  1. Alkali binding in hydrated Portland cement paste

    NARCIS (Netherlands)

    Chen, W.; Brouwers, H.J.H.

    2010-01-01

    The alkali-binding capacity of C–S–H in hydrated Portland cement pastes is addressed in this study. The amount of bound alkalis in C–S–H is computed based on the alkali partition theories firstly proposed by Taylor (1987) and later further developed by Brouwers and Van Eijk (2003). Experimental data

  2. Hydration process in Portland cement blended with activated coal gangue

    Institute of Scientific and Technical Information of China (English)

    Xian-ping LIU; Pei-ming WANG; Min-ju DING

    2011-01-01

    This paper deals with the hydration of a blend of Portland cement and activated coal gangue in order to determine the relationship between the degree of hydration and compressive strength development.The hydration process was investigated by various means:isothermal calorimetry,thermal analysis,non-cvaporable water measurement,and X-ray diffraction analysis.The results show that the activated coal gangue is a pozzolanic material that contributes to the hydration of the cement blend.The pozzolanic reaction occurs over a period of between 7 and 90 d,consuming portlandite and forming both crystal hydrates and ill-crystallized calcium silicate hydrates.These hydrates are similar to those found in pure Portland cement.The results show that if activated coal gangue is substituted for cement at up to 30% (w/w),it does not significantly affect the final compressive strength of the blend.A long-term compressive strength improvement can in fact be achieved by using activated coal gangue as a supplementary cementing material.The relationship between compressive strength and degree of hydration for both pure Portland cement and blended cement can be described with the same equation.However,the parameters are different since blended cement produces fewer calcium silicate hydrates than pure Portland cement at the same degree of hydration.

  3. Influence of Cellulose Ethers on Hydration Products of Portland Cement

    Institute of Scientific and Technical Information of China (English)

    MA Baoguo; OU Zhihua; JIAN Shouwei; XU Rulin

    2011-01-01

    Cellulose ethers are widely used to mortar formulations, and it is significant to understand the interaction between cellulose ethers and cement pastes. FT-IR spectra, thermal analysis and SEM are used to investigate hydration products in the cement pastes modified by HEMC and HPMC in this article. The results show that the hydration products in modified cement pastes were finally identical with those in the unmodified cement paste, but the major hydration products, such as CH (calcium hydroxide), ettringite and C-S-H, appeared later in the modified cement pastes than in the unmodified cement paste. The cellulose ethers decrease the outer products and increase inner products of C-S-H gels. Compared to unmodified cement pastes, no new products are found in the modified cement pastes in the present experiment. The HEMC and HPMC investigation shows almost the same influence on the hydration products of Portland cement.

  4. Hydration of Portland cement with additions of calcium sulfoaluminates

    Energy Technology Data Exchange (ETDEWEB)

    Le Saout, Gwenn, E-mail: gwenn.le-saout@mines-ales.fr [Empa, Swiss Federal Laboratories for Materials Science and Technology, Concrete and Construction Chemistry Laboratory, Ueberlandstrasse 129, CH-8600 Duebendorf (Switzerland); Lothenbach, Barbara [Empa, Swiss Federal Laboratories for Materials Science and Technology, Concrete and Construction Chemistry Laboratory, Ueberlandstrasse 129, CH-8600 Duebendorf (Switzerland); Hori, Akihiro [DENKA Chemicals GmbH, Wehrhahn-Center, Cantadorstr. 3, D-40211 Duesseldorf (Germany); Higuchi, Takayuki [Denki Kagaku Kogyo Kabushiki Kaisha (DENKA), Omi, Itoigawa, Niigata, 949-0393 (Japan); Winnefeld, Frank [Empa, Swiss Federal Laboratories for Materials Science and Technology, Concrete and Construction Chemistry Laboratory, Ueberlandstrasse 129, CH-8600 Duebendorf (Switzerland)

    2013-01-15

    The effect of mineral additions based on calcium aluminates on the hydration mechanism of ordinary Portland cement (OPC) was investigated using isothermal calorimetry, thermal analysis, X-ray diffraction, scanning electron microscopy, solid state nuclear magnetic resonance and pore solution analysis. Results show that the addition of a calcium sulfoaluminate cement (CSA) to the OPC does not affect the hydration mechanism of alite but controls the aluminate dissolution. In the second blend investigated, a rapid setting cement, the amorphous calcium aluminate reacts very fast to ettringite. The release of aluminum ions strongly retards the hydration of alite but the C-S-H has a similar composition as in OPC with no additional Al to Si substitution. As in CSA-OPC, the aluminate hydration is controlled by the availability of sulfates. The coupling of thermodynamic modeling with the kinetic equations predicts the amount of hydrates and pore solution compositions as a function of time and validates the model in these systems.

  5. Advances in understanding hydration of Portland cement

    Energy Technology Data Exchange (ETDEWEB)

    Scrivener, Karen L., E-mail: Karen.scrivener@epfl.ch [Laboratory of Construction Materials, Ecole Polytechnique Fédérale de Lausanne, 1015 (Switzerland); Juilland, Patrick [Sika Technology AG, Zürich (Switzerland); Monteiro, Paulo J.M. [Department of Civil and Environmental Engineering, University of California at Berkeley (United States)

    2015-12-15

    Progress in understanding hydration is summarized. Evidence supports the geochemistry dissolution theory as an explanation for the induction period, in preference to the inhibiting layer theory. The growth of C–S–H is the principal factor controlling the main heat evolution peak. Electron microscopy indicates that C–S–H “needles” grow from the surface of grains. At the peak, the surface is covered, but deceleration cannot be attributed to diffusion control. The shoulder peak comes from renewed reaction of C{sub 3}A after depletion of sulfate in solution, but release of sulfate absorbed on C–S–H means that ettringite continues to form. After several days space becomes the major factor controlling hydration. The use of new analytical technique is improving our knowledge of the action of superplasticizers and leading to the design of molecules for different applications. Atomistic modeling is becoming a topic of increasing interest. Recent publications in this area are reviewed.

  6. Portland cement hydration in the presence of admixtures: black gram pulse and superplasticizer

    Directory of Open Access Journals (Sweden)

    Viveka Nand Dwivedi

    2008-12-01

    Full Text Available Effect of admixtures such as black gram pulse (BGP and sulfonated naphthalene based superplasticizer (SP on the hydration of Portland cement has been studied. The hydration characteristics of OPC in the presence of BGP and SP were studied with the help of non evaporable water content determinations, calorimetric method, Mössbauer spectroscopic and atomic force microscopic techniques. Results have shown that both BGP and SP get adsorbed at the surface of cement and its hydration products. The hydration of Portland cement is retarded in the presence of both the admixtures and nanosize hydration products are formed.

  7. Hydration study of ordinary portland cement in the presence of zinc ions

    Directory of Open Access Journals (Sweden)

    Monica Adriana Trezza

    2007-12-01

    Full Text Available Hydration products of Portland cement pastes, hydrated in water and in the presence of zinc ions were studied comparatively at different ages. Hydration products were studied by X ray diffractions (XRD and infrared spectroscopy (IR. Although IR is not frequently used in cement chemistry, it evidenced a new phase Ca(Zn(OH32. 2H2O formed during cement hydration in the presence of zinc. The significant retardation of early cement hydration in the presence of zinc is assessed in detail by differential calorimetry as a complement to the study carried out by IR and XRD, providing evidence that permits to evaluate the kinetic of the early hydration.

  8. Effect of three natural pozzolans in portland cement hydration

    Directory of Open Access Journals (Sweden)

    Rahhal, V.

    2003-03-01

    Full Text Available Natural pozzolans have been used since ancient times and continues to be used today. The chemistry and morphological composition of natural pozzolans and their particle size distribution allows classifying them as more or less reactive pozzolan. In this research several techniques have been used to study the influence of pozzolan on portland cement hydration as much as to evaluate the mechanical and durable properties of concretes, mortars and pastes containing pozzolans. This paper describes the effect of incorporating three natural pozzolans to two cements with very different mineralogical composition. The techniques used were: conduction calorimetry and Fratini test. Results proved that pozzolanic activity and the acceleration and retardation of hydration reaction depend on the mineralogical composition of the portland cernent used. Effects of dilution, stimulation, acceleration or retardation reactions, behavior into areas of heat dissipation and pozzolanic activity depend on the percentage of pozzolan used and the age in which it has been analyzed.

    El uso de las puzolanas naturales se remonta a la antigüedad, no obstante, actualmente continúa su utilización. La composición química y morfológica de las puzolanas naturales, sumado al tamaño de sus partículas, las califican como más o menos reactivas. En el estudio de las mismas, se han aplicado variadas técnicas para el análisis de sus interferencias en las reacciones de hidratación de los cementos portland; así como para la evaluación de las propiedades resistentes y duraderas que pueden conferirle a los hormigones, morteros o pastas de los que formen parte. Este trabajo versará sobre los efectos que produce la incorporación de tres puzolanas naturales a dos cementos portland de muy diferente composición mineralógica. Las técnicas aplicadas para su estudio han sido: la calorimetría de conducción y el ensayo de Fratini. Los resultados obtenidos permiten determinar

  9. Hydration Study of Ordinary Portland Cement in the Presence of Lead(II) Oxide

    OpenAIRE

    Barbir, D.; Dabić, P.; Krolo, P.

    2013-01-01

    The aim of this work was to investigate the effect of the addition of lead(II) oxide on hydration heat and specific conductivity of a CEM I Portland cement. The heat released during hydration was determined by differential microcalorimetry up to 48 hours of hydration and the specific conductivity by a digital conductometer. Thermogravimetric analysis was employed in the characterization of the cement structure. The hydration heat results show that the addition of lead(II) oxide affects the...

  10. Portland cement hydration in the presence of admixtures: black gram pulse and superplasticizer

    OpenAIRE

    Viveka Nand Dwivedi; Shiva Saran Das; Nakshatra Bahadur Singh; Sarita Rai; Namdev Shriram Gajbhiye

    2008-01-01

    Effect of admixtures such as black gram pulse (BGP) and sulfonated naphthalene based superplasticizer (SP) on the hydration of Portland cement has been studied. The hydration characteristics of OPC in the presence of BGP and SP were studied with the help of non evaporable water content determinations, calorimetric method, Mössbauer spectroscopic and atomic force microscopic techniques. Results have shown that both BGP and SP get adsorbed at the surface of cement and its hydration products. Th...

  11. Research on the nanolevel influence of surfactants on structure formation of the hydrated Portland cement compositions

    Directory of Open Access Journals (Sweden)

    Guryanov Alexander

    2016-01-01

    Full Text Available The research of the structure formation process on a nanolevel of the samples of hydrated Portland cement compositions containing the modifying additives has been conducted with the help of small angle neutron scattering method. Carbonate and aluminum alkaline slimes as well as the complex additives containing surfactants were used as additives. The influence of slimes and surfactants on structural parameters change of Portland cement compositions of the average size of the disseminating objects, fractal dimension samples is considered. These Portland cement compositions are shown to be fractal clusters.

  12. Hydration of Blended Portland Cements Containing Calcium-Aluminosilicate Glass Powder and Limestone

    DEFF Research Database (Denmark)

    Moesgaard, Mette; Poulsen, S.L.; Herfort, D.

    2012-01-01

    in an accelerated hydration for alite (Ca3SiO5), the main constituent of Portland cement. A higher degree of limestone reaction has been observed in the blend containing both limestone and NCAS glass as compared to the limestone – Portland mixture. This reflects that limestone reacts with a part of the alumina......This work investigates the hydration of blended Portland cement containing 30 wt.% Na2O-CaO-Al2O3-SiO2 (NCAS) glass particles either as the only supplementary cementitious material (SCM) or in combination with limestone, using 29Si MAS NMR, powder XRD, and thermal analyses. The NCAS glass...... represents a potential alternative to traditional SCMs, used for reduction of the CO2 emission associated with cement production. It is found that the NCAS glass takes part in the hydration reactions after about two weeks of hydration and a degree of reaction of approx. 50 % is observed after 90 days...

  13. Effect of Fine Steel Slag Powder on the Early Hydration Process of Portland Cement

    Institute of Scientific and Technical Information of China (English)

    2006-01-01

    Hydration heat evolution, non-evaporative water, setting time and SEM tests were performed to investigate the effect of fine steel slag powder on the hydration process of Portland cement and its mechanism.The results show that the effect of fine steel slag powder on the hydration process of Portland cement is closely related to its chemical composition, mineral phases, fineness, etc.Fine steel slag powder retards the hydration of portland cement at early age.The major reason for this phenomenon is the relative high content of MgO , MnO2, P2 O5in steel slag, and MgO solid solved in C3 S contained in steel slag.

  14. Hydration of Blended Portland Cements Containing Calcium-Aluminosilicate Glass Powder and Limestone

    DEFF Research Database (Denmark)

    Moesgaard, M; Poulsen, Søren Lundsted; Herfort, D;

    2012-01-01

    M. MOESGAARD, S.L. POULSEN, D. HERFORT, M. STEENBERG, L.F. KIRKEGAARD, J. SKIBSTED, Y. YUE, Hydration of Blended Portland Cements Containing Calcium-Aluminosilicate Glass Powder and Limestone, Journal of the American Ceramic Society 95, 403 – 409 (2012).......M. MOESGAARD, S.L. POULSEN, D. HERFORT, M. STEENBERG, L.F. KIRKEGAARD, J. SKIBSTED, Y. YUE, Hydration of Blended Portland Cements Containing Calcium-Aluminosilicate Glass Powder and Limestone, Journal of the American Ceramic Society 95, 403 – 409 (2012)....

  15. Model Analysis of Initial Hydration and Structure Forming of Portland Cement

    Institute of Scientific and Technical Information of China (English)

    2007-01-01

    The auto efficiently hydration heat arrangement and the non-contacting electrical resistivity device were used to test the thermology effect and the resistivity variation of Portland cement hydration.The structure forming model of Portland cement initial hydration was established through the systematical experiments with different cements, the amount of mixing water and the chemical admixture. The experimental results show that, the structure forming model of cement could be divided into three stages, i e, solution-solution equilibrium period, structure forming period and structure stabilizing period. Along with the increase of mixing water, the time of inflexion appeared is in advance for thermal process of cement hydration and worsened for the structure forming process. Comparison with the control specimen, adding Na2SO4 makes the minimum critical point lower, the flattening period shorter and the growing slope after stage one steeper. So the hydration and structure forming process of Portland cement could be described more exactly by applying the thermal model and the structure-forming model.

  16. Influence of Calcium Sulfate State and Fineness of Cement on Hydration of Portland Cements Using Electrical Measurement

    Institute of Scientific and Technical Information of China (English)

    WEI Xiaosheng; LI Zongjin; XIAO Lianzhen; THONG Wangfai

    2006-01-01

    The influence of calcium sulfate state and fineness of cement on hydration of Portland cement was studied using electrical resistivity measurement. The bulk resistivity curve of the paste from the abnormal cement mainly with hemihydrate had a characteristic abnormal peak and rapid increase in early period. The resistivity measurement technique can be used to discriminate abnormal setting. For normal cement with gypsum, the increase in fineness of the Portland cement decreases the minimum resistivity due to a higher ionic concentration and increases the 24 hour resistivity due to a reduction in macroscopic pore size. Thesetting time, compressive strength, pore structure of pastes made from different cements were carried out to compare the influence of water to cement ratio, calcium sulfate state and fineness. It is found that the electrical and mechanical properties are strongly affected by the initial porosity, the presence of hemihydrate or gypsum, and the fineness of cement.

  17. Structural Investigations of Portland Cement Components, Hydration, and Effects of Admixtures by Solid-State NMR Spectroscopy

    DEFF Research Database (Denmark)

    Skibsted, Jørgen Bengaard; Andersen, Morten D.; Jakobsen, Hans Jørgen

    2006-01-01

    Solid-state, magic-angle spinning (MAS) NMR spectroscopy represents a valuable tool for structural investigations on the nanoscale of the most important phases in anhydrous and hydrated Portland cements and of various admixtures. This is primarily due to the fact that the method reflects the first...... in the cement phases. The role of flouride ions is of special interest for mineralized Portland cements and it demonstrated that the location of these anions in anhydrous and hydrated Portland cements can be clarified using 19F MAS or 29Si{19F} CP/MAS NMR despite these cements contain only about 0.2 wt...

  18. Effect of superplasticizers on the hydration kinetic and mechanical properties of Portland cement pastes

    Directory of Open Access Journals (Sweden)

    Safaa M.A. El-Gamal

    2012-04-01

    Full Text Available Hydration of ordinary Portland cement in the presence of two different types of superplasticizers namely sodium lignosulfonate (LS and naphthalene sulfonate-formaldehyde condensate (NSF was studied using different experimental techniques. Superplasticized ordinary Portland cement pastes were prepared using the values of standard water of consistency with different additions of each type of superplasticizers used. Pastes were hydrated for different time intervals under normal curing conditions. The results reveal that both superplasticizers increase the workability and reduce the standard water of consistency. This results in an improvement in the mechanical properties of superplasticized cement pastes at all ages of the hydration–hardening process. Naphthalene sulfonate-formaldehyde condensate was found to have the higher efficiency in improving the mechanical properties of the hardened pastes than that of sodium lignosulfonate superplasticizer.

  19. CALCIUM ORTHOPHOSPHATES HYDRATES: FORMATION, STABILITY AND INFLUENCE ON STANDARD PROPERTIES OF PORTLAND CEMENT

    Directory of Open Access Journals (Sweden)

    Kaziliunas A.

    2013-12-01

    Full Text Available Preparation of phosphogypsum to produce the binders requires a much higher input than preparation of natural gypsum stone. This makes it uncompetitive material. The investigations presented therein are meant to reduce this input by looking for the ways of rendering impurities harmless. Soluble acid orthophosphates are the main harmful impurity of phosphogypsum. The studies show that dry insoluble calcium orthophosphates hydrates (1.09 % and 2.18 % P2O5 in gypsum have little effect on W/C, setting times and soundness of Portland cement pastes. Insoluble calcium orthophosphates hydrates {CaHPO4∙2H2O, Ca8(HPO42(PO44∙5H2O and Ca9(HPO4(PO45(OH∙4H2O} formed in acidic medium (pH = 4.2 - 5.9 have been destroyed in alkaline medium and reduce standard compressive strength of cement up to 28 %. Calcium orthophosphates hydrates of hydroxyapatite group are stable in alcaline medium, while in dry state they reduce the standard compressive strength of cement until 10 %, but their suspensions prolong setting times of Portland cement as soluble orthophosphates – 2 - 3 times. Alkalis in cement increase pH of paste, but do not change the process of formation of calcium orthophosphates hydrates of hydroxyapatite group: it takes place through an intermediate phase - CaHPO4·2H2O, whose transformation into apatite lasts for 2 - 3 months.

  20. Relation between the Rheology Characteristic and Initial Hydration Structure of Portland Cement

    Institute of Scientific and Technical Information of China (English)

    2006-01-01

    Based on the rheology characteristic and the resistivity variation under alternating electric-field of Portland cement hydration by means of AR2000 advanced rheometer and non-contacting electrical resistivity device, the influence of cement kinds and the chemical admixtures on the initial rheology characteristic and structure forming and developing of cement hydration was studied. The relationship between the rheology characteristic, the initial hydration structure forming and the hydration process at very early ages was analyzed by macro properties and microstructure tests. The results showed that, the storage modulus, acted as S, could be described more subtle distinction accompanying with hydration of fresh paste model at very early period. Combining the resistivity alterations, a sudden change on structure forming emerged when the hydration of cement becoming inducing age. The rheology characteristic was interrelated to the hydration structure forming, development and the physical mechanics properties. The sudden change on storage modulus moved up due to the addition of retarder, but the structure forming and developing was retarded to a certain extent.

  1. Modeling of Hydration, Compressive Strength, and Carbonation of Portland-Limestone Cement (PLC) Concrete.

    Science.gov (United States)

    Wang, Xiao-Yong

    2017-01-26

    Limestone is widely used in the construction industry to produce Portland limestone cement (PLC) concrete. Systematic evaluations of hydration kinetics, compressive strength development, and carbonation resistance are crucial for the rational use of limestone. This study presents a hydration-based model for evaluating the influences of limestone on the strength and carbonation of concrete. First, the hydration model analyzes the dilution effect and the nucleation effect of limestone during the hydration of cement. The degree of cement hydration is calculated by considering concrete mixing proportions, binder properties, and curing conditions. Second, by using the gel-space ratio, the compressive strength of PLC concrete is evaluated. The interactions among water-to-binder ratio, limestone replacement ratio, and strength development are highlighted. Third, the carbonate material contents and porosity are calculated from the hydration model and are used as input parameters for the carbonation model. By considering concrete microstructures and environmental conditions, the carbon dioxide diffusivity and carbonation depth of PLC concrete are evaluated. The proposed model has been determined to be valid for concrete with various water-to-binder ratios, limestone contents, and curing periods.

  2. Modeling of Hydration, Compressive Strength, and Carbonation of Portland-Limestone Cement (PLC Concrete

    Directory of Open Access Journals (Sweden)

    Xiao-Yong Wang

    2017-01-01

    Full Text Available Limestone is widely used in the construction industry to produce Portland limestone cement (PLC concrete. Systematic evaluations of hydration kinetics, compressive strength development, and carbonation resistance are crucial for the rational use of limestone. This study presents a hydration-based model for evaluating the influences of limestone on the strength and carbonation of concrete. First, the hydration model analyzes the dilution effect and the nucleation effect of limestone during the hydration of cement. The degree of cement hydration is calculated by considering concrete mixing proportions, binder properties, and curing conditions. Second, by using the gel–space ratio, the compressive strength of PLC concrete is evaluated. The interactions among water-to-binder ratio, limestone replacement ratio, and strength development are highlighted. Third, the carbonate material contents and porosity are calculated from the hydration model and are used as input parameters for the carbonation model. By considering concrete microstructures and environmental conditions, the carbon dioxide diffusivity and carbonation depth of PLC concrete are evaluated. The proposed model has been determined to be valid for concrete with various water-to-binder ratios, limestone contents, and curing periods.

  3. The impact of zirconium oxide radiopacifier on the early hydration behaviour of white Portland cement.

    Science.gov (United States)

    Coleman, Nichola J; Li, Qiu

    2013-01-01

    Zirconium oxide has been identified as a candidate radiopacifying agent for use in Portland cement-based biomaterials. During this study, the impact of 20 wt.% zirconium oxide on the hydration and setting reactions of white Portland cement (WPC) was monitored by powder X-ray diffraction (XRD), (29)Si and (27)Al magic angle spinning nuclear magnetic resonance spectroscopy (MAS NMR), transmission electron microscopy (TEM) and Vicat apparatus. The presence of 20 wt.% zirconium oxide particles in the size-range of 0.2 to 5 μm was found to reduce the initial and final setting times of WPC from 172 to 147 min and 213 to 191 min, respectively. Zirconium oxide did not formally participate in the chemical reactions of the hydrating cement; however, the surface of the zirconium oxide particles presented heterogeneous nucleation sites for the precipitation and growth of the early C-S-H gel products which accelerated the initial setting reactions. The presence of zirconium oxide was found to have little impact on the development of the calcium (sulpho)aluminate hydrate phases.

  4. Hydration study of mechanically activated mixtures of Portland cement and fly ash

    Directory of Open Access Journals (Sweden)

    GORDANA STEFANOVIC

    2007-06-01

    Full Text Available Fly ash (FA can be used in cement mixtures with certain limitations. The problem of the mentioned mixtures lies in the insufficient activity of the particles of FA in the reactions which are important for the establishment of the mechanical characteristics of cement. This is particularly true for the hydration reactions. As a result of this, cement pastes formed by mixing ash and clinker have worse characteristics compared to those of pure Portland cement (PC, especially in the early period of setting. As is well known, FA can be a good solution for the neutralization of the negative effects generated due to the creation of free Ca(OH2 during the hydration of PC, provided that the problems with the low activity of FAare overcome. For the experiments in this study, a mixture of Portland cement and fly ash was used, the content of ash in the mixture being 30 % and 50 %. Mechanical activation was performed in a vibrating ring mill. The goal of this study was to demonstrate, through experimental results, that during the mechanical activation of a PC and FAmixture, the components in the mixture which mostly affect the direction, rate and range of hydration reactions occurring in the mixture had been activated. The values of the compressive strength of the activated and non-activated mixtures and the changes of their specific surface area proved that during the grinding process, the mixture PC+FA had been mechanically activated. The highest increase of compressivestrength was achieved in the early period of setting, which indicates an improvement in the early hydration of the mixture. XRD, DTA and TG analyses showed that the alite (C3S and belite (C2S from the PC and a part of the fly ash were activated.

  5. WOOD PRE-TREATMENT INFLUENCE ON THE HYDRATION OF PORTLAND CEMENT IN COMBINATION WITH SOME TROPICAL WOOD SPECIES

    Directory of Open Access Journals (Sweden)

    Nusirat Aderinsola SADIKU

    2014-06-01

    Full Text Available The influence of three pre-treatment methods on the hydration characteristics of Portland cement in combination with three tropical hardwood species was investigated. The maximum hydration temperature and time to reach maximum hydration temperature were analysed for the wood-cement-water mixtures of the three species after removing inhibitory extractives of wood samples by extraction with 5% Sodium hydroxide (NaOH, cold and hot water after removing inhibitory extractives of wood samples. There were differences in the hydration reaction of the wood species with Portland cement using the different pre-treatment methods. The compatibility of the wood species with Portland cement improved following pre-treatment. Sodium hydroxide pre-treatment had the most significant effect followed by hot water. Terminalia ivorensis (Idigbo, and Antiaris africana (Oriro species showed considerable improvement in their compatibility with Portland cement at 5% Sodium hydroxide pre-treatment with maximum hydration temperature of 65oC where Arere had 60.5oC where both cold and hot water were unable to raise the hydration temperature beyond 55.5oC . This study shows that the wood species requires more than cold and hot water extraction to make them suitable for wood cement composite materials as extraction with sodium hydroxide (1% solution was found to be the most effective treatment for the wood species under investigation.

  6. Recycling of porcelain tile polishing residue in portland cement: hydration efficiency.

    Science.gov (United States)

    Pelisser, Fernando; Steiner, Luiz Renato; Bernardin, Adriano Michael

    2012-02-21

    Ceramic tiles are widely used by the construction industry, and the manufacturing process of ceramic tiles generates as a major residue mud derived from the polishing step. This residue is too impure to be reused in the ceramic process and is usually discarded as waste in landfills. But the analysis of the particle size and concentration of silica of this residue shows a potential use in the manufacture of building materials based on portland cement. Tests were conducted on cement pastes and mortars using the addition of 10% and 20% (mass) of the residue. The results of compressive strength in mortars made up to 56 days showed a significant increase in compressive strength greater than 50%. The result of thermogravimetry shows that portlandite is consumed by the cement formed by the silica present in the residue in order to form calcium silicate hydrate and featuring a pozzolanic reaction. This effect improves the performance of cement, contributes to research and application of supplementary cementitious materials, and optimizes the use of portland cement, reducing the environmental impacts of carbon dioxide emissions from its production.

  7. Hydrated Ordinary Portland Cement as a Carbonic Cement: The Mechanisms, Dynamics, and Implications of Self-Sealing and CO2 Resistance in Wellbore Cements

    Energy Technology Data Exchange (ETDEWEB)

    Guthrie, George Drake Jr. [Los Alamos National Laboratory; Pawar, Rajesh J. [Los Alamos National Laboratory; Carey, James William [Los Alamos National Laboratory; Karra, Satish [Los Alamos National Laboratory; Harp, Dylan Robert [Los Alamos National Laboratory; Viswanathan, Hari S. [Los Alamos National Laboratory

    2017-07-28

    This report analyzes the dynamics and mechanisms of the interactions of carbonated brine with hydrated Portland cement. The analysis is based on a recent set of comprehensive reactive-transport simulations, and it relies heavily on the synthesis of the body of work on wellbore integrity that we have conducted for the Carbon Storage Program over the past decade.

  8. A Comparative Study Between the Early Stages Hydration of a High Strength and Sulphate Resistant Portland Cement and the Type II F Portland Cement Through Non Conventional Differential Thermal Analysis and Thermogravimetry

    OpenAIRE

    Neves Junior,Alex; Viana,Marcelo Mendes; Dweck,Jo; Toledo Filho,Romildo Dias

    2015-01-01

    This work presents a study, which compares the early stages of hydration of a High Initial Strength and Sulphate Resistant Portland Cement (HIS SR PC) with those of Type II F Portland Cement (PC II), by Non-Conventional Differential Thermal Analysis (NCDTA) within the first 24 hours of hydration. Water/cement (w/c) ratios equal to 0.5, 0.6 and 0.66 were used to prepare the pastes. The hydration of these two types of cement was monitored on real time by NCDTA curves, through the thermal effect...

  9. Hydration kinetics for the alite, belite, and calcium aluminate phase in Portland cements from 27Al and 29Si MAS NMR spectroscopy

    DEFF Research Database (Denmark)

    Skibsted, Jørgen; Jensen, Ole Mejlhede; Jakobsen, Hans Jørgen

    1997-01-01

    29Si magic-angle spinning (MAS) NMR spectroscopy is shown to be a valuable tool for obtaining the quantities of alite and belite in hydrated Portland cements. The hydration (1-180 days) of a white Portland cement with 10 wt.% silica fume added is investigated and the degrees of hydration for alite...... belite, and silica fume are determined. It is demonstrated that 27Al MAS NMR spectra of hydrated Portland cements can give quantitative information about the formation of ettringite and the conversion of this phase to monosulphate during hydration....

  10. Combined effect of sodium sulphate and superplasticizer on the hydration of fly ash blended Portland® cement

    OpenAIRE

    Mukesh Kumar; Narendra Pratap Singh; Sanjay Kumar Singh; Nakshatra Bahadur Singh

    2010-01-01

    Combined effect of polycarboxylate type superplasticizer and sodium sulphate on the hydration of fly ash blended Portland® cement has been studied by using different techniques. Water consistency, setting times, non-evaporable water contents, water percolation, air contents, compressive strengths and expansion in corrosive atmosphere were determined. Hydration products were examined with the help of DTA and X-ray diffraction techniques. It is found that the superplasticizer reduces the pore s...

  11. Structural Investigations of Portland Cement Components, Hydration, and Effects of Admixtures by Solid-State NMR Spectroscopy

    DEFF Research Database (Denmark)

    Skibsted, Jørgen Bengaard; Andersen, Morten D.; Jakobsen, Hans Jørgen

    2006-01-01

    Solid-state, magic-angle spinning (MAS) NMR spectroscopy represents a valuable tool for structural investigations on the nanoscale of the most important phases in anhydrous and hydrated Portland cements and of various admixtures. This is primarily due to the fact that the method reflects the firs.......% flourine. Finally, the detection and quantification of strätlingite (2CaO·Al2O3·SiO2·8H2O) in Portland cement mixtures containing metakaolin will be demonstrated....

  12. Microstructure and Composition of Hydration Products of Ordinary Portland Cement with Ground Steel-making Slag

    Institute of Scientific and Technical Information of China (English)

    LI Yong-xin; CHEN Yi-min; ZHANG Hong-tao; HE Xing-yang; WEI Jiang-xiong; ZHANG Wen-sheng

    2003-01-01

    The effect of ground steel-making slag on microstructure and composition of hydration products of ordinary Portland cement (OPC) was investigated by mercury intrusion porosimetry ( MIP ), X- ray diffraction (XRD) and differential thermal analysis (DTA). Results show that ground steel-making slag is a kind of high activity mineral additives and it can raise the longer-age strength of OPC mortar. The total porosity and average pore diameter of OPC paste with groand steel-making slag increase with the increase of the amount of ground steelmaking slag replacing OPC at various ages, while after 28 days most pores in OPC paste with ground steel-making slag do not influeace the strength because the diameter of those pores is in the rang of 20 to 50nm. The hydration mechanism of ground steel-making slag is similar to that of OPC but different from that of fly ash and blast furnace slag. The hydration products of ground steel-making slag contain quite a lot of Ca( OH)2 in long age.

  13. Hydration and microstructure of Portland cement partially substituted with ultrafine silica

    Directory of Open Access Journals (Sweden)

    Escalante, J. I.

    2009-12-01

    Full Text Available Geothermal waste, a by-product of steam power plants that use geothermal underground resources, was studied as a possible replacement for Portland cement. This waste consists primarily in amorphous nanometric silica with traces of sodium and potassium chlorides. The replacement ratios studied were 0, 10 and 20% in cements cured at 20 and 60 ºC. X-ray diffraction analysis showed that clinker phase hydration took place earlier in the presence of the geothermal waste. Scanning electron microscopy, in turn, revealed a reduction in porosity and intense calcium hydroxide consumption as a result of the pozzolanic reaction. The pastes containing 20% waste, however, an intense cracking was observed due to the formation of alkali silica reaction gel and ettringite. Cracking was more prominent at 60 ºC but was not observed in either the neat cement or the blend with 10 % waste. The presence of these detrimental phases was attributed to the formation of Friedel’s salt in the initial hydration stages, induced by the chlorides in the geothermal material.Se investigaron pastas de cemento Portland sustituido con un desecho geotérmico, subproducto de la generación de electricidad en plantas que emplean recursos geotérmicos. El desecho está compuesto principalmente de sílice amorfa de tamaño nanométrico, con cloruros de sodio y potasio. Se investigaron cementos con niveles de substitución de 0, 10 y 20%, curados a 20 y 60 °C. En presencia del desecho geotérmico, se observó por Difracción de rayos X cuantitativa que la hidratación de las fases del clínker se aceleró; además mediante microscopía electrónica de barrido se encontró una disminución en la porosidad y un intenso consumo de hidróxido de calcio por la reacción puzolánica. Sin embargo, para pastas con 20% de desecho geotérmico, se observó agrietamiento con la presencia de gel de reacción álcali sílice y ettringita; fue más acentuado a 60 °C y no se observó para pastas de

  14. Mitigating the effects of system resolution on computer simulation of Portland cement hydration

    NARCIS (Netherlands)

    Chen, W.; Brouwers, H.J.H.

    2008-01-01

    CEMHYD3D is an advanced, three-dimensional computer model for simulating the hydration processes of cement, in which the microstructure of the hydrating cement paste is represented by digitized particles in a cubic domain. However, the system resolution (which is determined by the voxel size) has a

  15. Nanostructural Deformation Analysis of Calcium Silicate Hydrate in Portland Cement Paste by Atomic Pair Distribution Function

    Directory of Open Access Journals (Sweden)

    Hiroshi Suzuki

    2016-01-01

    Full Text Available The deformation of nanostructure of calcium silicate hydrate (C-S-H in Portland cement (PC paste under compression was characterized by the atomic pair distribution function (PDF, measured using synchrotron X-ray diffraction. The PDF of the PC paste exhibited a unique deformation behavior for a short-range order below 2.0 nm, close to the size of the C-S-H globule, while the deformation for a long-range order was similar to that of a calcium hydroxide phase measured by Bragg peak shift. The compressive deformation of the C-S-H nanostructure was comprised of three stages with different interactions between globules. This behavior would originate from the granular nature of C-S-H, which deforms with increasing packing density by slipping the interfaces between globules, rearranging the overall C-S-H nanostructure. This new approach will lead to increasing applications of the PDF technique to understand the deformation mechanism of C-S-H in PC-based materials.

  16. Physical chemistry of portland-cement hydrate, radioactive-waste hosts: Final report, January 16, 1987--December 31, 1987

    Energy Technology Data Exchange (ETDEWEB)

    Grutzeck, M.W.

    1989-01-15

    This is a final report summarizing the results of a study of the physical and crystal chemistry of potential hydroxylated radioactive waste hosts compatible with portland cement. Research has focussed on the identification and evaluation of hydrated host phases for four ions: cesium, strontium, iodine and boron. These ions were chosen because they are among the most long lived of the radioactive waste ions as well as the most difficult to immobilize with cement-based materials. Results show that such phases do indeed exist, and that they are excellent host phases for the above ions.

  17. Effect of Calcium Aluminate Cement Variety on the Hydration of Portland Cement in Blended System

    Institute of Scientific and Technical Information of China (English)

    XU Linglin; WANG Peiming; Geert DE SCHUTTER; WU Guangming

    2014-01-01

    Two kinds of CACs with different monocalcium aluminate (CA) contents were used in the PC/CAC (PAC) mixtures. Effects of CA and CACs on the properties of PAC were analyzed by setting times and the compressive strength tests, and also by means of calorimetry, XRD, DTA-TG and ESEM. The experimental results show that the compressive strength of the PAC mortars decreases with increasing content of CAC while it declines sharply with a higher content of CA in CAC. Compared with neat PC paste, the content of calcium hydroxide in hydrates of PAC paste decreases significantly, and the hydration time of PC is prominently prolonged. Additionally, the higher the content of CA in CAC, the more obviously the hydration of PC is delayed, confirming that the CA phase in CAC plays an important role in the delay of PC hydration.

  18. Hydration of ordinary portland cements made from raw mix containing transition element oxides

    Energy Technology Data Exchange (ETDEWEB)

    Kakali, G.; Tsivilis, S.; Tsialtas, A. [National Technical Univ. of Athens (Greece)

    1998-03-01

    The use of industrial wastes, such as waste tires, waste oil, non-ferrous metal slag, or waste molding sand, as alternative raw materials and fuel in cement plants has been established from an environmental and recycling point of view and is expected to increase in the future. Cement is broadly used, among other hydraulic binders, in the solidification and stabilization of industrial and municipal wastes. This tendency to the use of wastes in the cement industry or the utilization of cement for the handling of wastes has led to the presence of several transition element compounds in the clinker and/or in the hydrated cement. The subject of this paper is the study of the hydration process in cements made from raw mixes containing transition element oxides. The oxides used are ZrO{sub 2}, V{sub 2}O{sub 5}, Ni{sub 2}O{sub 3}, CuO, Co{sub 2}O{sub 3}, MnO, Cr{sub 2}O{sub 3}, TiO{sub 2}, MoO{sub 3}, and ZnO, and their percentage in the raw mixes is 2% w/w. The cement pastes are cured in water for 24 h, 48 h, 7 days and 28 days. Hydration rate and products are studied by means of X-ray diffraction, differential scanning calorimetry, and thermogravimetric analysis. As it is concluded, the added oxides provoke, in general, a retardation of the hydration reactions. The effect is stronger during the first 2 days and becomes negligible at 28 days. The addition of CuO strongly delays the hydration even after 28 days. Its action is related to the formation of Cu(OH){sub 2} during the first days of hydration.

  19. Hydration of portland cement, natural zeolite mortar in water and sulphate solution

    Directory of Open Access Journals (Sweden)

    Janotka, I.

    2003-03-01

    Full Text Available The objective of this paper is to characterise sulphate resistance of mortars made from ordinary Portland cement ( PC and Portland-pozzolan cement with 35 wt.% of zeolite addition (zeolite-blended cement-ZBC . Mortars with two different cement types were tested in water and 5% sodium sulphate solution for 720 days. A favourable effect of zeolite on increased sulphate resistance of the cement is caused by decrease in free Ca(OH2 content of the mortar There is not sufficient of Ca(OH2 available for reacting with the sulphate solution to form voluminous reaction products. A decreased C3A, content due to 35 wt.% replacement of PC by zeolite is the next pronounced factor improving resistance of the mortar with such blended cement.

    El objetivo de este trabajo ha sido estudiar la resistencia a los sulfatos de morteros preparados con cemento portland ordinario (PC y cemento portland puzolánico, con un 35% en peso de zeolita (zeolite-blended cement (ZBC. Ambos tipos de morteros fueron conservados en agua y en una disolución de sulfato sódico al 5% durante 720 días. Se observó una mayor resistencia a los sulfatos en el mortero preparado con el cemento que contenía zeolita debido a su menor contenido en Ca(OH2. No hay cantidad suficiente de Ca(OH2 para que se produzca la reacción de los constituyentes de la pasta con la disolución de sulfato sódico y formar así productos de naturaleza expansiva. La disminución en el contenido de C,3A, debida a la sustitución de un 35% en peso de PC por zeolita, es el factor más determinante en el aumento de la resistencia del mortero en los cementos con adición.

  20. Effect of Nano-SiO₂ on the Hydration and Microstructure of Portland Cement.

    Science.gov (United States)

    Wang, Liguo; Zheng, Dapeng; Zhang, Shupeng; Cui, Hongzhi; Li, Dongxu

    2016-12-15

    This paper systematically studied the modification of cement-based materials by nano-SiO₂ particles with an average diameter of about 20 nm. In order to obtain the effect of nano-SiO₂ particles on the mechanical properties, hydration, and pore structure of cement-based materials, adding 1%, 3%, and 5% content of nano-SiO₂ in cement paste, respectively. The results showed that the reaction of nano-SiO₂ particles with Ca(OH)₂ (crystal powder) started within 1 h, and formed C-S-H gel. The reaction speed was faster after aging for three days. The mechanical properties of cement-based materials were improved with the addition of 3% nano-SiO₂, and the early strength enhancement of test pieces was obvious. Three-day compressive strength increased 33.2%, and 28-day compressive strength increased 18.5%. The exothermic peak of hydration heat of cement increased significantly after the addition of nano-SiO₂. Appearance time of the exothermic peak was advanced and the total heat release increased. Thermogravimetric-differential scanning calorimetry (TG-DSC) analysis showed that nano-SiO₂ promoted the formation of C-S-H gel. The results of mercury intrusion porosimetry (MIP) showed that the total porosity of cement paste with 3% nano-SiO₂ was reduced by 5.51% and 5.4% at three days and 28 days, respectively, compared with the pure cement paste. At the same time, the pore structure of cement paste was optimized, and much-detrimental pores and detrimental pores decreased, while less harmful pores and innocuous pores increased.

  1. Basalt waste added to Portland cement

    Directory of Open Access Journals (Sweden)

    Thiago Melanda Mendes

    2016-08-01

    Full Text Available Portland cement is widely used as a building material and more than 4.3 billion tons were produced in 2014, with increasing environmental impacts by this industry, mainly through CO2 emissions and consumption of non-removable raw materials. Several by-products have been used as raw materials or fuels to reduce environmental impacts. Basaltic waste collected by filters was employed as a mineral mixture to Portland cement and two fractions were tested. The compression strength of mortars was measured after 7 days and Scanning Electron Microscopy (SEM and Electron Diffraction Scattering (EDS were carried out on Portland cement paste with the basaltic residue. Gains in compression strength were observed for mixtures containing 2.5 wt.% of basaltic residue. Hydration products observed on surface of basaltic particles show the nucleation effect of mineral mixtures. Clinker substitution by mineral mixtures reduces CO2 emission per ton of Portland cement.

  2. Synthesis of pure Portland cement phases

    DEFF Research Database (Denmark)

    Wesselsky, Andreas; Jensen, Ole Mejlhede

    2009-01-01

    Pure phases commonly found in Portland cement clinkers are often used to test cement hydration behaviour in simplified experimental conditions. The synthesis of these phases is covered in this paper, starting with a description of phase relations and possible polymorphs of the four main phases...... in Portland cement, i.e. tricalcium silicate, dicalcium silicate, tricalcium aluminate and tetracalcium alumino ferrite. Details of the The process of solid state synthesis are is described in general including practical advice on equipment and techniques. Finally In addition, some exemplary mix compositions...

  3. PART II. HYDRATED CEMENTS

    Directory of Open Access Journals (Sweden)

    Milan Drabik

    2014-09-01

    Full Text Available Essential focus of the study has been to acquire thermoanalytical events, incl. enthalpies of decompositions - ΔH, of technological materials based on two types of Portland cements. The values of thermoanalytical events and also ΔH of probes of technological compositions, if related with the data of a choice of minerals of calcium-silicate-sulfate-aluminate hydrates, served as a valued input for the assessment of phases present and phase changes due to the topical hydraulic processes. The results indicate mainly the effects of "standard humidity" or "wet storage" of the entire hydration/hydraulic treatment, but also the presence of cement residues alongside calcium-silicate-sulfate-aluminate hydrates (during the tested period of treatment. "A diluting" effect of unhydrated cement residues upon the values of decomposition enthalpies in the studied multiphase system is postulated and discussed

  4. Dehydration kinetics of Portland cement paste at high temperature

    NARCIS (Netherlands)

    Zhang, Q.; Ye, G.

    2012-01-01

    Portland cement paste is a multiphase compound mainly consisting of calcium-silicate-hydrate (CSH) gel, calcium hydroxide (CH) crystal, and unhydrated cement core. When cement paste is exposed to high temperature, the dehydration of cement paste leads to not only the decline in strength, but also

  5. Dehydration kinetics of Portland cement paste at high temperature

    NARCIS (Netherlands)

    Zhang, Q.; Ye, G.

    2012-01-01

    Portland cement paste is a multiphase compound mainly consisting of calcium-silicate-hydrate (CSH) gel, calcium hydroxide (CH) crystal, and unhydrated cement core. When cement paste is exposed to high temperature, the dehydration of cement paste leads to not only the decline in strength, but also th

  6. Application of Neutron imaging in pore structure of hydrated wellbore cement: comparison of hydration of H20 with D2O based Portland cements

    Science.gov (United States)

    Dussenova, D.; Bilheux, H.; Radonjic, M.

    2012-12-01

    Wellbore Cement studies have been ongoing for decades. The studies vary from efforts to reduce permeability and resistance to corrosive environment to issues with gas migration also known as Sustained Casing Pressure (SCP). These practical issues often lead to health and safety problems as well as huge economic loss in oil and gas industry. Several techniques have been employed to reduce the impact of gas leakage. In this study we purely focus on expandable liners, which are introduced as part of oil well reconstruction and work-overs and as well abandonment procedures that help in prevention of SCP. Expandable liner is a tube that after application of a certain tool can increase its diameter. The increase in diameter creates extra force on hydrated cement that results in reducing width of interface fractures and cement-tube de-bonding. Moreover, this also causes cement to change its microstructure and other porous medium properties, primarily hydraulic conductivity. In order to examine changes before and after operations, cement pore structure must be well characterized and correlated to cement slurry design as well as chemical and physical environmental conditions. As modern oil well pipes and tubes contain iron, it is difficult to perform X-ray tomography of a bulk measurement of the cement in its wellbore conditions, which are tube wall-cement-tube wall. Neutron imaging is a complementary technique to x-ray imaging and is well suited for detection of light elements imbedded in metallic containers. Thus, Neutron Imaging (NI) is investigated as a tool for the detection of pore structure of hydrated wellbore cement. Recent measurements were conducted at the Oak Ridge National Laboratory (ORNL) High Flux Isotope Reactor (HFIR) neutron imaging facility. NI is is highly sensitive to light elements such as Hydrogen (H). Oil well cements that have undergone a full hydration contain on average 30%-40% of free water in its pore structure. The unreacted water is the main

  7. Study of the relation between hydrated portland cement composition and leaching resistance

    NARCIS (Netherlands)

    Eijk, van R.J.; Brouwers, H.J.H.

    1998-01-01

    The present paper addresses cement compositions that have an optimal resistance against acid attack and hence, low leaching rates and optimal waste containment. To this end a shrinking core leaching model is used that describes the leaching of metals from a cement sample. This process is directly re

  8. Shotcrete -- Understanding of the hydration process of mixes containing CAC and Portland cement and proposal for a simple rheological characterization

    Energy Technology Data Exchange (ETDEWEB)

    Bayoux, J.P.; Testud, M.; Guinot, D. [Lafarge Coppee Recherche, Saint-Quentin-Fallavier (France); Willocq, J.; Capmas, A. [Lafarge Fondu International, Neuilly-sur-Seine (France)

    1995-12-31

    In order to better understand the performances of CAC-slag cement and CAC--PC cement the hydration study of these mixes was undertaken. The hydrates which are responsible for the early stiffening/strengthening are identical in both mixes; it is only the time of appearance and amount which varies. Ettringite always forms first followed by the precipitation of C{sub 4}AH{sub 13}. They will both form faster then the temperature rises. As a complement, a simple laboratory equipment is proposed to characterize the stiffening behavior of the mixes straight after gauging.

  9. The use of electrical impedance spectroscopy for monitoring the hydration products of Portland cement mortars with high percentage of pozzolans

    Energy Technology Data Exchange (ETDEWEB)

    Cruz, J.M. [Departamento de Física Aplicada, Universitat Politècnica de València, Camino de Vera, 46022, Valencia (Spain); Fita, I.C., E-mail: infifer@fis.upv.es [Departamento de Física Aplicada, Universitat Politècnica de València, Camino de Vera, 46022, Valencia (Spain); Soriano, L.; Payá, J.; Borrachero, M.V. [ICITECH, Instituto de Ciencia y Tecnología del Hormigón, Universitat Politècnica de València (Spain)

    2013-08-15

    In this paper, mortars and pastes containing large replacement of pozzolan were studied by mechanical strength, thermogravimetric analysis (TGA), scanning electronic microscopy (SEM), mercury intrusion porosimetry (MIP) and electrical impedance spectroscopy (EIS). The effect of metakaolin (35%) and fly ash (60%) was evaluated and compared with an inert mineral addition (andalusite). The portlandite content was measured, finding that the pozzolanic reaction produced cementing systems with all portlandite fixed. The EIS measurements were analyzed by the equivalent electrical circuit (EEC) method. An EEC with three branches in parallel was applied. The dc resistance was related to the degree of hydration and allowed us to characterize plain and blended mortars. A constant phase element (CPE) quantified the electrical properties of the hydration products located in the solid–solution interface and was useful to distinguish the role of inert and pozzolanic admixtures present in the cement matrix.

  10. Influence of Metakaolin on Hydration Products of Portland Cement Pastes%偏高岭土对硅酸盐水泥水化产物的影响

    Institute of Scientific and Technical Information of China (English)

    丁卫清; 朱教群; 周卫兵; 孙正; 喻巍

    2014-01-01

    The content of hydration products calcium hydroxide,morphology,chemical composition and packing structure of C-S-H gel for portland cement pastes with different fraction of metakaolin were investigated by TG-DSC, AFM and SEM-EDAX.Effects of different dosages of metakaolin on characteristics of hydration products were also discussed.The results show that the content of hydration products calcium hydroxide was reduced by adding metaka-olin,from 18.68% to 13.66% when metakaolin content reaches 15% after 28 days.The particle size of C-S-H gel has been tended to become small with the increasing of metakaolin content,particles gather more closely.Metakaolin reacts with the hydration products Ca(OH)2 to produce C-S-H gel with lower molar ratio of CaO and SiO2 ,which has higher strength,better stability,the construction and chemical composition of C-S-H gel can be improved.%通过热重-差式扫描量热仪、原子力显微镜、扫描电子显微镜-能谱分析研究了偏高岭土对硅酸盐水泥水化产物Ca(OH)2的含量,C-S-H 凝胶的形貌特征、化学组成和堆聚结构的影响,讨论了水化产物性质随偏高岭土掺量变化的规律。结果表明:偏高岭土的掺入,水化产物Ca(OH)2的含量相应降低,在偏高岭土掺量15%时,水化28 d龄期试样中Ca(OH)2的质量分数由18.68%降低到13.66%;同时 C-S-H 凝胶颗粒尺寸随着偏高岭土掺量的增加而逐渐减小,堆聚更加紧密,偏高岭土与水泥水化产物Ca(OH)2反应生成结构致密稳定性更好的低Ca/Si值的 C-S-H 凝胶,改善了C-S-H 凝胶的结构和化学组成。

  11. 电阻率法测定硅酸盐水泥水化活化能%Activation Energy of Portland Cement Hydration by Electrical Resistivity Measurement

    Institute of Scientific and Technical Information of China (English)

    魏小胜; 肖莲珍

    2011-01-01

    研究了温度对水泥水化时电阻率的影响情况,建立了用于估算电阻率极大值的双曲线方程,提出根据不同温度时的电阻率可以计算孔隙液相活化能(Eas)和水化反应的活化能(Ear).试验所用水泥浆体试样的水灰比分别为0.30、0.35、0.40、0.45和0.55,养护温度分别为15、20℃和30℃,测试时间均为72h.为消除温度对孔隙液相离子迁移的影响,在15℃和30℃测得的电阻率值分别以20℃为基准进行了校正,分析了温度对水泥水化产物形成的影响.研究表明:当水灰比从0.55减小到0.30时.Eas从16.5kJ/mol增大到25.7kJ/mol,这是因为低水灰比水泥浆体的液相离子浓度较大.计算表明:硅酸盐水泥水化反应的活化能Ear为37.2 kJ/mol,这与ASTM C1074的推荐值(40 kJ/mol)比较接近.在不同养护温度下得到的电阻率双曲线方程表明:在所测试的温度范围内,温度越低,电阻率的极大值越大.%Temperature effect on the electrical resistivity of Portland cement pastes during first 72 h was investigated. The experiments were conducted on the cement pastes with various water cement ratios of 0.30, 0.35, 0.40, 0.45, 0.55 at different curing temperatures of 15, 20 and 30 ℃. The hyperbolic equation for each sample was established to estimate the ultimate resistivity. The electrical resistivity at various temperatures can determinate the activation energy for the liquid solution in pores (Eas) and the activation energy for hydration reaction (Ear). The electrical resistivities at 15 and 30 ℃ are obtained based on the value at 20 ℃ to eliminate the effect of temperature on the ionic mobility in the liquid solutions. The Eas increased with the decrease of water cement ratio due to a higher ion concentration in a lower water cement ratio paste solution, and the Eas ranged from 16.5 to 25.7 kJ/mol. The activation energy of cement hydration determined was 37.2 k J/mol, which was similar to the value recommended by the

  12. Hydration of Portoguese cements, measurement and modelling of chemical shrinkage

    DEFF Research Database (Denmark)

    Maia, Lino; Geiker, Mette Rica; Figueiras, Joaquim A.

    2008-01-01

    Development of cement hydration was studied by measuring the chemical shrinkage of pastes. Five types of Portuguese Portland cement were used in cement pastes with . Chemical shrinkage was measured by gravimetry and dilatometry. In gravimeters results were recorded automatically during at least...

  13. Effect of different mixing methods on the physical properties of Portland cement

    OpenAIRE

    Shahi, Shahriar; Ghasemi, Negin; Rahimi, Saeed; Yavari, Hamidreza; Samiei, Mohammad; Jafari, Farnaz

    2016-01-01

    Background The Portland cement is hydrophilic cement; as a result, the powder-to-liquid ratio affects the properties of the final mix. In addition, the mixing technique affects hydration. The aim of this study was to evaluate the effect of different mixing techniques (conventional, amalgamator and ultrasonic) on some selective physical properties of Portland cement. Material and Methods The physical properties to be evaluated were determined using the ISO 6786:2001 specification. One hundred ...

  14. Hydration of Portoguese cements, measurement and modelling of chemical shrinkage

    DEFF Research Database (Denmark)

    Maia, Lino; Geiker, Mette Rica; Figueiras, Joaquim A.

    2008-01-01

    form of the dispersion model. The development of hydration varied between the investigated cements; based on the measured data the degree of hydration after 24 h hydration at 20 C varied between 40 and 50%. This should be taken into account when comparing properties of concrete made from the different......Development of cement hydration was studied by measuring the chemical shrinkage of pastes. Five types of Portuguese Portland cement were used in cement pastes with . Chemical shrinkage was measured by gravimetry and dilatometry. In gravimeters results were recorded automatically during at least...

  15. Effect of temperature on the hydration process and strength development in blends of Portland cement and activated coal gangue or fly ash

    Institute of Scientific and Technical Information of China (English)

    Pei-ming WANG; Xian-ping LIU

    2011-01-01

    This paper describes the results of an investigation into the effect of the variation of curing temperatures between 0 and 60 ℃ on the hydration process,pore structure variation,and compressive strength development of activated coal gangue-cement blend (ACGC).Hardened ACGC pastes cured for hydration periods from 1 to 360 d were examined using the non-evaporable water method,thermal analysis,mercury intrusion porosimetry,and mechanical testing.To evaluate the specific effect of activated coal gangue (ACG) as a supplementary cementing material (SCM),a fly ash-cement blend (FAC) was used as a control.Results show that raising the curing temperature accelerates pozzolanic reactions involving the SCMs,increasing the degree of hydration of the cement blends,and hence increasing the rate of improvement in strength.The effect of curing temperature on FAC is greater than that on ACGC.The pore structure of the hardened cement paste is improved by increasing the curing temperature up to 40 ℃,but when the curing temperature reaches 60 ℃,the changing nature of the pore structure leads to a decrease in strength.The correlation between compressive strength and the degree of hydration and porosity is linear in nature.

  16. Conduction calorimetric studies of ternary binders based on Portland cement, calcium aluminate cement and calcium sulphate

    OpenAIRE

    Torrens Martín, David; Fernández Carrasco, Lucía; Blanco Varela, M.Teresa

    2013-01-01

    Different binders of Portland cement, calcium aluminate cement and calcium sulphate (PC/CAC/CS) have been investigated to determinate the in¿uence the CAC and CS amount in the reactions mechanism. Several mixtures were studied, ratios of 100, 85/15 and 75/25 of PC/CAC with 0, 3 and 5 % of CS. Conduction calorimetric technique was used to follow the hydration during 100 h. The XRD and FTIR techniques were used as support in the analysis of the hydration products. The results have shown tha...

  17. The hardening of Portland cement studied by ? NMR stray-field imaging

    Science.gov (United States)

    Nunes, Teresa; Randall, E. W.; Samoilenko, A. A.; Bodart, P.; Feio, G.

    1996-03-01

    Hydration and hardening processes of Portland cement (type I) were studied by analysis of the one-dimensional projections (profiles) obtained periodically with the 0022-3727/29/3/044/img8 stray-field imaging technique over two days. The influence of additives, such as gypsum, in Portland cement (type IA) was also investigated. The decay of the signal intensity as a function of time was found to be bi-exponential for type I and mono-exponential for type IA.

  18. Modelling the effects of waste components on cement hydration

    NARCIS (Netherlands)

    Eijk, van R.J.; Brouwers, H.J.H.

    2001-01-01

    Ordinary Portland Cement (OPC) is often used for the solidification/stabilization (S/S) of waste containing heavy metals and salts. These waste components will precipitate in the form of insoluble compounds on to unreacted cement clinker grains preventing further hydration. In this study the long te

  19. Modelling the effects of waste components on cement hydration

    NARCIS (Netherlands)

    Eijk, van R.J.; Brouwers, H.J.H.

    2000-01-01

    Ordinary Portland Cement (OPC) is often used for the Solidification/Stabilization (S/S) of waste containing heavy metals and salts. These waste componenents will precipitate in the form of insoluble compounds onto unreacted cement clinker grains preventing further hydration. In this study the long t

  20. Nanostructure of Calcium Silicate Hydrates in Cements

    KAUST Repository

    Skinner, L. B.

    2010-05-11

    Calcium silicate hydrate (CSH) is the major volume phase in the matrix of Portland cement concrete. Total x-ray scattering measurements with synchrotron x rays on synthetic CSH(I) shows nanocrystalline ordering with a particle diameter of 3.5(5) nm, similar to a size-broadened 1.1 nm tobermorite crystal structure. The CSH component in hydrated tricalcium silicate is found to be similar to CSH(I). Only a slight bend and additional disorder within the CaO sheets is required to explain its nanocrystalline structure. © 2010 The American Physical Society.

  1. Portland cement-blast furnace slag blends in oilwell cementing applications

    Energy Technology Data Exchange (ETDEWEB)

    Mueller, D.T.; DiLullo, G.; Hibbeler, J. [and others

    1995-12-31

    Recent investigations of blast furnace slag cementing technologies. have been expanded to include Portland cement/blast furnace slag blends. Mixtures of Portland cement and blast furnace slag, while having a long history of use in the construction industry, have not been used extensively in oilwell cementing applications. Test results indicate that blending blast furnace slag with Portland cement produces a high quality well cementing material. Presented are the design guidelines and laboratory test data relative to mixtures of blast furnace slag and Portland cements. Case histories delineating the use of blast furnace slag - Portland cement blends infield applications are also included.

  2. 76 FR 76760 - Gray Portland Cement and Cement Clinker From Japan

    Science.gov (United States)

    2011-12-08

    ... Portland Cement and Cement Clinker From Japan Determination On the basis of the record \\1\\ developed in the... antidumping duty order on gray Portland cement and cement clinker from Japan would be likely to lead to... the Commission are contained in USITC Publication 4281 (December 2011), entitled Gray Portland...

  3. Characteristics of Portland blast-furnace slag cement containing cement kiln dust and active silica

    Directory of Open Access Journals (Sweden)

    A. Abdel Rahman

    2016-09-01

    Full Text Available This investigation dealt with the effect of active silica, silica fume (SF or rice husk ash (RHA, on the mechanical and physico-chemical characteristics of the hardened blended cement pastes made of Portland blast-furnace slag cement (PSC containing cement kiln dust (CKD cured under normal conditions. Two blends made of PSC and CKD, improved by SF and two blends made of PSC and CKD improved by RHA were investigated. Hardened blended cement pastes were prepared from each cement blend by using water/cement ratio (W/C of 0.30 by weight and hydrated for various curing ages of 1, 3, 7, 28 and 90 days at the normal curing conditions under tap water at room temperature. Each cement paste was tested for its physico-chemical and mechanical characteristics; these characteristics include: compressive strength and kinetics of hydration. The phase composition of the formed hydration products was identified using X-ray diffraction (XRD and differential thermal analysis (DTA. It was found that the partial substitution of PSC by 10% and 15% of CKD is associated with an increase in the rate of hydration and a subsequent improvement of compressive strength of hardened PSC–CKD pastes. In addition, the replacement of PSC, in PSC–CKD blends, by 5% active silica was accompanied by further improvement of the physico-mechanical characteristics of the hardened PSC–CKD pastes.

  4. Sorption kinetics of superabsorbent polymers (SAPs) in fresh Portland cement-based pastes visualized and quantified by neutron radiography and correlated to the progress of cement hydration

    Energy Technology Data Exchange (ETDEWEB)

    Schroefl, Christof, E-mail: christof.schroefl@tu-dresden.de [Technische Universität Dresden, Fakultät Bauingenieurwesen, Institut für Baustoffe, DE-01062 Dresden (Germany); Mechtcherine, Viktor [Technische Universität Dresden, Fakultät Bauingenieurwesen, Institut für Baustoffe, DE-01062 Dresden (Germany); Vontobel, Peter; Hovind, Jan; Lehmann, Eberhard [Paul Scherrer Institut, Laboratory for Neutron Scattering and Imaging, CH-5232 Villigen/AG (Switzerland)

    2015-09-15

    Water sorption of two superabsorbent polymers in cement-based pastes has been characterized by neutron radiography. Cement pastes with W/C of 0.25 and 0.50 and one additionally containing silica fume (W/C = 0.42) were investigated. The SAPs differed in their inherent sorption kinetics in extracted cement pore solution (SAP 1: self-releasing; SAP 2: retentive). Desorption from SAP 1 started very early after paste preparation. Hence, its individual non-retentiveness governs its behavior only. SAP 2 released water into all matrices, but its kinetics were different. In the paste with the highest W/C, some moderate water release was recorded from the beginning. In the other two pastes, SAP 2 retained its stored liquid during the dormant period, i.e., up to the percolation threshold. Intense desorption then set in and continued throughout the acceleration period. These findings explain the pronouncedly higher efficiency of SAP 2 as internal curing admixture as compared to SAP 1.

  5. Hydration states of AFm cement phases

    Energy Technology Data Exchange (ETDEWEB)

    Baquerizo, Luis G., E-mail: luis.baquerizoibarra@holcim.com [Innovation, Holcim Technology Ltd., CH-5113 Holderbank (Switzerland); Matschei, Thomas [Innovation, Holcim Technology Ltd., CH-5113 Holderbank (Switzerland); Scrivener, Karen L. [Laboratory of Construction Materials, Ecole Polytechnique Fédérale de Lausanne, CH-1015 Lausanne (Switzerland); Saeidpour, Mahsa; Wadsö, Lars [Building Materials, Lund University, Box 124, 221 000 Lund (Sweden)

    2015-07-15

    The AFm phase, one of the main products formed during the hydration of Portland and calcium aluminate cement based systems, belongs to the layered double hydrate (LDH) family having positively charged layers and water plus charge-balancing anions in the interlayer. It is known that these phases present different hydration states (i.e. varying water content) depending on the relative humidity (RH), temperature and anion type, which might be linked to volume changes (swelling and shrinkage). Unfortunately the stability conditions of these phases are insufficiently reported. This paper presents novel experimental results on the different hydration states of the most important AFm phases: monocarboaluminate, hemicarboaluminate, strätlingite, hydroxy-AFm and monosulfoaluminate, and the thermodynamic properties associated with changes in their water content during absorption/desorption. This data opens the possibility to model the response of cementitious systems during drying and wetting and to engineer systems more resistant to harsh external conditions.

  6. Stabilization of chromium salt in ordinary portland cement

    Indian Academy of Sciences (India)

    Damir Barbir; Pero Dabić; Petar Krolo

    2012-12-01

    Ordinary Portland cement (OPC) samples containing the chromium salt have been investigated using differential microcalorimetry, conductometry and Fourier transform infrared spectroscopic analysis. The effect of chromium on OPC hydration was evaluated by continuous observing of early hydration. The microcalorimetrical results show that with increasing the share of chromium salt, heat maximums assume lower values and the occurrence of the maximum registered in the earlier hydration times. Conductometrical measurements show that with increasing addition of chromium salt, curve did not show any specific shape, immediate drop in specific conductivity is noticed and the maximum is reached earlier. This coincides with microcalorimetrical results. It can be concluded that the addition of chromium does not affect the mechanism of the hydration process, but it does affect the kinetic parameters and dynamics of the cement hydration process. It was found that chromium salt addition to the cement–water system is acceptable up to 2 wt.%. According to standard EN 196-3 for OPC, the beginning of binding time should occur after 60 minutes. Increased amount of chromium over 2 wt.% significantly accelerate the beginning of binding time and for the system it is not acceptable.

  7. Corrosion inhibitor mechanisms on reinforcing steel in Portland cement pastes

    Science.gov (United States)

    Martin, Farrel James

    2001-07-01

    The mechanisms of corrosion inhibitor interaction with reinforcing steel are investigated in the present work, with particular emphasis on effects associated with corrosion inhibitors admixed into Portland cement paste. The principal objective in reinforcing steel corrosion inhibition for Portland cement concrete is observed to be preservation of the naturally passive steel surface condition established by the alkaline environment. Introduction of chloride ions to the steel surface accelerates damage to the passive film. Excessive damage to the passive film leads to loss of passivity and a destabilization of conditions that facilitate repair of the passive film. Passive film preservation in presence of chloride ions is achieved either through stabilization of the passive film or by modification of the chemical environment near the steel surface. Availability of inhibitors to the steel surface and their tendency to stabilize passive film defects are observed to be of critical importance. Availability of admixed corrosion inhibitors to the passive film is affected by binding of inhibitors during cement paste hydration. It is determined that pore solution concentrations of inorganic admixed inhibitors tend to be lower than the admixed concentration, while pore solution concentrations of organic admixed inhibitors tend to be higher than the admixed concentration. A fundamental difference of inhibitor function is observed between film-forming and defect stabilizing corrosion inhibitors. Experiments are conducted using coupons of reinforcing steel that are exposed to environments simulating chloride-contaminated Portland cement concrete. A study of the steel/cement paste interface is also performed, and compounds forming at this interface are identified using X-Ray diffraction.

  8. Galvanic corrosion of Mg-Zr fuel cladding and steel immobilized in Portland cement and geopolymer at early ages

    Science.gov (United States)

    Rooses, Adrien; Lambertin, David; Chartier, David; Frizon, Fabien

    2013-04-01

    Galvanic corrosion behaviour of Mg-Zr alloy fuel cladding and steel has been studied in Ordinary Portland cement and Na-geopolymer. Portland cements implied the worse magnesium corrosion performances due to the negative effects of cement hydrates, grinding agents and gypsum on the galvanic corrosion. Galvanic corrosion in Na-geopolymer paste remains very low. Silicates and fluoride from the geopolymer activation solution significantly improve the corrosion resistance of the magnesium alloy while coupling with a cathode.

  9. Physical, mechanical, and durability properties of gypsum-Portland cement-natural pozzolan blends

    National Research Council Canada - National Science Library

    Colak A

    2001-01-01

    This paper deals with the effect of gypsum Portland cement and gypsum Portland cement natural pozzolan ratios on the physical, mechanical, and durability properties of gypsum Portland cement natural pozzolan blends...

  10. Modeling the influence of limestone addition on cement hydration

    Directory of Open Access Journals (Sweden)

    Ashraf Ragab Mohamed

    2015-03-01

    Full Text Available This paper addresses the influence of using Portland limestone cement “PLC” on cement hydration by characterization of its microstructure development. The European Standard EN 197-1:2011 and Egyptian specification ESS 4756-1/2009 permit the cement to contain up to 20% ground limestone. The computational tools assist in better understanding the influence of limestone additions on cement hydration and microstructure development to facilitate the acceptance of these more economical and ecological materials. μic model has been developed to enable the modeling of microstructural evolution of cementitious materials. In this research μic model is used to simulate both the influence of limestone as fine filler, providing additional surfaces for the nucleation and growth of hydration products. Limestone powder also reacts relatively slow with hydrating cement to form monocarboaluminate (AFmc phase, similar to the mono-sulfoaluminate (AFm phase formed in ordinary Portland cement. The model results reveal that limestone cement has accelerated cement hydration rate, previous experimental results and computer model “cemhyd3d” are used to validate this model.

  11. Assessment of Pollution Potentialities of some Portland Cement 1H ...

    African Journals Online (AJOL)

    ABSTRACT: Chemical analysis of some Portland cement commonly used in Nigeria was carried out. All the cement studies ... Determination of Loss on Ignition. 1g of each ... the specifications of American Standard for testing materials (ASTM ...

  12. Serviceability and Reinforcement of Low Content Whisker in Portland Cement

    Institute of Scientific and Technical Information of China (English)

    CAO Mingli; WEI Jianqiang; WANG Lijiu

    2011-01-01

    In order to explore the serviceability and reinforcement of CaCO3 whisker in portland cement matrix,the durability of CaCO3 whisker and effect of low whisker content(0%-4.0%)on the working performance and mechanical properties of portland cement were investigated.The experimental results show that CaCO3 whiskers have a good stability and serviceability in cement,and should not significantly alter the rheological properties of the cement paste.The flexural and compressive strength of portland cement reinforced by CaCO3 whiskers was increased by 33.3% and 12.83%,respectively.

  13. Alternative Fuel for Portland Cement Processing

    Energy Technology Data Exchange (ETDEWEB)

    Schindler, Anton K; Duke, Steve R; Burch, Thomas E; Davis, Edward W; Zee, Ralph H; Bransby, David I; Hopkins, Carla; Thompson, Rutherford L; Duan, Jingran; ; Venkatasubramanian, Vignesh; Stephen, Giles

    2012-06-30

    The production of cement involves a combination of numerous raw materials, strictly monitored system processes, and temperatures on the order of 1500 °C. Immense quantities of fuel are required for the production of cement. Traditionally, energy from fossil fuels was solely relied upon for the production of cement. The overarching project objective is to evaluate the use of alternative fuels to lessen the dependence on non-renewable resources to produce portland cement. The key objective of using alternative fuels is to continue to produce high-quality cement while decreasing the use of non-renewable fuels and minimizing the impact on the environment. Burn characteristics and thermodynamic parameters were evaluated with a laboratory burn simulator under conditions that mimic those in the preheater where the fuels are brought into a cement plant. A drop-tube furnace and visualization method were developed that show potential for evaluating time- and space-resolved temperature distributions for fuel solid particles and liquid droplets undergoing combustion in various combustion atmospheres. Downdraft gasification has been explored as a means to extract chemical energy from poultry litter while limiting the throughput of potentially deleterious components with regards to use in firing a cement kiln. Results have shown that the clinkering is temperature independent, at least within the controllable temperature range. Limestone also had only a slight effect on the fusion when used to coat the pellets. However, limestone addition did display some promise in regards to chlorine capture, as ash analyses showed chlorine concentrations of more than four times greater in the limestone infused ash as compared to raw poultry litter. A reliable and convenient sampling procedure was developed to estimate the combustion quality of broiler litter that is the best compromise between convenience and reliability by means of statistical analysis. Multi-day trial burns were conducted

  14. Hydration Characteristics of Metakaolin Admixtured Cement using DTA, XRD and SEM Techniques

    Science.gov (United States)

    Govindarajan, D.; Gopalakrishnan, R.

    2008-04-01

    The paper aims to investigate hydration and pozzolanic reaction in Portland cement paste with different replacement percentages (0%, 10%, 20% and 30%) of metakaolin. The compressive strength of the metakaolin admixtured cement was measured at 1 day, 1 week and 4 weeks. The compressive strength developments of the metakaolin admixtured cement are compared with Portland cement. It is found that metakaolin contributes significantly to strength development as an accelerating admixture for Portland cement. The pozzolanic reactions and the reaction products were determined by DTA, XRD and SEM.

  15. 76 FR 24519 - Gray Portland Cement and Cement Clinker From Japan; Institution of a Five-Year Review Concerning...

    Science.gov (United States)

    2011-05-02

    ... COMMISSION Gray Portland Cement and Cement Clinker From Japan; Institution of a Five-Year Review Concerning the Antidumping Duty Order on Gray Portland Cement and Cement Clinker From Japan AGENCY: United States... determine whether revocation of the antidumping duty order on gray portland cement and cement clinker...

  16. Radiopacity of portland cement associated with different radiopacifying agents.

    Science.gov (United States)

    Húngaro Duarte, Marco Antonio; de Oliveira El Kadre, Guâniara D'arc; Vivan, Rodrigo Ricci; Guerreiro Tanomaru, Juliane Maria; Tanomaru Filho, Mário; de Moraes, Ivaldo Gomes

    2009-05-01

    This study evaluated the radiopacity of Portland cement associated with the following radiopacifying agents: bismuth oxide, zinc oxide, lead oxide, bismuth subnitrate, bismuth carbonate, barium sulfate, iodoform, calcium tungstate, and zirconium oxide. A ratio of 20% radiopacifier and 80% white Portland cement by weight was used for analysis. Pure Portland cement and dentin served as controls. Cement/radiopacifier and dentin disc-shaped specimens were fabricated, and radiopacity testing was performed according to the ISO 6876/2001 standard for dental root sealing materials. Using Insight occlusal films, the specimens were radiographed near to a graduated aluminum stepwedge varying from 2 to 16 mm in thickness. The radiographs were digitized and radiopacity compared with the aluminum stepwedge using Digora software (Orion Corporation Soredex, Helsinki, Finland). The radiographic density data were converted into mmAl and analyzed statistically by analysis of variance and Tukey-Kramer test (alpha = 0.05). The radiopacity of pure Portland cement was significantly lower (p oxide and Portland cement/lead oxide presented the highest radiopacity values and differed significantly from the other materials (p oxide presented the lowest radiopacity values of all mixtures (p < 0.05). All tested substances presented higher radiopacity than that of dentin and may potentially be added to the Portland cement as radiopacifying agents. However, the possible interference of the radiopacifiers with the setting chemistry, biocompatibility, and physical properties of the Portland cement should be further investigated before any clinical recommendation can be done.

  17. 76 FR 2832 - National Emission Standards for Hazardous Air Pollutants From the Portland Cement Manufacturing...

    Science.gov (United States)

    2011-01-18

    ... the Portland Cement Manufacturing Industry and Standards of Performance for Portland Cement Plants... (NESHAP) from the Portland Cement Manufacturing Industry and Standards of Performance (NSPS) for Portland Cement Plants. The final rules were published on September 9, 2010. This direct final action...

  18. 77 FR 46371 - National Emission Standards for Hazardous Air Pollutants for the Portland Cement Manufacturing...

    Science.gov (United States)

    2012-08-03

    ... the Portland Cement Manufacturing Industry and Standards of Performance for Portland Cement Plants... Standards for Hazardous Air Pollutants for the Portland Cement Manufacturing Industry and Standards of Performance for Portland Cement Plants,'' which was published in the Federal Register on July 18, 2012....

  19. 76 FR 28318 - National Emission Standards for Hazardous Air Pollutants From the Portland Cement Manufacturing...

    Science.gov (United States)

    2011-05-17

    ... the Portland Cement Manufacturing Industry and Standards of Performance for Portland Cement Plants... Pollutants emitted by the Portland Cement Industry and the New Source Performance Standards for Portland Cement Plants issued under sections 112(d) and 111(b) of the Clean Air Act, respectively. The EPA is...

  20. 76 FR 2860 - National Emission Standards for Hazardous Air Pollutants From the Portland Cement Manufacturing...

    Science.gov (United States)

    2011-01-18

    ... the Portland Cement Manufacturing Industry and Standards of Performance for Portland Cement Plants... of Performance (NSPS) for Portland Cement Plants. The final rules were published on September 9, 2010... Portland Cement Manufacturing Industry Docket, Docket ID No. EPA-HQ-OAR-2002-0051, 1200 Pennsylvania...

  1. Hydration of fly ash cement

    Energy Technology Data Exchange (ETDEWEB)

    Etsuo Sakai; Shigeyoshi Miyahara; Shigenari Ohsawa; Seung-Heun Lee; Masaki Daimon [Tokyo Institute of Technology, Tokyo (Japan). Department of Metallurgy and Ceramics Science, Graduate School of Science and Engineering

    2005-06-01

    It is necessary to establish the material design system for the utilization of large amounts of fly ash as blended cement instead of disposing of it as a waste. Cement blended with fly ash is also required as a countermeasure to reduce the amount of CO{sub 2} generation. In this study, the influences of the glass content and the basicity of glass phase on the hydration of fly ash cement were clarified and hydration over a long curing time was characterized. Two kinds of fly ash with different glass content, one with 38.2% and another with 76.6%, were used. The hydration ratio of fly ash was increased by increasing the glass content in fly ash in the specimens cured for 270 days. When the glass content of fly ash is low, the basicity of glass phase tends to decrease. Reactivity of fly ash is controlled by the basicity of the glass phase in fly ash during a period from 28 to 270 days. However, at an age of 360 days, the reaction ratios of fly ash show almost identical values with different glass contents. Fly ash also affected the hydration of cement clinker minerals in fly ash cement. While the hydration of alite was accelerated, that of belite was retarded at a late stage.

  2. EFFECT OF PORTLAND-POZZOLAN CEMENTS ON CONCRETE MATURITY

    Directory of Open Access Journals (Sweden)

    Arın YILMAZ

    2004-03-01

    Full Text Available The maturity concept expressed by the combined effect of time and temperature on the concrete is a useful technique for prediction of the strength gain of concrete. According to maturity concept, samples of the same concrete at same maturity whatever combination of temperature and time, have approximately the same strength. Many maturity functions have been proposed for the last 50 years. The validity of these functions are only for ordinary portland cements. In this study, the suitable of traditional maturity functions for different types of Portland-pozzolan cements were investigated and a new maturity-strength relationship was tried to be established. For this purpose, four different pozzolans and one Portland cement was selected. Portland-pozzolan cements were prepared by using three different replacement amounts of % 5, % 20 and 40 % by weight of cement.

  3. HYDRATING CHARACTERISTICS OF MODIFIED PORTLAND WITH Ba-BEARING SULPHOALUMINATE MINERALS

    Directory of Open Access Journals (Sweden)

    Chenchen Gong

    2016-03-01

    Full Text Available The hydrating characteristics of modified Portland cement with Ba-bearing sulphoaluminate minerals were studied in this paper. Scanning Electron Microscopy-Energy Dispersive Spectrometer (SEM-EDS, mercury intrusion porosimeter (MIP and compressive strength were determined to characterize hydrating products and microstructure. Results show that basic physical properties of modified Portland cement with Ba-bearing sulphoaluminate minerals (SMPC are similar with PC except the shorter setting time. Ettringite and C-S-H are the main hydrating produces in SMPC, which is similar to Portland cement (PC. Because of volume expansion of ettringite, SMPC paste structure is denser than PC according to SEM-EDS analysis and the pore size and pore content of SMPC pastes was smaller especially for the harmful pores. Because sulfur aluminum barium calcium was a new early-strength mineral and parts of BaO went into the C₂S lattice and caused lattice distortion to enhance C₂S hydration activity, the compressive strengths of SMPC grew faster and higher than PC.

  4. Modification of Portland cement mortars with cactus gum

    OpenAIRE

    Hernandez-Zaragoza, Juan-Bosco; Caballero-Badillo, Carlos-Eduardo; Rosas-Juarez, Arnulfo; Lopez-Lara, Teresa; Hinojosa-Torres, Jaime; Castano, Victor-Manuel

    2007-01-01

    ????????, ?? ?????????? ??????? ?? ?????? ????????-???????, ??? ???????????????? ? ????????? ???????????, ???????????? ?????????? ?????????? ??????, ????????? ? ????????? ?????????????? ???????. ???????? ?????????? ???????? ??? ????????? ???????? ??? ????????? ?? 65 %, ????????? ?? ???????????? ?????????. Portland cement-based mortars of the standard type used for modern constructions, were modified by adding liophilized cactus gum, extracted froman indigenous Mexican cactus. The results show...

  5. Modification of Portland cement mortars with cactus gum

    OpenAIRE

    Hernandez-Zaragoza, Juan-Bosco; Caballero-Badillo, Carlos-Eduardo; Rosas-Juarez, Arnulfo; Lopez-Lara, Teresa; Hinojosa-Torres, Jaime; Castano, Victor-Manuel

    2007-01-01

    ????????, ?? ?????????? ??????? ?? ?????? ????????-???????, ??? ???????????????? ? ????????? ???????????, ???????????? ?????????? ?????????? ??????, ????????? ? ????????? ?????????????? ???????. ???????? ?????????? ???????? ??? ????????? ???????? ??? ????????? ?? 65 %, ????????? ?? ???????????? ?????????. Portland cement-based mortars of the standard type used for modern constructions, were modified by adding liophilized cactus gum, extracted froman indigenous Mexican cactus. The results show...

  6. Hydration of calcium aluminate cement determined by thermal analysis

    Science.gov (United States)

    Scheinherrová, Lenka; Trník, Anton

    2017-07-01

    Calcium aluminate cements (CACs) are a very important type of non-Portland or special cements. Since they are considerably more expensive, they are not used as a simple substitute for Portland cement. Their structure allows them to achieve high compressive strength. They resist very well to high temperatures and temperature changes, or also to chemical attacks. The original motivation, why the CACs were developed, was the idea of finding new cement chemistries that would be more resistant to sulfate attack then Portland cements. Nowadays, the main usage of the CACs is in high temperatures applications. In this paper, we study the hydration of a CAC up to one year of age to control what happens in CACs structure during aging. The variety in the main products of hydration is studied using differential scanning calorimetry and thermogravimetry in the temperature range from 25 °C to 1000 °C with a heating rate of 5 °C/min in an argon atmosphere. The basic physical and mechanical properties are also determined.

  7. The Influence of Diatomite on the Strength and Microstructure of Portland Cement

    Directory of Open Access Journals (Sweden)

    Liu Jun

    2016-01-01

    Full Text Available To study the influence of the types and mixing amount of diatomite on the Portland cement, we prepared the cement specimen doped with the calcined first-grade, first-grade and second-grade diatomite ,tested the 3d, 7d, 14d compressive strength, and studied and discussed phase, structure and morphology of diatomite in the binary system by the method of XRD, SEM . Experimental results show that with the addition of diatomite, the strength of cement paste increase; the optimal contents of calcined first-grade ,first-grade and second-grade diatomite in Portland cement are 5%,Compared to the blank group, the strength of specimen can be increased by 54.6%, 15.4% and 10.2%, respectively; At the same time ,the 7d microscopic hydration of different diatomite particles were analyzed through the experiment , and the shell of calcined diatomite particles were better hydrated than that of first-grade and second-grade diatomite particles. The results indicate that the diatomite can improve the strength of cement paste, the hydration of different diatomite particles can influence the growth of cement paste strength.

  8. 76 FR 50252 - Gray Portland Cement and Cement Clinker From Japan; Scheduling of an Expedited Five-Year Review...

    Science.gov (United States)

    2011-08-12

    ... COMMISSION Gray Portland Cement and Cement Clinker From Japan; Scheduling of an Expedited Five-Year Review Concerning the Antidumping Duty Order on Gray Portland Cement and Cement Clinker From Japan AGENCY: United... cement and cement clinker from Japan would be likely to lead to continuation or recurrence of...

  9. Performance Characteristics of Waste Glass Powder Substituting Portland Cement in Mortar Mixtures

    Science.gov (United States)

    Kara, P.; Csetényi, L. J.; Borosnyói, A.

    2016-04-01

    In the present work, soda-lime glass cullet (flint, amber, green) and special glass cullet (soda-alkaline earth-silicate glass coming from low pressure mercury-discharge lamp cullet and incandescent light bulb borosilicate glass waste cullet) were ground into fine powders in a laboratory planetary ball mill for 30 minutes. CEM I 42.5N Portland cement was applied in mortar mixtures, substituted with waste glass powder at levels of 20% and 30%. Characterisation and testing of waste glass powders included fineness by laser diffraction particle size analysis, specific surface area by nitrogen adsorption technique, particle density by pycnometry and chemical analysis by X-ray fluorescence spectrophotometry. Compressive strength, early age shrinkage cracking and drying shrinkage tests, heat of hydration of mortars, temperature of hydration, X-ray diffraction analysis and volume stability tests were performed to observe the influence of waste glass powder substitution for Portland cement on physical and engineering properties of mortar mixtures.

  10. Study of the action of phosphate ions contained in the mixing water on the hydration of a Portland cement; Etude de l'action des phosphates presents dans l'eau de gachage sur l'hydratation d'un ciment Portland

    Energy Technology Data Exchange (ETDEWEB)

    Benard, Ph

    2005-12-15

    Cementation is considered as the most attractive solution for the conditioning of low and intermediate radioactive wastes. The species contained in these wastes can strongly influence the reactivity of the cement pastes, it is in particular the case of the ortho-phosphate ions which are found in the evaporation concentrates. The aim of our work was to determine the influence of these ions on the hydration and the rheological properties of the cement pastes at early age as well as the mechanical and physical properties on the hardened material. (author)

  11. Laboratory Investigation on the Strength Gaining of Brick Aggregate Concrete Using Ordinary Portland Cement and Portland Composite Cement

    Directory of Open Access Journals (Sweden)

    Hoque M H, Numen E H, Islam N., Mohammed

    2014-05-01

    Full Text Available This study focused on the laboratory investigation of strength variation of brick aggregate concrete made with ordinary Portland cement (OPC and Portland composite cement (PCC.The investigation was conducted by testing concrete cylinder specimens at different ages of concrete with concrete mix ratios: 1:1.5:3 and 1:2:4 by volume and with water cement ratios=0.45 and 0.60. The test result reveals that at the early age, concrete composed with OPC attained larger compressive strength than the concrete made of PCC. However, in the later age concrete made with PCC achieved higher strength than OPC.

  12. DSC and TG Analysis of a Blended Binder Based on Waste Ceramic Powder and Portland Cement

    Science.gov (United States)

    Pavlík, Zbyšek; Trník, Anton; Kulovaná, Tereza; Scheinherrová, Lenka; Rahhal, Viviana; Irassar, Edgardo; Černý, Robert

    2016-03-01

    Cement industry belongs to the business sectors characteristic by high energy consumption and high {CO}2 generation. Therefore, any replacement of cement in concrete by waste materials can lead to immediate environmental benefits. In this paper, a possible use of waste ceramic powder in blended binders is studied. At first, the chemical composition of Portland cement and ceramic powder is analyzed using the X-ray fluorescence method. Then, thermal and mechanical characterization of hydrated blended binders containing up to 24 % ceramic is carried out within the time period of 2 days to 28 days. The differential scanning calorimetry and thermogravimetry measurements are performed in the temperature range of 25°C to 1000°C in an argon atmosphere. The measurement of compressive strength is done according to the European standards for cement mortars. The thermal analysis results in the identification of temperature and quantification of enthalpy and mass changes related to the liberation of physically bound water, calcium-silicate-hydrates dehydration and portlandite, vaterite and calcite decomposition. The portlandite content is found to decrease with time for all blends which provides the evidence of the pozzolanic activity of ceramic powder even within the limited monitoring time of 28 days. Taking into account the favorable results obtained in the measurement of compressive strength, it can be concluded that the applied waste ceramic powder can be successfully used as a supplementary cementing material to Portland cement in an amount of up to 24 mass%.

  13. Apatite formation on calcined kaolin-white Portland cement geopolymer.

    Science.gov (United States)

    Pangdaeng, S; Sata, V; Aguiar, J B; Pacheco-Torgal, F; Chindaprasirt, P

    2015-06-01

    In this study, calcined kaolin-white Portland cement geopolymer was investigated for use as biomaterial. Sodium hydroxide and sodium silicate were used as activators. In vitro test was performed with simulated body fluid (SBF) for bioactivity characterization. The formation of hydroxyapatite bio-layer on the 28-day soaked samples surface was tested using SEM, EDS and XRD analyses. The results showed that the morphology of hydroxyapatite was affected by the source material composition, alkali concentration and curing temperature. The calcined kaolin-white Portland cement geopolymer with relatively high compressive strength could be fabricated for use as biomaterial. The mix with 50% white Portland cement and 50% calcined kaolin had 28-day compressive strength of 59.0MPa and the hydroxyapatite bio-layer on the 28-day soaked sample surface was clearly evident. Copyright © 2015 Elsevier B.V. All rights reserved.

  14. Pavement management and rehabilitation of portland cement concrete pavements

    Science.gov (United States)

    Zegeer, C. V.; Agent, K. R.; Rizenbergs, R. L.; Curtayne, P. C.; Scullion, T.; Pedigo, R. D.; Hudson, W. R.; Roberts, F. L.; Karan, M. A.; Haas, R.

    Pavement management and rehabilitation projects and techniques are discussed. The following topics are discussed: economic analyses and dynamic programming in resurfacing project selection; implementation of an urban pavement management system; pavement performance modeling for pavement management; illustration of pavement management: from data inventory to priority analysis; rehabilitation of concrete pavements by using portland cement concrete overlays; pavement management study: Illinois tollway pavement overlays; resurfacing of plain jointed-concrete pavements; design procedure for premium composite pavement; model study of anchored pavement; prestressed concrete overlay at O'Hare International Airport: in-service evaluation; and, bonded portland cement concrete resurfacing.

  15. 77 FR 42367 - National Emission Standards for Hazardous Air Pollutants for the Portland Cement Manufacturing...

    Science.gov (United States)

    2012-07-18

    ... Standards for Hazardous Air Pollutants for the Portland Cement Manufacturing Industry and Standards of Performance for Portland Cement Plants; Proposed Rule #0;#0;Federal Register / Vol. 77 , No. 138 / Wednesday...-AQ93 National Emission Standards for Hazardous Air Pollutants for the Portland Cement...

  16. 76 FR 78240 - Gray Portland Cement and Clinker From Japan: Continuation of Antidumping Duty Order

    Science.gov (United States)

    2011-12-16

    ... International Trade Administration Gray Portland Cement and Clinker From Japan: Continuation of Antidumping Duty... antidumping duty order on gray portland cement and clinker from Japan, pursuant to section 751(c) of the... International Trade Commission (ITC) that revocation of the antidumping duty order on gray portland cement...

  17. Stabilization/solidification of selenium-impacted soils using Portland cement and cement kiln dust.

    Science.gov (United States)

    Moon, Deok Hyun; Grubb, Dennis G; Reilly, Trevor L

    2009-09-15

    Stabilization/solidification (S/S) processes were utilized to immobilize selenium (Se) as selenite (SeO(3)(2-)) and selenate (SeO(4)(2-)). Artificially contaminated soils were prepared by individually spiking kaolinite, montmorillonite and dredged material (DM; an organic silt) with 1000 mg/kg of each selenium compound. After mellowing for 7 days, the Se-impacted soils were each stabilized with 5, 10 and 15% Type I/II Portland cement (P) and cement kiln dust (C) and then were cured for 7 and 28 days. The toxicity characteristic leaching procedure (TCLP) was used to evaluate the effectiveness of the S/S treatments. At 28 days curing, P doses of 10 and 15% produced five out of six TCLP-Se(IV) concentrations below 10mg/L, whereas only the 15% C in DM had a TCLP-Se(IV) concentration phases for all three soil-cement slurries were calcium selenite hydrate (CaSeO(3).H(2)O) and selenate substituted ettringite (Ca(6)Al(2)(SeO(4))(3)(OH)(12).26H(2)O), respectively.

  18. Energy conservation potential of Portland Cement particle size distribution control

    Energy Technology Data Exchange (ETDEWEB)

    Tresouthick, S.W.

    1985-01-01

    The main objective of Phase 3 is to develop practical economic methods of controlling the particle size distribution of portland cements using existing or modified mill circuits with the principal aim of reducing electrical energy requirements for cement manufacturing. The work of Phase 3, because of its scope, will be carried out in 10 main tasks, some of which will be handled simultaneously. Progress on each of these tasks is discussed in this paper.

  19. Anti-Crack Performance of Low-Heat Portland Cement Concrete

    Institute of Scientific and Technical Information of China (English)

    2007-01-01

    The properties of low-heat Portland cement concrete(LHC) were studied in detail. The experimental results show that the LHC concrete has characteristics of a higher physical mechanical behavior, deformation and durability. Compared with moderate-heat Portland cement(MHC), the average hydration heat of LHC concrete is reduced by about 17.5%. Under same mixing proportion, the adiabatic temperature rise of LHC concrete was reduced by 2℃-3℃,and the limits tension of LHC concrete was increased by 10×10-6-15×10-6 than that of MHC. Moreover, it is indicated that LHC concrete has a better anti-crack behavior than MHC concrete.

  20. Stabilization/solidification of selenium-impacted soils using Portland cement and cement kiln dust

    Energy Technology Data Exchange (ETDEWEB)

    Moon, Deok Hyun, E-mail: dmoon10@hotmail.com [W.M. Keck Geoenvironmental Laboratory, Center for Environmental Systems, Stevens Institute of Technology, Hoboken, NJ 07030 (United States); Department of Environmental Engineering, Chosun University, Gwangju 501-759 (Korea, Republic of); Grubb, Dennis G. [W.M. Keck Geoenvironmental Laboratory, Center for Environmental Systems, Stevens Institute of Technology, Hoboken, NJ 07030 (United States); Schnabel Engineering, LLC, 510 East Gay Street, West Chester, PA 19380 (United States); Reilly, Trevor L. [W.M. Keck Geoenvironmental Laboratory, Center for Environmental Systems, Stevens Institute of Technology, Hoboken, NJ 07030 (United States)

    2009-09-15

    Stabilization/solidification (S/S) processes were utilized to immobilize selenium (Se) as selenite (SeO{sub 3}{sup 2-}) and selenate (SeO{sub 4}{sup 2-}). Artificially contaminated soils were prepared by individually spiking kaolinite, montmorillonite and dredged material (DM; an organic silt) with 1000 mg/kg of each selenium compound. After mellowing for 7 days, the Se-impacted soils were each stabilized with 5, 10 and 15% Type I/II Portland cement (P) and cement kiln dust (C) and then were cured for 7 and 28 days. The toxicity characteristic leaching procedure (TCLP) was used to evaluate the effectiveness of the S/S treatments. At 28 days curing, P doses of 10 and 15% produced five out of six TCLP-Se(IV) concentrations below 10 mg/L, whereas only the 15% C in DM had a TCLP-Se(IV) concentration <10 mg/L. Several treatments satisfied the USEPA TCLP best demonstrated available technology (BDAT) limits (5.7 mg/L) for selenium at pozzolan doses up to 10 times less than the treatments that established the BDAT. Neither pozzolan was capable of reducing the TCLP-Se(VI) concentrations below 25 mg/L. Se-soil-cement slurries aged for 30 days enabled the identification of Se precipitates by X-ray powder diffraction (XRD) and scanning electron microscopy (SEM)-energy dispersive X-ray spectroscopy (EDX). XRD and SEM-EDX analyses of the Se(IV)- and Se(VI)-soil-cement slurries revealed that the key selenium bearing phases for all three soil-cement slurries were calcium selenite hydrate (CaSeO{sub 3}.H{sub 2}O) and selenate substituted ettringite (Ca{sub 6}Al{sub 2}(SeO{sub 4}){sub 3}(OH){sub 12}.26H{sub 2}O), respectively.

  1. INFLUENCE OF POZZOLANA ON THE HYDRATION OF C4AF RICH CEMENT IN CHLORIDE ENVIRONMENT

    Directory of Open Access Journals (Sweden)

    IRMANTAS BARAUSKAS

    2013-03-01

    Full Text Available This study investigated the influence of natural pozzolana - opoka additive on the hydration of C4AF rich cement and the effects of chloride ions on the hydrates formed. In the samples, 25 % (by weight of the sintered C4AF rich cement and OPC was replaced with pozzolana. The mixtures were hardened for 28 days in water, soaked in a saturated NaCl solution for 3 months at 20°C. It was estimated that under normal conditions, pozzolana additive accelerates the hydration of calcium silicates and initiates the formation of CO32- - AFm in the Brownmillerite rich cement. However, the hydration of Brownmillerite cement with opoka additive is still slower to compare with hydration of Portland cement. Also, opoka decreases total porosity and threshold pore diameter of Brownmillerite cement paste after two days of hydration. After 28 days of hydration threshold pore diameter became smaller even to compare with threshold pore diameter of Portland cement. Opoka additive promotes the formation of Friedel’s salt in Brownmillerite samples treated in saturated NaCl solution, because CO32-–AFm affected by saturated NaCl solution become unstable and takes part in reactions producing Friedel’s salt.

  2. 水化普通硅酸盐水泥吸附水中氟化物的动力学与热力学解析%Kinetic and Thermodynamic Analysis of Fluoride Adsorption to Hydrated Portland Cement

    Institute of Scientific and Technical Information of China (English)

    曹艳; 任勇翔; 黄廷林; 张宏伟; 孙艳君

    2012-01-01

    The kinetic and thermodynamic processes of fluoride adsorption to hydrated Portland cement (HPC) were studied. The results indicated that the adsorption equilibrium was reached in 192 h, and the adsorption capacities were 14. 63 mg/g at 20 ℃ and 13. 14 mg/g at 4 ℃. Kinetic data were well described by the pseudo-second-order model, and the adsorption rate was controlled by the intra-particle diffusion. The fluoride adsorption behavior of the particles of HPC was appropriately fitted to the Langmuir isotherm. The adsorption enthalpy change of 16. 56 kJ/mol indicated that the adsorption process was mainly a chemical adsorption, and the adsorption was an endothermic reaction. The positive entropy change meant that the randomness was increased at the solid/solution interface during the adsorption of fluoride onto HPC. The adsorption of fluoride to HPC was a spontaneous process, since the changes of adsorption Gibbs free energy were negative at both 4 and 20 X.. The results of the desorption study and XRD analysis also suggested that the process of fluoride adsorption by HPC was mainly a chemical adsorption.%以水化普通硅酸盐水泥颗粒为除氟吸附剂,对其吸附水中氟化物的动力学和热力学过程进行了解析.结果表明:水化普通硅酸盐水泥对氟化物的吸附平衡时间为192 h,20℃时其吸附容量为14.63 mg/g,4℃时为13.14 mg/g.吸附速率特性与准二级动力学模型拟合性较好且吸附速率由颗粒内部扩散速率控制,吸附行为均满足Langmuir吸附等温式.吸附焓变为16.56 kJ/mol,表明该吸附过程是以化学吸附为主的吸热反应;吸附熵变为正值,说明该吸附过程是熵推动为主的过程;吉布斯自由能在4和20℃时均为负值,说明该吸附反应是一个自发过程.脱附研究与XRD分析结果也证实,该吸附反应以化学吸附过程为主.

  3. Bioactive coatings on Portland cement substrates: Surface precipitation of apatite-like crystals

    Energy Technology Data Exchange (ETDEWEB)

    Gallego, Daniel [Biomedical Engineering Department, Ohio State University, 1080 Carmack Road, 270 Bevis Hall, Columbus (OH) - 43210 (United States); Higuita, Natalia [Biomedical Engineering Department, Ohio State University, 1080 Carmack Road, 270 Bevis Hall, Columbus (OH) - 43210 (United States); Grupo de Investigacion en Ingenieria Biomedica CES-EIA (GIBEC), Carrera 43 A No. 52 Sur - 99, Sabaneta (Colombia); Garcia, Felipe [Grupo de Investigacion en Ingenieria Biomedica CES-EIA (GIBEC), Carrera 43 A No. 52 Sur - 99, Sabaneta (Colombia); Ferrell, Nicholas [Biomedical Engineering Department, Ohio State University, 1080 Carmack Road, 270 Bevis Hall, Columbus (OH) - 43210 (United States); Hansford, Derek J. [Biomedical Engineering Department, Ohio State University, 1080 Carmack Road, 270 Bevis Hall, Columbus (OH) - 43210 (United States)], E-mail: hansford.4@osu.edu

    2008-04-01

    We report a method for depositing bioactive coatings onto cement materials for bone tissue engineering applications. White Portland cement substrates were hydrated under a 20% CO{sub 2} atmosphere, allowing the formation of CaCO{sub 3}. The substrates were incubated in a calcium phosphate solution for 1, 3, and 6 days (CPI, CPII, and CPIII respectively) at 37 deg. C to induce the formation of carbonated apatite. Cement controls were prepared and hydrated with and without CO{sub 2} atmosphere (C+ and C- respectively). The presence of apatite-like crystals was verified by Scanning Electron Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS). The substrate cytocompatibility was evaluated via SEM after 24 hour cell cultures. SEM revealed the presence Ca(OH){sub 2} on C-, and CaCO{sub 3} on C+. Apatite-like crystals were detected only on CPIII, confirmed by phosphorus EDS peaks only for CPIII. Cells attached and proliferated similarly well on all the substrates except C-. These results prove the feasibility of obtaining biocompatible and bioactive coatings on Portland cement for bone tissue engineering applications.

  4. Experimental determination of carbonation rate in Portland cement at 25°C and relatively high CO2 partial pressure

    Science.gov (United States)

    Hernández-Rodríguez, Ana; Montegrossi, Giordano; Huet, Bruno; Virgili, Giorgio; Orlando, Andrea; Vaselli, Orlando; Marini, Luigi

    2016-04-01

    The aim of this work is to study the alteration of Portland class G Cement at ambient temperature under a relatively high CO2 partial pressure through suitably designed laboratory experiments, in which cement hydration and carbonation are taken into account separately. First, the hydration process was carried out for 28 days to identify and quantify the hydrated solid phases formed. After the completion of hydration, accompanied by partial carbonation under atmospheric conditions, the carbonation process was investigated in a stirred micro-reactor (Parr instrument) with crushed cement samples under 10 bar or more of pure CO2(g) and MilliQ water adopting different reaction times. The reaction time was varied to constrain the reaction kinetics of the carbonation process and to investigate the evolution of secondary solid phases. Chemical and mineralogical analyses (calcimetry, chemical composition, SEM and X-ray Powder Diffraction) were carried out to characterize the secondary minerals formed during cement hydration and carbonation. Water analyses were also performed at the end of each experimental run to measure the concentrations of relevant solutes. The specific surface area of hydrated cement was measured by means of the BET method to obtain the rates of cement carbonation. Experimental outcomes were simulated by means of the PhreeqC software package. The obtained results are of interest to understand the comparatively fast cement alteration in CO2 production wells with damaged casing.

  5. Cement with silica fume and granulated blast-furnace slag: strength behavior and hydration

    Directory of Open Access Journals (Sweden)

    Bonavetti, V. L.

    2014-09-01

    Full Text Available This paper analyses the influence of portland cement replacement by silica fume (up to 10% and/or granulated blast furnace slag (up to 70% on the hydration cement (XRD, heat of hydration, non evaporable water content and calcium hydroxide content curing under sealed conditions and their effect on the mechanical strength. The obtained results indicate that binary cements containing silica fume and ternary cements there was a significant increase of hydration rate at early age. At later ages, most of studied cements have an equivalent or greater strength that those obtained in the plain portland cement.En este trabajo se analiza la influencia de la incorporación al cemento portland de humo de sílice (hasta 10% y/o escoria granulada de alto horno (hasta 70% sobre la hidratación (DRX, calor de hidratación, contenido de agua no evaporable y de hidróxido de calcio, bajo condiciones de curado sellado y su incidencia sobre la resistencia mecánica. Los resultados obtenidos indican que en los cementos binarios con humo de sílice y en los cementos ternarios se produce un importante aumento de la velocidad de hidratación en las primeras edades, mientras que a edades más avanzadas la mayor parte del dominio estudiado alcanza o supera la resistencia obtenida por el cemento portland sin adición.

  6. 78 FR 10005 - National Emission Standards for Hazardous Air Pollutants for the Portland Cement Manufacturing...

    Science.gov (United States)

    2013-02-12

    ... Standards for Hazardous Air Pollutants for the Portland Cement Manufacturing Industry and Standards of Performance for Portland Cement Plants; Final Rule #0;#0;Federal Register / Vol. 78 , No. 29 / Tuesday... RIN 2060-AQ93 National Emission Standards for Hazardous Air Pollutants for the Portland...

  7. Applications of solid-state Nuclear Magnetic Resonance (NMR) in studies of Portland cements-based materials

    DEFF Research Database (Denmark)

    Skibsted, Jørgen; Andersen, Morten Daugaard; Jakobsen, Hans Jørgen

    2007-01-01

    Solid-state NMR spectroscopy represents an important research tool in the characterization of a range of structural properties for cement-based materials. Different approaches of the technique can be used to obtain information on hydration kinetics, mobile and bound water, porosity, and local...... atomic structures. After a short introduction to these NMR techniques, it is exemplified how magic-angle spinning (MAS) NMR can provide quantitative and structural information about specific phases in anhydrous and hydrated Portland cements with main emphasis on the incorporation of Al3+ ions...

  8. Long-term Performance of Moderate Heat Portland Cement with Double-expansive Sources

    Institute of Scientific and Technical Information of China (English)

    YE Qing; CHEN Huxing; KONG Deyu; WANG Shangxian; LOU Zonghan

    2007-01-01

    The long-term performance of moderate heat Portland cement with double-expansive sources (DE cement) in the system of high MgO clinker and gypsum was studied by XRD, SEM/EDAX and test methods for strength and expansion of cement. Results indicate that the periclase particle, whose size was 5-7.5 μm in DE cement clinker containing 4.8 % MgO, existed individually. The periclase hydration in hardened DE cement paste started at about 60 days and completed up to 2 000 days, and ettringite in the paste was stable from 3 days to 2 000 days. Under the conditions of 4.5%-5.0 % MgO in clinker and 2.8%-3.4 %SO3 in cement,ettringite expansion and brucite expansion in DE cement paste had a continuity, entirety and stability. At the ages of 90, 365, 730 and 2 000 days the expansion of the paste reached 0.07%-0.11%, 0.16%-0.21%, 0.21%-0.27% and 0.29%-0.38 %, respectively. The results suggest that by using this cement in mass concrete it may compensate its temperature shrinkage and autogenous shrinkage to some extent.

  9. Portland cement hydration: study of various techniques

    Directory of Open Access Journals (Sweden)

    Triviño Vázquez, F.

    1974-06-01

    Full Text Available Not availableLa complejidad de la química del cemento es motivo de que aún hoy día permanezcan sin aclarar muchos procesos que transcurren durante el fraguado y posterior endurecimiento de la pasta. La industria de la construcción precisa de un conocimiento técnico más sólido, ya que al saber el modo de actuar de los componentes de la pasta del cemento puede conseguir de este material: facilidad y economía en su empleo, resistencias mecánicas elevadas e inalterabilidad y duración en las obras realizadas. Cualquier nuevo conocimiento sobre la química de la pasta, por ello, suele tener inmediata aplicación o sirve como base para ulteriores investigaciones, que en su día darán nuevas propiedades prácticas al cemento o incluso a otros materiales diferentes. El comportamiento de la pasta durante las primeras 24 horas ha sido el motivo de este estudio. Se efectuaron medidas térmicas, de conductividad, de contenidos de productos solubles en agua, de productos cristalinos y de variaciones de solicitación de agua, por los métodos que veremos a continuación.

  10. Analysis of Chemical Composition of Portland Cement in Ghana: A Key to Understand the Behavior of Cement

    Directory of Open Access Journals (Sweden)

    Mark Bediako

    2015-01-01

    Full Text Available The performance of Portland cement in concrete or mortar formation is very well influenced by chemical compositions among other factors. Many engineers usually have little information on the chemical compositions of cement in making decisions for the choice of commercially available Portland cement in Ghana. This work analyzed five different brands of Portland cement in Ghana, namely, Ghacem ordinary Portland cement (OPC and Portland limestone cement (PLC, CSIR-BRRI Pozzomix, Dangote OPC, and Diamond PLC. The chemical compositions were analyzed with X-Ray Fluorescence (XRF spectrometer. Student’s t-test was used to test the significance of the variation in chemical composition between standard literature values and each of the commercial cement brands. Analysis of variance (ANOVA was also used to establish the extent of variations between chemical compositions and brand name of the all commercial Portland cement brands. Student’s t-test results showed that there were no significant differences between standard chemical composition values and that of commercial Portland cement. The ANOVA results also indicated that each brand of commercial Portland cement varies in terms of chemical composition; however, the specific brands of cement had no significant differences. The study recommended that using any brand of cement in Ghana was good for any construction works be it concrete or mortar formation.

  11. Vibrational study on the bioactivity of Portland cement-based materials for endodontic use

    Science.gov (United States)

    Taddei, P.; Tinti, A.; Gandolfi, M. G.; Rossi, P. L.; Prati, C.

    2009-04-01

    The bioactivity of a modified Portland cement (wTC) and a phosphate-doped wTC cement (wTC-P) was studied at 37 °C in Dulbecco's Phosphate Buffered Saline (DPBS). The cements, prepared as disks, were analysed at different ageing times (from 1 day to 2 months) by micro-Raman and ATR/FT-IR spectroscopies. The presence of deposits on the surface of the cements and the composition changes as a function of the storage time were investigated. The presence of an apatite deposit on the surface of both cements was already revealed after one day of ageing in DPBS. The trend of the I 965/I 991 Raman intensity ratio indicated the formation of a meanly thicker apatite deposit on the wTC-P cement at all the investigated times. This result was confirmed by the trend of the I 1030/I 945 IR intensity ratio calculated until 14 days of ageing. At 2 months, the thickness of the apatite deposit on wTC and wTC-P was about 200 and 500 μm, respectively, as estimated by micro-Raman spectroscopy, confirming the higher bioactivity of the phosphate-doped cement. Vibrational techniques allowed to gain more insights into the cement transformation and the different hydration rates of the various cement component. The setting of the cement and the formation of the hydrated silicate gel (C-S-H phase) was spectroscopically monitored through the I 830/I 945 IR intensity ratio.

  12. Mechanical Properties and Microstructure of Portland Cement Concrete Prepared with Coral Reef Sand

    Institute of Scientific and Technical Information of China (English)

    WANG Qiankun; LI Peng; TIAN Yapo; CHEN Wei; SU Chunyi

    2016-01-01

    The feasibility of using coral reef sand (CRS) in Portland cement concrete is investigated by testing the mechanical property and microstructure of concrete. The composition, structure and properties of the CRS are analyzed. Mechanical properties and microstructure of concrete with CRS are studied and compared to concrete with natural river sand. The relationship between the microstructure and performance of CRS concrete is established. The CRS has a porous surface with high water intake capacity, which contributes to the mechanical properties of concrete. The interfacial transition zone between the cement paste and CRS is densiifed compared to normal concrete with river sand. Hydration products form in the pore space of CRS and interlock with the matrix of cement paste, which increases the strength. The total porosity of concrete prepared with CRS is higher than that with natural sand. The main difference in pore size distribution is the fraction of ifne pores in the range of 100 nm.

  13. Solidification of ion exchange resins saturated with Na+ ions: Comparison of matrices based on Portland and blast furnace slag cement

    Science.gov (United States)

    Lafond, E.; Cau dit Coumes, C.; Gauffinet, S.; Chartier, D.; Stefan, L.; Le Bescop, P.

    2017-01-01

    This work is devoted to the conditioning of ion exchange resins used to decontaminate radioactive effluents. Calcium silicate cements may have a good potential to encapsulate spent resins. However, certain combinations of cement and resins produce a strong expansion of the final product, possibly leading to its full disintegration. The focus is placed on the understanding of the behaviour of cationic resins in the Na+ form in Portland or blast furnace slag (CEM III/C) cement pastes. During hydration of the Portland cement paste, the pore solution exhibits a decrease in its osmotic pressure, which causes a transient expansion of small magnitude of the resins. At 20 °C, this expansion takes place just after setting in a poorly consolidated material and is sufficient to induce cracks. In the CEM III/C paste, swelling of the resins also occurs, but before the end of setting, and induces limited stress in the matrix which is still plastic.

  14. Early hydration cement Effect of admixtures superplasticizers

    Directory of Open Access Journals (Sweden)

    Puertas, F.

    2001-06-01

    Full Text Available Early hydration of portland cement with superplasticizer admixtures of different nature has been studied. These admixtures were: one based on melamine synthetic, other based on vinyl copolymer and other based on polyacrylate copolymers. The dosage of the formers were constant (1% weigth of cement and for the third, the influence of admixture dosage was also evaluated, giving dosage values among 1-0.3%. The pastes obtained were studied by conduction calorimetry, XRD and FTIR. Also the apparent fluidity was determined by "Minislump" test. The main results obtained were: a superplasticizers admixtures used, regardless of their nature and for the polycarboxilate one the dosage, retard the silicate hydration (specially, alite phase, b The ettringite formation is affected by the nature of the admixture. cA relationship between the dosage of admixture based on polycarboxilates and the time at the acceleration has been established. A lineal relation (y = 11.03 + 16.05x was obtained. From these results is possible to know, in function of dosage admixture, the time when the masive hydration products and the setting times are produced. Also the total heat releases in these reactions is independent of the nature and dosage of admixture, saying that in all cases the reactions are the same.

    En el presente trabajo se ha estudiado la hidratación inicial de un cemento portland aditivado con superplastificantes de diferente naturaleza. Dichos aditivos fueron: uno basado en melaminas sintéticas, otro en copolímeros vinilicos y otro en policarboxilatos. La dosificación de los dos primeros se fijó constante en 1% en peso con relación al cemento, mientras que para el tercero se evaluó, también, la influencia de la dosificación, tomando proporciones desde el 1% hasta el 0,3%. Las pastas obtenidas se estudiaron por: calorimetría de conducción, DRX y FTIR. También se determinó la fluidez de la pasta a través del ensayo del "Minislump ". Los

  15. Early and late hydration of supersulphated cements of blast furnace slag with fluorgypsum

    Directory of Open Access Journals (Sweden)

    Bazaldúa-Medellín, M. E.

    2015-03-01

    Full Text Available The hydration, strength development and composition of hydration products of supersulphated cements were characterized from the first 48 hours up to 360 days. Two compositions of 80% Blast furnace slag, 10–15% Fluorgypsum and 10–5% Portland cement were cured in dry and wet conditions. The main hydration products were ettringite and C-S-H since the first hours and up to 360 days as evidenced by X-ray diffraction, thermal analysis and electron microscopy. The strength was favored by higher fluorgypsum contents and lower Portland cement contents. These cements generated heats of hydration of 40–57 KJ/Kg after 28 hours, which are lower than portland cement.Se realizó la caracterización de la hidratación, desarrollo de resistencia y la composición de los productos de hidratación de los cementos supersulfatados durante las primeras 48 horas y hasta 360 días. Se estudiaron dos composiciones de 80% de Escoria de alto horno, 10–15% de Fluoryeso y 10–5% de Cemento portland, se curaron en condiciones secas y húmedas. Los principales productos de hidratación fueron etringita y C-S-H desde las primeras horas y hasta 360 días, como se evidenció por difracción de rayos X, análisis térmico y microscopía electrónica de barrido. La resistencia se favoreció con mayor contenido de fluoryeso y bajos contenidos de cemento portland. Estos cementos generaron calores de hidratación de 40–57 KJ/Kg después de 28 horas, los cuales resultan más bajos que los generados por el cemento portland.

  16. Scrap tire ashes in portland cement production

    Directory of Open Access Journals (Sweden)

    Mónica Adriana Trezza

    2009-01-01

    Full Text Available Scrap tires are not considered harmful waste, but their stocking and disposal are a potential health and environmental risk. Properly controlled calcinations at high temperatures make tire combustion an interesting alternative due to its high calorific power, comparable to that of fuel-oil. Consequently, using them as an alternative combustible material in cement kilns makes it possible to give it a valuable use. However, it remains to be assured whether the impurities added to the clinker through these fuels do not affect its structure or properties.This paper shows the studies carried out on different clinkers under laboratory conditions with different levels of addition of scrap tire ashes, added by partially replacing traditional fuel in cement kilns.

  17. Polypropylene Fibers in Portland Cement Concrete Pavements.

    Science.gov (United States)

    1992-08-01

    Bibliography on Fiber- Reinforced Cement and Concrete," Miscellaneous Paper C-76-6, with supplements 1, 2, 3, and 4 ( 1977 , 1979, 1980, and 1982), US Army... Mindess , S., Bentur, A., Yan, C., and Vondran, G., "Impact Resistance of Concrete Containing Both Conventional Steel Reinforcement and Fibrillated...Roads, Streets, Walks, and Open Storage Areas," TM 5-822-6/AFM 88-7, Chap. 7, Washington, DC, 1977 . 18. __ , "Concrete Floor Slabs on Grade Subjected

  18. Rheological Properties of Very High-Strength Portland Cement Pastes: Influence of Very Effective Superplasticizers

    OpenAIRE

    Adriano Papo; Luciano Piani; Riccardo Ricceri

    2010-01-01

    The influence of the addition of very effective superplasticizers, that are commercially available, employed for maximising the solid loading of very high-strength Portland cement pastes, has been investigated. Cement pastes were prepared from deionized water and a commercially manufactured Portland cement (Ultracem 52.5 R). Cement and water were mixed with a vane stirrer according to ASTM Standard C305. The 0.38 to 0.44 water/cement ratio range was investigated. Three commercial superplastic...

  19. Evaluation of Compatibility between Beetle-Killed Lodgepole Pine (Pinus Contorta var. Latifolia Wood with Portland Cement

    Directory of Open Access Journals (Sweden)

    Ian D. Hartley

    2010-12-01

    Full Text Available The compatibility of wood from mountain pine beetle (Dendroctonus ponderosa killed lodgepole pine (Pinus contorta var. latifolia with Portland cement was investigated based on time-since-death as a quantitative estimator, and the presence of blue-stained sapwood, brown rot, or white rot as qualitative indicators. The exothermic behavior of cement hydration, maximum heat rate, time to reach this maximum, and total heat released within a 3.5–24 h interval were used for defining a new wood-cement compatibility index (CX. CX was developed and accounted for large discrepancies in assessing wood-cement compatibility compared to the previous methods. Using CX, no significant differences were found between fresh or beetle-killed wood with respect to the suitability for cement; except for the white rot samples which reached or exceeded the levels of incompatibility. An outstanding physicochemical behavior was also found for blue-stained sapwood and cement, producing significantly higher compatibility indices.

  20. Alkali segregation in Portland cement pastes

    Directory of Open Access Journals (Sweden)

    Triviño, F.

    1966-09-01

    Full Text Available Not availableEn el presente trabajo se pone de manifiesto experimentalmente la formación y presencia de aphthitalita -sulfato doble de potasio y sodio en la relación S04K2/S04Na2 = 3/1 en las pastas puras de cemento portland, desde el comienzo del fraguado de las mismas. Se estudia el mecanismo de la citada formación, íntimamente relacionada con el proceso general de formación de eflorescencias salinas, a base de una emigración de sulfatos alcalinos hacia las partes externas de las pastas, en virtud de fenómenos de exudación equivalentes a arrastres capilares. Se sintetiza y aísla la aphthitalita por dos procedimientos y se obtiene su difractograma.de rayos· X, a efectos de su identificación y de la confirmación de los resultados experimentales obtenidos, así como de la interpretación de los mismos.

  1. Incorporation of phosphorus guest ions in the calcium silicate phases of Portland cement from 31P MAS NMR spectroscopy.

    Science.gov (United States)

    Poulsen, Søren L; Jakobsen, Hans J; Skibsted, Jørgen

    2010-06-21

    Portland cements may contain small quantities of phosphorus (typically below 0.5 wt % P(2)O(5)), originating from either the raw materials or alternative sources of fuel used to heat the cement kilns. This work reports the first (31)P MAS NMR study of anhydrous and hydrated Portland cements that focuses on the phase and site preferences of the (PO(4))(3-) guest ions in the main clinker phases and hydration products. The observed (31)P chemical shifts (10 to -2 ppm), the (31)P chemical shift anisotropy, and the resemblance of the lineshapes in the (31)P and (29)Si MAS NMR spectra strongly suggest that (PO(4))(3-) units are incorporated in the calcium silicate phases, alite (Ca(3)SiO(5)) and belite (Ca(2)SiO(4)), by substitution for (SiO(4))(4-) tetrahedra. This assignment is further supported by a determination of the spin-lattice relaxation times for (31)P in alite and belite, which exhibit the same ratio as observed for the corresponding (29)Si relaxation times. From simulations of the intensities, observed in inversion-recovery spectra for a white Portland cement, it is deduced that 1.3% and 2.1% of the Si sites in alite and belite, respectively, are replaced by phosphorus. Charge balance may potentially be achieved to some extent by a coupled substitution mechanism where Ca(2+) is replaced by Fe(3+) ions, which may account for the interaction of the (31)P spins with paramagnetic Fe(3+) ions as observed for the ordinary Portland cements. A minor fraction of phosphorus may also be present in the separate phase Ca(3)(PO(4))(2), as indicated by the observation of a narrow resonance at delta((31)P) = 3.0 ppm for two of the studied cements. (31)P{(1)H} CP/MAS NMR spectra following the hydration of a white Portland cement show that the resonances from the hydrous phosphate species fall in the same spectral range as observed for (PO(4))(3-) incorporated in alite. This similarity and the absence of a large (31)P chemical shift ansitropy indicate that the hydrous (PO(4

  2. Glass powder blended cement hydration modelling

    Science.gov (United States)

    Saeed, Huda

    The use of waste materials in construction is among the most attractive options to consume these materials without affecting the environment. Glass is among these types of potential waste materials. In this research, waste glass in powder form, i.e. glass powder (GP) is examined for potential use in enhancing the characteristics of concrete on the basis that it is a pozzolanic material. The experimental and the theoretical components of the work are carried out primarily to prove that glass powder belongs to the "family" of the pozzolanic materials. The chemical and physical properties of the hydrated activated glass powder and the hydrated glass powder cement on the microstructure level have been studied experimentally and theoretically. The work presented in this thesis consists of two main phases. The first phase contains experimental investigations of the reaction of glass powder with calcium hydroxide (CH) and water. In addition, it includes experiments that are aimed at determining the consumption of water and CH with time. The reactivity, degree of hydration, and nature of the pore solution of the glass powder-blended cement pastes and the effect of adding different ratios of glass powder on cement hydration is also investigated. The experiments proved that glass powder has a pozzolanic effect on cement hydration; hence it enhances the chemical and physical properties of cement paste. Based on the experimental test results, it is recommended to use a glass powder-to-cement ratio (GP/C) of 10% as an optimum ratio to achieve the best hydration and best properties of the paste. Two different chemical formulas for the produced GP C-S-H gel due to the pure GP and GP-CH pozzolanic reaction hydration are proposed. For the pure GP hydration, the produced GP C-S-H gel has a calcium-to-silica ratio (C/S) of 0.164, water-to-silica ratio (H/S) of 1.3 and sodium/silica ratio (N/S) of 0.18. However, for the GP-CH hydration, the produced GP C-S-H gel has a C/S ratio of 1

  3. Effect of fly ash on the optimum sulfate of Portland Cement

    Science.gov (United States)

    Niemuth, Mark D.

    Calcium sulfate is typically added to ordinary portland cement (OPC) clinker during grinding to prevent flash set and to improve early-age strength development without causing volume instabilities. Recent changes to ASTM C150, Standard Specification for Portland Cement, have enabled greater flexibility in determining optimum sulfate levels in portland cement by not requiring ASTM C563, Approximation of Optimum SO3 in Hydraulic Cement Using Compressive Strength, to be used in setting sulfate target levels. ASTM C563 requires strength testing using only the hydraulic cement, which is not always indicative of the optimum sulfate for field use, since supplementary materials (e.g., fly ash) may be used by the concrete producer. Adding additional sulfate to account for the sulfate demand of fly ashes can enable an improvement in the early age strength for cement-fly ash systems and decrease in problems that may be attributed to OPC-admixture-fly ash incompatibility such as abnormal setting and slow strength gain. This thesis provides experimental data on the strength development and heat release during early hydration for cement-fly ash systems with different sulfate levels. The thesis focused on high calcium fly ashes, but low calcium fly ash was also tested. It is demonstrated that some fly ashes have their own sulfate demand and when these ashes are used in cement-fly ash blends there is effectively an increase in the optimal sulfate level that could be used for the OPC. It is also shown that optimum sulfate determined by heat of hydration measured with isothermal calorimetry is similar to the optimum sulfate determined by compressive strength at 1 day. Using isothermal calorimetry can result in substantial time and cost savings at plants for determining the optimal sulfate content. Theories for the mechanisms that drive the differences in sulfate demand in OPC are reviewed. These theories are adapted for OPC-fly ash blends and are outlined, tested and discussed. The

  4. Effects of composition and exposure on the solar reflectance of Portland cement concrete

    Energy Technology Data Exchange (ETDEWEB)

    Levinson, Ronnen; Akbari, Hashem

    2001-12-21

    Increasing the solar reflectance (albedo) of a paved surface keeps it cooler in the sun, reducing convection of heat from pavement to air and thereby decreasing the ambient air temperature. Simulations of the influence of pavement albedo on air temperature in Los Angeles predict that increasing the albedo of 1,250 km2 of pavement by 0.25 would save cooling energy worth $15M yr-1, and reduce smog-related medical and lost-work expenses by $76M yr-1. Most sidewalks and a small fraction of roads and parking areas are paved with portland cement concrete, which can be made quite reflective through suitable choice of cement and aggregate. Variations with composition and environmental exposure of the albedos of portland cement concrete pavements were investigated through laboratory fabrication and exposure of 32 mixes of concrete. Twenty-four mixes yielded substandard, ''rough'' concretes due to high, unmet aggregate water demand. The albedos of the remaining eight ''smooth'' concrete mixes ranged from 0.41 to 0.77 (mean 0.59). Simulated weathering, soiling, and abrasion each reduced average concrete albedo (mean decreases 0.06, 0.05, and 0.19, respectively), though some samples became slightly more reflective through weathering or soiling. Simulated rain (wetting) strongly depressed the albedos of concretes (mean decrease 0.23) until their surfaces were dried. Concrete albedo grew as the cement hydration reaction progressed (mean increase 0.08), but stabilized within six weeks of casting. White-cement concretes were on average significantly more reflective than gray-cement concretes. The albedo of the most-reflective white-cement concrete was 0.18 to 0.39 higher than that of the most-reflective gray-cement concrete, depending on state of exposure. Concrete albedo generally correlated with cement albedo and sand albedo, and, after abrasion, with rock albedo. Cement albedo had a disproportionately strong influence on the reflectance

  5. Waste brick's potential for use as a pozzolan in blended Portland cement.

    Science.gov (United States)

    Lin, Kae-Long; Chen, Bor-Yann; Chiou, Chyow-San; An Cheng

    2010-07-01

    This study investigated the pozzolanic reactions and engineering properties of waste brick-blended cements in relation to various replacement ratios (0-50%). The waste brick consisted of SiO(2) (63.21%), Al(2)O(3) (16.41%), Fe(2)O(3) (6.05%), Na(2)O (1.19%), K(2)O (2.83%) and MgO (1.11%), and had a pozzolanic activity index of 107%. The toxic characteristic leaching procedure (TCLP) results demonstrate that the heavy-metal content in waste bricks met the Environmental Protection Agency regulatory limits. Experimental results indicate that 10, 20, 30, 40 and 50% of cement can be replaced by waste brick, which causes the initial and final setting times to increase. Compressive strength development was slower in waste brick-blended cement (WBBC) pastes in the early ages; however, strength at the later ages increased significantly. Species analyses demonstrate that the hydrates in WBBC pastes primarily consisted of Ca(OH)(2) and calcium silicate hydrate (C-S-H) gel, like those found in ordinary Portland cement (OPC) paste. Pozzolanic reaction products formed in the WBBC pastes, in particular, various reaction products, including hydrates of calcium silicates (CSH), aluminates (CAH) and aluminosilicates (CASH), formed as expected, resulting in consumption of Ca(OH)(2) during the late ages of curing. The changes in the properties of WBBC pastes were significant as blend ratio increased, due to the pores of C-S-H gels and CAH filling via pozzolanic reactions. This filling of gel pores resulted in densification and subsequently enhanced the gel/space ratio and degree of hydration. Experimental results demonstrate waste brick can be supplementary cementitious material.

  6. Solidification/Stabilization of Fly Ash from a Municipal Solid Waste Incineration Facility Using Portland Cement

    Directory of Open Access Journals (Sweden)

    Qiang Tang

    2016-01-01

    Full Text Available This study investigated the solidification/stabilization of fly ash containing heavy metals using the Portland cement as a binder. It is found that both the cement/fly ash ratio and curing time have significant effects on the mechanical (i.e., compressive strength and leaching behaviors of the stabilized fly ash mixtures. When the cement/fly ash ratio increases from 4 : 6 to 8 : 2, the increase of compressive strength ratio raises from 42.24% to 80.36%; meanwhile, the leaching amount of heavy metals decreases by 2.33% to 85.23%. When the curing time increases from 3 days to 56 days, the compressive strength ratio of mixtures raises from 240.00% to 414.29%; meanwhile, the leaching amount of heavy metals decreases by 16.49% to 88.70%. The decrease of compressive strength with the lower cement/fly ash ratios and less curing time can be attributed to the increase of fly ash loading, which hinders the formation of ettringite and destroys the structure of hydration products, thereby resulting in the pozzolanic reaction and fixation of water molecules. Furthermore, the presence of cement causes the decrease of leaching, which results from the formation of ettringite and the restriction of heavy metal ion migration in many forms, such as C-S-H gel and adsorption.

  7. Distribution of sulfate between phases in Portland cement clinkers

    Energy Technology Data Exchange (ETDEWEB)

    Taylor, H.F.W.

    1999-08-01

    Sulfate can occur in Portland cement clinkers as alkali sulfates, potassium calcium sulfate (calcium langbeinite), anhydrite, and as a substituent in the major phases, especially alite and belite. Data for the contents in alit and belite are reviewed and relations to bulk clinker composition are discussed. Evidence on sulfate distribution from extraction procedures is similarly considered. A procedure for predicting sulfate distribution from bulk composition is described and tested and potential sources of error in such calculations are discussed. The evidence does not support suggests that, in concrete made with present-day cements and not subjected to an elevated temperature, damage through delayed ettringite formation can occur for reasons connected with the SO{sub 3} present in the clinker.

  8. Molecular Dynamics Modeling of Hydrated Calcium-Silicate-Hydrate (CSH) Cement Molecular Structure

    Science.gov (United States)

    2014-08-30

    properties of key hydrated cement constituent calcium-silicate-hydrate (CSH) at the molecular, nanometer scale level. Due to complexity, still unknown...public release; distribution is unlimited. Molecular Dynamics Modeling of Hydrated Calcium-Silicate- Hydrate (CSH) Cement Molecular Structure The views... Cement Molecular Structure Report Title Multi-scale modeling of complex material systems requires starting from fundamental building blocks to

  9. A Binder of Phosphogypsum-Ground Granulated Blast Furnace Slag-Ordinary Portland Cement

    Institute of Scientific and Technical Information of China (English)

    HUANG Yun; LIN Zongshou

    2011-01-01

    A new hydraulic cementitious binder was developed by mainly utilizing industrial byproducts phosphogypsum (PG) and ground granulated blast furnace slag (GGBFS) with small addition of ordinary portland cement (OPC). The hydration process and microstructure were studied by X-ray diffraction (XRD)and scanning electronic microscopy (SEM). OPC hydrated first at early age to form primarily C-S-H gel, ettringite and calcium hydroxide (CH). GGBFS activated by CH and sulfate ions hydrated continuously at later age, producing more and more hydration products, C-S-H gel and ettringite. Thus the paste developed a denser microstructure and its strength increased. The 28 d compressive strength of the mixture of 50% PG, 46% GGBFS and 4% OPC exceeded 45 MPa. The setting time was faster and 3 d and 7 d strength were higher when the proportion of OPC increased. But the 28 d strength decreased when OPC exceeded 4% due to large amount of ettringite formed at late hydration age which damaged the microstructure.

  10. 76 FR 54206 - Gray Portland Cement and Clinker From Japan: Final Results of the Expedited Third Sunset Review...

    Science.gov (United States)

    2011-08-31

    ... International Trade Administration Gray Portland Cement and Clinker From Japan: Final Results of the Expedited... review of the antidumping duty order on gray portland cement and clinker from Japan. As a result of this... duty order on gray portland cement and clinker from Japan \\1\\ pursuant to section 751(c) of the...

  11. Performance of portland limestone cements: Cements designed to be more sustainable that include up to 15% limestone addition

    Science.gov (United States)

    Barrett, Timothy J.

    where the limestone was blended (i.e., not interground) as needed, enabling variation of the size of the limestone particles. In addition, one of the commercially produced OPCs and PLCs were used with fly ash. A series of standardized tests were run to assess the physical effects of intergrinding limestone in portland cement, the effect of limestone presence and method of inclusion on the hydration reaction, and the associated mechanical and transport properties of concretes made with these limestone cements. The second phase of the study used a commercially produced OPC, a PLC, and a PLC-slag all made from the same parent clinker to quantify the early age shrinkage and cracking potential. The study presents a series of tests that quantify the fundamental origins of shrinkage in cementitious materials to elucidate the differences between PLC and OPC. The bulk shrinkage of these systems is then quantified under free and restrained conditions to provide an assessment of the susceptibility for cracking in portland limestone cements. The results of the first phase of this thesis showed that in general the PLC and OPC systems have similar hydration, set, and mechanical performance. Transport properties in this study show behavior that is +/- 30% of the conventional OPC system depending on the system. Literature has shown similar freeze-thaw resistance when these materials are used in properly air entrained mixtures, and the results for PLC systems with fly ash show added performance. Based on these results it appears that PLC that meets ASTM C595/AASHTO M234 should be able to be used interchangeably with OPC, while it should also be noted that the investigation of the influence of salts and sulfates on PLCs is still ongoing and should be monitored. The results of the second phase of this thesis showed that while the PLCs are finer, this comes primarily by reducing the very large particles (clinker particles greater than 30 microns) using advanced separator technology and

  12. Characterization of high-calcium fly ash and its influence on ettringite formation in portland cement pastes

    Science.gov (United States)

    Tishmack, Jody Kathleen

    High-calcium Class C fly ashes derived from Powder River Basin coal are currently used as supplementary cementing materials in portland cement concrete. These fly ashes tend to contain significant amounts of sulfur, calcium, and aluminum, thus they are potential sources of ettringite. Characterization of six high-calcium fly ashes originating from Powder River Basin coal have been carried out. The hydration products formed in pastes made from fly ash and water were investigated. The principal phases produced at room temperature were ettringite, monosulfate, and stratlingite. The relative amounts formed varied with the specific fly ash. Removal of the soluble crystalline sulfur bearing minerals indicated that approximately a third of the sulfur is located in the fly ash glass. Pore solution analyses indicated that sulfur concentrations increased at later ages. Three fly ashes were selected for further study based on their ability to form ettringite. Portland cement-fly ash pastes made with the selected fly ashes were investigated to evaluate ettringite and monosulfate formation. Each of the fly ashes were mixed with four different types of portland cements (Type I, I/II, II, and III) as well as three different Type I cements exhibiting a range of C3A and sulfate contents. The pastes had 25% or 35% fly ash by total weight of solids and a water:cement-fly ash ratio of 0.45. The samples were placed in a curing room (R.H. = 100, 23°C) and were then analyzed at various ages by x-ray diffraction (XRD) and differential scanning calorimetry (DSC) to determine the principal hydration products. The hydration products identified by XRD were portlandite, ettringite (an AFt phase), monosulfate, and generally smaller amounts of hemicarboaluminate and monocarboaluminate (all AFm phases). Although the amount of ettringite formed varied with the individual cement, only a modest correlation with cement sulfate content and no correlation with cement C3A content was observed. DSC

  13. Spent FCC catalyst for improving early strength Portland cement

    OpenAIRE

    Borrachero Rosado, María Victoria; Monzó Balbuena, José Mª; Paya Bernabeu, Jorge Juan; Vunda, Christian; VELÁZQUEZ RODRÍGUEZ, SERGIO; Soriano Martinez, Lourdes

    2014-01-01

    Spent fluid catalytic cracking (FCC) catalyst from the petrol industry has proven to be a very active pozzolanic material. This behavior leads to an additional increase in the strength of the mortar that contains this catalyst. Pozzolanic effects tend to be considered for periods above three days, whereas in shorter times, the influence of pozzolan is usually negligible. The reactivity of FCC is so high, however, that both pozzolanic effects and acceleration of cement hydration are evident in...

  14. Characterization and utilization of cement kiln dusts (CKDs) as partial replacements of Portland cement

    Science.gov (United States)

    Khanna, Om Shervan

    The characteristics of cement kiln dusts (CKDs) and their effects as partial replacement of Portland Cement (PC) were studied in this research program. The cement industry is currently under pressure to reduce greenhouse gas (GHG) emissions and solid by-products in the form of CKDs. The use of CKDs in concrete has the potential to substantially reduce the environmental impact of their disposal and create significant cost and energy savings to the cement industry. Studies have shown that CKDs can be used as a partial substitute of PC in a range of 5--15%, by mass. Although the use of CKDs is promising, there is very little understanding of their effects in CKD-PC blends. Previous studies provide variable and often conflicting results. The reasons for the inconsistent results are not obvious due to a lack of material characterization data. The characteristics of a CKD must be well-defined in order to understand its potential impact in concrete. The materials used in this study were two different types of PC (normal and moderate sulfate resistant) and seven CKDs. The CKDs used in this study were selected to provide a representation of those available in North America from the three major types of cement manufacturing processes: wet, long-dry, and preheater/precalciner. The CKDs have a wide range of chemical and physical composition based on different raw material sources and technologies. Two fillers (limestone powder and quartz powder) were also used to compare their effects to that of CKDs at an equivalent replacement of PC. The first objective of this study was to conduct a comprehensive composition analysis of CKDs and compare their characteristics to PC. CKDs are unique materials that must be analyzed differently from PC for accurate chemical and physical analysis. The present study identifies the chemical and physical analytical methods that should be used for CKDs. The study also introduced a method to quantify the relative abundance of the different

  15. Evolution of the hydration in cements with additions

    Directory of Open Access Journals (Sweden)

    Bonavetti, V. L.

    2002-12-01

    Full Text Available In this paper, the hydration mechanism of portland cement pastes with limestone, quartz and natural pozzolan (80/20 weight was analized. The techniques used were nonevaporable water content, pozzolanic activity and X-ray diffraction. Results show that filler effect increases initially the amount of hydration products in all pastes. For limestone pastes, the dilution effect is significant at long time, for quartz and pozzolan pastes the dilution effect was lower due to the contribution of the pozzolanic reaction.

    En el presente trabajo se analizó el mecanismo de hidratación de pastas de cemento portland normal con la incorporación de caliza, cuarzo y puzolana natural (proporción 80/20 en peso, por medio de la evaluación del contenido de agua no evaporable, la actividad puzolánica por vía química y la formación de productos de hidratación por DRX. Los resultados obtenidos permitieron determinar un aumento de la cantidad de productos de hidratación inicial debidos al efecto filler en todas las pastas. En las pastas con caliza se evidenció el efecto de dilución a edades avanzadas, en tanto que en las pastas con cuarzo y puzolana, este efecto fue menos predominante debido a la contribución de la reacción puzolánica.

  16. The influence of clay additives in Portland cement on the compressive strength of the cement stone

    Directory of Open Access Journals (Sweden)

    A.R. Gaifullin

    2015-11-01

    Full Text Available The introduction of mineral additives to binders, especially to Portland cement, is one of the promising trends for solving the resource and energy saving problems, as well as problems of environmental protection during production and application. Expanding the supplementary cementitious materials resource base can be achieved through the use of natural pozzolans and thermally activated polymineral clays(commonly known as glinites in Russia. One type of glinite is metakaolin, which is obtained by calcination of kaolin clays. Metakaolin is widely and effectively used as a pozzolanic additive due to its beneficial effect on the physical and mechanical properties of Portland cement-based materials. The obstacle to its wide production and use are the limited deposits of pure kaolin clays in many countries, including the Russian Federation. In this respect, the studies of pozzolanic activity of the most common mineral clays and their use in some countries have significantly advanced. Similar studies were widely performed in the 1940s in USSR. It seems reasonable to renew this trend to provide a scientific base for the production of local pozzolans made of clays commonly used in different regions. Comparative studies of the effect of 5 clays differing in mineral and chemical composition, calcination temperature and specific surface area, and high-quality metakaolin, on the strength of hardened Portland cement paste have been performed. It has been established that introducing 5…10 % of composite clays calcined at 400…8000 C° and milled to a specific surface area of 290…800 m2/kg into Portland cement enhanced the strength of the hardened cement paste considerably better than the introduction of metakaolin with a specific surface area of 1200 m2/kg. The findings of the study suggest that many kinds of commonly used polymineral clays have a specific calcination temperature and dispersity, which results in a higher pozzolanic activity compared with

  17. Use of waste gypsum to replace natural gypsum as set retarders in portland cement.

    Science.gov (United States)

    Chandara, Chea; Azizli, Khairun Azizi Mohd; Ahmad, Zainal Arifin; Sakai, Etsuo

    2009-05-01

    The present study is focused on clarifying the influence of waste gypsum (WG) in replacing natural gypsum (NG) in the production of ordinary Portland cement (OPC). WG taken from slip casting moulds in a ceramic factory was formed from the hydration of plaster of paris. Clinker and 3-5wt% of WG was ground in a laboratory ball mill to produce cement waste gypsum (CMWG). The same procedure was repeated with NG to substitute WG to prepare cement natural gypsum (CMNG). The properties of NG and WG were investigated via X-ray Diffraction (XRD), X-ray fluorescence (XRF) and differential scanning calorimetry (DSC)/thermogravimetric (TG) to evaluate the properties of CMNG and CMWG. The mechanical properties of cement were tested in terms of setting time, flexural and compressive strength. The XRD result of NG revealed the presence of dihydrate while WG contained dihydrate and hemihydrate. The content of dihydrate and hemihydrates were obtained via DSC/TG, and the results showed that WG and NG contained 12.45% and 1.61% of hemihydrate, respectively. Furthermore, CMWG was found to set faster than CMNG, an average of 15.29% and 13.67% faster for the initial and final setting times, respectively. This was due to the presence of hemihydrate in WG. However, the values obtained for flexural and compressive strength were relatively the same for CMNG and CMWG. Therefore, this result provides evidence that WG can be used as an alternative material to NG in the production of OPC.

  18. Experimental techniques for cement hydration studies

    Directory of Open Access Journals (Sweden)

    Andreas Luttge

    2011-10-01

    Full Text Available Cement hydration kinetics is a complex problem of dissolution, nucleation and growth that is still not well understood, particularly in a quantitative way. While cement systems are unique in certain aspects they are also comparable to natural mineral systems. Therefore, geochemistry and particularly the study of mineral dissolution and growth may be able to provide insight and methods that can be utilized in cement hydration research. Here, we review mainly what is not known or what is currently used and applied in a problematic way. Examples are the typical Avrami approach, the application of Transition State Theory (TST to overall reaction kinetics and the problem of reactive surface area. Finally, we suggest an integrated approach that combines vertical scanning interferometry (VSI with other sophisticated analytical techniques such as atomic force microscopy (AFM and theoretical model calculations based on a stochastic treatment.

  19. Water dynamics in hardened ordinary Portland cement paste or concrete: from quasielastic neutron scattering.

    Science.gov (United States)

    Bordallo, Heloisa N; Aldridge, Laurence P; Desmedt, Arnaud

    2006-09-14

    Portland cement reacts with water to form an amorphous paste through a chemical reaction called hydration. In concrete the formation of pastes causes the mix to harden and gain strength to form a rock-like mass. Within this process lies the key to a remarkable peculiarity of concrete: it is plastic and soft when newly mixed, strong and durable when hardened. These qualities explain why one material, concrete, can build skyscrapers, bridges, sidewalks and superhighways, houses, and dams. The character of the concrete is determined by the quality of the paste. Creep and shrinkage of concrete specimens occur during the loss and gain of water from cement paste. To better understand the role of water in mature concrete, a series of quasielastic neutron scattering (QENS) experiments were carried out on cement pastes with water/cement ratio varying between 0.32 and 0.6. The samples were cured for about 28 days in sealed containers so that the initial water content would not change. These experiments were carried out with an actual sample of Portland cement rather than with the components of cement studied by other workers. The QENS spectra differentiated between three different water interactions: water that was chemically bound into the cement paste, the physically bound or "glassy water" that interacted with the surface of the gel pores in the paste, and unbound water molecules that are confined within the larger capillary pores of cement paste. The dynamics of the "glassy" and "unboud" water in an extended time scale, from a hundred picoseconds to a few nanoseconds, could be clearly differentiated from the data. While the observed motions on the picosecond time scale are mainly stochastic reorientations of the water molecules, the dynamics observed on the nanosecond range can be attributed to long-range diffusion. Diffusive motion was characterized by diffusion constants in the range of (0.6-2) 10(-9) m(2)/s, with significant reduction compared to the rate of diffusion

  20. Comparison of the root-end sealing ability of MTA and Portland cement.

    Science.gov (United States)

    Islam, Intekhab; Chng, Hui Kheng; Yap, Adrian U Jin

    2005-08-01

    The aim of this study was to compare the in vitro sealing ability of ProRoot MTA, ProRoot MTA (Tooth-Coloured Formula), ordinary Portland cement and white Portland cement when used as root-end filling materials. Twenty-four single-rooted human premolars were prepared and obturated using standard techniques, then retrofilled with the test materials. The prepared teeth were immersed in 1% methylene blue dye for 72 hours and then assessed for dye leakage. The depth of dye penetration was measured and expressed as a percentage of the length of the retrofilling. Data was analysed using ANOVA and Fisher's Least Significant Test (LSD) (p cements, it is reasonable to consider Portland cement as a possible substitute for MTA as a root-end filling material. However, further tests, especially in vivo biocompatibility tests, need to be conducted before Portland cement can be recommended for clinical use.

  1. Micro and nanostructural characterization of surfaces and interfaces of Portland cement mortars using atomic force microscopy

    Energy Technology Data Exchange (ETDEWEB)

    Barreto, M.F.O.; Brandao, P.R.G., E-mail: matheusfob@yahoo.com.br, E-mail: pbrandao@demin.ufmg.br [Universidade Federal de Minas Gerais (UFMG), MG (Brazil)

    2014-07-01

    The characterization of Portland cement mortars is very important in the study the interfaces and surfaces that make up the system grout/ceramic block. In this sense, scanning electron microscopy and energy-dispersive (X-ray) spectrometer are important tools in investigating the morphology and chemical aspects. However, more detailed topographic information can be necessary in the characterization process. In this work, the aim was to characterize topographically surfaces and interfaces of mortars applied onto ceramic blocks. This has been accomplished by using the atomic force microscope (AFM) - MFP-3D-SA Asylum Research. To date, the results obtained from this research show that the characterization of cementitious materials with the help of AFM has an important contribution in the investigation and differentiation of hydrated calcium silicates (CSH), calcium hydroxide (Ca(OH)2, ettringite and calcium carbonate by providing morphological and micro topographical data, which are extremely important and reliable for the understanding of cementitious materials. (author)

  2. COMPARATIVE ANALYSIS OF PERFORMANCE OF PORTLAND CEMENT BLENDED WITH NANOSILICA AND SILICA FUME

    Directory of Open Access Journals (Sweden)

    J. I TOBÓN

    2010-01-01

    Full Text Available In this paper some physical properties of Colombian Portland cement type III replaced with nanosilica in percentages of 1, 3, 5 and 10% were evaluated. Main determined properties were fluidity, normal consistency, setting times, heat of hydration and compressive strength on pastes and mortars. It was made also a comparative analysis with samples substituted with commercial silica fume in percentages of 5, 10 and 15%. Results showed that the nanosilica from 5% beginning to have a major positive influence on the mechanical strength of mortars and with a 10% of substitution improvements in compressive strength up to 120% with respect to the control sample for one day of curing can be achieved. For longer curing time the improvement is decreased slightly, with near 80%, remaining this improvement in strength after 28 days of curing.

  3. Pulpotomies with portland cement in human primary molars

    Directory of Open Access Journals (Sweden)

    Taísa Regina Conti

    2009-02-01

    Full Text Available Two clinical cases in which Portland cement (PC was applied as a medicament after pulpotomy of mandibular primary molars in children are presented. Pulpotomy using PC was carried out in two mandibular first molars and one mandibular second molar, which were further followed-up. At the 3, 6 and 12-month follow-up appointments, clinical and radiographic examinations of the pulpotomized teeth and their periradicular area revealed that the treatments were successful in maintaining the teeth asymptomatic and preserving pulpal vitality. Additionally, the formation of a dentin bridge immediately below the PC could be observed in the three molars treated. PC may be considered as an effective alternative for primary molar pulpotomies, at least in a short-term period. Randomized clinical trials with human teeth are required in order to determine the suitability of PC before unlimited clinical use can be recommended.

  4. Detecting flaws in Portland cement concrete using TEM horn antennae

    Science.gov (United States)

    Al-Qadi, Imad L.; Riad, Sedki M.; Su, Wansheng; Haddad, Rami H.

    1996-11-01

    To understand the dielectric properties of PCC and better correlate them with type and severity of PCC internal defects, a study was conducted to evaluate PCC complex permittivity and magnetic permeability over a wideband of frequencies using both time domain and frequency domain techniques. Three measuring devices were designed and fabricated: a parallel plate capacitor, a coaxial transmission line, and transverse electromagnetic (TEM) horn antennae. The TEM horn antenna covers the microwave frequencies. The measurement technique involves a time domain setup that was verified by a frequency domain measurement. Portland cement concrete slabs, 60 by 75 by 14 cm, were cast; defects include delamination, delamination filled with water, segregation, and chloride contamination. In this paper, measurements using the TEM horn antennae and the feasibility of detecting flaws at microwave frequency are presented.

  5. Strength development, hydration reaction and pore structure of autoclaved slag cement with added silica fume

    Energy Technology Data Exchange (ETDEWEB)

    Xi, Y. [China Building Materials Academy, Beijing (China); Siemer, D.D. [LITCO, Idaho Falls, ID (United States); Scheetz, B.E. [Pennsylvania State Univ., University Park, PA (United States). Materials Research Lab.

    1997-01-01

    Under continuous hydrothermal treatment the strength of portland cement paste decreases with curing time and the pore structure coarsens. It was found in this study that the compressive strength of slag cement paste containing 67.5 wt.% ggbfs also decreases with time after 24 hour hydrothermal processing, but with a small addition of silica fume to the slag cement, the cement strength increases and the pore structure densifies when processed under comparable conditions. Based on observations XRD and SEM, these changes are attributed to: (1) changes in the hydration reactions and products by highly reactive silica fume, such that amorphous products dominate and the strength reducing phase {alpha}-C{sub 2}SH does not form; (2) slower hydration of slag, partially caused by the decreased pH of the pore solution, favors the formation of a dense pore structure; and (3) the space filling properties of the micro particles of silica fume.

  6. Sulfate resistance of ordinary Portland cement with fly ash

    Directory of Open Access Journals (Sweden)

    Irassar, Edgardo F.

    1989-03-01

    Full Text Available Low calcium fly ash has demonstrated to be an effective pozzolan to improve sulfate resistance of ordinary portland cement (type I. In this paper physico-chemical effects that produce this pozzolan in the mortar exposed to sulfate attack are studied. Dilution and dispersion affects are analyzed using mixes of cement with an inert mineral admixture. Mineralogical changes of mortar are studied using X-ray diffraction and the help of scanning electron microscope. The results show that fly ash delays mortar cracking phenomenon due to less content of unstable compounds in sulfate environment, greater available space to be occupied by expansive compounds and less CH present in the mortars.

    La ceniza volante de bajo contenido de óxido de calcio ha demostrado ser una efectiva puzolana para mejorar la resistencia a los sulfatos del cemento portland normal (CRN. En el presente trabajo se estudian los efectos físico-químicos que produce esta puzolana en el mortero expuesto al ataque de sulfatos. Se analizan los efectos de dilución y dispersión utilizando mezclas de cemento con una adición mineral inactiva. Los cambios mineralógicos del mortero se estudian con difracción de rayos X (DRX y la ayuda del microscopio electrónico. Los resultados indican que la ceniza volante retarda el fenómeno de fisuración del mortero debido a la menor cantidad de compuestos inestables en ambiente con sulfatos, el mayor espacio disponible para albergar a los compuestos expansivos y la disminución del CH presente en la mezcla.

  7. Modelling of Pb release during Portland cement alteration

    Energy Technology Data Exchange (ETDEWEB)

    Benard, A. [INERIS Mediterrannee, F-13545 Aix En Provence 04 (France); Rose, J.; Borschneck, D.; Bottero, J.Y. [Univ Paul Cezanne, CNRS, UMR 6635, CEREGE, IFR PMSE 112, F-13545 Aix En Provence, (France); Hazemann, J.L. [CNRS, Cristallog Lab, F-38042 Grenoble 09 (France); Proux, O. [Univ Grenoble 1, CNRS, UMR, LGIT, F-38400 St Martin Dheres (France); Trotignon, L. [CEA Cadarache, DTN, SMTM, Lab Modelisat Transferts Environm, 13 - Saint Paul lez Durance (France); Nonat, A. [Univ Bourgogne, CNRS, UMR 5613, Fac Sci Mirande, Lab Rech Reactivite Solides, F-21078 Dijon (France); Chateau, L. [ADEME, F-49004 Angers (France)

    2009-07-01

    Complex cementitious matrices undergo weathering with environmental exchange and can release metallic pollutants during alteration. The molecular mechanisms responsible for metal release are difficult to identify, though this is necessary if such processes are to be controlled. The present study determines and models the molecular mechanisms of Pb release during Portland cement leaching. As Pb release is strongly related to its speciation (i.e. atomic environment and the nature of bearing phases), the first objective of the present study was to investigate the evolution of Pb retention sites together with the evolution of the cement mineralogy during leaching. Complementary and efficient investigation tools were used, namely X-ray diffraction, micro-X-ray fluorescence and X-ray absorption fine structures. The second objective was to reproduce our results with a reactive transport code (CHESS/HYTEC) in order to test the proposed speciation model of Pb. Combined results indicate that in both the unaltered core and the altered layer of the leached cement, Pb(II) would be retained through C-S-H 'nano-structure', probably linked to a Q(1) or Q(2P) silicate tetrahedra. Moreover in the altered layer, the presence of Fe atoms in the atomic environment of Pb is highly probable. Unfortunately little is known about Fe phases in cement, which makes the interpretation difficult. Can Fe-substituted hydrogranet (C(3)AH(6)) be responsible for Pb retention? Modelling results were consistent with Pb retention through C-S-H in layers and also in an additional, possibly Fe-containing, Pb-retention phase in the altered layer. (authors)

  8. The effect of sulfate activation on the early age hydration of BFS:PC composite cement

    Energy Technology Data Exchange (ETDEWEB)

    Collier, N.C., E-mail: nick.collier@sheffield.ac.uk; Li, X.; Bai, Y.; Milestone, N.B.

    2015-09-15

    Blast furnace slag/Portland cement composites are routinely used for immobilising intermediate level nuclear wastes in the UK. Using high cement replacement levels reduces hydration exotherm and lowers pH. Although a lower grout pH will be beneficial in reducing the corrosion of certain encapsulated reactive metals such as aluminium, the degree of slag reaction will also be lower which may result in the formation of less hydration products and which in turn may reduce the capacity to immobilise waste ions. Adding neutral salts such as calcium and sodium sulfate to the composite cement can potentially increase slag activation without significantly altering the pH of the cement matrix. Thus the corrosion of any encapsulated metals would not be affected. This paper describes some of the properties of a hydrated 9:1 blast furnace slag:Portland cement matrix containing added sulfates of calcium and sodium. The findings show that all additives caused an increase in the amount of slag that reacted when cured for up to 28 days. This produced more material able to chemically bind waste ions. Activation with gypsum produced the highest rate of slag reaction.

  9. Hydration of blended cement pastes containing waste ceramic powder as a function of age

    Science.gov (United States)

    Scheinherrová, Lenka; Trník, Anton; Kulovaná, Tereza; Pavlík, Zbyšek; Rahhal, Viviana; Irassar, Edgardo F.; Černý, Robert

    2016-07-01

    The production of a cement binder generates a high amount of CO2 and has high energy consumption, resulting in a very adverse impact on the environment. Therefore, use of pozzolana active materials in the concrete production leads to a decrease of the consumption of cement binder and costs, especially when some type of industrial waste is used. In this paper, the hydration of blended cement pastes containing waste ceramic powder from the Czech Republic and Portland cement produced in Argentina is studied. A cement binder is partially replaced by 8 and 40 mass% of a ceramic powder. These materials are compared with an ordinary cement paste. All mixtures are prepared with a water/cement ratio of 0.5. Thermal characterization of the hydrated blended pastes is carried out in the time period from 2 to 360 days. Simultaneous DSC/TG analysis is performed in the temperature range from 25 °C to 1000 °C in an argon atmosphere. Using this thermal analysis, we identify the temperature, enthalpy and mass changes related to the liberation of physically bound water, calcium-silicate-hydrates gels dehydration, portlandite, vaterite and calcite decomposition and their changes during the curing time. Based on thermogravimetry results, we found out that the portlandite content slightly decreases with time for all blended cement pastes.

  10. Properties of SiMn slag as apozzolanic material in portland cement manufacture

    Directory of Open Access Journals (Sweden)

    Frías, M.

    2005-12-01

    Full Text Available The primary purpose of this study was to evaluate the behaviour of SiMn slag as a pozzolanic material in commercial Portland cement manufacture. This necessitated exploring different scientific and technical aspects to ensure a correct valuation. The results obtained revealed that silica and calcium are the main components of SiMn slag, whose pozzolanic activity occupies an intermediate position between silica fume and fly ash; it reduces heat of hydration and mortars made with cement containing SiMn slag exhibit compressive strength values similar to the figures for standard mortar. Consequently, the use of SiMn slag as an active addition to cement is feasible, inasmuch as the resulting product meets the requirements laid down in the present legislation.

    El objetivo principal de este trabajo es evaluar el comportamiento de la escoria de SiMn como material puzolánico en la fabricación de cementos Portland comerciales. Para ello, resulta necesario investigar diferentes aspectos científicos y técnicos que conlleven a una correcta valorización de las mismas. Los resultados obtenidos en el presente trabajo han puesto de manifiesto que la escoria de SiMn presenta una naturaleza sílico-cálcica, actividad puzolúnica intermedia entre el humo de sílice y ceniza volante, reduce el calor de hidratación y los morteros con escoria de SiMn muestra alcanzan resistencias a compresión similares a las del mortero patrón. Por lo tanto, la utilización de la escoria de SiMn como adición activa al cemento es viable, cumpliendo con las exigencias recogidas en la norma vigente.

  11. Methods to determine hydration states of minerals and cement hydrates

    Energy Technology Data Exchange (ETDEWEB)

    Baquerizo, Luis G., E-mail: luis.baquerizoibarra@holcim.com [Innovation, Holcim Technology Ltd., CH-5113 Holderbank (Switzerland); Matschei, Thomas [Innovation, Holcim Technology Ltd., CH-5113 Holderbank (Switzerland); Scrivener, Karen L. [Laboratory of Construction Materials, Ecole Polytechnique Fédérale de Lausanne, CH-1015 Lausanne (Switzerland); Saeidpour, Mahsa; Thorell, Alva; Wadsö, Lars [Building Materials, Lund University, Box 124, 221 000 Lund (Sweden)

    2014-11-15

    This paper describes a novel approach to the quantitative investigation of the impact of varying relative humidity (RH) and temperature on the structure and thermodynamic properties of salts and crystalline cement hydrates in different hydration states (i.e. varying molar water contents). The multi-method approach developed here is capable of deriving physico-chemical boundary conditions and the thermodynamic properties of hydrated phases, many of which are currently missing from or insufficiently reported in the literature. As an example the approach was applied to monosulfoaluminate, a phase typically found in hydrated cement pastes. New data on the dehydration and rehydration of monosulfoaluminate are presented. Some of the methods used were validated with the system Na{sub 2}SO{sub 4}–H{sub 2}O and new data related to the absorption of water by anhydrous sodium sulfate are presented. The methodology and data reported here should permit better modeling of the volume stability of cementitious systems exposed to various different climatic conditions.

  12. Influence of Portland Cement Class on the Corrosion Rate of Steel Reinforcement in Cement Mortar Caused by Penetrating Chloride and Sulfate from the Environment

    OpenAIRE

    Bikić, F.; Cacan, M.; Rizvanović, M.

    2013-01-01

    The influence of portland cement class on the corrosion rate of steel reinforcement in cement mortar caused by penetrating chloride or sulfate from the environment in already hardened cement mortar is investigated in this paper. Three classes of portland cement have been used for the tests, PC 35, PC 45 and PC 55. Cylindrical samples of cement mortar with steel reinfor- cement in the middle were treated 6 months at room temperature in the follow...

  13. Effect of Water to Cement Ratio and Age on Portland Composite Cement Mortar Porosity, Strength and Evaporation Rate

    Directory of Open Access Journals (Sweden)

    Enamur R. Latifee

    2016-08-01

    Full Text Available Durability and the compressive strength of concrete are directly related to the porosity. Water to cement ratio is the main parameter behind the nature and amount of pores within the matrix. Porosity is also influenced by the degree of cement hydration and the length of moist-curing. Even after the standard moist curing period, i.e. 28 days the concrete can gain strength and porosity can be reduced under ambient relative humidity and temperature. However, this fact, that is the age effect on porosity reduction of the cement mortar or concrete, kept in air with ambient relative humidity and temperature for long duration could not be found in the literature. Therefore, in this research, different w/c were used with constant amount Portland Composite Cement to find out whether the mortar porosity decreases significantly over time, after 28 days of water curing, while kept in air and if there is any interaction effect between the age of the mortar and different w/c; regarding porosity. It was also intended to find out if water-loss rate variation with different w/c has similar trend as porosity variation with different w/c. It was found that, there is significant decrease in porosity with time for the first six weeks in air and after that it dwindles down gradually, and there is no interaction between age and w/c. Also, after 100 days in air, samples were submerged under water for 24 hours and then kept in air for the evaporation in subsequent days. It has been found that the water evaporation vs. w/c curve, using 11-day evaporation of water from different w/c specimens in ambient condition is almost parallel to porosity vs. w/c curve. Therefore, 11-day evaporation of aged saturated mortar or concrete sample, such as core can also be used as a durability index, which can be used for old structure evaluation.

  14. Use of ancient copper slags in Portland cement and alkali activated cement matrices.

    Science.gov (United States)

    Nazer, Amin; Payá, Jordi; Borrachero, María Victoria; Monzó, José

    2016-02-01

    Some Chilean copper slag dumps from the nineteenth century still remain, without a proposed use that encourages recycling and reduces environmental impact. In this paper, the copper slag abandoned in landfills is proposed as a new building material. The slags studied were taken from Playa Negra and Púquios dumps, both located in the region of Atacama in northern Chile. Pozzolanic activity in lime and Portland cement systems, as well as the alkali activation in pastes with copper slag cured at different temperatures, was studied. The reactivity of the slag was measured using thermogravimetric analysis (TGA), scanning electron microscopy (SEM), X-ray diffraction (XRD), electrical conductivity and pH in aqueous suspension and Fourier Transform Infrared Spectroscopy (FTIR). Furthermore, copper slag-Portland cement mortars with the substitution of 25% (by weight) of cement by copper slag and alkali-activated slag mortars cured at 20 and 65 °C were made, to determine the compressive strength. The results indicate that the ancient copper slags studied have interesting binding properties for the construction sector.

  15. Influence of mixture ratio and pH to solidification/stabilization process of hospital solid waste incineration ash in Portland cement.

    Science.gov (United States)

    Sobiecka, Elzbieta; Obraniak, Andrzej; Antizar-Ladislao, Blanca

    2014-09-01

    Solidification/stabilization (S/S) is an established utilization technology to treat hazardous wastes. This research explored the influence of pH (3-12) on the immobilization of heavy metals present in five mixtures of hospital solid waste incinerator ash and Portland cement, following two different processes of waste solidification/stabilization (cement hydration and granulation). In general, cement hydration process resulted in more stable products than granulation process. A high ash content in the mixture with Portland cement (60wt%) resulted in the highest immobilization of Pb(2+) and Cu(2+), while a low ash content in the mixture (10wt%) resulted in the lowest leachability of Zn(2+). When ash and Portland cement was mixed in equal proportions (50wt%) the highest encapsulation was observed for Ni(2+), Cd(2+) and Cr(3+). Neutral and weak alkaline pH values within the range pH=7-8 resulted in the lowest leachability of the monitored heavy metals.

  16. Evaluation of the use of red mud as a pozzolanic additive in Portland cement; Avaliacao do uso de residuo de bauxita como aditivo pozolanico no cimento Portland

    Energy Technology Data Exchange (ETDEWEB)

    Fortes, Gustavo Mattos; Balbino, Thiago Gabriel Ferreira; Lourenco, Rafaela Roberta; Rodrigues, Jose de Anchieta [Universidade Federal de Sao Carlos (GEMM/DEMa/UFSCar), Sao Carlos, SP (Brazil). Departamento de Engenharia de Materias. Grupo de Engenharia de Microestrutura de Materiais; Montini, Marcelo [Alcoa Aluminio S.A., Pocos de Caldas, MG (Brazil)

    2011-07-01

    It is estimated that the aluminum industry generates approximately 13.7 million tones/year of red mud (RB) in Brazil. Although, being the RB rich in Al{sub 2}O{sub 3} and SiO{sub 2} and partially amorphous, a potential pozzolanic activity is suggested. Thus, this work aims to evaluate the application of 15w-% of RB, as a pozzolanic additive, to the ordinary Portland cement (CPI), simulating a pozzolanic compost Portland cement (CPII-Z). To study the pozzolanic activation of the RB, this one was added without calcination, calcinated at 400°C and at 600°C. The compressive strength was measured in mortars of CPI with additions of RB, of CPI and CPII (references), after 28 days of curing. The analysis of the apparent porosity and the characterization of the hydration products were done to complement the evaluation. The mortars with calcinated RB showed good results of mechanical strength, reaching more than 85% (45 MPa) of the CPI's strength and higher values than the CPII-Z32. (author)

  17. Blasted copper slag as fine aggregate in Portland cement concrete.

    Science.gov (United States)

    Dos Anjos, M A G; Sales, A T C; Andrade, N

    2017-07-01

    The present work focuses on assessing the viability of applying blasted copper slag, produced during abrasive blasting, as fine aggregate for Portland cement concrete manufacturing, resulting in an alternative and safe disposal method. Leaching assays showed no toxicity for this material. Concrete mixtures were produced, with high aggregate replacement ratios, varying from 0% to 100%. Axial compressive strength, diametrical compressive strength, elastic modulus, physical indexes and durability were evaluated. Assays showed a significant improvement in workability, with the increase in substitution of fine aggregate. With 80% of replacement, the concrete presented lower levels of water absorption capacity. Axial compressive strength and diametrical compressive strength decreased, with the increase of residue replacement content. The greatest reductions of compressive strength were found when the replacement was over 40%. For tensile strength by diametrical compression, the greatest reduction occurred for the concrete with 80% of replacement. After the accelerated aging, results of mechanic properties showed a small reduction of the concrete with blasted copper slag performance, when compared with the reference mixture. Results indicated that the blasted copper slag is a technically viable material for application as fine aggregate for concrete mixtures. Copyright © 2017 Elsevier Ltd. All rights reserved.

  18. Arsenic content in Portland cement: A literature review

    Directory of Open Access Journals (Sweden)

    Tenorio de Franca Talita

    2010-01-01

    Full Text Available Portland cement (PC is a hydraulic binding material widely used in the building industry. The main interest in its use in dentistry is focused on a possible alternative to mineral trioxide aggregate (MTA because PC is less expensive and is widely available. In dentistry, PC has been used in dental procedures such as pulpotomy, pulp capping, repair of root perforation and root-end filling. The purpose of this article is review the dental literature about the PC, its composition with special attention to arsenic content, properties, and application in dentistry. A bibliographic research was performed in Bireme, PubMed, LILACS and Scopus data bases looking for national and international studies about the PC composition, properties and clinical use. It was observed that PC has favorable biological properties very similar to those of MTA. The PC has shown good cell proliferation induction with formation of a monolayer cell, satisfactory inflammatory response, inhibitory effect of prostaglandin and antimicrobial effect. Studies have shown that PC is not cytotoxic, stimulates the apposition of reparative dentin and permits cellular attachment and growth. Regarding arsenic presence, its levels and release are low. PC has physical, chemical and biological properties similar to MTA. Arsenic levels and release are low, therefore, unable to cause toxic effects.

  19. The Pore Structure and Hydration Performance of Sulphoaluminate MDF Cement

    Institute of Scientific and Technical Information of China (English)

    HUANG Cong-yun; YUAN Run-zhang; LONG Shi-zong

    2004-01-01

    The hydration and pore structure of sulphoaluminate MDF cement were studied by X-ray diffractometer ( XRD ), scanning electron microscope (SEM) and mercury intrusion porosimeter ( MIP ) etc. The ex-perimental results indicate that hydration products of the materials are entringites ( Aft ), aluminium hydroxide andCSH (Ⅰ) gel etc. Due to its very low water-cement ratio, hydration function is only confined to the surfaces of ce-ment grains, and there is a lot of sulphoaluminate cement in the hardenite which is unhydrated yet. Hydration re-action was rapidly carried under the condition of the heat-pressing. Therefore cement hydrates Aft, CSH (Ⅰ) andaluminium hydroxide gel fill in pores. The expansibility of Aft makes the porosity of MDF cement lower ( less than1 percent ) and the size of pore smaller (80 percent pore was less than 250A), and enhances its strength.

  20. The impact of sulphate and magnesium on chloride binding in Portland cement paste

    Energy Technology Data Exchange (ETDEWEB)

    De Weerdt, K., E-mail: klaartje.d.weerdt@ntnu.no [Department of Structural Engineering, Norwegian University of science and Technology, Trondheim (Norway); SINTEF Building and Infrastructure, Trondheim (Norway); Orsáková, D. [Department of Civil Engineering, Technical University of Brno, Brno (Czech Republic); Geiker, M.R. [Department of Structural Engineering, Norwegian University of science and Technology, Trondheim (Norway)

    2014-11-15

    The effect of magnesium and sulphate present in sea water on chloride binding in Portland cement paste was investigated. Ground well hydrated cement paste was exposed to MgCl{sub 2}, NaCl, NaCl + MgCl{sub 2}, MgSO{sub 4} + MgCl{sub 2} and artificial sea water solutions with a range of concentrations at 20 °C. Chloride binding isotherms are determined and pH of the solutions were measured. A selection of samples was examined by SEM-EDS to identify phase changes upon exposure. The experimental data were compared with calculations of a thermodynamic model. Chloride binding from sea water was similar to chloride binding for NaCl solutions. The magnesium content in the sea water lead to a slight decrease in pH, but this did not result in a notable increase in chloride binding. The sulphate present in sea water reduces both chloride binding in C–S–H and AFm phases, as the C–S–H incorporates more sulphates instead of chlorides, and part of the AFm phases converts to ettringite.

  1. Immediate and delayed solubility of mineral trioxide aggregate and Portland cement

    Directory of Open Access Journals (Sweden)

    Augusto Bodanezi

    2008-04-01

    Full Text Available This study investigated the solubility of mineral trioxide aggregate (MTA and Portland cement since its mixture until 672 hours, by means of two complimentary methods. Metal ring molds filled with the cements were covered with distilled water and, at each experimental time (3, 24, 72, 168, 336 and 672 hours, were weighed as soon as the plates in which the samples have been placed. Empty rings served as the control group (n=8. Mean weight gain and loss was determined and analyzed statistically by two-way ANOVA and Tukey's test for all pairwise comparisons. Only Portland cement showed less than 3% weight loss through 24 hours. Detached MTA residues were heavier than those of Portland cement over the 3 to 168 hours. The weight of MTA rings increased more than that of Portland rings within 672 hours (p=0.05. The findings of the present study indicate that, in an aqueous environment MTA is more soluble than Portland cement and exceeds the maximum weight loss considered acceptable by ISO 6876 standard (2001.

  2. Investigation of the hydration and bioactivity of radiopacified tricalcium silicate cement, Biodentine and MTA Angelus.

    Science.gov (United States)

    Camilleri, Josette; Sorrentino, François; Damidot, Denis

    2013-05-01

    Novel root-end filling materials are composed of tricalcium silicate (TCS) and radiopacifier as opposed to the traditional mineral trioxide aggregate (MTA) which is made up of clinker derived from Portland cement and bismuth oxide. The aim of this research was to characterize and investigate the hydration of a tricalcium silicate-based proprietary brand cement (Biodentine™) and a laboratory manufactured cement made with a mixture of tricalcium silicate and zirconium oxide (TCS-20-Z) and compare their properties to MTA Angelus™. The materials investigated included a cement containing 80% of TCS and 20% zirconium oxide (TCS-20-Z), Biodentine™ and MTA Angelus™. The specific surface area and the particle size distribution of the un-hydrated cements and zirconium oxide were investigated using a gas adsorption method and scanning electron microscopy. Un-hydrated cements and set materials were tested for mineralogy and microstructure, assessment of bioactivity and hydration. Scanning electron microscopy, X-ray energy dispersive analysis, X-ray fluorescence spectroscopy, X-ray diffraction, Rietveld refined X-ray diffraction and calorimetry were employed. The radiopacity of the materials was investigated using ISO 6876 methods. The un-hydrated cements were composed of tricalcium silicate and a radiopacifier phase; zirconium oxide for both Biodentine™ and TCS-20-Z whereas bismuth oxide for MTA Angelus™. In addition Biodentine™ contained calcium carbonate particles and MTA Angelus™ exhibited the presence of dicalcium silicate, tricalcium aluminate, calcium, aluminum and silicon oxides. TCS and MTA Angelus™ exhibited similar specific surface area while Biodentine™ had a greater specific surface area. The cements hydrated and produced some hydrates located either as reaction rim around the tricalcium silicate grain or in between the grains at the expense of volume containing the water initially present in the mixture. The rate of reaction of tricalcium

  3. The influence of energy mixing in pastes of Portland cement used in well cementing; Influencia da energia de mistura em pastas de cimento Portland utilizadas em cimentacao de pocos petroliferos

    Energy Technology Data Exchange (ETDEWEB)

    Lima, Flank M.; Oliveira, Valeska G.; Martinelli, Antonio E.; Melo, Dulce M.A.; Cachina, Gustavo H.A.B. [Universidade Federal do Rio Grande do Norte (UFRN), Natal, RN (Brazil)

    2004-07-01

    Portland cement is by far the most important binding material used in oil well cementing. Its mixture process in field is one of the most important problems in well cementing practices. The objective of that process is to prepare the cement slurry with similar properties those found in preliminaries laboratory tests. That objective should be found, or else, the relevance of the calculations and tests accomplished to determine the displacement flow, friction pressure, thickening time and the fluid loss rate of cement slurry. It was verified that the mixture time increases significantly the energy of mixture of the pastes, provoking changes in the plastic viscosity, yield point and forces gel of pastes. The hydration rates of slurries were affected for the mixture conditions, causing a decrease of about 40% in thickening time. Measures of fluid loss evidenced that for larger mixture times happened a reduction of the percentile of free water of 4,2% to 0,0%, provoked by the increase of the reaction of the system. (author)

  4. The influence of energy mixing in pastes of Portland cement used in well cementing; Influencia da energia de mistura em pastas de cimento Portland utilizadas em cimentacao de pocos petroliferos

    Energy Technology Data Exchange (ETDEWEB)

    Lima, Flank M.; Oliveira, Valeska G.; Martinelli, Antonio E.; Melo, Dulce M.A.; Cachina, Gustavo H.A.B. [Universidade Federal do Rio Grande do Norte (UFRN), Natal, RN (Brazil)

    2004-07-01

    Portland cement is by far the most important binding material used in oil well cementing. Its mixture process in field is one of the most important problems in well cementing practices. The objective of that process is to prepare the cement slurry with similar properties those found in preliminaries laboratory tests. That objective should be found, or else, the relevance of the calculations and tests accomplished to determine the displacement flow, friction pressure, thickening time and the fluid loss rate of cement slurry. It was verified that the mixture time increases significantly the energy of mixture of the pastes, provoking changes in the plastic viscosity, yield point and forces gel of pastes. The hydration rates of slurries were affected for the mixture conditions, causing a decrease of about 40% in thickening time. Measures of fluid loss evidenced that for larger mixture times happened a reduction of the percentile of free water of 4,2% to 0,0%, provoked by the increase of the reaction of the system. (author)

  5. Enhancement of cemented waste forms by supercritical CO{sub 2} carbonation of standard portland cements

    Energy Technology Data Exchange (ETDEWEB)

    Rubin, J.B.; Carey, J.; Taylor, C.M.V.

    1997-08-01

    We are conducting experiments on an innovative transformation concept, using a traditional immobilization technique, that may significantly reduce the volume of hazardous or radioactive waste requiring transport and long-term storage. The standard practice for the stabilization of radioactive salts and residues is to mix them with cements, which may include additives to enhance immobilization. Many of these wastes do not qualify for underground disposition, however, because they do not meet disposal requirements for free liquids, decay heat, head-space gas analysis, and/or leachability. The treatment method alters the bulk properties of a cemented waste form by greatly accelerating the natural cement-aging reactions, producing a chemically stable form having reduced free liquids, as well as reduced porosity, permeability and pH. These structural and chemical changes should allow for greater actinide loading, as well as the reduced mobility of the anions, cations, and radionuclides in aboveground and underground repositories. Simultaneously, the treatment process removes a majority of the hydrogenous material from the cement. The treatment method allows for on-line process monitoring of leachates and can be transported into the field. We will describe the general features of supercritical fluids, as well as the application of these fluids to the treatment of solid and semi-solid waste forms. some of the issues concerning the economic feasibility of industrial scale-up will be addressed, with particular attention to the engineering requirements for the establishment of on-site processing facilities. Finally, the initial results of physical property measurements made on portland cements before and after supercritical fluid processing will be presented.

  6. A Short Study to Test the Compliance of Various Pakistani Ordinary Portland Cements with ASTM Composition Standards

    Directory of Open Access Journals (Sweden)

    A. Shahnaz

    2013-12-01

    Full Text Available Cement is widely used everywhere for construction purposes and quality comparison of different ordinary Portland cements is very important. Five different brands of cement were tested for their chemical constituents such as silica, alumina, iron, calcium, magnesium, sulfates, insoluble residue, free lime and loss on ignition with American standards for testing and materials (ASTM. Results for five locally produced Portland cements revealed that the chemical compositions of most cement as determined by standard methods lie within standard limits. But the difference in constituents of various brands of cements is due to quality control setup differences of different cement plants.

  7. The most suitable techiniques and methods to identify high alumina cement and based portland cement in concretes

    OpenAIRE

    Blanco, M. T.; Puertas, F; Vázquez, T.; de la Fuente, A

    1992-01-01

    Instrumental techniques are indicated and the most adequated methodologies for determining the nature of the binder in concretes are explained. These methods are: a) Determination of the Silicic Moduli through chemical analysis of the sample. This test reveáis very different valúes between cement portland based concrete and high alumina cement based concretes. b) X-ray diffraction. It is considered as the best method. In the present paper the main diffraction Unes corresponding to...

  8. Manganese substitutions into the portland cement clinker phases

    Directory of Open Access Journals (Sweden)

    Puertas, F.

    1989-06-01

    Full Text Available The effect of manganese substitution into the crystal structures of the main Portland cement clinker phases (3CaO.SiO2, 2CaO.SiO2, 3CaO.Al2O3, 2CaO.Fe2O3 y 4CaO.Al2O3.Fe2O3 has been studied by X-ray and analytical electron microscopy. In oxidizing conditions, the limit of solid solution in 3CaO.SiO2 is about 0.72 ±0.11% (wt, while in 2CaO.SiO2 is 1.53±0,12%(wt. Mn solid solubility on 3CaO.Al2O3structure, in oxidizing conditions is close to 0.78 ± 0,12% (wt. In identical atmosphere, the proportion of Mn in the ferrite phases (2CaO.Fe2O3 and 4CaO.Al2O3.Fe2O3 is 6.80 ± 0.87% (wt and 6.7% (wt, respectively. To each mentioned clinker phases a solid solution formula has been proposed. In these formula, the manganese substitutions and also the different oxidation states which this element can be introduced in those crystalline structure are defined.

    Se ha estudiado, por difracción de rayos X y microanálisis por espectroscopia de energías dispersivas, el efecto de la sustitución del manganeso en las estructuras cristalinas de las fases más importantes del clinker del cemento portland (3CaO.SiO2, 2CaO.SiO2, 3CaO.Al2O3, 2CaO.Fe2O3 y 4CaO.Al2O3.Fe2O3. En condiciones oxidantes, el límite de solubilidad sólida en 3CaO.SiO2 es del orden de 0,72 ± 0,11% en peso; mientras que en 2CaO.SiO2 es de 1,53 ±0,12% en peso. La solución sólida del Mn en la estructura del 3CaO.Al2O3, en condiciones oxidantes, es próxima al 0,78 ±0,12% en peso. En idéntica atmósfera, la proporción del Mn en las fases terríficas (2CaO.Fe2O3 y 4CaO.Al2

  9. Resistance to acid attack of portland cement mortars produced with red mud as a pozzolanic additive; Resistencia ao ataque acido de argamassas de cimento Portland produzido com residuo de bauxita como aditivo pozolanico

    Energy Technology Data Exchange (ETDEWEB)

    Balbino, Thiago Gabriel Ferreira; Fortes, Gustavo Mattos; Lourenco, Rafaela Roberta; Rodrigues, Jose de Anchieta [Universidade Federal de Sao Carlos (DEMa/PPGCEM/UFSCar), SP (Brazil). Programa de Pos-Graducao em Ciencia e Engenharia de Materiais. Departamento de Engenharia de Materiais; Montini, Marcelo [Alcoa Aluminio S.A., Pocos de Caldas, MG (Brazil)

    2011-07-01

    Portland cement structures are usually exposed to aggressive environments, which requires the knowledge of the performance of these materials under deleterious conditions. In this study, it was evaluated the resistance to acid attack of mortars that contain ordinary (CPI) and compost (CPII-Z) Portland cements, adding to the first red mud (RB) as a pozzolanic additive in different conditions: without calcination, calcined at 400 ° C and at 600 ° C. The specimens were subjected to HCl and H{sub 2}SO{sub 4} solutions, both with concentration of 1.0 Mol L{sup -1} for 28 days, monitoring the weight loss and leached material nature by atomic emission inductively coupled plasma (ICP). The hydration products were studied by thermogravimetric analysis (TGA) and X-ray diffraction (XRD) of the hydrated cement pastes. It was observed a reduction of portlandite amount in the RB containing cement pastes, indicating a possible pozzolanic activity of the red mud. The mortars prepared with RB were more resistant to HCl, while that ones with calcined RB present a better performance in H{sub 2}SO{sub 4} attack. (author)

  10. Substitution of the clayey mineral component by lignite fly ash in portland cement clinker synthesis

    Directory of Open Access Journals (Sweden)

    Jovanović Nataša

    2006-01-01

    Full Text Available Fly ash from four power plants in Serbia (PP "Morava" - Svilajnac, PP "Kolubara" - Veliki Grijani, PP "Kostolac" - units B1 and B2 - Kostolac and PP "Nikola Tesla" - units A and B - Obrenovac was utilized as the starting raw component for Portland cement clinker synthesis. Limestone and quartz sand from the "Holcim - Serbia, a.d." cement factory were the other two starting raw components. Based on the chemical composition of the raw components and from the projected cement moduli, the amounts of raw components in the raw mixtures were calculated. Six different raw mixtures were prepared - each one consisted of limestone, sand and different fly ash. A raw mixture from the industrial production of the "Holcim - Serbia, a.d." cement factory was used as the reference material. The prepared raw mixtures were sintered in a laboratory furnace at 1400°C. The chemical and mineralogical compositions of the synthesized clinkers were determined. The characteristics of clinkers, based on fly ash, were compared to the characteristics of the industrial Portland cement clinker from the "Holcim - Serbia, a.d." cement factory. The results of the investigation showed that fly ash from power plants in Serbia can be suitable for Portland cement clinker synthesis.

  11. Physicochemical Properties of MTA and Portland Cement after Addition of Aloe Vera.

    Science.gov (United States)

    Henrique Borges, Alvaro; Aguirre Guedes, Orlando; Evaristo Ricci Volpato, Luiz; Siebert Filho, Gilberto; Meireles Borba, Alexandre; Zina, Omar; Piva, Evandro; Estrela, Carlos

    2017-01-01

    The aim of this in vitro study was to determine the liquid-powder ratio, setting time, solubility, dimensional change, pH, and radiopacity of white structural and non-structural Portland cement, ProRoot MTA and MTA Bio, associated with a 2% glycolic solution containing Aloe Vera, as vehicle. Five samples of each material were used for each test, according to the American National Standards Institute/American Dental Association (ANSI/ADA) specification No. 57. Statistical analyses were performed using ANOVA and Tukey's test at 5% significance. When sample distribution was not normal, non-parametric analysis of variance and the Kruskal-Wallis test were used (α=0.05). No statistical differences were found in liquid-powder ratios among the tested materials. ProRoot MTA showed the longest setting time. Dimensional change values were acceptable in all groups. Also, no significant differences were found in pH values and pH was alkaline in all samples throughout the experiment. Mean radiopacity results obtained for white Portland cements did not meet ANSI/ADA requirements, and were significantly lower than those obtained for MTA-based cements. Finally, Portland cements showed significantly higher mean solubility values compared to the other samples. The physicochemical properties of the tested materials in association with Aloe Vera were compatible with ANSI/ADA requirements, except for the white Portland cements, which failed to meet the radiopacity specification.

  12. Carbonation of low heat portland cement paste procured in water for different time

    Institute of Scientific and Technical Information of China (English)

    Deping Chen; Etsuo Sakai; Masaki Daimon; Yoko Ohba

    2007-01-01

    The carbonation technique was applied to accelerate the hydration of low heat portland cement (LHC). Before carbonation, the demoulded pastes were precured in water for 0, 2, 7, and 21 d, respectively. The results show that procuring time in water strongly influences the carbonation process. The phenolphthalein test indicates that the paste precured in water for a shorter time is more quickly carbonated than that for a longer time. The content of calcium hydroxide increases with increasing the procuring time in water, whereas, the amount of absorbed carbon dioxide changes contrarily. Scanning electron microscope (SEM) observation shows that portlandite always fills up big air bubbles in the paste during precuring in water, and the mercury intrusion porosimetry (MIP) results show that there are less large capillary pores in the paste precured in water for a longer time. It is found that the paste without precuring in water has more carbon dioxide absorption during curing in carbon dioxide atmosphere, and its total pore volume decreases remarkably with an increase in the carbonation time than that precured in water. X-ray diffraction (XRD) and Brunauer-Emmett-Teller (BET) surface area analyses indicate that the carbonate products are vaterite and calcite; CxSHy,, formed from carbonation has low BET surface area in comparison with that of C-S-H formed from curing in water.

  13. Cements containing by-product gypsum

    Energy Technology Data Exchange (ETDEWEB)

    Bensted, J. [University of Greenwich, London (United Kingdom). School of Biological and Chemical Sciences

    1995-12-31

    Chemical by-product gypsum can readily replace natural gypsum in Portland cements and in blended cements like Portland pfa cement and Portland blast furnace cement without technical detriment in many instances. Indeed, sometimes the technical performance of the cement can be enhanced. The hydration chemistry is often changed, in that where there is at least some retardation of setting, more AFT phase (ettringite) is formed during early hydration at the expense of calcium silicate hydrates. By-product gypsum can also replace natural gypsum in speciality products like calcium aluminate cement-Portland cement mixes for producing quick setting cements and in calcium sulphoaluminate-type expansive cements. However, by-products gypsum have proved to be less successful for utilization in API Classes of oilwell cements, because of the greater difficulty in obtaining batch-to-batch consistency in properties like thickening time and slurry rheology. 11 refs., 3 figs., 5 tabs.

  14. Metakaolin sand – a promising addition for Portland cement

    Directory of Open Access Journals (Sweden)

    Janotka, I.

    2010-06-01

    Full Text Available The kaolin sand resource at the Vyšný Petrovec quarry in Slovakia comes to a total of 20 megatonnes. The metakaolin material obtained by heating kaolin sand at 650 ºC contains from 31.5 to 40% (wt metakaolinite, as well as illite, muscovite, quartz and feldspar. The aim of this study was to verify whether this calcined sand (MK1 is a pozzolanic material and characterize the cements and mortars prepared with it. The hydration reactions taking place in the blends were assessed with conduction calorimetry, X-ray diffraction (XRD and differential thermal analysis-thermogravimetry (DTA-TG. Blend and mortar strength development and pore structure were also evaluated. The results obtained showed that this metakaolin sand (MK-1 is a pozzolanic material apt for use as a cement addition and for making mortars.

    Las reservas de arena caolínica de la cantera eslovaca de Vyšný Petrovec ascienden a un total de 20 millones de toneladas. El material metacaolínico, que resulta al calentar la arena caolínica a 650 ºC, contiene entre un 31,5 y un 40% de metacaolinita, además de ilita, moscovita, cuarzo y feldespato. El objetivo de este estudio ha sido comprobar que esa arena calcinada es un material puzolánico; así como caracterizar los cementos y morteros preparados con dicha arena (MK-1. La hidratación de las mezclas se evaluó mediante calorimetría de conducción, y difracción de rayos X (DRX y Análisis térmico-diferencial y termogravimétrico (ATD-TG. Se ha evaluado el desarrollo resistente de las mezclas y morteros; así como su estructura porosa. Los resultados obtenidos han demostrado que esa arena metacolínica (MK-1 es un material puzolánico y que podría utilizarse como adición al cemento y en la preparación de morteros.

  15. The Property of Portland Cement and its Employment in Dentistry: Review of the Literature

    Directory of Open Access Journals (Sweden)

    Antonio Vinícius Holanda BARBOSA

    2007-03-01

    Full Text Available Objective: The aim of the present study was to investigate the performance of the Portland cement when used as material in the dentistry. Methods: It was accomplished a bibliographical research using scientific goods published in national and international literature, which intended to evaluate the physical properties, chemical and biological behavior, as well as the antimicrobial activity of this product. In the selected article, the authors used methods of investigation in vitro and in vivo for study comparing the cement with materials consecrated in dentistry. Conclusion: In agreement with the consulted bibliography it was possible to ensure the similarity in the chemical composition between the Portland cement and the MTA, in the effectiveness of the sealing ability of the roads areas between the root canal and the periodontal tissue, satisfactory antimicrobial action, and demonstrate favorable biological properties, stimulating the deposition of the cement and inducing the reparative pulpar answer.

  16. Use of copper slag in the manufacture of Portland cement

    Directory of Open Access Journals (Sweden)

    Aquilar Elguézabal, A.

    2006-03-01

    Full Text Available Given its chemical and mineralogical characteristics, copper slag, a solid industrial by-product, may serve as a partial substitute for silica and hematite in raw mixes used to manufacture Portland cement clinker. The benefits of such substitution include lower production costs and energy savings. The effect of slag-containing raw mixes on the reactivity of the CaO-Si02-Al203-Fe203 system was studied at three temperatures (1,350, 1,400 and 1,450ºC. Four mixes were used: M-1 and M-2 prepared with conventional prime materials and M-3 and M-4, in which ignimbrite and hematite were substituted for slag. In M-3 the slag replaced 45.54% of the ignimbrite and 100% of the hematite, and in M-4 100% of the mineral iron. The samples were clinkerized at 1,350, 1,400 and 1,450ºC. At 1,400ºC, clinker M-3 was found to have 10.7% less free lime than M-1, while the level in M-4 it was 15.93% lower than in M-2. The presence of the main clinker phases was confirmed by X-ray diffraction, which also showed that adding slag during c/inker manufacture slightly improves raw mix burnability without generating new unwanted phases. Consequently, recovery in cement kilns would appear to be an economically and environmentally feasible alternative to coprocessing such waste, although the industrial use of slag depends on its heavy metal content.En acuerdo con las características químicas y mineralógicas de la escoria de cobre, este residuo sólido industrial puede ser utilizado en el proceso de fabricación de clínker Portland como sustituto parcial de los minerales de sílice y hematita en la formación de mezclas crudas cuyos beneficios serían: disminución de los costos de producción de mezclas crudas y del consumo calorífico. El efecto de la adición de la escoria en las mezclas crudas sobre la reactividad del sistema CaO-Si02-Al203-Fe20 3 se estudió en tres niveles de temperatura (1.350, 1.400 Y 1.450ºC. Se trabajó con cuatro mezclas crudas, M-1 y M

  17. Hydration of Hybrid Alkaline Cement Containing a Very Large Proportion of Fly Ash: A Descriptive Model

    Directory of Open Access Journals (Sweden)

    Inés Garcia-Lodeiro

    2016-07-01

    Full Text Available In hybrid alkaline fly ash cements, a new generation of binders, hydration, is characterized by features found in both ordinary portland cement (OPC hydration and the alkali activation of fly ash (AAFA. Hybrid alkaline fly ash cements typically have a high fly ash (70 wt % to 80 wt % and low clinker (20 wt % to 30 wt % content. The clinker component favors curing at ambient temperature. A hydration mechanism is proposed based on the authors’ research on these hybrid binders over the last five years. The mechanisms for OPC hydration and FA alkaline activation are summarized by way of reference. In hybrid systems, fly ash activity is visible at very early ages, when two types of gel are formed: C–S–H from the OPC and N–A–S–H from the fly ash. In their mutual presence, these gels tend to evolve, respectively, into C–A–S–H and (N,C–A–S–H. The use of activators with different degrees of alkalinity has a direct impact on reaction kinetics but does not modify the main final products, a mixture of C–A–S–H and (N,C–A–S–H gels. The proportion of each gel in the mix does, however, depend on the alkalinity generated in the medium.

  18. Effects of Using Pozzolan and Portland Cement in the Treatment of Dispersive Clay

    OpenAIRE

    Vakili, A. H.; Selamat, M. R.; H. Moayedi

    2013-01-01

    Use of dispersive clay as construction material requires treatment such as by chemical addition. Treatments to dispersive clay using pozzolan and Portland cement, singly and simultaneously, were carried out in this study. When used alone, the optimum amount of pozzolan required to treat a fully dispersive clay sample was 5%, but the curing time to reduce dispersion potential, from 100% to 30% or less, was 3 month long. On the other hand, also when used alone, a 3% cement content was capable o...

  19. Reaction of CO2 and brine at the interface between Portland cement and casing steel: Application to CO2 sequestration

    Science.gov (United States)

    Carey, J. W.; Zhang, J.; Lichtner, P. C.; Grigg, R.; Svec, B.; Pawar, R.

    2008-12-01

    Prediction of CO2 leakage through wellbore systems is a multiscale problem in geologic sequestration. In order for wellbore leakage to occur, km-scale processes must deliver CO2 from the point of injection to the wellbore. But, in order for the wellbore to actually leak, μm-scale processes must operate to allow CO2 to flow up the wellbore. In this study, we describe experiments and modeling of microscale processes accompanying CO2 leakage along the cement-casing interface. This work fits within a broader predictive study of CO2 sequestration performance (Viswanathan et al. 2008, Env Sci and Tech, in press) that includes calculation of CO2-migration times to wellbores. Experiments carried out in this report consisted of synthetic wellbore systems constructed of Portland cement and casing-grade steel in which a mixture of CO2 and brine were forced along the cement-casing interface at in situ sequestration conditions (40 °C and 14 MPa). The CO2-brine mixture was pre- equilibrated by flow through limestone before encountering the cement-casing composite. (The limestone- equilibrated fluid was calculated to be strongly out of equilibrium with both cement and the casing.) We used a high CO2-brine flux (10-20 ml/hour along the interface) and hypothesized that the interface would widen with time due to dissolution of either or both cement and steel. In addition to experiments, we conducted reactive transport modeling of cement reactivity using FLOTRAN, which was modified to allow representation of solid solution in the dominant cement phase, calcium-silicate-hydrate. We also developed a corrosion model for the steel. The experimental results showed that the steel was more reactive than the Portland cement. Extensive deposits or oxidation products of FeCO3-rich material developed at the interface and in some places led to an apparent closure of the interface despite the large flux through the system. In contrast, alteration of the cement appeared to be limited by

  20. Assessment of the interaction of Portland cement-based materials with blood and tissue fluids using an animal model

    Science.gov (United States)

    Schembri Wismayer, P.; Lung, C. Y. K.; Rappa, F.; Cappello, F.; Camilleri, J.

    2016-01-01

    Portland cement used in the construction industry improves its properties when wet. Since most dental materials are used in a moist environment, Portland cement has been developed for use in dentistry. The first generation material is mineral trioxide aggregate (MTA), used in surgical procedures, thus in contact with blood. The aim of this study was to compare the setting of MTA in vitro and in vivo in contact with blood by subcutaneous implantation in rats. The tissue reaction to the material was also investigated. ProRoot MTA (Dentsply) was implanted in the subcutaneous tissues of Sprague-Dawley rats in opposite flanks and left in situ for 3 months. Furthermore the material was also stored in physiological solution in vitro. At the end of the incubation time, tissue histology and material characterization were performed. Surface assessment showed the formation of calcium carbonate for both environments. The bismuth was evident in the tissues thus showing heavy element contamination of the animal specimen. The tissue histology showed a chronic inflammatory cell infiltrate associated with the MTA. MTA interacts with the host tissues and causes a chronic inflammatory reaction when implanted subcutaneously. Hydration in vivo proceeds similarly to the in vitro model with some differences particularly in the bismuth oxide leaching patterns. PMID:27683067

  1. Comparative Analysis of Selected Physicochemical Properties of Pozzolan Portland and MTA-Based Cements.

    Science.gov (United States)

    Dorileo, Maura Cristiane Gonçales Orçati; Villa, Ricardo Dalla; Guedes, Orlando Aguirre; Aranha, Andreza Maria Fábio; Semenoff-Segundo, Alex; Bandeca, Matheus Coelho; Borges, Alvaro Henrique

    2014-01-01

    Physicochemical properties of pozzolan Portland cement were compared to ProRoot MTA and MTA BIO. To test the pH, the samples were immersed in distilled water for different periods of time. After the pH analysis, the sample was retained in the plastic recipient, and the electrical conductivity of the solution was measured. The solubility and radiopacity properties were evaluated according to specification 57 of the American National Standard Institute/American Dental Association (ANSI/ADA). The statistical analyses were performed using ANOVA and Tukey's test at a 5% level of significance. Pozzolan Portland cement exhibited pH and electrical conductivity mean values similar to those of the MTA-based cements. The solubilities of all tested materials were in accordance with the ANSI/ADA standards. Only the MTA-based cements met the ANSI/ADA recommendations for radiopacity. It might be concluded that the pH and electrical conductivity of pozzolan Portland cement are similar to and comparable to those of MTA-based cements.

  2. Rheological Properties of Very High-Strength Portland Cement Pastes: Influence of Very Effective Superplasticizers

    Directory of Open Access Journals (Sweden)

    Adriano Papo

    2010-01-01

    Full Text Available The influence of the addition of very effective superplasticizers, that are commercially available, employed for maximising the solid loading of very high-strength Portland cement pastes, has been investigated. Cement pastes were prepared from deionized water and a commercially manufactured Portland cement (Ultracem 52.5 R. Cement and water were mixed with a vane stirrer according to ASTM Standard C305. The 0.38 to 0.44 water/cement ratio range was investigated. Three commercial superplasticizing agents produced by Ruredil S.p.a. were used. They are based on a melamine resin (Fluiment 33 M, on a modified lignosulphonate (Concretan 200 L, and on a modified polyacrylate (Ergomix 1000. Rheological tests were performed at 25°C by using the rate controlled coaxial cylinder viscometer Rotovisko-Haake 20, system M5-osc., measuring device MV2P with serrated surfaces. The tests were carried out under continuous flow conditions. The results of this study were compared with those obtained in a previous article for an ordinary Portland cement paste.

  3. Microstructure and mechanical properties of microwave-assisted heating of pozzolan-Portland cement paste at a very early stage

    Directory of Open Access Journals (Sweden)

    Natt Makul

    2013-12-01

    Full Text Available Portland-pozzolan cement pastes at a very early stage subjecting to microwave heating were investigated. Microwave with a 2.45 GHz and multimode cavity was used for the experiments. The pastes containing pozzolan materials (pulverized fuel ash, metakaolin and silica fume were proportioned with a 0.38 water/solid mass ratio and a 20% by weight replacement of total solid content. It was observed that the temperature increased continuously during microwave heating. Some ettringite rods and amorphous C-S-H fibers appear at 4 hrs. The metakaolin-cement paste exhibited little difference between the watercured and microwave-cured pastes. For the silica fume-cement paste the SF particles under microwave curing had dispersed more than with the 4 hr–cement paste. The produced phases included calcium silicate hydrate, calcium hydroxide and xenotile. The pastes can be developed in compressive strength quite rapidly and also consumed more Ca(OH2 in the pozzolan reaction to produce more C-S-H.

  4. Physical and Thermodynamical Properties of Water Phases in Hardening Portland Cement Systems

    DEFF Research Database (Denmark)

    Hansen, T. Bæk

    The present study is devoted to the description of water phases in hardening portland cement paste systems containing a significant amount of micro-filler and having a low to moderate water/powder ratio. Emphasis has been placed on the early stages of the hardening process....

  5. Steel foundry electric arc furnace dust management: stabilization by using lime and Portland cement.

    Science.gov (United States)

    Salihoglu, Guray; Pinarli, Vedat

    2008-05-30

    The purpose of this study was to determine an appropriate treatment for steel foundry electric arc furnace dust (EAFD) prior to permanent disposal. Lime and Portland cement (PC)-based stabilization was applied to treat the EAFD that contains lead and zinc above the landfilling limits, and is listed by USEPA as hazardous waste designation K061 and by EU as 10 02 07. Three types of paste samples were prepared with EAFD content varying between 0 and 90%. The first type contained the EAFD and Portland cement, the second contained the EAFD, Portland cement, and lime, and the third contained the EAFD and lime. All the samples were subjected to toxicity characteristics leaching procedure (TCLP) after an air-curing period of 28 days. pH changes were monitored and acid neutralization capacity of the samples were examined. Treatment effectiveness was evaluated in terms of reducing the heavy metal leachability to the levels below the USEPA landfilling criteria. An optimum composition for the EAFD stabilization was formulated as 30% EAFD +35% lime +35% Portland cement to achieve the landfilling criteria. The pH interval, where the solubility of the heavy metals in the EAFD was minimized, was found to be between 8.2 and 9.4.

  6. Microstructure engineering of Portland cement pastes and mortars through addition of ultrafine layer silicates

    DEFF Research Database (Denmark)

    Lindgreen, Holger; Geiker, Mette; Krøyer, Hanne;

    2008-01-01

    Pozzolanic submicron-sized silica fume and the non-pozzolanic micron- and nano-sized layer silicates (clay minerals) kaolinite, smectite and palygorskite have been used as additives in Portland cement pastes and mortars. These layer silicates have different particle shape (needles and plates), su...

  7. Prediction of compressive strength up to 28 days from microstructure of Portland cement

    DEFF Research Database (Denmark)

    Svinning, K.; Høskuldsson, Agnar; Justnes, H.

    2008-01-01

    The influence of the characteristics or the microstructure of Portland cement on compressive strength up to 28 days has been statistically investigated by application of partial least square (PLS) analysis. The main groups of characteristics were mineralogy and superficial microstructure represen...

  8. Puzzolanic cements of greater resistance at the attack of selenitic waters than the high sulfate resistance portland cements, and viceverse

    Directory of Open Access Journals (Sweden)

    Talero, Rafael

    1987-09-01

    Full Text Available This work confirms the certainty of the predictions of useful service given by Kaluosek and al. for the sulphate resistant portland cements (type V, USA, subject to severe selenitic attack. Two sulphate resistant portland cements, were tested by means of the Le Chatelier Anstett method. The tarts were destroyed at ages of three years, having detected in them the presence of thaumasite by XRD. Even so, the impossibility and possibility thaumasite formation was confirmed in pozzolanic cements tarts, which either had or did not have adequate amount of pozzolana (diatomite for such purpose.

    Este trabajo confirman las predicciones de vida útil dadas por Kalousek y colaboradores, para los cementos portland de elevada resistencia al ataque de los iones sulfato (tipo V, USA, sometidos a un severo ataque selenitoso. Se ensayaron dos cementos portland de elevada resistencia al ataque del yeso, mediante el ensayo de Le Chatelier-Anstett. Sus tortas correspondientes se destruyeron a la edad de tres años, habiéndose detectado en las mismas la presencia de thaumasita por DRX. Asimismo se confirmó la imposibilidad y posibilidad de formación de thaumasita en tortas de cementos puzolánicos, los cuales tenían, o no, respectivamente, una adecuada cantidad de puzolana (diatomita para tales fines.

  9. Properties of expansive cements, made with Portland cement, gypsum and high alumina cement

    Directory of Open Access Journals (Sweden)

    Monfore, G. E.

    1966-03-01

    Full Text Available Not availableLos cementos expansivos se han desarrollado durante las tres décadas pasadas, principalmente por las investigaciones llevadas a cabo en Francia, URSS y Estados Unidos. Los cementos expansivos que fueron utilizados en los estudios de los cuales se da cuenta en el presente trabajo se obtuvieron mediante la mezcla de cemento Portland, cemento aluminoso y yeso. En las investigaciones se utilizaron morteros con los cuales se pudo determinar los efectos de la composición, tiempo y temperatura de curado sobre las resistencias, dilatación libre, retracción y desarrollo de resistencias en probetas pretensadas. Se hace una revisión sobre los estudios hechos con cementos expansivos y desarrollados en la Universidad de California. Las propiedades de taIes hormigones son, en términos generales, comparables a aquellos obtenidos con mezclas de cementos portland, cemento aluminoso y yeso. Es necesaria más información sobre pérdidas de tensión en los aceros y durabilidad de los hormigones autopretensados.

  10. A Thermoelectric Waste-Heat-Recovery System for Portland Cement Rotary Kilns

    Science.gov (United States)

    Luo, Qi; Li, Peng; Cai, Lanlan; Zhou, Pingwang; Tang, Di; Zhai, Pengcheng; Zhang, Qingjie

    2015-06-01

    Portland cement is produced by one of the most energy-intensive industrial processes. Energy consumption in the manufacture of Portland cement is approximately 110-120 kWh ton-1. The cement rotary kiln is the crucial equipment used for cement production. Approximately 10-15% of the energy consumed in production of the cement clinker is directly dissipated into the atmosphere through the external surface of the rotary kiln. Innovative technology for energy conservation is urgently needed by the cement industry. In this paper we propose a novel thermoelectric waste-heat-recovery system to reduce heat losses from cement rotary kilns. This system is configured as an array of thermoelectric generation units arranged longitudinally on a secondary shell coaxial with the rotary kiln. A mathematical model was developed for estimation of the performance of waste heat recovery. Discussions mainly focus on electricity generation and energy saving, taking a Φ4.8 × 72 m cement rotary kiln as an example. Results show that the Bi2Te3-PbTe hybrid thermoelectric waste-heat-recovery system can generate approximately 211 kW electrical power while saving 3283 kW energy. Compared with the kiln without the thermoelectric recovery system, the kiln with the system can recover more than 32.85% of the energy that used to be lost as waste heat through the kiln surface.

  11. Pulp tissue response to Portland cement associated with different radio pacifying agents on pulpotomy of human primary molars.

    Science.gov (United States)

    Marques, N; Lourenço Neto, N; Fernandes, A P; Rodini, C; Hungaro Duarte, M; Rios, D; Machado, M A; Oliveira, T

    2015-12-01

    The objective of this research was to evaluate the response of Portland cement associated with different radio pacifying agents on pulp treatment of human primary teeth by clinical and radiographic exams and microscopic analysis. Thirty mandibular primary molars were randomly divided into the following groups: Group I - Portland cement; Group II - Portland cement with iodoform (Portland cement + CHI3 ); Group III - Portland cement with zirconium oxide (Portland cement + ZrO2 ); and treated by pulpotomy technique (removal of a portion of the pulp aiming to maintain the vitally of the remaining radicular pulp tissue using a therapeutic dressing). Clinical and radiographic evaluations were recorded at 6, 12 and 24 months follow-up. The teeth at the regular exfoliation period were extracted and processed for histological analysis. Data were tested using statistical analysis with a significance level of 5%. The microscopic findings were descriptively analysed. All treated teeth were clinically and radiographically successful at follow-up appointments. The microscopic analysis revealed positive response to pulp repair with hard tissue barrier formation and pulp calcification in the remaining roots of all available teeth. The findings of this study suggest that primary teeth pulp tissue exhibited satisfactory biological response to Portland cement associated with radio pacifying agents. However, further studies with long-term follow-up are needed to determine the safe clinical indication of this alternative material for pulp therapy of primary teeth.

  12. Efeito do tempo de cura na rigidez de argamassas produzidas com cimento Portland Effect of the curing time on the stiffness of mortars produced with Portland cement

    Directory of Open Access Journals (Sweden)

    G. C. R. Garcia

    2011-03-01

    Full Text Available O concreto de cimento Portland é um dos materiais mais usados no mundo inteiro, entretanto, devido a sua estrutura ser muito complexa, torna-se imprescindível estudar suas propriedades com bastante profundidade. O concreto é produzido a partir de uma argamassa, de areia e cimento, com adição de agregados graúdos, sendo que suas propriedades estão basicamente suportadas nessa argamassa de constituição. O objetivo deste trabalho foi estudar a variação da rigidez de duas argamassas de composições com razão cimento:areia de 1:2 e 1:3 em função do tempo de cura, tendo como parâmetro a variação do módulo de Young. Os resultados mostraram que o módulo de Young cresce até atingir o valor máximo no oitavo dia, sendo que nos três primeiros dias esse crescimento é mais acentuado. A análise dos resultados indica que grande parte do processo de hidratação do cimento, com formação das ligações químicas responsáveis pela rigidez da argamassa, acontece nos primeiros dias de cura.Concrete produced with Portland cement is one of building materials most widely used worldwide. However, due to its highly complex structure, its properties require in-depth studies. Concrete is a mortar consisting of a mixture of cement, sand and coarse aggregates, and its properties are represented basically by the mortar base. The aim of this work was to study the change in stiffness of two mortar compositions cured at 25 ºC with a cement-to-sand ratio of 1:2 and 1:3, as a function of curing time using the variation of Young modulus as the measuring parameter. The results showed that Young modulus increases up to a maximum value on the 8th day, and that this increase is more pronounced during the first three days. An analysis of the results indicates that a large part of the cement hydration process, involving the formation of chemical bonds that are responsible for the mortar stiffness, takes place in the early days of curing.

  13. Corrosion of steel bars in cracked concrete made with ordinary portland, slag and fly ash cements

    Energy Technology Data Exchange (ETDEWEB)

    Mohammed, T.U.; Yamaji, T.; Hamada, H. [Port and Harbor Research Inst., Ministry of Land, Infrastructure and Transport (Japan); Aoyama, T. [PS Corp. (Japan)

    2001-07-01

    A study was conducted in which the marine durability of ordinary portland cement, slag and fly ash cement was examined using 15 year old plain and reinforced concrete cylindrical specimens. The performance of these cements was then examined for pre-cracked reinforced concrete prism samples. The process of manufacturing cement emits huge amounts of carbon dioxide into the global atmosphere. Replacing a portion of the cement with by-products from the steel industry and thermal power plants (which are both huge emitters of carbon dioxide) can lower carbon dioxide emissions and also solve the disposal issue of slag and fly ash while increasing the long-term durability of concrete structures. In this study, concrete cylindrical specimens were made of ordinary portland cement, slag and fly ash cements. The specimens were 100 x 100 x 600 mm prisms of different types of cement. Water-to-cement ratios were 0.45 and 0.55. Both tap water and seawater were used as mixing water. The samples were exposed in tidal pools for 15 years to evaluate the compressive strength of the concrete, corrosion of the steel bars, and chloride-ion concentrations in the concrete. It was shown that, with the exception of fly ash cements, the compressive strength of most cements increased after 15 years of exposure compared to its 28 day strength. Type C slag cement demonstrated the best performance against chloride-ion at the surface of concrete made with slag and fly ash. Voids in the steel-concrete interface make it possible for corrosion pits to develop. The use of seawater as mixing water results in earlier strength development at 28 days and does not cause to the strength of the concrete to regress after 15-years of exposure, but it causes more corrosion of steel bars at a lower cover depth. Corrosion of steel bars is not an issue at deeper cover depths. 15 refs., 19 tabs., 13 figs.

  14. The Influence of Diatomite on the Strength and Microstructure of Portland Cement

    OpenAIRE

    Liu Jun; Shao Peng; Wang Shihao

    2016-01-01

    To study the influence of the types and mixing amount of diatomite on the Portland cement, we prepared the cement specimen doped with the calcined first-grade, first-grade and second-grade diatomite ,tested the 3d, 7d, 14d compressive strength, and studied and discussed phase, structure and morphology of diatomite in the binary system by the method of XRD, SEM . Experimental results show that with the addition of diatomite, the strength of cement paste increase; the optimal contents of calcin...

  15. Mechanical properties of Portland cement and its constituents at the nano-level

    Science.gov (United States)

    French, Brent Alexander

    The following is a summary of research for a portion of the project titled Nano to Continuum Multi-Scale Modeling Techniques and Analysis For Cementitious Materials Under Dynamic Loading in association with North Carolina Agricultural & Technical State University and the US Army. This research investigates several attempts at creating a better Portland cement model at the atomistic level through molecular dynamics simulations. These models are modified to simulate damage to the basic cement structure, and are simulated using several combinations of forcefields and molecular dynamics tools. Experimental techniques such as nanoindentation, atomic force microscopy, and x-ray diffraction are applied to Portland cement samples to correlate mechanical properties among these techniques, as well as the numerical simulations.

  16. Properties of Portland-Composite Cements with metakaolin: Commercial and manufactured by Thermal Activation of Serbian Kaolin Clay

    Directory of Open Access Journals (Sweden)

    Mitrovic A.

    2012-09-01

    Full Text Available Portland-composite cements (CEM II were prepared with addition of 5 to 35% of metakaolin (MK, manufactured by thermal activation/calcination of Serbian kaolin clay, and commercial matakaolin (CMK. Performance of the composite cements was evaluated, through the setting time (initial and final, compressive strengths (for ages 2, 7, 28, 90 and 180 days and soundness, and compared with control cement (Portland cement – CEM I. Setting time (initial and final is accelerated in Portlandcomposite cements, for both metakaolins used. The acceleration is higher in cement with addition of commercial metakaolin. Lower compressive strength is obtained after 2 days of curing for all Portland-composite cements in comparison with control cement, since pozzolanic reaction still did not show its effect. After 7 days, pozzolanic reaction show its effect, manifested as compressive strength increase of Portland-composite cements with addition of up to 35% of CMK, and 25% in the case of cements with MK. After 28 days compressive strength was higher than that for control cement for cements prepared with addition of CMK, and with addition of up to 25% MK. After 90 days increased compressive strength was noticed with addition of 10 - 20% of CMK, and with 10 and 15% of MK, while after 180 days addition of both metakaolins influences compressive strength decrease. The results of the soundness, 0.5 mm for CEM I, and 1.0 mm in most Portland-composite cements indicate soundness increase with addition of metakaolins. Generally, better performance of Portland-composite cements was obtained with addition of commercial metakaolin, which may be attributed to the differences in the pozzolanic activity of the applied metakaolins, 20.5 MPa and 14.9 MPa for CMK and MK, respectively. By our previous findings pozzolanic activity of the thermally activated clay may be increased by subsequent milling of the metakaolin manufactured by thermal activation process.

  17. 76 FR 34252 - Notice Pursuant to the National Cooperative Research and Production Act of 1993; Portland Cement...

    Science.gov (United States)

    2011-06-13

    ... Cement Association Notice is hereby given that, on May 12, 2011, pursuant to Section 6(a) of the National Cooperative Research and Production Act of 1993, 15 U.S.C. 4301 et seq. (``the Act''), Portland Cement... specified circumstances. Specifically, Drake Cement, LLC, Scottsdale, AZ; Argos USA Corporation, Houston,...

  18. The use of glass powder as a partial Portland cement replacement

    Science.gov (United States)

    Pokorný, Jaroslav; Pavlíková, Milena; Tydlitát, Vratislav; Scheinherrová, Lenka; Rovnaníková, Pavla; Pavlík, Zbyšek

    2017-07-01

    Finely grinded waste glass powder can become material having suitable properties from the point of view of particle size and pozzolanic activity. Glass powder incorporation into cement paste and cement-based composites can bring improvement in porous structure resulting in increased mechanical strength and durability characteristics. On this account, two types of recycled glass powder are investigated in the presented paper as a possible partial Portland cement substitutes in cement blends. For raw glass powders, basic physical parameters and chemical composition are measured. The studied glass powders are applied as 5, 10 and 20 mass% of Portland cement replacement in cement paste mix composition, whereas water/binder ratio of 0.3 is used for all studied pastes. Fresh paste mixtures are characterized using initial and final setting time measurement. For hardened pastes cured 28 days in water, bulk density, matrix density, total open porosity and mechanical properties represented by flexural and compressive strength are accessed. Portlandite consumption by the pozzolanic reaction is monitored with TGA. The obtained results show effectiveness of a borosilicate glass powder that acts as a pozzolanic active admixture. This resulted in improvement of mechanical characteristics for cement substitution up to 10 mass%.

  19. Feasibility study of the Portland cement industry waste for the reduction of energy consumption

    Energy Technology Data Exchange (ETDEWEB)

    Bernardo, Ana Carla de Souza Masselli; Junqueira, Mateus Augusto F. Chaib; Jorge, Ariosto Bretanha; Silva, Rogerio Jose da [Universidade Federal de Itajuba (UNIFEI), MG (Brazil). Institute of Mechanical Engineering]. E-mails: anacarlasz@unifei.edu.br; mateus_afcj@yahoo.com.br; ariosto.b.jorge@unifei.edu.br; rogeriojs@unifei.edu.br

    2008-07-01

    The Portland cement industry demand a high specific consumption of energy for the production of the clinker. The energy consumption for clinker production varies between 3000 and 5300 kJ/kg of produced clinker. The clinker is produced by blending of different raw materials in order t o achieve precise chemical proportions of lime, silica, alumina and iron in the finished product and by burning them at high temperatures. The Portland cement is a mixture of clinker, gypsum and other materials. Due to need of high temperatures, tradition ally the fuels used in the cement industry are mineral coal, fuel oil, natural gas and petroleum coke. The fuel burning in high temperature leads to the formation of the pollutant thermal NOx. The level of emissions of this pollutant is controlled by environmental law, thus the formation of pollutants in process need be controlled. Moreover, industrial waste has been used by Portland cement industries as a secondary fuel through a technique called co -processing. Materials like waste oils, plastics, waste tyres and sewage sludge are often proposed as alternative fuels for the cement industry. The residues can be introduced as secondary fuel or secondary raw material. For energy conservation in the process, mineralizers are added during the process production of the clinker. The mineralizers promote certain reactions which decrease the temperature in the kiln and improve the quality of the clinker. The adequate quantity of constituents in production process is complex, for maintain in controlled level, the quality of final product, the operational conditions of kiln, and the pollutant emissions. The purpose of the present work is to provide an analysis of an optimal production point through of the optimization technique considering, the introduction of the fuels, industrial wastes as secondary fuels, and raw materials, for the reduction of energy in the process of Portland cement production. (author)

  20. Immobilization of Co (Ⅱ) Ions in Cement Pastes and Their Effects on the Hydration Characteristics

    Institute of Scientific and Technical Information of China (English)

    Eisa Hekal; Essam Kishar; Wafaa Hegazi; Maha Mohamed

    2011-01-01

    The immobilization of Co (Ⅱ) in various cement matrices was investigated by using the solidification/stabilization (S/S) technique. The different cement pastes used in this study were ordinary Portland cement in absence and presence of water reducing- and water repelling-admixtures as well as blended cement with kaolin. Two ratios of Co (Ⅱ) were used (0.5% and 1.0% by weight of the solid binder). The hydration characteristics of the used cement pastes were tested uia the determination of the combined water content, phase composition and compressive strength at different time intervals up to 180 d. The degree of immobilization of the added heavy metal ions was evaluated by determining the leached ion concentration after time intervals extended up to 180 d. The leachability experiments were carried out by using two modes: the static and the semi-dynamic leaching processes. It was noticed that the concentration of the leached Co2+ ions in the static mode of leachability was lower than the solubility of its hydroxide in all the investigated cement pastes.

  1. Effect on Hydration and Hardening of Tricalcium Phosphate Bone Cement

    Institute of Scientific and Technical Information of China (English)

    2005-01-01

    The bioactive α-Ca3 (PO4)2 bone cement was studied by XRD , SEM and isothermal calorimetric measurements. The results showed that a mixed pattern of TCP and hydroxylapatite were obtained after hydration and hardening. The mechanism of hydration and hardening of the α-Ca3 ( PO4 )2 was dissolution-precipitation,(NH4) H2 PO4 was the best set accelerator to the α-Ca3 ( PO4 )2 cement, and the HAP powers and the(NH4) H2 PO4 concentration had a great effect on the hydration rate of α-Ca3 ( PO4 )2.

  2. High-volume natural volcanic pozzolan and limestone powder as partial replacements for portland cement in self-compacting and sustainable concrete

    KAUST Repository

    Celik, Kemal

    2014-01-01

    A laboratory study demonstrates that high volume, 45% by mass replacement of portland cement (OPC) with 30% finely-ground basaltic ash from Saudi Arabia (NP) and 15% limestone powder (LS) produces concrete with good workability, high 28-day compressive strength (39 MPa), excellent one year strength (57 MPa), and very high resistance to chloride penetration. Conventional OPC is produced by intergrinding 95% portland clinker and 5% gypsum, and its clinker factor (CF) thus equals 0.95. With 30% NP and 15% LS portland clinker replacement, the CF of the blended ternary PC equals 0.52 so that 48% CO2 emissions could be avoided, while enhancing strength development and durability in the resulting self-compacting concrete (SCC). Petrographic and scanning electron microscopy (SEM) investigations of the crushed NP and finely-ground NP in the concretes provide new insights into the heterogeneous fine-scale cementitious hydration products associated with basaltic ash-portland cement reactions. © 2013 Published by Elsevier Ltd.

  3. Development of the Portland cement slurries with diatomaceous earth to the oil industry; Desenvolvimento de pastas de cimento Portland com adicao de diatomita para a industria do petroleo

    Energy Technology Data Exchange (ETDEWEB)

    Brito, Roseane A; Melo, Dulce M.A.; Martinelli, Antonio E.; Simao, Cristina A.; Paiva, Maria D.M. [Universidade Federal do Rio Grande do Norte (UFRN), Natal, RN (Brazil); Melo, Marcus A.F. [PETROBRAS, Rio de Janeiro, RJ (Brazil). Centro de Pesquisas (CENPES)

    2004-07-01

    The class-G Portland cement has been used with success in oil well cementing. The material is usually shipped to the Northeast Brazil, because the only plant that manufactures class-G is located in Cantagalo/RJ. The present work investigates the influence of the partial substitution of Portland cement by diatomaceous earth, aiming at reducing the costs in oil well cementing, improving the slurry properties and using local raw material. The diatomaceous earth has pozzolanic properties and can be used as extenders of cement slurries. This properties added to the lower cost and availability of this material in Northeast Brazil, make the diatomaceous earth a candidate material to produce light cements, to well conditions in advanced phases of production. It were evaluated the rheological properties of the slurries (at 25 and 52 deg C), volume of free water, compressive strength after curing for 8, 24 and 48 h at 38 deg C, and consistometry tests. The results show that the diatomaceous earth maintain the viscosity values and gel force suitable for use in oil well cementing. No free water was observed in the formulations. It was also verified that the compressive strength of slurries hardened with diatomaceous earth is similar to those with only Portland cement and that the minimum compressive strength of 300 psi, after curing for 8 h was reached. The thickening time was longer than the average value and the application value. (author)

  4. Coupled effect of cement hydration and temperature on hydraulic behavior of cemented tailings backfill

    Institute of Scientific and Technical Information of China (English)

    WU Di; CAI Si-jing

    2015-01-01

    Cemented tailings backfill (CTB) is made by mixing cement, tailings and water together, thus cement hydration and water seepage flow are the two crucial factors affecting the quality of CTB. Cement hydration process can release significant amount of heat to raise the temperature of CTB and in turn increase the rate of cement hydration. Meanwhile, the progress of cement hydration consumes water and produces hydration products to change the pore structures within CTB, which further influences the hydraulic behavior of CTB. In order to understand the hydraulic behavior of CTB, a numerical model was developed by coupling the hydraulic, thermal and hydration equations. This model was then implemented into COMSOL Multiphysics to simulate the evolutions of temperature and water seepage flow within CTB versus curing time. The predicted outcomes were compared with correspondent experimental results, proving the validity and availability of this model. By taking advantage of the validated model, effects of various initial CTB and curing temperatures, cement content, and CTB's geometric shapes on the hydraulic behavior of CTB were demonstrated numerically. The presented conclusions can contribute to preparing more environmentally friendly CTB structures.

  5. Interaction of ordinary Portland cement and Opalinus Clay: Dual porosity modelling compared to experimental data

    Science.gov (United States)

    Jenni, A.; Gimmi, T.; Alt-Epping, P.; Mäder, U.; Cloet, V.

    2017-06-01

    Interactions between concrete and clays are driven by the strong chemical gradients in pore water and involve mineral reactions in both materials. In the context of a radioactive waste repository, these reactions may influence safety-relevant clay properties such as swelling pressure, permeability or radionuclide retention. Interfaces between ordinary Portland cement and Opalinus Clay show weaker, but more extensive chemical disturbance compared to a contact between low-pH cement and Opalinus Clay. As a consequence of chemical reactions porosity changes occur at cement-clay interfaces. These changes are stronger and may lead to complete pore clogging in the case of low-pH cements. The prediction of pore clogging by reactive transport simulations is very sensitive to the magnitude of diffusive solute fluxes, cement clinker chemistry, and phase reaction kinetics. For instance, the consideration of anion-depleted porosity in clays substantially influences overall diffusion and pore clogging at interfaces. A new concept of dual porosity modelling approximating Donnan equilibrium is developed and applied to an ordinary Portland cement - Opalinus Clay interface. The model predictions are compared with data from the cement-clay interaction (CI) field experiment in the Mt Terri underground rock laboratory (Switzerland), which represent 5 y of interaction. The main observations such as the decalcification of the cement at the interface, the Mg enrichment in the clay detached from the interface, and the S enrichment in the cement detached from the interface, are qualitatively predicted by the new model approach. The model results reveal multiple coupled processes that create the observed features. The quantitative agreement of modelled and measured data can be improved if uncertainties of key input parameters (tortuosities, reaction kinetics, especially of clay minerals) can be reduced.

  6. Spectroscopic and microscopic characterization of portland cement based unleached and leached solidified waste

    Science.gov (United States)

    Salaita, Ghaleb N.; Tate, Philip H.

    1998-05-01

    In this study, portland cement based solidified/stabilized (S/S) waste and a cement-only control were studied before and after leaching. The solidified waste samples were prepared from a mix of organic-containing industrial waste sludge and portland cement. Toxicity characterization leaching procedure (TCLP) was the leaching test employed. The samples were studied using multi-surface analytical techniques including XPS, SIMS, XRD, FE-SEM and EDS. The data obtained from the various techniques show that leaching does not measurably affect the morphology or composition of the solidified waste sample. However, subtle changes in the composition of the cement control sample were observed. While the concentration of the elements observed on the surface of leached and unleached waste samples by XPS are very similar (except for Mg, Na and N), study of the corresponding cement samples exhibit differences in the level of C, Si, S, and Ca. The unleached cement sample shows lower levels of C and Si, but higher levels of O, S, Ca and Mg, indicating that leaching alters the cement sample. EDS analyses of the elemental composition of the bulk of the leached and unleached waste samples are similar, and also are similar for the leached and unleached cement samples, indicating that under the conditions of the TCLP test, leaching has no effect on the bulk. The high level of Ca present on the surface of the solidified waste indicates entrapment of the waste by the cement. The information and results obtained show that the surface analytical techniques used in this work, when combined with environmental wet methods, can provide a more complete picture of the concentration, chemical state and immobility of solidified waste.

  7. Clinical and computed tomographic evaluation of portland cement pulpotomy in primary molar: A case report

    Directory of Open Access Journals (Sweden)

    Kamrun Nahar

    2016-08-01

    Full Text Available The present case describes the clinical & radiographic outcome of a Portland Cement pulpotomy. The 5 years old girl presenting extensive carious exposure in her mandibular left 2nd deciduous molar and was suffering pain in her left lower jaw only on exposure to cold for last 2 days. She was ultimately diagnosed clinic-radio-graphically as a case of irreversible pulpitis. Coronal pulpotomy procedure was carried out in the responsible tooth and Portland cement (PC was applied as a medicament after pulpotomy. At the 3 & 6-months follow-up appointments, treated tooth was asymptomatic clinically and radiographic examinations revealed no sign of periradicular pathosis in the pulpotomized teeth. Additionally, the formation of a dentin bridge immediately below the PC in the treated tooth was confirmed by RVG and CBCT.

  8. Radiopacity evaluation of Portland and MTA-based cements by digital radiographic system

    Directory of Open Access Journals (Sweden)

    Alvaro Henrique Borges

    2011-06-01

    Full Text Available OBJECTIVE: The aim of the present study was to evaluate the radiopacity of Portland and MTA-based cements using the Digora TM digital radiographic system. MATERIAL AND METHODS: The performed tests followed specification number 57 from the American National Standard Institute/American Dental Association (2000 for endodontic sealing materials. The materials were placed in 5 acrylic plates, especially designed for this experiment, along with a graduated aluminum stepwedge varying from 1 to 10 mm in thickness. The set was radiographed at a 30 cm focus-object distance and with 0.2 s exposure time. After the radiographs were taken, the optical laser readings of radiographs were performed by Digora TM system. Five radiographic density readings were performed for each studied material and for each step of the aluminum scale. RESULTS: White ProRoot MTA (155.99±8.04, gray ProRoot MTA (155.96±16.30 and MTA BIO (143.13±16.94 presented higher radiopacity values (p<0.05, while white non-structural Portland (119.76±22.34, gray Portland (109.71±4.90 and white structural Portland (99.59±12.88 presented lower radiopacity values (p<0.05. CONCLUSIONS: It was concluded that MTA-based cements were the only materials presenting radiopacity within the ANSI/ADA specifications.

  9. Ageing of portland cement concrete cured under moist conditions

    NARCIS (Netherlands)

    Yu, Z.; Ye, G.; Van Breugel, K.; Chen, W.

    2014-01-01

    Deterioration of microstructure in cement concrete will cause changes in the transport properties of the concrete. Transport properties at different ages of the concrete provide information about the microstructural changes of the material. A way to measure the transport properties, i.e. the chlorid

  10. Petrographic Analysis of Portland Cement Concrete Cores from Pease Air National Guard Base, New Hampshire

    Science.gov (United States)

    2016-11-01

    Petrographic Analysis of Portland Cement Concrete Cores from Pease Air National Guard Base, New Hampshire E n g in e e r R e s e a rc h a n d...id, age of the concrete being evaluated and tests performed...4 3 Preface This study was conducted in support of the Air Force Civil Engineer Center (AFCEC) to assess concrete obtained from Pease

  11. Comparative Analysis of Selected Physicochemical Properties of Pozzolan Portland and MTA-Based Cements

    OpenAIRE

    Dorileo, Maura Cristiane Gonçales Orçati; Villa, Ricardo Dalla; Guedes, Orlando Aguirre; Aranha, Andreza Maria Fábio; Semenoff-Segundo, Alex; Bandeca, Matheus Coelho; Borges, Alvaro Henrique

    2014-01-01

    Physicochemical properties of pozzolan Portland cement were compared to ProRoot MTA and MTA BIO. To test the pH, the samples were immersed in distilled water for different periods of time. After the pH analysis, the sample was retained in the plastic recipient, and the electrical conductivity of the solution was measured. The solubility and radiopacity properties were evaluated according to specification 57 of the American National Standard Institute/American Dental Association (ANSI/ADA). Th...

  12. Influence of Crumb-Rubber in the Mechanical Response of Modified Portland Cement Concrete

    OpenAIRE

    Retama, J.; Ayala, A. G.

    2017-01-01

    The influence of crumb-rubber on the mechanical properties of Portland cement concrete (PCC) is studied by experimental tests and numerical simulations. The main hypothesis of the study is that replacing part of the stone aggregate with crumb-rubber in the mix modifies the energy dissipation during the cracking process and affects the concrete behaviour under monotonically increasing loads. The experimental research program characterizes the mechanical properties of PCC for three different ty...

  13. Mineral Trioxide Aggregate and Portland Cement for Direct Pulp Capping in Dog: A Histopathological Evaluation

    Directory of Open Access Journals (Sweden)

    Maryam Bidar

    2014-09-01

    Full Text Available Background and aims. Mineral trioxide aggregate and calcium hydroxide are considered the gold standard pulp-capping materials. Recently, Portland cement has been introduced with properties similar to those of mineral trioxide aggregate. His-topathological effects of direct pulp capping using mineral trioxide aggregate and Portland cements on dog dental pulp tis-sue were evaluated in the present study. Materials and methods. This histopatological study was carried out on 64 dog premolars. First, the pulp was exposedwith a sterile bur. Then, the exposed pulp was capped with white or gray mineral trioxide aggregates and white or gray Port-land cements in each quadrant and sealed with glass-ionomer. The specimens were evaluated under a light microscope after 6 months. Statistical analysis was carried out using Kruskal-Wallis test. Statistical significance was defined at α=5%. Results. There was no acute inflammation in any of the specimens. Chronic inflammation in white and gray mineral triox-ide aggregates and white and gray Portland cements was reported to be 45.5%, 27.3%, 57.1% and 34.1%, respectively. Al-though the differences were not statistically significant, severe inflammation was observed mostly adjacent to white mineral trioxide aggregate. The largest extent of increased vascularization (45% and the least increase in fibrous tissue were ob-served adjacent to white mineral trioxide aggregate, with no significant differences. In addition, the least calcified tissue formed adjacent to white mineral trioxide aggregate, although the difference was not significant. Conclusion. The materials used in this study were equally effective as pulp protection materials following direct pulp cap-ping in dog teeth.

  14. Effect of blastfurnace slag addition to Portland cement for cationic exchange resins encapsulation

    Directory of Open Access Journals (Sweden)

    Stefan L.

    2013-07-01

    Full Text Available In the nuclear industry, cement-based materials are extensively used to encapsulate spent ion exchange resins (IERs before their final disposal in a repository. It is well known that the cement has to be carefully selected to prevent any deleterious expansion of the solidified waste form, but the reasons for this possible expansion are not clearly established. This work aims at filling the gap. The swelling pressure of IERs is first investigated as a function of ions exchange and ionic strength. It is shown that pressures of a few tenths of MPa can be produced by decreases in the ionic strength of the bulk solution, or by ion exchanges (2Na+ instead of Ca2+, Na+ instead of K+. Then, the chemical evolution of cationic resins initially in the Na+ form is characterized in CEM I (Portland cement and CEM III (Portland cement + blastfurnace slag cements at early age and an explanation is proposed for the better stability of CEM III material.

  15. PEMANFAATAN FLY ASH SEBAGAI BAHAN CAMPURAN PEMBUATAN PORTLAND POSSOLAN CEMENT (PPC (Utilization of Fly Ash as A Mixing in Portland Pozzolan Cement (PPC Production

    Directory of Open Access Journals (Sweden)

    Ambo Upe

    2006-11-01

    Full Text Available ABSTRAK Fly ash atau abu terbang (Kode Limbah D 22.3 merupakan salah satu produk hasil pembakaran batubara yang dihasilkan PT. Semen Tonasa sebesar rata-rata 72.36 ton/hari. Telah dicoba memanfaatkan fly ash sebagai bahan campuran semen untuk menghasilkan Portland Pozzolan Cement (PPC. Selain itu, dilakukan uji Toxicity Characteristic Leaching Procedure (TCLP serta analisis kandungan logam berat dari fly ash dan PPC tersebut.  Hasil perocobaan menunjukkan bahwa fly ash memenuhi persaratan sebagai bahan campuran PPC dan memenuhi syarat peraturan pemerintah No.85/1999 tentang Pengelolaan Llimbah Bahan Berbahaya dan Beracun.   ABSTRACT Fly ash (Disposal code: D 223 is disposal produced in coal burning process of PT. Semen Tonasa. It is estimated that the produced fly ash are 72.36 ton/day. In this paper, the study examines the possibility of utilization the fly ash as a mixing material in fabrication of Portland Pozzoland Cement (PPC. Experimental results show that the produced PPC meets the standard quality requirement. The Toxicity Characteristic Leaching Procedure (TCLP also has been performed to analysis the heavy metal contained in the fly ash and PPC materials. This test indicates that all results for TCLP Metals property fill the Indonesian Government Regulation for Hazardous Waste as described in PP No. 85/1999

  16. The effects of utilizing silica fume in Portland Cement Pervious Concrete

    Science.gov (United States)

    Mann, Daniel Allen

    Silica fume has long been used as a supplementary cementing material to provide a high density, high strength, and durable building material. Silica fume has a particle size a fraction of any conventional cement, which allows it to increase concrete strength by decreasing the porosity especially near the aggregates surface. Because Portland Cement Pervious Concrete (PCPC) has a smaller bond area between aggregate and paste, silica fume has significant impacts on the properties of the PCPC. The research in this paper studies the workability of a cement paste containing silica fume in addition to analyzing the results of testing on Portland Cement Pervious Concrete mixtures that also contained silica fume. Testing conducted included a study of the effects of silica fume on cement's rheological properties at various dosage rates ranging from zero to ten percent by mass. It was determined that silica fume has negligible effects on the viscosity of cement paste until a dosage rate of five percent, at which point the viscosity increases rapidly. In addition to the rheological testing of the cement paste, trials were also conducted on the pervious concrete samples. Sample groups included mixes with river gravel and chipped limestone as aggregate, washed and unwashed, and two different void contents. Workability tests showed that mixtures containing a silica fume dosage rate of 5 percent or less had comparable or slightly improved workability when compared to control groups. Workability was found to decrease at a 7 percent dosage rate. Samples were tested for compressive strength at 7 and 28 days and splitting tensile strength at 28 days. It was found in most sample groups, strength increased with dosage rates of 3 to 5 percent but often decreased when the dosage reached 7 percent. Abrasion testing showed that both samples containing washed aggregate and samples containing silica fume exhibited a reduced mass loss.

  17. Effects of using pozzolan and Portland cement in the treatment of dispersive clay.

    Science.gov (United States)

    Vakili, A H; Selamat, M R; Moayedi, H

    2013-01-01

    Use of dispersive clay as construction material requires treatment such as by chemical addition. Treatments to dispersive clay using pozzolan and Portland cement, singly and simultaneously, were carried out in this study. When used alone, the optimum amount of pozzolan required to treat a fully dispersive clay sample was 5%, but the curing time to reduce dispersion potential, from 100% to 30% or less, was 3 month long. On the other hand, also when used alone, a 3% cement content was capable of reducing dispersion potential to almost zero percent in only 7 days; and a 2% cement content was capable of achieving similar result in 14 days. However, treatment by cement alone is costly and could jeopardize the long term performance. Thus, a combined 5% pozzolan and 1.5% cement content was found capable of reducing dispersion potential from 100% to zero percent in 14 days. The results indicate that although simultaneous treatment with pozzolan and cement would extend the required curing time in comparison to treatment by cement alone of a higher content, the task could still be carried out in a reasonable period of curing time while avoiding the drawbacks of using either pozzolan or cement alone.

  18. Effects of Using Pozzolan and Portland Cement in the Treatment of Dispersive Clay

    Directory of Open Access Journals (Sweden)

    A. H. Vakili

    2013-01-01

    Full Text Available Use of dispersive clay as construction material requires treatment such as by chemical addition. Treatments to dispersive clay using pozzolan and Portland cement, singly and simultaneously, were carried out in this study. When used alone, the optimum amount of pozzolan required to treat a fully dispersive clay sample was 5%, but the curing time to reduce dispersion potential, from 100% to 30% or less, was 3 month long. On the other hand, also when used alone, a 3% cement content was capable of reducing dispersion potential to almost zero percent in only 7 days; and a 2% cement content was capable of achieving similar result in 14 days. However, treatment by cement alone is costly and could jeopardize the long term performance. Thus, a combined 5% pozzolan and 1.5% cement content was found capable of reducing dispersion potential from 100% to zero percent in 14 days. The results indicate that although simultaneous treatment with pozzolan and cement would extend the required curing time in comparison to treatment by cement alone of a higher content, the task could still be carried out in a reasonable period of curing time while avoiding the drawbacks of using either pozzolan or cement alone.

  19. Comparative SEM study of the marginal adaptation of white and grey MTA and Portland cement.

    Science.gov (United States)

    Bidar, Maryam; Moradi, Saeed; Jafarzadeh, Hamid; Bidad, Salma

    2007-04-01

    The use of a suitable substance that prevents egress of potential contaminants into the periapical tissues is important in endodontic surgery. The aim of the present study was to compare the marginal adaptation of three root-end filling materials (white mineral trioxide aggregate (MTA), grey MTA and Portland cement), using scanning electron microscopy. Seventy-five single-rooted extracted human teeth were used. The canals were instrumented and filled with gutta-percha. Following root-end resection and cavity preparation, root-end cavities were filled with white MTA, grey MTA or Portland cement. Using a diamond saw, roots were longitudinally sectioned into two halves. Under scanning electron microscopy, the gaps between the material and dentinal wall were measured. The data were analysed using Kruskal-Wallis test. The mean of the gap in grey MTA, white MTA and Portland cement was 211.6, 349 and 326.3 microm, respectively. The results indicate that the gap between grey MTA and the dentinal wall is less than other materials, but there was no significant difference between the materials tested in this study (P > 0.05).

  20. Contribution to Portland cement hemihydrite and gypsum content determination

    Directory of Open Access Journals (Sweden)

    Moreno Arús, F.

    1974-09-01

    Full Text Available Not availableLa mayoría de los técnicos de cemento eceptan que las anormalidades del fraguado, conocidas como "falso fraguado" en el cemento portland, se deben primordialmente a la presencia de yeso parcialmente deshidratado (SO4Ca 1/2H2O. Si el clinker que se muele está enriquecido en cal libre, o la temperatura del molino es elevada (superior a los 110 ºC o hay escasa ventilación de éste, se llega a originar una parcial deshidratación del yeso, que se mantiene durante el proceso de ensilado y origina las anormalidades del fraguado anteriormente referidas. Por esta razón creemos muy importante el poder conocer el grado de deshidratación en que se encuentra el yeso en un cemento.

  1. Biocompatibility assessment of modified Portland cement in comparison with MTA® : In vivo and in vitro studies

    Directory of Open Access Journals (Sweden)

    I Khalil

    2012-01-01

    Full Text Available Aim: The aim of our study is to elaborate a new cement based on Portland cement (PC, Modified Portland Cement (MPC with modified chemical and physical properties that allow easier clinical manipulation and faster setting time than MTA® and then to evaluate its cytotoxicity in vitro and its biocompatibility in vivo in comparison with MTA® . Materials and Methods: Elaboration of MPC: Portland cement powder slenderly grinded to homogenize the particles, mixed with a radiopaque element and a setting time accelerator. A comparative in vitro study (MTS test of the toxic effect of MTA® and MPC with culture isolated from the calvaria of 18-day-old fetal Swiss OF1 mice are done. A comparative in vivo study of the biocompatibility of MTA® and MPC: Under general anaesthesia, three holes (2.5 mm were made in both the left and right femurs of six White New Zealand rabbits. In the first hole MPC is placed, in the second MTA® and the third one is left empty (negative control group. Three weeks after implantation, two rabbits are sacrificed, then two other rabbits over six weeks and the last two after twelve weeks. The neck of the femur is trimmed and prepared for undecalcified histological studies. Mann-Whitney test was used to analyze the results. Results: The cell viability test according to the morphological observations suggested the biocompatibility of the two biomaterials tested. The in vivo test showed similar biocompatibility between MTA® and MPC. Bone healing and minimal inflammatory response adjacent to MTA® and MPC implants were observed at all experimental periods (3, 6 and 12 weeks, suggesting that both materials are well tolerated. Conclusion: This pilot comparative study of MTA® and MPC showed no or very limited toxic effects of both cements in vitro and similar biocompatibility in vivo. However, additional in vivo and clinical studies should be done on MPC before it can be introduced in our clinical practice.

  2. Porous and adsorption properties of hydrated cement paste

    Directory of Open Access Journals (Sweden)

    Marina Biljana S.

    2004-01-01

    Full Text Available Adsorption isotherms of benzene on hydrated cement pastes prepared by cement ground with and without the addition of grinding aids, triethanol amine (TEA and ethylene glycol (EG were investigated. The adsorption isotherms were interpreted by means of the Dubinin-Astakhov (DA and Dubinin-Radushkevich-Stoeckli (DRS equations. The microporous structure of cement gel (C-S-H in the cement pastes, and changes in the Gibbs free energy of adsorption were determined. The mechanical properties of the cement pastes were also measured. It was evident that pastes with additives had different parameters of the DRS and DA equations: the volume and dimensions of the gel pores, the distribution of the dimensions, the characteristic energy of adsorption, and the change in the Gibbs free energy of adsorption. The mechanical properties were also different. The dispersity of the additive-containing ground cements had a favorable effect on the hydration processes. When applying TEA, it was also necessary to analyze its influence on the chemical behavior of hydration in the starting period.

  3. INVESTIGATING EFFECTS OF INTRODUCTION OF CORNCOB ASH INTO PORTLAND CEMENTS CONCRETE: MECHANICAL AND THERMAL PROPERTIES

    Directory of Open Access Journals (Sweden)

    Antonio Price

    2014-01-01

    Full Text Available The purpose of this study was to evaluate the benefits of replacing Ordinary Portland Cement (OPC with Corncob Ash (CCA blended cements. The cement industry contributes considerable amount of Carbon Dioxide (CO2 emissions into the atmosphere. The main contribution of CO2 emissions from cement production results from the process of creating Calcium Oxide (CaO from limestone (CaCO3 commonly known as the calcination process. Blending OPC with a pozzolanic material will assist in the reduction of CO2 emissions due to calcination as well as enhance the quality of OPC. There are various pozzolanic materials such as fly ash, rice husk, silica fume and CCA that could be promising partial replacement for OPC. In this study, CCA will serve as the primary blending agent with OPC. An experiment was performed to designate an appropriate percentage replacement of CCA that would comply with specific standards of cement production. The experimental plan was designed to analyze compressive strength, workability and thermal performance of various CCA blended cements. The data from the experiment indicates that up to 10% CCA replacement could be used in cement production without compromising the structural integrity of OPC. In addition, it was found that the compressive strength and workability of the resulting concrete could be improved when CCA is added to the mixtures. Furthermore, it was shown that the introduction of 10% CCA can lead to significant reduction in thermal conductivity of the mixture.

  4. The microstructure of Portland cement paste and its relationship to drying shrinkage: A study of blended cement paste

    Science.gov (United States)

    Olson, Rudolph Andrew, III

    1998-12-01

    The objective was to understand how the microstructure of cement paste influences its susceptibility to drying shrinkage. The strategy was to vary the microstructure via processing and relate the changes to the deformation behavior. There were many processing parameters to choose from that were capable of varying the microstructure, but one very effective way was through addition of mineral admixtures. Since the use of mineral admixtures also has the potential to address current economic, social, and environmental problems, achieving a better understanding of blended cement paste was an added benefit. Ground granulated blast furnace slag, fly ash, and silica fume were the mineral admixtures chosen for this study because they represent a wide range of reactivity. Blended cement pastes of various compositions and degrees of hydration were characterized. Calcium hydroxide, calcium silicate hydrate, pH, free water, and nitrogen surface area were the microstructural parameters chosen for analysis. Because calcium silicate hydrate is usually measured by indirect techniques which are not applicable to blended cements, a technique based on water adsorption was developed; results compared favorably with calculations from the Jennings-Tennis hydration model. The connectivity of the pore network was characterized using impedance spectroscopy. Drying shrinkage was analyzed on the macrolevel using bulk shrinkage measurements and the microstructural level using a deformation mapping technique. Several processing-microstructure-property relationships were developed. Mineral admixtures were found to significantly reduce the connectivity of the pore network and increase the nitrogen surface area of cement paste per gram of calcium silicate hydrate. The bulk drying shrinkage of blended cement pastes dried to 50% relative humidity was found to depend primarily on calcium hydroxide and calcium silicate hydrate content; shrinkage decreased with increasing amounts of calcium hydroxide

  5. Chemical characterization and bioactivity of epoxy resin and Portland cement-based sealers with niobium and zirconium oxide radiopacifiers.

    Science.gov (United States)

    Viapiana, Raqueli; Guerreiro-Tanomaru, Juliane Maria; Hungaro-Duarte, Marco Antonio; Tanomaru-Filho, Mário; Camilleri, Josette

    2014-09-01

    The purpose of this study was to characterize and to evaluate the bioactivity potential of experimental root canal sealers (ES) based on Portland cement, epoxy resin with nano- and micro-particles of niobium or zirconium oxide used as radiopacifiers in comparison to AH Plus and MTA Fillapex. Specimens of the sealers (10 mm in diameter×1 mm thick) were prepared and the radiopacity was evaluated according to ISO 6876 (2012) specifications. Characterization of the sealers was performed under the scanning electron microscope (SEM) immediately after setting and after immersion for 28 days in Hank's balanced salt solution (HBSS). In addition X-ray energy dispersive spectroscopy (EDS), X-ray diffraction (XRD) and Fourier transform infrared (FT-IR) spectroscopy were also performed. The pH and calcium ion release were measured after 1, 7, 14, 21 and 28 days after completion of seating using a digital pH meter and an atomic absorption spectrophotometer, respectively. The experimental sealers exhibited an average radiopacity of 2.5 mm thickness of aluminum, which was similar to MTA Fillapex (P>0.05) and inferior to AH Plus (Pepoxy resin and radiopacifier exhibited a degree of bioactivity although no evidence of cement hydration was demonstrated on material characterization. The radiopacifier particle size had limited effect on the sealer microstructure and chemical properties. Copyright © 2014 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  6. Use of coir pith particles in composites with Portland cement.

    Science.gov (United States)

    Brasileiro, Gisela Azevedo Menezes; Vieira, Jhonatas Augusto Rocha; Barreto, Ledjane Silva

    2013-12-15

    Brazil is the fourth largest world's producer of coconut (Cocos nucifera L.). Coconut crops generate several wastes, including, coir pith. Coir pith and short fibers are the byproducts of extracting the long fibers and account for approximately 70% of the mature coconut husk. The main use of coir pith is as an agricultural substrate. Due to its shape and small size (0.075-1.2 mm), this material can be considered as a particulate material. The aim of this study was to evaluate the use of coir pith as an aggregate in cementitious composites and to evaluate the effect of the presence of sand in the performance of these composites. Some composites were produced exclusively with coir pith particles and other composites with coir pith partially substituting the natural sand. The cementitious composites developed were tested for their physical and mechanical properties and characterized by X-ray diffraction, scanning electron microscopy, energy dispersive X-ray spectroscopy and Fourier transform infrared spectroscopy to evaluate the effect of coir pith particles addition in cement paste and sand-cement-mortar. The statistical significance of the results was evaluated by one-way analysis of variance (ANOVA) test followed by multiple comparisons of the means by Tukey's test that showed that the composites with coir pith particles, with or without natural sand, had similar mechanical results, i.e., means were not statistically different at 5% significance level. There was a reduction in bulk density and an improved post-cracking behavior in the composites with coir pith particles compared to conventional mortar and to cement paste. These composites can be used for the production of lightweight, nonstructural building materials, according to the values of compressive strength (3.97-4.35 MPa) and low bulk density (0.99-1.26 g/cm(3)).

  7. Reaction of rat subcutaneous tissue to mineral trioxide aggregate and Portland cement: A secondary level biocompatibility test

    Directory of Open Access Journals (Sweden)

    P Karanth

    2013-01-01

    Full Text Available Objectives: This secondary-level animal study was conducted to assess and compare the subcutaneous tissue reaction to implantation of white mineral trioxide aggregate (MTA and white Portland cement. Study Design: Polyethylene tubes filled with either freshly mixed white MTA (Group I or white Portland cement (Group II were implanted subcutaneously into 12 Wistar Albino rats. Each animal also received an empty polyethylene tube as the control (Group III. After 7, 14, 21 and 30 days, the implants, together with surrounding tissues were excised. Two pathologists blinded to the experimental procedure, evaluated sections taken from the biopsy specimens for the severity of the inflammatory response, calcification and the presence and thickness of fibrous capsule surrounding the implant. Statistical analysis was performed using the Cross-tabs procedure, Univariate analysis of the variance two-way and the Pearson product moment correlation to assess inter-rater variability between the two evaluators. Results: At 7 days, there was no significant difference in the severity of inflammation between the control group, white MTA, and white Portland cement groups. In the 14 day, 21 day and 30 day test periods, control group had significantly less inflammation than white MTA and white Portland cement. There was no significant difference in the grading of inflammation between white MTA and white Portland cement. All materials exhibited thick capsule at 7 days and thin capsule by 30 days. Conclusion: Both white MTA and white Portland cement were not completely non-irritating at the end of 30 days as evidenced by the presence of mild inflammation. However, the presence of a thin capsule around the materials, similar to the control group, indicates good tissue tolerance. White MTA and white Portland cement seem to be materials of comparable biocompatibility.

  8. Glycerol Salicylate-based Pulp-Capping Material Containing Portland Cement.

    Science.gov (United States)

    Portella, Fernando Freitas; Collares, Fabrício Mezzomo; Santos, Paula Dapper; Sartori, Cláudia; Wegner, Everton; Leitune, Vicente Castelo Branco; Samuel, Susana Maria Werner

    2015-01-01

    The purpose of this study was to evaluate the water sorption, solubility, pH and ability to diffuse into dentin of a glycerol salicylate-based, pulp-capping cement in comparison to a conventional calcium hydroxide-based pulp capping material (Hydcal). An experimental cement was developed containing 60% glycerol salicylate resin, 10% methyl salicylate, 25% calcium hydroxide and 5% Portland cement. Water sorption and solubility were determined based on mass changes in the samples before and after the immersion in distilled water for 7 days. Material discs were stored in distilled water for 24 h, 7 days and 28 days, and a digital pHmeter was used to measure the pH of water. The cement's ability to diffuse into bovine dentin was assessed by Raman spectroscopy. The glycerol salicylate-based cement presented higher water sorption and lower solubility than Hydcal. The pH of water used to store the samples increased for both cements, reaching 12.59 ± 0.06 and 12.54 ± 0.05 after 7 days, for Hydcal and glycerol salicylate-based cements, respectively. Both cements were able to turn alkaline the medium at 24 h and sustain its alkalinity after 28 days. Hydcal exhibited an intense diffusion into dentin up to 40 µm deep, and the glycerol salicylate-based cement penetrated 20 µm. The experimental glycerol salicylate-based cement presents good sorption, solubility, ability to alkalize the surrounding tissues and diffusion into dentin to be used as pulp capping material.

  9. Effect of saliva and blood contamination on the bi-axial flexural strength and setting time of two calcium-silicate based cements: Portland cement and biodentine.

    Science.gov (United States)

    Alhodiry, W; Lyons, M F; Chadwick, R G

    2014-03-01

    This study evaluated the effect of contamination with saliva and blood on the bi-axial flexural strength and setting time of pure gray Portland cement and Biodentine (Septodont, Allington, UK). A one-way ANOVA showed that contamination caused no significant difference between the cements in bi-axial flexural strength (P> 0.05). However there was a significant difference in setting time (Pcement taking longer than Biodentine, regardless of the contaminant, and contamination with blood increased the setting time of both materials. Biodentine was similar in strength to Portland cement, but had a shorter setting time for both contaminated and non-contaminated samples.

  10. Lime kiln dust as a potential raw material in portland cement manufacturing

    Science.gov (United States)

    Miller, M. Michael; Callaghan, Robert M.

    2004-01-01

    In the United States, the manufacture of portland cement involves burning in a rotary kiln a finely ground proportional mix of raw materials. The raw material mix provides the required chemical combination of calcium, silicon, aluminum, iron, and small amounts of other ingredients. The majority of calcium is supplied in the form of calcium carbonate usually from limestone. Other sources including waste materials or byproducts from other industries can be used to supply calcium (or lime, CaO), provided they have sufficiently high CaO content, have low magnesia content (less than 5 percent), and are competitive with limestone in terms of cost and adequacy of supply. In the United States, the lime industry produces large amounts of lime kiln dust (LKD), which is collected by dust control systems. This LKD may be a supplemental source of calcium for cement plants, if the lime and cement plants are located near enough to each other to make the arrangement economical.

  11. Properties of Portland cement concretes containing pozzolanic admixtures

    Science.gov (United States)

    Simmons, D. D.; Pasko, T. J., Jr.; Jones, W. R.

    1981-04-01

    A laboratory comparison was made of the properties of a concrete containing no pozzolan with several mixtures containing pozzolans. Used were a natural pozzolan (Lassenite), two fly ashes of different fineness and low carbon and an amorphous silica fume dust from a metal-producing plant. One cement, one coarse crushed limestone aggregate, and one fine river aggregate were used. Replacing a faster reacting binder with a slower one, produced lower early strengths and adversely affected the properties which are highly dependent on strength. The measures of durability were greatly affected by the air contents and aging or treatment prior to exposure. The amorphous silica fume dust increased the early strengths of a fly ash mixture.

  12. Dry-grinded ultrafine cements hydration. physicochemical and microstructural characterization

    Directory of Open Access Journals (Sweden)

    Foteini Kontoleontos

    2013-04-01

    Full Text Available The aim of the present research work was the evaluation of the physicochemical and microstructural properties of two ultrafine cements, produced by dry grinding of a commercial CEM I 42.5N cement. The effect of grinding on particle size distribution was determined by laser scattering analyzer. All cements were tested for initial and final setting times, consistency of standard paste, soundness, flow of normal mortar and compressive strengths after 1, 2, 7 and 28 days. The effect of the fineness on the heat of hydration was also investigated. The hydration products were determined by X-ray diffraction analysis and by Fourier transform infrared spectroscopy, at 1, 2, 7 and 28 days. The microstructure of the hardened cement pastes and their morphological characteristics were examined by scanning electron microscopy. Porosity and pore size distribution were evaluated by mercury intrusion porosimetry. The effects of greater fineness on compressive strengths were evident principally at early ages. After the first 24 hours of hydration, the compressive strength of the finest cements was about 3 times higher (over 48 MPa than the corresponding of CEM I 42.5N (15.1 MPa.

  13. Prospection of Portland cement raw material: A case study in the Marmara region of Turkey

    Science.gov (United States)

    Özgüner, A. M.

    2014-09-01

    Representative sampling of the raw materials used to make Portland cement, correct calculations for the possible clinker mixtures, sufficient reserves of the raw materials and selection of the correct infrastructure for the location of a cement factory are essential to the protection of the great investment in the factory. The results of chemical analyses of pipe samples taken in the field at right angles to the strikes of favourable limestone, clay, shale, and marl outcrops were used in Kind's lime saturation formula for clinker calculations of the possible mixtures. The cement modulus values were calculated using the corresponding clinker oxide ratios and were confirmed to be within the standard intervals for positive cement raw material mixtures. The most promising raw material source, a double lithologic mixture of limestone and mudstone was found during the prospection in north of Bilecik Province, where rhyolitic tuff outcrops with pozzolanic properties also exist. Some marble quarries nearby have been inclined to dispose of their marble wastes for use in cement production to prevent polluting the environment with them. The nearby Gemlik fertiliser factory provides inexpensive waste gypsum that can be used as a cool cement mixing material. The limestone, mudstone and trass raw material reserves in this area were calculated to be sufficient for the factory's requirements for more than 100 years of operation as results of the detailed geological mapping. The regional infrastructure is most suitable for distribution and marketing of cement products. The cement factory described in this study has been producing cement for the last 3 years, after coring and testing of the raw material reserves.

  14. Carbonatation Influence on Fly Ash and Portland Cement Mortars

    Directory of Open Access Journals (Sweden)

    P.L. Valdez–Tamez

    2009-01-01

    Full Text Available The influence of carbonation on mortars containing 25% of fly ash instead of the cementitious materials was studied. Mortar cylinder specimens were fabricated for 4 different W/C ratios: 0.35, 0.45, 0.55 and 0.65. Mortars with and without fly ash were subjected to an accelerated carbonation process. Volumetric weight, water absorption, compressive strength, water permeability, pH and mercury intrusion porosimetry of the mortar specimens were determined. Due to the fly ash pozzolanic potential, for all W/C ratios, results of the compressive strength tests at 28 days of the mortars with and without fly ash were similar. Mortars with fly ash presented similar water permeability as mortars without fly ash. PH results showed that alkalinity reduction is lower in mortars with fly ash compared to those containing cement only. In all the mortars, the porosimetric analysis indicated that porosity is reduced due to carbonation. Further more, it is showed the predominance of the macro and mesopores.

  15. Organic Additive Implantation onto Cement Hydration Products

    Institute of Scientific and Technical Information of China (English)

    ZHU Jipeng; LI Zongjin; YANG Ruochong; ZHANG Yamei

    2014-01-01

    In polymer modified cementitious materials, it is hard to set up a chemical connection between the added polymer and the cement moiety. In this study FS (functional silane) was adopted to form this connection as a bridge component which has the functional group forming bonds with polymer. To testify the connection between FS and cement moiety, Q2/Q1 ratio (Qx:intensity ratio) investigation was carried out by the means of quantitative solid state 29Si MAS NMR. The results show that the Q2/Q1 ratio has increased with the addition of FS which indicates that the silicon chain length has increased, and the quantity of silicon atoms at site of Q2, chain site, has enhanced, showing that the silicon atom of FS has connected to the silicon chain of cement moiety by the bond“-Si-O-Si-”formation.

  16. The Estimation of Compaction Parameter Values Based on Soil Properties Values Stabilized with Portland Cement

    Science.gov (United States)

    Lubis, A. S.; Muis, Z. A.; Pasaribu, M. I.

    2017-03-01

    The strength and durability of pavement construction is highly dependent on the properties and subgrade bearing capacity. This then led to the idea of the selection methods to estimate the density of the soil with the proper implementation of the system, fast and economical. This study aims to estimate the compaction parameter value namely the maximum dry unit weight (γd max) and optimum moisture content (wopt) of the soil properties value that stabilized with Portland Cement. Tests conducted in the laboratory of soil mechanics to determine the index properties (fines and liquid limit) and Standard Compaction Test. Soil samples that have Plasticity Index (PI) between 0-15% then mixed with Portland Cement (PC) with variations of 2%, 4%, 6%, 8% and 10%, each 10 samples. The results showed that the maximum dry unit weight (γd max) and wopt has a significant relationship with percent fines, liquid limit and the percentation of cement. Equation for the estimated maximum dry unit weight (γd max) = 1.782 - 0.011*LL + 0,000*F + 0.006*PS with R2 = 0.915 and the estimated optimum moisture content (wopt) = 3.441 + 0.594*LL + 0,025*F + 0,024*PS with R2 = 0.726.

  17. Chloride adsorption by calcined layered double hydroxides in hardened Portland cement paste

    Energy Technology Data Exchange (ETDEWEB)

    Yoon, Seyoon [School of Engineering, Kings College, University of Aberdeen, Aberdeen AB24 3UE (United Kingdom); Moon, Juhyuk, E-mail: juhyuk.moon@stonybrook.edu [Civil Engineering Program, Department of Mechanical Engineering, State University of New York at Stony Brook, New York 11794 (United States); Bae, Sungchul [Department of Civil and Environmental Engineering, University of California, Berkeley, CA 94720 (United States); Duan, Xiaonan [Department of Materials Science and Engineering, Cornell University, Ithaca, NY 14853 (United States); Giannelis, Emmanuel P. [Department of Materials Science and Engineering, Cornell University, Ithaca, NY 14853 (United States); Center for Refining and Petrochemicals, The Research Institute, King Fahd University of Petroleum and Minerals, Dhahran 31261 (Saudi Arabia); Monteiro, Paulo M. [Department of Civil and Environmental Engineering, University of California, Berkeley, CA 94720 (United States)

    2014-06-01

    This study investigated the feasibility of using calcined layered double hydroxides (CLDHs) to prevent chloride-induced deterioration in reinforced concrete. CLDHs not only adsorbed chloride ions in aqueous solution with a memory effect but also had a much higher binding capacity than the original layered double hydroxides (LDHs) in the cement matrix. We investigated this adsorption in hardened cement paste in batch cultures to determine adsorption isotherms. The measured and theoretical binding capacities (153 mg g{sup −1} and 257 mg g{sup −1}, respectively) of the CLDHs were comparable to the theoretical capacity of Friedel's salt (2 mol mol{sup −1} or 121 mg g{sup −1}), which belongs to the LDH family among cementitious phases. We simulated chloride adsorption by CLDHs through the cement matrix using the Fickian model and compared the simulation result to the X-ray fluorescence (XRF) chlorine map. Based on our results, it is proposed that the adsorption process is governed by the chloride transport through the cement matrix; this process differs from that in an aqueous solution. X-ray diffraction (XRD) analysis showed that the CLDH rebuilds the layered structure in a cementitious environment, thereby demonstrating the feasibility of applying CLDHs to the cement and concrete industries. - Highlights: • We examine the adsorption equilibrium and kinetics of CLDH in the hydrated cement. • CLDH capacity to bind chloride ions in the hydrated cement paste is determined. • We model chloride adsorption by CLDH through the cement matrix. • CLDH reforms the layered structure with ion adsorption in the cement matrix.

  18. Structural characterization of magnesium silicate hydrate: towards the design of eco-sustainable cements.

    Science.gov (United States)

    Tonelli, M; Martini, F; Calucci, L; Fratini, E; Geppi, M; Ridi, F; Borsacchi, S; Baglioni, P

    2016-02-28

    Magnesium-based cement is one of the most interesting eco-sustainable alternatives to standard cementitious binders. The reasons for the interest towards this material are twofold: (i) its production process, using magnesium silicates, brine or seawater, dramatically reduces CO2 emissions with respect to Portland cement production, and (ii) it is very well suited to applications in radioactive waste encapsulation. In spite of its potential, assessment of the structural properties of its binder phase (magnesium silicate hydrate or M-S-H) is far from complete, especially because of its amorphous character. In this work, a comprehensive structural characterization of M-S-H was obtained using a multi-technique approach, including a detailed solid-state NMR investigation and, in particular, for the first time, quantitative (29)Si solid-state NMR data. M-S-H was prepared through room-temperature hydration of highly reactive MgO and silica fume and was monitored for 28 days. The results clearly evidenced the presence in M-S-H of "chrysotile-like" and "talc-like" sub-nanometric domains, which are approximately in a 1 : 1 molar ratio after long-time hydration. Both these kinds of domains have a high degree of condensation, corresponding to the presence of a small amount of silanols in the tetrahedral sheets. The decisive improvement obtained in the knowledge of M-S-H structure paves the way for tailoring the macroscopic properties of eco-sustainable cements by means of a bottom-up approach.

  19. Surface Roughness and Porosity of Hydrated Cement Pastes

    Directory of Open Access Journals (Sweden)

    T. Ficker

    2011-01-01

    Full Text Available . Seventy-eight graphs were plotted to describe and analyze the dependences of the height and roughness irregularities on the water-to-cement ratio and on the porosity of the cement hydrates. The results showed unambiguously that the water-to-cement ratio or equivalently the porosity of the specimens has a decisive influence on the irregularities of the fracture surfaces of this material. The experimental results indicated the possibility that the porosity or the value of the water-to-cement ratio might be inferred from the height irregularities of the fracture surfaces. It was hypothesized that there may be a similarly strong correlation between porosity and surface irregularity, on the one hand, and some other highly porous solids, on the other, and thus the same possibility to infer porosity from the surfaces of their fracture remnants.

  20. Isothermal Calorimetry Study of Blended Cements and its Application in Numerical Simulations

    NARCIS (Netherlands)

    Xiong, X.; Van Breugel, K.

    2001-01-01

    Apparent activation energy (E) is generally used to consider the effect of temperature on the kinetics of cement hydration in the numerical simulation of cement hydration processes. This paper deals with an experimental study on the kinetics of Portland cement and blast furnace slag cement using iso

  1. Dimensional stability of materials based on Portland cement at the early stages

    Science.gov (United States)

    Mesa Yandy, Angélica; Zerbino, Raúl L.; Giaccio, Graciela M.; Russo, Nélida A.; Duchowicz, Ricardo

    2014-09-01

    In this work two fiber optic sensing techniques are used to study the dimensional stability in fresh state of different cementitious materials. A conventional Portland cement mortar and two commercial grouts were selected. The measurements were performed by using a Bragg grating embedded in the material and a non-contact Fizeau interferometer. The first technique was applied in a horizontal sample scheme, and the second one, by using a vertical configuration. In addition, a mechanical length comparator was used in the first case in order to compare the results. The evolution with time of the dimensional changes of the samples and the analysis of the observed behavior are included.

  2. Constitutive modeling of the aging viscoelastic properties of portland cement paste

    Science.gov (United States)

    Grasley, Zachary C.; Lange, David A.

    2007-12-01

    Analytical approaches for modeling aging viscoelastic behavior of concrete include the time-shift approach (analogous to time-temperature superposition), the solidification theory, and the dissolution-precipitation approach. The aging viscoelastic properties of concrete are generally attributed solely to the cement paste phase since the aggregates are typically linear elastic. In this study, the aging viscoelastic behavior of four different cement pastes has been measured and modeled according to both the time-shift approach and the solidification theory. The inability of each individual model to fully characterize the aging viscoelastic response of the materials provides insight into the mechanisms for aging of the viscoelastic properties of cement paste and concrete. A model that considers aging due to solidification in combination with inherent aging of the cement paste gel (modeled using the time-shift approach) more accurately predicted the aging viscoelastic behavior of portland cement paste than either the solidification or time-shift approaches independently. The results provide evidence that solidification and other intrinsic gel aging mechanisms are concurrently active in the aging process of cementitious materials.

  3. Effects of occupational dust exposure on the health status of portland cement factory workers

    Directory of Open Access Journals (Sweden)

    R Manjula

    2013-07-01

    Full Text Available Introduction: Chronic exposure to Portland cement dust has been reported to lead to greater prevalence of various clinical conditions (includes both respiratory and non-respiratory. These conditions are consistently associated with the degree and duration of exposure. Regular use of appropriate personal protective equipment if made available at the work site could protect the cement factory workers from adverse health effects. Objective: To study the morbidity profile of the cement factory workers. Type of Study: Retrospective cohort study. Material and Methods: This study was conducted in the Portland Cement Factory in North Karnataka. Data was collected using predesigned questionnaire by personal interview method and clinical examination. A total of 64 male workers are randomly selected who are working in various departments like crushing, raw/cement mill, rotary kiln and packing department. Equal number of unexposed controls was selected from the area atleast 5 kms from the factory and those who are not exposed to cement dust in the past, who are matched for age, Socio economic status and smoking with the exposed population. Statistical Analysis: Chisquare test for qualitative data and unpaired t test for quantitative data using Epi info. Results: A total of 64 male workers and equal number of matched controls who are not exposed to the cement dust were included in the study. Among exposed maximum of 36% were employed in Crushing department, 25% each in Packing and cement/raw mill. Systolic and Diastolic blood pressure was found to be higher among the exposed, which is statistically highly significant (p<0.001. There is significant increase in weight among exposed (p<0.001. Maximum 29(45.3% of the workers had stuffy nose and epistaxis when compared to unexposed with Relative risk(RR of 2.6, followed by Dermatological complaints and lower respiratory complaints with RR of 2.18 and 2.3 respectively. Conclusion: Personal protective equipment

  4. Influence of chloride in mortar made of Portland cement types II, III, and V on the near-field microwave reflection properties

    Science.gov (United States)

    Hu, Cairong; Benally, Aaron D.; Case, Tobias; Zoughi, Reza; Kurtis, Kimberly

    2000-07-01

    Corrosion of steel rebar in reinforced concrete structures, can be induced by the presence of chloride in the structure. Corrosion of steel rebar is a problematic issue in the construction industry as it compromises the strength and integrity of the structure. Although techniques exist for chloride detection and its migration into a structure, they are destructive, time consuming and cannot be used for the interrogation of large surfaces. In this investigation three different portland cement types; namely, ASTM types II, III and V were used, and six cubic (8' X 8' X 8') mortar specimens were produced all with water-to-cement (w/c) ratio of 0.6 and sand-to-cement (s/c) ratio of 1.5. Tap water was used when producing three of these specimens (one of each cement type). For the other three specimens calcium chloride was added to the mixing tap water resulting in a salinity of 2.5%. These specimens were placed in a hydration room for one day and thereafter left it the room temperature with low humidity. The reflection properties of these specimens, using an open-ended rectangular waveguide probe, were monitored daily at 3 GHz (S-band) and 10 GHz (X-band). The results show the influence of cement type on the reflection coefficient as well as the influence of chloride on the curing process and setting time.

  5. Dielectric properties of portland cement paste as a function of time since mixing

    Science.gov (United States)

    Camp, Paul R.; Bilotta, Stephen

    1989-12-01

    The dielectric properties of portland cement paste and mortar have been measured in the frequency range 100 Hz-7 MHz as a function of time since mixing. Over much of the spectrum, the ac conductance of the samples appears directly related to the amount of unbound water remaining in the sample and ionic conduction predominates. In addition, interesting structure was found in both the conductance and capacitance data at high frequencies as the free water content was reduced. We conclude that relatively simple measurements of this kind can be a useful tool in concrete research and may provide the basis for simple, in situ, nondestructive measurement of the degree of curing of concrete or for monitoring water migration in concrete structures. Measurements on sealed samples of partially or fully cured concrete reveal also the water-cement ratio of the original mix.

  6. Pore size distribution, strength, and microstructure of portland cement paste containing metal hydroxide waste

    Energy Technology Data Exchange (ETDEWEB)

    Majid, Z.A.; Mahmud, H.; Shaaban, M.G.

    1996-12-31

    Stabilization/solidification of hazardous wastes is used to convert hazardous metal hydroxide waste sludge into a solid mass with better handling properties. This study investigated the pore size development of ordinary portland cement pastes containing metal hydroxide waste sludge and rice husk ash using mercury intrusion porosimetry. The effects of acre and the addition of rice husk ash on pore size development and strength were studied. It was found that the pore structures of mixes changed significantly with curing acre. The pore size shifted from 1,204 to 324 {angstrom} for 3-day old cement paste, and from 956 to 263 {angstrom} for a 7-day old sample. A reduction in pore size distribution for different curing ages was also observed in the other mixtures. From this limited study, no conclusion could be made as to any correlation between strength development and porosity. 10 refs., 6 figs., 3 tabs.

  7. Increasing the compressive strength of portland cement concrete using flat glass powder

    Energy Technology Data Exchange (ETDEWEB)

    Miranda Junior, Edson Jansen Pedrosa de; Bezerra, Helton de Jesus Costa Leite; Politi, Flavio Salgado; Paiva, Antonio Ernandes Macedo, E-mail: edson.jansen@ifma.edu.br [Instituto Federal de Educacao, Ciencia e Tecnologia do Maranha (IFMA), Sao Luis, MA (Brazil). Dept. de Mecanica e Materiais

    2014-08-15

    This paper analyzes the compressive strength of Portland cement concrete in response to the incorporation of 5%, 10% and 20% of flat glass powder in place of sand, at w/c (water/cement) ratios of 0.50, 0.55 and 0.58. A statistical analysis of variance (ANOVA) was performed after 7, 14 and 28 days of curing. The compressive strength test results indicate that the concrete containing a w/c ratio of 0.50 can be used for structural applications, regardless of the waste glass content, as can that with a w/c ratio of 0.55 containing 20% of waste glass. We suggest that the use of flat glass powder in place of sand in the above mentioned percentages is feasible for the production of an environmentally appropriate and structurally applicable concrete. However, the concrete's fluidity and void content must be taken into account. (author)

  8. Microstructure Development and Transport Properties of Portland Cement-fly Ash Binary Systems: in view of service life predictions

    OpenAIRE

    Z. Yu

    2015-01-01

    Fly ash is a by-product of burning coal in electric power generating plants. It is commonly known that owing to its pozzolanic properties fly ash is widely used as a partial replacement for Portland cement in concrete. The use of fly ash in concrete not only reduces the landfill costs of fly ash, but also reduces the use of Portland cement in concrete, consequently reduces CO2 emission per ton concrete. More important, the presence of fly ash improves the durability of concrete and extends th...

  9. Improved quantification of alite and belite in anhydrous Portland cements by 29Si MAS NMR: Effects of paramagnetic ions

    DEFF Research Database (Denmark)

    Poulsen, Søren Lundsted; Kocaba, Vanessa; Le Saoût, Gwenn;

    2009-01-01

    The applicability, reliability, and repeatability of 29Si MAS NMR for determination of the quantities of alite (Ca3SiO5) and belite (Ca2SiO4) in anhydrous Portland cement was investigated in detail for 11 commercial Portland cements and the results compared with phase quantifications based...... on powder X-ray diffraction combined with Rietveld analysis and with Taylor-Bogue calculations. The effects from paramagnetic ions (Fe3+) on the spinning sideband intensities, originating from dipolar couplings between 29Si and the spins of the paramagnetic electrons, were considered and analyzed in spectra...

  10. A thermal comparator sensor for measuring autogenous deformation in hardening Portland cement paste

    DEFF Research Database (Denmark)

    Østergaard, Thomas; Jensen, Ole Mejlhede

    2003-01-01

    of the thermal comparator is based on thermal expansion of aluminium. A particular characteristic of the measuring system is the fixation of the thermal comparator sensor to the deforming specimen. The modular system ensures effective thermostatic control of the hydrating cement paste samples. The technique......This paper describes a simple and accurate experimental device specially developed to measure autogenous deformation in hardening cement-based materials. The measuring system consists of a so-called thermal comparator sensor and a modular thermostatically controlled system. The operating principle...

  11. Use of disposed waste ash from landfills to replace Portland cement.

    Science.gov (United States)

    Rukzon, Sumrerng; Chindaprasirt, Prinya

    2009-09-01

    In this study, waste ash was utilized as a pozzolanic material in blended Portland cement in order to reduce negative environmental effects and landfill volume required to dispose of waste ash. The influence of waste ash, namely palm oil fuel ash, rice husk ash and fly ash on compressive strength and sulfate resistance in mortar were studied and evaluated by some accelerated short-term techniques in sodium sulfate solutions. Ordinary Portland cement (OPC) was partially replaced with ground palm oil fuel ash (POA), ground rice husk ash (RHA) and classified fly ash (FA). Single pozzolan and a blend of equal weight portions of POA, RHA and FA were also used. The resistance to sulfate attack of mortar improves substantially with partial replacement of OPC with POA, RHA and FA. The use of a blend of equal weight portions of FA and POA or RHA produced mixes with good strength and resistance to sulfate attack. POA, RHA and FA have a high potential to be used as a pozzolanic material.

  12. Characterization of basic oxygen furnace slag and granite waste mixtures to Portland cement production

    Directory of Open Access Journals (Sweden)

    Luiz Alberto Baptista Pinto Junior

    Full Text Available Abstract The aim of this paper is to analyze mixtures of basic oxygen furnace slag and granite waste in order to produce Portland cement. X-ray patterns were carried out in both the basic oxygen furnace slag and granite waste. Then, mixtures were prepared to obtain the binary basicity of 0.5, 0.9 and 1.2. The mixtures were melted at 1500ºC. Two cooling steps were performed. The first cooling step was accomplished inside the furnace in order to determine the phases formed during the melting step. The second cooling process was carried out in water in order to obtain an amorphous structure. Images via scanning electrons microscopy and EDS spectrum were obtained for the mixtures cooling in water. The results showed that basic oxygen furnace slag contains a higher percent of CaO. A binary basicity of 4.6 was determined. The granite waste appeared as mainly a quartz phase. During the slow cooling step, silicates (akermanite and gehlenite were formed. On the fast cooling step, amorphous structures were obtained. In addition, images obtained via scanning electrons microscopy showed glass structures. EDS spectrum indicated that the glass structures were composed for calcium silicates. Thus, the results suggest that mixtures using basic oxygen furnace slag and granite waste presented characteristics desirable for Portland cement production.

  13. The Greenhouse Gas Emission from Portland Cement Concrete Pavement Construction in China.

    Science.gov (United States)

    Ma, Feng; Sha, Aimin; Yang, Panpan; Huang, Yue

    2016-06-24

    This study proposes an inventory analysis method to evaluate the greenhouse gas (GHG) emissions from Portland cement concrete pavement construction, based on a case project in the west of China. The concrete pavement construction process was divided into three phases, namely raw material production, concrete manufacture and pavement onsite construction. The GHG emissions of the three phases are analyzed by a life cycle inventory method. The CO₂e is used to indicate the GHG emissions. The results show that for 1 km Portland cement concrete pavement construction, the total CO₂e is 8215.31 tons. Based on the evaluation results, the CO₂e of the raw material production phase is 7617.27 tons, accounting for 92.7% of the total GHG emissions; the CO₂e of the concrete manufacture phase is 598,033.10 kg, accounting for 7.2% of the total GHG emissions. Lastly, the CO₂e of the pavement onsite construction phase is 8396.59 kg, accounting for only 0.1% of the total GHG emissions. The main greenhouse gas is CO₂ in each phase, which accounts for more than 98% of total emissions. N₂O and CH₄ emissions are relatively insignificant.

  14. Exposure to cement dust at a Portland cement factory and the risk of cancer.

    Science.gov (United States)

    Vestbo, J; Knudsen, K M; Raffn, E; Korsgaard, B; Rasmussen, F V

    1991-01-01

    The relation between exposure to cement dust and cancer was examined in a population of 546 cement workers and a reference population of 858 randomly sampled men of similar age and area of residence. In 1974 all men gave lifelong occupational and smoking histories; information on incidence of cancer in the period 1974-85 was obtained from the Danish Cancer Registry. No increased risk of overall cancer was found among cement workers. Among men with more than 20 years exposure to cement dust, 14 cases of respiratory cancer were observed (observed/expected (O/E) 1.52, 95% confidence interval (95% CI) 0.90-2.57) when compared with all Danish men. Men with 1-20 years exposure had O/E 1.14 (95% CI 0.59-2.19) based on nine cases of cancer. After excluding all men with documented exposure to asbestos during employment in an asbestos cement factory no increased risk of overall cancer or respiratory cancer was found among cement workers compared with white collar workers from the local reference population, using a Cox regression model controlling for age and smoking habits. Relative risks were 0.5 (95% CI 0.1-1.5) and 1.0 (95% CI 0.4-2.6) for men with 1-20 and more than 20 years of exposure to cement dust respectively compared with white collar workers. PMID:1772795

  15. A realistic molecular model of cement hydrates

    OpenAIRE

    PELLENQ, Roland J.-M.; Kushima, Akihiro; Shahsavari, Rouzbeh; Van Vliet, Krystyn J.; Markus J. Buehler; Yip, Sidney; Ulm, Franz-Josef

    2009-01-01

    Despite decades of studies of calcium-silicate-hydrate (C-S-H), the structurally complex binder phase of concrete, the interplay between chemical composition and density remains essentially unexplored. Together these characteristics of C-S-H define and modulate the physical and mechanical properties of this “liquid stone” gel phase. With the recent determination of the calcium/silicon (C/S = 1.7) ratio and the density of the C-S-H particle (2.6 g/cm3) by neutron scattering measurements, there...

  16. Effect of Nanosilica on the Fresh Properties of Cement-Based Grouting Material in the Portland-Sulphoaluminate Composite System

    Directory of Open Access Journals (Sweden)

    Shengli Li

    2016-01-01

    Full Text Available The effect of NS particle size and content on the fresh properties of the grouting material based on the portland-sulphoaluminate composite system was analyzed. The experimental results indicated that air content increased and apparent density decreased, with increased NS content, but the NS particle sizes have minimal effect on the air content and apparent density. The setting time of mortar was significantly shortened, with increased NS content; however, NS particle sizes had little influence on the setting time. The effect of fluidity on the mortars adding NS with particle size of 30 nm is larger than NS with particle sizes of 15 and 50 nm and the fluidity decreased with increased NS content, but the fluidity of mortars with the particle sizes of 15 and 50 nm is almost not affected by the NS content. XRD analysis shows that the formation of ettringite was promoted and the process of hydration reaction of cement was accelerated with the addition of NS. At the microscopic level, the interfacial transition zone (ITZ of the grouting material became denser and the formation of C-S-H gel was promoted after adding NS.

  17. Analysis of Metal Contents in Portland Type V and MTA-Based Cements

    Directory of Open Access Journals (Sweden)

    Maura Cristiane Gonçales Orçati Dorileo

    2014-01-01

    Full Text Available The aim of this study was to determine, by Atomic Absorption Spectrometry (AAS, the concentration levels of 11 metals in Type V gray and structural white PC, ProRoot MTA, and MTA Bio. Samples, containing one gram of each tested cement, were prepared and transferred to a 100 mL Teflon tube with a mixture of 7.0 mL of nitric acid and 21 mL of hydrochloric acid. After the reaction, the mixture was filtered and then volumed to 50 mL of distilled water. For each metal, specific patterns were determined from universal standards. Arsenic quantification was performed by hydride generator. The analysis was performed five times and the data were statistically analyzed at 5% level of significance. Only the cadmium presented concentration levels of values lower than the quantification limit of the device. The AAS analysis showed increased levels of calcium, nickel, and zinc in structural white PC. Type V PC presented the greatest concentration levels of arsenic, chromium, copper, iron, lead, and manganese (P<0.05. Bismuth was found in all cements, and the lowest concentration levels were observed in Portland cements, while the highest were observed in ProRoot MTA. Both PC and MTA-based cements showed evidence of metals inclusion.

  18. Utilization of municipal solid waste incineration ash in Portland cement clinker

    Energy Technology Data Exchange (ETDEWEB)

    Lam, Charles Hoi King; Barford, John Patrick; McKay, Gordon [Hong Kong University of Science and Technology, Department of Chemical and Biomolecular Engineering, Hong Kong (China)

    2011-08-15

    Municipal solid waste incineration (MSWI) ash is used in part as raw materials for cement clinker production by taking advantage of the high contents of SiO{sub 2}, Al{sub 2}O{sub 3}, and CaO. It is necessary for environmental reasons to establish a material utilization system for the incineration waste ash residue instead of disposing these ashes into landfill. The aim of this paper is to study the feasibility of replacing clinker raw materials by waste ash residue for cement clinker production. MSWI bottom ash and MSWI fly ash are the main types of ashes being evaluated. The ashes were mixed into raw mixture with different portions of ash residue to produce cement clinker in a laboratory furnace at approximately 1400 C. X-ray diffraction and X-ray fluorescence techniques were used to analyze the phase chemistry and chemical composition of clinkers in order to compare these ash-based clinkers with commercial Portland cement clinker. (orig.)

  19. HYDRATION AND PROPERTIES OF BLENDED CEMENT SYSTEMS INCORPORATING INDUSTRIAL WASTES

    Directory of Open Access Journals (Sweden)

    Heikal M.

    2013-06-01

    Full Text Available This paper aims to study the characteristics of ternary blended system, namely granulated blast-furnace slag (WCS, from iron steel company and Homra (GCB from Misr Brick (Helwan, Egypt and silica fume (SF at 30 mass % pozzolanas and 70 mass % OPC. The required water of standard consistency and setting times were measured as well as physico-chemical and mechanical characteristics of the hardened cement pastes were investigated. Some selected cement pastes were tested by TGA, DTA and FT-IR techniques to investigate the variation of hydrated products of blended cements. The pozzolanic activity of SF is higher than GCB and WCS. The higher activity of SF is mainly due to its higher surface area than the other two pozzolanic materials. On the other side, GCB is more pozzolanic than WCS due to GCB containing crystalline silica quartz in addition to an amorphous phase. The silica quartz acts as nucleating agents which accelerate the rate of hydration in addition to its amorphous phase, which can react with liberating Ca(OH2 forming additional hydration products.

  20. The Hydration of Blended Cement at Low W/B Ratio

    Institute of Scientific and Technical Information of China (English)

    HU Shu-guang; LU Lin-nu; HE Yong-jia; LI Yue; DING Qing-jun

    2003-01-01

    The hydration process, hydration product and hydration heat of blended cement paste mixed with mineral admixture and expansive agent at low W/B ratio are studied by XRD , thermo analysis , and calorimetry instrument, and they were compared with those of pure cement paste. The results show that pure cement and blended cement at low W/B ratio have the same types of hydration products, but their respective amounts of hydration products of various blended cements at same ages and the vatiation law of the amount of same hydration products with ages are different; Tim joint effect of tumefaction of gel-ettringite due to water absorption and the expansive pressure on the pore and riff caused by the crystalloid ettringite is the impetus of the volume expansion of cement paste , and the former effect is much greater than the latter one .

  1. Mechanical characterization of Portland cement mortars containing petroleum or coal tar

    Directory of Open Access Journals (Sweden)

    Garcés, P.

    2007-08-01

    Full Text Available This article discusses experimental data on the flexural and compressive strength of Portland cement mortars containing additions or cement replacements consisting in petroleum or coal tar, by-products of the oil and coal industries. The materials studied were two coal (BACA and BACB and two petroleum (BPP and BPT tars. The results show that it is feasible to use such materials as a partial replacement for cement in mortar manufacture. This should lead to the design of a new sustainable product that will contribute to lowering the environmental impact of construction materials while at the same time opening up an avenue for the re-use of this type of industrial by-products.En este artículo se presentan datos experimentales de resistencia a flexión y a compresión de morteros de cemento Portland con adición y sustitución de breas de petróleo y de alquitrán de carbón, que son subproductos de la industria del carbón o del petróleo. Los materiales estudiados son breas de alquitrán de carbón A (BACA y B (BACB, y dos breas de petróleo (BPP y (BPT. Los datos demuestran la viabilidad del uso de estas breas en la fabricación de morteros con menores contenidos de cemento, permitiendo diseñar un nuevo material sostenible con el medio ambiente y que contribuya a reducir el impacto ambiental de los materiales de construcción, hecho que permite abrir una nueva vía de valorización de estos subproductos.

  2. Comparing the Environmental Impacts of Alkali Activated Mortar and Traditional Portland Cement Mortar using Life Cycle Assessment

    Science.gov (United States)

    Matheu, P. S.; Ellis, K.; Varela, B.

    2015-11-01

    Since the year 1908 there has been research into the use alkali activated materials (AAM) in order to develop cementitious materials with similar properties to Ordinary Portland Cement. AAMs are considered green materials since their production and synthesis is not energy intensive. Even though AAMs have a high compressive strength, the average cost of production among other issues limits its feasibility. Previous research by the authors yielded a low cost AAM that uses mine tailings, wollastonite and ground granulated blast furnace slag (GGBFS). This mortar has an average compressive strength of 50MPa after 28 days of curing. In this paper the software SimaPro was used to create a product base cradle to gate Life Cycle Assessment (LCA). This compared the environmental impact of the AAM mortar to an Ordinary Portland Cement mortar (PCHM) with similar compressive strength. The main motivation for this research is the environmental impact of producing Ordinary Portland Cement as compared to alkali activated slag materials. The results of this LCA show that the Alkali Activated Material has a lower environmental impact than traditional Portland cement hydraulic mortar, in 10 out of 12 categories including Global Warming Potential, Ecotoxicity, and Smog. Areas of improvement and possible future work were also discovered with this analysis.

  3. Arsenic Encapsulation Using Portland Cement With Ferrous Sulfate/Lime And Terra-BondTM Technologies - Microcharacterization And Leaching Studies

    Science.gov (United States)

    This work reports the results of an investigation on the treatment and encapsulation of arsenic-containing materials by Portland cement with ferrous sulfate and lime (PFL) and Terra-BondTM, a commercially available patented technology. The arsenic materials treated we...

  4. Microstructure Development and Transport Properties of Portland Cement-fly Ash Binary Systems: in view of service life predictions

    NARCIS (Netherlands)

    Yu, Z.

    2015-01-01

    Fly ash is a by-product of burning coal in electric power generating plants. It is commonly known that owing to its pozzolanic properties fly ash is widely used as a partial replacement for Portland cement in concrete. The use of fly ash in concrete not only reduces the landfill costs of fly ash, bu

  5. Arsenic Encapsulation Using Portland Cement With Ferrous Sulfate/Lime And Terra-BondTM Technologies - Microcharacterization And Leaching Studies

    Science.gov (United States)

    This work reports the results of an investigation on the treatment and encapsulation of arsenic-containing materials by Portland cement with ferrous sulfate and lime (PFL) and Terra-BondTM, a commercially available patented technology. The arsenic materials treated we...

  6. The Early Strength of Slag Cements with Addition of Hydrate Microcrystals

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    The effect of hydrate microcrystals such as calcium silicate hydrates (CSH) and ettringite on the early strength of slag cements was studied.The authors explored the possibility of improving the early strength of the slag cement by applying crystal seed technology.It is shown that slag crystal seeds make the early strength of the cement increased due to the action of hydrate crystal seeds,which speed up the hydration of clinker minerals in the nucleation of ettringite.Therefore,the early strength of the slag cement is obviously improved.

  7. Characterization via nuclear magnetic resonance of Portland cement and related materials

    Science.gov (United States)

    Edwards, Christopher Lane

    The physicochemical and engineering performance properties of several API class G and H ordinary Portland cements (OPCs) from various foreign and domestic sources have been investigated. The engineering performance properties are found to vary from sample to sample, and sources for this variation were sought out and identified. Magic angle spinning (MAS) 29Si nuclear magnetic resonance (NMR) experiments were marked by unusual relaxation behavior due to paramagnetism inherent in OPCs. A model system was created to mimic the paramagnetism of the cements and the system's relaxation behavior was analyzed. The iron in the calcium aluminoferrite (C4AF) provides the paramagnetism sufficient to substantially increase the relaxation rates of the 29Si in the tricalcium silicate (C3S) and dicalcium silicate (C2S) of cement. Several relaxation techniques were evaluated for analyzing cement relaxation, and saturation recovery was identified as the preferred technique. Correlations of data from the saturation recovery experiments with engineering performance properties, especially the strength development of cement pastes, were obtained facilely. An error analysis of the NMR and engineering performance testing techniques was conducted, which indicated that NMR measurements produced less error than the engineering performance tests. A best practice, modified from the saturation recovery experiment, is proposed for use in property correlations. Additionally, 13C MAS NMR was used to characterize various fluorinated single-walled carbon nanotubes (F-SWNTs), which proved surprisingly effective in attenuating 13C-19F dipolar interactions and quantifying the extent of functionalization present at high degrees of reaction. The mixed-metal nanocluster known as FeMoC was also characterized by MAS NMR. The impact of the paramagnetic Fe3+ in the Keplerate cage on the 31P nuclei in the caged Keggin ion of FeMoC was evident in the greatly reduced relaxation times measured.

  8. Degradation of Alumina and Magnesia Chrome refractory bricks in Portland cement kiln – Corrected version*

    Directory of Open Access Journals (Sweden)

    Ben Addi K.

    2014-05-01

    Full Text Available In cement plants, the refractory products are particularly confronted to partially liquid oxide phases at temperature ranging between 900°C and 1700°C. All constituents of these products have to resist not only to thermal constraints, but also to the thermochemical solicitations which result from contact material/coating. In order to study the phenomenon of degradation of refractory bricks in cement kilns and to identify the causes of their degradation, we proceed to the examination of industrial cases in cement kiln. Many chemical tests of the degraded refractory bricks have been done and the results acquired were compared to the ones not used. The analysis of the results is doing using different techniques (Loss of ignition, X-ray Fluorescence, X-ray Diffraction. The results show that the degradation of the used bricks in the clinkering and cooling zone is due to the infiltration of aggressive elements such us sulphur, alkali (Na2O, K2O .... The chemical interaction between the Portland clinker phases and refractory material has also an importance on the stability of the coating and consequently on the life of the refractories.

  9. Monitoring accelerated carbonation on standard Portland cement mortar by nonlinear resonance acoustic test

    Science.gov (United States)

    Eiras, J. N.; Kundu, T.; Popovics, J. S.; Monzó, J.; Borrachero, M. V.; Payá, J.

    2015-03-01

    Carbonation is an important deleterious process for concrete structures. Carbonation begins when carbon dioxide (CO2) present in the atmosphere reacts with portlandite producing calcium carbonate (CaCO3). In severe carbonation conditions, C-S-H gel is decomposed into silica gel (SiO2.nH2O) and CaCO3. As a result, concrete pore water pH decreases (usually below 10) and eventually steel reinforcing bars become unprotected from corrosion agents. Usually, the carbonation of the cementing matrix reduces the porosity, because CaCO3 crystals (calcite and vaterite) occupy more volume than portlandite. In this study, an accelerated carbonation-ageing process is conducted on Portland cement mortar samples with water to cement ratio of 0.5. The evolution of the carbonation process on mortar is monitored at different levels of ageing until the mortar is almost fully carbonated. A nondestructive technique based on nonlinear acoustic resonance is used to monitor the variation of the constitutive properties upon carbonation. At selected levels of ageing, the compressive strength is obtained. From fractured surfaces the depth of carbonation is determined with phenolphthalein solution. An image analysis of the fractured surfaces is used to quantify the depth of carbonation. The results from resonant acoustic tests revealed a progressive increase of stiffness and a decrease of material nonlinearity.

  10. DURABILITY PERFORMANCE OF RFCC SPENT CATALYSTBLENDED PORTLAND CEMENT PASTE EXPOSED TO SEA WATER ATTACK

    Directory of Open Access Journals (Sweden)

    Allahverdi A.

    2013-12-01

    Full Text Available This paper discusses the performance of the paste of Portland cement blended with spent catalyst from Resid Fluidized Catalytic Cracking (RFCC unit of petroleum refining processes in sea water. 28-day cured paste specimens prepared from binary cement mixes containing different amounts of spent catalyst were exposed to Persian Gulf sea water. Compressive strength, weight, and length changes of the specimens were monitored and considered for evaluating the extent of deterioration. Laboratory techniques of X-ray diffractometry, scanning electron microscopy, and Energy dispersive X-ray spectroscopy were also used to study the deteriorated specimens. The results confirm that at relatively high replacement levels, the pozzolanic property of the spent catalyst and the increased open pore volume of such blended cements may result in contradictory consequences. Specimens of relatively higher replacement levels exhibit higher rates of deterioration in spite of their superior mechanical strength behavior caused by pozzolanic reaction. The results obtained by X-ray diffractometry confirm the presence of higher amounts of chlorine-containing Friedel’s salt in specimens containing RFCC spent catalyst compared to plain reference specimens.

  11. Influence of bismuth oxide concentration on the pH level and biocompatibility of white Portland cement

    Directory of Open Access Journals (Sweden)

    Marina Angélica MARCIANO

    2014-07-01

    Full Text Available Objectives: To investigate if there is a relation between the increase of bismuth oxide and the decrease of pH levels and an intensification of toxicity in the Portland cement. Material and Methods: White Portland cement (WPC was mixed with 0, 15, 20, 30 and 50% bismuth oxide, in weight. For the pH level test, polyethylene tubes were filled with the cements and immersed in Milli-Q water for 15, 30 and 60 days. After each period, the increase of the pH level was assessed. For the biocompatibility, two polyethylene tubes filled with the cements were implanted in ninety albino rats (n=6. The analysis of the intensity of the inflammatory infiltrate was performed after 15, 30 and 60 days. The statistical analysis was performed using the Kruskal-Wallis, Dunn and Friedman tests for the pH level and the Kruskal-Wallis and Dunn tests for the biological analysis (p0.05. For the inflammatory infiltrates, no significant statistical differences were found among the groups in each period (p>0.05. The 15% WPC showed a significant decrease of the inflammatory infiltrate from 15 to 30 and 60 days (p<0.05. Conclusions: The addition of bismuth oxide into Portland cement did not affect the pH level and the biological response. The concentration of 15% of bismuth oxide resulted in significant reduction in inflammatory response in comparison with the other concentrations evaluated.

  12. Standard Test Method for Bond Strength of Ceramic Tile to Portland Cement Paste

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2002-01-01

    1.1 This test method covers the determination of the ability of glazed ceramic wall tile, ceramic mosaic tile, quarry tile, and pavers to be bonded to portland cement paste. This test method includes both face-mounted and back-mounted tile. 1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

  13. Effects of High Temperature on the Residual Performance of Portland Cement Concretes

    Directory of Open Access Journals (Sweden)

    Evandro Tolentino

    2002-09-01

    Full Text Available In this work we analyzed the "residual" performance of Portland cement concretes heat-treated at 600 °C after cooling down to room temperature. Concretes with characteristic compressive strength at 28 days of 45 MPa and of 60 MPa were studied. The heat-treatment was carried out without any imposed load. We measured the residual compressive strength and modulus of elasticity. The geometry of the structure was described by mercury intrusion porosimetry and nitrogen sorption tests. We observed a decrease of residual compressive strength and modulus of elasticity, with the raise of heat-treatment temperature, as a result of heat-induced material degradation. The results also indicated that the microstructural damage increased steadily with increasing temperature. Based on the results of this experimental work we concluded that residual mechanical properties of concrete are dependent of their original non heat-treated values.

  14. Effects of Two Redispersible Polymer Powders on Efflorescence of Portland Cement-based Decorative Mortar

    Directory of Open Access Journals (Sweden)

    Huimei ZHU

    2014-09-01

    Full Text Available The effects of redispersible polymer powders of ethylene/Vinyl acetate copolymer (EVA and ethylene/vinyl laurate/vinyl chloride terpolymer (E/VL/VC on the efflorescence of Portland cement-based decorative mortar (PCBDM were studied. The results showed that EVA slightly prolongs the efflorescence duration of fresh PCBDM; and exacerbates efflorescence of hardened PCBDM, because it increases the content of soluble salts such as Ca2+, K+, Na+ ions in hardened PCBDM and promotes their migration. E/VL/VC exacerbates efflorescence of fresh PCBDM due to it easily dissolves in the surface water; but reduces efflorescence of hardened PCBDM, which is attributed to that it decreases the soluble salts content in hardened PCBDM and prohibits salts migration. DOI: http://dx.doi.org/10.5755/j01.ms.20.3.4053

  15. Influence of portland cement replacement in high calcium fly ash geopolymer paste

    Directory of Open Access Journals (Sweden)

    Tanakorn Phoo-ngernkham

    2014-03-01

    Full Text Available This article presents the influence of ordinary Portland cement (OPC replacement in high calcium fly ash (FA geopolymer paste. FA was used to replace OPC at the rate of 5, 10 and 15% by mass of binder. Sodium silicate (Na2SiO3 and 10 molar sodium hydroxide (NaOH solutions were used as the alkaline solution in the reaction. The Na2SiO3/NaOH ratio of 2.0 and the liquid/binder (L/B ratio of 0.60 were used in all mixtures. The results of increase OPC replacement, the setting time and compressive strain capacity decreased while the compressive strength and modulus of elasticity increased. The compressive strength and modulus of elasticity at 28 days of geopolymer pastes with 15% OPC replacement were 36.7 MPa and 13,300 MPa, respectively.

  16. Application of the fluorescence light microscopy in the textural study of portland cement clinker

    Directory of Open Access Journals (Sweden)

    Montoto San Miguel, Modesto

    1987-03-01

    Full Text Available The application of fluorescence light microscopy in the textural study of Portland cement clinker, specially its porosity, is presented. Principles and types of the technique are commented and the suggested sample preparation method is described. The use of fluorescence microscopy allows an easier study of the clinker porosity, and very proper images for automated quantification can be obtained. Besides, the samples can also be observed by reflected-light polarizing microscopy.

    Se presenta la utilidad de la microscopía óptica de fluorescencia para el estudio textural del clínker de cemento Portland, especialmente su porosidad. Se comentan los fundamentos y modalidades de la técnica, y se describe el método recomendado de preparación de muestras. La utilización de la microscopía de fluorescencia permite un estudio más fácil de la porosidad, obteniéndose imágenes muy apropiadas para su cuantificación mediante técnicas automatizadas. Además, las muestras para fluorescencia pueden ser estudiadas complementariamente por microscopía óptica de polarización por luz reflejada.

  17. Effect of Superplasticizers on the Early Age Hydration of Sulfoaluminate Cement

    Institute of Scientific and Technical Information of China (English)

    YUAN Xiaohui; CHEN Wei; YANG Mo

    2014-01-01

    The effects of two types of superplasticizers on the properties of CSA cement pastes during early hydration were studied. The influences of two types of superplasticizers on the properties of cement pastes, including the normal consistency, setting time, fluidity, and compressive strength, were investigated by using various methods. The hydration products of the cement pastes cured for 1 day and 3 days were studied by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results show that the PCE type superplasticizer retards the early age hydration while the FDN type superplasticizer accelerates the early age hydration of the CSA cement. Both types of superplasticizers have no influence on the further hydration of CSA cement, confirmed by the calorimeter tests as well. The ultrasonic pulse velocity measurements were used to probe the influence of two types of superplasticizers on the hydration of CSA cement pastes at a high water-cement ratio (0.45). The results show that the PCE type superplasticizer retards the early age hydration of the CSA cement while the FDN type superplasticizer has little influence on the early age hydration of the CSA cement.

  18. Regenerative Portland cement sorbents for fluidized-bed combustion of coal

    Energy Technology Data Exchange (ETDEWEB)

    Albanese, A S; Sethi, D; Steinberg, M

    1980-01-01

    Portland cements are commercially available construction materials that contain high concentrations of calcium silicates. The silicates are highly reactive towards SO/sub 2/ at temperatures and pressures encountered in atmospheric and pressurized FBC's. Of the Portland cements tested, PC III appears to have the highest sulfation capacity when sulfated by SO/sub 2/ at FBC conditions. A thermodynamic analysis of the sulfation of calcium silicates indicates that they are capable of reducing the concentration of SO/sub 2/ in FBC combustion gases to within the current EPA emission limits. The optimum temperature for sulfation of 16/20 mesh PC III pellets is about 1000/sup 0/C in comparison to about 875/sup 0/ for natural limestones. The higher observed optimum temperature is an advantage because combustion and power cycle efficiencies tend to increase as bed temperature increases. The reactions for regenerating sulfated calcium silicates are similar to those for regenerating calcium sulfate. However, the equilibrium partial pressures of SO/sub 2/ in the reductive decomposition of sulfated silicates are much higher than for sulfate lime. This implies that higher SO/sub 2/ concentrations will be attainable in the regenerator off-gas which will result in more economical conversion of SO/sub 2/ to sulfur or sulfuric acid. The sulfation capacity and regeneration efficiency of PC III pellets do not deteriorate with repeated sulfation/regeneration cycling. This indicates that PC III pellets are suitable for use in regenerative systems. The sulfation capacity of PC III is independent of pressure up to at least 10 atm.

  19. Assessment of ferrous chloride and Portland cement for the remediation of chromite ore processing residue.

    Science.gov (United States)

    Jagupilla, Santhi C; Wazne, Mahmoud; Moon, Deok Hyun

    2015-10-01

    Chromite Ore Processing Residue (COPR) is an industrial waste containing up to 7% chromium (Cr) including up to 5% hexavalent chromium [Cr(VI)]. The remediation of COPR has been challenging due to the slow release of Cr(VI) from a clinker like material and thereby the incomplete detoxification of Cr(VI) by chemical reagents. The use of sulfur based reagents such as ferrous sulfate and calcium polysulfide to detoxify Cr(VI) has exasperated the swell potential of COPR upon treatment. This study investigated the use of ferrous chloride alone and in combination with Portland cement to address the detoxification of Cr(VI) in COPR and the potential swell of COPR. Chromium regulatory tests, X-ray powder diffraction (XRPD) analyses and X-ray absorption near edge structure (XANES) analyses were used to assess the treatment results. The treatment results indicated that Cr(VI) concentrations for the acid pretreated micronized COPR as measured by XANES analyses were below the New Jersey Department of Environmental Protection (NJDEP) standard of 20 mg kg(-1). The Toxicity characteristic leaching procedure (TCLP) Cr concentrations for all acid pretreated samples also were reduced below the TCLP regulatory limit of 5 mg L(-1). Moreover, the TCLP Cr concentration for the acid pretreated COPR with particle size ⩽0.010 mm were less than the universal treatment standard (UTS) of 0.6 mg L(-1). The treatment appears to have destabilized all COPR potential swell causing minerals. The unconfined compressive strength (UCS) for the treated samples increased significantly upon treatment with Portland cement. Copyright © 2015 Elsevier Ltd. All rights reserved.

  20. Effect of High Doses of Chemical Admixtures on the Freeze-Thaw Durability of Portland Cement Concrete

    Science.gov (United States)

    2002-02-01

    volume (Neville 1988). The hydrated cement is often referred to as cement gel, which has a characteristic porosity of about 28% ( Mindess and Young...Structure, Properties, and Materials. New York: Prentice-Hall. Mindess , S., and J.F. Young (1981) Concrete. New York: Prentice-Hall. Neville, A.M

  1. Marine durability of 15 year old concrete specimens made with ordinary portland, slag, and fly ash cements

    Energy Technology Data Exchange (ETDEWEB)

    Mohammed, T.U.; Yamaji, T.; Hamada, H. [Port and Harbor Research Inst., Ministry of Land, Infrastructure and Transport (Japan); Aoyama, T. [PS Corp. (Japan)

    2001-07-01

    A study was conducted in which the marine durability of ordinary portland cement, slag and fly ash cement was examined using 15 year old plain and reinforced concrete cylindrical specimens. In addition, the performance of these cements was also examined in another study for pre-cracked reinforced concrete prism samples. The process of manufacturing cement emits huge amounts of carbon dioxide into the global atmosphere. Replacing a portion of the cement with by-products from the steel industry and thermal power plants (which are both huge emitters of carbon dioxide) can lower carbon dioxide emissions and also solve the disposal issue of slag and fly ash while increasing the long-term durability of concrete structures. In this study, concrete cylindrical specimens were made of ordinary portland cement, slag and fly ash cements. Water-to-cement ratios were 0.45 and 0.55 and the compressive strength of the concrete, corrosion of the steel bars, and chloride-ion concentrations in the concrete were evaluated. It was shown that, with the exception of fly ash cements, the compressive strength of most cements increased after 15 years of exposure compared to its 28 day strength. Type C slag cement demonstrated the best performance against chloride-ion at the surface of concrete made with slag and fly ash. Voids in the steel-concrete interface make it possible for corrosion pits to develop. The use of seawater as mixing water results in earlier strength development at 28 days and does not cause to the strength of the concrete to regress after 15-years of exposure, but it causes more corrosion of steel bars at a lower cover depth. Corrosion of steel bars is not an issue at deeper cover depths. 15 refs., 18 tabs., 8 figs.

  2. The effect of portland cement for solidification of soils contaminated by mine tailings containing heavy metals

    Science.gov (United States)

    Jian-Jun, Chen; Zheng-Miao, Xie

    2010-05-01

    Portland cement(PC) was used to solidify the lead-zinc mine tailings contaminated soils(CS) in this work. The soils were heavily polluted by heavy metals with lead(up to 19592 mg/kg), zinc(up to 647mg/kg), Cd(up to 14.65mg.kg) and Cu(up to 287mg/kg). Solidified/stabilized(s/s)forms with a range of cement contents, 40-90 wt%, were evaluated to determine the optimal binder content. Unconfined compression strength test(UCS), Chinese solid waste-extraction procedure for leaching toxicity - Horizontal vibration method, toxicity characteristic leaching procedures(TCLP) were used for physical and chemical characterization of the s/s forms. The procedure of Tessier et al.(1979) was used to separate S/S forms Pb, Zn, Cd, Cu into different fractions. The results show that addition of 50% cement was enough for the s/s forms to satisfy the MU10 requirements (0.10 MPa). Under the 50% addition, the content of the water-exchangeable fraction of Pb reduced from 2.25% to 0.2%, the carbonate-bound fraction and organic-bound fraction reduced by about half, while the Fe-Mn oxide-bound fraction was more than doubled. The residual fraction decreased 8% on the contrary. For Zn, except for the carbonate-bound fraction increased slightly, the features of other items were same as that of Pb. For Cd, the water-exchangeable fraction was reduced largely, the residual fraction and Fe-Mn oxide-bound fraction increased 2-3%. For Cu, A distinct feature is the organic-bound fraction reduced with the reduction in consumption of cement, at the same time, the residual fraction increased corresponding. Leaching test results indicate that the leaching contents of Pb2+ of the six specimens are quite different at low pH value(

  3. Production and hydration of calcium sulfoaluminate-belite cements derived from aluminium anodising sludge

    OpenAIRE

    da Costa, E.B.; Rodríguez, E.D.; Bernal, S.; Provis, J. L.; Gobbo, L.A.; Kirchheim, A.P.

    2016-01-01

    Calcium sulfoaluminate-belite cement (CSAB) offers lower CO2 emissions in its production, compared with Portland cement. However, for the production of CSAB a high amount of alumina is required, and the scarcity and high cost of high-purity bauxite make these cements costly at present. In this study, the use of uncalcined aluminium anodising sludge (AAS) as the main source of alumina to produce CSAB clinkers, replacing bauxite, was assessed. The CSAB clinkers produced were mainly composed of ...

  4. Propriedades mecânicas de materiais compósitos à base de cimento Portland e resina epoxi Mechanical properties of composite materials based on portland cement and epoxy resin

    Directory of Open Access Journals (Sweden)

    T. H. Panzera

    2010-03-01

    Full Text Available O estudo de materiais de alto desempenho e multifuncionais, como os compósitos poliméricos cimentícios, tem sido o foco de inúmeras pesquisas na indústria da construção civil. Este trabalho investiga o efeito da combinação de uma fase polimérica termorrígida, uma resina epóxi, com cimento Portland branco estrutural, seguido da avaliação da resistência à compressão e módulo de elasticidade. Este compósito, quando comparado individualmente com as suas matérias-prima originais, promove um aumento da resistência mecânica à compressão, redução da massa específica e, também uma mudança significativa do comportamento mecânico. As mudanças nas propriedades mecânicas estão associadas à hidratação da fase cimentícia na presença da resina, fato comprovado através da análise espectroscópica na região do infravermelho.The study of multi-functional materials of high performance, as the polymeric-cementitious composites, has been the focus of several researches in the industry of the civil engineering. This work investigates the effect of the combination of a thermorigid epoxy phase and the white Portland cement, followed by the evaluation of its compressive strength and modulus of elasticity. This composite, when the phases are individually compared, provides an increase of the compressive strength, a reduction of the density, and a significant change of the mechanical behaviour. The changes in mechanical behaviour are associated with the hydration of cement in the presence of resin, which was evident after infrared spectroscopy analysis.

  5. A mild alkali treated jute fibre controlling the hydration behaviour of greener cement paste

    Science.gov (United States)

    Jo, Byung-Wan; Chakraborty, Sumit

    2015-01-01

    To reduce the antagonistic effect of jute fibre on the setting and hydration of jute reinforced cement, modified jute fibre reinforcement would be a unique approach. The present investigation deals with the effectiveness of mild alkali treated (0.5%) jute fibre on the setting and hydration behaviour of cement. Setting time measurement, hydration test and analytical characterizations of the hardened samples (viz., FTIR, XRD, DSC, TGA, and free lime estimation) were used to evaluate the effect of alkali treated jute fibre. From the hydration test, the time (t) required to reach maximum temperature for the hydration of control cement sample is estimated to be 860 min, whilst the time (t) is measured to be 1040 min for the hydration of a raw jute reinforced cement sample. However, the time (t) is estimated to be 1020 min for the hydration of an alkali treated jute reinforced cement sample. Additionally, from the analytical characterizations, it is determined that fibre-cement compatibility is increased and hydration delaying effect is minimized by using alkali treated jute fibre as fibre reinforcement. Based on the analyses, a model has been proposed to explain the setting and hydration behaviour of alkali treated jute fibre reinforced cement composite.

  6. Crystallographic characterization of cement pastes hydrated with NaCl; Caracterizacao cristalografica de pastas de cimento hidratadas com NaCl

    Energy Technology Data Exchange (ETDEWEB)

    Melo, Carina Gabriela de Melo e; Martinelli, Antonio Eduardo; Melo, Dulce Maria Araujo; Melo, Marcus Antonio de Freitas; Melo, Vitor Rodrigo de Melo e [Universidade Federal do Rio Grande do Norte (UFRN), Natal, RN (Brazil)

    2012-07-01

    One of the major current challenges faced by oil companies is the exploration of pre salt basins. Salt layers deposited upon the evaporation of ocean water and continental separation are mainly formed by NaCl and isolate immense oil reservoirs. The mechanical stability and zonal isolation of oil wells that run through salt layers must be fulfilled by cement sheaths saturated with NaCl to assure chemical compatibility between cement and salt layer. The present study aimed at evaluating the effect of NaCl addition on the hydration of oil well cement slurries as well as identifying the nature of crystalline phases present in the hardened cement. To that end, cement slurries containing NaCl were mixed, hardened and characterized by X-ray diffraction. The results revealed that the presence of NaCl affects the formation of hydration products by the presence of Friedel's salt. The intensity of the corresponding peaks increase as the contents of NaCl in the slurry increase. High concentrations of NaCl in Portland slurries increase the setting time of cement and the presence of Friedel's salt decreases the strength of the hardened cement. (author)

  7. Properties of steel foundry electric arc furnace dust solidified/stabilized with Portland cement.

    Science.gov (United States)

    Salihoglu, Guray; Pinarli, Vedat; Salihoglu, Nezih Kamil; Karaca, Gizem

    2007-10-01

    Electric arc furnace dust from steel production is generated in considerable amounts worldwide and needs to be treated as hazardous waste. The aim of this study was to investigate the properties of electric arc furnace dust solidified/stabilized by using Portland cement. Mortar and paste samples were prepared with varying waste-to-binder ratios between 0% and 90%. A comprehensive experimental program was designed including XRF characterization, setting time, unconfined compressive strength, and toxicity characteristics leaching procedure (TCLP), synthetic precipitation leaching procedure (SPLP), and acid neutralization capacity (ANC) tests. The results were evaluated in order to determine if the solidified /stabilized product can be disposed of at a landfill site with domestic waste or at a segregated landfill. The effect of using sand on S/S performance was also investigated. The results indicated that the solidification /stabilization process using PC helps the heavy metals to be bound in the cement matrix, but the TCLP leaching results exceeded the EPA landfilling limits. The SPLP leaching results conformed to the limits implying that the waste or S/S products can be disposed of at a segregated landfill; however the low ANC of the S/S products reveals that there may be leaching in the long-term. The sand used in the mortar samples adversely affected the S/S performance, causing higher heavy metal leaching levels, and lower pH levels in the leachate after the TCLP extraction than those measured in the leachate of the paste samples.

  8. Freezing resistance of high iron phoasphoaluminate cement

    Science.gov (United States)

    Zhang, S. X.; Lu, L. C.; Wang, S. D.; Zhao, P. Q.; Gong, C. C.

    2017-03-01

    The influence of freeze-thaw cycle on the mechanical properties of high iron phoasphoaluminate cement was investigated in the present study. The visual examination was conducted to evaluate the surface damage. The deterioration considering the weight loss, modulus loss of relative dynamic elastic and strength loss of mortar were also investigated. The morphology of hydration products were analysed by SEM. Compared with ordinary Portland cement and sulphoaluminate cement, the frost resistance of high iron phosphoraluminate cement is better. Hydration products of high iron phoasphoaluminate cement contain sheet crystals, and a lot of gel form a dense three-dimensional network structure, which results in a lower porosity. Different from ordinary Portland cement, the hydration product of high iron phoasphoaluminate cement does not contain Ca(OH)2, and low alkalinity reduces its osmotic pressure. The lower porosity and osmotic pressure are the two main reasons which causes in the higher frost resistance of high iron phoasphoaluminate cement.

  9. Evolution and quantification of the main Sensitisers in commercial portland cements

    Directory of Open Access Journals (Sweden)

    Frías, M.

    2002-03-01

    Full Text Available The commercial Portland cements contain minor elements in their chemical compositions. The presence of these elements has a direct incidence in different aspects: rheological behaviour, reaction kinetics, environmental, etc. Some of them also have a negative effect on the human health; so, chromium (Cr, nickel (Ni and cobalt (Co are the main allergens present in Portland cements, causing of Professional Dermatitis in construction workers. The current study is focussed on the quantification of total and soluble chromium, nickel and cobalt in a wide range of Spanish commercial cements. These values can represent a contribution to the establishing of possible limitations or reductions of these elements in forthcoming standards. Analytical data show that clinkers are the main responsibles of the presence of soluble chromium in commercial cements. This fact could be indicating that chromium solubility (from inert Cr III to soluble Cr VI would be closely related to the clinkerisation conditions. On the other hand, there is not a direct ratio between total chromium and soluble chromium; it means that analytical results are punctual and not any case can be extrapolating ones. Ni and Co solubility in water is practically negligible either raw as clinkers.

    Los cementos Portland comerciales contienen elementos minoritarios en su composición química. La presencia de estos elementos tiene una incidencia directa en diferentes aspectos: comportamiento reológico, cinética de reacción, contaminación ambiental, etc. Algunos de ellos, aparte de su incidencia mencionada anteriormente, tienen un efecto negativo en la salud humana. Así, el cromo (Cr, níquel (Ni y cobalto (Co son los principales alérgenos contenidos en los cementos y, por lo tanto, los principales causantes de la Dermatitis Profesional. Este trabajo se centra en la cuantifîcación de los contenidos totales y solubles de cromo, níquel y cobalto presentes en los cementos comerciales

  10. Hydration studies of calcium sulfoaluminate cements blended with fly ash

    Energy Technology Data Exchange (ETDEWEB)

    García-Maté, M.; De la Torre, A.G. [Departamento de Química Inorgánica, Cristalografía y Mineralogía, Universidad de Málaga, 29071 Málaga (Spain); León-Reina, L. [Servicios Centrales de Apoyo a la Investigación, Universidad de Málaga, 29071 Málaga (Spain); Aranda, M.A.G. [Departamento de Química Inorgánica, Cristalografía y Mineralogía, Universidad de Málaga, 29071 Málaga (Spain); CELLS-Alba synchrotron, Carretera BP 1413, Km. 3.3, E-08290 Cerdanyola, Barcelona (Spain); Santacruz, I., E-mail: isantacruz@uma.es [Departamento de Química Inorgánica, Cristalografía y Mineralogía, Universidad de Málaga, 29071 Málaga (Spain)

    2013-12-15

    The main objective of this work is to study the hydration and properties of calcium sulfoaluminate cement pastes blended with fly ash (FA) and the corresponding mortars at different hydration ages. Laboratory X-ray powder diffraction, rheological studies, thermal analysis, porosimetry and compressive strength measurements were performed. The analysis of the diffraction data by Rietveld method allowed quantifying crystalline phases and overall amorphous contents. The studied parameters were: i) FA content, 0, 15 and 30 wt.%; and ii) water addition, water-to-CSA mass ratio (w/CSA = 0.50 and 0.65), and water-to-binder mass ratio (w/b = 0.50). Finally, compressive strengths after 6 months of 0 and 15 wt.% FA [w/CSA = 0.50] mortars were similar: 73 ± 2 and 72 ± 3 MPa, respectively. This is justified by the filler effect of the FA as no strong evidences of reactivity of FA with CSA were observed. These results support the partial substitution of CSA cements with FA with the economic and environmental benefits.

  11. Mineralogy and microstructure of two Mexican Portland cements for the confinement of radioactive waste; Mineralogia y microestructura de dos cementos mexicanos Portland para el confinamiento de desechos radiactivos

    Energy Technology Data Exchange (ETDEWEB)

    Galicia A, E. [Universidad Autonoma del Estado de Mexico, Facultad de Ciencias, Campus El Cerrillo, Piedras Blancas, Carretera Toluca-Ixtlahuaca Km. 15.5, Estado de Mexico (Mexico); Badillo A, V. E.; Ramirez S, J. R. [ININ, Carretera Mexico-Toluca s/n, 52750 Ocoyoacac, Estado de Mexico (Mexico); Nava E, N., E-mail: nasiega_181@hotmail.com [Instituto Mexicano del Petroleo, Eje Central Lazaro Cardenas No. 152, Col. San Bartolo Atepehuacan, 07730 Mexico D. F. (Mexico)

    2014-10-15

    The cementitious materials are involved in the different stages of radioactive waste management because they are used for the waste immobilization in the container, as well as filling in the spaces between containers vaults and also as engineering barrier and construction material in civil construction site. Therefore, is necessary to have a study of commercial cement available nationwide involving solid timely analysis in order to identify which phases are responsible for confinement of radionuclides, if considered the most reactive phase -CSH- or called secondary phases. In this research the hydration products of cement are presented as well as its importance in the nuclear industry. The analysis and observation of the cement clinker and the hydration products on the manufactured pulps with two commercial cements resistant to sulphates was realized using the observation technique of solid X-ray diffraction and nuclear analytic techniques of Moessbauer spectroscopy and X-Ray Fluorescence. The results show the presence of calcium silicate hydrates in the amorphous phase and the presence of ettringite crystals and portlandite sheets is appreciated. The abundant iron phase called tetra calcium ferro aluminate has been identified by Moessbauer spectroscopy. (Author)

  12. Evaluating portland cement concrete degradation by sulphate exposure through artificial neural networks modeling

    Energy Technology Data Exchange (ETDEWEB)

    Oliveira, Douglas Nunes de; Bourguignon, Lucas Gabriel Garcia; Tolentino, Evandro, E-mail: tolentino@timoteo.cefetmg.br [Centro Federal de Educacao Tecnologica de Minas Gerais (CEFET-MG), Timoteo, MG (Brazil); Costa, Rodrigo Moyses, E-mail: rodrigo@moyses.com.br [Universidade de Itauna, Itauna, MG (Brazil); Tello, Cledola Cassia Oliveira de, E-mail: tellocc@cdtn.br [Centro de Desenvolvimento da Tecnologia Nucelar (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil)

    2015-07-01

    A concrete is durable if it has accomplished the desired service life in the environment in which it is exposed. The durability of concrete materials can be limited as a result of adverse performance of its cement-paste matrix or aggregate constituents under either chemical or physical attack. Among other aggressive chemical exposures, the sulphate attack is an important concern. Water, soils and gases, which contain sulphate, represent a potential threat to the durability of concrete structures. Sulphate attack in concrete leads to the conversion of the hydration products of cement to ettringite, gypsum, and other phases, and also it leads to the destabilization of the primary strength generating calcium silicate hydrate (C-S-H) gel. The formation of ettringite and gypsum is common in cementitious systems exposed to most types of sulphate solutions. The present work presents the application of the neural networks for estimating deterioration of various concrete mixtures due to exposure to sulphate solutions. A neural networks model was constructed, trained and tested using the available database. In general, artificial neural networks could be successfully used in function approximation problems in order to approach the data generation function. Once data generation function is known, artificial neural network structure is tested using data not presented to the network during training. This paper is intent to provide the technical requirements related to the production of a durable concrete to be used in the structures of the Brazilian near-surface repository of radioactive wastes. (author)

  13. Prediction of chloride ingress and binding in cement paste

    DEFF Research Database (Denmark)

    Geiker, Mette Rica; Nielsen, Erik Pram; Herforth, Duncan

    2007-01-01

    This paper summarizes recent work on an analytical model for predicting the ingress rate of chlorides in cement-based materials. An integral part of this is a thermodynamic model for predicting the phase equilibria in hydrated Portland cement. The model’s ability to predict chloride binding...... in Portland cement pastes at any content of chloride, alkalis, sulfates and carbonate was verified experimentally and found to be equally valid when applied to other data in the literature. The thermodynamic model for predicting the phase equilibria in hydrated Portland cement was introduced into an existing...... Finite Difference Model for the ingress of chlorides into concrete which takes into account its multi-component nature. The “composite theory” was then used to predict the diffusivity of each ion based on the phase assemblage present in the hydrated Portland cement paste. Agreement was found between...

  14. The crucial effect of early-stage gelation on the mechanical properties of cement hydrates

    Science.gov (United States)

    Ioannidou, Katerina; Kanduč, Matej; Li, Lunna; Frenkel, Daan; Dobnikar, Jure; Del Gado, Emanuela

    2016-07-01

    Gelation and densification of calcium-silicate-hydrate take place during cement hydration. Both processes are crucial for the development of cement strength, and for the long-term evolution of concrete structures. However, the physicochemical environment evolves during cement formation, making it difficult to disentangle what factors are crucial for the mechanical properties. Here we use Monte Carlo and Molecular Dynamics simulations to study a coarse-grained model of cement formation, and investigate the equilibrium and arrested states. We can correlate the various structures with the time evolution of the interactions between the nano-hydrates during the preparation of cement. The novel emerging picture is that the changes of the physicochemical environment, which dictate the evolution of the effective interactions, specifically favour the early gel formation and its continuous densification. Our observations help us understand how cement attains its unique strength and may help in the rational design of the properties of cement and related materials.

  15. Effectiveness of shrinkage-reducing admixtures on Portland pozzolan cement concrete

    Directory of Open Access Journals (Sweden)

    Videla, C.

    2005-06-01

    Full Text Available Drying shrinkage causes tensile stress in restrained concrete members. Since all structural elements are subject to some degree of restraint, drying shrinkage is regarded to be one of the main causes of concrete cracking. The purpose of the present study was to evaluate the effectiveness of SRA in reducing drying shrinkage strain in Portland pozzolan cement concrete. The major variables examined included slump, admixture type and dose, and specimen size. The measured results indicate that any of the admixtures used in the study significantly reduced shrinkage. Concrete manufactured with shrinkage reducing admixtures shrank an average of 43% less than concrete without admixtures. As a rule, the higher the dose of admixture, the higher was its shrinkage reduction performance. The experimental results were compared to the shrinkage strain estimated with the ACI 209, CEB MC 90, B3, GL 2000, Sakata 1993 and Sakata 2001 models. Although none of these models was observed to accurately describe the behaviour of Portland pozzolan cement concrete with shrinkage reducing admixtures, the Sakata 2001 model, with a weighted coefficient of variation of under 30%, may be regarded to be roughly adequate.

    La retracción por secado es un fenómeno intrínseco del hormigón que produce tensiones de tracción en elementos restringidos de hormigón. Puesto que todos los elementos presentan algún grado de retracción, se considera a la retracción por secado como una de las principales causas de agrietamiento en proyectos de construcción en hormigón. Por lo tanto, el objetivo de esta investigación fue evaluar la efectividad de los aditivos reductores de retracción (SRA en hormigones fabricados con cemento Portland puzolánico. Las variables principales estudiadas incluyen el asentamiento de cono de Abrams, marca y dosis de aditivo reductor de retracción, y tamaño de espécimen de hormigón. Los resultados obtenidos permiten concluir que el uso de

  16. Physical and mechanical characterization of Portland cement mortars made with expanded polystyrene particles addition (EPS

    Directory of Open Access Journals (Sweden)

    Ferrándiz-Mas, V.

    2012-12-01

    Full Text Available On this work the influence of the addition of different types (commercial and recycled and contents of expanded polystyrene on the physical and mechanical properties of Portland cement mortars has been studied. Variables studied are: workability, air content, bulk density, mechanical strength, porosity, water absorption and sound absorption. Mixtures have been also characterized by scanning electron microscopy. Air-entraining agents, water retainer and superplasticizer additives have been used in order to improve the workability of mortars. The results show that the workability and mechanical strength decreases with increasing content of expanded polystyrene. Additives improve the workability and porosity, allowing manufacture mortars with high levels of recycled material that show mechanical properties suitable for use as masonry mortars, stucco and plaster.

    El objetivo de este estudio es evaluar la influencia de la adición de distintos tipos y dosificaciones de poliestireno expandido, tanto comerciales como procedentes de reciclado, sobre las características físicas y mecánicas de morteros de cemento portland. Las variables estudiadas fueron: consistencia, aire ocluido, densidad aparente, resistencias mecánicas, porosidad, absorción de agua y absorción acústica. Los morteros también se han caracterizado por microscopia electrónica de barrido. Con objeto de mejorar la trabajabilidad de los morteros se ha empleado aditivos aireante, retenedor de agua y fluidificante. Los resultados muestran que al aumentar la cantidad de poliestireno expandido la trabajabilidad y las resistencias mecánicas disminuyen. El empleo de aditivos mejora la trabajabilidad y la porosidad, permitiendo fabricar morteros con altos contenidos de residuo, con propiedades mecánicas adecuadas para su empleo como morteros de albañilería, revoco y enlucido.

  17. Root perforations treatment using mineral trioxide aggregate and Portland cements Cimentos de agregado trióxido mineral e Portland no tratamento de perfurações radiculares

    Directory of Open Access Journals (Sweden)

    José Dias da Silva Neto

    2010-12-01

    Full Text Available PURPOSE: Clinical, radiological and histological evaluation of root perforations treated with mineral trioxide aggregate (MTA or Portland cements, and calcium sulfate barrier. METHODS: One molar and 11 premolar teeth of a male mongrel dog received endodontic treatment and furcations were perforated with a high-speed round bur and treated with a calcium sulfate barrier. MTA, Portland cement type II (PCII and type V (PCV, and white Portland cement (WPC were used as obturation materials. The teeth were restored with composite resin and periapical radiographs were taken. The animal was euthanized 120 days post-surgery for treatment evaluation. RESULTS: Right lower first premolar (MTA, right lower third premolar (PCV, left lower second premolar (MTA, and right lower second premolar (WPC: clinically normal, slightly radio-transparent area on the furcation, little inflammatory infiltrate, and new-bone formation. Left lower third premolar (PCII, right upper first premolar (WPC, right upper third premolar (PCII, and left upper first molar (PCV: clinically normal, radiopaque area on the furcation, and new-bone formation. Right upper second premolar (MTA, left upper second premolar (WPC, left upper third premolar (PCII: presence of furcation lesion, large radiolucent area, and intense inflammatory infiltrate. CONCLUSION: All obturation materials used in this study induced new-bone formation.OBJETIVO: Avaliar clínica, radiológica e histologicamente perfurações radiculares tratadas com MTA e cimentos Portland, com barreira de sulfato de cálcio. MÉTODOS: A amostra foi constituída por 11 dentes pré-molares e um molar de cão macho, sem raça definida. Após tratamento endodôntico realizaram-se perfurações nas furcas com broca esférica de alta rotação e barreira de sulfato de cálcio. Foram utiliados os cimentos MTA, Portland tipo II (CPII, Portland tipo V (CPV e Portland branco estrutural (CPB. Os dentes foram restaurados com resina composta e

  18. Microstructure and mechanical properties of microwave-assisted heating of pozzolan-Portland cement paste at a very early stage

    OpenAIRE

    Natt Makul; Dinesh Kumar Agrawa

    2013-01-01

    Portland-pozzolan cement pastes at a very early stage subjecting to microwave heating were investigated. Microwave with a 2.45 GHz and multimode cavity was used for the experiments. The pastes containing pozzolan materials (pulverized fuel ash, metakaolin and silica fume) were proportioned with a 0.38 water/solid mass ratio and a 20% by weight replacement of total solid content. It was observed that the temperature increased continuously during microwave heating. Some ettringite rods and a...

  19. In vitro sealing ability of white and gray mineral trioxide aggregate (MTA and white Portland cement used as apical plugs

    Directory of Open Access Journals (Sweden)

    Patrícia Zanatta Aranha Coneglian

    2007-06-01

    Full Text Available This study evaluated the sealing ability of apical plugs made of white and gray MTA-Angelus® and white Portland cement placed via the root canal and having different thicknesses (2, 5 and 7 mm. Ninety extracted human single-rooted teeth were instrumented using a size 40 K-file to standardize the foraminal opening by the stepback technique. The teeth were assigned to 3 groups (n=30, according to the material used for fabrication of the apical plugs: A = gray MTA; B = white MTA; C = white Portland cement. The groups were subdivided into groups of 10 teeth each according to the apical plug thickness (2, 5 and 7 mm. Marginal apical dye leakage was assessed using 0.2% Rhodamine B solution in which the specimens were immersed for 72 hours at 37ºC. The roots were sectioned longitudinally in a buccolingual direction for apical plug exposure, and digital photographs were taken and analyzed by Image Tool image-analysis software. Data were analyzed statistically by Kruskal-Wallis and Dunn's tests. Significance level was set at 5%. The least percent leakage was observed for 5- and 7-mm-thick plugs (p0.05 was found between gray MTA and white Portland cement. Among the three materials analyzed, white MTA presented the highest marginal leakage (p<0.05. The findings of the present study showed that gray MTA and Portland cement had better sealing ability than white MTA when used as apical plugs. Dye leakage was smaller for 5- and 7-mm-thick plugs compared to 2-mm-thick plugs.

  20. Use of Variamine Blue dye in Spectrophotometric determination of Water Soluble Cr(VI in Portland Cement

    Directory of Open Access Journals (Sweden)

    Devesh K. Sharma

    2015-12-01

    Full Text Available Variamine blue dye as chromogenic reagent was used for Portland cement samples in determination of soluble hexavalent chromium. This method was based on the reaction of Cr(VI with potassium iodide in acidic medium to liberate iodine, which oxidized variamine blue to form a violet colored species having an absorption maximum 556 nm. The extraction of soluble Cr(VI for quantification in cement was done according to European method. The validity of this method was thoroughly examined by comparing with standard DPC method as well as the accuracy of the method was checked using a standard reference material of National Institute of Standards & Technology (NIST, USA.

  1. Influence of ultra-fine fly ash on hydration shrinkage of cement paste

    Institute of Scientific and Technical Information of China (English)

    GAO Ying-li; ZHOU Shi-qiong

    2005-01-01

    Hydration shrinkage generated by cement hydration is the cause of autogenous shrinkage of high strength concrete. It may result in the volume change and even cracking of mortar and concrete. According to the data analysis in a series of experimental studies, the influence of ultra-fine fly ash on the hydration shrinkage of composite cementitious materials was investigated. It is found that ultra-fine fly ash can reduce the hydration shrinkage of cement paste effectively, and the more the ultra-fine fly ash, the less the hydration shrinkage. Compared with cement paste without the ultra-fine fly ash, the shrinkage ratio of cement paste reduces from 23.4% to 39.7% when the ultra-fine fly ash replaces cement from 20% to 50%. Moreover, the microscopic mechanism of the ultra-fine fly ash restraining the hydration shrinkage was also studied by scanning electron microscopy, X-ray diffraction and hydrated equations. The results show that the hydration shrinkage can be restrained to a certain degree because the ultra-fine fly ash does not participate in the hydration at the early stage and the secondary hydration products are different at the later stage.

  2. Environmental CRIteria for CEMent based products, ECRICEM. Phase I. Ordinary Portland Cements. Phase II. Blended Cements. Executive Summary

    Energy Technology Data Exchange (ETDEWEB)

    Van der Sloot, H.A.; Van Zomeren, A. [ECN Biomass, Coal and Environmetal Research, Petten (Netherlands); Stenger, R. [Holcim Group Support Ltd, Holderbank (Switzerland); Schneider, M.; Spanka, G. [VDZ, Duesseldorf (Germany); Stoltenberg-Hansson, A. [NORCEM, HeidelbergCement Group, Brevik (Norway); Dath, P. [Holcim Belgium, Obourg (Belgium)

    2008-01-15

    The protection of the immediate environment of structural works is one of the essential requirements of the European Construction Products Directive (CPD). According to the CPD, construction products can only be put on the market, if the structural works built with them fulfil the relevant requirements for hygiene, and the protection of health and the environment. These essential requirements in the respective standards are specified at the national level by the individual member states. Cement and cementitious materials are considered to fulfil the fundamental requirements of the European Construction Products Directive and the corresponding national regulations. Therefore a technical regulation like the cement standard EN 197 in general does not cover separate requirements for determining compliance of cementitious materials with criteria on hygiene, health and environmental protection. Further regulations are laid down in cases where it appears necessary for constructive applications requiring a particular protection of water, soil and air.

  3. Hydration Heat Evolution of Cement and Its Relation With Setting Time

    Institute of Scientific and Technical Information of China (English)

    2006-01-01

    In order to veritably measure the first peak of hydration heat evolution that has been illustrated important in indicating cement behavior in early hydration, an improved way of water addition into cement in isothermally calorimetric experiment is put forward. The experimental results indicated that: the magnitude of first peak of heat evolution varies from sample to sample, correlation between heat evolution during first peak of heat evolution and initial (as well as final) setting time is unsatisfactory when samples are not classified; while groups of sample classified based on strength grade represent satisfactory correlations, which indicating the existence of close relation between hydration heat evolution in much earlier hydration age and setting property of cement in rather later age. Importance of first peak in hydration heat evolution for understanding cement setting property and reasons for sample classification are also discussed in this paper.

  4. Study on the hardening mechanism of cement asphalt binder

    Institute of Scientific and Technical Information of China (English)

    2010-01-01

    The hydration and hardening mechanism of cement asphalt binder(CAB) was studied.The early hydration process,hydration products and paste microstructure of CAB made by Portland cement and anionic asphalt emulsion were investigated by calorimetry,X-ray diffraction,and environmental scanning electron microscopy.The early hydration process of CAB can be characterized as 5 stages similar to those of Portland cement.There is no chemical reaction detected between cement and asphalt,hence no new hydration products other than those of Portland cement are produced.The hardening of CAB begins with the hydration of cement.When the hydration of cement comes into the acceleration period and its exothermic rate comes to the maximum,the coalescence of asphalt particles in asphalt emulsion is triggered.In the hardened system of CAB,it was found that the hydration products of cement form the skeleton and are covered by the continuous asphalt film.They formed an interpenetrating network system.The emulsifiers in the asphalt emulsion may retard the hydration process of cement.

  5. Hydration Characteristics and Immobilization of Cr (VI) in Slag Cement-CKD Pastes under Hydrothermal Treatment

    Institute of Scientific and Technical Information of China (English)

    M R Shatat; Gomaa A M Ali; M A Tantawy

    2015-01-01

    The effect of hydrothermal curing regimes on the hydration characteristics of slag cement containing different ratios of cement kiln dust has been studied. The samples for this study were combination of slag cement and cement kiln dust (5%-25%) without and with immobilization of 5% Cr (VI) by mass. Pastes were hydrothermally treated at 180℃ for different periods (2-24 h) in well closed stainless steel capsule. The hydration characteristics of these pastes were studied by measuring the compressive strength, bulk density, total porosity and combined water content. The findings were further supported by XRD and SEM analysis. The results indicated that the hydration characteristics of slag cement paste containing cement kiln dust 10% by mass were enhanced, especially at later ages (24 h) of hydration. That is due to the hydrothermal curing regimes of immobilized pastes accelerating hydration reactions and precipitation of CaCrO4, indicating that Cr (VI) can be solidiifed in the cement paste. This precipitation leads to pore formation in hydrated slag cement pastes.

  6. Influence of Crumb-Rubber in the Mechanical Response of Modified Portland Cement Concrete

    Directory of Open Access Journals (Sweden)

    J. Retama

    2017-01-01

    Full Text Available The influence of crumb-rubber on the mechanical properties of Portland cement concrete (PCC is studied by experimental tests and numerical simulations. The main hypothesis of the study is that replacing part of the stone aggregate with crumb-rubber in the mix modifies the energy dissipation during the cracking process and affects the concrete behaviour under monotonically increasing loads. The experimental research program characterizes the mechanical properties of PCC for three different types of concrete with a variable content of crumb-rubber. The experimental results showed that fracture energy and other properties are directly related to the rubber fineness used in the mixture. The material properties derived for these laboratory tests are used to study, by numerical models, its response through its damage evolution. The numerical model used to simulate the damage evolution of the concrete is the Embedded Discontinuity Method (EDM. One characteristic of the EDM is that it does not need to modify the mesh topology to propagate the damage through the continuum solid. For this study, the Disk-Shaped Compact Tension specimen geometry, normed by the D7313-13 of the ASTM, is used. Results showed that the numerical methods provide good approximation of the experimental curve in the elastic and softening branches.

  7. Study on Characteristics of Lightweight Aggregate Concrete Made From Foam and Ordinary Portland Cement

    Directory of Open Access Journals (Sweden)

    Ibrahim N.M.

    2016-01-01

    Full Text Available The production and characteristic of lightweight bubble aggregates (LBA are presented in this paper. The LBA are produced by mixing between the foam and ordinary Portland cement according to the composition which has been set. Then, the characteristics of LBA such as density, water absorption, specific gravity, compressive strength, aggregate impact value and microscopic analysis of the LBA are analyzed. Those characteristics are identified in order to ensure that the LBA are successfully categorized into lightweight aggregate. The loose bulk density is obtained at 812.5 kg/m3 which can be categorized under lightweight aggregate group. For water absorption the value obtained is 9.7 % which is slightly higher compared to normal aggregate. Meanwhile the average specific gravity obtained for the samples of LBAis 1.75. Compressive strength for the aggregates was 17.76 MPa. The highest compressive strength for LBA foamed concrete was obtained at 25% replacement with 7.83MPa. Thus, the LBA have a significant features and characteristics that can be used as coarse aggregates in concrete.

  8. Properties of high calcium fly ash geopolymer pastes with Portland cement as an additive

    Science.gov (United States)

    Phoo-ngernkham, Tanakorn; Chindaprasirt, Prinya; Sata, Vanchai; Pangdaeng, Saengsuree; Sinsiri, Theerawat

    2013-02-01

    The effect of Portland cement (OPC) addition on the properties of high calcium fly ash geopolymer pastes was investigated in the paper. OPC partially replaced fly ash (FA) at the dosages of 0, 5%, 10%, and 15% by mass of binder. Sodium silicate (Na2SiO3) and sodium hydroxide (NaOH) solutions were used as the liquid portion in the mixture: NaOH 10 mol/L, Na2SiO3/NaOH with a mass ratio of 2.0, and alkaline liquid/binder (L/B) with a mass ratio of 0.6. The curing at 60°C for 24 h was used to accelerate the geopolymerization. The setting time of all fresh pastes, porosity, and compressive strength of the pastes at the stages of 1, 7, 28, and 90 d were tested. The elastic modulus and strain capacity of the pastes at the stage of 7 d were determined. It is revealed that the use of OPC as an additive to replace part of FA results in the decreases in the setting time, porosity, and strain capacity of the paste specimens, while the compressive strength and elastic modulus seem to increase.

  9. Radiopacity and cytotoxicity of Portland cement associated with niobium oxide micro and nanoparticles

    Directory of Open Access Journals (Sweden)

    Leticia Boldrin MESTIERI

    2014-12-01

    Full Text Available Objective Mineral Trioxide Aggregate (MTA is composed of Portland Cement (PC and bismuth oxide (BO. Replacing BO for niobium oxide (NbO microparticles (Nbµ or nanoparticles (Nbη may improve radiopacity and bioactivity. The aim of this study was to evaluate the radiopacity and cytotoxicity of the materials: 1 PC; 2 White MTA; 3 PC+30% Nbµ; 4 PC+30% Nbη. Material and Methods For the radiopacity test, specimens of the different materials were radiographed along an aluminum step-wedge. For cell culture assays, Saos-2 osteoblastic-cells (ATCC HTB-85 were used. Cell viability was evaluated through MTT assay, and bioactivity was assessed by alkaline phosphatase activity assay. Results The results demonstrated higher radiopacity for MTA, followed by Nbµ and Nbη, which had similar values. Cell culture analysis showed that PC and PC+NbO associations promoted greater cell viability than MTA. Conclusions It was concluded that the combination of PC+NbO is a potential alternative for composition of MTA.

  10. The use of Portland cement in the repair of mandibular fractures in rats Uso de cimento Portland no reparo de fratura mandibular em ratos

    Directory of Open Access Journals (Sweden)

    Reginaldo Inojosa Carneiro Campello

    2011-12-01

    Full Text Available PURPOSE: To evaluate the bone healing of mandibular fractures following the use of Portland cement. METHODS: Thirty-two male Wistar rats were divided into control and experimental groups. In the control group the rats were submitted to a mandibular fracture, which was reduced, and the soft tissues were sutured. In the experimental group the rats had the mandibular fracture reduced and maintained with the Portland cement. The animals were euthanized 7 and 21 days after surgery by injecting a lethal dose of anesthetic. The following variables were studied: weight of the animals, radiographic images, histopathological features and time of surgery. RESULTS: A weight loss was observed in the specimens of both groups at the different times of evaluation, a greater difference in weight before and after surgery being found in the experimental group, which was statistically significant (p OBJETIVO: Avaliar a reparação óssea de fratura mandibular após o uso do cimento Portland (CP. MÉTODOS: Trinta e dois ratos machos Wistar foram divididos em grupo controle e grupo experimental. No grupo controle os ratos foram submetidos à fratura, redução e manutenção dos seguimentos com sutura dos tecidos moles. No grupo experimental foram submetidos a fratura, redução e manutenção dos segmentos fraturados com CP e sutura dos tecidos. Os animais foram eutanasiados com sete e 21 dias de pós-operatório através da injeção de dose letal dos anestésicos adotados. As variáveis estudadas foram: peso dos animais, avaliação tomográfica, avaliação histológica e tempo cirúrgico. RESULTADOS: Perda de peso foi observada nos espécimes de ambos os grupos nos diferentes intervalos de tempo considerados, sendo maior a diferença de peso antes e após cirurgia para o grupo experimental, que foi estatisticamente significante (p<0,05; p=0,041. Do ponto de vista histológico para a margem de erro fixada (5,0% as duas únicas diferenças significativas (p<0

  11. Hyperbolic Method to Analyze the Electrical Resistivity Curve of Portland Cements with Superplasticizer

    Institute of Scientific and Technical Information of China (English)

    WEI Xiaosheng; XIAO Lianzhen; LI Zongjin

    2008-01-01

    Electrical measurement was employed to investigate the early hydration characteristics of cement pastes with different dosages of superplasticizer in the same W/C ratio. The hyperbolic method was applied to analyze the electrical resistivity development. The peak point (Ph) on the hyperbolic curve could be easily read. The time (th) to reach the point Ph had strong relations with the setting time. th was delayed with the increment of the dosage of superplasticizer. The time th was used to plot the relationship between the initial setting time and final setting time. The hyperbolic equation was established to predict the ultimate resistivity.The retardation effect of the superplasticizer was confirmed in the same W/C ratio by setting time and isothermal heat eyolution.

  12. Partial replacement of Portland cement by red ceramic waste in mortars: study of pozzolanic activity; Substituicao parcial do cimento Portland por residuo de ceramica vermelha em argamassas: estudo da atividade pozolonica

    Energy Technology Data Exchange (ETDEWEB)

    Silva, A.R. da; Cabral, K.C.; Pinto, E.N. de M.G.l., E-mail: kleber.cabral@ufersa.edu.br [Universidade Federal Rural do Semi-Arido (UFERSA), Mossoro, RN (Brazil)

    2016-07-01

    The objective of this study is to analyze the pozzolanic activity of red ceramic residue on the partial replacement of Portland cement in mortars. The mortars were prepared by substituting 25% of the Portland cement for ground of ceramic residue with water cement’s factor of 0.48. The concrete used to construct the reference mortars and those with addiction was CPII-Z-32 (compound of Portland pozzolana cement). The chemical analysis and physical ceramic waste showed that this meets the requirements of NBR12653 (2014) for use as pozzolanic material. The pozzolanic activity index (IAP) obtained for the ceramic waste to twenty-eight days cure rate was 80.28%. (author)

  13. Compressive Strength of Volcanic Ash/Ordinary Portland Cement Laterized Concrete

    Directory of Open Access Journals (Sweden)

    Olusola K. O.

    2010-01-01

    Full Text Available This study investigates the effect of partial replacement of cement with volcanic ash (VA on the compressive strength of laterized concrete. A total of 192 cubes of 150mm dimensions were cast and cured in water for 7, 14, 21, and 28 days of hydration with cement replacement by VA and sand replacement by laterite both ranging from 0 to 30% respectively, while a control mix of 28-day target strength of 25 N/mm2 was adopted. The results show that the density and compressive strength of concrete decreased with increase in volcanic ash content. The 28-day, density dropped from 2390 kg/m3 to 2285 kg/m3 (i.e. 4.4% loss and the compressive strength from 25.08 N/mm2 to 17.98 N/mm2 (i.e. 28% loss for 0-30% variation of VA content with no laterite introduced. The compressive strength also decreased with increase in laterite content; the strength of the laterized concrete however increases as the curing age progresses.

  14. Influence of the Aggregate Volume on the Eleetrieal Resistivity and Properties of Portland Cement Concretes

    Institute of Scientific and Technical Information of China (English)

    WEI Xiaosheng; XIAO Lianzhen

    2011-01-01

    The electrical resistivity of concretes with various aggregate volume fractions (Va) of 0%-70%at water/cement (W/C) ratios of 0.4 and 0.5 during l day was monitored.It is found that the addition of normal aggregate to cement paste leads to a regular increase in concrete resistivity at each hydration stage and the electrical resistivity has a deeper increase for the lower W/C at a fixed aggregate volume fraction.The number of normalized resistivity (NR) of concrete to its paste matrix was introduced,which is only a function of aggregate volume fraction (Va).The quantitative relationships give an alternative method for the prediction of aggregate volume in the concrete.A logarithmic relation is established between the elastic modulus of concrete at 7 days or 28 days and the electrical resistivity of concrete at 1 day.The equations are obtained,the compressive strength of concrete at 7 days or 28 days can be determined by the electrical resistivity of concrete at 1 day and the used aggregate content in the concrete.The quantitative relationships give a non-destructive test (NDT) method for prediction of concrete elastic modulus and compressive strength.

  15. Influence of sodium borate on the early age hydration of calcium sulfoaluminate cement

    Energy Technology Data Exchange (ETDEWEB)

    Champenois, Jean-Baptiste; Dhoury, Mélanie [CEA, DEN, DTCD, SPDE, F-30207 Bagnols-sur-Cèze Cedex (France); Cau Dit Coumes, Céline, E-mail: celine.cau-dit-coumes@cea.fr [CEA, DEN, DTCD, SPDE, F-30207 Bagnols-sur-Cèze Cedex (France); Mercier, Cyrille [LMCPA, Université de Valenciennes et du Hainaut Cambrésis, 59600 Maubeuge (France); Revel, Bertrand [Centre Commun de Mesure RMN, Université Lille1 Sciences Technologies, Cité Scientifique, 59655 Villeneuve d' Ascq Cedex (France); Le Bescop, Patrick [CEA, DEN, DPC, SECR, F-91192 Gif-sur-Yvette (France); Damidot, Denis [Ecole des Mines de Douai, LGCgE-GCE, 59508 Douai (France)

    2015-04-15

    Calcium sulfoaluminate (CSA) cements are potential candidates for the conditioning of radioactive wastes with high sodium borate concentrations. This work thus investigates early age hydration of two CSA cements with different gypsum contents (0 to 20%) as a function of the mixing solution composition (borate and NaOH concentrations). Gypsum plays a key role in controlling the reactivity of cement. When the mixing solution is pure water, increasing the gypsum concentration accelerates cement hydration. However, the reverse is observed when the mixing solution contains sodium borate. Until gypsum exhaustion, the pore solution pH remains constant at ~ 10.8, and a poorly crystallized borate compound (ulexite) precipitates. A correlation is established between this transient precipitation and the hydration delay. Decreasing the gypsum content in the binder, or increasing the sodium content in the mixing solution, are two ways of reducing the stability of ulexite, thus decreasing the hydration delay.

  16. Interferometric microscopy study of the surface roughness of Portland cement under the action of different irrigants.

    Science.gov (United States)

    Ballester-Palacios, Maria L; Berástegui-Jimeno, Esther M; Parellada-Esquius, Neus; Canalda-Sahli, Carlos

    2013-09-01

    Some investigations suggested common Portland cement (PC) as a substitute material for MTA for endodontic use; both MTA and PC have a similar composition. The aim of this study was to determine the surface roughness of common PC before and after the exposition to different endodontic irrigating solutions: 10% and 20% citric acid, 17% ethylenediaminetetraacetic (EDTA) and 5% sodium hypochlorite. Fifty PC samples in the form of cubes were prepared. PC was mixed with distilled water (powder/liquid ratio 3:1 by weight). The samples were immersed for one minute in 10% and 20% citric acid, 17% EDTA and 5% sodium hypochlorite. After gold coating, PC samples were examined using the New View 100 Zygo interferometric microscope. It was used to examine and register the surface roughness and the profile of two different areas of each sample. Analysis of variance (ANOVA) was carried out, and as the requirements were not met, use was made of the Kruskal-Wallis test for analysis of the results obtained, followed by contrasts using Tukey's contrast tests. Sodium hypochlorite at a concentration of 5% significantly reduced the surface roughness of PC, while 20% citric acid significantly increased surface roughness. The other evaluated citric acid concentration (10%) slightly increased the surface roughness of PC, though statistical significance was not reached. EDTA at a concentration of 17% failed to modify PC surface roughness. Irrigation with 5% sodium hypochlorite and 20% citric acid lowered and raised the roughness values, respectively. The surface texture of PC is modified as the result of treatment with different irrigating solutions commonly used in endodontics, depending on their chemical composition and concentration.

  17. Quantitative determination of tricalcicum aluminate in portland cement by X-ray diffraction

    Directory of Open Access Journals (Sweden)

    Sagrera Moreno, José Luis

    1989-06-01

    Full Text Available Tricalcium aluminate (C3A is one of the constitutive phase of the cement-clinker. Its concentration influences the cement behaviour in sulphate aggressive soils. Therefore its quantification is very convenient and International standards fix its content when the concrete is used in contact with soils or liquids containing sulphate compounds. There are two possibilities in order to calculate the amount of C3A in clinker phases: one consist in a mathematical calculation from the results of the chemical analysis (Bogue formulae and the order is based in X-ray diffraction, using the height of the representative peak of the C3A phase. In the present note, the experimental procedure in order to determine the C3A content from X-ray test is presented.

    El aluminato tricáicico es una de las fases constitutivas del clinker de cemento portland. Su concentración en el cemento influye en el comportamiento de éste, en las obras sometidas a la posible agresividad de diferentes sulfatos cuando entran en contacto con las estructuras que se fabrican con él. Por ello la determinación de su concentración es un dato que puede invalidar su uso en una obra. De ahí que las normas internacionales fijen la cantidad de aluminato tricáicico según se clasifique la agresividad del entorno en el que una estructura será colocada. Existen fórmulas matemáticas para calcular la concentración de cada una de las fases del clinker a partir de las concentraciones de los elementos químicos de clinker expresados en forma de óxidos. Los posibles errores en los análisis químicos producen errores en los cálculos de las concentraciones de cada fase. Para determinar la concentración de dichas fases se puede emplear también la técnica de difracción de rayos X, basándose en la medida de la altura del pico representativo de la fase que se quiere determinar.

  18. Influence of supplementary cementitious materials on water transport kinetics and mechanical properties of hydrated lime and cement mortars

    Directory of Open Access Journals (Sweden)

    Ince, C.

    2015-06-01

    Full Text Available The purpose of this paper is an investigation of the possible role of supplementary cementitious materials (SCMs on water transport kinetics and mechanical properties of hydrated lime (CL90 and Portland cement (PC mortars. The properties of hydrated lime are significantly different from those of cement and therefore modifying fresh and hardened properties of these mortars are vital for mortar/substrate optimisation in masonry construction. The parameters investigated in this paper often are the main barriers to the use of hydrated lime in construction practice. The results show that transfer sorptivity and time to dewater freshly-mixed hydrated lime mortars can be modified when binder is partially replaced with SCMs. Compressive strength of CL90 mortars is increased systematically with the increased replacement levels of SCMs and the results are supported with the microstructural images. The ability to modify the water transport kinetics and mechanical properties allows compatibility between the mortar and the substrate unit in masonry construction.El objetivo de este artículo es investigar el papel de los materiales cementantes suplementarios (SCMs en la cinética de transporte del agua y en las propiedades mecánicas de los morteros de cal hidratada (CL90 y cemento Portland. Las propiedades de la cal hidratada son significativamente diferentes a las del cemento y por lo tanto el control de las propiedades de los morteros frescos y endurecidos es fundamental en la optimización mortero/substrato en albañilería. Los parámetros estudiados en este trabajo son a menudo las principales barreras para el uso de la cal hidratada en la práctica de la construcción. Los resultados indican que la absortividad y el tiempo necesario para deshidratar morteros de cal hidratada recién mezclados pueden ser controlados cuando el conglomerante es parcialmente remplazado por SCMs. La resistencia a compresión de los morteros CL90 aumenta sistem

  19. Potencialidades da metacaolinita e do tijolo queimado moído como substitutos parciais do cimento Portland Potentialities of metakaolin and crushed waste calcined clay brick as partial replacement of Portland cement

    Directory of Open Access Journals (Sweden)

    João de Farias Filho

    2000-12-01

    Full Text Available Avalia-se, neste trabalho, a potencialidade do uso da metacaolinita e dos resíduos de produção de tijolos cerâmicos queimados finamente moídos, como substitutos parciais do cimento Portland. Os materiais foram caracterizados física, química e mineralogicamente, além de determinado o índice de atividade pozolânica com cimento Portland. A evolução da resistência a compressão e a flexão das argamassas foi avaliada até as idades de, respectivamente, 365 e 208 dias. As porcentagens de substituição do cimento Portland, em peso, pelos materiais pozolânicos, variaram de 20 a 50%, enquanto o fator água/cimento variou de 0,37 a 0,45. Os resultados obtidos indicaram que a metacaolinita e o tijolo moído queimado possuem elevada atividade pozolânica e que a resistência a compressão, aos 28 dias, das argamassas mistas, foi superior à das argamassas de cimento Portland para os níveis de substituição e fatores água/cimento estudados. Um modelo matemático para predição da resistência à compressão das argamassas mistas é proposto com base em um desenho fatorial de experimentos.This paper evaluates the potentiality of metakaolin and crushed waste fired clay brick as cement replacement materials. They were characterised physically, chemically and mineralogically and their activity with Portland cement determined. The influence of the partial replacement of Portland cement on the development of compressive and flexural strength was evaluated until the age of, respectively, 365 and 208 days. The percentage of cement replacement, in weight, ranged from 20 to 50%, whereas the water/cement ratio ranged from 0.37 to 0.45. The results obtained show that the metakaolin and crushed calcined clay brick presented a good pozolanic activity and that the compressive strength of the blended mortars after 28 days of cure was higher than that observed for the reference Portland cement for all levels of cement replacement and water/cement ratio. A

  20. A sample holder for the study of isothermal heat of hydration of cement

    DEFF Research Database (Denmark)

    Hansen, Per Freiesleben; Jensen, Ole Mejlhede

    1998-01-01

    Different techniques for measuring heat of hydration of cement are discussed, and a sample holder designed specially for measuring isothermal heat of hydration is described. A particular characteristic of the sample holder is the vacuum mixing technique which ensures a momentary and homogeneous...

  1. Influence of the waste glass in the axial compressive strength of Portland cement concrete; Influencia dos residuos vitreos na resistencia a compressao axial do concreto de cimento Portland

    Energy Technology Data Exchange (ETDEWEB)

    Miranda Junior, E.J.P.; Paiva, A.E.M., E-mail: edson.jansen@hotmail.com [Instituto Federal de Educacao, Ciencia e Tecnologia do Maranhao (PPGEM/IFMA), Sao Luis, MA (Brazil). Programa de Pos-Graduacao em Engenharia de Materiais

    2012-07-01

    In this work, was studied the influence of the incorporation of waste glass, coming from the stage of thinning and polishing of a company of thermal glass treatments, in the axial compressive strength of Portland cement concrete. The coarse and ground aggregates used was crushed stone and sand, respectively. For production of the concrete, percentages of glass residues of 5%, 10% and 20% had been used in substitution to the sand, and relations water/cement (a/c) 0,50, 0,55 and 0,58. The cure of the test bodies was carried through in 7, 14 and 28 days. The statistics analysis of the results was carried out through of the analysis of variance for each one of the cure times. From the results of the compressive strength of the concrete, it could be observed that the concrete has structural application for the relation a/c 0,5, independently of waste glass percentage used, and for the relation a/c 0,55 with 20% of waste glass. (author)

  2. Design and manufacture of Portland cement - application of sensitivity analysis in exploration and optimisation Part II. Optimisation

    DEFF Research Database (Denmark)

    Svinning, K.; Høskuldsson, Agnar

    2006-01-01

    A program for a model-based optimisation has been developed. The program contains two subprograms. The first one does minimising or maximising constrained by one original PLS-component or one equal to a combination of several. The second one does searching for the optimal combination of PLS......-components, which gives max or min y. The program has proved to be applicable for achieving realistic results for implementation in the design of Portland cement with respect to performance and in the quality control during production....

  3. Chemo-physical modeling of cement mortar hydration: Role of aggregates

    Energy Technology Data Exchange (ETDEWEB)

    Jeong, Jena, E-mail: jeong@profs.estp.fr [Université Paris-Est, Institut de Recherche en Constructibilité, ESTP, 28 Avenue Président Wilson, 94234 Cachan (France); Ramézani, Hamidréza, E-mail: hamidreza.ramezani@univ-orleans.fr [CRMD, CNRS FRE 3520-Research Center on Divided Materials, École Polytechnique de l’Université d’Orléans, 8 rue Léonrad de Vinci, 45072 Orléans Cedex 2 (France); Leklou, Nordine, E-mail: nordine.leklou@univ-nantes.fr [LUNAM Université, Université de Nantes-IUT Saint-Nazaire, GeM, CNRS UMR 6183, Research Institute in Civil Engineering and Mechanics, 58 rue Michel Ange BP 420 44606 Saint Nazaire Cedex (France); Mounanga, Pierre, E-mail: pierre.mounanga@univ-nantes.fr [LUNAM Université, Université de Nantes-IUT Saint-Nazaire, GeM, CNRS UMR 6183, Research Institute in Civil Engineering and Mechanics, 58 rue Michel Ange BP 420 44606 Saint Nazaire Cedex (France)

    2013-07-20

    Graphical abstract: - Abstract: After mixing of the cement with water, most of the anhydride products sustain the hydration process and this leads to the hydrate products, e.g. CSH, Ca(OH){sub 2}, Afm and Aft. The mentioned hydration process is a highly complex phenomenon involving the chemically based thermo-activation inside the cement mortars during the early age hydration process. The chemo-thermal hydration reactions drasticaly increase at the early age of hydration after the mixing action and then it becomes less important and turns to be nearly asymptotic. The progress of the hydration phenomenon drives the material properties change during the very early age of cement hydration. Regarding the mortar and concrete, such hydration process would not be homogeneous through the cement matrix due to the aggregates presence. These inclusions will affect the temperature distribution as well as degree of hydration. In the current contribution, the chemical and thermal hydration have been firstly investigated by means of SEM observations using replica method and secondly by the 3D-FEM numerical experiments including two different case studies using glass beads as aggregates. The numerical experiments match fairly good the experimental measurements obtained using a pseudo-adiabatic testing setup for the case studies herein. The scanning electron microscopy (SEM) images observation demonstrates the gap spaces around the glass beads next to the external surfaces. These gaps can be essentially seen for the multi-glass beads case study. The role of the temperature and degree of hydration gradients are clearly obtained using the numerical samples. Some fresh routes and outlooks have been afterwards discussed.

  4. Influence of natural pozzolan, colemanite ore waste, bottom ash, and fly ash on the properties of Portland cement

    Energy Technology Data Exchange (ETDEWEB)

    Targan, S.; Olgun, A.; Erdogan, Y.; Sevinc, V. [Dumlupinar University, Kutahya (Turkey). Dept. of Chemistry

    2003-08-01

    The effect of natural pozzolan (NP), colemanite ore waste (CW), coal fly ash (FA), and coal bottom ash (BA) on the properties of cement and concrete was examined. The parameters studied included compressive strength, bending strength, volume expansion, and setting time. A number of cements were prepared (in the presence of fixed quantity of 10% FA, 10% BA, and 4% CW) by the replacement of Portland cement (PC) with NP in range of 5 - 30%. The results showed that the final setting time of cement pastes were generally accelerated when the NP replaced part of the cement. However, NP exhibited a significant retarding effect when used in combination with CW. The results also showed that the inclusion of NP at replacement levels of 5% resulted in an increase in compressive strength of the specimens compared with that of the control concrete. The replacement of PC by 10 - 15% of NP in the presence of fixed quantity of CW improves the bending strength of the specimens compared with control specimens after 60 days of curing age.

  5. Cement Formation:A Success Story in a Black Box: High Temperature Phase Formation of Portland Cement Clinker

    OpenAIRE

    2012-01-01

    Cement production has been subject to several technological changes, each of which requires detailed knowledgeabout the high multiplicity of processes, especially the high temperature process involved in the rotary kiln. This article gives an introduction to the topic of cement, including an overview of cement production, selected cement properties, and clinker phase relations. An extended summary of laboratory-scale investigations on clinkerization reactions, the most important reactions in ...

  6. Impact of the associated cation on chloride binding of Portland cement paste

    Energy Technology Data Exchange (ETDEWEB)

    De Weerdt, K., E-mail: klaartje.d.weerdt@ntnu.no [Department of Structural Engineering, Norwegian University of Science and Technology (Norway); Department of Engineering and Applied Sciences, University of Bergamo (Italy); Colombo, A. [Department of Structural Engineering, Norwegian University of Science and Technology (Norway); Department of Engineering and Applied Sciences, University of Bergamo (Italy); Coppola, L. [Department of Engineering and Applied Sciences, University of Bergamo (Italy); Justnes, H. [SINTEF Building and Infrastructure, Trondheim (Norway); Geiker, M.R. [Department of Structural Engineering, Norwegian University of Science and Technology (Norway)

    2015-02-15

    Well hydrated cement paste was exposed to MgCl{sub 2}, CaCl{sub 2} and NaCl solutions at 20 °C. The chloride binding isotherms for free chloride concentrations ranging up to 1.5 mol/l were determined experimentally. More chlorides were found to be bound when the associated cation was Mg{sup 2} {sup +} or Ca{sup 2} {sup +} compared to Na{sup +}. The chloride binding capacity of the paste appeared to be related to the pH of the exposure solution. In order to explain the cation dependency of the chloride binding a selection of samples was investigated in detail using experimental techniques such as TG, XRD and SEM–EDS to identify the phases binding the chlorides. The experimentally obtained data were compared with the calculations of a thermodynamic model, GEMS. It was concluded that the measured change in chloride binding depending on the cation was mainly governed by the pH of the exposure solution and thereby the binding capacity of the C-S-H.

  7. Evaluation of physical stability and leachability of Portland pozzolona cement (PPC) solidified chemical sludge generated from textile wastewater treatment plants.

    Science.gov (United States)

    Patel, Hema; Pandey, Suneel

    2012-03-15

    The chemical sludge generated from the treatment of textile dyeing wastewater is a hazardous waste as per Indian Hazardous Waste Management rules. In this paper, stabilization/solidification of chemical sludge was carried out to explore its reuse potential in the construction materials. Portland pozzolona cement (PPC) was selected as the binder system which is commercially available cement with 10-25% fly ash interground in it. The stabilized/solidified blocks were evaluated in terms of unconfined compressive strength, block density and leaching of heavy metals. The compressive strength (3.62-33.62 MPa) and block density (1222.17-1688.72 kg/m3) values as well as the negligible leaching of heavy metals from the stabilized/solidified blocks indicate that there is a potential of its use for structural and non-structural applications.

  8. The radiation stability of ground granulated blast furnace slag/ordinary Portland cement grouts containing organic admixtures

    Energy Technology Data Exchange (ETDEWEB)

    Palmer, J.D.; Fairhall, G.A. [British Nuclear Fuels, Sellafield (United Kingdom)

    1993-12-31

    At the British Nuclear Fuels (BNFL) Sellafield reprocessing plant in the United Kingdom, cement grouts based on ground granulated blast-furnace slag (BFS) and ordinary Portland cement (OPC) are used extensively for immobilizing radioactive wastes. These grouts have excluded organic admixtures in order to reduce process complexity and uncertainties, regarding the performance of organic admixtures with BFS/OPC grouts, particularly under irradiation. This study has investigated the effects of sulfonated melamine formaldehyde and naphthalene condensates on grout properties. The results show grout settlement and strengths increase on addition of additives, with the additives remaining largely in the pore solution. Under irradiation the additives breakdown liberating hydrogen and carbon dioxide. Strength and product dimensions are unaffected by irradiation.

  9. Phase I: energy-conservation potential of Portland cement particle-size-distribution control. Final report, March 1979

    Energy Technology Data Exchange (ETDEWEB)

    1979-03-01

    The properties of cements with carefully controlled particle-size distributions were compared with those of normally ground cements having a Blaine fineness of about 3600 cm/sup 2//g. Progressive reduction of the maximum particle size to 20 microns improved strength development. Further reduction to about 14 microns decreased rather than improved strength development. Some of these particle-size-controlled cements produce as-high, and often much-higher, strengths at ages from 1 to 60 days at Blaine finenesses 450 to 800 cm/sup 2//g lower than the normal grinds of the same composition. The cements with 20-micron maximum-size particles can have finenesses as low as 2800 cm/sup 2//g, whereas with larger particles, higher specific-surface areas are required for equal strengths. The improved strengths were a result of more-rapid and more-complete hydration of the cement. Variations of clinker composition did not significantly alter these conclusions. Drying shrinkage of the particle-size-controlled cements was in some cases less than for normally ground cements. They also performed better than normally ground cements over a wide range of mixing and curing temperature (42/sup 0/F to 100/sup 0/F). Direct energy conservation of 27% in finish grinding and 8.5% in more-efficient utilization of the cement is estimated to result from the use of particle-size-controlled cements. For a US production of 75 million tons, this corresponds to conservation of 46.5 trillion Btu/year.

  10. Research Progress in Applications of Calcium Sulphoaluminate Modified Portland Cement%硫铝酸钙改性硅酸盐水泥应用研究进展∗

    Institute of Scientific and Technical Information of China (English)

    葛大顺; 马素花; 李伟峰; 于锦; 沈晓冬; 汤国芳; 蔡建; 管娟

    2015-01-01

    Calcium sulphoaluminate modified Portland cement clinker has excellent characteristics of ordinary Portland cement clinker and sulphoaluminate cement clinker.Meanwhile this cement clinker has superior stimulating effect for fly-ash.These advantages confer SMP broad application prospects.Herein,the properties and hydration characteristics of SMP are summarized,and the composite properties of SMP with different mineral admixtures and the adaptability of this cement with chemical admixtures are also discussed.In addittion,the existing problems of SMP and improvement measures are proposed.%硫铝酸钙改性硅酸盐水泥熟料兼具硅酸盐水泥熟料和硫铝酸盐水泥熟料的优良性能,同时该种水泥熟料对粉煤灰等火山灰类材料具有超强的活性激发效果,这使得硫铝酸钙改性硅酸盐水泥具有广阔的应用前景。主要概括了硫铝酸盐改性硅酸盐水泥的性能及水化特性,综述了该种水泥与不同矿物掺合料的复合性能以及与化学外加剂的适应性,提出了硫铝酸钙改性硅酸盐水泥存在的问题及改善措施。

  11. Influence of SO{sub 2} deposition on cement mortar hydration

    Energy Technology Data Exchange (ETDEWEB)

    Martinez-Ramirez, S. [UMIST, Manchester (United Kingdom). Corrosion and Protection Centre

    1999-01-01

    The chemical reactions that occur during the hydration of Portland cement can be modified in the additional presence of certain compounds, such as SO{sub 2}, which may be present in areas of high pollutant gas concentration. This paper considers mortars that have been cured for 1 and 7 days and exposed to SO{sub 2} gas under dry and wet conditions. The role of ozone as gaseous catalyst in the reactions is studied. Fourier transform infrared spectrum analysis of the surface of the samples revealed carbonation had occurred; however, X-ray diffraction of the bulk material from the samples revealed Ca(OH){sub 2} only when the samples were exposed to dry conditions. In wet conditions, in the presence of water, the dissolution of CO{sub 2} gas is enhanced, the carbonation of the Ca(OH){sub 2} is promoted at higher levels, and thus no Ca(OH){sub 2} is detected. Under wet conditions, the degree of salt formation was greater than in dry conditions. In the presence of water, and due to Ca(OH){sub 2} carbonation, the pH of the pore solution is lower than 12; thus SO{sub 3}{sup 2{minus}} formation is favored. For the mortars exposed to dry conditions, kinetic salts such as K{sub 2}SO{sub 4} are formed. However, in the additional presence of water, thermodynamically stable products as K{sub 2}Ca(SO{sub 4}){sub 2}{center_dot}2H{sub 2}O and CaSO{sub 4}{center_dot}2H{sub 2}O are detected. The results of scanning electron microscopy indicated that the morphological composition of C-S-H gel resembles needle-like structures radiating from a grain. This morphology has been described by Taylor as type I.

  12. Microscopic air void analysis of hardened Portland cement concrete by the isolated shadow technique

    Science.gov (United States)

    Harris, Basil Mark

    The Isolated Shadow Technique is an image processing and analysis procedure for identifying and characterizing surface voids dispersed on an otherwise flat plane of heterogeneous solids. The objective of the Isolated Shadow Technique is to capture, process, and analyze images of a flat surface in which all of the features, save the boundary outlines of any surface voids, are eliminated. In short, the technique utilizes a series of digital images of the subject planar surface; where each image of the series is subjected to a unique lighting condition. By positioning the lights such that the shadows cast into the craters vary between images, these variations can be sequestered and the edges of the voids can subsequently be reconstructed from the isolated shadows. The primary purpose of this work was the development of the Isolated Shadow Technique for the particular application of quantitatively describing the microscopic voids in hardened Portland cement concrete. The Isolated Shadow System was developed for this application of the technique. The hardware and software of the system are described and the function is demonstrated. The system was found to have an average accuracy of 2.7% with a maximum deviation of 5.0% when compared to physical measurements. The results of polished sections of concrete specimens characterized by the Isolated Shadow System are compared to the results obtained with the commonly used standard methods (ASTM C 457; A and B). The coefficients of variation of parameters calculated to describe the air-void system (according to the ASTM C 457 formulations) are shown to be in the neighborhood of one percent when the observed test area includes at least 7,830 mmsp2 of polished concrete (with paste contents ranging from approximately 28% to 32%). The sensitivity of the air-void system parameters (as computed by the system) to changes in magnification and mosaic size are evaluated. A critical analysis of the underlying assumptions of the ASTM C

  13. Mossbauer Effect Study of the Hyper fine Structure of the Different Phases of Iron in the Portland Cement Produced in Qatar

    OpenAIRE

    Eissa, N. A. [نبيل عيسى; Sallam, H. A.; Al-Houty, L.; Al-Mauraikhy, M.

    1981-01-01

    Various samples of the raw materials used in the manufacture of Portland cement in Qatar, the clinker produced and the cement itself were studied by using Mossbauer Effect and X-ray diffraction analysis in order to investigate the hyperfine structure of the iron forms present and the distribution of these forms among the different phases of the cement. The results obtained revealed the presence of five forms of iron in the cement clinker (a) Fe3"1" ions in octahedral sites existed in the ferr...

  14. Calcium aluminate cement hydration in a high alkalinity environment

    Directory of Open Access Journals (Sweden)

    Palomo, Á.

    2009-03-01

    Full Text Available The present paper forms part of a broader research project that aims primarily to devise new cementitious products via the alkali activation of silico-aluminous materials. This work addresses the possibility of using small percentages of calcium aluminate cement (CAC as a source of reactive aluminium. For this reason, a preliminary review was needed of the behaviour of CACs in highly alkaline media (2, 8 and 12M NaOH solutions. Two, 28- and 180-day mechanical strength was determined and the reaction products were characterized with XRD and FTIR. The water-hydrated CAC was used as the control.The results obtained showed that CAC hardening took place much more slowly in highly alkaline media than in water. Nonetheless, the 28-day compressive strength obtained, ≥80MPa. As main reaction products, to ambient temperature and from the two days of cured, cubic aluminate C3AH6, and AH3 polymorphs are formed, instead of the usual hexagonal aluminatos (CAH10 and C2AH8 that are formed in the normal hydrate with water.El presente trabajo forma parte de una amplia investigación cuyo objetivo principal es el de elaborar nuevos materiales con propiedades cementantes mediante la activación alcalina de materiales de naturaleza silito-aluminosa. En estos estudios se contempla la posibilidad de utilizar pequeños porcentajes de cemento de aluminato de calcio (CAC como fuente de aluminio reactivo. Por ello inicialmente se ha estudiado el comportamiento de los CAC en medios fuertemente alcalinos (disoluciones de NaOH 2M, 8M y 12M. Se determinaron las resistencias mecánicas a 2, 28 y 180 días y se realizó una caracterización de los productos de reacción formados por DRX, FTIR. Como sistema de referencia se consideró la hidratación del CAC con agua.Los resultados obtenidos muestran que en medios fuertemente alcalinos se retrasan los procesos de rápido endurecimiento de CAC con agua. No obstante a 28 días se obtienen valores de resistencia a compresión

  15. Microstructure: Surface and cross-sectional studies of hydroxyapatite formation on the surface of white Portland cement paste in vitro

    Science.gov (United States)

    Chaipanich, Arnon; Torkittikul, Pincha

    2011-08-01

    The formation of hydroxyapatite was investigated at the surface and at the cross-section of white Portland cement paste samples before and after immersion in simulated body fluid. Scanning electron microscope images showed that hydroxyapatite were found at the surface of white Portland cement after immersion in simulated body fluid. Hydroxyapatite grains of mostly ≈1 μm size with some grain size of ≈2-3 μm were seen after 4 days immersion period. More estabilshed hydroxyapatite grain size of ≈3 μm grains were observed at longer period of immersion at 7 and 10 days. The cross-section of the samples was investigated using line scanning technique and was used to determine the hydroxyapatite layer. A strong spectrum of phosphorus is detected up to 6-8 μm depth for samples after 4, 7 and 10 days immersion in simulated body fluid when compared to weak spectrum detected before immersion. The increase in the phosphorus spectrum corresponds to the hydroxyapatite formation on the surface of the samples after the samples were placed in simulated body fluid.

  16. Characteristics and properties of oil-well cements auditioned with blast furnace slag; Cementos petroleros con adicion de escoria de horno alto. Caracteristicas y propiedades

    Energy Technology Data Exchange (ETDEWEB)

    Sanchez, R.; Palacios, M.; Puertas, F.

    2011-07-01

    The present paper addresses the alkali activation of Portland cements containing blast furnace slag (20 and 30% by cement weight) with a view to the possible use of these materials in oil well construction. The hydration studies conducted showed that in cement/slag blends, the sodium silicate activator partially inhibited the dissolution of the silicate phases in the Portland cement, retarding cement hydration and reducing the precipitation of reaction products. Due to such partial inhibition, the cement/slag blends had significantly lower mechanical strength than Portland cements hydrated with water. {sup 2}9Si and {sup 2}7Al MAS NMR and BSE/EDX studies, in turn, showed that the CSH gel forming in the alkali-activated cement/slag pastes contained Al in tetrahedral positions and low Ca/Si ratios. (Author) 29 refs.

  17. Manufacturing of mortars and concretes non-traditionals, by Portland cement, metakaoline and gypsum (15.05%

    Directory of Open Access Journals (Sweden)

    Talero, R.

    1999-12-01

    Full Text Available In a thorough previous research (1, it appeared that creation, evolution and development of the values of compressive mechanical strength (CS and flexural strength (FS, measured in specimens 1x1x6cm of mortar type ASTM C 452-68 (2, manufactured by ordinary Portland cement P-1 (14.11% C3A or PY-6 (0.00% C3A, metakaolin and gypsum (CaSO4∙2H2O -or ternary cements, CT-, were similar to the ones commonly developed in mortars and concretes of OPC. This paper sets up the experimental results obtained from non-traditional mortars and concretes prepared with such ternary cements -TC-, being the portland cement/metakaolin mass ratio, as follows: 80/20, 70/30 and 60/40. Finally, the behaviour of these cements against gypsum attack, has been also determined, using the following parameters: increase in length (ΔL%, compressive, CS, and flexural, FS, strengths, and ultrasound energy, UE. Experimental results obtained from these non-traditional mortars and concretes, show an increase in length (ΔL, in CS and FS, and in UE values, when there is addition of metakaolin.

    En una exhaustiva investigación anterior (1, se pudo comprobar que la creación, evolución y desarrollo de los valores de resistencias mecánicas a compresión, RMC, y flexotracción, RMF, proporcionados por probetas de 1x1x6 cm, de mortero 1:2,75, selenitoso tipo ASTM C 452-68 (2 -que habían sido preparadas con arena de Ottawa, cemento portland, P-1 (14,11% C3A o PY- 6 (0,00% C3A, metacaolín y yeso (CaSO4∙2H2O-, fue semejante a la que, comúnmente, desarrollan los morteros y hormigones tradicionales de cemento portland. En el presente trabajo se exponen los resultados experimentales obtenidos de morteros y hormigones no tradicionales, preparados con dichos cementos ternarios, CT, siendo las proporciones porcentuales en masa ensayadas, cemento portland/metacaolín, las siguientes: 80/20, 70

  18. The Hydration Characteristics and Expansion Machanism of Expansive Cement at Low W/B Ratio

    Institute of Scientific and Technical Information of China (English)

    LU Lin-nu; HE Yong-jia; LI Yue; DING Qing-jun; HU Shu-guang

    2003-01-01

    The hydration characteristics and expansion impetus of three kinds of cement paste under freeand confined-curing conditions were investigated, which were respectively mixed with three different kinds of expansive agent at low W/ B ratio. The results show that the hydration products of pure cement paste and paste mixed with expansive agent are same, but the amount of hydration products , un-hydrated C3 S and C2 S are obviously different at the same hydration age. At 3 d age, the amount of CH in pure cement paste is less than that of paste mixed with expaasive agent, but it is reverse when at 28d age. The amount of AFt at 3d and 28d age in pure cement paste is less than those of paste mixed with expansive agent. Regardless of under free- or confined-curing condition, the amount of ettringite produced varies little since 3 d age. The joint effect of the tumefaction of gel-ettringite due to water absorption and the expansive pressure on the pore caased by the crystalloid ettringite is the cause of the volume expansion of cement paste, and the former effect is much greater than the latter .

  19. Copper Slag Blended Cement: An Environmental Sustainable Approach for Cement Industry in India

    Directory of Open Access Journals (Sweden)

    Jagmeet Singh

    2016-04-01

    Full Text Available Indian cement industry is facing environmental issue of emission of carbon dioxide (CO2, a greenhouse gas. Blended cements including supplementary cementitious materials are substitute of Portland cement to reduce CO2 emission. The present paper investigates theappropriateness of copper slag (CS as supplementary cementitious material. Strength properties and hydration of mixes were determined at different replacement levels of CS with cement. Compressive, flexural and tensile strength of each mix was found out at different curing periods. The hydration of cement was investigated through X-ray diffraction (XRD. The strength test results showed that substitution of up to 20% of CS can significantly replace Portland cement.XRD test results were corresponding to strength test results. The present study encourages the utilization of CS as supplementary cementitious material to make economical and environmentally sustainable blended cement

  20. High-resolution synchrotron powder diffraction analysis of ordinary Portland cements: Phase coexistence of alite

    Science.gov (United States)

    de la Torre, Ángeles G.; Losilla, Enrique R.; Cabeza, Aurelio; Aranda, Miguel A. G.

    2005-08-01

    The mineralogical composition of four commercial and NIST RM-8488 Portland clinkers have been analysed by Rietveld methodology using high-resolution synchrotron X-ray powder diffraction data. Alite phase coexistence has been observed in four patterns. White Portland clinkers show a single alite or a very small amount of a second alite with smaller volume due to higher magnesium content. Grey Portland clinkers show a much pronounced alite phase coexistence which has been related to higher magnesium contents. Details about these analyses are given. Furthermore, the full mineralogical composition (including the non-diffracting content) has been determined from the overestimation of the added standard, α-Al2O3, in the Rietveld analyses. White clinkers contain ∼15 wt.% of non-diffracting content while this fraction is much smaller in grey clinkers, ∼7 wt.%.

  1. High-resolution synchrotron powder diffraction analysis of ordinary Portland cements: Phase coexistence of alite

    Energy Technology Data Exchange (ETDEWEB)

    Torre, Angeles G. de la [Departamento de Quimica Inorganica, Cristalografia y Mineralogia, Universidad de Malaga, 29071 Malaga (Spain); Losilla, Enrique R. [Departamento de Quimica Inorganica, Cristalografia y Mineralogia, Universidad de Malaga, 29071 Malaga (Spain); Cabeza, Aurelio [Departamento de Quimica Inorganica, Cristalografia y Mineralogia, Universidad de Malaga, 29071 Malaga (Spain); Aranda, Miguel A.G. [Departamento de Quimica Inorganica, Cristalografia y Mineralogia, Universidad de Malaga, 29071 Malaga (Spain)]. E-mail: g_aranda@uma.es

    2005-08-15

    The mineralogical composition of four commercial and NIST RM-8488 Portland clinkers have been analysed by Rietveld methodology using high-resolution synchrotron X-ray powder diffraction data. Alite phase coexistence has been observed in four patterns. White Portland clinkers show a single alite or a very small amount of a second alite with smaller volume due to higher magnesium content. Grey Portland clinkers show a much pronounced alite phase coexistence which has been related to higher magnesium contents. Details about these analyses are given. Furthermore, the full mineralogical composition (including the non-diffracting content) has been determined from the overestimation of the added standard, {alpha}-Al{sub 2}O{sub 3}, in the Rietveld analyses. White clinkers contain {approx}15 wt.% of non-diffracting content while this fraction is much smaller in grey clinkers, {approx}7 wt.%.

  2. A Histologic Evaluation on Tissue Reaction to Three Implanted Materials (MTA, Root MTA and Portland Cement Type I in the Mandible of Cats

    Directory of Open Access Journals (Sweden)

    F. Sasani

    2004-09-01

    Full Text Available Statement of Problem: Nowadays Mineral Trioxide aggregate (MTA is widely used for root end fillings, pulp capping, perforation repair and other endodontic treatments.Investigations have shown similar physical and chemical properties for Portland cement and Root MTA with those described for MTA.Purpose: The aim of this in vitro study was to evaluate the tissue reaction to implanted MTA, Portland cement and Root MTA in the mandible of cats.Materials and Methods: Under asepsis condition and general anesthesia, a mucoperiosteal flap, following the application of local anesthesia, was elevated to expose mandibular symphysis. Two small holes in both sides of mandible were drilled. MTA, Portland cement and Root MTA were mixed according to the manufacturers, recommendation and placed in bony cavities. In positive control group, the test material was Zinc oxide powder plus tricresoformalin. In negative control group, the bony cavities were left untreated. After 3,6 and 12 weeks, the animals were sacrificed and the mandibular sections were prepared for histologic examination under light microscope. The presence and thickness of inflammation, presence of fibrosis capsule, the severity of fibrosis and bone formation were investigated. The data were submitted to Exact Fisher test, chi square test and Kruskal-Wallis test for statistical analysis.Results: No statistically significant differences were found in the degree of inflammation,presence of fibrotic capsule, severity of fibrosis and inflammation thickness between Root MTA, Portland cement and MTA (P>0.05. There was no statistical difference in boneformation between MTA and Portland cement (P>0.05. However, bone formation was not found in any of the Root MTA specimens and the observed tissue was exclusively of fibrosis type.Conclusion: The physical and histological results observed with MTA are similar to those of Root MTA and Portland cement. Additionally, all of these three materials are biocompatible

  3. Effect of mixes made of coal bottom ash and fly ash on the mechanical strength and porosity of Portland cement

    Directory of Open Access Journals (Sweden)

    Argiz, C.

    2013-03-01

    Full Text Available New additions to the cement are needed to achieve a more sustainable and durable construction material. Within this context, bottom ashes can be used as a main constituent of Portland cements when it is mixed in an optimized proportion with fly ashes. The mechanical characteristics of standarized mortars made of mixes of pulverized coal combustion bottom and fly ashes are studied. The mortars were made of ordinary Portland cement (CEM I 42.5 N and mixes of bottom ashes with fly ashes in similar proportions to those of CEM II/A-V, CEM II/B-V and CEM IV/A (V. Summing up, it can be said that the utilization of bottom ashes mixed with fly ashes in replacement levels from 0% to 100% do not affect significantively on the mechanical caracteristics of the mortars considered in the present study which had an addition maximum content of 35%.

    La utilización de nuevas adiciones en el cemento es necesaria con el fin de obtener un material más sostenible y durable. En este sentido, las cenizas de fondo o cenicero de las centrales termoeléctricas de carbón se podrían reciclar siendo empleadas como un componente principal de los cementos Portland. Se han estudiado las propiedades mecánicas de unos morteros normalizados elaborados con mezclas de cenizas volantes con cenizas de fondo fabricados con unos porcentajes similares a los correspondientes de los CEM II/A-V, CEM II/B-V y CEM IV/A (V. En conclusión, la utilización de mezclas de cenizas de fondo o cenicero con cenizas volantes sustituyendo a éstas últimas entre el 0% y el 100%, no influye significativamente en el comportamiento mecánico de los morteros estudiados en los que el contenido máximo de adición ha sido del 35%, si bien afecta a determinados aspectos microestructurales, como la cantidad y distribución de poros capilares.

  4. Investigation on the potential of waste cooking oil as a grinding aid in Portland cement.

    Science.gov (United States)

    Li, Haoxin; Zhao, Jianfeng; Huang, Yuyan; Jiang, Zhengwu; Yang, Xiaojie; Yang, Zhenghong; Chen, Qing

    2016-12-15

    Although there are several methods for managing waste cooking oil (WCO), a significant result has not been achieved in China. A new method is required for safe WCO management that minimizes the environmental threat. In this context, this work was developed in which cement clinker and gypsum were interground with various WCOs, and their properties, such as grindability, water-cement ratio required to achieve a normal consistency, setting times, compressive strength, contents of calcium hydroxide and ettringite in the hardened paste, microstructure and economic and environmental considerations, were addressed in detail. The results show that, overall, WCO favorably improves cement grinding. WCO prolonged the cement setting times and resulted in longer setting times. Additionally, more remarkable effects were found in cements in which WCO contained more unsaturated fatty acid. WCOs increased the cement strength. However, this enhancement was rated with respect to the WCO contents and components. WCOs decreased the CH and AFt contents in the cement hardened paste. Even the AFt content at later ages was reduced when WCO was used. WCO also densify microstructure of the hardened cement paste. It is economically and environmentally feasible to use WCOs as grinding aids in the cement grinding process. These results contribute to the application of WCOs as grinding aids and to the safe management of WCO. Copyright © 2016 Elsevier Ltd. All rights reserved.

  5. Effects of chemical and mineral additives and the water/cement ratio on the thermal resistance of Portland cement concrete; O efeito de aditivos quimicos e minerais e da relacao agua/cimento na resistencia ao calor do concreto de concreto de cimento Portland

    Energy Technology Data Exchange (ETDEWEB)

    Cesar, Leandro Cesar Dias; Morelli, Arnaldo C.; Baldo, Joao Baptista [Sao Carlos Univ., SP (Brazil). Dept. de Engenharia de Materiais

    1998-07-01

    The exposure of Portland concrete to high temperatures (>250 deg C) can damage drastically the microstructural integrity of the material. Since the water/cement ratio as well as the inclusion of superplasticizers and mineral additives (silica fume) can alter constitutively and micro structurally the material, in this work it was investigated per effect of these additions on the damage resistance of portland concrete after exposure to high temperatures. (author)

  6. Formation of ettringite, Ca 6Al 2(SO 4) 3(OH) 12·26H 2O, AFt, and monosulfate, Ca 4Al 2O 6(SO 4)·14H 2O, AFm-14, in hydrothermal hydration of Portland cement and of calcium aluminum oxide—calcium sulfate dihydrate mixtures studied by in situ synchrotron X-ray powder diffraction

    Science.gov (United States)

    Christensen, Axel Nørlund; Jensen, Torben R.; Hanson, Jonathan C.

    2004-06-01

    In the hydration of calcium aluminum oxide-gypsum mixtures, i.e., Ca 3Al 2O 6, Ca 12Al 14O 33 and CaSO 4·2H 2O, the reaction products can be ettringite, Ca 6Al 2(SO 4) 3(OH) 12·26H 2O, monosulfate, Ca 4Al 2O 6(SO 4)·14H 2O, or the calcium aluminum oxide hydrate, Ca 4Al 2O 7·19H 2O. Ettringite is formed if sufficient CaSO 4·2H 2O is present in the mixture. Ettringite is converted to monosulfate when all CaSO 4·2H 2O is consumed in the synthesis of ettringite. The reactions were investigated in the temperature range 25-170°C using in situ synchrotron X-ray powder diffraction. This technique allows the study of very fast chemical reactions that are observed here under hydrothermal conditions. A new experimental approach was developed to perform in situ mixing of the reactants during X-ray data collection.

  7. Strengthening mechanism of cemented hydrate-bearing sand at microscales

    Science.gov (United States)

    Yoneda, Jun; Jin, Yusuke; Katagiri, Jun; Tenma, Norio

    2016-07-01

    On the basis of hypothetical particle-level mechanisms, several constitutive models of hydrate-bearing sediments have been proposed previously for gas production. However, to the best of our knowledge, the microstructural large-strain behaviors of hydrate-bearing sediments have not been reported to date because of the experimental challenges posed by the high-pressure and low-temperature testing conditions. Herein, a novel microtriaxial testing apparatus was developed, and the mechanical large-strain behavior of hydrate-bearing sediments with various hydrate saturation values (Sh = 0%, 39%, and 62%) was analyzed using microfocus X-ray computed tomography. Patchy hydrates were observed in the sediments at Sh = 39%. The obtained stress-strain relationships indicated strengthening with increasing hydrate saturation and a brittle failure mode of the hydrate-bearing sand. Localized deformations were quantified via image processing at the submillimeter and micrometer scale. Shear planes and particle deformation and/or rotation were detected, and the shear band thickness decreased with increasing hydrate saturation.

  8. Determination of strontium and simultaneous determination of strontium oxide, magnesium oxide and calcium oxide content of Portland cement by derivative ratio spectrophotometry.

    Science.gov (United States)

    Idriss, K A; Sedaira, H; Ahmed, S S

    2009-04-15

    A derivative spectrophotometric method has been developed for the determination of strontium in Portland cement. The method is applied successfully for the simultaneous determination of SrO, MgO and CaO. It is based on the use of Alizarin Complexone (AC) as a complexing agent and measurement of the derivative ratio spectra of the analytes. Interferences of manganese(II) and zinc(II) were eliminated by precipitation. The validity of the method was examined by analyzing several Standard Reference Material (SRM) Portland cement samples. The strontium complex formed at pH 9.5 allows precise and accurate determination of strontium over the concentration range of 1.5-18 mg L(-1) of strontium. The MDL (at 95% confidence level) was found to be 25 ng mL(-1) for strontium in National Institute of Standards and Technology (NIST) cement samples using the proposed method.

  9. Adsorption of cefixime from aqueous solutions using modified hardened paste of Portland cement by perlite; optimization by Taguchi method.

    Science.gov (United States)

    Rasoulifard, Mohammad Hossein; Khanmohammadi, Soghra; Heidari, Azam

    In the present study, we have used a simple and cost-effective removal technique by a commercially available Fe-Al-SiO2 containing complex material (hardened paste of Portland cement (HPPC)). The adsorbing performance of HPPC and modified HPPC with perlite for removal of cefixime from aqueous solutions was investigated comparatively by using batch adsorption studies. HPPC has been selected because of the main advantages such as high efficiency, simple separation of sludge, low-cost and abundant availability. A Taguchi orthogonal array experimental design with an OA16 (4(5)) matrix was employed to optimize the affecting factors of adsorbate concentration, adsorbent dosage, type of adsorbent, contact time and pH. On the basis of equilibrium adsorption data, Langmuir, Freundlich and Temkin adsorption isotherm models were also confirmed. The results showed that HPPC and modified HPPC were both efficient adsorbents for cefixime removal.

  10. Influence on the physical-mechanical properties of portland-cement mortar, have admixtures of colophony and tannin

    Directory of Open Access Journals (Sweden)

    Fernández Cánovas, M.

    1989-12-01

    Full Text Available The colophony has been used as an admixture in the Portland cement mortar with the intention to observe its influence on the air content, water absorption, adhesive capacity and mechanical properties. The results obtained have shown that, the colophony acts as air entrainment, reduces the permeability and improves the adhesion between the past and aggregates. Likewise, the addition of tannin and montan wax to the colophony has the efect of reducing the formation of foam and improves the impermeability of the mortar.

    Se ha empleado la colofonia como aditivo en el mortero de cemento portland con el fin de observar su influencia sobre el contenido de aire, absorción de agua, capacidad adhesiva y propiedades mecánicas. Los resultados obtenidos han puesto de manifiesto que la colofonia actúa como aireante, aumenta la impermeabilidad y mejora la adherencia de la pasta al árido. Asimismo, la adición de tanino y cera montana a la colofonia tiene el efecto de reducir la formación de espuma y mejorar también la impermeabilidad del mortero.

  11. Analysis by X-Ray images of EVA waste incorporated in Portland Cement; Analise atraves de imagens de raios X da incorporacao de residuo de EVA em cimento Portland

    Energy Technology Data Exchange (ETDEWEB)

    Marques, M.A.; Antunes, M.L.P.; Montagnoli, R.M.; Mancini, S.D., E-mail: marciomq@sorocaba.unesp.br [Universidade Estadual Paulista Julio de Mesquita Filho (UNESP), Sorocaba, SP (Brazil)

    2012-07-01

    The EVA is a copolymer used by Brazilian shoes industries. This material is cut for the manufacture of insoles. This operation generates about 18% of waste. The EVA waste can be reused in incorporation in Portland cement to construction without structural purposes. The aim of this work is to show X-rays images to assessment the space distribution of the wastes in the cement and to evaluate the use of this methodology. Cylindrical specimens were produced according to ABNT - NBR 5738 standards. The volume relation of sand and cement was 3:1, 10% and 30% of waste was incorporated in cement specimens. X-Rays images were obtained of cylindrical specimens in front projection. The images showed that the distribution of the waste is homogeneous, consistent with what was intended in this type of incorporation, which can provide uniformity in test results of compressive strength. (author)

  12. Rietveld full-profile quantification of Portland cement: the importance of including full crystallography of the phase polymorphs

    Energy Technology Data Exchange (ETDEWEB)

    Taylor, J.C.; Matulis, C.E [Commonwealth Scientific and Industrial Research Organization, Lucas Heights, NSW (Australia); Hinczak, I. [James Hardie Research Laboratories, Granville, NSW (Australia)

    1999-12-01

    Full text: Previous Rietveld quantifications of Portland cement clinkers used a fixed structural model for alite, the major clinker phase with a C{sub 3}S-type structure. From Rietveld quantification studies using the SlROQUANT{sup tm} program on XRD powder patterns of the three NIST SRM standard clinkers 8486, 8487, and 8488 (CoK{alpha}), it is shown that best results here are obtained using three C{sub 3}S models, one from each of the three crystal systems found in alite polymorphs. It is necessary to specify the phase crystallography well, owing to the extreme superposition of alite and belite XRD lines. Unsatisfactory results can sometimes occur when only one or two of these C{sub 3}S polymorphs are used in the Rietveld quantifications. Polymorphism in belite (clinker C{sub 2}S-type phase) and C{sub 3}A(aluminate phase), is also included. The Rietveld full-profile XRD method is shown to be as powerful in quantifying phases in Portland cement clinker as the microscope point-counting(MPC) method. The Rietveld method can in addition, discriminate between phase polymorphs, and is far less labour-intensive than MPC. Rietveld and MPC methods give the same results for the three NIST standard clinkers. The Rietveld oxide weight percentages, obtained from the Rietveld phase weight percentages by a reverse-Bogue calculation, assuming the average chemical compositions of the clinker phases of Taylor(1990), agree well with the XRF oxide percentages. The MPC method also agrees equally as well with XRF oxide percentages as the Rietveld method. Bogue weight percentages do not agree with Rietveld or MPC figures. Transformation of the Bogue percentages by the reverse-Bogue program to oxides does not give as good a comparison with XRF as does either the Rietveld or MPC method. Copyright (1999) Australian X-ray Analytical Association Inc.

  13. Long-term modeling of glass waste in portland cement- and clay-based matrices

    Energy Technology Data Exchange (ETDEWEB)

    Stockman, H.W.; Nagy, K.L. [Sandia National Labs., Albuquerque, NM (United States); Morris, C.E. [Wollongong Univ., NSW (Australia). Dept. of Civil and Mining Engineering

    1995-12-01

    A set of ``templates`` was developed for modeling waste glass interactions with cement-based and clay-based matrices. The templates consist of a modified thermodynamic database, and input files for the EQ3/6 reaction path code, containing embedded rate models and compositions for waste glass, cement, and several pozzolanic materials. Significant modifications were made in the thermodynamic data for Th, Pb, Ra, Ba, cement phases, and aqueous silica species. It was found that the cement-containing matrices could increase glass corrosion rates by several orders of magnitude (over matrixless or clay matrix systems), but they also offered the lowest overall solubility for Pb, Ra, Th and U. Addition of pozzolans to cement decreased calculated glass corrosion rates by up to a factor of 30. It is shown that with current modeling capabilities, the ``affinity effect`` cannot be trusted to passivate glass if nuclei are available for precipitation of secondary phases that reduce silica activity.

  14. Effect of Nano-TiO2 Addition on the Hydration and Hardening Process of Sulphoaluminate Cement

    Institute of Scientific and Technical Information of China (English)

    MA Baoguo; LI Hainan; MEI Junpeng; OUYANG Pei

    2015-01-01

    The influences of nano-TiO2 on the setting time, hydration process, hydration products and morphology of sulphoaluminate cement were studied by Vicat apparatus, isothermal calorimetry, X-ray diffraction (XRD), thermal analysis and scanning electron microscopy (SEM). The experimental results show that the incorporation of nano-TiO2 can obviously promote the setting and hardening process of sulphoaluminate cement, and shorten the interval between the initial and ifnal setting time, the hydration induction period of sulphoaluminate cement is significantly shortened and the acceleration period begins immediately, but the hydration exothermic rate at hydration stationary phase is not obviously impacted. The nano-TiO2 additives have inlfuence on the formation rate and degree of crystallinity, but do not affect the type of hydration process. The structure of hydration products is compact at middle age, but their content and microstructure do not change.

  15. Translational and rotational dynamics of water contained in aged Portland cement pastes studied by quasi-elastic neutron scattering.

    Science.gov (United States)

    Li, Hua; Zhang, Li-Li; Yi, Zhou; Fratini, Emiliano; Baglioni, Piero; Chen, Sow-Hsin

    2015-08-15

    Cement is a widely used construction material in the world. The quality and durability of aged cement pastes have a strong relationship with the water contained in it. The translational and rotational dynamics of water in ordinary Portland cement (OPC) pastes cured for 7, 14 and 30days were studied by analyzing Quasi-elastic Neutron Scattering (QENS) data. The effect of a new super-plasticizer (SP) additive was also studied by comparing the samples with and without the additive. By fitting the QENS spectra with the Jump-diffusion and Rotation-diffusion Model (JRM), six important parameters including the bound water index (BWI), the self-diffusion coefficient, D(t), the average residence time, τ0, the rotational diffusion constant, D(r), the rotational residence time, τ(r), and the mean squared displacement (MSD), 〈u(2)〉, were obtained. From these parameters, we can quantitatively follow the evolution of the bound water fraction (BWI). We can clearly see the different time ranges for the translational and rotational dynamics of water contained in the OPC pastes by τ0 and τ(r). From the MSD values compared with those of molecular dynamics simulation, we can distinguish between immobile water (mainly bound water) and mobile water, which includes confined water and ultraconfined water. Furthermore, by the fitted parameters' values and their change of slopes with increasing setting time for cement pastes with and without additive SP, it becomes clear that the effect of additive SP is to make the mobile water more confined and induce a more uniform the aging process during the evolution of the OPC pastes.

  16. Corrosion rate of steel embedded in blended Portland and fluid catalytic cracking catalyst residue (FC3R cement mortars

    Directory of Open Access Journals (Sweden)

    Payá, J.

    2008-12-01

    Full Text Available This paper reports on a study of the corrosion levels in steel bars embedded in mortars made with a blend of Portland cement and (0-20% spent fluid catalytic cracking catalyst residue (FC3R, with a variable (0.3-0.7 water/binder (w/b ratio. The specimens were stored in the following conditions: relative humidity of 40, 80 or 100% and CO2 concentrations of 5 and 100%. The steel corrosion rate was measured with polarization resistance techniques. In the absence of aggressive agents, the steel was found to remain duly passivated in mortars with an FC3R content of up to 15% under all the conditions of relative humidity tested. The reinforcement corrosion level in mortars with a w/b ratio of 0.3 and 15% FC3R subjected to accelerated carbonation was similar to the level observed in the unblended Portland cement control mortar.En este trabajo se ha estudiado el nivel de corrosión de barras de acero embebidas en morteros de cemento Portland con relación agua/material cementante (a/mc variable (0,3-0,7, en los que parte del cemento (0-20% se sustituyó por catalizador de craqueo usado (FC3R. Las condiciones de conservación de las probetas elaboradas fueron las siguientes: distintas humedades relativas (40, 80 y 100% y dos concentraciones de CO2 (5 y 100%. La velocidad de corrosión de los aceros se midió mediante la técnica de resistencia de polarización. Se ha podido determinar que, bajo las distintas condiciones de humedad relativa y ausencia de agresivo, los aceros se mantuvieron correctamente pasivados en los morteros con contenidos de FC3R de hasta el 15%. El nivel de corrosión que presenta el refuerzo embebidos en morteros con sustitución de un 15% de cemento por FC3R y relación a/mc 0,3, al ser sometidos a un proceso de carbonatación acelerada, era muy similar al mostrado por el mortero patrón, sin FC3R.

  17. Mössbauer, XRD, and Complex Thermal Analysis of the Hydration of Cement with Fly Ash

    Directory of Open Access Journals (Sweden)

    Vili Lilkov

    2013-01-01

    Full Text Available Hydration of cement with and without fly ash is studied with Mössbauer spectroscopy, XRD, and thermal analysis. Iron in cement is present as Fe3+-ions and occupies two octahedral positions, with close isomer shifts and quadrupole splittings. Iron in fly ash is present as Fe2+ and Fe3+, and the Mössbauer spectra display three doublets—two for Fe3+ in octahedral coordination and one for Fe2+. A third doublet was registered in the hydrating plain cement pastes after the 5th day, due to Fe3+ in tetrahedral coordination in the structure of the newly formed monosulphate aluminate. In cement pastes with fly ash, the doublet of tetrahedral iron is formed earlier because the quantity of ettringite and portlandite is low and more monosulphate crystallizes. No Fe(OH3 phase forms during hydration of C4AF. The fly ash displays pozzolanic properties, which lead to lowering of the portlandite quantity in the cement mixtures and increasing of the high temperature products.

  18. The Mechanical Properties and Hydration Characteristics of Cement Pastes Containing Added-calcium Coal Gangue

    Institute of Scientific and Technical Information of China (English)

    LI Dongxu; SONG Xuyan

    2008-01-01

    The mechanical properties of several kinds of coal gangue calcined with limestone were Researched so as to find the optimum way of calcinations with limestone. Mierostructure and property of hydration process of cement pastes containing added-calcium coal gangue were analyzed by means of scanning electron microscope (SEM) and method of mercury in trusion poremeasurement (MIP), etc. The experiment can approve those results: when proper amounst of gypsum and fluorite were taken as mineralizers in the course of calcinations of added-calcium coal gangue, activity of coal gangue can be effectively improved. The results of mechanical property and structural characteristic such as hydration process, hydration product and microstructure etc. of cement pastes containing added-calcium coal gangue are consistent.

  19. Durability Index Performance of High Strength Concretes Made Based on Different Standard Portland Cements

    Directory of Open Access Journals (Sweden)

    Stephen O. Ekolu

    2012-01-01

    Full Text Available A consortium of three durability index test methods consisting of oxygen permeability, sorptivity and chloride conductivity were used to evaluate the potential influence of four (4 common SANS 10197 cements on strength and durability of concrete. Twenty four (24 concrete mixtures of water-cement ratios (w/c's = 0.4, 0.5, 0.65 were cast using the cement types CEM I 42.5N, CEM II/A-M (V-L 42.5N, CEM IV/B 32.5R and CEM II/A-V 52.5N. The concretes investigated fall in the range of normal strength, medium strength and high strength concretes. It was found that the marked differences in oxygen permeability and sorptivity results observed at normal and medium strengths tended to vanish at high concrete strengths. Also, the durability effects attributed to use of different cement types appear to diminish at high strengths. Cements of low strength and/or that contained no extenders (CEM 32.5R, CEM I 42.5N showed greater sensitivity to sorptivity, relative to other cement types. Results also show that while concrete resistance to chlorides generally improves with increase in strength, adequately high chloride resistance may not be achieved based on high strength alone, and appropriate incorporation of extenders may be necessary.

  20. Follow up of the glassy phase formation as silicon oxide was added to Brownmillerite phase of Portland cement clinker

    Energy Technology Data Exchange (ETDEWEB)

    Hassaan, M. Y., E-mail: yousry@tedata.net.eg; Salem, S. M.; Ebrahim, F. M. [Al-Azhar University, Moessbauer Lab, Physics Department, Faculty of Science (Egypt)

    2009-01-15

    Brownmillerite phase is one of the four main phases of Portland cement clinker. It was prepared as pure C{sub 4}AF{sup 1} and C{sub 4}AF with different amount of SiO{sub 2}, (5, 10, 15, 20, 25, and 40 mol%) by addition. Pure C{sub 4}AF was prepared using CaO, Al{sub 2}O{sub 3} and Fe{sub 2}O{sub 3} according to the ratios 4:1:1. Each sample mixture was fired at 1,400 deg. C for 1 h then ground and introduced again to 1,400 deg. C for 1/2 h then quenched in air. The prepared samples were ground and measured using x-ray diffraction, scanning electron microscope, A.C. conductivity and Moessbauer spectroscopy. The results were correlated and discussed. The main finding is the formation of a glassy phase besides the C{sub 4}AF structure, in addition to the formation of the C{sub 2}S phase of cement clinker as SiO{sub 2} addition was upgraded. The electrical conductivity results showed that the 20 mol% SiO{sub 2} sample has the lowest ({sigma}) value.

  1. Examples of cooler reflective streets for urban heat-island mitigation : Portland cement concrete and chip seals

    Energy Technology Data Exchange (ETDEWEB)

    Pomerantz, M.; Akbari, H.; Chang, S.-C.; Levinson, R.; Pon, B.

    2003-04-30

    Part of the urban heat island effect can be attributed to dark pavements that are commonly used on streets and parking lots. In this paper we consider two light colored, hence cooler, alternative paving materials that are in actual use in cities today. These are Portland cement concrete (PCC) pavements and chip seals. We report measurements of the albedos of some PCC and chip sealed pavements in the San Francisco Bay Area. The albedos of the PCC pavements ranged from about 0.18 to 0.35. The temperatures of some PCC pavements are also measured and calculated. We then consider how the albedos of the constituent materials of the PCC (stone, sand and cement) contribute to the albedos of the resulting finished concrete. The albedos of a set of chip sealed pavements in San Jose, CA, were measured and correlated with the times of their placement. It is found that the albedos decrease with age (and use) but remain higher than that of standard asphalt concrete (AC) for about five years. After t hat, the albedos of the chip seals are about 0.12, similar to aged AC. The fact that many PCC pavements have albedos at least twice as high as aged AC suggests that it is possible to have pavement albedos that remain high for many years.

  2. In vitro cytotoxicity of white MTA, MTA Fillapex® and Portland cement on human periodontal ligament fibroblasts.

    Science.gov (United States)

    Yoshino, Patrícia; Nishiyama, Celso Kenji; Modena, Karin Cristina da Silva; Santos, Carlos Ferreira; Sipert, Carla Renata

    2013-01-01

    The aim of this study was to compare the in vitro cytotoxicity of white mineral trioxide aggregate (MTA), MTA Fillapex® and Portland cement (PC) on human cultured periodontal ligament fibroblasts. Periodontal ligament fibroblast culture was established and the cells were used for cytotoxic tests after the fourth passage. Cell density was set at 1.25 X10 4 cells/well in 96-well plates. Endodontic material extracts were prepared by placing sealer/cement specimens (5x3mm) in 1mL of culture medium for 72 h. The extracts were then serially two-fold diluted and inserted into the cell-seeded wells for 24, 48 and 72 h. MTT assay was employed for analysis of cell viability. Cell supernatants were tested for nitric oxide using the Griess reagent system. MTA presented cytotoxic effect in undiluted extracts at 24 and 72 h. MTA Fillapex® presented the highest cytotoxic levels with important cell viability reduction for pure extracts and at ½ and ¼ dilutions. In this study, PC did not induce alterations in fibroblast viability. Nitric oxide was detected in extract-treated cell supernatants and also in the extracts only, suggesting presence of nitrite in the soluble content of the tested materials. In the present study, MTA Fillapex displayed the highest cytotoxic effect on periodontal ligament fibroblasts followed by white MTA and PC.

  3. In-situ early-age hydration study of sulfobelite cements by synchrotron powder diffraction

    Energy Technology Data Exchange (ETDEWEB)

    Álvarez-Pinazo, G.; Cuesta, A.; García-Maté, M.; Santacruz, I.; Losilla, E.R. [Departamento de Química Inorgánica, Universidad de Málaga, Campus Teatinos S/N., 29071 Málaga (Spain); Sanfélix, S.G. [Unidad Técnica de Investigación de Materiales, AIDICO, Avda. Benjamín Franklin, 17 Paterna, Valencia (Spain); Fauth, F. [CELLS-Alba synchrotron, Carretera BP 1413, Km. 3.3, E-08290 Cerdanyola, Barcelona (Spain); Aranda, M.A.G. [Departamento de Química Inorgánica, Universidad de Málaga, Campus Teatinos S/N., 29071 Málaga (Spain); CELLS-Alba synchrotron, Carretera BP 1413, Km. 3.3, E-08290 Cerdanyola, Barcelona (Spain); De la Torre, A.G., E-mail: mgd@uma.es [Departamento de Química Inorgánica, Universidad de Málaga, Campus Teatinos S/N., 29071 Málaga (Spain)

    2014-02-15

    Eco-friendly belite calcium sulfoaluminate (BCSA) cement hydration behavior is not yet well understood. Here, we report an in-situ synchrotron X-ray powder diffraction study for the first hours of hydration of BCSA cements. Rietveld quantitative phase analysis has been used to establish the degree of reaction (α). The hydration of a mixture of ye'elimite and gypsum revealed that ettringite formation (α ∼ 70% at 50 h) is limited by ye'elimite dissolution. Two laboratory-prepared BCSA cements were also studied: non-active-BCSA and active-BCSA cements, with β- and α′{sub H}-belite as main phases, respectively. Ye'elimite, in the non-active-BCSA system, dissolves at higher pace (α ∼ 25% at 1 h) than in the active-BCSA one (α ∼ 10% at 1 h), with differences in the crystallization of ettringite (α ∼ 30% and α ∼ 5%, respectively). This behavior has strongly affected subsequent belite and ferrite reactivities, yielding stratlingite and other layered phases in non-active-BCSA. The dissolution and crystallization processes are reported and discussed in detail. -- Highlights: •Belite calcium sulfoaluminate cements early hydration mechanism has been determined. •Belite hydration strongly depends on availability of aluminum hydroxide. •Orthorhombic ye’elimite dissolved at a higher pace than cubic one. •Ye’elimite larger reaction degree yields stratlingite formation by belite reaction. •Rietveld method quantified gypsum, anhydrite and bassanite dissolution rates.

  4. Hydration Characteristics of Low-Heat Cement Substituted by Fly Ash and Limestone Powder

    Directory of Open Access Journals (Sweden)

    Si-Jun Kim

    2015-09-01

    Full Text Available This study proposed a new binder as an alternative to conventional cement to reduce the heat of hydration in mass concrete elements. As a main cementitious material, low-heat cement (LHC was considered, and then fly ash (FA, modified FA (MFA by vibrator mill, and limestone powder (LP were used as a partial replacement of LHC. The addition of FA delayed the induction period at the hydration heat curve and the maximum heat flow value (qmax increased compared with the LHC based binder. As the proportion and fineness of the FA increased, the induction period of the hydration heat curve was extended, and the qmax increased. The hydration production of Ca(OH2 was independent of the addition of FA or MFA up to an age of 7 days, beyond which the amount of Ca(OH2 gradually decreased owing to their pozzolanic reaction. In the case of LP being used as a supplementary cementitious material, the induction period of the hydration heat curve was reduced by comparison with the case of LHC based binder, and monocarboaluminate was observed as a hydration product. The average pore size measured at an age of 28 days was smaller for LHC with FA or MFA than for 100% LHC.

  5. Clinkering and hydration of belite-ye'elimite-alite cement

    OpenAIRE

    Londono-Zuluaga, Diana; Tobón, Jorge Iván; Aranda, Miguel A. G.; SANTACRUZ, ISABEL; De la Torre, Angeles G.

    2017-01-01

    Some belite-ye´elimite-ferrite (BYF) cements present low mechanical strengths mainly due to the slow reactivity of belite. A solution to this problem may be the activation of BYF clinkers by preparing them with a coexistence of alite and ye´elimite, which are known as belite-alite-ye´elimite (BAY) cements. The objective of this work was the preparation of BAY mortars that show higher mechanical strengths than BYF mortars. In order to attain this, the clinkering conditions to prepare BAY-c...

  6. Evolution and quantification of the main sensitisers in commercial Portland cements

    OpenAIRE

    2002-01-01

    [ES] Los cementos Portland comerciales contienen elementos minoritarios en su composición química. La presencia de estos elementos tiene una incidencia directa en diferentes aspectos: comportamiento reológico, cinética de reacción, contaminación ambiental, etc. Algunos de ellos, aparte de su incidencia mencionada anteriormente, tienen un efecto negativo en la salud humana. Así, el cromo (Cr), níquel (Ni) y cobalto (Co) son los principales alérgenos contenidos en los cementos y, po...

  7. Chloride adsorption by calcined layered double hydroxides in hardened Portland cement paste

    KAUST Repository

    Yoon, Seyoon

    2014-06-01

    This study investigated the feasibility of using calcined layered double hydroxides (CLDHs) to prevent chloride-induced deterioration in reinforced concrete. CLDHs not only adsorbed chloride ions in aqueous solution with a memory effect but also had a much higher binding capacity than the original layered double hydroxides (LDHs) in the cement matrix. We investigated this adsorption in hardened cement paste in batch cultures to determine adsorption isotherms. The measured and theoretical binding capacities (153 mg g -1 and 257 mg g-1, respectively) of the CLDHs were comparable to the theoretical capacity of Friedel\\'s salt (2 mol mol-1 or 121 mg g-1), which belongs to the LDH family among cementitious phases. We simulated chloride adsorption by CLDHs through the cement matrix using the Fickian model and compared the simulation result to the X-ray fluorescence (XRF) chlorine map. Based on our results, it is proposed that the adsorption process is governed by the chloride transport through the cement matrix; this process differs from that in an aqueous solution. X-ray diffraction (XRD) analysis showed that the CLDH rebuilds the layered structure in a cementitious environment, thereby demonstrating the feasibility of applying CLDHs to the cement and concrete industries. © 2014 Published by Elsevier B.V. All rights reserved.

  8. Effect of Hydroxyapatite and Shell on Cement Hydration and Sulfate Resistance%羟基磷灰石和贝壳对水泥水化和抗侵蚀性能的影响

    Institute of Scientific and Technical Information of China (English)

    王桂芸; 芦令超; 王守德; 赵丕琪

    2011-01-01

    Coastal cement concrete engineering has been eroded for a long time, and cant achieve their expected service lives. One solution was to just cultivate the ocean living beings on the surface of cement concrete engineering to resist the corrosion. The influences of hydroxyapatite, shell powder and calcium carbonate on the durability of 42.5R ordinary Portland cement and sulphoaluminate cement were investigated. The sulfate corrosion resistance coefficients of the cement would increase to some extent when appropriate content of hydroxyapatite, shell powder and calcium carbonate were added. When the content of calcium carbonate in the sulphoaluminate cement was 10%, the corrosion resistance coefficient was 1.16; and when the content of calcium carbonate in the ordinary Portland cement was 15%, the corrosion resistance coefficient reached 1.34, the performance of resistance to sulfate attack was best.When the hydroxyapatite was added into the ordinary Portland cement and the sulphoaluminate cement,the hydration heat was lower than that of the cement containing shell powder and calcium carbonate.When the hydroxyapatite, shell powder and calcium carbonate were added into the ordinary Portland cement, each hydration heat was lower than that of the ordinary Portland cement; this was helpful for the durability of the cement concrete engineering.%沿海水泥混凝土工程长期受到腐蚀,很难达到预期服役寿命.本文分析其中的原因,希望采用水泥混凝土表面生长海洋生物的方法来抵抗腐蚀.研究羟基磷灰石、贝壳和碳酸钙对硅酸盐42.5R水泥和硫铝酸盐水泥抗硫酸盐侵蚀性能的影响.结果表明:硅酸盐水泥和硫铝酸盐水泥中掺人适萤的羟基磷灰石、贝壳和碳酸钙时,其抗侵蚀系数有一定程度增加.当硫铝酸盐水泥中碳酸钙掺量为10%时,其抗侵蚀系数为1.16,硅酸盐水泥中碳酸钙掺量为15%时,其抗侵蚀系数达到1.34,抗硫酸盐侵蚀能力最强.硅酸盐

  9. Formulating a low-alkalinity cement for radioactive waste repositories

    Energy Technology Data Exchange (ETDEWEB)

    Coumes, C. Cau Dit; Courtois, S.; Leclercq, S.; Bourbon, X

    2004-07-01

    A multi-annual research program has been launched in January 2003 by CEA, EDF and ANDRA in order to formulate and characterize low-alkalinity and low-heat cements which would be compatible with an underground waste repository environment. Four types of bindings have been investigated: binary blends of Portland cement and silica fume or metakaolin, as well as ternary blends of Portland cement, fly ash and silica fume or metakaolin. Promising results have been obtained with a mixture comprising 37.5% Portland cement, 32.5% silica fume, and 30% fly ash: pH of water in equilibrium with fully hydrated cement is below 11. Moreover, silica fume compensates for the low reactivity of fly ash, while fly ash allows to reduce water demand, heat release, and dimensional variations of cement pastes and mortars. (authors)

  10. Microstructure engineering of Portland cement pastes and mortars through addition of ultrafine layer silicates

    DEFF Research Database (Denmark)

    Lindgreen, Holger; Geiker, Mette Rica; Krøyer, Hanne;

    2008-01-01

    , and the nano-structure of the C-S-H depends on type of layer silicate. The effect of layer silicate addition is most pronounced for palygorskite and smectite having the largest surface area and negative charges on the particle surfaces. The cement pastes containing palygorskite and bentonite have......, in comparison to the pure cement pasta and the paste containing kaolinite, a more open pore structure consisting of fine pores. Silica fume paste contains a significant amount of closed pores. As a secondary result, it is demonstrated that both the degree and duration of sample drying strongly modifies...

  11. Preliminary Examination of the System Fly Ash-Bottom Ash-Flue Gas Desulphurization Gypsum-Portland Cement-Water for Road Construction

    Directory of Open Access Journals (Sweden)

    R. Tokalic

    2013-01-01

    Full Text Available This paper describes an investigation into the use of three power plant wastes: fly ash, flue gas desulphurization gypsum, and bottom ash for subbase layers in road construction. Two kinds of mixtures of these wastes with Portland cement and water were made: first with fly ash consisting of coarser particles (<1.651 mm and second with fly ash consisting of smaller particles (<0.42 mm. The mass ratio of fly ash-Portland cement-flue gas desulphurization gypsum-bottom ash was the same (3 : 1 : 1 : 5 in both mixtures. For both mixtures, the compressive strength, the mineralogical composition, and the leaching characteristics were determined at different times, 7 and 28 days, after preparation. The obtained results showed that both mixtures could find a potential use for subbase layers in road construction.

  12. Effect of sewage sludge ash (SSA on the mechanical performance and corrosion levels of reinforced Portland cement mortars

    Directory of Open Access Journals (Sweden)

    Andión, L. G.ª

    2006-06-01

    Full Text Available The article describes a study conducted to determinecorrosion in reinforcement embedded in Portland cement(PC mortars with different percentages of sewage sludgeash (SSA admixtures. The polarization resistancetechnique was used to determine the steel corrosion rate(Icorr in the test specimens. The samples were subjectedto different environmental conditions and aggressiveagents: 100% relative humidity (RH, accelerated carbonationat 70% RH and seawater immersion. Portlandcement was partially substituted for SSA in the mixes atrates of 0, 10, 20, 30 and 60% (by mass to make thedifferent mortars. The results show that where cementwas replaced by SSA at rates of up to 10% by mass,mortar corrosion performance was comparable to thebehaviour observed in SSA-free mortars (control mortar:0% SSA. Data for higher rates are also shown. From themechanical standpoint, SSA exhibited moderate pozzolanicactivity and the best performance when SSA wasadded at a rate of 10% to mixes with a water/(binder:PC + SSA (w/b ratio of 0.5.Se ha estudiado el nivel de corrosion que presentan lasarmaduras embebidas en morteros fabricados con cementoPortland (CP con diferentes porcentajes de sustitucion deceniza de lodo de depuradora (CLD. Se ha utilizado la tecnicade la Resistencia a la Polarizacion para determinar lavelocidad de corrosion del acero embebido en las muestrasestudiadas. Las muestras se han sometido a diferentes condicionesambientales y agentes agresivos: 100% de humedadrelativa (HR, carbonatacion acelerada al 70% HR einmersion en agua de mar. Para la fabricacion de los distintosmorteros, el cemento Portland ha sido parcialmente sustituidopor CLD en los siguientes porcentajes en masa: 0,10, 20, 30 y 60%. Los resultados muestran que sustitucionesde cemento por CLD de hasta el 10% en masa no alteranel comportamiento frente a la corrosion de los morterosal compararlos con los morteros libres de CLD (morteroscontrol: 0% de sustitucion de cemento por CLD. Se

  13. Evaluation of Portland cement from X-ray diffraction associated with cluster analysis; Avaliacao de cimento Portland a partir da difracao de raios X associada a analise por agrupamento

    Energy Technology Data Exchange (ETDEWEB)

    Gobbo, Luciano de Andrade, E-mail: luciano.gobbo@panalytical.com [Panalytical Brasil, Sao Paulo, SP (Brazil); Montanheiro, Tarcisio Jose, E-mail: tarcisio.montanheiro@gmail.com [Instituto Geologico, Secretaria de Estado do Meio Ambiente, Sao Paulo, SP (Brazil); Montanheiro, Filipe, E-mail: flpmontanheiro@gmail.com [Universidade Estadual Paulista (LEBAC/UNESP), Rio Claro, SP (Brazil). Departamento de Geologia Aplicada. Lab. de Estudos de Bacias; Sant' Agostino, Lilia Mascarenhas, E-mail: agostino@usp.br [Universidade de Sao Paulo (USP), SP (Brazil). Instituto de Geociencias. Departamento de Geologia Sedimentar e Ambiental

    2013-12-15

    The Brazilian cement industry produced 64 million tons of cement in 2012, with noteworthy contribution of CP-II (slag), CP-III (blast furnace) and CP-IV (pozzolanic) cements. The industrial pole comprises about 80 factories that utilize raw materials of different origins and chemical compositions that require enhanced analytical technologies to optimize production in order to gain space in the growing consumer market in Brazil. This paper assesses the sensitivity of mineralogical analysis by X-ray diffraction associated with cluster analysis to distinguish different kinds of cements with different additions. This technique can be applied, for example, in the prospection of different types of limestone (calcitic, dolomitic and siliceous) as well as in the qualification of different clinkers. The cluster analysis does not require any specific knowledge of the mineralogical composition of the diffractograms to be clustered; rather, it is based on their similarity. The materials tested for addition have different origins: fly ashes from different power stations from South Brazil and slag from different steel plants in the Southeast. Cement with different additions of limestone and white Portland cement were also used. The Rietveld method of qualitative and quantitative analysis was used for measuring the results generated by the cluster analysis technique. (author)

  14. Effect of Combined Calcium Hydroxide and Accelerated Portland Cement on Bone Formation and Soft Tissue Healing in Dog Bone Lesions

    Directory of Open Access Journals (Sweden)

    Khorshidi H

    2015-09-01

    Full Text Available Statement of Problem: Recent literatures show that accelerated Portland cement (APC and calcium hydroxide Ca (OH2 may have the potential to promote the bone regeneration. However, certain clinical studies reveal consistency of Ca (OH2, as one of the practical drawbacks of the material when used alone. To overcome such inconvenience, the combination of the Ca (OH2 with a bone replacement material could offer a convenient solution. Objectives: To evaluate the soft tissue healing and bone regeneration in the periodontal intrabony osseous defects using accelerated Portland cement (APC in combination with calcium hydroxide Ca (OH2, as a filling material. Materials and Methods: Five healthy adult mongrel dogs aged 2-3 years old (approximately 20 kg in weight with intact dentition and healthy periodontium were selected for this study. Two one-wall defects in both mesial and distal aspects of the 3rd premolars of both sides of the mandible were created. Therefore, four defects were prepared in each dog. Three defects in each dog were randomly filled with one of the following materials: APC alone, APC mixed with Ca (OH2, and Ca (OH2 alone. The fourth defect was left empty (control. Upon clinical examination of the sutured sites, the amount of dehiscence from the adjacent tooth was measured after two and eight weeks, using a periodontal probe mesiodistally. For histometric analysis, the degree of new bone formation was estimated at the end of the eighth postoperative week, by a differential point-counting method. The percentage of the defect volume occupied by new osteoid or trabecular bone was recorded. Results: Measurement of wound dehiscence during the second week revealed that all five APCs had an exposure of 1-2 mm and at the end of the study all samples showed 3-4 mm exposure across the surface of the graft material, whereas the Ca (OH2, control, and APC + Ca (OH2 groups did not show any exposure at the end of the eighth week of the study. The most

  15. High-Strain-Rate behavior of Hydrated Cement Paste.

    Science.gov (United States)

    1987-01-29

    sample response under stress. It is now properly calibrated and fully operational. -24- VII. REFERENCES 1. S. Mindess and S.P. Shah (Eds.), "Cement-Based...Cem. Concr. Res., 3, 497 (1973). 8. B. Marchese, Cem. Concr. Res., 7, 9 (1977). 9. S. Mindess , in Proc. Eng. Sci. Found. Conf. 1979, Rindge, NH, p. 175, Eng. Foundation, New York (1980). -25- 51 I.M U Z &M__aw_./

  16. Clinical and Radiographic Evaluation of the Effectiveness of Formocresol, Mineral Trioxide Aggregate, Portland Cement, and Enamel Matrix Derivative in Primary Teeth Pulpotomies: A Two Year Follow-Up.

    Science.gov (United States)

    Yildirim, Ceren; Basak, Feridun; Akgun, Ozlem Marti; Polat, Gunseli Guven; Altun, Ceyhan

    2016-01-01

    The aim of this study was to evaluate and to compare clinical and radiographic outcomes of 4 materials (formocresol, mineral trioxide aggregate (MTA), Portland cement and enamel matrix derivative) using in primary teeth pulpotomies. Sixty-five patients aged 5-9 years (32 female, 33 male) were included in this study. A total of 140 primary first and second molars with deep caries were treated with pulpotomy. All teeth were then restored with stainless steel crowns. The treated teeth were evaluated clinically and radiographically at 3, 6, 12, 18 and 24 months. At 24 months, the clinical success rates of formocresol, MTA, Portland cement, and enamel matrix derivative were 96.9%, 100%, 93.9%, and 93.3%, respectively. The corresponding radiographic success rates were 84.4%, 93.9%, 86.7% and 78.1%, respectively. Although there were no statistically significant differences in clinical and radiographic success rates among the 4 groups, MTA appears to be superior to formocresol, Portland cement, and enamel matrix derivative as a pulpotomy agent in primary teeth.

  17. Contribution to the determination of gypsum and hemihydrates content in Portland cements

    Directory of Open Access Journals (Sweden)

    Moreno Arús, Fernando

    1975-09-01

    Full Text Available Not availableLa mayoría de los técnicos de cemento, aceptan, que las anormalidades del fraguado, conocidas como "falso fraguado" en el cemento portland, se deben primordialmente a la presencia de yeso parcialmente deshidratado (S04Ca1/2H20. Si el clínker que se muele está enriquecido en cal libre, o la temperatura del molino es elevada (superior a los 110 °C o hay escasa ventilación de éste, se llega a originar una parcial deshidratación del yeso, que se mantiene durante el proceso de ensilado y que origina las anormalidades del fraguado al que anteriormente nos hemos referido. Por esta razón creemos muy importante poder conocer el grado de deshidratación en que se encuentra el yeso en un cemento.

  18. Radon resistant potential of concrete manufactured using Ordinary Portland Cement blended with rice husk ash

    Science.gov (United States)

    Chauhan, R. P.; Kumar, Amit

    2013-12-01

    The emission of radon from building materials and soil depends upon the radium content, porosity, moisture content and radon diffusion length of materials. Several techniques have been used to reduce the radon emission from the soil using different flooring materials. But the effectiveness of radon shielding depends upon the diffusion of radon through these materials. The present study proposes a method for producing a radon resistant material for decreasing radon diffusion through it. The method involves rice husk ash (RHA) in addition to cement for the preparation of concrete used for flooring and walls. The radon diffusion, exhalation and mechanical property of concrete prepared by rice husk ash blended cement were studied. The addition of RHA caused the reduction in radon diffusion coefficient, exhalation rates, porosity and enhanced the compressive strength of concrete. The bulk radon diffusion coefficient of cementitious concrete was reduced upto 69% by addition of rice husk ash as compare to that of control concrete.

  19. CERAMIC WASTES AS RAW MATERIALS IN PORTLAND CEMENT CLINKER FABRICATION.· CHARACTERIZATION AND ALKALINE ACTIVATION

    OpenAIRE

    2006-01-01

    [EN] The world-wide cementindustry is seeking experimentalavenues that wi// lead to cementproduction that is less energy-intensive/ less damaging to the surrounding environment and less prolific in GHGemissions. In Spain andEurope in general, this approach is who//y consistent with the concept of sustainability and compliance with the Kyoto Protocol. The use ofdifferent kinds of industrial waste and by-products as alternative materials in cement manufacture has proved to ...

  20. Characterization of sugar cane bagasse ash as supplementary material for Portland cement

    OpenAIRE

    Janneth Torres Agredo; Ruby Mejía de Gutiérrez; Escandón Giraldo, Camilo E.; Luis Octavio González Salcedo

    2014-01-01

    Sugar Cane Bagasse is a by-product of the sugar agroindustry; it is partly used as fuel. However, bagasse ash (SCBA) is considered waste, which creates a disposal problem. Furthermore, if sugar cane bagasse is burned under controlled conditions, the SCBA can be potentially reused. This paper considers the technical viability of using SCBA as a partial replacement for cement. Two samples of SCBA from a Colombian sugar industry were characterized. The chemical composition of the samples shows h...

  1. Studies on the behaviour of different spent fluidized-bed catalytic cracking catalysts on Portland cement

    OpenAIRE

    J. PAYÁ; Borrachero, M. V.; Monzó, J.; Soriano, L.

    2009-01-01

    The fluidized-bed catalytic cracking catalyst (FCC) it is a residue from the industry of the petroleum that shows a high pozzolanic reactivity and, in cementing matrix, it significantly improves their mechanical behaviour as well as durability. In this research a comparative study on residues of catalyst from different sources has been carried out, in order to know if these residues can be used jointly in an indiscriminate way or, on the contrary, it is necessary to classify them according to...

  2. Effect of various Portland cement paste compositions on early-age strain

    Science.gov (United States)

    Guzzetta, Alana G.

    Early-age strain in paste, mortar, and concrete mixtures was investigated using a new method where the specimen shape was a cone frustum. Strain of the specimen from both the horizontal and vertical directions was captured by height change measurement. The volumetric strain was then calculated as a function of the height change and was plotted versus time. A correlation was found between the slopes of the volumetric strain curve resulting from this test method and the initial setting time of the tested material. An initial evaluation of the repeatability of this innovative test method was conducted. The early-age strain effects of aggregate volume, shrinkage reducing admixture, water-cementitious ratio (w/cm), and partial cement replacement with supplementary cementitious materials were tested and individually compared. From these comparisons, it was observed that ambient temperature, bleed water development, and rheological properties had a significant impact on the volumetric strain results. Data showed increased strain as aggregate volume was reduced and as the w/cm was changed from 0.25 up to 0.50. The addition of shrinkage reducing admixture generally caused an increase in the 36-hour volumetric strain value. In most of the mixtures, cement replacement with 20% fly ash or 10% metakaolin reduced the measured volumetric strain when the w/cm was 0.30. Replacement of cement with 10% silica fume caused an insignificant change in volumetric strain results.

  3. Characterization of sugar cane bagasse ash as supplementary material for Portland cement

    Directory of Open Access Journals (Sweden)

    Janneth Torres Agredo

    2014-03-01

    Full Text Available Sugar Cane Bagasse is a by-product of the sugar agroindustry; it is partly used as fuel. However, bagasse ash (SCBA is considered waste, which creates a disposal problem. Furthermore, if sugar cane bagasse is burned under controlled conditions, the SCBA can be potentially reused. This paper considers the technical viability of using SCBA as a partial replacement for cement. Two samples of SCBA from a Colombian sugar industry were characterized. The chemical composition of the samples shows high percentages of silica, 76.3% and 63.2%. The mineralogical and morphological characteristics of the waste were determined by X-ray diffraction patterns (XRD, thermal analysis (TG/DTA and scanning electron microscopy (SEM. The pozzolanic activity of SCBA was evaluated using the Frattini test and the strength activity index test (SAI. The ASTM C618 defines an SAI of at least 75% as a requirement for classifying material as a pozzolan. This condition was achieved in the experiments performed. The results indicate that SCBA produced in the manufacture of commercial cements can be recycled for use as pozzolanic material. This supplementary material can partially replace cement and therefore reduce CO2 emissions.

  4. Portland cement with additives in the repair of furcation perforations in dogs Cimento Portland com aditivos na reparação de perfurações radiculares em cães

    Directory of Open Access Journals (Sweden)

    José Dias da Silva Neto

    2012-11-01

    Full Text Available PURPOSE: To evaluate the use of Portland cements with additives as furcation perforation repair materials and assess their biocompatibility. METHODS: The four maxillary and mandibular premolars of ten male mongrel dogs (1-1.5 years old, weighing 10-15 kg received endodontic treatment (n=80 teeth. The furcations were perforated with a round diamond bur (1016 HL. The perforations involved the dentin, cementum, periodontal ligament, and alveolar bone. A calcium sulfate barrier was placed into the perforated bone to prevent extrusion of obturation material into the periradicular space. The obturation materials MTA (control, white, Type II, and Type V Portland cements were randomly allocated to the teeth. Treated teeth were restored with composite resin. After 120 days, the animals were sacrificed and samples containing the teeth were collected and prepared for histological analysis. RESULTS: There were no significant differences in the amount of newly formed bone between teeth treated with the different obturation materials (p=0.879. CONCLUSION: Biomineralization occurred for all obturation materials tested, suggesting that these materials have similar biocompatibility.OBJETIVO: Avaliar o uso de cimentos Portland aditivados na reparação de perfurações radiculares e a biocompatibilidade destes materiais. MÉTODOS: Oitenta pré-molares, quatro da arcada dentária superior e quatro da arcada inferior de 10 cães machos, sem raça definida, com idade em torno de um a um ano e meio, pesando entre 10 e 15 kg foram submetidos a tratamento endodôntico, sendo realizadas perfurações nas furcas com broca de diamante 1016 HL. A cavidade envolveu dentina e cemento, como também periodonto e o osso alveolar. Na porção óssea da obturação, barreira de sulfato de cálcio foi utilizada evitando extravasamento do cimento para o espaço periodontal. Foi realizada a distribuição randomizada dos cimentos MTA (controle, Portland tipo II, Portland tipo V e

  5. Effect of high doses of chemical admixtures on the strength development and freeze-thaw durability of portland cement mortar

    Science.gov (United States)

    Korhonen, Charles J.

    This thesis examines the low-temperature strength development of portland cement concrete made with high doses of chemical admixtures dissolved in the mixing water and the possible beneficial effect of these admixtures on that concrete's long-term freeze-thaw durability. The literature shows that high doses of chemical admixtures can protect fresh concrete against freezing and that, under certain conditions, these admixtures can enhance the freeze-thaw durability of concrete. The challenge is that there are no acceptance standards in the U.S. that allow chemicals to be used to protect concrete against freezing. Also, the perception is that chemicals might somehow harm the concrete. This perception seems to be based on the fact that deicing salts, when applied to concrete pavement, cause roadways to scale away. This study investigated the effect of high doses of commercially available admixtures on fresh concrete while it gained strength at low temperature and on hardened concrete exposed to repeated cycles of freezing and thawing in a moist environment. The reason for studying off-the-shelf admixtures was that these materials are approved for use in concrete; they were already governed by their own set of standards. Four mortars were examined, each with a different cement and water content, when dosed with five commercial admixtures. This allowed the fresh mortar to gain appreciable strength when it was kept at nearly -10C. The admixtures also enhanced the freeze-thaw durability of the mortar, even when it was not air-entrained. Clearly, as the dosage of admixture increased beyond approximately 22% by weight of water, the mortar appeared to be unaffected by up to 700 cycles of freezing and thawing.

  6. Evaluation of Photocatalytic Properties of Portland Cement Blended with Titanium Oxynitride (TiO2−xNy Nanoparticles

    Directory of Open Access Journals (Sweden)

    Juan D. Cohen

    2015-07-01

    Full Text Available Photocatalytic activity of Portland cement pastes blended with nanoparticles of titanium oxynitride (TiO2−xNy was studied. Samples with different percentages of TiO2−xNy (0.0%, 0.5%, 1%, 3% and TiO2 (1%, 3% were evaluated in order to study their self-cleaning properties. The presence of nitrogen in the tetragonal structure of TiO2 was evidenced by X-ray diffraction (XRD as a shift of the peaks in the 2θ axis. The samples were prepared with a water/cement ratio of 0.5 and a concentration of Rhodamine B of 0.5 g/L. After 65 h of curing time, the samples were irradiated with UV lamps to evaluate the reduction of the pigment. The color analysis was carried out using a Spectrometer UV/Vis measuring the coordinates CIE (Commission Internationale de l’Eclairage L*, a*, b*, and with special attention to the reddish tones (Rhodamine B color which correspond to a* values greater than zero. Additionally, samples with 0.5%, 1%, 3% of TiO2−xNy and 1%, 3% of TiO2 were evaluated under visible light with the purpose of determining the Rhodamine B abatement to wavelengths greater than 400 nm. The results have shown a similar behavior for both additions under UV light irradiation, with 3% being the addition with the highest photocatalytic efficiency obtained. However, TiO2−xNy showed activity under irradiation with visible light, unlike TiO2, which can only be activated under UV light.

  7. Hydration of tricalcium silicate in blended Cements manufactured with cuban tuffs

    Directory of Open Access Journals (Sweden)

    Duque Fernández, Gabriel Luis

    1989-03-01

    Full Text Available The tricalcium silicate (alite hydration velocity in cements with and without additives is studied in the presence of "Las Carolinas" quarry tuffs from Cienfuegos province, Cuba, the alite hydration velocity is enhanced reaching velocity constants 1.5 higher than in the standard cement.

    Se estudia la velocidad de hidratación del silicato tricálcico (alita presente en el cemento con y sin adiciones, demostrándose que en presencia de tobas del yacimiento "Las Carolinas" en la provincia de Cienfuegos, Cuba, se acelera la velocidad de hidratación de este componente, obteniéndose constantes de velocidad de reacción aproximadamente 1,5 veces mayores que en el cemento patrón.

  8. Behavior of multi-walled carbon nanotubes on the porosity and microstructure of cement-based materials

    Science.gov (United States)

    Nochaiya, Thanongsak; Chaipanich, Arnon

    2011-01-01

    The porosity and microstructure of a Portland cement-multi-walled carbon nanotube composite were investigated. Multi-walled carbon nanotubes (CNTs), up to 1 wt.% of cement, synthesized by infusion chemical vapor deposition, and Portland cement type I (PC) were used to produce pastes with a water to cement ratio of 0.5. Mercury intrusion porosimetry (MIP) and scanning electron microscopy (SEM) were used to characterize Portland cement-CNTs systems. MIP analysis of the results indicates that total porosity of the mixes with CNTs was found to decrease with increasing CNTs content. Moreover, an important effect of additional CNTs was a reduction in the number of mesopores, while SEM technique showed dispersion of CNTs between the hydration phases of Portland cement pastes.

  9. Cement hydration from hours to centuries controlled by diffusion through barrier shells of C-S-H

    Science.gov (United States)

    Rahimi-Aghdam, Saeed; Bažant, Zdeněk P.; Abdolhosseini Qomi, M. J.

    2017-02-01

    Although a few good models for cement hydration exist, they have some limitations. Some do not take into account the complete range of variation of pore relative humidity and temperature, and apply over durations limited from up a few months to up to about a year. The ones that are applicable for long durations are either computationally too intensive for use in finite element programs or predict the hydration to terminate after few months. However, recent tests of autogenous shrinkage and swelling in water imply that the hydration may continue, at decaying rate, for decades, provided that a not too low relative pore humidity (above 0.7) persists for a long time, as expected for the cores of thick concrete structural members. Therefore, and because design lifetimes of over hundred years are required for large concrete structures, a new hydration model for a hundred year lifespan and beyond is developed. The new model considers that, after the first day of hydration, the remnants of anhydrous cement grains, gradually consumed by hydration, are enveloped by contiguous, gradually thickening, spherical barrier shells of calcium-silicate hydrate (C-S-H). The hydration progress is controlled by transport of water from capillary pores through the barrier shells toward the interface with anhydrous cement. The transport is driven by a difference of humidity, defined by equivalence with the difference in chemical potential of water. Although, during the period of 4-24 h, the C-S-H forms discontinuous nano-globules around the cement grain, an equivalent barrier shell control was formulated for this period, too, for ease and effectiveness of calculation. The entire model is calibrated and validated by published test data on the evolution of hydration degree for various cement types, particle size distributions, water-cement ratios and temperatures. Computationally, this model is sufficiently effective for calculating the evolution of hydration degree (or aging) at every

  10. Comparison of the sealing ability of mineral trioxide aggregate and Portland cement used as root-end filling materials.

    Science.gov (United States)

    Shahi, Shahriar; Yavari, Hamid R; Rahimi, Saeed; Eskandarinezhad, Mahsa; Shakouei, Sahar; Unchi, Mahsa

    2011-12-01

    Inadequate apical seal is the major cause of surgical endodontic failure. The root-end filling material used should prevent egress of potential contaminants into periapical tissue. The purpose of this study was to compare the sealing ability of four root-end filling materials: white mineral trioxide aggregate (MTA), gray MTA, white Portland cement (PC) and gray PC by dye leakage test. Ninety-six human single-rooted teeth were instrumented, and obturated with gutta-percha. After resecting the apex, an apical cavity was prepared. The teeth were randomly divided into four experimental groups (A: white MTA, B: gray MTA, C: white PC and D: gray PC; n = 20) and two control groups (positive and negative control groups; n = 8). Root-end cavities in the experimental groups were filled with the experimental materials. The teeth were exposed to Indian ink for 72 hours. The extent of dye penetration was measured with a stereomicroscope at 16× magnification. The negative controls showed no dye penetration and dye penetration was seen in the entire root-end cavity of positive controls. However, there was no statistically significant difference among the four experimental groups (P > 0.05). All retrograde filling materials tested in this study showed the same microleakage in vitro. Given the low cost and apparently similar sealing ability of PC, PC could be considered as a substitute for MTA as a root-end filling material.

  11. An investigation on the use of tincal ore waste, fly ash, and coal bottom ash as Portland cement replacement materials

    Energy Technology Data Exchange (ETDEWEB)

    Kula, I.; Olgun, A.; Sevinc, V.; Erdogan, Y. [Dumlupinar University, Kutahya (Turkey). Dept. of Chemistry

    2002-02-01

    The possibility of using tincal ore waste (TW), coal bottom ash (BA), and fly ash (FA) as partial replacement in concrete was examined through a number of tests. The properties examined include setting time, compressive strength, mortar expansion, water consistency of mortar, and microstructure. The results showed that compressive strength of all specimens containing 1 wt.% of TW was higher than that of the control at the 28th day of curing. At 90 days, the contribution to strength by BA + TW and FA + TW was higher than in the concrete-prepared equivalent TW beyond 3 wt.% of Portland cement (PC) replacement. With the replacement of 3-5 wt.% of PC by TW, the compressive strength of the concrete decreased compared to control concrete. However, the values obtained are within the limit of Turkish Standards. Adding BA or FA with TW improved the performance relative to TW replacement only. Increasing replacement of TW gives rise to a higher setting time. As a result. TW, BA, and FA samples may be used as cementitious materials.

  12. A comparative evaluation of ProRoot mineral trioxide aggregate and Portland cement as a pulpotomy medicament

    Directory of Open Access Journals (Sweden)

    Dipti Bhagat

    2016-01-01

    Full Text Available Introduction: Recently, some studies have compared mineral trioxide aggregate (MTA with portland cement (PC, concluding that the principle ingredients of PC are similar to those of MTA. The purpose of the present study was to evaluate the biocompatibility of PC as a pulpotomy medicament. Materials and Methods: Thirty premolars that scheduled for extraction for therapeutic reasons were randomly assigned to two experimental groups: ProRoot MTA (PMTA and PC. After isolation and pulp exposure, pulpotomy was carried out and pulps were dressed with PMTA and PC. After 6 months, the teeth were extracted and prepared for histological analysis based on Cox et al. criteria. The data were analyzed by Z-test of proportion with 1% of allowed error. Results: No statistically significant difference was found between the two groups with respect to inflammatory response, soft tissue organization, and dentine bridge formation (P > 0.05. Conclusions: PC was associated with similar favorable biological response to pulpotomy treatment as PMTA. The findings of this study support the idea that PC can be considered a cheaper substitute to MTA.

  13. Thermal Stability of Certain Hydrated Phases in Systems Made Using Portland Cement.

    Science.gov (United States)

    1985-08-01

    underlying it (Lea 1971, pp 397-398; Smith 1978, Mindess and Young 1981, p 530; Carette et al 1982), consequently it will not be dealt with further here as it...34Stability of Ettringite on Heating," Jan 1972, Journal of the * American Ceramic Society, Vol 55, pp 55-56. Mindess , Sidney and J. Francis Young

  14. Analyses of microstructural properties of VA/VeoVA copolymer modified cement pastes

    Directory of Open Access Journals (Sweden)

    Carlos Eduardo M. Gomes

    2005-07-01

    Full Text Available Recently, modern techniques have been applied for analysis of the influence of polymers on microstructural properties of Portland cement, such as Thermogravimetric Analyses (TG, Scanning Electronic Microscopy (SEM, Fourier Transform Infrared Spectroscopy (FT-IR and Mercury Intrusion Porosimetry (MIP. In this study, thermogravimetric analyses were used to study the influence of vinyl acetate-versatic vinylester copolymer (VA/VeoVA in seven pastes of 28-day old Portland cement, in which distinct polymer contents and water/cement ratios were employed. In addition, analyses of FT-IR and MIP on Portland cement pastes modified by the copolymer were employed. The results showed that the addition of polymer interferes significantly in the reduction of Portlandite formation and increases the porosity of the matrices. A possible chemical interaction between the copolymer and hydrated products of Portland cement was also observed.

  15. Evaluation of the Apical Sealability of Mineral Trioxide Aggregate and Portland Cement as Root Canal Filling Cements: An in Vitro Study

    Directory of Open Access Journals (Sweden)

    M.S. Rekab

    2010-12-01

    Full Text Available Objective: One of the principle purposes of root canal obturation is to obtain hermetic sealing of the root canal system. According to the development of technology, many materials are now used in root canal filling. An in vitro dye leakage study was performed toevaluate the apical sealability of White-colored Mineral Trioxide Aggregate (WMTA and Gray-colored Portland Cement (GPC when used alone or as a sealer with gutta-percha points in root canal filling.Materials and Methods: Seventy-five single-rooted extracted human teeth were used in this study. After cleaning and shaping, the teeth were randomly divided into five equal groups of 15 teeth each based on the root canal filling material used; Group 1, (WMTAalone; Group 2, (GPC alone; Group 3, (Gutta-percha points + WMTA; Group 4,(Guttapercha points + GPC; Group 5, (Gutta-percha points + AH26. Methylene blue was used to determine the apical leakage. After sectioning the teeth longitudinally, linear dye penetrationwas measured with a caliper under the stereomicroscope. Data were analyzed by Kruskal-Wallis and one-way ANOVA tests with (P 0.05 as the level of significance.Results: The results showed that there were no statistically significant differences among the materials of five groups.Conclusion: (WMTA alone, (Gutta-percha points + WMTA, (GPC alone and (Guttapercha points + GPC may be used in the root canal filling.

  16. 砒砂岩对硅酸盐和硫铝酸盐水泥性能的影响%Impact of feldspathic stone on performance of Portland cement and sulphoaluminate cement

    Institute of Scientific and Technical Information of China (English)

    张云; 汪自庆; 何欢; 张雪冰; 申卫博

    2016-01-01

    The one-single and multi-level gradient test were selected to investigate the influence of feldspathic stone on the physical properties of Portland cement and sulphoaluminate cement,with the comparison of different feldspathic stone substitution,setting time,standard consistency water consumption and mechanical performance of Portland cement and sulphoaluminate cement were tested.The results show that the certain amount of feldspathic stone shortens the setting time of Portland cement and sulphoaluminate cement.The initial setting time of Portland cement and sulphoaluminate cement are shortened by 30% and 47%,and the water requirement for normal consistency of Portland cement and sulphoaluminate cement are increased by 6.6% and 21.7%,separately,when the substitution of feldspathic stone powders is 5%.Mechanical performance of Portland cement is positive with 10% mass fraction substitution of feldspathic stone,and the compressive strength of 3 d and 28 d are increased by 7.2% and 6%,respectively.The compressive strength of sulphoaluminate cement is decreased with the increasing of feldspathic stone.%为了研究砒砂岩对硅酸盐水泥和硫铝酸盐水泥物理性能的影响,采用单因素多水平梯度实验,通过不同砒砂岩掺量的对比,测定硅酸盐水泥和硫铝酸盐水泥的凝结时间、标准稠度用水量和胶砂强度等性能.结果表明:砒砂岩对硅酸盐水泥和硫铝酸盐水泥皆有促凝作用,当砒砂岩掺量质量分数为5%时硅酸盐水泥的初凝时间会缩短30%,硫铝酸盐水泥初凝时间缩短47%,硅酸盐水泥和硫铝酸盐水泥的标准稠度用水量分别增加6.6%和21.7%;砒砂岩掺量质量分数为10%时,硅酸盐水泥的3d和28 d的强度分别增加7.2%和6%,对其力学性能有较大影响;掺入砒砂岩后,硫铝酸盐水泥强度降低,且随掺量增加,抗压强度降幅增大.

  17. Avaliação preliminar do emprego de arenito zeolítico da região nordeste do Brasil como material pozolânico para cimento Portland Preliminary evaluation of sandstones from northeastern Brazil with pozzolanic properties for Portland cement

    Directory of Open Access Journals (Sweden)

    M. S. Picanço

    2011-12-01

    experimental study was mainly based on mineralogical characterization, including: X-ray diffraction (XRD, chemical analysis and heat flow calorimetry, besides pozzolanic activity assay and compressive strength. The results show that the mineralogical composition of the zeolitic sandstone is mainly quartz, zeolite (stilbite and smectite. Stilbite is the main pozzolanic phase, and the smectite can also play an important role. The hydration of the Portland cement was accelerated due to the very fine grained nature of the material. Meanwhile, the reactivity obtained was slightly below the standard requirements to be used in industrial scale. Additional studies should be carried out in order to evaluate if a further thermal treatment (between 300 °C and 500 °C may increase the pozzolanic activity due to the stilbite destruction around this temperature. The same happens with kaolinite that needs thermal treatment above 550 ºC to convert to the amorphous phase metakaolin in order to be used as one of the most commons pozzolans in the cement industry. The main purpose was to contribute for the production of an alternative kind of cement which produces less pollution to the environment (CO2 decrease in the atmosphere with cost saving. In addition, it is expected to contribute for the exploitation of the sedimentary zeolites occurrences which have been relatively well studied from a geological point, but are still not mined.

  18. Effect of poly car boxy late admixtures on portland cement paste setting and rheological behaviour

    Directory of Open Access Journals (Sweden)

    Puertas, F.

    2005-03-01

    Full Text Available The objective of the work was to determine the effects of polycarboxilated-type admixture on the setting times and the rheological properties of different types of cements including CEM I 42.5 R, CEM Il/B-V 42.5 N and CEM III/B 32.5 N, defined according to the UNE EN 197-1:2000 standard. The results show that there is a lineal relationship between the initial setting times and the admixture dosage. Mathematical equations that model this behaviour for each of the cements have been determined. The data obtained from the minislump test and from the rheological parameters determined using the rheometer (plastic viscosity and yield stress point to similar conclusions. It was also verified that the workability effect of the polycarboxilate admixture is most intense for blended cements.

    El objetivo de este trabajo ha sido estudiar el efecto de la dosificación de un aditivo basado en policarboxilatos sobre el inicio de tiempo de fraguado y las propiedades reo lógicas en pastas de diferentes tipos de cemento (CEM 142.5 R, CEM 11/ B-V42.5 NYCEMIII/B 32.5 N-Norma EN 197-1:2000. existe una relación lineal entre el inicio del fraguado y la dosificación del aditivo, se han determinado las ecuaciones matemáticas que describen este comportamiento para cada cemento, los resultados obtenidos sobre la fluidez de la pasta en el ensayo del "minislump" coinciden con la evolución de los valores de los parámetros reológicos (esfuerzo de cizalladura y viscosidad plástica determinados a través de un reómetro. el efecto fluidificante del aditivo superplastificante basado en policarboxilatos es mucho más marcado en cementos que contienen adiciones.

  19. SUGARCANE BAGASSE ASH AS A PARTIAL-PORTLAND-CEMENT-REPLACEMENT MATERIAL

    Directory of Open Access Journals (Sweden)

    MARCOS OLIVEIRA DE PAULA

    2010-01-01

    Full Text Available Esta investigación se centra en la evaluación de los efectos de la sustitución parcial del cemento Portland por cenizas de bagazo de caña de azúcar (CBC en morteros. El objetivo principal fue encontrar un uso adecuado para este residuo agrícola que es generado en una cantidad cada vez mayor en Brasil, ya que el uso de CBC como un mineral mezclado en morteros y concretos, contribuye a disminuir el impacto ambiental de estos materiales relacionados con la producción de cemento. Técnicas experimentales fueron aplicadas tanto para la caracterización del CBC, como para la evaluación de su uso como una mezcla de minerales en los morteros, basados en pruebas físicas y mecánicas. Los resultados de las pruebas con morteros indicaron la viabilidad de la sustitución parcial del cemento por CBC, hasta en un 20%.

  20. Freeze-Thaw Performance and Moisture-Induced Damage Resistance of Base Course Stabilized with Slow Setting Bitumen Emulsion-Portland Cement Additives

    Directory of Open Access Journals (Sweden)

    Mojtaba Shojaei Baghini

    2015-01-01

    Full Text Available Freeze-thaw (FT cycles and moisture susceptibility are important factors influencing the geotechnical characteristics of soil-aggregates. Given the lack of published information on the behavior of cement-bitumen emulsion-treated base (CBETB under environmental conditions, especially freezing and thawing, this study investigated the effects of these additives on the CBETB performance. The primary goal was to evaluate the resistance of CBETB to moisture damage by performing FT, Marshall conditioning, and AASHTO T-283 tests and to evaluate the long-term stripping susceptibility of CBETB while also predicting the liquid antistripping additives to assess the mixture’s durability and workability. Specimens were stabilized with Portland cement (0%–6%, bitumen emulsion (0%–5%, and Portland cement-bitumen emulsion mixtures and cured for 7 days, and their short- and long-term performances were studied. Evaluation results of both the Marshall stability ratio and the tensile strength ratio show that the additions of additives increase the resistance of the mixtures to moisture damage. Results of durability tests performed for determining the resistance of compacted specimens to repeated FT cycles indicate that the specimen with the 4% cement-3% bitumen emulsion mixture significantly improves water absorption, volume changes, and weight losses. This indicates the effectiveness of this additive as a road base stabilizer with excellent engineering properties for cold regions.

  1. HYDRATION CHARACTERISTICS OF PROMPT CEMENT IN THE PRESENCE CITRIC ACID AS RETARDER

    Directory of Open Access Journals (Sweden)

    Mohamed Heikal

    2015-03-01

    Full Text Available The aim of the present work is to study the influence of citric acid (CA as retarder on the properties of prompt cement pastes. The dosages of CA were 0.50, and 0.75, 1.00 and 1.25 mass % of prompt cement. The initial and final setting times, bulk density, compressive strength, total porosity, and hydration kinetics such as free lime, combined water contents and XRD for selected sample were investigated. The results obtained in this study showed that the addition of CA elongates the initial and final setting times and decreases the compressive strength and combined water contents, whereas, it increases the total porosity at all ages of hydration. CA retards the liberation of Ca(OH2 of prompt pastes. The free lime contents of prompt cement pastes are slightly increased up to 28 days then sharply increased up to 90 days. Thus, it is suggested that citrate sorbed onto the clinker surface and formed a protective layer around the clinker grains retarding their dissolution. The sharp increase of compressive strength at later ages after 28 days up to 90 days. The presence of 0.75 mass % citric acid achieves the initial and final setting time of the prompt cement according to the ASTM specification.

  2. Microstructure and its relationship to fracture in portland cement mortar and concrete

    Science.gov (United States)

    Abell, Anne Bernadine

    This research explores the relationship between the geometry of crack propagation and mechanical properties of mortar and concrete. The crack deflection and branching are measured using several microscopy techniques along with image analysis of crack profiles intruded by a low melting-point alloy. The toughness measured by mechanical testing, the fracture surface geometry, phases and elastic properties identified by image analysis and microscopy, along with the crack branching relationships are used to predict the increase in the toughness of these materials with respect to the flat-crack toughness using a micromechanical model. The effect of the model parameters, microscopy techniques, material elastic properties, void modeling and branching ratio were investigated. The parametric analysis and modeling conditions determine a nearly uniform flat-crack toughness for the cement matrix of the mortar samples and a higher flat-wrack toughness for the cement matrix of the concrete samples. The trend toward a single toughness value may be an indication that there is a single material parameter to describe the fracture energy of these materials.

  3. Biofouling e biodeterioração química de argamassa de cimento portland em reservatório de usina hidroelétrica Biofouling and chemical biodeterioration in hydroeletric power plant portland cement mortar

    Directory of Open Access Journals (Sweden)

    Kleber Franke Portella

    2009-01-01

    Full Text Available Last decade Brazilian rivers experimented progressive biofouling of Limnoperna fortunei communities and Cordylophora caspia hydroids. The microhabitat is so favorable that in around 1.5 years L. fortunei increased from 0.39 to nearby 149,000 units/m². Ten Portland cement mortar samples were produced with 1: 3.5: 0.4 dosages and installed for 1 year at Salto Caxias Brazilian Power Plant reservoir in 0.5 m and 1.0 m deep to investigate the biofouling influence on hydraulic civil structures. SEM, EDS, visual investigation and XRF results indicate none direct chemical interrelationships between L. fortunei and the mortar samples. However C. caspia diminished the mortar surface resistance and caused cement paste leaching.

  4. Laser-radiation scattering by cement in the process of hydration: simulation of the dynamics and experiment.

    Science.gov (United States)

    Gorsky, M P; Maksimyak, P P; Maksimyak, A P

    2012-04-01

    This paper discusses simulation of speckle-field dynamics during coherent light scattering by a cement surface in the process of hydration. Cement particles are represented by the spheres whose sizes and reflection indices are changing during the hydration process. The study of intensity fluctuations of scattered coherent radiation is a suitable technique for the analysis of both fast and slow processes of mineral binder hydration and formation of polycrystalline structures in the process of hardening. The results of simulation are in good agreement with the experimental data.

  5. Energetically Modified Cement (EMC) - Performance Mechanism

    Energy Technology Data Exchange (ETDEWEB)

    Ronin, Vladimir; Elfgren, Lennart [Luleaa Univ. of Technology (Sweden). Centre for High Performance Cement

    2003-03-01

    Energetically Modified Cements, EMC, made of intensively milled cement (50%) and fillers (50%) of quartz or fly ash have been compared to blends of Ordinary Portland Cement, OPC, and fillers. The EMCs have better properties than other blends and are comparable to unblended OPC. This remarkable fact can probably be explained as follows. The grinding process reduces the size of both cement grains and fillers. This combined with the creation of micro defects gives the ground cement a very high degree of hydration. The increased early hydration and a better distribution of hydration products results in an extensive pore size refinement of the hardened binder. This pore size refinement leads to a favorably reduced permeability and diffusivity and very good mechanical properties.

  6. Energetically Modified Cement (EMC) - Performance Mechanism

    Energy Technology Data Exchange (ETDEWEB)

    Ronin, Vladimir; Elfgren, Lennart [Luleaa Univ. of Technology (Sweden). Centre for High Performance Cement

    2003-03-01

    Energetically Modified Cements, EMC, made of intensively milled cement (50%) and fillers (50%) of quartz or fly ash have been compared to blends of Ordinary Portland Cement, OPC, and fillers. The EMCs have better properties than other blends and are comparable to unblended OPC. This remarkable fact can probably be explained as follows. The grinding process reduces the size of both cement grains and fillers. This combined with the creation of micro defects gives the ground cement a very high degree of hydration. The increased early hydration and a better distribution of hydration products results in an extensive pore size refinement of the hardened binder. This pore size refinement leads to a favorably reduced permeability and diffusivity and very good mechanical properties.

  7. Corrosion inhibitors for mild steel; stannous tin (SnII) in ordinary portland cement

    Energy Technology Data Exchange (ETDEWEB)

    Sagoe-Crentsil, K.K.; Glasser, F.P.; Yilmaz, V.T. (Univ. of Aberdeen (United Kingdom). Dept. of Chemistry)

    1994-01-01

    Salts containing divalent tin (SnII) are shown to give a measure of corrosion protection to mild steel embedded in cement paste. Results of linear polarization measurements are shown for samples cured at 40[degree] for up to 240 days in pastes containing initially 0-1628mM/l chloride: Sn[sup 2+], but not Sn[sup 4+], is an effective inhibitor at an initial concentration of 200mM/l. However tin solubility in pore fluid is very low: less than 0.01mM/l at 60d. It is speculated that tin stabilizes the passivating layers although no direct evidence for the incorporation of tin in corrosion product was found by analytical electron microscopy. Other theories of inhibition are discussed.

  8. Effects of glass fiber modified with calcium silicate hydrate (C-S-H(I)) reinforced cement

    Science.gov (United States)

    Xin, M.; Zhang, L.; Ge, S.; Cheng, X.

    2017-03-01

    In this paper, calcium silicate hydrate (C-S-H(I)) and glass fiber modified with C-S-H(I) (SiF) at ambient temperature were synthesized. SiF and untreated fiber (OF) were incorporated into cement paste. Phase composition of C-S-H(I), SiF and OF was characterized by XRD. The surface morphologies were characterized by SEM. Flexural performance of fiber reinforced cement (FRC) at different curing ages was investigated. Results indicated that both SiF and OF could reinforce cement paste. SiF had a more positive effect on improving the flexural performance of FRC than OF. The strength of SiF reinforced cement was 11.48MPa after 28 days curing when fiber volume was 1.0%, 12.55% higher than that of OF reinforced cement. The flexural strength increased with the addition of fiber volume. However, the large dosage of fiber might cause a decrease in flexural strength of FRC.

  9. Computation of X-ray powder diffractograms of cement components and its application to phase analysis and hydration performance of OPC cement

    Indian Academy of Sciences (India)

    Rohan Jadhav; N C Debnath

    2011-08-01

    The importance of computed X-ray diffraction patterns of various polymorphs of alite (3, 1, ), belite (, ), aluminate (cubic, orthorhombic), aluminoferrite, gypsum and hemihydrate in the quantitative phase analysis of cement and its early stage hydration performance is highlighted in this work with three OPC samples. The analysis shows that the predominant silicate phases present in all the samples are 3-alite phase and -belite phase, respectively. Both cubic and orthorhombic phases of C3A, brownmillerite, gypsum and hemihydrates are present at different levels. Quantitative phase analysis of cement by Rietveld refinement method provides more accurate and comprehensive data of the phase composition compared to Bogue method. The comparative hydration performance of these samples was studied with / ratio, 0.5 and the results are interpreted in the light of difference in phase compositions viz. -C2S/C3S ratio, fraction of finer cement particles present in the samples and theoretical modeling of C3S hydration.

  10. Influence of CO2 Laser Radiation on the Mechanical Properties of Portland Cement Pastes

    Directory of Open Access Journals (Sweden)

    González-Mota, R.

    2011-03-01

    Full Text Available This article presents the results of the treatment of fresh cement pastes with CO2 laser radiation (10.6μm, in order to improve its mechanical properties in addition to obtaining lower setting times than those of a natural setting (without radiation . It was observed that the CO2 laser radiation has a positive influence on the mechanical properties of cement paste, not due to the heat produced during irradiation, but due to the effect of electric field propagation on water molecules, whose are arranged around functional groups of the binder and by the effect of ration, causes a micro vibration effect, resulting in a more compact and less porous paste which has better mechanical properties compared to natural setting paste. The internal and surface temperature of the samples, the evolution of setting, Young's modulus (using ultrasonic pulse velocity and compressive strength were registered.En este artículo se presentan los resultados correspondientes al tratamiento de pastas frescas de cemento con radiación láser de CO2 (10.6µm, con el propósito de mejorar sus propiedades mecánicas además de obtener tiempos de fraguado menores a los del fraguado en forma natural (sin radiación. Se demostró que la radiación con láser de CO2 influye positivamente en las propiedades mecánicas de la pasta de cemento, no por el calentamiento producido durante la irradiación, sino por el efecto de la propagación del campo eléctrico sobre las moléculas de agua que están dispuestas alrededor de los grupos funcionales del aglutinante y que al rotar producen un efecto equivalente a micro vibraciones, dando como resultado un material más compacto, con menos poros y mejores propiedades mecánicas respecto al fraguado natural. Se registró la temperatura interna y superficial de las muestras, la evolución del fraguado, el módulo de Young y la resistencia a compresión.

  11. Potential use of natural red mud as pozzolan for Portland cement

    Directory of Open Access Journals (Sweden)

    Daniel Véras Ribeiro

    2011-03-01

    Full Text Available Red mud, the main waste generated in aluminum and alumina production by the Bayer process, is considered hazardous due to its high pH, according to the Brazilian standard NBR 10004/2004, and worldwide generation of this waste exceeds 117 million tons/year. In this work, non-calcined red mud was used, thus requiring less energy and time and reducing costs, which is the ideal condition for reusing wastes. Mortars containing 30 wt. (% of cement substituted by red mud showed higher strength of hardened products. The pozzolanic activity index was evaluated based on physical and mechanical parameters (Brazilian NBR 5751 and NBR 5752 standards and on a chemical analysis (European EN 196-5 standard. A comparison of the reference mixture (without red mud and the results obtained with red mud confirm the potential of non-calcined red mud for use a as pozzolanic additive in cementitious materials. The setting time (according to the MERCOSUL NM 65 standard tends to increase but workability remains almost unchanged.

  12. Early-age acoustic emission measurements in hydrating cement paste: Evidence for cavitation during solidification due to self-desiccation

    DEFF Research Database (Denmark)

    Lura, Pietro; Couch, J.; Jensen, Ole Mejlhede

    2009-01-01

    In this study, the acoustic emission activity of cement pastes was investigated during the first day of hydration. Deaired, fresh cement pastes were cast in sealed sample holders designed to minimize friction and restraint. The majority of acoustic emission events occurred in lower water to cement....... According to these experimental results, the acoustic emission measured around setting time was attributed to cavitation events occurring in the pores of the cement paste due to self-desiccation. This paper shows how acoustic emission might be used to indicate the time when the fluid–solid transition occurs...

  13. Formation of magnesium silicate hydrate (M-S-H) cement pastes using sodium hexametaphosphate

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Tingting [Faculty of Infrastructure Engineering, Dalian University of Technology, Dalian 116024 (China); Department of Materials, Centre for Advanced Structural Ceramics, Imperial College London, South Kensington Campus, London SW7 2AZ (United Kingdom); Department of Civil and Environmental Engineering, Imperial College London, South Kensington Campus, London SW7 2AZ (United Kingdom); Vandeperre, Luc J. [Department of Materials, Centre for Advanced Structural Ceramics, Imperial College London, South Kensington Campus, London SW7 2AZ (United Kingdom); Cheeseman, Christopher R., E-mail: c.cheeseman@imperial.ac.uk [Department of Civil and Environmental Engineering, Imperial College London, South Kensington Campus, London SW7 2AZ (United Kingdom)

    2014-11-15

    Magnesium silicate hydrate (M-S-H) gel is formed by the reaction of brucite with amorphous silica during sulphate attack in concrete and M-S-H is therefore regarded as having limited cementing properties. The aim of this work was to form M-S-H pastes, characterise the hydration reactions and assess the resulting properties. It is shown that M-S-H pastes can be prepared by reacting magnesium oxide (MgO) and silica fume (SF) at low water to solid ratio using sodium hexametaphosphate (NaHMP) as a dispersant. Characterisation of the hydration reactions by x-ray diffraction and thermogravimetric analysis shows that brucite and M-S-H gel are formed and that for samples containing 60 wt.% SF and 40 wt.% MgO all of the brucites react with SF to form M-S-H gel. These M-S-H cement pastes were found to have compressive strengths in excess of 70 MPa.

  14. Studies on the behaviour of different spent fluidized-bed catalytic cracking catalysts on Portland cement

    Directory of Open Access Journals (Sweden)

    Soriano, L.

    2009-12-01

    Full Text Available The fluidized-bed catalytic cracking catalyst (FCC it is a residue from the industry of the petroleum that shows a high pozzolanic reactivity and, in cementing matrix, it significantly improves their mechanical behaviour as well as durability. In this research a comparative study on residues of catalyst from different sources has been carried out, in order to know if these residues can be used jointly in an indiscriminate way or, on the contrary, it is necessary to classify them according to their characteristics. Thus, a study on five different FCC residues, supplied from different companies, has been carried out, and their physical-chemical characteristics, pozzolanic reactivity by means of thermogravimetric analysis and the evolution of the mechanical strength of mortars were studied. After analyzing all the aspects, it can be concluded that no significant differences among the different tested catalysts were found.El catalizador de craqueo catalítico (FCC es un residuo de la industria del petróleo que posee una elevada reactividad puzolánica y en matrices cementicias mejora de manera importante los aspectos mecánicos así como de durabilidad. En este trabajo se realiza un estudio comparativo sobre residuos de catalizador de distintos orígenes, para poder conocer si se pueden utilizar conjuntamente de forma indiscriminada o por el contrario hay que catalogarlos según su origen. Para ello, se realizó un estudio sobre cinco residuos de catalizador de craqueo catalítico distintos, suministrados por diferentes empresas y se estudiaron sus características fisicoquímicas, reactividad puzolánica a través de estudios termogravimétricos y la evolución de las resistencias mecánicas en morteros. Tras analizar todos los aspectos se concluye que no existen diferencias significativas entre los distintos catalizadores empleados.

  15. Hydration Properties of Ground Granulated Blast-Furnace Slag (GGBS Under Different Hydration Environments

    Directory of Open Access Journals (Sweden)

    Shuhua LIU

    2017-02-01

    Full Text Available The hydration properties of various cementitious materials containing Ground Granulated Blast-furnace Slag (GGBS, two alkali-activated slag cements (AAS-1 and AAS-2 in which sodium silicate and sodium hydroxide act as alkaline activators respectively, supersulfated cement (SSC and slag Portland cement(PSC, are compared with ordinary Portland cement (OPC to investigate the effect of activating environment on the hydration properties in this study by determining the compressive strength of the pastes, the hydration heat of binders within 96 hours, and the hydration products at age of 28 days. The results show that C-S-H gels are the main hydrated products for all cementitious systems containing GGBS. Ca(OH2 is the hydration products of OPC and PSC paste. However, ettringite and gypsum crystals instead of Ca(OH2 are detected in SSC paste. Additionally, tobermorite, a crystalline C-S-H, and calcite are hydrated products in AAS-1. Tobermorite, cowlesite and calcite are hydrated products of AAS-2 as well. Based on strength results, AAS-1 paste exhibits the highest compressive strength followed by POC, PSC, SSC in order at all testing ages and AAS-2 give the lowest compressive strength except for the early age at 3 days, which is higher than SSC but still lower than PSC. From hydration heat analysis, alkalinity in the reaction solution is a vital factor influencing the initial hydration rate and the initial hydration rate from higher to lower is AAS-2, AAS-1, OPC, PSC and SSC. Although AAS possesses a faster reaction rate in the initial hours, cumulative hydration heat of AAS is comparably lower than that of OPC, but higher than those of PSC and SSC in turn, which indicates that the hydration heat of clinkers is much higher than that of slag.DOI: http://dx.doi.org/10.5755/j01.ms.23.1.14934

  16. Evaluation of bacterial leakage of four root- end filling materials: Gray Pro Root MTA, White Pro Root MTA, Root MTA and Portland Cement (type I

    Directory of Open Access Journals (Sweden)

    Zarabian M.

    2005-07-01

    Full Text Available Background and Aim: Today several materials have been used for root- end filling in endodontic surgery. Optimal properties of Pro Root MTA in in-vitro and in-vivo studies has been proven. On the other hand, based on some studies, Root MTA (Iranian Pro Root MTA and Portland cement are similar to Pro Root MTA in physical and biologic properties. The aim of this study was to evaluate bacterial leakage (amount and mean leakage time of four root- end filling materials. Materials and Methods: In this experimental in-vitro study, seventy six extracted single- rooted human teeth were randomly divided into six groups for root-end filling with gray Pro Root MTA, white Pro Root MTA, Root MTA (Iranian Pro Root MTA, Portland Cement (type I and positive and negative control groups. Root canals were instrumented using the step- back technique. Root- end filling materials were placed in 3mm ultra sonic retro preparations. Samples and microleakage model system were sterilized in autoclave. The apical 3-4 mm of the roots were immersed in phenol red with 3% lactose broth culture medium. The coronal access of each specimen was inoculated every 24h with a suspension of Streptococcus sanguis (ATCC 10556. Culture media were observed every 24h for colour change indicating bacterial contamination for 60 days. Statistical analysis was performed using log- rank test with P<0.05 as the limit of significance. Results: At the end of study 50%, 56.25%, 56.25% and 50% of specimens filled with Gray Pro Root MTA, White Pro Root MTA. Root MTA and Portland Cement (type I had evidence of leakage respectively. The mean leakage time was 37.19±6.29, 36.44±5.81, 37.69±5.97 and 34.81±6.67 days respectively. Statistical analysis of data showed no significant difference among the leakage (amount and mean leakage time of the four tested root- end filling materials (P=0.9958. Conclusion: Based on the results of this study, there were no significant differences in leakage among the four

  17. Laser Radiation CO2 Effects in Cement Paste at Different Hydration Stages after Preparation

    Directory of Open Access Journals (Sweden)

    Moreno-Virgen M.R.

    2011-07-01

    Full Text Available In this work the changes occurring in cement pastes irradiated by 10.6µm CO2 laser at diff erent stages of hydration after preparation are presented. Raman spectroscopy, X-ray diffraction and Scanning Electronic Microscopy (SEM techniques were used to observe molecular structural changes. Intensity of cement paste Raman peaks after laser irradiation was monitored in samples irradiated 2, 3, 4, 5, 6, 7, 8, 9, 10 and 11 days after their preparation. Applied laser power changed Raman peaks intensity at 187.5cm-1, 563cm-1, 695cm-1, 750cm-1, 897cm-1, 1042cm-1 and 1159cm-1 that correspond to compounds already present in cement pastes. X-ray diffraction, SEM images and changes in the Raman peaks confirm the recrystalization of cement paste compounds into new phases (alite and belite after irradiation. The produced changes show a clear dependence on the applied laser power density and age of samples.

  18. 77 FR 5573 - Notice Pursuant to the National Cooperative Research and Production Act of 1993-Portland Cement...

    Science.gov (United States)

    2012-02-03

    ... Cement Association Notice is hereby given that, on January 6, 2012, pursuant to Section 6(a) of the... Cement Association (``PCA'') has filed written notifications simultaneously with the Attorney General and... this venture. Also, Texas-Lehigh Cement Company, Buda, TX; Arizona Cement Association, Phoenix,...

  19. 76 FR 12370 - Notice Pursuant to the National Cooperative Research and Production Act of 1993-Portland Cement...

    Science.gov (United States)

    2011-03-07

    ... Cement Association Notice is hereby given that, on February 02, 2011, pursuant to Section 6(a) of the... Cement Association (``PCA'') has filed written notifications simultaneously with the Attorney General and..., PA; Lehigh Cement Company LLC, Allentown, PA; Lehigh Northwest Cement Company, Seattle, WA;...

  20. Chromium behavior during cement-production processes: a clinkerization, hydration, and leaching study.

    Science.gov (United States)

    Sinyoung, Suthatip; Songsiriritthigul, Prayoon; Asavapisit, Suwimol; Kajitvichyanukul, Puangrat

    2011-07-15

    The behavior of chromium during the production of cement clinker, during the hydration of cement and during the leaching of cement mortars was investigated. The microstructures of clinker and mortar properties were investigated using free lime, XRD, SEM/EDS, and TG/DTA techniques. Chromium was found to be incorporated in the clinker phase. The formation of new chromium compounds such as Ca(6)Al(4)Cr(2)O(15), Ca(5)Cr(3)O(12), Ca(5)Cr(2)SiO(12), and CaCr(2)O(7), with chromium oxidation states of +3, +4.6, +5, and +6, respectively, was detected. After the hydration process, additional chromium compounds were identified in the mortar matrix, including Ca(5)(CrO(4))(3)OH, CaCrO(4)·2H(2)O, and Al(2)(OH)(4)CrO(4), with chromium oxidation states of +4.6, +6, and +6, respectively. Additionally, some species of chromium, such as Cr(3+) from Ca(6)Al(4)Cr(2)O(15) and Cr(6+) from CaCr(2)O(7), CaCrO(4)·2H(2)O, and Al(2)(OH)(4)CrO(4), were leached during leaching tests, whereas other species remained in the mortar. The concentrations of chromium that leached from the mortar following U.S. EPA Method 1311 and EA NEN 7375:2004 leaching tests were higher than limits set by the U.S. EPA and the Environment Agency of England and Wales related to hazardous waste disposal in landfills. Thus, waste containing chromium should not be allowed to mix with raw materials in the cement manufacturing process.

  1. Study on the hydration product of cement in early age using TEM

    Institute of Scientific and Technical Information of China (English)

    HAN Song; YAN PeiYu; LIU RengGuang

    2012-01-01

    The morphology,crystallization and elemental composition of cement hydration products in early age including Ca(OH)2,CSH gel,AFt and AFm were investigated by transmission electron microscopy (TEM).Compared with the results from SEM and XRD,the TEM method and its advantage in the investigation of early hydration products were discussed.The results showed that TEM method is more accurate and reliable than SEM in the investigation of early hydration products.The CSH gel was confirmed to be amorphous foil-like shape product with a lot of crumples in early hydration age.Its Ca/Si ratio is 1.3±0.2.The morphology difference of AFt and AFm was clarified.AFt and AFm are both poly-crystal with layered structure,composed of disordered nano crystal.The size of nano crystal is less than 20 nm.The difference of Ca/Si ratio results between SEM and TEM was investigated,and its reason was explained.

  2. Chromium behavior during cement-production processes: A clinkerization, hydration, and leaching study

    Energy Technology Data Exchange (ETDEWEB)

    Sinyoung, Suthatip [Department of Environmental Engineering, Faculty of Engineering, King Mongkut' s University of Technology Thonburi, Bangkok, 10140 (Thailand); Songsiriritthigul, Prayoon [Synchrotron Light Research Institute, PO Box 93 Nakhon Ratchasima, 30000 (Thailand); School of Physics, Suranaree University of Technology, Nakhon Ratchasima, 30000 (Thailand); Asavapisit, Suwimol, E-mail: suwimol_s@hotmail.com [Environmental Technology, School of Energy and Materials, King Mongkut' s University of Technology Thonburi, Bangkok, 10140 (Thailand); National Center of Excellence for Environmental and Hazardous Waste Management, Faculty of Engineering, King Mongkut' s University of Technology Thonburi, Bangkok, 10140 (Thailand); Kajitvichyanukul, Puangrat, E-mail: puangratk@nu.ac.th [National Center of Excellence for Environmental and Hazardous Waste Management, Faculty of Engineering, King Mongkut' s University of Technology Thonburi, Bangkok, 10140 (Thailand); Department of Civil Engineering, Faculty of Engineering, Naresuan University, Phitsanulok, 65000 (Thailand)

    2011-07-15

    Highlights: {yields} Behavior of chromium during cement-production processes. {yields} Formation of new chromium compounds in clinker with chromium oxidation states of +3, +4.6, +5, and +6. {yields} Addition of chromium altered the composition of the clinker phases, setting time, and compressive strength of hydrated mixes. {yields} Cr{sup 3+} and Cr{sup 6} were leached during leaching tests, whereas other species remained in the mortar. - Abstract: The behavior of chromium during the production of cement clinker, during the hydration of cement and during the leaching of cement mortars was investigated. The microstructures of clinker and mortar properties were investigated using free lime, XRD, SEM/EDS, and TG/DTA techniques. Chromium was found to be incorporated in the clinker phase. The formation of new chromium compounds such as Ca{sub 6}Al{sub 4}Cr{sub 2}O{sub 15}, Ca{sub 5}Cr{sub 3}O{sub 12}, Ca{sub 5}Cr{sub 2}SiO{sub 12}, and CaCr{sub 2}O{sub 7}, with chromium oxidation states of +3, +4.6, +5, and +6, respectively, was detected. After the hydration process, additional chromium compounds were identified in the mortar matrix, including Ca{sub 5}(CrO{sub 4}){sub 3}OH, CaCrO{sub 4}.2H{sub 2}O, and Al{sub 2}(OH){sub 4}CrO{sub 4}, with chromium oxidation states of +4.6, +6, and +6, respectively. Additionally, some species of chromium, such as Cr{sup 3+} from Ca{sub 6}Al{sub 4}Cr{sub 2}O{sub 15} and Cr{sup 6+} from CaCr{sub 2}O{sub 7}, CaCrO{sub 4}.2H{sub 2}O, and Al{sub 2}(OH){sub 4}CrO{sub 4}, were leached during leaching tests, whereas other species remained in the mortar. The concentrations of chromium that leached from the mortar following U.S. EPA Method 1311 and EA NEN 7375:2004 leaching tests were higher than limits set by the U.S. EPA and the Environment Agency of England and Wales related to hazardous waste disposal in landfills. Thus, waste containing chromium should not be allowed to mix with raw materials in the cement manufacturing process.

  3. Study of cements silicate phases hydrated under high pressure and high temperature; Etude des phases silicatees du ciment hydrate sous haute pression et haute temperature

    Energy Technology Data Exchange (ETDEWEB)

    Meducin, F.

    2001-10-01

    This study concerns the durability of oil-well cementing. Indeed, in oil well cementing a cement slurry is pumped down the steel casing of the well up the annular space between it and the surrounding rock to support and protect the casing. The setting conditions of pressure and temperature may be very high (up to 1000 bar and 250 deg C at the bottom of the oil-well). In this research, the hydration of the main constituent of cement, synthetic tri-calcium silicate Ca{sub 3}SiO{sub 2}, often called C{sub 3}S (C = CaO; S = SiO{sub 2} and H H{sub 2}O), is studied. Calcium Silicate hydrates are prepared in high-pressure cells to complete their phase diagram (P,T) and obtain the stability conditions for each species. Indeed, the phases formed in these conditions are unknown and the study consists in the hydration of C{sub 3}S at different temperatures, pressures, and during different times to simulate the oil-well conditions. In a first step (until 120 deg C at ambient pressure) the C-S-H, a not well crystallized and non-stoichiometric phase, is synthesized: it brings adhesion and mechanical properties., Then, when pressure and temperature increase, crystallized phases appear such as jaffeite (Ca{sub 6}(Si{sub 2}O{sub 7})(OH){sub 6}) and hillebrandite (Ca{sub 2}(SiO{sub 3})(OH){sub 2}). Silicon {sup 29}Si Nuclear Magnetic Resonance (using standard sequences MAS, CPMAS) allow us to identify all the silicates hydrates formed. Indeed, {sup 29}Si NMR is a valuable tool to determine the structure of crystallized or not-well crystallized phases of cement. The characterization of the hydrated samples is completed by other techniques: X- Ray Diffraction and Scanning Electron Microscopy. The following results are found: jaffeite is the most stable phase at C/S=3. To simulate the hydration of real cement, hydration of C{sub 3}S with ground quartz and with or without super-plasticizers is done. In those cases, new phases appear: kilchoanite mainly, and xonotlite. A large amount of

  4. The suitability of a supersulfated cement for nuclear waste immobilisation

    Science.gov (United States)

    Collier, N. C.; Milestone, N. B.; Gordon, L. E.; Ko, S.-C.

    2014-09-01

    Composite cements based on ordinary Portland cement are used in the UK as immobilisation matrices for low and intermediate level nuclear wastes. However, the high pore solution pH causes corrosion of some metallic wastes and undesirable expansive reactions, which has led to alternative cementing systems being examined. We have investigated the physical, chemical and microstructural properties of a supersulfated cement in order to determine its applicability for use in nuclear waste encapsulation. The hardened supersulfated cement paste appeared to have properties desirable for use in producing encapsulation matrices, but the high powder specific surface resulted in a matrix with high porosity. Ettringite and calcium silicate hydrate were the main phases formed in the hardened cement paste and anhydrite was present in excess. The maximum rate of heat output during hydration of the supersulfated cement paste was slightly higher than that of a 9:1 blastfurnace slag:ordinary Portland cement paste commonly used by the UK nuclear waste processing industry, although the total heat output of the supersulfated cement paste was lower. The pH was also significantly lower in the supersulfated cement paste. Aluminium hydroxide was formed on the surface of aluminium metal encapsulated in the cement paste and ettringite was detected between the aluminium hydroxide and the hardened cement paste.

  5. 含钡硫铝酸盐水泥的水化动力学与热力学研究%Study on Kinetics and Thermodynamics of Hydration of Ba-bearing Sulphoaluminate Cement

    Institute of Scientific and Technical Information of China (English)

    徐冠立; 孙遥; 林金辉

    2013-01-01

    Kinetics and thermodynamics of Ba-bearing sulphoaluminate cement hydrate reaction had been studied by XRD and isothermal calorimetry methods.The results showed that the rate of the hydration is diffusionally controlled,and its pattern is similar to tri-calcium aluminate and Portland cement.The hydration process could be divided into acceleration,deceleration and decay stages.The hydration is nucleation controlled at acceleration stage which means the reaction is autocatalytic.At deceleration stage,after layers of hydrate develops on the clinker particles causing the increasing obstruction,hydration rate decrease,and finally become controlled totally by diffusion at decay stage.%采用XRD和等温微量热法测试计算含钡硫铝酸盐水泥的水化动力学和热力学过程.结果表明,含钡硫铝酸盐水泥的水化过程主要受扩散过程控制,水化速率变化模式与铝酸钙、硅酸盐水泥类似.水化过程分为加速期、减速期和衰减期:在加速期,水化反应受成核反应控制,属自催化反应;从减速期开始,水化物在颗粒表面形成水化物薄膜,水化反应阻力加大,速率减缓;进入衰减期,水化反应完全受扩散过程控制.

  6. The suitability of a supersulfated cement for nuclear waste immobilisation

    Energy Technology Data Exchange (ETDEWEB)

    Collier, N.C., E-mail: nick.collier@sheffield.ac.uk [Immobilisation Science Laboratory, Department of Materials Science and Engineering, The University of Sheffield, Mappin Street, Sheffield S1 3JD (United Kingdom); Milestone, N.B. [Immobilisation Science Laboratory, Department of Materials Science and Engineering, The University of Sheffield, Mappin Street, Sheffield S1 3JD (United Kingdom); Callaghan Innovation, 69 Gracefield Road, PO Box 31310, Lower Hutt 5040 (New Zealand); Gordon, L.E. [Immobilisation Science Laboratory, Department of Materials Science and Engineering, The University of Sheffield, Mappin Street, Sheffield S1 3JD (United Kingdom); Geopolymer and Minerals Processing Group, Department of Chemical and Biomolecular Engineering, University of Melbourne, Parkville, Victoria 3010 (Australia); Ko, S.-C. [Holcim Technology Ltd, Hagenholzstrasse 85, CH-8050 Zurich (Switzerland)

    2014-09-15

    Highlights: • We investigate a supersulfated cement for use as a nuclear waste encapsulant. • High powder fineness requires a high water content to satisfy flow requirements. • Heat generation during hydration is similar to a control cement paste. • Typical hydration products are formed resulting in a high potential for waste ion immobilisation. • Paste pH and aluminium corrosion is less than in a control cement paste. - Abstract: Composite cements based on ordinary Portland cement are used in the UK as immobilisation matrices for low and intermediate level nuclear wastes. However, the high pore solution pH causes corrosion of some metallic wastes and undesirable expansive reactions, which has led to alternative cementing systems being examined. We have investigated the physical, chemical and microstructural properties of a supersulfated cement in order to determine its applicability for use in nuclear waste encapsulation. The hardened supersulfated cement paste appeared to have properties desirable for use in producing encapsulation matrices, but the high powder specific surface resulted in a matrix with high porosity. Ettringite and calcium silicate hydrate were the main phases formed in the hardened cement paste and anhydrite was present in excess. The maximum rate of heat output during hydration of the supersulfated cement paste was slightly higher than that of a 9:1 blastfurnace slag:ordinary Portland cement paste commonly used by the UK nuclear waste processing industry, although the total heat output of the supersulfated cement paste was lower. The pH was also significantly lower in the supersulfated cement paste. Aluminium hydroxide was formed on the surface of aluminium metal encapsulated in the cement paste and ettringite was detected between the aluminium hydroxide and the hardened cement paste.

  7. Study on Slag Powder in White Portland Cement%矿渣微粉在白色硅酸盐水泥中的应用研究

    Institute of Scientific and Technical Information of China (English)

    王念

    2014-01-01

    White Portland cement is widely used due to its inherent advantages of whiteness and strength.GGBS has a high whiteness and high late strength characteristics.It is a linkd of new green building materials with low-carbon en-vironmental protection,and has the effect of low-carbon emission reduction.GGBS is considered to replace part of the clinker used for preparation of white cement.It is studied that white Portland cement is prepared with GGBS in differ-ent proportions to replace the white cement clinker or flying powder.The results show it has a significant improvement on the two main indicators of the strength and whiteness.%白色硅酸盐水泥由于其本身具有白度和强度的优势而广泛应用;矿渣微粉是一种具有高白度以及后期高强度等特点的低碳环保新型绿色建材,因而我们考虑将矿粉取代部分熟料用来配制白水泥,达到低碳减排的效果。通过研究发现将矿粉以不同的比例取代熟料或双飞粉配制出的白水泥在强度和白度两大指标上都有显著改善。

  8. Arsenic encapsulation using Portland cement with ferrous sulfate/lime and Terra-Bond™ technologies - Microcharacterization and leaching studies.

    Science.gov (United States)

    Randall, Paul M

    2012-03-15

    This work reports the results of an investigation on the treatment and encapsulation of arsenic-containing materials by Portland cement with ferrous sulfate and lime (PFL) and Terra-Bond™, a commercially available patented technology. The arsenic materials included: chromated copper arsenate (CCA)-treated wood materials; scorodite-rich mine tailings from the La Trinidad Mine in California; and a soil/smelter dust mixture from the Anaconda Superfund site spiked with monosodium methyl arsenate (MSMA) to simulate an organoarsenic soil material. SEM/EDS and XRD spectra of PFL treated samples showed similarity across all three waste materials while Terra-Bond treated samples showed predominance of elemental sulfur. SEM/EDS of PFL treated samples showed that calcium was imbedded in the structure while micrographs of Terra-Bond treated samples showed the appearance of an epoxy material on the surface. The epoxy material appears to be responsible for encapsulating and reducing the leachability of arsenic. XANES spectra for the PFL treatment of CCA-containing samples showed that arsenic has a predominant pentavalent form (As +5), and the PFL treatment process did not alter the arsenic oxidation state. But, distinct differences were observed for XANES spectra of untreated and PFL treated scorodite-rich mine tailing which changed the arsenic coordination structure from a mixture of As (+3/+5) to exclusively As (+5). Both S/S techniques reduced the amount of arsenic released in the leaching tests. Most cases show lower amounts of arsenic released from wastes treated by the Terra-Bond™ technique when compared to the PFL technique. The pH of the solution significantly affected the leachability, with the amount of arsenic released increasing with pH. Sequential extraction results indicate that sodium hydroxide was favorable in releasing arsenic in the mine tailings. This is due to ligand displacement reactions of hydroxyl ions with arsenic species and high pH conditions that

  9. Raw mix designing, clinkerization and manufacturing of high-strength Portland cement from the limestone and clay of Darukhula Nizampur, Nowshera District, North-West Frontier Province (N.W.F.P.), Pakistan

    Institute of Scientific and Technical Information of China (English)

    Noor-ul-Amin; Tahir Shah; Khurshid Ali

    2009-01-01

    This paper covers the detailed version of the potential raw material deposits at Darukhula and the adjacent areas of Nizampur, the manufacturing of high-strength Portland cement samples from the same material and comparison of the physical and chemical parameters for resulting cement with British and Pakistan standard specifications, which include compressive strength, setting time, consistency, lechatelier expansion, Blaine and insoluble residue. It was found that the raw material available in the study area meets the standard specifications and the area is feasible for the cement plant installation. The area can provide raw material which is quite sufficient for the running of a cement plant.

  10. Probing the hydration of composite cement pastes containing fly ash and silica fume by proton NMR spin-lattice relaxation

    Institute of Scientific and Technical Information of China (English)

    2010-01-01

    Proton NMR spin-lattice relaxation (T1) was used as a prober for observing the hydration process of composite cement pastes blending fly ash and silica fume during the early age.The distribution at initial time,evolution curves and signals intensity of T1 were shown in this paper.Results demonstrate that the T1 distribution curves at initial time exhibit two peaks,which are regarded as two different water phases in the pastes.The evolution curves of T1 are in good agreement with the hydration process of composite pastes and could be roughly divided into four stages:initial period,dormant period,acceleration period and steady period.The hydration mechanism for each stage was discussed.The hydration of the composite cement pastes was retarded by the addition of fly ash and silica fume when compared to that of pure cement.However,the hydration degree of the cement in the blends was promoted.

  11. Healing of root perforations treated with Mineral Trioxide Aggregate (MTA and Portland cement Reparo de perfurações radiculares tratadas com Agregado Trióxido Mineral (MTA e cimento Portland

    Directory of Open Access Journals (Sweden)

    Norberto Juárez Broon

    2006-10-01

    Full Text Available Fourteen root perforations were performed for microscopic evaluation of the repair of interradicular tissue in dogs' teeth. These perforations were accomplished at low-speed with a STP 58 bur at the cervical third of the mesial root toward the furcation under irrigation with saline solution, followed by immediate sealing with ProRoot MTA, MTA-Angelus and white Portland cement. The dogs were killed after 90 days, revealing good results. The Kruskal-Wallis test did not demonstrate any statistically significant difference. It was concluded that the three materials showed good sealing in mineralized tissue, with complete closure, and they were free of inflammation in most teeth.Avaliou-se o reparo de perfurações em dentes de cães, tratadas com ProRoot MTA, MTA Angelus e cimento Portland branco. As perfurações foram feitas na região de furca de premolares, superiores e inferiores, com broca STP 58 sob refrigeração com soro fisiólogico. Os animais foram mortos após 90 dias e os dentes foram preparados para análise microscópica pela coloração da hematoxilina e eosina. Os três materiais propiciaram o selamento da perfuração com tecido mineralizado e o teste de Kruskal-Wallis demostrou não haver diferença estatística entre eles.

  12. Chemical composition, effective atomic number and electron density study of trommel sieve waste (TSW), Portland cement, lime, pointing and their admixtures with TSW in different proportions.

    Science.gov (United States)

    Kurudirek, Murat; Aygun, Murat; Erzeneoğlu, Salih Zeki

    2010-06-01

    The trommel sieve waste (TSW) which forms during the boron ore production is considered to be a promising building material with its use as an admixture with Portland cement and is considered to be an alternative radiation shielding material, also. Thus, having knowledge on the chemical composition and radiation interaction properties of TSW as compared to other building materials is of importance. In the present study, chemical compositions of the materials used have been determined using a wavelength dispersive X-ray fluorescence spectrometer (WDXRFS). Also, TSW, some commonly used building materials (Portland cement, lime and pointing) and their admixtures with TSW have been investigated in terms of total mass attenuation coefficients (mu/rho), photon interaction cross sections (sigma(t)), effective atomic numbers (Z(eff)) and effective electron densities (N(e)) by using X-rays at 22.1, 25keV and gamma-rays at 88keV photon energies. Possible conclusions were drawn with respect to the variations in photon energy and chemical composition.

  13. Effect of Curing Regime on Degree of Al3+Substituting for Si4+in C-S-H Gels of Hardened Portland Cement Pastes

    Institute of Scientific and Technical Information of China (English)

    HU Chenguang; HU Shuguang; DING Qingjun; FENG Xiaoxin; HUANG Xiulin

    2014-01-01

    The effect of curing regime on degree of Al3+substituting for Si4+(Al/Si ratio) in C-S-H gels of hardened Portland cement pastes was investigated by 29Si magic angel spinning (MAS) nuclear magnetic resonance (NMR) with deconvolution technique. The curing regimes included the constant temperature (20, 40, 60 and 80℃) and variable temperature (simulated internal temperature of mass concrete with 60℃peak). The results indicate that constant temperature of 20℃is beneficial to substitution of Al3+for Si4+, and Al/Si ratio changes to be steady after 180 d. The increase of Al/Si ratio at 40℃is less than that at 20℃for 28 d. The other three regimes of high temperature increase Al/Si ratio only before 3 d, on the contrary to that from 3 to 28 d. However, the 20℃curing stage from 28 to 180 d at variable temperature regime, is beneficial to the increase of Al/Si ratio which is still lower than that at constant temperature regime of 20℃for the same age. A nonlinear relation exists between the Al/Si ratio and temperature variation or mean chain length (MCL) of C-S-H gels, furthermore, the amount of Al3+which can occupy the bridging tetrahedra sites in C-S-H structure is insufficient in hardened Portland cement pastes.

  14. Interactions between hydrated cement paste and organic acids: Thermodynamic data and speciation modeling

    Energy Technology Data Exchange (ETDEWEB)

    De Windt, Laurent, E-mail: laurent.dewindt@mines-paristech.fr [MINES ParisTech, PSL Research University, Centre de Géosciences, 35 Rue St-Honoré, 77305 Fontainebleau Cedex (France); Bertron, Alexandra; Larreur-Cayol, Steeves; Escadeillas, Gilles [University of Toulouse, UPS/INSA/LMDC, 135 Av. de Rangueil, 31077 Toulouse Cedex 04 (France)

    2015-03-15

    Interactions of short-chain organic acids with hydrated cement phases affect structure durability in the agro-food and nuclear waste industries but can also be used to modify cement properties. Most previous studies have been experimental, performed at fixed concentrations and pH, without quantitatively discriminating among polyacidity effects, or complexation and salt precipitation processes. This paper addresses such issues by thermodynamic equilibrium calculations for acetic, citric, oxalic, succinic acids and a simplified hydrated CEM-I. The thermodynamic constants collected from the literature allow the speciation to be modeled over a wide range of pH and concentrations. Citric and oxalic had a stronger chelating effect than acetic acid, while succinic acid was intermediate. Similarly, Ca-citrate and Ca-oxalate salts were more insoluble than Ca-acetate and Ca-succinate salts. Regarding aluminium complexation, hydroxyls, sulfates, and acid competition was highlighted. The exploration of acid mixtures showed the preponderant effect of oxalate and citrate over acetate and succinate.

  15. Evolución de la Porosidad de Pastas de Cemento Portland por la Incorporación de una Puzolana Natural Evolution of Porosity in Portland Cement Pastes by addition of Natural Pozzolan

    Directory of Open Access Journals (Sweden)

    J.L. Fernández

    2004-01-01

    Full Text Available Se ha determinado la evolución que se produce en la porosidad de las pastas elaboradas con cemento Portland para uso general (CPN IRAM 50000, al incorporarle una puzolana natural de la región, en distintas proporciones y en función del tiempo de curado. El ensayo de porosidad se realiza según Norma API-RP-40, basada en la ley de Boyle, por la cual se determina el volumen de los vacíos de las pastas. Este se determina por diferencia entre el volumen total del gas a una presión P1 de 6.9.10(5 Pa y el volumen calibrado de una celda donde se encuentra la muestra a presión atmosférica P0. Posteriormente, se ingresa en la curva de calibración del porosímetro y se obtienen los volúmenes de sólido de las mezclas. Como conclusión se demuestra que la porosidad de las pastas disminuye con el aumento de la cantidad de cemento reemplazado y del tiempo de curadoA determination was made of the evolution of porosity in Portland cement pastes for general usage (CPN IRAM 50000 by incorporating different proportions of natural pozzolan from the region, and as a function of curing time. The API-RP-40 norm based on Boyle´s law was used to measure the porosity, determining the paste effective void volume. This is done by calculating the difference between the total gas space at a pressure P1 of 6,9 .10(5 Pa and the calibrated volume of the cell at atmospheric pressure P0. Then the paste volume was obtained by porosimeter calibration curves. In conclusion, this study demonstrates that the porosity of pastes decreases as a function of the amount of cement replaced and time of cure

  16. Effect of Additives on the Morphology of the Hydrated Product and Physical Properties of a Calcium Phosphate Cement

    Institute of Scientific and Technical Information of China (English)

    Xiupeng WANG; Jiandong YE; Yingjun WANG

    2008-01-01

    The morphology of a hydrated calcium phosphate cement (CPC) doped with several normally used additives was investigated by scanning electron microscopy (SEM) and the compressive strength of the cement was determined in this study. The hydrated products of CPC without additives was rod-like hydroxyapatite (HA) grains with around 2-5 μm in length and 100 nm in width. The addition of Sr obviously decreased the crystal size of the rod-like grains. CPCs containing carbonate, collagen and gelatin showed flake-like crystal morphology. Crylic acid-containing CPC presented flocculus-like structure. And malic acid-containing CPC exhibited oriented flake-like structure. The X-ray diffraction (XRD) analysis showed that the additives used in this study did not alter the hydration products of the cement. The compressive strength tests indicated that the compressive strength of the cement with rod-like morphology HA crystals was much higher than that of the cement with flake-like morphology HA crystals, and the cement with oriented flake-like morphology HA crystals .exhibited the poorest compressive strength.

  17. Perbandingan Sifat Fisik Beton Yang Menggunakan Semen Portland Pozzolan Dan Semen Portland Tipe I

    OpenAIRE

    Yusnita, Heni

    2011-01-01

    The research about concrete by using the Portland pozzolan cement and Portland cement type I has been done with the variation of submersion time is 7, 14, 21, and 28 days. The test is done for physics of the concrete. The sample is made from the ingredients 1 cement : 2 sand : 3 pebble. The result of the researching shows that the used of the Portland pozzolan cement can raise the impact of the concrete as much as 9,15% from concrete which uses the Portland cement type I. Orther side for the ...

  18. 全组分废弃混凝土再生水泥熟料烧成及水化性能研究%Study of sintering process and hydration of recycled cement clinker produced from all components of waste concrete

    Institute of Scientific and Technical Information of China (English)

    艾红梅; 常钧; 卢洪正; 燕芳; 韩立东

    2013-01-01

    With regards to the existing technical problems for the cementitious reusage of waste concrete in our country which lead to the low efficiency of various component separation in waste concrete ,high production cost and large energy consumption ,a new technology roadmap is raised using all components of waste concrete as part raw materials and burning clinker for producing recycled cement . The burnability of recycled cement raw mixtures , the mineral components of recycled cement clinker and the strength and microstructure of hydrated recycled cement are all investigated .The experimental results show that the technology of recycled cement produced from all components of waste concrete is feasible and the burnability of raw mixtures is good .However ,the strength of hydrated recycled cement mortar is lower than the technical requirements of Portland cement clinker strength ,due to the difference of experimental conditions between the laboratory and plant ;sintered recycled cement clinker admixed with the seed crystals of Portland cement clinker ,its mineral compositions and hydration products are basically the same as the industrial cement clinker .In addition ,the microstructure of C-S-H gel in the hydration products is also similar .%  针对我国废弃混凝土胶凝化再生利用技术存在的组分分离导致材料利用率低、生产成本和能耗高等问题,提出利用以石灰岩为粗骨料的全组分废弃混凝土作为生料原料,煅烧熟料、制备再生水泥的新思路。研究了再生水泥的生料易烧性以及熟料的矿物组成、水化强度和水化产物的微观形貌。结果表明:全组分废弃混凝土再生水泥技术是可行的;再生水泥生料易烧性较好,熟料胶砂强度低于硅酸盐水泥熟料技术要求,试验条件是影响强度的主要因素;引入熟料晶种煅烧的再生水泥熟料,其主要矿物成分和水化产物的组成与参比工业熟料基本相同

  19. 75 FR 4423 - Notice Pursuant to the National Cooperative Research and Production Act of 1993-Portland Cement...

    Science.gov (United States)

    2010-01-27

    ... Cement Association Notice is hereby given that, on December 14, 2009, pursuant to Section 6(a) of the... Cement Association (``PCA'') has filed written notifications simultaneously with the Attorney General and... damages under specified circumstances. Specifically, Continental Cement, Hannibal, MO has been added as...

  20. Reuse of a residue from petrochemical industry with portland cement Reutilización de un residuo de la industria petroquímica como adición al cemento portland

    Directory of Open Access Journals (Sweden)

    Janneth Torres Agredo

    2012-06-01

    Full Text Available In this article the possibility of using waste from the petrochemical industry,as partial replacement of Portland cement is studied, evaluating the presenceof contaminants in the waste and the encapsulation, once it is confined on the cement. This has been done, in order to find a use to this residue without cause damage to the environment. This residue, called spent fluid catalytic cracking catalyst (FCC, is mainly formed by a type Y zeolite, which is dispersing in an inorganic oxides matrix. The toxicity characteristic leaching proceeding was applied, in mortars adding with 20% of FCC as Portland cement replacement. The results showed that the residue does not represent a problem from the point of view of the leaching of elements, such as As, Pb, Zn, Cr, and La, which were below to the permissible limits. Additionally, the pozzolanic activity of FCC was evaluated according to ASTM C311, where the efficiency of the residue as pozzolanic addition is demonstrated. With the results the importance of reusing a residue of the petrochemical industry is emphasized, that decreases the amount of cement to be used and improves the mechanical resistance of the materials containing it.En el presente artículo se estudia la posibilidad de utilizar un residuo de la industria petroquímica, como sustitución parcial del cemento Portland, evaluando la presencia de elementos contaminantes en el residuo y su encapsulación, una vez se haya confinado con el cemento. Lo anterior, con el fin de determinar si su uso como material de construcción, puede o no causar un efecto negativo al medio ambiente. El residuo, denominado catalizador usado de craqueo catalítico (FCC, es un material que está compuesto por una zeolita tipo Y, dispersa en una matriz de óxidos inorgánicos. Se aplicó la técnica de TCLP (del inglés Toxicity Characteristic Leaching Procedure, en morteros adicionados con un 20%, de FCC con respecto a la cantidad de cemento. Los resultados

  1. The influence of loading on the corrosion of steel in cracked ordinary Portland cement and high performance concretes

    Science.gov (United States)

    Jaffer, Shahzma Jafferali

    Most studies that have examined chloride-induced corrosion of steel in concrete have focused on sound concrete. However, reinforced concrete is seldom uncracked and very few studies have investigated the influence of cracked concrete on rebar corrosion. Furthermore, the studies that have examined the relationship between cracks and corrosion have focused on unloaded or statically loaded cracks. However, in practice, reinforced concrete structures (e.g. bridges) are often dynamically loaded. Hence, the cracks in such structures open and close which could influence the corrosion of the reinforcing steel. Consequently, the objectives of this project were (i) to examine the effect of different types of loading on the corrosion of reinforcing steel, (ii) the influence of concrete mixture design on the corrosion behaviour and (iii) to provide data that can be used in service-life modelling of cracked reinforced concretes. In this project, cracked reinforced concrete beams made with ordinary Portland cement concrete (OPCC) and high performance concrete (HPC) were subjected to no load, static loading and dynamic loading. They were immersed in salt solution to just above the crack level at their mid-point for two weeks out of every four (wet cycle) and, for the remaining two weeks, were left in ambient laboratory conditions to dry (dry cycle). The wet cycle led to three conditions of exposure for each beam: (i) the non-submerged region, (ii) the sound, submerged region and (iii) the cracked mid-section, which was also immersed in the solution. Linear polarization resistance and galvanostatic pulse techniques were used to monitor the corrosion in the three regions. Potentiodynamic polarization, electrochemical current noise and concrete electrical resistance measurements were also performed. These measurements illustrated that (i) rebar corroded faster at cracks than in sound concrete, (ii) HPC was more protective towards the rebar than OPCC even at cracks and (iii) there

  2. Effect of Ba2+on microstructure of C-S-H in portland cement pastes at variable temperature regime%变温下 Ba2+对水泥浆体C-S-H微结构的影响

    Institute of Scientific and Technical Information of China (English)

    沈凡; 胡晨光; 赵明宇

    2014-01-01

    为从分子尺度优化C-S-H微结构提供理论依据,采用模拟大体积混凝土内部变温历程的养护制度,运用29 Si魔角旋转核磁共振(29 Si MAS NMR)结合去卷积技术,研究了变温条件下Ba(OH)2掺量为1.0%时对水泥浆体C-S-H微结构的影响规律。结果表明:在变温条件下掺加Ba(OH)2提高了水泥浆体中硅酸盐矿物水化程度,尤其在水化早期(3 d)时硅酸盐矿物水化程度增幅较大,进而使C-S-H结构中硅氧四面体二聚体数量增加,导致其C-S-H平均分子链长(MCL)显著低于纯水泥浆体,避免了纯水泥浆体在降温阶段出现C-S-H的MCL降低的现象。同时,掺加Ba(OH)2进一步降低了水泥浆体在变温过程下C-S-H中Al3+取代Si4+的程度。%In order to provide the theoretical basis for optimizing the microstructure of C -S -H at molecular scale,by simulating the variable temperature process in the interior of mass concrete and using the 29 Si Magic Angle Spinning Nuclear Magnetic Resonance (MAS NMR)combined with deconvolution technique,effect of 1.0% Ba(OH)2 on C-S-H microstructure in Portland cement pastes at variable temperature regime was in-vestigated.The results show that the hydration of silicate minerals in cement pastes is improved by mixing the Ba(OH)2 at variable temperature regime,especially at the early stage hydration(3 d).The amount of silicate tetrahedra dimers is increased,leading to the mean chain length (MCL)of C -S -H in cement pastes with Ba(OH)2 lower than that in pure cement pastes,avoiding the phenomenon of C-S-H MCL reduction in pure cement pastes at the cooling stage.Meanwhile,the degree of Al3+substituting for Si4+is further decreased by adding to Ba(OH)2 in cement pastes at variable temperature regime.

  3. A new quantification method based on SEM-EDS to assess fly ash composition and study the reaction of its individual components in hydrating cement paste

    Energy Technology Data Exchange (ETDEWEB)

    Durdziński, Paweł T., E-mail: pawel.durdzinski@gmail.com [Laboratory of Construction Materials, École Polytechnique Fédérale de Lausanne (EPFL), Station 12, CH-1015 Lausanne (Switzerland); Dunant, Cyrille F. [Laboratory of Construction Materials, École Polytechnique Fédérale de Lausanne (EPFL), Station 12, CH-1015 Lausanne (Switzerland); Haha, Mohsen Ben [HeidelbergCement Technology Center GmbH (HeidelbergCement AG), Rohrbacher Str. 95, 69181 Leimen (Germany); Scrivener, Karen L. [Laboratory of Construction Materials, École Polytechnique Fédérale de Lausanne (EPFL), Station 12, CH-1015 Lausanne (Switzerland)

    2015-07-15

    Calcareous fly ashes are high-potential reactive residues for blended cements, but their qualification and use in concrete are hindered by heterogeneity and variability. Current characterization often fails to identify the dominant, most reactive, amorphous fraction of the ashes. We developed an approach to characterize ashes using electron microscopy. EDS element composition of millions of points is plotted in a ternary frequency plot. A visual analysis reveals number and ranges of chemical composition of populations: silicate, calcium-silicate, aluminosilicate, and calcium-rich aluminosilicate. We quantified these populations in four ashes and followed their hydration in two Portland-ash systems. One ash reacted at a moderate rate: it was composed of 70 vol.% of aluminosilicates and calcium-silicates and reached 60% reaction at 90 days. The other reacted faster, reaching 60% at 28 days due to 55 vol.% of calcium-rich aluminosilicates, but further reaction was slower and 15 vol.% of phases, the silica-rich ones, did not react.

  4. Study of the Microstructure Evolution of Low-pH Cements Based on Ordinary Portland Cement (OPC) by Mid- and Near-Infrared Spectroscopy, and Their Influence on Corrosion of Steel Reinforcement.

    Science.gov (United States)

    García Calvo, José Luis; Sánchez Moreno, Mercedes; Alonso Alonso, María Cruz; Hidalgo López, Ana; García Olmo, Juan

    2013-06-18

    Low-pH cements are designed to be used in underground repositories for high level waste. When they are based on Ordinary Portland Cements (OPC), high mineral admixture contents must be used which significantly modify their microstructure properties and performance. This paper evaluates the microstructure evolution of low-pH cement pastes based on OPC plus silica fume and/or fly ashes, using Mid-Infrared and Near-Infrared spectroscopy to detect cement pastes mainly composed of high polymerized C-A-S-H gels with low C/S ratios. In addition, the lower pore solution pH of these special cementitious materials have been monitored with embedded metallic sensors. Besides, as the use of reinforced concrete can be required in underground repositories, the influence of low-pH cementitious materials on steel reinforcement corrosion was analysed. Due to their lower pore solution pH and their different pore solution chemical composition a clear influence on steel reinforcement corrosion was detected.

  5. Effect of supplementary cementing materials on the concrete corrosion control

    Energy Technology Data Exchange (ETDEWEB)

    Mejia de Gutierrez, R.

    2003-07-01

    Failure of concrete after a period of years, less than the life expected for which it was designed, may be caused by the environment to which it has been exposed or by a variety of internal causes. The incorporation of supplementary materials has at the Portland cement the purpose of improving the concrete microstructure and also of influence the resistance of concrete to environmental attacks. Different mineral by-products as ground granulated blast furnaces slag (GGBS), silica fume (SF), meta kaolin (MK), fly ash (FA) and other products have been used as supplementary cementing materials. This paper is about the behavior of concrete in the presence of mineral additions. Compared to Portland cements, blended cements show lower heat of hydration, lower permeability, greater resistance to sulphates and sea water. These blended cements find the best application when requirements of durability are regarded as a priority specially on high performance concrete: (Author) 11 refs.

  6. Preparation of sulphoaluminate belite cement from fly ash

    Energy Technology Data Exchange (ETDEWEB)

    Sahu, S.; Majling, J. (Slovak Technical Univ., Bratislava (Slovakia). Dept. of Ceramics, Glass and Cement)

    1994-01-01

    Sulphoaluminate belite cements containing the phases C[sub 2]S, C[sub 4]A[sub 3][bar S], C[sub 4]AF, C[bar S] were synthesized from limestone, fly ash and gypsum at 1,200 C. The correspondence between the predicted phase composition and real phase composition were checked. The influence of quantities of different phases in the hydration behavior and strength development were verified. Results show that an optimum proportion of phase quantities help in high strength development in early age. These cements fulfill all the requirement of Portland cement and have very high early strength. Porosity measurements show that the total pore volume in early period is comparatively less than that of Ordinary Portland Cement. Thus these cements can be usable for special purposes.

  7. Potencialidades de um caulim calcinado como material de substituição parcial do cimento portland em argamassas Potentialities of a calcined kaolin as material of partial replacement of portland cement in mortars

    Directory of Open Access Journals (Sweden)

    Marilia P. de Oliveira

    2006-06-01

    Full Text Available A utilização de argilas calcinadas na forma de metacaulinita, como material pozolânico para argamassas e concretos, tem recebido atenção considerável nos últimos anos. Este trabalho objetivou avaliar o desempenho mecânico de argamassas, nas quais foi utilizado um caulim calcinado proveniente do Estado da Paraíba, como material de substituição parcial do cimento Portland. Utilizaram-se duas finuras do caulim: passando nas peneiras ABNT 200 (0,074 mm e 325 (0,044 mm e calcinados nas temperaturas de 700, 800 e 900 ºC pelo tempo de 2 h. As amostras foram caracterizadas através de análise química, análise térmica diferencial, difração de raios-X e área específica. Obteve-se o índice de atividade pozolânica com a cal e o cimento Portland. O percentual de substituição adotado foi de 0, 10, 20, 30 e 40%. A relação aglomerante: areia foi de 1:1,5 e a relação água/aglomerante fixada igual 0,4. O efeito da substituição parcial do cimento na argamassa foi avaliado através da resistência à compressão simples, nas idades de 7, 28 e 90 dias. As argamassas estudadas apresentaram resistência superior em relação à da referência, até o nível de 30% de substituição.The use of burnt clays, in the metakaolin form, as pozzolanic material for mortars and concretes has received a remarkable attention in the last years. This paper aimed to evaluate the mechanical property of mortars, in which a calcined kaolin originating from the State of Paraiba, was used as partial cement replacement material. Two finess of the kaolin were used: ABNT 200 (0.074 mm and 325 (0.044 mm and burnt at temperatures of 700, 800 and 900 ºC for a period of 2 h. Both materials were characterized by chemical analysis, differential thermal analysis, X-ray diffraction, specific area tests. The pozolanic activity index was obtanied using lime and cement Portland. The amounts of replacement were 10, 20, 30 and 40%, besides the reference mortar. The binder

  8. Inorganic contaminants attenuation in acid mine drainage by fly ash and fly ash-ordinary Portland cement (OPC) blends : column experiments

    Energy Technology Data Exchange (ETDEWEB)

    Gitari, W.M. [Venda Univ., Thohoyandou (South Africa). Dept. of Ecology and Resources Management, School of Environmental Studies; Petrik, L.F.; Etchebers, O. [Western Cape Univ., Bellville (South Africa). Environmental and Nanosciences Group, Dept. of Chemistry; Key, D.L. [Western Cape Univ., Bellville (South Africa). Dept. of Chemistry; Okujeni, C. [Western Cape Univ., Bellville (South Africa). Dept. of Earth Sciences

    2010-07-01

    The infiltration of acid mine drainage (AMD) material into mine voids is one of the environmental impacts of underground coal mining. In this study, the mitigation of AMD in a mine void was simulated in laboratory conditions. Various mixtures of fly ash, solid residues, and Portland cement were added to packed columns over a 6-month period. The fly ash additions generated near-neutral to alkaline pH levels, which in turn induced precipitation, co-precipitation, and adsorption contaminant attenuation mechanisms. A modelling study demonstrated that the precipitation of ferrihydrite, Al-hydroxides, Al-oxyhydroxysulphates, gypsum, ettringite, manganite, and rhodochrosite lowered contaminant levels. Results of the study indicated that the pH regime and acidity level of the AMD strongly influenced both the leaching of the toxic trace elements as well as the attenuation of the AMD. 3 refs., 2 figs.

  9. Beta-tricalcium phosphate, white mineral trioxide aggregate, white Portland cement, ferric sulfate, and formocresol used as pulpotomy agents in primary pig teeth.

    Science.gov (United States)

    Shayegan, Amir; Petein, Michel; Abbeele, Astrid Vanden

    2008-04-01

    The purpose of this study was to evaluate and compare the effects of formocresol (FC), ferric sulfate (FS), white mineral trioxide aggregate (WMTA), white Portland cement (WPC), and beta-tricalcium phosphate (beta-TCP) on pulpotomized primary teeth of pigs. Fifty teeth of three 3-month old pigs were pulpotomized with these materials. Three weeks later, the animals were euthanized and the specimens were prepared for histological examination. There was no significant difference between beta-TCP, WMTA, and WPC in terms of primary pulp response, hard tissue formation, and normal pulp tissue preservation. But, both FS and FC irritated the pulp tissue, provoking a more inflammatory pulp response than beta-TCP, WMTA, and WPC. Beta-TCP, WMTA, and WPC are histologically more effective pulpotomy agents than formocresol and ferric sulfate in primary pig teeth.

  10. 磷石膏基水泥的早期水化性能研究%Early hydration properties of phosphogypsum-based cement

    Institute of Scientific and Technical Information of China (English)

    袁继峰; 刘彬; 董晓进

    2014-01-01

    研究了原样磷石膏、200℃煅烧磷石膏、800℃煅烧磷石膏制备的磷石膏水泥的力学性能(对应编号分别为:MPC-1、MPC-2和MPC-3),进行了不同改性磷石膏基水泥早期水化放热速率及28 d水化产物的测试分析。结果表明:煅烧磷石膏尤其高温煅烧磷石膏可发挥更好的硫酸盐激发效果,有效提高磷石膏基水泥的强度,尤其是早期强度。800℃煅烧磷石膏水泥MPC-3试样3、28 d强度分别为20.1、44.7 MPa,达到42.5R水泥强度等级要求;煅烧磷石膏基水泥的早期水化进程明显加快,相对MPC-1试样,MPC-2、MPC-3第二放热峰出现时间分别提前约10 h和17 h;磷石膏基水泥的水化产物主要为钙矾石和C-S-H凝胶,高温煅烧磷石膏基水泥水化产物更为密集。%Influence of phosphogypsum,200 ℃ calcined phosphogypsum and 800 ℃ calcined phosphogypsum on paste strength of modified phosphogypsum-based cement(No.:MPC-1 MPC-2 and MPC-3) were tested;Furthermore,early hydration exothermic rate and 28 d hydration products were systematically compared.Results showed that calcined phosphogypsum ,especially high temperature calcined phosphogypsum can play better stimulate sulfate effect,effectively improve strength of MPC,especially early strength.800 ℃ calcined phosphogypsum-based cement with the compressive strength 20.1 MPa at 3 d and 44.7 MPa at 28 d can meet the standard of Portland ce-ment of 42.5R grade in strengths.Early hydration process of MPC accelerated markedly ,the second exothermic peak of MPC-2 and MPC-3 can respectively advance for 10 h and 17 h relative to MPC-1.Hydration products of phosphogypsum-based cement were mainly ettringite and C-S-H gel,which were more intensive for MPC-2 and MPC-3.

  11. PURIFIED WASTE FCC CATALYST AS A CEMENT REPLACEMENT MATERIAL

    Directory of Open Access Journals (Sweden)

    Danute Vaiciukyniene

    2015-06-01

    Full Text Available Zeolites are commonly used in the fluid catalytic cracking process. Zeolite polluted with oil products and became waste after some time used. The quantity of this waste inevitably rises by expanding rapidly oil industry. The composition of these catalysts depends on the manufacturer and on the process that is going to be used. The main factors retarding hydration process of cement systems and modifying them strength are organic compounds impurities in the waste FCC catalyst. The present paper shows the results of using purified waste FCC catalyst (pFCC from Lithuania oil refinery, as Portland cement replacement material. For this purpose, the purification of waste FCC catalyst (FCC samples was treated with hydrogen peroxide. Hydrogen peroxide (H2O2 is one of the most powerful oxidizers known. By acting of waste with H2O2 it can eliminate the aforementioned waste deficiency, and the obtained product becomes one of the most promising ingredients, in new advanced building materials. Hardened cement paste samples with FCC or pFCC were formed. It was observed that the pFCC blended cements developed higher strength, after 28 days, compared to the samples with FCC or reference samples. Typical content of Portland cement substituting does not exceed 30 % of mass of Portland cement in samples. Reducing the consumption of Portland cement with utilizing waste materials is preferred for reasons of environmental protection.

  12. Considerations on the mechanical behavior and hydration process supersulphated cement (CSS) formulated with phosphogypsum; Consideracoes sobre a resistencia mecanica e o processo de hidratacao de cimentos supersulfatados (CSS) formulados com fosfogesso

    Energy Technology Data Exchange (ETDEWEB)

    Gracioli, Bruna; Varela, Maxwell Vinicius Favero; Beutler, Cheila Sirlene; Frare, Andreza; Luz, Caroline Angulski da; Pereira Filho, Jose Ilo, E-mail: maxwell@alunos.utfpr.edu.br, E-mail: cheila.beutler@gmail.com, E-mail: andreza2694@hotmail.com, E-mail: ilofilho@yahoo.com.br, E-mail: angulski@utfpr.edu.br [Universidade Tecnologica Federal do Parana (UTFPR), Pato Branco, PR (Brazil)

    2017-01-15

    Supersulfated Cements (SSC) are composed from blast furnace slag (90%), calcium sulfate (10-20%) and a small amount of alkali activator (up 5%). Gypsum is a conventional source of calcium sulfate, however, it can be replaced by phosphogypsum (PG), a byproduct from the production of phosphoric acid (H{sub 3}PO{sub 4}) with similar chemical and mineralogical composition of the gypsum. In Brazil, the production of this material is about 4.5 million tons per year. Because the SSC contains a higher calcium sulfate content (20%) in relation to Portland cement, a higher consumption of phosphogypsum is possible. The goal of this study was to investigate the phosphogypsum (PG) as an alternative source of calcium sulfate in order to obtain CSS. In addition to use of PG, the effects of both calcium sulfate and alkali activator content on the process of hydration were investigated. The results showed that SSC made with phosphogypsum met the minimum compressive strength required by the European standard for SSC (EN 15743/2010). Low heat of hydration rates mainly influenced by the low alkali activator content was observed. The excess of alkali activator (KOH) had different influences according to calcium sulfate content. In pastes made with low content (10%), 0.8% of KOH reduced the compressive strength, while in those with a high calcium sulfate content (20%) the high alkaline content resulted in the instability of ettringite. (author)

  13. In situ hydration of sulphoaluminate cement mixtures monitored by synchrotron x-ray diffraction

    Energy Technology Data Exchange (ETDEWEB)

    Turrillas, X. [Institut de Ciencia de Materials de Barcelona (ICMAB-CSIC), Barcelona (Spain); Martinez, L.G.; Carvalho, A.M.; Carezzato, G.L. [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil); Rossetto, C.M. [Faculdade de Tecnologia de Sao Paulo (FATEC), SP (Brazil)

    2016-07-01

    Full text: The hydration of calcium sulpho-aluminate cement mixtures was studied in situ by synchrotron X-ray diffraction at the XRD1 beamline of the Laboratorio Nacional de Luz Sincrotron (LNLS) in Campinas, SP. The powder specimens were introduced in borosilicate glass capillary tubes of 0.7 mm of internal diameter and imbued with deionized water. As the hydration reaction is very fast the capillaries were placed on the goniometer and the data collection was started after two minutes of mixing with water. The X-ray energy chosen to get an adequate flux for these short time acquisitions was 12 keV or more precisely 1.033258 Å, determined with polycrystalline corundum standard. Diffraction patterns were collected sequentially every 35 seconds for several hours at temperatures ranging from 40 degC to 55 degC with an accuracy better than 0.1 degC attained with the help of a hot air blower. The diffracted signal was collected with an array of twenty-four Mythen detectors at 760 mm from the capillary tube. The diffraction patterns had appropriate statistics to determine the kinetics of the reaction either by quantitative Rietveld analysis or by fitting isolated diffraction peaks to Gaussian curves as a function of time. The most important phases involved in the hydration are Klein´s salt, also known as Ye’elimite, Ca4(AlO2)6SO4, and gypsum, CaSO4.2H2O to yield Ettringite, Ca6Al2(SO4)3(OH)12 - 26H2O, phase responsible for the mechanical properties. (author)

  14. Effect of Exposure to Portland Cement Dust on the Periodontal Status and on the Outcome of Non-Surgical Periodontal Therapy

    Science.gov (United States)

    Abdelhamid, Alaa

    2016-01-01

    Background Cement dust contains heavy metals like nickel, cobalt, lead and chromium, pollutants hazardous to the biotic environment, with adverse impact for vegetation, human and animal health and ecosystems. Objective To investigate if long term exposure to cement dust can affect the periodontal health and affect the outcome of non-surgical periodontal therapy. Methods A total of sixty subjects were included in this study. Forty patients with chronic periodontitis were grouped into; Group I comprised of 20 patients with chronic periodontitis working in the Portland Cement Company and Group II comprised of 20 patients with chronic periodontitis who does not work in cement factories nor live near any of them. Twenty healthy subjects were included in this study as healthy control group (Group III). Clinical parameters including gingival index (GI), plaque index (PI), pocket depth (PD) and clinical attachment loss (CLA) were scored for all patients before and after periodontal therapy. All patients received non-surgical periodontal therapy together with strict oral hygiene program for one month. Gingival crevicular fluid (GCF) samples were collected from both groups at baseline and one month after periodontal therapy. Real time PCR (RT-PCR) was used to analyze the GCF samples for detection and assessment of the levels of IL-1β and TNFα. Results The two studied groups responded well to non-surgical periodontal treatment and there was no significant difference between GI and GII (P>0.05). The levels of TNFα was higher in GI than in GII before and after periodontal therapy (P0.05), but represented with a highly significant difference between G1 and GII after periodontal therapy (Psurgical periodontal treatment but it affects the levels of the pro-inflammatory mediators leading to more periodontal tissue destruction. PMID:27610057

  15. Relation between Portland cement carbonation, range of clinker burning and some expansive phenomena in the autoclave test

    Directory of Open Access Journals (Sweden)

    Ruiz de Cauna, A.

    1975-12-01

    Full Text Available Not availableEn este trabajo se estudia el doble pico que aparece en la región de altas temperaturas de las curvas derivatométricas, realizadas en atmósfera de vapor de agua, de los cementos portland anhidros e hidratados y en general el efecto de la carbonatación sobre los silicatos y aluminatos presentes en los cementos portland, especialmente sobre el perfil de las curvas derivatométricas de los cementos portland anhidros e hidratados. Se recogen y examinan los cambios experimentados en el doble pico al someter los cementos a la acción de diversos tratamientos y de agentes modificantes, tales como el tiempo, el CO2, la hidratación normal, las hidrataciones bajo agua a ebullición, en autoclave y en suspensión acuosa con agitación, la adición de puzolana y de fuertes proporciones de S04Ca. Se estudia y compara, asimismo, el comportamiento al análisis térmico bajo vapor de agua y al ensayo de autoclave de algunos clínkeres y cementos que presentan el doble pico en forma acusada y poco apreciable, respectivamente. De los resultados obtenidos se deducen conclusiones que explican los comportamientos experimentales observados. Las principales conclusiones se refieren a la interpretación de los picos que aparecen en las curvas derivatométricas o de velocidad de pérdida de peso de los cementos portland anhidros e hidratados, y a algunos aspectos de su carbonatación, a la probable existencia de un compuesto intermedio, consecuencia de la incompleta formación del silicato tricálcico y a la explicación de determinadas grandes expansiones producidas en el ensayo de autoclave.

  16. Effect of the use nickeliferous laterite and pumice as additives in the performance and durability of the Portland cement

    Directory of Open Access Journals (Sweden)

    María Carolina Rueda-Gualdrón

    2016-01-01

    Full Text Available En este trabajo se evalúa el comportamiento puzolánico de la laterita niquelífera de Cerromatoso (Córdoba y la pumita de Cemex (Boyacá en la preparación de morteros según normas NTC para agregados finos. Los morteros se prepararon con adiciones de 2,5%, 5% y 10% como sustitutos del cemento Portland tipo I, los cuales fueron sometidos a ensayos de resistencia mecánica antes y después de ser sometidos a ambientes extremos (altas temperaturas y ataques químicos como H2 SO4 y MgSO4 . Los resultados demuestran cómo estos materiales alternativos incrementan o disminuyen su grado de puzolanidad, así como el efecto de estos aditivos al interior de las mezclas de mortero en el tiempo, demostrando propiedades similares con relación a los morteros preparados con cemento Portland tipo I. Por lo tanto, los morteros tienen una respuesta aceptable ante las condiciones evaluadas, aunque es posible mejorar su desempeño y durabilidad, colaborando no solo con el ahorro energético en la producción del cemento Portland tipo I sino también en el uso de aditivos alternativos que permitan mitigar el impacto ambiental provocado por la industria cementera.

  17. Effect of Fly Ash and Silica Fume on Hydration Rate of Cement Pastes and Strength of Mortars

    Institute of Scientific and Technical Information of China (English)

    LIU Jun; ZHANG Yun; LIU Runqing; ZHANG Bing

    2014-01-01

    The effect of fly ash and silica fume on hydration rate and strength of cement in the early stage was studied. Contrast test was applied to the complex cementitious system to investigate the hydration rate. Combined with mechanical strength, the influence of fly ash and silica fume during the hydration process of complex binder was researched. The peak of the rate of hydration heat evolution and the mechanical strength decreased as the ratio of fly ash increased, however, as the ratio of silica fume increased, the peak of the rate of hydration heat evolution and the mechanical strength increased obviously. When the ratios of fly ash and silica fume are 10%and 5%, the peak of the rate of hydration heat evolution is the highest. At the same time 7 days of flexural and compressive strength are the highest as 8.89 MPa and 46.52 MPa, respectively. Fly ash and silica fume are the main factors affecting the hydration rate and the mechanical property.

  18. Assessment of Pozzolanic Activity Using Methods Based on the Measurement of Electrical Conductivity of Suspensions of Portland Cement and Pozzolan

    OpenAIRE

    Sergio Velázquez; JOSÉ M. MONZÓ; María V. Borrachero; Jordi Payá

    2014-01-01

    The use of methods based on measuring electrical conductivity to assess pozzolanic activity has recently been used primarily in aqueous suspensions of pozzolan: calcium hydroxide. However, the use of similar methods in suspensions of cement with pozzolans has not been widely studied. This paper proposes a new method for rapid assessment of the pozzolanic activity of mineral admixtures in aqueous cement suspensions. In this study, the conditions for the application of the method were optimized...

  19. Feasibility of using in situ fusion for the determination of Co, Cr and Mn in Portland cement by direct solid sampling graphite furnace atomic absorption spectrometry

    Science.gov (United States)

    Intima, Danielle Polidorio; de Oliveira, Elisabeth; Oliveira, Pedro Vitoriano

    2009-06-01

    In situ fusion on the boat-type graphite platform has been used as a sample pretreatment for the direct determination of Co, Cr and Mn in Portland cement by solid sampling graphite furnace atomic absorption spectrometry (SS-GF AAS). The 3-field Zeeman technique was adopted for background correction to decrease the sensitivity during measurements. This strategy allowed working with up to 200 µg of sample. The in situ fusion was accomplished using 10 µL of a flux mixture 4.0% m/v Na 2CO 3 + 4.0% m/v ZnO + 0.1% m/v Triton® X-100 added over the cement sample and heated at 800 °C for 20 s. The resulting mould was completely dissolved with 10 µL of 0.1% m/v HNO 3. Limits of detection were 0.11 µg g - 1 for Co, 1.1 µg g - 1 for Cr and 1.9 µg g - 1 for Mn. The accuracy of the proposed method has been evaluated by the analysis of certified reference materials. The values found presented no statistically significant differences compared to the certified values (Student's t-test, p < 0.05). In general, the relative standard deviation was lower than 12% ( n = 5).

  20. Potencial da cinza do bagaço da cana-de-açúcar como material de substituição parcial de cimento Portland Potential of sugarcane bagasse ash as a partial replacement material for Portland cement

    Directory of Open Access Journals (Sweden)

    Marcos O. de Paula

    2009-06-01

    Full Text Available Este trabalho, voltado para a avaliação do potencial da cinza do bagaço da cana-de-açúcar (CBC como material de substituição parcial do cimento Portland em argamassa, objetivou apresentar opção viável para a destinação deste resíduo, cuja quantidade gerada aumentará significativamente nos próximos anos, em decorrência da ampliação do setor de produção de álcool combustível; além disso, o emprego da CBC como adição mineral, substituindo parte do cimento em argamassas e concretos, contribui para a redução do impacto ambiental desses materiais, em boa parte decorrente da produção do cimento. O procedimento experimental abordou não só caracterização da CBC mas também a avaliação, através de ensaios físicos e mecânicos, em que os resultados mostraram que o bagaço apresenta rendimento de CBC de 10%, com a cinza sendo composta de 84% de SiO2 e 5% de Carbono. A sílica na CBC apresenta-se na fase amorfa e nas fases cristalinas de cristobalita e quartzo. Os índices de atividade pozolânica comprovam a reatividade da CBC. Do ponto de vista da resistência à compressão, argamassas com teores de CBC entre 0 e 30% indicaram a possibilidade de substituição de até 20% do cimento pela CBC.This study is focused on the evaluation of the effects of the partial replacement of Portland cement by sugarcane bagasse ash (CBC in mortars. The main objective was to find a suitable destination for an agricultural residue generated in an increasing amount in Brazil, as a result of the boom of the use of ethanol as an alternative fuel to gasoline. Also, the use of CBC as a mineral admixture in mortars and concretes contributes to a decrease in the environmental impact of these materials related to cement production. Experimental techniques were applied both for the CBC characterization and for the evaluation of its use as a mineral admixture in mortars, based on mechanical and physical tests. The yield of CBC from sugarcane

  1. Effect of hydrated lime and cement on moisture damage of recycled mixtures with foamed bitumen and emulsion

    OpenAIRE

    Nosetti, R.A.; Pérez Jiménez, Félix Edmundo; Martínez Reguero, Adriana Haydée; Miró Recasens, José Rodrigo

    2016-01-01

    Cold recycling with foamed bitumen can be used as a sustainable and cost-effective rehabilitation technique. This paper focuses on the evaluation of the resistance to the water action in mixtures with reclaimed asphalt pavement (RAP) and foamed bitumen by means of indirect tensile test, comparing the effect of two active fillers: cement and hydrated lime. Additionally, mixtures recycled with RAP and asphalt emulsions were also tested in order to compare the response of both technologies. Resu...

  2. Macrodefect-free cements: chemistry and impact of the environment

    Energy Technology Data Exchange (ETDEWEB)

    Drabik, M.; Galikova, L.; Mojumdar, S.C. [Slovak Academy of Sciences, Bratislava (Slovakia). Inst. of Inorganic Chemistry

    2002-07-01

    To control and improve the moisture resistance is a long felt necessity of the MDF cements, chemical approaches together with material science contribute to the progress. Present results support our previous hypothesis about the impregnation or barier effect of poly-P on the MDF cements and enlarge the validity of this hypothesis to the blends of SAFB clinker, Portland cement and HPMC or poly-P. Compactness of Al(Fe)-O-P cross-links increases the intrinsic density and, consequently, impregnates the system against the uptake of moisture. In a sense of the theory of functional polymers, the intensity of grafting of polymer chains to the surface of grains increases if poly-P is used and with the prolonged processing. The scope of moisture attack on MDF cements synthesized from the blends of SAFB clinker, Portland cement and HPMC or poly-P, as quantified using mass changes as measure of moisture resistance, is strongly affected by the nature of polymer. The addition of Portland cement in the raw mix improves the moisture resistance of MDF cements. Thermal analysis shows: (i) the irreversible mass gain of 3 - 10% is arisen from carbonation and secondary hydration of cement grains and (ii) the Al(Fe)-O-C(P) cross-links remain intact in the moist environment at either ambient or extreme levels of humidity. (orig.)

  3. Microscopic analysis of dog dental pulp after pulpotomy and pulp protection with mineral trioxide aggregate and white Portland cement Análise microscópica da polpa dental de cães após pulpotomia e proteção pulpar com agregado de trióxido mineral e cimento Portland branco

    Directory of Open Access Journals (Sweden)

    Renato Menezes

    2004-06-01

    Full Text Available Considering previous studies on the similarity between the chemical composition of the mineral trioxide aggregate and the Portland cement, the purpose of this study was to investigate the pulp response of dog's teeth after pulpotomy and direct pulp protection with MTA Angelus and white Portland cement. Thirty eight pulp remnants were protected with these materials. One hundred and twenty days after treatment, the animals were sacrificed and the specimens removed and prepared for histological analysis. Both materials demonstrated the same results when used as pulp capping materials, inducing hard tissue bridge formation and maintaining pulp vitality in all specimens. The MTA Angelus and the white Portland cement showed to be effective as pulp protection materials following pulpotomy.Considerando estudos anteriores sobre a similaridade entre a composição química do agregado de trióxido mineral e o cimento Portland, o objetivo deste estudo foi investigar a resposta pulpar de dentes de cães após pulpotomia e proteção pulpar direta com MTA Angelus e cimento Portland branco. Trinta e oito remanescentes pulpares foram recobertos com esses materiais. Cento e vinte dias após o tratamento, os animais foram sacrificados e os espécimes removidos e preparados para análise histológica. Ambos os materiais demonstraram os mesmos resultados quando utilizados como materiais de capeamento pulpar, induzindo a formação de ponte de tecido mineralizado e mantendo a vitalidade pulpar em todos os espécimes. Ambos matérias se mostraram efetivos como protetores pulpares após pulpotomia em dentes de cães.

  4. Gel/Space Ratio Evolution in Ternary Composite System Consisting of Portland Cement, Silica Fume, and Fly Ash

    Directory of Open Access Journals (Sweden)

    Mengxue Wu

    2017-01-01

    Full Text Available In cement-based pastes, the relationship between the complex phase assemblage and mechanical properties is usually described by the “gel/space ratio” descriptor. The gel/space ratio is defined as the volume ratio of the gel to the available space in the composite system, and it has been widely studied in the cement unary system. This work determines the gel/space ratio in the cement-silica fume-fly ash ternary system (C-SF-FA system by measuring the reaction degrees of the cement, SF, and FA. The effects that the supplementary cementitious material (SCM replacements exert on the evolution of the gel/space ratio are discussed both theoretically and practically. The relationship between the gel/space ratio and compressive strength is then explored, and the relationship disparities for different mix proportions are analyzed in detail. The results demonstrate that the SCM replacements promote the gel/space ratio evolution only when the SCM reaction degree is higher than a certain value, which is calculated and defined as the critical reaction degree (CRD. The effects of the SCM replacements can be predicted based on the CRD, and the theological predictions agree with the test results quite well. At low gel/space ratios, disparities in the relationship between the gel/space ratio and the compressive strength are caused by porosity, which has also been studied in cement unary systems. The ratio of cement-produced gel to SCM-produced gel ( G C to G S C M ratio is introduced for use in analyzing high gel/space ratios, in which it plays a major role in creating relationship disparities.

  5. SODIUM CITRATE INFLUENCE ON FORMATION OF CEMENT STONE IN THE ALUMINOUS BINDER

    Directory of Open Access Journals (Sweden)

    S. N. Leonovich

    2016-01-01

    Full Text Available The paper deals with the effect of sodium citrate on the formation of a cement stone in the aluminous binder. Formation of cement stone framework in cement hydraulic binder is accompanied with complicated physical and chemical processes of interphase interactions and dispersion, these processes are predicated on qualitative and quantitative composition of the cement mortar, continuous changes in its properties from preparation stage till curing. Addition of sodium citrate to tempering water enhances hydration of both Portland cement and calcium aluminate cement. Process pertaining to an increase of cement hydration rate is considered as a consequence of destruction in surface formations and exclusion of damping effect in respect of hydration rate and hydrolysis of products resulted from interaction of clinker material with tempering. It has been established that sodium citrate makes it possible to control processes of hydration, hydrolysis, binding and curing for cement mass. High degree of hydration of aluminous cement in the presence of sodium citrate provides fast binding and curing of binder, low porosity and rather high compression breaking strength of cement stone for all curing stages. An increase in concentration of sodium citrate in cement mixture up to 10 % of the cement mass exerts an influence not only on the process of cement mortar liquefaction, reduction of time for cement mass setting and hardening but also increases compression strength of cement stone. An analysis of the structure for cleavage surface of cement stone gives ground to declare that the addition of sodium citrate provides cement stone sealing and reduces its water absorption.

  6. On the effect of mixing on property development of cement pastes

    DEFF Research Database (Denmark)

    Geiker, Mette Rica; Bøhm, Anja; Kjeldsen, Ane Mette

    2006-01-01

    The method of mixing may affect the degree of agglomeration of particles in cement-based materials and thus the properties of the materials in their fresh, hardening, and hardened state. Paste (w/c=0.35) of white Portland cement with and without 10% silica fume and 0.65% superplasticizer were mixed...... was observed. The effect of mixing on development of hydration was not reflected in the resistance to migration of chloride ions in 28 days old samples....

  7. The influence of alkalinity of portland cement on the absorption characteristics of superabsorbent polymers (SAP) for use in internally cured concrete

    Science.gov (United States)

    Tabares Tamayo, Juan D.

    The concrete industry increasingly emphasizes advances in novel materials that promote construction of more resilient infrastructure. Due to its potential to improve concrete durability, internal curing (IC) of concrete by means of superabsorbent polymers (SAP) has been identified as one of the most promising technologies of the 21st century. The addition of superabsorbent polymers into a cementitious system promotes further hydration of cement by providing internal moisture during the hardening and strength development periods, and thus limits self-desiccation, shrinkage, and cracking. This thesis presents the work performed on the series of cement pastes with varying alkalinity of their pore solutions to provide a better understanding of: (1) the influence of the chemistry of the pore solution (i.e. its level of alkalinity and the type of ionic species present) on the absorption capacity of SAP, and (2) the effectiveness of SAP with different absorption capacities as an internal curing agent. This research work was divided into three stages: (a) materials characterization, (b) measurement of absorption capacity of SAP in synthetic pore solutions, and (c) evaluation of the internal curing effectiveness of SAP. During the first stage (Materials Characterization), pore solutions were extracted from the fresh (5 minutes old) cement pastes prepared using cements with three different levels of alkalinity. The pH values of the extracted solutions were determined (using the pH meter) and their chemical analysis was performed by means of titration (concentration of hydroxyl), ion chromatography (sulfates and chlorides), atomic absorption (AA) and inductively coupled plasma optical emission spectrometry (ICP) (sodium, potassium and calcium). The commercial SAP adopted for this study was used with "as-supplied" gradation and with the finer gradation obtained by grinding the original polymer in the 6850 Cryomilling Freezer/Mill. The physical properties of these SAP's, such

  8. THE HYDRATION OF AN ION-LEACHABLE GLASS USED IN GLASS-IONOMER CEMENTS

    Directory of Open Access Journals (Sweden)

    Jacek Klos

    2016-07-01

    Full Text Available A study is reported in which the interaction between a typical ionomer glass and water was evaluation in order to evaluate the importance of hydration in the setting of glass-ionomer cements. Glass G338 was mixed with water and the slurries were allowed to harden in metal moulds to create cylindrical specimens 6 mm high x 4 mm diameter. Samples of these specimens were found to disintegrate when placed in water. Following hardening at 37 °C for 1 hour in the moulds, one series of specimens was stored at 95% RH for 23 h, 1 week and 4 weeks, and the other stored for the same lengths of time, but sealed in the moulds. Raman spectra were recorded for glass G338 and glass-water blends stored for 24 hours and 4 weeks. The cylindrical specimens were found to have a degree of structural integrity, but proved to be extremely weak in compression (all specimens of whatever age up to 4 weeks having strengths of less that 1 MPa. Specimens lost mass on storage at 95% RH. Raman spectra showed no additional bands due to glass-water interactions compared with the dry glass itself, and changes in intensity were difficult to interpret, due to Fermi resonance in the regions of interest. It is concluded that binding in these specimens is due to hydrogen bonding between layers of water adsorbed onto glass powder surfaces.

  9. Solidificación-Estabilización de Cromo, Níquel y Plomo en una Matriz Sólida de Hormigón Fabricada con Cemento Portland Solidification-Stabilization of Chromium, Nickel and Lead in a Concrete Solid Matrix of Portland Cement

    Directory of Open Access Journals (Sweden)

    René A Lara-Díaz

    2009-01-01

    Full Text Available Se validó la técnica de cementación como alternativa para la solidificación-estabilización de residuos sintéticos de metales pesados, cromo, níquel y plomo, usando probetas sólidas de hormigón de cemento Portland. El proceso de cementación se realiza a partir de una mezcla base para obtener hormigón con resistencia a la compresión de 29.4 N/mm², los metales fueron incorporados como sales metálicas en el agua de amasado. Se realizaron pruebas de resistencia a la compresión, lixiviación de metales por la prueba PECT con absorción atómica y se calculó la eficiencia de retención. El hormigón fabricado con cemento Portland es adecuado para su uso en la solidificación-estabilización de níquel y plomo a una concentración máxima de 0.43% para níquel y 1.94% para plomo.The technique of cementation was validated as an alternative method for the solidification-stabilization of heavy metal synthetic wastes, chromium, nickel and lead, using concrete solid cylinders made of Portland cement. The cementation process takes place starting with a concrete mixture base with compressive strength of 29.4 N/mm². Metals were incorporated as metallic salts in the mixing water. Tests of compressive strength, leaching of metals by PECT with atomic absorption were performed and retention efficiencies were calculated. Concrete made with Portland cement is appropriate for the solidification-stabilization of nickel and lead, with maximum concentrations of 0.43% of nickel and 1.94% of lead in concrete.

  10. Continuous monitoring of the zinc-phosphate acid-base cement setting reaction by proton nuclear magnetic relaxation

    Science.gov (United States)

    Apih, T.; Lebar, A.; Pawlig, O.; Trettin, R.

    2001-06-01

    Proton nuclear magnetic relaxation is a well-established technique for continuous and non destructive monitoring of hydration of conventional Portland building cements. Here, we demonstrate the feasibility of nuclear magnetic resonance (NMR) monitoring of the setting reaction of zinc-phosphate acid-base dental cements, which harden in minutes as compared to days, as in the case of Portland cements. We compare the setting of cement powder (mainly, zinc oxide) prepared with clinically used aluminum-modified orthophosphoric acid solution with the setting of a model system where cement powder is mixed with pure orthophosphoric acid solution. In contrast to previously published NMR studies of setting Portland cements, where a decrease of spin-lattice relaxation time is attributed to enhanced relaxation at the growing internal surface, spin-lattice relaxation time T1 increases during the set of clinically used zinc-phosphate cement. Comparison of these results with a detailed study of diffusion, viscosity, and magnetic-field dispersion of T1 in pure and aluminum-modified orthophosphoric acid demonstrates that the increase of T1 in the setting cement is connected with the increase of molecular mobility in the residual phosphoric acid solution. Although not taken into account so far, such effects may also significantly influence the relaxation times in setting Portland cements, particularly when admixtures with an effect on water viscosity are used.

  11. Treating of cement during with supercritical fluid carbon dioxide

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Jae Min; Shin, Tae Wook; Whang, Jooho; Park Kwan Heun [Department of Nuclear Engineering, Kyunghee University, Yongin (Korea, Republic of)

    1999-07-01

    The main curing reactions of a portland cement are the formation of portlandite, Ca(OH){sub 2}, and calcium silicate hydrates, CSH. In nature, the cement extracts CO{sub 2} from air and convert the calcium hydroxide and CSH to calcium carbonate(CaCO{sub 3}), calcite. This process forms chemically stable and mechanically enhanced cement. By exposing an OPC to supercritical CO{sub 2}(SCCO2), the carbonate reaction was greatly accelerated. XRD analysis of compressive strength showed the mechanical enhancement.

  12. Assessment of Pozzolanic Activity Using Methods Based on the Measurement of Electrical Conductivity of Suspensions of Portland Cement and Pozzolan

    Science.gov (United States)

    Velázquez, Sergio; Monzó, José M.; Borrachero, María V.; Payá, Jordi

    2014-01-01

    The use of methods based on measuring electrical conductivity to assess pozzolanic activity has recently been used primarily in aqueous suspensions of pozzolan: calcium hydroxide. However, the use of similar methods in suspensions of cement with pozzolans has not been widely studied. This paper proposes a new method for rapid assessment of the pozzolanic activity of mineral admixtures in aqueous cement suspensions. In this study, the conditions for the application of the method were optimized, such as time, temperature, w/c ratio and dosage procedure. Finally, results are presented from the application of this method for characterizing the pozzolanic activity of the spent catalytic cracking catalyst. These results corroborate as previously reported, namely the high reactivity of this pozzolan obtained by other methods, such as thermogravimetry or evolution of the mechanical strength. In addition, the pozzolanic activity of the catalyst was compared with other pozzolans such as metakaolin and silica fume. PMID:28788261

  13. Assessment of Pozzolanic Activity Using Methods Based on the Measurement of Electrical Conductivity of Suspensions of Portland Cement and Pozzolan

    Directory of Open Access Journals (Sweden)

    Sergio Velázquez

    2014-11-01

    Full Text Available The use of methods based on measuring electrical conductivity to assess pozzolanic activity has recently been used primarily in aqueous suspensions of pozzolan: calcium hydroxide. However, the use of similar methods in suspensions of cement with pozzolans has not been widely studied. This paper proposes a new method for rapid assessment of the pozzolanic activity of mineral admixtures in aqueous cement suspensions. In this study, the conditions for the application of the method were optimized, such as time, temperature, w/c ratio and dosage procedure. Finally, results are presented from the application of this method for characterizing the pozzolanic activity of the spent catalytic cracking catalyst. These results corroborate as previously reported, namely the high reactivity of this pozzolan obtained by other methods, such as thermogravimetry or evolution of the mechanical strength. In addition, the pozzolanic activity of the catalyst was compared with other pozzolans such as metakaolin and silica fume.

  14. Grout Impregnation of Pre-Placed Recycled Concrete Pavement (RCP) for Rapid Repair of Deteriorated Portland Cement Concrete Airfield Pavement

    Science.gov (United States)

    2007-04-01

    Hammitt (1985) also reports a high failure rate when using cold mix asphalt for crater repairs and recommended that it be abandoned as a technique...cement-treated base, embankment base material, and aggregate for asphalt paving mixtures . RCP has been used successfully for all of these types of...that recycled asphalt pavement ( RAP ) and RCP have a substantial history of usage in pavement construction. He reports that cost savings of 20 to

  15. Quantitative Analysis of the Mineralogical Stages of the Clinkers of Portland Cement. Qualitative and Quantitative Analysis, by Infrared Spectroscopy of the Mineralogical Stages of the Clinker of Portland Cement

    Directory of Open Access Journals (Sweden)

    Käsner, Bernd

    1972-09-01

    Full Text Available Not availablePara la determinación cuantitativa de las fases mineralógicas del clinker de cemento portland, tan sólo se emplean el análisis microscópico y el de difracción de rayos X. Ambas técnicas exigen una preparación de muestras muy cuidadosa, lo que lleva bastante tiempo. A causa de estas circunstancias surge el interés de desarrollar un procedimiento con el que se pueda obtener resultados de exactitud y con poco trabajo, basado en la espectroscopia infrarroja. En principio existen dificultades, tanto en el método de trabajo como de interpretación de resultados. Por ejemplo, la formación y composición de las fases del clíñker se hallan sometidas a variaciones; por otra parte, aún no se ha llegado a elaborar un procedimiento para estudio por IR de sistemas que contengan varios componentes inorgánicos en estado sólido. Se ha pensado en la realización previa de análisis elementales, con los que se aclararían los de las fases minerales de los clínkeres, ya que no está aún suficientemente resuelto —a pesar de la importancia que esto representa— el análisis cuantitativo de estas fases.

  16. Studies on potential of Portland cement mortar for binding of waterworks sludge to reduce heavy metal leaching

    Indian Academy of Sciences (India)

    PARAMALINGGAM THANALECHUMI; ABDULL RAHIM MOHD YUSOFF; MOHANADOSS PONRAJ; HANIM AWAB

    2016-03-01

    The investigation of heavy metal leaching and physicochemical properties of cement-solidified waterworks sludge (CMWWS) formed by incorporating waterworks sludge (WWS) into cement mortar was carried out. The chemical composition, compressive strength and other physicochemical properties of the CMWWS cube specimens were determined using field emission scanning electron microscopy (FESEM), X-ray diffractometry (XRD) and Fourier transform-infrared spectroscopy (FTIR). The major type of chemical components present in CMWWS was found to be Al and Fe. The increasing amount of WWS added to cement mortar resulted in the increasing of organic matter, urchin-like morphology and clear peak intensity. At the end of 28 days of curing, the soaking solution became strongly basic and CMWWS cube specimens leached out higher amount of heavy metals. The compressive strength of CMWWS increased up to a WWS percentage of 10%, and basic (pH [ 7) curing solution was found to be better than water for curing purposes. It is concluded that solidification–stabilisation (S/S) technique is able to effectively reduce the leaching of heavy metals from the WWS and CMWWS containing up to 10% WWS can be used as construction material.

  17. Effect of metakaolin on strength and efflorescence quantity of cement-based composites.

    Science.gov (United States)

    Weng, Tsai-Lung; Lin, Wei-Ting; Cheng, An

    2013-01-01

    This study investigated the basic mechanical and microscopic properties of cement produced with metakaolin and quantified the production of residual white efflorescence. Cement mortar was produced at various replacement ratios of metakaolin (0, 5, 10, 15, 20, and 25% by weight of cement) and exposed to various environments. Compressive strength and efflorescence quantify (using Matrix Laboratory image analysis and the curettage method), scanning electron microscopy, and X-ray diffraction analysis were reported in this study. Specimens with metakaolin as a replacement for Portland cement present higher compressive strength and greater resistance to efflorescence; however, the addition of more than 20% metakaolin has a detrimental effect on strength and efflorescence. This may be explained by the microstructure and hydration products. The quantity of efflorescence determined using MATLAB image analysis is close to the result obtained using the curettage method. The results demonstrate the best effectiveness of replacing Portland cement with metakaolin at a 15% replacement ratio by weight.

  18. Examination of solidified and stabilized matrices as a result of solidification and stabilization process of arseniccontaining sludge with portland cement and lime

    Directory of Open Access Journals (Sweden)

    Tanapon Phenrat

    2004-02-01

    Full Text Available By solidification and stabilization (S/S with Portland cement and lime, it is possible to reduce arsenic concentration in leachate of the arsenic-containing sludge from arsenic removal process by coagulation with ferric chloride. From the initial arsenic concentration in leachate of unsolidified /unstabilized sludge which was around 20.75 mg/L, the arsenic concentrations in leachate of solidified/stabilized waste were reduced to 0.3, 0.58, 1.09, and 1.85 mg/L for the waste-to-binder ratios of 0.15, 0.25, 0.5, and 1, respectively, due tothe formation of insoluble calcium-arsenic compounds. To be more cost effective for the future, alternative uses of these S/S products were also assessed by measurement of compressive strength of the mortar specimens. It was found that the compressive strengths of these matrices were from 28 ksc to 461 ksc. In conclusion, considering compressive strength and leachability of the solidified matrices, some of these solidified/ stabilized products have potential to serve as an interlocking concrete paving block.

  19. Micro-observations of different types of nano-Al₂O₃on the hydration of cement paste with sludge ash replacement.

    Science.gov (United States)

    Luo, Huan-Lin; Lin, Deng-Fong; Shieh, Show-Ing; You, Yan-Fei

    2015-01-01

    In recent years, sewer systems and wastewater treatment plants have become important in developing countries. Consequently, the amount of sewage sludge produced by these countries has been gradually increasing, and determining how to properly recycle this sludge is becoming an important topic for researchers. In this study, to expand the recyclability of sewage sludge ash (SSA) in engineering applications, two types of nano-aluminium oxides (Al₂O₃), MC2A and MC2R, were added to SSA/cement paste and mortar specimens. The MC2R type (γ phase) had a smaller particle size and larger specific surface area than the MC2A type (α phase). The results indicate that the addition of nano-Al₂O₃to SSA/cement paste can effectively improve the hydration products of the paste. Moreover, the amount of hydration products increased as the amount of nano-Al₂O₃added to the SSA/cement paste increased. The test results indicate that MC2A nano-Al₂O₃can more uniformly distribute in the paste body and improve the hydration of cement than MC2R nano-Al₂O₃. Thus, more calcium-silicate-hydrate (C-S-H) gel and calcium aluminate hydrate (C-A-H) salts were produced, and the strength of the specimens was improved. This study suggests that MC2A nano-Al₂O₃is preferable to MC2R nano- Al₂O₃for SSA/cement specimen applications.

  20. Binary Effect of Fly Ash and Palm Oil Fuel Ash on Heat of Hydration Aerated Concrete

    Directory of Open Access Journals (Sweden)

    Taha Mehmannavaz

    2014-01-01

    Full Text Available The binary effect of pulverized fuel ash (PFA and palm oil fuel ash (POFA on heat of hydration of aerated concrete was studied. Three aerated concrete mixes were prepared, namely, concrete containing 100% ordinary Portland cement (control sample or Type I, binary concrete made from 50% POFA (Type II, and ternary concrete containing 30% POFA and 20% PFA (Type III. It is found that the temperature increases due to heat of hydration through all the concrete specimens especially in the control sample. However, the total temperature rises caused by the heat of hydration through both of the new binary and ternary concrete were significantly lower than the control sample. The obtained results reveal that the replacement of Portland cement with binary and ternary materials is beneficial, particularly for mass concrete where thermal cracking due to extreme heat rise is of great concern.

  1. Binary effect of fly ash and palm oil fuel ash on heat of hydration aerated concrete.

    Science.gov (United States)

    Mehmannavaz, Taha; Ismail, Mohammad; Radin Sumadi, Salihuddin; Rafique Bhutta, Muhammad Aamer; Samadi, Mostafa; Sajjadi, Seyed Mahdi

    2014-01-01

    The binary effect of pulverized fuel ash (PFA) and palm oil fuel ash (POFA) on heat of hydration of aerated concrete was studied. Three aerated concrete mixes were prepared, namely, concrete containing 100% ordinary Portland cement (control sample or Type I), binary concrete made from 50% POFA (Type II), and ternary concrete containing 30% POFA and 20% PFA (Type III). It is found that the temperature increases due to heat of hydration through all the concrete specimens especially in the control sample. However, the total temperature rises caused by the heat of hydration through both of the new binary and ternary concrete were significantly lower than the control sample. The obtained results reveal that the replacement of Portland cement with binary and ternary materials is beneficial, particularly for mass concrete where thermal cracking due to extreme heat rise is of great concern.

  2. Changes in constituent equilibrium leaching and pore water characteristics of a Portland cement mortar as a result of carbonation.

    Science.gov (United States)

    Garrabrants, A C; Sanchez, F; Kosson, D S

    2004-01-01

    Two equilibrium-based characterization protocols were applied to ground samples of a cement-based material containing metal oxide powders in both noncarbonated and carbonated states. The effects of carbonation were shown through comparison of (i) material buffering capacity, (ii) constituent equilibrium as a function of leachate pH, and (iii) constituent solubility and release as a function of liquid-to-solid (LS) ratio. As expected, the material alkalinity was significantly neutralized during carbonation. In addition, carbonation of the cement material led to the formation of calcium carbonate and a corresponding increase in arsenic release across the entire pH range. The solubility as a function of pH for lead and copper was lower in the alkaline pH range (pH>9) for carbonated samples compared with the parent material. When solubility and release as a function of LS ratio was compared, carbonation was observed to decrease calcium solubility, sodium and potassium release, and ionic strength. In response to carbonate solid formation, chloride and sulfate release as a function of LS ratio was observed to increase. Trends in constituent concentration as a function of LS ratio were extrapolated to estimate pore water composition at a 0.06 mL/g LS ratio. Significant differences were observed upon comparison of estimated pore water composition to leachate concentrations extracted at LS ratio of 5 mL/g. These differences show that practical laboratory extractions cannot be assumed directly representative of pore water concentrations.

  3. Solidification Coal Fly Ash on A Textile Factory as Allelochemi to Alternative Portland Cement Wall House Anti-Moss

    Directory of Open Access Journals (Sweden)

    Prabang Setyono

    2012-01-01