  1. Hot isostatic press waste option study report

    International Nuclear Information System (INIS)

    Russell, N.E.; Taylor, D.D.

    1998-02-01

    A Settlement Agreement between the Department of Energy and the State of Idaho mandates that all high-level radioactive waste now stored at the Idaho Chemical Processing Plant be treated so that it is ready to move out of Idaho for disposal by the target date of 2035. This study investigates the immobilization of all Idaho Chemical Processing Plant calcine, including calcined sodium bearing waste, via the process known as hot isostatic press, which produces compact solid waste forms by means of high temperature and pressure (1,050 C and 20,000 psi), as the treatment method for complying with the settlement agreement. The final waste product would be contained in stainless-steel canisters, the same type used at the Savannah River Site for vitrified waste, and stored at the Idaho National Engineering and Environmental Laboratory until a national geological repository becomes available for its disposal. The waste processing period is from 2013 through 2032, and disposal at the High Level Waste repository will probably begin sometime after 2065

  2. Hot isostatic press waste option study report

    Energy Technology Data Exchange (ETDEWEB)

    Russell, N.E.; Taylor, D.D.

    1998-02-01

    A Settlement Agreement between the Department of Energy and the State of Idaho mandates that all high-level radioactive waste now stored at the Idaho Chemical Processing Plant be treated so that it is ready to move out of Idaho for disposal by the target date of 2035. This study investigates the immobilization of all Idaho Chemical Processing Plant calcine, including calcined sodium bearing waste, via the process known as hot isostatic press, which produces compact solid waste forms by means of high temperature and pressure (1,050 C and 20,000 psi), as the treatment method for complying with the settlement agreement. The final waste product would be contained in stainless-steel canisters, the same type used at the Savannah River Site for vitrified waste, and stored at the Idaho National Engineering and Environmental Laboratory until a national geological repository becomes available for its disposal. The waste processing period is from 2013 through 2032, and disposal at the High Level Waste repository will probably begin sometime after 2065.

  3. Auxiliary equipment and special techniques used for hot isostatic pressing

    International Nuclear Information System (INIS)

    Pfeffer, J.B.; Odebo, U.

    1977-01-01

    The largest use for hot isostatic pressing (HIP) in production is in the consolidation of powder. In principle, powder is filled into a capsule of metal or glass, and the capsule is evacuated, sealed and loaded into the hot isostatic press. Consolidation takes place in the hot isostatic press, at which time the consolidated capsule is removed from the press and the encapsulation material is removed from the consolidated powder body. In both densification and defect healing, HIP is carried out without encapsulating the material. This is possible as the materials that lend themselves to HIP healing initially have a high density without communicating pores; therefore, the material acts as its own capsule. Considerations outside of the hot isostatic press that must be taken into account are examined. Information is included on powder manufacture, fabrication of capsules, powder handling, capsule sealing, and loading and unloading the press

  4. MICROSTRUCTURAL ANALYSIS OF HOT ISOSTATICALLY PRESSED AL-SIC

    NARCIS (Netherlands)

    Bronsveld, P.M.; Hosson, J.Th. De; Sargent, M.A.; Alsem, W.H.M.

    1991-01-01

    The difference between extruded and hot isostatically pressed (HIP) Al6061 both with a T6 final heat treatment and with a 30 wt.% SiC particulate reinforcement is one of densification. The higher density of the HIP material is not translated into a stronger material. The Mg2Si precipitation is

  5. Hot isostatic pressing of nanosized WC-Co hardmetals

    International Nuclear Information System (INIS)

    Azcona, I.; Ordonez, A.; Sanchez, J.M.; Castro, F.; Dominguez, L.

    2001-01-01

    A new technique based on hot isostatic pressing (HIP) has been developed to produce dense nanosized WC-Co hardmetals without the addition of grain growth inhibitors. The glass encapsulation process is the key for the effective application of isostatic pressure at temperatures well below those usually required for reaching the closed porosity state in the WC-Co system. Fully dense WC-Co samples with cobalt contents ranging from 10 to 12 wt. % have been obtained by this technique at temperatures between 1000 o C and 1200 o C with 150 MPa of applied isostatic pressure for 30 minutes. The role of isostatic pressure on the activation of densification mechanisms is discussed. (author)

  6. Bibliography on Hot Isostatic Pressing (HIP) Technology

    Science.gov (United States)

    1992-11-01

    Nimonic API, Rene’ 77 2. MA753, IN-853 7 3. C-103,WC-103 4. Alloy 454, PWA 1480 5. Mar- M250 , Maraging (250) 6. Rene 150, PA 101 (low C) 7. Inconel 718...Pressure Welding Parameters Bryant. W. A. Weld J 54 (12), 433-S-435-S, 1975 ( AD-DI02 316 Key Words: AISI 4340. MAR- M250 . AISI 1020, 9Ni-4Co steel. Inconel...creep rupture. hot corrosion, oxidation, grain size, thermomechanical treatment MAR- M250 1. Microstructures and Mechanical Properties of HIP

  7. Hot Isostatic Press (HIP) vitrification of radwaste concretes

    International Nuclear Information System (INIS)

    Siemer, D.D.; Scheetz, B.; Gougar, M.L.D.

    1995-01-01

    Properly formulated and properly ''canned'' radwaste concretes can be readily hot-isostatically-pressed (HIPed) into materials that exhibit performance equivalent to typical radwaste-type glasses. The HIPing conditions (temperature/pressure) required to turn a concrete waste form into a ''vitrified'' waste form are quite mild and therefore consistent with both safety and high productivity. This paper describes the process and its products with reference to its potential application to Idaho Chemical Processing Plant (ICPP) reprocessing wastes

  8. Hot isostatic pressing of glass-zeolite composites

    International Nuclear Information System (INIS)

    Hash, M.C.; Pereira, C.; Lewis, M.A.

    1996-01-01

    Glass-zeolite waste forms are being developed for immobilizing the chloride waste salt generated from the electrometallurgical treatment of spent fuel. Glass-zeolite composites with high densities were made using hot isostatic pressing (HIP) techniques. Processing parameters were investigated to yield desirable structural ceramic properties such as mechanical, chemical, and thermal stability. Limits for these parameters were determined by differential thermal and thermogravimetric analysis. The resulting ceramic properties such as bulk density, open or apparent porosity, and leach resistance were determined. In addition, phase equilibria and particle-size distribution were observed by optical light and electron microscopy. Pre-HIP processing techniques were also studied to ensure intimate mixing of the glass and zeolite powders. Particle size distributions resulting from dry blending procedure are appropriate for needed flow and packing characteristics

  9. Void formation in ODS EUROFER produced by hot isostatic pressing

    International Nuclear Information System (INIS)

    Ortega, Y.; Monge, M.A.; Castro, V. de; Munoz, A.; Leguey, T.; Pareja, R.

    2009-01-01

    Positron annihilation experiments were performed on oxide dispersion strengthened (ODS) and non-ODS EUROFER prepared by mechanical alloying and hot isostatic pressing. The results revealed the presence of small voids in these materials in the as-HIPed conditions. Their evolution under isochronal annealing experiments was investigated. The coincidence Doppler broadening spectra of ODS EUROFER exhibited a characteristic signature attributed to positron annihilation in Ar-decorated voids at the oxide particle/matrix interfaces. The variation of the positron annihilation parameters with the annealing temperature showed three stages: up to 623 K, between 823 and 1323 K, and above 1323 K. In the temperature range 823-1323 K void coarsening had effect. Above 1323 K some voids annealed out, but others, associated to oxide particles and small precipitates, survived to annealing at 1523 K. Transmission electron microscopy observations were also performed to verify the characteristics of the surviving defects after annealing at 1523 K.

  10. Void formation in ODS EUROFER produced by hot isostatic pressing

    Energy Technology Data Exchange (ETDEWEB)

    Ortega, Y. [Departamento de Fisica, Universidad Carlos III de Madrid, 28911 Leganes (Spain)], E-mail: yanicet@fis.ucm.es; Monge, M.A. [Departamento de Fisica, Universidad Carlos III de Madrid, 28911 Leganes (Spain); Castro, V. de [Department of Materials, University of Oxford, Oxford OX1 3PH (United Kingdom); Munoz, A.; Leguey, T.; Pareja, R. [Departamento de Fisica, Universidad Carlos III de Madrid, 28911 Leganes (Spain)

    2009-04-30

    Positron annihilation experiments were performed on oxide dispersion strengthened (ODS) and non-ODS EUROFER prepared by mechanical alloying and hot isostatic pressing. The results revealed the presence of small voids in these materials in the as-HIPed conditions. Their evolution under isochronal annealing experiments was investigated. The coincidence Doppler broadening spectra of ODS EUROFER exhibited a characteristic signature attributed to positron annihilation in Ar-decorated voids at the oxide particle/matrix interfaces. The variation of the positron annihilation parameters with the annealing temperature showed three stages: up to 623 K, between 823 and 1323 K, and above 1323 K. In the temperature range 823-1323 K void coarsening had effect. Above 1323 K some voids annealed out, but others, associated to oxide particles and small precipitates, survived to annealing at 1523 K. Transmission electron microscopy observations were also performed to verify the characteristics of the surviving defects after annealing at 1523 K.

  11. Ductility in hot isostatically pressed 250-grade maraging steel

    International Nuclear Information System (INIS)

    German, R.M.; Smugeresky, J.E.

    1978-01-01

    Prealloyed 250-grade maraging steel powder produced by the rotating electrode process was fully consolidated by hot isostatic pressing (HIP) at 1100 and 1200 0 C. The strength following aging (3 h at 480 0 C) equalled that of wrought material; however, ductility was negligible. This lack of ductility in the powder metallurgy product was traced to titanium segregation which occurred at the powder surface during power production. The formation of a titanium intermetallic at the prior particle boundaries during aging caused failure at low plastic strains. Altered aging treatments successfully broke up the embrittling film and resulted in a significant ductility recovery for the HIP material. Analysis of the fracture process indicates that further ductility gains are possible by reducing the titanium content, refining the particle size, and optimizing the thermal cycles

  12. Ductile Fracture Behaviour of Hot Isostatically Pressed Inconel 690 Superalloy

    Science.gov (United States)

    Cooper, A. J.; Brayshaw, W. J.; Sherry, A. H.

    2018-04-01

    Herein we assess the differences in Charpy impact behavior between Hot Isostatically Pressed and forged Inconel 690 alloy over the temperature range of 300 °C to - 196 °C. The impact toughness of forged 690 exhibited a relatively small temperature dependence, with a maximum difference of ca. 40 J measured between 300 °C and - 196 °C, whereas the HIP'd alloy exhibited a difference of approximately double that of the forged alloy over the same temperature range. We have conducted Charpy impact testing, tensile testing, and metallographic analyses on the as-received materials as well as fractography of the failed Charpy specimens in order to understand the mechanisms that cause the observed differences in material fracture properties. The work supports a recent series of studies which assess differences in fundamental fracture behavior between Hot Isostatically Pressed and forged austenitic stainless steel materials of equivalent grades, and the results obtained in this study are compared to those of the previous stainless steel investigations to paint a more general picture of the comparisons between HIP vs forged material fracture behavior. Inconel 690 was selected in this study since previous studies were unable to completely omit the effects of strain-induced martensitic transformation at the tip of the Chary V-notch from the fracture mechanism; Inconel 690 is unable to undergo strain-induced martensitic transformation due to the alloy's high nickel content, thereby providing a sister study with the omission of any martensitic transformation effects on ductile fracture behavior.

  13. Process and equipment development for hot isostatic pressing treatability study

    Energy Technology Data Exchange (ETDEWEB)

    Bateman, Ken; Wahlquist, Dennis; Malewitz, Tim

    2015-03-01

    Battelle Energy Alliance (BEA), LLC, has developed processes and equipment for a pilot-scale hot isostatic pressing (HIP) treatability study to stabilize and volume reduce radioactive calcine stored at Idaho National Laboratory (INL). In 2009, the U. S. Department of Energy signed a Record of Decision with the state of Idaho selecting HIP technology as the method to treat 5,800 yd^3 (4,400 m^3) of granular zirconia and alumina calcine produced between 1953 and 1992 as a waste byproduct of spent nuclear fuel reprocessing. Since the 1990s, a variety of radioactive and hazardous waste forms have been remotely treated using HIP within INL hot cells. To execute the remote process at INL, waste is loaded into a stainless-steel or aluminum can, which is evacuated, sealed, and placed into a HIP furnace. The HIP simultaneously heats and pressurizes the waste, reducing its volume and increasing its durability. Two 1 gal cans of calcine waste currently stored in a shielded cask were identified as candidate materials for a treatability study involving the HIP process. Equipment and materials for cask-handling and calcine transfer into INL hot cells, as well as remotely operated equipment for waste can opening, particle sizing, material blending, and HIP can loading have been designed and successfully tested. These results demonstrate BEA’s readiness for treatment of INL calcine.

  14. Densification of boron carbide at relatively low temperatures by hot pressing and hot isostatic pressing

    International Nuclear Information System (INIS)

    Telle, R.

    1988-01-01

    The poor sinterability of B 4 C limits its widespread application because both high temperatures and high pressures are required for a complete densification. Moreover, B 4 C suffers from a low strength and fracture toughness, possesses, however, a high potential because of its extreme hardness. Reaction hot pressing of B 4 C-WC-TiC-Si-Co mixtures resulting in B 4 C-TiB 2 -W 2 B 5 composites of high density exhibit remarkable mechanical properties. The influence of hot isostatic pressing (HIP) on the microstructure and the mechanical properties is investigated in cooperation with participants of the COST 503 activities and related to the strengthening and toughening mechanisms. Difficulties during densification by HIP arise from the evaporation of adsorbed volatiles as well as from the strong swelling of the powder compact due to the sintering reaction. Several HIP cycle designs were tested in order to prevent the bloating of the capsule and to control internal stresses due to the misfit of the thermal expansion of the entire phases. In comparison to single phase B 4 C ceramics, bending strength was improved to 1030 MPa, K Ic to 5.2 MPa/m, while hardness was comparable with HV1=38 GPa. Wear test were performed and related to the toughening mechanisms. (orig.) With 56 refs., 9 tabs., 64 figs

  15. Effect of hot isostatic pressing on reaction-bonded silicon nitride

    Science.gov (United States)

    Watson, G. K.; Moore, T. J.; Millard, M. L.

    1984-01-01

    Specimens of nearly theoretical density have been obtained through the isostatic hot pressing of reaction-bonded silicon nitride under 138 MPa of pressure for two hours at 1850, 1950, and 2050 C. An amorphous phase that is introduced by the hot isostatic pressing partly accounts for the fact that while room temperature flexural strength more than doubles, the 1200 C flexural strength increases significantly only after pressing at 2050 C.

  16. First wall and shield components manufacturing by hot isostatic pressing

    International Nuclear Information System (INIS)

    Lind, Anders; Tegman, R.

    1994-01-01

    At a meeting in Garching in June 1994 Hot Isostatic Pressing (HIP) was presented as a possible route to manufacture ITER first wall and shield components. The main advantages of the HIP concept include excellent and uniform mechanical properties of the produced materials and joints, high reliability and robustness of the HIP process, double containment of coolant, good flexibility concerning general design as well as size and location for inner cooling tubes, low cost and short delivery times, and a good near net shape capability for components in size up to 15 tons. To assess the applicability of HIP for the manufacturing of ITER first wall and shield components, it was agreed * to choose possible production parameters based in the present know-how, * to produce a compound mock-up in one shot from available solid steel/powder copper/steel tubes to demonstrate the joinability of the materials, * to examine the produced mock-up/materials by multi array ultrasonic testing, limited mechanical testing, metallography, scanning electron microscopy and energy dispersive spectroscopy, and * to compile data on Type 316L steels produced by HIP. Preliminary results and the mock-up were presented at a meeting in Garching in mid July 1994. This study clearly shows the excellent joinability of a copper alloy (Cu-0.5%Zr) and stainless steels (Type 304, 316 L) by HIP at temperatures close to the melting temperature of copper, with only limited influence on the microstructures, which makes it possible to HIP the first wall and shield structure in one step. Excellent mechanical properties of the compound are obtained with the copper alloy and not the joint being the weakest part. 7 refs, 21 figs, 1 tab

  17. Void formation in ODS EUROFER produced by hot isostatic pressing

    Energy Technology Data Exchange (ETDEWEB)

    Ortega, Y.; Monge, M.A.; Munoz, A.; Leguey, T.; Pareja, R. [Madrid Univ. Carlos-3, Dept. de Fisica (Spain); Castro, V. de [Oxford Univ., Dept. of Materials (United Kingdom)

    2007-07-01

    Full text of publication follows: An obstacle in the development of oxide dispersion strengthened (ODS) steels for structural applications in fusion reactors is the toughness lack of the material produced by powder metallurgy and consolidated by hot isostatic pressing (HIP). In particular, ODS EUROFER steel with Y{sub 2}O{sub 3} particles appears to exhibit poor impact properties. To asses the capabilities of this material, it is necessary elucidate if its failure is an inherent characteristic of the production process that can not be mitigated by normalizing and tempering treatments. In order to investigate this particular point, the evolution of the structural defects retained in the ODS material during isochronal annealing has been probed by positron annihilation spectroscopy. The present study has been performed on bail milled EUROFER powders consolidated by HIP, containing 0.25 wt % Y{sub 2}O{sub 3} and without Y{sub 2}O{sub 3}. For comparison, un-milled EUROFER powder consolidated under identical conditions, and as-received EUROFER97 plate produced by Boehler AG have been also investigated. Samples from these four materials were isochronally annealed for 90 min up to 1323 K. Materials produced from milled powders had a longer positron lifetime than the one produced from un-milled powder or the EUROFER plate. In the material containing Y{sub 2}O{sub 3}, i.e. in ODS EUROFER, annealing above 723 K produced a continuous increase in the mean positron lifetime <{tau}> up to reach a maximum value of 208 ps after annealing at 1223 K. A similar annealing behavior was observed for Y{sub 2}O{sub 3}-free milled EUROFER (milled EUROFER), but the <{tau}> value steeply changed from {approx}160 ps at 823 K to {approx}200 ps after annealing at 1023 K. Subsequent anneals above this temperature produced meaningless changes in <{tau}>. The <{tau}> increase in milled EUROFER was accompanied by the intensity increase of a lifetime component of {approx}360 ps that is characteristic

  18. Atlas of hot isostatic beryllium powder pressing diagrams

    International Nuclear Information System (INIS)

    Stoev, P.I.; Papirov, I.I.; Tikhinskij, G.F.; Vasil'ev, A.A.

    1995-01-01

    Diagrams of hot isotopic pressing (HIP) of beryllium powder with different grain size in a wide range of pressing parameters are built by mathematical modeling methods. The HIP diagrams presented are divided into 3 groups: parametric dependencies D=f(P,T); technological HIP diagrams; compacting mechanisms. The created data bank permits to optimise beryllium powder HIP with changing parameters. 4 refs., 23 figs

  19. Effect of hot isostatic pressing on the properties of sintered alpha silicon carbide

    Science.gov (United States)

    Watson, G. K.; Moore, T. J.; Millard, M. L.

    1985-01-01

    Two lots of alpha silicon carbide were isostatically hot-pressed under 138 MPa for 2 h in Ar at temperatures up to 2200 C. Nearly theoretically dense specimens resulted. Hot isostatic pressing increased both room-temperature strength and 1200 C strength, and resulted in improved reliability. One lot of material which was pressed at 2200 C showed increases of about 20 percent in room-temperature strength and about 50 percent in 1200 C flexural strength; the Weibull modulus improved about 100 percent.

  20. High density crystalline boron prepared by hot isostatic pressing in refractory metal containers

    Science.gov (United States)

    Hoenig, C.L.

    1993-08-31

    Boron powder is hot isostatically pressed in a refractory metal container to produce a solid boron monolith with a bulk density at least 2.22 g/cc and up to or greater than 2.34 g/cc. The refractory metal container is formed of tantalum, niobium, tungsten, molybdenum or alloys thereof in the form of a canister or alternatively plasma sprayed or chemical vapor deposited onto a powder compact. Hot isostatic pressing at 1,800 C and 30 PSI (206.8 MPa) argon pressure for four hours produces a bulk density of 2.34 g/cc. Complex shapes can be made.

  1. Defect structures in MgB2 wires introduced by hot isostatic pressing

    International Nuclear Information System (INIS)

    Liao, X Z; Serquis, A; Zhu, Y T; Civale, L; Hammon, D L; Peterson, D E; Mueller, F M; Nesterenko, V F; Gu, Y

    2003-01-01

    The microstructures of MgB 2 wires prepared by the powder-in-tube technique and subsequent hot isostatic pressing were investigated using transmission electron microscopy. A large amount of crystalline defects including small-angle twisting, tilting and bending boundaries, in which high densities of dislocations reside, was found forming sub-grains within MgB 2 grains. It is believed that these defects resulted from particle deformation during the hot isostatic pressing process and are effective flux pinning centres that contribute to the high critical current densities of the wires at high temperatures and at high fields

  2. Hot isostatic-pressing diagrams for fine-particle beryllium powders

    International Nuclear Information System (INIS)

    Stoev, P.I.; Papirov, I.I.; Tikhinskij, G.F.; Vasil'ev, A.A.

    1995-01-01

    Charts of hot isostatic pressing (HIP) for 4 and 8 μm grain beryllium powders are plotted. Values of thickening rates are calculated and their dependences on HIP pressure and temperature are plotted. It is shown, that the relative density powder at growth of HIP pressure and temperature

  3. Flux pinning in hot isostatically pressed Bi2Sr2CaCu2Ox

    International Nuclear Information System (INIS)

    Miller, D.J.; Sengupta, S.; Hettinger, J.D.; Shi, D.; Gray, K.E.; Nash, A.S.; Goretta, K.C.

    1992-01-01

    Magnetic hysteresis data were taken from 4.2 to 35 K on Bi 2 Sr 2 CaCu 2 O x samples that were hot isostatically pressed at 105 MPa in an inert atmosphere at 825 degree C. One set of samples was pressed for only 15 min while the other was pressed for 120 min. The samples pressed for 15 min contained a high density of dislocations and planar faults, while the samples pressed for 120 min contained fewer dislocations and faults, with most dislocations present within subgrain boundaries. The samples with the complex dislocation/planar fault structures exhibited substantially larger hysteresis loops, suggesting enhanced flux pinning

  4. Encapsulation of krypton-85 in zeolite molecular sieve with a hot isostatic press

    International Nuclear Information System (INIS)

    Christensen, A.B.; DelDebbio, J.A.; Knecht, D.A.; Tanner, J.E.

    1986-01-01

    This paper describes pilot and full-scale experiments which demonstrated the feasibility of immobilizing Kr-85 in a zeolite 5A/glass mixture and compacting it before disposal. The full volume of a one-liter hot isostatic press (HIP) was used to trap argon in zeolite 5A. For radioactive krypton the HIP was modified to isolate the Kr-85 in the work zone. Details of the HIP modifications, experimental procedure, and sample analysis are reported

  5. Consolidation of W–Ta composites: Hot isostatic pressing and spark and pulse plasma sintering

    Energy Technology Data Exchange (ETDEWEB)

    Dias, M., E-mail: marta.dias@itn.pt [Instituto de Plasmas e Fusão Nuclear, Instituto Superior Técnico, Universidade de Lisboa, Av. Rovisco Pais, 1049-001 Lisboa (Portugal); Guerreiro, F. [Instituto de Plasmas e Fusão Nuclear, Instituto Superior Técnico, Universidade de Lisboa, Av. Rovisco Pais, 1049-001 Lisboa (Portugal); Correia, J.B. [LNEG, Laboratório Nacional de Energia e Geologia, Estrada do Paço do Lumiar, 1649-038 Lisboa (Portugal); Galatanu, A. [National Institute of Materials Physics, Atomistilor 105 bis Bucharest-Magurele, 077125 Ilfov (Romania); Rosiński, M. [Warsaw University of Technology, Faculty of Materials Science and Engineering, Warsaw (Poland); Monge, M.A.; Munoz, A. [Departamento de Física, Univerdidad Carlos III de Madrid, Avd. de la Universidad 30, 28911 Madrid (Spain); Alves, E. [Instituto de Plasmas e Fusão Nuclear, Instituto Superior Técnico, Universidade de Lisboa, Av. Rovisco Pais, 1049-001 Lisboa (Portugal); Carvalho, P.A. [Instituto de Plasmas e Fusão Nuclear, Instituto Superior Técnico, Universidade de Lisboa, Av. Rovisco Pais, 1049-001 Lisboa (Portugal); CeFEMA, Instituto Superior Técnico, Universidade de Lisboa, Av. Rovisco Pais, 1049-001 Lisboa (Portugal)

    2015-10-15

    Highlights: • Consolidation of W–Ta composites using three techniques: HIP, SPS and PPS. • Comparison of consolidation methods in terms of W–Ta interdiffusion and densification. • Microstructure analysis in terms of oxides formation. - Abstract: Composites consisting of tantalum fiber/powder dispersed in a nanostructured W matrix have been consolidated by spark and pulse plasma sintering as well as by hot isostatic pressing. The microstructural observations revealed that the tungsten–tantalum fiber composites consolidated by hot isostatic pressing and pulse plasma sintering presented a continuous layer of Ta{sub 2}O{sub 5} phase at the W/Ta interfaces, while the samples consolidated by spark plasma sintering evidenced a Ta + Ta{sub 2}O{sub 5} eutectic mixture due to the higher temperature of this consolidation process. Similar results have been obtained for the tungsten–tantalum powder composites. A (W, Ta) solid solution was detected around the prior nanostructured W particles in tungsten–tantalum powder composites consolidated by spark and pulse plasma sintering. Higher densifications were obtained for composites consolidated by hot isostatic pressing and pulse plasma sintering.

  6. Effect of Temperature on the Fracture Toughness of Hot Isostatically Pressed 304L Stainless Steel

    Science.gov (United States)

    Cooper, A. J.; Brayshaw, W. J.; Sherry, A. H.

    2018-03-01

    Herein, we have performed J- Resistance multi-specimen fracture toughness testing of hot isostatically pressed (HIP'd) and forged 304L austenitic stainless steel, tested at elevated (300 °C) and cryogenic (- 140 °C) temperatures. The work highlights that although both materials fail in a pure ductile fashion, stainless steel manufactured by HIP displays a marked reduction in fracture toughness, defined using J 0.2BL, when compared to equivalently graded forged 304L, which is relatively constant across the tested temperature range.

  7. Effect of Temperature on the Fracture Toughness of Hot Isostatically Pressed 304L Stainless Steel

    OpenAIRE

    Cooper, Adam J.; Sherry, Andrew

    2018-01-01

    Herein, we have performed J-Resistance multi-specimen fracture toughness testing of hot isostatically pressed (HIP’d) and forged 304L austenitic stainless steel, tested at elevated (300 °C) and cryogenic (− 140 °C) temperatures. The work highlights that although both materials fail in a pure ductile fashion, stainless steel manufactured by HIP displays a marked reduction in fracture toughness, defined using J0.2BL, when compared to equivalently graded forged 304L, which is relatively constant...

  8. FeCrAl and Zr alloys joined using hot isostatic pressing for fusion energy applications

    International Nuclear Information System (INIS)

    Park, Dong Jun; Kim, Hyun Gil; Park, Jeong Yong; Jung, Yang Il; Park, Jung Hwan; Koo, Yang Hyun

    2016-01-01

    Highlights: • FeCrAl and Zr alloys were successfully joined by hot isostatic pressing (HIP). • The thickness of diffusion layer increased with an increase in HIP temperature. • Significant inter-diffusion was observed for HIP at 1150 °C. • Maximum joint strength was achieved at HIP temperature of 700 °C. - Abstract: FeCrAl and Zr alloys were joined by a hot isostatic pressing (HIP) method for fusion energy applications. The optimum conditions for the joining process were studied. The HIP temperatures were varied from 700 to 1050 °C. The mechanical properties of the HIPed samples were evaluated by four-point bending and tensile tests. The FeCrAl and Zr alloys HIPed at 700 °C showed higher joint strength than the other samples. The joint strength decreased with an increase in the HIP temperature from 700 to 950 °C and significantly dropped at 1050 °C. Transmission electron microscopy, scanning electron microscopy, and optical microscopy were used to characterize the joints and interface region of the HIPed samples. The joints appeared to be tightly bonded and no intermetallic compounds or gaps were observed at the interface for HIP temperatures up to 950 °C. A diffusion layer formed at the interface and its thickness increased with the HIP temperature. HIP at 1050 °C, on the other hand, resulted in significant inter-diffusion and formation of brittle inter-metallic compounds at the interface.

  9. Strength-toughness relations in sintered and isostatically hot-pressed ZrO2-toughened Al2O3

    International Nuclear Information System (INIS)

    Hori, S.; Yoshimura, M.; Somiya, S.

    1986-01-01

    The fracture toughness of fine-grained undoped ZrO 2 -toughened Al 2 O 3 (ZTA) was essentially unchanged by post-sintering hot isostatic pressing and increased monotonically with ZrO 2 additions up to 25 wt%. The strength of ZTA with 5 to 15 wt% tetragonal ZrO 2 , which depended monotonically on the amount of ZrO 2 present before hot isostatic pressing, was increased by pressing but became almost constant between 5 and 15 wt% ZrO 2 addition. The strength appeared to be controlled by pores before pressing and by surface flaws after pressing; the size of flaws after pressing increased with ZrO 2 content. The strength of ZTA containing mostly monoclinic ZrO 2 (20 to 25 wt%) remained almost constant despite the noticeable density increase upon hot isostatic pressing because the strength was controlled by preexisting microcracks whose extent did not change on postsintering pressing. These strength-toughness relations in sintered and isostatically hot-pressed ZTA are explained on the basis of R-curve behavior. The importance of the contribution of microcracks to the toughness of ZTA is emphasized

  10. Expanded Analysis of Hot Isostatic Pressed Iodine-Loaded Silver-Exchanged Mordenite

    Energy Technology Data Exchange (ETDEWEB)

    Jubin, R. T. [ORNL; Bruffey, S. H. [ORNL; Patton, K. K. [ORNL

    2014-09-30

    Reduced silver-exchanged mordenite (Ag0Z) is being evaluated as a potential material to control the release of radioactive iodine that is released during the reprocessing of used nuclear fuel into the plant off-gas streams. The purpose of this study was to determine if hot pressing could directly convert this iodine loaded sorbent into a waste form suitable for long-term disposition. The minimal pretreatment required for production of pressed pellets makes hot pressing a technically and economically desirable process. Initial scoping studies utilized hot uniaxial pressing (HUPing) to prepare samples of non-iodine-loaded reduced silver exchanged mordenite (Ag0Z). The resulting samples were very fragile due to the low pressure (~ 28 MPa) used. It was recommended that hot isostatic pressing (HIPing), performed at higher temperatures and pressures, be investigated. HIPing was carried out in two phases, with a third and final phase currently underway. Phase I evaluated the effects of pressure and temperature conditions on the manufacture of a pressed sample. The base material was an engineered form of silver zeolite. Six samples of Ag0Z and two samples of I-Ag0Z were pressed. It was found that HIPing produced a pressed pellet of high density. Analysis of each pressed pellet by scanning electron microscopy-energy dispersive spectrophotometry (SEM-EDS) and X-ray diffraction (XRD) demonstrated that under the conditions used for pressing, the majority of the material transforms into an amorphous structure. The only crystalline phase observed in the pressed Ag0Z material was SiO2. For the samples loaded with iodine (I-Ag0Z) iodine was present as AgI clusters at low temperatures, and transformed into AgIO4 at high temperatures. Surface mapping and EDS demonstrate segregation between silver iodide phases and silicon dioxide phases. Based on the results of the Phase I study, an expanded test matrix was developed to examine the effects of multiple source materials, compositional

  11. Processing and properties of calcium phosphates bioceramics by hot isostatic pressing

    Directory of Open Access Journals (Sweden)

    Boilet Laurent

    2013-11-01

    Full Text Available Stoichiometric β-tricalcium phosphate (β-TCP, hydroxyapatite (HA and biphasic calcium phosphate (TCP/HA 60/40 %wt, BCP40 powders were synthesized by chemical precipitation of aqueous solutions of diammonium phosphate and calcium nitrate. After a calcination treatment and a milling step, powders were shaped by slip-casting. The sintering temperature effect on the density and the average grain size was investigated. By natural sintering, densities between 98 and 99.8% were obtained. Hot Isostatic Pressing (HIP treatment was carried out after a pre-sintering of these materials. Transparent or translucent samples were obtained, indicating a relative density very close to the theoretical value (>99.9%. Mechanical properties (three-point bending strength, fracture toughness, Young's modulus and Vickers hardness were measured on hipped materials with similar grain size (∼0.7μm.

  12. Characterization of 316L(N)-IG SS joint produced by hot isostatic pressing technique

    International Nuclear Information System (INIS)

    Nakano, J.; Miwa, Y.; Tsukada, T.; Kikuchi, M.; Kita, S.; Nemoto, Y.; Tsuji, H.; Jitsukawa, S.

    2002-01-01

    Type 316L(N) stainless steel of the international thermonuclear experimental reactor grade (316L(N)-IG SS) is being considered for the first wall/blanket module. Hot isostatic pressing (HIP) technique is expected for the fabrication of the module. To evaluate the integrity and susceptibility to stress corrosion cracking (SCC) of HIPed 316L(N)-IG SS, tensile tests in vacuum and slow strain rate tests in high temperature water were performed. Specimen with the HIPed joint had similar tensile properties to specimens of 316L(N)-IG SS, and did not show susceptibility to SCC in oxygenated water at 423 K. Thermally sensitized specimen was low susceptible to SCC even in the creviced condition. It is concluded that the tensile properties of HIPed SS are as high as those of the base alloy and the HIP process caused no deleterious effects

  13. Room temperature deformation mechanisms in ultrafine-grained materials processed by hot isostatic pressing

    International Nuclear Information System (INIS)

    Cao, W.Q.; Dirras, G.F.; Benyoucef, M.; Bacroix, B.

    2007-01-01

    Ultrafine-grained (uf-g) and microcrystalline-grained (mc-g) irons have been fabricated by hot isostatic pressing of nanopowders. The mechanical properties have been characterized by compressive tests at room temperature and the resulting microstructures and textures have been determined by combining electron back scatter diffraction and transmission electron microscopy. A transition of the deformation mode, from work hardening to work softening occurs for grain sizes below ∼1 μm, reflecting a transition of the deformation mode from homogeneous to localized deformation into shear bands (SBs). The homogeneous deformation is found to be lattice dislocation-based while the deformation within SBs involves lattice dislocations as well as boundary-related mechanisms, possibly grain boundary sliding accommodated by boundary opening

  14. Yb:Y2O3 transparent ceramics processed with hot isostatic pressing

    Science.gov (United States)

    Wang, Jun; Ma, Jie; Zhang, Jian; Liu, Peng; Luo, Dewei; Yin, Danlei; Tang, Dingyuan; Kong, Ling Bing

    2017-09-01

    Highly transparent 5 at.% Yb:Y2O3 ceramics were fabricated by using a combination method of vacuum sintering and hot isostatic pressing (HIP). Co-precipitated Yb:Y2O3 powders, with 1 at.% ZrO2 as the sintering aid, were used as the starting material. The Yb:Y2O3 ceramics, vacuum sintered at 1700 °C for 2 h and HIPed at 1775 °C for 4 h, exhibited small grain size of 1.9 μm and highly dense microstructure. In-line optical transmittance of the ceramics reached 83.4% and 78.9% at 2000 and 600 nm, respectively. As the ceramic slab was pumped by a fiber-coupled laser diode at about 940 nm, a maximum output power of 0.77 W at 1076 nm was achieved, with a corresponding slope efficiency of 10.6%.

  15. Tensile and fracture characteristics of oxide dispersion strengthened Fe–12Cr produced by hot isostatic pressing

    Energy Technology Data Exchange (ETDEWEB)

    Castro, Vanessa de, E-mail: vanessa.decastro@uc3m.es [Departamento de Física, Universidad Carlos III de Madrid, Avda. de la Universidad 30, 28911 Leganés, Madrid (Spain); Garces-Usan, Jose Maria; Leguey, Teresa; Pareja, Ramiro [Departamento de Física, Universidad Carlos III de Madrid, Avda. de la Universidad 30, 28911 Leganés, Madrid (Spain)

    2013-11-15

    The mechanical characteristics of a model oxide dispersion strengthened (ODS) alloy with nominal composition Fe–12 wt%Cr–0.4 wt%Y{sub 2}O{sub 3} were investigated by means of microhardness measurements, tensile tests up to fracture in the temperature range of 298–973 K, and fracture surface analyses. A non-ODS Fe–12 wt%Cr alloy was also studied to assess the real capacity of the oxide dispersion for strengthening the alloy. The materials were produced by mechanical alloying followed by hot isostatic pressing consolidation and heat treatment at 1023 K. The strengthening effect of the oxide nanodispersion was effective at all temperatures studied, although the tensile strength converges towards the one obtained for the reference alloy at higher temperatures. Moreover, the ODS alloys failed prematurely at T < 673 K due to the presence of Y-rich inclusions, as seen in the fracture surface of these alloys.

  16. Development of oxide dispersion strengthened W alloys produced by hot isostatic pressing

    International Nuclear Information System (INIS)

    Martinez, J.; Savoini, B.; Monge, M.A.; Munoz, A.; Pareja, R.

    2011-01-01

    A powder metallurgy technique has been developed to produce oxide strengthened W-Ti and W-V alloys using elemental powders and nanosized powders of La 2 O 3 or Y 2 O 3 as starting materials. The alloys consolidated by hot isostatic pressing resulted in high-density materials having an ultrafine-grained structure and microhardness values in the range 7-13 GPa. Atom force microscopy studies show a topographic relief in the Ti and V pools that appear in the consolidated alloys. This relief is attributed to the heterogeneous nucleation of martensite plates. The preliminary transmission electron microscopy studies have revealed that a dispersion of nanoparticles can be induced in these alloys produced via the present technique.

  17. Development of oxide dispersion strengthened W alloys produced by hot isostatic pressing

    Energy Technology Data Exchange (ETDEWEB)

    Martinez, J.; Savoini, B.; Monge, M.A. [Departamento de Fisica, Universidad Carlos III de Madrid, 28911 Leganes (Spain); Munoz, A., E-mail: angel.munoz@uc3m.es [Departamento de Fisica, Universidad Carlos III de Madrid, 28911 Leganes (Spain); Pareja, R. [Departamento de Fisica, Universidad Carlos III de Madrid, 28911 Leganes (Spain)

    2011-10-15

    A powder metallurgy technique has been developed to produce oxide strengthened W-Ti and W-V alloys using elemental powders and nanosized powders of La{sub 2}O{sub 3} or Y{sub 2}O{sub 3} as starting materials. The alloys consolidated by hot isostatic pressing resulted in high-density materials having an ultrafine-grained structure and microhardness values in the range 7-13 GPa. Atom force microscopy studies show a topographic relief in the Ti and V pools that appear in the consolidated alloys. This relief is attributed to the heterogeneous nucleation of martensite plates. The preliminary transmission electron microscopy studies have revealed that a dispersion of nanoparticles can be induced in these alloys produced via the present technique.

  18. Tensile and fracture characteristics of oxide dispersion strengthened Fe–12Cr produced by hot isostatic pressing

    International Nuclear Information System (INIS)

    Castro, Vanessa de; Garces-Usan, Jose Maria; Leguey, Teresa; Pareja, Ramiro

    2013-01-01

    The mechanical characteristics of a model oxide dispersion strengthened (ODS) alloy with nominal composition Fe–12 wt%Cr–0.4 wt%Y 2 O 3 were investigated by means of microhardness measurements, tensile tests up to fracture in the temperature range of 298–973 K, and fracture surface analyses. A non-ODS Fe–12 wt%Cr alloy was also studied to assess the real capacity of the oxide dispersion for strengthening the alloy. The materials were produced by mechanical alloying followed by hot isostatic pressing consolidation and heat treatment at 1023 K. The strengthening effect of the oxide nanodispersion was effective at all temperatures studied, although the tensile strength converges towards the one obtained for the reference alloy at higher temperatures. Moreover, the ODS alloys failed prematurely at T < 673 K due to the presence of Y-rich inclusions, as seen in the fracture surface of these alloys

  19. Transformation of Cs-IONSIV® into a ceramic wasteform by hot isostatic pressing

    Science.gov (United States)

    Chen, Tzu-Yu; Maddrell, Ewan R.; Hyatt, Neil C.; Gandy, Amy S.; Stennett, Martin C.; Hriljac, Joseph A.

    2018-01-01

    A simple method to directly convert Cs-exchanged IONSIV® IE-911 into a ceramic wasteform by hot isostatic pressing (1100 °C/190 MPa/2 hr) is presented. Two major Cs-containing phases, Cs2TiNb6O18 and Cs2ZrSi6O15, and a series of mixed oxides form. The microstructure and phase assemblage of the samples as a function of Cs content were examined using XRD, XRF, SEM and TEM/EDX. The chemical aqueous durability of the materials was investigated using the MCC-1 and PCT-B standard test methods. For HIPed Cs-IONSIV® samples, the MCC-1 normalised release rates of Cs were low rates are indicative of a safe long-term immobilisation matrix for Cs formed directly from spent IONSIV®. It was also demonstrated that the phase formation can be altered by adding Ti metal due to a controlled redox environment.

  20. Tensile Fracture Behavior of 316L Austenitic Stainless Steel Manufactured by Hot Isostatic Pressing

    Science.gov (United States)

    Cooper, A. J.; Brayshaw, W. J.; Sherry, A. H.

    2018-02-01

    Herein we investigate how the oxygen content in hot isostatically pressed (HIP'd) 316L stainless steel affects the mechanical properties and tensile fracture behavior. This work follows on from previous studies, which aimed to understand the effect of oxygen content on the Charpy impact toughness of HIP'd steel. We expand on the work by performing room-temperature tensile testing on different heats of 316L stainless steel, which contain different levels of interstitial elements (carbon and nitrogen) as well as oxygen in the bulk material. Throughout the work we repeat the experiments on conventionally forged 316L steel as a reference material. The analysis of the work indicates that oxygen does not contribute to a measureable solution strengthening mechanism, as is the case with carbon and nitrogen in austenitic stainless steels (Werner in Mater Sci Eng A 101:93-98, 1988). Neither does oxygen, in the form of oxide inclusions, contribute to precipitation hardening due to the size and spacing of particles. However, the oxide particles do influence fracture behavior; fractography of the failed tension test specimens indicates that the average ductile dimple size is related to the oxygen content in the bulk material, the results of which support an on-going hypothesis relating oxygen content in HIP'd steels to their fracture mechanisms by providing additional sites for the initiation of ductile damage in the form of voids.

  1. Optimizing the Synthesis of Alumina Inserts Using Hot Isostatic Pressing (HIP)

    Science.gov (United States)

    Ariff, T. F.; Azhar, A. Z.; Sariff, M. N.; Rasid, S. N.; Zahari, S. Z.; Bahar, R.; Karim, M.; Nurul Amin, AKM

    2018-01-01

    Alumina or Aluminium Oxide (Al2O3) is well known for its high strength and hardness. Its low heat retention and low specific heat characteristics make it attractive to be used widely as a cutting tool for grinding, milling and turning processes. Various synthesis methods have been used for the purpose of enhancing the properties of the alumina inserts. However, the optimization process using Hot Isostatic Pressing (HIP) has not been performed. This research aims in finding the optimum parameters in synthesizing the alumina inserts (98Al2O3 1.6ZrO2 0.4MgO, 93Al2O3 6.4ZrO2 0.6MgO and 85Al2O3 14.5ZrO2 0.5MgO) using HIP at different temperatures (1200, 1250 and 1300°C) and sintering time (10, 30 and 60 minutes). Hardness, density, shrinkage and microstructure using SEM were analysed. The optimum sintering condition for the alumina insert was found in 98Al2O3 1.6ZrO2 0.4MgO sintered at 1300°C for 60 minutes for it exhibited the highest values of hardness (1917HV), density (3.95g/cm3), shrinkage (9.6%).

  2. Cyclic fatigue resistance of yttria-stabilized tetragonal zirconia polycrystals with hot isostatic press processing.

    Science.gov (United States)

    Koyama, Taku; Sato, Toru; Yoshinari, Masao

    2012-01-01

    This study investigated the influence of surface roughness and cyclic loading on fatigue resistance in Y-TZP subjected to hot isostatic pressing (HIP). Fifty Y-TZP cylinders 3.0 mm in diameter were divided into Group A (polished by centerless method; TZP-CP) or Group B (blasted and acid-etched: TZP-SB150E). Twenty five cp-titanium cylinders (Ti-SB150E) were used as a control. Static and cyclic tests were carried out according to ISO 14801. The cyclic fatigue test was performed in distilled water at 37°C. Surface morphology and roughness as well as crystal phase on the surfaces were also evaluated. Fracture force under the static test was 1,765N (TZP-CP), 1,220N (TZP-SB150E), and 850 N (yield force, Ti-SB150E). Fracture values under the cyclic test decreased to approximately 70% of those under the static tests. These results indicate that HIPed Y-TZP with a 3.0-mm diameter has sufficient durability for application to dental implants.

  3. A study on improving mechanical properties of porous HA tissue engineering scaffolds by hot isostatic pressing

    International Nuclear Information System (INIS)

    Zhao Jing; Xiao Suguang; Lu Xiong; Wang Jianxin; Weng Jie

    2006-01-01

    Various interconnected porous hydroxyapatite (HA) ceramic scaffolds are universally used to induct the tissue growth for bone repair and replacement, and serve to support the adhesion, transfer, proliferation and differentiation of cells. Impregnation of polyurethane sponges with a ceramic slurry is adopted to produce highly porous HA ceramic scaffolds with a 3D interconnected structure. However, high porosity always accompanies a decrease in the strength of the HA ceramic scaffolds. Therefore, it is significant to improve the strength of the HA ceramic scaffolds with highly interconnected porosity so that they are more suitable in clinical applications. In this work, highly porous HA ceramic scaffolds are first produced by the polymer impregnation approach, and subsequently further sintered by hot isostatic pressing (HIP). The phase composition, macro- and micro-porous structure, sintering and mechanical properties of the porous HA scaffolds are investigated by x-ray diffraction (XRD), scanning electron microscopy (SEM), nanoindentation analysis and compressive test. The experimental results show that the nanohardness and compressive strength of HIP-sintered porous HA ceramics are higher than those of commonly sintered HA scaffolds. The HIP technique can effectively improve the sintering property and densification of porous HA ceramic scaffolds, so inducing an increase in the compression strength

  4. High temperature mechanical performance of a hot isostatically pressed silicon nitride

    Energy Technology Data Exchange (ETDEWEB)

    Wereszczak, A.A.; Ferber, M.K.; Jenkins, M.G.; Lin, C.K.J. [and others

    1996-01-01

    Silicon nitride ceramics are an attractive material of choice for designers and manufacturers of advanced gas turbine engine components for many reasons. These materials typically have potentially high temperatures of usefulness (up to 1400{degrees}C), are chemically inert, have a relatively low specific gravity (important for inertial effects), and are good thermal conductors (i.e., resistant to thermal shock). In order for manufacturers to take advantage of these inherent properties of silicon nitride, the high-temperature mechanical performance of the material must first be characterized. The mechanical response of silicon nitride to static, dynamic, and cyclic conditions at elevated temperatures, along with reliable and representative data, is critical information that gas turbine engine designers and manufacturers require for the confident insertion of silicon nitride components into gas turbine engines. This final report describes the high-temperature mechanical characterization and analyses that were conducted on a candidate structural silicon nitride ceramic. The high-temperature strength, static fatigue (creep rupture), and dynamic and cyclic fatigue performance were characterized. The efforts put forth were part of Work Breakdown Structure Subelement 3.2.1, {open_quotes}Rotor Data Base Generation.{close_quotes} PY6 is comparable to other hot isostatically pressed (HIPed) silicon nitrides currently being considered for advanced gas turbine engine applications.

  5. Microstructure and thermal conductivity of Mo-TiC cermets processed by hot isostatic pressing

    International Nuclear Information System (INIS)

    Le Flem, Marion; Allemand, Alexandre; Urvoy, Stephane; Cedat, Denis; Rey, Colette

    2008-01-01

    In the scope of refractory material development for structural applications in the core of future nuclear reactors (gas fast reactors working between 500 o C and at least 800 o C in nominal conditions and up to 1650 o C in accidental scenarios), five Mo-TiC cermets, and single-phase TiC and Mo, were processed by hot isostatic pressing. Starting TiC volume contents were 0%, 12.5%, 25%, 37.5%, 50%, 75% and 100%. First, high dense specimens were characterized in terms of microstructure, composition and phase volume fractions. Cermets exhibited two phases in agreement with phase diagram previsions (Mo-TiC 1-2at.% and TiC-Mo 10-15at.% ), and a residual non-reacted TiC-rich phase (TiC-Mo 1at.% ). Second, heat capacity and thermal diffusivity were measured up to 1000 o C which allowed to evaluate the thermal conductivity of each cermet: this lays between TiC conductivity (12-18 W/m K) and Mo conductivity (95-125 W/m K), thermal properties continuously decreasing with starting TiC content. An analytical approach based on the volume fraction and properties of each constituent allowed to highlight the existence of thermal resistance at the interphases at low temperature

  6. Effect of reduced cobalt contents on hot isostatically pressed powder metallurgy U-700 alloys

    Science.gov (United States)

    Harf, F. H.

    1982-01-01

    The effect of reducing the cobalt content of prealloyed powders of UDIMET 700 (U-700) alloys to 12.7, 8.6, 4.3, and 0% was examined. The powders were hot isostatically pressed into billets, which were given heat treatments appropriate for turbine disks, namely partial solutioning at temperatures below the gamma prime solvus and four step aging treatments. Chemical analyses, metallographic examinations, and X-ray diffraction measurements were performed on the materials. Minor effects on gamma prime content and on room temperature and 650 C tensile properties were observed. Creep rupture lives at 650 C reached a maximum at the 8.4% concentration, while at 760 C a maximum in life was reached at the 4.3% cobalt level. Minimum creep rates increased with decreasing cobalt content at both test temperatures. Extended exposures at 760 and 815 C resulted in decreased tensile strengths and rupture lives for all alloys. Evidence of sigma phase formation was also found.

  7. The substitution of nickel for cobalt in hot isostatically pressed powder metallurgy UDIMET 700 alloys

    Science.gov (United States)

    Harf, F. H.

    1985-01-01

    Nickel was substituted in various proportions for cobalt in a series of five hot-isostatically-pressed powder metallurgy alloys based on the UDIMET 700 composition. These alloys were given 5-step heat treatments appropriate for use in turbine engine disks. The resultant microstructures displayed three distinct sizes of gamma-prime particles in a gamma matrix. The higher cobalt-content alloys contained larger amounts of the finest gamma-prime particles, and had the lowest gamma-gamma-prime lattice mismatch. While all alloys had approximately the same tensile properties at 25 and 650 gamma C, the rupture lives at 650 and 760 C peaked in the alloys with cobalt contents between 12.7 and 4.3 pct. Minimum creep rates increased as cobalt contents were lowered, suggesting their correlation with the gamma-prime particle size distribution and the gamma-gamma-prime mismatch. It was also found that, on overaging at temperatures higher than suitable for turbine disk use, the high cobalt-content alloys were prone to sigma phase formation.

  8. Fundamental Aspects of Zeolite Waste Form Production by Hot Isostatic Pressing

    Energy Technology Data Exchange (ETDEWEB)

    Jubin, Robert Thomas [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Bruffey, Stephanie H. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Jordan, Jacob A. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2017-02-01

    The direct conversion of iodine-bearing sorbents into a stable waste form is a research topic of interest to the US Department of Energy. The removal of volatile radioactive 129I from the off-gas of a nuclear fuel reprocessing facility will be necessary in order to comply with the regulatory requirements that apply to facilities sited within the United States (Jubin et al., 2012a), and any iodine-containing media or solid sorbents generated by this process would contain 129I and would be destined for eventual geological disposal. While recovery of iodine from some sorbents is possible, a method to directly convert iodineloaded sorbents to a durable waste form with little or no additional waste materials being formed and a potentially reduced volume would be beneficial. To this end, recent studies have investigated the conversion of iodine-loaded silver mordenite (I-AgZ) directly to a waste form by hot isostatic pressing (HIPing) (Bruffey and Jubin, 2015). Silver mordenite (AgZ), of the zeolite class of minerals, is under consideration for use in adsorbing iodine from nuclear reprocessing off-gas streams. Direct conversion of I-AgZ by HIPing may provide the following benefits: (1) a waste form of high density that is tolerant to high temperatures, (2) a waste form that is not significantly chemically hazardous, and (3) a robust conversion process that requires no pretreatment.

  9. Age hardening in rapidly solidified and hot isostatically pressed beryllium-aluminum-silver alloys

    International Nuclear Information System (INIS)

    Carter, D.H.; McGeorge, A.C.; Jacobson, L.A.; Stanek, P.W.

    1995-01-01

    Three different alloys of beryllium, aluminum and silver were processed to powder by centrifugal atomization in a helium atmosphere. Alloy compositions were, by weight, 50% Be, 47.5% Al, 2.5% Ag, 50% Be, 47% Al, 3% Ag, and 50% Be, 46% Al, 4% Ag. Due to the low solubility of both aluminum and silver in beryllium, the silver was concentrated in the aluminum phase, which appeared to separate from the beryllium in the liquid phase. A fine, continuous composite beryllium-aluminum microstructure was formed, which did not significantly change after hot isostatically pressing at 550 C for one hour at 30,000 psi argon pressure. Samples of HIP material were solution treated at 550 C for one hour, followed by a water quench. Aging temperatures were 150, 175, 200 and 225 C for times ranging from one half hour to 65 hours. Hardness measurements were made using a diamond pyramid indenter with a load of 1 kg. Results indicate that peak hardness was reached in 36--40 hours at 175 C and 12--16 hours at 200 C aging temperature, relatively independent of alloy composition

  10. Characterization of hot isostatically pressed Bi-Sr-Ca-Cu-O as a function of consolidation variables

    International Nuclear Information System (INIS)

    Goretta, K.C.; Miller, D.J.; Poeppel, R.B.; Nash, A.S.

    1992-01-01

    This paper reports that fully dense, bulk Bi 2 Sr 1.7 CaCu 2 O x superconductor pellets were made by hot isostatic pressing in an inert atmosphere. Electron microscopy revealed that rotation and bending of the platelike 2212 grains were responsible for much of the densification. Under processing conditions of 825 degrees C and 105 MPa, dense pellets were obtained in 15 min. Many dislocations, planar faults, and, perhaps, intergrowths of the Bi 2 Cr 2 CuO x phase were produced during pressing. The dislocations were largely present in subgrain boundaries when the pressing times were increased to 45-120 min

  11. An Assessment of the Ductile Fracture Behaviour of Hot Isostatically Pressed and Forged 304L Stainless Steel

    OpenAIRE

    Cooper, Adam; Smith, R. J.; Sherry, Andrew

    2017-01-01

    Type 300 austenitic stainless steel manufactured by hot isostatic pressing (HIP) has recently been shown to exhibit subtly different fracture behavior from that of equivalent graded forged steel, whereby the oxygen remaining in the component after HIP manifests itself in the austenite matrix as nonmetallic oxide inclusions. These inclusions facilitate fracture by acting as nucleation sites for the initiation, growth, and coalescence of microvoids in the plastically deforming austenite matrix....

  12. Hot Isostatic Pressing of Engineered Forms of I-AgZ

    Energy Technology Data Exchange (ETDEWEB)

    Jubin, Robert Thomas [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Watkins, Thomas R. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Bruffey, Stephanie H. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Jordan, Jacob A. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Parks, Mackenzie L. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2017-11-01

    Hot isostatic pressing (HIP) is being considered for direct conversion of 129I-bearing materials to a radiological waste form. The removal of volatile radioactive 129I from the off-gas of a nuclear fuel reprocessing facility will be necessary to comply with regulatory requirements regarding reprocessing facilities sited within the United States, and any iodine-containing media or solid sorbents generated by offgas abatement will require disposal. Zeolite minerals such as silver-exchanged mordenite (AgZ) have been studied as potential iodine sorbents and will contain 129I as chemisorbed AgI. Oak Ridge National Laboratory (ORNL) has conducted several recent studies on the HIP of both iodine-loaded AgZ (I-AgZ) and other iodine-bearing zeolite minerals. The goal of these research efforts is to achieve a stable, highly leach resistant material that is reduced in volume as compared to bulk iodine-loaded I-AgZ. Through the use of HIP, it may be possible to achieve this with the addition of little or no additional materials (waste formers). Other goals for the process include that the waste form will be tolerant to high temperatures and pressures, not chemically hazardous, and that the process will result in minimal secondary waste generation. This document describes the preparation of 27 samples that are distinct from previous efforts in that they are prepared exclusively with an engineered form of AgZ that is manufactured using a binder. Iodine was incorporated solely by chemisorption. This base material is expected to be more representative of an operational system than were samples prepared previously with pure minerals.

  13. Investigation of hot- iso-static press process for tungsten target samples

    International Nuclear Information System (INIS)

    Xu Yongli; Zhang Jinquan; Li Huaqing

    2006-01-01

    Zr and stainless steel (S.S.) were selected respectively as the cladding materials of W target. The e-beam weld was used to prepare the W-Zr and W-S.S. small samples for hot iso-static press (HIP) process. The technology parameters of HIP were investigated at 1200, 1300, 1400 degree C and 180 MPa, respectively. The micro-morphology of the interface, diffusion depths and composition as well as their micro-hardness were observed and determined. The bonding of W-Zr and W-S.S. is very well under the testing conditions. There is no any pore or micro-crack in the interface, and there is no grain growth of W below 1400 degree C either. The diffusion of Zr to W at the interface of W-Zr is preferred during HIP process, and the diffusion depths under testing conditions are 6-13 μm. The diffusion of W and Fe is considerable at the interface of W-S.S. Its depth is about 13 μm, and the diffusion of Cr and Ni is mall. The hardness at the interface of W-Zr and W-S.S. shows that a diffusion layer is present for both interface. A part of stainless steel cladding was melted after HIP contained the oxygen absorber Zr at 1300 degree C and 180 MPa. Therefore, 1200 degree C and 180 MPa is suitable for W-S.S. without Zr, but 1300 or 1400 degree C and 180 MPa is better for W-Zr. (authors)

  14. Preliminary Study on Hot Isostatic Pressing Diffusion Bonding for CLAM Steel

    International Nuclear Information System (INIS)

    Chunjing Li; Qunying Huang; Yican Wu

    2006-01-01

    China Low Activation Martensitic (CLAM) steel is being developed in ASIPP (Institute of Plasma Physics, Chinese Academy of Sciences) since three years ago. CLAM is selected as the major candidate structure materials for the FDS series design of fusion reactors and for China liquid metal LiPb Test Blanket Module (TBM) for ITER i.e. DFLL-TBM, which are being carried out in ASIPP. Since the hot isostatic pressing (HIP) bonding technique is one of the main candidate bonding techniques for manufacturing of the first wall of a fusion reactor, research of the HIP technique on CLAM/CLAM is greatly needed. Preliminary HIP diffusion bonding experiments on CLAM steel have been performed. A few machining approaches such as dry-milling, turnery and grounding etc. were used to prepare the sample surfaces and then they were degreased with a mixture of alcohol, ether and acetone in an ultrasonic bath. The samples were joined by HIP diffusion bonding with the compression pressure of 150 MPa and the holding time of 2 ∼ 3 hours under different temperatures between 950 deg. and 1100 deg.. Different seal techniques of the capsules were studied as well. Then appropriate post heat treatment was done. Tests on mechanical properties of the joints such as tensile strength and impact toughness have been performed. The preliminary results show that the tensile properties are roughly the same as those of the base material. The absorbed energy of the joints at present is a little low and further research is needed to increase it. Microstructure of the joints was studied by optical microscope, SEM and TEM. Compositions of the defects on the joining line were analyzed by EDS. Through analysis of the results, optimized parameters for HIP are given. (author)

  15. Development of Be/Glidcop joint obtained by hot isostatic pressing diffusion bonding for high in-service temperature

    Energy Technology Data Exchange (ETDEWEB)

    Saint-Antonin, F.; Bucci, P.; Burlet, H.; Le Marois, G. [CEA Centre d`Etudes de Grenoble, 38 (France); Barberi, D.; Laille, A.

    1998-01-01

    This paper addresses some aspects of the beryllium-Glidcop joining by Hot Isostatic Pressing diffusion Bonding. The quality of a joint is mainly dependent on the interface microstructure. Thus, as Be/copper direct bonding is not recommended, the choice of interlayers is a critical point. The joining process parameters, i.e. temperature, pressure and time, must take into account the in-service requirements, the mechanical and metallurgical properties of each material. The Be/Glidcop joining process developed at CEA/Grenoble is presented here. (author)

  16. Pore annihilation in a single-crystal nickel-base superalloy during hot isostatic pressing: Experiment and modelling

    International Nuclear Information System (INIS)

    Epishin, Alexander; Fedelich, Bernard; Link, Thomas; Feldmann, Titus; Svetlov, Igor L.

    2013-01-01

    Pore annihilation during hot isostatic pressing (HIP) was investigated in the single-crystal nickel-base superalloy CMSX-4 experimentally by interrupted HIP tests at 1288 °C/103 MPa. The kinetics of pore annihilation was determined by density measurement and quantitative metallography. Transmission electron microscopy of a HIPed specimen showed that the pores shrink via dislocation movement on octahedral glide planes. Theoretically pore closure under HIP condition was modelled by the finite element method using crystal plasticity and large strain theories. The modelling gives a similar kinetics of pore annihilation as observed experimentally, however somewhat higher annihilation rate

  17. Microstructural and mechanical characteristics of W–2Ti and W–1TiC processed by hot isostatic pressing

    Energy Technology Data Exchange (ETDEWEB)

    Muñoz, A., E-mail: angel.munoz@uc3m.es [Departamento de Física, Universidad Carlos III de Madrid, Avda. de la Universidad, 30, E28911 Leganés (Spain); Savoini, B. [Departamento de Física, Universidad Carlos III de Madrid, Avda. de la Universidad, 30, E28911 Leganés (Spain); Tejado, E. [Departamento de Ciencia de Materiales, E.T.S. I. de Ingenieros de Caminos, Canales y Puertos, Universidad Politécnica de Madrid, E28040 Madrid (Spain); Centro Nacional de Investigaciones Metalúrgicas (C.S.I.C), Av. Gregorio del Amo, 8, E2840 Madrid (Spain); Monge, M.A. [Departamento de Física, Universidad Carlos III de Madrid, Avda. de la Universidad, 30, E28911 Leganés (Spain); Pastor, J.Y. [Departamento de Ciencia de Materiales, E.T.S. I. de Ingenieros de Caminos, Canales y Puertos, Universidad Politécnica de Madrid, E28040 Madrid (Spain); Pareja, R. [Departamento de Física, Universidad Carlos III de Madrid, Avda. de la Universidad, 30, E28911 Leganés (Spain)

    2014-12-15

    W–2Ti and W–1TiC alloys were produced by mechanical alloying and consolidation by hot isostatic pressing. The composition and microstructural characteristics of these alloys were studied by X-ray diffraction, energy dispersion spectroscopy and scanning electron microscopy. The mechanical behavior of the consolidated alloys was characterized by microhardness measurements and three point bending tests. The mechanical characteristics of the W–2Ti alloy appear to be related to solution hardening. In W–1TiC, the residual porosity should be responsible for the poor behavior observed in comparison with W–2Ti.

  18. Microstructural and mechanical characteristics of W–2Ti and W–1TiC processed by hot isostatic pressing

    International Nuclear Information System (INIS)

    Muñoz, A.; Savoini, B.; Tejado, E.; Monge, M.A.; Pastor, J.Y.; Pareja, R.

    2014-01-01

    W–2Ti and W–1TiC alloys were produced by mechanical alloying and consolidation by hot isostatic pressing. The composition and microstructural characteristics of these alloys were studied by X-ray diffraction, energy dispersion spectroscopy and scanning electron microscopy. The mechanical behavior of the consolidated alloys was characterized by microhardness measurements and three point bending tests. The mechanical characteristics of the W–2Ti alloy appear to be related to solution hardening. In W–1TiC, the residual porosity should be responsible for the poor behavior observed in comparison with W–2Ti

  19. Interface analysis of A1 matrix composites produced by hot isostatic pressing, squeeze casting and semi-solid processing

    International Nuclear Information System (INIS)

    Shamsul, J.B.; Zainal Arifin Ahmad; Faaizulaswad, M.S.; Azmi, R.

    2000-01-01

    The interface analysis has been carried out an aluminium based composites system produced by hot isostatic pressing, squeeze casting and semi-solid processing. A range of different fabrication techniques has been used to produce different types of microstructure of Al 2124 (Al-Cu-Mg) reinforced with 5 weight % SiC particles. Blending followed by hot isostatic pressing is used to fabricate composite I. Composite II was 6061 (Al-Si-Mg) wrought aluminium alloy reinforced with fibres of alumina-silica (V f = 0.58) and fabricated by squeeze casting. Finally, A356 (AlSi7Mg0.3) alloy was reinforced with 20 Vol.% of SiC particles (13 μm) and namely as composite III. Composite III is fabricated by semi-solid processing. Interface analysis was done by optical microscopy, scanning and transmission electron microscopy. Composite I exhibited good interface bonding and dislocation was also observed near the interface. Elements such as Al, Fe, Cr, Mn were found near the interface of composite II and intermetallic of iron rich inclusion and Mg 2 Si were observed near the interface of composite III. (Author)

  20. An Assessment of the Ductile Fracture Behavior of Hot Isostatically Pressed and Forged 304L Stainless Steel

    Science.gov (United States)

    Cooper, A. J.; Smith, R. J.; Sherry, A. H.

    2017-05-01

    Type 300 austenitic stainless steel manufactured by hot isostatic pressing (HIP) has recently been shown to exhibit subtly different fracture behavior from that of equivalent graded forged steel, whereby the oxygen remaining in the component after HIP manifests itself in the austenite matrix as nonmetallic oxide inclusions. These inclusions facilitate fracture by acting as nucleation sites for the initiation, growth, and coalescence of microvoids in the plastically deforming austenite matrix. Here, we perform analyses based on the Rice-Tracey (RT) void growth model, supported by instrumented Charpy and J-integral fracture toughness testing at ambient temperature, to characterize the degree of void growth ahead of both a V-notch and crack in 304L stainless steel. We show that the hot isostatically pressed (HIP'd) 304L steel exhibits a lower critical void growth at the onset of fracture than that observed in forged 304L steel, which ultimately results in HIP'd steel exhibiting lower fracture toughness at initiation and impact toughness. Although the reduction in toughness of HIP'd steel is not detrimental to its use, due to the steel's sufficiently high toughness, the study does indicate that HIP'd and forged 304L steel behave as subtly different materials at a microstructural level with respect to their fracture behavior.

  1. Experimental and Simulation Analysis of Hot Isostatic Pressing of Gas Atomized Stainless Steel 316L Powder Compacts

    International Nuclear Information System (INIS)

    Lin, Dongguo; Park, Seong Jin; Ha, Sangyul; Shin, Youngho; Park, Dong Yong; Chung, Sung Taek; Bollina, Ravi; See, Seongkyu

    2016-01-01

    In this work, both experimental and numerical studies were conducted to investigate the densification behavior of stainless steel 316L (STS 316L) powders during hot isostatic pressing (HIP), and to characterize the mechanical properties of HIPed specimens. The HIP experiments were conducted with gas atomized STS 316L powders with spherical particle shapes under controlled pressure and temperature conditions. The mechanical properties of HIPed samples were determined based on a series of tensile tests, and the results were compared to a reference STS 316L sample prepared by the conventional process, i.e., extrusion and annealing process. Corresponding microstructures before and after tensile tests were observed using scanning electron microscopy and their relationships to the mechanical properties were addressed. Furthermore, a finite element simulation based on the power-law creep model was carried out to predict the density distribution and overall shape change of the STS316L powder compact during HIP process, which agreed well with the experimental results.

  2. Forming and control of pores by capsule-free hot isostatic pressing in NiTi shape memory alloys

    International Nuclear Information System (INIS)

    Yuan, B; Zhu, M; Gao, Y; Li, X; Chung, C Y

    2008-01-01

    In this study, the pore evolution process of porous NiTi shape memory alloys (SMAs) fabricated by capsule-free hot isostatic pressing (CF-HIP) was investigated by adopting different fabricating parameters. It is shown that porous NiTi SMAs with homogeneous pore distribution and nearly spherical pore shape can be prepared by CF-HIP under suitable conditions. In addition, two novel pore structures were produced, one with a sandwich-like structure, and another with controlled gradient of porosity along the radial direction, with pore size increasing from the outside towards the center of the specimen. The former was obtained by balancing the pressure in the HIP chamber and the gas pressure resulting from the gas expansion in the green sample. The latter resulted from the formation of air bubbles in the liquid phase during the sintering

  3. Effect of Hot-isostatic Pressing on Microstructure and Mechanical Properties of Second Generation Single Crystal Superalloy DD6

    Directory of Open Access Journals (Sweden)

    GUO Hui-ming

    2016-10-01

    Full Text Available Effects of the hot-isostatic pressing (HIP temperature (1280,1300,1320℃ on microstructures and mechanical properties of a second generation single crystal superalloy DD6 were investigated. The results show that the HIP treatment significantly decrease the cast porosity number of DD6 compared with standard treated specimens. Especially, the cast porosity volume fraction is deceased from 0.31% to 0.04% after the HIP treatment of 1300℃/100MPa, 4h. The cast eutectic volume fractions are remarkably reduced with increasing HIP temperature. The HIP treatments nearly unchanged the creep lives, While they greatly promote the low cycle fatigue lives. The elimination of cast microspores using the HIP treatment of 1300℃/100MPa, 4h result in the inhibition of crack initiation during fatigue and improve the low cycle fatigue lives one order of magnitude larger than that after standard heat treatment.

  4. Influence of surface treatment of yttria-stabilized tetragonal zirconia polycrystal with hot isostatic pressing on cyclic fatigue strength.

    Science.gov (United States)

    Iijima, Toshihiko; Homma, Shinya; Sekine, Hideshi; Sasaki, Hodaka; Yajima, Yasutomo; Yoshinari, Masao

    2013-01-01

    Hot isostatic pressing processed yttria-stabilized tetragonal zirconia polycrystal (HIP Y-TZP) has the potential for application to implants due to its high mechanical performance. The aim of this study was to investigate the influence of surface treatment of HIP Y-TZP on cyclic fatigue strength. HIP Y-TZP specimens were subjected to different surface treatments. Biaxial flexural strength was determined by both static and cyclic fatigue testing. In the cyclic fatigue test, the load was applied at a frequency of 10 Hz for 10(6) cycles in distilled water at 37°C. The surface morphology, roughness, and crystal phase of the surfaces were also evaluated. The cyclic fatigue strength (888 MPa) of HIP Y-TZP with sandblasting and acid-etching was more than twice that of Y-TZP as specified in ISO 13356 for surgical implants (320 MPa), indicating the clinical potential of this material.

  5. Experimental and Simulation Analysis of Hot Isostatic Pressing of Gas Atomized Stainless Steel 316L Powder Compacts

    Energy Technology Data Exchange (ETDEWEB)

    Lin, Dongguo; Park, Seong Jin [Pohang University of Science and Technology, Pohang (Korea, Republic of); Ha, Sangyul [Samsung Electro-Mechanics, Suwon (Korea, Republic of); Shin, Youngho [Doosan Heavy Industries and Construction Co., Ltd., Changwon (Korea, Republic of); Park, Dong Yong [Korea Institute of Energy Research, Daejeon (Korea, Republic of); Chung, Sung Taek [CetaTech Inc., Sacheon (Korea, Republic of); Bollina, Ravi [Bahadurpally Jeedimetla, Hyderabad (India); See, Seongkyu [POSCO, Pohang (Korea, Republic of)

    2016-10-15

    In this work, both experimental and numerical studies were conducted to investigate the densification behavior of stainless steel 316L (STS 316L) powders during hot isostatic pressing (HIP), and to characterize the mechanical properties of HIPed specimens. The HIP experiments were conducted with gas atomized STS 316L powders with spherical particle shapes under controlled pressure and temperature conditions. The mechanical properties of HIPed samples were determined based on a series of tensile tests, and the results were compared to a reference STS 316L sample prepared by the conventional process, i.e., extrusion and annealing process. Corresponding microstructures before and after tensile tests were observed using scanning electron microscopy and their relationships to the mechanical properties were addressed. Furthermore, a finite element simulation based on the power-law creep model was carried out to predict the density distribution and overall shape change of the STS316L powder compact during HIP process, which agreed well with the experimental results.

  6. Verification of the effect of surface preparation on Hot Isostatic Pressing diffusion bonding joints of CLAM steel

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Yanyun [University of Science and Technology of China, Hefei, Anhui 230027 (China); Institute of Nuclear Energy Safety Technology, Chinese Academy of Sciences, Hefei, Anhui 230031 (China); Li, Chunjing, E-mail: chunjing.li@fds.org.cn [Institute of Nuclear Energy Safety Technology, Chinese Academy of Sciences, Hefei, Anhui 230031 (China); Huang, Bo; Liu, Shaojun [Institute of Nuclear Energy Safety Technology, Chinese Academy of Sciences, Hefei, Anhui 230031 (China); Huang, Qunying [University of Science and Technology of China, Hefei, Anhui 230027 (China); Institute of Nuclear Energy Safety Technology, Chinese Academy of Sciences, Hefei, Anhui 230031 (China)

    2014-12-15

    Hot Isostatic Pressing (HIP) diffusion bonding with CLAM steel is the primary candidate fabrication technique for the first wall (FW) of DFLL-TBM. Surface state is one of the key factors for the joints quality. The effect of surface state prepared with grinder and miller on HIP diffusion bonding joints of CLAM steel was investigated. HIP diffusion bonding was performed at 140 MPa and 1373 K within 3 h. The mechanical properties of the joints were investigated with instrumented Charpy V-notch impact tests and the microstructures of the joints were analyzed with scanning electron microscopy (SEM). The results showed that the milled samples with fine surface roughness were more suitable for CLAM steel HIP diffusion bonding.

  7. Effects of Temperature and Pressure of Hot Isostatic Pressing on the Grain Structure of Powder Metallurgy Superalloy.

    Science.gov (United States)

    Tan, Liming; He, Guoai; Liu, Feng; Li, Yunping; Jiang, Liang

    2018-02-24

    The microstructure with homogeneously distributed grains and less prior particle boundary (PPB) precipitates is always desired for powder metallurgy superalloys after hot isostatic pressing (HIPping). In this work, we studied the effects of HIPping parameters, temperature and pressure on the grain structure in PM superalloy FGH96, by means of scanning electron microscope (SEM), electron backscatter diffraction (EBSD), transmission electron microscope (TEM) and Time-of-flight secondary ion spectrometry (ToF-SIMS). It was found that temperature and pressure played different roles in controlling PPB precipitation and grain structure during HIPping, the tendency of grain coarsening under high temperature could be inhibited by increasing HIPping pressure which facilitates the recrystallization. In general, relatively high temperature and pressure of HIPping were preferred to obtain an as-HIPped superalloy FGH96 with diminished PPB precipitation and homogeneously refined grains.

  8. M3FT-17OR0301070211 - Preparation of Hot Isostatically Pressed AgZ Waste Form Samples

    Energy Technology Data Exchange (ETDEWEB)

    Jubin, Robert Thomas [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Bruffey, Stephanie H. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Jordan, Jacob A. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2017-10-01

    The production of radioactive iodine-bearing waste forms that exhibit long-term stability and are suitable for permanent geologic disposal has been the subject of substantial research interest. One potential method of iodine waste form production is hot isostatic pressing (HIP). Recent studies at Oak Ridge National Laboratory (ORNL) have investigated the conversion of iodine-loaded silver mordenite (I-AgZ) directly to a waste form by HIP. ORNL has performed HIP with a variety of sample compositions and pressing conditions. The base mineral has varied among AgZ (in pure and engineered forms), silver-exchanged faujasite, and silverexchanged zeolite A. Two iodine loading methods, occlusion and chemisorption, have been explored. Additionally, the effects of variations in temperature and pressure of the process have been examined, with temperature ranges of 525°C–1,100°C and pressure ranges of 100–300 MPa. All of these samples remain available to collaborators upon request. The sample preparation detailed in this document is an extension of that work. In addition to previously prepared samples, this report documents the preparation of additional samples to support stability testing. These samples include chemisorbed I-AgZ and pure AgI. Following sample preparation, each sample was processed by HIP by American Isostatic Presses Inc. and returned to ORNL for storage. ORNL will store the samples until they are requested by collaborators for durability testing. The sample set reported here will support waste form durability testing across the national laboratories and will provide insight into the effects of varied iodine content on iodine retention by the produced waste form and on potential improvements in waste form durability provided by the zeolite matrix.

  9. Microstructure and properties of diffusion bonded Ti-6Al-4V parts using brazing-assisted hot isostatic pressing

    International Nuclear Information System (INIS)

    Wu, Z.; Mei, J.; Voice, W.; Beech, Steve; Wu, X.

    2011-01-01

    Highlights: → A low cost method of diffusion bonding has been developed for complex-shaped components of Ti6Al4V. → Vacuum brazing has been used to seal the periphery to allow encapsulation-free HIPping. → The tensile properties of the bonds are comparable with those of the bulk material, but the fatigue life was slightly reduced. - Abstract: Ti-6Al-4V couples have been diffusion bonded by hot isostatic pressing (HIPping) after vacuum brazing was used to seal the periphery of the bonding samples so that no encapsulation was required during HIPping. Analytical scanning electron microscopy was used to assess the microstructure of the HIPped interface and tensile and fatigue properties of bonded samples were compared with those of the bulk starting material. The tensile properties of the bonds were shown to be comparable with those of the bulk material, but the fatigue life was slightly downgraded. The fatigue fractures were initiated by inclusions on the bonding interface, caused by contamination before bonding, but the fatigue cracks did not propagate along the bonding interface indicating a strong bond. It is concluded that this technique of vacuum brazing plus HIPping could be used for encapsulation-free HIPping to produce complex-shaped components.

  10. Inversion defects in MgAl2O4 elaborated by pressureless sintering, pressureless sintering plus hot isostatic pressing, and spark plasma sintering

    International Nuclear Information System (INIS)

    Mussi, A.; Granger, G. Bernard; Addad, A.; Benameur, N.; Beclin, F.; Bataille, A.

    2009-01-01

    The distribution of inversion defects of Al was investigated in dense magnesium-aluminate spinel elaborated by pressureless sintering, pressureless sintering plus hot isostatic pressing, and spark plasma sintering. This study was conducted by energy electron loss spectroscopy analyses and more particularly by energy loss near edge structure investigations of the Al-L 2,3 edge. Several aspects are discussed with the purpose of understanding why charged defects dispersal reveals a special configuration.

  11. Effect of Tooling Material on the Internal Surface Quality of Ti6Al4V Parts Fabricated by Hot Isostatic Pressing

    Science.gov (United States)

    Cai, Chao; Song, Bo; Wei, Qingsong; Yan, Wu; Xue, Pengju; Shi, Yusheng

    2017-01-01

    For the net-shape hot isostatic pressing (HIP) process, control of the internal surface roughness of as-HIPped parts remains a challenge for practical engineering. To reveal the evolution mechanism of the internal surface of the parts during the HIP process, the effect of different tooling materials (H13, T8, Cr12 steel, and graphite) as internal cores on the interfacial diffusion and surface roughness was systematically studied.

  12. Justification and manufacturing quality assurance for the use of hot Isostatically pressed, reactor coolant system components in PWR plant

    International Nuclear Information System (INIS)

    Sulley, J. L.; Hookham, I. D.

    2008-01-01

    This paper presents an overview of the work undertaken by Rolls-Royce to introduce Hot Isostatically Pressed (HIP) components into Pressurised Water Reactor plant. It presents the work from a design justification and manufacturing quality assurance perspective, rather than from a pure metallurgical perspective, although some metallurgical and mechanical property comparisons with the traditional forged material are presented. Although the HIP process is not new, it was new in its application to Rolls-Royce designed nuclear reactor plant. In order to satisfy the regulatory requirement of 'Proven Engineering Practices' with regard to the introduction of new material processes, and to provide a robust manufacturing substantiation leg of a multi-legged safety case, Rolls-Royce has implemented an evolving, staged approach, starting with HIP bonding of solid valve seats into small bore valve pressure boundaries. This was followed by powder HIP consolidation of leak-limited, thin-walled toroids, and has culminated in the powder HIP consolidation of components, such as steam generator headers, large bore valves and pipe sections. The paper provides an overview of each of these stages and the approach taken with respect to justification. The paper describes the benefits that Rolls-Royce has realised so far through the introduction of HIPed components, and improvements planned for the future. Structural integrity benefits are described, such as improved grain structure, mechanical properties, and ultrasonic inspection. Project-based benefits are also described, such as provision of an alternative strategic sourcing route, cost and lead-time reduction. A full description is provided of key quality assurance steps applied to the process to ensure a high quality product is delivered commensurate with a high integrity nuclear application. 2008 Rolls-Royce plc. (authors)

  13. Microstructural and Microhardness Evolution from Homogenization and Hot Isostatic Pressing on Selective Laser Melted Inconel 718: Structure, Texture, and Phases

    Directory of Open Access Journals (Sweden)

    Raiyan Seede

    2018-05-01

    Full Text Available In this work, the microstructure, texture, phases, and microhardness of 45° printed (with respect to the build direction homogenized, and hot isostatically pressed (HIP cylindrical IN718 specimens are investigated. Phase morphology, grain size, microhardness, and crystallographic texture at the bottom of each specimen differ from those of the top due to changes in cooling rate. High cooling rates during the printing process generated a columnar grain structure parallel to the building direction in the as-printed condition with a texture transition from (001 orientation at the bottom of the specimen to (111 orientation towards the specimen top based on EBSD analysis. A mixed columnar and equiaxed grain structure associated with about a 15% reduction in texture is achieved after homogenization treatment. HIP treatment caused significant grain coarsening, and engendered equiaxed grains with an average diameter of 154.8 µm. These treatments promoted the growth of δ-phase (Ni3Nb and MC-type brittle (Ti, NbC carbides at grain boundaries. Laves phase (Fe2Nb was also observed in the as-printed and homogenized specimens. Ostwald ripening of (Ti, NbC carbides caused excessive grain growth at the bottom of the HIPed IN718 specimens, while smaller grains were observed at their top. Microhardness in the as-fabricated specimens was 236.9 HV and increased in the homogenized specimens by 19.3% to 282.6 HV due to more even distribution of secondary precipitates, and the nucleation of smaller grains. A 36.1% reduction in microhardness to 180.5 HV was found in the HIPed condition due to   γ ″ phase dissolution and differences in grain morphology.

  14. Influences of hot-isostatic-pressing temperature on microstructure, tensile properties and tensile fracture mode of Inconel 718 powder compact

    International Nuclear Information System (INIS)

    Chang, Litao; Sun, Wenru; Cui, Yuyou; Yang, Rui

    2014-01-01

    Inconel 718 powders have been hot-isostatic-pressed (HIPed) at representative temperatures to investigate the variations in microstructure, tensile properties and tensile fracture mode of the powder compact. Microstructure of the powder compacts were characterized by optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and so on. The results showed that the interdendritic precipitates inherited from the powders were partially retained in the powder compacts when the powders were HIPed at or below 1210 °C but were eliminated when HIPed at and above 1260 °C. The grain size uniformity of the powder compacts first increases and then decreases with increasing HIPing temperature. Prior particle boundaries (PPBs) were observed in the powder compacts HIPed at and below 1260 °C but was eliminated when HIPed at 1275 °C. The PPBs were decorated with carbide particles, the amount of the carbide particles at the PPBs decreases with increasing HIPing temperature. Most of the PPBs were pinned by the carbide particles in the compacts HIPed at 1140 °C. When the HIPing temperature was increased to 1210 °C and 1260 °C, a large number of PPBs de-pinned and moved beyond the pinning carbide particles, leading to grain growth and leaving carbide particles at the site of the original PPBs within the new grains. With increasing HIPing temperature, the 0.2% yield strength of the powder compacts at 650 °C decreases, the tensile elongation increases, and the tensile fracture mode changed from inter-particle dominant fracture to fully dimple ductile fracture

  15. Comparison of structure, morphology, and leach characteristics of multi-phase ceramics produced via melt processing and hot isostatic pressing

    Science.gov (United States)

    Dandeneau, Christopher S.; Hong, Tao; Brinkman, Kyle S.; Vance, Eric R.; Amoroso, Jake W.

    2018-04-01

    Melt processing of multi-phase ceramic waste forms offers potential advantages over traditional solid-state synthesis methods given both the prevalence of melters currently in use and the ability to reduce the possibility of airborne radionuclide contamination. In this work, multi-phase ceramics with a targeted hollandite composition of Ba1.0Cs0.3Cr1.0Al0.3Fe1.0Ti5.7O16 were fabricated by melt processing at 1675 °C and hot isostatic pressing (HIP) at 1250 and 1300 °C. X-ray diffraction analysis (XRD) confirmed hollandite as the major phase in all specimens. Zirconolite/pyrochlore peaks and weaker perovskite reflections were observed after melt processing, while HIP samples displayed prominent perovskite peaks and low-intensity zirconolite reflections. Melt processing produced specimens with large (>50 μm) well-defined hollandite grains, while HIP yielded samples with a more fine-grained morphology. Elemental analysis showed "islands" rich in Cs and Ti across the surface of the 1300 °C HIP sample, suggesting partial melting and partitioning of Cs into multiple phases. Photoemission data revealed multiple Cs 3d spin-orbit pairs for the HIP samples, with the lower binding energy doublets likely corresponding to Cs located in more leachable phases. Among all specimens examined, the melt-processed sample exhibited the lowest fractional release rates for Rb and Cs. However, the retention of Sr and Mo was greater in the HIP specimens.

  16. Influences of hot-isostatic-pressing temperature on microstructure, tensile properties and tensile fracture mode of Inconel 718 powder compact

    Energy Technology Data Exchange (ETDEWEB)

    Chang, Litao [Institute of Metal Research, Chinese Academy of Sciences, Shenyang (China); University of Chinese Academy of Sciences, Beijing (China); Sun, Wenru; Cui, Yuyou [Institute of Metal Research, Chinese Academy of Sciences, Shenyang (China); Yang, Rui, E-mail: ryang@imr.ac.cn [Institute of Metal Research, Chinese Academy of Sciences, Shenyang (China)

    2014-04-01

    Inconel 718 powders have been hot-isostatic-pressed (HIPed) at representative temperatures to investigate the variations in microstructure, tensile properties and tensile fracture mode of the powder compact. Microstructure of the powder compacts were characterized by optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and so on. The results showed that the interdendritic precipitates inherited from the powders were partially retained in the powder compacts when the powders were HIPed at or below 1210 °C but were eliminated when HIPed at and above 1260 °C. The grain size uniformity of the powder compacts first increases and then decreases with increasing HIPing temperature. Prior particle boundaries (PPBs) were observed in the powder compacts HIPed at and below 1260 °C but was eliminated when HIPed at 1275 °C. The PPBs were decorated with carbide particles, the amount of the carbide particles at the PPBs decreases with increasing HIPing temperature. Most of the PPBs were pinned by the carbide particles in the compacts HIPed at 1140 °C. When the HIPing temperature was increased to 1210 °C and 1260 °C, a large number of PPBs de-pinned and moved beyond the pinning carbide particles, leading to grain growth and leaving carbide particles at the site of the original PPBs within the new grains. With increasing HIPing temperature, the 0.2% yield strength of the powder compacts at 650 °C decreases, the tensile elongation increases, and the tensile fracture mode changed from inter-particle dominant fracture to fully dimple ductile fracture.

  17. Impact properties of reduced activation ferritic/martensitic steel, F82H jointed by hot isostatic pressing

    Energy Technology Data Exchange (ETDEWEB)

    Ogiwara, H.; Tanigawa, H. [Japan Atomic Energy Agency, Tokai-mura, Naga-gun, Ibaraki-ken (Japan); Hirose, T. [Blanket Engineering Group, Japan Atomic Energy Agency, Naka, Ibaraki (Japan); Enoeda, M. [Naka Fusion Research Establishment, J.A.E.R.I., Japan Atomic Energy Research Institute, Ibaraki-ken (Japan); Kohyama, A. [Kyoto Univ., lnstitute of Advanced Energy (Japan)

    2007-07-01

    Full text of publication follows: Reduced-activation ferritic/martensitic steels are the leading candidate structural material for the blanket system of fusion reactors. The important issue at the current stage is the finalization of a detailed manufacturing specification for ITER test blanket module. Hot isostatic pressing (HIP) process is one of the most important methods to fabricate the first wall with cooling channels. The objective of this paper is to optimize HIP condition to obtain the excellent joints mechanical properties. The materials used were F82H steels. The joint was produced by solid state HIP method. Before HIP treatments, specimens were heated in vacuum condition to out-gas. This treatment was conducted to decrease oxidation on the surfaces. HIP treatments were carried out for 2 h at 1100 deg. C - 140 MPa. The specimens were normalized at 960 deg. C for 0.5 h and tempered at 750 deg. C for 1.5 h. The bonding interface was characterized by scanning electron microscopy. Charpy impact tests and tensile tests were conducted to evaluate the mechanical properties of the HIP joint. Impact tests revealed that there were no significant differences in the ductile-brittle transition temperatures of HIP jointed specimens and base metal specimens, but the upper-shelf energy (USE) of the HIP joint specimens at room temperature was only about 10% of that of the base metal specimens. SEM observations of the fracture surface of HIP joint specimens revealed that a large number of oxides were formed on the HIP joint. This result indicates that oxides formed on the HIP joint are the dominant factor of the impact properties. Based on these results, the pre-HIP treatment conditions had been optimized to reduce the number of oxides, and USE of HIP joint specimens increased to about 50% of that of the base metal. The detailed analyses on the HIP joint microstructure will be reported. (authors)

  18. Influence of heat treatment on microstructure and tensile behavior of a hot isostatically pressed nickel-based superalloy

    Energy Technology Data Exchange (ETDEWEB)

    Qiu, Chunlei, E-mail: c.qiu@bham.ac.uk [School of Metallurgy and Materials, University of Birmingham, Edgbaston, Birmingham B15 2TT (United Kingdom); Wu, Xinhua; Mei, Junfa [School of Metallurgy and Materials, University of Birmingham, Edgbaston, Birmingham B15 2TT (United Kingdom); Andrews, Paul; Voice, Wayne [Rolls-Royce Plc, Derby DE24 8BJ (United Kingdom)

    2013-11-25

    Highlights: •Post-HIP heat treatment led to refined microstructure and improved tensile properties. •Deformation occurred mainly by forming stacking faults in γ′ at RT and elevated temperature. •Net-shape HIPed RR1000 failed in a transgranular fracture mode. -- Abstract: A nickel-based superalloy powder RR1000 has been hot isostatically pressed (HIPed) and heat treated to produce different microstructures. Microstructures were investigated using a scanning electron microscope (SEM). Tensile testing was performed at room temperature and 700 °C and the deformed samples were examined using SEM and transmission electron microscope (TEM). It was found that in the as-HIPed condition the microstructure consisted of coarse and irregular-shaped primary and secondary γ′ together with a low volume fraction of fine γ′ (<50 nm in diameter). Solution treatment below the γ′ solvus followed by air cooling resulted in the formation of finer cuboidal secondary γ′ (350–750 nm) and medium-sized spherical tertiary γ′ (100–200 nm). This led to an improvement of both the 0.2% yield strength and ultimate tensile strength. Ageing of the solution-treated or of the as-HIPed samples at 760 °C resulted in the precipitation of a high population of fine γ′ (around 50 nm) which further increased the strength. Within the resolution limit of the current TEM analysis, deformation at room temperature seemed to occur mainly by dislocations cutting through secondary γ′ and very fine γ′, accompanied by the formation of stacking faults within these precipitates; most of the medium-sized tertiary γ′ precipitates in solution-treated and aged samples were not cut through but were surrounded by dislocations. Deformation at 700 °C happened by dislocations cutting through γ′ precipitates and γ matrix, leading to the formation of extended stacking faults across both γ and γ′. It is suggested that the optimum treatment of the current powder superalloy is to

  19. Influence of heat treatment on microstructure and tensile behavior of a hot isostatically pressed nickel-based superalloy

    International Nuclear Information System (INIS)

    Qiu, Chunlei; Wu, Xinhua; Mei, Junfa; Andrews, Paul; Voice, Wayne

    2013-01-01

    Highlights: •Post-HIP heat treatment led to refined microstructure and improved tensile properties. •Deformation occurred mainly by forming stacking faults in γ′ at RT and elevated temperature. •Net-shape HIPed RR1000 failed in a transgranular fracture mode. -- Abstract: A nickel-based superalloy powder RR1000 has been hot isostatically pressed (HIPed) and heat treated to produce different microstructures. Microstructures were investigated using a scanning electron microscope (SEM). Tensile testing was performed at room temperature and 700 °C and the deformed samples were examined using SEM and transmission electron microscope (TEM). It was found that in the as-HIPed condition the microstructure consisted of coarse and irregular-shaped primary and secondary γ′ together with a low volume fraction of fine γ′ (<50 nm in diameter). Solution treatment below the γ′ solvus followed by air cooling resulted in the formation of finer cuboidal secondary γ′ (350–750 nm) and medium-sized spherical tertiary γ′ (100–200 nm). This led to an improvement of both the 0.2% yield strength and ultimate tensile strength. Ageing of the solution-treated or of the as-HIPed samples at 760 °C resulted in the precipitation of a high population of fine γ′ (around 50 nm) which further increased the strength. Within the resolution limit of the current TEM analysis, deformation at room temperature seemed to occur mainly by dislocations cutting through secondary γ′ and very fine γ′, accompanied by the formation of stacking faults within these precipitates; most of the medium-sized tertiary γ′ precipitates in solution-treated and aged samples were not cut through but were surrounded by dislocations. Deformation at 700 °C happened by dislocations cutting through γ′ precipitates and γ matrix, leading to the formation of extended stacking faults across both γ and γ′. It is suggested that the optimum treatment of the current powder superalloy is to

  20. Effect of standard heat treatment on the microstructure and mechanical properties of hot isostatically pressed superalloy inconel 718

    International Nuclear Information System (INIS)

    Rao, G. Appa; Kumar, Mahendra; Srinivas, M.; Sarma, D.S.

    2003-01-01

    Ni-Fe base superalloy, Inconel 718, was processed through powder metallurgy (P/M) hot isostatic pressing (HIP) route. In order to balance the strength and ductility, the HIPed material was given the standard heat treatment, viz. solution treatment at 980 deg. C for 1 h/water quenched (WQ) to room temperature and a two-step ageing treatment consisting of 720 deg. C for 8 h/furnace cooling (FC) at 55 deg. C h -1 to 620 deg. C and holding at 620 deg. C for 8 h before air cooling (AC) to room temperature. Optical microscopy and scanning electron microscopy (SEM) studies on the heat treated alloy have shown a homogeneous microstructure with fine grain size (25 μm) along with the presence of prior particle boundary (PPB) networks. Transmission electron microscopy (TEM) on the heat treated material has revealed the presence of oxides, MC carbides and δ-precipitates at the grain boundaries and a uniform precipitation of fine γ'' and γ' strengthening phases in the matrix. Tensile and stress rupture tests were performed on the heat treated material. While the yield strength (YS) and ultimate tensile strength (UTS) of the HIPed and heat treated alloy at room temperature and 650 deg. C were comparable to those of conventionally processed wrought IN 718, its ductility was lower. The stress rupture life of the HIPed alloy improved marginally due to heat treatment and met the minimum specification requirement of life hours but the rupture ductility was found to be inferior to that of the wrought material. The fractography of the failed samples has revealed the transgranular ductile mode of fracture in the as-solution treated alloy, while intergranular mode of failure with the decohesion of PPBs occurred more predominantly in the aged condition. This change of fracture mode with ageing treatment shows the ductility dependence on the relative strength of the matrix and PPBs. The TEM studies on the deformed alloy have revealed that the brittle oxides and carbides at the prior

  1. Effects of hot isostatic pressing on the elastic modulus and tensile properties of 316L parts made by powder bed laser fusion

    Energy Technology Data Exchange (ETDEWEB)

    Lavery, N.P., E-mail: N.P.Lavery@swansea.ac.uk [Materials Research Centre, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom); Zienkiewicz Centre for Computational Engineering, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom); Cherry, J.; Mehmood, S. [Materials Research Centre, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom); Zienkiewicz Centre for Computational Engineering, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom); Davies, H. [Materials Research Centre, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom); Girling, B.; Sackett, E. [Materials Research Centre, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom); Zienkiewicz Centre for Computational Engineering, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom); Brown, S.G.R. [Materials Research Centre, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom); Sienz, J. [Zienkiewicz Centre for Computational Engineering, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom)

    2017-05-02

    The microstructure and mechanical properties of 316L steel have been examined for parts built by a powder bed laser fusion process, which uses a laser to melt and build parts additively on a layer by layer basis. Relative density and porosity determined using various experimental techniques were correlated against laser energy density. Based on porosity sizes, morphology and distributions, the porosity was seen to transition between an irregular, highly directional porosity at the low laser energy density and a smaller, more rounded and randomly distributed porosity at higher laser energy density, thought to be caused by keyhole melting. In both cases, the porosity was reduced by hot isostatic pressing (HIP). High throughput ultrasound based measurements were used to calculate elasticity properties and show that the lower porosities from builds with higher energy densities have higher elasticity moduli in accordance with empirical relationships, and hot isostatic pressing improves the elasticity properties to levels associated with wrought/rolled 316L. However, even with hot isostatic pressing the best properties were obtained from samples with the lowest porosity in the as-built condition. A finite element stress analysis based on the porosity microstructures was undertaken, to understand the effect of pore size distributions and morphology on the Young's modulus. Over 1–5% porosity range angular porosity was found to reduce the Young's modulus by 5% more than rounded porosity. Experimentally measured Young's moduli for samples treated by HIP were closer to the rounded trends than the as-built samples, which were closer to angular trends. Tensile tests on specimens produced at optimised machine parameters displayed a high degree of anisotropy in the build direction and test variability for as-built parts, especially between vertical and horizontal build directions. The as-built properties were generally found to have a higher yield stress, but

  2. Effects of hot isostatic pressing on the elastic modulus and tensile properties of 316L parts made by powder bed laser fusion

    International Nuclear Information System (INIS)

    Lavery, N.P.; Cherry, J.; Mehmood, S.; Davies, H.; Girling, B.; Sackett, E.; Brown, S.G.R.; Sienz, J.

    2017-01-01

    The microstructure and mechanical properties of 316L steel have been examined for parts built by a powder bed laser fusion process, which uses a laser to melt and build parts additively on a layer by layer basis. Relative density and porosity determined using various experimental techniques were correlated against laser energy density. Based on porosity sizes, morphology and distributions, the porosity was seen to transition between an irregular, highly directional porosity at the low laser energy density and a smaller, more rounded and randomly distributed porosity at higher laser energy density, thought to be caused by keyhole melting. In both cases, the porosity was reduced by hot isostatic pressing (HIP). High throughput ultrasound based measurements were used to calculate elasticity properties and show that the lower porosities from builds with higher energy densities have higher elasticity moduli in accordance with empirical relationships, and hot isostatic pressing improves the elasticity properties to levels associated with wrought/rolled 316L. However, even with hot isostatic pressing the best properties were obtained from samples with the lowest porosity in the as-built condition. A finite element stress analysis based on the porosity microstructures was undertaken, to understand the effect of pore size distributions and morphology on the Young's modulus. Over 1–5% porosity range angular porosity was found to reduce the Young's modulus by 5% more than rounded porosity. Experimentally measured Young's moduli for samples treated by HIP were closer to the rounded trends than the as-built samples, which were closer to angular trends. Tensile tests on specimens produced at optimised machine parameters displayed a high degree of anisotropy in the build direction and test variability for as-built parts, especially between vertical and horizontal build directions. The as-built properties were generally found to have a higher yield stress, but lower upper

  3. Manufacturing and mechanical property test of the large-scale oxide dispersion strengthened martensitic mother tube by hot isostatic pressing and hot extrusion process

    International Nuclear Information System (INIS)

    Narita, Takeshi; Ukai, Shigeharu; Kaito, Takeji; Ohtsuka, Satoshi; Fujiwara, Masayuki

    2003-09-01

    Mass production capability of Oxide Dispersion Strengthened (ODS) ferritic steel cladding (9Cr) is evaluated in the Phase II of the Feasibility Studies on Commercialized Fast Reactor Cycle System. The cost for manufacturing mother tube is a dominant factor in the total cost for manufacturing ODS ferritic cladding. In this study, the large-scale 9Cr-ODS martensitic mother tube was produced by overseas supplier with mass production equipments for commercialized ODS steels. The process of manufacturing the ODS mother tube consists of raw material powder production, mechanical alloying by high energy ball mill, hot isostatic pressing(HIP), and hot extrusion. Following results were obtained in this study. (1) Micro structure of the ODS steels is equivalent to that of domestic products, and fine oxides are uniformly distributed. The mechanical alloying by large capacity (1 ton) ball mill can be satisfactorily carried out. (2) A large scale mother tube (65 mm OD x 48 mm ID x 10,000 mm L), which can produce about 60 pieces of 3 m length ODS ferritic claddings by four times cold rolling, have been successfully manufactured through HIP and Hot Extrusion process. (3) Rough surface of the mother tubes produced in this study can be improved by selecting the reasonable hot extrusion condition. (4) Hardness and tensile strength of the manufactured ODS steels are lower than domestic products with same chemical composition. This is owing to the high aluminum content in the product, and those properties could be improved by decreasing the aluminum content in the raw material powder. (author)

  4. Effect of heat treatment and hot isostatic pressing on the microstructure and mechanical properties of Inconel 625 alloy processed by laser powder bed fusion

    Energy Technology Data Exchange (ETDEWEB)

    Kreitcberg, Alena, E-mail: alena.kreitcberg.1@ens.etsmtl.ca [École de technologie supérieure, 110 Notre-Dame Street West, Montreal, Quebec H3C 1K3 Canada (Canada); Brailovski, Vladimir, E-mail: vladimir.brailovski@etsmtl.ca [École de technologie supérieure, 110 Notre-Dame Street West, Montreal, Quebec H3C 1K3 Canada (Canada); Turenne, Sylvain, E-mail: sylvain.turenne@polymtl.ca [École Polytechnique de Montréal, 2900 boul. Édouard-Montpetit, Montreal, Quebec H3T 1J4 Canada (Canada)

    2017-03-24

    The effect of different heat treatments and hot isostatic pressing on the microstructure and mechanical properties of laser powder bed fusion IN625 alloy was studied. The heat treatments were: stress relief annealing, recrystallization annealing and low-temperature solution treatment. The resulting microstructure and crystallographic textures were studied using optical and scanning electron microscopy. The mechanical properties of the as-built and post-treated IN625 alloy were obtained after tensile testing at room temperature and at 760 °C (1400 °F), and compared to those of an annealed wrought alloy of the same composition.

  5. Comparative evaluation of electrical conductivity of hydroxyapatite ceramics densified through ramp and hold, spark plasma and post sinter Hot Isostatic Pressing routes

    Energy Technology Data Exchange (ETDEWEB)

    Buchi Suresh, M., E-mail: suresh@arci.res.in; Biswas, P.; Mahender, V.; Johnson, Roy, E-mail: royjohnson@arci.res.in

    2017-01-01

    Hydroxyapatite ceramics synthesized through sonochemical route were processed and densified through ramp & hold (R&H) and Spark Plasma Sintering (SPS) routes. The effect of processing route on the relative density and electrical conductivity were studied. Further, the samples were Hot Isostatically Pressed (HIP) under argon pressure at elevated temperature to further densify the sample. All these samples processed under different conditions were characterized by X-ray diffraction, Scanning Electron Microscopy and AC Conductivity. The samples have exhibited hydroxyapatite phase; however, microstructures exhibited distinctly different grain morphologies and grain sizes. AC impedance spectroscopic measurement was carried out on hydroxyapatite samples processed through different routes and the corresponding spectra were analyzed by the analogy to equivalent circuit involving resistors and capacitors. SPS sintered sample after HIPing has exhibited the highest conductivity. This can be attributed to the higher density in combination with finer grain sizes. Activation energy based on Arrhenius equation is calculated and the prominent conduction mechanism is proposed. - Highlights: • Hot Isostatic Pressing (HIP) of SPS and R&H processed samples has resulted into densities near to theoretical densities • No change in the crystal structure is observed in SPS and R&H samples before and after HIP treatment • SPS processed and HIP treated samples resulted into higher conductivities with smaller grain sizes and grain boundary area.

  6. Formation of ultra-fine grained TiC-dispersed SUS316L by ball-milling and their consolidation by hot isostatic pressing

    International Nuclear Information System (INIS)

    Zheng, Yongjia; Yamasaki, Tohru; Fukami, Takeshi; Mitamura, Tohru; Terasawa, Mititaka

    2003-01-01

    In order to overcome the irradiation embrittlement in austenitic stainless steels, ultra-fine grained SUS316L steels with very fine TiC particles have been developed. The SUS316-TiC nanocomposite powders having 1.0 to 2.0 mass%TiC were prepared by ball-milling SUS316-TiC powder mixtures for 125h in an argon gas atmosphere. The milled powders were consolidated by hot isostatic pressing (HIP) under a pressure of 200 MPa at temperature between 700-1000degC, and the bulk materials with crystallite size ranging between 100-400 nm have been produced. The possibility of using fine-grained TiC particles for pinning grain boundaries and thereby to maintain the ultra-fine grained structures has been discussed. (author)

  7. Influence of Powder Surface Contamination in the Ni-Based Superalloy Alloy718 Fabricated by Selective Laser Melting and Hot Isostatic Pressing

    Directory of Open Access Journals (Sweden)

    Yen-Ling Kuo

    2017-09-01

    Full Text Available The aim of this study was to gain a deep understanding of the microstructure-mechanical relationship between solid-state sintering and full-melting processes. The IN718 superalloy was fabricated by hot isostatic pressing (HIP and selective laser melting (SLM. Continuous precipitates were clearly localized along the prior particle boundary (PPB in the HIP materials, while SLM materials showed a microstructure free of PPB. The mechanical properties of specimens that underwent SLM + solution treatment and aging were comparable to those of conventional wrought specimens both at room temperature and 650 °C. However, a drop was observed in the ductility of HIP material at 650 °C. The brittle particles along the PPB were found to affect the HIP materials’ creep life and ductility during solid-state sintering.

  8. Tensile ductility of an AlCoCrFeNi multi-phase high-entropy alloy through hot isostatic pressing (HIP) and homogenization

    Energy Technology Data Exchange (ETDEWEB)

    Tang, Zhi, E-mail: Zhi.Tang@alcoa.com [Department of Materials Science and Engineering, The University of Tennessee, Knoxville, TN 37996 (United States); Department of Materials Science and Engineering, Virginia Tech, Blacksburg, VA 24061 (United States); Senkov, Oleg N. [Air Force Research Laboratory, Materials and Manufacturing Directorate, Wright-Patterson Air Force Base, OH 45433 (United States); Parish, Chad M. [Oak Ridge National Laboratory, Oak Ridge, TN 37831 (United States); Zhang, Chuan; Zhang, Fan [CompuTherm LLC, 437 S. Yellowstone Dr., Suite 217, Madison, WI 53719 (United States); Santodonato, Louis J. [Department of Materials Science and Engineering, The University of Tennessee, Knoxville, TN 37996 (United States); Oak Ridge National Laboratory, Oak Ridge, TN 37831 (United States); Wang, Gongyao [Department of Materials Science and Engineering, The University of Tennessee, Knoxville, TN 37996 (United States); Zhao, Guangfeng; Yang, Fuqian [Department of Chemical and Materials Engineering, University of Kentucky, Lexington, KY 40506 (United States); Liaw, Peter K., E-mail: pliaw@utk.edu [Department of Materials Science and Engineering, The University of Tennessee, Knoxville, TN 37996 (United States)

    2015-10-28

    The microstructure and phase composition of an AlCoCrFeNi high-entropy alloy (HEA) were studied in as-cast (AlCoCrFeNi-AC, AC represents as-cast) and homogenized (AlCoCrFeNi-HP, HP signifies hot isostatic pressed and homogenized) conditions. The AlCoCrFeNi-AC ally has a dendritric structure in the consisting primarily of a nano-lamellar mixture of A2 (disordered body-centered-cubic (BCC)) and B2 (ordered BCC) phases, formed by an eutectic reaction. The homogenization heat treatment, consisting of hot isostatic pressed for 1 h at 1100 °C, 207 MPa and annealing at 1150 °C for 50 h, resulted in an increase in the volume fraction of the A1 phase and formation of a Sigma (σ) phase. Tensile properties in as-cast and homogenized conditions are reported at 700 °C. The ultimate tensile strength was virtually unaffected by heat treatment, and was 396±4 MPa at 700 °C. However, homogenization produced a noticeable increase in ductility. The AlCoCrFeNi-AC alloy showed a tensile elongation of only 1.0%, while after the heat-treatment, the elongation of AlCoCrFeNi-HP was 11.7%. Thermodynamic modeling of non-equilibrium and equilibrium phase diagrams for the AlCoCrFeNi HEA gave good agreement with the experimental observations of the phase contents in the AlCoCrFeNi-AC and AlCoCrFeNi-HP. The reasons for the improvement of ductility after the heat treatment and the crack initiation subjected to tensile loading were discussed.

  9. The effect of pre-treatment parameters on the quality of glass-ceramic wasteforms for plutonium immobilisation, consolidated by hot isostatic pressing

    Energy Technology Data Exchange (ETDEWEB)

    Thornber, Stephanie M.; Heath, Paul G. [Immobilisation Science Laboratory, Department of Materials Science & Engineering, The University of Sheffield, Sir Robert Hadfield Building, Mappin Street, Sheffield S1 3JD (United Kingdom); Da Costa, Gabriel P. [Immobilisation Science Laboratory, Department of Materials Science & Engineering, The University of Sheffield, Sir Robert Hadfield Building, Mappin Street, Sheffield S1 3JD (United Kingdom); Department of Chemical Engineering & Petroleum Engineering, Universidade Federal Fluminense, Rua Passo da Patria 156, CEP 24210-240, Niteroi, RJ (Brazil); Stennett, Martin C. [Immobilisation Science Laboratory, Department of Materials Science & Engineering, The University of Sheffield, Sir Robert Hadfield Building, Mappin Street, Sheffield S1 3JD (United Kingdom); Hyatt, Neil C., E-mail: n.c.hyatt@sheffield.ac.uk [Immobilisation Science Laboratory, Department of Materials Science & Engineering, The University of Sheffield, Sir Robert Hadfield Building, Mappin Street, Sheffield S1 3JD (United Kingdom)

    2017-03-15

    Glass-ceramics with high glass fractions (70 wt%) were fabricated in stainless steel canisters by hot isostatic pressing (HIP), at laboratory scale. High (600 °C) and low (300 °C) temperature pre-treatments were investigated to reduce the canister evacuation time and to understand the effect on the phase assemblage and microstructure of the hot isostatically pressed product. Characterisation of the HIPed materials was performed using scanning electron microscopy (SEM), coupled with energy dispersive X-ray analysis (EDX) and powder X-ray diffraction (XRD). This analysis showed the microstructure and phase assemblage was independent of the variation in pre-treatment parameters. It was demonstrated that a high temperature pre-treatment of batch reagents, prior to the HIP cycle, is beneficial when using oxide precursors, in order to remove volatiles and achieve high quality dense materials. Sample throughput can be increased significantly by utilising a high temperature ex-situ calcination prior to the HIP cycle. Investigation of glass-ceramic wasteform processing utilising a glass frit precursor, produced a phase assemblage and microstructure comparable to that obtained using oxide precursors. The use of a glass frit precursor should allow optimised throughput of waste packages in a production facility, avoiding the need for a calcination pre-treatment required to remove volatiles from oxide precursors. - Highlights: • Optimisation of pre-treatment parameters for HIP glass-ceramics was investigated. • Entrained porosity was minimised by ex-situ bake-out of oxide precursors at 600 °C. • Phase assemblage and microstructure proved independent of bake-out parameters. • Use of glass-frit precursor further improved process s throughput and simplification.

  10. The effect of pre-treatment parameters on the quality of glass-ceramic wasteforms for plutonium immobilisation, consolidated by hot isostatic pressing

    International Nuclear Information System (INIS)

    Thornber, Stephanie M.; Heath, Paul G.; Da Costa, Gabriel P.; Stennett, Martin C.; Hyatt, Neil C.

    2017-01-01

    Glass-ceramics with high glass fractions (70 wt%) were fabricated in stainless steel canisters by hot isostatic pressing (HIP), at laboratory scale. High (600 °C) and low (300 °C) temperature pre-treatments were investigated to reduce the canister evacuation time and to understand the effect on the phase assemblage and microstructure of the hot isostatically pressed product. Characterisation of the HIPed materials was performed using scanning electron microscopy (SEM), coupled with energy dispersive X-ray analysis (EDX) and powder X-ray diffraction (XRD). This analysis showed the microstructure and phase assemblage was independent of the variation in pre-treatment parameters. It was demonstrated that a high temperature pre-treatment of batch reagents, prior to the HIP cycle, is beneficial when using oxide precursors, in order to remove volatiles and achieve high quality dense materials. Sample throughput can be increased significantly by utilising a high temperature ex-situ calcination prior to the HIP cycle. Investigation of glass-ceramic wasteform processing utilising a glass frit precursor, produced a phase assemblage and microstructure comparable to that obtained using oxide precursors. The use of a glass frit precursor should allow optimised throughput of waste packages in a production facility, avoiding the need for a calcination pre-treatment required to remove volatiles from oxide precursors. - Highlights: • Optimisation of pre-treatment parameters for HIP glass-ceramics was investigated. • Entrained porosity was minimised by ex-situ bake-out of oxide precursors at 600 °C. • Phase assemblage and microstructure proved independent of bake-out parameters. • Use of glass-frit precursor further improved process s throughput and simplification.

  11. Hot-isostatic pressing of U-10Zr by grain boundary diffusion and creep cavitation. Part 2: Theory and data analysis

    International Nuclear Information System (INIS)

    McDeavitt, S.M.; Solomon, A.A.

    1997-01-01

    Uranium-10 wt % zirconium (U-10Zr) is a fuel alloy that has been used in the Experimental Breeder Reactor-II (EBR-II). The high burnup that was desired in this fuel system made high demands on the mechanical compatibility between fuel and cladding both during normal operation and during safety-related transients when rapid differential expansion may cause high stresses. In general, this mechanical stress can be reduced by cladding deformation if the cladding is sufficiently ductile at high burnup, and/or by fuel hot-pressing. Fortunately, the fuel is very porous when it contacts the cladding, but this porosity gradually fills with solid fission products (primarily lanthanides) that may limit the fuel's compressibility. If the porosity remains open, gaseous fission products are released and the porous fuel creeps rather than hot-presses under contact stresses. If the pores are closed by sintering or by solid fission products, the porous fuel will hot-isostatic press (HIP), as represented by the models to be discussed. HIP experiments performed at 700 C on U-10Zr samples with different impurity phase contents (Part 1) are analyzed in terms of several creep cavitation models. The coupled diffusion/creep cavitation model of Chen and Argon shows good quantitative agreement with measured HIP rates for hydride- and metal-derived U-10Zr materials, assuming that pores are uniformly distributed on grain boundaries and are of modal size, and that far-field strain rates are negligible. The analysis predicts, for the first time, an asymmetry between HIP and swelling at identical pressure-induced driving forces due to differences in grain boundary stresses. The differences in compressibility of hydride- and metal-derived U-10Zr can be partially explained by differences in pore size and spacing. The relevance of the experiments to description of in-reactor densification under external pressure or contact stress due to fuel/cladding mechanical interaction is discussed

  12. Sintering of ZrC by hot isostatic pressing (HIP) and spark plasma sintering (SPS). Effect of impurities

    International Nuclear Information System (INIS)

    Allemand, Alexandre; Le Flem - Dormeval, Marion; Guillard, Francois

    2005-01-01

    Carbides are generally used as structural materials for high temperature applications. Particularly, ZrC because of low activation, neutronic transparency, cubic structure (isotropic behaviour) and good thermal conductivity, is one of the candidates under consideration for structural materials in the core of new high temperature nuclear reactors (Generation IV). Just a few studies about densification of monolithic ZrC exist. They mainly involve natural sintering or hot pressing at high temperature (until 2700 deg. C). Unfortunately those processes induce grain growth and do not lead to fully densified ZrC. The aim of this study is to compare the characteristics and the properties of ZrC sintered by HIP and by SPS. Fully dense ZrC can be reached either by HIP or by SPS, grain size being more or less controlled. Microstructural observations and mechanical testing of several ZrC grades shows that powder impurities play an important role in the quality of the grain boundaries and consequently in the mechanical properties. In particular, the porosity falls from 17% to 3 % just by reducing the free carbon content in starting ZrC powder. The densification process of dense monolithic ZrC was improved by combining a HIP at 1600 deg. C (titanium canning) followed by a post-HIP at 1900 deg. C (no canning required). Four-point bending tests are in progress to confirm the improvement of fracture strength. (authors)

  13. Enhancement in the microstructure and neutron shielding efficiency of sandwich type of 6061Al–B4C composite material via hot isostatic pressing

    International Nuclear Information System (INIS)

    Park, Jin-Ju; Hong, Sung-Mo; Lee, Min-Ku; Rhee, Chang-Kyu; Rhee, Won-Hyuk

    2015-01-01

    Highlights: • 6061Al–B 4 C neutron shielding composites are fabricated by sintering and HIP. • HIP process improves the wettability of B 4 C particles into 6061Al matrix. • Neutron attenuation performance can be enhanced by application of HIP process. - Abstract: Sandwich type of 6061Al–B 4 C composite plates, which are used as a thermal neutron absorber for spent nuclear fuel pool storage rack, were fabricated using two different consolidation ways as sintering and hot isostatic pressing (HIP) processes and their thermal neutron shielding efficiency was investigated as a function of B 4 C concentration ranging from 0 to 40 wt.%. For this purpose, two respective inner core compaction parts of sintered and HIPped neutron absorbing composite materials were first produced and then cladded them between two outer plates by HIP process. The application of HIP process provided not only a lead of excellent interfacial adhesion due to the improved wettability but also an enhancement of thermal neutron shielding efficiency owing to the more uniform dispersion of B 4 C particles

  14. Development of manufacturing technology of radial plate in superconducting coil for fusion reactor by diffusion bonding by Hot Isostatic Pressing (HIP)

    International Nuclear Information System (INIS)

    Takano, Katsutoshi; Koizumi, Norikiyo; Masuo, Hiroshi; Natsume, Yoshihisa

    2014-01-01

    The radial plates (RPs), which is used in Toroidal field (TF) coil in ITER, are quite large, such as 13 m tall and 9 m wide, but thin, such as 10 cm thick, and are made of stainless steel. Even though they are very large structures, they require very high manufacturing tolerances and high mechanical strength at 4 K. The similar requirements will be required in the next generation fusion reactor. Therefore, the authors intend to develop efficient manufacturing methods in parallel with ITER TF coil RP manufacture. The authors therefore performed trial manufacture of the RP segments using a diffusion bonding method, namely Hot Isostatic Pressing (HIP). As a result of trials, it was clarified that even when HIPping is applied, the mechanical characteristic of base metal is not deteriorated. The machining period can be reduced by about 1/3 compared with the traditional manufacturing method. On the other hand, mechanical strength at 4 K is degraded due to weak bonding, that is no grain growth through joint, by HIPping. However, additional test indicates promising possibility of much better joint by higher temperature and joint surface treated HIPpings. These results justified that RP segment manufacturing is not only possible, but it is a technically valid manufacturing method that satisfies all requirements. (author)

  15. Selective Electron Beam Manufacturing of Ti-6Al-4V Strips: Effect of Build Orientation, Columnar Grain Orientation, and Hot Isostatic Pressing on Tensile Properties

    Science.gov (United States)

    Wang, J.; Tang, H. P.; Yang, K.; Liu, N.; Jia, L.; Qian, M.

    2018-03-01

    Many novel designs for additive manufacturing (AM) contain thin-walled (≤ 3 mm) sections in different orientations. Selective electron beam melting (SEBM) is particularly suited to AM of such thin-walled titanium components because of its high preheating temperature and high vacuum. However, experimental data on SEBM of Ti-6Al-4V thin sections remains scarce because of the difficulty and high cost of producing long, thin and smooth strip tensile specimens (see Fig. 1). In this study, 80 SEBM Ti-6Al-4V strips (180 mm long, 42 mm wide, 3 mm thick) were built both vertically (V-strips) and horizontally (H-strips). Their density, microstructure and tensile properties were investigated. The V-strips showed clearly higher tensile strengths but lower elongation than the H-strips. Hot isostatic pressing (HIP) produced the same lamellar α-β microstructures in terms of the average α-lath thickness in both types of strips. The retained prior-β columnar grain boundaries after HIP showed no measurable influence on the tensile properties, irrespective of their length and orientation, because of the formation of randomly distributed fine α-laths.[Figure not available: see fulltext.

  16. Effects of long-time elevated temperature exposures on hot-isostatically-pressed power-metallurgy Udimet 700 alloys with reduced cobalt contents

    Science.gov (United States)

    Hart, F. H.

    1984-01-01

    Because almost the entire U.S. consumption of cobalt depends on imports, this metal has been designated "strategic'. The role and effectiveness of cobalt is being evaluated in commercial nickel-base superalloys. Udiment 700 type alloys in which the cobalt content was reduced from the normal 17% down to 12.7%, 8.5%, 4.3%, and 0% were prepared by standard powder metallurgy techniques and hot isostatically pressed into billets. Mechanical testing and microstructural investigations were performed. The mechanical properties of alloys with reduced cobalt contents which were heat-treated identically were equal or better than those of the standard alloy, except that creep rates tended to increase as cobalt was reduced. The effects of long time exposures at 760 C on mechanical properties and at 760 C and 845 C on microstructures were determined. Decreased tensile properties and shorter rupture lives with increased creep rates were observed in alloy modifications. The exposures caused gamma prime particle coarsening and formation of sigma phase in the alloys with higher cobalt contents. Exposure at 845 C also reduced the amount of MC carbides.

  17. Production of an impermeable composite of irradiated graphite and glass by hot isostatic pressing as a long term leach resistant waste form

    Energy Technology Data Exchange (ETDEWEB)

    Fachinger, Johannes; Muller, Walter [FNAG ZU Hanau, Hanau (Germany); Marsat, Eric [FNAG SAS Le Pont de Claix (France); Grosse, Karl-Heinz; Seemann, Richard [ALD Hanau (Germany); Scales, Charlie; Easton, Michael Mark [NNL, Workington (United Kingdom); Anthony Banford [NNL, Warrington (United Kingdom); University of Manchester, Manchester (United Kingdom)

    2013-07-01

    negligible porosity and a water impermeable structure. Structural analysis shows that the glass in the composite has replaced the pores in the graphite structure. The typical pore volume of a graphite material is in the range of 20 vol.%. Therefore no volume increase will occur in comparison with the former graphite material. This IGM material will allow the encapsulation of graphite with package densities larger than 1.5 ton per cubic meter. Therefore a huge volume saving can be achieved by such an alternative encapsulation method. Disposal performance is also enhanced since little or no leaching of radionuclides is observed due to the impermeability of the material NNL and FNAG have proved that IGM can be produced by hot isostatic pressing (HIP) which has several advantages for radioactive materials over the HVP process. - The sealed HIP container avoids the release of any radionuclides. - The outside of the waste package is not contaminated. - The HIP process time is shorter than the HVP process time. The isostatic press avoids anisotropic density distributions. - Simple filling of the HIP container has advantages over the filling of an axial die. (authors)

  18. Production of an impermeable composite of irradiated graphite and glass by hot isostatic pressing as a long term leach resistant waste form

    International Nuclear Information System (INIS)

    Fachinger, Johannes; Muller, Walter; Marsat, Eric; Grosse, Karl-Heinz; Seemann, Richard; Scales, Charlie; Easton, Michael Mark; Anthony Banford

    2013-01-01

    negligible porosity and a water impermeable structure. Structural analysis shows that the glass in the composite has replaced the pores in the graphite structure. The typical pore volume of a graphite material is in the range of 20 vol.%. Therefore no volume increase will occur in comparison with the former graphite material. This IGM material will allow the encapsulation of graphite with package densities larger than 1.5 ton per cubic meter. Therefore a huge volume saving can be achieved by such an alternative encapsulation method. Disposal performance is also enhanced since little or no leaching of radionuclides is observed due to the impermeability of the material NNL and FNAG have proved that IGM can be produced by hot isostatic pressing (HIP) which has several advantages for radioactive materials over the HVP process. - The sealed HIP container avoids the release of any radionuclides. - The outside of the waste package is not contaminated. - The HIP process time is shorter than the HVP process time. The isostatic press avoids anisotropic density distributions. - Simple filling of the HIP container has advantages over the filling of an axial die. (authors)

  19. Growth kinetics and microstructural evolution during hot isostatic pressing of U-10 wt.% Mo monolithic fuel plate in AA6061 cladding with Zr diffusion barrier

    International Nuclear Information System (INIS)

    Park, Y.; Yoo, J.; Huang, K.; Keiser, D.D.; Jue, J.F.; Rabin, B.; Moore, G.; Sohn, Y.H.

    2014-01-01

    Phase constituents and microstructure changes in RERTR fuel plate assemblies as functions of temperature and duration of hot-isostatic pressing (HIP) during fabrication were examined. The HIP process was carried out as functions of temperature (520, 540, 560 and 580 °C for 90 min) and time (45–345 min at 560 °C) to bond 6061 Al-alloy to the Zr diffusion barrier that had been co-rolled with U-10 wt.% Mo (U10Mo) fuel monolith prior to the HIP process. Scanning and transmission electron microscopies were employed to examine the phase constituents, microstructure and layer thickness of interaction products from interdiffusion. At the interface between the U10Mo and Zr, following the co-rolling, the UZr 2 phase was observed to develop adjacent to Zr, and the α-U phase was found between the UZr 2 and U10Mo, while the Mo 2 Zr was found as precipitates mostly within the α-U phase. The phase constituents and thickness of the interaction layer at the U10Mo-Zr interface remained unchanged regardless of HIP processing variation. Observable growth due to HIP was only observed for the (Al,Si) 3 Zr phase found at the Zr/AA6061 interface, however, with a large activation energy of 457 ± 28 kJ/mole. Thus, HIP can be carried to improve the adhesion quality of fuel plate without concern for the excessive growth of the interaction layer, particularly at the U10Mo-Zr interface with the α-U, Mo 2 Zr, and UZr 2 phases

  20. Growth kinetics and microstructural evolution during hot isostatic pressing of U-10 wt.% Mo monolithic fuel plate in AA6061 cladding with Zr diffusion barrier

    Energy Technology Data Exchange (ETDEWEB)

    Park, Y.; Yoo, J.; Huang, K. [Advanced Materials Processing and Analysis Center, Department of Materials Science and Engineering, University of Central Florida, Orlando, FL 32816 (United States); Keiser, D.D.; Jue, J.F.; Rabin, B.; Moore, G. [Idaho National Laboratory, PO Box 1625, Idaho Falls, ID 83401 (United States); Sohn, Y.H., E-mail: Yongho.sohn@ucf.edu [Advanced Materials Processing and Analysis Center, Department of Materials Science and Engineering, University of Central Florida, Orlando, FL 32816 (United States)

    2014-04-01

    Phase constituents and microstructure changes in RERTR fuel plate assemblies as functions of temperature and duration of hot-isostatic pressing (HIP) during fabrication were examined. The HIP process was carried out as functions of temperature (520, 540, 560 and 580 °C for 90 min) and time (45–345 min at 560 °C) to bond 6061 Al-alloy to the Zr diffusion barrier that had been co-rolled with U-10 wt.% Mo (U10Mo) fuel monolith prior to the HIP process. Scanning and transmission electron microscopies were employed to examine the phase constituents, microstructure and layer thickness of interaction products from interdiffusion. At the interface between the U10Mo and Zr, following the co-rolling, the UZr{sub 2} phase was observed to develop adjacent to Zr, and the α-U phase was found between the UZr{sub 2} and U10Mo, while the Mo{sub 2}Zr was found as precipitates mostly within the α-U phase. The phase constituents and thickness of the interaction layer at the U10Mo-Zr interface remained unchanged regardless of HIP processing variation. Observable growth due to HIP was only observed for the (Al,Si){sub 3}Zr phase found at the Zr/AA6061 interface, however, with a large activation energy of 457 ± 28 kJ/mole. Thus, HIP can be carried to improve the adhesion quality of fuel plate without concern for the excessive growth of the interaction layer, particularly at the U10Mo-Zr interface with the α-U, Mo{sub 2}Zr, and UZr{sub 2} phases.

  1. Growth kinetics and microstructural evolution during hot isostatic pressing of U-10 wt.% Mo monolithic fuel plate in AA6061 cladding with Zr diffusion barrier

    Science.gov (United States)

    Park, Y.; Yoo, J.; Huang, K.; Keiser, D. D.; Jue, J. F.; Rabin, B.; Moore, G.; Sohn, Y. H.

    2014-04-01

    Phase constituents and microstructure changes in RERTR fuel plate assemblies as functions of temperature and duration of hot-isostatic pressing (HIP) during fabrication were examined. The HIP process was carried out as functions of temperature (520, 540, 560 and 580 °C for 90 min) and time (45-345 min at 560 °C) to bond 6061 Al-alloy to the Zr diffusion barrier that had been co-rolled with U-10 wt.% Mo (U10Mo) fuel monolith prior to the HIP process. Scanning and transmission electron microscopies were employed to examine the phase constituents, microstructure and layer thickness of interaction products from interdiffusion. At the interface between the U10Mo and Zr, following the co-rolling, the UZr2 phase was observed to develop adjacent to Zr, and the α-U phase was found between the UZr2 and U10Mo, while the Mo2Zr was found as precipitates mostly within the α-U phase. The phase constituents and thickness of the interaction layer at the U10Mo-Zr interface remained unchanged regardless of HIP processing variation. Observable growth due to HIP was only observed for the (Al,Si)3Zr phase found at the Zr/AA6061 interface, however, with a large activation energy of 457 ± 28 kJ/mole. Thus, HIP can be carried to improve the adhesion quality of fuel plate without concern for the excessive growth of the interaction layer, particularly at the U10Mo-Zr interface with the α-U, Mo2Zr, and UZr2 phases.

  2. The positive effect of hot isostatic pressing on improving the anisotropies of bending and impact properties in selective laser melted Ti-6Al-4V alloy

    International Nuclear Information System (INIS)

    Wu, Ming-Wei; Lai, Pang-Hsin

    2016-01-01

    Selective laser melting (SLM) is a versatile additive manufacturing process for fabricating solid or porous metallic materials with complicated three-dimensional shapes. SLM Ti alloys, particularly Ti-6Al-4V, and other alloys have been manufactured and analyzed in numerous studies. However, the high anisotropy of the microstructures and inconsistent mechanical properties of SLM materials have been extensively reported, and these disadvantages could prohibit its widespread use. To clarify how to alleviate the anisotropic behaviors of SLM materials, the main objective of this study was to evaluate the influences of hot isostatic pressing (HIP) on the microstructure, densification, bending strength, impact toughness, and fracture behavior of the as-built Ti-6Al-4V alloy. The results showed that the vertical and horizontal building directions obviously affect the bending and impact properties of as-built alloys. The transverse rupture strength (TRS) and impact energy of the horizontally-built alloy were respectively found to be 48% and 100% higher than those of the vertically-built one. In the vertically-built alloy, disc-shaped building defects, identified by X-ray computed tomography (CT) and microscopy, obviously reduce the effective load-bearing cross-section and deteriorate the bending and impact performances. After HIP at 1000 °C/150 MPa, the α′-martensite structure in the as-built alloy is transformed into an α+β lamellar one, and the disc-shaped building defects are evidently eliminated. As a result, the impact energies of as-built vertical and horizontal specimens are improved by 28 J (560%) and 19 J (190%), respectively, and the TRS of the as-built vertical alloy is raised by 550 MPa (37%). Consequently, the discrepancies in TRS and impact energy between the HIPed vertical and horizontal specimens are merely 3% and 14%, respectively, and the anisotropic behaviors of the SLM Ti-6Al-4V alloy are thus substantially lessened.

  3. Investigation of the Microstructure and Mechanical Properties of Copper-Graphite Composites Reinforced with Single-Crystal α-Al₂O₃ Fibres by Hot Isostatic Pressing.

    Science.gov (United States)

    Zhang, Guihang; Jiang, Xiaosong; Qiao, ChangJun; Shao, Zhenyi; Zhu, Degui; Zhu, Minhao; Valcarcel, Victor

    2018-06-11

    Single-crystal α-Al₂O₃ fibres can be utilized as a novel reinforcement in high-temperature composites owing to their high elastic modulus, chemical and thermal stability. Unlike non-oxide fibres and polycrystalline alumina fibres, high-temperature oxidation and polycrystalline particles boundary growth will not occur for single-crystal α-Al₂O₃ fibres. In this work, single-crystal α-Al₂O₃ whiskers and Al₂O₃ particles synergistic reinforced copper-graphite composites were fabricated by mechanical alloying and hot isostatic pressing techniques. The phase compositions, microstructures, and fracture morphologies of the composites were investigated using X-ray diffraction, a scanning electron microscope equipped with an X-ray energy-dispersive spectrometer (EDS), an electron probe microscopic analysis equipped with wavelength-dispersive spectrometer, and a transmission electron microscope equipped with EDS. The mechanical properties have been measured by a micro-hardness tester and electronic universal testing machine. The results show that the reinforcements were unevenly distributed in the matrix with the increase of their content and there were some micro-cracks located at the interface between the reinforcement and the matrix. With the increase of the Al₂O₃ whisker content, the compressive strength of the composites first increased and then decreased, while the hardness decreased. The fracture and strengthening mechanisms of the composite materials were explored on the basis of the structure and composition of the composites through the formation and function of the interface. The main strengthening mechanism in the composites was fine grain strengthening and solid solution strengthening. The fracture type of the composites was brittle fracture.

  4. The positive effect of hot isostatic pressing on improving the anisotropies of bending and impact properties in selective laser melted Ti-6Al-4V alloy

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Ming-Wei, E-mail: mwwu@ntut.edu.tw; Lai, Pang-Hsin

    2016-03-21

    Selective laser melting (SLM) is a versatile additive manufacturing process for fabricating solid or porous metallic materials with complicated three-dimensional shapes. SLM Ti alloys, particularly Ti-6Al-4V, and other alloys have been manufactured and analyzed in numerous studies. However, the high anisotropy of the microstructures and inconsistent mechanical properties of SLM materials have been extensively reported, and these disadvantages could prohibit its widespread use. To clarify how to alleviate the anisotropic behaviors of SLM materials, the main objective of this study was to evaluate the influences of hot isostatic pressing (HIP) on the microstructure, densification, bending strength, impact toughness, and fracture behavior of the as-built Ti-6Al-4V alloy. The results showed that the vertical and horizontal building directions obviously affect the bending and impact properties of as-built alloys. The transverse rupture strength (TRS) and impact energy of the horizontally-built alloy were respectively found to be 48% and 100% higher than those of the vertically-built one. In the vertically-built alloy, disc-shaped building defects, identified by X-ray computed tomography (CT) and microscopy, obviously reduce the effective load-bearing cross-section and deteriorate the bending and impact performances. After HIP at 1000 °C/150 MPa, the α′-martensite structure in the as-built alloy is transformed into an α+β lamellar one, and the disc-shaped building defects are evidently eliminated. As a result, the impact energies of as-built vertical and horizontal specimens are improved by 28 J (560%) and 19 J (190%), respectively, and the TRS of the as-built vertical alloy is raised by 550 MPa (37%). Consequently, the discrepancies in TRS and impact energy between the HIPed vertical and horizontal specimens are merely 3% and 14%, respectively, and the anisotropic behaviors of the SLM Ti-6Al-4V alloy are thus substantially lessened.

  5. Hot isostatically-pressed aluminosilicate glass-ceramic with natural crystalline analogues for immobilizing the calcined high-level nuclear waste at the Idaho Chemical Processing Plant

    International Nuclear Information System (INIS)

    Raman, S.

    1993-12-01

    The additives Si, Al, MgO, P 2 O 5 were mechanically blended with fluorinelsodium calcine in varying proportions. The batches were vacuum sealed in stainless steel canisters and hot isostatically pressed at 20,000 PSI and 1000 C for 4 hours. The resulting suite of glass-ceramic waste forms parallels the natural rocks in microstructural and compositional heterogeneity. Several crystalline phases ar analogous in composition and structure to naturally occurring minerals. Additional crystalline phases are zirconia and Ca-Mg borate. The glasses are enriched in silica and alumina. Approximately 7% calcine elements occur dissolved in this glass and the total glass content in the waste forms averages 20 wt%. The remainder of the calcine elements are partitioned into crystalline phases at 75 wt% calcine waste loading. The waste forms were tested for chemical durability in accordance with the MCC1-test procedure. The leach rates are a function of the relative proportions of additives and calcine, which in turn influence the composition and abundances of the glass and crystalline phases. The DOE leach rate criterion of less than 1 g/m 2 -day is met by all the elements B, Cs and Na are increased by lowering the melt viscosity. This is related to increased crystallization or devitrification with increases in MgO addition. This exploratory work has shown that the increases in waste loading occur by preferred partitioning of the calcine components among crystalline and glass phases. The determination of optimum processing parameters in the form of additive concentration levels, homogeneous blending among the components, and pressure-temperature stabilities of phases must be continued to eliminate undesirable effects of chemical composition, microstructure and glass devitrification

  6. Properties of hot pressed MgB2/Ti tapes

    International Nuclear Information System (INIS)

    Kovac, P.; Husek, I.; Melisek, T.; Fedor, J.; Cambel, V.; Morawski, A.; Kario, A.

    2009-01-01

    Hot axial and hot isostatic pressing was applied for single-core MgB 2 /Ti tapes. Differences in transport current density, n-exponents and critical current anisotropy are discussed and related to the grain connectivity influenced by pressing. The magnetic Hall probe scanning measurements allowed observing the isolated regions for axially hot pressed sample attributed to the longitudinally oriented cracks introduced by pressing. The highest current densities were measured for the tape subjected to hot isostatic pressing due to improved connectivity.

  7. A novel Fe–Cr–Nb matrix composite containing the TiB_2 neutron absorber synthesized by mechanical alloying and final hot isostatic pressing (HIP) in the Ti-tubing

    International Nuclear Information System (INIS)

    Litwa, Przemysław; Perkowski, Krzysztof; Zasada, Dariusz; Kobus, Izabela; Konopka, Gustaw; Czujko, Tomasz; Varin, Robert A.

    2016-01-01

    The Fe–Cr–Ti-Nb elemental powders were mechanically alloyed/ball milled with TiB_2 and a small quantity of Y_2O_3 ceramic to synthesize a novel Fe-based alloy-ceramic powder composite that could be processed by hot isostatic pressing (HIP) for a perceived potential application as a neutron absorber in nuclear reactors. After ball milling for the 30–80 h duration relatively uniform powders with micrometric sizes were produced. With increasing milling time a fraction of TiB_2 particles became covered with the much softer Fe-based alloy which resulted in the formation of a characteristic “core-mantel” structure. For the final HIP-ing process the mechanically alloyed powders were initially uniaxially pressed into rod-shaped compacts and then cold isostatically pressed (CIP-ed). Subsequently, the rod-shaped compacts were placed in the Ti-tubing and subjected to hot isostatic pressing (HIP) at 1150 °C/200 MPa pressure. The HIP-ing process resulted in the formation of the near-Ti and intermediate diffusional layers in the microstructure of HIP-ed samples which formed in accord with the Fe-Ti binary phase diagram. Those layers contain the phases such as α-Ti (HCP), the FeTi intermetallic and their hypo-eutectoid mixtures. In addition, needle-like particles were formed in both layers in accord with the Ti-B binary phase diagram. Nanohardness testing, using a Berkovich type diamond tip, shows that the nanohardness in the intermediate layer areas, corresponding to the composition of the hypo-eutectoid mixture of Ti-FeTi, equals 980.0 (±27.1) HV and correspondingly 1176.9 (±47.6) HV for the FeTi phase. The nanohardness in the sample's center in the areas with the fine mixture of Fe-based alloy and small TiB_2 particles equals 1048.3 (±201.8) HV. The average microhardness of samples HIP-ed from powders milled for 30 and 80 h is 588 HV and 733 HV, respectively. - Highlights: • A Fe–Cr–Nb-based composite with TiB_2 neutron absorbing ceramic was mechanically

  8. Thermal stability of the grain structure in the W-2V and W-2V-0.5Y2O3 alloys produced by hot isostatic pressing

    International Nuclear Information System (INIS)

    Martínez, J.; Savoini, B.; Monge, M.A.; Muñoz, A.; Armstrong, D.E.J.; Pareja, R.

    2013-01-01

    Highlights: • W-2V and ODS W-2V-0.5Y 2 O 3 alloys have been produced following a powder metallurgy route. • Grain microstructure and microhardness have been studied after isothermal treatments in vacuum. • Both alloys exhibit a duplex grain size population: a submicron-sized grain and a coarse grained one. • The Y 2 O 3 addition inhibits growth of the coarse grains for T 2 O 3 nanoparticles enhance the microhardness of W-2V-0.5Y 2 O 3 . -- Abstract: W-2V and ODS W-2V-0.5Y 2 O 3 alloys have been produced following a powder metallurgy route consisting of mechanical alloying and a subsequent high isostatic pressing HIP at 1573 K. The grain microstructure and microhardness recovery of the alloys have been studied in samples subjected to isothermal treatments in vacuum in temperature range 1073–1973 K. Both alloys exhibit a duplex grain size distribution consisting of a submicron-sized grain and a coarse-grained population. It has been found that the Y 2 O 3 addition inhibits growth of the coarse grains at T 2 O 3 , respectively, was observed at T ≥ 1573 K. It resulted that the rate constant for grain growth is 30 times higher in W-2V-0.5Y 2 O 3 than in W-2V. The considerable enhancement of the microhardness in the W-2V-0.5Y 2 O 3 appears to be associated to dispersion strengthening

  9. Treatment of zircaloy cladding hulls by isostatic pressing

    International Nuclear Information System (INIS)

    Tegman, R.; Burstroem, M.

    1984-12-01

    A method for the treatment of Zircaloy fuel hulls is proposed. It involves hot isostatic pressing (HIP) for making large, completely densified metallic bodies of the waste. The hulls are packed into a bellows-shaped container of steel. On packing the fuel hulls give a filling factor of only 14%, which is too low for non-deformable compaction in a normal container, but by using a belloped container, a non-deformable compaction can be obtained without any pretreatment of the hulls. Fully dense and mechanically strong blocks of Zircaloy can be fabricated by holding them at temperatures of around 1000 degrees C for three hours. It is also feasible to incorporate the other metallic parts of the fuel bundle, such as top and bottom tie plates and spacers, in the pressing. The HIP-densified hulls provide an effective means of self-containment of radioactive waste due to the excellent corrosion resistance of Zircaloy. A waste loading factor of close to 100% can be realized. Futher, a volume reduction factor of 7 and a surface reduction factor of aout 250 for a 1-ton canister can be achieved. Equilibrium calculations have shown that tritium present in the hulls can quantitatively be contained in the HIPed block. A study has been made of a possible process for industrilscale use. (Author)

  10. A novel Fe–Cr–Nb matrix composite containing the TiB{sub 2} neutron absorber synthesized by mechanical alloying and final hot isostatic pressing (HIP) in the Ti-tubing

    Energy Technology Data Exchange (ETDEWEB)

    Litwa, Przemysław [Department of Advanced Materials and Technologies, Military University of Technology, Kaliskiego 2, 00-908 Warsaw (Poland); Perkowski, Krzysztof [Department of Nanotechnology, Institute of Ceramics and Building Materials, Postępu 9, 02-676 Warsaw (Poland); Zasada, Dariusz [Department of Advanced Materials and Technologies, Military University of Technology, Kaliskiego 2, 00-908 Warsaw (Poland); Kobus, Izabela; Konopka, Gustaw [Department of Nanotechnology, Institute of Ceramics and Building Materials, Postępu 9, 02-676 Warsaw (Poland); Czujko, Tomasz [Department of Advanced Materials and Technologies, Military University of Technology, Kaliskiego 2, 00-908 Warsaw (Poland); Varin, Robert A., E-mail: robert.varin@uwaterloo.ca [Department of Mechanical and Mechatronics Engineering, University of Waterloo, 200 University Ave., Waterloo, ON N2L 3G1 (Canada)

    2016-07-25

    The Fe–Cr–Ti-Nb elemental powders were mechanically alloyed/ball milled with TiB{sub 2} and a small quantity of Y{sub 2}O{sub 3} ceramic to synthesize a novel Fe-based alloy-ceramic powder composite that could be processed by hot isostatic pressing (HIP) for a perceived potential application as a neutron absorber in nuclear reactors. After ball milling for the 30–80 h duration relatively uniform powders with micrometric sizes were produced. With increasing milling time a fraction of TiB{sub 2} particles became covered with the much softer Fe-based alloy which resulted in the formation of a characteristic “core-mantel” structure. For the final HIP-ing process the mechanically alloyed powders were initially uniaxially pressed into rod-shaped compacts and then cold isostatically pressed (CIP-ed). Subsequently, the rod-shaped compacts were placed in the Ti-tubing and subjected to hot isostatic pressing (HIP) at 1150 °C/200 MPa pressure. The HIP-ing process resulted in the formation of the near-Ti and intermediate diffusional layers in the microstructure of HIP-ed samples which formed in accord with the Fe-Ti binary phase diagram. Those layers contain the phases such as α-Ti (HCP), the FeTi intermetallic and their hypo-eutectoid mixtures. In addition, needle-like particles were formed in both layers in accord with the Ti-B binary phase diagram. Nanohardness testing, using a Berkovich type diamond tip, shows that the nanohardness in the intermediate layer areas, corresponding to the composition of the hypo-eutectoid mixture of Ti-FeTi, equals 980.0 (±27.1) HV and correspondingly 1176.9 (±47.6) HV for the FeTi phase. The nanohardness in the sample's center in the areas with the fine mixture of Fe-based alloy and small TiB{sub 2} particles equals 1048.3 (±201.8) HV. The average microhardness of samples HIP-ed from powders milled for 30 and 80 h is 588 HV and 733 HV, respectively. - Highlights: • A Fe–Cr–Nb-based composite with TiB{sub 2} neutron

  11. Progress in hot pressing

    International Nuclear Information System (INIS)

    Brodhag, C.; Thevenot, F.

    1988-01-01

    An experimental technique is described to study hot pressing of ceramics under conditions of controlled temperature and pressure during both the heating and final sintering stages. This method gives a better control of the final microstructure of the material. Transformation mechanisms can be studied during initial heating stage (impurity degasing, reaction, phase transformation, mechanical behavior of intergranular phase...) using computer control and graphical data representations. Some examples will be given for different systems studied in our laboratory: B (α, β, amorphous), B 12 O 2 (reaction of B + B 2 O 3 ), Si 3 N 4 ( + additives), TiN, Al 2 O 3 + AlON,ZrC

  12. Microstructure and Mechanical Properties of Long Ti-6Al-4V Rods Additively Manufactured by Selective Electron Beam Melting Out of a Deep Powder Bed and the Effect of Subsequent Hot Isostatic Pressing

    Science.gov (United States)

    Lu, S. L.; Tang, H. P.; Ning, Y. P.; Liu, N.; StJohn, D. H.; Qian, M.

    2015-09-01

    An array of eight long Ti-6Al-4V rods (diameter: 12 mm; height: 300 mm) have been additively manufactured, vertically and perpendicular to the powder bed, by selective electron beam melting (SEBM). The purpose was to identify and understand the challenges of fabricating Ti-6Al-4V samples or parts from a deep powder bed (more than 200-mm deep) by SEBM and the necessity of applying post heat treatment. The resulting microstructure and mechanical properties of these Ti-6Al-4V rods were characterized along their building ( i.e., axial) direction by dividing each rod into three segments (top, middle, and bottom), both before ( i.e., as-built) and after hot isostatic pressing (HIP). The as-built microstructure of each rod was inhomogeneous; it was coarsest in the top segment, which showed a near equilibrium α- β lamellar structure, and finest in the bottom segment, which featured a non-equilibrium mixed structure. The tensile properties varied along the rod axis, especially the ductility, but all tensile properties met the requirements specified by ASTM F3001-14. HIP increased the relative density from 99.03 pct of the theoretical density (TD) to 99.90 pct TD and homogenized the microstructure thereby leading to highly consistent tensile properties along the rod axis. The temperature of the stainless steel substrate used in the powder bed was monitored. The as-built inhomogeneous microstructure is attributed to the temperature gradient in the deep powder bed. Post heat treatment is thus necessary for Ti-6Al-4V samples or parts manufactured from a deep powder bed by SEBM. This differs from the additive manufacturing of small samples or parts from a shallow powder bed (less than 100-mm deep) by SEBM.

  13. Incineration ashes conditioning by isostatic pressing and melting

    International Nuclear Information System (INIS)

    Jouan, A.; Ouvrier, N.; Teulon, F.

    1990-01-01

    Alpha-bearing solid incineration wastes are conditioned for two principal reasons: to enhance the quality of the finished product for long-term storage, and to reduce the total waste volume. Isostatic pressing parameters were defined using containers 36 mm in diameter; the physicochemical properties of the compacted ashes were determined with 140 mm diameter containers and industrial feasibility was demonstrated with a large (300 mm diameter) container. Two types of ashes were used: ashes fabricated at Marcoule (either in devices developed by the CEA for the MELOX project with a standard MELOX composition, or by direct incineration at COGEMA's UP1 plant) and fly ash from a domestic waste incinerator. A major engineering study was also undertaken to compare the three known ash containment processes: isostatic pressing, melting, and cement-resin matrix embedding. The flowsheet, operational chronology and control principles were detailed for each process, and a typical plant layout was defined to allow comparisons of both investment and operating costs

  14. Hot-isostatic pressing (HIP). Pt. 2

    International Nuclear Information System (INIS)

    Bayer, E.; Moser, G.; Seilstorfer, H.

    1981-01-01

    After the description of the microstructure and strengthening mechanism of nickel- and cobalt-base superalloys, claims for the production of suitable powders for the HIP-technology are pointed out and methods to its realization are discussed. Taking the manufacture of turbine discs (ultrasonic form) as an example the possibilities of the near-net-shape-technology are shown. Investigations on mechanical properties and on microstructures are carried out to determine the effect of HIP-process-parameters on these features. (orig.) [de

  15. Hot-pressed geopolymer

    DEFF Research Database (Denmark)

    Ranjbar, Navid; Mehrali, Mohammad; Maheri, Mahmoud R.

    2017-01-01

    This research explores the use of simultaneous heating and pressing techniques in order to enhance the mechanical properties of fly ash (FA) based geopolymer under relatively low temperature conditions to ensure minimum-porosity. Four effective parameters of pressing force, alkali activator...

  16. Hot-pressing steatite bodies

    International Nuclear Information System (INIS)

    Aparicio Arroyo, E.

    1967-01-01

    Requirements for some special nuclear engineering ceramic shapes are: big size, impervious, dimensional accuracy and good mechanical and dielectric properties. Limitations of te conventional methods and advantages of te hot pressing techniques for the manufacturing of these shapes are discussed. Hot pressing characteristics of a certain steatite powder are studied. Occurrence of an optimum densification temperature just above the tale decomposition range is found. Experimental data show that the height/diameter ratio of the specimen has no effect on the sintering conditions. Increasing darkness from the graphite mould is detected above the optimum temperature. The hot-pressed steatite is compared with a fired dry-pressed sample of the same composition. (Author) 13 refs

  17. Factors influencing the creep strength of hot pressed beryllium

    International Nuclear Information System (INIS)

    Webster, D.; Crooks, D.D.

    1975-01-01

    The parameters controlling the creep strength of hot pressed beryllium block have been determined. Creep strength was improved by a high initial dislocation density, a coarse grain size, and a low impurity content. The impurities most detrimental to creep strength were found to be aluminum, magnesium, and silicon. A uniform distribution of BeO was found to give creep strength which was inferior to a grain boundary distribution. The creep strength of very high purity, hot isostatically pressed beryllium was found to compare favorably with that of other more commonly used high temperature metals

  18. Vacuum hot pressing of titanium-alloy powders

    International Nuclear Information System (INIS)

    Malik, R.K.

    1975-01-01

    Full or nearly full dense products of wrought-metal properties have been obtained by vacuum hot pressing (VHP) of several prealloyed Ti--6Al--4V powders including hydride, hydride/dehydride, and rotating electrode process (REP) spherical powder. The properties of billets VHP from Ti--6Al--4V hydride powder and from hydride/dehydride powders have been shown to be equivalent. The REP spherical powder billets processed by VHP or by hot isostatic pressing (HIP) resulted in equivalent tensile properties. The potential of VHP for fabrication of near net aircraft parts such as complex fittings and engine disks offers considerable cost savings due to reduced material and machining requirements

  19. A new hot pressing technique

    International Nuclear Information System (INIS)

    Carcey, J.

    1975-01-01

    An original hot pressing method which may be applied to ceramics, metals, and refractory powders is described. The products obtained are fine grained polycristalline materials, with homogeneous structure, very high density, unstrained and of very large dimensions (several square meters). This process equally applies to composite materials including powders, fibers, etc.. [fr

  20. Thermal stability of the grain structure in the W-2V and W-2V-0.5Y{sub 2}O{sub 3} alloys produced by hot isostatic pressing

    Energy Technology Data Exchange (ETDEWEB)

    Martínez, J.; Savoini, B.; Monge, M.A. [Departamento de Física, Universidad Carlos III de Madrid, 28911-Leganés Madrid (Spain); Muñoz, A., E-mail: angel.munoz@uc3m.es [Departamento de Física, Universidad Carlos III de Madrid, 28911-Leganés Madrid (Spain); Armstrong, D.E.J. [Department of Materials, University of Oxford, Park Road, Oxford OX1 3PH (United Kingdom); Pareja, R. [Departamento de Física, Universidad Carlos III de Madrid, 28911-Leganés Madrid (Spain)

    2013-10-15

    Highlights: • W-2V and ODS W-2V-0.5Y{sub 2}O{sub 3} alloys have been produced following a powder metallurgy route. • Grain microstructure and microhardness have been studied after isothermal treatments in vacuum. • Both alloys exhibit a duplex grain size population: a submicron-sized grain and a coarse grained one. • The Y{sub 2}O{sub 3} addition inhibits growth of the coarse grains for T < 1973 K. • The Y{sub 2}O{sub 3} nanoparticles enhance the microhardness of W-2V-0.5Y{sub 2}O{sub 3}. -- Abstract: W-2V and ODS W-2V-0.5Y{sub 2}O{sub 3} alloys have been produced following a powder metallurgy route consisting of mechanical alloying and a subsequent high isostatic pressing HIP at 1573 K. The grain microstructure and microhardness recovery of the alloys have been studied in samples subjected to isothermal treatments in vacuum in temperature range 1073–1973 K. Both alloys exhibit a duplex grain size distribution consisting of a submicron-sized grain and a coarse-grained population. It has been found that the Y{sub 2}O{sub 3} addition inhibits growth of the coarse grains at T < 1973 K. Submicron grain growth, with activation enthalpy of 1.9 and 2.49 eV for W-2V and W-2V-0.5Y{sub 2}O{sub 3}, respectively, was observed at T ≥ 1573 K. It resulted that the rate constant for grain growth is 30 times higher in W-2V-0.5Y{sub 2}O{sub 3} than in W-2V. The considerable enhancement of the microhardness in the W-2V-0.5Y{sub 2}O{sub 3} appears to be associated to dispersion strengthening.

  1. Microplasticity in hot-pressed beryllium

    International Nuclear Information System (INIS)

    Plane, D.C.; Bonfield, W.

    1977-01-01

    Closed hysteresis loops measured in the microstrain region of hot pressed, commercially pure, polycrystalline beryllium are correlated with a dislocation - impurity atom, energy dissipating mechanism. (author)

  2. Structure and hardness of TiAl-TiB2 composite prepared by hot isostatic pressing of mechanically alloyed powders. Mekanikaru aroingu funmatsu no HIP shoketsu ni yori sakuseishita TiAl/TiB2 fukugo zairyo no soshiki to kodo

    Energy Technology Data Exchange (ETDEWEB)

    Sato, T; Shimakage, K [Muroran Inst. of Technology, Hokkaido (Japan). Faculty of Engineering; Miyakawa, S [Muroran Inst. of Technology, Hokkaido (Japan). Graduate Student

    1992-11-20

    The practical application of Ti-Al system intermetallic compounds is expected as an advanced light heat resistant material. TiAl group out of them, as for the specific strength, has an equivalent maximum working temperature as that of the nickel base alloy, which is utilized as a turbine material for the current aircraft, and moreover it is also said that it is superior in the creep and rupture properties to the latter. In this study, by mechanical alloying (MA) of each mixed powder of Ti-Al and Ti-B, by suing heptane as a grinding aid, each MA powder of the amorphous TiAl containing carbon and extremely fine compound TiB2 were prepared, and subsequently the true density sintering by the hot isostatic pressing (HIP) was performed, and by doing these, the preparation of TiAl/TiB2 system composite material with a high composite ratio of TiO2 was tried. Consequently, by the MA treatment of the mixed powder of Ti and B for more than 50 hours, the compound powder of TiB2 mixed with TiB could be prepared, and its hardness has shown the maximum value Hmv=l200 with a composition of TiAl/25 mol % TiB2. 14 refs., 10 figs., 2 tabs.

  3. Preparation of amorphous-crystalline SiO{sub 2} composite by hot isostatic pressing (HIP). 2; HIP ho ni yoru SiO{sub 2} kei hishoshitsu-kesshoshitsu fukugo zairyo no sakusei. 2

    Energy Technology Data Exchange (ETDEWEB)

    Ito, S.; Nishii, J.; Fujii, T.; Akashi, K. [Science University of Tokyo, Tokyo (Japan). Faculty of Science and Tecnology

    2000-08-15

    The composites consisting of {alpha}-quartz crystallites and amorphous SiO{sub 2} were prepared by HIP technique, imitating the structure of natural agate. In the previous study, the K{sub IC} of the composite prepared from the mixed powder of crystallites and amorphous SiO{sub 2} was comparable to that of the natural agate (0.56MN/m{sup 1.5}). In this study, to increase the toughness of the composite, (1) the mixture of silica sol and {alpha}-quartz powder and (2) silica sol including nucleation promoter were examined as starting materials respectively. These starting materials were pressed into powder compacts with {phi} 10 multiplied 50mm in size. The Pyrex glass capsule containing the compact was hipped at 800-1,200 degrees C for 0-120 minutes under the pressure of 200 MPa. The K{sub IC} of the composite obtained from the mixture of silica sol and {alpha}-quartz powder was equivalent to that obtained in the previous study, while the maximum K{sub IC} (0.63 MN/m{sup 1.5}) was obtained when PbCl{sub 2} was used as a nucleation promoter. The nucleation promoter having low solubility in water was useful for the homogeneous generation of the crystallites. (author)

  4. Results of intermediate-scale hot isostatic press can experiments

    International Nuclear Information System (INIS)

    Nelson, L.O.; Vinjamuri, K.

    1995-05-01

    Radioactive high-level waste (HLW) has been managed at the Idaho Chemical Processing Plant (ICPP) for a number of years. Since 1963, liquid HLW has been solidified into a granular solid (calcine). Presently, over 3,800 m 3 of calcine is stored in partially-underground stainless steel bins. Four intermediate- scale HLW can tests (two 6-in OD x 12-in tall and two 4-in OD x 7-in tall) are described and compared to small-scale HIP can tests (1- to 3-in OD x 1- to 4.5-in tall). The intermediate-scale HIP cans were loaded with a 70/30 calcine/frit blend and HIPped at an off-site facility at 1050 degrees C; and 20 ksi. The dimensions of two cans (4-in OD x 7-in tall) were monitored during the HIP cycle with eddy-current sensors. The sensor measurements indicated that can deformation occurs rapidly at 700 degrees C; after which, there is little additional can shrinkage. HIP cans were subjected to a number of analyses including calculation of the overall packing efficiency (56 to 59%), measurement of glass-ceramic (3.0 to 3.2 g/cc), 14-day MCC-1 leach testing (total mass loss rates 2 day), and scanning electron microscopy (SEM). Based on these analyses, the glass-ceramic material produced in intermediate-scale cans is similar to material produced in small-scale cans. No major scale-up problems were indicated. Based on the packing efficiency observed in intermediate- and small-scale tests, the overall packing efficiency of production-scale (24-in OD x 36- to 190-in tall) cans would be approximately 64% for a pre-HIP right-circular cylinder geometry. An efficiency of 64% would represent a volume reduction factor of 2.5 over a candidate glass waste prepared at 33 wt% waste loading

  5. Development of Hot Isostatically Pressed Rene 95 Turbine Parts

    Science.gov (United States)

    1977-05-01

    Jull 17 ,. " 1ENE’ 95 TURBINE PARTS~ 7. AUTHOR(e) CO(A RRNNME P.)Mathur aWJ. Bartos AJ-3C0V hae1 9. PERFORMING ORGANIZATION NAME AND ADDRESS 10. PROGRAM...200 mesh coff .,acts prepared in the autoclave at 20500F and the -60 mesh compact prepared by *1650 0F14 hours, 2000°1/1 hour/OQ, + 1400°F/16 hours/AC...Product Acceptance plans (Appendix- Ill); the Quality Control of General Elctric Company was-extended to establish procedures and- organization , to

  6. Ceramic containers for spent nuclear fuel. II. Reactions between TiO2 and the steel canning during hot isostatic processing

    International Nuclear Information System (INIS)

    Bergman, B.; Forberg, S.

    1984-01-01

    Rutile was selected for some practical studies of processing and properties of ceramic containers. Hot isostatic pressing at 1280 0 C has resulted in reaction zones between the TiO 2 powder and the steel canning. The phases ilmenite, pseudobrookite, rutile, and iron have been identified by x-ray diffraction and by microprobe analysis. The microstructures have been interpreted by classical metallographic methods, and some microstructures obtained by hot pressing and rapid cooling have also been examined for purposes of comparison. Some implications of the microstructures have been discussed in terms of microcracking and slow crack growth. 13 refs., 7 figs

  7. Processing of surrogate nuclear fuel pellets for better dimensional control with dry bag isostatic pressing

    Energy Technology Data Exchange (ETDEWEB)

    Hoggan, Rita E., E-mail: Rita.hoggan@inl.gov; Zuck, Larry D., E-mail: Larry.zuck@inl.gov; Cannon, W. Roger, E-mail: cannon@rutgers.edu; Lessing, Paul A., E-mail: p.a.l.2@hotmail.com

    2016-12-15

    A study of improved methods of processing fuel pellets was undertaken using ceria and zirconia/yttria/alumina as surrogates. Through proper granulation, elimination of fines and vertical vibration (tapping) of the parts bag prior to dry bag isostatic pressing (DBIP), reproducibility of diameter profiles among multiple pellets of ceria was improved by almost an order of magnitude. Reproducibility of sintered pellets in these studies was sufficient to allow pellets to be introduced into the cladding with a gap between the pellet and cladding on the order of 50 μm to 100 μm but not a uniform gap with tolerance of ±12 μm as is currently required. Deviation from the mean diameter along the length of multiple pellets, and deviation from roundness, decreased after sintering. This is not generally observed with dry pressed pellets. Sintered shrinkage was uniform to ±0.05% and thus, as an alternative, pellets may be machined to tolerance before sintering, thus avoiding the waste associated with post-sinter grinding. - Highlights: • Three methods of granule preparation for two different powder sources were outlined and compared using tap density curves. • A dry bag isostatic press was used to fabricate pellets and longer rods. Thus longer pellets could be fabricated by this technique. • Vertical vibrations to pack granules decreased variation in dimensions from pellet to pellet by a factor of nine. • Sintering shrinkage varied by only 0.1% along the length of a rod. Thus green machining prior to sintering could result in tight tolerances.

  8. Nd:YAG transparent ceramics fabricated by direct cold isostatic pressing and vacuum sintering

    Science.gov (United States)

    Ge, Lin; Li, Jiang; Zhou, Zhiwei; Liu, Binglong; Xie, Tengfei; Liu, Jing; Kou, Huamin; Shi, Yun; Pan, Yubai; Guo, Jingkun

    2015-12-01

    The sintering behavior of neodymium doped yttrium aluminum garnet (Nd:YAG) ceramics was investigated on the basis of densification trajectory, microstructure evolution and transmittance. Nd:YAG ceramics with in-line transmittance of 83.9% at 1064 nm and 82.5% at 400 nm were obtained by direct cold isostatic pressing (CIP) at 250 MPa and solid-state reactive sintering at 1790 °C for 30 h under vacuum. Compared with the porosity and the average pore diameter of the sample from uniaxial dry-pressing followed by CIP, those from direct CIP are much smaller. The samples pressed at 250 MPa were sintered from 1500 °C to 1750 °C for 0.5-20 h to study their sintering behavior. At the temperature higher than 1500 °C, pure YAG phase is formed, followed by the densification and grain growth process. The relative density and the grain size increase with the increase of sintering time and temperature, and the sintering behavior is more sensitive to temperature than holding time. The mechanism controlling densification and grain growth at sintering temperature of 1550 °C is grain boundary diffusion.

  9. Method for hot pressing beryllium oxide articles

    Science.gov (United States)

    Ballard, Ambrose H.; Godfrey, Jr., Thomas G.; Mowery, Erb H.

    1988-01-01

    The hot pressing of beryllium oxide powder into high density compacts with little or no density gradients is achieved by employing a homogeneous blend of beryllium oxide powder with a lithium oxide sintering agent. The lithium oxide sintering agent is uniformly dispersed throughout the beryllium oxide powder by mixing lithium hydroxide in an aqueous solution with beryllium oxide powder. The lithium hydroxide is converted in situ to lithium carbonate by contacting or flooding the beryllium oxide-lithium hydroxide blend with a stream of carbon dioxide. The lithium carbonate is converted to lithium oxide while remaining fixed to the beryllium oxide particles during the hot pressing step to assure uniform density throughout the compact.

  10. ACTIVATED HOT PRESSING BEHAVIOR OF WC NANOPOWDERS

    Directory of Open Access Journals (Sweden)

    Edwin GEVORKYAN

    2010-06-01

    Full Text Available The questions of consolidation of nanopowders concerning hot compaction by pressing activated by electric current action are considered. Mechanisms of grain boundary creep-sliding which are sequentially prevalent in a forming of compacted structures under influence of temperature factor and in the presence of a direct electric heating are discussed. Structural-transformational sources and conditions of forming of high physical-mechanical properties of nanopowder refractory solid-state products are described.

  11. Behaviour and damage of a superalloy prepared by hot isostatic compression

    International Nuclear Information System (INIS)

    Dubiez-Le-Goff, Sophie

    2003-01-01

    This work deals with the behavior and damage of Udimet 720 superalloy prepared by hot isostatic compression. This alloy is considered for manufacturing turbine disks of high temperature reactors (HTR). The material choice for HTR turbine disk depends on the following criteria: a good creep resistance until 700 C, a good behaviour under an helium impure atmosphere, a possible implementation under a disk of 1.5 m diameter. (author) [fr

  12. Influence of cold isostatic pressing on the magnetic properties of Ni-Zn-Cu ferrite

    Science.gov (United States)

    Le, Trong Trung; Valdez-Nava, Zarel; Lebey, Thierry; Mazaleyrat, Frédéric

    2018-04-01

    In power electronics, there is the need to develop solutions to increase the power density of converters. Interleaved multicellular transformers allow interleaving many switching cells and, as a result, a possible increase in the power density. This converter is often composed of a magnetic core having the function of an intercell transformer (ICT) and, depending on the complexity of the designed architecture, its shape could be extremely complex. The switching frequencies (1-10 MHz) for the new wide band gap semiconductors (SiC, GaN) allow to interleave switching cell at higher frequencies than silicon-based semiconductors (materials, but their limit in frequency drive raises the need of higher frequency magnetic materials, such Ni-Zn ferrites. These materials can operate in medium and high power converters up to 10 MHz. We propose to use Ni0,30Zn0,57Cu0,15Fe2O4 ferrite and to compress it by cold isostatic pressing (CIP) into a a green ceramic block and to machine it to obtain the desired ICT of complex shape prior sintering. We compare the magnetic permeability spectra and hysteresis loops the CIP and uniaxially pressed ferrites. The effect of temperature and sintering time as well as high-pressure on properties will be presented in detail. The magnetic properties of the sintered cores are strongly dependent on the microstructure obtained.

  13. Effect of hot pressing additives on the leachability of hot pressed sodium hydrous titanium oxide

    International Nuclear Information System (INIS)

    Valentine, T.M.; Sambell, R.A.J.

    1980-01-01

    Sodium hydrous titanium oxide is an ion exchange resin which can be used for immobilizing medium level waste (MLW) liquors. When hot pressed, it undergoes conversion to a ceramic. Three low melting point materials (borax, bismuth trioxide, and a mixture of PbO/CuO) were added to the (Na)HTiO and the effect that each of these had on aiding densification was assessed. Hot pressing temperature, applied pressure, and percentage addition of hot pressing aid were varied. Percentage open porosity, flexural strength, and leachability were measured. There was a linear relationship between the percentage open porosity and the logarithm of the leach rate for a constant percentage addition of each additive

  14. Pressure slip casting and cold isostatic pressing of aluminum titanate green ceramics: A comparative evaluation

    Directory of Open Access Journals (Sweden)

    Ramanathan Papitha

    2013-12-01

    Full Text Available Aluminum titanate (Al2TiO5 green bodies were prepared from mixture of titania and alumina powders with different particle sizes by conventional slip casting (CSC, pressure slip casting (PSC and cold isostatic pressing (CIP. Precursor-powder mixtures were evaluated with respect to the powder properties, flow behaviours and shaping parameters. Green densities were measured and correlated with the fractographs. A substantial increase in green densities up to 60 %TD (theoretical density of 4.02 g/cm3, calculated based on rule of mixtures is observed with the application of 2–3 MPa pressure with PSC. While particle size distribution and solid loading are the most influential parameters in the case of CSC, with PSC pressure also plays a key role in achieving the higher green densities. Being a dry process, high pressure of > 100 MPa for CIP is essential to achieve densities in the range of 60–65 %TD. Slip pressurization under PSC conditions facilitate the rearrangement of particles through rolling, twisting and interlocking unlike CIP processing where pressure is needed to overcome the inter-particle friction.

  15. Influence of cold isostatic pressing on the magnetic properties of Ni-Zn-Cu ferrite

    Directory of Open Access Journals (Sweden)

    Trong Trung Le

    2018-04-01

    Full Text Available In power electronics, there is the need to develop solutions to increase the power density of converters. Interleaved multicellular transformers allow interleaving many switching cells and, as a result, a possible increase in the power density. This converter is often composed of a magnetic core having the function of an intercell transformer (ICT and, depending on the complexity of the designed architecture, its shape could be extremely complex. The switching frequencies (1-10 MHz for the new wide band gap semiconductors (SiC, GaN allow to interleave switching cell at higher frequencies than silicon-based semiconductors (<1 MHz. Intercell transformers must follow this increase in frequency times-fold the number of switching cells. Current applications for ICT transformers use Mn-Zn based materials, but their limit in frequency drive raises the need of higher frequency magnetic materials, such Ni-Zn ferrites. These materials can operate in medium and high power converters up to 10 MHz. We propose to use Ni0,30Zn0,57Cu0,15Fe2O4 ferrite and to compress it by cold isostatic pressing (CIP into a a green ceramic block and to machine it to obtain the desired ICT of complex shape prior sintering. We compare the magnetic permeability spectra and hysteresis loops the CIP and uniaxially pressed ferrites. The effect of temperature and sintering time as well as high-pressure on properties will be presented in detail. The magnetic properties of the sintered cores are strongly dependent on the microstructure obtained.

  16. Strength-ductility relationships in intermediate purity hot-pressed beryllium

    International Nuclear Information System (INIS)

    Stonehouse, A.J.; Bielawski, C.A.; Paine, R.M.

    1977-01-01

    The strength of vacuum hot-pressed, intermediate purity beryllium may be substantially increased without sacrifice of the strain capacity of the present grade (S-65) through decrease in the average grain size. Tensile strength of 517 MPa, 0.2% offset yield strength of 414 MPa with minimum 3% tensile elongation in all test directions could be commercially achieved. The tangent modulus of such material is quite attractive and suffers only about 10% degradation from room temperature to 260 0 C. The tangent modulus is dramatically enhanced by the presence of a yield point. The ductility of the materials studied did not appear to be affected by the BeO content across the range of 0.5 to 2.0% using nominal -44 to -15 μm powder particle sizes. All fine-grained pressings exhibited yield points in the as-pressed condition. Either full-density or sub-density hot-pressed billets given a hot isostatic pressing treatment without the use of cans showed only slight yield points after the HIP treatment with essentially the same strength and ductility factors as in the pressed condition. A plot of grain size vs yield strength in the as-pressed condition projects to an intercept with the fracture strength line at about 3 μm grain size. A similar plot after the HIP treatment shows a yield strength line parallel to the fracture strength line with no projected intercept predicting a completely brittle material. (author)

  17. Hot pressing of B4C/SiC composites

    International Nuclear Information System (INIS)

    Sahin, F.C.; Turhan, E.; Yesilcubuk, S.A.; Addemir, O.

    2005-01-01

    B 4 C/SiC ceramic composites containing 10-20-30 vol % SiC were prepared by hot pressing method. The effect of SiC addition and hot pressing temperature on sintering behaviour and mechanical properties of hot pressed composites were investigated. Microstructures of hot pressed samples were examined by SEM technique. Three different temperatures (2100 deg. C, 2200 deg. C and 2250 deg. C) were used to optimize hot pressing temperature applying 100 MPa pressure under argon atmosphere during the sintering procedure. The highest relative density of 98.44 % was obtained by hot pressing at 2250 deg. C. However, bending strengths of B 4 C/SiC composite samples were lower than monolithic B 4 C in all experimental conditions. (authors)

  18. High density high-TC ceramic superconductors by hot pressing

    International Nuclear Information System (INIS)

    Mak, S.; Chaklader, A.C.D.

    1989-01-01

    High density and high T C superconductor specimens, YBa 2 Cu 3 O x , have been produced by hot-pressing. The factors studied are the effect of hot pressing on the density, the oxygen stoichiometry, the crystal structure, and the critical temperature. Hot pressing followed by heat treatment increased the density of the specimen to 93%. The hot pressing itself did not significantly affect the oxygen content in the specimen, and although the crystal structure appeared to be orthorhombic, the specimens were not superconducting above liquid nitrogen temperature. The superconductivity was restored after head treatment in oxygen. The highest critical temperature (T C ) of the hot pressed pellets was 82K, which was slightly lower than the T C that could be obtained with the cold pressed/sintered pellets. (6 refs., 5 figs., tab.)

  19. Fabrication and properties of hot pressed bismuth tungstate

    International Nuclear Information System (INIS)

    Streicher, W.L.

    1978-01-01

    Bi 2 WO 6 is a synthetic polar material that is a possible candidate for energy conversion and detection systems. Previous research on this material has been concerned with crystal growth and sintering characteristics of polycrystalline compacts. This study involves itself with the fabrication of polycrystalline compacts by hot pressing techniques. Densities approaching theoretical crystal density were achieved by hot pressing at 850 0 C for one hour with pressures exceeding 35 MPa. Before hot pressing, the sintering range was determined by high temperature dilatometry of unfired Bi 2 WO 6 ceramics. Hot pressed discs were characterized by scanning electron microscopy, differential scanning calorimetry, and x-ray diffraction. Electrical properties were determined by dc resistivity, capacitance, and conductance measurements, ac poling, dc poling, and current-voltage measurements

  20. Dynamic Multiaxial Response of a Hot-Pressed Aluminum Nitride

    Science.gov (United States)

    2012-01-05

    Hutchinson, Adv. Appl . Mech. 29 (1992). [34] H. Ming-Yuan, J.W. Hutchinson, Int. J. Solids Struct. 25 (1989) 1053. [35] J. Salem , L. Ghosn, Int. J...Dynamic Multiaxial Response of a Hot- Pressed Aluminum Nitride by Guangli Hu, C. Q. Chen, K. T. Ramesh, and J. W. McCauley ARL-RP-0487...Laboratory Aberdeen Proving Ground, MD 21005-5066 ARL-RP-0487 June 2014 Dynamic Multiaxial Response of a Hot- Pressed Aluminum Nitride

  1. Role of aging time on the magnetic properties of Sm2Co17 permanent magnets processed through cold isostatic pressing

    Science.gov (United States)

    Ramudu, M.; Rajkumar, D. M.

    2018-04-01

    The effect of aging time on the magnetic properties of Sm2Co17 permanent magnets processed through a novel method of cold isostatic pressing was investigated. Sintered Sm2Co17 samples were subjected to different aging times in the range of 10-30 h and their respective microstructures were correlated with the magnetic properties obtained. The values of remanant magnetization (Br) were observed to be constant in samples aged from 10-20 h beyond which a gradual decrease in Br values was observed. The values of coercivity (Hc) displayed a sharp increase in samples aged from 10 to 20 h beyond which the coercivity values showed marginal improvement. Hence a good combination of magnetic properties could be achieved in samples aged for 20 h. A maximum energy product of 27 MGOe was achieved in the 20 h aged sample processed through a novel route.

  2. Study of the mechanical properties of stainless steel 316LN prepared by hot isostatic compression. Influence of preparation parameters

    International Nuclear Information System (INIS)

    Couturier, Raphael

    1999-01-01

    This research thesis has been performed within an R and D programme which aimed at optimising and certifying the HIP process (hot isostatic pressing) from a technological as well as metallurgical point of view. The objective has been to improve dimensional reproducibility of fabricated parts, and metallurgical properties of the dense material. Reference parts are those belonging to PWR primary circuit, and are made in cast austenitic-ferritic steel. Thus, the objective has been to show that these parts can be beneficially fabricated by powder metallurgy in austenitic grade. A mock part (a primary circuit pump wheel at the 1/2 scale) has first been fabricated by HIP, and a more complex shape generator has been designed. The author reports the determination of microstructure and mechanical characteristics of the austenitic 316LN steel produced by HIP and used to fabricate mock parts and demonstrator parts, the study of the relationship between dense material properties and fabrication parameters (temperature, pressure, consolidation time), and the analysis of the consequences of an elaboration by HIP on the 316LN steel with comparison with forged parts. After a presentation of the Powder Metallurgy elaboration technique, the author reports a bibliographical study on the precipitation at Prior Particle Boundaries (PPB), reports the study of microstructure and mechanical properties of the HIPed 316LN, and discusses the possibility of a decrease of precipitation at PPBs by adjusting powder degassing or a granulometric sorting. The last part reports the extension of the study of steel coherence to a temperature range which encompasses the primary circuit operation temperature (350 C). Resilience tests are performed as well as mechanical tests on notched axisymmetric samples. A finite element calculation of these samples allows the validation of the use of a Thomson-type model to describe the emergence of defects which are typical of a steel elaborated by powder

  3. Oxide formation and precipitation behaviors on interface of F82H steel joints during HIPing and hot pressing

    International Nuclear Information System (INIS)

    Kishimoto, H.; Ono, T.; Sakasegawa, H.; Tanigawa, H.; Ando, M.; Shibayama, T.; Kohno, Y.; Kohyama, A.

    2013-01-01

    Joining technologies for F82H steels are important issues for the development of fusion energy. The hot isostatic pressing (HIP) method is appropriate for consolidating the first wall of the blanket because of the flexibility of the shape of HIPed products. The HIP method is planned for fabricating a complex-shaped first wall component with built-in cooling channels; thus, accumulation of studies of microstructural and mechanical property changes, especially lower toughness of the HIPed joints, is essential. Present research aims to reveal the microstructural evolution of F82H joints fabricated by the HIP method compared with joints fabricated by hot pressing, focusing on the formation of oxides on the interface. F82H joints were characterized using 1/3-scale Charpy V-notch impact test, transmission electron microscope, scanning electron microscope, and electron probe analysis to survey the microstructural characteristics of the interface

  4. Process considerations for hot pressing ceramic nuclear waste forms

    International Nuclear Information System (INIS)

    Wilson, C.N.; Brite, D.W.

    1981-01-01

    Spray calcined simulated ceramic nuclear waste powders were hot pressed in graphite, nickel-lined graphite and ZrO 2 -lined Al 2 O 3 dies. Densification, initial off-gas, waste element retention and pellet-die interactions were evaluated. Indicated process considerations and limitations are discussed. 15 figures

  5. Nanoindentation hardness of hot-pressed boron suboxide

    International Nuclear Information System (INIS)

    Machaka, Ronald; Derry, Trevor E.; Sigalas, Iakovos

    2011-01-01

    Highlights: → The load-displacement indentation response of hot-pressed B 6 O is measured and analysed. → The nanoindentation hardness of hot-pressed boron suboxide is reported. → An approach is developed to simulate multi-cycling loading load-displacement curves. → A comprehensive model inter-comparison study of the ISE in hot-pressed B 6 O is also presented. → The fractal dimension is a better measure of ISE than the Meyer's index. - Abstract: The existence of the indentation size effect implies the absence of a single hardness value for the material under investigation especially at low applied loads. In this paper we present an investigation of the indentation size dependence behaviour of nanoindentation hardness in boron suboxide ceramic compacts prepared by uniaxial hot-pressing. Berkovich nanohardness indentations were conducted and analyzed accordingly. In addition to the ordinary Oliver and Pharr method of nanoindentation data analysis, a quantitative approach for the loading curve analysis is proposed. Using the proposed approach, the description and characterization of the observed indentation size effect through the application of the Meyer's law, and the classical and the modified proportional specimen resistance models as well as the multi-fractal scaling law was conducted and is reported. The load-independent hardness values deduced from our quantitative approach are comparable to the results calculated with conventional methods, especially with the multi-fractal scaling law.

  6. Nanoindentation hardness of hot-pressed boron suboxide

    Energy Technology Data Exchange (ETDEWEB)

    Machaka, Ronald, E-mail: Ronald.Machaka@wits.ac.za [DST/NRF Centre of Excellence in Strong Materials, University of the Witwatersrand, P. Bag 3, Wits, Johannesburg (South Africa); School of Chemical and Metallurgical Engineering, University of the Witwatersrand, P.O. Bag 3, Wits, Johannesburg 2050 (South Africa); Derry, Trevor E. [DST/NRF Centre of Excellence in Strong Materials, University of the Witwatersrand, P. Bag 3, Wits, Johannesburg (South Africa); School of Physics, University of the Witwatersrand, P.O. Bag 3, Wits, Johannesburg 2050 (South Africa); Sigalas, Iakovos [DST/NRF Centre of Excellence in Strong Materials, University of the Witwatersrand, P. Bag 3, Wits, Johannesburg (South Africa); School of Chemical and Metallurgical Engineering, University of the Witwatersrand, P.O. Bag 3, Wits, Johannesburg 2050 (South Africa)

    2011-07-15

    Highlights: {yields} The load-displacement indentation response of hot-pressed B{sub 6}O is measured and analysed. {yields} The nanoindentation hardness of hot-pressed boron suboxide is reported. {yields} An approach is developed to simulate multi-cycling loading load-displacement curves. {yields} A comprehensive model inter-comparison study of the ISE in hot-pressed B{sub 6}O is also presented. {yields} The fractal dimension is a better measure of ISE than the Meyer's index. - Abstract: The existence of the indentation size effect implies the absence of a single hardness value for the material under investigation especially at low applied loads. In this paper we present an investigation of the indentation size dependence behaviour of nanoindentation hardness in boron suboxide ceramic compacts prepared by uniaxial hot-pressing. Berkovich nanohardness indentations were conducted and analyzed accordingly. In addition to the ordinary Oliver and Pharr method of nanoindentation data analysis, a quantitative approach for the loading curve analysis is proposed. Using the proposed approach, the description and characterization of the observed indentation size effect through the application of the Meyer's law, and the classical and the modified proportional specimen resistance models as well as the multi-fractal scaling law was conducted and is reported. The load-independent hardness values deduced from our quantitative approach are comparable to the results calculated with conventional methods, especially with the multi-fractal scaling law.

  7. Fabrication of Y-TZP For Dental Crowns Applications by Combining Slip Casting and Cold Isostatic Pressing

    International Nuclear Information System (INIS)

    Hao, C.C.; Andanastuti Muchtar; Che Husna Azhari; Masfueh Razali; Mohamed Aboras

    2016-01-01

    Yttria-stabilized tetragonal zirconia polycrystalline (Y-TZP) is a popular material for dental restoration because of its outstanding mechanical properties and biocompatibility. Cold isostatic pressing (CIP) and slip casting are among several consolidation methods for Y-TZP. These methods produce Y-TZP with high mechanical properties. This study aims to enhance the mechanical properties of Y-TZP by combining slip casting and CIP. Y-TZP samples were fabricated using CIP, slip casting, and their combination. Subsequently, the green bodies of the samples were sintered at 1600 degree Celcius. Their mechanical properties (density and hardness) were tested and their microstructures were scrutinized under a scanning electron microscope. Compared with the other two methods, the combined method significantly improved the mechanical properties of Y-TZP. In addition, the combined method also produced a compact and homogeneous microstructure. Therefore, the combination of slip casting and CIP is recommended in the production of Y-TZP with high mechanical properties for dental crown applications. (author)

  8. Manufacturing of small scale W monoblock mockups by hot radial pressing

    International Nuclear Information System (INIS)

    Visca, Eliseo; Testani, C.; Libera, S.; Sacchetti, M.

    2003-01-01

    In the frame of the European Technology R and D programme for International thermonuclear experimental reactor (ITER) and in the area of high heat flux plasma facing components (HHFC), representative small-scale mock-ups were manufactured and tested to compare different concepts and joining technologies (i.e. active brazing, hot isostatic pressing (HIPping), diffusion bonding, etc.). On the basis of the results obtained by thermal fatigue tests, the monoblock concept resulted to be the most robust one, particularly when the HIPping manufacturing technology is used. Within this programme, ENEA developed an alternative technique for manufacturing plasma-facing components with a monoblock geometry of the ITER machine. The basic idea of this technique, named hot radial pressing (HRP), is to perform a radial diffusion bonding between the cooling tube and the armour tile by pressurising the internal tube only and by keeping the process parameters within the range in which the thermo-mechanical properties of the copper alloys are not yet degraded. The HRP is performed by a standard furnace, in which only a section of the canister is heated. The manufacturing procedure and the results of the screening and fatigue thermal tests performed on the ENEA mock-ups are reported in this paper

  9. Effects of internal gas pressure and microstructure on the mechanisms of hot-pressing and swelling in ceramics. Progress report, June 1, 1976--March 31, 1977

    International Nuclear Information System (INIS)

    Solomon, A.A.

    1977-02-01

    The low temperature isostatic pressurization system has been completed, operated successfully and calibrated. The new high temperature TD tungsten vessel and MoSi 2 element furnace system has also been designed and is presently under construction. Porous CoO single crystals have been grown using a ''skull melting'' process. Automated quantitative microscopy techniques are being developed using the KONTRON system to examine porosity evaluation during hot-pressing and sintering. Initial sintering experiments under variable isostatic pressures from 100 μm Hg to 2000 psi reveal no significant effect of ambient pressure. Nor were differences observed in sintering kinetics when either Helium or Argon were used as the pressurizing gas. Swelling experiments, conducted by reducing the ambient pressure after pore closure, revealed dramatic changes in density. The densification rates also appeared to depend on history, suggesting that mechanical deformation may play a dominant role in hot-pressing, at least during transients

  10. Method for hot pressing irregularly shaped refractory articles

    Science.gov (United States)

    Steinkamp, William E.; Ballard, Ambrose H.

    1982-01-01

    The present invention is directed to a method for hot pressing irregularly haped refractory articles with these articles of varying thickness being provided with high uniform density and dimensional accuracy. Two partially pressed compacts of the refractory material are placed in a die cavity between displaceable die punches having compact-contacting surfaces of the desired article configuration. A floating, rotatable block is disposed between the compacts. The displacement of the die punches towards one another causes the block to rotate about an axis normal to the direction of movement of the die punches to uniformly distribute the pressure loading upon the compacts for maintaining substantially equal volume displacement of the powder material during the hot pressing operation.

  11. Fundamental properties of monolithic bentonite buffer material formed by cold isostatic pressing for high-level radioactive waste repository

    International Nuclear Information System (INIS)

    Kawakami, S.; Yamanaka, Y.; Kato, K.; Asano, H.; Ueda, H.

    1999-01-01

    The methods of fabrication, handling, and emplacement of engineered barriers used in a deep geological repository for high level radioactive waste should be planned as simply as possible from the engineering and economic viewpoints. Therefore, a new concept of a monolithic buffer material around a waste package have been proposed instead of the conventional concept with the use of small blocks, which would decrease the cost for buffer material. The monolithic buffer material is composed of two parts of highly compacted bentonite, a cup type body and a cover. As the forming method of the monolithic buffer material, compaction by the cold isostatic pressing process (CIP) has been employed. In this study, monolithic bentonite bodies with the diameter of about 333 mm and the height of about 455 mm (corresponding to the approx. 1/5 scale for the Japanese reference concept) were made by the CIP of bentonite powder. The dry densities: ρd of the bodies as a whole were measured and the small samples were cut from several locations to investigate the density distribution. The swelling pressure and hydraulic conductivity as function of the monolithic body density for CIP-formed specimens were also measured. High density (ρd: 1.4--2.0 Mg/m 3 ) and homogeneous monolithic bodies were formed by the CIP. The measured results of the swelling pressure (3--15 MPa) and hydraulic conductivity (0.5--1.4 x 10 -13 m/s) of the specimens were almost the same as those for the uniaxial compacted bentonite in the literature. It is shown that the vacuum hoist system is an applicable handling method for emplacement of the monolithic bentonite

  12. Hot pressing, strength, and fracture of calcium hexaboride

    International Nuclear Information System (INIS)

    Dutta, S.K.

    1975-01-01

    Fracture behavior and strength of hot-pressed CaB 6 were studied. The modulus of elasticity determined by attaching strain gages to the tensile surface of the bend bars to measure strain, was 55 +- 3 x 10 6 psi. The results are compared with values for other low density ceramic materials (B 4 C, SiB 6 , Be 4 B, AlB 12 ) in a table. The fracture mode was observed for both modulus of rupture and impact test specimens. Predominantly transgranular fracture, associated with distinct step cleavages is evident. Fracture origins were examined in an effort to understand the strength limiting features in hot-pressed CaB 6 specimens. Surface defects, large grain agglomerations, and isolated pore pockets were observed and varied from bar to bar; these were similar to those found in B 4 C. (U.S.)

  13. Mechanical and thermophysical properties of hot-pressed SYNROC B

    International Nuclear Information System (INIS)

    Hoenig, C.L.; Newkirk, H.W.; Otto, R.A.; Brady, R.L.; Brown, A.E.; Ulrich, A.R.; Lum, R.C.

    1981-01-01

    The optimal SYNROC compositons for use with commercial waste are reviewed. Large amounts of powder (about 2.5 kg) were prepared by convention al ceramic operations to test the SYNROC concept on a processing scale. Samples, 15.2 cm in diameter, were hot pressed in graphite, and representative samples were cut for microstructural evaluations. Measured mechanical and thermophysical properties did not vary significantly as a function of sample location and were typical of titanate ceramic materials

  14. Graphite and boron carbide composites made by hot-pressing

    International Nuclear Information System (INIS)

    Miyazaki, K.; Hagio, T.; Kobayashi, K.

    1981-01-01

    Composites consisting of graphite and boron carbide were made by hot-pressing mixed powders of coke carbon and boron carbide. The change of relative density, mechanical strength and electrical resistivity of the composites and the X-ray parameters of coke carbon were investigated with increase of boron carbide content and hot-pressing temperature. From these experiments, it was found that boron carbide powder has a remarkable effect on sintering and graphitization of coke carbon powder above the hot-pressing temperature of 2000 0 C. At 2200 0 C, electrical resistivity of the composite and d(002) spacing of coke carbon once showed minimum values at about 5 to 10 wt% boron carbide and then increased. The strength of the composite increased with increase of boron carbide content. It was considered that some boron from boron carbide began to diffuse substitutionally into the graphite structure above 2000 0 C and densification and graphitization were promoted with the diffusion of boron. Improvements could be made to the mechanical strength, density, oxidation resistance and manufacturing methods by comparing with the properties and processes of conventional graphites. (author)

  15. Hot pressing of uranium nitride and mixed uranium plutonium nitride

    International Nuclear Information System (INIS)

    Chang, J.Y.

    1975-01-01

    The hot pressing characteristics of uranium nitride and mixed uranium plutonium nitride were studied. The utilization of computer programs together with the experimental technique developed in the present study may serve as a useful purpose of prediction and fabrication of advanced reactor fuel and other high temperature ceramic materials for the future. The densification of nitrides follow closely with a plastic flow theory expressed as: d rho/ dt = A/T(t) (1-rho) [1/1-(1-rho)/sup 2/3/ + B1n (1-rho)] The coefficients, A and B, were obtained from experiment and computer curve fitting. (8 figures) (U.S.)

  16. Preparation and microstructure of hot-pressed YIG

    International Nuclear Information System (INIS)

    Abdul Halim Shaari; Mansor Hashim; Sidek Haji Abd Aziz

    1992-01-01

    Bulk magnetic ceramics such as yttrium-iron-garnet (YIG) and nickel-zinc ferrite were prepared by the conventional-firing and hot-press techniques. Pre-sintering and sintering, both in air, were carried out at temperature ≥ 1200 0 C. Initial density and microstructural measurements show that the high density samples with uniform grain size can be readily achieved by hot-pressing. The well-defined microstructures, the high density attained. The agreement of saturation magnetization 4πMs values and the high resistivities indicated that the optimized preparation conditions for conventional firing yielded yttrium-iron-garnet of good quality. Quenched and isochronally annealed, the YIG samples were also found to retain their room-temperature saturation-magnetization and resonance linewidth values after any single heat treatment. However, the electrical resistivity and the effective linewidth clearly exhibited isochronal recovery. A possible model to explain this behaviour and its implications on microwave applications are discussed. Ferrites of the type MFe 2 O 4 where M=Mg, Mn, Co, Fe, Cu, Zn and Cd and of the type Ni1-2xSnxFe 2 O4 have also been prepared and their properties are being studied

  17. Beryllium window flange for synchrotron radiation X-ray beamline fabricated by hot isostatic press method

    International Nuclear Information System (INIS)

    Asaoka, Seiji; Maezawa, Hideki; Nishida, Kiyotoshi; Sakamoto, Naoki.

    1995-01-01

    The synchrotron radiation experimental facilities in National Laboratory for High Energy Physics are the experimental facilities for joint utilization, that possess the positron storage ring of 2.5 GeV exclusively used for synchrotron radiation. Synchrotron radiation is led through a mainstay beam channel to the laboratory, and in the beam line of X-ray, it is used for experiment through the taking-out window made of beryllium. At this time, the function of the taking-out window is to shut off between the ultrahigh vacuum in the mainstay beam channel and the atmosphere, and to cut the low energy component of synchrotron radiation spectra. The experiment using X-ray is carried out mostly in the atmosphere. The design of the efficient cooling water channel which is compatible with the flange construction is important under the high thermal load of synchrotron radiation. The beryllium window flange for synchrotron radiation X-ray was made by HIP method, and the ultrahigh vacuum test, the high pressure water flow test and the actual machine test were carried out by heat cycle. The properties required for the window material, the requirement of the construction, the new development of HIP method, and the experiments for evaluating the manufactured beryllium window are described. (K.I.)

  18. Hot isostatically pressed (HIPed) thick-walled component for a pressurised water reactor (PWR) application

    International Nuclear Information System (INIS)

    Hookham, I.; Burdett, B.; Bridger, K.; Sulley, J.L.

    2009-01-01

    This paper presents the work conducted to justify and provide a quality assured HIPed thick-walled component for a PWR application; the component being designed and manufactured by Rolls-Royce. Rolls-Royce has previously published (ICAPP 08) its overall, staged approach to the introduction of powder HIPed components; starting with thin-walled, leak limited pressure boundaries, and culminating in the use of the powder HIPed process for thick walled components. This paper presents details specific to a thick walled pressure vessel component. Results are presented of non-destructive and destructive examinations of one of a batch of components. Mechanical testing and metallurgical examination results of sample material taken from different sections of the component are presented. A full range of test results is provided covering, as examples: tensile, Charpy impact and sensitization susceptibility. Differences in weldability between the HIPed and the previous forged form are also documented. (author)

  19. Application of hot isostatic pressing to the manufacture of complex shaped moulds and tools

    International Nuclear Information System (INIS)

    Rigal, E.; Baccino, R.; Federzoni, L.; Moret, F.

    2000-01-01

    In this article, we briefly recall the physical mechanisms at the origin of the Barkhausen effect in ferromagnetic mediums and the thermoelectric power in conductor metals. We then present, for each of these phenomena, the measurement principles and their sensitivity to the microstructural state, notably in the case of precipitation phenomena and in the ones linked to plastic deformation. Finally, in the case of the formation of precipitates in an iron-based alloy, we show the complementarity of both techniques. (authors)

  20. Pengaruh Temperatur Pada Proses Hot Isostatic Pressing Terhadap Porositas, Keausan Dan Mikrostruktur Sludge Powder Duralumin

    OpenAIRE

    Multazam, Ahmad; Suprapto, Wahyono; Pratikto, Pratikto

    2014-01-01

    Sludge is the starting raw material in the process of forming wheels with forging method. Performance wheels strongly influenced by the quality of sludge. Sludge should have physical properties that light , soft and easy strengthened. One material that can be used as materials for sludge are: duralumin material. Duralumin is another name for aluminum & copper alloy (Al / Cu) with a Cu content of about 4 %. Making sludge powder duralumin with powder metallurgical methods can improve the qu...

  1. The feasibility of bonding aluminum alloy 6061 via hot isostatic pressing (HIP)/rolling

    International Nuclear Information System (INIS)

    Fenolietto, R.A.

    1991-01-01

    The advantage of developing a HIP bonding process for dispersion fuel plates is that applying a thin cladding in a more uniform manner could allow the upper limit for LEU U 3 Si-Al dispersion fuel plate densities to be overcome. Since much less mechanical deformation would be required, the existing process limitations on the density could be removed, theoretically allowing more fuel to be added. These increases are, of course, subject to irradiation behavior of the higher loadings which is not addressed in this paper. Initial results indicate that aluminum Alloy 6061 can be successfully bonded by seal welding via electron beam (EB), HIPping, and finishing with a limited amount of rolling. (orig.)

  2. Kinetics and mechanisms of creep in hot isostatically pressed niobium carbide

    International Nuclear Information System (INIS)

    Nixon, R.D.; Davis, R.F.; Bentley, J.

    1986-01-01

    Constant compressive stress creep experiments in the temperature and stress ranges of 1730K - 2100K and 16 MN/m 2 - 70 MM/m 2 on HIPed NbC 0.74 have revealed stress exponents of 2.0 under stress levels of 16-54 MN/m 2 at all temperatures investigated and 3.2 under stress levels of 54-70 MN/m 2 at 1830K. The activation energy of steady state creep is approximately 230 kJ/mol in the temperature range of 1730K - 1930K under 48-54 MN/m 2 and 470 kJ/mol in the temperature range of 1900K - 2100K under 64 MN/m 2 . TEM of the annealed but uncrept material reveals grown-in dislocation subboundaries. At 1730K and under 34-54 MN/m 2 , these subboundaries become single dislocations and dipoles. At 1830K and under 54-70 MN/m 2 the subboundaries evolve into simple tilt boundaries which are occasionally knitted, indicating more glide activity at higher stresses. At 1930K and under 34-54 MN/m 2 , hexagonal subboundaries form, but are not as well defined as in the annealed material. At 2100K and under 16-30 MN/m 2 , the subboundaries are well-defined hexagonal networks which become polygonized under higher stresses on 64 MN/m 2 . The experimental and TEM results indicate that at low temperatures (below 0.5 T m = 2073K) and at all stresses, creep occurs by dislocation glide which is accompanied by subgrain and high angle boundary interaction. At high temperature (above 0.5 T m ), strain occurs by glide and subboundary movement; recovery occurs by climb in the subboundary

  3. La2O3-reinforced W and W-V alloys produced by hot isostatic pressing

    International Nuclear Information System (INIS)

    Munoz, A.; Monge, M.A.; Savoini, B.; Rabanal, M.E.; Garces, G.; Pareja, R.

    2011-01-01

    W and W-V alloys reinforced with La 2 O 3 particles have been produced by MA and subsequent HIP at 1573 K and 195 MPa. The microstructure of the consolidated alloys has been characterized by scanning electron microscopy, energy dispersive spectroscopy analyses and X-ray diffraction. The mechanical properties were studied by nanoindentation measurements. The results show that practically full dense billets of W-V, W-V-La 2 O 3 and W-La 2 O 3 alloys can be produced. The microstructure analysis has shown that islands of V are present in W-V and W-V-1La 2 O 3 alloys. In W-1La 2 O 3 islands of La 2 O 3 are also present. The nanohardness of the W matrix increases with the addition of V, while decreases with the addition of La 2 O 3 .

  4. Influence of purity level on the mechanical properties of hot isostatically pressed beryllium

    International Nuclear Information System (INIS)

    Odegard, B.C. Jr.

    1979-09-01

    The procurement of a quantity of ultra-pure beryllium powder combined with special handling from powder to billet form resulted in the fabrication of high purity beryllium. The mechanical properties of these billets were contrasted to those of commercial grade billets to determine the influence of impurities and powder processing. The tensile test results show that the strength values are primarily dependent on the grain size in a behavior predictable by the Hall-Petch relationship. Only a fraction of the strength differential can be attributed to metallic impurities in solution. The grain size is controlled by the powder size distribution. The ductility is dominated by both grain size and oxide content. The fine grained, low oxide billets exhibited the highest ductilities. There is evidence to suggest that oxide distribution has a large influence on the ductility. The fracture toughness was highest for the high purity beryllium billets

  5. Fabrication of fully ceramic microencapsulated fuel by hot pressing

    International Nuclear Information System (INIS)

    Lee, H. G.; Kim, D. J; Park, J. Y.; Kim, W. J.; Lee, S. J

    2014-01-01

    Fully ceramic microencapsulated(FCM) nuclear fuel is one of the recently suggested concept to enhance stability nuclear fuel itself. The requirements to increase the accident tolerance of nuclear fuel are mainly two parts: First, the performance has to be maintained compared to the existing UO 2 nuclear fuel and zircaloy cladding system under the normal operation condition. Second, under the severe accident condition, the high temperature structural integrity has to be kept and the generation rate of hydrogen has to be decrease largely. FCM nuclear fuel consists of tristructural isotropic(TRISO) fuel particle and SiC matrix. The relative thermal conductivity of the SiC matrix as compared to UO 2 is quite good, yielding as-irradiated fuel centerline temperature compared to high temperature for the existing fuel leading to reduced stored energy in the core and reduced operational release of fission products from the fuel. Generally SiC ceramics are fabricated via liquid phase sintering due to strong covalent bonding property and low self-diffusivity coefficient. Hot pressing is very effective method to conduct sintering of SiC powder including different second phase. In this study, SiC-matrix composite including TRISO particles were sintered by hot pressing with Al 2 O 3 -Y 2 O 3 additive system. Various sintering condition were investigated to obtain high relative density above 95%. The internal distribution of TRISO particles within SiC-matrix composite was observed by x-ray radiograph. From the analysis of the cross-section of SiC-matrix composite, the fracture of TRISO particles was investigated. In order to uniform distribution of TRISO particle embedded in the SiC matrix, SiC powder overcoating is considered. SiC matrix composite including TRISO was fabricated by hot pressing. FCM pallets with full density were obtained with Al 2 O 3 -Y 2 O 3 additive system. From the microstructure image, the effect of the sintering additive contents and sintering mechanism

  6. Techniques for hot-press-bonding dissimilar metal combinations

    International Nuclear Information System (INIS)

    Watson, R.D.

    1966-05-01

    High strength diffusionless bonds can be produced in a variety of dissimilar metal combinations by the hot press bonding technique covered by Canadian Patent application 904,548 June 6, 1964. Some of the combinations that can be joined successfully are Zircaloy-2 and 416 stainless steel, 416 stainless steel and mild steel, 1S aluminum and mild steel, Zircaloy-2 and M257 SAP, and Zircaloy-2 and 1S aluminum. Several other combinations were attempted but suitable joints could not be produced. The methods of producing the joints, the joint strength that can be developed and a discussion of some of the problems associated with making the joints are included in the report. (author)

  7. A study of pressureless microwave sintering, microwave-assisted hot press sintering and conventional hot pressing on properties of aluminium/alumina nanocomposite

    Energy Technology Data Exchange (ETDEWEB)

    Abedinzadeh, Reza; Safavi, Seyed Mohsen; Karimzadeh, Fathallah [Isfahan University, Isfahan (Iran, Islamic Republic of)

    2016-05-15

    Bulk Al/4wt-%Al{sub 2}O{sub 3} nanocomposites were prepared by consolidating nanocomposite powders using pressureless microwave sintering, microwave-assisted hot press sintering and conventional hot pressing techniques. Microstructural observations revealed that the microwave-assisted hot press sintering at different sintering temperatures of 400.deg.C and 500.deg.C resulted in more densification and smaller grain size for Al/Al{sub 2}O{sub 3} nanocomposite as compared with the conventional hot pressing. Moreover, the application of pressure in microwave sintering process led to more densification and grain growth. Mechanical properties resulting from microhardness and nanoindentation tests were also compared between three-method processed samples. It was found that the microwave-assisted hot-pressed sample exhibited higher hardness and elastic modulus in comparison with microwave-sintered and conventional hot-pressed samples. The improvement in the mechanical properties can be ascribed to lower porosity of microwave-assisted hot-pressed sample.

  8. Hot pressing of B{sub 4}C/SiC composites

    Energy Technology Data Exchange (ETDEWEB)

    Sahin, F.C.; Turhan, E.; Yesilcubuk, S.A.; Addemir, O. [Ystanbul Technical University, Faculty of Chemistry and Metallurgy, Materials and Metallurgical Engineering Dept., Maslak-Ystanbul (Turkey)

    2005-07-01

    B{sub 4}C/SiC ceramic composites containing 10-20-30 vol % SiC were prepared by hot pressing method. The effect of SiC addition and hot pressing temperature on sintering behaviour and mechanical properties of hot pressed composites were investigated. Microstructures of hot pressed samples were examined by SEM technique. Three different temperatures (2100 deg. C, 2200 deg. C and 2250 deg. C) were used to optimize hot pressing temperature applying 100 MPa pressure under argon atmosphere during the sintering procedure. The highest relative density of 98.44 % was obtained by hot pressing at 2250 deg. C. However, bending strengths of B{sub 4}C/SiC composite samples were lower than monolithic B{sub 4}C in all experimental conditions. (authors)

  9. Improvement of nuclear reactor component materials by application of hot isostatic processing (HIP). Survey report on Phase 1

    International Nuclear Information System (INIS)

    Mueller, J.J.

    1975-12-01

    The report summarizes the results of an EPRI-sponsored state-of-the-art survey of hot isostatic processing (HIP). The purpose of the study was to identify potential nuclear plant applications of HIP with high pay-off through improvement in component quality and reliability. The survey shows that HIP will reduce cost and manufacturing time and improve quality and ease of nondestructive examination of all castings for which porosity is a problem. Nuclear valves are a prime example. Tubing, pipe, and sheet and bar present other possibilities of somewhat less immediate promise. This report includes a review of some of the EPRI motivations for undertaking this research; a brief explanation of HIP, the survey methodology exployed; the basic operations in the processes studied; a review of the historical applications of HIP to problem areas consistent with those addressed in the survey; the results of the survey and associated analyses of the problems; and the recommendations and justifications for the Phase II program

  10. Brine migration in hot-pressed polycrystalline sodium chloride

    International Nuclear Information System (INIS)

    Biggers, J.V.; Dayton, G.O.

    1982-12-01

    This report describes experiments designed to provide data on brine migration in polycrystalline salt. Polycrystalling samples of various grain sizes, density, and purity were prepared from several commercial-grade salts by hot-pressing. Three distinct experimental set-ups were used to place salt billets in an induced thermal gradient in contact with brine source. The test designs varied primarily in the way in which the thermal gradient was applied and monitored and the way in which brine migration was determined. All migration was in enclosed vessels which precluded visual observation of brine movement through the microstructure. Migration velocities were estimated either by the timed appearance of brine at the hot face of the sample, or by determination of the penetration distance of migration artifacts in the microstructure after tests of fixed duration. For various reasons both of these methods were subject to a large degree of error. Our results suggest, however, that the migration velocity in dense polycrystalline salt may be at least an order of magnitude greater than that suggested by single-crystal experiments. Microstructural analysis shows that brine prefers to migrate along paths of high crystalline activity such as grain and subgrain boundaries and is dispersed rather quickly in the microstructure. A series of tests were performed using various types of tracers in brine in order to flag migration paths and locate brine in the microstructure more decisively. These attempts failed and it appears that only the aqueous portion of the brine moves through the microstructure with the dissolved ions being lost and replaced rather quickly. This suggests the use of deuterium as a tracer in future work

  11. Effect of Fe on the phases and microstructure of TiC-Fe cermets by combustion synthesis/quasi-isostatic pressing

    International Nuclear Information System (INIS)

    Zhang Weifang; Zhang Xinghong; Wang Jianli; Hong Changqing

    2004-01-01

    Fully dense TiC-Fe cermets (x = 10, 20, 30, and 40 wt.%) were produced from Ti-C-Fe powder mixtures by combustion synthesis with quasi-isostatic pressing. The effect of Fe content on combustion temperature, combustion wave velocity, and final product density was investigated. The final product was characterized by XRD, SEM, and TEM. The combustion temperature and wave velocity decreased with increasing Fe content. Product density increased with increasing Fe content (96% at 30 wt.%). X-ray diffraction and transmission electron microscopy (TEM) revealed the final product to contain TiC, Fe phases, lath martensite, and Fe 2 Ti. The TiC particle size decreased with increasing Fe content. In addition, a low density of dislocations was observed in both the TiC particles and Fe binder, indicative of annealing and recrystallization, respectively

  12. Microscopic characterizations of membrane electrode assemblies prepared under different hot-pressing conditions

    International Nuclear Information System (INIS)

    Liang, Z.X.; Zhao, T.S.; Xu, C.; Xu, J.B.

    2007-01-01

    The durability of the membrane electrode assembly (MEA) for direct methanol fuel cells (DMFCs) is one of the most critical issues to be addressed before widespread commercialization of the DMFC technology. In this work, we investigated the effect of the hot-pressing duration on the performance and durability of the MEA prepared by hot-pressing technique. It was found that the 60-min hot pressing at 135 deg. C under the pressure of 4.0 MPa yielded a significantly improved MEA durability than did the 3-min hot pressing (a typical duration in practice) under the same condition, but no substantial difference was found in the cell performance of the MEAs prepared with the two different hot-pressing durations. The reason why the hot-pressing duration had no significant effect on cell performance is explained based on X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and Fourier transform infrared spectroscopy (FT-IR) characterizations of the changes in the physiochemical properties of MEAs and their constituent components, including the anode, cathode and Nafion membrane, before and after hot pressing with different durations

  13. Effects of internal gas pressure and microstructure on the mechanisms of hot-pressing and swelling in ceramics. Progress report, June 1, 1975--March 31, 1976

    International Nuclear Information System (INIS)

    Solomon, A.A.

    1976-02-01

    Pressurization system components for studying the hot-pressing and swelling behavior of CoO were built. A vacuum furnace was modified so that dimensional changes can be continuously monitored during sintering under high vacuum. Chracterization of the CoO starting powders was initiated. A technique was developed to form geometrically uniform pellet compacts of high green density using low pressure punch and die pressing followed by high pressure isostatic compaction to obtain uniform green density. Preliminary sintering experiments were carried out at 1 atm in air, inert gas, and under vacuum with specimen deflection continuously monitored. Resulting microstructures were characterized using mercury porosimetry and quantitative optical microscopy. Drastic differences in sintering rates in vacuum and air were observed

  14. Pre-Brazed Casting and Hot Radial Pressing: A Reliable Process for the Manufacturing of CFC and W Monoblock Mockups

    International Nuclear Information System (INIS)

    Visca, E.; Libera, S.; Mancini, A.; Mazzone, G.; Pizzuto, A.; Testani, C.

    2006-01-01

    ENEA association is involved in the European International Thermonuclear Experimental Reactor (ITER) R-and-D activities and in particular for the manufacturing of high heat flux plasma-facing components (HHFC), such as the divertor targets, the baffles and the limiters: During the last years ENEA has manufactured actively cooled mock-ups by using different technologies, namely brazing, diffusion bonding and hot isostatic pressing (HIPping). A new manufacturing process has been set up and tested. It was successfully applied for the manufacturing of W armoured monoblock mockups. This technique is the HRP (Hot Radial Pressing) based on performing a radial diffusion bonding between the cooling tube and the armour tile by pressurizing only the internal tube and by keeping the joining zone in vacuum and at the required bonding temperature. The heating is obtained by a standard air furnace. The next step was to apply the HRP technique for the manufacturing of CFC armoured monoblock components. For this purpose some issues have to be solved like as the low CFC tensile strength, the pure copper interlayer between the heat sink and the armour necessary to mitigate the stress at the joint interface and the low wettability of the pure copper on the CFC matrix. This paper reports the research path followed to manufacture a medium scale vertical target CFC and W armoured mockup by HRP. An ad hoc rig able to maintain the CFC in a compressive constant condition was also designed and tested. The casting of a soft copper interlayer between the tube and the tile was performed by a new technique: the Pre-Brazed Casting (PBC, ENEA patent). Some mock-ups with three NB31 CFC tiles were successfully manufactured and tested to thermal fatigue using electron beam facilities. They all reached at least 1000 cycles at 20 MW/m 2 without suffering any damage. The manufactured medium scale vertical target mock-up is now under testing at the FE2000 (France) facility. (author)

  15. Structure and characteristics of the hot pressed hydroxyapatite/poly-L-lactide composite

    Directory of Open Access Journals (Sweden)

    Ignjatović Nenad L.

    2002-01-01

    Full Text Available Hydroxyapatite/poly-L-lactide (HAp/PLL composite biomaterial can be obtained by different processing methods. Three-dimensional blocks of HAp/PLLA composite biomaterial with mechanical characteristics close to the natural bone tissue can be obtained by hot pressing procedure. Effects of synthesis and compacting on the structure and characteristics of the HAp/PLLA composite biomaterial were studied in this work. Using wade angle X-ray structural analyses (WAXS, differentially scanning calorimetry (DSC, thermogravimetric analysis (TGA and infrared (IR spectroscopy, the changes occurring in the material during synthesis and hot pressing were monitored. Surface microstructure was analyzed by scanning electronic microscopy (SEM coupled with electron-dispersion analysis (EDX. The results obtained indicate a possible decrease in the degree of crystallinity with hot pressing time increase. A block of HAp/PLLA composite biomaterial with 1.6 times lower crystallinity of the polymer phase was obtained by hot pressing in a given time interval with a maximum of 60 minutes. Results of TG analysis show that PLLA stability decreases with increasing hot pressing time, and vice versa. IR study proved that neither destructive changes in constituents nor formation of new phases occurred during hot pressing.

  16. Volatile organic compound emissions during hot-pressing of southern pine particleboard : panel size effects and trade-off between press time and temperature

    Science.gov (United States)

    Wenlong Wang; Douglas J. Gardner; Melissa G.D. Baumann

    2002-01-01

    In previous research, it was shown that decreasing either press temperature or press time generally resulted in decreased volatile organic compound (VOC) emissions during the hot-pressing of southern pine particleboard. However, because it is impossible to reduce both pressing time and temperature while maintaining panel physical and mechanical properties, this study...

  17. Hot-pressing steatite bodies; Obtencion de eseatita por prensado en caliente

    Energy Technology Data Exchange (ETDEWEB)

    Aparicio Arroyo, E

    1967-07-01

    Requirements for some special nuclear engineering ceramic shapes are: big size, impervious, dimensional accuracy and good mechanical and dielectric properties. Limitations of te conventional methods and advantages of te hot pressing techniques for the manufacturing of these shapes are discussed. Hot pressing characteristics of a certain steatite powder are studied. Occurrence of an optimum densification temperature just above the tale decomposition range is found. Experimental data show that the height/diameter ratio of the specimen has no effect on the sintering conditions. Increasing darkness from the graphite mould is detected above the optimum temperature. The hot-pressed steatite is compared with a fired dry-pressed sample of the same composition. (Author) 13 refs.

  18. Hot and cold pressing of (La,Ce)PO4-based nuclear waste forms

    International Nuclear Information System (INIS)

    Floran, R.J.; Rappaz, M.; Abraham, M.M.; Boatner, L.A.

    1981-01-01

    Synthetic analogs of the mineral monazite [(Ce,La,Ca,Th,U)(P,Si)O 4 ] are promising host phases for the isolation of actinide wastes. In the present investigation, the optimal conditions necessary to form high-density, simulated waste pellets from calcined LaPO 4 and CePO 4 powders have been examined. Pellets that are close to the theoretical density are necessary in order to minimize porosity and hence potential avenues along which fluid/waste interactions can take place. Calcined powders prepared by a urea precipitation process were cold pressed and hot pressed under a range of controlled conditions to form coherent, cylindrical pellets. Changes in density were examined as a function of pressure, temperature and duration of sintering. For cold-pressed pellets, a significant increase in density occurs during sintering between 1000 0 C and 1100 0 C. This increase is correlated with substantial grain coarsening of the pellet microstructure. A comparison of cold and hot pressing techniques suggests that, only after sintering, does the density of cold-pressed pellets approach (but not equal) that of the hot-pressed pellets. Densities >90% of the theoretical value of 5.11 g/cm 3 are easily attainable by hot pressing without sintering. The significance of density differences on pellet stability will be investigated in future leaching studies. The apparent advantages of the higher densities achieved by hot pressing must be weighed against the increased technological/engineering complexities involved when working at sustained high temperatures in a remote environment. Thus the cold pressing technique may ultimately prove more practical for large-scale commercial operations

  19. Microstructural analysis of hot press formed 22MnB5 steel

    Science.gov (United States)

    Aziz, Nuraini; Aqida, Syarifah Nur; Ismail, Izwan

    2017-10-01

    This paper presents a microstructural study on hot press formed 22MnB5 steel for enhanced mechanical properties. Hot press forming process consists of simultaneous forming and quenching of heated blank. The 22MnB5 steel was processed at three different parameter settings: quenching time, water temperature and water flow rate. 22MnB5 was processed using 33 full factorial design of experiment (DOE). The full factorial DOE was designed using three factors of quenching time, water temperature and water flow rate at three levels. The factors level were quenching time range of 5 - 11 s, water temperature; 5 - 27°C and water flow rate; 20 - 40 L/min. The as-received and hot press forming processed steel was characterised for metallographic study and martensitic structure area percentage using JEOL Field Emission Scanning Electron Microscopic (FESEM). From the experimental finding, the hot press formed 22MnB5 steel consisted of 50 to 84% martensitic structure area. The minimum quenching time of 8 seconds was required to obtain formed sample with high percentage of martensite. These findings contribute to initial design of processing parameters in hot press forming of 22MnB5 steel blanks for automotive component.

  20. Hot pressing of nanocrystalline tantalum using high frequency induction heating and pulse plasma sintering

    Science.gov (United States)

    Jakubowicz, J.; Adamek, G.; Sopata, M.; Koper, J. K.; Siwak, P.

    2017-12-01

    The paper presents the results of nanocrystalline powder tantalum consolidation using hot pressing. The authors used two different heating techniques during hot pressing: high-frequency induction heating (HFIH) and pulse plasma sintering (PPS). A comparison of the structure, microstructure, mechanical properties and corrosion resistance of the bulk nanocrystalline tantalum obtained in both techniques was performed. The nanocrystalline powder was made to start from the microcrystalline one using the high-energy ball milling process. The nanocrystalline powder was hot-pressed at 1000 °C, whereas, for comparison, the microcrystalline powder was hot pressed up to 1500 °C for proper consolidation. The authors found that during hot pressing, the powder partially reacts with the graphite die covered by boron nitride, which facilitated punches and powder displacement in the die during densification. Tantalum carbide and boride in the nanocrystalline material was found, which can improve the mechanical properties. The hardness of the HFIH and PPS nanocrystalline tantalum was as high as 625 and 615 HV, respectively. The microstructure was more uniform in the PPS nanomaterial. The corrosion resistance in both cases deteriorated, in comparison to the microcrystalline material, while the PPS material corrosion resistance was slightly better than that of the HFIH one.

  1. Structure and properties of hot-pressed boron carbide ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Koval' chenko, M S; Tkachenko, IU G; Koval' chuk, V V; Iurchenko, D Z; Satanin, S V [Institut Problem Materialovedeniia, Kiev (Ukrainian SSR)

    1990-07-01

    The microstructure and strength of B4C-TiB2-TiO{sub 2} ceramics samples, hot-compacted from a mixture of two types of B4C-TiO2-C powder, are examined. The two types are obtained by combining boric acid with either sucrose or carbon black. The grain-sizes of the two powders are found to be distinctly different from one another both before and after the grinding procedure and the degree of dispersion is not high. The strength tests show 600 MPa, the Vicker's hardness is 34.5 GPa, and the crack resistance coefficient of ceramics containing 15 percent TiB2 by mass is 5 MPa m exp 1/2. The use of soluble boron carbide powder helps achieve higher levels of strength and crack resistance. 5 refs.

  2. Radiophase development in hot-pressed alkoxide-derived titanate ceramics for nuclear waste stabilization

    International Nuclear Information System (INIS)

    Dickson, F.J.; Mitamura, H.; White, T.J.

    1989-01-01

    This paper reports phase development as a function of hot-pressing temperature studied in alkoxide-derived titanate-based ceramics doped with a 10 wt% loading of a sodium-rich (NAR) and a sodium-poor (NAP) simulated high-level waste. Pyrochlore was found to be the most abundant phase in both calcine powders. A pseudobrookite phase existed metastably at hot-pressing temperatures between 890 degrees and 920 degrees C. After hot-pressing at 1100 degrees C, the final phase assemblage for the NAP material consisted of zirconolite, hollandite-type, perovskite, alloy, and reduced rutile (Magneli phases). In addition, NAR samples contained hibonite, freudenbergite, and loveringite. Phase development was driven to completion over a very narrow temperature range (≤50 degrees C), beginning at 870 degrees and 850 degrees C for NAP and NAR, respectively, although full densification was not achieved below 1100 degrees C. Both waste forms exhibited comparable microstructure and aqueous durability

  3. Preparation of Ti-aluminide reinforced in situ aluminium matrix composites by reactive hot pressing

    International Nuclear Information System (INIS)

    Roy, D.; Ghosh, S.; Basumallick, A.; Basu, B.

    2007-01-01

    Aluminium based metal matrix composites reinforced with in situ Ti-aluminide and alumina particles were prepared by reactive hot pressing a powder mix of aluminium and nanosized TiO 2 powders. The reinforcements were formed in situ by exothermal reaction between the TiO 2 nano crystalline powder and aluminium. The thermal characteristics of the in situ reaction were studied with the aid of Differential scanning calorimetry (DSC). X-ray diffraction (XRD), Energy dispersive spectroscopy (EDS) and Scanning electron microscopy (SEM) techniques were employed to study the microstructural architecture of the composites as a function of hot pressing temperature and volume percent reinforcement. Microhardness measurements on the as prepared in situ aluminium matrix composites exhibit significant increase in hardness with increase in hot pressing temperature and volume fraction of reinforcement

  4. Solidification of glass powder by a hydrothermal hot-pressing technique

    International Nuclear Information System (INIS)

    Nishioka, Mamoru; Yanagisawa, Kazumichi; Yamasaki, Nakamichi

    1986-01-01

    A borosilicate glass powder was solidified with a NaOH solution or distilled water by the hydrothermal hot-pressing technique. The effect of hydrothermal conditions on the compressive strength was investigated, and the densification mechanism of the glass powder during the hydrothermal hot-pressing was discussed in terms of isothermal shrinkage. The glass powder was successfully solidified by hydrothermal hot-pressing at a reaction temperature lower than that of an ordinary pressure sintering. The solidified body obtained in the presence of distilled water (10 wt%) at 280 deg C had a high compressive strength of about 2300 kg/cm 2 . The analysis of initial densification process of the glass powder in hydrothermal hot-pressing with Murray's rate equation revealed that the densification proceeds both by viscous flow and by rearrangement process. Analysis of the shrinkage rates with a rate equation of hydrothermal reaction suggested that the dissolution of particles into solution controlled the initial densification of the glass powder, and that the alkaline metal acted as a catalyst. (author)

  5. Safe trapping of cesium into pollucite structure by hot-pressing method

    International Nuclear Information System (INIS)

    Omerašević, Mia; Matović, Ljiljana; Ružić, Jovana; Golubović, Željko; Jovanović, Uroš; Mentus, Slavko; Dondur, Vera

    2016-01-01

    A simple one-step method with direct thermal conversion at lower temperatures for preparing a stabile Cs-aluminsilicate phase, known as pollucite, is presented. Cs-exchanged form of Na, Ca-LTA type of zeolite (Cs-LTA) was pressureless sintered and hot pressed at certain temperatures in order to obtain pollucite. XRD and FTIR analysis were used to study structural changes of Cs-LTA before and after thermal treatments. Pressureless sintered sample recrystallized into pollucite phase after heat treatment at 1000 °C (3 h) (PLS1000) and hot pressed sample at 750 °C (3 h) using pressure of 35 MPa (HP750), indicating reduced temperature of 250°. SEM micrographs confirmed that HP750 has higher density than PLS1000 which leads to higher value of compressive strength. The HP750 showed better resistance to Cs leaching than the PLS1000. Base on these results one can conclude that hot pressing is the promising method for the permanent disposal of Cs radionuclides. - Highlights: • Na, Ca-LTA zeolite showed high affinity for Cs ions. • Pollucite phase was obtained using hot pressing at temperature as low as ​750 °C. • HP750 shows better mechanical and morphological properties than PLS1000. • HP750 has lower leaching rate of Cs ions than PLS1000.

  6. An overview of high thermal conductive hot press forming die material development

    Directory of Open Access Journals (Sweden)

    A.R. Zulhishamuddin

    2015-12-01

    Full Text Available Most of the automotive industries are using high strength steel components, which are produced via hot press forming process. This process requires die material with high thermal conductivity that increases cooling rate during simultaneous quenching and forming stage. Due to the benefit of high quenching rate, thermal conductive die materials were produced by adding carbide former elements. This paper presents an overview of the modification of alloying elements in tool steel for high thermal conductivity properties by transition metal elements addition. Different types of manufacturing processes involved in producing high thermal conductive materials were discussed. Methods reported were powder metallurgy hot press, direct metal deposition, selective laser melting, direct metal laser sintering and spray forming. Elements likes manganese, nickel, molybdenum, tungsten and chromium were proven to increase thermal conductivity properties. Thermal conductivity properties resulted from carbide network presence in the steel microstructure. To develop feasible and low cost hot press forming die material, casting of Fe-based alloy with carbide former composition can be an option. Current thermal conductivity properties of hot press forming die material range between 25 and 66 W/m.K. The wide range of thermal conductivity varies the mechanical properties of the resulting components and lifetime of HPF dies.

  7. Hot isostatic pressing of single-crystal nickel-base superalloys: Mechanism of pore closure and effect on Mechanical properties

    Directory of Open Access Journals (Sweden)

    Epishin Alexander I.

    2014-01-01

    Full Text Available Pore annihilation was investigated in the single-crystal nickel-base superalloy CMSX-4. HIP tests at 1288 °C/103 MPa were interrupted at different times, then the specimens were investigated by TEM, metallography and density measurements. The kinetics of pore annihilation was determined. The pore closure mechanism was identified as plastic deformation on the octahedral slip systems. A model describing the kinetics of pore closure has been developed on the base of crystal plasticity and large strain theory. Mechanical tests with the superalloy CMSX-4 and the Ru-containing superalloy VGM4 showed, that HIP significantly increases the fatigue life at low temperatures but has no effect on creep strength.

  8. La{sub 2}O{sub 3}-reinforced W and W-V alloys produced by hot isostatic pressing

    Energy Technology Data Exchange (ETDEWEB)

    Munoz, A., E-mail: angel.munoz@uc3m.es [Departamento de Fisica, Universidad Carlos III de Madrid, 28911 Leganes (Spain); Monge, M.A., E-mail: mmonge@fis.uc3m.es [Departamento de Fisica, Universidad Carlos III de Madrid, 28911 Leganes (Spain); Savoini, B., E-mail: bsavoi@fis.uc3m.es [Departamento de Fisica, Universidad Carlos III de Madrid, 28911 Leganes (Spain); Rabanal, M.E., E-mail: eugenia@ing.uc3m.es [Departamento de Ciencia e Ingenieria de Materiales e Ingenieria Quimica, Universidad Carlos III de Madrid, 28911 Leganes (Spain); Garces, G., E-mail: ggarces@cenim.csic.es [Centro Nacional de Investigaciones Melaturgicas, CENIM, 28040 Madrid (Spain); Pareja, R., E-mail: rpp@fis.uc3m.es [Departamento de Fisica, Universidad Carlos III de Madrid, 28911 Leganes (Spain)

    2011-10-01

    W and W-V alloys reinforced with La{sub 2}O{sub 3} particles have been produced by MA and subsequent HIP at 1573 K and 195 MPa. The microstructure of the consolidated alloys has been characterized by scanning electron microscopy, energy dispersive spectroscopy analyses and X-ray diffraction. The mechanical properties were studied by nanoindentation measurements. The results show that practically full dense billets of W-V, W-V-La{sub 2}O{sub 3} and W-La{sub 2}O{sub 3} alloys can be produced. The microstructure analysis has shown that islands of V are present in W-V and W-V-1La{sub 2}O{sub 3} alloys. In W-1La{sub 2}O{sub 3} islands of La{sub 2}O{sub 3} are also present. The nanohardness of the W matrix increases with the addition of V, while decreases with the addition of La{sub 2}O{sub 3}.

  9. Effect of hot isostatic pressing temperature on the microstructural and mechanical properties in the mullite-zirconia composites

    International Nuclear Information System (INIS)

    Greca, M.C.G.; Melo, M. de F.

    1990-01-01

    This work studies the densification, the microstrutural evolution (porosity and zirconia grain size) and bending strength (σ f ) of the two mullite-zirconia composites with TiO 2 additions (0.25 and 1,0 mole%) submitted to different kind of hipping cycles at several temperatures. The results have been shown that: i) HIPing temperature seem to have no influence in densification and mechanical behaviour. ii) Total densification only appears in composition with more quantity of titania (1.0 mole%) which prove that titanium enhance the mass transfer by changes in grain boundary microchemistry. iii) Mechanical behaviour is correlated with densification and microstructural evolution for both composites and degradation is present at 1500 0 C and 1550 0 C which is related with particle coarsening. (author) [pt

  10. Prediction of maximum casting defect size in MAR-M-247 alloy processed by hot isostatic pressing

    Czech Academy of Sciences Publication Activity Database

    Šmíd, Miroslav; Fintová, Stanislava; Kunz, Ludvík; Hutař, Pavel; Hrbáček, K.

    2015-01-01

    Roč. 22, č. 1 (2015), s. 25-32 ISSN 1335-0803 R&D Projects: GA MPO FR-TI4/030; GA MŠk(CZ) EE2.3.20.0214 Institutional support: RVO:68081723 Keywords : MAR-M 247 * Superalloys * Fatigue * Casting defects * Elevated temperatures Subject RIV: JL - Materials Fatigue, Friction Mechanics http://ojs.mateng.sk/index.php/Mateng/article/view/160/249

  11. The Manufacture of W-UO2 Fuel Elements for NTP Using the Hot Isostatic Pressing Consolidation Process

    Science.gov (United States)

    Broadway, Jeramie; Hickman, Robert; Mireles, Omar

    2012-01-01

    NTP is attractive for space exploration because: (1) Higher Isp than traditional chemical rockets (2)Shorter trip times (3) Reduced propellant mass (4) Increased payload. Lack of qualified fuel material is a key risk (cost, schedule, and performance). Development of stable fuel form is a critical path, long lead activity. Goals of this project are: Mature CERMET and Graphite based fuel materials and Develop and demonstrate critical technologies and capabilities.

  12. Effect of Hot-Pressing Temperature on the Subsequent Enzymatic Saccharification and Fermentation Performance of SPORL Pretreated Forest Biomass

    Science.gov (United States)

    Jingzhi Zhang; Andrea Laguna; Craig Clemons; Michael P. Wolcott; Rolland Gleisner; J.Y. Zhu; Xu Zhang

    2015-01-01

    Methods to increase the energy density ofbiofuel feedstock for shipment are important towards improving supply chain efficiency in upstream processes. Towards this end, densified pretreated lignocellulosic biomass was produced using hot-pressing. The effects offiber hornification induced by hot-pressing on enzymatic digestibilities of lodgepolepine and poplar NE222...

  13. Cold-pressed and hot-pressed rapeseed oil: The effects of roasting and seed moisture on the antioxi- dant activity, canolol, and tocopherol level.

    Science.gov (United States)

    Siger, Aleksander; Józefiak, Marta; Górnaś, Paweł

    2017-01-01

    The paper looks at the levels of canolol, tocopherols and antioxidant activity in cold-pressed and hot-pressed rapeseed oils produced from seeds of various moisture levels (5%, 7.5%, and 10%). The paper also considers the effects of seed roasting on the levels of these compounds. The material used for the tests was rapeseed cv. Adrianna. The quality of the oils obtained is determined using peroxide and acid values. The levels of canolol and tocopherols are analyzed using HPLC. The DPPH radical-scavenging activity method for oil samples and phenolic extract from oils was used. It has been demonstrated that the oils produced from rapeseeds with a 5% moisture content, and   in particular from cold-pressed oils, were characterized by the lowest peroxide values. Cold-pressed oils produced from rapeseeds with a 5% moisture content were characterized by higher levels of tocopherols and plastochromanol-8. In the case of hot-pressed oils, the highest levels of tocopherols were found in oils pro- duced from seeds with a 7.5% moisture content, and the greatest amount of PC-8 (more than 4 mg/100 g) was found in oils produced from seeds with a 10% moisture content. Hot-pressed oils have been shown to have higher levels of these compounds than cold-pressed oils. Both roasting and hot pressing led to an increase in the amount of canolol in the oils investigated. When analysing the antioxidant activity of the oils and phenolic extracts it was shown that phenolic compounds are responsible for approx. 10% of total antioxidant activity. Various levels of biologically active compounds were shown to be present in the rapeseed oil obtained from raw materials of a varying moisture content. The type of pressing process (cold-pressing or hot-pressing) and whether the seeds have undergone roasting has also been shown to affect the resulting oil and the level of native antioxidants it contains.

  14. Consolidation of titanium matrix composites to maximum density by different hot pressing techniques

    International Nuclear Information System (INIS)

    Montealegre Melendez, I.; Neubauer, E.; Danninger, H.

    2010-01-01

    In this present work, TiMMCs were manufactured through conventional and inductive hot pressing techniques. The starting materials were two titanium based powders as metal matrices, and two types of reinforcements, carbon nanofibres and nano-micro-boron particles. After several manufacturing runs with varying parameters, especially, optimized hot pressing parameters, the titanium compacts were characterized. Density and hardness measurements, chemical analyses and microstructural studies were conducted. The two objectives of this work were achieved. On one hand the influence, in the properties of TiMMCs, of the starting materials as matrix powder and reinforcements was determined. Higher content of impurities from the starting materials affected the hardness and the microstructure of the composites, independently of the manufacturing process. On another hand, the study of variations of the manufacturing process as temperature of consolidation and soaking time was reported. Higher densification was obtained at higher consolidation temperature; however, reaction between the matrix and the carbonaceous reinforcement was detected.

  15. Thermoelectric Properties of Hot-Pressed and PECS-Sintered Magnesium-Doped Copper Aluminum Oxide

    Science.gov (United States)

    Liu, Chang; Morelli, Donald T.

    2011-05-01

    Copper aluminum oxide (CuAlO2) is considered as a potential candidate for thermoelectric applications. Partially magnesium-doped CuAlO2 bulk pellets were fabricated using solid-state reactions, hot-pressing, and pulsed electric current sintering (PECS) techniques. X-ray diffraction and scanning electron microscopy were adopted for structural analysis. High-temperature transport property measurements were performed on hot-pressed samples. Electrical conductivity increased with Mg doping before secondary phases became significant, while the Seebeck coefficient displayed the opposite trend. Thermal conductivity was consistently reduced as the Mg concentration increased. Effects of Mg doping, preparation conditions, and future modification on this material's properties are discussed.

  16. Room temperature nanoindentation creep of hot-pressed B{sub 6}O

    Energy Technology Data Exchange (ETDEWEB)

    Machaka, Ronald, E-mail: RMachaka@csir.co.za [Light Metals, Materials Science and Manufacturing, Council for Scientific and Industrial Research, Office F7, Building 14F, P.O. Box 395, Pretoria 0001 (South Africa); DST/NRF Centre of Excellence in Strong Materials, University of the Witwatersrand, Private Bag 3, Wits, Johannesburg 2050 (South Africa); Derry, Trevor E. [DST/NRF Centre of Excellence in Strong Materials, University of the Witwatersrand, Private Bag 3, Wits, Johannesburg 2050 (South Africa); School of Physics, University of the Witwatersrand, Private Bag 3, Wits, Johannesburg 2050 (South Africa); Sigalas, Iakovos [DST/NRF Centre of Excellence in Strong Materials, University of the Witwatersrand, Private Bag 3, Wits, Johannesburg 2050 (South Africa); School of Chemical and Metallurgical Engineering, University of the Witwatersrand, Private Bag 3, Wits, Johannesburg 2050 (South Africa)

    2014-06-01

    Nanoindentation has become a widely used and versatile means of characterising the near-surface nanomechanical properties of a wide variety of materials. Yet, the nanomechanical properties of the polycrystalline boron suboxide (B{sub 6}O) material prepared by uniaxial hot-pressing are sparsely known. We recently reported on the nanoindentation profiles, nanoindentation hardness, and elastic modulus determined by using the Oliver–Pharr method. To complement our earlier reports on the analysis of the load–displacement indentation response of hot-pressed B{sub 6}O and for the first time, we present and discuss results giving an insight into the temporal evolution of the nanoindentation creep behaviour in B{sub 6}O ceramics.

  17. Densification and Grain Growth in Polycrystalline Olivine Rocks Synthesized By Evacuated Hot-Pressing

    Science.gov (United States)

    Meyers, C. D.; Kohlstedt, D. L.; Zimmerman, M. E.

    2017-12-01

    Experiments on laboratory-synthesized olivine-rich rocks form the starting material for many investigations of physical processes in the Earth's upper mantle (e.g., creep behavior, ionic diffusion, and grain growth). Typically, a fit of a constitutive law to experimental data provides a description of the kinetics of a process needed to extrapolate across several orders of magnitude from laboratory to geological timescales. Although grain-size is a critical parameter in determining physical properties such as viscosity, broad disagreement persists amongst the results of various studies of grain growth kinetics in olivine-rich rocks. Small amounts of impurities or porosity dramatically affect the kinetics of grain growth. In this study, we developed an improved method for densifying olivine-rich rocks fabricated from powdered, gem-quality single crystals that involves evacuating the pore space, with the aim of refining measurements of the kinetics of mantle materials. In previous studies, olivine powders were sealed in a metal can and hydrostatically annealed at roughly 300 MPa and 1250 °C. These samples, which appear opaque and milky-green, typically retain a small amount of porosity. Consequently, when annealed at 1 atm, extensive pore growth occurs, inhibiting grain growth. In addition, Fourier-transform infrared and confocal Raman spectroscopy reveal absorption peaks characteristic of CO2 in the pores of conventionally hot-pressed material. To avoid trapping of adsorbed contaminants, we developed an evacuated hot-pressing method, wherein the pore space of powder compacts is vented to vacuum during heating and pressurization. This method produces a highly dense, green-tinted, transparent material. No CO2 absorptions peaks exist in evacuated hot-pressed material. When reheated to annealing temperatures at 1 atm, the evacuated hot-pressed material undergoes limited pore growth and dramatically enhanced grain-growth rates. High-strain deformation experiments on

  18. Means to rise stability of matrices for hot pressing of non-ferrous metals

    International Nuclear Information System (INIS)

    Nagajtsev, A.A.; Piguzova, D.Kh.; Vajnpres, L.V.

    1975-01-01

    The paper deals with the basic trends adopted both in the USSR and abroad with respect to the development and industrial usage of new materials for hot pressing dies. Methods of their strengthening are also indicated. The paper presents results of production tests of new die steels and refractory alloys at a number of factories processing non-ferrous metals. The problems of their wide application in this field are considered

  19. Hot Deformation Behavior and Pulse Current Auxiliary Isothermal Forging of Hot Pressing Sintering TiAl Based Alloys.

    Science.gov (United States)

    Shi, Chengcheng; Jiang, Shaosong; Zhang, Kaifeng

    2017-12-16

    This paper focuses on the fabrication of as-forged Ti46.5Al2Cr1.8Nb-(W, B) alloy via pulse current auxiliary isothermal forging (PCIF). The starting material composed of near gamma (NG) microstructure was fabricated by adopting pre-alloyed powders via hot pressing sintering (HPS) at 1300 °C. Isothermal compression tests were conducted at a strain rate range of 0.001-0.1 s -1 and a temperature range of 1125-1275 °C to establish the constitutive model and processing map. The optimal hot deformation parameters were successfully determined (in a strain rate range of 10 -3 -2.5 × 10 -3 s -1 and temperature range of 1130-1180 °C) based on the hot processing map and microstructure observation. Accordingly, an as-forged TiAl based alloy without cracks was successfully fabricated by PCIF processing at 1175 °C with a nominal strain rate of 10 -3 s -1 . Microstructure observation indicated that complete dynamic recrystallization (DRX) and phase transformation of γ→α₂ occurred during the PCIF process. The elongation of as-forged alloy was 136%, possessing a good secondary hot workability, while the sintered alloy was only 66% when tested at 900 °C with a strain rate of 2 × 10 -4 s -1 .

  20. Immobilisation of 137Cs and 90Sr in hot-pressed clinoptilolite

    International Nuclear Information System (INIS)

    Briggs, A.; Jones, D.V.C.; Cole, G.B.; Valentine, T.M.; Preston, R.F.; Hawes, R.W.M.; Fones, M.D.

    1984-07-01

    It is shown that clinoptilolites from Nevada and Mudhills, California, can be vitrified by hot-pressing at 1000 to 1050 deg C for 30 min under 23 MPa pressure in graphite dies, or for 10 min under 3.5 MPa pressure in stainless steel bellows-shaped containers. Activity measurements before and after hot-pressing show that the radionuclides 137 Cs and 90 Sr are retained almost completely during the process. The hot-pressed material is shown to be extremely resistant to leaching of the nuclides, either in Soxhlet or long-term static leach tests. Gamma-irradiation increases their leachability; that of 90 Sr more than that of 137 Cs, but even so, the leach rates of both remain very low. X-ray diffraction spectra taken before and after heat-treatment for 10 days at temperatures up to 1000 deg C show no deleterious effects, and hydrothermal treatments at temperatures up to 90 deg C for 100 days, even in the presence of sodium ions in solution, are shown not to cause any changes detectable by X-ray diffraction. (author)

  1. Efficient transfer of large-area graphene films onto rigid substrates by hot pressing.

    Science.gov (United States)

    Kang, Junmo; Hwang, Soonhwi; Kim, Jae Hwan; Kim, Min Hyeok; Ryu, Jaechul; Seo, Sang Jae; Hong, Byung Hee; Kim, Moon Ki; Choi, Jae-Boong

    2012-06-26

    Graphene films grown on metal substrates by chemical vapor deposition (CVD) method have to be safely transferred onto desired substrates for further applications. Recently, a roll-to-roll (R2R) method has been developed for large-area transfer, which is particularly efficient for flexible target substrates. However, in the case of rigid substrates such as glass or wafers, the roll-based method is found to induce considerable mechanical damages on graphene films during the transfer process, resulting in the degradation of electrical property. Here we introduce an improved dry transfer technique based on a hot-pressing method that can minimize damage on graphene by neutralizing mechanical stress. Thus, we enhanced the transfer efficiency of the large-area graphene films on a substrate with arbitrary thickness and rigidity, evidenced by scanning electron microscope (SEM) and atomic force microscope (AFM) images, Raman spectra, and various electrical characterizations. We also performed a theoretical multiscale simulation from continuum to atomic level to compare the mechanical stresses caused by the R2R and the hot-pressing methods, which also supports our conclusion. Consequently, we believe that the proposed hot-pressing method will be immediately useful for display and solar cell applications that currently require rigid and large substrates.

  2. EFFECT OF CHEMICAL MODIFICATION AND HOT-PRESS DRYING ON POPLAR WOOD

    Directory of Open Access Journals (Sweden)

    Guo-Feng Wu

    2010-11-01

    Full Text Available Urea-formaldehyde prepolymer and hot-press drying were used to improve the properties of poplar wood. The wood was impregnated with the prepolymer using a pulse-dipping machine. The impregnated timbers were compressed and dried by a multilayer hot-press drying kiln. The drying rate was more rapid during the chemical modification and hot-press drying than conventional kiln-drying. In addition, the properties of timber were also enhanced obviously. When the compression rate was 28.6%, the basic density, oven dry density and air-dried density of modified wood improved 22%, 71%, and 70%, respectively. The bending strength and compressive strength parallel to grain increased 60% and 40%. The water uptake of treated wood was significantly decreased compared with the untreated wood. The FTIR analysis successfully showed that the intensity of hydroxyl and carbonyl absorption peaks decreased significantly, which was attributed to a reaction of the NHCH2OH of urea-formaldehyde prepolymer with the wood carboxyl (C=O and hydroxyl (-OH groups. The XRD results indicated that the degree of crystallinity increased from 35.09% to 36.91%. The morphologic models of chemical within wood were discovered by SEM.

  3. Improving the Quality of Hot Stamping Parts with Innovative Press Technology and Inline Process Control

    Science.gov (United States)

    Vollmer, R.; Palm, C.

    2017-09-01

    The increasing number of hot stamped parts in the automotive industry is challenging different process areas. This paper presents a method how to improve the production rates over the whole life cycle of a hot forming part. In the core element of a hot forming line, the hydraulic press, mainly two processing steps are performed. Forming and quenching of the sheet metal part. In addition to the forming operation, it is inevitable to optimize the quenching condition in the bottom dead centre in order to reach a fully martensitic structure and tight geometrical tolerances of the part. Deviations in the blank thickness, tool wear, polishing of classical tools impair the quenching condition and therefore the part quality over the time. A new press and tool design has been developed to counter this effect by providing homogenous contact pressure over the whole die. Especially with a multi cavity tool, the new method is advantageous. Test series have shown that the new tool and press concept can produce parts with a blank thickness of 1.0 mm within 8.0 s cycle time. The so called PCH flex principle makes it possible to produce such high output rates under reliable conditions.

  4. The fabrication of ZnO nanowire field-effect transistors combining dielectrophoresis and hot-pressing

    International Nuclear Information System (INIS)

    Chang, Y-K; Chau-N H, Franklin

    2009-01-01

    Zinc oxide nanowire field-effect transistors (NW-FETs) were fabricated combining the dielectrophoresis (DEP) and the hot-pressing methods. DEP was used to position both ends of the nanowires on top of the source and the drain electrodes, respectively. Hot-pressing of nanowires on the electrodes was then employed to ensure good contacts between the nanowires and the electrodes. The good device performance achieved with our method of fabrication indicates that DEP combined with hot-pressing has the potential to be applied to the fabrication of flexible electronics on a roll-to-roll basis.

  5. Chemical vapor deposition of tantalum on graphite cloth for making hot pressed fiber reinforced carbide-graphite composite

    International Nuclear Information System (INIS)

    Hollabaugh, C.M.; Davidson, K.V.; Radosevich, C.L.; Riley, R.E.; Wallace, T.C.

    1977-01-01

    Conditions for the CVD of a uniform coating of Ta on fibers of a woven graphite cloth were established. The effect of gas composition, pressure, and temperature were investigated, and the conditions that gave the desired results are presented. Several layers of the coated cloth were hot pressed to produce a TaC--C composite having uniformly dispersed, fine-grained TaC in graphite. Three compositions were hot pressed: 15, 25, and 40 volume percent carbide. 8 figures, 2 tables

  6. Numerical simulation of hot-pressed veneer products: Forming - Spring back – Distortion

    DEFF Research Database (Denmark)

    Ormarsson, Sigurdur; Sandberg, Dick

    2007-01-01

    Customers demand very high quality of veneered furniture products with regard to surface appearance, shape stability and stiffness. To meet these requirements, it is important to improve the manufacturing process by a better understanding of the thermo-hygro-mechanical behaviour of the individual...... veneers. During the manufacture of strongly curved products, the veneers are exposed to large membrane and bending deformations and to high pressure in the radial fibre direction. When hot-press forming is used, the veneers are also exposed to a high surface temperature during the pressing time (curing...... time). These severe conditions can result in plastic deformation perpendicular to the veneer surface as well as mechano-sorptive strains in the curved regions, since the heating can have a significant influence on the moisture distribution. How strong an influence these factors have on the distortion...

  7. Pre-brazed casting and hot radial pressing: A reliable process for the manufacturing of CFC and W monoblock mock-ups

    Energy Technology Data Exchange (ETDEWEB)

    Visca, Eliseo [Associazione EURATOM-ENEA sulla Fusione, C.R. Frascati, Via E. Fermi, 45, IT-00044 Frascati, RM (Italy)], E-mail: visca@frascati.enea.it; Libera, S.; Mancini, A.; Mazzone, G.; Pizzuto, A. [Associazione EURATOM-ENEA sulla Fusione, C.R. Frascati, Via E. Fermi, 45, IT-00044 Frascati, RM (Italy); Testani, C. [CSM S.p.A., IT-00128 Castel Romano, RM (Italy)

    2007-10-15

    ENEA is involved in the European International Thermonuclear Experimental Reactor (ITER) R and D activities and, in particular, for the manufacturing of high heat flux plasma-facing components (HHFC), such as the divertor targets, the baffles and the limiters. During last years, ENEA has manufactured actively cooled mock-ups by using different technologies, namely brazing, diffusion bonding and hot isostatic pressing (HIPping). A new manufacturing process has been set up and tested. It was successfully applied for the manufacturing of W armoured monoblock mock-ups. This technique is the HRP (hot radial pressing) based on performing a radial diffusion bonding between the cooling tube and the armour tile by pressurizing only internal tube and by keeping the joining zone in vacuum at the required bonding temperature. The heating is obtained by a standard air furnace. The HRP technique is now used for the manufacturing of CFC armoured monoblock components. For this purpose, some issues have to be faced, like the low CFC tensile strength, the pure copper interlayer between the heat sink and the armour necessary to mitigate the stress at the joint interface, and the low wettability of the pure copper on the CFC matrix. This paper reports the research path followed to manufacture a medium scale vertical target CFC and W armoured mock-up by HRP. A casting of a soft copper interlayer between the tube and the tile was obtained by a new technique: the pre-brazed casting (PBC, ENEA patent). Some preliminary mock-ups with three NB31 CFC tiles were successfully manufactured and tested to thermal fatigue using electron beam facilities. They all reached at least 1000 cycles at 20 MW/m{sup 2} without suffering any damage. The manufactured medium scale vertical target mock-up is now under testing at the FE2000 (France) facility. These activities were performed in the frame of ITER-EFDA contracts.

  8. Pre-brazed casting and hot radial pressing: A reliable process for the manufacturing of CFC and W monoblock mock-ups

    International Nuclear Information System (INIS)

    Visca, Eliseo; Libera, S.; Mancini, A.; Mazzone, G.; Pizzuto, A.; Testani, C.

    2007-01-01

    ENEA is involved in the European International Thermonuclear Experimental Reactor (ITER) R and D activities and, in particular, for the manufacturing of high heat flux plasma-facing components (HHFC), such as the divertor targets, the baffles and the limiters. During last years, ENEA has manufactured actively cooled mock-ups by using different technologies, namely brazing, diffusion bonding and hot isostatic pressing (HIPping). A new manufacturing process has been set up and tested. It was successfully applied for the manufacturing of W armoured monoblock mock-ups. This technique is the HRP (hot radial pressing) based on performing a radial diffusion bonding between the cooling tube and the armour tile by pressurizing only internal tube and by keeping the joining zone in vacuum at the required bonding temperature. The heating is obtained by a standard air furnace. The HRP technique is now used for the manufacturing of CFC armoured monoblock components. For this purpose, some issues have to be faced, like the low CFC tensile strength, the pure copper interlayer between the heat sink and the armour necessary to mitigate the stress at the joint interface, and the low wettability of the pure copper on the CFC matrix. This paper reports the research path followed to manufacture a medium scale vertical target CFC and W armoured mock-up by HRP. A casting of a soft copper interlayer between the tube and the tile was obtained by a new technique: the pre-brazed casting (PBC, ENEA patent). Some preliminary mock-ups with three NB31 CFC tiles were successfully manufactured and tested to thermal fatigue using electron beam facilities. They all reached at least 1000 cycles at 20 MW/m 2 without suffering any damage. The manufactured medium scale vertical target mock-up is now under testing at the FE2000 (France) facility. These activities were performed in the frame of ITER-EFDA contracts

  9. Waste treatment process by solidifying cementitious materials using hydrothermal hot-pressing

    International Nuclear Information System (INIS)

    Matsumoto, Y.; Kamakura, T.; Yamasaki, N.; Hashida, T.

    2001-01-01

    Solidification of low-level radioactive wastes containing Na 2 SO 4 with cement by hydrothermal hot-pressing (HHP) technique was examined. Relatively high mechanical strength, reduced leaching ratio of SO 3 , and higher resistance to the carbonation of the HHP product were attained in comparison with conventional concrete. The solidification by the HHP treatment may be proceeded by the rearrangement of particles and the bonding material formation among the particles by dissolution-deposition process. The possibility of developing the accelerated testing method for duration of cemented materials by hydrothermal method was discussed. (author)

  10. Room temperature nanoindentation creep of hot-pressed B6O

    CSIR Research Space (South Africa)

    Machaka, R

    2014-06-01

    Full Text Available of the nanoindentation creep behavior in B6O ceramics. 1 Room temperature nanoindentation creep of hot-pressed B6O Ronald Machakaa,b,* , Trevor E. Derryb,d, Iakovos Sigalasb,c aLight Metals, Materials Science and Manufacturing, Council for Scientific..., University of the Witwatersrand, Private Bag 3, Wits, Johannesburg 2050, South Africa dSchool of Physics, University of the Witwatersrand, Private Bag 3, Wits, Johannesburg 2050, 2050 South Africa Abstract: Nanoindentation has become a widely...

  11. Texture studies of hot-pressed K2Pb4Nb10O30 ceramics

    International Nuclear Information System (INIS)

    Filip'ev, V.S.; Zav'yalov, V.P.; Bunina, O.A.; Gavrilyachenko, S.V.; Fesenko, E.G.

    1984-01-01

    An X-ray diffraction analysis was used to investigate the texture in sampl es of K 2 Pb 4 Nb 10 O 30 ferroelectric produced by powder hot pressing and sintering at 1370-1500 k. A spontaneous formation of the secondary texture during ferroelectric phase transformation was revealed. An important role of internal stresses in the secondary texture formation was supported. The ceramic s with a high-grade texture is noted to be characterized by a high anisotropy of dielectric and piezoelectric properties, its parameters approaching to those of a monocrystal

  12. Ultra-low thermal conductivities of hot-pressed attapulgite and its potential as thermal insulation material

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Yuan; Ren, Zhifeng, E-mail: bohr123@163.com, E-mail: zren@uh.edu [Department of Physics and TcSUH, University of Houston, Houston, Texas 77204 (United States); Wang, Xiuzhang [Department of Physics and TcSUH, University of Houston, Houston, Texas 77204 (United States); Hubei Key Laboratory of Pollutant Analysis and Reuse Technology and School of Physics and Electronic Science, Hubei Normal University, Huangshi, Hubei 435002 (China); Wang, Yumei [Department of Physics and TcSUH, University of Houston, Houston, Texas 77204 (United States); Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190 (China); Tang, Zhongjia; Makarenko, Tatyana; Guloy, Arnold [Department of Chemistry, University of Houston, Houston, Texas 77204 (United States); Zhang, Qinyong, E-mail: bohr123@163.com, E-mail: zren@uh.edu [Center for Advanced Materials and Energy, Xihua University, Chengdu, Sichuan 610039 (China)

    2016-03-07

    In the past, there have been very few reports on thermal properties of attapulgite which is a widely used clay mineral. In this work, we report on extremely low thermal conductivities in attapulgite samples synthesized by hot-pressing. Attapulgite powder was hot-pressed at different temperatures into bulk samples, and a systematic study was conducted on the microstructures and thermal properties. Differential scanning calorimetry analysis shows that hot-pressing induces a rapid dehydration of the attapulgite powders. X-ray diffraction data and scanning/transmission electron microscopy reveal that the hot-pressed attapulgite features high porosity and complex microstructures, including an amorphous phase. As a result, the hot-pressed attapulgite exhibits thermal conductivity less than 2.5 W m{sup −1} K{sup −1} up to 600 °C. For one sample with porosity of 45.7%, the thermal conductivity is as low as 0.34 W m{sup −1} K{sup −1} at 50 °C. This suggests the potential of hot-pressed attapulgite as a candidate for thermal barrier materials.

  13. Hot pressing effect on (Bi 0.25 Sb 0.75 ) 2 Te 3 mechanical and ...

    Indian Academy of Sciences (India)

    Hot pressing effect on (Bi0.25Sb0.75)2Te3 mechanical and thermoelectric properties ... The crystal of this compound was prepared, pulverized in a particle size ratio of 64% ... microscopy and, for only once successful attempt, atomic force microscopy. The acquired images ensured to show homogeneous structures for hot ...

  14. Properties of nonvolatile and antibacterial bioboard produced from bamboo macromolecules by hot pressing

    Directory of Open Access Journals (Sweden)

    Shengbo Ge

    2018-03-01

    Full Text Available Employing the antibacterial property of industrial bamboo vinegar (IBV and the photocatalytic degradation of TiO2, bamboo macromolecules were pretreated and processed into nonvolatile and antibacterial bio board (NVABB. The NVABB was then analyzed by conducting Fourier-transform infrared spectroscopy, thermogravimetric analysis and differential thermal analysis. Results show that NVABB samples had average density of 0.96 g/cm3, which is appropriate for application. In terms of physical and mechanical properties, the best NVABB sample obtained from IBV, TiO2 and bamboo had an IBV pretreatment time of 10 min, 2% TiO2 and 1% bamboo charcoal. Fourier-transform infrared spectroscopy demonstrated that optimum conditions for hot pressing were a temperature of 170 °C, duration of 15 min and the addition of IBV and TiO2. Thermogravimetric analysis/differential thermal analysis curves suggest that the thermal degradation of NVABB was less than that of bamboo and that hot pressing obviously increased the thermal stability of HDBB samples. Analysis of the antimicrobial effect revealed that IBV pretreatment improves the antibacterial property of NVABB. Keywords: Industrial bamboo vinegar, Nonvolatile and antibacterial bio board, Bamboo macromolecules, Fourier-transform infrared spectroscopy, Thermogravimetric analysis/differential thermal analysis

  15. Mechanical properties of hot-pressed Al-4.5 wt. % Cu/WC composite

    Directory of Open Access Journals (Sweden)

    Samaneh Bernoosi

    2014-12-01

    Full Text Available In this study, the elemental powders of aluminum and copper were initially subjected to mechanical alloying using an attrition ball mill under argon atmosphere to produce an Al-4.5 wt% Cu powder alloy. The WC nanoparticles were then added to the powder alloy and milled in a planetary ball mill to explore the role of the WC nanoparticles on the mechanical properties of the fabricated composite powder. The experimental results revealed that a solid solution of Al-Cu could be formed after MA and a good dispersion of the WC nanoparticles in the aluminum matrix was obtained as characterized using X-ray diffraction and scanning electron microscopy, respectively. The results of hardness and compression tests of the hot pressed composites indicated that the MA followed by the hot-press processes was successful to fabricate an alloy and a metal matrix composite with considerable mechanical properties. However, a decreasing trend in the hardness and strength of the composites with the WC contents of more than 5wt% was observed. The maximum values of 260 HV and 575 MPa were obtained for a composite containing 5 wt% of nano ceramic particles.

  16. Fabrication of laminated ZrC-SiC composite by vacuum hot-pressing sintering

    Directory of Open Access Journals (Sweden)

    Yuanyuan Li

    2015-03-01

    Full Text Available Laminated ZrC-SiC ceramic was prepared through tape casting and hot pressing. The green tapes of ZrC and SiC were prepared at room temperature. In order to improve the density of composite, the binder of green tapes were removed at 550 °C for 1 h. The laminated structure and the cracks propagation path, which is not a straight line, are observed by optical metalloscope. The compact laminated ZrC-SiC composite sintered by vacuum hot-pressing at 1650 °C for 90 min under pressure of 20 MPa was researched by X-ray diffraction and scanning electron microscopy (SEM equipped with energy dispersive X-ray analysis. The results showed that interlayer bonding is tight, and no disordered phase has formed in the interlayers of ZrC or SiC, and the combination mode is physical mechanism.

  17. Microstructural evolution during hot pressing of the blended elemental Ti-6%Al-7%Nb alloy

    International Nuclear Information System (INIS)

    Henriques, V.A.R.; Sandim, H.R.Z.; Coelho, G.C.; Silva, C.R.M. da

    2003-01-01

    The Ti-6%Al-7%Nb (wt.%) α-β alloy was developed aiming the replacement of the traditional Ti-6%Al-4%V alloy in surgical implants owing to its larger biocompatibility. Samples of this alloy were obtained using the blended elemental (BE) technique. The isochronal hot pressing of the compacts was carried out in the range 700-1500 deg. C with a compaction pressure of 20 MPa and a heating rate of 20 deg. C min -1 . In this work, the behavior of the elementary powders during the hot pressing and the corresponding microstructural evolution were investigated. The alloy was characterized by means of scanning electron microscopy (SEM) in the backscattered mode (BSE), X-ray diffraction (XRD), and density measurements. The results indicate that the homogenization of the alloy is diffusion-controlled and Ti.Al intermediary compounds (TiAl and Ti 3 Al) are formed at lower temperatures. With increasing temperature, homogenization of the alloy takes place and a coarse plate-like α+intergranular β structure is found throughout the microstructure in temperatures above 1300 deg. C. The process variables were defined aiming to minimize interstitial pick-up (C, O, and N) and avoiding intensive grain growth

  18. Microstructure characteristics of high borated stainless steel fabricated by hot-pressing sintering

    Energy Technology Data Exchange (ETDEWEB)

    Zhou, Xuan; Wang, Mingjia, E-mail: mingjiawangysu@126.com; Zhao, Hongchang

    2016-04-25

    The present study investigated the microstructure of powder metallurgy (P/M) high borated stainless steel through hot-pressing sintering in a temperature range of 1000–1150 °C within 30 min under 30 MPa. Microstructure and phase examinations were carried out by applying scanning electron microscope, electron backscatter diffraction and X-ray diffraction analysis. The results of as-atomized powders demonstrated that many powders kept egg-type structure with an austenite outer layer and the eutectic borides were much finer than those in traditional cast products. Microstructure studies revealed that borides suffered Ostwald ripening and were significantly influenced by the sintering temperature. Orientation maps indicated that the inter-particle contact areas consisted of equiaxed grains and the regions consisting of large elongated grains partly inherited the microstructure characteristics of as-atomized powder particles. Furthermore, the mechanisms governing the morphological changes in microstructure were discussed. - Highlights: • Near-complete densification could be obtained through hot-pressing sintering. • There was no phase transformation and present phases were M{sub 2}B and austenite. • Borides suffered Ostwald ripening and were significantly influenced by temperature. • Inter-particle contact areas consisted of equiaxed grains for recrystallization. • Deformation-free zones exhibited elongated grains for dendritic arms coarsening.

  19. Effect of roll hot press temperature on crystallite size of PVDF film

    Energy Technology Data Exchange (ETDEWEB)

    Hartono, Ambran, E-mail: ambranhartono@yahoo.com; Sanjaya, Edi [Departement of Physics Faculty of Science and Technology, Islamic State University Syarif Hidayatullah , Jl. Juanda 95 Ciputat Jakarta (Indonesia); Djamal, Mitra; Satira, Suparno; Bahar, Herman [Theoretical High Energy Physics and Instrumentation Group Research, Faculty Mathematics and Natural Sciences, Institut Teknologi Bandung, Jl. Ganesa 10 Bandung (Indonesia); Ramli [Departement of Physics, Faculty of Mathematics and Natural Sciences, Universitas Negeri Padang, Jl.Prof. Hamka, Padang 25131 (Indonesia)

    2014-03-24

    Fabrication PVDF films have been made using Hot Roll Press. Preparation of samples carried out for nine different temperatures. This condition is carried out to see the effect of Roll Hot Press temperature on the size of the crystallite of PVDF films. To obtain the diffraction pattern of sample characterization is performed using X-Ray Diffraction. Furthermore, from the diffraction pattern is obtained, the calculation to determine the crystallite size of the sample by using the Scherrer equation. From the experimental results and the calculation of crystallite sizes obtained for the samples with temperature 130 °C up to 170 °C respectively increased from 7.2 nm up to 20.54 nm. These results show that increasing temperatures will also increase the size of the crystallite of the sample. This happens because with the increasing temperature causes the higher the degree of crystallization of PVDF film sample is formed, so that the crystallite size also increases. This condition indicates that the specific volume or size of the crystals depends on the magnitude of the temperature as it has been studied by Nakagawa.

  20. Mechanical properties and porosity of dental glass-ceramics hot-pressed at different temperatures

    Directory of Open Access Journals (Sweden)

    Carla Castiglia Gonzaga

    2008-09-01

    Full Text Available The objective of this work was to evaluate biaxial-flexural-strength (σf, Vickers hardness (HV, fracture toughness (K Ic, Young's modulus (E, Poisson's ratio (ν and porosity (P of two commercial glass-ceramics, Empress (E1 and Empress 2 (E2, as a function of the hot-pressing temperature. Ten disks were hot-pressed at 1065, 1070, 1075 and 1080 °C for E1; and at 910, 915, 920 and 925 °C for E2. The porosity was measured by an image analyzer software and s f was determined using the piston-on-three-balls method. K Ic and HV were determined by an indentation method. Elastic constants were determined by the pulse-echo method. For E1 samples treated at different temperatures, there were no statistical differences among the values of all evaluated properties. For E2 samples treated at different temperatures, there were no statistical differences among the values of σf, E, and ν, however HV and K Ic were significantly higher for 910 and 915 °C, respectively. Regarding P, the mean value obtained for E2 for 925 °C was significantly higher compared to other temperatures.

  1. Process simulation and experimental validation of Hot Metal Gas Forming with new press hardening steels

    Science.gov (United States)

    Paul, A.; Reuther, F.; Neumann, S.; Albert, A.; Landgrebe, D.

    2017-09-01

    One field in the work of the Fraunhofer Institute for Machine Tools and Forming Technology IWU in Chemnitz is industry applied research in Hot Metal Gas Forming, combined with press hardening in one process step. In this paper the results of investigations on new press hardening steels from SSAB AB (Docol®1800 Bor and Docol®2000 Bor) are presented. Hot tensile tests recorded by the project partner (University of West Bohemia, Faculty of Mechanical Engineering) were used to create a material model for thermo-mechanical forming simulations. For this purpose the provided raw data were converted into flow curve approximations of the real stress-real strain-curves for both materials and afterwards integrated in a LS-DYNA simulation model of Hot Metal Gas Forming with all relevant boundary conditions and sub-stages. Preliminary experimental tests were carried out using a tool at room temperature to permit evaluation of the forming behaviour of Docol 1800 Bor and Docol 2000 Bor tubes as well as validation of the simulation model. Using this demonstrator geometry (outer diameter 57 mm, tube length 300 mm, wall thickness 1.5 mm), the intention was to perform a series of tests with different furnace temperatures (from 870 °C to 1035 °C), maximum internal pressures (up to 67 MPa) and pressure build-up rates (up to 40 MPa/s) to evaluate the formability of Docol 1800 Bor and Docol 2000 Bor. Selected demonstrator parts produced in that way were subsequently analysed by wall thickness and hardness measurements. The tests were carried out using the completely modernized Dunkes/AP&T HS3-1500 hydroforming press at the Fraunhofer IWU. In summary, creating a consistent simulation model with all relevant sub-stages was successfully established in LS-DYNA. The computation results show a high correlation with the experimental data regarding the thinning behaviour. The Hot Metal Gas Forming of the demonstrator geometry was successfully established as well. Different hardness values

  2. Chemical composition and oxidative stability of jussara (Euterpe edulis M.) oil extracted by cold and hot mechanical pressing

    International Nuclear Information System (INIS)

    Da Cunha, A.L.A.; Freitas, S.P.; Godoy, R.L.O.; Cabral, L.M.C.; Tonon, R.V.

    2017-01-01

    The aim of this work was to evaluate the effect of mechanical pressing on jussara oil yield, oxidative stability and carotenoid profile with or without heat application. Firstly, jussara pulp was centrifuged for juice extraction, and the resulting cake was dried until reaching 10% moisture content. Then, oil extraction was performed in an expeller press at 25 ºC (cold pressing) and at 50 ºC (hot pressing). The process performance was evaluated by the oil yield, and the crude jussara oil was characterized for fatty acid composition, acid value, carotenoid profile and oxidative stability. Jussara oil contained 74% unsaturated fatty acids, mainly oleic and linoleic acids (48% and 24%, respectively). The oil yield was almost twice as high for the hot process as compared to the cold one. Additionally, hot pressing resulted in 25% higher total carotenoid content as compared to cold pressing, with β-carotene as the most abundant one. Hot and cold pressing showed no difference in oil oxidative stability and fatty acid composition. [es

  3. Effect of Furnish on Temperature and Vapor Pressure Behavior in the Center of Mat Panels during Hot Pressing

    Directory of Open Access Journals (Sweden)

    Muhammad Navis Rofii

    2014-07-01

    Full Text Available Particleboard achieves its overall performance characteristics during hot pressing process. As this process is influenced by several factors, particularly temperature and pressure, it is very important to understand the behavior of both. This study investigates the effects of furnish materials on temperature and vapor pressure behavior inside particleboard mat panels during hot pressing. Strand type particles from hinoki and ring-flaker recycled wood particles were used as furnish for laboratory-scale particleboard panels with a target density of 0.76 g/cm³. Mat panels with a moisture content of about 10% were hot pressed at a platen temperature of 180°C and an initial pressure of 3 MPa until the mat center reached the same temperature as the platen. A press monitoring device (PressMAN Lite was used for detecting the temperature and vapor pressure change in the center of the mat panels. The study showed that the furnish type affected the temperature and vapor behavior inside the mat panels. Particleboard made of hinoki strand resulted in a longer plateau time, a higher plateau temperature and a higher gas pressure generated during hot pressing than those of ring-flaker recycled wood particles. Mixed board resulted in values between those of the two other furnish materials.

  4. Fabrication of dense yttrium oxyfluoride ceramics by hot pressing and their mechanical, thermal, and electrical properties

    Science.gov (United States)

    Tahara, Ryuki; Tsunoura, Toru; Yoshida, Katsumi; Yano, Toyohiko; Kishi, Yukio

    2018-06-01

    Excellent corrosion-resistant materials have been strongly required to reduce particle contamination during the plasma process in semiconductor production. Yttrium oxyfluoride can be a candidate as highly corrosion-resistant material. In this study, three types of dense yttrium oxyfluoride ceramics with different oxygen contents, namely, YOF, Y5O4F7 and Y5O4F7 + YF3, were fabricated by hot pressing, and their mechanical, thermal, and electrical properties were evaluated. Y5O4F7 ceramics showed an excellent thermal stability up to 800 °C, a low loss factor, and volume resistivity comparable to conventional plasma-resistant oxides, such as Y2O3. From these results, yttrium oxyfluoride ceramics are strongly suggested to be used as electrostatic chucks in semiconductor production.

  5. Characteristics of hot-pressed fiber-reinforced ceramics with SiC matrix

    Science.gov (United States)

    Miyoshi, Tadahiko; Kodama, Hironori; Sakamoto, Hiroshi; Goto, Akihiro; Iijima, Shiroo

    1989-11-01

    Silicon carbide ceramics’ matrix composites with SiC or C filaments were fabricated through hot pressing, and the effects of the filament pullout on their fracture toughness were experimentally investigated. The C-rich coating layers on the SiC filaments were found to have a significant effect on the frictional stress at the filament/matrix interfaces, through assising the filamet pullout from the matrix. Although the coating layers were apt to burn out in the sintering process of SiC matrix compposites, a small addition of carbon to the raw materials was found to be effective for the retention of the layers on the fibers, thus increasing the fracture toughness of the composites. The fracture toughness of the C filament/SiC matrix composite increased with temperature due to the larger interfacial frictional stress at higher temperatures, because of the higher thermal expansion of the filament in the radial direction than that of the matrix.

  6. Interface characteristic during bonding of Be and HR-1 stainless steel by hot pressing

    International Nuclear Information System (INIS)

    Li Hui; Kang Renmu; Zhou Shangqi; Kong Jilan; Zhang Pengcheng

    2010-01-01

    Be and HR-I stainless steel was diffusion bonded by hot pressing. The microstructure,composition and phase distribution and mechanical properties of the joints were analyzed using the optical microscopy, scanning electron microscopy(SEM), scanning auger microspectroscopy(SAM) and x-ray diffraction(XRD), and the effect of different interlayer materials Cu and Al and Ag-Cu alloy was also discussed. The results show that it is not easy to joint Be and HR-1 stainless when Al was used as the interlayer material, but good joints can be obtained using Cu and Ag and Cu alloy as the interlayer materials, because the formation of Be-Fe brittle intermetallic compounds was prevented. Ag-Cu alloy is the best interlayer materials among them, as it can reduce the mutual diffusion between Be and Fe. (authors)

  7. TEM study of a hot-pressed Al2O3-NbC composite material

    Directory of Open Access Journals (Sweden)

    Wilson Acchar

    2005-03-01

    Full Text Available Alumina-based composites have been developed in order to improve the mechanical properties of the monolithic matrix and to replace the WC-Co material for cutting tool applications. Al2O3 reinforced with refractory carbides improves hardness, fracture toughness and wear resistance to values suitable for metalworking applications. Al2O3-NbC composites were uniaxially hot-pressed at 1650 °C in an inert atmosphere and their mechanical properties and microstructures were analyzed. Sintered density, average grain size, microhardness and fracture toughness measurements and microstructural features were evaluated. Results have shown that the mechanical properties of alumina-NbC are comparable to other carbide systems. Microstructural analysis has shown that the niobium carbide particles are mainly located at the grain boundaries of alumina grains, which is an evidence of the "pinning effect", produced by NbC particles.

  8. Effect of Liquid Phase Content on Thermal Conductivity of Hot-Pressed Silicon Carbide Ceramics

    International Nuclear Information System (INIS)

    Lim, Kwang-Young; Jang, Hun; Lee, Seung-Jae; Kim, Young-Wook

    2015-01-01

    Silicon carbide (SiC) is a promising material for Particle-Based Accident Tolerant (PBAT) fuel, fission, and fusion power applications due to its superior physical and thermal properties such as low specific mass, low neutron cross section, excellent radiation stability, low coefficient of thermal expansion, and high thermal conductivity. Thermal conductivity of PBAT fuel is one of very important factors for plant safety and energy efficiency of nuclear reactors. In the present work, the effect of Y 2 O 3 -Sc 2 O 3 content on the microstructure and thermal properties of the hot pressed SiC ceramics have been investigated. Suppressing the β to α phase transformation of SiC ceramics is beneficial in increasing the thermal conductivity of liquid-phase sintered SiC ceramics. Developed SiC ceramics with Y 2 O 3 -Sc 2 O 3 additives are very useful for thermal conductivity on matrix material of the PBAT fuel

  9. Phase transitions to 120 GPa for shock-compressed pyrolytic and hot-pressed boron nitride

    International Nuclear Information System (INIS)

    Gust, W.H.; Young, D.A.

    1977-01-01

    Shock-compression characteristics of two types of hexagonal graphitelike boron nitride have been investigated. Highly oriented very pure pyrolytic boron nitride exhibits shock-velocity versus particle-velocity discontinuities that appear to be manifestations of the initiation of a sluggish phase transition. This transition begins at 20 GPa and is driven to completion (melting) at 75 GPa. Discontinuities in the plot for impure hot-pressed boron nitride indicate initiation at 10 GPa and completion at 20 GPa. The (U/sub s/, U/sub p/) plots follow essentially the same paths for 4.0 < U/sub p/ < 5.2 km/sec. No evidence for a transition to a metalliclike state was seen. Temperature calculations indicate that the material is liquid above approx.80 GPa

  10. Transfer of microstructure pattern of CNTs onto flexible substrate using hot press technique for sensing applications

    International Nuclear Information System (INIS)

    Mishra, Prabhash; Tai, Nyan-Hwa; Harsh; Islam, S.S.

    2013-01-01

    Graphical abstract: - Highlights: • Successfully transfer of microstructure patterned CNTs on PET substrate. • Demonstrate as resistor-based NH 3 gas sensor in the sub-ppm range. • Excellent photodetector having instantaneous response and recovery characteristics. • An effective technique to grow and produce flexible electronic device. - Abstract: In this work, we report the successful and efficient transfer process of two- dimensional (2-D) vertically aligned carbon nanotubes (CNTs) onto polyethylene terephthalate (PET) substrate by hot pressing method with an aim to develop flexible sensor devices. Carbon nanotubes are synthesized by cold wall thermal chemical vapor deposition using patterned SiO 2 substrate under low pressure. The height of the pattern of CNTs is controlled by reaction time. The entire growth and transfer process is carried out within 30 min. Strong adhesion between the nanotube and polyethylene terephthalate substrate was observed in the post-transferred case. Raman spectroscopy and scanning electron microscope (SEM) studies are used to analyze the microstructure of carbon nanotube film before and after hot pressing. This technique shows great potential for the fabrication of flexible sensing devices. We report for the first time, the application of patterned microstructure developed by this technique in the development of gas sensor and optoelectronic device. Surface resistive mode is used for detection of ammonia (NH 3 ) gas in the sub-ppm range. An impressive photoconducting response is also observed in the visible wavelength. The reproducibility of the sample was checked and the results indicate the possibility of use of carbon nanotube as gas sensor, photodetector, CCDs etc

  11. Transfer of microstructure pattern of CNTs onto flexible substrate using hot press technique for sensing applications

    Energy Technology Data Exchange (ETDEWEB)

    Mishra, Prabhash [Department of Material Science and Engineering, National Tsing Hua University, Hsinchu 30013, Taiwan (China); Nano-Sensor Research Laboratory, F/O Engineering and Technology, Jamia Millia Islamia, Jamia Nagar, New Delhi (India); Tai, Nyan-Hwa [Department of Material Science and Engineering, National Tsing Hua University, Hsinchu 30013, Taiwan (China); Harsh [Nano-Sensor Research Laboratory, F/O Engineering and Technology, Jamia Millia Islamia, Jamia Nagar, New Delhi (India); Islam, S.S., E-mail: safiul5996@gmail.com [Nano-Sensor Research Laboratory, F/O Engineering and Technology, Jamia Millia Islamia, Jamia Nagar, New Delhi (India)

    2013-08-01

    Graphical abstract: - Highlights: • Successfully transfer of microstructure patterned CNTs on PET substrate. • Demonstrate as resistor-based NH{sub 3} gas sensor in the sub-ppm range. • Excellent photodetector having instantaneous response and recovery characteristics. • An effective technique to grow and produce flexible electronic device. - Abstract: In this work, we report the successful and efficient transfer process of two- dimensional (2-D) vertically aligned carbon nanotubes (CNTs) onto polyethylene terephthalate (PET) substrate by hot pressing method with an aim to develop flexible sensor devices. Carbon nanotubes are synthesized by cold wall thermal chemical vapor deposition using patterned SiO{sub 2} substrate under low pressure. The height of the pattern of CNTs is controlled by reaction time. The entire growth and transfer process is carried out within 30 min. Strong adhesion between the nanotube and polyethylene terephthalate substrate was observed in the post-transferred case. Raman spectroscopy and scanning electron microscope (SEM) studies are used to analyze the microstructure of carbon nanotube film before and after hot pressing. This technique shows great potential for the fabrication of flexible sensing devices. We report for the first time, the application of patterned microstructure developed by this technique in the development of gas sensor and optoelectronic device. Surface resistive mode is used for detection of ammonia (NH{sub 3}) gas in the sub-ppm range. An impressive photoconducting response is also observed in the visible wavelength. The reproducibility of the sample was checked and the results indicate the possibility of use of carbon nanotube as gas sensor, photodetector, CCDs etc.

  12. Investigation of microstructure in hot-pressed Nb–23Ti–15Al alloy

    International Nuclear Information System (INIS)

    Shi, Zhiwu; Wei, Hua; Zhang, Hongyu; Wu, Duoli; Jin, Tao; Sun, Xiaofeng; Zheng, Qi

    2015-01-01

    Highlights: • The Ti(O, C), a new strengthening phase, is found in Nb–Ti–Al alloys. • Ti(O, C) has a face-centered cubic structure and a lattice parameter of 4.27 Å. • Two different morphologies of Ti(O, C) are observed. • β and δ phases exhibit as large irregular blocks and equiaxed particles. • Ordering of β phase is observed in hot-pressed Nb–Ti–Al alloy. - Abstract: Microstructure of hot-pressed Nb–23Ti–15Al alloy has been systematically investigated, with emphasis on the characterization of Ti(O, C) phase. The microstructure and composition of Nb–23Ti–15Al alloy were characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD), transmission electron microscopy (TEM) and electron probe microanalysis (EPMA). The results indicate the presence of β, δ and Ti(O, C) phases in the alloy. The β phase exhibits as large irregular blocks, while the δ phase presents as small equiaxed particles linked together around β blocks. Ordering of β phase is shown by related selected area electronic diffraction (SAED) patterns and dark-field micrograph. The Ti(O, C), a solid-solution of TiO or TiC, is characterized for the first time in Nb–Ti–Al alloy. The Ti(O, C) has a face-centered cubic (FCC) structure and a moderate lattice parameter between that of TiO and TiC. Two different morphologies of Ti(O, C) are observed in the alloy: large cobblestone-like aggregated particles and small dispersive particles. The formation of Ti(O, C) phase can potentially increase high-temperature strength of Nb–Ti–Al alloy

  13. Investigation of microstructure in hot-pressed Nb–23Ti–15Al alloy

    Energy Technology Data Exchange (ETDEWEB)

    Shi, Zhiwu; Wei, Hua; Zhang, Hongyu; Wu, Duoli; Jin, Tao; Sun, Xiaofeng; Zheng, Qi, E-mail: qzheng@imr.ac.cn

    2015-07-05

    Highlights: • The Ti(O, C), a new strengthening phase, is found in Nb–Ti–Al alloys. • Ti(O, C) has a face-centered cubic structure and a lattice parameter of 4.27 Å. • Two different morphologies of Ti(O, C) are observed. • β and δ phases exhibit as large irregular blocks and equiaxed particles. • Ordering of β phase is observed in hot-pressed Nb–Ti–Al alloy. - Abstract: Microstructure of hot-pressed Nb–23Ti–15Al alloy has been systematically investigated, with emphasis on the characterization of Ti(O, C) phase. The microstructure and composition of Nb–23Ti–15Al alloy were characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD), transmission electron microscopy (TEM) and electron probe microanalysis (EPMA). The results indicate the presence of β, δ and Ti(O, C) phases in the alloy. The β phase exhibits as large irregular blocks, while the δ phase presents as small equiaxed particles linked together around β blocks. Ordering of β phase is shown by related selected area electronic diffraction (SAED) patterns and dark-field micrograph. The Ti(O, C), a solid-solution of TiO or TiC, is characterized for the first time in Nb–Ti–Al alloy. The Ti(O, C) has a face-centered cubic (FCC) structure and a moderate lattice parameter between that of TiO and TiC. Two different morphologies of Ti(O, C) are observed in the alloy: large cobblestone-like aggregated particles and small dispersive particles. The formation of Ti(O, C) phase can potentially increase high-temperature strength of Nb–Ti–Al alloy.

  14. Nanostructured Al–Zn–Mg–Cu–Zr alloy prepared by mechanical alloying followed by hot pressing

    International Nuclear Information System (INIS)

    Azimi, Amin; Shokuhfar, Ali; Zolriasatein, Ashkan

    2014-01-01

    Nanostructured Al–7.8 wt% Zn–2.6 wt% Mg–2 wt% Cu–0.1 wt% Zr alloy was mechanically alloyed (MA) from elemental powders and consolidated by hot press technique. The effect of the milling time and hot pressing process on microstructure was investigated by means of X-ray diffraction measurements (XRD) and analytical and scanning electron microscopy (SEM). Furthermore mechanical properties of samples with different MA time as well as pure aluminum were investigated by microhardness and compression tests. The results show that an Al–Zn–Mg–Cu–Zr homogenous supersaturated solid solution with a crystallite size of 27 nm was obtained after 40 h of milling time. Microstructure refinement and morphological changes of powders from flake to spherical shape were observed by increasing milling time. Phase and microstructural characterization of high density bulk nanostructured samples revealed that increasing milling time up to 40 h leads to formation of MgZn 2 precipitation in the alloy matrix. With increasing milling time, density of the samples and crystalline size decrease. Significant enhancement of hardness and compressive strength is observed in the aluminum alloy by increasing milling time up to 40 h which is much higher than pure aluminum. Crystallite size refinement in pure aluminum samples from micro- to nanoscales resulted in 107% and 100% improvement in compressive strength and hardness, respectively. Furthermore the compressive strength and hardness of Al–Zn–Mg–Cu–Zr alloy nanostructured samples increased to 179% and 172%, respectively, compared to nanostructured pure Al, which was produced as reference specimen. 40 h of MA was the optimum case for preparing such an Al alloy and more milling up to 50 h led to deterioration of mechanical properties

  15. Solidification of ion-exchange resins by hydrothermal hot-pressing

    International Nuclear Information System (INIS)

    Kaneko, M.

    1993-01-01

    The solidification reaction which easily occurs while continuously keeping the mixture of cation and anion exchange resins compressed under hydrothermal conditions has been demonstrated. Dehydration was considered to occur between sulphonic acid (-SO 3 H) from the cation exchange resin and quaternary ammonium [-CH 2 -N(CH 3 ) 3 OH] from anion-exchange resin-on terminal groups. The cation-and anion-exchange resins were mixed in a 1:1 weight ratio, put in a hot-pressing autoclave and compressed between pistons from the top and bottom at 600 kg cm -2 pressure. The material was continuously compressed during hydrothermal treatment at 200 kg cm -2 by a hydraulic jack and heated to a desired temperature with an induction heater. This system could be used for rapid temperature increasing up to 30 o c min -1 . The pressure and temperature were kept constant for 10 min. The autoclave was cooled to room temperature after the hydrothermal treatment. After the specimen was taken out, the ion-exchange radical reactions were estimated and the product structures were examined. The cation- and anion-exchange resin mixture was solidified. The resultant solidified body at a 300 o C reaction condition for 10 min had a 1.0 g cm -3 density and 700 kg cm -2 compressive strength, and the weight loss did not change in distilled water for 2 weeks. On the other hand, a solidification reaction did not occur at below 250 o C when only the cation or anion was solidified, but they were decomposed. These results suggest that a mixture of cation- and anion-exchange resins causes a solidification reaction under hydrothermal hot-pressing conditions at 300 o C. (author)

  16. Hot Press as a Sustainable Direct Recycling Technique of Aluminium: Mechanical Properties and Surface Integrity.

    Science.gov (United States)

    Yusuf, Nur Kamilah; Lajis, Mohd Amri; Ahmad, Azlan

    2017-08-03

    Meltless recycling technique has been utilized to overcome the lack of primary resources, focusing on reducing the usage of energy and materials. Hot press was proposed as a novel direct recycling technique which results in astoundingly low energy usage in contrast with conventional recycling. The aim of this study is to prove the technical feasibility of this approach by characterizing the recycled samples. For this purpose, AA6061 aluminium chips were recycled by utilizing hot press process under various operating temperature (T s = 430, 480, and 530 °C) and holding times (t s = 60, 90, and 120 min). The maximum mechanical properties of recycled chip are Ultimate tensile strength (UTS) = 266.78 MPa, Elongation to failure (ETF) = 16.129%, while, for surface integrity of the chips, the calculated microhardness is 81.744 HV, exhibited at T s = 530 °C and t s = 120 min. It is comparable to theoretical AA6061 T4-temper where maximum UTS and microhardness is increased up to 9.27% and 20.48%, respectively. As the desired mechanical properties of forgings can only be obtained by means of a final heat treatment, T5-temper, aging after forging process was employed. Heat treated recycled billet AA6061 (T5-temper) are considered comparable with as-received AA6061 T6, where the value of microhardness (98.649 HV) at 175 °C and 120 min of aging condition was revealed to be greater than 3.18%. Although it is quite early to put a base mainly on the observations in experimental settings, the potential for significant improvement offered by the direct recycling methods for production aluminium scrap can be clearly demonstrated. This overtures perspectives for industrial development of solid state recycling processes as environmentally benign alternatives of current melting based practices.

  17. Coercivity enhancement of HDDR-processed Nd-Fe-B permanent magnet with the rapid hot-press consolidation process

    Energy Technology Data Exchange (ETDEWEB)

    Nozawa, N. [Magnetic Materials Research Laboratory, NEOMAX Company, Hitachi Metals Ltd., Osaka 618-0013 (Japan); Sepehri-Amin, H. [Graduate School of Pure and Applied Sciences, University of Tsukuba, Tsukuba 305-8571 (Japan); Magnetic Materials Center, National Institute for Materials Science, Tsukuba 305-0047 (Japan); Ohkubo, T. [Magnetic Materials Center, National Institute for Materials Science, Tsukuba 305-0047 (Japan); Hono, K. [Graduate School of Pure and Applied Sciences, University of Tsukuba, Tsukuba 305-8571 (Japan); Magnetic Materials Center, National Institute for Materials Science, Tsukuba 305-0047 (Japan); Nishiuchi, T. [Magnetic Materials Research Laboratory, NEOMAX Company, Hitachi Metals Ltd., Osaka 618-0013 (Japan); Hirosawa, S., E-mail: Satoshi_Hirosawa@hitachi-metals.co.j [Magnetic Materials Research Laboratory, NEOMAX Company, Hitachi Metals Ltd., Osaka 618-0013 (Japan)

    2011-01-15

    High coercivity, fully dense anisotropic permanent magnets of submicron grain sizes were produced by rapid hot-press consolidation of hydrogenation-disproportionation-desorption-recombination (HDDR) processed Nd-Fe-Co-B powders. In the hot-press process, the coercivity of the consolidated material showed a sharp minimum prior to full densification. Thereafter, it reached a value 25% higher than that of the initial powder. Scanning electron microscopy and transmission electron microscopy observations revealed that the variation in H{sub cJ} was caused by a redistribution of Nd along the grain boundaries during hot pressing and that the high coercivity was attributable to the formation of thin, continuous Nd-rich phase along the grain boundaries.

  18. Ceramic nuclear waste forms. II. A ceramic-waste composite prepared by hot pressing. Progress report and preprint

    International Nuclear Information System (INIS)

    McCarthy, G.J.

    1975-01-01

    A feasibility study was conducted to determine whether nuclear waste calcine and a crystalline ceramic matrix can be fabricated by hot pressing into a composite waste form with suitable leaching resistance and thermal stability. It was found that a hard, dense composite could be formed using the typical commercial waste formulation PW-4b and a matrix of α-quartz with a small amount of a lead borosilicate glass added as a consolidation aide. Its density, waste loading, and leaching resistance are comparable to the glasses currently being considered for fixation of nuclear wastes. The hot pressed composite offers a closer approach to thermodynamic stability and improved thermal stability (in monolithic form) compared to glass waste forms. Recommendations for further optimization of the hot pressed waste form are given. (U.S.)

  19. Process controls for Bi2Te3-Sb2Te3 prepared by mechanical alloying and hot pressing

    International Nuclear Information System (INIS)

    Lee, Go-Eun; Kim, Il-Ho; Choi, Soon-Mok; Lim, Young-Soo; Seo, Won-Seon; Park, Jae-Soung; Yang, Seung-Ho

    2014-01-01

    p-Type Bi 2 Te 3 -Sb 2 Te 3 solid solutions were prepared by mechanical alloying (MA) and hot pressing (HP) under different process conditions, after which the transport and the thermoelectric properties were evaluated. The relative densities of all hot-pressed specimens were over 98%, and the microstructure and crystal orientation were independent of the HP direction. All specimens exhibited p-type conduction, and the electrical resistivity was observed to increase slightly with increasing temperature, indicating a degenerate semiconductor behavior. The carrier concentration decreased with increasing HP temperature while the mobility increased. The maximum figure of merit obtained was 0.86 at 323 K for Bi 0.5 Sb 1.5 Te 3 hot-pressed at 648 K.

  20. Microstructure and thermoelectric properties of β-FeSi2 ceramics fabricated by hot-pressing and spark plasma sintering

    International Nuclear Information System (INIS)

    Qu Xiurong; Lue Shuchen; Hu Jianmin; Meng Qingyu

    2011-01-01

    Highlights: → With increasing hot-pressing (HP) temperature, the thermoelectric figure of merit of β-FeSi 2 ceramics is improved slightly. → The grain size of the sample sintered by the spark plasma sintering (SPS) process is smaller than that by the HP process. → The SPS sample shows excellent thermoelectric performance attributed to low thermal conductivity. - Abstract: The microstructure and thermoelectric properties of β-FeSi 2 ceramics by hot pressing (HP) and spark plasma sintering (SPS) are investigated. With increasing hot-pressing temperature, the density, electronic conductivity and thermal conductivity of the samples increase significantly, the thermoelectric figure of merit is improved slightly. The microstructure study indicates that the sizes of the β-FeSi 2 and ε-FeSi phases in the sample sintered by the SPS process are smaller than that by the HP process. The SPS sample shows excellent thermoelectric performance due to the low thermal conductivity.

  1. Mechanical and thermal expansion properties of β-eucryptite prepared by sol-gel methods and hot pressing

    International Nuclear Information System (INIS)

    Xia, L.; Wen, G.W.; Qin, C.L.; Wang, X.Y.; Song, L.

    2011-01-01

    Research highlights: → Dense LAS glass-ceramics were fabricated by sol-gel and hot pressing technique. → The LAS glass-ceramics have relative good mechanical properties. → The negative thermal expansion behavior of LAS glass-ceramics was investigated. -- Abstract: The microstructures, mechanical properties and thermal expansion behavior of monolithic lithium aluminosilicate glass-ceramics, prepared by sol-gel method and hot pressing, were investigated by using X-ray diffraction, scanning and transmission electron microscopies, three-point bend tests and dilatometry. β-eucryptite appeared as main phase in the monolithic lithium aluminosilicate glass-ceramics. The glass ceramics exhibited high relative densities and the average flexural strength and fracture toughness values were 154 MPa and 2.46 MPa m 1/2 , respectively. The lithium aluminosilicate glass-ceramics hot pressed 1300 and 1350 o C demonstrated negative coefficient of thermal expansion, which was affected by amount and type of crystalline phases.

  2. Effect of phosphorus additions on hot pressing temperature and some properties of WC-Co hard alloys

    International Nuclear Information System (INIS)

    Dotsenko, V.M.; Simkina, Eh.S.; Tsypin, N.V.

    1977-01-01

    Results of studies on the effect of phosphorus additions on hot pressing temperature and some properties of VK6 and VK15 hard alloys are given. It is shown that alloying of hard alloys with 3-6 wt % phosphorus gives opportunity to lower substantially (for 200-300 deg) their hot pressing temperature. Hardness and density of alloys with phosphorus do not practically change. Some decrease of strength and wear-resistance characteristics is observed which is obviously connected with irregular distribution of phosphorus in the alloy

  3. Wettability of hot-pressed samples of boron-containing aluminium compounds by liquid metals and alloys

    International Nuclear Information System (INIS)

    Kharlamov, A.I.; Nizhenko, V.I.; Kirillova, N.V.; Floka, L.I.

    2000-01-01

    Highly dispersed powders of aluminium borides and borocarbides were sintered by hot pressing method. Temperature dependence of wettability of hot-pressed boride samples (α-AlB 12 and AlB 18 ) and aluminium borocarbides (Al 3 B 48 C 2 , Al 8 B 4 C 2 and AlB 24 C) by liquid aluminium, copper, germanium, silicon and melts Al + 25 wt.%Si and Cu + (3-6) wt.%Ti was studied. Dependence of a compound wettability on the ratio of components in it was analyzed [ru

  4. Isostatic compression of buffer blocks. Middle scale

    International Nuclear Information System (INIS)

    Ritola, J.; Pyy, E.

    2012-01-01

    Manufacturing of buffer components using isostatic compression method has been studied in small scale in 2008 (Laaksonen 2010). These tests included manufacturing of buffer blocks using different bentonite materials and different compression pressures. Isostatic mould technology was also tested, along with different methods to fill the mould, such as vibration and partial vacuum, as well as a stepwise compression of the blocks. The development of manufacturing techniques has continued with small-scale (30 %) blocks (diameter 600 mm) in 2009. This was done in a separate project: Isostatic compression, manufacturing and testing of small scale (D = 600 mm) buffer blocks. The research on the isostatic compression method continued in 2010 in a project aimed to test and examine the isostatic manufacturing process of buffer blocks at 70 % scale (block diameter 1200 to 1300 mm), and the aim was to continue in 2011 with full-scale blocks (diameter 1700 mm). A total of nine bentonite blocks were manufactured at 70 % scale, of which four were ring-shaped and the rest were cylindrical. It is currently not possible to manufacture full-scale blocks, because there is no sufficiently large isostatic press available. However, such a compression unit is expected to be possible to use in the near future. The test results of bentonite blocks, produced with an isostatic pressing method at different presses and at different sizes, suggest that the technical characteristics, for example bulk density and strength values, are somewhat independent of the size of the block, and that the blocks have fairly homogenous characteristics. Water content and compression pressure are the two most important properties determining the characteristics of the compressed blocks. By adjusting these two properties it is fairly easy to produce blocks at a desired density. The commonly used compression pressure in the manufacturing of bentonite blocks is 100 MPa, which compresses bentonite to approximately

  5. Isostatic compression of buffer blocks. Middle scale

    Energy Technology Data Exchange (ETDEWEB)

    Ritola, J.; Pyy, E. [VTT Technical Research Centre of Finland, Espoo (Finland)

    2012-01-15

    Manufacturing of buffer components using isostatic compression method has been studied in small scale in 2008 (Laaksonen 2010). These tests included manufacturing of buffer blocks using different bentonite materials and different compression pressures. Isostatic mould technology was also tested, along with different methods to fill the mould, such as vibration and partial vacuum, as well as a stepwise compression of the blocks. The development of manufacturing techniques has continued with small-scale (30 %) blocks (diameter 600 mm) in 2009. This was done in a separate project: Isostatic compression, manufacturing and testing of small scale (D = 600 mm) buffer blocks. The research on the isostatic compression method continued in 2010 in a project aimed to test and examine the isostatic manufacturing process of buffer blocks at 70 % scale (block diameter 1200 to 1300 mm), and the aim was to continue in 2011 with full-scale blocks (diameter 1700 mm). A total of nine bentonite blocks were manufactured at 70 % scale, of which four were ring-shaped and the rest were cylindrical. It is currently not possible to manufacture full-scale blocks, because there is no sufficiently large isostatic press available. However, such a compression unit is expected to be possible to use in the near future. The test results of bentonite blocks, produced with an isostatic pressing method at different presses and at different sizes, suggest that the technical characteristics, for example bulk density and strength values, are somewhat independent of the size of the block, and that the blocks have fairly homogenous characteristics. Water content and compression pressure are the two most important properties determining the characteristics of the compressed blocks. By adjusting these two properties it is fairly easy to produce blocks at a desired density. The commonly used compression pressure in the manufacturing of bentonite blocks is 100 MPa, which compresses bentonite to approximately

  6. Microstructure of in-situ Synthesized (TiB+TiC)/Ti Composites Prepared by Hot-pressing

    Institute of Scientific and Technical Information of China (English)

    Zhenzhu ZHENG; Lin GENG; Honglin WANG; Weimin ZHOU; Hongyu XU

    2003-01-01

    In-situ 5 vol.pct TiB whiskers and TiC particulates reinforced Ti composites were fabricated by blending Ti powderand B4C particulates followed by reactive hot-pressing. The microstructure of the composites was investigated byusing differential scanning c

  7. Hot radial pressing: An alternative technique for the manufacturing of plasma-facing components

    International Nuclear Information System (INIS)

    Visca, E.; Libera, S.; Mancini, A.; Mazzone, G.; Pizzuto, A.; Testani, C.

    2005-01-01

    The Hot radial pressing (HRP) manufacturing technique is based on the radial diffusion bonding principle performed between the cooling tube and the armour tile. The bonding is achieved by pressurizing the cooling tube while the joining interface is kept at the vacuum and temperature conditions. This technique has been used for the manufacturing of relevant mock-ups of the ITER divertor vertical target. Tungsten monoblock mock-ups were successfully tested to high heat flux thermal fatigue (20 MW/m 2 of absorbed heat flux for 1000 cycles). After these good results the activity is now focused on the developing of a manufacturing process suitable also for the CFC monoblock mock-ups. A FE calculation was performed to investigate the stress involved in the CFC tiles during the process and to avoid the CFC fracture. The results obtained by the FE calculation and by the test performed in air simulating a HRP manufacturing process for a CFC monoblock mock-ups is reported in the paper

  8. Mechanical properties of hot-pressed SiC-TiC composites

    Directory of Open Access Journals (Sweden)

    Kamil Kornaus

    2017-12-01

    Full Text Available SiC-TiC composites, with 0, 5, 10 and 20 vol.% of TiC, were sintered by the hot-pressing technique at temperature of 2000 °C under argon atmosphere. SiC sintering process was activated by liquid phase created by the reaction between Al2O3 and Y2O3, in which it is possible to dissolve passivating oxide layers (SiO2 and TiO2 and partially SiC and TiC carbides. Microstructure observation and density measurements confirmed that the composites were dense with uniformly distributed components. Differences in thermal expansion coefficients between SiC and TiC led to complex stress state occurrence. These stresses combined with the liquid-derived separate phase between grains boundaries increased fracture toughness of the composites, which ranged from 5.8 to 6.3 MPa·m0.5. Opposite to the bending strength, fracture toughness increased with the TiC volume fraction. By means of simulation of residual thermal stresses in the composites, it was found that with the increasing volume fraction of TiC, tensile stress in TiC grains is reduced simultaneously with strong rise of compressive stresses in the matrix.

  9. Fabrication of SiCp/Al Alloy Composites by In-situ Vacuum Hot Press Process

    Energy Technology Data Exchange (ETDEWEB)

    Choi, S. W.; Hong, S. K.; Kim, Y. M.; Kang, C. S. [Chonnam National University, Kwangju (Korea); Chang, S. Y. [Hanyang University, Seoul (Korea)

    2001-07-01

    SiCp/pure Al and SiCp/2024Al MMCs were fabricated by in-situ VHP process designed specially just in this study which is composed of the vacuum hot press at range from R.T. to 500 deg.C and the continuous extrusion without canning process at 520 deg.C. It was investigated the effect of SiC particle size, volume fraction and extrusion ratio on the tensile properties and micro structure in all composites. In case of the 10:1 extrusion ratio, but SiCp/pure Al and SiCp/2024Al composites were shown a sound appearance and a good micro structure without crack of SiCp as well as uniform distribution of SiCp. However, in case of the 16:1 extrusion ratio, the number of cracked SiC particles more than increased in a higher volume fraction composite and 2024Al matrix composite compared with pure Al matrix one. The tensile strength of the composites reinforced smaller SiCp was higher than that of the bigger SiCp reinforced in same volume fraction and extrusion ratio. (author) 14 refs., 14 figs.

  10. SGEM Hot Off the Press: ultrasound during critical care simulation: a randomized crossover study.

    Science.gov (United States)

    McKenna, Paul; Thoma, Brent; Milne, Ken; Bond, Chris

    2017-01-01

    As part of the Canadian Journal of Emergency Medicine's (CJEM) developing social media strategy, 1 we are collaborating with the Skeptics' Guide to Emergency Medicine (SGEM) to summarize and critically appraise the current emergency medicine (EM) literature using evidence-based medicine principles. In the "Hot Off the Press" series, we select original research manuscripts published in CJEM to be featured on the SGEM website/podcast 2 and discussed by the study authors and the online EM community. A similar collaboration is underway between the SGEM and Academic Emergency Medicine. What follows is a summary of the selected article the immediate post-publication synthesis from the SGEM podcast, commentary by the first author, and the subsequent discussion from the SGEM blog and other social media. Through this series, we hope to enhance the value, accessibility, and application of important, clinically relevant EM research. In this, the third SGEM HOP hosted collaboratively with CJEM, we discuss Olszynski et al.'s randomized crossover study evaluating the use of ultrasound simulator devices during critical care simulation. 3.

  11. Dynamic Failure and Fragmentation of a Hot-Pressed Boron Carbide

    Science.gov (United States)

    Sano, Tomoko; Vargas-Gonzalez, Lionel; LaSalvia, Jerry; Hogan, James David

    2017-12-01

    This study investigates the failure and fragmentation of a hot-pressed boron carbide during high rate impact experiments. Four impact experiments are performed using a composite-backed target configuration at similar velocities, where two of the impact experiments resulted in complete target penetration and two resulted in partial penetration. This paper seeks to evaluate and understand the dynamic behavior of the ceramic that led to either the complete or partial penetration cases, focusing on: (1) surface and internal failure features of fragments using optical, scanning electron, and transmission electron microscopy, and (2) fragment size analysis using state-of-the-art particle-sizing technology that informs about the consequences of failure. Detailed characterization of the mechanical properties and the microstructure is also performed. Results indicate that transgranular fracture was the primary mode of failure in this boron carbide material, and no stress-induced amorphization features were observed. Analysis of the fragment sizes for the partial and completely penetrated experiments revealed a possible correlation between larger fragment sizes and impact performance. The results will add insight into designing improved advanced ceramics for impact protection applications.

  12. Characterization and Formability of Titanium/Aluminum Laminate Composites Fabricated by Hot Pressing

    Science.gov (United States)

    Qin, Liang; Wang, Hui; Cui, Shengqiang; Wu, Qian; Fan, Minyu; Yang, Zonghui; Tao, Jie

    2017-07-01

    The Ti/Al laminate composites were prepared by hot pressing to investigate the forming performance due to the corresponding potential applications in both the aerospace and auto industry. The bonding interface morphology and element distributions were characterized by SEM and EDS. The phase constituent was detected by XRD. It was observed that these composites presented good bonding interfaces between Ti and Al layers, and no low-sized voids and intermetallic compounds formed at the interface. In addition, the formability of these laminate composites was studied by the uniaxial tension tests, the limit drawing ratio (LDR) and the forming limit curve (FLC) experiments, respectively. The results indicated that the flow stress increased along with the strain rate increment. A constitutive equation was developed for deformation behavioral description of these laminate composites. The LDR value was 1.8, and the most susceptible region to present cracks was located at the punch profile radius. The forming limit curve of the laminate composites was located between the curves of titanium and aluminum and intersected with the major strain line at approximately 0.31. The macroscopic cracks of the FLC sample demonstrated a saw-toothed crack feature.

  13. Hot-pressed silicon nitride with various lanthanide oxides as sintering additives

    Science.gov (United States)

    Ueno, K.; Toibana, Y.

    1984-01-01

    The effects of addition of various lanthanide oxides and their mixture with Y2O3 on the sintering of Si3N4 were investigated. The addition of simple and mixed lanthanide oxides promoted the densification of Si3N4 in hot-pressing at 1800 C under 300-400kg/ centimeters squared for 60 min. The crystallization of yttrium and lanthanide-silicon oxynitrides which was observed inn the sintered body containing yttrium-lanthanide mixed oxides as additives led to the formation of a highly refractory Si3N4 ceramic having a bending strength of 82 and 84 kg/millimeters squared at room temperature and 1300 C respectively. In a Y2O3+La2O3 system, a higher molar ratio of La2O3 to Y2O3 gave a higher hardness and strength at high temperatures. It was found that 90 min was an optimum sintering time for the highest strength.

  14. Effect of pressing temperature on the wear resistance of a Co-based Cr-Mo powder alloy produced by hot pressing

    Energy Technology Data Exchange (ETDEWEB)

    Somunkiran, Ilyas [Firat Univ., Elazig (Turkey). Metallurgical and Materials Engineering Dept.; Balin, Ahmet [Siirt Univ. (Turkey). Dept. of Vocational High School

    2016-02-01

    In this study, Co-based Cr-Mo powder alloy was produced at different pressing temperatures by using hot pressing technique and abrasive wear behaviors of the produced specimens were examined. Produced specimens were exposed to abrasive wear experiment using block on disc wear test device by applying a load of 50 N with 100-mesh SiC abrasive paper. Each specimen was investigated at 25, 50, 75 and 100 m. At the end of the experiment, abrasive wear results of the specimens were determined by calculating their mass losses. Microstructural properties of the specimens which were produced at different pressing temperatures were investigated by optical and SEM examinations and their wear resistances were examined by abrasive wear experiments. Consequently, it was observed that in Co-based Cr-Mo powder alloy produced by hot pressing technique; as sintering temperature increased, size of neck formations between the powder grains increased, porosity decreased and abrasive wear resistance increased. [German] In diesem Beitrag zugrunde liegenden Studie wurde eine Co-basierte Cr-Mo-Legierung mittels Heisspressens hergestellt und der Abrasivverschleisswiderstand dieser Proben untersucht. Die hergestellten Proben wurden dem Abrasivverschleissversuch durch einen Block-Scheibe-Versuchsaufbau unterzogen, wobei eine Kraft von 50 N mit einem SiC-Papier (100 mesh) verwendet wurde. Jede Probe wurde ueber eine Distanz von 25, 50, 75 und 100 m untersucht. Am Ende der jeweiligen Experimente wurden die Abrasivverschleissergebnisse ermittelt, indem die Massenverluste berechnet wurden. Die mikrostrukturellen Eigenschaften der Proben, die bei verschiedenen Presstemperaturen hergestellt wurden, wurden mittels optischer und Rasterelektronenmikroskopie bestimmt und ihr Verschleisswiderstand anhand der Verschleissversuche ermittelt. Schliesslich wurde beobachtet, dass bei steigender Sintertemperatur der heissgespressten Co-basierten Cr-Mo-Pulverlegierung die Groesse der Einschnuerungen zwischen den

  15. The effect of hot pressing time on the microstructure and properties of Laves phase NbCr{sub 2} alloys

    Energy Technology Data Exchange (ETDEWEB)

    Xiao, X. [College of Electromechanical Engineering, Nanjing University of Aeronautical and Astronautics, Nanjing 210016 (China); School of Materials Science and Engineering, Nanchang Institute of Aeronautical Technology, Nanchang 330063 (China); Lu, S.Q. [School of Materials Science and Engineering, Nanchang Institute of Aeronautical Technology, Nanchang 330063 (China)], E-mail: niatlusq@126.com; Hu, P.; Huang, M.G.; Nie, X.W. [School of Materials Science and Engineering, Nanchang Institute of Aeronautical Technology, Nanchang 330063 (China); Fu, M.W. [Department of Mechanical Engineering, Hong Kong Polytechnic University, Hung Hom, Kowloon, Hong Kong (China)

    2008-06-25

    The microstructure and properties were investigated on the Laves phase NbCr{sub 2} alloys prepared through 20 h mechanical alloying of niobium and chromium powders and subsequent hot pressing at 1250 deg. C for different time. The results indicate that the Laves phase NbCr{sub 2} alloy with homogeneous microstructure and fine grains and high relative density is obtained. With the increase of hot pressing time, the density, grain size and Vickers hardness increase, the fracture toughness, however, decreases gradually. The alloy fabricated by hot pressing at 1250 deg. C for 30 min has the best overall properties. Its average grain size reaches about 248 nm, the relative density is 97.8% and the fracture toughness at room temperature is more than 4.7 MPa m{sup 1/2}. Compared with the Laves phase NbCr{sub 2} alloy prepared by arc-melting, which has the fracture toughness of 1.2 MPa m{sup 1/2}, the fracture toughness in this research is increased significantly.

  16. Preparation of 50Ni-45Ti-5Zr powders by high-energy ball milling and hot pressing

    Energy Technology Data Exchange (ETDEWEB)

    Marinzeck de Alcantara Abdala, Julia, E-mail: juabdala@yahoo.com.b [Instituto de Pesquisa e Desenvolvimento, Universidade do Vale do Paraiba, Av. Shishima Hifumi, 2911, 12244-000 Sao Jose dos Campos (Brazil); Bacci Fernandes, Bruno, E-mail: brunobacci@yahoo.com.b [Divisao de Engenharia Mecanica, Instituto Tecnologico de Aeronautica, Praca Marechal-do-Ar Eduardo Gomes, 50, 12228-904 Sao Jose dos Campos (Brazil); Santos, Dalcy Roberto dos, E-mail: dalcy@iae.cta.b [Instituto de Aeronautica e Espaco, Centro Tecnologico Aeroespacial, Praca Marechal-do-Ar Eduardo Gomes, 50, 12228-904 Sao Jose dos Campos (Brazil); Rodrigues Henriques, Vinicius Andre, E-mail: vinicius@iae.cta.b [Instituto de Aeronautica e Espaco, Centro Tecnologico Aeroespacial, Praca Marechal-do-Ar Eduardo Gomes, 50, 12228-904 Sao Jose dos Campos (Brazil); Moura Neto, Carlos de, E-mail: mneto@ita.b [Divisao de Engenharia Mecanica, Instituto Tecnologico de Aeronautica, Praca Marechal-do-Ar Eduardo Gomes, 50, 12228-904 Sao Jose dos Campos (Brazil); Saraiva Ramos, Alfeu, E-mail: alfeu@univap.b [Instituto de Pesquisa e Desenvolvimento, Universidade do Vale do Paraiba, Av. Shishima Hifumi, 2911, 12244-000 Sao Jose dos Campos (Brazil)

    2010-04-16

    This study reports on the preparation of the 50Ni-45Ti-5Zr (at.%) alloy by high-energy ball milling and hot pressing. The elemental powder mixture was processed in silicon nitride and hardened steel vials, and samples were collected after different milling times. To recover the previous powders in addition wet milling isopropyl alcohol (for 20 min) was adopted. The mechanically alloyed powders were hot-pressed under vacuum at 900 {sup o}C for 1 h using pressure levels close to 200 MPa. The milled powders were characterized by means of scanning electron microscopy, X-ray diffraction, and energy dispersive spectrometry techniques. It was noted that the ductile starting powders were continuously cold-welded during ball milling. This fact was more pronounced during the processing of 50Ni-45Ti-5Zr powders in hardened steel vial. After milling for 5 h, the results suggested that amorphous and nanocrystalline structures were achieved. The complete consolidation was found after hot pressing of mechanically alloyed 50Ni-45Ti-5Zr powders, and a large amount of the B2-NiTi phase was formed mainly after processing in stainless steel balls and vial.

  17. Reduction of adhesive stain defect in flexible printed circuit board on hot pressing process: A case study of electronic component factory

    Directory of Open Access Journals (Sweden)

    Sakulkaew Srisang

    2015-03-01

    Full Text Available The objective of this research is a reduction of an adhesive stain defect in flexible printed circuit board in hot pressing process, the electronic factory. The manufacturing have been processing by sheet type of products with ninety-six pieces of flexible printed circuit boards. Causes of the problem include the before and internal hot pressing process. In process beginning times, the most right row of products between the cooling plate and the hot pressing machine has temperature 71.2◦C that is higher than glass transition temperature (Tg 60◦C. Those products’ temperature lead to evaporate a polyimide adhesive before hot pressing process beginning. The internal hot pressing process include the preheat times and the pressure time. In the preheat time the problem is a gap between lower and upper plate, was under specification (Under 1 mm and leaded to adhesive polyimide stain. In the actuality this time requires temperature and low pressure that mean a gap within 1 – 2 mm (between lower and upper plate. In pressure times the hot pressing plate surface is not flat and products are pressed by insufficient force that it lead to generate an adhesive stain on flexible printed circuit boards. That force is measured by the pre-scale paper and a result, RGB color, is provided. And then color density (From standard color sample and RGB color (From pre-scale paper is found out the relation by Photoshop program and multiple regression theory using. The formula is applied to compare with defect so as to find out the suitable color density (Defects reducing. The solving solutions is provided including the gap reduced adjustment between cooling plate and hot pressing machine before hot pressing process, the plate adjustment within specification in the preheat time and the pressing plate polishing in the pressure time. Results of study and solving are provide defect reduction from 24.4 percentage to 7.2 percentage of total study product.

  18. Hot working alkali halides for laser window applications

    International Nuclear Information System (INIS)

    Koepke, B.G.; Anderson, R.H.; Stokes, R.J.

    1975-01-01

    The techniques used to hot work alkali halide crystals into laser window blanks are reviewed. From the point of view of high power laser window applications one of the materials with a high figure of merit is KCl. Thus the materials examined are KCl and alloys of KCl-KBr containing 5 mole percent KBr. The fabrication techniques include conventional and constrained press forging, isostatic press forging and hot rolling. Optical properties are paramount to the ultimate usefulness of these materials. Results on the optical properties of the hot worked material are included together with mechanical properties and microstructural data

  19. Effect of deformation ratios on grain alignment and magnetic properties of hot pressing/hot deformation Nd-Fe-B magnets

    Science.gov (United States)

    Guo, Zhaohui; Li, Mengyu; Wang, Junming; Jing, Zheng; Yue, Ming; Zhu, Minggang; Li, Wei

    2018-05-01

    The magnetic properties, microstructure and orientation degrees of hot pressing magnet and hot deformation Nd-Fe-B magnets with different deformation ratios have been investigated in this paper. The remanence (Br) and maximum magnetic energy product ((BH)max) were enhanced gradually with the deformation ratio increasing from 0% to 70%, whereas the coercivity (HCj) decreased. The scanning electron microscopy (SEM) images of fractured surfaces parallel to the pressure direction during hot deformation show that the grains tend to extend perpendicularly to the c-axes of Nd2Fe14B grains under the pressure, and the aspect ratios of the grains increase with the increase of deformation ratio. Besides, the compression stress induces the long axis of grains to rotate and the angle (θ) between c-axis and pressure direction decreases. The X-ray diffraction (XRD) patterns reveal that orientation degree improves with the increase of deformation ratio, agreeing well with the SEM results. The hot deformation magnet with a deformation ratio of 70% has the best Br and (BH)max, and the magnetic properties are as followed: Br=1.40 T, HCj=10.73 kOe, (BH)max=42.30 MGOe.

  20. Microstructure and mechanical properties of Ti–22Al–25Nb alloy fabricated by vacuum hot pressing sintering

    Energy Technology Data Exchange (ETDEWEB)

    Jia, Jianbo, E-mail: jiajianbohit@163.com [National Key Laboratory for Precision Hot Processing of Metals, Harbin Institute of Technology, Harbin 150001 (China); School of Mechanical Engineering, Beihua University, Jilin 132021 (China); Zhang, Kaifeng; Jiang, Shaosong [National Key Laboratory for Precision Hot Processing of Metals, Harbin Institute of Technology, Harbin 150001 (China)

    2014-10-20

    A study has been undertaken to verify the feasibility of using a powder metallurgy (P/M) approach to fabricate Ti–22Al–25Nb alloys. Pre-alloyed powders with a nominal composition of Ti–22Al–25Nb (at%) obtained by argon atomization were sieved to the spherical size less than 180 μm and used for the fabrication of P/M Ti–22Al–25Nb alloys via hot pressing in vacuum. Vacuum hot pressing sintering was carried out in a temperature range of 950–1200 °C with a pressure of 35 MPa for 1 h followed by furnace cooling. Microstructure and phase composition examinations of the as-atomized powders and hot pressed (HP'ed) samples were conducted by applying optical microscopy, back-scatter electron imaging and X-ray diffraction analysis. Tensile tests were studied at room temperature and 650 °C, respectively. The results showed that all HP'ed samples were composed of coarse equiaxed B2 grains, fine lamellar O phase inside the B2 grains, and some α{sub 2} along B2 grain boundaries. The elongations of HP'ed samples were less than 3.95%, indicating the bad ductility at room temperature. However, the elongations were improved as the tensile temperature increased to 650 °C. The sample sintered at 1050 °C exhibited a better ductility with the elongation of 7.97% at 650 °C than that of other samples.

  1. Effect of surface acid etching on the biaxial flexural strength of two hot-pressed glass ceramics.

    Science.gov (United States)

    Hooshmand, Tabassom; Parvizi, Shaghayegh; Keshvad, Alireza

    2008-07-01

    The purpose of this study was to assess the effect of surface acid etching on the biaxial flexural strength of two hot-pressed glass ceramics reinforced by leucite or lithium disilicate crystals. Forty glass ceramic disks (14-mm diameter, 2-mm thick) consisting of 20 leucite-based ceramic disks (IPS Empress) and 20 lithia disilicate-based ceramic (IPS Empress 2) were produced by hot-pressing technique. All specimens were polished and then cleaned ultrasonically in distilled water. Ten specimens of each ceramic group were then etched with 9% hydrofluoric (HF) acid gel for 2 minutes and cleaned ultrasonically again. The biaxial flexural strength was measured by the piston-on-three-ball test in a universal testing machine. Data based on ten specimens in each group were analyzed by two-way ANOVA (alpha= 0.05). Microstructure of ceramic surfaces before and after acid etching was also examined by a scanning electron microscope. The mean biaxial flexural strength values for each group tested were (in MPa): nonetched IPS Empress = 118.6 +/- 25.5; etched IPS Empress = 102.9 +/- 15.4; nonetched IPS Empress 2 = 283.0 +/- 48.5; and etched IPS Empress 2 = 250.6 +/- 34.6. The results showed that the etching process reduced the biaxial flexural strengths significantly for both ceramic types (p= 0.025). No significant interaction between the ceramic type and etching process was found (p= 0.407). From the results, it was concluded that surface HF acid etching could have a weakening effect on hot-pressed leucite or lithia disilicate-based glass ceramic systems.

  2. The effect of hot isostatic pressing on the microstructure and tensile properties of an unmodified A356-T6 cast aluminum alloy

    International Nuclear Information System (INIS)

    Ran Guang; Zhou Jingen; Wang, Q.G.

    2006-01-01

    In this paper, the effect of HIPping process on the microstructure and tensile properties of an unmodified sand cast A356-T6 aluminum alloy was studied. The microstructure and tensile fracture surfaces of the alloy were examined by transmission electron microscope (TEM), scanning electron microscope (SEM) and optical microscope. The results show that sub-grain boundaries are formed by HIPping process, and some silicon precipitates are formed at the sub-grain boundaries during aging hardening. The needle-shape precipitates are Mg 2 Si particles according to SED pattern analysis. The lattice misfit between Mg 2 Si and aluminum matrix is about 0.256% for [111] Al //[410] Mg 2 Si HIPping process significantly reduces porosity volume fraction and pore sizes and thus improves ductility. However, the tensile strength is improved very marginally due to the brittle nature of the unmodified coarse microstructure. The sub-grain boundary formed in the HIPping process has not shown significant influence on the tensile properties. For the studied alloy with large secondary dendrite arm spacing (SDAS) (above 80μm), the tensile fracture exhibits a transgranular mode (along the cell boundaries) with quasi-cleavage feature

  3. HIP (hot isostatic pressing) sintering of Tantalum (Ta) and tantalum carbide (TaC) powder mixture: relations between microstructure and properties

    International Nuclear Information System (INIS)

    Valin, F.; Schnedecker, M.

    1994-01-01

    HIP sintering at 1630 C and 195 MPa, during 2 hours, can be used for complete densification of mixtures of commercial tantalum carbide and tantalum powders. HIPed material properties are depending upon initial compositions. For C/Ta ratios inferior to 80%, the monocarbide structure is preserved. A partial ordering of the carbon vacancies will result, for TaC(0.80), in microhardness maximization. The microstructurally homogenous TaC(0.45) shows an excellent toughness. 2 figs., 2 refs

  4. Effect of zirconium addition on the microstructure and mechanical properties of 15Cr-ODS ferritic Steels consolidated by hot isostatic pressing

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Haijian, E-mail: haijianxu@eis.hokudai.ac.jp [Key Laboratory for Anisotropy and Texture of Materials, Ministry of Education, Northeastern University, Shenyang 110819 (China); Material Science and Engineering, Faculty of Engineering, Hokkaido University, Sapporo 060-8628 (Japan); Lu, Zheng; Wang, Dongmei; Liu, Chunming [Key Laboratory for Anisotropy and Texture of Materials, Ministry of Education, Northeastern University, Shenyang 110819 (China)

    2017-01-15

    The influence of Zr addition on the microstructure and mechanical properties of mechanically alloyed (MA) ODS ferritic steels were studied in this work. The microstructure characteristics included the grain size, oxide particles number densities, size distributions, crystal structures and compositions. TEM foils measurements were complemented by studies of alloys on carbon extraction replica and focus ion beam (FIB) foils. The tensile properties were carried out at different temperatures. The microstructure and mechanical properties were analyzed and compared with nominal compositions (wt.%): Fe-15Cr-2W-0.3Y{sub 2}O{sub 3} and Fe-15Cr −2W-0.3Zr-0.3Y{sub 2}O{sub 3}. The experimental revealed that the addition of Zr increased the volume fraction of the smallest and equiaxed ferritic grains, number density of nano-oxide particles and decreased the average size of oxide particles within the ferritic matrix, promoting the formation of fine trigonal δ-phase Y{sub 4}Zr{sub 3}O{sub 12} nano-oxides and leading to the enhancement of the mechanical properties of the ODS steels.

  5. Fabrication of Polycrystalline Transparent Co+2: MgAl2O4 by a Combination of Spark Plasma Sintering (SPS and Hot Isostatic Pressing (HIP Processes

    Directory of Open Access Journals (Sweden)

    Sokol Maxim

    2017-01-01

    Full Text Available Transparent Co2+ doped MgAl2Ob4 spinel was fabricated by SPS consolidation followed by and HIP treatment. It was established that HIP treatment significantly improved transparency of the ceramic in a wide range of wavelengths, especially, in a range, which is relevant for Q-switching. Nonlinear absorption was demonstrated and the ground and excited state absorption cross sections were estimated. The positive effect of the HIP treatment on the optical properties is related to an elimination of extremely fine porosity and to the location of Co ions at Mg2+sites in the spinel ionic structure. The experimental results indicate that the fabricated specimens can be used as a passive laser Q-switching material.

  6. Investigation of the High-Cycle Fatigue Life of Selective Laser Melted and Hot Isostatically Pressed Ti-6Al-4v

    Science.gov (United States)

    2015-03-26

    marketed for production of parts with metal alloys: electron-beam melting and laser sintering (LS) [3, 10, 36]. The primary distinction between EBM and LS...staircase method described in ASTM STP 588 [68]. The first specimen in a staircase test is tested at a maximum stress level corresponding to the

  7. Hot pressing and lithification of gouge during the Mount St. Helens 2004-2008 eruption: insights from high temperature deformation experiments

    Science.gov (United States)

    Ryan, Amy G.; Russell, James K.; Heap, Michael J.

    2017-04-01

    and 850°C. This change in axial strain-time curves with increasing T suggests the inclusion of a second densification process, aside from mechanical compaction, at elevated T. It is our hypothesis that solid-state sintering, a process wherein crystalline particles are fused together as a result of atomic diffusion across grain boundaries (i.e., the process occurring during the industrial production of ceramics by hot (isostatic) pressing), is the dominant mechanism operating at high T and under pressure. While viscous sintering (i.e. welding) operates in many "melt-glass-rich" volcanic systems, solid-state sintering has yet to be explored as a densification mechanism operating on fine granular crystalline volcanic materials at conditions and timescales relevant to volcanic processes.

  8. Importance of Electrode Hot-Pressing Conditions for the Catalyst Performance of Proton Exchange Membrane Fuel Cells

    DEFF Research Database (Denmark)

    Andersen, Shuang Ma; Dhiman, Rajnish; Larsen, Mikkel Juul

    2015-01-01

    The catalyst performance in a proton exchange membrane fuel cell (PEMFC) depends on not only the choice of materials, but also on the electrode structure and in particular on the interface between the components. In this work, we demonstrate that the hot-pressing conditions used during electrode...... lamination have a great influence on the catalyst properties of a low-temperature PEMFC, especially on its durability. Lamination pressure, temperature and duration were systematically studied in relation to the electrochemical surface area, platinum dissolution, platinum particle size and electrode surface...

  9. Thermoelectric properties of Bi2Te3-Bi2Se3 solid solutions prepared by attrition milling and hot pressing

    International Nuclear Information System (INIS)

    Lee, Go-Eun; Kim, Il-Ho; Choi, Soon-Mok; Lim, Young-Soo; Seo, Won-Seon; Park, Jae-Soung; Yang, Seung-Ho

    2014-01-01

    Bi 2 Te 3-y Se y (y = 0.15 - 0.6) solid solutions were prepared by attrition milling and hot pressing. The lattice constants decreased with increasing Se content, indicating that the Se atoms were successfully substituted into the Te sites. All specimens exhibited n-type conduction, and their electrical resistivities increased slightly with increasing temperature. With increasing Se content, the Seebeck coefficients increased while the thermal conductivity decreased due to the increase in phonon scattering. The maximum figure of merit obtained was 0.63 at 440 K for the undoped Bi 2 Te 2.4 Se 0.6 solid solution.

  10. Nevada Isostatic Gravity Grid

    Data.gov (United States)

    National Oceanic and Atmospheric Administration, Department of Commerce — A 2 kilometer Isostatic anomaly grid for the state of Nevada. Number of columns is 269 and number of rows is 394. The order of the data is from the lower left to the...

  11. Biodegradable Poly(Lactic Acid/Multiwalled Carbon Nanotube Nanocomposite Fabrication Using Casting And Hot Press Techniques

    Directory of Open Access Journals (Sweden)

    Park S.G.

    2015-06-01

    Full Text Available Biodegradable advanced polymer composites have recently received a large amount of attention. The present study aimed to design poly(lactic acid multiwalled carbon nanotube nanocomposites (PLA/MWCNTs using a simple fabrication technique. A PLA sheet was first dissolved in dichloromethane, and MWCNTs were subsequently added at various concentrations (0.5, 1.5 and 5% while applying shear strain stirring to achieve dispersion of carbon nanotubes (CNTs. These solutions were then molded and a hot press was used to generate sheets free of voids with entrapped solvent. The prepared samples were characterized using field emission scanning electron microscopy (FE-SEM, x-ray diffraction (XRD, Fourier transform infrared spectroscopy (FTIR, and thermogravimetric analysis (TGA. Our data showed composite samples free of defects and voids, indicating that the hot press is capable of generating sufficiently compact polymer matrices. Additionally, TGA and FTIR showed significant bonding interactions between the PLA matrix and the nano-fillers. Collectively, our results suggest that incorporation of CNTs as nano-fillers into biodegradable polymers may have multiple applications in many different sectors.

  12. Influence of Sintering Temperature on the Microstructure and Mechanical Properties of In Situ Reinforced Titanium Composites by Inductive Hot Pressing

    Directory of Open Access Journals (Sweden)

    Cristina Arévalo

    2016-11-01

    Full Text Available This research is focused on the influence of processing temperature on titanium matrix composites reinforced through Ti, Al, and B4C reactions. In order to investigate the effect of Ti-Al based intermetallic compounds on the properties of the composites, aluminum powder was incorporated into the starting materials. In this way, in situ TixAly were expected to form as well as TiB and TiC. The specimens were fabricated by the powder metallurgy technique known as inductive hot pressing (iHP, using a temperature range between 900 °C and 1400 °C, at 40 MPa for 5 min. Raising the inductive hot pressing temperature may affect the microstructure and properties of the composites. Consequently, the variations of the reinforcing phases were investigated. X-ray diffraction, microstructural analysis, and mechanical properties (Young’s modulus and hardness of the specimens were carried out to evaluate and determine the significant influence of the processing temperature on the behavior of the composites.

  13. Investigation of a hot-pressed Nb–Ti–Al alloy: Mechanical alloying, microstructure and mechanical property

    Energy Technology Data Exchange (ETDEWEB)

    Shi, Zhiwu; Wei, Hua; Zhang, Hongyu; Jin, Tao; Sun, Xiaofeng; Zheng, Qi, E-mail: qzheng@imr.ac.cn

    2016-01-10

    The Nb–23Ti–15Al (at%) alloy was prepared by mechanical alloying (MA) and hot-pressing (HPing). The microstructure evolution of powder particles during MA and its influence on the microstructure and mechanical properties of the hot-pressed (HPed) alloy have been investigated. The powder and HPed alloy were characterized via X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results indicate that particle size increases in the first stage and then decreases in the second stage during MA; as milling speed increases, mechanically alloyed (MAed) powder with convoluted elemental lamellae, homogeneous Nb solid-solution and an amorphous phase could be obtained respectively in 24 h. Higher homogeneity in microstructure and composition of the MAed powder particles promotes the precipitation of the δ phase and refines the β and Ti(O,C) phases in the HPed alloy. Moreover, due to the phase equilibrium changes caused by Fe and Cr in the amorphous powder, σ phase appears in the alloy as a stable phase instead of the δ phase. Properly MAed powder contributes to higher hardness of the HPed alloy, for reasons of microstructure refinement and sufficient precipitating of strengthening phases.

  14. Investigation of a hot-pressed Nb–Ti–Al alloy: Mechanical alloying, microstructure and mechanical property

    International Nuclear Information System (INIS)

    Shi, Zhiwu; Wei, Hua; Zhang, Hongyu; Jin, Tao; Sun, Xiaofeng; Zheng, Qi

    2016-01-01

    The Nb–23Ti–15Al (at%) alloy was prepared by mechanical alloying (MA) and hot-pressing (HPing). The microstructure evolution of powder particles during MA and its influence on the microstructure and mechanical properties of the hot-pressed (HPed) alloy have been investigated. The powder and HPed alloy were characterized via X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results indicate that particle size increases in the first stage and then decreases in the second stage during MA; as milling speed increases, mechanically alloyed (MAed) powder with convoluted elemental lamellae, homogeneous Nb solid-solution and an amorphous phase could be obtained respectively in 24 h. Higher homogeneity in microstructure and composition of the MAed powder particles promotes the precipitation of the δ phase and refines the β and Ti(O,C) phases in the HPed alloy. Moreover, due to the phase equilibrium changes caused by Fe and Cr in the amorphous powder, σ phase appears in the alloy as a stable phase instead of the δ phase. Properly MAed powder contributes to higher hardness of the HPed alloy, for reasons of microstructure refinement and sufficient precipitating of strengthening phases.

  15. Microstructure, mechanical and tribological behavior of hot-pressed mechanically alloyed Al–Zn–Mg–Cu powders

    International Nuclear Information System (INIS)

    Azimi, A.; Fallahdoost, H.; Nejadseyfi, O.

    2015-01-01

    Highlights: • Nanocrystalline Al7050 alloy was synthesized by mechanical alloying. • Longer milling time led to increasing porosity in hot-pressed samples. • Significant improvement in strength and wear resistance was obtained by increasing the milling time up to 40 h. - Abstract: This research focuses on the preparation of Al7050 alloy via mechanical alloying and hot pressing techniques. The effect of milling time on the microstructure and densification response was investigated by X-ray diffraction (XRD) and scanning electron microscope (SEM). Furthermore, the mechanical properties of the samples including microhardness, compression strength, and wear resistance were examined as a function of milling time. The results of the experiments proved that by increasing the milling time the crystallite size was reduced, which has a significant effect on improving the mechanical properties. In addition, porosity formation increased when the milling time was increased due to reduction of the compressibility of finer particles. By increasing the milling time to more than 40 h, a relatively invariable crystallite size was obtained and it was observed that the porosities expanded in the samples. Therefore, the compressive strength, hardness, and wear resistance were enhanced up to 40 h milling time and then the strengthening effect was relatively diminished. On observing surfaces with SEM, the dominant wear mechanism was recognized as abrasion, delamination and adhesion

  16. Improvement of linerboard compressive strength by hot-pressing and addition of recovered lignin from spent pulping liquor

    Directory of Open Access Journals (Sweden)

    Saidan Motasem N.

    2015-01-01

    Full Text Available This paper evaluates the effect of addition of precipitated lignin, from spent pulping black liquor, to a wet single-ply linerboard handsheet followed by hot-pressing at different temperatures, on the improvement of its compressive strength. Linerboard handsheets for testing the effect of lignin addition were prepared so that the lignin-modified sheets would have the same basis weights as the control handsheets. Both the commercial and the black liquor lignin were added as a powder to wet handsheets after couching from the handsheet mold. The experiments and testing of the physical and strength properties of dried handsheets were conducted according to TAPPI test methods. The results revealed that the addition of the recovered lignin (at pH of 2 to the wet handsheet followed by hot-pressing at 150°C increased the compressive strength of linerboard handsheets by 10% to 20% above that for handsheets made without the addition of lignin. The same results were achieved using purchased lignin. However, with a 16% addition to linerboard, purchased lignin would be too expensive. These results indicate that inclusion of kraft lignin in linerboard sheets could be proved as an attractive option to reduce linerboard basis weight.

  17. Microstructures and mechanical properties of Fe-28Al-5Cr/TiC composites produced by hot-pressing sintering

    International Nuclear Information System (INIS)

    Zhang Xinghua; Yang Jun; Ma Jiqiang; Bi Qinling; Cheng Jun; Liang Yongmin; Liu Weimin

    2011-01-01

    Highlights: → The near fully dense Fe-28Al-5Cr/TiC composites are produced by hot-pressing sintering. → All the materials exhibit high compressive and bending strength. → Compressive strength increases but bending strength and ductility diminish with rising TiC amount in the composites. → Wear resistance significantly increases with rising TiC amount. - Abstract: The mechanical properties and microstructures of Fe-28Al-5Cr based composites reinforced with 15, 25, 35, 50 wt.% TiC ceramic particle, produced by hot-pressing sintering method, were investigated. The relative density of all the composites was up to 99%. The distribution of TiC was uniform in the composites. Results of XRD analysis showed that the composites were composed of TiC and disorder Fe 3 Al phases. All the materials exhibited very high strength of 1200-2000 MPa. The hardness and compressive strength of the composites increased obviously but compressive strain decreased gradually except 50% composite with increasing TiC content. The bending strength and deflection of the composites decreased significantly with increasing TiC content. The bending fracture surfaces of all the materials were examined using scanning electron microscopy (SEM). The fracture mode transformed gradually from tough dimple fracture mode to brittle cleavage facets crack mode with the increase of TiC content. Wear resistance of the Fe-28Al-5Cr alloy was also significantly improved by addition of TiC.

  18. Silver as a highly effective bonding layer for lead telluride thermoelectric modules assembled by rapid hot-pressing

    International Nuclear Information System (INIS)

    Li, C.C.; Drymiotis, F.; Liao, L.L.; Dai, M.J.; Liu, C.K.; Chen, C.L.; Chen, Y.Y.; Kao, C.R.; Snyder, G.J.

    2015-01-01

    Highlights: • Ag serves as a promising bonding material for PbTe operating at T Hot ⩽ 400 °C. • The Ag foils reacted vigorously with PbTe to form Ag 2 Te at 550 °C. • The Seebeck coefficient of Ag/PbTe/Ag is slightly higher than that of pure PbTe. • A cost-effective way for long-term operations at high temperature. - Abstract: We use the rapid hot-pressing method to bond Ag foil onto pure PbTe in order to assess its effectiveness as a bonding layer material for thermoelectric module applications. Scanning electron microscopy and X-ray diffraction are employed to examine intermetallic compound formation and microstructure evolution during isothermal aging at 400 °C and 550 °C. We find that Ag is a promising bonding material for PbTe modules operating at T Hot ⩽ 400 °C. Additionally, our approach highlights a highly effective and inexpensive method to metallize PbTe prior to module assembly

  19. Microstructure, hardness, corrosion resistance and porcelain shear bond strength comparison between cast and hot pressed CoCrMo alloy for metal-ceramic dental restorations.

    Science.gov (United States)

    Henriques, B; Soares, D; Silva, F S

    2012-08-01

    The purpose of this study was to compare the microstructure, hardness, corrosion resistance and metal-porcelain bond strength of a CoCrMo dental alloy obtained by two routes, cast and hot pressing. CoCrMo alloy substrates were obtained by casting and hot pressing. Substrates' microstructure was examined by the means of Optical Microscopy (OM) and by Scanning Electron Microscope (SEM) and Energy Dispersive X-ray Spectroscopy (EDS). Hardness tests were performed in a microhardness indenter. The electrochemical behavior of substrates was investigated through potentiodynamic tests in a saline solution (8g NaCl/L). Substrates were bonded to dental porcelain and metal-porcelain bond strength was assessed by the means of a shear test performed in a universal test machine (crosshead speed: 0.5 mm/min) until fracture. Fractured surfaces as well as undestroyed interface specimens were examined with Stereomicroscopy and SEM-EDS. Data was analyzed with Shapiro-Wilk test to test the assumption of normality. The t-test (pmicrostructures whereas hot pressed specimens exhibited a typical globular microstructure with a second phase spread through the matrix. The hardness registered for hot pressed substrates was greater than that of cast specimens, 438±24HV/1 and 324±8HV/1, respectively. Hot pressed substrates showed better corrosion properties than cast ones, i.e. higher OCP; higher corrosion potential (E(corr)) and lower current densities (i(corr)). No significant difference was found (p<0.05) in metal-ceramic bond strength between cast (116.5±6.9 MPa) and hot pressed (114.2±11.9 MPa) substrates. The failure type analysis revealed an adhesive failure for all specimens. Hot pressed products arise as an alternative to cast products in dental prosthetics, as they impart enhanced mechanical and electrochemical properties to prostheses without compromising the metal-ceramic bond strength. Copyright © 2012 Elsevier Ltd. All rights reserved.

  20. 'Ye Olde Hot Aire' : reporting on human contributions to climate change in the UK tabloid press

    International Nuclear Information System (INIS)

    Boykoff, Maxwell T; Mansfield, Maria

    2008-01-01

    This letter explores daily print media coverage of climate change in four United Kingdom (UK) tabloid newspapers: The Sun (and News of the World), Daily Mail (and Mail on Sunday), the Daily Express (and Sunday Express), and the Mirror (and Sunday Mirror). Through examinations of content in articles over the last seven years (2000-2006), triangulated with semi-structured interviews of journalists and editors, the study finds that UK tabloid coverage significantly diverged from the scientific consensus that humans contribute to climate change. Moreover, there was no consistent increase in the percentage of accurate coverage throughout the period of analysis and across all tabloid newspapers, and these findings are not consistent with recent trends documented in United States and UK 'prestige press' or broadsheet newspaper reporting. Findings from interviews indicate that inaccurate reporting may be linked to the lack of specialist journalists in the tabloid press. This study therefore contributes to wider discussions of socio-economic inequality, media and the environment. Looking to newspapers that are consumed by typically working class readership, this article contributes to ongoing investigations related to what media representations mean for ongoing science-policy interactions as well as potentialities for public engagement

  1. Reduction of adhesive stain defect in flexible printed circuit board on hot pressing process: a case study of electronic component factory

    Directory of Open Access Journals (Sweden)

    Sakulkaew Srisang

    2014-09-01

    Full Text Available The objective of this research is a reduction of an adhesive stain defect in flexible printed circuit board in hot pressing process, the electronic factory. The manufacturing have been processing by sheet type of products with ninety-six pieces of flexible printed circuit boards. Causes of the problem include the before and internal hot pressing process. In process beginning times, the most right row of products between the cooling plate and the hot pressing machine has temperature 71.2◦C that is higher than glass transition temperature (Tg 60◦C. Those products’ temperature lead to evaporate a polyimide adhesive before hot pressing process beginning. The internal hot pressing process include the preheat times and the pressure time. In the preheat time the problem is a gap between lower and upper plate, was under specification(Under 1 mm and leaded to adhesive polyimide stain. In the actuality this time requires temperature and low pressure that mean a gap within 1 – 2 mm (between lower and upper plate. In pressure times the hot pressing plate surface is not flat and products are pressed by insufficient force that it lead to generate an adhesive stain on flexible printed circuit boards. That force is measured by the pre-scale paper and a result, RGB color, is provided. And then color density (From standard color sample and RGB color (From pre-scale paper is found out the relation by Photoshop program and multiple regression theory using. The formula is applied to compare with defect so as to find out the suitable color density (Defects reducing. The solving solutions is provided including the gap reduced adjustment between cooling plate and hot pressing machine before hot pressing process, the plate adjustment within specification in the preheat time and the pressing plate polishing in the pressure time. Results of study and solving are provide defect reduction from 24.4 percentage to 7.2 percentage of total study product.

  2. Fractographical characterization of hot pressed and pressureless sintered AlN-doped ZrB{sub 2}–SiC composites

    Energy Technology Data Exchange (ETDEWEB)

    Ahmadi, Zohre [Department of Materials Engineering, Faculty of Mechanical Engineering, University of Tabriz, Tabriz (Iran, Islamic Republic of); Nayebi, Behzad [School of Materials and Metallurgy Engineering, Iran University of Science and Technology, Tehran (Iran, Islamic Republic of); Young Researchers and Elite Club, Khorramabad Branch, Islamic Azad University, Khorramabad (Iran, Islamic Republic of); Shahedi Asl, Mehdi [Department of Mechanical Engineering, University of Mohaghegh Ardabili, Ardabil (Iran, Islamic Republic of); Ghassemi Kakroudi, Mahdi, E-mail: mg_kakroudi@tabrizu.ac.ir [Department of Materials Engineering, Faculty of Mechanical Engineering, University of Tabriz, Tabriz (Iran, Islamic Republic of)

    2015-12-15

    In this paper, ZrB{sub 2}–SiC composites doped with 0–5 wt.% AlN were prepared by a low pressure hot pressing as well as a pressureless sintering methods at 1900 °C for 2 h. The influence of aluminum nitride addition on the sinterability and microstructure development of such ceramic composites was studied by a fractographical approach. The results revealed that only 1 wt.% AlN can aid the densification process of the hot pressed ceramic composite via the liquid phase sintering mechanism due to the formation of nano-scale metakaolinite spinel layers. In the pressureless sintering method, adding more AlN can increase the formation of gaseous products which raised the amount of porosities in the final microstructure. The formation of nano-graphite phase in the hot pressing process, the formation of Al{sub 2}OC in the pressureless sintering process, and the formation of BN in the both processes were disclosed by X-ray diffraction, SEM and TEM analyses. - Highlights: • The effect of AlN addition on densification of ZrB{sub 2}–SiC composites was studied. • AlN promotes the densification in hot pressed samples by liquid phase formation. • A fully dense composite was obtained by adding 1 wt.% AlN in hot pressing process. • In pressureless sintering, more AlN content intensifies the formation of porosities.

  3. Design Evolutuion of Hot Isotatic Press Cans for NTP Cermet Fuel Fabrication

    Science.gov (United States)

    Mireles, O. R.; Broadway, J.; Hickman, R.

    2014-01-01

    Nuclear Thermal Propulsion (NTP) is under consideration for potential use in deep space exploration missions due to desirable performance properties such as a high specific impulse (> 850 seconds). Tungsten (W)-60vol%UO2 cermet fuel elements are under development, with efforts emphasizing fabrication, performance testing and process optimization to meet NTP service life requirements [1]. Fuel elements incorporate design features that provide redundant protection from crack initiation, crack propagation potentially resulting in hot hydrogen (H2) reduction of UO2 kernels. Fuel erosion and fission product retention barriers include W coated UO2 fuel kernels, W clad internal flow channels and fuel element external W clad resulting in a fully encapsulated fuel element design as shown.

  4. New concept bioceramics composed of octacalcium phosphate (OCP) and dicarboxylic acid-intercalated OCP via hydrothermal hot-pressing

    Energy Technology Data Exchange (ETDEWEB)

    Ishihara, Shiho [Graduate School of Engineering, Osaka Prefecture University (Japan); Matsumoto, Takuya [Graduate School of Dentistry, Osaka University (Japan); Onoki, Takamasa, E-mail: onoki@mtr.osakafu-u.ac.jp [Graduate School of Engineering, Osaka Prefecture University (Japan); Sohmura, Taiji [Graduate School of Dentistry, Osaka University (Japan); Nakahira, Atsushi [Graduate School of Engineering, Osaka Prefecture University (Japan)

    2009-08-01

    Octacalcium phosphate (OCP) and adipic acid-intercalated complexed OCP (Adi-OCP) were synthesized. Moreover, we made ceramic bodies out of them through a hydrothermal hot-pressing (HHP) method. Characteristic features of both the powder and ceramics were investigated by the X-ray diffraction method (XRD). Surface morphology of the ceramics was observed by scanning electron microscopy (SEM). Density, compressive strength and pore size distribution of the ceramics were measured. Crystalline structure of the newly developed OCP ceramics had no phase transformation from the starting materials. Moreover, the newly developed OCP ceramics had good mechanical properties only through the HHP treatment with a temperature as low as 110 deg. C. In order to evaluate bioactivity, the ceramics were immersed in simulating body fluid (SBF). It was predicted that OCP and Adi-OCP had better bioactivity than that of conventional HAp ceramics.

  5. A trapped field of >3 T in bulk MgB2 fabricated by uniaxial hot pressing

    International Nuclear Information System (INIS)

    Durrell, J H; Dennis, A; Shi, Y; Xu, Z; Campbell, A M; Babu, N Hari; Cardwell, D A; Dancer, C E J; Todd, R I; Grovenor, C R M

    2012-01-01

    A trapped field of over 3 T has been measured at 17.5 K in a magnetized stack of two disc-shaped bulk MgB 2 superconductors of diameter 25 mm and thickness 5.4 mm. The bulk MgB 2 samples were fabricated by uniaxial hot pressing, which is a readily scalable, industrial technique, to 91% of their maximum theoretical density. The macroscopic critical current density derived from the trapped field data using the Biot–Savart law is consistent with the measured local critical current density. From this we conclude that critical current density, and therefore trapped field performance, is limited by the flux pinning available in MgB 2 , rather than by lack of connectivity. This suggests strongly that both increasing sample size and enhancing pinning through doping will allow further increases in trapped field performance of bulk MgB 2 . (rapid communication)

  6. Mechanochemical Effects on the Synthesis of Copper Orthophosphate and cyclo-Tetraphosphate Bulks by the Hydrothermal Hot Pressing Method

    Directory of Open Access Journals (Sweden)

    Isao Tanaka

    2009-01-01

    Full Text Available Copper orthophosphate, Cu3(PO42, and cyclo-tetraphosphates, Cu2P4O12, were synthesized using phosphoric acid and basic copper carbonate, and then treated with a planetary mill for up to 360 minutes. The un-milled and milled samples were characterized by X-ray diffraction (XRD and Fourier transform infrared (FT-IR spectroscopy. SEM images, particle size distribution, specific surface area, UV-Vis reflectance spectra were also used to evaluate the materials. The un-milled and milled materials were used to fabricate copper phosphate bulks by a hydrothermal hot pressing method. The influence of powder condition on the sintering behavior of the copper phosphates was studied.

  7. Intergranular phase of the Si3 N4 hot pressed with Mg O/Y2 O3

    International Nuclear Information System (INIS)

    Costa, Celio A.; Todd, Judith A.

    1997-01-01

    Monolithic and composite Si 3 N 4 hot-pressed with 3% Mgo or 6% Y 2 O 3 were analyzed with X-ray diffraction and transmission electron microscopy. The results showed materials to be composed of β-Si 3 N 4 grains and an intergranular phase which was partially crystalline and partially amorphous. For the materials sintered with Mg O, the identification of the intergranular phase was not conclusive. For the materials sintered with Y 2 O 3 . It was observed that the amount of intergranular crystalline phase decreased as whiskers were added to the material and the intergranular crystalline part had a crystallographic structure similar to yttrium-silicon-oxide-nitride family. (author)

  8. New concept bioceramics composed of octacalcium phosphate (OCP) and dicarboxylic acid-intercalated OCP via hydrothermal hot-pressing

    International Nuclear Information System (INIS)

    Ishihara, Shiho; Matsumoto, Takuya; Onoki, Takamasa; Sohmura, Taiji; Nakahira, Atsushi

    2009-01-01

    Octacalcium phosphate (OCP) and adipic acid-intercalated complexed OCP (Adi-OCP) were synthesized. Moreover, we made ceramic bodies out of them through a hydrothermal hot-pressing (HHP) method. Characteristic features of both the powder and ceramics were investigated by the X-ray diffraction method (XRD). Surface morphology of the ceramics was observed by scanning electron microscopy (SEM). Density, compressive strength and pore size distribution of the ceramics were measured. Crystalline structure of the newly developed OCP ceramics had no phase transformation from the starting materials. Moreover, the newly developed OCP ceramics had good mechanical properties only through the HHP treatment with a temperature as low as 110 deg. C. In order to evaluate bioactivity, the ceramics were immersed in simulating body fluid (SBF). It was predicted that OCP and Adi-OCP had better bioactivity than that of conventional HAp ceramics.

  9. Corrosion and wear behavior of functionally graded Al2024/SiC composites produced by hot pressing and consolidation

    Energy Technology Data Exchange (ETDEWEB)

    Erdemir, Fatih; Canakci, Aykut, E-mail: aykut@ktu.edu.tr; Varol, Temel; Ozkaya, Serdar

    2015-09-25

    Highlights: • Functionally graded Al2024/SiC composites were produced by hot pressing. • Effect of the number of graded layers was investigated on the corrosion behavior. • Functionally graded composites has the most corrosion resistant than composites. • Wear mechanisms of Al2024/SiC composites were explained. - Abstract: Functionally graded Al2024/SiC composites (FGMs) with varying percentage of SiC (30–60%) were produced by hot pressing and consolidation method. The effects of SiC content and number of layers of Al2024/SiC FGMs on the corrosion and wear behaviors were investigated. The microstructures of these composites were characterized by a scanning electron microscopy (SEM) with energy-dispersive X-ray spectroscopy (EDS). The corrosion performances of composites were evaluated by potentiodynamic polarization scans in 3.5% NaCl solution. Corrosion experiments shows that corrosion rate (1109 mpy) of two layered FGMs which containing 50 wt.% SiC were much higher than Al2024 matrix (2569 mpy) and Al2024/50 wt.% SiC composite (2201 mpy). Mechanical properties of these composites were evaluated by microhardness measurements and ball-on-disk wear tests. As the applied load change from 15 to 20 N, the wear rates of the Al2024 increased significantly and wear mechanism transformed from mild to severe wear regime. It has been shown that Al2024/40 wt.% SiC composite has lower wear rate where adhesive and abrasive wear mechanisms play a major role.

  10. Interfacial layers evolution during annealing in Ti-Al multi-laminated composite processed using hot press and roll bonding

    Science.gov (United States)

    Assari, A. H.; Eghbali, B.

    2016-09-01

    Ti-Al multi-laminated composites have great potential in high strength and low weight structures. In the present study, tri-layer Ti-Al composite was synthesized by hot press bonding under 40 MPa at 570 °C for 1 h and subsequent hot roll bonding at about 450 °C. This process was conducted in two accumulative passes to 30% and to 67% thickness reduction in initial and final passes, respectively. Then, the final annealing treatments were done at 550, 600, 650, 700 and 750 °C for 2, 4 and 6 h. Investigations on microstructural evolution and thickening of interfacial layers were performed by scanning electron microscopes, energy dispersive spectrometer, X-ray diffraction and micro-hardness tests. The results showed that the thickening of diffusion layers corresponds to amount of deformation. In addition to thickening of the diffusion layers, the thickness of aluminum layers decreased and after annealing treatment at 750 °C for 6 h the aluminum layers were consumed entirely, which occurred because of the enhanced interdiffusion of Ti and Al elements. Scanning electron microscope equipped with energy dispersive spectrometer showed that the sequence of interfacial layers as Ti3Al-TiAl-TiAl2-TiAl3 which are believed to be the result of thermodynamic and kinetic of phase formation. Micro-hardness results presented the variation profile in accordance with the sequence of intermetallic phases and their different structures.

  11. Investigation of Wear Behavior of Aluminum Matrix Composite Reinforced by Al2O3 and Produced by Hot Pressing Process

    Directory of Open Access Journals (Sweden)

    Halil ARIK

    2017-12-01

    Full Text Available In this study, Al powder produced by gas atomization technique has 72.06 µm average particle size and 99 % purity was mixed with as a reinforcement Al2O3 has 99.52% purity and 45 submicron particle size in a high energy ball mill for two hours. In order to obtain disk samples with 30 mm diameter and 6 mm thick mixed powders, after the characterization of particle size and morphology, were compacted in a single action press. Compaction process were carried out from mixed powders by hot pressing at 200 MPa pressure and 550 °C temperature for two hours. Then microstructural analysis, hardness and density measurements of powder metal composite parts were performed. After, the characterization of samples abrasion wear tests were performed according to ASTM-G99-05 by using TRIBOMETER T10/20 ball-on-disk abrasive wearing device. After the abrasive wear test of aluminum and composite powder metal parts produced under the identical test parameters, test results were compared and effect of Al2O3 on the wear properties of composite materials was exhibited. The test results showed that the composite parts have 62 % extra harness and better abrasion wear performance according to aluminum powder metal parts produced and tested under the identical conditions

  12. Effect of rapid solidification on the microstructure and mechanical properties of hot-pressed Al-20Si-5Fe alloys

    International Nuclear Information System (INIS)

    Rajabi, M.; Vahidi, M.; Simchi, A.; Davami, P.

    2009-01-01

    The aim of this work is to study the effect of cooling rate and subsequent hot consolidation on the microstructural features and mechanical strength of Al-20Si-5Fe-2X (X = Cu, Ni and Cr) alloys. Powder and ribbons were produced by gas atomization and melt spinning processes at two different cooling rates of 1 x 10 5 K/s and 5 x 10 7 K/s. The microstructure of the products was examined using optical microscopy, scanning electron microscopy, transmission electron microscopy, and X-ray diffraction. The particles were consolidated by hot pressing at 400 deg. C/250 MPa/1 h under a high purity argon atmosphere and the microstructure, hardness and compressive strength of the compacts were evaluated. Results showed a profound effect of the cooling rate, consolidation stage, and transition metals on the microstructure and mechanical strength of Al-20Si-5Fe alloys. While microstructural refining was obtained at both cooling rates, the microstructure of the atomized powder exhibited the formation of fine primary silicon (∼ 1 μm), eutectic Al-Si phase with eutectic spacing of ∼ 300 nm, and δ-iron intermetallic. Supersaturated Al matrix containing 5-7 at.% silicon and nanometric Si precipitates (20-40 nm) were determined in the microstructure of the melt-spun ribbons. The hot consolidation resulted in coarsening of Si particles in the atomized particles, and precipitation of Si and Fe-containing intermetallics from the supersaturated Al matrix in the ribbons. The consolidated ribbons exhibited higher mechanical strength compared to the atomized powders, particularly at elevated temperatures. The positive influence of the transition metals on the thermal stability of the Al-20Si-5Fe alloy was noticed, particularly in the Ni-containing alloy.

  13. Comparison between uniaxially and isostatically compacted bentonite

    International Nuclear Information System (INIS)

    Kalbantner, P.; Sjoeblom, R.; Boergesson, Lennart

    2001-12-01

    The purpose of the present report is to provide the Swedish Nuclear Fuel and Waste Management Company (SKB) with the knowledge base needed for their selection of reference method for manufacturing of bentonite blocks. The purpose is also to provide support for the direction of the further development work. Three types of blocks are compared in the present report: uniaxially compacted medium high blocks, isostatically compacted medium high blocks, isostatically compacted high blocks. The analyses is based on three process systems relating to the sequence of excavation of bentonite-transport-powder preparation-compaction-handling and emplacement of bentonite blocks. The need for further knowledge has been identified and documented in conjunction with these analyses. The comparison is primarily made with regard to the criteria safety/risk, quality/ technique and economy. It is carried out through identification of issues of significance and subsequent analysis and evaluation as well as more formally in a simplified AHP (AHP = Analytical Hierarchic Process). The result of the analyses is that the isostatic technique is applicable for the production of high as well as medium size blocks. The pressed blocks are assessed to fulfil the basic requirements with a very large margin. The result of the analyses is also that the uniaxial technique is applicable for the preparation of medium size blocks, which are assessed to fulfil the basic requirements with a large margin. The need for development and process control is assessed to be somewhat higher for the uniaxial technique. One example is the friction against the walls of the die during the compaction, including the significance of this friction for the development of stresses and discontinuities in the block. These results support a selection of the isostatic technique as the reference technique as it provides flexibility in the choice of block height. The uniaxial technique can form a second alternative if medium high

  14. The microstructures and mechanical properties of Al-15Si-2.5Cu-0.5Mg/(wt%)B{sub 4}C composites produced through hot pressing technique and subjected to hot extrusion

    Energy Technology Data Exchange (ETDEWEB)

    Ozer, Alpay, E-mail: alpiozer@gmail.com

    2016-11-01

    In this study, B{sub 4}C (5, 10, and 15 wt%) particle-reinforced Ecka Alumix 231{sup ®} aluminum matrix composites were produced through the hot pressing technique. Some of these samples were subjected to hot extrusion as a secondary treatment at 4:1 ratio at a temperature of 555 °C. The obtained samples were subjected to density measurement, hardness test, microstructure analysis, and three-point bending test, and their fracture surfaces were examined. A density of over 99% was found in the samples. Al-rich solid solution and primary Si, CuAl{sub 2}, Al{sub 2}CuMg, and Mg{sub 2}Si phases in the microstructure were determined through X-ray diffraction analysis. Grain sizes were found to be 20 μm and 2 μm in the microstructures of the samples produced through hot pressing technique and of those subjected to additional hot extrusion, respectively. High hardness values were obtained in the samples subjected to hot extrusion. In these samples, wt% B{sub 4}C particle ratio and transverse rupture strength increased considerably. Furthermore, the highest compressive strain value was obtained in the 10 wt% B{sub 4}C particle-reinforced composites subjected to hot extrusion. - Highlights: • Liquid phase formed at the temperature of hot pressing and hot extrusion. • In the samples, over 99.19% density was obtained. • Average matrix grain size was measured to be 2 μm through hot extrusion. • As wt% B{sub 4}C ratio increased, transverse rupture strength values increased. • High compressive strain values were obtained in the hot extrusion samples.

  15. Atom Probe Tomography of Phase and Grain Boundaries in Experimentally-Deformed and Hot-Pressed Wehrlite

    Science.gov (United States)

    Cukjati, J.; Parman, S. W.; Cooper, R. F.; Zhao, N.

    2017-12-01

    Atom probe tomography (APT) was used to characterize the chemistry of three grain boundaries: an olivine-olivine (ol-ol) and olivine-clinopyroxene (ol-cpx) boundary in fine-grained experimentally-deformed wehrlite and an ol-cpx boundary in a fine-grained, hot-pressed wehrlite. Grain boundaries were extracted and formed into APT tips using a focused ion beam (FIB). The tips were analyzed in a reflectron-equipped LEAP4000HR (Harvard University) at 1% or 0.5% detection rate, 5pJ laser energy and 100kHz pulse rate. Total ion counts are between 40 and 100 million per tip. Examination of grain and phase boundaries in wehrlite are of interest since slow-diffusing and olivine-incompatible cations present in cpx (e.g. Ca and Al) may control diffusion-accommodated grain boundary sliding and affect mantle rheology (Sundberg & Cooper, 2008). At steady state, ol-cpx aggregates are weaker than either ol or cpx end member, the results of which are not currently well-explained. We investigate grain boundary widths to understand the transport of olivine-incompatible elements. Widths of grain/phase boundary chemical segregation are between 3nm and 6nm for deformed ol-ol and ol-cpx samples; minimally-deformed (hot-pressed) samples having slightly wider chemical segregation widths. Chemical segregation widths were determined from profiles of Na, Al, P, Cl, K, Ca, or Ni, although not all listed elements can be used for all samples (e.g. Na, K segregation profiles can only be observed for ol-ol sample). These estimates are consistent with prior estimates of grain boundary segregation by atom probe tomography on ol-ol and opx-opx samples (Bachhav et al., 2015) and are less than ol-ol interface widths analyzed by STEM/EDX (Hiraga, Anderson, & Kohlstedt, 2007). STEM/EDX will be performed on deformed wehrlite to investigate chemical profile as a function of applied stress orientation and at length scales between those observable by APT and EPMA. Determination of phase boundary chemistry and

  16. Enhancement of mechanical strength in hot-pressed TiB2 composites by the addition of Fe and Ni

    International Nuclear Information System (INIS)

    Yen, C.F.; Yust, C.S.; Clark, G.W.

    1978-01-01

    Improvement in the fracture strength of TiB 2 composites through the addition of Fe and Ni is reported. Beam specimens containing up to 20 wt % of the metal component were fabricated by hot pressing above the eutectic temperature. Four point bending results indicated that the observed enhancement in strength was proportional to the vol % of the metal present. The results also revealed that TiB 2 --Ni composites have slightly better strength than TiB 2 --Fe samples at elevated temperatures, and that their strengths were consistently about twice that of pure TiB 2 . They also did not exhibit any serious degradation in strength up to 700 0 C. The fracture behavior was characterized using optical and scanning electron microscopy. The strengthening appears to be related to the presence of a metallic grain boundary phase between TiB 2 particles. The results further suggested that the formation of a special eutectic-like grain microstructure could render additional strengthening

  17. The influence of process parameters and additives on the densification, creep properties and strength of hot pressed silicon nitride

    International Nuclear Information System (INIS)

    Becker, R.

    1979-03-01

    One method of production of Si 3 N 4 parts is the hot pressing of powder compacts. According to the current technological know how, a liquid phase building additive (e.g. MgO) is essential for the complete densification of Si 3 N 4 . In this work it has been shown, how dense Si 3 N 4 may be produced without the conventional additives. The SiO 2 -coating of Si 3 N 4 particles here results in the liquid phase formation. On the basis of the above concept, the effect of MgO, Mg 3 N 2 , Al 2 O 3 and A1N-additions to a pure Si 3 N 4 powder have been studied in detail and the resulting material properties: densification, creep and high temperature strengths have been determined. Based on the results, it may be concluded, that HPSN is a dispersion of crystalline Si 3 N 4 in an amorphous matrix (glass content between 4-10 vol%). Depending on the amount and composition of the boundary phase (silicate glass) widely variing material properties may be obtained. (orig./GSCH) [de

  18. Vacuum hot-pressed beryllium and TiC dispersion strengthened tungsten alloy developments for ITER and future fusion reactors

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Xiang, E-mail: xliu@swip.ac.cn [Southwestern Institute of Physics, P.O. Box 432, Chengdu 610041, Sichuan (China); Chen, Jiming; Lian, Youyun; Wu, Jihong; Xu, Zengyu; Zhang, Nianman; Wang, Quanming; Duan, Xuro [Southwestern Institute of Physics, P.O. Box 432, Chengdu 610041, Sichuan (China); Wang, Zhanhong; Zhong, Jinming [Northwest Rare Metal Material Research Institute, CNMC, Ningxia Orient Group Co. Ltd.,No.119 Yejin Road, Shizuishan City, Ningxia,753000 (China)

    2013-11-15

    Beryllium and tungsten have been selected as the plasma facing materials of the ITER first wall (FW) and divertor chamber, respectively. China, as a participant in ITER, will share the manufacturing tasks of ITER first-wall mockups with the European Union and Russia. Therefore ITER-grade beryllium has been developed in China and a kind of vacuum hot-pressed (VHP) beryllium, CN-G01, was characterized for both physical, and thermo-mechanical properties and high heat flux performance, which indicated an equivalent performance to U.S. grade S-65C beryllium, a reference grade beryllium of ITER. Consequently CN-G01 beryllium has been accepted as the armor material of ITER-FW blankets. In addition, a modification of tungsten by TiC dispersion strengthening was investigated and a W–TiC alloy with TiC content of 0.1 wt.% has been developed. Both surface hardness and recrystallization measurements indicate its re-crystallization temperature approximately at 1773 K. Deuterium retention and thermal desorption behaviors of pure tungsten and the TiC alloy were also measured by deuterium ion irradiation of 1.7 keV energy to the fluence of 0.5–5 × 10{sup 18} D/cm{sup 2}; a main desorption peak at around 573 K was found and no significant difference was observed between pure tungsten and the tungsten alloy. Further characterization of the tungsten alloy is in progress.

  19. Effect of sintering temperature and boron carbide content on the wear behavior of hot pressed diamond cutting segments

    Directory of Open Access Journals (Sweden)

    Islak S.

    2015-01-01

    Full Text Available The aim of this study was to investigate the effect of sintering temperature and boron carbide content on wear behavior of diamond cutting segments. For this purpose, the segments contained 2, 5 and 10 wt.% B4C were prepared by hot pressing process carried out under a pressure of 35 MPa, at 600, 650 and 700 °C for 3 minutes. The transverse rupture strength (TRS of the segments was assessed using a three-point bending test. Ankara andesite stone was cut to examine the wear behavior of segments with boron carbide. Microstructure, surfaces of wear and fracture of segments were determined by scanning electron microscopy (SEM-EDS, and X-ray diffraction (XRD analysis. As a result, the wear rate decreased significantly in the 0-5 wt.% B4C contents, while it increased in the 5-10 wt.% B4C contents. With increase in sintering temperature, the wear rate decreased due to the hard matrix.

  20. Study on the isothermal oxidation behavior in air of Ti3AlC2 sintered by hot pressing

    Institute of Scientific and Technical Information of China (English)

    XU Xuewen; LI Yangxian; MEI Bingchu; ZHU Jiaoqun; LIU Heyan; QU Jingping

    2006-01-01

    The isothermal oxidation behavior at 900―1300℃ for 20 h in air of bulk Ti3AlC2 with 2.8 wt% TiC sintered by means of hot pressing was investigated in the work. The isothermal oxidation behavior generally followed a parabolic rate law. The parabolic rate constants increased from 1.39×10-10 kg2·m-4·s-1 at 900℃ to 5.56×10-9 kg2·m-4·s-1 at 1300℃. The calculated activation energy was 136.45 kJ/mol. It was demonstrated that Ti3AlC2 had excellent oxidation resistance due to the continuous, dense and adhesive protect scales consisted of a mass of α-Al2O3 and a little of TiO2 and/or Al2TiO5. In principle, the oxide scale was grown by the inward diffusion of O2- and the outward diffusion of Ti4+ and Al3+. The rapid outward diffusion of cations usually resulted in the formation of cracks, gaps, and holes.

  1. Thermoelectric Properties of Cu-doped Bi2-xSbxTe3 Prepared by Encapsulated Melting and Hot Pressing

    Science.gov (United States)

    Jung, Woo-Jin; Kim, Il-Ho

    2018-03-01

    P-type Bi2-xSbxTe3:Cum (x = 1.5-1.7 and m = 0.002-0.003) solid solutions were synthesized using encapsulated melting and were consolidated using hot pressing. The effects of Sb substitution and Cu doping on the charge transport and thermoelectric properties were examined. The lattice constants decreased with increasing Sb and Cu contents. As the amount of Sb substitution and Cu doping was increased, the electrical conductivity increased, and the Seebeck coefficient decreased owing to the increase in the carrier concentration. All specimens exhibited degenerate semiconductor characteristics and positive Hall and Seebeck coefficients, indicating p-type conduction. The increased Sb substitution caused a shift in the onset temperature of the intrinsic transition and bipolar conduction to higher temperatures. The electronic thermal conductivity increased with increasing Sb and Cu contents owing to the increase in the carrier concentration, while the lattice thermal conductivity slightly decreased due to alloy scattering. A maximum figure of merit, ZTmax = 1.25, was achieved at 373 K for Bi0.4Sb1.6Te3:Cu0.003.

  2. Prototype Development of Remote Operated Hot Uniaxial Press (ROHUP) to Fabricate Advanced Tc-99 Bearing Ceramic Waste Forms - 13381

    Energy Technology Data Exchange (ETDEWEB)

    Alaniz, Ariana J.; Delgado, Luc R.; Werbick, Brett M. [University of Nevada - Las Vegas, Howard R. Hughes College of Engineering, 4505 S. Maryland Parkway, Box 454009, Las Vegas, NV 89154-4009 (United States); Hartmann, Thomas [University of Nevada - Las Vegas, Harry Reid Canter, 4505 S. Maryland Parkway, Box 454009, Las Vegas, NV 89154-4009 (United States)

    2013-07-01

    The objective of this senior student project is to design and build a prototype construction of a machine that simultaneously provides the proper pressure and temperature parameters to sinter ceramic powders in-situ to create pellets of rather high densities of above 90% (theoretical). This ROHUP (Remote Operated Hot Uniaxial Press) device is designed specifically to fabricate advanced ceramic Tc-99 bearing waste forms and therefore radiological barriers have been included in the system. The HUP features electronic control and feedback systems to set and monitor pressure, load, and temperature parameters. This device operates wirelessly via portable computer using Bluetooth{sup R} technology. The HUP device is designed to fit in a standard atmosphere controlled glove box to further allow sintering under inert conditions (e.g. under Ar, He, N{sub 2}). This will further allow utilizing this HUP for other potential applications, including radioactive samples, novel ceramic waste forms, advanced oxide fuels, air-sensitive samples, metallic systems, advanced powder metallurgy, diffusion experiments and more. (authors)

  3. Sintering of Si C by hot-pressing with addition of Al2O3 and concentrate of rare earths

    International Nuclear Information System (INIS)

    Hwang, M.K.; Silva, C.R.M.

    2004-01-01

    Silicon carbide (SiC) has essentially covalent bonds (∼88%). The high covalency bond is responsible for the good mechanical properties, although it induces a low self diffusion coefficient, making densification more difficult. For a successful densification is necessary to apply pressure on the samples, and/or the addition of sintering additives, which improves the densification. In this SiC samples with alumina (Al2O3) and concentrate of rare earth (CRE) addition were sintered by hot pressing in argon atmospheric at 20 MPa of pressure, heating rate of 20 deg C/min up to 1800 deg C and a dwell time of 1 h. Initially the CRE was calcined at 1000 deg C during 1 h. After that, three mixtures were prepared with distinct concentrations in high energy mill and the samples were sintered. The aim of this work is to improve SiC densification by the liquid phase formation during sintering owing to the additives reactions between itself. The pressure intensify the driving force for densification, taking the liquid phase to drain easier through the grain boundaries, making possible best accommodation and rearrangement of the grains. The application of the pressure on the samples during sintering contributes to improve densification and becomes possible sintering in lower temperature than conventional one. The phases of the sintered samples were analyzed by X-ray diffraction and the morphology were verified by scanning electron microscopy. (author)

  4. Hot off the Press.

    Science.gov (United States)

    Hill, Robert A; Sutherland, Andrew

    2018-06-07

    A personal selection of 32 recent papers is presented covering various aspects of current developments in bioorganic chemistry and novel natural products such as mollebenzylanol A from Rhododendron molle.

  5. Comparison of Ti(C,N)-based cermets processed by hot-pressing sintering and conventional pressureless sintering

    International Nuclear Information System (INIS)

    Xu, Qingzhong; Ai, Xing; Zhao, Jun; Qin, Weizhen; Wang, Yintao; Gong, Feng

    2015-01-01

    Highlights: • The HP sintered Ti(C,N)-based cermets exhibit high hardness with fine grain size. • The PLS sintered cermets possess high mechanical properties with low porosity. • The applied pressure can rearrange particles and contribute to grain refinement. • The heating rate can greatly affect the solid and liquid phase sintering of cermets. - Abstract: A suitable sintering method is important to obtain the Ti(C,N)-based cermets with superior properties. In this paper, Ti(C,N)-based cermets were fabricated by hot-pressing sintering (HP) and conventional pressureless sintering (PLS) technology, respectively, to investigate the influence of different sintering methods on the microstructure and mechanical properties of cermets materials. The microstructure, fracture morphology, indention cracks and phase composition were observed and detected using scanning electron microscope (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The transverse rupture strength (TRS), Vickers hardness (HV) and fracture toughness (K IC ) were also measured. The results reveal that all of the Ti(C,N)-based cermets exhibit core–rim microstructures with black cores, white cores and grey rims embedded into metal binder phases. The grain size of the samples fabricated by HP is much finer and the structure is more compact than those fabricated by PLS, while there exist pores in the HP sintered samples. The sintering process has no influence on the phase composition of cermets, but affects the phase content and crystallinity. The samples fabricated by PLS present higher transverse rupture strength, fracture toughness and density than samples fabricated by HP. However, the HP sintered samples possess a higher hardness

  6. Physical and mechanical properties of parallel strand lumber made from hot pre-pressed long strand oil palm trunk waste

    Science.gov (United States)

    Fridiyanti, Inayah; Massijaya, M. Y.

    2018-03-01

    This research was focused on the utilization of oil palm trunk waste as a Parallel Strand Lumber (PSL) raw material. This research aimed to analyze the effect of adhesive types and glue spreads to the physical and mechanical properties of PSL. The adhesive types used were isocyanate and urea formaldehyde adhesives. The glue spreads used were 150 g/m2 and 300 g/m2. The research results showed that the moisture content of PSL ranged from 9.30% to 11.80%. The PSL density ranged from 0.64 to 0.78 g/cm3. The volume shrinkage ranged from 5.69 to 7.17%. Modulus of Elasticity (MOE) parallel to the grain and edge side ranged from 51.6 × 103 to 98.3 × 103 kg/cm2, and 62.1 × 103 to 99.9 × 103 kg/cm2, respectively. The Modulus of Rupture (MOR) parallel to the grain and edge side ranged from 269 to 724 kg/cm2 and 342 to 728 kg/cm2, respectively. The PSL hardness perpendicular to the grain, parallel to the grain and the edge side ranged from 135 to 300 kg/cm2, 87 to 321 kg/cm2, and 128 to 251 kg/cm2, respectively. The compressive strength ranged from 181 to 231 kg/cm2. The best adhesive and glue spreads of PSL was isocyanate with glue spread 300 g/m2. PSL made from hot pre-pressed long strand of oil palm trunk waste bonded by isocyanate fulfill JAS 1152: 2007. However, those of bonded by urea formaldehyde failed to fulfill the standard. The physical and mechanical properties of PSL made from oil palm trunk were better compared to those of solid oil palm trunk.

  7. Kaji Eksperimental dan Simulasi Ansys 14.5 Perlakuan Serat Tandan Kosong Kelapa Sawit Serta Pembuatan Komposit Busa Polimer pada Proses Hot Press Menggunakan Alat Uji Tarik

    OpenAIRE

    Ginting, Enda Prananta

    2016-01-01

    Along the innovations of the field of materials, natural fibers are used as reinforcement materials composite which are the fibers greatly affect and determine the strength of the composite. This experimental study reported the empty fruit bunches of oil palm fiber’s treatment process and manufacture of polymeric foam composite spesimens in the process of hot press machine followed by a tensile test. The issues, that characteristic of composites reinforced fibers has a light weight and relati...

  8. The influence of powder composition and sintering temperature on transformation kinetics, structure and mechanical properties of hot-pressed silicon nitride

    International Nuclear Information System (INIS)

    Knoch, H.; Ziegler, G.

    1977-01-01

    The strength at room temperature of hot-pressed silicon nitride is strongly dependent on the structure which in turn depends on powder composition and process parameters. Connections between production conditions (MgO content, pressing temperature, pressing time), structure (α/β content and morphology), and the properties at room temperature are discussed. The growth of oblong β grains - as a direct result of phase transition from α- to β-Si 3 N 4 - results in microstructural meshing and thus in a higher strength. Optimum mechanical properties are achieved after full phase transformation and with a microstructure as fine as possible. The direct connection between strength and transformed β fraction indicates a possible way for a relatively fast determination of optimum properties for a given initial powder. (orig.) [de

  9. The Novel Design and Manufacturing Technology of Densified RDF from Reclaimed Landfill without a Mixing Binding Agent Using a Hydraulic Hot Pressing Machine

    Directory of Open Access Journals (Sweden)

    Kerdsuwan Somrat

    2016-01-01

    Full Text Available The manufacturing of RDF (Refuse Derived Fuel from a conventional cold press extrusion machine is not suitable for producing RDF from reclaimed landfill since it is not identical in shape and form after production due to the swelling of the plastic fraction contained inside the reclaimed landfill and hence needs a very high compression force. Moreover, a binder agent is needed in order to keep the RDF in a similar shape and form. A novel design and manufacturing technology for a hydraulic hot pressing machine has been established and can produce high-quality RDF without any binder. The two electrical heaters are installed at the inner core and on the surface of the mold. The compression force on the mold is performed by a hydraulic jack. In addition, a newly-designed locking plate system which is designed by a slider to open and close along the paired horizontal slots, can reduce the cycle time of the manufacturing process and yield higher productivity. The testing properties of the RDF produced by the novel hydraulic hot pressing machine include the examination of size, shape, weight, unit density, bulk density, compression strength, moisture content, and heating value. The results showed that the RDF is suitable to be used as feedstock in an incinerator or gasifier to produce green and clean energy from reclaimed landfill.

  10. Microstructures and mechanical properties of Cu/Ti{sub 3}SiC{sub 2}/C/MWCNTs composites prepared by vacuum hot-pressing sintering

    Energy Technology Data Exchange (ETDEWEB)

    Xiaosong, Jiang, E-mail: xsjiang@yeah.net [School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Liu, Wanxia; Li, Jingrui [School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Shao, Zhenyi [Department of Mechanical Engineering, Chengdu Technological University, Chengdu, Sichuan 610031 (China); Zhu, Degui [School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China)

    2015-01-05

    Highlights: • Cu/Ti{sub 3}SiC{sub 2}/C/MWCNTs composites were prepared using vacuum hot-pressing sintering. • Dispersions of MWCNTs were prepared using 10 μg/ml gallic acid aqueous solution. • MWCNTs content has no effect on generation of TiC and Cu{sub 9}Si to effect matrix’s performance. - Abstract: Cu/Ti{sub 3}SiC{sub 2}/C/MWCNTs composites were prepared by vacuum hot-pressing sintering. Microstructures and mechanical properties of Cu/Ti{sub 3}SiC{sub 2}/C/MWCNTs composites with different multi-walled carbon nanotubes contents have been systematically investigated. The microstructures of the composites were examined by optical microscopy, X-ray diffraction, back scattered electron imaging, scanning electron microscope and energy dispersive spectrometer. The mechanical properties were determined from Brinell hardness and tensile tests. The results demonstrated that there was an optimum value of MWCNTs content which has an impact on microstructures and mechanical properties of Cu/Ti{sub 3}SiC{sub 2}/C/MWCNTs composites. Based on MWCNTs content on properties and microstructure of Cu/Ti{sub 3}SiC{sub 2}/C/MWCNTs composites, effects of MWCNTs on improvement of the composites and strengthening mechanism have been analyzed.

  11. Study on the process of sintering matrix metallic Fe-Cu-25%Nb and Fe-Cu-25%Co during hot pressing

    International Nuclear Information System (INIS)

    Batista, A.C.; Oliveira, H.C.P.; Souza, M.H.; Assis, P.S.

    2016-01-01

    The sintering process promotes densification and the evolution of the microstructure of the material, with consequent significant increase in hardness and mechanical strength. However, few studies show the influence of pressure and temperature during sintering by hot pressing. In this sense, this work aims to evaluate the microstructural changes and properties with the variation of pressure and temperature and the type suffered by sintering metal powders during sintering by hot pressing. For this, two samples were studied by changing the sintering parameters: 25% Fe-50% Cu-25% Nb and 25% Fe-50% Cu-25% Co. Samples were analyzed by SEM / EDS in order to check the morphology and the presence of pores, as well as the interaction between the metallic constituents of each sample by the EDS analysis in line. They also determined the relative density, porosity and Vickers hardness (HV5). At the end of the study it was concluded that niobium alloy composite element by sintering activated suffered together with the liquid phase sintering. For cobalt alloys were observed by liquid phase sintering. The increase in the severity of the sintering conditions (temperature and pressure) led to an improvement in physical and mechanical properties of the alloys, which indicates that these parameters are directly related to the mechanisms of diffusion in the sintering process, improving the properties and diffusivity between elements. (author)

  12. THERMOELECTRIC PROPERTIES OF HOT-PRESSED p-TYPE Mg2Si0.3Sn0.7 SOLID SOLUTION

    Directory of Open Access Journals (Sweden)

    G. N. Isachenko

    2014-05-01

    Full Text Available It is shown that thermoelectric energy conversion which gives the possibility for utilizing a low potential heat is one of the ways for adoption of energy-saving technologies; and semiconductor materials with p-type and n-type conductivities having high thermoelectric figure of merit are necessary for operation of thermoelectric generators. The paper deals with possibility of usage of the p-Mg2Si0.3Sn0.7 solid solution (with a nanostructured modification as a couple for the well studied thermoelectric material based on n-Mg2Si-Mg2Sn. A technological scheme for fabrication of heavily doped Mg2Si0.3Sn0.7 solid solution of p-type by hot pressing from nanopowder is developed. The given technology has made it possible to reduce duration of a homogeneous material fabrication and has improved its physical and chemical properties. The samples were made by three ways: direct fusion for polycrystals fabrication; hot pressing from microparticles; nanostructuring, i.e. hot pressing from nanoparticles. By X-ray diffraction it is shown that sizes of structural elements in the fabricated samples are about 40 nm. The probe technique is used for measurement of electric conductivity and Seebeck coefficient. The stationary absolute method is used for measurement of thermal conductivity. Thermoelectric figure of merit is defined by measured values of kinetic coefficients in the temperatures range of 77 – 800 K. It was demonstrated, that electric conductivity, Seebeck coefficient and the power factor do not depend practically on a way of solid solution preparation. Thermal conductivity of samples pressed from nanoparticles has appeared to be higher, than of samples, obtained by direct fusion; i.e. in this case nanostructuring has not led to increase of thermoelectric figure of merit. The conclusion is drawn, that polycrystalline semiconductor Mg2Si0.3Sn0.7 can be used as a p-branch for a thermoelectric generator though nanostructuring has not led to the figure of

  13. Thermoelectric properties of I-doped n-type Bi2Te3-based material prepared by hydrothermal and subsequent hot pressing

    Directory of Open Access Journals (Sweden)

    Fang Wu

    2017-04-01

    Full Text Available I-doped Bi2Te3−xIx (x=0, 0.05, 0.1, 0.2 flower-like nanoparticles were synthesized by a hydrothermal method through a careful adjustment of the amount of ethylenediamine tetraacetic acid surfactant. The nanopowders of flower-like nanoparticles were hot-pressed into bulk pellets and the thermoelectric properties of the pellets were investigated. The results showed that I-doping decreased the electrical resistivity effectively, and the thermal conductivitives of the Bi2Te3−xIx bulk samples was lower because of the closer atomic mass of I compared to Te. As a result, a ZT value of 1.1 was attained at 448 K for the Bi2Te2.9I0.1 sample.

  14. Development of Duplex Stainless Steels by Field-Assisted Hot Pressing: Influence of the Particle Size and Morphology of the Powders on the Final Mechanical Properties

    Science.gov (United States)

    García-Junceda, A.; Rincón, M.; Torralba, J. M.

    2018-01-01

    The feasibility of processing duplex stainless steels with promising properties using a powder metallurgical route, including the consolidation by field-assisted hot pressing, is assessed in this investigation. The influence of the particle size and morphology of the raw austenitic and ferritic powders on the final microstructure and properties is also evaluated for an austenitic content of 60 wt pct. In addition, the properties of a new microconstituent generated between the initial constituents are analyzed. The maximum sintered density (98.9 pct) and the best mechanical behavior, in terms of elastic modulus, nanohardness, yield strength, ultimate tensile strength, and ductility, are reached by the duplex stainless steel processed with austenitic and ferritic gas atomized stainless steel powders.

  15. Fabrication and Analysis of the Wear Properties of Hot-Pressed Al-Si/SiCp + Al-Si-Cu-Mg Metal Matrix Composite

    Science.gov (United States)

    Bang, Jeongil; Oak, Jeong-Jung; Park, Yong Ho

    2016-01-01

    The aim of this study was to characterize microstructures and mechanical properties of aluminum metal matrix composites (MMC's) prepared by powder metallurgy method. Consolidation of mixed powder with gas atomized Al-Si/SiCp powder and Al-14Si-2.5Cu-0.5Mg powder by hot pressing was classified according to sintering temperature and sintering time. Sintering condition was optimized using tensile properties of sintered specimens. Ultimate tensile strength of the optimized sintered specimen was 228 MPa with an elongation of 5.3% in longitudinal direction. In addition, wear properties and behaviors of the sintered aluminum-based MMC's were analyzed in accordance with vertical load and linear speed. As the linear speed and vertical load of the wear increased, change of the wear behavior occurred in order of oxidation of Al-Si matrix, formation of C-rich layer, Fe-alloying to matrix, and melting of the specimen

  16. Effects of internal gas pressure and microstructure on the mechanisms of hot-pressing and swelling in ceramics. Final report, June 1, 1979-May 31, 1980

    International Nuclear Information System (INIS)

    Solomon, A.A.

    1980-08-01

    The results of the study of the effects of internal and external gas pressures on ceramics are summarized. The new experimental systems for studying these phenomena are described. The study has shown that the rate of volume change in ZnO is linearly related to the total pressure driving force. Swelling and hot-pressing can be described on a consistent basis in terms of this driving force. For ZnO, Ni and UO 2 the rate of volume change is dependent on bulk diffusion. The porosity evolution during swelling is described and the resintering phenomenon is identified. Various models for pore growth and shrinkage are considered and related to the behavior of the different systems

  17. Fabrication of a Nano-ZnO/Polyethylene/Wood-Fiber Composite with Enhanced Microwave Absorption and Photocatalytic Activity via a Facile Hot-Press Method

    Directory of Open Access Journals (Sweden)

    Baokang Dang

    2017-11-01

    Full Text Available A polyethylene/wood-fiber composite loaded with nano-ZnO was prepared by a facile hot-press method and was used for the photocatalytic degradation of organic compounds as well as for microwave absorption. ZnO nanoparticles with an average size of 29 nm and polyethylene (PE powders were dispersed on the wood fibers’ surface through a viscous cationic polyacrylamide (CPAM solution. The reflection loss (RL value of the resulting composite was −21 dB, with a thickness of 3.5 mm in the frequency of 17.17 GHz. The PE/ZnO/wood-fiber (PZW composite exhibited superior photocatalytic activity (84% methyl orange degradation within 300 min under UV light irradiation. ZnO nanoparticels (NPs increased the storage modulus of the PZW composite, and the damping factor was transferred to the higher temperature region. The PZW composite exhibited the maximum flexural strength of 58 MPa and a modulus of elasticity (MOE of 9625 MPa. Meanwhile, it also displayed dimensional stability (thickness swelling value of 9%.

  18. Influence of Fiber Content on Mechanical and Morphological Properties of Woven Kenaf Reinforced PVB Film Produced Using a Hot Press Technique

    Directory of Open Access Journals (Sweden)

    Suhad D. Salman

    2016-01-01

    Full Text Available This work addresses the results of experimental investigation carried out on mechanical and morphological properties of plain woven kenaf fiber reinforced PVB film which was prepared by hot press technique. The composites were prepared with various fiber contents: 0%, 10%, 20%, 30%, 40%, 50%, and 60% (by weight, with the processing parameters 165°C, 20 min, and at a pressure of 8 MPa applied on the material. Tensile, flexural, and Charpy impact properties were studied as well as morphological properties of impact fracture surface. With the increase in kenaf fibers content up to 40%, the PVB composites have shown lower tensile and flexural strength accompanied with reduction in the ultimate strain of the composite. The results showed that impact properties were affected in markedly different ways by using various kenaf contents and decrease with the increase in kenaf fiber content up to 40%; however, high impact strength was observed even with 40% kenaf fiber content. Furthermore, scanning electron microscopy for impact samples was utilised to demonstrate the different failures in the fracture surfaces for various kenaf fibers contents.

  19. Microstructure and Mechanical Properties of Multiphase Strengthened Al/Si/Al_2O_3/SiO_2/MWCNTs Nano composites Sintered by In Situ Vacuum Hot Pressing

    International Nuclear Information System (INIS)

    Li, J.; Jiang, X.; Zhu, D.; Zhu, M.; Shao, Z.; Johnson, S.; Luo, Z.

    2015-01-01

    Eutectic Al/Si binary alloy is technically one of the most important Al casting alloys due to its high corrosion resistance, evident shrinkage reduction, low thermal expansion coefficient, high fluidity, and good weldability. In this work, multi phased Al/Si matrix nano composites reinforced with Al_2O_3 and multi walled carbon nano tubes (MWCNTs) have been sintered by an in situ vacuum hot-pressing method. The alumina Al_2O_3 nanoparticles were introduced by an in situ reaction of Al with SiO_2. Microstructure and mechanical properties of the sintered Al/Si/Al_2O_3/SiO_2/MWCNTs nano composites with different alumina contents were investigated. The mechanical properties were determined by micro-Vickers hardness and compressive and shear strength tests. The results demonstrated that in situ alumina and MWCNTs had impacts on microstructure and mechanical properties of the nano composites. Based on the mechanical properties and microstructure of the nano composites, strengthening and fracture mechanisms by multiple reinforcements were analyzed

  20. Fabrication of Hadfield-Cored Multi-layer Steel Sheet by Roll-Bonding with 1.8-GPa-Strength-Grade Hot-Press-Forming Steel

    Science.gov (United States)

    Chin, Kwang-Geun; Kang, Chung-Yun; Park, Jaeyeong; Lee, Sunghak

    2018-05-01

    An austenitic Hadfield steel was roll-bonded with a 1.8-GPa-strength-grade martensitic hot-press-forming (HPF) steel to fabricate a multi-layer steel (MLS) sheet. Near the Hadfield/HPF interface, the carburized and decarburized layers were formed by the carbon diffusion from the Hadfield (1.2%C) to HPF (0.35%C) layers, and could be regarded as kinds of very thin multi-layers of 35 μm in thickness. The tensile test and fractographic data indicated that the MLS sheet was fractured abruptly within the elastic range by the intergranular fracture occurred in the carburized layer. This was because C was mainly segregated at prior austenite grain boundaries in the carburized layer, which weakened grain boundaries to induce the intergranular fracture. In order to solve the intergranular facture problem, the MLS sheet was tempered at 200 °C. The stress-strain curve of the tempered MLS sheet lay between those of the HPF and Hadfield sheets, and a rule of mixtures was roughly satisfied. Tensile properties of the MLS sheet were dramatically improved after the tempering, and the intergranular fracture was erased completely. In particular, the yield strength up to 1073 MPa along with the high strain hardening and excellent ductility of 32.4% were outstanding because the yield strength over 1 GPa was hardly achieved in conventional austenitic steels.

  1. Thermoelectric properties of n-type Bi{sub 2}(Te{sub 1{minus}x}Se{sub x}){sub 3} fabricated by mechanical alloying and hot pressing

    Energy Technology Data Exchange (ETDEWEB)

    Kim, H J; Choi, J S; Oh, T S; Hyun, D B

    1997-07-01

    Thermoelectric properties of polycrystalline Bi{sub 2}(Te{sub 1{minus}x}Se{sub x}){sub 3} (0.05 {le} x {le} 0.25), fabricated by mechanical alloying and hot pressing, have been investigated. Formation of n-type Bi{sub 2}(Te{sub 0.9}Se{sub 0.1}){sub 3} alloy powders was completed by mechanical alloying for 3 hours at ball-to-material ratio of 5:1, and processing time for Bi{sub 2}(Te{sub 1{minus}x}Se{sub x}){sub 3} formation increased with Bi{sub 2}Se{sub 3} content x. Figure-of-merit of Bi{sub 2}(Te{sub 0.9}Se{sub 0.1}) was markedly increased by hot pressing at temperatures above 450 C, and maximum value of 1.9 x 10{sup {minus}3}/K was obtained by hot pressing at 550 C. With addition of 0.015 wt% Bi as acceptor dopant, figure-of-merit of Bi{sub 2}(Te{sub 0.9}Se{sub 0.1}){sub 3} was hot pressed at 550 C, could be improved to 2.1 x 10{sup {minus}3}/K. When Bi{sub 2}(Te{sub 1{minus}x}Se{sub x}){sub 3} was hot pressed at 550 C, figure-of-merit increased from 1.14 x 10{sup {minus}3}/K to 1.92 x 10{sup {minus}3}/K with increasing Bi{sub 2}Se{sub 3} content x from 0.05 to 0.15, and then decreased to 1.30 x 10{sup {minus}3}/K for x = 0.25 composition.

  2. Isostatic Model and Isostatic Gravity Anomalies of the Arabian Plate and Surroundings

    OpenAIRE

    M. K. Kaban; Sami El Khrepy; Nassir Al-Arifi

    2016-01-01

    The isostatic modeling represents one of the most useful ‘‘geological’’ reduction methods of the gravity field. With the isostatic correction, it is possible to remove a significant part of the effect of deep density heterogeneity, which dominates in the Bouguer gravity anomalies. Although there exist several isostatic compensation schemes, it is usually supposed that a choice of the model is not an important factor to first order, since the total weight of compensating m...

  3. Transformation plasticity and hot pressing

    International Nuclear Information System (INIS)

    Chaklader, A.C.D.

    1975-01-01

    The transformation plasticity during the phase transition of quartz to cristobalite, monoclinic reversible tetragonal of zirconia, metakaolin to a spinel phase, and brucite to periclase was investigated by studying their compaction characteristics. Viscous flow was found to be the predominant mechanism of mass transport (after an initial particle rearrangement stage) in the case of quartz to cristobalite phase change where the transformation was associated with the formation of an intermediate amorphous silica phase. The results on the monoclinic reversible tetragonal transformation of zirconia indicated that it is most likely controlled by internal strain induced by the stress associated with the volume change (ΔV/V) and the flow stress of the weaker phase. Particle movement and deformation of the weaker phase (possibly tetragonal) may be the manifestation of this plasticity. The plasticity in the case of metakaolin to a spinel phase appeared to start before the exothermic reaction (generally encountered in a dta plot) and may be diffusion controlled. The plasticity encountered during brucite to periclase transformation may be the combined effect of disintegration of precursor particles, vapor-phase lubrication and some deformability of freshly formed very fine MgO particles

  4. U.S. Isostatic Residual Gravity Grid

    Data.gov (United States)

    National Oceanic and Atmospheric Administration, Department of Commerce — isores.bin - standard grid containing isostatic residual gravity map for U.S. Grid interval = 4 km. Projection is Albers (central meridian = 96 degrees West; base...

  5. Hot pressing of U-UC cermets and stoichiometric uranium monocarbide; Preparation par frittage sous charge de cermets U-UC et de monocarbure stoechiometrique

    Energy Technology Data Exchange (ETDEWEB)

    Dubuisson, J; Houyvet, A; Le Boulbin, E; Lucas, R; Moranville, C [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

    1958-07-01

    High density fuels, either in uranium monocarbide or in U-UC cermets have been prepared on laboratory-scale, by hot pressing of mixtures of uranium powder and graphite in suitable proportions. Uranium powder is prepared by calcium reduction of UO{sub 2} followed by an acetic leaching at low temperature. An adequate protection-treatment permits the manipulation of the powder in the open air. Uranium and Graphite powders are intimately mixed and then hot pressed in a double effect graphite die at a temperature of 900-1000 deg. C under a charge of 200 kg/cm{sup 2} during 3 hours. A special design of the die avoids the breaking of the graphite during the sintering. In this way, samples are prepared, the characteristics of which are: 1) {+-} 5 pour cent of homogeneity for a ratio height/diameter = 2. 2) almost theoretical density (98 pour cent) 3) low concentration of unreacted carbon (heat treatment of stoichiometric monocarbide can be useful for completion of reaction) 4) the micrographic examination shows: - a network of monocarbide surrounding uranium in the case of low concentration cermets (<2,5 per cent C) - two networks intimately mixed for high concentration cermets (<2,5 per cent C) - a fine grain structure for the monocarbide (10 u). 5) In every case, the X rays examinations show a fine grain structure without any orientation, and no UC{sub 2}. Some indications are given on the physical (thermal cycling, conductibility) and chemical properties (corrosion, reaction with cladding materials). (author)Fren. [French] Une methode de preparation de combustibles de haute densite, soit en monocarbure d'uranium, soit en cermets U-UC, a ete mise au point au laboratoire. Il s'agit du frittage sous charge de melanges de poudres d'uranium et de graphite en proportion convenable. La poudre d'uranium est elaboree par calciothermie de l'oxyde UO{sub 2} suivie d'un lavage acetique a basse temperature. Un traitement de protection adequat pe sa manipulation a l'air. Les poudres

  6. On the Role of Processing Parameters in Producing Recycled Aluminum AA6061 Based Metal Matrix Composite (MMC-AlR) Prepared Using Hot Press Forging (HPF) Process.

    Science.gov (United States)

    Ahmad, Azlan; Lajis, Mohd Amri; Yusuf, Nur Kamilah

    2017-09-19

    Solid-state recycling, which involves the direct recycling of scrap metal into bulk material using severe plastic deformation, has emerged as a potential alternative to the conventional remelting and recycling techniques. Hot press forging has been identified as a sustainable direct recycling technique that has fewer steps and maintains excellent material performance. An experimental investigation was conducted to explore the hardness and density of a recycled aluminum-based metal matrix composite by varying operating temperature and holding time. A mixture of recycled aluminum, AA6061, and aluminum oxide were simultaneously heated to 430, 480, and 530 °C and forged for 60, 90, and 120 min. We found a positive increase in microhardness and density for all composites. The hardness increased approximately 33.85%, while density improved by about 15.25% whenever the temperature or the holding time were increased. Based on qualitative analysis, the composite endures substantial plastic deformation due to the presence of hardness properties due to the aluminum oxide embedded in the aluminum matrix. These increases were significantly affected by the operating temperature; the holding time also had a subordinate role in enhancing the metal matrix composite properties. Furthermore, in an effort to curb the shortage of primary resources, this study reviewed the promising performance of secondary resources produced by using recycled aluminum and aluminum oxide as the base matrix and reinforcement constituent, respectively. This study is an outline for machining practitioners and the manufacturing industry to help increase industry sustainability with the aim of preserving the Earth for our community in the future.

  7. On the Role of Processing Parameters in Producing Recycled Aluminum AA6061 Based Metal Matrix Composite (MMC-AlR Prepared Using Hot Press Forging (HPF Process

    Directory of Open Access Journals (Sweden)

    Azlan Ahmad

    2017-09-01

    Full Text Available Solid-state recycling, which involves the direct recycling of scrap metal into bulk material using severe plastic deformation, has emerged as a potential alternative to the conventional remelting and recycling techniques. Hot press forging has been identified as a sustainable direct recycling technique that has fewer steps and maintains excellent material performance. An experimental investigation was conducted to explore the hardness and density of a recycled aluminum-based metal matrix composite by varying operating temperature and holding time. A mixture of recycled aluminum, AA6061, and aluminum oxide were simultaneously heated to 430, 480, and 530 °C and forged for 60, 90, and 120 min. We found a positive increase in microhardness and density for all composites. The hardness increased approximately 33.85%, while density improved by about 15.25% whenever the temperature or the holding time were increased. Based on qualitative analysis, the composite endures substantial plastic deformation due to the presence of hardness properties due to the aluminum oxide embedded in the aluminum matrix. These increases were significantly affected by the operating temperature; the holding time also had a subordinate role in enhancing the metal matrix composite properties. Furthermore, in an effort to curb the shortage of primary resources, this study reviewed the promising performance of secondary resources produced by using recycled aluminum and aluminum oxide as the base matrix and reinforcement constituent, respectively. This study is an outline for machining practitioners and the manufacturing industry to help increase industry sustainability with the aim of preserving the Earth for our community in the future.

  8. Isostatic Model and Isostatic Gravity Anomalies of the Arabian Plate and Surroundings

    Science.gov (United States)

    Kaban, Mikhail K.; El Khrepy, Sami; Al-Arifi, Nassir

    2016-04-01

    The isostatic modeling represents one of the most useful "geological" reduction methods of the gravity field. With the isostatic correction, it is possible to remove a significant part of the effect of deep density heterogeneity, which dominates in the Bouguer gravity anomalies. Although there exist several isostatic compensation schemes, it is usually supposed that a choice of the model is not an important factor to first order, since the total weight of compensating masses remains the same. We compare two alternative models for the Arabian plate and surrounding area. The Airy model gives very significant regional isostatic anomalies, which cannot be explained by the upper crust structure or disturbances of the isostatic equilibrium. Also, the predicted "isostatic" Moho is very different from existing seismic observations. The second isostatic model includes the Moho, which is based on seismic determinations. Additional compensation is provided by density variations within the lithosphere (chiefly in the upper mantle). According to this model, the upper mantle under the Arabian Shield is less dense than under the Platform. In the Arabian platform, the maximum density coincides with the Rub' al Khali, one of the richest oil basin in the world. This finding agrees with previous studies, showing that such basins are often underlain by dense mantle, possibly related to an eclogite layer that has caused their subsidence. The mantle density variations might be also a result of variations of the lithosphere thickness. With the combined isostatic model, it is possible to minimize regional anomalies over the Arabian plate. The residual local anomalies correspond well to tectonic structure of the plate. Still very significant anomalies, showing isostatic disturbances of the lithosphere, are associated with the Zagros fold belt, the collision zone of the Arabian and Eurasian plates.

  9. Idaho Batholith Study Area Isostatic Gravity Grid

    Data.gov (United States)

    National Oceanic and Atmospheric Administration, Department of Commerce — A 2 kilometer isostatic gravity grid for the Idaho batholith study area. Number of columns is 331 and number of rows is 285. The order of the data is from the lower...

  10. Comparison of various isostatic marine gravity disturbances

    Indian Academy of Sciences (India)

    due to the fact that the same isostatic principle is applied in both these definitions expect for assuming a local (in the ..... Gladkikh V and Tenzer R 2011 A mathematical model of the ... and its Gravity Field; McGraw-Hill Book Company, Inc.

  11. Isostatic models and isostatic gravity anomalies of the Arabian plate and surroundings

    Science.gov (United States)

    Kaban, Mikhail K.; El Khrepy, Sami; Al-Arifi, Nassir

    2015-04-01

    Isostaic anomalies represent one of the most useful "geological" reduction of the gravity field. With the isostatic correction it is possible to remove a significant part of the effect of deep density heterogeneity, which dominates in the Bouguer gravity anomalies. This correction is based on the fact that a major part of the near-surface load is compensated by variations of the lithosphere boundaries (chiefly the Moho and LAB) and by density variations within the crust and upper mantle. It is usually supposed that it is less important to a first order, what is the actual compensation model when reducing the effect of compensating masses, since their total weight is exactly opposite to the near-surface load. We compare several compensating models for the Arabian plate and surrounding area. The Airy model gives very significant regional isostatic anomalies, which can not be explained by the upper crust structure or disturbances of the isostatic equilibrium. Also the predicted "isostatic" Moho is very different from the existing observations. The second group of the isostatic models includes the Moho, which is based on existing seismic determinations. Additional compensation is provided by density variations within the lithosphere (chiefly in the upper mantle). In this way we minimize regional anomalies over the Arabian plate. The residual local anomalies well correspond to tectonic structure of the plate. Still very significant anomalies are associated with the Zagros fold belt, the collision zone of the Arabian and Eurasian plates.

  12. Isostatic model for the Tharsis province, Mars

    International Nuclear Information System (INIS)

    Sleep, N.H.; Phillips, R.J.

    1979-01-01

    A crust-upper mantle configuration is proposed for the Tharsis province of Mars which is isostatic and satisfies the observed gravity data. The model is that of a low density upper mantle compensating loads at both the surface and crust-mantle boundary. Solutions are found for lithospheric thickness greater than about 300 km, for which the stress differences are less than 750 bars. This model for Tharsis is similar to the compensation mechanism under the Basin and Range province of the western United States. These provinces also compare favorably in the sense that they are both elevated regions of extensional tectonics and extensive volcanism

  13. 2.5-min Isostatic Gravity Grid for the United States

    Data.gov (United States)

    National Oceanic and Atmospheric Administration, Department of Commerce — The 2.5-min isostatic gravity data set was produced by regridding the 4-km residual isostatic gravity grid of the U.S. The isostatic residual gravity grid was...

  14. Al_2O_3/PVdF-HFP-CMC/PE separator prepared using aqueous slurry and post-hot-pressing method for polymer lithium-ion batteries with enhanced safety

    International Nuclear Information System (INIS)

    Deng, Yaoming; Song, Xiaona; Ma, Zhen; Zhang, Xinhe; Shu, Dong; Nan, Junmin

    2016-01-01

    A composite separator is prepared to improve the safety of lithium ion batteries (LIBs) based on a gravure coating aqueous slurry and post-hot-pressing method. An environmentally friendly aqueous slurry with an Al_2O_3 ceramic holder and polyvinylidene difluoride-hexafluoropropylene (PVdF-HFP) and carboxymethyl cellulose (CMC) dual-binders is coated on a polyolefin (PE) substrate to form a prototype Al-PHC/PE separator. Then, after assembling the separator in the batteries and hot-pressing at 70 °C and 0.8 MPa for 3 h, the granular PVdF-HFP is transformed into a colloidal structure containing an electrolyte, which can binds the Al_2O_3 nanoparticles together and increases the battery hardness. Compared with a PE separator (9 μm), the Al-PHC/PE-2 separator (12 μm, with a Al_2O_3/PVdF-HFP weight ratio of 7/3) displays a comparative ionic conductivity of 9.3 × 10"−"4 S cm"−"2 and exhibits no obvious thermal deformation at 110 °C for 60 min. All of the batteries assembled with Al-PHC/PE-2 separators passed nail penetration and impact tests. In addition, the capacity retention increases from 83.4% to 87.6% when the battery is assembled with Al-PHC/PE-2 instead of a PE separator and charge-discharged at 0.7C/1.0C for 350 cycles. The enhanced safety and cycle performance indicate the promising prospect of Al-PHC/PE separators in LIBs.

  15. The kinetics of dolomite reaction rim growth under isostatic and non-isostatic pressure conditions

    Science.gov (United States)

    Helpa, V.; Rybacki, E.; Morales, L. G.; Abart, R.; Dresen, G. H.

    2013-12-01

    During burial and exhumation, rocks are simultaneously exposed to metamorphic reactions and tectonic stresses. Therefore, the reaction rate of newly formed minerals may depend on chemical and mechanical driving forces. Here, we investigate the reaction kinetics of dolomite (CaMg[CO3]2) rim growth by solid-state reactions experiments on oriented calcite (CaCO3) and magnesite (MgCO3) single crystals under isostatic and non-isostatic pressure conditions. Cylindrical samples of 3-5 mm length and 7 mm diameter were drilled and polished perpendicular to the rhombohedral cleavage planes of natural clear crystals. The tests were performed using a Paterson-type deformation apparatus at P = 400 MPa confining pressure, temperatures, T, between 750 and 850°C, and reaction durations, t, of 2 - 146 h to calculate the kinetic parameters of dolomite rim growth under isostatic stress conditions. For non-isostatic reaction experiments we applied in addition differential stresses, σ, up to 40 MPa perpendicular to the contact interface at T = 750°C for 4 - 171 h duration, initiating minor inelastic deformation of calcite. The thickness of the resulting dolomite reaction rims increases linearly with the square root of time, indicating a diffusion-controlled reaction. The rims consist of two different textural domains. Granular dolomite grains (≈ 2 -5 μm grain size) form next to calcite and elongated palisade-shaped grains (1-6 μm diameter) grow perpendicular to the magnesite interface. Texture measurements with the electron backscatter diffraction technique indicate that the orientations of dolomite grains are mainly influenced by the orientation of the calcite educt crystal, in particular in the granular rim. To some extent, the texture of dolomite palisades is also influenced by the orientation of magnesite. The thickness of the two individual layers increases with temperature. At 400 MPa isostatic pressure, T = 750°C and t = 29 hours, a 5 μm thick granular dolomite layer

  16. Uncertainty in Greenland glacial isostatic adjustment

    DEFF Research Database (Denmark)

    Milne, G. A.; Lecavalier, B.; Kjeldsen, K. K.

    It is well known that the interpretation of geodetic data in Greenland to constrain recent ice mass changes requires knowledge of isostatic land motion associated with past changes in the ice sheet. In this talk we will consider a variety of factors that limit how well the signal due to past mass...... of the GIA model on predictions of land motion and gravity changes. The sensitivity of model output to plausible variations in both depth-dependent and lateral viscosity structure will be considered. With respect to the ice model, we will compare the relative contributions of loading during key periods...... of the ice history with a focus on the past few thousand years. In particular, we will show predictions of contemporary land motion and gravity changes due to loading changes following the Little Ice Age computed using a new reconstruction of ice thickness changes based largely on empirical data. A primary...

  17. Isostatic models and isostatic gravity anomalies of the Arabian plate and surroundings

    OpenAIRE

    M. K. Kaban; Sami El Khrepy; Nassir Al-Arifi

    2015-01-01

    Isostaic anomalies represent one of the most useful “geological” reduction of the gravity field. With the isostatic correction it is possible to remove a significant part of the effect of deep density heterogeneity, which dominates in the Bouguer gravity anomalies. This correction is based on the fact that a major part of the near-surface load is compensated by variations of the lithosphere boundaries (chiefly the Moho and LAB) and by density variations within the crust and upper man...

  18. MANU. Isostatic compression of buffer blocks. Small scale

    International Nuclear Information System (INIS)

    Laaksonen, R.

    2010-01-01

    between density, moisture, degree of saturation and strength of the specimen. Also tests should be carried out to produce information on homogeneity of large specimens and information on the effect of the isostatic pressure and duration of the compression. Tests should be done to show that also granulated material follows the found water content density relationship and to study the material loss due to machining to the final block dimensions. This must be done with large samples. Techniques like vibration or vacuum - separately or combined - may be used to precompact the material in the mould to reduce both mould size and contraction of the sample and tool material during pressing. It may also be possible to reshape the mould with a vacuum inside. Tests should also be carried out to study the swelling capacity of materials compressed to different densities under different water contents - both swelling pressure and volume increase capacity due to swelling. (orig.)

  19. 反应热压制备TiC/Al复合材料的形成途径研究%Investigation on Formation Path of TiC/Al Composite Obtained by Reactive Hot-pressing Technology

    Institute of Scientific and Technical Information of China (English)

    宋谋胜; 冉茂武

    2012-01-01

    利用场激发反应热压合成技术研究了Al-Ti-C混合粉末体系制备TiC/Al产物的过程与致密性,并结合DSC实验分析了该体系合成TiC相的形成途径.结果表明,采用反应热压合成法完全能够制备较致密的TiC/Al复合材料.该体系形成TiC相的反应过程为:Ti(s)+3Al(s)=TiAl3(s)→Al(s)=Al(l) →Ti(s)+3 Al(l)=TiAl3(s)→ TiAl3(s)=TiAl3(1)→TiAl3(l)+C(s)=TiC(s)+ Al((l)).混合粉末中的Al不仅作为稀释剂降低体系的反应温度而细化TiC晶粒,还作为反应剂参与了整个反应进程.%Utilizing the field activation reactive hot-pressing (RHP) technology, the process and densificatian of TiC/Al products obtained from Al-Ti-C mixtures system were investigated, eoupied with the DSC experiment to analyze iht formation path of TiC phase in this system. The results show that the dense TiC/Al composite can be fully fabricated by the reactive hot-pressing method. The reaction process of the Al-Ti-C system to form TiC phase can be expressed: Ti(s)+3Al(s)= TiAl3(s) →Al(s)=Al(1)→Ti(,s)+3Al(1)=TiAl,(s)→TiAl3(s)=TiAl3(1)→TiAl3(l)+C(s)=T(C(s)+Al(1). Al in the mixtures plays an important role in serving not only as a diluent to decrease the reaction temperature and thus to refine the TiC grains, but also as an intermediate reactant to participate in the whole reaction process.

  20. Industrial production of insulators using isostatic compaction method

    Energy Technology Data Exchange (ETDEWEB)

    Drugoveiko, O.P.; Ermolaeva, L.V.; Koren' , M.G.; Kreimer, B.D.; Panichev, G.I.; Ponomarev, A.P.; Rutkovskii, V.N.

    1985-07-01

    The process of shaping ceramic products from powders using isostatic compaction method is finding increasing industrial application. The production of electrical-engineering porcelain using isostatic compaction method is, according to the authors, a promising direction since this method permits one to obtain large and complex shaped products having uniform density distribution. The authors introduce an automatic isostatic compaction line at the ''Proletarii'' Factory for the production of the IOS-110-20000UKhL, T1 type insulators having the described dimensions. According to the technological process developed at the ''Elektrokeramika'' Production Complex, insulators were manufactured on the isostatic compaction line from the G-33 mass. Presspowder having a moisture content of 0.3-0.6% and a particle size of 90-160 micrometers was obtained in a spray dryer using disk spraying. The authors studied saturability by moisture of the powder obtained.

  1. Finite element concept to derive isostatic residual maps ...

    Indian Academy of Sciences (India)

    A new space-domain operator based on the shape function concept of finite element analysis has been developed to derive the ... not require explicit assumptions on isostatic models. Besides .... This information is implicit in the Bouguer ...

  2. The isostatic state of Mead crater

    Science.gov (United States)

    Banerdt, W. B.; Konopliv, A. S.; Rappaport, N. J.; Sjogren, W. L.; Grimm, R. E.; Ford, P. G.

    1994-01-01

    We have analyzed high-resolution Magellan Doppler tracking data over Mead crater, using both line-of-sight and spherical harmonic methods, and have found a negative gravity anomaly of about 4-5 mgal (at spacecraft altitude, 182 km). This is consistent with no isostatic compensation of the present topography; the uncertainty in the analysis allows perhaps as much as 30% compensation at shallow dpeths (approximately 25 km). This is similar to observations of large craters on Earth, which are not generally compensated, but contrasts with at least some lunar basins which are inferred to have large Moho uplifts and corresponding positive Bouguer anomalies. An uncompensated load of this size requires a lithosphere with an effective elastic lithosphere thickness greater than 30 km. In order for the crust-mantle boundary not to have participated in the deformation associated with the collapse of the transient cavity during the creation of the crater, the yield strength near the top of the mantle must have been significantly higher on Earth and Venus than on the Moon at the time of basin formation. This might be due to increased strength against frictional sliding at the higher confining pressures within the larger planets. Alternatively, the thinner crusts of Earth and Venus compared to that of the Moon may result in higher creep strength of the upper mantle at shallower depths.

  3. Control system for glassing hot presses

    Energy Technology Data Exchange (ETDEWEB)

    Howell, J.F.

    1984-06-13

    A software programmable control system has been developed that automates the glass fusing process used in the production of semiconductor thermopile elements. The new control system replaces an older, mostly manual, electromechanical design. This report describes the new control design and its functional features.

  4. Fabrication of Al-based composites reinforced with in situ devitrified Al{sub 84}Ni{sub 8.4}Y{sub 4.8}La{sub 1.8}Co{sub 1} particles by hot pressing consolidation

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Qing, E-mail: buaayq00@gmail.com; Zhang, Yitan; Zhang, Haiping; Zheng, Ruixiao; Xiao, Wenlong; Ma, Chaoli, E-mail: machaoli@buaa.edu.cn

    2015-11-05

    In this study, Al{sub 84}Ni{sub 8.4}Y{sub 4.8}La{sub 1.8}Co{sub 1} particles reinforced Al-based composites were prepared by hot pressing sintering and subsequent hot extrusion. The glassy powders were produced by gas atomization and then employed to mechanical milling. After hot pressing sintering, the nano-scale intermetallic compounds precipitated from metallic glass matrix due to higher temperature than super-cooled liquid region. The mechanical properties of 2024 alloy were improved by addition of glassy particles. The ultimate compressive stress increased from 482 MPa for 2024 alloy to 545 MPa, 627 MPa and 735 MPa for composites with 20 w.t.% 40 w.t.% and 60 w.t.% glassy powders addition, respectively, together with considerable fracture strain ranging between 2.9% and 13.6%. And the mechanical properties could be predicted by using the Rule of Mixture, which predicts the mechanical properties of the bulks from the volume weighed average of the constituent properties. - Highlights: • The composites are fabricate by hot pressing and extrusion. • The single phase of amorphous alloy is obtained by sieving. • The nano-scale compounds precipitates from glassy matrix. • The compressive strength reaches to the value of 735 MPa. • The strength can fit well with rule of mixture.

  5. Press Start

    Science.gov (United States)

    Harteveld, Casper

    This level sets the stage for the design philosophy called “Triadic Game Design” (TGD). This design philosophy can be summarized with the following sentence: it takes two to tango, but it takes three to design a meaningful game or a game with a purpose. Before the philosophy is further explained, this level will first delve into what is meant by a meaningful game or a game with a purpose. Many terms and definitions have seen the light and in this book I will specifically orient at digital games that aim to have an effect beyond the context of the game itself. Subsequently, a historical overview is given of the usage of games with a serious purpose which starts from the moment we human beings started to walk on our feet till our contemporary society. It turns out that we have been using games for all kinds of non-entertainment purposes for already quite a long time. With this introductory material in the back of our minds, I will explain the concept of TGD by means of a puzzle. After that, the protagonist of this book, the game Levee Patroller, is introduced. Based on the development of this game, the idea of TGD, which stresses to balance three different worlds, the worlds of Reality, Meaning, and Play, came into being. Interested? Then I suggest to quickly “press start!”

  6. Application of isostatic gravity anomaly in the Yellow Sea area

    Science.gov (United States)

    Hao, Z.; Qin, J.; Huang, W.; Wu, X.

    2017-12-01

    In order to study the deep crustal structure of the Yellow Sea area, we used the Airy-Heiskanen model to calculate the isostatic gravity anomaly of this area. Based on the Bouguer gravity anomaly and water depth data of this area, we chose the calculating parameters as standard crustal thickness 30 km, crust-mantle density difference 0.6g/cm3and grid spacing 0.1°×0.1°. This study reveals that there are six faults and four isostatic negative anomalies in the study area. The isostatic anomalies in much of Yellow Sea areas give priority to those with positive anomalies. The isostatic anomalies in North Yellow Sea are higher than South Yellow Sea with Jiashan-Xiangshui fault as the boundary. In the north of the study area, isostatic anomalies are characterized by large areas of positive anomaly. The change is relatively slow, and the trends give priority to the trend NE or NEE. In the middle of the north Yellow Sea basin, there is a local negative anomaly, arranged as a string of beads in NE to discontinuous distribution. Negative anomaly range is small, basically corresponds to the region's former Cenozoic sedimentary basin position. To the south of Jiashan-Xiangshui fault and west of Yellow Sea eastern margin fault, including most of the south Yellow Sea and Jiangsu province, the isostatic anomalies are lower. And the positive and negative anomalies are alternative distribution, and negative anomaly trap in extensive development. The trends give priority to NE, NEE, both to the NW. On the basis of the characteristics of isostatic gravity anomalies, it is concluded that the Yellow Sea belongs to continental crustal isostatic area whose isostatic anomalies is smooth and slow. ReferencesHeiskanen, W. A., F. A. V. Meinesz, and S. A. Korff (1958), The Earth and Its Gravity Field, McGraw-Hill, New York. Meng, X. J., X. H. Zhang, and J. Y. Yang (2014), Geophysical survey in eastern China seas and the characteristics of gravity and magnetic fields, Marine Geoglogy

  7. Annealing effects on the microstructure and mechanical properties of hot-rolled 14Cr-ODS steel

    International Nuclear Information System (INIS)

    Gao, R.; Zhang, T.; Ding, H.L.; Jiang, Y.; Wang, X.P.; Fang, Q.F.; Liu, C.S.

    2015-01-01

    The oxide dispersion strengthened ferritic steels with nominal composition (weight percent) of Fe–14Cr–2W-0.5Ti-0.06Si-0.2V-0.1Mn-0.05Ta-0.03C-0.3Y_2O_3 were fabricated by sol–gel method, mechanical alloying, and hot isostatic pressing techniques. The evolution of microstructure and mechanical properties of the hot-rolled specimens with heat treatment was investigated. Tensile strength and hardness of hot-rolled ODS steel are significantly enhanced due to the formation of mechanical twins and high density dislocations. Uniformly dispersed oxide particles (10–40 nm) and fine-grained structure (200–400 nm) are responsible for the superior mechanical properties of the hot-rolled specimen annealed between 650 °C and 850 °C. With further increasing annealing temperature, the grain size of the hot-rolled specimens increases while the size of oxide particles decreases, which leads to lower strength and hardness but better ductility. The tensile strength and total elongation of samples in the rolling direction are higher than those in the transverse direction after the same treatments owing to the grain anisotropy induced by the large mechanical deformation.

  8. Annealing effects on the microstructure and mechanical properties of hot-rolled 14Cr-ODS steel

    Science.gov (United States)

    Gao, R.; Zhang, T.; Ding, H. L.; Jiang, Y.; Wang, X. P.; Fang, Q. F.; Liu, C. S.

    2015-10-01

    The oxide dispersion strengthened ferritic steels with nominal composition (weight percent) of Fe-14Cr-2W-0.5Ti-0.06Si-0.2V-0.1Mn-0.05Ta-0.03C-0.3Y2O3 were fabricated by sol-gel method, mechanical alloying, and hot isostatic pressing techniques. The evolution of microstructure and mechanical properties of the hot-rolled specimens with heat treatment was investigated. Tensile strength and hardness of hot-rolled ODS steel are significantly enhanced due to the formation of mechanical twins and high density dislocations. Uniformly dispersed oxide particles (10-40 nm) and fine-grained structure (200-400 nm) are responsible for the superior mechanical properties of the hot-rolled specimen annealed between 650 °C and 850 °C. With further increasing annealing temperature, the grain size of the hot-rolled specimens increases while the size of oxide particles decreases, which leads to lower strength and hardness but better ductility. The tensile strength and total elongation of samples in the rolling direction are higher than those in the transverse direction after the same treatments owing to the grain anisotropy induced by the large mechanical deformation.

  9. Flexural strength and the probability of failure of cold isostatic pressed zirconia core ceramics.

    Science.gov (United States)

    Siarampi, Eleni; Kontonasaki, Eleana; Papadopoulou, Lambrini; Kantiranis, Nikolaos; Zorba, Triantafillia; Paraskevopoulos, Konstantinos M; Koidis, Petros

    2012-08-01

    The flexural strength of zirconia core ceramics must predictably withstand the high stresses developed during oral function. The in-depth interpretation of strength parameters and the probability of failure during clinical performance could assist the clinician in selecting the optimum materials while planning treatment. The purpose of this study was to evaluate the flexural strength based on survival probability and Weibull statistical analysis of 2 zirconia cores for ceramic restorations. Twenty bar-shaped specimens were milled from 2 core ceramics, IPS e.max ZirCAD and Wieland ZENO Zr, and were loaded until fracture according to ISO 6872 (3-point bending test). An independent samples t test was used to assess significant differences of fracture strength (α=.05). Weibull statistical analysis of the flexural strength data provided 2 parameter estimates: Weibull modulus (m) and characteristic strength (σ(0)). The fractured surfaces of the specimens were evaluated by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). The investigation of the crystallographic state of the materials was performed with x-ray diffraction analysis (XRD) and Fourier transform infrared (FTIR) spectroscopy. Higher mean flexural strength (Plines zones). Both groups primarily sustained the tetragonal phase of zirconia and a negligible amount of the monoclinic phase. Although both zirconia ceramics presented similar fractographic and crystallographic properties, the higher flexural strength of WZ ceramics was associated with a lower m and more voids in their microstructure. These findings suggest a greater scattering of strength values and a flaw distribution that are expected to increase failure probability. Copyright © 2012 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

  10. Chemical composition and oxidative stability of jussara (Euterpe edulis M.) oil extracted by cold and hot mechanical pressing; Composición química y estabilidad oxidativa del aceite de jussara (Euterpe edulis M.) extraído mediante prensado mecánico en frío y en caliente

    Energy Technology Data Exchange (ETDEWEB)

    Da Cunha, A.L.A.; Freitas, S.P.; Godoy, R.L.O.; Cabral, L.M.C.; Tonon, R.V.

    2017-07-01

    The aim of this work was to evaluate the effect of mechanical pressing on jussara oil yield, oxidative stability and carotenoid profile with or without heat application. Firstly, jussara pulp was centrifuged for juice extraction, and the resulting cake was dried until reaching 10% moisture content. Then, oil extraction was performed in an expeller press at 25 ºC (cold pressing) and at 50 ºC (hot pressing). The process performance was evaluated by the oil yield, and the crude jussara oil was characterized for fatty acid composition, acid value, carotenoid profile and oxidative stability. Jussara oil contained 74% unsaturated fatty acids, mainly oleic and linoleic acids (48% and 24%, respectively). The oil yield was almost twice as high for the hot process as compared to the cold one. Additionally, hot pressing resulted in 25% higher total carotenoid content as compared to cold pressing, with β-carotene as the most abundant one. Hot and cold pressing showed no difference in oil oxidative stability and fatty acid composition. [Spanish] El objetivo de este estudio fue evaluar el efecto del calor sobre el rendimiento del aceite, la estabilidad oxidativa y el perfil de carotenoides del aceite de Jussara extraído por prensado mecánico. En primer lugar, se centrifugó la pulpa de jussara para la extracción del zumo, y la torta resultante se secó para alcanzar el contenido de humedad de 10%. Posteriormente, la extracción del aceite se realizó en una prensa a 25 °C (prensado en frío) y a 50 °C (prensado en caliente). El desarrollo del proceso fue evaluado mediante el rendimiento de aceite y en bruto y éste se caracterizó mediante la composición en ácidos grasos, índice de acidez, perfil de carotenoides y la estabilidad oxidativa. El aceite de jussara presentó un 74% de ácidos grasos insaturados, principalmente ácidos oleico y linoleico (48% y 24%, respectivamente). El rendimiento del aceite para el proceso en caliente fue casi el doble, en comparaci

  11. Jamming of soft particles: geometry, mechanics, scaling and isostaticity

    International Nuclear Information System (INIS)

    Van Hecke, M

    2010-01-01

    Amorphous materials as diverse as foams, emulsions, colloidal suspensions and granular media can jam into a rigid, disordered state where they withstand finite shear stresses before yielding. Here we review the current understanding of the transition to jamming and the nature of the jammed state for disordered packings of particles that act through repulsive contact interactions and are at zero temperature and zero shear stress. We first discuss the breakdown of affine assumptions that underlies the rich mechanics near jamming. We then extensively discuss jamming of frictionless soft spheres. At the jamming point, these systems are marginally stable (isostatic) in the sense of constraint counting, and many geometric and mechanical properties scale with distance to this jamming point. Finally, we discuss current explorations of jamming of frictional and non-spherical (ellipsoidal) particles. Both friction and asphericity tune the contact number at jamming away from the isostatic limit, but in opposite directions. This allows one to disentangle the distance to jamming and the distance to isostaticity. The picture that emerges is that most quantities are governed by the contact number and scale with the distance to isostaticity, while the contact number itself scales with the distance to jamming. (topical review)

  12. The Darfur Swell, Africa: Gravity constraints on its isostatic compensation

    Science.gov (United States)

    Crough, S. Thomas

    The free-air gravity anomaly observed over the Darfur Swell is explainable by local isostatic balance with a root approximately 50 km deep on average. This root depth is similar to that inferred beneath other African domes and beneath oceanic midplate swells, suggesting that the Darfur Swell is a hotspot uplift created by lithospheric reheating.

  13. Finite element concept to derive isostatic residual maps

    Indian Academy of Sciences (India)

    A new space-domain operator based on the shape function concept of finite element analysis has been developed to derive the residual maps of the Gorda Plate of western United States. The technique does not require explicit assumptions on isostatic models. Besides delineating the Gorda Plate boundary, the residual ...

  14. Nickel powders shape effect upon their isostatic compaction behavior

    International Nuclear Information System (INIS)

    Cytermann, R.; Auguin, B.; Defresne, A.; Gilles, P.

    1975-01-01

    Two carbonyl nickel powders of the same purity, one spherical, the other of very irregular shape, were isostatically compacted at pressures from 0.5 to 13Kbars with two compacting speeds: 1Kbar/s and 1Kbar/15s. The influence of the powder shapes on the electrical resistivity, tensile strength and microcalorimetric measurements was studied [fr

  15. Finite element concept to derive isostatic residual maps ...

    Indian Academy of Sciences (India)

    These produce large regional lows that override or tend to mask the smaller anomalies originating from the mid and upper crustal geologic structures. The interpretation and understanding of these structures depend on how effectively the regional gravity anoma- lies are isolated so as to construct the isostatic residual maps.

  16. Jamming of soft particles: geometry, mechanics, scaling and isostaticity

    Energy Technology Data Exchange (ETDEWEB)

    Van Hecke, M, E-mail: mvhecke@physics.leidenuniv.n [Kamerlingh Onnes Laboratory, Leiden University, PO Box 9504, 2300 RA Leiden (Netherlands)

    2010-01-27

    Amorphous materials as diverse as foams, emulsions, colloidal suspensions and granular media can jam into a rigid, disordered state where they withstand finite shear stresses before yielding. Here we review the current understanding of the transition to jamming and the nature of the jammed state for disordered packings of particles that act through repulsive contact interactions and are at zero temperature and zero shear stress. We first discuss the breakdown of affine assumptions that underlies the rich mechanics near jamming. We then extensively discuss jamming of frictionless soft spheres. At the jamming point, these systems are marginally stable (isostatic) in the sense of constraint counting, and many geometric and mechanical properties scale with distance to this jamming point. Finally, we discuss current explorations of jamming of frictional and non-spherical (ellipsoidal) particles. Both friction and asphericity tune the contact number at jamming away from the isostatic limit, but in opposite directions. This allows one to disentangle the distance to jamming and the distance to isostaticity. The picture that emerges is that most quantities are governed by the contact number and scale with the distance to isostaticity, while the contact number itself scales with the distance to jamming. (topical review)

  17. ZrC Ceramics Prepared by Self-propagating High-temperature Synthesis/Single Action Pressing

    Directory of Open Access Journals (Sweden)

    CHENG Yong

    2017-01-01

    Full Text Available ZrC ceramics were prepared by mechanical axial compression of self-propagating high-temperature synthesis/single action pressing (SHS/SAP.The effects of pressure on microstructure and densification of the products,as well as the relationship between displacement/variation of the load curve and SHS reaction,were studied.The structure and properties of the products were investigated by XRD and SEM.In addition,the density was measured by the drain away liquid method.Meanwhile,universal testing machine was used to record the displacement and load curve alternations.The results indicate that products are mainly composed of ZrC phase,the process of exhaust are accelerated as the increasing of pressure as well,leading to the smaller size of porosity and crystal particles.Density manifested as an increasing pattern by the elevated pressure with no longer change at 80MPa.Due to the strong attenuation of pressure at the peak of temperature,the density of the production is only 65.7% in 120MPa.The end point of the SHS reaction and the plastic time of the products can be monitored by displacement and load curve.The results provide evidence for the application of self-propagating high-temperature synthesis/pseudo-hot isostatic pressing to further improve the density of ceramics.

  18. Theoretical and technical fundamentals of pressing porous powder articles of the complex shape

    International Nuclear Information System (INIS)

    Reut, O.; Piatsiushyk, Y.; Makarchuk, D.; Yakubouski, A.

    2001-01-01

    Intensification of technological processes, limited by the square of the surface of an active element porous powder field, is possible at the expense of magnification of the square of the surface of the latter by its addition. Thus the overall dimensions of such skew field are preserved. The analytical dependence of the factor of magnification of the surface K on geometrical parameters of a powder article of the complex shape is obtained. The optimization of these parameters in view of technological limitations for the maximization of K is carried out. The technique of calculating of the intense - deformed state of the powder skew field of the complex geometrical shape in the isostatic pressing is developed. The basic correlation permitting to calculate strain and deformation fields when pressing are gained. The technique of dry isostatic pressing of the article of the complex shape and the corresponding deforming instrument are developed. (author)

  19. Texturing of superconducting Bi-Pb-Sr-Ca-Cu-O ceramics by combining the effect of a magnetic field and hot pressing in one direction; Texturation des ceramiques supraconductrices Bi-Pb-Sr-Ca-Cu-O par combinaison des effets du champ magnetique et de la contrainte uniaxiale a haute temperature

    Energy Technology Data Exchange (ETDEWEB)

    Noudem, J G

    1995-10-27

    Superconducting Bi-(Pb)-Sr-Ca-Cu-O (Bi:2223) ceramics have a weak 77 K transport critical current density (Jc) due to porosity and the presence of misaligned platelets. In order to obtain higher critical current densities in these materials, it is necessary to increase their density and induce a preferential crystallographic orientation. We have developed a texturing process using solidification in a magnetic field combined with hot pressing. The experimental set-up provides a uniaxial pressure of 60 MPa and temperature up to 1100 deg C in a magnetic field of 8 T. Magnetic melt texturing (MMT) proved to be very effective in producing bulk oriented samples of polycrystalline Bi:2223 (crystallite c-axis oriented parallel to the field direction). These samples have Jc values of up to 1450 A/cm{sup 2} and a density of 5.1 g/cm{sup 3}. The texturing by hot pressing (HP) gives homogeneous, dense ({approx} 6 g/cm{sup 3}; 95 % of the theoretical limit) ceramics with a Jc of 2500 A/cm{sup 2}. Tapes of Ag/Bi:2223 provided by Alcatel Alsthom were also successful textured using HP. Finally we have demonstrated that the combination of solidification in a magnetic field with hot pressing (MMHPT) improves both the texture and density of the samples. Moreover the samples are very homogeneous and mechanically resistant. The 77 K transport critical current densities have values up to 3800 A/cm{sup 2} and 1100 A/cm{sup 2} along the (ab) and c-axis respectively. We have demonstrated that these samples are of potential use a current limiters. (author) 146 refs.

  20. PM-materials for hot working tools; PM-Werkstoffe fuer warmgehende Werkzeuge

    Energy Technology Data Exchange (ETDEWEB)

    Berns, H.; Broeckmann, C.; Theisen, W. [Bochum Univ. (Germany). Fakultaet fuer Maschinenbau; Wewers, B.

    2001-05-01

    Tools and wear parts for compacting tools are subjected to high abrasive wear and mechanical loading at elevated temperatures. MMC's based in iron- or nickel with hard particles are developed and investigated. The materials were manufactured from powders by hot isostatic pressing (HIP) and subsequently heat treated. Diffusion between hard phases and metal matrix brings about certain micro structures which were tested with respect to the resistance against sliding abrasion at room and elevated temperatures. Three-point bending tests and thermal cycling of the material was utilized to characterise the mechanical behaviour. Based on this results a toolkit for a roller press for briquetting was produced and brought into application. (orig.) [German] Werkzeuge und Verschleissteile fuer die Verarbeitung von mineralischen Guetern bei erhoehter Temperatur unterliegen sowohl hohem abrasivem Verschleiss als auch hohen mechanischen Lasten. Es werden hartphasenhaltige Verbundwerkstoffe auf Eisen- und Nickelbasis entwickelt und untersucht. Die Fertigung dieser MMC's erfolgt durch heiss isostatisches Pressen (HIP) und anschliessende Waermebehandlung. Durch Diffusion zwischen Hartphasen und Metallmatrix entstehen Gefuege, die bezueglich ihres Widerstandes gegen Abrasivverschleiss bei Raumtemperatur und gegen Korngleitverschliess bei erhoehter Temperatur geprueft werden. Zur Charakterisierung der mechanischen Eigeschaften werden Dreipunktbiegeversuche und thermsiche Ermuedungsversuche durchgefuehrt. Die gewonnenen Erkenntnisse werden genutzt, um einen Werkzeugsatz fuer eine Brikettierpresse herzustellen und in Einsatz zu bringen. (orig.)

  1. News/Press Releases

    Data.gov (United States)

    Office of Personnel Management — A press release, news release, media release, press statement is written communication directed at members of the news media for the purpose of announcing programs...

  2. Hot Flashes

    Science.gov (United States)

    Hot flashes Overview Hot flashes are sudden feelings of warmth, which are usually most intense over the face, neck and chest. Your skin might redden, as if you're blushing. Hot flashes can also cause sweating, and if you ...

  3. Reciprocating pellet press

    Science.gov (United States)

    Jones, Charles W.

    1981-04-07

    A machine for pressing loose powder into pellets using a series of reciprocating motions has an interchangeable punch and die as its only accurately machines parts. The machine reciprocates horizontally between powder receiving and pressing positions. It reciprocates vertically to press, strip and release a pellet.

  4. The Global University Press

    Science.gov (United States)

    Dougherty, Peter J.

    2012-01-01

    The modern world's understanding of American university press has long been shaped by university-press books. American university-press books are good international advertisements for the universities whose logos grace their spines. The growth of transnational scholarship and the expansion of digital communications networks are converging in ways…

  5. HOT 2015

    DEFF Research Database (Denmark)

    Hannibal, Sara Stefansen

    2016-01-01

    HOT samler og formidler 21 literacykyndiges bud på, hvad der er hot, og hvad der bør være hot inden for literacy – og deres begrundelser for disse bud.......HOT samler og formidler 21 literacykyndiges bud på, hvad der er hot, og hvad der bør være hot inden for literacy – og deres begrundelser for disse bud....

  6. WordPress Bible

    CERN Document Server

    Brazell, Aaron

    2010-01-01

    The WordPress Bible provides a complete and thorough guide to the largest self hosted blogging tool. This guide starts by covering the basics of WordPress such as installing and the principles of blogging, marketing and social media interaction, but then quickly ramps the reader up to more intermediate to advanced level topics such as plugins, WordPress Loop, themes and templates, custom fields, caching, security and more. The WordPress Bible is the only complete resource one needs to learning WordPress from beginning to end.

  7. WordPress Bible

    CERN Document Server

    Brazell, Aaron

    2011-01-01

    Get the latest word on the biggest self-hosted blogging tool on the marketWithin a week of the announcement of WordPress 3.0, it had been downloaded over a million times. Now you can get on the bandwagon of this popular open-source blogging tool with WordPress Bible, 2nd Edition. Whether you're a casual blogger or programming pro, this comprehensive guide covers the latest version of WordPress, from the basics through advanced application development. If you want to thoroughly learn WordPress, this is the book you need to succeed.Explores the principles of blogging, marketing, and social media

  8. Two layer powder pressing

    International Nuclear Information System (INIS)

    Schreiner, H.

    1979-01-01

    First, significance and advantages of sintered materials consisting of two layers are pointed out. By means of the two layer powder pressing technique metal powders are formed resulting in compacts with high accuracy of shape and mass. Attributes of basic powders, different filling methods and pressing techniques are discussed. The described technique is supposed to find further applications in the field of two layer compacts in the near future

  9. Isostatic compaction of beaker shaped bentonite blocks on the scale 1:4

    Energy Technology Data Exchange (ETDEWEB)

    Johannesson, Lars-Erik [Clay Technology AB, Lund (Sweden); Nord, Sven [Ifoe Ceramics AB, Bromoella (Sweden ); Pusch, Roland [Geodevelopment AB, Lund (Sweden); Sjoeblom, Rolf [AaF-Energikonsult AB, Stockholm (Sweden)

    2000-09-01

    The purpose of the present work is to test, on a scale of 1:4, the feasibility of manufacturing bentonite blocks by isostatic compaction for application as a buffer material in a repository for spent nuclear fuel. In order for the tests to be sensitive to any weaknesses of the method, the blocks were shaped as beakers. The scope included the following: 1. Preparation of powder: a. mixing of the bentonite and addition of water in predetermined amounts, b. sieving to remove any lumps generated; 2. Isostatic compaction: a. establishment of a separate laboratory for the handling of bentonite powder (weighing, mixing, filling, sampling and machining), b. development and design of equipment and procedures for compaction of bentonite to beaker-shaped specimens, c. compaction process operation, d. visual inspection; 3. Sampling and characterisation: a. extraction of samples from the blocks made, b. determination of water content, c. determination of density, d. determination of strain at maximum stress by means of bending tests, e. determination of tensile strength by means of bending tests, f. determination of geometries of the blocks prepared; 4. Post-treatment by means of machining: a. machining of blocks made, b. visual inspection; 5. Evaluation. The work went very smoothly. No significant obstacles or unexpected events were encountered. The conclusions are as follows: The conclusions drawn in this report from work on the (linear)scale of one to four are very relevant to the full scale. Mixing of bentonite powder as well as moistening can be carried out on a pilot scale with a good homogeneity and with maintained good quality of the press powder. The compaction of bentonite can be carried out in a similar manner to the present operation at Ifoe Ceramics AB. This implies a very efficient handling as well as a very efficient use of the time in the press which may account for a large proportion of the total cost. The blocks could readily be produced to reproducible

  10. Reduced activation ODS ferritic steel - recent development in high speed hot extrusion processing

    Energy Technology Data Exchange (ETDEWEB)

    Oksiuta, Zbigniew [Faculty of Mechanical Engineering, Bialystok Technical University (Poland); Lewandowska, Malgorzata; Kurzydlowski, Krzysztof [Faculty of Materials Science and Engineering, Warsaw University of Technology (Poland); Baluc, Nadine [Ecole Polytechnique Federale de Lausanne (EPFL), Centre de Recherches en Physique des Plasmas, Association Euratom-Confederation Suisse, Villigen PSI (Switzerland)

    2010-05-15

    The paper presents the microstructure and mechanical properties of an oxide dispersion strengthened (ODS), reduced activation, ferritic steel, namely the Fe-14Cr-2W-0.3Ti-0.3Y{sub 2}O{sub 3} alloy, which was fabricated by hot isostatic pressing followed by high speed hydrostatic extrusion (HSHE) and heat treatment HT at 1050 C. Transmission electron microscopy (TEM) observations revealed significant differences in the grain size and dislocation density between the as-HIPped and as-HSHE materials. It was also found that the microstructure of the steel is stable after HT. The HSHE process improves significantly the tensile and Charpy impact properties of the as-HIPped steel. The ultimate tensile strength at room temperature increases from 950 up to 1350 MPa, while the upper shelf energy increases from 3.0 up to 6.0 J. However, the ductile-to-brittle transition temperature (DBTT) remains relatively high (about 75 C).These results indicate that HSHE is a promising method for achieving grain refinement and thus improving the mechanical properties of ODS ferritic steels. (Abstract Copyright [2010], Wiley Periodicals, Inc.)

  11. HOT 2012

    DEFF Research Database (Denmark)

    Lund, Henriette Romme

    Undersøgelse af, hvad der er hot - og hvad der burde være hot på læseområdet med 21 læsekyndige. Undersøgelsen er gennemført siden 2010. HOT-undersøgelsen er foretaget af Nationalt Videncenter for Læsning - Professionshøjskolerne i samarb. med Dansklærerforeningen......Undersøgelse af, hvad der er hot - og hvad der burde være hot på læseområdet med 21 læsekyndige. Undersøgelsen er gennemført siden 2010. HOT-undersøgelsen er foretaget af Nationalt Videncenter for Læsning - Professionshøjskolerne i samarb. med Dansklærerforeningen...

  12. HOT 2014

    DEFF Research Database (Denmark)

    Lund, Henriette

    Undersøgelse af, hvad der er hot - og hvad der burde være hot på læseområdet med 21 læsekyndige. Undersøgelsen er gennemført siden 2010. HOT-undersøgelsen er foretaget af Nationalt Videncenter for Læsning - Professionshøjskolerne i samarb. med Dansklærerforeningen...

  13. HOT 2011

    DEFF Research Database (Denmark)

    Lund, Henriette Romme

    En undersøgelse af, hvad der er hot - og burde være hot på læseområdet. I undersøgelsen deltager 21 læsekyndige fra praksisfeltet, professionshøjskolerne og forskningsområdet.......En undersøgelse af, hvad der er hot - og burde være hot på læseområdet. I undersøgelsen deltager 21 læsekyndige fra praksisfeltet, professionshøjskolerne og forskningsområdet....

  14. Worldwide complete spherical Bouguer and isostatic anomaly maps

    Science.gov (United States)

    Bonvalot, S.; Balmino, G.; Briais, A.; Peyrefitte, A.; Vales, N.; Biancale, R.; Gabalda, G.; Reinquin, F.

    2011-12-01

    We present here a set of digital maps of the Earth's gravity anomalies (surface "free air", Bouguer and isostatic), computed at Bureau Gravimetric International (BGI) as a contribution to the Global Geodetic Observing Systems (GGOS) and to the global geophysical maps published by the Commission for the Geological Map of the World (CGMW). The free air and Bouguer anomaly concept is extensively used in geophysical interpretation to investigate the density distributions in the Earth's interior. Complete Bouguer anomalies (including terrain effects) are usually computed at regional scales by integrating the gravity attraction of topography elements over and beyond a given area (under planar or spherical approximations). Here, we developed and applied a worldwide spherical approach aimed to provide a set of homogeneous and high resolution gravity anomaly maps and grids computed at the Earth's surface, taking into account a realistic Earth model and reconciling geophysical and geodetic definitions of gravity anomalies. This first version (1.0) has been computed by spherical harmonics analysis / synthesis of the Earth's topography-bathymetry up to degree 10800. The detailed theory of the spherical harmonics approach is given in Balmino et al., (Journal of Geodesy, submitted). The Bouguer and terrain corrections have thus been computed in spherical geometry at 1'x1' resolution using the ETOPO1 topography/bathymetry, ice surface and bedrock models from the NOAA (National Oceanic and Atmospheric Administration) and taking into account precise characteristics (boundaries and densities) of major lakes, inner seas, polar caps and of land areas below sea level. Isostatic corrections have been computed according to the Airy Heiskanen model in spherical geometry for a constant depth of compensation of 30km. The gravity information given here is provided by the Earth Geopotential Model (EGM2008), developed at degree 2160 by the National Geospatial Intelligence Agency (NGA) (Pavlis

  15. Gravity and isostatic anomaly maps of Greece produced

    Science.gov (United States)

    Lagios, E.; Chailas, S.; Hipkin, R. G.

    A gravity anomaly map of Greece was first compiled in the early 1970s [Makris and Stavrou, 1984] from all available gravity data collected by different Hellenic institutions. However, to compose this map the data had to be smoothed to the point that many of the smaller-wavelength gravity anomalies were lost. New work begun in 1987 has resulted in the publication of an updated map [Lagios et al., 1994] and an isostatic anomaly map derived from it.The gravity data cover the area between east longitudes 19° and 27° and north latitudes 32° and 42°, organized in files of 100-km squares and grouped in 10-km squares using UTM zone 34 coordinates. Most of the data on land come from the gravity observations of Makris and Stavrou [1984] with additional data from the Institute of Geology and Mining Exploration, the Public Oil Corporation of Greece, and Athens University. These data were checked using techniques similar to those used in compiling the gravity anomaly map of the United States, but the horizontal gradient was used as a check rather than the gravity difference. Marine data were digitized from the maps of Morelli et al. [1975a, 1975b]. All gravity anomaly values are referred to the IGSN-71 system, reduced with the standard Bouger density of 2.67 Mg/m3. We estimate the errors of the anomalies in the continental part of Greece to be ±0.9 mGal; this is expected to be smaller over fairly flat regions. For stations whose height has been determined by leveling, the error is only ±0.3 mGal. For the marine areas, the errors are about ±5 mGal [Morelli, 1990].

  16. The alignment and isostatic mount bonding technique of the aerospace Cassegrain telescope primary mirror

    Science.gov (United States)

    Lin, Wei Cheng; Chang, Shenq-Tsong; Lin, Yu-Chuan; Hsu, Ming-Ying; Chang, Yu-Ting; Chang, Sheng-Hsiung; Huang, Ting-Ming

    2012-10-01

    In order to meet both optical performance and structural stiffness requirements of the aerospace Cassegrain telescope, iso-static mount is used as the interface between the primary mirror and the main plate. This article describes the alignment and iso-static mount bonding technique of the primary mirror by assistance of CMM. The design and assembly of mechanical ground support equipment (MGSE) which reduces the deformation of primary mirror by the gravity effect is also presented. The primary mirror adjusting MGSE consists of X-Y linear translation stages, rotation stage and kinematic constrain platform which provides the function of decenter, orientation, tilt and height adjustment of the posture sequentially. After CMM measurement, the radius of curvature, conic constant, decenter and tilt, etc. will be calculated. According to these results, the posture of the mirror will be adjusted to reduce the tilt by the designed MGSE within 0.02 degrees and the distance deviation from the best fitted profile of mirror to main plate shall be less than 0.01 mm. After that, EC 2216 adhesive is used to bond mirror and iso-static mount. During iso-static mount bonding process, CMM is selected to monitor the relative position deviation of the iso-static mount until the adhesive completely cured. After that, the wave front sensors and strain gauges are used to monitor the strain variation while the iso-static mount mounted in the main plate with the screws by the torque wrench. This step is to prevent deformation of the mirror caused from force of the iso-static mount during the mounting process. In the end, the interferometer is used for the optical performance test with +1G and -1G to check the alignment and bonding technique is well or not.

  17. ALUMINUM BOX BUNDLING PRESS

    Directory of Open Access Journals (Sweden)

    Iosif DUMITRESCU

    2015-05-01

    Full Text Available In municipal solid waste, aluminum is the main nonferrous metal, approximately 80- 85% of the total nonferrous metals. The income per ton gained from aluminum recuperation is 20 times higher than from glass, steel boxes or paper recuperation. The object of this paper is the design of a 300 kN press for aluminum box bundling.

  18. DSS / Press Room

    Science.gov (United States)

    Defense Security Service, U.S. Department of Defense Site Map | A-Z Index | Facebook | Twitter Locations Press Room Organizational Structure Careers at DSS Doing Business with DSS Frequently Asked Classification System (NCCS) National Industrial Security System (NISS) ODAA Business Management System (OBMS

  19. OAS :: Press Releases

    Science.gov (United States)

    subscriptions Videos Photos Live Webcast Social Media Facebook @oasofficial Facebook Twitter @oas_official Social Media Facebook Twitter Newsletters Press and Communications Department Contact us at: +1 (202) 370 Rights Actions against Corruption C Children Civil Registry Civil Society Contact Us Culture Cyber

  20. bbPress complete

    CERN Document Server

    Wynne, Rhys

    2013-01-01

    A concise guide, written in an easy-to-follow format.This book is aimed at ambitious website or blog owners looking to add a forum to their site quickly and easily. Basic experience in WordPress and with managing a website is expected. Knowledge of HTML and PHP will be a bonus, though it isn't necessary.

  1. Sintering of Si C by hot-pressing with addition of Al{sub 2}O{sub 3} and concentrate of rare earths; Sinterizacao por prensagem a quente com SiC com adicao de Al{sub 2}O{sub 3} e concentrado de terras raras

    Energy Technology Data Exchange (ETDEWEB)

    Hwang, M.K.; Silva, C.R.M. [Centro Tecnico Aeroespacial (CTA-IAE), Sao Jose dos Campos, SP (Brazil). Inst. de Atividades Espaciais]. E-mail: miriamk@iae.cta.br; Nono, M.C.A.; Vieira, R.A. [Instituto Nacional de Pesquisas Espaciais (INPE), Sao Jose dos Campos, SP (Brazil)

    2004-07-01

    Silicon carbide (SiC) has essentially covalent bonds ({approx}88%). The high covalency bond is responsible for the good mechanical properties, although it induces a low self diffusion coefficient, making densification more difficult. For a successful densification is necessary to apply pressure on the samples, and/or the addition of sintering additives, which improves the densification. In this SiC samples with alumina (Al2O3) and concentrate of rare earth (CRE) addition were sintered by hot pressing in argon atmospheric at 20 MPa of pressure, heating rate of 20 deg C/min up to 1800 deg C and a dwell time of 1 h. Initially the CRE was calcined at 1000 deg C during 1 h. After that, three mixtures were prepared with distinct concentrations in high energy mill and the samples were sintered. The aim of this work is to improve SiC densification by the liquid phase formation during sintering owing to the additives reactions between itself. The pressure intensify the driving force for densification, taking the liquid phase to drain easier through the grain boundaries, making possible best accommodation and rearrangement of the grains. The application of the pressure on the samples during sintering contributes to improve densification and becomes possible sintering in lower temperature than conventional one. The phases of the sintered samples were analyzed by X-ray diffraction and the morphology were verified by scanning electron microscopy. (author)

  2. Characteristics of isostatic gravity anomaly in Sichuan-Yunnan region, China

    Directory of Open Access Journals (Sweden)

    Bingcheng Liu

    2017-07-01

    Full Text Available Sichuan-Yunnan region in China, a tectonic transition belt where earthquakes occurred frequently and intensely, has a distinct variation characteristic of gradient zone of Bouguer gravity anomaly (BGA. Many deep faults and epicenters of severe earthquake scatter along the BGA gradient zones. Here we apply two forward models (Airy model and Vening Meinesz model of isostatic gravity mechanisms (local versus regional in this region to calculated the isostatic gravity anomaly (IGA. Afterwards, the relationship between IGA and distribution of faults as well as seismicity is also illustrated. The IGA results show that the two models are similar and most parts of the study area are in an isostatic state. Most featured faults are distributed along the steep anomaly gradient zones; earthquakes tend to occur in the non-isostatic area and steep gradient belt of IGA. The distribution of root thickness based on regional mechanism can be associated with the main trend of BGA variation. The regional mechanism is more plausible and closer to the reality because of its relatively further consideration of the horizontal forces derived from adjacent particles in the crust. Then we analyze the effect of isostasy on the tectonic movements and find that the isostatic adjustment is not the main cause of the continuous uplift process of Longmenshan Mountain fault zone, which is due to the Indian-Eurasian continental collision.

  3. Hot working behavior of selective laser melted and laser metal deposited Inconel 718

    Science.gov (United States)

    Bambach, Markus; Sizova, Irina

    2018-05-01

    The production of Nickel-based high-temperature components is of great importance for the transport and energy sector. Forging of high-temperature alloys often requires expensive dies, multiple forming steps and leads to forged parts with tolerances that require machining to create the final shape and a large amount of scrap. Additive manufacturing offers the possibility to print the desired shapes directly as net-shape components, requiring only little additional effort in machining. Especially for high-temperature alloys carrying a large amount of energy per unit mass, additive manufacturing could be more energy-efficient than forging if the energy contained in the machining scrap exceeds the energy needed for powder production and laser processing. However, the microstructure and performance of 3d-printed parts will not reach the level of forged material unless further expensive processes such as hot-isostatic pressing are used. Using the design freedom and possibilities to locally engineer material, additive manufacturing could be combined with forging operations to novel process chains, offering the possibility to reduce the number of forging steps and to create near-net shape forgings with desired local properties. Some innovative process chains combining additive manufacturing and forging have been patented recently, but almost no scientific knowledge on the workability of 3D printed preforms exists. The present study investigates the flow stress and microstructure evolution during hot working of pre-forms produced by laser powder deposition and selective laser melting (Figure 1) and puts forward a model for the flow stress.

  4. Myths About Press Freedom

    Directory of Open Access Journals (Sweden)

    Kaarle Nordenstreng

    2007-06-01

    Full Text Available This article intends to rectify three popular beliefs related to press freedom: (1 that the idea of a free marketplace of ideas with a self-righting truth belongs to original liberalism, (2 that UNESCO’s primary mission is to promote freedom of information, and (3 that the Universal Declaration of Human Rights provides legal safeguards for the media. These beliefs are shown, on the basis of the legacy of liberalism and documents of the international community, to be misleading myths. Instead of accurate readings of the idea of freedom, they serve as ideological positions which are harmful to democracy. The Millennium Declaration provides further proof that the international community has a much more balanced view of freedom of information than that typically held by media professionals. Therefore it is important to liberate the concept of press freedom from its ideological baggage.

  5. Thermal Expansion Behavior of Hot-Pressed Engineered Matrices

    Science.gov (United States)

    Raj, S. V.

    2016-01-01

    Advanced engineered matrix composites (EMCs) require that the coefficient of thermal expansion (CTE) of the engineered matrix (EM) matches those of the fiber reinforcements as closely as possible in order to reduce thermal compatibility strains during heating and cooling of the composites. The present paper proposes a general concept for designing suitable matrices for long fiber reinforced composites using a rule of mixtures (ROM) approach to minimize the global differences in the thermal expansion mismatches between the fibers and the engineered matrix. Proof-of-concept studies were conducted to demonstrate the validity of the concept.

  6. Raman spectra of hot-pressed boron suboxide

    CSIR Research Space (South Africa)

    Machaka, R

    2011-01-01

    Full Text Available on in- situ/online measurements (such as GIXRD, Raman Spectroscopy, FIB- Electron Microscopy) during (i) ion implantation, (ii) PLD growth of nanoparticles SW/MW-CNTs, oxide semiconductor multi-layer, metal/Si and metal/metal systems. Moreover, He...], aluminium magnesium boride ? AlMgB14 [8], and the newly synthesized boron subnitride ? B13N2 [9, 10]. With hardness values reported between 24 GPa and 45 GPa [7, 11, 12], B6O is sometimes considered to be the third hardest material only after diamond...

  7. HOT 2010

    DEFF Research Database (Denmark)

    Lund, Henriette Romme

    En undersøgelse af, hvad der er hot - og burde være hot på læseområdet. I undersøgelsen deltager en række læsekyndige fra praksisfeltet, professionshøjskolerne og forskningsområdet. Undersøgelsen er gentaget hvert år siden 2010.......En undersøgelse af, hvad der er hot - og burde være hot på læseområdet. I undersøgelsen deltager en række læsekyndige fra praksisfeltet, professionshøjskolerne og forskningsområdet. Undersøgelsen er gentaget hvert år siden 2010....

  8. HOT 2013

    DEFF Research Database (Denmark)

    Lund, Henriette Romme

    En undersøgelse af, hvad der er hot - og burde være hot på læseområdet. I undersøgelsen deltager en række læsekyndige fra praksisfeltet, professionshøjskolerne og forskningsområdet. Undersøgelsen er gentaget hvert år siden 2010.......En undersøgelse af, hvad der er hot - og burde være hot på læseområdet. I undersøgelsen deltager en række læsekyndige fra praksisfeltet, professionshøjskolerne og forskningsområdet. Undersøgelsen er gentaget hvert år siden 2010....

  9. Tectonics and Non-isostatic Topography of the Mariana Trench and Adjacent Plates

    Science.gov (United States)

    Hongyu, L.; Lin, J.; Zhou, Z.; Zhang, F.

    2017-12-01

    Multi-types of geophysical data including multibeam bathymetry, sediment thickness, gravity anomaly, and crustal magnetic age were analyzed to investigate tectonic processes of the Mariana Trench and the surrounding plates. We calculated non-Airy-isostatic topography by removing from the observed bathymetry the effects of sediment loading, thermal subsidence, and Airy local isostatically-compensated topography. The Mariana Trench was found to be associated with a clearly defined zone of negative non-isostatic topography, which was caused by flexural bending of the subducting Pacific plate and with the maximum depth anomaly and flexural bending near the Challenger Deep. In contrast, the Caroline Ridge and Caroline Islands Chain have much more subdued non-isostatic topography, indicating their higher topography is largely compensated by thicker crust. Along the Mariana Trough, the northern and central segments appear to be associated with relatively low magma supply as indicated by the relatively low topography and thin crust. In contrast, the southern Mariana Trough is associated with relatively high magma supply as indicated by the relatively high and smoother topography, an axial high spreading center, and relatively thick crust. The southern end of the Mariana Trough was also found to be associated with positive non-isostatic topographic anomaly, which might be caused by the complex tectonic deformation of the overriding Mariana and Philippine Sea plates and their interaction with the subducting Pacific plate. Analysis further revealed that the southern Mariana Arc, located between the Mariana Trench and Mariana Trough, is associated with positive non-isostatic topographic anomalies, which may be explained by the late stage magmatic loading on the older and thus stronger lithospheric plate of the Mariana volcanic arc.

  10. Cold Isostatic-Pressured Silver Nanowire Electrodes for Flexible Organic Solar Cells via Room-Temperature Processes.

    Science.gov (United States)

    Seo, Ji Hoon; Hwang, Inchan; Um, Han-Don; Lee, Sojeong; Lee, Kangmin; Park, Jeonghwan; Shin, Hyeonoh; Kwon, Tae-Hyuk; Kang, Seok Ju; Seo, Kwanyong

    2017-08-01

    Transparent conducting electrodes (TCEs) are considered to be an essential structural component of flexible organic solar cells (FOSCs). Silver nanowire (AgNW) electrodes are widely used as TCEs owing to their excellent electrical and optical properties. The fabrication of AgNW electrodes has faced challenges in terms of forming large uniform interconnected networks so that high conductivity and reproducibility can be achieved. In this study, a simple method for creating an intimate contact between AgNWs that uses cold isostatic pressing (CIP) is demonstrated. This method increases the conductivity of the AgNW electrodes, which enables the fabrication of high-efficiency inverted FOSCs that have a power conversion efficiency of 8.75% on flexible polyethylene terephthalate with no short circuiting occurring as the CIP process minimizes the surface roughness of the AgNW electrode. This allows to achieve 100% manufacturing yield of FOSCs. Furthermore, these highly efficient FOSCs are proven to only be 2.4% less efficient even for an extreme bending radius of R ≈ 1.5 mm, compared with initial efficiency. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  11. Absolute sea levels and isostatic changes of the eastern North Sea to central Baltic region during the last 900 years

    DEFF Research Database (Denmark)

    Hansen, Jens Morten; Aagaard, Troels; Binderup, Merete

    2012-01-01

    that ice-cap growth can be faster than ice-cap melting. By comparison with 29 long-term tide gauge measurements of the region we show that the isostatic implications of the sea-level curve are in nearly perfect agreement with Peltier's global isostatic VM2 model (applied by IPCC and PSMSL) and yield a 3...

  12. The effect of cushion-ram pulsation on hot stamping

    Science.gov (United States)

    Landgrebe, Dirk; Rautenstrauch, Anja; Kunke, Andreas; Polster, Stefan; Kriechenbauer, Sebastian; Mauermann, Reinhard

    2016-10-01

    Hot stamping is an important technology for manufacturing high-strength components. This technology offers the possibility to achieve significant weight reductions. In this study, cushion-ram pulsation (CRP), a new technology for hot stamping on servo-screw presses, was investigated and applied for hot stamping. Compared to a conventional process, the tests yielded a significantly higher drawing depth. In this paper, the CRP technology and the first test results with hot stamping were described in comparison to the conventional process.

  13. ISS Expedition 08 Press Kit

    Data.gov (United States)

    National Aeronautics and Space Administration — Press kit for ISS mission Expedition 08 from 10/2003-04/2004. Press kits contain information about each mission overview, crew, mission timeline, benefits, and media...

  14. WordPress multisite administration

    CERN Document Server

    Longren, Tyler

    2013-01-01

    This is a simple, concise guide with a step-by-step approach, packed with screenshots and examples to set up and manage a network blog using WordPress.WordPress Multisite Administration is ideal for anyone wanting to familiarize themselves with WordPress Multisite. You'll need to know the basics about WordPress, and having at least a broad understanding of HTML, CSS, and PHP will help, but isn't required.

  15. Four Theories of the Press.

    Science.gov (United States)

    Siebert, Fred S.; And Others

    A systematic understanding of the press requires an understanding of the social and political structures within which the press operates. This book discusses four theories that have determined the kind of press the Western world has had: authoritarian, libertarian, socially responsible, and Soviet communist. Each chapter discusses press…

  16. Towards Constraining Glacial Isostatic Adjustment in Greenland Using ICESat and GPS Observations

    DEFF Research Database (Denmark)

    Nielsen, Karina; Sørensen, Louise Sandberg; Khan, Shfaqat Abbas

    2014-01-01

    Constraining glacial isostatic adjustment (GIA) i.e. the Earth’s viscoelastic response to past ice changes, is an important task, because GIA is a significant correction in gravity-based ice sheet mass balance estimates. Here, we investigate how temporal variations in the observed and modeled cru...

  17. Isostatic gravity map of the Point Sur 30 x 60 quadrangle and adjacent areas, California

    Science.gov (United States)

    Watt, J.T.; Morin, R.L.; Langenheim, V.E.

    2011-01-01

    This isostatic residual gravity map is part of a regional effort to investigate the tectonics and water resources of the central Coast Range. This map serves as a basis for modeling the shape of basins and for determining the location and geometry of faults in the area. Local spatial variations in the Earth's gravity field (after removing variations caused by instrument drift, earth-tides, latitude, elevation, terrain, and deep crustal structure), as expressed by the isostatic anomaly, reflect the distribution of densities in the mid- to upper crust, which in turn can be related to rock type. Steep gradients in the isostatic gravity field often indicate lithologic or structural boundaries. Gravity highs reflect the Mesozoic granitic and Franciscan Complex basement rocks that comprise both the northwest-trending Santa Lucia and Gabilan Ranges, whereas gravity lows in Salinas Valley and the offshore basins reflect the thick accumulations of low-density alluvial and marine sediment. Gravity lows also occur where there are thick deposits of low-density Monterey Formation in the hills southeast of Arroyo Seco (>2 km, Marion, 1986). Within the map area, isostatic residual gravity values range from approximately -60 mGal offshore in the northern part of the Sur basin to approximately 22 mGal in the Santa Lucia Range.

  18. Modification of low density polyethylene, isostatic polypropylene and their blends by gamma radiation

    International Nuclear Information System (INIS)

    Santos Rosa, D. dos

    1991-01-01

    The effects of the gamma radiation (of a 60 Co source), over low density polyethylene, isostatic polypropylene and their blends of low density polyethylene / polypropylene were studied. The structures modifications were attended by infrared spectrometry (IV), differential scanning calorimeter (DSC), strain-strain measurement, density measurement and scanning electron microscope (SEM). (author)

  19. Which Freedom of the Press?

    DEFF Research Database (Denmark)

    Rytter, Jens Elo

    2010-01-01

    The article surveys the historical and current meaning of "Freedom of the Press" in constitutional and human rights law. Two different conceptions exist, the narrow one defining freedom of the press as the freedom of every one to publish without prior restraint, the broader one defining it as a...... privileged freedom of the organised press to gather and report on information of public interest. These two conceptions have very different answers to the question of whether the press should enjoy some privilege to be exempt from ordinary legislation when such legislation restricts the access of the press to inform...

  20. One step HIP canning of powder metallurgy composites

    Science.gov (United States)

    Juhas, John J. (Inventor)

    1990-01-01

    A single step is relied on in the canning process for hot isostatic pressing (HIP) powder metallurgy composites. The binders are totally removed while the HIP can of compatible refractory metal is sealed at high vacuum and temperature. This eliminates outgassing during hot isostatic pressing.

  1. An empirical model of glacio-isostatic movements and shore-level displacement in Fennoscandia

    Energy Technology Data Exchange (ETDEWEB)

    Paasse, T. [Geological Survey of Sweden, Uppsala (Sweden)

    2001-08-01

    Shore-level displacement in Fennoscandia is mainly due to two co-operative vertical movements, glacio-isostatic uplift and global eustatic sea level rise. The course of the glacio-isostatic uplift has been made discernible according to an investigation of the lake-tilting phenomenon. This information made it possible to start an iteration process that has given mathematical expression for factors involved both within the isostatic movements and the eustatic rise. There are two components involved in glacio-isostatic uplift. The main uplift, still in progress, acts slowly and is thus called the slow component. Arctan functions have proved to be suitable tools for describing the slow component. There are two main factors involved in the function used for calculation; A{sub s} (m), the download factor and B{sub s} (y{sup -1} ), which is an inertia factor. A strong linear correlation between the inertia factor Bs and lithosphere thickness has been found in the model. There was also a fast component involved in the crustal changes at the end of Late Weichselian and early Holocene. This component gave rise to fast subsidence followed by fast uplift during the final part of the deglaciation. Crustal subsidence is assumed to be due to reloading of the crust in the central parts of Fennoscandia during the Younger Dryas stadial. Normal distribution functions are used for calculating this component. Glacio-isostatic uplift and thus a regressive shore-level displacement was extremely rapid around 10,300 years BP. This fast regression was contemporaneous and occurred in a similar way at the West Coasts of Norway and Sweden as well as in the Baltic. The 'drainage' of the Baltic Ice Lake has been interpreted in the model as due to this fast regression. The slow component is most probably due to viscous flow in the asthenosphere and the fast component is assumed to be due to its elasticity.

  2. An empirical model of glacio-isostatic movements and shore-level displacement in Fennoscandia

    International Nuclear Information System (INIS)

    Paasse, T.

    2001-08-01

    Shore-level displacement in Fennoscandia is mainly due to two co-operative vertical movements, glacio-isostatic uplift and global eustatic sea level rise. The course of the glacio-isostatic uplift has been made discernible according to an investigation of the lake-tilting phenomenon. This information made it possible to start an iteration process that has given mathematical expression for factors involved both within the isostatic movements and the eustatic rise. There are two components involved in glacio-isostatic uplift. The main uplift, still in progress, acts slowly and is thus called the slow component. Arctan functions have proved to be suitable tools for describing the slow component. There are two main factors involved in the function used for calculation; A s (m), the download factor and B s (y -1 ), which is an inertia factor. A strong linear correlation between the inertia factor Bs and lithosphere thickness has been found in the model. There was also a fast component involved in the crustal changes at the end of Late Weichselian and early Holocene. This component gave rise to fast subsidence followed by fast uplift during the final part of the deglaciation. Crustal subsidence is assumed to be due to reloading of the crust in the central parts of Fennoscandia during the Younger Dryas stadial. Normal distribution functions are used for calculating this component. Glacio-isostatic uplift and thus a regressive shore-level displacement was extremely rapid around 10,300 years BP. This fast regression was contemporaneous and occurred in a similar way at the West Coasts of Norway and Sweden as well as in the Baltic. The 'drainage' of the Baltic Ice Lake has been interpreted in the model as due to this fast regression. The slow component is most probably due to viscous flow in the asthenosphere and the fast component is assumed to be due to its elasticity

  3. WordPress for dummies

    CERN Document Server

    Sabin-Wilson, Lisa

    2014-01-01

    The bestselling WordPress guide, fully updated to cover the 2013 enhancements WordPress has millions of users, and this popular guide has sold more than 105,000 copies in its previous editions. With the newest releases of WordPress, author and WordPress expert Lisa Sabin-Wilson has completely updated the book to help you use and understand all the latest features. You'll learn about both the hosted WordPress.com version and the more flexible WordPress.org, which requires third-party hosting. Whether you're switching to WordPress from another blogging platform or just beginning to blog, you'll

  4. Forming of AHSS using Servo-Presses

    Science.gov (United States)

    Groseclose, Adam Richard

    Stamping of Advanced High Strength Steel (AHSS) alloys poses several challenges due to the material's higher strength and low formability compared to conventional steels and other problems such as (a) inconsistency of incoming material properties, (b) ductile fracture during forming, (c) higher contact pressure and temperature rise during forming, (d) higher die wear leading to reduced tool life, (e) higher forming load/press capacity, and (f) large springback leading to dimensional inaccuracy in the formed part. [Palaniswamy et. al., 2007]. The use of AHSS has been increasing steadily in automotive stamping. New AHSS alloys (TRIP, TWIP) may replace some of the Hot Stamping applications. Stamping of AHSS alloys, especially higher strength materials, 780 MPa and higher, present new challenges in obtaining good part definition (corner and fillet radii), formability (fracture and resulting scrap) and in reducing springback. Servo-drive presses, having the capability to have infinitely variable and adjustable ram speed and dwell at BDC, offer a potential improvement in quality, part definition, and springback reduction especially when the infinitely adjustable slide motion is used in combination with a CNC hydraulic cushion. Thus, it is desirable to establish a scientific/engineering basis for improving the stamping conditions in forming AHSS using a servo-drive press.

  5. Isostatic anomaly characteristics and dynamic environment of New Britain Ocean trenches and neighboring Area in Papua New Guinea

    Science.gov (United States)

    Yang, G.; Shen, C.; Wang, J.

    2017-12-01

    we calculated the Bouguer gravity anomaly and the Airy-Heiskanen isostatic anomaly in the New Britain ocean trenches and its surrounding areas of Papua New Guinea using the topography model and the gravity anomaly model from Scripps Institute of Oceanography, and analyzed the characteristics of isostatic anomaly and the earthquake dynamic environment of this region. The results show that there are obviously differences in the isostatic state between each block in the region, and the crustal tectonic movement is very intense in the regions with high positive or negative isostatic gravity anomalies; A number of sub-plates in this area is driven by the external tectonic action such as plate subduction and thrust of the Pacific plate, the Indian - Australian plate and the Eurasian plate. From the distribution of isostatic gravity anomaly, the tectonic action of anti-isostatic movement in this region is the main source of power; from the isostatic gravity and the spatial distribution of the earthquake, with the further contraction of the Indian-Australian plate, the southwestern part of the Solomon Haiya plate will become part of the Owen Stanley fold belt, the northern part will enter the lower part of the Bismarck plate, eastern part will enter the front of the Pacific plate, the huge earthquake will migrate to the north and east of the Solomon Haiya plate.

  6. Influence of hot rolling and high speed hydrostatic extrusion on the microstructure and mechanical properties of an ODS RAF steel

    Energy Technology Data Exchange (ETDEWEB)

    Oksiuta, Z., E-mail: oksiuta@pb.edu.pl [Bialystok Technical University, Faculty of Mechanical Engineering, Wiejska 45c, 15-352 Bialystok (Poland); Lewandowska, M.; Kurzydlowski, K.J. [Warsaw University of Technology, Faculty of Materials Science and Engineering, Woloska 141, 02-504 Warsaw (Poland); Baluc, N. [Ecole Polytechnique Federale de Lausanne (EPFL), Centre de Recherches en Physique des Plasmas, Association Euratom-Confederation Suisse, 5232 Villigen PSI (Switzerland)

    2011-02-15

    An argon gas atomized, pre-alloyed Fe-14Cr-2W-0.3Ti (wt.%) reduced activation ferritic (RAF) steel powder was mechanically alloyed with 0.3wt.% Y{sub 2}O{sub 3} nano-particles in an attritor ball mill and consolidated by hot isostatic pressing at 1150 {sup o}C under a pressure of 200 MPa for 3 h. In the aim to improve its mechanical properties the ODS steel was then submitted to a thermo-mechanical treatment (TMT): hot rolling (HR) at 850 deg. C or high speed hydrostatic extrusion (HSHE) at 900 deg. C, followed by heat treatment (HT). Transmission electron microscopy (TEM) observations of the ODS alloys after TMT and heat treatment revealed the presence of elongated grains in the longitudinal direction, with an average width of 8 {mu}m and an average length of 75 {mu}m, and equiaxed grains, a few microns in diameter, in the transverse direction. Two populations of oxide particles were observed by TEM: large Ti-Al-O particles, up to 250 nm in diameter, usually located at the grain boundaries and small Y-Ti-O nanoclusters, about 2.5 nm in diameter, uniformly distributed in the matrix. Charpy impact tests revealed that the HSHE material exhibits a larger upper shelf energy (5.8 J) than the HR material (2.9 J). The ductile-to-brittle transition temperature of both alloys is relatively high, in the range of 55-72 deg. C. Tensile mechanical properties of both ODS alloys were found satisfactory over the full range of investigated temperatures (23-750 deg. C). The HSHE material exhibits better tensile strength and ductility than the HR material. These results indicate that HSHE can be considered as a promising TMT method for improving the mechanical properties of ODS RAF steels.

  7. HOT 2017

    DEFF Research Database (Denmark)

    Hannibal, Sara Stefansen

    HOT er en kvalitativ undersøgelse, der hvert år diskuterer og undersøger en lille udvalgt skare af danskkyndige fagpersoners bud på, hvad de er optagede af på literacyområdet her og nu – altså hvilke emner, de vil vurdere som aktuelle at forholde sig til i deres nuværende praksis.......HOT er en kvalitativ undersøgelse, der hvert år diskuterer og undersøger en lille udvalgt skare af danskkyndige fagpersoners bud på, hvad de er optagede af på literacyområdet her og nu – altså hvilke emner, de vil vurdere som aktuelle at forholde sig til i deres nuværende praksis....

  8. Modelling of powder die compaction for press cycle optimization

    Directory of Open Access Journals (Sweden)

    Bayle Jean-Philippe

    2016-01-01

    Full Text Available A new electromechanical press for fuel pellet manufacturing was built last year in partnership between CEA-Marcoule and ChampalleAlcen. This press was developed to shape pellets in a hot cell via remote handling. It has been qualified to show its robustness and to optimize the compaction cycle, thus obtaining a better sintered pellet profile and limiting damage. We will show you how 400 annular pellets have been produced with good geometry's parameters, based on press settings management. These results are according to a good phenomenological pressing knowledge with Finite Element Modeling calculation. Therefore, during die pressing, a modification in the punch displacement sequence induces fluctuation in the axial distribution of frictional forces. The green pellet stress and density gradients are based on these frictional forces between powder and tool, and between grains in the powder, influencing the shape of the pellet after sintering. The pellet shape and diameter tolerances must be minimized to avoid the need for grinding operations. To find the best parameters for the press settings, which enable optimization, FEM calculations were used and different compaction models compared to give the best calculation/physical trial comparisons. These simulations were then used to predict the impact of different parameters when there is a change in the type of powder and the pellet size, or when the behavior of the press changes during the compaction time. In 2016, it is planned to set up the press in a glove box for UO2 manufacturing qualification based on our simulation methodology, before actual hot cell trials in the future.

  9. Hot particles

    International Nuclear Information System (INIS)

    Merwin, S.E.; Moeller, M.P.

    1989-01-01

    Nuclear Regulatory Commission (NRC) licensees are required to assess the dose to skin from a hot particle contamination event at a depth of skin of7mg/cm 2 over an area of 1 cm 2 and compare the value to the current dose limit for the skin. Although the resulting number is interesting from a comparative standpoint and can be used to predict local skin reactions, comparison of the number to existing limits based on uniform exposures is inappropriate. Most incidents that can be classified as overexposures based on this interpretation of dose actually have no effect on the health of the worker. As a result, resources are expended to reduce the likelihood that an overexposure event will occur when they could be directed toward eliminating the cause of the problem or enhancing existing programs such as contamination control. Furthermore, from a risk standpoint, this practice is not ALARA because some workers receive whole body doses in order to minimize the occurrence of hot particle skin contaminations. In this paper the authors suggest an alternative approach to controlling hot particle exposures

  10. WordPress For Dummies

    CERN Document Server

    Sabin-Wilson, Lisa

    2011-01-01

    The bestselling guide to WordPress, fully updated to help you get your blog going! Millions of bloggers rely on WordPress, the popular, free blogging platform. This guide covers all the features and improvements in the most up-to-date version of WordPress. Whether you are switching to WordPress from another blogging platform or just starting your first blog, you'll find the advice in this friendly guide gets you up to speed on both the free-hosted WordPress.com version and WordPress.org, which requires the purchase of web hosting services, and figure out which version is best for you. You'll b

  11. WordPress Top Plugins

    CERN Document Server

    Corbin, Brandon

    2010-01-01

    Time flies when you're having fun. This is the right way to describe this WordPress Top Plugins book by Brandon Corbin. With real world examples and by showing you the perks of having these plugins installed on your websites, the author is all set to captivate your interest from start to end. Regardless of whether this is your first time working with WordPress, or you're a seasoned WordPress coding ninja, WordPress Top Plugins will walk you through finding and installing the best plugins for generating and sharing content, building communities and reader base, and generating real advertising r

  12. Gas hydrate dissociation off Svalbard induced by isostatic rebound rather than global warming.

    Science.gov (United States)

    Wallmann, Klaus; Riedel, M; Hong, W L; Patton, H; Hubbard, A; Pape, T; Hsu, C W; Schmidt, C; Johnson, J E; Torres, M E; Andreassen, K; Berndt, C; Bohrmann, G

    2018-01-08

    Methane seepage from the upper continental slopes of Western Svalbard has previously been attributed to gas hydrate dissociation induced by anthropogenic warming of ambient bottom waters. Here we show that sediment cores drilled off Prins Karls Foreland contain freshwater from dissociating hydrates. However, our modeling indicates that the observed pore water freshening began around 8 ka BP when the rate of isostatic uplift outpaced eustatic sea-level rise. The resultant local shallowing and lowering of hydrostatic pressure forced gas hydrate dissociation and dissolved chloride depletions consistent with our geochemical analysis. Hence, we propose that hydrate dissociation was triggered by postglacial isostatic rebound rather than anthropogenic warming. Furthermore, we show that methane fluxes from dissociating hydrates were considerably smaller than present methane seepage rates implying that gas hydrates were not a major source of methane to the oceans, but rather acted as a dynamic seal, regulating methane release from deep geological reservoirs.

  13. Utilizing Visual Effects Software for Efficient and Flexible Isostatic Adjustment Modelling

    Science.gov (United States)

    Meldgaard, A.; Nielsen, L.; Iaffaldano, G.

    2017-12-01

    The isostatic adjustment signal generated by transient ice sheet loading is an important indicator of past ice sheet extent and the rheological constitution of the interior of the Earth. Finite element modelling has proved to be a very useful tool in these studies. We present a simple numerical model for 3D visco elastic Earth deformation and a new approach to the design of such models utilizing visual effects software designed for the film and game industry. The software package Houdini offers an assortment of optimized tools and libraries which greatly facilitate the creation of efficient numerical algorithms. In particular, we make use of Houdini's procedural work flow, the SIMD programming language VEX, Houdini's sparse matrix creation and inversion libraries, an inbuilt tetrahedralizer for grid creation, and the user interface, which facilitates effortless manipulation of 3D geometry. We mitigate many of the time consuming steps associated with the authoring of efficient algorithms from scratch while still keeping the flexibility that may be lost with the use of commercial dedicated finite element programs. We test the efficiency of the algorithm by comparing simulation times with off-the-shelf solutions from the Abaqus software package. The algorithm is tailored for the study of local isostatic adjustment patterns, in close vicinity to present ice sheet margins. In particular, we wish to examine possible causes for the considerable spatial differences in the uplift magnitude which are apparent from field observations in these areas. Such features, with spatial scales of tens of kilometres, are not resolvable with current global isostatic adjustment models, and may require the inclusion of local topographic features. We use the presented algorithm to study a near field area where field observations are abundant, namely, Disko Bay in West Greenland with the intention of constraining Earth parameters and ice thickness. In addition, we assess how local

  14. Indre spenninger og ytre press

    DEFF Research Database (Denmark)

    Ibsen, Bjarne

    2011-01-01

    Anmeldelse af bogen 'Norsk idrett. Indre spenninger og ytre press' redigeret af Dag Vidar Hanstad, Gunnar Breivik, Mari Kristin Sisjord og Hans B. Skaset og udgivet af forlaet akilles.......Anmeldelse af bogen 'Norsk idrett. Indre spenninger og ytre press' redigeret af Dag Vidar Hanstad, Gunnar Breivik, Mari Kristin Sisjord og Hans B. Skaset og udgivet af forlaet akilles....

  15. BuddyPress theme development

    CERN Document Server

    Lister, Tammie

    2013-01-01

    This book is a hands-on tutorial guide to using BuddyPress.This book is great for designers and developers who are looking to learn how to develop BuddyPress themes. It's assumed that the reader has some understanding of Wordpress and is familiar with CSS and HTML.

  16. Head First WordPress

    CERN Document Server

    Siarto, Jeff

    2010-01-01

    Whether you're promoting your business or writing about your travel adventures, Head First WordPress will teach you not only how to make your blog look unique and attention-grabbing, but also how to dig into the more complex features of WordPress 3.0 to make your website work well, too. You'll learn how to move beyond the standard WordPress look and feel by customizing your blog with your own URL, templates, plugin functionality, and more. As you learn, you'll be working with real WordPress files: The book's website provides pre-fab WordPress themes to download and work with as you follow al

  17. Influence of hot rolling and high speed hydrostatic extrusion on the microstructure and mechanical properties of RAF ODS steel

    International Nuclear Information System (INIS)

    Oksiuta, Z.; Kurzydlowski, K.J.; Baluc, N.

    2009-01-01

    Argon gas atomized, pre-alloyed Fe-14Cr-2W-0.3Ti oxide dispersion strengthened (ODS) ferritic steel powder was mechanically alloyed with 0.3Y2O3 (wt.%) nano-particles in attritor ball mill and consolidated by hot isostatic pressing (HIP) at 1150 deg. C under pressure of 200 MPa for 3 hrs. To improve mechanical properties of as HIPped ODS ingots the material was undergone further thermo-mechanical treatment (TMT), namely: hot rolling (HR) at 850 deg. C or high speed hot extrusion (HSHE) at 850 deg. C. After TMT both materials were annealed at 1050 deg. C for 1 h in vacuum. Transmission electron microscopy (TEM) observations of the ODS alloys after TMT and heat treatment exhibited elongated in a longitudinal direction grains with an average size of 75 μm. However, an equiaxed, smaller than 500 nm grains were also found in the microstructure of both materials. Different size and morphology of oxides particles were also observed. Bigger, about 150 nm Ti-Al-O particles were usually located at grain boundaries whereas Y-Ti-O nanoclusters of about 5 nm were uniformly distributed in ODS steel matrix. The Charpy impact tests revealed significantly better about 90% (5.8 J) upper shelf energy (USE) of material after HSHE but ductile to brittle transition temperature (DBTT) of both alloys was unsatisfactory. As-HR ODS steel has shown DBTT of about 55 deg. C whereas HSHE ODS steel has about 75 deg. C. This relatively high values of transition temperature were probably caused by oxides particles present at grain boundaries of the ODS alloys which decreased fracture properties of the ODS steels. High temperature tensile properties of both ODS alloys are found to be satisfactory in full range of the testing temperature from 23 up to 750 deg. C. However, about 15% better UTS and YS0.2 (1350 MPa and 1285 MPa, respectively) as well as ductility were measured in the case of the as-HSHE ODS steel. These results indicates that HSHE process of the ODS steel can be considered as more

  18. Smashing WordPress Themes Making WordPress Beautiful

    CERN Document Server

    Hedengren, Thord Daniel

    2011-01-01

    The ultimate guide to WordPress Themes - one of the hottest topics on the web today WordPress is so much more than a blogging platform, and Smashing WordPress Themes teaches readers how to make it look any way they like - from a corporate site, to a photography gallery and moreWordPress is one of the hottest tools on the web today and is used by sites including The New York Times, Rolling Stone, flickr, CNN, NASA and of course Smashing MagazineBeautiful full colour throughout - web designers expect nothing lessSmashing Magazine will fully support this book by by promoting it through their webs

  19. Science coverage and the press

    International Nuclear Information System (INIS)

    Hawkes, N.

    1992-01-01

    The writer, a journalist, summarizes the discussion of the Chilton Seminar, February 1992, and discusses the problems of bridging the incomprehension gap between scientists and lay readers of the press. (Author)

  20. Zinc coated sheet steel for press hardening

    Science.gov (United States)

    Ghanbari, Zahra N.

    Galvanized steels are of interest to enhance corrosion resistance of press-hardened steels, but concerns related to liquid metal embrittlement have been raised. The objective of this study was to assess the soak time and temperature conditions relevant to the hot-stamping process during which Zn penetration did or did not occur in galvanized 22MnB5 press-hardening steel. A GleebleRTM 3500 was used to heat treat samples using hold times and temperatures similar to those used in industrial hot-stamping. Deformation at both elevated temperature and room temperature were conducted to assess the coating and substrate behavior related to forming (at high temperature) and service (at room temperature). The extent of alloying between the coating and substrate was assessed on undeformed samples heat treated under similar conditions to the deformed samples. The coating transitioned from an α + Gamma1 composition to an α (bcc Fe-Zn) phase with increased soak time. This transition likely corresponded to a decrease in availability of Zn-rich liquid in the coating during elevated temperature deformation. Penetration of Zn into the substrate sheet in the undeformed condition was not observed for any of the processing conditions examined. The number and depth of cracks in the coating and substrate steel was also measured in the hot-ductility samples. The number of cracks appeared to increase, while the depth of cracks appeared to decrease, with increasing soak time and increasing soak temperature. The crack depth appeared to be minimized in the sample soaked at the highest soak temperature (900 °C) for intermediate and extended soak times (300 s or 600 s). Zn penetration into the substrate steel was observed in the hot-ductility samples soaked at each hold temperature for the shortest soak time (10 s) before being deformed at elevated temperature. Reduction of area and elongation measurements showed that the coated sample soaked at the highest temperature and longest soak time

  1. Mathematical modelling of wet paper pressing

    NARCIS (Netherlands)

    Bežanovic, D.

    2005-01-01

    The aim of this project is to reduce energy costs in paper production by optimising the process in the press section of a paper machine. In this press section water is squeezed as it passes through the press nip. In a modern press section the moisture content of the sheet after three or four presses

  2. Isostatic Implications of Different Seismic and Gravity Derived Moho Depths for Antarctica

    Science.gov (United States)

    Ferraccioli, F.; Pappa, F.; Ebbing, J.

    2017-12-01

    Several studies with different methods have been performed to investigate the lithospheric structure of Antarctica, in particular the Moho as the crust-mantle boundary. Yet, seismological surveys are regionally limited or suffer from sparse station coverage due to the remoteness and size of the continent. On the other hand, gravity studies are inherently ambiguous and therefore not able to determine both the geometry and the density contrast of the Moho. Existing Moho depth models for Antarctica show large discrepancies, even among different seismological methods, but all the more between seismological and gravity models. As a first step towards a possible reconcilement, we perform non-linear gravity inversions with simultaneous consideration of seismological data. Depending on the seismological input data, different depths and density contrasts yield the best fit. The results, however, are not in line with the pure seismological models. Subsequently, we compute simple Airy-isostatic Moho depth models and evaluate these together with multiple Moho models from previous studies in terms of their gravitational signal, applying different values for the density contrast. The models' responses are checked against observational data: vertical gravity at 50 km altitude from the spherical harmonics expansion model GOCO05s, and the gravity gradient tensor at 225 km altitude from the GOCE gravity gradient grids. While the gravity responses from the seismological models show strong disagreements with the data, the Airy-isostatic models fit better. Yet, differences of up to 10 km in depth exist between the isostatic and the gravity-inverted Moho models. From these differences in vertical gravity, in the gravity gradients and in Moho depth, we identify regions where a simple density contrast is not sufficient to explain the observed gravitational field. We conclude that lateral and vertical density variations must be considered, which might originate from high-density lower

  3. Extensional Fault Evolution and its Flexural Isostatic Response During Iberia-Newfoundland Rifted Margin Formation

    Science.gov (United States)

    Gómez-Romeu, J.; Kusznir, N.; Manatschal, G.; Roberts, A.

    2017-12-01

    During the formation of magma-poor rifted margins, upper lithosphere thinning and stretching is achieved by extensional faulting, however, there is still debate and uncertainty how faults evolve during rifting leading to breakup. Seismic data provides an image of the present-day structural and stratigraphic configuration and thus initial fault geometry is unknown. To understand the geometric evolution of extensional faults at rifted margins it is extremely important to also consider the flexural response of the lithosphere produced by fault displacement resulting in footwall uplift and hangingwall subsidence. We investigate how the flexural isostatic response to extensional faulting controls the structural development of rifted margins. To achieve our aim, we use a kinematic forward model (RIFTER) which incorporates the flexural isostatic response to extensional faulting, crustal thinning, lithosphere thermal loads, sedimentation and erosion. Inputs for RIFTER are derived from seismic reflection interpretation and outputs of RIFTER are the prediction of the structural and stratigraphic consequences of recursive sequential faulting and sedimentation. Using RIFTER we model the simultaneous tectonic development of the Iberia-Newfoundland conjugate rifted margins along the ISE01-SCREECH1 and TGS/LG12-SCREECH2 seismic lines. We quantitatively test and calibrate the model against observed target data restored to breakup time. Two quantitative methods are used to obtain this target data: (i) gravity anomaly inversion which predicts Moho depth and continental lithosphere thinning and (ii) reverse post-rift subsidence modelling to give water and Moho depths at breakup time. We show that extensional faulting occurs on steep ( 60°) normal faults in both proximal and distal parts of rifted margins. Extensional faults together with their flexural isostatic response produce not only sub-horizontal exhumed footwall surfaces (i.e. the rolling hinge model) and highly rotated (60

  4. Conférence de presse | Press Conference

    CERN Multimedia

    CERN. Geneva; Bejar Alonso, Isabel

    2018-01-01

    10:00-11:00 Conférence de presse en présence de Lucio Rossi, chef du projet LHC à Haute Luminosité et Isabel Bejar Alonso, chargée de la configuration, de la qualité et des ressources du projet LHC à Haute Luminosité.

  5. Investing in a Large Stretch Press

    Science.gov (United States)

    Choate, M.; Nealson, W.; Jay, G.; Buss, W.

    1986-01-01

    Press for forming large aluminum parts from plates provides substantial economies. Study assessed advantages and disadvantages of investing in large stretch-forming press, and also developed procurement specification for press.

  6. WordPress 3 Cookbook

    CERN Document Server

    Shreves, Ric

    2011-01-01

    This is a Packt Cookbook, which means it contains step-by-step instructions to achieve a particular goal or solve a particular problem. There are plenty of screenshots and explained practical tasks to make comprehension quick and easy. This book is not specifically for developers or programmers; rather it can be used by anyone who wants to get more out of their WordPress blog by following step-by-step instructions. A basic knowledge of PHP/XHTML/CSS/WordPress is desirable but not necessary.

  7. Isostatic gravity map of the Monterey 30 x 60 minute quadrangle and adjacent areas, California

    Science.gov (United States)

    Langenheim, V.E.; Stiles, S.R.; Jachens, R.C.

    2002-01-01

    The digital dataset consists of one file (monterey_100k.iso) containing 2,385 gravity stations. The file, monterey_100k.iso, contains the principal facts of the gravity stations, with one point coded per line. The format of the data is described below. Each gravity station has a station name, location (latitude and longitude, NAD27 projection), elevation, and an observed gravity reading. The data are on the IGSN71 datum and the reference ellipsoid is the Geodetic Reference System 1967 (GRS67). The free-air gravity anomalies were calculated using standard formulas (Telford and others, 1976). The Bouguer, curvature, and terrain corrections were applied to the free-air anomaly at each station to determine the complete Bouguer gravity anomalies at a reduction density of 2.67 g/cc. An isostatic correction was then applied to remove the long-wavelength effect of deep crustal and/or upper mantle masses that isostatically support regional topography.

  8. Law and the Student Press.

    Science.gov (United States)

    Stevens, George E.; Webster, John B.

    Court cases and legal decisions involving the student press in the late 1960s and early 1970s are brought together in this book in order to show how the law has been applied to school officials and student journalists in high school, college, and the underground. The ten chapters cover the following topics: censorship, libel, obscenity, contempt,…

  9. Local and international press digest

    CERN Multimedia

    2008-01-01

    The following are the top stories in the Maltese and the international press today. The Times gives prominence to the Prime Minister's flying visit to Geneva yesterday, where he signed a research cooperation agreement with CERN, the European nuclear research organisation.

  10. Effect of gas release in hot molding on flexural strength of composite friction brake

    Science.gov (United States)

    Rusdja, Andy Permana; Surojo, Eko; Muhayat, Nurul; Raharjo, Wijang Wisnu

    2018-02-01

    Composite friction brake is a vital part of braking system which serves to reduce the speed of vehicle. To fulfill the requirement of brake performance, composite friction brake must have friction and mechanical characteristic as required. The characteristics of composite friction brake are affected by brake material formulation and manufacturing parameter. In the beginning of hot molding, intermittent hot pressing was carried out to release the gases that consist of ammonia gas and water vapor. In composite friction brake, phenolic resin containing hexamethylenetetramine (HMTA) is often used as a binder. During hot molding, the reaction of phenolic resin and HMTA forms ammonia gas. Hot molding also generates water vapor because raw materials absorb moisture from environment when they are placed in storage. The gas release in hot molding is supposed affecting mechanical properties because it avoid entrapped gas in composite, so that this research investigated effect of gas release on flexural strength. Manufacturing of composite specimen was carried out as follow: mixing of raw materials, cold molding, and hot molding. In this research, duration of intermittent hot pressing and number of gas release were varied. The flexural strength of specimen was measured using three point bending test. The results showed that flexural strength specimens that were manufactured without gas release, using 4 times gas release with intermittent hot pressing for 5 and 10 seconds were not remarkably different. Conversely, hot molding using 4 times gas release with intermittent hot pressing for 15 seconds decreased flexural strength of composite. Hot molding using 2, 4, and 8 times gas release with intermittent hot pressing for 10 seconds also had no effect on increasing flexural strength. Increasing of flexural strength of composite was obtained only by using 6 times gas release with intermittent hot pressing for 10 seconds.

  11. Solar 'hot spots' are still hot

    Science.gov (United States)

    Bai, Taeil

    1990-01-01

    Longitude distributions of solar flares are not random but show evidence for active zones (or hot spots) where flares are concentrated. According to a previous study, two hot spots in the northern hemisphere, which rotate with a synodic period of about 26.72 days, produced the majority of major flares, during solar cycles 20 and 21. The more prominent of these two hot spots is found to be still active during the rising part of cycle 22, producing the majority of northern hemisphere major flares. The synodic rotation period of this hot spot is 26.727 + or - 0.007 days. There is also evidence for hot spots in the southern hemisphere. Two hot spots separated by 180 deg are found to rotate with a period of 29.407 days, with one of them having persisted in the same locations during cycles 19-22 and the other, during cycles 20-22.

  12. Solar hot spots are still hot

    International Nuclear Information System (INIS)

    Bai, T.

    1990-01-01

    Longitude distributions of solar flares are not random but show evidence for active zones (or hot spots) where flares are concentrated. According to a previous study, two hot spots in the northern hemisphere, which rotate with a synodic period of about 26.72 days, produced the majority of major flares, during solar cycles 20 and 21. The more prominent of these two hot spots is found to be still active during the rising part of cycle 22, producing the majority of northern hemisphere major flares. The synodic rotation period of this hot spot is 26.727 + or - 0.007 days. There is also evidence for hot spots in the southern hemisphere. Two hot spots separated by 180 deg are found to rotate with a period of 29.407 days, with one of them having persisted in the same locations during cycles 19-22 and the other, during cycles 20-22. 14 refs

  13. Processing map and hot working mechanisms in a P/M TiAl alloy composite with in situ carbide and silicide dispersions

    International Nuclear Information System (INIS)

    Rao, K.P.; Prasad, Y.V.R.K.

    2010-01-01

    Research highlights: Mechanical alloying of Ti and Al with small additions of Si and C was used to synthesize metastable phases, which were incorporated in Ti-Al matrices using powder metallurgy techniques. These metastable phases (or also called as precursors), at higher temperatures, transformed in situ into very fine hard reinforcements that develop coherent interface with the surrounding matrix. Typically, Ti5Si3 and TiC are the end products after the synthesis of composite. In this study, hot working behavior of such composites has been studied using the concepts of processing maps to identify the safe and best processing conditions that should be adopted while forming this composite. Also, kinetic analysis of hot deformation has been performed to identify the dominant deformation mechanism. The results are compared with that of base TiAl matrix. The powder metallurgy route offers the advantage of working the material at much lower temperatures compared to the traditional cast and forge route. - Abstract: A titanium aluminide alloy composite with in situ carbide and silicide dispersions has been synthesized by mixing 90% of matrix with elemental composition of 46Ti-46Al-4Nb-2Cr-2Mn and 10% precursor with composition 55Ti-27Al-12Si-6C prepared by mechanical alloying. The powder mixture was blended for 2 h followed by hot isostatic pressing (HIP) at 1150 deg. C for 4 h under a pressure of 150 MPa. In addition to TiAl alloy matrix, the microstructure of the HIP'ed billet showed a small volume fraction of Nb-rich intermetallic phase along with carbide and silicide dispersions formed in situ during HIP'ing. Cylindrical specimens from the HIP'ed billets were compressed at temperatures and strain rates in the ranges of 800-1050 deg. C and 0.0001-1 s -1 . The flow curves exhibited flow softening leading to a steady-state flow at strain rates lower than 0.01 s -1 while fracture occurred at higher strain rates. The processing map developed on the basis of flow stress at

  14. Ultrasonic assisted hot metal powder compaction.

    Science.gov (United States)

    Abedini, Rezvan; Abdullah, Amir; Alizadeh, Yunes

    2017-09-01

    Hot pressing of metal powders is used in production of parts with similar properties to wrought materials. During hot pressing processes, particle rearrangement, plastic deformation, creep, and diffusion are of the most effective powder densification mechanisms. Applying ultrasonic vibration is thought to result in great rates of densification and therefore higher efficiency of the process is expected. This paper deals with the effects of power ultrasonic on the densification of AA1100 aluminum powder under constant applied stress. The effects of particle size and process temperature on the densification behavior are discussed. The results show that applying ultrasonic vibration leads to an improved homogeneity and a higher relative density. Also, it is found that the effect of ultrasonic vibration is greater for finer particles. Copyright © 2016 Elsevier B.V. All rights reserved.

  15. A press for the theater

    Directory of Open Access Journals (Sweden)

    Luciana Penna França

    2017-12-01

    Full Text Available Understanding the history of the amateur theater at the end of the XIXth century and the beginning of the XXth is possible, largely, because of the newspapers dedicated to the “theatrical affairs”. Such publications are important for the quantity and the diversity, revealing not only the place occupied by the theater in the capital, but also for the recognition of the press as a means of disclosure of plays, public education and opinion, artist projection, etc, not to mention personal affairs and requests, and the exchange of favors among managers and journalists. Even more, the press production of the dramatic amateurs clubs demonstrate the understanding of its role in the dissemination of ways to act and think beyond the stage and in the everyday life.

  16. Pressing technology for large bottoms

    International Nuclear Information System (INIS)

    Jilek, L.

    1986-01-01

    The technology has been selected of a circular plate bent into the shape of a trough, for pressing bottoms of pressure vessels from a circular plate of large diameter. The initial sheet is first bent in the middle by heating with the edges remaining straight. These are then welded longitudinally by electroslag welding and the circular shape is flame cut. The result will be a plate with a straight surface in the middle with raised edges which may be pressed into the desired shape. In this manner it is also possible to press pressure vessel bottoms with tube couplings from plates which are thickened in the middle and drilled; additional welding is then eliminated. Deformation from heat treatment may be avoided by the use of a fixture in the shape of a ring with a groove into which is fixed the edge of the bottom. During hardening of the bottom it will be necessary to care for the withdrawal of vapours and gases which would hamper uniform cooling. Bottom hardening with the grill and the cupola downwards has been proven. Deformation which occurs during treatment may to a certain extent be removed by calibration which cannot, however, be made without special fixtures and instruments. (J.B.)

  17. Spatio-spectral localization of isostatic coherence anisotropy in Australia and its relation to seismic anisotropy : Implications for lithopsheric deformation

    NARCIS (Netherlands)

    Simons, Frederik J.; Hilst, R.D. van der; Zuber, M.T.

    2003-01-01

    We investigate the two-dimensional (2-D) nature of the coherence between Bouguer gravity anomalies and topography on the Australian continent. The coherence function or isostatic response is commonly assumed to be isotropic. However, the fossilized strain field recorded by gravity anomalies and

  18. Process design of press hardening with gradient material property influence

    International Nuclear Information System (INIS)

    Neugebauer, R.; Schieck, F.; Rautenstrauch, A.

    2011-01-01

    Press hardening is currently used in the production of automotive structures that require very high strength and controlled deformation during crash tests. Press hardening can achieve significant reductions of sheet thickness at constant strength and is therefore a promising technology for the production of lightweight and energy-efficient automobiles. The manganese-boron steel 22MnB5 have been implemented in sheet press hardening owing to their excellent hot formability, high hardenability, and good temperability even at low cooling rates. However, press-hardened components have shown poor ductility and cracking at relatively small strains. A possible solution to this problem is a selective increase of steel sheet ductility by press hardening process design in areas where the component is required to deform plastically during crash tests. To this end, process designers require information about microstructure and mechanical properties as a function of the wide spectrum of cooling rates and sequences and austenitizing treatment conditions that can be encountered in production environments. In the present work, a Continuous Cooling Transformation (CCT) diagram with corresponding material properties of sheet steel 22MnB5 was determined for a wide spectrum of cooling rates. Heating and cooling programs were conducted in a quenching dilatometer. Motivated by the importance of residual elasticity in crash test performance, this property was measured using a micro-bending test and the results were integrated into the CCT diagrams to complement the hardness testing results. This information is essential for the process design of press hardening of sheet components with gradient material properties.

  19. Modularity of Pressing Tools for Screw Press Producing Solid Biofuels

    Directory of Open Access Journals (Sweden)

    Miloš Matúš

    2012-01-01

    Full Text Available This paper focuses on the development of the newly-patented structure of a screw briquetting machine for compacting biomass into a solid biofuel. The design of the machine is based on the results of a comprehensive study of the complicated process of biomass compaction. The patented structure meets two main goals: the elimination of axial forces, leading to increased lifetime of the bearings, and the new modular design of a pressing chamber and tools with their geometry based on the application of a mathematical model.

  20. MIS 5e relative sea-level changes in the Mediterranean Sea: Contribution of isostatic disequilibrium

    Science.gov (United States)

    Stocchi, Paolo; Vacchi, Matteo; Lorscheid, Thomas; de Boer, Bas; Simms, Alexander R.; van de Wal, Roderik S. W.; Vermeersen, Bert L. A.; Pappalardo, Marta; Rovere, Alessio

    2018-04-01

    Sea-level indicators dated to the Last Interglacial, or Marine Isotope Stage (MIS) 5e, have a twofold value. First, they can be used to constrain the melting of Greenland and Antarctic Ice Sheets in response to global warming scenarios. Second, they can be used to calculate the vertical crustal rates at active margins. For both applications, the contribution of glacio- and hydro-isostatic adjustment (GIA) to vertical displacement of sea-level indicators must be calculated. In this paper, we re-assess MIS 5e sea-level indicators at 11 Mediterranean sites that have been generally considered tectonically stable or affected by mild tectonics. These are found within a range of elevations of 2-10 m above modern mean sea level. Four sites are characterized by two separate sea-level stands, which suggest a two-step sea-level highstand during MIS 5e. Comparing field data with numerical modeling we show that (i) GIA is an important contributor to the spatial and temporal variability of the sea-level highstand during MIS 5e, (ii) the isostatic imbalance from the melting of the MIS 6 ice sheet can produce a >2.0 m sea-level highstand, and (iii) a two-step melting phase for the Greenland and Antarctic Ice Sheets reduces the differences between observations and predictions. Our results show that assumptions of tectonic stability on the basis of the MIS 5e records carry intrinsically large uncertainties, stemming either from uncertainties in field data and GIA models. The latter are propagated to either Holocene or Pleistocene sea-level reconstructions if tectonic rates are considered linear through time.

  1. Interaction between climate, volcanism, and isostatic rebound in Southeast Alaska during the last deglaciation

    Science.gov (United States)

    Praetorius, Summer; Mix, Alan; Jensen, Britta; Froese, Duane; Milne, Glenn A.; Wolhowe, Matthew; Addison, Jason A.; Prahl, Fred

    2016-01-01

    Observations of enhanced volcanic frequency during the last deglaciation have led to the hypothesis that ice unloading in glaciated volcanic terrains can promote volcanism through decompression melting in the shallow mantle or a reduction in crustal magma storage time. However, a direct link between regional climate change, isostatic adjustment, and the initiation of volcanism remains to be demonstrated due to the difficulty of obtaining high-resolution well-dated records that capture short-term climate and volcanic variability traced to a particular source region. Here we present an exceptionally resolved record of 19 tephra layers paired with foraminiferal oxygen isotopes and alkenone paleotemperatures from marine sediment cores along the Southeast Alaska margin spanning the last deglacial transition. Major element compositions of the tephras indicate a predominant source from the nearby Mt. Edgecumbe Volcanic Field (MEVF). We constrain the timing of this regional eruptive sequence to 14.6–13.1 ka. The sudden increase in volcanic activity from the MEVF coincides with the onset of Bølling–Allerød interstadial warmth, the disappearance of ice-rafted detritus, and rapid vertical land motion associated with modeled regional isostatic rebound in response to glacier retreat. These data support the hypothesis that regional deglaciation can rapidly trigger volcanic activity. Rapid sea surface temperature fluctuations and an increase in local salinity (i.e., δ18Osw) variability are associated with the interval of intense volcanic activity, consistent with a two-way interaction between climate and volcanism in which rapid volcanic response to ice unloading may in turn enhance short-term melting of the glaciers, plausibly via albedo effects on glacier ablation zones.

  2. An Ensemble Analysis of Antarctic Glacial Isostatic Adjustment and Sea Level

    Science.gov (United States)

    Lecavalier, B.; Tarasov, L.

    2016-12-01

    Inferences of past ice sheet evolution that lack any uncertainty assessment (implicit or explicit), have little value. A developing technique for explicit uncertainty quantification of glacial systems is Bayesian calibration of models against large observational data-sets (Tarasov et al., 2012). The foundation for a Bayesian calibration of a 3D glacial systems model (GSM) for Antarctica has recently been completed (Briggs et al., 2013; 2014; Briggs and Tarasov, 2013). Bayesian calibration thoroughly samples model uncertainties against fits to observational data to generate a probability distribution for the Antarctic Ice Sheet deglaciation with explicit and well-defined confidence intervals. To have validity as a complete inference of past ice sheet evolution, Bayesian calibration requires a model that "brackets reality".Past work has shown the GSM to have likely inadequate range of grounding line migration in certain sectors as well as persistent ice thickness biases in topographically complex regions (Briggs et al., 2014). To advance towards full calibration, these deficiencies are being addressed through a number of model developments. The grounding line scheme has been revised (Pollard and DeConto, 2012), the horizontal resolution is increased to 20 km, and boundary conditions are updated. The basal drag representation now includes the sub-grid treatment of the thermo-mechanical impacts of high basal roughness. Parametric uncertainties in basal drag for regions that are presently marine have been re-evaluated. The impact of past changes in ocean temperature on sub ice shelf melt is explicitly incorporated in the current ocean forcing parametric scheme. Uncertainties in earth rheology are also probed to robustly quantify uncertainties affiliated with glacial isostatic adjustment. The ensemble analysis of the Antarctic glacial system provides dynamical bounds on past and present Antarctica glacial isostatic adjustment and sea level contributions. This research

  3. Hot tub folliculitis

    Science.gov (United States)

    ... survives in hot tubs, especially tubs made of wood. Symptoms The first symptom of hot tub folliculitis ... may help prevent the problem. Images Hair follicle anatomy References D'Agata E. Pseudomonas aeruginosa and other ...

  4. WordPress Website Development

    OpenAIRE

    Lassila, Joonas

    2016-01-01

    The aim of this Bachelor’s thesis was to develop a WordPress mobile-first style website for the customer, Pohjois-Suomen Pesis. The main purpose of the development was to learn website designing principles and create a responsive website for the mobile and desktop platforms. The development process began defining the requirements of the website and creating the requirements document. Then next step was learning how to design a website layout and to choose the colour scheme for the site. T...

  5. Smashing WordPress Beyond the Blog

    CERN Document Server

    Hedengren, Thord Daniel

    2012-01-01

    The ultimate guide to WordPress, from the world's most popular resource for web designers and developers As one of the hottest tools on the web today for creating a blog, WordPress has evolved to be much more that just a blogging platform and has been pushed beyond its original purpose. With this new edition of a perennially popular WordPress resource, Smashing Magazine offers you the information you need so you can maximize the potential and power of WordPress. WordPress expert Thord Daniel Hedengren takes you beyond the basic blog to show you how to leverage the capabilities of WordPress to

  6. Teach yourself visually WordPress

    CERN Document Server

    Majure, Janet

    2012-01-01

    Get your blog up and running with the latest version of WordPress WordPress is one of the most popular, easy-to-use blogging platforms and allows you to create a dynamic and engaging blog, even if you have no programming skills or experience. Ideal for the visual learner, Teach Yourself VISUALLY WordPress, Second Edition introduces you to the exciting possibilities of the newest version of WordPress and helps you get started, step by step, with creating and setting up a WordPress site. Author and experienced WordPress user Janet Majure shares advice, insight, and best practices for taking full

  7. Modelling Hot Air Balloons.

    Science.gov (United States)

    Brimicombe, M. W.

    1991-01-01

    A macroscopic way of modeling hot air balloons using a Newtonian approach is presented. Misleading examples using a car tire and the concept of hot air rising are discussed. Pressure gradient changes in the atmosphere are used to explain how hot air balloons work. (KR)

  8. Pressing of three-layer, dry-formed MDF with binderless hardboard faces

    Science.gov (United States)

    Otto Suchsland; George E. Woodson; Charles W. McMillin

    1986-01-01

    Severely cooked Masonite pulp was used as face material in three-layer experimental medium-density fiberboard (MDF). The core layer consisted of conventional MDF furnish with resin binder added. The faces were formed absolutely dry without additives of any kind. The three-layer mat was hot-pressed to overall densities ranging from 44 to 56 pcf. The faces had hardboard-...

  9. Prediction of Pressing Quality for Press-Fit Assembly Based on Press-Fit Curve and Maximum Press-Mounting Force

    Directory of Open Access Journals (Sweden)

    Bo You

    2015-01-01

    Full Text Available In order to predict pressing quality of precision press-fit assembly, press-fit curves and maximum press-mounting force of press-fit assemblies were investigated by finite element analysis (FEA. The analysis was based on a 3D Solidworks model using the real dimensions of the microparts and the subsequent FEA model that was built using ANSYS Workbench. The press-fit process could thus be simulated on the basis of static structure analysis. To verify the FEA results, experiments were carried out using a press-mounting apparatus. The results show that the press-fit curves obtained by FEA agree closely with the curves obtained using the experimental method. In addition, the maximum press-mounting force calculated by FEA agrees with that obtained by the experimental method, with the maximum deviation being 4.6%, a value that can be tolerated. The comparison shows that the press-fit curve and max press-mounting force calculated by FEA can be used for predicting the pressing quality during precision press-fit assembly.

  10. Pellet presses for remote fuel fabrication

    International Nuclear Information System (INIS)

    Densley, P.J.

    1978-01-01

    Two types of mechanical presses are being tested from the remote operation and remote maintenance aspects. Results will be used to recommend the type of press and design considerations required for operation in a remotely operated and maintained process line

  11. Isostatic and Decompensative Gravity Anomalies of the Arabian Plate and Surrounding Regions: a Key for the Crustal Structure

    Science.gov (United States)

    Kaban, M. K.; El Khrepy, S.; Al-Arifi, N. S.

    2016-12-01

    The isostatic anomalies are often considered as one of the most useful correction of the gravity field for investigation of the upper crust structure in many practical applications. By applying this correction, a substantial part of the effect of deep density heterogeneity, which dominates in the Bouguer gravity anomaly, can be removed. With this approach, it is not even necessary to know the deep density structure of the crust and upper mantle in details; it is sufficient to prescribe some type of compensation (regional vs. local) and a compensation depth. However, even when all the parameters are chosen correctly, this reduction of the gravity field does not show the full gravity effect of unknown anomalies in the crust. The last ones should be also compensated to some extent; therefore their impact is substantially reduced by the isostatic compensation. Long ago (Cordell et al., 1991), it was suggested a so-called decompensative correction of the isostatic anomalies, which provides a possibility to separate these effects. However, the decompensative correction is very sensitive to the parameters of the compensation scheme. In the present study we analyse the ways to choose these parameters and extend this approach by assuming a possibility for the regional compensation via elastic deformations of the lithosphere. Based on this technique, we estimate the isostatic and decompensative anomalies for the Arabian plate and surrounding regions. The parameters of the isostatic model are chosen based on previous studies. It was demonstrated that the decompensative correction is very significant at the mid-range wavelengths and may exceed 100 mGal, therefore ignoring this effect would lead to wrong conclusions about the upper crust structure. The total amplitude of the decompensative anomalies reaches ±250 mGal, evidencing for both, large density anomalies of the upper crust (including sediments) and strong isostatic disturbances of the lithosphere. These results improve

  12. Press to compress contaminated wastes drums

    International Nuclear Information System (INIS)

    Prevost, J.

    1993-01-01

    This patent describes a press for contaminated wastes drums pressing. The press is made of a structure comprising a base and an upper stringer bind to the base by vertical bearers, a compression system comprising a main cylinder and a ram, connected to the upper stringer

  13. IDEAL: ACADEMIC PRESS JOURNALS ONLINE

    CERN Multimedia

    The Library

    2001-01-01

    All Academic Press journals are available online to CERN users for a test period which will last until the end of July. The service 'IDEALIBRARY' includes 174 scientific journals that cover several domains, ranging from engineering to mathematics, computing and physics. Titles covered are among others 'Atomic Data and Nuclear Data Tables', 'Nuclear Data Sheets', 'Annals of Physics', 'Journal of Parallel and Distributed Computing'. Reference citations present in each article are linked to the corresponding full text, when the latter is published by a member of the CrossRef consortium (members are: Elsevier, APS, AIP and others). Therefore, the navigation between articles and references is uninterrupted. A search engine allows queries by author, title and publication year. See http://www.idealibrary.com. At present the Library is evaluating a site license offer proposed by the publisher.

  14. Porous mandrels provide uniform deformation in hydrostatic powder metallurgy

    Science.gov (United States)

    Gripshover, P. J.; Hanes, H. D.

    1967-01-01

    Porous copper mandrels prevent uneven deformation of beryllium machining blanks. The beryllium powder is arranged around these mandrels and hot isostatically pressed to form the blanks. The mandrels are then removed by leaching.

  15. Professional WordPress design and development

    CERN Document Server

    Williams, Brad; Stern, Hal

    2014-01-01

    The highest rated WordPress development and design book on the market is back with an all new third edition. Professional WordPress is the only WordPress book targeted to developers, with advanced content that exploits the full functionality of the most popular CMS in the world. Fully updated to align with WordPress 4.1, this edition has updated examples with all new screenshots, and full exploration of additional tasks made possible by the latest tools and features. You will gain insight into real projects that currently use WordPress as an application framework, as well as the basic usage a

  16. Hot-working behavior of cast Pr-Fe-B magnets

    International Nuclear Information System (INIS)

    Shimoda, T.; Akioka, K.; Kobayashi, O.; Yamagami, T.; Ohki, T.; Miyagawa, M.; Yuri, T.

    1989-01-01

    The hot-working behavior of cast Pr-Fe-B magnets is investigated. The hot-working is done both at a low strain rate (hot-pressing) and a high strain rate (hot-rolling). Magnetic alignment induced by the hot-working is found to be closely related to the macrostructure of the cast ingots and the direction of principal stress. The appropriate structure is a columnar structure. The c-axis of the Pr2Fe14B phase is lying in the plane perpendicular to the growth direction of the dendrites. The principal stress during working should be given perpendicular to the growth direction

  17. Isostatic lines’ study to optimize steel space grid envelope structures for tall buildings according to their solicitations

    OpenAIRE

    Señís López, Roger

    2013-01-01

    Based on the first study completed with wind tunnel tests, the aim of this paper is to define a second methodology for the optimization of steel space grid envelope structures for tall buildings according to their isostatic lines according to their solicitations. It is by means of the comparison NatHaz online database and numerical simulation research of wind flow repercussion in buildings, through Computational Fluid Dynamics (CDF), that we can understand and analyse the grid ...

  18. The Influence of Sediment Isostatic Adjustment on Sea Level Change and Land Motion Along the U.S. Gulf Coast

    Science.gov (United States)

    Kuchar, Joseph; Milne, Glenn; Wolstencroft, Martin; Love, Ryan; Tarasov, Lev; Hijma, Marc

    2018-01-01

    Sea level rise presents a hazard for coastal populations, and the Mississippi Delta (MD) is a region particularly at risk due to the high rates of land subsidence. We apply a gravitationally self-consistent model of glacial and sediment isostatic adjustment (SIA) along with a realistic sediment load reconstruction in this region for the first time to determine isostatic contributions to relative sea level (RSL) and land motion. We determine optimal model parameters (Earth rheology and ice history) using a new high-quality compaction-free sea level indicator database. Using the optimal model parameters, we show that SIA can lower predicted RSL in the MD area by several meters over the Holocene and so should be taken into account when modeling these data. We compare modeled contemporary rates of vertical land motion with those inferred using GPS. This comparison indicates that isostatic processes can explain the majority of the observed vertical land motion north of latitude 30.7°N, where subsidence rates average about 1 mm/yr; however, subsidence south of this latitude shows large data-model discrepancies of greater than 3 mm/yr, indicating the importance of nonisostatic processes. This discrepancy extends to contemporary RSL change, where we find that the SIA contribution in the Delta is on the order of 10-1 mm/yr. We provide estimates of the isostatic contributions to 20th and 21st century sea level rates at Gulf Coast Permanent Service for Mean Sea Level tide gauge locations as well as vertical and horizontal land motion at GPS station locations near the MD.

  19. ISOSTATICALLY DISTURBED TERRAIN OF NORTHWESTERN ANDES MOUNTAINS FROM SPECTRALLY CORRELATED FREE-AIR AND GRAVITY TERRAIN DATA

    Directory of Open Access Journals (Sweden)

    Hernández P Orlando

    2006-12-01

    Full Text Available Recently revised models on global tectonics describe the convergence of the North Andes, Nazca, Caribbean and South American Plates and their seismicity, volcanism, active faulting and extreme
    topography. The current plate boundaries of the area are mainly interpreted from volcanic and seismic datasets with variable confidence levels. New insights on the isostatic state and plate boundaries of
    the northwestern Andes Mountains can be obtained from the spectral analysis of recently available gravity and topography data.
    Isostatically disturbed terrain produces free-air anomalies that are highly correlated with the gravity effects of the terrain. The terrain gravity effects (TGE and free air gravity anomalies (FAGA of the
    Andes mountains spectral correlation data confirms that these mountains are isostatically disturbed. Strong negative terrain-correlated FAGA along western South America and the Greater and Lesser Antilles are consistent with anomalously deepened mantle displaced by subducting oceanic plates.

    Inversion of the compensated terrain gravity effects (CTGE reveals plate subduction systems with alternating shallower and steeper subduction angles. The gravity modeling highlights crustal
    deformation from plate collision and subduction and other constraints on the tectonism of the plate boundary zones for the region.

  20. Hot Surface Ignition

    OpenAIRE

    Tursyn, Yerbatyr; Goyal, Vikrant; Benhidjeb-Carayon, Alicia; Simmons, Richard; Meyer, Scott; Gore, Jay P.

    2015-01-01

    Undesirable hot surface ignition of flammable liquids is one of the hazards in ground and air transportation vehicles, which primarily occurs in the engine compartment. In order to evaluate the safety and sustainability of candidate replacement fuels with respect to hot surface ignition, a baseline low lead fuel (Avgas 100 LL) and four experimental unleaded aviation fuels recommended for reciprocating aviation engines were considered. In addition, hot surface ignition properties of the gas tu...

  1. Glacial isostatic adjustment on the Northern Hemisphere - new results from GRACE

    Science.gov (United States)

    Mueller, J.; Steffen, H.; Gitlein, O.; Denker, H.; Timmen, L.

    2007-12-01

    The Earth's gravity field mapped by the Gravity Recovery and Climate Experiment (GRACE) satellite mission shows variations due to the integral effect of mass variations in the atmosphere, hydrosphere and geosphere. The Earth's gravity field is provided in form of monthly solutions by several institutions, e.~g. GFZ Potsdam, CSR and JPL. During the GRACE standard processing of these analysis centers, oceanic and atmospheric contributions as well as tidal effects are reduced. The solutions of the analysis centers differ slightly, which is due the application of different reduction models and center-specific processing schemes. We present our investigation of mass variations in the areas of glacial isostatic adjustment (GIA) in North America and Northern Europe from GRACE data. One key issue is the separation of GIA parts and the reduction of the observed quantities by applying dedicated filters (e.~g. isotropic, non-isotropic, and destriping filters) and global models of hydrological variations (e.~g. WGHM, LaDWorld, GLDAS). In a further step, we analyze the results of both regions regarding their reliability, and finally present a comparison to results of a geodynamical modeling and absolute gravity measurements. Our results clearly show that the quality of the GRACE-derived gravity- change signal benefits from improved reduction models and chosen analysis techniques. Nevertheless, the comparison to results of geodynamic models still reveals differences, and thus further studies are in progress.

  2. Gravity measurements in southeastern Alaska reveal negative gravity rate of change caused by glacial isostatic adjustment

    Science.gov (United States)

    Sun, W.; Miura, S.; Sato, T.; Sugano, T.; Freymueller, J.; Kaufman, M.; Larsen, C. F.; Cross, R.; Inazu, D.

    2010-12-01

    For the past 300 years, southeastern Alaska has undergone rapid ice-melting and land uplift attributable to global warming. Corresponding crustal deformation (3 cm/yr) caused by the Little Ice Age retreat is detectable with modern geodetic techniques such as GPS and tidal gauge measurements. Geodetic deformation provides useful information for assessing ice-melting rates, global warming effects, and subcrustal viscosity. Nevertheless, integrated geodetic observations, including gravity measurements, are important. To detect crustal deformation caused by glacial isostatic adjustment and to elucidate the viscosity structure in southeastern Alaska, Japanese and U.S. researchers began a joint 3-year project in 2006 using GPS, Earth tide, and absolute gravity measurements. A new absolute gravity network was established, comprising five sites around Glacier Bay, near Juneau, Alaska. This paper reports the network's gravity measurements during 2006-2008. The bad ocean model in this area hindered ocean loading correction: Large tidal residuals remain in the observations. Accurate tidal correction necessitated on-site tidal observation. Results show high observation precision for all five stations: day ice thickness changes. A gravity bias of about -13.2 ± 0.1 mGal exists between the Potsdam and current FG5 gravity data.

  3. Geologic and isostatic map of the Nenana Basin area, central Alaska

    Science.gov (United States)

    Frost, G.M.; Barnes, D.F.; Stanley, R.G.

    2002-01-01

    Introduction The Nenana Basin area is a prospective petroleum province in central Alaska, and this geologic and isostatic gravity map is part of a petroleum resource assessment of the area. The geology was compiled from published sources (Chapman and others, 1971, 1975a, 1975b, 1982; Chapman and Yeend, 1981; Csejtey and others, 1986; Jones and others, 1983; Pewe and others, 1966; Reed, 1961; and Weber and others, 1992), as shown on the index map (map sheet). Map units are organized and presented according to the scheme of lithotectonic terranes proposed by Jones and others (1987) and Silberling and Jones (1984); we recognize, however, that this terrane scheme is controversial and likely to be revised in the future. In some cases, we combined certain terranes because we were unable to match the terrane boundaries given by Jones and others (1987) and Silberling and Jones (1984) with specific faults shown on existing geologic maps. Postaccretion cover deposits represent overlap assemblages that depositionally overlie accreted terranes. Plutonic igneous rocks shown on this map include several plutons that are clearly postaccretionary, based on isotopic ages and (or) field relations. It is possible that some of the plutons predate accretion, but this has not been demonstrated. According to Jones and others (1982), the terranes in the area of our map were assembled during late Mesozoic or earliest Cenozoic time. The gravity contours are derived from data used in earlier compilations (Barnes, 1961, 1977; Hackett, 1981; Valin and others, 1991; Frost and Stanley, 1991) that are supplemented by some National Oceanic and Atmospheric Administration data along the Alaska Pipeline level line (W.E. Strange, written commun., 1980). The earlier compilations were used for simple Bouguer maps, prepared primarily by non-digital methods, and are superseded by this map. The present map is the result of digital processing that includes the 1967 Geodetic Reference System, the IGSN-71

  4. Preliminary isostatic residual gravity anomaly map of Paso Robles 30 x 60 minute quadrangle, California

    Science.gov (United States)

    McPhee, D.K.; Langenheim, V.E.; Watt, J.T.

    2011-01-01

    This isostatic residual gravity map is part of an effort to map the three-dimensional distribution of rocks in the central California Coast Ranges and will serve as a basis for modeling the shape of basins and for determining the location and geometry of faults within the Paso Robles quadrangle. Local spatial variations in the Earth\\'s gravity field, after accounting for variations caused by elevation, terrain, and deep crustal structure reflect the distribution of densities in the mid- to upper crust. Densities often can be related to rock type, and abrupt spatial changes in density commonly mark lithological or structural boundaries. High-density rocks exposed within the central Coast Ranges include Mesozoic granitic rocks (exposed northwest of Paso Robles), Jurassic to Cretaceous marine strata of the Great Valley Sequence (exposed primarily northeast of the San Andreas fault), and Mesozoic sedimentary and volcanic rocks of the Franciscan Complex [exposed in the Santa Lucia Range and northeast of the San Andreas fault (SAF) near Parkfield, California]. Alluvial sediments and Tertiary sedimentary rocks are characterized by low densities; however, with increasing depth of burial and age, the densities of these rocks may become indistinguishable from those of older basement rocks.

  5. Titanium Brazing for Structures and Survivability

    Science.gov (United States)

    2007-05-01

    first method ( Weld +HIP) was a tungsten inert gas ( TIG ) weld around the exterior of the Ti- 6Al-4V blocks followed by hot isostatic pressing (HIP) at...beam welding plus hot isostatic pressing (E-beam+HIP) process in the encapsulation of a ceramic within a titanium structure. The testing of the...different joining methods highlighted some definite candidates for the replacement of the E-beam+HIP process , such as the Weld +HIP, and demonstrated

  6. RELATIONSHIP BETWEEN COMPACTING PRESSURE AND CONDITIONS IN PRESSING CHAMBER DURING BIOMASS PRESSING

    Directory of Open Access Journals (Sweden)

    Peter Križan

    2016-02-01

    Full Text Available In this paper, we will present the impact of the conditions in pressing chambers during the pressing of wooden briquettes. The conditions in pressing chambers can significantly impact the resulting compacting pressure required for the pressing of briquettes. In the introduction, we show which parameters of the pressing chamber during pressing can impact the resulting compacting pressure. The experiment results which are shown in this paper described the detected impact of some important pressing chamber parameters. This experiment aims to detect the pressing chamber length impact and the impact of the way of pressing. By setting the pressing conditions, we will be able to achieve the suitable resulting compacting pressure with respect to the required final briquettes quality.

  7. Towards a more responsible press

    Directory of Open Access Journals (Sweden)

    Taimur ul Hassan

    2012-12-01

    Full Text Available The article analyses Pakistan’s newspapers’ performance with regard to civil society in2003 by using content analysis approach. There is no gainsaying that a strong civil society guaranteesa strong democracy. In Pakistan, spells of military rule have stunted the growth of democracy,adversely affecting civil society. Media too has suffered as a result. Normative theories of media callfor laying down norms and conventions for media. In democracy, all sections of society should berepresented in media. In Pakistan’s case, due to military regimes and quasi democratic governments,combined with the demands of market economy, the media have largely not been able to fulfill thisresponsibility towards society. Social Responsibility demands that the media must fulfill itsresponsibility towards society, while giving a free space to all voices of society. In Pakistan, whethernewspapers played that role in 2003 when civil society had accelerated its campaign to end honorkillings and crimes against women is investigated. The findings show that newspapers did supportcivil society, showing a gradual movement towards a more responsible press.

  8. Press Advertising – Varieties and Sub-Varieties. Methods of Promoting the Press

    OpenAIRE

    Mikosz, Joanna

    2016-01-01

    In the text entitled “Press advertising – varieties and sub-varieties. Methods of promoting the press”, the author discusses press advertising, which is a fast developing mass-media phenomenon. Modernity has granted press advertising a high quality of print and paper, as well as Infinite possibilities of combining various promotional forms with the press. The author argues that press advertising is one of the best ways in which a company can communicate with the market. Its advantage is, abov...

  9. Exercise in Experimental Plastics Technology: Hot Embossing of Polymers with surface microstructure

    DEFF Research Database (Denmark)

    Eriksson, Torbjörn Gerhard; Rasmussen, Henrik Koblitz

    2004-01-01

    Hot Embossing of polymers with surface microstructure Polymer materials have proven to be good materials for manufacturing nano/ and microstructure. There are three major processing techniques: hot embossing, injection moulding and casting. Hot embossing provides several advantages such as relati......Hot Embossing of polymers with surface microstructure Polymer materials have proven to be good materials for manufacturing nano/ and microstructure. There are three major processing techniques: hot embossing, injection moulding and casting. Hot embossing provides several advantages...... such as relatively low cost for embossing tools, simple operation and high replication accuracy for small features. Two different plastic materials will be used to replicate surface microstructures by hot embossing. The hot embossing will be done in a hydraulic press where it is easy to control temperature...

  10. Evaluation of hot forming effects mapping for CAE analyses

    Science.gov (United States)

    Knoerr, L.; Faath, T.; Dykeman, J.; Malcolm, S.

    2016-08-01

    Hot forming has grown significantly in the manufacturing of structural components within the vehicle Body-In-White construction. The superior strength of press hardened steels not only guarantee high resistance to deformation, it also brings a significant weight saving compared to conventional cold formed products. However, the benefit of achieving ultrahigh strength with hot stamping, comes with a reduction in ductility of the press hardened part. This will require advanced material modeling to capture the predicted performances accurately. A technique to optically measure and map the thinning distribution after hot stamping has shown to improve numerical analysis for fracture prediction. The proposed method to determine the forming effects and mapping to CAE models can be integrated into the Vehicle Development Process to shorten the time to production.

  11. Smashing WordPress Beyond the Blog

    CERN Document Server

    Hedengren, Thord Daniel

    2011-01-01

    Smashing WordPress shows you how to utilize the power of the WordPress platform, and provides a creative spark to help you build WordPress-powered sites that go beyond the obvious. The second edition of Smashing WordPress has been updated for WordPress 3.1+, which includes internal, custom post types, the admin bar, and lots of other useful new features. You will learn the core concepts used to post types, the admin bar, and lots of other useful new features. You will learn the core concepts used to build just about anything in WordPress, resulting in fast deployments and greater design flexib

  12. PRESS FREEDOM IN SINGAPORE AND MALAYSIA: DEFAMATION

    OpenAIRE

    Georgia Kate Chapman

    2015-01-01

    This paper focuses on the arguments around restriction on freedom of the press in the Strong States of Singapore and Malaysia. It assesses the presence of constraints on press freedoms in democratic western countries imposed by corporation rather than state and the similar effects that these constraints may have on bias present in publicly accessible news reporting. It argues that independence of the press does not just require protection from legal and executive regulation, but also protecti...

  13. WordPress 3.7 complete

    CERN Document Server

    Król, Karol

    2013-01-01

    WordPress 3.5 Complete: Third Edition is a comprehensive and step-by-step tutorial packed with screenshots and examples to make it easy and quick to pick it up.This WordPress book is a guide to WordPress for online publishers and web developers. If you are new to blogging and want to create your own blog or website from scratch, then ""WordPress 3.5 Complete: Third Edition"" is for you. No prior knowledge of HTML/CSS or PHP is required.

  14. Activation of Selected Core Muscles during Pressing

    Directory of Open Access Journals (Sweden)

    Thomas W. Nesser

    2015-10-01

    Full Text Available Introduction: Unstable surface training is often used to activate core musculature during resistance training. Unfortunately, unstable surface training is risky and leads to detraining. Purpose: The purpose of this study was to determine core muscle activation during stable surface ground-based lifts. Methods: Fourteen recreational trained and former NCAA DI athletes (weight 84.2 ± 13.3 kg; height 176.0 ± 9.5 cm; age 20.9 ± 2.0 years volunteered for participation. Subjects completed two ground-based lifts: overhead press and push-press. Surface EMG was recorded from 4 muscles on the right side of the body (Rectus Abdominus (RA, External Oblique (EO, Transverse Abdominus (TA, and Erector Spinae (ES. Results: Paired sample T-tests identified significant muscle activation differences between the overhead press and the push-press included ES and EO. Average and peak EMG for ES was significantly greater in push-press (P<0.01. Anterior displacement of COP was significantly greater in push-press compared to overhead press during the eccentric phase. Conclusion: The push-press was identified as superior in core muscle activation when compared to the overhead pressing exercise. Keywords: torso, stability, weight lifting, resistance training

  15. Improving Dryer and Press Efficiencies Through Combustion of Hydrocarbon Emissions

    Energy Technology Data Exchange (ETDEWEB)

    Sujit Banerjee

    2005-10-31

    Emission control devices on dryers and presses have been legislated into the industry, and are now an integral part of the drying system. These devices consume large quantities of natural gas and electricity and down-sizing or eliminating them will provide major energy savings. The principal strategy taken here focuses on developing process changes that should minimize (and in some cases eliminate) the need for controls. A second approach is to develop lower-cost control options. It has been shown in laboratory and full-scale work that Hazardous Air Pollutants (HAPs) emerge mainly at the end of the press cycle for particleboard, and, by extension, to other prod-ucts. Hence, only the air associated with this point of the cycle need be captured and treated. A model for estimating terpene emissions in the various zones of veneer dryers has been developed. This should allow the emissions to be concentrated in some zones and minimized in others, so that some of the air could be directly released without controls. Low-cost catalysts have been developed for controlling HAPs from dryers and presses. Catalysts conventionally used for regenerative catalytic oxidizers can be used at much lower temperatures for treating press emissions. Fluidized wood ash is an especially inexpensive mate-rial for efficiently reducing formaldehyde in dryer emissions. A heat transfer model for estimating pinene emissions from hot-pressing strand for the manufacture of flakeboard has been constructed from first principles and validated. The model shows that most of the emissions originate from the 1-mm layer of wood adjoining the platen surface. Hence, a simple control option is to surface a softwood mat with a layer of hardwood prior to pressing. Fines release a disproportionate large quantity of HAPs, and it has been shown both theo-retically and in full-scale work that particles smaller than 400 µm are principally responsible. Georgia-Pacific is considering green

  16. World Gravity Map: a set of global complete spherical Bouguer and isostatic anomaly maps and grids

    Science.gov (United States)

    Bonvalot, S.; Balmino, G.; Briais, A.; Kuhn, M.; Peyrefitte, A.; Vales, N.; Biancale, R.; Gabalda, G.; Reinquin, F.

    2012-04-01

    We present here a set of digital maps of the Earth's gravity anomalies (surface free air, Bouguer and isostatic), computed at Bureau Gravimetric International (BGI) as a contribution to the Global Geodetic Observing Systems (GGOS) and to the global geophysical maps published by the Commission for the Geological Map of the World (CGMW) with support of UNESCO and other institutions. The Bouguer anomaly concept is extensively used in geophysical interpretation to investigate the density distributions in the Earth's interior. Complete Bouguer anomalies (including terrain effects) are usually computed at regional scales by integrating the gravity attraction of topography elements over and beyond a given area (under planar or spherical approximations). Here, we developed and applied a worldwide spherical approach aimed to provide a set of homogeneous and high resolution gravity anomaly maps and grids computed at the Earth's surface, taking into account a realistic Earth model and reconciling geophysical and geodetic definitions of gravity anomalies. This first version (1.0) has been computed by spherical harmonics analysis / synthesis of the Earth's topography-bathymetry up to degree 10800. The detailed theory of the spherical harmonics approach is given in Balmino et al., (Journal of Geodesy, 2011). The Bouguer and terrain corrections have thus been computed in spherical geometry at 1'x1' resolution using the ETOPO1 topography/bathymetry, ice surface and bedrock models from the NOAA (National Oceanic and Atmospheric Administration) and taking into account precise characteristics (boundaries and densities) of major lakes, inner seas, polar caps and of land areas below sea level. Isostatic corrections have been computed according to the Airy-Heiskanen model in spherical geometry for a constant depth of compensation of 30km. The gravity information given here is provided by the Earth Geopotential Model (EGM2008), developed at degree 2160 by the National Geospatial

  17. AREVA in Mongolia - Press kit

    International Nuclear Information System (INIS)

    2013-01-01

    (hydrogeological tests, certification of the resources, in situ recovery tests, etc.) in the Dulaan Uul area ('Hot Mountain' in Mongolian) in a vast sedimentary basin of the Gobi desert. The geological data enabling a technical and economic feasibility of the mining project are being collected by AREVA with respect for the environment and in partnership with the Mongolian authorities

  18. Glacial Isostatic Adjustment as a Source of Noise for the Interpretation of GRACE Data

    Science.gov (United States)

    Wahr, J.; Velicogna, I.; Paulson, A.

    2009-05-01

    Viscoelastic relaxation in the Earth's mantle caused by wide-spread deglaciation following the last glacial maximum (LGM), can appear as a secular trend in measurements of the Earth's time-variable gravity field. The presence of this trend can provide an opportunity to use gravity observations to constrain models of the glacial isostatic adjustment (GIA) process. But it can also be a nuisance for people who are using the gravity observations to learn about other things. Gravity observations, whether from satellites or from ground-based gravimeters, can not distinguish between the gravitational effects of water/snow/ice variations on or near the surface, and those caused by density variations deep within the mantle. Unmodeled or mismodeled GIA signals can sometimes make it difficult to use gravity observations to learn about secular changes in water/snow/ice from such places as northern Canada, Scandinavia, Antarctica, and Greenland: places where there was considerable long-term deglaciation following the LGM. These issues have become particularly important since the 2002 launch of the GRACE gravity satellite mission. GIA signals in northern Canada and Scandinavia are clearly evident in the GRACE data. But the presence of GIA signals in these and other regions has sometimes caused problems for long-term hydrological and, especially, cryospheric studies with GRACE. GIA model errors, for example, are by far the largest source of uncertainty when using GRACE to estimate present-day thinning rates of the Antarctic ice sheet. This talk will discuss the contributions of the GIA signal to GRACE time-variable gravity measurements; partly as an opportunity to study the GIA process, but mostly as a source of uncertainty for other applications.

  19. Empirical estimation of present-day Antarctic glacial isostatic adjustment and ice mass change

    Science.gov (United States)

    Gunter, B. C.; Didova, O.; Riva, R. E. M.; Ligtenberg, S. R. M.; Lenaerts, J. T. M.; King, M. A.; van den Broeke, M. R.; Urban, T.

    2014-04-01

    This study explores an approach that simultaneously estimates Antarctic mass balance and glacial isostatic adjustment (GIA) through the combination of satellite gravity and altimetry data sets. The results improve upon previous efforts by incorporating a firn densification model to account for firn compaction and surface processes as well as reprocessed data sets over a slightly longer period of time. A range of different Gravity Recovery and Climate Experiment (GRACE) gravity models were evaluated and a new Ice, Cloud, and Land Elevation Satellite (ICESat) surface height trend map computed using an overlapping footprint approach. When the GIA models created from the combination approach were compared to in situ GPS ground station displacements, the vertical rates estimated showed consistently better agreement than recent conventional GIA models. The new empirically derived GIA rates suggest the presence of strong uplift in the Amundsen Sea sector in West Antarctica (WA) and the Philippi/Denman sectors, as well as subsidence in large parts of East Antarctica (EA). The total GIA-related mass change estimates for the entire Antarctic ice sheet ranged from 53 to 103 Gt yr-1, depending on the GRACE solution used, with an estimated uncertainty of ±40 Gt yr-1. Over the time frame February 2003-October 2009, the corresponding ice mass change showed an average value of -100 ± 44 Gt yr-1 (EA: 5 ± 38, WA: -105 ± 22), consistent with other recent estimates in the literature, with regional mass loss mostly concentrated in WA. The refined approach presented in this study shows the contribution that such data combinations can make towards improving estimates of present-day GIA and ice mass change, particularly with respect to determining more reliable uncertainties.

  20. Ice loading model for Glacial Isostatic Adjustment in the Barents Sea constrained by GRACE gravity observations

    Science.gov (United States)

    Root, Bart; Tarasov, Lev; van der Wal, Wouter

    2014-05-01

    The global ice budget is still under discussion because the observed 120-130 m eustatic sea level equivalent since the Last Glacial Maximum (LGM) can not be explained by the current knowledge of land-ice melt after the LGM. One possible location for the missing ice is the Barents Sea Region, which was completely covered with ice during the LGM. This is deduced from relative sea level observations on Svalbard, Novaya Zemlya and the North coast of Scandinavia. However, there are no observations in the middle of the Barents Sea that capture the post-glacial uplift. With increased precision and longer time series of monthly gravity observations of the GRACE satellite mission it is possible to constrain Glacial Isostatic Adjustment in the center of the Barents Sea. This study investigates the extra constraint provided by GRACE data for modeling the past ice geometry in the Barents Sea. We use CSR release 5 data from February 2003 to July 2013. The GRACE data is corrected for the past 10 years of secular decline of glacier ice on Svalbard, Novaya Zemlya and Frans Joseph Land. With numerical GIA models for a radially symmetric Earth, we model the expected gravity changes and compare these with the GRACE observations after smoothing with a 250 km Gaussian filter. The comparisons show that for the viscosity profile VM5a, ICE-5G has too strong a gravity signal compared to GRACE. The regional calibrated ice sheet model (GLAC) of Tarasov appears to fit the amplitude of the GRACE signal. However, the GRACE data are very sensitive to the ice-melt correction, especially for Novaya Zemlya. Furthermore, the ice mass should be more concentrated to the middle of the Barents Sea. Alternative viscosity models confirm these conclusions.

  1. Using coastal lagoons to better constrain the isostatic signal in the western Mediterranean Sea

    Science.gov (United States)

    Vacchi, M.; Rovere, A.; Melis, R. T.; Ghilardi, M.; Marriner, N.; Giaime, M.

    2017-12-01

    Coastal lagoons represent a very common feature of the microtidal Mediterranean coastlines. They are inland waterbodies, usually developing parallel to the coast, typically separated from the open sea by a sandy barrier. One or more restricted inlets ensure their continuous or intermittent connection to the open sea. The water depth is generally less than 1 m and seldom exceeds a few meters. They represent a very useful proxy for the reconstruction of Mediterranean Relative Sea Level (RSL). However, caution should be used in the definition of a correct indicative meaning that can be obtained only with a multiproxy analysis of both sedimentary features and faunal assemblages of the cores extracted in marshy to lagoonal environment. We report here the results of a wide coring campaign we carried out in in the last 2 years in a number of Mediterranean lagoons located close to important archaeological settlements in Corsica (France) Sardinia (Italy) and Mallorca Island (Spain). The multiproxy analysis of the cores allowed defining the depositional environments and their relationship (or non relationship) with the former mean sea level. These data were chronologically supported by a significant dataset of more than 100 new 14C dating performed on organic sediments, wood, plant remains and marine/lagoonal shells. We then produced alarge amount of new data to constrain the RSL evolution in the center of Western Mediterranean where the available geophysical models predict the largest glacio-hydro isostatic (GIA) influence at basin scale. However, such models where tested only on a limited dataset mainly composed of archaeological RSL indicators (i.e. last 2 ka BP). Our new record, expanding the last 10 ka BP, significantly improves the ability to define the general anatomy of Mediterranean Holocene RSL changes and to constrain the maximal GIA magnitude in the basin.

  2. Teenagers as Victims in the Press

    Science.gov (United States)

    Andersson, Gunvor; Lundstrom, Tommy

    2007-01-01

    Research into press reporting on young people has tended to concentrate on young people as offenders. In contrast, this article focuses on press coverage of teenagers as victims. Reports in two Swedish newspapers (a morning broadsheet and an evening tabloid) were studied over a period of four months and subjected to a qualitative analysis of…

  3. Communicators take nine Virginia Press Women awards

    OpenAIRE

    Owczarski, Mark

    2008-01-01

    Three Virginia Tech communicators have won Virginia Press Women awards. The winners - Susan Trulove, research division communications manager; Clara Cox, university publications director; and Heather Riley Chadwick, College of Architecture and Urban Studies communication manager - were announced at the Virginia Press Women Annual Spring Conference in Staunton, Va.

  4. 1979: The Campus Student Press in America.

    Science.gov (United States)

    Ingelhart, Louis E.

    1979-01-01

    Discusses a number of topics involving the campus press, including the independence of campus publications, censorship issues, the relationship between the student press and the college administrator, the financing of student newspapers, yearbook production and financing, probable future student publications trends, and the need for appropriate…

  5. Hot Weather Tips

    Science.gov (United States)

    ... the person plenty of water and fruit or vegetable juice even if they say they’re not thirsty. No alcohol, coffee or tea. Seek medical help if you suspect dehydration. Light meals: Avoid hot, heavy meals and don’ ...

  6. China's 'Hot Money' Problems

    National Research Council Canada - National Science Library

    Martin, Michael F; Morrison, Wayne M

    2008-01-01

    .... The recent large inflow of financial capital into China, commonly referred to as "hot money," has led some economists to warn that such flows may have a destabilizing effect on China's economy...

  7. The impact of lateral variations in lithospheric thickness on glacial isostatic adjustment in West Antarctica

    Science.gov (United States)

    Nield, Grace A.; Whitehouse, Pippa L.; van der Wal, Wouter; Blank, Bas; O'Donnell, John Paul; Stuart, Graham W.

    2018-04-01

    Differences in predictions of Glacial Isostatic Adjustment (GIA) for Antarctica persist due to uncertainties in deglacial history and Earth rheology. The Earth models adopted in many GIA studies are defined by parameters that vary in the radial direction only and represent a global average Earth structure (referred to as 1D Earth models). Over-simplifying actual Earth structure leads to bias in model predictions in regions where Earth parameters differ significantly from the global average, such as West Antarctica. We investigate the impact of lateral variations in lithospheric thickness on GIA in Antarctica by carrying out two experiments that use different rheological approaches to define 3D Earth models that include spatial variations in lithospheric thickness. The first experiment defines an elastic lithosphere with spatial variations in thickness inferred from seismic studies. We compare the results from this 3D model with results derived from a 1D Earth model that has a uniform lithospheric thickness defined as the average of the 3D lithospheric thickness. Irrespective of deglacial history and sub-lithospheric mantle viscosity, we find higher gradients of present-day uplift rates (i.e. higher amplitude and shorter wavelength) in West Antarctica when using the 3D models, due to the thinner-than-1D-average lithosphere prevalent in this region. The second experiment uses seismically-inferred temperature as input to a power-law rheology thereby allowing the lithosphere to have a viscosity structure. Modelling the lithosphere with a power-law rheology results in behaviour that is equivalent to a thinner-lithosphere model, and it leads to higher amplitude and shorter wavelength deformation compared with the first experiment. We conclude that neglecting spatial variations in lithospheric thickness in GIA models will result in predictions of peak uplift and subsidence that are biased low in West Antarctica. This has important implications for ice-sheet modelling

  8. Evaluating Greenland glacial isostatic adjustment corrections using GRACE, altimetry and surface mass balance data

    International Nuclear Information System (INIS)

    Sutterley, Tyler C; Velicogna, Isabella; Csatho, Beata; Rezvan-Behbahani, Soroush; Babonis, Greg; Van den Broeke, Michiel

    2014-01-01

    Glacial isostatic adjustment (GIA) represents a source of uncertainty for ice sheet mass balance estimates from the Gravity Recovery and Climate Experiment (GRACE) time-variable gravity measurements. We evaluate Greenland GIA corrections from Simpson et al (2009 Quat. Sci. Rev. 28 1631–57), A et al (2013 Geophys. J. Int. 192 557–72) and Wu et al (2010 Nature Geosci. 3 642–6) by comparing the spatial patterns of GRACE-derived ice mass trends calculated using the three corrections with volume changes from ICESat (Ice, Cloud, and land Elevation Satellite) and OIB (Operation IceBridge) altimetry missions, and surface mass balance products from the Regional Atmospheric Climate Model (RACMO). During the period September 2003–August 2011, GRACE ice mass changes obtained using the Simpson et al (2009 Quat. Sci. Rev. 28 1631–57) and A et al (2013 Geophys. J. Int. 192 557–72) GIA corrections yield similar spatial patterns and amplitudes, and are consistent with altimetry observations and surface mass balance data. The two GRACE estimates agree within 2% on average over the entire ice sheet, and better than 15% in four subdivisions of Greenland. The third GRACE estimate corrected using the (Wu et al 2010 Nature Geosci. 3 642–6)) GIA shows similar spatial patterns, but produces an average ice mass loss for the entire ice sheet that is 64 − 67 Gt yr −1 smaller. In the Northeast the recovered ice mass change is 46–49 Gt yr −1 (245–270%) more positive than that deduced from the other two corrections. By comparing the spatial and temporal variability of the GRACE estimates with trends of volume changes from altimetry and surface mass balance from RACMO, we show that the Wu et al (2010 Nature Geosci. 3 642–6) correction leads to a large mass increase in the Northeast that is inconsistent with independent observations. (paper)

  9. Radial and tangential gravity rates from GRACE in areas of glacial isostatic adjustment

    Science.gov (United States)

    van der Wal, Wouter; Kurtenbach, Enrico; Kusche, Jürgen; Vermeersen, Bert

    2011-11-01

    In areas dominated by Glacial Isostatic Adjustment (GIA), the free-air gravity anomaly rate can be converted to uplift rate to good approximation by using a simple spectral relation. We provide quantitative comparisons between gravity rates derived from monthly gravity field solutions (GFZ Potsdam, CSR Texas, IGG Bonn) from the Gravity Recovery and Climate Experiment (GRACE) satellite mission with uplift rates measured by GPS in these areas. The band-limited gravity data from the GRACE satellite mission can be brought to very good agreement with the point data from GPS by using scaling factors derived from a GIA model (the root-mean-square of differences is 0.55 mm yr-1 for a maximum uplift rate signal of 10 mm yr-1). The root-mean-square of the differences between GRACE derived uplift rates and GPS derived uplift rates decreases with increasing GRACE time period to a level below the uncertainty that is expected from GRACE observations, GPS measurements and the conversion from gravity rate to uplift rate. With the current length of time-series (more than 8 yr) applying filters and a hydrology correction to the GRACE data does not reduce the root-mean-square of differences significantly. The smallest root-mean-square was obtained with the GFZ solution in Fennoscandia and with the CSR solution in North America. With radial gravity rates in excellent agreement with GPS uplift rates, more information on the GIA process can be extracted from GRACE gravity field solutions in the form of tangential gravity rates, which are equivalent to a rate of change in the deflection of the vertical scaled by the magnitude of gravity rate vector. Tangential gravity rates derived from GRACE point towards the centre of the previously glaciated area, and are largest in a location close to the centre of the former ice sheet. Forward modelling showed that present day tangential gravity rates have maximum sensitivity between the centre and edge of the former ice sheet, while radial gravity

  10. Glacial isostatic adjustment and sea-level change. State of the art report

    International Nuclear Information System (INIS)

    Whitehouse, Pippa

    2009-04-01

    This report outlines the physics of glacial isostatic adjustment (GIA), how this affects sea-level, and the methods which are employed by researchers to study and understand these processes. The report describes the scientific background into the processes and methods presented in SKB TR-06-23 (INIS ref 38-021351). The purpose of this report is to provide a reference document for people who require a more in-depth understanding of GIA processes than is presented in the earlier report. The key components of the GIA system are described, and this is followed by a concise description of the processes that take place within and between these components during a glacial cycle. The report contains 4 chapters: Chapter 1, 'Introduction'; Chapter 2, 'GIA systems', describes the three main systems which are involved in the GIA process; the solid Earth, the hydrosphere and the cryosphere. The various parameters which govern the behaviour of these systems, and must be known in order to model GIA processes, are defined. Chapter 3, 'Governing equations', lays out the physics of GIA and derives the equations which must be solved to determine the redistribution of water over the surface of the Earth, and the solid Earth response. Secondary processes, such as ocean syphoning, are also described. The driving forces behind glacial cycles are briefly discussed. The methods used to solve these equations are laid out in chapter 4, 'State-of-the-art GIA models'. In this chapter, the different approaches used by different groups of researchers are discussed, as are the relative accuracy of the methods. Recent improvements to the theory are described, as are current shortcomings of the models. The various data sets used to calibrate and verify the accuracy of the modelling are also briefly described in this chapter. In the past few years advances in computational speed have enabled researchers to develop models which attempt to account for the effects 3-D Earth structure upon GIA processes

  11. The influence of lateral Earth structure on glacial isostatic adjustment in Greenland

    Science.gov (United States)

    Milne, Glenn A.; Latychev, Konstantin; Schaeffer, Andrew; Crowley, John W.; Lecavalier, Benoit S.; Audette, Alexandre

    2018-05-01

    We present the first results that focus on the influence of lateral Earth structure on Greenland glacial isostatic adjustment (GIA) using a model that can explicitly incorporate 3-D Earth structure. In total, eight realisations of lateral viscosity structure were developed using four global seismic velocity models and two global lithosphere (elastic) thickness models. Our results show that lateral viscosity structure has a significant influence on model output of both deglacial relative sea level (RSL) changes and present-day rates of vertical land motion. For example, lateral structure changes the RSL predictions in the Holocene by several 10 s of metres in many locations relative to the 1-D case. Modelled rates of vertical land motion are also significantly affected, with differences from the 1-D case commonly at the mm/yr level and exceeding 2 mm/yr in some locations. The addition of lateral structure was unable to account for previously identified data-model RSL misfits in northern and southern Greenland, suggesting limitations in the adopted ice model (Lecavalier et al. 2014) and/or the existence of processes not included in our model. Our results show large data-model discrepancies in uplift rates when applying a 1-D viscosity model tuned to fit the RSL data; these discrepancies cannot be reconciled by adding the realisations of lateral structure considered here. In many locations, the spread in model output for the eight different 3-D Earth models is of similar amplitude or larger than the influence of lateral structure (as defined by the average of all eight model runs). This reflects the differences between the four seismic and two lithosphere models used and implies a large uncertainty in defining the GIA signal given that other aspects that contribute to this uncertainty (e.g. scaling from seismic velocity to viscosity) were not considered in this study. In order to reduce this large model uncertainty, an important next step is to develop more accurate

  12. Use of GRACE determined secular gravity rates for glacial isostatic adjustment studies in North-America

    Science.gov (United States)

    van der Wal, Wouter; Wu, Patrick; Sideris, Michael G.; Shum, C. K.

    2008-10-01

    Monthly geopotential spherical harmonic coefficients from the GRACE satellite mission are used to determine their usefulness and limitations for studying glacial isostatic adjustment (GIA) in North-America. Secular gravity rates are estimated by unweighted least-squares estimation using release 4 coefficients from August 2002 to August 2007 provided by the Center for Space Research (CSR), University of Texas. Smoothing is required to suppress short wavelength noise, in addition to filtering to diminish geographically correlated errors, as shown in previous studies. Optimal cut-off degrees and orders are determined for the destriping filter to maximize the signal to noise ratio. The halfwidth of the Gaussian filter is shown to significantly affect the sensitivity of the GRACE data (with respect to upper mantle viscosity and ice loading history). Therefore, the halfwidth should be selected based on the desired sensitivity. It is shown that increase in water storage in an area south west of Hudson Bay, from the summer of 2003 to the summer of 2006, contributes up to half of the maximum estimated gravity rate. Hydrology models differ in the predictions of the secular change in water storage, therefore even 4-year trend estimates are influenced by the uncertainty in water storage changes. Land ice melting in Greenland and Alaska has a non-negligible contribution, up to one-fourth of the maximum gravity rate. The estimated secular gravity rate shows two distinct peaks that can possibly be due to two domes in the former Pleistocene ice cover: west and south east of Hudson Bay. With a limited number of models, a better fit is obtained with models that use the ICE-3G model compared to the ICE-5G model. However, the uncertainty in interannual variations in hydrology models is too large to constrain the ice loading history with the current data span. For future work in which GRACE will be used to constrain ice loading history and the Earth's radial viscosity profile, it is

  13. Glacial isostatic adjustment and sea-level change. State of the art report

    Energy Technology Data Exchange (ETDEWEB)

    Whitehouse, Pippa (Durham Univ., Dept. of Geography, Durham (United Kingdom))

    2009-04-15

    This report outlines the physics of glacial isostatic adjustment (GIA), how this affects sea-level, and the methods which are employed by researchers to study and understand these processes. The report describes the scientific background into the processes and methods presented in SKB TR-06-23 (INIS ref 38-021351). The purpose of this report is to provide a reference document for people who require a more in-depth understanding of GIA processes than is presented in the earlier report. The key components of the GIA system are described, and this is followed by a concise description of the processes that take place within and between these components during a glacial cycle. The report contains 4 chapters: Chapter 1, 'Introduction'; Chapter 2, 'GIA systems', describes the three main systems which are involved in the GIA process; the solid Earth, the hydrosphere and the cryosphere. The various parameters which govern the behaviour of these systems, and must be known in order to model GIA processes, are defined. Chapter 3, 'Governing equations', lays out the physics of GIA and derives the equations which must be solved to determine the redistribution of water over the surface of the Earth, and the solid Earth response. Secondary processes, such as ocean syphoning, are also described. The driving forces behind glacial cycles are briefly discussed. The methods used to solve these equations are laid out in chapter 4, 'State-of-the-art GIA models'. In this chapter, the different approaches used by different groups of researchers are discussed, as are the relative accuracy of the methods. Recent improvements to the theory are described, as are current shortcomings of the models. The various data sets used to calibrate and verify the accuracy of the modelling are also briefly described in this chapter. In the past few years advances in computational speed have enabled researchers to develop models which attempt to account for the

  14. WordPress web design for dummies

    CERN Document Server

    Sabin-Wilson, Lisa

    2013-01-01

    Updated, full-color guide to creating dynamic websites with WordPress 3.6 In this updated new edition, bestselling For Dummies author and WordPress expert Lisa Sabin-Wilson makes it easy for anyone with a basic knowledge of the WordPress software to create a custom site using complementary technologies such as CSS, HTML, PHP, and MySQL. You'll not only get up to speed on essential tools and technologies and further advance your own design skills, this book also gives you pages of great case studies, so you can see just how other companies and individuals are creating compelling, customized, a

  15. Teach yourself visually complete WordPress

    CERN Document Server

    Majure, Janet

    2013-01-01

    Take your WordPress skills to the next level with these tips, tricks, and tasks Congratulations on getting your blog up and running with WordPress! Now are you ready to take it to the next level? Teach Yourself VISUALLY Complete WordPress takes you beyond the blogging basics with expanded tips, tricks, and techniques with clear, step-by-step instructions accompanied by screen shots. This visual book shows you how to incorporate forums, use RSS, obtain and review analytics, work with tools like Google AdSense, and much more.Shows you how to use mobile tools to edit a

  16. WordPress 24-Hour Trainer

    CERN Document Server

    Plumley, George

    2011-01-01

    The eagerly anticipated second edition, completely updated for WordPress 3.1 As an open source content management system, WordPress allows users to easily build feature-rich web sites with no programming experience. This unique book-and-video package is a friendly, self-paced beginners guide to the latest release of WordPress. Lessons are focused on practical, everyday tasks that users will need to create and maintain their sites: entering new content, creating new pages, managing menus, making content search-engine friendly. Plus you'll find lots of tips based on years of experience teaching

  17. WordPress web application development

    CERN Document Server

    Ratnayake, Rakhitha Nimesh

    2013-01-01

    An extensive, practical guide that explains how to adapt WordPress features, both conventional and trending, for web applications.This book is intended for WordPress developers and designers who have the desire to go beyond conventional website development to develop quality web applications within a limited time frame and for maximum profit. Experienced web developers who are looking for a framework for rapid application development will also find this to be a useful resource. Prior knowledge with of WordPress is preferable as the main focus will be on explaining methods for adapting WordPres

  18. Professional WordPress Plugin Development

    CERN Document Server

    Williams, Brad; Tadlock, Justin

    2011-01-01

    Taking WordPress to the next level with advanced plugin developmentWordPress is used to create self-hosted blogs and sites, and it's fast becoming the most popular content management system (CMS) on the Web. Now you can extend it for personal, corporate and enterprise use with advanced plugins and this professional development guide. Learn how to create plugins using the WordPress plugin API: utilize hooks, store custom settings, craft translation files, secure your plugins, set custom user roles, integrate widgets, work with JavaScript and AJAX, create custom post types. You'll find a practic

  19. Thermal cycling tests of actively cooled beryllium copper joints

    Energy Technology Data Exchange (ETDEWEB)

    Roedig, M.; Duwe, R.; Linke, J.; Schuster, A.; Wiechers, B. [Forschungszentrum Juelich GmbH (Germany)

    1998-01-01

    Screening tests (steady state heating) and thermal fatigue tests with several kinds of beryllium-copper joints have been performed in an electron beam facility. Joining techniques under investigation were brazing with silver containing and silver-free braze materials, hot isostatic pressing (HIP) and diffusion bonding (hot pressing). Best thermal fatigue performance was found for the brazed samples. (author)

  20. IMPROVEMENT OF WEAR COMPONENT'S PERFORMANCE BY UTILIZING ADVANCED MATERIALS AND NEW MANUFACTURING TECHNOLOGIES: CASTCON PROCESS FOR MINING APPLICATIONS

    International Nuclear Information System (INIS)

    Xiaodi Huang; Richard Gertsch

    2001-01-01

    The fibrous monolith material was successfully consolidated in both the hot press and the hot isostatic press. Initial evaluations indicate the material will have a very high fracture toughness and be very hard. Tungsten carbide was successfully consolidated in an H13 tool steel with the incorporation of a Co-Cr layer between the WC and the steel