress corrosion) are presented. Intergranular corrosion is illustrated by stainless steel 18-10 family (fuels assemblies, heat exchanger of a breeder reactor) and by Inconel 600 (vapor generator J tubes), electrochemical corrosion by low alloy Mn-Ni-Mo steel coated with an austenitic steel (pressure vessel pipes), pitting corrosion by Inconel 600 (vapor generator) and by stainless steel 304L (raw water circuits), erosion/corrosion by carbon steels (PWR secondary circuits). (A.B.). 13 refs., 9 figs

  6. Influence of plastic strain localization on the stress corrosion cracking of austenitic stainless steels; Influence de la localisation de la deformation plastique sur la CSC d'aciers austenitiques inoxydables

    Energy Technology Data Exchange (ETDEWEB)

    Cisse, S.; Tanguy, B. [CEA Saclay, DEN, SEMI, 91 - Gif-sur-Yvette (France); Andrieu, E.; Laffont, L.; Lafont, M.Ch. [Universite de Toulouse. CIRIMAT, UPS/INPT/CNRS, 31 - Toulous (France)

    2010-03-15

    The authors present a research study of the role of strain localization on the irradiation-assisted stress corrosion cracking (IASCC) of vessel steel in PWR-type (pressurized water reactor) environment. They study the interaction between plasticity and intergranular corrosion and/or oxidation mechanisms in austenitic stainless steels with respect to sublayer microstructure transformations. The study is performed on three austenitic stainless grades which have not been sensitized by any specific thermal treatment: the A286 structurally hardened steel, and the 304L and 316L austenitic stainless steels

  7. Passivation of duplex stainless steel in solutions simulating chloride-contaminated concrete

    Directory of Open Access Journals (Sweden)

    Takenouti, H.

    2007-12-01

    Full Text Available Most studies published to date on the corrosion behaviour of stainless reinforcing steel are based on austenitic steel. The market presence of corrugated duplex steel is growing, however. The present study compared passivity in 2205 type duplex and 304 type austenitic stainless steel. Polarization tests in chloride-containing Ca(OH2 solutions confirmed the exceptional performance of duplex steels. X-ray photoelectronic spectroscopy (XPS showed that the passive layer generated on duplex stainless steel in media simulating concrete pore solutions had a higher Cr content than the layer formed on steel in contact with the air. The XPS results also revealed that in duplex steel the form adopted by the passive layer Fe oxides was Fe3O4 in the solutions simulating concrete, rather than Fe2O3, as in duplex steel exposed to air. Electrochemical impedance spectroscopy (EIS can be used to monitor the transformations taking place in the passive layer and analyze the factors involved.La mayoría de los estudios publicados hasta el momento sobre el comportamiento frente a la corrosión de armaduras de acero inoxidable se basan en aceros austeníticos. Sin embargo, la presencia en el mercado de aceros corrugados dúplex es cada vez más importante. En este trabajo se analiza la pasividad de un acero inoxidable dúplex tipo 2205 en comparación con la de un inoxidable austenítico tipo 304. Los ensayos de polarización en disoluciones de Ca(OH2 con cloruros confirman el excepcional comportamiento de los aceros dúplex. La espectroscopía fotoelectrónica de rayos X (XPS informa de que la capa pasiva generada en aceros inoxidables dúplex en medios que simulan la disolución de los poros del hormigón posee mayor contenido en óxidos de Cr que la formada en aire. También se puede deducir de los resultados de XPS que los óxidos de Fe de la capa pasiva de los aceros dúplex se encuentran en forma de Fe3O4 en las disoluciones que simulan el hormigón en vez de en

  8. A comparison of in vitro friction forces among conventional and self-ligating aesthetic orthodontic brackets

    OpenAIRE

    Leal, Rodrigo Severo

    2009-01-01

    O objetivo do presente estudo consistiu em comparar in vitro o atrito produzido por braquetes estéticos, convencionais e autoligados quando inseridos fios retangulares de aço inoxidável de diferentes dimensões, nas angulações de zero e três graus entre os braquetes. Foram utilizados 120 braquetes de 6 marcas comerciais (Gemini, Clarity convencional, Transcend, Inspire, Clarity autoligado, Damon autoligado), sendo 20 braquetes de cada marca comercial. Para os ensaios laboratoriais, foram colad...

  9. Modelamiento del proceso de recubrimiento de instrumental quirúrgico con cromoduro

    Directory of Open Access Journals (Sweden)

    Jairo Ruiz

    2003-01-01

    Full Text Available En este artículo se presenta un modelo estadístico que describe el comportamiento de la variable respuesta espesor del recubrimiento de cromoduro en los portagujas quirúrgicos, de acero inoxidable martensítico, como función del tiempo de exposición, la densidad de corriente y la temperatura; el modelo fue ajustado por medio de un diseño experimental rotacional compuesto de segundo orden. El modelo tiene un poder de explicación del 75% en la variabilidad de la respuesta, que se considera muy satisfactorio dada la complejidad del proceso.

  10. Comportamiento a fatiga del vástago de una prótesis para cadera al caminar//Fatigue behavior stem hip prosthesis for walking

    OpenAIRE

    Ángel Martínez-Delfín; Javier García-de-la-Figal-Costales; Luís Manuel Rodríguez-Milián; Reynaldo Rodríguez-Pérez

    2014-01-01

    La prótesis de cadera consiste en sustituir la parte superior fracturada del fémur por una pieza de material biocompatible. Debido a las cargas aleatorias que sobre esta prótesis actúan al caminar la persona injertada, surge la fatiga sobre la prótesis. En este trabajo se realiza el cálculo a fatiga del vástago de una prótesis de caderas fabricada con acero inoxidable austenítico AISI 316L GrQ y de uso actual. Para ellose emplea el método de los elementos finitos, considerando la compleja geo...

  11. Study of copper deposit on a porous electrode of carbon and stainless steel by sem-xrd and image analysis

    OpenAIRE

    Constanzo-R., Robinson; Pagliero-N., Antonio; Vergara-G., Froilán

    2014-01-01

    El objetivo de este trabajo fue realizar un análisis cualitativ o de la distribución de un electrodepósito de cobre en el inter ior de electrodos porosos (EP) de acero inoxidable y carbono grafito. Para ello, se reali zaron pruebas de electrodepositación de cobre a nivel de labora torio, con un posterior análisis de cortes de muestras de acero y grafito vía Microscopía Estereoscópica, Microscopía SEM-DRX y Análisis de Imagen, los cuales mostraron que el cobre no se deposita en forma uniforme ...

  12. Análise comparativa da distribuição de tensões em incisivo central superior, restaurado com diferentes sistemas de pinos intra-radiculares

    OpenAIRE

    Oliveira, Luana Cristina Araújo de [UNESP

    2002-01-01

    Neste trabalho é proposto analisar a distribuição de tensões produzidas na dentina radicular do incisivo central superior restaurado com diferentes sistemas de pinos intra-radiculares, através dos Métodos de Fotoelasticidade e Elementos Finitos. Esta análise foi realizada para os seguintes sistemas de pinos intra-radiculares: fibra de carbono, fibra de vidro, zircônio, aço inoxidável, titânio e metálico fundido (Liga de Cu-Al), o dente hígido foi utilizado como controle. Em ambos método foi c...

  13. Elasto-plastic hardening models adjustment to ferritic, austenitic and austenoferritic Rebar; Ajuste de los aceros corrugados ferríticos, austeníticos y austenoferríticos a los modelos de endurecimiento elastoplástico por deformación

    Energy Technology Data Exchange (ETDEWEB)

    Hortigóna, B.; Gallardo, J.M.; Nieto-García, E.J.; López, J.A.

    2017-09-01

    The elastoplastic behaviour of steel used for structural member fabrication has received attention to facilitate a mechanical-resistant design. New Zealand and South African standards have adopted various theoretical approaches to describe such behaviour in stainless steels. With respect to the building industry, describing the tensile behaviour of steel rebar used to produce reinforced concrete structures is of interest. Differences compared with the homogenous material described in the above mentioned standards and related literatures are discussed in this paper. Specifically, the presence of ribs and the TEMPCORE® technology used to produce carbon steel rebar may alter the elastoplastic model. Carbon steel rebar is shown to fit a Hollomon model giving hardening exponent values on the order of 0.17. Austenitic stainless steel rebar behaviour is better described using a modified Rasmussen model with a free fitted exponent of 6. Duplex stainless steel shows a poor fit to any previous model. [Spanish] Uno de los principales factores tenidos en cuenta en la fabricación de aceros estructurales es su comportamiento durante la fase elastoplástica o de endurecimiento por deformación. Normas neozelandesas y sudafricanas plantean diversas aproximaciones teóricas para describir dicho comportamiento en el caso de los aceros inoxidables. En el campo de la construcción resulta de interés la descripción del comportamiento tenso-deformacional de los aceros corrugados utilizados en las estructuras de hormigón armado. En este artículo se discuten los modelos planteados en las normas citadas anteriormente así como los existentes en la literatura tanto para los aceros corrugados inoxidables como para los aceros al carbono fabricados mediante el proceso denominado TEMPCORE® Los aceros TEMPCORE® analizados arrojan un valor del exponente de endurecimiento por deformación según el modelo de Hollomon de 0.17. Los aceros inoxidables austeníticos se ajustan mejor al modelo

  14. MA-KUAGRO: ELEMENTO DE LA CULTURA PALENQUERA Y SU INCIDENCIA EN LAS PRÁCTICAS PEDAGÓGICAS EN LA ESCUELA, SAN BASILIO PALENQUE, COLOMBIA

    Directory of Open Access Journals (Sweden)

    Dimas Del Rosario De Ávila Tórres

    2013-02-01

    Full Text Available La investigación analizó los elementos de la cultura palenquera presentes en la escuela, particularmente “kuagro” que es manifestación organizativa propia, y su vínculo con las prácticas pedagógicas del personal docente y el aprovechamiento académico estudiantil. Este estudio aporta al proceso etno-educativo llevado a cabo en San Basilio de Palenque y otras comunidades culturalmente diferenciadas en Colombia. La investigación fue de tipo cualitativo, se hizo uso del método de la consulta  a la memoria colectiva,  creado por la comunidad palenquera en el marco del proceso de etno-educación. Las técnicas y herramientas fueron la observación, entrevista y conversatorios con docentes, estudiantes, líderes y lideresas, miembros del consejo comunitario. Entre los resultados se menciona que existe una articulación en la Institución Educativa Benkos Biohó y la comunidad, ya que el acervo cultural es el eje principal de las prácticas pedagógicas. Entre estos, se ha incluido los patios productivos, las ceremonias fúnebres, la música, entre otros, con la  participación de la gente anciana y sabia de la comunidad. Sin embargo, a pesar de lo anterior, los saberes y prácticas pedagógicas son diversos desde la perspectiva de los docentes sensibilizados, no sensibilizados y los que están en proceso de sensibilización. Los docentes sensibilizados han logrado un mejor desempeño académico en los estudiantes.Summary The research analyzed the elements of the palenque culture that are present in the school, particularly "kuagro" that it’s his own organizational manifestation, and its link with the teachers pedagogical practices and student achievement. This study contributes to the ethno-educational process conducted in San Basilio de Palenque and other communities in Colombia that are culturally different. The research was qualitative; we made use of the method of consulting the collective memory, created by the palenque community

  15. The resistance of austenitic stainless steels to pitting corrosion in simulated BFS/OPC pore waters containing thiosulphate ions

    International Nuclear Information System (INIS)

    Betts, A.J.; Newman, R.C.

    1989-06-01

    Current plans for the disposal of intermediate-level nuclear waste involve the use of austenitic stainless steel drums. The immediate environment seen by both the inner and outer surfaces of these drums will be alkaline, as a consequence of the encasement of both the drum and its contents in concrete. Normally there would be no risk of localized corrosion of the steel in this situation, but a possible complication is introduced by the use of blast-furnace slag (BFS) to decrease the permeability of the concrete. Metal sulphides in the BFS react with air and water to yield thiosulphate ions, which are known to be corrosive towards stainless steels in environments of near-neutral pH. This research was carried out to study the effects of thiosulphate at alkaline pH, simulating the concrete environment. Types 304L and 316L stainless steel have been tested for pitting corrosion resistance in simulated BFS/Ordinary Portland Cement pore waters of pH 10-13, at 20 o C and 50 o C. The results show that the 316L steel is essentially immune to pitting. The 304L steel shows some pitting at the higher temperature, especially at the higher chloride concentrations, but only at pH values of less than 12, which would require serious deterioration of the cement matrix. (author)

  16. Mass production of multi-wall carbon nanotubes by metal dusting process with high yield

    Energy Technology Data Exchange (ETDEWEB)

    Ghorbani, H. [School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Narmak, Tehran (Iran, Islamic Republic of); Rashidi, A.M., E-mail: Rashidiam@ripi.ir [Nanotechnology Research Center, Research Institute of Petroleum Industry (RIPI), West Blvd. Azadi Sport Complex, P.O. Box 14665-1998, Tehran (Iran, Islamic Republic of); Rastegari, S.; Mirdamadi, S. [School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Narmak, Tehran (Iran, Islamic Republic of); Alaei, M. [Nanotechnology Research Center, Research Institute of Petroleum Industry (RIPI), West Blvd. Azadi Sport Complex, P.O. Box 14665-1998, Tehran (Iran, Islamic Republic of)

    2011-05-15

    Research highlights: {yields} Synthesis of carbon nanotubes over Fe-Ni nanoparticles supported alloy 304L. {yields} Production of carbon nanotubes with high yield (700-1000%) and low cost catalyst. {yields} Optimum growth condition is CO/H{sub 2} = 1/1, 100 cm{sup 3}/min, at 620 {sup o}C under long term repetitive thermal cycling. {yields} Possibility of the mass production by metal dusting process with low cost. -- Abstract: Carbon nanotube materials were synthesized over Fe-Ni nanoparticles generated during disintegration of the surface of alloy 304L under metal dusting environment. The metal dusting condition was simulated and optimized through exposing stainless steel samples during long term repetitive thermal cycling in CO/H{sub 2} = 1/1, total gas flow rate 100 cm{sup 3}/min, at 620 {sup o}C for 300 h. After reaction, surface morphology of the samples and also carbonaceous deposition which had grown on sample surfaces were examined by stereoscopy, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Results revealed that multi-wall carbon nanotubes could be formed over nanocatalyst generated on the alloy surface by exploiting metal dusting process. By optimization of reaction parameters the yields of carbon nanotube materials obtained were 700-1000%. Also it has been shown herein that the amount of carbon nanotube materials remarkably increases when the reaction time is extended up to 300 h, indicating a possibility of the mass production by this easy method.

  17. Product consistency testing of three reference glasses in stainless steel and perfluoroalkoxy resin vessels

    International Nuclear Information System (INIS)

    Olson, K.M.; Smith, G.L.; Marschman, S.C.

    1995-03-01

    Because of their chemical durability, silicate glasses have been proposed and researched since the mid-1950s as a medium for incorporating high-level radioactive waste (HLW) generated from processing of nuclear materials. A number of different waste forms were evaluated and ranked in the early 1980s; durability (leach resistance) was the highest weighted factor. Borosilicate glass was rated the best waste form available for incorporation of HLW. Four different types of vessels and three different glasses were used to study the possible effect of vessel composition on durability test results from the Production Consistency Test (PCT). The vessels were 45-m 304 stainless steel vessels, 150-m 304 L stainless steel vessels, and 60-m perfluoroalkoxy (PFA) fluoropolymer resin vessels. The three glasses were the Environmental Assessment glass manufactured by Corning Incorporated and supplied by Westinghouse Savannah River company, and West Valley Nuclear Services reference glasses 5 and 6, manufactured and supplied by Catholic University of America. Within experimental error, no differences were found in durability test results using the 3 different glasses in the 304L stainless steel or PFA fluoropolymer resin vessels over the seven-day test period

  18. Influence of surface conditions on fatigue strength through the numerical simulation of microstructure

    International Nuclear Information System (INIS)

    Le Pecheur, A.; Clavel, M.; Rey, C.; Bompard, P.; Le Pecheur, A.; Curtit, F.; Stephan, J.M.

    2010-01-01

    A thermal fatigue test (INTHERPOL) was developed by EDF in order to study the initiation of cracks. These tests are carried out on tubular specimens under various thermal loadings and surface finish qualities in order to give an account of these parameters on crack initiation. The main topic of this study is to test the sensitivity of different fatigue criteria to surface conditions using a micro/macro modelling approach. Therefore a 304L polycrystalline aggregate, used for cyclic plasticity based FE modelling, have been considered as a Representative Volume Element located at the surface and subsurface of the test tube. This aggregate has been cyclically strained according to the results issued from FE simulation of INTHERPOL thermal fatigue experiment. Different surface parameters have been numerically simulated: effects of local microstructure and of grains orientation, effects of machining: metallurgical prehardening, residual stress gradient, and surface roughness. Three different fatigue criteria (Manson Coffin, Fatemi Socie and dissipated energy types), previously fitted at a macro-scale for thermal fatigue of 304L, have been computed at a meso scale, in order to show the surface 'hot spots' features and test the sensitivity of these three criteria to different surface conditions. Results show that grain orientation and neighbouring play an important role on the location of hot spots, and also that the positive effect of pre-straining and the negative effect of roughness on fatigue life are not all similarly predicted by these different fatigue criteria. (authors)

  19. Investigation of the liquid low-level waste evaporator steam coil failure and supporting laboratory studies

    International Nuclear Information System (INIS)

    Pawel, S.J.; Keiser, J.R.; Longmire, H.F.

    1995-05-01

    Using a remote video camera, the internals of a low-level waste evaporator tank (termed 2A2, type 304L stainless steel construction, known to have failed steam coils) were inspected. This inspection revealed at least three rather substantial holes as opposed to crack- or pit-like leak sites near the nominal solution level position on one particular steam coil. This section was removed from the evaporator vessel, and subsequent hot cell examination revealed extensive general corrosion on the process side of the coil with little or no attack on the steam side. Hot cell metallography confirmed intense general corrosion on the process side and, in addition, revealed shallow intergranular attack at the leading edge of corrosion. No pits or cracks were detected in this section of the steam coil. Laboratory corrosion tests with coupons of 304L (and other high-alloy materials) isothermally exposed in a range of solutions similar to those expected in the evaporator reveal only very low corrosion rates below 40% sodium hydroxide and the solution boiling point. However, open-quotes dried filmclose quotes experiments revealed that much more dilute solutions became aggressive to stainless steel due to concentrating effects (evaporation and periodic wetting) at the air/solution interface. The high general corrosion rates observed on the failed coil section occurred at or near the air/solution interface and were attributed to such open-quotes splash zoneclose quotes activity

  20. EDF program on SCC initiation of cold-worked stainless steels in primary water

    Energy Technology Data Exchange (ETDEWEB)

    Huguenin, P.; Vaillant, F.; Couvant, T. [Electricite de France (EDF/RD), Site des Renardieres, 77 - Moret sur loing (France); Buisse, L. [EDF UTO, 93 - Noisy-Le-Grand (France); Huguenin, P.; Crepin, J.; Duhamel, C.; Proudhon, H. [MINES ParisTech, Centre des Materiaux, 91 - Evry (France); Ilevbare, G. [EPRI California (United States)

    2009-07-01

    A few cases of Intergranular Stress Corrosion Cracking (IGSCC) on cold-worked austenitic stainless steels in primary water have been detected in French Pressurized Water Reactors (PWRs). A previous program launched in the early 2000's identified the required conditions for SCC of cold-worked stainless steels. It was found that a high strain hardening coupled with cyclic loading favoured SCC, whereas cracking under static conditions appeared to be difficult. A propagation model was also proposed. The first available results of the present study demonstrate the strong influence of a trapezoidal cyclic loading on the creep of 304L austenitic stainless steel. While no creep was detected under a pure static loading, the creep rate was increased by a factor 102 under a trapezoidal cyclic loading. The first results of SCC initiation performed on notched specimens under a trapezoidal cyclic loading at low frequency are presented. The present study aims at developing an engineering model for IGSCC initiation of 304L, 316L and weld 308L stainless steels. The effect of the pre-straining on the SCC mechanisms is more specifically studied. Such a model will be based on (i) SCC initiation tests on notched and smooth specimens under 'trapezoidal' cyclic loading and, (ii) constant strain rate SCC initiation tests. The influence of stress level, cold-work level, strain path, surface roughness and temperature is particularly investigated. (authors)

  1. Corrosion of stainless steels in lead-bismuth eutectic up to 600 °C

    Science.gov (United States)

    Soler, L.; Martín, F. J.; Hernández, F.; Gómez-Briceño, D.

    2004-11-01

    An experimental program has been carried out to understand the differences in the corrosion behaviour between different stainless steels: the austenitic steels 304L and 316L, the martensitic steels F82Hmod, T91 and EM10, and the low alloy steel P22. The influence of oxygen level in Pb-Bi, temperature and exposure time is studied. At 600 °C, the martensitic steels and the P22 steel exhibit thick oxide scales that grow with time, following a linear law for the wet environment and a parabolic law for the dry one. The austenitic stainless steels show a better corrosion behaviour, especially AISI 304L. Under reducing conditions, the steels exhibit dissolution, more severe for the austenitic stainless steels. At 450 °C, all the materials show an acceptable behaviour provided a sufficient oxygen level in the Pb-Bi. At reducing conditions, the martensitic steels and the P22 steel have a good corrosion resistance, while the austenitic steels exhibit already dissolution at the longer exposures.

  2. Study on the hydrogen embrittlement and corrosion of stainless steels used as NI/MHX battery containers

    Energy Technology Data Exchange (ETDEWEB)

    Chuang, H.J.; Chan, S.L.I. [National Taiwan University, Taipei (China); Chen, S.Y. [Chung Shan Institute of Science and Technology, Lung-Tan (China)

    1998-07-01

    Stainless steels are used as the containers for Nickel-metal hydride (Ni/MHx) batteries. In this work stainless steel 304, 304L, 316, 316L, 17-4PH and 430 were selected to study their relative susceptibility to hydrogen embrittlement and alkaline corrosion under battery environments. Comparisons were made by immersion test under different hydrogen pressure over the electrolyte, U-bend tests and slow strain rate tensile test with cathodic H{sub 2} charging. The results showed that high strength 17-4PH suffered severe corrosion after long time immersion in the electrolyte solution and were sensitive to hydrogen embrittlement after hydrogen charging. Ferritic 430 performed better than 17-4PH during immersion test but lost its ductility after hydrogen charging. All the austenitic steels (304, 304L, 316, 316L) were found to be suitable as the materials for Ni/MHx battery container, and the present tests can not discriminate their relative resistance to the corrosion and hydrogen embrittlement in the electrolyte. 5 refs.

  3. The specific heat loss combined with the thermoelastic effect for an experimental analysis of the mean stress influence on axial fatigue of stainless steel plain specimens

    Directory of Open Access Journals (Sweden)

    G. Meneghetti

    2014-10-01

    Full Text Available The energy dissipated to the surroundings as heat in a unit volume of material per cycle, Q, was recently proposed by the authors as fatigue damage index and it was successfully applied to correlate fatigue data obtained by carrying out fully reversed stress- and strain-controlled fatigue tests on AISI 304L stainless steel plain and notched specimens. The use of the Q parameter to analyse the experimental results led to the definition of a scatter band having constant slope from the low- to the high-cycle fatigue regime. In this paper the energy approach is extended to analyse the influence of mean stress on the axial fatigue behaviour of unnotched cold drawn AISI 304L stainless steel bars. In view of this, stress controlled fatigue tests on plain specimens at different load ratios R (R=-1; R=0.1; R=0.5 were carried out. A new energy parameter is defined to account for the mean stress effect, which combines the specific heat loss Q and the relative temperature variation due to the thermoelastic effect corresponding to the achievement of the maximum stress level of the stress cycle. The new two-parameter approach was able to rationalise the mean stress effect observed experimentally. It is worth noting that the results found in the present contribution are meant to be specific for the material and testing condition investigated here.

  4. Impact of phase stability on the corrosion behavior of the austenitic candidate materials for NNWSI [Nevada Nuclear Waste Storage Investigations

    International Nuclear Information System (INIS)

    Bullen, D.B.; Gdowski, G.E.; McCright, R.D.

    1987-10-01

    The Nuclear Waste Management Program at Lawrence Livermore National Laboratory is responsible for the development of the waste package design to meet the Nuclear Regulatory Commission licensing requirements for the Nevada Nuclear Waste Storage Investigations (NNWSI) Project. The metallic container component of the waste package is required to assist in providing substantially complete containment of the waste for a period of up to 1000 years. Long term phase stability of the austenitic candidate materials (304L and 316L stainless steels and alloy 825) over this time period at moderate temperatures (100-250 0 C) can impact the mechanical and corrosion behavior of the metal barrier. A review of the technical literature with respect to phase stability of 304L, 316L and 825 is presented. The impact of martensitic transformations, carbide precipitation and intermediate (σ, chi, and eta) phase formation on the mechanical properties and corrosion behavior of these alloys at repository relevant conditions is discussed. The effect of sensitization on intergranular stress corrosion cracking (IGSCC) of each alloy is also addressed. A summary of the impact of phase stability on the degradation of each alloy in the proposed repository environment is included. 32 refs., 6 figs

  5. Development of high temperature reference electrodes for potentiometric analyses in supercritical water environments

    International Nuclear Information System (INIS)

    Tung Yuming; Yeh Tsungkuang; Wang Meiya

    2014-01-01

    A specifically designed reference electrode was developed for analyzing the electrochemical behaviors of alloy materials in supercritical water (SCW) environments and identifying the associated electrochemical parameters. In this study, Ag/AgCl reference electrodes and Zr/ZrO 2 reference electrodes suitable for high-temperature applications were manufactured and adopted to measure the electrochemical corrosion potentials (ECPs) of 304L stainless steel (SS) and nickel-based alloy 625 in SCW environments with various amounts of dissolved oxygen (DO). The Ag/AgCl reference electrode made in this laboratory was used as a calibration base for the laboratory-made Zr/ZrO 2 reference electrode at high temperatures up to 400degC. The two reference electrodes were then used for ECP measurements of 304L SS and alloy 625 specimens in 400degC SCW with various DO levels of 300 ppb, 1 ppm, 8.3 ppm, and 32 ppm and under deaerated conditions. The outcome indicated that concentration increases in DO in the designated SCW environment would yield increases in ECP of the two alloys and they exhibited different ECP responses to DO levels. In addition, the laboratory-made Zr/ZrO 2 reference electrode was able to continuously operate for several months and delivered consistent and steady ECP data of the specimens in SCW environments. (author)

  6. Selection of candidate canister materials for high-level nuclear waste containment in a tuff repository

    International Nuclear Information System (INIS)

    McCright, R.D.; Weiss, H.; Juhas, M.C.; Logan, R.W.

    1983-11-01

    A repository located at Yucca Mountain at the Nevada Test Site is a potential site for permanent geological disposal of high-level nuclear waste. The repository can be located in a horizon in welded tuff, a volcanic rock, which is above the static water level at this site. The environmental conditions in this unsaturated zone are expected to be air and water vapor dominated for much of the containment period. Type 304L stainless steel is the reference material for fabricating canisters to contain the solid high-level wastes. Alternative stainless alloys are considered because of possible susceptibility of 304L to localized and stress forms of corrosion. For the reprocessed glass wastes, the canisters serve as the recipient for pouring the glass with the result that a sensitized microstructure may develop because of the times at elevated temperatures. Corrosion testing of the reference and alternative materials has begun in tuff-conditioned water and steam environments. 21 references, 8 figures, 8 tables

  7. 3D RoboMET Characterization

    Energy Technology Data Exchange (ETDEWEB)

    Madison, Jonathan D. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Susan, Donald F. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Kilgo, Alice C. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)

    2015-10-01

    The goal of this project is to generate 3D microstructural data by destructive and non-destructive means and provide accompanying characterization and quantitative analysis of such data. This work is a continuing part of a larger effort to relate material performance variability to microstructural variability. That larger effort is called “Predicting Performance Margins” or PPM. In conjunction with that overarching initiative, the RoboMET.3D™ is a specific asset of Center 1800 and is an automated serialsectioning system for destructive analysis of microstructure, which is called upon to provide direct customer support to 1800 and non-1800 customers. To that end, data collection, 3d reconstruction and analysis of typical and atypical microstructures have been pursued for the purposes of qualitative and quantitative characterization with a goal toward linking microstructural defects and/or microstructural features with mechanical response. Material systems examined in FY15 include precipitation hardened 17-4 steel, laser-welds of 304L stainless steel, thermal spray coatings of 304L and geological samples of sandstone.

  8. Progress report on the influence of higher interpass temperatures on the integrity of austenitic stainless steel welded joints

    Energy Technology Data Exchange (ETDEWEB)

    Yarmuch, M.; Choi, L. [Alberta Research Council, Edmonton, AB (Canada); Armstrong, K.; Radu, I. [PCL Industrial Constructors Inc., Nisku, AB (Canada)

    2008-07-01

    This report discussed the progress of the Welding Productivity Group (TWPG) interpass temperature assessment project (ITAP). The project was initiated to evaluate the influence of interpass temperatures on the metallurgical, corrosive, and mechanical properties of austenitic stainless steel, carbon steel, and low-alloy pressure weldments. To date, the project has conducted experiments to determine if interpass temperatures in austenitic stainless steel weldments are higher than temperatures recommended by API requirements. Elevated interpass temperatures for various base materials have been evaluated. Preliminary metallurgical, mechanical, and laboratory corrosion data from 3 experiments with 304/304L and 316/316L stainless steel weldment test specimens has shown that no significant changes occur as a result of elevated interpass temperatures. Results from side bend specimens have demonstrated that elevated interpass temperatures produce acceptable weldment ductility. No intergranular cracking was observed during oxalic acid etch tests conducted for the 316/316L samples. Huey tests performed on the 304/304L specimens indicated that elevated interpass temperatures did not adversely affect the intergranular corrosion resistance of weldments with less than 3 weld passes. Huey tests performed on the 316 specimens showed a marked increase in corrosion rates and normalized weight losses. It was concluded that rates of attack correlate with the maximum interpass temperature and not the average weld metal ferrite number. 22 refs., 11 tabs., 12 figs.

  9. Multi-Function Waste Tank Facility Corrosion Test Report (Phase 1)

    International Nuclear Information System (INIS)

    Carlos, W. C.; Fritz, R. L.

    1993-01-01

    This report documents the results of the corrosion tests that were performed to aid in the selection of the construction materials for multi-function waste tanks to be built in the U.S. Department of Energy Hanford Site. Two alloys were tested: 304L and Alloy 20 austenitic stainless steel. The test media were aqueous solutions formulated to represent the extreme of the chemical compositions of waste to be stored in the tanks. The results summerized by alloy are as follows: For 304L the tests showed no stress-corrosion cracking in any of the nine test solutions. The tests showed pitting in on of the solutions. There were no indications of any weld heat-tint corrosion, nor any sign of preferential corrosion in the welded areas. For Alloy 20 the tests showed no general, pitting, or stress-corrosion cracking. One crevice corrosion coupon cracked at the web between a hole and the edge of the coupon in one of the solutions. Mechanical tests showed some possible crack extension in the same solution. Because of the failure of both alloys to meet test acceptance criteria, the tank waste chemistry will have to be restricted or an alternative alloy tested

  10. Compatibility of potential containment materials with molten lithium hydride at 800 C

    International Nuclear Information System (INIS)

    Pawel, S.J.

    1993-01-01

    A series of compatibility experiments has been performed for several stainless steels, carbon steels, and a nickel-base alloy in molten lithium hydride at 800 C for comparison with previous experiments on type 304L stainless steel. The results indicate that the mechanism of corrosion is the same for each of 304L, 304, 316L, and 309 stainless steel and that very similar corrosion in molten LiH is expected for each stainless alloy. Deviation from parabolic kinetics at extended exposure time for each stainless alloy is attributed in part to weight gains associated with lithium penetration. Stabilized (Nb and Ti) low carbon (< 0.06%) steels are observed to be essentially inert in LiH at 800 C with stable carbides and no grain growth. Mild steel (type 1020) is decarburized rapidly and exhibits extensive grain growth in LiH at 800 C. Both steels exhibit weight gains during exposure to molten LiH that are also related in part to lithium penetration. Alloy X (UNS N06002) exhibits extreme corrosion with essentially linear kinetics and dissolution of nickel sufficient to form subsurface voids. (orig.)

  11. The Aqueous Electrochemical Response of TiC–Stainless Steel Cermets

    Directory of Open Access Journals (Sweden)

    Chukwuma Onuoha

    2018-05-01

    Full Text Available A family of TiC–stainless steel ceramic–metal composites, or cermets, has been developed in the present study, using steel grades of 304 L, 316 L, or 410 L as the binder phase. Melt infiltration was used to prepare the cermets, with the steel binder contents varying between 10–30 vol. %. The corrosion behaviour was evaluated using a range of electrochemical techniques in an aqueous solution containing 3.5 wt. % NaCl. The test methods included potentiodynamic, cyclic, and potentiostatic polarisation. The corroded samples were subsequently characterised using scanning electron microscopy (SEM and energy dispersive X-ray spectroscopy (EDS, while the post-corrosion solutions were analysed using inductively coupled plasma optical emission spectroscopy (ICP-OES to determine the residual ionic and particulate material removed from the cermets during electrochemical testing. It was demonstrated that the corrosion resistance was enhanced through decreasing the steel binder content, which arises due to the preferential dissolution of the binder phase, while the TiC ceramic remains largely unaffected. Increasing corrosion resistance was observed in the sequence TiC-304 L > TiC-316 L > TiC-410 L.

  12. Effect of welding structure and δ-ferrite on fatigue properties for TIG welded austenitic stainless steels at cryogenic temperatures

    Science.gov (United States)

    Yuri, Tetsumi; Ogata, Toshio; Saito, Masahiro; Hirayama, Yoshiaki

    2000-04-01

    High-cycle and low-cycle fatigue properties of base and weld metals for SUS304L and SUS316L and the effects of welding structure and δ-ferrite on fatigue properties were investigated at cryogenic temperatures in order to evaluate the long-life reliability of the structural materials to be used in liquid hydrogen supertankers and storage tanks and to develop a welding process for these applications. The S-N curves of the base and weld metals shifted towards higher levels, i.e., the longer life side, with decreasing test temperatures. High-cycle fatigue tests demonstrated the ratios of fatigue strength at 10 6 cycles to tensile strength of the weld metals to be 0.35-0.7, falling below those of base metals with decreasing test temperatures. Fatigue crack initiation sites in SUS304L weld metals were mostly at blowholes with diameters of 200-700 μm, and those of SUS316L weld metals were at weld pass interface boundaries. Low-cycle fatigue tests revealed the fatigue lives of the weld metals to be somewhat lower than those of the base metals. Although δ-ferrite reduces the toughness of austenitic stainless steels at cryogenic temperatures, the effects of δ-ferrite on high-cycle and low-cycle fatigue properties are not clear or significant.

  13. Aerosols from metal cutting techniques typical of decommissioning nuclear facilities - experimental system for collection and characterization

    International Nuclear Information System (INIS)

    Newton, G.J.; Hoover, M.D.; Barr, E.B.; Wong, B.A.; Ritter, P.D.

    1982-01-01

    Decommissioning of radioactively contaminated sites has the potential for creating radioactive and other potentially toxic aerosols. We describe an experimental system to collect and characterize aerosols from metal cutting activities typical of those used in decommissioning of nuclear facilities. A special enclosure was designed for the experiment and consisted of a 2-in. x 4-in. stud frame with double walls of flame retardant polyethylene film. Large plexiglass windows allowed the cutting operations to be directed and filmed. Ventilation was 8500 L/min (300 CFM) exhausted through HEPA filters. Seven cutting techniques were evaluated: pipe cutter, reciprocating saw, band saw, chop saw, oxy-acetylene torch, electric arc cut rod and plasma torch. Two grinding tools were also evaluated. Materials cut were 2-, 3- and 4-in. dia schedule 40, 80 and 180 type 304L stainless steel pipe. Basic studies were done on uncontaminated pipe. Four-inch-diameter sections of schedule 180 type 304L stainless steel pipe with radioactively contaminated internal surfaces were also cut. The experiments controlled important variables including tools, cutting technique, and type and thickness of material. 15 references, 4 figures, 2 tables

  14. Thermal reliability test of Al-34%Mg-6%Zn alloy as latent heat storage material and corrosion of metal with respect to thermal cycling

    International Nuclear Information System (INIS)

    Sun, J.Q.; Zhang, R.Y.; Liu, Z.P.; Lu, G.H.

    2007-01-01

    The purpose of this study is to determine the thermal reliability and corrosion of the Al-34%Mg-6%Zn alloy as a latent heat energy storage material with respect to various numbers of thermal cycles. The differential scanning calorimeter (DSC) analysis technique was applied to the alloy after 0, 50, 500 and 1000 melting/solidification cycles in order to measure the melting temperatures and the latent heats of fusion of the alloy. The containment materials were stainless steel (SS304L), carbon steel (steel C20) in the corrosion tests. The DSC results indicated that the change in melting temperature for the alloy was in the range of 3.06-5.3 K, and the latent heat of fusion decreased 10.98% after 1000 thermal cycles. The results show that the investigated Al-34%Mg-6%Zn alloy has a good thermal reliability as a latent heat energy storage material with respect to thermal cycling for thermal energy storage applications in the long term in view of the small changes in the latent heat of fusion and melting temperature. Gravimetric analysis as mass loss (mg/cm 2 ), corrosion rate (mg/day) and a microscopic or metallographic investigation were performed for corrosion tests and showed that SS304L may be considered a more suitable alloy than C20 in long term thermal storage applications

  15. Prevention for possible microbiologically influenced corrosion (MIC) in RHLWE flush water system

    International Nuclear Information System (INIS)

    Hsu, T.C.; Jenkins, C.F.

    1995-01-01

    This report is in response to the request to provide a recommendation for the prevention of possible microbiologically influenced corrosion (MIC) for the RHLWE (Replacement High-Level Waste Evaporator) flush water (FW) system. The recent occurrences of MIC at DWPF prompted HLWE to evaluate the possibility of MIC occurring in this 304L stainless steel RHLWE flush water system. Concern was heightened by the fact that the well water used and the other conditions at H-Tank Farm are similar to those at DWPF. However, only one known leak has occurred in the existing 304L evaporator flush water systems in either tank farm (in 1H system), and no MIC Corrosion has been confirmed in the tank farm area. The design of the RHLWE flush water system (completed long before the occurrence of MIC at DWPF) was modeled after the existing evaporator flush water systems and did not specifically include MIC prevention considerations. Therefore, MIC prevention was not specifically considered during the design phase of this flush water system. The system is presently being installed. After an extensive evaluation, a task team concluded that the best biocide to prevent the occurrence of MIC would be NaOH at fairly low concentration. Sodium hydroxide (NaOH) is optimal in this application, because of its effectiveness, low cost, and familiarity to the Operations personnel (see Appendix A). However, it is the opinion of the task group that application should be withheld until MIC corrosion is demonstrated in the system

  16. SRL canister impact tests

    International Nuclear Information System (INIS)

    Kelker, J.W. Jr.

    1986-05-01

    The Defense Waste Processing Facility (DWPF) is being constructed at the SRP for the containerization of high-level nuclear waste as a waste form for eventual permanent disposal. The waste will be incorporated in molten glass and solidified in Type 304L stainless steel canisters 2 feet in diameter x 9 feet 10 inches long. The canisters have a minimum wall thickness of 3/8 inch. Over a three-year period, nineteen drop-tests of nine canisters, filled with simulated waste glass, were made in support of the DWPF containerization program. Eight of the canister evaluation tests were of Type 304L stainless steel material and one was of commercially pure titanium. Three different length (9.44, 5.06, and 7.88 inch) nozzle configurations containing final closure upset welds were evaluated for the stainless steel canisters. All impact tests of the stainless steel canisters, which included bottom-, side-, and top-drops, were acceptable. The bottom-drop test of the titanium canister, which contained a final closure upset weld, was acceptable; however, the top-drop resulted in a breaching of the top head where it joins the nozzle. The final closure titanium upset weld was acceptable. The titanium canister wall thickness was 1/4 inch

  17. Post-test evaluations of Waste Isolation Pilot Plant - Savannah River simulated defense HLW canisters and waste form

    International Nuclear Information System (INIS)

    Molecke, M.A.; Sorensen, N.R.; Harbour, J.R.; Ferrara, D.M.

    1993-01-01

    Eighteen nonradioactive defense high-level waste (DHLW) canisters were emplaced in and subjected to accelerated overtest thermal conditions for about three years at the bedded salt Waste Isolation Pilot Plant (WIPP) facility. Post-test laboratory corrosion results of several stainless steel 304L waste canisters, cast steel overpacks, and associated instruments ranged from negligible to moderate. We found appreciable surface corrosion and corrosion products on the cast steel overpacks. Pieces of both 304L and 316 stainless steel test apparatus underwent extensive stress-corrosion cracking failure and nonuniform attack. One of the retrieved test packages contained nonradioactive glass waste form from the Savannah River Site. We conducted post-test analyses of this glass to determine the degree of resultant glass fracturing, and whether any respirable fines were present. Linear glass fracture density ranged from about 1 to 8 fractures intersecting every 5 cm (2 inch) segment along a diameter line of the canister cross-section. Glass fines between 1 and 10 microns in diameter were detected, but were not quantified

  18. Container materials in environments of corroded spent nuclear fuel

    Science.gov (United States)

    Huang, F. H.

    1996-07-01

    Efforts to remove corroded uranium metal fuel from the K Basins wet storage to long-term dry storage are underway. The multi-canister overpack (MCO) is used to load spent nuclear fuel for vacuum drying, staging, and hot conditioning; it will be used for interim dry storage until final disposition options are developed. Drying and conditioning of the corroded fuel will minimize the possibility of gas pressurization and runaway oxidation. During all phases of operations the MCO is subjected to radiation, temperature and pressure excursions, hydrogen, potential pyrophoric hazard, and corrosive environments. Material selection for the MCO applications is clearly vital for safe and efficient long-term interim storage. Austenitic stainless steels (SS) such as 304L SS or 316L SS appear to be suitable for the MCO. Of the two, Type 304L SS is recommended because it possesses good resistance to chemical corrosion, hydrogen embrittlement, and radiation-induced corrosive species. In addition, the material has adequate strength and ductility to withstand pressure and impact loading so that the containment boundary of the container is maintained under accident conditions without releasing radioactive materials.

  19. Mass production of multi-wall carbon nanotubes by metal dusting process with high yield

    International Nuclear Information System (INIS)

    Ghorbani, H.; Rashidi, A.M.; Rastegari, S.; Mirdamadi, S.; Alaei, M.

    2011-01-01

    Research highlights: → Synthesis of carbon nanotubes over Fe-Ni nanoparticles supported alloy 304L. → Production of carbon nanotubes with high yield (700-1000%) and low cost catalyst. → Optimum growth condition is CO/H 2 = 1/1, 100 cm 3 /min, at 620 o C under long term repetitive thermal cycling. → Possibility of the mass production by metal dusting process with low cost. -- Abstract: Carbon nanotube materials were synthesized over Fe-Ni nanoparticles generated during disintegration of the surface of alloy 304L under metal dusting environment. The metal dusting condition was simulated and optimized through exposing stainless steel samples during long term repetitive thermal cycling in CO/H 2 = 1/1, total gas flow rate 100 cm 3 /min, at 620 o C for 300 h. After reaction, surface morphology of the samples and also carbonaceous deposition which had grown on sample surfaces were examined by stereoscopy, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Results revealed that multi-wall carbon nanotubes could be formed over nanocatalyst generated on the alloy surface by exploiting metal dusting process. By optimization of reaction parameters the yields of carbon nanotube materials obtained were 700-1000%. Also it has been shown herein that the amount of carbon nanotube materials remarkably increases when the reaction time is extended up to 300 h, indicating a possibility of the mass production by this easy method.

  20. Corrosion behaviour of dissimilar welds between ferritic-martensitic stainless steel and austenitic stainless steel from secondary circuit of CANDU NPP

    International Nuclear Information System (INIS)

    Popa, L.; Fulger, M.; Tunaru, M.; Velciu, L.; Lazar, M.

    2016-01-01

    Corrosion damages of welds occur in spite of the fact that the proper base metal and filler metal have been correctly selected, industry codes and standards have been followed and welds have been realized with full weld penetration and have proper shape and contour. In secondary circuit of a Nuclear Power Station there are some components which have dissimilar welds. The principal criteria for selecting a stainless steel usually is resistance to corrosion, and white most consideration is given to the corrosion resistance of the base metal, additional consideration should be given to the weld metal and to the base metal immediately adjacent to the weld zone. Our experiments were performed in chloride environmental on two types of samples: non-welded (410 or W 1.4006 ferritic-martensitic steel and 304L or W 1.4307 austenitic stainless steel) and dissimilar welds (dissimilar metal welds: joints between 410 ferritic-martensitic and 304L austenitic stainless steel). To evaluate corrosion susceptibility of dissimilar welds was used electrochemical method (potentiodynamic method) and optic microscopy (microstructural analysis). The present paper follows the localized corrosion behaviour of dissimilar welds between austenitic stainless steel and ferritic-martensitic steel in solutions containing chloride ions. It was evaluated the corrosion rates of samples (welded and non-welded) by electrochemical methods. (authors)

  1. Corrosion of stainless steels in lead-bismuth eutectic up to 600 deg. C

    International Nuclear Information System (INIS)

    Soler, L.; Martin, F.J.; Hernandez, F.; Gomez-Briceno, D.

    2004-01-01

    An experimental program has been carried out to understand the differences in the corrosion behaviour between different stainless steels: the austenitic steels 304L and 316L, the martensitic steels F82Hmod, T91 and EM10, and the low alloy steel P22. The influence of oxygen level in Pb-Bi, temperature and exposure time is studied. At 600 deg. C, the martensitic steels and the P22 steel exhibit thick oxide scales that grow with time, following a linear law for the wet environment and a parabolic law for the dry one. The austenitic stainless steels show a better corrosion behaviour, especially AISI 304L. Under reducing conditions, the steels exhibit dissolution, more severe for the austenitic stainless steels. At 450 deg. C, all the materials show an acceptable behaviour provided a sufficient oxygen level in the Pb-Bi. At reducing conditions, the martensitic steels and the P22 steel have a good corrosion resistance, while the austenitic steels exhibit already dissolution at the longer exposures

  2. Fiscal 1997 survey report. Subtask 6 (hydrogen utilization worldwide clean energy system technology) (WE-NET) (development of technology of low temperature materials); 1997 nendo seika hokokusho. Suiso riyo kokusai clean energy system gijutsu (WE-NET) subtask 6 teion zairyo gijutsu no kaihatsu

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    1998-03-01

    The paper described the results of the development of technology of low temperature materials in the fiscal 1997 WE-NET. Using experimental equipment for materials under the atmosphere of liquid hydrogen, an experiment on mechanical characteristics under the liquid hydrogen atmosphere (20K) was conducted of the base materials of candidate steels (SUS304L, SUS316L and A5083). In material evaluation experiments (tension/fracture toughness/fracture tests), characteristic behaviors of the materials were shown which are different from those shown in the environment of liquid He (4k), etc. Even if the amount of {delta} ferrite in the metal welded of the stainless steel is small, approximately 1%, the degradation of low temperature toughness occurred. Welded joints of stainless steel by submerged arc welding and MAG welding were in now way inferior in tension characteristic to those by TIG welding, but were inferior in toughness ranging from room temperature to extremely low temperature. As to aluminum alloys, materials excellent in extremely-low temperature toughness were able to be found. Under the low temperature hydrogen gas atmosphere, the lower the strain rate is, the higher the hydrogen brittleness susceptibility is around 220K (extremely large hydrogen brittleness temperature) (SUS304L). In the hydrogen gas of 100 atm, hydrogen invades the material at 100degC, but does not at 77k. 38 refs., 173 figs., 48 tabs.

  3. Utilizing clad piping to improve process plant piping integrity, reliability, and operations

    International Nuclear Information System (INIS)

    Chakravarti, B.

    1996-01-01

    During the past four years carbon steel piping clad with type 304L (UNS S30403) stainless steel has been used to solve the flow accelerated corrosion (FAC) problem in nuclear power plants with exceptional success. The product is designed to allow ''like for like'' replacement of damaged carbon steel components where the carbon steel remains the pressure boundary and type 304L (UNS S30403) stainless steel the corrosion allowance. More than 3000 feet of piping and 500 fittings in sizes from 6 to 36-in. NPS have been installed in the extraction steam and other lines of these power plants to improve reliability, eliminate inspection program, reduce O and M costs and provide operational benefits. This concept of utilizing clad piping in solving various corrosion problems in industrial and process plants by conservatively selecting a high alloy material as cladding can provide similar, significant benefits in controlling corrosion problems, minimizing maintenance cost, improving operation and reliability to control performance and risks in a highly cost effective manner. This paper will present various material combinations and applications that appear ideally suited for use of the clad piping components in process plants

  4. A study on the corrosion test of equipment material handling hot molten salt

    International Nuclear Information System (INIS)

    Ro, Seung Gy; Jeong, M.S.; Hong, S.S.; Cho, S.H.; Shin, Y.J.; Park, H.S.; Zhang, J.S.

    1999-02-01

    On this technical report, corrosion behavior of austenitic stainless steels of SUS 316L and SUS 304L in molten salt of LiCl-Li 2 O has been investigated in the temperature range of 650 - 850 dg C. Corrosion products of SUS 316L in molten salt consisted of two layers, an outer layer of LiCrO 2 and inner layer of Cr 2 O 3 .The corrosion layer was uniform in molten salt of LiCl, but the intergranular corrosion occurred in addition to the uniform corrosion in mixed molten salt of LiCl-Li 2 O. The corrosion rate increased slowly with the increase of temperature up to 750 dg C, but above 750 dg C rapid increase in corrosion rate observed. SUS 316L stainless steel showed slower corrosion rate and higher activation energy for corrosion than SUS 304L, exhibiting higher corrosion resistance in the molten salt. In heat-resistant alloy, dense protective oxide scale of LiCrO 2 was formed in molten salt of LiCl. Whereas in mixed molten salt of LiCl-Li 2 O, porous non-protective scale of Li(Cr, Ni, Fe)O 2 was formed. (Author). 44 refs., 4 tabs., 16 figs

  5. Analysis of factors influencing the reliability of retrievable storage canisters for containment of solid high-level radioactive waste

    International Nuclear Information System (INIS)

    Mecham, W.J.; Seefeldt, W.B.; Steindler, M.J.

    1976-08-01

    The reliability of stainless steel type 304L canisters for the containment of solidified high-level radioactive wastes in the glass and calcine forms was studied. A reference system, drawn largely from information furnished by Battelle Northwest Laboratories and Atlantic Richfield Hanford Company is described. Operations include filling the canister with the appropriate waste form, interim storage at a reprocessing plant, shipment in water to a Retrievable Surface Storage Facility (RSSF), interim storage at the RSSF, and shipment to a final disposal facility. The properties of stainless steel type 304L, fission product oxides, calcine, and glass were reviewed, and mechanisms of corrosion were identified and studied. The modes of corrosion important for reliability were stress-corrosion cracking, internal pressurization of the canister by residual impurities present, intergranular attack at the waste-canister interface, and potential local effects due to migration of fission products. The key role of temperature control throughout canister lifetime is considered together with interactive effects. Methods of ameliorating adverse effects and ensuring high reliability are identified and described. Conclusions and recommendations are presented

  6. Characterization of ion irradiation effects on the microstructure, hardness, deformation and crack initiation behavior of austenitic stainless steel:Heavy ions vs protons

    Science.gov (United States)

    Gupta, J.; Hure, J.; Tanguy, B.; Laffont, L.; Lafont, M.-C.; Andrieu, E.

    2018-04-01

    Irradiation Assisted Stress Corrosion Cracking (IASCC) is a complex phenomenon of degradation which can have a significant influence on maintenance time and cost of core internals of a Pressurized Water Reactor (PWR). Hence, it is an issue of concern, especially in the context of lifetime extension of PWRs. Proton irradiation is generally used as a representative alternative of neutron irradiation to improve the current understanding of the mechanisms involved in IASCC. This study assesses the possibility of using heavy ions irradiation to evaluate IASCC mechanisms by comparing the irradiation induced modifications (in microstructure and mechanical properties) and cracking susceptibility of SA 304 L after both type of irradiations: Fe irradiation at 450 °C and proton irradiation at 350 °C. Irradiation-induced defects are characterized and quantified along with nano-hardness measurements, showing a correlation between irradiation hardening and density of Frank loops that is well captured by Orowan's formula. Both irradiations (iron and proton) increase the susceptibility of SA 304 L to intergranular cracking on subjection to Constant Extension Rate Tensile tests (CERT) in simulated nominal PWR primary water environment at 340 °C. For these conditions, cracking susceptibility is found to be quantitatively similar for both irradiations, despite significant differences in hardening and degree of localization.

  7. A study for anticorrosion and tribological behaviors of thin/thick diamond-like carbon films in seawater

    Science.gov (United States)

    Ye, Yewei; Jia, Shujuan; Zhang, Dawei; Liu, Wei; Zhao, Haichao

    2018-03-01

    The thin and thick diamond-like carbon (DLC) films were prepared by unbalanced magnetron sputtering technique on 304L stainless steels and (100) silicon wafers. Microstructure, mechanical, corrosion and tribological properties were systematically investigated by SEM, Raman, nanoindenter, scratch tester, modulab electrochemical workstation and R-tec multifunctional tribological tester. Results showed that the adhesion force presented a descending trend with the growth in soaking time. The adhesion force of the thin DLC film with h